  1. Studies of Hot Crack Properties of Laser Welded Stainless Steel

    DEFF Research Database (Denmark)

    Juhl, Thomas Winther

    During the present work crack testing concerning small and fast solidifying laser welds in austenitic stainless steel has been studied. A set of methods has been applied to investigate alloy properties, including ·Application of known information to predict solidification phases from the alloy...... composition. ·Weld metal solidification rate measurements for prediction of phases. ·Various crack tests to assess the crack susceptibility of alloys. ·A combination of the above for selection of suitable, weldable alloys. The possibility of using such specific methods for alloys and applications has been...... to the crack behaviour, but do not show an expected correlation between the crack resistance and the solidification rate. The employment of pulsed seams is therefore assessed not to be usable in the present selection methods. From evaluation of several crack tests, the Weeter spot weld test has been chosen...

  2. Assessment of Hot Crack Properties of Laser Welded Stainless Steel

    DEFF Research Database (Denmark)

    Juhl, Thomas Winther; Olsen, Flemming Ove

    2003-01-01

    Crack testing concerning small and fast solidifying laser welds in austenitic stainless steel has been studied. A set of methods has been applied to investigate alloy properties, including (1) Application of known information to predict solidification phases, (2) Weld metal solidification rate...... crack tests, the Weeter spot weld test has been chosen to form a basis for the development of a practicable method to select specific alloys for welding applications. A new test, the Groove weld test was developed, which has reduced the time consumption and lightened the analysis effort considerably...... measurements for prediction of phases, (3) Various crack tests to assess the crack susceptibility of alloys and (4) A combination of the above for selection of suitable, weldable alloys. The possibility of using such specific methods for alloys and applications has been investigated and recommendations...

  3. Cause of Damage. Hot cracking; Schadensursache Heissrissigkeit

    Energy Technology Data Exchange (ETDEWEB)

    Wader, Therese [BENTELER Steel/Tube GmbH, Paderborn (Germany). Vorentwicklung Werkstoffe

    2016-10-15

    Under certain conditions, Nb-containing stainless steels are susceptible to hot cracking. Such conditions include low melting phases on the grain boundaries, a coarse-grained microstructure such as cast structures, microstructure orientations towards the main tensile direction and high processing temperatures. The case of damage was characterized using metallographic and microanalytical methods. In the laboratory, the critical temperature range for the formation of hot cracks could furthermore specifically be localized under mechanical stresses by means of a dilatometer aiming at clearly verifying the cause of the damage, namely ''hot cracks''.

  4. High chromium nickel base alloys hot cracking susceptibility

    International Nuclear Information System (INIS)

    Tirand, G.; Primault, C.; Robin, V.

    2014-01-01

    High Chromium nickel based alloys (FM52) have a higher ductility dip cracking sensitivity. New filler material with higher niobium and molybdenum content are developed to decrease the hot crack formation. The behavior of these materials is studied by coupling microstructural analyses and hot cracking test, PVR test. The metallurgical analyses illustrate an Nb and Mo enrichment of the inter-dendritic spaces of the new materials. A niobium high content (FM52MSS) induces the formation of primary carbide at the end of solidification. The PVR test reveal a solidification crack sensitivity of the new materials, and a lowest ductility dip cracking sensitivity for the filler material 52MSS. (authors)

  5. Test methods for evaluating hot cracking: Review and perspective

    International Nuclear Information System (INIS)

    Goodwin, G.M.

    1990-01-01

    The phenomenon of hot cracking is described and discussed, and criteria for tests to assess hot cracking are elucidated. The historical development of hot cracking tests is traced from the 1930s to present, with categorization of tests into several types. It is noted that the number of tests developed continues to increase dramatically. The number of literature citations also increases with time, with few popular tests receiving a major share of interest. Predominant countries of origin of both tests and citations shift with time, and a few journals account for most of the published information. Reviews of hot cracking are reviewed, and it is predicted that modeling and other developing analytical techniques will contribute greatly to an increase in our understanding of hot cracking. 30 refs., 10 figs., 1 tab

  6. Experimental and numerical approaches to studying hot cracking in stainless steel welds

    International Nuclear Information System (INIS)

    Le, Minh

    2014-01-01

    This work concerns experimental and numerical approaches to studying hot cracking in welds in stainless steel. Metallurgical weldability of two filler products used for the welding of an AISI-316L(N) austenitic stainless steel grade is evaluated. These filler metals are distinguished by their solidification microstructures: austeno-ferritic for the 19Cr-12Ni-2Mo grade and austenitic for the 19-15H Thermanit grade. The study of weldability concerns the assessment of the susceptibility to hot cracking of these three alloys, the proposition of a hot cracking criterion, and the evaluation of its transferability to structure-scale tests. Hot cracks are material separations occurring at high temperatures along the grain boundaries (dendrite boundaries), when the level of strain and the strain rate exceed a certain level. The hot cracks studied are formed during solidification from the liquid phase of weld metals. The bibliography study brings to the fore the complexity of initiation and propagation mechanisms of these material separations. Three types of tests are studied in this work: hot cracking tests, such as trapezoidal and Varestraint tests, allowing to initiate the phenomenon in controlled experimental conditions, and tests on the Gleeble thermomechanical simulator for thermomechanical (materials behavior laws, fracture properties) and metallurgical (brittle temperature range (BTR), evolution of delta ferrite) characterizations of the alloys. All these tests on the three materials were analyzed via numerical modeling and simulations implemented in the Cast3M finite element code in order to bring out a thermomechanical hot cracking criterion. (author) [fr

  7. A review of hot cracking in austenitic stainless steel weldments

    International Nuclear Information System (INIS)

    Shankar, V.; Gill, T.P.S.; Mannan, S.L.; Rodriguez, P.

    1991-01-01

    The occurrence of hot cracking in austenitic stainless steel weldments is discussed with respect to its origin and metallurgical contributory factors. Of the three types of hot cracking, namely solidification cracking, liquation and ductility dip cracking, solidification cracking occurs in the interdendritic regions in weld metal while liquation and ductility dip cracking occur intergranularly in the heat-affected zone (HAZ). Segregation of impurity and minor elements such as sulphur, phosphorous, silicon, niobium, boron etc to form low melting eutectic phases has been found to be the major cause of hot cracking. Control of HAZ cracking requires minimisation of impurity elements in the base metal. In stabilized stainless steels containing niobium, higher amounts of delta-ferrite have been found necessary to prevent cracking than in unstabilized compositions. Titanium compounds have been found to cause liquation cracking in maraging steels and titanium containing stainless steels and superalloys. In nitrogen added stainless steels, cracking resistance decreases when the solidification mode changes to primary austenitic due to nitrogen addition. A review of the test methods to evaluate hot cracking behaviour showed that several external restraint and semi-self-restraint tests are available. The finger Test, WRC Fissure Bend Test, the PVR test and the Varestraint Test are described along with typical test results. Hot ductility testing to reveal HAZ cracking tendency during welding is described, which is of particular importance to stabilized stainless steels. Based on the literature, recommendations are made for welding stabilized and nitrogen added steels, indicating areas of further work. (author). 81 refs., 30 figs., 1 tab

  8. Investigation of hot cracking in deep penetration electron beam welds

    Energy Technology Data Exchange (ETDEWEB)

    Thorvaldson, W.G.

    1978-06-10

    A defect in a deep penetration electron beam weld of 304L stainless steel to 21-6-9 stainless steel has been identified as a centerline hot crack. The study discussed in this report was made to define and to eliminate the cause of cracking.

  9. The Relation Between Alloy Chemistry and Hot-Cracking

    Science.gov (United States)

    Nunes, A. C., Jr.; Talia, J. E.

    2000-01-01

    Hot cracking is a problem in welding 2195 aluminum-lithium alloy. Weld wire additives seem to reduce the problem. This study proposes a model intended to clarify the way alloying elements affect hot-cracking. The brittle temperature range of an alloy extends wherever the tensile stress required to move the meniscus of the liquid film at the grain/dendrite boundaries is less than the bulks flow stress Sigma(sub B) of the grains: 2gamma/delta alloys outgas.) If the above condition is not met, the grains deform under stress and the liquid film remains in place. Curves of 2gamma/delta and sigma(sub B) vs. temperature in the range just below the melting temperature determine the hot cracking susceptibility of an alloy. Both are zero at onset of solidification. sigma(sub B) rises as the thermal activation of the slip mechanism is reduced. 2gamma/delta rises as the film thickness delta which can be estimated from the Scheil equation, drops. But, given an embrittled alloy, whether the alloy actually cracks is determined by the strain imposed upon it in the embrittled condition. A critical strain is estimated, Epsilon(sub C) on the order of Epsilon(sub C) is approximately delta/l where L = grain size and where the the volume increment due to the strain, concentrated at the liquid film, is on the order of the liquid film volume. In the early 80's an empirical critical strain cracking envelope Epsilon(sub C)(T) was incorporated into a damage criterion to estimate the effect of welding parameters on the formation of microfissures in a superalloy with good results. These concepts, liquid film decoherence vs. grain bulk deformation and critical strain, form the key elements of a quantitative theory of hot-cracking applicable for assessing the effect of alloying elements on hot-cracking during welding.

  10. Quantitative analysis of prediction models for hot cracking in ...

    Indian Academy of Sciences (India)

    A RodrМguez-Prieto

    2017-11-16

    Nov 16, 2017 ... In this paper, a systematic analysis of different methods of d-ferrite estimation is carried out based ... Keywords. d-Ferrite; hot cracking; prediction methods; stringency levels; decision tool. 1. .... prediction of d-ferrite content using a system of multi- ..... support the selection of some materials according to their.

  11. Contribution to the determination of priority constructive influences on the hot crack initiation of welded components

    International Nuclear Information System (INIS)

    Gollnow, Christian

    2015-01-01

    The previous research results do not allow a general hot crack characterisation although a variety of experimental and numerical knowledge is available. The reason for this is mainly the large number of influencing factors that complicate a complete description of the hot cracking phenomenon and especially solidification cracking. The hot crack formation and thus the solidification crack initiation can be described by the interaction of process, metallurgy and design. However, the literature examination shows that in the solidifaction crack characterisation the influence of the design aspect is often underestimated. The pre-stresses of the structural components is up to now not considered as an essential cause for the formation of solidification cracks. The evaluation of the influence of the various parameters is presented partly inconsistent. In addition, the targeted presentation of the design influence with respect to the solidification cracks in the weld is because the limited transferability of the various component-specific stresses on a laboratory scale and thus to the respective hot cracking tests restricted. Hence, the difficulty to transfer the results between laboratory specimen and component as well as the general hot crack characterisation is given. In this work the different types of stresses from the component welding in the laboratory and to quantify experimentally the solidification crack critical values, displacements and displacement rates were detected. In this regard external loaded hot cracking tests were carried out by using the advantages of contactless measurement techniques close to the weld and to analyse the welding process with respect to various local and global design-specific factors influencing the formation of solidification cracks in high alloyed steel. These investigations were performed on austenitic (1.4828) and ferritic (1.4509) materials with different mechanical and technological properties. To reflect the praxis relevant

  12. Influence of precipitation behavior on mechanical properties and hydrogen induced cracking during tempering of hot-rolled API steel for tubing

    Energy Technology Data Exchange (ETDEWEB)

    Moon, Joonoh, E-mail: mjo99@kims.re.kr [Ferrous Alloy Department, Advanced Metallic Materials Division, Korea Institute of Materials Science, 797 Changwondae-ro, Seongsan-gu, Changwon, Gyeongnam 642-831 (Korea, Republic of); Choi, Jongmin; Han, Seong-Kyung; Huh, Sungyul; Kim, Seong-Ju [Sheet Products Design Team, Technical Research Center, Hyundai Steel Company, 1480 Bukbusaneop-ro, Dangjin, Chungnam 343-823 (Korea, Republic of); Lee, Chang-Hoon; Lee, Tae-Ho [Ferrous Alloy Department, Advanced Metallic Materials Division, Korea Institute of Materials Science, 797 Changwondae-ro, Seongsan-gu, Changwon, Gyeongnam 642-831 (Korea, Republic of)

    2016-01-15

    Precipitation behavior and its effect on hydrogen embrittlement during tempering process of hot-rolled API steel designed with 0.4 wt% Cr and 0.25 wt% Mo were investigated. The base steel was normalized and then tempered at 650 °C for up to 60 min. The precipitation behavior of the examined steel was explored using transmission electron microscopy (TEM) analysis, and it was found that the precipitation sequence during tempering at 650 °C were as follows: MX+M{sub 3}C→MX→MX+M{sub 7}C{sub 3}+M{sub 23}C{sub 6}. The change of particle fraction was measured by electrolytic extraction technique. At the early stage of tempering, the particle fraction greatly decreased due to dissolution of M{sub 3}C particle, and increased after 10 min by the precipitation of M{sub 7}C{sub 3} and M{sub 23}C{sub 6} particles. The particle fraction showed a peak at 30 min tempering and decreased again due to the dissolution of M{sub 7}C{sub 3} particle. Vickers hardness tests of base steel and tempered samples were carried out, and then the hardness was changed by accompanying with the change of particle fraction. The sensitivity of hydrogen embrittlement was evaluated through hydrogen induced cracking (HIC) tests, and the results clearly proved that HIC resistance of tempered samples was better than that of base steel due to the formation of tempered martensite, and then the HIC resistance changed depending on the precipitation behavior during tempering, i.e., the precipitation of coarse M{sub 23}C{sub 6} and M{sub 7}C{sub 3} particles deteriorated the HIC resistance.

  13. Influence of precipitation behavior on mechanical properties and hydrogen induced cracking during tempering of hot-rolled API steel for tubing

    International Nuclear Information System (INIS)

    Moon, Joonoh; Choi, Jongmin; Han, Seong-Kyung; Huh, Sungyul; Kim, Seong-Ju; Lee, Chang-Hoon; Lee, Tae-Ho

    2016-01-01

    Precipitation behavior and its effect on hydrogen embrittlement during tempering process of hot-rolled API steel designed with 0.4 wt% Cr and 0.25 wt% Mo were investigated. The base steel was normalized and then tempered at 650 °C for up to 60 min. The precipitation behavior of the examined steel was explored using transmission electron microscopy (TEM) analysis, and it was found that the precipitation sequence during tempering at 650 °C were as follows: MX+M_3C→MX→MX+M_7C_3+M_2_3C_6. The change of particle fraction was measured by electrolytic extraction technique. At the early stage of tempering, the particle fraction greatly decreased due to dissolution of M_3C particle, and increased after 10 min by the precipitation of M_7C_3 and M_2_3C_6 particles. The particle fraction showed a peak at 30 min tempering and decreased again due to the dissolution of M_7C_3 particle. Vickers hardness tests of base steel and tempered samples were carried out, and then the hardness was changed by accompanying with the change of particle fraction. The sensitivity of hydrogen embrittlement was evaluated through hydrogen induced cracking (HIC) tests, and the results clearly proved that HIC resistance of tempered samples was better than that of base steel due to the formation of tempered martensite, and then the HIC resistance changed depending on the precipitation behavior during tempering, i.e., the precipitation of coarse M_2_3C_6 and M_7C_3 particles deteriorated the HIC resistance.

  14. Welding hot cracking in an austenitic stainless steel

    International Nuclear Information System (INIS)

    Kerrouault, N.

    2001-01-01

    The occurrence of hot cracking is linked to several conditions, in particular, the composition of the material and the local strains due to clambering. The aim of this study is to better analyse the implied mechanisms and to lead to a local thermomechanical criterion for hot cracking. The example studied is an AISI 321-type stainless steel (X10CrNiTi18-12) strongly prone to cracking. Two weldability tests are studied: - the first one consists in carrying out a fusion line by the TIG process on a thin sheet. In the case of the defect occurrence, the crack is longitudinal and follows the back of the molten bath. The influence of the operating conditions welding (speed, welding heat input, width test sample) is studied. - the second one is the Varestraint test. It is widely used to evaluate the sensitivity of a material to hot cracking. It consists in loading the material by bending during a fusion line by the TIG process and in characterising the defects quantity (length, number). Various thermal and mechanical instrumentation methods were used. The possibilities of a local instrumentation instrumentation being limited because of the melting, the experimental results were complemented by a numerical modelling whose aim is to simulate the thermomechanical evolution of the loading thanks to the finite element analysis code ABAQUS. First, the heat input for thermal simulation is set by the use of an inverse method in order to optimise the energy deposit mode during welding in the calculation. Then, the mechanical simulation needs the input of a constitutive law that fits the mechanical behaviour over a wide temperature range from ambient to melting temperature. Thus, a mechanical characterization is performed by selecting strain values and strain rates representative of what the material undergoes during the tests. The results come from tensile and compressive tests and allow to settle an elasto-visco-plastic constitutive law over temperatures up to liquidus. Once

  15. Statistical analysis of process parameters to eliminate hot cracking of fiber laser welded aluminum alloy

    Science.gov (United States)

    Wang, Jin; Wang, Hui-Ping; Wang, Xiaojie; Cui, Haichao; Lu, Fenggui

    2015-03-01

    This paper investigates hot cracking rate in Al fiber laser welding under various process conditions and performs corresponding process optimization. First, effects of welding process parameters such as distance between welding center line and its closest trim edge, laser power and welding speed on hot cracking rate were investigated experimentally with response surface methodology (RSM). The hot cracking rate in the paper is defined as ratio of hot cracking length over the total weld seam length. Based on the experimental results following Box-Behnken design, a prediction model for the hot cracking rate was developed using a second order polynomial function considering only two factor interaction. The initial prediction result indicated that the established model could predict the hot cracking rate adequately within the range of welding parameters being used. The model was then used to optimize welding parameters to achieve cracking-free welds.

  16. Hot-crack test for aluminium alloys welds using TIG process

    Science.gov (United States)

    Niel, A.; Deschaux-Beaume, F.; Bordreuil, C.; Fras, G.

    2010-06-01

    Hot cracking is a critical defect frequently observed during welding of aluminium alloys. In order to better understand the interaction between cracking phenomenon, process parameters, mechanical factors and microstructures resulting from solidification after welding, an original hot-cracking test during welding is developed. According to in-situ observations and post mortem analyses, hot cracking mechanisms are investigated, taking into account the interaction between microstructural parameters, depending on the thermal cycles, and mechanical parameters, depending on geometry and clamping conditions of the samples and on the thermal field on the sample. Finally, a process map indicating the limit between cracking and non-cracking zones according to welding parameters is presented.

  17. Dendritic microstructure and hot cracking of laser additive manufactured Inconel 718 under improved base cooling

    International Nuclear Information System (INIS)

    Chen, Yuan; Lu, Fenggui; Zhang, Ke; Nie, Pulin; Elmi Hosseini, Seyed Reza; Feng, Kai; Li, Zhuguo

    2016-01-01

    The base cooling effect was improved by imposing the continuous water flow on the back of the substrate during the laser additive manufacturing of Inconel 718 (IN718). The dendritic microstructure, crystal orientation and hot cracking behavior were studied by using optical microscopy (OM), scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD) techniques. The results showed that the crystal orientation was increased by increasing the base cooling effect during the deposition. Also, highly ordered columnar dendrites were established, and mono-crystalline texture was constructed in the final clad. It was fund that the effect of solidification cracking on the properties of final clad was negligible since it was only generated at the top region of the deposit, while liquation cracking was produced and remained in the heat affected zone (HAZ) and needed to be carefully controlled. The susceptibility to the liquation cracking showed a high dependence on the grain boundary misorientation, which was considered to be attributed to the stability of interdendritic liquation films, as well as the magnitude of local stress concentration in the last stage of solidification. - Highlights: • The base cooling effect was increased during laser additive manufacturing. • Highly ordered dendrites were established under improved base cooling. • The crystal orientation was increased by improving the base cooling effect. • Liquation cracking tendency was reduced due to the increase of base cooling. • Liquation cracking increased with the increase of grain boundary misorientation.

  18. Dendritic microstructure and hot cracking of laser additive manufactured Inconel 718 under improved base cooling

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Yuan; Lu, Fenggui; Zhang, Ke; Nie, Pulin; Elmi Hosseini, Seyed Reza; Feng, Kai, E-mail: fengkai@sjtu.edu.cn; Li, Zhuguo, E-mail: lizg@sjtu.edu.cn

    2016-06-15

    The base cooling effect was improved by imposing the continuous water flow on the back of the substrate during the laser additive manufacturing of Inconel 718 (IN718). The dendritic microstructure, crystal orientation and hot cracking behavior were studied by using optical microscopy (OM), scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD) techniques. The results showed that the crystal orientation was increased by increasing the base cooling effect during the deposition. Also, highly ordered columnar dendrites were established, and mono-crystalline texture was constructed in the final clad. It was fund that the effect of solidification cracking on the properties of final clad was negligible since it was only generated at the top region of the deposit, while liquation cracking was produced and remained in the heat affected zone (HAZ) and needed to be carefully controlled. The susceptibility to the liquation cracking showed a high dependence on the grain boundary misorientation, which was considered to be attributed to the stability of interdendritic liquation films, as well as the magnitude of local stress concentration in the last stage of solidification. - Highlights: • The base cooling effect was increased during laser additive manufacturing. • Highly ordered dendrites were established under improved base cooling. • The crystal orientation was increased by improving the base cooling effect. • Liquation cracking tendency was reduced due to the increase of base cooling. • Liquation cracking increased with the increase of grain boundary misorientation.

  19. Investigation of hot cracking resistance of 2205 duplex steel

    Energy Technology Data Exchange (ETDEWEB)

    Adamiec, J; Scibisz, B, E-mail: janusz.adamiec@polsl.pl [Silesian University of Technology, Faculty of Materials Science and Metallurgy, ul. Krasinskiego 8, PL-40019 Katowice (Poland)

    2010-02-15

    Austenitic duplex steel of the brand 2205 according to Avesta Sheffield is used for welded constructions (pipelines, tanks) in the petrol industry, chemical industry and food industry. It is important to know the range of high-temperature brittleness in designing welding technology for constructions made of this steel type. There is no data in literature concerning this issue. High-temperature brittleness tests using the simulator of heat flow device Gleeble 3800 were performed. The tests results allowed the evaluation of the characteristic temperatures in the brittleness temperature range during the joining of duplex steels, specifically the nil-strength temperature (NST) and nil-ductility temperatures (NDT) during heating, the strength and ductility recovery temperatures (DRT) during cooling, the R{sub f}parameter (R{sub f} = (T{sub liquidus} - NDT)/NDT) describing the duplex steel inclination for hot cracking, and the brittleness temperature range (BTR). It has been stated that, for the examined steel, this range is wide and amounts to ca. 90 deg. C. The joining of duplex steels with the help of welding techniques creates a significant risk of hot cracks. After analysis of the DTA curves a liquidus temperature of T{sub L} = 1465 deg. C and a solidus temperature of T{sub S} = 1454 deg. C were observed. For NST a mean value was assumed, in which the cracks appeared for six samples; the temperature was 1381 deg. C. As the value of the NDT temperature 1367 deg. C was applied while for DRT the assumed temperature was 1375 deg. C. The microstructure of the fractures was observed using a Hitachi S-3400N scanning electron microscope (SEM). The analyses of the chemical composition were performed using an energy-dispersive X-ray spectrometer (EDS), Noran System Six of Thermo Fisher Scientific. Essential differences of fracture morphology type over the brittle temperature range were observed and described.

  20. Investigation of hot cracking resistance of 2205 duplex steel

    Science.gov (United States)

    Adamiec, J.; Ścibisz, B.

    2010-02-01

    Austenitic duplex steel of the brand 2205 according to Avesta Sheffield is used for welded constructions (pipelines, tanks) in the petrol industry, chemical industry and food industry. It is important to know the range of high-temperature brittleness in designing welding technology for constructions made of this steel type. There is no data in literature concerning this issue. High-temperature brittleness tests using the simulator of heat flow device Gleeble 3800 were performed. The tests results allowed the evaluation of the characteristic temperatures in the brittleness temperature range during the joining of duplex steels, specifically the nil-strength temperature (NST) and nil-ductility temperatures (NDT) during heating, the strength and ductility recovery temperatures (DRT) during cooling, the Rfparameter (Rf = (Tliquidus - NDT)/NDT) describing the duplex steel inclination for hot cracking, and the brittleness temperature range (BTR). It has been stated that, for the examined steel, this range is wide and amounts to ca. 90 °C. The joining of duplex steels with the help of welding techniques creates a significant risk of hot cracks. After analysis of the DTA curves a liquidus temperature of TL = 1465 °C and a solidus temperature of TS = 1454 °C were observed. For NST a mean value was assumed, in which the cracks appeared for six samples; the temperature was 1381 °C. As the value of the NDT temperature 1367 °C was applied while for DRT the assumed temperature was 1375 °C. The microstructure of the fractures was observed using a Hitachi S-3400N scanning electron microscope (SEM). The analyses of the chemical composition were performed using an energy-dispersive X-ray spectrometer (EDS), Noran System Six of Thermo Fisher Scientific. Essential differences of fracture morphology type over the brittle temperature range were observed and described.

  1. Investigation of hot cracking resistance of 2205 duplex steel

    International Nuclear Information System (INIS)

    Adamiec, J; Scibisz, B

    2010-01-01

    Austenitic duplex steel of the brand 2205 according to Avesta Sheffield is used for welded constructions (pipelines, tanks) in the petrol industry, chemical industry and food industry. It is important to know the range of high-temperature brittleness in designing welding technology for constructions made of this steel type. There is no data in literature concerning this issue. High-temperature brittleness tests using the simulator of heat flow device Gleeble 3800 were performed. The tests results allowed the evaluation of the characteristic temperatures in the brittleness temperature range during the joining of duplex steels, specifically the nil-strength temperature (NST) and nil-ductility temperatures (NDT) during heating, the strength and ductility recovery temperatures (DRT) during cooling, the R f parameter (R f = (T liquidus - NDT)/NDT) describing the duplex steel inclination for hot cracking, and the brittleness temperature range (BTR). It has been stated that, for the examined steel, this range is wide and amounts to ca. 90 deg. C. The joining of duplex steels with the help of welding techniques creates a significant risk of hot cracks. After analysis of the DTA curves a liquidus temperature of T L = 1465 deg. C and a solidus temperature of T S = 1454 deg. C were observed. For NST a mean value was assumed, in which the cracks appeared for six samples; the temperature was 1381 deg. C. As the value of the NDT temperature 1367 deg. C was applied while for DRT the assumed temperature was 1375 deg. C. The microstructure of the fractures was observed using a Hitachi S-3400N scanning electron microscope (SEM). The analyses of the chemical composition were performed using an energy-dispersive X-ray spectrometer (EDS), Noran System Six of Thermo Fisher Scientific. Essential differences of fracture morphology type over the brittle temperature range were observed and described.

  2. Study of hot cracking potential in a 6-ton steel ingot casting

    Science.gov (United States)

    Yang, Jing'an; Liu, Baicheng; Shen, Houfa

    2018-04-01

    A new hot cracking potential (HCP) criterion, for the appearance of hot tearing in steel ingot castings, is proposed. The maximum value of the first principal stress, divided by the dynamic yield strength in the brittle temperature range (BTR), was used to identify the HCP. Experiments were carried out on a 6-ton P91 steel ingot in which severe hot tearing was detected in the upper centerline. Another ingot, with a better heat preservation riser, and without hot tearing, was used for comparison. Samples were obtained from the area of the ingot body with hot tearing, and their morphologies were inspected by a X-ray high energy industrial computed tomography. The carbon and sulfur distributions around the hot tearing were characterized by an infrared spectrometry carbon and sulfur analyzer. High temperature mechanical properties were obtained by a Gleeble thermal simulation machine, under different strain rates. Then, thermo-mechanical simulations using an elasto-viscoplastic finite-element model were conducted to analyze the stress and strain evolution during ingot solidification. The results showed that the hot tearing area, which was rich in both carbon and sulfur, was under excessive tensile stress in the BTR, bearing the highest HCP.

  3. Connection between hot tearing and cold cracking in DC-casting of AA7050 : Experiments and computer simulations

    NARCIS (Netherlands)

    Sosro Subroto, T.A.

    2014-01-01

    Direct-chill (DC) casting is one of the most common methods to produce ingots of high-strength aluminum alloys such as an AA7050. Despite of its superior mechanical properties, this alloy is prone to both hot tearing (HT) and cold cracking (CC) during DC casting. HT form above the solidus while CC

  4. Crack Growth Properties of Sealing Glasses

    Science.gov (United States)

    Salem, Jonathan A.; Tandon, R.

    2008-01-01

    The crack growth properties of several sealing glasses were measured using constant stress rate testing in 2% and 95% RH (relative humidity). Crack growth parameters measured in high humidity are systematically smaller (n and B) than those measured in low humidity, and velocities for dry environments are approx. 100x lower than for wet environments. The crack velocity is very sensitivity to small changes in RH at low RH. Confidence intervals on parameters that were estimated from propagation of errors were comparable to those from Monte Carlo simulation.

  5. Hot-crack test for aluminium alloys welds using TIG process

    Directory of Open Access Journals (Sweden)

    Deschaux-beaume F.

    2010-06-01

    Full Text Available Hot cracking is a critical defect frequently observed during welding of aluminium alloys. In order to better understand the interaction between cracking phenomenon, process parameters, mechanical factors and microstructures resulting from solidification after welding, an original hot-cracking test during welding is developed. According to in-situ observations and post mortem analyses, hot cracking mechanisms are investigated, taking into account the interaction between microstructural parameters, depending on the thermal cycles, and mechanical parameters, depending on geometry and clamping conditions of the samples and on the thermal field on the sample. Finally, a process map indicating the limit between cracking and non-cracking zones according to welding parameters is presented.

  6. The mechanism of hot crack formation in Ti-6A1-4V during cold crucible continuous casting

    Directory of Open Access Journals (Sweden)

    Hongsheng DING

    2004-08-01

    Full Text Available Hot crack is one of common defects in castings, which often results in failure of castings. This work studies the formation of hot cracks during cold crucible continous casting by means of experiments and thoretical analysis. The results show that the hot crack occurs on the surface and in the circumference of ingots, where the solidified shell and solidification front meet each other. The tendency of hot cracking decreases with the increase of withdrawal velocities in some extent. The hot crack is caused mainly by friction force between the shell and the crucible inner wall, and it takes place when the stress resulting from friction exceeds the tensile strength of the shell. The factors affecting the hot cracks are analyzed and verified. In order to decrease the tendency of hot cracks, technical parameters should be optimized.

  7. Relationship Between Solidification Microstructure and Hot Cracking Susceptibility for Continuous Casting of Low-Carbon and High-Strength Low-Alloyed Steels: A Phase-Field Study

    Science.gov (United States)

    Böttger, B.; Apel, M.; Santillana, B.; Eskin, D. G.

    2013-08-01

    Hot cracking is one of the major defects in continuous casting of steels, frequently limiting the productivity. To understand the factors leading to this defect, microstructure formation is simulated for a low-carbon and two high-strength low-alloyed steels. 2D simulation of the initial stage of solidification is performed in a moving slice of the slab using proprietary multiphase-field software and taking into account all elements which are expected to have a relevant effect on the mechanical properties and structure formation during solidification. To account for the correct thermodynamic and kinetic properties of the multicomponent alloy grades, the simulation software is online coupled to commercial thermodynamic and mobility databases. A moving-frame boundary condition allows traveling through the entire solidification history starting from the slab surface, and tracking the morphology changes during growth of the shell. From the simulation results, significant microstructure differences between the steel grades are quantitatively evaluated and correlated with their hot cracking behavior according to the Rappaz-Drezet-Gremaud (RDG) hot cracking criterion. The possible role of the microalloying elements in hot cracking, in particular of traces of Ti, is analyzed. With the assumption that TiN precipitates trigger coalescence of the primary dendrites, quantitative evaluation of the critical strain rates leads to a full agreement with the observed hot cracking behavior.

  8. Emerging issues in environmental cracking in hot water

    International Nuclear Information System (INIS)

    Andresen, P.L.; Morra, M.M.

    2007-01-01

    Extensive research and engineering application efforts have been made to understand and manage environmentally assisted cracking (EAC) in high temperature water. EAC is a complex phenomena involving dozens of important parameters, and important issues continue to emerge as careful studies have been performed. This paper summarizes a number of emerging issues, and highlights the need for improvements in experimental sophistication and for deeper probing into the nature and importance of these emerging issues. (author)

  9. Static and dynamical properties of hot nuclei

    International Nuclear Information System (INIS)

    Suraud, E.

    1990-01-01

    We briefly review our understanding of the formation of excited/hot nuclei in heavy-ion collisions at some tens of MeV/A. We recall the major theoretical frameworks used for describing as well the entrance channel of the reaction as the structure properties of hot nuclei. We finally focus on multifragmentation within insisting upon the theoretical challenge it does represent

  10. Diffractive optics for reduction of hot cracking in pulsed mode Nd:YAG laser welding

    DEFF Research Database (Denmark)

    Bagger, Claus; Olesen, Søren; Roos, Sven-Olov

    2001-01-01

    In order to reduce the susceptibility to hot cracking in pulsed mode laser welding of austenitic stainless steel, an optical system for reduction of the cooling rate is sought developed. Based on intensive numerical simulations, an optical system producing three focused spots is made. In a number...

  11. Effect of chemical composition and cooling conditions on solidification hot cracking of Ni-based alloys

    International Nuclear Information System (INIS)

    De Vito, Sophie

    2000-01-01

    Ni-based alloys 690 present solidification hot cracks during welding of vapour generators. Hot cracks are qualitatively known to be due to the formation of inter-dendritic liquid films and of secondary phases down to low temperatures. This study aims at establishing the link between thermodynamics, solidification and hot cracking. Experimental solidification paths of high purity alloys (with varying Nb and Si contents) are obtained from quenching during directional solidification and TIG-welding experiments. They are compared to Thermo-Calc computations, assuming no diffusion in the solid. From directional solidification samples, good agreement between computed and experimental solidification paths is shown in the quenched liquid. Secondary arms of dendrites are affected by solid state diffusion of Nb. Combined effect of diffusion and solute build-up in the liquid phase modifies micro-segregation in the solid region. Solidification paths from welding specimens are similar to those of the solid region of quenched samples. Nb solid state diffusion is negligible but undercooling compensates the effect of solid state diffusion in directional solidification. Evolution of liquid fraction at the end of the solidification is in accordance with the hot cracking classification of the alloys. Nb favours formation of inter-dendritic liquid films and eutectic-like phases down to low temperature. (author) [fr

  12. Influence of dipping time on cracking during bending of hot dip galvanized coatings with Sn and Ti contents

    Directory of Open Access Journals (Sweden)

    L. Zortea

    2010-10-01

    Full Text Available In the last years, the attention to environmental topics led a new approach solution in classical protection techniques, introducing innovative way oriented to optimize different coating properties. Hot-dip galvanizing is a classical process aimed to generate coatings on iron-based surfaces, used unchanged since 200 years: some chemical elements are added in the bath with different aims (e.g., Pb is really important for its fluidizing properties, sometimes replaced by Sn but sometimes these elements are dangerous for human health (e.g. … Pb!.In this work, the influence of dipping time and coatings chemical compositions on damaging micromechanisms was investigated considering different Sn and Ti contents. Main damaging micromechanisms in hot dip zinc coated ipersandelin steel specimens were investigated by means of bending tests. Longitudinal sections of bended specimens were observed by means of a LOM (Light Optical Microscope: main damage micromechanisms were identified as longitudinal and radial cracks.

  13. Contribution to the determination of priority constructive influences on the hot crack initiation of welded components; Beitrag zur Ermittlung vorrangig konstruktiver Einflussgroessen auf die Heissrissinitiierung an geschweissten Bauteilen

    Energy Technology Data Exchange (ETDEWEB)

    Gollnow, Christian

    2015-07-01

    The previous research results do not allow a general hot crack characterisation although a variety of experimental and numerical knowledge is available. The reason for this is mainly the large number of influencing factors that complicate a complete description of the hot cracking phenomenon and especially solidification cracking. The hot crack formation and thus the solidification crack initiation can be described by the interaction of process, metallurgy and design. However, the literature examination shows that in the solidifaction crack characterisation the influence of the design aspect is often underestimated. The pre-stresses of the structural components is up to now not considered as an essential cause for the formation of solidification cracks. The evaluation of the influence of the various parameters is presented partly inconsistent. In addition, the targeted presentation of the design influence with respect to the solidification cracks in the weld is because the limited transferability of the various component-specific stresses on a laboratory scale and thus to the respective hot cracking tests restricted. Hence, the difficulty to transfer the results between laboratory specimen and component as well as the general hot crack characterisation is given. In this work the different types of stresses from the component welding in the laboratory and to quantify experimentally the solidification crack critical values, displacements and displacement rates were detected. In this regard external loaded hot cracking tests were carried out by using the advantages of contactless measurement techniques close to the weld and to analyse the welding process with respect to various local and global design-specific factors influencing the formation of solidification cracks in high alloyed steel. These investigations were performed on austenitic (1.4828) and ferritic (1.4509) materials with different mechanical and technological properties. To reflect the praxis relevant

  14. Standard practice for determining cracking susceptibility of metals exposed under stress to a hot salt environment

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    1990-01-01

    1.1 This practice covers procedures for testing metals for embrittlement and cracking susceptibility when exposed under stress to a hot salt environment. This practice can be used for testing all metals for which service conditions dictate the need for such information. The test procedures described herein are generally applicable to all metal alloys; required adjustments in environmental variables (temperature, stress) to characterize a given materials system should be made. This practice describes the environmental conditions and degree of control required, and suggests means for obtaining this desired control. 1.2 This practice can be used both for alloy screening for determination of relative susceptibility to embrittlement and cracking, and for the determination of time-temperature-stress threshold levels for onset of embrittlement and cracking. However, certain specimen types are more suitable for each of these two types of characterizations. Note 1 This practice relates solely to the performance of ...

  15. Study of Hot Salt Stress Corrosion Crack Initiation of Alloy IMI 834 by using DC Potential Drop Method

    Energy Technology Data Exchange (ETDEWEB)

    Pustode, Mangesh D. [Bharat Forge Ltd., Pune (India); Dewangan, Bhupendra [Tata Steel, Jamshedpur (India); Raja, V. S. [Indian Institute of Technology Bombay, Mumbai (India); Paulose, Neeta; Babu, Narendra [Gas Turbine Research Establishment (GTRE), Bangalore (India)

    2016-10-15

    DC potential drop technique was employed during the slow strain rate tests to study the hot salt stress corrosion crack (HSSCC) initiation at 300 and 400 ℃. Threshold stresses for HSSCC initiation were found to about 88 % of the yield strength at both temperatures, but the time from crack initiation to final failure (Δtscc) decreased significantly with temperature, which reflects larger tendency for brittle fracture and secondary cracking. The brittle fracture features consisted of transgranular cracking through the primary α grain and discontinuous faceted cracking through the transformed β grains.

  16. Description of the initiation and progress of cracks for hot cracks in temperature resistant 1% CrMoV castings under creep or fatigue stress

    International Nuclear Information System (INIS)

    Bareiss, J.; Maile, K.; Berger, C.; Mayer, K.H.; Weiss, M.

    1994-01-01

    The results available so far have shown that under vibration stress at room temperature and at 530 C, the simplified equations of fracture mechanics are sufficient (in spite of the complicated fault geometries), in order to conservatively describe the behaviour of fault positions (open or partly-healed hot cracks) with regard to their crack initiation behaviour if combined with the findings US test technique. Here the sample castings which in the initial state showed fault indications of US type EET near the surface, tend to earlier initiation of a crack compared to lower fault positions of the samples. Internal fault positions (partially healed hot cracks) often only showed local cracks (trans-crystalline deformation cracks) within the fault area with an order of magnitude of about 10-50 μm, in spite of exceeding the threshold value Δ Ko. The comparison of the crack propagation behaviour of the sample castings, determined via the potential sensor method on medium lengths of fault with the results of crack growth of fracture mechanics samples in the da/dN- Δ K diagram showed for the evaluated sample castings with a relatively great initial depth or length of fault that the upper scatter band limit of the Paris Law determined for the material can be used to estimate the fault position behaviour. (orig./RHM) [de

  17. Net-shape and crack-free production of Nd–Fe–B magnets by hot deformation

    Energy Technology Data Exchange (ETDEWEB)

    Dirba, I., E-mail: dirba@fm.tu-darmstadt.de [Technische Universität Darmstadt, Materialwissenschaft, Alarich-Weiß-Str. 16, 64287 Darmstadt (Germany); IFW Dresden, Institute for Metallic Materials, P.O. Box 270116, 01171 Dresden (Germany); Sawatzki, S. [Technische Universität Darmstadt, Materialwissenschaft, Alarich-Weiß-Str. 16, 64287 Darmstadt (Germany); IFW Dresden, Institute for Metallic Materials, P.O. Box 270116, 01171 Dresden (Germany); Gutfleisch, O. [Technische Universität Darmstadt, Materialwissenschaft, Alarich-Weiß-Str. 16, 64287 Darmstadt (Germany)

    2014-03-15

    In order to reduce the amount of material waste and therefore to use the precious rare earth element Nd in a more efficient way, routes for the production of crack-free hot-deformed nanocrystalline Nd–Fe–B magnets (using melt-spun ribbons as a precursor) have been investigated. In contrast to the conventional route in which material flows into a cavity, pressing tool has been used in order to exert a back pressure during backward extrusion, leading to crack-free and net-shape production of radially oriented ring magnets, without detrimental influence on magnetic properties. Micrographs demonstrate overall good alignment of elongated platelet shaped grains with radially oriented c-axis in most parts of the ring. A mean remanence J{sub r} = 1.27 T and coercivity μ{sub 0i}H{sub c} = 1.5 T has been obtained. Degree of texture reaches around 0.7. Furthermore, die-upsetting has been performed for different degrees of deformation to obtain crack-free, mechanically and magnetically homogenous, axially oriented tablet magnets.

  18. Permeability and elastic properties of cracked glass under pressure

    Science.gov (United States)

    Ougier-Simonin, A.; GuéGuen, Y.; Fortin, J.; Schubnel, A.; Bouyer, F.

    2011-07-01

    Fluid flow in rocks is allowed through networks of cracks and fractures at all scales. In fact, cracks are of high importance in various applications ranging from rock elastic and transport properties to nuclear waste disposal. The present work aims at investigating thermomechanical cracking effects on elastic wave velocities, mechanical strength, and permeability of cracked glass under pressure. We performed the experiments on a triaxial cell at room temperature which allows for independent controls of the confining pressure, the axial stress, and pore pressure. We produced cracks in original borosilicate glass samples with a reproducible method (thermal treatment with a thermal shock of 300°C). The evolution of the elastic and transport properties have been monitored using elastic wave velocity sensors, strain gage, and flow measurements. The results obtained evidence for (1) a crack family with identified average aspect ratio and crack aperture, (2) a very small permeability which decreases as a power (exponential) function of pressure, and depends on (3) the crack aperture cube. We also show that permeability behavior of a cracked elastic brittle solid is reversible and independent of the fluid nature. Two independent methods (permeability and elastic wave velocity measurements) give these consistent results. This study provides data on the mechanical and transport properties of an almost ideal elastic brittle solid in which a crack population has been introduced. Comparisons with similar data on rocks allow for drawing interesting conclusions. Over the timescale of our experiments, our results do not provide any data on stress corrosion, which should be considered in further study.

  19. Properties of hot rolled steels for enamelling

    International Nuclear Information System (INIS)

    Gavrilovski, Dragica; Gavrilovski, Milorad

    2003-01-01

    The results of an investigation of the structure and properties of experimental produced hot rolled steels suitable for enamelling are presented in the paper. Hot rolled steels for enamelling represent a special group of the steels for conventional enamelling. Their quality has to be adapted to the method and conditions of enamelling. Therefore, these steels should meet some specific requirements. In addition to usual investigation of the chemical composition and mechanical properties, microstructure and quality of the steel surface also were investigated. The basic aim was to examine steels capability for enamelling, i. e. steels resistance to the fish scales phenomena, by trial enamelling, as well as quality of the steel - enamel contact surface, to evaluate the binding. Also, the changes of the mechanical properties, especially the yield point, during thermal treatment, as a very specific requirement, were investigated, by simplified method. Good results were obtained confirming the steels capability for enamelling. (Original)

  20. Effect of segregations on mechanical properties and crack propagation in spring steel

    Directory of Open Access Journals (Sweden)

    B. Žužek

    2015-10-01

    Full Text Available Considerable efforts have been made over the last decades to improve performance of spring steels, which would increase the service time of springs and also allow vehicles weight reduction. There are different possibilities of improving properties of spring steels, from modifying the chemical composition of steels to optimizing the deformation process and changing the heat treatment parameters. Another way of improving steel properties is through refining the microstructure and reducing amount of inclusions. Therefore, the focus of the current investigation was to determine the effect of more uniform and cleaner microstructure obtained through electro-slag remelting (ESR of steel on the mechanical and dynamic properties of spring steel, with special focus on the resistance to fatigue crack propagation. Effect of the microstructure refinement was evaluated in terms of tensile strength, elongation, fracture and impact toughness, and fatigue resistance under bending and tensile loading. After the mechanical tests the fracture surfaces of samples were analyzed using scanning electron microscope (SEM and the influence of microstructure properties on the crack propagation and crack propagation resistance was studied. Investigation was performed on hot rolled, soft annealed and vacuum heat treated 51CrV4 spring steel produced by conventional continuous casting and compared with steel additional refined through ESR. Results shows that elimination of segregations and microstructure refinement using additional ESR process gives some improvement in terms of better repeatability and reduced scattering, but on the other hand it has negative effect on crack propagation resistance and fatigue properties of the spring steel.

  1. A study on the mechanism of stress corrosion cracking of duplex stainless steels in hot alkaline-sulfide solution

    Science.gov (United States)

    Chasse, Kevin Robert

    Duplex stainless steels (DSS) generally have superior strength and corrosion resistance as compared to most standard austenitic and ferritic stainless grades owing to a balanced microstructure of austenite and ferrite. As a result of having favorable properties, DSS have been selected for the construction of equipment in pulp and paper, chemical processing, nuclear, oil and gas as well as other industries. The use of DSS has been restricted in some cases because of stress corrosion cracking (SCC), which can initiate and grow in either the ferrite or austenite phase depending on the environment. Thorough understanding of SCC mechanisms of DSS in chloride- and hydrogen sulfide-containing solutions has been useful for material selection in many environments. However, understanding of SCC mechanisms of DSS in sulfide-containing caustic solutions is limited, which has restricted the capacity to optimize process and equipment design in pulp and paper environments. Process environments may contain different concentrations of hydroxide, sulfide, and chloride, altering corrosion and SCC susceptibility of each phase. Crack initiation and growth behavior will also change depending on the relative phase distribution and properties of austenite and ferrite. The role of microstructure and environment on the SCC of standard grade UNS S32205 and lean grade UNS S32101 in hot alkaline-sulfide solution were evaluated in this work using electrochemical, film characterization, mechanical testing, X-ray diffraction, and microscopy techniques. Microstructural aspects, which included residual stress state, phase distribution, phase ratio, and microhardness, were related to the propensity for SCC crack initiation in different simulated alkaline pulping liquors at 170 °C. Other grades of DSS and reference austenitic and superferritic grades of stainless steel were studied using exposure coupons for comparison to understand compositional effects and individual phase susceptibility

  2. Properties of hot pressed MgB2/Ti tapes

    International Nuclear Information System (INIS)

    Kovac, P.; Husek, I.; Melisek, T.; Fedor, J.; Cambel, V.; Morawski, A.; Kario, A.

    2009-01-01

    Hot axial and hot isostatic pressing was applied for single-core MgB 2 /Ti tapes. Differences in transport current density, n-exponents and critical current anisotropy are discussed and related to the grain connectivity influenced by pressing. The magnetic Hall probe scanning measurements allowed observing the isolated regions for axially hot pressed sample attributed to the longitudinally oriented cracks introduced by pressing. The highest current densities were measured for the tape subjected to hot isostatic pressing due to improved connectivity.

  3. Crack

    Science.gov (United States)

    ... spending time in a rehab facility or getting cognitive-behavioral therapy or other treatments. Right now, there are no medicines to treat a crack addiction. If you smoke crack, talking with a counselor ...

  4. The development of crack measurement system using the direct current potential drop method for use in the hot cell

    International Nuclear Information System (INIS)

    Kim, Do-Sik; Ahn, Sang-Bok; Lee, Key-Soon; Kim, Yong-Suk; Kwon, Sang-Chul

    1999-01-01

    The crack length measurement system using the direct current potential drop (DCPD) method was developed for the detection of crack growth initiation and subsequent crack growth. The experimental precautions and data processing procedure required for its application were also described find discussed. The system presented herein was specially built for use in fracture toughness testing of unirradiated or irradiated pressure tube materials from nuclear reactor. The application of this system for fracture toughness determination was illustrated from the test of curved compact tension specimens removed from CANDU reactor pressure tubes. The crack extension was monitored using the DCPD method. It is found that the changes of the potential drop and the changes of the crack length have a linear relationship. The final crack front was marked by heat-tinting after the test and the specimen broken open for determination of the initial and final physical crack length. The physical crack lengths, obtained by the 9-point average method described in ASTM E1737-96 on heat-tinted fracture surface, were used to calibrate the DCPD method for each test on an individual basis by matching the change in voltage to the crack extension. It is found that this system can be recommended for determination of the J-integral resistance (J-R) curve of unirradiated or irradiation materials in the hot cell, especially when testing at elevated temperature and in the environment chamber or furnace. (author)

  5. Quantitative influence of minor and impurity elements on hot cracking susceptibility of extra high-purity type 310 stainless steel

    International Nuclear Information System (INIS)

    Saida, Kazuyoshi; Matsushita, Hideki; Nishimoto, Kazutoshi; Kiuchi, Kiyoshi; Nakayama, Junpei

    2013-01-01

    To evaluate the influence of minor and impurity elements such as C, Mn, P and S on the solidification and ductility-dip cracking susceptibilities of extra high-purity type 310 stainless steels, the transverse-Varestraint test was conducted by using several type 310 stainless steels with different amounts of C, Mn, P and S. Two types of hot cracks occurred in these steels by Varestraint test; solidification and ductility-dip cracks. The solidification cracking susceptibility was significantly reduced as the amounts of C, P and S decreased. The ductility-dip cracking susceptibility also reduced with a decrease in P and S contents. It adversely, however, increased as the C content of the steels was reduced. Mn didn't greatly affect the hot cracking susceptibility of the extra high-purity steels. The characteristic influence on solidification cracking was the ratio of P:S:C=1:1.3:0.56, while Mn negligibly ameliorated solidification cracking in the extra low S (and P) steels. The numerical analysis on the solidification brittle temperature range (BTR) revealed that the reduced solidification cracking susceptibility with decreasing the amounts of C, P and S in steel could be attributed to the reduced BTR due to the suppression of solidification segregation of minor and impurity elements in the finally solidified liquid film between dendrites. On the other hand, a molecular orbital analysis to estimate the binding strength of the grain boundary suggested that the increased ductility-dip cracking susceptibility in extra high-purity steels was caused by grain boundary embrittlement due to the refining of beneficial elements for grain boundary strengthening such as C. (author)

  6. Assessment of The Cracking Properties of Stainless Steel Alloys and their Usability for Laser Welding in Production

    DEFF Research Database (Denmark)

    Juhl, Thomas Winther

    2001-01-01

    Methods to assess stainless steel alloys’ cracking properties and usability for laser welding has been studied. Also tests to assess alloys’ susceptibility to hot cracking has been conducted. Among these is the so-called Weeter test which assesses the alloy by executing a number of spot welds...... to provoke cracking in the alloy. In this work the Weeter test has been modified and changed in order to develop a faster and easier test also applicable to small specimens. The new test, called a Groove test differs from the Weeter test by its procedure in which linear seam welds are conducted instead...... of spot welds. The Groove test has the advantage of an easier microscopy and analysis in the welds. Results from crack tests was partly confirmed by predictions made on the basis of the alloy’s constituents and solidification growth rate....

  7. The effects of zirconium and carbon on the hot cracking resistance of iron aluminides. Topical report

    Energy Technology Data Exchange (ETDEWEB)

    Mulac, B.L.; Edwards, G.R. [Colorado School of Mines, Golden, CO (United States). Dept. of Metallurgical and Materials Engineering; David, S.A. [Oak Ridge National Lab., TN (United States)

    1998-02-01

    Iron aluminides have been of interest for about 60 years because of their good high temperature strengths (below 600{degrees}C) and excellent oxidation and sulfidation resistance, as well as their relatively low cost and conservation of strategic elements. These advantageous properties have driven the development of iron aluminides as potential structural materials. However, the industrial application of iron aluminides has been inhibited because of a sharp reduction in strength at temperatures higher than 600{degrees}C and low ductility at ambient temperatures due to hydrogen embrittlement. Oak Ridge National Laboratory has shown in recent years that room temperature properties of alloys containing 28% Al (all compositions are in atomic percent unless otherwise noted) can be improved through thermomechanical processing and alloying. Iron aluminides must have good weldability if they are to be used as structural materials. A coarse fusion zone microstructure is formed when iron aluminides are welded, increasing their susceptibility to cold cracking in water vapor. A recent study at Colorado School of Mines has shown that refining the fusion zone microstructure by weld pool oscillation effectively reduces cold cracking. Weld pool inoculation has been shown to refine fusion zone microstructures, but coarse carbide distribution caused this approach to reducing cold cracking to be ineffective.

  8. Anomalous properties of hot dense nonequilibrium plasmas

    International Nuclear Information System (INIS)

    Ferrante, G; Zarcone, M; Uryupin, S A

    2005-01-01

    A concise overview of a number of anomalous properties of hot dense nonequilibrium plasmas is given. The possibility of quasistationary megagauss magnetic field generation due to Weibel instability is discussed for plasmas created in atom tunnel ionization. The collisionless absorption and reflection of a test electromagnetic wave normally impinging on the plasma with two-temperature bi-maxwellian electron velocity distribution function are studied. Due to the wave magnetic field influence on the electron kinetics in the skin layer the wave absorption and reflection significantly depend on the degree of the electron temperature anisotropy. The linearly polarized impinging wave during reflection transforms into an elliptically polarized one. The problem of transmission of an ultrashort laser pulse through a layer of dense plasma, formed as a result of ionization of a thin foil, is considered. It is shown that the strong photoelectron distribution anisotropy yields an anomalous penetration of the wave field through the foil

  9. Microstructure Evolution and Surface Cracking Behavior of Superheavy Forgings during Hot Forging

    Directory of Open Access Journals (Sweden)

    Zhenhua Wang

    2018-01-01

    Full Text Available In recent years, superheavy forgings that are manufactured from 600 t grade ingots have been applied in the latest generation of nuclear power plants to provide good safety. However, component production is pushing the limits of the current free-forging industry. Large initial grain sizes and a low strain rate are the main factors that contribute to the deformation of superheavy forgings during forging. In this study, 18Mn18Cr0.6N steel with a coarse grain structure was selected as a model material. Hot compression and hot tension tests were conducted at a strain rate of 10−4·s−1. The essential nucleation mechanism of the dynamic recrystallization involved low-angle grain boundary formation and subgrain rotation, which was independent of the original high-angle grain boundary bulging and the presence of twins. Twins were formed during the growth of dynamic recrystallization grains. The grain refinement was not obvious at 1150°C. A lowering of the deformation temperature to 1050°C resulted in a fine grain structure; however, the stress increased significantly. Crack-propagation paths included high-angle grain boundaries, twin boundaries, and the insides of grains, in that order. For superheavy forging, the ingot should have a larger height and a smaller diameter.

  10. Hot Rolling Scrap Reduction through Edge Cracking and Surface Defects Control

    Energy Technology Data Exchange (ETDEWEB)

    Beaudoin, Armand [Univ. of Illinois, Urbana-Champaign, IL (United States)

    2016-05-29

    The design of future aircraft must address the combined demands for fuel efficiency, reduced emissions and lower operating costs. One contribution to these goals is weight savings through the development of new alloys and design techniques for airframe structures. This research contributes to the light-weighting through fabrication of monolithic components from advanced aluminum alloys by making a link between alloy processing history and in-service performance. Specifically, this research demonstrates the link between growing cracks with features of the alloy microstructure that follow from thermo-mechanical processing. This is achieved through a computer model of crack deviation. The model is validated against experimental data from production scale aluminum alloy plate, and demonstration of the effect of changes in processing history on crack growth is made. The model is cast in the open-source finite element code WARP3D, which is freely downloadable and well documented. This project provides benefit along several avenues. First, the technical contribution of the computer model offers the materials engineer a critical means of providing guidance both upstream, to process tuning to achieve optimal properties, and downstream, to enhance fault tolerance. Beyond the fuel savings and emissions reduction inherent in the light-weighting of aircraft structures, improved fault tolerance addresses demands for longer inspection intervals over baseline, and a lower life cycle cost.

  11. Effect of copper, tin, phosphorous and arsenic on the surface cracking of a 18-8 stainless steel during hot compression tests

    International Nuclear Information System (INIS)

    Botella, J.; Fernandez, M.T.; Fernandez de Castillo, I.

    1998-01-01

    The effect of certain different concentrations of Cu, Sn, P and As on the surface cracking of 18-8 austenitic stainless steel hot compressed specimens has been studied, at 1,123 and 1,273 K, in an oxidizing atmosphere (air). A procedure for determining surface cracking has been established, and the cracking factor obtained in this ways is correlated with the chemical composition of the materials at both temperatures. The cracking factors obtained at 1,273 K have been compared with the reduction of area drops obtained by hot tension tests at the same temperature. (Author) 5 refs

  12. Problems of procedure for studying crack resistance

    International Nuclear Information System (INIS)

    Babak, A.V.; Uskov, E.I.

    1984-01-01

    Procedures are developed for studying crack resistance in sintered hot-worked tungsten within 20-2200 deg C. Certain structural properties of the installation for studying high-temperature crack resistance of tungsten are considered. Technological peculiarities of eccentric tensile strength of tungsten specimens and methodical peculiarities of initjation and fixation of initial cracks in specimens of different tungsten alloys are studied

  13. Welding hot cracking in an austenitic stainless steel; Fissuration a chaud en soudage d'un acier inoxydable austenitique

    Energy Technology Data Exchange (ETDEWEB)

    Kerrouault, N

    2001-07-01

    The occurrence of hot cracking is linked to several conditions, in particular, the composition of the material and the local strains due to clambering. The aim of this study is to better analyse the implied mechanisms and to lead to a local thermomechanical criterion for hot cracking. The example studied is an AISI 321-type stainless steel (X10CrNiTi18-12) strongly prone to cracking. Two weldability tests are studied: - the first one consists in carrying out a fusion line by the TIG process on a thin sheet. In the case of the defect occurrence, the crack is longitudinal and follows the back of the molten bath. The influence of the operating conditions welding (speed, welding heat input, width test sample) is studied. - the second one is the Varestraint test. It is widely used to evaluate the sensitivity of a material to hot cracking. It consists in loading the material by bending during a fusion line by the TIG process and in characterising the defects quantity (length, number). Various thermal and mechanical instrumentation methods were used. The possibilities of a local instrumentation instrumentation being limited because of the melting, the experimental results were complemented by a numerical modelling whose aim is to simulate the thermomechanical evolution of the loading thanks to the finite element analysis code ABAQUS. First, the heat input for thermal simulation is set by the use of an inverse method in order to optimise the energy deposit mode during welding in the calculation. Then, the mechanical simulation needs the input of a constitutive law that fits the mechanical behaviour over a wide temperature range from ambient to melting temperature. Thus, a mechanical characterization is performed by selecting strain values and strain rates representative of what the material undergoes during the tests. The results come from tensile and compressive tests and allow to settle an elasto-visco-plastic constitutive law over temperatures up to liquidus. Once

  14. Layer texture of hot-rolled BCC metals and its significance for stress-corrosion cracking of main gas pipelines

    Science.gov (United States)

    Perlovich, Yu. A.; Isaenkova, M. G.; Krymskaya, O. A.; Morozov, N. S.

    2016-10-01

    Based on data of X-ray texture analysis of hot-rolled BCC materials it was shown that the layerwise texture inhomogeneity of products is formed during their manufacturing. The effect can be explained by saturation with interstitial impurities of the surface layer, resulting in dynamical deformation aging (DDA). DDA prevents the dislocation slip under rolling and leads to an increase of lattice parameters in the external layer. The degree of arising inhomogeneity correlates with the tendency of hot-rolled sheets and obtained therefrom tubes to stress-corrosion cracking under exploitation, since internal layers have a compressive effect on external layers, and prevents opening of corrosion cracks at the tube surface.

  15. Transport properties of hot gluonic matter

    CERN Document Server

    Bluhm, Marcus

    2012-01-01

    We discuss the temperature dependence of the scaled jet quenching parameter of hot gluonic matter within a quasiparticle approach. A pronounced maximum in the vicinity of the transition temperature is observed, where the ratio of the scaled jet quenching parameter and the inverse specific shear viscosity increases above typical values for weakly coupled systems.

  16. Structure and properties of hot-pressed boron carbide ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Koval' chenko, M S; Tkachenko, IU G; Koval' chuk, V V; Iurchenko, D Z; Satanin, S V [Institut Problem Materialovedeniia, Kiev (Ukrainian SSR)

    1990-07-01

    The microstructure and strength of B4C-TiB2-TiO{sub 2} ceramics samples, hot-compacted from a mixture of two types of B4C-TiO2-C powder, are examined. The two types are obtained by combining boric acid with either sucrose or carbon black. The grain-sizes of the two powders are found to be distinctly different from one another both before and after the grinding procedure and the degree of dispersion is not high. The strength tests show 600 MPa, the Vicker's hardness is 34.5 GPa, and the crack resistance coefficient of ceramics containing 15 percent TiB2 by mass is 5 MPa m exp 1/2. The use of soluble boron carbide powder helps achieve higher levels of strength and crack resistance. 5 refs.

  17. Crack propagation studies and bond coat properties in thermal

    Indian Academy of Sciences (India)

    High threshold load at the interface between the ceramic layer and the bond coat was required to propagate the crack further into the bond coat. Once the threshold load was surpassed the crack propagated into the brittle bond coat without an appreciable increase in the load. At temperatures of 800°C the crack propagated ...

  18. Considering the edge-crack sensitivity of a hot-rolled steel in forming simulation

    Science.gov (United States)

    Gläsner, T.; Schneider, M.; Troitzsch, M.; Westhäuser, S.

    2016-11-01

    The formability of sheet metal materials is locally reduced by shear cutting operations, and as a result the risk of a crack during further processing is increased at the edge. Materials particularly susceptible to this are described as sensitive to edge-cracking. A procedure for quantitatively determining edge-crack sensitivity and for applying corresponding characteristic values has not been previously established. Below, two test methods and an approach for using the results in an extended forming limit diagram are presented. The producibility of a collar drawn test component as well as a chassis component is reevaluated using this extended forming limit diagram.

  19. On the hot cracking susceptibility of a semisolid aluminium 6061 weld: Application of a coupled solidification- thermomechanical model

    International Nuclear Information System (INIS)

    Rajani, H R Zareie; Phillion, A B

    2015-01-01

    A coupled solidification-thermomechanical model is presented that investigates the hot tearing susceptibility of an aluminium 6061 semisolid weld. Two key phenomena are considered: excessive deformation of the semisolid weld, initiating a hot tear, and the ability of the semisolid weld to heal the hot tear by circulation of the molten metal. The model consists of two major modules: weld solidification and thermomechanical analysis. 1) By means of a multi-scale model of solidification, the microstructural evolution of the semisolid weld is simulated in 3D. The semisolid structure, which varies as a function of welding parameters, is composed of solidifying grains and a network of micro liquid channels. The weld solidification module is utilized to obtain the solidification shrinkage. The size of the micro liquid channels is used as an indicator to assess the healing ability of the semisolid weld. 2) Using the finite element method, the mechanical interaction between the weld pool and the base metal is simulated to capture the transient force field deforming the semisolid weld. Thermomechanical stresses and shrinkage stresses are both considered in the analysis; the solidification contractions are extracted from the weld solidification module and applied to the deformation simulation as boundary conditions. Such an analysis enables characterization of the potential for excessive deformation of the weld. The outputs of the model are used to study the effect of welding parameters including welding current and speed, and also welding constraint on the hot cracking susceptibility of an aluminium alloy 6061 semisolid weld. (paper)

  20. Fabrication and properties of hot pressed bismuth tungstate

    International Nuclear Information System (INIS)

    Streicher, W.L.

    1978-01-01

    Bi 2 WO 6 is a synthetic polar material that is a possible candidate for energy conversion and detection systems. Previous research on this material has been concerned with crystal growth and sintering characteristics of polycrystalline compacts. This study involves itself with the fabrication of polycrystalline compacts by hot pressing techniques. Densities approaching theoretical crystal density were achieved by hot pressing at 850 0 C for one hour with pressures exceeding 35 MPa. Before hot pressing, the sintering range was determined by high temperature dilatometry of unfired Bi 2 WO 6 ceramics. Hot pressed discs were characterized by scanning electron microscopy, differential scanning calorimetry, and x-ray diffraction. Electrical properties were determined by dc resistivity, capacitance, and conductance measurements, ac poling, dc poling, and current-voltage measurements

  1. Effects of Niobium Microalloying on Microstructure and Properties of Hot-Dip Galvanized Sheet

    Energy Technology Data Exchange (ETDEWEB)

    Mohrbacher, Hardy [NiobelCon bvba, Brussels (Belgium)

    2010-04-15

    Niobium microalloying is effective in hot-rolled and cold-rolled steels by providing a fine-grained microstructure resulting in increased strength. To optimize the strengthening effect, alloy design and hot-rolling conditions have to be adapted. As a key issue the dissolution and precipitation characteristics of Nb are discussed in particular with regard to the run-out table conditions. It is then considered how the hot-rolled microstructure and the solute state of Nb interact with the hot-dip galvanizing cycle. The adjusted conditions allow controlling the morphology and distribution of phases in the cold-rolled annealed material. Additional precipitation hardening can be achieved as well. The derived options can be readily applied to produce conventional HSLA and IF high strength steels as well as to modem multiphase steels. It will be explained how important application properties such as strength, elongation, bendability, weldability and delayed cracking resistance can be influenced in a controlled and favorable way. Examples of practical relevance and experience are given.

  2. Numerical Analysis of Hot Cracking in Laser-Hybrid Welded Tubes

    Directory of Open Access Journals (Sweden)

    Moritz Oliver Gebhardt

    2013-01-01

    Full Text Available In welding experiments conducted on heavy wall pipes, the penetration mode (full or partial penetration occurred to be a significant factor influencing appearance of solidification cracks. To explain the observed phenomena and support further optimization of manufacturing processes, a computational model was developed, which used a sophisticated strategy to model the material. High stresses emerged in the models in regions which showed cracking during experiments. In partial penetration welding, they were caused by the prevention of weld shrinkage due to the cold and strong material below the joint. Another identified factor having an influence on high stress localization is bulging of the weld.

  3. Heat Treatment Optimization and Properties Correlation for H11-Type Hot-Work Tool Steel

    Science.gov (United States)

    Podgornik, B.; Puš, G.; Žužek, B.; Leskovšek, V.; Godec, M.

    2018-02-01

    The aim of this research was to determine the effect of vacuum-heat-treatment process parameters on the material properties and their correlations for low-Si-content AISI H11-type hot-work tool steel using a single Circumferentially Notched and fatigue Pre-cracked Tensile Bar (CNPTB) test specimen. The work was also focused on the potential of the proposed approach for designing advanced tempering diagrams and optimizing the vacuum heat treatment and design of forming tools. The results show that the CNPTB specimen allows a simultaneous determination and correlation of multiple properties for hot-work tool steels, with the compression and bending strength both increasing with hardness, and the strain-hardening exponent and bending strain increasing with the fracture toughness. On the other hand, the best machinability and surface quality of the hardened hot-work tool steel are obtained for hardness values between 46 and 50 HRC and a fracture toughness below 60 MPa√m.

  4. Effect of Cr, Ni, and Mo additions on the susceptibility of the 0Kh6n7m7c steel to hot cracking

    International Nuclear Information System (INIS)

    Tolstykh, L.G.; Pryakhin, A.V.; Popov, A.N.; Usynin, V.F.

    1977-01-01

    The effect of chromium, molybdenum, and nickel on the tendency of surfacing materials to form hot cracks (Vsub(kp) was studied using the mathematical statistics method. The St3 steel and 38KhN3MFA steel were used in the study. A device facilitating the hot cracking tendency test procedure was developed. It was found that, in the concentration range involved, Ni and Mo produce no effect on Vsub(kp), and Cr enhances it. A new powder wire, PP-OKh7N8M6S, capable of increasing surface material resistance by 1.5-2 times, has been developed

  5. Effect of microstructural anisotropy on fracture toughness of hot rolled 13Cr ODS steel - The role of primary and secondary cracking

    Science.gov (United States)

    Das, A.; Viehrig, H. W.; Bergner, F.; Heintze, C.; Altstadt, E.; Hoffmann, J.

    2017-08-01

    ODS steels have been known to exhibit anisotropic fracture behaviour and form secondary cracks. In this work, the factors responsible for the anisotropic fracture behaviour have been investigated using scanning electron microscopy and electron backscatter microscopy. Fracture toughness of hot rolled 13Cr ODS steel was determined using unloading compliance method for L-T and T-L orientations at various temperatures. L-T orientation had higher fracture toughness than T-L orientation and also contained more pronounced secondary cracking. Secondary cracks appeared at lower loads than primary cracks in both orientations. Primary crack propagation was found to be preferentially through fine grains in a bimodal microstructure. Grains were aligned and elongated the most towards rolling direction followed by T and S directions resulting in fracture anisotropy. Crystallographic texture and preferential alignment of Ti enriched particles parallel to rolling direction also contributed towards fracture anisotropy.

  6. Test Method Variability in Slow Crack Growth Properties of Sealing Glasses

    Science.gov (United States)

    Salem, J. A.; Tandon, R.

    2010-01-01

    The crack growth properties of several sealing glasses were measured by using constant stress rate testing in 2 and 95 percent RH (relative humidity). Crack growth parameters measured in high humidity are systematically smaller (n and B) than those measured in low humidity, and crack velocities for dry environments are 100x lower than for wet environments. The crack velocity is very sensitive to small changes in RH at low RH. Biaxial and uniaxial stress states produced similar parameters. Confidence intervals on crack growth parameters that were estimated from propagation of errors solutions were comparable to those from Monte Carlo simulation. Use of scratch-like and indentation flaws produced similar crack growth parameters when residual stresses were considered.

  7. Crack path predictions and experiments in plane structures considering anisotropic properties and material interfaces

    Directory of Open Access Journals (Sweden)

    P.O. Judt

    2015-10-01

    Full Text Available In many engineering applications special requirements are directed to a material's fracture behavior and the prediction of crack paths. Especially if the material exhibits anisotropic elastic properties or fracture toughnesses, e.g. in textured or composite materials, the simulation of crack paths is challenging. Here, the application of path independent interaction integrals (I-integrals, J-, L- and M-integrals is beneficial for an accurate crack tip loading analysis. Numerical tools for the calculation of loading quantities using these path-invariant integrals are implemented into the commercial finite element (FE-code ABAQUS. Global approaches of the integrals are convenient considering crack tips approaching other crack faces, internal boundaries or material interfaces. Curved crack faces require special treatment with respect to integration contours. Numerical crack paths are predicted based on FE calculations of the boundary value problem in connection with an intelligent adaptive re-meshing algorithm. Considering fracture toughness anisotropy and accounting for inelastic effects due to small plastic zones in the crack tip region, the numerically predicted crack paths of different types of specimens with material interfaces and internal boundaries are compared to subcritically grown paths obtained from experiments.

  8. Microstructure and mechanical properties of internal crack healing in a low carbon steel

    Energy Technology Data Exchange (ETDEWEB)

    Xin, Ruishan [Department of Mechanical Engineering, Tsinghua University, Beijing 100084 (China); Key Laboratory for Advanced Materials Processing Technology of Ministry of Education, Tsinghua University, Beijing 100084 (China); Ma, Qingxian, E-mail: maqxdme@mail.tsinghua.edu.cn [Department of Mechanical Engineering, Tsinghua University, Beijing 100084 (China); Key Laboratory for Advanced Materials Processing Technology of Ministry of Education, Tsinghua University, Beijing 100084 (China); Li, Weiqi [Department of Mechanical Engineering, Tsinghua University, Beijing 100084 (China); Key Laboratory for Advanced Materials Processing Technology of Ministry of Education, Tsinghua University, Beijing 100084 (China)

    2016-04-26

    The behavior of internal crack healing in a low carbon steel at elevated temperatures was investigated. The internal cracks were introduced into low carbon steel samples via the drilling and compression method. The microstructure of crack healing zone was observed using optical microscopy and scanning electron microscopy. The mechanical properties of crack healing zone at room temperature were tested. The results show that there are two mechanisms of crack healing in the low carbon steel. Crack healing is caused by atomic diffusion at lower temperatures, and mainly depends on recrystallization and grain growth at higher temperatures. The microstructural evolution of crack healing zone can be divided into four stages, and the fracture morphology of crack healing zone can be classified into five stages. At the initial healing stage, the fracture exhibits brittle or low ductile dimple fracture. The ultimate fracture mode is dimple and quasi-cleavage mixed fracture. Fine grain microstructures improve the ultimate tensile strength of crack healing zone, which is even higher than that of the matrix. The strength recovery rate is higher than that of the plasticity.

  9. The causes of relaxation- and hot cracking in the heat-affected zone of 22 NiMoCr 37 and 20 MnMoNi 55

    International Nuclear Information System (INIS)

    Schellhammer, W.

    1977-01-01

    Non-destructive and metallographic investigations with a view to relaxation cracking and hot cracking were carried out in 53 component-specific welds with wall thicknesses of 40 to 360 mm and 21 experimental welds with wall thicknesses of 140 to 275 mm of high-temperature, fine-grained structural steel 22 NiMoCr 37 as well as in 27 component-specific welds of high-strength, fine-grained structural steel 20 MnMoNi 55. Non-destructive tests and conventional metallographic analyses by means of transverse structure micrography were unable to give a sufficiently accurate picture of the two types of cracks in the micro- and millimeter range, a 'volumetric' method was employed (tangential structure micrography with stepwise abrasion) which permitted semi-automatic and fast evaluation. The experimental results showed the selective influence of several elements and led to the development of a method to evaluate the cumulative effect of the chemical elements on relaxation cracking and hot cracking by addition of the selective influence. The method gives quantitative data on material optimisation with regard to the reduction of brittle and crack-prone states and confirms the findings of welding simulation tests. (orig./IHOE) 891 IHOE/orig.- 892 HIS [de

  10. Mechanical and thermophysical properties of hot-pressed SYNROC B

    International Nuclear Information System (INIS)

    Hoenig, C.L.; Newkirk, H.W.; Otto, R.A.; Brady, R.L.; Brown, A.E.; Ulrich, A.R.; Lum, R.C.

    1981-01-01

    The optimal SYNROC compositons for use with commercial waste are reviewed. Large amounts of powder (about 2.5 kg) were prepared by convention al ceramic operations to test the SYNROC concept on a processing scale. Samples, 15.2 cm in diameter, were hot pressed in graphite, and representative samples were cut for microstructural evaluations. Measured mechanical and thermophysical properties did not vary significantly as a function of sample location and were typical of titanate ceramic materials

  11. Fatigue crack growth behaviors in hot-rolled low carbon steels: A comparison between ferrite–pearlite and ferrite–bainite microstructures

    International Nuclear Information System (INIS)

    Guan, Mingfei; Yu, Hao

    2013-01-01

    The roles of microstructure types in fatigue crack growth behaviors in ferrite–pearlite steel and ferrite–bainite steel were investigated. The ferrite–bainite dual-phase microstructure was obtained by intermediate heat treatment, conducted on ferrite–pearlite hot-rolled low carbon steel. This paper presents the results from investigation using constant stress-controlled fatigue tests with in-situ scanning electron microscopy (SEM), fatigue crack growth (FCG) rate tests, and fatigue fractography analysis. Microscopy images arrested by in-situ SEM showed that the fatigue crack propagation in F–P steel could become unstable more ealier compared with that in F–B steel. The fatigue cracks in ferrite–pearlite were more tortuous and could propagate more freely than that in ferrite–bainite microstructures. However, frequent crack branching were observed in ferrite–bainite steel and it indicated that the second hard bainite phase effectively retarded the crack propagation. The variation of FCG rate (da/dN) with stress intensity factor range (ΔK) for F–P and F–B steels was discussed within the Paris region. It was shown that FCG rate of F–P steel was higher than that of F–B steel. Moreover, the fatigue fracture surface analysis proved that grain boundaries could also play a role in the resistance of crack propagation.

  12. Thermal-mechanical properties of cracked UO2 pellets

    International Nuclear Information System (INIS)

    Williford, R.E.; Mohr, C.L.; Lanning, D.D.

    1980-11-01

    A series of experiments (IFA-431, 432, 513, and 527) sponsored by the Fuel Behavior Research Branch of the USNRC are being irradiated in the Halden Boiling Water Reactor to better define LWR fuel behavior over the normal operating range of power reactor fuel rods. One fuel behavior variable of interest is the thermally induced cracking of UO 2 fuel pellets. The effects of pellet cracking on the effective thermal conductivity and elastic moduli for the fragmented fuel were found to be primarily dependent on the free area in the r, theta plane of the fuel rod. The free area is defined as the area within the cladding inner surface that is not occupied by the fuel fragments themselves

  13. Effectiveness of Fiber Reinforcement on the Mechanical Properties and Shrinkage Cracking of Recycled Fine Aggregate Concrete

    Science.gov (United States)

    Nam, Jeongsoo; Kim, Gyuyong; Yoo, Jaechul; Choe, Gyeongcheol; Kim, Hongseop; Choi, Hyeonggil; Kim, Youngduck

    2016-01-01

    This paper presents an experimental study conducted to investigate the effect of fiber reinforcement on the mechanical properties and shrinkage cracking of recycled fine aggregate concrete (RFAC) with two types of fiber—polyvinyl alcohol (PVA) and nylon. A small fiber volume fraction, such as 0.05% or 0.1%, in RFAC with polyvinyl alcohol or nylon fibers was used for optimum efficiency in minimum quantity. Additionally, to make a comparative evaluation of the mechanical properties and shrinkage cracking, we examined natural fine aggregate concrete as well. The test results revealed that the addition of fibers and fine aggregates plays an important role in improving the mechanical performance of the investigated concrete specimens as well as controlling their cracking behavior. The mechanical properties such as compressive strength, splitting tensile strength, and flexural strength of fiber-reinforced RFAC were slightly better than those of non-fiber-reinforced RFAC. The shrinkage cracking behavior was examined using plat-ring-type and slab-type tests. The fiber-reinforced RFAC showed a greater reduction in the surface cracks than non-fiber-reinforced concrete. The addition of fibers at a small volume fraction in RFAC is more effective for drying shrinkage cracks than for improving mechanical performance. PMID:28773256

  14. Effectiveness of Fiber Reinforcement on the Mechanical Properties and Shrinkage Cracking of Recycled Fine Aggregate Concrete.

    Science.gov (United States)

    Nam, Jeongsoo; Kim, Gyuyong; Yoo, Jaechul; Choe, Gyeongcheol; Kim, Hongseop; Choi, Hyeonggil; Kim, Youngduck

    2016-02-26

    This paper presents an experimental study conducted to investigate the effect of fiber reinforcement on the mechanical properties and shrinkage cracking of recycled fine aggregate concrete (RFAC) with two types of fiber-polyvinyl alcohol (PVA) and nylon. A small fiber volume fraction, such as 0.05% or 0.1%, in RFAC with polyvinyl alcohol or nylon fibers was used for optimum efficiency in minimum quantity. Additionally, to make a comparative evaluation of the mechanical properties and shrinkage cracking, we examined natural fine aggregate concrete as well. The test results revealed that the addition of fibers and fine aggregates plays an important role in improving the mechanical performance of the investigated concrete specimens as well as controlling their cracking behavior. The mechanical properties such as compressive strength, splitting tensile strength, and flexural strength of fiber-reinforced RFAC were slightly better than those of non-fiber-reinforced RFAC. The shrinkage cracking behavior was examined using plat-ring-type and slab-type tests. The fiber-reinforced RFAC showed a greater reduction in the surface cracks than non-fiber-reinforced concrete. The addition of fibers at a small volume fraction in RFAC is more effective for drying shrinkage cracks than for improving mechanical performance.

  15. Atomic properties in hot plasmas from levels to superconfigurations

    CERN Document Server

    Bauche, Jacques; Peyrusse, Olivier

    2015-01-01

    This book is devoted to the calculation of hot-plasma properties which generally requires a huge number of atomic data. It is the first book that combines information on the details of the basic atomic physics and its application to atomic spectroscopy with the use of the relevant statistical approaches. Information like energy levels, radiative rates, collisional and radiative cross-sections, etc., must be included in equilibrium or non-equilibrium models in order to describe both the atomic-population kinetics and the radiative properties. From the very large number of levels and transitions involved in complex ions, some statistical (global) properties emerge. The book presents a coherent set of concepts and compact formulas suitable for tractable and accurate calculations. The topics addressed are: radiative emission and absorption, and a dozen of other collisional and radiative processes; transition arrays between level ensembles (configurations, superconfigurations); effective temperatures of configurat...

  16. The influence of creep properties on crack propagation in thermal barrier coatings

    International Nuclear Information System (INIS)

    Baeker, Martin

    2010-01-01

    Thermal barrier coatings are used to protect turbine blades from the high temperature of the process gas inside a turbine. They consist of a metallic bond coat and of a ceramic top coat with low thermal conductivity. During service, an additional oxide layer forms between bond coat and top coat that eventually causes failure. Finite element simulations show that the roughness of the interface between top and bond coat is crucial for determining the stress state. Lifetime models have been inferred that assume that cracks form in the peak positions at small oxide thickness and propagate when the oxide layer grows and the stress field shifts. A two-dimensional finite element model of crack propagation in the TBC layer is presented. Since the cracks propagate near a material interface and since plasticity may occur in the bond coat, standard tools of fracture mechanics for predicting the crack propagation direction are difficult to apply. This problem is circumvented in a very simple way by propagating short 'test cracks' in different directions and optimising to find the crack direction with the maximum energy release rate. It is shown that the energy release rate and the crack propagation direction are sensitive to the details of the stress state and especially to the creep properties of the materials. Implications for failure models are discussed.

  17. Mechanical Properties of a Bainitic Steel Producible by Hot Rolling

    Directory of Open Access Journals (Sweden)

    Rana R.

    2017-12-01

    Full Text Available A carbide-free bainitic microstructure is suitable for achieving a combination of ultra high strength and high ductility. In this work, a steel containing nominally 0.34C-2Mn-1.5Si-1Cr (wt.% was produced via industrial hot rolling and laboratory heat treatments. The austenitization (900°C, 30 min. and austempering (300-400°C, 3 h treatments were done in salt bath furnaces. The austempering treatments were designed to approximately simulate the coiling step, following hot rolling and run-out-table cooling, when the bainitic transformation would take place and certain amount of austenite would be stabilized due to suppression of carbide precipitation. The microstructures and various mechanical properties (tensile properties, bendability, flangeability, and room and subzero temperature impact toughness relevant for applications were characterized. It was found that the mechanical properties were highly dependent on the stability of the retained austenite, presence of martensite in the microstructure and the size of the microstructural constituents. The highest amount of retained austenite (~ 27 wt.% was obtained in the sample austempered at 375°C but due to lower austenite stability and coarser overall microstructure, the sample exhibited lower tensile ductility, bendability, flangeability and impact toughness. The sample austempered at 400°C also showed poor properties due to the presence of initial martensite and coarse microstructure. The best combination of mechanical properties was achieved for the samples austempered at 325-350°C with a lower amount of retained austenite but with the highest mechanical stability.

  18. Stress corrosion cracking properties of 15-5PH steel

    Science.gov (United States)

    Rosa, Ferdinand

    1993-01-01

    Unexpected occurrence of failures, due to stress corrosion cracking (SCC) of structural components, indicate a need for improved characterization of materials and more advanced analytical procedures for reliably predicting structures performance. Accordingly, the purpose of this study was to determine the stress corrosion susceptibility of 15-5PH steel over a wide range of applied strain rates in a highly corrosive environment. The selected environment for this investigation was a highly acidified sodium chloride (NaCl) aqueous solution. The selected alloy for the study was a 15-5PH steel in the H900 condition. The slow strain rate technique was selected to test the metals specimens.

  19. Fatigue crack growth prediction in 2xxx AA with friction stir weld HAZ properties

    Directory of Open Access Journals (Sweden)

    A. Tzamtzis

    2016-02-01

    Full Text Available An analytical model is developed to predict fatigue crack propagation rate under mode I loading in 2024 aluminum alloy with FSW HAZ material characteristics. Simulation of the HAZ local properties in parent 2024 AA was performed with overaging using specific heat treatment conditions. The model considers local cyclic hardening behavior in the HAZ to analyze crack growth. For the evaluation of the model, the analytical results have been compared with experimental fatigue crack growth on overaged 2024 alloy simulating material behavior at different positions within the HAZ. The analytical results showed that cyclic hardening at the crack tip can be used successfully with the model to predict FCG in a material at overaged condition associated with a location in the FSW HAZ.

  20. Optimising mechanical properties of hot forged nickel superalloy 625 components

    Science.gov (United States)

    Singo, Nthambe; Coles, John; Rosochowska, Malgorzata; Lalvani, Himanshu; Hernandez, Jose; Ion, William

    2018-05-01

    Hot forging and subsequent heat treatment were resulting in substandard mechanical properties of nickel superalloy, Alloy 625, components. The low strength was found to be due to inadequate deformation during forging, excessive grain growth and precipitation of carbides during subsequent heat treatment. Experimentation in a drop forging company and heat treatment facility led to the establishment of optimal parameters to minimise grain size and mitigate the adverse effects of carbide precipitation, leading to successful fulfilment of mechanical property specifications. This was achieved by reducing the number of operations, maximising the extent of deformation by changing the slug dimensions and its orientation in the die, and minimising the time of exposure to elevated temperatures in both the forging and subsequent heat treatment processes to avoid grain growth.

  1. Hot cracking characteristic of welding using Nd:YAG laser beam

    International Nuclear Information System (INIS)

    Ro, Kyoung Bo; Yoo, Young Tae; Oh, Yong Seak; Shin, Ho Jun; Kim, Ji Hwan

    2003-01-01

    The Nd:YAG laser process is known to have high speed and deep penetration capability to become one of the most advanced welding technologies. In spite of its good mechanical characteristics, SM45C carbon steel has a high carbon contents and suffers a limitation in the industrial application due to the poor welding properties. The major process parameters studied in the present laser welding experiment were position of focus, travel speed and laser power

  2. Properties influencing cracking and separation of palm nuts in a mechanical cracker cum separator

    Directory of Open Access Journals (Sweden)

    JOSHUA OLANREWAJU OLAOYE

    2018-01-01

    Full Text Available Experimental studies of some properties influencing cracking and separation of palm kernel from the shell was conducted in a palm kernel dual processing machine. A mechanical cracking cum separating machine was developed for the study. The cracking unit consists of feed hopper, impeller shaft, cracking drum and impeller blade. The nut falls by gravity through the hopper channel into the cracking drum where the cracking process takes place through the help of impeller blades that flip the palm nut against the walls of cylindrical cracking drum. The mass of cracked nut flows through the separating unit that separates the kernel from the shell. The separation is induced by high current of air mass generated by an axial fan. A dura palm variety was selected and a total sample of eighteen thousand (18000 palm nuts were obtained and divided into two groups (feed rates, A and B, of eight thousand and ten thousand palm nuts respectively. Sample groups A and B were further divided into five sub – groups of four hundred (400 and five hundred (500 palm kernel nuts. Each sub group (feed rate was replicated four times at different shaft speeds (600, 900, 1200, 1500 and 1800 rpm. Results showed that cracking efficiencies increased with respect to speed. Un-cracked nuts percentage ranged from 1.3 to 5.3% at 7.1% moisture content, and 1.6 to 4.5% for 400 and 500 feed rates, respectively. Cracking time for both feed rates decreased with shaft speed. Throughput capacity of 11.49 kg/h was observed to be the lowest at 600 rpm and moisture content of 7.1% for both 400 feed rates and the highest throughput capacity of 37.16 kg/h was recorded at 1800 rpm at moisture contents of 9.3% and 16.1%. The results of this study shows that moisture content, engine speed and feed rate are significant parameters that influence cracking of nuts and separation of palm kernel from the shell.

  3. Enhancement of strength properties of hot rolled 10KHSND steel

    International Nuclear Information System (INIS)

    Nasibov, A.G.; Popova, L.V.; Pikulin, S.A.; Globa, N.I.

    1989-01-01

    To find out the reasons of low hot rolling yield for 10KhSND steel sheets in mechanical properties, titanium effect in the range of 0.008-0.03% concentrations is studied. It is established that the titanium content in a solid solution is conserved within 0.003-0.005%, the rest of titanium is bound to carbonitrides Ti(C, N). It is shown that alloys with 0.025-0.03% titanium content possess the increased values of ultimate and yield strength the necessary level of impact strength and good wealdability. The good steel yield, when the titanium content is sustained at the given level, increases from 40 to 85%

  4. Analysis of hot rolling and hot forging effects on mechanical properties and microstructure of ZrNbMoGe alloy

    International Nuclear Information System (INIS)

    AH Ismoyo; Parikin; Bandriyana

    2014-01-01

    Research on formation technique by a combined method of rolling and forging has been carried out in order to improve the mechanical properties of ZrNbMoGe alloy to be used as fuel cladding in NPP (Nuclear Power Plant) application. The effects of rolling and forging were analyzed several tests. The tests were conducted for zirconium alloy specimen with a composition of (in % wt.) 97% Zr, 0,5% Mo, 2% Nb and 0,5% Ge, where the specimen was melted with an arc-furnace. The hot rolling and forging were conducted at 900 °C and 950 °C respectively. Hardness test was carried out by using a microhardness testing machine, while microstructure examination and crystal structure analysis were conducted with an optical microscope and an X-ray diffractometer. The results show that the hardness of the alloy increase from 141.21 HV (starting material) to 210.47 HV (hot rolled material) and 365.75 HV (hot forged material). Texturing phenomenon is clearly figured on the microstructure due to hot rolling and forging process. Analysis by diffractogram also indicates that the hot rolling and forging process has influence on the crystal orientation of dominant preferred direction in the reflection plane of (10ī1), recorded from the rise of intensity counting from about 2500 to 3000. In summary, hot forging and rolling process can change the mechanical properties (hardness and texture) and microstructure of materials. (author)

  5. Mechanical properties and examination of cracking in TMI-2 pressure vessel lower head material

    International Nuclear Information System (INIS)

    Diercks, D.R.; Neimark, L.A.

    1993-09-01

    Mechanical tests have been conducted on material from 15 samples removed from the lower head of the Three Mile Island unit 2 nuclear reactor pressure vessel. Measured properties include tensile properties and hardness profiles at room temperature, tensile and creep properties at temperatures of 600 to 1200 degrees C, and Charpy V-notch impact properties at -20 to +300 degrees C. These data, which were used in the subsequent analyses of the margin-to-failure of the lower head during the accident, are presented here. In addition, the results of metallographic and scanning electron microscope examinations of cladding cracking in three of the lower head samples are discussed

  6. Damage Mechanisms and Controlled Crack Propagation in a Hot Pressed Silicon Nitride Ceramic. Ph.D. Thesis - Northwestern Univ., 1993

    Science.gov (United States)

    Calomino, Anthony Martin

    1994-01-01

    The subcritical growth of cracks from pre-existing flaws in ceramics can severely affect the structural reliability of a material. The ability to directly observe subcritical crack growth and rigorously analyze its influence on fracture behavior is important for an accurate assessment of material performance. A Mode I fracture specimen and loading method has been developed which permits the observation of stable, subcritical crack extension in monolithic and toughened ceramics. The test specimen and procedure has demonstrated its ability to generate and stably propagate sharp, through-thickness cracks in brittle high modulus materials. Crack growth for an aluminum oxide ceramic was observed to be continuously stable throughout testing. Conversely, the fracture behavior of a silicon nitride ceramic exhibited crack growth as a series of subcritical extensions which are interrupted by dynamic propagation. Dynamic initiation and arrest fracture resistance measurements for the silicon nitride averaged 67 and 48 J/sq m, respectively. The dynamic initiation event was observed to be sudden and explosive. Increments of subcritical crack growth contributed to a 40 percent increase in fracture resistance before dynamic initiation. Subcritical crack growth visibly marked the fracture surface with an increase in surface roughness. Increments of subcritical crack growth loosen ceramic material near the fracture surface and the fracture debris is easily removed by a replication technique. Fracture debris is viewed as evidence that both crack bridging and subsurface microcracking may be some of the mechanisms contributing to the increase in fracture resistance. A Statistical Fracture Mechanics model specifically developed to address subcritical crack growth and fracture reliability is used together with a damaged zone of material at the crack tip to model experimental results. A Monte Carlo simulation of the actual experiments was used to establish a set of modeling input

  7. Finite-Element Analysis of Crack Arrest Properties of Fiber Reinforced Composites Application in Semi-Elliptical Cracked Pipelines

    Science.gov (United States)

    Wang, Linyuan; Song, Shulei; Deng, Hongbo; Zhong, Kai

    2018-04-01

    In nowadays, repair method using fiber reinforced composites as the mainstream pipe repair technology, it can provide security for X100 high-grade steel energy long-distance pipelines in engineering. In this paper, analysis of cracked X100 high-grade steel pipe was conducted, simulation analysis was made on structure of pipes and crack arresters (CAs) to obtain the J-integral value in virtue of ANSYS Workbench finite element software and evaluation on crack arrest effects was done through measured elastic-plastic fracture mechanics parameter J-integral and the crack arrest coefficient K, in a bid to summarize effect laws of composite CAs and size of pipes and cracks for repairing CAs. The results indicate that the K value is correlated with laying angle λ, laying length L2/D1, laying thickness T1/T2of CAs, crack depth c/T1 and crack length a/c, and calculate recommended parameters for repairing fiber reinforced composite CAs in terms of two different crack forms.

  8. Effect of chloride contamination in MON-1 propellant on crack growth properties of metals

    Science.gov (United States)

    Moran, C. M.; Toth, L. R.

    1981-01-01

    The effect of a high level of chloride content (800 ppm) in MON-1 propellant on the crack growth properties of seven materials was investigated. Sustained load tests were conducted at 49 C (120 F) temperature with thin gauge tensile specimens having a semi-elliptical surface flaw. Alloys included aluminum 1100, 3003, 5086 and 6061; corrosion resistant steel types A286 and 347; and titanium 6Al-4V. The configurations tested with precracked flaws exposed to MON-1 were: parent or base metal, center weld, and heat affected zone. It was concluded that this chloride level in MON-1 does not affect the stress corrosion, crack growth properties of these alloys after 1000 hour exposure duration under high stresses.

  9. Delayed hydride cracking and elastic properties of Excel, a candidate CANDU-SCWR pressure tube material

    International Nuclear Information System (INIS)

    Pan, Z.L.

    2010-01-01

    Excel, a Zr alloy which contains 3.5%Sn, 0.8%Nb and 0.8%Mo, shows high strength, good corrosion resistance, excellent creep-resistance and dimension stability and thus is selected as a candidate pressure tube material for CANDU-SCWR. In the present work, the delayed hydride cracking properties (K IH and the DHC growth rates), the hydrogen solubility and elastic modulus were measured in the irradiated and unirradiated Excel pressure tube material. (author)

  10. Effect of Hot-isostatic Pressing on Microstructure and Mechanical Properties of Second Generation Single Crystal Superalloy DD6

    Directory of Open Access Journals (Sweden)

    GUO Hui-ming

    2016-10-01

    Full Text Available Effects of the hot-isostatic pressing (HIP temperature (1280,1300,1320℃ on microstructures and mechanical properties of a second generation single crystal superalloy DD6 were investigated. The results show that the HIP treatment significantly decrease the cast porosity number of DD6 compared with standard treated specimens. Especially, the cast porosity volume fraction is deceased from 0.31% to 0.04% after the HIP treatment of 1300℃/100MPa, 4h. The cast eutectic volume fractions are remarkably reduced with increasing HIP temperature. The HIP treatments nearly unchanged the creep lives, While they greatly promote the low cycle fatigue lives. The elimination of cast microspores using the HIP treatment of 1300℃/100MPa, 4h result in the inhibition of crack initiation during fatigue and improve the low cycle fatigue lives one order of magnitude larger than that after standard heat treatment.

  11. Initiation of Stress Corrosion Cracking of 26Cr-1Mo Ferritic Stainless Steels in Hot Chloride Solution

    International Nuclear Information System (INIS)

    Kwon, H. S.; Hehemann, R. F.

    1987-01-01

    Elongation measurements of 26Cr-1Mo ferritic stainless steels undergoing stress corrosion in boiling LiCl solution allow the induction period to be distinguished from the propagation period of cracks by the deviation of elongation from the logarithmic creep law. Localised corrosion cells are activated exclusively at slip steps by loading and developed into corrosion trenches. No cracks have developed from the corrosion trenches until the induction period is exceeded. The induction period is regarded as a time for localised corrosion cells to achieve a critical degree of occlusion for crack initiation. The repassivation rate of exposed metal by creep or emergence of slip steps decreases as the load increases and is very sensitive to the microstructural changes that affect slip tep height. The greater susceptibility to stress corrosion cracking of either prestrained or grain coarsened 26Cr-1Mo alloy compared with that of mill annealed material results from a significant reduction of repassivation rate associated with the increased slip step height. The angular titanium carbonitrides particles dispersed in Ti-stabilized 26Cr-1Mo alloy have a detrimental effect on the resistance to stress corrosion cracking

  12. Fatigue and fatigue crack growth properties of 316LN and Incoloy 908 below 10 K

    International Nuclear Information System (INIS)

    Nyilas, A.; Zhang, J.; Obst, B.; Ulbricht, A.

    1992-01-01

    The cyclic loading characteristics of Tokamak type thermonuclear machines demand study of the fatigue response of the materials used in critical components. The large superconducting magnets and their superconductors will operate under cyclic mechanical stress conditions. The present paper is biased towards the current superconductor design of the NET (Next European Torus) model coil concept. The superconductor of this coil will be a cable-in-conduit Nb 3 Sn type with an enveloped stiff external jacket structure. The wall thickness of the jacket structure is within the range of 4-5 mm. The manufacturing of the jacket lengths for several hundred meters require an appropriate joining process due to the prefabricated section pieces available only in short lengths of 5-7 meters. The recently anticipated solution favors the flash butt welding technique. The performance of the superconductors jacket will depend on the material selection and the proper structural design according to the existing low temperature structural materials data base. The wind and react Nb 3 Sn-manufacturing process must also account the materials properties after ageing. A program was set up to elucidate the fatigue-life behavior and fatigue crack growth rate (FCGR) of the selected two candidate materials. These materials were the AISI 316LN with a specified low carbon content to avoid the embrittlement after the ageing process and the Incoloy 908. The 316LN material in the as received condition was tested with respect to its fatigue-life for specimens bearing predefined flaws and cracks. The propagation of surface cracks at 12 K and at 295 K was characterized with non standard specimens. The tests were performed in a cryogenic dynamic test facility under helium gas environment between 7 K and 20 K. Using the reference growth laws obtained from these measurements the total crack propagation starting with the initial crack length of the specimen could be predicted by numerical computation

  13. Comparison of Fatigue Properties and Fatigue Crack Growth Rates of Various Implantable Metals

    Science.gov (United States)

    Okazaki, Yoshimitsu

    2012-01-01

    The fatigue strength, effects of a notch on the fatigue strength, and fatigue crack growth rate of Ti-15Zr-4Nb-4Ta alloy were compared with those of other implantable metals. Zr, Nb, and Ta are important alloying elements for Ti alloys for attaining superior long-term corrosion resistance and biocompatibility. The highly biocompatible Ti-15Zr-4Nb-4Ta alloy exhibited an excellent balance between strength and ductility. Its notched tensile strength was much higher than that of a smooth specimen. The strength of 20% cold-worked commercially pure (C.P.) grade 4 Ti was close to that of Ti alloy. The tension-to-tension fatigue strength of an annealed Ti-15Zr-4Nb-4Ta rod at 107 cycles was approximately 740 MPa. The fatigue strength of this alloy was much improved by aging treatment after solution treatment. The fatigue strengths of C.P. grade 4 Ti and stainless steel were markedly improved by 20% cold working. The fatigue strength of Co-Cr-Mo alloy was markedly increased by hot forging. The notch fatigue strengths of 20% cold-worked C.P. grade 4 Ti, and annealed and aged Ti-15Zr-4Nb-4Ta, and annealed Ti-6Al-4V alloys were less than those of the smooth specimens. The fatigue crack growth rate of Ti-15Zr-4Nb-4Ta was the same as that of Ti-6Al-4V. The fatigue crack growth rate in 0.9% NaCl was the same as that in air. Stainless steel and Co-Cr-Mo-Ni-Fe alloy had a larger stress-intensity factor range (ΔK) than Ti alloy.

  14. Study of microstructure and fracture properties of blunt notched and sharp cracked high density polyethylene specimens.

    Science.gov (United States)

    Pan, Huanyu; Devasahayam, Sheila; Bandyopadhyay, Sri

    2017-07-21

    This paper examines the effect of a broad range of crosshead speed (0.05 to 100 mm/min) and a small range of temperature (25 °C and 45 °C) on the failure behaviour of high density polyethylene (HDPE) specimens containing a) standard size blunt notch and b) standard size blunt notch plus small sharp crack - all tested in air. It was observed that the yield stress properties showed linear increase with the natural logarithm of strain rate. The stress intensity factors under blunt notch and sharp crack conditions also increased linearly with natural logarithm of the crosshead speed. The results indicate that in the practical temperature range of 25 °C and 45 °C under normal atmosphere and increasing strain rates, HDPE specimens with both blunt notches and sharp cracks possess superior fracture properties. SEM microstructure studies of fracture surfaces showed craze initiation mechanisms at lower strain rate, whilst at higher strain rates there is evidence of dimple patterns absorbing the strain energy and creating plastic deformation. The stress intensity factor and the yield strength were higher at 25 °C compared to those at 45 °C.

  15. Investigation on the electrochemical properties and crack growth rates of stainless steels in BWR alkaline environments

    International Nuclear Information System (INIS)

    Wang, L.H.; Hsu, T.Y.; Huang, C.S.

    2000-01-01

    Increasing pH of reactor water to mildly alkaline is considered as one of the mitigating water chemistry strategies to reduce the activity release of radioactive oxides and suppress the growth rate of stress corrosion cracking. However, only limited experimental data are currently available in the published literature, it is imperative to perform additional tests to verify the effectiveness of slightly alkaline reactor water. Because the electrochemical behavior and SCC are intricately related, this study will attempt to investigates the electrochemical properties and measures the crack growth rates (CGRs) of type 304 stainless steel (SS) in both normal water chemistry (200 ppb O 2 , neutral pH 25 ) and alkaline chemistry (200 ppb O 2 , pH 25 = 8.0). The additive for pH control is potassium hydroxide (KOH). The crack growth rate was monitored by reversing DC potential drop technique. The electrochemical measurements include AC impedance measurement and potential pulsing test to measure the repassivation behavior. The characteristics of electrochemical properties and its effect on stress corrosion crocking in BWR alkaline environments have been further examined. (author)

  16. Characterization of low temperature creep properties of crack sealants using bending beam rehometry.

    Science.gov (United States)

    2009-11-01

    Crack sealing has been widely used as a routine preventative maintenance practice. Given its proper installation, crack sealants can extend : pavement service life by three to five years. However, current specifications for the selection of crack sea...

  17. Influence of Fissure Number on the Mechanical Properties of Layer-Crack Rock Models under Uniaxial Compression

    Directory of Open Access Journals (Sweden)

    Yun-liang Tan

    2018-01-01

    Full Text Available Many case studies have revealed that rock bursts generally occur in the high stress concentration area where layer-crack structures often exist, especially for brittle coal or rock masses. Understanding the mechanical properties of layer-crack rock models is beneficial for rational design and stability analysis of rock engineering project and rock burst prevention. This study experimentally investigated the influence of fissure number on the mechanical properties of layer-crack rock models through uniaxial compression tests. The digital speckle correlation method (DSCM and acoustic emission (AE techniques were applied to record and analyze the information of deformation and failure processes. Test results show the following: the bearing capacity of layer-crack specimen decreases compared with intact specimen, but their failure modes are similar, which are the splitting failure accompanied with local shear failure; the nonuniform deformation phenomenon begins to appear at the elastic deformation stage for layer-crack specimens; the AE behavior of intact specimens consists of three stages, that is, active stage, quiet stage, and major active stage, but for layer-crack specimens, it is characteristic by three peaks without quiet stage. In addition, as the fissure number of layer-crack specimens increases, the bearing capacity of specimens decreases, the appearing time of nonuniform deformation phenomenon in the specimen surface decreases, the AE events are denser and denser in each peak stage, and the risk of dynamic instability of layer-crack structure increases. At last, the failure mechanism of layer-crack structure and the related mitigation advices were discussed based on the test results. In general, the novelty is that this paper focuses on the failure mechanism of layer-crack structure directly.

  18. A Property of Crack Propagation at the Specimen of CFRP with Layer Angle

    Energy Technology Data Exchange (ETDEWEB)

    Hwang, Gue Wan; Cho, Jae Ung [Kongju Univ., Kongju (Korea, Republic of); Cho, Chong Du [Inha Univ., Incheon (Korea, Republic of)

    2016-12-15

    CFRP is the composite material manufactured by the hybrid resin on the basis of carbon fiber. As this material has the high specific strength and the light weight, it has been widely used at various fields. Particularly, the unidirectional carbon fiber can be applied with the layer angle. CFRP made with layer angle has the strength higher than with no layer angle. In this paper, the property of crack growth due to each layer angle was investigated on the crack propagation and fracture behavior of the CFRP compact tension specimen due to the change of layer angle. The value of maximum stress is shown to be decreased and the crack propagation is slowed down as the layer angle is increased. But the limit according to the layer angle is shown as the stress is increased again from the base point of the layer angle of 60°.This study result is thought to be utilized with the data which verify the probability of fatigue fracture when the defect inside the structure at using CFRP of mechanical structure happens.

  19. A Property of Crack Propagation at the Specimen of CFRP with Layer Angle

    International Nuclear Information System (INIS)

    Hwang, Gue Wan; Cho, Jae Ung; Cho, Chong Du

    2016-01-01

    CFRP is the composite material manufactured by the hybrid resin on the basis of carbon fiber. As this material has the high specific strength and the light weight, it has been widely used at various fields. Particularly, the unidirectional carbon fiber can be applied with the layer angle. CFRP made with layer angle has the strength higher than with no layer angle. In this paper, the property of crack growth due to each layer angle was investigated on the crack propagation and fracture behavior of the CFRP compact tension specimen due to the change of layer angle. The value of maximum stress is shown to be decreased and the crack propagation is slowed down as the layer angle is increased. But the limit according to the layer angle is shown as the stress is increased again from the base point of the layer angle of 60°.This study result is thought to be utilized with the data which verify the probability of fatigue fracture when the defect inside the structure at using CFRP of mechanical structure happens

  20. Low temperature tensile properties and stress corrosion cracking resistance in the super duplex stainless steels weldments

    International Nuclear Information System (INIS)

    Lee, Jeung Woo; Sung, Jang Hyun; Lee, Sung Keun

    1998-01-01

    Low temperature tensile properties and SCC resistances of super duplex stainless steels and their weldments are investigated. Tensile strengths increase remarkably with decreasing test temperature, while elongations decrease steeply at -196 .deg. C after showing peak or constant value down to -100 .deg. C. Owing to the low tensile deformation of weld region, elongations of welded specimen decrease in comparison to those of unwelded specimen. The welded tensile specimen is fractured through weld region at -196 .deg. C due to the fact that the finely dispersed ferrite phase in the austenite matrix increases an opportunity to supply the crack propagation path through the brittle ferrite phase at low temperature. The stress corrosion cracking initiates preferentially at the surface ferrite phase of base metal region and propagates through ferrite phase. When the corrosion crack meets with the fibrously aligned austenite phase to the tensile direction, the ferrite phase around austenite continues to corrode. Eventually, fracture of the austenite phase begins without enduring the tensile load. The addition of Cu+W to the super duplex stainless steel deteriorates the SCC resistance in boiling MgCl 2 solution, possibly due to the increment of pits in the ferrite phase and reduction of N content in the austenite phase

  1. Study on the cold and hot properties of medicinal herbs by thermotropism in mice behavior.

    Science.gov (United States)

    Zhao, Yan-Ling; Wang, Jia-Bo; Xiao, Xiao-He; Zhao, Hai-ping; Zhou, Can-ping; Zhang, Xue-ru; Ren, Yong-shen; Jia, Lei

    2011-02-16

    It is a common sense that chewing a mint leaf causes a cold feeling, while masticating a piece of ginger root is associated with a hot sensation. The Traditional Chinese Medicine has termed this phenomenon as cold and hot properties of herbs and applied them in treating certain human diseases successfully for thousands of years. Here, we have developed an Animal Thermotropism Behavior Surveillance System, and by using this device and other approaches, we not only verified the existence of, but also characterized and quantitated the cold and hot properties of medicinal herbs in animal behavioral experiments. The results suggested that the hot and cold properties of herbal drugs indeed correlated with the alteration of animal behavior in search for residence temperature. Copyright © 2010. Published by Elsevier Ireland Ltd.

  2. The radiolytic cracking decomposion of the plant cellulose materials and their chemcial properties

    International Nuclear Information System (INIS)

    Shou Hongxia

    1987-01-01

    Under the treatment with high energy radiation, plant cellulose materials undergo a series of changes in chemical and physical properties. This paper describes the chemical changes of water-soluble carbohydrate, easy-to-hydrolyse carbohydrate, hard-to-hydrolyse carbohydrate, amino acid and protein in rice straw after irradiation with 60 Co γ-ray. The content of water-soluble carbohydrate in rice straw can be increased significantly by such treatment. The combination treatment of irradiation and acid or alkali soaker can reduce the dose for the radiolytic cracking decomposition and produce a good effect

  3. Microstructures and mechanical properties of Fe-28Al-5Cr/TiC composites produced by hot-pressing sintering

    International Nuclear Information System (INIS)

    Zhang Xinghua; Yang Jun; Ma Jiqiang; Bi Qinling; Cheng Jun; Liang Yongmin; Liu Weimin

    2011-01-01

    Highlights: → The near fully dense Fe-28Al-5Cr/TiC composites are produced by hot-pressing sintering. → All the materials exhibit high compressive and bending strength. → Compressive strength increases but bending strength and ductility diminish with rising TiC amount in the composites. → Wear resistance significantly increases with rising TiC amount. - Abstract: The mechanical properties and microstructures of Fe-28Al-5Cr based composites reinforced with 15, 25, 35, 50 wt.% TiC ceramic particle, produced by hot-pressing sintering method, were investigated. The relative density of all the composites was up to 99%. The distribution of TiC was uniform in the composites. Results of XRD analysis showed that the composites were composed of TiC and disorder Fe 3 Al phases. All the materials exhibited very high strength of 1200-2000 MPa. The hardness and compressive strength of the composites increased obviously but compressive strain decreased gradually except 50% composite with increasing TiC content. The bending strength and deflection of the composites decreased significantly with increasing TiC content. The bending fracture surfaces of all the materials were examined using scanning electron microscopy (SEM). The fracture mode transformed gradually from tough dimple fracture mode to brittle cleavage facets crack mode with the increase of TiC content. Wear resistance of the Fe-28Al-5Cr alloy was also significantly improved by addition of TiC.

  4. Hot gauge field properties from the thermal variational principle

    International Nuclear Information System (INIS)

    Schroeder, Y.; Schulz, H.

    1995-10-01

    A Feynman-Jensen version of the thermal variational principle is applied to hot gauge fields, abelian as well as nonabelian: scalar electrodynamics (without scalar self-coupling) and the gluon plasma. The perturbatively known self-energies are shown to derive by variation from a free quadratic (''gaussian'') trial Lagrangian. Independence of the covariant gauge fixing parameter is reached (within the order g 2 studies and for scalar ED) after a reformulation of the partition function such that it depends on only even powers of the gauge field. This way, however, the potential non-perturbative power of the calculus seems to be ruined. (orig.)

  5. Microstructure and properties of hot roll bonding layer of dissimilar metals. 2. Bonding interface microstructure of Zr/stainless steel by hot roll bonding and its controlling

    International Nuclear Information System (INIS)

    Yasuyama, Masanori; Ogawa, Kazuhiro; Taka, Takao; Nakasuji, Kazuyuki; Nakao, Yoshikuni; Nishimoto, Kazutoshi.

    1996-01-01

    The hot roll bonding of zirconium and stainless steel inserted with tantalium was investigated using the newly developed rolling mill. The effect of hot rolling temperatures of zirconium/stainless steel joints on bonding interface structure was evaluated. Intermetallic compound layer containing cracks was observed at the bonding interface between stainless steel and tantalium when the rolling temperature was above 1373K. The hardness of the bonding layer of zirconium and tantalium bonded above 1273K was higher than tantalium or zirconium base metal in spite of absence of intermetallic compound. The growth of reaction layer at the stainless steel and tantalium interface and at the tantalium and zirconium interface was conforming a parabolic low when that was isothermally heated after hot roll bonding, and the growth rate was almost same as that of static diffusion bonding without using hot roll bonding process. It is estimated that the strain caused by hot roll bonding gives no effect on the growth of reaction layer. It was confirmed that the dissimilar joint of zirconium and stainless steel with insert of tantalium having the sound bonding interface were obtained at the suitable bonding temperature of 1173K by the usage of the newly developed hot roll bonding process. (author)

  6. Microstructure and properties of diffusion bonded Ti-6Al-4V parts using brazing-assisted hot isostatic pressing

    International Nuclear Information System (INIS)

    Wu, Z.; Mei, J.; Voice, W.; Beech, Steve; Wu, X.

    2011-01-01

    Highlights: → A low cost method of diffusion bonding has been developed for complex-shaped components of Ti6Al4V. → Vacuum brazing has been used to seal the periphery to allow encapsulation-free HIPping. → The tensile properties of the bonds are comparable with those of the bulk material, but the fatigue life was slightly reduced. - Abstract: Ti-6Al-4V couples have been diffusion bonded by hot isostatic pressing (HIPping) after vacuum brazing was used to seal the periphery of the bonding samples so that no encapsulation was required during HIPping. Analytical scanning electron microscopy was used to assess the microstructure of the HIPped interface and tensile and fatigue properties of bonded samples were compared with those of the bulk starting material. The tensile properties of the bonds were shown to be comparable with those of the bulk material, but the fatigue life was slightly downgraded. The fatigue fractures were initiated by inclusions on the bonding interface, caused by contamination before bonding, but the fatigue cracks did not propagate along the bonding interface indicating a strong bond. It is concluded that this technique of vacuum brazing plus HIPping could be used for encapsulation-free HIPping to produce complex-shaped components.

  7. Influence of complex particle emission on properties of giant dipole resonance of hot nuclei

    International Nuclear Information System (INIS)

    Wen Wanxin; Jin Genming

    2003-01-01

    The possible reasons for the discrepancy between calculation results based on the statistical evaporation model and experimental data of giant dipole resonance of very hot nuclei are discussed. Both of simulations with the standard CASCADE code and the code coupling complex particle emission are carried out. It is shown that the complex particle emission affects the properties of giant dipole resonance of very hot nuclei

  8. The multiwavelength spectrum of NGC 3115: hot accretion flow properties

    Science.gov (United States)

    Almeida, Ivan; Nemmen, Rodrigo; Wong, Ka-Wah; Wu, Qingwen; Irwin, Jimmy A.

    2018-04-01

    NGC 3115 is the nearest galaxy hosting a billion solar mass black hole and is also a low-luminosity active galactic nucleus (LLAGN). X-ray observations of this LLAGN are able to spatially resolve the hot gas within the sphere of gravitational influence of the supermassive black hole. These observations make NGC 3115 an important test bed for black hole accretion theory in galactic nuclei since they constrain the outer boundary conditions of the hot accretion flow. We present a compilation of the multiwavelength spectral energy distribution (SED) of the nucleus of NGC 3115 from radio to X-rays. We report the results from modelling the observed SED with radiatively inefficient accretion flow (RIAF) models. The radio emission can be well-explained by synchrotron emission from the RIAF without the need for contribution from a relativistic jet. We obtain a tight constraint on the RIAF density profile, ρ (r) ∝ r^{-0.73 _{-0.02} ^{+0.01}}, implying that mass-loss through subrelativistic outflows from the RIAF is significant. The lower frequency radio observation requires the synchrotron emission from a non-thermal electron population in the RIAF, similarly to Sgr A*.

  9. Structure and hot-rolled reinforcement rods properties evolution in the process of long service life

    International Nuclear Information System (INIS)

    Mikryukov, V.R.; Syomin, A.P.; Konovalov, S.V.; Ivanov, Yu.F.; Gromov, V.E.

    2006-01-01

    The physical nature of mechanical properties of hot-rolled reinforcement rods degradation during long-life operation is established by methods of transmission diffraction electron microscopy. It is shown that strength and plasticity properties decrease is due to cementite plates cutting and dissolution, microcracks formation process as a result of interstitial phase inclusions creation in the near-surface layer of material

  10. Structure and hot-rolled reinforcement rods properties evolution in the process of long service life

    Energy Technology Data Exchange (ETDEWEB)

    Mikryukov, V R [Siberian State Industrial University, Kirov str., 42. 654007, Novokuznetsk (Russian Federation); Syomin, A P [Siberian State Industrial University, Kirov str., 42. 654007, Novokuznetsk (Russian Federation); Konovalov, S V [Siberian State Industrial University, Kirov str., 42. 654007, Novokuznetsk (Russian Federation); Ivanov, Yu F [Siberian State Industrial University, Kirov str., 42. 654007, Novokuznetsk (Russian Federation); Gromov, V E [Siberian State Industrial University, Kirov str., 42. 654007, Novokuznetsk (Russian Federation)

    2006-08-25

    The physical nature of mechanical properties of hot-rolled reinforcement rods degradation during long-life operation is established by methods of transmission diffraction electron microscopy. It is shown that strength and plasticity properties decrease is due to cementite plates cutting and dissolution, microcracks formation process as a result of interstitial phase inclusions creation in the near-surface layer of material.

  11. Comparison of Crack Growth Test Results at Elevated Temperature and Design Code Material Properties for Grade 91 Steel

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Hyeong-Yeon; Kim, Woo-Gon; Kim, Nak-Hyun [Korea Atomic Energy Reserach Institute, Daejeon (Korea, Republic of)

    2015-01-15

    The material properties of crack growth models at an elevated temperature were derived from the results of numerous crack growth tests for Mod.9Cr-1Mo (ASME Grade 91) steel specimens under fatigue loading and creep loading at an elevated temperature. These crack growth models were needed for defect assessment under creep-fatigue loading. The mathematical crack growth rate models for fatigue crack growth (FCG) and creep crack growth (CCG) were determined based on the test results, and the models were compared with those of the French design code RCCMRx to investigate the conservatism of the code. The French design code RCC-MRx provides an FCG model and a CCG model for Grade 91 steel in Section III Tome 6. It was shown that the FCG model of RCC-MRx is conservative, while the CCG model is non-conservative compared with the present test data. Thus, it was shown that further validation of the property was required. Mechanical strength tests and creep tests were also conducted, and the test results were compared with those of RCC-MRx.

  12. The deformation of the front of a 3D interface crack propagating quasistatically in a medium with random fracture properties

    Science.gov (United States)

    Pindra, Nadjime; Lazarus, Véronique; Leblond, Jean-Baptiste

    One studies the evolution in time of the deformation of the front of a semi-infinite 3D interface crack propagating quasistatically in an infinite heterogeneous elastic body. The fracture properties are assumed to be lower on the interface than in the materials so that crack propagation is channelled along the interface, and to vary randomly within the crack plane. The work is based on earlier formulae which provide the first-order change of the stress intensity factors along the front of a semi-infinite interface crack arising from some small but otherwise arbitrary in-plane perturbation of this front. The main object of study is the long-time behavior of various statistical measures of the deformation of the crack front. Special attention is paid to the influences of the mismatch of elastic properties, the type of propagation law (fatigue or brittle fracture) and the stable or unstable character of 2D crack propagation (depending on the loading) upon the development of this deformation.

  13. On micro-meso relations homogenizing electrical properties of transversely cracked laminated composites

    KAUST Repository

    Lubineau, Gilles; Nouri, Hedi; Roger, Frederic

    2013-01-01

    A practical way to track the development of transverse cracking in a laminated composite is to monitor the change of its electrical resistance. Yet, the relations between transverse cracking and the global modification of resistivity is still

  14. Evaluation of Fatigue Crack Propagation of Gears Considering Uncertainties in Loading and Material Properties

    Directory of Open Access Journals (Sweden)

    Haileyesus B. Endeshaw

    2017-11-01

    Full Text Available Failure prediction of wind turbine gearboxes (WTGs is especially important since the maintenance of these components is not only costly but also causes the longest downtime. One of the most common causes of the premature fault of WTGs is attributed to the fatigue fracture of gear teeth due to fluctuating and cyclic torque, resulting from stochastic wind loading, transmitted to the gearbox. Moreover, the fluctuation of the torque, as well as the inherent uncertainties of the material properties, results in uncertain life prediction for WTGs. It is therefore essential to quantify these uncertainties in the life estimation of gears. In this paper, a framework, constituted by a dynamic model of a one-stage gearbox, a finite element method, and a degradation model for the estimation of fatigue crack propagation in gear, is presented. Torque time history data of a wind turbine rotor was scaled and used to simulate the stochastic characteristic of the loading and uncertainties in the material constants of the degradation model were also quantified. It was demonstrated that uncertainty quantification of load and material constants provides a reasonable estimation of the distribution of the crack length in the gear tooth at any time step.

  15. Physicochemical and phytochemical properties of cold and hot water extraction from Hibiscus sabdariffa.

    Science.gov (United States)

    Ramirez-Rodrigues, Milena M; Plaza, Maria L; Azeredo, Alberto; Balaban, Murat O; Marshall, Maurice R

    2011-04-01

    Hibiscus cold (25 °C) and hot (90 °C) water extracts were prepared in various time-temperature combinations to determine equivalent extraction conditions regarding their physicochemical and phytochemical properties. Equivalent anthocyanins concentration was obtained at 25 °C for 240 min and 90 °C for 16 min. Total phenolics were better extracted with hot water that also resulted in a higher antioxidant capacity in these extracts. Similar polyphenolic profiles were observed between fresh and dried hibiscus extracts. Hibiscus acid and 2 derivatives were found in all extracts. Hydroxybenzoic acids, caffeoylquinic acids, flavonols, and anthocyanins constituted the polyphenolic compounds identified in hibiscus extracts. Two major anthocyanins were found in both cold and hot extracts: delphynidin-3-sambubioside and cyanidin-3-sambubioside. In general, both cold and hot extractions yielded similar phytochemical properties; however, under cold extraction, color degradation was significantly lower and extraction times were 15-fold longer. Hibiscus beverages are prepared from fresh or dried calyces by a hot extraction and pasteurized, which can change organoleptic, nutritional, and color attributes. Nonthermal technologies such as dense phase carbon dioxide may maintain their fresh-like color, flavor, and nutrients. This research compares the physicochemical and phytochemical changes resulting from a cold and hot extraction of fresh and dried hibiscus calyces and adds to the knowledge of work done on color, quality attributes, and antioxidant capacity of unique tropical products. In addition, the research shows how these changes could lead to alternative nonthermal processes for hibiscus.

  16. Numerical simulation of temperature field, microstructure evolution and mechanical properties of HSS during hot stamping

    International Nuclear Information System (INIS)

    Shi, Dongyong; Liu, Wenquan; Ying, Liang; Hu, Ping; Shen, Guozhe

    2013-01-01

    The hot stamping of boron steels is widely used to produce ultra high strength automobile components without any spring back. The ultra high strength of final products is attributed to the fully martensitic microstructure that is obtained through the simultaneous forming and quenching of the hot blanks after austenization. In the present study, a mathematical model incorporating both heat transfer and the transformation of austenite is presented. A FORTRAN program based on finite element technique has been developed which permits the temperature distribution and microstructure evolution of high strength steel during hot stamping process. Two empirical diffusion-dependent transformation models under isothermal conditions were employed respectively, and the prediction capability on mechanical properties of the models were compared with the hot stamping experiment of an automobile B-pillar part

  17. Properties of Galvanized and Galvannealed Advanced High Strength Hot Rolled Steels

    Energy Technology Data Exchange (ETDEWEB)

    V.Y. Guertsman; E. Essadiqi; S. Dionne; O. Dremmailova; R. Bouchard; B. Voyzelle; J. McDermid; R. Fourmentin

    2008-04-01

    The objectives of the project were (i) to develop the coating process information to achieve good quality coatings on 3 advanced high strength hot rolled steels while retaining target mechanical properties, (ii) to obtain precise knowledge of the behavior of these steels in the various forming operations and (iii) to establish accurate user property data in the coated conditions. Three steel substrates (HSLA, DP, TRIP) with compositions providing yield strengths in the range of 400-620 MPa were selected. Only HSLA steel was found to be suitable for galnaizing and galvannealing in the hot rolled condition.

  18. Effect of hot densification on tribotechnical properties of sintered (Al-12Si)-40Sn alloy

    Science.gov (United States)

    Rusin, N. M.; Skorentsev, A. L.; Kolubaev, E. A.

    2017-12-01

    The paper describes the effect of hot densification on mechanical and tribotechnical properties of sintered samples of (Al-12Si)-40Sn composition. It proves that such treatment increases the strength and ductility of the studied materials and makes higher their wear resistant under dry friction against a steel counterbody.

  19. Analysis of a bending test on a full-scale PWR hot leg elbow containing a surface crack

    Energy Technology Data Exchange (ETDEWEB)

    Delliou, P. le [Electricite de France, EDF, 77 - Moret-sur-Loing (France). Dept. MTC; Julisch, P.; Hippelein, K. [Stuttgart Univ. (Germany). Staatliche Materialpruefungsanstalt; Bezdikian, G. [Electricite de France, EDF, 92 - Paris la Defense (France). Direction Production Transport

    1998-11-01

    EDF, in co-operation with Framatome, has conducted a large research programme on the mechanical behaviour of thermally aged cast duplex stainless steel elbows, which are part of the main primary circuit of French PWR. One important task of this programme consisted of testing a full-scale PWR hot leg elbow. The elbow contained a semi-elliptical circumferential notch machined on the outer surface of the intrados as well as casting defects located on the flanks. To simulate the end-of-life condition of the component regarding material toughness, it had undergone a 2400 hours ageing heat treatment at 400 C. The test preparation and execution, as well as the material characterization programme, were committed to MPA. The test was conducted under constant internal pressure and in-plane bending (opening mode) at 200 C. For safety reasons, it took place on an open air-site: the Meppen military test ground. At the maximum applied moment (6000 kN.m), the notch did not initiate. This paper presents the experimental results and the fracture mechanics analysis of the test, based on finite element calculations. (orig.)

  20. A study of pressureless microwave sintering, microwave-assisted hot press sintering and conventional hot pressing on properties of aluminium/alumina nanocomposite

    Energy Technology Data Exchange (ETDEWEB)

    Abedinzadeh, Reza; Safavi, Seyed Mohsen; Karimzadeh, Fathallah [Isfahan University, Isfahan (Iran, Islamic Republic of)

    2016-05-15

    Bulk Al/4wt-%Al{sub 2}O{sub 3} nanocomposites were prepared by consolidating nanocomposite powders using pressureless microwave sintering, microwave-assisted hot press sintering and conventional hot pressing techniques. Microstructural observations revealed that the microwave-assisted hot press sintering at different sintering temperatures of 400.deg.C and 500.deg.C resulted in more densification and smaller grain size for Al/Al{sub 2}O{sub 3} nanocomposite as compared with the conventional hot pressing. Moreover, the application of pressure in microwave sintering process led to more densification and grain growth. Mechanical properties resulting from microhardness and nanoindentation tests were also compared between three-method processed samples. It was found that the microwave-assisted hot-pressed sample exhibited higher hardness and elastic modulus in comparison with microwave-sintered and conventional hot-pressed samples. The improvement in the mechanical properties can be ascribed to lower porosity of microwave-assisted hot-pressed sample.

  1. The radiation swelling effect on fracture properties and fracture mechanisms of irradiated austenitic steels. Part II. Fatigue crack growth rate

    Energy Technology Data Exchange (ETDEWEB)

    Margolin, B., E-mail: margolinbz@yandex.ru; Minkin, A.; Smirnov, V.; Sorokin, A.; Shvetsova, V.; Potapova, V.

    2016-11-15

    The experimental data on the fatigue crack growth rate (FCGR) have been obtained for austenitic steel of 18Cr-10Ni-Ti grade (Russian analog of AISI 321 steel) irradiated up to neutron dose of 150 dpa with various radiation swelling. The performed study of the fracture mechanisms for cracked specimens under cyclic loading has explained why radiation swelling affects weakly FCGR unlike its effect on fracture toughness. Mechanical modeling of fatigue crack growth has been carried out and the dependencies for prediction of FCGR in irradiated austenitic steel with and with no swelling are proposed and verified with the obtained experimental results. As input data for these dependencies, FCGR for unirradiated steel and the tensile mechanical properties for unirradiated and irradiated steels are used.

  2. Solidification cracking in austenitic stainless steel welds

    Indian Academy of Sciences (India)

    M. Senthilkumar (Newgen Imaging) 1461 1996 Oct 15 13:05:22

    Hot cracking in stainless steel welds is caused by low-melting eutectics containing impurities such as S, ... Total crack length (TCL), used extensively in hot cracking assessment, exhibits greater variability due to ... behaviour appear to be complex and the mechanisms thereof are not completely under- stood. Development of ...

  3. Properties of hot and dense strongly interacting matter

    Energy Technology Data Exchange (ETDEWEB)

    Almasi, Gabor Andras

    2017-06-19

    In this thesis we consider effective models of quantum chromodynamics to learn about the chiral- and deconfinement phase transitions. In Chapter 1 we review basic properties of strongly interacting matter and the foundations of finite temperature field theory. We review furthermore the nonperturbative functional renormalization group (FRG) approach. In Chapter 2 we introduce the quark-meson (QM) model and its extensions including the Polyakov-loop variables and repulsive vector interactions between quarks. We then discuss features of the model both in the mean-field approximation and in the renormalization group treatment. A novel method to solve the renormalization group equations based on the Chebyshev polynomials is presented at the end of the chapter. In Chapter 3 the scaling behavior of the order parameter at the chiral phase transition is studied within effective models. We explore universal and nonuniversal structures near the critical point. These include the scaling functions, the leading corrections to scaling and the corresponding size of the scaling window as well as their dependence on an external symmetry breaking field. We consider two models in the mean-field approximation, the QM and the Polyakov-loop-extended quark-meson (PQM) models, and compare their critical properties with a purely bosonic theory, the O(N) linear sigma model in the N → ∞ limit. In these models the order parameter scaling function is found analytically using the high temperature expansion of the thermodynamic potential. The effects of a gluonic background on the nonuniversal scaling parameters are studied within the PQM model. Furthermore, numerical calculations of the scaling function and the scaling window are performed in the QM model using the FRG. Chapter 4 contains a study of the critical properties of net-baryon-number fluctuations at the chiral restoration transition in a medium at finite temperature and net baryon density. The chiral dynamics of quantum

  4. Evaluation of hot hardness, creep, fatigue and fracture properties of zirconia ceramics by an indentation technique

    International Nuclear Information System (INIS)

    Kutty, T.R.G.; Ganguly, C.; Upadhyaya, D.D.

    1996-01-01

    Zirconia ceramics have wide range engineering applications at room and elevated temperatures. For understanding the mechanical behaviour, the indentation technique was adapted for quick evaluation of hot hardness, creep, fatigue and fracture properties. A Vicker's diamond indentor with 10 N load was employed for hot hardness and creep measurement up to 1300 deg. The fatigue data were evaluated at room temperature by repeated indentation with a constant load (10-2500N) at the same location for a dwell time of 5s until it resulted in the formation of a lateral chip on the sample surface. Thus, the number of cycles for chip formation at a specific indentation load was obtained. The fracture toughness was evaluated at room temperature with a load of 300N using a Vicker's diamond indentor. The results of hot hardness, creep, fatigue, and fracture data ol 3Y-TZP and Mg-PSZ are discussed along with their microstructural features. (authors)

  5. The influence of prior ageing on microstructure, tensile properties and hot hardness of alloy 800HT

    International Nuclear Information System (INIS)

    El-Magd, E.

    1996-01-01

    For high temperature applications especially in the construction of equipment, carbide strengthened steels are widely used because of their good mechanical properties and relatively low cost. These materials undergo microstructural changes under such service conditions which contribute greatly to the strength properties and thus play an important role in equipment design considerations. The influence of a prior thermal ageing on the tensile strength values and the hot hardness of the austenitic iron base alloy, Alloy 800HT, is examined in this work. It was therefore necessary to carry out tensile and hot hardness tests with the solution treated and overaged material at ranges between room temperature and 900 . The microstructural changes are investigated using lightmicroscopy, SEM and TEM. The changes of the material properties with thermal pretreatment conditions is studied and discussed in the context of the determined microstructural development. (orig.) [de

  6. Modelling the influence of cracking and healing on modal properties of concrete beams

    NARCIS (Netherlands)

    Savija, B.; Schlangen, E.

    2015-01-01

    Concrete structures are commonly cracked when in service. To overcome issues arising from cracking, self-healing concrete is being developed. Together with the development of the material, techniques to verify and quantify self-healing are being developed. A number of destructive techniques have

  7. Microstructure distribution and mechanical properties prediction of boron alloy during hot forming using FE simulation

    International Nuclear Information System (INIS)

    Cui Junjia; Lei Chengxi; Xing Zhongwen; Li Chunfeng

    2012-01-01

    Highlights: ► We model microstructural evolution during hot forming using a metallo-thermo-mechanical model. ► The effect of water-cooled on temperature distribution of blank and tools was investigated. ► The effect of process parameters on microstructure and mechanical properties were investigated. ► FE results were compared to experimental results and the errors of mechanical properties were in a reasonable scope. - Abstract: As a theoretical tool predicting microstructural evolution of boron alloy, the finite element (FE) method has received considerable attention in recent years. In this work, we focus on the boron alloy under non-isothermal hot forming conditions and establish a fully coupled metallo-thermo-mechanical model taking account of cooling and oxide. Based on the proposed model, we investigate the phase transformation and predict the hardness during the hot forming process via FE simulation. In addition, according to the hardness, the tensile strength during non-isothermal forming is predicted. Supporting the feasibility of the proposed model is the experiments where BR1500HS alloy is hot-worked at various conditions that derive a promising agreement of microstructures, hardness, and tensile strength to the simulation data.

  8. Mitigation strategies for reflective cracking in pavements : [research project capsule].

    Science.gov (United States)

    2013-12-01

    Refl ection cracks are caused by discontinuities (cracks or joints) in underlying layers, : which propagate through hot-mix asphalt (HMA) overlay due to continuous movement : at the crack prompted by thermal expansion and traffi c loading. If the new...

  9. Analysis of stress intensity factor for a Griffith crack opened under constant pressure in a plate with temperature dependent properties

    International Nuclear Information System (INIS)

    Hata, Toshiaki

    1982-01-01

    Recently, the research on the thermal stress of structural materials has become important with the progress of nuclear reactor technology. In the case of large temperature gradient, the change of the physical properties of materials must be taken into account. The thermal stress analysis for the things with cracks taking the temperature dependence of properties into account has scarcely been carried out. In this report, the general method of solution of three-dimensional problems using perturbation method and the extension of thermo-elastic displacement potential method is shown for the case in which Young's modulus changes according to the exponential function of temperature. Moreover, using this method, the effect of the temperature dependence of properties on the stress intensity factor of the cracks subjected to internal pressure in a strip exposed to linear thermal flow was clarified. In the analysis, Young's modulus, the coefficient of linear thermal expansion and thermal conductivity were assumed to be dependent on temperature. The method of solution, the analysis of stress intensity factor considering the change of properties due to temperature, and the numerical calculation for a square plate with a crack are explained. (Kako, I.)

  10. Thermoelectric Properties of Hot-Pressed and PECS-Sintered Magnesium-Doped Copper Aluminum Oxide

    Science.gov (United States)

    Liu, Chang; Morelli, Donald T.

    2011-05-01

    Copper aluminum oxide (CuAlO2) is considered as a potential candidate for thermoelectric applications. Partially magnesium-doped CuAlO2 bulk pellets were fabricated using solid-state reactions, hot-pressing, and pulsed electric current sintering (PECS) techniques. X-ray diffraction and scanning electron microscopy were adopted for structural analysis. High-temperature transport property measurements were performed on hot-pressed samples. Electrical conductivity increased with Mg doping before secondary phases became significant, while the Seebeck coefficient displayed the opposite trend. Thermal conductivity was consistently reduced as the Mg concentration increased. Effects of Mg doping, preparation conditions, and future modification on this material's properties are discussed.

  11. The effect of hot multistage drawing on molecular structure and optical properties of polyethylene terephthalate fibers

    Directory of Open Access Journals (Sweden)

    Aminoddin Haji

    2012-08-01

    Full Text Available In this work, mechanical and structural parameters related to the optical properties of polyethylene terephthalate (PET fibers drawn at hot multistage have been investigated. The changes in optical parameters upon changing draw ratio are used to obtain the mechanical orientation factors and , various orientation functions f2(θ, f4(θ and f6(θ, and amorphous and crystalline orientation functions (f a and f c. Also, the numbers of random links between the network junction points (N1, the average optical orientation (Fav, and the distribution function of segment ω(cos θ were calculated. In addition, an empirical formula was suggested to correlate changes in the birefringence with the draw ratio and its constants were determined. The study demonstrated change on the molecular orientation functions and structural parameters upon hot multistage drawing. Significant variations in the characteristic properties of the drawn PET fibers were due to reorientation of the molecules caused by applied heat and external tension.

  12. Mechanical Properties of Hot Mix Crumb Rubber Modified Asphalt Concrete Using Waste Tire

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Nak Seok; Lee, Woo Yeol [Kyonggi University, Suwon (Korea)

    1998-06-30

    Wheel tracking and ravelling tests were conducted on the hot mix crumb rubber modified asphalt concrete using waste tire to evaluate the mechanical properties in comparison with conventional asphalt concrete. According to the test results, the modified product was superior to the conventional one by 50% in the resistance of permanent deformation and by 15% in the resistance of durability. The experimental results should recommend that the waste tire is positively recycled for asphalt concrete. (author). 11 refs., 6 tabs., 2 figs.

  13. Investigation of Microstructure and Mechanical Properties in Hot-work Tool Steels

    OpenAIRE

    Rey, Tomas

    2017-01-01

    Hot-work tool steels make up an important group of steels that are able to perform with good strength and toughness properties at elevated temperatures and stresses. They are able to gain this behavior through their alloy composition and heat treatment, which relies on the precipitation of alloy carbides to counter the loss in strength as the tempered material becomes more ductile. As demand grows for materials that are suitable for even harsher applications and that show improved mechanical ...

  14. Prediction of fatigue crack growth behaviour of an α-β titanium alloy in Paris-regime using LCF properties

    International Nuclear Information System (INIS)

    Varma, V.K.; Saxena, V.K.; Srinivas, M.

    1993-01-01

    A model has been developed in the recent past to predict fatigue crack growth (FCG) behaviour in the Paris-regime of various steels by employing low cycle fatigue (LCF) properties. The model forms its basis on the assumption that the cyclic damage process immediately ahead of a crack-tip, restricted in a small zone termed as process zone, is identical to those experienced in the LCF loading of a smooth specimen. Within the process zone, fatigue damage has been assumed in terms of product of stress and plastic strain which is analogous to the plastic strain energy density of the smooth specimen under fatigue loading. In this paper the model developed by Kujawski and Ellyin has been used to predict the FCG behaviour of an α-β titanium alloy in the Paris-regime by employing the experimentally obtained LCF properties. The FCG behaviour thus theoretically predicted was compared with the experimentally determined FCG behaviour

  15. Effect of Hot Rolling on the Microstructure and Mechanical Properties of Nitrogen Alloyed Austenitic Stainless Steel

    Science.gov (United States)

    Chenna Krishna, S.; Karthick, N. K.; Jha, Abhay K.; Pant, Bhanu; Cherian, Roy M.

    2018-05-01

    In the present investigation, the effect of multi-pass hot rolling in the temperature range of 700-1000 °C on the microstructure and mechanical properties of nitrogen alloyed austenitic stainless steel was studied with the aid of optical microscopy, tensile testing and x-ray diffraction measurements. The microstructural changes that occurred in the hot rolled specimens were elongation of grains in rolling direction, nucleation of new grains at the grain boundaries of elongated grains and growth of nucleated grains to form fully recrystallized grains. Elongated grains formed at lower rolling temperature (700-800 °C) due to inadequate strain/temperature for the initiation of dynamic recrystallization. At higher rolling temperature (900-1000 °C), fine grains formed due to dynamic recrystallization. Tensile properties showed strong dependency on the rolling temperature. Tensile strength increased with the decrease in the rolling temperature at the cost of ductility. Maximum strength was observed in samples hot rolled at 700 °C with yield strength of 917 MPa and ductility of 25%. This variation in the tensile properties with the rolling temperature is attributed to changes in the dislocation density and grain structure. The estimated yield strength from the dislocation density, solid solution and grain boundary strengthening closely matched with experimentally determined yield strength confirming the role of dislocation density and grain size in the strengthening.

  16. A Study on the Manufacturing Properties of Crack Self-Healing Capsules Using Cement Powder for Addition to Cement Composites

    OpenAIRE

    Choi, Yun-Wang; Oh, Sung-Rok; Choi, Byung-Keol

    2017-01-01

    We fabricated crack self-healing capsules using cement powder for mixing into cement composites and evaluated the properties of the capsule manufacturing process in this study. The manufacture of the self-healing capsules is divided into core production processing of granulating cement in powder form and a coating process for creating a wall on the surfaces of the granulated cement particles. The produced capsules contain unhardened cement and can be mixed directly with the cement composite m...

  17. On micro-meso relations homogenizing electrical properties of transversely cracked laminated composites

    KAUST Repository

    Lubineau, Gilles

    2013-11-01

    A practical way to track the development of transverse cracking in a laminated composite is to monitor the change of its electrical resistance. Yet, the relations between transverse cracking and the global modification of resistivity is still unclear that makes difficult to interpret these non-destructive-testing results. Here, we introduce the homogenization process that defines at the meso scale an equivalent homogeneous ply that is energetically equivalent to the cracked one. It is shown that this equivalent ply mainly depends on the cracking level while it can be considered independent on the rest of the laminated structure. The direct consequence is that the meso scale is a pertinent one to perform the homogenization. Then, non-destructive electrical measurements can be considered as a reliable technique to access meso scale damage indicators. © 2013 Elsevier Ltd.

  18. Transport properties of MnTe films with cracks produced in thermal cycling process

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Liang; Wang, Zhenhua; Zhang, Zhidong [Institute of Metal Research, University of Chinese Academy of Sciences, Chinese Academy of Sciences, Shenyang National Laboratory for Materials Science, Shenyang (China)

    2017-10-15

    As a promising material in antiferromagnetic spintronics, MnTe films manifested complex characteristics according to previous reports. In this work, we investigate in details the temperature dependence of resistivity of MnTe films grown on SiO{sub 2}/Si substrate and focus on the divaricating of cooling and warming resistivity-temperature (R-T) curves. It is found that such a divaricating in resistivity is associated with cracks produced in thermal cycles. By comparing the crystalline character and the morphology before and after the cycles, we verify the appearance of cracks and the release of stress in the films. Based on the temperature dependence of thermal-expansion coefficient of Si and MnTe, the origin of the cracks is the mismatched thermal-expansion coefficient (α). The humps, which only appear in the R-T curve of the first cooling process, are attributed to the produced cracks and/or the unreleased stress. (orig.)

  19. Evaluation on effects of chloride-induced deterioration on mechanical properties of RC beams with cracking damage

    International Nuclear Information System (INIS)

    Matsuo, Toyofumi; Matsumura, Takuro; Otsuka, Taku

    2015-01-01

    This paper discusses the influence of chloride-induced deterioration on mechanical properties of aging reinforced concrete (RC) structures and the applicability of the material degradation model that takes reinforcing steel corrosion into consideration for finite element analysis. We conducted the corrosion tests under the simulated tidal environment and the flexural loading tests for the RC beams with cracking damage and initial defects. Then, the experimental results were numerically correlated to validate the devised modeling. The obtained results were summarized as follows: (a) The cracking damage in specimens caused a minor effect on the reinforcing steel corrosion in the case where the thickness of cover concrete was 40 mm and main rebars did not yield before chloride attack. On the other hand the maximum corrosion ratio of the deteriorated part became considerably larger than that of the non-cracking part in the specimens where the cover concrete were removed partially to simulate spalling by the severe corrosion. (b) Based on the test results, we derived the corrosion velocity of reinforcing steel corresponding to cracking damage degrees. (c) In FEM analyses, we showed that the above modeling can estimate the flexural strength of RC beams in consideration of the degradation in elongation performance of reinforcing steel due to corrosion. (author)

  20. Identification of conduction and hot electron property in ZnS, ZnO and SiO2

    International Nuclear Information System (INIS)

    Huang Jinzhao; Xu Zheng; Zhao Suling; Li Yuan; Yuan Guangcai; Wang Yongsheng; Xu Xurong

    2007-01-01

    The impact excitation and ionization is the most important process in layered optimization scheme and solid state cathodoluminescence. The conduction property (semiconductor property) of SiO 2 , ZnS and ZnO is studied based on organic/inorganic electroluminescence. The hot electron property (acceleration and multiplication property) of SiO 2 and ZnS is investigated based on the solid state cathodoluminescence. The results show that the SiO 2 has the fine hot electron property and the conduction property is not as good as ZnO and ZnS

  1. Physical fracture properties (fracture surfaces as information sources; crackgrowth and fracture mechanisms; exemples of cracks)

    International Nuclear Information System (INIS)

    Meny, Lucienne.

    1979-06-01

    Fracture surfaces are considered as a useful source of informations: an introduction to fractography is presented; the fracture surface may be observed through X ray microanalysis, and other physical methods such as Auger electron spectroscopy or secundary ion emission. The mechanisms of macroscopic and microscopic crackgrowth and fracture are described, in the case of unstable fracture (cleavage, ductile with shear, intergranular brittleness) and of progressive crack propagation (creep, fatigue). Exemples of cracks are presented in the last chapter [fr

  2. Experimental investigation on influence of porous material properties on drying process by a hot air jet

    International Nuclear Information System (INIS)

    Di Marco, P; Filippeschi, S

    2012-01-01

    The drying process of porous media is a subject of scientific interest, and different mathematical approaches can be found in the literature. A previous paper by the same authors showed that the celebrated Martin correlation for hot air jet heat and mass transfer yields different degrees of accuracy (from 15% to 65%, increasing at high values of input power) if tested on different fabrics, the remaining conditions being the same. In this paper the fabric drying has been experimentally investigated more in depth. A dedicated experimental apparatus for hot jet drying was assembled and operated, in which a hot jet impinges perpendicularly onto a wet fabric. A calibrated orifice was adopted to measure the jet flow rate, with an accuracy better than 3%. The drying power was determined by continuously weighing with a precision scale a moistened patch exposed to the drying jet. The effect of the time of the exposure and the initial amount of water has been evaluated for each sample. During the hot jet exposure, the temperature distribution over the wet patch has been observed by an infrared thermo-camera. A mathematical model of water transport inside and outside the fabric was developed, in order to evidence the governing transport resistances. The theoretical predictions have been compared with the experimental results, and showed the necessity to modify correlations and models accounting for fabric properties.

  3. UHPLC/Q-TOFMS-based metabolomics for the characterization of cold and hot properties of Chinese materia medica.

    Science.gov (United States)

    Wang, Yang; Zhou, Shujun; Wang, Meng; Liu, Shuying; Hu, Yuanjia; He, Chengwei; Li, Peng; Wan, Jian-Bo

    2016-02-17

    The cold/hot property of Chinese materia medica (CMM) and the application of its corresponding knowledge in the diagnosis, differentiation and treatment of diseases have been considered to be the extremely important part of traditional Chinese medicine (TCM). As highly abstracted TCM theory, the cold/hot property of CMMs is still not fully understood and remains to be elucidated by systems biology approach. The cold and hot properties of CMM are mainly defined by the response of the body to a given CMM. Metabolomics is a promising systems biology method to profile entire endogenous metabolites and monitor their fluctuations related to an exogenous stimulus. Thus, a metabolomics approach was applied to characterize the cold and hot properties of CMMs. Mice were intragastrically administered three selected cold property CMMs (i.e., Rheum palmatum L., radix et rhizoma; Coptis chinensis Franch, rhizome and Scutellaria baicalensis Georgi, radix) and three hot property CMMs (i.e., Cinnamomum cassia (L.) J. Presl, cortex; Zingiber officinale Roscoe, rhizoma and Evodia rutaecarpa (Juss.) Benth., fructus) once daily for one week. The comprehensive metabolome changes in the plasma of mice after treatment with cold or hot property CMMs were characterized by ultra-high performance liquid chromatography/time of flight mass spectrometry (UHPLC/Q-TOF-MS), and the potential biomarkers related to cold and hot properties of CMM were explored. Metabolites perturbation in plasma occurs after treatment with cold CMMs and hot CMMs in mice, and 15 and 16 differential biomarkers were identified to be associated with the cold and hot properties of CMMs, respectively. Among them, LPC (18:0), LPC (18:1), LPC (20:4) and LPC (20:5) showed decreased trends in the cold property CMM treated groups, but increased in the hot property CMM treated groups. There is a strong connection between the cold/hot property of CMMs and lysophosphatidylcholines metabolism. This study offers new insight

  4. Cracked rocks with positive and negative Poisson's ratio: real-crack properties extracted from pressure dependence of elastic-wave velocities

    Science.gov (United States)

    Zaitsev, Vladimir Y.; Radostin, Andrey V.; Dyskin, Arcady V.; Pasternak, Elena

    2017-04-01

    We report results of analysis of literature data on P- and S-wave velocities of rocks subjected to variable hydrostatic pressure. Out of about 90 examined samples, in more than 40% of the samples the reconstructed Poisson's ratios are negative for lowest confining pressure with gradual transition to the conventional positive values at higher pressure. The portion of rocks exhibiting negative Poisson's ratio appeared to be unexpectedly high. To understand the mechanism of negative Poisson's ratio, pressure dependences of P- and S-wave velocities were analyzed using the effective medium model in which the reduction in the elastic moduli due to cracks is described in terms of compliances with respect to shear and normal loading that are imparted to the rock by the presence of cracks. This is in contrast to widely used descriptions of effective cracked medium based on a specific crack model (e.g., penny-shape crack) in which the ratio between normal and shear compliances of such a crack is strictly predetermined. The analysis of pressure-dependences of the elastic wave velocities makes it possible to reveal the ratio between pure normal and shear compliances (called q-ratio below) for real defects and quantify their integral content in the rock. The examination performed demonstrates that a significant portion (over 50%) of cracks exhibit q-ratio several times higher than that assumed for the conventional penny-shape cracks. This leads to faster reduction of the Poisson's ratio with increasing the crack concentration. Samples with negative Poisson's ratio are characterized by elevated q-ratio and simultaneously crack concentration. Our results clearly indicate that the traditional crack model is not adequate for a significant portion of rocks and that the interaction between the opposite crack faces leading to domination of the normal compliance and reduced shear displacement discontinuity can play an important role in the mechanical behavior of rocks.

  5. Investigation into the stress corrosion cracking properties of AA2099, an aluminum-lithium-copper alloy

    Science.gov (United States)

    Padgett, Barbara Nicole

    Recently developed Al-Li-Cu alloys show great potential for implementation in the aerospace industry because of the attractive mix of good mechanical properties and low density. AA2099 is an Al-Li-Cu alloy with the following composition Al-2.69wt%Cu-1.8wt%Li-0.6wt%Zn-0.3wt%Mg-0.3wt%Mn-0.08wt%Zr. The environmental assisted cracking and localized corrosion behavior of the AA2099 was investigated in this thesis. The consequences of uncontrolled grain boundary precipitation via friction stir welding on the stress corrosion cracking (SCC) behavior of AA2099 was investigated first. Using constant extension rate testing, intergranular corrosion immersion experiments, and potentiodynamic scans, the heat-affected zone on the trailing edge of the weld (HTS) was determined to be most susceptible of the weld zones. The observed SCC behavior for the HTS was linked to the dissolution of an active phase (Al2CuLi, T1) populating the grain boundary. It should be stated that the SCC properties of AA2099 in the as-received condition were determined to be good. Focus was then given to the electrochemical behavior of precipitate phases that may occupy grain and sub-grain boundaries in AA2099. The grain boundary micro-chemistry and micro-electrochemistry have been alluded to within the literature as having significant influence on the SCC behavior of Al-Li-Cu alloys. Major precipitates found in this alloy system are T1 (Al 2CuLi), T2 (Al7.5Cu4Li), T B (Al6CuLi3), and theta (Al2 Cu). These phases were produced in bulk form so that the electrochemical nature of each phase could be characterized. It was determined T1 was most active electrochemically and theta was least. When present on grain boundaries in the alloy, electrochemical behavior of the individual precipitates aligned with the observed corrosion behavior of the alloy (e.g. TB was accompanied by general pitting corrosion and T 1 was accompanied by intergranular corrosion attack). In addition to the electrochemical behavior of

  6. Extracting real-crack properties from non-linear elastic behaviour of rocks: abundance of cracks with dominating normal compliance and rocks with negative Poisson ratios

    Directory of Open Access Journals (Sweden)

    V. Y. Zaitsev

    2017-09-01

    Full Text Available Results of examination of experimental data on non-linear elasticity of rocks using experimentally determined pressure dependences of P- and S-wave velocities from various literature sources are presented. Overall, over 90 rock samples are considered. Interpretation of the data is performed using an effective-medium description in which cracks are considered as compliant defects with explicitly introduced shear and normal compliances without specifying a particular crack model with an a priori given ratio of the compliances. Comparison with the experimental data indicated abundance (∼ 80 % of cracks with the normal-to-shear compliance ratios that significantly exceed the values typical of conventionally used crack models (such as penny-shaped cuts or thin ellipsoidal cracks. Correspondingly, rocks with such cracks demonstrate a strongly decreased Poisson ratio including a significant (∼ 45 % portion of rocks exhibiting negative Poisson ratios at lower pressures, for which the concentration of not yet closed cracks is maximal. The obtained results indicate the necessity for further development of crack models to account for the revealed numerous examples of cracks with strong domination of normal compliance. Discovering such a significant number of naturally auxetic rocks is in contrast to the conventional viewpoint that occurrence of a negative Poisson ratio is an exotic fact that is mostly discussed for artificial structures.

  7. Evaluation of Detrimental Effects on Mechanical Properties of Zry-4 Due to Hydrogen Absorption by means of Scanning Electron Microscopy (SEM) In-Situ Observation of Crack Propagation

    International Nuclear Information System (INIS)

    Fernandez, L; Fernandez, G.E; Bertolino, G; Meyer, G

    2001-01-01

    The study of mechanical properties degradation of zirconium alloys due to hydrides assumes fundamental importance in the nuclear industry.During normal nuclear reactors operation, structural parts absorbed hydrogen generated from radiolysis of water, causing detrimental effects on mechanical properties.As a consequence, these materials are easily cracked in the presence of mechanical solicitation due to loss of ductility of the hydride-phase.The presence of cracks indicates fracture mechanic as the most suitable methodology in the study of mechanical properties degradation.In this work we used the crack tip opening displacement (CTOD) criteria to evaluate the detrimental effects on mechanical properties with the observation in SEM of crack propagation.The samples used were SEN (B) of Zry-4 and cathodic homogenous charged with hydrogen concentrations lower than 400 ppm

  8. Nd-Fe-B-Cu hot deformation processing: a comparison of deformation modes, microstructural development and magnetic properties

    International Nuclear Information System (INIS)

    Ferrante, M.; Sinka, V.; Assis, O.B.G.; Oliveira, I. de; Freitas, E. de

    1996-01-01

    Due to its relative simplicity and low cost the hot deformation of Nd-Fe-B ingots is rapidly reaching the status of a valid alternative to sintering. Among the possible deformation modes, pressing, rolling and forging are perhaps the most successful. This paper describes the research programme undertaken so far, by discussing the relationship between deformation mode, microstructure and magnetic properties of magnets produced by hot deformation mode, microstructure and magnetic properties of magnets produced by hot deformation of a number of Nd-fe-B-Cu alloys. Microstructural observation showed that both pressed and forged samples are characterized by a heterogeneous microstructure and from magnetic measurements it was concluded that magnetic properties differ when taken in the center or in the periphery of the sample. On the other hand roller magnets were homogeneous both in terms of microstructure and magnetic properties, and interpretations of the mechanisms of texture development and of microstructural development of hot deformed magnets is put forward. (author)

  9. Mechanical properties of copper-lithium alloys produced by mechanic alloyed and hot extrusion

    International Nuclear Information System (INIS)

    Castillo B, Ricardo; Gorziglia S, Ezio; Penaloza V, Augusto

    2004-01-01

    In this work are presented the progress carried out on the characterization of some physical and mechanical properties, together with the determination of the micro mechanism of fracture of the Cu-2% wt Li, that was obtained by mechanical alloying followed hot extrusion at 500 o C and 700 o C. Hardness and tensile mechanical tests were performed together with metallographic and fractographic analysis. The experimental results obtained with powders of the Cu-Li alloy studied are compared with powder of pure copper, under similar test conditions. The results show that by hot extrusion was allowed to obtain very high densification levels for the materials under study. Moreover, it was found that lithium reduce both the tensile strength and elongation, of copper by a mechanism of embrittlement. The results are compares with the literature (au)

  10. Effect of asymmetric hot rolling on texture, microstructure and magnetic properties in a non-grain oriented electrical steel

    Energy Technology Data Exchange (ETDEWEB)

    Chen, S., E-mail: Shangping.chen@tatasteel.com [Tata Steel, 1970 CA IJmuiden (Netherlands); Butler, J. [Tata Steel, S60 3AR South Yorkshire (United Kingdom); Melzer, S. [Tata Steel, 1970 CA IJmuiden (Netherlands)

    2014-11-15

    In this study, both asymmetric hot rolling (AHR) and conventional hot rolling (CHR) were carried out to study the effect of the hot rolling conditions on the evolution of the texture and microstructure in a non-grain oriented (NGO) steel. The microstructure and texture in the subsequent processing stages were characterised and related to the final magnetic properties. The results show that AHR, compared with CHR, tends to homogenise texture through thickness of the hot band strips. AHR results in a higher fraction of the θ-fibre ({0 0 1}) and a lower fraction of the γ-fibre ({1 1 1}) in the hot band strips, which are favourable features in relation to the magnetic properties of the strip. However, the favourable features observed in hot rolled AHR strips are eliminated after cold rolling and annealing. Contrarily, the required θ-fibre is decreased and the unwanted γ-fibre is intensified in the AHR sheet after cold rolling and their strength is maintained in the subsequent process steps. On the other hand, AHR does not produce a discernible change in the grain size in the hot band annealed strip and in the final annealed sheet, except that the magnetic anisotropy in the AHR is improved after skin pass and extra annealing as the result of the redistribution of the texture components within the θ-fibre, no significant improvement of the magnetic properties as a direct consequence of the application of asymmetric hot rolling has been observed under the current AHR experimental conditions. - Highlights: • Asymmetrical hot rolling (AHR) produces more uniform distribution of texture through the thickness of the hot rolled strips and of the hot band annealed strips when compared with conventional hot rolling (CHR). • AHR results in a higher fraction of the θ-fibre ({0 0 1}) and a lower fraction of the γ-fibre ({1 1 1}) in the hot band strips. The θ-fibre is decreased but the γ-fibre is intensified in the AHR sheet after cold rolling

  11. Effect of asymmetric hot rolling on texture, microstructure and magnetic properties in a non-grain oriented electrical steel

    International Nuclear Information System (INIS)

    Chen, S.; Butler, J.; Melzer, S.

    2014-01-01

    In this study, both asymmetric hot rolling (AHR) and conventional hot rolling (CHR) were carried out to study the effect of the hot rolling conditions on the evolution of the texture and microstructure in a non-grain oriented (NGO) steel. The microstructure and texture in the subsequent processing stages were characterised and related to the final magnetic properties. The results show that AHR, compared with CHR, tends to homogenise texture through thickness of the hot band strips. AHR results in a higher fraction of the θ-fibre ({0 0 1}) and a lower fraction of the γ-fibre ({1 1 1}) in the hot band strips, which are favourable features in relation to the magnetic properties of the strip. However, the favourable features observed in hot rolled AHR strips are eliminated after cold rolling and annealing. Contrarily, the required θ-fibre is decreased and the unwanted γ-fibre is intensified in the AHR sheet after cold rolling and their strength is maintained in the subsequent process steps. On the other hand, AHR does not produce a discernible change in the grain size in the hot band annealed strip and in the final annealed sheet, except that the magnetic anisotropy in the AHR is improved after skin pass and extra annealing as the result of the redistribution of the texture components within the θ-fibre, no significant improvement of the magnetic properties as a direct consequence of the application of asymmetric hot rolling has been observed under the current AHR experimental conditions. - Highlights: • Asymmetrical hot rolling (AHR) produces more uniform distribution of texture through the thickness of the hot rolled strips and of the hot band annealed strips when compared with conventional hot rolling (CHR). • AHR results in a higher fraction of the θ-fibre ({0 0 1}) and a lower fraction of the γ-fibre ({1 1 1}) in the hot band strips. The θ-fibre is decreased but the γ-fibre is intensified in the AHR sheet after cold rolling

  12. Tensile and stress corrosion cracking properties of type 304 stainless steel irradiated to a very high dose

    International Nuclear Information System (INIS)

    Chung, H.M.; Strain, R.V.; Shack, W.J.

    2001-01-01

    Certain safety-related core internal structural components of light water reactors, usually fabricated from Type 304 or 316 austenitic stainless steels (SSs), accumulate very high levels of irradiation damage (20-100 displacement per atom or dpa) by the end of life. Our databases and mechanistic understanding of the degradation of such highly irradiated components, however, are not well established. A key question is the nature of irradiation-assisted intergranular cracking at very high doses, i.e. is it purely mechanical failure or is it stress-corrosion cracking? In this work, hot-cell tests and microstructural characterization were performed on Type 304 SS from the hexagonal fuel can of the decommissioned EBR-II reactor after irradiation to ∼50 dpa at ∼370 deg. C. Slow-strain-rate tensile tests were conducted at 289 degree sign C in air and in water at several levels of electrochemical potential (ECP), and microstructural characteristics were analyzed by scanning and transmission electron microscopies. The material deformed significantly by twinning and exhibited surprisingly high ductility in air, but was susceptible to severe intergranular stress corrosion cracking (IGSCC) at high ECP. Low levels of dissolved O and ECP were effective in suppressing the susceptibility of the heavily irradiated material to IGSCC, indicating that the stress corrosion process associated with irradiation-induced grain-boundary Cr depletion, rather than purely mechanical separation of grain boundaries, plays the dominant role. However, although IGSCC was suppressed, the material was susceptible to dislocation channeling at a low ECP, and this susceptibility led to a poor work-hardening capability and low ductility

  13. Effects of hot water pre-extraction on surface properties of bagasse soda pulp.

    Science.gov (United States)

    Cordeiro, Nereida; Ashori, Alireza; Hamzeh, Yahya; Faria, Marisa

    2013-03-01

    In this work, the effects of hot water pre-extraction of depithed bagasse on the soda pulping and surface properties were studied. The conditions of hot water pre-extraction were: maximum temperature 170 °C, heat-up time 90 min, time at maximum temperature 10 min, and solid to liquor ratio (S:L) 1:8. Consequently, the pre-extracted and un-extracted bagasse chips were subjected to soda pulping at 160 °C for 1h with 11, 14 and 17% active alkali charge and an S:L of 1:5. The results showed that the hot water pre-extraction increased bagasse surface texture porosity by hemicellulose degradation. Therefore, the delignification was faster for pulping of pre-extracted samples. At a certain charge of alkali, pre-extracted samples showed higher screened yield and lower Kappa number. For instance, at 17% alkali charge, pre-extracted bagasse gave 11.3% higher pulp yield compared with the un-extracted ones. Inverse gas chromatography (IGC) results showed that the hot water pre-extraction changed the active sites on the bagasse surface, decreasing the dispersive energy and the basicity character, and affected the particle morphology. The pulping process decreased the hydrophobicity and the basicity of the bagasse surface. The surfaces of un-extracted and pre-extracted bagasse pulps had similar properties but different morphology. The pulps present higher surface area and permeability with more reactive capacity. Copyright © 2012 Elsevier B.V. All rights reserved.

  14. Setting Mechanical Properties of High Strength Steels for Rapid Hot Forming Processes

    Science.gov (United States)

    Löbbe, Christian; Hering, Oliver; Hiegemann, Lars; Tekkaya, A. Erman

    2016-01-01

    Hot stamping of sheet metal is an established method for the manufacturing of light weight products with tailored properties. However, the generally-applied continuous roller furnace manifests two crucial disadvantages: the overall process time is long and a local setting of mechanical properties is only feasible through special cooling techniques. Hot forming with rapid heating directly before shaping is a new approach, which not only reduces the thermal intervention in the zones of critical formability and requested properties, but also allows the processing of an advantageous microstructure characterized by less grain growth, additional fractions (e.g., retained austenite), and undissolved carbides. Since the austenitization and homogenization process is strongly dependent on the microstructure constitution, the general applicability for the process relevant parameters is unknown. Thus, different austenitization parameters are analyzed for the conventional high strength steels 22MnB5, Docol 1400M, and DP1000 in respect of the mechanical properties. In order to characterize the resulting microstructure, the light optical and scanning electron microscopy, micro and macro hardness measurements, and the X-ray diffraction are conducted subsequent to tensile tests. The investigation proves not only the feasibility to adjust the strength and ductility flexibly, unique microstructures are also observed and the governing mechanisms are clarified. PMID:28773354

  15. Metallurgical phenomena in laser finishing: Interdependences between solidification morphologies and hot cracking in laser welding of mostly austenitic materials. Final reportc; Metallkundliche Phaenomene der Laserstrahlmaterialbearbeitung. Teilvorhaben: Zusammenhaenge zwischen Erstarrungsmorphologien und Heissrissentstehung beim Laserschweissen von vornehmlich austenitischen Werkstoffen. Abschlussbericht

    Energy Technology Data Exchange (ETDEWEB)

    Schobbert, H.

    2000-06-01

    Austentic stainless steels are widely used in safety relevant applications such as chemical plant industry or off-shore industry. Due to the rapid development of laser welding processes, the economical efficiency increases and leads to a growing interest in industry for the production of, for example, straight bead welded pipes. A specific problem of laser welding is the economically desirable high welding speed, which leads in austenitic stainless steels to a change of solidification mode and thus, to a restricted hot cracking resistance. Thus, the solidification morphologies of austenitic stainless steels near the eutectic trough during laser welding were investigated. Thereby, the main aspect was the evaluation of a short-term metallurgical kinetic effects under rapid solidification conditions. It was proven that three widely used stainless steels (1.4828, 1.4306, and 1.4404) show a transition of primary solidifcation mode from primary ferritic to primary austenitic solidification depending on the solidification rate. The approximate value of the critical soldification rate can be determined using a newly developed model by analyzing the geometric structures of solidification. The critical solidification rate for the transition of the solidification mode depends on the chemical composition of the base metal. It was shown that austenitic stainless steels have a critical solidification rate of approximately 1 m/min. As a main result, it was proven that a transition of the solidification mode to primary austenitic solidification promotes the predicted susceptibiliyy of hot cracking. For this, a hot cracking test assembly has been developed in order to determine the hot cracking behavior under laser beam conditions. In contrast to existing hot crack tests, a critical strain rate for hot crack initiation could be measured. A classification of the materials with respect to their hot cracking susceptibility under the solidification conditions during laser welding can

  16. Magnetic and cytotoxic properties of hot-filament chemical vapour deposited diamond

    Energy Technology Data Exchange (ETDEWEB)

    Zanin, Hudson, E-mail: hudsonzanin@gmail.com [Faculdade de Engenharia Eletrica e Computacao, Departamento de Semicondutores, Instrumentos e Fotonica, Universidade Estadual de Campinas, UNICAMP, Av. Albert Einstein N.400, CEP 13 083-852 Campinas, Sao Paulo (Brazil); Peterlevitz, Alfredo Carlos; Ceragioli, Helder Jose [Faculdade de Engenharia Eletrica e Computacao, Departamento de Semicondutores, Instrumentos e Fotonica, Universidade Estadual de Campinas, UNICAMP, Av. Albert Einstein N.400, CEP 13 083-852 Campinas, Sao Paulo (Brazil); Rodrigues, Ana Amelia; Belangero, William Dias [Laboratorio de Biomateriais em Ortopedia, Faculdade de Ciencias Medicas, Universidade Estadual de Campinas, Rua Cinco de Junho 350 CEP 13083970, Campinas, Sao Paulo (Brazil); Baranauskas, Vitor [Faculdade de Engenharia Eletrica e Computacao, Departamento de Semicondutores, Instrumentos e Fotonica, Universidade Estadual de Campinas, UNICAMP, Av. Albert Einstein N.400, CEP 13 083-852 Campinas, Sao Paulo (Brazil)

    2012-12-01

    Microcrystalline (MCD) and nanocrystalline (NCD) magnetic diamond samples were produced by hot-filament chemical vapour deposition (HFCVD) on AISI 316 substrates. Energy Dispersive X-ray Spectroscopy (EDS) measurements indicated the presence of Fe, Cr and Ni in the MCD and NCD samples, and all samples showed similar magnetisation properties. Cell viability tests were realised using Vero cells, a type of fibroblastic cell line. Polystyrene was used as a negative control for toxicity (NCT). The cells were cultured under standard cell culture conditions. The proliferation indicated that these magnetic diamond samples were not cytotoxic. - Highlights: Black-Right-Pointing-Pointer Polycrystalline diamonds doped with Fe, Cr and Ni acquire ferromagnetic properties. Black-Right-Pointing-Pointer CVD diamonds have been prepared with magnetic and semiconductor properties. Black-Right-Pointing-Pointer Micro/nanocrystalline diamonds show good cell viability with fibroblast proliferation.

  17. PHOTOSPHERIC PROPERTIES OF WARM EUV LOOPS AND HOT X-RAY LOOPS

    Energy Technology Data Exchange (ETDEWEB)

    Kano, R. [National Astronomical Observatory of Japan, 2-21-1 Osawa, Mitaka, Tokyo 181-8588 (Japan); Ueda, K. [Department of Astronomy, Graduate School of Science, University of Tokyo, 7-3-1 Hongo, Bunkyo-ku, Tokyo 113-0033 (Japan); Tsuneta, S., E-mail: ryouhei.kano@nao.ac.jp [Institute of Space and Astronautical Science, Japan Aerospace Exploration Agency, 3-1-1 Yoshinodai, Chuo, Sagamihara, Kanagawa 252-5210 (Japan)

    2014-02-20

    We investigate the photospheric properties (vector magnetic fields and horizontal velocity) of a well-developed active region, NOAA AR 10978, using the Hinode Solar Optical Telescope specifically to determine what gives rise to the temperature difference between ''warm loops'' (1-2 MK), which are coronal loops observed in EUV wavelengths, and ''hot loops'' (>3 MK), coronal loops observed in X-rays. We found that outside sunspots, the magnetic filling factor in the solar network varies with location and is anti-correlated with the horizontal random velocity. If we accept that the observed magnetic features consist of unresolved magnetic flux tubes, this anti-correlation can be explained by the ensemble average of flux-tube motion driven by small-scale random flows. The observed data are consistent with a flux tube width of ∼77 km and horizontal flow at ∼2.6 km s{sup –1} with a spatial scale of ∼120 km. We also found that outside sunspots, there is no significant difference between warm and hot loops either in the magnetic properties (except for the inclination) or in the horizontal random velocity at their footpoints, which are identified with the Hinode X-Ray Telescope and the Transition Region and Coronal Explorer. The energy flux injected into the coronal loops by the observed photospheric motion of the magnetic fields is estimated to be 2 × 10{sup 6} erg s{sup –1} cm{sup –2}, which is the same for both warm and hot loops. This suggests that coronal properties (e.g., loop length) play a more important role in giving rise to temperature differences of active-region coronal loops than photospheric parameters.

  18. Effect of deformation ratios on grain alignment and magnetic properties of hot pressing/hot deformation Nd-Fe-B magnets

    Science.gov (United States)

    Guo, Zhaohui; Li, Mengyu; Wang, Junming; Jing, Zheng; Yue, Ming; Zhu, Minggang; Li, Wei

    2018-05-01

    The magnetic properties, microstructure and orientation degrees of hot pressing magnet and hot deformation Nd-Fe-B magnets with different deformation ratios have been investigated in this paper. The remanence (Br) and maximum magnetic energy product ((BH)max) were enhanced gradually with the deformation ratio increasing from 0% to 70%, whereas the coercivity (HCj) decreased. The scanning electron microscopy (SEM) images of fractured surfaces parallel to the pressure direction during hot deformation show that the grains tend to extend perpendicularly to the c-axes of Nd2Fe14B grains under the pressure, and the aspect ratios of the grains increase with the increase of deformation ratio. Besides, the compression stress induces the long axis of grains to rotate and the angle (θ) between c-axis and pressure direction decreases. The X-ray diffraction (XRD) patterns reveal that orientation degree improves with the increase of deformation ratio, agreeing well with the SEM results. The hot deformation magnet with a deformation ratio of 70% has the best Br and (BH)max, and the magnetic properties are as followed: Br=1.40 T, HCj=10.73 kOe, (BH)max=42.30 MGOe.

  19. Properties of nonvolatile and antibacterial bioboard produced from bamboo macromolecules by hot pressing

    Directory of Open Access Journals (Sweden)

    Shengbo Ge

    2018-03-01

    Full Text Available Employing the antibacterial property of industrial bamboo vinegar (IBV and the photocatalytic degradation of TiO2, bamboo macromolecules were pretreated and processed into nonvolatile and antibacterial bio board (NVABB. The NVABB was then analyzed by conducting Fourier-transform infrared spectroscopy, thermogravimetric analysis and differential thermal analysis. Results show that NVABB samples had average density of 0.96 g/cm3, which is appropriate for application. In terms of physical and mechanical properties, the best NVABB sample obtained from IBV, TiO2 and bamboo had an IBV pretreatment time of 10 min, 2% TiO2 and 1% bamboo charcoal. Fourier-transform infrared spectroscopy demonstrated that optimum conditions for hot pressing were a temperature of 170 °C, duration of 15 min and the addition of IBV and TiO2. Thermogravimetric analysis/differential thermal analysis curves suggest that the thermal degradation of NVABB was less than that of bamboo and that hot pressing obviously increased the thermal stability of HDBB samples. Analysis of the antimicrobial effect revealed that IBV pretreatment improves the antibacterial property of NVABB. Keywords: Industrial bamboo vinegar, Nonvolatile and antibacterial bio board, Bamboo macromolecules, Fourier-transform infrared spectroscopy, Thermogravimetric analysis/differential thermal analysis

  20. A Study on the Manufacturing Properties of Crack Self-Healing Capsules Using Cement Powder for Addition to Cement Composites

    Directory of Open Access Journals (Sweden)

    Yun-Wang Choi

    2017-01-01

    Full Text Available We fabricated crack self-healing capsules using cement powder for mixing into cement composites and evaluated the properties of the capsule manufacturing process in this study. The manufacture of the self-healing capsules is divided into core production processing of granulating cement in powder form and a coating process for creating a wall on the surfaces of the granulated cement particles. The produced capsules contain unhardened cement and can be mixed directly with the cement composite materials because they are protected from moisture by the wall material. Therefore, the untreated cement is present in the form of a capsule within the cement composite, and hydration can be induced by moisture penetrating the crack surface in the event of cracking. In the process of granulating the cement, it is important to obtain a suitable consistency through the kneading agent and to maintain the moisture barrier performance of the wall material. We can utilize the results of this study as a basis for advanced self-healing capsule technology for cement composites.

  1. Effects of Thermal Aging on Material Properties, Stress Corrosion Cracking, and Fracture Toughness of AISI 316L Weld Metal

    Science.gov (United States)

    Lucas, Timothy; Forsström, Antti; Saukkonen, Tapio; Ballinger, Ronald; Hänninen, Hannu

    2016-08-01

    Thermal aging and consequent embrittlement of materials are ongoing issues in cast stainless steels, as well as duplex, and high-Cr ferritic stainless steels. Spinodal decomposition is largely responsible for the well-known "748 K (475 °C) embrittlement" that results in drastic reductions in ductility and toughness in these materials. This process is also operative in welds of either cast or wrought stainless steels where δ-ferrite is present. While the embrittlement can occur after several hundred hours of aging at 748 K (475 °C), the process is also operative at lower temperatures, at the 561 K (288 °C) operating temperature of a boiling water reactor (BWR), for example, where ductility reductions have been observed after several tens of thousands of hours of exposure. An experimental program was carried out in order to understand how spinodal decomposition may affect changes in material properties in Type 316L BWR piping weld metals. The study included material characterization, nanoindentation hardness, double-loop electrochemical potentiokinetic reactivation (DL-EPR), Charpy-V, tensile, SCC crack growth, and in situ fracture toughness testing as a function of δ-ferrite content, aging time, and temperature. SCC crack growth rates of Type 316L stainless steel weld metal under simulated BWR conditions showed an approximate 2 times increase in crack growth rate over that of the unaged as-welded material. In situ fracture toughness measurements indicate that environmental exposure can result in a reduction of toughness by up to 40 pct over the corresponding at-temperature air-tested values. Material characterization results suggest that spinodal decomposition is responsible for the degradation of material properties measured in air, and that degradation of the in situ properties may be a result of hydrogen absorbed during exposure to the high-temperature water environment.

  2. Effect of hot-dip galvanizing processes on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel

    Science.gov (United States)

    Kuang, Chun-fu; Zheng, Zhi-wang; Wang, Min-li; Xu, Quan; Zhang, Shen-gen

    2017-12-01

    A C-Mn dual-phase steel was soaked at 800°C for 90 s and then either rapidly cooled to 450°C and held for 30 s (process A) or rapidly cooled to 350°C and then reheated to 450°C (process B) to simulate the hot-dip galvanizing process. The influence of the hot-dip galvanizing process on the microstructure and mechanical properties of 600-MPa hot-dip galvanized dual-phase steel (DP600) was investigated using optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), and tensile tests. The results showed that, in the case of process A, the microstructure of DP600 was composed of ferrite, martensite, and a small amount of bainite. The granular bainite was formed in the hot-dip galvanizing stage, and martensite islands were formed in the final cooling stage after hot-dip galvanizing. By contrast, in the case of process B, the microstructure of the DP600 was composed of ferrite, martensite, bainite, and cementite. In addition, compared with the yield strength (YS) of the DP600 annealed by process A, that for the DP600 annealed by process B increased by approximately 50 MPa because of the tempering of the martensite formed during rapid cooling. The work-hardening coefficient ( n value) of the DP600 steel annealed by process B clearly decreased because the increase of the YS affected the computation result for the n value. However, the ultimate tensile strength (UTS) and elongation ( A 80) of the DP600 annealed by process B exhibited less variation compared with those of the DP600 annealed by process A. Therefore, DP600 with excellent comprehensive mechanical properties (YS = 362 MPa, UTS = 638 MPa, A 80 = 24.3%, n = 0.17) was obtained via process A.

  3. Mechanical properties of hot-pressed Al-4.5 wt. % Cu/WC composite

    Directory of Open Access Journals (Sweden)

    Samaneh Bernoosi

    2014-12-01

    Full Text Available In this study, the elemental powders of aluminum and copper were initially subjected to mechanical alloying using an attrition ball mill under argon atmosphere to produce an Al-4.5 wt% Cu powder alloy. The WC nanoparticles were then added to the powder alloy and milled in a planetary ball mill to explore the role of the WC nanoparticles on the mechanical properties of the fabricated composite powder. The experimental results revealed that a solid solution of Al-Cu could be formed after MA and a good dispersion of the WC nanoparticles in the aluminum matrix was obtained as characterized using X-ray diffraction and scanning electron microscopy, respectively. The results of hardness and compression tests of the hot pressed composites indicated that the MA followed by the hot-press processes was successful to fabricate an alloy and a metal matrix composite with considerable mechanical properties. However, a decreasing trend in the hardness and strength of the composites with the WC contents of more than 5wt% was observed. The maximum values of 260 HV and 575 MPa were obtained for a composite containing 5 wt% of nano ceramic particles.

  4. Microstructure, Mechanical Properties, and Toughening Mechanisms of a New Hot Stamping-Bake Toughening Steel

    Science.gov (United States)

    Lin, Tao; Song, Hong-Wu; Zhang, Shi-Hong; Cheng, Ming; Liu, Wei-Jie; Chen, Yun

    2015-09-01

    In this article, the hot stamping-bake toughening process has been proposed following the well-known concept of bake hardening. The influences of the bake time on the microstructure and the mechanical properties of the hot stamped-baked part were studied by means of scanning electron microscopy, transmission electron microscopy, X-ray diffraction, and mechanical tests at room temperature. The results show that the amount of the retained austenite was nearly not changed by the bake process. Also observed were spherical Cu-rich precipitates of about 15 nm in martensite laths. According to the Orowan mechanism, their contribution of the Cu-rich precipitates to the strength is approximately 245 MPa. With the increase of the bake time, the tensile strength of the part was decreased, whereas both the ductility and the product of the tensile strength and ductility were increased then decreased. The tensile strength and ductility product and the tensile strength are as high as 21.9 GPa pct, 2086 MPa, respectively. The excellent combined properties are due to the transformation-induced plasticity effect caused by retained austenite.

  5. Fabrication of Al–TiC composites by hot consolidation technique: its microstructure and mechanical properties

    Directory of Open Access Journals (Sweden)

    Sangita Mohapatra

    2016-04-01

    Full Text Available Al-based metal matrix composites reinforced with different volume fraction of TiC particles as reinforcement was synthesized by the hot consolidation process. The titanium carbide used in this study was synthesized directly from the titanium ore (ilmenite, FeTiO3 by carbothermic reduction process through thermal plasma technique. The field emission scanning electron micrographs (FESEM reveals the homogeneous distribution of TiC particles in the Al-matrix. Enhanced Young's modulus and mechanical properties with appreciable ductility were observed in the composite samples. The significant increases in the mechanical properties of the composites demonstrate the effectiveness of the low-density TiC reinforcement.

  6. Evaluation of the mechanical properties of Niobium modified cast AISI H 13 hot work tool steel

    International Nuclear Information System (INIS)

    Noorian, A.; Kheirandish, Sh.; Saghafian, H.

    2010-01-01

    In this research, the effects of partially replacing of vanadium and molybdenum with niobium on the mechanical properties of AISIH 13 hot-work tool steel have been studied. Cast samples made of the modified new steel were homogenized and austenitized at different conditions, followed by tempering at the specified temperature ranges. Hardness, red hardness, three point bending test and Charpy impact test were carried out to evaluate the mechanical properties together with characterizing the microstructure of the modified steel using scanning electron microscope. The results show that niobium addition modifies the cast structure of Nb-alloyed steel, and increases its maximum hardness. It was found that bending strength; bending strain, impact strength, and red hardness of the modified cast steel are also higher than those of the cast H13 steel, and lower than those of the wrought H13 steel.

  7. Variation of microstructures and mechanical properties of hot heading process of super heat resisting alloy Inconel 718

    International Nuclear Information System (INIS)

    Choi, Hong Seok; Ko, Dae Chul; Kim, Byung Min

    2007-01-01

    Metal forming is the process changing shapes and mechanical properties of the workpiece without initial material reduction through plastic deformation. Above all, because of hot working carried out above recrystallization temperature can be generated large deformation with one blow, it can produce with forging complicated parts or heat resisting super alloy such as Inconel 718 has the worst forgeability. In this paper, we established optimal variation of hot heading process of the Inconel 718 used in heat resisting component and evaluated mechanical properties hot worked product. Die material is SKD61 and initial temperature is 300 .deg. C. Initial billet temperature and punch velocity changed, relatively. Friction coefficient is 0.3 as lubricated condition of hot working. CAE is carried out using DEFORM software before marking the tryout part, and it is manufactured 150 ton screw press with optimal condition. It is know that forming load was decreased according to decreasing punch velocity

  8. Structure-property relations and crack resistance at the bovine dentin-enamel junction.

    Science.gov (United States)

    Lin, C P; Douglas, W H

    1994-05-01

    The present report is a study of the fracture behavior of the dentin-enamel complex, involving enamel, dentin, and the dentin-enamel junction (DEJ), that combines experimental design, computational finite element analysis, and fractography. Seven chevron-notched short-bar bovine DEJ specimens were utilized in this study. The general plane of the DEJ was approximately perpendicular to the fracture plane. All specimens were stored at 37 degrees C and 100% relative humidity for 24 h prior to being tested. A fracture test set-up was designed for application of tensile load on the DEJ specimens to initiate a crack at the vertex of the chevron in the enamel, across the DEJ zone and into the bulk dentin. During fracture testing, a water chamber was used to avoid dehydration of the specimen. The results showed that the lower boundary value of the fracture toughness of the DEJ perpendicular to its own plane was 3.38 +/- 0.40 MN/m1.5 and 988.42 +/- 231.39 J/m2, in terms of KIC and GKC, respectively. In addition, there was an extensive plastic deformation (83 +/- 12%) collateral to the fracture process at the DEJ zone. The fractography revealed that the deviation of the crak path involved an area which was approximately 50-100 microns deep. The parallel-oriented coarse collagen bundles with diameters of 1-5 microns at the DEJ zone may play a significant role in resisting the enamel crack. This reflects the fact, that in the intact tooth, the multiple full thickness cracks commonly found in enamel do not typically cause total failure of the tooth by crack extension into the dentin.

  9. Pulsed-field gradient nuclear magnetic resonance study of transport properties of fluid catalytic cracking catalysts

    Czech Academy of Sciences Publication Activity Database

    Kortunov, P.; Vasenkov, S.; Kärger, J.; Fé Elía, M.; Perez, M.; Stöcker, M.; Papadopoulos, G. K.; Theodorou, D.; Drescher, B.; McElhiney, G.; Bernauer, B.; Krystl, V.; Kočiřík, Milan; Zikánová, Arlette; Jirglová, Hana; Berger, C.; Gläser, R.; Weitkamp, J.; Hansen, E. W.

    2005-01-01

    Roč. 23, č. 2 (2005), s. 233-237 ISSN 0730-725X Grant - others:TROCAT project - European Community(DE) G5RD-CT-2001-00520 Institutional research plan: CEZ:AV0Z40400503 Keywords : pulsed-field gradient * nuclear magnetic resonance * fluid catalytic cracking catalyst Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 1.361, year: 2005

  10. Mechanism of Solder Joint Cracks in Anisotropic Conductive Films Bonding and Solutions: Delaying Hot-Bar Lift-Up Time and Adding Silica Fillers

    Directory of Open Access Journals (Sweden)

    Shuye Zhang

    2018-01-01

    Full Text Available Micron sizes solder metallurgical joints have been applied in a thin film application of anisotropic conductive film and benefited three general advantages, such as lower joint resistance, higher power handling capability, and reliability, when compared with pressure based contact of metal conductor balls. Recently, flex-on-board interconnection has become more and more popular for mobile electronic applications. However, crack formation of the solder joint crack was occurred at low temperature curable acrylic polymer resins after bonding processes. In this study, the mechanism of SnBi58 solder joint crack at low temperature curable acrylic adhesive was investigated. In addition, SnBi58 solder joint cracks can be significantly removed by increasing the storage modulus of adhesives instead of coefficient of thermal expansion. The first approach of reducing the amount of polymer rebound can be achieved by using an ultrasonic bonding method to maintain a bonding pressure on the SnBi58 solder joints cooling to room temperature. The second approach is to increase storage modulus of adhesives by adding silica filler into acrylic polymer resins to prevent the solder joint from cracking. Finally, excellent acrylic based SnBi58 solder joints reliability were obtained after 1000 cycles thermal cycling test.

  11. Effects of hot rolling and titanium content on the microstructure and mechanical properties of high boron Fe–B alloys

    International Nuclear Information System (INIS)

    He, Lin; Liu, Ying; Li, Jun; Li, Binghong

    2012-01-01

    Highlights: ► The content of B is 1.8 wt.% in the high boron Fe–B alloys. ► Hot-rolling improves the mechanical properties, especially the elongation. ► The Ti content affects the microstructure and mechanical properties. ► Eutectic boride can be eliminated when the atomic ratio of Ti/B is no less than 0.5. ► Alloy exhibits balanced mechanical properties when the atomic ratio of Ti/B is 0.5. -- Abstract: High boron Fe–B alloys (1.8 wt.% B) with different titanium contents are fabricated by Vacuum Induction Melting (VIM) technique. The integrated mechanical properties of the as-cast alloys are poor, especially the ductility. In this investigation, hot-rolling technology is used to improve the microstructure and mechanical properties. The microstructure analysis shows that hot rolling can reduce the size and improve the distribution of the reinforcements. The mechanical properties testing indicates that the yield strength is unchanged basically, but the tensile strength and elongation are improved greatly by hot rolling, especially the elongation. The content of titanium also has great effects on the microstructures and mechanical properties of the hot-rolled alloys. For the hot-rolled alloys, with the titanium content increasing, the ultimate tensile strength and yield strength first decrease slightly and then increase. The elongation and impact toughness are improved significantly. In particular, when the atomic ratio of Ti to B is 0.5, the reinforcements are almost entirely TiB 2 and uniformly distributed in the Fe-matrix. The ternary Fe–B–Ti alloy exhibits balanced mechanical properties: yield strength, ultimate tensile strength, elongation and impact toughness are 334 MPa, 602 MPa, 16.2% and 213 kJ/m 2 , respectively.

  12. Metabolomics coupled with similarity analysis advances the elucidation of the cold/hot properties of traditional Chinese medicines.

    Science.gov (United States)

    Jia, Yan; Zhang, Zheng-Zheng; Wei, Yu-Hai; Xue-Mei, Qin; Li, Zhen-Yu

    2017-08-01

    It recently becomes an important and urgent mission for modern scientific research to identify and explain the theory of traditional Chinese medicine (TCM), which has been utilized in China for more than four millennia. Since few works have been contributed to understanding the TCM theory, the mechanism of actions of drugs with cold/hot properties remains unclear. In the present study, six kinds of typical herbs with cold or hot properties were orally administered into mice, and serum and liver samples were analyzed using an untargeted nuclear magnetic resonance (NMR) based metabolomics approach coupled with similarity analysis. This approach was performed to identify and quantify changes in metabolic pathways to elucidate drug actions on the treated mice. Our results showed that those drugs with same property exerted similar effects on the metabolic alterations in mouse serum and liver samples, while drugs with different property showed different effects. The effects of herbal medicines with cold/hot properties were exerted by regulating the pathways linked to glycometabolism, lipid metabolism, amino acids metabolism and other metabolic pathways. The results elucidated the differences and similarities of drugs with cold/hot properties, providing useful information on the explanation of medicinal properties of these TCMs. Copyright © 2017 China Pharmaceutical University. Published by Elsevier B.V. All rights reserved.

  13. Sensitivity of inertial confinement fusion hot spot properties to the deuterium-tritium fuel adiabat

    Energy Technology Data Exchange (ETDEWEB)

    Melvin, J.; Lim, H.; Rana, V.; Glimm, J. [Department of Applied Mathematics and Statistics, Stony Brook University, Stony Brook, New York 11794-3600 (United States); Cheng, B.; Sharp, D. H.; Wilson, D. C. [Los Alamos National Laboratory, Los Alamos, New Mexico 87545 (United States)

    2015-02-15

    We determine the dependence of key Inertial Confinement Fusion (ICF) hot spot simulation properties on the deuterium-tritium fuel adiabat, here modified by addition of energy to the cold shell. Variation of this parameter reduces the simulation to experiment discrepancy in some, but not all, experimentally inferred quantities. Using simulations with radiation drives tuned to match experimental shots N120321 and N120405 from the National Ignition Campaign (NIC), we carry out sets of simulations with varying amounts of added entropy and examine the sensitivities of important experimental quantities. Neutron yields, burn widths, hot spot densities, and pressures follow a trend approaching their experimentally inferred quantities. Ion temperatures and areal densities are sensitive to the adiabat changes, but do not necessarily converge to their experimental quantities with the added entropy. This suggests that a modification to the simulation adiabat is one of, but not the only explanation of the observed simulation to experiment discrepancies. In addition, we use a theoretical model to predict 3D mix and observe a slight trend toward less mixing as the entropy is enhanced. Instantaneous quantities are assessed at the time of maximum neutron production, determined dynamically within each simulation. These trends contribute to ICF science, as an effort to understand the NIC simulation to experiment discrepancy, and in their relation to the high foot experiments, which features a higher adiabat in the experimental design and an improved neutron yield in the experimental results.

  14. Sensitivity of inertial confinement fusion hot spot properties to the deuterium-tritium fuel adiabat

    International Nuclear Information System (INIS)

    Melvin, J.; Lim, H.; Rana, V.; Glimm, J.; Cheng, B.; Sharp, D. H.; Wilson, D. C.

    2015-01-01

    We determine the dependence of key Inertial Confinement Fusion (ICF) hot spot simulation properties on the deuterium-tritium fuel adiabat, here modified by addition of energy to the cold shell. Variation of this parameter reduces the simulation to experiment discrepancy in some, but not all, experimentally inferred quantities. Using simulations with radiation drives tuned to match experimental shots N120321 and N120405 from the National Ignition Campaign (NIC), we carry out sets of simulations with varying amounts of added entropy and examine the sensitivities of important experimental quantities. Neutron yields, burn widths, hot spot densities, and pressures follow a trend approaching their experimentally inferred quantities. Ion temperatures and areal densities are sensitive to the adiabat changes, but do not necessarily converge to their experimental quantities with the added entropy. This suggests that a modification to the simulation adiabat is one of, but not the only explanation of the observed simulation to experiment discrepancies. In addition, we use a theoretical model to predict 3D mix and observe a slight trend toward less mixing as the entropy is enhanced. Instantaneous quantities are assessed at the time of maximum neutron production, determined dynamically within each simulation. These trends contribute to ICF science, as an effort to understand the NIC simulation to experiment discrepancy, and in their relation to the high foot experiments, which features a higher adiabat in the experimental design and an improved neutron yield in the experimental results

  15. Sensitivity of inertial confinement fusion hot spot properties to the deuterium-tritium fuel adiabat

    Science.gov (United States)

    Melvin, J.; Lim, H.; Rana, V.; Cheng, B.; Glimm, J.; Sharp, D. H.; Wilson, D. C.

    2015-02-01

    We determine the dependence of key Inertial Confinement Fusion (ICF) hot spot simulation properties on the deuterium-tritium fuel adiabat, here modified by addition of energy to the cold shell. Variation of this parameter reduces the simulation to experiment discrepancy in some, but not all, experimentally inferred quantities. Using simulations with radiation drives tuned to match experimental shots N120321 and N120405 from the National Ignition Campaign (NIC), we carry out sets of simulations with varying amounts of added entropy and examine the sensitivities of important experimental quantities. Neutron yields, burn widths, hot spot densities, and pressures follow a trend approaching their experimentally inferred quantities. Ion temperatures and areal densities are sensitive to the adiabat changes, but do not necessarily converge to their experimental quantities with the added entropy. This suggests that a modification to the simulation adiabat is one of, but not the only explanation of the observed simulation to experiment discrepancies. In addition, we use a theoretical model to predict 3D mix and observe a slight trend toward less mixing as the entropy is enhanced. Instantaneous quantities are assessed at the time of maximum neutron production, determined dynamically within each simulation. These trends contribute to ICF science, as an effort to understand the NIC simulation to experiment discrepancy, and in their relation to the high foot experiments, which features a higher adiabat in the experimental design and an improved neutron yield in the experimental results.

  16. Mechanical properties and porosity of dental glass-ceramics hot-pressed at different temperatures

    Directory of Open Access Journals (Sweden)

    Carla Castiglia Gonzaga

    2008-09-01

    Full Text Available The objective of this work was to evaluate biaxial-flexural-strength (σf, Vickers hardness (HV, fracture toughness (K Ic, Young's modulus (E, Poisson's ratio (ν and porosity (P of two commercial glass-ceramics, Empress (E1 and Empress 2 (E2, as a function of the hot-pressing temperature. Ten disks were hot-pressed at 1065, 1070, 1075 and 1080 °C for E1; and at 910, 915, 920 and 925 °C for E2. The porosity was measured by an image analyzer software and s f was determined using the piston-on-three-balls method. K Ic and HV were determined by an indentation method. Elastic constants were determined by the pulse-echo method. For E1 samples treated at different temperatures, there were no statistical differences among the values of all evaluated properties. For E2 samples treated at different temperatures, there were no statistical differences among the values of σf, E, and ν, however HV and K Ic were significantly higher for 910 and 915 °C, respectively. Regarding P, the mean value obtained for E2 for 925 °C was significantly higher compared to other temperatures.

  17. Application of heat treatment and hot extrusion processes to improve mechanical properties of the AZ91 alloy

    Directory of Open Access Journals (Sweden)

    T. Reguła

    2010-04-01

    Full Text Available The main aim of this paper is to evaluate the effects of hot working (extrusion and hest treatment on room temperature mechanical properties of magnesium-based AZ91 alloy. The results were compared with as-cast condition. The examined material had been obtained by gravity casting to permanent moulds and subsequently subjected to heat treatment and/or processed by extrusion at 648 K. Microstructural and mechanical properties of properly prepared specimens were studied. Rm, Rp02 and A5 were determined from tensile tests. Brinell hardness tests were also conducted. The research has shown that hot working of AZ91 alloy provides high mechanical properties unattainable by cast material subjected to heat-treatment. The investigated alloy subjected to hot working and subsequently heat-treated has doubled its strength and considerably improved the elongation - compared with the as-cast material.

  18. Characterization of fracture patterns and hygric properties for moisture flow modelling in cracked concrete

    DEFF Research Database (Denmark)

    Rouchier, Simon; Janssen, Hans; Rode, Carsten

    2012-01-01

    porous media. Digital Image Correlation was performed during the fracturing of concrete samples, in which moisture uptake was then monitored using X-ray radiography. Finite-element simulations were then performed based on the measurements of the fracture patterns, in order to recreate the measured......Several years after their installation, building materials such as concrete present signs of ageing in the form of fractures covering a wide range of sizes, from microscopic to macroscopic cracks. All sizes of fractures can have a strong influence on heat and moisture flow in the building envelope...

  19. Corrosion cracking

    International Nuclear Information System (INIS)

    Goel, V.S.

    1985-01-01

    This book presents the papers given at a conference on alloy corrosion cracking. Topics considered at the conference included the effect of niobium addition on intergranular stress corrosion cracking, corrosion-fatigue cracking in fossil-fueled-boilers, fracture toughness, fracture modes, hydrogen-induced thresholds, electrochemical and hydrogen permeation studies, the effect of seawater on fatigue crack propagation of wells for offshore structures, the corrosion fatigue of carbon steels in seawater, and stress corrosion cracking and the mechanical strength of alloy 600

  20. Study of fatigue crack propagation in laminated metal composites alluminium 1100/alluminium 2024

    International Nuclear Information System (INIS)

    Tavares, R.I.

    1984-01-01

    A study has been made of fatigue crack propagation in laminated metal composites with different volume fraction of constituents. The composites were produced by hot rolling, combining 1100 and 2024 aluminum alloys in crack divider orientation. Mechanical and metallurgical properties of the composites and original alloys sheets have been evaluated. Paris type relationship, corresponding to stage II of fatigue crack propagation curves, has been determined by two different methods, wich have shown to be equivalent. A computer software in FORTRAN language was developed for all the mathematical manipulation of fatigue data including statistical analysis and graphics. (Author) [pt

  1. Processing and properties of calcium phosphates bioceramics by hot isostatic pressing

    Directory of Open Access Journals (Sweden)

    Boilet Laurent

    2013-11-01

    Full Text Available Stoichiometric β-tricalcium phosphate (β-TCP, hydroxyapatite (HA and biphasic calcium phosphate (TCP/HA 60/40 %wt, BCP40 powders were synthesized by chemical precipitation of aqueous solutions of diammonium phosphate and calcium nitrate. After a calcination treatment and a milling step, powders were shaped by slip-casting. The sintering temperature effect on the density and the average grain size was investigated. By natural sintering, densities between 98 and 99.8% were obtained. Hot Isostatic Pressing (HIP treatment was carried out after a pre-sintering of these materials. Transparent or translucent samples were obtained, indicating a relative density very close to the theoretical value (>99.9%. Mechanical properties (three-point bending strength, fracture toughness, Young's modulus and Vickers hardness were measured on hipped materials with similar grain size (∼0.7μm.

  2. Fabrication of dense yttrium oxyfluoride ceramics by hot pressing and their mechanical, thermal, and electrical properties

    Science.gov (United States)

    Tahara, Ryuki; Tsunoura, Toru; Yoshida, Katsumi; Yano, Toyohiko; Kishi, Yukio

    2018-06-01

    Excellent corrosion-resistant materials have been strongly required to reduce particle contamination during the plasma process in semiconductor production. Yttrium oxyfluoride can be a candidate as highly corrosion-resistant material. In this study, three types of dense yttrium oxyfluoride ceramics with different oxygen contents, namely, YOF, Y5O4F7 and Y5O4F7 + YF3, were fabricated by hot pressing, and their mechanical, thermal, and electrical properties were evaluated. Y5O4F7 ceramics showed an excellent thermal stability up to 800 °C, a low loss factor, and volume resistivity comparable to conventional plasma-resistant oxides, such as Y2O3. From these results, yttrium oxyfluoride ceramics are strongly suggested to be used as electrostatic chucks in semiconductor production.

  3. STUDY OF THE MECHANICAL PROPERTIES OF INCONEL 718 SUPERALLOY AFTER HOT TENSILE TESTS

    Directory of Open Access Journals (Sweden)

    Tarcila Sugahara

    2014-10-01

    Full Text Available This research work investigated some important mechanical properties of Inconel 718 superalloy using hot tensile tests like conventional yield strength to 0.2% strain (σe , ultimate strength (σr , and specific elongation (εu . Samples were strained to failure at temperatures of 600°C, 650°C, 700°C, 750°C, 800°C and 850°C and strain rate of 0.5 mm/min (2 × 10–4 s–1 according to ASTM E-8. The results showed higher values σe of yield strength at 700°C, this anomalous behavior can be attributed to the presence of hardening precipitates as observed in the TTT diagram of superalloy Inconel 718. Examination of the sample’s surfaces tensile fracture showed that with increasing temperature test the actuating mechanism changes from intergranular fracture to coalescence of the microcavities.

  4. Effects of asphalt rejuvenator on thermal and mechanical properties on oxidized hot mixed asphalt pavements

    Science.gov (United States)

    Farace, Nicholas A.; Buttlar, William G.; Reis, Henrique

    2016-04-01

    The utilization of asphalt rejuvenator, and its effectiveness for restoring thermal and mechanical properties was investigated via Disk-shaped Compact Tension (DC(T)) and acoustic emission (AE) testing for determining mechanical properties and embrittlement temperatures of the mixtures. During the DC(T) testing the fracture energies and peak loads were used to measure the resistance of the rejuvenated asphalt to low temperature cracking. The AE testing monitored the acoustic emission activity while the specimens were cooled from room temperature to -40 °C to estimate the temperature at which thermal cracking began (i.e. the embrittlement temperature). First, a baseline response was obtained by obtaining the mechanical and thermal response of virgin HMA samples and HMA samples that had been exposed to oxidative aging for 36 hours at 135°C. The results showed the virgin samples had much higher peak loads and fracture energies than the 36 hours aged samples. Acoustic Emission showed similar results with the virgin samples having embrittlement temperatures 10 °C cooler than the 36 hours aged specimens. Then, overaged for 36 hours specimens were treated different amounts of rejuvenator (10%, 15%, and 20% by weight of binder content) and left to dwell for increased amount of time periods varying from one to eight weeks. It was observed that the AE results showed an improvement of embrittlement temperature with increasing with the dwell times. The 8 weeks specimens had cooler embrittlement temperatures than the virgin specimens. Finally, the low temperature effects on fracture energy and peak load of the rejuvenated asphalt was investigated. Rejuvenator was applied (10% by weight of binder) to specimens aged 36 hours at 135 °C, and the dwell time was varied from 1 to 4 weeks. The results showed that the peak loads were restored to levels of the virgin specimens, and the fracture energies improved to levels beyond that of the virgin specimens. The results also showed a

  5. Hot soup! Correlating the severity of liquid scald burns to fluid and biomedical properties.

    Science.gov (United States)

    Loller, Cameron; Buxton, Gavin A; Kerzmann, Tony L

    2016-05-01

    Burns caused by hot drinks and soups can be both debilitating and costly, especially to pediatric and geriatric patients. This research is aimed at better understanding the fluid properties that can influence the severity of skin burns. We use a standard model which combines heat transfer and biomedical equations to predict burn severity. In particular, experimental data from a physical model serves as the input to our numerical model to determine the severity of scald burns as a consequence of actual fluid flows. This technique enables us to numerically predict the heat transfer from the hot soup into the skin, without the need to numerically estimate the complex fluid mechanics and thermodynamics of the potentially highly viscous and heterogeneous soup. While the temperature of the soup is obviously is the most important fact in determining the degree of burn, we also find that more viscous fluids result in more severe burns, as the slower flowing thicker fluids remain in contact with the skin for longer. Furthermore, other factors can also increase the severity of burn such as a higher initial fluid temperature, a greater fluid thermal conductivity, or a higher thermal capacity of the fluid. Our combined experimental and numerical investigation finds that for average skin properties a very viscous fluid at 100°C, the fluid must be in contact with the skin for around 15-20s to cause second degree burns, and more than 80s to cause a third degree burn. Copyright © 2015 Elsevier Ltd and ISBI. All rights reserved.

  6. Hot Press as a Sustainable Direct Recycling Technique of Aluminium: Mechanical Properties and Surface Integrity.

    Science.gov (United States)

    Yusuf, Nur Kamilah; Lajis, Mohd Amri; Ahmad, Azlan

    2017-08-03

    Meltless recycling technique has been utilized to overcome the lack of primary resources, focusing on reducing the usage of energy and materials. Hot press was proposed as a novel direct recycling technique which results in astoundingly low energy usage in contrast with conventional recycling. The aim of this study is to prove the technical feasibility of this approach by characterizing the recycled samples. For this purpose, AA6061 aluminium chips were recycled by utilizing hot press process under various operating temperature (T s = 430, 480, and 530 °C) and holding times (t s = 60, 90, and 120 min). The maximum mechanical properties of recycled chip are Ultimate tensile strength (UTS) = 266.78 MPa, Elongation to failure (ETF) = 16.129%, while, for surface integrity of the chips, the calculated microhardness is 81.744 HV, exhibited at T s = 530 °C and t s = 120 min. It is comparable to theoretical AA6061 T4-temper where maximum UTS and microhardness is increased up to 9.27% and 20.48%, respectively. As the desired mechanical properties of forgings can only be obtained by means of a final heat treatment, T5-temper, aging after forging process was employed. Heat treated recycled billet AA6061 (T5-temper) are considered comparable with as-received AA6061 T6, where the value of microhardness (98.649 HV) at 175 °C and 120 min of aging condition was revealed to be greater than 3.18%. Although it is quite early to put a base mainly on the observations in experimental settings, the potential for significant improvement offered by the direct recycling methods for production aluminium scrap can be clearly demonstrated. This overtures perspectives for industrial development of solid state recycling processes as environmentally benign alternatives of current melting based practices.

  7. Nanocomposites biodegradable coating on BOPET films to enhance hot seal strength properties

    Energy Technology Data Exchange (ETDEWEB)

    Barbaro, G., E-mail: giovannibarbaro@email.it; Galdi, M. R., E-mail: mrgaldi@unisa.it; Di Maio, L., E-mail: ldimaio@unisa.it; Incarnato, L., E-mail: lincarnato@unisa.it [Industrial Engineering Department, University of Salerno, Via Giovanni Paolo II 132, 84084 Fisciano (Italy)

    2015-12-17

    The coating technology is a strategic solution to improve the properties of flexible packaging films. Indeed, additional functional layers are often designed and added as coating on the substrate, in order to improve the characteristic of the flexible packaging and to meet the requirements for the desired gas or vapour barrier, for adhesion and sealing, or for improving the film printability, its aesthetics and durability. Moreover, this technology allows to functionalize a polymeric substrate applying materials with different chemistry, rheology, thermal and structural characteristics. BOPET films are widely used for food packaging applications thanks to their good gas barrier and mechanical properties, high transparency and for the excellent printability. In regard to sealing performance, BOPET films show poor sealing properties so they are mostly submitted to lamination processes with polyethylene. Nevertheless, this solution compromises the PET recyclability and influences the gas permeability of the multilayer PET based structures. The aim of this work is to investigate on the effect of nanocomposite biodegradable coatings for BOPET substrates in enhancing the heat sealing strength of eco-compatible PET/PLA films. At this regards, different percentages of Cloisite C30B (0%, 2% and 4%{sub wt/wt}) have been added to PLA by solution intercalation technique and the nanocomposite biodegradable materials produced have been applied on BOPET commercial films by casting. The BOPET coated films have been characterized in order to evaluate the heat sealing strength and the mechanical, gas permeability and surface properties. The results have shown that the addition of nanoclay in PLA coating significantly enhance the hot tack properties of the PET/PLA system produced, while the oxygen and water vapour permeability are slightly increased if compared to pure BOPET films.

  8. Nanocomposites biodegradable coating on BOPET films to enhance hot seal strength properties

    International Nuclear Information System (INIS)

    Barbaro, G.; Galdi, M. R.; Di Maio, L.; Incarnato, L.

    2015-01-01

    The coating technology is a strategic solution to improve the properties of flexible packaging films. Indeed, additional functional layers are often designed and added as coating on the substrate, in order to improve the characteristic of the flexible packaging and to meet the requirements for the desired gas or vapour barrier, for adhesion and sealing, or for improving the film printability, its aesthetics and durability. Moreover, this technology allows to functionalize a polymeric substrate applying materials with different chemistry, rheology, thermal and structural characteristics. BOPET films are widely used for food packaging applications thanks to their good gas barrier and mechanical properties, high transparency and for the excellent printability. In regard to sealing performance, BOPET films show poor sealing properties so they are mostly submitted to lamination processes with polyethylene. Nevertheless, this solution compromises the PET recyclability and influences the gas permeability of the multilayer PET based structures. The aim of this work is to investigate on the effect of nanocomposite biodegradable coatings for BOPET substrates in enhancing the heat sealing strength of eco-compatible PET/PLA films. At this regards, different percentages of Cloisite C30B (0%, 2% and 4% wt/wt ) have been added to PLA by solution intercalation technique and the nanocomposite biodegradable materials produced have been applied on BOPET commercial films by casting. The BOPET coated films have been characterized in order to evaluate the heat sealing strength and the mechanical, gas permeability and surface properties. The results have shown that the addition of nanoclay in PLA coating significantly enhance the hot tack properties of the PET/PLA system produced, while the oxygen and water vapour permeability are slightly increased if compared to pure BOPET films

  9. Nanocomposites biodegradable coating on BOPET films to enhance hot seal strength properties

    Science.gov (United States)

    Barbaro, G.; Galdi, M. R.; Di Maio, L.; Incarnato, L.

    2015-12-01

    The coating technology is a strategic solution to improve the properties of flexible packaging films. Indeed, additional functional layers are often designed and added as coating on the substrate, in order to improve the characteristic of the flexible packaging and to meet the requirements for the desired gas or vapour barrier, for adhesion and sealing, or for improving the film printability, its aesthetics and durability. Moreover, this technology allows to functionalize a polymeric substrate applying materials with different chemistry, rheology, thermal and structural characteristics. BOPET films are widely used for food packaging applications thanks to their good gas barrier and mechanical properties, high transparency and for the excellent printability. In regard to sealing performance, BOPET films show poor sealing properties so they are mostly submitted to lamination processes with polyethylene. Nevertheless, this solution compromises the PET recyclability and influences the gas permeability of the multilayer PET based structures. The aim of this work is to investigate on the effect of nanocomposite biodegradable coatings for BOPET substrates in enhancing the heat sealing strength of eco-compatible PET/PLA films. At this regards, different percentages of Cloisite C30B (0%, 2% and 4%wt/wt) have been added to PLA by solution intercalation technique and the nanocomposite biodegradable materials produced have been applied on BOPET commercial films by casting. The BOPET coated films have been characterized in order to evaluate the heat sealing strength and the mechanical, gas permeability and surface properties. The results have shown that the addition of nanoclay in PLA coating significantly enhance the hot tack properties of the PET/PLA system produced, while the oxygen and water vapour permeability are slightly increased if compared to pure BOPET films.

  10. Manufacturing and mechanical property test of the large-scale oxide dispersion strengthened martensitic mother tube by hot isostatic pressing and hot extrusion process

    International Nuclear Information System (INIS)

    Narita, Takeshi; Ukai, Shigeharu; Kaito, Takeji; Ohtsuka, Satoshi; Fujiwara, Masayuki

    2003-09-01

    Mass production capability of Oxide Dispersion Strengthened (ODS) ferritic steel cladding (9Cr) is evaluated in the Phase II of the Feasibility Studies on Commercialized Fast Reactor Cycle System. The cost for manufacturing mother tube is a dominant factor in the total cost for manufacturing ODS ferritic cladding. In this study, the large-scale 9Cr-ODS martensitic mother tube was produced by overseas supplier with mass production equipments for commercialized ODS steels. The process of manufacturing the ODS mother tube consists of raw material powder production, mechanical alloying by high energy ball mill, hot isostatic pressing(HIP), and hot extrusion. Following results were obtained in this study. (1) Micro structure of the ODS steels is equivalent to that of domestic products, and fine oxides are uniformly distributed. The mechanical alloying by large capacity (1 ton) ball mill can be satisfactorily carried out. (2) A large scale mother tube (65 mm OD x 48 mm ID x 10,000 mm L), which can produce about 60 pieces of 3 m length ODS ferritic claddings by four times cold rolling, have been successfully manufactured through HIP and Hot Extrusion process. (3) Rough surface of the mother tubes produced in this study can be improved by selecting the reasonable hot extrusion condition. (4) Hardness and tensile strength of the manufactured ODS steels are lower than domestic products with same chemical composition. This is owing to the high aluminum content in the product, and those properties could be improved by decreasing the aluminum content in the raw material powder. (author)

  11. Microstructural development under interrupted hot deformation and the mechanical properties of a cast Mg–Gd–Y–Zr alloy

    Energy Technology Data Exchange (ETDEWEB)

    Xiao, Zhenyu [Educational Key Laboratory of Nonferrous Metal Materials Science and Engineering, School of Materials Science and Engineering, Central South University, Changsha 410083 (China); Yang, Xuyue [Educational Key Laboratory of Nonferrous Metal Materials Science and Engineering, School of Materials Science and Engineering, Central South University, Changsha 410083 (China); Institute for Materials Microstructure, Central South University, Changsha 410083 (China); Yang, Yi; Zhang, Zhirou; Zhang, Duxiu; Li, Yi [Educational Key Laboratory of Nonferrous Metal Materials Science and Engineering, School of Materials Science and Engineering, Central South University, Changsha 410083 (China); Sakai, Taku [UEC Tokyo (The University of Electro-Communications), Chofu, Tokyo 182-8585 (Japan)

    2016-01-15

    Microstructural development under interrupted hot deformation of a cast Mg–Gd–Y–Zr alloy was investigated by optical microscopy (OM) and electron backscattering diffraction (EBSD) technology and the resultant mechanical properties were detected through tensile tests at room temperature. Ultrafine grains (UFGs) were remarkably developed under the condition of interrupted hot forging, resulting in an improvement of ambient mechanical properties. The basal texture was weakened by an effective increase of the volume fraction of UFGs under interrupted hot forging. These resulted in an improvement of tensile ductility with little or no drop in strength, i.e. the volume fraction of UFGs was raised from 30% to 70%, leading to an increase of the ambient tensile elongation from 15% to 23%.

  12. Mechanical and thermal expansion properties of β-eucryptite prepared by sol-gel methods and hot pressing

    International Nuclear Information System (INIS)

    Xia, L.; Wen, G.W.; Qin, C.L.; Wang, X.Y.; Song, L.

    2011-01-01

    Research highlights: → Dense LAS glass-ceramics were fabricated by sol-gel and hot pressing technique. → The LAS glass-ceramics have relative good mechanical properties. → The negative thermal expansion behavior of LAS glass-ceramics was investigated. -- Abstract: The microstructures, mechanical properties and thermal expansion behavior of monolithic lithium aluminosilicate glass-ceramics, prepared by sol-gel method and hot pressing, were investigated by using X-ray diffraction, scanning and transmission electron microscopies, three-point bend tests and dilatometry. β-eucryptite appeared as main phase in the monolithic lithium aluminosilicate glass-ceramics. The glass ceramics exhibited high relative densities and the average flexural strength and fracture toughness values were 154 MPa and 2.46 MPa m 1/2 , respectively. The lithium aluminosilicate glass-ceramics hot pressed 1300 and 1350 o C demonstrated negative coefficient of thermal expansion, which was affected by amount and type of crystalline phases.

  13. Hot cracking of welded joints of the 7CrMoVTiB 10-10 (T/P24) steel

    Energy Technology Data Exchange (ETDEWEB)

    Adamiec, J, E-mail: janusz.adamiec@polsl.pl [Department of Materials Science, Silesian University of Technology, Krasinskiego 8, 40-019 Katowice (Poland)

    2011-05-15

    Bainitic steel 7CrMoVTiB10-10 is one the newest steels for waterwalls of modern industrial boilers. In Europe, attempts have been made to make butt welded joints of pipes made of this steel of the diameter up to 51 mm and thickness up to 8 mm. Many cracks have been observed in the welded joint, both during welding and transport and storage. The reasons of cracking and the prevention methods have not been investigated. No comprehensive research is carried out in Europe in order to automate the welding process of the industrial boiler elements made of modern bainitic steel, such as 7CrMoVTiB10-10. There is no information about its overall, operative and local weldability, influence of heat treatment, as well as about resistance of the joints to cracking during welding and use. The paper presents experience of Energoinstal SA from development of technology and production of waterwalls of boilers made of the 7CrMoVTiB 10-10 steel on a multi-head automatic welder for submerged arc welding.

  14. Statistical properties of laser hot spots produced by a random phase plate

    International Nuclear Information System (INIS)

    Rose, H.A.; DuBois, D.F.

    1993-01-01

    A quantitative theory of laser hot spots, which control plasma instabilities in real laser--plasma interactions, is presented in the case of random phase plate (RPP) optics. It is shown that the probability density of intense hot spots with intensity I, P hot (I), is given by P hot (I)∼(I/I 0 2 )exp(-I/I 0 ) where I 0 is the average intensity, and that the detailed amplitude and phase variation of the laser field in the vicinity of an intense hot spot is uniquely specified by the optics and is deterministic. These hot spots may be the source of below threshold stimulated Raman scattering (SRS) and its variation with I 0 is shown to be super exponential. A brief preview of a quantitative nonlinear theory of hot-spot-induced laser filamentation is presented

  15. Properties of hot luminous stars; Proceedings of the First Boulder-Munich Workshop, Boulder, CO, Aug. 6-11, 1988

    International Nuclear Information System (INIS)

    Garmany, C.D.

    1990-01-01

    Various papers on the properties of hot luminous stars are presented. Individual topics addressed include: problems in photometry of early-type stars; digital optical morphology of OB spectra; massive-star content of the Magellanic Clouds; observations of massive OB stars; LSS 3074, a new double-lined early O-type binary; non-LTE line blanketing with elements 1-28; non-LTE analysis of four PG1159 stars; rescaling method for model atmospheres of hot stars; stellar wind albedo effects on hot photospheres; atomic data and models for hot star abundance determinations; ring nebulae analysis as a probe for WR atmospheres; coordinated observations of P Cygni; radiation-driven winds of hot luminous stars; winds of O stars: velocities and ionization; methods of radiative transfer in expanding atmospheres; mass loss from extragalactic O stars; H-alpha observations of O- and B-type stars; applicability of steady models for hot-star winds; mass of the O6Iaf star HD 153919; stellar winds in Beta Lyrae; models of WR stars; observational abundances of WR stars, the all-variable WC7 binary HD193793

  16. Structure and Optical Properties of the Atmospheric Boundary Layer over Dusty Hot Deserts

    Science.gov (United States)

    Chalermthai, B.; Al Marzooqi, M.; Basha, G.; Ouarda, T.; Armstrong, P.; Molini, A.

    2014-12-01

    Strong sensible heat fluxes and deep turbulent mixing - together with marked dustiness and a low substrate water content - represent a characteristic signature of the atmospheric boundary layer (ABL) over hot deserts, resulting in "thicker" mixing layers and peculiar optical properties. Beside these main common features however, desert boundary layers present extremely complex local structures that have been scarcely addressed in the literature, and whose understanding is essential in modeling processes such as transport and deposition of dust and pollutants, local wind fields, turbulent fluxes and their impacts on the sustainable development, human health and solar energy harvesting in these regions. In this study, we explore the potential of the joint usage of Lidar Ceilometer backscattering profiles and sun-photometer optical depth retrievals to quantitatively determine the vertical aerosol profile over dusty hot desert regions. Toward this goal, we analyze a continuous record of observations of the atmospheric boundary layer height from a single lens LiDAR ceilometer operated at Masdar Institute Field Station (24.4425N 54.6163E, Abu Dhabi, United Arab Emirates), starting March 2013, and the concurrent measurements of aerosol optical depth derived independently from the Masdar Institute AERONET sun-photometer. The main features of the desert ABL are obtained from the ceilometer range corrected backscattering profiles through bi-dimensional clustering technique we developed as a modification of the recently proposed single-profile clustering method, and therefore "directly" and "indirectly" calibrated to obtain a full diurnal cycle climatology of the aerosol optical depth and aerosol profiles. The challenges and the advantages of applying a similar methodology to the monitoring of aerosols and dust over hyper-arid regions are also discussed, together with the issues related to the sensitivity of commercial ceilometers to changes in the solar background.

  17. Improvement of Weldment Properties by Hot Forming Quenching of Friction Stir Welded TWB Sheet

    Directory of Open Access Journals (Sweden)

    Dae-Hoon Ko

    2014-04-01

    Full Text Available The purpose of this study is to improve the mechanical properties and formability of friction stir welded tailor-welded blanks (TWBs of Al6061 alloy with a new forming method called hot forming quenching (HFQ in which solid-solution heat-treated aluminum sheets are formed at elevated temperature. Forming and quenching during HFQ are simultaneously performed with the forming die for the solid-solution heat-treated sheet. In this study, specimens of aluminum TWBs were prepared by friction stir welding (FSW with a butt joint. The effectiveness of FSW joining was evaluated by observation of the macrostructure for different sheet thicknesses. In order to evaluate the formability of TWBs by HFQ, a hemisphere dome stretching test of the limit dome height achieved without specimen failure was performed with various tool temperatures. A Vickers test was also performed to measure weldment hardness as a function of position. The formability and mechanical properties of products formed by HFQ are compared with those formed by conventional forming methods, demonstrating the suitability of HFQ for sheet metal forming of friction stir welded TWBs.

  18. Ionic structures and transport properties of hot dense W and U plasmas

    Science.gov (United States)

    Hou, Yong; Yuan, Jianmin

    2016-10-01

    We have combined the average-atom model with the hyper-netted chain approximation (AAHNC) to describe the electronic and ionic structure of uranium and tungsten in the hot dense matter regime. When the electronic structure is described within the average-atom model, the effects of others ions on the electronic structure are considered by the correlation functions. And the ionic structure is calculated though using the hyper-netted chain (HNC) approximation. The ion-ion pair potential is calculated using the modified Gordon-Kim model based on the electronic density distribution in the temperature-depended density functional theory. And electronic and ionic structures are determined self-consistently. On the basis of the ion-ion pair potential, we perform the classical (CMD) and Langevin (LMD) molecular dynamics to simulate the ionic transport properties, such as ionic self-diffusion and shear viscosity coefficients, through the ionic velocity correlation functions. Due that the free electrons become more and more with increasing the plasma temperature, the influence of the electron-ion collisions on the transport properties become more and more important.

  19. A study on improving mechanical properties of porous HA tissue engineering scaffolds by hot isostatic pressing

    International Nuclear Information System (INIS)

    Zhao Jing; Xiao Suguang; Lu Xiong; Wang Jianxin; Weng Jie

    2006-01-01

    Various interconnected porous hydroxyapatite (HA) ceramic scaffolds are universally used to induct the tissue growth for bone repair and replacement, and serve to support the adhesion, transfer, proliferation and differentiation of cells. Impregnation of polyurethane sponges with a ceramic slurry is adopted to produce highly porous HA ceramic scaffolds with a 3D interconnected structure. However, high porosity always accompanies a decrease in the strength of the HA ceramic scaffolds. Therefore, it is significant to improve the strength of the HA ceramic scaffolds with highly interconnected porosity so that they are more suitable in clinical applications. In this work, highly porous HA ceramic scaffolds are first produced by the polymer impregnation approach, and subsequently further sintered by hot isostatic pressing (HIP). The phase composition, macro- and micro-porous structure, sintering and mechanical properties of the porous HA scaffolds are investigated by x-ray diffraction (XRD), scanning electron microscopy (SEM), nanoindentation analysis and compressive test. The experimental results show that the nanohardness and compressive strength of HIP-sintered porous HA ceramics are higher than those of commonly sintered HA scaffolds. The HIP technique can effectively improve the sintering property and densification of porous HA ceramic scaffolds, so inducing an increase in the compression strength

  20. A novel hot-melt extrusion formulation of albendazole for increasing dissolution properties.

    Science.gov (United States)

    Martinez-Marcos, Laura; Lamprou, Dimitrios A; McBurney, Roy T; Halbert, Gavin W

    2016-02-29

    The main aim of the research focused on the production of hot-melt extrusion (HME) formulations with increased dissolution properties of albendazole (ABZ). Therefore, HME was applied as a continuous manufacturing technique to produce amorphous solid dispersions of the poorly water soluble drug ABZ combined with the polymer matrix polyvinylpyrrolidone PVP K12. HME formulations of ABZ-PVP K12 comprised a drug content of 1%, 5% and 10% w/w. The main analytical characterisation techniques used were scanning electron microscopy (SEM), micro-computed tomography (μ-CT), X-ray powder diffraction (XRPD), differential scanning calorimetry (DSC) and dissolution profile studies. The application of SEM, XRPD and DSC evidenced drug physical transformation from crystalline to amorphous state and therefore, the achievement of an amorphous solid dispersion. The introduction of a novel technique, μ-CT, to characterise the internal structure of these materials revealed key information regarding materials distribution and void content. Dissolution profile studies evidenced a high increase in drug release profile compared to pure ABZ. These promising results can lead to a great enhancement of the oral bioavailability of ABZ dosage forms. Therefore, HME is a potential continuous manufacturing technique to overcome ABZ poor solubility properties and lead to a significant increase in the therapeutic effect. Copyright © 2016 Elsevier B.V. All rights reserved.

  1. Microstructure and Properties of a New Cr - Mn Steel without Boron Additions for Use in Hot Stamping

    Science.gov (United States)

    Zhou, H.; Zhu, G.; Li, Q.; Chen, Q.

    2015-09-01

    Anew hot-stamping steel that is alloyed with chromium and manganese and does not contain boron additions has been developed. The effect of reheating temperature and cooling rates on the mechanical properties and structure of the steel is determined. Atreatment regime that increases the ductility of the steel without a noticeable decrease in its strength is proposed.

  2. The effects of polymers' visco-elastoplastic properties on the micro cavities filling step of hot embossing process

    Science.gov (United States)

    Cheng, Gang; Barrière, Thierry

    2018-05-01

    The hot embossing process has been widely used in the manufacturing of polymer components, especially for the fabrication of micro or nano components. The significant advantage of the hot embossing process compared to the traditional injection moulding process is the excellent effective filling ratio for the high aspect ratio components and large surface structural components. The lack of material behavior modeling and numerical simulation limits the further development the hot embossing process, especially at the micro and nano scales. In this paper, a visco-elastoplastic behavior law has been proposed to describe the amorphous thermoplastic polymer mechanical properties in the hot embossing processing temperature range, which is lightly above their glass transition temperature. Uniaxial compression tests have been carried out in order to investigate the amorphous thermoplastic polymers properties. The material parameters in the visco-elastoplastic model have been identified according to the experimental results. A 3D numerical model has been created in the simulation software, which is based on the finite element method. The numerical simulation of the filling step of the hot embossing process has been effectuated by taking into account the viscous, elastic and plastic behaviors of thermoplastic polymers. The micro hot embossing process has been carried out using horizontal injection compression moulding equipment. A complete compression mould tool, equipped with the heating system, the cooling system, the ejection system and the vacuum system, has been designed and elaborated for this research work. The microfluidic devices based on the amorphous thermoplastic polymers have been successfully elaborated by hot embossing process. Proper agreement between the numerical simulation and the experimental elaboration has been obtained.

  3. Annealing effects on the microstructure and mechanical properties of hot-rolled 14Cr-ODS steel

    International Nuclear Information System (INIS)

    Gao, R.; Zhang, T.; Ding, H.L.; Jiang, Y.; Wang, X.P.; Fang, Q.F.; Liu, C.S.

    2015-01-01

    The oxide dispersion strengthened ferritic steels with nominal composition (weight percent) of Fe–14Cr–2W-0.5Ti-0.06Si-0.2V-0.1Mn-0.05Ta-0.03C-0.3Y_2O_3 were fabricated by sol–gel method, mechanical alloying, and hot isostatic pressing techniques. The evolution of microstructure and mechanical properties of the hot-rolled specimens with heat treatment was investigated. Tensile strength and hardness of hot-rolled ODS steel are significantly enhanced due to the formation of mechanical twins and high density dislocations. Uniformly dispersed oxide particles (10–40 nm) and fine-grained structure (200–400 nm) are responsible for the superior mechanical properties of the hot-rolled specimen annealed between 650 °C and 850 °C. With further increasing annealing temperature, the grain size of the hot-rolled specimens increases while the size of oxide particles decreases, which leads to lower strength and hardness but better ductility. The tensile strength and total elongation of samples in the rolling direction are higher than those in the transverse direction after the same treatments owing to the grain anisotropy induced by the large mechanical deformation.

  4. Annealing effects on the microstructure and mechanical properties of hot-rolled 14Cr-ODS steel

    Science.gov (United States)

    Gao, R.; Zhang, T.; Ding, H. L.; Jiang, Y.; Wang, X. P.; Fang, Q. F.; Liu, C. S.

    2015-10-01

    The oxide dispersion strengthened ferritic steels with nominal composition (weight percent) of Fe-14Cr-2W-0.5Ti-0.06Si-0.2V-0.1Mn-0.05Ta-0.03C-0.3Y2O3 were fabricated by sol-gel method, mechanical alloying, and hot isostatic pressing techniques. The evolution of microstructure and mechanical properties of the hot-rolled specimens with heat treatment was investigated. Tensile strength and hardness of hot-rolled ODS steel are significantly enhanced due to the formation of mechanical twins and high density dislocations. Uniformly dispersed oxide particles (10-40 nm) and fine-grained structure (200-400 nm) are responsible for the superior mechanical properties of the hot-rolled specimen annealed between 650 °C and 850 °C. With further increasing annealing temperature, the grain size of the hot-rolled specimens increases while the size of oxide particles decreases, which leads to lower strength and hardness but better ductility. The tensile strength and total elongation of samples in the rolling direction are higher than those in the transverse direction after the same treatments owing to the grain anisotropy induced by the large mechanical deformation.

  5. Recent progress to understand stress corrosion cracking in sodium borosilicate glasses: linking the chemical composition to structural, physical and fracture properties

    Science.gov (United States)

    Rountree, Cindy L.

    2017-08-01

    This topical review is dedicated to understanding stress corrosion cracking in oxide glasses and specifically the SiO_2{\\text-B_2O_3{\\text-}Na_2O} (SBN) ternary glass systems. Many review papers already exist on the topic of stress corrosion cracking in complex oxide glasses or overly simplified glasses (pure silica). These papers look at how systematically controlling environmental factors (pH, temperature...) alter stress corrosion cracking, while maintaining the same type of glass sample. Many questions still exist, including: What sets the environmental limit? What sets the velocity versus stress intensity factor in the slow stress corrosion regime (Region I)? Can researchers optimize these two effects to enhance a glass’ resistance to failure? To help answer these questions, this review takes a different approach. It looks at how systemically controlling the glass’ chemical composition alters the structure and physical properties. These changes are then compared and contrasted to the fracture toughness and the stress corrosion cracking properties. By taking this holistic approach, researchers can begin to understand the controlling factors in stress corrosion cracking and how to optimize glasses via the initial chemical composition.

  6. Buckling Analysis of Edge Cracked Sandwich Plate

    Directory of Open Access Journals (Sweden)

    Rasha Mohammed Hussein

    2016-07-01

    Full Text Available This work presents mainly the buckling load of sandwich plates with or without crack for different cases. The buckling loads are analyzed experimentally and numerically by using ANSYS 15. The experimental investigation was to fabricate the cracked sandwich plate from stainless steel and PVC to find mechanical properties of stainless steel and PVC such as young modulus. The buckling load for different aspect ratio, crack length, cracked location and plate without crack found. The experimental results were compared with that found from ANSYS program. Present of crack is decreased the buckling load and that depends on crack size, crack location and aspect ratio.

  7. Improving Mechanical Properties of Hot Mix Asphalt Using Fibres and Polymers in Developing Countries

    Science.gov (United States)

    Preciado, Jaime; Martínez Arguelles, Gilberto; Dugarte, Margareth; Bonicelli, Alessandra; Cantero, Julio; Vega, Daniela; Barros, Yennis

    2017-10-01

    The enhancement of mechanical properties and long term performance of hot mix asphalt (HMA) should be considered as a goal in order to achieve a transport infrastructure really sustainable. However, this issue becomes a difficult task, if conventional HMA are used. In fact, performance of conventional HMA, usually presents poor long term performance and functional distresses related to high and low temperatures, which in turn implies higher maintenance costs and superior carbon footprints. To overcome this weaken, bitumen industry has been developing new polymer modifiers, additives to improve HMA behaviour. One of the techniques most used in developed countries to enhance HMA behaviour is the use of modified bitumen. Modifying the bitumen, and then producing modified HMA requires specific equipment and facilities that may be time-consuming, expensive and hard to manage. For instance, to warranty a successful modifying process, storage and handling of the modified bitumen are issues very complex to handle. On the other hand, producing a polymer modified HMA by adding polymers and additives directly during the bitumen/aggregate mixing process may offer very interesting advantages since the economical, production and sustainability standpoint. This paper aimed to determine the feasibility of the incorporation of fibres and plastomeric polymers into different types of HMA by means of the “dry process” (to add polymers during the mixing of aggregate and bitumen in the HMA plant) to produce polymer modified mixes. Thus, laboratory tests including Marshall Stability, Indirect Tensile Stiffness Modulus, repeated load test and Indirect Tensile Strength test were performed to assess the effect of the inclusion of fibres and plastomeric polymers on mechanical and volumetric properties of selected mixes. Results showed that the modification of bituminous mixtures following the “dry process” could be used to improve the performance and long term properties of HMA.

  8. Effects of material property changes on irradiation assisted stress corrosion cracking

    Energy Technology Data Exchange (ETDEWEB)

    Nakano, Morihito; Fukuya, Koji; Fujii, Katsuhiko [Inst. of Nuclear Safety System Inc., Mihama, Fukui (Japan)

    2002-09-01

    Irradiation assisted stress corrosion cracking (IASCC) susceptibility and radiation-induced material changes in microstructure and microchemistry under pressurized water reactor (PWR) environment were examined on irradiated stainless steels (SSs), post-irradiation annealed SSs and post-irradiation deformed SS. The yield stress and grain boundary segregation were considerably high in SSs highly irradiated to 1-8 x 10{sup 26}n/m{sup 2} (E > 0.1 MeV) in PWR at 290-320degC, resulting in a high IASCC susceptibility. Following post-irradiation annealing of highly irradiated SSs, IASCC susceptibility showed significant recovery from 89% (as-irradiated) to 8% (550degC) of %IGSCC, while the hardness recovered from Hv375 (400degC) to Hv315 (550degC). Apparent recovery of segregation at grain boundaries was not observed. The SSs irradiated to 5.3 x 10{sup 24}n/m{sup 2} (E>1MeV) in the Japan Materials Testing Reactor (JMTR) at < 400degC, which had grain boundary segregation and low hardness, showed no IASCC susceptibility. Due to post-irradiation deforming for JMTR irradiated SS, the hardness increased but IASCC did not occur. These results suggested that the hardening would be a key factor for IASCC initiation under PWR hydrogenated water and that a yield stress threshold for IASCC initiation under slow strain rate tensile (SSRT) testing would the about 600MPa. (author)

  9. Effects of material property changes on irradiation assisted stress corrosion cracking

    International Nuclear Information System (INIS)

    Nakano, Morihito; Fukuya, Koji; Fujii, Katsuhiko

    2002-01-01

    Irradiation assisted stress corrosion cracking (IASCC) susceptibility and radiation-induced material changes in microstructure and microchemistry under pressurized water reactor (PWR) environment were examined on irradiated stainless steels (SSs), post-irradiation annealed SSs and post-irradiation deformed SS. The yield stress and grain boundary segregation were considerably high in SSs highly irradiated to 1-8 x 10 26 n/m 2 (E > 0.1 MeV) in PWR at 290-320degC, resulting in a high IASCC susceptibility. Following post-irradiation annealing of highly irradiated SSs, IASCC susceptibility showed significant recovery from 89% (as-irradiated) to 8% (550degC) of %IGSCC, while the hardness recovered from Hv375 (400degC) to Hv315 (550degC). Apparent recovery of segregation at grain boundaries was not observed. The SSs irradiated to 5.3 x 10 24 n/m 2 (E>1MeV) in the Japan Materials Testing Reactor (JMTR) at < 400degC, which had grain boundary segregation and low hardness, showed no IASCC susceptibility. Due to post-irradiation deforming for JMTR irradiated SS, the hardness increased but IASCC did not occur. These results suggested that the hardening would be a key factor for IASCC initiation under PWR hydrogenated water and that a yield stress threshold for IASCC initiation under slow strain rate tensile (SSRT) testing would the about 600MPa. (author)

  10. Effect of phosphorus additions on hot pressing temperature and some properties of WC-Co hard alloys

    International Nuclear Information System (INIS)

    Dotsenko, V.M.; Simkina, Eh.S.; Tsypin, N.V.

    1977-01-01

    Results of studies on the effect of phosphorus additions on hot pressing temperature and some properties of VK6 and VK15 hard alloys are given. It is shown that alloying of hard alloys with 3-6 wt % phosphorus gives opportunity to lower substantially (for 200-300 deg) their hot pressing temperature. Hardness and density of alloys with phosphorus do not practically change. Some decrease of strength and wear-resistance characteristics is observed which is obviously connected with irregular distribution of phosphorus in the alloy

  11. Formation of microstructure and properties on hot working and heat treatment of high strength modular cast iron

    International Nuclear Information System (INIS)

    Trajno, A.I.; Yusupov, V.S.; Kugushin, A.A.

    1999-01-01

    The possibility of plastic deformation of high strength modular cast iron (HSNCI) is under study. The microstructure and mechanical properties of hot worked and heat treated cast iron are investigated for the composition, %: Fe - 2.9 C - 2.4 Si - 0.7 Ni - 0.05 Mg - 0.04 Ce. It is stated that HSNCI can withstand various types of hot working without fracturing. Graphite inclusions lose their modular shape irreversibly during plastic deformation. Subsequent heat treatment affects the metal matrix only. The heating in oxidizing environment is noted to result in cast iron surface decarbonization [ru

  12. Microstructure and thermoelectric properties of β-FeSi2 ceramics fabricated by hot-pressing and spark plasma sintering

    International Nuclear Information System (INIS)

    Qu Xiurong; Lue Shuchen; Hu Jianmin; Meng Qingyu

    2011-01-01

    Highlights: → With increasing hot-pressing (HP) temperature, the thermoelectric figure of merit of β-FeSi 2 ceramics is improved slightly. → The grain size of the sample sintered by the spark plasma sintering (SPS) process is smaller than that by the HP process. → The SPS sample shows excellent thermoelectric performance attributed to low thermal conductivity. - Abstract: The microstructure and thermoelectric properties of β-FeSi 2 ceramics by hot pressing (HP) and spark plasma sintering (SPS) are investigated. With increasing hot-pressing temperature, the density, electronic conductivity and thermal conductivity of the samples increase significantly, the thermoelectric figure of merit is improved slightly. The microstructure study indicates that the sizes of the β-FeSi 2 and ε-FeSi phases in the sample sintered by the SPS process are smaller than that by the HP process. The SPS sample shows excellent thermoelectric performance due to the low thermal conductivity.

  13. Effects of excessive grain growth on the magnetic and mechanical properties of hot-deformed NdFeB magnets

    Energy Technology Data Exchange (ETDEWEB)

    Lin, M., E-mail: linm@nimte.ac.c [Key Laboratory of Magnetic Materials and Devices, Ningbo Institute of Material Technology and Engineering Chinese Academy of Science, Ningbo 315201 (China); Wang, H.J. [Division of Functional Materials, Central Iron and Steel Research Institute, Beijing 100081 (China); Yi, P.P.; Yan, A.R. [Key Laboratory of Magnetic Materials and Devices, Ningbo Institute of Material Technology and Engineering Chinese Academy of Science, Ningbo 315201 (China)

    2010-08-15

    The magnetic and mechanical properties of rare-earth magnets hot-deformed at temperature range 750-950 deg. C have been investigated. The grains tended to grow excessively from dozens of nanometers to several microns at the temperatures above 850 deg. C. The alignment of grains was disrupted by the hot deformation at the high temperatures. The Nd-rich phase was extruded at the temperatures which are higher than 850 deg. C. The Nd-rich phase extrusion resulted in the reduction of density by 1% and the reduction of remanence from 1.42 to 0.72 T. The reduction of grain boundaries caused by flat platelet-shaped grains changing to spherical grains and the weak binding strength among large grains of Nd{sub 2}Fe{sub 14}B phase may be the main reasons for the low mechanical strength of hot-deformed magnets.

  14. Statistical crack mechanics

    International Nuclear Information System (INIS)

    Dienes, J.K.

    1993-01-01

    Although it is possible to simulate the ground blast from a single explosive shot with a simple computer algorithm and appropriate constants, the most commonly used modelling methods do not account for major changes in geology or shot energy because mechanical features such as tectonic stresses, fault structure, microcracking, brittle-ductile transition, and water content are not represented in significant detail. An alternative approach for modelling called Statistical Crack Mechanics is presented in this paper. This method, developed in the seventies as a part of the oil shale program, accounts for crack opening, shear, growth, and coalescence. Numerous photographs and micrographs show that shocked materials tend to involve arrays of planar cracks. The approach described here provides a way to account for microstructure and give a representation of the physical behavior of a material at the microscopic level that can account for phenomena such as permeability, fragmentation, shear banding, and hot-spot formation in explosives

  15. Mechanical properties and drug release of venlafaxine HCl solid mini matrices prepared by hot-melt extrusion and hot or ambient compression.

    Science.gov (United States)

    Avgerinos, Theodoros; Kantiranis, Nikolaos; Panagopoulou, Athanasia; Malamataris, Stavros; Kachrimanis, Kyriakos; Nikolakakis, Ioannis

    2018-02-01

    Objective/significance: To elucidate the role of plasticizers in different mini matrices and correlate mechanical properties with drug release. Cylindrical pellets were prepared by hot-melt extrusion (HME) and mini tablets by hot (HC) and ambient compression (AC). Venlafaxine HCl was the model drug, Eudragit ® RSPO the matrix former and citric acid or Lutrol ® F127 the plasticizers. The matrices were characterized for morphology, crystallinity, and mechanical properties. The influence of plasticizer's type and content on the extrusion pressure (P e ) during HME and ejection during tableting was examined and the mechanical properties were correlated with drug release parameters. Resistance to extrusion and tablet ejection force were reduced by Lutrol ® F127 which also produced softer and weaker pellets with faster release, but harder and stronger HC tablets with slower release. HME pellets showed greater tensile strength (T) and 100 times slower release than tablets. P e correlated with T and resistance to deformation of the corresponding pellets (r 2  = 0.963 and 0.945). For both HME and HC matrices the decrease of drug release with T followed a single straight line (r 2  = 0.990) and for HME the diffusion coefficient (D e ) and retreat rate constant (k b ) decreased linearly with T (r 2  = 0.934 and 0.972). Lutrol ® F127 and citric acid are efficient plasticizers and Lutrol ® F127 is a thermal binder/lubricant in HC compression. The different bonding mechanisms of the matrices were reflected in the mechanical strength and drug release. Relationships established between T and drug release parameters for HME and HC matrices may be useful during formulation work.

  16. Effects of energy conservation on equilibrium properties of hot asymmetric nuclear matter

    Science.gov (United States)

    Zhang, Zhen; Ko, Che Ming

    2018-01-01

    Based on the relativistic Vlasov-Uehling-Uhlenbeck transport model, which includes relativistic scalar and vector potentials on baryons, we consider an N -Δ -π system in a box with periodic boundary conditions to study the effects of energy conservation in particle production and absorption processes on the equilibrium properties of the system. The density and temperature of the matter in the box are taken to be similar to the hot dense matter formed in heavy ion collisions at intermediate energies. We find that to maintain the equilibrium numbers of N ,Δ , and π , which depend on the mean-field potentials of N and Δ , we must include these potentials in the energy conservation condition that determines the momenta of outgoing particles after a scattering or decay process. We further find that the baryon scalar potentials mainly affect the Δ and pion equilibrium numbers, while the baryon vector potentials have considerable effect on the effective charged pion ratio at equilibrium. Our results thus indicate that it is essential to include in the transport model the effect of potentials in the energy conservation of a scattering or decay process, which is ignored in most transport models, for studying pion production in heavy ion collisions.

  17. Effect of Fe-Content on the Mechanical Properties of Recycled Al Alloys during Hot Compression

    Directory of Open Access Journals (Sweden)

    Hongzhou Lu

    2017-07-01

    Full Text Available It is unavoidable that Fe impurities will be mixed into Al alloys during recycling of automotive aluminum parts, and the Fe content has a significant effect on the mechanical properties of the recycled Al alloys. In this work, hot compression tests of two Fe-containing Al alloys were carried out at elevated temperatures within a wide strain rate range from 0.01 s−1 to 10 s−1. The effect of Fe content on the peak stress of the stress vs. strain curves, strain rate sensitivity and activation energy for dynamic recrystallization are analyzed. Results show that the recycled Al alloy containing 0.5 wt % Fe exhibits higher peak stresses and larger activation energy than the recycled Al alloy containing 0.1 wt % Fe, which results from the fact that there are more dispersed AlMgFeSi and/or AlFeSi precipitates in the recycled Al alloy containing 0.5 wt % Fe as confirmed by SEM observation and energy spectrum analysis. It is also shown that the Fe content has little effect on the strain rate sensitivity of the recycled Al alloys.

  18. Effect of metal properties of casts of steel-15Kh1M1FL on the crack resistance at 565 deg C

    International Nuclear Information System (INIS)

    Gladshtejn, V.I.; Sheshenev, M.F.

    1976-01-01

    Results are given of prolonged tests of the metal of industrial casts with various fluidity limits. It has been shown experimentally that a quite satisfactory crack resistance is characteristic of a metal with a fluidity limit in the range 30-50 kgf/mm 2 . Metallographic studies have been conducted. Upon variation of the structure and properties of the 15Kh1M1FL steel during operation, the rate of growth of small cracks (up to 2.0 mm) decreases almost by 3 orders of ten (from 1.4x10 -4 to 2.0x10 -7 mm/hour). Subsequent structural changes during prolonged operation (over 50000 hours) result in a gradual increase in the rate of crack growth. At the same time resistance towards appearance of the impermissible high rate of the crack growth, Ksub(10sup(-3)), diminishes monotonically with the operation time. The metal of industrial 15Kh1M1FL steel casts has good crack resistance (Ksub(10sup(-3)) =30-70 kgf/mmsup(3/2) and Vsub(ef) =) kgf/mm 2 ) and a satisfactory local plasticity (critical opening being no more than 0.20 mm for 10 3 hours)

  19. Effect of hot rolling on the microstructure and mechanical properties of Ti3Al based dual phase alloys

    International Nuclear Information System (INIS)

    Wu, J.; Zhang, L.; Hua, W.; Qiu, G.

    1999-01-01

    Development of α 2 -Ti 3 Al based dual phase alloys have shown some promising potentials in property improvement by introducing Ti 5 Si 3 silicide phase into the matrix via Si alloying. However, the presence of coarse network of Ti 5 Si 3 phase formed by eutectic reaction in the as-cast state also embrittles the alloy. Both hot rolling and powder metallurgy are considered to be the possible ways to refine the Ti 5 Si 3 phase in the matrix. Two Ti-Al-Si-Nb alloys whose Si contents are 2 and 5 at.% respectively were arc melted into ingots and then hot rolled to sheets in this investigation. Optical metallographic examination correlates the microstructures of the as-cast and as-rolled alloys with the different rolling amounts, showing that the coarse silicide network is broken into small particles after hot rolling. Mechanical property testing from room temperature to 800 C indicates that the strength and plastic elongation of the hot-rolled alloys are much higher than those of the as-cast ones. The data obtained in this investigation are comparable with those obtained in the P/M processed specimens. Fracture surfaces of the alloys are also examined

  20. Assessment of cracking in dissimilar metal welds

    International Nuclear Information System (INIS)

    Jenssen, Anders; Norrgaard, K.; Lagerstroem, J.; Embring, G.; Tice, D.R.

    2001-08-01

    During the refueling in 2000, indications were observed by non-destructive testing at four locations in the reactor pressure vessel (RPV) nozzle to safe end weld in Ringhals 4. All indications were confined to the outlet nozzle (hotleg) oriented at 25 deg, a nozzle with documented repair welding. Six boat samples were removed from the four locations, and the samples were subsequently subjected to a metallographic examination. The objectives were to establish the fracture morphology, and if possible the root cause for cracking. The examination revealed that cracks were present at all four boat sample locations and that they all were confined to the weld metal, alloy 182. Cracking extended in the axial direction of the safe-end. There was no evidence of any cracks extending into the RPV-steel, or the stainless steel safe-end. All cracking was interdendritic and significantly branched. Among others, these observations strongly suggested crack propagation mainly was caused by interdendritic stress corrosion cracking. In addition, crack type defects and isolated areas on the fracture surfaces suggested the presence of hot cracking, which would have been formed during fabrication. The reason for crack initiation could not be established based on the boat samples examined. However, increased stress levels due to repair welding, cold work from grinding, and defects produced during fabrication, e. g. hot cracks, may alone or in combination have contributed to crack initiation

  1. X-ray and SZ constraints on the properties of hot CGM

    Science.gov (United States)

    Singh, Priyanka; Majumdar, Subhabrata; Nath, Biman B.; Silk, Joseph

    2018-05-01

    We use observations of stacked X-ray luminosity and Sunyaev-Zel'dovich (SZ) signal from a cosmological sample of ˜80, 000 and 104,000 massive galaxies, respectively, with 1012.6 ≲ M500 ≲ 1013M⊙ and mean redshift, z¯ ˜ 0.1 - 0.14 to constrain the hot Circumgalactic Medium (CGM) density and temperature. The X-ray luminosities constrain the density and hot CGM mass, while the SZ signal helps in breaking the density-temperature degeneracy. We consider a simple power-law density distribution (ne∝r-3β) as well as a hydrostatic hot halo model, with the gas assumed to be isothermal in both cases. The datasets are best described by the mean hot CGM profile ∝r-1.2, which is shallower than an NFW profile. For halo virial mass ˜1012 - 1013M⊙, the hot CGM contains ˜ 20 - 30% of galactic baryonic mass for the power-law model and 4 - 11% for the hydrostatic halo model, within the virial radii. For the power-law model, the hot CGM profile broadly agrees with observations of the Milky Way. The mean hot CGM mass is comparable to or larger than the mass contained in other phases of the CGM for L* galaxies.

  2. Investigation and microstructural analyses of massive LSP impacts with coverage area on crack initiation location and tensile properties of AM50 magnesium alloy

    Energy Technology Data Exchange (ETDEWEB)

    Luo, K.Y.; Wang, C.Y. [School of Mechanical Engineering, Jiangsu University, Zhenjiang 212013 (China); Sun, G.F. [School of Mechanical Engineering, Southeast University, Nanjing 211189 (China); Cui, C.Y.; Sheng, J. [School of Mechanical Engineering, Jiangsu University, Zhenjiang 212013 (China); Lu, J.Z., E-mail: blueesky2005@163.com [School of Mechanical Engineering, Jiangsu University, Zhenjiang 212013 (China)

    2016-01-05

    The influence of massive laser shock peening (LSP) impacts with coverage area on tensile properties of AM50 magnesium alloy was investigated using MTS880-10 servo-hydraulic material testing machine system. Microstructure in the surface layer and fracture morphologies of as-machined and LSPed tensile specimens were also characterized and analyzed by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and cross-sectional optical microscopy (OM). Special attention is paid to the crack initiation location as a function of LSPed coverage area in the gauge part of tensile specimen. Experimental results and analysis indicate that coverage area significantly influenced tensile properties of the tensile specimen. In addition, the grain refinement process in the top surface layer of AM50 magnesium alloy caused by massive LSP impacts is presented. Furthermore, the underlying influence mechanism of LSPed coverage area on tensile properties and crack initiation location of tensile specimen was clearly revealed.

  3. Investigation and microstructural analyses of massive LSP impacts with coverage area on crack initiation location and tensile properties of AM50 magnesium alloy

    International Nuclear Information System (INIS)

    Luo, K.Y.; Wang, C.Y.; Sun, G.F.; Cui, C.Y.; Sheng, J.; Lu, J.Z.

    2016-01-01

    The influence of massive laser shock peening (LSP) impacts with coverage area on tensile properties of AM50 magnesium alloy was investigated using MTS880-10 servo-hydraulic material testing machine system. Microstructure in the surface layer and fracture morphologies of as-machined and LSPed tensile specimens were also characterized and analyzed by scanning electron microscopy (SEM), transmission electron microscopy (TEM) and cross-sectional optical microscopy (OM). Special attention is paid to the crack initiation location as a function of LSPed coverage area in the gauge part of tensile specimen. Experimental results and analysis indicate that coverage area significantly influenced tensile properties of the tensile specimen. In addition, the grain refinement process in the top surface layer of AM50 magnesium alloy caused by massive LSP impacts is presented. Furthermore, the underlying influence mechanism of LSPed coverage area on tensile properties and crack initiation location of tensile specimen was clearly revealed.

  4. Evaluation of the mechanical properties after thermal treatment of a structural hot rolled multiphase steel

    Directory of Open Access Journals (Sweden)

    Asensio-Lozano, J.

    2007-12-01

    Full Text Available The present paper corresponds to the experimental study conducted on a hot rolled (HR multiphase (MP steel, in which hardness, tensile and toughness properties were measured after the application of a series of subcritical and intercritical heat treatments (HT to the hot rolled stock. The aforementioned values were compared to the corresponding ones in the as-rolled state and after normalizing. The microstructure in the longitudinal plane of the strip was analyzed by light optical microscopy in the as-rolled state and in the HT samples. Longitudinal (L and transverse (T tensile and toughness specimens were cut to characterize every condition studied. Toughness properties were evaluated by means of Charpy V-notch tests conducted at 20 °C, 0 °C, –20 °C, –40 °C, –60 °C and –80 °C . It was observed that the yield stress increased with the increase in the heat treatment temperature in the subcritical range, while the tensile strength decreased slightly over the same range of temperatures. Uniform and total elongation only showed a slight improvement when the treatment was conducted at 620 °C and 700 °C, while the best toughness response corresponded to the sample treated at 500 °C for operating temperatures comprised between –40 °C and room temperature (RT.

    El presente estudio corresponde al trabajo experimental desarrollado en un acero multifase laminado en caliente, en el que se evaluaron las propiedades de dureza, tracción y tenacidad a impacto, tras realizar tratamientos térmicos subcríticos e intercríticos al material laminado en caliente. Los valores precedentes se comparan con el material de partida laminado en caliente y tras tratamiento de normalizado. Se analiza la microestructura en microscopía óptica de reflexión, en el plano longitudinal tanto en el estado laminado como en las muestras tratadas térmicamente. Se estudiaron los comportamientos longitudinales y transversales en tracción y frente a impacto

  5. Hot spot formation and stagnation properties in simulations of direct-drive NIF implosions

    Science.gov (United States)

    Schmitt, Andrew J.; Obenschain, Stephen P.

    2016-05-01

    We investigate different proposed methods of increasing the hot spot energy and radius in inertial confinement fusion implosions. In particular, shock mistiming (preferentially heating the inner edge of the target's fuel) and increasing the initial vapor gas density are investigated as possible control mechanisms. We find that only the latter is effective in substantially increasing the hot spot energy and dimensions while achieving ignition. In all cases an increase in the hot spot energy is accompanied by a decrease in the hot spot energy density (pressure) and both the yield and the gain of the target drop substantially. 2D simulations of increased vapor density targets predict an increase in the robustness of the target with respect to surface perturbations but are accompanied by significant yield degradation.

  6. Grain Refinement and Enhancement of Mechanical Properties of Hot Extruded Rare-Earth Containing Magnesium Alloy

    Directory of Open Access Journals (Sweden)

    Bita Pourbahari

    2017-12-01

    Full Text Available The effects of rare earth addition and hot extrusion process on the grain refinement of magnesium alloy were studied. The as-cast Mg-6Al-1Zn (AZ61 alloy had the average grain size of ~ 64 µm and its microstructure consisted of α-Mg and Mg17Al12 phase. By partial substitution of Al with Gd to reach Mg-4.8Gd-1.2Al-1Zn alloy, it was observed that the Mg17Al12 phase disappeared and two new intermetallic phases, i.e. (Mg,Al3Gd and Al2Gd, were identified. The extrusion process showed significant effects on the shape and size of intermetallics and grain size of the matrix. The grain size of the extruded Mg-6Al-1Zn alloy was refined from 64 µm to 13.4 µm as a result of recrystallization. Regarding the Mg-4.8Gd-1.2Al-1Zn alloy, the grain refinement was much more pronounced, where the extruded grain size has been refined from 698 µm to 2.4 µm (extruded at 385 °C and 1.3 µm (extruded at 320 °C. This was related to the presence of fine and widely dispersed intermetallic phases. Tensile strength and total elongation of extruded alloys were much higher than their as-cast counterparts and the extruded Mg-6Zn-1Al alloy showed magnificent mechanical properties. The latter was related to the absence of intermetallic particles, which act as stress risers.

  7. The effect of additional elements on the magnetic properties of hot-rolled Nd-Fe-B alloys

    International Nuclear Information System (INIS)

    Chang, W.C.; Nakamura, H.; Paik, C.R.; Sugimoto, S.; Okada, M.; Homma, M.

    1992-01-01

    The magnetic properties of hot-rolled Nd 16 Fe bal. B 6 M 1.5 (M = Cu, Ga and Al) and Nd 16 Fe 76 B 5.5 Ga 1.5 Al 1 alloys were investigated, in order to study the role of additive elements in improving the magnetic properties in the Nd-Fe-B system. It is found that the original grain size of Cu, Ga or Ga-Al added alloys is much finer than that of the ternary and Al added alloys. But the grain size is almost identical for all the alloys after hot-rolling at 1000degC with 90% reduction in thickness. The coercivity of hot-rolled alloys with Cu, Ga or Ga-Al addition is not improved as was expected, because Nd-rich liquid phase in these alloys is very easily squeezed out during high-reduction-ratio rolling. Less quantity and nonuniform distribution of Nd-rich phase between distributed grains are believed to be the main reasons to depress the effect on the grain boundary smoothing. This effect is not the same as those observed in the Pr-Fe-B system. The highest magnetic properties achieved in this study are B r = 10 kG, i H c = 8.2 kOe, (BH) max = 18.5 MGOe for the Nd 16 Fe 76.5 B 6 Al 1.5 alloy. (orig.)

  8. Effect of Hot water and dilute acid pretreatment on the chemical properties of liquorice root

    Directory of Open Access Journals (Sweden)

    zahra takzare

    2016-06-01

    Full Text Available Abstract In this study, the liquorice root (Glycyrrhiza glabra that was extracted in the factory in Kerman province, pre-hydrolyzed and then chemical compositions (Extractives, Lignin content, Holocellulose percent, the hydrolysis process yield and weight loss of the waste was measured. Pre-hydrolysis process was done on the above mentioned waste by hot water, hot water followed by 0.5 percent sulfuric acid and also alone sulfuric acid with different concentrations (0.5, 1, 1.5 and 2 percent The samples were pre-hydrolyzed in hot water at 150 °C and 30, 60 and 90 minutes as well as in the mixture of hot water and 0.5 % sulfuric acid at 150 °C and 60 minutes and also in pure sulfuric acid, at 130 °C and at 60 minutes. The results showed that the pre-hydrolyzed treatment with hot water in 60 minutes had been favorable performance in the respect of weight loss, lignin content and holocellulose percent. Also, in the case of pre-treatment including sulfuric acid, 2% dose can be good selected option in term of maximum holocellulose percent and minimum lignin content so that it can be suggested to produce higher value-added products such as bioethanol from licorice root bid.

  9. Effects of Al content on structure and mechanical properties of hot-rolled ZrTiAlV alloys

    International Nuclear Information System (INIS)

    Liang, S.X.; Yin, L.X.; Che, H.W.; Jing, R.; Zhou, Y.K.; Ma, M.Z.; Liu, R.P.

    2013-01-01

    Highlights: • Phase structure is greatly dependent on the Al content. • Intermetallic compound will precipitates while Al content is over 6.9 wt%. • Equiaxed α-phase grains present in the hot-rolled alloy with 6.9 wt% Al. • Alloys with Al content from 3.3 wt% to 5.6 wt% have good mechanical properties. - Abstract: Zirconium alloys show attractive properties for astronautic applications where the most important factors are anti-irradiation, corrosion resistance, anti-oxidant, very good strength-to-weight ratio. The effects of Al content (2.2–6.9 wt%) on structure and mechanical properties of the hot-rolled ZrTiAlV alloy samples were investigated in this study. Each sample of the hot-rolled ZrTiAlV alloys with Al contents from 2.2 wt% to 5.6 wt% is composed of the α phase and β phase, meanwhile, the relative content of the α phase increased with the Al content. However, the (ZrTi) 3 Al intermetallic compound was observed as the Al content increased to 6.9 wt%. Changes of phase compositions and structure with Al content distinctly affected mechanical properties of ZrTiAlV alloys. Yield strength of the alloy with 2.2 wt% Al is below 200 MPa. As Al content increased to 5.6 wt%, the yield strength, tensile strength and elongation of the examined alloy are 1088 MPa, 1256 MPa and 8%, respectively. As Al content further increased to 6.9 wt%, a rapid decrease in ductility was observed as soon as the (ZrTi) 3 Al intermetallic compound precipitated. Results show that the ZrTiAlV alloys with Al contents between 3.3 wt% and 5.6 wt% have excellent mechanical properties

  10. Influence of Hot-Working Conditions on High-Temperature Properties of a Heat-Resistant Alloy

    Science.gov (United States)

    Ewing, John F; Freeman, J W

    1957-01-01

    The relationships between conditions of hot-working and properties at high temperatures and the influence of the hot-working on response to heat treatment were investigated for an alloy containing nominally 20 percent molybdenum, 2 percent tungsten, and 1 percent columbium. Commercially produced bar stock was solution-treated at 2,200 degrees F. to minimize prior-history effects and then rolled at temperatures of 2,200 degrees, 2,100 degrees, 2,000 degrees, 1,800 degrees, and 1,600 degrees F. Working was carried out at constant temperature and with incremental decreases in temperature simulating a falling temperature during hot-working. In addition, a few special repeated cyclic conditions involving a small reduction at high temperature followed by a small reduction at a low temperature were used to study the possibility of inducing very low strengths by the extensive precipitation accompanying such properties. Most of the rolling was done in open passes with a few check tests being made with closed passes. Heat treatments at both 2,050 degrees and 2,200 degrees F. subsequent to working were used to study the influence on response to heat treatment.

  11. The effect of hot pressing time on the microstructure and properties of Laves phase NbCr{sub 2} alloys

    Energy Technology Data Exchange (ETDEWEB)

    Xiao, X. [College of Electromechanical Engineering, Nanjing University of Aeronautical and Astronautics, Nanjing 210016 (China); School of Materials Science and Engineering, Nanchang Institute of Aeronautical Technology, Nanchang 330063 (China); Lu, S.Q. [School of Materials Science and Engineering, Nanchang Institute of Aeronautical Technology, Nanchang 330063 (China)], E-mail: niatlusq@126.com; Hu, P.; Huang, M.G.; Nie, X.W. [School of Materials Science and Engineering, Nanchang Institute of Aeronautical Technology, Nanchang 330063 (China); Fu, M.W. [Department of Mechanical Engineering, Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong (China)

    2008-06-25

    The microstructure and properties were investigated on the Laves phase NbCr{sub 2} alloys prepared through 20 h mechanical alloying of niobium and chromium powders and subsequent hot pressing at 1250 deg. C for different time. The results indicate that the Laves phase NbCr{sub 2} alloy with homogeneous microstructure and fine grains and high relative density is obtained. With the increase of hot pressing time, the density, grain size and Vickers hardness increase, the fracture toughness, however, decreases gradually. The alloy fabricated by hot pressing at 1250 deg. C for 30 min has the best overall properties. Its average grain size reaches about 248 nm, the relative density is 97.8% and the fracture toughness at room temperature is more than 4.7 MPa m{sup 1/2}. Compared with the Laves phase NbCr{sub 2} alloy prepared by arc-melting, which has the fracture toughness of 1.2 MPa m{sup 1/2}, the fracture toughness in this research is increased significantly.

  12. Effect of hot isostatic pressing on the properties of sintered alpha silicon carbide

    Science.gov (United States)

    Watson, G. K.; Moore, T. J.; Millard, M. L.

    1985-01-01

    Two lots of alpha silicon carbide were isostatically hot-pressed under 138 MPa for 2 h in Ar at temperatures up to 2200 C. Nearly theoretically dense specimens resulted. Hot isostatic pressing increased both room-temperature strength and 1200 C strength, and resulted in improved reliability. One lot of material which was pressed at 2200 C showed increases of about 20 percent in room-temperature strength and about 50 percent in 1200 C flexural strength; the Weibull modulus improved about 100 percent.

  13. Evolution of the texture, mechanical properties, and microstructure of Cu-2.7Be alloys during hot cross-rolling

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Daibo; Liu, Chuming; Liu, Yadi; Gao, Yonghao; Jiang, Shunong [Central South University, School of Materials Science and Engineering, Changsha (China); Han, Tan [Suzhou Kinkou Copper Industry Limited Liability Company, Taicang (China)

    2015-09-15

    The evolution of the microstructure and texture of Cu-2.7Be alloys during hot rolling was investigated and related to the mechanical properties of the resulting sheets. Hot cross-rolling is shown to be an effective way to refine the hard and brittle secondary-phase particles in Cu-2.7Be alloys. The Cu- and brass-type textures increase and decrease in prevalence, respectively, during the rolling process. The yield strengths along the first and second rolling directions, and 45 to the former, are all enhanced because the corresponding Schmid factors decrease as the sheets are rolled thinner. The ductility anisotropy of the as-rolled sheets is related to the distribution and shape of the secondary-phase particles therein. (orig.)

  14. Investigation of the Microstructure and Mechanical Properties of Copper-Graphite Composites Reinforced with Single-Crystal α-Al₂O₃ Fibres by Hot Isostatic Pressing.

    Science.gov (United States)

    Zhang, Guihang; Jiang, Xiaosong; Qiao, ChangJun; Shao, Zhenyi; Zhu, Degui; Zhu, Minhao; Valcarcel, Victor

    2018-06-11

    Single-crystal α-Al₂O₃ fibres can be utilized as a novel reinforcement in high-temperature composites owing to their high elastic modulus, chemical and thermal stability. Unlike non-oxide fibres and polycrystalline alumina fibres, high-temperature oxidation and polycrystalline particles boundary growth will not occur for single-crystal α-Al₂O₃ fibres. In this work, single-crystal α-Al₂O₃ whiskers and Al₂O₃ particles synergistic reinforced copper-graphite composites were fabricated by mechanical alloying and hot isostatic pressing techniques. The phase compositions, microstructures, and fracture morphologies of the composites were investigated using X-ray diffraction, a scanning electron microscope equipped with an X-ray energy-dispersive spectrometer (EDS), an electron probe microscopic analysis equipped with wavelength-dispersive spectrometer, and a transmission electron microscope equipped with EDS. The mechanical properties have been measured by a micro-hardness tester and electronic universal testing machine. The results show that the reinforcements were unevenly distributed in the matrix with the increase of their content and there were some micro-cracks located at the interface between the reinforcement and the matrix. With the increase of the Al₂O₃ whisker content, the compressive strength of the composites first increased and then decreased, while the hardness decreased. The fracture and strengthening mechanisms of the composite materials were explored on the basis of the structure and composition of the composites through the formation and function of the interface. The main strengthening mechanism in the composites was fine grain strengthening and solid solution strengthening. The fracture type of the composites was brittle fracture.

  15. A comparison of two atomic models for the radiative properties of dense hot low Z plasmas

    International Nuclear Information System (INIS)

    Minguez, E.; Sauvan, P.; Gil, J.M.; Rodriguez, R.; Rubiano, J.G.; Florido, R.; Martel, P.; Angelo, P.; Schott, R.; Philippe, F.; Leboucher-Dalimier, E.; Mancini, R.

    2003-01-01

    In this work, two different atomic models (ANALOP based on parametric potentials and IDEFIX based on the dicenter model) are used to calculate the opacities for bound-bound transitions in hot dense, low Z plasmas, and the results are compared to each other. In addition, the ANALOP code has been used to compute free-bound cross sections for hydrogen-like ions

  16. Effect of hot water extracted hardwood and softwood chips on particleboard properties

    Science.gov (United States)

    Manuel Raul Pelaez-Samaniego; Vikram Yadama; Tsai Garcia-Perez; Eini Lowell; Thomas Amidon

    2014-01-01

    The affinity of particleboard (PB) to water is one of the main limitations for using PB in moisture-rich environments. PB dimensional stability and durability can be improved by reducing the available hydroxyl groups in wood through hemicellulose removal, for example, by hot water extraction (HWE), which increases wood resistance to moisture uptake. The resulting...

  17. Delayed hydride cracking: alternative pre-cracking method

    International Nuclear Information System (INIS)

    Mieza, Juan I.; Ponzoni, Lucio M.E.; Vigna, Gustavo L.; Domizzi, Gladys

    2009-01-01

    The internal components of nuclear reactors built-in Zr alloys are prone to a failure mechanism known as Delayed Hydride Cracking (DHC). This situation has triggered numerous scientific studies in order to measure the crack propagation velocity and the threshold stress intensity factor associated to DHC. Tests are carried out on fatigued pre-crack samples to ensure similar test conditions and comparable results. Due to difficulties in implementing the fatigue pre-crack method it would be desirable to replace it with a pre-crack produced by the same process of DHC, for which is necessary to demonstrate equivalence of this two methods. In this work tests on samples extracted from two Zr-2.5 Nb tubes were conducted. Some of the samples were heat treated to obtain a range in their metallurgical properties as well as different DHC velocities. A comparison between velocities measured in test samples pre-cracked by fatigue and RDIH is done, demonstrating that the pre-cracking method does not affect the measured velocity value. In addition, the incubation (t inc ), which is the time between the application of the load and the first signal of crack propagation, in samples pre-cracked by RDIH, was measured. It was found that these times are sufficiently short, even in the worst cases (lower speed) and similar to the ones of fatigued pre-cracked samples. (author)

  18. Crack propagation and fracture in silicon carbide

    International Nuclear Information System (INIS)

    Evans, A.G.; Lange, F.F.

    1975-01-01

    Fracture mechanics and strength studies performed on two silicon carbides - a hot-pressed material (with alumina) and a sintered material (with boron) - have shown that both materials exhibit slow crack growth at room temperature in water, but only the hot-pressed material exhibits significant high temperature slow crack growth (1000 to 1400 0 C). A good correlation of the observed fracture behaviour with the crack growth predicted from the fracture mechanics parameters shows that effective failure predictions for this material can be achieved using macro-fracture mechanics data. (author)

  19. Natural zeolite bitumen cracking

    Energy Technology Data Exchange (ETDEWEB)

    Kuznicki, S.M.; McCaffrey, W.C.; Bian, J.; Wangen, E.; Koenig, A. [Alberta Univ., Edmonton, AB (Canada). Dept. of Chemical and Materials Engineering

    2006-07-01

    A study was conducted to demonstrate how low cost heavy oil upgrading in the field could reduce the need for diluents while lowering the cost for pipelining. Low cost field upgrading could also contribute to lowering contaminant levels. The performance of visbreaking processes could be improved by using disposable cracking agents. In turn, the economics of field upgrading of in-situ derived bitumen would be improved. However, in order to be viable, such agents would have to be far less expensive than current commercial cracking catalysts. A platy natural zeolite was selected for modification and testing due to its unique chemical and morphological properties. A catalyst-bearing oil sand was then heat-treated for 1 hour at 400 degrees C in a sealed microreactor. Under these mild cracking conditions, the catalyst-bearing oil sand produced extractable products of much lower viscosity. The products also contained considerably more gas oil and middle distillates than raw oil sand processed under the same conditions as thermal cracking alone. According to model cracking studies using hexadecane, these modified mineral zeolites may be more active cracking agents than undiluted premium commercial FCC catalyst. These materials hold promise for partial upgrading schemes to reduce solvent requirements in the field. tabs., figs.

  20. Physicochemical and in vitro antioxidant properties of pectin extracted from hot pepper (Capsicum annuum L. var. acuminatum (Fingerh.)) residues with hydrochloric and sulfuric acids.

    Science.gov (United States)

    Xu, Honggao; Tai, Kedong; Wei, Tong; Yuan, Fang; Gao, Yanxiang

    2017-11-01

    Transformation of hot pepper residues to value-added products with concomitant benefits on environmental pollution would be of great value to capsicum oleoresin manufacturers. Pectin, a soluble dietary fiber with multiple functions, from hot pepper residues was investigated in this study. The extraction of hot pepper pectin using hydrochloric acid was first optimized using response surface methodology (RSM). The most efficient parameters for maximum hot pepper pectin yield (14.63%, dry basis) were a pH of 1.0, a temperature of 90 °C, an extraction time of 2 h and a liquid-to-solid ratio of 20 L g -1 . The pectin was mainly composed of uronic acids, and the major neutral sugars were galactose and glucose. The structure of hot pepper pectin was characterized by homogalacturonan and rhamnogalacturonan I elements. The physicochemical properties of hot pepper pectin extracted by sulfuric acid and hydrochloric acid were further investigated. The content of protein and degree of esterification in hot pepper pectin extracted with sulfuric acid solution (SP) were higher (P hot pepper pectin, hot pepper residues would be a new source to obtain pectin, and SP would be more preferred than HP. © 2017 Society of Chemical Industry. © 2017 Society of Chemical Industry.

  1. Microstructure, mechanical properties and stress corrosion cracking of Al–Zn–Mg–Zr alloy sheet with trace amount of Sc

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Xing [School of Materials Science and Engineering, Central South University, Changsha 410083 (China); Pan, Qinglin, E-mail: pql1964@126.com [School of Materials Science and Engineering, Central South University, Changsha 410083 (China); Li, Bo [School of Materials Science and Engineering, Central South University, Changsha 410083 (China); Liu, Zhiming; Huang, Zhiqi [Guangdong Fenglu Aluminum Co., Ltd, Foshan 528133 (China); Yin, Zhimin [School of Materials Science and Engineering, Central South University, Changsha 410083 (China)

    2015-11-25

    Microstructural and property evolution of the Al–Zn–Mg–0.10%Sc–0.10%Zr alloy sheet during its preparation were investigated in detail by means of optical microscopy (OM), scanning electron microscope (SEM), energy dispersive X-ray (EDX), transmission electron microscopy (TEM), Vickers micro-hardness test and room temperature tensile test. Stress corrosion cracking (SCC) behavior of the Al–Zn–Mg–0.10%Sc–0.10%Zr alloy under different heat treatments was studied using slow strain rate test. The results showed that serious dendritic segregation existed in as-cast condition. The suitable homogenization treatment for Al–Zn–Mg–0.10%Sc–0.10%Zr alloy was 470 °C/24 h. After homogenization treatment, dissoluble Zn and Mg enriched non-equilibrium phases dissolved into α-Al matrix completely. The suitable solid solution-aging treatment for Al–Zn–Mg–0.10%Sc–0.10%Zr alloy was solution treated at 470 °C for 60 min, followed by water quenching and then aged at 120 °C for 24 h. Under this aging temper, the grain structures were composed of sub-grains, η′ phases and nanometer-sized, spherical Al{sub 3}(Sc, Zr) particles. Grain boundary precipitates (GBPs) area fraction was found to be an important parameter to evaluate the SCC susceptibility. The improved corrosion resistance from increasing aging temperature or prolonging aging time was due to the discontinuous η precipitates along the grain boundary and the high area fraction of GBPs. The main strengthening mechanisms of Al–Zn–Mg–0.10%Sc–0.10%Zr alloy are precipitation strengthening derived from η′ precipitates, dispersion strengthening, sub-grain strengthening and grain refinement caused by coherent Al{sub 3}(Sc, Zr) particles. - Highlights: • The suitable homogenization treatment of the alloy has been identified. • Evolution of microstructure and mechanical properties is investigated. • Strengthening mechanisms of the alloy has been established. • The basic mechanism has

  2. Influence of Sintering Temperature on the Microstructure and Mechanical Properties of In Situ Reinforced Titanium Composites by Inductive Hot Pressing

    Directory of Open Access Journals (Sweden)

    Cristina Arévalo

    2016-11-01

    Full Text Available This research is focused on the influence of processing temperature on titanium matrix composites reinforced through Ti, Al, and B4C reactions. In order to investigate the effect of Ti-Al based intermetallic compounds on the properties of the composites, aluminum powder was incorporated into the starting materials. In this way, in situ TixAly were expected to form as well as TiB and TiC. The specimens were fabricated by the powder metallurgy technique known as inductive hot pressing (iHP, using a temperature range between 900 °C and 1400 °C, at 40 MPa for 5 min. Raising the inductive hot pressing temperature may affect the microstructure and properties of the composites. Consequently, the variations of the reinforcing phases were investigated. X-ray diffraction, microstructural analysis, and mechanical properties (Young’s modulus and hardness of the specimens were carried out to evaluate and determine the significant influence of the processing temperature on the behavior of the composites.

  3. Physical properties of SnS thin films grown by hot wall deposition

    International Nuclear Information System (INIS)

    Gremenok, V.; Ivanov, V.; Bashkirov, S.; Unuchak, D.; Lazenka, V.; Bente, K.; Tashlykov, I.; Turovets, A.

    2010-01-01

    Full text : Recently, considerable effort has been invested to gain a better and deeper knowledge of structural and physical properties of metal chalcogenide semiconductors because of their potential application in electrical and photonic devices. Among them, tin sulphide (SnS) has attracted attention because of band gap of 1.3 eV and an absorption coefficient greater than 10 4 cm - 1. Additionally, by using tin sulfide compounds for photovoltaic devices, the production costs are decreased, because these materials are cheap and abundant in nature. For the sythesis of SnS thin films by hot wall deposition, SnS ingots were used as the source materials synthesized from high purity elements (99.999 percent). The thin films were grown onto glass at substrate temperatures between 220 and 380 degrees Celsium. The thickness of the films was in the range of 1.0 - 2.5 μm. The crystal structure and crystalline phases of the materials were studied by XRD using a Siemens D-5000 diffractometer with CuK α (λ = 1.5418 A) radiation. In order to consider instrumental error, the samples were coated by Si powder suspended in acetone. The composition and surface morphology of thin films were investigated by electron probe microanalysis (EPMA) using a CAMECA SX-100, a scanning electron microscope JEOL 6400 and an atomic force microscope (AFM, Model: NT 206), respectively. Depth profiling was performed by Auger electron spectroscopy (AES) using a Perkin Elmer Physical Electronics 590. The electrical resistivity was studied by van der Pauw four-probe technique using silver paste contact. The optical transmittance was carried out using a Varian Cary 50 UV - VIS spectrophotometer in the range 500 - 2000 nm. The as-grown films exhibited a composition with a Sn/S at. percent ratio of 1.06. The AES depth profiles revealed relatively uniform composition through the film thickness. The XRD analysis of the SnS films showed that they were monophase (JCPDS 39-0354), polycrystalline with

  4. Mechanical Properties and Microstructure of High-Strength Steel Controlled by Hot Stamping Process

    Science.gov (United States)

    Ou, Hang; Zhang, Xu; Xu, Junrui; Li, Guangyao; Cui, Junjia

    2018-03-01

    A novel design and manufacturing method, dubbed "precast," of the cooling system and tools for a hot forming process was proposed in this paper. The integrated structures of the punch and blank holder were determined by analyzing the bending and reverse-bending deformation of the forming parts. The desired crashworthiness performance of an automotive front bumper constructed with this process was obtained by a tailored phase transformation, which generated martensite-bainite in the middle and full martensite transformation in the corner areas. Varying cooling effects in the formed parts caused the highest temperature to be located in the bottom and the lowest on the end of the formed parts. Moreover, the microstructural distributions demonstrated that the bottom possessed a relatively lower content of martensite, while, conversely, the end possessed a higher content. This was precisely the most desired phase distributions for the hot formed parts. For the six-process cycle stamping, the temperatures reached a stable status after an initial rapid increase in the first three process cycles. The microstructural results verified the feasibility of the hot forming tools under multiprocess cycles.

  5. A study to evaluate therapeutic properties of minerals of manghopir hot spring, karachi

    International Nuclear Information System (INIS)

    Javed, A.; Iqbal, J.; Khan, F.A.; Siddiqui, I.

    2009-01-01

    European balneologists have extensively studied the therapeutic value of mineral water. Mineral springs with different mineral contents are recommended for various therapeutic uses. People have been using geothermal water for bathing and good health for many thousands of years A mineral hot spring has greater than 1000 mg/L (ppm) of naturally dissolved solids. Hot mineral spring water contains elements like calcium, magnesium, sodium, potassium as sulphates, bi- carbonates and chlorides, which are used externally to cure many diseases. Manghopir spring contain 38-84 mg/L calcium, 29-56 mg/L magnesium, 388-555 mg/L sodium, 411-599 mg/L chloride, 186-442 mg/L sulphate, 10-25 mg/L potassium, and 1509-2188 mg/L total dissolved solids while the pH was in the range of 7.2-7.8. The temperature of Manghopir Euthermal hot spring remains constant ranging between 40 to 47 degree C. (author)

  6. Comparison of anti-corrosive properties between hot alkaline nitrate blackening and hydrothermal blackening routes

    Energy Technology Data Exchange (ETDEWEB)

    Fattah-alhosseini, A. [Department of Materials Engineering, Bu-Ali Sina University, Hamedan 65178-38695 (Iran, Islamic Republic of); Yazdani Khan, H., E-mail: hamid.yazdanikhan@gmail.com [Department of Materials Engineering, Bu-Ali Sina University, Hamedan 65178-38695 (Iran, Islamic Republic of); Heidarpour, A. [Department of Metallurgy and Materials Engineering, Hamedan University of Technology, Hamedan, 65155-579 (Iran, Islamic Republic of)

    2016-08-15

    In this study, the oxide films were formed on carbon steel by using hot alkaline nitrate and hydrothermal treatments. A dense and protective oxide film was obtained by hydrothermal method due to application of high pressure and by increasing solution temperature from boiling temperature (155 °C) to 250 °C. Oxide films were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), and electrochemical tests including potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). These analyses showed that the magnetite film which was formed on carbon steel surface by hydrothermal treatment offers the best resistance in 3.5 wt.% NaCl solution. Although thicker oxide film could be obtained via hot alkaline nitrate black oxidizing, corrosion resistance was lower as a result of being highly porous and the presence of hematite. - Highlights: • Oxide films have been formed on steel by using of hot alkaline nitrate and hydrothermal treatments. • A dense and protective oxide film was obtained by hydrothermal treatment. • SEM micrographs showed that a dense and protective oxide film was obtained by hydrothermal treatment. • Film formed by hydrothermal treatment could have the best resistance in 3.5 wt.% NaCl solution.

  7. Correlation of hot-microhardness with elevated-temperature tensile properties of low activation ferritic steel

    International Nuclear Information System (INIS)

    Hsu Chenyih

    1986-01-01

    Hot microhardness and elevated temperature tensile tests have been performed on 9Cr-2.5W-0.3V-0.15C(GA3X) low activation ferritic steel at temperatures from 20 0 C to 650 0 C. The uniform elongation of the tensile test correlated well with the ductility parameter of the microhardness test. The hot-microhardness test showed a sensitive response to the softening and changes in ductility of the GA3X steel. The ultimate tensile strength and 0.2% yield strength of this steel correlated well with hot microhardness data at test temperatures up to 400 0 C using Cahoon's expressions σ uts = (H/2.9)(n/0.217) n and σ ys = (H/3)(0.1) n , respectively, where H is the diamond pyramid hardness and n is the strain hardening exponent. A 20-30% underestimate of tensile strengths were obtained using Cahoon's expressions at temperatures above 400 0 C, which is probably attributed to creep deformation and may be improved by selecting a proper loading condition during the hardness test. (orig.)

  8. Structure and Properties of Silica Glass Densified in Cold Compression and Hot Compression

    Science.gov (United States)

    Guerette, Michael; Ackerson, Michael R.; Thomas, Jay; Yuan, Fenglin; Bruce Watson, E.; Walker, David; Huang, Liping

    2015-10-01

    Silica glass has been shown in numerous studies to possess significant capacity for permanent densification under pressure at different temperatures to form high density amorphous (HDA) silica. However, it is unknown to what extent the processes leading to irreversible densification of silica glass in cold-compression at room temperature and in hot-compression (e.g., near glass transition temperature) are common in nature. In this work, a hot-compression technique was used to quench silica glass from high temperature (1100 °C) and high pressure (up to 8 GPa) conditions, which leads to density increase of ~25% and Young’s modulus increase of ~71% relative to that of pristine silica glass at ambient conditions. Our experiments and molecular dynamics (MD) simulations provide solid evidences that the intermediate-range order of the hot-compressed HDA silica is distinct from that of the counterpart cold-compressed at room temperature. This explains the much higher thermal and mechanical stability of the former than the latter upon heating and compression as revealed in our in-situ Brillouin light scattering (BLS) experiments. Our studies demonstrate the limitation of the resulting density as a structural indicator of polyamorphism, and point out the importance of temperature during compression in order to fundamentally understand HDA silica.

  9. Computer simulation of cooling properties of UF5 hot-clusters in argon

    International Nuclear Information System (INIS)

    Okamoto, Tsuyoshi; Ohno, Fubito

    1999-01-01

    Brownian collision-coalescence models have been proposed by many researchers to describe a cluster or a particle growth process. In these mathematical models, the effect of a cluster temperature on a sticking probability is not included, although the cluster temperature is one of the most important factors which determines the particle growth rate at the incipient stage of coagulation. A hot-cluster consisting of 30 UF 5 molecules is formed in a computer and is bombarded with argon atoms. Measuring a kinetic energy of argon atom scattered from the hot-cluster, the cluster temperature can be estimated by molecular dynamics simulations. It is concluded that the hot-cluster is rapidly cooled under the conditions of molecular laser isotope separation (MLIS) process, so that the cluster-argon system can reach its thermal equilibrium state. Therefore, in the analysis of the dynamics of clustering process, the temperature of UF 5 molecular cluster may be set equal to that of argon gas. (author)

  10. Software Simulation of Hot Tearing

    DEFF Research Database (Denmark)

    Andersen, S.; Hansen, P.N.; Hattel, Jesper Henri

    1999-01-01

    The brittleness of a solidifying alloy in a temperature range near the solidus temperature has been recognised since the fifties as the mechanism responsible for hot tearing. Due to this brittlenes, the metal will crack under even small amounts of strain in that temperature range. We see these hot...... tears in castings close to hot centres, where the level of strain is often too high.Although the hot tearing mechanism is well understood, until now it has been difficult to do much to reduce the hot tearing tendency in a casting. In the seventies, good hot tearing criteria were developed by considering...... the solidification rate and the strain rate of the hot tear prone areas. But, until recently it was only possible to simulate the solidification rate, so that the criteria could not be used effectively.Today, with new software developments, it is possible to also simulate the strain rate in the hot tear prone areas...

  11. Hot coiled steel strip with elevated niobium content for pipelines and its weldability

    International Nuclear Information System (INIS)

    Brozda, J.; Zeman, M.

    2010-01-01

    Examinations and tests have been performed on thermomechanically rolled and hot coiled 14 mm thick steel strips with a low carbon and elevated niobium content, assigned for the production of pipelines. There were examined basic mechanical properties of the steels, brittle fracture resistance of the parent material and simulated HAZ's, susceptibility to cold cracking as well as properties of MMA and GMA welded joints. It was found that the tested steels are characterized by a good weldability, are not prone to cold cracking, have a low brittle fracture transition temperature and the HAZ of welded joints shows a sufficient high brittle fracture resistance. (authors)

  12. Mechanical properties and thermal stability of Al–Fe–Ni alloys prepared by centrifugal atomisation and hot extrusion

    International Nuclear Information System (INIS)

    Průša, F.; Vojtěch, D.; Michalcová, A.; Marek, I.

    2014-01-01

    In this work, Al–12Fe and Al–7Fe–5Ni (wt%) alloys prepared by a novel technique including centrifugal atomisation and hot extrusion were studied. The microstructures were investigated using light microscopy, electron scanning microscopy, transmission electron microscopy and X-ray diffraction. The mechanical properties were determined by Vickers hardness measurements and compressive stress–strain tests. To study the thermal stability, the mechanical properties were also measured after 100 h of annealing at 300 °C and 400 °C. In addition, creep tests at a stress of 120 MPa and a temperature of 300 °C were performed. The investigated materials were composed of fine-grained α-Al and intermetallic phases identified as Al 13 Fe 4 and Al 9 FeNi. The Vickers hardness and compressive yield strength were 68 HV5 and 183 MPa, respectively, for the Al–12Fe alloy and 73 HV5 and 226 MPa, respectively, for the Al–7Fe–5Ni alloy. After long-term annealing, the change in the mechanical properties was negligible, indicating the excellent thermal stability of both materials. The creep tests confirmed the highest thermal stability of the Al–7Fe–5Ni alloy with a total compressive creep strain of 15%. The “thermally stable” casting Al–12Si–1Cu–1Mg–1Ni alloy treated by the T6 regime was used as a reference material. The casting alloy exhibited sufficient mechanical properties (hardness and compressive yield strength) at room temperature. However, annealing remarkably softened and reduced its compressive yield strength to almost 50% of the initial values. Additionally, the total creep strain of the casting reference material was almost three times higher than that of the Al–7Fe–5Ni alloy. It has been proven that centrifugally atomised materials quickly compacted via hot extrusion can compete or even exceed the properties of common casting aluminium alloys that are used in automotive industry

  13. Influence of hot rolling and high speed hydrostatic extrusion on the microstructure and mechanical properties of RAF ODS steel

    International Nuclear Information System (INIS)

    Oksiuta, Z.; Kurzydlowski, K.J.; Baluc, N.

    2009-01-01

    Argon gas atomized, pre-alloyed Fe-14Cr-2W-0.3Ti oxide dispersion strengthened (ODS) ferritic steel powder was mechanically alloyed with 0.3Y2O3 (wt.%) nano-particles in attritor ball mill and consolidated by hot isostatic pressing (HIP) at 1150 deg. C under pressure of 200 MPa for 3 hrs. To improve mechanical properties of as HIPped ODS ingots the material was undergone further thermo-mechanical treatment (TMT), namely: hot rolling (HR) at 850 deg. C or high speed hot extrusion (HSHE) at 850 deg. C. After TMT both materials were annealed at 1050 deg. C for 1 h in vacuum. Transmission electron microscopy (TEM) observations of the ODS alloys after TMT and heat treatment exhibited elongated in a longitudinal direction grains with an average size of 75 μm. However, an equiaxed, smaller than 500 nm grains were also found in the microstructure of both materials. Different size and morphology of oxides particles were also observed. Bigger, about 150 nm Ti-Al-O particles were usually located at grain boundaries whereas Y-Ti-O nanoclusters of about 5 nm were uniformly distributed in ODS steel matrix. The Charpy impact tests revealed significantly better about 90% (5.8 J) upper shelf energy (USE) of material after HSHE but ductile to brittle transition temperature (DBTT) of both alloys was unsatisfactory. As-HR ODS steel has shown DBTT of about 55 deg. C whereas HSHE ODS steel has about 75 deg. C. This relatively high values of transition temperature were probably caused by oxides particles present at grain boundaries of the ODS alloys which decreased fracture properties of the ODS steels. High temperature tensile properties of both ODS alloys are found to be satisfactory in full range of the testing temperature from 23 up to 750 deg. C. However, about 15% better UTS and YS0.2 (1350 MPa and 1285 MPa, respectively) as well as ductility were measured in the case of the as-HSHE ODS steel. These results indicates that HSHE process of the ODS steel can be considered as more

  14. Fatigue property and fatigue cracks of ultra-fine grained copper processed by equal-channel angular pressing

    Czech Academy of Sciences Publication Activity Database

    Wang, Q.; Du, Z.; Liu, X.; Kunz, Ludvík

    2011-01-01

    Roč. 2011, č. 682 (2011), s. 231-237 ISSN 1013-9826 Institutional research plan: CEZ:AV0Z20410507 Keywords : ultrafine-grained copper * equal channel angular pressing * fatigue * fatigue cracks Subject RIV: JL - Materials Fatigue, Friction Mechanics

  15. Influence of hard particle addition and chemical interdiffusion on the properties of hot extruded tool steel compounds

    International Nuclear Information System (INIS)

    Silva, P.A.; Weber, S.; Inden, G.; Pyzalla, A.R.

    2009-01-01

    Low alloyed steel bars were co-extruded with pre-sintered tool steel powders with the addition of tungsten carbides (W 2 C/WC) as hard particles. During the hot extrusion process of these massive and powdery materials, an extrudate is formed consisting of a completely densified wear resistant coating layer and a bulk steel bar as the tough substrate core. This work combines experimental measurements (EPMA) and diffusion calculations (DICTRA TM ) to investigate the effect of hard particle addition and its dissolution, as well as the formation of M 6 C carbides on the properties of two different PM tool steel coatings hot extruded with a 1.2714 steel bar. A carburization effect resulting from the W 2 C hard particles is responsible for an increase of the 1.2344 steel matrix hardness. The mechanical properties of the interface region between coating matrix and substrate are influenced by chemical interdiffusion of carbon and other alloying elements occurring during heat treatment.

  16. Influence of substrate material on the microstructure and optical properties of hot wall deposited SnS thin films

    International Nuclear Information System (INIS)

    Bashkirov, S.A.; Gremenok, V.F.; Ivanov, V.A.; Shevtsova, V.V.; Gladyshev, P.P.

    2015-01-01

    Tin monosulfide SnS raises an interest as a promising material for photovoltaics. The influence of the substrate material on the microstructure and optical properties of SnS thin films with [111] texture obtained by hot wall vacuum deposition on glass, molybdenum and indium tin oxide substrates is reported. The lattice parameters for layers grown on different substrates were determined by X-ray diffraction and their deviations from the data reported in the literature for single α-SnS crystals were discussed. The change in the degree of preferred orientation of the films depending on the substrate material is observed. The direct nature of the optical transitions with the optical band gap of 1.15 ± 0.01 eV is reported. - Highlights: • SnS thin films were hot wall deposited on glass, molybdenum and indium tin oxide. • Physical properties of the films were studied with respect to the substrate type. • The SnS lattice parameter deviations were observed and the explanation was given. • The direct optical transitions with the band gap of 1.15 ± 0.01 eV were observed

  17. The main chemical properties of hot and cold mineral waters in Bayankhongor, Mongolia

    Directory of Open Access Journals (Sweden)

    D Oyuntsetseg

    2014-12-01

    Full Text Available In the current study, hot and cold mineral springs and sub mineral waters in the Bayankhongor province were examined for their chemical characteristics and identified cold mineral waters classification according to mineral water classification of Mongolia. The hot spring waters belong to Na+-HCO3- and Na+-SO42- types. The cold mineral spring of Lkham belongs to Ca2+-HCO3- type. All sub mineral waters are generally located in the two areas (northern part or mountain forest area and the southern part or Gobi desert area. TDS concentrations of cold springs of the southern part in the study area were higher than northern part’s cold springs. The total dissolved silica content of cold spring was ranged from 4.5mg/L to 26 mg/L which did not correspond to requirements of mineral water standard of Mongolia. Thus, these cold springs are belonging to sub mineral water classification. The sub mineral waters were characterized into four types such as a Ca2+-SO42-, Na+-SO42-, Na+-HCO3 and Ca2+ - HCO3 by their chemical composition in the study area. The values for the quartz, chalcedony geothermometer and the Na/K geothermometer were quite different. The silica-enthalpy mixing model predicts a subsurface reservoir temperature between 124 and 197°C and most of the hot waters have been  probably mixed with cold water. The result shows that an averaged value of calculated temperature ranges from 77°C to 119°C which indicates that studied area has low temperature geothermal resources. DOI: http://doi.dx.org/10.5564/mjc.v15i0.324 Mongolian Journal of Chemistry 15 (41, 2014, p56-62

  18. Effect of hot-air drying on the physicochemical properties of kaffir lime leaves (Citrus hystrix)

    OpenAIRE

    Juhari, Nurul Hanisah Binti; Lasekan, Ola; Muhammad, Kharidah; Karim, Shahrim

    2013-01-01

    The effect of hot-air drying namely drying time (3-15 h), drying temperature (40-80°C) and loading capacity (0.5-2.0 kg/m2 ) on the physicochemical characteristics of kaffir lime leaves was optimized using Response Surface Methodology. Twenty treatments were assigned based on the second- order CCD including 6 center points, 6 axial points and 8 factorial points. The quality of dried kaffir lime leaves was evaluated by determining moisture content, water activity, texture (brittleness) and Hun...

  19. Microstructure and mechanical properties of hot wire laser clad layers for repairing precipitation hardening martensitic stainless steel

    Science.gov (United States)

    Wen, Peng; Cai, Zhipeng; Feng, Zhenhua; Wang, Gang

    2015-12-01

    Precipitation hardening martensitic stainless steel (PH-MSS) is widely used as load-bearing parts because of its excellent overall properties. It is economical and flexible to repair the failure parts instead of changing new ones. However, it is difficult to keep properties of repaired part as good as those of the substrate. With preheating wire by resistance heat, hot wire laser cladding owns both merits of low heat input and high deposition efficiency, thus is regarded as an advantaged repairing technology for damaged parts of high value. Multi-pass layers were cladded on the surface of FV520B by hot wire laser cladding. The microstructure and mechanical properties were compared and analyzed for the substrate and the clad layer. For the as-cladded layer, microstructure was found non-uniform and divided into quenched and tempered regions. Tensile strength was almost equivalent to that of the substrate, while ductility and impact toughness deteriorated much. With using laser scanning layer by layer during laser cladding, microstructure of the clad layers was tempered to fine martensite uniformly. The ductility and toughness of the clad layer were improved to be equivalent to those of the substrate, while the tensile strength was a little lower than that of the substrate. By adding TiC nanoparticles as well as laser scanning, the precipitation strengthening effect was improved and the structure was refined in the clad layer. The strength, ductility and toughness were all improved further. Finally, high quality clad layers were obtained with equivalent or even superior mechanical properties to the substrate, offering a valuable technique to repair PH-MSS.

  20. Crack Propagation by Finite Element Method

    OpenAIRE

    H. Ricardo, Luiz Carlos

    2017-01-01

    Crack propagation simulation began with the development of the finite element method; the analyses were conducted to obtain a basic understanding of the crack growth. Today structural and materials engineers develop structures and materials properties using this technique. The aim of this paper is to verify the effect of different crack propagation rates in determination of crack opening and closing stress of an ASTM specimen under a standard suspension spectrum loading from FD&E SAE Keyh...

  1. Formation and early evolution of galaxies: Constraints on the properties of hot protogalaxies

    International Nuclear Information System (INIS)

    Berman, V.G.; Suchkov, A.A.

    1989-01-01

    In the framework of the hot model of galaxy formation, the following results are obtained: (1) to explain the mass and chemical composition of the intergalactic medium, the mass of the stellar component, and the mass of the x-ray coronas of giant elliptical and spiral galaxies (M s ∼ 10 11 Mass Sun ) the protogalaxies must have been heated to temperatures approximately five times greater than the virial temperature; (2) the x-ray luminosities of the coronas of models of spiral galaxies are less than for the analogous models of elliptical galaxies. Moreover, for unit potential of hidden mass the stellar mass of spiral galaxies is an order of magnitude greater; (3) if a hot protogalaxy is initially compact (R ∼ 20 kpc), then the stellar component is formed rapidly, during a time t ∼ 1 x 10 9 yr; but if the protogalaxy is diffuse (R ∼ 100 kpc), then t ∼ (5-7) x 10 9 yr; (4) coronas are not formed in models of heat-conducting protogalaxies; (5) hidden mass cannot be formed by low-mass stars formed in cooling flows - such flows do not arise if hidden mass is not present from the beginning. 23 refs., 4 figs., 2 tabs

  2. Hot tearing studies in AA5182

    Science.gov (United States)

    van Haaften, W. M.; Kool, W. H.; Katgerman, L.

    2002-10-01

    One of the major problems during direct chill (DC) casting is hot tearing. These tears initiate during solidification of the alloy and may run through the entire ingot. To study the hot tearing mechanism, tensile tests were carried out in semisolid state and at low strain rates, and crack propagation was studied in situ by scanning electron microscopy (SEM). These experimentally induced cracks were compared with hot tears developed in an AA5182 ingot during a casting trial in an industrial research facility. Similarities in the microstructure of the tensile test specimens and the hot tears indicate that hot tearing can be simulated by performing tensile tests at semisolid temperatures. The experimental data were compared with existing hot tearing models and it was concluded that the latter are restricted to relatively high liquid fractions because they do not take into account the existence of solid bridges in the crack.

  3. Microstructure, local mechanical properties and stress corrosion cracking susceptibility of an SA508-52M-316LN safe-end dissimilar metal weld joint by GTAW

    Energy Technology Data Exchange (ETDEWEB)

    Ming, Hongliang; Zhu, Ruolin [Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning KeyLaboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); University of Chinese Academy of Sciences, 19 Yuquan Road, Beijing 100049 (China); Zhang, Zhiming [Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning KeyLaboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Wang, Jianqiu, E-mail: wangjianqiu@imr.ac.cn [Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning KeyLaboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Han, En.-Hou.; Ke, Wei [Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning KeyLaboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Su, Mingxing [Shanghai Research Center for Weld and Detection Engineering Technique of Nuclear Equipment, Shanghai 201306 (China)

    2016-07-04

    The microstructure, local mechanical properties and local stress corrosion cracking susceptibility of an SA508-52M-316LN domestic dissimilar metal welded safe-end joint used for AP1000 nuclear power plant prepared by automatic gas tungsten arc welding was studied in this work by optical microscopy, scanning electron microscopy (with electron back scattering diffraction and an energy dispersive X-ray spectroscopy system), micro-hardness testing, local mechanical tensile testing and local slow strain rate tests. The micro-hardness, local mechanical properties and stress corrosion cracking susceptibility across this dissimilar metal weld joint vary because of the complex microstructure across the fusion area and the dramatic chemical composition change across the fusion lines. Briefly, Type I boundaries and Type II boundaries exist in 52Mb near the SA508-52Mb interface, a microstructure transition was found in SA508 heat affected zone, the residual strain and grain boundary character distribution changes as a function of the distance from the fusion boundary in 316LN heat affected zone, micro-hardness distribution and local mechanical properties along the DMWJ are heterogeneous, and 52Mw-316LN interface has the highest SCC susceptibility in this DMWJ while 316LN base metal has the lowest one.

  4. Influence of hot rolling and high speed hydrostatic extrusion on the microstructure and mechanical properties of an ODS RAF steel

    Energy Technology Data Exchange (ETDEWEB)

    Oksiuta, Z., E-mail: oksiuta@pb.edu.pl [Bialystok Technical University, Faculty of Mechanical Engineering, Wiejska 45c, 15-352 Bialystok (Poland); Lewandowska, M.; Kurzydlowski, K.J. [Warsaw University of Technology, Faculty of Materials Science and Engineering, Woloska 141, 02-504 Warsaw (Poland); Baluc, N. [Ecole Polytechnique Federale de Lausanne (EPFL), Centre de Recherches en Physique des Plasmas, Association Euratom-Confederation Suisse, 5232 Villigen PSI (Switzerland)

    2011-02-15

    An argon gas atomized, pre-alloyed Fe-14Cr-2W-0.3Ti (wt.%) reduced activation ferritic (RAF) steel powder was mechanically alloyed with 0.3wt.% Y{sub 2}O{sub 3} nano-particles in an attritor ball mill and consolidated by hot isostatic pressing at 1150 {sup o}C under a pressure of 200 MPa for 3 h. In the aim to improve its mechanical properties the ODS steel was then submitted to a thermo-mechanical treatment (TMT): hot rolling (HR) at 850 deg. C or high speed hydrostatic extrusion (HSHE) at 900 deg. C, followed by heat treatment (HT). Transmission electron microscopy (TEM) observations of the ODS alloys after TMT and heat treatment revealed the presence of elongated grains in the longitudinal direction, with an average width of 8 {mu}m and an average length of 75 {mu}m, and equiaxed grains, a few microns in diameter, in the transverse direction. Two populations of oxide particles were observed by TEM: large Ti-Al-O particles, up to 250 nm in diameter, usually located at the grain boundaries and small Y-Ti-O nanoclusters, about 2.5 nm in diameter, uniformly distributed in the matrix. Charpy impact tests revealed that the HSHE material exhibits a larger upper shelf energy (5.8 J) than the HR material (2.9 J). The ductile-to-brittle transition temperature of both alloys is relatively high, in the range of 55-72 deg. C. Tensile mechanical properties of both ODS alloys were found satisfactory over the full range of investigated temperatures (23-750 deg. C). The HSHE material exhibits better tensile strength and ductility than the HR material. These results indicate that HSHE can be considered as a promising TMT method for improving the mechanical properties of ODS RAF steels.

  5. Influence of stress on martensitic transformation and mechanical properties of hot stamped AHSS parts

    International Nuclear Information System (INIS)

    Chang, Y.; Li, X.D.; Zhao, K.M.; Wang, C.Y.; Zheng, G.J.; Hu, P.; Dong, H.

    2015-01-01

    Non-isothermal tension and compression tests of 22MnB5 boron steel were carried out in this study. How different stress state influences the martensitic transformation of advanced high strength steel (AHSS) parts was analyzed. The analysis reveals that the martensitic transformation starting temperature (M s ) changes with different stress states. Specifically, the M s temperature rises with increasing tensile stress, however, it rises first and then drops with increasing compressive stress. Moreover, a higher initial forming temperature leads to a higher M s temperature under the same stress. Simulation of an actual hot-formed AHSS B-pillar together with the microscopic metallography, hardness and martensitic content shows that in higher tensile stress dominated area, the martensitic content and hardness are usually higher than in other areas. Although the stress can promote the M s temperature, a lower cooling rate may lead to less martensite fraction

  6. Influence of stress on martensitic transformation and mechanical properties of hot stamped AHSS parts

    Energy Technology Data Exchange (ETDEWEB)

    Chang, Y.; Li, X.D. [School of Automotive Engineering, National Key Laboratory of Industrial Equipment Structural Analysis, Dalian University of Technology, Dalian 116024 (China); Zhao, K.M., E-mail: kmzhao@dlut.edu.cn [School of Automotive Engineering, National Key Laboratory of Industrial Equipment Structural Analysis, Dalian University of Technology, Dalian 116024 (China); Wang, C.Y. [Institute for Special Steels, Central Iron & Steel Research Institute, Beijing 100081 (China); Zheng, G.J.; Hu, P. [School of Automotive Engineering, National Key Laboratory of Industrial Equipment Structural Analysis, Dalian University of Technology, Dalian 116024 (China); Dong, H. [Institute for Special Steels, Central Iron & Steel Research Institute, Beijing 100081 (China)

    2015-04-01

    Non-isothermal tension and compression tests of 22MnB5 boron steel were carried out in this study. How different stress state influences the martensitic transformation of advanced high strength steel (AHSS) parts was analyzed. The analysis reveals that the martensitic transformation starting temperature (M{sub s}) changes with different stress states. Specifically, the M{sub s} temperature rises with increasing tensile stress, however, it rises first and then drops with increasing compressive stress. Moreover, a higher initial forming temperature leads to a higher M{sub s} temperature under the same stress. Simulation of an actual hot-formed AHSS B-pillar together with the microscopic metallography, hardness and martensitic content shows that in higher tensile stress dominated area, the martensitic content and hardness are usually higher than in other areas. Although the stress can promote the M{sub s} temperature, a lower cooling rate may lead to less martensite fraction.

  7. Structure and properties of highly oriented polyoxymethylene produced by hot stretching

    International Nuclear Information System (INIS)

    Zhao Xiaowen; Ye Lin

    2011-01-01

    Research highlights: → Highly oriented POM was fabricated through solid hot stretching technology → Tensile strength and modulus of POM increased remarkably with draw ratio. → The crystal structure of POM changed from spherulite to mat texture by drawing. → Crystallinity and orientation factor of POM increased remarkably by drawing. → The mechanical structure model of microfibril of POM was established. - Abstract: Highly oriented self-reinforced polyoxymethylene (POM) was successfully fabricated through solid phase hot stretching technology. The tensile strength and modulus increased with draw ratio, which reached 900 MPa and 12 GPa, respectively at a high draw ratio of 900% without remarkable drop of the elongation at break. The structure and morphology of the drawn products were studied and the mechanical structure model of microfibril of POM was established. Raman spectral exhibited a low-frequency shift, which indicated two types of molecular chains with different response to the stress. During drawing, the spherulitic structure of POM was broken up and the mat texture crystals were formed. With the increase of draw ratio, the melting peak moved to high temperature and an additional shoulder peak ascribed to melting of highly chain-extended and oriented crystalline blocks was observed. X-ray diffraction showed that the crystallinity and orientation factor increased, while the grain size perpendicular to (1 0 0) crystal plane of POM decreased by drawing. The α relaxation peak corresponding to the glass transition temperature of POM (T g ) moved to high temperature with draw ratio. The section morphology of drawn POM exhibited a fibrillar structure which contributed to the significantly high tensile strength and modulus of the product.

  8. Properties of Hot and Fast Rotating Atomic Nuclei Studied by Means of Giant Dipole Resonance in Exclusive Experiments

    International Nuclear Information System (INIS)

    Maj, A.

    2000-01-01

    This work entitled ''Properties of hot and fast rotating atomic nuclei studied by means of Giant Dipole Resonance in exclusive experiments'', is the habilitation thesis of dr. Adam Maj. It consists of the review (in Polish) of performed research and of attached reprints from 16 original publications (in English) which A. Maj is the main or one of the main authors. All the studies were performed in collaboration with the groups from Milano and Copenhagen, using the HECTOR array equipment (described in chapter V). The Giant Dipole Resonance couples to the quadrupole degrees of freedom of the nucleus, and therefore constitutes a unique probe to test the shapes of atomic nuclei. In addition, the γ decay of the GDR from highly excited nuclei is a very fast process, it can compete with other modes of nuclear decay, and therefore can provide the information on the initial stages of excited nuclei. The presented investigations were concentrated on the following aspects: the shapes and thermal shape fluctuations, the origin of the behaviour of the GDR width, the properties of some exotic nuclei (Jacobi shapes, superdeformation, superheavy nuclei) and on ''entrance channel'' effects. The GDR γ decay was measured for nuclei with very different masses: from light nuclei with A≅45, through A≅110, 145,170,190, up to superheavy nuclei with A≅270. The shapes of hot nuclei are not fixed but fluctuate. The extent of these fluctuations and their influence on the measured quantities (GDR strength function, angular distribution and effective shape) is discussed in chapter VI.1. The observed width of the GDR is found to arise from the interplay of two effects: the thermal shape fluctuations, which are controlled by the nuclear temperature, and the deformation effects, controlled by the angular momentum. The ''collisional damping'' effect, which should influence the intrinsic GDR width, was found to be negligible (chapter VI.2). The GDR γ decay from hot superheavy nucleus 272 Hs

  9. Heat treatment, microstructure and mechanical properties of a C–Mn–Al–P hot dip galvanizing TRIP steel

    Energy Technology Data Exchange (ETDEWEB)

    Ding, Wei [School of Material and Metallurgy, Inner Mongolia University of Science and Technology, Baotou 014010 (China); Department of Materials Science and Engineering, KTH Royal Institute of Technology, SE-100 44 Stockholm (Sweden); Bayan Obo multimetallic resource comprehensive utilization Key lab, Inner Mongolia University of Science and Technology, Baotou 014010 (China); Hedström, Peter [Department of Materials Science and Engineering, KTH Royal Institute of Technology, SE-100 44 Stockholm (Sweden); Li, Yan [Department of Materials Science and Engineering, KTH Royal Institute of Technology, SE-100 44 Stockholm (Sweden); Bayan Obo multimetallic resource comprehensive utilization Key lab, Inner Mongolia University of Science and Technology, Baotou 014010 (China)

    2016-09-30

    Heat treatments of a hot dip galvanizing TRIP (Transformation induced plasticity) steel with chemical composition 0.20C-1.50Mn-1.2Al-0.07P(mass%) were performed in a Gleeble 3500 laboratory equipment. The heat treatment process parameters were varied to investigate the effect of intercritical annealing temperature as well as isothermal bainitic transformation (IBT) temperature and time, on the microstructure and the mechanical properties. The microstructure was investigated using scanning electron microscopy, transmission electron microscopy and x-ray diffraction, while mechanical properties were evaluated by tensile testing. Furthermore, to generate a better understanding of the phase transformations during heat treatment, dilatometry trials were conducted. The desired microstructure containing ferrite, bainite, retained austenite and martensite was obtained after the heat treatments. It was further found that the IBT is critical in determining the mechanical properties of the steel, since it controls the fraction of bainite. With increasing bainite fraction, the fraction of retained austenite increases while the fraction of martensite decreases. The mechanical properties of the steel are excellent with a tensile strength above 780 MPa (expect in one case) and elongation above 22%.

  10. Heat treatment, microstructure and mechanical properties of a C–Mn–Al–P hot dip galvanizing TRIP steel

    International Nuclear Information System (INIS)

    Ding, Wei; Hedström, Peter; Li, Yan

    2016-01-01

    Heat treatments of a hot dip galvanizing TRIP (Transformation induced plasticity) steel with chemical composition 0.20C-1.50Mn-1.2Al-0.07P(mass%) were performed in a Gleeble 3500 laboratory equipment. The heat treatment process parameters were varied to investigate the effect of intercritical annealing temperature as well as isothermal bainitic transformation (IBT) temperature and time, on the microstructure and the mechanical properties. The microstructure was investigated using scanning electron microscopy, transmission electron microscopy and x-ray diffraction, while mechanical properties were evaluated by tensile testing. Furthermore, to generate a better understanding of the phase transformations during heat treatment, dilatometry trials were conducted. The desired microstructure containing ferrite, bainite, retained austenite and martensite was obtained after the heat treatments. It was further found that the IBT is critical in determining the mechanical properties of the steel, since it controls the fraction of bainite. With increasing bainite fraction, the fraction of retained austenite increases while the fraction of martensite decreases. The mechanical properties of the steel are excellent with a tensile strength above 780 MPa (expect in one case) and elongation above 22%.

  11. Hot-injection synthesis of Ni-ZnO hybrid nanocrystals with tunable magnetic properties and enhanced photocatalytic activity

    Energy Technology Data Exchange (ETDEWEB)

    Zeng, Deqian; Qiu, Yulong; Chen, Yuanzhi, E-mail: yuanzhi@xmu.edu.cn; Zhang, Qinfu; Liu, Xiang; Peng, Dong-Liang, E-mail: dlpeng@xmu.edu.cn [Xiamen University, Department of Materials Science and Engineering, Fujian Provincial Key Laboratory of Materials Genome, Collaborative Innovation Center of Chemistry for Energy Materials, College of Materials (China)

    2017-04-15

    Magnetic metal-semiconductor hybrid nanocrystals containing ferromagnetic Ni and semiconductor ZnO have been prepared via a hot-injection route. The Ni-ZnO hybrid nanocrystals have a flower-like morphology that consists of Ni inner cores and ZnO petal shells. In spite of their large lattice mismatch, ZnO nanocrystals can still grow on faceted Ni nanocrystals to form stable interfaces. The composition of Ni-ZnO hybrid nanocrystals is readily controlled, and the average size of Ni core is tunable from 25 to 50 nm. Room temperature ferromagnetic properties are observed in these hybrid nanocrystals, and tunable magnetic properties also can be achieved by varying the size of Ni core. The as-prepared Ni-ZnO hybrid nanocrystals exhibit enhanced photocatalytic performance under ultraviolet light illumination as compared to pure ZnO nanocrystals. Furthermore, the superior reusability of hybrid nanocrystals for photocatalytic application is achieved by virtue of their magnetic properties. The facile and efficient seed-mediate strategy is particularly attractive to construct hybrid magnetic-semiconducting heterostructures. The as-obtained Ni-ZnO hybrid nanocrystals offer great potential for various applications due to their combined magnetic and semiconducting properties and low-cost earth-abundant availability.

  12. Investigation of a hot-pressed Nb–Ti–Al alloy: Mechanical alloying, microstructure and mechanical property

    Energy Technology Data Exchange (ETDEWEB)

    Shi, Zhiwu; Wei, Hua; Zhang, Hongyu; Jin, Tao; Sun, Xiaofeng; Zheng, Qi, E-mail: qzheng@imr.ac.cn

    2016-01-10

    The Nb–23Ti–15Al (at%) alloy was prepared by mechanical alloying (MA) and hot-pressing (HPing). The microstructure evolution of powder particles during MA and its influence on the microstructure and mechanical properties of the hot-pressed (HPed) alloy have been investigated. The powder and HPed alloy were characterized via X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results indicate that particle size increases in the first stage and then decreases in the second stage during MA; as milling speed increases, mechanically alloyed (MAed) powder with convoluted elemental lamellae, homogeneous Nb solid-solution and an amorphous phase could be obtained respectively in 24 h. Higher homogeneity in microstructure and composition of the MAed powder particles promotes the precipitation of the δ phase and refines the β and Ti(O,C) phases in the HPed alloy. Moreover, due to the phase equilibrium changes caused by Fe and Cr in the amorphous powder, σ phase appears in the alloy as a stable phase instead of the δ phase. Properly MAed powder contributes to higher hardness of the HPed alloy, for reasons of microstructure refinement and sufficient precipitating of strengthening phases.

  13. Investigation of a hot-pressed Nb–Ti–Al alloy: Mechanical alloying, microstructure and mechanical property

    International Nuclear Information System (INIS)

    Shi, Zhiwu; Wei, Hua; Zhang, Hongyu; Jin, Tao; Sun, Xiaofeng; Zheng, Qi

    2016-01-01

    The Nb–23Ti–15Al (at%) alloy was prepared by mechanical alloying (MA) and hot-pressing (HPing). The microstructure evolution of powder particles during MA and its influence on the microstructure and mechanical properties of the hot-pressed (HPed) alloy have been investigated. The powder and HPed alloy were characterized via X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results indicate that particle size increases in the first stage and then decreases in the second stage during MA; as milling speed increases, mechanically alloyed (MAed) powder with convoluted elemental lamellae, homogeneous Nb solid-solution and an amorphous phase could be obtained respectively in 24 h. Higher homogeneity in microstructure and composition of the MAed powder particles promotes the precipitation of the δ phase and refines the β and Ti(O,C) phases in the HPed alloy. Moreover, due to the phase equilibrium changes caused by Fe and Cr in the amorphous powder, σ phase appears in the alloy as a stable phase instead of the δ phase. Properly MAed powder contributes to higher hardness of the HPed alloy, for reasons of microstructure refinement and sufficient precipitating of strengthening phases.

  14. A Factorial Design Approach to Analyse the Effect of Coarse Recycled Concrete Aggregates on the Properties of Hot Mix Asphalt

    Science.gov (United States)

    Tanty, Kiranbala; Mukharjee, Bibhuti Bhusan; Das, Sudhanshu Shekhar

    2018-06-01

    The present study investigates the effect of replacement of coarse fraction of natural aggregates by recycled concrete aggregates on the properties of hot mix asphalt (HMA) using general factorial design approach. For this two factors i.e. recycled coarse aggregates percentage [RCA (%)] and bitumen content percentage [BC (%)] are considered. Tests have been carried out on the HMA type bituminous concrete, prepared with varying RCA (%) and BC (%). Analysis of variance has been performed on the experimental data to determine the effect of the chosen factors on various parameters such as stability, flow, air void, void mineral aggregate, void filled with bitumen and bulk density. The study depicts that RCA (%) and BC (%) have significant effect on the selected responses as p value is less than the chosen significance level. In addition to above, the outcomes of the statistical analysis indicate that interaction between factors have significant effects on void mineral aggregate and bulk density of bituminous concrete.

  15. Experimental investigation on the thermal properties of hydrogen jet flame and hot currents in the downstream region

    Energy Technology Data Exchange (ETDEWEB)

    Imamura, Tomohiko; Mogi, Toshio; Wada, Yuji; Horiguchi, Sadashige [Research Core for Explosion Safety, National Institute of Advanced Industrial Science and Technology (AIST), 16-1 Onogawa, Tsukuba, Ibaraki 305-8569 (Japan); Hamada, Shota; Miyake, Atsumi; Ogawa, Terushige [Graduate School of Environment and Information Sciences, Yokohama National University, 79-7 Tokiwadai, Hodogaya-ku, Yokohama 240-8501 (Japan)

    2008-07-15

    A series of experiments were conducted to understand the thermal hazards of hydrogen jet flames. In particular, we focused on the temperature properties of hot currents in the downstream region, because it was expected that this involved the most serious thermal hazards. The flame length and width depended on the nozzle diameter and the spouting pressure, namely, the mass flow rate, with similar dependences that were reported by other researchers. The temperature rise from ambient air along the trajectory depended on the balance of the flame length and the traveling distance from the flame tip. The position of the trajectory depended not only on the balance of flame length and the traveling distance, but also on the horizontal momentum induced by the spouting pressure. Empirical formulae for predicting the position and temperature rise of the trajectory were developed by the flame length, traveling distance, spouting pressure, and nozzle diameter as variables. (author)

  16. A Factorial Design Approach to Analyse the Effect of Coarse Recycled Concrete Aggregates on the Properties of Hot Mix Asphalt

    Science.gov (United States)

    Tanty, Kiranbala; Mukharjee, Bibhuti Bhusan; Das, Sudhanshu Shekhar

    2018-02-01

    The present study investigates the effect of replacement of coarse fraction of natural aggregates by recycled concrete aggregates on the properties of hot mix asphalt (HMA) using general factorial design approach. For this two factors i.e. recycled coarse aggregates percentage [RCA (%)] and bitumen content percentage [BC (%)] are considered. Tests have been carried out on the HMA type bituminous concrete, prepared with varying RCA (%) and BC (%). Analysis of variance has been performed on the experimental data to determine the effect of the chosen factors on various parameters such as stability, flow, air void, void mineral aggregate, void filled with bitumen and bulk density. The study depicts that RCA (%) and BC (%) have significant effect on the selected responses as p value is less than the chosen significance level. In addition to above, the outcomes of the statistical analysis indicate that interaction between factors have significant effects on void mineral aggregate and bulk density of bituminous concrete.

  17. Effects of Changing Hot Rolling Direction on Microstructure, Texture and Mechanical Properties of Cu-2.7Be Sheets

    Science.gov (United States)

    Zhu, Daibo; Liu, Chuming; Yu, Haijun; Han, Tan

    2018-03-01

    A hot rolling scheme (cross-rolling and unidirectional rolling) was adopted to process Cu-2.7Be sheets used as multiplier dynodes in photomultiplier. The effects of changing rolling direction on microstructure, texture and mechanical properties were studied by a combination of XRD, EBSD and TEM. It was found that higher copper-type texture and lower brass texture intensity were obtained in the ultimately cross-rolling (CR) sheet compared with the unidirectional rolling (UR) sheet.The EBSD results indicated that the grain orientation from mainly for UR sample turns to random for CR sample. Great enhancements in YS and UTS after unidirectional rolling were attributed to the massive and polygonal γ precipitates. The CR sample exhibited lower anisotropy, because of the increase of S and γ precipitates with spherical and tiny shape.

  18. A study of the long-term properties of Jovian hot spots from HST and ground-based observations between 1994 and 1998

    Science.gov (United States)

    Arregui, E.; Rojas, J. F.; Sanchez-Lavega, A.; Lecacheux, J.; Colas, F.; Miyazaki, I.; Parker, D.

    2000-10-01

    We have used the HST-WFPC2 archived images of Jupiter in the period 1994-1998 together with a large set of CCD ground based images, to study the zonal distribution, long-term motions, lifetimes, interactions and other properties of the hot spot - plume regions at 7 degrees North. Red and near infrared filters covering the wavelength range 650 - 953 nm have been used since they show the hot spots with a high contrast. We have found that the hot spots have velocities ranging from 95 to 112 m/s and are grouped typically in families of three to six members. We do not found any correlation between their velocity and wavenumber. The long-term survey allowed us to identify mergers and splitting of the hot spots areas. The Spanish team was supported by Gobierno Vasco PI 034/97. The French team was supported by the "Programme National de Planetologie."

  19. Mechanical properties and thermal stability of Al–Fe–Ni alloys prepared by centrifugal atomisation and hot extrusion

    Energy Technology Data Exchange (ETDEWEB)

    Průša, F., E-mail: Filip.Prusa@vscht.cz; Vojtěch, D.; Michalcová, A.; Marek, I.

    2014-05-01

    In this work, Al–12Fe and Al–7Fe–5Ni (wt%) alloys prepared by a novel technique including centrifugal atomisation and hot extrusion were studied. The microstructures were investigated using light microscopy, electron scanning microscopy, transmission electron microscopy and X-ray diffraction. The mechanical properties were determined by Vickers hardness measurements and compressive stress–strain tests. To study the thermal stability, the mechanical properties were also measured after 100 h of annealing at 300 °C and 400 °C. In addition, creep tests at a stress of 120 MPa and a temperature of 300 °C were performed. The investigated materials were composed of fine-grained α-Al and intermetallic phases identified as Al{sub 13}Fe{sub 4} and Al{sub 9}FeNi. The Vickers hardness and compressive yield strength were 68 HV5 and 183 MPa, respectively, for the Al–12Fe alloy and 73 HV5 and 226 MPa, respectively, for the Al–7Fe–5Ni alloy. After long-term annealing, the change in the mechanical properties was negligible, indicating the excellent thermal stability of both materials. The creep tests confirmed the highest thermal stability of the Al–7Fe–5Ni alloy with a total compressive creep strain of 15%. The “thermally stable” casting Al–12Si–1Cu–1Mg–1Ni alloy treated by the T6 regime was used as a reference material. The casting alloy exhibited sufficient mechanical properties (hardness and compressive yield strength) at room temperature. However, annealing remarkably softened and reduced its compressive yield strength to almost 50% of the initial values. Additionally, the total creep strain of the casting reference material was almost three times higher than that of the Al–7Fe–5Ni alloy. It has been proven that centrifugally atomised materials quickly compacted via hot extrusion can compete or even exceed the properties of common casting aluminium alloys that are used in automotive industry.

  20. 3-D thermal stress analysis of hot spots in reactor piping using BEM

    International Nuclear Information System (INIS)

    Bains, R.S.; Sugimoto, Jun

    1994-08-01

    A three-dimensional steady state thermoelastic analysis has been conducted on the hot leg of a pressurized water reactor(PWR) containing localized hot spots resulting from fission product aerosol deposition occurring during a hypothetical severe accident. The boundary element method (BEM) of numerical solution was successfully employed to investigate the structural response of the hot leg. Convergence of solution can be realized provided sufficiently large number of elements are employed and correct modelling of the temperature transition region (TTR) adjacent to the hot spot on the inner surface is conducted. The only correct temperature field across the TTR is that which can be represented by the interpolation functions employed in the BEM code. Further, incorrect solutions can also be generated if the TTR is too thin. The nature of the deformation at the hot spot location depends on whether the thermal boundary condition on the outer surface of the hot leg is one of constant temperature or adiabatic. The analysis shows that at the location of the hot spot on the inner surface large compressive stresses can be established. On the outer surface at the same location, large tensile stresses can be established. The presence of these large stress elevations in the vicinity of the hot spot could be detrimental to the integrity of the hot leg. The tensile stresses are extremely important since they can act as sites of crack initiation and subsequent propagation. Once a crack propagates through the thickness, leak worthiness of the hot leg comes into question. Consequently, additional analysis incorporating the effects of plasticity and temperature dependence of the material properties must be conducted to ascertain the integrity of the hot leg. (J.P.N.)

  1. Mechanical properties of hot-pressed SiC-TiC composites

    Directory of Open Access Journals (Sweden)

    Kamil Kornaus

    2017-12-01

    Full Text Available SiC-TiC composites, with 0, 5, 10 and 20 vol.% of TiC, were sintered by the hot-pressing technique at temperature of 2000 °C under argon atmosphere. SiC sintering process was activated by liquid phase created by the reaction between Al2O3 and Y2O3, in which it is possible to dissolve passivating oxide layers (SiO2 and TiO2 and partially SiC and TiC carbides. Microstructure observation and density measurements confirmed that the composites were dense with uniformly distributed components. Differences in thermal expansion coefficients between SiC and TiC led to complex stress state occurrence. These stresses combined with the liquid-derived separate phase between grains boundaries increased fracture toughness of the composites, which ranged from 5.8 to 6.3 MPa·m0.5. Opposite to the bending strength, fracture toughness increased with the TiC volume fraction. By means of simulation of residual thermal stresses in the composites, it was found that with the increasing volume fraction of TiC, tensile stress in TiC grains is reduced simultaneously with strong rise of compressive stresses in the matrix.

  2. Physical properties characterization of WO3 films grown by hot-filament metal oxide deposition

    International Nuclear Information System (INIS)

    Diaz-Reyes, J.; Delgado-Macuil, R.J.; Dorantes-Garcia, V.; Perez-Benitez, A.; Balderas-Lopez, J.A.; Ariza-Ortega, J.A.

    2010-01-01

    WO 3 is grown by hot-filament metal oxide deposition (HFMOD) technique under atmospheric pressure and an oxygen atmosphere. By X-ray diffraction obtains that WO 3 presents mainly monoclinic crystalline phase. The chemical stoichiometry is obtained by X-ray Photoelectron Spectroscopy (XPS). The IR spectrum of the as-grown WO 3 presents broad peaks in the range of 1100 to 3600 cm -1 . A broad band in the 2200 to 3600 cm -1 region and the peaks sited at 1645 and 1432 cm -1 are well resolved, which are originated from moisture and are assigned to ν(OH) and δ(OH) modes of adsorbed water and the corresponding tungsten oxide vibrations are in infrared region from 400 to 1453 cm -1 and around 3492 cm -1 , which correspond to tungsten-oxygen (W-O) stretching, bending and lattice modes. The Raman spectrum shows intense peaks at 801, 710, 262 and 61 cm -1 that are typical Raman peaks of crystalline WO 3 (m-phase) that correspond to stretching vibrations of the bridging oxygen, which are assigned to W-O stretching (ν) and W-O bending (δ) modes, respectively. By transmittance measurements obtains that the WO 3 band gap can be varied from 2.92 to 3.13 eV in the investigated annealing temperature range.

  3. Atmospheric properties measurements and data collection from a hot-air balloon

    Science.gov (United States)

    Watson, Steven M.; Olson, N.; Dalley, R. P.; Bone, W. J.; Kroutil, Robert T.; Herr, Kenneth C.; Hall, Jeff L.; Schere, G. J.; Polak, M. L.; Wilkerson, Thomas D.; Bodrero, Dennis M.; Borys, R. O.; Lowenthal, D.

    1995-02-01

    Tethered and free-flying manned hot air balloons have been demonstrated as platforms for various atmospheric measurements and remote sensing tasks. We have been performing experiments in these areas since the winter of 1993. These platforms are extremely inexpensive to operate, do not cause disturbances such as prop wash and high airspeeds, and have substantial payload lifting and altitude capabilities. The equipment operated and tested on the balloons included FTIR spectrometers, multi-spectral imaging spectrometer, PM10 Beta attenuation monitor, mid- and far-infrared cameras, a radiometer, video recording equipment, ozone meter, condensation nuclei counter, aerodynamic particle sizer with associated computer equipment, a tethersonde and a 2.9 kW portable generator providing power to the equipment. Carbon monoxide and ozone concentration data and particle concentrations and size distributions were collected as functions of altitude in a wintertime inversion layer at Logan, Utah and summertime conditions in Salt Lake City, Utah and surrounding areas. Various FTIR spectrometers have been flown to characterize chemical plumes emitted from a simulated industrial stack. We also flew the balloon into diesel and fog oil smokes generated by U.S. Army and U.S. Air Force turbine generators to obtain particle size distributions.

  4. Structural and Optical Properties of Ultra-high Pure Hot Water Processed Ga2O3 Thin Film

    Directory of Open Access Journals (Sweden)

    Subramani SHANMUGAN

    2016-05-01

    Full Text Available Thin film based gas sensor is an advanced application of thin film especially Ga2O3 (GO thin film gas sensor is useful for high temperature gas sensor. The effect of moisture or environment on thin film properties has more influence on gas sensing properties. Radio Frequency sputtered Ga2O3 thin film was synthesized and processed in ultra-high pure hot water at 95 °C for different time durations. The structural properties were verified by the Xray Diffraction technique and the observed spectra revealed the formation of hydroxyl compound of Gallium (Gallium Oxide Dueterate – GOD on the surface of the thin film and evidenced for structural defects as an effect of moisture. Decreased crystallite size and increased dislocation density was showed the crystal defects of prepared film. From the Ultra Violet – Visible spectra, decreased optical transmittance was noticed for various processing time. The formation of needle like GOD was confirmed using Field Emission Secondary Electron Microscope (FESEM images.DOI: http://dx.doi.org/10.5755/j01.ms.22.2.7186

  5. Dry sliding tribological behavior and mechanical properties of Al2024–5 wt.%B4C nanocomposite produced by mechanical milling and hot extrusion

    International Nuclear Information System (INIS)

    Abdollahi, Alireza; Alizadeh, Ali; Baharvandi, Hamid Reza

    2014-01-01

    Highlights: • Nanostructured Al2024 and Al2024–B 4 C nanocomposite prepared via mechanical milling. • The milled powders formed by hot pressing and then exposed to hot extrusion. • Tribological behavior and mechanical properties of samples were investigated. • Al2024–B 4 C nanocomposite showed a better wear resistance and mechanical properties. - Abstract: In this paper, tribological behavior and mechanical properties of nanostructured Al2024 alloy produced by mechanical milling and hot extrusion were investigated before and after adding B 4 C particles. Mechanical milling was used to synthesize the nanostructured Al2024 in attrition mill under argon atmosphere up to 50 h. A similar process was used to produce Al2024–5 wt.%B 4 C composite powder. The milled powders were formed by hot pressing and then were exposed to hot extrusion in 750 °C with extrusion ratio of 10:1. To study the microstructure of milled powders and hot extruded samples, optical microscopy, transmission electron microscopy and scanning electron microscopy (SEM) equipped with an energy dispersive X-ray spectrometer (EDS) were used. The mechanical properties of samples were also compared together using tension, compression and hardness tests. The wear properties of samples were studied using pin-on-disk apparatus under a 20 N load. The results show that mechanical milling decreases the size of aluminum matrix grains to less than 100 nm. The results of mechanical and wear tests also indicate that mechanical milling and adding B 4 C particles increase strength, hardness and wear resistance of Al2024 and decrease its ductility remarkably

  6. Password cracking

    OpenAIRE

    Χριστοφάκης, Μιχαήλ Κ.

    2014-01-01

    Information security is the next big thing in computers society because of the rapidly growing security incidents and the outcomes of those. Hacking and cracking existed even from the start of the eighties decade when there was the first step of the interconnection through the internet between humans. From then and ever after there was a big explosion of such incidents mostly because of the worldwide web which was introduced in the early nineties. Following the huge steps forward of computers...

  7. Crack Propagation by Finite Element Method

    Directory of Open Access Journals (Sweden)

    Luiz Carlos H. Ricardo

    2018-01-01

    Full Text Available Crack propagation simulation began with the development of the finite element method; the analyses were conducted to obtain a basic understanding of the crack growth. Today structural and materials engineers develop structures and materials properties using this technique. The aim of this paper is to verify the effect of different crack propagation rates in determination of crack opening and closing stress of an ASTM specimen under a standard suspension spectrum loading from FDandE SAE Keyhole Specimen Test Load Histories by finite element analysis. To understand the crack propagation processes under variable amplitude loading, retardation effects are observed

  8. Properties enhancement and recoil loop characteristics for hot deformed nanocrystalline NdFeB permanent magnets

    International Nuclear Information System (INIS)

    Liu, Z. W.; Huang, Y. L.; Hu, S. L.; Zhong, X. C.; Yu, H. Y.; Gao, X. X.

    2013-01-01

    Nanocrystalline NdFeB magnets were prepared by spark plasma sintering (SPS) and SPS followed by HD using melt spun ribbons as the starting materials. The microstructure of SPSed and HDed magnets were analyzed. The effects of process including temperature and compression ratio on the microstructure and properties were investigated. High magnetic properties were obtained in anisotropic HDed magnets. The combination of Zn and Dy additions was successfully employed to improve the coercivity and thermal stability of the SPSed magnets. Open recoil loops were found in these magnets with Nd-rich composition and without soft magnetic phase for the first time. The relationship between the recoil loops and microstructure for SPS and HD NdFeB magnets were investigated. The investigations showed that the magnetic properties of SPS+HDed magnets are related to the extent of the aggregation of Nd-rich phase, which was formed during HD due to existence of porosity in SPSed precursor. Large local demagnetization fields induced by the Nd-rich phase aggregation leads to the open loops and significantly reduced the coercivity. By reducing the recoil loop openness, the magnetic properties of HDed NdFeB magnets were successfully improved. (author)

  9. Effects of hot rolled microstructure after twin-roll casting on microstructure, texture and magnetic properties of low silicon non-oriented electrical steel

    International Nuclear Information System (INIS)

    Liu, Hai-Tao; Wang, Yin-Ping; An, Ling-Zi; Wang, Zhao-Jie; Hou, Dao-Yuan; Chen, Jun-Mou; Wang, Guo-Dong

    2016-01-01

    In this work, a 0.71 wt%Si+0.44 wt%Al as-cast strip was produced by novel twin-roll casting. Some as-cast samples were respectively reheated and hot rolled at different temperatures in order to obtain different microstructure prior to cold rolling and annealing. The effects of the hot rolled microstructure on microstructure, texture evolution and magnetic properties were investigated in detail. A coarse deformed microstructure with λ-fiber texture was formed after hot rolling at 850–1050 °C, finally leading to an inhomogeneous recrystallization microstructure with strong λ-fiber, Goss and extremely weak γ-fiber texture. By contrast, a fine transformed microstructure was formed after hot rolling at 1150–1250 °C, finally leading to a fine and homogeneous recrystallization microstructure with stronger α-fiber, γ-fiber and much weaker λ-fiber texture. It should be noted that both the magnetic induction and core loss non-monotonically decreased or increased according to the hot rolling temperature. The unfavorable α-fiber and γ-fiber textures in the annealed sheets were much weaker than those of the conventional products regardless of the hot rolling temperature, thus contributing to a much higher magnetic induction. However, the average grain size in the annealed sheets was much lower than those of the conventional products regardless of the hot rolling temperature, thus leading to a higher core loss except the case of 1050 °C. Hence, it is underscored that better integrated magnetic properties than those of the conventional products can be obtained by optimizing the hot rolled microstructure to produce final desirable recrystallization microstructure and texture. - Highlights: • Non-oriented silicon steel was fabricated using twin-roll casting route. • Microstructure and texture evolution were clarified. • Effects of the hot rolled microstructure were investigated in detail. • Formation mechanism of the recrystallization texture was explored.

  10. Effects of hot rolled microstructure after twin-roll casting on microstructure, texture and magnetic properties of low silicon non-oriented electrical steel

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Hai-Tao, E-mail: liuht@ral.neu.edu.cn; Wang, Yin-Ping; An, Ling-Zi; Wang, Zhao-Jie; Hou, Dao-Yuan; Chen, Jun-Mou; Wang, Guo-Dong

    2016-12-15

    In this work, a 0.71 wt%Si+0.44 wt%Al as-cast strip was produced by novel twin-roll casting. Some as-cast samples were respectively reheated and hot rolled at different temperatures in order to obtain different microstructure prior to cold rolling and annealing. The effects of the hot rolled microstructure on microstructure, texture evolution and magnetic properties were investigated in detail. A coarse deformed microstructure with λ-fiber texture was formed after hot rolling at 850–1050 °C, finally leading to an inhomogeneous recrystallization microstructure with strong λ-fiber, Goss and extremely weak γ-fiber texture. By contrast, a fine transformed microstructure was formed after hot rolling at 1150–1250 °C, finally leading to a fine and homogeneous recrystallization microstructure with stronger α-fiber, γ-fiber and much weaker λ-fiber texture. It should be noted that both the magnetic induction and core loss non-monotonically decreased or increased according to the hot rolling temperature. The unfavorable α-fiber and γ-fiber textures in the annealed sheets were much weaker than those of the conventional products regardless of the hot rolling temperature, thus contributing to a much higher magnetic induction. However, the average grain size in the annealed sheets was much lower than those of the conventional products regardless of the hot rolling temperature, thus leading to a higher core loss except the case of 1050 °C. Hence, it is underscored that better integrated magnetic properties than those of the conventional products can be obtained by optimizing the hot rolled microstructure to produce final desirable recrystallization microstructure and texture. - Highlights: • Non-oriented silicon steel was fabricated using twin-roll casting route. • Microstructure and texture evolution were clarified. • Effects of the hot rolled microstructure were investigated in detail. • Formation mechanism of the recrystallization texture was explored.

  11. Hot Flashes

    Science.gov (United States)

    Hot flashes Overview Hot flashes are sudden feelings of warmth, which are usually most intense over the face, neck and chest. Your skin might redden, as if you're blushing. Hot flashes can also cause sweating, and if you ...

  12. HOT 2015

    DEFF Research Database (Denmark)

    Hannibal, Sara Stefansen

    2016-01-01

    HOT samler og formidler 21 literacykyndiges bud på, hvad der er hot, og hvad der bør være hot inden for literacy – og deres begrundelser for disse bud.......HOT samler og formidler 21 literacykyndiges bud på, hvad der er hot, og hvad der bør være hot inden for literacy – og deres begrundelser for disse bud....

  13. Mechanical properties of hot bituminous mixes manufactured with recycled aggregate of Silestone® waste

    Directory of Open Access Journals (Sweden)

    Rubio, M. C.

    2011-03-01

    Full Text Available This article presents the results of a research project which analyzes the viability of incorporating waste material from decorative quartz solid surfacing in the manufacture of hot bituminous mixes. For this purpose, various bituminous mixes were manufactured with waste aggregate in different percentage. A set of tests were carried out that permitted the characterization of the mechanical behavior of these mixes. The results of these tests were similar to the results obtained when conventional mixes made from virgin quarry aggregate were tested. The results for moisture sensitivity as well as for wheel track rutting on mixes showed the optimal performance of this waste material even under very demanding traffic conditions. Laboratory studies showed that the use of this waste material in the manufacture of bituminous mixes is technically viable and can provide high-quality recycled aggregates at a very low cost, which can be used in the pavement of road.

    Este artículo muestra los resultados de un proyecto de investigación que tiene por objeto analizar la viabilidad de incorporación de residuos procedentes de piedra decorativa en la fabricación de mezclas bituminosas en caliente. Para ello se fabricaron mezclas con áridos reciclados de residuos procedentes de piedra decorativa en distintos porcentajes, realizando un conjunto de ensayos que posibilitaron caracterizar el comportamiento mecánico de dichas mezclas. Los resultados obtenidos fueron similares a los de las mezclas convencionales fabricadas con áridos vírgenes procedentes de cantera. Los valores de resistencia conservada ante la acción del agua y deformación en pista, pusieron de manifiesto la aptitud del residuo incluso ante las condiciones de tráfico más exigentes. Los trabajos realizados en el laboratorio indican que la utilización del residuo en la fabricación de mezclas bituminosas es técnicamente viable, pudiendo obtenerse áridos reciclados de gran calidad y

  14. Hot Surface Ignition

    OpenAIRE

    Tursyn, Yerbatyr; Goyal, Vikrant; Benhidjeb-Carayon, Alicia; Simmons, Richard; Meyer, Scott; Gore, Jay P.

    2015-01-01

    Undesirable hot surface ignition of flammable liquids is one of the hazards in ground and air transportation vehicles, which primarily occurs in the engine compartment. In order to evaluate the safety and sustainability of candidate replacement fuels with respect to hot surface ignition, a baseline low lead fuel (Avgas 100 LL) and four experimental unleaded aviation fuels recommended for reciprocating aviation engines were considered. In addition, hot surface ignition properties of the gas tu...

  15. Universal Shapes formed by Interacting Cracks

    Science.gov (United States)

    Fender, Melissa; Lechenault, Frederic; Daniels, Karen

    2011-03-01

    Brittle failure through multiple cracks occurs in a wide variety of contexts, from microscopic failures in dental enamel and cleaved silicon to geological faults and planetary ice crusts. In each of these situations, with complicated curvature and stress geometries, pairwise interactions between approaching cracks nonetheless produce characteristically curved fracture paths known in the geologic literature as en passant cracks. While the fragmentation of solids via many interacting cracks has seen wide investigation, less attention has been paid to the details of individual crack-crack interactions. We investigate the origins of this widely observed crack pattern using a rectangular elastic plate which is notched on each long side and then subjected to quasistatic uniaxial strain from the short side. The two cracks propagate along approximately straight paths until the pass each other, after which they curve and release a lenticular fragment. We find that, for materials with diverse mechanical properties, the shape of this fragment has an aspect ratio of 2:1, with the length scale set by the initial cracks offset s and the time scale set by the ratio of s to the pulling velocity. The cracks have a universal square root shape, which we understand by using a simple geometric model and the crack-crack interaction.

  16. Cracking up (and down): Linking multi-domain hydraulic properties with multi-scale hydrological processes in shrink-swell soils

    Science.gov (United States)

    Stewart, R. D.; Rupp, D. E.; Abou Najm, M. R.; Selker, J. S.

    2017-12-01

    Shrink-swell soils, often classified as Vertisols or vertic intergrades, are found on every continent except Antarctica and within many agricultural and urban regions. These soils are characterized by cyclical shrinking and swelling, in which bulk density and porosity distributions vary as functions of time and soil moisture. Crack networks that form in these soils act as dominant environmental controls on the movement of water, contaminants, and gases, making it important to develop fundamental understanding and tractable models of their hydrologic characteristics and behaviors. In this study, which took place primarily in the Secano Interior region of South-Central Chile, we quantified soil-water interactions across scales using a diverse and innovative dataset. These measurements were then utilized to develop a set of parsimonious multi-domain models for describing hydraulic properties and hydrological processes in shrink-swell soils. In a series of examples, we show how this model can predict porosity distributions, crack widths, saturated hydraulic conductivities, and surface runoff (i.e., overland flow) thresholds, by capturing the dominant mechanisms by which water moves through and interacts with clayey soils. Altogether, these models successfully link small-scale shrinkage/swelling behaviors with large-scale thresholds, and can be applied to describe important processes such as infiltration, overland flow development, and the preferential flow and transport of fluids and gases.

  17. Mechanical properties and hot-rolled microstructures of a low carbon bainitic steel with Cu-P alloying

    International Nuclear Information System (INIS)

    Cui, W.F.; Zhang, S.X.; Jiang, Y.; Dong, J.; Liu, C.M.

    2011-01-01

    Highlights: → Mechanical properties and microstructures of low carbon bainite steel are examined. → Cu-P alloying promotes strengthening and uniform plastic deformation. → Cu-P alloying delays recovery process during rolling interval. → Lowering rolling temperature is favorable to increasing toughness. - Abstract: A low carbon bainitic steel with Cu-P alloying was developed. The new steel aims to meet the demand of high strength, high toughness and resistance to chloride ion corrosion for the components used in the environment of sea water and oceanic atmosphere. Mechanical properties of the steel were tested and strengthening and toughening mechanisms were analyzed by comparing hot-rolled microstructures of the low carbon bainitic steels with and without Cu-P alloying. The results show that Cu-P alloying provided strong solution strengthening with weak effect on ductility. The toughness loss caused by Cu-P alloying could be balanced by increasing the amount of martensite/remained austenite (M/A island) at lower finishing temperature. The static recovery process during rolling interval was delayed by the interaction of phosphorous, copper atoms with dislocations, which was favorable to the formation of bainitic plates. Super-fine Nb(C, N) particles precipitated on dislocations had coherency with bainite ferrite at 830 deg. C finishing temperature. Raising finishing temperature to 880 deg. C, Nb(C, N) particles were prone to coarsening and losing coherency. It was also found that no accurate lattice match relationship among retained austenite, martensite and bainite in granular bainitic microstructure.

  18. Mechanical properties and hot-rolled microstructures of a low carbon bainitic steel with Cu-P alloying

    Energy Technology Data Exchange (ETDEWEB)

    Cui, W.F., E-mail: wenfangcui@yahoo.com.cn [Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), Northeastern University, Shenyang 110004 (China); Zhang, S.X. [Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), Northeastern University, Shenyang 110004 (China); Technology Center of Laiwu Iron and Steel (Group) Co. Ltd., Laiwu 271104 (China); Jiang, Y. [School of Chemical Engineering, University of Queensland, Brisbane 4072 (Australia); Dong, J. [Technology Center of Laiwu Iron and Steel (Group) Co. Ltd., Laiwu 271104 (China); Liu, C.M. [Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), Northeastern University, Shenyang 110004 (China)

    2011-08-15

    Highlights: {yields} Mechanical properties and microstructures of low carbon bainite steel are examined. {yields} Cu-P alloying promotes strengthening and uniform plastic deformation. {yields} Cu-P alloying delays recovery process during rolling interval. {yields} Lowering rolling temperature is favorable to increasing toughness. - Abstract: A low carbon bainitic steel with Cu-P alloying was developed. The new steel aims to meet the demand of high strength, high toughness and resistance to chloride ion corrosion for the components used in the environment of sea water and oceanic atmosphere. Mechanical properties of the steel were tested and strengthening and toughening mechanisms were analyzed by comparing hot-rolled microstructures of the low carbon bainitic steels with and without Cu-P alloying. The results show that Cu-P alloying provided strong solution strengthening with weak effect on ductility. The toughness loss caused by Cu-P alloying could be balanced by increasing the amount of martensite/remained austenite (M/A island) at lower finishing temperature. The static recovery process during rolling interval was delayed by the interaction of phosphorous, copper atoms with dislocations, which was favorable to the formation of bainitic plates. Super-fine Nb(C, N) particles precipitated on dislocations had coherency with bainite ferrite at 830 deg. C finishing temperature. Raising finishing temperature to 880 deg. C, Nb(C, N) particles were prone to coarsening and losing coherency. It was also found that no accurate lattice match relationship among retained austenite, martensite and bainite in granular bainitic microstructure.

  19. The influence of process parameters and additives on the densification, creep properties and strength of hot pressed silicon nitride

    International Nuclear Information System (INIS)

    Becker, R.

    1979-03-01

    One method of production of Si 3 N 4 parts is the hot pressing of powder compacts. According to the current technological know how, a liquid phase building additive (e.g. MgO) is essential for the complete densification of Si 3 N 4 . In this work it has been shown, how dense Si 3 N 4 may be produced without the conventional additives. The SiO 2 -coating of Si 3 N 4 particles here results in the liquid phase formation. On the basis of the above concept, the effect of MgO, Mg 3 N 2 , Al 2 O 3 and A1N-additions to a pure Si 3 N 4 powder have been studied in detail and the resulting material properties: densification, creep and high temperature strengths have been determined. Based on the results, it may be concluded, that HPSN is a dispersion of crystalline Si 3 N 4 in an amorphous matrix (glass content between 4-10 vol%). Depending on the amount and composition of the boundary phase (silicate glass) widely variing material properties may be obtained. (orig./GSCH) [de

  20. Advances in chemical and physical properties of electric arc furnace carbon steel slag by hot stage processing and mineral mixing.

    Science.gov (United States)

    Liapis, Ioannis; Papayianni, Ioanna

    2015-01-01

    Slags are recognised as a highly efficient, cost effective tool in the metal processing industry, by minimising heat losses, reducing metal oxidation through contact with air, removing metal impurities and protecting refractories and graphite electrodes. When compared to natural aggregates for use in the construction industry, slags have higher specific weight that acts as an economic deterrent. A method of altering the specific weight of EAFC slag by hot stage processing and mineral mixing, during steel production is presented in this article. The method has minimal interference with the production process of steel, even by limited additions of appropriate minerals at high temperatures. Five minerals are examined, namely perlite, ladle furnace slag, bauxite, diatomite and olivine. Measurements of specific weight are accompanied by X-ray diffraction (XRD) and fluorescence (XRF) analysis and scanning electron microscopy spectral images. It is also shown how altering the chemical composition is expected to affect the furnace refractory lining. Additionally, the process has been repeated for the most suitable mix in gas furnace and physical properties (FI, SI, LA, PSV, AAV, volume stability) examined. Alteration of the specific weight can result in tailoring slag properties for specific applications in the construction sector. Copyright © 2014 Elsevier B.V. All rights reserved.

  1. Influence of postharvest hot water treatment on nutritional and functional properties of kumquat (Fortunella japonica Lour. Swingle Cv. Ovale) fruit.

    Science.gov (United States)

    Schirra, Mario; Palma, Amedeo; D'Aquino, Salvatore; Angioni, Alberto; Minello, Elisabeth V; Melis, Marinella; Cabras, Paolo

    2008-01-23

    The present study investigated the influence of a hot water dip (HWD) for 2 min at 50 degrees C, a standard and effective treatment for postharvest decay control of citrus fruit, on the nutritional and health-related properties of kumquats. The results show that most of the parameters examined, including titratable acidity, soluble solids content, maturity index, glucose, fructose, sucrose, ascorbic acid, dehydroascorbic acid, alpha- and gamma-tocopherols, beta-carotene, zeaxantin, rhoifolin, and antioxidant activity, were not significantly affected by treatment. The levels of beta-cryptoxanthin, narirutin, and total flavonoids increased after HWD, whereas lutein and total phenols decreased. The concentration of the essential oil and the relative percentage of the individual components of the essential oil were not affected by HWD except for the minor compound p-menta-1,5-dien-1-ol, which increased after HWD. After storage, lower levels of glucose, total sugars, beta-carotene, beta-cryptoxanthin and lutein were recorded in HWD fruit. A decrease in antioxidant activity and increases in alpha-tocopherol and total vitamin E were found both in control and HWD fruit. The influence of HWD at 50 degrees C for 2 min on individual nutraceuticals and health-related properties was thus generally low and may depend on storage conditions.

  2. Effect of Al-Si Coating on Weld Microstructure and Properties of 22MnB5 Steel Joints for Hot Stamping

    Science.gov (United States)

    Lin, Wenhu; Li, Fang; Wu, Dongsheng; Chen, Xiaoguan; Hua, Xueming; Pan, Hua

    2018-03-01

    22MnB5 hot stamping steels are gradually being used in tailor-welded blank applications. In this experiment, 1-mm-thick Al-Si coated and de-coated 22MnB5 steels were laser-welded and then hot-stamped. The chemical compositions, solidification process, microstructure and mechanical properties were investigated to reveal the effect of Al-Si coating and heat treatment. In the welded condition, the coated joints had an Al content of approximately 2.5 wt.% in the fusion zone and the de-coated joints had 0.5 wt.% Al. The aluminum promoted the δ-ferrite formation as the skeletal structure during solidification. In the high-aluminum weld, the microstructure consisted of martensite and long and band-like δ-ferrite. Meanwhile, the low-aluminum weld was full of lath martensite. After the hot stamping process, the δ-ferrite fraction increased from 10 to 24% in the coated joints and the lath martensite became finer in the de-coated joints. The tensile strengths of the coated joints or de-coated joints were similar to that before hot stamping, but the strength of the coated joints was reduced heavily after hot stamping compared to the de-coated joints and base material. The effect of δ-ferrite on the tensile properties became stronger when the fusion zone was soft and deformed first in the hot-stamped specimens. The coated weld showed a brittle fracture surface with many cleavage planes, and the de-coated weld showed a ductile fracture surface with many dimples in hot-stamped conditions.

  3. Cracks propagation by stress corrosion cracking in conditions of Boiling Water Reactor (BWR)

    International Nuclear Information System (INIS)

    Fuentes C, P.

    2003-01-01

    This work presents the results of the assays carried out in the Laboratory of Hot Cells of the National Institute of Nuclear Research (ININ) to a type test tube Compact Tension (CT), built in steel austenitic stainless type 304L, simulating those conditions those that it operates a Boiling Water Reactor (BWR), at temperature 288 C and pressure of 8 MPa, to determine the speed to which the cracks spread in this material that is of the one that different components of a reactor are made, among those that it highlights the reactor core vessel. The application of the Hydrogen Chemistry of the Water is presented (HWC) that is one alternative to diminish the corrosion effect low stress in the component, this is gets controlling the quantity of oxygen and of hydrogen as well as the conductivity of the water. The rehearsal is made following the principles of the Mechanics of Elastic Lineal Fracture (LEFM) that considers a crack of defined size with little plastic deformation in the tip of this; the measurement of crack advance is continued with the technique of potential drop of direct current of alternating signal, this is contained inside the standard Astm E-647 (Method of Test Standard for the Measurement of Speed of Growth of Crack by fatigue) that is the one that indicates us as carrying out this test. The specifications that should complete the test tubes that are rehearsed as for their dimensions, it forms, finish and determination of mechanical properties (tenacity to the fracture mainly) they are contained inside the norm Astm E-399, the one which it is also based on the principles of the fracture mechanics. The obtained results were part of a database to be compared with those of other rehearsals under different conditions, Normal Chemistry of the Water (NWC) and it dilutes with high content of O 2 ; to determine the conditions that slow more the phenomena of stress corrosion cracking, as well as the effectiveness of the used chemistry and of the method of

  4. Skyrme interaction and the properties of cold and hot neutron matter

    International Nuclear Information System (INIS)

    Mansour, H.M.M.; Hassan, M.Y.M.; Ramadan, S.

    1986-08-01

    The binding energy per particle, effective mass, magnetic susceptibility, etc for neutron matter are calculated using the Skyrme interaction SKII. Relativistic corrections to the non-relativistic Skyrme effective interaction to order 1/C 2 are also used to calculate the corrections for the binding energy of neutron matter. The correction is very small for small values of k h and increases as k n is increased. The thermal properties of neutron matter are calculated also using SKII force. The temperature dependences of the volume and spin pressure are determined. The results obtained show a similar trend as previous theoretical estimates by different methods of calculation. (author)

  5. Inferring strength and deformation properties of hot mix asphalt layers from the GPR signal: recent advances

    Science.gov (United States)

    Tosti, Fabio; Benedetto, Andrea; Bianchini Ciampoli, Luca; Adabi, Saba; Pajewski, Lara

    2015-04-01

    , of both the different strength provision of each layer composing the hot mix asphalt pavement structure, and of the attenuation occurring to electromagnetic waves during their in-depth propagation. Promising results are achieved by matching modelled and measured elastic modulus data. This continuous statistically-based model enables to consider the whole set of information related to each single depth, in order to provide a more comprehensive prediction of the strength and deformation behavior of such a complex multi-layered medium. Amongst some further developments to be tackled in the near future, a model improvement could be reached through laboratory activities under controlled conditions and by adopting several frequency bandwidths suited for purposes. In addition, the perspective to compare electromagnetic data with mechanical measurements retrieved continuously, i.e., by means of specifically equipped lorries, could pave the way to considerable enhancements in this field of research. Acknowledgements - This work has benefited from networking activities carried out within the EU funded COST Action TU1208 "Civil Engineering Applications of Ground Penetrating Radar".

  6. Prediction of long time creep rupture properties of welded joints using the results of short duration creep crack incubation tests

    Energy Technology Data Exchange (ETDEWEB)

    Hosseini, E.

    2013-07-01

    This dissertation submitted to the Swiss Federal Institute of Technology ETH in Zurich examines the applicability of the LICON methodology for the prediction of long-time creep rupture strength of a dissimilar metal weld. The LICON methodology is an approach for predicting the lifetime of materials under creep loading conditions. It predicts long-time uniaxial creep strength using the results from several short duration creep crack incubation tests in conjunction with the outcome of a mechanical analysis on the test-piece. This study has re-examined the previous application of the LICON methodology for 9%Cr and 1CrMoV steels. It has shown that application of the original Lion method (based on reference stress solutions) for certain materials is not appropriate. This study therefore proposes a new development for the Lion approach which uses finite-element analysis to account for the generated multiaxial stress states within welded uniaxial test-pieces.

  7. Prediction of long time creep rupture properties of welded joints using the results of short duration creep crack incubation tests

    International Nuclear Information System (INIS)

    Hosseini, E.

    2013-01-01

    This dissertation submitted to the Swiss Federal Institute of Technology ETH in Zurich examines the applicability of the LICON methodology for the prediction of long-time creep rupture strength of a dissimilar metal weld. The LICON methodology is an approach for predicting the lifetime of materials under creep loading conditions. It predicts long-time uniaxial creep strength using the results from several short duration creep crack incubation tests in conjunction with the outcome of a mechanical analysis on the test-piece. This study has re-examined the previous application of the LICON methodology for 9%Cr and 1CrMoV steels. It has shown that application of the original Lion method (based on reference stress solutions) for certain materials is not appropriate. This study therefore proposes a new development for the Lion approach which uses finite-element analysis to account for the generated multiaxial stress states within welded uniaxial test-pieces

  8. Mechanical properties and aesthetics of FRP orthodontic wire fabricated by hot drawing.

    Science.gov (United States)

    Imai, T; Watari, F; Yamagata, S; Kobayashi, M; Nagayama, K; Toyoizumi, Y; Nakamura, S

    1998-12-01

    The FRP wires 0.5 mm in diameter with a multiple fiber structure were fabricated by drawing the fiber polymer complex at 250 degrees C for an esthetic, transparent orthodontic wire. Biocompatible CaO-P2O5-SiO2-Al2O3 (CPSA) glass fibers of 8-20 microm in diameter were oriented unidirectionally in the longitudinal direction in PMMA matrix. The mechanical properties were investigated by 3-point flexural test. The FRP wire showed sufficient strength and a very good elastic recovery after deformation. Young's modulus and the flexural load at deflection 1 mm were nearly independent of the fiber diameter and linearly increased with the fiber fraction. The dependence on fiber fraction obeys well the rule of mixture. This FRP wire could cover the range of strength corresponding to the conventional metal orthodontic wires from Ni-Ti used in the initial stage of orthodontic treatments to Co-Cr used in the final stage by changing the volume ratio of glass fibers with the same external diameter. The estheticity in external appearance was excellent. Thus the new FRP wire can satisfy both mechanical properties necessary for an orthodontic wire and enough estheticity, which was not possible for the conventional metal wire.

  9. Cracking hydrocarbons

    Energy Technology Data Exchange (ETDEWEB)

    Forwood, G F; Lane, M; Taplay, J G

    1921-10-07

    In cracking and hydrogenating hydrocarbon oils by passing their vapors together with steam over heated carbon derived from shale, wood, peat or other vegetable or animal matter, the gases from the condenser are freed from sulfuretted hydrogen, and preferably also from carbon dioxide, and passed together with oil vapors and steam through the retort. Carbon dioxide may be removed by passage through slaked lime, and sulfuretted hydrogen by means of hydrated oxide of iron. Vapors from high-boiling oils and those from low-boiling oils are passed alternately through the retort, so that carbon deposited from the high-boiling oils is used up during treatment of low-boiling oils.

  10. Advances in chemical and physical properties of electric arc furnace carbon steel slag by hot stage processing and mineral mixing

    International Nuclear Information System (INIS)

    Liapis, Ioannis; Papayianni, Ioanna

    2015-01-01

    Highlights: • Addition of 10% perlite decreases specific weight of the slag by approx. 7.5%. • Slag-crucible interaction and thin coating layer result in variations in XRF. • XRD shows high glass content and smaller crystalline sizes due to rapid cooling. • SEM shows higher homogeneity and lower crystallisation for SiO 2 /CaO-rich samples. • Physical properties (LA, PSV, AAV) of modified slag show limited deterioration. - Abstract: Slags are recognised as a highly efficient, cost effective tool in the metal processing industry, by minimising heat losses, reducing metal oxidation through contact with air, removing metal impurities and protecting refractories and graphite electrodes. When compared to natural aggregates for use in the construction industry, slags have higher specific weight that acts as an economic deterrent. A method of altering the specific weight of EAFC slag by hot stage processing and mineral mixing, during steel production is presented in this article. The method has minimal interference with the production process of steel, even by limited additions of appropriate minerals at high temperatures. Five minerals are examined, namely perlite, ladle furnace slag, bauxite, diatomite and olivine. Measurements of specific weight are accompanied by X-ray diffraction (XRD) and fluorescence (XRF) analysis and scanning electron microscopy spectral images. It is also shown how altering the chemical composition is expected to affect the furnace refractory lining. Additionally, the process has been repeated for the most suitable mix in gas furnace and physical properties (FI, SI, LA, PSV, AAV, volume stability) examined. Alteration of the specific weight can result in tailoring slag properties for specific applications in the construction sector

  11. Advances in chemical and physical properties of electric arc furnace carbon steel slag by hot stage processing and mineral mixing

    Energy Technology Data Exchange (ETDEWEB)

    Liapis, Ioannis, E-mail: iliapis@sidenor.vionet.gr [AEIFOROS SA, 12th km Thessaloniki-Veroia Rd, PO Box 59, 57008 Ionia, Thessaloniki (Greece); Papayianni, Ioanna [Laboratory of Building Materials, Department of Civil Engineering, Aristotle University of Thessaloniki, 54124 Thessaloniki (Greece)

    2015-02-11

    Highlights: • Addition of 10% perlite decreases specific weight of the slag by approx. 7.5%. • Slag-crucible interaction and thin coating layer result in variations in XRF. • XRD shows high glass content and smaller crystalline sizes due to rapid cooling. • SEM shows higher homogeneity and lower crystallisation for SiO{sub 2}/CaO-rich samples. • Physical properties (LA, PSV, AAV) of modified slag show limited deterioration. - Abstract: Slags are recognised as a highly efficient, cost effective tool in the metal processing industry, by minimising heat losses, reducing metal oxidation through contact with air, removing metal impurities and protecting refractories and graphite electrodes. When compared to natural aggregates for use in the construction industry, slags have higher specific weight that acts as an economic deterrent. A method of altering the specific weight of EAFC slag by hot stage processing and mineral mixing, during steel production is presented in this article. The method has minimal interference with the production process of steel, even by limited additions of appropriate minerals at high temperatures. Five minerals are examined, namely perlite, ladle furnace slag, bauxite, diatomite and olivine. Measurements of specific weight are accompanied by X-ray diffraction (XRD) and fluorescence (XRF) analysis and scanning electron microscopy spectral images. It is also shown how altering the chemical composition is expected to affect the furnace refractory lining. Additionally, the process has been repeated for the most suitable mix in gas furnace and physical properties (FI, SI, LA, PSV, AAV, volume stability) examined. Alteration of the specific weight can result in tailoring slag properties for specific applications in the construction sector.

  12. Study of the mechanical properties of stainless steel 316LN prepared by hot isostatic compression. Influence of preparation parameters

    International Nuclear Information System (INIS)

    Couturier, Raphael

    1999-01-01

    This research thesis has been performed within an R and D programme which aimed at optimising and certifying the HIP process (hot isostatic pressing) from a technological as well as metallurgical point of view. The objective has been to improve dimensional reproducibility of fabricated parts, and metallurgical properties of the dense material. Reference parts are those belonging to PWR primary circuit, and are made in cast austenitic-ferritic steel. Thus, the objective has been to show that these parts can be beneficially fabricated by powder metallurgy in austenitic grade. A mock part (a primary circuit pump wheel at the 1/2 scale) has first been fabricated by HIP, and a more complex shape generator has been designed. The author reports the determination of microstructure and mechanical characteristics of the austenitic 316LN steel produced by HIP and used to fabricate mock parts and demonstrator parts, the study of the relationship between dense material properties and fabrication parameters (temperature, pressure, consolidation time), and the analysis of the consequences of an elaboration by HIP on the 316LN steel with comparison with forged parts. After a presentation of the Powder Metallurgy elaboration technique, the author reports a bibliographical study on the precipitation at Prior Particle Boundaries (PPB), reports the study of microstructure and mechanical properties of the HIPed 316LN, and discusses the possibility of a decrease of precipitation at PPBs by adjusting powder degassing or a granulometric sorting. The last part reports the extension of the study of steel coherence to a temperature range which encompasses the primary circuit operation temperature (350 C). Resilience tests are performed as well as mechanical tests on notched axisymmetric samples. A finite element calculation of these samples allows the validation of the use of a Thomson-type model to describe the emergence of defects which are typical of a steel elaborated by powder

  13. Impact properties of reduced activation ferritic/martensitic steel, F82H jointed by hot isostatic pressing

    Energy Technology Data Exchange (ETDEWEB)

    Ogiwara, H.; Tanigawa, H. [Japan Atomic Energy Agency, Tokai-mura, Naga-gun, Ibaraki-ken (Japan); Hirose, T. [Blanket Engineering Group, Japan Atomic Energy Agency, Naka, Ibaraki (Japan); Enoeda, M. [Naka Fusion Research Establishment, J.A.E.R.I., Japan Atomic Energy Research Institute, Ibaraki-ken (Japan); Kohyama, A. [Kyoto Univ., lnstitute of Advanced Energy (Japan)

    2007-07-01

    Full text of publication follows: Reduced-activation ferritic/martensitic steels are the leading candidate structural material for the blanket system of fusion reactors. The important issue at the current stage is the finalization of a detailed manufacturing specification for ITER test blanket module. Hot isostatic pressing (HIP) process is one of the most important methods to fabricate the first wall with cooling channels. The objective of this paper is to optimize HIP condition to obtain the excellent joints mechanical properties. The materials used were F82H steels. The joint was produced by solid state HIP method. Before HIP treatments, specimens were heated in vacuum condition to out-gas. This treatment was conducted to decrease oxidation on the surfaces. HIP treatments were carried out for 2 h at 1100 deg. C - 140 MPa. The specimens were normalized at 960 deg. C for 0.5 h and tempered at 750 deg. C for 1.5 h. The bonding interface was characterized by scanning electron microscopy. Charpy impact tests and tensile tests were conducted to evaluate the mechanical properties of the HIP joint. Impact tests revealed that there were no significant differences in the ductile-brittle transition temperatures of HIP jointed specimens and base metal specimens, but the upper-shelf energy (USE) of the HIP joint specimens at room temperature was only about 10% of that of the base metal specimens. SEM observations of the fracture surface of HIP joint specimens revealed that a large number of oxides were formed on the HIP joint. This result indicates that oxides formed on the HIP joint are the dominant factor of the impact properties. Based on these results, the pre-HIP treatment conditions had been optimized to reduce the number of oxides, and USE of HIP joint specimens increased to about 50% of that of the base metal. The detailed analyses on the HIP joint microstructure will be reported. (authors)

  14. Influence of purity level on the mechanical properties of hot isostatically pressed beryllium

    International Nuclear Information System (INIS)

    Odegard, B.C. Jr.

    1979-09-01

    The procurement of a quantity of ultra-pure beryllium powder combined with special handling from powder to billet form resulted in the fabrication of high purity beryllium. The mechanical properties of these billets were contrasted to those of commercial grade billets to determine the influence of impurities and powder processing. The tensile test results show that the strength values are primarily dependent on the grain size in a behavior predictable by the Hall-Petch relationship. Only a fraction of the strength differential can be attributed to metallic impurities in solution. The grain size is controlled by the powder size distribution. The ductility is dominated by both grain size and oxide content. The fine grained, low oxide billets exhibited the highest ductilities. There is evidence to suggest that oxide distribution has a large influence on the ductility. The fracture toughness was highest for the high purity beryllium billets

  15. Effect of hot band grain size on development of textures and magnetic properties in 2.0% Si non-oriented electrical steel sheet

    Energy Technology Data Exchange (ETDEWEB)

    Lee, K.M. [Department of Materials Science and Engineering, Korea University, 5-1, Anam-dong, Sungbuk-Gu, Seoul 136-701 (Korea, Republic of); Huh, M.Y., E-mail: myhuh@korea.ac.kr [Department of Materials Science and Engineering, Korea University, 5-1, Anam-dong, Sungbuk-Gu, Seoul 136-701 (Korea, Republic of); Lee, H.J.; Park, J.T.; Kim, J.S. [Electrical Steel Sheet Research Group, Technical Research Laboratories, POSCO, Goedong-dong, Pohang (Korea, Republic of); Shin, E.J. [Korea Atomic Energy Research Institute, Neutron Science Division, Daejeon 305-353 (Korea, Republic of); Engler, O. [Hydro Aluminium Rolled Products GmbH, Research and Development Bonn, P.O. Box 2468, D-53014 Bonn (Germany)

    2015-12-15

    The effect of hot band grain size on the development of crystallographic texture and magnetic properties in non-oriented electrical steel sheet was studied. After cold rolling the samples with different initial grain sizes displayed different microstructures and micro-textures but nearly identical macro-textures. The homogeneous recrystallized microstructure and micro-texture in the sample having small grains caused normal continuous grain growth. The quite irregular microstructure and micro-texture in the recrystallized sample with large initial grain size provided a preferential growth of grains in 〈001〉//ND and 〈113〉//ND which were beneficial for developing superior magnetic properties. - Highlights: • We produced hot bands of electrical steel with different grain size but same texture. • Hot band grain size strongly affected cold rolling and subsequent annealing textures. • Homogeneous recrystallized microstructure caused normal continuous grain growth. • Irregular recrystallized microstructure led to selective growth of <001>//ND grains. • Hot band with large grains was beneficial for superior magnetic properties.

  16. Fatigue crack growth and fracture behavior of bainitic rail steels.

    Science.gov (United States)

    2011-09-01

    "The microstructuremechanical properties relationships, fracture toughness, fatigue crack growth and fracture surface morphology of J6 bainitic, manganese, and pearlitic rail steels were studied. Microstructuremechanical properties correlation ...

  17. Shapes formed by interacting cracks

    Science.gov (United States)

    Daniels, Karen

    2012-02-01

    Brittle failure through multiple cracks occurs in a wide variety of contexts, from microscopic failures in dental enamel and cleaved silicon to geological faults and planetary ice crusts. In each of these situations, with complicated stress geometries and different microscopic mechanisms, pairwise interactions between approaching cracks nonetheless produce characteristically curved fracture paths. We investigate the origins of this widely observed ``en passant'' crack pattern by fracturing a rectangular slab which is notched on each long side and subjected to quasi-static uniaxial strain from the short side. The two cracks propagate along approximately straight paths until they pass each other, after which they curve and release a lens-shaped fragment. We find that, for materials with diverse mechanical properties, each curve has an approximately square-root shape, and that the length of each fragment is twice its width. We are able to explain the origins of this universal shape with a simple geometrical model.

  18. Crack propagation along polymer/non-polymer interfaces

    NARCIS (Netherlands)

    Vellinga, Willem-Pier; Fedorov, Alexander; De Hosson, Jeff T.

    2007-01-01

    Mechanisms of the propagation of crack fronts along interfaces between a glassy polymer and metal or glass are discussed. Specifically, the systems studied are Poly-Ethylene Terephthalate (PETG) spin-coated on A1, PETG-glass and PETG hot-pressed on Cr-sputtered glass. Cracks studied propagate in an

  19. Mechanical properties of hot mix asphalt made with recycled aggregates from reclaimed construction and demolition debris

    Directory of Open Access Journals (Sweden)

    Taibo, J.

    2007-03-01

    Full Text Available The mix design for asphalt mixtures containing recycled aggregates from construction and demolition debris was evaluated. The tests conducted to characterize the mechanical behaviour of these mixtures showed that the mechanical properties of mixtures with recycled and virgin aggregate are similar. The asphalt mixtures containing recycled aggregate proved to have lower resistance to water action. Nonetheless, recycled aggregate was found to be potentially usable in asphalt mixtures if higher quality materials are selected and such low resistance is corrected. This will call for expanding upon the preliminary work described in the present article.En este trabajo se dosificaron mezclas bituminosas fabricadas con áridos reciclados de residuos de construcción y demolición. Se realizaron una serie de ensayos que permitieron caracterizar el comportamiento mecánico de estas mezclas. Los parámetros mecánicos de las mezclas con áridos reciclados son similares a los de las mezclas fabricadas únicamente con áridos naturales de cantera. Sin embargo, las mezclas bituminosas con áridos reciclados tuvieron un mal comportamiento frente a la disminución de la resistencia por pérdida de cohesión por la acción del agua. No obstante, mediante la selección de materiales de mejor calidad y corrección de este mal comportamiento, existen posibilidades de utilizar áridos reciclados en mezclas bituminosas. Para ello será necesario ampliar la primera aproximación realizada en este artículo.

  20. Effects of LaB{sub 6} additions on the microstructure and mechanical properties of a sintered and hot worked P/M Ti alloy

    Energy Technology Data Exchange (ETDEWEB)

    Lou, Jia; Gabbitas, Brian, E-mail: briang@waikato.ac.nz; Yang, Fei; Raynova, Stella; Lu, Huiyang

    2016-07-25

    A trace amount of LaB{sub 6} powder was added to P/M Ti and Ti–6Al–4V alloy to improve mechanical properties and refine the microstructure. After sintering, TiB whiskers and La{sub 2}O{sub 3} dispersoids had formed in the microstructure. In a CP Ti alloy, the generation of secondary phases leads to a much refined microstructure, but the alignment of TiB whiskers led to a variation in mechanical properties. Open die forging (ODF) or powder compact extrusion (PCE) was carried out on sintered Ti–6Al–4V alloy to further improve the mechanical properties. This caused severe deformation and re-alignment of the TiB whiskers. Comparing the properties of hot worked Ti–6Al–4V alloy and Ti–6Al–4V alloy with boron additions, an addition of LaB{sub 6} leads to slightly lower strength but gives significant better ductility. - Highlights: • LaB{sub 6} powder was added to sintered and hot worked Ti and Ti–6Al–4V alloy. • TiB whiskers and La{sub 2}O{sub 3} dispersoids formed in the microstructure. • Different alignments of TiB{sub w} led to a variation in mechanical properties. • Hot working caused severe deformation and re-alignment of TiB{sub w}. • An addition of LaB{sub 6} is better than pure boron additions.

  1. Effects of hot isostatic pressing on the elastic modulus and tensile properties of 316L parts made by powder bed laser fusion

    Energy Technology Data Exchange (ETDEWEB)

    Lavery, N.P., E-mail: N.P.Lavery@swansea.ac.uk [Materials Research Centre, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Zienkiewicz Centre for Computational Engineering, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Cherry, J.; Mehmood, S. [Materials Research Centre, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Zienkiewicz Centre for Computational Engineering, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Davies, H. [Materials Research Centre, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Girling, B.; Sackett, E. [Materials Research Centre, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Zienkiewicz Centre for Computational Engineering, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Brown, S.G.R. [Materials Research Centre, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom); Sienz, J. [Zienkiewicz Centre for Computational Engineering, College of Engineering, Swansea University Bay Campus, Fabian Way, Swansea SA1 8EP (United Kingdom)

    2017-05-02

    The microstructure and mechanical properties of 316L steel have been examined for parts built by a powder bed laser fusion process, which uses a laser to melt and build parts additively on a layer by layer basis. Relative density and porosity determined using various experimental techniques were correlated against laser energy density. Based on porosity sizes, morphology and distributions, the porosity was seen to transition between an irregular, highly directional porosity at the low laser energy density and a smaller, more rounded and randomly distributed porosity at higher laser energy density, thought to be caused by keyhole melting. In both cases, the porosity was reduced by hot isostatic pressing (HIP). High throughput ultrasound based measurements were used to calculate elasticity properties and show that the lower porosities from builds with higher energy densities have higher elasticity moduli in accordance with empirical relationships, and hot isostatic pressing improves the elasticity properties to levels associated with wrought/rolled 316L. However, even with hot isostatic pressing the best properties were obtained from samples with the lowest porosity in the as-built condition. A finite element stress analysis based on the porosity microstructures was undertaken, to understand the effect of pore size distributions and morphology on the Young's modulus. Over 1–5% porosity range angular porosity was found to reduce the Young's modulus by 5% more than rounded porosity. Experimentally measured Young's moduli for samples treated by HIP were closer to the rounded trends than the as-built samples, which were closer to angular trends. Tensile tests on specimens produced at optimised machine parameters displayed a high degree of anisotropy in the build direction and test variability for as-built parts, especially between vertical and horizontal build directions. The as-built properties were generally found to have a higher yield stress, but

  2. Effects of hot isostatic pressing on the elastic modulus and tensile properties of 316L parts made by powder bed laser fusion

    International Nuclear Information System (INIS)

    Lavery, N.P.; Cherry, J.; Mehmood, S.; Davies, H.; Girling, B.; Sackett, E.; Brown, S.G.R.; Sienz, J.

    2017-01-01

    The microstructure and mechanical properties of 316L steel have been examined for parts built by a powder bed laser fusion process, which uses a laser to melt and build parts additively on a layer by layer basis. Relative density and porosity determined using various experimental techniques were correlated against laser energy density. Based on porosity sizes, morphology and distributions, the porosity was seen to transition between an irregular, highly directional porosity at the low laser energy density and a smaller, more rounded and randomly distributed porosity at higher laser energy density, thought to be caused by keyhole melting. In both cases, the porosity was reduced by hot isostatic pressing (HIP). High throughput ultrasound based measurements were used to calculate elasticity properties and show that the lower porosities from builds with higher energy densities have higher elasticity moduli in accordance with empirical relationships, and hot isostatic pressing improves the elasticity properties to levels associated with wrought/rolled 316L. However, even with hot isostatic pressing the best properties were obtained from samples with the lowest porosity in the as-built condition. A finite element stress analysis based on the porosity microstructures was undertaken, to understand the effect of pore size distributions and morphology on the Young's modulus. Over 1–5% porosity range angular porosity was found to reduce the Young's modulus by 5% more than rounded porosity. Experimentally measured Young's moduli for samples treated by HIP were closer to the rounded trends than the as-built samples, which were closer to angular trends. Tensile tests on specimens produced at optimised machine parameters displayed a high degree of anisotropy in the build direction and test variability for as-built parts, especially between vertical and horizontal build directions. The as-built properties were generally found to have a higher yield stress, but lower upper

  3. Structural properties of WO{sub 3} dependent of the annealing temperature deposited by hot-filament metal oxide deposition

    Energy Technology Data Exchange (ETDEWEB)

    Flores M, J. E. [Benemerita Universidad Autonoma de Puebla, Facultad de Ciencias de la Electronica, Av. San Claudio y 18 Sur, Ciudad Universitaria, Col. Jardines de San Manuel, 72570 Puebla (Mexico); Diaz R, J. [IPN, Centro de Investigacion en Biotecnologia Aplicada, Ex-Hacienda de San Molino Km 1.5 Tepetitla, 90700 Tlaxcala (Mexico); Balderas L, J. A., E-mail: eflores@ece.buap.mx [IPN, Unidad Profesional Interdisciplinaria de Biotecnologia, Av. Acueducto s/n, Col. Barrio la Laguna, 07340 Mexico D. F. (Mexico)

    2012-07-01

    In this work presents a study of the effect of the annealing temperature on structural and optical properties of WO{sub 3} that has been grown by hot-filament metal oxide deposition. The chemical stoichiometry was determined by X-ray photoelectron spectroscopy. By X-ray diffraction obtained that the as-deposited WO{sub 3} films present mainly monoclinic crystalline phase. WO{sub 3} optical band gap energy can be varied from 2.92 to 3.15 eV obtained by transmittance measurements by annealing WO{sub 3} from 100 to 500 C. The Raman spectrum of the as-deposited WO{sub 3} film shows four intense peaks that are typical Raman peaks of crystalline WO{sub 3} (m-phase) that corresponds to the stretching vibrations of the bridging oxygen that are assigned to W-O stretching ({upsilon}) and W-O bending ({delta}) modes, respectively, which enhanced and increased their intensity with the annealing temperature. (Author)

  4. Effect of Annealing Temperature on Microstructure and Mechanical Properties of Hot-Dip Galvanizing DP600 Steel

    Science.gov (United States)

    Hai-yan, Sun; Zhi-li, Liu; Yang, Xu; Jian-qiang, Shi; Lian-xuan, Wang

    Hot-dip galvanizing dual phase steel DP600 steel grade with low Si was produced by steel plant and experiments by simulating galvanizing thermal history. The microstructure was observed and analyzed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The effect of different annealing temperatures on the microstructure and mechanical properties of dual-phase steel was also discussed. The experimental results show that the dual-phase steel possesses excellent strength and elongation that match EN10346 600MPa standards. The microstructure is ferrite and martensite. TEM micrograph shows that white ferrite with black martensite islands inlay with a diameter of around 1um and the content of 14 18%. The volume will expand and phase changing take the form of shear transformation when ferrite converted to martensite. So there are high density dislocations in ferrite crystalline grain near martensite. The martensite content growing will be obvious along with annealing temperature going up. But the tendency will be weak when temperature high.

  5. Thermoelectric Properties of Cu-doped Bi2-xSbxTe3 Prepared by Encapsulated Melting and Hot Pressing

    Science.gov (United States)

    Jung, Woo-Jin; Kim, Il-Ho

    2018-03-01

    P-type Bi2-xSbxTe3:Cum (x = 1.5-1.7 and m = 0.002-0.003) solid solutions were synthesized using encapsulated melting and were consolidated using hot pressing. The effects of Sb substitution and Cu doping on the charge transport and thermoelectric properties were examined. The lattice constants decreased with increasing Sb and Cu contents. As the amount of Sb substitution and Cu doping was increased, the electrical conductivity increased, and the Seebeck coefficient decreased owing to the increase in the carrier concentration. All specimens exhibited degenerate semiconductor characteristics and positive Hall and Seebeck coefficients, indicating p-type conduction. The increased Sb substitution caused a shift in the onset temperature of the intrinsic transition and bipolar conduction to higher temperatures. The electronic thermal conductivity increased with increasing Sb and Cu contents owing to the increase in the carrier concentration, while the lattice thermal conductivity slightly decreased due to alloy scattering. A maximum figure of merit, ZTmax = 1.25, was achieved at 373 K for Bi0.4Sb1.6Te3:Cu0.003.

  6. Physical and mechanical properties of parallel strand lumber made from hot pre-pressed long strand oil palm trunk waste

    Science.gov (United States)

    Fridiyanti, Inayah; Massijaya, M. Y.

    2018-03-01

    This research was focused on the utilization of oil palm trunk waste as a Parallel Strand Lumber (PSL) raw material. This research aimed to analyze the effect of adhesive types and glue spreads to the physical and mechanical properties of PSL. The adhesive types used were isocyanate and urea formaldehyde adhesives. The glue spreads used were 150 g/m2 and 300 g/m2. The research results showed that the moisture content of PSL ranged from 9.30% to 11.80%. The PSL density ranged from 0.64 to 0.78 g/cm3. The volume shrinkage ranged from 5.69 to 7.17%. Modulus of Elasticity (MOE) parallel to the grain and edge side ranged from 51.6 × 103 to 98.3 × 103 kg/cm2, and 62.1 × 103 to 99.9 × 103 kg/cm2, respectively. The Modulus of Rupture (MOR) parallel to the grain and edge side ranged from 269 to 724 kg/cm2 and 342 to 728 kg/cm2, respectively. The PSL hardness perpendicular to the grain, parallel to the grain and the edge side ranged from 135 to 300 kg/cm2, 87 to 321 kg/cm2, and 128 to 251 kg/cm2, respectively. The compressive strength ranged from 181 to 231 kg/cm2. The best adhesive and glue spreads of PSL was isocyanate with glue spread 300 g/m2. PSL made from hot pre-pressed long strand of oil palm trunk waste bonded by isocyanate fulfill JAS 1152: 2007. However, those of bonded by urea formaldehyde failed to fulfill the standard. The physical and mechanical properties of PSL made from oil palm trunk were better compared to those of solid oil palm trunk.

  7. HotRegion: a database of predicted hot spot clusters.

    Science.gov (United States)

    Cukuroglu, Engin; Gursoy, Attila; Keskin, Ozlem

    2012-01-01

    Hot spots are energetically important residues at protein interfaces and they are not randomly distributed across the interface but rather clustered. These clustered hot spots form hot regions. Hot regions are important for the stability of protein complexes, as well as providing specificity to binding sites. We propose a database called HotRegion, which provides the hot region information of the interfaces by using predicted hot spot residues, and structural properties of these interface residues such as pair potentials of interface residues, accessible surface area (ASA) and relative ASA values of interface residues of both monomer and complex forms of proteins. Also, the 3D visualization of the interface and interactions among hot spot residues are provided. HotRegion is accessible at http://prism.ccbb.ku.edu.tr/hotregion.

  8. Structure and magnetic properties of hot deformed Nd2Fe14B magnets doped with DyHx nanoparticles

    Science.gov (United States)

    Wang, C. G.; Yue, M.; Zhang, D. T.; Liu, W. Q.; Zhang, J. X.

    2016-04-01

    Commercial NdFeB powders mixed with DyHx nanoparticles are hot pressed and hot deformed into anisotropic magnets by Spark Plasma Sintering (SPS). The hot deformed magnet exhibits strong c-axis crystallographic texture. The coercivity of the magnet doped with 1.0 wt% DyHx is increased by 66.7%, compared with the magnet without DyHx, while the remanence decreases only by 3%. TEM observation shows that there exists a continuous (Nd,Dy)2Fe14B layer between Nd-rich phase and NdFeB main phase.

  9. Study of stress corrosion cracking initiation of high alloy materials

    Energy Technology Data Exchange (ETDEWEB)

    Blahetova, Marie; Cihal, Vladimir; Lasek, Stanislav [Department of Materials Engineering, VSB - Technical University of Ostrava, tr. 17. listopadu 15, 708 33 Ostrava - Poruba (Czech Republic)

    2004-07-01

    The stainless steels and related alloys with sufficient resistance to a general corrosion can be susceptible to a localized corrosion (pitting, cracking, intergranular corrosion) in certain environment under specific conditions. The Drop Evaporation Test (DET) was developed for study of stainless materials resistance to stress corrosion cracking (SCC) at elevated temperatures 100 - 300 deg. C under constant external load using a chloride containing water solution. In the contribution the initiation and propagation of short cracks as well as pits were observed during the test. The crack initiation and/or propagation can be influenced by the cyclic thermal stresses, when the diluted water solution drops cool down the hot sample. The coordinates measurement of microscopic pits and sharp corrosion crack tips by the travelling microscope method allowed to derive the crack growth lengths and rates of short cracks. (authors)

  10. Study of stress corrosion cracking initiation of high alloy materials

    International Nuclear Information System (INIS)

    Blahetova, Marie; Cihal, Vladimir; Lasek, Stanislav

    2004-01-01

    The stainless steels and related alloys with sufficient resistance to a general corrosion can be susceptible to a localized corrosion (pitting, cracking, intergranular corrosion) in certain environment under specific conditions. The Drop Evaporation Test (DET) was developed for study of stainless materials resistance to stress corrosion cracking (SCC) at elevated temperatures 100 - 300 deg. C under constant external load using a chloride containing water solution. In the contribution the initiation and propagation of short cracks as well as pits were observed during the test. The crack initiation and/or propagation can be influenced by the cyclic thermal stresses, when the diluted water solution drops cool down the hot sample. The coordinates measurement of microscopic pits and sharp corrosion crack tips by the travelling microscope method allowed to derive the crack growth lengths and rates of short cracks. (authors)

  11. Influences of hot-isostatic-pressing temperature on microstructure, tensile properties and tensile fracture mode of Inconel 718 powder compact

    International Nuclear Information System (INIS)

    Chang, Litao; Sun, Wenru; Cui, Yuyou; Yang, Rui

    2014-01-01

    Inconel 718 powders have been hot-isostatic-pressed (HIPed) at representative temperatures to investigate the variations in microstructure, tensile properties and tensile fracture mode of the powder compact. Microstructure of the powder compacts were characterized by optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and so on. The results showed that the interdendritic precipitates inherited from the powders were partially retained in the powder compacts when the powders were HIPed at or below 1210 °C but were eliminated when HIPed at and above 1260 °C. The grain size uniformity of the powder compacts first increases and then decreases with increasing HIPing temperature. Prior particle boundaries (PPBs) were observed in the powder compacts HIPed at and below 1260 °C but was eliminated when HIPed at 1275 °C. The PPBs were decorated with carbide particles, the amount of the carbide particles at the PPBs decreases with increasing HIPing temperature. Most of the PPBs were pinned by the carbide particles in the compacts HIPed at 1140 °C. When the HIPing temperature was increased to 1210 °C and 1260 °C, a large number of PPBs de-pinned and moved beyond the pinning carbide particles, leading to grain growth and leaving carbide particles at the site of the original PPBs within the new grains. With increasing HIPing temperature, the 0.2% yield strength of the powder compacts at 650 °C decreases, the tensile elongation increases, and the tensile fracture mode changed from inter-particle dominant fracture to fully dimple ductile fracture

  12. Influences of hot-isostatic-pressing temperature on microstructure, tensile properties and tensile fracture mode of Inconel 718 powder compact

    Energy Technology Data Exchange (ETDEWEB)

    Chang, Litao [Institute of Metal Research, Chinese Academy of Sciences, Shenyang (China); University of Chinese Academy of Sciences, Beijing (China); Sun, Wenru; Cui, Yuyou [Institute of Metal Research, Chinese Academy of Sciences, Shenyang (China); Yang, Rui, E-mail: ryang@imr.ac.cn [Institute of Metal Research, Chinese Academy of Sciences, Shenyang (China)

    2014-04-01

    Inconel 718 powders have been hot-isostatic-pressed (HIPed) at representative temperatures to investigate the variations in microstructure, tensile properties and tensile fracture mode of the powder compact. Microstructure of the powder compacts were characterized by optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and so on. The results showed that the interdendritic precipitates inherited from the powders were partially retained in the powder compacts when the powders were HIPed at or below 1210 °C but were eliminated when HIPed at and above 1260 °C. The grain size uniformity of the powder compacts first increases and then decreases with increasing HIPing temperature. Prior particle boundaries (PPBs) were observed in the powder compacts HIPed at and below 1260 °C but was eliminated when HIPed at 1275 °C. The PPBs were decorated with carbide particles, the amount of the carbide particles at the PPBs decreases with increasing HIPing temperature. Most of the PPBs were pinned by the carbide particles in the compacts HIPed at 1140 °C. When the HIPing temperature was increased to 1210 °C and 1260 °C, a large number of PPBs de-pinned and moved beyond the pinning carbide particles, leading to grain growth and leaving carbide particles at the site of the original PPBs within the new grains. With increasing HIPing temperature, the 0.2% yield strength of the powder compacts at 650 °C decreases, the tensile elongation increases, and the tensile fracture mode changed from inter-particle dominant fracture to fully dimple ductile fracture.

  13. Investigation of Thermal and Viscoelastic Properties of Polymers Relevant to Hot Melt Extrusion, IV: Affinisol™ HPMC HME Polymers.

    Science.gov (United States)

    Gupta, Simerdeep Singh; Solanki, Nayan; Serajuddin, Abu T M

    2016-02-01

    Most cellulosic polymers cannot be used as carriers for preparing solid dispersion of drugs by hot melt extrusion (HME) due to their high melt viscosity and thermal degradation at high processing temperatures. Three HME-grade hydroxypropyl methylcelluloses, namely Affinisol™ HPMC HME 15 cP, Affinisol™ HPMC HME 100 cP, and Affinisol™ HPMC HME 4 M, have recently been introduced by The Dow Chemical Co. to enable the preparation of solid dispersion at lower and more acceptable processing temperatures. In the present investigation, physicochemical properties of the new polymers relevant to HME were determined and compared with that of Kollidon(®) VA 64. Powder X-ray diffraction (PXRD), modulated differential scanning calorimetry (mDSC), thermogravimetric analysis (TGA), moisture sorption, rheology, and torque analysis by melt extrusion were applied. PXRD and mDSC showed that the Affinisol™ polymers were amorphous in nature. According to TGA, the onset of degradation for all polymers was >220°C. The Affinisol™ polymers exhibited less hygroscopicity than Kollidon(®) VA 64 and another HPMC polymer, Methocel™ K100LV. The complex viscosity profiles of the Affinisol™ polymers as a function of temperature were similar. The viscosity of the Affinisol™ polymers was highly sensitive to the shear rate applied, and unlike Kollidon(®) VA 64, the viscosity decreased drastically when the angular frequency was increased. Because of the very high shear rate encountered during melt extrusion, Affinisol™ polymers showed capability of being extruded at larger windows of processing temperatures as compared to that of Kollidon(®) VA 64.

  14. Effect of standard heat treatment on the microstructure and mechanical properties of hot isostatically pressed superalloy inconel 718

    International Nuclear Information System (INIS)

    Rao, G. Appa; Kumar, Mahendra; Srinivas, M.; Sarma, D.S.

    2003-01-01

    Ni-Fe base superalloy, Inconel 718, was processed through powder metallurgy (P/M) hot isostatic pressing (HIP) route. In order to balance the strength and ductility, the HIPed material was given the standard heat treatment, viz. solution treatment at 980 deg. C for 1 h/water quenched (WQ) to room temperature and a two-step ageing treatment consisting of 720 deg. C for 8 h/furnace cooling (FC) at 55 deg. C h -1 to 620 deg. C and holding at 620 deg. C for 8 h before air cooling (AC) to room temperature. Optical microscopy and scanning electron microscopy (SEM) studies on the heat treated alloy have shown a homogeneous microstructure with fine grain size (25 μm) along with the presence of prior particle boundary (PPB) networks. Transmission electron microscopy (TEM) on the heat treated material has revealed the presence of oxides, MC carbides and δ-precipitates at the grain boundaries and a uniform precipitation of fine γ'' and γ' strengthening phases in the matrix. Tensile and stress rupture tests were performed on the heat treated material. While the yield strength (YS) and ultimate tensile strength (UTS) of the HIPed and heat treated alloy at room temperature and 650 deg. C were comparable to those of conventionally processed wrought IN 718, its ductility was lower. The stress rupture life of the HIPed alloy improved marginally due to heat treatment and met the minimum specification requirement of life hours but the rupture ductility was found to be inferior to that of the wrought material. The fractography of the failed samples has revealed the transgranular ductile mode of fracture in the as-solution treated alloy, while intergranular mode of failure with the decohesion of PPBs occurred more predominantly in the aged condition. This change of fracture mode with ageing treatment shows the ductility dependence on the relative strength of the matrix and PPBs. The TEM studies on the deformed alloy have revealed that the brittle oxides and carbides at the prior

  15. Elastic properties and strain-to-crack-initiation of calcium phosphate bone cements: Revelations of a high-resolution measurement technique.

    Science.gov (United States)

    Ajaxon, Ingrid; Acciaioli, Alice; Lionello, Giacomo; Ginebra, Maria-Pau; Öhman-Mägi, Caroline; Baleani, Massimiliano; Persson, Cecilia

    2017-10-01

    Calcium phosphate cements (CPCs) should ideally have mechanical properties similar to those of the bone tissue the material is used to replace or repair. Usually, the compressive strength of the CPCs is reported and, more rarely, the elastic modulus. Conversely, scarce or no data are available on Poisson's ratio and strain-to-crack-initiation. This is unfortunate, as data on the elastic response is key to, e.g., numerical model accuracy. In this study, the compressive behaviour of brushite, monetite and apatite cements was fully characterised. Measurement of the surface strains was done using a digital image correlation (DIC) technique, and compared to results obtained with the commonly used built-in displacement measurement of the materials testers. The collected data showed that the use of fixed compression platens, as opposed to spherically seated ones, may in some cases underestimate the compressive strength by up to 40%. Also, the built-in measurements may underestimate the elastic modulus by up to 62% as compared to DIC measurements. Using DIC, the brushite cement was found to be much stiffer (24.3 ± 2.3GPa) than the apatite (13.5 ± 1.6GPa) and monetite (7.1 ± 1.0GPa) cements, and elastic moduli were inversely related to the porosity of the materials. Poisson's ratio was determined to be 0.26 ± 0.02 for brushite, 0.21 ± 0.02 for apatite and 0.20 ± 0.03 for monetite. All investigated CPCs showed low strain-to-crack-initiation (0.17-0.19%). In summary, the elastic modulus of CPCs is substantially higher than previously reported and it is concluded that an accurate procedure is a prerequisite in order to properly compare the mechanical properties of different CPC formulations. It is recommended to use spherically seated platens and measuring the strain at a relevant resolution and on the specimen surface. Copyright © 2017 The Authors. Published by Elsevier Ltd.. All rights reserved.

  16. Development of a Small Punch Test Technique for an Evaluation of the Mechanical Properties of Irradiated Materials in a Hot Cell

    International Nuclear Information System (INIS)

    Kim, Do-Sik; Ahn, Sang-Bok; Yoo, Byung-Ok; Choo, Yong-Sun; Hong, Kwon-Pyo

    2006-01-01

    Miniaturized specimens have been widely used to evaluate the mechanical properties of steels and plastics. Especially for a study on the irradiation effects in nuclear materials, the small specimen test techniques have attracted considerable attention. Therefore, it is essential that the test techniques be developed and verified to extract the mechanical properties information from small specimens. Among the test techniques using small specimens, the small punch (SP) test technique using small disc-sized specimen has been successfully used to estimate the tensile properties (yield strength and ultimate tensile strength), DBTT (ductile-brittle transition temperature), fracture toughness and creep properties of metals irradiated in a reactor or a proton accelerator. In this paper, the existing SP test techniques are reviewed and summarized. In addition, the information on the development of the SP test procedure is obtained to evaluate the radiation effects on the mechanical properties of nuclear materials in a hot cell

  17. The effect of combination treatment of gamma irradiation with refrigeration or with hot water treatment on the storage life and organoleptic properties of carabao mangoes and lacatan bananas

    International Nuclear Information System (INIS)

    Barruel, D.S.

    1976-03-01

    This study aims to determine the best combination of irradiation-hot water and irradiation-low temperature storage as treatments to help achieve longer shelf-life extension of fruits with export value such as bananas and mangoes. Results have shown the combined irradiation and hot water treatment as a better treatment for mangoes over that of combined irradiation (50kr) and low temperature storage (15 0 C) or of single treatments with irradiation, refrigeration or hot water. A much lower dose of 30 krad was found to give the longest extension in shelf-life in mangoes subjected to irradiation and hot (55 0 C) water treatment. No significant differences in the organoleptic properties were found in the samples given the combination treatment when compared to samples given no treatment at all. The extension in shelf-life may be attributed to the synergistic effect of the treatments, which could have affected the senescence of the fruit and likewise controlled the growth of rot-causing microorganisms. Similar work was also done on bananas but the results are still preliminary

  18. Effect Mo Addition on Corrosion Property and Sulfide Stress Cracking Susceptibility of High Strength Low Alloy Steels

    International Nuclear Information System (INIS)

    Lee, Woo Yong; Koh, Seong Ung; Kim, Kyoo Young

    2005-01-01

    The purpose of this work is to understand the effect of Mo addition on SSC susceptibility of high strength low alloy steels in terms of microstructure and corrosion property. Materials used in this study are high strength low alloy (HSLA) steels with carbon content of 0.04wt% and Mo content varying from 0.1 to 0.3wt%. The corrosion property of steels was evaluated by immersion test in NACE-TM01-77 solution A and by analyzing the growth behavior of surface corrosion products. SSC resistance of steels was evaluated using constant load test. Electrochemical test was performed to investigate initial corrosion rate. Addition of Mo increased corrosion rate of steels by enhancing the porosity of surface corrosion products. however, corrosion rate was not directly related to SSC susceptibility of steels

  19. Effect of weld metal properties on fatigue crack growth behaviour of gas tungsten arc welded AISI 409M grade ferritic stainless steel joints

    International Nuclear Information System (INIS)

    Shanmugam, K.; Lakshminarayanan, A.K.; Balasubramanian, V.

    2009-01-01

    The effect of filler metals such as austenitic stainless steel, ferritic stainless steel and duplex stainless steel on fatigue crack growth behaviour of the gas tungsten arc welded ferritic stainless steel joints was investigated. Rolled plates of 4 mm thickness were used as the base material for preparing single 'V' butt welded joints. Centre cracked tensile (CCT) specimens were prepared to evaluate fatigue crack growth behaviour. Servo hydraulic controlled fatigue testing machine was used to evaluate the fatigue crack growth behaviour of the welded joints. From this investigation, it was found that the joints fabricated by duplex stainless steel filler metal showed superior fatigue crack growth resistance compared to the joints fabricated by austenitic and ferritic stainless steel filler metals. Higher yield strength, hardness and relatively higher toughness may be the reasons for superior fatigue performance of the joints fabricated by duplex stainless steel filler metal.

  20. Effect of heat treatment and hot isostatic pressing on the microstructure and mechanical properties of Inconel 625 alloy processed by laser powder bed fusion

    Energy Technology Data Exchange (ETDEWEB)

    Kreitcberg, Alena, E-mail: alena.kreitcberg.1@ens.etsmtl.ca [École de technologie supérieure, 110 Notre-Dame Street West, Montreal, Quebec H3C 1K3 Canada (Canada); Brailovski, Vladimir, E-mail: vladimir.brailovski@etsmtl.ca [École de technologie supérieure, 110 Notre-Dame Street West, Montreal, Quebec H3C 1K3 Canada (Canada); Turenne, Sylvain, E-mail: sylvain.turenne@polymtl.ca [École Polytechnique de Montréal, 2900 boul. Édouard-Montpetit, Montreal, Quebec H3T 1J4 Canada (Canada)

    2017-03-24

    The effect of different heat treatments and hot isostatic pressing on the microstructure and mechanical properties of laser powder bed fusion IN625 alloy was studied. The heat treatments were: stress relief annealing, recrystallization annealing and low-temperature solution treatment. The resulting microstructure and crystallographic textures were studied using optical and scanning electron microscopy. The mechanical properties of the as-built and post-treated IN625 alloy were obtained after tensile testing at room temperature and at 760 °C (1400 °F), and compared to those of an annealed wrought alloy of the same composition.

  1. Unsaturated Seepage Analysis of Cracked Soil including Development Process of Cracks

    Directory of Open Access Journals (Sweden)

    Ling Cao

    2016-01-01

    Full Text Available Cracks in soil provide preferential pathways for water flow and their morphological parameters significantly affect the hydraulic conductivity of the soil. To study the hydraulic properties of cracks, the dynamic development of cracks in the expansive soil during drying and wetting has been measured in the laboratory. The test results enable the development of the relationships between the cracks morphological parameters and the water content. In this study, the fractal model has been used to predict the soil-water characteristic curve (SWCC of the cracked soil, including the developmental process of the cracks. The cracked expansive soil has been considered as a crack-pore medium. A dual media flow model has been developed to simulate the seepage characteristics of the cracked expansive soil. The variations in pore water pressure at different part of the model are quite different due to the impact of the cracks. This study proves that seepage characteristics can be better predicted if the impact of cracks is taken into account.

  2. Effect of time-dependent material properties on the crack behavior in the interface of two polymeric materials

    Czech Academy of Sciences Publication Activity Database

    Zouhar, Michal; Hutař, Pavel; Náhlík, Luboš; Knésl, Zdeněk

    2011-01-01

    Roč. 47, č. 2 (2011), s. 203-210 ISSN 0191-5665 R&D Projects: GA ČR GC101/09/J027; GA ČR GD106/09/H035; GA ČR GA106/09/0279 Institutional research plan: CEZ:AV0Z20410507 Keywords : multilayer plastic pipes * bimaterial interface * stability criteria * critical stress * time -depended material properties Subject RIV: JL - Materials Fatigue, Friction Mechanics Impact factor: 0.409, year: 2011

  3. Crack closure and sequential effects in fatigue: A literature survey

    Science.gov (United States)

    Holmgren, M.

    A literature survey of the phenomenon of crack closure is reported here. The state of the art is reviewed and several empirical formulas for determining the crack closure are compared with each other. Their properties, advantages and disadvantages are briefly discussed. Experimental techniques for determining the crack closure stress are presented and experimental data from the literature are reported.

  4. The crack growth resistance of thin steel sheets under eccentric ...

    Indian Academy of Sciences (India)

    Ľ AMBRIŠKO

    2018-03-10

    Mar 10, 2018 ... Abstract. The stable crack growth in thin steel sheets is the topic of this paper. The crack opening was observed using a videoextensometry system, allowing the crack extension determination. JR-curve and dR-curve were established from obtained data. The ductile tearing properties of different thin sheets ...

  5. Hot ductility testing and weld simulation tests

    International Nuclear Information System (INIS)

    Weber, G.; Schick, M.

    1999-01-01

    The objective of the project was to enhance the insight into the causes of intergranular cracks detected in austenitic circumferential welds at BWR pipes. The susceptibility of a variety of austenitic pipe materials to hot cracking during welding and in-service intergranular crack corrosion was examined. The assumption was cracking in the root area of the HAZ of a multiple-layer weld. Hot-ductility tests and weld simulation tests specifically designed for the project were performed with the austenitic LWR pipe materials 1.4553 (X6 CrNiNb 18 10 S), 1.4550 (X10 CrNiNb 18 9), 1.4533 (X6 CrNiTi 18 9, two weld pools), and a non-stabilized TP 304 (X5 CrNi 18 10). (orig./CB) [de

  6. Modified Dugdale cracks and Fictitious cracks

    DEFF Research Database (Denmark)

    Nielsen, Lauge Fuglsang

    1998-01-01

    A number of theories are presented in the literature on crack mechanics by which the strength of damaged materials can be predicted. Among these are theories based on the well-known Dugdale model of a crack prevented from spreading by self-created constant cohesive flow stressed acting in local...... areas, so-called fictitious cracks, in front of the crack.The Modified Dugdale theory presented in this paper is also based on the concept of Dugdale cracks. Any cohesive stress distribution, however, can be considered in front of the crack. Formally the strength of a material weakened by a modified...... Dugdale crack is the same as if it has been weakened by the well-known Griffith crack, namely sigma_CR = (EG_CR/phi)^1/2 where E and 1 are Young's modulus and crack half-length respectively, and G_CR is the so-called critical energy release rate. The physical significance of G_CR, however, is different...

  7. Crack Growth Rate Properties of Gr.91 Steel for a Defect Assessment of a Component in a Sodium-cooled Fast Reactor

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Hyeong-Yeon; Kim, Woo-Gon [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2015-05-15

    In this study, the crack growth models were derived from a number of crack growth tests for Gr.91 steel specimens under fatigue loading and creep loading at elevated temperature. The test data from the experiments of fatigue crack growth (FCG) and creep crack growth (CCG) were obtained, and the test data were compared with those of the RCC-MRx to investigate conservatism of the crack growth models in RCC-MRx. It was shown that the FCG rate model of RCC-MRx was conservative while the CCG model was non-conservative for Gr.91 steel when compared with present test data. The FCG rate tests were conducted with round bar type single edge crack tension specimens, and standard C(T) specimens with a 12.7mm thickness. The FCG test results were compared with those of the FCG rate models of RCC-MRx that are based on 25.4mm thick C(T) specimens. It was shown that the FCG rate model of RCC-MRx was conservative when compared to the present test data. The CCG rate models were derived from the test data for standard C(T) specimens with 12.7mm thickness. The data were compared with those of the RCC-MRx that are based on 25.4mm thick C(T) specimens. Conservatism of the crack growth models in 2012 edition of the RCC-MRx code was reviewed with the present CCG test data.

  8. Hot rolling and annealing effects on the microstructure and mechanical properties of ODS austenitic steel fabricated by electron beam selective melting

    Science.gov (United States)

    Gao, Rui; Ge, Wen-jun; Miao, Shu; Zhang, Tao; Wang, Xian-ping; Fang, Qian-feng

    2016-03-01

    The grain morphology, nano-oxide particles and mechanical properties of oxide dispersion strengthened (ODS)-316L austenitic steel synthesized by electron beam selective melting (EBSM) technique with different post-working processes, were explored in this study. The ODS-316L austenitic steel with superfine nano-sized oxide particles of 30-40 nm exhibits good tensile strength (412 MPa) and large total elongation (about 51%) due to the pinning effect of uniform distributed oxide particles on dislocations. After hot rolling, the specimen exhibits a higher tensile strength of 482 MPa, but the elongation decreases to 31.8% owing to the introduction of high-density dislocations. The subsequent heat treatment eliminates the grain defects induced by hot rolling and increases the randomly orientated grains, which further improves the strength and ductility of EBSM ODS-316L steel.

  9. HOT 2012

    DEFF Research Database (Denmark)

    Lund, Henriette Romme

    Undersøgelse af, hvad der er hot - og hvad der burde være hot på læseområdet med 21 læsekyndige. Undersøgelsen er gennemført siden 2010. HOT-undersøgelsen er foretaget af Nationalt Videncenter for Læsning - Professionshøjskolerne i samarb. med Dansklærerforeningen......Undersøgelse af, hvad der er hot - og hvad der burde være hot på læseområdet med 21 læsekyndige. Undersøgelsen er gennemført siden 2010. HOT-undersøgelsen er foretaget af Nationalt Videncenter for Læsning - Professionshøjskolerne i samarb. med Dansklærerforeningen...

  10. Probability of crack-initiation and application to NDE

    Energy Technology Data Exchange (ETDEWEB)

    Prantl, G [Nuclear Safety Inspectorate HSK, (Switzerland)

    1988-12-31

    Fracture toughness is a property with a certain variability. When a statistical distribution is assumed, the probability of crack initiation may be calculated for a given problem defined by its geometry and the applied stress. Experiments have shown, that cracks which experience a certain small amount of ductile growth can reliably be detected by acoustic emission measurements. The probability of crack detection by AE-techniques may be estimated using this experimental finding and the calculated probability of crack initiation. (author).

  11. The influence of Ni addition and hot-extrusion on the microstructure and tensile properties of Al–15%Mg2Si composite

    International Nuclear Information System (INIS)

    Emamy, M.; Khodadadi, M.; Honarbakhsh Raouf, A.; Nasiri, N.

    2013-01-01

    Highlights: ► Ni content on the microstructure and tensile properties of Al–Mg 2 Si composite. ► Ni changed the size of primary Mg 2 Si from 42 μm to 17 μm. ► Higher UTS and elongation values obtained by addition of 5 wt% Ni. ► Fracture behavior changed from brittle to ductile by Ni addition and extrusion. - Abstract: The effects of nickel addition and hot-extrusion on the microstructure and tensile properties of in situ Al–15%Mg 2 Si composite specimens have been investigated. Al–15%Mg 2 Si composite ingots were prepared by an in situ process and different amounts of nickel (0.1, 0.3, 0.5, 1.0, 3.0 and 5.0 wt% Ni) were added to the remelted composite. Optical microscopy (OM) and scanning electron microscopy (SEM) indicated that Ni addition changes the morphology of both primary and eutectic Mg 2 Si phases and decreases the size of primary Mg 2 Si particles from 42 μm to 17 μm. Hot-extrusion was found to be powerful in breaking the eutectic network and changing the size and morphology of pseudo-eutectic Mg 2 Si phase. The results obtained from tensile testing revealed that both Ni addition and hot-extrusion process improve ultimate tensile strength (UTS) and elongation values. Fracture surface examinations revealed a transition from brittle fracture mode in as-cast composite to ductile fracture in hot-extruded composite after Ni addition. This can be attributed to the changes in size and morphology of primary and eutectic Mg 2 Si phases and also the formation of more and finer α-Al phase

  12. HOT 2014

    DEFF Research Database (Denmark)

    Lund, Henriette

    Undersøgelse af, hvad der er hot - og hvad der burde være hot på læseområdet med 21 læsekyndige. Undersøgelsen er gennemført siden 2010. HOT-undersøgelsen er foretaget af Nationalt Videncenter for Læsning - Professionshøjskolerne i samarb. med Dansklærerforeningen...

  13. Microstructures and mechanical properties of Cu/Ti{sub 3}SiC{sub 2}/C/MWCNTs composites prepared by vacuum hot-pressing sintering

    Energy Technology Data Exchange (ETDEWEB)

    Xiaosong, Jiang, E-mail: xsjiang@yeah.net [School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Liu, Wanxia; Li, Jingrui [School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Shao, Zhenyi [Department of Mechanical Engineering, Chengdu Technological University, Chengdu, Sichuan 610031 (China); Zhu, Degui [School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China)

    2015-01-05

    Highlights: • Cu/Ti{sub 3}SiC{sub 2}/C/MWCNTs composites were prepared using vacuum hot-pressing sintering. • Dispersions of MWCNTs were prepared using 10 μg/ml gallic acid aqueous solution. • MWCNTs content has no effect on generation of TiC and Cu{sub 9}Si to effect matrix’s performance. - Abstract: Cu/Ti{sub 3}SiC{sub 2}/C/MWCNTs composites were prepared by vacuum hot-pressing sintering. Microstructures and mechanical properties of Cu/Ti{sub 3}SiC{sub 2}/C/MWCNTs composites with different multi-walled carbon nanotubes contents have been systematically investigated. The microstructures of the composites were examined by optical microscopy, X-ray diffraction, back scattered electron imaging, scanning electron microscope and energy dispersive spectrometer. The mechanical properties were determined from Brinell hardness and tensile tests. The results demonstrated that there was an optimum value of MWCNTs content which has an impact on microstructures and mechanical properties of Cu/Ti{sub 3}SiC{sub 2}/C/MWCNTs composites. Based on MWCNTs content on properties and microstructure of Cu/Ti{sub 3}SiC{sub 2}/C/MWCNTs composites, effects of MWCNTs on improvement of the composites and strengthening mechanism have been analyzed.

  14. Comparison of finite element J-integral evaluations for the blunt crack model and the sharp crack model

    International Nuclear Information System (INIS)

    Pan, Y.C.; Kennedy, J.M.

    1983-01-01

    In assessing the safety of a liquid metal fast breeder reactor (LMFBR), a major concern is that of hot sodium coming into contact with either unprotected concrete or steel-lined concrete equipment cells and containment structures. An aspect of this is the potential of concrete cracking which would significantly influence the safety assessment. Concrete cracking in finite element analysis can be modeled as a blunt crack in which the crack is assumed to be uniformly distributed throughout the area of the element. A blunt crack model based on the energy release rate and the effective strength concepts which was insensitive to the element size was presented by Bazant and Cedolin. Some difficulties were encountered in incorporating their approach into a general purpose finite element code. An approach based on the J-integral to circumvent some of the difficulties was proposed by Pan, Marchertas, and Kennedy. Alternatively, cracking can also be modeled as a sharp crack where the crack surface is treated as the boundary of the finite element mesh. The sharp crack model is adopted by most researchers and its J-integral has been well established. It is desirable to establish the correlation between the J-integrals, or the energy release rates, for the blunt crack model and the sharp crack model so that data obtained from one model can be used on the other

  15. Application of the concrete aging model to the case of cracked materials and to the coupling with the mechanical properties; Application du modele de degradation du beton au cas des milieux fissures et au couplage avec la mecanique

    Energy Technology Data Exchange (ETDEWEB)

    Torrenti, J.M.; Adenot, F.; Tognazzi, C. [CEA/Saclay, 91 - Gif-sur-Yvette (France); Tognazzi, C. [Toulouse Univ., 31 (France). LMDC; Danese, S. [Ecole Nationale Superieure des Arts et Industries de Strasbourg, 67 - Strasbourg (France); Poyet, S. [Ecole Nationale Superieure de Cachan, 94 (France)

    1998-07-01

    Predicting the long-term behavior of concrete used in radioactive waste disposal requires the knowledge of the effects of constantly renewed water on its chemistry and its coupling with the mechanical properties. In contact with water, concrete undergoes chemical degradation. This degradation influences the mechanical performance of the material as well as cracks could interfere with the chemical degradation. This paper shows how these problems can be treated using the Ca{sup ++} concentration in pore solution as the state variable that conducts the evolution of chemical, physical and mechanical properties. Some comparisons with experimental results are shown. Finally, the problem of the numerical simulation of accelerated tests of cracked samples is discussed. (authors)

  16. HOT 2011

    DEFF Research Database (Denmark)

    Lund, Henriette Romme

    En undersøgelse af, hvad der er hot - og burde være hot på læseområdet. I undersøgelsen deltager 21 læsekyndige fra praksisfeltet, professionshøjskolerne og forskningsområdet.......En undersøgelse af, hvad der er hot - og burde være hot på læseområdet. I undersøgelsen deltager 21 læsekyndige fra praksisfeltet, professionshøjskolerne og forskningsområdet....

  17. Microscopic Examination of Distribution and Phenotypic Properties of Phylogenetically Diverse Chloroflexaceae-Related Bacteria in Hot Spring Microbial Mats

    DEFF Research Database (Denmark)

    Nübel, U.; Bateson, Mary M.; Vandieken, V.

    2002-01-01

    We investigated the diversity, distribution, and phenotypes of uncultivated Chloroflexaceae-related bacteria in photosynthetic microbial mats of an alkaline hot spring (Mushroom Spring, Yellowstone National Park). By applying a directed PCR approach, molecular cloning, and sequence analysis of 16S...

  18. Tribological properties of anti-wear PVD coatings for elevated temperatures application deposited onto X37CrMoV5-1 type hot work steel

    International Nuclear Information System (INIS)

    Dobrzanski, L.A.; Polok, M.; Adamiak, M.

    2003-01-01

    The paper presents results of tribological and adhesion investigations of anti-wear PVD coatings TiN, TiN/(Ti,Al)N and CrN types deposited in ion plating PVD process onto X37CrMoV5-1 type hot work tool steel. It was found that damage mechanism during scratch test in all investigated coatings begins with multiple spallings located on the scratch edges followed by cracking and tool coatings delamination. Regarding to the coating types it can be seen different location of such damages and loads typical for them. According to this observations it can be stated that highest adhesion among investigated coating present, CrN monolayer coating and the lowest one multilayers Ti/(Ti,Al)N coating. The wear resistance was investigated by pin-on-disc method performed in room and elevated to 500 o C temperatures. It was found that the lowest wear in to fixed investigation conditions in both room and elevated temperatures shows TiN monolayer coating. Additionally one can see that TiN coatings application improve wear resistance some five times. (author)

  19. Properties of 13HMF steel for steam pipelines as a result of impact and cracking resistance investigations; Wlasnosci stali 13HMF na rurociagi pary swiezej w swietle badan udarnosci i odpornosci na pekanie

    Energy Technology Data Exchange (ETDEWEB)

    Bilous, W.; Wasiak, J.; Hajewska, E.; Szteke, W.; Wagner, T. [Institute of Atomic Energy, Otwock-Swierk (Poland)

    1996-12-31

    Long lasting and safe exploitation of steam pipelines in energetics depends strongly on mechanical properties of material used for tubing production. Most of pipelines installed in polish energetics is made of Cr-Mo-V type steel. The investigation results of such steel (13MHF) concerning the influence of exploitation time on impact and cracking resistance have been presented, discussed and compared with the imported steel P91. 3 refs, 7 figs, 3 tabs.

  20. Quick Reaction Evaluation of Materials and Processes. Delivery Order 0011: Engineering Properties, Fatigue, and Crack Growth Data on SCS-6/Ti-6Al-4V Titanium Matrix Composite (16 Ply) Panels

    Science.gov (United States)

    2009-05-01

    tabs were bonded to the specimen using a TIG welding process to ensure adhesion of the tabs throughout the experiment. The shear specimens and the...AFRL-RX-WP-TR-2010-4175 QUICK REACTION EVALUATION OF MATERIALS AND PROCESSES Delivery Order 0011: Engineering Properties, Fatigue, and Crack...From - To) May 2009 Final 03 April 2006 – 29 May 2009 4. TITLE AND SUBTITLE QUICK REACTION EVALUATION OF MATERIALS AND PROCESSES Delivery Order

  1. Hardness properties and microscopic investigation of crack- crystal interaction in SiO(2)-MgO-Al(2)O(3)-K(2)O-B(2)O(3)-F glass ceramic system.

    Science.gov (United States)

    Roy, Shibayan; Basu, Bikramjit

    2010-01-01

    In view of the potential engineering applications requiring machinability and wear resistance, the present work focuses to evaluate hardness property and to understand the damage behavior of some selected glass-ceramics having different crystal morphologies with SiO(2)-MgO-Al(2)O(3)-K(2)O-B(2)O(3)-F composition, using static micro-indentation tests as well as dynamic scratch tests, respectively. Vickers hardness of up to 5.5 GPa has been measured in glass-ceramics containing plate like mica crystals. Scratch tests at a high load of 50 Nin artificial saliva were carried out in order to simulate the crack-microstructure interaction during real-time abrasion wear and machining operation. The experimental observations indicate that the novel "spherulitic-dendritic shaped "crystals, similar to the plate like crystals, have the potential to hinder the scratching induced crack propagation. In particular, such potential of the 'spherulitic-dendritic' crystals become more effective due to the larger interfacial area with the glass matrix as well as the dendritic structure of each mica plate, which helps in crack deflection and crack blunting, to a larger extent.While modest damage tolerant behavior is observed in case of 'spherulitic-dendritic' crystal containing material, severe brittle fracture of plate like crystals were noted, when both were scratched at 50 N load.

  2. Cocaine (Coke, Crack) Facts

    Science.gov (United States)

    ... That People Abuse » Cocaine (Coke, Crack) Facts Cocaine (Coke, Crack) Facts Listen Cocaine is a white ... 69 KB) "My life was built around getting cocaine and getting high." ©istock.com/ Marjot Stacey is ...

  3. Influence of cracks generation on the structural and optical properties of GaN/Al0.55Ga0.45N multiple quantum wells

    International Nuclear Information System (INIS)

    Sun, Q.; Zhang, J.C.; Huang, Y.; Chen, J.; Wang, J.F.; Wang, H.; Li, D.Y.; Wang, Y.T.; Zhang, S.M.; Yang, H.; Zhou, C.L.; Guo, L.P.; Jia, Q.J.

    2006-01-01

    Both cracked and crack-free GaN/Al 0.55 Ga 0.45 N multiple quantum wells (MQWs) grown on GaN template by metalorganic chemical vapor deposition have been studied by triple-axis X-ray diffraction, grazing-incidence X-ray reflectivity, atomic force microscope, photoluminescence spectroscopy and low-energy positron annihilation spectroscopy. The experimental results show that cracks generation not only deteriorates the surface morphology, but also leads to a period dispersion and roughens the interfaces of MQWs. The mean density of dislocations in MQWs, determined from the average full-width at half-maximum of ω-scan of each satellite peak, has been significantly enhanced by the cracks generation. Furthermore, the measurement of annihilation-line Doppler broadening reveals a higher concentration of negatively charged vacancies in the cracked MQWs. The combination of these vacancies and the high density of edge dislocations are assumed to contribute to the highly enhanced yellow luminescence in the cracked sample

  4. On the finite element modeling of the asymmetric cracked rotor

    Science.gov (United States)

    AL-Shudeifat, Mohammad A.

    2013-05-01

    The advanced phase of the breathing crack in the heavy duty horizontal rotor system is expected to be dominated by the open crack state rather than the breathing state after a short period of operation. The reason for this scenario is the expected plastic deformation in crack location due to a large compression stress field appears during the continuous shaft rotation. Based on that, the finite element modeling of a cracked rotor system with a transverse open crack is addressed here. The cracked rotor with the open crack model behaves as an asymmetric shaft due to the presence of the transverse edge crack. Hence, the time-varying area moments of inertia of the cracked section are employed in formulating the periodic finite element stiffness matrix which yields a linear time-periodic system. The harmonic balance method (HB) is used for solving the finite element (FE) equations of motion for studying the dynamic behavior of the system. The behavior of the whirl orbits during the passage through the subcritical rotational speeds of the open crack model is compared to that for the breathing crack model. The presence of the open crack with the unbalance force was found only to excite the 1/2 and 1/3 of the backward critical whirling speed. The whirl orbits in the neighborhood of these subcritical speeds were found to have nearly similar behavior for both open and breathing crack models. While unlike the breathing crack model, the subcritical forward whirling speeds have not been observed for the open crack model in the response to the unbalance force. As a result, the behavior of the whirl orbits during the passage through the forward subcritical rotational speeds is found to be enough to distinguish the breathing crack from the open crack model. These whirl orbits with inner loops that appear in the neighborhood of the forward subcritical speeds are then a unique property for the breathing crack model.

  5. The influence of powder composition and sintering temperature on transformation kinetics, structure and mechanical properties of hot-pressed silicon nitride

    International Nuclear Information System (INIS)

    Knoch, H.; Ziegler, G.

    1977-01-01

    The strength at room temperature of hot-pressed silicon nitride is strongly dependent on the structure which in turn depends on powder composition and process parameters. Connections between production conditions (MgO content, pressing temperature, pressing time), structure (α/β content and morphology), and the properties at room temperature are discussed. The growth of oblong β grains - as a direct result of phase transition from α- to β-Si 3 N 4 - results in microstructural meshing and thus in a higher strength. Optimum mechanical properties are achieved after full phase transformation and with a microstructure as fine as possible. The direct connection between strength and transformed β fraction indicates a possible way for a relatively fast determination of optimum properties for a given initial powder. (orig.) [de

  6. Development of Duplex Stainless Steels by Field-Assisted Hot Pressing: Influence of the Particle Size and Morphology of the Powders on the Final Mechanical Properties

    Science.gov (United States)

    García-Junceda, A.; Rincón, M.; Torralba, J. M.

    2018-01-01

    The feasibility of processing duplex stainless steels with promising properties using a powder metallurgical route, including the consolidation by field-assisted hot pressing, is assessed in this investigation. The influence of the particle size and morphology of the raw austenitic and ferritic powders on the final microstructure and properties is also evaluated for an austenitic content of 60 wt pct. In addition, the properties of a new microconstituent generated between the initial constituents are analyzed. The maximum sintered density (98.9 pct) and the best mechanical behavior, in terms of elastic modulus, nanohardness, yield strength, ultimate tensile strength, and ductility, are reached by the duplex stainless steel processed with austenitic and ferritic gas atomized stainless steel powders.

  7. Fabrication and Analysis of the Wear Properties of Hot-Pressed Al-Si/SiCp + Al-Si-Cu-Mg Metal Matrix Composite

    Science.gov (United States)

    Bang, Jeongil; Oak, Jeong-Jung; Park, Yong Ho

    2016-01-01

    The aim of this study was to characterize microstructures and mechanical properties of aluminum metal matrix composites (MMC's) prepared by powder metallurgy method. Consolidation of mixed powder with gas atomized Al-Si/SiCp powder and Al-14Si-2.5Cu-0.5Mg powder by hot pressing was classified according to sintering temperature and sintering time. Sintering condition was optimized using tensile properties of sintered specimens. Ultimate tensile strength of the optimized sintered specimen was 228 MPa with an elongation of 5.3% in longitudinal direction. In addition, wear properties and behaviors of the sintered aluminum-based MMC's were analyzed in accordance with vertical load and linear speed. As the linear speed and vertical load of the wear increased, change of the wear behavior occurred in order of oxidation of Al-Si matrix, formation of C-rich layer, Fe-alloying to matrix, and melting of the specimen

  8. Effect of carbon content on microstructure and mechanical properties of hot-rolled low carbon 12Cr-Ni stainless steel

    International Nuclear Information System (INIS)

    Zheng, H.; Ye, X.N.; Li, J.D.; Jiang, L.Z.; Liu, Z.Y.; Wang, G.D.; Wang, B.S.

    2010-01-01

    Research highlights: → Hot-rolled ultra low carbon martensite is characterized by dislocation cells substructure. → The formation of dislocation cells is attributed to high Ms and low interstitial atoms content. → Hot-rolled ultra low carbon 12Cr-Ni stainless steel has excellent impact toughness. → Delta ferrite deteriorates the impact toughness of hot-rolled 12Cr-Ni stainless steel. - Abstract: 12Cr-Ni stainless steels containing different carbon contents from 0.004 wt.% to 0.034 wt.% were hot-rolled and air-cooled. Their corresponding microstructures were observed with optical microscope and transmission electron microscope, and the Vickers hardness, tensile and impact tests were also carried out. It was found that the martensitic morphology was significantly influenced by carbon content. The as-received ultra low carbon martensite in the steel containing 0.004 wt.% C is characterized by dislocation cells substructure. The formation of dislocation cells is attributed to high martensite finishing point (above 400 deg. C) and low interstitial atoms content. On the other hand, the martensite in the steel containing 0.034 wt.% C consists mainly of typical martensite laths because of low martensite finishing point and high interstitial atoms content which hinder dislocation motion. Furthermore, carbon content has an evident effect on the mechanical properties of 12Cr-Ni steels. The hardness and strength of the as-received steels increase with an increase in carbon content, but their elongation and impact toughness decrease with the carbon content. The steel containing 0.004 wt.% C has excellent impact toughness due to the ultra low carbon content in the martensite composed of dislocation cells.

  9. Synthesis and anomalous magnetic properties of LaFeO{sub 3} nanoparticles by hot soap method

    Energy Technology Data Exchange (ETDEWEB)

    Fujii, Tatsuo, E-mail: tfujii@cc.okayama-u.ac.jp [Department of Applied Chemistry, Okayama University, Tsushima-naka 3-1-1, Okayama 700-8530 (Japan); Matsusue, Ikkoh; Nakatsuka, Daisuke; Nakanishi, Makoto; Takada, Jun [Department of Applied Chemistry, Okayama University, Tsushima-naka 3-1-1, Okayama 700-8530 (Japan)

    2011-10-03

    Highlights: {yields} Nanocrystalline LaFeO{sub 3} particles were synthesized by using hot soap technique. {yields} Average diameter of the obtained LaFeO{sub 3} nanoparticles was about 15 nm. {yields} They exhibited superparamagnetic behavior with a blocking temperature of 30 K. {yields} Large magnetization due to the presence of uncompensated surface spins was induced. - Abstract: Nanocrystalline LaFeO{sub 3} particles were synthesized at low temperatures by using hot soap technique. The synthesis was based on the thermal decomposition of organometallic compounds precipitated in a hot coordinating solvent. Moderate heat treatment at low temperature far below the combustion point of organic compounds produced spherical LaFeO{sub 3} nanoparticles with average diameter of about 15 nm. The crystalline phase, structure and particle size of obtained products were characterized by X-ray diffraction, infrared spectroscopy and transmission electron microscopy observations. In spite of the antiferromagnetic nature of bulk LaFeO{sub 3}, the obtained nanoparticles exhibited anomalous large magnetization. Superparamagnetic behavior with a blocking temperature of about 30 K was observed in both magnetization and Moessbauer spectroscopic analyses.

  10. Stress corrosion cracking experience in steam generators at Bruce NGS

    International Nuclear Information System (INIS)

    King, P.J.; Gonzalez, F.; Brown, J.

    1993-01-01

    In late 1990 and through 1991, units 1 and 2 at the Bruce A Nuclear Generating Station (BNGS-A) experienced a number of steam generator tube leaks. Tube failures were identified by eddy current to be circumferential cracks at U-bend supports on the hot-leg side of the boilers. In late 1991, tubes were removed from these units for failure characterization. Two active failure modes were found: corrosion fatigue in both units 1 and 2 and stress corrosion cracking (SCC) in unit 2. In unit 2, lead was found in deposits, on tubes, and in cracks, and the cracking was mixed-mode: transgranular and intergranular. This convincingly indicated the involvement of lead in the stress corrosion cracking failures. A program of inspection and tube removals was carried out to investigate more fully the extent of the problem. This program found significant cracking only in lead-affected boilers in unit 2, and also revealed a limited extent of non-lead-related intergranular stress corrosion cracking in other boilers and units. Various aspects of the failures and tube examinations are presented in this paper. Included is discussion of the cracking morphology, measured crack size distributions, and chemical analysis of tube surfaces, crack faces, and deposits -- with particular emphasis on lead

  11. High temperature cracking of steels: effect of geometry on creep crack growth laws

    International Nuclear Information System (INIS)

    Kabiri, M.R.

    2003-12-01

    This study was performed at Centre des Materiaux de l'Ecole des Mines de Paris. It deals with identification and transferability of high temperature creep cracking laws of steels. A global approach, based on C * and J non-linear fracture mechanics parameters has been used to characterize creep crack initiation and propagation. The studied materials are: the ferritic steels 1Cr-1Mo-1/4V (hot and cold parts working at 540 and 250 C) used in the thermal power stations and the austenitic stainless steel 316 L(N) used in the nuclear power stations. During this thesis a data base was setting up, it regroups several tests of fatigue, creep, creep-fatigue, and relaxation. Its particularity is to contain several creep tests (27 tests), achieved at various temperatures (550 to 650 C) and using three different geometries. The relevance of the C * parameter to describe the creep crack propagation was analysed by a means of systematic study of elasto-viscoplastic stress singularities under several conditions (different stress triaxiality). It has been shown that, besides the C * parameter, a second non singular term, denoted here as Q * , is necessary to describe the local variables in the vicinity of the crack tip. Values of this constraint parameter are always negative. Consequently, application of typical creep crack growth laws linking the creep crack growth rate to the C * parameter (da/dt - C * ), will be conservative for industrial applications. Furthermore, we showed that for ferritic steels, crack incubation period is important, therefore a correlation of Ti - C * type has been kept to predict crack initiation time Ti. For the austenitic stainless steel, the relevant stage is the one of the crack propagation, so that a master curve (da/dt - C * ), using a new data analysis method, was established. Finally, the propagation of cracks has been simulated numerically using the node release technique, allowing to validate analytical expressions utilised for the experimental

  12. Research progress on expansive soil cracks under changing environment.

    Science.gov (United States)

    Shi, Bei-xiao; Zheng, Cheng-feng; Wu, Jin-kun

    2014-01-01

    Engineering problems shunned previously rise to the surface gradually with the activities of reforming the natural world in depth, the problem of expansive soil crack under the changing environment becoming a control factor of expansive soil slope stability. The problem of expansive soil crack has gradually become a research hotspot, elaborates the occurrence and development of cracks from the basic properties of expansive soil, and points out the role of controlling the crack of expansive soil strength. We summarize the existing research methods and results of expansive soil crack characteristics. Improving crack measurement and calculation method and researching the crack depth measurement, statistical analysis method, crack depth and surface feature relationship will be the future direction.

  13. Effect of hot rolling on the structure and the mechanical properties of nitrogen-bearing austenitic-martensitic 14Kh15AN4M steel

    Science.gov (United States)

    Bannykh, O. A.; Betsofen, S. Ya.; Lukin, E. I.; Blinov, V. M.; Voznesenskaya, N. M.; Tonysheva, O. A.; Blinov, E. V.

    2016-04-01

    The effect of the rolling temperature and strain on the structure and the properties of corrosionresistant austenitic-martensitic 14Kh15AN4M steel is studied. The steel is shown to exhibit high ductility: upon rolling in the temperature range 700-1100°C at a reduction per pass up to 80%, wedge steel specimens are uniformly deformed along and across the rolling direction without cracking and other surface defects. Subsequent cold treatment and low-temperature tempering ensure a high hardness of the steel (50-56 HRC). Austenite mainly contributes to the hardening upon rolling in the temperature range 700-800°C at a reduction of 50-70%, and martensite makes the main contribution at higher temperatures and lower strains. Texture does not form under the chosen deformation conditions, which indicates dynamic recrystallization with the nucleation and growth of grains having no preferential orientation.

  14. Unified risk analysis of fatigue failure in ductile alloy components during all three stages of fatigue crack evolution process.

    Science.gov (United States)

    Patankar, Ravindra

    2003-10-01

    Statistical fatigue life of a ductile alloy specimen is traditionally divided into three stages, namely, crack nucleation, small crack growth, and large crack growth. Crack nucleation and small crack growth show a wide variation and hence a big spread on cycles versus crack length graph. Relatively, large crack growth shows a lesser variation. Therefore, different models are fitted to the different stages of the fatigue evolution process, thus treating different stages as different phenomena. With these independent models, it is impossible to predict one phenomenon based on the information available about the other phenomenon. Experimentally, it is easier to carry out crack length measurements of large cracks compared to nucleating cracks and small cracks. Thus, it is easier to collect statistical data for large crack growth compared to the painstaking effort it would take to collect statistical data for crack nucleation and small crack growth. This article presents a fracture mechanics-based stochastic model of fatigue crack growth in ductile alloys that are commonly encountered in mechanical structures and machine components. The model has been validated by Ray (1998) for crack propagation by various statistical fatigue data. Based on the model, this article proposes a technique to predict statistical information of fatigue crack nucleation and small crack growth properties that uses the statistical properties of large crack growth under constant amplitude stress excitation. The statistical properties of large crack growth under constant amplitude stress excitation can be obtained via experiments.

  15. Delayed hydride cracking: theoretical model testing to predict cracking velocity

    International Nuclear Information System (INIS)

    Mieza, Juan I.; Vigna, Gustavo L.; Domizzi, Gladys

    2009-01-01

    Pressure tubes from Candu nuclear reactors as any other component manufactured with Zr alloys are prone to delayed hydride cracking. That is why it is important to be able to predict the cracking velocity during the component lifetime from parameters easy to be measured, such as: hydrogen concentration, mechanical and microstructural properties. Two of the theoretical models reported in literature to calculate the DHC velocity were chosen and combined, and using the appropriate variables allowed a comparison with experimental results of samples from Zr-2.5 Nb tubes with different mechanical and structural properties. In addition, velocities measured by other authors in irradiated materials could be reproduced using the model described above. (author)

  16. Comparison of the hot-stamped boron-alloyed steel and the warm-stamped medium-Mn steel on microstructure and mechanical properties

    International Nuclear Information System (INIS)

    Li, Xiaodong; Chang, Ying; Wang, Cunyu; Hu, Ping; Dong, Han

    2017-01-01

    The application of high strength steels (HSS) for automotive structural parts is an effective way to realize lightweight and enhance safety. Therefore, improvements in mechanical properties of HSS are needed. In the present study, the warm stamping process of the third generation automotive medium-Mn steel was discussed, the characteristics of martensitic transformation were investigated, as well as the microstructure and mechanical properties were analyzed, compared to the popular hot-stamped 22MnB5 steel in the automotive industry. The results are indicated as follows. Firstly, the quenching rate of the medium-Mn steel can be selected in a wide range based on its CCT curves, which is beneficial to the control of forming process. Secondly, the influence of stamping temperature and pressure on the M s temperature of the medium-Mn steel is not obvious and can be neglected, which is favorable to the even distribution of martensitic microstructure and mechanical properties. Thirdly, the phenomenon of decarbonization is hardly found on the surface of the warm-stamped medium-Mn steel, and the ultra-fine-grained microstructure is found inside the medium-Mn steel after warm stamping. Besides, the warm-stamped medium-Mn steel holds the better comprehensive properties, such as a lower yield ratio, higher total elongation and higher tear toughness than the hot-stamped 22MnB5 steel. Furthermore, an actual warm-stamped B-pillar of medium-Mn steel is stamped and ultra-fine-grained martensitic microstructure is obtained. The mechanical properties are evenly distributed. As a result, this paper proves that the warm-stamped medium-Mn steel part can meet the requirements of lightweight and crash safety, and is promising for the industrial production of automotive structural parts.

  17. Comparison of the hot-stamped boron-alloyed steel and the warm-stamped medium-Mn steel on microstructure and mechanical properties

    Energy Technology Data Exchange (ETDEWEB)

    Li, Xiaodong [School of Automotive Engineering, State Key Lab of Structural Analysis for Industrial Equipment, Dalian University of Technology, Dalian 116024 (China); Chang, Ying, E-mail: yingc@dlut.edu.cn [School of Automotive Engineering, State Key Lab of Structural Analysis for Industrial Equipment, Dalian University of Technology, Dalian 116024 (China); Wang, Cunyu [East China Branch of Central Iron & Steel Research Institute (CISRI), Beijing 100081 (China); Hu, Ping [School of Automotive Engineering, State Key Lab of Structural Analysis for Industrial Equipment, Dalian University of Technology, Dalian 116024 (China); Dong, Han [East China Branch of Central Iron & Steel Research Institute (CISRI), Beijing 100081 (China)

    2017-01-02

    The application of high strength steels (HSS) for automotive structural parts is an effective way to realize lightweight and enhance safety. Therefore, improvements in mechanical properties of HSS are needed. In the present study, the warm stamping process of the third generation automotive medium-Mn steel was discussed, the characteristics of martensitic transformation were investigated, as well as the microstructure and mechanical properties were analyzed, compared to the popular hot-stamped 22MnB5 steel in the automotive industry. The results are indicated as follows. Firstly, the quenching rate of the medium-Mn steel can be selected in a wide range based on its CCT curves, which is beneficial to the control of forming process. Secondly, the influence of stamping temperature and pressure on the M{sub s} temperature of the medium-Mn steel is not obvious and can be neglected, which is favorable to the even distribution of martensitic microstructure and mechanical properties. Thirdly, the phenomenon of decarbonization is hardly found on the surface of the warm-stamped medium-Mn steel, and the ultra-fine-grained microstructure is found inside the medium-Mn steel after warm stamping. Besides, the warm-stamped medium-Mn steel holds the better comprehensive properties, such as a lower yield ratio, higher total elongation and higher tear toughness than the hot-stamped 22MnB5 steel. Furthermore, an actual warm-stamped B-pillar of medium-Mn steel is stamped and ultra-fine-grained martensitic microstructure is obtained. The mechanical properties are evenly distributed. As a result, this paper proves that the warm-stamped medium-Mn steel part can meet the requirements of lightweight and crash safety, and is promising for the industrial production of automotive structural parts.

  18. Monte Carlo simulation taking account of surface crack effect for stress corrosion cracking in a stainless steel SUS 304

    International Nuclear Information System (INIS)

    Tohgo, Keiichiro; Suzuki, Hiromitsu; Shimamura, Yoshinobu; Nakayama, Guen; Hirano, Takashi

    2008-01-01

    Stress corrosion cracking (SCC) in structural metal materials occurs by initiation and coalescence of micro cracks, subcritical crack propagation and multiple large crack formation or final failure under the combination of materials, stress and corrosive environment. In this paper, a Monte Carlo simulation for the process of SCC has been proposed based on the stochastic properties of micro crack initiation and fracture mechanics concept for crack coalescence and propagation. The emphasis in the model is put on the influence of semi-elliptical surface cracks. Numerical simulations are carried out based on CBB (creviced bent beam) test results of a sensitized stainless steel SUS 304 and the influence of micro crack initiation rate and coalescence condition on the simulation results is discussed. The numerical examples indicate the applicability of the present model to a prediction of the SCC behavior in real structures. (author)

  19. Experimental study on the shrinkage properties and cracking potential of high strength concrete containing industrial by-products for nuclear power plant concrete

    International Nuclear Information System (INIS)

    KIm, Baek Joong; Yi, Chong Ku

    2017-01-01

    In Korea, attempts have been made to develop high strength concrete for the safety and design life improvement of nuclear power plants. In this study, the cracking potentials of nuclear power plant-high strength concretes (NPP-HSCs) containing industrial by-products with W/B 0.34 and W/B 0.28, which are being reviewed for their application in the construction of containment structures, were evaluated through autogenous shrinkage, unrestrained drying shrinkage, and restrained drying shrinkage experiments. The cracking potentials of the NPP-HSCs with W/B 0.34 and W/B 0.28 were in the order of 0.34FA25 > 0.34FA25BFS25 > 0.34BFS50 > 0.34BFS65SF5 and 0.28FA25SF5 >> 0.28BFS65SF5 > 0.28BFS45SF5 > 0.28 FA20BFS25SF5, respectively. The cracking potentials of the seven mix proportions excluding 0.28FA25SF5 were lower than that of the existing nuclear power plant concrete; thus, the durability of a nuclear power plant against shrinkage cracking could be improved by applying the seven mix proportions with low cracking potentials

  20. Experimental study on the shrinkage properties and cracking potential of high strength concrete containing industrial by-products for nuclear power plant concrete

    Energy Technology Data Exchange (ETDEWEB)

    KIm, Baek Joong; Yi, Chong Ku [School of Civil, Environmental and Architectural Engineering, Korea University, Seoul (Korea, Republic of)

    2017-02-15

    In Korea, attempts have been made to develop high strength concrete for the safety and design life improvement of nuclear power plants. In this study, the cracking potentials of nuclear power plant-high strength concretes (NPP-HSCs) containing industrial by-products with W/B 0.34 and W/B 0.28, which are being reviewed for their application in the construction of containment structures, were evaluated through autogenous shrinkage, unrestrained drying shrinkage, and restrained drying shrinkage experiments. The cracking potentials of the NPP-HSCs with W/B 0.34 and W/B 0.28 were in the order of 0.34FA25 > 0.34FA25BFS25 > 0.34BFS50 > 0.34BFS65SF5 and 0.28FA25SF5 >> 0.28BFS65SF5 > 0.28BFS45SF5 > 0.28 FA20BFS25SF5, respectively. The cracking potentials of the seven mix proportions excluding 0.28FA25SF5 were lower than that of the existing nuclear power plant concrete; thus, the durability of a nuclear power plant against shrinkage cracking could be improved by applying the seven mix proportions with low cracking potentials.

  1. Exploring the spatial variation in quality-adjusted rental prices and identifying hot spots in Berlin’s residential property market

    DEFF Research Database (Denmark)

    Meulen, Philipp an de; Mitze, Timo Friedel

    2014-01-01

    In this work, we use residual values obtained from an estimated hedonic pricing model to assess the role of district-level neighbourhood effects for the spatial variation in quality-adjusted rental prices in Berlin between 2008 and 2013. By doing so, we also aim at identifying hot and cold spots ...... analysis (ESDA) toolbox, we finally pinpoint particular hot spots of the city’s residential property market associated with a significant spatial clustering of similar rental price values around individual observations....... proximity to the city centre compared to similar properties in Berlin’s periphery once we control for the properties’ physical characteristics. The observed temporal evolution of the rental price distribution between 2008 and 2013 thereby hints at an ongoing gentrification process in Germany’s capital...... associated with the current housing market boom. This visual impression is also confirmed by the application of quantile regressions for a correlation analysis between quality-adjusted rental price values and Berlin district-level characteristics obtained from the last census in 2011. Among other factors, we...

  2. Effects of Hot-Hydrostatic Canned Extrusion on the Stock Utilization, Microstructure and Mechanical Properties of TiBw/TC4 Composites with Quasi-Continuous Network.

    Science.gov (United States)

    Feng, Yangju; Li, Bing; Cui, Guorong; Zhang, Wencong

    2017-10-25

    In-situ TiB whisker-reinforced Ti-6Al-4V (TC4) titanium matrix composites (TiBw/TC4) with quasi-continuous networks were successfully fabricated by vacuum hot-pressing sintering. The effects of the hot-hydrostatic canned extrusion on stock utilization, microstructure and mechanical properties of the TiBw/TC4 composites were investigated. It was satisfactory that the utilization of composites could be obviously improved by canned extrusion compared to that extruded without canned extrusion. The microstructure results showed that after canned extrusion the grain was refined and the TiB whiskers were distributed from a random array state to a state in which the whiskers were distributed along the extrusion direction. The properties testing results revealed that the tensile strength, the hardness and the ductility of the composites all significantly improved after extrusion due to the grain refinement and orientation of the TiB whisker caused by extrusion. Tensile fracture results showed that when the TiB whiskers were randomly distributed only part of them played a role in strengthening the matrix during the deformation process (as-sintered composites), while when the TiB whiskers were oriented all whiskers could strengthen the matrix during the tensile testing process (as-extruded composites).

  3. Microstructure and mechanical properties of Ti–22Al–25Nb alloy fabricated by vacuum hot pressing sintering

    Energy Technology Data Exchange (ETDEWEB)

    Jia, Jianbo, E-mail: jiajianbohit@163.com [National Key Laboratory for Precision Hot Processing of Metals, Harbin Institute of Technology, Harbin 150001 (China); School of Mechanical Engineering, Beihua University, Jilin 132021 (China); Zhang, Kaifeng; Jiang, Shaosong [National Key Laboratory for Precision Hot Processing of Metals, Harbin Institute of Technology, Harbin 150001 (China)

    2014-10-20

    A study has been undertaken to verify the feasibility of using a powder metallurgy (P/M) approach to fabricate Ti–22Al–25Nb alloys. Pre-alloyed powders with a nominal composition of Ti–22Al–25Nb (at%) obtained by argon atomization were sieved to the spherical size less than 180 μm and used for the fabrication of P/M Ti–22Al–25Nb alloys via hot pressing in vacuum. Vacuum hot pressing sintering was carried out in a temperature range of 950–1200 °C with a pressure of 35 MPa for 1 h followed by furnace cooling. Microstructure and phase composition examinations of the as-atomized powders and hot pressed (HP'ed) samples were conducted by applying optical microscopy, back-scatter electron imaging and X-ray diffraction analysis. Tensile tests were studied at room temperature and 650 °C, respectively. The results showed that all HP'ed samples were composed of coarse equiaxed B2 grains, fine lamellar O phase inside the B2 grains, and some α{sub 2} along B2 grain boundaries. The elongations of HP'ed samples were less than 3.95%, indicating the bad ductility at room temperature. However, the elongations were improved as the tensile temperature increased to 650 °C. The sample sintered at 1050 °C exhibited a better ductility with the elongation of 7.97% at 650 °C than that of other samples.

  4. Effect of rapid solidification on the microstructure and mechanical properties of hot-pressed Al-20Si-5Fe alloys

    International Nuclear Information System (INIS)

    Rajabi, M.; Vahidi, M.; Simchi, A.; Davami, P.

    2009-01-01

    The aim of this work is to study the effect of cooling rate and subsequent hot consolidation on the microstructural features and mechanical strength of Al-20Si-5Fe-2X (X = Cu, Ni and Cr) alloys. Powder and ribbons were produced by gas atomization and melt spinning processes at two different cooling rates of 1 x 10 5 K/s and 5 x 10 7 K/s. The microstructure of the products was examined using optical microscopy, scanning electron microscopy, transmission electron microscopy, and X-ray diffraction. The particles were consolidated by hot pressing at 400 deg. C/250 MPa/1 h under a high purity argon atmosphere and the microstructure, hardness and compressive strength of the compacts were evaluated. Results showed a profound effect of the cooling rate, consolidation stage, and transition metals on the microstructure and mechanical strength of Al-20Si-5Fe alloys. While microstructural refining was obtained at both cooling rates, the microstructure of the atomized powder exhibited the formation of fine primary silicon (∼ 1 μm), eutectic Al-Si phase with eutectic spacing of ∼ 300 nm, and δ-iron intermetallic. Supersaturated Al matrix containing 5-7 at.% silicon and nanometric Si precipitates (20-40 nm) were determined in the microstructure of the melt-spun ribbons. The hot consolidation resulted in coarsening of Si particles in the atomized particles, and precipitation of Si and Fe-containing intermetallics from the supersaturated Al matrix in the ribbons. The consolidated ribbons exhibited higher mechanical strength compared to the atomized powders, particularly at elevated temperatures. The positive influence of the transition metals on the thermal stability of the Al-20Si-5Fe alloy was noticed, particularly in the Ni-containing alloy.

  5. HOT 2010

    DEFF Research Database (Denmark)

    Lund, Henriette Romme

    En undersøgelse af, hvad der er hot - og burde være hot på læseområdet. I undersøgelsen deltager en række læsekyndige fra praksisfeltet, professionshøjskolerne og forskningsområdet. Undersøgelsen er gentaget hvert år siden 2010.......En undersøgelse af, hvad der er hot - og burde være hot på læseområdet. I undersøgelsen deltager en række læsekyndige fra praksisfeltet, professionshøjskolerne og forskningsområdet. Undersøgelsen er gentaget hvert år siden 2010....

  6. HOT 2013

    DEFF Research Database (Denmark)

    Lund, Henriette Romme

    En undersøgelse af, hvad der er hot - og burde være hot på læseområdet. I undersøgelsen deltager en række læsekyndige fra praksisfeltet, professionshøjskolerne og forskningsområdet. Undersøgelsen er gentaget hvert år siden 2010.......En undersøgelse af, hvad der er hot - og burde være hot på læseområdet. I undersøgelsen deltager en række læsekyndige fra praksisfeltet, professionshøjskolerne og forskningsområdet. Undersøgelsen er gentaget hvert år siden 2010....

  7. Thermoelectric properties of Bi2Te3-Bi2Se3 solid solutions prepared by attrition milling and hot pressing

    International Nuclear Information System (INIS)

    Lee, Go-Eun; Kim, Il-Ho; Choi, Soon-Mok; Lim, Young-Soo; Seo, Won-Seon; Park, Jae-Soung; Yang, Seung-Ho

    2014-01-01

    Bi 2 Te 3-y Se y (y = 0.15 - 0.6) solid solutions were prepared by attrition milling and hot pressing. The lattice constants decreased with increasing Se content, indicating that the Se atoms were successfully substituted into the Te sites. All specimens exhibited n-type conduction, and their electrical resistivities increased slightly with increasing temperature. With increasing Se content, the Seebeck coefficients increased while the thermal conductivity decreased due to the increase in phonon scattering. The maximum figure of merit obtained was 0.63 at 440 K for the undoped Bi 2 Te 2.4 Se 0.6 solid solution.

  8. Effects of Deep Cryogenic Treatment on the Wear Resistance and Mechanical Properties of AISI H13 Hot-Work Tool Steel

    Science.gov (United States)

    Çiçek, Adem; Kara, Fuat; Kıvak, Turgay; Ekici, Ergün; Uygur, İlyas

    2015-11-01

    In this study, a number of wear and tensile tests were performed to elucidate the effects of deep cryogenic treatment on the wear behavior and mechanical properties (hardness and tensile strength) of AISI H13 tool steel. In accordance with this purpose, three different heat treatments (conventional heat treatment (CHT), deep cryogenic treatment (DCT), and deep cryogenic treatment and tempering (DCTT)) were applied to tool steel samples. DCT and DCTT samples were held in nitrogen gas at -145 °C for 24 h. Wear tests were conducted on a dry pin-on-disk device using two loads of 60 and 80 N, two sliding velocities of 0.8 and 1 m/s, and a wear distance of 1000 m. All test results showed that DCT improved the adhesive wear resistance and mechanical properties of AISI H13 steel. The formation of small-sized and uniformly distributed carbide particles and the transformation of retained austenite to martensite played an important role in the improvements in the wear resistance and mechanical properties. After cleavage fracture, the surfaces of all samples were characterized by the cracking of primary carbides, while the DCT and DCTT samples displayed microvoid formation by decohesion of the fine carbides precipitated during the cryo-tempering process.

  9. Investigation of Helicopter Longeron Cracks

    Science.gov (United States)

    Newman, John A.; Baughman, James; Wallace, Terryl A.

    2009-01-01

    Four cracked longerons, containing a total of eight cracks, were provided for study. Cracked regions were cut from the longerons. Load was applied to open the cracks, enabling crack surface examination. Examination revealed that crack propagation was driven by fatigue loading in all eight cases. Fatigue crack initiation appears to have occurred on the top edge of the longerons near geometric changes that affect component bending stiffness. Additionally, metallurgical analysis has revealed a local depletion in alloying elements in the crack initiation regions that may be a contributing factor. Fatigue crack propagation appeared to be initially driven by opening-mode loading, but at a crack length of approximately 0.5 inches (12.7 mm), there is evidence of mixed-mode crack loading. For the longest cracks studied, shear-mode displacements destroyed crack-surface features of interest over significant portions of the crack surfaces.

  10. Crack detecting method

    International Nuclear Information System (INIS)

    Narita, Michiko; Aida, Shigekazu

    1998-01-01

    A penetration liquid or a slow drying penetration liquid prepared by mixing a penetration liquid and a slow drying liquid is filled to the inside of an artificial crack formed to a member to be detected such as of boiler power generation facilities and nuclear power facilities. A developing liquid is applied to the periphery of the artificial crack on the surface of a member to be detected. As the slow-drying liquid, an oil having a viscosity of 56 is preferably used. Loads are applied repeatedly to the member to be detected, and when a crack is caused to the artificial crack, the permeation liquid penetrates into the crack. The penetration liquid penetrated into the crack is developed by the developing liquid previously coated to the periphery of the artificial crack of the surface of the member to be detected. When a crack is caused, since the crack is developed clearly even if it is a small opening, the crack can be recognized visually reliably. (I.N.)

  11. Cracking susceptibility of aluminum alloys during laser welding

    Directory of Open Access Journals (Sweden)

    Lara Abbaschian

    2003-06-01

    Full Text Available The influence of laser parameters in welding aluminum alloys was studied in order to reduce hot cracking. The extension of cracks at the welding surface was used as a cracking susceptibility (CS index. It has been shown that the CS changes with changing welding velocity for binary Al-Cu alloys. In general, the CS index increased until a maximum velocity and then dropped to zero, generating a typical lambda-curve. This curve is due to two different mechanisms: 1 the refinement of porosities with increasing velocity and 2 the changes in the liquid fraction due to decreasing microsegregation with increasing velocities.

  12. Stress-corrosion cracking properties of candidate fuel cladding alloys for the Canadian SCWR: a summary of literature data and recent test results

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, W.; Zeng, Y., E-mail: Wenyue@NRcan.gc.ca [CanmetMATERIALS, Hamilton, ON (Canada); Luo, J. [Univ. of Alberta, Edmonton, AB (Canada); Novotny, R. [JRC-European Commission, Patten (Netherlands); Li, J.; Amirkhiz, B.S., E-mail: Jian.li@nrcan.gc.ca [CanmetMATERIALS, Hamilton, ON (Canada); Guzonas, D. [Atomic Energy of Canada Limited, Chalk River, ON (Canada); Matchim, M.; Collier, J.; Yang, L., E-mail: lin.yang@nrcan.gc.ca [CanmetMATERIALS, Hamilton, ON (Canada)

    2014-07-01

    Cracking of fuel claddings is a serious concern when selecting candidate alloys for the development of a next-generation reactor. Whether the cracking is due to an environment-metal interaction such as stress-corrosion, or a pure metallurgical process such as localized plastic deformation along grain boundaries, the final impact is the same: cracking of the cladding can lead to fuel failure. In the course of a review of potential candidate alloys in preparation for further assessment under conditions relevant to the Canadian SCWR concept, relevant cracking studies reported for five short-listed alloys (namely 310S, 347H, 800H, 625 and 214) in the open literature were examined, and the key findings are provided in this paper. Discussions are also made of the recent SCC data from capsule tests and slow-strain rate tests (SSRT) in supercritical water. The data suggest that there is a threshold strain level below which SCC is not developed during SSRT tests. The practical implication of this finding is also discussed. (author)

  13. Ceramic containers for spent nuclear fuel. II. Reactions between TiO2 and the steel canning during hot isostatic processing

    International Nuclear Information System (INIS)

    Bergman, B.; Forberg, S.

    1984-01-01

    Rutile was selected for some practical studies of processing and properties of ceramic containers. Hot isostatic pressing at 1280 0 C has resulted in reaction zones between the TiO 2 powder and the steel canning. The phases ilmenite, pseudobrookite, rutile, and iron have been identified by x-ray diffraction and by microprobe analysis. The microstructures have been interpreted by classical metallographic methods, and some microstructures obtained by hot pressing and rapid cooling have also been examined for purposes of comparison. Some implications of the microstructures have been discussed in terms of microcracking and slow crack growth. 13 refs., 7 figs

  14. Curvilinear crack layer propagation

    Science.gov (United States)

    Chudnovsky, Alexander; Chaoui, Kamel; Moet, Abdelsamie

    1987-01-01

    An account is given of an experiment designed to allow observation of the effect of damage orientation on the direction of crack growth in the case of crack layer propagation, using polystyrene as the model material. The direction of crack advance under a given loading condition is noted to be determined by a competition between the tendency of the crack to maintain its current direction and the tendency to follow the orientation of the crazes at its tip. The orientation of the crazes is, on the other hand, determined by the stress field due to the interaction of the crack, the crazes, and the hole. The changes in craze rotation relative to the crack define the active zone rotation.

  15. Microstructure and property evolution of isotropic and anisotropic NdFeB magnets fabricated from nanocrystalline ribbons by spark plasma sintering and hot deformation

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Z W; Huang, H Y; Yu, H Y; Zhong, X C; Zeng, D C [School of Materials Science and Engineering, South China University of Technology, Guangzhou 510640 (China); Gao, X X; Zhu, J, E-mail: zwliu@scut.edu.cn [State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083 (China)

    2011-01-19

    Isotropic and anisotropic NdFeB magnets were synthesized by spark plasma sintering (SPS) and SPS+HD (hot deformation), respectively, using melt-spun ribbons as the starting materials. Spark plasma sintered magnets sintered at low temperatures (<700 {sup 0}C) almost maintained the uniform fine grain structure inherited from rapid quenching. At higher temperatures, due to the local high-temperature field caused by the spark plasma discharge, the grain growth occurred at the initial particle surfaces and the coarse grain zones formed in the vicinity of the particle boundaries. Since the interior of the particles maintained the fine grain structure, a distinct two-zone structure was formed in the spark plasma sintered magnets. The SPS temperature and pressure have important effects on the widths of coarse and fine grain zones, as well as the grain sizes in two zones. The changes in grain structure led to variations in the magnetic properties. By employing low SPS temperature and high pressure, high-density magnets with negligible coarse grain zone and an excellent combination of magnetic properties can be obtained. An anisotropic magnet with a maximum energy product of {approx}30 MG Oe was produced by the SPS+HD process. HD at 750 {sup 0}C did not lead to obvious grain growth and the two-zone structure still existed in the hot deformed magnets. Intergranular exchange coupling was demonstrated in the spark plasma sintered magnets and was enhanced by the HD process, which reduced the coercivity. Good temperature stability was manifested by low temperature coefficients of remanence and coercivity. The results indicated that nanocrystalline NdFeB magnets without significant grain growth and with excellent properties could be obtained by SPS and HD processes.

  16. Structural Properties of Zn-ZnO Core-Shell Microspheres Grown by Hot-Filament CVD Technique

    Directory of Open Access Journals (Sweden)

    R. López

    2012-01-01

    Full Text Available We report the hot-filament chemical vapor deposition (HFCVD growth of Zn-ZnO core-shell microspheres in the temperature range of 350–650°C only using ZnO pellets as raw material. The samples were characterized by scanning electron microscope (SEM, energy dispersive spectroscopy (EDS, and X-ray diffraction (XRD techniques. SEM micrographs showed the presence of solid microspheres and a Zn-ZnO layer in all samples. The observed heterogeneous morphology on each sample suggested two different growth mechanisms. On the one hand, solid microspheres were formed by means of gas phase nucleation of Zn atoms. The Zn-ZnO layer was formed on the substrate as result of surface reactions. It is possible that Zn microspheres condensed during the natural cooling of the HFCVD reactor as they were observed on the Zn-ZnO layer.

  17. A supramolecular structure insight for conversion property of cellulose in hot compressed water: Polymorphs and hydrogen bonds changes.

    Science.gov (United States)

    Wang, Yan; Lian, Jie; Wan, Jinquan; Ma, Yongwen; Zhang, Yingshi

    2015-11-20

    Waste paper samples with different cellulose supramolecular structure were treated in hot compressed water (HCW) at 375°C and 22.5MPa within 200s to evaluate the specific effect mechanism of cellulose supramolecular structure on the conversion of waste paper to reusable resource. Although the distribution of liquid products and the oligosaccharides were related to reaction time, depolymerization and decrystallization of the cellulose, the characteristics absorption peak of cellulose from FTIR analysis and crystal structure of the cellulose detected in the residues with hydrolysis rate up 96.5% indicated crystal structure was the dominant factor that affect conversion behavior of waste paper. The conversion of cellulose Iβ to cellulose Iα or cellulose I(α+β) in HCW demonstrated that the recrystallization occurred during the decrystallization of cellulose through the rearrangement of hydrogen bonds. Copyright © 2015 Elsevier Ltd. All rights reserved.

  18. Probing properties of hot and dense QCD matter with heavy flavor in the PHENIX experiment at RHIC

    Directory of Open Access Journals (Sweden)

    Nouicer Rachid

    2015-01-01

    Full Text Available Hadrons carrying heavy quarks, i.e. charm or bottom, are important probes of the hot and dense medium created in relativistic heavy ion collisions. Heavy quarkantiquark pairs are mainly produced in initial hard scattering processes of partons. While some of the produced pairs form bound quarkonia, the vast majority hadronize into particles carrying open heavy flavor. Heavy quark production has been studied by the PHENIX experiment at RHIC via measurements of single leptons from semi-leptonic decays in both the electron channel at mid-rapidity and in the muon channel at forward rapidity. A large suppression and azimuthal anisotropy of single electrons have been observed in Au + Au collisions at 200 GeV. These results suggest a large energy loss and flow of heavy quarks in the hot, dense matter. The PHENIX experiment has also measured J/ψ production at 200 GeV in p + p, d + Au, Cu + Cu and Au + Au collisions, both at mid- and forward-rapidities, and additionally Cu + Au and U + U at forward-rapidities. In the most energetic collisions, more suppression is observed at forward rapidity than at central rapidity. This can be interpreted either as a sign of quark recombination, or as a hint of additional cold nuclear matter effects. The centrality dependence of nuclear modification factor, RAA(pT, for J/ψ in U + U collisions at √sNN = 193 GeV shows a similar trend to the lighter systems, Au + Au and Cu + Cu, at similar energy 200 GeV.

  19. Vibration Analysis of Cracked Composite Bending-torsion Beams for Damage Diagnosis

    OpenAIRE

    Wang, Kaihong

    2004-01-01

    An analytical model of cracked composite beams vibrating in coupled bending-torsion is developed. The beam is made of fiber-reinforced composite with fiber angles in each ply aligned in the same direction. The crack is assumed open. The local flexibility concept is implemented to model the open crack and the associated compliance matrix is derived. The crack introduces additional boundary conditions at the crack location and these effects in conjunction with those of material properties are i...

  20. Fatigue crack paths under the influence of changes in stiffness

    Directory of Open Access Journals (Sweden)

    G. Kullmer

    2016-02-01

    Full Text Available An important topic of the Collaborative Research Centre TRR 30 of the Deutsche Forschungsgemeinschaft (DFG is the crack growth behaviour in graded materials. In addition, the growth of cracks in the neighbourhood of regions and through regions with different material properties belongs under this topic. Due to the different material properties, regions with differing stiffness compared to the base material may arise. Regions with differing stiffness also arise from ribs, grooves or boreholes. Since secure findings on the propagation behaviour of fatigue cracks are essential for the evaluation of the safety of components and structures, the growth of cracks near changes in stiffness has to be considered, too. Depending on the way a crack penetrates the zone of influence of such a change in stiffness and depending on whether this region is more compliant or stiffer than the surrounding area the crack may grow towards or away from this region. Both cases result in curved crack paths that cannot be explained only by the global loading situation. To evaluate the influence of regions with differing stiffness on the path of fatigue cracks the paths and the stress intensity factors of cracks growing near and through regions with differing stiffness are numerically determined with the program system ADAPCRACK3D. Therefore, arrangements of changes in stiffness modelled as material inclusions with stiffness properties different from the base material or modelled as ribs and grooves are systematically varied to develop basic conclusions about the crack growth behaviour near and through changes in stiffness.

  1. Influence of Fiber Content on Mechanical and Morphological Properties of Woven Kenaf Reinforced PVB Film Produced Using a Hot Press Technique

    Directory of Open Access Journals (Sweden)

    Suhad D. Salman

    2016-01-01

    Full Text Available This work addresses the results of experimental investigation carried out on mechanical and morphological properties of plain woven kenaf fiber reinforced PVB film which was prepared by hot press technique. The composites were prepared with various fiber contents: 0%, 10%, 20%, 30%, 40%, 50%, and 60% (by weight, with the processing parameters 165°C, 20 min, and at a pressure of 8 MPa applied on the material. Tensile, flexural, and Charpy impact properties were studied as well as morphological properties of impact fracture surface. With the increase in kenaf fibers content up to 40%, the PVB composites have shown lower tensile and flexural strength accompanied with reduction in the ultimate strain of the composite. The results showed that impact properties were affected in markedly different ways by using various kenaf contents and decrease with the increase in kenaf fiber content up to 40%; however, high impact strength was observed even with 40% kenaf fiber content. Furthermore, scanning electron microscopy for impact samples was utilised to demonstrate the different failures in the fracture surfaces for various kenaf fibers contents.

  2. Microstructure and Mechanical Properties of Multiphase Strengthened Al/Si/Al_2O_3/SiO_2/MWCNTs Nano composites Sintered by In Situ Vacuum Hot Pressing

    International Nuclear Information System (INIS)

    Li, J.; Jiang, X.; Zhu, D.; Zhu, M.; Shao, Z.; Johnson, S.; Luo, Z.

    2015-01-01

    Eutectic Al/Si binary alloy is technically one of the most important Al casting alloys due to its high corrosion resistance, evident shrinkage reduction, low thermal expansion coefficient, high fluidity, and good weldability. In this work, multi phased Al/Si matrix nano composites reinforced with Al_2O_3 and multi walled carbon nano tubes (MWCNTs) have been sintered by an in situ vacuum hot-pressing method. The alumina Al_2O_3 nanoparticles were introduced by an in situ reaction of Al with SiO_2. Microstructure and mechanical properties of the sintered Al/Si/Al_2O_3/SiO_2/MWCNTs nano composites with different alumina contents were investigated. The mechanical properties were determined by micro-Vickers hardness and compressive and shear strength tests. The results demonstrated that in situ alumina and MWCNTs had impacts on microstructure and mechanical properties of the nano composites. Based on the mechanical properties and microstructure of the nano composites, strengthening and fracture mechanisms by multiple reinforcements were analyzed

  3. The microstructures and mechanical properties of Al-15Si-2.5Cu-0.5Mg/(wt%)B{sub 4}C composites produced through hot pressing technique and subjected to hot extrusion

    Energy Technology Data Exchange (ETDEWEB)

    Ozer, Alpay, E-mail: alpiozer@gmail.com

    2016-11-01

    In this study, B{sub 4}C (5, 10, and 15 wt%) particle-reinforced Ecka Alumix 231{sup ®} aluminum matrix composites were produced through the hot pressing technique. Some of these samples were subjected to hot extrusion as a secondary treatment at 4:1 ratio at a temperature of 555 °C. The obtained samples were subjected to density measurement, hardness test, microstructure analysis, and three-point bending test, and their fracture surfaces were examined. A density of over 99% was found in the samples. Al-rich solid solution and primary Si, CuAl{sub 2}, Al{sub 2}CuMg, and Mg{sub 2}Si phases in the microstructure were determined through X-ray diffraction analysis. Grain sizes were found to be 20 μm and 2 μm in the microstructures of the samples produced through hot pressing technique and of those subjected to additional hot extrusion, respectively. High hardness values were obtained in the samples subjected to hot extrusion. In these samples, wt% B{sub 4}C particle ratio and transverse rupture strength increased considerably. Furthermore, the highest compressive strain value was obtained in the 10 wt% B{sub 4}C particle-reinforced composites subjected to hot extrusion. - Highlights: • Liquid phase formed at the temperature of hot pressing and hot extrusion. • In the samples, over 99.19% density was obtained. • Average matrix grain size was measured to be 2 μm through hot extrusion. • As wt% B{sub 4}C ratio increased, transverse rupture strength values increased. • High compressive strain values were obtained in the hot extrusion samples.

  4. Multifragmentation of hot nuclei

    International Nuclear Information System (INIS)

    Tamain, B.

    1990-10-01

    It is difficult to deposit a large amount (∼ 1 Gev) of excitation energy into a nucleus. And if one wants to deposit large excitation energy values, the best way consists of shooting a given target nucleus with several nucleons, which can be achieved by using intermediate energy (10-100 MeV/nucleon) heavy ions. Such very excited objects were named hot nuclei. The study of hot nuclei has been undertaken only for 7 years because intermediate energy heavy ion facilities were not available before. The game is then to determine the decay properties of such nuclei, their limits of existence. Their study is connected with general properties of nuclear matter: namely its equation of state. Of special interest, is the onset of a new decay mechanism: multifragmentation, which is the non-sequential disassembly of a hot nucleus into several light nuclei (often called intermediate-mass fragments or IMF) or particles. This paper, shows how this mechanism can reflect fundamental properties of nuclear matter, but also how its experimental signature is difficult to establish. Multifragmentation has also been studied by using very energetic projectiles (protons and heavy ions) in the relativistic or ultra-relativistic region. The multifragmentation question of hot nuclei is far from being solved. One knows that IMF production increases when the excitation energy brought into a system is strongly increased, but very little is known about the mechanisms involved and a clear onset for multifragmentation is not established

  5. Microstructure development and mechanical properties of quenching and partitioning (Q and P) steel and an incorporation of hot-dipping galvanization during Q and P process

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Jing; Yu, Hao, E-mail: yhzhmr@126.com

    2013-12-01

    The “quenching and partitioning” (Q and P) process has recently been substantiated to be a unique technological route for the production of high strength steels with significant amounts of retained austenite, and thus to provide better combination of strength and ductility. In this work, intercritically annealed specimens followed by Q and P treatment have been applied to low-carbon steel with chemical composition typical for conventional TRIP-assisted steels. Microstructure of the steel treated by the Q and P process was characterized by means of optical microscope, SEM, TEM and XRD. The study suggests that microstructure is mainly composed of ferrite, lath martensite, martensite–austenite islands, retained austenite and a small amount of bainite formed during partitioning. The fraction of bainite formed during partitioning is proportional to quenching temperature. The mechanical property of specimen treated by the Q and P process exhibits an improved combination of strength and ductility than that of the Q and T process. Two schemes of hot-dipping galvanization processes were designed. The results indicate that both hot-dip galvanizing schemes present a limited reduction in tensile strength and a slight enhancement of ductility. The scheme of galvanizing and partitioning after the quenching progress shows a better combination of strength and ductility.

  6. Dynamic thermo-chemo-mechanical strain of Zircaloy-4 slotted rings for evaluating strategies that mitigate stress corrosion cracking

    Energy Technology Data Exchange (ETDEWEB)

    Ferrier, G.A.; Metzler, J.; Farahani, M.; Chan, P.K.; Corcoran, E.C. [Royal Military College of Canada, Kingston, ON (Canada)

    2014-07-01

    Stress corrosion cracking (SCC) in Zircaloy-4 fuel sheaths has been investigated by static loading of slotted ring samples under hot and corrosive conditions. However, in nuclear reactors, power ramps can have short (e.g., 10-20 minutes) and recurring time frames due to dynamic processes such as on-power refuelling, adjuster rod manoeuvres, and load following. Therefore, to enable out-reactor dynamic testing, an apparatus was designed to dynamically strain slotted ring samples under SCC conditions. This apparatus can additionally be used to test fatigue properties. Unique capabilities of this apparatus and preliminary results obtained from static and dynamic tests are presented. (author)

  7. Effect of Cooling Rate on the Microstructure and Mechanical Properties of C-Mn-Al-Si-Nb Hot-Rolled TRIP Steels

    Science.gov (United States)

    Fu, B.; Y Lu, M.; Y Yang, W.; Li, L. F.; Y Zhao, Z.

    2017-12-01

    A novel thermomechanical process to manufacture hot-rolled TRIP steels has been proposed based on dynamic transformation of undercooled austenite (DTUA). The cooling rate between DTUA and isothermal bainitic treatment in the novel process is important. In the present study, effect of this cooling rate on the final microstructures and mechanical properties of a C-Mn-Al-Si-Nb TRIP steel was investigated. The results showed that the volume fractions of acicular ferrite and retained austenite were increased with the increment of cooling rate. As a consequence, higher yield strength and larger total elongation were obtained for the investigated steel with higher cooling rate. In addition, a value of 30.24 GPa% for the product of tensile strength and total elongation was acquired when the cooling rate was 25 K/s. This value has met the standard of the “Third Generation” of advanced high strength sheet steels.

  8. Thermoelectric properties of I-doped n-type Bi2Te3-based material prepared by hydrothermal and subsequent hot pressing

    Directory of Open Access Journals (Sweden)

    Fang Wu

    2017-04-01

    Full Text Available I-doped Bi2Te3−xIx (x=0, 0.05, 0.1, 0.2 flower-like nanoparticles were synthesized by a hydrothermal method through a careful adjustment of the amount of ethylenediamine tetraacetic acid surfactant. The nanopowders of flower-like nanoparticles were hot-pressed into bulk pellets and the thermoelectric properties of the pellets were investigated. The results showed that I-doping decreased the electrical resistivity effectively, and the thermal conductivitives of the Bi2Te3−xIx bulk samples was lower because of the closer atomic mass of I compared to Te. As a result, a ZT value of 1.1 was attained at 448 K for the Bi2Te2.9I0.1 sample.

  9. Research on the Microstructures and Mechanical Properties of Ti Micro-Alloyed Cold Rolled Hot-Dip Galvanizing DP980 Steel

    Science.gov (United States)

    Han, Yun; Kuang, Shuang; Qi, Xiumei; Xie, Chunqian; Liu, Guanghui

    Effects of galvanizing simulation parameters on microstructures and mechanical properties of Ti-microalloyed cold rolled hot-dip galvanizing DP980 steel were investigated in this study by optical microscopy (OM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS) and tensile test. Moreover, the precipitation behavior of Ti in the experimental steel was also studied. The results show that, as the heating temperature increases, the tensile strength of experimental galvanizing DP980 steel decreases while the yield ratio and elongation of the steel are enhanced. The microstructures of experimental steels exhibit typical dual phase steel character and the volume fractions of MA islands are almost 30%. In addition, lots of nano-sized TiC precipitates can be found in the ferrite grains.

  10. Microstructure and mechanical properties of 2.5 vol. % TiBw/Ti6Al4V composites plates fabricated by hot-hydrostatic canned extrusion

    Science.gov (United States)

    Zhang, Wencong; Zhang, Lingjia; Feng, Yangju; Cui, Guorong; Chen, Wenzhen

    2018-04-01

    Plates of 2.5 vol. % TiB whisker-reinforced Ti6Al4V titanium matrix composites (TiBw/Ti64) with network structure were successfully fabricated by hot-hydrostatic extrusion with steel cup at 1100 °C. The dimensions of plates were about 150mm in length, 27mm in width and 2mm in thickness. After extrusion, the original equiaxed-network structure formed by TiB whiskers still existed, but was compressed in cross-section and stretched in longitudinal section and then the TiB whiskers were directional distribution along the extrusion direction. Furthermore, the mechanical properties results showed that the strength, hardness and ductility of the plates were significantly improved compared to as-sintered composites.

  11. I. The properties of hot Ca-like fragments from the 40Ca+40Ca reaction at 35 AMeV

    International Nuclear Information System (INIS)

    Planeta, R.; Gawlikowicz, W.; Wieloch, A.

    2001-01-01

    The creation of hot Ca-like fragments was investigated in the 40 Ca + 40 Ca reaction at 35 AMeV. Using the AMPHORA 4π detector system, the primary projectile-like fragment was reconstructed and its properties were determined. Both primary and secondary distributions are compared with the predictions of a Monte Carlo code describing a heavy-ion collision as a two-step process. Some of the nucleons which are identified as participants in the first step are transferred in the second step to these final states, which correspond on the average to the maximum value of entropy (thermodynamic probability). The model allows for competition between mean-field effects and nucleon-nucleon interactions in the overlap zone of the interacting nuclei. The analysis presented here suggests a thermalized source picture of the decay of the projectile-like fragment. The validity of the reconstruction procedure for projectile-like fragments is discussed. (orig.)

  12. [Experimental study on two-way application of traditional Chinese medicines capable of promoting blood circulation and removing blood stasis with neutral property in cold and hot blood stasis syndrome I].

    Science.gov (United States)

    Hao, Er-Wei; Deng, Jia-Gang; Du, Zheng-Cai; Yan, Ke; Zheng, Zuo-Wen; Wang, Qin; Huang, Li-Zhen; Bao, Chuan-Hong; Deng, Xiu-Qiong; Lu, Xiao-Yan; Tang, Zhi-Ling

    2012-11-01

    To study the action characteristics of "two-way application and conditioned dominance" of traditional Chinese medicines with neutral property by observing the action characteristic of 10 traditional Chinese medicines capable of promoting blood circulation and removing blood stasis with neutral property in the microcirculation in rats with heat stagnation and blood stasis syndrome. The rat model with heat stagnation and blood stasis syndrome was established by injecting carrageenan and dry yeast, and the rat model with cold stagnation and blood stasis syndrome was built by the body freezing method. Ten traditional Chinese medicines with neutral property, including 5 with hot property and 5 with cold property, were selected for intervention to observe blood flow rate and flow state indicators in rat auricles and make a comparative analysis on action characteristics of traditional Chinese medicines with neutral property. ANOVA showed that among the 10 traditional Chinese medicines with neutral property, 6 such as Typhae Pollen, Sappan Lignum and Vaccariae Semen can obviously increase the blood flow rate (P traditional Chinese medicines with cold property can increase the blood flow rate (P medicines showed no notable effect; among the 5 traditional Chinese medicines with hot property, Carthamus tinctorius and Ligusticum chuanxiong can increase the blood flow rate (P traditional Chinese medicines with natural and cold properties showed similar effect on heat stagnation and blood stasis syndrome and better effect in increasing blood flow rate than those with hot property; those with natural and hot properties showed similar effect and better effect in increasing blood flow rate than those with cold property. Under the condition of heat stagnation and blood stasis syndrome, traditional Chinese medicines with neutral property have the similar action characteristics with those with cold property; wile under the condition of cold stagnation and blood stasis syndrome

  13. Design Evolutuion of Hot Isotatic Press Cans for NTP Cermet Fuel Fabrication

    Science.gov (United States)

    Mireles, O. R.; Broadway, J.; Hickman, R.

    2014-01-01

    Nuclear Thermal Propulsion (NTP) is under consideration for potential use in deep space exploration missions due to desirable performance properties such as a high specific impulse (> 850 seconds). Tungsten (W)-60vol%UO2 cermet fuel elements are under development, with efforts emphasizing fabrication, performance testing and process optimization to meet NTP service life requirements [1]. Fuel elements incorporate design features that provide redundant protection from crack initiation, crack propagation potentially resulting in hot hydrogen (H2) reduction of UO2 kernels. Fuel erosion and fission product retention barriers include W coated UO2 fuel kernels, W clad internal flow channels and fuel element external W clad resulting in a fully encapsulated fuel element design as shown.

  14. Nonparametric Change Point Diagnosis Method of Concrete Dam Crack Behavior Abnormality

    OpenAIRE

    Li, Zhanchao; Gu, Chongshi; Wu, Zhongru

    2013-01-01

    The study on diagnosis method of concrete crack behavior abnormality has always been a hot spot and difficulty in the safety monitoring field of hydraulic structure. Based on the performance of concrete dam crack behavior abnormality in parametric statistical model and nonparametric statistical model, the internal relation between concrete dam crack behavior abnormality and statistical change point theory is deeply analyzed from the model structure instability of parametric statistical model ...

  15. Effect of intercritical deformation on microstructure and mechanical properties of a low-silicon aluminum-added hot-rolled directly quenched and partitioned steel

    Energy Technology Data Exchange (ETDEWEB)

    Tan, Xiao-Dong, E-mail: tan.x@mpie.de [State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819 (China); Max-Planck-Institut für Eisenforschung GmbH, Max-Planck-Str. 1, 40237 Düsseldorf (Germany); Xu, Yun-Bo, E-mail: yunbo_xu@126.com [State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819 (China); Ponge, Dirk [Max-Planck-Institut für Eisenforschung GmbH, Max-Planck-Str. 1, 40237 Düsseldorf (Germany); Yang, Xiao-Long; Hu, Zhi-Ping; Peng, Fei [State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819 (China); Ju, Xiao-Wei [CERI LONG PRODUCT CO., LTD., Beijing 100176 (China); Wu, Di [State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819 (China); Raabe, Dierk [Max-Planck-Institut für Eisenforschung GmbH, Max-Planck-Str. 1, 40237 Düsseldorf (Germany)

    2016-02-22

    Here, we applied hot-rolling in conjunction with direct quenching and partitioning (HDQ&P) processes with different rolling schedules to a low-C low-Si Al-added steel. Ferrite was introduced into the steel by intercritical rolling and air cooling after hot-rolling. The effect of intercritcal deformation on the microstructure evolution and mechanical properties was investigated. The promotion of austenite stabilization and the optimization of the TRIP effect due to a moderate degree of intercritical deformation were systematically explored. The results show that the addition of 1.46 wt% of Al can effectively promote ferrite formation. An intercritical deformation above 800 °C can result in a pronounced bimodal grain size distribution of ferrite and some elongated ferrite grains containing sub-grains. The residual strain states of both austenite and ferrite and the occurrence of bainite transformation jointly increase the retained austenite fraction due to its mechanical stabilization and the enhanced carbon partitioning into austenite from its surrounding phases. An intercritical deformation below 800 °C can profoundly increase the ferrite fraction and promote the recrystallization of deformed ferrite. The formation of this large fraction of ferrite enhances the carbon enrichment in the untransformed austenite and retards the bainite transformation during the partitioning process and finally enhances martensite transformation and decreases the retained austenite fraction. The efficient TRIP effect of retained austenite and the possible strain partitioning of bainite jointly improve the work hardening and formability of the steel and lead to the excellent mechanical properties with relatively high tensile strength (905 MPa), low yield ratio (0.60) and high total elongation (25.2%).

  16. Effect of two-step intercritical annealing on microstructure and mechanical properties of hot-rolled medium manganese TRIP steel containing δ-ferrite

    International Nuclear Information System (INIS)

    Xu, Yun-bo; Hu, Zhi-ping; Zou, Ying; Tan, Xiao-dong; Han, Ding-ting; Chen, Shu-qing; Ma, De-gang; Misra, R.D.K.

    2017-01-01

    The microstructure-properties relationship, work-hardening behavior and retained austenite stability have been systematically investigated in a hot-rolled medium manganese transformation-induced-plasticity (TRIP) steel containing δ-ferrite subjected to one-step and two-step intercritical annealing. The steel exhibited tensile strength of 752 MPa and total elongation of 52.7% for one-step intercritical annealing at 740 °C, tensile strength of 954 MPa and total elongation of 39.2% in the case of intercritical quenching at 800 °C and annealing at 740 °C. The austenite obtained by two-step annealing mostly consists of refined lath structures and increased fraction of block-type particles existing at various kinds of sites, which is highly distinguished from those characterized by long lath morphology and small amounts of granular shape in one-step annealed samples. In spite of a higher C and Mn content in austenite and finer austenite laths, two-step annealing can lead to an active and continuous TRIP effect provided by a mixed blocky and lath-type austenitic structure with lower stability, contributing to a higher UTS. In contrast, one-step annealing gave rise to a less active but sustained TRIP effect given by the dominant lath-like austenite having higher stability, leading to a very high elongation. The further precipitation of vanadium carbides and the presence of both dislocation substructure and fine equiaxed grain in ferrite matrix facilitate the increase of yield strength after double annealing. - Highlights: • A novel two-step process was applied to a hot-rolled Fe-0.2C-6.5Mn-3Al steel. • The interplay between different microstructures and mechanical properties was studied. • Two-step annealing led to an active and continuous TRIP. • An outstanding combination of strength of 954 MPa and elongation of 39.2% was obtained.

  17. Effect of two-step intercritical annealing on microstructure and mechanical properties of hot-rolled medium manganese TRIP steel containing δ-ferrite

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Yun-bo [State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, People' s Republic China (China); Hu, Zhi-ping, E-mail: huzhiping900401@126.com [State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, People' s Republic China (China); Zou, Ying; Tan, Xiao-dong; Han, Ding-ting; Chen, Shu-qing [State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, People' s Republic China (China); Ma, De-gang [Tangshan Iron and Steel Company, Tangshan 063000, People' s Republic China (China); Misra, R.D.K. [Laboratory for Excellence in Advanced Steel Research, Department of Metallurgical, Materials and Biomedical Engineering, University of Texas at El Paso, TX 79968 (United States)

    2017-03-14

    The microstructure-properties relationship, work-hardening behavior and retained austenite stability have been systematically investigated in a hot-rolled medium manganese transformation-induced-plasticity (TRIP) steel containing δ-ferrite subjected to one-step and two-step intercritical annealing. The steel exhibited tensile strength of 752 MPa and total elongation of 52.7% for one-step intercritical annealing at 740 °C, tensile strength of 954 MPa and total elongation of 39.2% in the case of intercritical quenching at 800 °C and annealing at 740 °C. The austenite obtained by two-step annealing mostly consists of refined lath structures and increased fraction of block-type particles existing at various kinds of sites, which is highly distinguished from those characterized by long lath morphology and small amounts of granular shape in one-step annealed samples. In spite of a higher C and Mn content in austenite and finer austenite laths, two-step annealing can lead to an active and continuous TRIP effect provided by a mixed blocky and lath-type austenitic structure with lower stability, contributing to a higher UTS. In contrast, one-step annealing gave rise to a less active but sustained TRIP effect given by the dominant lath-like austenite having higher stability, leading to a very high elongation. The further precipitation of vanadium carbides and the presence of both dislocation substructure and fine equiaxed grain in ferrite matrix facilitate the increase of yield strength after double annealing. - Highlights: • A novel two-step process was applied to a hot-rolled Fe-0.2C-6.5Mn-3Al steel. • The interplay between different microstructures and mechanical properties was studied. • Two-step annealing led to an active and continuous TRIP. • An outstanding combination of strength of 954 MPa and elongation of 39.2% was obtained.

  18. Purifying oils, cracking oils, catalysts. [British Patent

    Energy Technology Data Exchange (ETDEWEB)

    1936-02-05

    Hydrocarbon oils are refined by treating while substantially in the liquid phase between 200/sup 0/ and 400/sup 0/C with a phosphoric acid catalyst deposited on metallurgical coke, a suitable blast furnace slag, silica gel or other carrier with similar properties, until the objectionable components are converted into innocuous substances by polymerization cracking, isomerization and/or alkylation. By this treatment the bromine number is reduced, the end-point of the A.S.T.M. distillation is increased, the octane number is raised, mercaptans are converted to hydrogen sulphide and olefines, thioethers and thiophenes are converted to mereaptans, and the initial boiling point is lowered. The process is applicable to gasoline, cracked distillate, kerosine and lubricating oil, obtained by distilling or cracking petroleum, shale and hydrogenated oils; and is particularly applicable for stabilizing cracked distillates.

  19. Effect of liquid metal embrittlement on low cycle fatigue properties and fatigue crack propagation behavior of a modified 9Cr–1Mo ferritic–martensitic steel in an oxygen-controlled lead–bismuth eutectic environment at 350 °C

    Energy Technology Data Exchange (ETDEWEB)

    Gong, Xing, E-mail: gongxingzfl@hotmail.com [SCK-CEN (Belgian Nuclear Research Centre), Boeretang 200, B-2400 Mol (Belgium); KU Leuven, Department of Metallurgy and Materials Engineering, Kasteelpark Arenberg 44, Box 2450, B-3001 Heverlee (Belgium); Marmy, Pierre, E-mail: pierre.marmy@sckcen.be [SCK-CEN (Belgian Nuclear Research Centre), Boeretang 200, B-2400 Mol (Belgium); Qin, Ling, E-mail: Ling.Qin@mtm.kuleuven.be [KU Leuven, Department of Metallurgy and Materials Engineering, Kasteelpark Arenberg 44, Box 2450, B-3001 Heverlee (Belgium); Verlinden, Bert, E-mail: Bert.Verlinden@mtm.kuleuven.be [KU Leuven, Department of Metallurgy and Materials Engineering, Kasteelpark Arenberg 44, Box 2450, B-3001 Heverlee (Belgium); Wevers, Martine, E-mail: Martine.Wevers@mtm.kuleuven.be [KU Leuven, Department of Metallurgy and Materials Engineering, Kasteelpark Arenberg 44, Box 2450, B-3001 Heverlee (Belgium); Seefeldt, Marc, E-mail: Marc.Seefeldt@mtm.kuleuven.be [KU Leuven, Department of Metallurgy and Materials Engineering, Kasteelpark Arenberg 44, Box 2450, B-3001 Heverlee (Belgium)

    2014-11-17

    The low cycle fatigue properties of a modified 9Cr–1Mo ferritic–martensitic steel (T91) have been tested in stagnant liquid lead–bismuth eutectic (LBE) with oxygen concentrations ranging from 1.16×10{sup −6} to 6.0×10{sup −10} wt% at 350 °C. The effect of liquid metal embrittlement (LME) on fatigue endurance, fatigue crack propagation modes and secondary cracking has been studied. The results showed that the fatigue lives of T91 steel in a low oxygen concentration LBE were drastically reduced compared to those in vacuum due to the presence of LME. The microstructural observations on the fatigue crack propagation modes revealed that fatigue cracks in LBE mainly propagate across prior-austenite grain boundaries and then cut through martensitic lath boundaries, simultaneously leaving a few plastic flow traces and characteristic brittle features. Intergranular and interlath cracking occurred occasionally and their occurrence depended on the orientation of the boundaries relative to the stress axis. The complexity of the LME-induced fracture features can be attributed to a mixture of the multiple failure modes. No obvious plastic shear strain localization was present around the crack tips when LME occurred. However, using a high resolution electron backscatter diffraction (EBSD) technique, highly localized plastic shear strain was observed in the vicinity of the crack tips in vacuum, manifested by the presence of very fine subgrains along the crack walls. A qualitative mechanism was proposed to account for the LME phenomenon in the T91/LBE system. In addition, the secondary cracking at fatigue striations was different in the presence of LBE compared to vacuum. This phenomenon was elucidated by taking into account the influence of the LME on the fatigue crack propagation rate.

  20. Physical properties characterization of WO{sub 3} films grown by hot-filament metal oxide deposition

    Energy Technology Data Exchange (ETDEWEB)

    Diaz-Reyes, J., E-mail: jdiazr2001@yahoo.com [Centro de Investigacion en Biotecnologia Aplicada del Instituto Politecnico Nacional, Ex-Hacienda de San Juan Molino, Km. 1.5, Tepetitla, Tlaxcala, 90700 (Mexico); Delgado-Macuil, R.J. [Centro de Investigacion en Biotecnologia Aplicada del Instituto Politecnico Nacional, Ex-Hacienda de San Juan Molino, Km. 1.5, Tepetitla, Tlaxcala, 90700 (Mexico); Dorantes-Garcia, V. [Preparatoria ' Simon Bolivar' de la Benemerita Universidad Autonoma de Puebla, 4 Oriente 408, Col. Centro, Atlixco, Puebla, C. P. 74200 (Mexico); Perez-Benitez, A. [Facultad de Ciencias Quimicas de la Benemerita Universidad Autonoma Puebla, 14 Sur y Av. San Claudio, Col. San Manuel, Puebla, Puebla, C. P. 72570 (Mexico); Balderas-Lopez, J.A. [Unidad Profesional Interdisciplinaria de Biotecnologia del Instituto Politecnico Nacional, Avenida Acueducto S/N, Col. Barrio la Laguna, Ticoman, Del. Gustavo A. Madero, Mexico, D.F. 07340 (Mexico); Ariza-Ortega, J.A. [Centro de Investigacion en Biotecnologia Aplicada del Instituto Politecnico Nacional, Ex-Hacienda de San Juan Molino, Km. 1.5, Tepetitla, Tlaxcala, 90700 (Mexico)

    2010-10-25

    WO{sub 3} is grown by hot-filament metal oxide deposition (HFMOD) technique under atmospheric pressure and an oxygen atmosphere. By X-ray diffraction obtains that WO{sub 3} presents mainly monoclinic crystalline phase. The chemical stoichiometry is obtained by X-ray Photoelectron Spectroscopy (XPS). The IR spectrum of the as-grown WO{sub 3} presents broad peaks in the range of 1100 to 3600 cm{sup -1}. A broad band in the 2200 to 3600 cm{sup -1} region and the peaks sited at 1645 and 1432 cm{sup -1} are well resolved, which are originated from moisture and are assigned to {nu}(OH) and {delta}(OH) modes of adsorbed water and the corresponding tungsten oxide vibrations are in infrared region from 400 to 1453 cm{sup -1} and around 3492 cm{sup -1}, which correspond to tungsten-oxygen (W-O) stretching, bending and lattice modes. The Raman spectrum shows intense peaks at 801, 710, 262 and 61 cm{sup -1} that are typical Raman peaks of crystalline WO{sub 3} (m-phase) that correspond to stretching vibrations of the bridging oxygen, which are assigned to W-O stretching ({nu}) and W-O bending ({delta}) modes, respectively. By transmittance measurements obtains that the WO{sub 3} band gap can be varied from 2.92 to 3.13 eV in the investigated annealing temperature range.

  1. The versatility of hot-filament activated chemical vapor deposition

    International Nuclear Information System (INIS)

    Schaefer, Lothar; Hoefer, Markus; Kroeger, Roland

    2006-01-01

    In the field of activated chemical vapor deposition (CVD) of polycrystalline diamond films, hot-filament activation (HF-CVD) is widely used for applications where large deposition areas are needed or three-dimensional substrates have to be coated. We have developed processes for the deposition of conductive, boron-doped diamond films as well as for tribological crystalline diamond coatings on deposition areas up to 50 cm x 100 cm. Such multi-filament processes are used to produce diamond electrodes for advanced electrochemical processes or large batches of diamond-coated tools and parts, respectively. These processes demonstrate the high degree of uniformity and reproducibility of hot-filament CVD. The usability of hot-filament CVD for diamond deposition on three-dimensional substrates is well known for CVD diamond shaft tools. We also develop interior diamond coatings for drawing dies, nozzles, and thread guides. Hot-filament CVD also enables the deposition of diamond film modifications with tailored properties. In order to adjust the surface topography to specific applications, we apply processes for smooth, fine-grained or textured diamond films for cutting tools and tribological applications. Rough diamond is employed for grinding applications. Multilayers of fine-grained and coarse-grained diamond have been developed, showing increased shock resistance due to reduced crack propagation. Hot-filament CVD is also used for in situ deposition of carbide coatings and diamond-carbide composites, and the deposition of non-diamond, silicon-based films. These coatings are suitable as diffusion barriers and are also applied for adhesion and stress engineering and for semiconductor applications, respectively

  2. Characterization and methodology for calculating the mechanical properties of a TRIP-steel submitted to hot stamping and quenching and partitioning (Q&P)

    International Nuclear Information System (INIS)

    Ariza, E.A.; Nishikawa, A.S; Goldenstein, H.; Tschiptschin, A.P.

    2016-01-01

    Thermomechanical simulation of quenching, hot stamping, and quenching and partitioning processes of a high-strength TRIP-assisted steel were carried out in a Gleeble®3S50 thermo-mechanical simulator, coupled to the synchrotron X-ray diffraction line. The microstructures and mechanical properties were analyzed using Field Emission Gun Scanning Electron Microscopy (FEG-SEM), X-ray diffraction, and nanoindentation. The microstructures of thermomechanical treated specimens were modeled using the Object Oriented Finite Element (OOF) technique. The modeled microstructures were then fed into a finite element model to predict the mechanical behavior. By using a reverse algorithm method, the elasto-plastic mechanical properties of different microconstituents were determined. This was done through the analysis of instrumented nanoindentation loading-penetration curves. Tensile properties of the thermomechanical processed steels were measured by tensile testing of subsized specimens cut from samples processed on the Gleeble®3S50. The comparison between the experimental results and those of the reverse algorithm and the OOF modeled microstructure showed quite good agreement.

  3. High-Temperature Hot Air/Silane Coupling Modification of Wood Fiber and Its Effect on Properties of Wood Fiber/HDPE Composites

    Directory of Open Access Journals (Sweden)

    Feng Chen

    2017-03-01

    Full Text Available The surfaces of poplar wood fibers were modified using high-temperature hot air (HTHA treatment and silane coupling agent. The single factor test was then used to investigate the performances (e.g., the change of functional groups, polarity, cellulose crystallinity, and thermal stability of modified poplar wood fibers (mPWF through Fourier transform infrared spectrometry, X-ray diffraction and thermo-gravimetric analysis for the subsequent preparation of wood-plastic composites (WPCs. The effect of HTHA treatment conditions—such as temperature, inlet air velocity, and feed rate—on the performances of WPCs was also investigated by scanning electron microscopy and dynamic mechanical analysis. The main findings indicated that HTHA treatment could promote the hydration of mPWF and improve the mechanical properties of WPCs. Treatment temperature strongly affected the mechanical properties and moisture adsorption characteristics of the prepared composites. With the increase of treated temperature and feed rate, the number of hydroxyl groups, holocellulose content, and the pH of mPWF decreased. The degree of crystallinity and thermal stability and the storage modulus of the prepared composites of mPWF increased. However, dimensional stability and water absorption of WPCs significantly reduced. The best mechanical properties enhancement was observed with treatment temperature at 220 °C. This study demonstrated the feasibility for the application of an HTHA treatment in the WPC production industry.

  4. Characterization and methodology for calculating the mechanical properties of a TRIP-steel submitted to hot stamping and quenching and partitioning (Q&P)

    Energy Technology Data Exchange (ETDEWEB)

    Ariza, E.A., E-mail: andersonariza@usp.br [Department of Metallurgical and Materials Engineering, University of São Paulo, Av. Prof. Mello Moraes, 2463, São Paulo, SP CEP 05508-030 (Brazil); Brazilian Nanotechnology National Laboratory, LNNano, CNPEM, Brazilian Center for Research in Energy and Materials (Brazil); Nishikawa, A.S; Goldenstein, H. [Department of Metallurgical and Materials Engineering, University of São Paulo, Av. Prof. Mello Moraes, 2463, São Paulo, SP CEP 05508-030 (Brazil); Tschiptschin, A.P. [Department of Metallurgical and Materials Engineering, University of São Paulo, Av. Prof. Mello Moraes, 2463, São Paulo, SP CEP 05508-030 (Brazil); Brazilian Nanotechnology National Laboratory, LNNano, CNPEM, Brazilian Center for Research in Energy and Materials (Brazil)

    2016-08-01

    Thermomechanical simulation of quenching, hot stamping, and quenching and partitioning processes of a high-strength TRIP-assisted steel were carried out in a Gleeble®3S50 thermo-mechanical simulator, coupled to the synchrotron X-ray diffraction line. The microstructures and mechanical properties were analyzed using Field Emission Gun Scanning Electron Microscopy (FEG-SEM), X-ray diffraction, and nanoindentation. The microstructures of thermomechanical treated specimens were modeled using the Object Oriented Finite Element (OOF) technique. The modeled microstructures were then fed into a finite element model to predict the mechanical behavior. By using a reverse algorithm method, the elasto-plastic mechanical properties of different microconstituents were determined. This was done through the analysis of instrumented nanoindentation loading-penetration curves. Tensile properties of the thermomechanical processed steels were measured by tensile testing of subsized specimens cut from samples processed on the Gleeble®3S50. The comparison between the experimental results and those of the reverse algorithm and the OOF modeled microstructure showed quite good agreement.

  5. Texture evolution in Nd:YAG-laser welds of AZ31 magnesium alloy hot rolled sheets and its influence on mechanical properties

    International Nuclear Information System (INIS)

    Commin, Lorelei; Dumont, Myriam; Rotinat, Rene; Pierron, Fabrice; Masse, Jean-Eric; Barrallier, Laurent

    2011-01-01

    Research highlights: → AZ31 LBW fusion zone results in Mg 17 (Al-Zn) 12 precipitation, twins formation and {0 0 2} texture modification. → The mechanical properties were reduced after LBW but the fracture occurred in the base metal. → The mechanical properties were reduced after LBW but the fracture occurred in the base metal. → A recovery of elongation and UTS can be achieved by a 300 deg. C/1 h heat treatment. The texture evolution is mainly responsible for the yield strength reduction in the fusion zone. - Abstract: AZ31 hot rolled magnesium alloy presents a strong basal texture. Using laser beam welding (LBW) as a joining process induces high temperature gradients leading to major texture changes. Electron back scattered diffraction (EBSD) was used to study the texture evolution, and tensile tests coupled with speckle interferometry were performed to understand its influence on mechanical properties. The random texture obtained in the LBW fusion zone is mainly responsible for the yield strength reduction.

  6. Predominantly elastic crack growth under combined creep-fatigue cycling

    International Nuclear Information System (INIS)

    Lloyd, G.J.

    1979-01-01

    A rationalization of the various observed effects of combined creep-fatigue cycling upon predominantly elastic fatigue-crack propagation in austenitic steel is presented. Existing and new evidence is used to show two main groups of behaviour: (i) material and cycling conditions which lead to modest increases (6-8 times) in the rate of crack growth are associated with relaxation-induced changes in the material deformation characteristics, and (ii) material and cycling conditions severe enough to generate internal fracture damage lead to significant (up to a factor of 30) increases in crack growth rate when compared with fast-cycling crack propagation rates at the same temperature. A working hypothesis is presented to show that the boundary between the two groups occurs when the scale of the nucleated creep damage is of the same magnitude as the crack tip opening displacement. This leads to the possibility of unstable crack advance. Creep crack growth rates are shown to provide an upper bound to creep-fatigue crack growth rates when crack advance is unstable. If the deformation properties only are affected by the creep-fatigue cycling then creep crack growth rates provide a lower bound. The role of intergranular oxygen corrosion in very low frequency crack growth tests is also briefly discussed. (author)

  7. Crack layer theory

    Science.gov (United States)

    Chudnovsky, A.

    1987-01-01

    A damage parameter is introduced in addition to conventional parameters of continuum mechanics and consider a crack surrounded by an array of microdefects within the continuum mechanics framework. A system consisting of the main crack and surrounding damage is called crack layer (CL). Crack layer propagation is an irreversible process. The general framework of the thermodynamics of irreversible processes are employed to identify the driving forces (causes) and to derive the constitutive equation of CL propagation, that is, the relationship between the rates of the crack growth and damage dissemination from one side and the conjugated thermodynamic forces from another. The proposed law of CL propagation is in good agreement with the experimental data on fatigue CL propagation in various materials. The theory also elaborates material toughness characterization.

  8. Atomistics of crack propagation

    International Nuclear Information System (INIS)

    Sieradzki, K.; Dienes, G.J.; Paskin, A.; Massoumzadeh, B.

    1988-01-01

    The molecular dynamic technique is used to investigate static and dynamic aspects of crack extension. The material chosen for this study was the 2D triangular solid with atoms interacting via the Johnson potential. The 2D Johnson solid was chosen for this study since a sharp crack in this material remains stable against dislocation emission up to the critical Griffith load. This behavior allows for a meaningful comparison between the simulation results and continuum energy theorems for crack extension by appropriately defining an effective modulus which accounts for sample size effects and the non-linear elastic behavior of the Johnson solid. Simulation results are presented for the stress fields of moving cracks and these dynamic results are discussed in terms of the dynamic crack propagation theories, of Mott, Eshelby, and Freund

  9. Thermomechanical finite element analysis of hot water boiler structure

    Directory of Open Access Journals (Sweden)

    Živković Dragoljub S.

    2012-01-01

    Full Text Available The paper presents an application of the Finite Elements Method for stress and strain analysis of the hot water boiler structure. The aim of the research was to investigate the influence of the boiler scale on the thermal stresses and strains of the structure of hot water boilers. Results show that maximum thermal stresses appear in the zone of the pipe carrying wall of the first reversing chamber. This indicates that the most critical part of the boiler are weld spots of the smoke pipes and pipe carrying plate, which in the case of significant scale deposits can lead to cracks in the welds and water leakage from the boiler. The nonlinear effects were taken into account by defining the bilinear isotropic hardening model for all boiler elements. Temperature dependency was defined for all relevant material properties, i. e. isotropic coefficient of thermal expansion, Young’s modulus, and isotropic thermal conductivity. The verification of the FEA model was performed by comparing the measured deformations of the hot water boiler with the simulation results. As a reference object, a Viessmann - Vitomax 200 HW boiler was used, with the installed power of 18.2 MW. CAD modeling was done within the Autodesk Inventor, and stress and strain analysis was performed in the ANSYS Software.

  10. Hot Ductility Behavior of a Peritectic Steel during Continuous Casting

    Directory of Open Access Journals (Sweden)

    Mustafa Merih Arıkan

    2015-06-01

    Full Text Available Hot ductility properties of a peritectic steel for welded gas cylinders during continuous casting were studied by performing hot tensile tests at certain temperatures ranging from 1200 to 700 °C for some cooling rates by using Gleeble-3500 thermo-mechanical test and simulation machine in this study. The effects of cooling rate and strain rate on hot ductility were investigated and continuous casting process map (time-temperature-ductility were plotted for this material. Reduction of area (RA decreases and cracking susceptibility increases during cooling from solidification between certain temperatures depending on the cooling rate. Although the temperatures which fracture behavior change upon cooling during continuous casting may vary for different materials, it was found that the type of fracture was ductile at 1100 and 1050 °C; semi-ductile at 1000 °C, and brittle at 800 °C for the steel P245NB. There is a ductility trough between 1000 and 725 °C. The ductility trough gets slightly narrower as the cooling rate decreases.

  11. Preparation and properties of carbonaceous products prepared by the cracking of natural gas; Fabrication et proprietes de corps carbones prepares par craquage de gaz naturel

    Energy Technology Data Exchange (ETDEWEB)

    Blum, P L; Bochirol, L; Rappeneau, J; Cornuault, P; Blanchard, R; Moreau, C [Commissariat a l' Energie Atomique, Grenoble (France). Centre d' Etudes Nucleaires

    1964-07-01

    Complete results are presented of tests recently carried out at the Grenoble Nuclear Research Centre in an attempt to transform natural gas (gas from Lacq), used as a source of pyrolytic carbon, into carbonaceous products with improved properties. Several methods have been studied: 1 - By using normal grade industrial graphite as support (density of about 1.50) products having densities of about 1.80 are obtained. Their open porosity (6 to 7 per cent) is lower than that of conventional graphites, and several of their characteristics are more or less equal to, or better than those obtained from a double impregnation witch pitch. 2 - The use as supporting material of the semi-products ('cooked') usually used for graphite production does not lead to satisfactory results. The main reasons for this are given. 3 - A new process, called 'BB5', has been developed. The starting materials here are powdered products (petrol coke or graphite) which are put into shape with the use of a binder which can be dispersed in water. The supports thus produced make it possible, because of their porous structure, to make the most of the densification produced by cracking natural gas below 1000 deg. C. The products obtained, which are made up of equal amounts approximately of the supporting material and of pyrocarbon can attain densities of over 1.90. Their very low open porosity can be reduced almost to zero and their impermeability is then excellent (k=10{sup -8} cm{sup 2}sec{sup -1}). They have also a remarkably high resistance to compression, values of 15 to 20 kg/mm{sup 2} being obtained for those carbons which have not undergone a final graphitization treatment. Some examples are given of possible nuclear applications of the materials produced in this manner. (authors) [French] On expose l'ensemble des essais effectues recemment au CEN-G pour preparer, a partir de gaz naturel (gaz de Lacq) comme source de carbone pyrolytique, des corps carbones de caracteristiques ameliorees

  12. Improvement of microstructure and mechanical properties of high dense SiC ceramics manufactured by high-speed hot pressing

    International Nuclear Information System (INIS)

    Voyevodin, V.; Sayenko, S.; Lobach, K.; Tarasov, R.; Zykova, A.; Svitlychnyi, Ye.; Surkov, A.; Abelentsev, V.; Ghaemi, H.; Szkodo, M.; Gajowiec, G.; Kmiec, M.; Antoszkiewicz, M.

    2017-01-01

    Non-oxide ceramics possess high physical-mechanical properties, corrosion and radiation resistance, which can be used as a protective materials for radioactive wastes disposal. The aim of the present study was the manufacturing of high density SiC ceramics with advanced physical and mechanical parameters. The high performance on the properties of produced ceramics was determined by the dense and monolithic structure. The densified silicon carbide samples possessed good mechanical strength, with a high Vickers micro hardness up to 28.5 GPa.

  13. Hot Gas Halos in Galaxies

    Science.gov (United States)

    Mulchaey, John

    Most galaxy formation models predict that massive low-redshift disk galaxies are embedded in extended hot halos of externally accreted gas. Such gas appears necessary to maintain ongoing star formation in isolated spirals like the Milky Way. To explain the large population of red galaxies in rich groups and clusters, most galaxy evolution models assume that these hot gas halos are stripped completely when a galaxy enters a denser environment. This simple model has been remarkably successful at reproducing many observed properties of galaxies. Although theoretical arguments suggest hot gas halos are an important component in galaxies, we know very little about this gas from an observational standpoint. In fact, previous observations have failed to detect soft X-ray emission from such halos in disk galaxies. Furthermore, the assumption that hot gas halos are stripped completely when a galaxy enters a group or cluster has not been verified. We propose to combine proprietary and archival XMM-Newton observations of galaxies in the field, groups and clusters to study how hot gas halos are impacted by environment. Our proposed program has three components: 1) The deepest search to date for a hot gas halo in a quiescent spiral galaxy. A detection will confirm a basic tenet of disk galaxy formation models, whereas a non-detection will seriously challenge these models and impose new constraints on the growth mode and feedback history of disk galaxies. 2) A detailed study of the hot gas halos properties of field early-type galaxies. As environmental processes such as stripping are not expected to be important in the field, a study of hot gas halos in this environment will allow us to better understand how feedback and other internal processes impact hot gas halos. 3) A study of hot gas halos in the outskirts of groups and clusters. By comparing observations with our suite of simulations we can begin to understand what role the stripping of hot gas halos plays in galaxy

  14. Prevention of shrinkage cracking in tight concrete structures

    International Nuclear Information System (INIS)

    Alvaredo, A.M.; Wittmann, F.H.

    1995-01-01

    It is shown that crack formation and propagation in concrete members subjected to restrained shrinkage can be realistically predicted by means of a comprehensive approach including a diffusion analysis and fracture mechanics considerations. The conditions for stable crack propagation regarding dimensions of the concrete member, degree of restraint to the imposed deformation and material properties are discussed. Guidelines on the prevention of shrinkage cracking of concrete structures are given. (author). 10 refs., 5 figs

  15. The Cracking Mechanism of Ferritic-Austenitic Cast Steel

    Directory of Open Access Journals (Sweden)

    Stradomski G.

    2016-12-01

    Full Text Available In the high-alloy, ferritic - austenitic (duplex stainless steels high tendency to cracking, mainly hot-is induced by micro segregation processes and change of crystallization mechanism in its final stage. The article is a continuation of the problems presented in earlier papers [1 - 4]. In the range of high temperature cracking appear one mechanism a decohesion - intergranular however, depending on the chemical composition of the steel, various structural factors decide of the occurrence of hot cracking. The low-carbon and low-alloy cast steel casting hot cracking cause are type II sulphide, in high carbon tool cast steel secondary cementite mesh and / or ledeburite segregated at the grain solidified grains boundaries, in the case of Hadfield steel phosphorus - carbide eutectic, which carrier is iron-manganese and low solubility of phosphorus in high manganese matrix. In duplex cast steel the additional factor increasing the risk of cracking it is very “rich” chemical composition and related with it processes of precipitation of many secondary phases.

  16. Influence of Short Austenitization Treatments on the Mechanical Properties of Low-Alloy Steels for Hot Forming Applications

    Science.gov (United States)

    Holzweissig, Martin Joachim; Lackmann, Jan; Konrad, Stefan; Schaper, Mirko; Niendorf, Thomas

    2015-07-01

    The current work elucidates an improvement of the mechanical properties of tool-quenched low-alloy steel by employing extremely short austenitization durations utilizing a press heating arrangement. Specifically, the influence of different austenitization treatments—involving austenitization durations ranging from three to 15 seconds—on the mechanical properties of low-alloy steel in comparison to an industrial standard furnace process was examined. A thorough set of experiments was conducted to investigate the role of different austenitization durations and temperatures on the resulting mechanical properties such as hardness, bending angle, tensile strength, and strain at fracture. The most important finding is that the hardness, the bending angle as well as the tensile strength increase with shortened austenitization durations. Furthermore, the ductility of the steels exhibits almost no difference following the short austenitization durations and the standard furnace process. The enhancement of the mechanical properties imposed by the short heat treatments investigated, is related to a refinement of microstructural features as compared to the standard furnace process.

  17. Particle-in-cell studies of laser-driven hot spots and a statistical model for mesoscopic properties of Raman backscatter

    International Nuclear Information System (INIS)

    Albright, B.J.; Yin, L.; Bowers, K.J.; Kline, J.L.; Montgomery, D.S.; Fernandez, J.C.; Daughton, W.

    2006-01-01

    The authors use explicit particle-in-cell simulations to model stimulated scattering processes in media with both solitary and multiple laser hot spots. These simulations indicate coupling among hot spots, whereby scattered light, plasma waves, and hot electrons generated in one laser hot spot may propagate to neighboring hot spots, which can be destabilized to enhanced backscatter. A nonlinear statistical model of a stochastic beam exhibiting this coupled behavior is described here. Calibration of the model using particle-in-cell simulations is performed, and a threshold is derived for 'detonation' of the beam to high reflectivity. (authors)

  18. Fatigue-crack propagation in gamma-based titanium aluminide alloys at large and small crack sizes

    International Nuclear Information System (INIS)

    Kruzic, J.J.; Campbell, J.P.; Ritchie, R.O.

    1999-01-01

    Most evaluations of the fracture and fatigue-crack propagation properties of γ+α 2 titanium aluminide alloys to date have been performed using standard large-crack samples, e.g., compact-tension specimens containing crack sizes which are on the order of tens of millimeters, i.e., large compared to microstructural dimensions. However, these alloys have been targeted for applications, such as blades in gas-turbine engines, where relevant crack sizes are much smaller ( 5 mm) and (c ≅ 25--300 microm) cracks in a γ-TiAl based alloy, of composition Ti-47Al-2Nb-2Cr-0.2B (at.%), specifically for duplex (average grain size approximately17 microm) and refined lamellar (average colony size ≅150 microm) microstructures. It is found that, whereas the lamellar microstructure displays far superior fracture toughness and fatigue-crack growth resistance in the presence of large cracks, in small-crack testing the duplex microstructure exhibits a better combination of properties. The reasons for such contrasting behavior are examined in terms of the intrinsic and extrinsic (i.e., crack bridging) contributions to cyclic crack advance

  19. Chemical milling solution reveals stress corrosion cracks in titanium alloy

    Science.gov (United States)

    Braski, D. N.

    1967-01-01

    Solution of hydrogen flouride, hydrogen peroxide, and water reveals hot salt stress corrosion cracks in various titanium alloys. After the surface is rinsed in water, dried, and swabbed with the solution, it can be observed by the naked eye or at low magnification.

  20. Comparative study of direct and inverse problems of cracked beams

    Directory of Open Access Journals (Sweden)

    Mahieddine Chettah

    2018-01-01

    Full Text Available In recent decades, the analysis and evaluation of the cracked structures were hot spots in several engineering fields and has been the subject of great interest with important and comprehensive surveys covering various methodologies and applications, in order to obtain reliable and effective methods to maintain the safety and performance of structures on a proactive basis. The presence of a crack, not only causes a local variation in the structural parameters (e.g., the stiffness of a beam at its location, but it also has a global effect which affects the overall dynamic behavior of the structure (such as the natural frequencies. For this reason, the dynamic characterization of the cracked structures can be used to detect damage from non-destructive testing. The objective of this paper is to compare the accuracy and ability of two methods to correctly predict the results for both direct problem to find natural frequencies and inverse problem to find crack’s locations and depths of a cracked simply supported beam. Several cases of crack depths and crack locations are investigated. The crack is supposed to remain open. The Euler–Bernoulli beam theory is employed to model the cracked beam and the crack is represented as a rotational spring with a sectional flexibility. In the first method, the transfer matrix method is used; the cracked beam is modeled as two uniform sub-segments connected by a rotational spring located at the cracked section. In the second method which is based on the Rayleigh’s method, the mode shape of the cracked beam is constructed by adding a cubic polynomial function to that of the undamaged beam. By applying the compatibility conditions at crack’s location and the corresponding boundary conditions, the general forms of characteristic equations for this cracked system are obtained. The two methods are then utilized to determine the locations and depths by using any two natural frequencies of a cracked simply

  1. Investigations on avoidance of hot cracks during laser welding of austenitic Cr-Ni steels and nickel-based alloys using temperature field tailoring. Final report; Untersuchungen zur Vermeidung von Heissrissen beim Laserstrahlschweissen von austenitischen Cr-Ni-Staehlen und Nickelbasislegierungen mittels Temperaturfeld-Tailoring. Schlussbericht

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    2013-08-08

    The aim of the project was to transfer the developed method of laser beam welding of heat treated machining steels of temperature field tailoring on hot crack endangered austenitic Cr-Ni steels and nickel-based alloys. With this method, transient thermal stresses adjacent to the weld are produced by an travelling induction heating so that the hot cracking is prevented during welding. As test materials the austenitic Cr-Ni steel with sulfur additive 1.4305, the Cr-Ni steels 1.4404 and 1.4435 and the nickel-based alloy Udimet 720 were selected. As a result of the research it was shown that a hot crack-free laser welding in the investigated materials using at least three different welding and material-technical approaches is possible. [German] Das Ziel des Forschungsvorhabens bestand darin, das fuer das Laserstrahlschweissen verguetbarer Automatenstaehle entwickelte Verfahren des Temperaturfeld-Tailorings auf heissrissgefaehrdete austenitische Cr-Ni-Staehle und Nickelbasislegierungen zu uebertragen. Mit diesem Verfahren werden waehrend des Schweissens transiente thermische Spannungen neben der Schweissnaht durch eine mitlaufende induktive Erwaermung so erzeugt, dass die Heissrissbildung verhindert wird. Als Versuchswerkstoffe wurden der austenitische Cr-Ni-Stahl mit Schwefelzusatz 1.4305, die Cr-Ni-Staehle 1.4404 und 1.4435 sowie die Nickelbasislegierung Udimet 720 ausgewaehlt. Im Ergebnis des Forschungsvorhabens konnte gezeigt werden, dass ein heissrissfreies Laserstrahlschweissen bei den untersuchten Werkstoffen unter Nutzung von mindestens drei verschiedenen schweiss- und werkstofftechnischen Ansaetzen moeglich ist: Erstens koennen mit einem Temperaturfeld-Tailoring bei im Stumpfstoss zu verschweissenden Blechen aus austenitischen Staehlen bis mindestens 6 mm Dicke senkrecht zur Naht und parallel zur Blechoberflaeche wirkende transiente Druckspannungen erzeugt werden, die der Bildung von Mittelrippenrissen oder dazu parallel liegenden Heissrissen entgegenwirken

  2. Cracked gas generator

    Energy Technology Data Exchange (ETDEWEB)

    Abthoff, J; Schuster, H D; Gabler, R

    1976-11-17

    A small cracked-gas generator in a vehicle driven, in particular, by an air combustion engine has been proposed for the economic production of the gases necessary for low toxicity combustion from diesel fuel. This proceeds via catalytic crack-gasification and exploitation of residual heat from exhaust gases. This patent application foresees the insertion of one of the catalysts supporting the cracked-gas reaction in a container through which the reacting mixture for cracked-gas production flows in longitudinal direction. Further, air ducts are embedded in the catalyst through which exhaust gases and fresh air flow in counter direction to the cracked gas flow in the catalyst. The air vents are connected through heat conduction to the catalyst. A cracked gas constituting H/sub 2//CO/CO/sub 2//CH/sub 4/ and H/sub 2/O can be produced from the air-fuel mixture using appropriate catalysts. By the addition of 5 to 25% of cracked gas to the volume of air drawn in by the combustion engine, a more favourable combustion can be achieved compared to that obtained under normal combustion conditions.

  3. HOT 2017

    DEFF Research Database (Denmark)

    Hannibal, Sara Stefansen

    HOT er en kvalitativ undersøgelse, der hvert år diskuterer og undersøger en lille udvalgt skare af danskkyndige fagpersoners bud på, hvad de er optagede af på literacyområdet her og nu – altså hvilke emner, de vil vurdere som aktuelle at forholde sig til i deres nuværende praksis.......HOT er en kvalitativ undersøgelse, der hvert år diskuterer og undersøger en lille udvalgt skare af danskkyndige fagpersoners bud på, hvad de er optagede af på literacyområdet her og nu – altså hvilke emner, de vil vurdere som aktuelle at forholde sig til i deres nuværende praksis....

  4. Structure-property investigations on a laser beam welded dissimilar joint of aluminium AA6056 and titanium Ti6Al4V for aeronautical applications. Part II: resistance to fatigue crack propagation and fracture

    Energy Technology Data Exchange (ETDEWEB)

    Horstmann, M.; Ventzke, V.; Petrovski, B.; Kocak, M. [GKSS Research Centre Geesthacht, Institute of Materials Research, Materials Mechanics, Geesthacht (Germany); Kocik, R.; Tempus, G. [AIRBUS Deutschland GmbH, Metal Technology, Bremen (Germany); Vaidya, W.V.

    2009-10-15

    Investigations were continued on the dissimilar laser beam welds of AA6056 and Ti6Al4V, fabricated by inserting Ti-sheet into the profiled Al-sheet and melting AA6056 alone. By using microstructure, hardness and strength as the criteria, sites exhibiting non-uniform microstructure and localized plastic deformation due to strength mismatch were investigated in two orientations: crack parallel to the weld and crack perpendicular to the weld for fatigue crack propagation and fracture toughness at room temperature. Effect of temper of AA6056 on these properties was studied for two conditions; welding in T4 followed by post weld heat treatment T6, and welding in T6 and naturally aged for a defined period. The orientation ''crack parallel to the weld'' was investigated in 3 locations on the side of AA6056: the interface and the two changeovers on the Al-side. Firstly, between the fusion zone and the heat affected zone (3 mm from the interface) and secondly, between (primary) heat affected zone and towards the base material (7 mm from the interface). Although brittle intermetallic TiAl{sub 3} had been formed at the interface, uncontrolled separation or debonding at the interface was not observed. Insofar the bond quality of the weld was good. However, the ranking of interface was the lowest since fatigue crack propagation was relatively faster than that in the fusion zone and heat affected zone, and fracture toughness was low. Therefore, unstable fatigue crack propagation is observed when the crack propagates perpendicular to the weld from AA6056 towards Ti6Al4V. The results have shown that the dissimilar joints exhibit improved performance when laser beam welded in the T6 condition. (Abstract Copyright [2009], Wiley Periodicals, Inc.) [German] Teil II: Widerstand gegen Ermuedungsrissausbreitung und Bruch Die Untersuchungen an der laserstrahlgeschweissten Mischverbindung aus AA6056 und Ti6Al4V wurden fortgesetzt. Fuer die Ermuedungsrissausbreitungs

  5. Hot particles

    International Nuclear Information System (INIS)

    Merwin, S.E.; Moeller, M.P.

    1989-01-01

    Nuclear Regulatory Commission (NRC) licensees are required to assess the dose to skin from a hot particle contamination event at a depth of skin of7mg/cm 2 over an area of 1 cm 2 and compare the value to the current dose limit for the skin. Although the resulting number is interesting from a comparative standpoint and can be used to predict local skin reactions, comparison of the number to existing limits based on uniform exposures is inappropriate. Most incidents that can be classified as overexposures based on this interpretation of dose actually have no effect on the health of the worker. As a result, resources are expended to reduce the likelihood that an overexposure event will occur when they could be directed toward eliminating the cause of the problem or enhancing existing programs such as contamination control. Furthermore, from a risk standpoint, this practice is not ALARA because some workers receive whole body doses in order to minimize the occurrence of hot particle skin contaminations. In this paper the authors suggest an alternative approach to controlling hot particle exposures

  6. Study of the properties of plasma deposited layers of nickel-chrome-aluminium-yttrium coatings resistant to oxidation and hot corrosion

    Directory of Open Access Journals (Sweden)

    Mihailo R. Mrdak

    2012-04-01

    Full Text Available The aim of this study was to examine the properties of Ni22Cr10Al1Y layers in order to obtain optimal structural - mechanical properties with the optimization of depositing parameters. Powder was deposited by the atmospheric plasma spray (APS process with the current intensity of 600, 700 and 800A, with a corresponding plasma gun power supply of 22KW, 34KW and 28KW. The evaluation of the Ni22Cr10Al1Y coating layers was made on the basis of their microhardness, tensile strength and microstructure performance. The best performance was obtained in the layers deposited with 800A and the 34KW plasma gun power supply. The coating with the best characteristics was tested to oxidation in the furnace for heat treatment without a protective atmosphere at 1100°C for one hour. The examination of the morphology of Ni22Cr10Al1Y powder particles was carried out on the SEM (Scanning Electron Microscope as well as the EDS analysis of the best layers. The microstructure of the deposited coating layers was examined with a light microscope. The microstructure analysis was performed according to the TURBOMECA standard. The mechanical properties of layers were evaluated by the method HV0.3 for microhardness and by tensile testing for bond strength. The research has shown that plasma gun power supply significantly affects the mechanical properties and microstructure of coatings that are of crucial importance for the protection of components exposed to high temperature oxidation and hot corrosion.

  7. THERMOELECTRIC PROPERTIES OF HOT-PRESSED p-TYPE Mg2Si0.3Sn0.7 SOLID SOLUTION

    Directory of Open Access Journals (Sweden)

    G. N. Isachenko

    2014-05-01

    Full Text Available It is shown that thermoelectric energy conversion which gives the possibility for utilizing a low potential heat is one of the ways for adoption of energy-saving technologies; and semiconductor materials with p-type and n-type conductivities having high thermoelectric figure of merit are necessary for operation of thermoelectric generators. The paper deals with possibility of usage of the p-Mg2Si0.3Sn0.7 solid solution (with a nanostructured modification as a couple for the well studied thermoelectric material based on n-Mg2Si-Mg2Sn. A technological scheme for fabrication of heavily doped Mg2Si0.3Sn0.7 solid solution of p-type by hot pressing from nanopowder is developed. The given technology has made it possible to reduce duration of a homogeneous material fabrication and has improved its physical and chemical properties. The samples were made by three ways: direct fusion for polycrystals fabrication; hot pressing from microparticles; nanostructuring, i.e. hot pressing from nanoparticles. By X-ray diffraction it is shown that sizes of structural elements in the fabricated samples are about 40 nm. The probe technique is used for measurement of electric conductivity and Seebeck coefficient. The stationary absolute method is used for measurement of thermal conductivity. Thermoelectric figure of merit is defined by measured values of kinetic coefficients in the temperatures range of 77 – 800 K. It was demonstrated, that electric conductivity, Seebeck coefficient and the power factor do not depend practically on a way of solid solution preparation. Thermal conductivity of samples pressed from nanoparticles has appeared to be higher, than of samples, obtained by direct fusion; i.e. in this case nanostructuring has not led to increase of thermoelectric figure of merit. The conclusion is drawn, that polycrystalline semiconductor Mg2Si0.3Sn0.7 can be used as a p-branch for a thermoelectric generator though nanostructuring has not led to the figure of

  8. Annealing effects on the structural and optical properties of vanadium oxide film obtained by the hot-filament metal oxide deposition technique (HFMOD)

    Energy Technology Data Exchange (ETDEWEB)

    Scarminio, Jair; Silva, Paulo Rogerio Catarini da, E-mail: scarmini@uel.br, E-mail: prcsilva@uel.br [Universidade Estadual de Londrina (UEL), PR (Brazil). Departamento de Fisica; Gelamo, Rogerio Valentim, E-mail: rogelamo@gmail.com [Universidade Federal do Triangulo Mineiro (UFTM), Uberaba, MG (Brazil); Moraes, Mario Antonio Bica de, E-mail: bmoraes@mailhost.ifi.unicamp.br [Universidade Estadual de Campinas (UNICAMP), SP (Brazil)

    2017-01-15

    Vanadium oxide films amorphous, nonstoichiometric and highly absorbing in the optical region were deposited on ITO-coated glass and on silicon substrates, by the hot-filament metal oxide deposition technique (HFMOD) and oxidized by ex-situ annealing in a furnace at 200, 300, 400 and 500 deg C, under an atmosphere of argon and rarefied oxygen. X-ray diffraction, Raman and Rutherford backscattering spectroscopy as well as optical transmission were employed to characterize the amorphous and annealed films. When annealed at 200 and 300 deg C the as-deposited opaque films become transparent but still amorphous. Under treatments at 400 and 500 deg C a crystalline nonstoichiometric V{sub 2}O{sub 5} structure is formed. All the annealed films became semiconducting, with their optical absorption coefficients changing with the annealing temperature. An optical gap of 2.25 eV was measured for the films annealed at 400 and 500 deg C. The annealing in rarefied oxygen atmosphere proved to be a useful and simple ex-situ method to modulate the structural and optical properties of vanadium oxide films deposited by HFMOD technique. This technique could be applied to other amorphous and non-absorbing oxide films, replacing the conventional and sometimes expensive method of modulate desirable film properties by controlling the film deposition parameters. Even more, the HFMOD technique can be an inexpensive alternative to deposit metal oxide films. (author)

  9. Selective Electron Beam Manufacturing of Ti-6Al-4V Strips: Effect of Build Orientation, Columnar Grain Orientation, and Hot Isostatic Pressing on Tensile Properties

    Science.gov (United States)

    Wang, J.; Tang, H. P.; Yang, K.; Liu, N.; Jia, L.; Qian, M.

    2018-03-01

    Many novel designs for additive manufacturing (AM) contain thin-walled (≤ 3 mm) sections in different orientations. Selective electron beam melting (SEBM) is particularly suited to AM of such thin-walled titanium components because of its high preheating temperature and high vacuum. However, experimental data on SEBM of Ti-6Al-4V thin sections remains scarce because of the difficulty and high cost of producing long, thin and smooth strip tensile specimens (see Fig. 1). In this study, 80 SEBM Ti-6Al-4V strips (180 mm long, 42 mm wide, 3 mm thick) were built both vertically (V-strips) and horizontally (H-strips). Their density, microstructure and tensile properties were investigated. The V-strips showed clearly higher tensile strengths but lower elongation than the H-strips. Hot isostatic pressing (HIP) produced the same lamellar α-β microstructures in terms of the average α-lath thickness in both types of strips. The retained prior-β columnar grain boundaries after HIP showed no measurable influence on the tensile properties, irrespective of their length and orientation, because of the formation of randomly distributed fine α-laths.[Figure not available: see fulltext.

  10. Creep Behavior and Durability of Cracked CMC

    Science.gov (United States)

    Bhatt, R. T.; Fox, Dennis; Smith, Craig

    2015-01-01

    To understand failure mechanisms and durability of cracked Ceramic matrix composites (CMCs), Melt Infiltration (MI) SiCSiC composites with Sylramic-iBN fibers and full Chemical vapour infiltration SiCSiC composites with Sylramic-ion bombarded BN (iBN) and Hi-Nicalon -S fibers were pre-cracked between 150 to 200 megapascal and then creep and Sustained Peak Low Cycle Fatigue (SPLCF) tested at 13150 C at stress levels from 35 to 103 megapascal for up to 200 hours under furnace and burner rig conditions. In addition creep testing was also conducted on pre-cracked full Chemical vapour infiltration SiCSiC composites at 14500 C between 35 and 103 megapascal for up to 200 hours under furnace conditions. If the specimens survived the 200 hour durability tests, then they were tensile tested at room temperature to determine their residual tensile properties. The failed specimens were examined by Scanning electron microscope (SEM) to determine the failure modes and mechanisms. The influence of crack healing matrix, fiber types, crack density, testing modes and interface oxidation on durability of cracked Ceramic matrix composites (CMCs) will be discussed.

  11. Electromagnetic pulsed thermography for natural cracks inspection

    Science.gov (United States)

    Gao, Yunlai; Tian, Gui Yun; Wang, Ping; Wang, Haitao; Gao, Bin; Woo, Wai Lok; Li, Kongjing

    2017-01-01

    Emerging integrated sensing and monitoring of material degradation and cracks are increasingly required for characterizing the structural integrity and safety of infrastructure. However, most conventional nondestructive evaluation (NDE) methods are based on single modality sensing which is not adequate to evaluate structural integrity and natural cracks. This paper proposed electromagnetic pulsed thermography for fast and comprehensive defect characterization. It hybrids multiple physical phenomena i.e. magnetic flux leakage, induced eddy current and induction heating linking to physics as well as signal processing algorithms to provide abundant information of material properties and defects. New features are proposed using 1st derivation that reflects multiphysics spatial and temporal behaviors to enhance the detection of cracks with different orientations. Promising results that robust to lift-off changes and invariant features for artificial and natural cracks detection have been demonstrated that the proposed method significantly improves defect detectability. It opens up multiphysics sensing and integrated NDE with potential impact for natural understanding and better quantitative evaluation of natural cracks including stress corrosion crack (SCC) and rolling contact fatigue (RCF). PMID:28169361

  12. Optical Fier Based System for Multiple Thermophysical Properties for Glove Box, Hot Cell and In-Pile Application

    Energy Technology Data Exchange (ETDEWEB)

    Ban, Heng

    2017-11-30

    Thermal diffusivity of materials is of interest in nuclear applications at temperatures in excess of 2000°C. Commercial laser flash apparatus (LFA) that heats samples with a furnace typically do not reach these elevated temperatures nor are they easily adapted to a glove-box or hot cell environment. In this research, we performed work on an experimental technique using single laser surface heating, i.e. heating the disk sample only at its front surface with the continuous wave (CW) laser, to allow measurement of thermal diffusivity at very high temperatures within a small chamber. Thermal diffusivity is measured using a separate pulsed laser on the front side and IR detector on the rear side. The new way of heating provides easy operation in comparison to other heating methods. The measurement of sample reference temperature is needed for the measured thermal diffusivity. A theoretical model was developed to describe transient heat transfer across the sample due to the laser pulse, starting from the steady state temperature of the sample heated by the CW laser. The experimental setup was established with a 500W CW laser and maximum 50 Joule pulse laser irradiated at the front surface of the sample. The induced temperature rise at the rear surface, along with the steady-state temperature at the front surface, was recorded for the determination of thermal diffusivity and the sample temperature. Three samples were tested in vacuum over a wide temperature range of 500°C to 2100°C, including graphite, Inconel 600 and tungsten. The latter two samples were coated with sprayed graphite on their front surfaces in order to achieve surface absorption/emission needs, i.e. high absorptivity of the front surface against relatively low emissivity of the rear surface. Thermal diffusivity of graphite determined by our system are within a 5% difference of the commercial LFA data at temperatures below 1300°C and agree well with its trend at higher temperatures. Good agreement

  13. Modelling of environmentally assisted cracking

    International Nuclear Information System (INIS)

    Aaltonen, P.; Saario, T.; Ehrnsten, U.; Haenninen, H.; Itaeaho, M.; Piippo, J.

    1998-01-01

    During the use of nuclear reactors the properties of the structural materials change. Variations in the operation environment, such as changes in water chemistry, may enhance the development and growth of flaws. Neutron radiation causes embrittlement for in-core vessel materials. Radiation, together with water chemistry, increases the possibility of stress corrosion cracking in stainless steels and superalloys used in the reactor internal parts. Research on structural materials endeavours to study the ageing mechanisms of materials, and the possibilities and methods of preventing or forecasting the damage caused to structures by ageing. (orig.)

  14. On Early Age Crack Formation in FRC Slabs

    DEFF Research Database (Denmark)

    Olesen, John Forbes; Stang, Henrik

    1997-01-01

    The problem of early age crack formation in FRC slabs due to restrained temperature and shrinkage deformations, is given an analytical treatment. A model taking into account the ageing properties of the tensile softening curve and the continued development in the temperature and shrinkage...... deformations after crack initiation, is presented. Based on this model a design strategy for FRC slabs is outlined....

  15. Modeling of air flow through a narrow crack

    International Nuclear Information System (INIS)

    Trojek, T.; Cechak, T.; Moucka, L.; Fronka, A.

    2004-01-01

    Radon transport in dwellings is governed to a significant extent by pressure differences and properties of transport pathways. A model of air flow through narrow cracks was created in order to facilitate prediction of air velocity and air flow. Theoretical calculations, based on numerical solution of a system of differential equations, were compared with measurements carried out on a window crack. (P.A.)

  16. From mud cracks to Optoelectronic devices- Our efforts in translating ...

    Indian Academy of Sciences (India)

    Prof.GU.Kulkarni

    ….a material that is transparent to visible light and yet electrically conducting. Not a trivial solution… ... ➢Poor mechanical properties (cracks when bent) – not good for flexible electronics. ITO: Limitations ..... Crack modeling. Prof. S. Tarafadar ...

  17. Inspecting cracks in foam insulation

    Science.gov (United States)

    Cambell, L. W.; Jung, G. K.

    1979-01-01

    Dye solution indicates extent of cracking by penetrating crack and showing original crack depth clearly. Solution comprised of methylene blue in denatured ethyl alcohol penetrates cracks completely and evaporates quickly and is suitable technique for usage in environmental or structural tests.

  18. Self-repair of cracks in brittle material systems

    Science.gov (United States)

    Dry, Carolyn M.

    2016-04-01

    One of the most effective uses for self repair is in material systems that crack because the cracks can allow the repair chemical to flow into the crack damage sites in all three dimensions. In order for the repair chemical to stay in the damage site and flow along to all the crack and repair there must be enough chemical to fill the entire crack. The repair chemical must be designed appropriately for the particular crack size and total volume of cracks. In each of the three examples of self repair in crackable brittle systems, the viscosity and chemical makeup and volume of the repair chemicals used is different for each system. Further the chemical delivery system has to be designed for each application also. Test results from self repair of three brittle systems are discussed. In "Self Repair of Concrete Bridges and Infrastructure" two chemicals were used due to different placements in bridges to repair different types of cracks- surface shrinkage and shear cracks, In "Airplane Wings and Fuselage, in Graphite" the composite has very different properties than the concrete bridges. In the graphite for airplane components the chemical also had to survive the high processing temperatures. In this composite the cracks were so definite and deep and thin that the repair chemical could flow easily and repair in all layers of the composite. In "Ceramic/Composite Demonstrating Self Repair" the self repair system not only repaired the broken ceramic but also rebounded the composite to the ceramic layer

  19. Fatigue crack growth in austenitic stainless steel piping

    International Nuclear Information System (INIS)

    Bethmont, M.; Cheissoux, J.L.; Lebey, J.

    1981-04-01

    The study presented in this paper is being carried out with a view to substantiating the calculations of the fatigue crack growth in pipes made of 316 L stainless steel. The results obtained may be applied to P.W.R. primary piping. It is divided into two parts. First, fatigue tests (cyclic pressure) are carried out under hot and cold conditions with straight pipes machined with notches of various dimensions. The crack propagation and the fatigue crack growth rate are measured here. Second, calculations are made in order to interpret experimental results. From elastic calculations the stress intensity factor is assessed to predict the crack growth rate. The results obtained until now and presented in this paper relate to longitudinal notches

  20. Modelling of Corrosion Cracks

    DEFF Research Database (Denmark)

    Thoft-Christensen, Palle

    Modelling of corrosion cracking of reinforced concrete structures is complicated as a great number of uncertain factors are involved. To get a reliable modelling a physical and mechanical understanding of the process behind corrosion in needed.......Modelling of corrosion cracking of reinforced concrete structures is complicated as a great number of uncertain factors are involved. To get a reliable modelling a physical and mechanical understanding of the process behind corrosion in needed....

  1. Cracking the Gender Codes

    DEFF Research Database (Denmark)

    Rennison, Betina Wolfgang

    2016-01-01

    extensive work to raise the proportion of women. This has helped slightly, but women remain underrepresented at the corporate top. Why is this so? What can be done to solve it? This article presents five different types of answers relating to five discursive codes: nature, talent, business, exclusion...... in leadership management, we must become more aware and take advantage of this complexity. We must crack the codes in order to crack the curve....

  2. Dynamic nanomechanical properties of novel Si-rich intermetallic coatings growth on a medical 316 LVM steel by hot dipping in a hypereutectic Al-25Si alloy.

    Science.gov (United States)

    Frutos, E; González-Carrasco, J L

    2015-06-01

    This aim of this study is to determine the elastoplastic properties of Ni-free Al3FeSi2 intermetallic coatings grown on medical stainless steel under different experimental conditions. Elastoplastic properties are defined by the plasticity index (PI), which correlates the hardness and the Young's modulus. Special emphasis is devoted to correlate the PI with the wear resistance under sliding contact, determined by scratch testing, and fracture toughness, determined by using a novel method based on successive impacts with small loads. With regard to the substrate, the developed coatings are harder and exhibit a lower Young's reduced modulus, irrespective of the experimental conditions. It has been shown that preheating of the samples prior to hot dipping and immersion influences the type and volume fraction of precipitates, which in turn also affect the nanomechanical properties. The higher the preheating temperature is, the greater the Young's reduced modulus is. For a given preheating condition, an increase of the immersion time yields a decrease in hardness. Although apparent friction coefficients of coated specimens are smaller than those obtained on AISI 316 LVM, they increase when using preheating or higher immersion times during processing, which correlates with the PI. The presence of precipitates produces an increase in fracture toughness, with values greater than those presented by samples processed on melted AlSi alloys with lower Si content (12 wt%). Therefore, these intermetallic coatings could be considered "hard but tough", suitable to enhance the wear resistance, especially when using short periods of immersion. Copyright © 2015 Elsevier Ltd. All rights reserved.

  3. SSRI Facilitated Crack Dancing

    Directory of Open Access Journals (Sweden)

    Ravi Doobay

    2017-01-01

    Full Text Available Choreoathetoid movement secondary to cocaine use is a well-documented phenomenon better known as “crack dancing.” It consists of uncontrolled writhing movements secondary to excess dopamine from cocaine use. We present a 32-year-old male who had been using cocaine for many years and was recently started on paroxetine, a selective serotonin reuptake inhibitor (SSRI for worsening depression four weeks before presentation. He had been doing cocaine every 2 weeks for the last three years and had never “crack danced” before this episode. The authors have conducted a thorough literature review and cited studies that suggest “crack dancing” is associated with excess dopamine. There has never been a documented case report of an SSRI being linked with “crack dancing.” The authors propose that the excess dopaminergic effect of the SSRI lowered the dopamine threshold for “crack dancing.” There is a communication with the Raphe Nucleus and the Substantia Nigra, which explains how the SSRI increases dopamine levels. This is the first documented case of an SSRI facilitating the “crack dance.”

  4. Characterization of Material Properties at Brady Hot Springs, Nevada by Inverse Modeling of Data from Seismology, Geodesy, and Hydrology

    Science.gov (United States)

    Wang, H. F.; Feigl, K. L.; Patterson, J.; Parker, L.; Reinisch, E. C.; Zeng, X.; Cardiff, M. A.; Fratta, D.; Lord, N. E.; Thurber, C. H.; Robertson, M.; Miller, D. E.; Akerley, J.; Kreemer, C.; Morency, C.; Davatzes, N. C.

    2017-12-01

    The PoroTomo project consists of poroelastic tomography by adjoint inverse modeling of data from seismology, geodesy, and hydrology. The goal of the PoroTomo project is to assess an integrated technology for characterizing and monitoring changes in the rock mechanical properties of an enhanced geothermal system in 3 dimensions with a spatial resolution better than 50 meters. In March 2016, we deployed the integrated technology in a 1500-by-500-by-400-meter volume at Brady. The 15-day deployment included 4 distinct time intervals with intentional manipulations of the pumping rates in injection and production wells. The data set includes: active seismic sources, fiber-optic cables for Distributed Acoustic Sensing (DAS) and Distributed Temperature Sensing (DTS) arranged vertically in a borehole to 400 m depth and horizontally in a trench 8700 m in length and 0.5 m in depth; 244 seismometers on the surface, 3 pressure sensors in observation wells, continuous geodetic measurements at 3 GPS stations, and 7 InSAR acquisitions. To account for the mechanical behavior of both the rock and the fluids, we are developing numerical models for the 3-D distribution of the material properties. We present an overview of results, including:Tomographic images of P-wave velocity estimated from seismic body waves [Thurber et al., this meeting].Tomographic images of phase velocity estimated from ambient noise correlation functions [Zeng et al., this meeting].Models of volumetric contraction to account for subsidence observed by InSAR and GPS [Reinisch et al., this meeting].Interpretation of pressure and temperature data [Patterson et al., this meeting].Taken together, these results support a conceptual model of highly permeable conduits along faults channeling fluids from shallow aquifers to the deep geothermal reservoir tapped by the production wells. The PoroTomo project is funded by a grant from the U.S. Department of Energy.

  5. Effect of Heat Treatment on the Microstructure and Mechanical Properties of Nitrogen-Alloyed High-Mn Austenitic Hot Work Die Steel

    Directory of Open Access Journals (Sweden)

    Yi Zhang

    2017-03-01

    Full Text Available In view of the requirements for mechanical properties and service life above 650 °C, a high-Mn austenitic hot work die steel, instead of traditional martensitic hot work die steel such as H13, was developed in the present study. The effect of heat treatment on the microstructure and mechanical properties of the newly developed work die steel was studied. The results show that the microstructure of the high-Mn as-cast electroslag remelting (ESR ingot is composed of γ-Fe, V(C,N, and Mo2C. V(C,N is an irregular multilateral strip or slice shape with severe angles. Most eutectic Mo2C carbides are lamellar fish-skeleton-like, except for a few that are rod-shaped. With increasing solid solution time and temperature, the increased hardness caused by solid solution strengthening exceeds the effect of decreased hardness caused by grain size growth, but this trend is reversed later. As a result, the hardness of specimens after various solid solution heat treatments increases first and then decreases. The optimal combination of hardness and austenitic grain size can be obtained by soaking for 2 h at 1170 °C. The maximum Rockwell hardness (HRC is 47.24 HRC, and the corresponding austenite average grain size is 58.4 μm. When the solid solution time is 3 h at 1230 °C, bimodality presented in the histogram of the austenite grain size as a result of further progress in secondary recrystallization. Compared with the single-stage aging, the maximum impact energy of the specimen after two-stage aging heat treatment was reached at 16.2 J and increased by 29.6%, while the hardness decreased by 1–2 HRC. After two-stage aging heat treatment, the hardness of steel reached the requirements of superior grade H13, and the maximum impact energy was 19.6% higher than that of superior grade H13, as specified in NADCA#207-2003.

  6. Cracks propagation by stress corrosion cracking in conditions of Boiling Water Reactor (BWR); Propagacion de grietas por corrosion bajo esfuerzo en condiciones de reactor de agua hirviente (BWR)

    Energy Technology Data Exchange (ETDEWEB)

    Fuentes C, P

    2003-07-01

    This work presents the results of the assays carried out in the Laboratory of Hot Cells of the National Institute of Nuclear Research (ININ) to a type test tube Compact Tension (CT), built in steel austenitic stainless type 304L, simulating those conditions those that it operates a Boiling Water Reactor (BWR), at temperature 288 C and pressure of 8 MPa, to determine the speed to which the cracks spread in this material that is of the one that different components of a reactor are made, among those that it highlights the reactor core vessel. The application of the Hydrogen Chemistry of the Water is presented (HWC) that is one alternative to diminish the corrosion effect low stress in the component, this is gets controlling the quantity of oxygen and of hydrogen as well as the conductivity of the water. The rehearsal is made following the principles of the Mechanics of Elastic Lineal Fracture (LEFM) that considers a crack of defined size with little plastic deformation in the tip of this; the measurement of crack advance is continued with the technique of potential drop of direct current of alternating signal, this is contained inside the standard Astm E-647 (Method of Test Standard for the Measurement of Speed of Growth of Crack by fatigue) that is the one that indicates us as carrying out this test. The specifications that should complete the test tubes that are rehearsed as for their dimensions, it forms, finish and determination of mechanical properties (tenacity to the fracture mainly) they are contained inside the norm Astm E-399, the one which it is also based on the principles of the fracture mechanics. The obtained results were part of a database to be compared with those of other rehearsals under different conditions, Normal Chemistry of the Water (NWC) and it dilutes with high content of O{sub 2}; to determine the conditions that slow more the phenomena of stress corrosion cracking, as well as the effectiveness of the used chemistry and of the method of

  7. Impact initiation of explosives and propellants via statistical crack mechanics

    Science.gov (United States)

    Dienes, J. K.; Zuo, Q. H.; Kershner, J. D.

    2006-06-01

    A statistical approach has been developed for modeling the dynamic response of brittle materials by superimposing the effects of a myriad of microcracks, including opening, shear, growth and coalescence, taking as a starting point the well-established theory of penny-shaped cracks. This paper discusses the general approach, but in particular an application to the sensitivity of explosives and propellants, which often contain brittle constituents. We examine the hypothesis that the intense heating by frictional sliding between the faces of a closed crack during unstable growth can form a hot spot, causing localized melting, ignition, and fast burn of the reactive material adjacent to the crack. Opening and growth of a closed crack due to the pressure of burned gases inside the crack and interactions of adjacent cracks can lead to violent reaction, with detonation as a possible consequence. This approach was used to model a multiple-shock experiment by Mulford et al. [1993. Initiation of preshocked high explosives PBX-9404, PBX-9502, PBX-9501, monitored with in-material magnetic gauging. In: Proceedings of the 10th International Detonation Symposium, pp. 459-467] involving initiation and subsequent quenching of chemical reactions in a slab of PBX 9501 impacted by a two-material flyer plate. We examine the effects of crack orientation and temperature dependence of viscosity of the melt on the response. Numerical results confirm our theoretical finding [Zuo, Q.H., Dienes, J.K., 2005. On the stability of penny-shaped cracks with friction: the five types of brittle behavior. Int. J. Solids Struct. 42, 1309-1326] that crack orientation has a significant effect on brittle behavior, especially under compressive loading where interfacial friction plays an important role. With a reasonable choice of crack orientation and a temperature-dependent viscosity obtained from molecular dynamics calculations, the calculated particle velocities compare well with those measured using

  8. A Three-Stage Mechanistic Model for Solidification Cracking During Welding of Steel

    Science.gov (United States)

    Aucott, L.; Huang, D.; Dong, H. B.; Wen, S. W.; Marsden, J.; Rack, A.; Cocks, A. C. F.

    2018-03-01

    A three-stage mechanistic model for solidification cracking during TIG welding of steel is proposed from in situ synchrotron X-ray imaging of solidification cracking and subsequent analysis of fracture surfaces. Stage 1—Nucleation of inter-granular hot cracks: cracks nucleate inter-granularly in sub-surface where maximum volumetric strain is localized and volume fraction of liquid is less than 0.1; the crack nuclei occur at solute-enriched liquid pockets which remain trapped in increasingly impermeable semi-solid skeleton. Stage 2—Coalescence of cracks via inter-granular fracture: as the applied strain increases, cracks coalesce through inter-granular fracture; the coalescence path is preferential to the direction of the heat source and propagates through the grain boundaries to solidifying dendrites. Stage 3—Propagation through inter-dendritic hot tearing: inter-dendritic hot tearing occurs along the boundaries between solidifying columnar dendrites with higher liquid fraction. It is recommended that future solidification cracking criterion shall be based on the application of multiphase mechanics and fracture mechanics to the failure of semi-solid materials.

  9. Ultrasonic sizing of fatigue cracks

    International Nuclear Information System (INIS)

    Burns, D.J.

    1983-12-01

    Surface and buried fatigue cracks in steel plates have been sized using immersion probes as transmitters-receivers, angled to produce shear waves in the steel. Sizes have been estimated by identifying the ultrasonic waves diffracted from the crack tip and by measuring the time taken for a signal to travel to and from the crack tip. The effects of compression normal to a fatigue crack and of crack front curvature are discussed. Another diffraction technique, developed by UKAEA, Harwell, is reviewed

  10. Numerical simulations of material mismatch and ductile crack growth

    Energy Technology Data Exchange (ETDEWEB)

    Oestby, Erling

    2002-07-01

    Both the global geometry and inhomogeneities in material properties will influence the fracture behaviour of structures in presence of cracks. In this thesis numerical simulations have been used to investigate how some aspects of both these issues affect the conditions at the crack-tip. The thesis is organised in an introduction chapter, summarising the major findings and conclusions, a review chapter, presenting the main aspects of the developments in the field of fracture mechanics, and three research papers. Paper I considers the effect of mismatch in hardening exponent on the local near-tip stress field for stationary interface cracks in bi-materials under small scale yielding conditions. It is demonstrated that the stress level in the weaker material increases compared to what is found in the homogeneous material for the same globally applied load level, with the effect being of increasing importance as the crack-tip is approached. Although a coupling between the radial and angular dependence of the stress fields exists, the evolving stress field can still be normalised with the applied J. The effect on the increase in stress level can closely be characterised by the difference in hardening exponent, {delta}n, termed the hardening mismatch, and is more or less independent of the absolute level of hardening in the two materials. Paper II and Ill deal with the effects of geometry, specimen size, hardening level and yield stress mismatch in relation to ductile crack growth. The ductile crack growth is simulated through use of the Gurson model. In Paper H the effect of specimen size on the crack growth resistance is investigated for deep cracked bend and shallow cracked tensile specimens. At small amounts of crack growth the effect of specimen size on the crack growth resistance is small, but a more significant effect is found for larger amounts of crack growth. The crack growth resistance decreases in smaller specimens loaded in tension, whereas the opposite is

  11. Crack growth rate of PWR piping

    International Nuclear Information System (INIS)

    Bethmont, M.; Doyen, J.J.; Lebey, J.

    1979-01-01

    The Aquitaine 1 program, carried out jointly by FRAMATOME and the CEA is intended to improve knowledge about cracking mechanisms in AISI 316 L austenitic stainless steel under conditions similar to those of the PWR environment (irradiation excluded). Experiments of fatigue crack growth are performed on piping elements, scale 1/4 of primary pipings, by means of internal hydraulic cyclic pressure. Interpretation of results requires a knowledge of the stress intensity factor Ksub(I) at the front of the crack. Results of a series of calculations of Ksub(I) obtained by different methods for defects of finite and infinite length (three dimensional calculations) are given in the paper. The following have been used: calculations by finite elements, calculations by weight function. Notches are machined on the test pipes, which are subjected to internal hydraulic pressure cycles, under cold conditions, to initiate a crack at the tip of the notch. They are then cycled at a frequency of 4 cycles/hour on on water demineralised loop at a temperature of 280 0 C, the pressure varying at each cycle between approximately 160 bars and 3 bars. After each test, a specimen containing the defect is taken from the pipe for micrographic analysis. For the first test the length of the longitudinal external defect is assumed infinite. The number of cycles carried out is 5880 cycles. Two defects are machined in the tube for the second test. The number of cycles carried out is N = 440. The tests are performed under hot conditions (T = 280 0 C). For the third test two defects are analysed under cold and hot conditions. The number of cycles carried out for the external defect is 7000 when hot and 90000 when cold. The number of cycles for the internal defect is 1650 when hot and 68000 when cold. In order to interpret the results, the data da/dN are plotted on a diagram versus ΔK. Comparisons are made between these results and the curves from laboratory tests

  12. Microstructure and properties of hot extruded Mg-3Zn-Y-xCu (x = 0, 1, 3, 5) alloys

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Bao-sheng; Kuang, Ya-fei; Fang, Da-qing; Chai, Yue-sheng [Taiyuan Univ. of Science and Technology (China). College of Materials Science and Engineering; Taiyuan Univ. of Science and Technology (China). Engineering Research Center for Magnesium Alloys of Shanxi Province; Zhang, Yue-zhong [Taiyuan Univ. of Science and Technology (China). Engineering Research Center for Magnesium Alloys of Shanxi Province; Taiyuan Univ. of Science and Technology (China). College of Chemical and Biological Engineering

    2017-04-15

    In petroleum drilling engineering, materials with high strength and rapid degradation are required for degradable fracturing ball applications. In this work, the microstructure, mechanical properties, and corrosion behavior of extruded Mg-3Zn-Y-xCu (x = 0, 1, 3, 5 weight percent) alloys are investigated using optical microscopy, scanning electronic microscopy equipped with energy dispersive X-ray spectroscopy, X-ray diffraction, transmission electronic microscopy, compression tests, electrochemical measurements, and hydrogen evolution tests, to explore their potential as excellent candidate alloys for degradable fracturing ball applications. It is found that the Mg-3Zn-Y alloy is mainly composed of α-Mg, Mg{sub 3}Zn{sub 3}Y{sub 2}, and Mg{sub 3}Zn{sub 6}Y phases. After Cu addition, a new MgZnCu phase is formed, while the Mg{sub 3}Zn{sub 3}Y{sub 2} phase disappears. The Mg-3Zn-Y-3Cu alloy shows the highest compressive strength (473 MPa) and yield strength (402 MPa), mainly attributed to the combined effect of the fine-grain and dispersed precipitation of Mg{sub 3}Zn{sub 6}Y and MgZnCu. The corrosion rate of Mg-3Zn-Y-3Cu reaches 0.41 mm day{sup -1} in 3.5 wt.% KCl solution. Consequently, Mg-3Zn-Y-3Cu alloy is a suitable degradable fracturing ball-seat material.

  13. A consistent partly cracked XFEM element for cohesive crack growth

    DEFF Research Database (Denmark)

    Asferg, Jesper L.; Poulsen, Peter Noe; Nielsen, Leif Otto

    2007-01-01

    Present extended finite element method (XFEM) elements for cohesive crack growth may often not be able to model equal stresses on both sides of the discontinuity when acting as a crack-tip element. The authors have developed a new partly cracked XFEM element for cohesive crack growth with extra...... enrichments to the cracked elements. The extra enrichments are element side local and were developed by superposition of the standard nodal shape functions for the element and standard nodal shape functions for a sub-triangle of the cracked element. With the extra enrichments, the crack-tip element becomes...... capable of modelling variations in the discontinuous displacement field on both sides of the crack and hence also capable of modelling the case where equal stresses are present on each side of the crack. The enrichment was implemented for the 3-node constant strain triangle (CST) and a standard algorithm...

  14. A crack growth evaluation method for interacting multiple cracks

    International Nuclear Information System (INIS)

    Kamaya, Masayuki

    2003-01-01

    When stress corrosion cracking or corrosion fatigue occurs, multiple cracks are frequently initiated in the same area. According to section XI of the ASME Boiler and Pressure Vessel Code, multiple cracks are considered as a single combined crack in crack growth analysis, if the specified conditions are satisfied. In crack growth processes, however, no prescription for the interference between multiple cracks is given in this code. The JSME Post-Construction Code, issued in May 2000, prescribes the conditions of crack coalescence in the crack growth process. This study aimed to extend this prescription to more general cases. A simulation model was applied, to simulate the crack growth process, taking into account the interference between two cracks. This model made it possible to analyze multiple crack growth behaviors for many cases (e.g. different relative position and length) that could not be studied by experiment only. Based on these analyses, a new crack growth analysis method was suggested for taking into account the interference between multiple cracks. (author)

  15. Crack resistance of austenitic pipes with circumferential through-wall cracks

    International Nuclear Information System (INIS)

    Foerster, K.; Grueter, L.; Setz, W.; Bhandari, S.; Debaene, J.P.; Faidy, C.; Schwalbe, K.H.

    1993-01-01

    For monotonously increasing load the correct evaluation of the crack resistance properties of a structure is essential for safety analyses. Considerable attention has been given to the through-wall case, since this is generally believed to be the controlling case with regard to complete pipe failure. The maximum load conditions for circumferential crack growth in pipes under displacement-controlled loadings has been determined. The need for crack resistance curves, measured on circumferentially through-wall cracked straight pipes of austenitic stainless steel 316L under bending, is emphasized by the limitation in the data range on small specimens and by the differences in the procedures. To answer open questions and to improve calculational methods a joint fracture mechanics program is being performed by Electricite de France, Novatome and Siemens-Interatom. The working program contains experimental and theoretical investigations on the applicability of small-specimen data to real structures. 10 refs., 10 figs., 4 tabs

  16. Coolant compatibility studies. The effect of irradiation on tensile properties and stress corrosion cracking sensitivity of martensitic steels. MANET 4 - complementary studies

    International Nuclear Information System (INIS)

    Nystrand, A.C.

    1994-02-01

    Tensile and stress corrosion cracking tests have been carried out on MANET-type (1.4914 and FV448) and reduced activation (LA12TaLC) high-chromium martensitic steels. The materials had previously been exposed up to 5000 h at ∼275 degrees C in the core, above the core and remote from the core of a high pressure water loop in the Studsvik R2 reactor. After the mechanical testing the materials were examined visually and metallographically. The steel samples exposed in the core section showed large increases in tensile yield strengths when tested at 250 degrees C. However, the magnitude of the radiation hardening was considerably smaller in the reduced activation steel compared to the commercial steels; this observation is consistent with published data on other high-chromium martensitic steels and is associated with the lower chromium content of the LA12TaLC steel (8.9%) compared with those of the commercial steels (10.6 and 11.3%). Irradiation assisted stress corrosion cracking (IASCC) was not detected in any of the stressed steel samples after autoclave testing for times up to 1500 h at 250 degrees C in air-saturated high purity water. This apparent resistance to IASCC may be due to the high chromium martensitic steels not being sensitized by the irradiation in a comparable manner to that shown by the austenitic steels. However, additional studies are required to clarify some of the existing uncertainties with respect to IASCC of these martensitic steels

  17. Are High-redshift Galaxies Hot? Temperature of z > 5 Galaxies and Implications for Their Dust Properties

    International Nuclear Information System (INIS)

    Faisst, Andreas L.; Capak, Peter L.; Masters, Daniel C.; Yan, Lin; Pavesi, Riccardo; Riechers, Dominik A.; Barišić, Ivana; Cooke, Kevin C.; Kartaltepe, Jeyhan S.

    2017-01-01

    Recent studies have found a significant evolution and scatter in the relationship between the UV spectral slope ( β UV ) and the infrared excess (IRX; L IR / L UV ) at z > 4, suggesting different dust properties of these galaxies. The total far-infrared (FIR) luminosity is key for this analysis, but it is poorly constrained in normal (main-sequence) star-forming z > 5 galaxies, where often only one single FIR point is available. To better inform estimates of the FIR luminosity, we construct a sample of local galaxies and three low-redshift analogues of z > 5 systems. The trends in this sample suggest that normal high-redshift galaxies have a warmer infrared (IR) spectral energy distribution (SED) compared to average z < 4 galaxies that are used as priors in these studies. The blueshifted peak and mid-IR excess emission could be explained by a combination of a larger fraction of metal-poor interstellar medium being optically thin to ultraviolet (UV) light and a stronger UV radiation field due to high star formation densities. Assuming a maximally warm IR SED suggests a 0.6 dex increase in total FIR luminosities, which removes some tension between the dust attenuation models and observations of the IRX− β relation at z > 5. Despite this, some galaxies still fall below the minimum IRX− β relation derived with standard dust cloud models. We propose that radiation pressure in these highly star-forming galaxies causes a spatial offset between dust clouds and young star-forming regions within the lifetime of O/B stars. These offsets change the radiation balance and create viewing-angle effects that can change UV colors at fixed IRX. We provide a modified model that can explain the location of these galaxies on the IRX− β diagram.

  18. Are High-redshift Galaxies Hot? Temperature of z > 5 Galaxies and Implications for Their Dust Properties

    Energy Technology Data Exchange (ETDEWEB)

    Faisst, Andreas L.; Capak, Peter L.; Masters, Daniel C. [Infrared Processing and Analysis Center, California Institute of Technology, Pasadena, CA 91125 (United States); Yan, Lin [Cahill Center for Astronomy and Astrophysics, California Institute of Technology, Pasadena, CA 91125 (United States); Pavesi, Riccardo; Riechers, Dominik A. [Department of Astronomy, Cornell University, Space Sciences Building, Ithaca, NY 14853 (United States); Barišić, Ivana [Max-Planck Institut für Astronomie, Königstuhl 17, D-69117, Heidelberg (Germany); Cooke, Kevin C.; Kartaltepe, Jeyhan S., E-mail: afaisst@ipac.caltech.edu [School of Physics and Astronomy, Rochester Institute of Technology, 84 Lomb Memorial Drive, Rochester, NY 14623 (United States)

    2017-09-20

    Recent studies have found a significant evolution and scatter in the relationship between the UV spectral slope ( β {sub UV}) and the infrared excess (IRX; L {sub IR}/ L {sub UV}) at z > 4, suggesting different dust properties of these galaxies. The total far-infrared (FIR) luminosity is key for this analysis, but it is poorly constrained in normal (main-sequence) star-forming z > 5 galaxies, where often only one single FIR point is available. To better inform estimates of the FIR luminosity, we construct a sample of local galaxies and three low-redshift analogues of z > 5 systems. The trends in this sample suggest that normal high-redshift galaxies have a warmer infrared (IR) spectral energy distribution (SED) compared to average z < 4 galaxies that are used as priors in these studies. The blueshifted peak and mid-IR excess emission could be explained by a combination of a larger fraction of metal-poor interstellar medium being optically thin to ultraviolet (UV) light and a stronger UV radiation field due to high star formation densities. Assuming a maximally warm IR SED suggests a 0.6 dex increase in total FIR luminosities, which removes some tension between the dust attenuation models and observations of the IRX− β relation at z > 5. Despite this, some galaxies still fall below the minimum IRX− β relation derived with standard dust cloud models. We propose that radiation pressure in these highly star-forming galaxies causes a spatial offset between dust clouds and young star-forming regions within the lifetime of O/B stars. These offsets change the radiation balance and create viewing-angle effects that can change UV colors at fixed IRX. We provide a modified model that can explain the location of these galaxies on the IRX− β diagram.

  19. Evolution of thermo-physical properties of Akuama (picralima nitida) seed and antioxidants retention capacity during hot air drying

    Science.gov (United States)

    Ndukwu, M. C.; Bennamoun, L.; Anozie, O.

    2018-05-01

    Interest in picralima nitida is growing over the years because of its therapeutic application in human and animal medicine. In many countries the dried seed is compounded and sold as drugs but there is limited information on the process variables associated with its thermal processing. The study therefore, is focused on the evolution of physical properties, heat and mass transfer coefficient, specific heat capacity, energy utilization and quality characteristics of the seed during oven and microwave drying. The goal is to generate data using theoretical and empirical steps for process model development that can be applied in dryer design. The results obtained showed that the coefficient of heat and mass transfer varied from 0.0421-1.326 W/m2 K and 1.49 × 10-7 - 8.47 × 10-6 m/s respectively while the specific heat capacity ranged between 1189 and 2531 J/ kg K. The volume of the seed shrank gradually with a non-linear exponential shape for all drying treatments. The intrinsic particle and bulk densities decreased while the porosity of the seed increased with drying period, indicating an increase in internal voids of the seeds. The energy and specific energy utilized for drying peaked after 14 h, 12 h and 7 h of continuous drying at 50, 60 and 70 °C for oven drying treatment. Effective moisture diffusivities for all treatments ranged from 5.37 × 10-10 - 1.45 × 10-7 m/s2 with activation energy of 27.82 kJ/mol and 20 W/g for oven and microwave respectively. Flavonoide was the least stable at high temperature among the screend compound.

  20. Distinguishing oil and water layers in a cracked porous medium using pulsed neutron logging data based on Hudson's crack theory

    Science.gov (United States)

    Zhang, Xueang; Yang, Zhichao; Tang, Bin; Wang, Renbo; Wei, Xiong

    2018-05-01

    During geophysical surveys, water layers may interfere with the detection of oil layers. In order to distinguish between oil and water layers in porous cracked media, research on the properties of the cracks, the oil and water layers, and their relation to pulsed neutron logging characteristics is essential. Using Hudson's crack theory, we simulated oil and water layers in a cracked porous medium with different crack parameters corresponding to the well log responses. We found that, in a cracked medium with medium-angle (40°-50°) cracks, the thermal neutron count peak value is higher and more sensitive than those in low-angle and high-angle crack environments; in addition, the thermal neutron density distribution shows more minimum values than in other cases. Further, the thermal neutron count and the rate of change for the oil layer are greater than those of the water layer, and the time spectrum count peak value for the water layer in middle-high-angle (40°-70°) cracked environments is higher than that of the oil layer. The thermal neutron density distribution sensitivity is higher in the water layer with a range of small crack angles (0°-30°) than in the oil layer with the same range of angles. In comparing the thermal neutron density distribution, thermal neutron count peak, thermal neutron density distribution sensitivity, and time spectrum maximum in the oil and water layers, we find that neutrons in medium-angle (40°-50°) cracked reservoirs are more sensitive to deceleration and absorption than those in water layers; neutrons in approximately horizontal (0°-30°) cracked water layers are more sensitive to deceleration than those in reservoirs. These results can guide future work in the cracked media neutron logging field.

  1. Facts and views on the role of anionic impurities, crack tip chemistry and oxide films in environmentally assisted cracking

    International Nuclear Information System (INIS)

    Aaltonen, P.; Bojinov, M.; Helin, M.

    2002-01-01

    The aim of this literature study has been to evaluate the level of understanding of the role of anionic impurities in environmentally assisted cracking (EAC) of iron- and nickel-based alloys in the coolant conditions of a boiling water reactor (BWR) - type nuclear power plant, mainly under normal water chemistry (NWC). The study has been motivated by a need to find the most relevant experimental approaches that can be applied when looking for correlations between crack growth rate and measurable electrochemical and chemical parameters. Special crack tip chemistry conditions are established, when trace amounts are present in the BWR coolant and become enriched within a crack. Anions may influence both the conductivity and the pH of the coolant within the crack. In addition, they may influence the composition, structure and properties of the oxide films formed on crack walls either directly via adsorption or incorporation or indirectly via the effect of changes in pH within the crack. Based on the proposed mechanisms for EAC, oxide films formed on crack wall surfaces are likely to play a key role in determing the crack growth rate of structural materials. The prediction of the influence of anionic impurities is thus likely to be facilitated by means of understanding their effect on the films on crack walls. One of the most promising approaches to experimentally clarify this influence is based on investigating the electrochemical behaviour of oxide films Fe- and Ni-based materials in high-temperature conditions simulating the special chemistry within a stress corrosion crack. Results from such studies should be compared and combined with ex situ analytical results obtained using modern electron microscopic techniques. In addition to crack growth, currently available electro-chemical techniques should also be applied to find out whether crack initiation can be explained and modelled on the basis of the electrochemical behaviour of oxide films. (orig.)

  2. Tensile property improvement of TWIP-cored three-layer steel sheets fabricated by hot-roll-bonding with low-carbon steel or interstitial-free steel

    Science.gov (United States)

    Park, Jaeyeong; Kim, Jung-Su; Kang, Minju; Sohn, Seok Su; Cho, Won Tae; Kim, Hyoung Seop; Lee, Sunghak

    2017-01-01

    TWIP-cored three-layer steel sheets were newly fabricated by hot rolling of TWIP steel sheet surrounded by low-carbon (LC) or interstitial-free (IF) steel sheets. TWIP/LC or TWIP/IF interfaces were well bonded without pores or voids, while a few pearlites were thinly formed along the interfaces. The strengths and elongation of the TWIP-cored sheets increased as the volume fraction of TWIP-cored region increased, and were also well matched with the ones calculated by a rule of mixtures based on volume fraction or force fraction. According to digital image correlation and electron back-scatter diffraction analyses, very high strain hardening effect in the initial deformation stage and active twin formation in the interfacial region beneficially affected the overall homogeneous deformation in the TWIP-cored sheets without any yield point phenomenon occurring in the LC sheet and serrations occurring in the TWIP sheet, respectively. These TWIP-cored sheets can cover a wide range of yield strength, tensile strength, and ductility levels, e.g., 320~498 MPa, 545~878 MPa, and 48~54%, respectively, by controlling the volume fraction of TWIP-cored region, and thus present new applications to multi-functional automotive steel sheets requiring excellent properties.

  3. A comparative study of the effect of spray drying and hot-melt extrusion on the properties of amorphous solid dispersions containing felodipine.

    Science.gov (United States)

    Mahmah, Osama; Tabbakh, Rami; Kelly, Adrian; Paradkar, Anant

    2014-02-01

    To compare the properties of solid dispersions of felodipine for oral bioavailability enhancement using two different polymers, polyvinylpyrrolidone (PVP) and hydroxypropyl methylcellulose acetate succinate (HPMCAS), by hot-melt extrusion (HME) and spray drying. Felodipine solid dispersions were prepared by HME and spray drying techniques. PVP and HPMCAS were used as polymer matrices at different drug : polymer ratios (1 : 1, 1 : 2 and 1 : 3). Detailed characterization was performed using differential scanning calorimetry, powder X-ray diffractometry, scanning electron microscopy and in-vitro dissolution testing. Dissolution profiles were evaluated in the presence of sodium dodecyl sulphate. Stability of different solid dispersions was studied under accelerated conditions (40°C/75% RH) over 8 weeks. Spray-dried formulations were found to release felodipine faster than melt extruded formulations for both polymer matrices. Solid dispersions containing HMPCAS exhibited higher drug release rates and better wettability than those produced with a PVP matrix. No significant differences in stability were observed except with HPMCAS at a 1 : 1 ratio, where crystallization was detected in spray-dried formulations. Solid dispersions of felodipine produced by spray drying exhibited more rapid drug release than corresponding melt extruded formulations, although in some cases improved stability was observed for melt extruded formulations. © 2013 Royal Pharmaceutical Society.

  4. Hot tearing susceptibility of binary Mg–Y alloy castings

    International Nuclear Information System (INIS)

    Wang, Zhi; Huang, Yuanding; Srinivasan, Amirthalingam; Liu, Zheng; Beckmann, Felix; Kainer, Karl Ulrich; Hort, Norbert

    2013-01-01

    Highlights: ► Quantitatively and qualitatively assessing hot tearing susceptibility for different alloys. ► Monitoring the hot tearing propagation process. ► Detecting the hot tearing initiation/onset temperature. ► Recording the stress and strain evolution during the casting solidification and the subsequent cooling. - Abstract: The influence of Y content on the hot tearing susceptibility (HTS) of binary Mg–Y alloys has been predicted using thermodynamic calculations based on Clyne and Davies model. The calculated results are compared with experimental results determined using a constrained rod casting (CRC) apparatus with a load cell and data acquisition system. Both thermodynamic calculations and experimental measurements indicate that the hot tearing susceptibility as a function of Y content follows the “λ” shape. The experimental results show that HTS first increases with increase in Y content, reaches the maximum at about 0.9 wt.%Y and then decreases with further increase the Y content. The maximum susceptibility observed in Mg–0.9 wt.%Y alloy is attributed to its coarsened columnar microstructure, large solidification range and small amount of eutectic at the time of hot tearing. The initiation of hot cracks is monitored during CRC experiments. It corresponds to a drop in load increment on the force curves. The critical solid fractions at which the hot cracks are initiated are in the range from 0.9 to 0.99. It is also found that it decreases with increasing the content of Y. The hot cracks propagate along the dendritic or grain boundaries through the interdendritic separation or tearing of interconnected dendrites. Some of the formed cracks are possible to be healed by the subsequent refilling of the remained liquids

  5. Influence of structure and properties of tubular billets of the 12 Kh 18N10T steel on deformability of tubes at cold-rolling mills

    International Nuclear Information System (INIS)

    Vil'yams, O.S.; Bol'shova, N.M.; Olejnik, O.V.; Velikotnaya, E.S.

    1979-01-01

    Metallographic analysis of the defects of the ''oblique cracks'' type on the surface of hot-rolled tubes of the 12Kh18N10T steel has been carried out. Recommended is the complex of mechanical properties and the structure factors (grain size) of conversion hot-rolled tubes, providing the combination of ductility and high rapture strength during rolling at pilger mills. At a grain size not coarser than number 5, a billet must have σsub(T) 5 >=40 %. Hot-rolled coarse-grained billet is not recommended for warm rolng because of high strain hardening

  6. The positive effect of hot isostatic pressing on improving the anisotropies of bending and impact properties in selective laser melted Ti-6Al-4V alloy

    International Nuclear Information System (INIS)

    Wu, Ming-Wei; Lai, Pang-Hsin

    2016-01-01

    Selective laser melting (SLM) is a versatile additive manufacturing process for fabricating solid or porous metallic materials with complicated three-dimensional shapes. SLM Ti alloys, particularly Ti-6Al-4V, and other alloys have been manufactured and analyzed in numerous studies. However, the high anisotropy of the microstructures and inconsistent mechanical properties of SLM materials have been extensively reported, and these disadvantages could prohibit its widespread use. To clarify how to alleviate the anisotropic behaviors of SLM materials, the main objective of this study was to evaluate the influences of hot isostatic pressing (HIP) on the microstructure, densification, bending strength, impact toughness, and fracture be