  1. Effect of Cr content on the SHS reaction of Cr-Ti-C system

    International Nuclear Information System (INIS)

    Zhang, W.N.; Wang, H.Y.; Wang, P.J.; Zhang, J.; He, L.; Jiang, Q.C.

    2008-01-01

    The effect of Cr content on the self-propagating high temperature synthesis (SHS) reaction of Cr-Ti-C system has been investigated in this research. The thermodynamics calculation indicates that the TiC possesses higher thermodynamic stability than the Cr 23 C 6 , Cr 7 C 3 and Cr 3 C 2 phases, and the formation of TiC is the most exothermic. Additionally, the adiabatic combustion temperature (T ad ) decreases with the increase of Cr content except for the phase transition regions. The XRD result shows that the type of products synthesized by SHS changes that a higher Cr content corresponds to higher chromium carbide. When Cr content is 10 wt.%, only solid solution (Ti,Cr)C ss is formed in the products. When Cr content increases to 20 wt.%, besides (Ti,Cr)C ss , the Cr 7 C 3 phase is also detected. With the Cr content further increasing to 30 and 40 wt.%, the products consist of (Ti,Cr)C ss , Cr 23 C 6 , Cr 7 C 3 and Cr, and therefore, much higher chromium carbide is synthesized. When Cr content reaches 50 wt.%, however, the Cr 7 C 3 disappears and the final products become (Ti,Cr)C ss , Cr 23 C 6 and Cr. Moreover, when Cr content increases from 10 to 20 wt.%, the lattice parameter of (Ti,Cr)C ss decreases, while it increases when the Cr content ranges from 20 to 50 wt.%. Furthermore, the microstructure shows that the TiC particulate size decreases from ∼8 to ∼2 μm with the increase of Cr content from 10 to 50 wt.%, and the morphology shape of TiC particulate becomes more and more spherical

  2. Effect of free Cr content on corrosion behavior of 3Cr steels in a CO2 environment

    Science.gov (United States)

    Li, Wei; Xu, Lining; Qiao, Lijie; Li, Jinxu

    2017-12-01

    The corrosion behavior of 3Cr steels with three microstructures (martensite, bainite, combined ferrite and pearlite) in simulated oil field formation water with a CO2 partial pressure of 0.8 MPa was investigated. The relationships between Cr concentrations in corrosion scales and corrosion rates were studied. The precipitated phases that contained Cr were observed in steels of different microstructures, and free Cr content levels were compared. The results showed that steel with the martensite microstructure had the highest free Cr content, and thus had the highest corrosion resistance. The free Cr content of bainite steel was lower than that of martensite steel, and the corrosion rate of bainite steel was higher than that of martensite steel. Because large masses of Cr were combined in ferrite and pearlite steel, the corrosion rates of ferrite and pearlite steel were the highest. Free Cr content in steel affects its corrosion behavior greatly.

  3. Influences of Cr content and PWHT on microstructure and oxidation behavior of stainless steel weld overlay cladding materials in high temperature water

    Energy Technology Data Exchange (ETDEWEB)

    Cao, X.Y.; Ding, X.F. [National Center for Materials Service Safety, University of Science and Technology Beijing, 30 Xueyuan Road, 100083 Beijing (China); Lu, Y.H., E-mail: lu_yonghao@mater.ustb.edu.cn [National Center for Materials Service Safety, University of Science and Technology Beijing, 30 Xueyuan Road, 100083 Beijing (China); Zhu, P. [Suzhou Nuclear Power Research Institute Co. Ltd., 1788 Xihuan Road, 215004 Suzhou (China); Shoji, T. [National Center for Materials Service Safety, University of Science and Technology Beijing, 30 Xueyuan Road, 100083 Beijing (China); Fracture and Reliability Research Institute, Tohoku University, 6-6-01 Aramaki Aoba, Aoba-ku, Sendai City 980-8579 (Japan)

    2015-12-15

    Influences of Cr content and post weld heat treatment (PWHT) on microstructure and oxidation behavior of stainless steel cladding materials in high temperature water were investigated. The amounts of metal oxidized and dissolved were estimated to compare the oxidation behaviors of cladding materials with different Cr contents and PWHT. The results indicated that higher Cr content led to formation of more ferrite content, and carbides were found along δ/γ phase interface after PWHT. Higher Cr content enhanced the pitting resistance and compactness of the oxide film to reduce metal amount oxidized and dissolved, which mitigated the weight changes and the formation of Fe-rich oxides. PWHT promoted more and deeper pitting holes along the δ/γ phase interface due to formation of carbides, which resulted in an increase in metal amount oxidized and dissolved, and were also responsible for more Fe-rich oxides and higher weight changes. - Highlights: • The amounts of metal oxidized and metal dissolved were estimated. • Higher Cr content increased ferrite content and PWHT led to formation of carbides. • PWHT promoted more and deeper pitting holes along the δ/γ phase interface. • Lower Cr content and PWHT promoted the metal amounts oxidized and dissolved. • Lower Cr content and PWHT increased weight changes and Fe-rich film formation.

  4. Modeling on Fe-Cr microstructure: evolution with Cr content

    International Nuclear Information System (INIS)

    Diaz Arroyo, D.; Perlado, J.M.; Hernandez-Mayoral, M.; Caturla, M.J.; Victoria, M.

    2007-01-01

    Full text of publication follows: The minimum energy configuration of interstitials in the Fe-Cr system, which is the base for the low activation steels being developed in the European fusion reactor materials community, is determined by magnetism. Magnetism plays also a role in the atomic configurations found with increasing Cr content. Results will be presented from a program in which the microstructure evolution produced after heavy ion irradiation in the range from room temperature to 80 K is studied as a function of the Cr content in alloys produced under well controlled conditions, i.e. from high purity elements and with adequate heat treatment. It is expected that these measurements will serve as matrix for model validation. The first step in such modeling sequence is being performed by modeling the evolution of displacement cascades in Fe using the Dudarev -Derlet and Mendeleev potentials for Fe and the Caro potential for Fe-Cr. It is of particular interest to study the evolution of high-energy cascades, where an attempt will be made to clarify the role of the evolution of sub-cascades. Kinetic Monte Carlo (kMC) techniques will be used then to simulate the defect evolution. A new parallel kMC code is being implemented for this purpose. (authors)

  5. Fe, Cr, Ni, Cu, Mg, Al, Ti, and S contents in plants and soil of heaps of nickel smelting works

    Energy Technology Data Exchange (ETDEWEB)

    Banasova, V; Hajduk, J

    1977-01-01

    The writers established the Fe, Ce, Cr, Ni, Ca, Mg, Al, Ti and S contents in the neopedon of heaps piling up from processing of nickel ore as well as in the plants: Cardaria draba, Salsola cali, Agropyrum repens, Bromus erectus, Calamagrostis epigeios, Cynodon dactylon and Matricaria inodora, growing on such heaps. Ca, Mg and S contents were found to be higher in dicotyledons and Fe, Al, Ti, Ni and Cr contents higher in monocotyledons. The analyzed dicotyledons appeared to be concentrators of Ca and S. Highest Fe, Al, Ti, Ni and Cr contents were found in individuals of the species Agropyrum repens. The neopedon as well as the plants had extraordinarily high Cr concentrations. The species Salsola cali has been found to possess an unusually higher affinity to the dump substrate after processing of nickel ore and to be a concentrator of Mg. 16 references, 1 table.

  6. FP corrosion dependence on carbon and chromium content in Fe-Cr steel

    International Nuclear Information System (INIS)

    Sasaki, Koei; Tanigaki, Takanori; Fukumoto, Ken-ichi; Uno, Masayoshi

    2015-01-01

    In an attempt to investigate Cs or Cs-Te corrosion dependence on chromium or carbon content in Fe-Cr steel, cesium and Cs-Te corrosion test were performed to three specimens, Fe-9Cr-0C, Fe-9Cr-0.14C and Fe-13Cr-0.14C, for 100 hours at 973K in simulated high burn-up fuel pin environment. Cesium corrosion depth has no dependence on chromium or carbon content in Fe-Cr steel. Cs-Te corrosion was appeared in only Fe-13Cr-0.14C which has chromium carbides ranged along grain boundary. Appearance of the Cs-Te corrosion was determined by distribution or arrangement of chromium carbides which depends on chromium and carbon content. (author)

  7. The effect of Si content on the fracture toughness of CrAlN/Si3N4 coatings

    International Nuclear Information System (INIS)

    Liu, S.; Wheeler, J. M.; Davis, C. E.; Clegg, W. J.; Zeng, X. T.

    2016-01-01

    CrAlN/Si 3 N 4 nanocomposite coatings with different Si contents were deposited to understand how Si influences the microstructure and mechanical behaviour of the coatings, in particular, the fracture toughness. The coating composition, chemical bonding, microstructure, and mechanical properties were studied by energy dispersive spectroscopy, x-ray photoelectron spectroscopy, x-ray diffraction, and nanoindentation, respectively. Using a micro double cantilever beam sample, it was found that the fracture toughness of CrAlN/Si 3 N 4 coatings was higher than that of both the CrN and CrAlN coatings and increased with increasing Si content. Cross-sectional transmission electron microscopy suggested that this was caused by the suppression of cracking at columnar boundaries

  8. Ni, Co, and Cr contents in the soil and in some plants of Dobsina asbestos heaps

    Energy Technology Data Exchange (ETDEWEB)

    Banasova, V

    1978-01-01

    Results of analyses of substrates of heaps after mining and working of asbestos as well as of two plants viz. Melilotus officinalis Lam. and Calamagrostis epigeios Roth. for Ni, Co and Cr. Ni and Co concentrations in the analyzed plants and heap substrates were found to be higher than in common soils and in plants growing at unsophisticated localities. The values ascertained are at the same time lower than in soils and plants on serpentines. There were very low Cr contents in substrates of the studied heaps. On the contrary, in both analyzed plant species Cr concentration was found to be much higher than in the investigated heap substrates. At that locality Melilotus officinalis and Calamagrostis epigeios appear to be concentrators of chromium.

  9. Effect of silicon contents on the microstructures and mechanical properties of heat affected zones for 9Cr2WVTa steels

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Jian [Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Science, 110016, Shenyang (China); Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Science, 110016, Shenyang (China); Lu, Shanping, E-mail: shplu@imr.ac.cn [Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Science, 110016, Shenyang (China); Rong, Lijian [Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Science, 110016, Shenyang (China); Li, Dianzhong [Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Science, 110016, Shenyang (China)

    2016-03-15

    The weldability of 9Cr2WVTa steels with silicon content varying from 0.30 wt.% to 1.36 wt.% was studied to meet the requirement of Generation-Ⅳ nuclear reactor. Samples of enlarged HAZs were fabricated by a thermal-mechanical simulator based on the simulation and measurement of non-equilibrium phase transformation. The content of δ-ferrite in the HAZs increased with the silicon content and the peak temperature of welding thermal cycle. The impact toughness in the HAZs decreased in different degrees when the δ-ferrite exhibits stripe (lower than 4.82%) or blocky types (higher than 4.82%). Post weld heat treatment (PWHT) has a significant role on improving the toughness. Adding silicon content increased the volume of δ-ferrite and therefore, decreased the tensile strength of the HAZs for 9Cr2WVTa steels. Silicon also as solid solution strengthening element increased the tensile strength. The 9Cr2WVTa steel has good weldability when the silicon content is lower than 0.60 wt.%. - Highlights: • The weldability of 9Cr2WVTa steel with different silicon contents was studied. • The impact toughness decreased in different degrees owing to the δ-ferrite. • PWHT has a significant role on improving the impact toughness. • The 9Cr2WVTa steel with silicon content not exceeding 0.60 wt.% has good weldability.

  10. The influence of Cr content on the mechanical properties of ODS ferritic steels

    Science.gov (United States)

    Li, Shaofu; Zhou, Zhangjian; Jang, Jinsung; Wang, Man; Hu, Helong; Sun, Hongying; Zou, Lei; Zhang, Guangming; Zhang, Liwei

    2014-12-01

    The present investigation aimed at researching the mechanical properties of the oxide dispersion strengthened (ODS) ferritic steels with different Cr content, which were fabricated through a consolidation of mechanical alloyed (MA) powders of 0.35 wt.% nano Y2O3 dispersed Fe-12.0Cr-0.5Ti-1.0W (alloy A), Fe-16.0Cr-0.5Ti-1.0W (alloy B), and Fe-18.0Cr-0.5Ti-1.0W (alloy C) alloys (all in wt.%) by hot isostatic pressing (HIP) with 100 MPa pressure at 1150 °C for 3 h. The mechanical properties, including the tensile strength, hardness, and impact fracture toughness were tested by universal testers, while Young's modulus was determined by ultrasonic wave non-destructive tester. It was found that the relationship between Cr content and the strength of ODS ferritic steels was not a proportional relationship. However, too high a Cr content will cause the precipitation of Cr-enriched segregation phase, which is detrimental to the ductility of ODS ferritic steels.

  11. Effect of tungsten content on the microstructure and tensile properties of Ni–xW–6Cr alloys

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Shulin [Center for Thorium Molten Salt Reactor System, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Ye, Xiang-Xi, E-mail: yexiangxi@sinap.ac.cn [Center for Thorium Molten Salt Reactor System, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Jiang, Li [Center for Thorium Molten Salt Reactor System, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Cui, Chuanyong [Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Li, Zhijun, E-mail: lizhijun@sinap.ac.cn [Center for Thorium Molten Salt Reactor System, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Huang, Hefei; Leng, Bin [Center for Thorium Molten Salt Reactor System, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Zhou, Xingtai, E-mail: zhouxingtai@sinap.ac.cn [Center for Thorium Molten Salt Reactor System, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China)

    2016-02-08

    Ni–xW–6Cr alloys have been considered as one of the potential structural materials for molten salt techniques, whereas their microstructure and mechanical performance have not been sufficiently studied. In this study, the microstructure and tensile deformation behavior of Ni–(10–35 wt%)W–6Cr alloys have been systematically investigated. The phase diagram calculations indicated that the solubility limit of W is 34 wt% in Ni–xW–6Cr alloy. α-W phase is formed in the matrix while the W content exceeds such limit. The fracture of the Ni–(10–35 wt%)W–6Cr alloys at room temperature is in the transgranular ductile fracture mode. The tensile properties of alloys, except for the elongation of Ni–35 wt%W–6Cr alloy, are improved with the increase of W content, which can be explained by the larger lattice distortion, the lower stack fault energy and the higher length fraction of twin boundaries (Σ3 and Σ9 type) in the Ni–(10–35 wt%)W–6Cr alloys caused by the addition of more W. The reduced elongation of the Ni–35 wt%W–6Cr alloy is ascribed to the particles in α-W phase which act as the main nucleation sites for cracking.

  12. The effect of Si content on the fracture toughness of CrAlN/Si{sub 3}N{sub 4} coatings

    Energy Technology Data Exchange (ETDEWEB)

    Liu, S. [Singapore Institute of Manufacturing Technology, 71 Nanyang Drive, Singapore 638075 (Singapore); Gordon Laboratory, Department of Materials Science and Metallurgy, 27 Charles Babbage Rd., Cambridge CB3 0FS (United Kingdom); Wheeler, J. M. [Laboratory for Nanometallurgy, ETH Zürich, Vladimir-Prelog-Weg 5, 8093 Zurich (Switzerland); Davis, C. E.; Clegg, W. J. [Gordon Laboratory, Department of Materials Science and Metallurgy, 27 Charles Babbage Rd., Cambridge CB3 0FS (United Kingdom); Zeng, X. T. [Singapore Institute of Manufacturing Technology, 71 Nanyang Drive, Singapore 638075 (Singapore)

    2016-01-14

    CrAlN/Si{sub 3}N{sub 4} nanocomposite coatings with different Si contents were deposited to understand how Si influences the microstructure and mechanical behaviour of the coatings, in particular, the fracture toughness. The coating composition, chemical bonding, microstructure, and mechanical properties were studied by energy dispersive spectroscopy, x-ray photoelectron spectroscopy, x-ray diffraction, and nanoindentation, respectively. Using a micro double cantilever beam sample, it was found that the fracture toughness of CrAlN/Si{sub 3}N{sub 4} coatings was higher than that of both the CrN and CrAlN coatings and increased with increasing Si content. Cross-sectional transmission electron microscopy suggested that this was caused by the suppression of cracking at columnar boundaries.

  13. Alloying effect on hardening of martensite stainless steels of the Fe-Cr-Ni and Fe-Cr-Co systems

    International Nuclear Information System (INIS)

    Fel'dgandler, Eh.G.; Savkina, L.Ya.

    1975-01-01

    The effect of alloying elements is considered on the γ → a-transformation and hardening of certain compositions of the ternary Fe-Cr-Ni- and Fe-Cr-Co alloy systems with the martensite structure. In martensite Fe-(10 to 14)% Cr base steels the elements Co, Cu, W, Ni, Mo, Si, Cr decrease, Mn, Si, Mo, Cu increase, and Cr, Ni, Co decrease the temperature of α → γ-transition. The tempering of martensite steels of the Fe-Cr-Ni- and Fe-Cr-Co-systems containing 10 to 14% Cr, 4 to 9% Ni, and 7 to 12% Co does not lead to hardening. Alloyage of the martensite Fe-Cr-Ni-, Fe-Cr-Co- and Fe-Cr-Ni-Co base separately with Mo, W, Si or Cu leads to a hardening during tempering, the hardening being the higher, the higher is the content of Ni and, especially, of Co. The increase in the content of Mo or Si produces the same effect as the increase in the Co content. In on Fe-Cr-Co or Fe-Cr-Ni-Co based steels alloyed with Mo or Si, two temperature ranges of ageing have been revealed which, evidently, have different hardening natures. The compositions studied could serve as the base material for producing maraging stainless steels having a complex variety of properties

  14. Comparison of secondary system piping Cr content with inspection data

    International Nuclear Information System (INIS)

    Tapping, R.L.; Mitchell, A.M.

    1997-06-01

    For several years a number of Ontario Hydro and CANDU-6 stations have been sampling sections of secondary-side piping for chromium content. Several hundred of these measurements have been made, and comparisons with inspection data drawn. There is special interest in chromium concentrations in the range 0.01< Cr<0.1 wt.%, in order to better define the effect of trace chromium content on susceptibility to flow-assisted corrosion. (author)

  15. Effect of Cr content on the FAC of pipe material at 150 .deg. C

    International Nuclear Information System (INIS)

    Park, Tae Jun; Kim, Hong Pyo

    2013-01-01

    Flow accelerated corrosion (FAC) of the carbon steel piping in nuclear power plants (NPPs) has been major issue in nuclear industry. During the FAC, a protective oxide layer on carbon steel dissolves into flowing water leading to a thinning of the oxide layer and accelerating corrosion of base material. As a result, severe failures may occur in the piping and equipment of NPPs. Effect of alloying elements on FAC of pipe materials was studied with rotating cylinder FAC test facility at 150 .deg. C and at flow velocity of 4m/s. The facility is equipped with on line monitoring of pH, conductivity, dissolved oxygen(DO) and temperature. Test solution was the demineralized water, and DO concentration was less than 1 ppb. Surface appearance of A 106 Gr. B which is used widely in secondary pipe in NPPs showed orange peel appearance, typical appearance of FAC. The materials with Cr content higher than 0.17wt.% showed pit. The pit is thought to early degradation mode of FAC. The corrosion product within the pit was enriched with Cr, Mo, Cu, Ni and S. But S was not detected in SA336 F22V with 2.25wt.% Cr. The enrichment of Cr and Mo seemed to be related with low, solubility of Cr and Mo compared to Fe. Measured FAC rate was compared with Ducreaux's relationship and showed slightly lower FAC rate than Ducreaux's relationship

  16. Distribution of Heavy Metal Content Hg and Cr of Environmental Samples at Surabaya Area

    International Nuclear Information System (INIS)

    Agus Taftazani

    2007-01-01

    Determination of Hg and Cr content of Surabaya river and coastal environmental samples using Instrumental Neutron Activation Analysis (INAA) have been done. The environmental samples were water, sediment, Eichhornia crassipes (Mart) Solmms, Rhizophora stylosa, Johnius (Johnieops) borneensis fish, and Moolgarda delicate fish at 12 locations selected of Surabaya area. Dry powder of sediment and biotic samples and concentrate water samples was irradiated by neutron flux 1.05 x 10 11 n.cm -2 .det -1 during 12 hours. The analytical result showed that the concentration of the heavy metals of river water are smaller than Perda Surabaya City No. 02/2004 for the 4 th level water which are Hg (0.005 ppm) and Cr (1.000 ppm). All locations coastal water samples have Hg and Cr concentrations are higher than Kepmen LH No.51/2004 Hg (0.001 ppm) and Cr (0.005 ppm). The Hg concentration of fish samples have exceeded the threshold according to Kep. Dirjen POM No.03725/B/SK/VII/89 about the maximum concentration of metal pollution in food. The concentration of heavy metals in sediment, Eichhornia crassipes (Mart) Solmms and Rhizophora stylosa are not regulated, so then heavy metals pollution can not be referred to. The concentration of Hg and Cr elements of water samples are smaller than that of biotic and sediment samples. The distribution factor (F d ) is bigger than bioaccumulation factor (F b ). (author)

  17. Effect of Cr Contents and Heat Treating on Reverted Austenite in Maraging Steel Weldments

    Science.gov (United States)

    Kim, S. W.; Lee, H. W.

    2018-05-01

    By conducting flux cored arc welding (FCAW) on maraging steels with Cr contents of 1.4 and 5.2 wt%, this study observed the effects of Cr content and heat treating on reverted austenite formation in welded maraging steel. Aging treatment was carried out at the temperatures of 450, 480 and 530 °C for 3 h in each condition. As the aging temperature increased, reverted austenite was formed along the interdendritic and intercellular grain boundaries, and the proportion of reverted austenite increased with increasing Cr addition. The aging process led to the segregation of Ti and Mo along the interdendritic and intercellular grain boundaries. Some of the welded specimens were subjected to solution heat treatment at 820 and 1250 °C for 1 h after welding, resulting in a decrease in reverted austenite fraction.

  18. Effect of Cr3C2 content on the microstructure and properties of Mo2NiB2-based cermets

    International Nuclear Information System (INIS)

    Xie, Lang; Li, XiaoBo; Zhang, Dan; Yang, ChengMing; Yin, FuCheng; Xiangtan Univ., Hunan; Xiangtan Univ., Hunan; Xiao, YiFeng

    2015-01-01

    Four series of Mo 2 NiB 2 -based cermets with Cr 3 C 2 addition of between 0 and 7.5 wt.% in 2.5 wt.% increments were studied by means of scanning electron microscopy, energy dispersive X-ray analysis and X-ray diffractometry. The transverse rupture strength and hardness were also measured. It was found that Cr 3 C 2 completely dissolved in Mo 2 NiB 2 -based cermets. Cr 3 C 2 addition improved the wettability of the Ni binder phase on the Mo 2 NiB 2 hard phase, which resulted in a decrease in the porosity and an increase in the phase uniformity. The cermets with 2.5 wt.% Cr 3 C 2 content showed relatively fine grains and almost full density. A high Cr 3 C 2 content resulted in the formation of M 6 C (M = Mo, Cr, Ni) phase. In addition, energy dispersive X-ray spectroscopy results showed that the content of Mo in the binder decreased with increasing Cr 3 C 2 content. The cermets with 2.5 wt.% Cr 3 C 2 addition exhibited the highest transverse rupture strength of 2210 MPa, whereas the cermets without Cr 3 C 2 addition exhibited the highest hardness.

  19. The influence of Cr content in Fe-Cr-Co alloys on the magnetic properties and Moessbauer effect

    International Nuclear Information System (INIS)

    Yan Yong; Sho Hanru; Li Dexin; Li Guodong; Li Dongshen; Zhen Jinshan

    1986-01-01

    Fe-xCr-8Co (x=24, 25, 27, 29 and 32 wt%) permanent magnetic alloys have been studied by Moessbauer effect, magnetic balance and vibrating-sample magnetometer. It is indicated that the optimum permanent magnetic properties obtained for the composition of the alloys at about x=27. The value of Cr content in these alloys sigificantly influences the average hyperfine field, the saturation magnetic moment, the proportion of paramagnetic phase and orientation of magnetic moment in these alloys. The intrinsic coercive force is gradually reduced with the temperature decreasing from 290 to 77 K. The paramagnetic peak in the spectrum disappears at about 125 K. The certain mechanism has been suggested to explain the experimental results. (Auth.)

  20. Influence of boron content on the microstructure and tribological properties of Cr-B-N coatings in water lubrication

    Science.gov (United States)

    Ma, Qiang; Zhou, Fei; Gao, Song; Wu, Zhiwei; Wang, Qianzhi; Chen, Kangmin; Zhou, Zhifeng; Li, Lawrence Kwok-Yan

    2016-07-01

    Cr-B-N coatings with different boron contents were deposited on Si(1 0 0) wafers and 316 L stainless steels using unbalanced magnetron sputtering system by way of adjusting the CrB2 target currents. The microstructure and mechanical properties of Cr-B-N coatings were investigated by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), white light interferometric three dimensional profilometer and nano-indentation tester, respectively. The tribological properties of Cr-B-N/SiC tribopairs in water were studied using ball-on-disk tribometer. The results showed that the Cr-B-N coatings showed a fine nanocomposite structure consisted of CrN nanograins and amorphous BN phase regardless of boron contents, and the typical columnar structure became featureless with increasing the CrB2 target current. The hardness and reduced elastic modulus first increased to 28.9 GPa and 330 GPa at the CrB2 target current of 2 A, and then decreased gradually with further increasing the CrB2 target current to 4 A. As compared with the CrN/SiC tribopairs, the lowest friction coefficient of Cr-B-N/SiC ball tribopairs in water was 0.15, and the wear resistance of Cr-B-N coatings was effectively enhanced.

  1. Properties of welded joints of 2,25Cr-1Mo steel with various carbon content

    International Nuclear Information System (INIS)

    Vornovitskij, I.N.; Brodetskaya, E.Z.; Pozdnyakova, A.S.

    1980-01-01

    Properties of welded joints of 2,25 Cr - 1 Mo steel pipelines with different carbon content are considered. It is shown that application of electrodes developed in some countries for welding permits in many cases to exclude heat treatment of welded joints owing to high ductility of weld deposited metal. To improve the ductility, it is necessary to limit both carbon content down to 0,03-0,06% and detrimental elements (sulfur, phosphorus). Heat affected zone hardness may be increased at the expense of carbon. Weld deposited metal possesses the highest long-term strength at the given test temperature; in this case long-term strength of welded joints and base metal is practically the same. The long-term strength of high-carbon steel is higher at the test temperature of 565 deg C as compared to mean-carbon and low-carbon steels, whose long-term strength is practically equal at this temperature. The long-term strength of high-carbon and mean-carbon steels is practically the same and higher as compared with low-carbon one at the test temperature of 510 deg C

  2. Magnetic features of Fe-Cr-Co alloys with tailoring chromium content fabricated by spark plasma sintering

    International Nuclear Information System (INIS)

    Rastabi, Reza Amini; Ghasemi, Ali; Tavoosi, Majid; Ramazani, Mazaher

    2017-01-01

    Structural and magnetic characterization of Fe-Cr-Co alloys during milling, annealing and consolidation processes was the goal of this study. In this regards, different powder mixtures of Fe 80−x Cr x Co 20 (15≤x≤35) were mechanically milled in a planetary ball mill and then were consolidated by spark plasma sintering (SPS). The produced samples were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). According to achieved results, the structure of as-milled samples in different compositions consists of single α phase solid solution with coercivity and saturation of magnetization in the range of 110–200 Oe and 150–220 emu/g, respectively. The magnetic properties of consolidated samples depend on the kinds of formed precipitates in microstructure and the maximum values of coercive force and saturation of magnetization obtained in Fe 55 Cr 25 Co 20 magnetic (with single α phase) alloy were 107 Oe and Ms 172 emu/g, respectively. In fact, the formation of non-magnetic σ and γ phases has a destructive effect on magnetic properties of consolidated samples with higher Cr content. Since such magnet requires less cobalt, and contains similar magnetic feature with superior ductility compare to the AlNiCo 5, it could be considered as a promising candidate for employing instead of AlNiCo 5. - Highlights: • Milled samples consist of single phase α-solid solution. • Saturation of magnetization of Fe 65 Cr 15 Co 20 reached to 172 emu/g. • Fe 65 Cr 15 Co 20 alloy is the suitable composition fabricated by SPS.

  3. Influence of Nb content on grain size and mechanical properties of 18 wt% Cr ferritic stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Kang, Y. [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Mao, W.M., E-mail: weiminmao@263.net [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Chen, Y.J. [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Jing, J.; Cheng, M. [Taizhou Xinyu Precision Manufacture Company Limited, Jiangyan 225500, Jiangsu (China)

    2016-11-20

    The influence of Nb contents between 0.20 and 1.20 wt% on the grain size and mechanical properties of 18 wt% Cr ferritic stainless steel produced by investment casting was investigated. The average grain sizes of the three steels decreased apparently with increasing Nb content mainly due to the increasing number of pre-existing oxides formed at higher temperature, which were more likely to be the nuclei of heterogeneous nucleation. The thermodynamic analysis of Nb(C,N) formation was in conformity to the experimental result that the Nb(C,N) precipitates became larger with increasing Nb content. The as-cast specimen with the smallest grain size of steel C had the worse tensile strength and elongation in comparison with the as-cast specimens of steels A and B, mostly owing to the catenarian and dendritic Nb(C,N) particles distributed densely at the grain boundaries. The mechanical properties of specimens were not improved remarkably through high temperature solid-solution, whereas the mechanical properties of normalized specimens in the three steels were improved to different degrees. The coalescence and sparse distribution of smaller precipitates at grain boundaries after normalizing effectively weakened the local stress concentration arising from the reticular distribution of particles. The normalized specimen of steel A with 0.24 wt% Nb still showed good mechanical properties. Normalizing at 850 °C for 2 h is the appropriate heat treatment for the 18 wt% Cr ferritic stainless steel. The comparatively rational Nb content of the ferritic stainless steel is between 0.20 and 0.40 wt% for investment casting production.

  4. Magnetic features of Fe-Cr-Co alloys with tailoring chromium content fabricated by spark plasma sintering

    Energy Technology Data Exchange (ETDEWEB)

    Rastabi, Reza Amini; Ghasemi, Ali, E-mail: ali13912001@yahoo.com; Tavoosi, Majid; Ramazani, Mazaher

    2017-03-15

    Structural and magnetic characterization of Fe-Cr-Co alloys during milling, annealing and consolidation processes was the goal of this study. In this regards, different powder mixtures of Fe{sub 80−x}Cr{sub x}Co{sub 20} (15≤x≤35) were mechanically milled in a planetary ball mill and then were consolidated by spark plasma sintering (SPS). The produced samples were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometer (VSM). According to achieved results, the structure of as-milled samples in different compositions consists of single α phase solid solution with coercivity and saturation of magnetization in the range of 110–200 Oe and 150–220 emu/g, respectively. The magnetic properties of consolidated samples depend on the kinds of formed precipitates in microstructure and the maximum values of coercive force and saturation of magnetization obtained in Fe{sub 55}Cr{sub 25}Co{sub 20} magnetic (with single α phase) alloy were 107 Oe and Ms 172 emu/g, respectively. In fact, the formation of non-magnetic σ and γ phases has a destructive effect on magnetic properties of consolidated samples with higher Cr content. Since such magnet requires less cobalt, and contains similar magnetic feature with superior ductility compare to the AlNiCo 5, it could be considered as a promising candidate for employing instead of AlNiCo 5. - Highlights: • Milled samples consist of single phase α-solid solution. • Saturation of magnetization of Fe{sub 65}Cr{sub 15}Co{sub 20} reached to 172 emu/g. • Fe{sub 65}Cr{sub 15}Co{sub 20} alloy is the suitable composition fabricated by SPS.

  5. Oxidation-resistant Ge-doped silicide coating on Cr-Cr2Nb alloys by pack cementation

    International Nuclear Information System (INIS)

    He Yirong

    1997-01-01

    The halide-activated pack cementation process was modified to produce a Ge-doped silicide diffusion coating on Cr-Cr 2 Nb alloys in a single processing step. The morphology and composition of the coating depended both on the pack composition and processing schedule and also on the composition and microstructure of the substrate. Higher Ge content in the pack suppressed the formation of CrSi 2 and reduced the growth kinetics of the coating. Ge was not homogeneously distributed in the coatings. Under cyclic and isothermal oxidation conditions, the Ge-doped silicide coating protected the Cr-Nb alloys from significant oxidation and from pesting by the formation of a Ge-doped silica film. (orig.)

  6. Effect of carbon content on microstructure and mechanical properties of hot-rolled low carbon 12Cr-Ni stainless steel

    International Nuclear Information System (INIS)

    Zheng, H.; Ye, X.N.; Li, J.D.; Jiang, L.Z.; Liu, Z.Y.; Wang, G.D.; Wang, B.S.

    2010-01-01

    Research highlights: → Hot-rolled ultra low carbon martensite is characterized by dislocation cells substructure. → The formation of dislocation cells is attributed to high Ms and low interstitial atoms content. → Hot-rolled ultra low carbon 12Cr-Ni stainless steel has excellent impact toughness. → Delta ferrite deteriorates the impact toughness of hot-rolled 12Cr-Ni stainless steel. - Abstract: 12Cr-Ni stainless steels containing different carbon contents from 0.004 wt.% to 0.034 wt.% were hot-rolled and air-cooled. Their corresponding microstructures were observed with optical microscope and transmission electron microscope, and the Vickers hardness, tensile and impact tests were also carried out. It was found that the martensitic morphology was significantly influenced by carbon content. The as-received ultra low carbon martensite in the steel containing 0.004 wt.% C is characterized by dislocation cells substructure. The formation of dislocation cells is attributed to high martensite finishing point (above 400 deg. C) and low interstitial atoms content. On the other hand, the martensite in the steel containing 0.034 wt.% C consists mainly of typical martensite laths because of low martensite finishing point and high interstitial atoms content which hinder dislocation motion. Furthermore, carbon content has an evident effect on the mechanical properties of 12Cr-Ni steels. The hardness and strength of the as-received steels increase with an increase in carbon content, but their elongation and impact toughness decrease with the carbon content. The steel containing 0.004 wt.% C has excellent impact toughness due to the ultra low carbon content in the martensite composed of dislocation cells.

  7. Structure and grindability of dental Ti-Cr alloys

    International Nuclear Information System (INIS)

    Hsu, H.-C.; Wu, S.-C.; Chiang, T.-Y.; Ho, W.-F.

    2009-01-01

    The purpose of this study was to investigate the structure and microhardness of a series of binary Ti-Cr alloys with Cr contents up to 30 wt%. In addition, the grindability was also evaluated using an electric dental handpiece with SiC wheels, with the goal of developing a titanium alloy with better mechanical properties and machinability than commercially pure titanium (c.p. Ti), a metal generally considered to be difficult to machine. This study evaluated the phase and structure of Ti-Cr alloys, using an X-ray diffraction (XRD) for phase analysis and optical microscope for microstructure of the etched alloys. Grindability was evaluated by measuring the amount of metal volume removed after grinding for 1 min. Results indicated that the structure of Ti-Cr alloys is sensitive to the Cr content. The cast c.p. Ti has a hexagonal α phase. With 5 wt% Cr, metastable β phase starts to be retained. With Cr contents higher than 10 wt%, the equi-axed β phase is almost entirely retained. In addition, athermal ω phase was found in the Ti-5Cr and Ti-10Cr alloys. The largest quantity of ω phase and highest microhardness were found in Ti-10Cr alloy. The grinding rate of the Ti-Cr alloys showed a similar tendency to the microhardness. The Ti-10Cr alloy exhibited the best grindability, especially at 1000 m/min, which presumably due to the brittle nature of the alloy containing the ω phase in the β matrix.

  8. Cr(III) and Cr(VI) in leather and elicitation of eczema

    DEFF Research Database (Denmark)

    Hansen, Malene Barré; Menne, Torkil; Johansen, Jeanne Duus

    2006-01-01

    The aim of the present study was to investigate the relation between the content of Cr(VI) and soluble Cr(III) in leather and the ability of the leather to elicit eczema in chromium allergic patients. An array of chromium-tanned leather samples was analysed for the content of total Cr(VI) and sol...

  9. Tribological behaviour at high temperature of hard CrAlN coatings doped with Y or Zr

    International Nuclear Information System (INIS)

    Sánchez-López, J.C.; Contreras, A.; Domínguez-Meister, S.; García-Luis, A.; Brizuela, M.

    2014-01-01

    The tribological properties of CrAlN, CrAlYN and CrAlZrN coatings deposited by direct current reactive magnetron sputtering are studied by means of pin-on-disc experiments at room temperature, 300, 500 and 650 °C using alumina balls as counterparts. The influence of the metallic composition (Al, Y and Zr) on the friction, wear properties and oxidation resistance is studied by means of scanning electron microscopy, energy dispersive X-ray analysis and Raman analysis of the contact region after the friction tests. The results obtained allow us to classify the tribological behaviour of the CrAl(Y,Zr)N coatings into three groups according to the nature of the dopant and aluminium content. The sliding wear mechanism is characterized by the formation of an overcoat rich in chromium and aluminium oxides whose particular composition is determined by the initial chemical characteristics of the coating and the testing temperature. The fraction of Cr 2 O 3 becomes more significant as the Al content decreases and the temperature increases. The addition of Y, and particularly Zr, favours the preferential formation of Cr 2 O 3 versus CrO 2 leading to a reduction of friction and wear of the counterpart. Conversely, the tribological behaviour of pure CrAlN coatings is characterized by higher friction but lower film wear rates as a result of higher hardness and major presence of aluminium oxides on the coating surface. - Highlights: • Comparative tribological study at high temperature of CrAlN, CrAlYN and CrAlZrN films • Fraction of Cr 2 O 3 raises as the Al content decreases and the temperature increases. • Zr doping favours lower and steady friction coefficient due to higher Cr 2 O 3 formation. • Sliding wear mechanism becomes predominantly abrasive as the Al content increases. • Excellent tribological performance of CrAlN doped with low Y contents (≈ 2 at.%)

  10. Structural and morphological evolution in magnetron co-sputtered (Zn, Cr)O films

    International Nuclear Information System (INIS)

    Hu, Y M; Chiou, J W; Han, T C; Chen, Y T; Hsu, C W; Chen, G J; Chou, W Y; Chang, J; Hsu, J Y; Yu, Y C

    2008-01-01

    In this study, x-ray diffraction, scanning electron microscopy, micro-Raman spectroscopy, x-ray absorption near-edge structure and particle-induced x-ray emission are used to characterize the microstructure of (Zn, Cr)O films prepared using a co-sputtering method. We found that the Cr ions did not substitute for the Zn sites but instead formed Cr nano-particles and secondary oxide phases (SOPs) of Cr 2 O 3 and/or ZnCr 2 O 4 in co-sputtered Zn 1-x Cr x O films with Cr content x ≥ 0.1. Evidence is presented for the evolution of SOPs formed in (Zn, Cr)O films with increasing Cr sputtering power. Based on the inspection of the Cr and Zn contents in (Zn, Cr)O films, we conclude that the formation of the Cr 2 O 3 phase is driven by a substantial increase in the atomic ratio of Cr/Zn, followed by the formation of a ZnCr 2 O 4 phase promoted by a higher content of Cr than of Zn in film with increasing Cr sputtering power. It seems that a strong preference of Cr for octahedral rather than tetrahedral coordination with oxygen would trigger the formation of SOPs rather than the substitution of Cr into Zn sites and could be an obstacle for achieving a real Cr-substituted ZnO dilute magnetic oxide.

  11. Silicon content design of CrSiN films for good anti-corrosion and anti-wear performances in NaOH solution

    Science.gov (United States)

    Wang, Haixin; Ye, Yuwei; Wang, Chunting; Zhang, Guangan; Liu, Wei

    2018-06-01

    The CrSiN films with different silicon contents were fabricated by medium frequency magnetron sputtering. The 304L stainless steel and Si (1 0 0) wafer were used for substrate specimens. Film plasticity, corrosion and tribological behaviors in 0.1 M NaOH solution were systematically investigated. Results show that the plasticity of CrN film could be improved by the addition of silicon. During the corrosion test, with the increase of silicon content, the corrosion current density exhibited a descending trend and impedance presented a rising trend. The COF and wear rate of as-prepared CrSiN film initially decreased and then increased as the silicon content increased. The CrSiN film with 12.7 at.% Si exhibited the lowest COF of 0.04 and a wear rate of 6.746  ×  10‑8 mm3 Nm‑1 in 0.1 M NaOH solution.

  12. Molecular dynamics study on threshold displacement energies in Fe-Cr alloys

    Science.gov (United States)

    Fu, Jiawei; Ding, Wenyi; Zheng, Mingjie; Mao, Xiaodong

    2018-03-01

    The threshold displacement energies (Ed) of Fe and Cr atoms in Fe-Cr alloys with Cr contents ranging from 0% to 21% have been obtained with molecular dynamics (MD) method. The values of Ed have been calculated along the three high-symmetry crystallographic directions [0 0 1], [0 1 1] and [1 1 1], a slightly 2° tilt from these directions, and a high-index crystallographic directions [1 3 5]. The results showed that [0 1 1] crystallographic direction had the highest Ed among the three high-symmetry directions in each Cr content alloy. Fe-9Cr had higher weighted average Ed than the other Cr content alloys for both Fe and Cr PKA due to its statistically high Ed along the [0 1 1] crystallographic direction up to 44.3 eV. And the statistical analysis on the primary damage configuration demonstrated that 〈1 1 0〉Fe-Fe dumbbells were the dominant defect structures after relaxation. These data can enrich the database of Ed in Fe-Cr alloys and have potential applications in guiding the optimization design of radiation-resistant RAFM steels.

  13. EFFECT OF REACTIVE MATERIALS ON THE CONTENT OF SELECTED ELEMENTS IN INDIAN MUSTARD GROWN IN CR(VI-CONTAMINATED SOILS

    Directory of Open Access Journals (Sweden)

    Maja Radziemska

    2016-04-01

    Full Text Available Reactive materials represent a promising agent for environmental co-remediation. The research was aimed to determine the influence of hexavalent chromium in doses of 0, 25, 50, and 150 mg Cr(VI.kg-1 of soil as well as zero valent-iron, and lignite additives on the content of macroelements in the Indian mustard (Brassica juncea L.. The average accumulation of the analysed elements in Indian mustard grown in Cr(VI contaminated soil were found to follow the decreasing order Mg>Na>P>Ca>K. Soil contamination at 150 mg Cr(VI.kg-1 of soil led to the highest increase in magnesium, calcium, sodium, and potassium content in Indian mustard. The application of zero-valent iron had a positive influence on the average Na and K content of the tested plant. The application of lignite had a positive influence on the average magnesium, sodium and calcium content in the above-ground parts of the studied plant. In the non-amended treatments (without reactive materials, the increasing rates of chromium (VI had an explicitly positive effect on the content of phosphorous and sodium in Indian mustard.

  14. Removal of hexavalent Cr by coconut coir and derived chars--the effect of surface functionality.

    Science.gov (United States)

    Shen, Ying-Shuian; Wang, Shan-Li; Tzou, Yu-Min; Yan, Ya-Yi; Kuan, Wen-Hui

    2012-01-01

    The Cr(VI) removal by coconut coir (CC) and chars obtained at various pyrolysis temperatures were evaluated. Increasing the pyrolysis temperature resulted in an increased surface area of the chars, while the corresponding content of oxygen-containing functional groups of the chars decreased. The Cr(VI) removal by CC and CC-derived chars was primarily attributed to the reduction of Cr(VI) to Cr(III) by the materials and the extent and rate of the Cr(VI) reduction were determined by the oxygen-containing functional groups in the materials. The contribution of pure Cr(VI) adsorption to the overall Cr(VI) removal became relatively significant for the chars obtained at higher temperatures. Accordingly, to develop a cost-effective method for removing Cr(VI) from water, the original CC is more advantageous than the carbonaceous counterparts because no pyrolysis is required for the application and CC has a higher content of functional groups for reducing Cr(VI) to less toxic Cr(III). Copyright © 2011 Elsevier Ltd. All rights reserved.

  15. Influence of chemical composition in crystallographic texture Fe-Cr-Mo alloys; Influencia da composicao quimica na textura cristalografica de ligas Fe-Cr-Mo

    Energy Technology Data Exchange (ETDEWEB)

    Moura, L.B.; Guimaraes, R.F. [Instituto Federal de Educacao, Ciencia e Tecnologia do Ceara, Fortaleza, CE (Brazil). Dept. da Industria; Abreu, H.F.G. [Universidade Federal do Ceara (UFC), Fortaleza, CE (Brazil)

    2010-07-01

    The use of steels with higher contents of Mo in the oil industry has been an alternative to reduce the effect of naphthenic corrosion in refining units. The addition of Mo in Fe-Cr alloys in the same manner that increases resistance to corrosion naphthenic causes some difficulties such as difficulty of forming, welding and embrittlement. In this work, experimental ingots of Fe-Cr-Mo alloys (Cr - 9, 15 and 17%, Mo - 5, 7 and 9%) were melted in vacuum induction furnace and hot and cold rolled in a laboratory rolling mill. The influence of chemical composition on crystallographic texture of samples subjected to the same thermo-mechanical treatment was analyzed by x-ray diffraction. The results indicate that fiber (111) becomes more intense with increasing Mo and/or Cr contents. (author)

  16. Bonding and bio-properties of hybrid laser/magnetron Cr-enriched DLC layers

    Energy Technology Data Exchange (ETDEWEB)

    Jelinek, Miroslav, E-mail: jelinek@fzu.cz [Institute of Physics, Academy of Sciences of the Czech Republic, v.v.i, Na Slovance 2, 18221 Prague (Czech Republic); Czech Technical University in Prague, Faculty of Biomedical Engineering, nam. Sitna 3105, 27201 Kladno (Czech Republic); Zemek, Josef [Institute of Physics, Academy of Sciences of the Czech Republic, v.v.i, Na Slovance 2, 18221 Prague (Czech Republic); Vandrovcová, Marta; Bačáková, Lucie [Institute of Physiology of the Czech Academy of Sciences of the Czech Republic, v.v.i., Videnska 1083, 14220 Prague 4 (Czech Republic); Kocourek, Tomáš; Remsa, Jan; Písařík, Petr [Institute of Physics, Academy of Sciences of the Czech Republic, v.v.i, Na Slovance 2, 18221 Prague (Czech Republic); Czech Technical University in Prague, Faculty of Biomedical Engineering, nam. Sitna 3105, 27201 Kladno (Czech Republic)

    2016-01-01

    Chromium-enriched diamond-like carbon (DLC) layers were prepared by a hybrid technology using a combination of pulsed laser deposition (PLD) and magnetron sputtering. XRD revealed no chromium peaks, indicating that the layers are mostly amorphous. Carbon (sp{sup 2} and sp{sup 3} bonds) and chromium bonds were determined by XPS from C 1s, O 1s, and Cr 2p photoelectron peaks. Depending on the deposition conditions, the concentration of Cr in DLC layers moved from zero to 10 at.% for as-received sample surfaces, and to about 31 at.% after mild sputter-cleaning by argon ion cluster beam. It should be noted that the most stable Cr{sup 3+} bonding state is in Cr{sub 2}O{sub 3} and Cr(OH){sub 3}, and that there is the toxic Cr{sup 6+} state in CrO{sub 3}. The surface content of hexavalent chromium in the Cr 2p3/2 spectra is rather low, but discernible. The population density of Saos-2 cells was the highest in samples containing higher concentrations of chromium 7.7 and 10 at.%. This means that higher concentrations of chromium supported the cell adhesion and proliferation. In addition, as revealed by a LIVE/DEAD viability/cytotoxicity kit, the cells on all Cr-containing samples maintained high viability (96 to 99%) on days 1 and 3 after seeding. However, this seemingly positive cell behavior could be associated with the risk of dedifferentiation and oncogenic transformation of cells. - Highlights: • DLC and chromium-enriched DLC layers were prepared by hybrid laser–magnetron deposition. • The content of chromium in DLC varied up to 10 at.% (31 at.% after ion beam sputtering). • The surface content of toxic hexavalent chromium in the Cr 2p3/2 spectra is rather low but discernible. • Higher concentrations of chromium supported the cell adhesion and proliferation. • Cells on all Cr-containing samples maintained high viability (96 to 99%).

  17. The influence of nickel content on microstructures of Fe-Cr-Ni austenitic alloys irradiated with nickel ions

    International Nuclear Information System (INIS)

    Muroga, T.; Yoshida, N.; Garner, F.A.

    1990-11-01

    The objectives of this effort is to identify the mechanisms involved in the radiation-induced evolution of microstructure in materials intended for fusion applications. The results of this study are useful in interpreting the results of several other ongoing experiments involving either spectral or isotopic tailoring to study the effects of helium on microstructure evolution. Ion-irradiated Fe-15Cr-XNi (X = 20, 35, 45, 60, 75) ternary alloys and a 15Cr-85Ni binary alloy were examined after bombardment at 675 degree C and compared to earlier observations made on these same alloys after irradiation in EBR-II at 510 or 538 degree C. The response of the ion-irradiated microstructures to nickel content appears to be very consistent with that of neutron irradiation even though there are four orders of magnitude difference in displacement rate and over 200 degree C difference in temperature. It appears that the transition to higher rates of swelling during both types of irradiation is related to the operation of some mechanisms that is not directly associated with void nucleation. 6 refs., 8 figs

  18. Chromium Extraction via Chemical Processing of Fe-Cr Alloys Fine Powder with High Carbon Content

    Science.gov (United States)

    Torres, D. M.; Navarro, R. C. S.; Souza, R. F. M.; Brocchi, E. A.

    2017-06-01

    Ferrous alloys are important raw materials for special steel production. In this context, alloys from the Fe-Cr system, with typical Cr weight fraction ranging from 0.45 to 0.95, are prominent, particularly for the stainless steel industry. During the process in which these alloys are obtained, there is considerable production of fine powder, which could be reused after suitable chemical treatment, for example, through coupling pyrometallurgical and hydrometallurgical processes. In the present study, the extraction of chromium from fine powder generated during the production of a Fe-Cr alloy with high C content was investigated. Roasting reactions were performed at 1073 K, 1173 K, and 1273 K (800 °C, 900 °C, and 1000 °C) with 300 pct (w/w) excess NaOH in an oxidizing atmosphere (air), followed by solubilization in deionized water, selective precipitation, and subsequent calcination at 1173 K (900 °C) in order to convert the obtained chromium hydroxide to Cr2O3. The maximum achieved Cr recovery was around 86 pct, suggesting that the proposed chemical route was satisfactory regarding the extraction of the chromium initially present. Moreover, after X-ray diffraction analysis, the final produced oxide has proven to be pure Cr2O3 with a mean crystallite size of 200 nm.

  19. Content of Cr, Cu, Pb, and Zn on Pacific white shrimp cultured in modern farm at BLUPPB, Karawang, West Java

    Science.gov (United States)

    Takarina, N. D.; Rahman, A.; Siswanting, T.; Pin, T. J.

    2018-03-01

    Heavy metal is one of the hazardous substances which often found in shrimp farm. Since this shrimp become mostly favorable food, it is necessary to determine the content of metal in this shrimps. This research was aimed to determine the content of Cr, Cu, Pb, and Zn on Pacific white shrimp cultured on the modern farm at BLUPPB, Karawang, West Java. Samples were taken from five farms. During transport, samples were kept in a more relaxed box. Farms used were designed using black plastic as the bottom layer to separate contact with soil. Heavy metal of Cr, Cu, Pb, and Zn on shrimp meat was analyzed using Atomic Absorption Spectrophotometry method. The content of Cr was ranged from 0.06 – 0.38 ppm and Pb were 0.02 – 0.05 ppm. The content of Cu was ranged from 1.89 – 15.25 ppm and Zn were 2.16 – 3.92 ppm. According to government rules and literature, those content were below a threshold which was 0.4 ppm for Cu, 0.5 ppm for Pb, 20 ppm for Cu and 0.2 ppm for Zn.

  20. Correlation between bulk- and surface chemistry of Cr-tanned leather and the release of Cr(III) and Cr(VI).

    Science.gov (United States)

    Hedberg, Yolanda S; Lidén, Carola; Odnevall Wallinder, Inger

    2014-09-15

    About 1-3% of the adult general population in Europe is allergic to chromium (Cr). The assessment of the potential release of Cr(III) and Cr(VI) from leather is hence important from a human health and environmental risk perspective. The Cr(VI) content in leather was recently restricted in the European Union. The aim of this study was to assess possible correlations between the bulk and surface chemistry of leather, released Cr(III) and Cr(VI), and capacities of co-released leather specific species to reduce and complex released Cr. Four differently tanned leathers were characterized by scanning electron microscopy with energy dispersive spectroscopy, X-ray photoelectron spectroscopy, attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectroscopy, and the diphenylcarbazide colorimetric method. Their characteristics were compared with results on Cr(III) and Cr(VI) release into artificial sweat (ASW, pHleather-specific species were shown to reduce Cr(VI), both in ASW and in PB. Their reduction capacities correlated with findings of the surface content of Cr and of released Cr. Leather samples without this capacity, and with less aromatic surface groups visible by ATR-FTIR, revealed Cr(VI) both at the surface and in solution (PB). Copyright © 2014 The Authors. Published by Elsevier B.V. All rights reserved.

  1. High temperature properties of the Cr-Nb-Al-N coatings with increasing Al contents

    OpenAIRE

    Li, W. Z.; Polcar, T.; Evaristo, M.; Cavaleiro, A.

    2013-01-01

    Cr-Nb-Al-N coatings with Al content from 0 to 12 at.% were deposited by d.c. reactive magnetron sputtering. The coatings were annealed in protective atmosphere at 800 and 900 °C for 1 h and exposed to air at 800, 900 and 1200 °C for different times. The chemical composition, structure, microstructure, hardness and adhesive/cohesive strength of the coatings, in as-deposited and annealed conditions, were investigated and the oxidation resistance was evaluated. As expected, the Al content increa...

  2. Influence of Mn contents in 0Cr18Ni10Ti thin wall stainless steel tube on TIG girth weld quality

    Science.gov (United States)

    Liu, Bo

    2017-03-01

    Three kinds of cold worked 0Cr18Ni10Ti thin wall stainless steel tubes with the manganese contents of 1.27%, 1.35% and 1.44% and the cold worked 0Cr18Ni10Ti stainless steel end plug with manganese content of 1.35% were used for TIG girth welding in the present investigation. The effect of different manganese contents in stainless steel tube on weld quality was studied. The results showed that under the same welding conditions, the metallographic performance of the girth weld for the thin wall stainless steel tube with the manganese element content 1.44% welded with end plug was the best. Under the appropriate welding conditions, the quality of the girth weld increased with the increase of the manganese content till 1.44%. It was found that in the case of the Mn content of 1.44%, and under the proper welding condition the welding defects, such as welding cracks were effectively avoided, and the qualified weld penetration can be obtained.. It is concluded that the appropriate increase of the manganese content can significantly improve the TIG girth weld quality of the cold worked 0Cr18Ni10Ti stainless steel tube.

  3. Fracture toughness and sliding properties of magnetron sputtered CrBC and CrBCN coatings

    Science.gov (United States)

    Wang, Qianzhi; Zhou, Fei; Ma, Qiang; Callisti, Mauro; Polcar, Tomas; Yan, Jiwang

    2018-06-01

    CrBC and CrBCN coatings with low and high B contents were deposited on 316L steel and Si wafers using an unbalanced magnetron sputtering system. Mechanical properties including hardness (H), elastic modulus (E) and fracture toughness (KIc) as well as residual stresses (σ) were quantified. A clear correlation between structural, mechanical and tribological properties of coatings was found. In particular, structural analyses indicated that N incorporation in CrBC coatings with high B content caused a significant structural evolution of the nanocomposite structure (crystalline grains embedded into an amorphous matrix) from nc-CrB2/(a-CrBx, a-BCx) to nc-CrN/(a-BCx, a-BN). As a result, the hardness of CrBC coating with high B content decreased from 23.4 to 16.3 GPa but the fracture toughness was enhanced. Consequently, less cracks initiated on CrBCN coatings during tribological tests, which combined with the shielding effect of a-BN on wear debris, led to a low friction coefficient and wear rate.

  4. Low-activation Mn-Cr austenitic stainless steel with further reduced content of long-lived radioactive elements

    Energy Technology Data Exchange (ETDEWEB)

    Onozuka, M.; Saida, T.; Hirai, S. [Mitsubishi Heavy Ind. Ltd., Yokohama (Japan); Kusuhashi, M.; Sato, I.; Hatakeyama, T. [The Japan Steel Works Ltd., Chatsu-machi 4, Muroran 051-8505 (Japan)

    1998-06-01

    Low-activation austenitic stainless steel based on Mn-Cr non-magnetic steels has been developed. The alloying elements of long-life activation, such as Ni, Mo and Co, were eliminated and substituted with Mn along with an addition of N. A Mn-Cr austenitic stainless steel, 24.5Mn-13.5Cr-0.02C-0.2N, has been developed successfully. Examined material properties, including mechanical, thermal and magnetic properties, as well as weldability and characteristics of corrosion resistance, are presented. It was found that the alloy has excellent material properties virtually equivalent to those of 316SS. In this study, the applicability of the Schaeffler, DeLong and Hull constitution diagrams for the stainless steels with low Ni and high Mn contents was also examined. The boundary conditions distinguishing the single austenite phase from the others have been identified for the Mn-Cr steels. (orig.) 22 refs.

  5. Low-activation Mn Cr austenitic stainless steel with further reduced content of long-lived radioactive elements

    Science.gov (United States)

    Onozuka, Masanori; Saida, Tomikane; Hirai, Shouzou; Kusuhashi, Mikio; Sato, Ikuo; Hatakeyama, Tsuyoshi

    1998-06-01

    Low-activation austenitic stainless steel based on Mn-Cr non-magnetic steels has been developed. The alloying elements of long-life activation, such as Ni, Mo and Co, were eliminated and substituted with Mn along with an addition of N. A Mn-Cr austenitic stainless steel, 24.5Mn-13.5Cr-0.02C-0.2N, has been developed successfully. Examined material properties, including mechanical, thermal and magnetic properties, as well as weldability and characteristics of corrosion resistance, are presented. It was found that the alloy has excellent material properties virtually equivalent to those of 316SS. In this study, the applicability of the Schaeffler, DeLong and Hull constitution diagrams for the stainless steels with low Ni and high Mn contents was also examined. The boundary conditions distinguishing the single austenite phase from the others have been identified for the Mn-Cr steels.

  6. Unraveling the mechanism responsible for the contrasting tolerance of Synechocystis and Synechococcus to Cr(VI): Enzymatic and non-enzymatic antioxidants

    Energy Technology Data Exchange (ETDEWEB)

    Gupta, Alka [Molecular Biology Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400085 (India); Ballal, Anand, E-mail: aballal@barc.gov.in [Molecular Biology Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400085 (India); Homi Bhabha National Institute, Training School Complex, Anushakti Nagar, Mumbai 40085 (India)

    2015-07-15

    Highlights: • Cr(VI) accumulation generates higher ROS in Synechocystis than in Synechococcus. • Synechococcus exhibits better photosynthetic activity in response to Cr(VI). • Synechococcus has higher enzymatic/non-enzymatic antioxidants than Synechocystis. • Synechococcus shows better tolerance to other oxidative stresses than Synechocystis. • Differential detoxification of ROS is responsible for the contrasting tolerance to Cr(VI) - Abstract: Two unicellular cyanobacteria, Synechocystis and Synechococcus, showed contrasting tolerance to Cr(VI); with Synechococcus being 12-fold more tolerant than Synechocystis to potassium dichromate. The mechanism responsible for this differential sensitivity to Cr(VI) was explored in this study. Total content of photosynthetic pigments as well as photosynthetic activity decreased at lower concentration of Cr(VI) in Synechocystis as compared to Synechococcus. Experiments with {sup 51}Cr showed Cr to accumulate intracellularly in both the cyanobacteria. At lower concentrations, Cr(VI) caused excessive ROS generation in Synechocystis as compared to that observed in Synechococcus. Intrinsic levels of enzymatic antioxidants, i.e., superoxide dismutase, catalase and 2-Cys-peroxiredoxin were considerably higher in Synechococcus than Synechocystis. Content of total thiols (both protein as well as non-protein) and reduced glutathione (GSH) was also higher in Synechococcus as compared to Synechocystis. This correlated well with higher content of carbonylated proteins observed in Synechocystis than Synechococcus. Additionally, in contrast to Synechocystis, Synechococcus exhibited better tolerance to other oxidative stresses like high intensity light and H{sub 2}O{sub 2}. The data indicate that the disparity in the ability to detoxify ROS could be the primary mechanism responsible for the differential tolerance of these cyanobacteria to Cr(VI)

  7. Influence of chemical composition in crystallographic texture Fe-Cr-Mo alloys

    International Nuclear Information System (INIS)

    Moura, L.B.; Guimaraes, R.F.

    2010-01-01

    The use of steels with higher contents of Mo in the oil industry has been an alternative to reduce the effect of naphthenic corrosion in refining units. The addition of Mo in Fe-Cr alloys in the same manner that increases resistance to corrosion naphthenic causes some difficulties such as difficulty of forming, welding and embrittlement. In this work, experimental ingots of Fe-Cr-Mo alloys (Cr - 9, 15 and 17%, Mo - 5, 7 and 9%) were melted in vacuum induction furnace and hot and cold rolled in a laboratory rolling mill. The influence of chemical composition on crystallographic texture of samples subjected to the same thermo-mechanical treatment was analyzed by x-ray diffraction. The results indicate that fiber (111) becomes more intense with increasing Mo and/or Cr contents. (author)

  8. On the sintering behaviour of steel bonded TiC-Cr3C2 and TiC-Cr3C2-WC mixed carbides

    International Nuclear Information System (INIS)

    Stojanov, L.G.; Exner, H.E.

    1978-01-01

    Powder mixtures of TiC+Cr 3 C 2 and TiC+Cr 3 C 2 + WC were hot pressed to nearly full density. The lattice parameter of the resulting cubic mixed crystal decreases linearly with increasing additions of Cr 3 C 2 and (Cr 3 C 2 +WC 1:1). Microhardness increases with Cr 3 C 2 content up to 20 wt.%. By addition of WC, microhardness is increased further and reaches a maximum value of approx. 38 000 MN/m 2 for 20 wt.% Cr 3 C 2 and 20 wt.% WC. From these solid solutions powder compositions of Ferro-TiC type were produced by milling with 55 wt.% Fe and 0.4 wt.% C. The sintering behaviour of these powders was studied in a vacuum dilatometer. The pronounced increase of shrinkage by Cr 3 C 2 and higher amounts of Cr 3 C 2 +WC dissolved in TiC previous to binder phase melting is attributed to the increased solubility of the carbide in solid iron. Presintering at 700 0 C in hydrogen has a negative influence on sintering activity and requires much higher temperatures for complete densification during subsequent vacuum sintering. (orig.) [de

  9. Influence of pig manure biochar mineral content on Cr(III) sorption capacity

    DEFF Research Database (Denmark)

    Wnetrzak, Renata; Leahy, J.J.; Chojnacka, Katarzyna W.

    2014-01-01

    BACKGROUND: The adsorption of Cr(III) ions on various pig manure biochar (BC) samples was investigated to determine the effect of operating conditions (initial pH, sorbate and sorbent concentrations) on sorptive capacity. The BC samples with higher sorption capacity showed high surface area...

  10. Comparison of extrapolation methods for creep rupture stresses of 12Cr and 18Cr10NiTi steels

    International Nuclear Information System (INIS)

    Ivarsson, B.

    1979-01-01

    As a part of a Soviet-Swedish research programme the creep rupture properties of two heat resisting steels namely a 12% Cr steel and an 18% Cr12% Ni titanium stabilized steel have been studied. One heat from each country of both steels were creep tested. The strength of the 12% Cr steels was similar to earlier reported strength values, the Soviet steel being some-what stronger due to a higher tungsten content. The strength of the Swedish 18/12 Ti steel agreed with earlier results, while the properties of the Soviet steel were inferior to those reported from earlier Soviet creep testings. Three extrapolation methods were compared on creep rupture data collected in both countries. Isothermal extrapolation and an algebraic method of Soviet origin gave in many cases rather similar results, while the parameter method recommended by ISO resulted in higher rupture strength values at longer times. (author)

  11. Correlation between bulk- and surface chemistry of Cr-tanned leather and the release of Cr(III) and Cr(VI)

    Energy Technology Data Exchange (ETDEWEB)

    Hedberg, Yolanda S., E-mail: yolanda@kth.se [KTH Royal Institute of Technology, School of Chemical Science and Engineering, Department of Chemistry, Division of Surface and Corrosion Science, SE-10044 Stockholm (Sweden); Institute of Environmental Medicine, Karolinska Institutet, Box 210, SE-17177 Stockholm (Sweden); Lidén, Carola, E-mail: carola.liden@ki.se [Institute of Environmental Medicine, Karolinska Institutet, Box 210, SE-17177 Stockholm (Sweden); Odnevall Wallinder, Inger, E-mail: ingero@kth.se [KTH Royal Institute of Technology, School of Chemical Science and Engineering, Department of Chemistry, Division of Surface and Corrosion Science, SE-10044 Stockholm (Sweden)

    2014-09-15

    Graphical abstract: - Highlights: • Released reducing/complexing leather-specific species can reduce released Cr(VI). • No co-released species enable the formation of Cr(VI) in solution. • The major Cr species released from leather in phosphate buffer was Cr(III) (>82%). • No Cr(VI) was released into artificial sweat. - Abstract: About 1–3% of the adult general population in Europe is allergic to chromium (Cr). The assessment of the potential release of Cr(III) and Cr(VI) from leather is hence important from a human health and environmental risk perspective. The Cr(VI) content in leather was recently restricted in the European Union. The aim of this study was to assess possible correlations between the bulk and surface chemistry of leather, released Cr(III) and Cr(VI), and capacities of co-released leather specific species to reduce and complex released Cr. Four differently tanned leathers were characterized by scanning electron microscopy with energy dispersive spectroscopy, X-ray photoelectron spectroscopy, attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectroscopy, and the diphenylcarbazide colorimetric method. Their characteristics were compared with results on Cr(III) and Cr(VI) release into artificial sweat (ASW, pH < 6.5) and phosphate buffer (PB, pH 7.5–8.0), measured by means of spectrophotometry and atomic absorption spectroscopy. Co-released leather-specific species were shown to reduce Cr(VI), both in ASW and in PB. Their reduction capacities correlated with findings of the surface content of Cr and of released Cr. Leather samples without this capacity, and with less aromatic surface groups visible by ATR-FTIR, revealed Cr(VI) both at the surface and in solution (PB)

  12. Atomistic simulation of the influence of Cr on the mobility of the edge dislocation in Fe(Cr) alloys

    International Nuclear Information System (INIS)

    Hafez Haghighat, S.M.; Terentyev, D.; Schaeublin, R.

    2011-01-01

    In this work Fe-Cr compounds, as model alloys for the ferritic base steels that are considered as main candidates for the structural materials of the future fusion reactors, are studied using molecular dynamics simulations. The Cr or so-called α' precipitates, which are obstacles to dislocations, affect mechanical properties, leading to hardening and loss of ductility. The flow stress to move an edge dislocation in a Cr solid solution in pure Fe is studied as a function of Cr content. The strength of a nanometric Cr precipitate as obstacle to an edge dislocation in pure Fe is investigated as a function of its Cr content. Results show that with increasing Cr content the precipitate obstacle strength increases, with a strong sensitivity to the local atomic order. Temperature induces a monotonic decrease of the flow stress of the Cr solid solution and of the Cr precipitate obstacle strength.

  13. The influence of cooling rate and Fe/Cr content on the evolution of Fe-rich compounds in a secondary Al-Si-Cu diecasting alloy

    Science.gov (United States)

    Fabrizi, A.; Timelli, G.

    2016-03-01

    This study investigates the morphological evolution of primary α-Al(Fe,Mn,Cr)Si phase in a secondary Al-Si-Cu alloy with respect to the initial Fe and Cr contents as well as to the cooling rate. The solidification experiments have been designed in order to cover a wide range of cooling rates, and the Fe and Cr contents have been varied over two levels. Metallographic and image analysis techniques have been used to quantitatively examine the microstructural changes occurring at different experimental conditions. The morphological evolution of the α-Fe phase has been also analysed by observing deep etched samples. By changing the cooling rate, α-Al15(Fe,Mn,Cr)3Si2 dodecahedron crystals, as well as Chinese- script, branched structures and dendrites form, while primary coarse β-Al5(Fe,Mn)Si needles appear in the alloy with the highest Fe content at low cooling rates.

  14. Empirical constraints on partitioning of platinum group elements between Cr-spinel and primitive terrestrial magmas

    Science.gov (United States)

    Park, Jung-Woo; Kamenetsky, Vadim; Campbell, Ian; Park, Gyuseung; Hanski, Eero; Pushkarev, Evgeny

    2017-11-01

    pattern with high Rh and low Os. The Intraplate Group Cr-spinels show flat patterns with positive Ru anomalies. Our results, together with the experimental and empirical data from previous studies, show that PGE patterns of Cr-spinel largely mimic that of the rock in which they are found, and that Rh, Ir and Os contents increase with increasing Fe3+ contents (i.e. magnetite component) in Cr-spinel, although Ru does not. These observations suggest that the enrichment of Rh and IPGEs in Cr-spinel is controlled by a combination of the Rh and IPGE contents in parental melts and the magnetite component of the spinel. Empirical partition coefficients (D) for Rh and IPGEs between Cr-spinels and silicate melts were calculated using the Rh and IPGE contents of the Cr-spinel and their host volcanic rocks after subtracting the accumulation effect of Cr-spinel. The D values for the Intraplate and MORB Group Cr-spinels increase with increasing magnetite component in Cr-spinel and range from 6 to 512, which is consistent with previously reported experimental and empirical values. In contrast, the Arc Group Cr-spinels have significantly higher D values (e.g. up to ∼3700 for Ru) than those of the Intraplate and MORB Group at the same magnetite concentration in the Cr-spinel, suggesting Rh and IPGEs dissolved in silicate melt have stronger affinity for Cr spinel under arc magma conditions than in intraplate magmas. This may be partly attributed to the low temperature of arc magmas relative to intraplate magmas, which leads to the Arc Group Cr-spinels having more octahedral sites at the same magnetite components than the Intraplate Group Cr-spinels. Because of significantly higher D values for the Arc Group Cr-spinels, compared with the Intraplate Group and MORB Group spinels, fractional crystallization of Cr-spinel will more efficiently fractionate Rh and IPGE from Pd and Pt in arc systems than in intraplate and MORB systems, which accounts for the highly fractionated PGE patterns in

  15. Radiation damage in Fe-Cr alloys: Atomistic studies

    International Nuclear Information System (INIS)

    Terentyev, Dmitry; Malerba, Lorenzo; Bonny, Giovanni; Castin, Nicolas

    2009-01-01

    High-Cr ferritic-martensitic steels are the most promising candidate structural materials for future advanced fission reactors, as well as for fusion systems, due to their better thermomechanical properties and higher radiation resistance as compared to austenitic steels. The performance of these steels, especially under irradiation, appears to be largely determined by the Cr content. For instance, the current choice of steel compositions around ∼9 wt% Cr is mainly based on the observation of a local minimum in the ductile-brittle transition temperature shift at this composition. On the other hand, reduced void swelling is observed between 3 and 12 wt% Cr. The origin of these and other Cr-dependent effects remained unexplained for a long time, thereby calling for a physical modelling effort addressing these questions. In this presentation, an overview is given on the effort made in recent years to construct a whole modelling framework, from ab initio to dislocations, to provide explanations to the above-mentioned issues. Ab initio calculations combined to the development of the interatomic potentials capable of grasping key features of Cr atoms embedded in perfect and defected Fe matrix, were required. Primary damage, defect migration, Cr mass transport, phase separation, Cr-defect segregation and dislocation-defect interactions could then be studied using fully atomistic approaches. Our research shows that many of the effects of Cr content on the behaviour of these alloys under irradiation can be attributed to the only recently highlighted high solubility of Cr in Fe (∼10 wt%), below which, in addition, Cr atoms tend to order. The presentation will clarify how this aspect, combined with the high affinity between Cr atoms and self-interstitials defects, influences and partly explain both microstructure evolution and mechanical behaviour of high-Cr steels under irradiation. (author)

  16. Heavy metal content (Cd, Ni, Cr and Pb) in soil amendment with a low polluted biosolid

    Science.gov (United States)

    Gomez Lucas, Ignacio; Lag Brotons, Alfonso; Navarro-Pedreño, Jose; Belén Almendro-Candel, Maria; Jordán, Manuel M.; Bech, Jaume; Roca, Nuria

    2016-04-01

    The progressively higher water quality standards in Europe has led to the generation of large quantities of sewage sludge derived from wastewater treatment (Fytili and Zabaniotou 2008). Composting is an effective method to minimize these risks, as pathogens are biodegraded and heavy metals are stabilized as a result of organic matter transformations (Barker and Bryson 2002; Noble and Roberts 2004). Most of the studies about sewage sludge pollution are centred in medium and high polluted wastes. However, the aim of this study was to assess the effects on soil heavy metal content of a low polluted sewage sludge compost in order to identify an optimal application rate based in heavy metal concentration under a period of cultivation of a Mediterranean horticultural plant (Cynara carducnculus). The experiment was done between January to June: rainfall was 71 mm, the volume of water supplied every week was 10.5 mm, mean air temperatures was 14.2, 20.4 (maximum), and 9.2◦C (minimum). The soil was a clay-loam anthrosol (WRB 2006). The experimental plot (60 m2) was divided into five subplots with five treatments corresponding to 0, 2, 4, 6, and 8 kg compost/m2. Three top-soil (first 20 cm) samples from each treatment were taken (January, April and June) and these parameters were analysed: pH, electrical conductivity, organic matter and total content of heavy metals (microwave acid digestion followed by AAS-spectrometry determination). The results show that sewage sludge compost treatments increase the organic matter content and salinity (electrical conductivity of the soils) and diminish the pH. Cd and Ni total content in top-soil was affected and both slightly reduce their concentration. Pb and Cr show minor changes. In general, the application of this low polluted compost may affect the mobility of Cd and Ni due to the pH modification and the water added by irrigation along time but Pb and Cr remain their content in the top-soil. References Barker, A.V., and G.M. Bryson

  17. Determination of Cr(VI) in wood specimen: A XANES study at the Cr K edge

    International Nuclear Information System (INIS)

    Strub, E.; Plarre, R.; Radtke, M.; Reinholz, U.; Riesemeier, H.; Schoknecht, U.; Urban, K.; Juengel, P.

    2008-01-01

    The content of chromium in different oxidation states in chromium-treated wood was studied with XANES (X-ray absorption near-edge structure) measurements at the Cr K absorption edge. It could be shown that wood samples treated with Cr(VI) (pine and beech) did still contain a measurable content of Cr(VI) after four weeks conditioning. If such wood samples were heat exposed for 2 h with 135 deg. C prior conditioning, Cr(VI) was no longer detected by XANES, indicating a complete reduction to chromium (III)

  18. The influence of cooling rate and Fe/Cr content on the evolution of Fe-rich compounds in a secondary Al-Si-Cu diecasting alloy

    International Nuclear Information System (INIS)

    Fabrizi, A; Timelli, G

    2016-01-01

    This study investigates the morphological evolution of primary α-Al(Fe,Mn,Cr)Si phase in a secondary Al-Si-Cu alloy with respect to the initial Fe and Cr contents as well as to the cooling rate. The solidification experiments have been designed in order to cover a wide range of cooling rates, and the Fe and Cr contents have been varied over two levels. Metallographic and image analysis techniques have been used to quantitatively examine the microstructural changes occurring at different experimental conditions. The morphological evolution of the α-Fe phase has been also analysed by observing deep etched samples. By changing the cooling rate, α-Al 15 (Fe,Mn,Cr) 3 Si 2 dodecahedron crystals, as well as Chinese- script, branched structures and dendrites form, while primary coarse β-Al 5 (Fe,Mn)Si needles appear in the alloy with the highest Fe content at low cooling rates. (paper)

  19. Effects of V and Cr on Laser Cladded Fe-Based Coatings

    Directory of Open Access Journals (Sweden)

    Haiyang Wang

    2018-03-01

    Full Text Available Fe-based coatings with high V and Cr content were obtained by laser cladding using Fe-based powder with different Cr3C2 and FeV50 content. The results showed that Fe-based coatings were uniform and dense. The constituent phases were mainly composed of α-Fe solid solution with the increase of Cr3C2 and FeV50, γ-Fe and V8C7 phases were achieved. The microstructure of the coatings exhibited a typical dendrite structure. The concentration of C, V and Cr were saturated in dendritic areas, and the other alloying elements were mainly dissolved in the interdendritic areas. The hardness and wear resistance of Fe-based coatings were enhanced with the Cr3C2 and FeV50 addition. The specimen with 15% Cr3C2 and 16% FeV50 had the highest hardness of 66.1 ± 0.6 HRC, which was 1.05 times higher than the sample with 4.5% Cr3C2 and 5% FeV50, and the wear resistance of the former was three times greater than the latter.

  20. Structural, electrical, and dielectric properties of Cr doped ZnO thin films: Role of Cr concentration

    Energy Technology Data Exchange (ETDEWEB)

    Gürbüz, Osman, E-mail: osgurbuz@yildiz.edu.tr; Okutan, Mustafa

    2016-11-30

    Highlights: • Magnetic material of Cr and semiconductor material of ZnO were grown by the magnetron sputtering co-sputter technique. • Perfect single crystalline structures were grown. • DC and AC conductivity with dielectric properties as a function of frequency (f = 5Hz–13 MHz) at room temperature were measured and compared. • Cr doped ZnO can be used in microwave, sensor and optoelectronic devices as the electrical conductivity increases while dielectric constant decreases with the Cr content. - Abstract: An undoped zinc oxide (ZnO) and different concentrations of chromium (Cr) doped ZnO Cr{sub x}ZnO{sub 1−x} (x = 3.74, 5.67, 8.10, 11.88, and 15.96) thin films were prepared using a magnetron sputtering technique at room temperature. These films were characterized by X-ray diffraction (XRD), High resolution scanning electron microscope (HR-SEM), and Energy dispersive X-ray spectrometry (EDS). XRD patterns of all the films showed that the films possess crystalline structure with preferred orientation along the (100) crystal plane. The average crystallite size obtained was found to be between 95 and 83 nm which was beneficial in high intensity recording peak. Both crystal quality and crystallite sizes decrease with increasing Cr concentration. The crystal and grain sizes of the all film were investigated using SEM analysis. The surface morphology that is grain size changes with increase Cr concentration and small grains coalesce together to form larger grains for the Cr{sub 11.88}ZnO and Cr{sub 15.96}ZnO samples. Impedance spectroscopy studies were carried out in the frequencies ranging from 5 Hz to 13 MHz at room temperature. The undoped ZnO film had the highest dielectric value, while dielectric values of other films decreased as doping concentrations increased. Besides, the dielectric constants decreased whereas the loss tangents increased with increasing Cr content. This was considered to be related to the reduction of grain size as Cr content in Zn

  1. Effects of the Cr2O3 Content on the Viscosity of CaO-SiO2-10 Pct Al2O3-Cr2O3 Quaternary Slag

    Science.gov (United States)

    Wu, Tuo; Zhang, Yanling; Yuan, Fang; An, Zhuoqing

    2018-04-01

    The present study experimentally investigates the effect of Cr2O3 on the viscosity of molten slags. The viscosities of CaO-SiO2-10 pct Al2O3-Cr2O3 quaternary slags with two different binary basicities (R, basic slag with R = 1.2 and acidic slag with R = 0.8) were measured by the rotating cylindrical method from 1813 K to 1953 K (1540 °C to 1680 °C). The results showed that the viscosity of both types of slag decreased as the Cr2O3 content increased, but the viscosity of acidic slags exhibited a greater decrease. The slags showed good Newtonian behavior at such high temperatures. Cr2O3 could act as a network modifier to simplify the Si-O-Si tetrahedral structure, as verified by the Raman spectral analysis, which was consistent with the decreasing trend of viscosity. The activation energy of viscous flow decreased slightly with increasing Cr2O3, but increasing the basicity seemed to be more effective in decreasing the viscosity than adding Cr2O3.

  2. Observations of defect structure evolution in proton and Ni ion irradiated Ni-Cr binary alloys

    Energy Technology Data Exchange (ETDEWEB)

    Briggs, Samuel A., E-mail: sabriggs2@wisc.edu [University of Wisconsin-Madison, 1415 Engineering Drive, Madison, WI 53706 (United States); Barr, Christopher M. [Drexel University, 3141 Chestnut Street, Philadelphia, PA 19104 (United States); Pakarinen, Janne [University of Wisconsin-Madison, 1415 Engineering Drive, Madison, WI 53706 (United States); SKC-CEN Belgian Nuclear Research Centre, Boeretang 200, B-2400 Mol (Belgium); Mamivand, Mahmood [University of Wisconsin-Madison, 1415 Engineering Drive, Madison, WI 53706 (United States); Hattar, Khalid [Sandia National Laboratories, PO Box 5800, Albuquerque, NM 87185 (United States); Morgan, Dane D. [University of Wisconsin-Madison, 1415 Engineering Drive, Madison, WI 53706 (United States); Taheri, Mitra [Drexel University, 3141 Chestnut Street, Philadelphia, PA 19104 (United States); Sridharan, Kumar [University of Wisconsin-Madison, 1415 Engineering Drive, Madison, WI 53706 (United States)

    2016-10-15

    Two binary Ni-Cr model alloys with 5 wt% Cr and 18 wt% Cr were irradiated using 2 MeV protons at 400 and 500 °C and 20 MeV Ni{sup 4+} ions at 500 °C to investigate microstructural evolution as a function of composition, irradiation temperature, and irradiating ion species. Transmission electron microscopy (TEM) was applied to study irradiation-induced void and faulted Frank loops microstructures. Irradiations at 500 °C were shown to generate decreased densities of larger defects, likely due to increased barriers to defect nucleation as compared to 400 °C irradiations. Heavy ion irradiation resulted in a larger density of smaller voids when compared to proton irradiations, indicating in-cascade clustering of point defects. Cluster dynamics simulations were in good agreement with the experimental findings, suggesting that increases in Cr content lead to an increase in interstitial binding energy, leading to higher densities of smaller dislocation loops in the Ni-18Cr alloy as compared to the Ni-5Cr alloy. - Highlights: • Binary Ni-Cr alloys were irradiated with protons or Ni ions at 400 and 500 °C. • Higher irradiation temperatures yield increased size, decreased density of defects. • Hypothesize that varying Cr content affects interstitial binding energy. • Fitting CD models for loop nucleation to data supports this hypothesis.

  3. Content of heavy metals in gleyic chernozem of Srem loess terrace under alfalfa

    Directory of Open Access Journals (Sweden)

    Jakšić Snežana

    2012-01-01

    Full Text Available Production of high-quality forage from alfalfa is influenced not only by the presence of nutrients, but also by the absence of harmful elements, such as heavy metals. The examination of the total heavy metals content (Ni, Cr, Pb and As in gleyic chernozem soil of Srem loess terrace in Hrtkovci, under alfalfa (Medicago sativa L. were carried out in 2011 in order to determine suitability for the production of safe forage. It total content of Pb, As and Crwas below the maximum permitted concentrations. The content of As, Cr and Ni was higher in the surface layer, unlike Pb, whose content was higher in the deeper layers of soil. A significant positive correlation was found between the total content of Ni, Cr and As. An increased concentration of Ni was found, which was above the maximum permitted concentration. It is necessary to further control its content and accessibility examination and extraction from plants, to prevent its entry into the food chain and provide safe food.

  4. Biliary excretion and distribution of 51Cr(III) and 51Cr(VI) in rats

    International Nuclear Information System (INIS)

    Cikrt, M.; Bencko, V.

    1979-01-01

    The biliary excretion and distribution of 51 Cr after intravenous administration of 51 Cr(III) ( 51 CrCl 3 ) or 51 Cr(VI) (Na 2 51 CrO 4 .4H 2 O) were studied in rats. The cumulative biliary excretion of 51 Cr 24 hrs after the injection was significantly higher after administration of 51 Cr(VI) than of 51 Cr(III) (3.51+-0.7% and 0.51+-0.05% of administered dose, respectively). This difference was especially due to a higher rate of biliary excretion of 51 Cr in the first hours after 51 Cr(VI) administration. The excretion of 51 Cr via feces was also higher after administration of 51 Cr(VI) (7.35+-0.45%) of administered dose, as against 4.23+-0.23% after 51 Cr(III). On the other hand, no significant difference in urinary excretion of 51 Cr was found. Statistically significant differences were also observed in the distribution of 51 Cr in the organism after administration of both valence states of the metal. (author)

  5. Metal ions released from fixed orthodontic appliance affect hair mineral content.

    Science.gov (United States)

    Mikulewicz, Marcin; Wołowiec, Paulina; Loster, Bartłomiej; Chojnacka, Katarzyna

    2015-02-01

    The objective was to evaluate metal ion accumulation in hair of patients undergoing orthodontic treatment with fixed appliances in time. The patients (N = 47) participated in a questionnaire survey. Hair sampling was performed at the beginning and in the 4th, 8th, and 12th month of the treatment. The content of metals (Cr, Ni, Fe) in hair was analyzed by ICP-OES equipped with USN nebulizer. The peak release of Cr and Fe occurred after 4 months of the treatment, and the peak release of Ni gradually increased throughout the whole year of the therapy. During 1 year treatment, an average accumulation of metals in hair tissue was 7.42 ± 14.19 μg of Ni, 8.94 ± 13.1 μg of Cr, and 131 ± 279 μg of Fe. The mean content of Cr was higher than the 90th percentile value for this element. The upper limit of literature reference ranges for Cr, Ni, and Fe in hair was not exceeded. The value of exposure (kinetics and dose) of orthodontic patients to metal ions released from orthodontic appliances can be assessed by hair mineral analysis. The content of Cr was statistically significantly higher during the treatment than before the beginning of therapy.

  6. Investigation of preparation technique and tribological properties of CrN piston rings coatings

    International Nuclear Information System (INIS)

    Cai Zhihai; Zhang Ping; Zhao Junjun; Du Jun; Niu Qingyin

    2009-01-01

    By using multi-ion plating, CrN films were made on surface of piston rings to improve its tribological properties and service life. Effects of nitrogen content to prepare the film on hardness and phase structure were studied. The high-temperature tribological properties of Cr plating and CrN films were compared with CETR friction tester. The results show that nitrogen partial pressure significantly affects the mechanical properties of CrN films. With increasing N 2 partial pressure, preferential growth orientation of the film changed from Cr 2 N(211) to CrN(220) phase, leading to two hardness peaks corresponding to the Cr 2 N and CrN phases,respectively. Having higher high-temperature wear resistance and lower friction coefficient than Cr plating, the CrN films are suitable for piston rings under high temperature conditions. (authors)

  7. Study of fatigue and fracture behavior of NbCr{sub 2}-based alloys: Phase stability in Nb-Cr-Ni ternary system

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, J.H.; Liaw, P.K. [Univ. of Tennessee, Knoxville, TN (United States). Dept. of Materials Science and Engineering; Liu, C.T. [Oak Ridge National Lab., TN (United States). Metals and Ceramics Div.

    1997-12-01

    Phase stability in a ternary Nb-Cr-Ni Laves phase system was studied in this paper. Their previous study in NbCr{sub 2}-based transition-metal Laves phases has shown that the average electron concentration factor, e/a, is the dominating factor in controlling the phase stability of NbCr{sub 2}-based Laves phases when the atomic size ratios are kept identical. Since Ni has ten out-shell electrons, the substitution of Ni for Cr in NbCr{sub 2} will increase the average electron concentration of the alloy, thus leading to the change of the crystal structures from C15 to C14. In this paper, a number of pseudo-binary Nb(Cr,Ni){sub 2} alloys were prepared, and the crystal structures of the alloys after a long heat-treatment at 1000 C as a function of the Ni content were determined by the X-ray diffraction technique. The boundaries of the C15/C14 transition were determined and compared to their previous predictions. It was found that the electron concentration and phase stability correlation is obeyed in the Nb-Cr-Ni system. However, the e/a ratio corresponding to the C15/C14 phase transition was found to move to a higher value than the predicted one. The changes in the lattice constant, Vickers hardness and fracture toughness were also determined as a function of the Ni content, which were discussed in light of the phase stability difference of the alloys.

  8. Influência do teor de Mo na microestrutura de ligas Fe-9Cr-xMo Effect of the content of molybdenum in the microstructure of Fe-9Cr-xMo alloy

    Directory of Open Access Journals (Sweden)

    Rodrigo Freitas Guimarães

    2010-12-01

    Full Text Available Aços Cr-Mo são usados na indústria do petróleo em aplicações com óleos crus ricos em compostos sulfurosos. Aços comerciais como 2.5Cr1Mo ou 9Cr1Mo têm se mostrado ineficientes em consequência de altos índices de corrosão naftênica. Uma estratégia para resolver este problema é o aumento do teor de molibdênio destes aços. Neste trabalho foi estudado o efeito do aumento do teor de molibdênio na microestrutura de ligas Fe-9Cr-xMo, solubilizadas e soldadas. Foram levantados os diagramas de fases com auxílio de um programa comercial para verificar as possíveis fases a serem formadas e identificar os problemas de soldagem. A microestrutura das ligas solubilizadas foi analisada por microscopia óptica e EBSD, além da medição da dureza. Foram realizadas soldagens autógenas para verificar o efeito do aporte térmico na microestrutura e na dureza das ligas. O aumento do teor de molibdênio resultou no aumento da dureza das ligas. A análise microestrutural das ligas soldadas apresentou uma particularidade para a liga com menor teor de molibdênio, a presença de martensita. Já as ligas com maior teor de molibdênio apresentaram uma microestrutura completamente ferrítica. A formação de martensita pode ser um problema na solda da liga com menor teor de molibdênio, uma vez que a mesma pode causar perdas nas propriedades mecânicas comprometendo sua aplicação.Cr-Mo steels are used in the petroleum industry in applications with crude oils rich in sulfur compounds. 2.5Cr1Mo or 9Cr1Mo do not resist to operating conditions when in contact with crude oils. The increasing of molybdenum content can improve the corrosion resistance of these alloys. This paper studied the effect of increased concentration of molybdenum in the microstructure of Fe-9Cr-xMo alloys, annealed and welded. Phase diagrams were built with the aid of commercial program to check the possible phases to be formed and to identify the problems of welding. Analyses were

  9. Effects of Ni and Mo on the microstructure and some other properties of Co-Cr dental alloys

    International Nuclear Information System (INIS)

    Matkovic, Tanja; Matkovic, Prosper; Malina, Jadranka

    2004-01-01

    Influences of adding Ni and Mo on the microstructure and properties of as-cast Co-Cr base alloys have been investigated in order to determine the region of their optimal characteristics for biomedical application. The alloys were produced by arc-melting technique under argon atmosphere. Using optical metallography and scanning electron micro analyser it has been established that among 10 samples of Co-Cr-Ni alloys only samples 5 and 9 with the composition Co 55 Cr 40 Ni 5 and Co 60 Cr 30 Ni 10 have appropriate dendritic solidification microstructure. This microstructure, typical for commercial dental alloys, appears and beside greater number of as-cast Co-Cr-Mo alloys. The results of hardness and corrosion resistance measurements revealed the strong influence of different alloy chemistry and of as-cast microstructure. Hardness of alloys decreases with nickel content, but increases with chromium content. Therefore all Co-Cr-Ni alloys have significantly lower hardness than Co-Cr-Mo alloys. Corrosion resistance of alloys in artificial saliva was evaluated on the base of pitting potential. Superior corrosion characteristics have the samples with typical dendritic microstructure and higher chromium content, until nickel content have not significant effect. According to this, in ternary Co-Cr-Ni phase diagram was located the small concentration region (about samples 5 and 9) in them alloy properties can satisfied the high requirements for biomedical applications. This region is considerably larger in Co-Cr-Mo phase diagram

  10. Engineering Potato Starch with a Higher Phosphate Content.

    Directory of Open Access Journals (Sweden)

    Xuan Xu

    Full Text Available Phosphate esters are responsible for valuable and unique functionalities of starch for industrial applications. Also in the cell phosphate esters play a role in starch metabolism, which so far has not been well characterized in storage starch. Laforin, a human enzyme composed of a carbohydrate-binding module and a dual-specificity phosphatase domain, is involved in the dephosphorylation of glycogen. To modify phosphate content and better understand starch (dephosphorylation in storage starch, laforin was engineered and introduced into potato (cultivar Kardal. Interestingly, expression of an (engineered laforin in potato resulted in significantly higher phosphate content of starch, and this result was confirmed in amylose-free potato genetic background (amf. Modified starches exhibited altered granule morphology and size compared to the control. About 20-30% of the transgenic lines of each series showed red-staining granules upon incubation with iodine, and contained higher phosphate content than the blue-stained starch granules. Moreover, low amylose content and altered gelatinization properties were observed in these red-stained starches. Principle component and correlation analysis disclosed a complex correlation between starch composition and starch physico-chemical properties. Ultimately, the expression level of endogenous genes involved in starch metabolism was analysed, revealing a compensatory response to the decrease of phosphate content in potato starch. This study provides a new perspective for engineering starch phosphate content in planta by making use of the compensatory mechanism in the plant itself.

  11. Influence of Cu Content on the Microstructure and Mechanical Properties of Cr-Cu-N Coatings

    Directory of Open Access Journals (Sweden)

    Ji Cheng Ding

    2018-01-01

    Full Text Available The Cr-Cu-N coatings with various Cu contents (0–25.18 (±0.17 at.% were deposited on Si wafer and stainless steel (SUS 304 substrates in reactive Ar+N2 gas mixture by a hybrid coating system combining pulsed DC and RF magnetron sputtering techniques. The influence of Cu content on the coating composition, microstructure, and mechanical properties was investigated. The microstructure of the coatings was significantly altered by the introduction of Cu. The deposited coatings exhibit solid solution structure with different compositions in all of the samples. Addition of Cu is intensively favored for preferred orientation growth along (200 direction by restricting in (111 direction. With increasing Cu content, the surface and cross-sectional morphology of coatings were changed from triangle cone-shaped, columnar feature to broccoli-like and compact glassy microstructure, respectively. The mechanical properties including the residual stress, nanohardness, and toughness of the coatings were explored on the basis of Cu content. The highest hardness was obtained at the Cu content of 1.49 (±0.10 at.%.

  12. Influence of moisture content and temperature on degree of carbonation and the effect on Cu and Cr leaching from incineration bottom ash.

    Science.gov (United States)

    Lin, Wenlin Yvonne; Heng, Kim Soon; Sun, Xiaolong; Wang, Jing-Yuan

    2015-09-01

    This study investigated the influence of moisture content and temperature on the degree of carbonation of municipal solid waste (MSW) incineration bottom ash (IBA) from two different incineration plants in Singapore. The initial rate of carbonation was affected by the nominal moisture content used. Carbonation temperature seemed to play a part in changing the actual moisture content of IBA during carbonation, which in turn affected the degree of carbonation. Results showed that 2h of carbonation was sufficient for the samples to reach a relatively high degree of carbonation that was close to the degree of carbonation observed after 1week of carbonation. Both Cu and Cr leaching also showed significant reduction after only 2h of carbonation. Therefore, the optimum moisture content and temperature were selected based on 2h of carbonation. The optimum moisture content was 15% for both incineration plants while the optimum temperature was different for the two incineration plants, at 35°C and 50°C. The effect on Cu and Cr leaching from IBA after accelerated carbonation was evaluated as a function of carbonation time. Correlation coefficient, Pearson's R, was used to determine the dominant leaching mechanism. The reduction in Cu leaching was found to be contributed by both formation of carbonate mineral and reduction of DOC leaching. On the other hand, Cr leaching seemed to be dominantly controlled by pH. Copyright © 2015 Elsevier Ltd. All rights reserved.

  13. The effect of O{sub 2} content on the corrosion behaviour of X65 and 5Cr in water-containing supercritical CO{sub 2} environments

    Energy Technology Data Exchange (ETDEWEB)

    Hua, Yong, E-mail: leo.huayong@gmail.com; Barker, Richard; Neville, Anne

    2015-11-30

    Highlights: • Corrosion behaviour was evaluated in water-containing SC-CO{sub 2} with different O{sub 2} levels. • Corrosion was observed when no free water was present. • Localized corrosion was a fundamental consideration in water-containing CO{sub 2} systems. • O{sub 2} content plays a key role in influencing the critical water content. - Abstract: The general and localized corrosion behaviour of X65 carbon steel and 5Cr low alloy steel were evaluated in a water-saturated supercritical CO{sub 2} environment in the presence of varying concentrations of O{sub 2}. Experiments were performed at a temperature of 35 °C and a pressure of 80 bar to simulate the conditions encountered during CO{sub 2} transport and injection. Results indicated that increasing O{sub 2} concentration from 0 to 1000 ppm caused a progressive reduction in the general corrosion rate, but served to increase the extent of localized corrosion observed on both materials. Pitting (or localized attack) rates for X65 ranged between 0.9 and 1.7 mm/year, while for 5Cr rose from 0.3 to 1.4 mm/year as O{sub 2} concentration was increased from 0 to 1000 ppm. General corrosion rates were over an order of magnitude lower than the pitting rates measured. Increasing O{sub 2} content in the presence of X65 and 5Cr suppressed the growth of iron carbonate (FeCO{sub 3}) on the steel surface and resulted in the formation of a corrosion product consisting mainly of iron oxide (Fe{sub 2}O{sub 3}). 5Cr was shown to offer more resistance to pitting corrosion in comparison to X65 steel over the conditions tested. At concentrations of O{sub 2} above 500 ppm 5Cr produced general corrosion rates less than 0.04 mm/year, which were half that recorded for X65. The improved corrosion resistance of 5Cr was believed to be at least partially attributed to the formation of a Cr-rich film on the steel surface which was shown using X-ray photoelectron spectroscopy to contain chromium oxide (Cr{sub 2}O{sub 3}) and chromium

  14. Corrosion and Wear Behaviors of Cr-Doped Diamond-Like Carbon Coatings

    Science.gov (United States)

    Viswanathan, S.; Mohan, L.; Bera, Parthasarathi; Kumar, V. Praveen; Barshilia, Harish C.; Anandan, C.

    2017-08-01

    A combination of plasma-enhanced chemical vapor deposition and magnetron sputtering techniques has been employed to deposit chromium-doped diamond-like carbon (DLC) coatings on stainless steel, silicon and glass substrates. The concentrations of Cr in the coatings are varied by changing the parameters of the bipolar pulsed power supply and the argon/acetylene gas composition. The coatings have been studied for composition, morphology, surface nature, nanohardness, corrosion resistance and wear resistance properties. The changes in I D / I G ratio with Cr concentrations have been obtained from Raman spectroscopy studies. Ratio decreases with an increase in Cr concentration, and it has been found to increase at higher Cr concentration, indicating the disorder in the coating. Carbide is formed in Cr-doped DLC coatings as observed from XPS studies. There is a decrease in sp 3/ sp 2 ratios with an increase in Cr concentration, and it increases again at higher Cr concentration. Nanohardness studies show no clear dependence of hardness on Cr concentration. DLC coatings with lower Cr contents have demonstrated better corrosion resistance with better passive behavior in 3.5% NaCl solution, and corrosion potential is observed to move toward nobler (more positive) values. A low coefficient of friction (0.15) at different loads is observed from reciprocating wear studies. Lower wear volume is found at all loads on the Cr-doped DLC coatings. Wear mechanism changes from abrasive wear on the substrate to adhesive wear on the coating.

  15. Cr(III) reactivity and foot dermatitis in Cr(VI) positive patients

    DEFF Research Database (Denmark)

    Hansen, Malene Barré; Menné, Torkil; Johansen, Jeanne Duus

    2006-01-01

    Chromium allergy has become synonymous with Cr(VI) allergy. However, real exposure to chromium from leather products may include both Cr(III) and Cr(VI). In this study, we investigate the reactivity to both Cr(VI) and Cr(III) in consecutive patients to analyse the relation between foot eczema/leather...... to Cr(III). The increased risk was not due to a higher degree of sensitivity to Cr(VI). Leather was reported most frequently as the suspected cause of chromium dermatitis (54%). However, Cr(VI) allergics having foot eczema and positive or doubtful Cr(III) reactions often had positive reactions to other...

  16. Structure and grindability of cast Ti-5Cr-xFe alloys

    International Nuclear Information System (INIS)

    Hsu, H.-C.; Pan, C.-H.; Wu, S.-C.; Ho, W.-F.

    2009-01-01

    The purpose of this study was to investigate the structure, microhardness and grindability of Ti-5Cr and a series of ternary Ti-5Cr-xFe alloys with 0.1, 0.5, 1, 3 and 5 wt.% Fe, respectively. This study evaluated the phase and structure of Ti-5Cr and Ti-5Cr-xFe alloys, using an X-ray diffraction (XRD) for phase analysis and optical microscope for microstructure of the etched alloys. In addition, grindability was evaluated by measuring the amount of metal volume removed after grinding for 1 min at each of the four rotational speeds of the wheel (500, 750, 1000 or 1200 m/min), with the goal of developing a titanium alloy with better machinability than commercially pure titanium (c.p. Ti). The results showed that the structure of Ti-5Cr-xFe alloys is sensitive to the Fe content. With Fe contents higher than 0.5 wt.%, the equi-axed β phase is entirely retained, while ω phase was found in the Ti-5Cr, Ti-5Cr-0.1Fe, Ti-5Cr-0.5Fe and Ti-5Cr-1Fe alloys. The largest quantity of ω phase and highest microhardness were found in Ti-5Cr-0.5Fe and Ti-5Cr-1Fe alloys. The grinding rates of the Ti-5Cr and Ti-5Cr-xFe alloys showed a similar tendency to the microhardness. The Ti-5Cr, Ti-5Cr-0.1Fe, Ti-5Cr-0.5Fe and Ti-5Cr-1Fe alloys exhibited the best grindability, especially at 500, 750 and 1000 m/min. Furthermore, the grindability of the tested metals increased in proportion to grinding speed up to 1000 m/min, with a decrease after 1200 m/min. This study concluded that Fe may be used to harden titanium and improve the grindability

  17. Mechanical properties and oxidation behaviour of (Al,Cr)N and (Al,Cr,Si)N coatings for cutting tools deposited by HPPMS

    Energy Technology Data Exchange (ETDEWEB)

    Bobzin, K.; Bagcivan, N.; Immich, P. [Surface Engineering Institute, RWTH Aachen University, Augustinerbach 4-22, D-52056 Aachen (Germany); Bolz, S. [Surface Engineering Institute, RWTH Aachen University, Augustinerbach 4-22, D-52056 Aachen (Germany)], E-mail: info1@iot.rwth-aachen.de; Cremer, R.; Leyendecker, T. [CemeCon AG, Wuerselen (Germany)

    2008-12-01

    Hard coatings with high hardness, high oxidation resistance and thermal stability are used for economical machining. In this regard nanostructured (Cr,Al)N and nc-(Cr,Al)N/a-Si{sub 3}N{sub 4} films were sputtered on tungsten carbide tools and WC/Co samples by using the HPPMS (High Power Pulse Magnetron Sputtering) technology. The relationship between coating composition, microstructure and mechanical properties was investigated by using X-ray diffraction, Scanning Electron Microscopy (SEM), and Nanoindentation. The maximum hardness value was about 40 GPa. For the coatings the Al-content was varied from 10-90 at.% while the silicon content was about 5 at.% for the (Cr,Al,Si)N. As this study focuses on oxidation behaviour of the deposited coatings, annealing tests were carried out in air at 1000 deg. C . HPPMS is a promising technology to ensure a uniform coating distribution, especially for complex shaped substrates like cutting tools or moulds. SEM pictures of the cross section have been taken around the cutting edge to determine the deposition rate and the film growth. The coatings morphology has been compared to m. f. (middle frequency)- and d. c. (direct current)-sputtered nanocomposite (Cr,Al,Si)N films indicating enhanced properties due to the application of the HPPMS-technology with regard to denser structure, higher hardness, favourable surface topography and better thickness uniformity.

  18. Study on the metabolism of physiological amounts of Cr(III) intragastrical administration in normal rats using activable enriched stable isotope Cr-50 compound as a tracer

    International Nuclear Information System (INIS)

    Feng, W.Y.; Ding, W.J.; Qian, Q.F.; Chai, Z.F.

    1998-01-01

    In order to study the metabolism of physiological amounts of 51 Cr (10μg/100 g of body wt.) intragastrically administered in rats, the activable enriched stable isotope Cr-50 compound Cr 2 O 3 was used as a tracer. The absorption and distribution of 51 Cr(III) in rats with time were studied. Significant 51 Cr contents were found in all the organs and tissues of interest. The kidney, liver and bone contain higher amounts of 51 Cr than others. The fact that specific activities of 51 Cr are notably high in kidney, bone, spleen and pancreas and decrease gradually with time suggests that there are tighter binding of chromium in these organs. The excretion of 51 Cr at various time intervals was also studied. Almost totally intragastrically administered dose was excreted in the feces. The increased urinary excretion of 51 Cr with time indicates that the urine-chromium is the metabolic derivative of organism. In view of the tissues distribution and excretion, it can be concluded that no more than 1% of the dose was absorbed from the gastrointestinal tract. (author)

  19. The effect of aluminum content on phase constitution and heat treatment behavior of Ti-Cr-Al alloys for healthcare application

    International Nuclear Information System (INIS)

    Sugano, Daisuke; Ikeda, Masahiko

    2005-01-01

    As life expectancy steadily increases, developing reliable functional materials for healthcare applications gains importance. Titanium and its alloys, while attractive for such applications, are expensive. The present investigation suggests that it may be possible to reduce costs by using new, low-cost beta Ti alloys. To assess their reliability, the heat treatment behavior of beta Ti alloys, Ti-7 mass% Cr with varying Al content (0%, 1.5%, 3.0% and 4.5%), was investigated through electrical resistivity and Vickers hardness measurements. In the Ti-7Cr-0Al alloy quenched from 1173 K, only the beta phase was identified by X-ray diffraction (XRD). In Ti-7Cr-1.5 to 4.5 Al alloys, XRD detected both beta and orthorhombic martensite. On isochronal heat treatment behavior of Ti-7Cr-3.0, 4.5 Al alloys, resistivity at liquid nitrogen temperature and resistivity ratio increased between 423 and 523 K.These increases are due to reverse transformation of orthorhombic martensite to the metastable beta phase

  20. Culture Optimization and Amino Acid Composition of Cr-Enriched Mycelia of Pleurotus cornucopiae SD-01

    Directory of Open Access Journals (Sweden)

    Fan-Yun Meng

    2010-01-01

    Full Text Available Chromium(III is an essential trace element for humans and animals. Pleutorus cornucopiae SD-01 is a nutritional and functional mushroom containing many kinds of bioactive ingredients. The aims of this work are to optimize the conditions of P. cornucopiae SD-01 cultivation with Cr enrichment in submerged culture by determining the dry cell mass, Cr content in mycelia and the rate of Cr enrichment, and to analyze the amino acid composition of Cr-enriched mycelia. The optimal medium contained (in g/L: potato 200, sucrose 25, yeast extract 4, KH2PO4 1 and MgSO4·7H2O 1. The optimum parameters of liquid culture were temperature 25 °C, cultivation time 6 days, the volume of the medium 100 mL, rotation speed 160 rpm and initial pH=6.5. Under the optimized conditions, the values of the dry cell mass, Cr content in mycelia and the rate of Cr enrichment were (6.63±0.35 g/L, (3670±211 μg/g and (12.15±1.01 % respectively, which were by (23.23±1.22, (18.19±1.06 and (45.68±2.67 % respectively, higher than those in the control. Chromium(III in Cr-enriched mycelia was mainly combined with protein and polysaccharide. The contents of total amino acids and essential amino acids in Cr-enriched mycelia were increased by (31.25±0.58 and (44.26±0.76 %, respectively.

  1. Corrosion behavior of high purity Fe-Cr-Ni alloys in trans-passive condition

    International Nuclear Information System (INIS)

    Mayuzumi, Masami; Ohta, Jyoji; Kako, Kenji

    1998-01-01

    The corrosion behavior of high-purity (99.99%) Fe-Cr-Ni alloys was investigated in 13 N nitric acid with/without Ce 4+ ions to clarify the effect of impurities on the trans-passive corrosion of stainless steel. The following results were obtained. (1) Almost no intergranular corrosion was observed in the high-purity alloys, although the corrosion rate of the matrix region was nearly the same as that of a commercial stainless steel with the same Cr and Ni content. (2) Due to the improved intergranular corrosion resistance, the effect of the purification became significant in the corrosion condition with the grain-separation being predominant. (3) The high-purity alloys showed higher susceptivility to intergranular corrosion with aging treatment between 873 K and 1073 K. Although the sulfuric acid/copper sulfate test suggested the formation of Cr-depleted zones, a grain boundary micro-analysis using a FETEM with an EDX did not reveal any change in Cr content or impurity segregain along the grain boundaries. The mechanism of corrosion enhancement resulting from the aging treatment remains nuclear. (author)

  2. Accumulation and tolerance characteristics of chromium in a cordgrass Cr-hyperaccumulator, Spartina argentinensis

    International Nuclear Information System (INIS)

    Redondo-Gomez, Susana; Mateos-Naranjo, Enrique; Vecino-Bueno, Inmaculada; Feldman, Susana R.

    2011-01-01

    The cordgrass Spartina argentinensis, which occurs in inland marshes of the Chaco-Pampean regions of Argentina, has been found to be a new chromium hyperaccumulator. A glasshouse experiment was designed to investigate the effect of Cr 6+ from 0 to 20 mmol l -1 on growth and photosynthetic apparatus of S. argentinensis by measuring chlorophyll fluorescence parameters, gas exchange and photosynthetic pigment concentrations. Boron, calcium, chromium, copper, iron, manganese, magnesium, potassium and phosphorous concentrations were also determined. S. argentinensis showed phytotoxicity at tiller concentration of 4 mg g -1 Cr, and symptoms of stress at tiller concentration of 1.5 mg g -1 Cr, as well as reductions in leaf gas exchange, in chlorophyll a fluorescence parameters, in photosynthetic pigment contents and in the uptake of essential nutrients. Reductions in net photosynthetic rate could be accounted for by non-stomatal limitations. Moreover, the bioaccumulator factors exceeded greatly the critical value (1.0) for all Cr treatments, and the transport factors indicated that this species has a higher ability to transfer Cr from roots to tillers at higher Cr concentrations. These results confirmed that S. argentinensis is a chromium hyperaccumulator and that it may be useful for restoring Cr-contaminated sites.

  3. Accumulation and tolerance characteristics of chromium in a cordgrass Cr-hyperaccumulator, Spartina argentinensis

    Energy Technology Data Exchange (ETDEWEB)

    Redondo-Gomez, Susana, E-mail: susana@us.es [Departamento de Biologia Vegetal y Ecologia, Facultad de Biologia, Universidad de Sevilla, Apartado 1095, 41080 Sevilla (Spain); Mateos-Naranjo, Enrique; Vecino-Bueno, Inmaculada [Departamento de Biologia Vegetal y Ecologia, Facultad de Biologia, Universidad de Sevilla, Apartado 1095, 41080 Sevilla (Spain); Feldman, Susana R. [Biologia, Facultad de Ciencias Agrarias y CIUNR, Universidad Nacional de Rosario (Spain)

    2011-01-30

    The cordgrass Spartina argentinensis, which occurs in inland marshes of the Chaco-Pampean regions of Argentina, has been found to be a new chromium hyperaccumulator. A glasshouse experiment was designed to investigate the effect of Cr{sup 6+} from 0 to 20 mmol l{sup -1} on growth and photosynthetic apparatus of S. argentinensis by measuring chlorophyll fluorescence parameters, gas exchange and photosynthetic pigment concentrations. Boron, calcium, chromium, copper, iron, manganese, magnesium, potassium and phosphorous concentrations were also determined. S. argentinensis showed phytotoxicity at tiller concentration of 4 mg g{sup -1} Cr, and symptoms of stress at tiller concentration of 1.5 mg g{sup -1} Cr, as well as reductions in leaf gas exchange, in chlorophyll a fluorescence parameters, in photosynthetic pigment contents and in the uptake of essential nutrients. Reductions in net photosynthetic rate could be accounted for by non-stomatal limitations. Moreover, the bioaccumulator factors exceeded greatly the critical value (1.0) for all Cr treatments, and the transport factors indicated that this species has a higher ability to transfer Cr from roots to tillers at higher Cr concentrations. These results confirmed that S. argentinensis is a chromium hyperaccumulator and that it may be useful for restoring Cr-contaminated sites.

  4. Role of Y in the oxidation resistance of CrAlYN coatings

    Science.gov (United States)

    Domínguez-Meister, S.; El Mrabet, S.; Escobar-Galindo, R.; Mariscal, A.; Jiménez de Haro, M. C.; Justo, A.; Brizuela, M.; Rojas, T. C.; Sánchez-López, J. C.

    2015-10-01

    CrAlYN coatings with different aluminum (4-12 at.%) and yttrium (2-5 at.%) contents are deposited by d.c. reactive magnetron sputtering on silicon and M2 steel substrates using metallic targets and Ar/N2 mixtures. The influence of the nanostructure and chemical elemental distribution on the oxidation resistance after heating in air at 1000 °C is studied by means of cross-sectional scanning electron microscopy (X-SEM), energy dispersive X-ray analysis (EDX), X-ray diffraction (XRD) and glow discharge optical emission spectroscopy (GD-OES). The sequential exposure to the metallic targets during the synthesis leads to a multilayer structure where concentration of metallic elements (Cr, Al and Y) is changing periodically. A good oxidation resistance is observed when Al- and Y-rich regions are separated by well-defined CrN layers, maintaining crystalline coherence along the columnar structure. This protective behavior is independent of the type of substrate and corresponds to the formation of a thin mixed (Al, Cr)-oxide scale that protects the film underneath. The GD-OES and XRD analysis have demonstrated that Y acts as a reactive element, blocking the Fe and C atoms diffusion from the steel and favoring higher Al/Cr ratio in the passivation layer after heating. The coating with Y content around 4 at.% exhibited the best performance with a thinner oxide scale, a delay in the CrN decomposition and transformation to Cr2N, and a more effective Fe and C blocking.

  5. Synthesis and Characterization of High-Entropy Alloy AlFeCoNiCuCr by Laser Cladding

    Directory of Open Access Journals (Sweden)

    Xiaoyang Ye

    2011-01-01

    Full Text Available High-entropy alloys have been recently found to have novel microstructures and unique properties. In this study, a novel AlFeCoNiCuCr high-entropy alloy was prepared by laser cladding. The microstructure, chemical composition, and constituent phases of the synthesized alloy were characterized by SEM, EDS, XRD, and TEM, respectively. High-temperature hardness was also evaluated. Experimental results demonstrate that the AlFeCoNiCuCr clad layer is composed of only BCC and FCC phases. The clad layers exhibit higher hardness at higher Al atomic content. The AlFeCoNiCuCr clad layer exhibits increased hardness at temperature between 400–700°C.

  6. The effect of silicon content on high temperature oxidation of 80Ni-20Cr alloys

    International Nuclear Information System (INIS)

    Takei, Atsushi; Nii, Kazuyoshi

    1981-01-01

    The effect of Si content on the oxidation behavior of 80Ni-20Cr alloys has been studied in the cyclic oxidation in an air stream at 1373K. The addition of 1% and 5%Si to the alloy lowered the mass gain in oxidation, whereas the amount of spalling of oxide scale was increased with the addition of Si. The structure of oxide layers observed by microphotography, X-ray diffraction and electron probe microanalysis (EPMA) were different with the Si content of alloys. The oxide layer of the alloy with 1%Si consists of multi-layers, that is Ni oxide, Cr 2 O 3 and SiO 2 as the external oxide layer. The oxide layer remaining on the alloy with 5%Si, however, was made of a single oxide layer of Cr 2 O 3 containing small amounts of Si and Ni. In spite of the fact that the amount of Si in this alloy is larger than that of the alloy with 1%Si, the SiO 2 oxide layer was not observed at the oxide-alloy interface. It was found by EPMA that the concentration of Si in the oxidized 5%Si alloy substrate was increased in the vicinity of the surface, although Si in the 1%Si alloy was depleted. From the above results the internal oxidation of Si is assumed in the near-surface region of the 5%Si alloy. The internal oxidation of the 5%Si alloy was confirmed by an increase in hardness in the near-surface region. The difference in oxidation behavior between the 1%Si and 5%Si alloys can be understood under the assumption that the oxide layer formed of the 5%Si alloy contained much larger amounts of Ni and Si than that on the 1%Si alloy, and that this oxide layer tends to crack more easily, thus being less protective for the penetration of oxygen. (author)

  7. Microstructure and mechanical properties of Ti-Zr-Cr biomedical alloys.

    Science.gov (United States)

    Wang, Pan; Feng, Yan; Liu, Fengchao; Wu, Lihong; Guan, Shaokang

    2015-06-01

    The Ti-15Zr-xCr (0≤x≤10, wt.%) alloys were investigated to develop new biomedical materials. It was found that the phase constitutions and mechanical properties strongly depended on the Cr content. The Ti-15Zr alloy was comprised of α' phase and a small fraction of β phase was detected with adding 1wt.% Cr. With addition of 5wt.% or more, the β phase was completely retained. In addition, the ω phase was detected in the Ti-15Zr-5Cr alloy and Ti-15Zr-7Cr alloy which exhibited the highest compressive Young's modulus and the lowest ductility. On the other hand, all the Ti-15Zr-xCr alloys without ω phase exhibited high microhardness, high yield strength and superior ductility. Furthermore, the elastic energy of Ti-15Zr-10Cr alloy (5.89MJ/m(3)) with only β phase and that of Ti-15Zr-3Cr alloy (4.04MJ/m(3)) with α' phase and small fraction of β phase was higher than the elastic energy of c.p. Ti (1.25MJ/m(3)). This study demonstrated that Ti-15Zr-3Cr alloy and Ti-15Zr-10Cr alloy with superior mechanical properties are potential materials for biomedical applications. Copyright © 2015. Published by Elsevier B.V.

  8. Inhibited Aluminization of an ODS FeCr Alloy

    International Nuclear Information System (INIS)

    Vande Put Ep Rouaix, Aurelie; Pint, Bruce A.

    2012-01-01

    Aluminide coatings are of interest for fusion energy applications both for compatibility with liquid Pb-Li and to form an alumina layer that acts as a tritium permeation barrier. Oxide dispersion strengthened (ODS) ferritic steels are a structural material candidate for commercial reactor concepts expected to operate above 600 C. Aluminizing was conducted in a laboratory scale chemical vapor deposition reactor using accepted conditions for coating Fe- and Ni-base alloys. However, the measured mass gains on the current batch of ODS Fe-14Cr were extremely low compared to other conventional and ODS alloys. After aluminizing at two different Al activities at 900 C and at 1100 C, characterization showed that the ODS Fe-14Cr specimens formed a dense, primarily AlN layer that prevented Al uptake. This alloy batch contained a higher (> 5000 ppma) N content than the other alloys coated and this is the most likely reason for the inhibited aluminization. Other factors such as the high O content, small (∼ 140 nm) grain size and Y-Ti oxide nano-clusters in ODS Fe-14Cr also could have contributed to the observed behavior. Examples of typical aluminide coatings formed on conventional and ODS Fe- and Ni-base alloys are shown for comparison.

  9. High-temperature mechanical properties of high-purity 70 mass% Cr-Fe alloy

    Energy Technology Data Exchange (ETDEWEB)

    Asahina, M.; Harima, N.; Takaki, S.; Abiko, K. [Tohoku Univ., Sendai (Japan). Inst. for Materials Research

    2002-01-16

    An ingot of high-purity 70 mass% Cr-Fe alloy was prepared by high-frequency induction melting in a high-purity argon atmosphere using a cold copper crucible. Its tensile properties such as hot-ductility and tensile strength were measured, and compared with the results for a high-purity 50 mass% Cr-Fe alloy, a high-purity 60 mass% Cr-Fe alloy and a Ni-based super-alloy. The formation of {sigma}-phase was also examined. The purity of a 70Cr-Fe alloy (70 mass% Cr-Fe alloy) ingot is more than 99.98 mass% and the total amount of gaseous impurities (C, N, O, S, H) in the 70Cr-Fe alloy is 69.9 mass ppm. The strength of the 70Cr-Fe alloy is higher than those of the 60Cr-Fe alloy and the 50Cr-Fe alloy at the temperatures between 293 and 1573 K, without decrease in ductility with increasing Cr content. The 70Cr-Fe alloy also possesses excellent high-temperature ductility. The {sigma}-phase was not observed after aging of 3.6 Ms at 873 K. Consequently, the 70Cr-Fe alloy is an excellent alloy as the base of super heat-resistant alloys. (orig.)

  10. Effect of Cr on the passive film formation mechanism of steel rebar in saturated calcium hydroxide solution

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Ming; Cheng, Xuequn [Corrosion and Protection Center, University of Science and Technology Beijing, Beijing, 100083 (China); Li, Xiaogang, E-mail: lixiaogang@ustb.edu.cn [Corrosion and Protection Center, University of Science and Technology Beijing, Beijing, 100083 (China); Ningbo Institute of Material Technology & Engineering, Chinese Academy of Sciences, Ningbo, 315201, Zhejiang (China); Pan, Yue; Li, Jun [Corrosion and Protection Center, University of Science and Technology Beijing, Beijing, 100083 (China)

    2016-12-15

    Highlights: • Cr inhibits the formation of passive film at the beginning of its formation. • Cr promotes the formation of a denser and more compact passive film. • The passive film thickness presents a slight increase as the content of Cr goes up. - Abstract: Passive films grow on the surface of Cr-modified steels subjected to saturated Ca(OH){sub 2} solution. Electrochemical techniques, such as measurement of open circuit potentials, polarization curves, and electrochemical impedance spectroscopy combined with X-ray photoelectron spectrometer and auger electron spectroscopy, were applied to study the influence of low Cr content on the passive film formation mechanism of steel rebar in saturated Ca(OH){sub 2} solution. Results show that Cr inhibits the formation of passive film at the beginning of its formation. Corrosion current density decreases and polarization resistance increases with the extension of the immersion time. A stable passive film takes at least three days to form. The passive film resistance of HRB400 carbon steel is higher than that of Cr-modified steels in the early stage of immersion (<72 h). The polarization resistance of Cr-modified steel is larger after a stable passive film is formed (>72 h), and Cr promotes the formation of a denser and more compact passive film. The stable passive film is primarily made up of iron oxides with a thickness of 5–6 nm. Cr are involved in the formation of passive films, thereby resulting in a film that consists of an inner layer that contains Cr–Fe oxides and an outer layer that contains Fe oxides, whose thickness presents a slight increase as the content of Cr increases.

  11. Compositional and structural properties of pulsed laser-deposited ZnS:Cr films

    Science.gov (United States)

    Nematollahi, Mohammadreza; Yang, Xiaodong; Seim, Eivind; Vullum, Per Erik; Holmestad, Randi; Gibson, Ursula J.; Reenaas, Turid W.

    2016-02-01

    We present the properties of Cr-doped zinc sulfide (ZnS:Cr) films deposited on Si(100) by pulsed laser deposition. The films are studied for solar cell applications, and to obtain a high absorption, a high Cr content (2.0-5.0 at.%) is used. It is determined by energy-dispersive X-ray spectroscopy that Cr is relatively uniformly distributed, and that local Cr increases correspond to Zn decreases. The results indicate that most Cr atoms substitute Zn sites. Consistently, electron energy loss and X-ray photoelectron spectroscopy showed that the films contain mainly Cr2+ ions. Structural analysis showed that the films are polycrystalline and textured. The films with ~4 % Cr are mainly grown along the hexagonal [001] direction in wurtzite phase. The average lateral grain size decreases with increasing Cr content, and at a given Cr content, increases with increasing growth temperature.

  12. Effect of Cr addition on the structural, magnetic and mechanical properties of magnetron sputtered Ni-Mn-In ferromagnetic shape memory alloy thin films

    Energy Technology Data Exchange (ETDEWEB)

    Akkera, Harish Sharma [Indian Institute of Technology Roorkee, Functional Nanomaterials Research Lab, Department of Physics, Roorkee, Uttarakhand (India); Madanapalle Institute of Technology and Science, Department of Physics, Madanapalle, Chittoor, Andhra Pradesh (India); Kaur, Davinder [Indian Institute of Technology Roorkee, Functional Nanomaterials Research Lab, Department of Physics, Roorkee, Uttarakhand (India)

    2016-12-15

    The effect of Cr substitution for In on the structural, martensitic phase transformation and mechanical properties of Ni-Mn-In ferromagnetic shape memory alloy (FSMA) thin films was systematically investigated. X-ray diffraction results revealed that the Ni-Mn-In-Cr thin films possessed purely austenitic cubic L2{sub 1} structure at lower content of Cr, whereas higher Cr content, the Ni-Mn-In-Cr thin films exhibited martensitic structure at room temperature. The temperature-dependent magnetization (M-T) and resistance (R-T) results confirmed that the monotonous increase in martensitic transformation temperatures (T{sub M}) with the addition of Cr content. Further, the room temperature nanoindentation studies revealed the mechanical properties such as hardness (H), elastic modulus (E), plasticity index (H/E) and resistance to plastic deformation (H{sup 3}/E {sup 2}) of all the samples. The addition of Cr content significantly enhanced the hardness (28.2 ± 2.4 GPa) and resistance to plastic deformation H{sup 3}/E{sup 2} (0.261) of Ni{sub 50.4}Mn{sub 34.96}In{sub 13.56}Cr{sub 1.08} film as compared with pure Ni-Mn-In film. As a result, the appropriate addition of Cr significantly improved the mechanical properties with a decrease in grain size, which could be further attributed to the grain boundary strengthening mechanism. These findings indicate that the Cr-doped Ni-Mn-In FSMA thin films are potential candidates for microelectromechanical systems applications. (orig.)

  13. Neutron irradiation effects in Fe and Fe-Cr at 300 °C

    International Nuclear Information System (INIS)

    Chen, Wei-Ying; Miao, Yinbin; Gan, Jian; Okuniewski, Maria A.; Maloy, Stuart A.; Stubbins, James F.

    2016-01-01

    Fe and Fe-Cr (Cr = 10–16 at.%) specimens were neutron-irradiated at 300 °C to 0.01, 0.1 and 1 dpa. The TEM observations indicated that the Cr significantly reduced the mobility of dislocation loops and suppressed vacancy clustering, leading to distinct damage microstructures between Fe and Fe-Cr. Irradiation-induced dislocation loops in Fe were heterogeneously observed in the vicinity of grown-in dislocations, whereas the loop distribution observed in Fe-Cr is much more uniform. Voids were observed in the irradiated Fe samples, but not in irradiated Fe-Cr samples. Increasing Cr content in Fe-Cr results in a higher density, and a smaller size of irradiation-induced dislocation loops. Orowan mechanism was used to correlate the observed microstructure and hardening, which showed that the hardening in Fe-Cr can be attributed to the formation of dislocation loops and α′ precipitates. -- Graphical abstract: Addition of Cr in Fe suppressed the mobility of mobile 1/2<111> dislocation loops and increased the proportion of immobile <100> dislocation loops, leading to a transition of loop distribution from highly heterogeneous to uniform. Display Omitted

  14. Microstructure and wear behaviour of silicon doped Cr-N nanocomposite coatings

    Energy Technology Data Exchange (ETDEWEB)

    Bao Mingdong, E-mail: bmingd@yahoo.com.c [School of mechanical engineering, Ningbo University of Technology, Ningbo 315016 (China); Yu Lei; Xu Xuebo [School of mechanical engineering, Ningbo University of Technology, Ningbo 315016 (China); He Jiawen [State Key Lab. for Mechanical Behavior of Materials, Xi' an Jiaotong University, Xi' an, 710049 (China); Sun Hailin [Teer Coatings Ltd., Berry Hill Industrial Estate, Droitwich Worcestershire WR9 9AS (United Kingdom); Zhejiang Huijin-Teer Coatings Technolgy Co., Ltd., Lin' an 311305 (China); Teer, D.G. [Teer Coatings Ltd., Berry Hill Industrial Estate, Droitwich Worcestershire WR9 9AS (United Kingdom)

    2009-07-01

    Hard Cr-N and silicon doped Cr-Si-N nanocomposite coatings were deposited using closed unbalanced magnetron sputtering ion plating system. Coatings doped with various Si contents were synthesized by changing the power applied on Si targets. Composition of the films was analyzed using glow discharge optical emission spectrometry (GDOES). Microstructure and properties of the coatings were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), and nano-indentation. The harnesses and the elastic modulus of Cr-Si-N coatings gradually increased with rising of silicon content and exhibited a maximum at silicon content of 4.1 at.% and 5.5 at.%. The maximum hardness and elastic modulus of the Cr-Si-N nanocomposite coatings were approximately 30 GPa and 352 GPa, respectively. Further increase in the silicon content resulted in a decrease in the hardness and the elastic modulus of the coatings. Results from XRD analyses of CrN coatings indicated that strongly preferred orientations of (111) were detected. The diffraction patterns of Cr-Si-N coatings showed a clear (220) with weak (200) and (311) preferred orientations, but the peak of CrN (111) was decreased with the increase of Si concentration. The XRD data of single-phase Si{sub 3}N{sub 4} was free of peak. The peaks of CrN (111) and (220) were shifted slightly and broadened with the increase of silicon content. SEM observations of the sections of Cr-Si-N coatings with different silicon concentrations showed a typical columnar structure. It was evident from TEM observation that nanocomposite Cr-Si-N coatings exhibited nano-scale grain size. Friction coefficient and specific wear rate (SWR) of silicon doped Cr-N coatings from pin-on-disk test were significantly lower in comparison to that of CrN coatings.

  15. Effect of Cu on microstructure, mechanical properties, corrosion resistance and cytotoxicity of CoCrW alloy fabricated by selective laser melting.

    Science.gov (United States)

    Lu, Yanjin; Ren, Ling; Xu, Xiongcheng; Yang, Yang; Wu, Songquan; Luo, Jiasi; Yang, Mingyu; Liu, Lingling; Zhuang, Danhong; Yang, Ke; Lin, Jinxin

    2018-05-01

    In the study, CoCrWCu alloys with differing Cu content (2, 3, 4 wt%) were prepared by selective laser melting using mixture powders consisting of CoCrW and Cu, aiming at investigating the effect of Cu on the microstructures, mechanical properties, corrosion behavior and cytotoxicity. The SEM observations indicated that the Cu content up to 3 wt% caused the Si-rich precipitates to segregate along grain boundaries and in the grains, and EBSD analysis suggested that the Cu addition decreased the recrystallization degree and increased the grain diameter and fraction of big grains. The tensile tests found that the increasing Cu content led to a decrease of mechanical properties compared with Cu-free CoCrW alloy. The electrochemical tests revealed that the addition of Cu shifted the corrosion potential toward nobler positive, but increased the corrosion current density. Also, a more protective passive film was formed when 2 wt% Cu content was added, but the higher Cu content up to 3 wt% was detrimental to the corrosion resistance. It was noted that there was no cytotoxicity for Cu-bearing CoCrW alloys to MG-63 cell and the cells could spread well on the surfaces of studied alloys. Meanwhile, the Cu-bearing CoCrW alloy exhibited an excellent antibacterial performance against E.coli when Cu content was up to 3 wt%. It is suggested that the feasible fabrication of Cu-bearing CoCrW alloy by SLM using mixed CoCrW and Cu powders is a promising candidate for use in antibacterial oral repair products. This current study also can aid in the further design of antibacterial Cu-containing CoCrW alloying powders. Copyright © 2018 Elsevier Ltd. All rights reserved.

  16. Higher adsorption capacity of Spirulina platensis alga for Cr(VI) ions removal: parameter optimisation, equilibrium, kinetic and thermodynamic predictions.

    Science.gov (United States)

    Gunasundari, Elumalai; Senthil Kumar, Ponnusamy

    2017-04-01

    This study discusses about the biosorption of Cr(VI) ion from aqueous solution using ultrasonic assisted Spirulina platensis (UASP). The prepared UASP biosorbent was characterised by Fourier transform infrared spectroscopy, X-ray diffraction, Brunauer-Emmet-Teller, scanning electron spectroscopy and energy dispersive X-ray and thermogravimetric analyses. The optimum condition for the maximum removal of Cr(VI) ions for an initial concentration of 50 mg/l by UASP was measured as: adsorbent dose of 1 g/l, pH of 3.0, contact time of 30 min and temperature of 303 K. Adsorption isotherm, kinetics and thermodynamic parameters were calculated. Freundlich model provided the best results for the removal of Cr(VI) ions by UASP. The adsorption kinetics of Cr(VI) ions onto UASP showed that the pseudo-first-order model was well in line with the experimental data. In the thermodynamic study, the parameters like Gibb's free energy, enthalpy and entropy changes were evaluated. This result explains that the adsorption of Cr(VI) ions onto the UASP was exothermic and spontaneous in nature. Desorption of the biosorbent was done using different desorbing agents in which NaOH gave the best result. The prepared material showed higher affinity for the removal of Cr(VI) ions and this may be an alternative material to the existing commercial adsorbents.

  17. Structural relaxation and colour in the spinel-magnesiochromite (MgAl2O4-MgCr2O4) and gahnite-zincochromite (ZnAl2O4-ZnCr2O4) solid solution series

    Science.gov (United States)

    Hålenius, U.; Andreozzi, G. B.; Skogby, H.

    2009-04-01

    Recent studies on binary mineral solid solution series utilising synchrotron based x-ray absorption spectroscopies have indicated strong structural relaxation. For instance, it has been suggested that the real Cr-O bond distances remain nearly constant (relaxation parameter (ɛ) of 0.85, where ɛ=1 equals full relaxation) over the entire compositional range of the MgAl2O4-MgCr2O4 series (Juhin et al. 2007). In the present study we have measured room temperature optical absorption spectra of synthetic single crystals of the ZnAl2-2xCr2xO4 (0.03?x?1) and MgAl2-2xCr2xO4(0.02?x?1) series with the aim to explore the real architecture of the structure and in particular the Cr-O distance as function of composition. Our crystals were synthesized by means of flux-growth methods under atmospheric pressure and temperature profiles resulting in an estimated cation ordering temperature of ca 850 °C. Crystals close to the spinel (sensu stricto) and gahnite end-member compositions were faintly red in colour. With increasing Cr-content the crystals become more intensely red-coloured and at the higher Cr-contents there is a distinct shift towards a dark greenish colouration. These colour changes are reflected in the measured optical spectra by the position and intensity of the two spin-allowed electronic d-d transitions in octahedrally coordinated Cr3+ at ca 18000 (4A2g -4T2g (4F) transition) and 25000 cm-1(4A2g -4T1g (4F) transition). The energy of the first transition (?1-band) is ca 1200 cm-1 lower in magnesiochromite than in weakly Cr-doped spinel (x=0.02) and ca 1400 cm-1 lower in zincochromite than in gahnite with the lowest Cr-content (x=0.03). Concomitantly the energy of the second transition (?2-band) decreases with increasing Cr-content in both series by ca. 1800 cm-1. From the position of the ?1-band, a decrease in crystal field splitting, 10Dq, for six-coordinated Cr3+ with increasing Cr-content in the MgAl2-2xCr2xO4 and ZnAl2-2xCr2xO4 series of 6.5 and 7

  18. X-ray fluorescence analysis of Cr6+ component in mixtures of Cr2O3 and K2CrO4

    International Nuclear Information System (INIS)

    Tochio, Tatsunori; Sakakura, Shusuke; Oohashi, Hirofumi

    2010-01-01

    X-ray fluorescence analysis using Cr K α spectra was applied to the determination of the mixing ratio of Cr 6+ to (Cr 6+ + Cr 3+ ) in several mixtures of K 2 CrO 4 and Cr 2 O 3 . Because the powder of K 2 CrO 4 contained large particles that were more than 50 μm in diameter, it was ground between a pestle and a mortar for about 8 h. The coarse particles still remaining were removed by using a sieve with 325-mesh (44 μm) in order to reduce the difference in absorption effects between emissions from Cr 6+ and those from Cr 3+ . The mixing ratio, K 2 CrO 4 /(K 2 CrO 4 + Cr 2 O 3 ), of the five mixtures investigated is 0.50, 0.40, 0.20, 0.10, and 0.05 in weight, respectively. Each spectrum obtained was analyzed by decomposing it into two reference spectra, those of the two pure materials, K 2 CrO 4 and Cr 2 O 3 , with a constant background. The results for the mixtures containing K 2 CrO 4 of more than 20 wt% are that the relative deviation from the true value is less than ∼5%. On the other hand, when the content of K 2 CrO 4 decreases to less than 10 wt%, the relative deviation gets so large as 20 - 25%. The error coming from a peak separation of spectrum involved in our results were estimated by applying our method to five sets of data for each mixture computationally generated, taking into account the uncertainty in total counts of real measurements. (author)

  19. X-ray fluorescence analysis of Cr(6+) component in mixtures of Cr(2)O(3) and K(2)CrO(4).

    Science.gov (United States)

    Tochio, Tatsunori; Sakakura, Shusuke; Oohashi, Hirofumi; Mizota, Hirohisa; Zou, Yanhui; Ito, Yoshiaki; Fukushima, Sei; Tanuma, Shigeo; Shoji, Takashi; Fujimura, Hajime; Yamashita, Michiru

    2010-01-01

    X-ray fluorescence analysis using Cr K(alpha) spectra was applied to the determination of the mixing ratio of Cr(6+) to (Cr(6+) + Cr(3+)) in several mixtures of K(2)CrO(4) and Cr(2)O(3). Because the powder of K(2)CrO(4) contained large particles that were more than 50 microm in diameter, it was ground between a pestle and a mortar for about 8 h. The coarse particles still remaining were removed by using a sieve with 325-mesh (44 microm) in order to reduce the difference in absorption effects between emissions from Cr(6+) and those from Cr(3+). The mixing ratio, K(2)CrO(4)/(K(2)CrO(4) + Cr(2)O(3)), of the five mixtures investigated is 0.50, 0.40, 0.20, 0.10, and 0.05 in weight, respectively. Each spectrum obtained was analyzed by decomposing it into two reference spectra, those of the two pure materials, K(2)CrO(4) and Cr(2)O(3), with a constant background. The results for the mixtures containing K(2)CrO(4) of more than 20 wt% are that the relative deviation from the true value is less than approximately 5%. On the other hand, when the content of K(2)CrO(4) decreases to less than 10 wt%, the relative deviation gets so large as 20 - 25%. The error coming from a peak separation of spectrum involved in our results were estimated by applying our method to five sets of data for each mixture computationally generated, taking into account the uncertainty in total counts of real measurements.

  20. Selected Heavy Metals Content in Soil and Arundina graminifolia from Pelepah Kanan Mine, Kota Tinggi, Johor, Malaysia

    International Nuclear Information System (INIS)

    Sahibin Abdul Rahim; Zulfahmi Ali Rahman; Wan Mohd Razi Idris; Azman Hashim; Tukimat Lihan; Muhd Barzani Gasim; Jumaat Adam; Lim, F.N.

    2009-01-01

    Heavy metals composition of Cd, Co, Cr, Ni, Pb and Zn in Arundina graminifolia collected from mining area at Lombong Pelepah Kanan, Kota Tinggi, Johor were determined. The heavy metal content was also analysed in their soil substrates. The plants were separated into different portions for example root, stem and leaf and extracted for their heavy metal content by digestion method whereas the soils heavy metal content was extracted by sequential extraction. Heavy metal content in soil and plant extract was determined using the Flame Atomic Absorption Spectrophotometer. Heavy metal contents of Cd, Cr, Ni and Pb in plants were compared with their content in the control plant, whereas the Co and Zn contents were three to five folds higher. As for heavy metal content in different plant parts, it was found that Cd concentration was high in roots (2.03 mg/ kg) followed by leaf (1.67 mg/ kg) and stem (1.49 mg/ kg). Co concentration was high in leaf (9.26 mg/ kg) followed by root (9.18 mg/ kg) and stem (6.94 mg/ kg). For Cr, the concentration in decreasing sequence was root (0.46 mg/ kg) > leaf (0.19 mg/ kg) > stem (0.08 mg/ kg). Ni concentration was higher in leaf (2.78 mg/ kg) followed by root (2.71 mg/ kg) and stem (1.66 mg/ kg). Concentration in decreasing order was root (10.34 mg/ kg) > leaf (4.18 mg/ kg) > stem (3.75 mg/ kg). Zn concentration was higher in leaf (44.03 mg/ kg) followed by root (32.30 mg/ kg) and stem (13.21 mg/ kg). Total heavy metal content in soil was 2.07 - 5.59 mg/ kg, 8.72 - 39.93 mg/ kg, 1.81 - 2.14 mg/ kg, 2.66 - 6.87 mg/ kg, 23.02 - 51.56 mg/ kg and 0.64 - 2.61 mg/ kg for Ni, Zn, Cd, Pb, Co and Cr, respectively. The available fraction of heavy metals in soil was 21.9 % for Ni, 15.3 % for Zn, 49.9 % for Cd, 19.3 % for Pb, 45.7 % for Co and nil percent for Cr. Biological adsorption coefficient for the heavy metals studied was very low except for Zn where BAC value slightly higher than 1. This plant was not suitable to be used as a phyto

  1. Distribution of chromium species in a Cr-polluted soil: presence of Cr(III) in glomalin related protein fraction.

    Science.gov (United States)

    Gil-Cardeza, María L; Ferri, Alejandro; Cornejo, Pablo; Gomez, Elena

    2014-09-15

    The accumulation of Cr in soil could be highly toxic to human health; therefore Cr soil distribution was studied in rhizosphere soils from Ricinus communis and Conium maculatum and bare soil (BS) from an industrial and urban area in Argentina. Total Cr, Cr(VI) and Cr(III) concentrations were determined in 3 soil fractions: total, extractable and associated to total-glomalin-related protein (T-GRSP). BS had the highest total Cr and total Cr(VI) concentrations. Total Cr(VI) concentration from both rhizosphere soils did not differ from the allowed value for residential area in Argentina (8 μg Cr(VI) g(-1) soil), while total Cr(VI) in BS was 1.8 times higher. Total Cr concentration in all the soils was higher than the allowed value (250 μg Cr g(-1) soil). Extractable and associated to T-GRSP Cr(VI) concentrations were below the detection limit. Cr(III) bound to T-GRSP was the highest in the BS. These findings are in agreement with a long term effect of glomalin in sequestrating Cr. In both plant species, total Cr was higher in root than in shoot and both species presented arbuscular mycorrhizal fungi (AMF). As far as we know, this is the first study that reports the presence of Cr in T-GRSP fraction of soil organic matter. These findings suggest that Cr mycorrhizostabilization could be a predominant mechanism used by R. communis and C. maculatum to diminish Cr soil concentration. Nevertheless, further research is needed to clarify the contribution of native AMF isolated from R. communis and C. maculatum rhizosphere to the Cr phytoremediation process. Copyright © 2014 Elsevier B.V. All rights reserved.

  2. Oxidation study of Cr-Ru hard coatings

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Yung-I, E-mail: yichen@mail.ntou.edu.tw; Kuo, Yu-Chu; Chen, Sin-Min

    2012-01-01

    Cr-Ru alloy coatings with Cr content ranging from 47 to 83 at.% were deposited at 400 Degree-Sign C by direct current magnetron co-sputtering with a Ti interlayer on silicon substrates. With a total input power of 300 W, the Cr content in the Cr-Ru coatings increased linearly with the increasing input power of Cr. The intermetallic compound phase Cr{sub 2}Ru with columnar structure was identified for the as-deposited Cr{sub 56}Ru{sub 44} and Cr{sub 65}Ru{sub 35} coatings, resulting in an increase of hardness up to 15-16 GPa. To evaluate the performance of Cr-Ru coatings as a protective coating on glass molding dies, the annealing treatment was conducted at 600 Degree-Sign C in a 50 ppm O{sub 2}-N{sub 2} atmosphere. The outward diffusion and preferential oxidization of Cr in the Cr-Ru coatings resulted in the variations of the crystalline structure, chemical composition distribution, and surface hardness after annealing. X-ray diffraction and transmission electron microscopy (TEM) proved that an oxide scale consisting of Cr{sub 2}O{sub 3} formed on the free surface. Scanning electron microscopy and TEM observed the surface morphology and structural variation. The chemical composition depth profiles were analyzed by Auger electron microscopy, verifying the presence of a Cr-depleted zone beneath the oxide scale. The hardness of Cr{sub 56}Ru{sub 44} and Cr{sub 65}Ru{sub 35} coatings decreased to 11-12 GPa after annealing, accompanied by the replacement of the Cr{sub 2}Ru phase by the Ru phase. - Highlights: Black-Right-Pointing-Pointer We prepared crystalline Cr-Ru alloy coatings by direct current magnetron sputtering. Black-Right-Pointing-Pointer Cr-Ru coatings were annealed at 600 Degree-Sign C for 2 h in a 50 ppm O{sub 2}-N{sub 2} atmosphere. Black-Right-Pointing-Pointer Cr diffused outwardly and oxidized to form a stable and protective oxide scale. Black-Right-Pointing-Pointer The original columnar grains recrystallized to polycrystalline grains.

  3. Synthesis and chemistry of chromium in CrAPO-5 molecular sieves

    NARCIS (Netherlands)

    Weckhuysen, B.M.; Schoonheydt, R.A.

    1994-01-01

    CrAPO-5 molecular sieves were synthesized hydrothermally starting with different Cr precursors and Cr and template contents. The behavior of Cr was investigated spectroscopically by diffuse reflectance spectroscopy (d.r.s.) and electron spin resonance (e.s.r.). In the gels, Cr 3+ and Cr 8+ are

  4. Corrosion testing of NiCrAl(Y) coating alloys in high-temperature and supercritical water

    International Nuclear Information System (INIS)

    Biljan, S.; Huang, X.; Qian, Y.; Guzonas, D.

    2011-01-01

    With the development of Generation IV (Gen IV) nuclear power reactors, materials capable of operating in high-temperature and supercritical water environment are essential. This study focuses on the corrosion behavior of five alloys with compositions of Ni20Cr, Ni5Al, Ni50Cr, Ni20Cr5Al and Ni20Cr10AlY above and below the critical point of water. Corrosion tests were conducted at three different pressures, while the temperature was maintained at 460 o C, in order to examine the effects of water density on the corrosion. From the preliminary test results, it was found that the binary alloys Ni20Cr and Ni50Cr showed weight loss above the critical point (23.7 MPa and 460 o C). The higher Cr content alloy Ni50Cr suffered more weight loss than Ni-20Cr under the same conditions. Accelerated weight gain was observed above the critical point for the binary alloy Ni5Al. The combination of Cr, Al and Y in Ni20Cr10AlY provides stable scale formation under all testing conditions employed in this study. (author)

  5. MD simulation of atomic displacement cascades in Fe-10 at.%Cr binary alloy

    International Nuclear Information System (INIS)

    Tikhonchev, M.; Svetukhin, V.; Kadochkin, A.; Gaganidze, E.

    2009-01-01

    Molecular dynamics simulation of atomic displacement cascades up to 20 keV has been performed in Fe-10 at.%Cr binary alloy at a temperature of 600 K. The N-body interatomic potentials of Finnis-Sinclair type were used. According to the obtained results the dependence of 'surviving' defects amount is well approximated by power function that coincides with other researchers' results. Obtained cascade efficiency for damage energy in the range from 10 to 20 keV is ∼0.2 NRT that is slightly higher than for pure α-Fe. In post-cascade area Cr fraction in interstitials is in range 2-5% that is essentially lower than Cr content in the base alloy. The results on size and amount of vacancy and interstitial clusters generated in displacement cascades are obtained. For energies of 2 keV and higher the defect cluster average size increases and it is well approximated by a linear dependence on cascade energy both for interstitials and vacancies.

  6. MD simulation of atomic displacement cascades in Fe-10 at.%Cr binary alloy

    Energy Technology Data Exchange (ETDEWEB)

    Tikhonchev, M., E-mail: tikhonchev@sv.ulsu.r [Ulyanovsk State University, Leo Tolstoy Str., 42, Ulyanovsk 432970 (Russian Federation); Joint Stock Company, ' State Scientific Center Research Institute of Atomic Reactors' , 433510 Dimitrovgrad-10 (Russian Federation); Svetukhin, V.; Kadochkin, A. [Ulyanovsk State University, Leo Tolstoy Str., 42, Ulyanovsk 432970 (Russian Federation); Gaganidze, E. [Forschungszentrum Karlsruhe, IMF II, 3640, D-76021 Karlsruhe (Germany)

    2009-12-15

    Molecular dynamics simulation of atomic displacement cascades up to 20 keV has been performed in Fe-10 at.%Cr binary alloy at a temperature of 600 K. The N-body interatomic potentials of Finnis-Sinclair type were used. According to the obtained results the dependence of 'surviving' defects amount is well approximated by power function that coincides with other researchers' results. Obtained cascade efficiency for damage energy in the range from 10 to 20 keV is approx0.2 NRT that is slightly higher than for pure alpha-Fe. In post-cascade area Cr fraction in interstitials is in range 2-5% that is essentially lower than Cr content in the base alloy. The results on size and amount of vacancy and interstitial clusters generated in displacement cascades are obtained. For energies of 2 keV and higher the defect cluster average size increases and it is well approximated by a linear dependence on cascade energy both for interstitials and vacancies.

  7. Chemical diffusion of Cr, Ni and Si in welded joints. II

    International Nuclear Information System (INIS)

    Kucera, J.; Ciha, K.

    1987-01-01

    The results are given of a study in chemical diffusion in welded joints P2/A and P3/A. P2 stands for the steel (Fe-17.48 Cr-8.15 Ni-0.14 Si), P3 for (Fe-18.52 Cr-8.20 Ni-1.78 Si) and A for the Fe-Arema. Triadic sandwiche-like samples were diffusion heated at temperatures from 920 to 1170 degC. The concentration distributions N(x,t) of the given elements were measured with microprobe JXA-3A. The evaluation of the experimental data was carried out either by Grube's method, or in some cases by the spline-polynomial method. The evaluated diffusivities D-bar satisfy the Arrhenius relation and yield the standard diffusion characteristics D 0 and H. The diffusivities D-bar of Cr, Ni and Si in P1/A, in P2/A and P3/A welded joints vary with Si content in P1, P2 and P3 alloys, similar to the Cr-51 and Ni-63 self-diffusivities in Fe-18 Cr-12 Ni-X Si steels, and tend to increase with increasing Si content. The values D-bar measured in the vicinity of grain boundaries are higher than the bulk diffusion coefficients. The most rapid diffusant is Si and the slowest one Ni. Thus, the relations D-bar Si :D-bar Cr :D-bar Ni ≅ 6:3:1 (P3/A) and D-bar Si :D-bar Cr :D-bar Ni ≅ 1.7:1.4:1 (P3/A) are valid at 1050 degC. Comparing the results with those published if can be noted that the Cr-51 and Ni-63 self-diffusion in Fe-18 Cr-12 Ni-X Si steels is faster than chemical diffusion of these elements in the said steel welded joints P2/A and P3/A; X varies from 0.14 to 1.98. (author). 7 tabs., 7 figs., 20 refs

  8. Role of Y in the oxidation resistance of CrAlYN coatings

    Energy Technology Data Exchange (ETDEWEB)

    Domínguez-Meister, S.; El Mrabet, S. [Instituto de Ciencia de Materiales de Sevilla (CSIC-Univ. Sevilla), Avda., Américo Vespucio 49, Sevilla 41092 (Spain); Escobar-Galindo, R. [Instituto de Ciencia de Materiales de Madrid (ICMM-CSIC), Sor Juana Inés de la Cruz 3, Cantoblanco 28049 (Spain); Mariscal, A.; Jiménez de Haro, M.C.; Justo, A. [Instituto de Ciencia de Materiales de Sevilla (CSIC-Univ. Sevilla), Avda., Américo Vespucio 49, Sevilla 41092 (Spain); Brizuela, M. [TECNALIA, Mikeletegui Pasealekua, 2, Donostia-San Sebastián 20009 (Spain); Rojas, T.C. [Instituto de Ciencia de Materiales de Sevilla (CSIC-Univ. Sevilla), Avda., Américo Vespucio 49, Sevilla 41092 (Spain); Sánchez-López, J.C., E-mail: jcslopez@icmse.csic.es [Instituto de Ciencia de Materiales de Sevilla (CSIC-Univ. Sevilla), Avda., Américo Vespucio 49, Sevilla 41092 (Spain)

    2015-10-30

    Highlights: • The oxidation behavior of CrAlYN films (Al < 10 at.%) depends on the Al/Y distribution. • ∼4 at.% Y enhances the oxidation resistance up to 1000 °C of CrAlYN-coated M2 steels. • Controlled inward oxygen diffusion affects positively the film oxidation resistance. • Mixed Al–Y oxides appear to block the diffusion of elements from the substrate. • Yttrium modifies the passivation layer composition by increasing the Al/Cr ratio. - Abstract: CrAlYN coatings with different aluminum (4–12 at.%) and yttrium (2–5 at.%) contents are deposited by d.c. reactive magnetron sputtering on silicon and M2 steel substrates using metallic targets and Ar/N{sub 2} mixtures. The influence of the nanostructure and chemical elemental distribution on the oxidation resistance after heating in air at 1000 °C is studied by means of cross-sectional scanning electron microscopy (X-SEM), energy dispersive X-ray analysis (EDX), X-ray diffraction (XRD) and glow discharge optical emission spectroscopy (GD-OES). The sequential exposure to the metallic targets during the synthesis leads to a multilayer structure where concentration of metallic elements (Cr, Al and Y) is changing periodically. A good oxidation resistance is observed when Al- and Y-rich regions are separated by well-defined CrN layers, maintaining crystalline coherence along the columnar structure. This protective behavior is independent of the type of substrate and corresponds to the formation of a thin mixed (Al, Cr)-oxide scale that protects the film underneath. The GD-OES and XRD analysis have demonstrated that Y acts as a reactive element, blocking the Fe and C atoms diffusion from the steel and favoring higher Al/Cr ratio in the passivation layer after heating. The coating with Y content around 4 at.% exhibited the best performance with a thinner oxide scale, a delay in the CrN decomposition and transformation to Cr{sub 2}N, and a more effective Fe and C blocking.

  9. Correlation between heavy metal contents and antioxidant activities in medicinal plants grown in copper mining areas

    International Nuclear Information System (INIS)

    Maharia, R.S.; Dutta, R.K.; Acharya, R.; Reddy, A.V.R.

    2012-01-01

    Three commonly used medicinal plants, e.g., Adhatoda vasica, Cassia fistula, and Withania somnifera grown in two contrasting environmental conditions, namely from copper mining site and from control site corresponding to soil not contaminated with Cu, to understand correlations between high Cu bioaccumulation in medicinal plants on their antioxidant activities. Concentrations of some essential metals, e.g., Cr, Mn, Fe, Cu, Zn, and Se in the leaves of these plants were measured by instrumental neutron activation analysis. The Cu levels in the samples from mining site were in the range of 32.6 to 57.2 mg/kg, which were 5-7 folds higher than the control samples, while Cr levels were about 2-folds higher in the mining site. Speciation studies of Cr revealed negligible content of toxic hexavalent Cr. Antioxidant assay of these plants from both the sampling sites, measured as total phenolic content, total flavonoid content, 2,2'-diphenyl-1-picrylhydrazyl, free radical scavenging ability, and chelating ability with ferrous ions exhibited maximum activity for A. vasica, while that of W. somnifera was minimum. However, the variations in the antioxidant activities for each medicinal plant species from mining site and control site did not reveal significant differences. (author)

  10. Oxidation of Cr(III)-Fe(III) Mixed-phase Hydroxides by Chlorine: Implications on the Control of Hexavalent Chromium in Drinking Water.

    Science.gov (United States)

    Chebeir, Michelle; Liu, Haizhou

    2018-05-17

    The occurrence of chromium (Cr) as an inorganic contaminant in drinking water is widely reported. One source of Cr is its accumulation in iron-containing corrosion scales of drinking water distribution systems as Cr(III)-Fe(III) hydroxide, i.e., FexCr(1-x)(OH)3(s), where x represents the Fe(III) molar content and typically varies between 0.25 and 0.75. This study investigated the kinetics of inadvertent hexavalent chromium Cr(VI) formation via the oxidation of FexCr(1-x)(OH)3(s) by chlorine as a residual disinfectant in drinking water, and examined the impacts of Fe(III) content and drinking water chemical parameters including pH, bromide and bicarbonate on the rate of Cr(VI) formation. Data showed that an increase in Fe(III) molar content resulted in a significant decrease in the stoichiometric Cr(VI) yield and the rate of Cr(VI) formation, mainly due to chlorine decay induced by Fe(III) surface sites. An increase in bicarbonate enhanced the rate of Cr(VI) formation, likely due to the formation of Fe(III)-carbonato surface complexes that slowed down the scavenging reaction with chlorine. The presence of bromide significantly accelerated the oxidation of FexCr(1-x)(OH)3(s) by chlorine, resulting from the catalytic effect of bromide acting as an electron shuttle. A higher solution pH between 6 and 8.5 slowed down the oxidation of Cr(III) by chlorine. These findings suggested that the oxidative conversion of chromium-containing iron corrosion products in drinking water distribution systems can lead to the occurrence of Cr(VI) at the tap, and the abundance of iron, and a careful control of pH, bicarbonate and bromide levels can assist the control of Cr(VI) formation.

  11. Further improvement of mechanical and tribological properties of Cr-doped diamond-like carbon nanocomposite coatings by N codoping

    Science.gov (United States)

    Zou, Changwei; Xie, Wei; Tang, Xiaoshan

    2016-11-01

    In this study, the effects of nitrogen codoping on the microstructure and mechanical properties of Cr-doped diamond-like carbon (DLC) nanocomposite coatings were investigated in detail. Compared with undoped DLC coatings, the Cr-DLC and N/Cr-DLC coatings showed higher root-mean-square (RMS) roughness values. However, from the X-ray photoelectron spectroscopy (XPS) and Raman results, the fraction of sp2 carbon bonds of N/Cr-DLC coatings increased with increasing N content, which indicated the graphitization of the coatings. The hardness and elastic modulus of N/Cr-DLC coatings with 1.8 at. % N were about 26.8 and 218 GPa, respectively. The observed hardness increase with N codoping was attributed to the incorporation of N in the C network along with the formation of CrC(N) nanoparticles, as confirmed from the transmission electron microscopy (TEM) results. The internal stress markedly decreased from 0.93 to 0.32 GPa as the N content increased from 0 to 10.3 at. %. Furthermore, N doping significantly improved the high-temperature dry friction behavior of DLC coatings. The friction coefficient of N/Cr-DLC coatings with 8.0 and 10.3 at. % N was kept at about 0.2 during the overall sliding test at 500 °C. These results showed that appropriate N doping could promote the mechanical and tribological properties of Cr-DLC nanocomposite coatings.

  12. Elder Abuse and Neglect Content in Higher Education Programs on Aging.

    Science.gov (United States)

    Stein, Karen F.

    This study sought to: (1) investigate the degree to which course content on elder abuse and neglect is a part of higher education curriculums in aging; (2) determine which specific elder abuse and neglect course content is included in required and elective coursework; and (3) describe the attitudes of instructors toward including elder abuse and…

  13. Distribution coefficients for Pb+2 and Cr+6 with variation in soil particle size

    International Nuclear Information System (INIS)

    Singhal, R.K.; Preetha, J.; Gurg, R.P.

    2003-01-01

    Simulated experiments were conducted in the laboratory to evaluate the impact of soil particle size on the distribution coefficient (K d ) for soil - water system for Pb as Pb +2 and Cr as Cr +6 . The variation in particle size leads to variation in mineralogical and organic carbon (OC) contents which in turn lead to variation in cation exchange capacity (CEC). The conditions were kept as close to that of the natural environment during the spiking of the soil. The spiked soil is fractionated in seven different fractions between 500 - 355 μm and 105 - > 75 μm contains relatively higher percentage of OC than the other fractions. The CEC of different fractions of the soil is determined by ammonium acetate method. Higher CEC was observed for particle in the range of 105 - > 75 μm. The analysis of Pb and Cr was carried out using Atomic Absorption Spectrometer after the complete destruction f the soil matrix. Among the various fractions, the K d values are higher for 75μm for Pb +2 and Cr +6 and their ranges are 4.3-9.6 x 10 5 ml/gm and 2.1-24.8 x 10 6 ml/gm, respectively. (author)

  14. Preliminary assessment of metal-porcelain bonding strength of CoCrW alloy after 3 wt.% Cu addition

    International Nuclear Information System (INIS)

    Lu, Yanjin; Zhao, Chaoqian; Ren, Ling; Guo, Sai; Gan, Yiliang; Yang, Chunguang; Wu, Songquan; Lin, Junjie; Huang, Tingting; Yang, Ke; Lin, Jinxin

    2016-01-01

    In this work, a novel Cu-bearing CoCrW alloy fabricated by selective laser melting for dental application has been studied. For its successful application, the bonding strength of metal-porcelain is essential to be systematically investigated. Therefore, the aim of this study was to evaluate the metal-porcelain bonding strength of CoCrWCu alloy by three-point bending test, meanwhile the Ni-free CoCrW alloy was used as control. The oxygen content was investigated by an elemental analyzer; X-ray photoelectron spectroscopy (XPS) was used to analyze the surface chemical composition of CoCrW based alloy after preoxidation treatment; the fracture mode was investigated by X-ray energy spectrum analysis (EDS) and scanning electron microscope (SEM). Result from the oxygen content analysis showed that the content of oxygen dramatically increased after the Cu addition. And the XPS suggested that Co-oxidation, Cr_2O_3, CrO_2, WO_3, Cu_2O and CuO existed on the preoxidated surface of the CoCrWCu alloy; the three-point bending test showed that the bonding strength of the CoCrWCu alloy was 43.32 MPa, which was lower than that of the CoCrW group of 47.65 MPa. However, the average metal-porcelain bonding strength is significantly higher than the minimum value in the ISO 9693 standard. Results from the SEM images and EDS indicated that the fracture mode of CoCrWCu-porcelain was mixed between cohesive and adhesive. Based on the results obtained in this study, it can be indicated that the Cu-bearing CoCrW alloy fabricated by the selective laser melting is a promising candidate for use in dental application. - Highlights: • The bonding strength of metal-porcelain was slightly decreased with Cu addition; • Cu not only led to promote the diffusion of O and W element but also inhibited the diffusivity of Co in the outward direction; • The changed oxidation behavior resulted in lowering the bonding strength;

  15. Preliminary assessment of metal-porcelain bonding strength of CoCrW alloy after 3 wt.% Cu addition

    Energy Technology Data Exchange (ETDEWEB)

    Lu, Yanjin; Zhao, Chaoqian [Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155Yangqiao Road West, Fuzhou (China); Ren, Ling [Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang (China); Guo, Sai; Gan, Yiliang [Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155Yangqiao Road West, Fuzhou (China); Yang, Chunguang [Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang (China); Wu, Songquan; Lin, Junjie; Huang, Tingting [Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155Yangqiao Road West, Fuzhou (China); Yang, Ke, E-mail: kyang@imr.ac.cn [Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang (China); Lin, Jinxin, E-mail: franklin@fjirsm.ac.cn [Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155Yangqiao Road West, Fuzhou (China)

    2016-06-01

    In this work, a novel Cu-bearing CoCrW alloy fabricated by selective laser melting for dental application has been studied. For its successful application, the bonding strength of metal-porcelain is essential to be systematically investigated. Therefore, the aim of this study was to evaluate the metal-porcelain bonding strength of CoCrWCu alloy by three-point bending test, meanwhile the Ni-free CoCrW alloy was used as control. The oxygen content was investigated by an elemental analyzer; X-ray photoelectron spectroscopy (XPS) was used to analyze the surface chemical composition of CoCrW based alloy after preoxidation treatment; the fracture mode was investigated by X-ray energy spectrum analysis (EDS) and scanning electron microscope (SEM). Result from the oxygen content analysis showed that the content of oxygen dramatically increased after the Cu addition. And the XPS suggested that Co-oxidation, Cr{sub 2}O{sub 3}, CrO{sub 2}, WO{sub 3}, Cu{sub 2}O and CuO existed on the preoxidated surface of the CoCrWCu alloy; the three-point bending test showed that the bonding strength of the CoCrWCu alloy was 43.32 MPa, which was lower than that of the CoCrW group of 47.65 MPa. However, the average metal-porcelain bonding strength is significantly higher than the minimum value in the ISO 9693 standard. Results from the SEM images and EDS indicated that the fracture mode of CoCrWCu-porcelain was mixed between cohesive and adhesive. Based on the results obtained in this study, it can be indicated that the Cu-bearing CoCrW alloy fabricated by the selective laser melting is a promising candidate for use in dental application. - Highlights: • The bonding strength of metal-porcelain was slightly decreased with Cu addition; • Cu not only led to promote the diffusion of O and W element but also inhibited the diffusivity of Co in the outward direction; • The changed oxidation behavior resulted in lowering the bonding strength;.

  16. Effect of Cr-N codoping on structural phase transition, Raman modes, and optical properties of TiO2 nanoparticles

    Science.gov (United States)

    Hassnain Jaffari, G.; Tahir, Adnan; Ali, Naveed Zafar; Ali, Awais; Qurashi, Umar S.

    2018-04-01

    Noncompensated cation-anion codoping in TiO2 nanoparticles has been achieved by a chemical synthesis route. Significant reduction in the optical bandgap and enhancement in the absorption of visible light have been observed. Structural phase transformation has been tracked in detail as a function of doping and heat treatment temperature. Anatase to rutile phase transition temperature for doped samples was higher in comparison to the pure TiO2 nanoparticles. Nitrogen and chromium addition increases the phase transformation barrier, where the effect of the former dopant is of more significance. The Raman results showed an increase in the oxygen content with higher post annealing temperatures. With Cr incorporation, the peak associated with the Eg mode has been found to shift towards a higher wave number, while with nitrogen incorporation, the shift was towards a lower wave number. A decrease in reflectance with N co-doping for all samples, irrespective of phase and annealing temperatures, has been observed. In compositions with nitrogen of the same content, bandgap reduction was higher in the rutile phase in comparison to the anatase phase. In general, overall results revealed that with a higher loading fraction of ammonia, the N content increases, while Cr addition prevents nitrogen loss even up to high post annealing temperatures, i.e., 850 °C.

  17. Evaluation of the tolerance of three cultivars of barley to Zn, Cd or Cr in a growth chamber experiment

    Directory of Open Access Journals (Sweden)

    González A.

    2013-04-01

    Full Text Available To evaluate the tolerance of three cultivars of barley for the phytoremediation of soils contaminated by metals, a growth chamber experiment with plants exposed to increasing concentrations of Zn, Cd and Cr was conducted. Growth parameters, chlorophyll content and chlorophyll fluorescence were measured at 15 and 29 days after treatment application. Metal concentration in the plant was also measured. In all cases, the amount of metal accumulated in the plant increased by increasing the concentration of the applied metal. Chlorophyll content and chlorophyll fluorescence were higher in the first sampling indicating the negative effect on these parameters of the highest metal concentrations. Cr treatments affected significantly plant growth. Height and dry weights plants were significantly lower (p <0.05 than those treated with Zn and Cd. Physiological parameters measured and water content were also lower in plants treated with Cr. Plaisant and Pedrezuela varieties accumulated more Zn and Cd than Reinette, which accumulated greater amount of Cr than the other two cultivars. This fact shows the interest in selecting the most tolerant varieties when using a crop for phytoremediation of contaminated soils.

  18. Structure change in 25 Cr - 20 Ni steels as a function of their Cr, Ni, Si and W content

    International Nuclear Information System (INIS)

    Gribaudo, L.M.; Durand, F.; Durand-Charre, M.

    1983-01-01

    The influence of varying the Cr, Ni, Si and W concentrations on the type and composition of the carbides of solidification and on the phase shift temperature is studied with 18 alloys of composition close to stainless steel-25-20 (AISI 310) composition. Experimental techniques used are differential thermal analysis, microprobe and scanning electron microscope. Crystallization is interpreted with the equilibrium diagram Ni-Cr-C. The formation of the interdendritic σ phase for a chromium rich alloys is interpreted with the phase equilibrium diagram of Fe-Ni-Cr-C. Mechanical properties and corrosion resistance are dependent on the morphology of the carbides M 7 C 3 and M 23 C 6 [fr

  19. Study on Cr(VI) Leaching from Cement and Cement Composites

    Science.gov (United States)

    Palascakova, Lenka; Kanuchova, Maria

    2018-01-01

    This paper reports an experimental study on hexavalent chromium leaching from cement samples and cement composites containing silica fume and zeolite additions that were subjected to various leaching agents. The water-soluble Cr(VI) concentrations in cements ranged from 0.2 to 3.2 mg/kg and represented only 1.8% of the total chromium content. The presence of chromium compounds with both chromium oxidation states of III and VI was detected in the cement samples by X-ray photoelectron spectroscopy (XPS). Leaching tests were performed in a Britton-Robinson buffer to simulate natural conditions and showed increased dissolution of Cr(VI) up to 6 mg/kg. The highest amount of leached hexavalent chromium was detected after leaching in HCl. The findings revealed that the leaching of chromium from cements was higher by 55–80% than that from the cement composites. A minimum concentration was observed for all cement samples when studying the relationship between the soluble Cr(VI) and the cement storage time. PMID:29690550

  20. Influence of Fe(Cr) miscibility on thin film grain size and stress

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, Xuyang; Kaub, Tyler; Martens, Richard L.; Thompson, Gregory B., E-mail: gthompson@eng.ua.edu

    2016-08-01

    During the post coalescence portion of thin film deposition, thin film stress is related to the grain size and adatom mobility of the depositing material. Using a Fe(Cr) alloy thin film, the manipulation of the tensile stress for thick films was studied as a function of Cr solute content up to 8 at.%. Solute concentrations up to 4 at.% resulted in an approximate 50% increase in grain size that resulted in a reduction of the tensile stress to be lower than either elemental film. Upon increasing the Cr content, the grain size refined and the tensile stress of the films increased. Atom probe characterization of the grain boundaries confirmed Cr chemical partitioning which refined the grain size and altered the film's texture, both of which contributed to the change in film stress. The use of intrinsic segregation, rather than deposition processing parameters, appears to be another viable option for regulating film stress. - Highlights: • Solute segregation to regulate grain size in controlling film stress • Quantification of Cr interfacial excess as a function of alloy content • Quantification of texture fiber alignment as a function of Cr content.

  1. From solid solution to cluster formation of Fe and Cr in α-Zr

    International Nuclear Information System (INIS)

    Burr, P.A.; Wenman, M.R.; Gault, B.; Moody, M.P.; Ivermark, M.; Rushton, M.J.D.; Preuss, M.; Edwards, L.; Grimes, R.W.

    2015-01-01

    To understand the mechanisms by which the re-solution of Fe and Cr additions increase the corrosion rate of irradiated Zr alloys, the solubility and clustering of Fe and Cr in model binary Zr alloys was investigated using a combination of experimental and modelling techniques — atom probe tomography (APT), x-ray diffraction (XRD), thermoelectric power (TEP) and density functional theory (DFT). Cr occupies both interstitial and substitutional sites in the α-Zr lattice; Fe favours interstitial sites, and a low-symmetry site that was not previously modelled is found to be the most favourable for Fe. Lattice expansion as a function of Fe and Cr content in the α-Zr matrix deviates from Vegard's law and is strongly anisotropic for Fe additions, expanding the c-axis while contracting the a-axis. Matrix content of solutes cannot be reliably estimated from lattice parameter measurements, instead a combination of TEP and APT was employed. Defect clusters form at higher solution concentrations, which induce a smaller lattice strain compared to the dilute defects. In the presence of a Zr vacancy, all two-atom clusters are more soluble than individual point defects and as many as four Fe or three Cr atoms could be accommodated in a single Zr vacancy. The Zr vacancy is critical for the increased apparent solubility of defect clusters; the implications for irradiation induced microstructure changes in Zr alloys are discussed.

  2. From solid solution to cluster formation of Fe and Cr in α-Zr

    Energy Technology Data Exchange (ETDEWEB)

    Burr, P.A., E-mail: burr.patrick@gmail.com [Centre for Nuclear Engineering and Department of Materials, Imperial College London, London, SW7 2AZ (United Kingdom); Institute of Materials Engineering, Australian Nuclear Science & Technology Organisation, Menai, New South Wales 2234 (Australia); Wenman, M.R. [Centre for Nuclear Engineering and Department of Materials, Imperial College London, London, SW7 2AZ (United Kingdom); Gault, B.; Moody, M.P. [Department of Materials, University of Oxford, Parks Road, Oxford, OX1 3PH (United Kingdom); Ivermark, M. [High Temperature Materials, Sandvik Materials Technology, 734 27 Hallstahammar (Sweden); University of Manchester, School of Materials, M13 9PL (United Kingdom); Rushton, M.J.D. [Centre for Nuclear Engineering and Department of Materials, Imperial College London, London, SW7 2AZ (United Kingdom); Preuss, M. [University of Manchester, School of Materials, M13 9PL (United Kingdom); Edwards, L. [Institute of Materials Engineering, Australian Nuclear Science & Technology Organisation, Menai, New South Wales 2234 (Australia); Grimes, R.W. [Centre for Nuclear Engineering and Department of Materials, Imperial College London, London, SW7 2AZ (United Kingdom)

    2015-12-15

    To understand the mechanisms by which the re-solution of Fe and Cr additions increase the corrosion rate of irradiated Zr alloys, the solubility and clustering of Fe and Cr in model binary Zr alloys was investigated using a combination of experimental and modelling techniques — atom probe tomography (APT), x-ray diffraction (XRD), thermoelectric power (TEP) and density functional theory (DFT). Cr occupies both interstitial and substitutional sites in the α-Zr lattice; Fe favours interstitial sites, and a low-symmetry site that was not previously modelled is found to be the most favourable for Fe. Lattice expansion as a function of Fe and Cr content in the α-Zr matrix deviates from Vegard's law and is strongly anisotropic for Fe additions, expanding the c-axis while contracting the a-axis. Matrix content of solutes cannot be reliably estimated from lattice parameter measurements, instead a combination of TEP and APT was employed. Defect clusters form at higher solution concentrations, which induce a smaller lattice strain compared to the dilute defects. In the presence of a Zr vacancy, all two-atom clusters are more soluble than individual point defects and as many as four Fe or three Cr atoms could be accommodated in a single Zr vacancy. The Zr vacancy is critical for the increased apparent solubility of defect clusters; the implications for irradiation induced microstructure changes in Zr alloys are discussed.

  3. Effect of Ti/Cr content on the microstructures and hydrogen storage properties of Laves phase-related body-centered-cubic solid solution alloys

    Energy Technology Data Exchange (ETDEWEB)

    Young, K., E-mail: kwo.young@basf.com [BASF/Battery Materials-Ovonic, 2983 Waterview Drive, Rochester Hills, MI 48309 (United States); Wong, D.F. [BASF/Battery Materials-Ovonic, 2983 Waterview Drive, Rochester Hills, MI 48309 (United States); Department of Chemical Engineering and Materials Science, Wayne State University, MI 48202 (United States); Wang, L. [BASF/Battery Materials-Ovonic, 2983 Waterview Drive, Rochester Hills, MI 48309 (United States)

    2015-02-15

    Highlights: • Influences of Ti/Cr to BCC to hydrogen storage properties were reported. • A new activation using hydrogen pressure at 5 MPa was developed. • A discharge capacity of 463 mA h g{sup −1} was reported on a C14(36%)/BCC(64%) alloy. • Increase in Ti/Cr increases storage capacity and decreases high-rate performance. • The high-rate performance was dominated by the surface reaction. - Abstract: A series of BCC/C14 mixed phase alloys with the chemical composition of Ti{sub 13.6+x}Zr{sub 2.1}V{sub 44}Cr{sub 13.2−x}Mn{sub 6.9}Fe{sub 2.7}Co{sub 1.4}Ni{sub 15.7}Al{sub 0.3}, x = 0, 2, 4, 6, 8, 10, and 12, was fabricated, and their structural, gaseous phase and electrochemical hydrogen storage properties were studied. Raising the maximum pressure for measuring the gaseous hydrogen storage capacity allowed these alloys to reach full activation, and the maximum discharge capacities ranged from 375 to 463 mA h g{sup −1}. As the Ti/Cr ratio in the alloy composition increased, the maximum gaseous hydrogen storage capacity improved due to the expansion in both BCC and C14 unit cells. However, reversibility decreased due to the higher stability of the hydride phase, as indicated by the lower equilibrium pressures measured for these alloys. As with most other metal hydride alloys, the electrochemical capacities measured at 50 and 4 mA g{sup −1} fell between the boundaries set by the maximum and reversible gaseous hydrogen storage capacities. The poorer high-rate dischargeability observed with higher Ti/Cr ratios was attributed to the lower surface exchange current (less catalytic). Two other negative impacts observed with higher Ti/Cr ratios in the alloy composition are poorer cycle stability and lower open-circuit voltage.

  4. Content of Heavy Metal in the Dust of Leisure Squares and Its Health Risk Assessment-A Case Study of Yanta District in Xi'an.

    Science.gov (United States)

    Shao, Tianjie; Pan, Lihuan; Chen, Zhiqing; Wang, Ruiyuan; Li, Wenjing; Qin, Qing; He, Yuran

    2018-02-25

    Taking Yanta District in Xi'an as the research object, the present study measures the contents of Cadmium (Cd), Lead (Pb), Copper (Cu), Nickel (Ni), and Chromium (Cr) in dust samples and further assesses the health risk of heavy metals intake through dust based on the assessment method of human exposure risk proposed by U.S. EPA, with an aim to investigate the content of heavy metal in the dust of leisure squares and its exposure risk. As the results indicate, the average contents of five heavy metals are obviously higher than the soil background value in Shaanxi Province. Therefore, Cd, Ni, Cu, Pb, and Cr are obviously enriched in urban surface dust in Shaanxi Province, due to the influence of human activities. In addition, it can also be found that the non-carcinogen exposure risk in children is significantly higher than that in adults with the risk values of these five heavy metals all one order of magnitude higher than those of adults. Irrespective of whether addressing the results for children or adults, the non-carcinogen exposure doses of five heavy metals are sorted as Cr > Pb > Cu > Ni > Cd. According to the present situation, for a child, the total non-carcinogenic risk values of five heavy metals have exceeded the safety limit in 11 of the 20 leisure squares in Yanta District of Xi'an. That means the leisure squares are no longer suitable for physical and recreational activities. For the five heavy metals, the average non-carcinogenic risk value of Cr is largest, and causes the largest threat to health in Yanta District, Xi'an. The carcinogenic exposure doses of the heavy metals Cr, Cd, and Ni are very low in respiratory pathways and there is no carcinogenic health risk. In general, the Cr content in dust in domestic cities is higher than that of foreign cities; however, the Pb content is much lower.

  5. Content of Heavy Metal in the Dust of Leisure Squares and Its Health Risk Assessment—A Case Study of Yanta District in Xi’an

    Directory of Open Access Journals (Sweden)

    Tianjie Shao

    2018-02-01

    Full Text Available Taking Yanta District in Xi’an as the research object, the present study measures the contents of Cadmium (Cd, Lead (Pb, Copper (Cu, Nickel (Ni, and Chromium (Cr in dust samples and further assesses the health risk of heavy metals intake through dust based on the assessment method of human exposure risk proposed by U.S. EPA, with an aim to investigate the content of heavy metal in the dust of leisure squares and its exposure risk. As the results indicate, the average contents of five heavy metals are obviously higher than the soil background value in Shaanxi Province. Therefore, Cd, Ni, Cu, Pb, and Cr are obviously enriched in urban surface dust in Shaanxi Province, due to the influence of human activities. In addition, it can also be found that the non-carcinogen exposure risk in children is significantly higher than that in adults with the risk values of these five heavy metals all one order of magnitude higher than those of adults. Irrespective of whether addressing the results for children or adults, the non-carcinogen exposure doses of five heavy metals are sorted as Cr > Pb > Cu > Ni > Cd. According to the present situation, for a child, the total non-carcinogenic risk values of five heavy metals have exceeded the safety limit in 11 of the 20 leisure squares in Yanta District of Xi’an. That means the leisure squares are no longer suitable for physical and recreational activities. For the five heavy metals, the average non-carcinogenic risk value of Cr is largest, and causes the largest threat to health in Yanta District, Xi’an. The carcinogenic exposure doses of the heavy metals Cr, Cd, and Ni are very low in respiratory pathways and there is no carcinogenic health risk. In general, the Cr content in dust in domestic cities is higher than that of foreign cities; however, the Pb content is much lower.

  6. Content of Heavy Metal in the Dust of Leisure Squares and Its Health Risk Assessment—A Case Study of Yanta District in Xi’an

    Science.gov (United States)

    Shao, Tianjie; Pan, Lihuan; Chen, Zhiqing; Wang, Ruiyuan; Li, Wenjing; Qin, Qing; He, Yuran

    2018-01-01

    Taking Yanta District in Xi’an as the research object, the present study measures the contents of Cadmium (Cd), Lead (Pb), Copper (Cu), Nickel (Ni), and Chromium (Cr) in dust samples and further assesses the health risk of heavy metals intake through dust based on the assessment method of human exposure risk proposed by U.S. EPA, with an aim to investigate the content of heavy metal in the dust of leisure squares and its exposure risk. As the results indicate, the average contents of five heavy metals are obviously higher than the soil background value in Shaanxi Province. Therefore, Cd, Ni, Cu, Pb, and Cr are obviously enriched in urban surface dust in Shaanxi Province, due to the influence of human activities. In addition, it can also be found that the non-carcinogen exposure risk in children is significantly higher than that in adults with the risk values of these five heavy metals all one order of magnitude higher than those of adults. Irrespective of whether addressing the results for children or adults, the non-carcinogen exposure doses of five heavy metals are sorted as Cr > Pb > Cu > Ni > Cd. According to the present situation, for a child, the total non-carcinogenic risk values of five heavy metals have exceeded the safety limit in 11 of the 20 leisure squares in Yanta District of Xi’an. That means the leisure squares are no longer suitable for physical and recreational activities. For the five heavy metals, the average non-carcinogenic risk value of Cr is largest, and causes the largest threat to health in Yanta District, Xi’an. The carcinogenic exposure doses of the heavy metals Cr, Cd, and Ni are very low in respiratory pathways and there is no carcinogenic health risk. In general, the Cr content in dust in domestic cities is higher than that of foreign cities; however, the Pb content is much lower. PMID:29495319

  7. Kinetics of Cr(III) and Cr(VI) removal from water by two floating macrophytes.

    Science.gov (United States)

    Maine, M A; Hadad, H R; Sánchez, G; Caffaratti, S; Pedro, M C

    2016-01-01

    The aim of this work was to compare Cr(III) and Cr(VI) removal kinetics from water by Pistia stratiotes and Salvinia herzogii. The accumulation in plant tissues and the effects of both Cr forms on plant growth were also evaluated. Plants were exposed to 2 and 6 mg L(-1) of Cr(III) or Cr(VI) during 30 days. At the end of the experiment, Cr(VI) removal percentages were significantly lower than those obtained for Cr(III) for both macrophytes. Cr(III) removal kinetics involved a fast and a slow component. The fast component was primarily responsible for Cr(III) removal while Cr(VI) removal kinetics involved only a slow process. Cr accumulated principally in the roots. In the Cr(VI) treatments a higher translocation from roots to aerial parts than in Cr(III) treatments was observed. Both macrophytes demonstrated a high ability to remove Cr(III) but not Cr(VI). Cr(III) inhibited the growth at the highest studied concentration of both macrophytes while Cr(VI) caused senescence. These results have important implications in the use of constructed wetlands for secondary industrial wastewater treatment. Common primary treatments of effluents containing Cr(VI) consists in its reduction to Cr(III). Cr(III) concentrations in these effluents are normally below the highest studied concentrations in this work.

  8. Metabolic Effects of CX3CR1 Deficiency in Diet-Induced Obese Mice.

    Directory of Open Access Journals (Sweden)

    Rachana Shah

    Full Text Available The fractalkine (CX3CL1-CX3CR1 chemokine system is associated with obesity-related inflammation and type 2 diabetes, but data on effects of Cx3cr1 deficiency on metabolic pathways is contradictory. We examined male C57BL/6 Cx3cr1-/- mice on chow and high-fat diet to determine the metabolic effects of Cx3cr1 deficiency. We found no difference in body weight and fat content or feeding and energy expenditure between Cx3cr1-/- and WT mice. Cx3cr1-/- mice had reduced glucose intolerance assessed by intraperitoneal glucose tolerance tests at chow and high-fat fed states, though there was no difference in glucose-stimulated insulin values. Cx3cr1-/- mice also had improved insulin sensitivity at hyperinsulinemic-euglycemic clamp, with higher glucose infusion rate, rate of disposal, and hepatic glucose production suppression compared to WT mice. Enhanced insulin signaling in response to acute intravenous insulin injection was demonstrated in Cx3cr1-/- by increased liver protein levels of phosphorylated AKT and GSK3β proteins. There were no differences in adipose tissue macrophage populations, circulating inflammatory monocytes, adipokines, lipids, or inflammatory markers. In conclusion, we demonstrate a moderate and reproducible protective effect of Cx3cr1 deficiency on glucose intolerance and insulin resistance.

  9. Microstructure and phase evolution in laser clad chromium carbide-NiCrMoNb

    International Nuclear Information System (INIS)

    Venkatesh, L.; Samajdar, I.; Tak, Manish; Doherty, Roger D.; Gundakaram, Ravi C.; Prasad, K. Satya; Joshi, S.V.

    2015-01-01

    Highlights: • Microstructural development during laser cladding has been studied. • In this multi component system Cr 7 C 3 is found to be the stable carbide phase. • Phases were identified by EBSD since XRD results were not conclusive. • Increase in laser power and/or scanning speed reduced the carbide content. • Hardness seems to depend on phase content as well as microstructure. - Abstract: Microstructural development in laser clad layers of Chromium carbide (Cr x C y )-NiCrMoNb on SA 516 steel has been investigated. Although the starting powder contained both Cr 3 C 2 and Cr 7 C 3 , the clad layers showed only the presence of Cr 7 C 3 . Microtexture measurements by electron back scattered diffraction (EBSD) revealed primary dendritic Cr 7 C 3 with Ni rich FCC metallic phase being present in the interdendritic spaces. Further annealing of the laser clad layers and furnace melting of the starting powder confirmed that Cr 7 C 3 is the primary as well as stable carbide phase in this multi component system. Increase in laser power and scanning speed progressively reduced carbide content in the laser clad layers. Increased scanning speed, which enhances the cooling rate, also led to reduction in the secondary arm spacing (λ 2 ) of the Cr 7 C 3 dendrites. The clad layer hardness increased with carbide content and with decreased dendrite arm spacing.

  10. Effect of Al content on structure and mechanical properties of the Al{sub x}CrNbTiVZr (x = 0; 0.25; 0.5; 1) high-entropy alloys

    Energy Technology Data Exchange (ETDEWEB)

    Yurchenko, N.Yu. [Laboratory of Bulk Nanostructured Materials, Belgorod State University, Belgorod 308015 (Russian Federation); Stepanov, N.D., E-mail: stepanov@bsu.edu.ru [Laboratory of Bulk Nanostructured Materials, Belgorod State University, Belgorod 308015 (Russian Federation); Shaysultanov, D.G. [Laboratory of Bulk Nanostructured Materials, Belgorod State University, Belgorod 308015 (Russian Federation); Tikhonovsky, M.A. [National Science Center “Kharkov Institute of Physics and Technology”, NAS of Ukraine, Kharkov, 61108 (Ukraine); Salishchev, G.A. [Laboratory of Bulk Nanostructured Materials, Belgorod State University, Belgorod 308015 (Russian Federation)

    2016-11-15

    In present study, structure and mechanical properties of the Al{sub x}CrNbTiVZr (x = 0; 0.25; 0.5; 1) high-entropy alloys after arc melting and annealing at 1200 °C for 24 h are investigated. The CrNbTiVZr alloy is composed of body centered cubic (bcc) and C15 (face centered cubic) Laves phases while the Al{sub x}CrNbTiVZr (x = 0.25; 0.5; 1) alloys consist of bcc and two C14 (hexagonal close packed) Laves phases with different chemical compositions. Thermodynamic modeling predicts existence of two phases – bcc and C15 Laves phase and broadening of single bcc phase field due to Al addition. The density of the alloys decreases with the increase of Al content. The alloys are found to be extremely brittle at room temperature and 600 °C. The alloys have high strength at temperatures of 800–1000 °C. For example, yield strength at 800 °C increases from 440 MPa for the CrNbTiVZr alloy to 1250 MPa for the AlCrNbTiVZr alloy. The experimental phase composition of the Al{sub x}CrNbTiVZr alloys is compared with predicted equilibrium phases and the factors governing the transformation of C15 to C14 Laves phases due to Al addition to the CrNbTiVZr alloy analyzed. Specific properties of the alloys are compared with other high-entropy alloys and commercial Ni-based superalloys. - Highlights: •Al{sub x}CrNbTiVZr (x = 0; 0.25; 0.5; 1) alloys are arc melted and annealed at 1200 °C. •The CrNbTiVZr alloy has bcc and C15 Laves phases. •The Al-containing alloys are composed of bcc and two C14 Laves phases. •The alloys demonstrate high specific strength at temperatures of 800 °C and 1000 °C. •The strength of the alloys increases in proportion with increase of Al content.

  11. Effect of Ti content on structure and properties of Al2CrFeNiCoCuTix high-entropy alloy coatings

    International Nuclear Information System (INIS)

    Qiu, X.W.; Zhang, Y.P.; Liu, C.G.

    2014-01-01

    Highlights: • Al 2 CrFeNiCoCuTi x high-entropy alloy coatings were prepared by laser cladding. • Al 2 CrFeNiCoCuTi x coatings show excellent corrosion resistance and wear resistance. • Al 2 CrFeNiCoCuTi x coatings play a good protective effect on Q235 steel. • Ti element promotes the formation of a BCC structure in a certain extent. -- Abstract: The Al 2 CrFeNiCoCuTi x high-entropy alloy coatings were prepared by laser cladding. The structure, hardness, corrosion resistance, wear resistance and magnetic property were studied by metallurgical microscope, scanning electron microscopy with spectroscopy (SEM/EDS), X-ray diffraction, micro/Vickers hardness tester, electrochemical workstation tribometer and multi-physical tester. The result shows that, Al 2 CrFeNiCoCuTi x high-entropy alloy samples consist of the cladding zone, bounding zone, heat affected zone and substrate zone. The bonding between the cladding layer and the substrate of a good combination; the cladding zone is composed mainly of equiaxed grains and columnar crystal; the phase structure of Al 2 CrFeNiCoCuTi x high-entropy alloy coatings simple for FCC, BCC and Laves phase due to high-entropy affect. Ti element promotes the formation of a BCC structure in a certain extent. Compared with Q235 steel, the free-corrosion current density of Al 2 CrFeNiCoCuTi x high-entropy alloy coatings is reduced by 1–2 orders of magnitude, the free-corrosion potential is more “positive”. With the increasing of Ti content, the corrosion resistance of Al 2 CrFeCoCuNiTi x high-entropy alloy coatings enhanced in 0.5 mol/L HNO 3 solution. Compared with Q235 steel, the relative wear resistance of Al 2 CrFeCoCuNiTi x high-entropy alloy coatings has improved greatly; both the hardness and plasticity are affecting wear resistance. Magnetization loop shows that, Ti 0.0 high-entropy alloy is a kind of soft magnetic materials

  12. Bioaccumulation of Copper (Cu) and Chromium (Cr) on export comodity vanamei shrimp from Karawang, West Java

    Science.gov (United States)

    Rahman, A.; Takarina, N. D.; Siswantining, T.; Pin, T. G.; Soedjiarti, T.

    2018-05-01

    Karawang is one of regencies in West Java which has great potential for vannamei culture. The farm here was modern farm and using Citarum River as water source. Human activities like household and industry around the river cause its quality decrease and give negative impact to shrimp farm. This research was aimed to investigate the bioaccumulation of copper (Cu) and chromium (Cr) on vannamei shrimp from Karawang, West Java. Amount of shrimp’s meat and carapace were used for heavy metal measurement using Atomic Absorption Specthrophotometry. Result showed that contents of copper both in meat and carapace were higher than content of chromium. Moreover, the content of both metals was higher on carapace compared to meat. Since the content of meat were below threshold, so it is safe for consumption. There is no significant difference content of both metals in carapace.

  13. Substrate bias effects on composition and coercivity of CoCrTa/Cr thin films on canasite and glass

    Science.gov (United States)

    Deng, Y.; Lambeth, D. N.; Sui, X.; Lee, L.-L.; Laughlin, D. E.

    1993-05-01

    CoCrTa/Cr thin films were prepared by rf diode sputtering onto canasite and glass substrates at various bias voltages from two targets of different compositions (Co82.8Cr14.6Ta2.6 and Co86Cr12Ta2). While Auger depth profile analysis indicates that there is some broadening at the CoCrTa-Cr interface, x-ray fluorescence spectroscopy reveals that changes in alloy composition due to the resputtering processes are even more prominent. For both targets, as the substrate bias increases the Co content in the films declines, and the magnetization decreases. The maximum film coercivity appears to correlate to the final film composition. By investigating the results from both targets, it is concluded that the coercivity reaches a maximum when the film composition is in the neighborhood of Co84Cr13Ta3. Thus, to optimize the coercivity different bias voltages are required for each target. Excessive substrate bias, however, leads to films with low magnetization and coercivity.

  14. Fabrication of V-Cr-Ti-Y-Al-Si alloys by levitation melting

    Energy Technology Data Exchange (ETDEWEB)

    Chuto, Toshinori; Satou, Manabu; Abe, Katsunori [Department of Quantum Science and Energy Engineering, Tohoku University, Sendai, Miyagi (Japan); Nagasaka, Takuya; Muroga, Takeo [National Inst. for Fusion Science, Toki, Gifu (Japan); Shibayama, Tamaki [Center for Advanced Research of Energy Technology, Hokkaido University, Sapporo, Hokkaido (Japan); Tomiyama, Shigeki [Daido Bunseki Research Inc., Nagoya, Aichi (Japan); Sakata, Masafumi [Daido Steel Co. Ltd., Nagoya (Japan)

    2000-09-01

    Three allows of V-4Cr-4Ti type containing Si, Al and Y were fabricated by 2.5 kg scale levitation melting in this study. Workability and recrystallization behavior of the alloys were studied in order to establish the fabrication method of high-purity large ingot of V-Cr-Ti-Si-Al-Y type alloys, especially reducing interstitial impurity levels. Oxygen contents decreased with increasing yttrium contents and were kept below 180 mass ppm over wide region in the ingots. Nitrogen contents in the V-Cr-Ti-Y-Si-Al type alloys were only 100 mass ppm, which were as low as that in the starting materials. Only the V-4Cr-4Ti-0.1Y, Si, Al alloy could be cold-rolled at as-melted condition. Because large yttrium inclusions were observed in the alloys containing 0.5 mass%Y, it is necessary to optimize yttrium contents to avoid large inclusions and to obtain good workability. (author)

  15. Fabrication of V-Cr-Ti-Y-Al-Si alloys by levitation melting

    International Nuclear Information System (INIS)

    Chuto, Toshinori; Satou, Manabu; Abe, Katsunori; Nagasaka, Takuya; Muroga, Takeo; Shibayama, Tamaki; Tomiyama, Shigeki; Sakata, Masafumi

    2000-01-01

    Three allows of V-4Cr-4Ti type containing Si, Al and Y were fabricated by 2.5 kg scale levitation melting in this study. Workability and recrystallization behavior of the alloys were studied in order to establish the fabrication method of high-purity large ingot of V-Cr-Ti-Si-Al-Y type alloys, especially reducing interstitial impurity levels. Oxygen contents decreased with increasing yttrium contents and were kept below 180 mass ppm over wide region in the ingots. Nitrogen contents in the V-Cr-Ti-Y-Si-Al type alloys were only 100 mass ppm, which were as low as that in the starting materials. Only the V-4Cr-4Ti-0.1Y, Si, Al alloy could be cold-rolled at as-melted condition. Because large yttrium inclusions were observed in the alloys containing 0.5 mass%Y, it is necessary to optimize yttrium contents to avoid large inclusions and to obtain good workability. (author)

  16. Structural and Giant Magneto-impedance properties of Cr-incorporated Co-Fe-Si-B amorphous microwires

    Energy Technology Data Exchange (ETDEWEB)

    Sarkar, Partha [NDE and Magnetic Materials Group, CSIR-National Metallurgical Laboratory, Jamshedpur 831007 (India); Basu Mallick, A. [Department of Metallurgy and Materials Engineering, Bengal Engineering and Science University, Shibpur, Howrah 711103 (India); Roy, R.K. [NDE and Magnetic Materials Group, CSIR-National Metallurgical Laboratory, Jamshedpur 831007 (India); Panda, A.K., E-mail: akpanda@nmlindia.org [NDE and Magnetic Materials Group, CSIR-National Metallurgical Laboratory, Jamshedpur 831007 (India); Mitra, A. [NDE and Magnetic Materials Group, CSIR-National Metallurgical Laboratory, Jamshedpur 831007 (India)

    2012-04-15

    The investigation is focused on the effect of Cr incorporation for Co/Fe in (Co{sub 0.5}Fe{sub 0.5}){sub 78-x}Cr{sub x}Si{sub 8}B{sub 14} (x=0-12) amorphous microwires of 110 {mu}m diameter prepared by in-water quenching technique. The rise in crystallization onset T{sub X1} with Cr addition revealed the elemental contribution against devitrification and a consequent thermal stability. Cr is unfavorable towards ferromagnetic ordering leading to a linear drop in Curie temperature T{sub ca} with its rise in concentration. The presence of low Cr content upto Cr-4 at.% has been effective in drastically improving the Giant magneto-impedance (GMI) property. Cr content in the range of 4{<=}X{<=}10 has low magnetostriction and maximum field sensitivity in the as-quenched state. The GMI properties are further improved after annealing treatment. High content of Cr>10 is found to be deleterious towards GMI behavior and its consequent application as sensor material. - Highlights: Black-Right-Pointing-Pointer Cr incorporation in CoFeSiB alloy enhanced thermal stability against devitrification. Black-Right-Pointing-Pointer Optimal Cr content induced low magnetostriction in the rapidly quenched microwires. Black-Right-Pointing-Pointer High GMI ratio and field sensitivity was obtained with optimum Cr in the microwires. Black-Right-Pointing-Pointer Annealing treatment at 725 K for 15 min improved the GMI response of microwires.

  17. Microstructure and phase evolution in laser clad chromium carbide-NiCrMoNb

    Energy Technology Data Exchange (ETDEWEB)

    Venkatesh, L., E-mail: venkatesh@arci.res.in [International Advanced Research Centre for Powder Metallurgy and New Materials (ARCI), Balapur, Hyderabad 500005 (India); Department of Metallurgical Engineering & Materials Science, IIT Bombay, Powai, Mumbai 400076 (India); Samajdar, I. [Department of Metallurgical Engineering & Materials Science, IIT Bombay, Powai, Mumbai 400076 (India); Tak, Manish [International Advanced Research Centre for Powder Metallurgy and New Materials (ARCI), Balapur, Hyderabad 500005 (India); Doherty, Roger D. [Department of Materials Engineering, Drexel University, Philadelphia, PA 19104 (United States); Gundakaram, Ravi C.; Prasad, K. Satya; Joshi, S.V. [International Advanced Research Centre for Powder Metallurgy and New Materials (ARCI), Balapur, Hyderabad 500005 (India)

    2015-12-01

    Highlights: • Microstructural development during laser cladding has been studied. • In this multi component system Cr{sub 7}C{sub 3} is found to be the stable carbide phase. • Phases were identified by EBSD since XRD results were not conclusive. • Increase in laser power and/or scanning speed reduced the carbide content. • Hardness seems to depend on phase content as well as microstructure. - Abstract: Microstructural development in laser clad layers of Chromium carbide (Cr{sub x}C{sub y})-NiCrMoNb on SA 516 steel has been investigated. Although the starting powder contained both Cr{sub 3}C{sub 2} and Cr{sub 7}C{sub 3}, the clad layers showed only the presence of Cr{sub 7}C{sub 3}. Microtexture measurements by electron back scattered diffraction (EBSD) revealed primary dendritic Cr{sub 7}C{sub 3} with Ni rich FCC metallic phase being present in the interdendritic spaces. Further annealing of the laser clad layers and furnace melting of the starting powder confirmed that Cr{sub 7}C{sub 3} is the primary as well as stable carbide phase in this multi component system. Increase in laser power and scanning speed progressively reduced carbide content in the laser clad layers. Increased scanning speed, which enhances the cooling rate, also led to reduction in the secondary arm spacing (λ{sub 2}) of the Cr{sub 7}C{sub 3} dendrites. The clad layer hardness increased with carbide content and with decreased dendrite arm spacing.

  18. Stress corrosion cracking of stainless steels under deaerated high-temperature water. Influence of grain boundary carbide precipitation, and effect of Mo and Cr in alloys

    International Nuclear Information System (INIS)

    Yamada, Takuyo; Terachi, Takumi; Miyamoto, Tomoki; Arioka, Koji

    2007-01-01

    In order to evaluate the influence of grain boundary carbide on IGSCC susceptibility of stainless steel, crack growth rate tests were performed under deaerated or 0.3 ppm hydrogenated pure water environments at 320degC using half-inch compact tension (CT) specimens. In our previous report, CT testing showed that the susceptibility of CW316 to IGSCC was inhibited by the precipitation of grain boundary carbide under these environments. The result suggested quite different behavior from that in an oxygenated high-temperature water environment. In this study, the influence of (1) Mo and (2) Cr content in alloys, and (3) Cr depletion at the grain boundary on the IGSCC growth behavior in stainless steel was studied at 320degC under a 0.3-ppm hydrogenated pure-water environment. As a result, (1) IGSCC growth was observed on non-sensitized CW20%316, CW20%304, CW20%20Cr316, and CW20%20Cr304 under a 0.3-ppm hydrogenated pure-water environment at 320degC. (2) IGSCC growth was not observed for sensitized CW20%316 and CW20%304 (at 650degC x 48 or 24 h) and healing heat-treated CW20%316 (at 650degC x 48 h + 900degC x 0.5 h) under the same water environment. (3) The susceptibility of high Cr content materials (CW20%20Cr316 and CW20% 20Cr304) to IGSCC resistance was improved that of conventional CW316 and CW304 under the same water environment. The higher Cr content is effective in inhibiting susceptibility to IGSCC, but the inhibiting effect of Cr content is smaller than the effect of the grain boundary carbide. (4) These differences in IGSCC suggest that grain boundary carbide has a beneficial effect in improving IGSCC resistance, at least in a 0.3-ppm hydrogenated pure-water environment, despite the Mo content and Cr depletion at grain boundary. (author)

  19. Impact behavior of 9-Cr and 12-Cr ferritic steels after low-temperature irradiation

    International Nuclear Information System (INIS)

    Klueh, R.L.; Vitek, J.M.; Corwin, W.R.; Alexander, D.J.

    1987-01-01

    Miniature Charpy impact specimens of 9Cr-1MoVNb and 12Cr-1MoVW steels and these steels with 1 and 2% Ni were irradiated in the High-Flux Isotope Reactor (HFIR) at 50 0 C to displacement damage levels of up to 9 dpa. Nickel was added to study the effect of transmutation helium. Irradiation caused an increase in the ductile-brittle transition temperature (DBTT). The 9Cr-1MoVNb steels, with and without nickel, showed a larger shift than the 12Cr-1MoVW steels, with and without nickel. The results indicated that helium also increased the DBTT. The same steels were previously irradiated at higher temperatures. From the present and past tests, the effect of irradiation temperature on the DBTT behavior can be evaluated. For the 9Cr-1MoVNb steel, there is a continuous decrease in the magnitude of the DBTT increase up to an irradiation temperature of about 400 0 C, after which the shift drops rapidly to zero at about 450 0 C. The DBTT of the 12Cr-1MoVW steel shows a maximum increase at an irradiation temperature of about 400 0 C and less of an increase at either higher or lower irradiation temperatures

  20. Influence of manganese, carbon and nitrogen on high-temperature strength of Fe-Cr-Mn austenitic alloys

    International Nuclear Information System (INIS)

    Hosoi, Y.; Okazaki, Y.; Wade, N.; Miyahara, K.

    1990-01-01

    High Mn-Cr-Fe base alloys are candidates for the first wall material of fusion reactors because of rapid decay of radioactivity of the alloys after neutron irradiation compared with that of Ni-Cr-Fe base alloys. Their high temperature properties, however, are not clearly understood at present. In this paper, a study has been made of the effects of Mn, C and N content on the high-temperature tensile strength and creep properties of a 12% CR-Fe base alloy. Mn tends to decrease tensile strength and proof stress at intermediate temperatures. At higher temperatures in the austenite range, however, tensile properties scarcely depend on Mn content. C and N additions improve the tensile properties markedly. The combined addition of 0.2%C and 0.2%N to a 12%Cr-15%Mn-Fe base alloy makes the strength at 873K as high as that of a modified type 316 stainless steel. Combined alloying with C and N also improves the creep strength. Cold working is very useful in increasing the creep strength because of the finely dispersed precipitates in the matrix during creep. From these results, Fe-12%Cr-15%Mn-15%Mn-0.2%c-0.2%N is recommended as one of the most suitable alloys in this system for high temperature usage. (author)

  1. Cr 3d surface and bulk states in Sn1-xCrxTe/Cr crystals

    International Nuclear Information System (INIS)

    Guziewicz, E.; Szamota-Sadowska, K.; Kowalski, B.J.; Grodzicka, E.; Story, T.; Orlowski, B.A.; Johnson, R.L.

    1997-01-01

    We report a new approach to investigate metal-semiconductor interface formation. Photoemission spectroscopy was applied in order to investigate the clean surface of a Sn 0.97 Cr 0.03 Te crystal and to observe its changes under sequential deposition of small amounts of Cr atoms. In order to analyse the Cr 3d contribution to the valence band, the Fano-type resonance tuned to the Cr 3p-3d transmission was used. The experiment was designed to follow the Sn 0.97 Cr 0.03 Te/Cr interface formation process. At the clean Sn 0.97 Cr 0.03 Te surface, the Cr 3d states contribution to the valence band was found to be positioned 0.8 eV below Fermi level. After the Cr deposition processes the contribution shifted to a higher binding energy and another contribution 5.8 eV below the Fermi level also observed. (author)

  2. Induction of mutants with higher protein content in soy bean

    International Nuclear Information System (INIS)

    Hiraiwa, S.; Tanaka, S.; Nakamura, S.

    1976-01-01

    Two experiments were carried out to examine the effects of ionizing radiation on protein content of soy beans and to estimate the potential value of ionizing radiation in soy bean breeding. In the first experiment seeds of three cultivars were acutely irradiated by gamma ray doses of 8 krad and 16 krad. Seeds of M 3 plants were analysed for protein content by the Biuret method. Selection within each variety was made to isolate plants having about 2% higher protein content than the control populations. In the second experiment growing plants of a soy bean cultivar were irradiated with 2.9 krad and 6.1 krad, from germination to maturation, in a 60 Co gamma field. Seeds on individual lines in M 5 , M 6 and M 7 plants were determined for their protein contents by the Kjeldahl method and the upper 10% of the treated lines were selected for progeny testing. From the results of the analysis of variance for each trait, significant differences were observed between the control variety and selected lines for all the traits. Six out of 19 lines showed significant increases in both 100 seed weight and protein content, and four lines promising. The mean protein content of selected lines increased 0.68% compared with the control variety. Genetic gain expected from selection for high protein content was therefore considered at about 1%; however, the likelihood of a large increase in protein content would greatly increase if large populations derived from irradiated seeds were observed

  3. LaCrO{sub 3}-dispersed Cr for metallic interconnect of planar SOFC

    Energy Technology Data Exchange (ETDEWEB)

    Song, Rak-Hyun; Shin, Dong Ryul [Korea Institute of Energy Research, Taejon (Korea, Republic of); Dokiya, Masayuki [National Institute of Materials and Chemical Research, Ibaraki (Japan)

    1996-12-31

    In the planar SOFC, the interconnect materials plays two roles as an electrical connection and as a gas separation plate in a cell stack. The interconnect materials must be chemically stable in reducing and oxidizing environments, and have high electronic conductivity, high thermal conductivity, matching thermal expansion with an electrolyte, high mechanical strength, good fabricability, and gas tightness. Lanthanum chromite so far has been mainly used as interconnect materials in planar SOFC. However, the ceramic materials are very weak in mechanical strength and have poor machining property as compared with metal. Also the metallic materials have high electronic conductivity and high thermal conductivity. Recently some researchers have studied metallic interconnects such as Al{sub 2}O{sub 3}/Inconel 600 cermet, Ni-20Cr coated with (LaSr)CoO{sub 3}, and Y{sub 2}O{sub 3-} or La{sub 2}O{sub 3}-dispersed Cr alloy. These alloys have still some problems because Ni-based alloys have high thermal expansion, the added Al{sub 2}O{sub 3}, Y{sub 2}O{sub 3} and La{sub 2}O{sub 3} to metals have no electronic conductivity, and the oxide formed on the surface of Cr alloy has high volatility. To solve these problems, in this study, LaCrO{sub 3}-dispersed Cr for metallic interconnect of planar SOFC was investigated. The LaCrO{sub 3}-dispersed Cr can be one candidate of metallic interconnect because LaCrO{sub 3} possesses electronic conductivity and Cr metal has relatively low thermal expansion. The content of 25 vol.% LaCrO{sub 3} Was selected on the basis of a theoretically calculated thermal expansion. The thermal expansion, electrical and oxidation properties were examined and the results were discussed as related to SOFC requirements.

  4. Cr(VI) removal from aqueous solution by dried activated sludge biomass

    International Nuclear Information System (INIS)

    Wu Jun; Zhang Hua; He Pinjing; Yao Qian; Shao Liming

    2010-01-01

    Batch experiments were conducted to remove Cr(VI) from aqueous solution using activated sludge biomass. The effects of acid pretreatment of the biomass, initial pH, biomass and Cr(VI) concentrations on Cr(VI) removal efficiency were investigated. Proton consumption during the removal process and the reducing capacity of sludge biomass were studied. The results show that acid pretreatment could significantly improve Cr(VI) removal efficiency and increase Cr(VI) reducing capacity by 20.4%. Cr(VI) removal was remarkably pH-dependent; lower pH (pH = 1, 2) facilitated Cr(VI) reduction while higher pH (pH = 3, 4) favored sorption of the converted Cr(III). Lower Cr(VI) concentration as well as higher biomass concentration could accelerate Cr(VI) removal. Cr(VI) reduction was not the only reason for proton consumption in the removal process. Pseudo-second-order adsorption kinetic model could successfully simulate Cr(VI) removal except under higher pH conditions (pH = 3, 4).

  5. In-BWR and out-of-pile nodular corrosion behavior of Zry-2/4 type melts with varying Fe, Cr, and Ni content and varying process history

    International Nuclear Information System (INIS)

    Ruhmann, H.; Manzel, R.; Sell, H.J.

    1996-01-01

    Zircaloy-based materials with constant tin content, a constant sum of Fe and Cr content, and different Fe/Cr ratios were manufactured from small ingots (6 kg) by forging, β-quenching, hot rolling, and cold rolling with two different annealing sequences resulting in two accumulated annealing parameters. To study the effect of Ni, chromium was substituted by nickel in one alloy. As a reference material standard, ASTM Zry-2 was manufactured in a similar way. These materials were examined for precipitate size by TEM and for their out-of-pile corrosion behavior in 400 C steam up to 319 days and in 500 C steam up to 24 h in a static and in a refreshed autoclave. Furthermore, samples made from these alloys were irradiated in a commercial BWR for two years. Results of the test are given

  6. Epithermal Neutron Activation Analysis (ENAA) of Cr(VI)-reducer Basalt-inhabiting Bacteria

    CERN Document Server

    Tsibakhashvili, N Ya; Kirkesali, E I; Aksenova, N G; Kalabegishvili, T L; Murusidze, I G; Mosulishvili, L M; Holman, H Y N

    2005-01-01

    Epithermal neutron activation analysis (ENAA) has been applied to studying elemental composition of Cr(VI)-reducer bacteria isolated from polluted basalts from the Republic of Georgia. Cr(VI)-reducing ability of the bacteria was examined by electron spin resonance (ESR) demonstrating that the bacteria differ in the rates of Cr(VI) reduction. A well-pronounced correlation between the ability of the bacteria to accumulate Cr(V) and their ability to reduce Cr(V) to Cr(III) observed in our experiments is discussed. Elemental analysis of these bacteria also revealed that basalt-inhabiting bacteria are distinguished by relative contents of essential elements such as K, Na, Mg, Fe, Mn, Zn, and Co. A high rate of Cr(III) formation correlates with a high concentration of Co in the bacterium. ENAA detected some similarity in the elemental composition of the bacteria. The relatively high contents of Fe detected in the bacteria (140-340 $\\mu $g/g of dry weight) indicate bacterial adaptation to the environmental condition...

  7. Effect of Fe Content on the Microstructure and Mechanical Properties of Ti-Al-Mo-V-Cr-Fe Alloys

    Directory of Open Access Journals (Sweden)

    Bae K.C.

    2017-06-01

    Full Text Available To investigate the effect of Fe content on the correlation between the microstructure and mechanical properties in near-b titanium alloys, the Ti-5Al-5Mo-5V-1Cr-xFe alloy system has been characterized in this study. As the Fe content increased, the number of nucleation sites and the volume fraction of the α phase decreased. We observed a significant difference in the shape and size of the α phase in the matrix before and after Fe addition. In addition, these morphological deformations were accompanied by a change in the shape of the α phase, which became increasingly discontinuous, and changed into globular-type α phase in the matrix. These phenomena affected the microstructure and mechanical properties of Ti alloys. Specimen #2 exhibited a high ultimate tensile strength (1071 MPa, which decreased with further addition of Fe.

  8. The charge transfer induced by Cr doping in MgB2

    International Nuclear Information System (INIS)

    Zhang Huarong; Zhao Jiyin; Shi Lei

    2005-01-01

    Mg 1-x Cr x B 2 polycrystal bulk samples with 0 x 5% have been synthesized by a solid-state reaction and studied by X-ray diffraction, SEM and Raman spectrum. It is found that the c-axis of the lattice decreases as the Cr content increases, while the a-axis remains unchanged. Moreover, crystal grain size increases apparently with Cr doping concentration increase. The normal-state resistivity increases and the superconducting transition temperature (T c ) decreases from 38.2 K (x = 0) to 35.1 K (x 0.03) with the increase of Cr content. It is suggested that the charge transfer between the Mg-layer and the B-layer causes the decrease of the charge carrier concentration and induces the changes of T c and normal-state resistivity. On the other hand, by the Raman scattering study, it is found that the linewidth of Raman spectrum increases with the increase of Cr content, which is resulted by the competition between the electron-phonon interaction and substitution-induced disorder. The Raman peak has no evident shift due to the countervailing between the effects of the electron-phonon coupling and the grain size

  9. Development of Cr3C2-25(Ni20Cr) nanostructured coatings

    International Nuclear Information System (INIS)

    Cunha, Cecilio Alvares da

    2012-01-01

    This study is divided in two parts. The first part is about the preparation of nanostructured Cr 3 C 2 -25(Ni20Cr) powders by high energy milling followed by characterization of the milled and the as received powder. Analyses of some of the data obtained were done using a theoretical approach. The second part of this study is about the preparation and characterization of coatings prepared with the nanostructured as well as the as received Cr 3 C 2 -25(Ni20Cr) powders. The high temperature erosion-oxidation (E-O) behavior of the coatings prepared with the two types of powders has been compared based on a technological approach. The average crystallite size of the Cr 3 C 2 -25(Ni20Cr) powder decreased rapidly from 145 nm to 50 nm in the initial stages of milling and thereafter decreased slowly to a steady state value of around 10 nm with further increase in milling time. This steady state corresponds to the beginning of a dynamic recovery process. The maximum lattice strain (ε = 1,17%) was observed in powders milled for 16 hours, and this powders critical crystallite size was 28 nm. In contrast, the lattice parameter attained a minimum for powders milled for 16 hours. Upon reaching the critical crystallite size, the dislocation density attained a steady state regime and all plastic deformation introduced in the material there after was in the form of events occurring at the grain boundaries, due mainly to grain boundary sliding. The deformation energy stored in the crystal lattice of the Cr 3 C 2 -25(Ni20Cr) powders milled for different times was determined from enthalpy variation measurements. These results indicated that the maximum enthalpy variation (δH = 722 mcal) also occurred for powders milled for 16 hours. In a similar manner, the maximum specific heat variation (δC p = 0,278 cal/gK) occurred for powders milled for 16 hours. The following mechanical properties of Cr 3 C 2 -25(Ni20Cr) coatings prepared using the HVOF thermal spray process were determined

  10. Thermal stability of nanocomposite CrC/a-C:H thin films

    International Nuclear Information System (INIS)

    Gassner, G.; Mayrhofer, P.H.; Patscheider, J.; Mitterer, C.

    2007-01-01

    The thermal stability of low-friction Me-C/a-C:H coatings is important for their potential applications in the tool and automotive industry. Recently we showed that CrC x /a-C:H coatings prepared by unbalanced magnetron sputtering of a Cr target in Ar + CH 4 glow discharges exhibit a nanocomposite structure where metastable fcc CrC nanocrystals are encapsulated by an a-C:H phase. Here, we present the structural evolution of these nanocomposite CrC/a-C:H coatings during annealing. High-temperature X-ray diffraction in vacuum and differential scanning calorimetry (DSC) combined with thermo-gravimetric analysis in Ar atmosphere indicate decomposition of the formed metastable fcc CrC phase and subsequent formation of Cr 3 C 2 and Cr 7 C 3 and structural transformation of the a-C:H matrix phase towards higher sp 2 bonding contents at temperatures above 450 deg. C. Combined DSC and mass spectrometer analysis as well as elemental profiling after annealing in vacuum by elastic recoil detection analysis relate this transformation to the loss of bonded hydrogen at temperatures above 200 deg. C. Due to these structural changes the coefficient of friction depends on the annealing temperature of the nanocomposite a-C:H coatings and shows a minimum of ∼ 0.13 for T = 200 deg. C. The more complex tribochemical reactions, influenced by the hydrogen loss from the coating during in-situ high temperatures ball-on disc tests, result in coefficient of friction values below 0.05 for T < 120 deg. C

  11. Chromium-induced accumulation of peroxide content, stimulation of ...

    African Journals Online (AJOL)

    Chromium (Cr)-induced oxidative damage and changes in contents of chlorophyll, protein, peroxide and malondialdehyde (MDA) and activities of enzymatic antioxidants were investigated in 4-day-old green gram (Vigna radiata L. cv. Wilczek) seedlings. Cr increased the contents of peroxide and MDA but decreased the ...

  12. Ostwald ripening of decomposed phases in Cu-Ni-Cr alloys

    International Nuclear Information System (INIS)

    Hernandez-Santiago, Felipe; Lopez-Hirata, Victor; Dorantes-Rosales, Hector J.; Saucedo-Munoz, Maribel L.; Gonzalez-Velazquez, Jorge L.; Paniagua-Mercado, Ana Ma.

    2008-01-01

    A study of the coarsening process of the decomposed phases was carried out in the Cu-34 wt.% Ni-4 wt.% Cr and Cu-45 wt.% Ni-10 wt.% Cr alloys using transmission electron microscopy. As aging progressed, the morphology of the coherent decomposed Ni-rich phase changed from cuboids to platelets aligned in the Cu-rich matrix directions. Prolonged aging caused the loss of coherency between the decomposed phases and the morphology of the Ni-rich phase changed to ellipsoidal. The variation of mean radius of the coherent decomposed phases with aging time followed the modified LSW theory for thermally activated growth in ternary alloy systems. The linear variation of the density number of precipitates and matrix supersaturation with aging time, also confirmed that the coarsening process followed the modified LSW theory in both alloys. The coarsening rate was faster in the symmetrical Cu-45 wt.% Ni-10 wt.% Cr alloy due to its higher volume fraction of precipitates. The activation energy for thermally activated growth was determined to be about 182 and 102 kJ mol -1 in the Cu-34 wt.% Ni-4 wt.% Cr and Cu-45 wt.% Ni-10 wt.% Cr alloys, respectively. The lower energy for the former alloy seems to be related to an increase in the atomic diffusion process as the chromium content increases. The size distributions of precipitates in the Cu-Ni-Cr alloys were broader and more symmetric than that predicted by the modified LSW theory for ternary alloys

  13. Chromium Fractions Changes Compared With Total-Cr As Determined by Neutron Activation Analysis Technique

    International Nuclear Information System (INIS)

    Abdel-Sabour, M.F.; Abdou, F.M.; Elwan, I.M.; Al-Salama, Y.J.

    2003-01-01

    Fifteen soil samples were chosen from different locations (five different locations at north greater Cairo, Egypt to represent different soils (alluvial and sandy) as well as different source of contaminated wastewater (sewage and industrial effluent). Using sequential extraction technique (extracting the soil with different solutions, which is designed to separate metal fractions), Cr was separated into six operationally defined fractions water soluble, exchangeable, carbonate bound, Fe-Mn oxides bound, organic bound and residual fractions. Result of soil total-Cr indicated the serious accumulation of Cr in soils subjected to prolonged irrigation with contaminated wastewater. As it could seen, total-Cr in the tested contaminated soils exceeds the permissible levels (75-100)ppm Cr by several order of magnitude particularly at the surface and subsurface layers. The highest accumulation of total Cr down to depth 60 cm was observed in case of soil E. Data showed that values of total Cr determined by NAA method were always higher than the relevant values determined either by AAS or those calculated after the sequential extraction method. T-test analysis showed the significant difference between NAA and either AAS or sequential extraction methods. Although T-test analysis showed that were significant differences between total content in soils as determined by destructive (AAS or SUM) and non-destructive (NAA) analytical techniques however, strong liner relation between NAA and other tested methods was obtained. Chromium distribution between different extractants shows that the greatest amounts are found in the residual and Occluded in Fe and Mn-Oxides fractions followed by carbonate or organic fractions. In most cases the proportion of all tested Cr-forms has increased in contaminated soil layers with higher enrichment in organically bound Cr, occluded in Fe and Mn oxides, carbonate exchangeable and soluble fractions. Results indicate that soil properties have a

  14. Magnetic and Moessbauer study of Mg{sub 0.9}Mn{sub 0.1}Cr{sub x}Fe{sub 2-x}O{sub 4} ferrites

    Energy Technology Data Exchange (ETDEWEB)

    Elzain, M., E-mail: elzain@squ.edu.om; Widatallah, H.; Gismelseed, A.; Bouziane, K.; Yousif, A.; Al Rawas, A.; Al-Omari, I.; Sellai, A. [Sultan Qaboos University, Department of Physics, College of Science (Oman)

    2006-02-15

    The ferrites Mg{sub 0.9}Mn{sub 0.1}Cr{sub x}Fe{sub 2-x}O{sub 4} (0x0.9) were prepared using the conventional double sintering method. The XRD showed that the samples maintain a single spinel cubic phase. The Moessbauer measurements were carried out at room and liquid nitrogen temperatures. From the area ratios of the A and B sites, it was found that the Fe cation population of the A and B sites decreases in proportion to Cr concentration. The contact hyperfine fields at the A and B sites were found to decrease with increasing Cr contents. This was found to be in approximate agreement with the results of magnetization measurement. The distributions of Mg and Mn cations versus Cr concentration were also determined using the Moessbauer and magnetization results. The Curie temperatures were determined and found to agree with the reported values. As the Cr contents increases the relative magnetization, was found to increase at low temperatures and decreases at higher temperatures.

  15. Higher milk fat content is associated with higher 25-hydroxyvitamin D concentration in early childhood.

    Science.gov (United States)

    Vanderhout, Shelley M; Birken, Catherine S; Parkin, Patricia C; Lebovic, Gerald; Chen, Yang; O'Connor, Deborah L; Maguire, Jonathon L

    2016-05-01

    Current guidelines for cow's milk consumption in children older than age 2 years suggest 1% or 2% milk to reduce the risk of obesity. Given that milk is the main dietary source of vitamin D for North American children and that vitamin D is fat soluble, we hypothesized 25-hydroxyvitamin D (25(OH)D) concentration to be positively associated with the fat content of milk. The objective was to determine the relationship between the fat content of milk consumed and the serum 25(OH)D concentration; our secondary objective was to explore the role that the volume of milk consumed played in this relationship. We completed a cross-sectional study of children aged 12-72 months in the TARGetKids! research network. Multivariable linear regression was used to test the association between milk fat content and child 25(OH)D, adjusted for clinically relevant covariates. The interaction between volume of milk and fat content was examined. Two thousand eight hundred fifty-seven children were included in the analysis. The fat content of milk was positively associated with 25(OH)D (p = 0.03), and the interaction between the volume of milk consumed and the milk fat content was statistically significant (p = 0.005). Children who drank 1% milk needed 2.46 cups (95% confidence interval (CI) 2.38-2.54) of milk to have a 25(OH)D concentration similar to that of children who drank 1 cup of homogenized milk (3.25% fat). Children who consumed 1% milk had 2.05 (95% CI 1.73-2.42) times higher odds of having a 25(OH)D concentration <50 nmol/L compared with children who consumed homogenized milk. In conclusion, recommendations for children to drink lower-fat milk (1% or 2%) may compromise serum 25(OH)D levels and may require study to ensure optimal childhood health.

  16. Correlation of microstructure and fracture toughness of advanced 9Cr/CrMoV dissimilarly welded joint

    Energy Technology Data Exchange (ETDEWEB)

    Guo, Qian [Shanghai Key Laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Lu, Fenggui, E-mail: Lfg119@sjtu.edu.cn [Shanghai Key Laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Liu, Xia [Shanghai Turbine Plant of Shanghai Electric Power Generation Equipment Co. Ltd., Shanghai 200240 (China); Yang, Renjie [Shanghai Turbine Works Company, Shanghai 200240 (China); Cui, Haichao [Shanghai Key Laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Gao, Yulai, E-mail: ylgao@shu.edu.cn [State Key Laboratory of Advanced Special Steels, Shanghai University, Shanghai 200072 (China)

    2015-06-25

    In this paper, the fracture toughness and the related microstructure characteristics of dissimilarly welded joint manufactured by advanced 9Cr and CrMoV steels were systematically investigated. The dissimilarly welded joint was fabricated by narrow gap submerged arc welding (NG-SAW) applying multi-layer and multi-pass technique. Fracture toughness, as one of the most important property to assess the reliability of welded joint, was studied for different regions including CrMoV base metal (CrMoV-BM), heat affected zone (HAZ) of CrMoV side (CrMoV-HAZ), weld metal (WM), heat affected zone of 9Cr side (9Cr-HAZ) and 9Cr base metal (9Cr-BM). It was found that the fracture toughness of CrMoV-BM, CrMoV-HAZ and WM was better than that of 9Cr-HAZ and 9Cr-BM. In order to illustrate these results, the microstructure of the whole welded joint was observed by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM) detailedly. It was found that the fine high-temperature tempered martensite and bainite in WM, CrMoV-BM and CrMoV-HAZ contribute to the higher fracture toughness, while lower fracture toughness for 9Cr-BM and HAZ was caused by coarse tempered lath-martensite. Furthermore, the fracture morphology showed that ductile fracture occurred in WM and CrMoV side, while brittle fracture appeared in BM and HAZ of 9Cr side.

  17. Photon emission produced by Kr+ ions bombardment of Cr and Cr2O3 targets

    International Nuclear Information System (INIS)

    Boujlaidi, A. El; Hammoum, K.; Jadoual, L.; Jourdani, R.; Ait El Fqih, M.; Aouchiche, H.; Kaddouri, A.

    2015-01-01

    The sputter induced photon spectroscopy technique was used to study the luminescence spectra of the species sputtered from chromium powder and its oxide Cr 2 O 3 , during 5 keV Kr + ions bombardment in vacuum better than 10 −7 torr. The optical spectra recorded between 350 and 470 nm exhibit discrete lines which are attributed to neutral excited atoms of chromium (Cr I lines). The experiments are also performed under 10 −5 torr ultra pure oxygen partial pressure. The results demonstrate that the measured intensities of the emitted photons are always higher in the presence of oxygen and even higher than those obtained for Cr 2 O 3 target. In the presence of oxygen vapor we assume that an oxide film is formed on the chromium surface which is responsible of the increase of photon emission. This variation in the intensities is correctly explained in the model of electron transfer processes between the excited sputtered atom and the bombarded surface. This model suggests that the structure formed on the Cr surface in the case of oxygenated chromium is closer to that of Cr 2 O 3 oxide

  18. Volatile-rich komatiitic and picritic melt inclusions in Cr-spinel beach sand from Gorgona Island, Colombia

    Science.gov (United States)

    Shimizu, K.; Shimizu, N.; Suzuki, K.; Tatsumi, Y.; Komiya, T.; Maruyama, S.

    2007-12-01

    Volatile content of komatiite is a key to constrain thermal evolution of the deep Earth. We report volatile contents with major and trace element compositions of melt inclusions (MIs) in chromian spinel (Cr-spinel) from beach sands of Gorgona Island, Colombia. Gorgona Island is ~90 Ma volcanic island, where picrites and the world-youngest komatiites occur. As Cr-spinel is dense and rigid oxide mineral that crystallizes only at early stages of crystallization, it is considered to be a superior container for retaining primitive melt, even including volatiles. Volatile (H2O, CO2, S, F and Cl) and trace element (K2O, Sr, Y, Zr, Nb, Ba, La, Ce, Sm, Dy, Yb) compositions of ~80 MIs were analyzed by SIMS (Cameca-1280 and 3f, respectively) at WHOI. MIs in the Cr-spinel from Gorgona Is. are classified into three types by their host Cr-spinel compositions such as low-Ti (P-type), high-Ti with high-Cr# (BK-type) and high-Ti with low-Cr# (K-type). MIs of P-type, BK-type and K-type are mostly in compositional ranges of picrite, high TiO2 komatiite (some basalt) and low TiO2 komatiite in Gorgona Island, respectively. Water content of P-type MIs is variable, ranging from 0.05 to 0.9 wt%, whereas those of BK and K-type MIs are limited (500 ppm) do not contain (shrinkage) bubbles and many of them are low in K2O. H2O/K2O, CO2/K2O, S/K2O and F/K2O ratios are positively correlated with Y/Sr ratios, indicating degassing trends of melt at crystallization, magma mixing and/or assimilation. Undegassed H2O/K2O, CO2/K2O, S/K2O and F/K2O ratios of komatiitic (picritic) melt are estimated to be ~10 (~40), ~80 (n.d.), ~7(~3) and ~1(~0.5), respectively, which are much higher than those estimated for the depleted source mantle of the MORB [1.6, 0.7, 1.6 and 0.2, respectively; Salters, V. & Stracke, A. (2004), Composition of the depleted mantle. Geochem. Geophys. Geosys. 5 (2003GC000597)]. The results suggest that Gorgona komatiite and picrite magmas were derived from volatile-rich sources. CO2

  19. A novel solid phase extraction procedure on Amberlite XAD-1180 for speciation of Cr(III), Cr(VI) and total chromium in environmental and pharmaceutical samples

    International Nuclear Information System (INIS)

    Narin, Ibrahim; Kars, Ayse; Soylak, Mustafa

    2008-01-01

    Due to the toxicity of chromium, species depend on their chemical properties and bioavailabilities, speciation of chromium is very important in environmental samples. A speciation procedure for chromium(III), chromium(VI) and total chromium in environmental samples is presented in this work, prior to flame atomic absorption spectrometric determination of chromium. The procedure is based on the adsorption of Cr(III)-diphenylcarbazone complex on Amberlite XAD-1180 resin. After oxidation of Cr(III), the developed solid phase extraction system was applied to determinate the total chromium. Cr(III) was calculated as the difference between the total Cr content and the Cr(VI) content. The analytical conditions for the quantitative recoveries of Cr(VI) on Amberlite XAD-1180 resin were investigated. The effects of some alkaline, earth alkaline, metal ions and also some anions were also examined. Preconcentration factor was found to be 75. The detection limits (LOD) based on three times sigma of the blank (N: 21) for Cr(VI) and total chromium were 7.7 and 8.6 μg/L, respectively. Satisfactory results for the analysis of total chromium in the stream sediment (GBW7310) certified reference material for the validation of the presented method was obtained. The procedure was applied to food, water and pharmaceutical samples successfully

  20. Synthesis of Higher Alcohols via Syngas on Cu/Zn/Si Catalysts. Effect of Polyethylene Glycol Content

    Science.gov (United States)

    Cui, Rong-Ji; Yan, Xing; Fan, Jin-Chuan; Huang, Wei

    2018-05-01

    Cu/Zn/Si catalysts with different polyethylene glycol (PEG) content were prepared by a complete liquid-phase method, and characterized by XRD, H2-TPR, N2-adsorption, and XPS. The influence of PEG content on the higher alcohols synthesis from syngas was investigated. The results showed that addition of PEG can influence the texture and surface properties of the catalysts, and therefore affect their activity and product distribution. With an increase in PEG content, BET surface area, Cu crystallite size and surface active ingredient content of the catalysts first increased and then decreased, the CO conversion had similar variation tendency. However, the pore volume and pore diameter of the catalyst increased, and the binding energy of the active component and the content of Cu2O decreased, which resulted in higher catalyst selectivity towards higher alcohols. The highest C2+OH selectivity in total alcohols was 60.6 wt %.

  1. Oxidation mechanism of Fe–16Cr alloy as SOFC interconnect in dry/wet air

    International Nuclear Information System (INIS)

    Chen, Zhi-Yuan; Wang, Li-Jun; Li, Fu-Shen; Chou, Kuo-Chih

    2013-01-01

    Highlights: •A special thermodynamic description corresponding to the kinetics was applied. •We reported the relationships of degradation time with temperature and moisture. •”Turning time” in the Fe–16Cr alloy oxidation kinetic model was given. •The oxidation mechanism of Fe–16Cr alloy in the wet air was discussed. -- Abstract: Experimental study on the oxidation corrosions of Fe–16Cr alloy was carried out at 800–1100 °C under dry/wet air conditions. Faster oxidation rate was observed at higher temperature and water vapor content. The degradation time t d between two stages in oxidation process showed an exponential relationship with elevating corrosion temperature in dry air, and a linear relationship with the water content in the case of water vapor introduced to the system. The mechanism of oxidation corrosions of Fe–16Cr alloy was suggested by the Real Physical Picture (RPP) model. It was found that the break-away oxidation in stage II was controlled by diffusion at initial both in dry and wet air, then became linear with the exposure time, which implied that the oxidation rate was then controlled by chemical reaction of the interface between the metal and the oxidized scale. Moreover, the effect of water in the oxidation process is not only to supply more oxygen into system, but also to modify the structures of oxide scale due to the existence of hydrogen atom, which results in the accelerated corrosions

  2. [Response of Nostoc flageliforme cell to Cu2+, Cr2+ and Pb2+ stress].

    Science.gov (United States)

    Guo, Jinying; Shi, Mingke; Zhao, Yanli; Ren, Guoyan; Yi, Junpeng; Niu, Leilei; Li, Juan

    2013-06-04

    This study aimed to investigate the effects of Cu2+, Cr2+ and Pb2+ stress on Nostoc flagelliforme cell. The response of Nostoc flagelliforme cell was analyzed under the stress. The modified BG11 culture medium containing different heavy metal ions of 0, 0.1, 1.0, 10, 100 mg/L was used to cultivate Nostoc flagelliforme cell at 25 degrees C and light intensity of 80 micromol/(m x s). Electrolyte leakage, the activities of superoxide dismutase, the content of malondialdehyde, proline, soluble protein and trehalose were analyzed. Under 1 - 100 mg/L Cu2+, Cr2+ and Pb2+ stress, electrolyte leakage and malondialdehyde contents in Nostoc flagelliforme cell were higher than those in the control group during heavy metal ions stress. Meanwhile, superoxide dismutase activity increased slightly under 10 mg/L, but was lower afterwards. The contents of proline, soluble protein and trehalose increased under 10 mg/L heavy metal ions stress, while declined under extreme heavy metal ions stress (100 mg/L). Nostoc flagelliforme cell has resistance to low heavy metal ions stress, but is damaged badly under extreme heavy metal ions stress.

  3. Using precipitated Cr on the surface of Cu-Cr alloy powders as catalyst synthesizing CNTs/Cu composite powders by water-assisted CVD

    Science.gov (United States)

    Zhou, Honglei; Liu, Ping; Chen, Xiaohong; Bi, Liming; Zhang, Ke; Liu, Xinkuan; Li, Wei; Ma, Fengcang

    2018-02-01

    Given that the conventional catalyst is easily soluble in the matrix to result in the poor performance of the CNTs/Cu composite materials, the Cr nano-particles precipitated on the surface of Cu-Cr particles are first used as catalysts to prepare the CNTs/Cu composite powders by means of water-assisted chemical vapor deposition in situ synthesis. The results show that the morphological difference of the precipitated Cr nano-particle is obvious with the change of solution and aging treatment, and the morphology, length and diameter of the synthetic CNTs are also different. The catalyst of Cr nano-particle has the best morphology and the synthesized CNTs had a good wettability with Cu particles when the Cu-Cr composite powders was solution-treated at 1023 K for 60 min and then was aged at 723 K for 120 min. The length, diameter, yield and purity of the synthesized CNTs can be also affected by the moisture content in the reaction gas. It is the most suitable for the growth of CNTs when the moisture content is 0.4%, and the high purity and defect-free CNTs with the smooth pipe wall, a diameter of 20 ˜ 30 nm and a length of up to 1800 nm can be obtained. The yield of CNTs with the moisture content of 0.4% reached to 138%, which was increased by 119% to compare with that without moisture. In this paper, a feasible technology was offered for the preparation of high performance CNTs/Cu composites.

  4. Microchemical effects in irradiated Fe–Cr alloys as revealed by atomistic simulation

    Energy Technology Data Exchange (ETDEWEB)

    Malerba, L., E-mail: lmalerba@sckcen.be [Structural Materials Modelling and Microstructure Unit, SMA/NMS, Studiecentrum voor Kernenergie, Centre d’Etudes de l’Energie Nucléaire (SCK-CEN), Boeretang 200, 2400 Mol (Belgium); Bonny, G.; Terentyev, D. [Structural Materials Modelling and Microstructure Unit, SMA/NMS, Studiecentrum voor Kernenergie, Centre d’Etudes de l’Energie Nucléaire (SCK-CEN), Boeretang 200, 2400 Mol (Belgium); Zhurkin, E.E. [Experimental Nuclear Physics Department, K-89, Faculty of Physics and Mechanics, Saint-Petersburg State Polytechnical University, 29 Polytekhnicheskaya Str., 195251 St. Petersburg (Russian Federation); Hou, M. [Physique des Solides Irradiés et des Nanostructures CP234, Faculté des Sciences, Université Libre de Bruxelles, Bd du Triomphe, B-1050 Bruxelles (Belgium); Vörtler, K.; Nordlund, K. [Association EURATOM-Tekes, Department of Physics, P.O. Box 43, FI-00014, University of Helsinki (Finland)

    2013-11-15

    Neutron irradiation produces evolving nanostructural defects in materials, that affect their macroscopic properties. Defect production and evolution is expected to be influenced by the chemical composition of the material. In turn, the accumulation of defects in the material results in microchemical changes, which may induce further changes in macroscopic properties. In this work we review the results of recent atomic-level simulations conducted in Fe–Cr alloys, as model materials for high-Cr ferritic–martensitic steels, to address the following questions: 1. Is the primary damage produced in displacement cascades influenced by the Cr content? If so, how? 2. Does Cr change the stability of radiation-produced defects? 3. Is the diffusivity of cascade-produced defects changed by Cr content? 4. How do Cr atoms redistribute under irradiation inside the material under the action of thermodynamic driving forces and radiation-defect fluxes? It is found that the presence of Cr does not influence the type of damage created by displacement cascades, as compared to pure Fe, while cascades do contribute to redistributing Cr, in the same direction as thermodynamic driving forces. The presence of Cr does change the stability of point-defects: the effect is weak in the case of vacancies, stronger in the case of self-interstitials. In the latter case, Cr increases the stability of self-interstitial clusters, especially those so small to be invisible to the electron microscope. Cr reduces also significantly the diffusivity of self-interstitials and their clusters, in a way that depends in a non-monotonic way on Cr content, as well as on cluster size and temperature; however, the effect is negligible on the mobility of self-interstitial clusters large enough to become visible dislocation loops. Finally, Cr-rich precipitate formation is favoured in the tensile region of edge dislocations, while it appears not to be influenced by screw dislocations; prismatic dislocation loops

  5. Development of Cr{sub 3}C{sub 2}-25(Ni20Cr) nanostructured coatings; Desenvolvimento de revestimentos nanostruturados de Cr{sub 3}C{sub 2}-25(Ni20Cr)

    Energy Technology Data Exchange (ETDEWEB)

    Cunha, Cecilio Alvares da

    2012-07-01

    This study is divided in two parts. The first part is about the preparation of nanostructured Cr{sub 3}C{sub 2}-25(Ni20Cr) powders by high energy milling followed by characterization of the milled and the as received powder. Analyses of some of the data obtained were done using a theoretical approach. The second part of this study is about the preparation and characterization of coatings prepared with the nanostructured as well as the as received Cr{sub 3}C{sub 2}-25(Ni20Cr) powders. The high temperature erosion-oxidation (E-O) behavior of the coatings prepared with the two types of powders has been compared based on a technological approach. The average crystallite size of the Cr{sub 3}C{sub 2}-25(Ni20Cr) powder decreased rapidly from 145 nm to 50 nm in the initial stages of milling and thereafter decreased slowly to a steady state value of around 10 nm with further increase in milling time. This steady state corresponds to the beginning of a dynamic recovery process. The maximum lattice strain ({epsilon} = 1,17%) was observed in powders milled for 16 hours, and this powders critical crystallite size was 28 nm. In contrast, the lattice parameter attained a minimum for powders milled for 16 hours. Upon reaching the critical crystallite size, the dislocation density attained a steady state regime and all plastic deformation introduced in the material there after was in the form of events occurring at the grain boundaries, due mainly to grain boundary sliding. The deformation energy stored in the crystal lattice of the Cr{sub 3}C{sub 2}-25(Ni20Cr) powders milled for different times was determined from enthalpy variation measurements. These results indicated that the maximum enthalpy variation ({delta}H = 722 mcal) also occurred for powders milled for 16 hours. In a similar manner, the maximum specific heat variation ({delta}C{sub p} = 0,278 cal/gK) occurred for powders milled for 16 hours. The following mechanical properties of Cr{sub 3}C{sub 2}-25(Ni20Cr) coatings

  6. Oxidation resistance of CrN/(Cr,V)N hard coatings deposited by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Panjan, P., E-mail: peter.panjan@ijs.si [Jožef Stefan Institute, Jamova 39, 1000 Ljubljana (Slovenia); Drnovšek, A.; Kovač, J.; Gselman, P. [Jožef Stefan Institute, Jamova 39, 1000 Ljubljana (Slovenia); Bončina, T. [University of Maribor, Faculty of Mechanical Engineering, Smetanova 17, 2000 Maribor (Slovenia); Paskvale, S.; Čekada, M.; Kek Merl, D.; Panjan, M. [Jožef Stefan Institute, Jamova 39, 1000 Ljubljana (Slovenia)

    2015-09-30

    In recent years vanadium-doped hard coatings have become available as possible candidates for self-lubrication at high temperatures. Their low coefficient of friction has mainly been attributed to the formation of the V{sub 2}O{sub 5} phase. However, the formation of vanadium oxides must be controlled by the out-diffusion of vanadium in order to achieve the combination of a low coefficient of friction and good mechanical properties for the protective coatings. In this work the application of a nanolayer of CrN/(Cr,V)N hard coating was proposed as a way to better control the out-diffusion of vanadium, while the topmost chromium oxide layer acts as barrier for the vanadium diffusion. However, the aim of this investigation was not only to focus on the formation of the oxide layer. Special attention was given to the oxidation process that takes place at the growth defects, where we observed a strong diffusion of vanadium taking place. The CrN/(Cr,V)N nanolayer coatings were deposited by DC unbalanced magnetron sputtering in an CC800/9 (CemeCon) industrial unit. The vanadium concentration in the (Cr,V)N layers was varied in the range 1.0–11.5 at.%. - Highlights: • Oxidation processes of CrN/(Cr,V)N nanolayers with vanadium content were investigated. • The CrN/(Cr,V)N hard layers were oxidized at high temperature in O2 atm. • The top chromium oxide layer acts as a diffusion barrier for vanadium ions during oxidation. • Important role of growth defects during the oxidation process is demonstrated.

  7. Oxidation resistance of CrN/(Cr,V)N hard coatings deposited by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Panjan, P.; Drnovšek, A.; Kovač, J.; Gselman, P.; Bončina, T.; Paskvale, S.; Čekada, M.; Kek Merl, D.; Panjan, M.

    2015-01-01

    In recent years vanadium-doped hard coatings have become available as possible candidates for self-lubrication at high temperatures. Their low coefficient of friction has mainly been attributed to the formation of the V_2O_5 phase. However, the formation of vanadium oxides must be controlled by the out-diffusion of vanadium in order to achieve the combination of a low coefficient of friction and good mechanical properties for the protective coatings. In this work the application of a nanolayer of CrN/(Cr,V)N hard coating was proposed as a way to better control the out-diffusion of vanadium, while the topmost chromium oxide layer acts as barrier for the vanadium diffusion. However, the aim of this investigation was not only to focus on the formation of the oxide layer. Special attention was given to the oxidation process that takes place at the growth defects, where we observed a strong diffusion of vanadium taking place. The CrN/(Cr,V)N nanolayer coatings were deposited by DC unbalanced magnetron sputtering in an CC800/9 (CemeCon) industrial unit. The vanadium concentration in the (Cr,V)N layers was varied in the range 1.0–11.5 at.%. - Highlights: • Oxidation processes of CrN/(Cr,V)N nanolayers with vanadium content were investigated. • The CrN/(Cr,V)N hard layers were oxidized at high temperature in O2 atm. • The top chromium oxide layer acts as a diffusion barrier for vanadium ions during oxidation. • Important role of growth defects during the oxidation process is demonstrated.

  8. Excellent corrosion resistance of 18Cr-20Ni-5Si steel in liquid Pb-Bi

    International Nuclear Information System (INIS)

    Kurata, Y.; Futakawa, M.

    2004-01-01

    The corrosion properties of three austenitic steels with different Si contents were studied under oxygen-saturated liquid Pb-Bi condition for 3000 h. The three austenitic steels did not exhibit appreciable dissolution of Ni and Cr at 450 deg. C. At 550 deg. C, the thick ferrite layer produced by dissolution of Ni and Cr was found in JPCA and 316SS with low Si contents while the protective oxide film composed of Si and O was formed on 18Cr-20Ni-5Si steel and prevented dissolution of Ni and Cr

  9. Contents of several elements in trees grown on the serpentine soil

    International Nuclear Information System (INIS)

    Tomita, Michio; Katayama, Yukio; Takada, Jitsuya; Nishimura, Kazuo.

    1990-01-01

    Determination of Mg-, Ca-, Cr-, Mn-, Fe- and Ni-content in akamatsu (P. densiflora), konara (Q. serrata) and ryoubu (C. barbinervis) which were grown on the serpentine soil, as well as in soil, were performed by the neutron activation method or the atomic absorption spectrophotometry. It turned out that contents of these elements was higher in leaves than wood. It was also found that Ni content in the leaves of konara as well as of ryoubu reflected the concentration of the acid extractable Ni in the serpentine soil. The elemental contents in akamatsu leaves were heavily affected by the characteristic contents of the serpentine soil. It is suggested that these trees are available for the indicator of soil-environment. (author)

  10. Structural, optical and magnetic properties of Cr doped SnO2 nanoparticles stabilized with polyethylene glycol

    International Nuclear Information System (INIS)

    Subramanyam, K.; Sreelekha, N.; Murali, G.; Reddy, D. Amaranatha; Vijayalakshmi, R.P.

    2014-01-01

    Pure and Cr (1, 3, 5 and 7 at%) doped SnO 2 nanoparticles were synthesized in aqueous solution by a simple chemical co-precipitation method using polyethylene glycol (PEG) as a stabilizing agent. The effect of Cr doping on the structural, optical and magnetic properties of SnO 2 nanoparticles was investigated. EDAX spectra confirmed the presence of Sn, O and Cr in near stoichiometry. XRD patterns revealed that particles of all samples were crystallized in single phase rutile type tetragonal crystal structure (P4 2 /mnm) of SnO 2 . The peak positions with Cr concentration shifted to higher 2θ values. Lattice parameters were also decreased with increasing Cr concentration. TEM studies indicated that the particle size is in the range of 8–10 nm. The optical absorption studies indicated that the absorption edge shifted towards lower wavelengths with inclusion of Cr content. FTIR spectrum displays various bands that are due to fundamental overtones of PEG and O–Sn–O entities. Further it revealed that the undoped and as well as Cr doped SnO 2 nanoparticles were capped by PEG. Magnetization measurements at room temperature revealed that all the doped samples were ferromagnetic in nature. Well defined strong room temperature ferromagnetic hysteresis loop was observed for 1% Cr doped SnO 2 nanoparticles

  11. Epithermal neutron activation analysis of CR(VI)-reducer basalt-inhabiting bacteria

    International Nuclear Information System (INIS)

    Tsibakhashvili, N.Ya.; Kalabegishvili, T.L.; Murusidze, I.G.; Mosulishvili, L.M.; Frontas'eva, M.V.; Kirkesali, E.I.; Aksenova, N.G.; Holman, H.Y.

    2005-01-01

    Epithermal neutron activation analysis (ENAA) has been applied to studying elemental composition of Cr(VI)-reducer bacteria isolated from polluted basalts from the Republic of Georgia. Cr(VI)-reducing ability of the bacteria was examined by electron spin resonance (ESR) demonstrating that the bacteria differ in the rates of Cr(VI) reduction. A well-pronounced correlation between the ability of the bacteria to accumulate Cr(VI) and their ability to reduce Cr(V) to Cr(III) observed in our experiments is discussed. Elemental analysis of these bacteria also revealed that basalt-inhabiting bacteria are distinguished by relative contents of essential elements such as K, Na, Mg, Fe, Mn, Zn, and Co. A high rate of Cr(III) formation correlates with a high concentration of Co in the bacterium. ENAA detected some similarity in the elemental composition of the bacteria. The relatively high contents of Fe detected in the bacteria (140-340 μg/g of dry weight) indicate bacterial adaptation to the environmental conditions typical of the basalts. The concentrations of at least 12-19 different elements ranging from major- to ultratrace ones were determined in each type of bacteria simultaneously. The range of concentrations spans over 8 orders of magnitude

  12. Behaviour of Z phase in 9–12%Cr steels

    DEFF Research Database (Denmark)

    Danielsen, Hilmar Kjartansson; Hald, John

    2006-01-01

    The literature on the behaviour of modified Z phase Cr(V,Nb)N in creep resistant martensitic 9–12%Cr steels is briefly reviewed. Ten different 9–12%Cr steels were investigated after prolonged exposure at 600–660uC; the modified Z phase was found in all of them. In steels with high Cr content (11......–12%), Z phase precipitates much faster than in 9%Cr steels. Precipitation of Z phase is associated with dissolution of MX carbonitrides, and causes a breakdown in long term creep strength in 9–12%Cr steels. High Cr steels show creep instabilities accompanied with Z phase precipitation, whereas low Cr...... steels show good long term creep stability. A niobium free CrVN variant of the modified Z phase was observed for the first time during the course of this work. The solution temperature of the Cr(V,Nb)N and CrVN modified Z phases was found to be close to 800uC for 11–12%Cr steels, much lower than the 1200...

  13. Microstructural Characterization of Clad Interface in Welds of Ni-Cr-Mo High Strength Low Alloy Steel

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Hong-Eun; Kim, Min-Chul; Lee, Ho-Jin; Kim, Keong-Ho [KAERI, Daejeon (Korea, Republic of); Lee, Ki-Hyoung [KAIST, Daejeon (Korea, Republic of); Lee, Chang-Hee [Hanyang Univ., Seoul (Korea, Republic of)

    2011-08-15

    SA508 Gr.4N Ni-Cr-Mo low alloy steel, in which Ni and Cr contents are higher than in commercial SA508 Gr.3 Mn-Mo-Ni low alloy steels, may be a candidate reactor pressure vessel (RPV) material with higher strength and toughness from its tempered martensitic microstructure. The inner surface of the RPV is weld-cladded with stainless steels to prevent corrosion. The goal of this study is to evaluate the microstructural properties of the clad interface between Ni-Cr-Mo low alloy steel and stainless weldment, and the effects of post weld heat treatment (PWHT) on the properties. The properties of the clad interface were compared with those of commercial Mn-Mo-Ni low alloy steel. Multi-layer welding of model alloys with ER308L and ER309L stainless steel by the SAW method was performed, and then PWHT was conducted at 610°C for 30 h. The microstructural changes of the clad interface were analyzed using OM, SEM and TEM, and micro-Vickers hardness tests were performed. Before PWHT, the heat affected zone (HAZ) showed higher hardness than base and weld metals due to formation of martensite after welding in both steels. In addition, the hardness of the HAZ in Ni-Cr-Mo low alloy steel was higher than that in Mn-Mo-Ni low alloy steel due to a comparatively high martensite fraction. The hardness of the HAZ decreased after PWHT in both steels, but the dark region was formed near the fusion line in which the hardness was locally high. In the case of Mn-Mo-Ni low alloy steel, formation of fine Cr-carbides in the weld region near the fusion line by diffusion of C from the base metal resulted in locally high hardness in the dark region. However, the precipitates of the region in the Ni-Cr-Mo low alloy steel were similar to that in the base metal, and the hardness in the region was not greatly different from that in the base metal.

  14. Microstructural Characterization of Clad Interface in Welds of Ni-Cr-Mo High Strength Low Alloy Steel

    International Nuclear Information System (INIS)

    Kim, Hong-Eun; Kim, Min-Chul; Lee, Ho-Jin; Kim, Keong-Ho; Lee, Ki-Hyoung; Lee, Chang-Hee

    2011-01-01

    SA508 Gr.4N Ni-Cr-Mo low alloy steel, in which Ni and Cr contents are higher than in commercial SA508 Gr.3 Mn-Mo-Ni low alloy steels, may be a candidate reactor pressure vessel (RPV) material with higher strength and toughness from its tempered martensitic microstructure. The inner surface of the RPV is weld-cladded with stainless steels to prevent corrosion. The goal of this study is to evaluate the microstructural properties of the clad interface between Ni-Cr-Mo low alloy steel and stainless weldment, and the effects of post weld heat treatment (PWHT) on the properties. The properties of the clad interface were compared with those of commercial Mn-Mo-Ni low alloy steel. Multi-layer welding of model alloys with ER308L and ER309L stainless steel by the SAW method was performed, and then PWHT was conducted at 610°C for 30 h. The microstructural changes of the clad interface were analyzed using OM, SEM and TEM, and micro-Vickers hardness tests were performed. Before PWHT, the heat affected zone (HAZ) showed higher hardness than base and weld metals due to formation of martensite after welding in both steels. In addition, the hardness of the HAZ in Ni-Cr-Mo low alloy steel was higher than that in Mn-Mo-Ni low alloy steel due to a comparatively high martensite fraction. The hardness of the HAZ decreased after PWHT in both steels, but the dark region was formed near the fusion line in which the hardness was locally high. In the case of Mn-Mo-Ni low alloy steel, formation of fine Cr-carbides in the weld region near the fusion line by diffusion of C from the base metal resulted in locally high hardness in the dark region. However, the precipitates of the region in the Ni-Cr-Mo low alloy steel were similar to that in the base metal, and the hardness in the region was not greatly different from that in the base metal.

  15. Performance of Cr-doped ZnO for acetone sensing

    Energy Technology Data Exchange (ETDEWEB)

    Al-Hardan, N.H., E-mail: naif_imen@ukm.my [Institute of Microengineering and Nanoelectronics (IMEN), Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor (Malaysia); Abdullah, M.J.; Aziz, A. Abdul [School of Physics, Universiti Sains Malaysia, 11800 USM, Penang (Malaysia)

    2013-04-01

    Zinc oxide (ZnO) doped with chromium (Cr) was synthesized by reactive co-sputtering for gas sensing applications. The effect of varying the contents of Cr (from 1 to 4 at%) on the ZnO gas sensor response was studied. X-ray diffraction analysis reveals the high orientation of c-axis of the prepared films. The optimum operating temperature of the undoped ZnO was 400 °C and shifted to 300 °C for the Cr-doped ZnO under the acetone vapour. The 1% Cr doping ZnO gas sensor was most sensitive for the acetone vapour. The ability of the 1% Cr-doped ZnO to produce repeatable results under different acetone vapour concentrations was tested. The timing properties of the doped Cr ZnO gas sensor were 70 and 95 s for the rise and recovery time respectively.

  16. Rutherford backscattering spectrometry of thin NiCr layers

    International Nuclear Information System (INIS)

    Anklam, H.J.

    1984-01-01

    The possibilities and problems of characterizing thin films of NiCr by means of Rutherford backscattering spectrometry (RBS) are demonstrated. Thin resistor films of NiCr (10 to 30 nm thick) are deposited on SiO 2 by sputtering in air or oxygen. The electrical properties depend both on integral chemical composition of films and on local distribution of elements. The determination of composition (Ni-Cr ratio, oxygen content) and of depth profiles of elements by the aid of RBS is described. For solving special analytical problems different substrates as amorphous SiO 2 , Si monocrystals, and glassy carbon are used

  17. Dielectric response and room temperature ferromagnetism in Cr doped anatase TiO2 nanoparticles

    Science.gov (United States)

    Naseem, Swaleha; Khan, Wasi; Khan, Shakeel; Husain, Shahid; Ahmad, Abid

    2018-02-01

    In the present work, nanocrystalline samples of Ti1-xCrxO2 (x = 0, 0.02, 0.04, 0.06 and 0.08) were synthesized in anatase phase through simple and cost effective acid modified sol gel method. The influence of Cr doping on thermal, microstructural, electrical and magnetic properties was investigated in TiO2 host matrix. The surface morphology has revealed less agglomeration and considerable reduction in particle size in case of Cr doped TiO2 as compared to undoped TiO2 nanoparticles (NPs). Energy dispersive x-ray spectroscopy (EDS), Raman and X-ray photoelectron spectroscopy (XPS) established high purity, appropriate stoichiometry and oxidation states of the compositions. The dielectric properties of the nanoparticles were altered by the doping concentration, applied frequency as well as temperature variation. The variation in dielectric constant (ε‧), dielectric loss (δ) and ac conductivity as a function of frequency and temperature at different doping concentration of Cr were interpreted in the light of Maxwell Wagner theory, space charge polarization mechanism and drift mobility of charge carriers. Both undoped and Cr doped TiO2 samples exhibit room temperature ferromagnetism (RTFM) that remarkably influenced by means of the Cr content. The significant enhancement in the magnetization was observed at 4% Cr doping. However, decrease in magnetization for higher doping signify antiferromagnetic interactions between Cr ions or superexchange mechanism. These results reveal that the oxygen vacancies play a crucial role to initiate the RTFM. Therefore, the present investigation suggests the potential applications of Cr doped TiO2 nanoparticles for spintronics application.

  18. Inputs and spatial distribution patterns of Cr in Jiaozhou Bay

    Science.gov (United States)

    Yang, Dongfang; Miao, Zhenqing; Huang, Xinmin; Wei, Linzhen; Feng, Ming

    2018-03-01

    Cr pollution in marine bays has been one of the critical environmental issues, and understanding the input and spatial distribution patterns is essential to pollution control. In according to the source strengths of the major pollution sources, the input patterns of pollutants to marine bay include slight, moderate and heavy, and the spatial distribution are corresponding to three block models respectively. This paper analyzed input patterns and distributions of Cr in Jiaozhou Bay, eastern China based on investigation on Cr in surface waters during 1979-1983. Results showed that the input strengths of Cr in Jiaozhou Bay could be classified as moderate input and slight input, and the input strengths were 32.32-112.30 μg L-1 and 4.17-19.76 μg L-1, respectively. The input patterns of Cr included two patterns of moderate input and slight input, and the horizontal distributions could be defined by means of Block Model 2 and Block Model 3, respectively. In case of moderate input pattern via overland runoff, Cr contents were decreasing from the estuaries to the bay mouth, and the distribution pattern was parallel. In case of moderate input pattern via marine current, Cr contents were decreasing from the bay mouth to the bay, and the distribution pattern was parallel to circular. The Block Models were able to reveal the transferring process of various pollutants, and were helpful to understand the distributions of pollutants in marine bay.

  19. Structural Properties of the Cr(III)-Fe(III) (Oxy)Hydroxide Compositional Series: Insights for a Nanomaterial 'Solid Solution'

    International Nuclear Information System (INIS)

    Tang, Y.; Zhang, L.; Michel, F.M.; Harrington, R.; Parise, J.B.; Reeder, R.J.

    2010-01-01

    Chromium(III) (oxy)hydroxide and mixed Cr(III)-Fe(III) (oxy)hydroxides are environmentally important compounds for controlling chromium speciation and bioaccessibility in soils and aquatic systems and are also industrially important as precursors for materials and catalyst synthesis. However, direct characterization of the atomic arrangements of these materials is complicated because of their amorphous X-ray properties. This study involves synthesis of the complete Cr(III)-Fe(III) (oxy)hydroxide compositional series, and the use of complementary thermal, microscopic, spectroscopic, and scattering techniques for the evaluation of their structural properties. Thermal analysis results show that the Cr end member has a higher hydration state than the Fe end member, likely associated with the difference in water exchange rates in the first hydration spheres of Cr(III) and Fe(III). Three stages of weight loss are observed and are likely related to the loss of surface/structural water and hydroxyl groups. As compared to the Cr end member, the intermediate composition sample shows lower dehydration temperatures and a higher exothermic transition temperature. XANES analysis shows Cr(III) and Fe(III) to be the dominant oxidation states. XANES spectra also show progressive changes in the local structure around Cr and Fe atoms over the series. Pair distribution function (PDF) analysis of synchrotron X-ray total scattering data shows that the Fe end member is nanocrystalline ferrihydrite with an intermediate-range order and average coherent domain size of ∼27 (angstrom). The Cr end member, with a coherent domain size of ∼10 (angstrom), has only short-range order. The PDFs show progressive structural changes across the compositional series. High-resolution transmission electron microscopy (HRTEM) results also show the loss of structural order with increasing Cr content. These observations provide strong structural evidence of chemical substitution and progressive structural

  20. Structural, optical and magnetic properties of Cr doped SnO{sub 2} nanoparticles stabilized with polyethylene glycol

    Energy Technology Data Exchange (ETDEWEB)

    Subramanyam, K.; Sreelekha, N. [Department of Physics, Sri Venkateswara University, Tirupati 517502 (India); Murali, G. [Department of BIN Fusion Technology and Department of Polymer-Nano Science and Technology, Chonbuk National University, Jeonju, Jeonbuk (Korea, Republic of); Reddy, D. Amaranatha [Department of Chemistry and Chemical Institute for Functional Materials, Pusan National University, Busan 609-735 (Korea, Republic of); Vijayalakshmi, R.P., E-mail: vijayaraguru@gmail.com [Department of Physics, Sri Venkateswara University, Tirupati 517502 (India)

    2014-12-01

    Pure and Cr (1, 3, 5 and 7 at%) doped SnO{sub 2} nanoparticles were synthesized in aqueous solution by a simple chemical co-precipitation method using polyethylene glycol (PEG) as a stabilizing agent. The effect of Cr doping on the structural, optical and magnetic properties of SnO{sub 2} nanoparticles was investigated. EDAX spectra confirmed the presence of Sn, O and Cr in near stoichiometry. XRD patterns revealed that particles of all samples were crystallized in single phase rutile type tetragonal crystal structure (P4{sub 2}/mnm) of SnO{sub 2}. The peak positions with Cr concentration shifted to higher 2θ values. Lattice parameters were also decreased with increasing Cr concentration. TEM studies indicated that the particle size is in the range of 8–10 nm. The optical absorption studies indicated that the absorption edge shifted towards lower wavelengths with inclusion of Cr content. FTIR spectrum displays various bands that are due to fundamental overtones of PEG and O–Sn–O entities. Further it revealed that the undoped and as well as Cr doped SnO{sub 2} nanoparticles were capped by PEG. Magnetization measurements at room temperature revealed that all the doped samples were ferromagnetic in nature. Well defined strong room temperature ferromagnetic hysteresis loop was observed for 1% Cr doped SnO{sub 2} nanoparticles.

  1. Creep and creep fatigue crack behavior of 1Cr- and 9Cr-steels

    International Nuclear Information System (INIS)

    Maile, K.; Klenk, A.; Schellenberg, G.; Granacher, J.; Tramer, M.

    2000-01-01

    A large database for creep crack initiation and propagation under constant load conditions is available on conventional power plant steels of types 1%Cr and 12%Cr. Modern plants are often used in the medium and peak load regime, thus the dominant loading situation in high temperature components is creep fatigue. For life assessment data about crack initiation and growth under creep fatigue loading are required. These characteristics can not be substituted by pure fatigue or creep crack data. Therefore, a comprehensive test programme was started to investigate the creep fatigue crack behaviour of a 1%CrMoNiV turbine rotor steel (30CrMoNiV 4 11) at 550 C and a new 9%CrMoVNb pipe steel (type P 9 1) at 600 C. DENT-specimen with 15 and 60 mm thickness as well as side grooved CT-specimen with 25 and 50 mm thickness have been tested to determine possible influences of geometry and thus to check the transferability of the data to components. The creep fatigue crack growth results of tests with dwell times between t H = 0,32h and 10 h lie in the scatterbands given by creep crack growth results. Nevertheless a higher crack growth rate under creep fatigue conditions can be stated. An increase in crack growth rate due to creep fatigue is clearly visible. Loading situations with frequencies higher than 1.10 -4 Hz should be not assessed with pure creep crack results or sufficient safety margins have to be applied. (orig.)

  2. Effects of Cr 3+ impurity concentration on the crystallography of synthetic emerald crystals

    Science.gov (United States)

    Lee, Pei-Lun; Huang, Eugene; Lee, Jan-Shing; Yu, Shu-Cheng

    2011-06-01

    Flux method has been adopted for the synthesis of emerald crystals using PbO-V 2O 5 as a flux in order to study the crystallography of the synthetic crystals. In general, the hue of green color of emerald deepens with the addition of Cr 3+. The molar volume of the synthesized crystals was found to increase with the incorporation of Cr 2O 3 dopant. The substitution of Cr 3+ for Al 3+ in the octahedral sites of beryl results in the expansion of a-axis, while c-axis remains nearly unchanged. The maximum Cr 2O 3-content allowed in the crystal lattice of emerald has been found to be about 3.5 wt%. When the doping Cr 2O 3-content exceeds 3.5 wt%, a significant anomaly in lattice parameters starts to take place, accompanying the precipitation of an unknown phase in the emerald matrix.

  3. TSEE from Fe-Cr alloy system and its application to the estimation of gasoline deterioration

    International Nuclear Information System (INIS)

    Shimada, H.; Nakajima, K.

    1983-01-01

    The exoelectron glow curves for oxide surface on Fe-Cr alloy were measured as a function of Cr content. It was seen that with increasing Cr content the total counts of thermally stimulated exoelectron emission (TSEE), threshold temperature for measuring the glow curve (starting temperature of the glow curve) and the activation energy clearly indicate a good coincidence with the oxidation process of the surface. The interaction of Fe-Cr alloy with gasoline was examined by applying the test for the oxidation induced period (ASTM D525). The induction period became minimum at about 4%Cr, and the deposit of gasoline gum was maximum at its composition. The results were compared with that of TSEE, and it was found that the catalytic effect of Fe-Cr alloy on the deterioration of gasoline is explained from the starting temperature of the glow curves. (author)

  4. High temperature tribological performance of CrAlYN/CrN nanoscale multilayer coatings deposited on ?-TiAl

    OpenAIRE

    Walker, J.C.; Ross, I.M.; Reinhard, C.; Rainforth, W.M.; Hovsepian, P.Eh.

    2009-01-01

    This paper details the effect of temperature on the frictional behaviour of highly novel CrAlYN/CrN multilayer coatings, deposited by High Power Impulse Magnetron Sputtering (HIPIMS) on a Titanium Aluminide alloy used as fan blade material in the aerospace and a turbo-charger wheel in the automotive industries. The work was the first to discover the high temperature oxide 'glaze' layer formation which occurred on CrN multilayer-type coatings at higher temperatures and has received significant...

  5. Ecological risk assessment of a coastal zone in Southern Vietnam: Spatial distribution and content of heavy metals in water and surface sediments of the Thi Vai Estuary and Can Gio Mangrove Forest.

    Science.gov (United States)

    Costa-Böddeker, Sandra; Hoelzmann, Philipp; Thuyên, Lê Xuân; Huy, Hoang Duc; Nguyen, Hoang Anh; Richter, Otto; Schwalb, Antje

    2017-01-30

    Enrichment of heavy metals was assessed in the Thi Vai Estuary and in the Can Gio Mangrove Forest (SE, Vietnam). Cd, Co, Cr, Cu, Mn, Ni, Pb and Zn contents in water and in sediments were measured. Total organic carbon, nitrogen, phosphorus and C/N ratios were determined. Cu and Cr values were higher than threshold effect level of toxicity, while Ni exceeded probable effect level, indicating the risk of probable toxicity effects. Enrichment factors (EF), contamination factor (CF) and Geo-accumulation index (I-geo) were determined. CF reveals moderate to considerable pollution with Cr and Ni. EF suggests anthropogenic sources of Cr, Cu and Ni. I-geo indicates low contamination with Co, Cu and Zn and moderate contamination with Cr and Ni. Overall metal contents were lower than expected for this highly industrialized region, probably due to dilution, suggesting that erosion rates and hydrodynamics may also play a role in metal contents distribution. Copyright © 2016 Elsevier Ltd. All rights reserved.

  6. 51Cr diffusion in Zr-Sn alloys

    International Nuclear Information System (INIS)

    Nicolai, L.I.; Migoni, R.L.; Hojvat de Tendler, Ruth

    1982-01-01

    The 51 Cr volume diffusion in Zr-Sn alloys is measured in polycrystals with big grains by the thin-film method. The Sn content in the alloys ranges from 0.39% at to 6.66 % at. In the beta-phase the analysed temperature range is 982 deg C-1240 deg C. The Sn dehances the 51 Cr diffusion in beta-Zr, the effect being small but well defined. Assuming the formation of Sn-Cr dimers, the linear dehancement coefficient b and the parameters for the variation of b with temperature were calculated. The parameters Q and D o were calculated for the more diluted alloys and, upon application of the Zener theory for D o , a negative contribution to the activation entropy is found. Three experiments at different temperatures were performed in the alpha-phase. 51 Cr diffuses very fast in alpha-Zr-Sn. No definite correlation is found between the 51 Cr diffusivity and the increasing Sn concentration, probably due to the anisotropy of the alfa-phase. (M.E.L.) [es

  7. Bioaccumulation and subcellular partitioning of Cr(III) and Cr(VI) in the freshwater green alga Chlamydomonas reinhardtii

    Energy Technology Data Exchange (ETDEWEB)

    Aharchaou, Imad [Laboratoire Interdisciplinaire des Environnements Continentaux, UMR 7360, Université de Lorraine and CNRS, 8 rue du Général Delestraint, 57070 Metz (France); Rosabal, Maikel; Liu, Fengjie [Institut National de la Recherche Scientifique, Centre Eau Terre Environnement (INRS-ETE), 490 rue de la Couronne, Québec (Québec) G1K 9A9 (Canada); Battaglia, Eric; Vignati, Davide A.L. [Laboratoire Interdisciplinaire des Environnements Continentaux, UMR 7360, Université de Lorraine and CNRS, 8 rue du Général Delestraint, 57070 Metz (France); Fortin, Claude, E-mail: claude.fortin@ete.inrs.ca [Institut National de la Recherche Scientifique, Centre Eau Terre Environnement (INRS-ETE), 490 rue de la Couronne, Québec (Québec) G1K 9A9 (Canada)

    2017-01-15

    Highlights: • C. reinhardtii accumulated similar levels of Cr(III) and Cr(VI). • The subcellular partitioning of Cr(III) and Cr(VI) was similar. • Cr(III) and Cr(VI) associated mainly with organelles and heat-stable proteins. • Metallomic analysis showed two main Cr-binding biomolecules after 72 h of exposure. - Abstract: Chromium occurs in aquatic environments under two main redox forms, namely Cr(III) and Cr(VI), with different geochemical and biochemical properties. Cr(VI) readily crosses biological membranes of living organisms and once inside the cells it undergoes a rapid reduction to Cr(III). The route of entry for the latter form is, however, poorly known. Using the radioactive tracer {sup 51}Cr we compared the accumulation (absorption and adsorption) of the two Cr forms by the green unicellular alga Chlamydomonas reinhardii after 1 h and 72 h of exposure to 100 nM of either Cr(III) or Cr(VI) at pH 7. Both Cr forms had similar accumulation, with a major part in the extracellular (adsorbed) fraction after 1 h and a major part of total accumulated Cr in the intracellular (absorbed) fraction after 72 h. We also investigated the intracellular partitioning of Cr using an operational fractionation scheme and found that both Cr forms had similar distributions among fractions: Cr was mostly associated with organelles (23 ± 12% after 1 h and 37 ± 7% after 72 h) and cytosolic heat-stable proteins and peptides (39 ± 18% after 1 h and 35 ± 3% after 72 h) fractions. Further investigations using a metallomic approach (SEC-ICP-MS) were performed with the heat-stable proteins and peptides fraction to compare the distribution of the two Cr forms among various biomolecules of this fraction. One Cr-binding biomolecule (∼28 kDa) appeared after 1 h of exposure for both Cr species. After 72 h another biomolecule of lower molecular weight (∼0.7 kDa) was involved in binding Cr and higher signal intensities were observed for Cr(VI) than for Cr(III). We show, for the

  8. Bioaccumulation and subcellular partitioning of Cr(III) and Cr(VI) in the freshwater green alga Chlamydomonas reinhardtii

    International Nuclear Information System (INIS)

    Aharchaou, Imad; Rosabal, Maikel; Liu, Fengjie; Battaglia, Eric; Vignati, Davide A.L.; Fortin, Claude

    2017-01-01

    Highlights: • C. reinhardtii accumulated similar levels of Cr(III) and Cr(VI). • The subcellular partitioning of Cr(III) and Cr(VI) was similar. • Cr(III) and Cr(VI) associated mainly with organelles and heat-stable proteins. • Metallomic analysis showed two main Cr-binding biomolecules after 72 h of exposure. - Abstract: Chromium occurs in aquatic environments under two main redox forms, namely Cr(III) and Cr(VI), with different geochemical and biochemical properties. Cr(VI) readily crosses biological membranes of living organisms and once inside the cells it undergoes a rapid reduction to Cr(III). The route of entry for the latter form is, however, poorly known. Using the radioactive tracer "5"1Cr we compared the accumulation (absorption and adsorption) of the two Cr forms by the green unicellular alga Chlamydomonas reinhardii after 1 h and 72 h of exposure to 100 nM of either Cr(III) or Cr(VI) at pH 7. Both Cr forms had similar accumulation, with a major part in the extracellular (adsorbed) fraction after 1 h and a major part of total accumulated Cr in the intracellular (absorbed) fraction after 72 h. We also investigated the intracellular partitioning of Cr using an operational fractionation scheme and found that both Cr forms had similar distributions among fractions: Cr was mostly associated with organelles (23 ± 12% after 1 h and 37 ± 7% after 72 h) and cytosolic heat-stable proteins and peptides (39 ± 18% after 1 h and 35 ± 3% after 72 h) fractions. Further investigations using a metallomic approach (SEC-ICP-MS) were performed with the heat-stable proteins and peptides fraction to compare the distribution of the two Cr forms among various biomolecules of this fraction. One Cr-binding biomolecule (∼28 kDa) appeared after 1 h of exposure for both Cr species. After 72 h another biomolecule of lower molecular weight (∼0.7 kDa) was involved in binding Cr and higher signal intensities were observed for Cr(VI) than for Cr(III). We show, for the

  9. Structural analysis and magnetic properties of solid solutions of Co–Cr system obtained by mechanical alloying

    International Nuclear Information System (INIS)

    Betancourt-Cantera, J.A.; Sánchez-De Jesús, F.; Bolarín-Miró, A.M.; Betancourt, I.; Torres-Villaseñor, G.

    2014-01-01

    In this paper, a systematic study on the structural and magnetic properties of Co 100−x Cr x alloys (0 1−x Cr x (0 2 /kg) for the Co 90 Cr 10 , which decreases with the increasing of the Cr content up to x=80, as a consequence of the dilution effect of the magnetic moment which is caused by the Cr content and by the competition between ferromagnetic and antiferromagnetic exchange interactions. The coercivity increases up to 34 kA/m (435 Oe) for Co 40 Cr 60 . For Cr rich compositions, it is observed an important decrease reaching 21 kA/m (272 Oe) for Co 10 Cr 90, it is related to the grain size and the structural change. Besides, the magnetic anisotropy constant was determined for each composition. Magnetic thermogravimetric analysis allowed to obtain Curie temperatures corresponding to the formation of hcp-Co(Cr) and fcc-Co(Cr) solid solutions. - Highlights: • Mechanical alloying (MA) induces the formation of solid solutions of Co–Cr system in non-equilibrium. • We report the crystal structure and the magnetic behavior of Co–Cr alloys produced by MA. • MA improves the magnetic properties of Co–Cr system

  10. Matrix Transformation in Boron Containing High-Temperature Co-Re-Cr Alloys

    Science.gov (United States)

    Strunz, Pavel; Mukherji, Debashis; Beran, Přemysl; Gilles, Ralph; Karge, Lukas; Hofmann, Michael; Hoelzel, Markus; Rösler, Joachim; Farkas, Gergely

    2018-03-01

    An addition of boron largely increases the ductility in polycrystalline high-temperature Co-Re alloys. Therefore, the effect of boron on the alloy structural characteristics is of high importance for the stability of the matrix at operational temperatures. Volume fractions of ɛ (hexagonal close-packed—hcp), γ (face-centered cubic—fcc) and σ (Cr2Re3 type) phases were measured at ambient and high temperatures (up to 1500 °C) for a boron-containing Co-17Re-23Cr alloy using neutron diffraction. The matrix phase undergoes an allotropic transformation from ɛ to γ structure at high temperatures, similar to pure cobalt and to the previously investigated, more complex Co-17Re-23Cr-1.2Ta-2.6C alloy. It was determined in this study that the transformation temperature depends on the boron content (0-1000 wt. ppm). Nevertheless, the transformation temperature did not change monotonically with the increase in the boron content but reached a minimum at approximately 200 ppm of boron. A probable reason is the interplay between the amount of boron in the matrix and the amount of σ phase, which binds hcp-stabilizing elements (Cr and Re). Moreover, borides were identified in alloys with high boron content.

  11. INFLUENCE OF ANNEALING ON HARDNESS OF Cr-Mn-Ni CAST IRONS

    Directory of Open Access Journals (Sweden)

    V. V. Netrebko

    2015-01-01

    Full Text Available The necessary level of material’s hardness is determined by the exploitation conditions and presence of technological operations during manufacturing of articles. Mechanical edge cutting machining of wear resistant materials is impeded because of their high hardness. It is recommended to apply annealing in order to decrease hardness and improve machinability. The purpose of the work consisted in obtaining of regression dependences of cast iron’s macrohardness on its chemical content after annealing at 730 °С. With the use of mathematical experimental design the regression dependences of cast iron’s macrohardness and structural components’ microhardness on С, Cr, Mn, Ni content have been established. The minimal hardness of 27,6 HRC after annealing at 730 °С is obtained in the cast iron containing: 3,9% С; 11,4% Cr; 0,6% Mn; 0,2% Ni. The maximal hardness of 70,4 HRC is obtained when the content is as follows: 1,1% С; 25,6% Cr; 5,4% Mn; 3,0% Ni. Annealing at 730 °С decreases the cast irons’ hardness containing the minimal amount of Cr, Mn and Ni. Annealing at 730 °С is recommended for cast irons alloyed by Mn and Ni for increasing of hardness.

  12. Effect of Cr doping on the structural, morphological, optical and electrical properties of indium tin oxide films

    Science.gov (United States)

    Mirzaee, Majid; Dolati, Abolghasem

    2015-03-01

    We report on the preparation and characterization of high-purity chromium (0.5-2.5 at.%)-doped indium tin oxide (ITO, In:Sn = 90:10) films deposited by sol-gel-mediated dip coating. The effects of different Cr-doping contents on structural, morphological, optical and electrical properties of the films were characterized by means of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), field emission scanning electron microscopy (FESEM), UV-Vis spectroscopy and four-point probe methods. XRD showed high phase purity cubic In2O3 and indicated a contraction of the lattice with Cr doping. FESEM micrographs show that grain size decreased with increasing the Cr-doping content. A method to determine chromium species in the sample was developed through the decomposition of the Cr 2 p XPS spectrum in Cr6+ and Cr3+ standard spectra. Optical and electrical studies revealed that optimum opto-electronic properties, including minimum sheet resistance of 4,300 Ω/Sq and an average optical transmittance of 85 % in the visible region with a band gap of 3.421 eV, were achieved for the films doped with Cr-doping content of 2 at.%.

  13. Effect of carbon content on solidification behaviors and morphological characteristics of the constituent phases in Cr-Fe-C alloys

    International Nuclear Information System (INIS)

    Lin, Chi-Ming; Lai, Hsuan-Han; Kuo, Jui-Chao; Wu, Weite

    2011-01-01

    A combination of transmission electron microscopy, electron backscatter diffraction and wavelength dispersive spectrum has been used to identify crystal structure, grain boundary characteristic and chemical composition of the constituent phases in Cr-Fe-C alloys with three different carbon concentrations. Depending on the three different carbon concentrations, the solidification structures are found to consist of primary α-phase and [α + (Cr,Fe) 23 C 6 ] eutectic in Cr-18.4Fe-2.3 C alloy; primary (Cr,Fe) 23 C 6 and [α + (Cr,Fe) 23 C 6 ] eutectic in Cr-24.5Fe-3.8 C alloy and primary (Cr,Fe) 7 C 3 and [α + (Cr,Fe) 7 C 3 ] eutectic in Cr-21.1Fe-5.9 C alloy, respectively. The grain boundary analysis is useful to understand growth mechanism of the primary phase. The morphologies of primary (Cr,Fe) 23 C 6 and (Cr,Fe) 7 C 3 carbides are faceted structures with polygonal shapes, different from primary α-phase with dendritic shape. The primary (Cr,Fe) 23 C 6 and (Cr,Fe) 7 C 3 carbides with strong texture exist a single crystal structure and contain a slight low angle boundary, resulting in the polygonal growth mechanism. Nevertheless, the primary α-phase with relative random orientation exhibits a polycrystalline structure and comprises a massive high-angle boundary, caused by the dendritic growth mechanism. - Highlights: ► Microstructures of the as-clad Cr-based alloys are characterized by TEM. ► EBSD technique has been use to characterize the grain boundary of primary phases. ► We examine transitions in morphology about the primary phases. ► Morphologies of primary carbides are polygonal different from primary α-phase. ► Solidification structures rely on C concentrations in Cr-Fe-C alloy.

  14. Crystal structure, Raman scattering and magnetic properties of CuCr2-xZrxSe4 and CuCr2-xSnxSe4 selenospinels

    Science.gov (United States)

    Pinto, C.; Galdámez, A.; Barahona, P.; Moris, S.; Peña, O.

    2018-06-01

    Selenospinels, CuCr2-xMxSe4 (M = Zr and Sn), were synthesized via conventional solid-state reactions. The crystal structure of CuCr1.5Sn0.5Se4, CuCr1.7Sn0.3Se4, CuCr1.5Zr0.5Se4, and CuCr1.8Zr0.2Se4 were determined using single-crystal X-ray diffraction. All the phases crystallized in a cubic spinel-type structure. The chemical compositions of the single-crystals were examined using energy-dispersive X-ray analysis (EDS). Powder X-ray diffraction patterns of CuCr1.3Sn0.7Se4 and CuCr1.7Sn0.3Se4 were consistent with phases belonging to the Fd 3 bar m Space group. An analysis of the vibrational properties on the single-crystals was performed using Raman scattering measurements. The magnetic properties showed a spin glass behavior with increasing Sn content and ferromagnetic order for CuCr1.7Sn0.3Se4.

  15. A study of oxidation resistant coating on TiAl alloys by Cr evaporation and pack cementation

    International Nuclear Information System (INIS)

    Jung, Dong Ju; Jung, Hwan Gyo; Kim, Kyoo Young

    2002-01-01

    A Cr+Al-type composite coating is applied to improve the properties of aluminide coating layers, AiAl 3 , formed on TiAl alloys. This method is performed by Cr evaporation on the TiAl-XNb(X= 1,6at%) substrate followed by pack aluminizing. The coating layer formed by the composite coating process consists of the outer layer of Al 4 Cr and the inner layer of TiAl 3 regardless of the Nb content. however, these coating layers are transformed to Ti(Al,Cr) 3 layers with Ll 2 structures during oxidation. In particular, as Nb content increases, the grain size of the inner TiAl 3 layer becomes smaller and the diffusion rate of Cr increases after oxidation. Faster formation of a Ti(Al,Cr) 3 layer with an Ll 2 structure through Nb addition is more effective to improve cracking resistance at the beginning of oxidation of TiAl alloys. However, growth of Ti(Al,Cr) 3 formed on the coating layer becomes slower as the Nb content in the coating layer is increased. As a result, the addition of a large amount of Nb to composite coating layer is not desirable due to poor ductility of the coating layer. A Ti(Al,Cr) 3 layer with an Ll 2 structure developed during oxidation showed much better ductility compared with other coating layers

  16. Validation of FNAA method for testing the elements of Mn, Cr and Mg on the Gajahwong river sediment sample

    International Nuclear Information System (INIS)

    Wisjachudin Faisal; Elin Nuraini

    2010-01-01

    Validation of elements of Mn, Cr and Mg by using FNAA method has been performed. NBS SRM 8704 (Bufallo River Sediment), was used as the standard reference material, with the neutrons generator operating condition at the optimum voltage of 110 kV. Energy and channel number of calibration lines obtained with the standard equation as y = 1.034 x + 151.21. From the analysis of SRM, the results show that only Mg can be analyzed, because Cr and Mn are located at the same peak point (interferences), so that they can not be analyzed. From the analysis for Mg element (SRM), the precision and the accuration obtained are 95.53 % and 94.88%, while the average price of expanded uncertainty for the various locations is 0.233 ± 0.012. Mg content analysis result at various locations along the river Gajahwong ranging from 85.41 – 103.55 ppm. When compared with previous studies showing the elements content of Fe, Al and Si is much higher than Mg content. (author)

  17. Engaging adolescents with LD in higher order thinking about history concepts using integrated content enhancement routines.

    Science.gov (United States)

    Bulgren, Janis; Deshler, Donald D; Lenz, B Keith

    2007-01-01

    The understanding and use of historical concepts specified in national history standards pose many challenges to students. These challenges include both the acquisition of content knowledge and the use of that knowledge in ways that require higher order thinking. All students, including adolescents with learning disabilities (LD), are expected to understand and use concepts of history to pass high-stakes assessments and to participate meaningfully in a democratic society. This article describes Content Enhancement Routines (CERs) to illustrate instructional planning, teaching, and assessing for higher order thinking with examples from an American history unit. Research on the individual components of Content Enhancement Routines will be illustrated with data from 1 of the routines. The potential use of integrated sets of materials and procedures across grade levels and content areas will be discussed.

  18. NAA for studying detoxification of Cr and Hg by Arthrobacter globiformis 151B

    International Nuclear Information System (INIS)

    Tsibakhashvili, N.; Mosulishvili, L.; Kirkesali, E.; Murusidze, I.; Frontasyeva, M.V.; Pavlov, S.S.; Zinicovscaia, I.I.

    2010-01-01

    Instrumental neutron activation analysis was used to study accumulation of Hg(II) and Cr(VI) ions in Arthrobacter globiformis 151B, a gram-positive, Cr(VI)-reducer aerobic bacterium isolated from basalt sample taken from the most polluted region in the Republic of Georgia (Kazreti). Experiments were focused on (1) accumulation of Hg(II) in bacterial cells; (2) accumulation of Cr(VI) in A. globiformis 151B in the presence of Hg(II) and (3) effects of Hg(II) and mixture of Cr(VI)-Hg(II) on the elemental composition of bacteria. It was shown that this bacterial strain possesses uptake mechanisms by which mercury toxicity can be reduced in environment and that accumulation of Cr(VI) in A. globiformis 151B is much higher in the presence of Hg(II) ions. Accumulation of Hg(II), similar to the Cr(VI) accumulation, follows well the Lengmuir-Freundlich model. NAA measurements showed increased content of Fe in bacteria under Hg and Cr action, suggesting that Fe-containing biomolecules play a decisive role in detoxifying of heavy metals by A. globiformis 151B. A concentration of 5000 μg/L of Hg(II) was found to be critical for A. globiformis 151B. At this concentration of Hg(II) the concentrations of both essential (Na, Mg, Al, Cl, K, Mn, Zn) and some non-essential elements (Rb, Sb, Sc, As) changed drastically along with a decrease of the biomass of bacteria by a factor of two. One may assume that under this high exposure to Hg(II) the structure of the bacterial cell wall was destroyed. (author)

  19. Biosorption of Cr(VI) by coconut coir: Spectroscopic investigation on the reaction mechanism of Cr(VI) with lignocellulosic material

    International Nuclear Information System (INIS)

    Shen, Ying-Shuian; Wang, Shan-Li; Huang, Shiuh-Tsuen; Tzou, Yu-Min; Huang, Jang-Hung

    2010-01-01

    In this study, the removal mechanism of Cr(VI) from water by coconut coir (CC) was investigated using X-ray photoelectron spectroscopy (XPS), Cr K-edge X-ray absorption near edge structure (XANES) and FTIR spectroscopy. The results showed that, upon reaction with CC at pH 3, Cr(VI) was reduced to Cr(III), which was either bound to CC or released back into solution. As revealed by the FTIR spectra of CC before and after reacting with Cr(VI), the phenolic methoxyl and hydroxyl groups of lignin in CC are the dominant drivers of Cr(VI) reduction, giving rise to carbonyl and carboxyl groups on CC. These functional groups can subsequently provide binding sites for Cr(III) resulting from Cr(VI) reduction. In conjunction with forming complexes with carbonyl and carboxyl groups, the formation of Cr(III) hydroxide precipitate could also readily occur as revealed by the linear combination fitting of the Cr K-edge XANES spectrum using a set of reference compounds. The phenolic groups in lignin are responsible for initiating Cr(VI) reduction, so lignocellulosic materials containing a higher amount of phenolic groups are expected to be more effective scavengers for removal of Cr(VI) from the environment.

  20. Biosorption of Cr(VI) by coconut coir: Spectroscopic investigation on the reaction mechanism of Cr(VI) with lignocellulosic material

    Energy Technology Data Exchange (ETDEWEB)

    Shen, Ying-Shuian [Department of Soil and Environmental Sciences, National Chung Hsing University, 250 Kuo Kuang Road, Taichung 40227, Taiwan (China); Wang, Shan-Li, E-mail: slwang@nchu.edu.tw [Department of Soil and Environmental Sciences, National Chung Hsing University, 250 Kuo Kuang Road, Taichung 40227, Taiwan (China); Huang, Shiuh-Tsuen [Department of Soil and Environmental Sciences, National Chung Hsing University, 250 Kuo Kuang Road, Taichung 40227, Taiwan (China); Department of Science Application and Dissemination, National Taichung University, Taichung, Taiwan (China); Tzou, Yu-Min; Huang, Jang-Hung [Department of Soil and Environmental Sciences, National Chung Hsing University, 250 Kuo Kuang Road, Taichung 40227, Taiwan (China)

    2010-07-15

    In this study, the removal mechanism of Cr(VI) from water by coconut coir (CC) was investigated using X-ray photoelectron spectroscopy (XPS), Cr K-edge X-ray absorption near edge structure (XANES) and FTIR spectroscopy. The results showed that, upon reaction with CC at pH 3, Cr(VI) was reduced to Cr(III), which was either bound to CC or released back into solution. As revealed by the FTIR spectra of CC before and after reacting with Cr(VI), the phenolic methoxyl and hydroxyl groups of lignin in CC are the dominant drivers of Cr(VI) reduction, giving rise to carbonyl and carboxyl groups on CC. These functional groups can subsequently provide binding sites for Cr(III) resulting from Cr(VI) reduction. In conjunction with forming complexes with carbonyl and carboxyl groups, the formation of Cr(III) hydroxide precipitate could also readily occur as revealed by the linear combination fitting of the Cr K-edge XANES spectrum using a set of reference compounds. The phenolic groups in lignin are responsible for initiating Cr(VI) reduction, so lignocellulosic materials containing a higher amount of phenolic groups are expected to be more effective scavengers for removal of Cr(VI) from the environment.

  1. Biosorption of Cr(VI) by coconut coir: spectroscopic investigation on the reaction mechanism of Cr(VI) with lignocellulosic material.

    Science.gov (United States)

    Shen, Ying-Shuian; Wang, Shan-Li; Huang, Shiuh-Tsuen; Tzou, Yu-Min; Huang, Jang-Hung

    2010-07-15

    In this study, the removal mechanism of Cr(VI) from water by coconut coir (CC) was investigated using X-ray photoelectron spectroscopy (XPS), Cr K-edge X-ray absorption near edge structure (XANES) and FTIR spectroscopy. The results showed that, upon reaction with CC at pH 3, Cr(VI) was reduced to Cr(III), which was either bound to CC or released back into solution. As revealed by the FTIR spectra of CC before and after reacting with Cr(VI), the phenolic methoxyl and hydroxyl groups of lignin in CC are the dominant drivers of Cr(VI) reduction, giving rise to carbonyl and carboxyl groups on CC. These functional groups can subsequently provide binding sites for Cr(III) resulting from Cr(VI) reduction. In conjunction with forming complexes with carbonyl and carboxyl groups, the formation of Cr(III) hydroxide precipitate could also readily occur as revealed by the linear combination fitting of the Cr K-edge XANES spectrum using a set of reference compounds. The phenolic groups in lignin are responsible for initiating Cr(VI) reduction, so lignocellulosic materials containing a higher amount of phenolic groups are expected to be more effective scavengers for removal of Cr(VI) from the environment. 2010 Elsevier B.V. All rights reserved.

  2. Microcosm investigation on phytoremediation of Cr using Azolla pinnata.

    Science.gov (United States)

    Rai, Prabhat Kumar

    2010-01-01

    The extent of Chromium (Cr) pollution in Singrauli industrial region, India was assessed and phytoremediation capacity of a small water fern, Azolla pinnata R.BR (Azollaceae) was observed to purify waters polluted by Cr under microcosm condition. Azolla pinnata endemic to India is a potential hyper-accumulator of heavy metals. During 13 days of the experiment the fern was grown in the aqueous medium containing Cr3+ and CrO4(2-) ions, each in a concentration 0.5, 1.0, and 3.0 mg L(-1). The presence of these ions caused a + 3.1 to -37.5% inhibition of Azolla pinnata growth in comparison to the control. After 13 days of the experiment, metal contents in the solution was decreased up to 70% (CrO4(2-) 3.0 mg L(-1) treatment) to 88% (CrO4(2-) 0.5 mg L(-1) treatment). In the Azolla pinnata tissues, the concentration of couple of the ionic forms of Cr under investigation ranged from 415 to 1095 mg kg(-1) dry mass (dm); the highest level being found for Cr (III) containing solution.

  3. Grain Refinement and Mechanical Properties of Cu-Cr-Zr Alloys with Different Nano-Sized TiCp Addition.

    Science.gov (United States)

    Zhang, Dongdong; Bai, Fang; Wang, Yong; Wang, Jinguo; Wang, Wenquan

    2017-08-08

    The TiC p /Cu master alloy was prepared via thermal explosion reaction. Afterwards, the nano-sized TiC p /Cu master alloy was dispersed by electromagnetic stirring casting into the melting Cu-Cr-Zr alloys to fabricate the nano-sized TiC p -reinforced Cu-Cr-Zr composites. Results show that nano-sized TiC p can effectively refine the grain size of Cu-Cr-Zr alloys. The morphologies of grain in Cu-Cr-Zr composites changed from dendritic grain to equiaxed crystal because of the addition and dispersion of nano-sized TiC p . The grain size decreased from 82 to 28 μm with the nano-sized TiC p content. Compared with Cu-Cr-Zr alloys, the ultimate compressive strength (σ UCS ) and yield strength (σ 0.2 ) of 4 wt% TiC p -reinforced Cu-Cr-Zr composites increased by 6.7% and 9.4%, respectively. The wear resistance of the nano-sized TiCp-reinforced Cu-Cr-Zr composites increased with the increasing nano-sized TiCp content. The wear loss of the nano-sized TiC p -reinforced Cu-Cr-Zr composites decreased with the increasing TiC p content under abrasive particles. The eletrical conductivity of Cu-Cr-Zr alloys, 2% and 4% nano-sized TiCp-reinforced Cu-Cr-Zr composites are 64.71% IACS, 56.77% IACS and 52.93% IACS, respectively.

  4. Evaluation of 2 1/4 Cr-1 Mo steel for liquid lithium containment. II. Effects of post-weld heat treatment and niobium content. Annual report, 1979

    Energy Technology Data Exchange (ETDEWEB)

    Anderson, T.L.; Edwards, G.R.

    1979-01-01

    The lithium corrosion resistance of the regular grade of 2 1/4 Cr-1 Mo steel can be vastly improved with a proper postweld heat treatment, but even greater improvements are needed. Results indicate that if weldments were tempered sufficiently long at 760C to remove all Mo/sub 2/C from the microstructure, even greater resistance to attack by low nitrogen lithium could be achieved. Corrosion tests should eventually be performed on regular grade 2 1/4 Cr-1 Mo steel weldments which have been given a long-term (> 25 h) post-weld temper at 760C. Lithium corrosion resistance of regular grade 2 1/4 Cr-1 Mo steel may also be improved by employing a quench and temper heat treatment. Quenched microstructures have more homogenous distribution of carbides than isothermally annealed microstructures, and if properly tempered, should provide excellent lithium corrosion resistance. Furthermore, the toughness of such a lower bainite microstructure should be better than that of the ferrite-bainitic microstructure created by an isothermal anneal. Numerous parameters, all potentially deleterious to the lithium corrosion resistance of 2 1/4 Cr-1 Mo steel, remain to be investigated; two such variables are velocity effects and lead content in the lithium.

  5. Evaluation of 2 1/4 Cr-1 Mo steel for liquid lithium containment. II. Effects of post-weld heat treatment and niobium content. Annual report, 1979

    International Nuclear Information System (INIS)

    Anderson, T.L.; Edwards, G.R.

    1979-01-01

    The lithium corrosion resistance of the regular grade of 2 1/4 Cr-1 Mo steel can be vastly improved with a proper postweld heat treatment, but even greater improvements are needed. Results indicate that if weldments were tempered sufficiently long at 760C to remove all Mo 2 C from the microstructure, even greater resistance to attack by low nitrogen lithium could be achieved. Corrosion tests should eventually be performed on regular grade 2 1/4 Cr-1 Mo steel weldments which have been given a long-term (> 25 h) post-weld temper at 760C. Lithium corrosion resistance of regular grade 2 1/4 Cr-1 Mo steel may also be improved by employing a quench and temper heat treatment. Quenched microstructures have more homogenous distribution of carbides than isothermally annealed microstructures, and if properly tempered, should provide excellent lithium corrosion resistance. Furthermore, the toughness of such a lower bainite microstructure should be better than that of the ferrite-bainitic microstructure created by an isothermal anneal. Numerous parameters, all potentially deleterious to the lithium corrosion resistance of 2 1/4 Cr-1 Mo steel, remain to be investigated; two such variables are velocity effects and lead content in the lithium

  6. Effect of CrO3 Sealing Time on Anodized A12024-T3

    Science.gov (United States)

    Korda, Akhmad A.; Hidayat, R. Z.

    2016-08-01

    The effect of CrO3 sealing time on anodized aluminum alloy has been investigated. A1 2024-T3 were used as substrate. Anodizing was carried out using chromic acid. CrO3 sealing was conducted in CrO3 solution for 30, 60, 90, 120 and 150 minutes. As comparison, other specimens were also prepared as anodized and boiled water sealing. Thickness of the coating was observed by optical microscope. Anodized and sealing layer was analyzed by X- ray diffraction. The hardness of as anodized, boiled water sealing and CrO3 sealing were compared. The highest hardness is achieved by CrO3 sealed specimen and followed by boiled water sealing and as anodized specimens. The longer the processes of CrO3 sealing the higher layer thickness and therefore the higher hardness of the oxide layer. The best resistance to electrolyte penetration is achieved by the CrO3 sealed specimen followed by boiled water sealed and as anodized specimens. The higher thickness of oxide layer, the higher the resistance against electrolyte penetration.

  7. Effect of CrO_3 Sealing Time on Anodized A12024-T3

    International Nuclear Information System (INIS)

    Korda, Akhmad A; Hidayat, R Z

    2016-01-01

    The effect of CrO_3 sealing time on anodized aluminum alloy has been investigated. A1 2024-T3 were used as substrate. Anodizing was carried out using chromic acid. CrO_3 sealing was conducted in CrO_3 solution for 30, 60, 90, 120 and 150 minutes. As comparison, other specimens were also prepared as anodized and boiled water sealing. Thickness of the coating was observed by optical microscope. Anodized and sealing layer was analyzed by X- ray diffraction. The hardness of as anodized, boiled water sealing and CrO_3 sealing were compared. The highest hardness is achieved by CrO_3 sealed specimen and followed by boiled water sealing and as anodized specimens. The longer the processes of CrO3 sealing the higher layer thickness and therefore the higher hardness of the oxide layer. The best resistance to electrolyte penetration is achieved by the CrO_3 sealed specimen followed by boiled water sealed and as anodized specimens. The higher thickness of oxide layer, the higher the resistance against electrolyte penetration. (paper)

  8. The association of personal semantic memory to identity representations: insight into higher-order networks of autobiographical contents.

    Science.gov (United States)

    Grilli, Matthew D

    2017-11-01

    Identity representations are higher-order knowledge structures that organise autobiographical memories on the basis of personality and role-based themes of one's self-concept. In two experiments, the extent to which different types of personal semantic content are reflected in these higher-order networks of memories was investigated. Healthy, young adult participants generated identity representations that varied in remoteness of formation and verbally reflected on these themes in an open-ended narrative task. The narrative responses were scored for retrieval of episodic, experience-near personal semantic and experience-far (i.e., abstract) personal semantic contents. Results revealed that to reflect on remotely formed identity representations, experience-far personal semantic contents were retrieved more than experience-near personal semantic contents. In contrast, to reflect on recently formed identity representations, experience-near personal semantic contents were retrieved more than experience-far personal semantic contents. Although episodic memory contents were retrieved less than both personal semantic content types to reflect on remotely formed identity representations, this content type was retrieved at a similar frequency as experience-far personal semantic content to reflect on recently formed identity representations. These findings indicate that the association of personal semantic content to identity representations is robust and related to time since acquisition of these knowledge structures.

  9. Thermodynamic properties of CdCr2S4

    International Nuclear Information System (INIS)

    Kesler, Ya.A.; Shchelkotunov, V.A.; Tret'yakov, Yu.D.; Kamyshova, V.K.; Gordeev, I.V.; Alferov, V.A.

    1977-01-01

    The true thermal capacity of ferromagnetic chromium spinel CdCr 2 S 4 has been measured in the temperature range of 172-673 K. Coefficient of linear expansion has been measured in the temperature range of 173-677 K. A change in heat content of the compound has been found by the mixing method (298-750 K). The lattice contribution into thermal capacity, the contribution of thermal expansion, the values of isothermal compressibility factor, and the Crueneisen constants have been calculated from true and mean heat capacity of CdCr 2 S 4 in a wide temperature range. The lattice energy V has been calculated for CdCr 2 S 4 ; it amounts -4226 kcal/mol

  10. Preferred orientation in Cr- and Co-based thin films and its effects on the read/write performance of the media

    Science.gov (United States)

    Tsai, Hsiao-chu; Lal, Brij B.; Eltoukhy, Atef

    1992-04-01

    This work investigates the formation of preferred crystallographic orientation (PO) in Cr underlayer as well as CoCrTa and CoCrPtTa thin films and its effects on the recording performance of longitudinal media. The results show that the thin-film media with comparable coercivity but different crystalline PO as measured by x-ray diffraction exhibit significant difference in high-frequency signal amplitude, pulse width, and signal-to-noise ratio. To illustrate the effect of PO on parametric performance, CoCrTa/Cr and CoCrPtTa/Cr media were sputtered on different substrates and/or using special sputtering processes to achieve comparable coercivity but different PO in the films. A PO of Cr(200), which normally occurs on the NiP/Al substrates under adequate sputtering conditions, is found to be the key to obtaining a PO of Co(11.0) in Co-alloy media. The consequence of preferred in-plane c-axis orientation is a higher coercivity and better parametric performance of the medium. The formation of PO in the Cr underlayer is found to be related to the substrate material and the oxygen content in the sputtered films. The nonmetallic canasite substrates tend to promote PO of more stable Cr(110) rather than Cr(200). Consequently, this leads to a PO of out-of-plane c axis on the following Co films. The PO of magnetic layer appears to be an important factor in determining the parametric performance of the media.

  11. Molecular beam and pulsed laser deposition of ZnS:Cr for intermediate band solar cells

    OpenAIRE

    Nematollahi, Mohammadreza; Yang, Xiaodong; Aas, Lars Martin Sandvik; Ghadyani, Zahra; Kildemo, Morten; Gibson, Ursula; Reenaas, Turid Worren

    2015-01-01

    We have investigated the structural and optical properties of Cr-doped ZnS (ZnS:Cr) thin films (0–7.5 at.% Cr) for use in intermediate band solar cells. The films were grown on Si(100) in molecular beam epitaxy (MBE) and pulsed laser deposition (PLD) equipments. Introducing Cr into ZnS resulted in Cr related subbandgap absorption, but also reduced the grain size. The sub-bandgap absorption increased with increasing Cr content, and with increasing growth temperature, but did not depend on the ...

  12. Porous CrN thin films by selectively etching CrCuN for symmetric supercapacitors

    KAUST Repository

    Wei, Binbin

    2018-03-18

    Transition metal nitrides are regarded as a new class of excellent electrode materials for high-performance supercapacitors due to their superior chemical stability and excellent electrical conductivity. We synthesize successfully the porous CrN thin films for binder-free supercapacitor electrodes by reactive magnetron co-sputtering and selective chemical etching. The porous CrN thin film electrodes exhibit high-capacitance performance (31.3 mF cm−2 at 1.0 mA cm−2) and reasonable cycling stability (94% retention after 20000 cycles). Moreover, the specific capacitance is more than two-fold higher than that of the CrN thin film electrodes in previous work. In addition, a symmetric supercapacitor device with a maximum energy density of 14.4 mWh cm−3 and a maximum power density of 6.6 W cm−3 is achieved. These findings demonstrate that the porous CrN thin films will have potential applications in supercapacitors.

  13. Porous CrN thin films by selectively etching CrCuN for symmetric supercapacitors

    Science.gov (United States)

    Wei, Binbin; Mei, Gui; Liang, Hanfeng; Qi, Zhengbing; Zhang, Dongfang; Shen, Hao; Wang, Zhoucheng

    2018-05-01

    Transition metal nitrides are regarded as a new class of excellent electrode materials for high-performance supercapacitors due to their superior chemical stability and excellent electrical conductivity. We synthesize successfully the porous CrN thin films for binder-free supercapacitor electrodes by reactive magnetron co-sputtering and selective chemical etching. The porous CrN thin film electrodes exhibit high-capacitance performance (31.3 mF cm-2 at 1.0 mA cm-2) and reasonable cycling stability (94% retention after 20000 cycles). Moreover, the specific capacitance is more than two-fold higher than that of the CrN thin film electrodes in previous work. In addition, a symmetric supercapacitor device with a maximum energy density of 14.4 mWh cm-3 and a maximum power density of 6.6 W cm-3 is achieved. These findings demonstrate that the porous CrN thin films will have potential applications in supercapacitors.

  14. Hexavalent chromium content in stainless steel welding fumes is dependent on the welding process and shield gas type.

    Science.gov (United States)

    Keane, Michael; Stone, Samuel; Chen, Bean; Slaven, James; Schwegler-Berry, Diane; Antonini, James

    2009-02-01

    Occupational exposure to welding fumes is a known health hazard. To isolate elements in stainless steel welding fumes with high potential for adverse health outcomes, fumes were generated using a robotic gas metal arc system, using four shield gases of varying oxygen content. The objective was to measure Cr(VI) concentrations in a broad spectrum of gas metal arc welding processes, and identify processes of exceptionally high or low Cr(VI) content. The gases used were 95% Ar/5% O(2), 98% Ar/2% O(2), 95% Ar/5%CO(2), and 75% He/25% Ar. The welder was operated in axial spray mode (Ar/O(2), Ar/CO(2)), short-circuit (SC) mode (Ar/CO(2) low voltage and He/Ar), and pulsed axial-spray mode (98% Ar/2% O(2)). Results indicate large differences in Cr(VI) in the fumes, with Ar/O(2) (Pulsed)>Ar/O(2)>Ar/CO(2)>Ar/CO(2) (SC)>He/Ar; values were 3000+/-300, 2800+/-85, 2600+/-120, 1400+/-190, and 320+/-290 ppm respectively (means +/- standard errors for 2 runs and 3 replicates per run). Respective rates of Cr(VI) generation were 1.5, 3.2, 4.4, 1.3, and 0.46 microg/min; generation rates were also calculated in terms of microg Cr(VI) per metre of wire used. The generation rates of Cr(VI) increased with increasing O(3) concentrations. Particle size measurements indicated similar distributions, but somewhat higher >0.6 microm fractions for the short-circuit mode samples. Fumes were also sampled into 2 selected size ranges, a microspatter fraction (>or=0.6 microm) and a fine (welding type and shield gas type, and this presents an opportunity to tailor welding practices to lessen Cr(VI) exposures in workplaces by selecting low Cr(VI)-generating processes. Short-circuit processes generated less Cr(VI) than axial-spray methods, and inert gas shielding gave lower Cr(VI) content than shielding with active gases. A short circuit He/Ar shielded process and a pulsed axial spray Ar/O(2) process were both identified as having substantially lower Cr(VI) generation rates per unit of wire used relative

  15. A New Method to Produce Ni-Cr Ferroalloy Used for Stainless Steel Production

    Science.gov (United States)

    Chen, Pei-Xian; Chu, Shao-Jun; Zhang, Guo-Hua

    2016-08-01

    A new electrosilicothermic method has been proposed in the present paper to produce Ni-Cr ferroalloy, which can be used for the production of 300 series stainless steel. Based on this new process, the Ni-Si ferroalloy is first produced as the intermediate alloy, and then the desiliconization process of Ni-Si ferroalloy melt with chromium concentrate is carried out to generate Ni-Cr ferroalloy. The silicon content in the Ni-Si ferroalloy produced in the submerged arc furnace should be more than 15 mass% (for the propose of reducing dephosphorization), in order to make sure the phosphorus content in the subsequently produced Ni-Cr ferroalloy is less than 0.03 mass%. A high utilization ratio of Si and a high recovery ratio of Cr can be obtained after the desiliconization reaction between Ni-Si ferroalloy and chromium concentrate in the electric arc furnace (EAF)-shaking ladle (SL) process.

  16. Determination of the 51Cr source strength at BNL

    International Nuclear Information System (INIS)

    Boger, J.; Hahn, R.L.; Chu, Y.Y.

    1995-11-01

    Neutron activation analysis (NAA) and γ-ray counting have been used to measure the activity of 24 samples removed from the GALLEX radioactive Cr neutrino source. In 9.86% of the disintegrations, 51 Cr decays with the emission of a 320-keV γ-ray. Counting this γ-ray provides a direct means to obtain the disintegration rates of the Cr samples. Based upon these disintegration rates, the authors obtain a strength of 63.1 ± 1.0 PBq for the entire Cr source. The Cr source activity has also been obtained through measuring the 51 V content of each sample by means of NAA. 51 V is the decay daughter for all decay modes of 51 Cr. Through neutron bombardment, radioactive 52 V is produced, which decays with the emission of a 1,434-keV γ-ray. By counting this γ-ray from NAA, they obtain a disintegration rate of 62.1 ± 1.0 PBq for the entire source. These values are consistent with all other measurements of the source strength done at other GALLEX Laboratories

  17. Controlled Growth of Carbon Nanotubes on Micropatterned Au/Cr Composite Film and Field Emission from Their Arrays

    Science.gov (United States)

    Kamide, Koichi; Araki, Hisashi; Yoshino, Katsumi

    2003-12-01

    Carbon nanotube (CNT) arrays with a controlled density are prepared on a micropatterned Au/Cr composite film formed on a quartz glass plate by pyrolysis of Ni-phthalocyanine at 800°C. It is clarified from characteristic X-ray analyses for those samples that a catalytic Ni nanoparticle is not contained within the base of the whisker-like CNT in contrast to that of the bamboo-like CNT, suggesting that the growth process of the present novel CNT is incompatible with that of the bamboo-like CNT. In the Au/Cr composite film, both the Cr atomic content of approximately 30% and the presence of the Ni catalyst devoid of a particle-like shape are important factors for the growth of CNTs. Field emission from the novel CNT arrays exhibits a lower turn-on voltage and a higher current density compared with that from the bamboo-like arrays formed on a quartz plate.

  18. Evaluation of mechanical properties and nano-meso structures of 9–11%Cr ODS steels

    Energy Technology Data Exchange (ETDEWEB)

    Tanno, Takashi, E-mail: tanno.takashi@jaea.go.jp [Japan Atomic Energy Agency, Oarai, Ibaraki 311-1393 (Japan); Ohtsuka, Satoshi; Yano, Yasuhide; Kaito, Takeji [Japan Atomic Energy Agency, Oarai, Ibaraki 311-1393 (Japan); Oba, Yojiro; Ohnuma, Masato [National Institute for Materials Science, Tsukuba 305-1195 (Japan); Koyama, Shinichi; Tanaka, Kenya [Japan Atomic Energy Agency, Oarai, Ibaraki 311-1393 (Japan)

    2013-09-15

    Highlights: • We successfully manufactured 11Cr-ODS steels with residual α-ferrite controlled. • Dispersion conditions of nano oxide particles were quantitatively characterized. • Tungsten solid solution could improve only tensile strength of ODS steels at 973 K. • Oxide dispersion strengthening was dominant in creep strength of ODS steels at 973 K. -- Abstract: This study carried out mechanical tests and microstructural characterizations of several 9Cr and 11Cr-ODS tempered martensitic steels. From those results, the appropriate chemical composition range of 11Cr-ODS tempered martensitic steel was discussed from the viewpoint of high temperature strength improvement. It was shown that the residual α-ferrite fraction in 11Cr-ODS steel was successfully controlled to the same level as the 9Cr-ODS steel, which has excellent high temperature strength, by selecting the chemical compositions on the basis of the multi-component phase diagram. The tensile strength decreased with decreasing W content from 2.0 to 1.4 wt%. On the other hand, creep strength at 973 K did not degrade by the decreasing W content. Both tensile strength and creep strength increased with increasing population of the nano-sized oxide particles. Small angle X-ray scattering analysis revealed that titanium and excess oxygen contents were key parameters in order to improve the dispersion conditions of nano-sized oxide particles.

  19. Cr2O3-doped MOX fuel: doping and sintering atmosphere optimization

    International Nuclear Information System (INIS)

    Thomas, R.

    2013-01-01

    Optimal use of the Mixed Oxide (U,Pu)O 2 nuclear fuel in pressurized water reactors is mainly limited by the behavior of gaseous fission produced during irradiation. Within the MOX microstructure, the probability of fission gas release is increased by the presence of rich localized plutonium areas exhibiting a higher local burn-up. A solution consists in optimizing plutonium distribution within the industrial product and promoting the crystalline growth of the fuel grains. For this purpose, addition of chromium sesquioxide during the manufacturing process is currently considered. A previous thesis has shown that the best results are obtained for a Cr addition slightly greater than the solubility limit of Cr in (U,Pu)O 2 . In order to explain the enhanced plutonium homogeneity, the author highlighted the formation of PuCrO 3 precipitates at grain boundaries. A sintering model under reducing atmosphere, with chromium addition, was proposed. However, several points have to be more thoroughly investigated, especially regarding the solubility limit of chromium, as well as the optimal conditions of PuCrO 3 precipitates formation. In a first part, speciation of solubilized and precipitated chromium in the mixed oxide (U,Pu)O 2 is studied using electron probe microanalysis (EPMA) and X-ray absorption spectroscopy (XAS). It was shown that the oxidation state and the environment of soluble chromium within the (U,Pu)O 2 matrix do not depend on the oxygen partial pressure during sintering, neither on the plutonium content of the mixed oxide. However, both chemical nature of the precipitates and chromium solubility depend on the thermodynamic variable and on the plutonium content.Based on these results, a chromium solubility model in the mixed oxide (U,Pu)O 2-x was built using the law of mass action governing solubility equilibrium. This model is described as a function of the plutonium content (y) of the solid solution (U 1-y Pu y )O 2-x (y = 0,11; 0,275 et 1) and in the

  20. CrCuAgN PVD nanocomposite coatings: Effects of annealing on coating morphology and nanostructure

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Xingguang, E-mail: xingguangliu1@gmail.com [Department of Materials Science and Engineering, Sir Robert Hadfield Building, The University of Sheffield, Mappin Street, Sheffield, S1 3JD (United Kingdom); Iamvasant, Chanon, E-mail: ciamvasant1@sheffield.ac.uk [Department of Materials Science and Engineering, Sir Robert Hadfield Building, The University of Sheffield, Mappin Street, Sheffield, S1 3JD (United Kingdom); Liu, Chang, E-mail: chang.liu@sheffield.ac.uk [Department of Materials Science and Engineering, Sir Robert Hadfield Building, The University of Sheffield, Mappin Street, Sheffield, S1 3JD (United Kingdom); Matthews, Allan, E-mail: allan.matthews@manchester.ac.uk [Pariser Building - B24 ICAM, School of Materials, The University of Manchester, Manchester, M13 9PL (United Kingdom); Leyland, Adrian, E-mail: a.leyland@sheffield.ac.uk [Department of Materials Science and Engineering, Sir Robert Hadfield Building, The University of Sheffield, Mappin Street, Sheffield, S1 3JD (United Kingdom)

    2017-01-15

    Highlights: • Coatings with nitrogen content up to 16 at.% exhibit a metallic Cr solid solution, even after post-coat annealing at 300 °C and 500 °C. • At higher N/Cr atomic ratios (approaching Cr{sub 2}N stoichiometry), chromium was still inclined to exist in solid solution with nitrogen, rather than as a ceramic nitride phase, even after annealing at 500 °C. • Transportation of Cu and Ag to the surface depends on annealing temperature, annealing duration, nitrogen concentration and ‘global’ Cu + Ag concentration. • Incorporation of copper appears to be a powerful strategy to enhance Ag mobility at low concentration (∼3 at.% Ag in this study) under moderately high service temperature. • A significant decrease in friction coefficient was obtained at room temperature after annealing, or during sliding wear testing at elevated temperature. - Abstract: CrCuAgN PVD nanocomposite coatings were produced using pulsed DC unbalanced magnetron sputtering. This investigation focuses on the effects of post-coat annealing on the surface morphology, phase composition and nanostructure of such coatings. In coatings with nitrogen contents up to 16 at.%, chromium exists as metallic Cr with N in supersaturated solid solution, even after 300 °C and 500 °C post-coat annealing. Annealing at 300 °C did not obviously change the phase composition of both nitrogen-free and nitrogen-containing coatings; however, 500 °C annealing resulted in significant transformation of the nitrogen-containing coatings. The formation of Ag aggregates relates to the (Cu + Ag)/Cr atomic ratio (threshold around 0.2), whereas the formation of Cu aggregates relates to the (Cu + Ag + N)/Cr atomic ratio (threshold around 0.5). The primary annealing-induced changes were reduced solubility of Cu, Ag and N in Cr, and the composition altering from a mixed ultra-fine nanocrystalline and partly amorphous phase constitution to a coarser, but still largely nanocrystalline structure. It was also

  1. Phase transitions of doped carbon in CrCN coatings with modified mechanical and tribological properties via filtered cathodic vacuum arc deposition

    International Nuclear Information System (INIS)

    Guan, J.J.; Wang, H.Q.; Qin, L.Z.; Liao, B.; Liang, H.; Li, B.

    2017-01-01

    The CrCN coatings were fabricated onto Si (1 1 1) wafers and SUS304 stainless steel plates using filtered cathodic vacuum arc deposition (FCVAD) technique under different flow ratios of N_2/C_2H_2 gas mixture. The morphology, crystalline structure and chemical composition of the coatings were characterized. It was found that the grain size reduce with increasing carbon content, which makes the CrCN coatings refined and smooth. The quasi-one-dimensional carbolite phase was also found in CrN host lattice with C_2H_2 content ranging from 5% to 20%, and it will be evolved into amorphous carbon and amorphous CN_x phases as C_2H_2 content exceeds 20%. Moreover, we examined the mechanical and tribological properties of the CrCN coatings, and the experimental results confirmed that the friction coefficient of the coatings descend to the lowest value as 0.39 with 30% C_2H_2 content, due to the graphite (sp"2 C−C) phase embed in CrN host lattice; while the chromium carbon (Cr_3C_2) and diamond (sp"3 C−C) phases may give rise to the increase of the coating hardness with the highest value at 23.97 GPa under 20% C_2H_2 content.

  2. Phase transitions of doped carbon in CrCN coatings with modified mechanical and tribological properties via filtered cathodic vacuum arc deposition

    Science.gov (United States)

    Guan, J. J.; Wang, H. Q.; Qin, L. Z.; Liao, B.; Liang, H.; Li, B.

    2017-04-01

    The CrCN coatings were fabricated onto Si (1 1 1) wafers and SUS304 stainless steel plates using filtered cathodic vacuum arc deposition (FCVAD) technique under different flow ratios of N2/C2H2 gas mixture. The morphology, crystalline structure and chemical composition of the coatings were characterized. It was found that the grain size reduce with increasing carbon content, which makes the CrCN coatings refined and smooth. The quasi-one-dimensional carbolite phase was also found in CrN host lattice with C2H2 content ranging from 5% to 20%, and it will be evolved into amorphous carbon and amorphous CNx phases as C2H2 content exceeds 20%. Moreover, we examined the mechanical and tribological properties of the CrCN coatings, and the experimental results confirmed that the friction coefficient of the coatings descend to the lowest value as 0.39 with 30% C2H2 content, due to the graphite (sp2 Csbnd C) phase embed in CrN host lattice; while the chromium carbon (Cr3C2) and diamond (sp3 Csbnd C) phases may give rise to the increase of the coating hardness with the highest value at 23.97 GPa under 20% C2H2 content.

  3. Influence of Z-phase on long-term creep stability of martensitic 9-12% Cr steels

    Energy Technology Data Exchange (ETDEWEB)

    Danielsen, Hilmar K. [Technical Univ. of Denmark, Lyngby (Denmark). Dept. of Mechanical Engineering; Hald, John [DONG Energy A/S (Denmark); Vattenfall (Denmark)

    2010-07-01

    The long-term creep strength of the new generation of martensitic creep resistant 9-12%Cr steels since the well-known steel Grade 91 relies strongly on particle strengthening by fine Mn nitrides based on V and Nb. During long-term high-temperature exposures the Mn nitrides may be replaced by the thermodynamically more stable Z-phases (Cr(V,Nb)N) causing a breakdown in creep strength. Cr contents above 10.5% strongly accelerate Z-phase precipitation, which explains the lack of success for all attempts to develop martensitic creep resistant steels with high Cr content for oxidation protection. However 9%Cr steels do not seem to be affected by the Z-phase. Careful control of the Z-phase precipitation process has led to the design of experimental 12%Cr martensitic steels strengthened by fine Z-phase nitrides based on Nb or Ta. Such steels may again enable the combination of high strength and oxidation resistance in the same alloy. This opens a new pathway for further alloy development of the heat resistant martensitic steels. (orig.)

  4. Chromium (VI Induced Biochemical Changes and Gum Content in Cluster Bean (Cyamopsis tetragonoloba L. at Different Developmental Stages

    Directory of Open Access Journals (Sweden)

    Punesh Sangwan

    2013-01-01

    Full Text Available Chromium (Cr contamination by various industries and other activities is known to inhibit plants growth and development. The present study was conducted using pot experiments in a net house to determine the effect of Cr (VI on biochemical parameters such as photosynthetic pigments, reducing sugars, and important minerals at different stages of growth in leaves, stem, and roots of clusterbean, a multipurpose fodder crop including a source of guar gum. Guar gum content was estimated in seeds at maturity. All biochemical contents showed a great variation with respect to increase in Cr concentration at different stages of growth. The levels of K, Fe, and Zn decreased, while Cr and Na content increased with increase in Cr concentration. Cr induced toxicity in clusterbean appears at 0.5 mg Cr (VI Kg−1 soil with maximum inhibitory effect at 2 mg Cr (VI Kg−1 soil, where impaired sugar supply resulted in decreased guar gum synthesis and altered micronutrient content. The study reveals the possible role of these biochemical parameters in decreasing plant growth and development under heavy metal stress.

  5. Effect of composition and heat treatment on the phase formation of mechanically alloyed Cr-B and Mo-B powders

    International Nuclear Information System (INIS)

    Wu, H M; Hu, C J; Pai, K Y

    2009-01-01

    Blended elemental Cr-B and Mo-B powders in atomic ratio of 67:33, 50:50, and 20:80 were subjected to mechanical alloying up to 60 h and subsequent heat treatment to investigate effect of composition and heat treatment on the phase formation of Cr-B and Mo-B powders. It was studied by X-ray diffraction and differential thermal analysis. Mechanical alloying these powder mixtures for 60 h leads essentially to a amorphous structure except for the Mo 20 B 80 powder, which creates a partially amorphous MoB 4 structure. Annealing at lower temperatures relieves the strains cumulative in the milled powders and creates no new phase. The structures obtained after annealing the milled powders at higher temperature vary and depend on the overall composition of the powder mixtures. Annealing the milled Mo-B powders having greater Mo content ends up with a dissociation reaction at higher temperature.

  6. Precipitation Kinetics of Cr2N in High Nitrogen Austenitic Stainless Steel

    Institute of Scientific and Technical Information of China (English)

    SHI Feng; WANG Li-jun; CUI Wen-fang; LIU Chun-ming

    2008-01-01

    The precipitation behavior of Cr2N during isothermal aging in the temperature range from 700℃to 950℃ in Fe-18Cr-12Mn-0.48N(in mass percent)high nitrogen austenitic stainless steel,including morphology and content of precipitate,was investigated using optical microscopy,scanning electron microscopy,and transmission electron microscopy.The isothermal precipitation kinetics curve of Cr2N and the corresponding precipitation activation energy were obtained.The results show that Cr2N phase precipitates in a cellular way and its morphology is transformed from initial granular precipitates to lamellar ones in the cell with increasing aging time.The nose temperature of Cr2N precipitation is about 800℃,with a corresponding incubation period of 30 min,and the ceiling temperature of Cr2N precipitation is 950℃.The diffusion activation energy of Cr2N precipitation is 296 kJ/mol.

  7. Influence of the C content on the permeation of hydrogen in Fe alloys with low contents of C

    Directory of Open Access Journals (Sweden)

    I. Peñalva

    2016-12-01

    The experimental permeation results were analyzed using a non-linear least square fitting. The final resulting values of the permeability were paired off in order to determine the effect of the C content: pure Fe versus FeC, FeP versus FePC and Fe10%Cr versus Fe10%CrC. According to the results, the influence of the metallurgical composition of C in Fe alloys on the permeability of hydrogen is discussed together with the synergistic effects caused by the presence of P and Cr.

  8. Effect of genotype, Cr(III and Cr(VI on plant growth and micronutrient status in Silene vulgaris (Moench

    Directory of Open Access Journals (Sweden)

    A. E. Pradas-del-Real

    2013-06-01

    Full Text Available Chromium released into the environment from industrial activities has become an important environmental concern. Silene vulgaris has been proven to be tolerant to many heavy metals, so it is considered an interesting species in the revegetation and restoration of polluted soils, but no information is available about its response to Cr. The objective of this work was to study uptake and influence on plant growth of Cr(III and Cr(VI in six genotypes (four hermaphrodites and two females of S. vulgaris from different sites of Madrid (Spain. Plants were treated for 12 days with 60 µM of Cr(III or Cr(VI in semihydroponics. Dry weights, soil-plant analysis development values (SPAD reading with chlorophylls and micronutrient and total Cr concentrations were determined. Metal uptake was higher in presence of Cr(VI than of Cr(III and poorly translocated to the shoots. In both cases S. vulgaris did not show visual toxicity symptoms, biomass reduction, or differences among SPAD values as consequence of Cr additions. However genotypes SV36 and SV38 showed Fe and Mn imbalance. This is the first report on the relatively good performance of hermaphrodite and female S. vulgaris genotypes in Cr uptake and physiological traits, but further studies will be necessary to elucidate the mechanisms by which the gender may influence these variables. S. vulgaris presented high diversity at genotypic level; the treatment with hexavalent Cr increased the differences among genotypes so the use of cuttings from an homogeneous genotype seems to be an adequate method for the study of this species.

  9. Oxide scale formation of modified FeCrAl coatings exposed to liquid lead

    Energy Technology Data Exchange (ETDEWEB)

    Fetzer, Renate, E-mail: renate.fetzer@kit.edu [Karlsruhe Institute of Technology, P.O. Box 3640, 76021 Karlsruhe (Germany); Weisenburger, Alfons; Jianu, Adrian; Mueller, Georg [Karlsruhe Institute of Technology, P.O. Box 3640, 76021 Karlsruhe (Germany)

    2012-02-15

    Highlights: Black-Right-Pointing-Pointer Modified FeCrAl coatings show oxide scale formation when exposed to liquid lead. Black-Right-Pointing-Pointer Formation of thin Al-rich oxide scales is promoted by the presence of Y. Black-Right-Pointing-Pointer FeCrAlY with at least 8 wt.% Al forms thin Al-rich oxide scales. Black-Right-Pointing-Pointer For low Al content, thick multilayer Fe-based oxide scales are found. - Abstract: Modified FeCrAl coatings were studied with respect to their capability to form a thin protective oxide scale in liquid lead environment. They were manufactured by low pressure plasma spraying and GESA surface melting, thereby tuning the Al content. The specimens were exposed for 900 h to liquid lead containing 10{sup -6} and 10{sup -8} wt.% oxygen, respectively, at various temperatures from 400 to 550 Degree-Sign C. Threshold values for an Al content that guarantees the formation of thin protective Al-rich oxide scales are determined, dependent on the respective chromium content, on the presence of yttrium in the modified coating, and on the exposure conditions.

  10. Improvement of physico-mechanical properties of Mg–Zn nanoferrites via Cr{sup 3+} doping

    Energy Technology Data Exchange (ETDEWEB)

    Mansour, S.F., E-mail: salws_fahim@yahoo.com [Physics Department, Faculty of Science, Zagazig University, Zagazig (Egypt); Abdo, M.A., E-mail: mhmd_ahmd20@yahoo.com [Physics Department, Faculty of Science, Zagazig University, Zagazig (Egypt); El-Dek, S.I. [Materials Science and Nanotechnology Department, Faculty of Post graduate Studies for Advanced Sciences, (PSAS), Beni-Suef University, Beni-Suef (Egypt)

    2017-01-15

    A series of Mg{sub 0.8}Zn{sub 0.2}Cr{sub x}Fe{sub 2−x}O{sub 4} (0≤x≤0.025) nanoferrites were prepared by citrate–nitrate auto-combustion method. X-ray diffraction assured the formation of the ferrites in nanoscale and in single phase spinel structure. The magnetic and mechanical properties were investigated. All the elastic moduli values increase slowly and steadily with increasing Cr{sup 3+} content reaching the critical composition x=0.02. The magnetic parameters increased up to x=0.02 and then decreased with further Cr doping. Versatile applications were recommended owing to the porous nature of the nanoferrites. - Highlights: • Citrate–nitrate technique was successful in producing nanoparticles of Mg–Zn–Cr ferrites. • Experimental and theoretical lattice constants are in good agreement. • All elastic moduli increased with rising Cr doping content up to x=0.02. • An increment in M{sub s} and H{sub c} values was observed up to x=0.02. • Porous spongy grains recommend the use of the nanoferrite in catalytic applications.

  11. Effect of the edaphic factors and metal content in soil on the diversity of Trichoderma spp.

    Science.gov (United States)

    Racić, Gordana; Körmöczi, Péter; Kredics, László; Raičević, Vera; Mutavdžić, Beba; Vrvić, Miroslav M; Panković, Dejana

    2017-02-01

    Influence of edaphic factors and metal content on diversity of Trichoderma species at 14 different soil sampling locations, on two depths, was examined. Forty-one Trichoderma isolates from 14 sampling sites were determined as nine species based on their internal transcribed spacer (ITS) sequences. Our results indicate that weakly alkaline soils are rich sources of Trichoderma strains. Also, higher contents of available K and P are connected with higher Trichoderma diversity. Increased metal content in soil was not inhibiting factor for Trichoderma species occurrence. Relationship between these factors was confirmed by locally weighted sequential smoothing (LOESS) nonparametric smoothing analysis. Trichoderma strain (Szeged Microbiology Collection (SZMC) 22669) from soil with concentrations of Cr and Ni above remediation values should be tested for its potential for bioremediation of these metals in polluted soils.

  12. The MSFR as a flexible CR reactor: the viewpoint of safety

    Energy Technology Data Exchange (ETDEWEB)

    Fiorina, C.; Cammi, A. [Politecnico di Milano, Via La Masa 34, 20136 Milan (Italy); Franceschini, F. [Westinghouse Electric Company LL, 1000 Westinghouse Dr., Cranberry Township, PA 16066 (United States); Krepel, J. [Paul Scherrer Institut, PSI WEST, 5234 Villigen (Switzerland)

    2013-07-01

    In this paper, the possibility has first been discussed of using the liquid-fuelled Molten Salt Fast Reactor (MSFR) as a flexible conversion ratio (CR) reactor without design modification. By tuning the reprocessing rate it is possible to determine the content of fission products in the core, which in turn can significantly affect the neutron economy without incurring in solubility problems. The MSFR can thus be operated as U-233 breeder (CR>1), iso-breeder (CR=1) and burner reactor (CR<1). In particular a 40 year doubling time can be achieved, as well as a considerable Transuranics and MA (minor actinide) burning rate equal to about 150 kg{sub HN}/GWE-yr. The safety parameters of the MSFR have then been evaluated for different fuel cycle strategies. Th use and a softer spectrum combine to give a strong Doppler coefficient, one order of magnitude higher compared to traditional fast reactors (FRs). The fuel expansion coefficient is comparable to the Doppler coefficient and is only mildly affected by core compositions, thus assisting the fuel cycle flexibility of the MSFR. βeff and generation time are comparable to the case of traditional FRs, if a static fuel is assumed. A notable reduction of βeff is caused by salt circulation, but a low value of this parameter is a limited concern in the MSFR thanks to the lack of a burnup reactivity swing and of positive feedbacks. A simple approach has also been developed to evaluate the MSFR capabilities to withstand all typical double-fault accidents, for different fuel cycle options.

  13. Exploring the Content of Instrumental Lessons and Gender Relations in Australian Higher Education

    Science.gov (United States)

    Zhukov, Katie

    2008-01-01

    This observational study analysed the lesson content of 24 instrumental lessons (piano, strings and winds) using a gender-balanced sample (equal numbers of male/female teachers and students) from five Australian higher education institutions to ascertain the priorities of topics in advanced applied music lessons in the Western Classical tradition.…

  14. Phase transitions of doped carbon in CrCN coatings with modified mechanical and tribological properties via filtered cathodic vacuum arc deposition

    Energy Technology Data Exchange (ETDEWEB)

    Guan, J.J. [Faculty of Materials and Energy, Southwest University, Chongqing 400715 (China); Wang, H.Q. [College of Nuclear Science and Technology, Beijing Normal University, Beijing 100875 (China); Qin, L.Z., E-mail: qin8394@163.com [Faculty of Materials and Energy, Southwest University, Chongqing 400715 (China); Liao, B.; Liang, H. [College of Nuclear Science and Technology, Beijing Normal University, Beijing 100875 (China); Li, B. [Faculty of Materials and Energy, Southwest University, Chongqing 400715 (China)

    2017-04-15

    The CrCN coatings were fabricated onto Si (1 1 1) wafers and SUS304 stainless steel plates using filtered cathodic vacuum arc deposition (FCVAD) technique under different flow ratios of N{sub 2}/C{sub 2}H{sub 2} gas mixture. The morphology, crystalline structure and chemical composition of the coatings were characterized. It was found that the grain size reduce with increasing carbon content, which makes the CrCN coatings refined and smooth. The quasi-one-dimensional carbolite phase was also found in CrN host lattice with C{sub 2}H{sub 2} content ranging from 5% to 20%, and it will be evolved into amorphous carbon and amorphous CN{sub x} phases as C{sub 2}H{sub 2} content exceeds 20%. Moreover, we examined the mechanical and tribological properties of the CrCN coatings, and the experimental results confirmed that the friction coefficient of the coatings descend to the lowest value as 0.39 with 30% C{sub 2}H{sub 2} content, due to the graphite (sp{sup 2} C−C) phase embed in CrN host lattice; while the chromium carbon (Cr{sub 3}C{sub 2}) and diamond (sp{sup 3} C−C) phases may give rise to the increase of the coating hardness with the highest value at 23.97 GPa under 20% C{sub 2}H{sub 2} content.

  15. Dephosphorization of melts with chromium content

    International Nuclear Information System (INIS)

    Motloch, Z.

    1985-01-01

    A survey is given of the results of laboratory and pilot plant research into the dephosphorization of high-chromium melts reported in the literature, mostly Japanese. The use of high-alloy chromium and chromium-nickel steels in nuclear power engineering showed the negative impact of phosphorus on stress corrosion at high temperatures and on the development of cracks under overlays during welding. For a number of years attention is therefore being devoted to the attainment of a low phosphorus content in these steels. Current dephosphorization methods may be divided into oxidation and reduction methods. Oxidation dephosphorization may be carried out using synthetic mixtures: in the use of CaO-FeCl 2 , BaO-BaCl 2 -Cr 2 O 3 , Li 2 CO 3 -CaO-CaF 2 -FeO and Na 2 CO 3 /K 2 CO 3 -NaCl/KCl/KF/CaCl 2 /FeCl 2 a high initial C content, low content of Cr and Si and a low temperature of the melt are advantageous for dephosphorization. Experiments have also been made with dephosphorization in a bottom-blown oxygen converter and in an AOD converter. The most frequently used substances for reduction dephosphorization are calcium and calcium carbide; the best C content ranges between 0.5 and 1.8%, a high Cr content and a high bath temperature are also advantageous. The use of the reduction procedure is greatly limited by the generation of highly toxic phosphine. Another tested method - electroslag remelting is not suitable for commercial application for its economic exactingness. (A.K.)

  16. Structural, morphological, and optical characterizations of Mo, CrN and Mo:CrN sputtered coatings for potential solar selective applications

    Science.gov (United States)

    Ibrahim, Khalil; Mahbubur Rahman, M.; Taha, Hatem; Mohammadpour, Ehsan; Zhou, Zhifeng; Yin, Chun-Yang; Nikoloski, Aleksandar; Jiang, Zhong-Tao

    2018-05-01

    Mo, CrN, and Mo:CrN sputtered coatings synthesized onto silicon Si(100) substrates were investigated as solar selective surfaces and their potential applications in optical devices. These coatings were characterized using XRD, SEM, UV-vis, and FTIR techniques. XRD investigation, showed a change in CrN thin film crystallite characteristic due to Mo doping. Compared to the CrN coating, the Mo:CrN film has a higher lattice parameter and lower grain size of 4.19 nm and 106.18 nm, respectively. FESEM morphology confirmed the decrement in Mo:CrN crystal size due to Mo doping. Optical analysis showed that in the visible range of the solar spectrum, the CrN coatings exhibit the highest solar absorptance of 66% while the lowest thermal emittance value of 5.67 was recorded for the CrN coating doped with Mo. Consequently, the highest solar selectivity of 9.6, and the energy band-gap of 2.88 eV were achieved with the Mo-doped CrN coatings. Various optical coefficients such as optical absorption coefficient, refractive index, extinction coefficient, real and imaginary parts of dielectric constants, and energy loss functions of these coatings were also estimated from the optical reflectance data recorded in the wavelength range of 190-2300 nm.

  17. Influence of Z-phase on long-term creep stability of martensitic 9-12%Cr steels

    Energy Technology Data Exchange (ETDEWEB)

    Hald, J. [DONG Energy (Denmark)]|[Vattenfall Europe AG, Berlin (Germany)]|[DTU Mechanical Engineering (Denmark); Danielsen, H.K. [DTU Mechanical Engineering (Denmark)

    2008-07-01

    The long-term creep strength of the new generation of martensitic creep resistant 9- 12% Cr steels since the well-known steel Grade 91 relies strongly on particle strengthening by fine MN nitrides based on V and Nb. During long-term hightemperature exposures the MN nitrides may be replaced by the thermodynamically more stable Z-phases (Cr(V,Nb)N) causing a breakdown in creep strength. Cr contents above 10.5% strongly accelerate Z-phase precipitation, which explains the lack of success for all attempts to develop martensitic creep resistant steels with high Cr content for oxidation protection. The Z-phase nucleation process by Cr-diffusion into pre-existing MN nitrides is rate controlling for the Z-phase transformation. More work is needed before effects of chemical composition on the nucleation process can be reliably modeled. Careful control of the Z-phase precipitation process has led to the design of experimental 12%Cr martensitic steels strengthened by Z-phase. Such steels may again enable the combination of high strength and oxidation resistance in the same alloy. This opens a new pathway for further alloy development of the heat resistant martensitic steels. (orig.)

  18. HIGH TEMPERATURE TENSILE PROPERTIES OF NEW FE-CR-MN DEVELOPED STEEL

    Directory of Open Access Journals (Sweden)

    M. Mahmoudiniya

    2017-03-01

    Full Text Available Nowadays, Ni-free austenitic stainless steels are being developed rapidly and high price of nickel is one of the most important motivations for this development. At present research a new FeCrMn steel was designed and produced based on Fe-Cr-Mn-C system. Comparative studies on microstructure and high temperature mechanical properties of  new steel and AISI 316 steel were done. The results showed that new FeCrMn developed steel has single austenite phase microstructure, and its tensile strength and toughness were higher than those of 316 steel at 25, 200,350 and 500°C. In contrast with 316 steel, the new FeCrMn steel did not show strain induced transformation and dynamic strain aging phenomena during tensile tests that represented higher austenite stability of new developed steel. Lower density and higher strength of the new steel caused higher specific strength in comparison with the 316 one that can be considered as an important advantage in structural applications but in less corrosive environment

  19. Millimeter-wave spectroscopy of CrC (X(3)Σ(-)) and CrCCH (X̃ (6)Σ(+)): Examining the chromium-carbon bond.

    Science.gov (United States)

    Min, J; Ziurys, L M

    2016-05-14

    Pure rotational spectroscopy of the CrC (X(3)Σ(-)) and CrCCH (X̃ (6)Σ(+)) radicals has been conducted using millimeter/sub-millimeter direct absorption methods in the frequency range 225-585 GHz. These species were created in an AC discharge of Cr(CO)6 and either methane or acetylene, diluted in argon. Spectra of the CrCCD were also recorded for the first time using deuterated acetylene as the carbon precursor. Seven rotational transitions of CrC were measured, each consisting of three widely spaced, fine structure components, arising from spin-spin and spin-rotation interactions. Eleven rotational transitions were recorded for CrCCH and five for CrCCD; each transition in these cases was composed of a distinct fine structure sextet. These measurements confirm the respective (3)Σ(-) and (6)Σ(+) ground electronic states of these radicals, as indicated from optical studies. The data were analyzed using a Hund's case (b) Hamiltonian, and rotational, spin-spin, and spin-rotation constants have been accurately determined for all three species. The spectroscopic parameters for CrC were significantly revised from previous optical work, while those for CrCCH are in excellent agreement; completely new constants were established for CrCCD. The chromium-carbon bond length for CrC was calculated to be 1.631 Å, while that in CrCCH was found to be rCr-C = 1.993 Å - significantly longer. This result suggests that a single Cr-C bond is present in CrCCH, preserving the acetylenic structure of the ligand, while a triple bond exists in CrC. Analysis of the spin constants suggests that CrC has a nearby excited (1)Σ(+) state lying ∼16 900 cm(-1) higher in energy, and CrCCH has a (6)Π excited state with E ∼ 4800 cm(-1).

  20. Rational construction of Z-scheme Ag_2CrO_4/g-C_3N_4 composites with enhanced visible-light photocatalytic activity

    International Nuclear Information System (INIS)

    Luo, Jin; Zhou, Xiaosong; Ma, Lin; Xu, Xuyao

    2016-01-01

    Highlights: • Novel visible-light driven Ag_2CrO_4/g-C_3N_4 composites were synthesized. • Ag_2CrO_4/g-C_3N_4 exhibited enhanced visible-light photocatalytic activity. • The reasons for the enhanced photocatalytic activity were revealed. - Abstract: Novel visible-light driven Z-scheme Ag_2CrO_4/g-C_3N_4 composites with different contents of Ag_2CrO_4 were fabricated by a facile chemical precipitation method and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), UV–vis diffuse reflectance spectroscopy (UV-vis DRS), photoluminescence (PL) spectroscopy and photoelectrochemical measurements. Compared with individual g-C_3N_4 and Ag_2CrO_4, the Ag_2CrO_4/g-C_3N_4 composites displayed much larger photocatalytic activities for the photocatalytic degradation of methyl orange (MO) solution at room temperature under visible light irradiation (λ > 420 nm). Importantly, the optimum photodegradation rate constant of the Ag_2CrO_4/g-C_3N_4 composite at a theoretical weight content of 8.0% Ag_2CrO_4 for the photodegradation of MO was 0.0068 min"−"1, which was 5.7 and 4.3 times higher than that of pure g-C_3N_4 and Ag_2CrO_4, respectively. Such enormous enhancement in photocatalytic performance was predominantly ascribed to the efficient separation and transfer of photogenerated electrons and holes at the Ag_2CrO_4/g-C_3N_4 interface imparted through the Z-scheme electron transfer. Furthermore, radical trap experiments depicted that both the holes and superoxide radical anions were thought to dominate oxidative species of the Ag_2CrO_4/g-C_3N_4 composite for MO degradation under visible light irradiation. Ultimately, a tentative Z-scheme photodegradation mechanism was proposed. This work may be useful for the rational design of new types of Z-scheme photocatalysts and provide some illuminate insights into the Z-scheme transfer mechanism for application in energy

  1. Enhanced photodegradation activity of methyl orange over Ag2CrO4/SnS2 composites under visible light irradiation

    International Nuclear Information System (INIS)

    Luo, Jin; Zhou, Xiaosong; Ma, Lin; Xu, Xuyao; Wu, Jingxia; Liang, Huiping

    2016-01-01

    Highlights: • Novel visible-light-driven Ag 2 CrO 4 /SnS 2 composites are synthesized. • Ag 2 CrO 4 /SnS 2 exhibits higher photocatalytic activity than pure Ag 2 CrO 4 and SnS 2 . • Ag 2 CrO 4 /SnS 2 exhibits excellent stability for the photodegradation of MO. • The possible photocatalytic mechanism was discussed in detail. - Abstract: Novel Ag 2 CrO 4 /SnS 2 composites were prepared by a simple chemical precipitation method and characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy, UV–vis diffuse reflectance spectroscopy and photoluminescence spectroscopy. The visible light photocatalytic tests showed that the Ag 2 CrO 4 /SnS 2 composites enhanced photocatalytic activities for the photodegradation of methyl orange (MO) under visible light irradiation (λ > 420 nm), and the optimum rate constant of Ag 2 CrO 4 /SnS 2 at a weight content of 1.0% Ag 2 CrO 4 for the degradation of MO was 2.2 and 1.5 times larger than that of pure Ag 2 CrO 4 and SnS 2 , respectively. The improved activity could be attributed to high separation efficiency of photogenerated electrons-hole pairs on the interface of Ag 2 CrO 4 and SnS 2 , which arised from the synergistic effect between Ag 2 CrO 4 and SnS 2 . Moreover, the possible photocatalytic mechanism with superoxide radical anions and holes species as the main reactive species in photocatalysis process was proposed on the basis of experimental results.

  2. Synthesis, characterization and stability of Cr(III) and Fe(III) hydroxides

    International Nuclear Information System (INIS)

    Papassiopi, N.; Vaxevanidou, K.; Christou, C.; Karagianni, E.; Antipas, G.S.E.

    2014-01-01

    Highlights: • Fe(III)–Cr(III) hydroxides enhance groundwater quality better than pure Cr(III) compounds. • Crystalline Cr(OH) 3 ·3H 2 O was unstable, with a solubility higher than 50 μg/l. • Amorphous Cr(OH) 3 (am) was stable with a solubility lower than 50 μg/l in the range 5.7 0.75 Cr 0.25 (OH) 3 , the stability region was extended to 4.8 3 ·xH 2 O whereas in the presence of iron the precipitate is a mixed Fe (1−x) Cr x (OH) 3 phase. In this study, we report on the synthesis, characterisation and stability of mixed (Fe x ,Cr 1−x )(OH) 3 hydroxides as compared to the stability of Cr(OH) 3 . We established that the plain Cr(III) hydroxide, abiding to the approximate molecular formula Cr(OH) 3 ·3H 2 O, was crystalline, highly soluble, i.e. unstable, with a tendency to transform into the stable amorphous hydroxide Cr(OH) 3 (am) phase. Mixed Fe 0.75 Cr 0.25 (OH) 3 hydroxides were found to be of the ferrihydrite structure, Fe(OH) 3 , and we correlated their solubility to that of a solid solution formed by plain ferrihydrite and the amorphous Cr(III) hydroxide. Both our experimental results and thermodynamic calculations indicated that mixed Fe(III)–Cr(III) hydroxides are more effective enhancers of groundwater quality, in comparison to the plain amorphous or crystalline Cr(III) hydroxides, the latter found to have a solubility typically higher than 50 μg/l (maximum EU permitted Cr level in drinking water), while the amorphous Cr(OH) 3 (am) phase was within the drinking water threshold in the range 5.7 0.75 Cr 0.25 (OH) 3 hydroxides studied were of extended stability in the 4.8 < pH < 13.5 range

  3. Microstructure and Room-Temperature Mechanical Properties of FeCrMoVTi x High-Entropy Alloys

    Science.gov (United States)

    Guo, Jun; Huang, Xuefei; Huang, Weigang

    2017-07-01

    FeCrMoVTi x ( x values represent the molar ratio, where x = 0, 0.5, 1.0, 1.5, and 2.0) high-entropy alloys were prepared by a vacuum arc melting method. The effects of Ti element on the microstructure and room-temperature mechanical properties of the as-cast FeCrMoVTi x alloys were investigated. The results show that the prepared alloys exhibited typical dendritic microstructure and the size of the microstructure became fine with increasing Ti content. The FeCrMoV alloy exhibited a single body-centered cubic structure (BCC1) and the alloys prepared with Ti element exhibited BCC1 + BCC2 mixed structure. The new BCC2 phase is considered as (Fe, Ti)-rich phase and was distributed in the dendrite region. With the increase of Ti content, the volume fraction of the BCC2 phase increased and its shape changed from a long strip to a network. For the FeCrMoV alloy, the fracture strength, plastic strain, and hardness reached as high as 2231 MPa, 28.2%, and 720 HV, respectively. The maximum hardness of 887 HV was obtained in the FeCrMoVTi alloy. However, the fracture strength, yield stress, and plastic strain of the alloys decreased continuously as Ti content increased. In the room-temperature compressive test, the alloys showed typical brittle fracture characteristics.

  4. Ceramide content is higher in type I compared to type II fibers in obesity and type 2 diabetes mellitus

    DEFF Research Database (Denmark)

    Kristensen, Ditte Bech; Prats Gavalda, Clara; Larsen, Steen

    2012-01-01

    This study investigated fiber-type-specific muscle ceramide content in obese subjects and type 2 diabetes patients. Two substudies, one which compared type 2 diabetes patients to both lean- and obese BMI-matched subjects and the other study which compared lean body-matched post-obese, obese......, and control subjects, were performed. A fasting blood sample was obtained and plasma insulin and glucose determined. A muscle biopsy was obtained from deltoideus and vastus lateralis, and fiber-type ceramide content was determined by fluorescence immunohistochemistry. Insulin sensitivity estimated by Quicki...... index was higher in lean compared to type 2 diabetes patients and obese controls. Also in control and post-obese subjects, a higher insulin sensitivity was observed compared to obese subjects. Ceramide content was consistently higher in type I than in type II muscle fibers and higher in deltoideus than...

  5. Solute transport and the prediction of breakaway oxidation in gamma + beta Ni-Cr-Al alloys

    Science.gov (United States)

    Nesbitt, J. A.; Heckel, R. W.

    1984-01-01

    The Al transport and the condition leading to breakaway oxidation during the cyclic oxidation of gamma + beta NiCrAl alloys have been studied. The Al concentration/distance profiles were measured after various cyclic oxidation exposures at 1200 C. It was observed that cyclic oxidation results in a decreasing Al concentration at the oxide/metal interface, maintaining a constant flux of Al to the Al2O3 scale. It was also observed that breakaway oxidation occurs when the Al concentration at the oxide/metal interface approaches zero. A numerical model was developed to simulate the diffusional transport of Al and to predict breakaway oxidation in gamma + beta NiCrAl alloys undergoing cyclic oxidation. In a comparison of two alloys with similar oxide spalling characteristics, the numerical model was shown to predict correctly the onset of breakaway oxidation in the higher Al-content alloy.

  6. Effect of titanium on the creep deformation behaviour of 14Cr-15Ni-Ti stainless steel

    Science.gov (United States)

    Latha, S.; Mathew, M. D.; Parameswaran, P.; Nandagopal, M.; Mannan, S. L.

    2011-02-01

    14Cr-15Ni-Ti modified stainless steel alloyed with additions of phosphorus and silicon is a potential candidate material for the future cores of Prototype Fast Breeder Reactor. In order to optimise the titanium content in this steel, creep tests have been conducted on the heats with different titanium contents of 0.18, 0.23, 0.25 and 0.36 wt.% at 973 K at various stress levels. The stress exponents indicated that the rate controlling deformation mechanism was dislocation creep. A peak in the variation of rupture life with titanium content was observed around 0.23 wt.% titanium and the peak was more pronounced at lower stresses. The variation in creep strength with titanium content was correlated with transmission electron microscopic investigations. The peak in creep strength exhibited by the material with 0.23 wt.% titanium is attributed to the higher volume fraction of fine secondary titanium carbide (TiC) precipitates.

  7. Effect of titanium on the creep deformation behaviour of 14Cr-15Ni-Ti stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Latha, S. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, Tamil Nadu 603 102 (India); Mathew, M.D., E-mail: mathew@igcar.gov.in [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, Tamil Nadu 603 102 (India); Parameswaran, P.; Nandagopal, M. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam, Tamil Nadu 603 102 (India); Mannan, S.L. [National Engineering College, Kovilpatti, Tamil Nadu 628 503 (India)

    2011-02-28

    14Cr-15Ni-Ti modified stainless steel alloyed with additions of phosphorus and silicon is a potential candidate material for the future cores of Prototype Fast Breeder Reactor. In order to optimise the titanium content in this steel, creep tests have been conducted on the heats with different titanium contents of 0.18, 0.23, 0.25 and 0.36 wt.% at 973 K at various stress levels. The stress exponents indicated that the rate controlling deformation mechanism was dislocation creep. A peak in the variation of rupture life with titanium content was observed around 0.23 wt.% titanium and the peak was more pronounced at lower stresses. The variation in creep strength with titanium content was correlated with transmission electron microscopic investigations. The peak in creep strength exhibited by the material with 0.23 wt.% titanium is attributed to the higher volume fraction of fine secondary titanium carbide (TiC) precipitates.

  8. Effect of titanium on the creep deformation behaviour of 14Cr-15Ni-Ti stainless steel

    International Nuclear Information System (INIS)

    Latha, S.; Mathew, M.D.; Parameswaran, P.; Nandagopal, M.; Mannan, S.L.

    2011-01-01

    14Cr-15Ni-Ti modified stainless steel alloyed with additions of phosphorus and silicon is a potential candidate material for the future cores of Prototype Fast Breeder Reactor. In order to optimise the titanium content in this steel, creep tests have been conducted on the heats with different titanium contents of 0.18, 0.23, 0.25 and 0.36 wt.% at 973 K at various stress levels. The stress exponents indicated that the rate controlling deformation mechanism was dislocation creep. A peak in the variation of rupture life with titanium content was observed around 0.23 wt.% titanium and the peak was more pronounced at lower stresses. The variation in creep strength with titanium content was correlated with transmission electron microscopic investigations. The peak in creep strength exhibited by the material with 0.23 wt.% titanium is attributed to the higher volume fraction of fine secondary titanium carbide (TiC) precipitates.

  9. Liquidus projection of the Nb-Cr-Al system near the Al3(Nb,Cr) + Cr(Al,Nb) eutectic region

    International Nuclear Information System (INIS)

    Souza, S.A.; Ferrandini, P.L.; Nunes, C.A.; Coelho, A.A.; Caram, R.

    2006-01-01

    The system Nb-Cr-Al was investigated in the region near the Al 3 (Nb,Cr) + Cr(Al,Nb) eutectic and the liquidus projection of that region was determined based on the microstructural characterization of arc melted alloys. The characterization utilized scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), differential thermal analysis (DTA) and X-ray diffraction (XRD). The results allowed one to determine three primary solidification liquidus surfaces ((Cr,Al) 2 Nb, Cr(Al,Nb) and Al 3 (Nb,Cr)), that are originated from the binary systems Cr-Nb, Cr-Al and Al-Nb. It is proposed the occurrence of the invariant reaction L + (Cr,Al) 2 Nb ↔ Al 3 (Nb,Cr) + Cr(Al,Nb) and of a point of minimum, which involves a three phase reaction, L ↔ Al 3 (Nb,Cr) + Cr(Al,Nb). All alloys studied showed formation of the Al 3 (Nb,Cr) + Cr(Al,Nb) eutectic as the last solidification step with Al(Nb)Cr 2 precipitating from Cr(Al,Nb)

  10. Cr6+-containing phases in the system CaO-Al2O3-CrO42--H2O at 23 °C

    Science.gov (United States)

    Pöllmann, Herbert; Auer, Stephan

    2012-01-01

    Synthesis and investigation of lamellar calcium aluminium hydroxy salts was performed to study the incorporation of chromate ions in the interlayer of lamellar calcium aluminium hydroxy salts. Different AFm-phases (calcium aluminate hydrate with alumina, ferric oxide, mono-anion phase) containing chromate were synthesized. These AFm-phases belong to the group of layered double hydroxides (LDHs). 3CaO·Al2O3·CaCrO4·nH2O and C3A·1/2Ca(OH)2·1/2CaCrO4·12H2O were obtained as pure phases and their different distinct interlayer water contents and properties determined. Solid solution of chromate-containing phases and tetracalcium-aluminate-hydrate (TCAH) were studied. The uptake of chromate into TCAH from solutions was proven. Chromate contents in solution decrease to <0.2 mg/l.

  11. [Structure and luminescence properties of Ga2O3 : Cr3+ by Al doping].

    Science.gov (United States)

    Wang, Xian-Sheng; Wan, Min-Hua; Wang, Yin-Hai; Zhao, Hui; Hu, Zheng-Fa; Li, Hai-Ling

    2013-11-01

    The Al doping gallate phosphor (Ga(1-x)Al(x))2O3 : Cr3+ (x = 0, 0.1, 0.2, 0.3, 0.4, 0.5) was synthesized by a high temperature solid-state reaction method. The X-ray diffractions show that the phase of the phosphors remains to be Ga2 O3 structure with increase in the contents of Al3+ ion. Beside, the fact that the X-ray diffraction peak shifts towards big angles with increasing Al3+ ions content shows that Al3+ ions entered the Ga2 O3 lattice. The peaks of the excitation spectra located at 258, 300, 410 and 550 nm are attributed to the band to band transition of the matrix, charge transfer band transition, and 4A2 --> 4T1 and 4A2 --> 4T2 transition of Cr3+ ions, respectively. Those excitation spectrum peak positions show different degrees of blue shift with the increase in the Al3+ ions content. The blue shift of the first two peaks are due to the band gap energy of substrate and the electronegativity between Cr3+ ions and ligands increasing, respectively. The blue shift of the energy level transition of Cr3+ ion is attributed to crystal field strength increasing. The Cr3+ ion luminescence changes from a broadband emission to a narrow-band emission with Al3+ doping, because the emission of Cr3+ ion changed from 4 T2 --> 4A2 to 2E --> 4A2 transition with the crystal field change after Al3+ ions doping. The Al3+ ions doping improved the long afterglow luminescence properties of samples, and the sample showed a longer visible near infrared when Al3+ ions content reaches 0.5. The thermoluminescence curve shows the sample with suitable trap energy level, and this is also the cause of the long afterglow luminescence materials.

  12. Amorphization of C-implanted Fe(Cr) alloys

    International Nuclear Information System (INIS)

    Knapp, J.A.; Follstaedt, D.M.; Sorensen, N.R.; Pope, L.E.

    1991-01-01

    The amorphous phase formed by implanting C into Fe alloyed with Cr, which is a prototype for the amorphous phase formed by implanting C into stainless steels, is compared to that formed by implanting C and Ti into Fe and steels. The composition range of the phase has been examined; higher Cr and C concentrations are required than needed with Ti and C. The friction and wear benefits obtained by implanting stainless steels with C only do not persist for the long durations and high wear loads found with Ti and C. However, the amorphous Fe-Cr-C alloys exhibit good aqueous corrosion resistance. (orig.)

  13. Distribution coefficients of 134Cs, 60Co, 65Zn and 51Cr in different contaminated soils affected by organic waste disposal

    International Nuclear Information System (INIS)

    Metwally, E.

    2003-01-01

    Batch adsorption experiments were conducted with mixtures of solutes of different concentrations of some radionuclides as 1 34Sc, 6 0Co, 6 5Zn and 5 1Cr, in five different soils. The soils varied in their organic matter source and content due to prolonged irrigation with primary treated sewage effluent or untreated industrial wastewater. the distribution coefficients (K d ) were measured at different equilibrium times namely, 2, 24, 48, 72, 144 and 336 h. statistical correlation and curve fittings indicated that metal sorption into soils was influenced by the presence of clays, organic matter content and hydrous oxides of Fe and Mn. The highest log K d values were obtained in case of Cs in all investigated soils with a general mean of 1.878 0.28. Log K d for Cr exhibited a higher values than those did for at any tested soil (general mean 1.675 .33 and 1.658 0.24 for Cr and Co respectively). Zinc had the lowest log K d values, indicating that Cs is highly retained in soil than other tested elements and Zn is relatively mobile in soil than other tested elements. The investigated elements retention in soil could be arranged in the following order: Cs > Cr > Co > Zn. Soils enriched in organic matter exhibited the highest sorption caption capacity for all tested metals. Variability in the distribution coefficient due to soils and metals interactions were discussed

  14. Heavy metal contents and transfer capacities of Phragmites australis and Suaeda salsa in the Yellow River Delta, China

    Science.gov (United States)

    Zhang, Shuai; Bai, Junhong; Wang, Wei; Huang, Laibing; Zhang, Guangliang; Wang, Dawei

    2018-04-01

    Plant samples including roots, stems and leaves of Phragmites australis and Suaeda salsa were collected in the short-term flooding and tidal flooding wetlands of the Yellow River Delta of China. Six heavy metals (e.g., As, Cd, Cr, Cu, Pb, and Zn) were measured in roots, stems and leaves of each plant species using inductively coupled plasma atomic absorption spectrometry (ICP-AAS) to investigate the levels, and transfer capabilities of heavy metals in these two plant species. Our results showed that in the tidal flooding wetlands, the contents of As, Cr and Cd in roots of Phragmites australis and Suaeda salsa were higher than those in their stems and leaves. Suaeda salsa showed higher contents of Pb and Zn in leaves than those in roots and stems, whereas lower levels of Pb and Zn were observed in Phragmites australis. In the short-term flooding wetlands, heavy metal contents exhibited a big difference between different tissues of Phragmites australis and Suaeda salsa, and both plant species showed higher levels of Pb and Zn in leaves. Suaeda salsa roots enriched more As and Cd, whereas higher enrichment levels were observed in Phragmites australis leaves, which indicated different transfer capacities of these two wetland plants. The transfer factors for stems and leaves of Phragmites australis in the tidal flooding wetlands significantly differed from those in the short-term flooding wetlands, however, no significant differences in transfer factors for stems and leaves of Suaeda salsa were observed between these two types of wetlands.

  15. Effect of chemical composition of Ni-Cr dental casting alloys on the bonding characterization between porcelain and metal.

    Science.gov (United States)

    Huang, H-H; Lin, M-C; Lee, T-H; Yang, H-W; Chen, F-L; Wu, S-C; Hsu, C-C

    2005-03-01

    The purpose of this study was to investigate the influence of chemical composition of Ni-Cr dental casting alloys on the bonding behaviour between porcelain and metal. A three-point bending test was used to measure the fracture load of alloy after porcelain firing. A scanning electron microscope, accompanied by an energy dispersion spectrometer, was used to analyse the morphology and chemical composition of the fracture surface. An X-ray photoelectron spectrometer and glow discharge spectrometer were used to identify the structure and cross-sectional chemical composition, respectively, of oxide layers on Ni-Cr alloys after heat treatment at 990 degrees C for 5 min. Results showed that the oxide layers formed on all Ni-Cr alloys contained mainly Cr2O3, NiO, and trace MoO3. The Ni-Cr alloy with a higher Cr content had a thicker oxide layer, as well as a weaker bonding behaviour of porcelain/metal interface. The presence of Al (as Al2O3) and Be (as BeO) on the oxide layer suppressed the growth of the oxide layer, leading to a better porcelain/metal bonding behaviour. However, the presence of a small amount of Ti (as TiO2) on the oxide layer did not have any influence on the bonding behaviour. The fracture propagated along the interface between the opaque porcelain and metal, and exhibited an adhesive type of fracture morphology.

  16. CoCrMo alloy vs. UHMWPE Particulate Implant Debris Induces Sex Dependent Aseptic Osteolysis Responses In Vivo using a Murine Model

    Science.gov (United States)

    Landgraeber, Stefan; Samelko, Lauryn; McAllister, Kyron; Putz, Sebastian; Jacobs, Joshua.J.; Hallab, Nadim James

    2018-01-01

    Background: The rate of revision for some designs of total hip replacements due to idiopathic aseptic loosening has been reported as higher for women. However, whether this is environmental or inherently sex-related is not clear. Objective: Can particle induced osteolysis be sex dependent? And if so, is this dependent on the type of implant debris (e.g. metal vs polymer)? The objective of this study was to test for material dependent inflammatory osteolysis that may be linked to sex using CoCrMo and implant grade conventional polyethylene (UHMWPE), using an in vivo murine calvaria model. Methods: Healthy 12 week old female and male C57BL/6J mice were treated with UHMWPE (1.0um ECD) or CoCrMo particles (0.9um ECD) or received sham surgery. Bone resorption was assessed by micro-computed tomography, histology and histomorphometry on day 12 post challenge. Results: Female mice that received CoCrMo particles showed significantly more inflammatory osteolysis and bone destruction compared to the females who received UHMWPE implant debris. Moreover, females challenged with CoCrMo particles exhibited 120% more inflammatory bone loss compared to males (p<0.01) challenged with CoCrMo implant debris (but this was not the case for UHMWPE particles). Conclusion: We demonstrated sex-specific differences in the amount of osteolysis resulting from CoCrMo particle challenge. This suggests osteo-immune responses to metal debris are preferentially higher in female compared to male mice, and supports the contention that there may be inherent sex related susceptibility to some types of implant debris. PMID:29785221

  17. Ion irradiation effects on high purity bcc Fe and model FeCr alloys

    International Nuclear Information System (INIS)

    Bhattacharya, Arunodaya

    2014-01-01

    FeCr binary alloys are a simple representative of the reduced activation ferritic/martensitic (F-M) steels, which are currently the most promising candidates as structural materials for the sodium cooled fast reactors (SFR) and future fusion systems. However, the impact of Cr on the evolution of the irradiated microstructure in these materials is not well understood in these materials. Moreover, particularly for fusion applications, the radiation damage scenario is expected to be complicated further by the presence of large quantities of He produced by the nuclear transmutation (∼ 10 appm He/dpa). Within this context, an elaborate ion irradiation study was performed at 500 C on a wide variety of high purity FeCr alloys (with Cr content ranging from ∼ 3 wt.% to 14 wt.%) and a bcc Fe, to probe in detail the influence of Cr and He on the evolution of microstructure. The irradiations were performed using Fe self-ions, in single beam mode and in dual beam mode (damage by Fe ions and co-implantation of He), to separate ballistic damage effect from the impact of simultaneous He injection. Three different dose ranges were studied: high dose (157 dpa, 17 appm He/dpa for the dual beam case), intermediate dose (45 dpa, 57 appm He/dpa for dual beam case) and in-situ low dose (0.33 dpa, 3030 appm He/dpa for the dual beam case). The experiments were performed at the JANNuS triple beam facility and dual beam in situ irradiation facility at CEA-Saclay and CSNSM, Orsay respectively. The microstructure was principally characterized by conventional TEM, APT and EDS in STEM mode. The main results are as follows: 1) A comparison of the cavity microstructure in high dose irradiated Fe revealed strong swelling reduction by the addition of He. It was achieved by a drastic reduction in cavity sizes and an increased number density. This behaviour was observed all along the damage depth, up to the damage peak. 2) Cavity microstructure was also studied in the dual beam high dose

  18. A mHealth cardiac rehabilitation exercise intervention: findings from content development studies

    Directory of Open Access Journals (Sweden)

    Pfaeffli Leila

    2012-05-01

    Full Text Available Abstract Background Involving stakeholders and consumers throughout the content and study design ensures interventions are engaging and relevant for end-users. The aim of this paper is to present the content development process for a mHealth (mobile phone and internet-based cardiac rehabilitation (CR exercise intervention. Methods An innovative mHealth intervention was developed with patient input using the following steps: conceptualization, formative research, pre-testing, and pilot testing. Conceptualization, including theoretical and technical aspects, was undertaken by experts. For the formative component, focus groups and interviews with cardiac patients were conducted to discuss their perceptions of a mHealth CR program. A general inductive thematic approach identified common themes. A preliminary library of text and video messages were then developed. Participants were recruited from CR education sessions to pre-test and provide feedback on the content using an online survey. Common responses were extracted and compiled. An iterative process was used to refine content prior to pilot testing and conduct of a randomized controlled trial. Results 38 CR patients and 3 CR nurses participated in the formative research and 20 CR patients participated in the content pre-testing. Participants perceived the mHealth program as an effective approach to inform and motivate patients to exercise. For the qualitative study, 100% (n = 41 of participants thought it to be a good idea, and 11% of participants felt it might not be useful for them, but would be for others. Of the 20 participants who completed the online survey, 17 out of 20 (85% stated they would sign up to a program where they could receive information by video messages on a website, and 12 out of 20 (60% showed interest in a texting program. Some older CR patients viewed technology as a potential barrier as they were unfamiliar with text messaging or did not have mobile phones. Steps to

  19. Effects of Bond Coating on NiCrBSi-Mo Composite Functional Coating Properties in Plasma Spraying NiCrBSi-Mo/Ni Coating

    OpenAIRE

    DU Ji-yu; LI Fang-yi; LU Hai-yang; SHANG Jian-tong; LI Zhen

    2017-01-01

    Nickel-based bond coating and composite functional coating were sprayed on leaf blade steel material FV520B successively by using air plasma spraying system. NiCrBSi-Mo powder deposition rate, coating porosity, bonding strength and surface hardness were tested. The results indicate that, for the NiCrBSi-Mo/Ni coating, bond coating with 180-220μm thickness can improve NiCrBSi-Mo powder deposition rate while the surface coating with lower porosity, higher bonding strength and high hardness is p...

  20. Total Contents and Sequential Extraction of Heavy Metals in Soils Irrigated with Wastewater, Akaki, Ethiopia

    Science.gov (United States)

    Fitamo, Daniel; Itana, Fisseha; Olsson, Mats

    2007-02-01

    The Akaki River, laden with untreated wastes from domestic, industrial, and commercial sources, serves as a source of water for irrigating vegetable farms. The purpose of this study is to identify the impact of waste-water irrigation on the level of heavy metals and to predict their potential mobility and bioavailability. Zn and V had the highest, whereas Hg the lowest, concentrations observed in the soils. The average contents of As, Co, Cr, Cu, Ni, Zn, V, and Hg of both soils; and Pb and Se from Fluvisol surpassed the mean + 2 SD of the corresponding levels reported for their uncontaminated counterparts. Apparently, irrigation with waste water for the last few decades has contributed to the observed higher concentrations of the above elements in the study soils (Vertisol and Fluvisol) when compared to uncontaminated Vertisol and Fluvisol. On the other hand, Vertisol accommodated comparatively higher average levels of Cr, Cu, Ni, Zn, etc V, and Cd, whereas high contents of Pb and Se were observed in Fluvisol. Alternatively, comparable levels of Co and Hg were found in either soil. Except for Ni, Cr, and Cd in contaminated Vertisol, heavy metals in the soils were not significantly affected by the depth (0-20 and 30-50 cm). When the same element from the two soils was compared, the levels of Cr, Cu, Ni, Pb, Se, Zn, V, Cd at 0-20 cm; and Cr, Ni, Cu, Cd, and Zn at 30-50 cm were significantly different. Organic carbon (in both soils), CEC (Fluvisol), and clay (Vertisol) exhibited significant positive correspondences with the total heavy metal levels. Conversely, Se and Hg contents revealed perceptible associations with carbonate and pH. The exchangeable fraction was dominated by Hg and Cd, whereas the carbonate fraction was abounded with Cd, Pb, and Co. conversely, V and Pb displayed strong affinity to reducible fraction, where as Cr, Cu, Zn, and Ni dominated the oxidizable fraction. Cr, Hg, Se, and Zn (in both soils) showed preference to the residual fraction

  1. Aging properties studies in a Cu-Ag-Cr Alloy

    International Nuclear Information System (INIS)

    Jia, S.G.; Zheng, M.S.; Liu, P.; Ren, F.Z.; Tian, B.H.; Zhou, G.S.; Lou, H.F.

    2006-01-01

    A Cu-Ag-Cr alloy was produced by means of vacuum induction melting. The effects of aging processes on microhardness and conductivity of Cu-Ag-Cr alloy were studied. The microstructure of the alloy was examined using transmission electron microscope (TEM). Aging at 450 deg. C for 4 h, the alloy has an excellent combination of microhardness and conductivity, the microhardness and conductivity reach 132 HV and 80% IACS, respectively. The precipitates responsible for the age-hardening effect are fcc Cr. The fine and dispersed precipitates are fully coherent with the Cu matrix and make the Cu-Ag-Cr alloy possesses higher hardness and conductivity

  2. Photocatalytic CO2 reduction by Cr-substituted Ba2 (In2-xCrx)O5·(H2O)δ (0.04 ≤ x ≤ 0.60)

    KAUST Repository

    Yoon, Songhak; Gaul, Michael; Sharma, Sitansh; Son, Kwanghyo; Hagemann, Hans; Ziegenbalg, Dirk; Schwingenschlö gl, Udo; Widenmeyer, Marc; Weidenkaff, Anke

    2018-01-01

    Cr-substituted polycrystalline Ba2(In2-xCrx)O5·(H2O)δ powders (0.04 ≤ x ≤ 0.60) were synthesized by solid state reaction to investigate the relation of crystal structure, thermochemical, magnetic, and optical properties. The Cr-substitution results in an unit cell expansion and formation of the higher-symmetric tetragonal phase together with increased oxygen and hydrogen contents. Magnetic property measurements reveal that the diamagnetic pristine Ba2In2O5·(H2O)δ becomes magnetically ordered upon Cr-substitution. By UV–vis spectroscopy a gradual shift of the absorption-edge energy to lower values was observed. Numerical calculations showed that the observed bandgap narrowing was ascribed to the Cr induced states near the Fermi level. The correlation between the changes of crystal chemistry, magnetic, and optical properties of Cr-substituted Ba2(In2-xCrx)O5·(H2O)δ can be explained by the replacement of In by Cr. Consequently, an enhanced photocatalytic CO2 reduction activity was observed with increasing Cr substitution, compatible with the state-of-the-art high surface area TiO2 photocatalyst (P-25).

  3. Photocatalytic CO2 reduction by Cr-substituted Ba2 (In2-xCrx)O5·(H2O)δ (0.04 ≤ x ≤ 0.60)

    KAUST Repository

    Yoon, Songhak

    2018-02-09

    Cr-substituted polycrystalline Ba2(In2-xCrx)O5·(H2O)δ powders (0.04 ≤ x ≤ 0.60) were synthesized by solid state reaction to investigate the relation of crystal structure, thermochemical, magnetic, and optical properties. The Cr-substitution results in an unit cell expansion and formation of the higher-symmetric tetragonal phase together with increased oxygen and hydrogen contents. Magnetic property measurements reveal that the diamagnetic pristine Ba2In2O5·(H2O)δ becomes magnetically ordered upon Cr-substitution. By UV–vis spectroscopy a gradual shift of the absorption-edge energy to lower values was observed. Numerical calculations showed that the observed bandgap narrowing was ascribed to the Cr induced states near the Fermi level. The correlation between the changes of crystal chemistry, magnetic, and optical properties of Cr-substituted Ba2(In2-xCrx)O5·(H2O)δ can be explained by the replacement of In by Cr. Consequently, an enhanced photocatalytic CO2 reduction activity was observed with increasing Cr substitution, compatible with the state-of-the-art high surface area TiO2 photocatalyst (P-25).

  4. Photocatalytic CO2 reduction by Cr-substituted Ba2(In2-xCrx)O5·(H2O)δ (0.04 ≤ x ≤ 0.60)

    Science.gov (United States)

    Yoon, Songhak; Gaul, Michael; Sharma, Sitansh; Son, Kwanghyo; Hagemann, Hans; Ziegenbalg, Dirk; Schwingenschlogl, Udo; Widenmeyer, Marc; Weidenkaff, Anke

    2018-04-01

    Cr-substituted polycrystalline Ba2(In2-xCrx)O5·(H2O)δ powders (0.04 ≤ x ≤ 0.60) were synthesized by solid state reaction to investigate the relation of crystal structure, thermochemical, magnetic, and optical properties. The Cr-substitution results in an unit cell expansion and formation of the higher-symmetric tetragonal phase together with increased oxygen and hydrogen contents. Magnetic property measurements reveal that the diamagnetic pristine Ba2In2O5·(H2O)δ becomes magnetically ordered upon Cr-substitution. By UV-vis spectroscopy a gradual shift of the absorption-edge energy to lower values was observed. Numerical calculations showed that the observed bandgap narrowing was ascribed to the Cr induced states near the Fermi level. The correlation between the changes of crystal chemistry, magnetic, and optical properties of Cr-substituted Ba2(In2-xCrx)O5·(H2O)δ can be explained by the replacement of In by Cr. Consequently, an enhanced photocatalytic CO2 reduction activity was observed with increasing Cr substitution, compatible with the state-of-the-art high surface area TiO2 photocatalyst (P-25).

  5. Determination of mineral contents of wild Boletus edulis mushroom and its edible safety assessment.

    Science.gov (United States)

    Su, Jiuyan; Zhang, Ji; Li, Jieqing; Li, Tao; Liu, Honggao; Wang, Yuanzhong

    2018-04-06

    This study aimed to determine the contents of main mineral elements of wild Boletus edulis and to assess its edible safety, which may provide scientific evidence for the utilization of this species. Fourteen mineral contents (Ba, Ca, Cd, Co, Cr, Cu, Fe, Mg, Mn, Na, Ni, Sr, V and Zn) in the caps and stipes of B. edulis as well as the corresponding surface soils collected from nine different geographic regions in Yunnan Province, southwest China were determined. The analyses were performed using inductively coupled plasma atomic emission spectrometer (ICP-AES) after microwave digestion. Measurement data were analyzed using variance and Pearson correlation analysis. Edible safety was evaluated according to the provisionally tolerable weekly intake (PTWI) of heavy metals recommended by United Nations Food and Agriculture Organization and World Health Organization (FAO/WHO). Mineral contents were significantly different with the variance of collection areas. B. edulis showed relative abundant contents of Ca, Fe, Mg and Na, followed by Ba, Cr, Cu, Mn and Zn, and the elements with the lower content less were Cd, Co, Ni, Sr and V. The elements accumulation differed significantly in caps and stipes. Among them, Cd and Zn were bioconcentrated (BCF > 1) while others were bioexcluded (BCF < 1). The mineral contents in B. edulis and its surface soil were positively related, indicating that the elements accumulation level was related to soil background. In addition, from the perspective of food safety, if an adult (60 kg) eats 300 g fresh B. edulis per week, the intake of Cd in most of tested mushrooms were lower than PTWI value whereas the Cd intakes in some other samples were higher than this standard. The results indicated that the main mineral contents in B. edulis were significantly different with respect to geographical distribution, and the Cd intake in a few of regions was higher than the acceptable intakes with a potential risk.

  6. Microstructural characterization, formation mechanism and fracture behavior of the needle δ phase in Fe–Ni–Cr type superalloys with high Nb content

    Energy Technology Data Exchange (ETDEWEB)

    Ning, Yongquan, E-mail: luckyning@nwpu.edu.cn [School of Materials Science & Engineering, Northwestern Polytechnical University, Xi' an 710072 (China); Huang, Shibo [Anshan Iron & Steel Group Corporation Bayuquan Subsidiary Company, Bayuquan 115007 (China); Fu, M.W. [Department of Mechanical Engineering, Hong Kong Polytechnic University, Hung Hom, Kowloon, Hong Kong (China); Dong, Jie [Inspection & Research Institute of Boiler & Pressure Vessel of Jiangxi Province, Nanchang 330029 (China)

    2015-11-15

    Microstructural characterization, formation mechanism and fracture behavior of the needle δ phase in Fe–Ni–Cr type superalloys with high Nb content (GH4169, equivalent to Inconel 718) have been quantitatively investigated in this research. The typical microstructures of δ phases with the stick, mixed and needle shapes obviously present in Inconel 718 after the isothermal upsetting at the temperature of 980–1060 °C with the initial strain rate of 10{sup −3}–10{sup −1} s{sup −1}. It is found that the shape of the δ phase has a great effect on the mechanical properties of the alloy, viz., the stick δ phase behaves good plasticity and the needle δ phase has good strength. In addition, the needle δ phase can be used to control the grain size as it can prevent grain growth. The combined effect of the localized necking and microvoid coalescence leads to the final ductile fracture of the GH4169 components with the needle δ phase. Both dislocation motion and atom diffusion are the root-cause for the needle δ phase to be firstly separated at grain boundary and then at sub-boundary. The formation mechanism of the needle δ phase is the new finding in this research. Furthermore, it is the primary mechanism for controlling the needle δ phase in Fe–Ni–Cr type superalloys with high Nb content. - Highlights: • Shape of the δ phase takes great effect on mechanical property. • Needle δ phase plays a great role to prevent grain growth. • Needle δ phase can enhance the fracture strength. • Microstructure mechanism of the needle δ phase has been investigated. • Fracture behavior of the needle δ phase has been studied.

  7. Contents of trace elements in blood of healthy old people assayed by ICP-MS

    International Nuclear Information System (INIS)

    Wen Xinyu; Tong Hongli; Wang Ling; Zhou Heping; Tian Yaping

    2008-01-01

    To investigate the levels of 11 trace elements in serum of healthy old people to provide scientific basis for prevention and treatment of geriatric diseases, the serum were separated from blood samples according to standard procedure. The serum samples were underwent digestion, elimination of nitric acid, volume fixation and then assayed by inductively coupled plasma mass spectrometry. The results showed that the contents of Al in elderly people's serum is higher than those in young people (P<0.01), while the contents of V, Cr, Cu and Se in elderly people's serum were lower than those in young people (P<0.05). There were no significant differences in other trace elements between two groups. The contents of some trace elements in elderly people's serum changed significantly. (authors)

  8. Characterization and carbon monoxide oxidation activity of La1-ySryCr1-xRuxO3 perovskites

    Directory of Open Access Journals (Sweden)

    C. MARINOVA

    2000-01-01

    Full Text Available The oxidation of CO over La1-ySryCr1-xRuxO3 perovskite type oxides with y=0.3 and 0 £ x £ 0.100 have been studied. X-ray fluorescence analysis confirmed that content of elements in the bulk corresponds to the established nominal perovskite stoichiometry, indicating that no significant oxidation of ruthenium into volatile polyvalent oxides with their consequented escape from the sample occurred in air up to the temperature of 1000°C. According to X-ray diffraction analysis, all sampls achieved the perovskite hexagonal with the presence of some SrCrO4. X-ray photoelectron spectroscopy analysis of ruthenium samples shows higher Ru and Sr surface concentraitions than in the bulk. The binding energy for Ru3p is virtually the same in all samples and consistent with that of Ru4+ (463.6-464.3eV. Kinetic studies were performed in a differential recycle reactor with a recycling ratio 80. The results show that substitution of Ru4+ for Cr3+ in La1-ySryCrO3 leads to a significant increase in both the activity and the activation energy. The global CO oxidation rate, referred on the BET surface area, correlates with the surface Ru4+ atomic concentraiton. Hence, the activity reflect the surface enrichment in ruthenium. Moreover, an identical apparent activation energy E = 93 kJ/mol and the same specific rate per ruthenium surface ion were obtained for samples with a Ru content x ³ 0.05 suggest that exposed Ru4+ ions mainly participate in the reaction.

  9. Application of double-spike isotope dilution for the accurate determination of Cr(III), Cr(VI) and total Cr in yeast.

    Science.gov (United States)

    Yang, Lu; Ciceri, Elena; Mester, Zoltán; Sturgeon, Ralph E

    2006-11-01

    A method is presented for the simultaneous determination of Cr(III) and Cr(VI) in yeast using species-specific double-spike isotope dilution (SSDSID) with anion-exchange liquid chromatography (LC) separation and sector field inductively coupled plasma mass spectrometric (SF-ICP-MS) detection. Total Cr is quantitated using ID SF-ICP-MS. Samples were digested on a hot plate at 95+/-2 degrees C for 6 h in an alkaline solution of 0.5 M NaOH and 0.28 M Na2CO3 for the determination of Cr(III) and Cr(VI), whereas microwave-assisted decomposition with HNO3 and H2O2 was used for the determination of total Cr. Concentrations of 2,014+/-16, 1,952+/-103 and 76+/-48 mg kg-1 (one standard deviation, n=4, 3, 3), respectively were obtained for total Cr, Cr(III) and Cr(VI) in the yeast sample. Significant oxidation of Cr(III) to Cr(VI) (24.2+/-7.6% Cr(III) oxidized, n=3) and reduction of Cr(VI) to Cr(III) (37.6+/-6.5% Cr(VI) reduced, n=3) occurred during alkaline extraction and subsequent chromatographic separation at pH 7. Despite this significant bidirectional redox transformation, quantitative recoveries for both Cr(III) and Cr(VI) were achieved using the SSDSID method. In addition, mass balance between total Cr and the sum of Cr(III) and Cr(VI) concentrations was achieved. Method detection limits of 0.3, 2 and 30 mg kg-1 were obtained for total Cr, Cr(VI) and Cr(III), respectively, based on a 0.2-g sub-sample.

  10. The effects of heavy metal ions on the chlorophyll content and cell membrane permeability of charophytes

    International Nuclear Information System (INIS)

    Fu Hualong; Chen Hao; Dong Bin; Qing Renwei

    2001-01-01

    The authors studied the effects of several heavy metal ions in different concentrations (Cd 2+ , Hg 2+ , Pb 2+ , Cr 6+ ) on the chlorophyll content and cell membrane permeability of Chara vulgaris L. It was discovered that the effects of heavy metal ions on the chlorophyll content and cell membrane permeability of Chara vulgaris L. changed with their different concentration. The trend was that the chlorophyll content and cell membrane permeability were decreased with the increase of the heavy metal ions. The degree of chlorophyll content affected was Cr 6+ , Cd 2+ , Hg 2+ , Pb 2+ , and that of cell membrane permeability affected was Cd 2+ , Cr 6+ , Hg 2+ , Pb 2+

  11. Soybean seeds expressing feedback-insensitive cystathionine γ-synthase exhibit a higher content of methionine.

    Science.gov (United States)

    Song, Shikui; Hou, Wensheng; Godo, Itamar; Wu, Cunxiang; Yu, Yang; Matityahu, Ifat; Hacham, Yael; Sun, Shi; Han, Tianfu; Amir, Rachel

    2013-04-01

    Soybean seeds provide an excellent source of protein for human and livestock nutrition. However, their nutritional quality is hampered by a low concentration of the essential sulfur amino acid, methionine (Met). In order to study factors that regulate Met synthesis in soybean seeds, this study used the Met-insensitive form of Arabidopsis cystathionine γ-synthase (AtD-CGS), which is the first committed enzyme of Met biosynthesis. This gene was expressed under the control of a seed-specific promoter, legumin B4, and used to transform the soybean cultivar Zigongdongdou (ZD). In three transgenic lines that exhibited the highest expression level of AtD-CGS, the level of soluble Met increased significantly in developing green seeds (3.8-7-fold). These seeds also showed high levels of other amino acids. This phenomenon was more prominent in two transgenic lines, ZD24 and ZD91. The total Met content, which including Met incorporated into proteins, significantly increased in the mature dry seeds of these two transgenic lines by 1.8- and 2.3-fold, respectively. This elevation was accompanied by a higher content of other protein-incorporated amino acids, which led to significantly higher total protein content in the seeds of these two lines. However, in a third transgenic line, ZD01, the level of total Met and the level of other amino acids did not increase significantly in the mature dry seeds. This line also showed no significant change in protein levels. This suggests a positive connection between high Met content and the synthesis of other amino acids that enable the synthesis of more seed proteins.

  12. Structural analysis and magnetic properties of solid solutions of Co–Cr system obtained by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Betancourt-Cantera, J.A. [Área Académica de Ciencias de la Tierra y Materiales, UAEH Carr., Pachuca-Tulancingo Km. 4.5, Pachuca, Hidalgo 42184 (Mexico); Sánchez-De Jesús, F., E-mail: fsanchez@uaeh.edu.mx [Área Académica de Ciencias de la Tierra y Materiales, UAEH Carr., Pachuca-Tulancingo Km. 4.5, Pachuca, Hidalgo 42184 (Mexico); Bolarín-Miró, A.M. [Área Académica de Ciencias de la Tierra y Materiales, UAEH Carr., Pachuca-Tulancingo Km. 4.5, Pachuca, Hidalgo 42184 (Mexico); Betancourt, I.; Torres-Villaseñor, G. [Departamento de Materiales Metálicos y Cerámicos, Instituto de Investigaciones en Materiales, Universidad Nacional Autónoma de México, México D.F. 04510 (Mexico)

    2014-03-15

    In this paper, a systematic study on the structural and magnetic properties of Co{sub 100−x}Cr{sub x} alloys (0Cr elemental powders were used as precursors, and mixed in an adequate weight ratio to obtain Co{sub 1−x}Cr{sub x} (0Cr-bcc structures were obtained. The saturation polarization indicated a maximum value of 1.17 T (144 Am{sup 2}/kg) for the Co{sub 90}Cr{sub 10}, which decreases with the increasing of the Cr content up to x=80, as a consequence of the dilution effect of the magnetic moment which is caused by the Cr content and by the competition between ferromagnetic and antiferromagnetic exchange interactions. The coercivity increases up to 34 kA/m (435 Oe) for Co{sub 40}Cr{sub 60}. For Cr rich compositions, it is observed an important decrease reaching 21 kA/m (272 Oe) for Co{sub 10}Cr{sub 90,} it is related to the grain size and the structural change. Besides, the magnetic anisotropy constant was determined for each composition. Magnetic thermogravimetric analysis allowed to obtain Curie temperatures corresponding to the formation of hcp-Co(Cr) and fcc-Co(Cr) solid solutions. - Highlights: • Mechanical alloying (MA) induces the formation of solid solutions of Co–Cr system in non-equilibrium. • We report the crystal structure and the magnetic behavior of Co–Cr alloys produced by MA. • MA improves the magnetic properties of Co–Cr system.

  13. Advanced oxidation of rhodamine B with hydrogen peroxide over ZnCr layered double hydroxide catalysts

    Directory of Open Access Journals (Sweden)

    Nguyen Tien Thao

    2017-09-01

    Full Text Available Zn/Cr layered zinc hydroxide materials with different molar ratios of Cr/Zn have been synthesized through the coprecipitation method at pH of 9.0–9.5. At high Cr/Zn molar ratios of 0.5/1–1/3, the materials possess some layered structure with carbonate anions between the interlayer galleries. The catalysts present uniform particle sizes and quite high surface area. An isomorphous substitution of Zn2+ by Cr3+ in the brucite-like sheets makes the layered Cr-doped zinc hydroxides potential catalysts for efficient oxidation of rhodamine B with H2O2 solution. The experimental results indicated that the intra-lattice Cr3+ ions are more active than Cr2O3 components in the oxidative removal of rhodamine B. The degradation efficiency is dependent on the intra lattice Cr3+ contents and reaction variables. The Cr/Zn LDH gave a high decolorization (99% of rhodamine B at near neutral pH and room temperature.

  14. Effects of EDTA on the electronic properties of passive film formed on Fe-20Cr in pH 8.5 buffer solution

    International Nuclear Information System (INIS)

    Cho, Eun Ae; Kwon, Hyuk Sang; Beranrd, Frederic

    2003-01-01

    The electronic properties of the passive film formed on Fe-20Cr ferritic stainless steel in pH 8.5 buffer solution containing 0.05 M EDTA (ethylene diammine tetraacetic acid) were examined by the photocurrent measurements and Mott-Schottky analysis for the film. XPS depth profile for the film demonstrated that Cr content in the outermost layer of the passive film was higher in the solution with EDTA than that in the solution without EDTA, due to selective dissolution of Fe by EDTA. In the solution with EDTA, the passive film showed characteristics of an amorphous or highly disordered n-type semiconductor. The band gap energies of the passive film are estimated to be ∼ 3.0 eV, irrespective of film formation potential from 0 to 700 mV SCE and of presence of EDTA. However, the donor density of the passive film formed in the solution with EDTA is much higher than that formed in the solution without EDTA, due to an increase in oxygen vacancy resulted from the dissolution of Fe-oxide in the outermost layer of the passive film. These results support the proposed model that the passive film formed on Fe-20Cr in pH 8.5 buffer solution mainly consists of Cr-substituted γ-Fe 2 O 3

  15. LEAN-GREEN MANUFACTURING: COLLABORATIVE CONTENT AND LANGUAGE INTEGRATED LEARNING IN HIGHER EDUCATION AND ENGINEERING COURSES

    Directory of Open Access Journals (Sweden)

    MARCELO RUDOLFO CALVETE GASPAR

    2017-09-01

    Full Text Available Lean and Green manufacturing processes aim at achieving lower material and labour costs, while reducing impacts on the environment, and promoting sustainability as a whole. This paper reports on a pilot experiment with higher education and engineering students, exploring the full potential of a collaborative approach on courses integrating the Portuguese Polytechnic of Castelo Branco engineering studies curricula, while simultaneously improving their proficiency in English. Content and Language Integrated Learning (CLIL has become a key area of curricular innovation since it is known for improving both language and content teacher and student motivation. In this context, instructional design for CLIL entailed tandem work of content (engineering and language (English teacher to design learning sequences and strategies. This allowed students to improve not only their language skills in English but also their knowledge in the specific engineering domain content on green and lean manufacturing processes.

  16. Effect of laser absorption on picosecond laser ablation of Cr12MoV mold steel, 9Cr18 stainless steel and H13A cemented carbide

    Science.gov (United States)

    Wu, Baoye; Liu, Peng; Wang, Xizhao; Zhang, Fei; Deng, Leimin; Duan, Jun; Zeng, Xiaoyan

    2018-05-01

    Due to excellent properties, Cr12MoV mold steel, 9Cr18 stainless steel and H13A cemented carbide are widely used in industry. In this paper, the effect of absorption of laser light on ablation efficiency and roughness have been studied using a picosecond pulse Nd:YVO4 laser. The experimental results reveal that laser wavelength, original surface roughness and chemical composition play an important role in controlling ablation efficiency and roughness. Firstly, higher ablation efficiency with lower surface roughness is achieved on the ablation of 9Cr18 at 532, comparing with 1064 nm. Secondly, the ablation efficiency increases while the Ra of the ablated region decreases with the decrease of original surface roughness on ablation of Cr12MoV mold steel at 532 nm. Thirdly, the ablation efficiency of H13A cemented carbide is much higher than 9Cr18 stainless steel and Cr12MoV mold steel at 1064 nm. Scanning electron microscopy images reveals the formation of pores on the surface of 9Cr18 stainless steel and Cr12MoV mold steel at 532 nm while no pores are formed at 1064 nm. As to H13A cemented carbide, worm-like structure is formed at 1064 nm. The synergetic effects of the heat accumulation, plasma shielding and ablation threshold on laser ablation efficiency and machining quality were analyzed and discussed systematically in this paper.

  17. THE STRUCTURE AND MECHANICAL PROPERTIES OF NiCrBSi COATINGS PREPARED BY LASER BEAM CLADDING

    Directory of Open Access Journals (Sweden)

    Zita Iždinská

    2010-03-01

    Full Text Available In this work, the influence of processing conditions on the microstructure and abrasive wear behavior of a NiCrBSi laser clad coating is analyzed. The powder was applied onto a mild steel substrate (Fe–0.17% C by different laser powers and cladding speeds providing 0.7 – 1.2 mm thick coatings. The microstructure of coatings was analyzed by scanning electron microscopy (SEM. Energy-dispersive X-ray spectroscopy (EDX was applied for chemical analysis and tribological properties of coatings were evaluated by pin-on-disc wear test. EDX analysis reveals the influence of cladding speed on dilution of iron from the substrate into the coating. Higher iron content matches with lower hardness and wear resistance of appropriate coatings. Obtained results indicate that laser cladding is suitable technique for manufacturing NiCrBSi abrasive wear coatings and that it is possible to find out proper parameters in order to optimize tribological behavior of these coatings.

  18. Electronic structure and superconductivity of fcc Cr

    International Nuclear Information System (INIS)

    Xu, J.; Freeman, A.J.; Jarlborg, T.; Brodsky, M.B.

    1984-01-01

    Results of self-consistent electronic structure calculations are reported for metastable fcc Cr metal. Unlike the case of bcc Cr which has E/sub F/ at a minimum in the density of states (DOS), the DOS at E/sub F/ in fcc Cr is at a peak making this one of the higher-DOS metals with the fcc structure (e.g., comparable with that of Ni and Pt). A calculated Stoner factor of 0.82 indicates that ferromagnetic ordering is not expected. Calculations of the electron-phonon coupling parameter lambda and superconducting transition temperature T/sub c/ were made using the rigid-ion approximation and strong-coupling theory with various estimates of the (unknown) phonon contribution. We conclude that T/sub c/'sroughly-equal2.5 K are reasonable, although they are substantially smaller than the T/sub c/roughly-equal10 K derived from measurements on Au-Cr-Au sandwiches

  19. Hydrogen storage performance of Ti-V-based BCC phase alloys with various Fe content

    International Nuclear Information System (INIS)

    Yu, X.B.; Feng, S.L.; Wu, Z.; Xia, B.J.; Xu, N.X.

    2005-01-01

    The effect of Fe content on hydrogen storage characteristics of Ti-10Cr-18Mn-(32-x)V-xFe (x = 0, 2, 3, 4, 5) alloys has been investigated at 353 K. The X-ray diffraction (XRD) patterns and scanning electron microscopy (SEM) images of the alloys present BCC and C14 two-phase structures for all of the Fe-containing alloys. With the increasing Fe content, the lattice parameters of the BCC phase decrease, which results in an increase of the hydrogen desorption plateau pressure of the alloys. Among the studied alloys, Ti-10Cr-18Mn-27V-5Fe alloy exhibits the smallest PCT plateau slope and a more suitable plateau pressure (0.1 MPa equ <1 MPa). The maximum and effective capacities of the alloy are 3.32 wt.% and 2.26 wt.%, respectively, which are higher than other reported Fe-containing BCC phase alloys. In addition, the V/Fe ratio in this alloy is close to that of (VFe) alloy, whose cost is much lower than that of pure V

  20. Changes of plasma levels of homocysteine (Hcy) and urinary albumin contents in patients with type 2 diabetes complicated with nephropathy

    International Nuclear Information System (INIS)

    Song Lili

    2010-01-01

    Objective: To study the changes of plasma levels of homocysteine (Hcy) and urinary albumin contents in patients with type 2 diabetes complicated with nephropathy. Methods: Plasma Hcy (with fluorescence immunoassay) fasting glucose, BUN, Cr (with biochemistry) levels and urinary albumin contents (with RIA) were determined in 36 DM2 patients without nephropathy, 30 DM2 patients with nephropathy and 30 controls. Results: The fasting blood glucose levels in the 2 groups of diabetic patients were not much different. Again, the BUN and Cr levels in the 3 groups of patients were about the same. The plasma Hcy levels in the group of patients with diabetic nephropathy were significantly higher than those in both controls and DM2 patients without nephropathy (all P<0.01). Conclusion: Hyperhomocysteinemia is a risk factor for nephropathy in DM2 patients. (authors)

  1. GABA content within the ventromedial prefrontal cortex is related to trait anxiety.

    Science.gov (United States)

    Delli Pizzi, Stefano; Padulo, Caterina; Brancucci, Alfredo; Bubbico, Giovanna; Edden, Richard A; Ferretti, Antonio; Franciotti, Raffaella; Manippa, Valerio; Marzoli, Daniele; Onofrj, Marco; Sepede, Gianna; Tartaro, Armando; Tommasi, Luca; Puglisi-Allegra, Stefano; Bonanni, Laura

    2016-05-01

    The ventromedial prefrontal cortex (vmPFC) plays a key role in emotion processing and regulation. vmPFC dysfunction may lead to disinhibition of amygdala causing high anxiety levels. γ-Aminobutyric acid (GABA) inter-neurons within vmPFC shape the information flow to amygdala. Thus, we hypothesize that GABA content within vmPFC could be relevant to trait anxiety. Forty-three healthy volunteers aged between 20 and 88 years were assessed for trait anxiety with the Subscale-2 of the State-Trait-Anxiety Inventory (STAI-Y2) and were studied with proton magnetic resonance spectroscopy to investigate GABA and Glx (glutamate+glutamine) contents within vmPFC. Total creatine (tCr) was used as internal reference. Partial correlations assessed the association between metabolite levels and STAI-Y2 scores, removing the effect of possible nuisance factors including age, educational level, volumes of gray matter and white matter within magnetic resonance spectroscopy voxel. We observed a positive relationship between GABA/tCr and STAI-Y2 scores. No significant relationships were found between Glx/tCr and STAI-Y2 and between tCr/water and STAI-Y2. No differences were found between males and females as regards to age, STAI-Y2, GABA/tCr, Glx/tCr, tCr/water, gray matter and white matter volumes. We suggest a close relationship between GABA content within vmPFC and trait anxiety providing new insights in the physiology of emotional brain. © The Author (2015). Published by Oxford University Press. For Permissions, please email: journals.permissions@oup.com.

  2. CoQ10 Deficiency May Indicate Mitochondrial Dysfunction in Cr(VI Toxicity

    Directory of Open Access Journals (Sweden)

    Xiali Zhong

    2017-04-01

    Full Text Available To investigate the toxic mechanism of hexavalent chromium Cr(VI and search for an antidote for Cr(VI-induced cytotoxicity, a study of mitochondrial dysfunction induced by Cr(VI and cell survival by recovering mitochondrial function was performed. In the present study, we found that the gene expression of electron transfer flavoprotein dehydrogenase (ETFDH was strongly downregulated by Cr(VI exposure. The levels of coenzyme 10 (CoQ10 and mitochondrial biogenesis presented by mitochondrial mass and mitochondrial DNA copy number were also significantly reduced after Cr(VI exposure. The subsequent, Cr(VI-induced mitochondrial damage and apoptosis were characterized by reactive oxygen species (ROS accumulation, caspase-3 and caspase-9 activation, decreased superoxide dismutase (SOD and ATP production, increased methane dicarboxylic aldehyde (MDA content, mitochondrial membrane depolarization and mitochondrial permeability transition pore (MPTP opening, increased Ca2+ levels, Cyt c release, decreased Bcl-2 expression, and significantly elevated Bax expression. The Cr(VI-induced deleterious changes were attenuated by pretreatment with CoQ10 in L-02 hepatocytes. These data suggest that Cr(VI induces CoQ10 deficiency in L-02 hepatocytes, indicating that this deficiency may be a biomarker of mitochondrial dysfunction in Cr(VI poisoning and that exogenous administration of CoQ10 may restore mitochondrial function and protect the liver from Cr(VI exposure.

  3. The role of Zr and Nb in oxidation/sulfidation behavior of Fe-Cr-Ni alloys

    Energy Technology Data Exchange (ETDEWEB)

    Natesan, K. (Argonne National Lab., IL (USA)); Baxter, D.J. (Argonne National Lab., IL (USA) INCO Alloy Ltd., Hereford, England (UK))

    1990-11-01

    05Structural Fe-Cr-Ni alloys may undergo rapid degradation at elevated temperatures unless protective surface oxide scales are formed and maintained. The ability of alloys to resist rapid degradation strongly depends on their Cr content and the chemistry of the exposure environment. Normally, 20 wt % Cr is required for service at temperatures up to 1000{degree}C; the presence of sulfur, however, inhibits formation of a protective surface oxide scale. The oxidation and sulfidation behavior of Fe-Cr-Ni alloys is examined over a wide temperature range (650 to 1000{degree}C), with particular emphasis on the effects of alloy Cr content and the radiation of reactive elements such as Nb and Zr. Both Nb and Zr are shown to promote protective oxidation behavior on the 12 wt % Cr alloy in oxidizing environments and to suppress sulfidation in mixed oxygen/sulfur environments. Additions of Nb and Zr at 3 wt % level resulted in stabilization of Cr{sub 2}O{sub 3} scale and led to a barrier layer of Nb- or Zr-rich oxide at the scale/metal interface, which acted to minimize the transport of base metal cations across the scale. Oxide scales were preformed in sulfur-free environments and subsequently exposed to oxygen/sulfur mixed-gas atmospheres. Preformed scales were found to delay the onset of breakaway corrosion. Corrosions test results obtained under isothermal and thermal cycling conditions are presented. 58 refs., 55 figs., 8 tabs.

  4. Synthesis of (Cr,V){sub 2}(C,N) solid solution powders by thermal processing precursors

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Anrui [School of Materials Science & Engineering, Sichuan University, Chengdu, 610065 (China); Liu, Ying [School of Materials Science & Engineering, Sichuan University, Chengdu, 610065 (China); Key Laboratory of Advanced Special Material & Technology, Ministry of Education, Chengdu, 610065 (China); Ma, Shiqing; Qiu, Yuchong; Rong, Pengcheng; Ye, Jinwen [School of Materials Science & Engineering, Sichuan University, Chengdu, 610065 (China)

    2017-06-01

    The single-phase (Cr,V){sub 2}(C,N) solid solution powders were fabricated via carbothermal reduction-nitridation (CRN) processing technique. The effects of heat treatment temperature, nitrogen pressure and carbon proportion were experimentally studied in detail by X-ray Diffraction (XRD), Scanning Electron Microscope (SEM), Transmission Electron Microscope (TEM) and thermal analysis. The chemical transformations of vanadium and chromium compounds were as follows: precursors → V{sub 2}O{sub 3}, Cr{sub 2}O{sub 3} → Cr{sub 3}C{sub 2}, Cr{sub 2}O{sub 3}, (Cr,V){sub 2}(C,N) → (Cr,V){sub 2}(C,N). When the heat-treated temperature was below 1200 °C, chromium oxides didn’t completely react. However, higher temperature ∼1300 °C could not only lead to the segregation of some nitrides and carbon black, but also to the occurrence of fiber-bridged particles. The system nitrogen pressure over 0.03 MPa would cause a subtle transformation of (Cr,V){sub 2}(C,N) to VCrN{sub 2}. When the carbon proportion was below 15 wt%, the oxides could not be completely reduced, while when the carbon proportion was above 15.5 wt%, some undesired carbides, like Cr{sub 23}C{sub 6} and Cr{sub 3}C{sub 2}, would form. Ultimately, the homogeneously distributed pure-phase (Cr,V){sub 2}(C,N) spherical particles with the average size of ∼1.5 μm were obtained at the optimal conditions of the treatment of precursors at 1200 °C for 1 h with the nitrogen pressure of 0.03 MPa and carbon content of 15.5 wt%. The chemical composition of the solid solution with the optimal process could be drawn as (Cr{sub 0.85}V{sub 0.15}){sub 2}(C{sub 0.57}N{sub 0.43}). Thermal processing precursors method shows the advantages of lower synthesis temperature, shorter period and finer particles when comparing with the conventional preparations. - Highlights: • Single phase of (Cr,V){sub 2}(C,N) powders were synthesized for the first time. • Precursors were used to prepared the powders by carbothermal

  5. Bainitic Transformation and Properties of Low Carbon Carbide-Free Bainitic Steels with Cr Addition

    Directory of Open Access Journals (Sweden)

    Mingxing Zhou

    2017-07-01

    Full Text Available Two low carbon carbide-free bainitic steels (with and without Cr addition were designed, and each steel was treated by two kinds of heat treatment procedure (austempering and continuous cooling. The effects of Cr addition on bainitic transformation, microstructure, and properties of low carbon bainitic steels were investigated by dilatometry, metallography, X-ray diffraction, and a tensile test. The results show that Cr addition hinders the isothermal bainitic transformation, and this effect is more significant at higher transformation temperatures. In addition, Cr addition increases the tensile strength and elongation simultaneously for austempering treatment at a lower temperature. However, when the austempering temperature is higher, the strength increases and the elongation obviously decreases by Cr addition, resulting in the decrease in the product of tensile strength and elongation. Meanwhile, the austempering temperature should be lower in Cr-added steel than that in Cr-free steel in order to obtain better comprehensive properties. Moreover, for the continuous cooling treatment in the present study, the product of tensile strength and elongation significantly decreases with Cr addition due to more amounts of martensite.

  6. Effect of pre-oxidation on high temperature sulfidation behavior of FeCr and FeCrAl alloys

    Directory of Open Access Journals (Sweden)

    Pillis Marina Fuser

    2004-01-01

    Full Text Available High temperature corrosion of structural alloys in sulfur bearing environments is many orders of magnitude higher than in oxidizing environments. Efforts to increase sulfidation resistance of these alloys include addition of alloying elements. Aluminum additions to iron-chromium alloys bring about increase in sulfidation resistance. This paper reports the effect of pre-oxidation on the sulfidation behavior of Fe-20Cr and Fe-20Cr-5Al alloys in H2-2% H2S environment at 800 °C. The surfaces of sulfidized specimens were also examined. Pre-oxidation of the two alloys results in an incubation period during subsequent sulfidation. After this incubation period, the Fe-20Cr alloy showed sulfidation behavior similar to that when the alloy was not pre-oxidized. The incubation period during sulfidation of the Fe-20Cr-5Al alloy was significantly longer, over 45 h, compared to 2 h for the Al free alloy. Based on the microscopic and gravimetric data a mechanism for sulfidation of these alloys with pre-oxidation has been proposed.

  7. Cr-substitution effect on structural, optical and electrical properties of Cr{sub x}Ce{sub 1−x}PO{sub 4} (x = 0.00, 0.08, 0.10 and 0.20) nanorods

    Energy Technology Data Exchange (ETDEWEB)

    Fadhalaoui, Amor [Laboratoire de Chimie des Matériaux, Faculté des Sciences de Bizerte, Zarzouna, Bizerte 7021 (Tunisia); Dhaouadi, Hassouna, E-mail: dhaouadihassouna@yahoo.fr [Laboratoire Matériaux Traitement et Analyse, INRAP, Technopôle Sidi-Thabet, Tunis 2020 (Tunisia); Marouani, Houda [Laboratoire de Chimie des Matériaux, Faculté des Sciences de Bizerte, Zarzouna, Bizerte 7021 (Tunisia); Kouki, Abdessalem [L3M, FSB, Zarzouna, Bizerte 7021 (Tunisia); Madani, Adel [Department of Physics, Applied Science College, Umm Al Qura University, Makkah (Saudi Arabia); Rzaigui, Mohamed [Laboratoire de Chimie des Matériaux, Faculté des Sciences de Bizerte, Zarzouna, Bizerte 7021 (Tunisia)

    2016-01-15

    Graphical abstract: The Cr{sub x}Ce{sub 1−x}PO{sub 4} (x = 0.00, 0.08, 0.10 and 0.20) nanorods synthesized under hydrothermal conditions. - Highlights: • Cr{sub x}Ce{sub 1−x}PO{sub 4} (x = 0.00–0.20) nanorods were synthesized by hydrothermal method. • Mean crystallite size of the products decreases with Cr-content. • Obvious improvements of the electrical conductivity comparatively to CePO4. - Abstract: Cr{sub x}Ce{sub 1−x}PO{sub 4} (x = 0.00–0.20) nanorods were synthesized using the hydrothermal method. The as-prepared samples were characterized by X-ray diffraction (XRD), infrared absorption spectroscopy (IR) and transmission electron microscopy (TEM). The XRD results revealed the formation of a pure CePO{sub 4} hexagonal phase. TEM images confirmed the nano-size character of the as-prepared samples. Impedance spectroscopy analysis was used to analyze the electrical behavior of samples as a function of frequency at different temperatures. The increase of Cr-amount led to an increase in the total conductivities and decreased the activation energies (E{sub a} (x = 0.00) = 1.08 eV to E{sub a} (x = 0.20) = 0.80 eV). The optical properties of Cr{sub x}Ce{sub 1−x}PO{sub 4} nanomaterials were investigated using UV–vis spectroscopy. The band-gap energy values decreased with increasing Cr-content showing a red-shift trend. The improvement of the electrical conductivity and optical properties makes the Cr{sub x}Ce{sub 1−x}PO{sub 4} nanomaterials possible candidates to be used as electrolytes in solid oxide fuel cells, in photocatalytic and photovoltaic applications.

  8. Effect of Cr doping on structural and magnetic properties of ZnS nanoparticles

    International Nuclear Information System (INIS)

    Virpal,; Singh, Jasvir; Sharma, Sandeep; Singh, Ravi Chand

    2016-01-01

    The structural, optical and magnetic properties of pure and Cr doped ZnS nanoparticles were studied at room temperature. X-ray diffraction analysis confirmed the absence of any mixed phase and the cubic structure of ZnS in pure and Cr doped ZnS nanoparticles. Fourier transfer infrared spectra confirmed the Zn-S stretching bond at 664 cm"−"1 of ZnS in all prepared nanoparticles. The UV-Visible absorption spectra showed blue shift which became even more pronounced in Cr doped ZnS nanoparticles. However, at relatively higher Cr concentrations a slower red shift was shown by the doped nanoparticles. This phenomenon is attributed to sp-d exchange interaction that becomes prevalent at higher doping concentrations. Further, magnetic hysteresis measurements showed that Cr doped ZnS nanoparticles exhibited ferromagnetic behavior at room temperature.

  9. Oxidation behavior of arc evaporated Al-Cr-Si-N thin films

    Energy Technology Data Exchange (ETDEWEB)

    Tritremmel, Christian; Daniel, Rostislav; Mitterer, Christian; Mayrhofer, Paul H.; Lechthaler, Markus; Polcik, Peter [Christian Doppler Laboratory for Advanced Hard Coatings, Department of Physical Metallurgy and Materials Testing, Montanuniversitaet Leoben, Franz-Josef-Strasse 18, A-8700 Leoben (Austria); Christian Doppler Laboratory for Application Oriented Coating Development, Department of Physical Metallurgy and Materials Testing, Montanuniversitaet Leoben, Franz-Josef-Strasse 18, A-8700 Leoben (Austria); OC Oerlikon Balzers AG, Iramali 18, LI-9496 Balzers (Liechtenstein); PLANSEE Composite Materials GmbH, Siebenbuergerstrasse 23, D-86983 Lechbruck am See (Germany)

    2012-11-15

    The impact of Al and Si on the oxidation behavior of Al-Cr-(Si)-N thin films synthesized by arc evaporation of powder metallurgically prepared Al{sub x}Cr{sub 1-x} targets with x = Al/(Al + Cr) of 0.5, 0.6, and 0.7 and (Al{sub 0.5}Cr{sub 0.5}){sub 1-z}Si{sub z} targets with Si contents of z = 0.05, 0.1, and 0.2 in N{sub 2} atmosphere was studied in detail by means of differential scanning calorimetry, thermogravimetric analysis (TGA), x-ray diffraction, and Raman spectroscopy. Dynamical measurements in synthetic air (up to 1440 Degree-Sign C) revealed the highest onset temperature of pronounced oxidation for nitride coatings prepared from the Al{sub 0.4}Cr{sub 0.4}Si{sub 0.2} target. Isothermal TGA at 1100, 1200, 1250, and 1300 Degree-Sign C highlight the pronounced improvement of the oxidation resistance of Al{sub x}Cr{sub 1-x}N coatings by the addition of Si. The results show that Si promotes the formation of a dense coating morphology as well as a dense oxide scale when exposed to air.

  10. Microstructure and Mechanical Properties of n-irradiated Fe-Cr Model Alloys

    International Nuclear Information System (INIS)

    Matijasevic, Milena; Al Mazouzi, Abderrahim

    2008-01-01

    High chromium ( 9-12 wt %) ferritic/martensitic steels are candidate structural materials for future fusion reactors and other advanced systems such as accelerator driven systems (ADS). Their use for these applications requires a careful assessment of their mechanical stability under high energy neutron irradiation and in aggressive environments. In particular, the Cr concentration has been shown to be a key parameter to be optimized in order to guarantee the best corrosion and swelling resistance, together with the least embrittlement. In this work, the characterization of the neutron irradiated Fe-Cr model alloys with different Cr % with respect to microstructure and mechanical tests will be presented. The behavior of Fe-Cr alloys have been studied using tensile tests at different temperature range ( from -160 deg. C to 300 deg. C). Irradiation-induced microstructure changes have been studied by TEM for two different irradiation doses at 300 deg. C. The density and the size distribution of the defects induced have been determined. The tensile test results indicate that Cr content affects the hardening behavior of Fe-Cr binary alloys. Hardening mechanisms are discussed in terms of Orowan type of approach by correlating TEM data to the measured irradiation hardening. (authors)

  11. Influence of trimethylsilane flow on the microstructure, mechanical and tribological properties of CrSiCN coatings in water lubrication

    International Nuclear Information System (INIS)

    Wu, Zhiwei; Zhou, Fei; Wang, Qianzhi; Zhou, Zhifeng; Yan, Jiwang; Li, Lawrence Kwok-Yan

    2015-01-01

    Highlights: • CrSiCN coatings with different Si and C contents were deposited. • CrSiCN coatings consisted of Cr(C,N) nanocrystallites and amorphous phases such as a-Si_3N_4(SiC, SiCN) and a-C(a-CN_x). • CrSiCN coatings exhibited the highest hardness of 21.3 GPa at the TMS flow of 10 sccm. • CrSiCN coatings deposited at the TMS flow of 10 sccm possessed the excellent tribological properties in water. • The wear mechanism changed from tribochemical wear to mechanical wear when the TMS flow increased. - Abstract: CrSiCN coatings with different silicon and carbon contents were deposited on silicon wafers and 316L stainless steels using unbalanced magnetron sputtering via adjusting trimethylsilane (TMS) flow, and their microstructure and mechanical properties were characterized by X-ray diffraction (XRD), scanning electron microscopy(SEM), X-ray photoelectrons spectroscopy(XPS) and nano-indenter, respectively. The tribological properties of CrSiCN coatings sliding against SiC balls in water were investigated using ball-on-disk tribometer. The results showed that the CrSiCN coatings had fine composite microstructure consisting of nanocrystallites of Cr(C, N) crystal and amorphous phases such as a-Si_3N_4 and a-C(a-CN_x). The typical columnar structures changed from fine cluster to coarse ones when the Si content was beyond 3.4 at.%. With an increase in the TMS flow, the hardness and Young's modulus of Corsican coatings all first increased, and then rapidly decreased, but the compressive stress in the coatings varied in the range of 2.8–4.8 GPa. When the TMS flow was 10 sccm, the CrSiCN coatings exhibited the highest hardness of 21.3 GPa and the lowest friction coefficient (0.11) and wear rate (8.4 × 10"−"8 mm"3/N m). But when the TMS flow was beyond 15 sccm, the tribological properties of CrSiCN coatings in water became poor.

  12. Fracture toughness of MgCr2O4-ZrO2 composities

    International Nuclear Information System (INIS)

    Singh, J.P.

    1985-01-01

    The effect of unstabilized ZrO 2 inclusions on the fracture surface energy of MgCr 2 O 4 was studied as a function of ZrO 2 content. It was observed that fracture surface energy increases with increasing ZrO 2 content, and reaches the maximum value of 24.5 j/m 2 at 16.5 vol% ZrO 2 . This represents an approx. = fourhold increase in the fracture surface energy of Mg 2 O 4 as a result of ZrO 2 inclusions. It is proposed that this improvement results from the energy absorbed by the microcracks formed in the MgCr 2 O 4 matrix as a result of the tetragonal → monoclinic phase transormation of ZrO 2 and the associated volume expansion

  13. Influence of N2/Ar Flow Ratio on Microstructure and Properties of the AlCrSiN Coatings Deposited by High-Power Impulse Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Bai-Song Li

    2017-12-01

    Full Text Available The cutting properties of tools can be greatly improved by AlCrSiN coatings. The AlCrSiN coatings with nitrogen content in the range of 28.2–56.3 at.% were prepared by varying the N2/Ar flow ratio from 1/4 to 1/1. The influence of N2/Ar flow ratio on composition, microstructure, and mechanical properties, as well as the tribological properties, of the coatings was investigated. With increasing N content, the coating microstructure gradually evolved from single fcc-(Cr,AlN (200 phase to the mixture of fcc-(Cr,AlN and hcp-(Cr,AlN phase, which corresponds to an increased crystallinity within the coatings. The coating presents the highest hardness and best wear resistance for an N2/Ar flow ratio of 1/1, but the film adhesive strength and inner stress decreased obviously with increasing N2/Ar flow ratio, which was attributed to the rapid reduction of particle kinetic energy induced by the obstruction of neutral nitride particles between target and substrates. The highest H3/E*2 value exhibited the lowest wear rate, at 0.81 × 10−14 m3/(N·m, indicating that it had the best resistance to plastic deformation. The main wear mechanisms of the as-deposited coatings were abrasive wear and adhesive wear. The increasing crystallinity of the interior coatings resulted in higher hardness and better tribological behavior with an increase in N2/Ar flow ratio.

  14. Colour due to Cr3+ ions in oxides: a study of the model system MgO:Cr3+

    DEFF Research Database (Denmark)

    Aramburu, J. A.; Garcia-Fernandez, P.; García Lastra, Juan Maria

    2013-01-01

    Seeking to understand why the cubic centre in MgO:Cr3+ has the same 10Dq value as emerald, ab initio cluster and periodic supercell calculations have been performed. It is found that the equilibrium Cr3+-O2- distance, R, in MgO:Cr3+ is equal to 2.03 Å and thus 0.06 Å higher than that measured...... for the emerald. Calculations carried out on the isolated CrO69- complex at R = 2.03 Å give 10Dq = 14 510 cm-1, which is 10% smaller than the experimental figure for MgO:Cr3+. Nevertheless, when the internal electric field, ER(r), due to the rest of the lattice ions is also taken into account, the calculated 10Dq...... = 16 210 cm-1 coincides with the experimental value. Accordingly, the colour shift for different oxides doped with Cr3+ can be well understood on the basis of this extrinsic contribution to 10Dq usually ignored in a ligand field description. The calculated electrostatic potential, VR(r), related to ER(r...

  15. Effect of manganese and chromium on microstructure and toughness of Fe-Cr-Mn alloys resulting from solid-solution treatment

    International Nuclear Information System (INIS)

    Okazaki, Yoshimitsu; Miyahara, Kazuya; Wade, Noboru; Hosoi, Yuzo

    1989-01-01

    This study is aimed at making clear the effect of Mn and Cr on the microstructure and toughness of an Fe-Cr-Mn alloy which is considered as one of the candidate alloys for reduced activation materials for the first wall application of the fusion reactor. The microstructures of Fe-12% Cr-(5∼30)% Mn(mass%) alloys after solution treatment at 1373 K for 3.6 ks are markedly varied with Mn contents; α'(martensite) + δ(ferrite) in 5% Mn alloy, α' + δ + ε(martensite) + γ(austenite) in the 10% Mn alloy, α' + ε + γ in 15% Mn alloy, ε + γ in the 20% Mn alloy, and ε + γ +δ in the 25% Mn alloy, and γ + δ in the 30% Mn alloy. It is to be noted that the δ phase increases with increasing Mn content when the Fe-12% Cr alloy contains more than 25% Mn, which suggests that Mn plays the role of a ferrite former. In Fe-15% Mn-Cr alloy, the δ phase is not observed in the range of Cr contents up to 12%, whereas it is markedly increased with the addition of 16% Cr. C, N and Ni are very helpful in forming the γ phase in these alloys as generally known in Fe-Cr-Ni alloys. The toughness evaluated by the Charpy impact test at 273 K and room temperature is very low in the 5% Mn alloy which consists of the α' and δ phases. It is, however, significantly improved by a small amount of the γ phase and increases with increase of γ phase stability. (author)

  16. The impedance properties of the oxide film on the Ni-Cr-Mo Alloy-22 in neutral concentrated sodium chloride solution

    Energy Technology Data Exchange (ETDEWEB)

    Jakupi, P.; Zagidulin, D.; Noel, J.J. [Department of Chemistry, University of Western Ontario, London, Ontario, N6A-3K7 (Canada); Shoesmith, D.W., E-mail: dwshoesm@uwo.ca [Department of Chemistry, University of Western Ontario, London, Ontario, N6A-3K7 (Canada)

    2011-07-01

    The oxide film properties on Alloy-22 in the applied potential (E) range -600 mV to 600 mV (vs. saturated KCl, Ag/AgCl reference electrode) were characterized by Electrochemical Impedance Spectroscopy (EIS) in near neutral pH, 5 M NaCl solutions, at 30 deg. C. The impedance properties of the film were compared to the chromium content of the film determined by X-ray photoelectron spectroscopy (XPS). The oxide film properties on Alloy-22 may be divided into three applied potential (E) ranges: -600 mV {<=} E < -300 mV, -300 mV {<=} E {<=} 300 mV, and E > 300 mV. For the range -600 mV {<=} E < -300 mV the film resistance (R{sub film}) increases with potential accompanied by an increase in Cr{sub 2}O{sub 3} content; in the range -300 mV {<=} E {<=} 300 mV, R{sub film} values and the Cr{sub 2}O{sub 3} content of the oxide film achieve their maximum values; for E > 300 mV, a decrease in both R{sub film} and Cr{sub 2}O{sub 3} is observed accompanied by a significant increase in Cr(OH){sub 3}. Comparison of the impedance properties for Alloy-22 to those of Ni-Cr alloys indicate that the barrier layer oxide on Alloy-22 contains a lower number of less mobile defects, most likely Cr interstitials. Destruction of the barrier layer for E > 300 mV leads to the formation of a thicker, less protective bilayer, which is high in Mo content.

  17. Si effects on radiation induced segregation in high purity Fe-18Cr-14Ni alloys irradiated by Ni ions

    International Nuclear Information System (INIS)

    Ohta, Joji; Kako, Kenji; Mayuzumi, Masami; Kusanagi, Hideo; Suzuki, Takayoshi

    1999-01-01

    To illustrate the effects of the element Si on radiation induced segregation, which causes irradiation assisted stress corrosion cracking (IASCC), we investigated grain boundary chemistry of high purity Fe-18Cr-14Ni-Si alloys irradiated by Ni ions using FE-TEM. The addition of Si up to 1% does not affect the Cr depletion at grain boundaries, while it slightly enhances the depletion of Fe and the segregation of Ni and Si. The addition of 2% Si causes the depletion of Cr and Fe and the segregation of Ni and Si at grain boundaries. Thus, the Si content should be as low as possible. In order to reduce the depletion of Cr at grain boundaries, which is one of the major causes of IASCC, Si content should be less than 1%. (author)

  18. Results obtained so far with the production of turbine and valve casings made of the new 9% Cr cast steel types G-X 12 CrMoWVNbN 10 11 and G-X 12 CrMoVNbN 91; Erfahrungsbericht ueber die Herstellung von Turbinen- und Ventilgehaeusen aus den neuen 9% Cr-Stahlgusssorten G-X 12 CrMoWVNbN 10 1 1 und G-X 12 CrMoVNbN 91

    Energy Technology Data Exchange (ETDEWEB)

    Schuster, F.; Buberl, A.; Hanus, R. [VOEST-ALPINE STAHL LINZ GmbH, Linz (Austria); Cerjak, H. [Technische Univ., Graz (Austria)

    1996-12-31

    In the course of production start-up of new 9-10% Cr cast steel types, and application of R and D results to practice, the following examinations and modifications have been performed: 1. Reduction of average chromium content from 10.5 to 9.5% in order to suppress delta ferrite segregation, and adjustment of austenite and ferrite stabilizing alloying constituents. 2. Analysis of typical defects in castings, and modification of casting and feeding techniques in compliance with the saturation behaviour of the new 9-10% Cr steels. These measures achieved a reduction of feeding-based flaws (shrinkage) in the last few cast pieces. 3. The good weldability was proven of the new 9-10% Cr steels by means of welding tests and crack-free production and construction welds made in cast pieces. (orig./MM) [Deutsch] Im Zuge der Produktionsaufnahme neuer 9-10% Cr-Stahlgusssorten und der Ueberleitung der F and E Ergebnisse in die betriebliche Praxis wurden folgende Untersuchungen und Anpassungen vorgenommen: 1. Um die Deltaferritausscheidung zu unterdruecken, wurde der mittlere Chromgehalt von 10,5 auf 9,5% abgesenkt und die austenit- und ferritstabilisierenden Legierungselemente besser angepasst. 2. Die Analyse typischer Fehlererscheinungen an Gussstuecken machten eine Anpassung der Giess- und Speisungstechnik an das Saettigungsverhalten der neuen 9-10% Cr-Staehle erforderlich. Diese Massnahmen fuehrten zu einer Verringerung der Speisungsfehler (Lunker) bei den zuletzt abgegossenen Gussstuecken. 3. Bei Schweissversuchen und an Gussstuecken rissfrei ausgefuehrten Fertigungs- und Konstruktionsschweissungen konnte die gute Schweisseignung der neuen 9-10% Cr-Staehle nachgewiesen werden. (orig./MM)

  19. Flexural strength of pure Ti, Ni-Cr and Co-Cr alloys submitted to Nd:YAG laser or TIG welding.

    Science.gov (United States)

    Rocha, Rick; Pinheiro, Antônio Luiz Barbosa; Villaverde, Antonio Balbin

    2006-01-01

    Welding of metals and alloys is important to Dentistry for fabrication of dental prostheses. Several methods of soldering metals and alloys are currently used. The purpose of this study was to assess, using the flexural strength testing, the efficacy of two processes Nd:YAG laser and TIG (tungsten inert gas) for welding of pure Ti, Co-Cr and Ni-Cr alloys. Sixty cylindrical specimens were prepared (20 of each material), bisected and welded using different techniques. Four groups were formed (n=15). I: Nd:YAG laser welding; II- Nd:YAG laser welding using a filling material; III- TIG welding and IV (control): no welding (intact specimens). The specimens were tested in flexural strength and the results were analyzed statistically by one-way ANOVA. There was significant differences (pTIG and laser welding and also between laser alone and laser plus filling material. In conclusion, TIG welding yielded higher flexural strength means than Nd:YAG laser welding for the tested Ti, Co-Cr and Ni-Cr alloys.

  20. Investigation on the oxidation behavior of AlCrVxN thin films by means of synchrotron radiation and influence on the high temperature friction

    Science.gov (United States)

    Tillmann, Wolfgang; Kokalj, David; Stangier, Dominic; Paulus, Michael; Sternemann, Christian; Tolan, Metin

    2018-01-01

    Friction minimization is an important topic which is pursued in research and industry. In addition to the use of lubricants, friction-reducing oxide phases can be utilized which occur during. These oxides are called Magnéli phases and especially vanadium oxides exhibit good friction reducing properties. Thereby, the lubrication effect can be traced back to oxygen deficiencies. AlCrN thin films are being used as coatings for tools which have to withstand high temperatures. A further improvement of AlCrN thin films concerning their friction properties is possible by incorporation of vanadium. This study analyzes the temperature dependent oxidation behavior of magnetron sputtered AlCrVN thin films with different vanadium contents up to 13.5 at.-% by means of X-ray diffraction and X-ray absorption near-edge spectroscopy. Up to 400 °C the coatings show no oxidation. A higher temperature of 700 °C leads to an oxidation and formation of Magnéli phases of the coatings with vanadium contents above 10.7 at.-%. Friction coefficients, measured by ball-on-disk test are correlated with the oxide formation in order to figure out the effect of vanadium oxides. At 700 °C a decrease of the friction coefficient with increasing vanadium content can be observed, due to the formation of VO2, V2O3 and the Magnéli phase V4O7.

  1. Preliminary Microstructural and Microscratch Results of Ni-Cr-Fe and Cr3C2-NiCr Coatings on Magnesium Substrate

    Science.gov (United States)

    Istrate, B.; Munteanu, C.; Lupescu, S.; Benchea, M.; Vizureanu, P.

    2017-06-01

    Thermal coatings have a large scale application in aerospace and automotive field, as barriers improving wear mechanical characteristics and corrosion resistance. In present research, there have been used two types of coatings, Ni-Cr-Fe, respectively Cr3C2-NiCr which were deposited on magnesium based alloys (pure magnesium and Mg-30Y master alloy). There have been investigated the microstructural aspects through scanning electronic microscopy and XRD analysis and also a series of mechanical characteristics through microscratch and indentation determinations. The results revealed the formation of some adherent layers resistant to the penetration of the metallic indenter, the coatings did not suffer major damages. Microstructural analysis highlighted the formation of Cr3C2, Cr7C3, Cr3Ni2, Cr7Ni3, FeNi3, Cr-Ni phases. Also, the apparent coefficient of friction for Ni-Cr-Fe coatings presents superior values than Cr3C2-NiCr coatings.

  2. Synthesis, characterization and stability of Cr(III) and Fe(III) hydroxides

    Energy Technology Data Exchange (ETDEWEB)

    Papassiopi, N.; Vaxevanidou, K.; Christou, C.; Karagianni, E.; Antipas, G.S.E., E-mail: gantipas@metal.ntua.gr

    2014-01-15

    Highlights: • Fe(III)–Cr(III) hydroxides enhance groundwater quality better than pure Cr(III) compounds. • Crystalline Cr(OH){sub 3}·3H{sub 2}O was unstable, with a solubility higher than 50 μg/l. • Amorphous Cr(OH){sub 3}(am) was stable with a solubility lower than 50 μg/l in the range 5.7 < pH < 11. • For mixed Fe{sub 0.75}Cr{sub 0.25}(OH){sub 3}, the stability region was extended to 4.8 < pH < 13.5. -- Abstract: Chromium is a common contaminant of soils and aquifers and constitutes a major environmental problem. In nature, chromium usually exists in the form of two oxidation states, trivalent, Cr(III), which is relatively innocuous for biota and for the aquatic environment, and hexavalent, Cr(VI) which is toxic, carcinogenic and very soluble. Accordingly, the majority of wastewater and groundwater treatment technologies, include a stage where Cr(VI) is reduced to Cr(III), in order to remove chromium from the aqueous phase and bind the element in the form of environmentally stable solid compounds. In the absence of iron the final product is typically of the form Cr(OH){sub 3}·xH{sub 2}O whereas in the presence of iron the precipitate is a mixed Fe{sub (1−x)}Cr{sub x}(OH){sub 3} phase. In this study, we report on the synthesis, characterisation and stability of mixed (Fe{sub x},Cr{sub 1−x})(OH){sub 3} hydroxides as compared to the stability of Cr(OH){sub 3}. We established that the plain Cr(III) hydroxide, abiding to the approximate molecular formula Cr(OH){sub 3}·3H{sub 2}O, was crystalline, highly soluble, i.e. unstable, with a tendency to transform into the stable amorphous hydroxide Cr(OH){sub 3}(am) phase. Mixed Fe{sub 0.75}Cr{sub 0.25}(OH){sub 3} hydroxides were found to be of the ferrihydrite structure, Fe(OH){sub 3}, and we correlated their solubility to that of a solid solution formed by plain ferrihydrite and the amorphous Cr(III) hydroxide. Both our experimental results and thermodynamic calculations indicated that mixed Fe(III)–Cr

  3. Room temperature magnetocaloric effect in Ni-Mn-In-Cr ferromagnetic shape memory alloy thin films

    Energy Technology Data Exchange (ETDEWEB)

    Akkera, Harish Sharma [Functionalnanomaterials Research Lab, Department of Physics, Indian Institute of Technology Roorkee, Uttarakhand-247667 (India); Singh, Inderdeep [Mechanical and Industrial Engineering Department, Indian Institute of Technology Roorkee, Uttarakhand-24667 (India); Kaur, Davinder, E-mail: dkaurfph@iitr.ernet.in [Functionalnanomaterials Research Lab, Department of Physics, Indian Institute of Technology Roorkee, Uttarakhand-247667 (India)

    2017-02-15

    The influence of Cr substitution for In on the martensitic phase transformation and magnetocaloric effect (MCE) has been investigated in Ni-Mn-Cr-In ferromagnetic shape memory alloy (FSMA) thin films fabricated by magnetron sputtering. Temperature dependent magnetization (M-T) measurements demonstrated that the martensitic transformation temperatures (T{sub M}) monotonously increase with the increase of Cr content due to change in valence electron concentration (e/a) and cell volume. From the study of isothermal magnetization curves (M-H), magnetocaloric effect around the martensitic transformation has been investigated in these FSMA thin films. The magnetic entropy change ∆S{sub M} of 7.0 mJ/cm{sup 3}-K was observed in Ni{sub 51.1}Mn{sub 34.9}In{sub 9.5}Cr{sub 4.5} film at 302 K in an applied field of 2 T. Further, the refrigerant capacity (RC) was also calculated for all the films in an applied field of 2 T. These findings indicate that the Cr doped Ni-Mn-In FSMA thin films are potential candidates for room temperature micro-length-scale magnetic refrigeration applications. - Highlights: • The Cr content leads to an increase in the martensitic transformation temperature. • The ∆S{sub M} =7 mJ/cm{sup 3}-K at 302 K was observed in the Ni{sub 51.1}Mn{sub 34.9}In{sub 9.5}Cr{sub 4.5}. • The RC =39.2 mJ/K at 2 T was obtained in Ni{sub 51.1}Mn{sub 34.9}In{sub 9.5}Cr{sub 4.5} film.

  4. Changes induced in a ZnS:Cr-based electroluminescent waveguide structure by intrinsic near-infrared laser radiation

    International Nuclear Information System (INIS)

    Vlasenko, N. A.; Oleksenko, P. F.; Mukhlyo, M. A.; Veligura, L. I.

    2013-01-01

    The causes of changes that occur in a thin-film electroluminescent metal-insulator-semiconductor-insulator-metal waveguide structure based on ZnS:Cr (Cr concentration of ∼4 × 10 20 cm −3 ) upon lasing (λ ≈ 2.6 μm) and that induce lasing cessation are studied. It is established that lasing ceases because of light-scattering inhomogeneities formed in the structure and, hence, optical losses enhance. The origin of the inhomogeneities and the causes of their formation are clarified by studying the surface topology and the crystal structure of constituent layers of the samples before and after lasing. The studies are performed by means of atomic force microscopy and X-ray radiography. It is shown that a substantial increase in the sizes of grains on the surface of the structure is the manifestation of changes induced in the ZnS:Cr film by recrystallization. Recrystallization is initiated by local heating by absorbed laser radiation in existing Cr clusters and quickened by a strong electric field (>1 MV cm −1 ). The changes observed in the ZnS:Cr film are as follows: the textured growth of ZnS crystallites, an increase in the content of Cr clusters, and the appearance of some CrS and a rather high ZnO content. Some ways for improving the stability of lasing in the ZnS:Cr-based waveguide structures are proposed

  5. Effect of carbon and manganese on the microstructure and mechanical properties of 9Cr2WVTa deposited metals

    Science.gov (United States)

    Wang, Jian; Rong, Lijian; Li, Dianzhong; Lu, Shanping

    2017-03-01

    Six 9Cr2WVTa deposited metals with different carbon and manganese contents have been studied to reveal the role of major elements, which guide for the design of welding consumables for reduced activation ferritic/martensitic steel and meet for the requirements of accelerator driven systems-lead fusion reactors. The typical microstructure for the 9Cr2WVTa deposited metals is the lath martensite along with the fine stripe δ-ferrite. The chemical compositions influence the solidification sequence and therefore, change the δ-ferrite content in the deposited metal. The impact toughness for the 9Cr2WVTa deposited metals decreases remarkably when the δ-ferrite content is more than 5.2 vol%, also the impact toughness decreases owing to the high quenching martensite formation. Increasing the level of manganese addition, α phase of each alloy shifts to the bottom right according to the CCT diagram.

  6. Passive behaviour of alloy corrosion-resistant steel Cr10Mo1 in simulating concrete pore solutions with different pH

    International Nuclear Information System (INIS)

    Ai, Zhiyong; Jiang, Jinyang; Sun, Wei; Song, Dan; Ma, Han; Zhang, Jianchun; Wang, Danqian

    2016-01-01

    Highlights: • A new alloy corrosion-resistant steel Cr10Mo1 is developed for reinforcing rebar of concrete in severe environments. • The effects of pH on the passive behaviour of Cr10Mo1 steel compared with plain carbon steel were studied systematically by electrochemical techniques and surface analysis. • The mechanism for self-reinforcing passivity against carbonation of the corrosion-resistant steel is revealed. - Abstract: The passive behaviour of new alloy corrosion-resistant steel Cr10Mo1 and plain carbon steel (as a comparison) in simulating concrete pore solutions of different pH (ranging from 13.5 to 9.0) under open circuit potential conditions, was evaluated by various electrochemical techniques: potentiodynamic polarization, capacitance measurements and electrochemical impedance spectroscopy. The chemical composition and structure of passive films were investigated by X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectroscopy (SIMS). The electrochemical responses of passive films show that Cr10Mo1 steel has an increasing passivity with pH decreasing while carbon steel dose conversely, revealing carbonation does no negative effect on passivation of the corrosion-resistant steel. SIMS reveals that the passive film on the corrosion-resistant steel presents a bilayer structure: an outer layer mainly consisting of Fe oxides and hydroxides, and an inner layer enriched in Cr species, while only a Fe-concentrated layer for carbon steel. According to the XPS analysis results, as the pH decreases, more stable and protective Cr oxides are enriched in the film on Cr10Mo1 steel while Fe oxides gradually decompose. Higher content of Cr oxides in the film layer provides Cr10Mo1 corrosion-resistant steel more excellent passivity at lower pH.

  7. Passive behaviour of alloy corrosion-resistant steel Cr10Mo1 in simulating concrete pore solutions with different pH

    Energy Technology Data Exchange (ETDEWEB)

    Ai, Zhiyong, E-mail: 230139452@seu.edu.cn [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China); Jiang, Jinyang, E-mail: jiangjinyang16@163.com [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China); Sun, Wei, E-mail: sunwei@seu.edu.cn [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China); Song, Dan, E-mail: songdancharls@hhu.edu.cn [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China); College of Mechanics and Materials, Hohai University, Nanjing 210098, Jiangsu (China); Ma, Han, E-mail: mahan-iris@shasteel.cn [Research Institute of Jiangsu Shasteel Iron and Steel, Zhangjiagang 215625, Jiangsu (China); Zhang, Jianchun, E-mail: Zhangjc-iris@shasteel.cn [Research Institute of Jiangsu Shasteel Iron and Steel, Zhangjiagang 215625, Jiangsu (China); Wang, Danqian, E-mail: wonderbaba@126.com [School of Materials Science and Engineering, Southeast University, Nanjing 211189, Jiangsu (China); Jiangsu Key Laboratory of Construction Materials, Nanjing 211189, Jiangsu (China)

    2016-12-15

    Highlights: • A new alloy corrosion-resistant steel Cr10Mo1 is developed for reinforcing rebar of concrete in severe environments. • The effects of pH on the passive behaviour of Cr10Mo1 steel compared with plain carbon steel were studied systematically by electrochemical techniques and surface analysis. • The mechanism for self-reinforcing passivity against carbonation of the corrosion-resistant steel is revealed. - Abstract: The passive behaviour of new alloy corrosion-resistant steel Cr10Mo1 and plain carbon steel (as a comparison) in simulating concrete pore solutions of different pH (ranging from 13.5 to 9.0) under open circuit potential conditions, was evaluated by various electrochemical techniques: potentiodynamic polarization, capacitance measurements and electrochemical impedance spectroscopy. The chemical composition and structure of passive films were investigated by X-ray photoelectron spectroscopy (XPS) and secondary ion mass spectroscopy (SIMS). The electrochemical responses of passive films show that Cr10Mo1 steel has an increasing passivity with pH decreasing while carbon steel dose conversely, revealing carbonation does no negative effect on passivation of the corrosion-resistant steel. SIMS reveals that the passive film on the corrosion-resistant steel presents a bilayer structure: an outer layer mainly consisting of Fe oxides and hydroxides, and an inner layer enriched in Cr species, while only a Fe-concentrated layer for carbon steel. According to the XPS analysis results, as the pH decreases, more stable and protective Cr oxides are enriched in the film on Cr10Mo1 steel while Fe oxides gradually decompose. Higher content of Cr oxides in the film layer provides Cr10Mo1 corrosion-resistant steel more excellent passivity at lower pH.

  8. Microstructures of neutron-irradiated Fe-12Cr-XMn (X=15-30) ternary alloys

    International Nuclear Information System (INIS)

    Miyahara, K.; Hosoi, Y.; Garner, F.A.

    1992-01-01

    The objective of this effort is to determine the factors which control the stability of irradiated alloys proposed for reduced activation applications. The Fe-Cr-Mn alloy system is being studied as an alternative to the Fe-Cr-Ni system because of the need to reduce long-term radioactivation in fusion-power devices. In this study, four Fe-12Cr-XMn (X =15, 20, 25, 30 wt%) alloys were irradiated in the Fast Flux Test Facility to 20 dpa at 643K and 40 dpa at 679, 793, and 873K to investigate the influence of manganese content on void swelling and phase stability. The results confirm and expand the results of earlier studies that indicate that the Fe-Cr-Mn system is relatively unstable compared to that of the Fe-Cr-Ni system, with alpha and sigma phases forming as a consequence of thermal aging or high temperature irradiation

  9. Content

    DEFF Research Database (Denmark)

    Keiding, Tina Bering

    secondary levels. In subject matter didactics, the question of content is more developed, but it is still mostly confined to teaching on lower levels. As for higher education didactics, discussions on selection of content are almost non-existent on the programmatic level. Nevertheless, teachers are forced...... curriculum, in higher education, and to generate analytical categories and criteria for selection of content, which can be used for systematic didactical reflection. The larger project also concerns reflection on and clarification of the concept of content, including the relation between content at the level......Aim, content and methods are fundamental categories of both theoretical and practical general didactics. A quick glance in recent pedagogical literature on higher education, however, reveals a strong preoccupation with methods, i.e. how teaching should be organized socially (Biggs & Tang, 2007...

  10. Determination of Cr2O3 in chrome-tanned leather by radionuclide-excited X-ray fluorescence analysis

    International Nuclear Information System (INIS)

    Melich, M.; Palagyi, S.; Kern, M.

    1989-01-01

    Preliminary results on the determination of Cr 2 O 3 in chrome-tanned leather by measuring the content of Cr by means of radionuclide-excited XRF analysis are reported. For excitation a 3.7 GBq 238 Pu source was used and the characteristic K X-rays of Cr were detected with a planar Si(Li) detector. Both smooth and rough sides of the leather were analyzed directly or with a pair of V/Ti balanced filters. A fairly good correlation was found between Cr Kx counts of the rough side and the Cr 2 O 3 concentrations determined chemically in the range of 3.5 to 6.0% Cr 2 O 3 . The method renders possible a rapid and non-destructive determination of Cr 2 O 3 in various leather samples. (author)

  11. Influence of Ni-Cr substitution on the magnetic and electric properties of magnesium ferrite nanomaterials

    Energy Technology Data Exchange (ETDEWEB)

    Iqbal, Muhammad Javed, E-mail: mjiqauchem@yahoo.com [Surface and Solid State Chemistry Laboratory, Department of Chemistry, Quaid-i-Azam University, Islamabad 45320 (Pakistan); Ahmad, Zahoor [Surface and Solid State Chemistry Laboratory, Department of Chemistry, Quaid-i-Azam University, Islamabad 45320 (Pakistan); Meydan, Turgut [Wolfson Centre for Magnetics, School of Engineering, Cardiff University, Cardiff CF24 3AA (United Kingdom); Nlebedim, Ikenna Cajetan [Ames Laboratory of US Department of Energy, Ames, IA 50011 (United States)

    2012-02-15

    Graphical abstract: Variation of saturation magnetization (M{sub S}) and magnetocrystalline anisotropy coefficient (K{sub 1}) with Ni-Cr content for Mg{sub 1-x}Ni{sub x}Cr{sub x}Fe{sub 2-x}O{sub 4} (x = 0.0-0.5). Highlights: Black-Right-Pointing-Pointer Mg{sub 1-x}Ni{sub x}Cr{sub x}Fe{sub 2-x}O{sub 4} are synthesized by novel PEG assisted microemulsion method. Black-Right-Pointing-Pointer High field regime of M-H loops are modeled using Law of Approach to saturation. Black-Right-Pointing-Pointer A considerable increase in the value of M{sub S} from 148 kA/m to 206 kA/m is achieved Black-Right-Pointing-Pointer {rho}{sup RT} enhanced to the order of 10{sup 9} {Omega}cm at potential operational range around 300 K. -- Abstract: The effect of variation of composition on the structural, morphological, magnetic and electric properties of Mg{sub 1-x}Ni{sub x}Cr{sub x}Fe{sub 2-x}O{sub 4} (x = 0.0-0.5) nanocrystallites is presented. The samples were prepared by novel polyethylene glycol (PEG) assisted microemulsion method with average crystallite size of 15-47 nm. The microstructure, chemical, and phase analyses of the samples were studied by the scanning electron microscopy (SEM), atomic force microscopy (AFM), energy dispersive X-ray fluorescence (ED-XRF), and X-ray diffraction (XRD). Compositional variation greatly affected the magnetic and structural properties. The high-field regimes of the magnetic loops are modelled using the Law of Approach (LOA) to saturation in order to extract information about their anisotropy and the saturation magnetization. Thermal demagnetization measurements are carried out using VSM and significant enhancement of the Curie temperature from 681 K to 832 K has been achieved by substitution of different contents of Ni-Cr. The dc-electrical resistivity ({rho}{sup RT}) at potential operational range around 300 K is increased from 7.5 Multiplication-Sign 10{sup 8} to 4.85 Multiplication-Sign 10{sup 9} {Omega}cm with the increase in Ni-Cr contents

  12. RIGScan CR: RIGScan CR49.

    Science.gov (United States)

    2004-01-01

    RIGScan CR49, a 125I-labelled CR monoclonal antibody directed against the tumour-associated antigen TAG-72, is undergoing development with Neoprobe for the intraoperative detection of metastatic colorectal cancer. The Neoprobe's proprietary RIGS (radioimmunoguided surgery) technology combines an injectable radiolabelled cancer-targeting agent and hand-held radiation detection probe that emits an audible tone when located tissue has accumulated a significant amount of the radioactive agent. Neoprobe's RIGS technology also includes a patented surgical method providing surgeons with real-time information to locate tumour deposits that can not be detected by other conventional methods. The RIGS technology has been evaluated in late clinical studies for the detection of adenocarcinomas including primary colorectal, gastrointestinal, breast, ovarian, pancreatic, prostate and neuroendocrine/endocrine. Neoprobe signed an option agreement for its first-generation RIGScan compound, RIGScan CR, with OncoSurg Inc. (formerly NuRigs Ltd). The second-generation humanised RIGScan CR agent was also optionally licensed to OncoSurg Inc. In 1997, Neoprobe filed for approval with the US FDA and the EMEA for RIGScan CR for the intraoperative detection of metastatic colorectal cancer. Both regulatory agencies have requested additional clinical data. On 19 April 2004, Neoprobe announced that it had met with the US FDA to discuss its position on submitting additional clinical information in response to the FDA's questions regarding the Biologic Licence Application (BLA) for RIGScan CR49. The company provided the FDA with new information related to a survival differential for patients whose colorectal cancer was evaluated with RIGScan CR49. The information was not available at the time of the BLA's submission in 1997. The agency indicated that it would consider accepting survival data from one of the two phase III trials, NEO2-14, but not from another trial NEO2-13, as supportive data for a

  13. Microstructure characteristics and temperature-dependent high cycle fatigue behavior of advanced 9% Cr/CrMoV dissimilarly welded joint

    International Nuclear Information System (INIS)

    Wu, Qingjun; Lu, Fenggui; Cui, Haichao; Ding, Yuming; Liu, Xia; Gao, Yulai

    2014-01-01

    Advanced 9% Cr and CrMoV steels chosen as candidate materials are first welded by narrow-gap submerged arc welding (NG-SAW) to fabricate the heavy section rotor. The present work focuses on studying the high-cycle fatigue (HCF) behavior of advanced 9% Cr/CrMoV dissimilarly welded joint at different temperatures. Conditional fatigue strength of this dissimilarly welded joint was obtained by HCF tests at room temperature (RT), 400 °C and 470 °C. It was observed that the failure occurred at the side of CrMoV base metal (BM), weld metal (WM) and heat affected zone (HAZ) of CrMoV side over 5×10 7 cycles for the specimens tested at RT, 400 °C and 470 °C. The detailed microstructures of BMs, WMs and HAZs as well as fracture appearance were observed by optical microscopy (OM) and scanning electron microscopy (SEM). Precipitation and aggregation of carbides along the grain boundaries were clearly detected with the increase of temperature, which brought a negative effect on the fatigue properties. It is interesting to note that the inclusion size leading to crack initiation became smaller for the HCF test at higher temperature. Therefore, reduction in the inclusion size in a welded joint helps to improve the HCF performance at high temperature

  14. Microstructure characteristics and temperature-dependent high cycle fatigue behavior of advanced 9% Cr/CrMoV dissimilarly welded joint

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Qingjun [Shanghai Key Laboratory of Materials Laser Processing and Modification, Shanghai Jiao Tong University, Shanghai 200240 (China); Lu, Fenggui, E-mail: Lfg119@sjtu.edu.cn [Shanghai Key Laboratory of Materials Laser Processing and Modification, Shanghai Jiao Tong University, Shanghai 200240 (China); Shanghai Key Laboratory of Modern Metallurgy and Materials Processing, Shanghai University, Shanghai 200072 (China); Cui, Haichao [Shanghai Key Laboratory of Materials Laser Processing and Modification, Shanghai Jiao Tong University, Shanghai 200240 (China); Ding, Yuming; Liu, Xia [Shanghai Turbine Plant of Shanghai Electric Power Generation Equipment Co. Ltd., Shanghai 200240 (China); Gao, Yulai, E-mail: ylgao@shu.edu.cn [Shanghai Key Laboratory of Modern Metallurgy and Materials Processing, Shanghai University, Shanghai 200072 (China)

    2014-10-06

    Advanced 9% Cr and CrMoV steels chosen as candidate materials are first welded by narrow-gap submerged arc welding (NG-SAW) to fabricate the heavy section rotor. The present work focuses on studying the high-cycle fatigue (HCF) behavior of advanced 9% Cr/CrMoV dissimilarly welded joint at different temperatures. Conditional fatigue strength of this dissimilarly welded joint was obtained by HCF tests at room temperature (RT), 400 °C and 470 °C. It was observed that the failure occurred at the side of CrMoV base metal (BM), weld metal (WM) and heat affected zone (HAZ) of CrMoV side over 5×10{sup 7} cycles for the specimens tested at RT, 400 °C and 470 °C. The detailed microstructures of BMs, WMs and HAZs as well as fracture appearance were observed by optical microscopy (OM) and scanning electron microscopy (SEM). Precipitation and aggregation of carbides along the grain boundaries were clearly detected with the increase of temperature, which brought a negative effect on the fatigue properties. It is interesting to note that the inclusion size leading to crack initiation became smaller for the HCF test at higher temperature. Therefore, reduction in the inclusion size in a welded joint helps to improve the HCF performance at high temperature.

  15. Structure and magnetic properties of Co{sub 2}(Cr{sub 1−x}Fe{sub x})Al, (0 ≤ x ≤ 1) Heusler alloys prepared by mechanical alloying

    Energy Technology Data Exchange (ETDEWEB)

    Srivastava, Yogesh, E-mail: 123209001_yogesh@manit.ac.in [Department of Materials Science & Metallurgical Engineering, Ceramic & Powder Metallurgy Laboratory, Maulana Azad National Institute of Technology, Bhopal, Madhya Pradesh 462003 (India); Vajpai, Sanjay Kumar, E-mail: vajpaisk@gmail.com [Department of Materials Science & Metallurgical Engineering, Maulana Azad National Institute of Technology, Bhopal, Madhya Pradesh 462003 (India); Srivastava, Sanjay, E-mail: s.srivastava.msme@gmail.com [Department of Materials Science & Metallurgical Engineering, Maulana Azad National Institute of Technology, Bhopal, Madhya Pradesh 462003 (India)

    2017-07-01

    Highlights: • A series of nanocrystalline Co{sub 2}(Cr{sub 1−x}Fe{sub x})Al Heusler alloy by powder metallurgy. • Effect of substitution of Fe for Cr on the microstructure and magnetic properties. • Increasing amounts of B2 type disordered structure with increasing Fe content. • Enhanced Ms, Mr, Hc, and Tc with increasing Fe content. • Relative magnetic anisotropy decreased with increasing Fe content. - Abstract: In the present study, a series of nanocrystalline Co{sub 2}(Cr{sub 1−x}Fe{sub x})Al Heusler alloy powders were successfully prepared by high energy ball milling and the effect of substitution of Fe for Cr on the microstructure and magnetic properties was investigated in detail. The Co{sub 2}CrAl alloy powder consisted of only A2 type disordered structure whereas the substitution of Cr by Fe led to the appearance of increasing amounts of B2 type disordered structure along with A2 type structure. All the Co{sub 2}(Cr{sub 1−x}Fe{sub x})Al Heusler alloy powders demonstrated high spontaneous magnetization together with a very small hysteresis losses. The saturation magnetization, remanence, coercivity, and Curie temperature increased with increasing Fe content. The increasing magnetization with increasing Fe content was attributed to the replacement of antiferromagnetic Cr by strongly ferromagnetic Fe and an increasing amounts of relatively more ordered, atomically as well as ferromagnetically, B2 structure as compared to that of A2 phase. The increment in remanence and coercivity with increasing Fe content were associated with the variation in microstructural characteristics, such as grain size, lattice defects, and the presence of small amounts of magnetic/nonmagnetic secondary phases. The increment in Curie temperature with increasing Fe content was attributed to the enhancement of d-d exchange interaction due to the possible occupancy of vacant sites by Fe atoms. All the Heusler alloys indicated extremely low magnetic anisotropy and the

  16. A simple Cr(VI)–S(IV)–O{sub 2} system for rapid and simultaneous reduction of Cr(VI) and oxidative degradation of organic pollutants

    Energy Technology Data Exchange (ETDEWEB)

    Yuan, Yanan; Yang, Shaojie [Department of Environmental Science, Hubei Key Lab of Biomass Resource Chemistry and Environmental Biotechnology, School of Resources and Environmental Science, Wuhan University, 430079 (China); Zhou, Danna, E-mail: zdncug@163.com [Faculty of Material Science and Chemistry, China University of Geosciences, Wuhan 430074 (China); Wu, Feng [Department of Environmental Science, Hubei Key Lab of Biomass Resource Chemistry and Environmental Biotechnology, School of Resources and Environmental Science, Wuhan University, 430079 (China)

    2016-04-15

    Highlights: • Rapid and simultaneous reduction of Cr(VI) and degradation of organic pollutants occur. • Oxysulfur radicals generated in Cr(VI)–S(IV)–O{sub 2} system oxidize the organic pollutants. • Acidic pH facilitates the reactions from both directions of reduction and oxidation. • Degradation potential of aromatic amines depends on the substituted groups. • Cr(VI)–S(IV)–O{sub 2} system is promising for “waste control by waste”. - Abstract: Hexavalent chromium (Cr(VI)), a heavy-metal contaminant, can be easily reduced to less toxic trivalent chromium (Cr(III)) by sulfite ions (S(IV)). However, S(IV) has not drawn as much attention as the ferrous ion has. We report herein a novel Cr(VI)–S(IV)–O{sub 2} system containing sulfite ions that rapidly and simultaneously reduces Cr(VI) and oxidize organic pollutants in the presence of oxygen in aqueous solutions. This Cr(VI)–S(IV)-O{sub 2} system contains the initiator Cr(VI), the reductant S(IV), and the oxidant O{sub 2}, which produce oxysulfur radicals (mainly SO{sub 4}·{sup −} and SO{sub 5}·{sup −}) and hydroxyl radicals (OH·). The Cr(VI)/S(IV) molar ratio, pH, and oxygen content play important roles in the entire reaction system. Acidic conditions (pH 3.0) facilitated degradation of organic compounds and reduction of Cr(VI) as well. In addition, experiments of rapid degradation of several kinds of organic pollutants such as azo dye (acid orange 7, AO7), aniline, phenol, bisphenol A etc were also conducted. Preliminary results show that the removal rates of the analogs of phenols or aromatic amines in this Cr(VI)–S(IV)–O{sub 2} system have a relationship with the electronic parameters (Hammett constant, σ) of the substituted groups. Thus, the Cr(VI)–S(IV)–O{sub 2} system, provides an excellent strategy of “waste control by waste” for removing multiple industrial contaminants.

  17. Optimization of Arc-Sprayed Ni-Cr-Ti Coatings for High Temperature Corrosion Applications

    Science.gov (United States)

    Matthews, S.; Schweizer, M.

    2013-04-01

    High Cr content Ni-Cr-Ti arc-spray coatings have proven successful in resisting the high temperature sulfidizing conditions found in black liquor recovery boilers in the pulp and paper industry. The corrosion resistance of the coatings is dependent upon the coating composition, to form chromium sulfides and oxides to seal the coating, and on the coating microstructure. Selection of the arc-spray parameters influences the size, temperature and velocity of the molten droplets generated during spraying, which in turn dictates the coating composition and formation of the critical coating microstructural features—splat size, porosity and oxide content. Hence it is critical to optimize the arc-spray parameters in order to maximize the corrosion resistance of the coating. In this work the effect of key spray parameters (current, voltage, spray distance and gas atomizing pressure) on the coating splat thickness, porosity content, oxide content, microhardness, thickness, and surface profile were investigated using a full factorial design of experiment. Based on these results a set of oxidized, porous and optimized coatings were prepared and characterized in detail for follow-up corrosion testing.

  18. Effects of Zr Addition on Strengthening Mechanisms of Al-Alloyed High-Cr ODS Steels.

    Science.gov (United States)

    Ren, Jian; Yu, Liming; Liu, Yongchang; Liu, Chenxi; Li, Huijun; Wu, Jiefeng

    2018-01-12

    Oxide dispersion strengthened (ODS) steels with different contents of zirconium (denoted as 16Cr ODS, 16Cr-0.3Zr ODS and 16Cr-0.6Zr ODS) were fabricated to investigate the effects of Zr on strengthening mechanism of Al-alloyed 16Cr ODS steel. Electron backscatter diffraction (EBSD) results show that the mean grain size of ODS steels could be decreased by Zr addition. Transmission electron microscope (TEM) results indicate that Zr addition could increase the number density but decrease the mean diameter and inter-particle spacing of oxide particles. Furthermore, it is also found that in addition to Y-Al-O nanoparticles, Y-Zr-O oxides with finer size were observed in 16Cr-0.3Zr ODS and 16Cr-0.6Zr ODS steels. These changes in microstructure significantly increase the yield strength (YS) and ultimate tensile strength (UTS) of ODS steels through mechanisms of grain boundary strengthening and dispersion strengthening.

  19. Effect of d electrons on defect properties in equiatomic NiCoCr and NiCoFeCr concentrated solid solution alloys

    Science.gov (United States)

    Zhao, Shijun; Egami, Takeshi; Stocks, G. Malcolm; Zhang, Yanwen

    2018-01-01

    The role of d electrons in determining distributions of formation and migration energies for point defects in equiatomic NiCoCr and NiCoFeCr concentrated solid solution alloys (CSAs) are studied regarding electron density deformation flexibility based on first-principles calculations. The disordered state is taken into account by constructing special quasirandom structures. The migration barriers are determined by directly optimizing the saddle point. It is found that the formation energies of interstitials in CSAs are lower than those in pure Ni, whereas the formation energies of vacancies are higher. In both NiCoCr and NiCoFeCr, Co-related dumbbell interstitials exhibit lower formation energies. Notably, the distributions of migration energies for Cr interstitials and vacancies exhibit a remarkable overlap region. A detailed analysis of electronic properties reveals that the electronic charge deformation flexibility regarding eg to t2g transition has a dominant effect on defect energetics for different elements in CSAs. Thus the electron deformation ability is suggested as a key factor in understanding the peculiar defect behavior in CSAs.

  20. Fretting Corrosion Behavior of Experimental Ti-20Cr Compared to Titanium.

    Science.gov (United States)

    Sawada, Tomofumi; Schille, Christine; Almadani, Atif; Geis-Gerstorfer, Jürgen

    2017-02-17

    Experimental cast titanium alloys containing 20 mass% chromium (Ti-20Cr) show preferable mechanical properties and a good corrosion resistance. This study evaluated the fretting corrosion behavior of Ti-20Cr. Ti-20Cr ( n = 4) and commercially pure titanium (CP-Ti, n = 6) disk specimens were used. The fretting corrosion test was performed by electrochemical corrosion at 0.3 V in 0.9% saline solution and mechanical damage using 10 scratching cycles with three different scratching speeds (10-40 mm/s) at 10 N. After testing, the activation peak, repassivation time and surface morphology of each specimen were analyzed. The differences between the results were tested by parametric tests (α = 0.05). The average activation peaks were significantly higher in CP-Ti than in Ti-20Cr ( p Ti. Slight differences in the repassivation time were observed between the materials at every scratching speed; faster scratching speeds showed shorter repassivation times in both materials ( p Ti showed severe damage and significantly higher wear depth than Ti-20Cr ( p < 0.05). In conclusion, adding chromium to titanium reduced surface damage and improved the fretting corrosion resistance.

  1. Cr3+ and Cr4+ luminescence in glass ceramic silica

    International Nuclear Information System (INIS)

    Martines, Marco A.U.; Davolos, Marian R.; Jafelicci, Miguel Junior; Souza, Dione F. de; Nunes, Luiz A.O.

    2008-01-01

    This paper reports on the effect of glass ceramic silica matrix on [CrO 4 ] 4- and Cr 2 O 3 NIR and visible luminescence. Chromium-containing silica was obtained by precipitation from water-glass and chromium nitrate acid solution with thermal treatment at 1000 deg. C. From XRD results silica and silica-chromium samples are crystalline. The chromium emission spectrum presents two main broad bands: one in the NIR region (1.1-1.7μm) and other in the visible region (0.6-0.7μm) assigned to Cr 4+ and to Cr 3+ , respectively. This thermal treated glass ceramic silica-chromium sample stabilizes the [CrO 4 ] 4- where Cr 4+ substitutes for Si 4+ and also hexacoordinated Cr 3+ group probably as segregated phase in the system. It can be pointed out that luminescence spectroscopy is a powerful tool for detecting the two chromium optical centers in the glass ceramic silica

  2. Electroless siliconizing Fe-3% Cr-3% Si alloy

    International Nuclear Information System (INIS)

    Nurlina, Enung; Darmono, Budy; Purwadaria, Sunara

    2000-01-01

    In this research Fe-3%Cr-3%Mo-3%Si and Fe-3%Cr-3%Cu-3%Si alloys had been coated by silicon metal without electricity current which knows as electroless siliconizing. Coating was conducted by immersed sampler into melt fluoride-chloride salt bath at temperature of 750 o C for certain period. The layer consisted of Fe3Si phase. Observation by microscope optic and EDAX showed that the silicide layer were thick enough, adherent, free for crack and had silicon content on the surface more than 15%. The growth rate of silicide layer followed parabolic rate law, where the process predominantly controlled by interdiffusion rate in the solid phase. Key words : electroless siliconizing, the melt fluoride- chloride salt mix, silicide layer

  3. Application of a three-feature dispersed-barrier hardening model to neutron-irradiated Fe-Cr model alloys

    Science.gov (United States)

    Bergner, F.; Pareige, C.; Hernández-Mayoral, M.; Malerba, L.; Heintze, C.

    2014-05-01

    An attempt is made to quantify the contributions of different types of defect-solute clusters to the total irradiation-induced yield stress increase in neutron-irradiated (300 °C, 0.6 dpa), industrial-purity Fe-Cr model alloys (target Cr contents of 2.5, 5, 9 and 12 at.% Cr). Former work based on the application of transmission electron microscopy, atom probe tomography, and small-angle neutron scattering revealed the formation of dislocation loops, NiSiPCr-enriched clusters and α‧-phase particles, which act as obstacles to dislocation glide. The values of the dimensionless obstacle strength are estimated in the framework of a three-feature dispersed-barrier hardening model. Special attention is paid to the effect of measuring errors, experimental details and model details on the estimates. The three families of obstacles and the hardening model are well capable of reproducing the observed yield stress increase as a function of Cr content, suggesting that the nanostructural features identified experimentally are the main, if not the only, causes of irradiation hardening in these model alloys.

  4. Mechanical, tribological and corrosion properties of CrBN films deposited by combined direct current and radio frequency magnetron sputtering

    International Nuclear Information System (INIS)

    Jahodova, Vera; Ding, Xing-zhao; Seng, Debbie H.L.; Gulbinski, W.; Louda, P.

    2013-01-01

    Cr–B–N films were deposited on stainless steel substrates by a combined direct current and radio frequency (RF) reactive unbalanced magnetron sputtering process using two elemental Cr and one compound BN targets. Boron content in the as-deposited films was qualitatively analyzed by time-of-flight secondary ion mass spectroscopy. Films' microstructure, mechanical and tribological properties were characterized by X-ray diffraction, nanoindentation and pin-on-disk tribometer experiments. Corrosion behavior of the Cr–B–N films was evaluated by electrochemical potentiodynamic polarization method in a 3 wt.% NaCl solution. All the films were crystallized into a NaCl-type cubic structure. At lower RF power applied on the BN target (≤ 600 W), films are relatively randomly oriented, and films' crystallinity increased with increasing RF power. With increasing RF power further (≥ 800 W), films became (200) preferentially oriented, and films' crystallinity decreased gradually. With incorporation of a small amount of boron atoms into the CrN films, hardness, wear- and corrosion-resistance were all improved evidently. The best wear and corrosion resistance was obtained for the film deposited with 600 W RF power applied on the BN target. - Highlights: • CrBN films deposited by direct current and radio frequency magnetron sputtering. • CrBN exhibited higher hardness, wear- and corrosion-resistance than pure CrN. • The best wear- and corrosion-resistant film was deposited with 600 W RF power

  5. Structure and magnetic properties of Gd2Co17-xCr x (1.17 ≤ x ≤ 3.0) compounds

    International Nuclear Information System (INIS)

    Fuquan, B.; Tegus, O.; Dagula, W.; Brueck, E.; Klaasse, J.C.P.; Buschow, K.H.J.

    2007-01-01

    The structure and magnetic properties of Gd 2 Co 17-x Cr x (1.17 ≤ x ≤ 3.0) compounds have been investigated by means of X-ray diffraction (XRD) and magnetization measurements. The powder X-ray diffraction patterns show that all samples crystallize as a single phase with the rhombohedral Th 2 Zn 17 -type structure. The lattice parameters a and the unit cell volume V increases slightly with increasing Cr content, but the c parameter varies in a less simple way with increasing Cr content. The X-ray diffraction patterns of the magnetically aligned samples show that all compounds investigated have uniaxial anisotropy. Spin reorientation phenomena occur in all of the compounds. The Curie temperature T C , the spin reorientation temperature T sr , the spontaneous magnetization M 0 and the saturation magnetization M s decrease with the increasing Cr content. The anisotropy constant K 1 and the anisotropy field B a of the compounds at room temperature reach a maximum for x = 1.76. The M 0 and M s increase with increasing temperature from 5 K to 300 K. The easy-axis anisotropy of all compounds changes to easy-plane anisotropy at low temperatures and the spin reorientation phenomena are more pronounced for low Cr concentration

  6. 51Cr-ethylenediaminetetraacetic acid absorption test

    International Nuclear Information System (INIS)

    Aabakken, L.

    1989-01-01

    The 51 Cr-ethylenediaminetetraacetic acid (EDTA) absorption test was evaluated in 83 healthy, male volunteers. Base-line 24 h excretion after peroral administration ranged from 0.88% to 7.96%, with a higher median absorption than reported by most authors (2.45%). However, the reproducibility and stability of the method and the reproducibility of the results were satisfactory. Urinary excretion after intraduodenal installation (n=18) was comparable to that seen after peroral test dose administration, indicating a limited significance of gastric 51 Cr-EDTA absorption under normal conditions. In 16 subjects a single intake of alcohol immediately before the test gave a modest and short-lasting increase in 51 Cr-EDTA absorption. No correlation was seen to body mass index, creatinine clearance, urinary volume, or small-bowel transit time, possibly reducing the number of confounding factors in the evaluation of absorption data. A small but significant negative correlation was, however, found to body surface area and age

  7. Heavy metals in fish tissues/stomach contents in four marine wild commercially valuable fish species from the western continental shelf of South China Sea.

    Science.gov (United States)

    Gu, Yang-Guang; Lin, Qin; Huang, Hong-Hui; Wang, Liang-Gen; Ning, Jia-Jia; Du, Fei-Yan

    2017-01-30

    The concentrations of heavy metals (Cd, Pb, Cr, Ni, Cu and Zn) were determined in four commercially valuable fish species (Thunnus obesus, Decapterus lajang, Cubiceps squamiceps and Priacanthus macracanthus), collected in the western continental shelf of the South China Sea. Concentrations of Cd, Pb, Cr, Ni, Cu, and Zn in fish muscles were 0.006-0.050, 0.13-0.68, 0.18-0.85, 0.11-0.25, 0.12-0.77, and 2.41-4.73μg/g, wet weight, respectively. Concentrations of heavy metals in all species were below their acceptable daily upper limit, suggesting human consumption of these wild fish species may be safe, with health risk assessment based on the target hazard quotients (THQ) and total THQ, indicating no significant adverse health effects with consumption. The average concentrations of Zn were higher in gills than in stomach contents, backbones or muscle, while conversely, the other heavy metals had higher concentrations in stomach contents than in other tissues. Copyright © 2016 Elsevier Ltd. All rights reserved.

  8. Effects of Al addition and minor elements on oxidation behaviour of FeCr alloys

    International Nuclear Information System (INIS)

    Herbelin, J.M.; Mantel, M.

    1995-01-01

    It is shown that the addition of aluminium is very effective for the high temperature oxidation resistance of FeCr alloys. 1% aluminium produces a continuous protective Al 2 O 3 oxide for FeCr alloy that contains more than 13% of chromium. However this aluminium content is not enough for the high temperature resistance of thin foils and a 5% aluminium content is needed since the substrate plays the role of an aluminium reserve susceptible to oxidation. Impurity elements such as sulphur are detrimental and give rise to scaling of the oxide layer. Active elements such as Y, Ce, La, Zr are therefore necessary to tie up sulphur and increase the life of the alloys. (orig.)

  9. Study on the prediction of soil heavy metal elements content based on visible near-infrared spectroscopy

    Science.gov (United States)

    Liu, Jinbao; Zhang, Yang; Wang, Huanyuan; Du, Yichun

    2018-06-01

    The estimation of soils heavy metal content can reflect the impending surroundings of surface, which lays theoretical foundation for using covered vegetation to monitor environment and investigate resource. In this study, the contents of Cr, Mn, Ni, Cu, Zn, As, Cd, Hg and Pb in 44 soil samples were collected from Fufeng County, Yangling County and Wugong County, Shaanxi Province and were used as data sources. ASD FieldSpec HR (350-2500 nm), and then the NOR, MSC and SNV of the reflectance were pretreated, the first deviation, second deviation and reflectance reciprocal logarithmic transformation were carried out. The optimal spectroscopy estimation model of nine heavy metal elements of Cr, Mn, Ni, Cu, Zn, As, Cd, Hg and Pb was established by regression method. Comparing the diffuse reflectance characteristics of different heavy metal contents and the effect of different pretreatment methods on the establishment of soil heavy metal spectral inversion model. The results of chemical analysis show that there was a serious Hg pollution in the study area, and the Cd content was close to the critical value. The results show that: (1) NOR, MSC and SNV were adopted for the acquisition of visible near-infrared. Combining differential transformation can improve the information of heavy metal elements in the soil, and use the correlation band energy Significantly improve the stability and predictability of the model. (2) The modeling accuracy of the optimal model of nine heavy metal spectra of Cr, Mn, Ni, Cu, Zn, As, Cd, Hg and Pb by PLSR method were 0.70, 0.79, 0.69, 0.81, 0.86, 0.58, 0.55, 0.99, 0.62. (3) The optimal estimation model of different elements using different treatment methods has better stability and higher precision, and can realize the rapid prediction of nine kinds of heavy metal elements in this region.

  10. Distribution of Cr atoms in the surface zone of Fe-rich Fe–Cr alloys quenched into various media: Mössbauer spectroscopic study

    International Nuclear Information System (INIS)

    Dubiel, Stanisław M.; Cieślak, Jakub; Żukrowski, Jan

    2015-01-01

    Graphical abstract: Chromium depletion, Δx = x_k − x, in Fe_1_0_0_−_xCr_x (x = 2.2, 3.9, 6.4, 8.5, 10.25, 10.75, 14.9, 15.15) alloys quenched into LN (left panel) and those quenched onto brass (right panel) as found from CEMS (pre surface zone) and TRANS (bulk) Mössbauer spectra (x_k – Cr content in the pre surface or bulk as estimated from the average hyperfine field found for the quenched samples). - Highlights: • Effect of quenching media on Cr atom distribution in Fe–Cr alloys was determined. • Significant differences between bulk and pre surface zone were revealed. • Quenching into water and LH resulted in surface oxidation of samples. • Samples quenched onto a block of brass were not oxidized. - Abstract: Effect of a quenching medium (water, liquid nitrogen and block of brass) on a distribution of Cr atoms in the surface zone of Fe_1_0_0_−_xCr_x (x ≤ 19) alloys was studied with the Mössbauer spectroscopy. The distribution of Cr atoms was expressed in terms of the Cowley–Warren short-range order (SRO) parameters: 〈α_1〉 for the first neighbor-shell, 〈α_2〉 for the second neighbor-shell and 〈α_1_2〉 for both neighbor-shells. It was revealed that none of the quenching media resulted in a random distribution of atoms, yet the degree of randomness was the highest for the samples quenched onto the block of brass. The quenching into water and liquid nitrogen caused a partial oxidation of samples’ surface accompanied by a chromium depletion of the bulk. Quantitative analysis of various phases in the studied samples both in their bulk as well as in pre surface zones was carried out.

  11. Bulk and surface properties of liquid Al-Cr and Cr-Ni alloys

    International Nuclear Information System (INIS)

    Novakovic, R

    2011-01-01

    The energetics of mixing and structural arrangement in liquid Al-Cr and Cr-Ni alloys has been analysed through the study of surface properties (surface tension and surface segregation), dynamic properties (chemical diffusion) and microscopic functions (concentration fluctuations in the long-wavelength limit and chemical short-range order parameter) in the framework of statistical mechanical theory in conjunction with quasi-lattice theory. The Al-Cr phase diagram exhibits the existence of different intermetallic compounds in the solid state, while that of Cr-Ni is a simple eutectic-type phase diagram at high temperatures and includes the low-temperature peritectoid reaction in the range near a CrNi 2 composition. Accordingly, the mixing behaviour in Al-Cr and Cr-Ni alloy melts was studied using the complex formation model in the weak interaction approximation and by postulating Al 8 Cr 5 and CrNi 2 chemical complexes, respectively, as energetically favoured.

  12. Bulk and surface properties of liquid Al-Cr and Cr-Ni alloys.

    Science.gov (United States)

    Novakovic, R

    2011-06-15

    The energetics of mixing and structural arrangement in liquid Al-Cr and Cr-Ni alloys has been analysed through the study of surface properties (surface tension and surface segregation), dynamic properties (chemical diffusion) and microscopic functions (concentration fluctuations in the long-wavelength limit and chemical short-range order parameter) in the framework of statistical mechanical theory in conjunction with quasi-lattice theory. The Al-Cr phase diagram exhibits the existence of different intermetallic compounds in the solid state, while that of Cr-Ni is a simple eutectic-type phase diagram at high temperatures and includes the low-temperature peritectoid reaction in the range near a CrNi(2) composition. Accordingly, the mixing behaviour in Al-Cr and Cr-Ni alloy melts was studied using the complex formation model in the weak interaction approximation and by postulating Al(8)Cr(5) and CrNi(2) chemical complexes, respectively, as energetically favoured.

  13. Redox transformation and reductive immobilization of Cr(VI) in the Columbia River hyporheic zone sediments

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Fen; Liu, Yuanyuan; Zachara, John M.; Bowden, Mark E.; Kennedy, David W.; Plymale, Andrew E.; Liu, Chongxuan,

    2017-12-01

    An experimental and modeling study was conducted to investigate the redox transformation and reductive immobilization of groundwater contaminant Cr in hyporheic zone (HZ) sediments from U.S. Department of Energy’s Hanford site, where groundwater Cr(VI) is migrating and discharging to the nearby Columbia River. Experimental results revealed that Cr(VI) can be reduced to immobile reduced Cr by the HZ sediments in the presence/absence of O2. Anaerobic pre-incubation of the sediments increased the effective rate of Cr reduction that was correlated with the increase in HCl-extractable Fe(II) content in the sediments. The reduced Cr was stable in exposure to O2 under field-relevant pH (~7.5) and Mn-containing (~0.02% w/w) conditions. The Cr(VI) reduction rate showed a multi-rate behavior, apparently reflecting the presence of reductants with different reactivity in the sediments. The results from this study indicated that the HZ sediments can reductively immobilize Cr and the sediment redox capacity can be recharged through microbial activities. The results implied that HZ can play a role as a natural permeable redox barrier for removing groundwater Cr before it discharges into a river system.

  14. The thermoluminescence and optically stimulated luminescence properties of Cr-doped alpha alumina transparent ceramics

    International Nuclear Information System (INIS)

    Liu, Qiang; Yang, Qiu Hong; Zhao, Guang Gen; Lu, Shen Zhou; Zhang, Hao Jia

    2013-01-01

    Highlights: •Polycrystalline Cr:α-Al 2 O 3 transparent ceramics were obtained with vacuum sintering method. •The influence of different concentration of Cr 2 O 3 on the thermoluminescence and optical stimulated luminescence properties of Cr:α-Al 2 O 3 transparent ceramics was studied. •It had a main peak at 503 K of very high intensity and linear concentration dependence up to high concentration. •It showed so interesting results with high TL sensitivity and high stability of OSL signal that Cr:α-Al 2 O 3 transparent ceramics might be a promising material in TL dosimetry and replace Cr:α-Al 2 O 3 crystals. -- Abstract: Polycrystalline Cr:α-Al 2 O 3 transparent ceramics were fabricated by conventional solid-state processing under vacuum condition. The SEM microstructure photographs of Cr:α-Al 2 O 3 transparent ceramics doped with different content of Cr 2 O 3 were investigated. The absorption, emission spectra, thermoluminescence and optical stimulated luminescence of Cr:α-Al 2 O 3 transparent ceramics were comparable to those of Cr:α-Al 2 O 3 crystals. The influence of different concentration of Cr 2 O 3 on the thermoluminescence and optical stimulated luminescence properties of Cr:α-Al 2 O 3 transparent ceramics was discussed. It showed so interesting results with high TL sensitivity and high stability of OSL signal that Cr:α-Al 2 O 3 transparent ceramics might be a promising material in TL dosimetry and replace Cr:α-Al 2 O 3 crystals

  15. Effects of processing parameters on Be/CuCrZr joining

    International Nuclear Information System (INIS)

    Park, Jeong-Yong; Lee, Jung-Suk; Choi, Byung-Kwon; Park, Sang-Yun; Hong, Bong Guen; Jeong, Yong Hwan; Jung, Ki-Jung

    2007-01-01

    A joining of Be/CuCrZr has been considered as the key technology for the fabrication of the ITER first wall. Among the joining methods, Hot isostatic pressing (HIP), which is one of the diffusion bonding methods, is the most feasible method to join the Be and CuCrZr alloy. In the HIP joining of Be and CuCrZr, the interlayer was used to prevent the formation of brittle intermetallic compounds in the interface. Therefore, it is crucial to select a suitable interlayer for a joining of Be and CuCrZr. On the other hand, the diffusion between Be and CuCrZr would be enhanced with an increase of the HIP joining temperature, thereby increasing the joint strength. However, the HIP joining temperature is limited by the mechanical properties of CuCrZr. During the fabrication process of the ITER first wall, CuCrZr is subjected to several thermal cycles including a solution annealing, a cooling and an aging. The HIP joining of Be and CuCrZr corresponds to the aging of CuCrZr. The HIP joining at a higher temperature would cause a degradation of the mechanical properties of CuCrZr by an overaging effect although it is preferable for an improvement of the joint strength. In this study, the effect of the cooling rate on the mechanical properties of aged CuCrZr was investigated to find the maximum HIP temperature without a degradation of the mechanical properties of CuCrZr

  16. CO 2-rich komatiitic melt inclusions in Cr-spinels within beach sand from Gorgona Island, Colombia

    Science.gov (United States)

    Shimizu, Kenji; Shimizu, Nobumichi; Komiya, Tsuyoshi; Suzuki, Katsuhiko; Maruyama, Shigenori; Tatsumi, Yoshiyuki

    2009-10-01

    The volatile content of komatiite is a key to constrain the thermal and chemical evolution of the deep Earth. We report the volatile contents with major and trace element compositions of ~ 80 melt inclusions in chromian spinels (Cr-spinels) from beach sands on Gorgona Island, Colombia. Gorgona Island is a ~ 90 Ma volcanic island, where picrites and the youngest komatiites known on the Earth are present. Melt inclusions are classified into three types on the basis of their host Cr-spinel compositions: low Ti (P type), high Ti with high Cr # (K1 type) and high Ti with low Cr # (K2 type). Chemical variations of melt inclusions in the Cr-spinels cover all of the island's lava types. P-type inclusions mainly occur in the picrites, K1-type in high-TiO 2 komatiites (some enriched basalts: E-basalts) and K2-type in low-TiO 2 komatiites. The H 2O and CO 2 contents of melt inclusions within Cr-spinels from the beach sand are highly variable (H 2O: 0.03-0.9 wt.%; CO 2: 40-4000 ppm). Evaluation of volatile content is not entirely successful because of compositional alterations of the original melt by degassing, seawater/brine assimilation and post-entrapment modification of certain elements and volatiles. However, the occurrence of many melt inclusions with low H 2O/K 2O ratios indicates that H 2O/K 2O of Gorgona komatiite is not much different from that of modern mid-oceanic ridge basalt (MORB) or oceanic island basalt. Trend of CO 2/Nb and Zr/Y ratios, accounted for by two-component mixing between the least degassed primary komatiite and low-CO 2/Nb evolved basalt, allow us to estimate a primary CO 2/Nb ratio of 4000 ± 2200 or a CO 2 content of 0.16 ± 0.09 wt.%. The determined CO 2/Nb ratio is unusually high, compared to that of MORB (530). Although the presence of CO 2 in the Gorgona komatiite does not affect the magma generation temperature, CO 2 degassing may have contributed to the eruption of high-density magmas. High CO 2/Nb and the relatively anhydrous nature of

  17. Effect of small addition of Cr on stability of retained austenite in high carbon steel

    Energy Technology Data Exchange (ETDEWEB)

    Hossain, Rumana; Pahlevani, Farshid, E-mail: f.pahlevani@unsw.edu.au; Sahajwalla, Veena

    2017-03-15

    High carbon steels with dual phase structures of martensite and austenite have considerable potential for industrial application in high abrasion environments due to their hardness, strength and relatively low cost. To design cost effective high carbon steels with superior properties, it is crucial to identify the effect of Chromium (Cr) on the stability of retained austenite (RA) and to fully understand its effect on solid-state phase transition. This study addresses this important knowledge gap. Using standard compression tests on bulk material, quantitative X-ray diffraction analysis, nano-indentation on individual austenitic grains, transmission electron microscopy and electron backscatter diffraction–based orientation microscopy techniques, the authors investigated the effect of Cr on the microstructure, transformation behaviour and mechanical stability of retained austenite in high carbon steel, with varying Cr contents. The results revealed that increasing the Cr %, altered the morphology of the RA and increased its stability, consequently, increasing the critical pressure for martensitic transformation. This study has critically addressed the elastoplastic behaviour of retained austenite – and provides a deep understanding of the effect of small additions of Cr on the metastable austenite of high carbon steel from the macro- to nano-level. Consequently, it paves the way for new applications for high carbon low alloy steels. - Highlights: • Effect of small addition of Cr on metastable austenite of high carbon steel from the macro- to nano-level • A multi-scale study of elastoplastic behaviour of retained austenite in high carbon steel • The mechanical stability of retained austenite during plastic deformation increased with increasing Cr content • Effect of grain boundary misorientation angle on hardness of individual retained austenite grains in high carbon steel.

  18. Role of Oxides and Porosity on High-Temperature Oxidation of Liquid-Fueled HVOF Thermal-Sprayed Ni50Cr Coatings

    Science.gov (United States)

    Song, B.; Bai, M.; Voisey, K. T.; Hussain, T.

    2017-02-01

    High chromium content in Ni50Cr thermally sprayed coatings can generate a dense and protective scale at the surface of coating. Thus, the Ni50Cr coating is widely used in high-temperature oxidation and corrosion applications. A commercially available gas atomized Ni50Cr powder was sprayed onto a power plant steel (ASME P92) using a liquid-fueled high velocity oxy-fuel thermal spray with three processing parameters in this study. Microstructure of as-sprayed coatings was examined using oxygen content analysis, mercury intrusion porosimetry, scanning electron microscope (SEM), energy-dispersive x-ray spectroscopy (EDX) and x-ray diffraction (XRD). Short-term air oxidation tests (4 h) of freestanding coatings (without boiler steel substrate) in a thermogravimetric analyzer at 700 °C were performed to obtain the kinetics of oxidation of the as-sprayed coating. Long-term air oxidation tests (100 h) of the coated substrates were performed at same temperature to obtain the oxidation products for further characterization in detail using SEM/EDX and XRD. In all samples, oxides of various morphologies developed on top of the Ni50Cr coatings. Cr2O3 was the main oxidation product on the surface of all three coatings. The coating with medium porosity and medium oxygen content has the best high-temperature oxidation performance in this study.

  19. Experimental and computational study on the effect of yttrium on the phase stability of sputtered Cr-Al-Y-N hard coatings

    International Nuclear Information System (INIS)

    Rovere, F.; Music, D.; Schneider, J.M.; Mayrhofer, P.H.

    2010-01-01

    The effect of Y incorporation into cubic Cr-Al-N (B1) was studied using ab initio calculations, X-ray diffraction and energy-dispersive X-ray analysis of sputtered quaternary nitride films. The data obtained indicate that the Y incorporation shifts the critical Al content, where the hexagonal (B4) structure is stable, to lower values. The calculated critical Al contents of x ∼ 0.75 for Cr 1-x Al x N and x ∼ 0.625 for Cr 1-x-y Al x Y y N with y = 0.125 are consistent with experimentally obtained values of x = 0.69 for Cr 1-x Al x N and x = 0.68 and 0.61 for Cr 1-x-y Al x Y y N with y = 0.02 and 0.06, respectively. This may be understood based on the electronic structure. Both Cr and Al can randomly be substituted by Y. The substitution of Cr by Y increases the phase stability due to depletion of non-bonding (anti-bonding) states, while the substitution of Al by Y decreases the phase stability mainly due to lattice strain.

  20. The Content of Heavy Metals (Cu, Zn, Cr, Ni, Pb in The Soil Near The Arterial Roads in Wroclaw (Poland

    Directory of Open Access Journals (Sweden)

    Sobczyk Karolina

    2017-01-01

    Full Text Available The concentrations of heavy metals in soils along the motorway bypass of Wroclaw (AOW and the Eastern Ring Road of Wroclaw (WOW, Poland, have been determined. The soil samples were collected from the levels of 0-25 cm within 2 m from the edge of the road. The mineralizates were prepared in HNO3, 60%, using the Microwave Digestion System. The content of Cu, Zn, Cr, Ni and Pb in soils were determined using FAAS method. The physicochemical parameters, the conductivity and pH of the soil solutions were measured to evaluate the salinity of the soils and their active and exchangeable acidity. The pollution indexes (WN showing the enrichment of soils in metals have been determined. Excess of metal concentrations in soils compared to the geochemical background in uncontaminated soils of Poland has been observed. Permissible concentrations of heavy metals relative to the standard for soils, according to the Polish Ministry of Environment Regulation from September 1st, 2016, have not been exceeded.

  1. Microstructure and mechanical properties of nanostructure multilayer CrN/Cr coatings on titanium alloy

    International Nuclear Information System (INIS)

    Wiecinski, Piotr; Smolik, Jerzy; Garbacz, Halina; Kurzydlowski, Krzysztof J.

    2011-01-01

    Five different nanostructured, multilayer coatings (CrN/Cr)x8 with different thickness ratio of Cr and CrN layers were deposited by PAPVD (Plasma Assisted Physical Vapour Deposition) vacuum arc method on Ti6Al4V titanium alloy. The microstructure, chemical and phase composition of the CrN and Cr sub-layers were characterized by SEM with EDX and Cs-corrected dedicated STEM on cross-sections prepared by focus ion beam. Besides, hardness and Young's modulus of the (Cr/CrN)x8 coatings has been measured. The adhesion has been tested by scratch test method. The obtained (CrN/Cr) multilayer coatings, 5-6 μm in thickness, have homogeneous and nanocrystalline structure, free of pores and cracks. The microstructures of Cr and CrN layers consist of columnar grains below 100 nm in diameter. The hardness and Young's modulus of these coatings depend linearly on thickness ratio of Cr and CrN layers. The decrease of the thickness ratio Cr/CrN 0.81 to 0.15 results in the increase of hardness from 1275 HV to 1710 HV and Young's modulus from 260 GPa to 271 GPa.

  2. Effect of Dynamic Reheating Induced by Weaving on the Microstructure of GTAW Weld Metal of 25% Cr Super Duplex Stainless Steel Weld Metal

    Directory of Open Access Journals (Sweden)

    Hee-Joon Sung

    2017-11-01

    Full Text Available The importance of the additional growth and/or transformation of the austenite phase that occurs in weld metals of super duplex stainless steel upon reheating is known. However, the effects have not been fully investigated, especially with respect to reheating induced by weaving during single-pass welding. In this work, bead-on-pipe gas tungsten arc welding (GTAW was conducted on super duplex stainless steel to understand the effect of weaving on the microstructure of weld metal. Microstructural analysis, electron backscatter diffraction (EBSD, and focused ion beam transmission electron microscopy (FIB-TEM were carried out to investigate the relationship between weaving and microstructural change. The weaving of GTAW produced a dynamic reheated area just before the weld bead during welding. It was revealed that extensive reheated weld existed even after one welding pass, and that the content of the austenite phase in the reheated area was higher than that in the non-reheated area, indicating the existence of a large quantity of intragranular austenite phase. In addition, the Cr2N content in the reheated area was lower than that in the non-reheated area. This reduction of Cr2N was closely related to the reheating resulting from weaving. TEM analysis revealed that Cr2N in the non-reheated area was dispersed following heating and transformed to secondary austenite.

  3. Hot corrosion behavior of Ni-Cr-W-C alloys in impure helium gas

    International Nuclear Information System (INIS)

    Ohmura, Taizo; Sahira, Kensho; Sakonooka, Akihiko; Yonezawa, Noboru

    1976-01-01

    Influence of the minor alloy constituents such as Al, Mn and Si on the hot corrosion behavior of Ni-20Cr-20W-0.07C alloy was studied in 99.995% helium gas at 1000 0 C, comparing with that behavior of commercial Ni-base superalloys (Hastelloy X and Inconel 617). The low oxidizing potential in the impure helium gas usually causes selective oxidation of these elements and the growth of oxide whiskers on the surface of specimen at elevated temperature. The intergranular attack was caused by selective oxidation of Al, Si and Mn. The spalling of oxide film was restrained by addition of Mn and Si, providing tough spinel type oxide film on the surface and 'Keyes' on the oxide-matrix interface respectively. The amount and the morphology of the oxide whiskers depended on Si and Mn content. More than 0.29% of Si content without Mn always caused the growth of rather thinner whiskers with smooth surface, and the whiskers analyzed by electron diffraction patterns and EPMA to be Cr 2 O 3 containing Si. Mn addition changed the whiskers to thicker ones of spinel type oxide (MnCr 2 O 1 ) with rough surface. On the basis of these results, the optimum content of Al, Mn and Si to minimize the growth of whiskers, the intergranular attack and the spalling of oxide film was discussed. (auth.)

  4. Surface morphology of scale on FeCrAl (Pd, Pt, Y) alloys

    International Nuclear Information System (INIS)

    Amano, T.; Takezawa, Y.; Shiino, A.; Shishido, T.

    2008-01-01

    The high temperature oxidation behavior of Fe-20Cr-4Al, floating zone refined (FZ) Fe-20Cr-4Al, Fe-20Cr-4Al-0.5Pd, Fe-20Cr-4Al-0.5Pt and Fe-20Cr-4Al-(0.01, 0.02, 0.05, 0.1, 0.2, 0.5)Y alloys was studied in oxygen for 0.6-18 ks at 1273-1673 K by mass gain measurements, X-ray diffraction and scanning electron microscopy. The mass gains of FeCrAl, FZ FeCrAl, FeCrAlPd and FeCrAlPt alloys showed almost the same values. Those of FeCrAl-(0.01, 0.02, 0.05, 0.1, 0.2, 0.5)Y alloys decreased with increasing yttrium of up to 0.1% followed by an increase with the yttrium content after oxidation for 18 ks at 1473 K. Needle-like oxide particles were partially observed on FeCrAl alloy after oxidation for 7.2 ks at 1273 K. These oxide particles decreased in size with increasing oxidation time of more than 7.2 ks at 1473 K, and then disappeared after oxidation for 7.2 ks at 1573 K. It is suggested that a new oxide develops at the oxygen/scale interface. The scale surface of FeCrAl alloy showed a wavy morphology after oxidation for 7.2 ks at 1273 K which then changed to planar morphology after an oxidation time of more than 7.2 ks at 1573 K. On the other hand, the scale surfaces of other alloys were planar after all oxidation conditions in this study. The scale surfaces of FeCrAl, FZ FeCrAl, FeCrAlPd and FeCrAlPt alloys were rough, however, those of FeCrAl-(0.1, 0.2, 0.5)Y alloys were smooth. The oxide scales formed on FeCrAl-(0.1, 0.2, 0.5)Y alloys were found to be α-Al 2 O 3 with small amounts of Y 3 Al 5 O 12 , and those of the other alloys were only α-Al 2 O 3

  5. Structure and wear behavior of AlCrSiN-based coatings

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Yun [School of Mechanical Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Chengdu Tool Research Institute Co., Ltd., Chengdu 610500 (China); Du, Hao [School of Manufacturing Science and Engineering, Sichuan University, Chengdu 610065 (China); Chen, Ming, E-mail: mchen@sjtu.edu.cn [School of Mechanical Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Yang, Jun [Chengdu Tool Research Institute Co., Ltd., Chengdu 610500 (China); Xiong, Ji [School of Manufacturing Science and Engineering, Sichuan University, Chengdu 610065 (China); Zhao, Haibo [The Analysis and Testing Centre, Sichuan University, Chengdu 610065 (China)

    2016-05-01

    Graphical abstract: - Highlights: • AlCrSiN based coating showed amorphous structure. • AlCrSiN/Me{sub x}N coatings obtained better wear resistance. • Molybdenum and niobium increased the coating hardness and wear resistance. - Abstract: AlCrN, AlCrSiCN, AlCrSiN/MoN, and AlCrSiN/NbN coatings have been deposited on high-polished WC–Co cemented carbide substrate and tools by mid-frequency magnetron sputtering in Ar/N{sub 2} mixtures. Al{sub 0.6}Cr{sub 0.4}, Al{sub 0.6}Cr{sub 0.3}Si{sub 0.1}, and C/Mo/Nb targets were used during the deposition. The microstructure and mechanical properties of as-deposited coatings were investigated. Investigations of the wear behaviors of coated tools were also performed. The results showed that cubic structure was formed in the coatings. Broader CrAlN (1 1 1) and (2 0 0) peaks without SiN{sub x} peak were formed in the AlCrSiN/Me{sub x}N coatings, which showed a nanocomposited structure. Meanwhile, according to SEM micrographs, AlCrN exhibited a columnar structure, while, AlCrSiCN, AlCrSiN/MoN, and AlCrSiN/NbN coatings showed nanocrystalline morphology. The nano-multilayered coatings performed higher hardness, H/E, and H{sup 3}/E{sup 2} ratios compared with AlCrN coating. Through the Rockwell adhesion test, all the coatings exhibited adhesion strength quality HF1. After turning Inconel 718 under dry condition, the nano-multilyered coatings showed better wear resistance than AlCrN coating. Due to the molybdenum and niobium in the coating, AlCrSiN/MoN and AlCrSiN/NbN coatings showed the best wear resistance.

  6. Cr-Ni ALLOY ELECTRODEPOSITION AND COMPARISON WITH CONVENTIONAL PURE Cr COATING TECHNIQUE

    Directory of Open Access Journals (Sweden)

    M. Moniruzzaman

    2012-12-01

    Full Text Available Cr coating is widely used as the outer surface of precision parts due to its attractive appearance and superior corrosion resistance properties. It is obtained by electrodeposition via a conventional bath with hexavalent Cr ions. This manufacturing technique has many drawbacks, such as very low efficiency and high operating temperature and it is hazardous to health. In this work, we studied a Cr-Ni alloy deposition technique and compared the alloy coating properties to those with conventional Cr coating. Sequential two-step alloy electrodeposition was also compared. We took varying concentrations of Cr, Ni and complexing agents for the electrodeposition of Cr-Ni alloy and sequential Cr-Ni alloy coating on mild steel. Operating parameters, i.e. current density and temperature, were varied to examine their effects on the coating properties. The coatings thus obtained were characterized by visual observation, corrosion test, microhardness measurement, morphology and chemical analysis. The Cr-Ni alloy coating was found to be more corrosion resistant in 5% NaCl solution and harder than the pure Cr coating obtained by conventional electrodeposition. Toxic gas was produced in a much lower extent in the alloy coating than the conventional Cr coating technique. Again, the two-step Cr-Ni alloy coating was found better in terms of corrosion resistance as well as hardness compared to the Cr-Ni alloy coating. The process was also found to be much more environmentally friendly.

  7. Electronic structure and magnetic ordering of the semiconducting chromium trihalides CrCl3, CrBr3, and CrI3

    KAUST Repository

    Wang, Hao

    2011-03-01

    We present results from an electronic structure investigation of the chromium halides CrCl3, CrBr3, and CrI3, as obtained by the linearized augmented plane wave method of density functional theory. Our interest focuses on the chloride. While all three halides display strong ferromagnetic coupling within the halide-Cr-halide triple layers, our emphasis is on differences in the interlayer magnetic coupling. In agreement with experimental results, our calculations indicate ferromagnetic ordering for CrBr3 as well as CrI3. The antiferromagnetic state of CrCl3 can be reproduced by introducing an on-site electron-electron repulsion. However, we observe that the ground state depends critically on the specific approach used. Our results show that a low temperature structural phase transition from monoclinic to trigonal is energetically favourable for CrCl3. © 2011 IOP Publishing Ltd.

  8. Submerged cultivation of mycelium with high ergothioneine content from the culinary-medicinal king oyster mushroom Pleurotus eryngii (higher Basidiomycetes) and its composition.

    Science.gov (United States)

    Liang, Chih-Hung; Huang, Ling-Yi; Ho, Kung-Jui; Lin, Shin-Yi; Mau, Jeng-Leun

    2013-01-01

    The culinary-medicinal king oyster mushroom, Pleurotus eryngii, was used to produce mycelia with high ergothioneine content using a one-factor-at-a-time method. The optimal culture conditions for mycelia harvested at day 14 were 25°C, 10% inoculation rate, 2% glucose, 0.5% yeast extract, and no adjustment to the initial pH value. With histidine or amino acid mix added, biomasses and the ergothioneine content of mycelia were higher than those of the control. The ergothioneine content of mycelia harvested at days 16-20 were higher than that of mycelia harvested at day 14. In addition, the ergothioneine content of mycelia from the fermentor (5.84-5.76 mg/g) was much higher than that of mycelia from the shaken flask (4.93-5.04 mg/g). Mycelia with high ergothioneine content showed a profile of proximate composition similar to that of regular mycelia but lost its characteristic umami taste. Overall, mycelia high in ergothioneine could be prepared by optimal culture conditions, the addition of precursors, prolonged harvest, and aeration in the fermentor.

  9. Studies on nitrogen mapping by various CR-39 track detectors

    Energy Technology Data Exchange (ETDEWEB)

    Somogyi, G.; Varga, Zs.; Hunyadi, I.; Freyer, K.; Treutler, H.Ch.

    1986-01-01

    The use of CR-39 track detectors for nitrogen distribution measurements via the /sup 14/N(n,p)/sup 14/C reaction is studied. The proton detection properties of different CR-39 products have been analyzed. The variation of background track density induced in the bulk of detectors is examined under different conditions of neutron irradiation. Analysis of our experimental data has led to the conclusion that the sources of proton background tracks are the fast neutron component of the neutron source, chlorine impurities in the detector and nitrogen diffused from the air into the upper layer of the detector. Efforts have been made to decrease the nitrogen content of diffusion origin by removing the upper detector layer and by outgassing the CR-39 sheet in vacuum before irradiation. Finally the ''signal/noise'' ratio for a steel specimen and the sensitivity of nitrogen determination are given.

  10. Effect of alloy content on microstructure and microchemistry of ...

    Indian Academy of Sciences (India)

    This paper presents the results of an experimental study on the microstructural evolution in 9Cr reduced activation ferritic/martensitic steels during short term thermal exposures. Since the microstructure is strongly influenced by the alloying additions, mainly W, Ta and C contents, the effect of varying W and Ta contents on ...

  11. Improvements in the susceptibility to hydrogen attack and stress-relief cracking of 2 1/4Cr-1Mo steels

    International Nuclear Information System (INIS)

    Imanaka, T.; Sato, S.; Shimomura, J.; Aso, K.

    1985-01-01

    The influence of sulphur content at extremely low level on the susceptibility to hydrogen attack and stress-relief cracking in 2 1/4Cr-1Mo steels was studied. The reduction of sulphur content and/or the addition of REM (rare earth metal) or Ca in accordance with sulphur content remarkably improve the resistivity against hydrogen attack and stress-relief cracking. Micro-structural examination has showed that there exist Mn-REM-S-Al-O complex particles in the REM-added steels. It is concluded that the effect of REM on hydrogen attack and stress-relief cracking is to reduce ''the free sulphur'' in 2 1/4Cr-1Mo steels

  12. Evidences for the Formation of Chromium in the Unusual Oxidation State Cr(IV). I. Chemical Reactivity, Microhomogeneity, and Crystal Structures of the Nonstoichiometric Channel Compounds Tl xCr 5Se 8(0 ≤ x≤ 1)

    Science.gov (United States)

    Bensch, W.; Helmer, O.; Näther, C.

    1996-11-01

    The topotactic redox reaction between TlCr 5Se 8and bromine in acetonitrile leads to the formation of metastable samples with 0 ≤ xtransition metal chalcogenide crystallizing in the TlV 5S 8type structure with a Tl content xtopotactic redox reaction does not follow simple kinetics but is rather explained on the basis of the superposition of at least three different fundamental steps. EDAX investigations conducted on selected single crystals reveal that dependent on the deintercalation temperature, Tl is laterally inhomogeneous distributed along the needle axis which coincides with the crystallographic baxis. A pronounced maximum is observed at the middle of the crystals. In stoichiometric TlCr 5Se 8the detailed analysis of the anisotropic displacement parameters of the Tl atoms reveal that the Tl atoms are displaced from the central position by about 0.26 Å. As a consequence the Tl atoms are coordinated by seven Se atoms in an irregular coordination polyhedron. Since the positions x0 zare related by a center of symmetry they cannot be occupied simultaneously. Hence it must be assumed that TlCr 5Se 8has a domain structure with local symmetry Cm. In the Tl poorer phases the refinement of the Tl atoms at the central position leads to unusual high U22components. The observed microinhomogenity as well as an enhanced mobility and/or static disorder of the Tl atom within the channel may be responsible for this. The value for U11decreases with decreasing Tl content whereas U33is not affected. This observation is indicative for a different displacement of the Tl atoms from the central position. With respect to the possible reaction mechanisms, according to our structural investigations, the oxidation of monovalent Tl to trivalent Tl can be excluded. With decreasing Tl content the lattice parameters exhibit very anisotropic behavior, which is a direct consequence of the large changes of the interatomic Cr-Cr distances. The average as well as the nonbonding Se-Se distances

  13. Colour due to Cr3+ ions in oxides: a study of the model system MgO:Cr3+

    International Nuclear Information System (INIS)

    Aramburu, J A; García-Fernández, P; Moreno, M; García-Lastra, J M; Barriuso, M T

    2013-01-01

    Seeking to understand why the cubic centre in MgO:Cr 3+ has the same 10Dq value as emerald, ab initio cluster and periodic supercell calculations have been performed. It is found that the equilibrium Cr 3+ –O 2− distance, R, in MgO:Cr 3+ is equal to 2.03 Å and thus 0.06 Å higher than that measured for the emerald. Calculations carried out on the isolated CrO 6 9- complex at R = 2.03 Å give 10Dq = 14 510 cm −1 , which is 10% smaller than the experimental figure for MgO:Cr 3+ . Nevertheless, when the internal electric field, E R (r), due to the rest of the lattice ions is also taken into account, the calculated 10Dq = 16 210 cm −1 coincides with the experimental value. Accordingly, the colour shift for different oxides doped with Cr 3+ can be well understood on the basis of this extrinsic contribution to 10Dq usually ignored in a ligand field description. The calculated electrostatic potential, V R (r), related to E R (r), is found to be attractive when the electronic density is lying along 〈110〉 directions and |r| > 1 Å driven by the first shell of twelve Mg 2+ ions. The action of V R (r) upon the CrO 6 9- complex slightly decreases the energy of t 2g (xy,xz,yz) orbitals with respect to that for e g (3z 2 − r 2 ,x 2 − y 2 ) orbitals, thus enhancing the 10Dq value by 0.2 eV. However, the addition of V R (r) induces very small changes in the electronic density, a relevant fact that is related to the 2 E( 2g 3 ) → 4 A 2 (t 2g 3 ) emission energy being nearly independent of the host lattice along the series of Cr 3+ -doped oxides. (paper)

  14. Correlation between heavy metal contents and antioxidants in medicinal plants grown in mining areas

    International Nuclear Information System (INIS)

    Maharia, R.; Dutta, R.K.; Acharya, R.; Reddy, A.V.R.

    2010-01-01

    Full texts: Medicinal plants are widely used as alternate therapeutic agents for various diseases. Three medicinal plants grown in copper mining regions of Khetri in Rajasthan was analyzed for heavy metal contents by instrumental neutron activation analysis. The copper levels were found to be two to three folds higher in these plant leaves as compared to the reported copper levels in the medicinal plants grown in environmentally friendly regions. In our previous study on heavy metals in soil and medicinal plant of Khetri region we have shown bioaccumulation of Cu in the medicinal plants. In addition, the levels of Cr, Fe and Zn were also higher. Antioxidant properties of medicinal plants are one of their major therapeutic functionalities. The role of elevated levels of heavy metals in the medicinal plants was studied with respect to their antioxidant properties. Standard procedures were used for measuring total phenols, flavanoids and DPPH assay of these medicinal plants which were correlated with the heavy metals contents of these plants

  15. HIP joining of Be/CuCrZr for fabrication of ITER first wall

    International Nuclear Information System (INIS)

    Park, Jeong-Yong; Choi, Byung-Kwon; Park, Sang-Yoon; Kim, Hyun-Gil; Kim, Jun-Hwan; Hong, Bong Guen; Jeong, Yong Hwan

    2007-01-01

    The effects of different interlayer types and the temperature have been investigated in order to optimize the HIP joining conditions of Be to CuCrZr. Ti/Cu and Cr/Cu interlayers were coated onto a Be surface before a HIP joining. HIP temperature was changed from 580 to 620 deg. C. No intermetallic compounds or defects were formed at the interface of the joint specimens. The joining strength measured by the four-point bend test and the shear test was higher in the joint specimen with Ti/Cu interlayers when compared to that with Cr/Cu interalyers and it was increased with an increase of the HIP temperature from 580 to 620 deg. C. The yield strength of the aged CuCrZr was higher than 150 MPa at 250 deg. C up to an aging temperature of 620 deg. C after a water quenching. It is therefore suggested that the HIP temperature of the Be/CuCrZr joint could be increased to 620 deg. C based on the results obtained from this study

  16. Fe-Cr-V ternary alloy-based ferritic steels for high- and low-temperature applications

    International Nuclear Information System (INIS)

    Rieth, M.; Materna-Morris, E.; Dudarev, S.L.; Boutard, J.-L.; Keppler, H.; Mayor, J.

    2009-01-01

    10V, 10Cr15V, 10Cr10V0.2C, 10Cr10V0.4C. Tensile specimens have been fabricated, heat treated at 1100 deg. C for 2 hours for normalization, and tested at temperatures up to 700 deg. C. The investigations were completed by hardness tests, metallographic imaging, and microstructure analysis. The content of intermetallic (Laves) phases increases with the vanadium content and the addition of carbon leads to carbide (VC) precipitation at the grain boundaries. In general, typical ferritic microstructures are recognizable with huge grain sizes (several 100 μm) for the 10Cr5-15V alloys and with smaller grain sizes (about 50 μm) for the 10Cr10V0.2- 0.4C alloys. However, the tensile tests performed so far have indicated about the same strength level at 700 deg. C. (author)

  17. Rational construction of Z-scheme Ag{sub 2}CrO{sub 4}/g-C{sub 3}N{sub 4} composites with enhanced visible-light photocatalytic activity

    Energy Technology Data Exchange (ETDEWEB)

    Luo, Jin, E-mail: lj328520504@126.com; Zhou, Xiaosong; Ma, Lin; Xu, Xuyao

    2016-12-30

    Highlights: • Novel visible-light driven Ag{sub 2}CrO{sub 4}/g-C{sub 3}N{sub 4} composites were synthesized. • Ag{sub 2}CrO{sub 4}/g-C{sub 3}N{sub 4} exhibited enhanced visible-light photocatalytic activity. • The reasons for the enhanced photocatalytic activity were revealed. - Abstract: Novel visible-light driven Z-scheme Ag{sub 2}CrO{sub 4}/g-C{sub 3}N{sub 4} composites with different contents of Ag{sub 2}CrO{sub 4} were fabricated by a facile chemical precipitation method and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), UV–vis diffuse reflectance spectroscopy (UV-vis DRS), photoluminescence (PL) spectroscopy and photoelectrochemical measurements. Compared with individual g-C{sub 3}N{sub 4} and Ag{sub 2}CrO{sub 4}, the Ag{sub 2}CrO{sub 4}/g-C{sub 3}N{sub 4} composites displayed much larger photocatalytic activities for the photocatalytic degradation of methyl orange (MO) solution at room temperature under visible light irradiation (λ > 420 nm). Importantly, the optimum photodegradation rate constant of the Ag{sub 2}CrO{sub 4}/g-C{sub 3}N{sub 4} composite at a theoretical weight content of 8.0% Ag{sub 2}CrO{sub 4} for the photodegradation of MO was 0.0068 min{sup −1}, which was 5.7 and 4.3 times higher than that of pure g-C{sub 3}N{sub 4} and Ag{sub 2}CrO{sub 4}, respectively. Such enormous enhancement in photocatalytic performance was predominantly ascribed to the efficient separation and transfer of photogenerated electrons and holes at the Ag{sub 2}CrO{sub 4}/g-C{sub 3}N{sub 4} interface imparted through the Z-scheme electron transfer. Furthermore, radical trap experiments depicted that both the holes and superoxide radical anions were thought to dominate oxidative species of the Ag{sub 2}CrO{sub 4}/g-C{sub 3}N{sub 4} composite for MO degradation under visible light irradiation. Ultimately, a tentative Z-scheme photodegradation mechanism

  18. A Content Analysis of General Chemistry Laboratory Manuals for Evidence of Higher-Order Cognitive Tasks

    Science.gov (United States)

    Domin, Daniel S.

    1999-01-01

    The science laboratory instructional environment is ideal for fostering the development of problem-solving, manipulative, and higher-order thinking skills: the skills needed by today's learner to compete in an ever increasing technology-based society. This paper reports the results of a content analysis of ten general chemistry laboratory manuals. Three experiments from each manual were examined for evidence of higher-order cognitive activities. Analysis was based upon the six major cognitive categories of Bloom's Taxonomy of Educational Objectives: knowledge, comprehension, application, analysis, synthesis, and evaluation. The results of this study show that the overwhelming majority of general chemistry laboratory manuals provide tasks that require the use of only the lower-order cognitive skills: knowledge, comprehension, and application. Two of the laboratory manuals were disparate in having activities that utilized higher-order cognition. I describe the instructional strategies used within these manuals to foster higher-order cognitive development.

  19. High Cr ODS steels R and D for high burnup fuel cladding

    International Nuclear Information System (INIS)

    Kimura, A.; Kasada, R.; Kishimoto, H.; Iwata, N.; Cho, H.-S.; Toda, N.; Yutani, K.; Ukai, S.; Fujiwara, M.

    2007-01-01

    High-performance cladding materials is essential to realize highly efficient and high-burnup operation over 150 GWd/t of so called Generation IV nuclear energy systems, such as supercritical-water-cooled reactor (SCWR) and lead-cooled fast reactor (LFR). Oxide dispersion strengthening (ODS) ferritic/ martensitic steels, which contain 9-12%Cr, show rather high resistance to neutron irradiation embrittlement and high strength at elevated temperatures. However, their corrosion resistance is not good enough in SCW and in lead at high temperatures. High-Cr ODS steels have been developed to improve corrosion resistance. An increase in Cr content an addition resulted in a drastic improvement of corrosion resistance in SCW and in lead. On the contrary, high-Cr steels often show an enhancement of aging embrittlement as well as irradiation embrittlement. Anisotropy in tensile properties is another issue. In order to overwhelm these issues, surveillance tests of the material performance have been performed for high Cr-ODS steels produced by new processing technologies. It is demonstrated that the dispersion of nono-sized oxide particles in high density is effective to attain high-performance and high-Cr ODS steels have a high potential as fuel cladding materials for SCWR and LFR with high efficiency and high burnup. (authors)

  20. Comparative study of creep behaviour in three Cr Ni 15/15 steel stabilized with Ti and with different contents in W, Mn, Mo and Bor

    International Nuclear Information System (INIS)

    Solano, R.R.; Rivas, M. de las; Schirra, M.; Seith, B.

    1975-01-01

    The main difference between the three steels which are tested at temperature range from 650 0 C to 750 0 C is due to the hardening elements pf the matrix and the Boron content: 1. 12R72HV (X10NiCrMoTiB 1515) 2% Mn 1,5% Mo 80 ppmB 2. Vaccutherm (X12CrNiWTi 1613) 3% W 2,5 ppmB 3. RGT 21 (X12CrNiWTi 1613) 3% W 50 ppm B. The investigations of all casts are carried out in two different heat treatments which are suitable for the conditions required for the operation of the reactor. Cond. I: 1150 0 C 30 min, water quenced; 800 0 32 hour, air; 10% cold work. Cond. II: 1150 0 C 30 min, water quenched; 10% cold work. In connection with creep test the condition I irrespective of 3 steels show no remarkable difference. The observation at 750 0 C test temperature and also at condition II above 650 0 C on Boron-free Vaccutherm cast shows an unfavourable behaviour. There is no significant difference in the stress dependence of secondary creep rate and also absolute creep rate. A definite superiority is to be found for 12R72HV when considering the values for time-yield-limit-ratio and ductility compared to the W-steels. The test results shows different fracture behaviour. Transcrystalline fracture is found on cast 12R72HV, whereas RGT 21 and Vaccutherm show transition from transcrystalline to intercrystalline fracture, depending on the rupture time and test temperature. The long term rupture specimens show intercrystalline fracture. (author)

  1. Conversion of MX Nitrides to Modified Z-Phase in 9-12%Cr Ferritic Steels

    DEFF Research Database (Denmark)

    Cipolla, Leonardo

    for Z-phase formation was highlighted during the studies. Several 9-12%Cr commercial steels with prolonged high-temperature exposures have been investigated, too. The same mechanism of Z-phase formation observed in 12%Cr model alloys was identified in industrial 9-12%Cr steels after thousands of hours......The 9-12%Cr ferritic steels are extensively used in modern steam power plants at service temperature up to 620°C. Currently the best perform ing ferritic creep resistance steel is the ASTM Grade 92, whose high temperature strength has recently been assessed by European Creep Collaborative Committee...... in 2005 as 600°C/113MPa/10 5h. All previous attempts made in the last twenty years to develop ferritic steels for 650°C applications have failed due to the incapacity to combine the superior oxidation resistance, given by 12%Cr content, with excellent creep resistance of high-alloyed ferritic steels...

  2. Structure and magnetic properties of Cr nanoparticles and Cr2O3 nanoparticles

    International Nuclear Information System (INIS)

    Zhang, W.S.; Brueck, E.; Zhang, Z.D.; Tegus, O.; Li, W.F.; Si, P.Z.; Geng, D.Y.; Buschow, K.H.J.

    2005-01-01

    We have synthesized Cr nanoparticles by arc-discharge and Cr 2 O 3 nanoparticles by subsequent annealing the as-prepared Cr nanoparticles. The structure of these nanoparticles is studied by means of X-ray diffraction, X-ray photoelectron spectroscopy, and high-resolution transmission electron microscope. Most of the particles show a good crystal habit of well-defined cubic or orthorhombic shape, while some small particles show spherical shape. The as-prepared Cr nanoparticles have a BCC Cr core coated with a thin Cr 2 O 3 layer. Cr in the core of the particles heated at 873 K for 4 h is changed to Cr 2 O 3 . The results of magnetic measurements show that the Cr nanoparticles exhibit mainly antiferromagnetic properties, in addition to a weak-ferromagnetic component at lower fields. The weak-ferromagnetic component may be ascribed to uncompensated surface spins. For the field-cooled Cr 2 O 3 nanoparticles, an exchange bias is observed in the hysteresis loops, which can be interpreted as the exchange coupling between the uncompensated spins at the surface and the spins in the core of the Cr 2 O 3 nanoparticles

  3. Design of Novel Precipitate-Strengthened Al-Co-Cr-Fe-Nb-Ni High-Entropy Superalloys

    Science.gov (United States)

    Antonov, Stoichko; Detrois, Martin; Tin, Sammy

    2018-01-01

    A series of non-equiatomic Al-Co-Cr-Fe-Nb-Ni high-entropy alloys, with varying levels of Co, Nb and Fe, were investigated in an effort to obtain microstructures similar to conventional Ni-based superalloys. Elevated levels of Co were observed to significantly decrease the solvus temperature of the γ' precipitates. Both Nb and Co in excessive concentrations promoted the formation of Laves and NiAl phases that formed either during solidification and remained undissolved during homogenization or upon high-temperature aging. Lowering the content of Nb, Co, or Fe prevented the formation of the eutectic type Laves. In addition, lowering the Co content resulted in a higher number density and volume fraction of the γ' precipitates, while increasing the Fe content led to the destabilization of the γ' precipitates. Various aging treatments were performed which led to different size distributions of the strengthening phase. Results from the microstructural characterization and hardness property assessments of these high-entropy alloys were compared to a commercial, high-strength Ni-based superalloy RR1000. Potentially, precipitation-strengthened high-entropy alloys could find applications replacing Ni-based superalloys as structural materials in power generation applications.

  4. Comparison of the Content of Web Sites of Higher Education Institutions Providing for Sports Management Education: The Case of Turkish and English Universities

    Science.gov (United States)

    Katirci, Hakan

    2016-01-01

    Considering various themes, this study aims to examine the content of web sites of universities that provide sports management education in higher education level in Turkey and in England. Within this framework, the websites of the higher education institutions that provide sports management education are analyzed by using the content analysis…

  5. Chromium-rich lawsonite in high-Cr eclogites from the Făgăras Massif (South Carpathians)

    Science.gov (United States)

    Negulescu, E.; Săbău, G.

    2012-12-01

    Lawsonite is a relatively rare phase in natural rocks, because of its thermal decomposition during exhumation, and Cr-bearing lawsonite being restricted to only a few occurrences worldwide. Here we report Cr-lawsonite in eclogites hosted in a medium-grade metamorphic complex. Several high-Cr eclogite lenses occur in the Topolog Complex (Făgăras Massif) of dominantly gneissic-amphibolitic composition. High Cr contents are the result of emerald-green mm-sized nodules containing Cr-rich minerals, embedded in a gray-green matrix of kyanite, clinopyroxene, garnet, amphibole, zoisite, and rutile. Garnets occur as porphyroblasts or in coronas around clinopyroxene aggregates probably replacing former magmatic pyroxene. Relict gabbroic textures (sometimes pegmatoid) and whole rock geochemistry indicate a gabbroic cumulate origin. The REE pattern, displaying a slight positive Eu anomaly and a tea spoon-shaped LREE depletion is also indicative of a cumulate origin, as also noted by Pe Piper & Piper (2002) for the Othrys gabbro (as well as others in the Vourinos and Pindos ophiolitic suites) with the same unusual REE-pattern. The emerald-green Cr-rich nodules are unevenly distributed in the rock, and always enclosed in Cr-rich clinopyroxenes (up to 5.46% Cr2O3) which may exhibit Cr-diffusion haloes towards normal Cr-free matrix pyroxene. The nodules consist of diablastic chromite, rutile and Cr-rich kyanite of up to 15.67 wt% Cr2O3, Cr-bearing epidote, to which Cr-rich staurolite (up to 10.45% Cr2O3; XMg up to 0.68) and Cr-rich lawsonite (up to 9.17% Cr2O3) may exceptionally associate. Cr concentrations in kyanite and lawsonite are, to our knowledge, the highest reported so far. Cr-lawsonite was identified in a single sample, as small single phase inclusions armoured in Cr-kyanite. Equilibrium PT-conditions of 2.6 GPa and 610o C were derived from the garnet-mantled clinopyroxene aggregates using multi-equilibria calculation with the PTGIBBS routine of Brandelik & Massonne

  6. Redox transformation and reductive immobilization of Cr(VI) in the Columbia River hyporheic zone sediments

    Science.gov (United States)

    Xu, Fen; Liu, Yuanyuan; Zachara, John; Bowden, Mark; Kennedy, David; Plymale, Andrew E.; Liu, Chongxuan

    2017-12-01

    An experimental and modeling study was conducted to investigate the redox transformation and reductive immobilization of groundwater contaminant Cr in hyporheic zone (HZ) sediments from U.S. DOE's Hanford Site, where groundwater Cr(VI) is migrating and discharging to the nearby Columbia River. Experimental results revealed that Cr(VI) can be reduced and immobilized by the HZ sediments in the presence/absence of O2. Anaerobic pre-incubation of the sediments increased the effective rate of Cr reduction that was correlated with the increase in HCl-extractable Fe(II) content in the sediments. The reduced Cr was stable when exposed to O2 under field-relevant pH (7.5) with and without dissolved Mn(II), which might be oxidized to form Mn(III/IV) oxides that may oxidize reduced Cr. The Cr(VI) reduction rate showed a multi-rate behavior, apparently reflecting the presence of reductants with different reactivity in the sediments. The results from this study indicated that the HZ sediments can reductively immobilize Cr and the sediment redox capacity can be recharged through microbial activities. The results implied that HZ can play a role as a natural permeable redox barrier for removing groundwater Cr before it discharges into a river system.

  7. The Effect of Radiator on CR-39 Registration of Fast Neutrons

    International Nuclear Information System (INIS)

    El-Badrya, B.A.; Hegazya, T.M.; Morsya, A.A.; Zaki, M.F.

    2008-01-01

    Three different configurations of a personal neutron dosimeter using CR-39 plastic detector were placed in Plastiplast pouch composed from inside to outside of Aluminum ( 27 Al, 40 Ξ m), polyethylene (PE, 20 Ξ m), Cellulose Nitrate (CN, 40 Ξ m). One dosimeter was composed of a CR-39 detector and a PE radiator (1 mm thick), another of two CR-39 detectors with one serving as radiator, and the other of CR-39 alone (without radiator). These dosimeters have been irradiated with fast neutrons of average energy 4.5 MeV with neutron fluence ranging from 5.5 x 10 6 to 0.5 x 10 8 cm - 2 emitted from 241 Am-Be neutron source. The polymeric materials have been chosen on the basis of their hydrogen contents, which are as followed: CR-39, 48%, Polyethylene, 66.7% and CN, 32% by atomic ratio to produce protons via (n, p) elastic scattering with hydrogen and increasing the detection efficiency of CR-39. After irradiation, the dose equivalent response of the detectors has been studied by using conventional etching for two periods, 6h and 8h for these configurations. The thicknesses and compositions of the radiators are chosen so as to suppress the CR-39 response below 4 MeV by preventing the recoils of hydrogen nuclei, out of the hydrogen-rich radiators (PE, CR-39), from reaching the post-etch surface of the detector. Track counting was performed using an automated system. It was found that the dosemeter responses were linear as a function of a neutron equivalent dose and that the CR-39 detector has the same response with radiator or without radiator and thus appears as a promising fast neutron dosimeter. The results are discussed and compared with the literature

  8. Development of ODS FeCrAl alloys for accident-tolerant fuel cladding

    Energy Technology Data Exchange (ETDEWEB)

    Dryepondt, Sebastien N. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Hoelzer, David T. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Pint, Bruce A. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Unocic, Kinga A. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2015-09-18

    FeCrAl alloys are prime candidates for accident-tolerant fuel cladding due to their excellent oxidation resistance up to 1400 C and good mechanical properties at intermediate temperature. Former commercial oxide dispersion strengthened (ODS) FeCrAl alloys such as PM2000 exhibit significantly better tensile strength than wrought FeCrAl alloys, which would alloy for the fabrication of a very thin (~250 m) ODS FeCrAl cladding and limit the neutronic penalty from the replacement of Zr-based alloys by Fe-based alloys. Several Fe-12-Cr-5Al ODS alloys where therefore fabricated by ball milling FeCrAl powders with Y2O3 and additional oxides such as TiO2 or ZrO2. The new Fe-12Cr-5Al ODS alloys showed excellent tensile strength up to 800 C but limited ductility. Good oxidation resistance in steam at 1200 and 1400 C was observed except for one ODS FeCrAl alloy containing Ti. Rolling trials were conducted at 300, 600 C and 800 C to simulate the fabrication of thin tube cladding and a plate thickness of ~0.6mm was reached before the formation of multiple edge cracks. Hardness measurements at different stages of the rolling process, before and after annealing for 1h at 1000 C, showed that a thinner plate thickness could likely be achieved by using a multi-step approach combining warm rolling and high temperature annealing. Finally, new Fe-10-12Cr-5.5-6Al-Z gas atomized powders have been purchased to fabricate the second generation of low-Cr ODS FeCrAl alloys. The main goals are to assess the effect of O, C, N and Zr contents on the ODS FeCrAl microstructure and mechanical properties, and to optimize the fabrication process to improve the ductility of the 2nd gen ODS FeCrAl while maintaining good mechanical strength and oxidation resistance.

  9. Effect of Cr and Mo on strain ageing behaviour of low carbon steel

    International Nuclear Information System (INIS)

    Pereloma, E.V.; Bata, V.; Scott, R.I.; Smith, R.M.

    2010-01-01

    This work explores the effects of Cr (0.26-0.74 wt%) and Mo (0.09-0.3 wt%) additions on the kinetics of strain ageing process in low carbon steel. The strain ageing behaviour of the steels was investigated by using tensile tests and transmission electron microscopy. The results have shown that Mo-alloyed steels undergo the same four stages of ageing as unalloyed low carbon steel, whereas Cr-alloyed steels exhibit only three stages of ageing. At the same time, the addition of Mo accelerates the ageing response, while alloying with Cr reduces the rate of strain ageing by ∼3 times in comparison with non-alloyed low carbon steel. It especially delays the offset of Stage III. This is explained by the reduction of carbon content in ferrite due to the enrichment of cementite with Cr leading to the reduction of its equilibrium solubility in ferrite.

  10. Effect of Cr and Mo on strain ageing behaviour of low carbon steel

    Energy Technology Data Exchange (ETDEWEB)

    Pereloma, E.V., E-mail: elenap@uow.edu.au [School of Mechanical, Materials and Mechatronic Engineering, University of Wollongong, Northfields Avenue, Wollongong, NSW 2522 (Australia); Bata, V. [Department of Materials Engineering, Monash University (Australia); Scott, R.I.; Smith, R.M. [BlueScope Steel Limited, Port Kembla (Australia)

    2010-04-25

    This work explores the effects of Cr (0.26-0.74 wt%) and Mo (0.09-0.3 wt%) additions on the kinetics of strain ageing process in low carbon steel. The strain ageing behaviour of the steels was investigated by using tensile tests and transmission electron microscopy. The results have shown that Mo-alloyed steels undergo the same four stages of ageing as unalloyed low carbon steel, whereas Cr-alloyed steels exhibit only three stages of ageing. At the same time, the addition of Mo accelerates the ageing response, while alloying with Cr reduces the rate of strain ageing by {approx}3 times in comparison with non-alloyed low carbon steel. It especially delays the offset of Stage III. This is explained by the reduction of carbon content in ferrite due to the enrichment of cementite with Cr leading to the reduction of its equilibrium solubility in ferrite.

  11. Detection sensitivity of laser-induced breakdown spectroscopy for Cr II in liquid samples

    International Nuclear Information System (INIS)

    Rai, Nilesh K.; Rai, Awadhesh K.; Kumar, Akshaya; Thakur, Surya N.

    2008-01-01

    The performance of laser-induced breakdown spectroscopy (LIBS) has been evaluated for detection of toxic metals such as Cr in water. Pure aqueous solutions (unitary matrix) with variable Cr concentration were used to construct calibration curves and to estimate the LIBS limit of detection (LOD). The calibration curves for Cr in a binary matrix (Cr plus Cd) and a tertiary matrix (Cr plus Cd and Co) were used to evaluate the matrix effect on the LOD. The LOD for Cr was found to be 1.1, 1.5, and 2.0 ppm (parts in 10 6 ) in a unitary, binary, and tertiary matrix, respectively. Once calibrated, the system was utilized for the detection and quantification of the Cr in tannery wastewater collected from different locations in the industrial area of Kanpur, India, where Cr concentrations were determined to be far higher than the U.S. Environmental Protection Agency safe drinking water limit of 0.05 ppm

  12. Effect of Cr2O3 on the microstructure and non-ohmic properties of (Co, Sb)-doped SnO2 varistors

    International Nuclear Information System (INIS)

    Aguilar M, J. A.; Pech C, M. I.; Hernandez, M. B.; Rodriguez, E.; Garcia O, L.; Glot, A. B.

    2013-01-01

    The effect of Cr 2 O 3 addition on the physical characteristics, microstructure, and current-voltage properties of (Co-Sb)-doped SnO 2 varistors was investigated. SnO 2 -Co 3 O 4 -Sb 2 O 5 ceramics with additions of 0.0, 0.03, 0.05 and 0.07 mol % Cr 2 O 3 were sintered at 1350 C under ambient atmosphere and characterized micro structurally and electrically. The characterization by X-ray diffraction and scanning electron microscopy show that the microstructure remains as a single phase material with multimodal size distribution of SnO 2 grains. The greatest effect of Cr 2 O 3 additions is manifested in the electric breakdown field. Additions of high levels (0.07 and 0.05 %) of this oxide promote and increase of approximately 55% in this parameter compared to the Cr 2 O 3 -free sample. Another physical property is affected: the measured density values decreases as the Cr 2 O 3 content increases. A change in the nonlinearity coefficient value is produced only at the highest Cr 2 O 3 content while at intermediate levels there is not change at all. Consequently, when seeking high nonlinearity coefficients, intermediate levels of Cr 2 O 3 are not recommended. (Author)

  13. Trace element control in binary Ni-25Cr and ternary Ni-30Co-30Cr master alloy castings

    Energy Technology Data Exchange (ETDEWEB)

    Detrois, Martin [National Energy Technology Lab. (NETL), Albany, OR (United States); Oak Ridge Inst. for Science and Education (ORISE), Oak Ridge, TN (United States); Jablonski, Paul D. [National Energy Technology Lab. (NETL), Albany, OR (United States);

    2017-10-23

    Electro-slag remelting (ESR) is used for control of unwanted elements in commercial alloys. This study focuses on master alloys of Ni-25Cr and Ni-30Co-30Cr, processed through a combination of vacuum induction melting (VIM) and electro-slag remelting (ESR). Minor additions were made to control tramp element levels and modify the melting characteristics. Nitrogen and sulfur levels below 10 ppm and oxygen levels below 100 ppm were obtained in the final products. The role of the alloy additions in lowering the tramp element content, the resulting residual inclusions and the melting characteristics were determined computationally and confirmed experimentally. Additions of titanium were beneficial to the control of oxygen levels during VIM and nitrogen levels during ESR. Aluminum additions helped to control oxygen levels during remelting, however, aluminum pickup occurred when excess titanium was present during ESR. The usefulness of these master alloys for use as experimental remelt stock will also be discussed.

  14. Atomic resolution investigations of phase transformation from TaN to CrTaN in a steel matrix

    DEFF Research Database (Denmark)

    Danielsen, Hilmar Kjartansson; Hald, John

    2012-01-01

    strength of the steel. The Cr content promotes Z-phase precipitation, making MN strengthening of these materials unfeasible, since 12%Cr is necessary for oxidation resistance. The authors have suggested an acceleration of Z-phase precipitation to obtain a fine and stable distribution of CrMN instead of MN...... atoms diffuse from the steel matrix into TaN precipitates and physically transform them into CrTaN. The crystal structure of the precipitates changes from that of a typical MN NaCl type crystal structure to a Z-phase crystal structure with alternating double layers of Cr and TaN. Since there is a large......In development of 12%Cr high temperature steels used for fossil fired power plants, the precipitation of large Z-phase particles, CrMN, has been identified as a major problem since they replace small and finely distributed MN particles. This causes a premature breakdown in the longterm creep...

  15. Homogeneous and Heterogeneous (Fex, Cr1-x)(OH)3 Precipitation: Implications for Cr Sequestration.

    Science.gov (United States)

    Dai, Chong; Zuo, Xiaobing; Cao, Bo; Hu, Yandi

    2016-02-16

    The formation of (Fe, Cr)(OH)3 nanoparticles determines the fate of aqueous Cr in many aquatic environments. Using small-angle X-ray scattering, precipitation rates of (Fe, Cr)(OH)3 nanoparticles in solution and on quartz were quantified from 0.1 mM Fe(III) solutions containing 0-0.25 mM Cr(III) at pH = 3.7 ± 0.2. Concentration ratio of aqueous Cr(III)/Fe(III) controlled the chemical composition (x) of (Fex, Cr1-x)(OH)3 precipitates, solutions' supersaturation with respect to precipitates, and the surface charge of quartz. Therefore, the aqueous Cr(III)/Fe(III) ratio affected homogeneous (in solution) and heterogeneous (on quartz) precipitation rates of (Fex, Cr1-x)(OH)3 through different mechanisms. The sequestration mechanisms of Cr(III) in precipitates were also investigated. In solutions with high aqueous Cr(III)/Fe(III) ratios, surface enrichment of Cr(III) on the precipitates occurred, resulting in slower particle growth in solutions. From solutions with 0-0.1 mM Cr(III), the particles on quartz grew from 2 to 4 nm within 1 h. Interestingly, from solution with 0.25 mM Cr(III), particles of two distinct sizes (2 and 6 nm) formed on quartz, and their sizes remained unchanged throughout the reaction. Our study provided new insights on homogeneous and heterogeneous precipitation of (Fex, Cr1-x)(OH)3 nanoparticles, which can help determine the fate of Cr in aquatic environments.

  16. Chemical and electrochemical lithium insertion into ternary transition metal sulfides MMo[sub 2]S[sub 4] (M: V, Cr, Fe)

    Energy Technology Data Exchange (ETDEWEB)

    Maffi, S.; Peraldo Bicelli, L. (Milan Polytechnic (Italy). Dept. of Applied Physical Chemistry CNR, Milan (Italy). Research Centre on Electrode Processes); Barriga, C.; Lavela, P.; Morales, J.; Tirado, J.L. (Cordoba Univ. (Spain). Dept. de Quimica Inorganica e Ingenieria Quimica)

    1992-08-01

    The effects of lithium insertion in MMo[sub 2]S[sub 4] (M: V, Cr, Fe) have been studied by means of chemical and electrochemical insertion methods. The reaction has a topotactic character and a higher degree of lithium insertion was found for the compound FeMo[sub 2]S[sub 4] which has a greater unit cell volume. For this compound the changes in lattice parameters with lithium content are also more pronounced. The voltage composition curves show a smooth voltage decrease with a quasi-plateau located at around 1.3 V. For discharge at lithium content higher than 0.8, the voltage decreases quickly followed by an extended plateau below 1 V, a region where electrolyte decomposition may occur. The X-ray powder diffraction patterns of the electrochemical lithiated compounds show that the original monoclinic structure is maintained up to 0.8 e[sup -] per mole, buth with a significant change in the intensity of the peaks, indicative of an alteration of cation distribution for this degree of insertion. For high lithium content, such disorder promotes the collapse of the structure, resulting in the loss of long-range order of the material. (orig.).

  17. Magnetic susceptibilities of liquid Cr-Au, Mn-Au and Fe-Au alloys

    Energy Technology Data Exchange (ETDEWEB)

    Ohno, S.; Shimakura, H. [Niigata University of Pharmacy and Applied Life Sciences, Higashijima, Akiha-ku, Niigata 956-8603 (Japan); Tahara, S. [Faculty of Science, University of the Ryukyus, Nishihara-cho, Okinawa 903-0213 (Japan); Okada, T. [Niigata College of Technology, Kamishin’eicho, Nishi-ku, Niigata 950-2076 (Japan)

    2015-08-17

    The magnetic susceptibility of liquid Cr-Au, Mn-Au, Fe-Au and Cu-Au alloys was investigated as a function of temperature and composition. Liquid Cr{sub 1-c}Au{sub c} with 0.5 ≤ c and Mn{sub 1-c}Au{sub c} with 0.3≤c obeyed the Curie-Weiss law with regard to their dependence of χ on temperature. The magnetic susceptibilities of liquid Fe-Au alloys also exhibited Curie-Weiss behavior with a reasonable value for the effective number of Bohr magneton. On the Au-rich side, the composition dependence of χ for liquid TM-Au (TM=Cr, Mn, Fe) alloys increased rapidly with increasing TM content, respectively. Additionally, the composition dependences of χ for liquid Cr-Au, Mn-Au, and Fe-Au alloys had maxima at compositions of 50 at% Cr, 70 at% Mn, and 85 at% Fe, respectively. We compared the composition dependences of χ{sub 3d} due to 3d electrons for liquid binary TM-M (M=Au, Al, Si, Sb), and investigated the relationship between χ{sub 3d} and E{sub F} in liquid binary TM-M alloys at a composition of 50 at% TM.

  18. Hot corrosion of Co-Cr, Co-Cr-Al, and Ni-Cr alloys in the temperature range of 700-750 deg C

    Science.gov (United States)

    Chiang, K. T.; Meier, G. H.

    1980-01-01

    The effect of SO3 pressure in the gas phase on the Na2SO4 induced hot corrosion of Co-Cr, Ni-Cr, and Co-Cr-Al alloys was studied in the temperature range 700 to 750 C. The degradation of the Co-Cr and Ni-Cr alloys was found to be associated with the formation of liquid mixed sulfates (CoSO4-Na2SO4 or NiSO4-Na2SO4) which provided a selective dissolution of the Co or Ni and a subsequent sulfidation oxidation mode of attack which prevented the maintenance of a protective Cr2O3 film. A clear mechanism was not developed for the degradation of Co-Cr-Al alloys. A pitting corrosion morphology was induced by a number of different mechanisms.

  19. Microstructure and Wear Behavior of FeCoCrNiMo0.2 High Entropy Coatings Prepared by Air Plasma Spray and the High Velocity Oxy-Fuel Spray Processes

    Directory of Open Access Journals (Sweden)

    Tianchen Li

    2017-09-01

    Full Text Available In the present research, the spherical FeCoCrNiMo0.2 high entropy alloy (HEA powders with a single FCC solid solution structure were prepared by gas atomization. Subsequently, the FeCoCrNiMo0.2 coatings with a different content of oxide inclusions were prepared by air plasma spraying (APS and high-velocity oxy-fuel spraying (HVOF, respectively. The microstructure, phase composition, mechanical properties, and tribological behaviors of these HEA coatings were investigated. The results showed that both HEA coatings showed a typical lamellar structure with low porosity. Besides the primary FCC phase, a mixture of Fe2O3, Fe3O4, and AB2O4 (A = Fe, Co, Ni, and B = Fe, Cr was identified as the oxide inclusions. The oxide content of the APS coating and HVOF coating was calculated to be 47.0% and 12.7%, respectively. The wear resistance of the APS coating was approximately one order of magnitude higher than that of the HVOF coating. It was mainly attributed to the self-lubricated effect caused by the oxide films. The mass loss of the APS coating was mainly ascribed to the breakaway of the oxide film, while the main wear mechanism of the HVOF coating was the abrasive wear.

  20. Oxidation resistance of TiN, CrN, TiAlN and CrAlN coatings deposited by lateral rotating cathode arc

    International Nuclear Information System (INIS)

    Chim, Y.C.; Ding, X.Z.; Zeng, X.T.; Zhang, S.

    2009-01-01

    In this paper, four kinds of hard coatings, TiN, CrN, TiAlN and CrAlN (with Al/Ti or Al/Cr atomic ratio around 1:1), were deposited on stainless steel substrates by a lateral rotating cathode arc technique. The as-deposited coatings were annealed in ambient atmosphere at different temperatures (500-1000 o C) for 1 h. The evolution of chemical composition, microstructure, and microhardness of these coatings after annealing at different temperatures was systematically analyzed by energy dispersive X-ray spectroscopy (EDX), X-ray diffraction (XRD) and nanoindentation experiments. The oxidation behaviour and its influence on overall hardness of these four coatings were compared. It was found that the ternary TiAlN and CrAlN coatings have better oxidation resistance than their binary counterparts, TiN and CrN coatings. The Cr-based coatings (CrN and CrAlN) exhibited evidently better oxidation resistance than the Ti-based coatings (TiN and TiAlN). TiN coating started to oxidize at 500 o C. After annealing at 700 o C no N could be detected by EDX, indicating that the coating was almost fully oxidized. After annealed at 800 o C, the coating completely delaminated from the substrate. TiAlN started to oxidize at 600 o C. It was nearly fully oxidized (with little residual nitrogen detected in the coating by EDX) and partially delaminated at 1000 o C. Both CrN and CrAlN started to oxidize at 700 o C. CrN was almost fully oxidized (with little residual nitrogen detected in the coating by EDX) and partially delaminated at 900 o C. The oxidation rate of the CrAlN coating is quite slow. After annealing at 1000 o C, only about 19 at.% oxygen was detected and the coating showed no delamination. The Ti-based (TiN and TiAlN) coatings were not able to retain their hardness at higher temperatures (≥ 700 o C). On the other hand, the hardness of CrAlN was stable at a high level between 33 and 35 GPa up to an annealing temperature of 800 o C and still kept at a comparative high value of

  1. Synthesis of Patchouli Biochar Cr2O3 Composite Using Double Acid Oxidators for Paracetamol Adsorption

    Directory of Open Access Journals (Sweden)

    Tutik Setianingsih

    2018-01-01

    Full Text Available Composite built by patchouli biochar and metal oxide, Cr2O3, is a potential material for remediation of contaminated wasterwater. Oxidation of biochar using acid or salt oxidators can improve its surface polar functional groups. This treatment may be able to increase impregnation of metal cation (as salt before calcination to form its oxide. In this research, 3 types of oxidators were used to oxidize the biochar before impregnation with purpose to study its influence toward physichochemistry and adsorption performance of the composite. Preparation of the composite included 3 steps, including preparation of biochar by pyrolisis of patchouli biomass using ZnCl2 activator at 450 oC, oxidation of the biochar using 3 different oxidators (H2SO4-HNO3, H3PO4-HNO3, H2O2–HNO3 at 60 oC, impregnation of the oxidized biochar using CrCl3 followed by calcination process to form biochar–Cr2O3 composite at 600 oC. Characterization using X-ray diffraction indicated that the composite containes the Cr2O3 structure. FTIR spectrophotometry characterization indicates the different content of C=O, C-O, and –OH on the composite surface. SEM images shows irregular micro ball shapes. EDX characterization indicates the different Cr content in the composite with same sequence with FTIR absorbances of both C-O and –OH. Adsorption of paracetamol indicates effect of Cr2O3 showing the same sequence of both.

  2. Effect of Mo contents on corrosion behaviors of welded duplex stainless steel

    Science.gov (United States)

    Bae, Seong Han; Lee, Hae Woo

    2013-05-01

    The corrosion behaviour and change of the phase fraction in welded 24Cr Duplex stainless steel was investigated for different chemical composition ranges of Mo contents. Filler metal was produced by fixing the contents of Cr, Ni, N, and Mn while adjusting the Mo content to 0.5, 1.4, 2.5, 3.5 wt%. The δ-ferrite fraction was observed to increase as the content of Mo increased. A polarisation test conducted in a salt solution, indicated the pitting corrosion potential increased continuously to 3.5 wt% Mo, while the corrosion potential changed most between 0.5 and 1.41 wt% Mo. The location of the pitting corrosion in 0.5 wt% Mo steel was randomly distributed, but it occurred selectively at the grain boundary between the γ- and δ-ferrite phases in 1.4, 2.5 and 3.5 wt% Mo steel. Energy dispersive X-ray spectroscopy mapping analysis showed that areas deficient in Cr, Mo, and Ni occurred around the grain boundary of the γ- and δ-ferrite phases. Non-metallic inclusions are thought to act as initiation points for the pitting corrosion that occurs in the salt solution initially as a result of the potential difference between the matrix structure and the incoherent inclusions.

  3. Selected Heavy Metal Content in Ultra basic Soil and Mengkudu (Morinda citrifolia) from Kuala Pilah, Negeri Sembilan, Malaysia

    International Nuclear Information System (INIS)

    Sahibin Abdul Rahim; Wan Mohd Razi Idris; Zulfahmi Ali Rahman; Kadderi Mohd Desa; Tukimat Lihan; Azman Hashim; Sharilnizam Yusof; Kuan, L.H.

    2009-01-01

    This study was carried out at an ultra basic area, Selaru (S1 and S2) dan Felda Rokan Barat (S3), Kuala Pilah, Negeri Sembilan. Eighteen samples of plant and their substrates were collected from study area. The purpose of this study was to determine heavy metal such as Ni, Cr, Mn, Co, Fe and Zn contents in soils and different parts of the plant, such as leaf, stem, root and fruit. Biologal Absorption Coefficient (BAC) of the plant was obtained by calculation. Heavy metals content in the plant were extracted by digestion method whereas in soil the heavy metals were extracted by sequential extraction. Heavy metals content in soil and plant extract was determined using Flame Atomic Absorption Spectrophotometer. It was found that heavy metal concentrations in soil substrate for mengkudu (Morinda citrifolia) were high for Fe followed by Cr, Ni, Mn, Zn and Co with average concentration of 1208.5, 583.4, 352.4, 352.4, 70.7 and 53.6 mg.kg -1 , respectively. Available Mn and Zn concentrations were higher than the other heavy metals in term of percentage. Fe and Mn were dominant in all parts of plants however in terms of BAC average, Co showed the highest enrichment value in all parts of the plants. (author)

  4. Characterization of Ni–Cr alloys using different casting techniques and molds

    International Nuclear Information System (INIS)

    Chen, Wen-Cheng; Teng, Fu-Yuan; Hung, Chun-Cheng

    2014-01-01

    This study differentiated the mechanical properties of nickel–chromium (Ni–Cr) alloys under various casting techniques (different casting molds and casting atmospheres). These techniques were sampled by a sand mold using a centrifugal machine in ambient air (group I) and electromagnetic induction in an automatic argon castimatic casting machine (group II). The specimen casting used a graphite mold by a castimatic casting machine (group III). The characteristics of the Ni–Cr alloys, yield and ultimate tensile strength, bending modulus, microhardness, diffraction phase, grindability, ability to spring back, as well as ground microstructure and pattern under different casting conditions were evaluated. The group III specimens exhibited the highest values in terms of strength, modulus, hardness, and grindability at a grind rate of 500 rpm. Moreover, group III alloys exhibited smaller grain sizes, higher ability to spring back, and greater ductility than those casted by sand investment (groups I and II). The main factor, “casting mold,” significantly influenced all mechanical properties. The graphite mold casting of the Ni–Cr dental alloys in a controlled atmosphere argon casting system provided an excellent combination of high mechanical properties and good ability to spring back, and preserved the ductile properties for application in Ni–Cr porcelain-fused system. The results can offer recommendations to assist a prosthetic technician in selecting the appropriate casting techniques to obtain the desired alloy properties. - Highlights: • Properties of Ni–Cr alloys using various casting techniques are characterized. • Alloys cast by graphite mold exhibited higher recovery angle and more ductility. • Alloys cast by graphite mold exhibited higher strength and grinding rate. • Alloys in this study increase operative room to adjust the precision for prosthesis

  5. Characterization of Ni–Cr alloys using different casting techniques and molds

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Wen-Cheng, E-mail: wencchen@fcu.edu.tw [Advanced Medical Devices and Composites Laboratory, Department of Fiber and Composite Materials, College of Engineering, Feng Chia University, Taichung 40724, Taiwan (China); Teng, Fu-Yuan [Department of Dentistry, Kaohsiung Armed Forces General Hospital, Kaohsiung 802, Taiwan (China); School of Dentistry, College of Dental Medicine, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Hung, Chun-Cheng [School of Dentistry, College of Dental Medicine, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Department of Dentistry, Kaohsiung Medical University Hospital, Kaohsiung 807, Taiwan (China)

    2014-02-01

    This study differentiated the mechanical properties of nickel–chromium (Ni–Cr) alloys under various casting techniques (different casting molds and casting atmospheres). These techniques were sampled by a sand mold using a centrifugal machine in ambient air (group I) and electromagnetic induction in an automatic argon castimatic casting machine (group II). The specimen casting used a graphite mold by a castimatic casting machine (group III). The characteristics of the Ni–Cr alloys, yield and ultimate tensile strength, bending modulus, microhardness, diffraction phase, grindability, ability to spring back, as well as ground microstructure and pattern under different casting conditions were evaluated. The group III specimens exhibited the highest values in terms of strength, modulus, hardness, and grindability at a grind rate of 500 rpm. Moreover, group III alloys exhibited smaller grain sizes, higher ability to spring back, and greater ductility than those casted by sand investment (groups I and II). The main factor, “casting mold,” significantly influenced all mechanical properties. The graphite mold casting of the Ni–Cr dental alloys in a controlled atmosphere argon casting system provided an excellent combination of high mechanical properties and good ability to spring back, and preserved the ductile properties for application in Ni–Cr porcelain-fused system. The results can offer recommendations to assist a prosthetic technician in selecting the appropriate casting techniques to obtain the desired alloy properties. - Highlights: • Properties of Ni–Cr alloys using various casting techniques are characterized. • Alloys cast by graphite mold exhibited higher recovery angle and more ductility. • Alloys cast by graphite mold exhibited higher strength and grinding rate. • Alloys in this study increase operative room to adjust the precision for prosthesis.

  6. Influence of carbides and microstructure of CoCrMo alloys on their metallic dissolution resistance.

    Science.gov (United States)

    Valero-Vidal, C; Casabán-Julián, L; Herraiz-Cardona, I; Igual-Muñoz, A

    2013-12-01

    CoCrMo alloys are passive and biocompatible materials widely used as joint replacements due to their good mechanical properties and corrosion resistance. Electrochemical behaviour of thermal treated CoCrMo alloys with different carbon content in their bulk alloy composition has been analysed. Both the amount of carbides in the CoCrMo alloys and the chemical composition of the simulated body fluid affect the electrochemical properties of these biomedical alloys, thus passive dissolution rate was influenced by the mentioned parameters. Lower percentage of carbon in the chemical composition of the bulk alloy and thermal treatments favour the homogenization of the surface (less amount of carbides), thus increasing the availability of Cr to form the oxide film and improving the corrosion resistance of the alloy. © 2013.

  7. Citric acid enhanced the antioxidant defense system and chromium uptake by Lemna minor L. grown in hydroponics under Cr stress.

    Science.gov (United States)

    Sallah-Ud-Din, Rasham; Farid, Mujahid; Saeed, Rashid; Ali, Shafaqat; Rizwan, Muhammad; Tauqeer, Hafiz Muhammad; Bukhari, Syed Asad Hussain

    2017-07-01

    Phytoextraction is a cost-effective and eco-friendly technique for the removal of pollutants, mainly heavy metal(loids) especially from polluted water and metal-contaminated soils. The phytoextraction of heavy metals is, in general, limited due to the low availability of heavy metals in the growth medium. Organic chelators can help to improve the phytoextraction by increasing metal mobility and solubility in the growth medium. The present research was carried out to examine the possibility of citric acid (CA) in improving chromium (Cr) phytoextraction by Lemna minor (duckweed). For this purpose, healthy plants were collected from nearby marsh and grown in hydroponics under controlled conditions. Initial metal contents of both marsh water and plant were measured along with physico-chemical properties of the marsh water. Different concentrations of Cr and CA were applied in the hydroponics in different combinations after defined intervals. Continuous aeration was supplied and pH maintained at 6.5 ± 0.1. Results showed that increasing concentration of Cr significantly decreased the plant biomass, photosynthetic pigments, leaf area, and antioxidant enzyme activities (like catalase, ascorbate peroxidase, superoxide dismutase, peroxidase). Furthermore, Cr stress increased the Cr concentrations, electrolyte leakage, hydrogen peroxide, and malondialdehyde contents in plants. The addition of CA alleviated the Cr-induced toxicity in plants and further enhanced the Cr uptake and its accumulation in L. minor. The addition of CA enhanced the Cr concentration in L. minor by 6.10, 26.5, 20.5, and 20.2% at 0, 10, 100, and 200 μM Cr treatments, respectively, compared to the respective Cr treatments without CA. Overall, the results of the present study showed that CA addition may enhance the Cr accumulation and tolerance in L. minor by enhancing the plant growth and activities of antioxidant enzymes.

  8. Synthesis and characterization of CrCN–DLC composite coatings by cathodic arc ion-plating

    Energy Technology Data Exchange (ETDEWEB)

    Wang, R.Y. [School of Power and Mechanical Engineering, Wuhan University, Wuhan 430072 (China); Wang, L.L. [Key Laboratory of Artificial Nanomaterials and Nanostructure of Ministry of Education, School of Physics and Technology, Wuhan University, Wuhan 430072 (China); Liu, H.D. [School of Power and Mechanical Engineering, Wuhan University, Wuhan 430072 (China); Yan, S.J. [Key Laboratory of Artificial Nanomaterials and Nanostructure of Ministry of Education, School of Physics and Technology, Wuhan University, Wuhan 430072 (China); Chen, Y.M. [School of Power and Mechanical Engineering, Wuhan University, Wuhan 430072 (China); Fu, D.J. [Key Laboratory of Artificial Nanomaterials and Nanostructure of Ministry of Education, School of Physics and Technology, Wuhan University, Wuhan 430072 (China); Yang, B., E-mail: toyangbing@163.com [School of Power and Mechanical Engineering, Wuhan University, Wuhan 430072 (China)

    2013-07-15

    CrCN–DLC composite coatings were deposited onto silicon (1 0 0) and cemented carbides substrates using pure Cr targets under C{sub 2}H{sub 2} ambient by cathodic arc ion plating system. The influence of C{sub 2}H{sub 2} flow rate on the structure and mechanical properties of the coatings was investigated systemically. The coatings structure and bonding state were characterized by XRD, Raman and X-ray photoelectron spectroscopy. The chemical composition was measured by EDS. The mechanical performance and tribological behaviour of the coatings were studied by a hardness tester and ball-on-disc wear tester. The results showed that with increasing C{sub 2}H{sub 2} flow rate from 50 to 100 sccm, the corresponding hardness of coatings increased firstly and then decreased with further addition of C{sub 2}H{sub 2} flow rate. The coatings deposited at lower C{sub 2}H{sub 2} flow rate (less than 200 sccm) exhibited a relatively higher hardness value (more than HV{sub 0.025}2000) and then the hardness decrease with increasing C{sub 2}H{sub 2} flow rate. The friction coefficient also exhibited similar variation trend, when the C{sub 2}H{sub 2} flow rate was higher than 100 sccm, the friction coefficient decreased and then maintained in a relatively lower value from 0.18 to 0.24, which may be attribute to the increasing carbon content and the coating exhibited more diamond-like structure.

  9. Crystallization kinetics and magnetic properties of FeSiCr amorphous alloy powder cores

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Hu-ping [School of Logistics Engineering, Wuhan University of Technology, Wuhan 430063 (China); Wang, Ru-wu, E-mail: ruwuwang@hotmail.com [National Engineering Research Center For Silicon Steel, Wuhan 430080 (China); College of Materials Science and Metallurgical Engineering, Wuhan University of Science and Technology, Wuhan 430081 (China); Wei, Ding [School of Optical and Electronic Information, Huazhong University of Science and Technology, Wuhan 430074 (China); Zeng, Chun [National Engineering Research Center For Silicon Steel, Wuhan 430080 (China)

    2015-07-01

    The crystallization kinetics of FeSiCr amorphous alloy, characterized by the crystallization activation energy, Avrami exponent and frequency factor, was studied by non-isothermal differential scanning calorimetric (DSC) measurements. The crystallization activation energy and frequency factor of amorphous alloy calculated from Augis–Bennett model were 476 kJ/mol and 5.5×10{sup 18} s{sup −1}, respectively. The Avrami exponent n was calculated to be 2.2 from the Johnson–Mehl–Avrami (JMA) equation. Toroid-shaped Fe-base amorphous powder cores were prepared from the commercial FeSiCr amorphous alloy powder and subsequent cold pressing using binder and insulation. The characteristics of FeSiCr amorphous alloy powder and the effects of compaction pressure and insulation content on the magnetic properties, i.e., effective permeability μ{sub e}, quality factor Q and DC-bias properties of FeSiCr amorphous alloy powder cores, were investigated. The FeSiCr amorphous alloy powder cores exhibit a high value of quality factor and a stable permeability in the frequency range up to 1 MHz, showing superior DC-bias properties with a “percent permeability” of more than 82% at H=100 Oe. - Highlights: • The crystallization kinetics of FeSiCr amorphous alloy was investigated. • The FeSiCr powder cores exhibit a high value of Q and a stable permeability. • The FeSiCr powder cores exhibit superior DC-bias properties.

  10. Amorphous alloys in the U-Cr-V system

    International Nuclear Information System (INIS)

    Ray, R.; Musso, E.

    1979-01-01

    Amorphous uranium-chromium-vanadium alloys and a method of producing them are described. The uranium content of the alloys may vary between 60 and 80 atom percent, and chromium and vanadium between 0 and 40 atom percent, most particularly between 20 and 40 atom percent. A maximum of 10 atom percent of Cr or V may be replaced by other alloying elements, including metalloids and at least one transtion metal element. (LL)

  11. Effects of crumb rubber content and curing time on the properties of asphalt concrete and stone mastic asphalt using dry process

    Directory of Open Access Journals (Sweden)

    H.T. Tai Nguyen

    2018-05-01

    Full Text Available Along with the rapid increase in the number of road vehicles, a large amount of waste tires have been created, causing negative effects to the environment. Many attempts have been made to effectively reduce this type of solid waste including the reuse of recycled rubber powder from waste tires as an additive for improving the performance of asphalt mixtures. In this work, the authors aim to study the effects of crumb rubber (CR on the mechanical properties, especially the rutting resistance, of CR modified asphalt concrete (AC and stone mastic asphalt (SMA by varying two factors-namely, the content of additive and the curing time. The dimension of used CR ranges from 0 to 2.36 mm, which is not too coarse for promoting the CR–bitumen interaction and not too fine for facilitating the production of CR. The content of CR was increased gradually from 0 to 3% to examine the effects of CR content on the engineering properties and determine the optimal content in the mixture. It was observed that the optimal content is 1.5–2%, while the optimal curing time that contributes to the maximal increase in the mechanical characteristics of both mixtures could not be determined. In the range of 0–5 h of curing time, the longer the asphalt mixture is maintained at a high temperature, the better the performance of mixture will be. Ageing was found to have influence on the performance of asphalt mixtures; however, its effects are not as important as those of CR modification. Keywords: Crumb rubber, Dry process, Asphalt concrete, SMA, Curing time

  12. Chromium sorption and Cr(VI) reduction to Cr(III) by grape stalks and yohimbe bark.

    Science.gov (United States)

    Fiol, Núria; Escudero, Carlos; Villaescusa, Isabel

    2008-07-01

    In this work, two low cost sorbents, grape stalks and yohimbe bark wastes were used to remove Cr(VI) and Cr(III) from aqueous solutions. Batch experiments were designed to obtain Cr(VI) and Cr(III) sorption data. The mechanism of Cr(III) and Cr(VI) removal and Cr(VI) reduction to Cr(III) by the two vegetable wastes, has been investigated. Fourier transform infrared rays (FTIR) and X-ray photoelectron spectroscopy (XPS) analysis on solid phase were performed to determine the main functional groups that might be involved in metal uptake and to confirm the presence of Cr(III) on the sorbent, respectively. Results put into evidence that both sorbents are able to reduce Cr(VI) to its trivalent form.

  13. FT-Raman spectroscopic analysis of Nd:YAG and Er,Cr:YSGG laser irradiated enamel for preventive purposes

    Science.gov (United States)

    Ana, P. A.; Kauffmann, C. M. F.; Bachmann, L.; Soares, L. E. S.; Martin, A. A.; Gomes, A. S. L.; Zezell, D. M.

    2014-03-01

    This study evaluated the effect of combining laser irradiation with fluoride on an enamel microstructure and demineralization by FT-Raman spectroscopy (FTRS). Eighty human enamel slabs were divided into eight groups: (G1) untreated; (G2) acidulated phosphate fluoride application (APF—1.23% F- for 4 min) (G3) Nd:YAG irradiation (84.9 J cm-2, 60 mJ/pulse) (G4) Nd:YAG + APF; (G5) APF + Nd:YAG; (G6) Er,Cr:YSGG irradiation (2.8 J cm-2, 12.5 mJ/pulse) (G7) Er,Cr:YSGG + APF; and (G8) APF + Er,Cr:YSGG. After treatment, the samples were submitted to a ten-day pH-cycling model. Chemical changes were determined on the slabs before and after treatment, and also after pH-cycling, by FTRS in the range 400-4000 cm-1. The inorganic bands at 440, 590, 870, 960, 1100 cm-1, and the organic bands at 1270, 1450, 1670, 2945 cm-1 were considered. Demineralization promoted reduction in organic contents; Nd:YAG laser irradiation promoted loss of carbonate and organic content, while Er,Cr:YSGG did not produce significant changes in the relative band intensities of organic and inorganic contents of the enamel. In lased samples, no effects caused by pH-cycling on enamel were observed. In conclusion, laser treatment and its association with fluoride can somehow interfere with the demineralization dynamics, reducing its effects over the enamel.

  14. First-Principles Calculations for Chemical Reaction between Sodium Diethyldithiocarbamate and Transition-Metal (Cr) atom to Produce Cr(DDC)3 and Cr(DDC)2ODDC

    Science.gov (United States)

    Setiyanto, Henry; Muhida, Rifki; Kishi, Tomoya; Rempillo, Ofelia; Rahman, Mahmudur; Dipojono, Hermawan Kresno; Di\\ {n}o, Wilson Agerico; Matsumoto, Shigeno; Kasai, Hideaki

    2006-10-01

    We investigate the chemical reaction between a Cr transition-metal atom and sodium diethyldithiocarbamate (NaDDC), a complexing agent used to detect and extract Cr in human blood samples. Using density-functional-theory-based calculations, we determine their stable structures of Cr(DDC)2ODDC and Cr(DDC)3 complexes and obtain their dissociation energies. We found dissociation energies of -10.66 and -3.24 eV for Cr(DDC)2ODDC and Cr(DDC)3 complexes, respectively. Hence, on the basis of dissociation energies, we have verified that the reaction of NaDDC with Cr produces Cr(DDC)2ODDC as a major product.

  15. Annealing effects on structure and mechanical properties of CoCrFeNiTiAlx high-entropy alloys

    International Nuclear Information System (INIS)

    Zhang, K B; Fu, Z Y; Zhang, J Y; Wang, W M; Lee, S W; Niihara, K

    2011-01-01

    Novel CoCrFeNiTiAl x (x:molar ratio, other elements are equimolar) high-entropy alloys were prepared by vacuum arc melting and these alloys were subsequently annealed at 1000 deg. C for 2 h. The annealing effects on structure and mechanical properties were investigated. Compared with the as-cast alloys, there are many complex intermetallic phases precipitated from the solid solution matrix in the as-annealed alloys with Al content lower than Al 1.0 . Only simple BCC solid solution structure appears in the as-annealed Al 1.5 and Al 2.0 alloys. This kind of alloys exhibit high resistance to anneal softening. Most as-annealed alloys possess even higher Visker hardness than the as-cast ones. The as-annealed Al 0.5 alloys shows the highest compressive strength while the Al 0 alloy exhibits the best ductility, which is about 2.6 GPa and 13%, respectively. The CoCrFeNiTiAl x high-entropy alloys possess integrated high temperature mechanical property as well.

  16. The role of the Mg2+ ions in Cr3+ spectroscopy for near-stoichiometric LiNbO3 crystals

    International Nuclear Information System (INIS)

    Han, T P J; Jaque, F; Bermudez, V; Dieguez, E

    2003-01-01

    The optical spectroscopy of Cr 3+ ions doped into near-stoichiometric LiNbO 3 crystals, pure and co-doped with MgO, has been investigated. In the near-stoichiometric LiNbO 3 :Cr(0.2 mol%):Mg(2 mol%) crystal, the optical spectra resemble those previously observed for congruent LiNbO 3 :Cr:MgO samples when the total MgO content exceeds the 4.6 mol% threshold. The coexistence of two types of Cr 3+ centre ([Cr] Li and [Cr] Nb ) characterized the optical and luminescence spectra of this sample. The concentration equilibrium between the two types of centre is strongly displaced towards the [Cr 3+ ] Nb centre, permitting us to obtain with accuracy the parameters of the broad bands. The R-line associated with the [Cr] Nb centre is only observable in the low-temperature emission spectrum. The Fano anti-resonance lines present have been observed to be more pronounced for the near-stoichiometric samples than for congruent ones

  17. In silico CrNF, a half-metallic ferromagnetic nitride–fluoride mimicking CrO2

    International Nuclear Information System (INIS)

    Matar, Samir F.

    2014-01-01

    Isoelectronic with CrO 2 , CrNF is proposed in silico based on rutile derived structures with DFT computations. The ground state structure defined from cohesive energies is of MgUO 4 -type, characterized by short covalent Cr–N and long ionic Cr–F distances. Like CrO 2 it is a half-metallic ferromagnet with M=2 μ B /FU integer magnetization with reduced band gap at minority spins. Major difference of magnetic response to pressure characterizes CrNF as a soft ferromagnet versus hard magnetic CrO 2 . The chemical bonding properties point to prevailing covalent Cr–N versus ionic Cr–F bonding. Different synthesis routes are examined. - Highlights: • DFT identification of CrNF is based on isoelectronicity and rutile derivatives. • Similarly to CrO 2 , CrNF is a half-metallic ferromagnet with reduced band gap. • Strong pressure dependence of magnetization of CrNF oppositely to CrO 2 . • Covalent Cr–N bonding prevails in spite of the presence of ionic Cr–F. • Cohesive energies favor the synthesis for which protocols are proposed

  18. Visible light-responded C, N and S co-doped anatase TiO{sub 2} for photocatalytic reduction of Cr(VI)

    Energy Technology Data Exchange (ETDEWEB)

    Lei, X.F., E-mail: leixuefei69@163.com [School of Resources and Materials, Northeastern University at Qinhuangdao, Qinhuangdao 066004 (China); Institute of Metallurgical Resource and Environmental Engineering, Northeastern University, Shenyang 110819 (China); Liaoning Key Laboratory of Metallurgical Resource Recycling Science, Shenyang 110819 (China); Liaoning Engineering and Technology Research Center of Boron Resource, Comprehensive, Utilization, Shenyang 110819 (China); Liaoning Provincial Universities Key Laboratory of Boron Resource Ecological, Utilization, Technology and Boron Materials, Shenyang 110819 (China); Xue, X.X.; Yang, H. [Institute of Metallurgical Resource and Environmental Engineering, Northeastern University, Shenyang 110819 (China); Liaoning Key Laboratory of Metallurgical Resource Recycling Science, Shenyang 110819 (China); Liaoning Engineering and Technology Research Center of Boron Resource, Comprehensive, Utilization, Shenyang 110819 (China); Liaoning Provincial Universities Key Laboratory of Boron Resource Ecological, Utilization, Technology and Boron Materials, Shenyang 110819 (China); Chen, C.; Li, X.; Pei, J.X.; Niu, M.C.; Yang, Y.T.; Gao, X.Y. [School of Resources and Materials, Northeastern University at Qinhuangdao, Qinhuangdao 066004 (China)

    2015-10-15

    The (C, N and S) co-doped TiO{sub 2} (TH-TiO{sub 2}) samples were synthesized by a sol-gel method calcined at 500 °C, employing butyl titanate as the titanium source and thiourea as the dopant. The structures of TH-TiO{sub 2} samples were characterized by X-ray diffraction (XRD), Transmission electron microscope (TEM), X-ray photoelectron spectroscopy (XPS), UV–vis diffuse reflectance spectra (DRS), photoluminescence (PL) spectroscopy, Thermo gravimetry and differential thermal analysis (TG-DTA), Scanning electron microscopy (SEM) and nitrogen adsorption–desorption isotherms. The photocatalytic activities were checked through the photocatalytic reduction of Cr(VI) as a model compound under visible light irradiation. The results showed that the thiourea content played an important role on the microstructure and photocatalytic activity of the samples. According to XPS results, (C, N and S) atoms were successfully co-doped into the nanostructures of TH-TiO{sub 2} samples. TH-TiO{sub 2} samples with thiourea: Ti molar ratio of 1.5 exhibits higher photocatalytic activity than that of the other samples under visible light irradiation, which can be attributed to the synergic effect of the pure anatase structure, the higher light absorption characteristics in visible regions, separation efficiency of electron–hole pairs, the specific surface area and the optimum (C, N and S) content. - Graphical abstract: (C, N and S) co-doped TiO{sub 2} samples show good photocatalytic activity for Cr (VI) reduction under visible light irradiation. - Highlights: • (C, N and S) co-doping in TH-TiO{sub 2} samples can promote the formation of the pure anatase structure. • (C, N and S) atoms were successfully co-doped into the nanostructures of TH-TiO{sub 2} samples. • The band gap energy of TH-TiO{sub 2} samples reduced after (C, N and S) co-doping. • (C, N and S) co-doped TiO{sub 2} samples were effective for the photocatalytic reduction of Cr(VI) under visible light

  19. Chromium isotope inventory of Cr(VI)-polluted groundwaters at four industrial sites in Central Europe

    Science.gov (United States)

    Novak, Martin; Martinkova, Eva; Chrastny, Vladislav; Stepanova, Marketa; Curik, Jan; Szurmanova, Zdenka; Cron, Marcel; Tylcer, Jiri; Sebek, Ondrej

    2016-04-01

    Chromium is one of the most toxic elements, especially in its dissolved Cr(VI) form. In the Czech Republic (Central Europe), massive contamination of groundwater has been reported at more than 200 industrial operations. Under suitable conditions, i.e., low Eh, and high availability of reductive agents, Cr(VI) in groundwater may be spontaneously reduced to solid, largely non-toxic Cr(III). This process is associated with a Cr isotope fractionation, with the residual liquid Cr(VI) becoming enriched in the heavier isotope 53Cr. At industrial operations that have been closed and/or where no further leakage of Cr(VI) occurs, the contaminated groundwater plume may be viewed as a closed system. At such sites, an increasing degree of Cr(VI) reduction should result in an increasing del53/52Cr value of the residual liquid. Here we present del53/52Cr systematics at four contaminated Czech sites, focusing on groundwaters. At two of the four sites (Zlate Hory, Loucna) we were also able to analyze the source of contamination. Chromium in the electroplating solutes was isotopically relatively light, with del53/52Cr values 4.0 per mil (mean of +1.7 per mil); at Letnany, del53/52Cr ranged between +2.0 and +4.5 per mil (mean of +3.2 per mil); and at Velesin, del53/52Cr ranged between +0.5 and +4.5 per mil (mean of +2.7 per mil). Cr(VI) reduction may proceed at Zlate Hory and Loucna, where del53/52Cr(VI) values in groundwater were on average higher than those of the contamination source. At these two sites, our Cr isotope data are not consistent with the existing estimates of the amount of dissolved and precipitated Cr: The pool size of solid Cr(III) in the soil was estimated at 6600 and 500 kg at Zlate Hory and Loucna, respectively. At the same time, the pool size of dissolved Cr(VI) was estimated at 50 and 1.2 kg at Zlate Hory and Loucna, respectively. It follows that, at both sites, less than 1 % of the entire Cr that had leaked into the aquifer an a liquid form remained in the

  20. Slurry Erosion Behavior of Destabilized and Deep Cryogenically Treated Cr-Mn-Cu White Cast Irons

    Directory of Open Access Journals (Sweden)

    S. Gupta

    2016-12-01

    Full Text Available The effects of destabilization treatment and destabilization followed by cryogenic treatment have been evaluated on the microstructural evolution and sand-water slurry erosion behavior of Cr-Mn-Cu white cast irons. The phase transformations after the destabilization and cryotreatment have been characterized by bulk hardness measurement, optical and scanning electron microscopy, x-ray diffraction analysis. The static corrosion rate has been measured in tap water (with pH=7 and the erosion-corrosion behavior has been studied by slurry pot tester using sand-water slurry. The test results indicate that the cryogenic treatment has a significant effect in minimizing the as-cast retained austenite content and transforming into martensitic and bainitic matrix embedded with ultra-fine M7C3 alloy carbides. In contrast, by conventional destabilization treatment retained austenite in the matrix are not fully eliminated. The slurry erosive wear resistance has been compared with reference to destabilized and cryotreated high chromium iron samples which are commonly employed for such applications. The cryotreated Cr-Mn-Cu irons have exhibited a comparable erosive wear performance to those of high chromium irons. Higher hardness combined with improved corrosion resistance result in better slurry erosion resistance.

  1. Relationship between bias voltage and microstructure as well as properties of CrAlYN films

    International Nuclear Information System (INIS)

    Fu Ying-Ying; Li Hong-Xuan; Ji Li; Liu Xiao-Hong; Zhou Hui-Di; Chen Jian-Min; Liu Liu

    2015-01-01

    In this work, a series of CrAlYN films doped with 1 at.% yttrium were deposited by unbalanced reactive magnetron sputtering under different bias voltages. The effects of bias voltage on microstructure and properties of the CrAlYN films were subsequently investigated. It is found that all the as-deposited films have similar chemical composition and crystalline structure. However, the bias voltage has significant impact on the mechanical properties and oxidation resistance of the resulting films. Namely, the film deposited at 100 V has the highest hardness and best oxidation resistance, which are mainly attributed to its denser structure and higher Al content than others. In addition, the film obtained at 100 V exhibits superior oxidation resistance even at 1000 °C, and good friction and wear properties at 600 and 800 °C, and the latter two are mainly ascribed to the formation of compact transfer layer on the worn surfaces. However, this film experienced obvious wear loss at low testing temperatures (i.e., 200 and 400 °C) due to the serious abrasive wear. (paper)

  2. Structure and corrosion properties of PVD Cr-N coatings

    International Nuclear Information System (INIS)

    Liu, C.; Bi, Q.; Ziegele, H.; Leyland, A.; Matthews, A.

    2002-01-01

    PVD Cr-N coatings produced by physical vapor deposition (PVD) are increasingly used for mechanical and tribological applications in various industrial sectors. These coatings are particularly attractive for their excellent corrosion resistance, which further enhances the lifetime and service quality of coated components. PVD Cr-N coated steels in an aqueous solution are usually corroded by galvanic attack via through-coating 'permeable' defects (e.g., pores). Therefore, the corrosion performance of Cr-N coated steel is determined by a number of variables of the coating properties and corrosive environment. These variables include: (i) surface continuity and uniformity; (ii) through-coating porosity; (iii) film density and chemical stability; (iv) growth stresses; (v) interfacial and intermediate layers; (vi) coating thickness; (vii) coating composition; and (viii) substrate properties. In this article, PVD Cr-N coatings were prepared, by electron-beam PVD and sputter deposition, with different compositions, thicknesses, and surface roughnesses, by changing the N 2 flow rate, applying multilayering techniques and changing the substrate finish prior to coating. The microstructure of such coatings is investigated by various analytical techniques such as glancing angle x-ray diffraction and scanning electron microscopy, which are also correlated with the corrosion performance of the coated steel. Both dc polarization and ac impedance spectroscopy were employed to investigate the corrosion resistance of Cr-N coated steel in a 0.5N NaCl solution. It has been found that the N 2 flow rate during reactive deposition strongly determines the microstructure of Cr-N coatings (due to the changing nitrogen content in the film) and can thus affect the corrosion resistance of coated systems. The surface finish of the steel substrate also affects the uniformity and coverage of PVD coatings; grooves and inclusions on the original substrate can raise the susceptibility of coated

  3. Low-field spin dynamics of Cr7Ni and Cr7Ni-Cu -Cr 7Ni molecular rings as detected by μ SR

    Science.gov (United States)

    Sanna, S.; Arosio, P.; Bordonali, L.; Adelnia, F.; Mariani, M.; Garlatti, E.; Baines, C.; Amato, A.; Sabareesh, K. P. V.; Timco, G.; Winpenny, R. E. P.; Blundell, S. J.; Lascialfari, A.

    2017-11-01

    Muon spin rotation measurements were used to investigate the spin dynamics of heterometallic Cr7Ni and Cr7Ni -Cu-Cr7Ni molecular clusters. In Cr7Ni the magnetic ions are arranged in a quasiplanar ring and interact via an antiferromagnetic exchange coupling constant J , while Cr7Ni -Cu-Cr7Ni is composed of two Cr7Ni linked by a bridging moiety containing one Cu ion, that induces an inter-ring ferromagnetic interaction J'≪J . The longitudinal muon relaxation rate λ collected at low magnetic fields μ0H BPP)-like heuristic fitting model that takes into account of a distribution of electronic spin characteristic times for T >5 K, while the shoulder presented by Cr7Ni can be reproduced by a BPP function that incorporates a single electronic characteristic time theoretically predicted to dominate for T <5 K. The flattening of λ (T ) in Cr7Ni -Cu-Cr7Ni occurring at very low temperature can be tentatively attributed to field-dependent quantum effects and/or to an inelastic term in the spectral density of the electronic spin fluctuations.

  4. Role of oxides and porosity on high temperature oxidation of liquid fuelled HVOF thermal sprayed Ni50Cr coatings

    OpenAIRE

    Song, B.; Bai, M.; Voisey, K.T.; Hussain, Tanvir

    2017-01-01

    High chromium content in Ni50Cr thermally sprayed coatings can generate a dense and protective scale at the surface of coating. Thus, the Ni50Cr coating is widely used in high temperature oxidation and corrosion applications. A commercially available gas atomized Ni50Cr powder was sprayed onto a power plant steel (ASME P92) using a liquid fuelled high velocity oxy-fuel (HVOF) thermal spray with three processing parameters in this study. Microstructure of as-sprayed coatings was examined using...

  5. [Thallium content in adults older than 45 ages at Hezhang County of Guizhou Province].

    Science.gov (United States)

    Zhang, Wenli; Yao, Dancheng; Feng, Jiali; Zeng, Dong; Fan, Di; Shang, Qi

    2011-05-01

    To investigate the feature of Thallium content in adults of heavy metal contaminated district due to mining of Hezhang County, Guizhou Province. METHODS The subjects older than 45 ages were randomly recruited from the mineralized district (Magu village) and no-mineralized district (Salaxi viillage) , urine of villagers were collected and thallium content in urine were detected with ICP-MS. The average thallium contents in urine of Magu villagers were higner than those of Salaxi villagers,The urinary thallium contents of female were higner than those of male. The urinary thallium contents of residents in two districts were mostly under the upper limit of exposure in human bodies. There was no villager suffered from chronic poisoning of thallium in the two observing districts, the 95% upper limits of urinary thallium content for nonoccupational women older than 45 ages in Magu village was 8 microg/gCr and those for other nonoccupational subjects older than 45 ages was 5 microg/gCr.

  6. Manufacture of semifinished items of alloys V-4Ti-4Cr and V-10Ti-5Cr for use as a structural material in fusion applications

    International Nuclear Information System (INIS)

    Potapenko, M.M.; Drobishev, V.A.; Filkin, V.Y.; Gubkin, I.N.; Myasnikov, V.V.; Nikulin, A.D.; Shingarev, E.N.; Vedernikov, G.P.; Votinov, S.N.; Zurabov, V.S.; Zolotarev, A.B.

    1996-01-01

    Vanadium-titanium-chromium alloys are considered as structural materials with the most appropriate properties for fusion applications. However, the final ratio V-Ti-Cr in an alloy is not yet determined. On the one hand, it is offered to optimize structure on the basis of an alloy V-4Ti-4Cr. On the other hand, it is proposed that the optimum of total Ti and Cr content should be near 15%, and the Ti to Cr ratio should be 2:1. Melting, casting and processing by pressure of ingots of vanadium alloys V-4Ti-4Cr and V-10Ti-5Cr weighing as much as 50 kg are considered in the report. The ingots in diameters up to 130 mm were obtained by melting in vacuum-arc furnaces. Results on chemical uniformity and structure of the ingots are presented. A basic scheme of semifinished items manufacture is submitted. Rod and tube hot extrusion conditions are presented. A new technology for protection of ingot and billet surface from gases during hot processing is used to discard application of protective stainless steel and to lower temperature of processing. Sheet and tube products were made from extruded billets by cold rolling with intermediate heat treatment. The list of obtained products, including sheets 0.5-5 mm thick, rods 10-18 mm in diameter and tubes from 50 mm up to 6.0 mm in diameter is presented. The availability of large-scale ingots processing with weight above 300 kg is discussed. (orig.)

  7. XRD and TEM analysis of microstructure in the welding zone of 9Cr ...

    Indian Academy of Sciences (India)

    Unknown

    XRD and TEM analysis of microstructure in the welding zone of. 9Cr–1Mo–V–Nb ... steel, which has highest Cr content in the heat-resisting. Cr–Mo ... This research provides essential ... film samples were observed under TEM and select elec-.

  8. High plant uptake of radiocesium from organic soils due to Cs mobility and low soil K content

    International Nuclear Information System (INIS)

    Sanchez, A.L.; Wright, S.M.; Naylor, C.; Kennedy, V.H.; Dodd, B.A.; Singleton, D.L.; Barnett, C.L.; Stevens, P.A.

    1999-01-01

    Post-Chernobyl experience has demonstrated that persistently high plant transfer of 137 Cs occurs from organic soils in upland and seminatural ecosystems. The soil properties influencing this transfer have been known for some time but have not been quantified. A pot experiment was conducted using 23 soils collected from selected areas of Great Britain, which were spiked with 134 Cs, and Agrostis capillaris grown for 19--45 days. The plant-to-soil 134 Cs concentration ratio (CR) varied from 0.06 to 44; log CR positively correlated to soil organic matter content (R 2 = 0.84), and CR values were highest for soils with low distribution coefficients (K d ) of 134 Cs. Soils with high organic matter contents and high concentrations of NH 4 + in solution showed high 134 Cs mobility (low K d ). The plant-to-soil solution 134 Cs ratio decreased sharply with increasing soil solution K + . A two parameter linear model, used to predict log CR from soil solution K + and K d , explained 94% of the variability in CR values. In conclusion, the high transfer of 134 Cs in organic soils is related to both the high 134 Cs mobility (low clay content and high NH 4 + concentrations) and low K availability

  9. Effect of interfacial defects on the electronic and magnetic properties of epitaxial CrAs/InAs and CrAs/CdSe half-metallic multilayers

    International Nuclear Information System (INIS)

    Galanakis, I.; Lekkas, I.

    2010-01-01

    We present an extended study of single impurity atoms at the interface between the half-metallic ferromagnetic zinc-blende CrAs compound and the zinc-blende binary InAs and CdSe semiconductors in the form of very thin multilayers. Contrary to the case of impurities in the perfect bulk CrAs studied in Galanakis and Pouliasis [J. Magn. Magn. Mater. 321 (2009) 1084] defects at the interfaces do not alter in general the half-metallic character of the perfect systems. The only exception are Void impurities at Cr or In(Cd) sites which lead, due to the lower-dimensionality of the interfaces with respect to the bulk CrAs, to a shift of the p bands of the nearest neighboring As(Se) atom to higher energies and thus to the loss of the half-metallicity. But Void impurities are Schottky-type and should exhibit high formation energies and thus we expect the interfaces in the case of thin multilayers to exhibit a robust half-metallic character.

  10. Effect of Ni and Cr on IGSCC growth rate of Ni-Cr-Fe alloys in PWR primary water

    International Nuclear Information System (INIS)

    Arioka, K.; Yamada, T.; Aoki, M.; Miyamoto, T.

    2015-01-01

    The purpose of this research is to examine the dependence of SCC (Stress Corrosion Crack) growth on nickel and chromium in PWR primary water; the objective is to obtain the basic knowledge to understand SCC behavior of steam generator tubing materials. The second objective is to understand whether accelerated testing at higher temperatures is appropriate for predicting SCC initiation and growth at lower temperatures. For these objectives, SCC growth was measured in PWR primary water at 290, 320, 330, 340, and 360 C. degrees under static load conditions. Tests were performed using 0.5 T compact tension type specimen using 20%CW X%Ni-16%Cr-Fe alloys in the range of nickel concentration between 16 to 60% and laboratory melted nuclear grade 20% cold worked Alloy 800 (USN N08800, CW800NG). Four important patterns were observed. First, significant effect of nickel on IGSCC resistance was observed at 340 and 360 C. degrees. The rate of IGSCC growth decreases with increasing nickel concentration in the range of nickel concentration between 10% to 25% nickel; and then, the rate of IGSCC increases with increasing nickel concentration in the range of Ni content between 50% and 76%. This trend is quite similar to the results reported by Coriou and Staehle tested in deaerated pure water at 350 C. degrees. However, no significant dependence of Ni content on IGSCC in PWR water at 320 and 290 C. degrees was observed. The change in SCC growth dependence on nickel concentration suggested that the main rate limiting processes on IGSCC growth seems to change between 320 and 340 C. degrees. Secondly, significant beneficial effects of chromium in alloys were observed at 320 C. degrees. However, no beneficial effect of chromium addition in alloys was observed at 360 C. degrees. Thirdly, peak temperatures in growth rate of IGSCC were observed in almost all test materials except for 20%CW Alloy 600. Finally, intergranular attack was observed in some alloys at lower temperature, and the

  11. Study on the prediction of soil heavy metal elements content based on visible near-infrared spectroscopy.

    Science.gov (United States)

    Liu, Jinbao; Zhang, Yang; Wang, Huanyuan; Du, Yichun

    2018-06-15

    The estimation of soils heavy metal content can reflect the impending surroundings of surface, which lays theoretical foundation for using covered vegetation to monitor environment and investigate resource. In this study, the contents of Cr, Mn, Ni, Cu, Zn, As, Cd, Hg and Pb in 44 soil samples were collected from Fufeng County, Yangling County and Wugong County, Shaanxi Province and were used as data sources. ASD FieldSpec HR (350-2500nm), and then the NOR, MSC and SNV of the reflectance were pretreated, the first deviation, second deviation and reflectance reciprocal logarithmic transformation were carried out. The optimal spectroscopy estimation model of nine heavy metal elements of Cr, Mn, Ni, Cu, Zn, As, Cd, Hg and Pb was established by regression method. Comparing the diffuse reflectance characteristics of different heavy metal contents and the effect of different pretreatment methods on the establishment of soil heavy metal spectral inversion model. The results of chemical analysis show that there was a serious Hg pollution in the study area, and the Cd content was close to the critical value. The results show that: (1) NOR, MSC and SNV were adopted for the acquisition of visible near-infrared. Combining differential transformation can improve the information of heavy metal elements in the soil, and use the correlation band energy Significantly improve the stability and predictability of the model. (2) The modeling accuracy of the optimal model of nine heavy metal spectra of Cr, Mn, Ni, Cu, Zn, As, Cd, Hg and Pb by PLSR method were 0.70, 0.79, 0.69, 0.81, 0.86, 0.58, 0.55, 0.99, 0.62. (3) The optimal estimation model of different elements using different treatment methods has better stability and higher precision, and can realize the rapid prediction of nine kinds of heavy metal elements in this region. Copyright © 2018 Elsevier B.V. All rights reserved.

  12. The effect of microstructural stability on long-term creep behaviour of 11 %Cr steels for steam power plants with operating steam temperatures up to 650 C

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Y.; Scholz, A.; Berger, C. [Technische Univ. Darmstadt (DE). Inst. fuer Werkstoffkunde (IFW); Kauffmann, F.; Maile, K. [Stuttgart Univ. (DE). Materialpruefungsanstalt (MPA); Mayer, K.H. [Alstom Power, Nuernberg (Germany)

    2010-07-01

    The investigations of advanced ferritic/martensitic steels for 650 C power plant components focus on the improvement of high-temperature creep properties with respect to chemical composition. This study deals with the development of new heat resistant 11-12%Cr ferritic-martensitic steels with sufficient creep and oxidation resistance up to 650 application by using basic principles and concepts of physical metallurgy. The highest creep strength could be achieved with a 0.04% Nb alloyed 11%CrWCoMoVB melt, which is in addition alloyed with a higher C and B content as well as with lower W and Co portions. The microstructure evolution during creep of this newly developed steel was investigated in comparison to a sister alloy which comprises 0.06% Ta instead of the Nb. (orig.)

  13. Effect of carbon and manganese on the microstructure and mechanical properties of 9Cr2WVTa deposited metals

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Jian [Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, 110016, Shenyang (China); Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, 110016, Shenyang (China); Rong, Lijian [Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, 110016, Shenyang (China); Li, Dianzhong [Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, 110016, Shenyang (China); Lu, Shanping, E-mail: shplu@imr.ac.cn [Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, 110016, Shenyang (China); Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, 110016, Shenyang (China)

    2017-03-15

    Six 9Cr2WVTa deposited metals with different carbon and manganese contents have been studied to reveal the role of major elements, which guide for the design of welding consumables for reduced activation ferritic/martensitic steel and meet for the requirements of accelerator driven systems-lead fusion reactors. The typical microstructure for the 9Cr2WVTa deposited metals is the lath martensite along with the fine stripe δ-ferrite. The chemical compositions influence the solidification sequence and therefore, change the δ-ferrite content in the deposited metal. The impact toughness for the 9Cr2WVTa deposited metals decreases remarkably when the δ-ferrite content is more than 5.2 vol%, also the impact toughness decreases owing to the high quenching martensite formation. Increasing the level of manganese addition, α phase of each alloy shifts to the bottom right according to the CCT diagram. - Highlights: • The typical deposited metals is the lath martensite with the fine stripe δ-ferrite. • The impact toughness is dependent on the δ-ferrite and the high quenching martensite. • The chemical compositions influence the solidification sequence.

  14. Electronic structure and magnetic ordering of the semiconducting chromium trihalides CrCl3, CrBr3, and CrI3

    KAUST Repository

    Wang, Hao; Eyert, Volker; Schwingenschlö gl, Udo

    2011-01-01

    for CrBr3 as well as CrI3. The antiferromagnetic state of CrCl3 can be reproduced by introducing an on-site electron-electron repulsion. However, we observe that the ground state depends critically on the specific approach used. Our results show that a

  15. Mathematical models applied to the Cr(III) and Cr(VI) breakthrough curves.

    Science.gov (United States)

    Ramirez C, Margarita; Pereira da Silva, Mônica; Ferreira L, Selma G; Vasco E, Oscar

    2007-07-19

    Trivalent and hexavalent chromium continuous biosorption was studied using residual brewer Saccharomyces cerevisiae immobilized in volcanic rock. The columns used in the process had a diameter of 4.5 cm and a length of 140 cm, working at an inlet flow rate of 15 mL/min. Breakthrough curves were used to study the yeast biosorption behavior in the process. The saturation time (ts) was 21 and 45 h for Cr(III) and Cr(VI), respectively, and a breakthrough time (tb) of 4 h for Cr(III) and 5 h for Cr(VI). The uptake capacity of the biosorbent for Cr(III) and Cr(VI) were 48 and 60 mg/g, respectively. Two non-diffusional mathematical models with parameters t0 and sigma were used to adjust the experimental data obtained. Microsoft Excel tools were used for the mathematical solution of the two parameters used.

  16. The lattice distortion effect for zinc-blende CrAs and CrSb

    International Nuclear Information System (INIS)

    Yamana, Keita; Geshi, Masaaki; Tsukamoto, Hidekazu; Uchida, Ichiro; Shirai, Masafumi; Kusakabe, Koichi; Suzuki, Naoshi

    2004-01-01

    We investigated the stability of the ferromagnetism of CrAs and CrSb in the zinc-blende structure against the lattice distortion, systematically. A calculation within the generalized gradient approximation using a full potential linearized augmented plane wave method was performed. We compared the ferromagnetic state and the antiferromagnetic state assuming tetragonal distortion with the lattice constants a and c changing independently and determined the spin polarization ratio in the ferromagnetic phase. The result shows that complete spin polarization (half-metallic ferromagnetism) remains stable even in the presence of large tetragonal distortion. On the other hand, our calculation shows that two monolayers of CrAs is enough to produce a half-metallic state in the CrAs/GaAs multilayer. Thus, the present result suggests that the half-metallic nature persists in various atomic-scale superlattices made of distorted CrAs or CrSb

  17. Internal carbonitriding behavior of Ni-V, Ni-Cr, and Ni-3Nb alloys

    International Nuclear Information System (INIS)

    Allen, A.T.; Douglass, D.L.

    1999-01-01

    Ni-2V, Ni-5V, Ni-12V, Ni-10Cr, Ni-20Cr, and Ni-3Nb alloys were carbonitrided in C 3 H 6 and NH 3 gas mixtures (bal H 2 ) over the range 700--1,000 C. Carbonitridation of Ni-12V and Ni-20Cr in C 3 H 6 /NH 3 /H 2 (1.5/1.5/97 v/o) and (1.5/10/88.5 v/o) produced duplex subscales consisting of near-surface nitrides with underlying carbides. Growth of each zone obeyed the parabolic rate law under most conditions. The presence of carbon generally did not effect the depth of the nitride zones compared to nitriding the alloys in NH 3 /H 2 (10/90 v/o). However, at 700 C, the nitride zones were deeper in the carbonitrided Ni-V alloys and Ni-20Cr. The presence of nitrogen generally increased the depth of the carbide zones in Ni-12V and Ni-20Cr compared to carburizing these alloys in C 3 H 6 /H 2 (1.5/98.5 v/o). VN, CrN, and NbN formed in Ni-V, Ni-Cr, and Ni-Nb alloys, respectively, whereas the underlying carbide layers contained V 4 C 3 in Ni-12V, Cr 3 C 2 above a zone of Cr 7 C 3 in Ni-20Cr, and NbC in Ni-3Nb. The solubilities and diffusivities of nitrogen and carbon in nickel were determined. Nitrogen and carbon each exhibited retrograde solubility with temperature in pure Ni in both carbonitriding environments. Nitrogen diffusion in nickel was generally lower in each carbonitriding mixture compared to nitrogen diffusion in a nitriding environment, except at 700 C when nitrogen diffusion was higher. Carbon diffusion in nickel was generally higher in the carbonitriding environments compared to carbon diffusion in a carburizing environment

  18. Developing Accounting Information System Course Content for Iraqi Higher Education Institution: An Instrument Design

    Directory of Open Access Journals (Sweden)

    Naseem Yousif Hanna Lallo

    2013-07-01

    Full Text Available In ensuring that competent graduates are produced in the universities, the course used embedding knowledge in the students, mindsets needs to be effective. However, the unusual circumstances that happened in Iraq were affected on a universities course. The revolution in information technology (IT affects most of our activations. As a result, it is important to consider the impact of IT on accounting careers. Developing accenting information system course content can generate an accountant who is armed with the knowledge and skills before entering accounting job. Also the development process required instructors have characteristics that make the integrating process of IT knowledge components in AIS course content more smoothly. Iraq is the country facing many difficulties that makes its higher education institutions (HEIs suffered from un updated learning environment and technological backwardness. This causes a low level of accounting graduates’ knowledge and in turn leads to led to consider the Iraqi accountant incapable of working with international organizations and companies or conducting was it professionally. The aim of this paper is to explain the role of IT knowledge elements in developing AIS course content in Iraqi HEIs with considering the moderate effect of the instructors’ characteristics. Furthermore, this paper discusses the development and validation of the quantitative instrument (questionnaire for IT knowledge elements in Iraqi HEIs. Moreover, the reliability of the constructs is also discussed.

  19. Crystal structure and magnetic properties of Cr doped barium hexaferrite

    Science.gov (United States)

    Kumar, Sunil; Supriya, Sweety; Pandey, Rabichandra; Pradhan, Lagen Kumar; Kar, Manoranjan

    2018-04-01

    The Cr3+ substituted BaFe12O19 has been synthesized by modified sol-gel method to tailor the magnetic anisotropy and coercivity for technological applications. Some basic studies have revealed that this substitution leads to unusual interactions among the magnetic sublattices of the M-type hexaferrite. In order to investigate these interactions, BaFe12-xCrxO19 (x = 0.0, 0.5, 1.0, 2.0, and 4.0) M-type hexaferrites were characterized by employing XRD (X-ray Diffractometer). It is confirmed that, all the samples are in nanocrystalline and single phase, no impurity has been detected within the XRD limit. The magnetic hysteresis (m-H) loops revealed the ferromagnetic nature of nanoparticles (NPs). The coercive field were increasing with the increasing Cr3+ content, but after the percolation limit it decreases. The magnetocrystalline anisotropy is increasing with the Cr3+ concentration in samples and high values of magnetocrystalline anisotropy revealed that all samples are hard magnetic materials. Magnetic hysteresis loops were analyzed using the Law of Approach to Saturation method.

  20. Comparison of AlCrN and AlCrTiSiN coatings deposited on the surface of plasma nitrocarburized high carbon steels

    International Nuclear Information System (INIS)

    Chen, Wanglin; Zheng, Jie; Lin, Yue; Kwon, Sikchol; Zhang, Shihong

    2015-01-01

    Highlights: • The duplex coatings were produced by combination of nitrocarburizing and multi-arc ion plating. • The γ′-phase plays the nucleation sites for the coating nitrides. • The compound layers (CL) considerably enhance mechanical and tribological properties of the duplex PVD coatings. • The main wear mechanisms of the PVD coatings with and without CL are oxidation wear, the combination of spalling, chipping and oxidation wear, respectively. - Abstract: The AlCrN and AlCrTiSiN coatings were produced on the surface of plasma nitrocarburized T10 steels by multi-arc ion plating. The comparison of the microstructures and mechanical properties of the duplex coatings were investigated by means of X-ray diffraction, optical microscope, scanning electron microscope and transmission electron microscope, in association with mechanical property measurement. The results show that the AlCrN coatings with columnar grown are mainly composed of nanocrytalline fcc-(Cr,Al)N phases with {111} preferred orientation, whereas the superlattice and nanocomposite AlCrTiSiN coatings with planar growth mainly consist of nanocrystalline fcc-(Cr,Al)N phases with {100} perfected orientation, hcp-AlN and Si 3 N 4 amorphous phases. The AlCrTiSiN duplex coating with the compound layer reveals higher hardness, adhesion strength, load capacity and lower friction coefficient when compared with the other duplex coatings, which is due to its superlattice and nanocomposite structure. Additionally, these improved properties are related to the appearance of the γ′-phase which plays the nucleation sites for the coating nitrides and provides a strong supporting effect for the AlCrN and AlCrTiSiN coatings. The main wear mechanism of the duplex coatings without compound layer is spalling and chipping wear as well as tribooxidation wear, whereas the main wear mechanism of the duplex coatings with compound layer is tribooxidation wear

  1. An approach to breeding for higher protein content in bread wheat

    International Nuclear Information System (INIS)

    Jain, H.K.; Singhal, N.C.; Singh, M.P.; Austin, A.

    1975-01-01

    This study deals with the development of a suitable experimental approach for improving the protein content of seeds in bread wheat. It has been found that scoring of protein content on a per seed basis rather than as a percentage of seed weight gives better results. In the first place, the heritability of protein content increases nearly three times when scoring is done on the basis of seed number. Also, protein content scored in this way showed a significant positive correlation with seed size. Correlation between seed size and percentage of protein in the seed is negative. An important implication of these findings is that scoring of protein content on the basis of seed number should help to avoid selection of genotypes showing reduced starch synthesis and, therefore, a lower yield of grains as well as protein on a per acre basis. Also, the observations suggest that selection for larger seed size may be an important means of improving the protein content of wheat. These and other implications are discussed. (author)

  2. Consequence of doping mediated strain and the activation energy on the structural and optical properties of ZnO:Cr nanoparticles

    International Nuclear Information System (INIS)

    Bhargava, Richa; Sharma, Prashant K.; Kumar, Sanjeev; Pandey, Avinash C.; Kumar, Naresh

    2010-01-01

    We report on the sol-gel synthesis of Zn 1-x Cr x O (x=0.0, 0.05, 0.10, 0.15 and 0.20) nanoparticles. These nanoparticles were characterized by using thermogravimetry/differential scanning calorimetry (TG/DSC), X-ray diffraction (XRD), transmission electron microscopy (TEM), Raman and Photoluminescence (PL). Electronegativity of Cr ions (Cr 3+ ) reduces the final decomposition temperature by 40 o C and activation energy of the reaction when Cr is doped into ZnO. Doping of higher Cr concentration (x≥0.10) into ZnO shows formation of secondary spinel (ZnCr 2 O 4 ) phase along with the hexagonal (ZnO) and is revealed by XRD. Formation of secondary phase changes the activation energy of the reaction and thus the strain in ZnO lattice. In Raman spectra, additional Raman modes have been observed for Zn 1-x Cr x O nanoparticles, which can be assigned to the modes generated due to Cr doping. The Cr doping into ZnO is also supported by PL, in which vacancies are formed with Cr ion incorporation and emission band shifts towards higher wavelength. - Graphical abstract: Cr-doped ZnO nanostructures were synthesized by sol-gel. XRD (a) revealed secondary phase of ZnCr 2 O 4 with increase in Cr concentration. The Cr concentration also changes activation energy of the reaction (b).

  3. A mechanical and tribological study of Cr/CrN multilayer coatings

    Energy Technology Data Exchange (ETDEWEB)

    Arias, D.F., E-mail: diegomas@gmail.com [Grupo GEMA, Universidad Católica de Pereira, Pereira (Colombia); Gómez, A. [Laboratório de Fenômenos de Superficie, Escola Politécnica, Universidade de Sao Paulo, Sao Paulo (Brazil); Pontificia Universidad Javeriana Cali (Colombia); Vélez, J.M. [Escuela de Ingeniería de Materiales, Universidad Nacional de Colombia Sede Medellín (Colombia); Souza, R.M. [Laboratório de Fenômenos de Superficie, Escola Politécnica, Universidade de Sao Paulo, Sao Paulo (Brazil); Olaya, J.J. [Departamento de Ingeniería Mecánica y Mecatrónica, Universidad Nacional de Colombia, Bogotá (Colombia)

    2015-06-15

    Multilayer Cr/CrN coatings with different periodicities were grown on silicon substrates by means of a magnetron sputtering technique. Thin films with only Cr or CrN were also grown, in order to use them as reference samples. Structural, morphological, mechanical and tribological characterization were carried out by using X-ray diffraction (XRD), atomic force microscopy (AFM), nanohardness and nanoscratch techniques, respectively. The characterization results were analyzed as a function of the bilayer thickness (period). In general, the multilayer hardness value increased with the decrease in period. In addition, the validity of the Hall-Petch relationship was confirmed for grain sizes and period values greater than 146 nm and 333 nm, respectively. The coefficient of friction (COF) increased with increasing load, which indicates the contribution of the adhesion to the COF. - Highlights: • Multilayer Cr/CrN coatings with layer thickness between 200 and 1000 nm were grown. • Neither bias voltage not temperature were applied during deposition. • The hardness improves with the increase of the number of bilayers. • The wear rate decreases with the increase of the number of bilayers.

  4. Production of bio-sugar and bioethanol from coffee residue (CR) by acid-chlorite pretreatment.

    Science.gov (United States)

    Kim, Ho Myeong; Choi, Yong-Soo; Lee, Dae-Seok; Kim, Yong-Hwan; Bae, Hyeun-Jong

    2017-07-01

    Nowadays, coffee residue (CR) after roasting is recognized as one of the most useful resources in the world for producing the biofuel and bio-materials. In this study, we evaluated the potential of bio-sugar and bioethanol production from acid-chlorite treated CR. Notably, CR treated three times with acid-chlorite after organic solvent extraction (OSE-3), showed the high monosaccharide content, and the efficient sugar conversion yield compared to the other pretreatment conditions. The OSE-3 (6% substrate loading, w/v) can produce bio-sugar (0.568g/g OSE-3). Also, simultaneous saccharification and fermentation (SSF) produced ethanol (0.266g/g OSE-3), and showed an ethanol conversion yield of 73.8% after a 72-h reaction period. These results suggest that acid-chlorite pretreatment can improve the bio-sugar and bioethanol production of CR by removing the phenolic and brown compounds. Copyright © 2017 Elsevier Ltd. All rights reserved.

  5. Microstructural Characterization of Y{sub 2}O{sub 3} ODS-Fe-Cr Model Alloy s

    Energy Technology Data Exchange (ETDEWEB)

    De Castro, V.; Jenkins, M.L. [Oxford Univ., Dept. of Materials (United Kingdom); Leguey, T.; Mufioz, A.; Pareja, R.; Monge, M.A. [Madrid Univ. Carlos 3, Dept. de Fisica (Spain)

    2007-07-01

    Full text of publication follows: Reduced activation ferritic/martensitic (RAFM) steels with Cr contents ranging between 9-12 wt% are promising candidates for use as structural materials in future fusion reactors. They are likely to be superior to austenitic steels because of their better thermal properties and higher swelling resistance. A major concern of these materials is their maximum service temperature, as this determines the overall efficiency of the reactor. It has been demonstrated that one way to increase this temperature is to homogeneously disperse hard nano-sized oxide particles, such as Y{sub 2}O{sub 3}, into the steel matrix. Oxide dispersion strengthened (ODS) steels produced by mechanical milling and hot isostatic pressing (HIP ) are considered as potential structural materials for fusion reactors. In Europe, efforts have been focused on the ODS-RAFM-9CrW steel EUROFER. These ODS steels show good tensile and creep properties, acceptable ductility, but poor impact properties. Microstructural characterization of real steels, especially of the structures of oxide/steel matrix interfaces which play an important role in the performance of the material, is a difficult task. In the present work we have fabricated and characterised a simpler model ODS system based on a Fe-Cr binary alloy, in the belief that this will help us better to understand complex ODS-RAFM steels. Two Fe-12wt% Cr batches, one containing 0.3 wt% Y{sub 2}O{sub 3} and the other Y{sub 2}O{sub 3} free have been produced by milling plus compaction by HIP. These materials are being characterized by X-ray diffraction, electron microscopy and atom probe field ion microscopy. Results will be compared with those obtained for ODS-EUROFER produced under the same conditions. (authors)

  6. Properties of rapidly solidified Fe-Cr-Al ribbons for the use as automotive exhaust gas catalyst substrates

    International Nuclear Information System (INIS)

    Emmerich, K.

    1993-01-01

    Metallic honeycomb structures are used as catalyst substrates in automotive exhaust gas systems. This application requires an outstanding corrosion resistance at elevated temperatures of the substrate material. Technical improvements can be achieved by the use of rapid solidification technology for the production of the Fe-Cr-Al ribbons since the Al content can be substantially increased from about 5% Al in the conventionally rolled material to about 12% Al in the rapid solidified ribbon. As a result the lifetime of the ribbon in a higher-temperature corrosion environment is drastically increased. In addition the scale/metal adherance is improved. The impediment of recrystallization in the rapidly solidified ribbons prevents an embrittlement even in carbonizing atmospheres. (orig.)

  7. Effect of inclusion content on the creep rupture properties of type 17Cr-8Ni-2Mo weld metals

    International Nuclear Information System (INIS)

    Senior, B.A.

    1988-01-01

    It has been known for some time that austenitic weldments exhibit low and variable creep rupture properties, but many of the factors controlling these properties are not well understood. In this investigation, two welds (Type 316) with similar compositions and fabricated using the same welding parameters, but with different electrode coatings, have been examined after creep testing. The results indicate that the inclusion and silicon content of type 316 welds can strongly influence their creep rupture properties, a high inclusion density being associated with poor creep rupture properties, and a low silicon content with a higher creep rate. This has been explained with reference to the micromechanism of creep failure operating in these welds. (author)

  8. Species dependent radiotracer study of Cr(VI) and Cr(III) using an aqueous biphasic system

    Energy Technology Data Exchange (ETDEWEB)

    Roy, K.; Lahiri, S. [Chemical Sciences Div., Saha Inst. of Nuclear Physics, Kolkata (India)

    2008-07-01

    The speciation study of Cr(III) and Cr(VI) was carried out using a polyethylene glycol (PEG) based aqueous biphasic extraction system (ABS). Neutron activated Cr(III) and Cr(VI) salts were assayed in a HPGe detector before and after employing aqueous biphasic extraction. Different salts of various salting out abilities were taken as the salt rich phase. The best condition for extraction of Cr(VI) and the maximum differential attitude of ABS to Cr(VI) and Cr(III) was observed when 2 M Na{sub 2}SO{sub 4} and PEG 4000 (50% w/w) solutions were used. Cr(III) can also be extracted by the PEG with prior complexation with diphenylthiocarbazone (dithizone). The chromium dithizonate complex is quantitatively extracted by the PEG rich phase. (orig.)

  9. Migration of Cr-vacancy clusters and interstitial Cr in α-Fe using the dimer method

    International Nuclear Information System (INIS)

    Chen, D.; Gao, F.; Hu, S. Y.; Sun, X.; Heinisch, H. L.; Henager, C. H.; Khaleel, M. A.; Hu, W. Y.; Terentyev, D.

    2010-01-01

    The migration mechanisms and the corresponding activation energies of Cr-vacancy (Cr-V) clusters and Cr interstitials in α-Fe have been investigated using the dimer and the nudged elastic-band methods. Dimer searches are employed to find the possible transition states of these defects and the lowest-energy paths are used to determine the energy barriers for migration. A substitutional Cr atom can migrate to a nearest-neighbor vacancy through an energy barrier of 0.56 eV but this simple mechanism alone is unlikely to lead to the long-distance migration of Cr unless there is a supersaturated concentration of vacancies in the system. The Cr-vacancy clusters can lead to long-distance migration of a Cr atom that is accomplished by Fe and Cr atoms successively jumping to nearest-neighbor vacancy positions, defined as a self-vacancy-assisted migration mechanism, with the migration energies ranging from 0.64 to 0.89 eV. In addition, a mixed Cr-Fe dumbbell interstitial can easily migrate through Fe lattices, with the migration energy barrier of 0.17, which is lower than that of the Fe-Fe interstitial. The on-site rotation of the Cr-Fe interstitial and Cr atom hopping from one site to another are believed to comprise the dominant migration mechanism. The calculated binding energies of Cr-V clusters are strongly dependent on the size of clusters and the concentration of Cr atoms in clusters.

  10. P-type Al-doped Cr-deficient CrN thin films for thermoelectrics

    Science.gov (United States)

    le Febvrier, Arnaud; Van Nong, Ngo; Abadias, Gregory; Eklund, Per

    2018-05-01

    Thermoelectric properties of chromium nitride (CrN)-based films grown on c-plane sapphire by dc reactive magnetron sputtering were investigated. In this work, aluminum doping was introduced in CrN (degenerate n-type semiconductor) by co-deposition. Under the present deposition conditions, over-stoichiometry in nitrogen (CrN1+δ) rock-salt structure is obtained. A p-type conduction is observed with nitrogen-rich CrN combined with aluminum doping. The Cr0.96Al0.04N1.17 film exhibited a high Seebeck coefficient and a sufficient power factor at 300 °C. These results are a starting point for designing p-type/n-type thermoelectric materials based on chromium nitride films, which are cheap and routinely grown on the industrial scale.

  11. FT-Raman spectroscopic analysis of Nd:YAG and Er,Cr:YSGG laser irradiated enamel for preventive purposes

    International Nuclear Information System (INIS)

    Ana, P A; Kauffmann, C M F; Gomes, A S L; Bachmann, L; Soares, L E S; Martin, A A; Zezell, D M

    2014-01-01

    This study evaluated the effect of combining laser irradiation with fluoride on an enamel microstructure and demineralization by FT-Raman spectroscopy (FTRS). Eighty human enamel slabs were divided into eight groups: (G1) untreated; (G2) acidulated phosphate fluoride application (APF—1.23% F − for 4 min); (G3) Nd:YAG irradiation (84.9 J cm −2 , 60 mJ/pulse); (G4) Nd:YAG + APF; (G5) APF + Nd:YAG; (G6) Er,Cr:YSGG irradiation (2.8 J cm −2 , 12.5 mJ/pulse); (G7) Er,Cr:YSGG + APF; and (G8) APF + Er,Cr:YSGG. After treatment, the samples were submitted to a ten-day pH-cycling model. Chemical changes were determined on the slabs before and after treatment, and also after pH-cycling, by FTRS in the range 400−4000 cm −1 . The inorganic bands at 440, 590, 870, 960, 1100 cm −1 , and the organic bands at 1270, 1450, 1670, 2945 cm −1 were considered. Demineralization promoted reduction in organic contents; Nd:YAG laser irradiation promoted loss of carbonate and organic content, while Er,Cr:YSGG did not produce significant changes in the relative band intensities of organic and inorganic contents of the enamel. In lased samples, no effects caused by pH-cycling on enamel were observed. In conclusion, laser treatment and its association with fluoride can somehow interfere with the demineralization dynamics, reducing its effects over the enamel. (paper)

  12. Enhanced Cr(VI) removal from groundwater by Fe0-H2O system with bio-amended iron corrosion

    DEFF Research Database (Denmark)

    Yin, Weizhao; Li, Yongtao; Wu, Jinhua

    2017-01-01

    Abstract A one-pot bio-iron system was established to investigate synergetic abiotic and biotic effects between iron and microorganisms on Cr(VI) removal. More diverse iron corrosion and reactive solids, such as green rusts, lepidocrocite and magnetite were found in the bio-iron system than...... transfer on the solid phase. The results also showed that the reduction of Cr(VI) by microorganisms was insignificant, indicating the adsorption/co-precipitation of Cr by iron oxides on iron surface was responsible for the overall Cr(VI) removal. Our study demonstrated that the bio-amended iron corrosion...... in the Fe0-H2O system, leading to 4.3 times higher Cr(VI) removal efficiency in the bio-iron system than in the Fe0-H2O system. The cycling experiment also showed that the Cr(VI) removal capacity of Fe0 in the bio-iron system was 12.4 times higher than that in the Fe0-H2O system. A 62 days of life...

  13. Microstructural Evolution of NiCoCrAlHfYSi and NiCoCrAlTaY Coatings Deposited by AC-HVAF and APS

    Science.gov (United States)

    Han, Yujun; Chen, Hongfei; Gao, Dong; Yang, Guang; Liu, Bin; Chu, Yajie; Fan, Jinkai; Gao, Yanfeng

    2017-12-01

    The chemical composition of NiCoCrAlHfYSi with a suitable particle size, deposited using an activated combustion-high velocity air fuel (AC-HVAF) spray, is a potentially promising process because dense, continuous and pure alumina can be formed on the surface of the MCrAlY metallic coatings after isothermal oxidation exposure. The NiCoCrAlHfYSi (Amdry386) and NiCoCrAlTaY (Amdry997) coatings were produced using AC-HVAF and APS, respectively. Isothermal oxidation was subsequently conducted at 1050 °C in air for 200 h. This paper compares the characteristics of four coated samples, including the surface roughness, elastic modulus, hardness, oxide content, microstructural characteristics and phase evolution of thermally grown oxides (TGO). The growth of both the TGO and alumina scales in the TGO of the HVAF386 coating was relatively rapid. The θ- to α-alumina phase transformation was strongly determined by the Hf and Si dopants in the HVAF386 coating. Finally, the extent of grain refinement and deformation storage energy in the HVAF997 coatings were determined to be significantly crucial for the θ- to α-alumina phase transformation.

  14. Optical and structural investigation on sodium borosilicate glasses doped with Cr2O3

    Science.gov (United States)

    Ebrahimi, E.; Rezvani, M.

    2018-02-01

    In this work, Sodium borosilicate glasses with chemical composition of 60% SiO2-20% B2O3-20%Na2O doped with different contents of Cr2O3 were prepared by melting-quenching method. Physical, structural and optical properties of glasses were investigated by studying density and molar volume, Fourier Transform Infrared (FT-IR) Spectra and UV-visible absorption spectroscopy. The results showed an increase in density of glasses with the increase of Cr2O3 that can be due to addition of oxide with high molar mass. The optical absorption spectra of un-doped glass reveals UV absorption due to trace iron impurities with no visible band however Cr2O3 doped glasses shows absorption in visible range that are characteristic. Increasing of Cr3 + ions in the glassy microstructure of samples provides a semiconducting character to Sodium borosilicate glass by reducing the direct and indirect optical band gaps of glass samples from 3.79 to 2.59 (ev) and 3.36 to 2.09 (ev), respectively. These changes could be attributed to the role of Cr3 + ions as the network former which asserts improvement of semiconducting behavior in presence of Cr2O3.

  15. Influence of trimethylsilane flow on the microstructure, mechanical and tribological properties of CrSiCN coatings in water lubrication

    Science.gov (United States)

    Wu, Zhiwei; Zhou, Fei; Wang, Qianzhi; Zhou, Zhifeng; Yan, Jiwang; Li, Lawrence Kwok-Yan

    2015-11-01

    CrSiCN coatings with different silicon and carbon contents were deposited on silicon wafers and 316L stainless steels using unbalanced magnetron sputtering via adjusting trimethylsilane (TMS) flow, and their microstructure and mechanical properties were characterized by X-ray diffraction (XRD), scanning electron microscopy(SEM), X-ray photoelectrons spectroscopy(XPS) and nano-indenter, respectively. The tribological properties of CrSiCN coatings sliding against SiC balls in water were investigated using ball-on-disk tribometer. The results showed that the CrSiCN coatings had fine composite microstructure consisting of nanocrystallites of Cr(C, N) crystal and amorphous phases such as a-Si3N4 and a-C(a-CNx). The typical columnar structures changed from fine cluster to coarse ones when the Si content was beyond 3.4 at.%. With an increase in the TMS flow, the hardness and Young's modulus of Corsican coatings all first increased, and then rapidly decreased, but the compressive stress in the coatings varied in the range of 2.8-4.8 GPa. When the TMS flow was 10 sccm, the CrSiCN coatings exhibited the highest hardness of 21.3 GPa and the lowest friction coefficient (0.11) and wear rate (8.4 × 10-8 mm3/N m). But when the TMS flow was beyond 15 sccm, the tribological properties of CrSiCN coatings in water became poor.

  16. Oxidation behavior of Al/Cr coating on Ti2AlNb alloy at 900 °C

    Science.gov (United States)

    Yang, Zhengang; Liang, Wenping; Miao, Qiang; Chen, Bowen; Ding, Zheng; Roy, Nipon

    2018-04-01

    In this paper, the Al/Cr coating was fabricated on the surface of Ti2AlNb alloy via rf magnetron sputtering and double glow treatment to enhance oxidation resistance. The protective coating with an outer layer of Al and inner layer of Cr has great bonding strength due to the in-diffusion of Cr and the inter-diffusion between Al and Cr to form Al-Cr alloyed layer which has great hardness. Acoustic emission curve which was detected via WS-2005 scratch tester indicates the bonding strength between Al/Cr coating and substrate is great. Morphology of Ti2AlNb alloy with Al/Cr coating after scratch test shows that the scratch is smooth without disbanding, and the depth and breadth of scratch are changed uniformly. The mass change was reduced after oxidation test due to the Al/Cr protective coating. Isothermal oxidation test at 900 °C was researched. Results indicate that Al/Cr coating provided oxidation resistance of Ti2AlNb alloy with prolonged air exposure at 900 °C. Al2O3 was detected by XRD patterns and SEM images, and was formed on the surface of Ti2AlNb alloy to protect substrate during oxidation test. A certain content of Cr is beneficial for the formation of Al2O3. Besides, Cr2O3 was produced under Al2O3 by outward diffusion of Cr to protect substrate sequentially, no cracks were discovered on Al/Cr protective coating. The process of Ti outward diffusion into surface was suppressive due to integration of Cr-Ti and Al-Ti intermetallics. A steady, adherent and continuous coated layer of Al/Cr on Ti2AlNb alloy increases oxidation resistance.

  17. Validity and reliability of the session-RPE method for quantifying training in Australian football: a comparison of the CR10 and CR100 scales.

    Science.gov (United States)

    Scott, Tannath J; Black, Cameron R; Quinn, John; Coutts, Aaron J

    2013-01-01

    The purpose of this study was to examine and compare the criterion validity and test-retest reliability of the CR10 and CR100 rating of perceived exertion (RPE) scales for team sport athletes that undertake high-intensity, intermittent exercise. Twenty-one male Australian football (AF) players (age: 19.0 ± 1.8 years, body mass: 83.92 ± 7.88 kg) participated the first part (part A) of this study, which examined the construct validity of the session-RPE (sRPE) method for quantifying training load in AF. Ten male athletes (age: 16.1 ± 0.5 years) participated in the second part of the study (part B), which compared the test-retest reliability of the CR10 and CR100 RPE scales. In part A, the validity of the sRPE method was assessed by examining the relationships between sRPE, and objective measures of internal (i.e., heart rate) and external training load (i.e., distance traveled), collected from AF training sessions. Part B of the study assessed the reliability of sRPE through examining the test-retest reliability of sRPE during 3 different intensities of controlled intermittent running (10, 11.5, and 13 km·h(-1)). Results from part A demonstrated strong correlations for CR10- and CR100-derived sRPE with measures of internal training load (Banisters TRIMP and Edwards TRIMP) (CR10: r = 0.83 and 0.83, and CR100: r = 0.80 and 0.81, p training load (distance, higher speed running and player load) for both the CR10 (r = 0.81, 0.71, and 0.83) and CR100 (r = 0.78, 0.69, and 0.80) were significant (p reliability for both the CR10 (31.9% CV) and CR100 (38.6% CV) RPE scales after short bouts of intermittent running. Collectively, these results suggest both CR10- and CR100-derived sRPE methods have good construct validity for assessing training load in AF. The poor levels of reliability revealed under field testing indicate that the sRPE method may not be sensible to detecting small changes in exercise intensity during brief intermittent running bouts. Despite this limitation

  18. Ni-Cr thin film resistor fabrication for GaAs monolithic microwave integrated circuits

    International Nuclear Information System (INIS)

    Vinayak, Seema; Vyas, H.P.; Muraleedharan, K.; Vankar, V.D.

    2006-01-01

    Different Ni-Cr alloys were sputter-deposited on silicon nitride-coated GaAs substrates and covered with a spin-coated polyimide layer to develop thin film metal resistors for GaAs monolithic microwave integrated circuits (MMICs). The contact to the resistors was made through vias in the polyimide layer by sputter-deposited Ti/Au interconnect metal. The variation of contact resistance, sheet resistance (R S ) and temperature coefficient of resistance (TCR) of the Ni-Cr resistors with fabrication process parameters such as polyimide curing thermal cycles and surface treatment given to the wafer prior to interconnect metal deposition has been studied. The Ni-Cr thin film resistors exhibited lower R S and higher TCR compared to the as-deposited Ni-Cr film that was not subjected to thermal cycles involved in the MMIC fabrication process. The change in resistivity and TCR values of Ni-Cr films during the MMIC fabrication process was found to be dependent on the Ni-Cr alloy composition

  19. Submerged Cultivation of Mycelium with High Ergothioneine Content from the Culinary-Medicinal Golden Oyster Mushroom, Pleurotus citrinopileatus (Higher Basidiomycetes).

    Science.gov (United States)

    Lin, Shin-Yi; Chien, Shih-Chang; Wang, Sheng-Yang; Mau, Jeng-Leun

    2015-01-01

    The optimization of submerged culture of the culinary-medicinal golden oyster mushroom, Pleurotus citrinopileatus, was studied using a one-factor-at-a-time, two-stage stimulation and central composite rotatable design to produce mycelia with high ergothioneine content. The optimal culture conditions for mycelia harvested at day 22 were a temperature of 25°C, an inoculation ratio of 5%, 2% glucose, 0.5% yeast extract, and adjustment of the initial pH value to 10. The biomass and ergothioneine content were 8.28 g/L and 10.65 mg/g dry weight (dw), respectively. The addition of an amino acid precursor increased the ergothioneine content of mycelia; cysteine was the most effective. In addition, the results obtained from central composite rotatable design showed that the recommended combination for cysteine, histidine, and methionine was 8, 4, and 0.5 mmol/L, respectively. The predicted ergothioneine content was 13.90 mg/g dw, whereas the experimental maximal ergothioneine content was 14.57 mg/g dw. With the addition of complex precursors and under optimal culture conditions, mycelia harvested at days 16-20 had higher ergothioneine content. Accordingly, the information obtained could be used to produce mycelia with high ergothioneine content.

  20. Role of butter layer in low-cycle fatigue behavior of modified 9Cr and CrMoV dissimilar rotor welded joint

    International Nuclear Information System (INIS)

    Wu, Qingjun; Lu, Fenggui; Cui, Haichao; Liu, Xia; Wang, Peng; Tang, Xinhua

    2014-01-01

    Highlights: • Modified 9Cr–CrMoV dissimilar turbine rotor was successfully welded by NG-SAW. • LCF properties of both welded joints were approximate at smaller strain amplitude. • Tempered martensite with amounts of carbides in HAZ contributed to weakest zones. • Matched BL determined LCF properties of whole joint for dissimilar welded rotor. - Abstract: The present work aims at studying the role of butter layer (BL) in low-cycle fatigue (LCF) behavior of modified 9Cr steel and CrMoV steel dissimilar welded joint. The significant difference of the chemical composition of base metals (BMs) makes it a challenge to achieve sound welded joint. Therefore, buttering was considered to obtain a transition layer between the dissimilar steels. The LCF tests of two kinds of specimens without and with butter layer were performed applying strain-controlled cyclic load with different axial strain amplitudes. The test results indicated that the number of cycles at higher strain amplitudes of welded joint without butter layer was greatly higher than that of the joint with butter layer, while the fatigue lifetime to crack initiation (2N f ) became closer to each other at low and middle strain amplitudes. The failure was in the tempered heat affected zone (HAZ) at the CrMoV side for specimens without BL, while the fracture occurred at the tempered HAZ in the BL for specimens with BL. The microstructure details of BM, BL, HAZ and weld metals (WMs) were revealed by optical microscopy (OM). It was found that the tempered martensite was major microstructure for welded joint and much more carbides were observed in tempered HAZ than other parts due to the repeated tempering. Microhardness test indicated a softest zone existing tempered HAZ of BL and also there was a softer zone in tempered HAZ at the CrMoV side due to repeated tempering during welding and post weld heat treatment (PWHT). And scanning electron microscopy (SEM) was applied to observe the fractography. It was

  1. Fabrication of Fe-Cr-Mo powder metallurgy steel via a mechanical-alloying process

    Science.gov (United States)

    Park, Jooyoung; Jeong, Gowoon; Kang, Singon; Lee, Seok-Jae; Choi, Hyunjoo

    2015-11-01

    In this study, we employed a mechanical-alloying process to manufacture low-alloy CrL and CrM steel powders that have similar specifications to their water-atomized counterparts. X-ray diffraction showed that Mo and Cr are alloyed in Fe after four cycles of planetary milling for 1 h at 150 RPM with 15-min pauses between the cycles (designated as P2C4 process). Furthermore, the measured powder size was found to be similar to that of the water-atomized counterparts according to both scanning electron microscope images and laser particle size analysis. The samples were sintered at 1120 °C, after which the P2C4-milled CrL showed similar hardness to that of water-atomized CrL, whereas the P2C4-milled CrM showed about 45% lower hardness than that of its water-atomized counterpart. Water-atomized CrM consists of a well-developed lathtype microstructure (bainite or martensite), while a higher fraction of polygonal ferrite is observed in P2C4-milled CrM. This phase difference causes the reduction of hardness in the P2C4-milled CrM, implying that the phase transformation behavior of specimens produced via powder metallurgy is influenced by the powder fabrication method.

  2. /sup 51/Cr-bleomycin, a new oncophilic radiopharmaceutical. Pt. 1

    Energy Technology Data Exchange (ETDEWEB)

    Rembelska, M J; Liniecki, J

    1982-04-01

    A method was developed for labelling bleomycin with /sup 51/Cr. The complex was administered to mice (Swiss and C57-B1/6) bearing 5 transplantable tumours: Ehrlich ascites tumour, NK/Ly lymphoma, Lewis lung carcinoma, melanoma B-16, and Sarcoma 180. Activity concentration in neoplasms, blood and numerous organs was determined 12, 24 and 48 hrs after injection. An identical procedure was applied using /sup 58/Co-bleomycin as a reference oncophilic substance. Tumour/non-tumor ratios exceeding substantially unity were found for blood, muscle and bone indicating preferential accumulation of both /sup 58/Co and /sup 51/Cr in all the neoplasms tested. The ratios were lower (by a factor 2-3) for /sup 51/Cr than for /sup 58/Co; however, it is postulated that the gamma-quantum energy of /sup 51/Cr which is higher than that of the commonly used /sup 57/Co, should offset to some degree this difference when scintigraphic tumour detection in a patient is to be attempted. In conclusion, clinical trials with /sup 51/Cr-bleomycin, which is cheaper than its /sup 57/Co-counterpart, appear warranted.

  3. [Differential study of the bonding characterization of dental porcelain to Ni-Cr alloys].

    Science.gov (United States)

    Wei, Fang; Zhan, De-song; Wang, Yan-yan

    2008-10-01

    To study the bonding capability when Ni-Cr porcelain alloy was added with Ti, compound rare earth metals and removed the element of Be. Ni-Cr-Ti porcelain alloys manufactured by Institute of Metal Research of Chinese Academy of Sciences were tested. The test alloys were divided into three groups according to whether containing Be and compound rare earth metals or not. And HI BOND Ni-Cr base-metal alloy was chosen as control. The metal-ceramic specimens were prepared for shear test, scanning electron microscope (SEM) and energy spectrum analysis. The shear bond strength of the four groups were analyzed. No significant difference were observed among them (P > 0.05). No crackle was found and they were contacted tightly between the porcelain and metal. The composition and contents of the four groups' interfaces were closed. The shear bond strength of the self-made Ni-Cr-Ti porcelain alloys all can satisfy the clinical requirements. Experimental groups containing Ti, compound rare earth metals and removing the element of Be can be used as better recommendation for clinical practice.

  4. Evaluation of consequence due to higher hydrazine content in partitioning stream of PUREX process

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, K. Suresh [Bhabha Atomic Research Centre, Mumbai (India). Special Nuclear Recycle Facility

    2016-07-01

    Hydrazine nitrate is being used as a stabilizer for U(IV) as well as Pu(III) during partitioning of Pu in PUREX process by scavenging the nitrous acid present along with nitric acid. As hydrazine hydrate as well as its salts have been successfully used for scrubbing of degradation products of TBP to aqueous phase, experiments were conducted to evaluate the consequence of hydrazine content during Pu partitioning. It was observed that higher amount of hydrazine nitrate along with uranous nitrate in the partitioning stream of PUREX process leads to build up of DBP in aqueous phase and resulted in precipitation of Pu.

  5. Study of phase transformations in Fe-Mn-Cr Alloys

    International Nuclear Information System (INIS)

    Schule, W.; Panzarasa, A.; Lang, E.

    1988-01-01

    Nickel free alloys for fusion reactor applications are examined. Phase changes in fifteen, mainly austenitic iron-manganese-chromium-alloys of different compositions were investigated in the temperature range between -196 0 C and 1000 0 C after different thermo-mechanical treatments. A range of different physical measuring techniques was employed to investigate the structural changes occurring during heating and cooling and after cold-work: electrical resistivity techniques, differential thermal analysis, magnetic response, Vickers hardness and XRD measurement. The phase boundary between the α Fe-phase and the γ-phase of the iron manganese alloy is approximately maintained if chromium is added to the two component materials. Consequently all the alloy materials for contents of manganese smaller than about 30% Mn are not stable below 500 0 C. This concerns also the AMCR alloys. However the α Fe-phase is not formed during slow cooling from 1000 0 C to ambient temperature and is only obtained if nucleation sites are provided and after very long anneals. A cubic α Mn-type-phase is found for alloys with 18% Cr and 15% Mn, with 13% Cr and 25% Mn, with 10% Cr and 30% Mn, and with 10% Cr and 40% Mn. For these reasons the γ-phase field of the iron-chromium-manganese alloys is very small below 600 0 C and much narrower than reported in the literature. 95 figs. 22 refs

  6. Enhanced Piezoelectric Response of AlN via CrN Alloying

    Energy Technology Data Exchange (ETDEWEB)

    Manna, Sukriti; Talley, Kevin R.; Gorai, Prashun; Mangum, John; Zakutayev, Andriy; Brennecka, Geoff L.; Stevanović, Vladan; Ciobanu, Cristian V.

    2018-03-01

    Since AlN has emerged as an important piezoelectric material for a wide variety of applications, efforts have been made to increase its piezoelectric response via alloying with transition metals that can substitute for Al in the wurtzite lattice. We report on density functional theory calculations of structure and properties of the CrxAl1-xN system for Cr concentrations ranging from zero to beyond the wurtzite-rocksalt transition point. By studying the different contributions to the longitudinal piezoelectric coefficient, we propose that the physical origin of the enhanced piezoelectricity in CrxAl1-xN alloys is the increase of the internal parameter u of the wurtzite structure upon substitution of Al with the larger Cr ions. Among a set of wurtzite-structured materials, we find that CrxAl1-xN has the most sensitive piezoelectric coefficient with respect to alloying concentration. Based on these results, we propose that CrxAl1-xN is a viable piezoelectric material whose properties can be tuned via Cr composition. We support this proposal by combinatorial synthesis experiments, which show that Cr can be incorporated in the AlN lattice up to 30% before a detectable transition to rocksalt occurs. At this Cr content, the piezoelectric modulus d33 is approximately 4 times larger than that of pure AlN. This finding, combined with the relative ease of synthesis under nonequilibrium conditions, may position CrxAl1-xN as a prime piezoelectric material for applications such as resonators and acoustic wave generators.

  7. Enhanced Piezoelectric Response of AlN via CrN Alloying

    Science.gov (United States)

    Manna, Sukriti; Talley, Kevin R.; Gorai, Prashun; Mangum, John; Zakutayev, Andriy; Brennecka, Geoff L.; Stevanović, Vladan; Ciobanu, Cristian V.

    2018-03-01

    Since AlN has emerged as an important piezoelectric material for a wide variety of applications, efforts have been made to increase its piezoelectric response via alloying with transition metals that can substitute for Al in the wurtzite lattice. We report on density functional theory calculations of structure and properties of the Crx Al1 -x N system for Cr concentrations ranging from zero to beyond the wurtzite-rocksalt transition point. By studying the different contributions to the longitudinal piezoelectric coefficient, we propose that the physical origin of the enhanced piezoelectricity in Crx Al1 -x N alloys is the increase of the internal parameter u of the wurtzite structure upon substitution of Al with the larger Cr ions. Among a set of wurtzite-structured materials, we find that Crx Al1 -x N has the most sensitive piezoelectric coefficient with respect to alloying concentration. Based on these results, we propose that Crx Al1 -x N is a viable piezoelectric material whose properties can be tuned via Cr composition. We support this proposal by combinatorial synthesis experiments, which show that Cr can be incorporated in the AlN lattice up to 30% before a detectable transition to rocksalt occurs. At this Cr content, the piezoelectric modulus d33 is approximately 4 times larger than that of pure AlN. This finding, combined with the relative ease of synthesis under nonequilibrium conditions, may position Crx Al1 -x N as a prime piezoelectric material for applications such as resonators and acoustic wave generators.

  8. CrAlN coatings deposited by cathodic arc evaporation at different substrate bias

    International Nuclear Information System (INIS)

    Romero, J.; Gomez, M.A.; Esteve, J.; Montala, F.; Carreras, L.; Grifol, M.; Lousa, A.

    2006-01-01

    CrAlN is a good candidate as an alternative to conventional CrN coatings especially for high temperature oxidation-resistance applications. Different CrAlN coatings were deposited on hardened steel substrates by cathodic arc evaporation (CAE) from chromium-aluminum targets in a reactive nitrogen atmosphere at negative substrate bias between - 50 and - 400 V. The negative substrate bias has important effects on the deposition growth rate and crystalline structure. All our coatings presented hardness higher than conventional CrN coatings. The friction coefficient against alumina and tungsten carbide balls was around 0.6. The sliding wear coefficient of the CrAlN coatings was very low while an important wear was observed in the balls before a measurable wear were produced in the coatings. This effect was more pronounced as the negative substrate bias was increased

  9. Role of defects on the electronic and magnetic properties of CrAs, CrSe and CrSb zinc-blende compounds

    International Nuclear Information System (INIS)

    Galanakis, I.; Pouliasis, S.G.

    2009-01-01

    We present an extended study of single impurity atoms and atomic swaps in half-metallic CrAs, CrSb and CrSe zinc-blende compounds. Although the perfect alloys present a rather large gap in the minority-spin band, all defects under study, with the exception of void impurities at Cr and sp sites and Cr impurities at sp sites (as long as no swap occurs), induce new states within the gap. The Fermi level can be pinned within these new minority states depending on the lattice constant used for the calculations and the electronegativity of the sp atoms. Although these impurity states are localized in space around the impurity atoms and very fast we regain the bulk behavior, their interaction can lead to wide bands within the gap and thus loss of the half-metallic character

  10. Improvement of stress-rupture property by Cr addition in Ni-based single crystal superalloys

    International Nuclear Information System (INIS)

    Chen, J.Y.; Feng, Q.; Cao, L.M.; Sun, Z.Q.

    2011-01-01

    Research highlights: → Cr improved the stress-rupture life of single crystal superalloys significantly. → Cr increased the Re partitioning ratio and resulted in more negative misfit. → Mechanism for improving the stress-rupture life by Cr addition is addressed here. - Abstract: The effects of Cr addition on the microstructure and stress-rupture property have been investigated in three experimental Ni-based single crystal superalloys containing various levels of Cr addition (0-5.7 wt.%). The Re partitioning ratio increased and the lattice misfit became more negative with increasing the Cr addition in both dendrite core and interdendritic region. The changes of elemental partitioning behaviors and the lattice misfit show good agreement with the change of γ' morphology. Cr addition increased the stress-rupture life at 1100 deg. C/140 MPa significantly due to higher γ' volume fraction, more negative lattice misfit and a well rafting structure as well as less width of γ channels. High Cr addition (5.7 wt.%) increased the degree of Re and Cr supersaturation in the γ phase and promoted the formation of topologically close-packed (TCP) phases significantly under thermal exposure and creep deformation at 1100 deg. C.

  11. Comparison of Mineral Element Content in a Functional Food Maca (Lepidium meyenii Walp. from Asia and South America

    Directory of Open Access Journals (Sweden)

    Ji Zhang

    2015-01-01

    Full Text Available Contents of eight mineral elements in maca (Lepidium meyenii Walp. from China and Peru were determined by inductively coupled plasma optical emission spectroscopy. Cu contents in maca samples from China (2.5–31 mg kg−1 dry weight, dw were higher than the samples from Peru (<2.1 mg kg−1 dw. Na in two samples from China was found to be significantly of high content (2400 and 2600 mg kg−1 dw. The contents (mg kg−1 dw of B, Co, Cr, Li, Ni, and Zn were, respectively, 8.1–21, <0.023, <1.1~3.5, 0.020–0.17, 0.085–4.5, and 10–39 for the samples from China, while being 6.6–12, <0.023, <1.1~2.3, 0.035–0.063, 0.68–1.7, and 27–39 for the samples from Peru.

  12. The Reduction of Cr(VI) to Cr(III) by Natural Fe-Bearing Minerals: A Synchrotron XAS Study

    Science.gov (United States)

    Xu, H.; Guo, X.; Ding, M.; Migdissov, A. A.; Boukhalfa, H.; Sun, C.; Roback, R. C.; Reimus, P. W.; Katzman, D.

    2017-12-01

    Cr(VI) in the form of CrO42- is a pollutant species in groundwater and soils that can pose health and environmental problems. Cr(VI) associated with use as a corrosion inhibitor at a power plant from 1956-1972 is present in a deep groundwater aquifer at Los Alamos National Laboratory. A potential remediation strategy for the Cr contamination is reduction of Cr(VI) to Cr(III) via the acceptance of electrons from naturally occurring or induced Fe(II) occurring in Fe-bearing minerals. In this work, using synchrotron-based X-ray techniques, we investigated the Cr reduction behavior by Fe-bearing minerals from outcrop and core samples representative of the contaminated portion of the aquifer. Samples were exposed to solutions with a range of known Cr (VI) concentrations. XANES and EXAFS spectra showed that all the Cr(VI) had been reduced to Cr(III), and micro XRF mapping revealed close correlation of Cr and Fe distribution, implying that Fe(II) in minerals reduced Cr(VI) in the solution. Similar behavior was observed from in-situ XANES measurements on Cr reduction and adsorption by mineral separates from the rock samples in Cr(VI)-bearing solutions. In addition, to obtain reference parameters for interpreting the data of natural samples, we collected Cr and Fe EXAFS spectra of Cr(III)-Fe(III) hydroxide solid solutions, which show progressive changes in the local structure around Cr and Fe over the whole series.

  13. Calibration of CR-39 for radon-related parameters using sealed cup technique

    International Nuclear Information System (INIS)

    Abo-Elmagd, M.; Daif, M. M.

    2010-01-01

    Effective radium content, mass and areal radon exhalation rates of soil and rock samples are important radon-related parameters and can be used as a better indicator of radon risk. A sealed cup fitted to a CR-39 detector and to the sample under measurement is an advantageous passive device for the measurement of these parameters. The main factors affecting the results are the detector calibration factor and the sample weight. The results of an active technique (Lucas cell) and the CR-39 detector have been found to be correlated resulting in a reliable detector calibration factor. The result illustrates the dependence of the CR-39 calibration factor with the sample weight which is difficult to use in practice, because each sample weight has its own calibration factor of CR-39. It is reported to demonstrate the advantage of a back diffusion correction. After correcting the results for back diffusion effects, one obtains an approximately constant calibration factor for the sample volumes up to one-third the total sealed cup volume. For this condition the calibration factor is equal to 0.237 track cm -2 per Bq m -3 d with about 1% uncertainty. (authors)

  14. The effect of Al and Cr additions on pack cementation zinc coatings

    International Nuclear Information System (INIS)

    Chaliampalias, D.; Papazoglou, M.; Tsipas, S.; Pavlidou, E.; Skolianos, S.; Stergioudis, G.; Vourlias, G.

    2010-01-01

    Zinc is widely used as a protective coating material due to its corrosion resistant properties. The structure and oxidation resistance of Al and Cr mixed zinc coatings, deposited by pack cementation process, is thoroughly examined in this work. The morphology and chemical composition of the as-deposited and oxidized samples was accomplished by electron microscopy while the phase identification was performed by XRD diffraction analysis. The experimental results showed that the addition of aluminum or chromium in the pack mixture forms only Al and Cr rich phases on the surface of the specimens without affecting significantly the phase composition of the rest zinc coatings. In the case of Zn-Al coatings, the overlying layer contains high concentrations of Al together with lower amounts of zinc and iron and in Zn-Cr coatings this layer contains Cr, Fe and Zn atoms and has much smaller thickness. The presence of these additional layers promotes significantly the oxidation resistance of the zinc pack coatings and they preserve most of their initial thickness and chemical content when exposed to an aggressive environment while their oxidation mass gain was measured at low levels during the oxidation tests.

  15. Characterization of Polish rape and honeydew honey according to their mineral contents using ICP-MS and F-AAS/AES

    International Nuclear Information System (INIS)

    Madejczyk, Maria; Baralkiewicz, Danuta

    2008-01-01

    In this work twelve elements (Al, B, Ca, Cr, Cu, Fe, K, Mg, Mn, Na, Ni and Zn) were determined in 30 honey samples from various locations within Poland and in two different types of honey- rape and honeydew. Trace elements (Al, B, Cr, Mn and Ni) were determined by Inductively Coupled Plasma-Mass Spectrometry (ICP-MS), however, major elements (Ca, K, Mg, Na) and Cu, Fe, Zn were determined by Flame Atomic Absorption Spectrometry (F-AAS). Cluster analysis of honey data revealed that the origin of honey samples correlated with their chemical composition. It was shown that rape honey includes lower amounts of manganese than honeydew honeys. Also honeydew honey includes much higher concentrations of Al, Cu, K, Fe and Ni in comparison with rape honey. Moreover honeydew honey was found to have a higher mineral content, which reflects sources from which the honey is composed. Trace element analysis showed that the differences in the values found in honey samples could be used as evidence of the quality of honey samples

  16. A CR-39 track dosemeter for routine individual neutron monitoring

    International Nuclear Information System (INIS)

    Luszik-Bhadra, M.; Alberts, W.G.; Dietz, E.; Guldbakke, S.; Matzke, M.; d'Errico, F.

    1994-01-01

    A personal neutron dosemeter for routine individual monitoring is proposed. It is based on a CR-39 track detector covered on three separate areas by converters with different boron contents and inserted into a commercial TLD albedo dosemeter capsule. The dose readings from three areas of the electrochemically etched CR-39 detector are combined to yield a dose equivalent response which is almost independent of the incident neutron energy in the range from thermal neutrons up to 20 MeV. In addition, the dose contributions of thermal, intermediate and fast neutrons can be determined separately. Unlike the TLD albedo dosemeter, which in general requires prior in-field calibration and whose use is then restricted to that field, this dosemeter can be used in neutron fields without any knowledge of the spectral distribution with the same calibration factor. The angular dependence of the dosemeter's response has been measured and compared with that of the directional dose equivalent H'(10). The lower limit of detection is 0.15 mSv. It is possible to obtain an independent, second dose reading from the same Cr-39 detector for neutron energies above 100 keV. The dosemeter has also been successfully tested for use in accident dosimetry applying chemical etching and an optical density reading of the CR-39 detector. (author)

  17. Effects of filler metal composition on the microstructure and mechanical properties for ER NiCrFe-7 multi-pass weldments

    Energy Technology Data Exchange (ETDEWEB)

    Mo, Wenlin; Lu, Shanping, E-mail: shplu@imr.ac.cn; Li, Dianzhong; Li, Yiyi

    2013-10-10

    The effects of the minor elements Ti and Nb on the microstructure and mechanical properties for multi-pass weldments from the alloy ER NiCrFe-7 were studied using an optical microscope (OM), scanning electron microscope (SEM), transmission electron microscope (TEM), electron probe micro analysis (EPMA), as well as tensile and bend tests. The results show that grain size does not change significantly by increasing the Ti content from 0.28 wt% to 0.87 wt% in the weld metal (WM), whereas the grain boundaries become tortuous. The intragranular precipitate in the WM with Ti are AlO and Ti(C, N), whereas the intragranular precipitate in the WM with Nb are AlO and MX (M=Nb, Ti, X=C, N). As the Ti and Nb content increased in the WM, more MX was produced. Furthermore, the majority of C was fixed in the grain, not segregated to the grain boundaries; and less M{sub 23}C{sub 6} (M=Cr, Fe) formed at the grain boundaries. Fewer ductility-dip-cracking (DDC) was observed for WM with higher levels of Ti and Nb. The tensile strength and elongation simultaneously increased with an increase in Ti and Nb in WM. The number and length of the cracks in the bend specimens decreased upon adding Ti and Nb.

  18. Adsorption and diffusion of fluorine on Cr-doped Ni(111) surface: Fluorine-induced initial corrosion of non-passivated Ni-based alloy

    Energy Technology Data Exchange (ETDEWEB)

    Ren, Cui-Lan, E-mail: rencuilan@sinap.ac.cn [Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Key Laboratory of Interfacial Physics and Technology, Chinese Academy of Sciences, Shanghai 201800 (China); Han, Han [Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Gong, Wen-Bin [Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Suzhou Institute of Nano-Tech and Nano-Bionics, Chinese Academy of Sciences, Shanghai 215123 (China); Wang, Cheng-Bin; Zhang, Wei [Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Key Laboratory of Interfacial Physics and Technology, Chinese Academy of Sciences, Shanghai 201800 (China); Cheng, Cheng [Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Huai, Ping, E-mail: huaiping@sinap.ac.cn [Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Zhu, Zhi-Yuan [Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Key Laboratory of Interfacial Physics and Technology, Chinese Academy of Sciences, Shanghai 201800 (China)

    2016-09-15

    Adsorption and diffusion behaviors of fluorine on Cr-doped Ni(111) surface are investigated by using first-principles simulation. It shows that the Cr in the Cr-doped Ni(111) surface serve a trap site for fluorine with adsorption energy 3.52 eV, which is 1.04 eV higher than that on Ni(111) surface. Moreover, the Cr atom is pulled out the surface for 0.41 Å after the fluorine adsorption, much higher than that on Ni(111) surface. Further diffusion behaviors analysis confirms the conclusion because the fluorine diffusion from neighbored sites onto the Cr top site is an energy barrierless process. Detailed electronic structure analysis shows that a deeper hybrid state of F 2 p-Cr 3 d indicates a strong F−Cr interaction. The Ni−Cr bond is elongated and weakened due to the new formed F−Cr bonding. Our results help to understanding the basic fluorine-induced initial corrosion mechanism for Ni-based alloy in molten salt environment.

  19. Making User-Generated Content Communities Work in Higher Education - The Importance of Setting Incentives

    Science.gov (United States)

    Vom Brocke, Jan; White, Cynthia; Walker, Ute; Vom Brocke, Christina

    The concept of User-Generated Content (UGC) offers impressive potential for innovative learning and teaching scenarios in higher education. Examples like Wikipedia and Facebook illustrate the enormous effects of multiple users world-wide contributing to a pool of shared resources, such as videos and pictures and also lexicographical descriptions. Apart from single examples, however, the systematic use of these virtual technologies in higher education still needs further exploration. Only few examples display the successful application of UGC Communities at university scenarios. We argue that a major reason for this can be seen in the fact that the organizational dimension of setting up UGC Communities has widely been neglected so far. In particular, we indicate the need for incentive setting to actively involve students and achieve specific pedagogical objectives. We base our study on organizational theories and derive strategies for incentive setting that have been applied in a practical e-Learning scenario involving students from Germany and New Zealand.

  20. Cr(VI) reduction and immobilization by novel carbonaceous modified magnetic Fe_3O_4/halloysite nanohybrid

    International Nuclear Information System (INIS)

    Tian, Xike; Wang, Weiwei; Tian, Na; Zhou, Chaoxin; Yang, Chao; Komarneni, Sridhar

    2016-01-01

    Highlights: • A novel magnetic nonohybrids (Fe_3O_4/HNTs@C) were synthesized for Cr(VI) removal. • Cr(VI) was reduced to Cr(III) by Fe_3O_4 nanoparticles and hydroxyl groups. • Cr ions were attached on Fe_3O_4/HNTs@C by ion exchange and coordination interaction. - Abstract: In this work, a novel “Dumbbell-like” magnetic Fe_3O_4/Halloysite nanohybrid (Fe_3O_4/HNTs@C) with oxygen-containing organic group grafting on the surface of natural halloysite nanotubes (HNTs) and homogeneous Fe_3O_4 nanospheres selectively aggregating at the tips of modified halloysite nanotubes was successfully synthesized. XRD, TEM, IR spectroscopy, XPS and VSM were used to characterize this newly halloysite nanohybrid and its formation mechanism was discussed. Cr(VI) ions adsorption experiments showed that the Fe_3O_4/halloysite nanohybrid exhibited higher adsorption ability with a maximum adsorption capacity of 132 mg/L at 303 K, which is about 100 times higher than that of unmodified halloysite nanotubes. More importantly, with the reduction of Fe_3O_4 and electron–donor effect of oxygen-containing organic groups, Cr(VI) ions were easily reduced into low toxicity Cr(III) and then adsorbed onto the surface of halloysite nanohybrid. In addition, appreciable magnetization was observed due to the aggregation of magnetite nanoparticles, which make adsorbent facility separated from aqueous solutions after Cr pollution adsorption.

  1. Spin reorientation and magnetic anisotropy in Y2Co17-xCr x (x 1.17-3.0) compounds

    International Nuclear Information System (INIS)

    Fuquan, B.; Tegus, O.; Dagula, W.; Brueck, E.; Boer, F.R. de; Buschow, K.H.J.

    2005-01-01

    Spin reorientation transitions and magnetic anisotropy in Y 2 Co 17-x Cr x (x = 1.17-3.0) compounds have been investigated by means of X-ray diffraction and magnetization measurements. The powder X-ray diffraction patterns show that most samples crystallize as a single phase with the rhombohedral Th 2 Zn 17 -type structure. However, in the compound Y 2 Co 14 Cr 3 the Th 2 Zn 17 phase coexist with the hexagonal Th 2 Ni 17 -type phase. The lattice parameters a and c hardly change and the unit cell volume V increases slightly with increasing Cr content. The X-ray diffraction patterns of the aligned powder of the samples have confirmed that at room temperature the compound with x = 1.17 has planar anisotropy, but the compounds with x = 1.76, 2.34 and 3.00 have uniaxial anisotropy. Spin reorientation phenomena occur in all of the compounds. With increasing Cr content, the Curie temperature, the spin reorientation temperature, the spontaneous magnetization, and the anisotropy constant K 2 of the Y 2 Co 17-x Cr x (x = 1.17-3.0) compounds decrease strongly while the anisotropy constant K 1 increases in the range of x from 1.17 to 2.34 and then decreases in the range of x from 2.34 to 3.00

  2. TEM investigations on the effect of chromium content and of stress relief treatment on precipitation in Alloy 82

    International Nuclear Information System (INIS)

    Sennour, M.; Chaumun, E.; Crépin, J.; Duhamel, C.; Gaslain, F.; Guerre, C.; Curières, I. de

    2013-01-01

    Highlights: •Slight change of the Cr content does not affect the microstructure of the butt welds. •Stress relief thermal treatment leads to the intergranular precipitation of Cr 23 C 6 . •The Cr 23 C 6 carbides are supposed to improve the SCC resistance of the butt welds. -- Abstract: Nickel-base alloys are widely used in nuclear Pressurized Water Reactors (PWRs). Most of them have been found susceptible to Stress Corrosion Cracking (SCC) in nominal PWR primary water. The time to initiation depends on the material and is longer for weld metals than for Alloy 600. This study will focus on Alloy 82, which is used in Dissimilar Metal Welds (DMWs). In service, DMWs are either in the as-welded state or have undergone a stress relief treatment. Previous SCC studies showed that the heat treatment reduces significantly the SCC susceptibility of the weld. In this context, this study focuses on the microstructure characterization of the weld in the as-welded state and in the heat-treated state. As chromium content is also a key factor for the SCC susceptibility, welds with low chromium content and medium chromium content were studied. The lower SCC susceptibility of the heat-treated welds was attributed to intergranular Cr 23 C 6 resulting from a combined effect of heat treatment and chromium and carbon contents. These intergranular carbides could explain the better behavior of Alloy 82, compared to other nickel-base alloys

  3. Plantago lanceolata growth and Cr uptake after mycorrhizal inoculation in a Cr amended substrate

    Directory of Open Access Journals (Sweden)

    Amaia Nogales

    2012-03-01

    Full Text Available Arbuscular mycorrhizal fungi from two chromium contaminated sites, one with 275 mg kg-1 of Cr (zone A and the other with 550 mg kg-1 Cr (zone B, were multiplied and tentatively identified. The effect of both fungal consortia on Plantago lanceolata plant growth in a substrate amended with 200 mg kg-1 of Cr and with 400 mg kg-1 Cr was assessed and compared with the growth of plants inoculated with Glomus intraradices BEG72. Only the plants inoculated with G. intraradices BEG72 and with the fungal consortia obtained from the area with a high Cr contamination (zone B grew in the soil with 400 mg kg-1 of Cr. The consortia of fungi from zone B, decreased the plant’s uptake/translocation of the heavy metal compared with G. intraradices BEG72. These results underscore the differential effect of AM fungi in conferring bioprotection in Cr contaminated soils.

  4. Effect of Cr4+ impurities in Nd:Cr:GSGG and Nd:Cr:YAG laser materials on parameters of lasers at solar pumping

    International Nuclear Information System (INIS)

    Payziyev, Sh.D.; Bakhramov, S.A.; Shayimov, F.F.; Fayziev, A.Sh.

    2015-01-01

    The analysis of an effect of Cr 4+ impurity ions, existent in Nd 3+ :Cr 3+ :GSGG and Nd 3+ :Cr 3+ :YAG laser materials on output parameters of solar pumped lasers is carried out by modeling of lasing process at solar pumping. (authors)

  5. Effect of aluminum content on the passivation behavior of Fe-Al alloys in sulfuric acid solution

    DEFF Research Database (Denmark)

    Chiang, Wen-Chi; Luu, W.C.; Wu, J.K.

    2006-01-01

    -Al alloys, which the Al content of alloy exceeds 19 at %, have wide passivation regions with low passivation current. However, when the Al content of Fe-Al alloys exceeds this range, the increment of Al content has slight influence on passivation behavior compared with ternary Cr addition....

  6. Effects of environment on the release of Ni, Cr, Fe, and Co from new and recast Ni-Cr alloy.

    Science.gov (United States)

    Oyar, Perihan; Can, Gülşen; Atakol, Orhan

    2014-07-01

    The addition of previously cast alloy to new alloy for economic reasons may increase the release of elements. The purpose of this study was to analyze the effects of the immersion period, immersion media, and addition of previously cast alloy to new alloy on the release of elements. Disk-shaped specimens were prepared from a Ni-Cr alloy (Ni: 61 wt%, Cr: 26 wt%, Mo: 11 wt%, Si: 1.5 wt%, Fe, Ce, Al, and Co alloy (group N) and 50% new/50% recast alloy (group R). After the immersion of the specimens in both NaCl (pH 4) and artificial saliva (pH 6.7) for 3, 7, 14, 30, and 60 days, the release of ions was determined by using atomic absorption spectrometry. Data were analyzed with a 3-way ANOVA (α=.001). The release of Ni was significantly affected by the immersion period, of Ni and Cr by the alloy and media (Palloy (Palloy in artificial saliva was 109.71 for Ni, 6.49 for Cr, 223.22 for Fe, and 29.90 μg/L for Co. The release of Co in NaCl was below the detection limit in both groups. The release of Ni in NaCl and artificial saliva increased with the length of the immersion period in both groups. The release of Cr and Fe was higher in artificial saliva than in NaCl in group R, regardless of the immersion period. The release of Co in NaCl was below the detection limit in both groups. Copyright © 2014 The Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

  7. Sintering behaviour and mechanical properties of Cr3C2–NiCr ...

    Indian Academy of Sciences (India)

    fracture toughness. Keywords. Cermet; Cr3C2–NiCr; sintering; mechanical properties. ... et al investigated the mechanical properties of VC, Cr3C2 and NbC doped ..... Huang S G, Li L, Van der Biest O and Vleugels J 2008 J. Alloys. Compds.

  8. Observation of room temperature ferromagnetism in ZnTe:Cr films grown onto glass substrate by thermal evaporation method

    Energy Technology Data Exchange (ETDEWEB)

    Soundararajan, D; Mangalaraj, D; Nataraj, D [Thin Film Laboratory, Department of Physics, Bharathiar University, Coimbatore -641 046 (India); Dorosinskii, L [National Institute of Metrology (TUBITAK -UME), P.K. 54, 41470, Gebze -Kocaeli (Turkey); Santoyo-Salazar, J, E-mail: dorosins@ume.tubitak.gov.t [Universidad Nacional Autonoma de Mexico, Instituto de Investigaciones en Materiales, Mexico D.F. 04510 (Mexico)

    2009-03-01

    ZnTe and ZnTe:Cr films were prepared onto glass substrates using thermal evaporation method. Structural properties of the prepared samples were analyzed using X-ray diffractometer, and the presence of ZnCrTe phase was identified along with poor crystallinity. Composition analysis was done using XPS and the Cr content in the film was found to be 0.05 atomic percent. Transmittance spectra were recorded using UV-Vis spectrophotometer. The valence state of Cr in ZnTe:Cr film is determined to be +2 using electron spin resonance (ESR) spectroscopy. Magnetic moment data as a function of magnetic field were recorded using Superconducting Quantum Interference Device (SQUID) magnetometer at temperatures 5, 77 and 300 K. The results showed minority ferromagnetic behavior even at room temperature. Magnetic domains were observed using Magnetic Force Microscopy and the average value of domain size is 3.7 nm.

  9. Tea waste biomass activated carbon electrode for simultaneous removal of Cr(VI) and fluoride by capacitive deionization.

    Science.gov (United States)

    Gaikwad, Mahendra S; Balomajumder, Chandrajit

    2017-10-01

    Capacitive deionization is promising less energy based desalination technique to achieve pure water. In the present study microporous activated carbon was prepared from tea waste biomass by chemical and thermal modification. Further TWBAC was used for preparation of the electrode. The TWBAC electrode was applied in the self-made CDI set up for simultaneous removal of hexavalent chromium [Cr(VI)] and fluoride (F) form mixed feed solution of Cr(VI) and F. The performance of TWBAC electrode was found effective for simultaneous removal of Cr(VI) and F from mixed feed solution. The maximum electrosorption capacity of Cr(VI) and F were found 0.77 and 0.74 mg g -1 for 10 mg L -1 and 2.83 and 2.49 mg g -1 for 100 mg L -1 mixed feed solution respectively. The higher removal of Cr(VI) was found due to the electrosorption selectivity of the divalent CrO 4 2- is higher than that of the monovalent F - . Multicomponent isotherm modeling and kinetic study were carried out in this study. TWBAC CDI electrode could be useful for treatment of a low concentrated Cr(VI) and F containing wastewater. Copyright © 2017 Elsevier Ltd. All rights reserved.

  10. Structural, optical and ferromagnetic properties of Cr doped TiO2 nanoparticles

    International Nuclear Information System (INIS)

    Choudhury, Biswajit; Choudhury, Amarjyoti

    2013-01-01

    Graphical abstract: Doping of Cr 3+ distorts the lattice of TiO 2 , generate oxygen vacancies and create d-band states in the mid band gap of TiO 2 . Incorporation of Cr 3+ also imparts magnetism in non-magnetic TiO 2 by undergoing coupling with the neighboring oxygen vacancies. -- Highlights: • Incorporation of Cr 3+ increases the concentration of oxygen vacancies in TiO 2 nanoparticles. • Doped TiO 2 nanoparticles contain absorption peaks corresponding to d–d transition of Cr 3+ into TiO 2 . • Pure and doped TiO 2 nanoparticles contain emission peaks related to oxygen vacancies. • Pure TiO 2 shows diamagnetism while Cr doped TiO 2 shows ferromagnetism. • The ferromagnetism is due to the interaction of Cr 3+ ions via oxygen vacancies. -- Abstract: Cr doped TiO 2 nanoparticles are prepared with three different concentrations of chromium, 1.5%, 3.0% and 4.5 mol% respectively. Doping decreases the crystallinity and increases the width of the X-ray diffraction peak. The Raman active E g peak of TiO 2 nanoparticles become asymmetric and shifted to higher energy on doping of 4.5% chromium. Electron paramagnetic resonance spectra reveal the presence of Cr 3+ in the host TiO 2 matrix. The absorption spectra of Cr doped TiO 2 nanoparticles contain absorption peaks corresponding to d–d transition of Cr 3+ in octahedral coordination. Most of the visible emission peaks are due to the electrons trapped in the oxygen vacancy centers. Undoped TiO 2 nanoparticles show diamagnetism at room temperature while all chromium doped samples show ferromagnetism. The magnetization of the doped samples increases at 1.5% and 3.0% and decreases at 4.5%. The ferromagnetism arises owing to the interaction of the neighboring Cr 3+ ions via oxygen vacancies. The decrease of magnetization at the highest doping is possibly due to the antiferromagnetic interactions of Cr 3+ pairs or due to Cr 3+ -O 2− -Cr 3+ superexchange interaction in the lattice

  11. Phase Evolution in and Creep Properties of Nb-Rich Nb-Si-Cr Eutectics

    Science.gov (United States)

    Gang, Florian; Kauffmann, Alexander; Heilmaier, Martin

    2018-03-01

    In this work, the Nb-rich ternary eutectic in the Nb-Si-Cr system has been experimentally determined to be Nb-10.9Si-28.4Cr (in at. pct). The eutectic is composed of three main phases: Nb solid solution (Nbss), β-Cr2Nb, and Nb9(Si,Cr)5. The ternary eutectic microstructure remains stable for several hundred hours at a temperature up to 1473 K (1200 °C). At 1573 K (1300 °C) and above, the silicide phase Nb9(Si,Cr)5 decomposes into α-Nb5Si3, Nbss, and β-Cr2Nb. Under creep conditions at 1473 K (1200 °C), the alloy deforms by dislocation creep while the major creep resistance is provided by the silicide matrix. If the silicide phase is fragmented and, thus, its matrix character is destroyed by prior heat treatment [ e.g., at 1773 K (1500 °C) for 100 hours], creep is mainly controlled by the Laves phase β-Cr2Nb, resulting in increased minimum strain rates. Compared to state of the art Ni-based superalloys, the creep resistance of this three-phase eutectic alloy is significantly higher.

  12. Evaluation of trace elements contents in healthy and seborrhoeic skin samples by SRTXRF

    International Nuclear Information System (INIS)

    Soares, Julio C.A.C.; Anjos, Marcelino J.; Lopes, Ricardo T.

    2009-01-01

    The aim of this work is to evaluate the concentrations of trace elements content in seborrhoeic keratosis (SK) skin lesions as well in normal skin and compare them. These data was acquired by Synchrotron Radiation Total Reflection X-ray Fluorescence (SRTXRF). It focused elements with atomic number greater than 14. This stage of research was supported by LNLS - Brazilian Synchrotron Light Laboratory in Campinas/Sao Paulo-Brazil. The collection of lesion and healthy skin samples, including papillary dermis and epidermis, from the same patient, has involved 5 males and females with ages varying from 34 to 80 years old. The results have shown the presence of P, S, Cl, K, Ca, Ti, Cr, Fe, Ni, Cu, and Zn in healthy skin. The comparison with lesion contents has revealed significant differences in contents of Fe, K, Cr, and Zn. (author)

  13. Evaluation of trace elements contents in healthy and seborrhoeic skin samples by SRTXRF

    Energy Technology Data Exchange (ETDEWEB)

    Soares, Julio C.A.C.; Anjos, Marcelino J.; Lopes, Ricardo T., E-mail: marcelin@lin.ufrj.b, E-mail: ricardo@lin.ufrj.b [Federal University of Rio de Janeiro (UFRJ/COPPE), Rio de Janeiro, RJ (Brazil). Nuclear Engineering Program. Nuclear Instrumentation Lab.

    2009-07-01

    The aim of this work is to evaluate the concentrations of trace elements content in seborrhoeic keratosis (SK) skin lesions as well in normal skin and compare them. These data was acquired by Synchrotron Radiation Total Reflection X-ray Fluorescence (SRTXRF). It focused elements with atomic number greater than 14. This stage of research was supported by LNLS - Brazilian Synchrotron Light Laboratory in Campinas/Sao Paulo-Brazil. The collection of lesion and healthy skin samples, including papillary dermis and epidermis, from the same patient, has involved 5 males and females with ages varying from 34 to 80 years old. The results have shown the presence of P, S, Cl, K, Ca, Ti, Cr, Fe, Ni, Cu, and Zn in healthy skin. The comparison with lesion contents has revealed significant differences in contents of Fe, K, Cr, and Zn. (author)

  14. Structural and Visible-Near Infrared Optical Properties of Cr-Doped TiO2 for Colored Cool Pigments

    Science.gov (United States)

    Yuan, Le; Weng, Xiaolong; Zhou, Ming; Zhang, Qingyong; Deng, Longjiang

    2017-11-01

    Chromium-doped TiO2 pigments were synthesized via a solid-state reaction method and studied with X-ray diffraction, SEM, XPS, and UV-VIS-NIR reflectance spectroscopy. The incorporation of Cr3+ accelerates the transition from the anatase phase to the rutile phase and compresses the crystal lattice. Moreover, the particle morphology, energy gap, and reflectance spectrum of Cr-doped TiO2 pigments is affected by the crystal structure and doping concentration. For the rutile samples, some of the Cr3+ ions are oxidized to Cr4+ after sintering at a high temperature, which leads to a strong near-infrared absorption band due to the 3A2 → 3 T1 electric dipole-allowed transitions of Cr4+. And the decrease of the band gap causes an obvious redshift of the optical absorption edges as the doping concentration increases. Thus, the VIS and near-infrared average reflectance of the rutile Ti1 - x Cr x O2 sample decrease by 60.2 and 58%, respectively, when the Cr content increases to x = 0.0375. Meanwhile, the color changes to black brown. However, for the anatase Ti1 - x Cr x O2 pigments, only the VIS reflection spectrum is inhibited by forming some characteristic visible light absorption peaks of Cr3+. The morphology, band gap, and NIR reflectance are not significantly affected. Finally, a Cr-doped anatase TiO2 pigment with a brownish-yellow color and 90% near-infrared reflectance can be obtained.

  15. The influences of impurity content, tensile strength, and grain size on in-service temper embrittlement of CrMoV steels

    International Nuclear Information System (INIS)

    Cheruvu, N.S.; Seth, B.B.

    1989-01-01

    The influences of impurity levels, grain size, and tensile strength on in-service temper embrittlement of CrMoV steels have been investigated. The samples for this study were taken from steam turbine CrMoV rotors which had operated for 15 to 26 years. The effects of grain size and tensile strength on embrittlement susceptibility were separated by evaluating the embrittlement behavior of two rotor forgings made from the same ingot after an extended step-cooling treatment. Among the residual elements in the steels, only P produces a significant embrittlement. The variation of P and tensile strength has no effect on in-service temper embrittlement susceptibility, as measured by the shift in fracture appearance transition temperature (FATT). However, the prior austenite grain size plays a major role in service embrittlement. The fine grain steels with a grain size of ASTM No. 9 or higher are virtually immune to in-service embrittlement. In steels having duplex grain sizes, embrittlement susceptibility is controlled by the size of coarser grains. For a given steel chemistry, the coarse grain steel is more susceptible to in-service embrittlement, and a decrease in ASTM grain size number from 4 to 0/1 increases the shift in FATT by 61 degrees C (10/10 degrees F). It is demonstrated that long-term service embrittlement can be simulated, except in very coarse grain steels, by using the extended step-cooling treatment. The results of step-cooling studies show that the coarse grain rotor steels take longer time during service to reach a fully embrittled state than the fine grain rotor steels

  16. Characteristics of Modified 9Cr-1Mo Steel for Reactor Pressure Vessel of Very High Temperature Gas Cooled Reactor

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Sung Ho; Ryu, W. S.; Han, Chang Hee; Yoon, J. H.; Chang, Jong Hwa

    2004-11-15

    Many researches and developments have been progressed for the construction of VHTR by 2020 in Korea. Modified 9Cr-1Mo steel has been receiving attention for the application to the reactor pressure vessel material of VHTR. We collected and analyzed the research data for modified 9Cr-1Mo steel in order to understand the characteristics of modified 9Cr-1Mo steel. The modified 9Cr-1Mo steel is a modified alloy system similar to conventional 9Cr-1Mo grade ferritic steel. Modifications include additions of vanadium, niobium, and nitrogen, as well as lower carbon content. In this report, we summarized the change of microstructure and mechanical properties after tempering, thermal aging, and irradiation. Modified 9Cr-1Mo steel has high strength and thermal conductivity, low thermal expansion, and good resistance to corrosion. But the irradiation embrittlement behavior of modified 9Cr-1Mo steel should be evaluated and the evaluation methodology also should be developed. At the same time, the characteristics of weldment which is the weak part in pressure vessel should be evaluated.

  17. Black Cr/α-Cr2O3 nanoparticles based solar absorbers

    International Nuclear Information System (INIS)

    Khamlich, S.; Nemraoui, O.; Mongwaketsi, N.; McCrindle, R.; Cingo, N.; Maaza, M.

    2012-01-01

    Monodisperse spherical core–shell particles of Cr/α-Cr 2 O 3 with high adhesion were successfully coated on rough copper substrates by a simple self-assembly-like method for the use in solar thermal absorbers. The structure and morphology of the core-shell particles of Cr/α-Cr 2 O 3 were effectively controlled by deposition temperature and the pH of the initial precursor solution. Their characterizations were carried out with X-ray diffraction, scanning electron microscopy, energy dispersive spectrometry and attenuated total reflection, as well as UV–vis diffuse reflectance spectroscopy. The samples aged for more than 40 h at 75 °C exhibit the targeted high absorbing optical characteristic “Black chrome” while those aged for ≤40 h show a significant high UV–vis diffuse reflectance “green color”.

  18. Influence of irradiation with energy-rich particles on the hardness of the Fe-Cr alloy; Einfluss der Bestrahlung mit energiereichen Teilchen auf die Haerte von Fe-Cr-Legierungen

    Energy Technology Data Exchange (ETDEWEB)

    Heintze, Cornelia

    2013-01-14

    Ferritic/martensitic and oxide dispersion strengthened ferritic/martensitic steels are candidate structural materials for components exposed to high neutron fluxes in future nuclear applications like fusion and generation IV fission reactors. The ductilebrittle transition and its shift to higher temperatures which is predominantly caused by irradiation hardening are main concerns for these materials. In the present work, the irradiation behaviour of binary Fe-Cr model alloys, which represent a simplified model for ferritic/martensitic steels, is studied. To this end irradiation with iron ions is used in order to simulate the neutron-induced damage. Due to the limited penetration depth characterization methods suitable for thin layers have to be applied. In the present case, nanohardness testing and transmission electron microscopy (TEM) are employed. The results, including the irradiation-induced hardness change of the layer as a function of chromium content, fluence and irradiation temperature and, for selected cases, quantitative TEM analyses, were exploited to identify irradiation-induced dislocation loops as one source of irradiation hardening. Additional results of small-angle neutron scattering experiments on neutron-irradiated specimens of the same alloys show that nm-scaled α'-phase precipitates also significantly contribute to the irradiation-induced hardness increase. An Orowan model is used to estimate the obstacle strengths posed to dislocation glide by these lattice defects. The topic is stepwise extended to more complex situations with respect to the irradiation conditions and the materials. Considering simultaneous and sequential irradiations with iron- and helium-ions it is shown that the effect of helium on irradiation hardening depends on the chronological order of the irradiations and that the simultaneous introduction of helium in fusion-relevant concentrations amplifies irradiation hardening based on a synergistic effect. There is no

  19. Parametric and experimentally informed BWR Severe Accident Analysis Utilizing FeCrAl - M3FT-17OR020205041

    Energy Technology Data Exchange (ETDEWEB)

    Ott, Larry J. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Howell, Michael [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Robb, Kevin R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2017-08-01

    Iron-chromium-aluminum (FeCrAl) alloys are being considered as advanced fuel cladding concepts with enhanced accident tolerance. At high temperatures, FeCrAl alloys have slower oxidation kinetics and higher strength compared with zirconium-based alloys. FeCrAl could be used for fuel cladding and spacer or mixing vane grids in light water reactors and/or as channel box material in boiling water reactors (BWRs). There is a need to assess the potential gains afforded by the FeCrAl accident-tolerant-fuel (ATF) concept over the existing zirconium-based materials employed today. To accurately assess the response of FeCrAl alloys under severe accident conditions, a number of FeCrAl properties and characteristics are required. These include thermophysical properties as well as burst characteristics, oxidation kinetics, possible eutectic interactions, and failure temperatures. These properties can vary among different FeCrAl alloys. Oak Ridge National Laboratory has pursued refined values for the oxidation kinetics of the B136Y FeCrAl alloy (Fe-13Cr-6Al wt %). This investigation included oxidation tests with varying heating rates and end-point temperatures in a steam environment. The rate constant for the low-temperature oxidation kinetics was found to be higher than that for the commercial APMT FeCrAl alloy (Fe-21Cr-5Al-3Mo wt %). Compared with APMT, a 5 times higher rate constant best predicted the entire dataset (root mean square deviation). Based on tests following heating rates comparable with those the cladding would experience during a station blackout, the transition to higher oxidation kinetics occurs at approximately 1,500°C. A parametric study varying the low-temperature FeCrAl oxidation kinetics was conducted for a BWR plant using FeCrAl fuel cladding and channel boxes using the MELCOR code. A range of station blackout severe accident scenarios were simulated for a BWR/4 reactor with Mark I containment. Increasing the FeCrAl low-temperature oxidation rate

  20. Tribological Behavior of Al-Cr Coating Obtained by Dgpsm and IIP Composite Technology

    Science.gov (United States)

    Luo, Xixi; Yao, Zhengjun; Zhang, Pingze; Zhou, Keyin; Chen, Yu; Tao, Xuewei

    An Al-Cr composite alloyed layer composed of an Al enriched layer, a Cr enriched layer and a transition layer from the surface to the bulk along the cross-section was deposited on a 45# steel substrate by composite technology, where Cr was deposited using double glow plasma surface metallurgy (DGPSM), and Al was then implanted by ion implantation (IIP) to achieve higher micro-hardness and excellent abrasive resistance. The composite alloyed layer is approximately 5μm, and as metallurgical adherence to the substrate. The phases are Al8Cr5, Fe2AlCr, Cr23C6, Cr (Al) and Fe (Cr, Al) solid solution. The wear resistance tests were performed under various rotational speed (i.e. 280, 560 and 840r/min) with silicon nitride balls as the counterface material at ambient temperature. The Al-Cr composite alloyed layer exhibits excellent wear resistance when the speed is 280r/min with a friction coefficient as low as 0.3, which is attributed to Al8Cr5 in the Al implanted layer that withstands abrasive wear. Better wear resistance (friction coefficient: 0.254) at 560r/min is resulted from the formation of a high micro-hardness zone, and an oxidation layer with lubrication capacity. In addition, the composite alloyed layer suffers severe oxidative wear and adhesive wear at 840r/min due to the increment of the frictional heating. When compared to the 45# steel substrate, the enhanced wear resistance of the Al-Cr composite alloyed layer demonstrates the viable method developed in this work.

  1. Isotope Effects in the Bonds of beta-CrOOH and beta-CrOOD

    DEFF Research Database (Denmark)

    Nørlund Christensen, A.; Hansen, P.; Lehmann, M. S.

    1976-01-01

    Samples of orthorhombic chromium oxide hydroxide, beta -CrOOH, and the deuterated compound, beta -CrOOD, were prepared hydrothermally. The crystal structures were determined by powder profile refinement technique using neutron diffraction data. Unit cells are: beta -CrOOH: a equals 4. 862(2) A, b...... equals 4. 298(a) A, c equals 2. 995(1) A; beta -CrOOD: a equals 4. 873(5) A, b equals 4. 332(7) A, c equals 2. 963(2) A, with Z equals 2. The space group is P2//1nm or Pnnm....

  2. Effect of Cr{sub 2}O{sub 3} on the microstructure and non-ohmic properties of (Co, Sb)-doped SnO{sub 2} varistors

    Energy Technology Data Exchange (ETDEWEB)

    Aguilar M, J. A. [Centro de Investigac ion en Materiales Avanzados, S. C., Alianza Norte No. 202, Parque de Investigacion e Innovacion Tecnologica, Nueva Carretera Aeropuerto Km. 10 Apodaca 66600, Nuevo Leon (Mexico); Pech C, M. I. [IPN, Centro de Investigacion y de Estudios Avanzados, Unidad Saltillo, Carretera Saltillo-Monterrey Km. 13, Saltillo 25900, Coahuila (Mexico); Hernandez, M. B.; Rodriguez, E.; Garcia O, L. [Universidad Autonoma de Nuevo Leon, Facultad de Ingenieria Mecanica y Electrica, San Nicolas de los Garza, Nuevo Leon (Mexico); Glot, A. B., E-mail: josue.aguilar@cimav.edu.mx [Universidad Tecnologica de la Mixteca, Division de Estudios de Posgrado, Carretera Acatlima Km. 2.5, Huajuapan de Leon 69000, Oaxaca (Mexico)

    2013-10-01

    The effect of Cr{sub 2}O{sub 3} addition on the physical characteristics, microstructure, and current-voltage properties of (Co-Sb)-doped SnO{sub 2} varistors was investigated. SnO{sub 2}-Co{sub 3}O{sub 4}-Sb{sub 2}O{sub 5} ceramics with additions of 0.0, 0.03, 0.05 and 0.07 mol % Cr{sub 2}O{sub 3} were sintered at 1350 C under ambient atmosphere and characterized micro structurally and electrically. The characterization by X-ray diffraction and scanning electron microscopy show that the microstructure remains as a single phase material with multimodal size distribution of SnO{sub 2} grains. The greatest effect of Cr{sub 2}O{sub 3} additions is manifested in the electric breakdown field. Additions of high levels (0.07 and 0.05 %) of this oxide promote and increase of approximately 55% in this parameter compared to the Cr{sub 2}O{sub 3}-free sample. Another physical property is affected: the measured density values decreases as the Cr{sub 2}O{sub 3} content increases. A change in the nonlinearity coefficient value is produced only at the highest Cr{sub 2}O{sub 3} content while at intermediate levels there is not change at all. Consequently, when seeking high nonlinearity coefficients, intermediate levels of Cr{sub 2}O{sub 3} are not recommended. (Author)

  3. Creep strength and microstructural evolution of 9-12% Cr heat resistant steels during creep exposure at 600 C and 650 C

    Energy Technology Data Exchange (ETDEWEB)

    Mendez Martin, Francisca [Graz Univ. of Technology (Austria). Inst. for Materials Science and Welding; Panait, Clara Gabriela [MINES ParisTech, UMR CNRS, Evry (France). Centre des Materiaux; V et M France CEV, Aulnoye-Aymeries (France); Bendick, Walter [Salzgitter Mannesmann Forschung GmbH (SZMF), Duisburg (DE)] (and others)

    2010-07-01

    9-12% Cr heat resistant steels are used for applications at high temperatures and pressures in steam power plants. 12% Cr steels show higher creep strength and higher corrosion resistance compared to 9% Cr steels for short term creep exposure. However, the higher creep strength of 12 %Cr steels drops increasingly after 10,000-20,000 h of creep. This is probably due to a microstructural instability such as the precipitation of new phases (e.g. Laves phases and Z-phases), the growth of the precipitates and the recovery of the matrix. 9% Cr and 12% Cr tempered martensitic steels that have been creep tested for times up to 50,000 h at 600 C and 650 C were investigated using Transmission Electron Microscopy (TEM) on extractive replicas and thin foils together with Backscatter Scanning Electron Microscopy (BSE-SEM) to better understand the different creep behaviour of the two different steels. A significant precipitation of Laves phase and low amounts of Z-phase was observed in the 9% Cr steels after long-term creep exposure. The size distribution of Laves phases was measured by image analysis of SEM-BSE images. In the 12% Cr steel two new phases were identified, Laves phase and Z-phase after almost 30,000 h of creep test. The quantification of the different precipitated phases was studied. (orig.)

  4. Density of Liquid Ni-Cr Alloy

    Institute of Scientific and Technical Information of China (English)

    2003-01-01

    The density of liquid Ni-Cr alloy was measured by a modified sessile drop method. The density of liquid Ni-Cr alloywas found to decrease with increasing temperature and Cr concentration in the alloy. The molar volume of liquidNi-Cr alloy increases with increasing the Cr concentration in the alloy. The molar volume of Ni-Cr alloy determinedin the present work shows a positive deviation from the linear molar volume.

  5. Analysis of PTA hardfacing with CoCrWC and CoCrMoSi alloys

    Directory of Open Access Journals (Sweden)

    Adriano Scheid

    2013-12-01

    Full Text Available CoCrWC alloys are widely used to protect components that operate under wear and high temperature environments. Enhanced performance has been achieved with the CoCrMoSi alloys but processing this alloy system is still a challenge due to the presence of the brittle Laves phase, particularly when welding is involved. This work evaluated Plasma Transferred Arc coatings processed with the Co-based alloy CoMoCrSi - Tribaloy T400, reinforced with Laves phase, comparing its weldability to the CoCrWC - Stellite 6, reinforced with carbides. Coatings were also analyzed regarding the response to temperature exposure at 600°C for 7 days and subsequent effect on microstructure and sliding abrasive wear. Coatings characterization was carried out by light and scanning electron microscopy, X-ray diffraction and Vickers hardness. CoCrWC coatings exhibited a Cobalt solid solution dendritic microstructure and a thin interdendritic region with eutectic carbides, while CoCrMoSi deposits exhibit a large lamellar eutectic region of Laves phase and Cobalt solid solution and a small fraction of primary Laves phase. Although phase stability was observed by X-ray diffraction, coarsening of the microstructure occurred for both alloys. CoCrMoSi showed thicker lamellar Laves phase and CoCrWC coarser eutectic carbides. Coatings stability assessed by wear tests revealed that although the wear rate of the as-deposited CoCrMoSi alloy was lower than that of CoCrWC alloy its increase after temperature exposure was more significant, 22% against 15%. Results were discussed regarding the protection of industrial components in particular, bearings in 55AlZn hot dip galvanizing components.

  6. Femtosecond Cr:LiSAF and Cr:LiCAF lasers pumped by tapered diode lasers.

    Science.gov (United States)

    Demirbas, Umit; Schmalz, Michael; Sumpf, Bernd; Erbert, Götz; Petrich, Gale S; Kolodziejski, Leslie A; Fujimoto, James G; Kärtner, Franz X; Leitenstorfer, Alfred

    2011-10-10

    We report compact, low-cost and efficient Cr:Colquiriite lasers that are pumped by high brightness tapered laser diodes. The tapered laser diodes provided 1 to 1.2 W of output power around 675 nm, at an electrical-to-optical conversion efficiency of about 30%. Using a single tapered diode laser as the pump source, we have demonstrated output powers of 500 mW and 410 mW together with slope efficiencies of 47% and 41% from continuous wave (cw) Cr:LiSAF and Cr:LiCAF lasers, respectively. In cw mode-locked operation, sub-100-fs pulse trains with average power between 200 mW and 250 mW were obtained at repetition rates around 100 MHz. Upon pumping the Cr:Colquiriite lasers with two tapered laser diodes (one from each side of the crystal), we have observed scaling of cw powers to 850 mW in Cr:LiSAF and to 650 mW in Cr:LiCAF. From the double side pumped Cr:LiCAF laser, we have also obtained ~220 fs long pulses with 5.4 nJ of pulse energy at 77 MHz repetition rate. These are the highest energy levels reported from Cr:Colquiriite so far at these repetition rates. Our findings indicate that tapered diodes in the red spectral region are likely to become the standard pump source for Cr:Colquiriite lasers in the near future. Moreover, the simplified pumping scheme might facilitate efficient commercialization of Cr:Colquiriite systems, bearing the potential to significantly boost applications of cw and femtosecond lasers in this spectral region (750-1000 nm).

  7. Prospects for Martensitic 12 % Cr Steels for Advanced Steam Power Plants

    DEFF Research Database (Denmark)

    Hald, John

    2016-01-01

    and FB2 are now used in power plants up to 600–620 °C steam temperature. For higher steam temperatures up to 650 °C steels with 11–12 % Cr are needed for better resistance against steam oxidation. However, fine V and Nb based nitrides may transform to coarse Z-phase [Cr(V,Nb)N] nitrides in steels...

  8. The roles of complement receptors type 1 (CR1, CD35) and type 3 (CR3, CD11b/CD18) in the regulation of the immune complex-elicited respiratory burst of polymorphonuclear leukocytes in whole blood

    DEFF Research Database (Denmark)

    Nielsen, C H; Antonsen, S; Matthiesen, S H

    1997-01-01

    cells using the monoclonal antibody (mAb) 3D9 resulted in a 1.9-fold increase in the IC-elicited PMN RB after 5 min of incubation, rising to 3.1-fold after 40 min. This enhancement was not due to increased IC deposition on PMN. Blockade of CR3 abrogated the mAb 3D9-induced rise in RB activity...... and inhibited the IC binding to PMN in a whole blood cell preparation, with or without mAb 3D9, by approximately 40% from 15-40 min while reducing their RB over 40 min to approximately one third. Blockade of CR1 on either erythrocytes (E) or leukocytes, before mixing the populations, revealed...... that the potentiation of the RB by mAb 3D9 was associated with abrogation of E-CR1 function, whereas blockade of leukocyte-CR1 had a diminishing effect. Exposure to IC at high concentrations induced release of both specific and azurophilic granule contents from PMN. The latter was CR3 dependent in that blockade...

  9. The microstructure of neutron-irradiated Fe-Cr alloys: A small-angle neutron scattering study

    International Nuclear Information System (INIS)

    Heintze, C.; Bergner, F.; Ulbricht, A.; Eckerlebe, H.

    2009-01-01

    Ferritic-martensitic chromium steels are candidate materials for future applications in both Gen-IV fission and fusion technology. Experimental investigation of neutron-irradiated Fe-Cr model alloys is important in order to gain a better understanding of the interplay of chromium content and irradiation behaviour. Small-angle neutron scattering (SANS) is particularly well suited to unfold the size distribution of non-planar irradiation-induced nanoscale features such as defect-solute clusters, nanovoids and α'- particles. This size distribution represents a statistically reliable average over a macroscopic volume. Assumptions on the dominant type of features can be checked against the ratio of magnetic and nuclear scattering. The materials investigated in this work are commercial-purity Fe-Cr alloys of nominal compositions Fe-2.5Cr, Fe-5Cr, Fe- 9Cr and Fe-12.5Cr (at %). Neutron irradiation was performed in the reactor BR2 at Mol (Belgium) at a temperature of 300 deg. C and neutron flux of 9 x 10 13 cm -2 s -1 (E > 1 MeV) [Matijasevic, JNM 377 (2008) 147]. The neutron exposures expressed in units of displacements per atom correspond to 0.6 and 1.5 dpa. A wavelength of 0.58 nm and three detector-sample distances of 1, 4 and 16 m were used in the SANS experiments carried out at the SANS-2 facility of GKSS Geesthacht (Germany). The samples were placed in a saturation magnetic field in order to separate magnetic and nuclear contributions. The scattering curves obtained for the unirradiated conditions of the four Fe-Cr alloys were taken as reference. We have found that the volume fraction of scatterers slightly increases with neutron exposure (Fe-9Cr) or exhibits a saturation-like behaviour (Fe-2.5Cr, Fe-5Cr and Fe-12.5Cr) and that the volume fraction at 1.5 dpa is an increasing function of the chromium level with a slight increase up to 9 at%Cr and a steep increase between 9 and 12.5 at%Cr. The radii of irradiation-induced scatterers are essentially less than 8 nm and

  10. Determination of the chromium content of laboratory rabbit skeletal muscles by neutron activation analysis

    International Nuclear Information System (INIS)

    Lux, F.; Trebert Haeberlin, S.; Erhardt, W.

    1986-01-01

    The chromium content of skeletal muscle of laboratory rabbits has been determined using neutron activation analysis. The procedure for separation of 51 Cr by distillation of chromium oxychloride, described in the literature, has been improved. The arrangements necessary to minimize the chromium blank values are described. The main component of this blank is caused by the residual chromium contamination of the surface of the sample vial; typical values of this component are 0.049 ng Cr (without lyophilization) and 0.12 ng Cr (with lyophilization). The analyses of standard reference materials (SRM) yielded values of the chromium contents that are in agreement (I) with the certified value in the case of NBS Citrus Leaves, and (II) with the latest published value of 9.2+-2.5 ng/g in the case of IAEA animals muscle (H-4). NBS Orchard Leaves was found not to be an appropriate SRM for testing the method. In analyses of samples of thigh muscle of bastard rabbits chromium contents of 6.2-22.9 ng/g (fresh weight basis) were obtained. Comparison of these data with a previously found value of 1.2 ng/g, the literature value [de

  11. Microstructure and Mechanical Characterization of a Dissimilar Friction-Stir-Welded CuCrZr/CuNiCrSi Butt Joint

    Directory of Open Access Journals (Sweden)

    Youqing Sun

    2018-05-01

    Full Text Available Dissimilar CuNiCrSi and CuCrZr butt joints were successfully frictionstirwelded at constant welding speed of 150 mm/min and rotational speed of 1400 rpm with the CuCrZr alloy or the CuNiCrSi alloy located on the advancing side (AS. The microstructure and mechanical properties of joints were investigated. When the CuCrZr alloy was located on the AS, the area of retreating material in the nugget zone was a little bigger. The Cr solute-rich particles were found in the nugget zone on CuCrZr side (CuCrZr-NZ while a larger density of solute-rich particles identified as the concentration of Cr and Si element was found in the nugget zone on CuNiCrSi side (CuNiCrSi-NZ. The Cr precipitates and δ-Ni2Si precipitates were found in the base metal on CuNiCrSi side (CuNiCrSi-BM but only Cr precipitates can be observed in the base metal on CuCrZr side (CuCrZr-BM. Precipitates were totally dissolved into Cu matrix in both CuCrZr-NZ and CuNiCrSi-NZ, which led to a sharp decrease in both micro-hardness and tensile strength from BM to NZ. When the CuNiCrSi was located on the AS, the tensile testing results showed the fracture occurred at the CuCrZr-NZ, while the fracture was found at the mixed zone of CuNiCrSi-NZ and CuCrZr-NZ for the other case.

  12. 53Cr NMR study of CuCrO2 multiferroic

    Science.gov (United States)

    Smol'nikov, A. G.; Ogloblichev, V. V.; Verkhovskii, S. V.; Mikhalev, K. N.; Yakubovskii, A. Yu.; Kumagai, K.; Furukawa, Y.; Sadykov, A. F.; Piskunov, Yu. V.; Gerashchenko, A. P.; Barilo, S. N.; Shiryaev, S. V.

    2015-11-01

    The magnetically ordered phase of the CuCrO2 single crystal has been studied by the nuclear magnetic resonance (NMR) method on 53Cr nuclei in the absence of an external magnetic field. The 53Cr NMR spectrum is observed in the frequency range νres = 61-66 MHz. The shape of the spectrum depends on the delay tdel between pulses in the pulse sequence τπ/2- t del-τπ- t del-echo. The spin-spin and spin-lattice relaxation times have been measured. Components of the electric field gradient, hyperfine fields, and the magnetic moment on chromium atoms have been estimated.

  13. Heterogeneity of Cr in Mytilus edulis: Implications for the Cr isotope system as a paleo-redox proxy

    Science.gov (United States)

    Bruggmann, Sylvie; Klaebe, Robert; Frei, Robert

    2017-04-01

    Changes in 53Cr/52Cr (δ53Cr) values recorded by biogenic carbonates are emerging as a proxy for variations in the redox state of the Earth's oceans and atmosphere (e.g. [1], [2]). We investigate the ability of modern carbonate shells (Mytilus edulis) to record the δ53Cr composition of ambient seawater in order to assess their utility as a paleo-redox proxy. Samples of cultivated M. edulis from the Kiel Fjord, Germany, were analyzed for their δ53Cr composition and Cr concentrations [Cr] using TIMS. To disentangle the pathway of Cr into the carbonate shell, a series of step-digestions of their organic outer sheaths (periostraca) and their intra-layer composition were performed. Bulk analyses of specimens with intact periostraca returned 16 to 34 ppb Cr with δ53Cr values ranging from 0.28 to 0.65 ± 0.1 (2SE) and thus fall within the range of surface seawater from the Baltic Sea (0.3 - 0.6 \\permil [3]). Partial removal of periostraca resulted in lower [Cr] (5 to 17 ppb) and δ53Cr values (-0.05 ± 0.15 \\permil). These results show a positive correlation between the amount of organic matter present in a sample and both [Cr] and δ53Cr (n = 9). With nearly complete removal of periostraca, the remaining [Cr] is significantly lower (less than 5 ppb) and can only be accessed by incineration of the carbonate shell. The correlation between [Cr], δ53Cr and the amount of periostracum present in bulk samples indicates that a significant proportion of preserved Cr may be associated with the organic outer sheath. The Cr endmember accessed after incineration is less likely associated with the carbonate crystal lattice. Instead, the δ53Cr values obtained after incineration are similar to those reported from terrestrial rocks, suggesting the influence of detrital particles. Alternatively, Cr may be reduced and subsequently re-oxidized during the mineralization of biogenic carbonates [4]. Seasonal changes in primary productivity in seawater may further influence the shell

  14. Tensile properties of the modified 13Cr martensitic stainless steels

    Energy Technology Data Exchange (ETDEWEB)

    Mabruri, Efendi, E-mail: effe004@lipi.go.id; Anwar, Moch Syaiful, E-mail: moch.syaiful.anwar@lipi.go.id; Prifiharni, Siska, E-mail: siska.prifiharni@lipi.go.id; Romijarso, Toni B.; Adjiantoro, Bintang [Research Center for Metallurgy and Materials, Indonesian Institute of Sciences (LIPI) Kawasan Puspiptek Gd. 470 Serpong, Tangerang Selatan 15314 (Indonesia)

    2016-04-19

    This paper reports the influence of Mo and Ni on the tensile properties of the modified 13Cr martensitic stainless steels in tempered condition. Four steels with different content of Mo and Ni were prepared by induction melting followed by hot forging, quenching and tempering. The experimental results showed that the addition of about 1% and 3% Mo has a beneficial effect to increase both the tensile strength and the elongation of the steels. On the contrary, the addition of about 3% Ni into the martensitic stainless steel results in decreasing of both the tensile strength and the elongation. Among the alloys investigated the 13Cr3Mo type steel exhibited largest tensile strength of 1348 MPa and largest elongation of 12%. The observation on the tensile fractured surfaces by using scanning electron microscope supported these findings.

  15. Tensile properties of the modified 13Cr martensitic stainless steels

    International Nuclear Information System (INIS)

    Mabruri, Efendi; Anwar, Moch Syaiful; Prifiharni, Siska; Romijarso, Toni B.; Adjiantoro, Bintang

    2016-01-01

    This paper reports the influence of Mo and Ni on the tensile properties of the modified 13Cr martensitic stainless steels in tempered condition. Four steels with different content of Mo and Ni were prepared by induction melting followed by hot forging, quenching and tempering. The experimental results showed that the addition of about 1% and 3% Mo has a beneficial effect to increase both the tensile strength and the elongation of the steels. On the contrary, the addition of about 3% Ni into the martensitic stainless steel results in decreasing of both the tensile strength and the elongation. Among the alloys investigated the 13Cr3Mo type steel exhibited largest tensile strength of 1348 MPa and largest elongation of 12%. The observation on the tensile fractured surfaces by using scanning electron microscope supported these findings.

  16. 2nd Gen FeCrAl ODS Alloy Development For Accident-Tolerant Fuel Cladding

    Energy Technology Data Exchange (ETDEWEB)

    Dryepondt, Sebastien N. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Massey, Caleb P. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Edmondson, Philip D. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2016-08-01

    Extensive research at ORNL aims at developing advanced low-Cr high strength FeCrAl alloys for accident tolerant fuel cladding. One task focuses on the fabrication of new low Cr oxide dispersion strengthened (ODS) FeCrAl alloys. The first Fe-12Cr-5Al+Y2O3 (+ ZrO2 or TiO2) ODS alloys exhibited excellent tensile strength up to 800 C and good oxidation resistance in steam up to 1400 C, but very limited plastic deformation at temperature ranging from room to 800 C. To improve alloy ductility, several fabrication parameters were considered. New Fe-10-12Cr-6Al gas-atomized powders containing 0.15 to 0.5wt% Zr were procured and ball milled for 10h, 20h or 40h with Y2O3. The resulting powder was then extruded at temperature ranging from 900 to 1050 C. Decreasing the ball milling time or increasing the extrusion temperature changed the alloy grain size leading to lower strength but enhanced ductility. Small variations of the Cr, Zr, O and N content did not seem to significantly impact the alloy tensile properties, and, overall, the 2nd gen ODS FeCrAl alloys showed significantly better ductility than the 1st gen alloys. Tube fabrication needed for fuel cladding will require cold or warm working associated with softening heat treatments, work was therefore initiated to assess the effect of these fabrications steps on the alloy microstructure and properties. This report has been submitted as fulfillment of milestone M3FT 16OR020202091 titled, Report on 2nd Gen FeCrAl ODS Alloy Development for the Department of Energy Office of Nuclear Energy, Advanced Fuel Campaign of the Fuel Cycle R&D program.

  17. Mobility of dislocations in thermal aged and irradiated Fe-Cr alloys

    International Nuclear Information System (INIS)

    Terentyev, D.; Bonny, G.; Malerba, L.

    2007-01-01

    Full text of publication follows: The choice of the Cr concentration in reduced-activation ferritic/martensitic steels for fusion applications is largely based on the observed minimum radiation-induced embrittlement, in terms of ductile-to-brittle transition temperature shift (ΔDBTT), found around 9%Cr [1]. To date, no physical explanation for the existence of this minimum has been provided. It is known that in high-Cr ferritic alloys the precipitation of the Cr-rich, coherent α' phase occurs for concentrations above 9% Cr, both due to irradiation or thermal ageing at high enough temperature [2]. The formation of a fine dispersion of precipitates can therefore explain the increased embrittlement above this concentration, but it is unclear why the ΔDBTT should increase also for lower Cr concentrations. In addition, it is suspected that under irradiation a' precipitation may be induced also for Cr contents below 9% [3]. At the same time, it is known that below 9% Cr ferritic alloys exhibit a tendency to ordering, i.e. Cr atoms are not distributed as in a random solid solution and try to be as far apart as possible from each other, thereby tending to create a superlattice [4]. In order to cast some light on the effect that these phase changes may have on dislocation motion in the presence of radiation damage, we study at the atomic level the mobility of dislocations in FeCr alloys of different concentrations where Cr is distributed in different fashions (i.e. ordered, clustered or in a random solid solution) and in the presence of radiation damage (e.g. point-defect clusters created by cascades). The microstructure will be obtained by making the system evolve according to the acting thermodynamic driving forces (also in the presence of defects) using Metropolis Monte Carlo techniques. Subsequently, the simulation of the dislocation motion will be performed using large scale molecular dynamics, whereby the corresponding stress-strain curve can be obtained. The

  18. Kinetic stable Cr isotopic fractionation between aqueous Cr(III)-Cl-H2O complexes at 25 °C: Implications for Cr(III) mobility and isotopic variations in modern and ancient natural systems

    Science.gov (United States)

    Babechuk, Michael G.; Kleinhanns, Ilka C.; Reitter, Elmar; Schoenberg, Ronny

    2018-02-01

    The stable Cr isotope fractionation preserved in natural substances has been attributed predominantly to Cr(III)-Cr(VI) redox transformations. However, non-redox reaction pathways (e.g., ligand-promoted dissolution, ligand exchange, adsorption of Cr(III)) are liable to contribute to isotopic fractionation in natural systems given that soluble Cr(III)-ligands have been directly documented or modeled in several marine, continental, and hydrothermal environments. This study isolates the stable Cr isotope fractionation accompanying Cl-H2O ligand exchange during the transformation of three aqueous species in the Cr(III)-Cl-H2O system, [CrCl2(H2O)4]+aq (abr. CrCl2+ or S1), [CrCl(H2O)5]2+aq (abr. CrCl2+ or S2), and [Cr(H2O)6]3+aq (abr. Cr3+ or S3), at low pH (≤2). In dilute HCl (0.01 to 1 M), Cr3+ is the kinetically favoured species and transformation of CrCl2+ to CrCl2+ to Cr3+ via 2 steps of dechlorination/hydrolyzation begins immediately upon dissolution of a Cr(III)-Cl solid. Individual species are separated with cation exchange chromatography at different stages of transformation and inter- and intra-species (across an elution peak of one species) isotopic fractionation of up to 1 and 2‰ (δ53/52Cr), respectively, is documented. Comparison of peak elution characteristics with Cr-Cl-H-O isotopologue mass abundances suggests mass-dependent sorting of isotopologues alone cannot explain intra-species fractionation, supporting a previously published proposal that preferential adsorption of light Cr isotopes on the resin is driven by vibrational energy effects. The transformation of CrCl2+ to CrCl2+ is faster than CrCl2+ to Cr3+ and the rates of both transformations increase with solution pH. Preferential reaction of light Cr(III) isotopes into product species occurs during each transformation, consistent with closed-system, kinetic fractionation during Cl-H2O ligand exchange. Inter-species fractionation is assessed using time-series experiments beginning from the

  19. Reduction of Cr(VI) to Cr(III) using silicon nanowire arrays under visible light irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Fellahi, Ouarda [Institut d' Electronique, de Microélectronique et de Nanotechnologie (IEMN), UMR CNRS 8520, Avenue Poincaré—BP 70478, 59652 Villeneuve d' Ascq Cedex (France); Centre de Recherche en Technologie des Semi-conducteurs pour l' Energétique-CRTSE 02, Bd Frantz Fanon, BP. 140, Alger 7 Merveilles (Algeria); Barras, Alexandre [Institut d' Electronique, de Microélectronique et de Nanotechnologie (IEMN), UMR CNRS 8520, Avenue Poincaré—BP 70478, 59652 Villeneuve d' Ascq Cedex (France); Pan, Guo-Hui [State Key Laboratory of Luminescence and Applications, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 3888 Dong Nanhu Road, Changchun 130033 (China); Coffinier, Yannick [Institut d' Electronique, de Microélectronique et de Nanotechnologie (IEMN), UMR CNRS 8520, Avenue Poincaré—BP 70478, 59652 Villeneuve d' Ascq Cedex (France); Hadjersi, Toufik [Centre de Recherche en Technologie des Semi-conducteurs pour l' Energétique-CRTSE 02, Bd Frantz Fanon, BP. 140, Alger 7 Merveilles (Algeria); Maamache, Mustapha [Laboratoire de Physique Quantique et Systèmes Dynamiques, Département de Physique, Université de Sétif, Sétif 19000 (Algeria); Szunerits, Sabine [Institut d' Electronique, de Microélectronique et de Nanotechnologie (IEMN), UMR CNRS 8520, Avenue Poincaré—BP 70478, 59652 Villeneuve d' Ascq Cedex (France); and others

    2016-03-05

    Highlights: • Cr(VI) reduction to Cr(III) using silicon nanowires decorated with Cu nanoparticles. • The reduction takes place at room temperature and neutral pH under visible light. • The photocatalytic reduction was enhanced by addition of adipic or citric acid. - Abstract: We report an efficient visible light-induced reduction of hexavalent chromium Cr(VI) to trivalent Cr(III) by direct illumination of an aqueous solution of potassium dichromate (K{sub 2}Cr{sub 2}O{sub 7}) in the presence of hydrogenated silicon nanowires (H-SiNWs) or silicon nanowires decorated with copper nanoparticles (Cu NPs-SiNWs) as photocatalyst. The SiNW arrays investigated in this study were prepared by chemical etching of crystalline silicon in HF/AgNO{sub 3} aqueous solution. The Cu NPs were deposited on SiNW arrays via electroless deposition technique. Visible light irradiation of an aqueous solution of K{sub 2}Cr{sub 2}O{sub 7} (10{sup −4} M) in presence of H-SiNWs showed that these substrates were not efficient for Cr(VI) reduction. The reduction efficiency achieved was less than 10% after 120 min irradiation at λ > 420 nm. Addition of organic acids such as citric or adipic acid in the solution accelerated Cr(VI) reduction in a concentration-dependent manner. Interestingly, Cu NPs-SiNWs was found to be a very efficient interface for the reduction of Cr(VI) to Cr(III) in absence of organic acids. Almost a full reduction of Cr(VI) was achieved by direct visible light irradiation for 140 min using this photocatalyst.

  20. Are Mergers a Win-Win Strategic Model? A Content Analysis of Inter-Institutional Collaboration between Higher Education Institutions

    Science.gov (United States)

    Ripoll-Soler, Carlos; de-Miguel-Molina, María

    2014-01-01

    The main goal of this paper, based on a content analysis of the literature about models of inter-institutional collaboration between higher education institutions, is to establish the characteristics that set them apart, contextualize each of these models in terms of the features of the setting in which they are implemented, and ascertain their…