Thermal conductivity of high purity vanadium

International Nuclear Information System (INIS)

Jung, W.D.

1975-01-01

The thermal conductivity, Seebeck coefficient, and electrical resistivity of four high-purity vanadium samples were measured over the temperature range 5 to 300 0 K. The highest purity sample had a resistance ratio (rho 273 /rho 4 . 2 ) of 1524. The highest purity sample had a thermal conductivity maximum of 920 W/mK at 9 0 K and had a thermal conductivity of 35 W/mK at room temperature. At low temperatures, the thermal resistivity was limited by the scattering of electrons by impurities and phonons. The thermal resistivity of vanadium departed from Matthiessen's rule at low temperatures. The electrical resistivity and Seebeck coefficient of high purity vanadium showed no anomalous behavior above 130 0 K. The intrinsic electrical resistivity at low temperatures was due primarily to interband scattering of electrons. The Seebeck coefficient was positive from 10 to 240 0 K and had a maximum which was dependent upon sample purity

Dislocation loops in ultra-high purity Fe(Cr) alloys after 7.2 MeV proton irradiation

Science.gov (United States)

Chen, J.; Duval, F.; Jung, P.; Schäublin, R.; Gao, N.; Barthe, M. F.

2018-05-01

Ultra-high purity Fe(Cr) alloys (from 0 wt% Cr to 14 wt% Cr) were 3D homogeneously irradiated by 0-7.2 MeV protons to 0.3 dpa at nominal temperatures from 270 °C to 500 °C. Microstructural changes were observed by transmission electron microscopy (TEM). The results showed that evolution of dislocation loops depends on the Cr content. Below 300 °C, large ½ a0 loops are dominating. Above 300 °C, a0 loops with a habit plane {100} appear. Loop sizes of both types are more or less the same. At temperatures from 310 °C to 400 °C, a0 loops form clusters with the same {100} habit plane as the one of the loops forming them. This indicates that loops of the same variant start gliding under mutual elastic interaction. At 500 °C, dislocation loops form disc shaped clusters about 1000 nm in diameter and sitting on {111} and/or {100} planes in the pure Fe samples. Based on these observations a quantitative analysis of the dislocation loops configurations and their temperature dependence is made, leading to an understanding of the basic mechanisms of formation of these loops.

Modelling of hydrogen permeability of membranes for high-purity hydrogen production

Science.gov (United States)

Zaika, Yury V.; Rodchenkova, Natalia I.

2017-11-01

High-purity hydrogen is required for clean energy and a variety of chemical technology processes. Different alloys, which may be well-suited for use in gas-separation plants, were investigated by measuring specific hydrogen permeability. One had to estimate the parameters of diffusion and sorption to numerically model the different scenarios and experimental conditions of the material usage (including extreme ones), and identify the limiting factors. This paper presents a nonlinear mathematical model taking into account the dynamics of sorption-desorption processes and reversible capture of diffusing hydrogen by inhomogeneity of the material’s structure, and also modification of the model when the transport rate is high. The results of numerical modelling allow to obtain information about output data sensitivity with respect to variations of the material’s hydrogen permeability parameters. Furthermore, it is possible to analyze the dynamics of concentrations and fluxes that cannot be measured directly. Experimental data for Ta77Nb23 and V85Ni15 alloys were used to test the model. This work is supported by the Russian Foundation for Basic Research (Project No. 15-01-00744).

Effect of initial grain size on dynamic recrystallization in high purity austenitic stainless steels

International Nuclear Information System (INIS)

El Wahabi, M.; Gavard, L.; Montheillet, F.; Cabrera, J.M.; Prado, J.M.

2005-01-01

The influence of initial microstructure on discontinuous dynamic recrystallization (DDRX) has been investigated by using high purity and ultra high purity austenitic stainless steels with various initial grain sizes. After uniaxial compression tests at constant strain rates and various temperatures, the steady state microstructure or the state corresponding to the maximum strain (ε = 1) attained in the test was analyzed by scanning electron microscopy aided with automated electron back scattering diffraction. Recrystallized grain size d rec and twin boundary fraction f TB measurements were carried out. The mechanical behavior was also investigated by comparing experimental stress-strain curves with various initial grain sizes. DDRX kinetics was described by the classical Avrami equation. It was concluded that larger initial grain sizes promoted a delay in the DDRX onset in the two alloys. It was also observed that the softening process progressed faster for smaller initial grain sizes. The effect of initial grain size is larger in the HP material and becomes more pronounced at low temperature

Melt-drop technique for the production of high-purity metal powder

International Nuclear Information System (INIS)

Aldinger, F.; Linck, E.; Claussen, N.

1977-01-01

The production of high-purity powders of metals and alloys such as beryllium, titanium alloys, or superalloys is a problem. Oxidation of these materials cannot be avoided. Oxidation occurs in inert gases and even in reducing atmospheres when any gas impurities are present. Therefore, the powder production of these materials has to be performed either in high vacuum or at least in a static atmosphere of inert gas purified immediately before coming into contact with the disintegrating material. These requirements are very well met by the melt-drop technique presented in this paper, especially for coarse powders which must not necessarily be cold-workable. This is true, for example, for superalloys where high-temperature applications require large grain sizes; or in titanium alloys because the final microstructure will be achieved by a thermomechanical treatment. In the case of beryllium and beryllium alloys, where grain sizes <5 μm are desired, further milling is necessary. But the melt-drop technique offers a simple and clean method directly from the purifying process of vacuum melting. In melt-drop processes a liquid metal flows through a nozzle at the bottom of a crucible or the melt is just poured through a sieve. The theory of disintegration of a liquid jet into droplets, dates back to the 19th century. More recent investigations attempted to produce uniformly sized droplets by applying a capillary wave of given wave length to the jet. But this has been done only with non-metallic materials. Evidence is presented to prove the theory and show that this concept is applicable to the production of metal powders with controlled particle size

High-purity aluminium creep under high hydrostatic pressure

International Nuclear Information System (INIS)

Zajtsev, V.I.; Lyafer, E.I.; Tokij, V.V.

1977-01-01

The effect of the hydrostatic pressure on the rate of steady-state creep of high-purity aluminium was investigated. It is shown that the hydrostatic pressure inhibits the creep. The activation volume of the creep is independent of the direction in the range of (4.7-6.2) kg/mm 2 and of the pressure in the range of (1-7.8000) atm. It is concluded that self-diffusion does not control the creep of high-purity aluminium at room temperature in the investigated stress and pressure range

Production of high purity granular metals: cadmium, zinc, lead

Directory of Open Access Journals (Sweden)

Shcherban A. P.

2017-04-01

Full Text Available Cadmium, zinc and lead are constituent components of many semiconductor compounds. The obtained high purity distillates and ingots are large-size elements, which is not always convenient to use, and thus require additional grinding, which does not always allow maintaining the purity of the original materials. For the growth of semiconductor and scintillation single crystals it is advisable to use "friable" granular high-purity distillates, which can be processed without the risk of contamination. For example, the European low-background experiment LUCIFER required more than 20 kg of high-purity granulated zinc, which was agreed to be supplied by NSC KIPT. This task was then extended to cadmium and lead. Motivated by these tasks, the authors of this paper propose complex processes of deep refining of cadmium, zinc and lead by vacuum distillation. A device producing granules has been developed. The process of granulation of high-purity metals is explored. The purity of produced granules for cadmium and zinc is >99,9999, and >99,9995% for lead granules. To prevent oxidation of metal granules during exposition to air, chemical methods of surface passivation were used. Organic solvent based on dimethylformamide used as a coolant improves the resistance of granules to atmospheric corrosion during the granulation of high purity Cd, Zn and Pb.

Contribution of the low cycle fatigue on ultra high purity Ni-Cr-Fe alloys and on Ni monocrystals to the understanding of the hydrogen role in stress corrosion cracking for the alloys 600 and 690

International Nuclear Information System (INIS)

Renaudot, N.

1999-06-01

We discuss the role of hydrogen in cracking of Ni base alloys used for pressurised water reactor (PWR) primary tubes (alloy 600 and 690). Cracking can be explained by a Stress Corrosion Cracking (SCC) phenomenon. For this purpose, Low cycle fatigue (R = - 1) under cathodic charging at room temperature is conducted to study hydrogen effects on propagation of cracks mechanically initiated by the formation of Persistent Slip Bands (PSB). Low cycle fatigue on Ultra High Purity specimens (Ni, alloy 600 and 690) reveals the very important hydrogen effect on crack propagation rate, whatever the Cr content in the Ni base alloy. If Cr seems to have an effect over-hydrogen penetration in specimens (by a protective film formation), it have no beneficial effect when hydrogen have diffused ahead of a crack tip. Propagation rates (transgranular or intergranular) are highly increased, no matter of the absence of impurities like sulphur. Then, in PWR, the difference in the behaviour of alloy 600 and 690 could be due to a slower microcrack propagation rate for alloy 690. Protective films could play an important role in this difference, which is to study. Low cycle fatigue on Ni single crystals oriented for single slip shows, for the first time on bulk specimen, a macroscopic softening which can be explained. by hydrogen-dislocation interactions. Moreover, a simple quantitative model based on these interactions results in the same softening as the one observed experimentally. These results allow to validate experimentally one of the most important steps in the 'Corrosion Enhanced Plasticity (CEP) model', i.e. the softening ahead of a stress corrosion crack tip by hydrogen dislocation interactions. This is of importance because this model can explain cracking in numerous FCC materials-environment couple. (author)

Batch extractive distillation for high purity methanol

International Nuclear Information System (INIS)

Zhang Weijiang; Ma Sisi

2006-01-01

In this paper, the application in chemical industry and microelectronic industry, market status and the present situation of production of high purity methanol at home and abroad were introduced firstly. Purification of industrial methanol for high purity methanol is feasible in china. Batch extractive distillation is the best separation technique for purification of industrial methanol. Dimethyl sulfoxide was better as an extractant. (authors)

Corrosion of aluminum alloys as a function of alloy composition

International Nuclear Information System (INIS)

Johnson, A.B. Jr.

1969-10-01

A study was initiated which included nineteen aluminum alloys. Tests were conducted in high purity water at 360 0 C and flow tests (approx. 20 ft/sec) in reactor process water at 130 0 C (TF-18 loop tests). High-silicon alloys and AlSi failed completely in the 360 0 C tests. However, coupling of AlSi to 8001 aluminum suppressed the failure. The alloy compositions containing iron and nickel survived tht 360 0 C autoclave exposures. Corrosion rates varied widely as a function of alloy composition, but in directions which were predictable from previous high-temperature autoclave experience. In the TF-18 loop flow tests, corrosion penetrations were similar on all of the alloys and on high-purity aluminum after 105 days. However, certain alloys established relatively low linear corrosion rates: Al-0.9 Ni-0.5 Fe-0.1 Zr, Al-1.0 Ni-0.15 Fe-11.5 Si-0.8 Mg, Al-1.2 Ni-1.8 Fe, and Al-7.0 Ni-4.8 Fe. Electrical polarity measurements between AlSi and 8001 alloys in reactor process water at temperatures up to 150 0 C indicated that AlSi was anodic to 8001 in the static autoclave system above approx. 50 0 C

Variations of color with alloying elements in Pd-free Au-Pt-based high noble dental alloys

International Nuclear Information System (INIS)

Shiraishi, Takanobu; Takuma, Yasuko; Miura, Eri; Fujita, Takeshi; Hisatsune, Kunihiro

2007-01-01

The effects of alloying addition of a small amount of base metals (In, Sn, Fe, Zn) on color variations in Pd-free Au-Pt-based high noble dental alloys were investigated in terms of rectilinear and polar color coordinates. The ternary Au-Pt-X (X = In, Sn, Fe, Zn) and quaternary Au-Pt-In-Y (Y = Sn, Fe, Zn) alloys were prepared from high purity component metals. The amount of alloying base metals, X and Y, were restricted up to 2 at.%. The alloying addition of a small amount of Fe, In, Sn, to a binary Au-10 at.% Pt alloy (referred to as AP10) effectively increased chroma, C *. On the other hand, the addition of Zn to the parent alloy AP10 did not change color coordinates greatly. The increase in chroma in the present Au-Pt-based high noble alloys was attributed to the increase in the slope of spectral reflectance curve at its absorption edge near 515 nm. It was found that the addition of a small amount of Fe to the parent alloy AP10 markedly increased lightness, L *, and the addition of Sn gave a very light tint of red to the parent alloy. Although red-green chromaticity index a * contributed to chroma to some extent, contribution of yellow-blue chromaticity index b * was much greater in determining chroma in this Pd-free Au-Pt-based multi-component alloys. The present results are expected to be valuable in case color is to be taken into account in designing Pd-free Au-Pt-based high noble dental alloys

Variations of color with alloying elements in Pd-free Au-Pt-based high noble dental alloys

Energy Technology Data Exchange (ETDEWEB)

Shiraishi, Takanobu [Department of Dental and Biomedical Materials Science, Unit of Basic Medical Sciences, Graduate School of Biomedical Sciences, Nagasaki University, 1-7-1 Sakamoto, Nagasaki 852-8588 (Japan)]. E-mail: siraisi@nagasaki-u.ac.jp; Takuma, Yasuko [Department of Dental and Biomedical Materials Science, Unit of Basic Medical Sciences, Graduate School of Biomedical Sciences, Nagasaki University, 1-7-1 Sakamoto, Nagasaki 852-8588 (Japan); Miura, Eri [Department of Dental and Biomedical Materials Science, Unit of Basic Medical Sciences, Graduate School of Biomedical Sciences, Nagasaki University, 1-7-1 Sakamoto, Nagasaki 852-8588 (Japan); Fujita, Takeshi [Department of Dental and Biomedical Materials Science, Unit of Basic Medical Sciences, Graduate School of Biomedical Sciences, Nagasaki University, 1-7-1 Sakamoto, Nagasaki 852-8588 (Japan); Hisatsune, Kunihiro [Department of Dental and Biomedical Materials Science, Unit of Basic Medical Sciences, Graduate School of Biomedical Sciences, Nagasaki University, 1-7-1 Sakamoto, Nagasaki 852-8588 (Japan)

2007-06-15

The effects of alloying addition of a small amount of base metals (In, Sn, Fe, Zn) on color variations in Pd-free Au-Pt-based high noble dental alloys were investigated in terms of rectilinear and polar color coordinates. The ternary Au-Pt-X (X = In, Sn, Fe, Zn) and quaternary Au-Pt-In-Y (Y = Sn, Fe, Zn) alloys were prepared from high purity component metals. The amount of alloying base metals, X and Y, were restricted up to 2 at.%. The alloying addition of a small amount of Fe, In, Sn, to a binary Au-10 at.% Pt alloy (referred to as AP10) effectively increased chroma, C *. On the other hand, the addition of Zn to the parent alloy AP10 did not change color coordinates greatly. The increase in chroma in the present Au-Pt-based high noble alloys was attributed to the increase in the slope of spectral reflectance curve at its absorption edge near 515 nm. It was found that the addition of a small amount of Fe to the parent alloy AP10 markedly increased lightness, L *, and the addition of Sn gave a very light tint of red to the parent alloy. Although red-green chromaticity index a * contributed to chroma to some extent, contribution of yellow-blue chromaticity index b * was much greater in determining chroma in this Pd-free Au-Pt-based multi-component alloys. The present results are expected to be valuable in case color is to be taken into account in designing Pd-free Au-Pt-based high noble dental alloys.

High-Purity Glasses Based on Arsenic Chalcogenides

Science.gov (United States)

2001-06-01

Chemical interaction of chalcogenides and some impurities (CS 2, TeO2 ) with the quartz glass at high temperature leads to the thin layers formation...UNCLASSIFIED Defense Technical Information Center Compilation Part Notice ADPO1 1523 TITLE: High-Purity Glasses Based on Arsenic Chalcogenides...Materials Vol. 3, No. 2, June 2001, p. 341 - 349 HIGH-PURITY GLASSES BASED ON ARSENIC CHALCOGENIDES M. F. Churbanov, I. V. Scripachev, G. E. Snopatin, V. S

A study on the influence of trace elements (C, S, B, Al, N) on the hot ductility of the high purity austenitic alloy Fe-Ni 36% (INVAR)

Energy Technology Data Exchange (ETDEWEB)

Simonetta-Perrot, M T

1994-11-01

In order to study the damage mechanisms leading to the ductility decrease of the Invar alloy at 600 C, a high-purity Fe-Ni 36% sample has been doped with trace elements with the purpose of identifying the role of sulfur, sulfur with Al N or B N precipitates and sulfur with boron, on the ductility, the failure modes, the intergranular damage and the plastic deformation mechanisms prior to failure. A new AES segregation quantification method has been used to study the kinetics and thermodynamics of intergranular and surface segregations and determine the relation between sulfur segregation and grain joint fragility. refs., figs., tabs.

High-purity germanium crystal growing

International Nuclear Information System (INIS)

Hansen, W.L.; Haller, E.E.

1982-10-01

The germanium crystals used for the fabrication of nuclear radiation detectors are required to have a purity and crystalline perfection which is unsurpassed by any other solid material. These crystals should not have a net electrically active impurity concentration greater than 10 10 cm - 3 and be essentially free of charge trapping defects. Such perfect crystals of germanium can be grown only because of the highly favorable chemical and physical properties of this element. However, ten years of laboratory scale and commercial experience has still not made the production of such crystals routine. The origin and control of many impurities and electrically active defect complexes is now fairly well understood but regular production is often interrupted for long periods due to the difficulty of achieving the required high purity or to charge trapping in detectors made from crystals seemingly grown under the required conditions. The compromises involved in the selection of zone refining and crystal grower parts and ambients is discussed and the difficulty in controlling the purity of key elements in the process is emphasized. The consequences of growing in a hydrogen ambient are discussed in detail and it is shown how complexes of neutral defects produce electrically active centers

Method of high purity silane preparation

Science.gov (United States)

Tsuo, Y. Simon; Belov, Eugene P.; Gerlivanov, Vadim G.; Zadde, Vitali V.; Kleschevnikova, Solomonida I.; Korneev, Nikolai N.; Lebedev, Eugene N.; Pinov, Akhsarbek B.; Ryabenko, Eugene A.; Strebkov, Dmitry S.; Chernyshev, Eugene A.

2000-01-01

A process for the preparation of high purity silane, suitable for forming thin layer silicon structures in various semiconductor devices and high purity poly- and single crystal silicon for a variety of applications, is provided. Synthesis of high-purity silane starts with a temperature assisted reaction of metallurgical silicon with alcohol in the presence of a catalyst. Alcoxysilanes formed in the silicon-alcohol reaction are separated from other products and purified. Simultaneous reduction and oxidation of alcoxysilanes produces gaseous silane and liquid secondary products, including, active part of a catalyst, tetra-alcoxysilanes, and impurity compounds having silicon-hydrogen bonds. Silane is purified by an impurity adsorption technique. Unreacted alcohol is extracted and returned to the reaction with silicon. Concentrated mixture of alcoxysilanes undergoes simultaneous oxidation and reduction in the presence of a catalyst at the temperature -20.degree. C. to +40.degree. C. during 1 to 50 hours. Tetra-alcoxysilane extracted from liquid products of simultaneous oxidation and reduction reaction is directed to a complete hydrolysis. Complete hydrolysis of tetra-alcoxysilane results in formation of industrial silica sol and alcohol. Alcohol is dehydrated by tetra-alcoxysilane and returned to the reaction with silicon.

Nb-Based Nb-Al-Fe Alloys: Solidification Behavior and High-Temperature Phase Equilibria

Science.gov (United States)

Stein, Frank; Philips, Noah

2018-03-01

High-melting Nb-based alloys hold significant promise for the development of novel high-temperature materials for structural applications. In order to understand the effect of alloying elements Al and Fe, the Nb-rich part of the ternary Nb-Al-Fe system was investigated. A series of Nb-rich ternary alloys were synthesized from high-purity Nb, Al, and Fe metals by arc melting. Solidification paths were identified and the liquidus surface of the Nb corner of the ternary system was established by analysis of the as-melted microstructures and thermal analysis. Complementary analysis of heat-treated samples yielded isothermal sections at 1723 K and 1873 K (1450 °C and 1600 °C).

Inconel type resistive alloys based on ultrahigh purity nickel

International Nuclear Information System (INIS)

Matsarin, K.A.; Matsarin, S.K.

2000-01-01

The new nickel high-ohm alloys (ρ = 1.2-1.4 μOhm · m), containing the W, Al, Mo alloying elements in the quantity, not exceeding their solubility in a solid solution, are developed on the basis of the Inconel-type standard alloy. The optical composition of the alloy was determined by the results of the alloy was determined by the results of the electric resistance measurement and technological effectiveness indices (relative to the pressure and workable metal yield). The following optimal component concentrations were established: 14-17 %Cr; 10-12 %Fe; 0.5-1.0 %Cu; 1.0-1.5 %Mn; 0.1-0.2 %C; 0.4-0.6 %Si; 0.5-3.0 %W; 5-16 %Mo; 0.5-2.0 %Al; the remainder - Ni. The new alloys are recommended as materials for resistive elements of direct-glow cathode nodes of low capacity electron tubes [ru

The effects of vacuum induction melting and electron beam melting techniques on the purity of NiTi shape memory alloys

Energy Technology Data Exchange (ETDEWEB)

Otubo, J. [Instituto Tecnologico de Aeronautica (ITA), 12228-900 S.J. Campos, SP (Brazil) and DEMA-FEM-UNICAMP, 13083-000 Campinas, SP (Brazil)]. E-mail: jotubo@ita.br; Rigo, O.D. [DEMA-FEM-UNICAMP, 13083-000 Campinas, SP (Brazil); Neto, C. Moura [Instituto Tecnologico de Aeronautica (ITA), 12228-900 S.J. Campos, SP (Brazil); Mei, P.R. [DEMA-FEM-UNICAMP, 13083-000 Campinas, SP (Brazil)

2006-11-25

The usual process to produce NiTi shape memory alloys is by vacuum induction melting (VIM) using graphite crucible that contaminates the bath with carbon. The contamination by oxygen comes from residual oxygen inside the melting chamber. A new alternative process to produce NiTi alloys is by electron beam melting (EBM) using water-cooled copper crucible that eliminates the carbon contamination and the oxygen contamination would be minimized due to operation in high vacuum. This work compares the two processes and shows that the carbon contamination is four to ten times lower for EBM compared to VIM products and that the final oxygen content is much more dependent on the starting raw materials. The purity of the final product should be very important mainly in terms of biomedical applications and the contaminations by carbon and oxygen affect the direct and reverse martensitic transformation temperatures.

Fabrication of high quality anodic aluminum oxide (AAO) on low purity aluminum—A comparative study with the AAO produced on high purity aluminum

International Nuclear Information System (INIS)

Michalska-Domańska, Marta; Norek, Małgorzata; Stępniowski, Wojciech J.; Budner, Bogusław

2013-01-01

Highlights: • Nanoporous alumina was fabricated by anodization in sulfuric acid solution with glycol. • The AAO manufacturing on low- and high-purity Al was compared. • The pores size was ranging between 30 and 50 nm. • No difference in the quality of the AAO fabricated on both Al types was observed. • The current vs. anodization time curves were recorded. -- Abstract: In this work the quality, arrangement, composition, and regularity of nanoporous AAO formed on the low-purity (AA1050) and high-purity aluminum during two-step anodization in a mixture of sulfuric acid solution (0.3 M), water and glycol (3:2, v/v), at various voltages (15, 20, 25, 30, 35 V) and at temperature of −1 °C, are investigated. The electrochemical conditions have allowed to obtain pores with the size ranging from 30 to 50 nm, which are much larger than those usually obtained by anodization in a pure sulfuric acid solution (<20 nm). The mechanism of the AAO growth is discussed. It was found that with the increase of applied anodizing voltage a number of incorporated sulfate ions in the aluminum oxide matrix increases, which was connected with the appearance of an unusual area in the current vs. time curves. On the surface of anodizing low- and high-purity aluminum, the formation of hillocks was observed, which was associated with the sulfate ions incorporation. The sulfate ions are replacing the oxygen atom/atoms in the AAO amorphous crystal structure and, consequently, the AAO template swells, the oxide cracks and uplifts causing the formation of hillocks. The same mechanism occurs for both low- and high-purity aluminum. Nanoporous AAO characterized by a very high regularity, not registered previously for low purity aluminum, was obtained. Furthermore, no significant difference in the regularity ratio between the AAO obtained on low- and high-purity aluminum, was observed. The electrochemical conditions applied in this study can be, thus, used for the fabrication of high quality

Effect of Zr Purity and Oxygen Content on the Structure and Mechanical Properties of Melt-Spun and Suction-Cast Cu46Zr42Al7Y5 Alloy

Directory of Open Access Journals (Sweden)

Kozieł T.

2016-06-01

Full Text Available The effect of oxygen content in zirconium on the structure and mechanical properties of the Cu46Zr42Al7Y5 alloy, in the form of melt-spun ribbons and suction-cast rods, was investigated. Two types of Zr, rod and crystal bar of different nominal purities and oxygen contents, were used to synthesize the alloy by arc melting. Rapidly solidified ribbons were produced by melt spinning and their amorphous structures were confirmed by X-ray diffractometry (XRD and differential scanning calorimetry (DSC. Bulk samples in the form of rods were cast using a special water-cooled suction casting unit attached to the arc melting system. XRD and DSC studies proved the amorphous structure of the bulk alloy synthesized from low-oxygen Zr and partial crystallization of the same alloy for high-oxygen Zr. In both bulk samples, uniformly distributed crystalline particles were identified as yttrium oxides. Higher mean compressive strength of amorphous alloy was observed. The hardness of amorphous phase was close to 500 HV1 in both bulk alloys, while the hardness of crystalline dendritic areas, observed in the alloy synthesized from high oxygen Zr, was lower by about 50 HV1.

Surface preparation for high purity alumina ceramics enabling direct brazing in hydrogen atmospheres

Science.gov (United States)

Cadden, Charles H.; Yang, Nancy Yuan Chi; Hosking, Floyd M.

2001-01-01

The present invention relates to a method for preparing the surface of a high purity alumina ceramic or sapphire specimen that enables direct brazing in a hydrogen atmosphere using an active braze alloy. The present invention also relates to a method for directly brazing a high purity alumina ceramic or sapphire specimen to a ceramic or metal member using this method of surface preparation, and to articles produced by this brazing method. The presence of silicon, in the form of a SiO.sub.2 -containing surface layer, can more than double the tensile bond strength in alumina ceramic joints brazed in a hydrogen atmosphere using an active Au-16Ni-0.75 Mo-1.75V filler metal. A thin silicon coating applied by PVD processing can, after air firing, produce a semi-continuous coverage of the alumina surface with a SiO.sub.2 film. Room temperature tensile strength was found to be proportional to the fraction of air fired surface covered by silicon-containing films. Similarly, the ratio of substrate fracture versus interface separation was also related to the amount of surface silicon present prior to brazing. This process can replace the need to perform a "moly-manganese" metallization step.

Formation and transformation of binary intermetallic phases in high purity Al-Fe alloys

International Nuclear Information System (INIS)

Griger, A.; Stefaniay, V.; Kovacs-Csetenyi, E.; Turmezey, T.

1990-01-01

The solid solubility of iron in aluminium is very low (<0.04%), (all compositions are given in w%) therefore most of the iron content appears as intermetallic phases in combination with aluminium and other elements. The amount of iron does not exceed the level of the eutectic concentration in the commercial aluminium alloys, however the non-desired effect of these primary phases of large size must be taken into consideration. In the case of rapid solidification (RS) the eutectic point shifts to higher values of iron content. The eutectic has a very fine structure and the primary phases formed at high cooling rates have also very low particle size. Because of it, for the sake of improvement of the thermo-mechanical properties of the RS aluminium alloys the quantity of iron can be increased up to 8-10%. Above this concentration the favourable properties do not develop while the elongation decreases

Magnesium secondary alloys: Alloy design for magnesium alloys with improved tolerance limits against impurities

Energy Technology Data Exchange (ETDEWEB)

Blawert, C., E-mail: carsten.blawert@gkss.d [GKSS Forschungszentrum Geesthacht GmbH, Max-Planck-Str. 1, 21502 Geesthacht (Germany); Fechner, D.; Hoeche, D.; Heitmann, V.; Dietzel, W.; Kainer, K.U. [GKSS Forschungszentrum Geesthacht GmbH, Max-Planck-Str. 1, 21502 Geesthacht (Germany); Zivanovic, P.; Scharf, C.; Ditze, A.; Groebner, J.; Schmid-Fetzer, R. [TU Clausthal, Institut fuer Metallurgie, Robert-Koch-Str. 42, 38678 Clausthal-Zellerfeld (Germany)

2010-07-15

The development of secondary magnesium alloys requires a completely different concept compared with standard alloys which obtain their corrosion resistance by reducing the levels of impurities below certain alloy and process depending limits. The present approach suitable for Mg-Al based cast and wrought alloys uses a new concept replacing the {beta}-phase by {tau}-phase, which is able to incorporate more impurities while being electro-chemically less detrimental to the matrix. The overall experimental effort correlating composition, microstructure and corrosion resistance was reduced by using thermodynamic calculations to optimise the alloy composition. The outcome is a new, more impurity tolerant alloy class with a composition between the standard AZ and ZC systems having sufficient ductility and corrosion properties comparable to the high purity standard alloys.

Preparation of high-purity cerium nitrate

International Nuclear Information System (INIS)

Avila, Daniela Moraes; Silva Queiroz, Carlos Alberto da; Santos Mucillo, Eliana Navarro dos

1995-01-01

The preparation of high-purity cerium nitrate has been carried out Cerium oxide has been prepared by fractioned precipitation and ionic exchange techniques, using a concentrate with approximately 85% of cerium oxide from NUCLEMON as raw material. Five sequential ion-exchange columns with a retention capacity of 170 g each have been used. The ethylenediamine-tetraacetic acid (EDTA) was used as eluent. The cerium content has been determined by gravimetry and iodometry techniques. The resulting cerium oxide has a purity > 99%. This material was transformed in cerium nitrate to be used as precursor for the preparation of Zirconia-ceria ceramics by the coprecipitation technique. (author)

Low-cost high purity production

Science.gov (United States)

Kapur, V. K.

1978-01-01

Economical process produces high-purity silicon crystals suitable for use in solar cells. Reaction is strongly exothermic and can be initiated at relatively low temperature, making it potentially suitable for development into low-cost commercial process. Important advantages include exothermic character and comparatively low process temperatures. These could lead to significant savings in equipment and energy costs.

Impurity levels and fatigue lives of pseudoelastic NiTi shape memory alloys

International Nuclear Information System (INIS)

Rahim, M.; Frenzel, J.; Frotscher, M.; Pfetzing-Micklich, J.; Steegmüller, R.; Wohlschlögel, M.; Mughrabi, H.; Eggeler, G.

2013-01-01

In the present work we show how different oxygen (O) and carbon (C) levels affect fatigue lives of pseudoelastic NiTi shape memory alloys. We compare three alloys, one with an ultrahigh purity and two which contain the maximum accepted levels of C and O. We use bending rotation fatigue (up to cycle numbers >10 8 ) and scanning electron microscopy (for investigating microstructural details of crack initiation and growth) to study fatigue behavior. High cycle fatigue (HCF) life is governed by the number of cycles required for crack initiation. In the low cycle fatigue (LCF) regime, the high-purity alloy outperforms the materials with higher number densities of carbides and oxides. In the HCF regime, on the other hand, the high-purity and C-containing alloys show higher fatigue lives than the alloy with oxide particles. There is high experimental scatter in the HCF regime where fatigue cracks preferentially nucleate at particle/void assemblies (PVAs) which form during processing. Cyclic crack growth follows the Paris law and does not depend on impurity levels. The results presented in the present work contribute to a better understanding of structural fatigue of pseudoelastic NiTi shape memory alloys

Recovery of high-purity hydrogen from COG

Energy Technology Data Exchange (ETDEWEB)

Tsukiyama, Y

1982-01-01

A general account of the latest trends in the recovery of high-purity hydrogen from coke oven gas (COG), the article being based on both Japanese and overseas literature: 1) Deep-freeze separation: impurities are liquefied and removed. This method make use of the fact that hydrogen is hard to liquefy. 2) The PSA method: high-purity hydrogen is recovered by the adsorption of other constituents at high pressures. This technique makes use of the fact that the adsorption capacity of an adsorbent varies with the partial pressure of the substances being adsorbed. 3) Membrane separation: a permeation separation method that uses a functional polymer separation membrane, and that depends on the fact that hydrogen has a low molecular weight in comparison with the other constituents. (19 refs.) (In Japanese)

Establishing comparability and compatibility in the purity assessment of high purity zinc as demonstrated by the CCQM-P149 intercomparison

Science.gov (United States)

Vogl, Jochen; Kipphardt, Heinrich; Richter, Silke; Bremser, Wolfram; del Rocío Arvizu Torres, María; Manzano, Judith Velina Lara; Buzoianu, Mirella; Hill, Sarah; Petrov, Panayot; Goenaga-Infante, Heidi; Sargent, Mike; Fisicaro, Paola; Labarraque, Guillaume; Zhou, Tao; Turk, Gregory C.; Winchester, Michael; Miura, Tsutomu; Methven, Brad; Sturgeon, Ralph; Jährling, Reinhard; Rienitz, Olaf; Mariassy, Michal; Hankova, Zuzana; Sobina, Egor; Ivanovich Krylov, Anatoly; Anatolievich Kustikov, Yuri; Vladimirovich Smirnov, Vadim

2018-04-01

For the first time, an international comparison was conducted on the determination of the purity of a high purity element. Participants were free to choose any analytical approach appropriate for their institute’s applications and services. The material tested was a high purity zinc, which had earlier been assessed for homogeneity and previously used in CCQM-K72 for the determination of six defined metallic impurities. Either a direct metal assay of the Zn mass fraction was undertaken by EDTA titrimetry, or an indirect approach was used wherein all impurities, or at least the major ones, were determined and their sum subtracted from ideal purity of 100%, or 1 kg kg-1. Impurity assessment techniques included glow discharge mass spectrometry, inductively coupled plasma mass spectrometry and carrier gas hot extraction/combustion analysis. Up to 91 elemental impurities covering metals, non-metals and semi-metals/metalloids were quantified. Due to the lack of internal experience or experimental capabilities, some participants contracted external laboratories for specific analytical tasks, mainly for the analysis of non-metals. The reported purity, expressed as zinc mass fraction in the high purity zinc material, showed excellent agreement for all participants, with a relative standard deviation of 0.011%. The calculated reference value, w(Zn)  =  0.999 873 kg kg-1, was assigned an asymmetric combined uncertainty of  +0.000 025 kg kg-1 and  -0.000 028 kg kg-1. Comparability amongst participating metrology institutes is thus demonstrated for the purity determination of high purity metals which have no particular difficulties with their decomposition/dissolution process when solution-based analytical methods are used, or which do not have specific difficulties when direct analysis approaches are used. Nevertheless, further development is required in terms of uncertainty assessment, quantification of non-metals and the determination of purity

Growth of high purity semiconductor epitaxial layers by liquid phase ...

Indian Academy of Sciences (India)

Unknown

semiconductor materials in high purity form by liquid phase epitaxy (LPE) technique. Various possible sources of impurities in such ... reference to the growth of GaAs layers. The technique of growing very high purity layers ... the inner walls of the gas lines and (e) the containers for storing, handling and cleaning of the mate-.

Relative effects of chromium and niobium on microstructure and mechanical properties as a function of oxygen content in TiAl alloys

International Nuclear Information System (INIS)

Lamirand, M.; Bonnentien, J.-L.; Ferriere, G.; Guerin, S.; Chevalier, J.-P.

2007-01-01

The effects of 2 at.% chromium and niobium on microstructure and mechanical properties of Ti-48Al-x(Cr, Nb) have been investigated for alloys with different oxygen content, ranging from ultra-high purity to doped alloys. Chromium and niobium additions have significant effects for the high purity alloys, whereas for alloys containing oxygen, no significant modification is observed due to the strong stabilizing effect of oxygen on the lamellar microstructure

Thermal and electrical conductivities of high purity tantalum

International Nuclear Information System (INIS)

Archer, S.L.

1978-01-01

The electrical resistivity and thermal conductivity of three high purity tantalum samples have been measured as functions of temperature over a temperature range of 5K to 65K. Sample purities ranged up to a resistivity ratio of 1714. The highest purity sample had a residual resistivity of .76 x 10 -10 OMEGA-m. The intrinsic resistivity varied as T 3 . 9 from 10K to 31K. The thermal conductivity of the purest sample had a maximum of 840 W/mK at 9.8K. The intrinsic thermal resistivity varied as T 2 . 4 from 10K to 35K. At low temperatures electrons were scattered primarily by impurities and by phonons with both interband and intraband transitions observed. The electrical and thermal resistivity is departed from Matthiessen's rule at low temperatures

Development of high purity niobium material for superconducting cavities

International Nuclear Information System (INIS)

Umezawa, Hiroaki; Takeuchi, Koichi; Sakita, Kohei; Suzuki, Takafusa; Saito, Kenji; Noguchi, Shuichi.

1993-01-01

For the superconducting niobium cavities, issues of thermal quench and field emission have to be solved to achieve a high field gradient (>25MV/m) for TESLA (TeV Energy Superconducting Linear Accelerator). In order to overcome the quench, upgrading of thermal conductivity of niobium material at the low temperature is very important. On the reduction of the field emission not only dust particles but also defect, impurity and inhomogeneity should be considered. Therefore development of high purity niobium material is very important to solve these issues. This paper describes the our latest R and D for high purity niobium material. (author)

Production of high purity radiothallium

International Nuclear Information System (INIS)

Lebowitz, E.; Greene, M.W.

1976-01-01

The method of producing high-purity thallium-201 for use as a myocardial scanning agent comprises the steps of irradiating a thallium target with protons to give the reaction 203 Tl(p,3n) 201 Pb, separating in ion exchange columns the lead from the thallium isotopes, permitting the lead to decay, and then purifying the thallium solution and converting the thallium present to thallous form in which it can be used

The Research about Preparation of High Purity Hexachlorodisilane

Science.gov (United States)

Wan, Ye; Zhao, Xiong; Yan, Dazhou; Zhao, Yu; Guo, Shuhu; Wang, Lei; Yang, Dian

2017-12-01

This article demonstrated a technology for producing high purity hexachlorodisilane what is one raw material of Semiconductor industry, which using the method of combination adsorption with rectification, whose material was from polysilicon residues of polysilicon company. This technology could remove most high boiling points chloro-silicane impurities and metal impurities effectively. The purity of Si2Cl6 produced by this technology can be up to 99.9%, the content of metal impurities can be low at 4ppb, which can meet the requirement of industy using completely. The technology extends the routes of Si2Cl6 in localization, having the advantages of simple process, continuous operation, and large capacity and so on.

Analytical monitoring of systems for the production of high-purity, desalinated water

International Nuclear Information System (INIS)

Kunert, I.

1988-01-01

The purity requirements to be met by high-purity water currently push the most sensitive analytical methods to their utmost limits of sensitivity. The required degree of purity of the water at present can only be achieved by application of membrane processes, and pre-purification of the feedwater to a quality corresponding to that of the raw water source. The contribution in hand discusses the analytical monitoring of the raw water treatment plant, the water treatment prior to the treatment by reverse osmosis, monitoring and control of the modules for reverse osmosis, and the monitoring of high-purity water production for the microelectronics industry. (orig./RB) [de

Comparison of the effect of neutron irradiation on high purity vanadium and vanadium oxygen alloys

International Nuclear Information System (INIS)

Arsenault, R.J.; Bressers, J.

1977-01-01

An investigation of the effect of neutron damage on the low temperature deformation characteristics of high purity vanadium (R/sub 300K//R/sub 4.2K/ = 1100) was undertaken for two purposes. One purpose was to determine if reducing the purity interstitial content to a lower level would result in a large difference in the effective stress between irradiated and non-irradiated samples. The present data along with previously obtained data does indicate that the difference increases as the impurity interstitial content is reduced. The explanation of this observation is based on the rapid increase of the non-irradiated yield stress at 77 0 K due to small increases in the oxygen content; however, the increase of the yield stress of the irradiated samples is much less with the same increase in oxygen content. A second purpose of this investigation was to determine the size and density of observable neutron produced defects as a function of oxygen content by transmission electron microscopy, and to relate the changes in density with changes in the yield stress. It was found that the density decreases and the size increases as the oxygen content decreases. There is qualitative agreement between the increase in yield stress at 300 0 K and the observable defect density. However, the change in the yield stress at 77 0 K due to neutron irradiation cannot be related to defect density and size

Characterisation of two AGATA asymmetric high purity germanium capsules

International Nuclear Information System (INIS)

Colosimo, S.J.; Moon, S.; Boston, A.J.; Boston, H.C.; Cresswell, J.R.; Harkness-Brennan, L.; Judson, D.S.; Lazarus, I.H.; Nolan, P.J.; Simpson, J.; Unsworth, C.

2015-01-01

The AGATA spectrometer is an array of highly segmented high purity germanium detectors. The spectrometer uses pulse shape analysis in order to track Compton scattered γ-rays to increase the efficiency of nuclear spectroscopy studies. The characterisation of two high purity germanium detector capsules for AGATA of the same A-type has been performed at the University of Liverpool. This work will examine the uniformity of performance of the two capsules, including a comparison of the resolution and efficiency as well as a study of charge collection. The performance of the capsules shows good agreement, which is essential for the efficient operation of the γ-ray tracking array

Characterisation of two AGATA asymmetric high purity germanium capsules

Energy Technology Data Exchange (ETDEWEB)

Colosimo, S.J., E-mail: sjc@ns.ph.liv.ac.uk [Department of Physics, Oliver Lodge Laboratory, University of Liverpool, Liverpool L69 7ZE (United Kingdom); Moon, S.; Boston, A.J.; Boston, H.C.; Cresswell, J.R.; Harkness-Brennan, L.; Judson, D.S. [Department of Physics, Oliver Lodge Laboratory, University of Liverpool, Liverpool L69 7ZE (United Kingdom); Lazarus, I.H. [STFC Daresbury, Daresbury, Warrington WA4 4AD (United Kingdom); Nolan, P.J. [Department of Physics, Oliver Lodge Laboratory, University of Liverpool, Liverpool L69 7ZE (United Kingdom); Simpson, J. [STFC Daresbury, Daresbury, Warrington WA4 4AD (United Kingdom); Unsworth, C. [Department of Physics, Oliver Lodge Laboratory, University of Liverpool, Liverpool L69 7ZE (United Kingdom)

2015-02-11

The AGATA spectrometer is an array of highly segmented high purity germanium detectors. The spectrometer uses pulse shape analysis in order to track Compton scattered γ-rays to increase the efficiency of nuclear spectroscopy studies. The characterisation of two high purity germanium detector capsules for AGATA of the same A-type has been performed at the University of Liverpool. This work will examine the uniformity of performance of the two capsules, including a comparison of the resolution and efficiency as well as a study of charge collection. The performance of the capsules shows good agreement, which is essential for the efficient operation of the γ-ray tracking array.

Heterogeneous nucleation of entrained eutectic Si in high purity melt spun Al-Si alloys investigated by entrained droplet technique and DSC

International Nuclear Information System (INIS)

Li, J H; Schumacher, P; Albu, M; Hofer, F; Ludwig, T H; Arnberg, L

2016-01-01

Entrained droplet technique and DSC analyses were employed to investigate the influence of trace elements of Sr, Eu and P on the heterogeneous nucleation of entrained eutectic Si in high purity melt spun Al-5wt.% Si alloys. Sr and Eu addition was found to exert negative effects on the nucleation process, while an increased undercooling was observed. This can be attributed to the formation of phosphide compounds having a lower free energy and hence may preferentially form compared to AlP. Only a trace P addition was found to have a profound effect on the nucleation process. The nucleation kinetics is discussed on the basis of the classical nucleation theory and the free growth model, respectively. The estimated AlP patch size was found to be sufficient for the free growth of Si to occur within the droplets, which strongly indicates that the nucleation of Si on an AlP patch or AlP particle is a limiting step for free growth. The maximum nucleation site density within one droplet is directly related to the size distribution of AlP particles or AlP patches for Si nucleation, but is independent of the cooling rates. Although the nucleation conditions were optimized in entrained droplet experiments, the observed mechanisms are also valid at moderate cooling conditions, such as in shape casting. (paper)

High purity in steels as a criterion for materials development

International Nuclear Information System (INIS)

Jacobi, H.

1995-01-01

This summarizing report discusses the materials and application prospects for higher purity in steels, which will make possible further advances in materials behaviour and workability. Improvements in purity and homogeneity permit in particular more rational production of thin foils and wire, one-piece shaping of complicated bodywork components and the drawing, wall-ironing and flanging of two-piece beverage cans. Welded designs in plant and mechanical engineering can be fabricated with less effort and less weight. Difficult component geometries and shaping processes can be more easily mastered. Steels with optimized fracture toughness can be exposed to more extreme loads at even lower temperatures: applications worthy of mention include offshore engineering and large-diameter linepipes for use in arctic regions and at great underwater depths. Liquefied-gas transport vessels can be made more resistant to brittle rupture. The bending fatigue strength and service-life of valve-spring and rolling-bearing steels can be significantly increased. High-purity surfaces on piston rods and cylinders guarantee reliability in hydraulic systems, and high-purity calendering rolls permit defect-free embossing of paper surfaces. (orig.)

Growth and characterization of high-purity SiC single crystals

Science.gov (United States)

Augustine, G.; Balakrishna, V.; Brandt, C. D.

2000-04-01

High-purity SiC single crystals with diameter up to 50 mm have been grown by the physical vapor transport method. Finite element analysis was used for thermal modeling of the crystal growth cavity in order to reduce stress in the grown crystal. Crystals are grown in high-purity growth ambient using purified graphite furniture and high-purity SiC sublimation sources. Undoped crystals up to 50 mm in diameter with micropipe density less than 100 cm -2 have been grown using this method. These undoped crystals exhibit resistivities in the 10 3 Ω cm range and are p-type due to the presence of residual acceptor impurities, mainly boron. Semi-insulating SiC material is obtained by doping the crystal with vanadium. Vanadium has a deep donor level located near the middle of the band gap, which compensates the residual acceptor resulting in semi-insulating behavior.

Dynamical recrystallization of high purity austenitic stainless steels

International Nuclear Information System (INIS)

Gavard, L.

2001-01-01

The aim of this work is to optimize the performance of structural materials. The elementary mechanisms (strain hardening and dynamical regeneration, germination and growth of new grains) occurring during the hot working of metals and low pile defect energy alloys have been studied for austenitic stainless steels. In particular, the influence of the main experimental parameters (temperature, deformation velocity, initial grain size, impurities amount, deformation way) on the process of discontinuous dynamical recrystallization has been studied. Alloys with composition equal to those of the industrial stainless steel-304L have been fabricated from ultra-pure iron, chromium and nickel. Tests carried out in hot compression and torsion in order to cover a wide range of deformations, deformation velocities and temperatures for two very different deformation ways have allowed to determine the rheological characteristics (sensitivity to the deformation velocity, apparent activation energy) of materials as well as to characterize their microstructural deformations by optical metallography and electron back-scattered diffraction. The influence of the initial grain size and the influence of the purity of the material on the dynamical recrystallization kinetics have been determined. An analytical model for the determination of the apparent mobility of grain boundaries, a semi-analytical model for the dynamical recrystallization and at last an analytical model for the stationary state of dynamical recrystallization are proposed as well as a new criteria for the transition between the refinement state and the state of grain growth. (O.M.)

Confined recrystallization of high-purity aluminium during accumulative roll bonding of aluminium laminates

International Nuclear Information System (INIS)

Chekhonin, Paul; Beausir, Benoît; Scharnweber, Juliane; Oertel, Carl-Georg; Hausöl, Tina; Höppel, Heinz Werner; Brokmeier, Heinz-Günter; Skrotzki, Werner

2012-01-01

Aluminium laminates consisting of high-purity aluminium and commercially pure aluminium have been produced by accumulative roll bonding (ARB) at ambient temperature for up to 10 cycles. To study the microstructure and texture development of the high-purity aluminium layers with regard to the shrinking layer thickness during ARB, microstructure and texture investigations were carried out by electron backscatter diffraction and neutron and X-ray diffraction, respectively. While the commercially pure aluminium layers develop an ultrafine-grained microstructure, partial discontinuous recrystallization occurs in the high-purity layers. The texture of the high-purity layers mainly consists of Cube and “Tilted Cube” (tilted with respect to the transverse direction) components. The experimental results are discussed with respect to confined recrystallization in the ARB aluminium laminates.

Perspectives of data-driven LPV modeling of high-purity distillation columns

NARCIS (Netherlands)

Bachnas, A.A.; Toth, R.; Mesbah, A.; Ludlage, J.H.A.

2013-01-01

Abstract—This paper investigates data-driven, Linear- Parameter-Varying (LPV) modeling of a high-purity distillation column. Two LPV modeling approaches are studied: a local approach, corresponding to the interpolation of Linear Time- Invariant (LTI) models identified at steady-state purity levels,

Activation analysis of high purity metals and application to study on physical properties

International Nuclear Information System (INIS)

Ueda, Yoshitake; Hashimoto, Eiji; Matsushita, Rokuji.

1994-01-01

In order to determine the true characteristics of matters, the utmost reduction of impurities is indispensable. By the heightening of the purity of aluminum, that of 99.9999% purity has been obtained, but efforts have been exerted to further heighten the purity. For the purpose, it is important to know the behavior of trace impurities during refining, and the quantitative research by neutron activation analysis for various impurities has been carried out. The research on the electron condition of trace impurity atoms in refined aluminum is also important. The band refining of high purity aluminum is explained. By repeating the refining 10 times, the sample of RRR exceeding 30000 was obtained. The impurities contributing to the resistivity are Sc, Ti, V and Cr. Based on the results, the heightening of aluminum purity was attempted by devising the new procedure. As for the electric properties of solute elements in high purity metals, those of transition elements and rare earth elements in aluminum are reported. As the result of measuring the remaining resistance, the sample having the RRR exceeding 45000 after the correction for size effect was done has been obtained. At present, the efforts toward further high purity are continued. (K.I.)

Nearly Blinking-Free, High-Purity Single-Photon Emission by Colloidal InP/ZnSe Quantum Dots.

Science.gov (United States)

Chandrasekaran, Vigneshwaran; Tessier, Mickaël D; Dupont, Dorian; Geiregat, Pieter; Hens, Zeger; Brainis, Edouard

2017-10-11

Colloidal core/shell InP/ZnSe quantum dots (QDs), recently produced using an improved synthesis method, have a great potential in life-science applications as well as in integrated quantum photonics and quantum information processing as single-photon emitters. Single-particle spectroscopy of 10 nm QDs with 3.2 nm cores reveals strong photon antibunching attributed to fast (70 ps) Auger recombination of multiple excitons. The QDs exhibit very good photostability under strong optical excitation. We demonstrate that the antibunching is preserved when the QDs are excited above the saturation intensity of the fundamental-exciton transition. This result paves the way toward their usage as high-purity on-demand single-photon emitters at room temperature. Unconventionally, despite the strong Auger blockade mechanism, InP/ZnSe QDs also display very little luminescence intermittency ("blinking"), with a simple on/off blinking pattern. The analysis of single-particle luminescence statistics places these InP/ZnSe QDs in the class of nearly blinking-free QDs, with emission stability comparable to state-of-the-art thick-shell and alloyed-interface CdSe/CdS, but with improved single-photon purity.

High frequency ohmic loss of beryllium and its alloy with aluminium

International Nuclear Information System (INIS)

Prentslau, N.N.

1999-01-01

The surface resistance of Be of different purity and its alloy with Al (50%Be-50%Al) is investigated at temperatures ranged from 4,2 to 300 K in the 0-10 10 Hz frequency region. It is shown that within the temperature range (in the vicinity of 77 K) where beryllium is a de hyper conductor. Its surface resistance and the surface resistance of the alloy are minimum compared to that of other metals, in particular, of aluminium. The temperature dependence of the surface resistance of Be and its alloys is well described by the classical formulae of electrodynamics

The solubility of hydrogen and deuterium in alloyed, unalloyed and impure plutonium metal

Energy Technology Data Exchange (ETDEWEB)

Richmond, Scott [Los Alamos National Laboratory; Bridgewater, Jon S [Los Alamos National Laboratory; Ward, John W [Los Alamos National Laboratory; Allen, Thomas A [Los Alamos National Laboratory

2009-01-01

Pressure-Composition-Temperature (PCT) data are presented for the plutonium-hydrogen (Pu-H) and plutonium-deuterium (Pu-D) systems in the solubility region up to terminal solubility (precipitation of PuH{sub 2}). The heats of solution for PuH{sub s} and PuD{sub s} are determined from PCT data in the ranges 350-625 C for gallium alloyed Pu and 400-575 C for unalloyed Pu. The solubility of high purity plutonium alloyed with 2 at.% gallium is compared to high purity unalloyed plutonium. Significant differences are found in hydrogen solubility for unalloyed Pu versus gallium alloyed Pu. Differences in hydrogen solubility due to an apparent phase change are observable in the alloyed and unalloyed solubilities. The effect of iron impurities on Pu-Ga alloyed Pu is shown via hydrogen solubility data as preventing complete homogenization.

The solubility of hydrogen and deuterium in alloyed, unalloyed and impure plutonium metal

International Nuclear Information System (INIS)

Richmond, S; Bridgewater, J S; Ward, J W; Allen, T H

2010-01-01

Pressure-Composition-Temperature (PCT) data are presented for the plutonium-hydrogen (Pu-H) and plutonium-deuterium (Pu-D) systems in the solubility region up to terminal solubility (precipitation of PuH 2 ). The heats of solution for PuH S and PuD S are determined from PCT data in the ranges 350-625 deg. C for gallium alloyed Pu and 400-575 deg. C for unalloyed Pu. The solubility of high purity plutonium alloyed with 2 at.% gallium is compared to high purity unalloyed plutonium. Significant differences are found in hydrogen solubility for unalloyed Pu versus gallium alloyed Pu. Differences in hydrogen solubility due to an apparent phase change are observable in the alloyed and unalloyed solubilities. The effect of iron impurities on Pu-Ga alloyed Pu is shown via hydrogen solubility data as preventing complete homogenization.

Phase constitution and corrosion resistance of Al–Co alloys

Energy Technology Data Exchange (ETDEWEB)

Palcut, Marián, E-mail: marian.palcut@gmail.com; Priputen, Pavol; Šalgó, Kristián; Janovec, Jozef

2015-09-15

Al–24Co, Al–25Co, Al–26Co, Al–27Co and Al–28Co alloys (composition in atomic percent) were prepared by arc-melting in high purity argon. Each alloy was found to consist of several microstructure constituents. Precipitation sequences of different intermetallic compounds were described based on a previously published Al–Co phase diagram and non-equilibrium processes taking place during casting. Electrochemical corrosion was investigated by potentiodynamic polarization in aqueous NaCl solution at room temperature. A large amount of pitting is observed, with some of the phases being preferentially corroded. The nobility of Al–Co intermetallic compounds is discussed in terms of chemical composition and crystal structure. Conclusions towards the alloy stability are provided. - Highlights: • Al–24Co to Al–28Co alloys were prepared by arc-melting in high purity argon. • Precipitation sequences of different intermetallic compounds have been observed. • Anodic alloy dissolution takes place by galvanic mechanism. • Nobility of Al–Co intermetallic compounds increases with increasing Co concentration.

Corrosion in Supercritical carbon Dioxide: Materials, Environmental Purity, Surface Treatments, and Flow Issues

Energy Technology Data Exchange (ETDEWEB)

Sridharan, Kumar; Anderson, Mark

2013-12-10

The supercritical CO{sub 2} Brayton cycle is gaining importance for power conversion in the Generation IV fast reactor system because of its high conversion efficiencies. When used in conjunction with a sodium fast reactor, the supercritical CO{sub 2} cycle offers additional safety advantages by eliminating potential sodium-water interactions that may occur in a steam cycle. In power conversion systems for Generation IV fast reactors, supercritical CO{sub 2} temperatures could be in the range of 30°C to 650°C, depending on the specific component in the system. Materials corrosion primarily at high temperatures will be an important issue. Therefore, the corrosion performance limits for materials at various temperatures must be established. The proposed research will have four objectives centered on addressing corrosion issues in a high-temperature supercritical CO{sub 2} environment: Task 1: Evaluation of corrosion performance of candidate alloys in high-purity supercritical CO{sub 2}: The following alloys will be tested: Ferritic-martensitic Steels NF616 and HCM12A, austenitic alloys Incoloy 800H and 347 stainless steel, and two advanced concept alloys, AFA (alumina forming austenitic) steel and MA754. Supercritical CO{sub 2} testing will be performed at 450°C, 550°C, and 650°C at a pressure of 20 MPa, in a test facility that is already in place at the proposing university. High purity CO{sub 2} (99.9998%) will be used for these tests. Task 2: Investigation of the effects of CO, H{sub 2}O, and O{sub 2} impurities in supercritical CO{sub 2} on corrosion: Impurities that will inevitably present in the CO{sub 2} will play a critical role in dictating the extent of corrosion and corrosion mechanisms. These effects must be understood to identify the level of CO{sub 2} chemistry control needed to maintain sufficient levels of purity to manage corrosion. The individual effects of important impurities CO, H{sub 2}O, and O{sub 2} will be investigated by adding them

The flow stress of high-purity refractory body-centred cubic metals and its modification by atomic defects

International Nuclear Information System (INIS)

Seeger, A.

1995-01-01

The strong temperature and strain-rate dependence of the flow stress of high-purity refractory body-centred cubic metals has been shown to be an intrinsic property and is usually ascribed to a high Peierls barrier of a o left angle 111 right angle /2 screw dislocations. These barriers are overcome by the formation of kink pairs on the screw dislocations. The paper reports on recent, very complete flow-stress data on ultra-high purity Mo crystals obtained by two different experimental techniques and covering the temperature range 4 K to 460 K. The results are in accord with earlier work of Brunner and Diehl on α-Fe, who showed that below the so-called knee temperature, T K , three regimes in the temperature variation of the flow-stress should be distinguished. Two of them are fully accounted for by the same glide mechanism, namely elementary glide steps on {211} planes. The so-called upper bend separating these two regimes in an inherent feature of the theory of kink-pair formation and does not indicate a change in the glide mechanism. There is, however, strong evidence that the so-called lower bend, separating the range of {211} elementary glide steps from the low-temperature flow-stress regime, is due to a change in the glide mechanism. It is argued that at the lower bend the screw-dislocation cores undergo a ''first-order phase transition'' from a low-temperature configuration that allows glide of a given screw dislocation on any of its three {110} glide planes to a high-temperature configuration that can glide only on one definite {211} plane. Between T K and the lower-bend temperature, T, bcc metals may show the unique phenomena of alloy and irradiation softening. With regard to the latter phenomenon, Brunner and Diehl distinguish between ''primary'' and ''secondary'' softening. It is shown that alloy softening and the ''secondary irradiation softening'' of bcc metals may be explained by an ''overheating'' of the phase transition in the dislocation core. (orig./WL)

Composition analysis of Ta-W alloy using NAA and EDXRF techniques

International Nuclear Information System (INIS)

Swain, K.K.; Remya Devi, P.S.; Chavan, Trupti A.; Verma, R.; Reddy, A.V.R.

2015-01-01

Tantalum-Tungsten (Ta-W) alloy is a high strength alloy and is used in corrosion resistant chemical process equipment's including heat exchangers, condensers, heating and cooling coils and reaction vessels. Ta-W alloy is also used as ion extraction plate during laser Isotope separation of uranium and hence the composition is critical for its optimal application. The composition of the alloy was determined by neutron activation analysis (NAA) and energy dispersive X-ray fluorescence spectrometry (EDXRF) techniques. Ta-W alloy sample was received from Nuclear Fuel Complex (NFC), Hyderabad. For NAA, samples (50 - 500 mg) were sealed in polyethylene. High purity Ta foil (30 - 40 mg) and W foil (10 - 20 mg) were packed and used as comparators. Samples and standards were irradiated in the graphite reflector position of Advanced Heavy Water Reactor Critical Facility (AHWR CF) reactor, BARC, Mumbai for 4 hours. After suitable decay period, radioactivity assay was carried out using a 45% relative efficiency high purity germanium (HPGe) detector coupled to MCA with 8 k conversion gain

Zone refining high-purity germanium

International Nuclear Information System (INIS)

Hubbard, G.S.; Haller, E.E.; Hansen, W.L.

1977-10-01

The effects of various parameters on germanium purification by zone refining have been examined. These parameters include the germanium container and container coatings, ambient gas and other operating conditions. Four methods of refining are presented which reproducibly yield 3.5 kg germanium ingots from which high purity (vertical barN/sub A/ - N/sub D/vertical bar less than or equal to2 x 10 10 cm -3 ) single crystals can be grown. A qualitative model involving binary and ternary complexes of Si, O, B, and Al is shown to account for the behavior of impurities at these low concentrations

Preserving high-purity 233U

International Nuclear Information System (INIS)

Krichinsky, Alan; Giaquinto, Joe; Canaan, Doug

2016-01-01

The MARC X Conference hosted a workshop for the scientific community to communicate needs for high-purity 233 U and its by-products in order to preserve critical items otherwise slated for downblending and disposal. Currently, only small portions of the U.S. holdings of separated 233 U are being preserved. However, many additional kilograms of 233 U (>97 % pure) still are destined to be disposed, and it is unlikely that this material will ever be replaced due to a lack of operating production capability. Summaries of information conveyed at the workshop and feedback obtained from the scientific community are presented herein. (author)

Biodegradability engineering of biodegradable Mg alloys: Tailoring the electrochemical properties and microstructure of constituent phases

Science.gov (United States)

Cha, Pil-Ryung; Han, Hyung-Seop; Yang, Gui-Fu; Kim, Yu-Chan; Hong, Ki-Ha; Lee, Seung-Cheol; Jung, Jae-Young; Ahn, Jae-Pyeong; Kim, Young-Yul; Cho, Sung-Youn; Byun, Ji Young; Lee, Kang-Sik; Yang, Seok-Jo; Seok, Hyun-Kwang

2013-01-01

Crystalline Mg-based alloys with a distinct reduction in hydrogen evolution were prepared through both electrochemical and microstructural engineering of the constituent phases. The addition of Zn to Mg-Ca alloy modified the corrosion potentials of two constituent phases (Mg + Mg2Ca), which prevented the formation of a galvanic circuit and achieved a comparable corrosion rate to high purity Mg. Furthermore, effective grain refinement induced by the extrusion allowed the achievement of much lower corrosion rate than high purity Mg. Animal studies confirmed the large reduction in hydrogen evolution and revealed good tissue compatibility with increased bone deposition around the newly developed Mg alloy implants. Thus, high strength Mg-Ca-Zn alloys with medically acceptable corrosion rate were developed and showed great potential for use in a new generation of biodegradable implants. PMID:23917705

All electrochemical fabrication of a bilayer membrane composed of nanotubular photocatalyst and palladium toward high-purity hydrogen production

Energy Technology Data Exchange (ETDEWEB)

Hattori, Masashi [Institute for Materials Chemistry and Engineering, Kyushu University, Kasuga 816-8580 (Japan); Noda, Kei, E-mail: nodakei@elec.keio.ac.jp [Department of Electronics and Electrical Engineering, Keio University, Hiyoshi, Yokohama 223-8522 (Japan)

2015-12-01

Graphical abstract: - Highlights: • A bilayer membrane composed of TiO{sub 2} nanotube array and palladium was fabricated. • The TiO{sub 2}/Pd bilayer membrane was prepared with an all-electrochemical process. • The membrane consists of pure Pd and anatase TiO{sub 2} nanotubes with no alloy formation. • Photocatalytic H{sub 2} production and concomitant separation were demonstrated. • High-purity H{sub 2} production rate and apparent quantum yield were evaluated. - Abstract: We developed an all-electrochemical technique for fabricating a bilayer structure of a titanium dioxide (TiO{sub 2}) nanotube array (TNA) and a palladium film (TNA/Pd membrane), which works for photocatalytic high-purity hydrogen production. Electroless plating was used for depositing the Pd film on the TNA surface prepared by anodizing a titanium foil. A 3-μm-thick TNA/Pd membrane without any pinholes in a 1.5-cm-diameter area was fabricated by transferring a 1-μm-thick TNA onto an electroless-plated 2-μm-thick Pd film with a mechanical peel-off process. This ultrathin membrane with sufficient mechanical robustness showed photocatalytic H{sub 2} production via methanol reforming under ultraviolet illumination on the TNA side, immediately followed by the purification of the generated H{sub 2} gas through the Pd layer. The hydrogen production rate and the apparent quantum yield for high-purity H{sub 2} production from methanol/water mixture with the TNA/Pd membrane were also examined. This work suggests that palladium electroless plating is more suitable and practical for preparing a well-organized TNA/Pd heterointerface than palladium sputter deposition.

Pressure-assisted sintering of high purity barium titanate

NARCIS (Netherlands)

van den Cruijsem, S.; Varst, van der P.G.T.; With, de G.; Bortzmeyer, D.; Boussuge, M.; Chartier, Th.; Hausonne, J.M.; Mocellin, A.; Rousset, A.; Thevenot, F.

1997-01-01

The dielectric behaviour of High Purity Barium titanate (HPB) ceramics is strongly dependent on the grain size and porosity. For applications, control of grain size and porosity is required. Pressure-assisted sintering techniques at relatively low temperatures meet these requirements. In this study,

Surface passivation of high purity granular metals: zinc, cadmium, lead

Directory of Open Access Journals (Sweden)

Pirozhenko L. A.

2017-10-01

Full Text Available For the high purity metals (99.9999%, such as zinc, cadmium, and lead, which are widely used as initial components in growing semiconductor and scintillation crystals (CdTe, CdZnTe, ZnSe, (Cd, Zn, Pb WO4, (Cd, Zn, Pb MoO4 et al., it is very important to ensure reliable protection of the surface from oxidation and adsorption of impurities from the atmosphere. The specific features of surface passivation of high purity cadmium, lead and zinc are not sufficiently studied and require specific methodologies for further studies. The use of organic solutions in the schemes of chemical passivation of the investigated metals avoids hydrolysis of the obtained protective films. The use of organic solvents with pure cation and anion composition as the washing liquid prevents chemisorption of ions present in the conventionally used distilled water. This keeps the original purity of the granular metals. Novel compositions of etchants and etching scheme providing simultaneous polishing and passivation of high purity granular Zn, Cd and Pb are developed. Chemical passivation allows storing metals in the normal atmospheric conditions for more than half a year for Zn and Cd and up to 30 days for Pb without changing the state of the surface. The use of the glycerol-DMF solution in the processes for obtaining Pb granules provides self-passivation of metal surfaces and eliminates the additional chemical processing while maintaining the quality of corrosion protection.

Event timing in high purity germanium coaxial detectors

International Nuclear Information System (INIS)

El-Ibiary, M.Y.

1979-08-01

The timing of gamma ray radiation in systems using high purity coaxial germanium detectors is analyzed and compared to that of systems using Ge(Li) detectors. The analysis takes into account the effect of the residual impurities on the electric field distribution, and hence on the rate of rise of the electrical pulses delivered to the timing module. Conditions under which the electric field distribution could lead to an improvement in timing performance, are identified. The results of the analysis confirm the experimental results published elsewhere and when compared with those for Ge(Li) detectors, which usually operate under conditions of charge carrier velocity saturation, confirm that high purity germanium detectors need not have inferior timing characteristics. A chart is given to provide a quantitative basis on which the trade off between the radius of the detector and its time resolution may be made

Preparation and characterization of sintered Mo-Re alloys

International Nuclear Information System (INIS)

Morito, F.

1993-01-01

By the method of powder metallurgy, we have tried to fabricate Mo-Re alloys, which were electron beam weldable. Severe quality control was carried out during the whole fabrication process focused to reducing oxygen contamination. It is inevitable that the starting raw powders of Mo and Re were both high purity with 99.99 mass% up. Moreover, high vacuum sintering was performed before final sintering with high-purity hydrogen gas. As a result, we obtained electron beam weldable Mo-Re alloys, the total oxygen content of which was about 10 mass ppm or less, respectively. Several specimens were melted by electron beam welding (EBW) method. It was found that EBW gives an easy and effective survey to examine the weldability and the quality of the materials. Fracture surfaces examined by AES exhibited very low content of oxygen, carbon and nitrogen or that less than detectability limit. In conclusion, we have succeeded to obtain defect-free welds of sintered Mo-Re alloys. Furthermore it was found that Mo-Re alloys showed excellent potentialities not only in mechanical properties at low temperature but also in the respects of microstructure. (orig.)

Radiation corrosion in aluminum alloy bellows

International Nuclear Information System (INIS)

Konno, Osamu

1987-01-01

Testing was carried out in which materials for vacuum devices (Al, Ti, Cu, SUS) are exposed to electron beams (50 MeV, average current 80 μA) to determine the changes in the quantity, partial pressure and composition of the gases released from the materials. The test appratus used are made of Al alloys alone. During the test, vacuum leak is found in the Al alloy bellows used in the drive device. The leak is found to result from corrosion caused by water. The surface structure is analyzed by SEM, EPMA, ESCA and IMA. It is confirmed that the Al alloy used as material for the bellows if highly resistant to corrosion. It is concluded that it is necessary to use high purity cooling water to prevent the cooling water from causing corrosion. It has been reported that high purity aluminum is very high in resistance to corrosion. Based on these measurements and considerations, it is suggested that when aluminum is to be used as material for vacuum devices in an accelerator, it is required to provide protection film on its surface to prevent corrosion or to use cooling water pipes cladded with pure aluminum and an aluminum alloy. In addition, the temperature of the cooling water should be set after adequately considering the environmental conditions in the room. (Nogami, K.)

Biocompatibility of dental alloys

Energy Technology Data Exchange (ETDEWEB)

Braemer, W. [Heraeus Kulzer GmbH and Co. KG, Hanau (Germany)

2001-10-01

Modern dental alloys have been used for 50 years to produce prosthetic dental restorations. Generally, the crowns and frames of a prosthesis are prepared in dental alloys, and then veneered by feldspar ceramics or composites. In use, the alloys are exposed to the corrosive influence of saliva and bacteria. Metallic dental materials can be classified as precious and non-precious alloys. Precious alloys consist of gold, platinum, and small amounts of non-precious components such as copper, tin, or zinc. The non-precious alloys are based on either nickel or cobalt, alloyed with chrome, molybdenum, manganese, etc. Titanium is used as Grade 2 quality for dental purposes. As well as the dental casting alloys, high purity electroplated gold (99.8 wt.-%) is used in dental technology. This review discusses the corrosion behavior of metallic dental materials with saliva in ''in vitro'' tests and the influence of alloy components on bacteria (Lactobacillus casei and Streptococcus mutans). The test results show that alloys with high gold content, cobalt-based alloys, titanium, and electroplated gold are suitable for use as dental materials. (orig.)

Evaluation of purity with its uncertainty value in high purity lead stick by conventional and electro-gravimetric methods.

Science.gov (United States)

Singh, Nahar; Singh, Niranjan; Tripathy, S Swarupa; Soni, Daya; Singh, Khem; Gupta, Prabhat K

2013-06-26

A conventional gravimetry and electro-gravimetry study has been carried out for the precise and accurate purity determination of lead (Pb) in high purity lead stick and for preparation of reference standard. Reference materials are standards containing a known amount of an analyte and provide a reference value to determine unknown concentrations or to calibrate analytical instruments. A stock solution of approximate 2 kg has been prepared after dissolving approximate 2 g of Pb stick in 5% ultra pure nitric acid. From the stock solution five replicates of approximate 50 g have been taken for determination of purity by each method. The Pb has been determined as PbSO4 by conventional gravimetry, as PbO2 by electro gravimetry. The percentage purity of the metallic Pb was calculated accordingly from PbSO4 and PbO2. On the basis of experimental observations it has been concluded that by conventional gravimetry and electro-gravimetry the purity of Pb was found to be 99.98 ± 0.24 and 99.97 ± 0.27 g/100 g and on the basis of Pb purity the concentration of reference standard solutions were found to be 1000.88 ± 2.44 and 1000.81 ± 2.68 mg kg-1 respectively with 95% confidence level (k = 2). The uncertainty evaluation has also been carried out in Pb determination following EURACHEM/GUM guidelines. The final analytical results quantifying uncertainty fulfills this requirement and gives a measure of the confidence level of the concerned laboratory. Gravimetry is the most reliable technique in comparison to titremetry and instrumental method and the results of gravimetry are directly traceable to SI unit. Gravimetric analysis, if methods are followed carefully, provides for exceedingly precise analysis. In classical gravimetry the major uncertainties are due to repeatability but in electro-gravimetry several other factors also affect the final results.

The High Strain Rate Deformation Behavior of High Purity Magnesium and AZ31B Magnesium Alloy

Science.gov (United States)

Livescu, Veronica; Cady, Carl M.; Cerreta, Ellen K.; Henrie, Benjamin L.; Gray, George T.

The deformation in compression of pure magnesium and AZ31B magnesium alloy, both with a strong basal pole texture, has been investigated as a function of temperature, strain rate, and specimen orientation. The mechanical response of both metals is highly dependent upon the orientation of loading direction with respect to the basal pole. Specimens compressed along the basal pole direction have a high sensitivity to strain rate and temperature and display a concave down work hardening behavior. Specimens loaded perpendicularly to the basal pole have a yield stress that is relatively insensitive to strain rate and temperature and a work hardening behavior that is parabolic and then linearly upwards. Both specimen orientations display a mechanical response that is sensitive to temperature and strain rate. Post mortem characterization of the pure magnesium was conducted on a subset of specimens to determine the microstructural and textural evolution during deformation and these results are correlated with the observed work hardening behavior and strain rate sensitivities were calculated.

Synthesis of High Purity Nonsymmetric Dialkylphosphinic Acid Extractants.

Science.gov (United States)

Wang, Junlian; Xie, Meiying; Liu, Xinyu; Xu, Shengming

2017-10-19

We present the synthesis of (2,3-dimethylbutyl)(2,4,4'-trimethylpentyl)phosphinic acid as an example to demonstrate a method for the synthesis of high purity nonsymmetric dialkylphosphinic acid extractants. Low toxic sodium hypophosphite was chosen as the phosphorus source to react with olefin A (2,3-dimethyl-1-butene) to generate a monoalkylphosphinic acid intermediate. Amantadine was adopted to remove the dialkylphosphinic acid byproduct, as only the monoalkylphosphinic acid can react with amantadine to form an amantadine∙mono-alkylphosphinic acid salt, while the dialkylphosphinic acid cannot react with amantadine due to its large steric hindrance. The purified monoalkylphosphinic acid was then reacted with olefin B (diisobutylene) to yield nonsymmetric dialkylphosphinic acid (NSDAPA). The unreacted monoalkylphosphinic acid can be easily removed by a simple base-acid post-treatment and other organic impurities can be separated out through the precipitation of the cobalt salt. The structure of the (2,3-dimethylbutyl)(2,4,4'-trimethylpentyl)phosphinic acid was confirmed by 31 P NMR, 1 H NMR, ESI-MS, and FT-IR. The purity was determined by a potentiometric titration method, and the results indicate that the purity can exceed 96%.

High purity materials as targets for radioisotope production: Needs ...

Indian Academy of Sciences (India)

Unknown

lity of high purity target materials, natural or enriched, are crucial for any successful radioisotope pro- gramme. Selection ... and blockages detection in buried pipelines are rendered ..... from reputed international suppliers with analysis report.

Stress corrosion of very high purity stainless steels in alkaline media

International Nuclear Information System (INIS)

Hechmat-Dehcordi, Ebrahim

1981-01-01

This research thesis reports the study of stress corrosion resistance of stainless steels in caustic environments. It notably concerns the electronuclear industrial sector, the production of soda by electrolysis, and the preparation of hydrogen as energy vector. After a presentation of the experimental conditions, the author highlights the influence of purity on stress corrosion cracking of 20Cr-25Ni-type austenitic alloys. The specific action of a high number of addition metallic and non-metallic elements has been studied. Stress corrosion tests have been also performed in autoclave on austeno-ferritic (21 to 25 pc Cr - 6 to 10 pc Ni) as well as ferritic (26 pc Cr) grades. The author reports the study of electrochemical properties of stainless steel in soda by means of potentiostatic techniques with an application of Pourbaix thermodynamic equilibrium diagrams, and the study of the chemical composition of passivation thin layers by Auger spectroscopy. He more particularly studies the influence of electrode potential and of some addition elements on the chemical characteristics of oxides developed at the surface of austenite. Then, the author tries to establish correlations between strain hardening microstructure of the various steels and their sensitivity to stress corrosion [fr

High purity radioactive beams at the bevalac

International Nuclear Information System (INIS)

Alonso, J.R.; Chatterjee, A.; Tobias, C.A.

1979-03-01

Peripheral nuclear fragmentation reactions of primary Bevalac heavy ion beams are used to produce secondary beams of radioactive nuclei. The large cross section and small deflection of the projectile fragments lead to high production and delivery efficiency for these beams. Dispersive beam transport allows good separation and purification of the desired secondary beams. 11 C and 19 Ne beams of high purity and good intensity (almost 0.2% of the primary beam current) are presently being used for biomedical experiments

Effect of water purity on intergranular stress corrosion cracking of stainless steel and nickel alloys in BWRs

Energy Technology Data Exchange (ETDEWEB)

Gordon, B. [Structural Integrity Associates (United States); Garcia, S. [Electric Power Research Institute (United States)

2011-07-01

Boiling water reactors (BWRs) operate with very high purity water. While even the utilization of a very low conductivity water (e.g., 0.06 {mu}S/cm) coolant cannot prevent intergranular stress corrosion cracking (IGSCC) of sensitized stainless steel and nickel alloys under oxygenated conditions, the presence of certain impurities in the coolant can dramatically increase the probability of this most insidious form of corrosion. The goal of this paper is to present the effect of effect of only a few ionic impurities plus zinc on the IGSCC propensities of BWR stainless steel piping and reactor internals under both oxygenated, i.e., normal water chemistry (NWC) and deoxygenated, i.e., hydrogen water chemistry (HWC) conditions. More specifically, of the numerous impurities identified in the BWR coolant (e.g., lithium, sodium, potassium, silica, borate, chromate, phosphate, sulphate, chloride, nitrate, cuprous, cupric, ferrous, etc.) only strong acid anions sulfate and chloride that are stable in the highly reducing crack tip environment rather than the bulk water conductivity will be discussed in detail. Nitrate will be briefly discussed as representing a species that is not thermodynamically stable in the crack while the effects of zinc is discussed as a deliberate additive to the BWR environment. (authors)

Effects of Cr and Nb contents on the susceptibility of Alloy 600 type Ni-base alloys to stress-corrosion cracking in a simulated BWR environment

International Nuclear Information System (INIS)

Akashi, Masatsune

1995-01-01

In order to discuss the effects of chromium and niobium contents on the susceptibility of Alloy 600 type nickel-base alloys to stress-corrosion cracking in the BWR primary coolant environment, a series of creviced bent-beam (CBB) tests were conducted in a high-temperature, high-purity water environment. Chromium, niobium, and titanium as alloying elements improved the resistivity to stress-corrosion cracking, whereas carbon enhanced the susceptibility to it. Alloy-chemistry-based correlations have been defined to predict the relative resistances of alloys to stress-corrosion cracking. A strong correlation was found, for several heats of alloys, between grain-boundary chromium depletion and the susceptibility to stress-corrosion cracking

A High-Purity Alumina for Use in Studies of Shock Loaded Samples

Science.gov (United States)

Lacina, David; Neel, Christopher

2017-06-01

We report the results of plate impact experiments on a potential new ``standard'' material, Coorstek Plasmapure-UC (99.9% purity) polycrystalline alumina, for use in non-conduction, impact environment, shock loading studies. This work was motivated by a desire to find a 99.9% purity alumina to replace the now unavailable Coors Vistal (99.9%) alumina, as it was hoped the Hugoniot elastic limit (HEL) of the new standard would match the 9-11 GPa value of Vistal. Shock response data, including the HEL, Hugoniot particle velocities, Hugoniot shock velocities, stress vs volume, and release wave speeds, was obtained up to 14 GPa. This data will be compared with Hugoniot curve data for other high purity alumina to contrast differences in the shock response, and is intended to be useful in impedance matching calculations. We will show that the HEL of Plasmapure-UC alumina is 5.5 GPa and speculate on causes for this lower than expected value. We will also explore why the elastic-plastic response for Plasmapure-UC alumina differs from what has been observed from other high purity alumina. The final result of this work is to recommend a well-characterized, lower purity alumina (Coorstek AD-995) as a potential new ``standard'' material.

High strength alloys

Science.gov (United States)

Maziasz, Phillip James [Oak Ridge, TN; Shingledecker, John Paul [Knoxville, TN; Santella, Michael Leonard [Knoxville, TN; Schneibel, Joachim Hugo [Knoxville, TN; Sikka, Vinod Kumar [Oak Ridge, TN; Vinegar, Harold J [Bellaire, TX; John, Randy Carl [Houston, TX; Kim, Dong Sub [Sugar Land, TX

2010-08-31

High strength metal alloys are described herein. At least one composition of a metal alloy includes chromium, nickel, copper, manganese, silicon, niobium, tungsten and iron. System, methods, and heaters that include the high strength metal alloys are described herein. At least one heater system may include a canister at least partially made from material containing at least one of the metal alloys. At least one system for heating a subterranean formation may include a tubular that is at least partially made from a material containing at least one of the metal alloys.

Effect of heat treatment conditions on stress corrosion cracking resistance of alloy X-750 in high temperature water

International Nuclear Information System (INIS)

Yonezawa, Toshio; Onimura, Kichiro; Sakamoto, Naruo; Sasaguri, Nobuya; Susukida, Hiroshi; Nakata, Hidenori.

1984-01-01

In order to improve the resistance of the Alloy X-750 in high temperature and high purity water, the authors investigated the influence of heat treatment condition on the stress corrosion cracking resistance of the alloy. This paper describes results of the stress corrosion cracking test and some discussion on the mechanism of the stress corrosion cracking of Alloy X-750 in deaerated high temperature water. The following results were obtained. (1) The stress corrosion cracking resistance of Alloy X-750 in deaerated high temperature water remarkably depended upon the heat treatment condition. The materials solution heat treated and aged within temperature ranges from 1065 to 1100 0 C and from 704 to 732 0 C, respectively, have a good resistance to the stress corrosion cracking in deaerated high temperature water. Especially, water cooling after the solution heat treatment gives an excellent resistance to the stress corrosion cracking in deaerated high temperature water. (2) Any correlations were not observed between the stress corrosion cracking susceptibility of Alloy X-750 in deaerated high temperature water and grain boundary chromium depleted zones, precipitate free zones and the grain boundary segregation of impurity elements and so on. It appears that there are good correlations between the stress corrosion cracking resistance of the alloy in the environment and the kinds, morphology and coherency of precipitates along the grain boundaries. (author)

Tests of ball bearing used in high-temperature and high-purity water

International Nuclear Information System (INIS)

Leng Chengmu; Hao Shouxin.

1987-01-01

According to the particular conditions and the operation environments in high-temperature and high-purity water, the test content and the measurement instrumentation for the ball bearing were defined. Through various tests, operational performances of the bearing have preliminarily been understood. It provided some useful information for the engineering application of the bearing

Radiochemical purity of Mo and Tc solution obtained after irradiation and dissolution of Mo-100-enriched and ultra-high-purity natural Mo disks

Energy Technology Data Exchange (ETDEWEB)

Tkac, Peter [Argonne National Lab. (ANL), Argonne, IL (United States); Gromov, Roman [Argonne National Lab. (ANL), Argonne, IL (United States); Chemerisov, Sergey D. [Argonne National Lab. (ANL), Argonne, IL (United States); Rotsch, David A. [Argonne National Lab. (ANL), Argonne, IL (United States); Vandegrift, George F. [Argonne National Lab. (ANL), Argonne, IL (United States)

2016-09-01

Four irradiations of ultra-high-purity natural Mo targets and one irradiation using 97.4% Mo-100-enriched material were performed. The purpose of these irradiations was to determine whether the presence of Sn stabilizer in the H₂O₂ used for the dissolution of sintered Mo disks can affect the radiochemical purity of the final K₂MoO₄ in 5M KOH solution. Results from radiochemical purity tests performed using thin-layer paper chromatography show that even 2– 3× excess of Sn-stabilized H₂O₂ typically used for dissolution of sintered Mo disks did not affect the radiochemical purity of the final product.

Grain boundary selective oxidation and intergranular stress corrosion crack growth of high-purity nickel binary alloys in high-temperature hydrogenated water

Energy Technology Data Exchange (ETDEWEB)

Bruemmer, S. M.; Olszta, M. J.; Toloczko, M. B.; Schreiber, D. K.

2018-02-01

The effects of alloying elements in Ni-5at%X binary alloys on intergranular (IG) corrosion and stress corrosion cracking (SCC) have been assessed in 300-360°C hydrogenated water at the Ni/NiO stability line. Alloys with Cr or Al additions exhibited grain boundary oxidation and IGSCC, while localized degradation was not observed for pure Ni, Ni-Cu or Ni-Fe alloys. Environment-enhanced crack growth was determined by comparing the response in water and N2 gas. Results demonstrate that selective grain boundary oxidation of Cr and Al promoted IGSCC of these Ni alloys in hydrogenated water.

Fused salt processing of impure plutonium dioxide to high-purity plutonium metal

International Nuclear Information System (INIS)

Mullins, L.J.; Christensen, D.C.; Babcock, B.R.

1982-01-01

A process for converting impure plutonium dioxide (approx. 96% pure) to high-purity plutonium metal (>99.9%) was developed. The process consists of reducing the oxide to an impure plutonium metal intermediate with calcium metal in molten calcium chloride. The impure intermediate metal is cast into an anode and electrorefined to produce high-purity plutonium metal. The oxide reduction step is being done now on a 0.6-kg scale with the resulting yield being >99.5%. The electrorefining is being done on a 4.0-kg scale with the resulting yield being 80 to 85%. The purity of the product, which averages 99.98%, is essentially insensitive to the purity of the feed metal. The yield, however, is directly dependent on the chemical composition of the feed. To date, approximately 250 kg of impure oxide has been converted to pure metal by this processing sequence. The availability of impure plutonium dioxide, together with the need for pure plutonium metal, makes this sequence a valuable plutonium processing tool

Analysis technique of impurity in high purity deuterium by cryogenic gas-chromatography

International Nuclear Information System (INIS)

Zhou Junbo; Gao Liping

2007-01-01

A veracious and applicable quantitative analysis method of O 2 , N 2 and H 2 , HD in high purity deuterium by the chromatogram columniation filled with 5A molecular sieve and alumina was researched and constituted at natural temperature and 77 K, respectively. Minimum detecting limit of the present method is (150-200) x 10 -6 for H 2 and HD, and it can meet the need of quantitative analysis of the impurity during high purity deuterium preparation. (authors)

Hydrogen concentration and distribution in high-purity germanium crystals

International Nuclear Information System (INIS)

Hansen, W.L.; Haller, E.E.; Luke, P.N.

1981-10-01

High-purity germanium crystals used for making nuclear radiation detectors are usually grown in a hydrogen ambient from a melt contained in a high-purity silica crucible. The benefits and problems encountered in using a hydrogen ambient are reviewed. A hydrogen concentration of about 2 x 10 15 cm -3 has been determined by growing crystals in hydrogen spiked with tritium and counting the tritium β-decays in detectors made from these crystals. Annealing studies show that the hydrogen is strongly bound, either to defects or as H 2 with a dissociation energy > 3 eV. This is lowered to 1.8 eV when copper is present. Etching defects in dislocation-free crystals grown in hydrogen have been found by etch stripping to have a density of about 1 x 10 7 cm -3 and are estimated to contain 10 8 H atoms each

Some aspects of ICP-AES analysis of high purity rare earths

International Nuclear Information System (INIS)

Murty, P.S.; Biswas, S.S.

1991-01-01

Inductively coupled plasma atomic emission spectrometry (ICP-AES) is a technique capable of giving high sensitivity in trace elemental analysis. While the technique possesses high sensitivity, it lacks high selectivity. Selectivity is important where substances emitting complex spectra are to be analysed for trace elements. Rare earths emit highly complex spectra in a plasma source and the determination of adjacent rare earths in a high purity rare earth matrix, with high sensitivity, is not possible due to the inadequate selectivity of ICP-AES. One approach that has yielded reasonably good spectral selectivity in the high purity rare earth analysis by ICP-AES is by employing a combination of wavelength modulation techniques and high resolution echelle grating. However, it was found that by using a high resolution monochromator senstitivities either comparable to or better than those reported by the wavelength modulation technique could be obtained. (author). 2 refs., 2 figs., 2 tabs

Effect of cobalt on microstructure and properties of AlCr1.5CuFeNi2Cox high-entropy alloys

Science.gov (United States)

Kukshal, Vikas; Patnaik, Amar; Bhat, I. K.

2018-04-01

The present paper investigates the effect of Co addition on the alloying behaviour, microstructure and the resulting properties of cast AlCr1.5CuFeNi2Cox high-entropy alloys intended to be used for high temperature applications. The elements Al, Cr, Cu, Fe, Ni and Co (Purity > 99) weighing approximately 800 g was melted in a high temperature vacuum induction furnace. The microstructure, phase transformation, density, microhardness and compressive strength of the samples were analysed using x-ray diffraction (XRD), scanning electron microscopes (SEM), Vickers microhardness tester and universal Testing machine. The crystalline structure of the alloys exhibits simple FCC and BCC phases. The microstructures investigation of the alloys shows the segregation of copper in the interdendritic region resulting in Cu-rich FCC phase. The addition of Co further enhances the formation of FCC phase resulting in the decrease in micro hardness value of the alloys, which varies from 471 HV to 364 HV with increase in the cobalt content from x = 0 to x = 1 (molar ratio). The similar decreasing trend is also observed for the compressive strength of the alloys.

Structure and mechanical properties of nanostructured Al-0.3%Cu alloy

DEFF Research Database (Denmark)

Wakeel, Aneela; Huang, Tianlin; Wu, Guilin

2014-01-01

An Al-0.3%Cu alloy has been produced using extremely high purity (99.9996%) Al and OFHC Cu.The alloy was cold rolled to 98% thickness reduction, forming a stable lamellar structure that has a lamellar boundary spacing of about 200nm and a tensile strength of 225MPa. During recovery annealing at t...

Isolation of high purity americium metal via distillation

Science.gov (United States)

Squires, Leah N.; King, James A.; Fielding, Randall S.; Lessing, Paul

2018-03-01

Pure americium metal is a crucial component for the fabrication of transmutation fuels. Unfortunately, americium in pure metal form is not available; however, a number of mixed metals and mixed oxides that include americium are available. In this manuscript a method is described to obtain high purity americium metal from a mixture of americium and neptunium metals with lead impurity via distillation.

Ion-exchange preparation of high-purity vanadium acid from industrial liquors

International Nuclear Information System (INIS)

Sajdakhmedov, U.A.; Arslanov, Sh.S.; Vulikh, A.I.

1994-01-01

The results of investigations on production of special-purity vanadium acid and vanadium oxide directly from process solutions (technical grade liquors) using ionites are presented. Potentiality of thorough purification of vanadium(5) oxide, when producing vanadium acid on the KU-2 cationite with subsequent purification on anionite, is shown. On the basis of the results obtained a principle flowsheet of ion-exchange production of high-purity vanadium(5) oxide from industrial liquors has been developed. 2 refs.; 1 fig.; 4 tabs

Diffusion bonding and brazing of high purity copper for linear collider accelerator structures

Directory of Open Access Journals (Sweden)

J. W. Elmer

2001-05-01

Full Text Available Diffusion bonding and brazing of high purity copper were investigated to develop procedures for joining precision machined copper components for the Next Linear Collider (NLC. Diffusion bonds were made over a range of temperatures from 400 °C to 1000 °C, under two different loading conditions [3.45 kPa (0.5 psi and 3.45 MPa (500 psi], and on two different diamond machined surface finishes. Brazes were made using pure silver, pure gold, and gold-nickel alloys, and different heating rates produced by both radiation and induction heating. Braze materials were applied by both physical vapor deposition (PVD and conventional braze alloy shims. Results of the diffusion bonding experiments showed that bond strengths very near that of the copper base metal could be made at bonding temperatures of 700 °C or higher at 3.45 MPa bonding pressure. At lower temperatures, only partial strength diffusion bonds could be made. At low bonding pressures (3.45 kPa, full strength bonds were made at temperatures of 800 °C and higher, while no bonding (zero strength was observed at temperatures of 700 °C and lower. Observations of the fracture surfaces of the diffusion bonded samples showed the effects of surface finish on the bonding mechanism. These observations clearly indicate that bonding began by point asperity contact, and flatter surfaces resulted in a higher percentage of bonded area under similar bonding conditions. Results of the brazing experiments indicated that pure silver worked very well for brazing under both conventional and high heating rate scenarios. Similarly, pure silver brazed well for both the PVD layers and the braze alloy shims. The gold and gold-containing brazes had problems, mainly due to the high diffusivity of gold in copper. These problems led to the necessity of overdriving the temperature to ensure melting, the presence of porosity in the joint, and very wide braze joints. Based on the overall findings of this study, a two

TIGRESS highly-segmented high-purity germanium clover detector

Science.gov (United States)

Scraggs, H. C.; Pearson, C. J.; Hackman, G.; Smith, M. B.; Austin, R. A. E.; Ball, G. C.; Boston, A. J.; Bricault, P.; Chakrawarthy, R. S.; Churchman, R.; Cowan, N.; Cronkhite, G.; Cunningham, E. S.; Drake, T. E.; Finlay, P.; Garrett, P. E.; Grinyer, G. F.; Hyland, B.; Jones, B.; Leslie, J. R.; Martin, J.-P.; Morris, D.; Morton, A. C.; Phillips, A. A.; Sarazin, F.; Schumaker, M. A.; Svensson, C. E.; Valiente-Dobón, J. J.; Waddington, J. C.; Watters, L. M.; Zimmerman, L.

2005-05-01

The TRIUMF-ISAC Gamma-Ray Escape-Suppressed Spectrometer (TIGRESS) will consist of twelve units of four high-purity germanium (HPGe) crystals in a common cryostat. The outer contacts of each crystal will be divided into four quadrants and two lateral segments for a total of eight outer contacts. The performance of a prototype HPGe four-crystal unit has been investigated. Integrated noise spectra for all contacts were measured. Energy resolutions, relative efficiencies for both individual crystals and for the entire unit, and peak-to-total ratios were measured with point-like sources. Position-dependent performance was measured by moving a collimated source across the face of the detector.

Giant magnetocaloric effect in Gd5(Si2Ge2 alloy with low purity Gd

Directory of Open Access Journals (Sweden)

Cleber Santiago Alves

2004-12-01

Full Text Available Gd5(Ge1-xSi x, x < 4 based alloys are potential candidates for magnetic refrigeration in the range ~20 - ~290 K. However, one of the greatest obstacles for the use of that technology in large scale is the utilization of high pure Gd metal (99.99 wt. (% to produce the GdGeSi alloys, since the impurity elements decrease the intensity of the magnetocaloric effect (EMC¹. In this work, we prove that annealing of the Gd5Ge2Si2 can promote remarkable values for the EMC in comparison to those obtained for the alloy with high pure Gd. Also, the as cast alloy and the annealed alloy are not monophasic, but have at least two crystalline phases in their microstructure. Results for X-ray analysis, optical and electronic microscopy and magnetization measurements are reported.

High purity neodymium acetate from mixed rare earth carbonates

International Nuclear Information System (INIS)

Queiroz, Carlos A. da Silva; Rocha, Soraya M. Rizzo da; Vasconcellos, Mari E. de; Lobo, Raquel M.; Seneda, Jose A.; Pedreira, Walter dos R.

2011-01-01

A simple and economical chemical process for obtaining high purity neodymium acetate is discussed. The raw material in the form rare earth carbonate is produced industrially from the chemical treatment of Brazilian monazite. Ion exchange chromatography technique with a strong cationic resin, proper to water treatment, and without the use of retention ions was used for the fractionating of the rare earth elements (REE). In this way, it was possible to obtain 99.9% pure Nd 2 O 3 in yields greater than or equal 80%, with the elution of the REE using ammonium salt of ethylenediaminetetraacetic acid (EDTA) solution in pH controlled. The complex of EDTA-neodymium was transformed into neodymium oxide, which was subsequently dissolved in acetic acid to obtain the neodymium acetates. Molecular absorption spectrophotometry was used to monitor the neodymium content during the process and sector field inductively coupled plasma mass spectrometry was used to certify the purity of the neodymium acetates. The typical neodymium acetates obtained contain the followings contaminants in μg g -1 : Sc(5.1); Y (0.9); La (1.0); Ce (6.1); Pr (34,4); Sm (12.8); Eu (1.1); Gd (15.4); Tb (29.3); Dy (5.2), Ho(7.4); Er (14.6); Tm (0.3); Yb (2.5); Lu (1.0). The high purity neodymium acetates obtained from this procedure have been applied, replacing the imported product, in research and development area on rare earth catalysts. (author)

Scalable preparation of high purity rutin fatty acid esters following enzymatic synthesis

DEFF Research Database (Denmark)

Lue, Bena-Marie; Guo, Zheng; Xu, Xuebing

2010-01-01

Investigations into expanded uses of modified flavonoids are often limited by the availability of these high purity compounds. As such, a simple, effective and relatively fast method for isolation of gram quantities of both long and medium chain fatty acid esters of rutin following scaled......-up biosynthesis reactions was established. Acylation reactions of rutin and palmitic or lauric acids were efficient in systems containing dried acetone and molecular sieves, yielding from 70–77% bioconversion after 96 h. Thereafter, high purity isolates (>97%) were easily obtained in significant quantities...

Analysis of heterogeneities in strain and microstructure in aluminum alloy and magnesium processed by high-pressure torsion

Energy Technology Data Exchange (ETDEWEB)

Panda, Subrata, E-mail: subrata.panda@univ-lorraine.fr [Université de Lorraine, Laboratory of Excellence on Design of Alloy Metals for low-mass Structures (DAMAS), Ile du Saulcy, Metz F-57045 (France); Université de Lorraine, Laboratoire d' Etude des Microstructures et de Mécanique des Matériaux (LEM3 UMR 7239), Ile du Saulcy, Metz F-57045 (France); Toth, Laszlo S., E-mail: laszlo.toth@univ-lorraine.fr [Université de Lorraine, Laboratory of Excellence on Design of Alloy Metals for low-mass Structures (DAMAS), Ile du Saulcy, Metz F-57045 (France); Université de Lorraine, Laboratoire d' Etude des Microstructures et de Mécanique des Matériaux (LEM3 UMR 7239), Ile du Saulcy, Metz F-57045 (France); Fundenberger, Jean-Jacques, E-mail: jean-jacques.fundenberger@univ-lorraine.fr [Université de Lorraine, Laboratory of Excellence on Design of Alloy Metals for low-mass Structures (DAMAS), Ile du Saulcy, Metz F-57045 (France); Université de Lorraine, Laboratoire d' Etude des Microstructures et de Mécanique des Matériaux (LEM3 UMR 7239), Ile du Saulcy, Metz F-57045 (France); Perroud, Olivier, E-mail: olivier.perroud@univ-lorraine.fr [Université de Lorraine, Laboratory of Excellence on Design of Alloy Metals for low-mass Structures (DAMAS), Ile du Saulcy, Metz F-57045 (France); Université de Lorraine, Laboratoire d' Etude des Microstructures et de Mécanique des Matériaux (LEM3 UMR 7239), Ile du Saulcy, Metz F-57045 (France); and others

2017-01-15

Two distinct bulk light metals were opted to study the shear strain evolution and associated heterogeneities in texture/microstructure development during torsional straining by high pressure torsion (HPT): a face centered cubic Al alloy (A5086) and a hexagonal commercial purity Mg. Relatively thick disk samples - four times thicker than usually employed in HPT process - were processed to 180° and 270° rotations. With the help of X-ray tomography, the shear strain gradients were examined in the axial direction. The results showed strongly localized shear deformation in the middle plane of the disks in both materials. These gradients involved strong heterogeneities in texture, microstructure and associated hardness, in particular through the thickness direction at the periphery of the disk where the interplay between significant strain hardening and possible dynamic recrystallization could occur. - Highlights: •HPT processing was conducted on bulk specimens thicker than the usual thin-disks. •The Al alloy (A5086) and commercial purity magnesium samples were compared. •Distributions of strain and microhardness were evaluated in the radial and axial direction. •Plastic deformation is highly localized in the middle plane at outer edge in both materials. •Different DRX rates governed the differences in microstructure and hardening behavior.

Acoustic emission from a solidifying aluminum-lithium alloy

Science.gov (United States)

Henkel, D. P.; Wood, J. D.

1992-01-01

Physical phenomena associated with the solidification of an AA2090 Al-Li alloy have been characterized by AE methods. Repeatable patterns of AE activity as a function of solidification time are recorded and explained for ultrahigh-purity (UHP) aluminum and an Al-4.7 wt pct Cu binary alloy, in addition to the AA2090 Al-Li alloy, by the complementary utilization of thermal, AE, and metallographic methods. One result shows that the solidification of UHP aluminum produces one discrete period of high AE activity as the last 10 percent of solid forms.

Demands made on high-purity copper for special purposes

International Nuclear Information System (INIS)

Roettges, D.

1977-01-01

The properties (electrical resistivity, residual impurities) of high-purity copper produced on a technical scale are reported as well as its practical applications. The paper discusses a high-oxygen copper (SV) with low residual resistivity at low temperatures and an oxygen-free (hydrogen-stable) copper (BE electronic) with low gas content. The SV quality has been specially developed for use as stabilizer in superconductors while the BE quality is used in high and ultrahigh vacuum. (GSC) [de

Neutron activation analysis of high purity substances

International Nuclear Information System (INIS)

Gil'bert, Eh.N.

1987-01-01

Peculiarities of neutron-activation analysis (NAA) of high purity substances are considered. Simultaneous determination of a wide series of elements, high sensitivity (the lower bound of determined contents 10 -9 -10 -10 %), high selectivity and accuracy (Sr=0.10-0.15, and may be decreased up to 0.001), possibility of analysis of the samples from several micrograms to hundreds of grams, simplicity of calibration may be thought NAA advantages. Questions of accounting of NAA systematic errors associated with the neutron flux screening by the analysed matrix and with production of radionuclides of determined elements from accompanying elements according to concurrent nuclear reactions, as well as accounting of errors due to self-absorption of recorded radiation by compact samples, are considered

High-power laser diodes with high polarization purity

Science.gov (United States)

Rosenkrantz, Etai; Yanson, Dan; Peleg, Ophir; Blonder, Moshe; Rappaport, Noam; Klumel, Genady

2017-02-01

Fiber-coupled laser diode modules employ power scaling of single emitters for fiber laser pumping. To this end, techniques such as geometrical, spectral and polarization beam combining (PBC) are used. For PBC, linear polarization with high degree of purity is important, as any non-perfectly polarized light leads to losses and heating. Furthermore, PBC is typically performed in a collimated portion of the beams, which also cancels the angular dependence of the PBC element, e.g., beam-splitter. However, we discovered that single emitters have variable degrees of polarization, which depends both on the operating current and far-field divergence. We present data to show angle-resolved polarization measurements that correlate with the ignition of high-order modes in the slow-axis emission of the emitter. We demonstrate that the ultimate laser brightness includes not only the standard parameters such as power, emitting area and beam divergence, but also the degree of polarization (DoP), which is a strong function of the latter. Improved slow-axis divergence, therefore, contributes not only to high brightness but also high beam combining efficiency through polarization.

Preparation of high-purity zirconium dioxide from baddeleyite

International Nuclear Information System (INIS)

Voskobojnikov, N.B.; Skiba, G.S.

1996-01-01

Interaction of baddeleyite concentrate with calcium oxide and calcium chloride in the process of caking is studied. The influence of grain size on calcium zirconate formation is tested. Conditions for cake leaching by hydrochloric acid and zirconium(4) oxychloride purification from calcium and silicon compounds by recrystallization are reported. Zirconium dioxide corresponding to specifications (6-2 special purity) is obtained with a high (more than 90%) chemical yield. 9 refs., 1 tab

Corrosion behaviour of alloy Ti-35 in boiling nitric acid solution

International Nuclear Information System (INIS)

Lan Cui; Qiu Shaoyu

2005-01-01

This report states the corrosion behaviors of alloy Ti-35 in boiling nitric acid solution. The results show that its general corrosion rate is by far superior to high-purity austenitic stainless steel with super-low carbon content, the stress corrosion and crevice corrosion have been not discovered in its samples, and oxide film can be quickly reproduced in scratch. The microstructural analysis on samples shows that there is a thin compact TiO 2 film on the sample surface of alloy Ti-35, and most of the film possess the crystal structure of rutile type, the other has the crystal structure of anatase type. This oxide layer plays a role in hindering corrosion development, so the corrosion resistance of alloy Ti-35 is raised. In contrast with it, the oxide film on the sample surface of austenitic stainless steel is not found. It is evident that alloy Ti-35 can become the prime candidate structural material for dissolver of reprocessing facility of spent fuel and be substituted for high-purity austenitic stainless steel with super-low carbon content which is used now. (authors)

Spectroscopic Determination of Trace Contaminants in High Purity Oxygen

Science.gov (United States)

Hornung, Steven D.

2011-01-01

Oxygen used for extravehicular activities (EVA) must be free of contaminants because a difference in a few tenths of a percent of argon or nitrogen content can mean significant reduction in available EVA time. These inert gases build up in the extravehicular mobility unit because they are not metabolized or scrubbed from the atmosphere. Measurement of oxygen purity above 99.5% is problematic, and currently only complex instruments such as gas chromatographs or mass spectrometers are used for these determinations. Because liquid oxygen boil-off from the space shuttle will no longer be available to supply oxygen for EVA use, other concepts are being developed to produce and validate high purity oxygen from cabin air aboard the International Space Station. A prototype optical emission technique capable of detecting argon and nitrogen below 0.1% in oxygen was developed at White Sands Test Facility. This instrument uses a glow discharge in reduced pressure gas to produce atomic emission from the species present. Because the atomic emission lines from oxygen, nitrogen, and argon are discrete and in many cases well-separated, trace amounts of argon and nitrogen can be detected in the ultraviolet and visible spectrum. This is a straightforward, direct measurement of the target contaminants and may lend itself to a device capable of on-orbit verification of oxygen purity. System design and optimized measurement parameters are presented.

A light hydrocarbon fuel processor producing high-purity hydrogen

Science.gov (United States)

Löffler, Daniel G.; Taylor, Kyle; Mason, Dylan

This paper discusses the design process and presents performance data for a dual fuel (natural gas and LPG) fuel processor for PEM fuel cells delivering between 2 and 8 kW electric power in stationary applications. The fuel processor resulted from a series of design compromises made to address different design constraints. First, the product quality was selected; then, the unit operations needed to achieve that product quality were chosen from the pool of available technologies. Next, the specific equipment needed for each unit operation was selected. Finally, the unit operations were thermally integrated to achieve high thermal efficiency. Early in the design process, it was decided that the fuel processor would deliver high-purity hydrogen. Hydrogen can be separated from other gases by pressure-driven processes based on either selective adsorption or permeation. The pressure requirement made steam reforming (SR) the preferred reforming technology because it does not require compression of combustion air; therefore, steam reforming is more efficient in a high-pressure fuel processor than alternative technologies like autothermal reforming (ATR) or partial oxidation (POX), where the combustion occurs at the pressure of the process stream. A low-temperature pre-reformer reactor is needed upstream of a steam reformer to suppress coke formation; yet, low temperatures facilitate the formation of metal sulfides that deactivate the catalyst. For this reason, a desulfurization unit is needed upstream of the pre-reformer. Hydrogen separation was implemented using a palladium alloy membrane. Packed beds were chosen for the pre-reformer and reformer reactors primarily because of their low cost, relatively simple operation and low maintenance. Commercial, off-the-shelf balance of plant (BOP) components (pumps, valves, and heat exchangers) were used to integrate the unit operations. The fuel processor delivers up to 100 slm hydrogen >99.9% pure with <1 ppm CO, <3 ppm CO 2. The

High-purity Cu nanocrystal synthesis by a dynamic decomposition method

Science.gov (United States)

Jian, Xian; Cao, Yu; Chen, Guozhang; Wang, Chao; Tang, Hui; Yin, Liangjun; Luan, Chunhong; Liang, Yinglin; Jiang, Jing; Wu, Sixin; Zeng, Qing; Wang, Fei; Zhang, Chengui

2014-12-01

Cu nanocrystals are applied extensively in several fields, particularly in the microelectron, sensor, and catalysis. The catalytic behavior of Cu nanocrystals depends mainly on the structure and particle size. In this work, formation of high-purity Cu nanocrystals is studied using a common chemical vapor deposition precursor of cupric tartrate. This process is investigated through a combined experimental and computational approach. The decomposition kinetics is researched via differential scanning calorimetry and thermogravimetric analysis using Flynn-Wall-Ozawa, Kissinger, and Starink methods. The growth was found to be influenced by the factors of reaction temperature, protective gas, and time. And microstructural and thermal characterizations were performed by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, and differential scanning calorimetry. Decomposition of cupric tartrate at different temperatures was simulated by density functional theory calculations under the generalized gradient approximation. High crystalline Cu nanocrystals without floccules were obtained from thermal decomposition of cupric tartrate at 271°C for 8 h under Ar. This general approach paves a way to controllable synthesis of Cu nanocrystals with high purity.

Characterization of a high-purity germanium detector for small-animal SPECT.

Science.gov (United States)

Johnson, Lindsay C; Campbell, Desmond L; Hull, Ethan L; Peterson, Todd E

2011-09-21

We present an initial evaluation of a mechanically cooled, high-purity germanium double-sided strip detector as a potential gamma camera for small-animal SPECT. It is 90 mm in diameter and 10 mm thick with two sets of 16 orthogonal strips that have a 4.5 mm width with a 5 mm pitch. We found an energy resolution of 0.96% at 140 keV, an intrinsic efficiency of 43.3% at 122 keV and a FWHM spatial resolution of approximately 1.5 mm. We demonstrated depth-of-interaction estimation capability through comparison of pinhole acquisitions with a point source on and off axes. Finally, a flood-corrected flood image exhibited a strip-level uniformity of less than 1%. This high-purity germanium offers many desirable properties for small-animal SPECT.

Development of fabrication technology for low activation vanadium alloys as fusion blanket structural materials

International Nuclear Information System (INIS)

Nagasaka, T.; Muroga, T.; Fukumoto, K.; Watanabe, H.; Grossbeck, M.L.; Chen, J.M.

2005-01-01

High purity vanadium alloy products, such as plates, wires and tubes, were fabricated from reference high-purity V-4Cr-4Ti ingots designated as NIFS-HEAT, by using technologies applicable to industrial scale fabrication. Impurity behavior during breakdown, and its effect on mechanical properties were investigated. It was revealed that mechanical properties of the products were significantly improved by the control of Ti-C, N, O precipitation induced during the processes. (author)

Wet routes of high purity BaTiO3 nanopowders

International Nuclear Information System (INIS)

Wang Liqiu; Liu Liang; Xue Dongfeng; Kang Hongmin; Liu Changhou

2007-01-01

High purity BaTiO 3 nanopowders were prepared in wet routes through stearic acid gel (SAG) and acetic acid gel (AAG) techniques, respectively. BaTiO 3 samples were characterized by X-ray diffraction, transmission electron microscope, Fourier transform infrared spectrometry, X-ray fluorescence spectrometry, and thermal gravimetric analysis. The present results indicate that both methods have a similar reaction process during calcination, while BaTiO 3 crystallites were initially formed at 550 deg. C by SAG and 800 deg. C by AAG. Both methods could produce BaTiO 3 powders with a cubic perovskite structure, while they had different grain size distributions within 25-50 nm for SAG and 50-80 nm for AAG. BaTiO 3 samples prepared by SAG had a lower agglomeration than those by AAG. SAG has shown many distinctive advantages in the preparation of high purity BaTiO 3 nanopowders, without Ba and Ti losses and hazardous wastes

Development of high purity large forgings for nuclear power plants

International Nuclear Information System (INIS)

Tanaka, Yasuhiko; Sato, Ikuo

2011-01-01

The recent increase in the size of energy plants has been supported by the development of manufacturing technology for high purity large forgings for the key components of the plant. To assure the reliability and performance of the large forgings, refining technology to make high purity steels, casting technology for gigantic ingots, forging technology to homogenize the material and consolidate porosity are essential, together with the required heat treatment and machining technologies. To meet these needs, the double degassing method to reduce impurities, multi-pouring methods to cast the gigantic ingots, vacuum carbon deoxidization, the warm forging process and related technologies have been developed and further improved. Furthermore, melting facilities including vacuum induction melting and electro slag re-melting furnaces have been installed. By using these technologies and equipment, large forgings have been manufactured and shipped to customers. These technologies have also been applied to the manufacture of austenitic steel vessel components of the fast breeder reactors and components for fusion experiments.

Development of high purity large forgings for nuclear power plants

Science.gov (United States)

Tanaka, Yasuhiko; Sato, Ikuo

2011-10-01

The recent increase in the size of energy plants has been supported by the development of manufacturing technology for high purity large forgings for the key components of the plant. To assure the reliability and performance of the large forgings, refining technology to make high purity steels, casting technology for gigantic ingots, forging technology to homogenize the material and consolidate porosity are essential, together with the required heat treatment and machining technologies. To meet these needs, the double degassing method to reduce impurities, multi-pouring methods to cast the gigantic ingots, vacuum carbon deoxidization, the warm forging process and related technologies have been developed and further improved. Furthermore, melting facilities including vacuum induction melting and electro slag re-melting furnaces have been installed. By using these technologies and equipment, large forgings have been manufactured and shipped to customers. These technologies have also been applied to the manufacture of austenitic steel vessel components of the fast breeder reactors and components for fusion experiments.

Process for the production of high purity deuterium

International Nuclear Information System (INIS)

Arrathoon, R.

1977-01-01

A process for the electrolysis of heavy water which results in the production of high purity deuterium without periodic replenishment of the electrolyte with additional deuterated compounds is defined. Electrolysis is effected through the use of an inexpensive cation-action permselective membrane which is essentially a solid polymer electrolyte and which is capable of automatically separating the evolved deuterium and oxygen gas. This cation-active permselective membrane does not introduce any intrinsic impurities or tritium contamination in the generated deuterium gas, does not require periodic revitalization with deuterated compounds or other chemical compounds, and is characterized by an unusually high electrical efficiency

Effect of Mechanical Alloying Atmospheres and Oxygen Concentration on Mechanical Properties of ODS Ferritic Steels

International Nuclear Information System (INIS)

Noh, Sanghoon; Choi, Byoungkwon; Han, Changhee; Kim, Kibaik; Kang, Sukhoon; Chun, Youngbum; Kim, Taekyu

2013-01-01

Finely dispersed nano-oxide particles with a high number density in the homogeneous grain matrix are essential to achieve superior mechanical properties at high temperatures, and these unique microstructures can be obtained through the mechanical alloying (MA) and hot consolidation process. The microstructure and mechanical property of ODS steel significantly depends on its powder property and the purity after the MA process. These contents should be carefully controlled to improve the mechanical property at elevated temperature. In particular, appropriate the control of oxygen concentration improves the mechanical property of ODS steel at high temperature. An effective method is to control the mechanical alloying atmosphere by high purity inert gas. In the present study, the effects of mechanical alloying atmospheres and oxygen concentration on the mechanical property of ODS steel were investigated. ODS ferritic alloys were fabricated in various atmospheres, and the HIP process was used to investigate the effects of MA atmospheres and oxygen concentration on the microstructure and mechanical property. ODS ferritic alloys milled in an Ar-H 2 mixture, and He is effective to reduce the excess oxygen concentration. The YH 2 addition made an extremely reduced oxygen concentration by the internal oxygen reduction reaction and resulted in a homogeneous microstructure and superior creep strength

The effect of carbon distribution on deformation and cracking of Ni-16Cr-9Fe-C alloys

International Nuclear Information System (INIS)

Hertzberg, J.L.; Was, G.S.

1995-01-01

Constant extension rate tensile (CERT) tests and constant load tensile (CLT) tests were conducted on controlled purity Ni-16Cr-9Fe-C alloys. The amount and form of carbon were varied in order to investigate the roles of carbon in solution and as intergranular (IG) carbides in the deformation and IG cracking behavior in 360 C argon and primary water environments. Results show that the strength, ductility and creep resistance of these alloys are increased with carbon present in solid solution, while IG cracking on the fracture surface is suppressed. Alloys containing carbon in the form of IG carbides, however, exhibit reduced strength and ductility relative to carbon in solution, while maintaining high IG cracking resistance with respect to carbon-free alloys. CERT results of commercial alloy 600 and controlled purity, carbon containing alloys yield comparable failure strains and IG cracking amounts. CLT comparisons with creep tests of alloy 600 suggest that alloys containing IG carbides are more susceptible to creep than those containing all carbon in solid solution

The European Expression Of Interest For High Purity U-233 Materials

Energy Technology Data Exchange (ETDEWEB)

Giaquinto, Joseph M. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Younkin, James R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

2017-04-01

The purpose of this letter report is to document the response for an Expression of Interest (EOI) sent to the European Safeguards and research and development (R&D) scientific communities for the distribution of small amounts of high purity ²³³U materials for use in safeguards, nonproliferation, and basic R&D in the nuclear disciplines. The intent for the EOI was to gauge the level of international interest for these materials from government and research institutions with programmatic missions in the nuclear security or nuclear R&D arena. The information contained herein is intended to provide information to assist key decision makers in DOE as to the ultimate disposition path for the high purity materials currently being recovered at Oak Ridge National Laboratory (ORNL) and only those items for which there is no United States (U.S.) sponsor identified.

Preparation of uranium-plutonium mixed nitride pellets with high purity

International Nuclear Information System (INIS)

Arai, Yasuo; Shiozawa, Ken-ichi; Ohmichi, Toshihiko

1992-01-01

Uranium-plutonium mixed nitride pellets have been prepared in the gloveboxes with high purity Ar gas atmosphere. Carbothermic reduction of the oxides in N 2 -H 2 mixed gas stream was adopted for synthesizing mixed nitride. Sintering was carried out in various conditions and the effect on the pellet characteristics was investigated. (author)

Corrosion of Nickel-Based Alloys in Ultra-High Temperature Heat Transfer Fluid

Science.gov (United States)

Wang, Tao; Reddy, Ramana G.

2017-03-01

MgCl2-KCl binary system has been proposed to be used as high temperature reactor coolant. Due to its relatively low melting point, good heat capacity and excellent thermal stability, this system can also be used in high operation temperature concentrating solar power generation system as heat transfer fluid (HTF). The corrosion behaviors of nickel based alloys in MgCl2-KCl molten salt system at 1,000 °C were determined based on long-term isothermal dipping test. After 500 h exposure tests under strictly maintained high purity argon gas atmosphere, the weight loss and corrosion rate analysis were conducted. Among all the tested samples, Ni-201 demonstrated the lowest corrosion rate due to the excellent resistance of Ni to high temperature element dissolution. Detailed surface topography and corrosion mechanisms were also determined by using scanning electron microscopy (SEM) equipped with energy dispersive spectrometer (EDS).

Neutron activation analysis of high purity tellurium

International Nuclear Information System (INIS)

Gil'bert, Eh.N.; Verevkin, G.V.; Obrazovskij, E.G.; Shatskaya, S.S.

1980-01-01

A scheme of neutron activation analysis of high purity tellurium is developed. Weighed amount of Te (0.5 g) is irradiated for 20-40 hr in the flux of 2x10 13 neutron/(cm 2 xs). After decomposition of the sample impurities of gold and palladium are determined by the extraction with organic sulphides. Tellurium separation from the remaining impurities is carried out by the extraction with monothiobenzoic acid from weakly acidic HCl solutions in the presence of iodide-ions, suppressing silver extraction. Remaining impurity elements in the refined product are determined γ-spectrometrically. The method allows to determine 34 impurities with determination limits 10 -6 -10 -11 g

Neutron activation analysis of high-purity zinc

International Nuclear Information System (INIS)

Khodzhamberdyeva, A.A.; Usmanova, M.M.; Gil'bert, Eh.N.; Ivanov, I.M.; Yankovskaya, T.A.; Kholyavko, E.P.

1987-01-01

The methods of neutron activation analysis of high-purity zinc with preliminary separation of the zinc base using extraction by trialkylbenzylammonium rhodanide in carbon tetrachloride from 0.5-2.0 M nitric acid solutions is developed. Only rhenium is quantitatively extracted together with zinc. Gold, iridium and molybdenum are extracted to 50-60%, and selenium - to 20%. The Na, K, La, Cr, Sc, Co, Cs, Rb, Fe, Zr, Sn, Te, As, Cd, Hf, W, Sb, Sm impurities remain in the aqueous phase. The methods permits to determine the impurities above with detection limits from 1x10 -6 to 4x10 -11 g

Creating high-purity angular-momentum-state Rydberg atoms by a pair of unipolar laser pulses

Science.gov (United States)

Xin, PeiPei; Cheng, Hong; Zhang, ShanShan; Wang, HanMu; Xu, ZiShan; Liu, HongPing

2018-04-01

We propose a method of producing high-purity angular-momentum-state Rydberg atoms by a pair of unipolar laser pulses. The first positive-polarity optical half-cycle pulse is used to prepare an excited-state wave packet while the second one is less intense, but with opposite polarity and time delayed, and is employed to drag back the escaping free electron and clip the shape of the bound Rydberg wave packet, selectively increasing or decreasing a fraction of the angular-momentum components. An intelligent choice of laser parameters such as phase and amplitude helps us to control the orbital-angular-momentum composition of an electron wave packet with more facility; thus, a specified angular-momentum state with high purity can be achieved. This scheme of producing high-purity angular-momentum-state Rydberg atoms has significant application in quantum-information processing.

Effect of the microstructure on electrical properties of high-purity germanium

Science.gov (United States)

Podkopaev, O. I.; Shimanskii, A. F.; Molotkovskaya, N. O.; Kulakovskaya, T. V.

2013-05-01

The interrelation between the electrical properties and the microstructure of high-purity germanium crystals has been revealed. The electrical conductivity of polycrystalline samples increases and the life-time of nonequilibrium charge carriers in them decreases with a decrease in the crystallite sizes.

High-precision efficiency calibration of a high-purity co-axial germanium detector

Energy Technology Data Exchange (ETDEWEB)

Blank, B., E-mail: blank@cenbg.in2p3.fr [Centre d' Etudes Nucléaires de Bordeaux Gradignan, UMR 5797, CNRS/IN2P3, Université de Bordeaux, Chemin du Solarium, BP 120, 33175 Gradignan Cedex (France); Souin, J.; Ascher, P.; Audirac, L.; Canchel, G.; Gerbaux, M.; Grévy, S.; Giovinazzo, J.; Guérin, H.; Nieto, T. Kurtukian; Matea, I. [Centre d' Etudes Nucléaires de Bordeaux Gradignan, UMR 5797, CNRS/IN2P3, Université de Bordeaux, Chemin du Solarium, BP 120, 33175 Gradignan Cedex (France); Bouzomita, H.; Delahaye, P.; Grinyer, G.F.; Thomas, J.C. [Grand Accélérateur National d' Ions Lourds, CEA/DSM, CNRS/IN2P3, Bvd Henri Becquerel, BP 55027, F-14076 CAEN Cedex 5 (France)

2015-03-11

A high-purity co-axial germanium detector has been calibrated in efficiency to a precision of about 0.15% over a wide energy range. High-precision scans of the detector crystal and γ-ray source measurements have been compared to Monte-Carlo simulations to adjust the dimensions of a detector model. For this purpose, standard calibration sources and short-lived online sources have been used. The resulting efficiency calibration reaches the precision needed e.g. for branching ratio measurements of super-allowed β decays for tests of the weak-interaction standard model.

Research of a novel biodegradable surgical staple made of high purity magnesium

Directory of Open Access Journals (Sweden)

Hongliu Wu

2016-12-01

Full Text Available Surgical staples made of pure titanium and titanium alloys are widely used in gastrointestinal anastomosis. However the Ti staple cannot be absorbed in human body and produce artifacts on computed tomography (CT and other imaging examination, and cause the risk of incorrect diagnosis. The bioabsorbable staple made from polymers that can degrade in human body environment, is an alternative. In the present study, biodegradable high purity magnesium staples were developed for gastric anastomosis. U-shape staples with two different interior angles, namely original 90° and modified 100°, were designed. Finite element analysis (FEA showed that the residual stress concentrated on the arc part when the original staple was closed to B-shape, while it concentrated on the feet for the modified staple after closure. The in vitro tests indicated that the arc part of the original staple ruptured firstly after 7 days immersion, whereas the modified one kept intact, demonstrating residual stress greatly affected the corrosion behavior of the HP-Mg staples. The in vivo implantation showed good biocompatibility of the modified Mg staples, without inflammatory reaction 9 weeks post-operation. The Mg staples kept good closure to the Anastomosis, no leaking and bleeding were found, and the staples exhibited no fracture or severe corrosion cracks during the degradation.

High purity liquid phase epitaxial gallium arsenide nuclear radiation detector

International Nuclear Information System (INIS)

Alexiev, D.; Butcher, K.S.A.

1991-11-01

Surface barrier radiation detector made from high purity liquid phase epitaxial gallium arsenide wafers have been operated as X- and γ-ray detectors at various operating temperatures. Low energy isotopes are resolved including 241 Am at 40 deg C. and the higher gamma energies of 235 U at -80 deg C. 15 refs., 1 tab., 6 figs

Native oxidation of ultra high purity Cu bulk and thin films

International Nuclear Information System (INIS)

Iijima, J.; Lim, J.-W.; Hong, S.-H.; Suzuki, S.; Mimura, K.; Isshiki, M.

2006-01-01

The effect of microstructure and purity on the native oxidation of Cu was studied by using angle-resolved X-ray photoelectron spectroscopy (AR-XPS) and spectroscopic ellipsometry (SE). A high quality copper film prepared by ion beam deposition under a substrate bias voltage of -50 V (IBD Cu film at V s = -50 V) showed an oxidation resistance as high as an ultra high purity copper (UHP Cu) bulk, whereas a Cu film deposited without substrate bias voltage (IBD Cu film at V s = 0 V) showed lower oxidation resistance. The growth of Cu 2 O layer on the UHP Cu bulk and both types of the films obeyed in principle a logarithmic rate law. However, the growth of oxide layer on the IBD Cu films at V s = 0 and -50 V deviated upward from the logarithmic rate law after the exposure time of 320 and 800 h, respectively. The deviation from the logarithmic law is due to the formation of CuO on the Cu 2 O layer after a critical time

Deuterium permeation and diffusion in high-purity beryllium

International Nuclear Information System (INIS)

Abramov, E.; Riehm, M.P.; Thompson, D.A.; Smeltzer, W.W.

1990-01-01

The permeation rate of deuterium through high-purity beryllium membranes was measured using the gas-driven permeation technique. The time-dependent and the steady-state deuterium flux data were analyzed and the effective diffusivities of the samples were determined. Using multilayer permeation theory the effects of surface oxide were eliminated and the diffusion coefficients of the bulk beryllium determined. The diffusion parameters obtained for the extra-grade beryllium samples (99.8%) are D 0 =6.7x10 -9 m 2 /s and E D =28.4 kJ/mol. For the high-grade beryllium samples (99%) the parameters are D 0 =8.0x10 -9 m 2 /s and E D =35.1 kJ/mol. (orig.)

Influence of Magnesium Alloy Degradation on Undifferentiated Human Cells.

Science.gov (United States)

Cecchinato, Francesca; Agha, Nezha Ahmad; Martinez-Sanchez, Adela Helvia; Luthringer, Berengere Julie Christine; Feyerabend, Frank; Jimbo, Ryo; Willumeit-Römer, Regine; Wennerberg, Ann

2015-01-01

Magnesium alloys are of particular interest in medical science since they provide compatible mechanical properties with those of the cortical bone and, depending on the alloying elements, they have the capability to tailor the degradation rate in physiological conditions, providing alternative bioresorbable materials for bone applications. The present study investigates the in vitro short-term response of human undifferentiated cells on three magnesium alloys and high-purity magnesium (Mg). The degradation parameters of magnesium-silver (Mg2Ag), magnesium-gadolinium (Mg10Gd) and magnesium-rare-earth (Mg4Y3RE) alloys were analysed after 1, 2, and 3 days of incubation in cell culture medium under cell culture condition. Changes in cell viability and cell adhesion were evaluated by culturing human umbilical cord perivascular cells on corroded Mg materials to examine how the degradation influences the cellular development. The pH and osmolality of the medium increased with increasing degradation rate and it was found to be most pronounced for Mg4Y3RE alloy. The biological observations showed that HUCPV exhibited a more homogeneous cell growth on Mg alloys compared to high-purity Mg, where they showed a clustered morphology. Moreover, cells exhibited a slightly higher density on Mg2Ag and Mg10Gd in comparison to Mg4Y3RE, due to the lower alkalinisation and osmolality of the incubation medium. However, cells grown on Mg10Gd and Mg4Y3RE generated more developed and healthy cellular structures that allowed them to better adhere to the surface. This can be attributable to a more stable and homogeneous degradation of the outer surface with respect to the incubation time.

State-of-the-art in analytical characterization of high purity solid ...

Indian Academy of Sciences (India)

Facilities and some results of several spectroscopic methods which have potential applications in the field of analysis of solid high purity substances and which have been elaborated in Russia, will be discussed in this paper. Laser nondispersive atomic fluorescence method with glow discharge cathode sputtering atomiser, ...

Fabrication of novel cryomill for synthesis of high purity metallic nanoparticles

Science.gov (United States)

Kumar, Nirmal; Biswas, Krishanu

2015-08-01

The successful preparation of free standing metal nanoparticles with high purity in bulk quantity is the pre-requisite for any potential application. This is possible by using ball milling at cryogenic temperature. However, the most of ball mills available in the market do not allow preparing high purity metal nanoparticles by this route. In addition, it is not possible to carry out in situ measurements of process parameters as well as diagnostic of the process. In the present investigation, we present a detailed study on the fabrication of a cryomill, which is capable of avoiding contaminations in the product. It also provides in situ measurements and diagnostic of the low temperature milling process. Online monitoring of the milling temperature and observation of ball motion are the important aspects in the newly designed mill. The nanoparticles prepared using this fabricated mill have been found to be free standing and also free from contaminations.

Nickel alloys and high-alloyed special stainless steels. Properties, manufacturing, applications. 4. compl. rev. ed.

International Nuclear Information System (INIS)

Heubner, Ulrich; Kloewer, Jutta; Alves, Helena; Behrens, Rainer; Schindler, Claudius; Wahl, Volker; Wolf, Martin

2012-01-01

This book contains the following eight topics: 1. Nickel alloys and high-alloy special stainless steels - Material overview and metallurgical principles (U. Heubner); 2. Corrosion resistance of nickel alloys and high-alloy special stainless steels (U. Heubner); 3. Welding of nickel alloys and high-alloy special stainless steels (T. Hoffmann, M. Wolf); 4. High-temperature materials for industrial plant construction (J. Kloewer); 5. Nickel alloys and high-alloy special stainless steels as hot roll clad composites-a cost-effective alternative (C. Schindler); 6. Selected examples of the use of nickel alloys and high-alloy special stainless steels in chemical plants (H. Alves); 7. The use of nickel alloys and stainless steels in environmental engineering (V. Wahl); 8: Nickel alloys and high-alloy special stainless steels for the oil and gas industry (R. Behrens).

Modification of Al-Si (13%) alloy using different modifiers

International Nuclear Information System (INIS)

Ikram, N.; Raza, M.R.; Ahmad, R.

2007-01-01

During present research work LM 13 aluminium silicon alloy was prepared using high purity aluminium ingot and various master alloys of AI-Si, AI-Cu, AI-Ni, AIFe, AI-Mn and AI-Mg. A gas fired crucible pit type furnace was used to prepare various heats of LM 13 alloy. Degassing procedure was carried out by using perforated bell type plunger using the degassing tablet. Modification was performed by plunging the modifier at the bottom of the crucible containing the molten metal. Three types of modifiers sodium salt, metallic sodium and strontium in the form of AI-Sr master alloy were used in order to evaluate the microstructure and tensile properties of the alloy. Degassed, unmodified and modified test samples for metallurgical testing purposes were prepared according to the standard procedures. (author)

High purity zirconium obtainment through the iodine compounds transport method

International Nuclear Information System (INIS)

Bolcich, J.C.; Zuzek, E.; Dutrus, S.M.; Corso, H.L.

1987-01-01

This paper describes the experimental method and the equipment designed, constructed and actually applied for the high purity zirconium obtainment from a zirconium sponge of the nuclear type. The mechanism of purification is based on the impure metal attack with gaseous iodine (at 200 deg C) to obtain zirconium tetra iodine as main product which is then transformed into a pure zirconium base (at 1000-1300 deg C), precipitating the metallic zirconium and releasing the gaseous iodine. From the first experiences carried out, pure zirconium has been obtained from an initial filament of 0.5 mm of diameter as well as wires up to 2.5 mm of diameter. This work presents the results from the studies and analysis made to characterize the material obtained. Finally, the refining methods to which the zirconium produced may be submitted so as to optimize the final purity are discussed. (Author)

Recycling of high purity selenium from CIGS solar cell waste materials

Energy Technology Data Exchange (ETDEWEB)

Gustafsson, Anna M.K., E-mail: anna.gustafsson@chalmers.se; Foreman, Mark R.StJ.; Ekberg, Christian

2014-10-15

Highlights: • A new method for recycling of selenium from CIGS solar cell materials is presented. • Separation of selenium as selenium dioxide after heating in oxygen atmosphere. • Complete selenium separation after oxidation of <63 μm particles at 800 °C for 1 h. • After reduction of selenium dioxide the selenium purity was higher than 99.999 wt%. - Abstract: Copper indium gallium diselenide (CIGS) is a promising material in thin film solar cell production. To make CIGS solar cells more competitive, both economically and environmentally, in comparison to other energy sources, methods for recycling are needed. In addition to the generally high price of the material, significant amounts of the metals are lost in the manufacturing process. The feasibility of recycling selenium from CIGS through oxidation at elevated temperatures was therefore examined. During oxidation gaseous selenium dioxide was formed and could be separated from the other elements, which remained in solid state. Upon cooling, the selenium dioxide sublimes and can be collected as crystals. After oxidation for 1 h at 800 °C all of the selenium was separated from the CIGS material. Two different reduction methods for reduction of the selenium dioxide to selenium were tested. In the first reduction method an organic molecule was used as the reducing agent in a Riley reaction. In the second reduction method sulphur dioxide gas was used. Both methods resulted in high purity selenium. This proves that the studied selenium separation method could be the first step in a recycling process aimed at the complete separation and recovery of high purity elements from CIGS.

An ICP AES method for determination of dysprosium and terbium in high purity yttrium oxide

International Nuclear Information System (INIS)

Rupawate, V.H.; Hareendran, K.N.; Roy, S.B.

2011-01-01

High purity yttrium finds interesting application in astronavigation, luminescence, nuclear energy and metallurgical industries. Most of these applications require yttrium oxide of highest purity. Consequently there is a need for production of high purity yttrium oxide. Separation and purification of yttrium from other rare earths is a challenging task due to their close chemical properties. Liquid-liquid extraction and ion exchange have been widely used in the production of yttrium oxide of highest purity. Determination of impurities, especially other rare earths, in ppm level is required for process development and chemical characterization of the high purity Y 2 O 3 . Many methods have been described in literature. However since the advent of ICP AES much work in this area has been carried out by this technique. This paper describes the work done for determination of dysprosium (Dy) and terbium (Tb) in yttrium oxide using a high resolution sequential ICP AES. Emission spectra of rare earth elements are very complex and due to this complexity it is important to select spectral interference free analyte lines for determination of rare earths in rare earth matrix. For the determination of Dy and Tb in Y 2 O 3 , sensitive lines of Dy and Tb are selected from the instrument wavelength table and spectral interference free emission lines for the determination is selected by scanning around the selected wavelengths using 5 g/L Y solution and 5 mg/L standard solutions of Dy and Tb prepared in 4% nitric acid. It is found 353.170 nm line of Dy and 350.917 nm line Tb is suitable for quantitative determination. The signal to background ratio increases with increase in matrix concentration, i.e. from 1 to 5 mg/L. The optimum forward power is determined and it is found to be 1100W for Dy and 1000W for Tb. The instrument is calibrated using matrix matched standards containing 5g/L of Y matrix. Samples are dissolved in nitric acid and Y concentration is maintained at 5g/L. Two

High purity samarium oxide from mixed rare earth carbonates

International Nuclear Information System (INIS)

Queiroz, Carlos A. da S.; Seneda, Jose A.; Vasconcellos, Mari E. de; Pedreira Filho, Walter dos R.

2013-01-01

A simple and economical chemical process for the production of highly pure samarium oxides is discussed. The raw material, which was used in the form of rare earth carbonates was produced industrially from the chemical treatment of Brazilian monazite. Ion exchange chromatography was performed using a strong cationic resin that is typically employed in water treatment processes to fractionate rare earth elements (REE) without the use of retention ions. Under these conditions, 99.9% pure Sm 2 O 3 was eluted using the ammonium salt of ethylenediaminetetraacetic acid (EDTA) at a controlled pH. The EDTA-samarium complex was separated from EDTA and then precipitated as oxalate and fired to samarium oxide. Molecular absorption spectrophotometry was used to monitor the samarium content during the proposed process, and sector field inductively coupled plasma mass spectrometry was used to certify the purity of the samarium oxide. Typical samarium oxide obtained from the proposed procedure contained the following contaminants in micrograms per gram: Sc (20.90); Y (11.80); La (8.4); Ce (4.3); Pr (2.5); Nd (5.1); Eu (94); Gd (114); Tb (3.6); Dy (2.5), Ho (2.3); Er (3.0); Tm (2.3); Yb (38,2); Lu (25.6). The high-purity samarium oxides produced in the present study can be used as an alternative to imported products in research and development applications. (author)

Deuterium permeation and diffusion in high purity beryllium

International Nuclear Information System (INIS)

Abramov, E.

1990-05-01

The permeation rate of deuterium through high-purity beryllium membranes was measured using the gas-driven permeation technique. The time-dependent and the steady-state deuterium flux data were analyzed and the effective diffusivities of the samples were determined. A multilayer permeation theory was used in order to eliminate the surface oxide effects and the diffusion coefficients of the bulk beryllium were determined. The diffusion parameters obtained for the extra-grade beryllium samples (99.8%) are D 0 = 6.7 x 10 -9 [m 2 /s] and E D = 28.4 [KJ/mol]; and for the high-grade beryllium samples (99%) the parameters are D 0 = 8.0 x 10 -9 [m 2 /s] and E D = 35.1 [KJ/mol

Recovery of high-purity metallic Pd from Pd(II)-sorbed biosorbents by incineration.

Science.gov (United States)

Won, Sung Wook; Lim, Areum; Yun, Yeoung-Sang

2013-06-01

This work reports a direct way to recover metallic palladium with high purity from Pd(II)-sorbed polyethylenimine-modified Corynebacterium glutamicum biosorbent using a combined method of biosorption and incineration. This study is focused on the incineration part which affects the purity of recovered Pd. The incineration temperature and the amount of Pd loaded on the biosorbent were considered as major factors in the incineration process, and their effects were examined. The results showed that both factors significantly affected the enhancement of the recovery efficiency and purity of the recovered Pd. SEM-EDX and XRD analyses were used to confirm that Pd phase existed in the ash. As a result, the recovered Pd was changed from PdO to zero-valent Pd as the incineration temperature was increased from 600 to 900°C. Almost 100% pure metallic Pd was recovered with recovery efficiency above 99.0% under the conditions of 900°C and 136.9 mg/g. Copyright © 2013 Elsevier Ltd. All rights reserved.

Contribution of the low cycle fatigue on ultra high purity Ni-Cr-Fe alloys and on Ni monocrystals to the understanding of the hydrogen role in stress corrosion cracking for the alloys 600 and 690; Apport de la fatigue oligocyclique sur alliages Ni-Cr-Fe d'ultra haute purete et sur monocristaux de Ni a la comprehension sous contrainte des alliages 600 et 69O

Energy Technology Data Exchange (ETDEWEB)

Renaudot, N

1999-06-01

We discuss the role of hydrogen in cracking of Ni base alloys used for pressurised water reactor (PWR) primary tubes (alloy 600 and 690). Cracking can be explained by a Stress Corrosion Cracking (SCC) phenomenon. For this purpose, Low cycle fatigue (R = - 1) under cathodic charging at room temperature is conducted to study hydrogen effects on propagation of cracks mechanically initiated by the formation of Persistent Slip Bands (PSB). Low cycle fatigue on Ultra High Purity specimens (Ni, alloy 600 and 690) reveals the very important hydrogen effect on crack propagation rate, whatever the Cr content in the Ni base alloy. If Cr seems to have an effect over-hydrogen penetration in specimens (by a protective film formation), it have no beneficial effect when hydrogen have diffused ahead of a crack tip. Propagation rates (transgranular or intergranular) are highly increased, no matter of the absence of impurities like sulphur. Then, in PWR, the difference in the behaviour of alloy 600 and 690 could be due to a slower microcrack propagation rate for alloy 690. Protective films could play an important role in this difference, which is to study. Low cycle fatigue on Ni single crystals oriented for single slip shows, for the first time on bulk specimen, a macroscopic softening which can be explained. by hydrogen-dislocation interactions. Moreover, a simple quantitative model based on these interactions results in the same softening as the one observed experimentally. These results allow to validate experimentally one of the most important steps in the 'Corrosion Enhanced Plasticity (CEP) model', i.e. the softening ahead of a stress corrosion crack tip by hydrogen dislocation interactions. This is of importance because this model can explain cracking in numerous FCC materials-environment couple. (author)

Influence of Magnesium Alloy Degradation on Undifferentiated Human Cells.

Directory of Open Access Journals (Sweden)

Francesca Cecchinato

Full Text Available Magnesium alloys are of particular interest in medical science since they provide compatible mechanical properties with those of the cortical bone and, depending on the alloying elements, they have the capability to tailor the degradation rate in physiological conditions, providing alternative bioresorbable materials for bone applications. The present study investigates the in vitro short-term response of human undifferentiated cells on three magnesium alloys and high-purity magnesium (Mg.The degradation parameters of magnesium-silver (Mg2Ag, magnesium-gadolinium (Mg10Gd and magnesium-rare-earth (Mg4Y3RE alloys were analysed after 1, 2, and 3 days of incubation in cell culture medium under cell culture condition. Changes in cell viability and cell adhesion were evaluated by culturing human umbilical cord perivascular cells on corroded Mg materials to examine how the degradation influences the cellular development.The pH and osmolality of the medium increased with increasing degradation rate and it was found to be most pronounced for Mg4Y3RE alloy. The biological observations showed that HUCPV exhibited a more homogeneous cell growth on Mg alloys compared to high-purity Mg, where they showed a clustered morphology. Moreover, cells exhibited a slightly higher density on Mg2Ag and Mg10Gd in comparison to Mg4Y3RE, due to the lower alkalinisation and osmolality of the incubation medium. However, cells grown on Mg10Gd and Mg4Y3RE generated more developed and healthy cellular structures that allowed them to better adhere to the surface. This can be attributable to a more stable and homogeneous degradation of the outer surface with respect to the incubation time.

High-purity Cu nanocrystal synthesis by a dynamic decomposition method

OpenAIRE

Jian, Xian; Cao, Yu; Chen, Guozhang; Wang, Chao; Tang, Hui; Yin, Liangjun; Luan, Chunhong; Liang, Yinglin; Jiang, Jing; Wu, Sixin; Zeng, Qing; Wang, Fei; Zhang, Chengui

2014-01-01

Cu nanocrystals are applied extensively in several fields, particularly in the microelectron, sensor, and catalysis. The catalytic behavior of Cu nanocrystals depends mainly on the structure and particle size. In this work, formation of high-purity Cu nanocrystals is studied using a common chemical vapor deposition precursor of cupric tartrate. This process is investigated through a combined experimental and computational approach. The decomposition kinetics is researched via differential sca...

Hydrogen in niobium-titanium alloys

International Nuclear Information System (INIS)

Silva, J.R.G. da; Cabral, F.A.O.; Florencio, O.

1985-01-01

High purity Nb-Ti polycrystalline alloys were doped with hydrogen in equilibrium with the gaseous atmosphere at a pressure of 80 torr. at different temperatures. The partial molar enthalpy and entropy of the hydrogen solution at high dilution, ΔH sup(-) 0 and ΔS sup(-) 0 , were calculated from the equilibrium solubility data. The ΔH sup(-) 0 values are compared with the electron screened proton model of metal-hydrogen solutions. The addition of titanium to niobium has the effect to increase the hydrogen solubility at a given equilibrium temperature. (Author) [pt

Alloying effect of 3D transition elements on the ductility of chromium

International Nuclear Information System (INIS)

Matsumoto, Y.; Fukumori, J.; Morinaga, M.; Furui, M.; Nambu, T.; Sakaki, T.

1996-01-01

Chromium and its alloys have good corrosion resistance in corrosive environments and good oxidation resistance at high temperatures. In addition, they exhibit an excellent combination of low density and high creep strength. However, there is still a large barrier to the practical use because of their poor ductility at room temperature. According to recent investigations, an environmental effect was found on the ductility of high purity polycrystalline chromium. In this study, in order to find a way to improve the ductility of chromium at room temperature, the alloying effect on the ductility of chromium was investigated experimentally in several test environments

Simultaneous determination of dysprosium, holmium and erbium in high purity rare earth oxides by second order derivative spectrophotometry

International Nuclear Information System (INIS)

Anbu, M.; Prasada Rao, T.; Iyer, C. S. P.; Damodaran, A. D.

1996-01-01

High purity individual rare earth oxides are increasingly used as major components in lasers (Y 2 O 3 ), phosphors (YVO 3 , Eu 2 O 3 ), magnetic bubble memory films (Gd 2 O 3 ) and refractive-index lenses and fibre optics (La 2 O 3 ). The determination of individual lanthanides in high purity rare earth oxides is a more important and difficult task. This paper reports the utilization of higher order derivative spectrophotometry for the simultaneous determination of dysprosium, holmium and erbium in high purity rare earth oxides. The developed procedure is simple, reliable and allows the determination of 0.001 to 0.2% of dysprosium, holmium and erbium in several rare earth. (author). 9 refs, 2 figs, 2 tabs

Report on the FY 1999 research survey on the development of high ductile chromium alloys; 1999 nendo koensei kuromu gokin no kaihatsu ni kansuru kenkyu chosa hokokusho

Energy Technology Data Exchange (ETDEWEB)

NONE

2000-03-01

The R and D of chromium alloys had been conducted till about the 1970s, which brought the unfavorable results. That's why chromium alloys are brittle at normal temperature and difficult in processing. However, the technology development in recent years review them. The development is earnestly desired also of the materials exceeding the Ni base super alloys which are heat resistant materials for power generation. Cr is rich as resource and light-weighted, and the oxidation film is stable and self-restorational at high temperature. The alloys are excellent in processability at normal temperature and excellent also in toughness. The nitrogen content is strongly concerned with brittleness and intergranular fracture at normal temperature. Therefore, Cr alloys were trially manufactured by the HIP sintering/hot forging method using electrolytic Cr powder with high-purity (99.99%) and low-nitrogen (10ppm) to study a possibility of improving brittleness at normal temperature, mechanical properties at high temperature, oxidation resistance, high-temperature corrosion resistance, etc. A variety of excellent characteristics of Cr alloys were made clear. However, also made clear were the problems: strength is low at normal temperature/high temperature; screw process is impossible because of high notch sensibility; those are not almighty high-temperature corrosion resistant materials. Further efforts should be exerted for the commercialization. (NEDO)

A highly ductile magnesium alloy system

International Nuclear Information System (INIS)

Gao, W; Liu, H

2009-01-01

Magnesium (Mg) alloys are finding increasing applications in industry mainly due to their high strength-to-weight ratio. However, they have intrinsically poor plastic deformation ability at room temperature. Therefore, the vast majority of Mg alloys are used only in cast state, severely limiting the development of their applications. We have recently discovered a new Mg alloy system that possesses exceptionally high ductility as well as good mechanical strength. The superior plasticity allows this alloy system to be mechanically deformed at room temperature, directly from an as-cast alloy plate, sheet or ingot into working parts. This type of cold mechanical forming properties has never been reported with any other Mg alloy systems.

Solidification processing of intermetallic Nb-Al alloys

Science.gov (United States)

Smith, Preston P.; Oliver, Ben F.; Noebe, Ronald D.

1992-01-01

Several Nb-Al alloys, including single-phase NbAl3 and the eutectic of Nb2Al and NbAl3, were prepared either by nonconsumable arc melting in Ar or by zone processing in He following initial induction melting and rod casting, and the effect of the solidification route on the microstructure and room-temperature mechanical properties of these alloys was investigated. Automated control procedures and melt conditions for directional solidification of NbAl3 and the Nb2Al/Nb3Al eutectic were developed; high purity and stoichiometry were obtained. The effects of ternary additions of Ti and Ni are described.

Dissolution of high-purity lead and subsequent crystal growth during the preparation of corrosion coupons

Energy Technology Data Exchange (ETDEWEB)

McGarvey, G.B. [Atomic Energy of Canada Limited, Chalk River, Ontario (Canada); McDougall, T.E.; Owen, D.G. [Atomic Energy of Canada Limited, Pinawa, Manitoba (Canada)

1997-07-01

High-purity lead discs were prepared using several combinations of polishing, rinsing and ultrasonic treatment. Physical degradation of the lead surface and the premature generation and deposition of oxides on the surface were observed for certain combinations of preparation steps. Ultrasonic treatment of the discs was found to be particularly detrimental as it induced significant crystal growth and, in several instances, deterioration of the polished surface. Simple air drying of freshly rinsed discs also led to oxide formation on the surface after as short a time as 1 min. An effective method for preparing discs from high-purity lead is described. (author)

Dissolution of high-purity lead and subsequent crystal growth during the preparation of corrosion coupons

International Nuclear Information System (INIS)

McGarvey, G.B.; McDougall, T.E.; Owen, D.G.

1997-01-01

High-purity lead discs were prepared using several combinations of polishing, rinsing and ultrasonic treatment. Physical degradation of the lead surface and the premature generation and deposition of oxides on the surface were observed for certain combinations of preparation steps. Ultrasonic treatment of the discs was found to be particularly detrimental as it induced significant crystal growth and, in several instances, deterioration of the polished surface. Simple air drying of freshly rinsed discs also led to oxide formation on the surface after as short a time as 1 min. An effective method for preparing discs from high-purity lead is described. (author)

Vacuum-induction melting, refining, and casting of uranium and its alloys

Energy Technology Data Exchange (ETDEWEB)

Jackson, R J

1989-10-11

The vacuum-induction melting (VIM), refining, and casting of uranium and its alloys are discussed. Emphasis is placed on historical development, VIM equipment, crucible and mold design, furnace atmospheres, melting parameters, impurity pickup, ingot quality, and economics. The VIM procedures used to produce high-purity, high-quality sound ingots at the US Department of Energy Rocky Flats Plant are discussed in detail.

Release characteristics of tritium from high-purity lithium oxide

International Nuclear Information System (INIS)

O'Kula, K.R.; Vogelsang, W.F.

1985-01-01

Rates of tritium release from neutronirradiated lithium oxide were determined from isothermal release experiments. High-purity, monocrystalline lithium oxide was purged ex-reactor with helium and helium-hydrogen gas streams. Overall release was found to be controlled by solid-phase diffusion, and was predominantly in the form of condensible species. The result of an independent concentration profile analysis at 923 K was in agreement with the gas release diffusion coefficient. Sweeping the Li 2 O with hydrogen-containing gas was found to enhance tritium removal during the early stage of each run

Manufacturing of High Entropy Alloys

Science.gov (United States)

Jablonski, Paul D.; Licavoli, Joseph J.; Gao, Michael C.; Hawk, Jeffrey A.

2015-07-01

High entropy alloys (HEAs) have generated interest in recent years due to their unique positioning within the alloy world. By incorporating a number of elements in high proportion they have high configurational entropy, and thus they hold the promise of interesting and useful properties such as enhanced strength and phase stability. The present study investigates the microstructure of two single-phase face-centered cubic (FCC) HEAs, CoCrFeNi and CoCrFeNiMn, with special attention given to melting, homogenization and thermo-mechanical processing. Large-scale ingots were made by vacuum induction melting to avoid the extrinsic factors inherent in small-scale laboratory button samples. A computationally based homogenization heat treatment was applied to both alloys in order to eliminate segregation due to normal ingot solidification. The alloys fabricated well, with typical thermo-mechanical processing parameters being employed.

Trace elements in high purity materials for advanced technology: contribution of neutron activation analysis and radioanalytical technique

International Nuclear Information System (INIS)

Gallorini, M.; Pietra, R.; Sabbioni, E.

1991-01-01

Neutron activation analysis and radioanalytical techniques have been employed to investigate problems related to trace elements and high purity technology materials. Applications of these techniques are overviewed: semiconductor technology as in the case of As and In ion implantation in high purity silicon; problems related to trace elements impurities in thermometric measurements; coating materials to prevent trace elements contamination in biological sampling and metals release from human prostheses. (author) 8 refs.; 2 figs.; 8 tabs

Nucleation and growth of fatigue cracks in magnesium alloys of different structure

International Nuclear Information System (INIS)

Grinberg, N.M.; Serdyuk, V.A.; Malinkina, T.I.; Kamyshkov, A.S.

1982-01-01

Duration of the fatigue crack nucleation and growth rate have been in a wide range of stress intensity factor variations for MA2-1, MA2-1 hp (higher purity), MA12, (T2, T6 and T8), MA15, IMB6, MA21 magnesium alloys of different composition and structural state. The threshold and criti- cal values of stress intensity factors, Ksub(th) and Ksub(fc) are determined for those alloys, and morphology of fracture is studied at different stages of crack growth. Duration of the nucleation stage of a fatigue crack, the rate and micromechanisms of its growth are found to depedend on alloying and structural state of magnesium alloys. The best crack resistance characteristics has the MA2-1 alloy, the poorest - MA12 (T2) alloy. It is stated that thermal treatment by hardening and ageing increases the resistance of the MA12 alloy to fatigue fracture and the MA2-1 alloy of higher purity gives poorer parameters of crack resistance [ru

Process for producing high purity isoolefins and dimers thereof by dissociation of ethers

Science.gov (United States)

Smith, L.A. Jr.; Jones, E.M. Jr.; Hearn, D.

1984-05-08

Alkyl tertiary butyl ether or alkyl tertiary amyl ether is dissociated by vapor phase contact with a cation acidic exchange resin at temperatures in the range of 150 to 250 F at LHSV of 0.1 to 20 to produce a stream consisting of unreacted ether, isobutene or isoamylene and an alcohol corresponding to the alkyl radical. After the alcohol is removed, the ether/isoolefin stream may be fractionated to obtain a high purity isoolefin (99+%) or the ether/isoolefin stream can be contacted in liquid phase with a cation acidic exchange resin to selectively dimerize the isoolefin in a highly exothermic reaction, followed by fractionation of the dimerization product to produce high purity diisoolefin (97+%). In the case where the alkyl is C[sub 3] to C[sub 6] and the corresponding alcohol is produced on dissociation of the ether, combined dissociation-distillation may be carried out such that isoolefin is the overhead product and alcohol the bottom. 2 figs.

Preparation of High Purity CdTe for Nuclear Detector: Electrical and Nuclear Characterization

Science.gov (United States)

Zaiour, A.; Ayoub, M.; Hamié, A.; Fawaz, A.; Hage-ali, M.

High purity crystal with controllable electrical properties, however, control of the electrical properties of CdTe has not yet been fully achieved. Using the refined Cd and Te as starting materials, extremely high-purity CdTe single crystals were prepared by the traditional vertical THM. The nature of the defects involved in the transitions was studied by analyzing the position of the energy levels by TSC method. The resolution of 4.2 keV (FWHM) confirms the high quality and stability of the detectors: TSC spectrum was in coherence with detectors spectrum with a horizontal plate between 0.2 and 0.6 eV. The enhancement in resolution of detectors with a full width at half- maximum (less than 0.31 meV), lead to confirm that the combination of vacuum distillation and zone refining was very effective to obtain more purified CdTe single crystals for photovoltaic or nuclear detectors with better physical properties.

High-Purity Fe3S4 Greigite Microcrystals for Magnetic and Electrochemical Performance

NARCIS (Netherlands)

Li, Guowei; Zhang, Baomin; Yu, Feng; Novakova, Alla A.; Krivenkov, Maxim S.; Kiseleva, Tatiana Y.; Chang, Liao; Rao, Jiancun; Polyakov, Alexey O.; Blake, Graeme R.; de Groot, Robert A.; Palstra, Thomas T. M.

2014-01-01

High-purity Fe3S4 (greigite) microcrystals with octahedral shape were synthesized via a simple hydrothermal method using a surfactant. The as-prepared samples have the inverse spinel structure with high crystallinity. The saturation magnetization (M-s) reaches 3.74 mu(B) at 5 K and 3.51 mu(B) at

Approaches to the accurate characterization of high purity metal fluorides and fluoride glasses

Science.gov (United States)

Beary, E. S.; Paulsen, P. J.; Rains, T. C.; Ewing, K. J.; Jaganathan, J.; Aggarwal, I.

1990-11-01

The analytical challenges posed by the measurement of trace contaminants in high purity metal fluorides require that innovative chemical preparation procedures be used to enhance existing instrumental techniques. The instrumental techniques used to analyze these difficult matrices must be sensitive enough to detect extremely low levels of trace impurities, and the background interferences derived from the matrix (metal fluoride or glass) must be minimized. A survey of analytical techniques that have the necessary characteristics to analyze these materials will be given. In addition, means of controlling the chemical blank will be presented. Mass and atomic spectrometric techniques will be discussed, specifically graphite furnace atomic absorption spectrometry (GFAAS) and inductively coupled plasma-mass spectrometry (ICP-MS). Analytical procedures using GFAAS and ICP-MS have been developed to determine sub ppb (part per billion) levels of contaminants in high purity fluoride materials.

Recent developments in high purity niobium metal production at CBMM

International Nuclear Information System (INIS)

Abdo, Gustavo Giovanni Ribeiro; Sousa, Clovis Antonio de Faria; Guimarães, Rogério Contato; Ribas, Rogério Marques; Vieira, Alaércio Salvador Martins; Menezes, Andréia Duarte; Fridman, Daniel Pallos; Cruz, Edmundo Burgos

2015-01-01

CBMM is a global supplier of high quality niobium products including pure niobium, the focus of this paper. CBMM’s position has been consolidated over three decades of producing high purity niobium metal ingots. The company supplies, among other products, commercial and reactor grade niobium ingots. One of the main uses of CBMM’s ingots is for the manufacture of particle accelerators (superconducting radio frequency – SRF – cavities), where the purity and homogeneity of niobium metal is essentially important for good performance. CBMM constantly strives to improve process controls and product quality, and is currently implementing innovations in production, research and development to further improve ingot quality. The main aim is to reduce the content of interstitial elements, such as nitrogen (N), oxygen (O), carbon (C), and hydrogen (H), starting with the raw materials through the final step of ingot production. CBMM held the first trial to produce the world’s largest-diameter niobium ingot (as cast 535 mm). The results of this initial trial presented very low levels of interstitial impurities (N, O, C, H), allowing the achievement of residual resistivity ratio (RRR) values very close to 300 in a six-melt process in an electron beam furnace. These values were reached with 850 ppm of tantalum. SRF cavities will be produced with this material in order to study the effect of low impurities and high RRR on the Q factor and accelerating gradient

Phonon broadening in high entropy alloys

Science.gov (United States)

Körmann, Fritz; Ikeda, Yuji; Grabowski, Blazej; Sluiter, Marcel H. F.

2017-09-01

Refractory high entropy alloys feature outstanding properties making them a promising materials class for next-generation high-temperature applications. At high temperatures, materials properties are strongly affected by lattice vibrations (phonons). Phonons critically influence thermal stability, thermodynamic and elastic properties, as well as thermal conductivity. In contrast to perfect crystals and ordered alloys, the inherently present mass and force constant fluctuations in multi-component random alloys (high entropy alloys) can induce significant phonon scattering and broadening. Despite their importance, phonon scattering and broadening have so far only scarcely been investigated for high entropy alloys. We tackle this challenge from a theoretical perspective and employ ab initio calculations to systematically study the impact of force constant and mass fluctuations on the phonon spectral functions of 12 body-centered cubic random alloys, from binaries up to 5-component high entropy alloys, addressing the key question of how chemical complexity impacts phonons. We find that it is crucial to include both mass and force constant fluctuations. If one or the other is neglected, qualitatively wrong results can be obtained such as artificial phonon band gaps. We analyze how the results obtained for the phonons translate into thermodynamically integrated quantities, specifically the vibrational entropy. Changes in the vibrational entropy with increasing the number of elements can be as large as changes in the configurational entropy and are thus important for phase stability considerations. The set of studied alloys includes MoTa, MoTaNb, MoTaNbW, MoTaNbWV, VW, VWNb, VWTa, VWNbTa, VTaNbTi, VWNbTaTi, HfZrNb, HfMoTaTiZr.

Developing precipitation hardenable high entropy alloys

Science.gov (United States)

Gwalani, Bharat

High entropy alloys (HEAs) is a concept wherein alloys are constructed with five or more elements mixed in equal proportions; these are also known as multi-principle elements (MPEs) or complex concentrated alloys (CCAs). This PhD thesis dissertation presents research conducted to develop precipitation-hardenable high entropy alloys using a much-studied fcc-based equi-atomic quaternary alloy (CoCrFeNi). Minor additions of aluminium make the alloy amenable for precipitating ordered intermetallic phases in an fcc matrix. Aluminum also affects grain growth kinetics and Hall-Petch hardenability. The use of a combinatorial approach for assessing composition-microstructure-property relationships in high entropy alloys, or more broadly in complex concentrated alloys; using laser deposited compositionally graded AlxCrCuFeNi 2 (0 mechanically processed via conventional techniques. The phase stability and mechanical properties of these alloys have been investigated and will be presented. Additionally, the activation energy for grain growth as a function of Al content in these complex alloys has also been investigated. Change in fcc grain growth kinetic was studied as a function of aluminum; the apparent activation energy for grain growth increases by about three times going from Al0.1CoCrFeNi (3% Al (at%)) to Al0.3CoCrFeNi. (7% Al (at%)). Furthermore, Al addition leads to the precipitation of highly refined ordered L12 (gamma') and B2 precipitates in Al0.3CoCrFeNi. A detailed investigation of precipitation of the ordered phases in Al0.3CoCrFeNi and their thermal stability is done using atom probe tomography (APT), transmission electron microscopy (TEM) and Synchrotron X-ray in situ and ex situ analyses. The alloy strengthened via grain boundary strengthening following the Hall-Petch relationship offers a large increment of strength with small variation in grain size. Tensile strength of the Al0.3CoFeNi is increased by 50% on precipitation fine-scale gamma' precipitates

High purity heavy water production: need for total organic carbon determination in process water streams

International Nuclear Information System (INIS)

Ayushi; Kumar, Sangita D.; Reddy, A.V.R.; Vithal, G.K.

2009-01-01

In recent times, demand for high purity heavy water (99.98% pure) in industries and laboratories has grown by manifold. Its application started in nuclear industry with the design of CANDU reactor, which uses natural uranium as fuel. In this reactor the purest grade of heavy water is used as the moderator and the primary coolant. Diverse industrial applications like fibre optics, medicine, semiconductors etc. use high purity heavy water extensively to achieve better performance of the specific material. In all these applications there is a stringent requirement that the total organic carbon content (TOC) of high purity heavy water should be very low. This is because the presence of TOC can lead to adverse interactions in different applications. To minimize the TOC content in the final product there is a need to monitor and control the TOC content at each and every stage of heavy water production. Hence a simple, rapid and accurate method was developed for the determination of TOC content in process water samples. The paper summarizes the results obtained for the TOC content in the water samples collected from process streams of heavy water production plant. (author)

Charge collection performance of a segmented planar high-purity germanium detector

Energy Technology Data Exchange (ETDEWEB)

Cooper, R.J. [Department of Physics, The University of Liverpool, Oliver Lodge Laboratory, Liverpool Merseyside L69 7ZE (United Kingdom)], E-mail: R.Cooper@liverpool.ac.uk; Boston, A.J.; Boston, H.C.; Cresswell, J.R.; Grint, A.N.; Harkness, L.J.; Nolan, P.J.; Oxley, D.C.; Scraggs, D.P. [Department of Physics, The University of Liverpool, Oliver Lodge Laboratory, Liverpool Merseyside L69 7ZE (United Kingdom); Lazarus, I.; Simpson, J. [STFC Daresbury Laboratory, Warrington, Cheshire WA4 4AD (United Kingdom); Dobson, J. [Rosemere Cancer Centre, Royal Preston Hospital, Preston PR2 9HT (United Kingdom)

2008-10-01

High-precision scans of a segmented planar high-purity germanium (HPGe) detector have been performed with a range of finely collimated gamma ray beams allowing the response as a function of gamma ray interaction position to be quantified. This has allowed the development of parametric pulse shape analysis (PSA) techniques and algorithms for the correction of imperfections in performance. In this paper we report on the performance of this detector, designed for use in a positron emission tomography (PET) development system.

Synthesis and thermoelectric properties of fine-grained FeVSb system half-Heusler compound polycrystals with high phase purity

International Nuclear Information System (INIS)

Zou Minmin; Li Jingfeng; Guo Peijun; Kita, Takuji

2010-01-01

Nearly single-phased FeVSb half-Heusler compound thermoelectric materials with fine grains of diameter 100-200 nm were prepared from their elemental powders by combining mechanical alloying (MA) and spark plasma sintering. The resultant bulk samples showed a relatively low room-temperature electrical resistivity on the order of 10 μΩm, and a moderate negative Seebeck coefficient with a maximum value of -175 μV K -1 at 300 0 C. It was found that proper excessive addition of V relative to the stoichiometric composition (FeVSb) during MA enhanced the phase purity and hence the power factor of the spark plasma sintered samples, resulting in a large power factor value of 2480 μW m -1 K -2 when the elemental powders were mixed with the composition FeV 1.15 Sb. Its thermal conductivity was significantly reduced mainly due to refined grain sizes, resulting in a high dimensionless figure of merit ZT of 0.31 at a low-to-mid temperature (300 0 C) as for undoped half-Heusler compounds.

Study of corrosion processes on Al-AA 6061 crevices immersed in high purity water and sodium citrate solution

International Nuclear Information System (INIS)

Rodriguez, Sebastian A.; Haddad, Roberto; Lanzani, Liliana A.

2004-01-01

An experimental approach has been developed to study the corrosion behavior of artificial crevices manufactured with high purity aluminum and AA 6061 alloy, immersed in dematerialised water and sodium citrate solution (96,5 μS/cm). Alkaline attack was found on the surrounding of iron rich particles in the external zone of the crevice, as a result of localized oxygen reduction reaction on these sites. This attack was not observed in the zone inside the crevice. Study of the phase Mg 2 Si by EDS allowed establishing that there is not preferential dissolution inside the crevice. The formation of a stable and non-soluble complex between Al and citrate anion inhibited the production of Al(OH) 3 precipitate, which was observed on the surface of specimens immersed in pure water. Investigations of the aluminum oxide evolution on AA 6061 surfaces in water showed that it was composed by two layers: an internal one made of Bohemite and an external one in direct contact with the water, with a Bayerite structure. The surface analysis was accomplished using XR, OM and SEM techniques. (author) [es

Amplitude dependent damping in single crystalline high purity molybdenum

International Nuclear Information System (INIS)

Zelada-Lambri, G.I; Lambri, O.A; Garcia, J.A; Lomer, J.N

2004-01-01

Amplitude dependent damping measurements were performed on high purity single crystalline molybdenum at several different constant temperatures between room temperature and 1273K. The employed samples were single crystals with the orientation, having a residual resistivity ratio of about 8000. Previously to the amplitude dependent damping tests, the samples were subjected to different thermomechanical histories. Amplitude dependent damping effects appear only during the first heating run in temperature where the samples have the thermomechanical state of the deformation process at room temperature. In the subsequent run-ups in temperature, i.e, after subsequent annealings, amplitude dependent damping effects were not detected (au)

Development of high performance ODS alloys

Energy Technology Data Exchange (ETDEWEB)

Shao, Lin [Texas A & M Univ., College Station, TX (United States); Gao, Fei [Univ. of Michigan, Ann Arbor, MI (United States); Garner, Frank [Texas A & M Univ., College Station, TX (United States)

2018-01-29

This project aims to capitalize on insights developed from recent high-dose self-ion irradiation experiments in order to develop and test the next generation of optimized ODS alloys needed to meet the nuclear community's need for high strength, radiation-tolerant cladding and core components, especially with enhanced resistance to void swelling. Two of these insights are that ferrite grains swell earlier than tempered martensite grains, and oxide dispersions currently produced only in ferrite grains require a high level of uniformity and stability to be successful. An additional insight is that ODS particle stability is dependent on as-yet unidentified compositional combinations of dispersoid and alloy matrix, such as dispersoids are stable in MA957 to doses greater than 200 dpa but dissolve in MA956 at doses less than 200 dpa. These findings focus attention on candidate next-generation alloys which address these concerns. Collaboration with two Japanese groups provides this project with two sets of first-round candidate alloys that have already undergone extensive development and testing for unirradiated properties, but have not yet been evaluated for their irradiation performance. The first set of candidate alloys are dual phase (ferrite + martensite) ODS alloys with oxide particles uniformly distributed in both ferrite and martensite phases. The second set of candidate alloys are ODS alloys containing non-standard dispersoid compositions with controllable oxide particle sizes, phases and interfaces.

Oxidation characteristics of the electron beam surface-treated Alloy 617 in high temperature helium environments

International Nuclear Information System (INIS)

Lee, Ho Jung; Sah, Injin; Kim, Donghoon; Kim, Hyunmyung; Jang, Changheui

2015-01-01

The oxidation characteristics of the electron beam surface-treated Alloy 617, which has an Al-rich surface layer, were evaluated in high temperature helium environments. Isothermal oxidation tests were performed in helium (99.999% purity) and VHTR-helium (helium of prototypical VHTR chemistry containing impurities like CO, CO 2 , CH 4 , and H 2 ) environments at 900 °C for up to 1000 h. The surface-treated Alloy 617 showed an initial transient oxidation stage followed by the steady-state oxidation in all test environments. In addition, the steady-state oxidation kinetics of the surface-treated Alloy 617 was 2-order of magnitude lower than that of the as-received Alloy 617 in both helium environments as well as in air. The improvement in oxidation resistance was primarily due to the formation of the protective Al 2 O 3 layer on the surface. The weight gain was larger in the order of air, helium, and VHTR-helium, while the parabolic rate constants (k p ) at steady-state were similar for all test environments. In both helium environments, the oxide structure consisted of the outer transition Al 2 O 3 with a small amount of Cr 2 O 3 and inner columnar structured Al 2 O 3 without an internal oxide. In the VHTR-helium environment, where the impurities were added to helium, the initial transient oxidation increased but the steady state kinetics was not affected

Progress in Preparation and Research of High Entropy Alloys

Directory of Open Access Journals (Sweden)

CHEN Yong-xing

2017-11-01

Full Text Available The current high entropy alloys' studies are most in block, powder, coating, film and other areas. There are few studies of high entropy alloys in other areas and they are lack of unified classification. According to the current high entropy alloys' research situation, The paper has focused on the classification on all kinds of high entropy alloys having been researched, introduced the selecting principle of elements, summarized the preparation methods, reviewed the research institutions, research methods and research contents of high entropy alloys, prospected the application prospect of high entropy alloys, put forward a series of scientific problems of high entropy alloys, including less research on mechanism, incomplete performance research, unsystematic thermal stability study, preparation process parameters to be optimized, lightweight high entropy alloys' design, the expansion on the research field, etc, and the solutions have been given. Those have certain guiding significance for the expansion of the application of high entropy alloys subjects in the future research direction.

High temperature niobium alloys

International Nuclear Information System (INIS)

Wojcik, C.C.

1991-01-01

Niobium alloys are currently being used in various high temperature applications such as rocket propulsion, turbine engines and lighting systems. This paper presents an overview of the various commercial niobium alloys, including basic manufacturing processes, properties and applications. Current activities for new applications include powder metallurgy, coating development and fabrication of advanced porous structures for lithium cooled heat pipes

Corrosion and protection of magnesium alloys

Energy Technology Data Exchange (ETDEWEB)

Ghali, E. [Laval Univ., Quebec City, PQ (Canada). Dept. of Mining and Metallurgy

2000-07-01

The oxide film on magnesium offers considerable surface protection in rural and some industrial environments and the corrosion rate lies between that of aluminum and low carbon steels. Galvanic coupling of magnesium alloys, high impurity content such as Ni, Fe, Cu and surface contamination are detrimental for corrosion resistance of magnesium alloys. Alloying elements can form secondary particles which are noble to the Mg matrix, thereby facilitating corrosion, or enrich the corrosion product thereby possibly inhibiting the corrosion rate. Bimetallic corrosion resistance can be increased by fluxless melt protection, choice of compatible alloys, insulating materials, and new high-purity alloys. Magnesium is relatively insensible to oxygen concentration. Pitting, corrosion in the crevices, filiform corrosion are observed. Granular corrosion of magnesium alloys is possible due to the cathodic grain-boundary constituent. More homogeneous microstructures tend to improve corrosion resistance. Under fatigue loading conditions, microcrack initiation in Mg alloys is related to slip in preferentially oriented grains. Coating that exclude the corrosive environments can provide the primary defense against corrosion fatigue. Magnesium alloys that contain neither aluminum nor zinc are the most SCC resistant. Compressive surface residual stresses as that created by short peening increase SCC resistance. Cathodic polarization or cladding with a SCC resistant sheet alloy are good alternatives. Effective corrosion prevention for magnesium alloy components and assemblies should start at the design stage. Selective surface preparation, chemical treatment and coatings are recommended. Oil application, wax coating, anodizing, electroplating, and painting are possible alternatives. Recently, it is found that a magnesium hydride layer, created on the magnesium surface by cathodic charging in aqueous solution is a good base for painting. (orig.)

Comparison of Deformation in High-Purity Single/Large Grain and Polycrystalline Niobium Superconducting Cavities

International Nuclear Information System (INIS)

Ganapati Rao Myneni; Peter Kneisel

2005-01-01

The current approach for the fabrication of superconducting radio frequency (SRF) cavities is to roll and deep draw sheets of polycrystalline high-purity niobium. Recently, a new technique was developed at Jefferson Laboratory that enables the fabrication of single-crystal high-purity Nb SRF cavities. To better understand the differences between SRF cavities fabricated out of fine-grained polycrystalline sheet in the standard manner and single crystal cavities fabricated by the new technique, two half-cells were produced according to the two different procedures and compared using a variety of analytical techniques including optical microscopy, scanning laser confocal microscopy, profilometry, and X-ray diffraction. Crystallographic orientations, texture, and residual stresses were determined in the samples before and after forming and this poster presents the results of this ongoing study

Human parvovirus B19 infection in hemophiliacs first infused with two high-purity, virally attenuated factor VIII concentrates.

Science.gov (United States)

Azzi, A; Ciappi, S; Zakvrzewska, K; Morfini, M; Mariani, G; Mannucci, P M

1992-03-01

Human parvovirus B19 can be transmitted by coagulation factor concentrates and is highly resistant to virucidal methods. To evaluate whether the additional removal of virus by chromatographic methods during the manufacture of high-purity concentrates reduces the risk of B19 transmission, we have prospectively evaluated the rate of anti-B19 seroconversion in two groups of susceptible (anti-B19 negative) hemophiliacs infused with high-purity, heated (pasteurized) or solvent-detergent-treated factor VIII concentrates. Both products infected a relatively high proportion of patients (nine of 20).

High purity and semi-insulating 4H-SiC crystals grown by physical vapor transport

Energy Technology Data Exchange (ETDEWEB)

Augustine, G.; Hobgood, H.McD.; Balakrishna, V.; Dunne, G.T.; Hopkins, R.H.; Thomas, R.N. [Northrop Grumman Corp., Pittsburgh, PA (United States). Science and Technology Center; Doolittle, W.A.; Rohatgi, A. [Georgia Inst. of Tech., Atlanta, GA (United States). School of Electrical and Computer Engineering

1998-06-01

High purity undoped and semi-insulating vanadium doped 4H-SiC single crystals with diameters up to 50 mm were grown by the physical vapor transport method. Undoped crystals exhibiting resistivities in the 10{sup 2} to 10{sup 3} {Omega}-cm range and photoconductive decay (PCD) lifetimes in the 2 to 9 {mu}s range, were grown from high purity SiC sublimation sources. The crystals were p-type due to the presence of residual acceptor impurities, mainly boron. The semi-insulating behavior of the vanadium doped crystals is attributed to compensation of residual acceptors by the deep level vanadium donor located near the middle of the band gap. (orig.) 6 refs.

Preparation of high-purity cerium nitrate; Preparacao de nitrato de cerio de alta pureza

Energy Technology Data Exchange (ETDEWEB)

Avila, Daniela Moraes; Silva Queiroz, Carlos Alberto da; Santos Mucillo, Eliana Navarro dos [Instituto de Pesquisas Energeticas e Nucleares (IPEN), Sao Paulo, SP (Brazil)

1995-12-31

The preparation of high-purity cerium nitrate has been carried out Cerium oxide has been prepared by fractioned precipitation and ionic exchange techniques, using a concentrate with approximately 85% of cerium oxide from NUCLEMON as raw material. Five sequential ion-exchange columns with a retention capacity of 170 g each have been used. The ethylenediamine-tetraacetic acid (EDTA) was used as eluent. The cerium content has been determined by gravimetry and iodometry techniques. The resulting cerium oxide has a purity > 99%. This material was transformed in cerium nitrate to be used as precursor for the preparation of Zirconia-ceria ceramics by the coprecipitation technique. (author) 2 tabs.

Structural alloys for high field superconducting magnets

International Nuclear Information System (INIS)

Morris, J.W. Jr.

1985-08-01

Research toward structural alloys for use in high field superconducting magnets is international in scope, and has three principal objectives: the selection or development of suitable structural alloys for the magnet support structure, the identification of mechanical phenomena and failure modes that may influence service behavior, and the design of suitable testing procedures to provide engineering design data. This paper reviews recent progress toward the first two of these objectives. The structural alloy needs depend on the magnet design and superconductor type and differ between magnets that use monolithic and those that employ force-cooled or ICCS conductors. In the former case the central requirement is for high strength, high toughness, weldable alloys that are used in thick sections for the magnet case. In the latter case the need is for high strength, high toughness alloys that are used in thin welded sections for the conductor conduit. There is productive current research on both alloy types. The service behavior of these alloys is influenced by mechanical phenomena that are peculiar to the magnet environment, including cryogenic fatigue, magnetic effects, and cryogenic creep. The design of appropriate mechanical tests is complicated by the need for testing at 4 0 K and by rate effects associated with adiabatic heating during the tests. 46 refs

Rare earth impurities in high purity lanthanum oxide determined by neutron activation analysis

International Nuclear Information System (INIS)

Nguyen Van Suc; Desai, H.B.; Parthasarathy, R.; Gangadharan, S.

1992-01-01

Individual rare earth impurities in high purity La 2 O 3 (≥99.9%) have been determined by NAA after pre-separation of the matrix (La). The separation is carried out on an anion exchanger (Dowex 1x8) using different mixtures of methanol/nitric acid as eluants. The rare earth elements from Dy to Lu are eluted quantitatively using a 10% 1M HNO 3 - 90% methanol mixture, while the light rare earths from Ce to Gd are eluted quantitatively using a 10% 0.05M HNO 3 - 90% methanol mixture. La, which is retained on the column, is eluted using 0.1M HNO 3 . The recoveries of the various rare earth elements have been checked using radiotracers and also by spiking the sample with known amount of elements, and the recoveries are found to be quantitative. Results obtained on a typical high purity lanthanum oxide are reported here. (author) 5 refs.; 1 fig

Manufacturing and Characterization of Ultra Pure Ferrous Alloys Final Report CRADA No. TC02069.0

Energy Technology Data Exchange (ETDEWEB)

Lesuer, D. [Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States); McGreevy, T. E. [Caterpillar Inc., Mossville, IL (United States)

2017-09-06

This CRADA was a.collaborative effort between the Lawrence Livermore National Security LLC (formerly University of California)/Lawrence Livermore National Laboratory (LLNL),and Caterpillar Inc. (CaterpiHar), to further advance levitation casting techniques (developed at the Central Research Institute for Material (CRIM) in St. Petersburg, Russia) for use in manufacturing high purity metal alloys. This DOE Global Initiatives for Proliferation Prevention Program (IPP) project was to develop and demonstrate the levitation casting technology for producing ultra-pure alloys.

Radiochemical neutron activation analysis based multi-elemental analysis of high purity gallium

International Nuclear Information System (INIS)

Tashimova, F.A.; Sadikov, I.I; Salimov, M.I.; Zinov'ev, V.G.

2006-01-01

Full text: Gallium is one of the widely used materials in semiconductor and optoelectronics industry. Gallium is used to produce infrared detectors, piezoelectric sensors, high- and low-temperature transistors for space and defense technology. One of the most important requirements for semiconductor materials of gallium compounds is an excessive high purity for layers and films. Information on impurities (type of an impurity, concentration, character of distribution) is important as for better understanding of the physical and chemical processes taking place in formed semiconductor structures and for the 'know-how' of devices on their basis. The object of this work is to develop radiochemical neutron activation technique for analysis of high purity gallium. Irradiation of 0.1 g of gallium sample in neutron flux of 5·10 13 cm -2 s -1 for 5 hours will result in induced activity of more than 10 8 Bq, due to 72 Ga radionuclide, half-life of which is 14.1 hours. Therefore to perform instrumental NAA of gallium long period (10 day) cooling is required, and high sensitive determination of elements producing short- and long-lived radionuclides (T 1/2 72 Ga. We have studied the behavior of gallium in extraction-chromatographic system 'TBP-HCl'. The experiments have shown that higher factor of distribution (D) and capacity on gallium can be achieved when 'TBP-4M HCl' system is used. However more than 10 trace elements have high D and thus they cannot be separated from 72 Ga. To resolve the problem and increase the number of separated trace elements we have used preliminary satisfaction of chromatographic column with tellurium, which has D higher than the most of elements in 'TBP-4M HCl' system and thus suppresses extraction of elements. Distribution profile of gallium along the column and elution curve of 25 trace elements have been measured. Chemical yields of separated elements measured by using radiotracers are more than 93%. On the basis of the carried out researches

Obtention of high purity silica from the flotation waste of itabiritic ore

International Nuclear Information System (INIS)

Martins, Polyana Fabricia Fernandes

2016-01-01

Banded iron formations are exploited as iron mineral in 'Quadrilatero Ferrifero' of Minas Gerais (MG) State, Brazil. About half of the amount of extracted material becomes tailings, which are stored in tailing dams or used for filling mining pits. Tens of thousands of tons are generated daily in operating mines in this region, causing concern about the environmental liabilities, and costs to manage the tailing dams. Miners are committed to finding uses for these wastes in other productive chains. This thesis aimed to obtain high purity silica from the flotation tailings of banded iron formations using classical techniques for ore processing, such as particle size classification and magnetic separation, followed by hydrometallurgical leaching, also alkaline fusion and chemical precipitation. The tailings samples was collected in the tailings dam of Peak Mine operated by Vale A.S., in Itabirito – MG. This sample had initially 33.4% by weight SiO 2 , 57.4% wt Fe 2 O 3 and 8.31% wt Al 2 O 3 . After desliming for disposal of the fine particles (-37μm) the composition was 68.0% SiO 2 , 31.4% Fe 2 O 3 and 0.50% Al 2 O 3 . After magnetic separation, the composition was 93.8% SiO 2 , 1.16% Fe 2 O 3 and 3.80% Al 2 O 3 . After acid leaching l or digestion to remove impurities, it was possible to obtain silica with 98% purity. The fusion with sodium hydroxide, followed by alkaline leaching of sodium silicate and silica precipitation gave purities of about 99.5%. Values even higher may be possible with optimization of the parameters of alkaline fusion or by repeating the process from the product with purity of 99.5%. The iron oxide content and the aluminum main contaminants were 0.01% and 0.07%, respectively. Amorphous silica was obtained with high specific surface (322 m 2 /g) and particle size less than 200 nm. Depending on the application, a control should be made for the impurities, such as phosphorus, potassium and boron. (author)

Preparation of high purity yttrium single crystals by electrotransport

International Nuclear Information System (INIS)

Volkov, V.T.; Nikiforova, T.V.; Ionov, A.M.; Pustovit, A.N.; Sikharulidse, G.G.

1981-01-01

The possibility of obtaining yttrium crystals of high purity by the method of solid state electrotransport (SSE) was investigated in the present work. The behaviour of low contents of iron, aluminium, silicon, tantalum, copper, silver and vanadium as metallic impurities was studied using mass spectrometry. It is shown that all the impurities investigated, except copper, migrate to the anode. During electrotransfer a purification with respect to these impurities by a factor of 4 - 6 is obtained. It is proposed that the diffusion coefficients of the metallic impurities investigated are anomalously high and that the behaviour of the impurities during SSE in adapters necessitates further investigation. By using a three-stage process with intermediate removal of the anode end yttrium single crystals with a resistance ratio rho 293 /rhosub(4.2)=570 were produced. (Auth.)

Germanium field-effect transistor made from a high-purity substrate

International Nuclear Information System (INIS)

Hansen, W.L.; Goulding, F.S.; Haller, E.E.

1978-11-01

Field effect transistors have been fabricated on high-purity germanium substrates using low-temperature technology. The aim of this work is to preserve the low density of trapping centers in high-quality starting material by low-temperature ( 0 C) processing. The use of germanium promises to eliminate some of the traps which cause generation-recombination noise in silicon field-effect transistors (FET's) at low temperatures. Typically, the transconductance (g/sub m/) in the germanium FET's is 10 mA/V and the gate leakage can be less than 10 -12 A. Present devices exhibit a large 1/f noise component and most of this noise must be eliminated if they are to be competitive with silicon FET's commonly used in high-resolution nuclear spectrometers

The ion-exchange obtaining of high purity samarium oxide

International Nuclear Information System (INIS)

Brzyska, W.; Soltysiak, I.; Cygan, J.

1987-01-01

The use of lactic acid - EDTA mixture as an eluent for the obtaining of high purity samarium oxide was studied. The studies were carried out at room temperature on cation exchange resin Wofatit KPS X 8. The best results were obtained for lactic acid (0,26 mol/dm 3 ) - EDTA (0,013 mol/dm 3 ) mixture at pH 3,3. As the result of 57% samarium concentrate elution with column load 1:3 and flow rate 0,4 cm/min, over 99% pure samarium oxide with 73% yield has been obtained. The yield of spectrally pure Sm 2 O 3 exceeded 45%. (author)

New, fast corroding high ductility Mg–Bi–Ca and Mg–Bi–Si alloys, with no clinically observable gas formation in bone implants

International Nuclear Information System (INIS)

Remennik, S.; Bartsch, I.; Willbold, E.; Witte, F.; Shechtman, D.

2011-01-01

Highlights: ► Biodegradable, biocompatible and highly ductile Mg alloys based on the Mg–Bi system have been produced by rapid solidification and extrusion processes. ► The implants corroded fast within the first 4 weeks after implantation in rabbit bone, but no gas formation has been clinically observed. ► The corrosion rate could be significantly reduced in vitro and in vivo by using high purity magnesium for the alloy production. - Abstract: Current approaches to initial corrosion rate reduction of biodegradable magnesium alloys include alloying with rare earth elements, mechanical processing, coatings and the use of metallic glasses. The latter has limited ductility needed for implant adaptively to various surgery procedures. Furthermore, slow corroding magnesium alloys, coatings or metallic glasses have not proved to be fully dissolvable in vivo. With this in mind, we have developed a new class of biocompatible, biodegradable ductile magnesium alloys with 40% elongation at room temperature. The alloys are based on the Mg–Bi system and undergo a series of production routes, which include rapid solidification (RS) and various extrusion processes. The Mg–Bi–Si (B-BS) system exhibited a high corrosion rates in vitro and was excluded from in vivo screening. In preliminary experiments of Mg–Bi–Ca (B-BX) in rabbit femur bones, the alloy corroded rapidly without any clinically visible gas formation. Only 30% of the B-BX implant remained uncorroded after 4 weeks of implantation. After using low iron Mg for implant preparation the corrosion rate of HP-B-BX was reduced in bone leaving 70% of the implant uncorroded after 4 weeks, while the corrosion in intramuscular and subcutaneous sites were still high leaving only 40% and 10% uncorroded after 4 weeks. The foreign body reaction was very mild and enhanced bone formation could be observed in the vicinity of the corroding implant. Thus, these new magnesium alloys are potentially promising biomaterials

Improved procedure for high purity gaseous peroxyacyl nitrate production: use of heavy lipid solvents

Energy Technology Data Exchange (ETDEWEB)

Gaffney, J S; Fajer, R; Senum, G I

1984-01-01

An improved procedure is described for the production of peroxyacyl nitrates (PAN's) in the gas phase. The method of Nielsen et al. (1982) has been modified to yield PAN's of high purity with no further chromatographic purification required. Extraction of PAN's from the nitration of the peracids is accomplished by use of a heavy lipid solvent (n-tridecane). This solvent's low vapor pressure allows the simple separation and preparation of high purity gaseous PAN's (>98%) as determined by Fourier transform infrared spectroscopy (FTIR). Using this method infrared integrated band strengths are reported for peroxyacetyl nitrate (PAN) perdeutero-peroxyacetyl nitrate (PAN-D/sub 3/) and peroxyproprionyl nitrate (PPN). The method allows facile production of large amounts of gaseous PAN's for smog chamber and laboratory studies, toxicological and health effects research, as well as for calibration of PAN analyses.

Shock loading influence on mechanical behavior of high purity iron

International Nuclear Information System (INIS)

Buy, Francois; Voltz, Christophe

2004-01-01

This paper proposes the analysis of shock wave effects for high purity iron. The method developed is based on the characterization of the mechanical behavior of as received and shocked material. Shock effect is generated through plate impact tests performed in the range of 4 GPa to 39 GPa on a single stage light gas gun or a powder gun. Therefore, as-received and impacted materials are characterized. A formalism proposed by J.R.Klepaczko and based on physical relations has been adopted to describe stress strain curves

Cladding Alloys for Fluoride Salt Compatibility

Energy Technology Data Exchange (ETDEWEB)

Muralidharan, Govindarajan [ORNL; Wilson, Dane F [ORNL; Walker, Larry R [ORNL; Santella, Michael L [ORNL; Holcomb, David Eugene [ORNL

2011-06-01

This report provides an overview of several candidate technologies for cladding nickel-based corrosion protection layers onto high-temperature structural alloys. The report also provides a brief overview of the welding and weld performance issues associated with joining nickel-clad nickel-based alloys. From the available techniques, two cladding technologies were selected for initial evaluation. The first technique is a line-of-sight method that would be useful for cladding large structures such as vessel interiors or large piping. The line-of-sight method is a laser-based surface cladding technique in which a high-purity nickel powder mixed into a polymer binder is first sprayed onto the surface, baked, and then rapidly melted using a high-power laser. The second technique is a vapor phase technique based on the nickel-carbonyl process that is suitable for cladding inaccessible surfaces such as the interior surfaces of heat exchangers. An initial evaluation for performed on the quality of nickel claddings processed using the two selected cladding techniques.

MoNbTaV Medium-Entropy Alloy

Directory of Open Access Journals (Sweden)

Hongwei Yao

2016-05-01

Full Text Available Guided by CALPHAD (Calculation of Phase Diagrams modeling, the refractory medium-entropy alloy MoNbTaV was synthesized by vacuum arc melting under a high-purity argon atmosphere. A body-centered cubic solid solution phase was experimentally confirmed in the as-cast ingot using X-ray diffraction and scanning electron microscopy. The measured lattice parameter of the alloy (3.208 Å obeys the rule of mixtures (ROM, but the Vickers microhardness (4.95 GPa and the yield strength (1.5 GPa are about 4.5 and 4.6 times those estimated from the ROM, respectively. Using a simple model on solid solution strengthening predicts a yield strength of approximately 1.5 GPa. Thermodynamic analysis shows that the total entropy of the alloy is more than three times the configurational entropy at room temperature, and the entropy of mixing exhibits a small negative departure from ideal mixing.

Degradation mode survey candidate titanium-base alloys for Yucca Mountain project waste package materials. Revision 1

Energy Technology Data Exchange (ETDEWEB)

Gdowski, G.E.

1997-12-01

The Yucca Mountain Site Characterization Project (YMP) is evaluating materials from which to fabricate high-level nuclear waste containers (hereafter called waste packages) for the potential repository at Yucca Mountain, Nevada. Because of their very good corrosion resistance in aqueous environments titanium alloys are considered for container materials. Consideration of titanium alloys is understandable since about one-third (in 1978) of all titanium produced is used in applications where corrosion resistance is of primary importance. Consequently, there is a considerable amount of data which demonstrates that titanium alloys, in general, but particularly the commercial purity and dilute {alpha} grades, are highly corrosion resistant. This report will discuss the corrosion characteristics of Ti Gr 2, 7, 12, and 16. The more highly alloyed titanium alloys which were developed by adding a small Pd content to higher strength Ti alloys in order to give them better corrosion resistance will not be considered in this report. These alloys are all two phase ({alpha} and {beta}) alloys. The palladium addition while making these alloys more corrosion resistant does not give them the corrosion resistance of the single phase {alpha} and near-{alpha} (Ti Gr 12) alloys.

In vitro characterization of high purity factor IX concentrates for the treatment of hemophilia B.

Science.gov (United States)

Limentani, S A; Gowell, K P; Deitcher, S R

1995-04-01

This study employed sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE) analysis and immunoblotting to assess the purity of seven high purity factor IX concentrates: Aimafix (Aima), AlphaNine-SD (Alpha Therapeutic), Factor IX VHP (Biotransfusion), Immunine (Immuno), Mononine (Armour Pharmaceutical), Nanotiv (Kabi Pharmacia), and 9MC (Blood Products Laboratory). The mean specific activity of these products ranged from 68 U factor IX/mg (Aimafix) to 246 U factor IX/mg (Mononine). SDS-PAGE analysis showed that the highest purity product, Mononine, had a single contaminating band under non-reducing conditions. Two additional bands were detected when this product was analyzed under reducing conditions. All other products had multiple contaminating bands that were more apparent under reducing than non-reducing conditions. The immunoblot for factor IX showed a dominant factor IX band for all products. In addition, visible light chain of factor IX was detected for AlphaNine-SD, Factor IX VHP, Immunine, Mononine, Nanotiv, and 9MC, suggesting that the factor IX in these products had undergone partial activation to factor IXa. Another contaminating band was visible at 49,500 for all of the products except 9MC. In addition to this band, high molecular weight contaminants were apparent for some products, most notably AlphaNine-SD. The identity of these bands is unknown. Immunoblotting failed to demonstrate factor VII as a contaminant of any of the high purity products, although factor VIIa could be detected in some lots of Immunine, Nanotiv, and 9MC by a clot-based assay. Factor X contaminated Aimafix, AlphaNine-SD, Factor IX VHP, Immunine, Nanotiv, and 9MC, but activation products of factor X were not detected.(ABSTRACT TRUNCATED AT 250 WORDS)

Methods to improve and understand the sensitivity of high purity germanium detectors for searches of rare events

International Nuclear Information System (INIS)

Volynets, Oleksandr

2012-01-01

Observation of neutrinoless double beta-decay could answer fundamental questions on the nature of neutrinos. High purity germanium detectors are well suited to search for this rare process in germanium. Successful operation of such experiments requires a good understanding of the detectors and the sources of background. Possible background sources not considered before in the presently running GERDA high purity germanium detector experiment were studied. Pulse shape analysis using artificial neural networks was used to distinguish between signal-like and background-like events. Pulse shape simulation was used to investigate systematic effects influencing the efficiency of the method. Possibilities to localize the origin of unwanted radiation using Compton back-tracking in a granular detector system were examined. Systematic effects in high purity germanium detectors influencing their performance have been further investigated using segmented detectors. The behavior of the detector response at different operational temperatures was studied. The anisotropy effects due to the crystallographic structure of germanium were facilitated in a novel way to determine the orientation of the crystallographic axes.

Methods to improve and understand the sensitivity of high purity germanium detectors for searches of rare events

Energy Technology Data Exchange (ETDEWEB)

Volynets, Oleksandr

2012-07-27

Observation of neutrinoless double beta-decay could answer fundamental questions on the nature of neutrinos. High purity germanium detectors are well suited to search for this rare process in germanium. Successful operation of such experiments requires a good understanding of the detectors and the sources of background. Possible background sources not considered before in the presently running GERDA high purity germanium detector experiment were studied. Pulse shape analysis using artificial neural networks was used to distinguish between signal-like and background-like events. Pulse shape simulation was used to investigate systematic effects influencing the efficiency of the method. Possibilities to localize the origin of unwanted radiation using Compton back-tracking in a granular detector system were examined. Systematic effects in high purity germanium detectors influencing their performance have been further investigated using segmented detectors. The behavior of the detector response at different operational temperatures was studied. The anisotropy effects due to the crystallographic structure of germanium were facilitated in a novel way to determine the orientation of the crystallographic axes.

Preparation of a high strength Al–Cu–Mg alloy by mechanical alloying and press-forming

International Nuclear Information System (INIS)

Tang Huaguo; Cheng Zhiqiang; Liu Jianwei; Ma Xianfeng

2012-01-01

Highlights: ► A high strength aluminum alloy of Al–2 wt.%Mg–2 wt.%Cu has been prepared by mechanical alloying and press-forming. ► The alloy only consists of solid solution α-Al. ► The grains size of α-Al was about 300 nm–5 μm. ► The solid solution strengthening and the grain refinement strengthening are the main reasons for such a high strength. - Abstract: A high strength aluminum alloy, with the ratio of 96 wt.%Al–2 wt.%Mg–2 wt.%Cu, has been prepared by mechanical alloying and press-forming. The alloy exhibited a high tensile strength of 780 MPa and a high microhardness of 180 HV. X-ray diffraction characterizations confirmed that the alloy only consists of a solid solution α-Al. Microstructure characterizations revealed that the grain size of α-Al was about 300 nm–5 μm. The solid solution strengthening and the grain refinement strengthening were considered to be the reason for such a high strength.

Preparation of a high strength Al-Cu-Mg alloy by mechanical alloying and press-forming

Energy Technology Data Exchange (ETDEWEB)

Tang Huaguo [State Key Laboratory of Rare Earth Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China); Cheng Zhiqiang [College of Resources and Environment, Jilin Agricultural University, Changchun 130118 (China); Liu Jianwei [State Key Laboratory of Rare Earth Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China); Ma Xianfeng, E-mail: xfma@ciac.jl.cn [State Key Laboratory of Rare Earth Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China)

2012-07-30

Highlights: Black-Right-Pointing-Pointer A high strength aluminum alloy of Al-2 wt.%Mg-2 wt.%Cu has been prepared by mechanical alloying and press-forming. Black-Right-Pointing-Pointer The alloy only consists of solid solution {alpha}-Al. Black-Right-Pointing-Pointer The grains size of {alpha}-Al was about 300 nm-5 {mu}m. Black-Right-Pointing-Pointer The solid solution strengthening and the grain refinement strengthening are the main reasons for such a high strength. - Abstract: A high strength aluminum alloy, with the ratio of 96 wt.%Al-2 wt.%Mg-2 wt.%Cu, has been prepared by mechanical alloying and press-forming. The alloy exhibited a high tensile strength of 780 MPa and a high microhardness of 180 HV. X-ray diffraction characterizations confirmed that the alloy only consists of a solid solution {alpha}-Al. Microstructure characterizations revealed that the grain size of {alpha}-Al was about 300 nm-5 {mu}m. The solid solution strengthening and the grain refinement strengthening were considered to be the reason for such a high strength.

The role of time-dependent deformation in intergranular crack initiation of alloy 600 steam generator tubing material

International Nuclear Information System (INIS)

Was, G.S.; Lian, K.

1998-03-01

Intergranular stress corrosion cracking (IGSCC) of two commercial alloy 600 conditions (600LT, 600HT) and controlled- purity Ni-18Cr-9Fe alloys (CDMA, CDTT) were investigated using constant extension rate tensile (CERT) tests in primary water (0.01M LiOH+0.01M H 3 BO 3 ) with 1 bar hydrogen overpressure at 360 degrees C and 320 degrees C. Heat treatments produced two types of microstructures in both commercial and controlled-purity alloys: one dominated by grain boundary carbides (600HT and CDTT) and one dominated by intragranular carbides (600LT and CDMA). CERT tests were conducted over a range of strain rates and at two temperatures with interruptions at specific strains to determine the crack depth distributions. Results show that in all samples, IGSCC was the dominant failure mode. For both the commercial alloy and the controlled-purity alloys, the microstructure with grain boundary carbides showed delayed crack initiation and shallower crack depths than did the intragranular carbide microstructure under all experimental conditions. This data indicates that a grain boundary carbide microstructure is more resistant to IGSCC than an intragranular carbide microstructure. Observations support both the film rupture/slip dissolution mechanism and enhanced localized plasticity. The advantage of these results over previous studies is that the different carbide distributions were obtained in the same commercial alloy using different heat treatments, and in the other case, in nearly identical controlled-purity alloys. Therefore, observations of the effects of carbide distribution on IGSCC can more confidently be attributed to the carbide distribution alone rather than other potentially significant differences in microstructure or composition

High resolution gamma-ray spectroscopy at high count rates with a prototype High Purity Germanium detector

Science.gov (United States)

Cooper, R. J.; Amman, M.; Vetter, K.

2018-04-01

High-resolution gamma-ray spectrometers are required for applications in nuclear safeguards, emergency response, and fundamental nuclear physics. To overcome one of the shortcomings of conventional High Purity Germanium (HPGe) detectors, we have developed a prototype device capable of achieving high event throughput and high energy resolution at very high count rates. This device, the design of which we have previously reported on, features a planar HPGe crystal with a reduced-capacitance strip electrode geometry. This design is intended to provide good energy resolution at the short shaping or digital filter times that are required for high rate operation and which are enabled by the fast charge collection afforded by the planar geometry crystal. In this work, we report on the initial performance of the system at count rates up to and including two million counts per second.

High purity ferritic Cr-Mo stainless steel

International Nuclear Information System (INIS)

Knoth, J.

1977-01-01

In five years, E-BRITE 26-1 ferritic stainless steel has won an important place in the spectrum of materials suitable for use in chemical process equipment. It provides, in stainless steel, performance-capability characteristics comparable to more expensive alloys. It has demonstrated cost-effectiveness in equipment used for caustic, nitric-urea, organic chemicals, pulping liquors, refinery streams, and elsewhere. User confidence in the reliability and integrity of Grade XM 27 has increased to the point where large critical systems are now routinely specified in the alloy. The market acceptance of this material has attracted attempts to produce substitute versions of the alloy. Imitation, should be viewed with caution. Stabilized 26-IS must be examined over a lengthy period of time to determine if its own corrosion resistance, ductility, fabricability and reproducibility properties could ever be likened to those of E-BRITE 26-1. (orig.) [de

Obtaining water with a high degree of purity by using reverse osmosis

Directory of Open Access Journals (Sweden)

Nicolae Chirilă

2011-12-01

Full Text Available In this paper, we used the method of reverse osmosis in order to obtain water with a high degree of purity. For this aim, we used the TKA 20-120ECO device. We completed physic-chemical determinations for the water of supply, as well as for the water obtained after the osmosis process. The results that we obtained are relevant and interesting.

WC-3015 alloy (high-temperature alloy)

International Nuclear Information System (INIS)

Anon.

1974-01-01

WC-3015 Nb alloy containing 28 to 30 Hf, 1 to 2 Zr, 13 to 16 W, 0 to 4 Ta, 0 to 5 Ti, 0.07 to 0.33 C, less than or equal to 0.02 N, less than or equal to 0.03 O, less than or equal to 0.001 H was developed for use at high temperature in oxidizing environments. Its composition can be tailored to meet specific requirements. When WC-3015 is exposed to O at elevated temperature, Hf and Nb oxidized preferentially and HfO 2 dissolves in Nb 2 O 5 to form 6HfO-Nb 2 O 5 . This complex oxide has a tight cubic lattice which resists the diffusion of O into the substrate. During 24-h exposure to air at 2400 0 F, the alloy oxidizes to a depth of approximately 0.035 in. with a surface recession of 0 to 0.004 in. Oxidation resistance of WC-3015 welds and base material can be further enhanced greatly by applying silicide coatings. WC-3015 alloy can be machined by conventional and electrical-discharge methods. It can be hot worked readily by extrusion, forging or rolling. Cold working can be used at room or elevated temperature. It can be welded by the electron-beam or Tig processes. Physical constants, typical mechanical properties at 75 to 2400 0 F, and effects of composition and heat treatment on tensile and stress-rupture properties of the alloy are tabulated

A solvent-extraction module for cyclotron production of high-purity technetium-99m.

Science.gov (United States)

Martini, Petra; Boschi, Alessandra; Cicoria, Gianfranco; Uccelli, Licia; Pasquali, Micòl; Duatti, Adriano; Pupillo, Gaia; Marengo, Mario; Loriggiola, Massimo; Esposito, Juan

2016-12-01

The design and fabrication of a fully-automated, remotely controlled module for the extraction and purification of technetium-99m (Tc-99m), produced by proton bombardment of enriched Mo-100 molybdenum metallic targets in a low-energy medical cyclotron, is here described. After dissolution of the irradiated solid target in hydrogen peroxide, Tc-99m was obtained under the chemical form of 99m TcO 4 - , in high radionuclidic and radiochemical purity, by solvent extraction with methyl ethyl ketone (MEK). The extraction process was accomplished inside a glass column-shaped vial especially designed to allow for an easy automation of the whole procedure. Recovery yields were always >90% of the loaded activity. The final pertechnetate saline solution Na 99m TcO 4 , purified using the automated module here described, is within the Pharmacopoeia quality control parameters and is therefore a valid alternative to generator-produced 99m Tc. The resulting automated module is cost-effective and easily replicable for in-house production of high-purity Tc-99m by cyclotrons. Copyright © 2016 Elsevier Ltd. All rights reserved.

Synthesis of high purity monoglycerides from crude glycerol and palm stearin

Directory of Open Access Journals (Sweden)

Pakamas Chetpattananondh

2008-07-01

Full Text Available The optimum conditions for the glycerolysis of palm stearin and crude glycerol derived from biodiesel process werefound to be a reaction temperature of 200oC with a molar ratio of crude glycerol to palm stearin of 2.5:1, and a reaction timeof 20 minutes. The yield and purity of monoglycerides obtained under these conditions was satisfactory as compared withthe glycerolysis of pure glycerol. To increase the purity of monoglycerides a two-step process, removal of residual glyceroland crystallization, was proposed instead of either vacuum or molecular distillation. Residual glycerol was removed byadding hydrochloric acid followed by washing with hot water. Optimum conditions for crystallization were achieved byusing isooctane as a solvent and a turbine impeller speed of 200 rpm at a crystallization temperature of 35oC. A purity notexceeding 99 percent of monoglycerides was obtained with monopalmitin as the major product.

Copper alloys for high heat flux structure applications

International Nuclear Information System (INIS)

Zinkle, S.J.; Fabritsiev, S.A.

1994-01-01

The mechanical and physical properties of copper alloys are reviewed and compared with the requirements for high heat flux structural applications in fusion reactors. High heat flux structural materials must possess a combination of high thermal conductivity and high mechanical strength. The three most promising copper alloys at the present time are oxide dispersion-strengthened copper (Cu-Al 2 O 3 ) and two precipitation-hardened copper alloys (Cu-Cr-Zr and Cu-Ni-Be). These three alloys are capable of room temperature yield strengths >400 MPa and thermal conductivities up to 350 W/m-K. All of these alloys require extensive cold working to achieve their optimum strength. Precipitation-hardened copper alloys such Cu-Cr-Zr are susceptible to softening due to precipitate overaging and recrystallization during brazing, whereas the dislocation structure in Cu-Al 2 O 3 remains stabilized during typical high temperature brazing cycles. All three alloys exhibit good resistance to irradiation-induced softening and void swelling at temperatures below 300 degrees C. The precipitation-strengthened allows typically soften during neutron irradiation at temperatures above about 300 degrees C and therefore should only be considered for applications operating at temperatures 2 O 3 ) is considered to be the best candidate for high heat flux structural applications

The metallurgy of high temperature alloys

Science.gov (United States)

Tien, J. K.; Purushothaman, S.

1976-01-01

Nickel-base, cobalt-base, and high nickel and chromium iron-base alloys are dissected, and their microstructural and chemical components are assessed with respect to the various functions expected of high temperature structural materials. These functions include the maintenance of mechanical integrity over the strain-rate spectrum from creep resistance through fatigue crack growth resistance, and such alloy stability expectations as microstructural coarsening resistance, phase instability resistance and oxidation and corrosion resistance. Special attention will be given to the perennial conflict and trade-off between strength, ductility and corrosion and oxidation resistance. The newest developments in the constitution of high temperature alloys will also be discussed, including aspects relating to materials conservation.

Synthesis of high purity rutile nanoparticles from medium-grade Egyptian natural ilmenite

Directory of Open Access Journals (Sweden)

Mohamed G. Shahien

2015-09-01

Full Text Available The Egyptian magmatic ilmenite is classified as a medium-grade ore. The present work is an attempt to produce a high-quality TiO2 that can be used in several industries from this medium-grade raw material using the mechanical activation, carbothermic reduction, hydrochloric acid leaching and calcination. A mixture from the ilmenite (FeTiO3 and activated carbon was milled for 30 h. This mixture was annealed at 1200 °C for one hour and the product was leached by hydrochloric acid and calcined at 600 °C for two hours. The role of the ball milling was to grind the raw ilmenite to obtain the nano size, and the carbothermic reduction was to reduce all the Fe-Ti phases to a mixture from Fe metal and TiO2. Leaching procedure was carried out to remove all the Fe metal and obtain a high-grade TiO2. After leaching and calcination of the milled and annealed mixture of FeTiO3/C under the optimal conditions, TiO2 nanoparticles with a size of 10–100 nm and purity more than 95% were obtained. The qualifications of the synthesized high purity rutile nanoparticles from the Egyptian natural ilmenite match the conditions of many industrial applications.

Large-scale synthesis of high-purity well-aligned carbon nanotubes using pyrolysis of iron(II) phthalocyanine and acetylene

Science.gov (United States)

Liu, B. C.; Lee, T. J.; Lee, S. H.; Park, C. Y.; Lee, C. J.

2003-08-01

Well-aligned carbon nanotubes (CNTs) with high purity have been produced by pyrolysis of iron(II) phthalocyanine and acetylene at 800 °C. The synthesized CNTs have a length of 75 μm and diameters ranging from 20 to 60 nm. The CNTs have a bamboo-like structure and exhibit good crystallinity of graphite sheets. The growth rate of the CNTs was rapidly increased with adding C 2H 2. Our results demonstrate that the proposed growth method is suitable to large-scale synthesis of high-purity well-aligned CNTs on various substrates.

CO impurities effect on LaNi4∙7Al0∙3 hydrogen storage alloy ...

Indian Academy of Sciences (India)

Administrator

LaNi4∙7Al0∙3 alloy was prepared by vacuum induction melting in high purity helium atmosphere, .... The particle size of the ... tated Ni, and hydrogen molecules are dissociated into .... range of 30–150 °C, the sample weight loss is about 1∙3%.

Hysec Process: production of high-purity hydrogen from coke oven gas

Energy Technology Data Exchange (ETDEWEB)

Nishida, S

1984-01-01

An account is given of the development of the Hysec Process by the Kansai Netsukagaku and Mitsubishi Kakoki companies. The process is outlined and its special features noted. The initial development aim was to obtain high-purity hydrogen from coke oven gas by means of PSA. To achieve this, ways had to be found for removing the impurities in the coke oven gas and the trace amounts of oxygen which are found in the product hydrogen. The resulting hydrogen is 99.9999% pure. 3 references.

Effects of neutron irradiation to 63 dpa on the properties of various commercial copper alloys

International Nuclear Information System (INIS)

Brager, H.R.

1985-04-01

High purity copper and six commercial copper alloys were neutron irradiated to 47 and 63 dpa at about 450 0 C in the FFTF. Immersion density measurements showed a wide range of swelling behavior after irradiation to 63 dpa. At one extreme was CuBe in the aged and tempered (AT) condition which had densified slightly. At the other extreme was 20% CW Cu-0.1% Ag which swelled over 45%. Electrical resistivity measurements followed trends similar to previously published results for the same alloys irradiated to 16 dpa: a continued change in conductivity with fluence which appears to relate to void formation, transmutation products and coarsening of second phase precipitates. These results were compared with electrical conductivity of unirradiated alloys examined after aging for 10,000 hours. The most irradiation resistant high-conductivity copper alloys examined after 63 dpa are A125 and MZC. Cu-2.0Be, only a moderate-conductivity alloy, exhibits very consistent irradiation resistant properties

High strength tungsten heavy alloys with molybdenum additions

International Nuclear Information System (INIS)

Bose, A.; Sims, D.M.; German, R.M.

1987-01-01

Tungsten heavy alloys are candidates for numerous applications based on the unique combination of high density, high strength, and high ductility coupled with excellent machinability. Though there has been considerable research on heavy alloys, the primary focus has been on the ductility. These alloys are well suited for ballistic uses due to their high densities and it is expected that for superior ballistic performance, a high hardness, high strength and moderate ductility alloy would be ideal. The major goal of this investigation was to obtain heavy alloys with hardness greater than HRA 72. It is evident from the phase diagrams that molybdenum, which goes into solution in tungsten, nickel and iron, could act as a potential strengthening addition. With this in view, tungsten heavy alloys with molybdenum additions were fabricated from mixed elemental powders. A baseline composition of 90W-7Ni-3Fe was chosen to its good elongation and moderate strength. The molybdenum additions were made by replacing the tungsten. Compared to the baseline properties with no molybdenum addition, the strength and hardness showed a continuous increase with molybdenum addition. The ductility of the alloy continued to decrease with increasing molybdenum content, but even with 16% wt. % molybdenum of the elongation was still around 6%. An interesting facet of these alloying additions is the grain refinement that is brought about by adding to molybdenum to the system. The grain refinement is related to the lower solubility of tunbsten in the matrix due to partial displacement by molybdenum

High-temperature brazing, present situation and development trends - brazing alloys

International Nuclear Information System (INIS)

Lugscheider, E.

1980-01-01

The range of application of high-temperature brazing is described. The process is defined. High-temperature nickel-base brazing alloys (alloying constituents, types of products. properties of the brazing alloys) and high-temperature brazing alloys for special metals and ceramics are dealt with. (orig.) [de

Thermal Plasma Spheroidization of High-Nitrogen Stainless Steel Powder Alloys Synthesized by Mechanical Alloying

Science.gov (United States)

Razumov, Nikolay G.; Popovich, Anatoly A.; Wang, QingSheng

2018-03-01

This paper presents the results of experimental studies on the treatment of Fe-23Cr-11Mn-1N high-nitrogen stainless steel powder alloys, synthesized by the mechanical alloying (MA) of elemental powders in the flow of a thermal plasma. Fe-23Cr-11Mn-1N high-nitrogen stainless steel powder alloys were prepared by MA in the attritor under an argon atmosphere. For spheroidization of Fe-23Cr-11Mn-1N high-nitrogen stainless steel powder alloys, the TekSphero 15 plant manufactured by Tekna Plasma Systems Inc was used. The studies have shown the possibility of obtaining Fe-23Cr-11Mn-1N high-nitrogen spherical powders steel alloys from the powder obtained by MA. According to the results of a series of experiments, it was found that the results of plasma spheroidization of powders essentially depend on the size of the fraction due to some difference in the particle shape and flowability, and on the gas regime of the plasma torch. It is established that during the plasma spheroidization process, some of the nitrogen leaves the alloy. The loss rate of nitrogen depends on the size of the initial particles.

Physical and mechanical metallurgy of high purity Nb for accelerator cavities

International Nuclear Information System (INIS)

Bieler, T.R.; Wright, N.T.; Pourboghrat, F.; Compton, C.; Hartwig, K.T.; Baars, D.; Zamiri, A.; Chandrasekaran, S.; Darbandi, P.; Jiang, H.; Skoug, E.; Balachandran, S.; Ice, G.E.; Liu, W.

2010-01-01

In the past decade, high Q values have been achieved in high purity Nb superconducting radio frequency (SRF) cavities. Fundamental understanding of the physical metallurgy of Nb that enables these achievements is beginning to reveal what challenges remain to establish reproducible and cost-effective production of high performance SRF cavities. Recent studies of dislocation substructure development and effects of recrystallization arising from welding and heat treatments and their correlations with cavity performance are considered. With better fundamental understanding of the effects of dislocation substructure evolution and recrystallization on electron and phonon conduction, as well as the interior and surface states, it will be possible to design optimal processing paths for cost-effective performance using approaches such as hydroforming, which minimizes or eliminates welds in a cavity.

Fabrication and research of high purity germanium detectors with abrupt and thin diffusion layer

International Nuclear Information System (INIS)

Rodriguez Cabal, A. E.; Diaz Garcia, A.

1997-01-01

A different high purity germanium detector's fabrication method is described. A very thin diffusion film with an abrupt change of the type of conductivity is obtained. The fine diffusion layer thickness makes possibly their utilization in experimental systems in which all the data are elaborated directly on the computer. (author) [es

Fabrication of V-Cr-Ti-Y-Al-Si alloys by levitation melting

Energy Technology Data Exchange (ETDEWEB)

Chuto, Toshinori; Satou, Manabu; Abe, Katsunori [Department of Quantum Science and Energy Engineering, Tohoku University, Sendai, Miyagi (Japan); Nagasaka, Takuya; Muroga, Takeo [National Inst. for Fusion Science, Toki, Gifu (Japan); Shibayama, Tamaki [Center for Advanced Research of Energy Technology, Hokkaido University, Sapporo, Hokkaido (Japan); Tomiyama, Shigeki [Daido Bunseki Research Inc., Nagoya, Aichi (Japan); Sakata, Masafumi [Daido Steel Co. Ltd., Nagoya (Japan)

2000-09-01

Three allows of V-4Cr-4Ti type containing Si, Al and Y were fabricated by 2.5 kg scale levitation melting in this study. Workability and recrystallization behavior of the alloys were studied in order to establish the fabrication method of high-purity large ingot of V-Cr-Ti-Si-Al-Y type alloys, especially reducing interstitial impurity levels. Oxygen contents decreased with increasing yttrium contents and were kept below 180 mass ppm over wide region in the ingots. Nitrogen contents in the V-Cr-Ti-Y-Si-Al type alloys were only 100 mass ppm, which were as low as that in the starting materials. Only the V-4Cr-4Ti-0.1Y, Si, Al alloy could be cold-rolled at as-melted condition. Because large yttrium inclusions were observed in the alloys containing 0.5 mass%Y, it is necessary to optimize yttrium contents to avoid large inclusions and to obtain good workability. (author)

Fabrication of V-Cr-Ti-Y-Al-Si alloys by levitation melting

International Nuclear Information System (INIS)

Chuto, Toshinori; Satou, Manabu; Abe, Katsunori; Nagasaka, Takuya; Muroga, Takeo; Shibayama, Tamaki; Tomiyama, Shigeki; Sakata, Masafumi

2000-01-01

Three allows of V-4Cr-4Ti type containing Si, Al and Y were fabricated by 2.5 kg scale levitation melting in this study. Workability and recrystallization behavior of the alloys were studied in order to establish the fabrication method of high-purity large ingot of V-Cr-Ti-Si-Al-Y type alloys, especially reducing interstitial impurity levels. Oxygen contents decreased with increasing yttrium contents and were kept below 180 mass ppm over wide region in the ingots. Nitrogen contents in the V-Cr-Ti-Y-Si-Al type alloys were only 100 mass ppm, which were as low as that in the starting materials. Only the V-4Cr-4Ti-0.1Y, Si, Al alloy could be cold-rolled at as-melted condition. Because large yttrium inclusions were observed in the alloys containing 0.5 mass%Y, it is necessary to optimize yttrium contents to avoid large inclusions and to obtain good workability. (author)

High damping Fe-Mn martensitic alloys for engineering applications

International Nuclear Information System (INIS)

Baik, S.-H.

2000-01-01

Conventional methods for reducing vibration in engineering designs (i.e. by stiffening or detuning) may be undesirable or inadequate in conditions where size or weight must be minimized or where complex vibration spectra exist. Alloys which combine high damping capacity with good mechanical properties can provide attractive technical and economic solutions to problems involving seismic, shock and vibration isolation. To meet these trends, we have developed a new high damping Fe-17%Mn alloy. Also, the alloy has advantages of good mechanical properties and is more economical than any other known damping alloys (a quarter the cost of non-ferrous damping alloy). Thus, the high damping Fe-17%Mn alloy can be widely applied to household appliances, automobiles, industrial facilities and power plant components with its excellent damping capacity (SDC, 30%) and mechanical property (T.S. 700 MPa). It is the purpose of this paper to introduce the characterization of the high damping Fe-17%Mn alloy and the results of retrofit of several such applications. (orig.)

Crystallographic Analysis of Nucleation at Hardness Indentations in High-Purity Aluminum

DEFF Research Database (Denmark)

Xu, Chaoling; Zhang, Yubin; Lin, Fengxiang

2016-01-01

Nucleation at Vickers hardness indentations has been studied in high-purity aluminum cold-rolled 12 pct. Electron channeling contrast was used to measure the size of the indentations and to detect nuclei, while electron backscattering diffraction was used to determine crystallographic orientations....... It is found that indentations are preferential nucleation sites. The crystallographic orientations of the deformed grains affect the hardness and the nucleation potentials at the indentations. Higher hardness gives increased nucleation probabilities. Orientation relationships between nuclei developed...... they form. Finally, possible nucleation mechanisms are briefly discussed....

Thermal behavior of Ni (99.967% and 99.5% purity) deformed to an ultra-high strain by high pressure torsion

DEFF Research Database (Denmark)

Zhang, H.W.; Huang, Xiaoxu; Pippan, R.

2010-01-01

Polycrystalline Ni of two purities (99.967% (4N) and 99.5% (2N)) was deformed to an ultra-high strain of εvM = 100 (εvM, von Mises strain) by high pressure torsion at room temperature. The 4N and 2N samples at this strain are nanostructured with an average boundary spacing of 100 nm, a high density...

A Study of the Surface Quality of High Purity Copper after Heat Treatment

CERN Document Server

Aicheler, M; Atieh, S; Calatroni, S; Riddone, G; Lebet, S; Samoshkin, A

2011-01-01

Themanufacturing flow of accelerating structures for the compact linear collider, based on diamond-machined high purity copper components, include several thermal cycles (diffusion bonding, brazing of cooling circuits, baking in vacuum, etc.). The high temperature cycles may be carried out following different schedules and environments (vacuum, reducing hydrogen atmosphere, argon, etc.) and develop peculiar surface topographies which have been the object of extended observations. This study presents and discusses the results of scanning electron microscopy (SEM) and optical microscopy investigations.

Low-temperature internal friction in high-purity monocrystalline and impure polycrystalline niobium after plastic deformation

International Nuclear Information System (INIS)

Wasserbaech, W.; Thompson, E.

2001-01-01

The internal friction Q -1 of plastically deformed, high-purity monocrystalline and impure polycrystalline niobium specimens was measured in the temperature range between 65 mK and about 2 K. Plastic deformation has a pronounced effect on the internal friction Q -1 of the high-purity monocrystalline specimens, and the effect has been found to be almost temperature independent. By contrast, surprisingly, the internal friction Q -1 of the impure polycrystalline specimens was found to be almost independent of the extent of plastic deformation. Comparison of the experimental results with different models of a dynamic scattering of acoustic phonons by dislocations leads to the conclusion that the results cannot be explained with the two-level tunneling model. Instead it is suggested that a strong interaction between acoustic phonons and geometrical kinks in non-screw dislocations is responsible for the observed internal friction Q -1 . (orig.)

Protective claddings for high strength chromium alloys

Science.gov (United States)

Collins, J. F.

1971-01-01

The application of a Cr-Y-Hf-Th alloy as a protective cladding for a high strength chromium alloy was investigated for its effectiveness in inhibiting nitrogen embrittlement of a core alloy. Cladding was accomplished by a combination of hot gas pressure bonding and roll cladding techniques. Based on bend DBTT, the cladding alloy was effective in inhibiting nitrogen embrittlement of the chromium core alloy for up to 720 ks (200hours) in air at 1422 K (2100 F). A significant increase in the bend DBTT occurred with longer time exposures at 1422 K or short time exposures at 1589 K (2400 F).

Single-phase high-entropy alloys. An overview

Energy Technology Data Exchange (ETDEWEB)

Kozak, Roksolana; Steurer, Walter [ETH Zurich (Switzerland). Lab. of Crystallography; Sologubenko, Alla [ETH Zurich (Switzerland). Lab. of Nanotechnology

2015-02-01

The term 'high-entropy alloys (HEAs)' first appeared about 10 years ago defining alloys composed of n=5-13 principal elements with concentrations of approximately 100/n at.% each. Since then many equiatomic (or near equiatomic) single- and multi-phase multicomponent alloys were developed, which are reported for a combination of tunable properties: high hardness, strength and ductility, oxidation and wear resistance, magnetism, etc. In our paper, we focus on probably single-phase HEAs (solid solutions) out of all HEAs studied so far, discuss ways of their prediction, mechanical properties. In contrast to classical multielement/multiphase alloys, only single-phase multielement alloys (solid solutions) represent the basic concept underlying HEAs as mixing-entropy stabilized homogenous materials. The literature overview is complemented by own studies demonstrating that the alloys CrFeCoNi, CrFeCoNiAl{sub 0.3} and PdFeCoNi homogenized at 1300 and 1100 C, respectively, for 1 week are not single-phase HEAs, but a coherent mixture of two solid solutions.

Disgust and the moralization of purity.

Science.gov (United States)

Horberg, E J; Oveis, Christopher; Keltner, Dacher; Cohen, Adam B

2009-12-01

Guided by appraisal-based models of the influence of emotion upon judgment, we propose that disgust moralizes--that is, amplifies the moral significance of--protecting the purity of the body and soul. Three studies documented that state and trait disgust, but not other negative emotions, moralize the purity moral domain but not the moral domains of justice or harm/care. In Study 1, integral feelings of disgust, but not integral anger, predicted stronger moral condemnation of behaviors violating purity. In Study 2, experimentally induced disgust, compared with induced sadness, increased condemnation of behaviors violating purity and increased approval of behaviors upholding purity. In Study 3, trait disgust, but not trait anger or trait fear, predicted stronger condemnation of purity violations and greater approval of behaviors upholding purity. We found that, confirming the domain specificity of the disgust-purity association, disgust was unrelated to moral judgments about justice (Studies 1 and 2) or harm/care (Study 3). Finally, across studies, individuals of lower socioeconomic status (SES) were more likely than individuals of higher SES to moralize purity but not justice or harm/care.

Preparation, heat treatment, and mechanical properties of the uranium-5 weight percent chromium eutectic alloy

International Nuclear Information System (INIS)

Townsend, A.B.

1980-10-01

The eutectic alloy of uranium-5 wt % chromium (U-5Cr) was prepared from high-purity materials and cast into 1-in.-thick ingots. This material was given several simple heat treatments, the mechanical properties of these heat-treated samples were determined; and the microstructure was examined. Some data on the melting point and transformation temperatures were obtained

Potential utility of eGFP-expressing NOG mice (NOG-EGFP as a high purity cancer sampling system

Directory of Open Access Journals (Sweden)

Shima Kentaro

2012-06-01

Full Text Available Abstract Purpose It is still technically difficult to collect high purity cancer cells from tumor tissues, which contain noncancerous cells. We hypothesized that xenograft models of NOG mice expressing enhanced green fluorescent protein (eGFP, referred to as NOG-EGFP mice, may be useful for obtaining such high purity cancer cells for detailed molecular and cellular analyses. Methods Pancreato-biliary cancer cell lines were implanted subcutaneously to compare the tumorigenicity between NOG-EGFP mice and nonobese diabetic/severe combined immunodeficiency (NOD/SCID mice. To obtain high purity cancer cells, the subcutaneous tumors were harvested from the mice and enzymatically dissociated into single-cell suspensions. Then, the cells were sorted by fluorescence-activated cell sorting (FACS for separation of the host cells and the cancer cells. Thereafter, the contamination rate of host cells in collected cancer cells was quantified by using FACS analysis. The viability of cancer cells after FACS sorting was evaluated by cell culture and subsequent subcutaneous reimplantation in NOG-EGFP mice. Results The tumorigenicity of NOG-EGFP mice was significantly better than that of NOD/SCID mice in all of the analyzed cell lines (p  Conclusions This method provides a novel cancer sampling system for molecular and cellular analysis with high accuracy and should contribute to the development of personalized medicine.

High-Purity Semiconducting Single-Walled Carbon Nanotubes: A Key Enabling Material in Emerging Electronics.

Science.gov (United States)

Lefebvre, Jacques; Ding, Jianfu; Li, Zhao; Finnie, Paul; Lopinski, Gregory; Malenfant, Patrick R L

2017-10-17

Semiconducting single-walled carbon nanotubes (sc-SWCNTs) are emerging as a promising material for high-performance, high-density devices as well as low-cost, large-area macroelectronics produced via additive manufacturing methods such as roll-to-roll printing. Proof-of-concept demonstrations have indicated the potential of sc-SWCNTs for digital electronics, radiofrequency circuits, radiation hard memory, improved sensors, and flexible, stretchable, conformable electronics. Advances toward commercial applications bring numerous opportunities in SWCNT materials development and characterization as well as fabrication processes and printing technologies. Commercialization in electronics will require large quantities of sc-SWCNTs, and the challenge for materials science is the development of scalable synthesis, purification, and enrichment methods. While a few synthesis routes have shown promising results in making near-monochiral SWCNTs, gram quantities are available only for small-diameter sc-SWCNTs, which underperform in transistors. Most synthesis routes yield mixtures of SWCNTs, typically 30% metallic and 70% semiconducting, necessitating the extraction of sc-SWCNTs from their metallic counterparts in high purity using scalable postsynthetic methods. Numerous routes to obtain high-purity sc-SWCNTs from raw soot have been developed, including density-gradient ultracentrifugation, chromatography, aqueous two-phase extraction, and selective DNA or polymer wrapping. By these methods (termed sorting or enrichment), >99% sc-SWCNT content can be achieved. Currently, all of these approaches have drawbacks and limitations with respect to electronics applications, such as excessive dilution, expensive consumables, and high ionic impurity content. Excess amount of dispersant is a common challenge that hinders direct inclusion of sc-SWCNTs into electronic devices. At present, conjugated polymer extraction may represent the most practical route to sc-SWCNTs. By the use of

Cladding Alloys for Fluoride Salt Compatibility Final Report

Energy Technology Data Exchange (ETDEWEB)

Muralidharan, Govindarajan [ORNL; Wilson, Dane F [ORNL; Santella, Michael L [ORNL; Holcomb, David Eugene [ORNL

2011-05-01

This interim report provides an overview of several candidate technologies for cladding nickel-based corrosion protection layers onto high-temperature structural alloys. The report also provides a brief overview of the welding and weld performance issues associated with joining nickel-clad nickel-based alloys. From the available techniques, two cladding technologies were selected for initial evaluation. The first technique is a line-of-sight method that would be useful for coating large structures such as vessel interiors or large piping. The line-of-sight method is a laser-based surface cladding technique in which a high-purity nickel powder mixed into a polymer binder is first sprayed onto the surface, baked, and then rapidly melted using a high power laser. The second technique is a vapor phase technique based on the nickel-carbonyl process that is suitable for coating inaccessible surfaces such as the interior surfaces of heat exchangers. The final project report will feature an experimental evaluation of the performance of the two selected cladding techniques.

Local deposition of high-purity Pt nanostructures by combining electron beam induced deposition and atomic layer deposition

NARCIS (Netherlands)

Mackus, A.J.M.; Mulders, J.J.L.; Sanden, van de M.C.M.; Kessels, W.M.M.

2010-01-01

An approach for direct-write fabrication of high-purity platinum nanostructures has been developed by combining nanoscale lateral patterning by electron beam induced deposition (EBID) with area-selective deposition of high quality material by atomic layer deposition (ALD). Because virtually pure,

Effect of erbium modification on the microstructure, mechanical and corrosion characteristics of binary Mg–Al alloys

Energy Technology Data Exchange (ETDEWEB)

Seetharaman, Sankaranarayanan, E-mail: seetharaman.s@nus.edu.sg [Department of Mechanical Engineering, National University of Singapore, 9 Engineering Drive 1, 117576 (Singapore); Blawert, Carsten [Helmholtz-Zentrum Geesthacht, Magnesium Innovation Centre, Max-Planck-Straße 1, D-21502, Geesthacht (Germany); Ng, Baoshu Milton [Department of Mechanical Engineering, National University of Singapore, 9 Engineering Drive 1, 117576 (Singapore); Wong, Wai Leong Eugene [School of Mechanical and Systems Engineering, New Castle University International Singapore, 180 Ang Mo Kio Avenue 8, 569830 (Singapore); Goh, Chwee Sim [ITE Technology Development Centre, ITE College Central, 2 Ang Mo Kio Drive, 567720 (Singapore); Hort, Norbert [Helmholtz-Zentrum Geesthacht, Magnesium Innovation Centre, Max-Planck-Straße 1, D-21502, Geesthacht (Germany); Gupta, Manoj, E-mail: mpegm@nus.edu.sg [Department of Mechanical Engineering, National University of Singapore, 9 Engineering Drive 1, 117576 (Singapore)

2015-11-05

In this study, new erbium modified Mg–Al alloys were developed by integrating trace erbium (in the form of Al{sub 94.67}Er{sub 5.33} master alloy) into pure Mg using disintegrated melt deposition technique. The developed Er- modified Mg–Al alloys were investigated for their microstructural, mechanical and corrosion characteristics in comparison with their unmodified counterparts. Microstructural investigation revealed (i) improved purity, (ii) (marginal) grain refinement, (iii) more uniform second phase distribution and (iv) Al{sub 3}Er phase formation due to Er modification. Mechanical property measurements revealed an overall enhancement under indentation, tension and compression loads. A remarkable improvement in tensile ductility (without adverse effects on strength) by +19%, +29%, and +58% was obtained in Mg–3Al–0.1Er, Mg–6Al–0.3Er and Mg–9Al–0.5Er when compared to Mg–3Al, Mg–6Al and Mg–9Al respectively. While the Mg–6Al–0.3Er alloy exhibited best ductility, the Mg–9Al–0.5Er has the best strength under both tension and compression loads. Corrosion characteristics evaluated by hydrogen evolution, salt spray and electrochemical impedance experiments revealed improved corrosion resistance of Er modified Mg–Al alloys by the enhanced purity levels and the formation of Al–Er phases. - Highlights: • New erbium modified Mg–Al alloys successfully synthesized using DMD method. • Erbium modification promoted Al{sub 3}Er formation and improved the purity. • Remarkable improvement in tensile ductility obtained after erbium modification. • The developed erbium modified Mg–Al alloys exhibit improved corrosion resistance.

Effect of erbium modification on the microstructure, mechanical and corrosion characteristics of binary Mg–Al alloys

International Nuclear Information System (INIS)

Seetharaman, Sankaranarayanan; Blawert, Carsten; Ng, Baoshu Milton; Wong, Wai Leong Eugene; Goh, Chwee Sim; Hort, Norbert; Gupta, Manoj

2015-01-01

In this study, new erbium modified Mg–Al alloys were developed by integrating trace erbium (in the form of Al 94.67 Er 5.33 master alloy) into pure Mg using disintegrated melt deposition technique. The developed Er- modified Mg–Al alloys were investigated for their microstructural, mechanical and corrosion characteristics in comparison with their unmodified counterparts. Microstructural investigation revealed (i) improved purity, (ii) (marginal) grain refinement, (iii) more uniform second phase distribution and (iv) Al 3 Er phase formation due to Er modification. Mechanical property measurements revealed an overall enhancement under indentation, tension and compression loads. A remarkable improvement in tensile ductility (without adverse effects on strength) by +19%, +29%, and +58% was obtained in Mg–3Al–0.1Er, Mg–6Al–0.3Er and Mg–9Al–0.5Er when compared to Mg–3Al, Mg–6Al and Mg–9Al respectively. While the Mg–6Al–0.3Er alloy exhibited best ductility, the Mg–9Al–0.5Er has the best strength under both tension and compression loads. Corrosion characteristics evaluated by hydrogen evolution, salt spray and electrochemical impedance experiments revealed improved corrosion resistance of Er modified Mg–Al alloys by the enhanced purity levels and the formation of Al–Er phases. - Highlights: • New erbium modified Mg–Al alloys successfully synthesized using DMD method. • Erbium modification promoted Al 3 Er formation and improved the purity. • Remarkable improvement in tensile ductility obtained after erbium modification. • The developed erbium modified Mg–Al alloys exhibit improved corrosion resistance

Physical and mechanical metallurgy of high purity Nb for accelerator cavities

Directory of Open Access Journals (Sweden)

T. R. Bieler

2010-03-01

Full Text Available In the past decade, high Q values have been achieved in high purity Nb superconducting radio frequency (SRF cavities. Fundamental understanding of the physical metallurgy of Nb that enables these achievements is beginning to reveal what challenges remain to establish reproducible and cost-effective production of high performance SRF cavities. Recent studies of dislocation substructure development and effects of recrystallization arising from welding and heat treatments and their correlations with cavity performance are considered. With better fundamental understanding of the effects of dislocation substructure evolution and recrystallization on electron and phonon conduction, as well as the interior and surface states, it will be possible to design optimal processing paths for cost-effective performance using approaches such as hydroforming, which minimizes or eliminates welds in a cavity.

High conductivity Be-Cu alloys for fusion reactors

International Nuclear Information System (INIS)

Lilley, E.A.; Adachi, Takao; Ishibashi, Yoshiki

1995-01-01

The optimum material has not yet been identified. This will result in heat from plasma to the first wall and divertor. That is, because of cracks and melting by thermal power and shock. Today, it is considered to be some kinds of copper, alloys, however, for using, it must have high conductivity. And it is also needed another property, for example, high strength and so on. We have developed some new beryllium copper alloys with high conductivity, high strength, and high endurance. Therefore, we are introducing these new alloys as suitable materials for the heat sink in fusion reactors

Effect of microplastic deformation on the electron ultrasonic absorption in high-purity molybdenum monocrystals

International Nuclear Information System (INIS)

Pal'-Val', P.P.; Kaufmann, Kh.-J.

1983-01-01

The low temperature (100-6 K) linear absorption of ultrasound (88 kHz) by high purity molybdenum single crystals have been studied. Both unstrained samples and samples sub ected to microplastic deformation (epsilon 0 approximately 10 -4 , during 10 min, at 6 K. A new relaxation peak of absorption at 10 K has been found in strained samples

Review of lithium iron-base alloy corrosion studies

International Nuclear Information System (INIS)

DeVan, J.H.; Selle, J.E.; Morris, A.E.

1976-01-01

An extensive literature search was conducted on the compatibility of ferrous alloys with lithium, with the emphasis on austenitic stainless steels. The information is summarized and is divided into two sections. The first section gives a brief summary and the second is an annotated bibliography. Comparisons of results are complicated by differences in lithium purity, alloy composition, alloy treatment, flow rates, and lithium handling procedures. For long-term application, austenitic stainless steels appear to be limited to about 500 0 C. While corrosion can probably not be decreased to zero, a considerable reduction to tolerable and predictable amounts appears possible

An evaluation of a lathe-cut high-copper amalgam alloy.

Science.gov (United States)

Knibbs, P J; Plant, C G; Shovelton, D S; Jones, P A

1987-09-01

Modification of an amalgam alloy may give rise to improved physical properties. The physical properties of a newly formulated, single-composition lathe-cut amalgam alloy were studied and found to be superior to those of a conventional lathe-cut amalgam alloy. However, such modification in formulation may result in changes in the clinical handling properties of the material. The high-copper amalgam alloy was assessed by a panel of general practitioners who found that the general handling properties of the material were similar to those of conventional lathe-cut amalgam alloys. The longer term performance of the high-copper alloy was assessed by means of a blind, controlled clinical trial carried out by two operators. A 1-year assessment of the resulting restorations and tooth replicas could not distinguish between the high-copper alloy and a conventional alloy. The two alloys had both given good clinical results.

Precipitation of hydrides in high purity niobium after different treatments

Energy Technology Data Exchange (ETDEWEB)

Barkov, F.; Romanenko, A.; Trenikhina, Y.; Grassellino, A.

2013-01-01

Precipitation of lossy non-superconducting niobium hydrides represents a known problem for high purity niobium in superconducting applications. Using cryogenic optical and laser confocal scanning microscopy we have directly observed surface precipitation and evolution of niobium hydrides in samples after different treatments used for superconducting RF cavities for particle acceleration. Precipitation is shown to occur throughout the sample volume, and the growth of hydrides is well described by the fast diffusion-controlled process in which almost all hydrogen is precipitated at $T=140$~K within $\\sim30$~min. 120$^{\\circ}$C baking and mechanical deformation are found to affect hydride precipitation through their influence on the number of nucleation and trapping centers.

Dynamic high-temperature characterization of an iridium alloy in tension

Energy Technology Data Exchange (ETDEWEB)

Song, Bo [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Nelson, Kevin [Sandia National Lab. (SNL-CA), Livermore, CA (United States); Jin, Helena [Sandia National Lab. (SNL-CA), Livermore, CA (United States); Lipinski, Ronald J. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Bignell, John [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Ulrich, G. B. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); George, E. P. [Ruhr Univ., Bochum (Germany)

2015-09-01

Iridium alloys have been utilized as structural materials for certain high-temperature applications, due to their superior strength and ductility at elevated temperatures. The mechanical properties, including failure response at high strain rates and elevated temperatures of the iridium alloys need to be characterized to better understand high-speed impacts at elevated temperatures. A DOP-26 iridium alloy has been dynamically characterized in compression at elevated temperatures with high-temperature Kolsky compression bar techniques. However, the dynamic high-temperature compression tests were not able to provide sufficient dynamic high-temperature failure information of the iridium alloy. In this study, we modified current room-temperature Kolsky tension bar techniques for obtaining dynamic tensile stress-strain curves of the DOP-26 iridium alloy at two different strain rates (~1000 and ~3000 s-1) and temperatures (~750°C and ~1030°C). The effects of strain rate and temperature on the tensile stress-strain response of the iridium alloy were determined. The DOP-26 iridium alloy exhibited high ductility in stress-strain response that strongly depended on both strain rate and temperature.

Induction skull melting facility: an advanced system for electromagnetic processing of metals and alloys

International Nuclear Information System (INIS)

Sugilal, G.; Agarwal, K.

2017-01-01

Induction Skull Melting (ISM) is an advanced technology for processing highly refractory and extremely reactive metals and their alloys to produce ultra-high purity products. In ISM, the metallic charge is melted in a water-cooled, copper crucible. The crucible is segmented so that the magnetic field can penetrate into the metallic charge to be melted. By virtue of the strong electromagnetic stirring, the ISM technology can also be used to homogenize alloys of metals, which are difficult to be combined uniformly in composition due to large difference in specific gravity. In view of various important applications in frontier areas of material research, development and production, Bhabha Atomic Research Centre developed the ISM technology indigenously

Variation of low temperature internal friction of microplastic deformation of high purity molybdenum single crystals

International Nuclear Information System (INIS)

Pal-Val, P.P.; Kaufmann, H.J.

1984-01-01

Amplitude and temperature spectra of ultrasound absorption in weakly deformed high purity molybdenum single crystals of different orientations were measured. The results were discussed in terms of parameter changes related to quasiparticle or dislocation oscillations, respectively, dislocation point defect interactions as well as defect generation at microplastic deformation. (author)

Variation of low temperature internal friction of microplastic deformation of high purity molybdenum single crystals

Energy Technology Data Exchange (ETDEWEB)

Pal-Val, P.P. (AN Ukrainskoj SSR, Kharkov. Fiziko-Tekhnicheskij Inst. Nizkikh Temperatur); Kaufmann, H.J. (Akademie der Wissenschaften der DDR, Berlin)

1984-08-01

Amplitude and temperature spectra of ultrasound absorption in weakly deformed high purity molybdenum single crystals of different orientations were measured. The results were discussed in terms of parameter changes related to quasiparticle or dislocation oscillations, respectively, dislocation point defect interactions as well as defect generation at microplastic deformation.

Strengthening Purity: Moral Purity as a Mediator of Direct and Extended Cross-Group Friendships on Sexual Prejudice.

Science.gov (United States)

Vezzali, Loris; Brambilla, Marco; Giovannini, Dino; Paolo Colucci, Francesco

2017-01-01

The present research investigated whether enhanced perceptions of moral purity drive the effects of intergroup cross-group friendships on the intentions to interact with homosexuals. High-school students (N = 639) reported their direct and extended cross-group friendships with homosexuals as well as their beliefs regarding the moral character of the sexual minority. Participants further reported their desire to interact with homosexuals in the future. Results showed that both face-to-face encounters and extended contact with homosexuals increased their perceived moral purity, which in turn fostered more positive behavioral intentions. Results further revealed the specific role of moral purity in this sense, as differential perceptions along other moral domains (autonomy and community) had no mediation effects on behavioral tendencies toward homosexuals. The importance of these findings for improving intergroup relations is discussed, together with the importance of integrating research on intergroup contact and morality.

Irradiation-assisted stress corrosion cracking of austenitic alloys

International Nuclear Information System (INIS)

Was, G.S.; Atzmon, M.

1991-01-01

An experimental program has been conducted to determine the mechanism of irradiation-assisted stress-corrosion cracking (IASCC) in austenitic stainless steel. High-energy protons have been used to produce grain boundary segregation and microstructural damage in samples of controlled impurity content. The densities of network dislocations and dislocation loops were determined by transmission electron microscopy and found to resemble those for neutron irradiation under LWR conditions. Grain boundary compositions were determined by in situ fracture and Auger spectroscopy, as well as by scanning transmission electron microscopy. Cr depletion and Ni segregation were observed in all irradiated samples, with the degree of segregation depending on the type and amount of impurities present. P, and to a lesser extent P, impurities were observed to segregate to the grain boundaries. Irradiation was found to increase the susceptibility of ultra-high-purity (UHP), and to a much lesser extent of UHP+P and UHP+S, alloys to intergranular SCC in 288 degree C water at 2 ppm O 2 and 0.5 μS/cm. No intergranular fracture was observed in arcon atmosphere, indicating the important role of corrosion in the embrittlement of irradiated samples. The absence of intergranular fracture in 288 degree C argon and room temperature tests also suggest that the embrittlement is not caused by hydrogen introduced by irradiation. Contrary to common belief, the presence of P impurities led to a significant improvement in IASCC over the ultrahigh purity alloy

Electron beam welding of high-purity copper accelerator cells

International Nuclear Information System (INIS)

Delis, K.; Haas, H.; Schlebusch, P.; Sigismund, E.

1986-01-01

The operating conditions of accelerator cells require high thermal conductivity, low gas release in the ultrahigh vacuum, low content of low-melting metals and an extremely good surface quality. In order to meet these requirements, high-purity copper (OFHC, Grade 1, according to ASTM B 170-82 and extra specifications) is used as structural material. The prefabricated components of the accelerator cells (noses, jackets, flanges) are joined by electron beam welding, the weld seam being assessed on the basis of the same criteria as the base material. The welding procedures required depend, first, on the material and, secondly, on the geometries involved. Therefore experimental welds were made first on standardized specimens in order to study the behaviour of the material during electron beam welding and the influence of parameter variations. The welded joints of the cell design were planned on the basis of these results. Seam configuration, welding procedures and the parameters were optimized on components of original geometry. The experiments have shown that high-quality joints of this grade of copper can be produced by the electron beam welding process, if careful planning and preparation of the seams and adequate containment of the welding pool are assured. (orig.)

General and localized corrosion of carbon and low-alloy steels in oxygenated high-temperature water. Final report

International Nuclear Information System (INIS)

Macdonald, D.D.; Smialowska, S.; Pednekar, S.

1983-02-01

The susceptibilities to stress corrosion cracking (SCC) of two carbon steels, SA106-grB and SA333-gr6, which are used in seamless BWR piping, and a low-alloy pressure vessel steel, A508-C12, were studied in high purity water as a function of oxygen concentration (0.16 to 8 ppM) and temperature (50 to 288 0 C) . The susceptibility to SCC was measured using the slow strain rate technique. The fracture surfaces of the test specimens were also examined using SEM to determine the mode of failure. In water containing 1 and 8 ppM oxygen and at temperatures above 135 0 C, transgranular stress corrosion cracking (TGSCC) was observed to occur in A508-C12, SA333-gr6 and SA106grB steels at very high stresses. The susceptibility to SCC increased with temperature

Facile synthesis of upconversion nanoparticles with high purity using lanthanide oleate compounds

Science.gov (United States)

Kang, Ning; Ai, Chao-Chao; Zhou, Ya-Ming; Wang, Zuo; Ren, Lei

2018-02-01

A novel strategy for preparing highly pure NaYF4-based upconversion nanoparticles (UCNPs) was developed using lanthanide oleate compounds [Ln(OA)3] as the precursor, denoted as the Ln-OA preparation method. Compared to the conventional solvothermal method for synthesizing UCNPs using lanthanide chloride compounds (LnCl3) as the precursor (denoted as the Ln-Cl method), the Ln-OA strategy exhibited the merits of high purity, reduced purification process and a uniform size in preparing core and core-shell UCNPs excited by a 980 or 808 nm near infrared (NIR) laser. This work sheds new insight on the preparation of UCNPs and promotes their application in biomedical fields.

Experimental and numerical simulations of ELM-like transient damage behaviors to different grade tungsten and tungsten alloys

Energy Technology Data Exchange (ETDEWEB)

Liu, Xiang, E-mail: xliu@swip.ac.cn [Southwestern Institute of Physics, P.O. Box 432, Chengdu 610041, Sichuan (China); Lian, Youyun; Chen, Lei; Chen, Zhenkui; Chen, Jiming; Duan, Xuru [Southwestern Institute of Physics, P.O. Box 432, Chengdu 610041, Sichuan (China); Fan, Jinlian [Central South University, Changsha 410083 (China); Song, Jiupeng [Xiamen Honglu Tungsten & Molybdenum Industry Co., Ltd, Xiamen (China)

2015-08-15

Transient heat loads, such as plasma disruptions and ELMs, could induce plastic deformations, cracking, melting, even fatigue cracks and creep of tungsten (W) surface. A high purity W, CVD-W coating, TiC dispersion strengthened and K doped tungsten alloys were tested in a 60 kW electron-beam facility by simulating the transient load events under different base temperatures. It was found that CVD-W, W-TiC and W-K alloys have higher crack thresholds than high purity W, meanwhile CVD-W is more sensitive to the crack disappearing at elevated base temperatures. On the other hand, repetitive pulse loading like ELMs can induce serious network cracks even the power density was quite lower than the crack threshold determined by a single shot. The ABAQUS code was used to simulate the crack behaviors of ITER grade pure W by a single shot and a FE-SAFE code was adopted to estimate the fatigue life under ELMs-like loads. A good agreement with experiment results was found.

Structural transformations of heat treated Co-less high entropy alloys

Science.gov (United States)

Mitrica, D.; Tudor, A.; Rinaldi, A.; Soare, V.; Predescu, C.; Berbecaru, A.; Stoiciu, F.; Badilita, V.

2018-03-01

Co is considered to be one of the main ingredients in superalloys. Co is considered a critical element and its substitution is difficult due to its unique ability to form high temperature stable structures with high mechanical and corrosion/oxidation resistance. High entropy alloys (HEA) represent a relatively new concept in material design. HEA are characterised by a high number of alloying elements, in unusually high proportion. Due to their specific particularities, high entropy alloys tend to form predominant solid solution structures that develop potentially high chemical, physical and mechanical properties. Present paper is studying Co-less high entropy alloys with high potential in severe environment applications. The high entropy alloys based on Al-Cr-Fe-Mn-Ni system were prepared by induction melting and casting under protective atmosphere. The as-cast specimens were heat treated at various temperatures to determine the structure and property behaviour. Samples taken before and after heat treatment were investigated for chemical, physical, structural and mechanical characteristics. Sigma phase composition and heat treatment parameters had major influence over the resulted alloy structure and properties.

Se-Se isoelectronic centers in high purity CdTe

Energy Technology Data Exchange (ETDEWEB)

Najjar, Rita; Andre, Regis; Mariette, Henri [CEA-CNRS, Nanophysique et Semiconducteurs, Institut Neel, 25 rue des martyrs, 38042 Grenoble (France); Golnik, Andrzej; Kossacki, Piotr; Gaj, Jan A. [Institute of Experimental Physics, University of Warsaw, Hoza 69, 00-681 Warsaw (Poland)

2010-06-15

We evidence zero-dimensional exciton states trapped on isoelectronic Se centers in CdTe quantum wells, {delta}-doped with Se. Thanks to special precautions taken to have very high purity CdTe heterostructures, it is possible to observe, in photoluminescence spectra, sharp discrete lines arising from individual centers related to the Se doping. These emission lines appear at about 40 meV below the CdTe band gap energy. The most prominent lines are attributed to the recombination of excitons bound to nearest-neighbor selenium pairs in a tetrahedral CdTe environment. This assignment is confirmed by a common linear polarization direction of the emitted light, parallel to <110>. These excitons localized on individual isoelectronic traps are good candidates as single photon emitters (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

[Compressive and bend strength of experimental admixed high copper alloys].

Science.gov (United States)

Sourai, P; Paximada, H; Lagouvardos, P; Douvitsas, G

1988-01-01

Mixed alloys for dental amalgams have been used mainly in the form of admixed alloys, where eutectic spheres are blend with conventional flakes. In the present study the compressive strength, bend strength and microstructure of two high-copper alloys (Tytin, Ana-2000) is compared with three experimental alloys prepared of the two high copper by mixing them in proportions of 3:1, 1:1 and 1:3 by weight. The results revealed that experimental alloys inherited high early and final strength values without any significant change in their microstructure.

Corrosion behaviour of high temperature alloys in impure helium environments

International Nuclear Information System (INIS)

Shindo, Masami; Quadakkers, W.J.; Schuster, H.

1986-01-01

Corrosion tests with Ni-base high temperature alloys were carried out at 900 and 950 0 C in simulated high temperature reactor helium environments. It is shown that the carburization and decarburization behaviour is strongly affected by the Cr and Ti(Al) contents of the alloys. In carburizing environments, additions of Ti, alone or in combination with Al, significantly improve the carburization resistance. In oxidizing environment, the alloys with high Cr and Al(Ti) contents are the most resistant against decarburization. In this environment alloys with additions of Ti and Al show poor oxidation resistance. The experimental results obtained are compared with a recently developed theory describing corrosion of high temperature alloys in high temperature reactor helium environments. (orig.)

Effect of composition on the fabrication and properties of Ag-Cu alloy sheathed (Bi,Pb)2223 tapes

International Nuclear Information System (INIS)

Nakamura, Yuichi; Nakashima, Sohei; Inada, Ryoji; Oota, Akio

2004-01-01

To achieve high J c values as well as high mechanical strength, the effects of Ag-Cu alloy sheath and initial composition of precursor on the microstructure and J c properties of Ag-Cu alloy sheathed tapes were investigated. The alkaline-earth cuprate particles were found to form preferentially near the interface between superconducting core and sheath. Although the worse (Bi,Pb)2223 purity and microstructure of alloy sheathed tapes, the reduction of J c values of the tapes was small especially in 7-filaments tapes. This might be explained by the well grain alignment of (Bi,Pb)2223 into the middle region of the filament due to the high strength of alloy sheath. The usage of the Cu deficient composition was effective to reduce the total amount of 14:24 particle while the filament thickness should be thin to maintain J c values for Ag-Cu alloy sheathed tapes due to the lack of Cu diffusion from the sheath to convert 2212 into (Bi,Pb) in the middle region of the filament

Operation of a high-purity silicon diode alpha particle detector at 1.4 K

International Nuclear Information System (INIS)

Martoff, C.J.; Kaczanowicz, E.; Neuhauser, B.J.; Lopez, E.; Zhang, Y.; Ziemba, F.P.

1991-01-01

Detection of alpha particles at temperatures as low as 1.4 K was demonstrated using a specially fabricated Si diode. The diode was 475 mm 2 by 0.280 mm thick, fabricated from high-purity silicon with degenerately doped contacts. This is an important step toward development of dual-mode (ionization plus phonon) silicon detectors for low energy radiation. (orig.)

Operation of a high-purity silicon diode alpha particle detector at 1. 4 K

Energy Technology Data Exchange (ETDEWEB)

Martoff, C.J.; Kaczanowicz, E. (Temple Univ., Philadelphia, PA (USA)); Neuhauser, B.J.; Lopez, E.; Zhang, Y. (San Francisco State Univ., CA (USA)); Ziemba, F.P. (Quantrad Corp. (USA))

1991-03-01

Detection of alpha particles at temperatures as low as 1.4 K was demonstrated using a specially fabricated Si diode. The diode was 475 mm{sup 2} by 0.280 mm thick, fabricated from high-purity silicon with degenerately doped contacts. This is an important step toward development of dual-mode (ionization plus phonon) silicon detectors for low energy radiation. (orig.).

High-strength and high-RRR Al-Ni alloy for aluminum-stabilized superconductor

CERN Document Server

Wada, K; Sakamoto, H; Yamamoto, A; Makida, Y

2000-01-01

The precipitation type aluminum alloys have excellent performance as the increasing rate in electric resistivity with additives in the precipitation state is considerably low, compared to that of the aluminum alloy with additives in the solid-solution state. It is possible to enhance the mechanical strength without remarkable degradation in residual resistivity ratio (RRR) by increasing content of selected additive elements. Nickel is the suitable additive element because it has very low solubility in aluminum and low increasing rate in electric resistivity, and furthermore, nickel and aluminum form intermetallic compounds which effectively resist the motion of dislocations. First, Al-0.1wt%Ni alloy was developed for the ATLAS thin superconducting solenoid. This alloy achieved high yield strength of 79 MPa (R.T.) and 117 MPa (4.2 K) with high RRR of 490 after cold working of 21% in area reduction. These highly balanced properties could not be achieved with previously developed solid-solution aluminum alloys. ...

Contribution to the study of the conductivity of high purity water

International Nuclear Information System (INIS)

Nens, Ch.

1964-01-01

In this work a study is made more particularly of two points: the production of high purity water and the estimation of this purity by means of conductivity measurements. As far as water purification is concerned it is observed that the de-ionisation produced by ion exchange resins in mixed beds leads to a water having a lower conductivity than that obtained by distillation. This low conductivity however, measured at the column exit before the water comes into contact with air is not stable. In fact the carbon dioxide in the water gives rise to an equilibrium with production of the ions HCO 3 - , CO 3 -- . These ions are retained during the passage of the water through the resins. They reappear again at the column exit as a result of the displacement of the hydration equilibrium of CO 2 ; because of this the conductivity of the water increases with time. The water obtained by successive distillations does not behave in the same way because no carbon dioxide is present. Distillation is however a costly purification process on an industrial scale, especially if large quantities of water have to be treated. The measurement of these low conductivities is very delicate. The method employed makes use of a direct current and gives reproducible results if care is taken to exclude interfering electric fields by screening the apparatus. (author) [fr

Streamer knotwilg branching: sudden transition in morphology of positive streamers in high-purity nitrogen

International Nuclear Information System (INIS)

Heijmans, L C J; Clevis, T T J; Nijdam, S; Van Veldhuizen, E M; Ebert, U

2015-01-01

We describe a peculiar branching phenomenon in positive repetitive streamer discharges in high purity nitrogen. We name it knotwilg branching after the Dutch word for a pollard willow tree. In a knotwilg branching a thick streamer suddenly splits into many thin streamers. Under some conditions this happens for all streamers in a discharge at about the same distance from the high-voltage electrode tip. At this distance, the thick streamers suddenly bend sharply and appear to propagate over a virtual surface surrounding the high-voltage electrode, rather than following the background electric field lines. From these bent thick streamers many, much thinner, streamers emerge that roughly follow the background electric field lines, creating the characteristic knotwilg branching. We have only found this particular morphology in high purity nitrogen at pressures in the range 50 to 200 mbar and for pulse repetition rates above 1 Hz; the experiments were performed for an electrode distance of 16 cm and for fast voltage pulses of 20 or 30 kV. These observations clearly disagree with common knowledge on streamer propagation. We have analyzed the data of several tens of thousands of discharges to clarify the phenomena. We also present some thoughts on how the ionization of the previous discharges could concentrate into some pre-ionization region near the needle electrode and create the knotwilg morphology, but we present no final explanation. (paper)

High purity hydrogen production system by the PSA method

Energy Technology Data Exchange (ETDEWEB)

1986-01-01

In a process developed by Nippon Steel, coke oven gas is compressed and purified of tarry matter, sulphur compounds and gum-formers by adsorption. It is then passed through a three-tower pressure-swing adsorption system to recover hydrogen whose purity can be selected in the range 99 to 99.999%. A composite adsorption agent is used.

Fabrication of spherical high-nitrogen stainless steel powder alloys by mechanical alloying and thermal plasma spheroidization

Science.gov (United States)

Razumov, Nikolay G.; Wang, Qing Sheng; Popovich, Anatoly A.; Shamshurin, Aleksey I.

2018-04-01

This paper describes the results of experimental studies on the treatment of Fe-23Cr-11Mn-1N high-nitrogen stainless steel powder alloys, synthesized by the mechanical alloying (MA) of elemental powders in the flow of a radio frequency thermal plasma. The as-milled powder with irregular particles were successfully converted into spherical high-nitrogen stainless steel powder alloy. Measurement of the residual nitrogen content in the obtained powder, shown that during the plasma spheroidization process, part of the nitrogen escapes from the alloy.

Processing of Cu-Cr alloy for combined high strength and high conductivity

Directory of Open Access Journals (Sweden)

A.O Olofinjanaa

2017-11-01

Full Text Available High strength and high conductivity (HSHC are two intrinsic properties difficult to combine in metallic alloy design because; almost all strengthening mechanisms also lead to reduced conductivity. Precipitation hardening by nano-sized precipitates had proven to be the most adequate way to achieve the optimum combination of strength and conductivity in copper based alloys. However, established precipitation strengthened Cu- alloys are limited to very dilute concentration of solutes thereby limiting the volume proportion hardening precipitates. In this work, we report the investigation of the reprocessing of higher Cr concentration Cu- based alloys via rapid solidification. It is found that the rapid solidification in the as-cast ribbon imposed combined solution extension and ultra-refinement of Cr rich phases. X-ray diffraction evidences suggest that the solid solution extension was up to 6wt%Cr. Lattice parameters determined confirmed the many folds extension of solid solution of Cr in Cu.  Thermal aging studies of the cast ribbons indicated that peak aging treatments occurred in about twenty minutes. Peak aged hardness ranged from about 200 to well over 300Hv. The maximum peak aged hardness of 380Hv was obtained for alloy containing 6wt.%Cr but with conductivity of about 50%IACS. The best combined strength/conductivity was obtained for 4wt.%Cr  alloy with hardness of 350HV and conductivity of 80% IACS. The high strengths observed are attributed to the increased volume proportion of semi-coherent Cr rich nano-sized precipitates that evolved from the supersaturated solid solution of Cu-Cr that was achieved from the high cooling rates imposed by the ribbon casting process. The rapid overaging of the high Cr concentration Cu-Cr alloy is still a cause for concern in optimising the process for reaching peak HSHC properties. It is still important to investigate a microstructural design to slow or severely restrict the overaging process. The optimum

A fundamental self-generated quenching center for lanthanide-doped high-purity solids

International Nuclear Information System (INIS)

Auzel, F.

2002-01-01

An intrinsic self-generated quenching center for lanthanide-doped high-purity solids is presented for transitions, which cannot be quenched by cross-relaxation. This center, in fact a cluster-like pair of active centers, is shown to come from a particular multiphonon-assisted energy transfer between them. Being due to the vibronic properties of the host it cannot be suppressed. Its role in lanthanide first excited states self-quenching is analyzed and a simple mathematical expression is derived. This law is compared with experimental results for self-quenching in Er-doped fluorophosphate glasses

Measurement of oxide-layer thickness of internal granules in high-purity aluminium

International Nuclear Information System (INIS)

Takacs, S.; Ditroi, F.; Mahunka, I.

1989-01-01

Charged-particle activation analysis was used for the determination of bulk oxygen concentration in aluminium. High-purity aluminium samples and mixtures containing different amounts of alumina were irradiated by 13 MeV 3 He particles. The aim of the investigation was to determine the oxide-layer thickness on the surface of internal aluminium granules. The measurement was carried out by determining the bulk oxygen concentration in the samples, and calculating the oxide-layer thickness, by using model conditions about the microstructure of the aluminium samples. (author) 5 refs

Annealing behavior of high permeability amorphous alloys

International Nuclear Information System (INIS)

Rabenberg, L.

1980-06-01

Effects of low temperature annealing on the magnetic properties of the amorphous alloy Co 71 4 Fe 4 6 Si 9 6 B 14 4 were investigated. Annealing this alloy below 400 0 C results in magnetic hardening; annealing above 400 0 C but below the crystallization temperature results in magnetic softening. Above the crystallization temperature the alloy hardens drastically and irreversibly. Conventional and high resolution transmission electron microscopy were used to show that the magnetic property changes at low temperatures occur while the alloy is truly amorphous. By imaging the magnetic microstructures, Lorentz electron microscopy has been able to detect the presence of microscopic inhomogeneities in this alloy. The low temperature annealing behavior of this alloy has been explained in terms of atomic pair ordering in the presence of the internal molecular field. Lorentz electron microscopy has been used to confirm this explanation

Microstructural development from interdiffusion and reaction between U−Mo and AA6061 alloys annealed at 600° and 550 °C

Energy Technology Data Exchange (ETDEWEB)

Perez, E., E-mail: Emmanuel.Perez@inl.gov [Nuclear Fuels and Materials Division, Idaho National Laboratory, P.O. Box 1625, Idaho Falls, ID 83415-6188 (United States); Keiser, D.D., E-mail: dennis.keiser@inl.gov [Nuclear Fuels and Materials Division, Idaho National Laboratory, P.O. Box 1625, Idaho Falls, ID 83415-6188 (United States); Sohn, Y.H., E-mail: yongho.sohn@ucf.edu [Department of Materials Science and Engineering, University of Central Florida, 4000 Central Florida Blvd., Orlando, FL 32816 (United States)

2016-08-15

The U.S. Material Management and Minimization Reactor Conversion Program is developing low enrichment fuel systems encased in Al-alloy for use in research and test reactors. Monolithic fuel plates have local regions where the U−Mo fuel plate may come into contact with the Al-alloy 6061 (AA6061) cladding. This results in the development of interdiffusion zones with complex microstructures with multiple phases. In this study, the microstructural development of diffusion couples, U−7 wt%Mo, U−10 wt%Mo, and U−12 wt%Mo vs. AA6061, annealed at 600 °C for 24 h and at 550 °C for 1, 5, and 20 h, were analyzed by scanning electron microscopy with x-ray energy dispersive spectroscopy. The microstructural development and kinetics were compared to diffusion couples U−Mo vs. high purity Al and binary Al−Si alloys. The diffusion couples developed complex interaction regions where phase development was influenced by the alloying additions of the AA6061. - Highlights: • Diffusion couples of U−7Mo, U−10Mo, and U−12Mo vs. AA6061 were analyzed by SEM with XEDS. • The couples were annealed at 600 °C for 24 h and at 550 °C for 1, 5 and 20 h. • The interaction regions were more complex than those in diffusion couples of U−Mo vs. high purity Al and Al−Si alloys. • Analysis showed that the alloying additions of the AA6061 were present in the interaction regions. • Phase development was significantly influenced by the alloying additions of the AA6061.

Obtaining high purity silica from rice hulls

Directory of Open Access Journals (Sweden)

José da Silva Júnior

2010-01-01

Full Text Available Many routes for extracting silica from rice hulls are based on direct calcining. These methods, though, often produce silica contaminated with inorganic impurities. This work presents the study of a strategy for obtaining silica from rice hulls with a purity level adequate for applications in electronics. The technique is based on two leaching steps, using respectively aqua regia and Piranha solutions, which extract the organic matrix and inorganic impurities. The material was characterized by Fourier-transform infrared spectroscopy (FTIR, powder x-ray diffraction (XRD, x-ray fluorescence (XRF, scanning electron microscopy (SEM, particle size analysis by laser diffraction (LPSA and thermal analysis.

Neutron activation determination of impurities in high-purity bismuth with separation of matrix in form of hydroxide

International Nuclear Information System (INIS)

Artyukhin, P.I.; Shavinskij, B.M.; Mityakin, Yu.L.

1979-01-01

The technique of neutron activation determination of 15 impurity elements (Au, Ag, Ba, Cd, Co, Cs, Cu, Hg, K, Na, Ni, Se, Sr, Te, Zn) in high-purity bismuth (impurity content is approximately 10 -6 -10 -10 %) is presented. Bismuth hydroxide precipitation by ammonia from nitric acid solutions was used to separate bismuth from alkali, alkaline earth metals and elements forming stable ammines. Gold, selenium and tellurium are isolated in the form of metals at reduction by muriatic hydrazine. Results of analyzing two samples of special purity bismuth are presented. Neutron flux comprised 0.8-1x10 13 n/cm 2 xs. Radiation time was equal to 90 hours

Ternary alloying study of MoSi2

International Nuclear Information System (INIS)

Yi, D.; Li, C.; Akselsen, O.M.; Ulvensoen, J.H.

1998-01-01

Ternary alloying of MoSi 2 with adding a series of transition elements was investigated by X-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy (TEM), and energy dispersive spectroscopy (EDS). Iron, Co, Ni, Cr, V, Ti, and Nb were chosen as alloying elements according to the AB 2 structure map or the atomic size factor. The studied MoSi 2 base alloys were prepared by the arc melting process from high-purity metals. The EDS analysis showed that Fe, Co, and Ni have no solid solubility in as-cast MoSi 2 , while Cr, V, Ti, and Nb exhibit limited solid solubilities, which were determined to be 1.4 ± 0.7, 1.4 ± 0.4, 0.4 ± 0.1, and 0.8 ± 0.1. Microstructural characterization indicated that Mo-Si-M VIII (M VIII = Fe, Co, Ni) and Mo-Si-Cr alloys have a two-phase as-cast microstructure, i.e., MoSi 2 matrix and the second-phase FeSi 2 , CoSi, NiSi 2 , and CrSi 2 , respectively. In as-cast Mo-Si-V, Mo-Si-Ti, and Mo-Si-Nb alloys, besides MoSi 2 and C40 phases, the third phases were observed, which have been identified to be (Mo, V) 5 Si 3 , TiSi 2 , and (Mo, Nb) 5 Si 3

High-entropy alloys as high-temperature thermoelectric materials

Energy Technology Data Exchange (ETDEWEB)

Shafeie, Samrand [Surface and Microstructure Engineering Group, Materials and Manufacturing Technology, Chalmers University of Technology, SE-41296 Gothenburg (Sweden); Department of Chemistry and Chemical Engineering, Chalmers University of Technology, SE-41296 Gothenburg (Sweden); Guo, Sheng, E-mail: sheng.guo@chalmers.se [Surface and Microstructure Engineering Group, Materials and Manufacturing Technology, Chalmers University of Technology, SE-41296 Gothenburg (Sweden); Hu, Qiang [Institute of Applied Physics, Jiangxi Academy of Sciences, Nanchang 330029 (China); Fahlquist, Henrik [Bruker AXS Nordic AB, 17067 Solna (Sweden); Erhart, Paul [Department of Applied Physics, Chalmers University of Technology, SE-41296 Gothenburg (Sweden); Palmqvist, Anders, E-mail: anders.palmqvist@chalmers.se [Department of Chemistry and Chemical Engineering, Chalmers University of Technology, SE-41296 Gothenburg (Sweden)

2015-11-14

Thermoelectric (TE) generators that efficiently recycle a large portion of waste heat will be an important complementary energy technology in the future. While many efficient TE materials exist in the lower temperature region, few are efficient at high temperatures. Here, we present the high temperature properties of high-entropy alloys (HEAs), as a potential new class of high temperature TE materials. We show that their TE properties can be controlled significantly by changing the valence electron concentration (VEC) of the system with appropriate substitutional elements. Both the electrical and thermal transport properties in this system were found to decrease with a lower VEC number. Overall, the large microstructural complexity and lower average VEC in these types of alloys can potentially be used to lower both the total and the lattice thermal conductivity. These findings highlight the possibility to exploit HEAs as a new class of future high temperature TE materials.

The element analysis of high purity beryllium by method of laser mass-spectrometry

International Nuclear Information System (INIS)

Virich, V.D.; Kisel', O.V.; Kovtun, K.V.; Pugachev, N.S.; Yakobson, L.A.

2003-01-01

The operation is devoted to examination of a possibility of the analysis of element composition pure and high purity model of a beryllium is model by a method of laser mass spectrometry. The advantages of a method in a part of finding of a small amount of admixtures in comparison with other modes of the analysis are exhibited. The possibility of quantitative definition of a content in beryllium samples of gas-making admixtures-C,N,O surveyed

Perfomance of a high purity germanium multi-detector telescope for long range particles

International Nuclear Information System (INIS)

Riepe, G.; Protic, D.; Suekoesd, C.; Didelez, J.P.; Frascaria, N.; Gerlic, E.; Hourani, E.; Morlet, M.

1980-01-01

A telescope of stacked high purity germanium detectors designed for long range charged particles was tested using medium energy protons. Particle identification and the rejection of the low energy tail could be accomplished on-line allowing the measurement of complex spectra. The efficiency of the detector stack for protons was measured up to 156 MeV incoming energy. The various factors affecting the energy resolution are discussed and their estimated contributions are compared with the experimental results

High strength ferritic alloy

International Nuclear Information System (INIS)

1977-01-01

A high strength ferritic steel is specified in which the major alloying elements are chromium and molybdenum, with smaller quantities of niobium, vanadium, silicon, manganese and carbon. The maximum swelling is specified for various irradiation conditions. Rupture strength is also specified. (U.K.)

Microstructure and Mechanical Behavior of High-Entropy Alloys

Science.gov (United States)

Licavoli, Joseph J.; Gao, Michael C.; Sears, John S.; Jablonski, Paul D.; Hawk, Jeffrey A.

2015-10-01

High-entropy alloys (HEAs) have generated interest in recent years due to their unique positioning within the alloy world. By incorporating a number of elements in high proportion, usually of equal atomic percent, they have high configurational entropy, and thus, they hold the promise of interesting and useful properties such as enhanced strength and alloy stability. The present study investigates the mechanical behavior, fracture characteristics, and microstructure of two single-phase FCC HEAs CoCrFeNi and CoCrFeNiMn with some detailed attention given to melting, homogenization, and thermo-mechanical processing. Ingots approaching 8 kg in mass were made by vacuum induction melting to avoid the extrinsic factors inherent to small-scale laboratory button samples. A computationally based homogenization heat treatment was given to both alloys in order to eliminate any solidification segregation. The alloys were then fabricated in the usual way (forging, followed by hot rolling) with typical thermo-mechanical processing parameters employed. Transmission electron microscopy was subsequently used to assess the single-phase nature of the alloys prior to mechanical testing. Tensile specimens (ASTM E8) were prepared with tensile mechanical properties obtained from room temperature through 800 °C. Material from the gage section of selected tensile specimens was extracted to document room and elevated temperature deformation within the HEAs. Fracture surfaces were also examined to note fracture failure modes. The tensile behavior and selected tensile properties were compared with results in the literature for similar alloys.

Microstructural characterization of as-cast hf-b alloys

Directory of Open Access Journals (Sweden)

João Carlos Jânio Gigolotti

2012-04-01

Full Text Available An accurate knowledge of several metal-boron phase diagrams is important to evaluation of higher order systems such as metal-silicon-boron ternaries. The refinement and reassessment of phase diagram data is a continuous work, thus the reevaluation of metal-boron systems provides the possibility to confirm previous data from an investigation using higher purity materials and better analytical techniques. This work presents results of rigorous microstructural characterization of as-cast hafnium-boron alloys which are significant to assess the liquid composition associated to most of the invariant reactions of this system. Alloys were prepared by arc melting high purity hafnium (minimum 99.8% and boron (minimum 99.5% slices under argon atmosphere in water-cooled copper crucible with non consumable tungsten electrode and titanium getter. The phases were identified by scanning electron microscopy, using back-scattered electron image mode and X-ray diffraction. In general, a good agreement was found between our data and those from the currently accepted Hafnium-Boron phase diagram. The phases identified are αHfSS and B-RhomSS, the intermediate compounds HfB and HfB2 and the liquide L. The reactions are the eutectic L ⇔ αHfSS + HfB and L ⇔ HfB2 + B-Rhom, the peritectic L + HfB2 ⇔ HfB and the congruent formation of HfB2.

Effect of Nb on magnetic and mechanical properties of TbDyFe alloys

Science.gov (United States)

Wang, Naijuan; Liu, Yuan; Zhang, Huawei; Chen, Xiang; Li, Yanxiang

2018-03-01

The intrinsic brittleness in giant magnetostrictive material TbDyFe alloy has devastating influence on the machinability and properties of the alloy, thus affecting its applications. The purpose of this paper is to study the mechanical properties of the TbDyFe alloy by alloying with Nb element. The samples (Tb0.3Dy0.7)xFe2xNby (y = 0, 0.01, 0.04, 0.07, 0.1; 3x + y = 1) were melted in an arc melting furnace under high purity argon atmosphere. The microstructure, magnetostrictive properties and mechanical performance of the alloys were studied systematically. The results showed that NbFe2 phases were observed in the alloys with the addition of Nb. Moreover, both the NbFe2 phases and rare earth (RE)-rich phases were increased with the increasing of Nb element. The mechanical properties results revealed that the fracture toughness of the alloy with the addition of Nb enhanced 1.5-5 times of the Nb-free alloy. Both the NbFe2 phase and the RE-rich phase had the ability to prevent crack propagation, so that they can strengthen the REFe2 body. However, NbFe2 phase is a paramagnetic phase, which can reduce the magnetostrictive properties of the alloy by excessive precipitation.

Superconducting radio-frequency cavities made from medium and low-purity niobium ingots

Science.gov (United States)

Ciovati, Gianluigi; Dhakal, Pashupati; Myneni, Ganapati R.

2016-06-01

Superconducting radio-frequency cavities made of ingot niobium with residual resistivity ratio (RRR) greater than 250 have proven to have similar or better performance than fine-grain Nb cavities of the same purity, after standard processing. The high purity requirement contributes to the high cost of the material. As superconducting accelerators operating in continuous-wave typically require cavities to operate at moderate accelerating gradients, using lower purity material could be advantageous not only to reduce cost but also to achieve higher Q 0-values. In this contribution we present the results from cryogenic RF tests of 1.3-1.5 GHz single-cell cavities made of ingot Nb of medium (RRR = 100-150) and low (RRR = 60) purity from different suppliers. Cavities made of medium-purity ingots routinely achieved peak surface magnetic field values greater than 70 mT with an average Q 0-value of 2 × 1010 at 2 K after standard processing treatments. The performances of cavities made of low-purity ingots were affected by significant pitting of the surface after chemical etching.

Combining thermodynamic modeling and 3D printing of elemental powder blends for high-throughput investigation of high-entropy alloys – Towards rapid alloy screening and design

International Nuclear Information System (INIS)

Haase, Christian; Tang, Florian; Wilms, Markus B.; Weisheit, Andreas; Hallstedt, Bengt

2017-01-01

High-entropy alloys have gained high interest of both academia and industry in recent years due to their excellent properties and large variety of possible alloy systems. However, so far prediction of phase constitution and stability is based on empirical rules that can only be applied to selected alloy systems. In the current study, we introduce a methodology that enables high-throughput theoretical and experimental alloy screening and design. As a basis for thorough thermodynamic calculations, a new database was compiled for the Co–Cr–Fe–Mn–Ni system and used for Calphad and Scheil simulations. For bulk sample production, laser metal deposition (LMD) of an elemental powder blend was applied to build up the equiatomic CoCrFeMnNi Cantor alloy as a first demonstrator. This production approach allows high flexibility in varying the chemical composition and, thus, renders itself suitable for high-throughput alloy production. The microstructure, texture, and mechanical properties of the material processed were characterized using optical microscopy, EBSD, EDX, XRD, hardness and compression testing. The LMD-produced alloy revealed full density, strongly reduced segregation compared to conventionally cast material, pronounced texture, and excellent mechanical properties. Phase constitution and elemental distribution were correctly predicted by simulations. The applicability of the introduced methodology to high-entropy alloys and extension to compositionally complex alloys is discussed.

Combining thermodynamic modeling and 3D printing of elemental powder blends for high-throughput investigation of high-entropy alloys – Towards rapid alloy screening and design

Energy Technology Data Exchange (ETDEWEB)

Haase, Christian, E-mail: christian.haase@iehk.rwth-aachen.de [Department of Ferrous Metallurgy, RWTH Aachen University, 52072 Aachen (Germany); Tang, Florian [Institute for Materials Applications in Mechanical Engineering, RWTH Aachen University, 52062 Aachen (Germany); Wilms, Markus B.; Weisheit, Andreas [Fraunhofer Institute for Laser Technology ILT, 52074 Aachen (Germany); Hallstedt, Bengt [Institute for Materials Applications in Mechanical Engineering, RWTH Aachen University, 52062 Aachen (Germany)

2017-03-14

High-entropy alloys have gained high interest of both academia and industry in recent years due to their excellent properties and large variety of possible alloy systems. However, so far prediction of phase constitution and stability is based on empirical rules that can only be applied to selected alloy systems. In the current study, we introduce a methodology that enables high-throughput theoretical and experimental alloy screening and design. As a basis for thorough thermodynamic calculations, a new database was compiled for the Co–Cr–Fe–Mn–Ni system and used for Calphad and Scheil simulations. For bulk sample production, laser metal deposition (LMD) of an elemental powder blend was applied to build up the equiatomic CoCrFeMnNi Cantor alloy as a first demonstrator. This production approach allows high flexibility in varying the chemical composition and, thus, renders itself suitable for high-throughput alloy production. The microstructure, texture, and mechanical properties of the material processed were characterized using optical microscopy, EBSD, EDX, XRD, hardness and compression testing. The LMD-produced alloy revealed full density, strongly reduced segregation compared to conventionally cast material, pronounced texture, and excellent mechanical properties. Phase constitution and elemental distribution were correctly predicted by simulations. The applicability of the introduced methodology to high-entropy alloys and extension to compositionally complex alloys is discussed.

Dynamical recrystallization of high purity austenitic stainless steels; Recristallisation dynamique d'aciers inoxydables austenitiques de haute purete

Energy Technology Data Exchange (ETDEWEB)

Gavard, L

2001-01-01

The aim of this work is to optimize the performance of structural materials. The elementary mechanisms (strain hardening and dynamical regeneration, germination and growth of new grains) occurring during the hot working of metals and low pile defect energy alloys have been studied for austenitic stainless steels. In particular, the influence of the main experimental parameters (temperature, deformation velocity, initial grain size, impurities amount, deformation way) on the process of discontinuous dynamical recrystallization has been studied. Alloys with composition equal to those of the industrial stainless steel-304L have been fabricated from ultra-pure iron, chromium and nickel. Tests carried out in hot compression and torsion in order to cover a wide range of deformations, deformation velocities and temperatures for two very different deformation ways have allowed to determine the rheological characteristics (sensitivity to the deformation velocity, apparent activation energy) of materials as well as to characterize their microstructural deformations by optical metallography and electron back-scattered diffraction. The influence of the initial grain size and the influence of the purity of the material on the dynamical recrystallization kinetics have been determined. An analytical model for the determination of the apparent mobility of grain boundaries, a semi-analytical model for the dynamical recrystallization and at last an analytical model for the stationary state of dynamical recrystallization are proposed as well as a new criteria for the transition between the refinement state and the state of grain growth. (O.M.)

TiAu based shape memory alloys for high temperature applications

International Nuclear Information System (INIS)

Wadood, Abdul; Yamabe-Mitarai, Yoko; Hosoda, Hideki

2014-01-01

TiAu (equiatomic) exhibits phase transformaion from B2 (ordered bcc) to thermo-elastic orthorhombic B19 martensite at about 875K and thus TiAu is categorized as high temperature shape memory alloy. In this study, recent research and developments related to TiAu based high temperature shape memory alloys will be discussed in the Introduction part. Then some results of our research group related to strengthening of TiAu based high temperature shape memory alloys will be presented. Potential of TiAu based shape memory alloys for high temperature shape memory materials applications will also be discussed

Radiochemical neutron activation analysis of zirconium and zirconium-niobium alloys

International Nuclear Information System (INIS)

Tashimova, F.A.; Sadikov, I.I.; Salimov, M.

2004-01-01

Full text: Zirconium and zirconium-niobium alloys are used on nuclear technology, as fuel cladding of nuclear reactors. Their nuclear-physical, mechanical and thermophysical properties are influenced them matrix and impurity composition, therefore determination of matrix and impurity content of these materials is a very important task. Neutron activation analysis is one from multielemental and high sensible techniques that are widely applied in analysis of high purity materials. Investigation of nuclear-physical characteristics of zirconium has shown that instrumental variant NAA is unusable for analysis due to high radioactivity of a matrix. Therefore it is necessary carrying out radiochemical separation of impurity radionuclides from matrix. Study of the literature datum have shown, that zirconium and niobium are very well extracted from muriatic solution with 5% tributyl phosphineoxide (TBPO) solution in toluene and 0,75 M solution of di-2-ethyl hexyl phosphoric acid (HDEHP) in cyclohexanone. Investigation of these elements extraction in these systems has shown that more effective and selective separation of matrix radionuclides is achieved in HDEHP-3M HCI system. This system is also extracted and hafnium, witch is an accompanying element of zirconium and its high content prevented determination of other impurity elements in sample. Therefore we used extraction system HDEHP-3M HCl for analysis of zirconium and zirconium-niobium alloys in chromatographic variant. By measurement of distribution profile of a matrix and of elution curve of determined elements is established, that for effective separation of impurity and matrix radionuclides there is enough chromatographic column with diameter 1 cm and height of a sorbent layer 7 cm, thus volume of elute, necessary for complete elution of determinate elements is 35-40 ml. On the basis of the carried out researches the technique of radiochemical NAA of high purity zirconium and zirconium-niobium alloy, which allows to

Supercritical water corrosion of high Cr steels and Ni-base alloys

International Nuclear Information System (INIS)

Jang, Jin Sung; Han, Chang Hee; Hwang, Seong Sik

2004-01-01

High Cr steels (9 to 12% Cr) have been widely used for high temperature high pressure components in fossil power plants. Recently the concept of SCWR (supercritical water-cooled reactor) has aroused a keen interest as one of the next generation (Generation IV) reactors. Consequently Ni-base (or high Ni) alloys as well as high Cr steels that have already many experiences in the field are among the potential candidate alloys for the cladding or reactor internals. Tentative inlet and outlet temperatures of the anticipated SCWR are 280 and 510 .deg. C respectively. Among many candidate alloys there are austenitic stainless steels, Ni base alloys, ODS alloys as well as high Cr steels. In this study the corrosion behavior of the high Cr steels and Ni base (or high Ni) alloys in the supercritical water were investigated. The corrosion behavior of the unirradiated base metals could be used in the near future as a guideline for the out-of-pile or in-pile corrosion evaluation tests

A Study of Magnesium-Base Metallic Systems and Development of Principles for Creation of Corrosion-Resistant Magnesium Alloys

Science.gov (United States)

Mukhina, I. Yu.

2014-11-01

The effect of 26 alloying elements on the corrosion resistance of high-purity magnesium in a 0.5-n solution of sodium chloride and in a humid atmosphere (0.005 n) is studied. The Mg - Li, Mg - Ag, Mg - Zn, Mg - Cu, Mg - Gd, Mg - Al, Mg - Zr, Mg - Mn and other binary systems, which present interest as a base for commercial or perspective castable magnesium alloys, are studied. The characteristics of corrosion resistance of the binary alloys are analyzed in accordance with the group and period of the Mendeleev's periodic law. The roles of the electrochemical and volume factors and of the factor of the valence of the dissolved element are determined.

Nanocrystalline Ni-Co Alloy Synthesis by High Speed Electrodeposition

Directory of Open Access Journals (Sweden)

Jamaliah Idris

2013-01-01

Full Text Available Electrodeposition of nanocrystals is economically and technologically viable production path for the synthesis of pure metals and alloys both in coatings and bulk form. The study presents nanocrystalline Ni-Co alloy synthesis by high speed electrodeposition. Nanocrystalline Ni-Co alloys coatings were prepared by direct current (DC and deposited directly on steel and aluminum substrates without any pretreatment, using high speed electrodeposition method. The influence of the electrolysis parameters, such as cathodic current density and temperature at constant pH, on electrodeposition and microstructure of Ni-Co alloys were examined. A homogeneous surface morphology was obtained at all current densities of the plated samples, and it was evident that the current density and temperature affect the coating thickness of Ni-Co alloy coatings.

Nanocrystalline Ni-Co Alloy Synthesis by High Speed Electrodeposition

OpenAIRE

Idris, Jamaliah; Christian, Chukwuekezie; Gaius, Eyu

2013-01-01

Electrodeposition of nanocrystals is economically and technologically viable production path for the synthesis of pure metals and alloys both in coatings and bulk form. The study presents nanocrystalline Ni-Co alloy synthesis by high speed electrodeposition. Nanocrystalline Ni-Co alloys coatings were prepared by direct current (DC) and deposited directly on steel and aluminum substrates without any pretreatment, using high speed electrodeposition method. The influence of the electrolysis par...

The determination of boron in aluminium of high purity

International Nuclear Information System (INIS)

Cook, E.B.T.; Holan, H.

1977-01-01

A description is given of the investigations that led to the development of chemical methods for the determination of boron within the range 0,25 to 1,0 p.p.m. in aluminium of high purity. Methods were developed that incorporated fluorimetry, directly in solutions containing aluminium and after separation of boron by liquid-liquid extraction into 2-ethyl-1,3 hexanediol. A published spectrophotometric method, involving extraction of the BF 4 sup(-) complex with methylene blue into dichloroethane, was modified for application to alluminium samples. Details of this modified procedure and the fluorimetric-extraction procedure are appended. The precision of the methylene-blue method is about 6 percent relative and is recommended for precision and speed in preference to others. Separation of boron by distillation and spectrophotometric determination with curcumin gave low values in comparison with those obtained by the other methods. Agreement between the boron values obtained on the samples tested was good for the fluorimetric and methylene-blue spectrophotometric methods

Synthesis and characterization of straight and stacked-sheet AlN nanowires with high purity

International Nuclear Information System (INIS)

Lei, M.; Yang, H.; Li, P.G.; Tang, W.H.

2008-01-01

Large-scale AlN nanowires with hexagonal crystal structure were synthesized by the direct nitridation method at high temperatures. The experimental results indicate that these single-crystalline AlN nanowires have high purity and consist of straight and stacked-sheet nanowires. It is found that straight AlN nanowire grows along [1, 1, -2, 0] direction, whereas the stacked-sheet nanowire with hexagonal cross section is along [0 0 0 1] direction. It is thought that vapor-solid (VS) mechanism should be responsible for the growth of AlN nanowires

High-alloy steels and nickel alloys for construction of industrial plants. Pt. 2

International Nuclear Information System (INIS)

2007-01-01

Vol. 2 of the 8. Dresden Corrosion Protection Seminar comprises eight papers, most of which are in the form of PowerPoint presentations: High-temperature materials and their applications in chemical engineering (J. Kloever); Alloy 602 CA in metal dusting conditions; Material requirements in future power plants (H. Schneider); Status report on material qualification for the 700 C technology in coal power plants (R. Mohrmann); Materials for nuclear fusion (M. Paju); The degradation mechanism relaxation cracking as exemplified by the alloys 800 H and 617 (H.C. van Wortel); Specific requirements on the design of a pressurised manifold of Alloy 800 H in refineries, a case study (I. Rommerskirchen et al.); Materials for electro-surfacing for corrosion protection in conditions of high-temperature corrosion (M.Spiegel) [de

Novel pre-alloyed powder processing of modified alnico 8: Correlation of microstructure and magnetic properties

Energy Technology Data Exchange (ETDEWEB)

Anderson, I. E., E-mail: andersoni@ameslab.gov; Kassen, A. G.; White, E. M. H.; Zhou, L.; Tang, W.; Palasyuk, A.; Dennis, K. W.; McCallum, R. W.; Kramer, M. J. [Ames Laboratory (USDOE), Iowa State University, Ames, Iowa 50011 (United States)

2015-05-07

Progress is reviewed on development of an improved near-final bulk magnet fabrication process for alnico 8, as a non-rare earth permanent magnet with promise for sufficient energy density and coercivity for electric drive motors. This study showed that alnico bulk magnets in near-final shape can be made by simple compression molding from spherical high purity gas atomized pre-alloyed powder. Dwell time at peak sintering temperature (1250 °C) greatly affected grain size of the resulting magnet alloys. This microstructure transformation was demonstrated to be useful for gaining partially aligned magnetic properties and boosting energy product. While a route to increased coercivity was not identified by these experiments, manufacturability of bulk alnico magnet alloys in near-final shapes was demonstrated, permitting further processing and alloy modification experiments that can target higher coercivity and better control of grain anisotropy during grain growth.

Fundamental corrosion characterization of high-strength titanium alloys

International Nuclear Information System (INIS)

Schutz, R.W.; Grauman, J.S.

1984-01-01

Many commercially available and several developmental high-strength titanium alloys were evaluated for application in chloride-containing environments with respect to general, crevice, and stress corrosion resistance. Studies in boiling reducing and oxidizing acid chloride media permitted identification of certain high-strength titanium alloys, containing ≥4 weight % molybdenum, which are significantly more resistant than unalloyed titanium with respect to general and crevice attack. Data regression analysis suggests that molybdenum and vanadium impart a significant positive effect on alloy corrosion resistance under reducing acid chloride conditions, whereas aluminum is detrimental. Little effect of metallurgical condition (that is, annealed versus aged) on corrosion behavior of the higher molybdenum-containing alloys was noted. No obvious susceptibility to chloride and sulfide stress corrosion cracking (SCC) was detected utilizing U-bend specimens at 177 0 C

Mesophase Formation Stabilizes High-purity Magic-sized Clusters

KAUST Repository

Nevers, Douglas R.; Williamson, Curtis B.; Savitzky, Benjamin H; Hadar, Ido; Banin, Uri; Kourkoutis, Lena F.; Hanrath, Tobias; Robinson, Richard D.

2018-01-01

Magic-sized clusters (MSCs) are renowned for their identical size and closed-shell stability that inhibit conventional nanoparticle (NP) growth processes. Though MSCs have been of increasing interest, understanding the reaction pathways toward their nucleation and stabilization is an outstanding issue. In this work, we demonstrate that high concentration synthesis (1000 mM) promotes a well-defined reaction pathway to form high-purity MSCs (>99.9%). The MSCs are resistant to typical growth and dissolution processes. Based on insights from in-situ X-ray scattering analysis, we attribute this stability to the accompanying production of a large, hexagonal organic-inorganic mesophase (>100 nm grain size) that arrests growth of the MSCs and prevents NP growth. At intermediate concentrations (500 mM), the MSC mesophase forms, but is unstable, resulting in NP growth at the expense of the assemblies. These results provide an alternate explanation for the high stability of MSCs. Whereas the conventional mantra has been that the stability of MSCs derives from the precise arrangement of the inorganic structures (i.e., closed-shell atomic packing), we demonstrate that anisotropic clusters can also be stabilized by self-forming fibrous mesophase assemblies. At lower concentration (<200 mM or >16 acid-to-metal), MSCs are further destabilized and NPs formation dominates that of MSCs. Overall, the high concentration approach intensifies and showcases inherent concentration-dependent surfactant phase behavior that is not accessible in conventional (i.e., dilute) conditions. This work provides not only a robust method to synthesize, stabilize, and study identical MSC products, but also uncovers an underappreciated stabilizing interaction between surfactants and clusters.

Mesophase Formation Stabilizes High-purity Magic-sized Clusters

KAUST Repository

Nevers, Douglas R.

2018-01-27

Magic-sized clusters (MSCs) are renowned for their identical size and closed-shell stability that inhibit conventional nanoparticle (NP) growth processes. Though MSCs have been of increasing interest, understanding the reaction pathways toward their nucleation and stabilization is an outstanding issue. In this work, we demonstrate that high concentration synthesis (1000 mM) promotes a well-defined reaction pathway to form high-purity MSCs (>99.9%). The MSCs are resistant to typical growth and dissolution processes. Based on insights from in-situ X-ray scattering analysis, we attribute this stability to the accompanying production of a large, hexagonal organic-inorganic mesophase (>100 nm grain size) that arrests growth of the MSCs and prevents NP growth. At intermediate concentrations (500 mM), the MSC mesophase forms, but is unstable, resulting in NP growth at the expense of the assemblies. These results provide an alternate explanation for the high stability of MSCs. Whereas the conventional mantra has been that the stability of MSCs derives from the precise arrangement of the inorganic structures (i.e., closed-shell atomic packing), we demonstrate that anisotropic clusters can also be stabilized by self-forming fibrous mesophase assemblies. At lower concentration (<200 mM or >16 acid-to-metal), MSCs are further destabilized and NPs formation dominates that of MSCs. Overall, the high concentration approach intensifies and showcases inherent concentration-dependent surfactant phase behavior that is not accessible in conventional (i.e., dilute) conditions. This work provides not only a robust method to synthesize, stabilize, and study identical MSC products, but also uncovers an underappreciated stabilizing interaction between surfactants and clusters.

Superconducting radio-frequency cavities made from medium and low-purity niobium ingots

International Nuclear Information System (INIS)

Ciovati, Gianluigi; Dhakal, Pashupati; Myneni, Ganapati R

2016-01-01

Superconducting radio-frequency cavities made of ingot niobium with residual resistivity ratio (RRR) greater than 250 have proven to have similar or better performance than fine-grain Nb cavities of the same purity, after standard processing. The high purity requirement contributes to the high cost of the material. As superconducting accelerators operating in continuous-wave typically require cavities to operate at moderate accelerating gradients, using lower purity material could be advantageous not only to reduce cost but also to achieve higher Q 0 -values. In this contribution we present the results from cryogenic RF tests of 1.3–1.5 GHz single-cell cavities made of ingot Nb of medium (RRR = 100–150) and low (RRR = 60) purity from different suppliers. Cavities made of medium-purity ingots routinely achieved peak surface magnetic field values greater than 70 mT with an average Q 0 -value of 2 × 10 10 at 2 K after standard processing treatments. The performances of cavities made of low-purity ingots were affected by significant pitting of the surface after chemical etching. (paper)

Tuning for optimal performance in angle control, uniformity, and energy purity

International Nuclear Information System (INIS)

Liebert, Reuel B.; Olson, Joseph C.; Arevalo, Edwin A.; Downey, Daniel F.

2005-01-01

Advances in reducing the sizes of device structures and line widths place increasing demands on the accuracy of dopant placement and the control of dopant motion during activation anneals. Serial process high current ion implantation systems seek to produce beams in which the angles are controlled to high precision avoiding the angles introduced by conical structures used for holding wafers on spinning discs in batch systems. However, ion optical corrections and control of incident beam angle, dose uniformity, high throughput and energy purity often present apparently contradictory requirements in machine design. Data is presented to illustrate that tuning procedures can be used to simultaneously optimize angle purity in both x and y planes as well as control energy purity and dose uniformity

Effect of Aluminum Purity on the Pore Formation of Porous Anodic Alumina

International Nuclear Information System (INIS)

Kim, Byeol; Lee, Jin Seok

2014-01-01

Anodic alumina oxide (AAO), a self-ordered hexagonal array, has various applications in nanofabrication such as the fabrication of nanotemplates and other nanostructures. In order to obtain highly ordered porous alumina membranes, a two-step anodization or prepatterning of aluminum are mainly conducted with straight electric field. Electric field is the main driving force for pore growth during anodization. However, impurities in aluminum can disturb the direction of the electric field. To confirm this, we anodized two different aluminum foil samples with high purity (99.999%) and relatively low purity (99.8%), and compared the differences in the surface morphologies of the respective aluminum oxide membranes produced in different electric fields. Branched pores observed in porous alumina surface which was anodized in low-purity aluminum and the size; dimensions of the pores were found to be usually smaller than those obtained from high-purity aluminum. Moreover, anodization at high voltage proceeds to a significant level of conversion because of the high speed of the directional electric field. Consequently, anodic alumina membrane of a specific morphology, i. e., meshed pore, was produced

Effect of Aluminum Purity on the Pore Formation of Porous Anodic Alumina

Energy Technology Data Exchange (ETDEWEB)

Kim, Byeol; Lee, Jin Seok [Sookmyung Women' s Univ., Seoul (Korea, Republic of)

2014-02-15

Anodic alumina oxide (AAO), a self-ordered hexagonal array, has various applications in nanofabrication such as the fabrication of nanotemplates and other nanostructures. In order to obtain highly ordered porous alumina membranes, a two-step anodization or prepatterning of aluminum are mainly conducted with straight electric field. Electric field is the main driving force for pore growth during anodization. However, impurities in aluminum can disturb the direction of the electric field. To confirm this, we anodized two different aluminum foil samples with high purity (99.999%) and relatively low purity (99.8%), and compared the differences in the surface morphologies of the respective aluminum oxide membranes produced in different electric fields. Branched pores observed in porous alumina surface which was anodized in low-purity aluminum and the size; dimensions of the pores were found to be usually smaller than those obtained from high-purity aluminum. Moreover, anodization at high voltage proceeds to a significant level of conversion because of the high speed of the directional electric field. Consequently, anodic alumina membrane of a specific morphology, i. e., meshed pore, was produced.

High Purity Hydrogen Production with In-Situ Carbon Dioxide and Sulfur Capture in a Single Stage Reactor

Energy Technology Data Exchange (ETDEWEB)

Nihar Phalak; Shwetha Ramkumar; Daniel Connell; Zhenchao Sun; Fu-Chen Yu; Niranjani Deshpande; Robert Statnick; Liang-Shih Fan

2011-07-31

Enhancement in the production of high purity hydrogen (H{sub 2}) from fuel gas, obtained from coal gasification, is limited by thermodynamics of the water gas shift (WGS) reaction. However, this constraint can be overcome by conducting the WGS in the presence of a CO{sub 2}-acceptor. The continuous removal of CO{sub 2} from the reaction mixture helps to drive the equilibrium-limited WGS reaction forward. Since calcium oxide (CaO) exhibits high CO{sub 2} capture capacity as compared to other sorbents, it is an ideal candidate for such a technique. The Calcium Looping Process (CLP) developed at The Ohio State University (OSU) utilizes the above concept to enable high purity H{sub 2} production from synthesis gas (syngas) derived from coal gasification. The CLP integrates the WGS reaction with insitu CO{sub 2}, sulfur and halide removal at high temperatures while eliminating the need for a WGS catalyst, thus reducing the overall footprint of the hydrogen production process. The CLP comprises three reactors - the carbonator, where the thermodynamic constraint of the WGS reaction is overcome by the constant removal of CO{sub 2} product and high purity H{sub 2} is produced with contaminant removal; the calciner, where the calcium sorbent is regenerated and a sequestration-ready CO{sub 2} stream is produced; and the hydrator, where the calcined sorbent is reactivated to improve its recyclability. As a part of this project, the CLP was extensively investigated by performing experiments at lab-, bench- and subpilot-scale setups. A comprehensive techno-economic analysis was also conducted to determine the feasibility of the CLP at commercial scale. This report provides a detailed account of all the results obtained during the project period.

Microcapillary Features in Silicon Alloyed High-Strength Cast Iron

Directory of Open Access Journals (Sweden)

R.K. Hasanli

2017-04-01

Full Text Available Present study explores features of silicon micro capillary in alloyed high-strength cast iron with nodular graphite (ductile iron produced in metal molds. It identified the nature and mechanism of micro liquation of silicon in a ductile iron alloyed with Nickel and copper, and demonstrated significant change of structural-quality characteristics. It was concluded that the matrix of alloyed ductile iron has a heterogeneous structure with cross reinforcement and high-silicon excrement areas.

Automation of the Characterization of High Purity Germanium Detectors

Science.gov (United States)

Dugger, Charles ``Chip''

2014-09-01

Neutrinoless double beta decay is a rare hypothesized process that may yield valuable insight into the fundamental properties of the neutrino. Currently there are several experiments trying to observe this process, including the Majorana DEMONSTRAOR experiment, which uses high purity germanium (HPGe) detectors to generate and search for these events. Because the event happens internally, it is essential to have the lowest background possible. This is done through passive detector shielding, as well as event discrimination techniques that distinguish between multi-site events characteristic of gamma-radiation, and single-site events characteristic of neutrinoless double beta decay. Before fielding such an experiment, the radiation response of the detectors must be characterized. A robotic arm is being tested for future calibration of HPGe detectors. The arm will hold a source at locations relative to the crystal while data is acquired. Several radioactive sources of varying energy levels will be used to determine the characteristics of the crystal. In this poster, I will present our work with the robot, as well as the characterization of data we took with an underground HPGe detector at the WIPP facility in Carlsbad, NM (2013). Neutrinoless double beta decay is a rare hypothesized process that may yield valuable insight into the fundamental properties of the neutrino. Currently there are several experiments trying to observe this process, including the Majorana DEMONSTRAOR experiment, which uses high purity germanium (HPGe) detectors to generate and search for these events. Because the event happens internally, it is essential to have the lowest background possible. This is done through passive detector shielding, as well as event discrimination techniques that distinguish between multi-site events characteristic of gamma-radiation, and single-site events characteristic of neutrinoless double beta decay. Before fielding such an experiment, the radiation response of

Recovery of high purity proteins from polyacrylamide gels using ultraviolet scanning densitometry

International Nuclear Information System (INIS)

Bartolini, P.; Arkaten, R.; Ribela, M.T.C.P.

1988-07-01

We present here a technique for the purification of proteins carried out by a quantitative analytical method used in conjunction with a preparative gel electrophoresis. Both methods employ densitometric ultraviolet scanning of unstained protein bands, a procedure wich is particulary suitable for the purification and recovery of biologically active polypeptides. In short, the purified extracted protein, isolated in a segment cut out from a preparative gel, is recovered by a second (reversed) electrophoresis. We performed the extractions and recoveries of different amounts of two standard proteins (BSA and STI) and a polypeptide hormone (hGH). Our main interest, especially for the hormone is the complete protein recovery with retention of bio and immunoactivity and high purity. For the proteins tested, the mean recovery was of 93 + - 5% obtaining a mean purity of 95 + - 7%. We conclude that the proposed method should have interesting applications, particularly in the obtention of very pure hormones, as are needed for radioligand assays, for radiolabelling and specific antibody raising. We emphasize the simplicity and rapidity of the method (the entire preparative process: first electrophoresis, UV scanning and reversed electrophoresis can be performed in approximately six hours) and its efficiency in recovering pure proteins even on a milligram scale. We thank the support from the IAEA (4299/RB) and FINEP (43.86.0351.00) and CENE (Brazil). (author) [pt

Corrosion-Resistant High-Entropy Alloys: A Review

Directory of Open Access Journals (Sweden)

Yunzhu Shi

2017-02-01

Full Text Available Corrosion destroys more than three percent of the world’s gross domestic product. Therefore, the design of highly corrosion-resistant materials is urgently needed. By breaking the classical alloy-design philosophy, high-entropy alloys (HEAs possess unique microstructures, which are solid solutions with random arrangements of multiple elements. The particular locally-disordered chemical environment is expected to lead to unique corrosion-resistant properties. In this review, the studies of the corrosion-resistant HEAs during the last decade are summarized. The corrosion-resistant properties of HEAs in various aqueous environments and the corrosion behavior of HEA coatings are presented. The effects of environments, alloying elements, and processing methods on the corrosion resistance are analyzed in detail. Furthermore, the possible directions of future work regarding the corrosion behavior of HEAs are suggested.

Microstructure and corrosion of Pd-modified Ti alloys produced by powder metallurgy

International Nuclear Information System (INIS)

Ashworth, M.A.; Davenport, A.J.; Ward, R.M.; Hamilton, H.G.C.

2010-01-01

A method for the fabrication of titanium alloy parts with enhanced corrosion resistance by a powder metallurgy route is presented in this paper. Commercial purity titanium powders modified with Pd have been hot isostatically pressed (HIPped) and the microstructure and distribution of the noble metal characterised by optical and scanning electron microscopy. The electrochemistry of the HIPped alloy has been assessed and the effect of powder size fraction evaluated. Results show that the phase composition and electrochemistry of the HIPped Pd-modified alloy is equivalent to that of wrought grade 7 Ti.

Spall behaviors of high purity copper under sweeping detonation

Energy Technology Data Exchange (ETDEWEB)

Yang, Yang, E-mail: yangyanggroup@163.com [School of Material Science and Engineering, Central South University, Changsha 410083 (China); Institute of Fluid Physics, China Academy of Engineering Physics, Mianyang 621900 (China); National Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing 100081 (China); Key Laboratory of Nonferrous Metals Material Science and Engineering of Ministry of Education, Central South University, Changsha 410083 (China); Zhi-qiang, Peng; Xing-zhi, Chen [School of Material Science and Engineering, Central South University, Changsha 410083 (China); Key Laboratory of Nonferrous Metals Material Science and Engineering of Ministry of Education, Central South University, Changsha 410083 (China); Zhao-liang, Guo; Tie-gang, Tang; Hai-bo, Hu [Institute of Fluid Physics, China Academy of Engineering Physics, Mianyang 621900 (China); Qing-ming, Zhang [National Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing 100081 (China)

2016-01-10

Suites of sweeping detonation experiments were conducted to assess the spall behavior of high purity copper samples with different heat treatment histories. Incipient spall samples were obtained at different sweeping detonation condition. Metallographic and Electron Backscattered Diffraction (EBSD) analyses were performed on the soft-recovered samples. The effects of grain boundaries, grain size, crystal orientation and loading direction on the spall behaviors were discussed. Spall plane branching was found in the main spall plane of the damage samples. For similar microstructure, the area of voids increase with the increase of shock stress, and the coalescence of voids also become more obvious. Results from EBSD analysis show that the grain sizes were decreased and the grains were elongated along the direction of the plate width. Triple junctions composed of two or more general high angle boundaries are the preferred locations for intergranular damage. Voids prefer to nucleate in the grain boundaries composed of grain with high Taylor Factor (TF) than other grains. The damage areas in the grains with high TF are more severe. Boundaries close to perpendicular to the loading direction are more susceptible to void nucleation than the boundaries close to parallel to the loading direction, but the difference of voids nucleated in these two boundaries is less significant than the results obtained by plate impact experiment. It would be caused by the obliquity between the shock loading direction and the plate normal.

Research for magnetocaloric effect of Gd{sub 1-x}Dy{sub x} alloy

Energy Technology Data Exchange (ETDEWEB)

Hou, Xueling; Shitao, Li; An, Zhang; Hui, Xu; Ni, Jiansen; Zhou, Bangxin [Institute of Materials, Shanghai University, Shanghai 20007 (China)

2007-12-15

The magnetocaloric effect (MEC) in Gd{sub 1-x}Dy{sub x} (x=0.13,0.20,0.27,0.34,0.40) alloys is investigated using commercial elements with purity of up to 99.80% for Gd and Dy. These alloys are prepared by arc melting in stoichiometric proportions on a water-cooled copper crucible under high pure argon atmosphere. As a result, when x was changed from 0 to 40at%, the adiabatic temperature change ({delta}T) increases from 1.6 K to 3.1 K, the Curie temperature decreased from 288 K to 245.5 K. Gd{sub 73}Dy{sub 27} exhibits the largest {delta}T{sub max} value of 3.1 K at the T{sub C} value of 260 K among the alloys investigated up to 1.2 T (tesla) applied field, it is almost same as the {delta}T of high pure unitary Gd (99.99%) and is clearly superior to commercial unitary Gd (99.80%). The T{sub C} of Gd{sub 73}Dy{sub 27} alloy is minor to high pure unitary Gd (99.99%) and commercially unitary Gd (99.80%). But this alloy prepared by commercial elements with low cost has better MEC to be a promising candidate for magnetic working substances for room temperature magnetic refrigeration. (copyright 2008 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Release of Si from Silicon, a Ferrosilicon (FeSi) Alloy and a Synthetic Silicate Mineral in Simulated Biological Media

Science.gov (United States)

Herting, Gunilla; Jiang, Tao; Sjöstedt, Carin; Odnevall Wallinder, Inger

2014-01-01

Unique quantitative bioaccessibility data has been generated, and the influence of surface/material and test media characteristics on the elemental release process were assessed for silicon containing materials in specific synthetic body fluids at certain time periods at a fixed loading. The metal release test protocol, elaborated by the KTH team, has previously been used for classification, ranking, and screening of different alloys and metals. Time resolved elemental release of Si, Fe and Al from particles, sized less than 50 µm, of two grades of metallurgical silicon (high purity silicon, SiHG, low purity silicon, SiLG), an alloy (ferrosilicon, FeSi) and a mineral (aluminium silicate, AlSi) has been investigated in synthetic body fluids of varying pH, composition and complexation capacity, simple models of for example dermal contact and digestion scenarios. Individual methods for analysis of released Si (as silicic acid, Si(OH)4) in synthetic body fluids using GF-AAS were developed for each fluid including optimisation of solution pH and graphite furnace parameters. The release of Si from the two metallurgical silicon grades was strongly dependent on both pH and media composition with the highest release in pH neutral media. No similar effect was observed for the FeSi alloy or the aluminium silicate mineral. Surface adsorption of phosphate and lactic acid were believed to hinder the release of Si whereas the presence of citric acid enhanced the release as a result of surface complexation. An increased presence of Al and Fe in the material (low purity metalloid, alloy or mineral) resulted in a reduced release of Si in pH neutral media. The release of Si was enhanced for all materials with Al at their outermost surface in acetic media. PMID:25225879

Release of Si from silicon, a ferrosilicon (FeSi alloy and a synthetic silicate mineral in simulated biological media.

Directory of Open Access Journals (Sweden)

Gunilla Herting

Full Text Available Unique quantitative bioaccessibility data has been generated, and the influence of surface/material and test media characteristics on the elemental release process were assessed for silicon containing materials in specific synthetic body fluids at certain time periods at a fixed loading. The metal release test protocol, elaborated by the KTH team, has previously been used for classification, ranking, and screening of different alloys and metals. Time resolved elemental release of Si, Fe and Al from particles, sized less than 50 µm, of two grades of metallurgical silicon (high purity silicon, SiHG, low purity silicon, SiLG, an alloy (ferrosilicon, FeSi and a mineral (aluminium silicate, AlSi has been investigated in synthetic body fluids of varying pH, composition and complexation capacity, simple models of for example dermal contact and digestion scenarios. Individual methods for analysis of released Si (as silicic acid, Si(OH4 in synthetic body fluids using GF-AAS were developed for each fluid including optimisation of solution pH and graphite furnace parameters. The release of Si from the two metallurgical silicon grades was strongly dependent on both pH and media composition with the highest release in pH neutral media. No similar effect was observed for the FeSi alloy or the aluminium silicate mineral. Surface adsorption of phosphate and lactic acid were believed to hinder the release of Si whereas the presence of citric acid enhanced the release as a result of surface complexation. An increased presence of Al and Fe in the material (low purity metalloid, alloy or mineral resulted in a reduced release of Si in pH neutral media. The release of Si was enhanced for all materials with Al at their outermost surface in acetic media.

A simple dissolved metals mixing method to produce high-purity MgTiO3 nanocrystals

International Nuclear Information System (INIS)

Pratapa, Suminar; Baqiya, Malik A.; Istianah,; Lestari, Rina; Angela, Riyan

2014-01-01

A simple dissolved metals mixing method has been effectively used to produce high-purity MgTiO 3 (MT) nanocrystals. The method involves the mixing of independently dissolved magnesium and titanium metal powders in hydrochloric acid followed by calcination. The phase purity and nanocrystallinity were determined by making use of laboratory x-ray diffraction data, to which Rietveld-based analyses were performed. Results showed that the method yielded only one type magnesium titanate powders, i.e. MgTiO 3 , with no Mg 2 TiO 4 or MgTi 2 O 5 phases. The presence of residual rutile or periclase was controlled by adding excessive Mg up to 5% (mol) in the stoichiometric mixing. The method also resulted in MT nanocrystals with estimated average crystallite size of 76±2 nm after calcination at 600°C and 150±4 nm (at 800°C). A transmission electron micrograph confirmed the formation of the nanocrystallites

High-throughput computational search for strengthening precipitates in alloys

International Nuclear Information System (INIS)

Kirklin, S.; Saal, James E.; Hegde, Vinay I.; Wolverton, C.

2016-01-01

The search for high-strength alloys and precipitation hardened systems has largely been accomplished through Edisonian trial and error experimentation. Here, we present a novel strategy using high-throughput computational approaches to search for promising precipitate/alloy systems. We perform density functional theory (DFT) calculations of an extremely large space of ∼200,000 potential compounds in search of effective strengthening precipitates for a variety of different alloy matrices, e.g., Fe, Al, Mg, Ni, Co, and Ti. Our search strategy involves screening phases that are likely to produce coherent precipitates (based on small lattice mismatch) and are composed of relatively common alloying elements. When combined with the Open Quantum Materials Database (OQMD), we can computationally screen for precipitates that either have a stable two-phase equilibrium with the host matrix, or are likely to precipitate as metastable phases. Our search produces (for the structure types considered) nearly all currently known high-strength precipitates in a variety of fcc, bcc, and hcp matrices, thus giving us confidence in the strategy. In addition, we predict a number of new, currently-unknown precipitate systems that should be explored experimentally as promising high-strength alloy chemistries.

Non-equiatomic high entropy alloys: Approach towards rapid alloy screening and property-oriented design

Energy Technology Data Exchange (ETDEWEB)

Pradeep, K.G. [Max-Planck-Institut für Eisenforschung GmbH, Max-Planck-str.1, 40237 Düsseldorf (Germany); Materials Chemistry, RWTH Aachen University, Kopernikusstr.10, 52074 Aachen (Germany); Tasan, C.C., E-mail: c.tasan@mpie.de [Max-Planck-Institut für Eisenforschung GmbH, Max-Planck-str.1, 40237 Düsseldorf (Germany); Yao, M.J. [Max-Planck-Institut für Eisenforschung GmbH, Max-Planck-str.1, 40237 Düsseldorf (Germany); Deng, Y. [Max-Planck-Institut für Eisenforschung GmbH, Max-Planck-str.1, 40237 Düsseldorf (Germany); Department of Engineering Design and Materials, Norwegian University of Science and Technology, No-7491 Trondheim (Norway); Springer, H. [Max-Planck-Institut für Eisenforschung GmbH, Max-Planck-str.1, 40237 Düsseldorf (Germany); Raabe, D., E-mail: d.raabe@mpie.de [Max-Planck-Institut für Eisenforschung GmbH, Max-Planck-str.1, 40237 Düsseldorf (Germany)

2015-11-11

The high entropy alloy (HEA) concept has triggered a renewed interest in alloy design, even though some aspects of the underlying thermodynamic concepts are still under debate. This study addresses the short-comings of this alloy design strategy with the aim to open up new directions of HEA research targeting specifically non-equiatomic yet massively alloyed compositions. We propose that a wide range of massive single phase solid solutions could be designed by including non-equiatomic variants. It is demonstrated by introducing a set of novel non-equiatomic multi-component CoCrFeMnNi alloys produced by metallurgical rapid alloy prototyping. Despite the reduced configurational entropy, detailed characterization of these materials reveals a strong resemblance to the well-studied equiatomic single phase HEA: The microstructure of these novel alloys exhibits a random distribution of alloying elements (confirmed by Energy-Dispersive Spectroscopy and Atom Probe Tomography) in a single face-centered-cubic phase (confirmed by X-ray Diffraction and Electron Backscatter Diffraction), which deforms through planar slip (confirmed by Electron-Channeling Contrast Imaging) and leads to excellent ductility (confirmed by uniaxial tensile tests). This approach widens the field of HEAs to non-equiatomic multi-component alloys since the concept enables to tailor the stacking fault energy and associated transformation phenomena which act as main mechanisms to design useful strain hardening behavior.

Non-equiatomic high entropy alloys: Approach towards rapid alloy screening and property-oriented design

International Nuclear Information System (INIS)

Pradeep, K.G.; Tasan, C.C.; Yao, M.J.; Deng, Y.; Springer, H.; Raabe, D.

2015-01-01

The high entropy alloy (HEA) concept has triggered a renewed interest in alloy design, even though some aspects of the underlying thermodynamic concepts are still under debate. This study addresses the short-comings of this alloy design strategy with the aim to open up new directions of HEA research targeting specifically non-equiatomic yet massively alloyed compositions. We propose that a wide range of massive single phase solid solutions could be designed by including non-equiatomic variants. It is demonstrated by introducing a set of novel non-equiatomic multi-component CoCrFeMnNi alloys produced by metallurgical rapid alloy prototyping. Despite the reduced configurational entropy, detailed characterization of these materials reveals a strong resemblance to the well-studied equiatomic single phase HEA: The microstructure of these novel alloys exhibits a random distribution of alloying elements (confirmed by Energy-Dispersive Spectroscopy and Atom Probe Tomography) in a single face-centered-cubic phase (confirmed by X-ray Diffraction and Electron Backscatter Diffraction), which deforms through planar slip (confirmed by Electron-Channeling Contrast Imaging) and leads to excellent ductility (confirmed by uniaxial tensile tests). This approach widens the field of HEAs to non-equiatomic multi-component alloys since the concept enables to tailor the stacking fault energy and associated transformation phenomena which act as main mechanisms to design useful strain hardening behavior.

Gain limits of a Thick GEM in high-purity Ne, Ar and Xe

CERN Document Server

Miyamoto, J; Peskov, V

2010-01-01

The dependence of the avalanche charge gain in Thick Gas Electron Multipliers (THGEM) on the purity of Ne, Ar and Xe filling gases was investigated. The gain, measured with alpha-particles in standard conditions (atmospheric pressure, room temperature), was found to considerably drop in gases purified by non-evaporable getters. On the other hand, small N2 admixtures to noble gases resulted in high reachable gains. The results are of general relevance in the operation of gas-avalanche detectors in noble gases, particularly that of two-phase cryogenic detectors for rare events.

Developing prospects of NiAlMn high temperature shape memory alloy

International Nuclear Information System (INIS)

Zou Min

1999-01-01

The reason and information on high temperature shape memory alloy research are introduced briefly Also, referring to some experimental reports on NiAlMn high temperature shape memory alloy, it is pointed out that ductility and memory property of this alloy can be improved by adapting proper composition and procedure to control its microstructure. Meanwhile, the engineering details must be considered when NiAlMn high temperature shape memory alloy being developed so as to resolve the problems of its practical use

Synthesis of high-purity Li{sub 8}ZrO{sub 6} powder by solid state reaction under hydrogen atmosphere

Energy Technology Data Exchange (ETDEWEB)

Shin-mura, Kiyoto; Otani, Yu; Ogawa, Seiya [Course of Mechanical Engineering, Graduate School of Engineering, Tokai University, 4-1-1 Kitakaname, Hiratsuka, Kanagawa 259-1292 (Japan); Niwa, Eiki; Hashimoto, Takuya [Department of Physics, College of Humanities and Sciences, Nihon University, 3-8-1 Sakurajousui, Setagaya-ku, Tokyo 156-8550 (Japan); Hoshino, Tsuyoshi [Breeding Functional Materials Development Group, Department of Blanket Systems Research, Rokkasho Fusion Institute, Sector of Fusion Research and Development, Japan Atomic Energy Agency, 2-166 Obuchi, Omotedate, Rokkasho-mura, Kamikita-gun, Aomori 039-3212 (Japan); Sasaki, Kazuya, E-mail: k_sasaki@tokai-u.ac.jp [Course of Mechanical Engineering, Graduate School of Engineering, Tokai University, 4-1-1 Kitakaname, Hiratsuka, Kanagawa 259-1292 (Japan); Department of Prime Mover Engineering, School of Engineering, Tokai University, 4-1-1 Kitakaname, Hiratsuka, Kanagawa 259-1292 (Japan)

2016-11-01

Highlights: • A fine pure Li{sub 8}ZrO{sub 6} powder was synthesized by using Li{sub 2}CO{sub 3} and ZrO{sub 2} via a solid state reaction. • Influences on the purity of product powder, lattice defect, and crystal orientation were revealed. • The suitable synthesis conditions of the fine and high purity Li{sub 8}ZrO{sub 6} powder were found. • The reaction process of the synthesis of Li{sub 8}ZrO{sub 6} was estimated. - Abstract: Li{sub 8}ZrO{sub 6} contains a large amount of Li and has a significant potential as a tritium breeder. However, few syntheses of fine-grain, high-purity Li{sub 8}ZrO{sub 6} powder have been reported. In this study, a high-purity powder of Li{sub 8}ZrO{sub 6} was synthesized by solid state reaction under hydrogen atmosphere combined with an effective lithium source and a suitable initial Li:Zr molar ratio. Mixed powders of Li{sub 2}CO{sub 3} and ZrO{sub 2} were fired at around 630 °C in H{sub 2} for several hours and several firing cycles. The low firing temperature inhibited the vaporization of Li during the heating, so that excessive amounts of Li were not needed for the synthesis, and the Li:Zr ratio in the starting material was 10:1 (mol:mol). In this synthesis, Li{sub 2}O was generated via the decomposition of Li{sub 2}CO{sub 3} during firing in H{sub 2}, and reacted with ZrO{sub 2} to form Li{sub 6}Zr{sub 2}O{sub 7}, which reacted with itself to form Li{sub 8}ZrO{sub 6}.

High Bismuth Alloys as Lead-Free Alternatives for Interconnects in High-Temperature Electronics

Science.gov (United States)

Mallampati, Sandeep

Predominant high melting point solders for high-temperature electronics (operating temperatures from 200 to 250°C) are Pb-based which are being banned from usage due to their toxic nature. In this study, high bismuth alloy compositions (Bi-14Cu-8Sn, Bi-20Sb-10Cu, Bi-15Sb-10Cu and Bi-10Sb-10Cu) were designed, cast, and characterized to understand their potential as replacements. The desirable aspect of Bi is its high melting temperature, which is 271°C. Alloying elements Sn, Sb and Cu were added to improve some of its properties such as thermal conductivity, plasticity, and reactivity with Cu and Ni surface. Metallographic sectioning and microstructure analysis were performed on the bulk alloys to compare the evolution of phases predicted from equilibrium phase diagrams. Reflow processes were developed to make die-attach samples out of the proposed alloys and die-shear testing was carried out to characterize mechanical integrity of the joint. Thermal shock between -55°C to 200°C and high temperature storage at 200°C were performed on the assembled die-attach samples to study microstructure evolution and mechanical behavior of the reflowed alloys under accelerated testing conditions. In addition, heat dissipation capabilities, using flash diffusivity, were measured on the bulk alloys and also on the die-attach assembly. Finally, tensile testing was performed on the dogbone specimens to identify the potential for plastic deformation and electron backscatter diffraction (EBSD) analysis was used to study the grain orientations on the fracture surfaces and their influence on the crack propagation. Bi-14Cu-8Sn has formed BiNi by on the die backside metallization and the reaction with Cu was poor. This has resulted in weaker substrate side interface. It was observed that Bi-Sb alloys have strong reactivity with Ni (forming Bi3Ni, BiNi and NiSb intermetallic phases), and with Cu (forming Cu2Sb, Cu4Sb). Spallation was observed in NiSb interfacial intermetallic layer and

High strength cast aluminum alloy development

Science.gov (United States)

Druschitz, Edward A.

The goal of this research was to understand how chemistry and processing affect the resulting microstructure and mechanical properties of high strength cast aluminum alloys. Two alloy systems were investigated including the Al-Cu-Ag and the Al-Zn-Mg-Cu systems. Processing variables included solidification under pressure (SUP) and heat treatment. This research determined the range in properties that can be achieved in BAC 100(TM) (Al-Cu micro-alloyed with Ag, Mn, Zr, and V) and generated sufficient property data for design purposes. Tensile, stress corrosion cracking, and fatigue testing were performed. CuAl2 and Al-Cu-Fe-Mn intermetallics were identified as the ductility limiting flaws. A solution treatment of 75 hours or longer was needed to dissolve most of the intermetallic CuAl 2. The Al-Cu-Fe-Mn intermetallic was unaffected by heat treatment. These results indicate that faster cooling rates, a reduction in copper concentration and a reduction in iron concentration might increase the ductility of the alloy by decreasing the size and amount of the intermetallics that form during solidification. Six experimental Al-Zn-Mg-Cu series alloys were produced. Zinc concentrations of 8 and 12wt% and Zn/Mg ratios of 1.5 to 5.5 were tested. Copper was held constant at 0.9%. Heat treating of the alloys was optimized for maximum hardness. Al-Zn-Mg-Cu samples were solution treated at 441°C (826°F) for 4 hours before ramping to 460°C (860°F) for 75 hours and then aged at 120°C (248°F) for 75 hours. X-ray diffraction showed that the age hardening precipitates in most of these alloys was the T phase (Mg32Zn 31.9Al17.1). Tensile testing of the alloys showed that the best mechanical properties were obtained in the lowest alloy condition. Chilled Al-8.2Zn-1.4Mg-0.9Cu solidified under pressure resulted in an alloy with a yield strength of 468MPa (68ksi), tensile strength of 525MPa (76ksi) and an elongation of 9%.

High-pressure torsion of aluminum with ultrahigh purity (99.9999%) and occurrence of inverse Hall-Petch relationship

Energy Technology Data Exchange (ETDEWEB)

Ito, Yuki [Department of Materials Science and Engineering, Kyushu University, Fukuoka 819-0395 (Japan); Edalati, Kaveh, E-mail: Kaveh.edalati@zaiko6.zaiko.kyushu-u.ac.jp [Department of Materials Science and Engineering, Kyushu University, Fukuoka 819-0395 (Japan); WPI, International Institute for Carbon-Neutral Energy Research (WPI-I2CNER), Kyushu University, Fukuoka 819-0395 (Japan); Horita, Zenji [Department of Materials Science and Engineering, Kyushu University, Fukuoka 819-0395 (Japan); WPI, International Institute for Carbon-Neutral Energy Research (WPI-I2CNER), Kyushu University, Fukuoka 819-0395 (Japan)

2017-01-02

Severe plastic deformation through the high-pressure torsion (HPT) method was applied to pure aluminum with a wide range of purity levels such as 99% (A1100), 99.5% (A1050), 99.99% (4NAl), 99.999% (5NAl) and 99.9999% (6NAl). The hardness of 6NAl decreased with straining and saturated to a level below the hardness level of the annealed sample. This softening behavior, which was similar to the behavior of metals with low melting temperatures such as indium, tin, lead and zinc, was not observed in 5NAl or less pure Al. It was found that the grain-size dependence of hardness became less significant with increasing the purity level, while the HPT-processed 6NAl followed an inverse Hall-Petch relationship. In 6NAl with large grain sizes, dislocations accumulated in the grains in the form of dislocation cells and enhanced the hardness, but when the grain size was small, the dislocations moved fast and disappeared in high-angle grain boundaries.

Amorphous germanium as an electron or hole blocking contact on high-purity germanium detectors

International Nuclear Information System (INIS)

Hansen, W.L.; Haller, E.E.

1976-10-01

Experiments were performed in an attempt to make thin n + contacts on high-purity germanium by the solid phase/sup 1)/ epitaxial regrowth of arsenic doped amorphous germanium. After cleaning the crystal surface with argon sputtering and trying many combinations of layers, it was not found possible to induce recrystallization below 400 0 C. However, it was found that simple thermally evaporated amorphous Ge made fairly good electron or hole blocking contacts. Excellent spectrometers have been made with amorphous Ge replacing the n + contact. As presently produced, the amorphous Ge contact diodes show a large variation in high-voltage leakage current

Additive Manufacturing of High-Entropy Alloys by Laser Processing

NARCIS (Netherlands)

Ocelik, V.; Janssen, Niels; Smith, Stefan; De Hosson, J. Th M.

This contribution concentrates on the possibilities of additive manufacturing of high-entropy clad layers by laser processing. In particular, the effects of the laser surface processing parameters on the microstructure and hardness of high-entropy alloys (HEAs) were examined. AlCoCrFeNi alloys with

Effects of neutron irradiation at 4500C and 16 dpa on the properties of various commercial copper alloys

International Nuclear Information System (INIS)

Brager, H.R.; Heinisch, H.L.; Garner, F.A.

1985-01-01

High-purity copper and eight copper alloys were irradiated to approx.16 dpa at approx.450 0 C in the MOTA experiment in FFTF. These alloys were also examined after aging at 400 0 C for 1000 hours. The radiation-induced changes in the electrical conductivity, tensile properties, and density were measured and compared to those of the aged materials. The changes in conductivity can be either positive or negative depending on the alloy. Changes in tensile properties of most, but not all, of the alloys seem to be primarily dependent on thermal effects rather than the effect of atomic displacements. Radiation at 450 0 C induced changes in density varying from 0.66% densification to 16.6% swelling. The latter occurred in Cu-O.1% Ag and implies a swelling rate of at least 1%/dpa. 6 references, 3 figures, 2 tables

Damage process of high purity tungsten coatings by hydrogen beam heat loads

International Nuclear Information System (INIS)

Tamura, S.; Tokunaga, K.; Yoshida, N.; Taniguchi, M.; Ezato, K.; Sato, K.; Suzuki, S.; Akiba, M.; Tsunekawa, Y.; Okumiya, M.

2005-01-01

To investigate the synergistic effects of heat load and hydrogen irradiation, cyclic heat load tests with a hydrogen beam and a comparable electron beam were performed for high purity CVD-tungsten coatings. Surface modification was examined as a function of the peak temperature by changing the heat flux. Scanning Electron Microscopy analysis showed that the surface damage caused by the hydrogen beam was more severe than that by the electron beam. In the hydrogen beam case, cracking at the surface occurred at all peak temperatures examined from 300 deg. C to 1600 deg. C. These results indicate that the injected hydrogen induces embrittlement for the CVD-tungsten coating

Functional aluminum alloys for ultra high vacuum use

International Nuclear Information System (INIS)

Kato, Yutaka; Tsukamoto, Kenji; Isoyama, Eizo

1985-01-01

Ultra high vacuum systems made of aluminum alloys are actively developed. The reasons for using aluminum alloys are low residual radioactivity, light weight, good machinability, good thermal conductivity, non-magnetism. The important function required for ultra high vacuum materials is low outgassing rate, but surface gas on ordinary aluminum is much. Then the research on aluminum surface structure with low outgassing rate has been made and the special extrusion method, that is, extrusion method with the conditions of preventing air from entering inside of pipe and of taking in mixture gas of Ar + O 2 , was developed. 6063 alloy obtained by special extrusion method showed low outgassing rate (2 x 10 -13 Torr. 1/s. cm 2 ) by only 150 deg C, 24 h baking. For the future it will be important to develop aluminum alloys with low dynamic outgassing rate as well as low static outgassing rate. (author)

Hydrofluoric Acid Corrosion Study of High-Alloy Materials

International Nuclear Information System (INIS)

Osborne, P.E.

2002-01-01

A corrosion study involving high-alloy materials and concentrated hydrofluoric acid (HF) was conducted in support of the Molten Salt Reactor Experiment Conversion Project (CP). The purpose of the test was to obtain a greater understanding of the corrosion rates of materials of construction currently used in the CP vs those of proposed replacement parts. Results of the study will help formulate a change-out schedule for CP parts. The CP will convert slightly less than 40 kg of 233 U from a gas (UF 6 ) sorbed on sodium fluoride pellets to a more stable oxide (U 3 O 8 ). One by-product of the conversion is the formation of concentrated HF. Six moles of highly corrosive HF are produced for each mole of UF 6 converted. This acid is particularly corrosive to most metals, elastomers, and silica-containing materials. A common impurity found in 233 U is 232 U. This impurity isotope has several daughters that make the handling of the 233 U difficult. Traps of 233 U may have radiation fields of up to 400 R at contact, a situation that makes the process of changing valves or working on the CP more challenging. It is also for this reason that a comprehensive part change-out schedule must be established. Laboratory experiments involving the repeated transfer of HF through 1/2-in. metal tubing and valves have proven difficult due to the corrosivity of the HF upon contact with all wetted parts. Each batch of HF is approximately 1.5 L of 33 wt% HF and is transferred most often as a vapor under vacuum and at temperatures of up to 250 C. Materials used in the HF side of the CP include Hastelloy C-276 and Monel 400 tubing, Haynes 230 and alloy C-276 vessels, and alloy 400 valve bodies with Inconel (alloy 600) bellows. The chemical compositions of the metals discussed in this report are displayed in Table 1. Of particular concern are the almost 30 vendor-supplied UG valves that have the potential for exposure to HF. These valves have been proven to have a finite life due to failure

Precipitation in an Al–Mg–Cu alloy and the effect of a low amount of Ag

Energy Technology Data Exchange (ETDEWEB)

Mihara, Mami, E-mail: mihara.m.aa@m.titech.ac.jp [Department of Metallurgy and Ceramics Science, Tokyo Institute of Technology, Tokyo 152-8552 (Japan); Marioara, Calin D., E-mail: Calin.D.Marioara@sintef.no [SINTEF Materials and Chemistry, N-7465 Trondheim (Norway); Andersen, Sigmund J., E-mail: Sigmund.J.Andersen@sintef.no [SINTEF Materials and Chemistry, N-7465 Trondheim (Norway); Holmestad, Randi, E-mail: randi.holmestad@ntnu.no [Faculty of Physics, Norwegian University of Science and Technology, N-7491 Trondheim (Norway); Kobayashi, Equo, E-mail: equo@mtl.titech.ac.jp [Department of Metallurgy and Ceramics Science, Tokyo Institute of Technology, Tokyo 152-8552 (Japan); Sato, Tatsuo, E-mail: sato.tatsuo8@gmail.com [Precision and Intelligence Laboratory, Tokyo Institute of Technology, Yokohama 226-8503 (Japan)

2016-03-21

Two high-purity aluminium alloys based on composition Al–3.0Mg–1.0Cu (wt%), one with added 0.4 wt% Ag, were compared up to 11 days ageing at 443 K by means of transmission electron microscopy and hardness measurements. The base alloy exhibits an inhomogeneous precipitate microstructure with a high density of fine needle-shaped Guinier-Preston-Bagaryatsky (GPB) zones together with coarser precipitates of S′-Al{sub 2}CuMg and rods of the structurally unknown Z-phase. The S′ phase is preferably formed on dislocations. The addition of Ag has a strong effect, leading to a homogeneous distribution with fine Ag-containing icosahedral quasi-crystalline precipitates (iQC). Both the GPB zones in the base alloy and the iQC phase in the Ag added alloy survive even after long term ageing. Ag is found to suppress the formation of the S′ phase. It is suggested that the Z phase is an approximation phase to the quasi-crystalline phase as is the case for the T-phase, implying they are based on similar (Bergman) clusters.

Effects of Alloying Elements on Room and High Temperature Tensile Properties of Al-Si Cu-Mg Base Alloys =

Science.gov (United States)

Alyaldin, Loay

In recent years, aluminum and aluminum alloys have been widely used in automotive and aerospace industries. Among the most commonly used cast aluminum alloys are those belonging to the Al-Si system. Due to their mechanical properties, light weight, excellent castability and corrosion resistance, these alloys are primarily used in engineering and in automotive applications. The more aluminum is used in the production of a vehicle, the less the weight of the vehicle, and the less fuel it consumes, thereby reducing the amount of harmful emissions into the atmosphere. The principal alloying elements in Al-Si alloys, in addition to silicon, are magnesium and copper which, through the formation of Al2Cu and Mg2Si precipitates, improve the alloy strength via precipitation hardening following heat treatment. However, most Al-Si alloys are not suitable for high temperature applications because their tensile and fatigue strengths are not as high as desired in the temperature range 230-350°C, which are the temperatures that are often attained in automotive engine components under actual service conditions. The main challenge lies in the fact that the strength of heat-treatable cast aluminum alloys decreases at temperatures above 200°C. The strength of alloys under high temperature conditions is improved by obtaining a microstructure containing thermally stable and coarsening-resistant intermetallics, which may be achieved with the addition of Ni. Zr and Sc. Nickel leads to the formation of nickel aluminide Al3Ni and Al 9FeNi in the presence of iron, while zirconium forms Al3Zr. These intermetallics improve the high temperature strength of Al-Si alloys. Some interesting improvements have been achieved by modifying the composition of the base alloy with additions of Mn, resulting in an increase in strength and ductility at both room and high temperatures. Al-Si-Cu-Mg alloys such as the 354 (Al-9wt%Si-1.8wt%Cu-0.5wt%Mg) alloys show a greater response to heat treatment as a

Purity Evaluation of Single-Walled Carbon Nanotubes Using Thermogravimetric Analysis

International Nuclear Information System (INIS)

Goak, Jeung Choon; Kim, Tae Yang; Jung, Jongwan; Seo, Young-Soo; Lee, Naesung; Sok, Junghyun

2013-01-01

This study evaluated the purity of single-walled carbon nanotubes (SWCNTs) in the arc-synthesized SWCNT samples by using thermogravimetric analysis (TGA). The as-produced SWCNT samples were heat-treated in air for 20 h at 275-475°C and characterized by scanning and transmission electron microscopes and TGA to establish oxidation temperature ranges of SWCNTs and carbonaceous impurities comprising the samples. Based on these oxidation temperature ranges, derivative thermogravimetric curves were deconvoluted, and differentiated peaks were assigned to SWCNTs and carbonaceous impurities. The compositions and the SWCNT purities of the samples were obtained simply by calculating the areal ratios under the deconvoluted curves. TGA studies on purity evaluation and thermal stabilities of SWCNTs and carbonaceous impurities are likely to provide us with a simple route of thermal oxidation purification to acquire high-purity SWCNT samples.

Corrosion behaviour of Al-Fe-Ti-V medium entropy alloy

Science.gov (United States)

Bodunrin, M. O.; Obadele, B. A.; Chown, L. H.; Olubambi, P. A.

2017-12-01

Alloys containing up to four multi-principal elements in equiatomic ratios are referred to as medium entropy alloys (MEA). These alloys have attracted the interest of many researchers due to the superior mechanical properties it offers over the traditional alloys. The design approach of MEA often results to simple solid solution with either body centered cubic; face centered cubic structures or both. As the consideration for introducing the alloys into several engineering application increases, there have been efforts to study the corrosion behaviour of these alloys. Previous reports have shown that some of these alloys are more susceptible to corrosion when compared with traditional alloys due to lack of protective passive film. In this research, we have developed AlFeTiV medium entropy alloys containing two elements (Ti and Al) that readily passivate when exposed to corrosive solutions. The alloys were produced in vacuum arc furnace purged with high purity argon. Open circuit potential and potentiodynamic polarisation tests were used to evaluate the corrosion behaviour of the as-cast AlFeTiV alloy in 3.5 wt% NaCl and 1 M H2SO4. The corrosion performance of the alloy was compared with Ti-6Al-4V alloy tested under similar conditions. The results show that unlike in Ti-6Al-4V alloy, the open circuit potential of the AlFeTiV alloy move towards the negative values in both 3.5 wt% NaCl and 1 M H2SO4 solutions indicating that self-activation occurred rapidly on immersion. Anodic polarisation of the alloys showed that AlFeTiV alloy exhibited a narrow range of passivity in both solutions. In addition, the alloys exhibited lower Ecorr and higher Icorr when compared with traditional Ti-6Al-4V alloy. The traditional Ti-6Al-4V alloy showed superior corrosion resistant to the AlFeTiV alloy in both 3.5 wt.% NaCl and 1 M H2SO4 solutions.

N-Type delta Doping of High-Purity Silicon Imaging Arrays

Science.gov (United States)

Blacksberg, Jordana; Hoenk, Michael; Nikzad, Shouleh

2005-01-01

A process for n-type (electron-donor) delta doping has shown promise as a means of modifying back-illuminated image detectors made from n-doped high-purity silicon to enable them to detect high-energy photons (ultraviolet and x-rays) and low-energy charged particles (electrons and ions). This process is applicable to imaging detectors of several types, including charge-coupled devices, hybrid devices, and complementary metal oxide/semiconductor detector arrays. Delta doping is so named because its density-vs.-depth characteristic is reminiscent of the Dirac delta function (impulse function): the dopant is highly concentrated in a very thin layer. Preferably, the dopant is concentrated in one or at most two atomic layers in a crystal plane and, therefore, delta doping is also known as atomic-plane doping. The use of doping to enable detection of high-energy photons and low-energy particles was reported in several prior NASA Tech Briefs articles. As described in more detail in those articles, the main benefit afforded by delta doping of a back-illuminated silicon detector is to eliminate a "dead" layer at the back surface of the silicon wherein high-energy photons and low-energy particles are absorbed without detection. An additional benefit is that the delta-doped layer can serve as a back-side electrical contact. Delta doping of p-type silicon detectors is well established. The development of the present process addresses concerns specific to the delta doping of high-purity silicon detectors, which are typically n-type. The present process involves relatively low temperatures, is fully compatible with other processes used to fabricate the detectors, and does not entail interruption of those processes. Indeed, this process can be the last stage in the fabrication of an imaging detector that has, in all other respects, already been fully processed, including metallized. This process includes molecular-beam epitaxy (MBE) for deposition of three layers, including

Sorption techniques for production of high purity refractory metals

International Nuclear Information System (INIS)

Shatalov, V.V.; Peganov, V.A.; Logvinenko, I.A.; Molchanova, T.V.

2004-01-01

A consideration is given to potentialities of sorption processes tot provide a high quality of refractory metal and their alloys when using hydrometallurgical methods for raw material processing. The efficiency of application of ion exchange technology is shown for complex solutions reprocessing for various types of polymetallic raw materials, among them uranium ores, enriched concentrates of refractory metal ores, intermediate products, waste solutions. Based on investigation results on the behaviour of elements in process solutions and the mechanism of their sorption and elution, the process of pure chemical compounds production are developed which provide thereafter manufacturing compact metals. The flowsheets developed are mastered on a commercial scale [ru

Determination of tungsten in high-alloy steels and heat resisting alloys by isotope dilution-spark source mass spectrometry

International Nuclear Information System (INIS)

Saito, Morimasa; Yamada, Kei; Okochi, Haruno; Hirose, Fumio

1983-01-01

Tungsten in high-alloy steels and heat-resisting alloys was determined by isotope dilution method combined with spark source mass spectrometry by using 183 W enriched tungsten. The spike solution was prepared by fusing tungsten trioxide in sodium carbonate. A high-alloy steel sample was dissolved in the mixture of sulfuric acid and phosphoric acid together with the spike solution; a sample of heat resisting alloy was similarly dissolved in the mixture of hydrochloric acid, nitric acid, sulfuric acid, and phosphoric acid. The solution was evaporated to give dense white fumes. Tungsten was separated from the residue by a conventional cinchonine salt-precipitation method. The salt was ignited, and the residue was mixed with graphite powder and pressed into electrodes. The isotope 183 W and 184 W were measured. The method was applied to the determination of tungsten in JSS and NBS standard high-alloy steels and JAERI standard nickel- and NBS standard cobalt-base heat resisting alloys containing more than 0.05% tungsten. The results were obtained with satisfactory precision and accuracy. However, the results obtained for JSS standard high- speed steels containing molybdenum tended to be significantly lower than the certified values. (author)

Effect of temperature on corrosion of steels in high purity water

International Nuclear Information System (INIS)

Honda, Takashi; Kashimura, Eiji; Ohashi, Kenya; Furutani, Yasumasa; Ohsumi, Katsumi; Aizawa, Motohiro; Matsubayashi, Hideo.

1987-01-01

Effect of temperature on corrosion behavior of steels was evaluated in the range of 150 - 300 deg C in high purity water containing about 200 ppb oxygen. The exposure tests were carried out in actual and simulated reactor water of BWR plants. Through X-ray diffractometry, SIMS, XPS and chemical analyses, it was clarified that the chemical composition and morphology of oxide films formed on austenitic stainless steel changed above about 250 deg C. Chromium dissolved easily through corrosion above this temperature, and the oxide films primarily consisted of spinel type oxides containing high concentration of nickel. Further, as the protectivety of oxide films increased with temperature, the corrosion rate had a peak around 250 deg C after a long exposure period. A major phase of oxide films on carbon steel was magnetite in the whole temperature range. However, as the oxide films formed at high temperatures had very compact structures, the effect of temperature on the corrosion rate was similar to that observed on stainless steel. (author)

Design of Refractory High-Entropy Alloys

Science.gov (United States)

Gao, M. C.; Carney, C. S.; Doğan, Ö. N.; Jablonksi, P. D.; Hawk, J. A.; Alman, D. E.

2015-11-01

This report presents a design methodology for refractory high-entropy alloys with a body-centered cubic (bcc) structure using select empirical parameters (i.e., enthalpy of mixing, atomic size difference, Ω-parameter, and electronegativity difference) and CALPHAD approach. Sixteen alloys in equimolar compositions ranging from quinary to ennead systems were designed with experimental verification studies performed on two alloys using x-ray diffraction, energy-dispersive spectroscopy, and scanning electron microscopy. Two bcc phases were identified in the as-cast HfMoNbTaTiVZr, whereas multiple phases formed in the as-cast HfMoNbTaTiVWZr. Observed elemental segregation in the alloys qualitatively agrees with CALPHAD prediction. Comparisons of the thermodynamic mixing properties for liquid and bcc phases using the Miedema model and CALPHAD are presented. This study demonstrates that CALPHAD is more effective in predicting HEA formation than empirical parameters, and new single bcc HEAs are suggested: HfMoNbTiZr, HfMoTaTiZr, NbTaTiVZr, HfMoNbTaTiZr, HfMoTaTiVZr, and MoNbTaTiVZr.

High Temperature Properties and Recent Research Trend of Mg-RE Alloys

Energy Technology Data Exchange (ETDEWEB)

Nam, Soo Woo [Korea Institute of Science and Technology Information, Seoul (Korea, Republic of)

2017-04-15

For the applications in automotive, aircraft, aerospace, and electronic industries, the lightest structural Mg alloys have received much attention since 2000. There has been some progress for the improvement of the mechanical properties such as room temperature strength, formability and mechanical anisotropy. However, the high temperature strength of Mg alloys is very low to be used for the parts and structures of high temperature conditions. For the last decade, considerable efforts are concentrated for the development of Mg alloys to be used at high temperature. Newly developing Mg-RE alloys are the good examples for the high temperature use. In this regard, this review paper introduces the recent research trends for the development of Mg-RE alloys strengthened with some precipitates and the long period stacking ordered (LPSO) structures related RE elements.

High Temperature Properties and Recent Research Trend of Mg-RE Alloys

International Nuclear Information System (INIS)

Nam, Soo Woo

2017-01-01

For the applications in automotive, aircraft, aerospace, and electronic industries, the lightest structural Mg alloys have received much attention since 2000. There has been some progress for the improvement of the mechanical properties such as room temperature strength, formability and mechanical anisotropy. However, the high temperature strength of Mg alloys is very low to be used for the parts and structures of high temperature conditions. For the last decade, considerable efforts are concentrated for the development of Mg alloys to be used at high temperature. Newly developing Mg-RE alloys are the good examples for the high temperature use. In this regard, this review paper introduces the recent research trends for the development of Mg-RE alloys strengthened with some precipitates and the long period stacking ordered (LPSO) structures related RE elements.

Alloy model for high temperature superconductors

International Nuclear Information System (INIS)

Weissmann, M.; Saul, A.

1991-07-01

An alloy model is proposed for the electronic structure of high temperature superconductors. It is based on the assumption that holes and extra electrons are localized in small copper oxygen clusters, that would be the components of such alloy. This model, when used together with quantum chemical calculations on small clusters, can explain the structure observed in the experimental densities of states of both hole and electron superconductors close to the Fermi energy. The main point is the strong dependence of the energy level distribution and composition on the number of electrons in a cluster. The alloy model also suggests a way to correlate Tc with the number of holes, or extra electrons, and the number of adequate clusters to locate them. (author). 21 refs, 4 figs, 1 tab

ASSET, An Information System for Alloy Corrosion in High Temperature Gases

International Nuclear Information System (INIS)

R. C. John; A. D. Pelton; A. L. Young; W. T. Thompson; I. G. Wright

2001-01-01

A large database for corrosion data and a corrosion prediction information system for metals and alloys corroding in high-temperature gases have been created. Corrosion data for about 75 commercial alloys, 4600 corrosion data measurements, and six million exposure hours have been compiled into an information system, ASSET. ASSET allows prediction of sound metal thickness losses for metals and alloys corroding by several common corrosion mechanisms at high-temperatures as functions of gas composition, temperature, time, and alloy. This paper presents examples of predicted metal losses of alloys corroding in standard conditions for several corrosion mechanisms expected in high-temperature gases. ASSET also provides a comprehensive capability to analyze the thermochemical interactions between alloys, corrosion products and exposure conditions. Some of the uses of the data compilation and the corrosion prediction feature are illustrated for oxidizing, sulfidizing, sulfidizing/oxidizing , and carburizing conditions

[Studies on high temperature oxidation of noble metal alloys for dental use. (III) On high temperature oxidation resistance of noble metal alloys by adding small amounts of alloying elements. (author's transl)].

Science.gov (United States)

Ohno, H

1976-11-01

The previous report pointed out the undesirable effects of high temperature oxidation on the casting. The influence of small separate additions of Zn, Mg, Si, Be and Al on the high temperature oxidation of the noble metal alloys was examined. These alloying elements were chosen because their oxide have a high electrical resistivity and they have much higher affinity for oxygen than Cu. The casting were oxidized at 700 degrees C for 1 hour in air. The results obtained were as follows: 1. The Cu oxides are not observed on the as-cast surface of noble metal alloys containing small amounts of Zn, Mg, Si, Be, and Al. The castings have gold- or silver-colored surface. 2. After heating of the unpolished and polished castings, the additions of Si, Be and Al are effective in preventing oxidation of Cu in the 18 carats gold alloys. Especially the golden surface is obtained by adding Be and Al. But there is no oxidation-resistance on the polished castings in the alloys containing Zn and Mg. 3. The zinc oxide film formed on the as-cast specimen is effective in preventing of oxidation Cu in 18 carats gold alloys. 4. It seems that the addition of Al is most available in dental application.

Effects of cyclic tensile loading on stress corrosion cracking susceptibility for sensitized Type 304 stainless steel in 290 C high purity water

International Nuclear Information System (INIS)

Takaku, H.; Tokiwai, M.; Hirano, H.

1979-01-01

The effects of load waveform on intergranular stress corrosion cracking (IGSCC) susceptibility have been examined for sensitized Type 304 stainless steels in a 290 C high purity water loop. Concerning the strain rate in the trapezoidal stress waveform, it was found that IGSCC susceptibility was higher for smaller values of the strain rate. It was also shown that IGSCC susceptibility became higher when the holding time at the upper stress was prolonged, and when the upper stress was high. The occurrence of IGSCC for sensitized Type 304 stainless steel became easy due to the application of cyclic tensile stress in 290 C high purity water

Materials Properties Database for Selection of High-Temperature Alloys and Concepts of Alloy Design for SOFC Applications

Energy Technology Data Exchange (ETDEWEB)

Yang, Z Gary; Paxton, Dean M.; Weil, K. Scott; Stevenson, Jeffry W.; Singh, Prabhakar

2002-11-24

To serve as an interconnect / gas separator in an SOFC stack, an alloy should demonstrate the ability to provide (i) bulk and surface stability against oxidation and corrosion during prolonged exposure to the fuel cell environment, (ii) thermal expansion compatibility with the other stack components, (iii) chemical compatibility with adjacent stack components, (iv) high electrical conductivity of the surface reaction products, (v) mechanical reliability and durability at cell exposure conditions, (vii) good manufacturability, processability and fabricability, and (viii) cost effectiveness. As the first step of this approach, a composition and property database was compiled for high temperature alloys in order to assist in determining which alloys offer the most promise for SOFC interconnect applications in terms of oxidation and corrosion resistance. The high temperature alloys of interest included Ni-, Fe-, Co-base superal

High-purity fatty acid methyl ester production from canola, soybean, palm, and yellow grease lipids by means of a membrane reactor

International Nuclear Information System (INIS)

Cao Peigang; Dube, Marc A.; Tremblay, Andre Y.

2008-01-01

High-purity fatty acid methyl ester (FAME) was produced from different lipids, such as soybean oil, canola oil, a hydrogenated palm oil/palm oil blend, yellow grease, and brown grease, combined with methanol using a continuous membrane reactor. The membrane reactor combines reaction and separation in a single unit, provides continuous mixing of raw materials, and maintains a high molar ratio of methanol to lipid in the reaction loop while maintaining two phases during the reaction. It was demonstrated that the membrane reactor can be operated using a very broad range of feedstocks at highly similar operating conditions to produce FAME. The total glycerine and free glycerine contents of the FAME produced were below the ASTM D6751 standard after a single reaction step. Under essentially the same reaction conditions, a conventional batch reaction was not able to achieve the same degree of FAME purity. The effect of the fatty acid composition of the lipid feedstocks on the FAME purity was also shown. It was demonstrated that, due to the fatty acid composition, FAME from virgin soybean oil and virgin canola oil was produced in the membrane reactor within ASTM specifications even without a water washing step

Searching for Next Single-Phase High-Entropy Alloy Compositions

Directory of Open Access Journals (Sweden)

David E. Alman

2013-10-01

Full Text Available There has been considerable technological interest in high-entropy alloys (HEAs since the initial publications on the topic appeared in 2004. However, only several of the alloys investigated are truly single-phase solid solution compositions. These include the FCC alloys CoCrFeNi and CoCrFeMnNi based on 3d transition metals elements and BCC alloys NbMoTaW, NbMoTaVW, and HfNbTaTiZr based on refractory metals. The search for new single-phase HEAs compositions has been hindered by a lack of an effective scientific strategy for alloy design. This report shows that the chemical interactions and atomic diffusivities predicted from ab initio molecular dynamics simulations which are closely related to primary crystallization during solidification can be used to assist in identifying single phase high-entropy solid solution compositions. Further, combining these simulations with phase diagram calculations via the CALPHAD method and inspection of existing phase diagrams is an effective strategy to accelerate the discovery of new single-phase HEAs. This methodology was used to predict new single-phase HEA compositions. These are FCC alloys comprised of CoFeMnNi, CuNiPdPt and CuNiPdPtRh, and HCP alloys of CoOsReRu.

A study of hydrogen permeation in aluminum alloy treated by various oxidation processes

International Nuclear Information System (INIS)

Song Wenhai; Long Bin

1997-01-01

A set of oxide coatings was formed on the surface of an Al alloy (wt%: Fe, 0.24; Si, 1.16; Cu, 0.05-0.2; Zn, 0.1; Al, residual) by means of various oxidation processes. The hydrogen permeability through the aluminum alloy and its coating materials was determined by a vapor phase permeation technique at temperatures ranging from 400 to 500 C using high-purity H 2 (99.9999%) gas with an upstream hydrogen pressure of 10 4 -10 5 Pa. The experimental results show that the hydrogen permeability through aluminum oxide coating is 100-2000 times lower than that through the aluminum alloy substrate. This means that the aluminum oxide is a significant hydrogen permeation barrier. A high hydrogen permeation resistance was observed in an oxide layer prefilmed in 200 C water, while an anodized aluminum oxide film had a less obstructive effect, possibly caused by the porous structure of the anodic oxide. The hydrogen permeability through films of aluminum oxide was not a simple function of the aluminum-oxide phase configuration. (orig.)

Conference Proceedings of the Meeting of the Structures and Materials Panel of AGARD (67th) on New Light Alloys, Held in Mierlo, Netherlands on 3-5 October 1988

Science.gov (United States)

1989-08-01

120’C. Recently, a high purity version of AZ91 , designated AZ91E , has been developed by the Dow Chemical Co and AMAX Magnesium 12 . The alloy contains...the pure magnesium standard. Akavipat et al28,29 implanted iron and boron ions into the surface of magnesium alloys. Typically, the corrosion current...for implanted samples was a factor 10 smaller than in unimplanted samples. Iron usually has a detrimental effect on the corrosion rate of magnesium

Corrosion Characteristics of Ti-xTa Alloys with Ta contents

International Nuclear Information System (INIS)

Kim, H. J.; Choe, H. C.

2013-01-01

The purpose of this study was to investigate corrosion characteristics of Ti-xTa alloys with Ta contents. Ti-xTa alloys used as samples (x=30, 40%) were arc-melted under argon atmosphere of 99.9% purity. Ti-xTa alloys were homogenized for 12hr at 1000 .deg. C and then water quenched. The surface characteristics of Ti-xTa alloys were investigated using optical microscopy (OM) and X-ray diffractometer (XRD). The anodic corrosion behaviors of the specimens were examined through potentiodynamic, potentiostatic and galvanostatic test in 0.9 % NaCl solution at 36.5 ± 1 .deg. C. After corrosion test, the surface characteristics of Ti-xTa alloys were investigated using OM. The microstructure of Ti-Ta alloy showed the beta structure with Ta content. The corrosion resistance of Ti alloy was improved by increasing Ta content and the corrosion morphology of Ti-Ta alloy showed that the site attacked by chloride ion decreased from the active to passive region with Ta content. Potential of Ti-40Ta alloy increased as time increased, whereas, current density of Ti-40Ta alloy decreased as time increased compared to Ti-30 alloy

Formation and Disruption of W-Phase in High-Entropy Alloys

Directory of Open Access Journals (Sweden)

Sephira Riva

2016-05-01

Full Text Available High-entropy alloys (HEAs are single-phase systems prepared from equimolar or near-equimolar concentrations of at least five principal elements. The combination of high mixing entropy, severe lattice distortion, sluggish diffusion and cocktail effect favours the formation of simple phases—usually a bcc or fcc matrix with minor inclusions of ordered binary intermetallics. HEAs have been proposed for applications in which high temperature stability (including mechanical and chemical stability under high temperature and high mechanical impact is required. On the other hand, the major challenge to overcome for HEAs to become commercially attractive is the achievement of lightweight alloys of extreme hardness and low brittleness. The multicomponent AlCrCuScTi alloy was prepared and characterized using powder X-ray diffraction (PXRD, scanning-electron microscope (SEM and atomic-force microscope equipped with scanning Kelvin probe (AFM/SKP techniques. Results show that the formation of complex multicomponent ternary intermetallic compounds upon heating plays a key role in phase evolution. The formation and degradation of W-phase, Al2Cu3Sc, in the AlCrCuScTi alloy plays a crucial role in its properties and stability. Analysis of as-melted and annealed alloy suggests that the W-phase is favoured kinetically, but thermodynamically unstable. The disruption of the W-phase in the alloy matrix has a positive effect on hardness (890 HV, density (4.83 g·cm−3 and crack propagation. The hardness/density ratio obtained for this alloy shows a record value in comparison with ordinary heavy refractory HEAs.

Determination of microamounts of carbon in various metals and alloys by the combustion-nonaqueous titrimetric method

Energy Technology Data Exchange (ETDEWEB)

Yoshimori, T; Koike, A [Science Univ. of Tokyo (Japan). Faculty of Engineering; Katoh, N

1977-12-01

Microamounts of carbon (7 -- 600 ppm) in ferrous and non-ferrous metals and alloys were determined by the combustion-nonaqueous titrimetric method. The carbon dioxide liberated by the combustion of a sample was absorbed with dimethylformamide (DMF) containing monoethanolamine and then the absorbent was titrated with the standard benzene-methanol solution of tetra-n-butylammonium hydroxide (0.007-0.002 M). The end point of the titration was located either visibly by using thymolphthalein as an indicator or potentiometrically by using a couple of platinum and calomel (containing DMF) electrodes. Pure benzoic acid was used as the standard substance for the standardization. Many improvements were given on both the combustion apparatus and the procedure. Microamounts of carbon in various samples were determined by the proposed method. They are : plain carbon and high purity ferritic stainless steels (0.05 -- 0.002% C), Inconel X-750 (0.027% C), copper alloys (20 -- 30 ppm C), tantalum powder (40 ppm C) and high purity metallic uranium (7 ppm C). All results were quite satisfactory and indicate that the proposed method was adaptable for the determination of carbon less than 100 ppm in various samples without use of any standard samples or calibration curves.

Fast Slip Velocity in a High-Entropy Alloy

Science.gov (United States)

Rizzardi, Q.; Sparks, G.; Maaß, R.

2018-04-01

Due to fluctuations in nearest-neighbor distances and chemistry within the unit cell, high-entropy alloys are believed to have a much higher resistance to dislocation motion than pure crystals. Here, we investigate the coarse-grained dynamics of a number of dislocations being active during a slip event. We found that the time-resolved dynamics of slip is practically identical in Au and an Al0.3CoCrFeNi high-entropy alloy, but much faster than in Nb. Differences between the FCC-crystals are seen in the spatiotemporal velocity profile, with faster acceleration and slower velocity relaxation in the high-entropy alloy. Assessing distributions that characterize the intermittently evolving plastic flow reveals material-dependent scaling exponents for size, duration, and velocity-size distributions. The results are discussed in view of the underlying dislocation mobility.

Research and Application of New Type of High Performance Titanium Alloy

Directory of Open Access Journals (Sweden)

ZHU Zhishou

2016-06-01

Full Text Available With the continuous extension of the application quantity and range for titanium alloy in the fields of national aviation, space, weaponry, marine and chemical industry, etc., even more critical requirements to the comprehensive mechanical properties, low cost and process technological properties of titanium alloy have been raised. Through the alloying based on the microstructure parameters design, and the comprehensive strengthening and toughening technologies of fine grain strengthening, phase transformation and process control of high toughening, the new type of high performance titanium alloy which has good comprehensive properties of high strength and toughness, anti-fatigue, failure resistance and anti-impact has been researched and manufactured. The new titanium alloy has extended the application quantity and application level in the high end field, realized the industrial upgrading and reforming, and met the application requirements of next generation equipment.

Improved Mo-Re VPS Alloys for High-Temperature Uses

Science.gov (United States)

Hickman, Robert; Martin, James; McKechnie, Timothy; O'Dell, John Scott

2011-01-01

Dispersion-strengthened molybdenum- rhenium alloys for vacuum plasma spraying (VPS) fabrication of high-temperature-resistant components are undergoing development. In comparison with otherwise equivalent non-dispersion-strengthened Mo-Re alloys, these alloys have improved high-temperature properties. Examples of VPS-fabricated high-temperature-resistant components for which these alloys are expected to be suitable include parts of aircraft and spacecraft engines, furnaces, and nuclear power plants; wear coatings; sputtering targets; x-ray targets; heat pipes in which liquid metals are used as working fluids; and heat exchangers in general. These alloys could also be useful as coating materials in some biomedical applications. The alloys consist of 60 weight percent Mo with 40 weight percent Re made from (1) blends of elemental Mo and Re powders or (2) Re-coated Mo particles that have been subjected to a proprietary powder-alloying-and-spheroidization process. For most of the dispersion- strengthening experiments performed thus far in this development effort, 0.4 volume percent of transition-metal ceramic dispersoids were mixed into the feedstock powders. For one experiment, the proportion of dispersoid was 1 volume percent. In each case, the dispersoid consisted of either ZrN particles having sizes <45 m, ZrO2 particles having sizes of about 1 m, HfO2 particles having sizes <45 m, or HfN particles having sizes <1 m. These materials were chosen for evaluation on the basis of previously published thermodynamic stability data. For comparison, Mo-Re feedstock powders without dispersoids were also prepared.

Synthesis of Fe-based amorphous composite coatings with low purity materials by laser cladding

Energy Technology Data Exchange (ETDEWEB)

Zhu Qingjun [School of Materials Science and Engineering, Shandong University, Jinan 250061 (China)]. E-mail: sduzhu@yahoo.com.cn; Qu Shiyao [School of Materials Science and Engineering, Shandong University, Jinan 250061 (China); Wang Xinhong [School of Materials Science and Engineering, Shandong University, Jinan 250061 (China); Zou Zengda [School of Materials Science and Engineering, Shandong University, Jinan 250061 (China)

2007-06-30

Amorphous composite coatings Fe{sub 38}Ni{sub 30-X}Si{sub 16}B{sub 14}V{sub 2}M {sub X} (X = 0, 1, 2) (M contains Al, Ti, Mo, and C) were prepared with low purity of raw materials by laser cladding. X-ray diffraction and transmission electron microscopy results show that the coating have an amorphous structure with a few crystalline phase on it. The amorphous phase is the primary phase. The glass forming ability as well as the microhardness of the Fe-based alloy made from low purity raw materials can be much enhanced by adding small amount of multi-components. However, the elements addition has its optimal quantity. When X is equal to 1, the microstructure of the coating contains 97.93% amorphous phase and 2.07% crystalline phase on it. As a result, the microhardness of the coating reaches maximum. With further increasing of the additions, the amorphous phase in the coating lessens instead of augment and the crystalline phase begins to accumulate, which result in the decrease of the microhardness.

Powder Metallurgy Processing of a WxTaTiVCr High-Entropy Alloy and Its Derivative Alloys for Fusion Material Applications.

Science.gov (United States)

Waseem, Owais Ahmed; Ryu, Ho Jin

2017-05-16

The W x TaTiVCr high-entropy alloy with 32at.% of tungsten (W) and its derivative alloys with 42 to 90at.% of W with in-situ TiC were prepared via the mixing of elemental W, Ta, Ti, V and Cr powders followed by spark plasma sintering for the development of reduced-activation alloys for fusion plasma-facing materials. Characterization of the sintered samples revealed a BCC lattice and a multi-phase structure. The selected-area diffraction patterns confirmed the formation of TiC in the high-entropy alloy and its derivative alloys. It revealed the development of C15 (cubic) Laves phases as well in alloys with 71 to 90at.% W. A mechanical examination of the samples revealed a more than twofold improvement in the hardness and strength due to solid-solution strengthening and dispersion strengthening. This study explored the potential of powder metallurgy processing for the fabrication of a high-entropy alloy and other derived compositions with enhanced hardness and strength.

Producing titanium-niobium alloy by high energy beam

Energy Technology Data Exchange (ETDEWEB)

Sharkeev, Yu. P., E-mail: sharkeev@ispms.tsc.ru [Institute of Strength Physics and Materials Science, SB RAS, 2/4 Akademicheski Prosp., Tomsk, 634055 (Russian Federation); National Research Tomsk Polytechnic University, 30 Lenin Av., Tomsk, 634050 (Russian Federation); Golkovski, M. G., E-mail: golkoski@mail.ru [Budker Institute of Nuclear Physics, 11 Akademika Lavrentiev Prosp., Novosibirsk, 630090 (Russian Federation); Glukhov, I. A., E-mail: gia@ispms.tsc.ru; Eroshenko, A. Yu., E-mail: eroshenko@ispms.tsc.ru; Fortuna, S. V., E-mail: s-fortuna@mail.ru [Institute of Strength Physics and Materials Science, SB RAS, 2/4 Akademicheski Prosp., Tomsk, 634055 (Russian Federation); Bataev, V. A., E-mail: bataev@vadm.ustu.ru [Novosibirsk State Technical University, 20 K. Marx Prosp., Novosibirsk, 630073 (Russian Federation)

2016-01-15

The research is involved in producing a Ti-Nb alloy surface layer on titanium substrate by high energy beam method, as well as in examining their structures and mechanical properties. Applying electron-beam cladding it was possible to produce a Ti-Nb alloy surface layer of several millimeters, where the niobium concentration was up to 40% at. and the structure itself could be related to martensite quenching structure. At the same time, a significant microhardness increase of 3200-3400 MPa was observed, which, in its turn, is connected with the formation of martensite structure. Cladding material of Ti-Nb composition could be the source in producing alloys of homogeneous microhardness and desired concentration of alloying niobium element.

Dynamic High-Temperature Characterization of an Iridium Alloy in Compression at High Strain Rates

Energy Technology Data Exchange (ETDEWEB)

Song, Bo [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States). Experimental Environment Simulation Dept.; Nelson, Kevin [Sandia National Lab. (SNL-CA), Livermore, CA (United States). Mechanics of Materials Dept.; Lipinski, Ronald J. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States). Advanced Nuclear Fuel Cycle Technology Dept.; Bignell, John L. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States). Structural and Thermal Analysis Dept.; Ulrich, G. B. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Radioisotope Power Systems Program; George, E. P. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Radioisotope Power Systems Program

2014-06-01

Iridium alloys have superior strength and ductility at elevated temperatures, making them useful as structural materials for certain high-temperature applications. However, experimental data on their high-temperature high-strain-rate performance are needed for understanding high-speed impacts in severe elevated-temperature environments. Kolsky bars (also called split Hopkinson bars) have been extensively employed for high-strain-rate characterization of materials at room temperature, but it has been challenging to adapt them for the measurement of dynamic properties at high temperatures. Current high-temperature Kolsky compression bar techniques are not capable of obtaining satisfactory high-temperature high-strain-rate stress-strain response of thin iridium specimens investigated in this study. We analyzed the difficulties encountered in high-temperature Kolsky compression bar testing of thin iridium alloy specimens. Appropriate modifications were made to the current high-temperature Kolsky compression bar technique to obtain reliable compressive stress-strain response of an iridium alloy at high strain rates (300 – 10000 s^-1) and temperatures (750°C and 1030°C). Uncertainties in such high-temperature high-strain-rate experiments on thin iridium specimens were also analyzed. The compressive stress-strain response of the iridium alloy showed significant sensitivity to strain rate and temperature.

Aluminum alloy production for the reinforcement of the CMS conductor

CERN Document Server

Sequeira-Lopes-Tavares, S; Campi, D; Curé, B; Horváth, I L; Riboni, P; Sgobba, Stefano; Smith, R P

2002-01-01

The Compact Muon Solenoid (CMS) is one of the general-purpose detectors to be provided for the Large Hadron Collider (LHC) project at CERN. The design field of the CMS superconducting magnet is 4 T, the magnetic length is 12.5 m and the free bore is 6 m. To reinforce the high-purity (99.998%) Al-stabilized conductor of the magnet against the magnetic loadings experienced during operation at 4.2 K, two continuous sections of Al-alloy (AA) reinforcement are Electron Beam (EB) welded to it. The reinforcements have a section of 24*18 mm and are produced in continuous 2.55 km lengths. The alloy EN AW-6082 has been selected for the reinforcement due to its excellent extrudability, high strength in the precipitation hardened states, high toughness and strength at cryogenic temperature and good EB weldability. Each of the continuous lengths of the reinforcement is extruded billet on billet and press quenched on-line from the extrusion temperature in an industrial extrusion plant. In order to insure the ready EB welda...

Comparison of Response Characteristics of High-Purity Germanium Detectors using Analog Versus Digital Processing

International Nuclear Information System (INIS)

Luke, S J; Raschke, K

2004-01-01

In this article we will discuss some of the results of the response characteristics of High Purity germanium detectors using analog versus digital processing of the signals that are outputted from the detector. The discussion will focus on whether or not there is a significant difference in the response of the detector with digital electronics that it limits the ability of the detection system to get reasonable gamma ray spectrometric results. Particularly, whether or not the performance of the analysis code Pu600 is compromised

Interaction of alumina with liquid Pb{sub 83}Li{sub 17} alloy

Energy Technology Data Exchange (ETDEWEB)

Jain, Uttam, E-mail: uttamj@barc.gov.in [Fusion Reactor Materials Section, Bhabha Atomic Research Centre, Mumbai 400085 (India); Mukherjee, Abhishek; Sonak, Sagar; Kumar, Sanjay [Fusion Reactor Materials Section, Bhabha Atomic Research Centre, Mumbai 400085 (India); Mishra, Ratikant [Chemistry Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Krishnamurthy, Nagaiyar [Fusion Reactor Materials Section, Bhabha Atomic Research Centre, Mumbai 400085 (India)

2014-11-15

Highlights: • The role of oxygen in the interaction of alumina with Pb{sub 83}Li{sub 17} alloy was studied. • Li of Pb{sub 83}Li{sub 17} alloy undergoes oxidation even in flowing high pure argon atmosphere. • It was seen that alumina reacts with Pb{sub 83}Li{sub 17} alloy at 550 °C to form LiAlO{sub 2} compound. • The reaction is rapid in the presence of oxygen and happens more slowly in the presence of flowing argon. - Abstract: Eutectic lead lithium (Pb{sub 83}Li{sub 17}) alloy is being considered a coolant, neutron multiplier and tritium breeder for International Thermonuclear Experimental Reactor (ITER) and Fusion Power Reactors (FPR). In order to reduce the magneto-hydrodynamic drag (MHD) and to prevent corrosion of structural materials due to the flow of lead lithium (Pb{sub 83}Li{sub 17}) alloy, alumina (Al{sub 2}O{sub 3}) is proposed as a candidate ceramic coating material. Interaction of liquid Pb{sub 83}Li{sub 17} alloy with Al{sub 2}O{sub 3} at the operating temperature of these reactors is therefore an important issue. The present paper deals with the characterization of Pb{sub 83}Li{sub 17} alloy and its interaction with Al{sub 2}O{sub 3} at the reactor operating temperature. The interaction was studied using EPMA, XRD and thermal analysis technique. The result indicates that alumina can interact with Pb{sub 83}Li{sub 17} alloy at 550 °C even in high purity argon atmosphere. The role of oxygen in the interaction process has also been discussed.

Hydrofluoric Acid Corrosion Study of High-Alloy Materials

Energy Technology Data Exchange (ETDEWEB)

Osborne, P.E.

2002-09-11

A corrosion study involving high-alloy materials and concentrated hydrofluoric acid (HF) was conducted in support of the Molten Salt Reactor Experiment Conversion Project (CP). The purpose of the test was to obtain a greater understanding of the corrosion rates of materials of construction currently used in the CP vs those of proposed replacement parts. Results of the study will help formulate a change-out schedule for CP parts. The CP will convert slightly less than 40 kg of {sup 233}U from a gas (UF{sub 6}) sorbed on sodium fluoride pellets to a more stable oxide (U{sub 3}O{sub 8}). One by-product of the conversion is the formation of concentrated HF. Six moles of highly corrosive HF are produced for each mole of UF{sub 6} converted. This acid is particularly corrosive to most metals, elastomers, and silica-containing materials. A common impurity found in {sup 233}U is {sup 232}U. This impurity isotope has several daughters that make the handling of the {sup 233}U difficult. Traps of {sup 233}U may have radiation fields of up to 400 R at contact, a situation that makes the process of changing valves or working on the CP more challenging. It is also for this reason that a comprehensive part change-out schedule must be established. Laboratory experiments involving the repeated transfer of HF through 1/2-in. metal tubing and valves have proven difficult due to the corrosivity of the HF upon contact with all wetted parts. Each batch of HF is approximately 1.5 L of 33 wt% HF and is transferred most often as a vapor under vacuum and at temperatures of up to 250 C. Materials used in the HF side of the CP include Hastelloy C-276 and Monel 400 tubing, Haynes 230 and alloy C-276 vessels, and alloy 400 valve bodies with Inconel (alloy 600) bellows. The chemical compositions of the metals discussed in this report are displayed in Table 1. Of particular concern are the almost 30 vendor-supplied UG valves that have the potential for exposure to HF. These valves have been

Creep property of carbon and nitrogen free high strength new alloys

Energy Technology Data Exchange (ETDEWEB)

Muneki, S., E-mail: ABE.Fujio@nims.go.j [Heat Resistant Design Group, Steel Research Center, National Institute for Materials Science (Japan); Okubo, H.; Abe, F. [Heat Resistant Design Group, Steel Research Center, National Institute for Materials Science (Japan)

2010-06-15

The carbon and nitrogen free new alloys which were composed of supersaturated martensitic microstructure with high dislocation density before the creep test have been investigated systematically. These alloys were produced from the new approach which raised creep strength by the utilization of the reverse transformed austenite phase as a matrix and intermetallic compounds such as Laves phase and mu-phase as precipitates during heating before the creep test. It is important that these alloys are independent of any carbides and nitrides as strengthening factors. The high temperature creep test over 700 {sup o}C exceeds 50,000 h, and the test is continuous. Creep behavior of the alloys is found to be different from that of the conventional high-Cr ferritic steels. The addition of boron to the alloy pulled the recrystallization temperature up in the high temperature, and it became a creep test in the un-recrystallization condition, and the creep property of high temperature over 700 {sup o}C was drastically improved. The minimum creep rates of Fe-Ni alloys at 700 {sup o}C are found to be much lower than those of the conventional high Cr ferritic heat resistant steels, which is due to fine dispersion strengthening useful even at 700 {sup o}C in these alloys. As a result it became clear that the value for 100,000 h was exceeded at 700 {sup o}C and 100 MPa calculated from the Larson-Miller parameter at C = 20.

The method for production of high purity carrier free ortophosphoric acid labeled with isotopes Phosphorus-32 and Phosphorus-33

International Nuclear Information System (INIS)

Abdukayumov, M.N.; Abdusalyamov, A.N.; Chistyakov, P.G.; Yuldashev, B.S.

2001-01-01

Extensive application for various radioactive isotopes was found in an extremity of the 20-Th century in a science and production. Labeled compounds are used with growing effectiveness in a molecular biology, gene engineering, medicine and other areas. Phosphorus-32 and Phosphorus-33 isotopes as a different labeled compounds that are used mainly in molecular biology are produced at the Radiopreparat enterprise of the Institute of Nuclear Physics of Academy of Sciences of Uzbekistan Republic. The quality of labeled preparations is very high. The specifications for above mentioned preparations corresponds to demands most of customers in different countries. P-32 or P-33 labeled orthophosphoric acid has high radiochemical purity (more than 99 %) and specific radioactivity close to theoretical. Orthophosphoric acid prepared by the described above method has radiochemical purity about 95 % and output of the target product 99%

Minor-alloyed Cu-Ni-Si alloys with high hardness and electric conductivity designed by a cluster formula approach

Directory of Open Access Journals (Sweden)

Dongmei Li

2017-08-01

Full Text Available Cu-Ni-Si alloys are widely used due to their good electrical conductivities in combination with high strength and hardness. In the present work, minor-alloying with M = (Cr, Fe, Mo, Zr was conducted for the objective of further improving their hardness while maintaining their conductivity level. A cluster-plus-glue-atom model was introduced to design the compositions of M-alloyed Cu-Ni-Si alloys, in which an ideal composition formula [(Ni,Si,M-Cu12]Cu3 (molar proportion was proposed. To guarantee the complete precipitation of solute elements in fine δ-Ni2Si precipitates, the atomic ratio of (Ni,M/Si was set as 2/1. Thus the designed alloy series of Cu93.75(Ni/Zr3.75Si2.08(Cr/Fe/Mo0.42 (at% were arc-melted into ingots under argon atmosphere, and solid-solutioned at 950 °C for 1 h plus water quenching and then aged at 450 °C for different hours. The experimental results showed that these designed alloys exhibit high hardness (HV > 1.7 GPa and good electrical conductivities (≥ 35% IACS. Specifically, the quinary Cu93.75Ni3.54Si2.08(Cr/Fe0.42Zr0.21 alloys (Cu-3.32Ni-0.93Si-0.37(Cr/Fe−0.30Zr wt% possess both a high hardness with HV = 2.5–2.7 GPa, comparable to the high-strength KLFA85 alloy (Cu-3.2Ni-0.7Si-1.1Zn wt%, HV = 2.548 GPa, and a good electrical conductivity (35–36% IACS.

Mechanical properties and microstructure of copper alloys and copper alloy-stainless steel laminates for fusion reactor high heat flux applications

Science.gov (United States)

Leedy, Kevin Daniel

A select group of copper alloys and bonded copper alloy-stainless steel panels are under consideration for heat sink applications in first wall and divertor structures of a planned thermonuclear fusion reactor. Because these materials must retain high strengths and withstand high heat fluxes, their material properties and microstructures must be well understood. Candidate copper alloys include precipitate strengthened CuNiBe and CuCrZr and dispersion strengthened Cu-Alsb2Osb3 (CuAl25). In this study, uniaxial mechanical fatigue tests were conducted on bulk copper alloy materials at temperatures up to 500sp°C in air and vacuum environments. Based on standardized mechanical properties measurement techniques, a series of tests were also implemented to characterize copper alloy-316L stainless steel joints produced by hot isostatic pressing or by explosive bonding. The correlation between mechanical properties and the microstructure of fatigued copper alloys and the interface of copper alloy-stainless steel laminates was examined. Commercial grades of these alloys were used to maintain a degree of standardization in the materials testing. The commercial alloys used were OMG Americas Glidcop CuAl25 and CuAl15; Brush Wellman Hycon 3HP and Trefimetaux CuNiBe; and Kabelmetal Elbrodur and Trefimetaux CuCrZr. CuAl25 and CuNiBe alloys possessed the best combination of fatigue resistance and microstructural stability. The CuAl25 alloy showed only minimal microstructural changes following fatigue while the CuNiBe alloy consistently exhibited the highest fatigue strength. Transmission electron microscopy observations revealed that small matrix grain sizes and high densities of submicron strengthening phases promoted homogeneous slip deformation in the copper alloys. Thus, highly organized fatigue dislocation structure formation, as commonly found in oxygen-free high conductivity Cu, was inhibited. A solid plate of CuAl25 alloy hot isostatically pressed to a 316L stainless steel

Crack initiation behavior of neutron irradiated model and commercial stainless steels in high temperature water

Energy Technology Data Exchange (ETDEWEB)

Stephenson, Kale J., E-mail: kalejs@umich.edu; Was, Gary S.

2014-01-15

Highlights: • Environmental constant extension rate tensile tests were performed on neutron irradiated steel. • Percentage of intergranular cracking quantified the cracking susceptibility. • Cracking susceptibility varied with test environment, solute addition, and cold work. • No singular microstructural change could explain increases in cracking susceptibility with irradiation dose. • The increment of yield strength due to irradiation correlated well with cracking susceptibility. -- Abstract: The objective of this study was to isolate key factors affecting the irradiation-assisted stress corrosion cracking (IASCC) susceptibility of eleven neutron-irradiated austenitic stainless steel alloys. Four commercial purity and seven high purity stainless steels were fabricated with specific changes in composition and microstructure, and irradiated in a fast reactor spectrum at 320 °C to doses between 4.4 and 47.5 dpa. Constant extension rate tensile (CERT) tests were performed in normal water chemistry (NWC), hydrogen water chemistry (HWC), or primary water (PW) environments to isolate the effects of environment, elemental solute addition, alloy purity, alloy heat, alloy type, cold work, and irradiation dose. The irradiated alloys showed a wide variation in IASCC susceptibility, as measured by the relative changes in mechanical properties and crack morphology. Cracking susceptibility measured by %IG was enhanced in oxidizing environments, although testing in the lowest potential environment caused an increase in surface crack density. Alloys containing solute addition of Ni or Ni + Cr exhibited no IASCC. Susceptibility was reduced in materials cold worked prior to irradiation, and increased with increasing irradiation dose. Irradiation-induced hardening was accounted for by the dislocation loop microstructure, however no relation between crack initiation and radiation hardening was found.

Alloying behavior of iron, gold and silver in AlCoCrCuNi-based equimolar high-entropy alloys

International Nuclear Information System (INIS)

Hsu, U.S.; Hung, U.D.; Yeh, J.W.; Chen, S.K.; Huang, Y.S.; Yang, C.C.

2007-01-01

High-entropy alloys are newly developed alloys that are composed, by definition, of at least five principal elements with concentrations in the range of 5-35 at.%. Therefore, the alloying behavior of any given principal element is significantly affected by all the other principal elements present. In order to elucidate this further, the influence of iron, silver and gold addition on the microstructure and hardness of AlCoCrCuNi-based equimolar alloys has been examined. The as-cast AlCoCrCuNi base alloy is found to have a dendritic structure, of which only solid solution FCC and BCC phases can be observed. The BCC dendrite has a chemical composition close to that of the nominal alloy, with a deficiency in copper however, which is found to segregate and form a FCC Cu-rich interdendrite. The microstructure of the iron containing alloys is similar to that of the base alloy. It is found that both of these aforementioned alloys have hardnesses of about 420 HV, which is equated to their similar microstructures. The as-cast ingot forms two layers of distinct composition with the addition of silver. These layers, which are gold and silver in color, are determined to have a hypoeutectic Ag-Cu composition and a multielement mixture of the other principal elements, respectively. This indicates the chemical incompatibility of silver with the other principal elements. The hardnesses of the gold (104 HV) and silver layers (451 HV) are the lowest and highest of the alloy systems studied. This is attributed to the hypoeutectic Ag-Cu composition of the former and the reduced copper content of the latter. Only multielement mixtures, i.e. without copper segregation, form in the gold containing alloy. Thus, it may be said that gold acts as a 'mixing agent' between copper and the other elements. Although several of the atom pairs in the gold containing alloy have positive enthalpies, thermodynamic considerations show that the high entropy contribution is sufficient to counterbalance

Mechanical properties of aluminium-uranium alloy and aluminium commercially pure at several temperatures

International Nuclear Information System (INIS)

Quadros, N.F. de.

1976-01-01

The mechanical properties of Ai-U (18,4 wt %) alloy with and without heat treatment were determined, and they were compared with the mechanical properties of aluminum alloy of commercial purity, AI-1100, at tempiratures of 25, 500, 550 and 600 0 C, the changes of both the yield point stress and the ultimate tensile strength as a function of temperature may be described through two emperical relationships. A fractography study was also made [pt

The rapid synthesis of high purity [{sup 18}F]butyrophenone neuroleptics from nitro precursors for PET study

Energy Technology Data Exchange (ETDEWEB)

Hashizume, Kazunari; Hashimoto, Naoto; Kato, Hiroo; Cork, D G; Miyake, Yoshihiro [National Cardiovascular Center, Suita, Osaka (Japan)

1995-04-01

We have completed rapid syntheses of [{sup 18}F]butyrophenone neuroleptics ([{sup 18}F]haloperidol and [{sup 18}F]spiperone) from their nitro precursors in high radiochemical yields (up to 21%) by combining a one-step nitro-fluoro exchange reaction and a novel high performance liquid chromatography (HPLC) separation method. The synthesis time was ca. 95 min and both the radiochemical and chemical purities of the labeled products were over 99%. (author).

Effect of the leaching of Ru-Se-Fe and Ru-Mo-Fe obtained by mechanical alloying on electrocatalytical behavior for the oxygen reduction reaction

International Nuclear Information System (INIS)

Ezeta, A.; Arce, E.M.; Solorza, O.; Gonzalez, R.G.; Dorantes, H.

2009-01-01

In the present work, Ru-Se-Fe and Ru-Mo-Fe alloyed nanoparticles were synthesized from high purity powders (Ru, Se and Mo) by means of the high-energy mechanical alloying. Fe was integrated to the alloys because of the erosion of the mill balls. The ORR electrocatalytic performance of the alloys (lixiviated or not) was evaluated in a rotating disc electrode (RDE) at room temperature. X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used for the structure characterization of the materials. Small-particle clusters with granular morphology and nanometric sizes were obtained in all the cases. According to the Tafel parameters from the RDE results, a first order ORR is present in both electrocatalytic systems through a 4e - global multielectron transference to form water: O 2 + 4H + + e - → H 2 O. The electrocatalytic activity showed that the mechanical alloying enabled to obtain nanoparticle electrocatalysts with good ORR performance. Lixiviation of the mechanical alloying powders not improves the catalytical responses.

High-strength shape memory steels alloyed with nitrogen

International Nuclear Information System (INIS)

Ullakko, K.; Jakovenko, P.T.; Gavriljuk, V.G.

1996-01-01

Since shape memory effect in Fe-Mn-Si systems was observed, increasing attention has been paid to iron based shape memory alloys due to their great technological potential. Properties of Fe-Mn-Si shape memory alloys have been improved by alloying with Cr, Ni, Co and C. A significant improvement on shape memory, mechanical and corrosion properties is attained by introducing nitrogen in Fe-Mn-Si based systems. By increasing the nitrogen content, strength of the matrix increases and the stacking fault energy decreases, which promote the formation of stress induced martensite and decrease permanent slip. The present authors have shown that nitrogen alloyed shape memory steels exhibit recoverable strains of 2.5--4.2% and recovery stresses of 330 MPa. In some cases, stresses over 700 MPa were attained at room temperature after cooling a constrained sample. Yield strengths of these steels can be as high as 1,100 MPa and tensile strengths over 1,500 MPa with elongations of 30%. In the present study, effect of nitrogen alloying on shape memory and mechanical properties of Fe-Mn-Si, Fe-Mn-Si-Cr-Ni and Fe-Mn-Cr-Ni-V alloys is studied. Nitrogen alloying is shown to exhibit a beneficial effect on shape memory properties and strength of these steels

High-temperature deformation of a mechanically alloyed niobium-yttria alloy

International Nuclear Information System (INIS)

Chou, I.; Koss, D.A.; Howell, P.R.; Ramani, A.S.

1997-01-01

Mechanical alloying (MA) and hot isostatic pressing have been used to process two Nb alloys containing yttria particles, Nb-2 vol.%Y 2 O 3 and Nb-10 vol.%Y 2 O 3 . Similar to some thermomechanically processed nickel-based alloys, both alloys exhibit partially recrystallized microstructures, consisting of a 'necklace' of small recrystallized grains surrounding much larger but isolated, unrecrystallized, cold-worked grains. Hot compression tests from 1049 to 1347 C (0.5-0.6T MP ) of the 10% Y 2 O 3 alloy show that MA material possesses a much higher yield and creep strength than its powder-blended, fully recrystallized counterpart. In fact, the density-compensated specific yield strength of the MA Nb-10Y 2 O 3 exceeds that of currently available commercial Nb alloys. (orig.)

A Critical Review of High Entropy Alloys and Related Concepts (Postprint)

Science.gov (United States)

2016-10-21

1301e1305. [306] C. Huang, Y.Z. Zhang, R. Vilar, J.Y. Shen, Dry sliding wear behavior of laser clad TiVCrAlSi high entropy alloy coatings on Ti-6Al...Res. 652e654 (2013) 1115e1118. [313] C. Huang, Y. Zhang, J. Shen, R. Vilar, Thermal stability and oxidation resis- tance of laser clad TiVCrAlSi high...Section 7.1.3). Finally, it is not always true that SS alloys are ductile. Well-known examples include b- titanium alloys, a- titanium alloys with small

Vanadium alloy membranes for high hydrogen permeability and suppressed hydrogen embrittlement

International Nuclear Information System (INIS)

Kim, Kwang Hee; Park, Hyeon Cheol; Lee, Jaeho; Cho, Eunseog; Lee, Sang Mock

2013-01-01

The structural properties and hydrogen permeation characteristics of ternary vanadium–iron–aluminum (V–Fe–Al) alloy were investigated. To achieve not only high hydrogen permeability but also strong resistance to hydrogen embrittlement, the alloy composition was modulated to show high hydrogen diffusivity but reduced hydrogen solubility. We demonstrated that matching the lattice constant to the value of pure V by co-alloying lattice-contracting and lattice-expanding elements was quite effective in maintaining high hydrogen diffusivity of pure V

Corrosion properties of cladding materials from Zr1Nb alloy

International Nuclear Information System (INIS)

Kloc, K.; Kosler, S.

1975-01-01

The corrosion behaviour was observed of the Zr1Nb alloy in hot water and superheated steam and the effects of impurity content, of the purity of the corrosion environment and of the heat treatment of the alloy were studied on the alloy corrosion resistance. Also studied were the absorption of hydrogen by the alloy and its behaviour in reactor situations. It was ascertained that the alloy has a good corrosion resistance up to a temperature of 350 degC. The corrosion resistance is reduced by the presence of nitrogen above 50 to 70 ppm and of carbon above 50 to 90 ppm. A graphic representation is given of the dependence of corrosion resistance on the temperature of annealing, the nitrogen content of the alloy and the time of the action of hot water or steam, as well as the dependence of the hydrogen content in the alloy on the peripheral tension of the cladding in hot water both in non-active environment and at irradiation with a neutron flux of approximately 10 20 n/cm 2 . (J.B.)

Efficiency correction for disk sources using coaxial High-Purity Ge detectors

International Nuclear Information System (INIS)

Chatani, Hiroshi.

1993-03-01

Efficiency correction factors for disk sources were determined by making use of closed-ended coaxial High-Purity Ge (HPGe) detectors, their relative efficiencies for a 3' 'x3' ' NaI(Tl) with the 1.3 MeV γ-rays were 30 % and 10 %, respectively. Parameters for the correction by mapping method were obtained systematically, using several monoenergetic (i.e. no coincidence summing loses) γ-ray sources produced by irradiation in the Kyoto University Reactor (KUR) core. These were found out that (1) the systematics of the Gaussian fitting parameters, which were calculated using the relative efficiency distributions of HPGe, to the γ-ray energies are recognized, (2) the efficiency distributions deviate from the Gaussian distributions outside of the radii of HPGe. (3) mapping method is a practical use in satisfactory accuracy, as the results in comparison with the disk source measurements. (author)

Preparation of high-purity Pr{sup 3+} doped Ge–As–Se–In–I glasses for active mid-infrared optics

Energy Technology Data Exchange (ETDEWEB)

Karaksina, E.V.; Shiryaev, V.S., E-mail: shiryaev@ihps.nnov.ru; Kotereva, T.V.; Velmuzhov, A.P.; Ketkova, L.A.; Snopatin, G.E.

2016-09-15

The multi-stage method for the synthesis of high-purity Ge–As–Se–In–I glasses doped with Pr{sup 3+} ions is developed. It is based on the chemical distillation purification of glass-forming melt and the chemical transport reactions for purification and vacuum loading of indium. The level of purity of glasses, synthesized by this method, is higher in comparison with the traditional direct melting method for glass synthesis. The high-purity Pr{sup 3+}-doped Ge–As–Se–In and Pr{sup 3+}-doped Ge–As–Se–In–I glass samples are prepared; the optical, thermal and luminescent properties are investigated. The purest host glass samples, obtained by the multi-stage purification techniques, contain a low concentration of limiting impurities: hydrogen − ≤0.05 ppm (wt) and oxygen − ≤0.1 ppm (wt), that is, at present, the best result for multi-component chalcogenide glasses for mid-IR active fibers. The samples of Pr{sup 3+}-doped Ge–As–Se–In glass fibers have the minimum optical losses of 0.58 dB/m at the wavelength of 2.72 μm and exhibit an intense broadband luminescence in the spectral range of 3.5–5.5 μm, with a maximum shifted to longer wavelengths as compared with the bulk samples.

X-ray fluorescence determination of Sn, Sb, Pb in lead-based bearing alloys using a solution technique

Science.gov (United States)

Tian, Lunfu; Wang, Lili; Gao, Wei; Weng, Xiaodong; Liu, Jianhui; Zou, Deshuang; Dai, Yichun; Huang, Shuke

2018-03-01

For the quantitative analysis of the principal elements in lead-antimony-tin alloys, directly X-ray fluorescence (XRF) method using solid metal disks introduces considerable errors due to the microstructure inhomogeneity. To solve this problem, an aqueous solution XRF method is proposed for determining major amounts of Sb, Sn, Pb in lead-based bearing alloys. The alloy samples were dissolved by a mixture of nitric acid and tartaric acid to eliminated the effects of microstructure of these alloys on the XRF analysis. Rh Compton scattering was used as internal standard for Sb and Sn, and Bi was added as internal standard for Pb, to correct for matrix effects, instrumental and operational variations. High-purity lead, antimony and tin were used to prepare synthetic standards. Using these standards, calibration curves were constructed for the three elements after optimizing the spectrometer parameters. The method has been successfully applied to the analysis of lead-based bearing alloys and is more rapid than classical titration methods normally used. The determination results are consistent with certified values or those obtained by titrations.

Radio frequency and linearity performance of transistors using high-purity semiconducting carbon nanotubes.

Science.gov (United States)

Wang, Chuan; Badmaev, Alexander; Jooyaie, Alborz; Bao, Mingqiang; Wang, Kang L; Galatsis, Kosmas; Zhou, Chongwu

2011-05-24

This paper reports the radio frequency (RF) and linearity performance of transistors using high-purity semiconducting carbon nanotubes. High-density, uniform semiconducting nanotube networks are deposited at wafer scale using our APTES-assisted nanotube deposition technique, and RF transistors with channel lengths down to 500 nm are fabricated. We report on transistors exhibiting a cutoff frequency (f(t)) of 5 GHz and with maximum oscillation frequency (f(max)) of 1.5 GHz. Besides the cutoff frequency, the other important figure of merit for the RF transistors is the device linearity. For the first time, we report carbon nanotube RF transistor linearity metrics up to 1 GHz. Without the use of active probes to provide the high impedance termination, the measurement bandwidth is therefore not limited, and the linearity measurements can be conducted at the frequencies where the transistors are intended to be operating. We conclude that semiconducting nanotube-based transistors are potentially promising building blocks for highly linear RF electronics and circuit applications.

Fabrication high-purity Fe nanochains with near theoretical limit value of saturation magnetization of bulk Fe

Energy Technology Data Exchange (ETDEWEB)

Bian, Erkang [Henan University, Key Laboratory for Special Functional Materials of Ministry of Education (China); Xu, Yanling [Henan University, The Audit Department (China); Lou, Shiyun, E-mail: lousy@henu.edu.cn [Henan University, Key Laboratory for Special Functional Materials of Ministry of Education (China); Fu, Yunlong, E-mail: yunlongfu@dns.sxnu.edu.cn [Shanxi Normal University, School of Chemistry and Material Science (China); Zhou, Shaomin, E-mail: smzhou@henu.edu.cn [Henan University, Key Laboratory for Special Functional Materials of Ministry of Education (China)

2016-11-15

High-yield purity chain-like one-dimensional nanostructures consisting of single crystal Fe nanoparticles have been produced by using solution dispersion approach. Room temperature magnetic measurement shows that the as-fabricated Fe nanochains are ferromagnetic with a high saturation magnetization (203 emu/g) whereas the nanoparticles are single magnetic domains, which indicate that the as-synthesized products have superparamagnetism behavior with the saturation magnetization of about 28 emu/g. Maybe this results from the directional alignment of the nanoparticles. The excellent characteristic may have led to the potential applications in spin filtering, high density magnetic recording, and nanosensors.

DC Electric Arc Furnace Application for Production of Nickel-Boron Master Alloys

Science.gov (United States)

Alkan, Murat; Tasyürek, Kerem Can; Bugdayci, Mehmet; Turan, Ahmet; Yücel, Onuralp

2017-09-01

In this study, nickel-boron (Ni-B) alloys were produced via a carbothermic reduction starting from boric acid (H3BO3) with high-purity nickel oxide (NiO), charcoal, and wood chips in a direct current arc furnace. In electric arc furnace experiments, different starting mixtures were used, and their effects on the chemical compositions of the final Ni-B alloys were investigated. After the reduction and melting stages, Ni-B alloys were obtained by tapping from the bottom of the furnace. The samples from the designated areas were also taken and analyzed. The chemical composition of the final alloys and selected samples were measured with wet chemical analysis. The Ni-B alloys had a composition of up to 14.82 mass% B. The phase contents of the final alloys and selected samples were measured using x-ray diffraction (XRD). The XRD data helped predict possible reactions and reaction mechanisms. The material and energy balance calculations were made via the XRD Rietveld and chemical compositions. Nickel boride phases started to form 600 mm below the surface. The targeted NiB phase was detected at the tapping zone of the crucible (850-900 mm depth). The energy consumption was 1.84-4.29 kWh/kg, and the electrode consumption was 10-12 g/kg of raw material charged.

Sensor locations and noise reduction in high-purity batch distillation control loops

Directory of Open Access Journals (Sweden)

Oisiovici R.M.

2000-01-01

Full Text Available The influence of the sensor locations on the composition control of high-purity batch distillation columns has been investigated. Using concepts of the nonlinear control theory, an input-output linearizing controller was implemented to keep the distillate composition constant at a desired value by varying the reflux ratio. An Extended Kalman Filter was developed to estimate the compositions required in the control algorithm using temperature measurements. In the presence of measurement noise, the control performance depended greatly on the sensor locations. Placing the sensors further from the top stages reduced the detrimental effects of noise but increased the inference error. To achieve accurate composition control, both noise reduction and composition estimate accuracy should be considered in the selection of the sensor locations.

A new high-strength iron base austenitic alloy with good toughness and corrosion resistance (GE-EPRI alloy-TTL)

International Nuclear Information System (INIS)

Ganesh, S.

1989-01-01

A new high strength, iron based, austenitic alloy has been successfully developed by GE-EPRI to satisfy the strength and corrosion resistance requirements of large retaining rings for high capacity generators (>840Mw). This new alloy is a modified version of the EPRI alloy-T developed by the University of California, Berkeley, in an earlier EPRI program. It is age hardenable and has the nominal composition (weight %): 34.5 Ni, 5Cr, 3Ti, 1Nb, 1Ta, 1Mo, .5Al, .3V, .01B. This composition was selected based on detailed metallurgical and processing studies on modified versions of alloy-T. These studies helped establish the optimum processing conditions for the new alloy and enabled the successful scale-up production of three large (50-52 inch dia) test rings from a 5,000 lb VIM-VAR billet. The rings were metallurgically sound and exhibited yield strength capabilities in the range 145 to 220 ksi depending on the extent of hot/cold work induced. The test rings met or exceeded all the property goals. The above alloy can provide a good combination of strength, toughness and corrosion resistance and, through an suitable modification of chemistry or processing conditions, could be a viable candidate for high strength LWR internal applications. 3 figs

Accelerated irradiation growth of zirconium alloys

International Nuclear Information System (INIS)

Griffiths, M.; Gilbert, R.W.; Fidleris, V.

1989-01-01

This paper discusses how sponge zirconium and Zr-2.5 wt% Nb, Zircaloy, or Excel alloys all exhibit accelerated irradiation growth compared with high-purity crystal-bar zirconium for irradiation temperatures between 550 to 710 K and fluences between 0.1 to 10 x 10 25 n · m -2 (E > 1 MeV). There is generally an incubation period or fluence before the onset of accelerated or breakaway growth, which is dependent on the particular material being irradiated, its metallurgical condition before irradiation, and the irradiation temperature. Transmission electron microscopy has shown that there is a correlation between accelerated irradiation growth and the appearance of c-component vacancy loops on basal planes. Measurements in some specimens indicate that a significant fraction of the strain can be directly attributed to the loops themselves. There is considerable evidence to show that their formation is dependent both on the specimen purity and on the irradiation temperature. Materials that have a high interstitial-solute content contain c-component loops and exhibit high growth rates even at low fluences ( 2 :5 n · m -2 , E > 1 MeV). For sponge zirconium and the Zircaloys, c-component loop formation and the associated acceleration of growth (breakaway) during irradiation occurs because the intrinsic interstitial solute (mainly, oxygen, carbon and nitrogen) in the zirconium matrix is supplemented by interstitial iron, chromium, and nickel from the radiation-induced dissolution of precipitates. (author)

Work hardening characteristics in Al base alloys with 12.6 and 45 wt.% Zn

International Nuclear Information System (INIS)

Abd El-Salam, F.; Mostafa, M.M.; Wahab, L.A.; Mostafa, M.T.; Abd El-Aziz, Sh.M.

2008-01-01

The stress-strain curves were obtained for Al-Zn alloys of 12.6 wt.% Zn (alloy I) and 45 wt.% Zn (alloy II) with elements of purity (99.99). The monotonic shift of these curves towards lower flow stress and higher ductility was interrupted at the transformation temperatures 483 K (alloy I) and both 543, 603 K (alloy II). By increasing deformation temperature, Young's modulus, Y, yield and fracture stresses, σ y and σ f , respectively, fracture time, t f , the coefficient of parabolic work hardening, χ, decreased while fracture strain, ε f , and dislocation slip distance, L, increased. From the obtained X-rays diffraction patterns the lattice strain, ε, crystallite size, η, and dislocation density, ρ, were obtained at different deformation temperatures around transformation

High Temperature Mechanical Constitutive Modeling of a High-Nb TiAl Alloy

Directory of Open Access Journals (Sweden)

DONG Chengli

2018-02-01

Full Text Available Uniaxial tensile, low cycle fatigue, fatigue-creep interaction and creep experiments of a novel high-Nb TiAl alloy (i.e. Ti-45Al-8Nb-0.2W-0.2B-0.02Y (atom fraction/% were conducted at 750℃ to obtain its tested data and curves. Based on Chaboche visco-plasticity unified constitutive model, Ohno-Wang modified non-linear kinematic hardening was introduced in Chaboche constitutive model to describe the cyclic hardening/softening, and Kachanov damage was coupled in Chaboche constitutive model to characterize the accelerated creep stage. The differential equations of the constitutive model discretized by explicit Euler method were compiled in to ABAQUS/UMAT to simulate the mechanical behavior of high-Nb TiAl alloy at different test conditions. The results show that Chaboche visco-plasticity unified constitutive model considering both Ohno-Wang modified non-linear kinematic hardening and Kachanov damage is able to simulate the uniaxial tensile, low cycle fatigue, fatigue-creep interaction and creep behavior of high-Nb TiAl alloy and has high accuracy.

Excessively High Vapor Pressure of Al-based Amorphous Alloys

Directory of Open Access Journals (Sweden)

Jae Im Jeong

2015-10-01

Full Text Available Aluminum-based amorphous alloys exhibited an abnormally high vapor pressure at their approximate glass transition temperatures. The vapor pressure was confirmed by the formation of Al nanocrystallites from condensation, which was attributed to weight loss of the amorphous alloys. The amount of weight loss varied with the amorphous alloy compositions and was inversely proportional to their glass-forming ability. The vapor pressure of the amorphous alloys around 573 K was close to the vapor pressure of crystalline Al near its melting temperature, 873 K. Our results strongly suggest the possibility of fabricating nanocrystallites or thin films by evaporation at low temperatures.

Corrosion of high-density sintered tungsten alloys. Part 2

International Nuclear Information System (INIS)

Batten, J.J.; Moore, B.T.

1988-12-01

The behaviour of four high-density sintered tungsten alloys has been evluated and compared with that of pure tungsten. Rates of corrosion during the cyclic humidity and the salt mist tests were ascertained from weight loss measurements. Insight into the corrosion mechanism was gained from the nature of the corrosion products and an examination of the corroded surfaces. In the tests, the alloy 95% W, 2.5% Ni, 1.5% Fe was the most corrosion resistant. The data showed that copper as an alloying element accelerates corrosion of tungsten alloys. Both attack on the tungsten particles and the binder phase were observed together with tungsten grain loss. 6 refs., 3 tabs.,

Analysis of the strain-aging phenomena in high purity niobium: competition between hardening and recovery

International Nuclear Information System (INIS)

Andreone, C.; Cizeron, G.; Larere, A.

1981-01-01

The strain-aging phenomena in high purity niobium were studied using tensile tests. Four parameters were considered which characterize the yield point, the permanent hardening, the recovery and the apparent yield stress. Five successive steps can be distinguished from the changes in these parameters with changes in the aging temperature. The detailed analysis of the phenomena involved concerns mainly the locking of dislocations by first- and second-type segregations and the opposite effect of reorganization of the dislocation network. (Auth.)

Cross Purposes: Love and Purity at a Puerto Rican Protestant High School

Science.gov (United States)

Seale-Collazo, James

2013-01-01

A "native" Christian ethnographer finds religious education at this church-sponsored school to pursue two distinct, and occasionally conflicting, curricula: "love" and "purity." The curriculum of love draws on what Turner called liminality and communitas in an effort to promote spiritual "encounters with…

High temperature mechanical forming of Mg alloys

International Nuclear Information System (INIS)

Mwembela, A.; McQueen, H.J.; Myshlyaev, M.

2002-01-01

Mg alloys are hot worked in the range 180-450 o C and 0.0-10 s -1 ; the present project data are compared with a wide selection of published results. The flow stresses and their dependence on temperature and strain rate are fairly similar to simple Al alloys: however, the hot ductility is much lower (≤3 in torsion). Twinning plays a significant role in Mg alloys almost independently of temperature; the twins initiate at low strains in grains poorly oriented for basal slip and in consequence become well disposed for such slip. As T rises, there is increasing formation of subgrains that spread toward the grain centers from grain and twin boundaries: this is indicative of stress concentrations inducing non-basal sup which helps provide the geometrically necessary dislocations. Above about 240 o C, dynamic (DRX) nucleates at grain and twin boundaries, preferentially at intersections; this again is evidence of non-basal slip that provides the highly misoriented cells. The boundaries in which further strain concentrates producing further DRX. The microstructure remains very heterogeneous compared to the uniform dynamically recovered substructure in Al alloys, thus giving rise to the reduced ductility. These results are employed to interpret the mechanical and microstructural behavior of Mg alloys in extrusion, rolling and forging. (author)

Isothermal oxidation behavior of ternary Zr-Nb-Y alloys at high temperature

Energy Technology Data Exchange (ETDEWEB)

Prajitno, Djoko Hadi, E-mail: djokohp@batan.go.id [Research Center for Nuclear Materials and Radiometry, Jl. Tamansari 71, Bandung 40132 (Indonesia); Soepriyanto, Syoni; Basuki, Eddy Agus [Metallurgy Engineering, Institute Technology Bandung, Jl. Ganesha 10, Bandung 40132 (Indonesia); Wiryolukito, Slameto [Materials Engineering, Institute Technology Bandung, Jl. Ganesha 10, Bandung 40132 (Indonesia)

2014-03-24

The effect of yttrium content on isothermal oxidation behavior of Zr-2,5%Nb-0,5%Y, Zr-2,5%Nb-1%Y Zr-2,5%Nb-1,5%Y alloy at high temperature has been studied. High temperature oxidation carried out at tube furnace in air at 600,700 and 800°C for 1 hour. Optical microscope is used for microstructure characterization of the alloy. Oxidized and un oxidized specimen was characterized by x-ray diffraction. In this study, kinetic oxidation of Zr-2,5%Nb with different Y content at high temperature has also been studied. Characterization by optical microscope showed that microstructure of Zr-Nb-Y alloys relatively unchanged and showed equiaxed microstructure. X-ray diffraction of the alloys depicted that the oxide scale formed during oxidation of zirconium alloys is monoclinic ZrO2 while unoxidised alloy showed two phase α and β phase. SEM-EDS examination shows that depletion of Zr composition took place under the oxide layer. Kinetic rate of oxidation of zirconium alloy showed that increasing oxidation temperature will increase oxidation rate but increasing yttrium content in the alloys will decrease oxidation rate.

Sorption-enhanced water gas shift reaction for high-purity hydrogen production: Application of a Na-Mg double salt-based sorbent and the divided section packing concept

International Nuclear Information System (INIS)

Lee, Chan Hyun; Lee, Ki Bong

2017-01-01

Highlights: •Na-Mg double salt-based sorbent was used for high-temperature CO 2 sorption. •Divided section packing concept was applied to the SE-WGS reaction. •High-purity H 2 was produced from the SE-WGS reaction with divided section packing. •High-purity H 2 productivity could be further enhanced by modifying packing method. -- Abstract: Hydrogen is considered a promising environmentally benign energy carrier because it has high energy density and produces no pollutants when it is converted into other types of energy. The sorption-enhanced water gas shift (SE-WGS) reaction, where the catalytic WGS reaction and byproduct CO 2 removal are carried out simultaneously in a single reactor, has received considerable attention as a novel method for high-purity hydrogen production. Since the high-purity hydrogen productivity of the SE-WGS reaction is largely dependent on the performance of the CO 2 sorbent, the development of sorbents having high CO 2 sorption capacity is crucial. Recently, a Na-Mg double salt-based sorbent has been considered for high-temperature CO 2 capture since it has been reported to have a high sorption capacity and fast sorption kinetics. In this study, the SE-WGS reaction was experimentally demonstrated using a commercial catalyst and a Na-Mg double salt-based sorbent. However, the SE-WGS reaction with a one-body hybrid solid, a physical admixture of catalyst and sorbent, showed poor reactivity and reduced CO 2 sorption uptake. As a result, a divided section packing concept was suggested as a solution. In the divided section packing method, the degree of mixing for the catalyst and sorbent in a column can be controlled by the number of sections. High-purity hydrogen (<10 ppm CO) was produced directly from the SE-WGS reaction with divided section packing, and the hydrogen productivity was further improved when the reactor column was divided into more sections and packed with more sorbent.

The determination of minor amounts of rare earth elements in high purity earth oxides by HPLC/IDMS

International Nuclear Information System (INIS)

Stijfhoorn, D.E.; Stray, H.; Hjelmseth, H.

1991-05-01

Since the early seventies isotopic dilution mass spectrometry (IDMS) has been used at Institutt for energiteknikk, Kjeller, Norway for determination and certification of rare earth elements in high purity Y 2 O 3 . These lanthanides have, during the last few decades, become more widely used in highly specialized technology. High purity, quality 4 N (99.99%) or even 5 N materials are needed for phosphors, lasers, optical fibers, X-ray films, and in contrast fluids for magnetic resonance imaging (MRI). However, in a matrix constisting primarily of a single lanthanide, IDMS alone will not be effective due to isobaric interferences from the main elements or the mono-oxides formed in the ion source. On the other hand, high performance liquid chromatography (HPLC) may be used, but the detection limit will be in the order of 5 to 10 ppm/W. In this work a combination of HPLC and IDMS has been used to lower the detection limit to 1 ppm/W, where the sample is spiked before separation by HPLC, followed by IDMS analysis of the HPLC- fractions. In some cases the HPLC-process has to be repeated to remove the main element completly. Results are presented for Dy 2 O 3 and Nd 2 O 3 , but similar separating procedures can be applied for other rare earth oxides. 3 refs., 2 figs. 2 tabs

Some aspects of anelastic and microplastic creep of pure Al and two Al-alloys

Energy Technology Data Exchange (ETDEWEB)

Sgobba, S. (Lab. de Metallurgie Mecanique, Dept. des Materiaux, Ecole Polytechnique Federale de Lausanne (Switzerland)); Kuenzi, H.U. (Lab. de Metallurgie Mecanique, Dept. des Materiaux, Ecole Polytechnique Federale de Lausanne (Switzerland)); Ilschner, B. (Lab. de Metallurgie Mecanique, Dept. des Materiaux, Ecole Polytechnique Federale de Lausanne (Switzerland))

1993-11-01

Anelastic creep of pure Al, commercial Al-Cu and a binary Al-Cu alloy has been measured at room temperature by means of a high resolution laser interferometer. The irreversible component of the deformation was also quantified from measurements of the anelastic creep recovery. The dependence of the deformation-time curves on thermal treatment and cold work is analyzed. The mechanisms responsible for the room temperature anelastic creep are discussed. Materials loaded below their elastic limit can present either a pure anelastic behavior (commercial Al-Cu) or additional viscoelastic creep (pure Al, high purity Al-Cu). For commercial Al-Cu, the presence of an irreversible deformation appears to be mainly related to the state of the surface. A viscoelastic after effect has been measured for this alloy after a Cu-electroplating treatment. As a typical result for room temperature creep, the irreversible deformation depends logarithmically on load time. (orig.).

Some aspects of anelastic and microplastic creep of pure Al and two Al-alloys

International Nuclear Information System (INIS)

Sgobba, S.; Kuenzi, H.U.; Ilschner, B.

1993-01-01

Anelastic creep of pure Al, commercial Al-Cu and a binary Al-Cu alloy has been measured at room temperature by means of a high resolution laser interferometer. The irreversible component of the deformation was also quantified from measurements of the anelastic creep recovery. The dependence of the deformation-time curves on thermal treatment and cold work is analyzed. The mechanisms responsible for the room temperature anelastic creep are discussed. Materials loaded below their elastic limit can present either a pure anelastic behavior (commercial Al-Cu) or additional viscoelastic creep (pure Al, high purity Al-Cu). For commercial Al-Cu, the presence of an irreversible deformation appears to be mainly related to the state of the surface. A viscoelastic after effect has been measured for this alloy after a Cu-electroplating treatment. As a typical result for room temperature creep, the irreversible deformation depends logarithmically on load time. (orig.)

Purity and adulterant analysis of crack seizures in Brazil.

Science.gov (United States)

Fukushima, André R; Carvalho, Virginia M; Carvalho, Débora G; Diaz, Ernesto; Bustillos, Jose Oscar William Vega; Spinosa, Helenice de S; Chasin, Alice A M

2014-10-01

Cocaine represents a serious problem to society. Smoked cocaine is very addictive and it is frequently associated with violence and health issues. Knowledge of the purity and adulterants present in seized cocaine, as well as variations in drug characteristics are useful to identify drug source and estimate health impact. No data are available regarding smoked cocaine composition in most countries, and the smoked form is increasing in the Brazilian market. The purpose of the present study is to contribute to the current knowledge on the status of crack cocaine seized samples on the illicit market by the police of São Paulo. Thus, 404 samples obtained from street seizures conducted by the police were examined. The specimens were macroscopically characterized by color, form, odor, purity, and adulterant type, as well as smoke composition. Samples were screened for cocaine using modified Scott test and thin-layer chromatographic (TLC) technique. Analyses of purity and adulterants were performed with gas chromatography equipped with flame ionization detector (GC-FID). Additionally, smoke composition was analyzed by GC-mass spectrometry (MS), after samples burning. Samples showed different colors and forms, the majority of which is yellow (74.0%) or white (20.0%). Samples free of adulterants represented 76.3% of the total. Mean purity of the analyzed drug was 71.3%. Crack cocaine presented no correlations between macroscopic characteristics and purity. Smoke analysis showed compounds found also in the degradation of diesel and gasoline. Therefore, the drug marketed as crack cocaine in São Paulo has similar characteristics to coca paste. High purity can represent a greater risk of dependency and smoke compounds are possibly worsening drug health impact. Copyright © 2014 Elsevier Ireland Ltd. All rights reserved.

Determination of uranium in natural waters and high-purity aluminum by flow-injection on-line preconcentration and ICP-MS detection

International Nuclear Information System (INIS)

Seki, Tatsuya; Oguma, Koichi

2004-01-01

A flow injection method has been developed for the determination of uranium is natural waters and high-purity aluminum by use of on-line preconcentration on a U/TEVA TM column and ICP-MS detection. The sample solution prepared as a nitric acid solution in 3 mol l -1 was passed through the U/TEVA TM column to collect uranium and uranium adsorbed was eluted with 0.1 mol l -1 nitric acid. The effluent was introduced directly into the nebulizer of the ICP-MS and 238 U was measured. The detection limit, calculated as 3-times the standard deviation of the background noise, was 3pg and the sample throughput was about 10 per hour. The proposed method was successfully applied to the determination of uranium in river-water reference materials, a seawater reference material and high-purity aluminum reference materials. (author)

Development of a facility for the recovery of high-purity hydrogen from coke oven gas by pressure swing adsorption

Energy Technology Data Exchange (ETDEWEB)

Nakamura, M; Saida, K; Uenoyama, K; Sugishita, M; Imokawa, K

1985-01-01

This paper reports 1) a pressure swing adsorption (PSA) system comprising three towers, each packed with three different adsorbents; and 2) studies of the application of this system to the recovery of high-purity hydrogen from coke oven gas. Running the adsorption plant at 35 C and 9.5 kg/cm/sup 2/ gives optimum operating stability and economy. In addition, an optimum time cycle for the three-tower system has been developed. Gas from the PSA equipment proper still contains traces of oxygen. This is removed in a further tower packed with Pd catalyst. The ultimate recovery of hydrogen is closely related to its concentration in the raw coke oven gas and to the degree of purity attained. 3 references.

Surface characterization for high purity Fe-Cr alloys

International Nuclear Information System (INIS)

Iwai, H.; Oiwa, R.; Takaki, S.; Abiko, K.

1995-01-01

Fe-50mass%Cr was prepared in a cold crucible furnace with induction heating, then refined by floating-zone melting (FZM). The chemistries on the surface before and after FZM were compared by XPS measurement. C and O were observed on top surfaces both before and after as a hydrocarbon, carbonyl group and carboxyl group which are adsorbed chemical components. The other impurities were observed on the surface in both cases; however, the number and level of impurities on the surface after FZM were much larger than those on the surface before FZM; these adhered to the surface during sample preparation for XPS measurement. It is concluded that sample preparation introduces contamination which affects the detection limit of chemical analytical instruments. Sn was only observed on the top surface after FZM. It was segregated Sn which was contained in chromium as a starting material. It must be eliminated before starting. From XPS depth profiling results, it was concluded that 0.2 nm thickness of carbon such as hydrocarbon and organic components are adsorbed on the 1 nm thickness of oxide layer. Below the oxide layer, a lack of Cr was observed down to a depth of 6 nm. (orig.)

Classification of alloys using laser induced breakdown spectroscopy with principle component analysis

Science.gov (United States)

Syuhada Mangsor, Aneez; Haider Rizvi, Zuhaib; Chaudhary, Kashif; Safwan Aziz, Muhammad

2018-05-01

The study of atomic spectroscopy has contributed to a wide range of scientific applications. In principle, laser induced breakdown spectroscopy (LIBS) method has been used to analyse various types of matter regardless of its physical state, either it is solid, liquid or gas because all elements emit light of characteristic frequencies when it is excited to sufficiently high energy. The aim of this work was to analyse the signature spectrums of each element contained in three different types of samples. Metal alloys of Aluminium, Titanium and Brass with the purities of 75%, 80%, 85%, 90% and 95% were used as the manipulated variable and their LIBS spectra were recorded. The characteristic emission lines of main elements were identified from the spectra as well as its corresponding contents. Principal component analysis (PCA) was carried out using the data from LIBS spectra. Three obvious clusters were observed in 3-dimensional PCA plot which corresponding to the different group of alloys. Findings from this study showed that LIBS technology with the help of principle component analysis could conduct the variety discrimination of alloys demonstrating the capability of LIBS-PCA method in field of spectro-analysis. Thus, LIBS-PCA method is believed to be an effective method for classifying alloys with different percentage of purifications, which was high-cost and time-consuming before.

Structural evolution of Cu{sub (1−X)}Y{sub X} alloys prepared by mechanical alloying: Their thermal stability and mechanical properties

Energy Technology Data Exchange (ETDEWEB)

Mula, Suhrit, E-mail: smulafmt@iitr.ernet.in [Department of Metallurgical and Materials Engineering, Indian Institute of Technology Roorkee, Roorkee 247667 (India); Setman, Daria [Physics of Nanostructured Materials, University of Vienna, Boltzmanngasse 5, A-1090 Wien (Austria); Youssef, Khaled [Department of Materials Science and Technology, Qatar University, P.O. Box 2713, Doha (Qatar); Scattergood, R.O.; Koch, Carl C [Department of Materials Science and Engineering, NC State University, Raleigh, NC 27695 (United States)

2015-04-05

Highlights: • Metastable solid solutions were prepared from Cu–Y nonequilibrium compositions by mechanical alloying. • Gibbs free energy change as per Miedema’s model confirms the formation of metastable alloys. • High Y content alloys showed high thermal stability during extensive annealing at high temperatures. • Stabilized alloys showed very high hardness and improved yield strength. • Mechanisms of high thermal stability and improved mechanical properties were discussed. - Abstract: In the present study, an attempt has been made to synthesize copper based disordered solid solutions by mechanical alloying (MA) of non-equilibrium compositions. The blended compositions of Cu–1% Y, Cu–3% Y, Cu–5% Y and Cu–7.5% Y (at.%) (all the compositions will be addressed as % only hereafter until unless it is mentioned) were ball-milled for 8 h, and then annealed at different temperatures (200–800 °C) for different length of duration (1–5 h) under high purity argon + 2 vol.% H{sub 2} atmosphere. X-ray diffraction (XRD) analysis and Gibbs free energy change calculation confirm the formation of disordered solid solution (up to 7.5%) of Y in Cu after milling at a room temperature for 8 h. The XRD grain size was calculated to be as low as 7 nm for 7.5% Y and 22 nm for 1% Y alloy. The grain size was retained within 35 nm even after annealing for 1 h at 800 °C. Transmission electron microscopy (TEM) analysis substantiates the formation of ultra-fine grained nanostructures after milling. Microhardness value of the as-milled samples was quite high (3.0–4.75 GPa) compared to that of pure Cu. The hardness value increased with increasing annealing temperatures up to 400 °C for the alloys containing 3–7.5% Y, and thereafter it showed a decreasing trend. The increase in the hardness after annealing is attributed to the formation of uniformly distributed ultrafine intermetallic phases in the nanocrystalline grains. The stabilization effect is achieved due to

Abridged acid-base wet-milling synthesis of high purity hydroyapatite

Directory of Open Access Journals (Sweden)

Sandi Carolina Ruiz-Mendoza

2008-06-01

Full Text Available There is a plethora of routes to produce hydroxyapatite(HA and in general calcium phosphates(CP but production usually leads to a mixture of several phases. Besides ionic contamination, most of these methods are cumbersome, restricted to small volumes of product and require a lot of thermal energy. The acid-base route eliminates foreign ions or additives and its only byproduct is water. Heterogeneous reaction drawback is that solid reactants do not easily come in contact with each other and therefore addition and stirring times become very lengthy and still the product is a mixture. The synthesis started from calcium hydroxide and phosphoric acid (PA. Ball milling was used to favor kinetics and stoichiometry. Six sets of PA addition, paddle stirring and ball milling times were used. Products were evaluated by X ray diffraction (XRD, Fourier Transform Infrared (FTIR, scanning electron microscopy (SEM, X ray fluorescence (XRF and Ca/P ratio. Chemical analysis for calcium proceeded through oxalate precipitate and phosphorus by the phosphomolibdate technique. A set of conditions yielding high purity HA was established.

Multicurie, transportable, integrally shielded 123Xe → 123I generator and processing system for high-purity iodine-123 production

International Nuclear Information System (INIS)

Lagunas-Solar, M.C.; Thibeau, H.L.; Goodart, C.E.; Little, F.E.; Navarro, N.J.; Hartnett, D.E.

1985-01-01

An integrally shielded 123 Xe → 123 I generator system has been designed and tested under production conditions for its suitability as a multicurie handling device from which to produce radiopharmaceutical-quality high-purity no-carrier-added (NCA) 123 I. The 123 Xe → 123 I generator system is expected to provide an alternative to current techniques and to increase the availability and reliability of high-purity 123 I made via the 127 I(p,5n) 123 Xe → 123 I nuclear reaction. The generator system is based on the Crocker Nuclear Laboratory's continuous-flow production system which has been operating since 1974 for the multicurie production of 123 I. The generator system, which consists of an integrally shielded xenon trap and separate loading and processing apparatuses, is simple and reliable to operate, can be adapted to computerized control, and provides a safe working environment for the repeated handling of multicurie amounts of Xe-I radioactivities

Study on corrosion resistance of high - entropy alloy in medium acid liquid and chemical properties

International Nuclear Information System (INIS)

Florea, I; Buluc, G; Florea, R M; Carcea, I; Soare, V

2015-01-01

High-entropy alloy is a new alloy which is different from traditional alloys. The high entropy alloys were started in Tsing Hua University of Taiwan since 1995 by Yeh et al. Consisting of a variety of elements, each element occupying a similar compared with other alloy elements to form a high entropy. We could define high entropy alloys as having approximately equal concentrations, made up of a group of 5 to 11 major elements. In general, the content of each element is not more than 35% by weight of the alloy. During the investigation it turned out that this alloy has a high hardness and is also corrosion proof and also strength and good thermal stability. In the experimental area, scientists used different tools, including traditional casting, mechanical alloying, sputtering, splat-quenching to obtain the high entropy alloys with different alloying elements and then to investigate the corresponding microstructures and mechanical, chemical, thermal, and electronic performances. The present study is aimed to investigate the corrosion resistance in a different medium acid and try to put in evidence the mechanical properties. Forasmuch of the wide composition range and the enormous number of alloy systems in high entropy alloys, the mechanical properties of high entropy alloys can vary significantly. In terms of hardness, the most critical factors are: hardness/strength of each composing phase in the alloy, distribution of the composing phases. The corrosion resistance of an high entropy alloy was made in acid liquid such as 10%HNO 3 -3%HF, 10%H 2 SO 4 , 5%HCl and then was investigated, respectively with weight loss experiment. Weight loss test was carried out by put the samples into the acid solution for corrosion. The solution was maintained at a constant room temperature. The liquid formulations used for tests were 3% hydrofluoric acid with 10% nitric acid, 10% sulphuric acid, 5% hydrochloric acid. Weight loss of the samples was measured by electronic scale. (paper)

Corrosion considerations of high-nickel alloys and titanium alloys for high-level radioactive waste disposal containers

International Nuclear Information System (INIS)

Gdowski, G.E.; McCright, R.D.

1991-07-01

Corrosion resistant materials are being considered for the metallic barrier of the Yucca Mountain Project's high-level radioactive waste disposal containers. High nickel alloys and titanium alloys have good corrosion resistance properties and are considered good candidates for the metallic barrier. The localized corrosion phenomena, pitting and crevice corrosion, are considered as potentially limiting for the barrier lifetime. An understanding of the mechanisms of localized corrosion of how various parameters affect it will be necessary for adequate performance assessments of candidate container materials. Examples of some of the concerns involving candidate container materials. Examples of some of the concerns of involving localized corrosion are discussed. The effects of various parameters, such as temperature and concentration of halide species, on localized corrosion are given. In addition concerns about aging of the protective oxide layer in the expected service temperature range (50 to 250 degrees C) are presented. Also some mechanistic considerations of localized corrosion are given. 31 refs., 1 tab

Computers in the investigation of the impurity content of high-purity materials

International Nuclear Information System (INIS)

Makarov, Yu.B.; Yan'kov, S.V.

1987-01-01

The efficiency of the concept of data banks for the accumulation and processing of information is now generally acknowledged. In scientific investigations not only bibliographic but also factual data banks are becoming more and more prevalent. In this article, the authors consider the possibilities of providing a data bank on high-purity materials for the study of impurity contents. Also in this paper, the authors distinguish the following groups of problems that arise in the study of impurity composition and presents examples of their proposed solutions to these problems: the analysis of error and the determination of the most probably value of impurity concentration; the estimation of average properties of impurity composition with respect to groups of impurities and samples, and the forecast of the complete impurity composition

Neutron activation analysis of high purity silver using high resolution gamma-spectrometry

International Nuclear Information System (INIS)

Gilbert, E.N.; Veriovkin, G.V.; Botchkaryov, B.N.; Godovikov, A.A.; Zhavoronkov, V.Ya.; Mikhailov, V.A.

1975-01-01

A method of neutron activation determination of microimpurities in high purity silver has been developed. For matrix activity separation the extraction of silver by dibuthylsulfide /DBS/ was employed. The purification coefficient was 10 8 after triple extraction. To study the behaviour of microimpurities in the extraction procedure and to determine their chemical yields some tracer experiments were undertaken with radionuclides of Na, Se, Fe, Co, Cu, As, Sc, Te, Zr, Hf, Mo, W, Cd, In, Sb, La, Ce, Eu, Ta, Re, Ir, Ru. All the elements studied were found to remain in the aqueous phase up to 96-99% after triple extraction with DBS. To estimate the accuracy of the method and to study the mutual influence of the elements in the sample in various relative amounts on the accuracy of the analysis, a number of experiments of ''added-found'' type was performed and the results were treated statistically. In these experiments model mixtures of 30 nuclides were analysed after triple DBS extraction. The t-criterion values for the confidence interval at P=0.95 show the absence of systematic errors. Variation coefficient values do not exceed 15%. Using Ge/Li/ detector it was possible to determine 30 elements simultaneously in silver samples. (T.G.)

Gravimetric and volumetric determination of the purity of electrolytically refined silver and the produced silver nitrate

Directory of Open Access Journals (Sweden)

Ačanski Marijana M.

2007-01-01

Full Text Available Silver is, along with gold and the platinum-group metals, one of the so called precious metals. Because of its comparative scarcity, brilliant white color, malleability and resistance to atmospheric oxidation, silver has been used in the manufacture of coins and jewelry for a long time. Silver has the highest known electrical and thermal conductivity of all metals and is used in fabricating printed electrical circuits, and also as a coating for electronic conductors. It is also alloyed with other elements such as nickel or palladium for use in electrical contacts. The most useful silver salt is silver nitrate, a caustic chemical reagent, significant as an antiseptic and as a reagent in analytical chemistry. Pure silver nitrate is an intermediate in the industrial preparation of other silver salts, including the colloidal silver compounds used in medicine and the silver halides incorporated into photographic emulsions. Silver halides become increasingly insoluble in the series: AgCl, AgBr, AgI. All silver salts are sensitive to light and are used in photographic coatings on film and paper. The ZORKA-PHARMA company (Sabac, Serbia specializes in the production of pharmaceutical remedies and lab chemicals. One of its products is chemical silver nitrate (argentum-nitricum (l. Silver nitrate is generally produced by dissolving pure electrolytically refined silver in hot 48% nitric acid. Since the purity of silver nitrate, produced in 2002, was not in compliance with the p.a. level of purity, there was doubt that the electrolytically refined silver was pure. The aim of this research was the gravimetric and volumetric determination of the purity of electrolytically refined silver and silver nitrate, produced industrially and in a laboratory. The purity determination was carried out gravimetrically, by the sedimentation of silver(I ions in the form of insoluble silver salts: AgCl, AgBr and Agi, and volumetrically, according to Mohr and Volhardt. The

The suppression of dissolution for alloy 690 in high temperature and high pressure water with chromium ion implantation

International Nuclear Information System (INIS)

Shibata, Toshio; Fujimoto, Shinji; Ohtani, Saburou; Watanabe, Masanori; Hirao, Kyozo; Okumoto, Masaru; Shibaike, Hiroyuki.

1994-01-01

As the material of heat exchanger tubes for PWRs, the nickel alloys such as alloy 690 and alloy 600 have been used, but 58 Ni and 60 Co contained as an impurity elute in primary cooling water, and are radioactivated, in this way, they become the cause of radiation exposure. By increasing chromium concentration, the corrosion resistance of nickel alloys is improved, and for modern heat exchangers, the alloy 690, of which the chromium content is increased up to 30%, has been adopted, and excellent results have been obtained. In this research, aiming at the further reduction of radiation exposure, by increasing the chromium concentration in surface layer using ion implantation technology, the change of the corrosion behavior of alloy 690 in high temperature, high pressure water was investigated. The chemical composition of the alloy 690 used, and the making of plate specimens are shown. The polarization behavior of alloy 690 in 0.1 mol/l sulfuric acid deaerated at normal temperature is reported, and the effect of suppressing dissolution was remarkable in the specimens with much implantation. The electrochemical behavior of alloy 690 in simulated cooling water was investigated. Immobile case has high chromium content and is thin. (K.I.)

Quantitative influence of minor and impurity elements on hot cracking susceptibility of extra high-purity type 310 stainless steel

International Nuclear Information System (INIS)

Saida, Kazuyoshi; Matsushita, Hideki; Nishimoto, Kazutoshi; Kiuchi, Kiyoshi; Nakayama, Junpei

2013-01-01

To evaluate the influence of minor and impurity elements such as C, Mn, P and S on the solidification and ductility-dip cracking susceptibilities of extra high-purity type 310 stainless steels, the transverse-Varestraint test was conducted by using several type 310 stainless steels with different amounts of C, Mn, P and S. Two types of hot cracks occurred in these steels by Varestraint test; solidification and ductility-dip cracks. The solidification cracking susceptibility was significantly reduced as the amounts of C, P and S decreased. The ductility-dip cracking susceptibility also reduced with a decrease in P and S contents. It adversely, however, increased as the C content of the steels was reduced. Mn didn't greatly affect the hot cracking susceptibility of the extra high-purity steels. The characteristic influence on solidification cracking was the ratio of P:S:C=1:1.3:0.56, while Mn negligibly ameliorated solidification cracking in the extra low S (and P) steels. The numerical analysis on the solidification brittle temperature range (BTR) revealed that the reduced solidification cracking susceptibility with decreasing the amounts of C, P and S in steel could be attributed to the reduced BTR due to the suppression of solidification segregation of minor and impurity elements in the finally solidified liquid film between dendrites. On the other hand, a molecular orbital analysis to estimate the binding strength of the grain boundary suggested that the increased ductility-dip cracking susceptibility in extra high-purity steels was caused by grain boundary embrittlement due to the refining of beneficial elements for grain boundary strengthening such as C. (author)

The probability distribution of intergranular stress corrosion cracking life for sensitized 304 stainless steels in high temperature, high purity water

International Nuclear Information System (INIS)

Akashi, Masatsune; Kenjyo, Takao; Matsukura, Shinji; Kawamoto, Teruaki

1984-01-01

In order to discuss the probability distribution of intergranular stress corrsion carcking life for sensitized 304 stainless steels, a series of the creviced bent beem (CBB) and the uni-axial constant load tests were carried out in oxygenated high temperature, high purity water. The following concludions were resulted; (1) The initiation process of intergranular stress corrosion cracking has been assumed to be approximated by the Poisson stochastic process, based on the CBB test results. (2) The probability distribution of intergranular stress corrosion cracking life may consequently be approximated by the exponential probability distribution. (3) The experimental data could be fitted to the exponential probability distribution. (author)

Development of high-strength aluminum alloys for basket in transport and storage cask for high burn-up spent fuel

International Nuclear Information System (INIS)

Maeguchi, T.; Sakaguchi, Y.; Kamiwaki, Y.; Ishii, M.; Yamamoto, T.

2004-01-01

Mitsubishi Heavy Industries, Ltd. (MHI) has developed high-strength borated aluminum alloys (high-strength B-Al alloys), suitable for application to baskets in transport and storage casks for high burn-up spent fuels. Aluminum is a suitable base material for the baskets due to its low density and high thermal conductivity. The aluminum basket would reduce weight of the cask, and effectively release heat generated by spent fuels. MHI had already developed borated aluminum alloys (high-toughness B-Al alloy), and registered them as ASME Code Case ''N-673''. However, there has been a strong demand for basket materials with higher strength in the case of MSF (Mitsubishi Spent Fuel) casks for high-burn up spent fuels, since the basket is required to stand up to higher stress at higher temperature. The high-strength basket material enables the design of a compact cask under a limitation of total size and weight. MHI has developed novel high-strength B-Al alloys which meet these requirements, based on a new manufacturing process. The outline of mechanical and metallurgical characteristics of the high-strength B-Al alloys is described in this paper

Nanotubular surface and morphology of Ti-binary and Ti-ternary alloys for biocompatibility

International Nuclear Information System (INIS)

Choe, Han-Cheol

2011-01-01

The nanotubular surface of Ti-binary and Ti-ternary alloys for biomaterials has been investigated using various methods of surface characterization. Binary Ti-xNb (x = 10, 20, 30, and 40 wt.%) and ternary Ti-30Ta-xNb (x = 3, 7 and 15 wt.%) alloys were prepared by using the high-purity sponges; Ti, Ta and Zr spheres. The nanotube on the alloy surface was formed in 1.0 M H 3 PO 4 with small additions of NaF (0.5 and 0.8 wt.%), using a potentiostat. For cell proliferation, an MC3T3-E1 mouse osteoblast was used. The surface characteristics were investigated using field-emission scanning electron microscope, energy dispersive spectroscopy, and X-ray photoelectron spectroscopy. Binary Ti-xZr alloys had a lamellar and a needle-like structure, whereas, ternary Ti-30Ta-xZr alloys had equiaxed grains with a lamellar martensitic α' structure. The thickness of the needle-like laths of the α-phase increased as the Zr content increased. The nanotubes formed on the α phase and β phase showed a different size and shape appearance with Zr content. As the Zr content increased from 3 to 40 wt.%, the diameter of the nanotubes in Ti-xZr and Ti-30Ta-xZr alloy decreased from 200 nm to 50 nm. The nanotubular Ti-30Ta-15Zr alloy surface with a diameter of 50 nm provided a good osseointegration; cell proliferation, migration and differentiation.

Long term immersion test of aluminum alloy AA 6061 used for fuel cladding in MTR type reactors

International Nuclear Information System (INIS)

Linardi, Evelina M.; Rodriguez, Sebastian; Haddad, Roberto; Lanzani, Liliana

2009-01-01

In this work we present the results of long term immersion tests performed in the aluminum alloy AA 6061, used for fuel cladding in MTR type reactors. The tests were performed at open circuit potential in high purity water (ρ = 18.2 MΩ.cm) and in 10 -3 M NaCl solution. Two kinds of assemblies were studied: simple sheets and artificial crevices, immersed during 6, 12 and 18 months at room temperature. In both media and both assemblies, the aluminum hydroxide phases crystalline bayerite and bohemite were identified. It was found that a kind of localized attack named alkaline attack occurs around the iron-rich intermetallics. These particles were confirmed to control the corrosion of the AA 6061 alloy in an aerated medium. Immersion times for up to 18 months did not increase the oxide growth or the alkaline attack on the AA 6061 alloy. (author)

Matrix Transformation in Boron Containing High-Temperature Co-Re-Cr Alloys

Science.gov (United States)

Strunz, Pavel; Mukherji, Debashis; Beran, Přemysl; Gilles, Ralph; Karge, Lukas; Hofmann, Michael; Hoelzel, Markus; Rösler, Joachim; Farkas, Gergely

2018-03-01

An addition of boron largely increases the ductility in polycrystalline high-temperature Co-Re alloys. Therefore, the effect of boron on the alloy structural characteristics is of high importance for the stability of the matrix at operational temperatures. Volume fractions of ɛ (hexagonal close-packed—hcp), γ (face-centered cubic—fcc) and σ (Cr2Re3 type) phases were measured at ambient and high temperatures (up to 1500 °C) for a boron-containing Co-17Re-23Cr alloy using neutron diffraction. The matrix phase undergoes an allotropic transformation from ɛ to γ structure at high temperatures, similar to pure cobalt and to the previously investigated, more complex Co-17Re-23Cr-1.2Ta-2.6C alloy. It was determined in this study that the transformation temperature depends on the boron content (0-1000 wt. ppm). Nevertheless, the transformation temperature did not change monotonically with the increase in the boron content but reached a minimum at approximately 200 ppm of boron. A probable reason is the interplay between the amount of boron in the matrix and the amount of σ phase, which binds hcp-stabilizing elements (Cr and Re). Moreover, borides were identified in alloys with high boron content.

Corrosion resistance of aluminum-magnesium alloys in glacial acetic acid

International Nuclear Information System (INIS)

Zaitseva, L.V.; Romaniv, V.I.

1984-01-01

Vessels for the storage and conveyance of glacial acetic acid are produced from ADO and AD1 aluminum, which are distinguished by corrosion resistance, weldability and workability in the hot and cold conditions but have low tensile strength. Aluminum-magnesium alloys are stronger materials close in corrosion resistance to technical purity aluminum. An investigation was made of the basic alloying components on the corrosion resistance of these alloys in glacial acetic acid. Both the base metal and the weld joints were tested. With an increase in temperature the corrosion rate of all of the tested materials increases by tens of times. The metals with higher magnesium content show more pitting damage. The relationship of the corrosion resistance of the alloys to magnesium content is confirmed by the similar intensity of failure of the joint metal of all of the investigated alloys and by electrochemical investigations. The data shows that AMg3 alloy is close to technically pure ADO aluminum. However, the susceptibility of even this material to local corrosion eliminates the possibility of the use of aluminum-magnesium alloys as reliable constructional materials in glacial acetic acid

Welding of Invar Fe-36 Ni Alloy used for tooling of composite materials

International Nuclear Information System (INIS)

Corbacho, J.L.; Suarez, J.C.; Molleda, F.

1997-01-01

Invar alloy has been used for a long time almost exclusively for the manufacturing of high precision devices. Recently, however, new structural uses, such as bulky composite tooling for aerospace industry, have forced to reconsider all the welding procedures previously used. The aim of this research work is to get some insight into several of the problems of welding of invar, while proposing solutions concerned with experience or actual uses. Several issues have been considered, such as precautions with regards the purity of the inert shielding gas and the absence of residues on the surface, role of the titanium added with the filler metal, sensitivity of the alloy to reheat cracking, existence of precipitates and inclusions, etc. The presence of a characteristic banding on the weld pool, its origin and incidence on joint's properties have been also investigated. (Author) 28 refs

Analysis of the Purity of Cetrimide by Titrations

DEFF Research Database (Denmark)

Andersen, Jens Enevold Thaulov; Rasmussen, Claus/Dallerup; Nielsen, Hans/Boye

2006-01-01

. Titration by perchloric acid showed a 99.69 ± 0.05 % purity of cetrimide and titration by silver nitrate showed a 99.85% ± 0.05 % purity while the traditional assay method predicted a purity of only 97.1 ± 0.4. It was found that the discrepancy could be identified as differences in selectivity during...