helium corrosion behavior: Topics by WorldWideScience.org

Sample records for helium corrosion behavior

Effects of Impurity on the Corrosion Behavior of Alloy 617 in the Helium Environment

International Nuclear Information System (INIS)

Jung, Sujin; Kim, Dong Jin; Lee, Gyeong Geun

2013-01-01

The helium coolant in the primary circuit inevitably includes minor impurities such as H 2 , CO, CH 4 , and H 2 O under operating condition. Material degradation is aggravated through oxidation, carburization, and decarburization under the impure helium environment. In this study, high-temperature corrosion tests were carried out at 850-950 .deg. C in the impure helium environment. The mass changes of the specimens were measured and the microstructures were analyzed quantitatively. In addition, all corrosion tests were conducted in the pure helium environment and the results were compared to the results under the impure helium. Alloy 617 specimens showed a parabolic oxidation behavior at all temperatures under the impure helium environment. All specimens had similar microstructure in the outer Cr-oxide layers, internal Al-oxides, and carbide-depleted zone. The weight increase of the corroded specimens in the pure helium was relatively reduced. Microstructure result, oxide layer and carbide depleted zone were hardly ever observed. The impurity in helium affected the corrosion behavior of Alloy 617 and may cause a decrease in the mechanical properties. Therefore, the control of minor impurities in VHTR helium is necessary for the application of Alloy 617 to the IHX material of a VHTR
High-Temperature Corrosion Behavior of Alloy 617 in Helium Environment of Very High Temperature Gas Reactor

International Nuclear Information System (INIS)

Lee, Gyeong-Geun; Jung, Sujin; Kim, Daejong; Jeong, Yong-Whan; Kim, Dong-Jin

2012-01-01

Alloy 617 is a Ni-base superalloy and a candidate material for the intermediate heat exchanger (IHX) of a very high temperature gas reactor (VHTR) which is one of the next generation nuclear reactors under development. The high operating temperature of VHTR enables various applications such as mass production of hydrogen with high energy efficiency. Alloy 617 has good creep resistance and phase stability at high temperatures in an air environment. However, it was reported that the mechanical properties decreased at a high temperature in an impure helium environment. In this study, high-temperature corrosion tests were carried out at 850°C-950°C in a helium environment containing the impurity gases H_2, CO, and CH_4, in order to examine the corrosion behavior of Alloy 617. Until 250 h, Alloy 617 specimens showed a parabolic oxidation behavior at all temperatures. The activation energy for oxidation in helium environment was 154 kJ/mol. The SEM and EDS results elucidated a Cr-rich surface oxide layer, Al-rich internal oxides and depletion of grain boundary carbides. The thickness and depths of degraded layers also showed a parabolic relationship with time. A normal grain growth was observed in the Cr-rich surface oxide layer. When corrosion tests were conducted in a pure helium environment, the oxidation was suppressed drastically. It was elucidated that minor impurity gases in the helium would have detrimental effects on the high temperature corrosion behavior of Alloy 617 for the VHTR application.
Hot corrosion behavior of Ni-Cr-W-C alloys in impure helium gas

International Nuclear Information System (INIS)

Ohmura, Taizo; Sahira, Kensho; Sakonooka, Akihiko; Yonezawa, Noboru

1976-01-01

Influence of the minor alloy constituents such as Al, Mn and Si on the hot corrosion behavior of Ni-20Cr-20W-0.07C alloy was studied in 99.995% helium gas at 1000 0 C, comparing with that behavior of commercial Ni-base superalloys (Hastelloy X and Inconel 617). The low oxidizing potential in the impure helium gas usually causes selective oxidation of these elements and the growth of oxide whiskers on the surface of specimen at elevated temperature. The intergranular attack was caused by selective oxidation of Al, Si and Mn. The spalling of oxide film was restrained by addition of Mn and Si, providing tough spinel type oxide film on the surface and 'Keyes' on the oxide-matrix interface respectively. The amount and the morphology of the oxide whiskers depended on Si and Mn content. More than 0.29% of Si content without Mn always caused the growth of rather thinner whiskers with smooth surface, and the whiskers analyzed by electron diffraction patterns and EPMA to be Cr 2 O 3 containing Si. Mn addition changed the whiskers to thicker ones of spinel type oxide (MnCr 2 O 1 ) with rough surface. On the basis of these results, the optimum content of Al, Mn and Si to minimize the growth of whiskers, the intergranular attack and the spalling of oxide film was discussed. (auth.)
Corrosion behaviour of high temperature alloys in impure helium environments

International Nuclear Information System (INIS)

Shindo, Masami; Quadakkers, W.J.; Schuster, H.

1986-01-01

Corrosion tests with Ni-base high temperature alloys were carried out at 900 and 950 0 C in simulated high temperature reactor helium environments. It is shown that the carburization and decarburization behaviour is strongly affected by the Cr and Ti(Al) contents of the alloys. In carburizing environments, additions of Ti, alone or in combination with Al, significantly improve the carburization resistance. In oxidizing environment, the alloys with high Cr and Al(Ti) contents are the most resistant against decarburization. In this environment alloys with additions of Ti and Al show poor oxidation resistance. The experimental results obtained are compared with a recently developed theory describing corrosion of high temperature alloys in high temperature reactor helium environments. (orig.)
Stress corrosion cracking of U-0.1% Cr in humid helium atmosphere

International Nuclear Information System (INIS)

Zalkind, S.; Eshkenazy, R.; Harush, S.; Halperin, D.; Moreno, D.; Abramov, E.; Venkert, A.

1994-01-01

Rivets were matched into adapted drilled holes in plates, both made of U-0.1% Cr alloy and were placed in different environments containing dry air and helium and humid air and helium for a variety of exposure times. After opening, the most significant amounts of corrosion products were detected in the specimens that stayed for three years in humid helium (5% RH) environment. Radial cracks, developed in the bore edge, were detected in the specimens. X-ray diffraction patterns of the corrosion products gave the composition of UH 3 and UO 2 . The microstructure was examined using light and electron microscopy techniques. The hydride phase that was observed, formed mainly beneath the oxide layer and penetrated into the metal matrix as needle-like forms. The formation of a lower density hydride phase, yielded in a large volume change causing the development of high stresses at the rivet-bore interface. The combination of the high stress and the weakening of the bore edge due to the presence of the brittle hydride phase led to radial crack formation around the bore edge. (orig.)
Influence of heating rate on corrosion behavior of Ni-base heat resistant alloys in simulated VHTR helium environment

International Nuclear Information System (INIS)

Kurata, Yuji; Kondo, Tatsuo

1985-04-01

The influence of heating rate on corrosion and carbon transfer was studied for Ni-base heat resistant alloys exposed to simulated VHTR(very high temperature reactor) coolant environment. Special attention was focused to relationship between oxidation and carburization at early stage of exposure. Tests were conducted on two heats of Hastelloy XR with different boron(B) content and the developmental alloys, 113MA and KSN. Two kinds of heating rates, i.e. 80 0 C/min and 2 0 C/min, were employed. Corrosion tests were carried out at 900 0 C up to 500 h in JAERI Type B helium, one of the simulated VHTR primary coolant specifications. Under higher heating rate, oxidation resistance of both heats of Hastelloy XR(2.8 ppmB and 40 ppmB) were equivalent and among the best, then KSN and 113MA followed in the order. Under lower heating rate only alloy, i.e. Hastelloy XR with 2.8 ppmB, showed some deteriorated oxidation resistance while all others being unaffected by the heating rate. On the other hand the carbon transfer behavior showed strong dependence on the heating rate. In case of higher heating rate, significant carburization occured at early stage of exposure and thereafter the progress of carburization was slow in all the alloys. On the other hand only slow carburization was the case throughout the exposure in case of lower heating rate. The carburization in VHTR helium environment was interpreted as to be affected by oxide film formation in the early stage of exposure. The carbon pick-up was largest in Hastelloy XR with 40 ppmB and it was followed by Hastelloy XR with 2.8 ppmB. 113MA and KSN were carburized only slightly. The observed difference of carbon pick-up among the alloys tested was interpreted to be attributed mainly to the difference of the carbon activity, the carbide precipitation characteristics among the alloys tested. (author)
Corrosion tests of high temperature alloys in impure helium

International Nuclear Information System (INIS)

Berka, Jan; Kalivodova, Jana; Vilemova, Monika; Skoumalova, Zuzana; Brabec, Petr

2014-01-01

Czech research organizations take part several projects concerning technologies and materials for advanced gas cooled reactors, as an example international project ARCHER supported by EU within FP7, also several national projects supported by Technology Agency of the Czech Republic are solved in cooperation with industrial and research organization. Within these projects the material testing program is performed. The results presented in these paper concerning high temperature corrosion and degradation of alloys (800 H, SS 316 and P91) in helium containing minor impurities (H_2, CO, CH_4, HZO) at temperatures up to 760°C. After corrosion tests (up to 1500 hours) the specimens was investigated by several methods (gravimetry, SEM-EDX, optical microscopy, hardness and micro-hardness testing etc. (author)
Corrosion of nickel-base heat resistant alloys in simulated VHTR coolant helium at very high temperatures

International Nuclear Information System (INIS)

Shindo, Masami; Kondo, Tatsuo

1976-01-01

A comparative evaluation was made on three commercial nickel-base heat resistant alloys exposed to helium-base atmosphere at 1000 0 C, which contained several impurities in simulating the helium cooled very high temperature nuclear reactor (VHTR) environment. The choice of alloys was made so that the effect of elements commonly found in commercial alloys were typically examined. The corrosion in helium at 1000 0 C was characterized by the sharp selection of thermodynamically unstable elements in the oxidizing process and the resultant intergranular penetration and internal oxidation. Ni-Cr-Mo-W type solution hardened alloy such as Hastelloy-X showed comparatively good resistance. The alloy containing Al and Ti such as Inconel-617 suffered adverse effect in contrast to its good resistance to air oxidation. The alloy nominally composed only of noble elements, Ni, Fe and Mo, such as Hastelloy-B showed least apparent corrosion, while suffered internal oxidation due to small amount of active impurities commonly existing in commercial heats. The results were discussed in terms of selection and improvement of alloys for uses in VHTR and the similar systems. (auth.)
Effects of a range of machined and ground surface finishes on the simulated reactor helium corrosion of several candidate structural materials

International Nuclear Information System (INIS)

Thompson, L.D.

1981-02-01

This report discusses the corrosion behavior of several candidate reactor structural alloys in a simulated advanced high-temperature gas-cooled reactor (HTGR) environment over a range of lathe-machined and centerless-ground surface finishes. The helium environment contained 50 Pa H 2 /5 Pa CO/5 Pa CH 4 / 2 O (500 μatm H 2 /50 μatm CO/50 μatm CH 4 / 2 O) at 900 0 C for a total exposure of 3000 h. The test alloys included two vacuum-cast superalloys (IN 100 and IN 713LC); a centrifugally cast austenitic alloy (HK 40); three wrought high-temperature alloys (Alloy 800H, Hastelloy X, and Inconel 617); and a nickel-base oxide-dispersion-strengthened alloy (Inconel MA 754). Surface finish variations did not affect the simulated advanced-HTGR corrosion behavior of these materials. Under these conditions, the availability of reactant gaseous impurities controls the kinetics of the observed gas-metal interactions. Variations in the near-surface activities and mobilities of reactive solute elements, such as chromium, which might be expected to be affected by changes in surface finish, do not seem to greatly influence corrosion in this simulated advanced HTGR environment. 18 figures, 4 tables
The corrosion behavior of DWPF glasses

International Nuclear Information System (INIS)

Ebert, W.L.; Bates, J.K.

1995-01-01

The authors analyzed the corroded surfaces of reference glasses developed for the Defense Waste Processing Facility (DWPF) to characterize their corrosion behavior. The corrosion mechanism of nuclear waste glasses must be known in order to provide source terms describing radionuclide release for performance assessment calculations. Different DWPF reference glasses were corroded under conditions that highlighted various aspects of the corrosion process and led to different extents of corrosion. The glasses corroded by similar mechanisms, and a phenomenological description of their corrosion behavior is presented here. The initial leaching of soluble glass components results in the formation of an amorphous gel layer on the glass surface. The gel layer is a transient phase that transforms into a layer of clay crystallites, which equilibrates with the solution as corrosion continues. The clay layer does not act as a barrier to either water penetration or glass dissolution, which continues beneath it, and may eventually separate from the glass. Solubility limits for glass components may be established by the eventual precipitation of secondary phases; thus, corrosion of the glass becomes controlled by the chemical equilibrium between the solution and the assemblage of secondary phases. In effect, the solution is an intermediate phase through which the glass transforms to an energetically more favorable assemblage of phases. Implications regarding the prediction of long-term glass corrosion behavior are discussed
The Effects of CO{sub 2} Pressure on Corrosion and Carburization Behaviors of Chromia-forming Austenitic Alloys

Energy Technology Data Exchange (ETDEWEB)

Lee, Ho Jung; Kim, Sung Hwan; Jang, Changheui [KAIST, Daejeon (Korea, Republic of)

2015-05-15

By applying S-CO{sub 2} cycle to SFR, the inherent safety could be improved by alleviating the concern of explosive reaction between high temperature steam and liquid sodium as well as increased thermal efficiency at 500-550 .deg. C compared to helium Brayton cycle. Meanwhile, from the material point of view, a compatibility such as corrosion and carburization of candidate materials in S-CO{sub 2} environment should be evaluated to assure the long-term integrity of IHX. It has been previously reported that Ni-base alloys and high-Cr Fe-base austenitic alloys showed a good corrosion resistance by the formation of thin chromia layer while carburization behaviors of those materials were not properly investigated. Corrosion and carburization behaviors of three chromia-forming austenitic alloys (Ni-base alloys and Alloy 800HT) were evaluated in S-CO{sub 2} (200 bar) and CO{sub 2} (1 bar) environment at 550.650 .deg. C for 1000 h. For all test materials, a good corrosion resistance was exhibited by the formation of thin chromia (Cr{sub 2}O{sub 3}) with small amount of minor oxides such as Mn1.5Cr1.5O{sub 4}, Al{sub 2}O{sub 3}, and TiO{sub 2}.
High temperature oxidation and corrosion behavior of Ni-base superalloy in He environment

International Nuclear Information System (INIS)

Lee, Gyoeng Geun; Park, Ji Yeon; Jung, Su jin

2010-11-01

Ni-base superalloy is considered as a IHX (Intermediate Heat Exchanger) material for VHTR (Very High Temperature Gas-Cooled Reactor). The helium environment in VHTR contains small amounts of impure gases, which cause oxidation, carburization, and decarburization. In this report, we conducted the literature survey about the high temperature behavior of Ni-base superalloys in air and He environments. The basic information of Ni-base superalloy and the basic metal-oxidation theory were briefly stated. The He effect on the corrosion of Ni-base superalloy was also summarized. This works would provide a brief suggestion for the next research topic for the application of Ni-base superalloy to VHTR
Corrosion behaviors and effects of corrosion products of plasma electrolytic oxidation coated AZ31 magnesium alloy under the salt spray corrosion test

International Nuclear Information System (INIS)

Wang, Yan; Huang, Zhiquan; Yan, Qin; Liu, Chen; Liu, Peng; Zhang, Yi; Guo, Changhong; Jiang, Guirong; Shen, Dejiu

2016-01-01

Highlights: • Corrosion behaviors of a PEO coating was investigated after the salt spray test. • Corrosion products have significant effects on corrosion behaviors of the coating. • An electrochemical corrosion model is proposed. - Abstract: The effects of corrosion products on corrosion behaviors of AZ31 magnesium alloy with a plasma electrolytic oxidation (PEO) coating were investigated under the salt spray corrosion test (SSCT). The surface morphology, cross-sectional microstructure, chemical and phase compositions of the PEO coating were determined using scanning electron microscopy (SEM) equipped with energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction analysis (XRD), respectively. Further, the corrosion process of the samples under the SSCT was examined in a non-aqueous electrolyte (methanol) using electrochemical impedance spectroscopy (EIS) coupled with equivalent circuit. The results show that the inner layer of the coating was destroyed firstly and the corrosion products have significant effects on the corrosion behaviors of the coating. The results above are discussed and an electrochemical corrosion model is proposed in the paper.
Corrosion behaviors and effects of corrosion products of plasma electrolytic oxidation coated AZ31 magnesium alloy under the salt spray corrosion test

Energy Technology Data Exchange (ETDEWEB)

Wang, Yan; Huang, Zhiquan; Yan, Qin; Liu, Chen; Liu, Peng; Zhang, Yi [State Key Laboratory of Metastable Materials Science and Technology, College of Materials Science and Engineering, Yanshan University, Qinhuangdao 066004 (China); Guo, Changhong; Jiang, Guirong [College of Mechanical Engineering, Yanshan University, Qinhuangdao 066004 (China); Shen, Dejiu, E-mail: DejiuShen@163.com [State Key Laboratory of Metastable Materials Science and Technology, College of Materials Science and Engineering, Yanshan University, Qinhuangdao 066004 (China)

2016-08-15

Highlights: • Corrosion behaviors of a PEO coating was investigated after the salt spray test. • Corrosion products have significant effects on corrosion behaviors of the coating. • An electrochemical corrosion model is proposed. - Abstract: The effects of corrosion products on corrosion behaviors of AZ31 magnesium alloy with a plasma electrolytic oxidation (PEO) coating were investigated under the salt spray corrosion test (SSCT). The surface morphology, cross-sectional microstructure, chemical and phase compositions of the PEO coating were determined using scanning electron microscopy (SEM) equipped with energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction analysis (XRD), respectively. Further, the corrosion process of the samples under the SSCT was examined in a non-aqueous electrolyte (methanol) using electrochemical impedance spectroscopy (EIS) coupled with equivalent circuit. The results show that the inner layer of the coating was destroyed firstly and the corrosion products have significant effects on the corrosion behaviors of the coating. The results above are discussed and an electrochemical corrosion model is proposed in the paper.
Thermal release behavior of helium from copper irradiated by He+ ions

International Nuclear Information System (INIS)

Yamauchi, T.; Tokura, S.; Yamanaka, S.; Miyake, M.

1988-01-01

Thermal release behavior of helium from copper irradiated by 20 keV He + ions with a dose of 2x10 15 to 3x10 17 ions/cm 2 has been studied. The shape of the thermal release curves and thew number of helium release peaks strongly depend on the irradiation dose. Results from SEM surface observastion after post-irradiation heating suggested that helium release caused various surface damages such as blistering, flaking, and hole formation. Helium release resulting in small holes was analyzed and helium bubble growth mechanisms are discussed. (orig.)
Corrosion behavior of Mg/graphene composite in aqueous electrolyte

International Nuclear Information System (INIS)

Selvam, M.; Saminathan, K.; Siva, P.; Saha, P.; Rajendran, V.

2016-01-01

In the present work, the electrochemical corrosion behavior of magnesium (Mg) and thin layer graphene coated Mg (Mg/graphene) are studied in different salt electrolyte such as NaCl, KCl and Na_2SO_4. The phase structure, crystallinity, and surface morphology of the samples are investigated using X-ray diffraction (XRD) analysis, scanning electron microscopy coupled with energy dispersive X-ray analysis (SEM/EDAX), and Raman spectroscopy techniques. The electrochemical corrosion behavior of the Mg and graphene coated Mg are also investigated using Electrochemical Impedance Spectroscopy (EIS) analysis. The tafel plot reveals that the corrosion of Mg drastically drops when coated with thin layer graphene (Mg/graphene) compared to Mg in KCl electrolyte. Moreover, the EIS confirms that Mg/graphene sample shows improve corrosion resistance and lower corrosion rate in KCl solution compare to all other electrolytes studied in the present system. - Highlights: • The corrosion behavior of magnesium alloy (AZ91) was investigated in three different electrolyte solution. • To study the anti-corrosion behavior of graphene coated with magnesium alloy. • To improve the corrosion resistance for magnesium alloy. • Nyquist plots confirms that MgG shows better corrosion resistance and lower corrosion rate in KCl solution.
Corrosion behavior of Mg/graphene composite in aqueous electrolyte

Energy Technology Data Exchange (ETDEWEB)

Selvam, M. [Centre for Nano Science and Technology, KS Rangasamy College of Technology, Tiruchengode, 637215, Tamil Nadu (India); Saminathan, K., E-mail: ksaminath@gmail.com [Centre for Nano Science and Technology, KS Rangasamy College of Technology, Tiruchengode, 637215, Tamil Nadu (India); Siva, P. [Centre for Nano Science and Technology, KS Rangasamy College of Technology, Tiruchengode, 637215, Tamil Nadu (India); Saha, P. [Department of Ceramic Engineering, National Institute of Technology, Rourkela, India-769008 (India); Rajendran, V. [Centre for Nano Science and Technology, KS Rangasamy College of Technology, Tiruchengode, 637215, Tamil Nadu (India)

2016-04-01

In the present work, the electrochemical corrosion behavior of magnesium (Mg) and thin layer graphene coated Mg (Mg/graphene) are studied in different salt electrolyte such as NaCl, KCl and Na{sub 2}SO{sub 4}. The phase structure, crystallinity, and surface morphology of the samples are investigated using X-ray diffraction (XRD) analysis, scanning electron microscopy coupled with energy dispersive X-ray analysis (SEM/EDAX), and Raman spectroscopy techniques. The electrochemical corrosion behavior of the Mg and graphene coated Mg are also investigated using Electrochemical Impedance Spectroscopy (EIS) analysis. The tafel plot reveals that the corrosion of Mg drastically drops when coated with thin layer graphene (Mg/graphene) compared to Mg in KCl electrolyte. Moreover, the EIS confirms that Mg/graphene sample shows improve corrosion resistance and lower corrosion rate in KCl solution compare to all other electrolytes studied in the present system. - Highlights: • The corrosion behavior of magnesium alloy (AZ91) was investigated in three different electrolyte solution. • To study the anti-corrosion behavior of graphene coated with magnesium alloy. • To improve the corrosion resistance for magnesium alloy. • Nyquist plots confirms that MgG shows better corrosion resistance and lower corrosion rate in KCl solution.
Friction, adhesion and corrosion performance of metallurgical coatings in HTGR-helium

International Nuclear Information System (INIS)

Engel, R.; Kleemann, W.

1981-01-01

The friction-, adhesion-, thermal cycling- and corrosion performance of several metallurgical coating systems have been tested in a simulated HTGR-test atmosphere at elevated temperatures. The coatings were applied to a solid solution strengthened Ni-based superalloy. Component design requires coatings for the protection of mating surfaces, since under reactor operating conditions, contacting surfaces of metallic components under high pressures are prone to friction and wear damage. The coatings will have to protect the metal surface for 30 years up to 950 0 C in HTGR-helium. The materials tested were various refractory carbides with or without metallic binders and intermetallic compounds. The coatings evaluated were applied by plasma spraying-, detonation gun- and chemical vapor deposition techniques. These yielded two types of coatings which employ different mechanisms to improve the tribiological properties and maintain coating integrity. (Auth.)
Flow-induced corrosion behavior of absorbable magnesium-based stents.

Science.gov (United States)

Wang, Juan; Giridharan, Venkataraman; Shanov, Vesselin; Xu, Zhigang; Collins, Boyce; White, Leon; Jang, Yongseok; Sankar, Jagannathan; Huang, Nan; Yun, Yeoheung

2014-12-01

The aim of this work was to study corrosion behavior of magnesium (Mg) alloys (MgZnCa plates and AZ31 stents) under varied fluid flow conditions representative of the vascular environment. Experiments revealed that fluid hydrodynamics, fluid flow velocity and shear stress play essential roles in the corrosion behavior of absorbable magnesium-based stent devices. Flow-induced shear stress (FISS) accelerates the overall corrosion (including localized, uniform, pitting and erosion corrosions) due to the increased mass transfer and mechanical force. FISS increased the average uniform corrosion rate, the localized corrosion coverage ratios and depths and the removal rate of corrosion products inside the corrosion pits. For MgZnCa plates, an increase of FISS results in an increased pitting factor but saturates at an FISS of ∼0.15Pa. For AZ31 stents, the volume loss ratio (31%) at 0.056Pa was nearly twice that (17%) at 0Pa before and after corrosion. Flow direction has a significant impact on corrosion behavior as more severe pitting and erosion corrosion was observed on the back ends of the MgZnCa plates, and the corrosion product layer facing the flow direction peeled off from the AZ31 stent struts. This study demonstrates that flow-induced corrosion needs be understood so that Mg-based stents in vascular environments can be effectively designed. Copyright © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
Passive Corrosion Behavior of Alloy 22

International Nuclear Information System (INIS)

R.B. Rebak; J.H. Payer

2006-01-01

Alloy 22 (NO6022) was designed to stand the most aggressive industrial applications, including both reducing and oxidizing acids. Even in the most aggressive environments, if the temperature is lower than 150 F (66 C) Alloy 22 would remain in the passive state having particularly low corrosion rates. In multi-ionic solutions that may simulate the behavior of concentrated ground water, even at near boiling temperatures, the corrosion rate of Alloy 22 is only a few nano-meters per year because the alloy is in the complete passive state. The corrosion rate of passive Alloy 22 decreases as the time increases. Immersion corrosion testing also show that the newer generation of Ni-Cr-Mo alloys may offer a better corrosion resistance than Alloy 22 only in some highly aggressive conditions such as in hot acids

Corrosion behaviors and effects of corrosion products of plasma electrolytic oxidation coated AZ31 magnesium alloy under the salt spray corrosion test

Science.gov (United States)

Wang, Yan; Huang, Zhiquan; Yan, Qin; Liu, Chen; Liu, Peng; Zhang, Yi; Guo, Changhong; Jiang, Guirong; Shen, Dejiu

2016-08-01

The effects of corrosion products on corrosion behaviors of AZ31 magnesium alloy with a plasma electrolytic oxidation (PEO) coating were investigated under the salt spray corrosion test (SSCT). The surface morphology, cross-sectional microstructure, chemical and phase compositions of the PEO coating were determined using scanning electron microscopy (SEM) equipped with energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction analysis (XRD), respectively. Further, the corrosion process of the samples under the SSCT was examined in a non-aqueous electrolyte (methanol) using electrochemical impedance spectroscopy (EIS) coupled with equivalent circuit. The results show that the inner layer of the coating was destroyed firstly and the corrosion products have significant effects on the corrosion behaviors of the coating. The results above are discussed and an electrochemical corrosion model is proposed in the paper.
Corrosion behavior of Ti-39Nb alloy for dentistry.

Science.gov (United States)

Fojt, Jaroslav; Joska, Ludek; Malek, Jaroslav; Sefl, Vaclav

2015-11-01

To increase an orthopedic implant's lifetime, researchers are now concerned on the development of new titanium alloys with suitable mechanical properties (low elastic modulus-high fatigue strength), corrosion resistance and good workability. Corrosion resistance of the newly developed titanium alloys should be comparable with that of pure titanium. The effect of medical preparations containing fluoride ions represents a specific problem related to the use of titanium based materials in dentistry. The aim of this study was to determine the corrosion behavior of β titanium alloy Ti-39Nb in physiological saline solution and in physiological solution containing fluoride ions. Corrosion behavior was studied using standard electrochemical techniques and X-ray photoelectron spectroscopy. It was found that corrosion properties of the studied alloy were comparable with the properties of titanium grade 2. The passive layer was based on the oxides of titanium and niobium in several oxidation states. Alloying with niobium, which was the important part of the alloy passive layer, resulted in no significant changes of corrosion behavior. In the presence of fluoride ions, the corrosion resistance was higher than the resistance of titanium. Copyright © 2015 Elsevier B.V. All rights reserved.
Corrosion behavior of Ti–39Nb alloy for dentistry

Energy Technology Data Exchange (ETDEWEB)

Fojt, Jaroslav, E-mail: fojtj@vscht.cz [Institute of Chemical Technology, Technicka 5, 166 28 Prague (Czech Republic); Joska, Ludek [Institute of Chemical Technology, Technicka 5, 166 28 Prague (Czech Republic); Malek, Jaroslav [UJP Praha, Nad Kamínkou 1345, 156 10 Prague-Zbraslav (Czech Republic); Sefl, Vaclav [Institute of Chemical Technology, Technicka 5, 166 28 Prague (Czech Republic)

2015-11-01

To increase an orthopedic implant's lifetime, researchers are now concerned on the development of new titanium alloys with suitable mechanical properties (low elastic modulus–high fatigue strength), corrosion resistance and good workability. Corrosion resistance of the newly developed titanium alloys should be comparable with that of pure titanium. The effect of medical preparations containing fluoride ions represents a specific problem related to the use of titanium based materials in dentistry. The aim of this study was to determine the corrosion behavior of β titanium alloy Ti–39Nb in physiological saline solution and in physiological solution containing fluoride ions. Corrosion behavior was studied using standard electrochemical techniques and X-ray photoelectron spectroscopy. It was found that corrosion properties of the studied alloy were comparable with the properties of titanium grade 2. The passive layer was based on the oxides of titanium and niobium in several oxidation states. Alloying with niobium, which was the important part of the alloy passive layer, resulted in no significant changes of corrosion behavior. In the presence of fluoride ions, the corrosion resistance was higher than the resistance of titanium. - Highlights: • Alloy Ti–39Nb shows excellent corrosion resistance in physiological solution. • Corrosion resistance of Ti–39Nb alloy is significantly higher than that of titanium in the presence of fluoride ions. • The electrochemical impedance spectroscopy indicates a porous passive layer. • Passive layer of the alloy is enriched by niobium.
Corrosion behavior of Ti–39Nb alloy for dentistry

International Nuclear Information System (INIS)

Fojt, Jaroslav; Joska, Ludek; Malek, Jaroslav; Sefl, Vaclav

2015-01-01

To increase an orthopedic implant's lifetime, researchers are now concerned on the development of new titanium alloys with suitable mechanical properties (low elastic modulus–high fatigue strength), corrosion resistance and good workability. Corrosion resistance of the newly developed titanium alloys should be comparable with that of pure titanium. The effect of medical preparations containing fluoride ions represents a specific problem related to the use of titanium based materials in dentistry. The aim of this study was to determine the corrosion behavior of β titanium alloy Ti–39Nb in physiological saline solution and in physiological solution containing fluoride ions. Corrosion behavior was studied using standard electrochemical techniques and X-ray photoelectron spectroscopy. It was found that corrosion properties of the studied alloy were comparable with the properties of titanium grade 2. The passive layer was based on the oxides of titanium and niobium in several oxidation states. Alloying with niobium, which was the important part of the alloy passive layer, resulted in no significant changes of corrosion behavior. In the presence of fluoride ions, the corrosion resistance was higher than the resistance of titanium. - Highlights: • Alloy Ti–39Nb shows excellent corrosion resistance in physiological solution. • Corrosion resistance of Ti–39Nb alloy is significantly higher than that of titanium in the presence of fluoride ions. • The electrochemical impedance spectroscopy indicates a porous passive layer. • Passive layer of the alloy is enriched by niobium
Creep-rupture behavior of 2-1/4 Cr-1 Mo steel, Alloy 800H and Hastelloy Alloy X in a simulated HTGR helium environment

International Nuclear Information System (INIS)

Lai, G.Y.; Wolwowicz, R.J.

1979-12-01

Creep-rupture testing was conducted on 1 1/4 Cr-1 Mo steel, Alloy 800H and Hastelloy Alloy X in flowing helium containing nominal concentration of following gases: 1500 μatm H 2 , 450 μatm CO, 50 μatm CH 4 , 50 μatm H 2 O and 5 μatm CO 2 . This environment is believed to represent maximum permissible levels of impurities in the primary coolant for the steam-cycle system of a high-temperature gas-cooled reactor (HTGR) when it is operating continuously with a water and/or steam leak at technical specification limits. Two or three heats of material for each alloy were investigated. Tests were conducted at 482 0 C and 760 0 C (1200 0 F and 1400 0 F) for Alloy 800H, and at 760 0 C and 871 0 C (1400 0 F and 1600 0 F) for Hastelloy Alloy X for times up to 10,000 h. Selected tests were performed on same heat of material in both air and helium environments to make a direct comparison of creep-rupture behaviors between two environments. Metallurgical evaluation was performed on selected post test specimens with respect to gas-metal interactions which included oxidation, carburization and/or decarburization. Correlation between gaseous corrosion and creep-rupture behavior was attempted. Limited tests were also performed to investigate the specimen size effects on creep-rupture behavior in the helium environment
Corrosion behaviors of ceramics against liquid sodium. Sodium corrosion characteristics of sintering additives

International Nuclear Information System (INIS)

Tachi, Yoshiaki; Kano, Shigeki; Hirakawa, Yasushi; Yoshida, Eiichi

1998-01-01

It has been progressed as the Frontier Materials Research to research and develop ceramics to apply for several components of fast breeder reactor using liquid sodium as coolant instead of metallic materials. Grain boundary of ceramics has peculiar properties compared with matrix because most of ceramics are produced by hardening and firing their raw powders. Some previous researchers indicated that ceramics were mainly corroded at grain boundaries by liquid sodium, and ceramics could not be used under corrosive environment. Thus, it is the most important for the usage of ceramics in liquid sodium to improve corrosion resistance of grain boundaries. In order to develop the advanced ceramics having good sodium corrosion resistance among fine ceramics, which have recently been progressed in quality and characteristics remarkably, sodium corrosion behaviors of typical sintering additives such as MgO, Y 2 O 3 and AlN etc. have been examined and evaluated. As a result, the followings have been clarified and some useful knowledge about developing advanced ceramics having good corrosion resistance against liquid sodium has been obtained. (1) Sodium corrosion behavior of MgO depended on Si content. Samples containing large amount of Si were corroded severely by liquid sodium, whereas others with low Si contents showed good corrosion resistance. (2) Both Y 2 O 3 and AlN, which contained little Si, showed good sodium corrosion resistance. (3) MgO, Y 2 O 3 and AlN are thought to be corroded by liquid sodium, if they contain some SiO 2 . Therefore, in order to improve sodium corrosion resistance, it is very important for these ceramics to prevent the contamination of matrix with SiO 2 through purity control of their raw powders. (author)
Monitoring on corrosion behavior of steam generator tubings

International Nuclear Information System (INIS)

Takamatsu, H.; Isobe, S.; Sato, M.; Arioka, K.; Tsuruta, T.

1988-01-01

The importance of chemistry in high temperature aqueous solutions is widely recognized for understanding corrosion phenomena in PWR SG crevice environments. Potential and pH are two important parameters, among other environmental factors affecting localized corrosion processes, such as IGA and/or SCC in SG crevices. In this article, we discuss the potential-pH-IGA/SCC diagram of Alloy 600 as a basis for evaluating the corrosion behavior of SG tubings, and two examples of monitoring, corrosion potential monitoring in the bulk secondary water and pH monitoring in simulated SG crevices. (author)
Investigation of corrosion behavior of Mg-steel laser-TIG hybrid lap joints

International Nuclear Information System (INIS)

Liu Liming; Xu Rongzheng

2012-01-01

Highlights: ► Galvanic corrosion increases the corrosion rate of the Mg-steel joint. ► Fe splashes lower the corrosion resistance of the joint greatly. ► The effect of grain refinement on the corrosion behavior of the joint is slight. ► Ni or Cu interlayer could not improve the corrosion resistance of fusion zone. ► The arc-sprayed coating could enhance the reliability of weld joint. - Abstract: The paper investigates the corrosion behavior of the lap joint of AZ31 magnesium alloy to Q235 steel with salt solution immersion testing and electrochemical testing. It is demonstrated that grain refinement resulting from the welding process has little effect on the corrosion behavior of the lap joint. However, the cathodic phases formed in the welding process and the galvanic corrosion between magnesium alloy and steel decrease the corrosion resistance of the joint greatly. Besides, neither Cu nor Ni, as filler material, could improve the corrosion resistance of the joint, but the arc-sprayed Al coating acting as a protective layer could.
The Effect of Homogenization on the Corrosion Behavior of Al-Mg Alloy

Science.gov (United States)

Li, Yin; Hung, Yuanchun; Du, Zhiyong; Xiao, Zhengbing; Jia, Guangze

2018-04-01

The effect of homogenization on the corrosion behavior of 5083-O aluminum alloy is presented in this paper. The intergranular corrosion and exfoliation corrosion were used to characterize the discussed corrosion behavior of 5083-O aluminum alloy. The variations in the morphology, the kind and distribution of the precipitates, and the dislocation configurations in the samples after the homogenization were evaluated using optical microscopy (OM), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The effects of the highly active grain boundary character distribution and the types of constituent particles on the corrosion are discussed on the basis of experimental observations. The results indicated that the corrosion behavior of 5083-O alloy was closely related to the microstructure obtained by the heat treatment. Homogenization carried out after casting had the optimal effect on the overall corrosion resistance of the material. Nevertheless, all samples could satisfy the requirements of corrosion resistance in marine applications.
Corrosion behavior of Zr-x(Nb, Sn and Cu) binary alloys

International Nuclear Information System (INIS)

Kim, M. H.; Lee, M. H.; Park, S. Y.; Jung, Y. H.; We, M. Y.

1999-01-01

For the development of advanced zirconium alloys for nuclear fuel cladding, the corrosion behaviors of zirconium binary alloys were studied on the Zr-xNb, Zr-xSn, and Zr-xCu alloys. The corrosion test were performed in water at 360 deg C, steam at 400 deg C and LiOH at 360 deg C for 45 days. The corrosion behaviors of Zr-xNb was similar to that of Zr-xCu alloys. However, the corrosion behavior of Zr-xSn was different from Zr-xNb and Zr-xCu. The weight gain of Zr-xNb and Zr-xCu was increased with addition of alloying elements. When Sn is added to Zr matrix in range below the solubility limit, the corrosion resistance decrease with increasing Sn-content, while in the range over solubility limit, Sn has an adverse effect on the corrosion resistance. Especially, Zr-xSn alloys showed higher corrosion resistance than Zr-xNb and Zr-xCu alloys in LiOH solution
Flexural behavior of bonded post-tensioned concrete beams under strand corrosion

International Nuclear Information System (INIS)

Zhang, Xuhui; Wang, Lei; Zhang, Jianren; Ma, Yafei; Liu, Yongming

2017-01-01

Highlights: • Flexural behavior of bonded PT beams with strand corrosion is experimental tested. • Cracking, stiffness, ultimate strength, failure & ductility of beams are clarified. • A coefficient is proposed to measure incompatible strain between strand & concrete. - Abstract: An experimental test is performed to investigate the flexural behavior of bonded post-tensioned concrete beams under strand corrosion. Eight beams are designed and subjected to accelerated method to different corrosion levels. The initial stiffness of beams is observed by cyclic loading-unloading test during the corrosion procedure. Corrosion effects on concrete cracking, post-cracking stiffness, ultimate strength, failure mode and ductility are then clarified by the flexural test. And, a coefficient is introduced to quantify the incompatible strain between corroded strand and concrete. Results show that the prestress force loss of strand has almost the linear relation with corrosion loss. Strand corrosion affects slightly the initial stiffness of beam before flexural cracking, but degrades significantly the post-cracking stiffness of beam as the corrosion loss exceeds 27.0%. Slight corrosion of strand has little effects on beams flexural behavior. The severe corrosion, however, decreases the number of crack, changes the failure mode form the concrete crushing to strand rupture, degrades the ductility and the ultimate strength of beams, and leads to the incompatible strain between strand and concrete. In the present test, the incompatible strain decreases about 20% of the flexural strength as the corrosion loss exceeds 27.0%.
Flexural behavior of bonded post-tensioned concrete beams under strand corrosion

Energy Technology Data Exchange (ETDEWEB)

Zhang, Xuhui [College of Civil Engineering and Mechanics, Xiangtan University, 411105 Xiangtan (China); School of Civil Engineering and Architecture, Changsha University of Science & Technology, 410114 Changsha (China); Industry Key Laboratory of Traffic Infrastructure Security Risk Management (CSUST), 410114 Changsha (China); Wang, Lei, E-mail: leiwlei@hotmail.com [School of Civil Engineering and Architecture, Changsha University of Science & Technology, 410114 Changsha (China); Industry Key Laboratory of Traffic Infrastructure Security Risk Management (CSUST), 410114 Changsha (China); Zhang, Jianren; Ma, Yafei [School of Civil Engineering and Architecture, Changsha University of Science & Technology, 410114 Changsha (China); Industry Key Laboratory of Traffic Infrastructure Security Risk Management (CSUST), 410114 Changsha (China); Liu, Yongming [School for Engineering of Matter, Transport and Energy, Arizona State University, 85281 Tempe, AZ (United States)

2017-03-15

Highlights: • Flexural behavior of bonded PT beams with strand corrosion is experimental tested. • Cracking, stiffness, ultimate strength, failure & ductility of beams are clarified. • A coefficient is proposed to measure incompatible strain between strand & concrete. - Abstract: An experimental test is performed to investigate the flexural behavior of bonded post-tensioned concrete beams under strand corrosion. Eight beams are designed and subjected to accelerated method to different corrosion levels. The initial stiffness of beams is observed by cyclic loading-unloading test during the corrosion procedure. Corrosion effects on concrete cracking, post-cracking stiffness, ultimate strength, failure mode and ductility are then clarified by the flexural test. And, a coefficient is introduced to quantify the incompatible strain between corroded strand and concrete. Results show that the prestress force loss of strand has almost the linear relation with corrosion loss. Strand corrosion affects slightly the initial stiffness of beam before flexural cracking, but degrades significantly the post-cracking stiffness of beam as the corrosion loss exceeds 27.0%. Slight corrosion of strand has little effects on beams flexural behavior. The severe corrosion, however, decreases the number of crack, changes the failure mode form the concrete crushing to strand rupture, degrades the ductility and the ultimate strength of beams, and leads to the incompatible strain between strand and concrete. In the present test, the incompatible strain decreases about 20% of the flexural strength as the corrosion loss exceeds 27.0%.
Corrosion behavior of sensitized duplex stainless steel.

Science.gov (United States)

Torres, F J; Panyayong, W; Rogers, W; Velasquez-Plata, D; Oshida, Y; Moore, B K

1998-01-01

The present work investigates the corrosion behavior of 2205 duplex stainless steel in 0.9% NaCl solution after various heat-treatments, and compares it to that of 316L austenitic stainless steel. Both stainless steels were heat-treated at 500, 650, and 800 degrees C in air for 1 h, followed by furnace cooling. Each heat-treated sample was examined for their microstructures and Vickers micro-hardness, and subjected to the X-ray diffraction for the phase identification. Using potentiostatic polarization method, each heat-treated sample was corrosion-tested in 37 degrees C 0.9% NaCl solution to estimate its corrosion rate. It was found that simulated sensitization showed an adverse influence on both steels, indicating that corrosion rates increased by increasing the sensitization temperatures.
Investigation of corrosion behavior of Mg-steel laser-TIG hybrid lap joints

Energy Technology Data Exchange (ETDEWEB)

Liu Liming, E-mail: liulm@dlut.edu.cn [Key Laboratory of Liaoning Advanced Welding and Joining Technology, School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024 (China); Xu Rongzheng [Key Laboratory of Liaoning Advanced Welding and Joining Technology, School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024 (China)

2012-01-15

Highlights: Black-Right-Pointing-Pointer Galvanic corrosion increases the corrosion rate of the Mg-steel joint. Black-Right-Pointing-Pointer Fe splashes lower the corrosion resistance of the joint greatly. Black-Right-Pointing-Pointer The effect of grain refinement on the corrosion behavior of the joint is slight. Black-Right-Pointing-Pointer Ni or Cu interlayer could not improve the corrosion resistance of fusion zone. Black-Right-Pointing-Pointer The arc-sprayed coating could enhance the reliability of weld joint. - Abstract: The paper investigates the corrosion behavior of the lap joint of AZ31 magnesium alloy to Q235 steel with salt solution immersion testing and electrochemical testing. It is demonstrated that grain refinement resulting from the welding process has little effect on the corrosion behavior of the lap joint. However, the cathodic phases formed in the welding process and the galvanic corrosion between magnesium alloy and steel decrease the corrosion resistance of the joint greatly. Besides, neither Cu nor Ni, as filler material, could improve the corrosion resistance of the joint, but the arc-sprayed Al coating acting as a protective layer could.
Behavior of helium gas atoms and bubbles in low activation 9Cr martensitic steels

Science.gov (United States)

Hasegawa, Akira; Shiraishi, Haruki; Matsui, Hideki; Abe, Katsunori

1994-09-01

The behavior of helium-gas release from helium-implanted 9Cr martensitic steels (500 appm implanted at 873 K) during tensile testing at 873 K was studied. Modified 9Cr-1Mo, low-activation 9Cr-2W and 9Cr-0.5V were investigated. Cold-worked AISI 316 austenitic stainless steel was also investigated as a reference which was susceptible helium embrittlement at high temperature. A helium release peak was observed at the moment of rupture in all the specimens. The total quantity of helium released from these 9Cr steels was in the same range but smaller than that of 316CW steel. Helium gas in the 9Cr steels should be considered to remain in the matrix at their lath-packets even if deformed at 873 K. This is the reason why the martensitic steels have high resistance to helium embrittlement.
Behavior of helium gas atoms and bubbles in low activation 9Cr martensitic steels

International Nuclear Information System (INIS)

Hasegawa, Akira; Shiraishi, Haruki; Matsui, Hideki; Abe, Katsunori

1994-01-01

The behavior of helium-gas release from helium-implanted 9Cr martensitic steels (500 appm implanted at 873 K) during tensile testing at 873 K was studied. Modified 9Cr-1Mo, low-activation 9Cr-2W and 9Cr-0.5V were investigated. Cold-worked AISI 316 austenitic stainless steel was also investigated as a reference which was susceptible helium embrittlement at high temperature. A helium release peak was observed at the moment of rupture in all the specimens. The total quantity of helium released from these 9Cr steels was in the same range but smaller than that of 316CW steel. Helium gas in the 9Cr steels should be considered to remain in the matrix at their lath-packets even if deformed at 873 K. This is the reason why the martensitic steels have high resistance to helium embrittlement. ((orig.))
Corrosion behavior of 321 stainless steel in low-acidity uranium nitrate solution

International Nuclear Information System (INIS)

Liao Junsheng; Sun Ying; Zhang Wanglin; Ding Ping; Yang Jiangrong; Wu Lunqiang

2003-01-01

Weighing and electrochemical methods have been used to investigate the high-temperature uniform corrosion and electrochemical corrosion behavior of lCr18Ni9Ti (321) stainless steel in uranium nitrate solution at different concentrations and pH values. The uniform corrosion results showed that the corrosion rate of 321 stainless steel was less than 0.04 g/m 2 .h, and the visible change of surface smoothness was not observed through 960 h. It was perfect corrosion-resisting in obtained conditions. The electro-chemical corrosion behavior study has been performed to investigate 321 stainless steel in uranium nitrate solutions of the dissolved and saturated oxygen. The corrosion potential and corrosion current density were obtained. Auger photoelectron spectroscopy for measurement of uranium in specimen was used to indicate that uranium is in corrosion product. The corrosion film was measured by Ar ion gun sputter, and the thickness is 10-15 nm. (authors)
Corrosion and Corrosion-Fatigue Behavior of 7075 Aluminum Alloys Studied by In Situ X-Ray Tomography

Science.gov (United States)

Stannard, Tyler

7XXX Aluminum alloys have high strength to weight ratio and low cost. They are used in many critical structural applications including automotive and aerospace components. These applications frequently subject the alloys to static and cyclic loading in service. Additionally, the alloys are often subjected to aggressive corrosive environments such as saltwater spray. These chemical and mechanical exposures have been known to cause premature failure in critical applications. Hence, the microstructural behavior of the alloys under combined chemical attack and mechanical loading must be characterized further. Most studies to date have analyzed the microstructure of the 7XXX alloys using two dimensional (2D) techniques. While 2D studies yield valuable insights about the properties of the alloys, they do not provide sufficiently accurate results because the microstructure is three dimensional and hence its response to external stimuli is also three dimensional (3D). Relevant features of the alloys include the grains, subgrains, intermetallic inclusion particles, and intermetallic precipitate particles. The effects of microstructural features on corrosion pitting and corrosion fatigue of aluminum alloys has primarily been studied using 2D techniques such as scanning electron microscopy (SEM) surface analysis along with post-mortem SEM fracture surface analysis to estimate the corrosion pit size and fatigue crack initiation site. These studies often limited the corrosion-fatigue testing to samples in air or specialized solutions, because samples tested in NaCl solution typically have fracture surfaces covered in corrosion product. Recent technological advancements allow observation of the microstructure, corrosion and crack behavior of aluminum alloys in solution in three dimensions over time (4D). In situ synchrotron X-Ray microtomography was used to analyze the corrosion and cracking behavior of the alloy in four dimensions to elucidate crack initiation at corrosion pits
Online monitoring of corrosion behavior in molten metal using laser-induced breakdown spectroscopy

Science.gov (United States)

Zeng, Qiang; Pan, Congyuan; Li, Chaoyang; Fei, Teng; Ding, Xiaokang; Du, Xuewei; Wang, Qiuping

2018-04-01

The corrosion behavior of structure materials in direct contact with molten metals is widespread in metallurgical industry. The corrosion of casting equipment by molten metals is detrimental to the production process, and the corroded materials can also contaminate the metals being produced. Conventional methods for studying the corrosion behavior by molten metal are offline. This work explored the application of laser-induced breakdown spectroscopy (LIBS) for online monitoring of the corrosion behavior of molten metal. The compositional changes of molten aluminum in crucibles made of 304 stainless steel were obtained online at 1000 °C. Several offline techniques were combined to determine the corrosion mechanism, which was highly consistent with previous studies. Results proved that LIBS was an efficient method to study the corrosion mechanism of solid materials in molten metal.
Corrosion Behavior of Heat Affected Zone of AISI 321 stainless steel

International Nuclear Information System (INIS)

Ahn, Yong Sik; Park, Hwa Soon; Kim, Yeong Hwan; Won, Tae Yeon; Lee, Sang Lae

1994-01-01

Intergranular corrosion behavior of heat affected zone(HAZ) has been investigated for Ti-stabilized austenitic stainless steel AISI 321. It was observed that grain boundaries at HAZ of the steel with Ti/C ratio of 6.2 were corroded significantly after sensitization heat treatment. The increase of the Ti/C ratio up to 9.6 results in the evident decrease of intergranular corrosion. Weld simulation and intergranular corrosion test in 65% HNO 3 was performed. Influence of various thermal cycles on the intergranular corrosion was investigated. These results are discussed in terms of the behavior of TiC and Cr 23 C 6 precipitates

Analysis of corrosion behavior of KOFA cladding

International Nuclear Information System (INIS)

Lee, Chan Bock; Kim, Ki Hang; Seo, Keum Seok; Chung, Jin Gon

1994-01-01

The corrosion behavior of KOFA cladding was analyzed using the oxide measurement data of KOFA fuel irradiated up to the fuel rod burnup of 35,000 MWD/MTU for two cycles in Kori-2. Even though KOFA cladding is a standard Zircaloy-4 manufactured by Westinghouse according to the Siemens/KWU's HCW (Highly Cold Worked) standard Zircaloy-4 specification, it was expected that in-pile corrosion behavior of KOFA cladding would not be equivalent to that of Siemens/KWU's cladding due to the differences in such manufacturing processes as cold work and heat treatment. The analysis of measured KOFA cladding oxidation showed that oxidation of KOFA cladding is at least 19 % lower than the design analysis based upon Siemens/KWU's HCW standard Zircaloy-4 cladding. Lower corrosion of KOFA cladding seems to result from the differences in the manufacturing processes and chemical composition although the burnup and oxide layer thickness of the measured fuel rods is relatively low and the amount of the oxidation data base is small
Corrosion behavior of the aluminum under the simulated environmental condition of low-level waste. Part 1. Effect of dry storage on the corrosion behavior of pre-filmed specimen

International Nuclear Information System (INIS)

Fujiwara, Kazutoshi; Tani, Junichi; Tanaka, Yukihisa

2016-01-01

Aluminum alloy remains in the Low-level Radioactive Waste (LLW) generated at nuclear facilities. It is well known that aluminum reactors to the alkaline component of cement, or water, generating hydrogen gas. For the saft management of radioactive waste disposal facilities, it is necessary to evaluate the corrosion behavior of aluminum and the hydrogen generation behavior in consideration with transition of the burial environment. In the present study, the corrosion behaviors of aluminum in the alkaline solutions at 15degC were evaluated. Pure aluminium was used as specimen. The test solutions used in this study were water in equilibrium with the cement paste grain produced from ordinary portland cement (OPC). The temperature and pH of solutions were 15degC and 11.5-12.5, respectively. In order to make a corrosion product on the surface, the specimens were immersed in the solution for about 3000 hours as pretreatment. The corrosion behaviors of pre-filmed specimen were evaluated after drying. The test results shows that the maximum in a corrosion rate appeared in early stages and it decrease to less than 1x10 -3 mm/y. The maximum did not appear when the corrosion products were formed in the OPC grain as conditions similar to actual environment. (author)
The corrosion behavior of iron and aluminum under waste disposal conditions

International Nuclear Information System (INIS)

Fujisawa, R.; Cho, T.; Sugahara, K.; Takizawa, Y.; Hironaga, M.

1997-01-01

The generation of hydrogen gas from metallic waste in corrosive disposal environment is an important issue for the safety analysis of low-level radioactive waste disposal facilities in Japan. In particular iron and aluminum are the possibly important elements regarding the gas generation. However, the corrosion behavior of these metals has not been sufficiently investigated under the highly alkaline non-oxidizing disposal conditions yet. The authors studied the corrosion behavior of iron and aluminum under simulated disposal environments. The quantity of hydrogen gas generated from iron was measured in a closed cell under highly alkaline non-oxidizing conditions. The observed corrosion rate of iron in the initial period of immersion was 4 nm/year at 15 C, 20 nm/year at 30 C, and 200 nm/year at 45 C. The activation energy was found to be 100 kJ/mol from Arrhenius plotting of the above corrosion rates. The corrosion behavior of aluminum was studied under an environment simulating conditions in which aluminum was solidified with mortar. In the initial period aluminum corroded rapidly with a corrosion rate of 20 mm/year. However, the corrosion rate decreased with time, and after 1,000 hours the rate reached 0.001 to 0.01 mm/year. Thus the authors obtained data on hydrogen gas generation from iron and aluminum under the disposal environment relevant to the safety analysis of low-level radioactive disposal facilities in Japan
The corrosion behavior of hafnium in high-temperature-water environments

Energy Technology Data Exchange (ETDEWEB)

Rishel, D.M.; Smee, J.D.; Kammenzind, B.F.

1999-10-01

The high-temperature-water corrosion performance of hafnium is evaluated. Corrosion kinetic data are used to develop correlations that are a function of time and temperature. The evaluation is based on corrosion tests conducted in out-of-pile autoclaves and in out-of-flux locations of the Advanced Test Reactor (ATR) at temperatures ranging from 288 to 360 C. Similar to the corrosion behavior of unalloyed zirconium, the high-temperature-water corrosion response of hafnium exhibits three corrosion regimes: pretransition, posttransition, and spalling. In the pretransition regime, cubic corrosion kinetics are exhibited, whereas in the posttransition regime, linear corrosion kinetics are exhibited. Because of the scatter in the spalling regime data, it is not reasonable to use a best fit of the data to describe spalling regime corrosion. Data also show that neutron irradiation does not alter the corrosion performance of hafnium. Finally, the data illustrate that the corrosion rate of hafnium is significantly less than that of Zircaloy-2 and Zircaloy-4.
Corrosion behavior of Cu during graphene growth by CVD

International Nuclear Information System (INIS)

Dong, Yuhua; Liu, Qingqing; Zhou, Qiong

2014-01-01

Highlights: • Graphene films were deposited on the Cu by chemical vapor deposition method. • Annealing affects the corrosion property of Cu. • Graphene films improve corrosion performance of Cu for a short period of time. - Abstract: The corrosion performance of Cu samples may be affected by annealing at high temperatures during graphene growth via the chemical vapor deposition method. In this study, multiple graphene films were deposited on Cu and characterized by Raman spectroscopy and transmission electron microscopy. The corrosion behavior of Cu immersed in 3.5 wt.% NaCl solution was investigated using electrochemical impedance spectroscopy. The Cu morphology was observed by optical microscopy and scanning electron microscopy. Results indicated that annealing affects the corrosion process of Cu. The presence of graphene films on the Cu substrate improved the corrosion performance of the material for a short period of time
Corrosion Behavior of Brazed Zinc-Coated Structured Sheet Metal

Directory of Open Access Journals (Sweden)

A. Nikitin

2017-01-01

Full Text Available Arc brazing has, in comparison to arc welding, the advantage of less heat input while joining galvanized sheet metals. The evaporation of zinc is reduced in the areas adjacent to the joint and improved corrosion protection is achieved. In the automotive industry, lightweight design is a key technology against the background of the weight and environment protection. Structured sheet metals have higher stiffness compared to typical automobile sheet metals and therefore they can play an important role in lightweight structures. In the present paper, three arc brazing variants of galvanized structured sheet metals were validated in terms of the corrosion behavior. The standard gas metal arc brazing, the pulsed arc brazing, and the cold metal transfer (CMT® in combination with a pulsed cycle were investigated. In experimental climate change tests, the influence of the brazing processes on the corrosion behavior of galvanized structured sheet metals was investigated. After that, the corrosion behavior of brazed structured and flat sheet metals was compared. Because of the selected lap joint, the valuation of damage between sheet metals was conducted. The pulsed CMT brazing has been derived from the results as the best brazing method for the joining process of galvanized structured sheet metals.
Research on A3 steel corrosion behavior of basic magnesium sulfate cement

Science.gov (United States)

Xing, Sainan; Wu, Chengyou; Yu, Hongfa; Jiang, Ningshan; Zhang, Wuyu

2017-11-01

In this paper, Tafel polarization technique is used to study the corrosion behavior of A3 steel basic magnesium sulfate, and then analyzing the ratio of raw materials cement, nitrites rust inhibitor and wet-dry cycle of basic magnesium sulfate corrosion of reinforced influence, and the steel corrosion behavior of basic magnesium sulfate compared with magnesium oxychloride cement and Portland cement. The results show that: the higher MgO/MgSO4 mole ratio will reduce the corrosion rate of steel; Too high and too low H2O/MgSO4 mole ratio may speed up the reinforcement corrosion effect; Adding a small amount of nitrite rust and corrosion inhibitor, not only can obviously reduce the alkali type magnesium sulfate in the early hydration of cement steel bar corrosion rate, but also can significantly reduce dry-wet circulation under the action of alkali type magnesium sulfate cement corrosion of reinforcement effect. Basic magnesium sulfate cement has excellent ability to protect reinforced, its long-term corrosion of reinforcement effect and was equal to that of Portland cement. Basic magnesium sulfate corrosion of reinforced is far below the level in the MOC in the case.
Corrosion behavior of zinc-nickel alloy electrodeposited coatings

Energy Technology Data Exchange (ETDEWEB)

Fabri Miranda, F.J. [USIMINAS, Ipatinga, Minas Gerais (Brazil); Margarit, I.C.P.; Mattos, O.R.; Barcia, O.E. [UFRJ, Rio de Janeiro (Brazil); Wiart, R. [Univ. Pierre et M. Curie, Paris (France)

1999-08-01

Various types of zinc-electrocoated steel sheets are used to improve the durability of car bodies. Among these coatings, the Zn-Ni alloy has higher corrosion resistance than pure Zn, as well as better welding and painting properties. The corrosion mechanism of the Zn-Ni alloy has been investigated mainly on the basis of accelerated tests and electrochemical measurements. There are few data about long-term corrosion tests. In the present study, the behavior of unpainted Zn-Ni alloy coated steel was studied during 3 years of exposure in industrial and marine environments. Electrochemical impedance spectroscopy (EIS) and surface analysis (scanning electron microscopy [SEM] and Auger electron spectroscopy [AES]) were the experimental techniques used. Long-term atmospheric corrosion mechanism of Zn-Ni coatings was discussed and compared with that proposed based on short-term tests.
Effect of compression deformation on the microstructure and corrosion behavior of magnesium alloys

International Nuclear Information System (INIS)

Snir, Y.; Ben-Hamu, G.; Eliezer, D.; Abramov, E.

2012-01-01

Highlights: ► Metallurgical features (mainly twinning, dislocation accumulation, and dynamic recrystallization). ► The thermo-mechanical state (amount of deformation and its temperature). ► The corrosion behavior of wrought Mg-alloys. This correlation was emphasized by the mechanical behavior measured through micro-hardness. ► Microstructural changes during deformation, and potentio-dynamic corrosion tests were correlated. - Abstract: The effect of deformation on the corrosion and mechanical behavior of wrought Mg-alloys AZ31, AM50, and ZK60 was investigated. The materials’ behavior was correlated to the changes in metallurgical features, during compression, into different amounts of deformation at three temperatures: 250° C, 280° C, and 350° C. The metallurgical features were monitored by optical microscope, scanning electron microscope (SEM), and transmission electron microscopy (TEM). It was observed that there is a very strong correlation between three features: 1. metallurgical features (mainly twinning, dislocation accumulation, and dynamic recrystallization); 2. The thermo-mechanical state (amount of deformation and its temperature); and 3. The corrosion behavior of wrought Mg-alloys. This correlation was emphasized by the mechanical behavior measured through micro-hardness. Microstructural changes during deformation, and potentio-dynamic corrosion tests were correlated. These results show that studies on the effect of thermo-mechanical state (related to the microstructure) on the corrosion behavior of wrought Mg-alloys are essential in order to optimize their applicability to plastic forming processes.
The effects of bacteria on the corrosion behavior of carbon steel in compacted bentonite

International Nuclear Information System (INIS)

Nishimura, T.; Wada, R.; Nishimoto, H.; Fujiwara, K.; Taniguchi, N.; Honda, A.

1999-10-01

As a part of evaluation of corrosion life of carbon steel overpack, the experimental studies have been performed on the effects of bacteria on the corrosion behavior of carbon steel in compacted bentonite using iron bacteria (IB) as a representative oxidizing bacteria and sulphur reducing bacteria (SRB) as a representative reducing bacteria. The results of the experimental studies showed that; The activity of SRB was low in compacted bentonite in spite of applying suitable condition for the action of bacteria such as temperature and nutritious solution. Although the corrosion behavior of carbon steel was affected by the existence of bacteria in simple solution, the corrosion rates of carbon steel in compacted bentonite were several μ m/year -10 μ m/year irrespective of coexistence of bacteria and that the corrosion behavior was not affected by the existence of bacteria. According to these results, it was concluded that the bacteria would not affect the corrosion behavior of carbon steel overpack under repository condition. (author)
Assessment of Embrittlement of VHTR Structural Alloys in Impure Helium Environments

Energy Technology Data Exchange (ETDEWEB)

Crone, Wendy; Cao, Guoping; Sridhara, Kumar

2013-05-31

The helium coolant in high-temperature reactors inevitably contains low levels of impurities during steady-state operation, primarily consisting of small amounts of H{sub 2}, H{sub 2}O, CH{sub 4}, CO, CO{sub 2}, and N{sub 2} from a variety of sources in the reactor circuit. These impurities are problematic because they can cause significant long-term corrosion in the structural alloys used in the heat exchangers at elevated temperatures. Currently, the primary candidate materials for intermediate heat exchangers are Alloy 617, Haynes 230, Alloy 800H, and Hastelloy X. This project will evaluate the role of impurities in helium coolant on the stress-assisted grain boundary oxidation and creep crack growth in candidate alloys at elevated temperatures. The project team will: • Evaluate stress-assisted grain boundary oxidation and creep crack initiation and crack growth in the temperature range of 500-850°C in a prototypical helium environment. • Evaluate the effects of oxygen partial pressure on stress-assisted grain boundary oxidation and creep crack growth in impure helium at 500°C, 700°C, and 850°C respectively. • Characterize the microstructure of candidate alloys after long-term exposure to an impure helium environment in order to understand the correlation between stress-assisted grain boundary oxidation, creep crack growth, material composition, and impurities in the helium coolant. • Evaluate grain boundary engineering as a method to mitigate stress-assisted grain boundary oxidation and creep crack growth of candidate alloys in impure helium. The maximum primary helium coolant temperature in the high-temperature reactor is expected to be 850-1,000°C.Corrosion may involve oxidation, carburization, or decarburization mechanisms depending on the temperature, oxygen partial pressure, carbon activity, and alloy composition. These corrosion reactions can substantially affect long-term mechanical properties such as crack- growth rate and fracture
Correlation between the oxide impedance and corrosion behavior of Zr-Nb-Sn-Fe-Cu alloys

Science.gov (United States)

Park, Sang-Yoon; Lee, Myung-Ho; Jeong, Yong-Hwan; Jung, Youn-Ho

2004-12-01

The correlation between the oxide impedance and corrosion behavior of two series of Zr-Nb-Sn-Fe-Cu alloys was evaluated. Corrosion tests were performed in a 70 ppm LiOH aqueous solution at 360°C for 300 days. The results of the corrosion tests revealed that the corrosion behavior of the alloys depended on the Nb and Sn content. The impedance characteristics for the pre- and post-transition oxide layers formed on the surface of the alloys were investigated in sulfuric acid at room temperature. From the results, a pertinent equivalent circuit model was preferably established, explaining the properties of double oxide layers. The impedance of the oxide layers correlated with the corrosion behavior; better corrosion resistance always showed higher electric resistance for the inner layers. It is thus concluded that a pertinent equivalent circuit model would be useful for evaluating the long-term corrosion behavior of Zr-Nb-Sn-Fe-Cu alloys.
Effect of microstructure on corrosion behavior of Ag-30Cu-27Sn alloy in vitro media

International Nuclear Information System (INIS)

Salehisaki, Mehdi; Aryana, Maryam

2014-01-01

Highlights: • High cooling rates decrease the number of Ag intermetallic particles in Cu-rich phase. • Increasing cooling rate improves corrosion behavior of Ag-30Cu-27Sn dental alloy. • Cathode/anode ratio in Cu-rich phases determines the corrosion behavior of alloy. - Abstract: In the present work, three simple heat treatment cycles were used to study the effects of microstructure on electrochemical corrosion behavior of Ag-30Cu-27Sn dental alloy. The electrochemical impedance spectroscopy (EIS) measurements and potentiodynamic polarization tests were carried out to investigate the corrosion behavior of as-cast and heat treated samples in synthetic saliva solution. The presence of intermetallic compounds were studied by X-ray diffraction method (XRD) and scanning electron microscopy (SEM) with energy dispersive X-ray detector (EDAX). The microstructural observations and electrochemical corrosion results revealed that, increasing the cooling rate improves the corrosion behavior of under investigation samples. Improvement of the corrosion behavior is attributed to reducing the area of fine distributed Ag 3 Sn islands in the Cu-rich matrix which decrease the cathode/anode ratio of microgalvanic cells
In vitro corrosion behavior of bioceramic, metallic, and bioceramic-metallic coated stainless steel dental implants.

Science.gov (United States)

Fathi, M H; Salehi, M; Saatchi, A; Mortazavi, V; Moosavi, S B

2003-05-01

The most common metals and alloys used in dentistry may be exposed to a process of corrosion in vivo that make them cytotoxic. The biocompatibility of dental alloys is primarily related to their corrosion behavior. The aim of this work was to evaluate the corrosion behavior and thus the biocompatibility of the uncoated and coated stainless steels and compare the effect of type of coatings on corrosion behavior. Three types of coatings, hydroxyapatite (HA), titanium (Ti), and a double-layer HA/Ti on AISI 316L stainless steel were made. HA coating was produced using plasma-spraying technique and Ti coating was made using physical vapor deposition process. In order to perform a novel double-layer composite coating, a top layer of HA was plasma-sprayed over a physical vapor deposited Ti layer on AISI 316L stainless steel. Structural characterization techniques including XRD, SEM and EDX were used to investigate the microstructure, morphology and crystallinity of the coatings. Electrochemical potentiodynamic tests were performed in physiological solutions in order to determine and compare the corrosion behavior of the coated and uncoated specimens as an indication of biocompatibility. Double-layer HA/Ti coating on AISI 316L SS had a positive effect on improvement of corrosion behavior. The decrease in corrosion current densities was significant for these coated specimens and was much lower than the values obtained for uncoated and single HA coated specimens. Ti coating on AISI 316L SS also has a beneficial effect on corrosion behavior. The results were compared with the results of corrosion behavior of HA coated commercially pure titanium (cpTi) and uncoated cpTi. These results demonstrated that the double-layer HA/Ti coated 316L SS can be used as an endodontic implant and two goals including improvement of corrosion resistance and bone osteointegration can be obtained simultaneously.
Corrosion behavior of magnesium-graphene composites in sodium chloride solutions

Directory of Open Access Journals (Sweden)

Muhammad Rashad

2017-09-01

Full Text Available Coating of graphene and graphene/polymer composites on metals improves the corrosion resistance of metal substrates. On other hand, graphene embedded inside metal (especially Mg matrices increases or decreases corrosion, is a crucial factor and must be explored. In present study, electrochemical behaviors of magnesium alloys (AZ31 and AZ61 and their composites reinforced with graphene nanoplatelets (GNPs were carried out in 3.5% NaCl solution by polarization method. The surface morphology of composites before and after corrosion tests were analyzed using scanning electron microscopy. Experimental results revealed that presence of graphene nanoplatelets in different matrices decrease corrosion resistance of composites. This may be attributed to presence of graphene nanoplatelets which activates the corrosion of magnesium/alloys due to the occurrence of galvanic corrosion and this effect increases with increasing graphene nanoplatelets content. Further, an appropriate model describing the corrosion mechanism was proposed.
The effect of heat treatments on the corrosion behavior of Zircaloy-4

International Nuclear Information System (INIS)

Zhou Bangxin; Zhao Wenjin; Miao Zhi; Pan Shufang; Li Cong; Jiang Yourong

1996-06-01

The effect of penultimate annealing temperature and cooling rate on the corrosion behavior of Zircaloy-4 cladding tube has been investigated. Both nodular corrosion and uniform corrosion resistance can be improved obviously after changing the heat treatment from the original annealing at 650 degree C to quenching from 830 degree C (upper temperature of alpha phase region or lower temperature of beta phase region). Although the nodular corrosion resistance can be improved obviously after quenching from beta phase, there was a second transition in the variation between weight gain and exposure time, which shows a poor uniform corrosion resistance after a long exposure time during the autoclave tests. The main factor of affecting corrosion behavior is the solid solution contents of Fe and Cr in alpha zirconium rather than the size of second phase particles. About 200 μg/g Fe and Cr super saturated solid solution in alpha zirconium could get good uniform and nodular corrosion resistance, but much more solid solution contents of Fe and Cr in alpha zirconium could bring about a trend toward poor uniform corrosion resistance for long-term exposure time. (14 refs., 10 figs., 1 tab.)
Effect of Ti3+ ion on the Corrosion Behavior of Alloy 600

International Nuclear Information System (INIS)

Lee, Chang Bong; Lim, Han Gwi; Kim, Bok Hee; Kim, Ki Ju

1999-01-01

Alloy 600 has been widely used as a steam generator tubing material in pressurized water reactors(PWRs) nuclear power plants. Corrosion of steam generator tubing mainly occurs on the secondary water side. The purpose of this work is primarily concerned with examining the effect of Ti 3+ ion concentrations on the corrosion behavior of the Alloy 600 steam generator tubing material. Corrosion behavior of the Alloy 600 steam generator tubing material was studied in aqueous solutions with varying Ti 3+ ion concentration at room temperature. Potentiodynamic and potentiostatic polarization techniques were used to determine the corrosion and pitting potentials for the Alloy 600 test material. The addition of Ti 3+ ion to 1000ppm, showed inhibition effect on the corrosion of Alloy 600. But the corrosion of Alloy 600 was accelerated when the concentration of Ti 3+ ion exceeded 1000ppm, it is assumed that the effect of general corrosion of Alloy 600 is more sensitive than pitting corrosion. It is considered that the passive film which was formed on the Alloy 600 surface in the 100ppm Ti 3+ ion containing solution is mainly consisted of TiO 2
An electrochemical study of the corrosion behavior of primer coated 2219-T87 aluminum

Science.gov (United States)

Danford, M. D.; Higgins, R. H.

1985-01-01

The corrosion behavior for 2219-T87 aluminum coated with various primers, including those used for the external tank and solid rocket boosters of the Space Shuttle Transportation System, were investigated using electrochemical techniques. Corrosion potential time, polarization resistance time, electrical resistance time, and corrosion rate time measurements were all investigated. It was found that electrical resistance time and corrosion rate time measurement were most useful for studying the corrosion behavior of painted aluminum. Electrical resistance time determination give useful information concerning the porosity of paint films, while corrosion rate time curves give important information concerning overall corrosion rates and corrosion mechanisms. In general, the corrosion rate time curves all exhibited at least one peak during the 30 day test period, which was attributed, according to the proposed mechanisms, to the onset of the hydrogen evolution reaction and the beginning of destruction of the protective properties of the paint film.
Fabrication and corrosion behavior of fresh porous silicon in sodium hydroxide solution

International Nuclear Information System (INIS)

Lai, Chuan; Li, Xueming; Zhang, Daixiong; Xiang, Zhen; Yang, Wenjing; Guo, Xiaogang

2014-01-01

The corrosion behavior of fresh porous silicon (f-PS) in sodium hydroxide (NaOH) solution in the presence and absence of ethanol was studied by weight loss measurements and scanning electron microscope (SEM) technique. The phenomena and progress of f-PS corrosion in 1.0 M NaOH at 318 K was obtained and described. Weight loss measurements show that the corrosion rate increases with increasing temperature and concentration of NaOH solution. Meanwhile, the corrosion rate first increases with increasing volume ratio of ethanol in 1.0 M NaOH, and then decreases. Additionally, the thermodynamic and kinetic parameters (E a , A, ΔH a and ΔS a ) for f-PS corrosion were obtained and discussed. And the effect factors (T, c and v) of f-PS corrosion in NaOH solution were studied in this paper. - Highlights: • The corrosion behavior of f-PS in NaOH solution was studied for the first time. • Phenomena and progress of f-PS corrosion in NaOH solution was obtained and described. • The effect factors (T, c and v) of f-PS corrosion in NaOH solution were studied. • The kinetic and thermodynamic parameters were obtained and discussed. • The corrosion rate can be improved by adding ethanol into NaOH solution
Corrosion Behavior of SA508 Coupled with and without Magnetite in Chemical Cleaning Environments

International Nuclear Information System (INIS)

Son, Yeong-Ho; Jeon, Soon-Hyeok; Song, Geun Dong; Hur, Do Haeng; Lee, Jong-Hyeon

2017-01-01

To mitigate these problems, chemical cleaning process has been widely used. However, the chemical cleaning solution can affect the corrosion of SG structural materials as well as the magnetite dissolution. During the chemical cleaning process, the galvanic corrosion between SG materials and magnetite is also anticipated because they are in electrical connection. However, the corrosion measurement or monitoring for the materials has been performed without consideration of galvanic effect coupled with magnetite during the chemical cleaning process. In this study, the effect of temperature and EDTA concentration on the corrosion behavior of SA508 tubesheet material with and without magnetite was studied in chemical cleaning solutions. The galvanic corrosion behavior between SA508 and magnetite is predicted by using the mixed potential theory and its effect on the corrosion rate of SA508 is also discussed. By newly designed immersion test, it was confirmed that the extent of galvanic corrosion effect between SA508 and magnetite increased with increasing temperature and EDTA concentration. The galvanic corrosion behavior of SA508 coupled with magnetite in chemical cleaning environments was predicted by the mixed potential theory and verified by ZRA and LP technique. Galvanic coupling increased the corrosion rate of SA508 due to the shift in its potential to the anodic direction. Therefore, the galvanic corrosion effect between SA508 and magnetite should be considered when the corrosion measurement is performed during the chemical cleaning process in steam generators.

Heat Exchanger Tube to Tube Sheet Joints Corrosion Behavior

Directory of Open Access Journals (Sweden)

M. Iancu

2013-03-01

Full Text Available Paper presents the studies made by the authors above the tube to tube sheet fittings of heat exchanger with fixed covers from hydrofining oil reforming unit. Tube fittings are critical zones for heat exchangers failures. On a device made from material tube and tube sheet at real joints dimensions were establish axial compression force and traction force at which tube is extracted from expanded joint. Were used two shapes joints with two types of fittings surfaces, one with smooth hole of tube sheet and other in which on boring surface we made a groove. From extracted expanded tube zones were made samples for corrosion tests in order to establish the corrosion rate, corrosion potential and corrosion current in working mediums such as hydrofining oil and industrial water at different temperatures. The corrosion rate values and the temperature influence are important to evaluate joints durability and also the results obtained shows that the boring tube sheet shape with a groove on hole tube shape presents a better corrosion behavior then the shape with smooth hole tube sheet.
Corrosion behavior of carbon steel in wet Na-bentonite medium

International Nuclear Information System (INIS)

Yeon, Jae-Won; Ha, Young-Kyoung; Choi, In-Kyu; Chun, Kwan-Sik

1996-01-01

Corrosion behaviors of carbon steel in wet Na-bentonite medium were studied. Corrosion rate of carbon steel in wet bentonite was measured to be 20 μm/yr at 25 deg C using the AC impedance technique. This value is agreed with that obtained by weight loss at 40 deg C for 1 year. The effect of bicarbonate ion on the corrosion of carbon steel in wet bentonite was also evaluated. The carbon steels in wet bentonite having 0.001, 0.01, and 0.1 M concentration of bicarbonate ion gave corrosion rates of 20, 8, and 0.2 μm/yr, respectively. Corrosion potentials of specimens were also measured and compared with the AC impedance results. Both results indicated that bicarbonate ion could effectively reduce the corrosion rate of carbon steels in bentonite due to the formation of protective layer on the carbon steel. (author)
Electrochemical corrosion behavior of gas atomized Al–Ni alloy powders

International Nuclear Information System (INIS)

Osório, Wislei R.; Spinelli, José E.; Afonso, Conrado R.M.; Peixoto, Leandro C.; Garcia, Amauri

2012-01-01

Highlights: ► Spray-formed Al–Ni alloy powders have cellular microstructures. ► Porosity has no deleterious effect on the electrochemical corrosion behavior. ► Better pitting corrosion resistance is related to a fine powder microstructure. ► A coarse microstructure can be related to better general corrosion resistance. - Abstract: This is a study describing the effects of microstructure features of spray-formed Al–Ni alloy powders on the electrochemical corrosion resistance. Two different spray-formed powders were produced using nitrogen (N 2 ) gas flow (4 and 8 bar were used). Electrochemical impedance spectroscopy (EIS), potentiodynamic anodic polarization techniques and an equivalent circuit analysis were used to evaluate the electrochemical behavior in a dilute 0.05 M NaCl solution at room temperature. It was found that a N 2 gas pressure of 8 bar resulted in a microstructure characterized by a high fraction of small powders and fine cell spacings, having improved pitting potential but higher corrosion current density when compared with the corresponding results of a coarser microstructure array obtained under a lower pressure. A favorable effect in terms of current density and oxide protective film formation was shown to be associated with the coarser microstructure, however, its pitting potential was found to be lower than that of the finer microstructure.
The corrosion and stress corrosion cracking behavior of a novel alumina-forming austenitic stainless steel in supercritical water

Energy Technology Data Exchange (ETDEWEB)

Sun, Hongying [School of Mechanical Engineering, Anyang Institute of Technology, Anyang 455002 (China); Yang, Haijie [Modern Engineering Training Center, Anyang Institute of Technology, Anyang 455002 (China); Wang, Man [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Giron-Palomares, Benjamin [School of Mechanical Engineering, Anyang Institute of Technology, Anyang 455002 (China); Zhou, Zhangjian, E-mail: zhouzhj@mater.ustb.edu.cn [School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Zhang, Lefu [School of Nuclear Science and Engineering, Shanghai Jiaotong University, No 800 Dongchuan Road, Shanghai (China); Zhang, Guangming, E-mail: ustbzgm@163.com [School of Automobile & Transportation, Qingdao Technological University, Qingdao 266520 (China)

2017-02-15

The general corrosion and stress corrosion behavior of Fe-27Ni-15Cr-5Al-2Mo-0.4Nb alumina-forming austenitic (AFA) steel were investigated in supercritical water under different conditions. A double layer oxide structure was formed: a Fe-rich outer layer (Fe{sub 2}O{sub 3} and Fe{sub 3}O{sub 4}) and an Al-Cr-rich inner layer. And the inner layer has a low growth rate with exposing time, which is good for improvement of corrosion resistance. Additionally, some internal nodular Al-Cr-rich oxides were also observed, which resulted in a local absence of inner layer. Stress corrosion specimens exhibited a combination of high strength, good ductility and low susceptibility. The stress strength and elongation was reduced by increasing temperature and amount of dissolved oxygen. In addition, the corresponding susceptibility was increased with decreased temperatures and increased oxygen contents. - Highlights: • The general corrosion and SCC in SCW of the AFA steel have been limited reported. • Fe-rich inner and Al-Cr-rich outer layers are formed in 650 °C/25 MPa/10 ppb SCW. • The SCC behavior exhibits a combination of high strength and good ductility. • Strength and elongation are lowered by increase of temperature and oxygen content. • The AFA steel shows low SCC susceptibility and a superior corrosion resistance.
The corrosion and stress corrosion cracking behavior of a novel alumina-forming austenitic stainless steel in supercritical water

International Nuclear Information System (INIS)

Sun, Hongying; Yang, Haijie; Wang, Man; Giron-Palomares, Benjamin; Zhou, Zhangjian; Zhang, Lefu; Zhang, Guangming

2017-01-01

The general corrosion and stress corrosion behavior of Fe-27Ni-15Cr-5Al-2Mo-0.4Nb alumina-forming austenitic (AFA) steel were investigated in supercritical water under different conditions. A double layer oxide structure was formed: a Fe-rich outer layer (Fe 2 O 3 and Fe 3 O 4 ) and an Al-Cr-rich inner layer. And the inner layer has a low growth rate with exposing time, which is good for improvement of corrosion resistance. Additionally, some internal nodular Al-Cr-rich oxides were also observed, which resulted in a local absence of inner layer. Stress corrosion specimens exhibited a combination of high strength, good ductility and low susceptibility. The stress strength and elongation was reduced by increasing temperature and amount of dissolved oxygen. In addition, the corresponding susceptibility was increased with decreased temperatures and increased oxygen contents. - Highlights: • The general corrosion and SCC in SCW of the AFA steel have been limited reported. • Fe-rich inner and Al-Cr-rich outer layers are formed in 650 °C/25 MPa/10 ppb SCW. • The SCC behavior exhibits a combination of high strength and good ductility. • Strength and elongation are lowered by increase of temperature and oxygen content. • The AFA steel shows low SCC susceptibility and a superior corrosion resistance.
Investigations on Microstructure and Corrosion behavior of Superalloy 686 weldments by Electrochemical Corrosion Technique

Science.gov (United States)

Arulmurugan, B.; Manikandan, M.

2018-02-01

In the present study, microstructure and the corrosion behavior of Nickel based superalloy 686 and its weld joints has been investigated by synthetic sea water environment. The weldments were fabricated by Gas Tungsten Arc Welding (GTAW) and Pulsed Current Gas Tungsten Arc Welding (PCGTAW) techniques with autogenous mode and three different filler wires (ERNiCrMo-4, ERNiCrMo-10 and ERNiCrMo-14). Microstructure and Scanning electron microscope examination was carried out to evaluate the structural changes in the fusion zones of different weldments. Energy Dispersive X-ray Spectroscopy (EDS) analysis was carried out to evaluate the microsegregation of alloying elements in the different weld joints. Potentiodynamic polarization study was experimented on the base metal and weld joints in the synthetic sea water environment to evaluate the corrosion rate. Tafel’s interpolation technique was used to obtain the corrosion rate. The microstructure examination revealed that the fine equiaxed dendrites were observed in the pulsed current mode. EDS analysis shows the absence of microsegregation in the current pulsing technique. The corrosion rates of weldments are compared with the base metal. The results show that the fine microstructure with the absence of microsegregation in the PCGTA weldments shows improved corrosion resistance compared to the GTAW. Autogenous PCGTAW shows higher corrosion resistance irrespective of all weldments employed in the present study.
Electrochemical corrosion behavior of AZ91D alloy in ethylene glycol

International Nuclear Information System (INIS)

Fekry, A.M.; Fatayerji, M.Z.

2009-01-01

The effect of concentration on the corrosion behavior of Mg-based alloy AZ91D was investigated in ethylene glycol-water solutions using electrochemical techniques i.e. potentiodynamic polarization, electrochemical impedance measurements (EIS) and surface examination via scanning electron microscope (SEM) technique. This can provide a basis for developing new coolants for magnesium alloy engine blocks. Corrosion behavior of AZ91D alloy by coolant is important in the automotive industry. It was found that the corrosion rate of AZ91D alloy decreased with increasing concentration of ethylene glycol. For AZ91D alloy in chloride >0.05 M or fluoride 0.05 M for fluoride containing ethylene glycol solution, some inhibition effect has been observed. The corrosion of AZ91D alloy in the blank can be effectively inhibited by addition of 0.05 mM paracetamol that reacts with AZ91D alloy and forms a protective film on the surface at this concentration as confirmed by surface examination.
Corrosion behavior of construction materials for ionic liquid hydrogen compressor

DEFF Research Database (Denmark)

Arjomand Kermani, Nasrin; Petrushina, Irina; Nikiforov, Aleksey Valerievich

2016-01-01

The corrosion behavior of various commercially available stainless steels and nickel-based alloys as possible construction materials for components which are in direct contact with one of five different ionic liquids was evaluated. The ionic liquids, namely: 1-ethyl-3-methylimidazolium triflate, 1...... liquid hydrogen compressor. An electrochemical cell was specially designed, and steady-state cyclic voltammetry was used to measure the corrosion resistance of the alloys in the ionic liquids at 23 °C, under atmospheric pressure. The results showed a very high corrosion resistance and high stability...... for all the alloys tested. The two stainless steels, AISI 316L and AISI 347 showed higher corrosion resistance compared to AISI 321 in all the ionic liquids tested. It was observed that small addition of molybdenum, tantalum, and niobium to the alloys increased the corrosion stability in the ionic liquids...
Electrochemical and corrosion behavior of two chromium dental alloys in artificial bioenvironments

Directory of Open Access Journals (Sweden)

Banu Alexandra

2017-01-01

Full Text Available The purpose of this study is to compare the corrosion and tarnish behavior of NiCrMo and CoCrMo cast dental alloys in artificial bio environments. The cobalt chromium alloys are known and used in dentistry for many years, but its difficult machinability because of the strength and hardness, is an argument for scientists to study alternative materials with comparable biocompatibility. On the other hand, for dentistry devices beside corrosion behavior is important the aesthetic so, the used alloys have to preserve their shining and do not stain. The corrosion resistance has been evaluated using the Atomic mass spectroscopy method for ion release determination, the anodic polarization curves and the open circuit potential – time monitoring for corrosion behavior evaluation and optical microscopy for the structure analysis. The tarnish tendency of alloys was estimated using the method of cyclic immersion with frequency of 10 seconds for each minute during 72 hours in Na2S containing solution. The most important conclusion is that the alloys are comparable from corrosion and tarnish point of view, but we recommend to use the nickel base alloy only for orthodontic devices implanted for short periods of time, because of higher quantity of released ions.
Electrochemical corrosion behavior of AZ91D alloy in ethylene glycol

Energy Technology Data Exchange (ETDEWEB)

Fekry, A.M. [Chemistry Department, Faculty of Science, Cairo University, Giza 12613 (Egypt)], E-mail: hham4@hotmail.com; Fatayerji, M.Z. [Chemistry Department, Faculty of Science, Cairo University, Giza 12613 (Egypt)

2009-11-01

The effect of concentration on the corrosion behavior of Mg-based alloy AZ91D was investigated in ethylene glycol-water solutions using electrochemical techniques i.e. potentiodynamic polarization, electrochemical impedance measurements (EIS) and surface examination via scanning electron microscope (SEM) technique. This can provide a basis for developing new coolants for magnesium alloy engine blocks. Corrosion behavior of AZ91D alloy by coolant is important in the automotive industry. It was found that the corrosion rate of AZ91D alloy decreased with increasing concentration of ethylene glycol. For AZ91D alloy in chloride >0.05 M or fluoride <0.05 M containing 30% ethylene glycol solution, they are more corrosive than the blank (30% ethylene glycol-70% water). However, at concentrations <0.05 for chloride or >0.05 M for fluoride containing ethylene glycol solution, some inhibition effect has been observed. The corrosion of AZ91D alloy in the blank can be effectively inhibited by addition of 0.05 mM paracetamol that reacts with AZ91D alloy and forms a protective film on the surface at this concentration as confirmed by surface examination.
Improved corrosion behavior of nanocrystalline zinc produced by pulse-current electrodeposition

International Nuclear Information System (INIS)

Youssef, Kh.M.S.; Koch, C.C.; Fedkiw, P.S.

2004-01-01

Pulse electrodeposition was used to produce nanocrystalline (nc) zinc from zinc chloride electrolyte with polyacrylamide and thiourea as additives. Field emission scanning electron microscopy (FESEM) was used to study the grain size and surface morphology of the deposits and X-ray diffraction was used to examine their preferred orientation. Corrosion behavior of the electrodeposited nc zinc in comparison with electrogalvanized (EG) steel in de-aerated 0.5 N NaOH solution was studied using potentiodynamic polarization and impedance measurements. A scanning electron microscope (SEM) was used to characterize the surface morphology of the EG steel before corrosion testing. Surface morphologies of nc zinc deposits and EG steel were also studied after potentiondynamic polarization by SEM. Nanocrystalline zinc (56 nm) with random orientation was produced. The estimated corrosion rate of nc zinc was found to be about 60% lower than that of EG steel, 90 and 229 μA/cm 2 , respectively. The surface morphology of corroded nc zinc was characterized by discrete etch pits, however, uniform corrosion was obtained after potentiodynamic polarization of EG steel. The passive film formed on the nc zinc surface seems to be a dominating factor for the corrosion behavior observed
Corrosion behavior, mechanical properties, and long-term aging of nickel-plated uranium

International Nuclear Information System (INIS)

Dini, J.W.; Johnson, H.R.; Schoenfelder, C.W.

1976-01-01

The behavior of nickel-plated uranium upon exposure to moist nitrogen was evaluated. Plating thicknesses of 0.051 mm (2 mil) were adequate to prevent corrosion. Specimens with thinner coats showed some corrosion and some reduction in mechanical properties during subsequent testing. Plated samples exposed to dry air at ambient pressure for 10 y showed no corrosion and no degradation of mechanical properties. Surface and bulk hydrogen content, as well as free hydrogen generated during the test, were measured to determine the extent of corrosion. Results support an earlier proposed mechanism for uranium corrosion at low humidities
Influence of silica nanospheres on corrosion behavior of magnesium matrix syntactic foam

Science.gov (United States)

Qureshi, W.; Kannan, S.; Vincent, S.; Eddine, N. N.; Muhammed, A.; Gupta, M.; Karthikeyan, R.; Badari, V.

2018-04-01

Over the years, the development of Magnesium alloys as biodegradable implants has seen significant advancements. Magnesium based materials tend to provide numerous advantages in the field of biomedical implants over existing materials such as titanium or stainless steel. The present research focuses on corrosive behavior of Magnesium reinforced with different volume percentages of Hollow Silica Nano Spheres (HSNS). These behaviors were tested in two different simulated body fluids (SBF) namely, Hank’s Buffered Saline Solution (HBSS) and Phosphate Buffered Solution (PBS). This corrosion study was done using the method of electrochemical polarization with a three-electrode configuration. Comparative studies were established by testing pure Mg which provided critical information on the effects of the reinforcing material. The HSNS reinforced Mg displayed desirable characteristics after corrosion experiments; increased corrosion resistance was witnessed with higher volume percentage of HSNS.
Corrosion behavior of stainless steel weldments in physiological solutions

Science.gov (United States)

Farooq, A.; Azam, M.; Deen, K. M.

2018-01-01

In this study corrosion behavior of TIG welded 316L stainless steel plates in simulated biological solutions is investigated. The mechanical testing results showed slight decrease in ductility after welding and the fracture surface represented mixed cleavage and inclusions containing dimple structure. The heat affected and weld zone (WZ) demonstrated higher corrosion potential and relatively large pitting tendency than base metal (BM) in both Hank’s and Ringer’s solution. The formation of delta (δ) ferrite in the heat affected and WZ decreased the corrosion resistance as confirmed from potentiodynamic Tafel scans. The decrease in pitting resistance and lower protection tendency of the WZ compared to BM and heat affected zone was also quantified from the cyclic polarization trends.
Electrochemical corrosion behavior of A 516 steel using corrosive environments with varying concentrations of sodium thiosulphate

International Nuclear Information System (INIS)

Karim, F.; Arif, M.; Reza, I.; Akram, M.; Hussain, N.; Ali, L.

2012-01-01

The corrosion behavior of A 516 steel was studied by potentiodynamic polarization technique. Environment used for these tests was sodium chloride (5%), acetic acid (0.5%) and sodium thiosulphate with varying concentration from 0.001 M to 1 M. Surface study was also carried out using optical microscope. The potentiodynamic polarization results revealed the formation of large number of pits in the sample, which was tested in the solution containing NaCl. Pitting corrosion study of alloy A516 G-70 was also conducted to see the effect of different concentrations of thiosulfate with or without addition of NaCl and acetic acid at room temperature. It was observed that different thiosulfate concentrations did not produce any difference in the polarization behavior of the alloys, when added in 5% NaCl and 0.5% acetic acid solution. However, in the absence of NaCl and acetic acid, thiosulfate concentration 0.001 mol/l or higher did produce general corrosion and pitting in the alloy at room temperature is shown.(Orig./A.B.)
An Investigation on Corrosion Behavior of a Multi-layer Modified Aluminum Brazing Sheet

Directory of Open Access Journals (Sweden)

Liu Wei

2016-01-01

Full Text Available The corrosion behavior of a multi-layer modified aluminum brazing sheet (AA4045/3003Mod./AA7072/AA4045 was investigated. The results shows that, the existence of BDP, which forms at the interface between clad and core layer during brazing, changes the corrosion form of the air side of the material from inter-granular corrosion to local exfoliation corrosion. The addition of anti-corrosion layer makes the corrosion form of the water side from inter-granular corrosion into uniform exfoliation corrosion. Compared to the normal triple-layer brazing sheet at the same thickness, the time to perforation of the modified four-layer brazing sheet is increased by more than 200%.
Corrosion of graphitic high temperature reactor materials in steam/helium mixtures at total pessures of 3-55 bar and temperatures of 900-1150 C (1173-1423K)

International Nuclear Information System (INIS)

Hinssen, H.K.; Loenissen, K.J.; Katscher, W.; Moormann, R.

1993-03-01

In course of accident examination for (HTR), experiments on the corrosion behavior of graphitic reactor materials in steam have been performed a total pressures of 3-55bar and temperatures of 900-1150 C (1173-1423K); these experiments and their evaluation are documented here. Reactor materials examined are the structure graphite V483T2 and the fuel element matrices A3-27 and A3-3. In all experiments, the steam partial pressure was 474mbar (inert gas helium). The dependence of reaction rates and density profiles on burn-off, total pressure and temperature has been examined. Experimental reaction rates depending on burn-off are fitted by theoretical curves, a procedure, which allows rate comparison for a well defined burn-off. Comparing rates as a function of total pressure, V483T2 shows a linear dependence on 1√p total , whereas for matrix materials a pressure independent rate was found for p total 4mm for A3-3. (orig.) [de
Corrosion behavior of alloy 800H (Fe-21Cr-32Ni) in supercritical water

International Nuclear Information System (INIS)

Tan, L.; Allen, T.R.; Yang, Y.

2011-01-01

Research highlights: → Testing conditions and sample microstructures showed effects on corrosion behaviors. → EBSD and FIB/TEM were used to characterize microstructure in addition to SEM/EDS and XRD. → The formation mechanism of mushroom-shaped oxidation is proposed. → Oxidation thermodynamics and kinetics predict and interpret the corrosion behaviors. - Abstract: The effect of testing conditions (temperature, time, and oxygen content) and material's microstructure (the as-received and the grain boundary engineered conditions) on the corrosion behavior of alloy 800H in high-temperature pressurized water was studied using a variety of characterization techniques. Oxidation was observed as the primary corrosion behavior on the samples. Oxide exfoliation was significantly mitigated on the grain boundary engineered samples compared to the as-received ones. The oxide formation, including some 'mushroom-shaped oxidation', is predicted via a combination of thermodynamics and kinetics influenced by the preferential diffusion of specific species using short-cut diffusion paths.
Corrosion Behavior of Low-C Medium-Mn Steel in Simulated Marine Immersion and Splash Zone Environment

Science.gov (United States)

Zhang, Dazheng; Gao, Xiuhua; Su, Guanqiao; Du, Linxiu; Liu, Zhenguang; Hu, Jun

2017-05-01

The corrosion behavior of low-C medium-Mn steel in simulated marine immersion and splash zone environment was studied by static immersion corrosion experiment and wet-dry cyclic corrosion experiment, respectively. Corrosion rate, corrosion products, surface morphology, cross-sectional morphology, elemental distribution, potentiodynamic polarization curves and electrochemical impedance spectra were used to elucidate the corrosion behavior of low-C medium-Mn steel. The results show that corrosion rate in immersion zone is much less than that in splash zone owing to its relatively mild environment. Manganese compounds are detected in the corrosion products and only appeared in splash zone environment, which can deteriorate the protective effect of rust layer. With the extension of exposure time, corrosion products are gradually transformed into dense and thick corrosion rust from the loose and porous one in these two environments. But in splash zone environment, alloying elements of Mn appear significant enrichment in the rust layer, which decrease the corrosion resistance of the steel.
Electrochemical corrosion behavior of Ni-containing hypoeutectic Al-Si alloy

Directory of Open Access Journals (Sweden)

Abul Hossain

2015-12-01

Full Text Available Electrochemical corrosion characteristics of the thermally treated 2 wt % Ni-containing Al-6Si-0.5Mg alloy were studied in NaCl solutions. The corrosion behavior of thermally treated (T6 Al-6Si-0.5Mg (-2Ni alloys in 0.1 M NaCl solution was investigated by electrochemical potentiodynamic polarization technique consisting of linear polarization method using the fit of Tafel plot and electrochemical impedance spectroscopy (EIS techniques. Generally, linear polarization experiments revealed a decrease of the corrosion rate at thermal treated Al-6Si-0.5Mg-2Ni alloy. The EIS test results showed that there is no significant change in charge transfer resistance (Rct after addition of Ni to Al-6Si-0.5Mg alloy. The magnitude of the positive shift in the open circuit potential (OCP, corrosion potential (Ecorr and pitting corrosion potential (Epit increased with the addition of Ni to Al-6Si-0.5Mg alloy. The forms of corrosion in the studied Al-6Si-0.5Mg alloy (except Al-6Si-0.5Mg-2Ni alloy are pitting corrosion as obtained from the scanning electron microscopy (SEM study.

Study on metal material corrosion behavior of packaging of cement solidified form

International Nuclear Information System (INIS)

He Zhouguo; Lin Meiqiong; Fan Xianhua

1997-01-01

The corrosion behavior of A3 carbon steel is studied by the specimens that are exposed to atmosphere, embedded in cement solidified form or immersed in corrosion liquid. The corrosion rate is determined by mass change of the specimens. In order to compare the corrosion resistant performance of various coatings, the specimens painted with various material such as epoxide resin, propionic acid resin, propane ether resin and Ti-white paint are tested. The results of the tests show that corrosion rate of A3 carbon steel is less than 10 -3 mm·a -1 in the atmosphere and the cement solidified from, less than 0.1 mm·a -1 in the corrosion liquids, and pH value in the corrosion liquids also affect the corrosion rate of A3 carbon steel. The corrosion resistant performance of Ti-white paint is better than that of other paints. So, A3 carbon steel as packaging material can meet the requirements during storage
Corrosion behavior of austempered ductile iron (ADI) in iron ore slurry

African Journals Online (AJOL)

Corrosion behavior of austempered ductile iron (ADI) in iron ore slurry was studied as a function of the microstructure developed by austempering at 380 and 300°C for different exposure time in the slurry. The corrosion rates of the ADI balls immersed in the iron ore slurry was determined using weight loss method.
Corrosion behavior of oxide dispersion strengthened ferritic steels in supercritical water

Energy Technology Data Exchange (ETDEWEB)

Gao, Wenhua [School of Nuclear Science and Engineering, Shanghai Jiao Tong University, No. 800 Dongchuan Road, Shanghai 200240 (China); Guo, Xianglong, E-mail: guoxianglong@sjtu.edu.cn [School of Nuclear Science and Engineering, Shanghai Jiao Tong University, No. 800 Dongchuan Road, Shanghai 200240 (China); Shen, Zhao [Department of Materials Science, University of Oxford, Parks Road, Oxford OX1 3PH (United Kingdom); Zhang, Lefu, E-mail: lfzhang@sjtu.edu.cn [School of Nuclear Science and Engineering, Shanghai Jiao Tong University, No. 800 Dongchuan Road, Shanghai 200240 (China)

2017-04-01

The corrosion resistance of three different Cr content oxide dispersion strengthened (ODS) ferritic steels in supercritical water (SCW) and their passive films formed on the surface have been investigated. The results show that the dissolved oxygen (DO) and chemical composition have significant influence on the corrosion behavior of the ODS ferritic steels. In 2000 ppb DO SCW at 650 °C, the 14Cr-4Al ODS steel forms a tri-layer oxide film and the surface morphologies have experienced four structures. For the tri-layer oxide film, the middle layer is mainly Fe-Cr spinel and the Al is gradually enriched in the inner layer. - Highlights: • We evaluated the corrosion resistance of three different Cr content ODS steels at 650 °C in supercritical water. • Corrosion behavior of ODS steels is rarely reported and ODS steel may be promising material for generation IV reactors. • We found total opposite phenomenon compared to Lee's work before. Our result may be more reasonable.
Corrosion Behavior of Steels in Supercritical CO₂ for Power Cycle Applications

Energy Technology Data Exchange (ETDEWEB)

Repukaiti, Richard [National Energy Technology Lab. (NETL), Albany, OR (United States); Oregon State Univ., Corvallis, OR (United States); Teeter, Lucas [National Energy Technology Lab. (NETL), Albany, OR (United States); Oregon State Univ., Corvallis, OR (United States); Ziomek-Moroz, Margaret [National Energy Technology Lab. (NETL), Albany, OR (United States); Dogan, Omer [National Energy Technology Lab. (NETL), Albany, OR (United States); Tucker, Julie [Oregon State Univ., Corvallis, OR (United States)

2017-07-07

In order to understand issues with corrosion of heat exchanger materials in direct supercritical carbon dioxide (sCO₂) power cycles, a series of autoclave exposure experiments and electrochemical experiments have been conducted. Corrosion behaviors of 347H stainless steel and P91 martensitic-ferrtic steel in sCO₂ environment have been compared. In autoclave exposure tests performed at 50°C- 245°C and 80 bar. Mass change measurements, surface characterization, and corrosion product analysis have been conducted to understand the corrosion behavior of steels in sCO₂ containing H₂O and O₂. Electrochemical tests performed at room temperature and 50°C, a simulation environment of water condensation phase with dissolved CO₂ was prepared to evaluate the corrosion resistance of materials. From both types of experiments, generally 347H showed higher corrosion resistance than P91.
Effects of Alloyed Carbon on the General Corrosion and the Pitting Corrosion Behavior of FeCrMnN Stainless Steels

Energy Technology Data Exchange (ETDEWEB)

Ha, Heon-Young; Lee, Tae-Ho; Kim, Sung-Joon [Korea Institute of Materials Science, Changwon (Korea, Republic of)

2011-10-15

The effects of alloyed carbon on the pitting corrosion, the general corrosion, and the passivity behavior of Fe{sub 1}8Cr{sub 1}0Mn{sub 0}.4Nx{sub C} (x=0 ⁓ 0.38 wt%) alloys were investigated by various electrochemical methods and XPS analysis. The alloyed carbon increased the general corrosion resistance of the FeCrMnN matrix. Carbon enhanced the corrosion potential, reduced the metal dissolution rate, and accelerated the hydrogen evolution reaction rate in various acidic solutions. In addition, carbon promoted the pitting corrosion resistance of the matrix in a chloride solution. The alloyed carbon in the matrix increased the chromium content in the passive film, and thus the passive film became more protective.
Corrosion behavior of duplex and reference cladding in NPP Grohnde

International Nuclear Information System (INIS)

Besch, O.A.; Yagnik, S.K.; Eucken, C.M.; Bradley, E.R.

1996-01-01

The Nuclear Fuel Industry Research (NFIR) Group undertook a lead test assembly (LTA) program in NPP Grohnde PWR in Germany to assess the corrosion performance of duplex and reference cladding. Two identical 16 by 16 LTAs, each containing 32 peripheral test rods, completed four reactor cycles, reaching a peak rod burnup of 46 MWd/kgU. The results from poolside examinations performed at the end of each cycle, together with power histories and coolant chemistry, are reported. Five different cladding materials were characterized during fabrication. The corrosion performance of the cladding materials was tracked in long-term tests in high-pressure, high-temperature autoclaves. The relative ranking of corrosion behavior in such tests corresponded well with the in-reactor corrosion performance. The extent and distribution of hydriding in duplex and reference specimens during the autoclave testing has been characterized. The in-reactor corrosion data indicate that the low-tin Zircaloy-4 reference cladding, R2, had an improved corrosion resistance compared to high-tin Zircaloy-4 reference cladding, R1. Two types of duplex cladding, D1 (Zr-2.5% Nb) and D2 (Zr-0.4% Fe-0.5% Sn), showed an even further improvement in corrosion resistance compared to R2 cladding. The third duplex cladding, D3 (Zr-4 + 1.0% Nb), had significantly less corrosion resistance, which was inferior to R1. The in-reactor and out-reactor corrosion performances have been ranked
Atmospheric Corrosion Behavior of 2A12 Aluminum Alloy in a Tropical Marine Environment

Directory of Open Access Journals (Sweden)

Zhongyu Cui

2015-01-01

Full Text Available Atmospheric corrosion behavior of 2A12 aluminum alloy exposed to a tropical marine environment for 4 years was investigated. Weight loss of 2A12 alloy in the log-log coordinates can be well fitted with two linear segments, attributing to the evolution of the corrosion products. EIS results indicate that the corrosion product layer formed on the specimens exposed for 12 months or longer presents a good barrier effect. Corrosion morphology changes from pitting corrosion to severe intergranular corrosion with the extension of exposure time, resulting in the reduction of the mechanical properties.
The effect of urea on the corrosion behavior of different dental alloys.

Science.gov (United States)

Geckili, Onur; Bilhan, Hakan; Bilgin, Tayfun; Anthony von Fraunhofer, J

2012-01-01

Intraoral corrosion of dental alloys has biological, functional, and esthetic consequences. Since it is well known that the salivary urea concentrations undergo changes with various diseases, the present study was undertaken to determine the effect of salivary urea concentrations on the corrosion behavior of commonly used dental casting alloys. Three casting alloys were subjected to polarization scans in synthetic saliva with three different urea concentrations. Cyclic polarization clearly showed that urea levels above 20 mg/100 ml decreased corrosion current densities, increased the corrosion potentials and, at much higher urea levels, the breakdown potentials. The data indicate that elevated urea levels reduced the corrosion susceptibility of all alloys, possibly through adsorption of organics onto the metal surface. This study indicates that corrosion testing performed in sterile saline or synthetic saliva without organic components could be misleading.
Corrosion behavior of Zircaloy 4 cladding material. Evaluation of the hydriding effect

International Nuclear Information System (INIS)

Blat, M.

1997-04-01

In this work, particular attention has been paid to the hydriding effect in PIE and laboratory test to validate a detrimental hydrogen contribution on Zircaloy 4 corrosion behavior at high burnup. Laboratory corrosion tests results confirm that hydrides have a detrimental role on corrosion kinetics. This effect is particularly significant for cathodic charged samples with a massive hydride outer layer before corrosion test. PIE show that at high burnup a hydride layer is formed underneath the metal/oxide interface. The results of the metallurgical examinations are discussed with respect to the possible mechanisms involved in this detrimental effect of hydrogen. Therefore, according to the laboratory tests results and PIE, hydrogen could be a strong contributor to explain the increase in corrosion rate at high burnup. (author)
An electrochemical investigation of the corrosion behavior of aluminum alloys in chloride containing solutions

International Nuclear Information System (INIS)

Campos Filho, Jorge Eustaquio de

2005-01-01

Aluminum alloys have been used as cladding materials for nuclear fuel in research reactors due to its corrosion resistance. Aluminum owes its good corrosion resistance to a protective barrier oxide film formed and strongly bonded to its surface. In pool type TRIGA IPR-R1 reactor, located at Centro de Desenvolvimento da Tecnologia Nuclear in Belo Horizonte, previous immersion coupon tests revealed that aluminum alloys suffer from pitting corrosion, in spite of high quality of water control. Corrosion attack is initiated by breaking the protective oxide film on aluminum alloy surface. Chloride ions can break this oxide film and stimulate metal dissolution. In this study the aluminum alloys 1050, 5052 and 6061 were used to evaluate their corrosion behavior in chloride containing solutions. The electrochemical techniques used were potentiodynamic anodic polarization and cyclic polarization. Results showed that aluminum alloys 5052 and 6061 present similar corrosion resistance in low chloride solutions (0,1 ppm NaCl) and in reactor water but both alloys are less resistant in high chloride solution (1 ppm NaCl). Aluminum alloy 1050 presented similar behavior in the three electrolytes used, regarding to pitting corrosion, indicating that the concentration of the chloride ions was not the only variable to influence its corrosion susceptibility. (author)
Structural characteristics and corrosion behavior of biodegradable Mg-Zn, Mg-Zn-Gd alloys.

Science.gov (United States)

Kubásek, J; Vojtěch, D

2013-07-01

In this research, binary Mg-Zn (up to 3 wt% Zn) and ternary Mg-Zn-Gd (up to 3 wt% Gd, 3 wt% Zn) alloys were prepared by induction melting in an argon atmosphere. The structures of these alloys were characterized using light and scanning electron microscopy, energy dispersive spectrometry, X-ray diffraction and X-ray fluorescence. In addition, Brinell hardness measurements were taken to supplement these studies. Corrosion behavior was evaluated by immersion tests and potentiodynamic measurements in a physiological solution (9 g/l NaCl). Depending on the composition, structures of the as-cast alloys contained α-Mg dendrites, MgZn, Mg5Gd and Mg3Gd2Zn3 phases. Compared to pure Mg, zinc improved the corrosion resistance of binary Mg-Zn. Gadolinium also improved the corrosion resistance in the case of Mg-1Zn-3Gd alloy. The highest corrosion rate was observed for Mg-3Zn-3Gd alloy. Our results improve the understanding of the relationships between the structure and corrosion behavior of our studied alloy systems.
Analogies in the microscopic behavior of superfluid and classical helium studied by neturon scattering [Analogieen in het microscopische gedrag van superfluid en klassiek helium

NARCIS (Netherlands)

Crevecoeur, R.M.

1996-01-01

In this thesis we have presented the results of a neutron scattering study of the analogies in the microscopic behavior of superfluid and classical helium. Therefore we performed both neutron-diffraction experiments to study the structure and inelastic neutron scattering experiments to study the
Corrosion behavior of stainless steel and zirconium in nitric acid containing highly oxidizing species

International Nuclear Information System (INIS)

Mayuzumi, Masami; Fujita, Tomonari

1994-01-01

Corrosion behavior of 304ELC, 310Nb stainless steels and Zirconium was investigated in the simulated dissolver solution of a reprocessing plant to obtain fundamental data for life prediction. Corrosion of heat transfer surface was also investigated in nitric acid solutions containing Ce ion. The results obtained are as follows: (1) Stainless steels showed intergranular corrosion in the simulated dissolver solution. The corrosion rate increased with time and reached to a constant value after several hundred hours of immersing time. The constant corrosion rate changed depending on potential suggesting that corrosion potential dominates the corrosion process. 310Nb showed superior corrosion resistance to 304ELC. (2) Corrosion rate of stainless steels increased in the heat transfer condition. The causes of corrosion enhancement are estimated to be higher corrosion potential and higher temperature of heat transfer surface. (3) Zirconium showed perfect passivity in all the test conditions employed. (author)
Effects of copper and titanium on the corrosion behavior of newly fabricated nanocrystalline aluminum in natural seawater

International Nuclear Information System (INIS)

Sherif, El-Sayed M.; Ammar, Hany Rizk; Khalil, Khalil Abdelrazek

2014-01-01

Graphical abstract: - Highlights: • We fabricated nanocrystalline Al and some of its alloys by mechanical alloying method. • The corrosion behavior of the fabricated materials in natural seawater was reported. • We found that Al suffers both uniform and localized corrosion in the seawater. • The presence of Cu significantly decreased the corrosion of Al. • The addition of Ti to the Al–Cu alloy presented more protection to Al against corrosion. - Abstract: Fabrication of a newly nanocrystalline Al and two of its alloys, namely Al–10%Cu; and Al–10%Cu–5%Ti has been carried out using mechanical alloying (MA) technique. The corrosion behavior of these materials in aerated stagnant Arabian Gulf seawater (AGSW) at room temperature has been reported. Cyclic potentiodynamic polarization (CPP), chronoamperometric current-time (CCT) and electrochemical impedance spectroscopy (EIS) measurements along with scanning electron microscopy (SEM) and X-ray energy dispersive (EDX) investigations were employed to report the corrosion behavior of the fabricated materials. All results indicated that Al suffers both uniform and localized corrosion in the AGSW test solution. The presence of 10%Cu decreases the corrosion current density, the anodic and cathodic currents and corrosion rate and increases the corrosion resistance of Al. The addition of 5%Ti to the Al–10%Cu alloy produced further decreases in the corrosion parameters. Measurements together confirmed that the corrosion of the fabricated materials in AGSW decreases in the order Al > Al–10%Cu > Al–10%Cu–5%Ti
Effects of copper and titanium on the corrosion behavior of newly fabricated nanocrystalline aluminum in natural seawater

Energy Technology Data Exchange (ETDEWEB)

Sherif, El-Sayed M., E-mail: esherif@ksu.edu.sa [Mechanical Engineering Department, College of Engineering, King Saud University, P.O. Box 800, Al-Riyadh 11421 (Saudi Arabia); Electrochemistry and Corrosion Laboratory, Department of Physical Chemistry, National Research Centre , (NRC), Dokki, 12622, Cairo 8 (Egypt); Ammar, Hany Rizk [Metallurgical and Materials Engineering Department, Faculty of Petroleum and Mining Engineering, Suez University, Suez (Egypt); Khalil, Khalil Abdelrazek [Metallurgical and Materials Engineering Department, Faculty of Petroleum and Mining Engineering, Suez University, Suez (Egypt); Mechanical Design and Materials Department, Faculty of Energy Engineering, Aswan University, Aswan (Egypt)

2014-05-01

Graphical abstract: - Highlights: • We fabricated nanocrystalline Al and some of its alloys by mechanical alloying method. • The corrosion behavior of the fabricated materials in natural seawater was reported. • We found that Al suffers both uniform and localized corrosion in the seawater. • The presence of Cu significantly decreased the corrosion of Al. • The addition of Ti to the Al–Cu alloy presented more protection to Al against corrosion. - Abstract: Fabrication of a newly nanocrystalline Al and two of its alloys, namely Al–10%Cu; and Al–10%Cu–5%Ti has been carried out using mechanical alloying (MA) technique. The corrosion behavior of these materials in aerated stagnant Arabian Gulf seawater (AGSW) at room temperature has been reported. Cyclic potentiodynamic polarization (CPP), chronoamperometric current-time (CCT) and electrochemical impedance spectroscopy (EIS) measurements along with scanning electron microscopy (SEM) and X-ray energy dispersive (EDX) investigations were employed to report the corrosion behavior of the fabricated materials. All results indicated that Al suffers both uniform and localized corrosion in the AGSW test solution. The presence of 10%Cu decreases the corrosion current density, the anodic and cathodic currents and corrosion rate and increases the corrosion resistance of Al. The addition of 5%Ti to the Al–10%Cu alloy produced further decreases in the corrosion parameters. Measurements together confirmed that the corrosion of the fabricated materials in AGSW decreases in the order Al > Al–10%Cu > Al–10%Cu–5%Ti.
Electrochemical migration, whisker formation, and corrosion behavior of printed circuit board under wet H2S environment

International Nuclear Information System (INIS)

Zou, Shiwen; Li, Xiaogang; Dong, Chaofang; Ding, Kangkang; Xiao, Kui

2013-01-01

Highlights: •The electrochemical migration, whisker formation, and corrosion behavior of PCB under wet H 2 S environment were observed and studied systematically. •The process of electrochemical migration of solder joints is explained. •The corrosion mechanism of PCB interconnectors induced by micro pores under wet H 2 S environment is discussed, and the corrosion reaction model is proposed. -- Abstract: Electrochemical migration, whisker formation, and corrosion behavior of printed circuit board (PCB) under wet H 2 S environment were analyzed by environment scanning electron microscope (ESEM), Energy dispersive X-ray spectroscopy (EDS) with mapping and element phase cluster (EPC) techniques, Raman Spectrum analysis and electrochemical impedance spectroscopy (EIS) technology. The results showed that nonuniform corrosion behavior occurred on PCB surfaces under 1 ppm wet H 2 S at 40 °C; whiskers formed on the inner sidewall of via-holes with a growth rate of 1.2 Å/s; numerous corrosion products migrated through the pore of plated gold layer, which broke off the protective layer. The corrosion rate was accelerated according to the big-cathode-small-anode model
Mechanical and corrosion behaviors of developed copper-based metal matrix composites

Science.gov (United States)

Singh, Manvandra Kumar; Gautam, Rakesh Kumar; Prakash, Rajiv; Ji, Gopal

2018-03-01

This work investigates mechanical properties and corrosion resistances of cast copper-tungsten carbide (WC) metal matrix composites (MMCs). Copper matrix composites have been developed by stir casting technique. Different sizes of micro and nano particles of WC particles are utilized as reinforcement to prepare two copper-based composites, however, nano size of WC particles are prepared by high-energy ball milling. XRD (X-rays diffraction) characterize the materials for involvement of different phases. The mechanical behavior of composites has been studied by Vickers hardness test and compression test; while the corrosion behavior of developed composites is investigated by electrochemical impedance spectroscopy in 0.5 M H2SO4 solutions. The results show that hardness, compressive strength and corrosion resistance of copper matrix composites are very high in comparison to that of copper matrix, which attributed to the microstructural changes occurred during composite formation. SEM (Scanning electron microscopy) reveals the morphology of the corroded surfaces.
Effect of Sulfur and Chlorine on Fireside Corrosion Behavior of Inconel 740 H Superalloy

Science.gov (United States)

Jin-tao, Lu; Yan, Li; Zhen, Yang; Jin-yang, Huang; Ming, Zhu; Gu, Y.

2018-03-01

Fireside corrosion behavior of Inconel 740H superalloy was studied at 750 °C in simulated coal ash/flue gas environments by means of XRD, SEM and EDS. The results indicated that the corrosion behavior was strongly related to the SO2 levels and was significantly affected by NaCl additions. In presence of the atmospheres with 0.1 % SO2, the alloy exhibited the highest corrosion resistance due to formation of a stable and dense Cr2O3 film. In presence of the atmosphere with 1.5 % SO2, however, a non-coherent and porous Cr2O3 film was formed. The thickness of film and internal sulfides were substantially increased. The NaCl additions significantly accelerated the corrosion process. A non-protective outer oxide film was formed, composed by multiple layers with serious inner sulfide and spallation. The depths of internal oxidizing and sulfuration zones were significantly increased. The mechanism of ash corrosion formation was also discussed.
Correlation between zirconium oxide impedance and corrosion behavior of Zr-Nb-Sn-Fe-Cu alloys

International Nuclear Information System (INIS)

Park, Sang Yoon; Lee, Myung Ho; Choi, Byoung Kwon; Jeong, Yong Hwan; Jung, Youn Ho

2001-01-01

To evaluate the correlation of Zr oxide impedance and corrosion behavior of Zr-Nb-Sn-Fe-Cu alloys, the corrosion behavior of the alloys was tested in the autoclave containing 70 ppm LiOH solution at 360 .deg. C. The characteristics of the oxide on the alloys were investigated by using the electrochemical impedance spectrosocpy (EIS) method. The corrosion resistance of the alloys was evaluated from the corrosion rate determined as a function of the concentration of Nb. The equivalent circuit of the oxide was composed on the base of the spectrum from EIS measurements on the oxide layers that had formed at pre-and post-transition regions on the curve of corrosion rate. By using the capacitance characteristics of the equivalent circuit, the thickness of impervious layer, it's electrical resistance and characteristics of space charge layer were evaluated. The corrosion characteristics of the Zr-Nb-Sn-Fe-Cu alloys were successfully explained by applying the EIS test results
Electrochemical corrosion behavior of a Ti-35Nb alloy for medical prostheses

International Nuclear Information System (INIS)

Cremasco, Alessandra; Osorio, Wislei R.; Freire, Celia M.A.; Garcia, Amauri; Caram, Rubens

2008-01-01

Since the 1980s, the titanium alloys show attractive properties for biomedical applications where the most important factors are, firstly, biocompatibility, corrosion and mechanical resistances, low modulus of elasticity, very good strength to weight ratio, reasonable formability and osseointegration. The aim of this study was to investigate the effects of two different heat treatments; furnace cooling and water quenching, on the general electrochemical corrosion resistance of Ti-35 wt%Nb alloy samples immersed in a 0.9% NaCl (0.15 mol L -1 ) solution at 25 deg. C and neutral pH range. The samples were obtained using a non-consumable tungsten electrode furnace with a water-cooled copper hearth under argon atmosphere. The microstructural pattern was examined by scanning electron microscopy (SEM) and X-ray diffractometry (XRD). In order to evaluate the electrochemical corrosion behavior of such Ti-Nb alloy samples, corrosion tests were performed by using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves. Analyses of an equivalent circuit have also been used to provide quantitative support for the discussions and understanding of the corrosion behavior. It was found that water quenching provides a microstructural pattern consisting of an alpha-martensite acicular phase which decreases the material electrochemical performance due to the stress-induced martensitic transformation

Electrochemical corrosion behavior of a Ti-35Nb alloy for medical prostheses

Energy Technology Data Exchange (ETDEWEB)

Cremasco, Alessandra [Department of Materials Engineering, State University of Campinas, UNICAMP, P.O. Box 6122, 13083-970 Campinas, SP (Brazil); Osorio, Wislei R. [Department of Materials Engineering, State University of Campinas, UNICAMP, P.O. Box 6122, 13083-970 Campinas, SP (Brazil)], E-mail: wislei@fem.unicamp.br; Freire, Celia M.A.; Garcia, Amauri; Caram, Rubens [Department of Materials Engineering, State University of Campinas, UNICAMP, P.O. Box 6122, 13083-970 Campinas, SP (Brazil)

2008-05-30

Since the 1980s, the titanium alloys show attractive properties for biomedical applications where the most important factors are, firstly, biocompatibility, corrosion and mechanical resistances, low modulus of elasticity, very good strength to weight ratio, reasonable formability and osseointegration. The aim of this study was to investigate the effects of two different heat treatments; furnace cooling and water quenching, on the general electrochemical corrosion resistance of Ti-35 wt%Nb alloy samples immersed in a 0.9% NaCl (0.15 mol L{sup -1}) solution at 25 deg. C and neutral pH range. The samples were obtained using a non-consumable tungsten electrode furnace with a water-cooled copper hearth under argon atmosphere. The microstructural pattern was examined by scanning electron microscopy (SEM) and X-ray diffractometry (XRD). In order to evaluate the electrochemical corrosion behavior of such Ti-Nb alloy samples, corrosion tests were performed by using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves. Analyses of an equivalent circuit have also been used to provide quantitative support for the discussions and understanding of the corrosion behavior. It was found that water quenching provides a microstructural pattern consisting of an alpha-martensite acicular phase which decreases the material electrochemical performance due to the stress-induced martensitic transformation.
Comparison of Corrosion Behavior of Electrochemically Deposited Nano-Cobalt-Coated Ni Sheet

Directory of Open Access Journals (Sweden)

Nasser Al-Aqeeli

2013-01-01

Full Text Available Corrosion behavior of nano-coblat-coated Ni sheet was compared with pure Ni and 20% Fe-Ni alloy sheet using potentiodynamic polarization and linear polarization technique in 0.1 M NaCl solution at room temperature. Results showed that corrosion resistance properties of nano-Co-coated Ni sheet were almost same as that of pure Ni sheet, however corrosion resistance of 20% Fe-Ni sheet was decreased significantly. Pitting potential of 20% Fe-Ni sheet was subsequently decreased as compared to pure Ni sheet as well as nano-cobalt-coated Ni sheet. SEM/EDS analysis of the corroded surfaces showed that both pure Ni and nano-coblat-coated Ni sheet did not show any appreciable corrosion however significant corrosion was observed in the case of 20% Fe-Ni sheet.
Evaluation of corrosive behavior of SAE 5155 by corrosion environment

International Nuclear Information System (INIS)

An, Jae Pil; Park, Keyung Dong

2005-01-01

In this study, the influence of shot peening and corrosive condition for corrosion property was investigated on immersed in 3.5% NaCl, 10% HNO 3 + 3% HF, 6% FeCl 3 . The immersion test was performed on two kinds of specimen. The immersion periods was performed 30days. Corrosion potential, weight loss were investigated from experimental results. From test results, the effect of shot peening on the corrosion was evaluated
Study of the corrosion behavior of magnesium alloy weddings in NaCl solutions by gravimetric tests

Energy Technology Data Exchange (ETDEWEB)

Segarra, J. A.; Calderon, B.; Portoles, A.

2015-07-01

In this article, the corrosion behavior of commercial AZ31 welded plates in aqueous chloride media was investigated by means of gravimetric techniques and Neutral Salt Spray tests (NSS). The AZ31 samples tested were welded using Gas Tugsten Arc Welding (GTAW) and different filler materials. Material microstructures were investigated by optical microscopy to stablish the influence of those microstructures in the corrosion behavior. Gravimetric and NSS tests indicate that the use of more noble filler alloys for the sample welding, preventing the reduction of aluminum content in weld beads, does not imply a better corrosion behavior. (Author)
Effect of calcium on the microstructure and corrosion behavior of microarc oxidized Mg-xCa alloys.

Science.gov (United States)

Pan, Yaokun; Chen, Chuanzhong; Feng, Rui; Cui, Hongwei; Gong, Benkui; Zheng, Tingting; Ji, Yarou

2018-01-16

Magnesium alloys are potential biodegradable implants for biomedical applications, and calcium (Ca) is one kind of ideal element being examined for magnesium alloys and biodegradable ceramic coatings owing to its biocompatibility and mechanical suitability. In this study, microarc oxidation (MAO) coatings were prepared on Mg-xCa alloys to study the effect of Ca on the microstructure and corrosion resistance of Mg-xCa alloys and their surface MAO coatings. The electrochemical corrosion behavior was investigated using an electrochemical workstation, and the degradability and bioactivity were evaluated by soaking tests in simulated body fluid (SBF) solutions. The corrosion products were characterized by scanning electron microscopy, x-ray diffractometry, and Fourier transform infrared spectrometry. The effects of Ca on the alloy phase composition, microstructure, MAO coating formation mechanism, and corrosion behavior were investigated. Results showed that the Mg-0.82Ca alloy and MAO-coated Mg-0.82Ca exhibited the highest corrosion resistance. The number and distribution of Mg 2 Ca phases can be controlled by adjusting the Ca content in the Mg-xCa alloys. The proper amount of Ca in magnesium alloy was about 0.5-0.8 wt. %. The pore size, surface roughness, and corrosion behavior of microarc oxidized Mg-xCa samples can be controlled by the number and distribution of the Mg 2 Ca phase. The corrosion behaviors of microarc oxidized Mg-Ca in SBF solutions were discussed.
Review on stress corrosion and corrosion fatigue failure of centrifugal compressor impeller

Science.gov (United States)

Sun, Jiao; Chen, Songying; Qu, Yanpeng; Li, Jianfeng

2015-03-01

Corrosion failure, especially stress corrosion cracking and corrosion fatigue, is the main cause of centrifugal compressor impeller failure. And it is concealed and destructive. This paper summarizes the main theories of stress corrosion cracking and corrosion fatigue and its latest developments, and it also points out that existing stress corrosion cracking theories can be reduced to the anodic dissolution (AD), the hydrogen-induced cracking (HIC), and the combined AD and HIC mechanisms. The corrosion behavior and the mechanism of corrosion fatigue in the crack propagation stage are similar to stress corrosion cracking. The effects of stress ratio, loading frequency, and corrosive medium on the corrosion fatigue crack propagation rate are analyzed and summarized. The corrosion behavior and the mechanism of stress corrosion cracking and corrosion fatigue in corrosive environments, which contain sulfide, chlorides, and carbonate, are analyzed. The working environments of the centrifugal compressor impeller show the behavior and the mechanism of stress corrosion cracking and corrosion fatigue in different corrosive environments. The current research methods for centrifugal compressor impeller corrosion failure are analyzed. Physical analysis, numerical simulation, and the fluid-structure interaction method play an increasingly important role in the research on impeller deformation and stress distribution caused by the joint action of aerodynamic load and centrifugal load.
Influence of Freeze-Thaw Damage on the Steel Corrosion and Bond-Slip Behavior in the Reinforced Concrete

Directory of Open Access Journals (Sweden)

Fangzhi Zhu

2016-01-01

Full Text Available This paper mainly studies the behavior of steel corrosion in various reinforced concrete under freeze-thaw environment. The influence of thickness of concrete cover is also discussed. Additionally, the bond-slip behavior of the reinforced concrete after suffering the freeze-thaw damage and steel corrosion has also be presented. The results show that the freeze-thaw damage aggravates the steel corrosion in concrete, and the results become more obvious in the concrete after suffering serious freeze-thaw damage. Compared with the ordinary concrete, both air entrained concrete and waterproofing concrete possess better resistance to steel corrosion under the same freeze-thaw environment. Moreover, increasing the thicknesses of concrete cover is also an effective method of improving the resistance to steel corrosion. The bond-slip behavior of reinforced concrete with corroded steel decreases with the increase of freeze-thaw damage, especially for the concrete that suffered high freeze-thaw cycles. Moreover, there exists a good correlation between the parameters of bond-slip and freeze-thaw cycles. The steel corrosion and bond-slip behavior of reinforced concrete should be considered serious under freeze-thaw cycles environment, which significantly impact the durability and safety of concrete structure.
The effects of Nitinol phases on corrosion and fatigue behavior

Science.gov (United States)

Denton, Melissa

The purpose of these studies was to provide a detailed understanding of Nitinol phases and their effects on corrosion and fatigue life. The two primary phases, austenite and martensite, were carefully evaluated with respect to material geometry, corrosion behavior, wear, and fatigue life. Material characterization was performed using several techniques that include metallography, scanning electron microscopy (SEM), transmission electron microscopy (TEM), atomic force microscopy (AFM), x-ray photoelectron spectrum (XPS), and Auger electron spectroscopy (AES). Uniaxial tensile tests were conducted to determine the mechanical properties such as elongation, ultimate tensile strength, modulus, transformation strain, and plateau stress. In addition, accelerated wear testing and four point bend fatigue testing were completed to study the fatigue life and durability of the material. The corrosion of Nitinol was found to be dependent on various surface conditions. Electrochemical corrosion behavior of each phase was investigated using cyclic potentiodyamic polarization testing. The corrosion response of electropolished Nitinol was found to be acceptable, even after durability testing. Stress-induced martensite had a lower breakdown potential due to a rougher surface morphology, while thermally induced martensite and austenite performed similarly well. The surface conditioning also had a significant effect on Nitinol mechanical properties. Electropolishing provided a smooth mirror finish that reduced localized texture and enhanced the ductility of the material. Quasi-static mechanical properties can be good indicators of fatigue life, but further fatigue testing revealed that phase transformations had an important role as well. The governing mechanisms for the fatigue life of Nitinol were determined to be both martesitic phase transformations and surface defects. A new ultimate dislocation strain model was proposed based on specific accelerated step-strain testing.
Effects of Fe and Cr on corrosion behavior of ZrFeCr alloys in 500 oC steam

International Nuclear Information System (INIS)

Wang Jun; Fan Hongyuan; Xiong Ji; Liu Hong; Miao Zhi; Ying Shihao; Yang Gang

2011-01-01

Research highlights: Amount and size of SPP will effect the corrosion resistance of Zr alloy at 500 o C/10.3 MPa. - Abstract: A study of the corrosion behaviors of ZrFeCr alloy and the influence of microstructure on corrosion resistance are described by X-ray diffraction and scanning electron microscope in this paper. The results show that several ZrFeCr alloys exhibit protective behavior throughout the test and oxide growth is stable and protective. The best alloy has the composition Zr1.0Fe0.6Cr. Fitting of the weight gain curves for the protective oxide alloys in the region of protective behavior, it showed nearly cubic behavior for the most protective alloys. The Zr1.0Fe0.6Cr has the more laves Zr(Fe,Cr) 2 precipitate in matrix and it has the better corrosion resistance. The Zr0.2Fe0.1Cr has little precipitate, the biggest hydrogen absorption and the worst corrosion resistance. The number of precipitates and the amount of hydrogen absorption in Zr alloy plays an important role on corrosion resistance behaviors in 500 o C/10.3 MPa steam.
Stress-corrosion behavior of aluminum-lithium alloys in aqueous environments

Science.gov (United States)

Pizzo, P. P.; Galvin, R. P.; Nelson, H. G.

1983-01-01

The stress corrosion susceptibility of two powder metallurgy (P/M) alloys, Al-Li-Cu and Al-Li-Cu-Mg two mechanically attrited (M/A) alloys, Al-Li-Cu and Al-Li-Mg; and two wrought, ingot alloys, X-2020 and AA7475, are compared. Time-dependent fracture in an aqueous sodium chloride environment under alternate immersion condition was found to vary significantly between alloys. The stress corrosion behavior of the two powder metallurgy processed alloys was studied in detail under conditions of crack initiation, static crack growth, and fatigue crack growth. A variety of stress corrosion tests were performed including smooth surface, time-to-failure tests; potentiostatic tests on smooth surfaces exposed to constant applied strain rates; and fracture mechanics-type tests under static and cyclic loads. Both alloys show surface pitting and subsequent intergranular corrosion. Pitting is more severe in the magnesium-bearing alloy and is associated with stringer particles strung along the extrusion direction as a result of P/M processing.
Microgalvanic Corrosion Behavior of Cu-Ag Active Braze Alloys Investigated with SKPFM

Directory of Open Access Journals (Sweden)

Armen Kvryan

2016-04-01

Full Text Available The nature of microgalvanic couple driven corrosion of brazed joints was investigated. 316L stainless steel samples were joined using Cu-Ag-Ti and Cu-Ag-In-Ti braze alloys. Phase and elemental composition across each braze and parent metal interface was characterized and scanning Kelvin probe force microscopy (SKPFM was used to map the Volta potential differences. Co-localization of SKPFM with Energy Dispersive Spectroscopy (EDS measurements enabled spatially resolved correlation of potential differences with composition and subsequent galvanic corrosion behavior. Following exposure to the aggressive solution, corrosion damage morphology was characterized to determine the mode of attack and likely initiation areas. When exposed to 0.6 M NaCl, corrosion occurred at the braze-316L interface preceded by preferential dissolution of the Cu-rich phase within the braze alloy. Braze corrosion was driven by galvanic couples between the braze alloys and stainless steel as well as between different phases within the braze microstructure. Microgalvanic corrosion between phases of the braze alloys was investigated via SKPFM to determine how corrosion of the brazed joints developed.
Structure and Corrosion Behavior of Arc-Sprayed Zn-Al Coatings on Ductile Iron Substrate

Science.gov (United States)

Bonabi, Salar Fatoureh; Ashrafizadeh, Fakhreddin; Sanati, Alireza; Nahvi, Saied Mehran

2018-02-01

In this research, four coatings including pure zinc, pure aluminum, a double-layered coating of zinc and aluminum, and a coating produced by simultaneous deposition of zinc and aluminum were deposited on a cast iron substrate using electric arc-spraying technique. The coatings were characterized by XRD, SEM and EDS map and spot analyses. Adhesion strength of the coatings was evaluated by three-point bending tests, where double-layered coating indicated the lowest bending angle among the specimens, with detection of cracks at the coating-substrate interface. Coatings produced by simultaneous deposition of zinc and aluminum possessed a relatively uniform distribution of both metals. In order to evaluate the corrosion behavior of the coatings, cyclic polarization and salt spray tests were conducted. Accordingly, pure aluminum coating showed susceptibility to pitting corrosion and other coatings underwent uniform corrosion. For double-layered coating, SEM micrographs revealed zinc corrosion products as flaky particles in the pores formed by pitting on the surface, an indication of penetration of corrosion products from the lower layer (zinc) to the top layer (aluminum). All coatings experienced higher negative corrosion potentials than the iron substrate, indicative of their sacrificial behavior.
Microstructure and corrosion behavior of laser processed NiTi alloy.

Science.gov (United States)

Marattukalam, Jithin J; Singh, Amit Kumar; Datta, Susmit; Das, Mitun; Balla, Vamsi Krishna; Bontha, Srikanth; Kalpathy, Sreeram K

2015-12-01

Laser Engineered Net Shaping (LENS™), a commercially available additive manufacturing technology, has been used to fabricate dense equiatomic NiTi alloy components. The primary aim of this work is to study the effect of laser power and scan speed on microstructure, phase constituents, hardness and corrosion behavior of laser processed NiTi alloy. The results showed retention of large amount of high-temperature austenite phase at room temperature due to high cooling rates associated with laser processing. The high amount of austenite in these samples increased the hardness. The grain size and corrosion resistance were found to increase with laser power. The surface energy of NiTi alloy, calculated using contact angles, decreased from 61 mN/m to 56 mN/m with increase in laser energy density from 20 J/mm(2) to 80 J/mm(2). The decrease in surface energy shifted the corrosion potentials to nobler direction and decreased the corrosion current. Under present experimental conditions the laser power found to have strong influence on microstructure, phase constituents and corrosion resistance of NiTi alloy. Copyright © 2015 Elsevier B.V. All rights reserved.
Study on the hot corrosion behavior of a cast Ni-base superalloy

Energy Technology Data Exchange (ETDEWEB)

Wang, W.; Guo, J.T.; Zhang, J.; Yuan, C.; Zhou, L.Z.; Hu, Z.Q. [Chinese Academy of Sciences, Shenyang (China). Inst. of Metal Research

2010-07-01

Hot corrosion behavior of Nickel-base cast superalloy K447 in 90% Na{sub 2}SO{sub 4} + 10% NaCl melting salt at 850 C and 900 C was studied. The hot corrosion kinetic of the alloy follows parabolic rate law under the experimental conditions. The external layer is mainly Cr{sub 2}O{sub 3} scale which is protective to the alloy, the intermediate layer is the Ti-rich phase, and the internal layer is mainly the international oxides and sulfides. With increased corrosion time and temperature, the oxide scales are gradually dissolved in the molten salt and then precipitate as a thick and non-protective scale. Chlorides cause the formation of volatile species, which makes the oxide scale disintegrate and break off. The corrosion kinetics and morphology examinations tend to support the basic dissolution model for hot corrosion mechanisms. (orig.)
Corrosion behavior of niobium coated 304 stainless steel in acid solution

Energy Technology Data Exchange (ETDEWEB)

Pan, T.J., E-mail: tjpan@cczu.edu.cn [School of Material Science and Engineering, Jiangsu Collaborative Innovation Center for Photovolatic Science and Engineering, Changzhou University, Changzhou 213164 (China); Jiangsu Key Laboratory of Material Surface Technology, Changzhou 213164 (China); Chen, Y.; Zhang, B. [School of Material Science and Engineering, Jiangsu Collaborative Innovation Center for Photovolatic Science and Engineering, Changzhou University, Changzhou 213164 (China); Hu, J. [School of Material Science and Engineering, Jiangsu Collaborative Innovation Center for Photovolatic Science and Engineering, Changzhou University, Changzhou 213164 (China); Jiangsu Key Laboratory of Material Surface Technology, Changzhou 213164 (China); Li, C. [Light Industry College of Liaoning University, Shenyang 110036 (China)

2016-04-30

Highlights: • The Nb coating produced by HEMAA offers good protection for 304SS in acid solution. • The coating increases corrosion potential and induces decrease of corrosion rate. • The protection of coating is ascribed to the stability of Nb in acid solution. - Abstract: The niobium coating is fabricated on the surface of AISI Type 304 stainless steel (304SS) by using a high energy micro arc alloying technique in order to improvecorrosion resistance of the steel against acidic environments. The electrochemical corrosion resistance of the niobium coating in 0.7 M sulfuric acid solutions is evaluated by electrochemical impedance spectroscopy, potentiodynamic polarization and the open circuit potential versus time. Electrochemical measurements indicate that the niobium coating increases the free corrosion potential of the substrate by 110 mV and a reduction in the corrosion rate by two orders of magnitude compared to the substrate alone. The niobium coating maintains large impedance and effectively offers good protection for the substrate during the long-term exposure tests, which is mainly ascribed to the niobium coating acting inhibiting permeation of corrosive species. Finally, the corresponding electrochemical impedance models are proposed to elucidate the corrosion resistance behavior of the niobium coating in acid solutions.
Corrosion behavior of niobium coated 304 stainless steel in acid solution

International Nuclear Information System (INIS)

Pan, T.J.; Chen, Y.; Zhang, B.; Hu, J.; Li, C.

2016-01-01

Highlights: • The Nb coating produced by HEMAA offers good protection for 304SS in acid solution. • The coating increases corrosion potential and induces decrease of corrosion rate. • The protection of coating is ascribed to the stability of Nb in acid solution. - Abstract: The niobium coating is fabricated on the surface of AISI Type 304 stainless steel (304SS) by using a high energy micro arc alloying technique in order to improvecorrosion resistance of the steel against acidic environments. The electrochemical corrosion resistance of the niobium coating in 0.7 M sulfuric acid solutions is evaluated by electrochemical impedance spectroscopy, potentiodynamic polarization and the open circuit potential versus time. Electrochemical measurements indicate that the niobium coating increases the free corrosion potential of the substrate by 110 mV and a reduction in the corrosion rate by two orders of magnitude compared to the substrate alone. The niobium coating maintains large impedance and effectively offers good protection for the substrate during the long-term exposure tests, which is mainly ascribed to the niobium coating acting inhibiting permeation of corrosive species. Finally, the corresponding electrochemical impedance models are proposed to elucidate the corrosion resistance behavior of the niobium coating in acid solutions.
Influence of Hydrostatic Pressure on the Corrosion Behavior of Superhydrophobic Surfaces on Bare and Oxidized Aluminum Substrates.

Science.gov (United States)

Ou, J F; Fang, X Z; Zhao, W J; Lei, S; Xue, M S; Wang, F J; Li, C Q; Lu, Y L; Li, W

2018-05-22

It is generally recognized that superhydrophobic surfaces in water may be used for corrosion resistance due to the entrapped air in the solid/liquid interface and could find potential applications in the protection of ship hull. For a superhydrophobic surface, as its immersion depth into water increases, the resultant hydrostatic pressure is also increased, and the entrapped air can be squeezed out much more easily. It is therefore predicted that high hydrostatic pressure would cause an unexpected decrease in corrosion resistance for the vessels in deep water (e.g., submarines) because of the unstable entrapped air. In this work, in order to clarify the role of hydrostatic pressure in the corrosion behavior of superhydrophobic surfaces, two typical superhydrophobic surfaces (SHSs) were prepared on bare and oxidized aluminum substrates, respectively, and then were immersed into the NaCl aqueous solutions with different depths of ∼0 cm (hydrostatic pressure ∼0 kPa), 10 cm (1 kPa), and 150 cm (15 kPa). It was found out for the SHSs on the oxidized Al, as the hydrostatic pressure increased, the corrosion behavior became severe. However, for the SHSs on the bare Al, their corrosion behavior was complex due to hydrostatic pressure. It was found that the corrosion resistance under 1 kPa was the highest. Further mechanism analysis revealed that this alleviated corrosion behavior under 1 kPa resulted from suppressing the oxygen diffusion through the liquid and reducing the subsequent corrosion rate as compared with 0 kPa, whereas the relatively low hydrostatic pressure (HP) could stabilize the entrapped air and hence enhance the corrosion resistance, compared with 15 kPa. The present study therefore provided a fundamental understanding for the applications of SHSs to prevent the corrosion, especially for various vessels in deep water.
Corrosion behavior of corrosion resistant alloys in stimulation acids

Energy Technology Data Exchange (ETDEWEB)

Cheldi, Tiziana [ENI E and P Division, 20097 San Donato Milanese Milano (Italy); Piccolo, Eugenio Lo; Scoppio, Lucrezia [Centro Sviluppo Materiali, via Castel Romano 100, 00128 Rome (Italy)

2004-07-01

In the oil and gas industry, selection of CRAs for downhole tubulars is generally based on resistance to corrosive species in the production environment containing CO{sub 2}, H{sub 2}S, chloride and in some case elemental sulphur. However, there are non-production environments to which these materials must also be resistant for either short term or prolonged duration; these environments include stimulation acids, brine and completion fluids. This paper reports the main results of a laboratory study performed to evaluate the corrosion and stress corrosion behaviour to the acidizing treatments of the most used CRAs for production tubing and casing. Laboratory tests were performed to simulate both 'active' and 'spent' acids operative phases, selecting various environmental conditions. The selected steel pipes were a low alloyed steel, martensitic, super-martensitic, duplex 22 Cr, superduplex 25 Cr and super-austenitic stainless steels (25 Cr 35 Ni). Results obtained in the 'active' acid environments over the temperature range of 100-140 deg. C, showed that the blend acids with HCl at high concentration and HCl + HF represented too much severe conditions, where preventing high general corrosion and heavy localised corrosion by inhibition package becomes very difficult, especially for duplex steel pipe, where, in some case, the specimens were completely dissolved into the solution. On the contrary, all steels pipes were successfully protected by inhibitor when organic acid solution (HCOOH + CH{sub 3}COOH) were used. Furthermore, different effectiveness on corrosion protection was showed by the tested inhibitors packages: e.g. in the 90% HCl at 12% + 10 CH{sub 3}COOH acid blend. In 'spent' acid environments, all steel pipes showed to be less susceptible to the localised and general corrosion attack. Moreover, no Sulphide Stress Corrosion Cracking (SSC) was observed. Only one super-austenitic stainless steel U-bend specimen showed
Corrosion behavior of aluminum-alumina composites in aerated 3.5 percent chloride solution

Science.gov (United States)

Acevedo Hurtado, Paul Omar

Aluminum based metal matrix composites are finding many applications in engineering. Of these Al-Al2O3 composites appear to have promise in a number of defense applications because of their mechanical properties. However, their corrosion behavior remains suspect, especially in marine environments. While efforts are being made to improve the corrosion resistance of Al-Al2O3 composites, the mechanism of corrosion is not well known. In this study, the corrosion behavior of powder metallurgy processed Al-Cu alloy reinforced with 10, 15, 20 and 25 vol. % Al2O3 particles (XT 1129, XT 2009, XT 2048, XT 2031) was evaluated in aerated 3.5% NaCl solution using microstructural and electrochemical measurements. AA1100-O and AA2024T4 monolithic alloys were also studied for comparison purposes. The composites and unreinforced alloys were subjected to potentiodynamic polarization and Electrochemical Impedance Spectroscopy (EIS) testing. Addition of 25 vol. % Al2O 3 to the base alloys was found to increase its corrosion resistance considerably. Microstructural studies revealed the presence of intermetallic Al2Cu particles in these composites that appeared to play an important role in the observations. Pitting potential for these composites was near corrosion potential values, and repassivation potential was below the corresponding corrosion potential, indicating that these materials begin to corrode spontaneously as soon as they come in contact with the 3.5 % NaCl solution. EIS measurements indicate the occurrence of adsorption/diffusion phenomena at the interface of the composites which ultimately initiate localized or pitting corrosion. Polarization resistance values were extracted from the EIS data for all the materials tested. Electrically equivalent circuits are proposed to describe and substantiate the corrosive processes occurring in these Al-Al2O 3 composite materials.
Electrochemical corrosion behaviors of the X90 linepipe steel in NS4 solution

Directory of Open Access Journals (Sweden)

Jinheng Luo

2016-10-01

Full Text Available Oil and gas line pipes are laid underground and run through different areas in the laying process, so they will be subjected to different degrees of corrosion and even crack, leading to enormous casualties and economic losses. In order to guarantee the safe operation of line pipes, therefore, it is significant to investigate the electrochemical corrosion behaviors of pipe steel in a simulated soil environment. In this paper, the electrochemical corrosion behaviors of the base metals and welding materials of API 5L X90 steel longitudinally submerged arc welding pipes in near-neutral simulated soil solution (NS4 were studied by means of the electrochemical impedance spectroscopy (EIS and the potentiodynamic polarization testing technology. It is shown that the typical characteristic of anodic dissolution is presented but with no passivation phenomenon when X90 linepipe steel is put in NS4 solution. The base material is thermodynamically more stable than the seam weld material. The base material and seam weld samples were polarized under −850 mV polarization potential for different durations. It is demonstrated that with the proceeding of polarization, the polarization resistance and the corrosion resistance increase while the corrosion current density decreases. And the corrosion resistance of base material is better than that of seam weld material.

Comparison of corrosion behavior between fusion cladded and explosive cladded Inconel 625/plain carbon steel bimetal plates

International Nuclear Information System (INIS)

Zareie Rajani, H.R.; Akbari Mousavi, S.A.A.; Madani Sani, F.

2013-01-01

Highlights: ► Both explosive and fusion cladding aggravate the corrosion resistance of Inconel 625. ► Fusion cladding is more detrimental to nonuniform corrosion resistance. ► Single-layered fusion coat does not show any repassivation ability. ► Adding more layers enhance the corrosion resistance of fusion cladding Inconel 625. ► High impact energy spoils the corrosion resistance of explosive cladding Inconel 625. -- Abstract: One of the main concerns in cladding Inconel 625 superalloy on desired substrates is deterioration of corrosion resistance due to cladding process. The present study aims to compare the effect of fusion cladding and explosive cladding procedures on corrosion behavior of Inconel 625 cladding on plain carbon steel as substrate. Also, an attempt has been made to investigate the role of load ratio and numbers of fusion layers in corrosion behavior of explosive and fusion cladding Inconel 625 respectively. In all cases, the cyclic polarization as an electrochemical method has been applied to assess the corrosion behavior. According to the obtained results, both cladding methods aggravate the corrosion resistance of Inconel 625. However, the fusion cladding process is more detrimental to nonuniform corrosion resistance, where the chemical nonuniformity of fusion cladding superalloy issuing from microsegregation, development of secondary phases and contamination of clad through dilution hinders formation of a stable passive layer. Moreover, it is observed that adding more fusion layers can enhance the nonuniform corrosion resistance of fusion cladding Inconel 625, though this resistance still remains weaker than explosive cladding superalloy. Also, the results indicate that raising the impact energy in explosive cladding procedure drops the corrosion resistance of Inconel 625.
The effect of recrystallization on corrosion and electrochemical behavior of 7150 Al alloy

Energy Technology Data Exchange (ETDEWEB)

Peng, G.S.; Chen, K.H.; Fang, H.C.; Chen, S.Y.; Chao, H. [State Key Laboratory for Powder Metallurgy, Central South University, Changsha, Hunan 410083 (China)

2011-01-15

By weight loss, potentiodynamic polarization, cyclic voltammetry, and electrochemical impedance spectroscopy (EIS) techniques complemented by optical and scanning electron microscopy observations, the effect of recrystallization on the corrosion, and electrochemical behavior of 7150 Al alloy was studied. The results indicated that the high recrystallization fraction 7150-1 was worse than the low recrystallization fraction 7150-2 on corrosion resistance. The analysis of EIS indicated that 7150-1 exhibited obvious pitting corrosion at 5 h immersion time, whereas 7150-2 showed no obvious pitting corrosion even at 33 h. The corrosion route developed along the grain boundary of recrystallization grains, not along the grain boundary of unrecrystallization grains. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)
Effect of free Cr content on corrosion behavior of 3Cr steels in a CO2 environment

Science.gov (United States)

Li, Wei; Xu, Lining; Qiao, Lijie; Li, Jinxu

2017-12-01

The corrosion behavior of 3Cr steels with three microstructures (martensite, bainite, combined ferrite and pearlite) in simulated oil field formation water with a CO2 partial pressure of 0.8 MPa was investigated. The relationships between Cr concentrations in corrosion scales and corrosion rates were studied. The precipitated phases that contained Cr were observed in steels of different microstructures, and free Cr content levels were compared. The results showed that steel with the martensite microstructure had the highest free Cr content, and thus had the highest corrosion resistance. The free Cr content of bainite steel was lower than that of martensite steel, and the corrosion rate of bainite steel was higher than that of martensite steel. Because large masses of Cr were combined in ferrite and pearlite steel, the corrosion rates of ferrite and pearlite steel were the highest. Free Cr content in steel affects its corrosion behavior greatly.
Notch Effect on Tensile Deformation Behavior of 304L and 316L Steels in Liquid Helium and Hydrogen

International Nuclear Information System (INIS)

Shibata, K.; Fujii, H.

2004-01-01

Tensile tests of type 304L and 316L steels were carried out using round bar specimens with a notch in liquid helium, hydrogen, liquid nitrogen and at ambient temperature. The obtained tensile strengths were compared with the tensile strengths of smooth specimens. For smooth specimens, tensile strength increased with a decrease in temperature and the strengths in liquid helium and hydrogen show similar values in both steels. For notched specimen of 304L steel, tensile strength (including fracture strength) increased noticeably from ambient to liquid nitrogen temperature but showed a large decrease in liquid helium and hydrogen. In liquid hydrogen and helium, the tensile strength is a little lower in liquid hydrogen than in liquid helium and both strengths are lower than tensile strengths of smooth specimens. For notched specimen of 316L steel, an increase in tensile strength from ambient to liquid nitrogen temperature was not so large and a decrease from liquid nitrogen to liquid hydrogen was small. The tensile strengths in liquid helium and hydrogen were nearly same and higher than those of smooth specimens. Different behavior of serration was observed between liquid helium and hydrogen, and between 304L and 316L steels. The reasons for these differences were discussed using computer simulation
Preliminary study on the corrosion behavior of carbon steel in Horonobe groundwater environment

International Nuclear Information System (INIS)

Taniguchi, Naoki; Kogawa, Noritaka; Maeda, Kazuto

2006-08-01

It is necessary to understand the corrosion behavior of candidate overpack materials to plan the in-situ engineered barrier test at underground laboratory constructing at Horonobe and to design the overpacks suitable to Horonobe environment. The preliminary corrosion tests of carbon steel which is a candidate material for overpacks were carried out using artificial groundwater and actual groundwater sampled at Horonobe. As the results of anodic polarization experiments, the anodic polarization curves of carbon steel in buffer material were active dissolution type, and the corrosion type of carbon steel in Horonobe groundwater environment was expected to be general corrosion. The results of immersion test under air equilibrium condition showed that the degrees of corrosion localization were not exceeded the data obtained in previous studies. The trend of corrosion rates in buffer material under anaerobic condition were similar to the data obtained in previous studies. Based on the experimental results, it was confirmed that the corrosion assessment model and assumed corrosion rate in second progress report (H12 report) can be applied to the assessment for Horonobe groundwater condition. (author)
Corrosion behavior of high purity Fe-Cr-Ni alloys in trans-passive condition

International Nuclear Information System (INIS)

Mayuzumi, Masami; Ohta, Jyoji; Kako, Kenji

1998-01-01

The corrosion behavior of high-purity (99.99%) Fe-Cr-Ni alloys was investigated in 13 N nitric acid with/without Ce 4+ ions to clarify the effect of impurities on the trans-passive corrosion of stainless steel. The following results were obtained. (1) Almost no intergranular corrosion was observed in the high-purity alloys, although the corrosion rate of the matrix region was nearly the same as that of a commercial stainless steel with the same Cr and Ni content. (2) Due to the improved intergranular corrosion resistance, the effect of the purification became significant in the corrosion condition with the grain-separation being predominant. (3) The high-purity alloys showed higher susceptivility to intergranular corrosion with aging treatment between 873 K and 1073 K. Although the sulfuric acid/copper sulfate test suggested the formation of Cr-depleted zones, a grain boundary micro-analysis using a FETEM with an EDX did not reveal any change in Cr content or impurity segregain along the grain boundaries. The mechanism of corrosion enhancement resulting from the aging treatment remains nuclear. (author)
Stress Corrosion Cracking Behavior of LD10 Aluminum Alloy in UDMH and N2O4 propellant

Science.gov (United States)

Zhang, Youhong; Chang, Xinlong; Liu, Wanlei

2018-03-01

The LD10 aluminum alloy double cantilever beam specimens were corroded under the conditions of Unsymmetric Uimethyl Hydrazine (UDMH), Dinitrogen Tetroxide (N2O4), and 3.5% NaCl environment. The crack propagation behavior of the aluminum alloy in different corrosion environment was analyzed. The stress corrosion cracking behavior of aluminum alloy in N2O4 is relatively slight and there are not evident stress corrosion phenomenons founded in UDMH.
Corrosion and alteration of materials from the nuclear industry; La Corrosion et l'alteration des materiaux du nucleaire

Energy Technology Data Exchange (ETDEWEB)

Beauvy, M.; Berthoud, G.; Defranceschi, M.; Ducros, G.; Feron, D.; Guerin, Y.; Latge, C.; Limoge, Y.; Madic, C.; Santarini, G.; Seiler, J.M.; Vernaz, E.; Richet, C.

2010-07-01

The control of the corrosion phenomenon is of prime importance for the nuclear industry. The efficiency and the safety of facilities can be affected by this phenomenon. The nuclear industry has to face corrosion for a large variety of materials submitted to various environments. Metallic corrosion operates in the hot and aqueous environment of water reactors which represent the most common reactor type in the world. Progresses made in the control of the corrosion of the different components of these reactors allow to improve their safety. Corrosion is present in the facilities of the back-end of the fuel cycle as well (corrosion in acid environment in fuel reprocessing plants, corrosion of waste containers in disposal and storage facilities, etc). The future nuclear systems will widen even more the range of materials to be studied and the situations in which they will be placed (corrosion by liquid metals or by helium impurities). Very often, corrosion looks like a patchwork of particular cases in its description. The encountered corrosion problems and their study are presented in this book according to chapters representing the main sectors of the nuclear industry and classified with respect to their phenomenology. This monograph illustrates the researches in progress and presents some results of particular importance obtained recently. Content: 1 - Introduction: context, stakes and goals; definition of corrosion; a complex science; corrosion in the nuclear industry; 2 - corrosion in water reactors - phenomenology, mechanisms, remedies: A - uniform corrosion: mechanisms, uniform corrosion of fuel cladding, in-situ measurement of generalized corrosion rate by electrochemical methods, uniform corrosion of nickel alloys, characterization of the passive layer and growth mechanisms, the PACTOLE code - an integrating tool, influence of water chemistry on corrosion and contamination, radiolysis impact on uniform corrosion; B - stress corrosion: stress corrosion cracking
Long term corrosion behavior of the WAK-HLW glass in salt solutions

International Nuclear Information System (INIS)

Luckscheiter, B.; Nesovic, M.

1998-01-01

The corrosion behavior of the HLW glass GP WAK1 containing simulated HLW oxides from the WAK reprocessing plant in Karlsruhe is investigated in long-term corrosion experiments at high S/V ratios in two reference brines at 110 and 190 C. In case of the MgCl 2 -rich solution the leachate becomes increasingly acid with reaction time up to a final pH of about 3.5 at 190 C. In the NaCl-rich solution the pH rises to about 8.5 after one year of reaction. The release of soluble elements in MgCl 2 solution, under Si-saturated conditions, is proportional to the surface area of the sample and the release increases at 190 C according to a t 1/2 rate law. This time dependence may be an indication of diffusion controlled matrix dissolution. However, at 110 C the release of the mobile elements cannot be described by a t 1/2 rate law as the time exponents are much lower than 0.5. This difference in corrosion behavior may be explained by the higher pH of about 5 at 110 C. In case of NaCl solution under alkaline conditions, the release of soluble elements is not proportional to the surface area of the sample and it increases with time exponents much lower than 0.5. After one year of reaction at 190 C a sharp increase of the release values of some elements was observed. This increase might be explained by the high pH of the solution attained after one year. The corrosion mechanism in NaCl solution, as well as in MgCl 2 solution at 110 C, has not yet been explained. By corrosion experiments in water at constant pH values between 2 and 10, it could be shown that the time exponents of the release of Li and B decrease with increasing pH of the solution. This result can explain qualitatively the differences found in the corrosion behavior of the glass under the various conditions
Corrosion Behavior of Metal Active Gas Welded Joints of a High-Strength Steel for Automotive Application

Science.gov (United States)

Garcia, Mainã Portella; Mantovani, Gerson Luiz; Vasant Kumar, R.; Antunes, Renato Altobelli

2017-10-01

In this work, the corrosion behavior of metal active gas-welded joints of a high-strength steel with tensile yield strength of 900 MPa was investigated. The welded joints were obtained using two different heat inputs. The corrosion behavior has been studied in a 3.5 wt.% NaCl aqueous solution using electrochemical impedance spectroscopy and potentiodynamic polarization tests. Optical microscopy images, scanning electron microscopy and transmission electron microscopy with energy-dispersive x-ray revealed different microstructural features in the heat-affected zone (HAZ) and the weld metal (WM). Before and after the corrosion process, the sample was evaluated by confocal laser scanning microscopy to measure the depth difference between HAZ and WM. The results showed that the heat input did not play an important role on corrosion behavior of HSLA steel. The anodic and cathodic areas of the welded joints could be associated with depth differences. The HAZ was found to be the anodic area, while the WM was cathodic with respect to the HAZ. The corrosion behavior was related to the amount and orientation nature of carbides in the HAZ. The microstructure of the HAZ consisted of martensite and bainite, whereas acicular ferrite was observed in the weld metal.
Influence of Temperature on Corrosion Behavior of 2A02 Al Alloy in Marine Atmospheric Environments

Directory of Open Access Journals (Sweden)

Min Cao

2018-02-01

Full Text Available The corrosion behavior of 2A02 Al alloy under 4 mg/cm2 NaCl deposition at different temperatures (from 30 to 80 °C has been studied. This corrosion behavior was researched using mass-gain, scanning electron microscopy-SEM, laser scanning confocal microscopy-LSCM, X-ray photoelectron spectroscopy-XPS and other techniques. The results showed and revealed that the corrosion was maximal at 60 °C after 200 h of exposure. The increase of temperature not only affected the solubility of oxygen gas in the thin film, but also promoted the transport of ions (such as Cl−, and the formation of protective AlO(OH, which further affects the corrosion speed.
Influence of Temperature on Corrosion Behavior of 2A02 Al Alloy in Marine Atmospheric Environments

Science.gov (United States)

Cao, Min; Liu, Li; Fan, Lei; Yu, Zhongfen; Li, Ying; Oguzie, Emeka E.; Wang, Fuhui

2018-01-01

The corrosion behavior of 2A02 Al alloy under 4 mg/cm2 NaCl deposition at different temperatures (from 30 to 80 °C) has been studied. This corrosion behavior was researched using mass-gain, scanning electron microscopy-SEM, laser scanning confocal microscopy-LSCM, X-ray photoelectron spectroscopy-XPS and other techniques. The results showed and revealed that the corrosion was maximal at 60 °C after 200 h of exposure. The increase of temperature not only affected the solubility of oxygen gas in the thin film, but also promoted the transport of ions (such as Cl−), and the formation of protective AlO(OH), which further affects the corrosion speed. PMID:29401690
Corrosion Behavior of Welded Joints for Cargo Oil Tanks of Crude Oil Carrier

Institute of Scientific and Technical Information of China (English)

Jin-shan WEI; Yan-chang QI; Zhi-ling TIAN; Yun PENG

2016-01-01

E32 grade corrosion resistant steel was welded with welding wires with three different S contents.The mi-crostructure,mechanical properties,inclusions,and corrosion behavior of welded joint were investigated.The joint coupon corrosion test and potentiodynamic polarization test were carried out under the simulated corrosion environ-ment of the inner bottom plates of cargo oil tanks.The pitting initiation and propagation mechanism of the weld metal were studied by scanning electron microscopy and infinite focus.The results indicated that the microstructures of three kinds of weld metals are all composed of acicular ferrite,ferrite side-plate and proeutectoid ferrite.The micro-structure of heat-affected zone is composed predominantly of bainite.Joint welded with low S filler wire has good me-chanical properties.S can decrease free corrosion potential and increase the corrosion tendency.The pitting initiation is oxide inclusion or sulfide-oxide inclusion complex.S can induce the formation of occluded area and promote the corrosion propagation.The chemical compositions of weld metal is similar to base metal,which can limit the galvanic corrosion between weld metal and base metal,and avoid formation of corrosion step.
Effect of niobium element on the electrochemical corrosion behavior of depleted uranium

Energy Technology Data Exchange (ETDEWEB)

Wu, Yanping, E-mail: wuyanping-2@126.com; Wu, Quanwen; Zhu, Shengfa, E-mail: zhushf-306@163.com; Pu, Zhen; Zhang, Yanzhi; Wang, Qinguo; Lang, Dingmu; Zhang, Yuping

2016-09-15

Depleted uranium (DU) has many military and civilian uses. However, its high chemical reactivity limits its application. The effect of Nb content on corrosion behavior of DU is evaluated by scanning Kelvin probe and electrochemical corrosion measurements. The Volta potential value of DU and U-2.5 wt% Nb is about the same level, the Volta potential value of U-5.7 wt% Nb has a rise of 370mV{sub SHE} in comparison with DU. The polarization current of U-5.7 wt% Nb alloy is about an order of magnitude of that of DU. The Nb{sub 2}O{sub 5} is the protective layer for the U-Nb alloys. The negative potential of Nb-depleted α phase is the main reason of the poor corrosion resistance of DU and U-2.5 wt% Nb alloy. - Highlights: • New method (scanning Kelvin probe) was used to study the corrosion property. • Three types of corrosion morphologies were found after potentiodynamic polarization. • The effect of impurity elements on corrosion property was mentioned. • The corrosion mechanism of DU and U-Nb alloys was discussed.
Electrochemical corrosion behavior of carbon steel with bulk coating holidays

Institute of Scientific and Technical Information of China (English)

无

2006-01-01

With epoxy coal tar as the coating material, the electrochemical corrosion behavior of Q235 with different kinds of bulk coating holidays has been investigated with EIS (Electrochemical Impedance Spectroscopy) in a 3.5vol% NaCl aqueous solution.The area ratio of bulk coating holiday to total coating area of steel is 4.91%. The experimental results showed that at free corrosionpotential, the corrosion of carbon steel with disbonded coating holiday is heavier than that with broken holiday and disbonded & broken holiday with time; Moreover, the effectiveness of Cathodic Protection (CP) of carbon steel with broken holiday is better than that with disbonded holiday and disbonded & broken holiday on CP potential -850 mV (vs CSE). Further analysis indicated that the two main reasons for corrosion are electrolyte solution slowly penetrating the coating, and crevice corrosion at steel/coating interface near holidays. The ratio of impedance amplitude (Z) of different frequency to minimum frequency is defined as K value. The change rate of K with frequency is related to the type of coating holiday.
The Effect of Friction Stir Welding on Corrosion Behavior of Ti-6Al-4V

Science.gov (United States)

Nasresfahani, Ali Reza; Soltanipur, Abdol Reza; Farmanesh, Khosro; Ghasemi, Ali

2017-09-01

Fusion welding can deteriorate corrosion behavior of Ti-6Al-4V alloy. However, the use of friction stir welding leads to a more appropriate corrosion resistance. In this study, the corrosion resistance of welded zones of Ti-6Al-4V alloy using friction stir welding technique is evaluated. For these purposes, the study of structural characteristics using SEM and FESEM equipped with EDS micro-analyses was conducted. Micro-hardness test was also employed to estimate the hardness of welded zones. Corrosion behavior was investigated by a potentiostat instrument. SEM micrographs, EDS and XRD analyses confirmed non-uniformity of chemical composition within the welded zones. The results reveal that the stir zone contains typical alpha and prior beta phases. Nevertheless, thermomechanical zone included equiaxed and bimodal lamellae structure. Furthermore, the presence of different types of phases and microstructure in the thermomechanical zone led to reduced corrosion resistance. The corresponding values of corrosion current density in the stir zone, thermomechanical zone and base metal were 0.048, 0.55 and 0.032 µA, respectively. Corresponding corrosion potential for these zones was estimated as -207, -110 and -157 mV. Evidently, the results show that corrosion resistance of thermomechanical zone is less than that of the stir zone and both zones have lower value than the base metal.
Fatigue behavior of Type 316 stainless steel following neutron irradiation inducing helium

International Nuclear Information System (INIS)

Grossbeck, M.L.; Liu, K.C.

1980-01-01

Since a tokamak reactor operates in a cyclic mode, thermal stresses will result in fatigue in structural components, especially in the first wall and blanket. There has been limited work on fatigue in irradiated alloys but none on irradiated materials containing significant amounts of irradiation-induced helium. To provide scoping data and to study the effects of irradiation on fatigue behavior, 20%-cold-worked type 316 stainless steel from the MFE reference heat was studied
Effect of corrosion and sandblasting on the high cycle fatigue behavior of reinforcing B500C steel bars

Directory of Open Access Journals (Sweden)

Marina C. Vasco

2017-10-01

Full Text Available In a series of applications, steel reinforced concrete structures are subjected to fatigue loads during their service life, what in most cases happens in corrosive environments. Surface treatments have been proved to represent proper processes in order to improve both fatigue and corrosion resistances. In this work, the effect of corrosion and sandblasting on the high cycle fatigue behavior reinforcing steel bars is investigated. The investigated material is the reinforcing steel bar of technical class B500C, of nominal diameter of 12 mm. Steel bars specimens were first exposed to corrosion in alternate salt spray environment for 30 and 60 days and subjected to both tensile and fatigue tests. Then, a series of specimens were subjected to common sandblasting, corroded and mechanically tested. Metallographic investigation and corrosion damage evaluation regarding mass loss and martensitic area reduction were performed. Tensile tests were conducted after each corrosion exposure period prior to the fatigue tests. Fatigue tests were performed at a stress ratio, R, of 0.1 and loading frequency of 20 Hz. All fatigue tests series as well as tensile test were also performed for as received steel bars to obtain the reference behavior. The results have shown that sandblasting hardly affects the tensile behavior of the uncorroded material. The effect of sandblasting on the tensile behavior of pre-corroded specimens seems to be also limited. On the other hand, fatigue results indicate an improved fatigue behavior for the sandblasted material after 60 days of corrosion exposure. Martensitic area reductions, mass loss and depth of the pits were significantly smaller for the case of sandblasted materials, which confirms an increased corrosion resistance
Analysis of the Corrosion Behavior of an A-TIG Welded SS 409 Weld Fusion Zone

Science.gov (United States)

Vidyarthy, R. S.; Dwivedi, D. K.

2017-11-01

AISI 409 (SS 409) ferritic stainless steel is generally used as the thick gauge section in freight train wagons, in ocean containers, and in sugar refinery equipment. Activating the flux tungsten inert gas (A-TIG) welding process can reduce the welding cost during fabrication of thick sections. However, corrosion behavior of the A-TIG weld fusion zone is a prime concern for this type of steel. In the present work, the effect of the A-TIG welding process parameters on the corrosion behavior of a weld fusion zone made of 8-mm-thick AISI 409 ferritic stainless-steel plate has been analyzed. Potentiodynamic polarization tests were performed to evaluate the corrosion behavior. The maximum corrosion potential ( E corr) was shown by the weld made using a welding current of 215 A, a welding speed of 95 mm/min, and a flux coating density of 0.81 mg/cm2. The minimum E corr was observed in the weld made using a welding current of 190 A, a welding speed of 120 mm/min, and a flux coating density of 1.40 mg/cm2. The current study also presents the inclusive microstructure-corrosion property relationships using the collective techniques of scanning electron microscopy, energy-dispersive x-ray spectroscopy, and x-ray diffraction.
Corrosion behavior of electrodeposited Co-Fe alloys in aerated solutions

Energy Technology Data Exchange (ETDEWEB)

Chansena, A. [Research Unit on Corrosion, College of Data Storage Innovation, King Mongkut' s Institute of Technology Ladkrabang, Bangkok 10520 (Thailand); Sutthiruangwong, S., E-mail: sutha.su@kmitl.ac.th [Department of Chemistry, Faculty of Science, King Mongkut' s Institute of Technology Ladkrabang, Bangkok 10520 (Thailand); Research Unit on Corrosion, College of Data Storage Innovation, King Mongkut' s Institute of Technology Ladkrabang, Bangkok 10520 (Thailand)

2017-05-01

Co-Fe alloy is an important component for reader-writer in hard disk drive. The surface of the alloy is exposed to the environment both in gas phase and in liquid phase during manufacturing process. The study of corrosion behavior of Co-Fe alloys can provide useful fundamental data for reader-writer production planning especially when corrosion becomes a major problem. The corrosion study of electrodeposited Co-Fe alloys from cyclic galvanodynamic polarization was performed using potentiodynamic polarization technique. The composition of electrodeposited Co-Fe alloys was determined by X-ray fluorescence spectrometry. The patterns from X-ray diffractometer showed that the crystal structure of electrodeposited Co-Fe alloys was body-centered cubic. A vibrating sample magnetometer was used for magnetic measurements. The saturation magnetization (M{sub s}) was increased and the intrinsic coercivity (H{sub ci}) was decreased with increasing Fe content. The corrosion rate study was performed in aerated deionized water and aerated acidic solutions at pH 3, 4 and 5. The corrosion rate diagram for Co-Fe alloys was constructed. It was found that the corrosion rate of Co-Fe alloys was increased with increasing Fe content in both aerated deionized water and aerated acidic solutions. In aerated pH 3 solution, the Co-Fe alloy containing 78.8% Fe showed the highest corrosion rate of 7.7 mm yr{sup −1} with the highest M{sub s} of 32.0 A m{sup 2} kg{sup −1}. The corrosion rate of the alloy with 23.8% Fe was at 1.1 mm yr{sup −1} with M{sub s} of 1.2 A m{sup 2} kg{sup −1}. In aerated deionized water, the alloy with the highest Fe content of 78.5% still showed the highest corrosion rate of 0.0059 mm yr{sup −1} while the alloy with the lowest Fe content of 20.4% gave the lowest corrosion rate of 0.0045 mm yr{sup −1}. - Highlights: • The aeration during corrosion measurement simulates reader-writer head production environment. • The corrosion rate diagram for Co-Fe alloys

Tritium and helium behavior in irradiated beryllium

International Nuclear Information System (INIS)

Billone, M.C.; Lin, C.C.; Baldwin, D.L.

1990-11-01

Large quantities of Be (> 100 metric tons) are planned for use in the ITER blanket design to enhance tritium breeding and to act as a thermal barrier between coolant and breeder. Tritium retention/release and He-induced swelling are important issues in blanket design. The data base on tritium and helium behavior in Be is reviewed. New data on tritium retention/release and He bubble growth are presented for Be irradiated to 5 x 10 22 n(E > 1 MeV)/cm 2 at ∼75 degree C and postirradiation-annealed for 700 hours at 500 degree C. A model (diffusion/desorption) is proposed and tested against the data base to determine tritium diffusivity and the desorption rate constant. Similarly a model for He-induced swelling is developed and tested against the data base. The dependence of tritium retention and release on He content and impurities (e.g. BeO) is also explored. 11 refs., 6 figs
Long-term corrosion behaviors of Hastelloy-N and Hastelloy-B3 in moisture-containing molten FLiNaK salt environments

International Nuclear Information System (INIS)

Ouyang, Fan-Yi; Chang, Chi-Hung; Kai, Ji-Jung

2014-01-01

Highlights: •Corrosion behaviors of Hastelloy-N and -B3 in molten FLiNaK salt at 700 °C. •The alleviated corrosion rate of alloys was observed after long-hour immersion. •Long-term corrosion rate was limited by diffusion from matrix to alloy surface. •Corrosion pattern transferred from intergranular corrosion into general corrosion. •Presence of minor H 2 O did not greatly influence the long-term corrosion behavior. -- Abstract: This study investigated long-term corrosion behaviors of Ni-based Hastelloy-N and Hastelloy-B3 under moisture-containing molten alkali fluoride salt (LiF–NaF–KF: 46.5–11.5–42%) environment at an ambient temperature of 700 °C. The Hastelloy-N and Hastelloy-B3 experienced similar weight losses for tested duration of 100–1000 h, which was caused by aggregate dissolution of Cr and Mo into FLiNaK salts. The corrosion rate of both alloys was high initially, but then reduced during the course of the test. The alleviated corrosion rate was due to the depletion of Cr and Mo near surface of the alloys and thus the long-term corrosion rate was controlled by diffusion of Cr and Mo outward to the alloy surface. The results of microstructural characterization revealed that the corrosion pattern for both alloys tended to be intergranular corrosion at early stage of corrosion test, and then transferred to general corrosion for longer immersion hours
Corrosion behavior of a superduplex stainless steel in chloride aqueous solution

Science.gov (United States)

Dabalà, Manuele; Calliari, Irene; Variola, Alessandra

2004-04-01

Super duplex stainless steels (SDSS) have been widely used as structural materials for chemical plants (especially in those engaged in phosphoric acid production), in the hydrometallurgy industries, and as materials for offshore applications due to their excellent corrosion resistance in chloride environments, compared with other commercial types of ferritic stainless steels. These alloys also possess superior weldability and better mechanical properties than austenitic stainless steels. However, due to their two-phase structure, the nature of which is very dependent on their composition and thermal history, the behavior of SDSS regarding localized corrosion appears difficult to predict, especially in chloride environments. To improve their final properties, the effect of the partition of the alloying elements between the two phases, and the composition and microstructure of each phase are the key to understanding the localized corrosion phenomena of SDSS. This paper concerns the effects of the SDSS microstructure and heat treatment on the SDSS corrosion resistance in aqueous solutions, containing different amounts of NaCl at room temperature.
Stress-corrosion behavior of aluminum-lithium alloys in aqueous salt environments

Science.gov (United States)

Pizzo, P. P.; Galvin, R. P.; Nelson, H. G.

1984-01-01

The stress corrosion susceptibility of two powder metallurgy (P/M) alloys, Al-Li-Cu and Al-Li-Cu-Mg; two mechanically attrited (M/A) alloys, Al-Li-Cu and Al-Li-Mg; and two wrought, ingot alloys, X-2020 and AA7475, are compared. Time-dependent fracture in an aqueous sodium chloride environment under alternate immersion condition was found to vary significantly between alloys. The stress corrosion behavior of the two powder metallurgy processed alloys was studied in detail under conditions of crack initiation, static crack growth, and fatigue crack growth. A variety of stress corrosion tests were performed including smooth surface, time-to-failure tests; potentiostatic tests on smooth surfaces exposed to constant applied strain rates; and fracture mechanics-type tests under static and cyclic loads. Both alloys show surface pitting and subsequent intergranular corrosion. Pitting is more severe in the magnesium-bearing alloy and is associated with stringer particles strung along the extrusion direction as a result of P/M processing.
Effect of Nitrite Inhibitor on the Macrocell Corrosion Behavior of Reinforcing Steel

Directory of Open Access Journals (Sweden)

Zhonglu Cao

2015-01-01

Full Text Available The effect of nitrite ions on the macrocell corrosion behavior of reinforcing steel embedded in cement mortar was investigated by comparing and analyzing the macrocell corrosion current, macrocell polarization ratios, and slopes of anodic and cathodic steels. Based on the experimental results, the relationship between macrocell potential difference and macrocell current density was analyzed, and the mechanism of macrocell corrosion affected by nitrite ions was proposed. The results indicated that nitrite ions had significant impact on the macrocell polarization ratios of cathode and anode. The presence of nitrite could reduce the macrocell current by decreasing the macrocell potential difference and increasing the macrocell polarization resistance of the anode.
Effects of laser shock peening on stress corrosion behavior of 7075 aluminum alloy laser welded joints

Energy Technology Data Exchange (ETDEWEB)

Wang, J.T., E-mail: jiasqq1225@126.com [School of Mechanical Engineering, Jiangsu University, Zhenjiang 212013 (China); School of Materials Engineering, Jiangsu University of Technology, Changzhou 213001 (China); Zhang, Y.K. [School of Mechanical Engineering, Jiangsu University, Zhenjiang 212013 (China); School of Mechanical Engineering, Southeast University, Nanjing 211189 (China); Chen, J.F.; Zhou, J.Y.; Ge, M.Z.; Lu, Y.L.; Li, X.L. [School of Materials Engineering, Jiangsu University of Technology, Changzhou 213001 (China)

2015-10-28

7075 aluminum alloy weldments were processed by an intensive process known as laser shock peening (LSP), meanwhile its stress corrosion behaviors were observed by scanning electron microscopy (SEM) and slow strain rate tensile (SSRT) tests. Results showed that the effect of LSP on corrosion behavior of the joint was fairly useful and obvious. With LSP, the elongation, time of fracture and static toughness after the SSRT test were improved by 11.13%, 20% and 100%, respectively. At the same time, the location of the fracture also changed. LSP led to a transition of the fracture type from transgranular to intergranular The reasons for these enhancements of the joint on corrosion behavior were caused by microstructure, residual stress, micro-hardness, and fracture appearance.
Corrosion behavior of Al6061 alloy weldment produced by friction stir welding process

Directory of Open Access Journals (Sweden)

Farhad Gharavi

2015-07-01

Full Text Available In this work, the corrosion behavior of welded lap joints of AA6061-T6 aluminum alloy produced by friction stir welding process has been investigated. Corrosion properties of welded lap joints were studied by cyclic polarization and electrochemical impedance spectroscopy tests. All tests were performed in an aerated 0.6 mol L−1 NaCl aqueous solution with pH = 6.5 at a temperature of 30 °C to characterize corrosion morphology and realize corrosion features of weld regions as opposed to the parent alloy. The microstructure of weld nugget (WN, heated affected zone (HAZ, and parent alloy were analyzed using scanning electron microscopy and energy dispersive spectroscopy. The experimental results indicated that the welding process has a major effect on the corrosion resistance, which possibly associated to the break-down and dissolution of intermetallic particles. It is supposed that an increasing in intermetallic distributed throughout the matrix of weld regions increases the galvanic corrosion couples. Furthermore, by decreasing the grain size in the weld regions, the susceptibility to corrosion is enhanced. The pitting corrosion and intergranular attack are the dominant corrosion types in the weld regions and the parent alloy.
Corrosion Behavior of Three Nanoclay Dispersion Methods of Epoxy/Organoclay Nanocomposites

Directory of Open Access Journals (Sweden)

Wiwat Keyoonwong

2012-01-01

Full Text Available The aims of this study, firstly, to obtain high degree of clay exfoliation in the epoxy matrix by three dispersion methods such as normal mixing, shear mixing, and high-speed mixing and, secondly, to investigate corrosion behavior of epoxy/organoclay nanocomposite, immersion test, weight change, and penetration behavior were conducted. From the three mixing methods, the high-speed mixing method showed larger clay interlayer distance, smaller clay aggregate, and more homogeneity and expectedly resulted in high anticorrosive properties. Penetration depths of these nanocomposites showed a small difference; however, the most noticeable improvements in anticorrosion performance for epoxy/organoclay nanocomposites under high-speed mixing method were found to reduce penetration and weight uptake which are described via the model of nanoparticulate-filled structure and discussed in corrosion protection mechanism against environmental liquid penetration.
Fretting Corrosion Behavior of Experimental Ti-20Cr Compared to Titanium.

Science.gov (United States)

Sawada, Tomofumi; Schille, Christine; Almadani, Atif; Geis-Gerstorfer, Jürgen

2017-02-17

Experimental cast titanium alloys containing 20 mass% chromium (Ti-20Cr) show preferable mechanical properties and a good corrosion resistance. This study evaluated the fretting corrosion behavior of Ti-20Cr. Ti-20Cr ( n = 4) and commercially pure titanium (CP-Ti, n = 6) disk specimens were used. The fretting corrosion test was performed by electrochemical corrosion at 0.3 V in 0.9% saline solution and mechanical damage using 10 scratching cycles with three different scratching speeds (10-40 mm/s) at 10 N. After testing, the activation peak, repassivation time and surface morphology of each specimen were analyzed. The differences between the results were tested by parametric tests (α = 0.05). The average activation peaks were significantly higher in CP-Ti than in Ti-20Cr ( p Ti. Slight differences in the repassivation time were observed between the materials at every scratching speed; faster scratching speeds showed shorter repassivation times in both materials ( p Ti showed severe damage and significantly higher wear depth than Ti-20Cr ( p < 0.05). In conclusion, adding chromium to titanium reduced surface damage and improved the fretting corrosion resistance.
Effect of Aging Temperature on Corrosion Behavior of Sintered 17-4 PH Stainless Steel in Dilute Sulfuric Acid Solution

Science.gov (United States)

Szewczyk-Nykiel, Aneta; Kazior, Jan

2017-07-01

The general corrosion behavior of sintered 17-4 PH stainless steel processed under different processing conditions in dilute sulfuric acid solution at 25 °C was studied by open-circuit potential measurement and potentiodynamic polarization technique. The corrosion resistance was evaluated based on electrochemical parameters, such as polarization resistance, corrosion potential, corrosion current density as well as corrosion rate. The results showed that the precipitation-hardening treatment could significantly improve the corrosion resistance of the sintered 17-4 PH stainless steel in studied environment. As far as the influence of aging temperature on corrosion behavior of the sintered 17-4 PH stainless steel is concerned, polarization resistance and corrosion rate are reduced with increasing aging temperature from 480 up to 500 °C regardless of the temperature of solution treatment. It can be concluded that the highest corrosion resistance in 0.5 M H2SO4 solution exhibits 17-4 PH after solution treatment at 1040 °C followed by aging at 480 °C.
Corrosion Behavior of Heat-Treated AlSi10Mg Manufactured by Laser Powder Bed Fusion

Directory of Open Access Journals (Sweden)

Marina Cabrini

2018-06-01

Full Text Available This experimental work is aimed at studying the effect of microstructural modifications induced by post-processing heat treatments on the corrosion behavior of silicon-aluminum alloys produced by means of laser powder bed fusion (LPBF. The manufacturing technique leads to microstructures characterized by the presence of melt pools, which are quite different compared to casting alloys. In this study, the behavior of an AlSi10Mg alloy was evaluated by means of intergranular corrosion tests according to ISO 11846 standard on heat-treated samples ranging from 200 to 500 °C as well as on untreated samples. We found that temperatures above 200 °C reduced microhardness of the alloy, and different corrosion morphologies occurred due to the modification of both size and distribution of silicon precipitates. Selective penetrating attacks occurred at melt pool borders. The intergranular corrosion phenomena were less intense for as-produced specimens without heat treatments compared to the heat-treated specimens at 200 and 300 °C. General corrosion morphologies were noticed for specimens heat treated at temperatures exceeding 400 °C.
Influence of heat treatment on the machinability and corrosion behavior of AZ91 Mg alloy

Directory of Open Access Journals (Sweden)

Swetha Chowdary V

2018-03-01

Full Text Available In the present study, AZ91 Mg alloy was heat treated at 410 °C for 6, 12 and 24 h to investigate the influence of heat treatment on machinability and corrosion behavior. The effect of soaking time on the amount and distribution of Mg17Al12 (β – phase was analyzed under the optical microscope. Microhardness measurements demonstrated the increased hardness with increased heat treatment soaking time, which can be attributed to the solid solution strengthening. The influence of super saturated α-grains on reducing the cutting force (Fz with respect to increased cutting speed was observed as prominent. The corrosion behavior of the heat treated specimens was studied by conducting electrochemical tests. Surprisingly, corrosion rate of heat treated samples was observed as increased compared with the base material. From the results, it is evident that the machinability of AZ91 Mg alloy can be improved by producing super saturated α-grains through heat treatment but at the cost of losing corrosion resistance. Keywords: AZ91 Mg alloy, Solid solution, Turning, Corrosion, Machinability
Electrochemical Corrosion Behavior of Low Carbon I-Beam Steels In Simulated Yucca Mountain Repository Environment

Energy Technology Data Exchange (ETDEWEB)

Arjunan, Venugopal; Lamb, Joshua; Chandra, Dhanesh; Daemen, Jack; Jones, Denny A.; Engelhard, Mark H.; Lea, Alan S.

2005-04-01

The electrochemical corrosion behavior of low carbon steel was examined in a simulated Yucca Mountain (YM) ground water by varying the electrolyte concentration and temperature under aerated and deaerated conditions. The results show that in deaerated conditions, the corrosion rate is low in the order of 0.6 to 4.5mpy, between 25 to 85 C, respectively. However, in aerated conditions the measured rates were expectedly very high, in the order of 3-55mpy in the above mentioned temperature levels. The rates initially increased up to 45 C, and a decreasing trend was observed with further increase in temperature from 65 to 85 C. The maximum corrosion rate was occurred at 45 C (54.5mpy). The low corrosion rates observed in all deaerated conditions, and in aerated solutions at higher temperatures were due to the preferential adsorption of Mg-species on the steel surface, as identified by XPS analyses. The results also indicate possible localized corrosion behavior of carbon steel in aerated conditions up to 45 C.
Electrochemical Corrosion Behavior of Low Carbon I-Beam Steels In Simulated Yucca Mountain Repository Environment

International Nuclear Information System (INIS)

Arjunan, Venugopal; Lamb, Joshua; Chandra, Dhanesh; Daemen, Jack; Jones, Denny A.; Engelhard, Mark H.; Lea, Alan S.

2005-01-01

The electrochemical corrosion behavior of low carbon steel was examined in a simulated Yucca Mountain (YM) ground water by varying the electrolyte concentration and temperature under aerated and deaerated conditions. The results show that in deaerated conditions, the corrosion rate is low in the order of 0.6 to 4.5mpy, between 25 to 85 C, respectively. However, in aerated conditions the measured rates were expectedly very high, in the order of 3-55mpy in the above mentioned temperature levels. The rates initially increased up to 45 C, and a decreasing trend was observed with further increase in temperature from 65 to 85 C. The maximum corrosion rate was occurred at 45 C (54.5mpy). The low corrosion rates observed in all deaerated conditions, and in aerated solutions at higher temperatures were due to the preferential adsorption of Mg-species on the steel surface, as identified by XPS analyses. The results also indicate possible localized corrosion behavior of carbon steel in aerated conditions up to 45 C
Influence of chloride ion concentration on the corrosion behavior of Al-bearing TRIP steels

Energy Technology Data Exchange (ETDEWEB)

El-Taib Heakal, F., E-mail: fakihaheakal@yahoo.com [Chemistry Department, Faculty of Science, Cairo University, Giza 12613 (Egypt); Tantawy, N.S. [Chemistry Department, Girl' s College for Arts, Science and Education, Ain Shams University, Cairo (Egypt); Shehta, O.S. [Physical Chemistry Department, National Research Centre, Dokki, Giza (Egypt)

2011-10-17

Highlights: {yields} Systematic increase of chloride concentration has a critical influence on TRIP steel corrosion. {yields} TRIP microalloyed with Nb and Cr showed lower corrosion rate and smaller threshold Cl{sup -} value. {yields} Increasing Al content by 220 times in the TRIP deteriorates its corrosion behavior. {yields} Impedance results and surface examinations confirmed the obtained results. - Abstract: The effect of a systematic increase of chloride ion concentration on the electrochemical corrosion behavior of two types of Al-bearing TRIP steels (T{sub 1} and T{sub 2}) was studied in aqueous NaCl solutions. Several electrochemical techniques were used comprising open circuit potential measurements, potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS). Chloride concentration has a critical influence on the corrosion rate of the two tested steel samples. For both steels the corrosion rate first increased with increasing chloride content up to a certain critical concentration (CC), and then decreased in solution with chloride level higher than the threshold value. TRIP steel T{sub 1} microalloyed with Nb and Cr as compared to steel T{sub 2} not containing these two elements, exhibited lower corrosion rate and smaller CC value, indicating better corrosion resistance to chloride attack, albeit the Al content in T{sub 2} is 220 times higher than that in T{sub 1}. This is because Nb alloyed with TRIP steel likely enhances the formation on the surface of a stable rust layer enriched with other passivating elements Al, Cu, Cr and Ni, which has higher corrosion resistance and hence improve greatly the passive performance of the TRIP sample. The ac impedance data are in good agreement with the OCP and dc polarization measurements. Surface examinations via scanning electron microscope confirmed well the obtained results.
Influence of chloride ion concentration on the corrosion behavior of Al-bearing TRIP steels

International Nuclear Information System (INIS)

El-Taib Heakal, F.; Tantawy, N.S.; Shehta, O.S.

2011-01-01

Highlights: → Systematic increase of chloride concentration has a critical influence on TRIP steel corrosion. → TRIP microalloyed with Nb and Cr showed lower corrosion rate and smaller threshold Cl - value. → Increasing Al content by 220 times in the TRIP deteriorates its corrosion behavior. → Impedance results and surface examinations confirmed the obtained results. - Abstract: The effect of a systematic increase of chloride ion concentration on the electrochemical corrosion behavior of two types of Al-bearing TRIP steels (T 1 and T 2 ) was studied in aqueous NaCl solutions. Several electrochemical techniques were used comprising open circuit potential measurements, potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS). Chloride concentration has a critical influence on the corrosion rate of the two tested steel samples. For both steels the corrosion rate first increased with increasing chloride content up to a certain critical concentration (CC), and then decreased in solution with chloride level higher than the threshold value. TRIP steel T 1 microalloyed with Nb and Cr as compared to steel T 2 not containing these two elements, exhibited lower corrosion rate and smaller CC value, indicating better corrosion resistance to chloride attack, albeit the Al content in T 2 is 220 times higher than that in T 1 . This is because Nb alloyed with TRIP steel likely enhances the formation on the surface of a stable rust layer enriched with other passivating elements Al, Cu, Cr and Ni, which has higher corrosion resistance and hence improve greatly the passive performance of the TRIP sample. The ac impedance data are in good agreement with the OCP and dc polarization measurements. Surface examinations via scanning electron microscope confirmed well the obtained results.
Corrosion of high temperature alloys in the primary circuit helium of high temperature gas cooled reactors. Pt. 2

International Nuclear Information System (INIS)

Quadakkers, W.J.

1985-01-01

The reactive impurities H 2 O, CO, H 2 and CH 4 which are present in the primary coolant helium of high temperature gas-cooled reactors can cause scale formation, internal oxidation and carburization or decarburization of the high temperature structural alloys. In Part 1 of this contribution a theoretical model was presented, which allows the explanation and prediction of the observed corrosion effects. The model is based on a classical stability diagram for chromium, modified to account for deviations from equilibrium conditions caused by kinetic factors. In this paper it is shown how a stability diagram for a commercial alloy can be constructed and how this can be used to correlate the corrosion results with the main experimental parameters, temperature, gas and alloy composition. Using the theoretical model and the presented experimental results, conditions are derived under which a protective chromia based surface scale will be formed which prevents a rapid transfer of carbon between alloy and gas atmosphere. It is shown that this protective surface oxide can only be formed if the carbon monoxide pressure in the gas exceeds a critical value. Psub(CO), which depends on temperature and alloy composition. Additions of methane only have a limited effect provided that the methane/water ratio is not near to, or greater than, a critical value of around 100/1. The influence of minor alloying additions of strong oxide forming elements, commonly present in high temperature alloys, on the protective properties of the chromia surface scales and the kinetics of carbon transfer is illustrated. (orig.) [de
Corrosion behavior of CLAM steel weldment in flowing liquid Pb-17Li at 480 °C

International Nuclear Information System (INIS)

Chen Xizhang; Shen Zheng; Chen Xing; Lei Yucheng; Huang Qunying

2011-01-01

Highlights: ► The research shows that the CLAM steel weldment have its own corrosion mechanism in liquid Pb-17Li alloy. The basic rule of the corrosion behaviour of weldments is that the coorosion rate decreases obviously with the increasing of exposed time. ► The weight loss of CLAM steel weldment is far higer than the base metal after exposed to Pb-17Li alloy. Corrosion has little effects on elements of weldment sample surfaces. And an easier corrosion area in the weld joint are found. ► A simple presumably corrosion behavior model is established. The model demonstrate that the easier corroded area will be formed when the direction of martensite laths form small-angle with the specimen surface, The easy corrosion area is the martensite lath area lack of Cr and distributes like laths, the cross-section area is 1 μm 2 to 4 μm 2, the existence of the easier corrosion area is one of the reasons that lead to the difference of the corrosion rate. - Abstract: CLAM (China Low Activation Martensitic) steel is considered as one of the candidate structural materials in liquid LiPb blanket concepts. Welding is one of the essential technologies for its practical application, CLAM steel weldment shows a great difference with base metal due to the effect of welding thermal cycle. In order to investigate the corrosion behavior and mechanism of CLAM weldments in liquid Pb-17Li, the experiments were performed by exposing the TIG weldment samples in flowing LiPb at 480 °C. The weight loss test of exposed specimens show that in 500 h, 1000 h dynamic conditions, corrosion resistance of CLAM steel weldment is poor, SEM analysis shows that the thicker martensite lath in weld area lead to higher corrosion amount, EDS results show that the influence of corrosion on surface elements is small, and surface corrosion is even, EDX analysis shows that the penetration of Pb-17Li does not exist in the joint. With the increasing of exposure time, the corrosion rate decreases
Corrosion behavior of materials selected for FMIT lithium system

International Nuclear Information System (INIS)

Bazinet, G.D.; Down, M.G.; Matlock, D.K.

1983-01-01

The corrosion program consisted of a multi-disciplinary approach utilizing the liquid lithium test resources and capabilities of several laboratories. Specific concerns associated with the overall objective of materials corrosion behavior were evaluated at each laboratory. Testing conditions included: approx. 3700 hours of exposure to flowing lithium at temperatures from 230 0 C to 270 0 C and approx. 6500 hours of exposure to flowing lithium at an isothermal temperature of 270 0 C. Principal areas of investigation, to be discussed here briefly, included lithium corrosion effects on the following: (1) types 304 and 304L austenitic stainless steels, which are specified as reference materials for the FMIT lithium system; (2) type 304 stainless steel weldments (w/type 308 stainless steel filler) typical of specified tube and butt welds in the lithium system design; (3) titanium, zirconium and yttrium, which represent potential hot trap getter materials; (4) BNi4 braze alloy, used as a potential attachement method in the plug/seat fabrication of liquid lithium valves; and (5) type 321 stainless steel bellows, typical of bellows used in potential liquid lithium valve designs
Effects of Friction Stir Welding on Corrosion Behaviors of AA2024-T4 Aluminum Alloy

Directory of Open Access Journals (Sweden)

Ales Steve Korakan

2017-01-01

Full Text Available In this work, the corrosion behavior of welded joints of AA2024-T4 Al alloy produced by friction stir welding process has been investigated. Tests were performed in an aerated 3.5% NaCl aqueous solution with pH = 7 at 20±2°C. Corrosion rate and corrosion morphology of weld regions were evaluated and compared to those of the parent metal. The microstructure of weld nugget, thermomechanical affected zone, heated affected zone, and parent metal were analyzed using scanning electron microscopy and energy dispersive spectroscopy. It was observed that corrosion initiated at FSW related spots and the sizes of local corrosion increased with time.

Effects of external stresses on hot corrosion behavior of stainless steel TP347HFG

International Nuclear Information System (INIS)

Fu, Jiapeng; Zhou, Qulan; Li, Na; Liu, Zhuhan; Liu, Taisheng

2016-01-01

Highlights: • Hot corrosion tests of TP347HFG under different stresses were conducted. • The corrosion resistance was strengthened by the exertion of tensile stresses. • External stresses promoted faster formation of the protective Cr_2O_3 layer. • Specimens under critical stress 40 MPa condition present the best resistance. - Abstract: Hot corrosion experiments of alloy TP347HFG under different stresses were conducted. Corroded specimens were examined by means of corrosion products, morphology and compositional changes in corrosion scales. The corrosion behavior was strongly associated with the formation of oxides layers. The corrosion resistance was strengthened by the external stress. It seemed that the exertion of stresses caused many micro cracks and defects, which acted as faster and easier diffusion paths for Cr atoms to diffuse to the surface, and thus, promote faster formation of the protective Cr_2O_3 oxide layer. Critical stress 40 MPa was found, specimens under which present the best resistance.
Corrosion behavior of low energy, high temperature nitrogen ion ...

Indian Academy of Sciences (India)

Corrosion behavior of low energy, high temperature nitrogen ion-implanted AISI 304 stainless steel. M GHORANNEVISS1, A SHOKOUHY1,∗, M M LARIJANI1,2,. S H HAJI HOSSEINI 1, M YARI1, A ANVARI4, M GHOLIPUR SHAHRAKI1,3,. A H SARI1 and M R HANTEHZADEH1. 1Plasma Physics Research Center, Science ...
Influence of the casting processing route on the corrosion behavior of dental alloys.

Science.gov (United States)

Galo, Rodrigo; Rocha, Luis Augusto; Faria, Adriana Claudia; Silveira, Renata Rodrigues; Ribeiro, Ricardo Faria; de Mattos, Maria da Gloria Chiarello

2014-12-01

Casting in the presence of oxygen may result in an improvement of the corrosion performance of most alloys. However, the effect of corrosion on the casting without oxygen for dental materials remains unknown. The aim of this study was to investigate the influence of the casting technique and atmosphere (argon or oxygen) on the corrosion behavior response of six different dental casting alloys. The corrosion behavior was evaluated by electrochemical measurements performed in artificial saliva for the different alloys cast in two different conditions: arc melting in argon and oxygen-gas flame centrifugal casting. A slight decrease in open-circuit potential for most alloys was observed during immersion, meaning that the corrosion tendency of the materials increases due to the contact with the solution. Exceptions were the Co-based alloys prepared by plasma, and the Co-Cr-Mo and Ni-Cr-4Ti alloys processed by oxidized flame, in which an increase in potential was observed. The amount of metallic ions released into the artificial saliva solution during immersion was similar for all specimens. Considering the pitting potential, a parameter of high importance when considering the fluctuating conditions of the oral environment, Co-based alloys show the best performance in comparison with the Ni-based alloys, independent of the processing route. Copyright © 2014 Elsevier B.V. All rights reserved.
Investigation of electrochemical corrosion behavior in a 3.5 wt.% NaCl solution of boronized dual-phase steel

International Nuclear Information System (INIS)

Kayali, Yusuf; Anaturk, Bilal

2013-01-01

Highlights: ► Corrosion behaviors in a 3.5% NaCl solution of boronized Dual-Phase (DP) steels were examined. ► The martensite ratio increased with an increase in the intercritical annealing temperature. ► The corrosion resistance decreased with increase of the martensite ratio. ► The boride layer increased the corrosion resistance of DP steel 2–3-fold. ► The superior properties of DP steel as well as poor corrosion properties were improved by the boriding process. - Abstract: In this study, corrosion behaviors of boronized and non-boronized dual-phase steel were investigated with Tafel extrapolation and linear polarization methods in a 3.5 wt.% NaCl solution. Microstructure analyses show that the boride layer on the dual-phase steel surface had a flat and saw smooth morphology. It was detected by X-ray diffraction (XRD) analysis that the boride layer contained FeB and Fe 2 B phases. The amount of martensite increases with an increase in the intercritical annealing temperature. Both the amount of martensite and the morphology of the phase constituents have an influence on the corrosion behavior of dual-phase steel. A higher corrosion tendency was observed with an increased amount of martensite. The corrosion resistance of boronized dual-phase steel is higher compared with that of dual-phase steel
Electrochemical and corrosion behavior of a 304 stainless-steel-based metal alloy wasteform in dilute aqueous environments

International Nuclear Information System (INIS)

Chen, Jian; Asmussen, R. Matthew; Zagidulin, Dmitrij; Noël, James J.; Shoesmith, David W.

2013-01-01

Highlights: ► We investigated the corrosion behavior of a metal alloy in six reference solutions. ► Majority of rhenium used as a technetium surrogate contained within a Fe 2 Mo phase. ► This prototype alloy exhibited generally passive behavior in all environments. ► Passivity breakdown events can occur and lead to localized corrosion. - Abstract: The electrochemical and corrosion behavior of a stainless-steel-based alloy made as a prototype metallic nuclear wasteform to immobilize 99 Tc, has been studied in a number of reference solutions ranging in pH from 4 to 10. The results showed the 47SS(304)-9Zr–23Mo prototype alloy contained at least five distinct phases with the majority of the Re, used as a Tc surrogate, contained within a Fe 2 Mo intermetallic phase. Polarization studies showed this alloy exhibited generally passive behavior in a range of dilute aqueous environments. Impedance measurements indicated passivity breakdown events can occur and lead to localized corrosion, especially in slightly alkaline conditions.
THE CORROSION BEHAVIOR AND WEAR RESISTANCE OF GRAY CAST IRON

Directory of Open Access Journals (Sweden)

Lina F. Kadhim

2018-01-01

Full Text Available Gray cast iron has many applications as pipes , pumps and valve bodies where it has influenced by heat and contact with other solutions . This research has studied the corrosion behavior and Vickers hardness of gray cast iron by immersion in four strong alkaline solutions (NaOH, KOH, Ca(OH2, LiOHwith three concentrations (1%,2%,3% of each solution. Dry sliding wear has carried out before and after the heat treatments (stress relief ,normalizing, hardening and tempering. In this work ,maximum wear strength has obtained at tempered gray cast iron and minimum corrosion rate has obtained in LiOH solution by forming protective white visible oxide layer.
Corrosion and oxidation of vanadium-base alloys

International Nuclear Information System (INIS)

Loomis, B.A.; Wiggins, G.

1983-10-01

The corrosion of several V-base alloys on exposure at elevated temperatures to helium environments containing hydrogen and/or water vapor are presented. These results are utilized to discuss the consequences of the selection of certain radiation-damage resistant, V-base alloys for structural materials applications in a fusion reactor
Corrosion Behavior of Superalloys in Hot Lithium Molten Salt

International Nuclear Information System (INIS)

Cho, Soo-Haeng; Hur, Jin-Mok; Seo, Chung-Seok; Park, Seoung-Won

2006-01-01

The Li-reduction process involves the chemical reduction of spent fuel oxides by liquid lithium metal in a molten LiCl salt bath at 650 .deg. C followed by a separate electrochemical reduction of lithium oxide (Li 2 O), which builds up in the salt bath. This process requires a high purity inert gas atmosphere inside remote hot cell nuclear facility to prevent unwanted Li oxidation and fires during the handling of chemically active Li metal. In light of the limitations of the Li-reduction process, a direct electrolytic reduction technology is being developed by KAERI to enhance process safety and economic viability. The electrolytic reduction of spent oxide fuel involves the liberation of oxygen in a molten LiCl electrolyte, which results in a chemically aggressive environment that is too corrosive for typical structural materials. Even so, the electrochemical process vessel must be resilient at ∼ 650 .deg. C in the presence of oxygen to enable high processing rates and an extended service life. But, the mechanism and the rate of the corrosion of metals in LiCl-Li 2 O molten salt under oxidation condition are not clear. In the present work, the corrosion behavior and corrosion mechanism of superalloys have been studied in the molten salt of LiCl-Li 2 O under oxidation condition
Microstructure, Corrosion and Magnetic Behavior of an Aged Dual-Phase Stainless Steel

Science.gov (United States)

Ziouche, A.; Haddad, A.; Badji, R.; Zergoug, M.; Zoubiri, N.; Bedjaoui, W.; Abaidia, S.

2018-03-01

In the present work, the effect of the precipitation phenomena on corrosion and magnetic behavior of an aged dual-phase stainless steel was investigated. Aging treatment caused the precipitation of the σ phase, chromium carbides and secondary austenite, which was accompanied by the shifting of the δ/γ interfaces inside the δ ferrite grains. Aging between 700 and 850 °C strongly deteriorated the pitting corrosion resistance of the studied material. Magnetic investigation of the aged material using the vibration sample magnetic technique revealed the sensitivity of the intrinsic magnetic properties to the smallest microstructural change. This was confirmed by the Eddy current technique that led also to the evaluation of the aging-induced localized corrosion.
Electrochemical behavior of tube-fin assembly for an aluminum automotive condenser with improved corrosion resistance

Directory of Open Access Journals (Sweden)

M.A. Pech-Canul

Full Text Available An aluminum automotive condenser was designed to exhibit high corrosion resistance in the seawater acetic acid test (SWAAT combining zinc coated microchannel tubes and fins made with AA4343/AA3003(Zn/AA4343 brazing sheet. Electrochemical measurements in SWAAT solution were carried out under laboratory conditions using tube-fin assembly and individual fin and tube samples withdrawn from the condenser core. The aim was to gain information on the protective role of the zinc sacrificial layer and about changes in corrosion behavior as a function of immersion time. External corrosion of the tube-fin system was simulated by immersion of mini-core samples under open circuit conditions. The corrosion rate increased rapidly during the first 6 h and slowly afterwards. The short time behavior was related to the dissolution of the oxide film and fast dissolution of the outermost part of the zinc diffusion layer. With the aid of cross-sectional depth corrosion potential profiles, it was shown that as the sacrificial layer gets dissolved, the surface concentration of zinc decreases and the potential shifts to less negative values. The results of galvanic coupling of tube and fins in a mini-cell showed that the tube became the anode while the fins exhibited cathodic behavior. An evolution in the galvanic interaction was observed, due to the progressive dissolution of the sacrificial zinc layer. The difference of uncoupled potentials between tube and fins decreased from 71 mV to 32 mV after 84 h of galvanic coupling. At the end of such period there was still a part of the zinc sacrificial layer remaining which would serve for protection of the tube material for even longer periods and there were indications of slight corrosion in the fins. Keywords: Aluminum, Automotive, Corrosion, Galvanic, Zn coating
Effect of Plastic Deformation on the Corrosion Behavior of a Super-Duplex Stainless Steel

Science.gov (United States)

Renton, Neill C.; Elhoud, Abdu M.; Deans, William F.

2011-04-01

The role of plastic deformation on the corrosion behavior of a 25Cr-7Ni super-duplex stainless steel (SDSS) in a 3.5 wt.% sodium chloride solution at 90 °C was investigated. Different levels of plastic strain between 4 and 16% were applied to solution annealed tensile specimens and the effect on the pitting potential measured using potentiodynamic electrochemical techniques. A nonlinear relationship between the pitting potential and the plastic strain was recorded, with 8 and 16% causing a significant reduction in average E p, but 4 and 12% causing no significant change when compared with the solution-annealed specimens. The corrosion morphology revealed galvanic interaction between the anodic ferrite and the cathodic austenite causing preferential dissolution of the ferrite. Mixed potential theory and the changing surface areas of the two phases caused by the plastic deformation structures explain the reductions in pitting potential at certain critical plastic strain levels. End-users and manufacturers should evaluate the corrosion behavior of specific cold-worked duplex and SDSSs using their as-produced surface finishes assessing in-service corrosion performance.
The effect of brazing parameters on corrosion behavior of brazed aluminum joints

Science.gov (United States)

Ghasimakbari, Farzam; Hadian, Ali Mohammad; Ershadrad, Soheil; Omidazad, Amir Mansour

2018-01-01

Fluid transmission pipes made of aluminum are widely used in petrochemical industries. For many applications, they have to be brazed to each other. The brazed joints, in many cases, are encountered with corrosive medias. This paper reports a part of a work to investigate the corrosion behavior of brazed AA6061 using AA4047 as filler metal with and without the use of flux under different brazing atmospheres. The samples brazed under air, vacuum, argon, and hydrogen atmospheres. The interfacial area of the joints was examined to ensure being free of any defects. The sides of each test piece were covered with an insulator and the surface of the joint was encountered to polarization test. The results revealed a significant difference of corrosion resistance. The samples that brazed under argon and hydrogen atmospheres had better corrosion resistance than other samples. The microstructure of the corroded joints revealed that the presence of defects, impurities due to use of flux and depth of filter metal penetration in base metal are crucial variables on the corrosion resistance of the joints.
Microstructure and Corrosion Behavior of Laser Synthesized Cobalt Based Powder on Ti-6Al-4V

Science.gov (United States)

Adesina, O. S.; Popoola, A. P. I.; Pityana, S. L.; Oloruntoba, D. T.

2018-05-01

The corrosion behavior of titanium alloys when used for various dynamic offshore components has been a major concern of titanium drilling risers in deepwater energy extraction. A way of achieving specified requirement is the development of coatings suitable to protect the base material against corrosion. In this work, laser cladding technique which is known as a leading edge due to its distinctive properties and outcomes was used in synthesizing Co-based powder on titanium alloy. The processing parameters used were laser power of 900W; scan speed of 0.6 to 1.2 m/min; powderfeedrate1.0g/min;beamspotsize3mm;gasflowrate1.2L/min.The effects of cobalt addition and laser parameters on corrosion behavior of laser clad Ti6AL4V coating in 0.5M sulfuric medium were investigated using linear potentiodynamic polarization. The changes in microstructure and corrosion behavior were analyzed using scanning electron microscopy (SEM) while the X –ray diffraction (XRD) indicates the intermetallics in the coatings. Results showed that the coatings displayed good metallurgical bonding with dendritic formations between the coatings and the substrate. The anodic current density increased with lower scan speed. However, the corrosion current densities of laser-clad samples were lower than Ti6Al4V alloy.
Effect of Cu addition on microstructure and corrosion behavior of spray-deposited Zn–30Al alloy

International Nuclear Information System (INIS)

Wang Feng; Xiong Baiqing; Zhang Yongan; Liu Hongwei; Li Zhihui; Li Xiwu; Qu Chu

2012-01-01

Highlights: ► Zn–30Al–xCu alloys were synthesized by the spray atomization and deposition technique. ► Immersion test and electrochemical measurements have been used to estimate the corrosion rate and the behavior. ► The result indicates that the 1 wt.% Cu addition displays superior corrosion resistance. - Abstract: In this study, one binary Zn–30Al and three ternary Zn–30Al–Cu alloys were synthesized by the spray atomization and deposition technique. The microstructures of the spray-deposited alloys were investigated by means of scanning electron microscope (SEM), transmission electron microscope (TEM), X-ray diffraction (XRD). Immersion test, potentiodynamic polarization and electrochemical impedance measurements have been used to estimate the corrosion rate and the behavior. The results indicate that the 1 wt.% Cu addition to spray-deposited Zn–30Al alloy does not make significant change in microstructure. However, with the 2, 4 wt.% Cu additions to the alloy, some ε-CuZn 4 compounds with particle or irregular shapes were observed on the grain boundaries in the microstructures. Immersion test and electrochemical measurements confirmed that the 1 wt.% Cu addition displays superior corrosion resistance, whereas the 2, 4 wt.% Cu additions have a baneful effect on the corrosion behavior.
Corrosion behavior of boride layers evaluated by the EIS technique

Energy Technology Data Exchange (ETDEWEB)

Campos, I. [Instituto Politecnico Nacional. SEPI-ESIME U.P. Adolfo Lopez Mateos, Zacatenco, Mexico D.F. 07738 (Mexico)], E-mail: icampos@ipn.mx; Palomar-Pardave, M. [Universidad Autonoma Metropolitana-Azcapotzalco, Materials Department, Avenue San Pablo 180 Col. Reynosa Tamaulipas, Mexico D.F. 02200 (Mexico); Amador, A. [Tecnologico de Monterrey, Campus Ciudad de Mexico, Calle del Puente 222 Col. Ejidos de Huipulco, Mexico D.F. 14380 (Mexico); VillaVelazquez, C. [Instituto Politecnico Nacional. SEPI-ESIME U.P. Adolfo Lopez Mateos, Zacatenco, Mexico D.F. 07738 (Mexico); Hadad, J. [Tecnologico de Monterrey, Campus Ciudad de Mexico, Calle del Puente 222 Col. Ejidos de Huipulco, Mexico D.F. 14380 (Mexico)

2007-09-30

The corrosion behavior of boride layers at the AISI 304 steel surface is evaluated in the present study. Electrochemical impedance spectroscopy (EIS) technique was used for the evaluation of the polarization resistance at the steel surface, with the aid of AUTOLAB potentiostat. Samples were treated with boron paste thickness of 4 and 5 mm, in the range of temperatures 1123 {<=} T {<=} 1273 K and exposed time of 4 and 6 h. The electrochemical technique employed 10 mV AC with a frequency scan range from 8 kHz to 3 mHz in deaerated 0.1 M NaCl solution. Nyquist diagrams show that the highest values of corrosion resistance are present in the samples borided at the temperature of 1273 K, with treatment time of 4 h and 4 mm of boron paste thickness. The values of corrosion resistance on borided steels are compared with the porosity exhibited in the layers.
Potentiodynamic polarization study of the corrosion behavior of palladium-silver dental alloys.

Science.gov (United States)

Sun, Desheng; Brantley, William A; Frankel, Gerald S; Heshmati, Reza H; Johnston, William M

2018-04-01

Although palladium-silver alloys have been marketed for over 3 decades for metal-ceramic restorations, understanding of the corrosion behavior of current alloys is incomplete; this understanding is critical for evaluating biocompatibility and clinical performance. The purpose of this in vitro study was to characterize the corrosion behavior of 3 representative Pd-Ag alloys in simulated body fluid and oral environments and to compare them with a high-noble Au-Pd alloy. The study obtained values of important electrochemical corrosion parameters, with clinical relevance, for the rational selection of casting alloys. The room temperature in vitro corrosion characteristics of the 3 Pd-Ag alloys and the high-noble Au-Pd alloy were evaluated in 0.9% NaCl, 0.09% NaCl, and Fusayama solutions. After simulated porcelain firing heat treatment, 5 specimens of each alloy were immersed in the electrolytes for 24 hours. For each specimen, the open-circuit potential (OCP) was first recorded, and linear polarization was then performed from -20 mV to +20 mV (versus OCP) at a rate of 0.125 mV/s. Cyclic polarization was subsequently performed on 3 specimens of each alloy from -300 mV to +1000 mV and back to -300 mV (versus OCP) at a scanning rate of 1 mV/s. The differences in OCP and corrosion resistance parameters (zero-current potential and polarization resistance) among alloys and electrolyte combinations were compared with the 2-factor ANOVA (maximum-likelihood method) with post hoc Tukey adjustments (α=.05). The 24-hour OCPs and polarization resistance values of the 3 Pd-Ag alloys and the Au-Pd alloy were not significantly different (P=.233 and P=.211, respectively) for the same electrolyte, but significant differences were found for corrosion test results in different electrolytes (Palloy and electrolyte (P=.249 and P=.713, respectively). The 3 Pd-Ag silver alloys appeared to be resistant to chloride ion corrosion, and passivation and de-alloying were identified for these
Corrosion and passivation behavior of various stainless steels in libr solution used in absorption-type refrigeration system

International Nuclear Information System (INIS)

Shahid, M.

2007-01-01

Various structural materials have been suggested for the refrigeration units to combat high corrosiveness of the absorbent. The corrosion behavior of three grades of austenitic stainless steels, have been investigated in lithium bromide (LiBr) solutions, using electrochemical techniques. Potentiodynamic E- log-i curves, potential-time scans and polarization resistance diagrams obtained by using three-electrode system connected to a computerized Gamry at the rate framework, have been used to analyze their corrosion and passivation behavior in various concentrations of LiBr i.e. commercial LiBr (850 g/J solution containing chromate inhibitor), 400 g/l LiBr and 700 g/J LiBr solutions, at room temperature. Relatively higher corrosion current was observed in SS304 exposed to inhibitor-free electrolyte compared to inhibited commercial solution. Inhibitor proved to be more efficient in case of AISI 304 as it showed significantly higher corrosion rate in un-inhibited solutions. (author)
Effect of hydrogen on the corrosion behavior of the Mg–xZn alloys

Directory of Open Access Journals (Sweden)

Yingwei Song

2014-09-01

Full Text Available Hydrogen evolution reaction is inevitable during the corrosion of Mg alloys. The effect of hydrogen on the corrosion behavior of the Mg–2Zn and Mg–5Zn alloys is investigated by charging hydrogen treatment. The surface morphologies of the samples after charging hydrogen were observed using a scanning electron microscopy (SEM and the corrosion resistance was evaluated by polarization curves. It is found that there are oxide films formed on the surface of the charged hydrogen samples. The low hydrogen evolution rate is helpful to improve the corrosion resistance of Mg alloys, while the high hydrogen evolution rate can increases the defects in the films and further deteriorates their protection ability. Also, the charging hydrogen effect is greatly associated with the microstructure of Mg substrate.
Effect of Secondary Phase Precipitation on the Corrosion Behavior of Duplex Stainless Steels.

Science.gov (United States)

Chan, Kai Wang; Tjong, Sie Chin

2014-07-22

Duplex stainless steels (DSSs) with austenitic and ferritic phases have been increasingly used for many industrial applications due to their good mechanical properties and corrosion resistance in acidic, caustic and marine environments. However, DSSs are susceptible to intergranular, pitting and stress corrosion in corrosive environments due to the formation of secondary phases. Such phases are induced in DSSs during the fabrication, improper heat treatment, welding process and prolonged exposure to high temperatures during their service lives. These include the precipitation of sigma and chi phases at 700-900 °C and spinodal decomposition of ferritic grains into Cr-rich and Cr-poor phases at 350-550 °C, respectively. This article gives the state-of the-art review on the microstructural evolution of secondary phase formation and their effects on the corrosion behavior of DSSs.
Pressurized-helium breakdown at very low temperatures

Energy Technology Data Exchange (ETDEWEB)

Metas, R J

1972-06-01

An investigation of the electrical-breakdown behavior of helium at very low temperatures has been carried out to assist the design and development of superconducting power cables. At very high densities, both liquid and gaseous helium showed an enhancement in electric strength when pressurized to a few atmospheres; conditioned values of breakdown fields then varied between 30 and 45 MV/m. Breakdown processes occurring over a wide range of helium densities are discussed. 24 references.

Grain size effect in corrosion behavior of electrodeposited nanocrystalline Ni coatings in alkaline solution

International Nuclear Information System (INIS)

Wang Liping; Zhang Junyan; Gao Yan; Xue Qunji; Hu Litian; Xu Tao

2006-01-01

Effects of grain size reduction on the electrochemical corrosion behavior of nanocrystalline Ni produced by pulse electrodeposition were characterized using potentiodynamic polarization testing and electrochemical impedance spectroscopy; X-ray photoelectron spectroscopy were used to confirm the electrochemical measurements and the suggested mechanisms. The corrosion resistance of Ni coatings in alkaline solutions considerably increased as the grain size decreased from microcrystalline to nanocrystalline. The higher corrosion resistance of NC Ni may be due to the more rapid formation of continuous Ni(OH) 2 passive films compared with coarse-grained Ni coatings
Influence of processing variables and alloy chemistry on the corrosion behavior of ZIRLO nuclear fuel cladding

International Nuclear Information System (INIS)

Comstock, R.J.; Sabol, G.P.; Schoenberger, G.

1996-01-01

Variations in the thermal heat treatments used during the fabrication of ZIRLO (Zr-1Nb-1Sn-0.1Fe) fuel clad tubing and in ZIRLO alloy chemistry were explored to develop a further understanding of the relationship between processing, microstructure, and cladding corrosion performance. Heat treatment variables included intermediate tube annealing temperatures as well as a beta-phase heat treatment during the latter stages of the tube reduction schedule. Chemistry variables included deviations in niobium and tin content from the nominal composition. The effects of both heat treatment and chemistry on corrosion behavior were assessed by autoclave tests in both pure and lithiated water and high-temperature steam. Analytical electron microscopy demonstrated that the best out-reactor corrosion performance is obtained for microstructures containing a fine distribution of beta-niobium and Zr-Nb-Fe particles. Deviations from this microstructure, such as the presence of beta-zirconium phase, tend to degrade corrosion resistance. ZIRLO fuel cladding was irradiated in four commercial reactors. In all cases, the microstructure in the cladding included beta-niobium and Zr-Nb-Fe particles. ZIRLO fuel cladding processed with a late-stage beta heat treatment to further refine the second-phase particle size exhibited in-reactor corrosion behavior that was similar to reference ZIRLO cladding. Variations of the in-reactor corrosion behavior of ZIRLO were correlated to tin content, with higher oxide thickness observed in the ZIRLO cladding containing higher tin. The results of these studies indicate that optimum corrosion performance of ZIRLO is achieved by maintaining a uniform distribution of fine second-phase particles and controlled levels of tin
Effects of annealing on tensile property and corrosion behavior of Ti-Al-Zr alloy

International Nuclear Information System (INIS)

Kim, Tae-Kyu; Choi, Byung-Seon; Jeong, Yong-Hwan; Lee, Doo-Jeong; Chang, Moon-Hee

2002-01-01

The effects of annealing on the tensile property and corrosion behavior of Ti-Al-Zr alloy were evaluated. The annealing in the temperature range from 500 to 800 deg. C for 1 h induced the growth of the grain and the precipitate sizes. The results of tensile tests at room temperature showed that the strengths and the ductility were almost independent of the annealing temperature. However, the results of corrosion test in an ammonia aqueous solution of pH 9.98 at 360 deg. C showed that the corrosion resistance depended on the annealing temperature, and the corrosion rate was accelerated with increasing annealing temperature. Hydrogen contents absorbed during the corrosion test of 220 days also increased with the annealing temperature. It could be attributed to the growth of Fe-rich precipitates by annealing. It is thus suggested that the lower annealing temperatures provide the better corrosion properties without degrading the tensile properties
Dependence of Crystallographic Orientation on Pitting Corrosion Behavior of Ni-Fe-Cr Alloy 028

Science.gov (United States)

Zhang, LiNa; Szpunar, Jerzy A.; Dong, JianXin; Ojo, Olanrewaju A.; Wang, Xu

2018-03-01

The influence of crystallographic orientation on the pitting corrosion behavior of Ni-Fe-Cr alloy 028 was studied using a combination of X-ray diffraction (XRD), electron backscatter diffraction (EBSD), potentiodynamic polarization technique, and atomic force microscopy (AFM). The results show that there is anisotropy of pitting corrosion that strongly depends on crystallographic orientation of the surface plane. The distribution of pit density in a standard stereographic triangle indicates that the crystallographic planes close to {100} are more prone to pitting corrosion compared to planes {110} and {111}. The surface energy calculation of (001) and (111) shows that the plane with a high atomic packing density has a low surface energy with concomitant strong resistance to pitting corrosion. A correlation function between crystallographic orientation and pitting corrosion susceptibility suggests a method that not only predicts the pitting resistance of known textured materials, but also could help to improve corrosion resistance by controlling material texture.
Influence of sulfide concentration on the corrosion behavior of pure copper in synthetic seawater

International Nuclear Information System (INIS)

Taniguchi, Naoki; Kawasaki, Manabu

2008-01-01

Corrosion rate and stress corrosion cracking (SCC) behavior of pure copper under anaerobic conditions were studied by immersion tests and slow strain rate tests (SSRT) in synthetic seawater containing Na 2 S. The corrosion rate was increased with sulfide concentration both in simple saline solution and in bentnite-sand mixture. The results of SSRT showed that copper was susceptible to intergranular attack; selective dissolution at lower sulfide concentration (less than 0.005 M) and SCC at higher sulfide concentration (0.01 M). It was expected that if the sulfide concentration in groundwater is less than 0.001 M, pure copper is possible to exhibit superior corrosion resistance under anaerobic condition evident by very low corrosion rates and immunity to SCC. In such a low sulfide environment, copper overpack has the potential to achieve super-long lifetimes exceeding several tens of thousands years according to long-term simulations of corrosion based on diffusion of sulfide in buffer material
Effect of pH on corrosion behavior of CuCrZr in solution without and with NaCl

Energy Technology Data Exchange (ETDEWEB)

Kwok, C.T.; Wong, P.K. [Department of Electromechanical Engineering, University of Macau (China); Man, H.C. [Department of Industrial and Systems Engineering, Hong Kong Polytechnic University (Hong Kong); Cheng, F.T., E-mail: apaftche@polyu.edu.h [Department of Applied Physics, Hong Kong Polytechnic University (Hong Kong)

2009-10-01

CuCrZr is a high copper alloy widely used as electrical and thermal conducting material, especially in heat exchangers in nuclear reactors. In this respect, the physical and fatigue properties of CuCrZr have been extensively studied. The electrochemical behavior of CuCrZr, on the other hand, has not been adequately investigated. In the present study, the effect of pH on the corrosion behavior of CuCrZr in aqueous solutions without and with chloride (0.6 M NaCl) was studied. The pH of the solutions is found to exert significant influence on the corrosion behavior of CuCrZr. In acidic solutions without chloride, the corrosion of CuCrZr is ascribed to active dissolution with soluble products. In neutral and alkaline solutions without NaCl, the presence of oxides on the surface of CuCrZr leads to a noble shift in corrosion potential and passivation results in increased corrosion resistance. In chloride solutions at various pH values, the chloride ions influence the formation of the surface layers and the anodic dissolution process during polarization. At high pH, CuCrZr shows significant passivity and high corrosion resistance due to the growth of Cu{sub 2}O/Cu(OH) film which hinders further dissolution whereas at low pH the corrosion resistance is lowered due to active dissolution of Cu.
Effect of pH on corrosion behavior of CuCrZr in solution without and with NaCl

International Nuclear Information System (INIS)

Kwok, C.T.; Wong, P.K.; Man, H.C.; Cheng, F.T.

2009-01-01

CuCrZr is a high copper alloy widely used as electrical and thermal conducting material, especially in heat exchangers in nuclear reactors. In this respect, the physical and fatigue properties of CuCrZr have been extensively studied. The electrochemical behavior of CuCrZr, on the other hand, has not been adequately investigated. In the present study, the effect of pH on the corrosion behavior of CuCrZr in aqueous solutions without and with chloride (0.6 M NaCl) was studied. The pH of the solutions is found to exert significant influence on the corrosion behavior of CuCrZr. In acidic solutions without chloride, the corrosion of CuCrZr is ascribed to active dissolution with soluble products. In neutral and alkaline solutions without NaCl, the presence of oxides on the surface of CuCrZr leads to a noble shift in corrosion potential and passivation results in increased corrosion resistance. In chloride solutions at various pH values, the chloride ions influence the formation of the surface layers and the anodic dissolution process during polarization. At high pH, CuCrZr shows significant passivity and high corrosion resistance due to the growth of Cu 2 O/Cu(OH) film which hinders further dissolution whereas at low pH the corrosion resistance is lowered due to active dissolution of Cu.
Corrosion behavior of porous chromium carbide in supercritical water

International Nuclear Information System (INIS)

Dong Ziqiang; Chen Weixing; Zheng Wenyue; Guzonas, Dave

2012-01-01

Highlights: ► Corrosion behavior of porous Cr 3 C 2 in various SCW conditions was investigated. ► Cr 3 C 2 is stable in SCW at temperature below 420–430 °C. ► Cracks and disintegration were observed at elevated testing temperatures. ► Degradation of Cr 3 C 2 is related to the intermediate product CrOOH. - Abstract: The corrosion behavior of highly porous chromium carbide (Cr 3 C 2 ) prepared by a reactive sintering process was characterized at temperatures ranging from 375 °C to 625 °C in a supercritical water environment with a pressure of 25–30 MPa. The test results show that porous chromium carbide is stable in SCW environments at temperatures under 425 °C, above which disintegration occurred. The porous carbide was also tested under hydrothermal conditions of pressures between 12 MPa and 50 MPa at constant temperatures of 400 °C and 415 °C, respectively. The pressure showed little effect on the stability of chromium carbide in the tests at those temperatures. The mechanism of disintegration of chromium carbide in SCW environments is discussed.
Corrosion and alteration of materials from the nuclear industry

International Nuclear Information System (INIS)

Beauvy, M.; Berthoud, G.; Defranceschi, M.; Ducros, G.; Feron, D.; Guerin, Y.; Latge, C.; Limoge, Y.; Madic, C.; Santarini, G.; Seiler, J.M.; Vernaz, E.; Richet, C.

2010-01-01

The control of the corrosion phenomenon is of prime importance for the nuclear industry. The efficiency and the safety of facilities can be affected by this phenomenon. The nuclear industry has to face corrosion for a large variety of materials submitted to various environments. Metallic corrosion operates in the hot and aqueous environment of water reactors which represent the most common reactor type in the world. Progresses made in the control of the corrosion of the different components of these reactors allow to improve their safety. Corrosion is present in the facilities of the back-end of the fuel cycle as well (corrosion in acid environment in fuel reprocessing plants, corrosion of waste containers in disposal and storage facilities, etc). The future nuclear systems will widen even more the range of materials to be studied and the situations in which they will be placed (corrosion by liquid metals or by helium impurities). Very often, corrosion looks like a patchwork of particular cases in its description. The encountered corrosion problems and their study are presented in this book according to chapters representing the main sectors of the nuclear industry and classified with respect to their phenomenology. This monograph illustrates the researches in progress and presents some results of particular importance obtained recently. Content: 1 - Introduction: context, stakes and goals; definition of corrosion; a complex science; corrosion in the nuclear industry; 2 - corrosion in water reactors - phenomenology, mechanisms, remedies: A - uniform corrosion: mechanisms, uniform corrosion of fuel cladding, in-situ measurement of generalized corrosion rate by electrochemical methods, uniform corrosion of nickel alloys, characterization of the passive layer and growth mechanisms, the PACTOLE code - an integrating tool, influence of water chemistry on corrosion and contamination, radiolysis impact on uniform corrosion; B - stress corrosion: stress corrosion cracking
Effect of Mucin and Bicarbonate Ion on Corrosion Behavior of AZ31 Magnesium Alloy for Airway Stents.

Science.gov (United States)

Jang, Yongseok; Owuor, Daniel; Waterman, Jenora T; White, Leon; Collins, Boyce; Sankar, Jagannathan; Gilbert, Thomas W; Yun, Yeoheung

2014-08-15

The biodegradable ability of magnesium alloys is an attractive feature for tracheal stents since they can be absorbed by the body through gradual degradation after healing of the airway structure, which can reduce the risk of inflammation caused by long-term implantation and prevent the repetitive surgery for removal of existing stent. In this study, the effects of bicarbonate ion (HCO₃ - ) and mucin in Gamble's solution on the corrosion behavior of AZ31 magnesium alloy were investigated, using immersion and electrochemical tests to systematically identify the biodegradation kinetics of magnesium alloy under in vitro environment, mimicking the epithelial mucus surfaces in a trachea for development of biodegradable airway stents. Analysis of corrosion products after immersion test was performed using scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX) and X-ray diffraction (XRD). Electrochemical impedance spectroscopy (EIS) was used to identify the effects of bicarbonate ions and mucin on the corrosion behavior of AZ31 magnesium alloys with the temporal change of corrosion resistance. The results show that the increase of the bicarbonate ions in Gamble's solution accelerates the dissolution of AZ31 magnesium alloy, while the addition of mucin retards the corrosion. The experimental data in this work is intended to be used as foundational knowledge to predict the corrosion behavior of AZ31 magnesium alloy in the airway environment while providing degradation information for future in vivo studies.
Corrosion behavior of novel imitation-gold copper alloy with rare earth in 3.5% NaCl solution

International Nuclear Information System (INIS)

Chen, J.L.; Li, Z.; Zhu, A.Y.; Luo, L.Y.; Liang, J.

2012-01-01

Highlights: → The design alloy has better anti-tarnish property than that of H7211 alloy during salt-spray test. → The corrosion rate of design alloy is much lower than that of H7211 alloy as immersed in NaCl solution. → In the low frequency region, the capacitive behavior normally faded and diffusion process had a key role. → In the medium frequency region, the Bode pattern showed a capacitive behavior. -- Abstract: A novel imitation-gold copper alloy with rare earth was designed and prepared. The corrosion behavior of the alloy immersed in 3.5% NaCl solution and its anti-tarnish property in the salt spray for different days has been studied. The designed alloy (CuZnAlNiMeRe) has more excellent anti-tarnish property and lower corrosion rate than those of currency coinage materials of H7211 alloy (used in China). A uniform and compact of corrosion film has been formed after the designed alloy immersed in 3.5% NaCl solution. The corrosion current densities I corr of the alloy decreased while the polarization resistance R p increased with time. The capacitance of the corrosion product film C film of the alloy decreased while the charge transfer resistance R ct . The Warburg diffusion impedance W R and the resistance of the equivalent circuit R increased with time.
Effect of aging time on intergranular corrosion behavior of a newly developed LDX 2404 lean duplex stainless steel

Energy Technology Data Exchange (ETDEWEB)

Zhao, Hui [School of Materials Engineering, Shanghai University of Engineering Science, Shanghai 201620 (China); Zhang, Ziying, E-mail: zzying@sues.edu.cn [School of Materials Engineering, Shanghai University of Engineering Science, Shanghai 201620 (China); Zhang, Huizhen [School of Management, University of Shanghai for Science and Technology, Shanghai 200093 (China); Hu, Jun [School of Materials Engineering, Shanghai University of Engineering Science, Shanghai 201620 (China); Li, Jin [Department of Materials Science, Fudan University, Shanghai 200433 (China)

2016-07-05

The effect of aging at 700 °C for various times on the intergranular corrosion behavior of LDX 2404 duplex stainless steel is investigated by morphological observation and electrochemical detection. Scanning electronic microscopy and transmission electronic microscopy analysis reveal that Cr{sub 2}N, M{sub 23}C{sub 6} and the sigma and chi phases nucleate simultaneously at the initial stages of aging. The granular particles of sigma phase grow larger but fewer with the increase of aging time. The electrochemical detection results show that intergranular corrosion become more severe and the corrosion type evolves from intergranular corrosion into general corrosion as the holding time extends to 48 h. - Highlights: • The IGC behavior of aged LDX 2404 is investigated. • Cr{sub 2}N, M{sub 23}C{sub 6} and the σ and χ phases nucleate simultaneously at the initial stages of aging. • IGC resistance decreases with the increase of aging time. • The corrosion type evolves from IGC into general corrosion for longer aging times.
Corrosion inhibition behavior of Ketosulfone for Zinc in acidic medium

African Journals Online (AJOL)

The corrosion inhibition behavior of Ketosulfone for zinc is investigated by polarization and AC-impedance techniques at 303-333K. The Tafel plots indicates that the Ketosulfone is a mixed type inhibitor. The interaction between metal and inhibitor is explained by Langmuir adsorption isotherm. DG0ads andDH0ads value ...
Corrosion behavior of materials selected for FMIT lithium system

Energy Technology Data Exchange (ETDEWEB)

Bazinet, G.D.; Down, M.G.; Matlock, D.K.

1983-01-01

The corrosion program consisted of a multi-disciplinary approach utilizing the liquid lithium test resources and capabilities of several laboratories. Specific concerns associated with the overall objective of materials corrosion behavior were evaluated at each laboratory. Testing conditions included: approx. 3700 hours of exposure to flowing lithium at temperatures from 230/sup 0/C to 270/sup 0/C and approx. 6500 hours of exposure to flowing lithium at an isothermal temperature of 270/sup 0/C. Principal areas of investigation, to be discussed here briefly, included lithium corrosion effects on the following: (1) types 304 and 304L austenitic stainless steels, which are specified as reference materials for the FMIT lithium system; (2) type 304 stainless steel weldments (w/type 308 stainless steel filler) typical of specified tube and butt welds in the lithium system design; (3) titanium, zirconium and yttrium, which represent potential hot trap getter materials; (4) BNi4 braze alloy, used as a potential attachement method in the plug/seat fabrication of liquid lithium valves; and (5) type 321 stainless steel bellows, typical of bellows used in potential liquid lithium valve designs.
Investigation of high temperature corrosion behavior on 304L austenite stainless steel in corrosive environments

Energy Technology Data Exchange (ETDEWEB)

Sahri, M. I.; Othman, N. K.; Samsu, Z.; Daud, A. R. [School of Applied Physics, Faculty of Science and Technology, Universiti Kebangsaan Malaysia, 43600 UKM Bangi Selangor (Malaysia)

2014-09-03

In this work, 304L stainless steel samples were exposed at 700 °C for 10hrs in different corrosive environments; dry oxygen, molten salt, and molten salt + dry oxygen. The corrosion behavior of samples was analyzed using weight change measurement technique, optical microscope (OM) and Scanning Electron Microscope (SEM) equipped with Energy Dispersive X-ray (EDX). The existence phases of corroded sample were determined using X-ray Diffraction (XRD). The lowest corrosion rate was recorded in dry oxygen while the highest was in molten salt + dry oxygen environments with the value of 0.0062 mg/cm{sup 2} and −13.5225 mg/cm{sup 2} respectively. The surface morphology of sample in presence of salt mixture showed scale spallation. Oxide scales of Fe{sub 3}O{sub 4}, Fe{sub 2}O{sub 3} were the main phases developed and detected by XRD technique. Cr{sub 2}O{sub 3} was not developed in every sample as protective layers but chromate-rich oxide was developed. The cross-section analysis found the oxide scales were in porous, thick and non-adherent that would not an effective barrier to prevent from further degradation of alloy. EDX analysis also showed the Cr-element was low compared to Fe-element at the oxide scale region.
Evaluating the effects of hydroxyapatite coating on the corrosion behavior of severely deformed 316Ti SS for surgical implants

International Nuclear Information System (INIS)

Mhaede, Mansour; Ahmed, Aymen; Wollmann, Manfred; Wagner, Lothar

2015-01-01

The present work investigates the effects of severe plastic deformation by cold rolling on the microstructure, the mechanical properties and the corrosion behavior of austenitic stainless steel (SS) 316Ti. Hydroxyapatite coating (HA) was applied on the deformed material to improve their corrosion resistance. The martensitic transformation due to cold rolling was recorded by X-ray diffraction spectra. The effects of cold rolling on the corrosion behavior were studied using potentiodynamic polarization. The electrochemical tests were carried out in Ringer's solution at 37 ± 1 °C. Cold rolling markedly enhanced the mechanical properties while the electrochemical tests referred to a lower corrosion resistance of the deformed material. The best combination of both high strength and good corrosion resistance was achieved after applying hydroxyapatite coating. - Highlights: • Cold rolling markedly increases the hardness of SS 316Ti from 125 to 460 HV10. • Higher deformation degrees lead to lower corrosion resistance. • Application of HA-coating leads to significant improvement of the corrosion resistance
Effect of H2O2 on the corrosion behavior of 304L stainless steel

International Nuclear Information System (INIS)

Song, Taek Hoh; Kim, In Sub; Noh, Sung Kee

1995-01-01

In connection with the safe storage of high level nuclear waste, effect of H 2 O 2 on the corrosion behavior of 304L stainless steel was examined. Open circuit potentials and polarization curves were measured with and without H 2 O 2 . The experimental results show that H 2 O 2 increased corrosion potential and decreased pitting potential. The passive range, therefore, decreased as H 2 O 2 concentration increased, indicating that pitting resistance was decreased by the existence of H 2 O 2 in the electrolyte. These effects of H 2 O 2 on corrosion of 304L stainless steel are considered to be similar to those of γ-irradiation. To compare the effects of H 2 O 2 with those of O 2 , cathodic and anodic polarization curves were made in three types of electrolyte such as aerated, deaerated, and stirred electrolyte. The experimental results show that the effects of H 2 O 2 on the corrosion behavior were very similar to those of O 2 such as increase of corrosion potential, decrease of pitting resistance, and increase of repassivation potential. In acid and alkaline media, the corrosion potential shifts by H 2 O 2 were restricted by the large current density of proton reduction and by the le Chatelier's principle respectively. 13 figs., 1 tabs., 17 refs. (Author)
Hot corrosion behavior of magnesia-stabilized ceramic material in a lithium molten salt

Energy Technology Data Exchange (ETDEWEB)

Cho, Soo-Haeng, E-mail: nshcho1@kaeri.re.kr [Korea Atomic Energy Research Institute, Daejeon 305-353 (Korea, Republic of); Kim, Sung-Wook [Korea Atomic Energy Research Institute, Daejeon 305-353 (Korea, Republic of); Kim, Dae-Young [Graduate School of Energy Science and Technology, Chungnam National University, Daejeon 305-764 (Korea, Republic of); Lee, Jong-Hyeon, E-mail: jonglee@cnu.ac.kr [Graduate School of Energy Science and Technology, Chungnam National University, Daejeon 305-764 (Korea, Republic of); Graduate School of Advanced Materials Engineering, Chungnam National University, Daejeon 305-764 (Korea, Republic of); Rapidly Solidified Materials Research Center, Chungnam National University, Daejeon 305-764 (Korea, Republic of); Hur, Jin-Mok [Korea Atomic Energy Research Institute, Daejeon 305-353 (Korea, Republic of)

2017-07-15

The isothermal and cyclic corrosion behaviors of magnesia-stabilized zirconia in a LiCl-Li{sub 2}O molten salt were investigated at 650 °C in an argon atmosphere. The weights of as-received and corroded specimens were measured and the microstructures, morphologies, and chemical compositions were analyzed by scanning electron microscopy, X-ray energy dispersive spectroscopy, and X-ray diffraction. For processes where Li is formed at the cathode during electrolysis, the corrosion rate was about five times higher than those of isothermal and thermal cycling processes. During isothermal tests, the corrosion product Li{sub 2}ZrO{sub 3} was formed after 216 h. During thermal cycling, Li{sub 2}ZrO{sub 3} was not detected until after the completion of 14 cycles. There was no evidence of cracks, pores, or spallation on the corroded surfaces, except when Li was formed. We demonstrate that magnesia-stabilized zirconia is beneficial for increasing the hot corrosion resistance of structural materials subjected to high temperature molten salts containing Li{sub 2}O. - Highlights: •Corrosion mechanism of MSZin LiCl-Li{sub 2}O molten salt is proposed. •Formation of Li{sub 2}ZrO{sub 3}is main corrosion mechanism. •There were no cracks, pores and spallation after corrosion test. •MSZ shows high corrosion resistance to LiCl-Li{sub 2}O molten salt.
Effect of ion implantation on the corrosion behavior of lead and a lead-antimony alloy

International Nuclear Information System (INIS)

Zhang, S.T.; Kong, F.P.; Muller, R.H.

1994-01-01

Ion implantation of different metals in Pb and Pb-4% Sb has been found to improve the open-circuit corrosion resistance of the two metals in 5M H 2 SO 4 . Titanium ions were implanted under different conditions of ion dose and ion energy. Optimum implantation conditions resulted in an up to 72-fold reduction of corrosion currents. The implantation of V, Cr, Ni, and W has been investigated for one implantation condition and has also resulted in decreased corrosion currents. The corrosion behavior was characterized by the current response to small anodic potential steps. Surface analysis and depth profiles have shown the importance of the spatial distribution of the implanted ions for their effects on the anodic and cathodic parts of the corrosion reactions
The corrosion behavior of the T1 (Al2CuLi) intermetallic compound in aqueous environments

Science.gov (United States)

Buchheit, R. G.; Stoner, G. E.

1989-01-01

The intermetallic compound T1 (Al2CuLi) is suspected to play an important role in the localized corrosion at subgrain boundaries in Al-Li-Cu alloys. The intermetallic was synthesized for characterization of its corrosion behavior. Experiments performed included open circuit potential measurements, potentiodynamic polarization, and corrosion rate vs. pH in solutions whose pH was varied over the range of 3 to 11. Subgrain boundary pitting and continuous subgrain boundary corrosion are discussed in terms of the data obtained. Evidence suggesting the dealloying of copper from this compound is also presented.

Influence of the microstructure on the corrosion behavior of magnetron sputter-quenched amorphous metallic alloys

Science.gov (United States)

Thakoor, A. P.; Khanna, S. K.; Williams, R. M.; Landel, R. F.

1983-01-01

The microstructure and corrosion behavior of magnetron sputter deposited amorphous metallic films of (Mo6ORu40)82B18 under varying sputtering atmospheres have been investigated. The microstructural details and topology of the films have been studied by scanning electron microscopy and correlated with the deposition conditions. By reducing the pressure of pure argon gas, the characteristic features of rough surface and columnar growth full of vertical voids can be converted into a mirror-smooth finish with very dense deposits. Films deposited in the presence of O2 or N2 exhibit columnar structure with vertical voids. Film deposited in pure argon at low pressure show remarkably high corrosion resistance due to the formation of a uniform passive surface layer. The influence of the microstructure and surface texture on the corrosion behavior is discussed.
Effect of Secondary Phase Precipitation on the Corrosion Behavior of Duplex Stainless Steels

Directory of Open Access Journals (Sweden)

Kai Wang Chan

2014-07-01

Full Text Available Duplex stainless steels (DSSs with austenitic and ferritic phases have been increasingly used for many industrial applications due to their good mechanical properties and corrosion resistance in acidic, caustic and marine environments. However, DSSs are susceptible to intergranular, pitting and stress corrosion in corrosive environments due to the formation of secondary phases. Such phases are induced in DSSs during the fabrication, improper heat treatment, welding process and prolonged exposure to high temperatures during their service lives. These include the precipitation of sigma and chi phases at 700–900 °C and spinodal decomposition of ferritic grains into Cr-rich and Cr-poor phases at 350–550 °C, respectively. This article gives the state-of the-art review on the microstructural evolution of secondary phase formation and their effects on the corrosion behavior of DSSs.
Electrochemical behavior of tube-fin assembly for an aluminum automotive condenser with improved corrosion resistance

Science.gov (United States)

Pech-Canul, M. A.; Guía-Tello, J. C.; Pech-Canul, M. I.; Aguilar, J. C.; Gorocica-Díaz, J. A.; Arana-Guillén, R.; Puch-Bleis, J.

An aluminum automotive condenser was designed to exhibit high corrosion resistance in the seawater acetic acid test (SWAAT) combining zinc coated microchannel tubes and fins made with AA4343/AA3003(Zn)/AA4343 brazing sheet. Electrochemical measurements in SWAAT solution were carried out under laboratory conditions using tube-fin assembly and individual fin and tube samples withdrawn from the condenser core. The aim was to gain information on the protective role of the zinc sacrificial layer and about changes in corrosion behavior as a function of immersion time. External corrosion of the tube-fin system was simulated by immersion of mini-core samples under open circuit conditions. The corrosion rate increased rapidly during the first 6 h and slowly afterwards. The short time behavior was related to the dissolution of the oxide film and fast dissolution of the outermost part of the zinc diffusion layer. With the aid of cross-sectional depth corrosion potential profiles, it was shown that as the sacrificial layer gets dissolved, the surface concentration of zinc decreases and the potential shifts to less negative values. The results of galvanic coupling of tube and fins in a mini-cell showed that the tube became the anode while the fins exhibited cathodic behavior. An evolution in the galvanic interaction was observed, due to the progressive dissolution of the sacrificial zinc layer. The difference of uncoupled potentials between tube and fins decreased from 71 mV to 32 mV after 84 h of galvanic coupling. At the end of such period there was still a part of the zinc sacrificial layer remaining which would serve for protection of the tube material for even longer periods and there were indications of slight corrosion in the fins.
Effects of annealing on the corrosion behavior and mechanical properties of Ti-Al-V alloy

International Nuclear Information System (INIS)

Kim, T. K.; Choi, B. S.; Baek, J. H.; Choi, B. K.; Jeong, Y. H.; Lee, D. J.; Jang, M. H.; Jeong, Y. H.

2002-01-01

In order to determine the annealing condition after cold rolling, the effects of annealing on the corrosion behavior and mechanical properties of Ti-Al-V alloy were evaluated. The results of tensile tests at room temperature showed that the strengths and the ductility were almost independent of the annealing temperature. The results of hardness test also revealed that the hardness was independent of the annealing, However, the results of corrosion test in an ammoniated water of pH 9.98 at 360 .deg. C showed that the corrosion resistance depended on the annealing temperature, and the corrosion rate was accelerated with increasing annealing temperature. Hydrogen contents absorbed during the corrosion test of 120 days also increased with the annealing temperature. It may be attributed to the growth of α' precipitates by annealing. It is thus suggested that the lower annealing temperatures provide the better corrosion properties without degrading the tensile properties
Hydrogen assisted cracking and CO2 corrosion behaviors of low-alloy steel with high strength used for armor layer of flexible pipe

Science.gov (United States)

Liu, Zhenguang; Gao, Xiuhua; Du, Linxiu; Li, Jianping; Zhou, Xiaowei; Wang, Xiaonan; Wang, Yuxin; Liu, Chuan; Xu, Guoxiang; Misra, R. D. K.

2018-05-01

In this study, hydrogen induced cracking (HIC), sulfide stress corrosion cracking (SSCC) and hydrogen embrittlement (HE) were carried out to study hydrogen assisted cracking behavior (HIC, SSCC and HE) of high strength pipeline steel used for armor layer of flexible pipe in ocean. The CO2 corrosion behavior of designed steel with high strength was studied by using immersion experiment. The experimental results demonstrate that the corrosion resistance of designed steel with tempered martensite to HIC, SSCC and HE is excellent according to specific standards, which contributes to the low concentration of dislocation and vacancies previously formed in cold rolling process. The corrosion mechanism of hydrogen induced cracking of designed steel, which involves in producing process, microstructure and cracking behavior, is proposed. The designed steel with tempered martensite shows excellent corrosion resistance to CO2 corrosion. Cr-rich compound was first formed on the coupon surface exposed to CO2-saturated brine condition and chlorine, one of the corrosion ions in solution, was rich in the inner layer of corrosion products.
Corrosion behavior of biodegradable material AZ31 coated with beeswax-colophony resin

Science.gov (United States)

Gumelar, Muhammad Dikdik; Putri, Nur Ajrina; Anggaravidya, Mahendra; Anawati, Anawati

2018-05-01

Magnesium (Mg) and its alloys are potential candidates for biodegradable implant materials owing to their ability to degrade spontaneously in a physiological environment. However, the degradation rate is still considered too fast in human body solution. A coating is typically applied to slowdown corrosion rate of Mg alloys. In this work, an organic coating of mixture beeswax-colophony with ratios of 40-60, 50-50, and 60-40 in wt% was synthesized and applied on commercial magnesium alloyAZ31. The coated specimens were then characterized with SEM and XRF. The corrosion behavior of the coated specimens was evaluated by immersion test in 0.9 wt% NaCl solution at 37°C for 14 days. The results indicated that the coating material improved the corrosion resistance of the AZ31 alloy.
Study of Rust Effect on the Corrosion Behavior of Reinforcement Steel Using Impedance Spectroscopy

Science.gov (United States)

Bensabra, Hakim; Azzouz, Noureddine

2013-12-01

Most studies on corrosion of steel reinforcement in concrete are conducted on steel samples with polished surface (free of all oxides) in order to reproduce the same experimental conditions. However, before embedding in concrete, the steel bars are often covered with natural oxides (rust), which are formed during exposure to the atmosphere. The presence of this rust may affect the electrochemical behavior of steel rebar in concrete. In order to understand the effect of rust on the corrosion behavior of reinforcement steel, potentiodynamic and electrochemical impedance spectroscopy (EIS) tests were carried out in a simulated concrete pore solution using steel samples with two different surface conditions: polished and rusted samples. The obtained results have shown that the presence of rust on the steel bar has a negative effect on its corrosion behavior, with or without the presence of chlorides. This detrimental effect can be explained by the fact that the rust provokes a decrease of the electrolyte resistance at the metal-concrete interface and reduces the repassivating ability. In addition, the rust layer acts as a barrier against the hydroxyl ion diffusion, which prevents the realkalinization phenomenon.
Effect of magnesium hydride on the corrosion behavior of an AZ91 magnesium alloy in sodium chloride solution

International Nuclear Information System (INIS)

Chen Jian; Dong Junhua; Wang Jianqiu; Han Enhou; Ke Wei

2008-01-01

The effect of magnesium hydride on the corrosion behavior of an as-cast AZ91 alloy in 3.5 wt.% NaCl solution was investigated using gas collection method and potentiostatic test. The Pourbaix diagram of Mg-H 2 O system was built using thermodynamic calculation. It was possible that magnesium hydride could form in the whole pH range in theory. The experimental results showed that at cathodic region, magnesium hydride formed on surface, which was the controlling process for the corrosion behavior of AZ91 alloy; at anodic region and free corrosion potential, magnesium hydride model and partially protective film model, monovalent magnesium ion model and particle undermining model were responsible for the corrosion process of AZ91 alloy
Effect of Mucin and Bicarbonate Ion on Corrosion Behavior of AZ31 Magnesium Alloy for Airway Stents

Directory of Open Access Journals (Sweden)

Yongseok Jang

2014-08-01

Full Text Available The biodegradable ability of magnesium alloys is an attractive feature for tracheal stents since they can be absorbed by the body through gradual degradation after healing of the airway structure, which can reduce the risk of inflammation caused by long-term implantation and prevent the repetitive surgery for removal of existing stent. In this study, the effects of bicarbonate ion (HCO3− and mucin in Gamble’s solution on the corrosion behavior of AZ31 magnesium alloy were investigated, using immersion and electrochemical tests to systematically identify the biodegradation kinetics of magnesium alloy under in vitro environment, mimicking the epithelial mucus surfaces in a trachea for development of biodegradable airway stents. Analysis of corrosion products after immersion test was performed using scanning electron microscopy (SEM, energy dispersive X-ray spectroscopy (EDX and X-ray diffraction (XRD. Electrochemical impedance spectroscopy (EIS was used to identify the effects of bicarbonate ions and mucin on the corrosion behavior of AZ31 magnesium alloys with the temporal change of corrosion resistance. The results show that the increase of the bicarbonate ions in Gamble’s solution accelerates the dissolution of AZ31 magnesium alloy, while the addition of mucin retards the corrosion. The experimental data in this work is intended to be used as foundational knowledge to predict the corrosion behavior of AZ31 magnesium alloy in the airway environment while providing degradation information for future in vivo studies.
Effects of chitosan inhibitor on the electrochemical corrosion behavior of 2205 duplex stainless steel

Science.gov (United States)

Yang, Se-fei; Wen, Ying; Yi, Pan; Xiao, Kui; Dong, Chao-fang

2017-11-01

The effects of chitosan inhibitor on the corrosion behavior of 2205 duplex stainless steel were studied by electrochemical measurements, immersion tests, and stereology microscopy. The influences of immersion time, temperature, and chitosan concentration on the corrosion inhibition performance of chitosan were investigated. The optimum parameters of water-soluble chitosan on the corrosion inhibition performance of 2205 duplex stainless steel were also determined. The water-soluble chitosan showed excellent corrosion inhibition performance on the 2205 duplex stainless steel. Polarization curves demonstrated that chitosan acted as a mixed-type inhibitor. When the stainless steel specimen was immersed in the 0.2 g/L chitosan solution for 4 h, a dense and uniform adsorption film covered the sample surface and the inhibition efficiency (IE) reached its maximum value. Moreover, temperature was found to strongly influence the corrosion inhibition of chitosan; the inhibition efficiency gradually decreased with increasing temperature. The 2205 duplex stainless steel specimen immersed in 0.4 g/L water-soluble chitosan at 30°C displayed the best corrosion inhibition among the investigated specimens. Moreover, chitosan decreased the corrosion rate of the 2205 duplex stainless steel in an FeCl3 solution.
Al-Co Alloys Prepared by Vacuum Arc Melting: Correlating Microstructure Evolution and Aqueous Corrosion Behavior with Co Content

Directory of Open Access Journals (Sweden)

Angeliki Lekatou

2016-02-01

Full Text Available Hypereutectic Al-Co alloys of various Co contents (7–20 weight % (wt.% Co were prepared by vacuum arc melting, aiming at investigating the influence of the cobalt content on the microstructure and corrosion behavior. Quite uniform and directional microstructures were attained. The obtained microstructures depended on the Co content, ranging from fully eutectic growth (7 wt.% and 10 wt.% Co to coarse primary Al9Co2 predominance (20 wt.% Co. Co dissolution in Al far exceeded the negligible equilibrium solubility of Co in Al; however, it was hardly uniform. By increasing the cobalt content, the fraction and coarseness of Al9Co2, the content of Co dissolved in the Al matrix, and the hardness and porosity of the alloy increased. All alloys exhibited similar corrosion behavior in 3.5 wt.% NaCl with high resistance to localized corrosion. Al-7 wt.% Co showed slightly superior corrosion resistance than the other compositions in terms of relatively low corrosion rate, relatively low passivation current density and scarcity of stress corrosion cracking indications. All Al-Co compositions demonstrated substantially higher resistance to localized corrosion than commercially pure Al produced by casting, cold rolling and arc melting. A corrosion mechanism was formulated. Surface films were identified.
Studies on the Corrosion Behavior of TiCode-12 with the Variation of Environmental Factors and Heat Treatment Conditions

International Nuclear Information System (INIS)

Yoon, S. R.; Kim, T. Y.; Lee, K. H.

1989-01-01

Corrosion behavior of TiCode-12 (Ti-0.8Ni-0.3Mo) has been studied by means of electrochemical polarization measurements and corrosion morphology examinations in various corrosive environments and different heat treatment conditions of the alloy. 1N H 2 SO 4 at 45 .deg. C was taken as a standard corrosive solution in which Cl - , Fe 3+ and Br - ion were added to investigate their effects. Acid concentration and temperature were also varied. Polarization behaviors of pure Ti, Ni, Mo and Ti 2 Ni were compared with those of heat-treated TiCode-12 specimens to find out how the constituent elements and the intermetallic compound formed during heat treatment of TiCode-12 affect the corrosion of the alloy. Mill-annealed TiCode-12 showed primary and secondary active-passive transition behavior in all the tested H 2 SO 4 solutions. The former behavior was confirmed to be due to Ti and the latter due to Ni and Mo. The passive current densities increased with increased Cl - ion concentration but decreased reversely beyond certain concentration. Fe 3+ ion raised the corrosion potential of TiCode-12 to the passive region, thus reducing the corrosion rate. Br - ion was turned out to be a critical species to induce the pitting of TiCode-12 by some unknown reason. Cathodic polarization behavior of pure Ni and Ti 2 Ni revealed that hydrogen evolution reaction was promoted on these electrodes in acid media. This was ascribed to the cause for sensitization phenomena of TiCode-12 heat-treated in the temperature range in which the eutectoid reaction β→α + Ti 2 Ni occurs. Near pits, observed on a sensitized TiCode-12 specimen immersed in H 2 SO 4 , always found were β crystals in which Ni peak was detected by EDS
Recent work on graphite corrosion in dragon HTR

International Nuclear Information System (INIS)

Wilkinson, V.J.; Parsons, P.D.; Lind, R.

1976-01-01

Recent studies are described of graphite corrosion in the Dragon reactor as a consequence of a programme of moisture additions to the helium coolant. The pattern of oxidation was significantly different from that expected from out-of-pile studies. Explanations are suggested in terms of flow and pore structure effects. (orig.) [de
The Behavior of Environmentally Friendly Corrosion Preventative Compounds in an Aggressive Coastal Marine Environment

Science.gov (United States)

Montgomery, Eliza L.; Calle, Luz Marina; Curran Jerome C.; Kolody, Mark R.

2013-01-01

The shift to use environmentally friendly technologies throughout future space-related launch programs prompted a study aimed at replacing current petroleum and solvent-based Corrosion Preventive Compounds (CPCs) with environmentally friendly alternatives. The work in this paper focused on the identification and evaluation of environmentally friendly CPCs for use in protecting flight hardware and ground support equipment from atmospheric corrosion. The CPCs, while a temporary protective coating, must survive in the aggressive coastal marine environment that exists throughout the Kennedy Space Center, Florida. The different protection behaviors of fifteen different soft film CPCs, both common petroleum-based and newer environmentally friendly types, were evaluated on various steel and aluminum substrates. The CPC and substrate systems were subjected to atmospheric testing at the Kennedy Space Center's Beachside Atmospheric Corrosion Test Site, as well as cyclic accelerated corrosion testing. Each CPC also underwent physical characterization and launch-related compatibility testing . The initial results for the fifteen CPC systems are reported : Key words: corrosion preventive compound, CPC, spaceport, environmentally friendly, atmospheric exposure, marine, carbon steel, aluminum alloy, galvanic corrosion, wire on bolt.
Maintenance free gas bearing helium blower for nuclear plant

Science.gov (United States)

Molyneaux, A., Dr; Harris, M., Prof; Sharkh, S., Prof; Hill, S.; de Graaff, T.

2017-08-01

This paper describes the design, testing and operation of novel helium blowers used to recirculate the helium blanketing gas in the nuclear reactor used as a neutron source at the Institut Laue Langevan, Grenoble, France. The laser sintered shrouded centrifugal wheel operates at speeds up to 45000 rpm supported on helium lubricated hydrodynamic spiral groove bearings, and is driven by a sensorless permanent magnet motor. The entire machine is designed to keep the helium gas (polluted by a small amount of D2O) out of contact with any iron or copper materials which would contribute to the corrosion of parts of the circuit. It is designed to have zero maintenance during a lifetime of 40,000 hours of continuous operation. This paper will describe the spiral groove journal and thrust bearings. Design and manufacture of the 1 kW motor and centrifugal wheel will be explained including their CFD and FEA analyses. Measurements of rotor displacement will be presented showing the behaviour under factory testing as well as details of the measured centrifugal wheel and motor performances. Two machines are incorporated into the circuit to provide redundancy and the first blower has been in continuous operation since Jan 2015. The blower was designed, manufactured, assembled and tested in the UK using predominantly UK suppliers.
Corrosion behavior of 2205 duplex stainless steel.

Science.gov (United States)

Platt, J A; Guzman, A; Zuccari, A; Thornburg, D W; Rhodes, B F; Oshida, Y; Moore, B K

1997-07-01

The corrosion of 2205 duplex stainless steel was compared with that of AISI type 316L stainless steel. The 2205 stainless steel is a potential orthodontic bracket material with low nickel content (4 to 6 wt%), whereas the 316L stainless steel (nickel content: 10 to 14 wt%) is a currently used bracket material. Both stainless steels were subjected to electrochemical and immersion (crevice) corrosion tests in 37 degrees C, 0.9 wt% sodium chloride solution. Electrochemical testing indicates that 2205 has a longer passivation range than 316L. The corrosion rate of 2205 was 0.416 MPY (milli-inch per year), whereas 316L exhibited 0.647 MPY. When 2205 was coupled to 316L with equal surface area ratio, the corrosion rate of 2205 reduced to 0.260 MPY, indicating that 316L stainless steel behaved like a sacrificial anode. When 316L is coupled with NiTi, TMA, or stainless steel arch wire and was subjected to the immersion corrosion test, it was found that 316L suffered from crevice corrosion. On the other hand, 2205 stainless steel did not show any localized crevice corrosion, although the surface of 2205 was covered with corrosion products, formed when coupled to NiTi and stainless steel wires. This study indicates that considering corrosion resistance, 2205 duplex stainless steel is an improved alternative to 316L for orthodontic bracket fabrication when used in conjunction with titanium, its alloys, or stainless steel arch wires.
Microstructure and Corrosion Behavior of Ni-Alloy/CrN Nanolayered Coatings

Directory of Open Access Journals (Sweden)

Hao-Hsiang Huang

2011-01-01

Full Text Available The Ni-alloy/CrN nanolayered coatings, Ni-Al/CrN and Ni-P/CrN, were deposited on (100 silicon wafer and AISI 420 stainless steel substrates by dual-gun sputtering technique. The influences of the layer microstructure on corrosion behavior of the nanolayered thin films were investigated. The bilayer thickness was controlled approximately 10 nm with a total coating thickness of 1m. The single-layer Ni-alloy and CrN coatings deposited at 350∘C were also evaluated for comparison. Through phase identification, phases of Ni-P and Ni-Al compounds were observed in the single Ni-alloy layers. On the other hand, the nanolayered Ni-P/CrN and Ni-Al/CrN coatings showed an amorphous/nanocrystalline microstructure. The precipitation of Ni-Al and Ni-P intermetallic compounds was suppressed by the nanolayered configuration of Ni-alloy/CrN coatings. Through Tafel analysis, the corr and corr values ranged from –0.64 to –0.33 V and 1.42×10−5 to 1.14×10−6 A/cm2, respectively, were deduced for various coating assemblies. The corrosion mechanisms and related behaviors of the coatings were compared. The coatings with a nanolayered Ni-alloy/CrN configuration exhibited a superior corrosion resistance to single-layer alloy or nitride coatings.
Study of corrosion behavior of carbon steel under seawater film using the wire beam electrode method

International Nuclear Information System (INIS)

Liu, Zaijian; Wang, Wei; Wang, Jia; Peng, Xin; Wang, Yanhua; Zhang, Penghui; Wang, Haijie; Gao, Congjie

2014-01-01

Corrosion behavior of carbon steel under seawater film with various thickness was investigated by the wire beam electrode (WBE) method. It was found that the corrosion rate of carbon steel increased significantly under thin seawater film than it was immersed in seawater. The current variation under seawater film indicated that the thickness of diffusion layer of oxygen was about 500 μm, and the maximal current appeared around 40 μm, at which corrosion rate transited from cathodic control to anodic control. The results suggest that WBE method is helpful to study the corrosion process under thin electrolyte film
Annealing Effect on Corrosion Behavior of the Beta-Quenched HANA Alloy

International Nuclear Information System (INIS)

Kim, Hyun Gil; Kim, Il Hyun; Choi, Byung Kwan; Park, Sang Yoon; Park, Jeong Yong; Jeong, Yong Hwan

2009-01-01

The advanced fuel cladding materials named as HANA cladding have been developed at KAERI for application of high burn-up and that cladding showed an improved performance in both in-pile and out-of-pile conditions. However, the cladding performance could be changed by the annealing conditions during the tube manufacturing process. Especially, the corrosion resistance is considerably sensitive to their microstructure which is determined by a manufacturing process in the high Nb-containing zirconium alloys. They reported that the corrosion properties of the Nb-containing Zr alloys were considerably affected by the microstructure conditions such as the Nb concentration in the matrix and the second phase types. Therefore, the corrosion behavior of HANA cladding having the high Nb could be considerably affected by the annealing time and temperatures. The purpose of this study is focused on the annealing effect of the beta quenched HANA alloy to obtain the optimum annealing conditions
Comparison of the long-time corrosion behavior of certain Zr alloys in PWR, BWR, and laboratory tests

International Nuclear Information System (INIS)

Garzarolli, F.; Broy, Y.; Busch, R.A.

1996-01-01

Laboratory corrosion tests have always been an important tool for Zr alloy development and optimization. However, it must be known whether a test is representative for the application in-reactor. To shed more light on this question, coupons of several Zr alloys were exposed under isothermal conditions in BWR and PWR type environments. For evaluation of the in-PWR tests and for comparison of out-of-pile and in-pile tests, the different temperatures and times were normalized to a temperature-independent normalized time by assuming an activation temperature (Q/R) of 14,200 K. Comparison of in-PWR and out-of-pile corrosion behavior of Zircaloy shows that corrosion deviates to higher values in PWR if a weight gain of about 50 mg/dm 2 is exceeded. In the case of the Zr2.5Nb alloy, a slight deviation of corrosion as compared to laboratory results starts in PWR only above a weight gain of 100 mg/dm 2 . In BWR, corrosion of Zircaloy is enhanced early in time if compared with out-of-pile. Zr2.5Nb exhibits higher corrosion results in BWR than Zircaloy-4. Alloying chemistry and material condition affect corrosion of Zr alloys. However, several of the material parameters have shown a different ranking in the different environments. Nevertheless, several material parameters influencing in-reactor corrosion like the second phase particle (SPP) size of in-PWR behavior as the Sn and Fe content can be optimized by out-of-pile corrosion tests

Polarization and EIS studies to evaluate the effect of aluminum concentration on the corrosion behavior of SAC105 solder alloy

Directory of Open Access Journals (Sweden)

Liyana N. K.

2018-03-01

Full Text Available This paper presents an investigation on corrosion behavior of Sn-1.0Ag-0.5Cu-XAl (X = 0, 0.1, 0.5, 1.0 by means of polarization and electrochemical impedance spectroscopy (EIS measurements in 3.5 wt.% NaCl solution. The results show that addition of aluminum into SAC105 shifts the corrosion current density and passivation current density towards more positive values. It is also found that with an increase in aluminum concentration in SAC105 solder alloy, the corrosion current density increases and polarization resistance decreases. This suggests that SAC105 with the highest concentration of Al has the lowest corrosion resistance. In this case, the corrosion behavior seems to be attributed to anodic dissolution of aluminum and Sn-matrix.
Properties, weldability and corrosion behavior of supermartensitic stainless steels for on- and offshore applications

Energy Technology Data Exchange (ETDEWEB)

Taban, Emel; Kaluc, Erdinc; Ojo, Olatunji Oladimeji [Kocaeli Univ. (Turkey). Welding Research, Education and Training Center

2016-08-01

Stimulated material-environment interactions inside and around flowlines of deep or ultra deep wells during oil and gas exploration, and fabrication economy of pipelines have been the major challenges facing the oil and gas industries. Presumably, an extensive focus on high integrity, performance and material economy of flowlines have realistically made supermartensitic stainless steels (SMSS) efficient and effective material choices for fabricating onshore and offshore pipelines. Supermartensitic stainless steels exhibit high strength, good low temperature toughness, sufficient corrosion resistance in sweet and mildly sour environments, and good quality weldability with both conventional welding processes and modern welding methods such as laser beam welding, electron beam welding and hybrid welding approaches. In terms of economy, supermartensitic stainless steels are cheaper and they are major replacements for more expensive duplex stainless steels required for tubing applications in the oil and gas industry. However, weld areas of SMSS pipes are exposed to sulphide stress cracking (SSC), so intergranular stress corrosion cracking (IGSCC) or stress corrosion cracking can occur. In order to circumvent this risk of cracking, a post-weld heat treatment (PWHT) for 5 minutes at about 650 C is recommended. This paper provides detailed literature perusal on supermartensitic stainless steels, their weldability and corrosion behaviors. It also highlights a major research area that has not been thoroughly expounded in literature; fatigue loading behaviors of welded SMSS under different corrosive environments have not been thoroughly detailed in literature.
Structural Characteristics and Corrosion Behavior of Bio-Degradable Zn-Li Alloys in Stent Application

Science.gov (United States)

Zhao, Shan

Zinc has begun to be studied as a bio-degradable material in recent years due to its excellent corrosion rate and optimal biocompatibility. Unfortunately, pure Zn's intrinsic ultimate tensile strength (UTS; below 120 MPa) is lower than the benchmark (about 300 MPa) for cardiovascular stent materials, raising concerns about sufficient strength to support the blood vessel. Thus, modifying pure Zn to improve its mechanical properties is an important research topic. In this dissertation project, a new Zn-Li alloy has been developed to retain the outstanding corrosion behavior from Zn while improving the mechanical characteristics and uniform biodegradation once it is implanted into the artery of Sprague-Dawley rats. The completed work includes: Manufactured Zn-Li alloy ingots and sheets via induction vacuum casting, melt spinning, hot rolling deformation, and wire electro discharge machining (wire EDM) technique; processed alloy samples using cross sectioning, mounting, etching and polishing technique; • Characterized alloy ingots, sheets and wires using hardness and tensile test, XRD, BEI imaging, SEM, ESEM, FTIR, ICP-OES and electrochemical test; then selected the optimum composition for in vitro and in vivo experiments; • Mimicked the degradation behavior of the Zn-Li alloy in vitro using simulated body fluid (SBF) and explored the relations between corrosion rate, corrosion products and surface morphology with changing compositions; • Explanted the Zn-Li alloy wire in abdominal aorta of rat over 12 months and studied its degradation mechanism, rate of bioabsorption, cytotoxicity and corrosion product migration from histological analysis.
Properties, weldability and corrosion behavior of supermartensitic stainless steels for on- and offshore applications

International Nuclear Information System (INIS)

Taban, Emel; Kaluc, Erdinc; Ojo, Olatunji Oladimeji

2016-01-01

Stimulated material-environment interactions inside and around flowlines of deep or ultra deep wells during oil and gas exploration, and fabrication economy of pipelines have been the major challenges facing the oil and gas industries. Presumably, an extensive focus on high integrity, performance and material economy of flowlines have realistically made supermartensitic stainless steels (SMSS) efficient and effective material choices for fabricating onshore and offshore pipelines. Supermartensitic stainless steels exhibit high strength, good low temperature toughness, sufficient corrosion resistance in sweet and mildly sour environments, and good quality weldability with both conventional welding processes and modern welding methods such as laser beam welding, electron beam welding and hybrid welding approaches. In terms of economy, supermartensitic stainless steels are cheaper and they are major replacements for more expensive duplex stainless steels required for tubing applications in the oil and gas industry. However, weld areas of SMSS pipes are exposed to sulphide stress cracking (SSC), so intergranular stress corrosion cracking (IGSCC) or stress corrosion cracking can occur. In order to circumvent this risk of cracking, a post-weld heat treatment (PWHT) for 5 minutes at about 650 C is recommended. This paper provides detailed literature perusal on supermartensitic stainless steels, their weldability and corrosion behaviors. It also highlights a major research area that has not been thoroughly expounded in literature; fatigue loading behaviors of welded SMSS under different corrosive environments have not been thoroughly detailed in literature.
Influence of Element Substitution on Corrosion Behavior of Bi2Te3-Based Compounds

Science.gov (United States)

Kohri, Hitoshi; Yagasaki, Takayoshi

2018-02-01

Atmospheric water may condense on the surface of Bi2Te3-based compounds constituting the Peltier module, depending on the operating environment used. In the stage of disposal, Bi2Te3-based compounds may come into contact with water in waste disposal sites. There are very few publications about the influence of condensed water on Peltier modules. Bi2Te3-Sb2Te3 or Bi2Te3-Bi2Se3 pseudo binary system compounds are used as p-type material or n-type material, respectively. The lattice distortion will be induced in the crystal of Bi2Te3-based compounds by element substitution due to the reduction in their thermal conductivity. However, the influence of element substitution on the corrosion behavior of Bi2Te3-based compounds remains unclear. In this study, the influence of element substitution on the corrosion behavior of Bi2Te3-based compounds with practical compositions has been investigated. Bi0.5Sb1.5Te3 or Bi2Te2.85Se0.15 was prepared by the vertical Bridgman method. The electrochemical properties at room temperature were evaluated by cyclic voltammetry in a standard three-electrode cell. The working electrolyte was a naturally aerated 0.6 or 3.0 mass% NaCl solution. From the tendency for corrosion potential for all the samples, the corrosion sensitivity of ternary compounds was slightly higher than that of binary compounds. From the trend of current density, it was found that Bi0.5Sb1.5Te3 had a corrosion resistance intermediate between Bi2Te3 and Sb2Te3. On the other hand, corrosion resistance was affected despite a small amount of Se substitution, and the corrosion resistance of Bi2Te2.85Se0.15 was close to or lower than that of Bi2Se3. From the observation results of the corrosion products, the trends of morphology and composition of corrosion products for Bi0.5Sb1.5Te3 or Bi2Te2.85Se0.15 were consistent with those of Sb2Te3 or Bi2Se3, respectively. From the results of x-ray photoelectron spectroscopy for the electrolyte after testing, the possibility that a
Influence of Element Substitution on Corrosion Behavior of Bi2Te3-Based Compounds

Science.gov (United States)

Kohri, Hitoshi; Yagasaki, Takayoshi

2018-06-01

Atmospheric water may condense on the surface of Bi2Te3-based compounds constituting the Peltier module, depending on the operating environment used. In the stage of disposal, Bi2Te3-based compounds may come into contact with water in waste disposal sites. There are very few publications about the influence of condensed water on Peltier modules. Bi2Te3-Sb2Te3 or Bi2Te3-Bi2Se3 pseudo binary system compounds are used as p-type material or n-type material, respectively. The lattice distortion will be induced in the crystal of Bi2Te3-based compounds by element substitution due to the reduction in their thermal conductivity. However, the influence of element substitution on the corrosion behavior of Bi2Te3-based compounds remains unclear. In this study, the influence of element substitution on the corrosion behavior of Bi2Te3-based compounds with practical compositions has been investigated. Bi0.5Sb1.5Te3 or Bi2Te2.85Se0.15 was prepared by the vertical Bridgman method. The electrochemical properties at room temperature were evaluated by cyclic voltammetry in a standard three-electrode cell. The working electrolyte was a naturally aerated 0.6 or 3.0 mass% NaCl solution. From the tendency for corrosion potential for all the samples, the corrosion sensitivity of ternary compounds was slightly higher than that of binary compounds. From the trend of current density, it was found that Bi0.5Sb1.5Te3 had a corrosion resistance intermediate between Bi2Te3 and Sb2Te3. On the other hand, corrosion resistance was affected despite a small amount of Se substitution, and the corrosion resistance of Bi2Te2.85Se0.15 was close to or lower than that of Bi2Se3. From the observation results of the corrosion products, the trends of morphology and composition of corrosion products for Bi0.5Sb1.5Te3 or Bi2Te2.85Se0.15 were consistent with those of Sb2Te3 or Bi2Se3, respectively. From the results of x-ray photoelectron spectroscopy for the electrolyte after testing, the possibility that a
Effect of Sn addition on the corrosion behavior of Ti-7Cu-Sn cast alloys for biomedical applications.

Science.gov (United States)

Tsao, L C

2015-01-01

The aim of this study was to investigate the effects of Sn content on the microstructure and corrosion resistance of Ti7CuXSn (x=0-5 wt.%) samples. The corrosion tests were carried out in 0.9 wt.% NaCl solution at 25 °C. The electrochemical corrosion behavior of the Ti7CuXSn alloy samples was evaluated using potentiodynamic polarization curves, electrochemical impedance spectroscopy (EIS), and equivalent circuit analysis. The resulting impedance parameters and polarization curves showed that adding Sn improved the electrochemical corrosion behavior of the Ti7CuXSn alloy. The Ti7CuXSn alloy samples were composed of a dual-layer oxide consisting of an inner barrier layer and an outer porous layer. Copyright © 2014 Elsevier B.V. All rights reserved.
The effect of various deformation processes on the corrosion behavior of casing and tubing carbon steels in sweet environment

Science.gov (United States)

Elramady, Alyaa Gamal

The aim of this research project is to correlate the plastic deformation and mechanical instability of casing steel materials with corrosion behavior and surface change, in order to identify a tolerable degree of deformation for casing steel materials. While the corrosion of pipeline and casing steels has been investigated extensively, corrosion of these steels in sweet environments with respect to plastic deformation due to bending, rolling, autofrettage, or handling needs more investigation. Downhole tubular expansion of pipes (casings) is becoming standard practice in the petroleum industry to repair damaged casings, shutdown perforations, and ultimately achieve mono-diameter wells. Tubular expansion is a cold-drawing metal forming process, which consists of running conical mandrels through casings either mechanically using a piston or hydraulically by applying a back pressure. This mechanism subjects the pipes to large radial plastic deformations of up to 30 pct. of the inner diameter. It is known that cold-working is a way of strengthening materials such as low carbon steel, but given that this material will be subjected to corrosive environments, susceptibility to stress corrosion cracking (SCC) should be investigated. This research studies the effect of cold-work, in the form of cold-rolling and cold-expansion, on the surface behavior of API 5CT steels when it is exposed to a CO2-containing environment. Cold-work has a pronounced influence on the corrosion behavior of both API 5CT K55 and P110 grade steels. The lowest strength grade steel, API 5CT K55, performed poorly in a corrosive environment in the slow strain rate test. The ductile material exhibited the highest loss in strength and highest susceptibility to stress corrosion cracking in a CO 2-containing environment. The loss in strength declined with cold-rolling, which can be ascribed to the surface compressive stresses induced by cold-work. On the other hand, API 5CT P110 grade steels showed higher
Strength and corrosion behavior of SiC - based ceramics in hot coal combustion environments

Energy Technology Data Exchange (ETDEWEB)

Breder, K.; Parten, R.J. [Oak Ridge National Lab., TN (United States)

1996-08-01

As part of an effort to evaluate the use of advanced ceramics in a new generation of coal-fired power plants, four SiC-based ceramics have been exposed to corrosive coal slag in a laboratory furnace and two pilot scale combustors. Initial results indicate that the laboratory experiments are valuable additions to more expensive pilot plant experiments. The results show increased corrosive attack with increased temperature, and that only slight changes in temperature may significantly alter the degree of strength degradation due to corrosive attack. The present results are part of a larger experimental matrix evaluating the behavior of ceramics in the coal combustion environment.
Effect of Nb on the Microstructure, Mechanical Properties, Corrosion Behavior, and Cytotoxicity of Ti-Nb Alloys.

Science.gov (United States)

Han, Mi-Kyung; Kim, Jai-Youl; Hwang, Moon-Jin; Song, Ho-Jun; Park, Yeong-Joon

2015-09-09

In this paper, the effects of Nb addition (5-20 wt %) on the microstructure, mechanical properties, corrosion behavior, and cytotoxicity of Ti-Nb alloys were investigated with the aim of understanding the relationship between phase/microstructure and various properties of Ti-xNb alloys. Phase/microstructure was analyzed using X-ray diffraction (XRD), SEM, and TEM. The results indicated that the Ti-xNb alloys (x = 10, 15, and 20 wt %) were mainly composed of α + β phases with precipitation of the isothermal ω phase. The volume percentage of the ω phase increased with increasing Nb content. We also investigated the effects of the alloying element Nb on the mechanical properties (including Vickers hardness and elastic modulus), oxidation protection ability, and corrosion behavior of Ti-xNb binary alloys. The mechanical properties and corrosion behavior of Ti-xNb alloys were found to be sensitive to Nb content. These experimental results indicated that the addition of Nb contributed to the hardening of cp-Ti and to the improvement of its oxidation resistance. Electrochemical experiments showed that the Ti-xNb alloys exhibited superior corrosion resistance to that of cp-Ti. The cytotoxicities of the Ti-xNb alloys were similar to that of pure titanium.
Corrosion behavior of amorphous and crystalline Cu50Ti50 and Cu50Zr50 alloys

International Nuclear Information System (INIS)

Naka, M.; Hoshimoto, K.; Masumoto, T.

1978-01-01

Corrosion rates and anodic polarization curves of amorphous and crystalline Cu 50 Ti 50 and Cu 50 Zr 50 alloys have been examined in various acidic, neutral and alkaline solutions. The amorphous alloys are very stable in acidic and alkaline solutions, but unstable in agressive chloride solutions. The corrosion resistance of these amorphous alloys is higher than that of the crystallized alloys. The high corrosion resistance of amorphous alloys is attributable to the high chemical homogeneity of amorphous alloys without localized crystalline defects such as precipitates, segregates, grain boundaries, etc. Metalloid elements play an important role in the corrosion behavior of amorphous alloys; the addition of phosphorus to amorphous Cu-Ti alloy greatly increases the corrosion resistance, even in 1N HCl. (Auth.)
Corrosion behavior of a self-sealing pore micro-arc oxidation film on AM60 magnesium alloy

International Nuclear Information System (INIS)

Dong, Kaihui; Song, Yingwei; Shan, Dayong; Han, En-Hou

2015-01-01

Highlights: • Pore sealing constituents fall off and titanium oxides remain during corrosion. • Dark regions of film are corroded by migration of corrosion media through pores. • Light regions of film are corroded by transverse expansion of cracks. • Both outer and inner layers of the film provide effective protection to substrate. - Abstract: The deterioration process of a self-sealing pore micro-arc oxidation (MAO) film was investigated. The surface and cross-section corrosion morphologies were observed by scanning electron microscopy (SEM). Chemical composition was detected by EDS elemental mapping and XRD. The corrosion process was analyzed by electrochemical impedance spectroscopy (EIS). The surface of the film in dark and light regions exhibits different corrosion behavior. In the dark regions, the corrosion process mainly concentrates on the migration of corrosion media through the pores inward. In the light regions, the transverse expansion of cracks plays a key role, accompanying the exfoliation of film constituents.
Corrosion behavior of Si-enriched steels for nuclear applications in liquid lead–bismuth

Energy Technology Data Exchange (ETDEWEB)

Kurata, Yuji, E-mail: kurata.yuji@jaea.go.jp [Japan Atomic Energy Agency, Tokai-mura, Ibaraki-ken 319-1195 (Japan)

2013-06-15

Highlights: ► The corrosion behavior of Si-enriched steels in liquid lead–bismuth was studied. ► The corrosion tests were conducted at the two controlled oxygen levels. ► The Si addition reduces the scale thickness under the high oxygen condition. ► The Si addition has no significant effect under the low oxygen condition. -- Abstract: The corrosion behavior of Si-enriched steels in liquid lead–bismuth was studied in order to develop accelerator driven systems for transmutation of long-lived radioactive wastes and lead–bismuth cooled fast reactors. The corrosion tests of 316SS, Si-enriched 316SS, Mod.9Cr–1Mo steel (T91) and Si-enriched T91 were conducted at 550 °C in liquid lead–bismuth at the two controlled oxygen levels. Both the additions of 2.5 wt.% Si to 316SS and 1.5 wt.% Si to T91 had the effect of reducing the thickness of oxide layer in liquid lead–bismuth at the high oxygen concentration (2.5 × 10{sup −5} wt.%). Although the Si addition to 316SS reduced the depth of ferritization caused by Ni dissolution in liquid lead–bismuth at the low oxygen concentration (4.4 × 10{sup −8} wt.%), it could not suppress the ferritization and the penetration of Pb and Bi completely. The Si addition to T91 did not have the effect of preventing the penetration of Pb and Bi in the liquid lead–bismuth at the low oxygen concentration. The oxide scales formed on both Si-enriched steels did not have sufficient corrosion resistance under the low oxygen condition.
Electrochemical approach to corrosion behavior of ferritic steels in Flibe melt

International Nuclear Information System (INIS)

Nishimura, H.; Suzuki, A.; Terai, T.; Kondo, M.; Sagara, A.; Noda, N.

2007-01-01

Full text of publication follows: A mixture of LiF-BeF 2 , Flibe, is considered as a candidate material for tritium breeding in a fusion liquid blanket. Flibe has favorable characteristics such as high chemical stability and low electric conductivity. However, it produces TF with neutron irradiation, which is corrosive to structural materials. Therefore, the compatibility of structural materials with Flibe is a critical issue. Up to the present, the compatibility of some materials with Flibe was examined by carrying out simple immersion tests under limited conditions. By visual observations and analyses such as XRD on the surfaces after washing out Flibe from specimens, it was found that ferritic steels seemed to have good compatibility. However, strictly speaking, surface condition of the specimens should not be same as that during immersion in melt because these specimens were subjected to heat treatments and washing processes in order to remove solidified Flibe. Therefore, we planed electrochemical experiment to observe corrosion behavior during immersion. In this study, by carrying out cyclic voltammetry on specimens to observe alteration of surface condition of specimen in Flibe melt from moment to moment, the compatibility of ferritic steel with Flibe melt was discussed on. JLF-1 JOYO-II heat ferritic steel (Fe-9.000r-1.98W-0.09C-0.49Mn-0.20V-0.083Ta) which is a candidate low activation ferritic steel as a structural material of fusion reactor was chosen as a test specimen. Fe-9Cr and Fe-2W alloys were also chosen for comparison. The size of all specimens was 20 x 10 x 1 mm. A electrochemical cell was assembled using these specimens as working electrodes. Pt was chosen as a material for quasi-reference electrode. A Ni crucible which was the container of electrolyte, Flibe, was used as a counter electrode. 600 grams of Flibe was prepared and purified by HF/H 2 bubbling before being filled in the Ni crucible. Each specimen was dunked into Flibe at 773, 823 and
Effect of H2O2 on the corrosion behavior of 304L stainless steel

International Nuclear Information System (INIS)

Song, Taek Ho

1994-02-01

In connection with the safe storage of high level nuclear waste, effect of H 2 O 2 on the corrosion behavior of 304L stainless steel was examined. Open circuit potentials and polarization curves were measured with and without H 2 O 2 . The experimental results show that H 2 O 2 increased corrosion potential and decreased pitting potential. The passive range, therefore, decreased as H 2 O 2 concentration increased, indicating that pitting resistance was decreased by the existence of H 2 O 2 in the electrolyte. These effects of H 2 O 2 on corrosion of 304L stainless steel are considered to be similar to those of γ-irradiation. To compare the effects of H 2 O 2 with those of O 2 , cathodic and anodic polarization curves were made in three types of electrolyte such as aerated, deaerated, and stirred electrolyte. The experimental results show that the effects of H 2 O 2 on the corrosion behavior were very similar to those of O 2 such as increase of corrosion potential, decrease of pitting resistance, and increase of repassivation potential. Further, H 2 O 2 played much greater role in controlling cathodic reaction rate in neutral water environment. In acid and alkaline media, potential shifts by H 2 O 2 were restricted by the large current density of proton reduction and by the le Chatelier's principle respectively
Corrosion behavior in high heat input welded heat-affected zone of Ni-free high-nitrogen Fe–18Cr–10Mn–N austenitic stainless steel

International Nuclear Information System (INIS)

Moon, Joonoh; Ha, Heon-Young; Lee, Tae-Ho

2013-01-01

The pitting corrosion and interphase corrosion behaviors in high heat input welded heat-affected zone (HAZ) of a metastable high-nitrogen Fe–18Cr–10Mn–N austenitic stainless steel were explored through electrochemical tests. The HAZs were simulated using Gleeble simulator with high heat input welding condition of 300 kJ/cm and the peak temperature of the HAZs was changed from 1200 °C to 1350 °C, aiming to examine the effect of δ-ferrite formation on corrosion behavior. The electrochemical test results show that both pitting corrosion resistance and interphase corrosion resistance were seriously deteriorated by δ-ferrite formation in the HAZ and their aspects were different with increasing δ-ferrite fraction. The pitting corrosion resistance was decreased by the formation of Cr-depleted zone along δ-ferrite/austenite (γ) interphase resulting from δ-ferrite formation; however it didn't depend on δ-ferrite fraction. The interphase corrosion resistance depends on the total amount of Cr-depleted zone as well as ferrite area and thus continuously decreased with increasing δ-ferrite fraction. The different effects of δ-ferrite fraction on pitting corrosion and interphase corrosion were carefully discussed in terms of alloying elements partitioning in the HAZ based on thermodynamic consideration. - Highlights: • Corrosion behavior in the weld HAZ of high-nitrogen austenitic alloy was studied. • Cr 2 N particle was not precipitated in high heat input welded HAZ of tested alloy. • Pitting corrosion and interphase corrosion show a different behavior. • Pitting corrosion resistance was affected by whether or not δ-ferrite forms. • Interphase corrosion resistance was affected by the total amount of δ-ferrite
Study of the corrosion behavior and the corrosion films formed on the surfaces of Mg–xSn alloys in 3.5 wt.% NaCl solution

International Nuclear Information System (INIS)

Wang, Jingfeng; Li, Yang; Huang, Song; Zhou, Xiaoen

2014-01-01

Highlights: • Corrosion of four cast Mg–xSn alloys in 3.5 wt.% NaCl solution was investigated. • Both Mg(OH) 2 /SnO 2 corrosion product film and Mg(OH) 2 /MgSnO 3 clusters formed on Mg–1.5Sn. • Compact Mg(OH) 2 /MgSnO 3 film suppressed the cathodic effect of the impurity inclusions. • Mg–xSn (x = 0.5, 1.0, 2.0 wt.%) alloys only formed loose Mg(OH) 2 /SnO 2 corrosion product film. - Abstract: The corrosion behavior and the corrosion films formed on the surfaces of Mg–xSn (x = 0.5, 1.0, 1.5, and 2.0 wt.%) alloys in 3.5 wt.% NaCl solution were investigated by immersion tests, electrochemical measurements, corrosion morphology observations, and X-ray diffraction analysis. Immersion tests and electrochemical measurements illustrated that the best corrosion resistance was reported for the Mg–1.5Sn alloy. Both Mg(OH) 2 /SnO 2 corrosion product film and Mg(OH) 2 /MgSnO 3 clusters formed on Mg–1.5Sn alloy surface. Mg(OH) 2 /MgSnO 3 clusters were compact and suppressed the cathodic effect of the impurity inclusions greatly. The Mg–xSn (x = 0.5, 1.0, and 2.0 wt.%) alloys only formed loose Mg(OH) 2 /SnO 2 corrosion product film during the corrosion process
Slow positron beam study of corrosion behavior of AM60B magnesium alloy in NaCl solution

International Nuclear Information System (INIS)

Yang, W.; Zhu, Z.J.; Wang, J.J.; Wu, Y.C.; Zhai, T.; Song, G.-L.

2016-01-01

Highlights: • Positron annihilation is a sensitive tool to characterize the corrosion layer. • The interfacial voids promoted the formation of Mg(OH) 2 corrosion layer. • Mg(OH) 2 precipitated during early corrosion stage provided a temporary protection. - Abstract: The corrosion behavior of super vacuum die-cast AM60B magnesium alloys immersed in a 5 wt% NaCl solution was investigated by slow positron beam technique, XRD, XPS, SEM and potentiodynamic polarization tests. The XRD and XPS results indicated that Mg(OH) 2 was main corrosion product in the salt solution. With prolonging the immersion time, a significant decrease of Doppler-broadened annihilation line-width parameter near the surface after corrosion was observed and interpreted that the pre-existing interfacial voids between oxide film and matrix might promote the formation of Mg(OH) 2 corrosion layer. Polarization tests found that Mg(OH) 2 could provide a temporary protection.
Testing of degradation of alloy 800 H in impure helium at 760 °C

Czech Academy of Sciences Publication Activity Database

Berka, J.; Vilémová, Monika; Sajdl, P.

2015-01-01

Roč. 464, September (2015), s. 221-229 ISSN 0022-3115 Institutional support: RVO:61389021 Keywords : High temperature corrosion * impure helium * 800 H * Generation IV nuclear reactors Subject RIV: JF - Nuclear Energetics OBOR OECD: Nuclear related engineering Impact factor: 2.199, year: 2015 http://www.sciencedirect.com/science/article/pii/S0022311515002019#
Electrical insulation characteristics of liquid helium under high speed rotating field

International Nuclear Information System (INIS)

Ishii, I.; Fuchino, S.; Okano, M.; Tamada, N.

1996-01-01

Electrical breakdown behavior of liquid helium was investigated under high speed rotating field. In the development of superconducting turbine generator it is essential to get the knowledge of electrical insulation characteristics of liquid helium under high speed rotating field. When the current of the field magnet of a superconducting generator is changed, changing magnetic field generates heat in the conductor and it causes bubbles in the liquid helium around the conductor. The behavior of the bubbles is affected largely by the buoyancy which is generated by the centrifugal force. Electrical breakdown behavior of the liquid helium is strongly dependent on the gas bubbles in the liquid. Electrical breakdown voltage between electrodes was measured in a rotating cryostat with and without heater input for bubble formation. Decrease of the breakdown voltage by the heater power was smaller in the rotating field than that in the non rotating field

Corrosion Behavior of Cu40Zn in Sulfide-Polluted 3.5% NaCl Solution

Science.gov (United States)

Song, Q. N.; Xu, N.; Bao, Y. F.; Jiang, Y. F.; Gu, W.; Yang, Z.; Zheng, Y. G.; Qiao, Y. X.

2017-10-01

The corrosion behavior of a duplex-phase brass Cu40Zn in clean and sulfide-polluted 3.5% NaCl solutions was investigated by conducting electrochemical and gravimetric measurements. The corrosion product films were analyzed by scanning electron microscopy, energy-dispersive spectroscopy and x-ray diffraction. The presence of sulfide shifted the corrosion potential of Cu40Zn toward a more negative value by 100 mV and increased the mass loss rate by a factor of 1.257 compared with the result in the clean solution. The corrosion product film in the clean solution was thin and compact; it mainly consisted of oxides, such as ZnO and Cu2O. By contrast, the film in the sulfide-polluted solution was thick and porous. It mainly contained sulfides and zinc hydroxide chloride (i.e., Zn5(OH)8Cl2·H2O). The presence of sulfide ions accelerated the corrosion damage of Cu40Zn by hindering the formation of protective oxides and promoting the formation of a defective film which consisted of sulfides and hydroxide chlorides.
Nitinol: Tubing versus sputtered film - microcleanliness and corrosion behavior.

Science.gov (United States)

Wohlschlögel, Markus; Lima de Miranda, Rodrigo; Schüßler, Andreas; Quandt, Eckhard

2016-08-01

Corrosion behavior and microcleanliness of medical-device grade Nitinol tubing (Nix Ti1- x , x = 0.51; outer diameter 7 mm, wall thickness 0.5 mm), drawn from various ingot qualities, are compared to the characteristics of sputtered Nitinol film material (Nix Ti1- x , x = 0.51; thickness 50 µm). Electropolished tubing half-shell samples are tested versus as-received sputtered film samples. Inclusion size distributions are assessed using quantitative metallography and corrosion behavior is investigated by potentiodynamic polarization testing in phosphate-buffered saline at body temperature. For the sputtered film samples, the surface chemistry is additionally analyzed employing Auger Electron Spectroscopy (AES) composition-depth profiling. Results show that the fraction of breakdowns in the potentiodynamic polarization test correlates with number and size of the inclusions in the material. For the sputtered Nitinol film material no inclusions were detectable by light microscopy on the one hand and no breakdowns were found in the potentiodynamic polarization test on the other hand. As for electropolished Nitinol, the sputtered Nitinol film material reveals Nickel depletion and an Oxygen-to-Titanium intensity ratio of ∼2:1 in the surface oxide layer, as measured by AES. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 104B: 1176-1181, 2016. © 2015 Wiley Periodicals, Inc.
Corrosion of beryllium

International Nuclear Information System (INIS)

Mueller, J.J.; Adolphson, D.R.

1987-01-01

The corrosion behavior of beryllium in aqueous and elevated-temperature oxidizing environments has been extensively studied for early-intended use of beryllium in nuclear reactors and in jet and rocket propulsion systems. Since that time, beryllium has been used as a structural material in les corrosive environments. Its primary applications include gyro systems, mirror and reentry vehicle structures, and aircraft brakes. Only a small amount of information has been published that is directly related to the evaluation of beryllium for service in the less severe or normal atmospheric environments associated with these applications. Despite the lack of published data on the corrosion of beryllium in atmospheric environments, much can be deduced about its corrosion behavior from studies of aqueous corrosion and the experiences of fabricators and users in applying, handling, processing, storing, and shipping beryllium components. The methods of corrosion protection implemented to resist water and high-temperature gaseous environments provide useful information on methods that can be applied to protect beryllium for service in future long-term structural applications
Investigation of corrosion behavior of nitrogen doped and platinum/ruthenium doped diamond-like carbon thin films in Hank's solution

International Nuclear Information System (INIS)

Khun, N.W.; Liu, E.

2011-01-01

Undoped (DLC), nitrogen-doped (N-DLC) and platinum/ruthenium doped diamond-like carbon (PtRu-DLC) thin films were deposited on p-Si (100) substrates using a DC magnetron sputtering deposition system. The chemical composition, bonding structure, surface morphology and adhesion strength of the films were characterized using X-ray photoelectron spectroscopy (XPS), micro-Raman spectroscopy, atomic force microscopy (AFM) and micro-scratch test, respectively. The corrosion behavior of the films in a Hank's solution was investigated using potentiodynamic polarization test. The corrosion results revealed that the PtRu-DLC film had the highest corrosion potential among the films used in this study. Highlights: → DLC thin films were deposited on Si substrates via dc magnetron sputtering. → Some DLC films were doped with N and/or Pt/Ru. → The film corrosion behavior was studied in a Hank solution with polarization test. → The PtRu-DLC film showed the highest corrosion potential among the films studied.
Corrosion behavior of dental alloys used for retention elements in prosthodontics.

Science.gov (United States)

Nierlich, Judith; Papageorgiou, Spyridon N; Bourauel, Christoph; Hültenschmidt, Robert; Bayer, Stefan; Stark, Helmut; Keilig, Ludger

2016-06-01

The purpose of this study was to investigate the corrosion behavior of 10 different high noble gold-based dental alloys, used for prosthodontic retention elements, according to ISO 10271. Samples of 10 high-noble and noble gold-based dental alloys were subjected to: (i) static immersion tests with subsequent analysis of ion release for eight different elements using mass spectrometry; (ii) electrochemical tests, including open-circuit potential and potentiodynamic scans; and (iii) scanning electron microscopy, followed by energy-dispersive X-ray microscopy. The results were analyzed using one-way ANOVA and Sidak multiple-comparisons post-hoc test at a level of significance of α = 0.05. Significant differences were found among the 10 alloys studied for all ions (P alloys. Scanning electron microscopy analysis confirmed the existence of typically small-diameter corrosion defects, whilst the energy-dispersive X-ray analysis found no significant alteration in the elemental composition of the alloys. The results of this study reveal the variability in the corrosive resistance among the materials used for retention elements in prosthodontics. © 2016 Eur J Oral Sci.
Corrosion behavior of sodium-exposed stainless steels in chloride-containing aqueous solutions

International Nuclear Information System (INIS)

Wu, P.C.S.; Grundy, B.R.; Miller, R.L.

1979-01-01

The corrosion behavior of sodium-exposed stainless steels in chloride-containing aqueous solutions was investigated. Results showed that sodium-corroded Type 316 stainless steel (prototypic Liquid Metal Fast Breeder Reactor (LMFBR) fuel cladding) maintains its integrity after five months exposure in these solutions at 82 0 C and with chloride content up to 500 ppM. In contrast, sensitized and sodium mass transfer deposit-containing Type 304 stainless steel failed in the high chloride solution (500 ppM) within ten days at the same temperature. The failure was initiated by pitting and subsequently accelerated by intergranular attack. The results also show that high pH tends to reduce the susceptibility to failure while procedures commonly used for sodium removal have no significant effect on the water corrosion behavior of the test material. Based on the current results, it is concluded that water shortage is feasible for spent fuels in a LMFBR reprocessing plant
Tribological behavior of zirconium coatings in high temperature helium

International Nuclear Information System (INIS)

Cachon, Lionel; Albaladejo, Serge; Taraud, Pascal

2005-01-01

In France, a comprehensive research and development program is leaded by the CEA, since 2001, for the Gas Cooled Reactor (GCR) project using helium as cooling fluid, in order to establish the feasibility of the technology of an early VHTR prototype to be started by 2015, and then to qualify the generic VHTR technology, so as to meet similar objectives for the GFR. In this frame a tribology program has been launched. The purpose of the work presented in this paper is to describe the CEA Helium tribology study: high temperature gas cooled reactors require wear protection (thermal barriers, control rod drive mechanisms, reactor internals, ...). Tests in helium atmosphere are necessary to be fully representative of tribological environments and finally to check the possible materials or coatings which can provide a reliable answer to these situations. The main characteristics and first experimental results are thus described. This paper focus on tribology tests leaded in the temperature range 800-1000degC, on ceramic (ZrO 2 -Y 2 O 3 ) with and without solid lubricant like CaF2). (author)
Corrosion Behavior in 3.5% NaCl Solutions of γ-TiAl Processed by Electron Beam Melting Process

Directory of Open Access Journals (Sweden)

Asiful Hossain Seikh

2015-12-01

Full Text Available In this work, the corrosion behavior of γ-TiAl alloy produced by electron beam melting (EBM process in 3.5% NaCl solution was reported. The study has been performed using potentiodynamic polarization resistance and electrochemical impedance spectroscopy techniques and complemented by scanning electron microscopy investigations. All measurements were carried out after different periods of alloy exposure in the chloride solutions and at different temperatures. The results showed that the EBM produced γ-TiAl alloy has excellent corrosion resistance confirmed by the high values of polarization resistance and the low values of corrosion current and corrosion rate. With increase in immersion time, the corrosion potential moved to a higher positive value with a decrease in corrosion current and corrosion rate, which suggests an improvement in corrosion resistance. On the other hand, the increase of temperature was found to significantly increase the corrosion of the processed γ-TiAl alloy.
Atmospheric Corrosion Behavior and Mechanism of a Ni-Advanced Weathering Steel in Simulated Tropical Marine Environment

Science.gov (United States)

Wu, Wei; Zeng, Zhongping; Cheng, Xuequn; Li, Xiaogang; Liu, Bo

2017-12-01

Corrosion behavior of Ni-advanced weathering steel, as well as carbon steel and conventional weathering steel, in a simulated tropical marine atmosphere was studied by field exposure and indoor simulation tests. Meanwhile, morphology and composition of corrosion products formed on the exposed steels were surveyed through scanning electron microscopy, energy-dispersive x-ray spectroscopy and x-ray diffraction. Results indicated that the additive Ni in weathering steel played an important role during the corrosion process, which took part in the formation of corrosion products, enriched in the inner rust layer and promoted the transformation from loose γ-FeOOH to dense α-FeOOH. As a result, the main aggressive ion, i.e., Cl-, was effectively separated in the outer rust layer which leads to the lowest corrosion rate among these tested steels. Thus, the resistance of Ni-advanced weathering steel to atmospheric corrosion was significantly improved in a simulated tropical marine environment.
Theoretical and experimental investigation of magnetic field related helium leak in helium vessel of a large superconducting magnet

Science.gov (United States)

Bhattachryya, Pranab; Gupta, Anjan Dutta; Dhar, S.; Sarma, P. R.; Mukherjee, Paramita

2017-06-01

The helium vessel of the superconducting cyclotron (SCC) at the Variable Energy Cyclotron centre (VECC), Kolkata shows a gradual loss of insulation vacuum from 10-7 mbar to 10-4 mbar with increasing coil current in the magnet. The insulation vacuum restores back to its initial value with the withdrawal of current. The origin of such behavior has been thought to be related to the electromagnetic stress in the magnet. The electromagnetic stress distribution in the median plane of the helium vessel was studied to figure out the possible location of the helium leak. The stress field from the possible location was transferred to a simplified 2D model with different leak geometries to study the changes in conductance with coil current. The leak rate calculated from the changes in the leak geometry was compared with the leak rate calculated from the experimental insulation vacuum degradation behavior to estimate the initial leak shape and size.
Prediction of metal corrosion using feed-forward neural networks

International Nuclear Information System (INIS)

Mahjani, M.G.; Jalili, S.; Jafarian, M.; Jaberi, A.

2004-01-01

The reliable prediction of corrosion behavior for the effective control of corrosion is a fundamental requirement. Since real world corrosion never seems to involve quite the same conditions that have previously been tested, using corrosion literature does not provide the necessary answers. In order to provide a methodology for predicting corrosion in real and complex situations, artificial neural networks can be utilized. Feed-forward artificial neural network (FFANN) is an information-processing paradigm inspired by the way the densely interconnected, parallel structure of the human brain process information.The aim of the present work is to predict corrosion behavior in critical conditions, such as industrial applications, based on some laboratory experimental data. Electrochemical behavior of stainless steel in different conditions were studied, using polarization technique and Tafel curves. Back-propagation neural networks models were developed to predict the corrosion behavior. The trained networks result in predicted value in good comparison to the experimental data. They have generally been claimed to be successful in modeling the corrosion behavior. The results are presented in two tables. Table 1 gives corrosion behavior of stainless-steel as a function of pH and CuSO 4 concentration and table 2 gives corrosion behavior of stainless - steel as a function of electrode surface area and CuSO 4 concentration. (authors)
The Corrosion Behavior of Stainless Steel 316L in Novel Quaternary Eutectic Molten Salt System

Science.gov (United States)

Wang, Tao; Mantha, Divakar; Reddy, Ramana G.

2017-03-01

In this article, the corrosion behavior of stainless steel 316L in a low melting point novel LiNO3-NaNO3-KNO3-NaNO2 eutectic salt mixture was investigated at 695 K which is considered as thermally stable temperature using electrochemical and isothermal dipping methods. The passive region in the anodic polarization curve indicates the formation of protective oxides layer on the sample surface. After isothermal dipping corrosion experiments, samples were analyzed using SEM and XRD to determine the topography, corrosion products, and scale growth mechanisms. It was found that after long-term immersion in the LiNO3-NaNO3-KNO3-NaNO2 molten salt, LiFeO2, LiFe5O8, Fe3O4, (Fe, Cr)3O4 and (Fe, Ni)3O4 oxides were formed. Among these corrosion products, LiFeO2 formed a dense and protective layer which prevents the SS 316L from severe corrosion.
Corrosion characteristics of K-claddings

International Nuclear Information System (INIS)

Park, J. Y.; Choi, B. K.; Jung, Y. H.; Jung, Y. H.

2004-01-01

The Improvement of the corrosion resistance of nuclear fuel claddings is the critical issue for the successful development of the high burn-up fuel. KAERI have developed the K-claddings having a superior corrosion resistance by controlling the alloying element addition and optimizing the manufacturing process. The comparative evaluation of the corrosion resistance for K-claddings and the foreign claddings was performed and the effect of the heat treatment on the corrosion behavior of K-claddings was also examined. Corrosion tests were carried out in the conditions of 360 .deg. C pure water, PWR-simulating loop and 400 .deg. C steam, From the results of the corrosion tests, it was found that the corrosion resistance of K-claddings is superior to those of Zry4 and A claddings and K6 showed a better corrosion resistance than K3. The corrosion behavior of K-cladding was strongly influenced by the final annealing rather than the intermediate annealing, and the corrosion resistance increased with decreasing the final annealing temperature
The Development of an In-Situ TEM Technique for Studying Corrosion Behavior as Applied to Zirconium-Based Alloys

Science.gov (United States)

Harlow, Wayne

Zirconium-based alloys are a commonly used material for nuclear fuel rod cladding, due to its low neutron cross section and good corrosion properties. However, corrosion is still a limiting factor in fuel rod lifespan, which restricts burn up levels, and thus efficiency, that can be achieved. While long-term corrosion behavior has been studied through both reactor and autoclave samples, the oxide nucleation and growth behavior has not been extensively studied. This work develops a new technique to study the initial stages of corrosion in zirconium-based alloys and the microstructural effects on this process by developing an environmental cell system for the TEM. Nanoscale oxidation parameters are developed, as is a new FIB technique to support this method. Precession diffraction is used in conjunction with in-situ TEM to observe the initial stages of corrosion in these alloys, and oxide thickness is estimated using low-loss EELS. In addition, the stress stabilization of tetragonal ZrO 2 is explored in the context of sample preparation for TEM. It was found that in-situ environmental TEM using an environmental cell replicates the oxidation behavior observed in autoclaved samples in both oxide structure and phases. Utilizing this technique, it was shown that cracking of the oxide layer in zirconium-based alloys is related to oxide relaxation, and not thermal changes. The effect of secondary phase particles on oxidation behavior did not present significant results, however a new method for studying initial oxidation rates using low-loss EELS was developed.
Corrosion Behavior of X80 Steel with Coupled Coating Defects under Alternating Current Interference in Alkaline Environment.

Science.gov (United States)

Li, Zhong; Li, Caiyu; Qian, Hongchang; Li, Jun; Huang, Liang; Du, Cuiwei

2017-06-28

The corrosion behavior of X80 steel in the presence of coupled coating defects was simulated and studied under the interference of alternating current (AC) in an alkaline environment. The results from electrochemical measurements showed that the electrode potential of the coating defect with the smaller exposed area was lower than that with the larger area, which indicated that the steel with the smaller coating defect was more prone to corrosion. The result of weight loss tests also showed that the smaller coating defect had induced a higher corrosion rate. However, the corrosion rate of X80 steel at the larger coating defect decreased gradually with the increase of the larger defect area at a constant smaller defect area. The corrosion morphology images showed that the coating defects with smaller areas suffered from more severe pitting corrosion.
Comparison of the corrosion behaviors of the glass-bonded sodalite ceramic waste form and reference HLW glasses

International Nuclear Information System (INIS)

Ebert, W. L.; Lewis, M. A.

1999-01-01

A glass-bonded sodalite ceramic waste form is being developed for the long-term immobilization of salt wastes that are generated during spent nuclear fuel conditioning activities. A durable waste form is prepared by hot isostatic pressing (HIP) a mixture of salt-loaded zeolite powders and glass frit. A mechanistic description of the corrosion processes is being developed to support qualification of the CWF for disposal. The initial set of characterization tests included two standard tests that have been used extensively to study the corrosion behavior of high level waste (HLW) glasses: the Material Characterization Center-1 (MCC-1) Test and the Product Consistency Test (PCT). Direct comparison of the results of tests with the reference CWF and HLW glasses indicate that the corrosion behaviors of the CWF and HLW glasses are very similar
Hot corrosion behavior of Ni-based superalloys in lithium molten salt

International Nuclear Information System (INIS)

Cho, Soo Haeng; Lim, Jong Ho; Chung, Joon Ho; Hur, Jin Mok; Seo, Chung Seok; Park, Seoung Won

2004-01-01

The Li-reduction process involves the chemical reduction of spent fuel oxides by liquid lithium metal in a molten LiCl salt bath at 650 .deg. C followed by a separate electrochemical reduction of lithium oxide (Li 2 O), which builds up in the salt bath. This process requires a high purity inert gas atmosphere inside remote hot cell nuclear facility to prevent unwanted Li oxidation and fires during the handling of chemically active Li metal. In light of the limitations of the Li-reduction process, a direct electrolytic reduction technology is being developed by KAERI to enhance process safety and economic viability. The electrolytic reduction of spent oxide fuel involves the liberation of oxygen in a molten LiCl electrolyte, which results in a chemically aggressive environment that is too corrosive for typical structural materials. Even so, the electrochemical process vessel must be resilient at 650 .deg. C in the presence of oxygen to enable high processing rates and an extended service life. But, the mechanism and the rate of the corrosion of metals in LiCl-Li 2 O molten salt under oxidation condition are not clear. In the present work, the corrosion behavior and corrosion mechanism of Ni-based superalloys have been studied in the molten salt of LiCl-Li 2 O under oxidation condition
A review of the corrosion and pyrophoricity behavior of uranium and plutonium

International Nuclear Information System (INIS)

Totemeier, T.C.

1995-06-01

This report presents a review of the corrosion and pyrophoricity behavior of uranium and plutonium. For each element, the reactions with oxygen, water vapor, and aqueous solutions are described in terms of reaction rates, products, and mechanisms. Their pyrophoric tendencies in terms of measured ignition temperatures are discussed, and the effects of the important variables specific area, gas composition, and prior storage rare stated. The implications of the observed behavior for current storage issues are considered
Effects of cold working on the pitting corrosion behavior s of AISI 304 stainless steels

Energy Technology Data Exchange (ETDEWEB)

Jung, Kee Min; Kim, Jong Soo; Kim, Young Jun; Kwon, Houk Sang [KAIST, Daejon (Korea, Republic of)

2015-12-15

These microstructural changes by cold working can lead improvement of mechanical properties, however from a corrosion resistant point of view, the effects of cold working on the corrosion resistance of stainless steel have been argued. Several studies has been focused on the influence of cold working on the localized corrosion resistance of stainless steels. However, the opinions about the role of cold working on the localized corrosion resistance are highly in consistence. Some studies report that the pitting potential of austenitic stainless steels decreased with cold working level, on the other hands, other studies claimed that the pitting resistance was increased by cold working. Therefore it is necessary to verify how cold working affects pitting corrosion behavior of austenitic stainless steels. In the present work, the influence of cold working on the localized corrosion of AISI 304stainless steel in the neutral chloride solution was studied based on point defect model (PDM). The fraction of deformation-induced martensite was linearly increased with cold rolling level. Through cold rolling, the pitting potential was decreased, the metastable pitting event density was significantly increased and the repassivation potential was decreased. The overall localized corrosion resistance was decreased with cold working, however cold working level increased from 30 % to 50 %, localized corrosion resistance was recovered. The accumulated cation vacancy generates a void at metal/film interface, therefore film breakdown accelerates for cold worked alloys.
Effects of cold working on the pitting corrosion behavior s of AISI 304 stainless steels

International Nuclear Information System (INIS)

Jung, Kee Min; Kim, Jong Soo; Kim, Young Jun; Kwon, Houk Sang

2015-01-01

These microstructural changes by cold working can lead improvement of mechanical properties, however from a corrosion resistant point of view, the effects of cold working on the corrosion resistance of stainless steel have been argued. Several studies has been focused on the influence of cold working on the localized corrosion resistance of stainless steels. However, the opinions about the role of cold working on the localized corrosion resistance are highly in consistence. Some studies report that the pitting potential of austenitic stainless steels decreased with cold working level, on the other hands, other studies claimed that the pitting resistance was increased by cold working. Therefore it is necessary to verify how cold working affects pitting corrosion behavior of austenitic stainless steels. In the present work, the influence of cold working on the localized corrosion of AISI 304stainless steel in the neutral chloride solution was studied based on point defect model (PDM). The fraction of deformation-induced martensite was linearly increased with cold rolling level. Through cold rolling, the pitting potential was decreased, the metastable pitting event density was significantly increased and the repassivation potential was decreased. The overall localized corrosion resistance was decreased with cold working, however cold working level increased from 30 % to 50 %, localized corrosion resistance was recovered. The accumulated cation vacancy generates a void at metal/film interface, therefore film breakdown accelerates for cold worked alloys

Corrosion behavior of ion implanted nickel-titanium orthodontic wire in fluoride mouth rinse solutions.

Science.gov (United States)

Iijima, Masahiro; Yuasa, Toshihiro; Endo, Kazuhiko; Muguruma, Takeshi; Ohno, Hiroki; Mizoguchi, Itaru

2010-01-01

This study investigated the corrosion properties of ion implanted nickel-titanium wire (Neo Sentalloy Ionguard) in artificial saliva and fluoride mouth rinse solutions (Butler F Mouthrinse, Ora-Bliss). Non ion implanted nickel-titanium wire (Neo Sentalloy) was used as control. The anodic corrosion behavior was examined by potentiodynamic polarization measurement. The surfaces of the specimens were examined with SEM. The elemental depth profiles were characterized by XPS. Neo Sentalloy Ionguard in artificial saliva and Butler F Mouthrinse (500 ppm) had a lower current density than Neo Sentalloy. In addition, breakdown potential of Neo Sentalloy Ionguard in Ora-Bliss (900 ppm) was much higher than that of Neo Sentalloy although both wires had similar corrosion potential in Ora-Bliss (450 and 900 ppm). The XPS results for Neo Sentalloy Ionguard suggested that the layers consisted of TiO(2) and TiN were present on the surface and the layers may improve the corrosion properties.
The Localized Corrosion Behavior Associated with Microstructure of F53 Super Duplex Stainless Steel

International Nuclear Information System (INIS)

Kim, Soon-Tae; Lee, In-Sung; Kong, Kyeong-Ho; Park, Yong-Soo; Lee, Jong-Hoon; Yang, Won-Jon

2015-01-01

The localized corrosion behavior associated with microstructure of F53 super duplex stainless steel (SDSS) was investigated using a potentiodynamic polarization test, a critical crevice temperature test, an electron probe micro-analyzer analysis, and scanning electron microscopy-energy dispersive spectroscopy analyses. Crevice corrosion was initiated at the α/γ phase boundaries, MO x inclusions (where M is Cr, Mn, Al, Fe, or Ti), as well as Cr and Mo depleted areas adjacent to the σ-phases precipitated in the F53 SDSS alloy. This alloy had been annealed at 1050 ℃ followed by improper water-cooling, and the corrosion was propagated into the α-phases because the pitting resistance equivalent number (PREN) of the α-phase was smaller than that of the γ-phase. As cooling rate increased, the variation of the α-phases decreased, and the content of the Cr and Mo rich σ-phases decreased, thereby increasing the corrosion resistance.
The Localized Corrosion Behavior Associated with Microstructure of F53 Super Duplex Stainless Steel

Energy Technology Data Exchange (ETDEWEB)

Kim, Soon-Tae; Lee, In-Sung; Kong, Kyeong-Ho; Park, Yong-Soo [Yonsei University, Seoul (Korea, Republic of); Lee, Jong-Hoon; Yang, Won-Jon [Korea Institute of Materials Science, Changwon (Korea, Republic of)

2015-07-15

The localized corrosion behavior associated with microstructure of F53 super duplex stainless steel (SDSS) was investigated using a potentiodynamic polarization test, a critical crevice temperature test, an electron probe micro-analyzer analysis, and scanning electron microscopy-energy dispersive spectroscopy analyses. Crevice corrosion was initiated at the α/γ phase boundaries, MO{sub x} inclusions (where M is Cr, Mn, Al, Fe, or Ti), as well as Cr and Mo depleted areas adjacent to the σ-phases precipitated in the F53 SDSS alloy. This alloy had been annealed at 1050 ℃ followed by improper water-cooling, and the corrosion was propagated into the α-phases because the pitting resistance equivalent number (PREN) of the α-phase was smaller than that of the γ-phase. As cooling rate increased, the variation of the α-phases decreased, and the content of the Cr and Mo rich σ-phases decreased, thereby increasing the corrosion resistance.
Characterization and corrosion behavior of F6NM stainless steel treated in high temperature water

Science.gov (United States)

Li, Zheng-yang; Cai, Zhen-bing; Yang, Wen-jin; Shen, Xiao-yao; Xue, Guo-hong; Zhu, Min-hao

2018-03-01

F6NM martensitic stainless steel was exposed to 350 °C water condition for 500, 1500, and 2500 h to simulate pressurized water reactor (PWR) condition. The characterization and corrosion behavior of the oxide film were investigated. Results indicate that the exposed steel surface formed a double-layer oxide film. The outer oxide film is Fe-rich and contains two type oxide particles. However, the inner oxide film is Cr-rich, and two oxide films, whose thicknesses increase with increasing exposure time. The oxide film reduces the corrosion behavior because the outer oxide film has many crack and pores. Finally, the mechanism and factors affecting the formation of the oxide film were investigated.
Helium behaviour in nuclear glasses

International Nuclear Information System (INIS)

Fares, T.

2011-01-01

The present thesis focuses on the study of helium behavior in R7T7 nuclear waste glass. Helium is generated by the minor actinides alpha decays incorporated in the glass matrix. Therefore, four types of materials were used in this work. These are non radioactive R7T7 glasses saturated with helium under pressure, glasses implanted with 3 He + ions, glasses doped with curium and glasses irradiated in nuclear reactor. The study of helium solubility in saturated R7T7 glass has shown that helium atoms are inserted in the glass free volume. The results yielded a solubility of about 10 16 at. cm -3 atm. -1 . The incorporation limit of helium in this type of glass has been determined; its value amounted to about 2*10 21 at. cm -3 , corresponding to 2.5 at.%. Diffusion studies have shown that the helium migration is controlled by the single population dissolved in the glass free volume. An ideal diffusion model was used to simulate the helium release data which allowed to determine diffusion coefficients obeying to the following Arrhenius law: D = D 0 exp(-E a /kBT), where D 0 = 2.2*10 -2 and 5.4*10 -3 cm 2 s -1 and E a = 0.61 eV for the helium saturated and the curium doped glass respectively. These results reflect a thermally activated diffusion mechanism which seems to be not influenced by the glass radiation damage and helium concentrations studied in the present work (up to 8*10 19 at. g -1 , corresponding to 0.1 at.%). Characterizations of the macroscopic, structural and microstructural properties of glasses irradiated in nuclear reactor did not reveal any impact associated with the presence of helium at high concentrations. The observed modifications i.e. a swelling of 0.7 %, a decrease in hardness by 38 %, an increase between 8 and 34 % of the fracture toughness and a stabilization of the glass structure under irradiation, were attributed to the glass nuclear damage induced by the irradiation in reactor. Characterizations by SEM and TEM of R7T7 glasses implanted
Corrosion Behavior of Surface-Treated Implant Ti-6Al-4V by Electrochemical Polarization and Impedance Studies

Science.gov (United States)

Paul, Subir; Yadav, Kasturi

2011-04-01

Implant materials for orthopedic and heart surgical services demand a better corrosion resistance material than the presently used titanium alloys, where protective oxide layer breaks down on a prolonged stay in aqueous physiological human body, giving rise to localized corrosion of pitting, crevice, and fretting corrosion. A few surface treatments on Ti alloy, in the form of anodization, passivation, and thermal oxidation, followed by soaking in Hank solution have been found to be very effective in bringing down the corrosion rate as well as producing high corrosion resistance surface film as reflected from electrochemical polarization, cyclic polarization, and Electrochemical Impedance Spectroscopy (EIS) studies. The XRD study revealed the presence of various types of oxides along with anatase and rutile on the surface, giving rise to high corrosion resistance film. While surface treatment of passivation and thermal oxidation could reduce the corrosion rate by 1/5th, anodization in 0.3 M phosphoric acid at 16 V versus stainless steel cathode drastically brought down the corrosion rate by less than ten times. The mechanism of corrosion behavior and formation of different surface films is better understood from the determination of EIS parameters derived from the best-fit equivalent circuit.
Chemical and structural effects of phosphorus on the corrosion behavior of ion beam mixed Fe-Cr-P alloys

International Nuclear Information System (INIS)

Demaree, J.D.; Was, G.S.; Sorensen, N.R.

1992-01-01

An experimental program was conducted to determine the mechanisms by which phosphorus affects the corrosion and passivation behavior of Fe-Cr-P alloys. To identify separately the effects of structure and chemistry on the corrosion behavior, thin films of Fe-10Cr-xP (0≤x≤35 at.%) were prepared by ion beam mixing. Films with a phosphorus content greater than approximately 20at.% were found to be entirely amorphous. Devitrification of the amorphous phase was accomplished by heating the samples to 450degC in an inert environment. Standard polarization tests of the sulfuric acid (with and without Cl - ) indicated that the films containing phosphorus were more corrosion resistant than Fe-10Cr, at both active and passive potentials. There was a monotonic relationship between the amount of phosphorus in the alloy and the corrosion resistance, with the open-circuit corrosion rate of Fe-10Cr-35P nearly four orders of magnitude lower than that of Fe-10Cr. Devitrification of the alloys had no significant effect on the corrosion rate, indicating that the primary effect of phosphorus is chemical in nature, and not structural. The passive oxides were depth-profiled using X-ray photoelectron spectroscopy, which indicated that phosphorus was a primary constituent, as phosphate. The presence of phosphate in the passive oxides reduced the overall corrosion rate directly, by suppressing anodic dissolution. The presence of phosphorus did enhance chromium enrichment in the oxide, but that was not thought to be the primary mechanism by which phosphorus increased the corrosion resistance. (orig.)
Effect of annealing treatment on microstructure evolution and the associated corrosion behavior of a super-duplex stainless steel

International Nuclear Information System (INIS)

Deng, B.; Jiang, Y.M.; Gao, J.; Li, J.

2010-01-01

The influence of annealing temperature on the pitting corrosion of a super-duplex stainless steel (SDSS) with mischmetal addition was investigated in chloride solution by critical pitting temperature (CPT) measurement. The corrosion behavior is strongly dependent on the microstructure, namely the presence of secondary phases, elemental partitioning behavior and volume fractions of ferrite and austenite. Based on CPT results and alloying rules, the optimal annealing temperature is determined as 1070 o C and a guideline for further development of improved SDSS is formulated.
Corrosion behavior of mild steel and SS 304L in presence of dissolved nickel under aerated and deaerated conditions

Directory of Open Access Journals (Sweden)

Mohd Mobin

2011-12-01

Full Text Available In dual purpose water/power co-generation plants, the presence of high concentration of Cu and Ni in the re-circulating brine/condensate as a result of condenser tubes corrosion has been attributed as one of the several causes of corrosion damage of flash chamber materials and water touched parts of the boilers. The present investigation deals with the effect of dissolved nickel in the concentration range of 10 ppb to 100 ppm on the corrosion behavior of mild steel and SS 304L in two aqueous medium namely, distilled water and artificial seawater. The effect of pH, dissolved oxygen and flow condition of aqueous medium on the corrosion behavior was also monitored. The experimental techniques include immersion test and electrochemical tests which include free corrosion potential measurements and potentiodynamic polarization measurements. The corrosion rate of mild steel and SS 304L under different experimental conditions was determined by weight loss method and spectrophotometric determination of iron ion entered into the test solution during the period of immersion. The pH of the test solution was also monitored during the entire period of immersion. The left over nickel ions present in the test solution after completion of immersion was also estimated using Atomic Absorption Spectrophotometer. The surface morphology of the corroded steel surface was also examined using scanning electron microscopy (SEM. The results of the studies show that SS 304L largely remains unaffected in both distilled water and artificial seawater under different experimental conditions. However, the effect of nickel on the corrosion behavior of mild steel is quite pronounced and follows interesting trends.
Thermal fluid dynamic behavior of coolant helium gas in a typical reactor VHTGR channel of prismatic core

International Nuclear Information System (INIS)

Belo, Allan Cavalcante

2016-01-01

The current studies about the thermal fluid dynamic behavior of the VHTGR core reactors of 4 th generation are commonly developed in 3-D analysis in CFD (computational fluid dynamics), which often requires considerable time and complex mathematical calculations for carrying out these analysis. The purpose of this project is to achieve thermal fluid dynamic analysis of flow of gas helium refrigerant in a typical channel of VHTGR prismatic core reactor evaluating magnitudes of interest such as temperature, pressure and fluid velocity and temperature distribution in the wall of the coolant channel from the development of a computer code in MATLAB considering the flow on one-dimensional channel, thereby significantly reducing the processing time of calculations. The model uses three different references to the physical properties of helium: expressions given by the KTA (German committee of nuclear safety standards), the computational tool REFPROP and a set of constant values for the entire channel. With the use of these three references it is possible to simulate the flow treating the gas both compressible and incompressible. The results showed very close values for the interest quantities and revealed that there are no significant differences in the use of different references used in the project. Another important conclusion to be observed is the independence of helium in the gas compressibility effects on thermal fluid dynamic behavior. The study also indicated that the gas undergoes no severe effects due to high temperature variations in the channel, since this goes in the channel at 914 K and exits at approximately 1263 K, which shows the excellent use of helium as a refrigerant fluid in reactor channels VHTGR. The comparison of results obtained in this work with others in the literature served to confirm the effectiveness of the one-dimensional consideration of method of gas flow in the coolant channel to replace the models made in 3-D for the pressure range and
Effects of applying an external magnetic field during the deep cryogenic heat treatment on the corrosion resistance and wear behavior of 1.2080 tool steel

International Nuclear Information System (INIS)

Akhbarizadeh, Amin; Amini, Kamran; Javadpour, Sirus

2012-01-01

Highlights: ► Deep cryogenic increases the carbide percentage and make a more homogenous distribution. ► Deep cryogenic improve the wear resistance and corrosion behavior of 1.2080 tool steel. ► Applying the magnetic field weaker the carbide distribution and decreases the carbides percentage. ► Magnetized samples showed weaker corrosion and wear behavior. -- Abstract: This work concerns with the effect of applying an external magnetic field on the corrosion behavior, wear resistance and microstructure of 1.2080 (D2) tool steel during the deep cryogenic heat treatment. These analyses were performed via scanning electron microscope (SEM), optical microscope (OM), transmission electron microscope (TEM) and X-ay diffraction (XRD) to study the microstructure, a pin-on-disk wear testing machine to study the wear behavior, and linear sweep voltammetry to study the corrosion behavior of the samples. It was shown that the deep cryogenic heat treatment eliminates retained austenite and makes a more uniform carbide distribution with higher percentage. It was also observed that the deep cryogenic heat treatment improves the wear behavior and corrosion resistance of 1.2080 tool steel. In comparison between the magnetized and non-magnetized samples, the carbide percentage decreases and the carbide distribution weakened in the magnetized samples; subsequently, the wear behavior and corrosion resistance attenuated compared in the magnetized samples.
Irreversible adsorption of atmospheric helium on olivine: A lobster pot analogy

Science.gov (United States)

Protin, Marie; Blard, Pierre-Henri; Marrocchi, Yves; Mathon, François

2016-04-01

This study reports new experimental results that demonstrate that large amounts of atmospheric helium may be adsorbed onto the surfaces of olivine grains. This behavior is surface-area-related in that this contamination preferentially affects grains that are smaller than 125 μm in size. One of the most striking results of our study is that in vacuo heating at 900 °C for 15 min is not sufficient to completely remove the atmospheric contamination. This suggests that the adsorption of helium may involve high-energy trapping of helium through irreversible anomalous adsorption. This trapping process of helium can thus be compared to a ;lobster pot; adsorption: atmospheric helium easily gets in, but hardly gets out. While this type of behavior has previously been reported for heavy noble gases (Ar, Kr, Xe), this is the first time that it has been observed for helium. Adsorption of helium has, until now, generally been considered to be negligible on silicate surfaces. Our findings have significant implications for helium and noble gas analysis of natural silicate samples, such as for cosmic-ray exposure dating or noble gas characterization of extraterrestrial material. Analytical procedures in future studies should be adapted in order to avoid this contamination. The results of this study also allow us to propose an alternative explanation for previously described matrix loss of cosmogenic 3He.
Corrosion behavior of steels in liquid lead bismuth with low oxygen concentrations

Science.gov (United States)

Kurata, Yuji; Futakawa, Masatoshi; Saito, Shigeru

2008-02-01

Corrosion tests in pots were conducted to elucidate corrosion behavior of various steels in liquid lead-bismuth for 3000 h under the condition of an oxygen concentration of 5 × 10 -8 wt% at 450 °C and an oxygen concentration of 3 × 10 -9 wt% at 550 °C, respectively. Significant corrosion was not observed at 450 °C for ferritic/martensitic steels, F82H, Mod.9Cr-1Mo steel, 410SS, 430SS except 2.25Cr-1Mo steel. Pb-Bi penetration into steels and dissolution of elements into Pb-Bi were severe at 550 °C even for ferritic/martensitic steels. Typical dissolution attack occurred for pure iron both at 550 °C without surface Fe 3O 4 and at 450 °C with a thin Fe 3O 4 film. Ferritization due to dissolution of Ni and Cr, and Pb-Bi penetration were recognized for austenitic stainless steels, 316SS and 14Cr-16Ni-2Mo steel at both temperatures of 450 °C and 550 °C. The phenomena were mitigated for 18Cr-20Ni-5Si steel. In some cases oxide films could not be a corrosion barrier in liquid lead-bismuth.
Effect of carburizing helium environment on creep behavior of Ni-base heat-resistant alloys for high-temperature gas-cooled reactors

International Nuclear Information System (INIS)

Kurata, Yuji; Ogawa, Yutaka; Nakajima, Hajime

1988-01-01

Creep tests were conducted on Ni-base heat-resistant alloys Hastelloy XR and XR-II, i.e. versions of Hastelloy X modified for nuclear applications, at 950degC using four types of helium environment with different impurity compositions, and mainly the effect of carburization was examined. For all the materials tested, the values of creep rupture time obtained under the carburizing conditions were similar to or longer than those in the commonly used, standard test environment (JAERI Type B helium). The difference among the results was interpreted by the counterbalancing effects of the strengthening due to carburization and possible weakening caused under very low oxidizing potential. In the corrosion monitoring specimens pronounced carbon pick-up was observed in the environment with high carbon activity and very low oxidizing potential. Based on the results obtained in the present and the previous works, it is suggested that a moderate control of the impurity chemistry is important rather than simple purification of the coolant in protecting the material from the environment-enhanced degradation. Either condition with high or low extremes in the oxidizing and carburizing potentials may cause enhanced degradation and thus are desirable to be avoided at the elevated temperatures. (author)
Effect of Local Strain Distribution of Cold-Rolled Alloy 690 on Primary Water Stress Corrosion Crack Growth Behavior

Directory of Open Access Journals (Sweden)

Kim S.-W.

2017-06-01

Full Text Available This work aims to study the stress corrosion crack growth behavior of cold-rolled Alloy 690 in the primary water of a pressurized water reactor. Compared with Alloy 600, which shows typical intergranular cracking along high angle grain boundaries, the cold-rolled Alloy 690, with its heterogeneous microstructure, revealed an abnormal crack growth behavior in mixed mode, that is, in transgranular cracking near a banded region, and in intergranular cracking in a matrix region. From local strain distribution analysis based on local mis-orientation, measured along the crack path using the electron back scattered diffraction method, it was suggested that the abnormal behavior was attributable to a heterogeneity of local strain distribution. In the cold-rolled Alloy 690, the stress corrosion crack grew through a highly strained area formed by a prior cold-rolling process in a direction perpendicular to the maximum principal stress applied during a subsequent stress corrosion cracking test.
Hot Corrosion Behavior of Stainless Steel with Al-Si/Al-Si-Cr Coating

Science.gov (United States)

Fu, Guangyan; Wu, Yongzhao; Liu, Qun; Li, Rongguang; Su, Yong

2017-03-01

The 1Cr18Ni9Ti stainless steel with Al-Si/Al-Si-Cr coatings is prepared by slurry process and vacuum diffusion, and the hot corrosion behavior of the stainless steel with/without the coatings is studied under the condition of Na2SO4 film at 950 °C in air. Results show that the corrosion kinetics of stainless steel, the stainless steel with Al-Si coating and the stainless steel with Al-Si-Cr coating follow parabolic laws in several segments. After 24 h corrosion, the sequence of the mass gain for the three alloys is the stainless steel with Al-Si-Cr coating coating coating. The corrosion products of the three alloys are layered. Thereinto, the corrosion products of stainless steel without coating are divided into two layers, where the outside layer contains a composite of Fe2O3 and FeO, and the inner layer is Cr2O3. The corrosion products of the stainless steel with Al-Si coating are also divided into two layers, of which the outside layer mainly consists of Cr2O3, and the inner layer is mainly SiO2. The corrosion film of the stainless steel with Al-Si-Cr coating is thin and dense, which combines well with substrate. Thereinto, the outside layer is mainly Cr2O3, and the inside layer is Al2O3. In the matrix of all of the three alloys, there exist small amount of sulfides. Continuous and protective films of Cr2O3, SiO2 and Al2O3 form on the surface of the stainless steel with Al-Si and Al-Si-Cr coatings, which prevent further oxidation or sulfide corrosion of matrix metals, and this is the main reason for the much smaller mass gain of the two alloys than that of the stainless steel without any coatings in the 24 h hot corrosion process.
Effect of H{sub 2}O{sub 2} on the corrosion behavior of 304L stainless steel

Energy Technology Data Exchange (ETDEWEB)

Song, Taek Hoh; Kim, In Sub [Korea Advanced Institute of Science and Technology, Taejon (Korea, Republic of); Noh, Sung Kee [Korea Atomic Energy Research Institute, Taejon (Korea, Republic of)

1995-08-01

In connection with the safe storage of high level nuclear waste, effect of H{sub 2}O{sub 2} on the corrosion behavior of 304L stainless steel was examined. Open circuit potentials and polarization curves were measured with and without H{sub 2}O{sub 2}. The experimental results show that H{sub 2}O{sub 2} increased corrosion potential and decreased pitting potential. The passive range, therefore, decreased as H{sub 2}O{sub 2} concentration increased, indicating that pitting resistance was decreased by the existence of H{sub 2}O{sub 2} in the electrolyte. These effects of H{sub 2}O{sub 2} on corrosion of 304L stainless steel are considered to be similar to those of {gamma}-irradiation. To compare the effects of H{sub 2}O{sub 2} with those of O{sub 2}, cathodic and anodic polarization curves were made in three types of electrolyte such as aerated, deaerated, and stirred electrolyte. The experimental results show that the effects of H{sub 2}O{sub 2} on the corrosion behavior were very similar to those of O{sub 2} such as increase of corrosion potential, decrease of pitting resistance, and increase of repassivation potential. In acid and alkaline media, the corrosion potential shifts by H{sub 2}O{sub 2} were restricted by the large current density of proton reduction and by the le Chatelier`s principle respectively. 13 figs., 1 tabs., 17 refs. (Author).
Corrosion electrochemical behaviors of silane coating coated magnesium alloy in NaCl solution containing cerium nitrate

Energy Technology Data Exchange (ETDEWEB)

Luo, F.; Li, Q.; Zhong, X.K.; Gao, H.; Dai, Y.; Chen, F.N. [School of Chemistry and Chemical Engineering, Southwest University Chongqing (China)

2012-02-15

Sol-gel coatings cannot provide adequate corrosion protection for metal/alloys in the corrosive environments due to their high crack-forming potential. This paper demonstrates the possibility to employ cerium nitrate as inhibitor to decrease the corrosion development of sol-gel-based silane coating on the magnesium alloy in NaCl solution. Cerium nitrate was added into the NaCl solution where the silane coating coated magnesium alloy was immersed. Scanning electron microscopy (SEM) was used to examine surface morphology of the silane coating coated magnesium alloy immersed in NaCl solutions doped and undoped with cerium nitrate. The corrosion electrochemical behaviors were investigated using potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) tests. The results showed that the introduction of cerium nitrate into NaCl solution could effectively inhibit the corrosion of the silane coating coated magnesium alloy. Moreover, the influence of concentration of cerium nitrate on the corrosion inhibition and the possible inhibiting mechanism were also discussed in detail. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)
Corrosion Behavior and Oxide Film Formation of T91 Steel under Different Water Chemistry Operation Conditions

Energy Technology Data Exchange (ETDEWEB)

Zhang, D. Q.; Shi, C.; Li, J.; Gao, L. X. [Shanghai University of Electric Power, Shanghai (China); Lee, K. Y. [Dalian University of Technology, Dalian (China)

2017-02-15

The corrosion behavior of a ferritic/martensitic steel T91 exposed to an aqueous solution containing chloride and sulfate ions is investigated depending on the stimulated all-volatile treatment (AVT) and under oxygenated treatment (OT) conditions. The corrosion of T91 steel under OT condition is severe, while the corrosion under AVT condition is not. The co-existence of chloride and sulfate ions has antagonistic effect on the corrosion of T91 steel in both AVT and OT conditions. Unlike to corrosion resistance in the aqueous solution, OT pretreatment provides T91 steel lower oxidation-resistance than VAT pretreatment. From scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDS) and X-ray diffraction (XRD) analysis, the lower corrosion resistance in the aqueous solution by VAT conditions possibly is due to the formation of pits. In addition, the lower oxidation resistance of T91 steel pretreated by OT conditions is explained as follows: the cracks formed during the immersion under OT conditions accelerated peeling-off rate of the oxide film.
Corrosion behavior and mechanism of MAO coated Ti{sub 6}Al{sub 4}V with a grain-fined surface layer

Energy Technology Data Exchange (ETDEWEB)

Gu, Yanhong, E-mail: gu_yanhong@163.com [School of Mechanical Engineering, Beijing Institute of Petrochemical Technology, Beijing 102617 (China); Chen, Lingling, E-mail: daisy_chenlingling@163.com [School of Mechanical Engineering, Beijing Institute of Petrochemical Technology, Beijing 102617 (China); College of Mechanical and Electrical Engineering, Beijing University of Chemical Technology, Beijing 100029 (China); Yue, Wen, E-mail: yw@cugb.edu.cn [School of Engineering and Technology, China University of Geosciences, Beijing 100083 (China); Chen, Ping, E-mail: chenp@ustb.edu.cn [School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083 (China); Chen, Fei, E-mail: chenfei@bipt.edu.cn [School of Mechanical Engineering, Beijing Institute of Petrochemical Technology, Beijing 102617 (China); Ning, Chengyun, E-mail: imcyning@scut.edu.cn [College of Materials Science and Engineering, South China University of Technology, Guangzhou 510640 (China)

2016-04-15

In order to enhance the corrosion behavior of Ti{sub 6}Al{sub 4}V, a MAO coating was prepared on the surface refined by ultrasonic cold forging technology (UCFT). The surface roughness value and the grain were evaluated by atomic force microscope (AFM) and transmission electron microscope (TEM). The microstructure and phase component of the coated samples were analyzed by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The corrosion behavior of all the samples was examined by potentiodynamic polarization and electrode impedance spectroscopy (EIS) tests in a 3.5% NaCl solution. The results show that UCFT can reduce the surface roughness value and refine the grains. The micro-pore size of the UCFT-MAO sample is smaller and the pore number is less than those of MAO sample. The thickness of the coated sample is about 10 μm. The UCFT-MAO sample possesses the highest micro-hardness among all the samples. The UCFT-MAO sample has the best corrosion resistance with the lowest corrosion current density and the highest electrochemical impedance, which is attributed to UCFT pretreatment prior to MAO process on titanium alloys. The influence of UCFT on the corrosion process and corrosion mechanism were discussed. - Highlights: • UCFT was used to refine the grain before MAO coatings were prepared on Ti alloys. • UCFT treated Ti alloys have decreased surface roughness and refined grain. • Surface performance of MAO coatings on UCFT treated Ti alloys has been improved. • The influence of UCFT on the corrosion behavior and mechanism of MAO coatings was discussed.

Corrosion Behavior of Carbon Steel in Concrete Material Composed of Tin Slag Waste in Aqueous Chloride Solution

Science.gov (United States)

Rustandi, Andi; Cahyadi, Agung; Taruli Siallagan, Sonia; Wafa' Nawawi, Fuad; Pratesa, Yudha

2018-01-01

Tin slag is a byproduct of tin ore smelting process which is rarely utilized. The main purpose of this work is to investigate the use of tin slag for concrete cement material application compared to the industrial Ordinary Portland Cement (OPC). Tin slag composition was characterized by XRD and XRF analysis. The characterization results showed the similar chemical composition of tin slag and OPC. It also revealed the semi crystalline structure of tin slag sample. Several electrochemical tests were performed to evaluate corrosion behavior of tin slag, OPC and various mixed composition of both materials and the addition of CaO. The corrosion behavior of OPC and tin slag were evaluated by using Cyclic Polarization, Electrochemical Impedance Spectroscopy (EIS) and Electrochemical Frequency Modulation (EFM) methods. Aqueous sodium chloride (NaCl) solution with 3.5% w.t concentration which similar to seawater was used as the electrolyte in this work. The steel specimen used as the reinforce bar (rebar) material of the concrete was carbon steel AISI 1045. The rebar was embedded in the concrete cement which composed of OPC and the various composition of tin slag including slag without addition of CaO and slag mixed with addition of 50 % CaO. The electrochemical tests results revealed that tin slag affected its corrosion behavior which becoming more active and increasing the corrosion rate as well as decreasing the electrochemical impedance.
Effect of Multipass Friction Stir Processing on Mechanical and Corrosion Behavior of 2507 Super Duplex Stainless Steel

Science.gov (United States)

Mishra, M. K.; Gunasekaran, G.; Rao, A. G.; Kashyap, B. P.; Prabhu, N.

2017-02-01

The microstructure, mechanical properties, and corrosion behavior of 2507 super duplex stainless steel after multipass friction stir processing (FSP) were examined. A significant refinement in grain size of both ferrite and austenite was observed in stir zone resulting in improved yield and tensile strength. Electrochemical impedance spectroscopy and anodic polarization studies in 3.5 wt.% NaCl solution showed nobler corrosion characteristics with increasing number of FSP passes. This was evident from the decrease in corrosion current density, decrease in passive current density, and increase in polarization resistance. Also, the decrease in density of defects, based on Mott-Schottky analysis, further confirms the improvement in corrosion resistance of 2507 super duplex stainless steel after multipass FSP.
Surface properties and corrosion behavior of Co-Cr alloy fabricated with selective laser melting technique.

Science.gov (United States)

Xin, Xian-zhen; Chen, Jie; Xiang, Nan; Wei, Bin

2013-01-01

We sought to study the corrosion behavior and surface properties of a commercial cobalt-chromium (Co-Cr) alloy which was fabricated with selective laser melting (SLM) technique. For this purpose, specimens were fabricated using different techniques, such as SLM system and casting methods. Surface hardness testing, microstructure observation, surface analysis using X-ray photoelectron spectroscopy (XPS) and electrochemical corrosion test were carried out to evaluate the corrosion properties and surface properties of the specimens. We found that microstructure of SLM specimens was more homogeneous than that of cast specimens. The mean surface hardness values of SLM and cast specimens were 458.3 and 384.8, respectively; SLM specimens showed higher values than cast ones in hardness. Both specimens exhibited no differences in their electrochemical corrosion properties in the artificial saliva through potentiodynamic curves and EIS, and no significant difference via XPS. Therefore, we concluded that within the scope of this study, SLM-fabricated restorations revealed good surface properties, such as proper hardness, homogeneous microstructure, and also showed sufficient corrosion resistance which could meet the needs of dental clinics.
Study on fracture and stress corrosion cracking behavior of casing sour service materials

International Nuclear Information System (INIS)

Sequera, C.; Gordon, H.

2003-01-01

Present work describes sulphide stress corrosion cracking and fracture toughness tests performed to high strength sour service materials of T-95, C-100 and C-110 oil well tubular grades. P-110 was considered as a reference case, since it is one of the high strength materials included in specification 5CT of American Petroleum Institute, API. Sulphide stress corrosion cracking, impact and fracture toughness values obtained in the tests show that there is a correspondence among them. A decreasing classification order was established, namely C-100, T-95, C-110 and P-110. Special grades steels studied demonstrated a better behavior in the evaluated properties than the reference case material grade: P-110. Results obtained indicate that a higher sulphide stress corrosion cracking resistance is related to a higher toughness. The fracture toughness results evidence the hydrogen influence on reducing the toughness values. (author)
Corrosion behavior of cast Ti-6Al-4V alloyed with Cu.

Science.gov (United States)

Koike, Marie; Cai, Zhuo; Oda, Yutaka; Hattori, Masayuki; Fujii, Hiroyuki; Okabe, Toru

2005-05-01

It has recently been found that alloying with copper improved the inherently poor grindability and wear resistance of titanium. This study characterized the corrosion behavior of cast Ti-6Al-4V alloyed with copper. Alloys (0.9 or 3.5 mass % Cu) were cast with the use of a magnesia-based investment in a centrifugal casting machine. Three specimen surfaces were tested: ground, sandblasted, and as cast. Commercially pure titanium and Ti-6Al-4V served as controls. Open-circuit potential measurement, linear polarization, and potentiodynamic cathodic polarization were performed in aerated (air + 10% CO(2)) modified Tani-Zucchi synthetic saliva at 37 degrees C. Potentiodynamic anodic polarization was conducted in the same medium deaerated by N(2) + 10% CO(2). Polarization resistance (R(p)), Tafel slopes, and corrosion current density (I(corr)) were determined. A passive region occurred for the alloy specimens with ground and sandblasted surfaces, as for CP Ti. However, no passivation was observed on the as-cast alloys or on CP Ti. There were significant differences among all metals tested for R(p) and I(corr) and significantly higher R(p) and lower I(corr) values for CP Ti compared to Ti-6Al-4V or the alloys with Cu. Alloying up to 3.5 mass % Cu to Ti-6Al-4V did not change the corrosion behavior. Specimens with ground or sandblasted surfaces were superior to specimens with as-cast surfaces. (c) 2005 Wiley Periodicals, Inc.
Comparative study on structure, corrosion properties and tribological behavior of pure Zn and different Zn-Ni alloy coatings

Energy Technology Data Exchange (ETDEWEB)

Tafreshi, M. [Department of Metallurgy and Materials Engineering, South Tehran Branch, Islamic Azad University, Tehran (Iran, Islamic Republic of); Allahkaram, S.R., E-mail: akaram@ut.ac.ir [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, P.O.Box: 11155-4563, Tehran (Iran, Islamic Republic of); Farhangi, H. [School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, P.O.Box: 11155-4563, Tehran (Iran, Islamic Republic of)

2016-11-01

Zn and Zn-Ni alloy coatings were electrodeposited from sulfate based electrolytes. The effect of alloys Ni content on morphology, microstructure, corrosion properties, microhardness and tribological behavior of these coatings were investigated and the results were compared with Zn film. According to X-ray diffraction patterns, different intermediate phases (η-Ni{sub 3}Zn{sub 22}, γ-Ni{sub 5}Zn{sub 21}, β-Zn-Ni) were formed by increasing the coatings Ni content from 11 to 17 wt%. Polarization and EIS results revealed that all the alloy coatings had better corrosion resistance than the Zn film. Zn-14 wt%Ni coating had the least corrosion current density and maximum polarization resistance between all the samples. Microhardness of the coatings was improved by increasing their Ni percentage to 17%. However, Zn-14 wt%Ni coating had the lowest wear loss and friction coefficient, while Zn film had the worst wear resistance between all the coatings. - Highlights: • Effect of Ni alloying element on morphology and structure of Zn electrodeposits. • Comparing corrosion behavior of Zn and Zn-Ni coatings. • Influence of Ni content on hardness of Zn-Ni films. • A comparison of tribological behavior of Zn and different Zn-Ni electrodeposits.
Nucleation and growth of intermetallic precipitates in Zircaloy-2 and zircaloy-4 and correlation to nodular corrosion behavior

International Nuclear Information System (INIS)

Maussner, G.; Steinberg, E.; Tenckhoff, E.

1987-01-01

One of the fundamental aspects in the history of the development of zirconium alloys for nuclear applications is the corrosion behavior under in-pile conditions. In boiling-water reactors (BWRs) and pressurized-water reactors (PWRs) the zirconium alloys Zircaloy-2 and Zircaloy-4 are the most commonly used materials, permitting attainment of a very high level of integrity and reliability. Nevertheless, efforts are required to optimize these well-established alloys with regard to their resistance to nodular corrosion, where improvements will give long-term advantages in fuel integrity and fuel economy. Phenomenological studies allow correlation of the nodular corrosion behavior with the morphological appearance of precipitated intermetallic phases in the microstructures of Zry-2 and Zry-4. To understand the fundamental processes of precipitation, particle nucleation-and-growth studies were made with Zry-2 and Zry-4 in different fabrication dimensions and with variations in β-quenching rates followed by isothermal and isochronical heat treatments. The microstructural characteristics of the precipitates were investigated by optical and transmission-electron microscopy. The macroscopic behavior was studied by electrical-resistivity measurements and hardness measurements. The nodular-corrosion susceptibility was determined by weight-gain and nodule distribution measurements after a 500 0 C laboratory-autoclave test
Corrosion Behavior of Pipeline Carbon Steel under Different Iron Oxide Deposits in the District Heating System

Directory of Open Access Journals (Sweden)

Yong-Sang Kim

2017-05-01

Full Text Available The corrosion behavior of pipeline steel covered by iron oxides (α-FeOOH; Fe3O4 and Fe2O3 was investigated in simulated district heating water. In potentiodynamic polarization tests; the corrosion rate of pipeline steel is increased under the iron oxide but the increaseing rate is different due to the differnet chemical reactions of the covered iron oxides. Pitting corrosion was only observed on the α-FeOOH-covered specimen; which is caused by the crevice corrosion under the α-FeOOH. From Mott-Schottky and X-ray diffraction results; the surface reaction and oxide layer were dependent on the kind of iron oxides. The iron oxides deposit increases the failure risk of the pipeline and localized corrosion can be occurred under the α-FeOOH-covered region of the pipeline. Thus, prevention methods for the iron oxide deposit in the district pipeline system such as filtering or periodic chemical cleaning are needed.
Creep properties of superalloys for the HTGR in impure helium environments

International Nuclear Information System (INIS)

Kawakami, H.; Nakanishi, T.

1981-01-01

This paper describes creep behaviors of two heat resistant alloys, Hastelloy X and Incoloy 800, in helium environments of the HTGR. In impure helium environments, these alloys are susceptible to carburization and oxidization. We have investigated these effects separately, and related them to the creep behaviors of the alloys. Experiments were carried out at 900 0 C both in helium and in air. Carburization results in decrease of secondary creep strain rate and delay of tertiary creep initiation. Oxidization caused decrease in tertiary creep strain rate of Hastelloy X, but did not that of Incoloy 800. Enhancement in tertiary creep strain rate of Hastelloy X in a very weakly oxidizing environment was confirmed in creep crack growth experiment using notched plate specimens. The rupture time of Hastelloy X in helium was short when compared with in air. Stress versus rupture time curves for both environments were parallel up to 5000 hours test, and a ratio of rupture stress in helium to that in air was about 0.9. In case of Incoloy 800, rupture time in helium was markedly prolonged as compared with that in air. (orig.)
Laser beam welding of Waspaloy: Characterization and corrosion behavior evaluation

Science.gov (United States)

Shoja Razavi, Reza

2016-08-01

In this work, a study on Nd:YAG laser welding of Waspaloy sheets has been made. Microstructures, phase changes and hardness of the laser joint were investigated using optical microscopy, scanning electron microscopy (SEM), field emission scanning electron microscopy (FESEM), energy dispersive spectroscopy (EDS), X-ray diffraction analysis (XRD) and vickers microhardness (HV0.3). Corrosion behavior of the weldment at low temperature in 3.5%wt NaCl solution at room temperature was also investigated using open circuit potential and cyclic potentiodynamic polarization tests. Hot corrosion studies were conducted on samples in the molten salt environment (Na2SO4-60%V2O5) at 900 °C for 50 h. Results indicated that the microstructure of weld zone was mainly dendritic grown epitaxially in the direction perpendicular to the weld boundary and heat transfer. Moreover, the Ti-Mo carbide particles were observed in the structure of the weld zone and base metal. The average size of carbides formed in the base metal (2.97±0.5 μm) was larger than that of the weld zone (0.95±0.2 μm). XRD patterns of the weld zone and base metal showed that the laser welding did not alter the phase structure of the weld zone, being in γ-Ni(Cr) single phase. Microhardness profile showed that the hardness values of the weld zone (210-261 HV) were lower than that of the base metal (323-330 HV). Electrochemical and hot corrosion tests indicated that the corrosion resistance of the weld metal was greater than the base metal in both room and high temperatures.
Corrosion Behavior of High Pressure Die Cast Al-Ni and Al-Ni-Ca Alloys in 3.5% NaCl Solution

Energy Technology Data Exchange (ETDEWEB)

Arthanari, Srinivasan; Jang, Jae Cheol; Shin, Kwang Seon [Seoul National University, Seoul (Korea, Republic of)

2017-06-15

In this investigation corrosion behavior of newly developed high-pressure die cast Al-Ni (N15) and Al-Ni-Ca (NX1503) alloys was studied in 3.5% NaCl solution. The electrochemical corrosion behavior was evaluated using open circuit potential (OCP) measurement, potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS) techniques. Potentiodynamic polarization results validated that NX1503 alloy exhibited lower corrosion current density (i{sub corr}) value (5.969 μA/cm{sup 2}) compared to N15 (7.387 μA/cm{sup 2}). EIS-Bode plots revealed a higher impedance (|Z|) value and maximum phase angle value for NX1503 than N15 alloy. Equivalent circuit curve fitting analysis revealed that surface layer (R{sub 1}) and charge transfer resistance (R{sub ct}) values of NX1503 alloy was higher compared to N15 alloy. Immersion corrosion studies were also conducted for alloys using fishing line specimen arrangement to simultaneously measure corrosion rates from weight loss (P{sub W}) and hydrogen volume (P{sub H}) after 72 hours and NX1503 alloy had lower corrosion rate compared to N15 alloy. The addition of Ca to N15 alloy significantly reduced the Al{sub 3}Ni intermetallic phase and further grain refinement may be attributed for reduction in the corrosion rate.
On the improvement of HTGR fuel elements corrosion resistance

International Nuclear Information System (INIS)

Chernikov, A.S.; Kurbakov, S.D.

1996-01-01

The results of corrosion tests of matrix graphite based on calcinated (30PG graphite) and non-calcinated (MPG graphite) petroleum cokes in helium containing 0.01-1 vol.% water vapour in the temperature range 600-1200degC are presented. The results of investigation of matrix graphite components reactivity are considered. It is shown that the filler graphite 30PG has the minimum activity towards the water vapour. The influence of impurities content on the oxidation rate are considered. The results of corrosion tests of matrix graphite coated with protective layers (silicon carbide and aluminium phosphates) in the air environment at 1600degC, 1 h, are given. (author)
Plasma electrolytic oxidation of AZ91D magnesium alloy with different additives and its corrosion behavior

Energy Technology Data Exchange (ETDEWEB)

Cao, Fa-he; Cao, Jiang-lin; Zhang, Zhao [Department of Chemistry, Zhejiang University, Hangzhou 310027 (China); Zhang, Jian-qing; Cao, Chu-nan [Department of Chemistry, Zhejiang University, Hangzhou 310027 (China); State Key Laboratory for Corrosion and Protection, Institute of Metal Research, The Chinese Academy of Sciences, Shenyang 110016 (China)

2007-09-15

Plasma electrolytic oxidation (PEO) of Mg-based AZ91D alloys was investigated using 50 Hz AC anodizing technique in an alkaline borate solution, which contained a new kind of organic additive and without F, P, and Cr. The anodizing technological parameters have been optimized and a kind of ivory-white smooth anodic film with high corrosion resistance was obtained. It was found that the formation of the anodic films was always coupled with sparking and oxygen evolution, whose intensity changed with the additive and anodizing voltage. All EIS plots have two capacitive loops and one low frequency inductive component. Two capacitive arcs present the barrier and porous layer of the PEO film and the inductive component in the low frequency domain is a complex behavior due to the porous structure connected to the electrolyte. EIS plots and fitting results show that a self-sealing process of the PEO firm with different additives takes place in the beginning of immersion time, then corrosion attack becomes a preponderant process to promote the degradation of the film. Tafel results show that PEO treatment decreases the corrosion current density by four, even five orders of magnitude, while additives content does not affect strongly the electrochemical corrosion behavior. Salt spray test shows that the PEO film formed with NaAlO{sub 2} and Na{sub 2}SiO{sub 3} presents good corrosion resistance, over 600 h without any sealing treatment. The difference of corrosion resistance arose by additives examined by electrochemical techniques and salt spray test does not show strict corresponding relationship. (Abstract Copyright [2007], Wiley Periodicals, Inc.)
Comparative study on the corrosion behavior of Ti-Nb and TMA alloys for dental application in various artificial solutions

International Nuclear Information System (INIS)

Bai, Y.J.; Wang, Y.B.; Cheng, Y.; Deng, F.; Zheng, Y.F.; Wei, S.C.

2011-01-01

The corrosion behavior of Ti-Nb dental alloy in artificial saliva with and without the addition of lactic acid and sodium fluoride was investigated by electrochemical techniques, with the commercial Titanium-molybdenum alloy (TMA) as a comparison. The chemical composition, microstructure and constitutional phase were characterized via energy dispersive spectrometry, optical microscope and X-ray diffraction, meanwhile the open circuit potential, electrochemical impedance spectroscopy and potentiodynamic polarization measurements were carried out to study the corrosion resistance of experimental alloys, with the corroded surface being further characterized by scanning electron microscopy and X-ray photoelectron spectroscopy. It was found that the corrosion behavior of Ti-Nb alloy was similar to those TMA alloy samples in both artificial and acidified saliva solutions, whereas statistical analysis of the electrochemical impedance spectroscopy and polarization parameters showed Ti-Nb alloy exhibited better corrosion resistance in fluoridated saliva and fluoridated acidified saliva. SEM observation indicated that TMA alloy corroded heavily than Ti-Nb alloy in fluoride containing saliva. XPS surface analysis suggested that Nb 2 O 5 played an important role in anti-corrosion from the attack of fluoride ion. Based on the above finding, Ti-Nb alloy is believed to be suitable for the usage in certain fluoride treated dental works with excellent corrosion resistance in fluoride-containing oral media.
Corrosion Inhibition and Adsorption Behavior of Clove Oil on Iron in Acidic Medium

Directory of Open Access Journals (Sweden)

Archana Saxena

2012-01-01

Full Text Available Corrosion behavior of iron in hydrochloric acid solution was studied using weight loss as well Scanning electron microscopy study without and with clove oil. The percentage inhibition efficiency increases with increasing clove oil concentration. All the data revel that the oil acts as an excellent inhibitor for the corrosion of iron in HCl solution. Thermodynamic, kinetic parameters and equilibrium constant for adsorption process were calculated from the experimental data. The adsorption of clove oil on experimental metals was found to follow the Langmuir adsorption isotherm at all the concentration studies. Scanning electron microscope (SEM, investigations also indicate that clove oil greatly lowers the dissolution currents.
A comparative corrosion behavior of Mg, AZ31 and AZ91 alloys in 3.5% NaCl solution

Directory of Open Access Journals (Sweden)

I.B. Singh

2015-06-01

Full Text Available The corrosion behavior of Mg, AZ31 and AZ91 has been evaluated in 3.5% NaCl solution using weight loss, electrochemical polarization and impedance measurements. Corrosion rate derived from the weight losses demonstrated the occurrence of steeply fast corrosion reaction on AZ91 alloy after three hours of immersion, indicating the start of galvanic corrosion. An increase of corrosion rate with immersion time was also observed for AZ31 but with lesser extent than AZ91 alloy. Whereas Mg metals showed a decrease of corrosion rate with immersion time, suggesting the formation of a protective layer on their surfaces. In contrast, the corrosion current density (Icorr derived from the Tafel plots, exhibited their corrosion resistances in order of Mg > AZ91 > AZ31. Electrochemical charge transfer resistance (Rct and double layer capacitance measured by electrochemical impedance spectroscopy (EIS, are well in accordance with the measured Icorr. EIS measurements with time and microstructural examination of the corroded and uncorroded samples are helpful in elucidation of results measured by electrochemical polarization.
Corrosion behavior of carbon steel for overpack in groundwater containing bicarbonate ions

International Nuclear Information System (INIS)

Nishimura, Toshiyasu; Dong, Junpha

2009-01-01

Carbon steel is considered in Japan the candidate material for overpacks in high-level radioactive waste disposal. Effects of bicarbonate solutions on the corrosion behavior and corrosion products of carbon steel were investigated by electrochemical measurements, FT-IR and XRD analyses. The anodic polarization measurements showed that bicarbonate ions (HCO 3 - ) accelerated the anodic dissolution and the outer layer film formation of carbon steel in the case of high concentrations, on the other hand, it inhibited these processes in the case of low concentrations. The FT-IR and XRD analyses of the anodized film showed that siderite (FeCO 3 ) was formed in 0.5 to 1.0 mol/L bicarbonate solution, and Fe 2 (OH) 2 CO 3 in 0.1 to 0.2 mol/L bicarbonate solution, while Fe 6 (OH) 12 CO 3 was formed in 0.02 to 0.05 mol/L bicarbonate solutions. The stability of these corrosion products was able to be explained by using the actual potential-pH diagrams for the Fe-H 2 O-CO 2 system. (author)
Corrosion behavior of as-cast binary Mg-Bi alloys in Hank's solution

Directory of Open Access Journals (Sweden)

Wei-li Cheng

2015-11-01

Full Text Available Biodegradable Mg-xBi (x = 3, 6 and 9wt.% alloys were fabricated by ingot casting, and the change of corrosion behavior of the alloys in the Hank's solution was analyzed with respect to the microstructure using optical micrograph (OM, X-ray diffraction (XRD, scanning electron microscope (SEM equipped with an energy dispersive X-ray spectrometer (EDS, electrochemical and immersion tests. The results show that the microstructures of the as-cast Mg-Bi alloys mainly consisted of dendritic ?Mg grains and Mg3Bi2 phase in common, with the secondary dendrite arm spacing (SDAS decreasing significantly from 41.2 靘 to 25.4 靘 and the fraction of Mg3Bi2 increasing from 3.1% to 10.7%. Furthermore, the corrosion rate increasing from 1.32 mm昦-1 to 8.07 mm昦-1 as the Bi content was increased from 3wt.% to 9wt.%. The reduced corrosion resistance was mainly ascribed to the increasing fraction of the second phase particles, which bring positive effects on the development of pitting.
Adsorption behavior of caffeine as a green corrosion inhibitor for copper

International Nuclear Information System (INIS)

Souza, Fernando Sílvio de; Giacomelli, Cristiano; Gonçalves, Reinaldo Simões; Spinelli, Almir

2012-01-01

Electrochemical and impedance experiments were carried out to evaluate the corrosion behavior of copper in aerated 0.1 mol L −1 H 2 SO 4 solutions in the presence of three xanthine derivatives with similar chemical structures. The corrosion rate of copper was found to increase in the presence of theophylline and theobromine and decrease in the presence of caffeine. The adsorption and inhibitory effect of caffeine on copper surfaces in aerated 0.1 mol L −1 H 2 SO 4 solutions were then investigated in detail by potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), contact angle measurements, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and fluorescence experiments. The data obtained indicate that caffeine behaves as a cathodic-type inhibitor adsorbing onto the copper surface according to the Temkin isotherm, with the negative ∆G° ads value of − 31.1 kJ mol −1 signifying a spontaneous adsorption process. The corrosion inhibition efficiency increased with caffeine concentration in the range of 1.0–10.0 mmol L −1 . Furthermore, the EIS results obtained at the open-circuit potential and surface analysis (SEM, EDS and fluorescence) clearly demonstrated the adsorption of the organic compound onto the copper electrode. The contact angle measurements revealed the formation of a hydrophobic protective film. This film covers up to 72% of the total active surface, acts as a protective barrier and prevents interaction between the metal, water and oxygen molecules. - Highlights: ► We have investigated the adsorption and corrosion inhibition of caffeine on copper surfaces. ► Caffeine behaves as a cathodic-type inhibitor. ► Caffeine adsorbs onto copper surface according to Temkin isotherm. ► There exists the formation of a hydrophobic film that acts as a protective barrier. ► This corrosion inhibitor covers up to 72% of the total active surface of copper.
Corrosion behavior of zirconia in acidulated phosphate fluoride

Directory of Open Access Journals (Sweden)

Anie Thomas

2016-02-01

Full Text Available ABSTRACT Objective The corrosion behavior of zirconia in acidulated phosphate fluoride (APF representing acidic environments and fluoride treatments was studied. Material and Methods Zirconia rods were immersed in 1.23% and 0.123% APF solutions and maintained at 37°C for determined periods of time. Surfaces of all specimens were imaged using digital microscopy and scanning electron microscopy (SEM. Sample mass and dimensions were measured for mass loss determination. Samples were characterized by powder X-ray diffraction (XRD to detect changes in crystallinity. A biosensor based on electrochemical impedance spectroscopy (EIS was used to detect ion dissolution of material into the immersion media. Results Digital microscopy revealed diminishing luster of the materials and SEM showed increased superficial corrosion of zirconia submerged in 1.23% APF. Although no structural change was found, the absorption of salts (sodium phosphate onto the surface of the materials bathed in 0.123% APF was significant. EIS indicated a greater change of impedance for the immersion solutions with increasing bathing time. Conclusion Immersion of zirconia in APF solutions showed deterioration limited to the surface, not extending to the bulk of the material. Inferences on zirconia performance in acidic oral environment can be elucidated from the study.

Corrosion-Resistant High-Entropy Alloys: A Review

Directory of Open Access Journals (Sweden)

Yunzhu Shi

2017-02-01

Full Text Available Corrosion destroys more than three percent of the world’s gross domestic product. Therefore, the design of highly corrosion-resistant materials is urgently needed. By breaking the classical alloy-design philosophy, high-entropy alloys (HEAs possess unique microstructures, which are solid solutions with random arrangements of multiple elements. The particular locally-disordered chemical environment is expected to lead to unique corrosion-resistant properties. In this review, the studies of the corrosion-resistant HEAs during the last decade are summarized. The corrosion-resistant properties of HEAs in various aqueous environments and the corrosion behavior of HEA coatings are presented. The effects of environments, alloying elements, and processing methods on the corrosion resistance are analyzed in detail. Furthermore, the possible directions of future work regarding the corrosion behavior of HEAs are suggested.
Influences of the quantity of Mg2Sn phase on the corrosion behavior of Mg-7Sn magnesium alloy

International Nuclear Information System (INIS)

Liu Xianbin; Shan Dayong; Song Yingwei; Chen Rongshi; Han Enhou

2011-01-01

The influence of the quantity of the Mg 2 Sn phase on the corrosion behavior of different solution temperature treated Mg-7Sn magnesium alloy has been investigated by electrochemical measurements, scanning electron microscope (SEM) observation, X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) analysis. With the increase of solution temperature, the quantity of Mg 2 Sn phase decreased and the tin concentration of matrix increased. The dissolved tin in Mg matrix took part in the film formation and the constituent of film was magnesium oxide and stannic oxide. The corrosion mode and corrosion rate were associated with the quantity of Mg 2 Sn phases and tin concentration of the matrix. If most of tin was present as Mg 2 Sn, the corrosion mode was pitting corrosion and it accelerated the corrosion rate. If most of tin was dissolved in matrix, the corrosion mode was filiform corrosion and it decreased the corrosion rate. The experiment evidences demonstrated that the corrosion resistance can be improved by increasing the tin concentration of matrix and the lowest corrosion rate was observed for sample solution treated at 540 o C.
Corrosion fatigue cracking behavior of Inconel 690 (TT) in secondary water of pressurized water reactors

International Nuclear Information System (INIS)

Xiao Jun; Chen Luyao; Qiu Shaoyu; Chen Yong; Lin Zhenxia; Fu Zhenghong

2015-01-01

Inconel 690 (TT) is one of the key materials for tubes of steam generators for pressurized water reactors, where it is susceptible to corrosion fatigue cracking. In this paper, the corrosion fatigue cracking behavior of Inconel 690 (TT) was investigated under small scale yielding conditions, in the simulated secondary water of pressurized water reactor. It was observed that the fatigue crack growth rate was accelerated by a maximum factor up to 3 in the simulated secondary water, comparing to that in room temperature air. In addition, it was found that the accelerating effect was influenced by out-of-plane cracking of corrosion fatigue cracks and also correlated with stress intensity factor range, maximum stress intensity factor and stress ratio. (authors)
Corrosion behavior of ferritic stainless steel with 15wt% chromium for the automobile exhaust system

Science.gov (United States)

Li, Hua-bing; Jiang, Zhou-hua; Feng, Hao; Zhu, Hong-chun; Sun, Bin-han; Li, Zhen

2013-09-01

The effect of chloride ion concentration, pH value, and grain size on the pitting corrosion resistance of a new ferritic stainless steel with 15wt% Cr was investigated using the anodic polarization method. The semiconducting properties of passive films with different chloride ion concentrations were performed using capacitance measurement and Mott-Schottky analysis methods. The aging precipitation and intergranular corrosion behavior were evaluated at 400-900°C. It is found that the pitting potential decreases when the grain size increases. With the increase in chloride ion concentration, the doping density and the flat-bland potential increase but the thickness of the space charge layer decreases. The pitting corrosion resistance increases rapidly with the decrease in pH value. Precipitants is identified as Nb(C,N) and NbC, rather than Cr-carbide. The intergranular corrosion is attributed to the synergistic effects of Nb(C,N) and NbC precipitates and Cr segregation adjacent to the precipitates.
Deformation behavior, corrosion resistance, and cytotoxicity of Ni-free Zr-based bulk metallic glasses.

Science.gov (United States)

Liu, L; Qiu, C L; Chen, Q; Chan, K C; Zhang, S M

2008-07-01

Two Ni-free bulk metallic glasses (BMGs) of Zr(60)Nb(5)Cu(22.5)Pd(5)Al(7.5) and Zr(60)Nb(5)Cu(20)Fe(5)Al(10) were successfully prepared by arc-melting and copper mold casting. The thermal stability and crystallization were studied using differential scanning calorimetry. It demonstrates that the two BMGs exhibit very good glass forming ability with a wide supercooled liquid region. A multi-step process of crystallization with a preferential formation of quasicrystals occurred in both BMGs under continuous heating. The deformation behavior of the two BMGs was investigated using quasi-static compression testing. It reveals that the BMGs exhibit not only superior strength but also an extended plasticity. Corrosion behaviors of the BMGs were investigated in phosphate buffered solution by electrochemical polarization. The result shows that the two BMGs exhibit excellent corrosion resistance characterized by low corrosion current densities and wide passive regions. X-ray photoelectron spectroscopy analysis revealed that the passive film formed after anodic polarization was highly enriched in zirconium, niobium, and aluminum oxides. This is attributed to the excellent corrosion resistance. Additionally, the potential cytotoxicity of the two Ni-free BMGs was evaluated through cell culture for 1 week followed by 3-(4,5-Dimethylthiazol-2-yl-)-2,5-diphenyltetrazolium bromide assay and SEM observation. The results indicate that the two Ni-free BMGs exhibit as good biocompatibility as Ti-6Al-4V alloy, and thus show a promising potential for biomedical applications. (c) 2007 Wiley Periodicals, Inc.
The Hydrogen Pickup Behavior for Zirconium-based Alloys in Various Out-of-pile Corrosion Test Conditions

Energy Technology Data Exchange (ETDEWEB)

Aomi, M.; Etoh, Y.; Ishimoto, S.; Une, K. [Nippon Nuclear Fuel Development, Co., Ltd., 2163 Narita-cho, Oarai-machi, Ibaraki-ken, 311-1313 (Japan); Ito, K. [Global Nuclear Fuel Japan Co., Ltd., 3-1 Uchikawa 2-chome, Yokosuka-shi, Kanagawa-ken, 239-0836 (Japan)

2009-06-15

An acceleration of hydrogen absorption in zirconium alloy claddings at high burnups is one of the most important issues limiting the fuel performance from the viewpoint of cladding integrity. In this context, advanced cladding materials with higher corrosion resistant and lower hydrogen absorption properties have been widely searched in various organizations. In this study, four kinds of zirconium-based alloys, whose in-pile data had been acquired [1,2] were subjected to comprehensive out-of-pile corrosion tests with various temperature and atmosphere conditions in order to investigate the correlation between in-pile and out-of-pile corrosion and hydrogen pick-up behavior, i.e. Zry-2, GNF-Ziron (Zry-2-based alloy with {approx}0.25 wt % of Fe), Hi-FeNi Zircaloy (Zry-2-based alloy with {approx}0.25 wt % of Fe and {approx}0.1 wt% Ni), and VB (Zr-based alloy containing Sn, Cr, and {approx}0.5 wt % of Fe). All the alloys were annealed in RXA condition. The out-of-pile corrosion tests were carried out in three different conditions of 400 deg. C steam, 475 deg. C supercritical water, and 290 deg. C LiOH aqueous solution. In addition to these alloys, several Zry-2-based alloys with various iron contents were tested in 290 deg. C LiOH aqueous solution. Among the four corrosion conditions, the 290 deg. C LiOH aqueous solution test well screened the hydrogen pick-up behavior of the alloys. The hydrogen absorption decreased with higher iron contents in the alloys in both the out-of-pile and in-pile conditions. Especially, the distinct suppression of hydrogen absorption was observed for VB with the highest iron content. The similar dependence of iron content on the hydrogen pick-up fraction was also obtained for the Zry-2-based alloys with different iron contents, which were corroded in the 290 deg. C LiOH aqueous solution condition. As for the corrosion behavior in the 290 deg. C LiOH aqueous solution condition, the weight gains of Zry-2, GNF-Ziron and VB followed the 1
Investigation of corrosion behavior of nitrogen doped and platinum/ruthenium doped diamond-like carbon thin films in Hank's solution

Energy Technology Data Exchange (ETDEWEB)

Khun, N.W.; Liu, E., E-mail: MEJLiu@ntu.edu.sg

2011-10-10

Undoped (DLC), nitrogen-doped (N-DLC) and platinum/ruthenium doped diamond-like carbon (PtRu-DLC) thin films were deposited on p-Si (100) substrates using a DC magnetron sputtering deposition system. The chemical composition, bonding structure, surface morphology and adhesion strength of the films were characterized using X-ray photoelectron spectroscopy (XPS), micro-Raman spectroscopy, atomic force microscopy (AFM) and micro-scratch test, respectively. The corrosion behavior of the films in a Hank's solution was investigated using potentiodynamic polarization test. The corrosion results revealed that the PtRu-DLC film had the highest corrosion potential among the films used in this study. Highlights: {yields} DLC thin films were deposited on Si substrates via dc magnetron sputtering. {yields} Some DLC films were doped with N and/or Pt/Ru. {yields} The film corrosion behavior was studied in a Hank solution with polarization test. {yields} The PtRu-DLC film showed the highest corrosion potential among the films studied.
The effect of Pseudoxanthomonas sp. as manganese oxidizing bacterium on the corrosion behavior of carbon steel

Energy Technology Data Exchange (ETDEWEB)

Ashassi-Sorkhabi, H., E-mail: habib_ashassi@yahoo.com [Electrochemistry Research Laboratory, Physical Chemistry Department, Faculty of Chemistry, University of Tabriz, Tabriz (Iran, Islamic Republic of); Moradi-Haghighi, M. [Electrochemistry Research Laboratory, Physical Chemistry Department, Faculty of Chemistry, University of Tabriz, Tabriz (Iran, Islamic Republic of); Zarrini, G. [Microbiology laboratory, Biology Department, Science Faculty, University of Tabriz, Tabriz (Iran, Islamic Republic of)

2012-02-01

The present study investigated the role of manganese oxidizing bacterium (MOB), namely Pseudoxanthomonas sp. on the corrosion behavior of carbon steel. This bacterium was isolated from sewage treatment plants and identified by biochemical and molecular methods. The electrochemical techniques such as open circuit potentiometry, electrochemical impedance spectroscopy, potentiodynamic and cyclic polarization were used to measure the corrosion rate and observe the corrosion mechanism. Also, scanning electron microscopy and X-ray diffraction studies were applied to surface analysis. This study revealed the strong adhesion of the biofilm on the metal surface in the presence of Pseudoxanthomonas sp. that enhanced the corrosion of carbon steel. X-ray diffraction patterns identified a high content of MnO{sub 2} deposition within these biofilms. This is the first report that discloses the involvement of Pseudoxanthomonas sp. as manganese oxidizing bacteria on the corrosion of carbon steel. - Highlights: Black-Right-Pointing-Pointer A new type of manganese oxidizing bacteria, namely Pseudoxanthomonas sp. was indicated. Black-Right-Pointing-Pointer This bacterium can create a biofilm on the part of metal surface and affect localized corrosion. Black-Right-Pointing-Pointer In the presence of biofilm, the diffusion of oxygen vacancies and manganese ions has occurred.
The effect of Pseudoxanthomonas sp. as manganese oxidizing bacterium on the corrosion behavior of carbon steel

International Nuclear Information System (INIS)

Ashassi-Sorkhabi, H.; Moradi-Haghighi, M.; Zarrini, G.

2012-01-01

The present study investigated the role of manganese oxidizing bacterium (MOB), namely Pseudoxanthomonas sp. on the corrosion behavior of carbon steel. This bacterium was isolated from sewage treatment plants and identified by biochemical and molecular methods. The electrochemical techniques such as open circuit potentiometry, electrochemical impedance spectroscopy, potentiodynamic and cyclic polarization were used to measure the corrosion rate and observe the corrosion mechanism. Also, scanning electron microscopy and X-ray diffraction studies were applied to surface analysis. This study revealed the strong adhesion of the biofilm on the metal surface in the presence of Pseudoxanthomonas sp. that enhanced the corrosion of carbon steel. X-ray diffraction patterns identified a high content of MnO 2 deposition within these biofilms. This is the first report that discloses the involvement of Pseudoxanthomonas sp. as manganese oxidizing bacteria on the corrosion of carbon steel. - Highlights: ► A new type of manganese oxidizing bacteria, namely Pseudoxanthomonas sp. was indicated. ► This bacterium can create a biofilm on the part of metal surface and affect localized corrosion. ► In the presence of biofilm, the diffusion of oxygen vacancies and manganese ions has occurred.
Corrosion behavior of Ni-based structural materials for electrolytic reduction in lithium molten salt

International Nuclear Information System (INIS)

Cho, Soo Haeng; Park, Sung Bin; Lee, Jong Hyeon; Hur, Jin Mok; Lee, Han Soo

2011-01-01

In this study, the corrosion behavior of new Ni-based structural materials was studied for electrolytic reduction after exposure to LiCl-Li 2 O molten salt at 650 deg. C for 24-216 h under an oxidizing atmosphere. The new alloys with Ni, Cr, Al, Si, and Nb as the major components were melted at 1700 deg. C under an inert atmosphere. The melt was poured into a preheated metallic mold to prepare an as-cast alloy. The corrosion products and fine structures of the corroded specimens were characterized by scanning electron microscope (SEM), Energy Dispersive X-ray Spectroscope (EDS), and X-ray diffraction (XRD). The corrosion products of as cast and heat treated low Si/high Ti alloys were Cr 2 O 3 , NiCr 2 O 4 , Ni, NiO, and (Al,Nb,Ti)O 2 ; those of as cast and heat treated high Si/low Ti alloys were Cr 2 O 3 , NiCr 2 O 4 , Ni, and NiO. The corrosion layers of as cast and heat treated low Si/high Ti alloys were continuous and dense. However, those of as cast and heat treated high Si/low Ti alloys were discontinuous and cracked. Heat treated low Si/high Ti alloy showed the highest corrosion resistance among the examined alloys. The superior corrosion resistance of the heat treated low Si/high Ti alloy was attributed to the addition of an appropriate amount of Si, and the metallurgical evaluations were performed systematically.
Evaluation of materials for heat exchanging components in advanced helium-cooled reactors

International Nuclear Information System (INIS)

Schubert, F.

1984-01-01

The qualification of metallic materials for advanced HTR applications is based on creep behaviour, fatigue properties, structural stability and corrosion resistance. A brief state of the art is provided for the materials for heat exchanging components. The experimental results are treated with respect to the importance for the design, the characteristic of time-depend materials behaviour are evaluated. Of specific interest are the possible effects of helium on the mechanical properties. Helium, which serves as primary coolant, contains traces of reactive impurities such as hydrogen, methane, carbon monoxide and water vapor. The evaluation of the HTR materials program serves as basis for structural design rules of components with operation temperatures above 800 deg C. The materials mechanical topics are discussed. Alloy improvement and the progress in development of new alloys are reviewed. (author)
Corrosion and wear behavior of functionally graded Al2024/SiC composites produced by hot pressing and consolidation

Energy Technology Data Exchange (ETDEWEB)

Erdemir, Fatih; Canakci, Aykut, E-mail: aykut@ktu.edu.tr; Varol, Temel; Ozkaya, Serdar

2015-09-25

Highlights: • Functionally graded Al2024/SiC composites were produced by hot pressing. • Effect of the number of graded layers was investigated on the corrosion behavior. • Functionally graded composites has the most corrosion resistant than composites. • Wear mechanisms of Al2024/SiC composites were explained. - Abstract: Functionally graded Al2024/SiC composites (FGMs) with varying percentage of SiC (30–60%) were produced by hot pressing and consolidation method. The effects of SiC content and number of layers of Al2024/SiC FGMs on the corrosion and wear behaviors were investigated. The microstructures of these composites were characterized by a scanning electron microscopy (SEM) with energy-dispersive X-ray spectroscopy (EDS). The corrosion performances of composites were evaluated by potentiodynamic polarization scans in 3.5% NaCl solution. Corrosion experiments shows that corrosion rate (1109 mpy) of two layered FGMs which containing 50 wt.% SiC were much higher than Al2024 matrix (2569 mpy) and Al2024/50 wt.% SiC composite (2201 mpy). Mechanical properties of these composites were evaluated by microhardness measurements and ball-on-disk wear tests. As the applied load change from 15 to 20 N, the wear rates of the Al2024 increased significantly and wear mechanism transformed from mild to severe wear regime. It has been shown that Al2024/40 wt.% SiC composite has lower wear rate where adhesive and abrasive wear mechanisms play a major role.
In situ ellipsometric investigation of stainless steel corrosion behavior in buffered solutions with amino acids

International Nuclear Information System (INIS)

Vinnichenko, M.V.; Pham, M.T.; Chevolleau, T.; Poperenko, L.V.; Maitz, M.F.

2003-01-01

The corrosion of metals is associated both with a release of ions and changes in optical surface properties. In this study, these two effects were correlated by a potentiodynamic corrosion test and in situ probing of the surface by ellipsometry. The studies were carried out with stainless steel (SS) AISI 304 and 316 in phosphate buffered saline (PBS) and in Dulbecco's modified minimal essential medium (DMEM) at pH 7.4. In both media, 304 steel is more susceptible to corrosion than 316 grade. The 316 steel shows a higher corrosion potential and higher corrosion current density in PBS than in DMEM, for 304 steel this behavior is vice versa. Ellipsometry demonstrated a higher sensitivity than potentiodynamics to surface modification in the cathodic area. In DMEM the removal of a surface layer at negative potential and a further repassivation with increasing potential was characteristic. In PBS a surface layer started to grow immediately. X-ray photoelectron spectra of this layer formed in PBS are consistent with iron phosphate. Its formation is inhibited in DMEM; the presence of amino acids is discussed as the reason
Corrosion behaviour of high temperature alloys in the cooling gas of high temperature reactors

International Nuclear Information System (INIS)

Quadakkers, W.J.; Schuster, H.

1989-01-01

The reactive impurities in the primary cooling helium of advanced high temperature gas cooled reactors (HTGR) can cause oxidation, carburization or decarburization of the heat exchanging metallic components. By studies of the fundamental aspects of the corrosion mechanisms it became possible to define operating conditions under which the metallic construction materials show, from the viewpoint of technical application, acceptable corrosion behaviour. By extensive test programmes with exposure times of up to 30,000 hours, a data base has been obtained which allows a reliable extrapolation of the corrosion effects up to the envisaged service lives of the heat exchanging components. (author). 6 refs, 7 figs
Helium 3 precipitation in AISI 316L stainless steel induced by radioactive decay of tritium: Microstructural study of helium bubble precipitation

International Nuclear Information System (INIS)

Brass, A.M.; Chene, J.

1994-01-01

The development of the thermonuclear technology has given rise to a renewed interest in the study of the behavior of helium in metals. A great amount of work is still required for the understanding of the role of helium on the mechanical properties of structural materials for fusion technology, especially austenitic stainless steels. This article deals with the study of the influence of thermomechanical heat treatments, aging conditions (temperature and time), and helium concentration of helium bubble precipitation in a 316L austenitic steel. Helium was generated by the radioactive decay of tritium (tritium trick). Helium bubbles impede the grain growth in 316L steel aged at 1,373 K and also the recrystallization reaction at this temperature if cold working is performed prior to aging. Transmission electron microscopy (TEM) observations indicated a weak helium precipitation at 1,073 and 1,223 K, presumably due to the presence of trapping sites for tritium, and no bubble growth after aging up to 100 hours. Precipitation sites are mainly dislocations in the matrix at 1,073 K and grain boundaries and individual dislocations in the matrix at 1,223 K. The large bubble size (50 nm) observed at 1,373 K, even for short aging times (0.083), can partly be attributed to bubble dragging by dislocations toward the grain boundaries. Cold deformation prior to aging leads to a larger bubble size due to growth enhancement during recrystallization. Decreasing the helium content leads to a smaller helium bubble size and density. Tritium trapping at helium bubbles may favor helium 3 accumulation on defects such as grain boundaries, as observed by tritium autoradiography
Effect of cold working on the aging and corrosion behavior of Fe-Mn-Al stainless steel

International Nuclear Information System (INIS)

Ghayad, I.M.; Girgis, N.N.; Ghanem, W.; Hamada, A.S.

2004-01-01

The cold working; aging process; and corrosion behavior of the Fe-Mn-Al stainless steel having a composition of Fe-29wt%Mn-3.5wt%Al-0.5wt%C were investigated. Three different groups of specimens of the alloy were subjected to different procedures of cold working and aging. The first group were cold worked then solution treated at 1100 deg. C for 24 hr, coded as CW+ST. The second group were cold worked, solution treated at 1100 deg. C for 24 hr then cold worked again, coded as CW+ST+CW. The third group were solution treated at 1100 deg. C for 24 hr then cold worked, coded as ST+CW. Subsequent aging treatments of the controlled-worked alloy showed age hardening similar to that reported for the solution-treated alloys. The strengthening of the experimental alloy due to the controlled-working and aging is discussed on the basis of microstructural observations and X-ray diffraction analysis. The corrosion behavior of the different groups of the alloy, CW+ST; CW+ST+CW; ST+CW, with their peak aged and over aged conditions has been examined in 3.5% NaCl solution. The electrochemical techniques, potentiodynamic polarization and Tafel plots were employed. All the alloy groups did not passivate in 3.5% NaCl solution and the major corrosion type observed was general corrosion. The peak aged and over aged of the CW+ST+CW exhibited higher corrosion rates due to the formation of ferrite phase that formed a galvanic couple with the austenitic matrix. (authors)
Corrosion behavior of Haynes registered 230 registered nickel-based super-alloys for integrated coal gasification combined cycle syngas plants. A plant exposure study

International Nuclear Information System (INIS)

Lee, Sungkyu; Lee, Jieun; Kang, Suk-Hwan; Lee, Seung-Jong; Yun, Yongseung; Kim, Min Jung

2015-01-01

The corrosion behavior of commercially available Haynes registered 230 registered nickel-based alloy samples was investigated by exposure to coal-gasifying integrated coal gasification combined cycle pilot plant facilities affiliated with the Institute for Advanced Engineering (2.005 MPa and 160-300 C). The morphological and microstructural analyses of the exposed samples were conducted using scanning electron microscopy and energy-dispersive X-ray spectroscopy analysis on the external surface of the recovered corrosion test samples to obtain information of the corrosion scale. These analyses based on the pre- and post-exposure corrosion test samples combined with thermodynamic Ellingham-Pourbaix stability diagrams provided preliminary insight into the mechanism of the observed corrosion behavior prevailing in the piping materials that connected the particulate removal unit and water scrubber of the integrated coal gasification combined cycle pilot plant. Uniform material wastage was observed after 46 hours of operation, and a preliminary corrosion mechanism was suggested: the observed material waste and corrosion behavior of the Haynes registered 230 registered nickel-based alloy samples cut off from the coal syngas integrated coal gasification combined cycle plant were explained by the formation of discontinuous (complex) oxide phases and subsequent chlorine-induced active oxidation under the predominantly reducing environment encountered. This contribution continues the already published studies of the Fe-Ni-Cr-Co alloy Haynes registered 556 registered .
Corrosion Behavior of Ti-13Nb-13Zr and Ti-6Al-4V Alloys for Biomaterial Application

Energy Technology Data Exchange (ETDEWEB)

Saji, Viswanathan S.; Jeong, Yong Hoon; Choe, Han Cheol [Chosun University, Gwangju (Korea, Republic of); Yu, Jin Woo [Shingyeong University, Hwaseong (Korea, Republic of)

2010-02-15

Ti-13Nb-13Zr (TNZ) alloy has attracted considerable research attention in the last decade as a suitable substitute for the commercially used Ti-6Al-4V (TAV) alloy for orthopedic and dental implant applications. Hence, in the present work, a comparative evaluation has been performed on the electrochemical corrosion behavior of TNZ and TAV alloys in 0.9 wt.% NaCl solution. The result of the study showed that both the alloys had similar electrochemical behavior. The corrosion resistance of TAV alloy is found to be marginally superior to that of TNZ alloy.
Corrosion Behavior of Ti-13Nb-13Zr and Ti-6Al-4V Alloys for Biomaterial Application

International Nuclear Information System (INIS)

Saji, Viswanathan S.; Jeong, Yong Hoon; Choe, Han Cheol; Yu, Jin Woo

2010-01-01

Ti-13Nb-13Zr (TNZ) alloy has attracted considerable research attention in the last decade as a suitable substitute for the commercially used Ti-6Al-4V (TAV) alloy for orthopedic and dental implant applications. Hence, in the present work, a comparative evaluation has been performed on the electrochemical corrosion behavior of TNZ and TAV alloys in 0.9 wt.% NaCl solution. The result of the study showed that both the alloys had similar electrochemical behavior. The corrosion resistance of TAV alloy is found to be marginally superior to that of TNZ alloy
Synthesis, mechanical properties and corrosion behavior of powder metallurgy processed Fe/Mg2Si composites for biodegradable implant applications.

Science.gov (United States)

Sikora-Jasinska, M; Paternoster, C; Mostaed, E; Tolouei, R; Casati, R; Vedani, M; Mantovani, D

2017-12-01

Recently, Fe and Fe-based alloys have shown their potential as degradable materials for biomedical applications. Nevertheless, the slow corrosion rate limits their performance in certain situations. The shift to iron matrix composites represents a possible approach, not only to improve the mechanical properties, but also to accelerate and tune the corrosion rate in a physiological environment. In this work, Fe-based composites reinforced by Mg 2 Si particles were proposed. The initial powders were prepared by different combinations of mixing and milling processes, and finally consolidated by hot rolling. The influence of the microstructure on mechanical properties and corrosion behavior of Fe/Mg 2 Si was investigated. Scanning electron microscopy and X-ray diffraction were used for the assessment of the composite structure. Tensile and hardness tests were performed to characterize the mechanical properties. Potentiodynamic and static corrosion tests were carried out to investigate the corrosion behavior in a pseudo-physiological environment. Samples with smaller Mg 2 Si particles showed a more homogenous distribution of the reinforcement. Yield and ultimate tensile strength increased when compared to those of pure Fe (from 400MPa and 416MPa to 523MPa and 630MPa, respectively). Electrochemical measurements and immersion tests indicated that the addition of Mg 2 Si could increase the corrosion rate of Fe even twice (from 0.14 to 0.28mm·year -1 ). It was found that the preparation method of the initial composite powders played a major role in the corrosion process as well as in the corrosion mechanism of the final composite. Copyright © 2017 Elsevier B.V. All rights reserved.

Effect of Precipitate State on Mechanical Properties, Corrosion Behavior, and Microstructures of Al-Zn-Mg-Cu Alloy

Science.gov (United States)

Peng, Xiaoyan; Li, Yao; Xu, Guofu; Huang, Jiwu; Yin, Zhimin

2018-03-01

The mechanical properties, corrosion behavior and microstructures of the Al-Zn-Mg-Cu alloy under various ageing treatments were investigated comparatively. The results show that the tensile strength and corrosion resistance are strongly affected by the precipitate state. Massive fine intragranular precipitates contribute to high strength. Discontinuous coarse grain boundary precipitates containing high Cu content, as well as the narrow precipitate free zone, result in low corrosion susceptibility. After the non-isothermal ageing (NIA) treatment, the tensile strength of 577 MPa is equivalent to that of 579 MPa for the T6 temper. Meanwhile, the stress corrosion susceptibility r tf and the maximum corrosion depth are 97.8% and 23.5 μm, which are comparable to those of 92.8% and 26.7 μm for the T73 temper. Moreover, the total ageing time of the NIA treatment is only 7.25 h, which is much less than that of 48.67 h for the retrogression and re-ageing condition.
Effect of soil compositions on the electrochemical corrosion behavior of carbon steel in simulated soil solution

Energy Technology Data Exchange (ETDEWEB)

Liu, T.M. [College of Materials Science and Engineering, Chongqing University (China); Luo, S.X. [Department of Chemistry, Zunyi Normal College, Zunyi (China); Sun, C. [State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang (China); Wu, Y.H.

2010-04-15

In this study, effect of cations, Ca{sup 2+}, Mg{sup 2+}, K{sup +}, and anions, SO{sub 4}{sup 2-}, HCO{sub 3}{sup -}, NO{sub 3}{sup -} on electrochemical corrosion behavior of carbon steel in simulated soil solution was investigated through potentiodynamic polarization curves and electrochemical impedance spectroscopy. The results indicate that the Ca{sup 2+}and Mg{sup 2+} can decrease the corrosion current density of carbon steel in simulated soil solution, and K{sup +}, SO{sub 4}{sup 2-}, HCO{sub 3}{sup -}, and NO{sub 3}{sup -} can increase the corrosion density. All the above ions in the simulated soil solution can decrease its resistivity, but they have different effect on the charge transfer resistivity. This finding can be useful in evaluating the corrosivity of certain soil through chemical analysis, and provide data for construction engineers. (Abstract Copyright [2010], Wiley Periodicals, Inc.)
Effect of Heat Treatment on Corrosion Behaviors of Mg-5Y-1.5Nd Alloys

Directory of Open Access Journals (Sweden)

Xiumin Ma

2016-01-01

Full Text Available Corrosion behavior of Mg-5Y-1.5Nd alloy was investigated after heat treatment. The microstructure and precipitation were studied by scanning electron microscope (SEM and energy dispersive spectrometer (EDS. The weight loss rates of different samples were arranged as T6-24 h>T6-6 h>T6-14 h>as-cast>T4. The open circuit potential (OCP showed that T4 sample had a more positive potential than that of other samples. The potentiodynamic polarization curves showed that the T6-24 h sample had the highest corrosion current density of 245.362 μA·cm−2, whereas the T4 sample had the lowest at 52.164 μA·cm−2. The EIS results confirmed that the heat treatment reduced the corrosion resistance for Mg-5Y-1.5Nd alloy, because the precipitations acted as the cathode of electrochemical reactions to accelerate the corrosion process. The corrosion rates of different samples were mainly determined by the amount and distribution of the precipitations. The precipitations played dual roles that depended on the amount and distribution. The presence of the phase in the alloys could deteriorate the corrosion performance as it could act as an effective galvanic cathode. Otherwise, a fine and homogeneous phase appeared to be a better anticorrosion barrier.
Corrosion behavior of environmental assessment glass in product consistency tests of extended duration

International Nuclear Information System (INIS)

Bates, J.K.; Buck, E.C.; Ebert, W.L.; Luo, J.S.; Tam, S.W.

1998-01-01

We have conducted static dissolution tests to study the corrosion behavior of the Environmental Assessment (EA) glass, which is the benchmark glass for high-level waste glasses being produced at US Department of Energy facilities. These tests were conducted to evaluate the behavior of the EA glass under the same long-term and accelerated test conditions that are being used to evaluate the corrosion of waste glasses. Tests were conducted at 90 C in a tuff groundwater solution at glass surface area/solution volume (WV) ratios of about 2000 and 20,000 m -1 . The glass dissolved at three distinct dissolution rates in tests conducted at 2000 m -1 . Based on the release of boron, dissolution within the first seven days occurred at a rate of about 0.65 g/(m 2 · d). The rate between seven and 70 days decreased to 0.009 g/(m 2 · d). An increase in the dissolution rate occurred at longer times after the precipitation of zeolite phases analcime, gmelinite, and an aluminum silicate base. The dissolution rate after phase formation was about 0.18 g/(m 2 · d). The formation of the same zeolite alteration phases occurred after about 20 days in tests at 20,000 m - . The average dissolution rate over the first 20 days was 0.5 g/(m 2 · d) and the rate after phase formation was about 0.20 g/(m 2 · d). An intermediate stage with a lower rate was not observed in tests at 20,000 m -1 . The corrosion behavior of EA glass is similar to that observed for other high-level waste glasses reacted under the same test conditions. The dissolution rate of EA glass is higher than that of other high-level waste glasses both in 7-day tests and after alteration phases form
Understanding the corrosion behavior of isomorphous Cu–Ni alloy from its electron work function

Energy Technology Data Exchange (ETDEWEB)

Huang, X.C.; Lu, H.; Li, D.Y., E-mail: dongyang.li@ualberta.ca

2016-04-15

The electrode potential or galvanic series is usually used to reflect the nobility of metals and semi-metals. However, this potential is environment-dependent and the intrinsic nobility of a metal is ultimately governed by its electron stability, which can be represented by the electron work function (EWF). This article reports our studies on the corrosion behavior of isomorphous Cu–Ni alloy in HCl and NaCl solutions, respectively. It was demonstrated that the EWF of the alloy increased as the Ni concentration was increased, so did the corrosion resistance in the acidic solution. In the sodium chloride solution, however, the trend was reversed due to adsorption, hydrolysis and the formation of oxide scale on Cu-rich samples, which more or less prevented them from further corrosion in this solution. In order to confirm this, corrosive wear tests were performed to analyze the performance of the alloy when the effect of oxide scale was eliminated or minimized by the mechanical action. - Highlights: • Increasing %Ni resulted in higher overall electron work function of Cu–Ni alloy. • Higher EWF corresponded to higher resistance to corrosion in a HCl solution. • Trend was reversed in a NaCl solution due to the formation of oxide scale. • During slurry-jet tests, alloys with higher EWFs performed better.
Understanding the corrosion behavior of isomorphous Cu–Ni alloy from its electron work function

International Nuclear Information System (INIS)

Huang, X.C.; Lu, H.; Li, D.Y.

2016-01-01

The electrode potential or galvanic series is usually used to reflect the nobility of metals and semi-metals. However, this potential is environment-dependent and the intrinsic nobility of a metal is ultimately governed by its electron stability, which can be represented by the electron work function (EWF). This article reports our studies on the corrosion behavior of isomorphous Cu–Ni alloy in HCl and NaCl solutions, respectively. It was demonstrated that the EWF of the alloy increased as the Ni concentration was increased, so did the corrosion resistance in the acidic solution. In the sodium chloride solution, however, the trend was reversed due to adsorption, hydrolysis and the formation of oxide scale on Cu-rich samples, which more or less prevented them from further corrosion in this solution. In order to confirm this, corrosive wear tests were performed to analyze the performance of the alloy when the effect of oxide scale was eliminated or minimized by the mechanical action. - Highlights: • Increasing %Ni resulted in higher overall electron work function of Cu–Ni alloy. • Higher EWF corresponded to higher resistance to corrosion in a HCl solution. • Trend was reversed in a NaCl solution due to the formation of oxide scale. • During slurry-jet tests, alloys with higher EWFs performed better.
Corrosion behavior induced by LiCl-KCl in type 304 and 316 stainless steel and copper at low temperature

Energy Technology Data Exchange (ETDEWEB)

Sim, Jee Hyung; Kim, Yong Soo; Cho, Il Je [Dept. of Nuclear Engineering, Hanyang University, Seoul (Korea, Republic of)

2017-06-15

The corrosion behavior of stainless steel (304 and 316 type) and copper induced by LiCl-KCl at low temperatures in the presence of sufficient oxygen and moisture was investigated through a series of experiments (at 30°C, 40°C, 60°C, and 80°C for 24 hours, 48 hours, 72 hours, and 96 hours). The specimens not coated on one side with an aqueous solution saturated with LiCl-KCl experienced no corrosion at any temperature, not even when the test duration exceeded 96 hours. Stainless steel exposed to LiCl-KCl experienced almost no corrosion below 40°C, but pitting corrosion was observed at temperatures above 60°C. As the duration of the experiment was increased, the rate of corrosion accelerated in proportion to the temperature. The 316 type stainless steel exhibited better corrosion resistance than did the 304 type. In the case of copper, the rate of corrosion accelerated in proportion to the duration and temperature but, unlike the case of stainless steel, the corrosion was more general. As a result, the extent of copper corrosion was about three times that of stainless steel.
Corrosion behavior of the tube - tubular plate joint zone in the presence of sediments

International Nuclear Information System (INIS)

Lucan, D.; Fulger, M.; Pirvan, I.; Cotolan, V.

1997-01-01

The corrosion is a very important problem which concerns the safe operation of steam generators. The predominant part of corrosion problems is related to the local concentration of aggressive species and/or to the impurities from the slow-flow regions, like those created by cracks in tube - tubular plate joint zones. The consequences of such local concentrations are very important and as such entail interest in the design and utilization of steam generators. This study presents the results of the corrosion tests performed under specific operation conditions of the secondary circuit in NPP (temperature, 260 o C; pressure, 5.1 MPa) on a crack simulating device made of carbon steel SA 508 cl.2 (forming the tubular plate) and Incoloy-800 (forming the tubes). The chemical medium of these tests was the following: solution of NaCl, 25g/l (pH=10.5); solution of NaCl, 50 g/l (pH=10.5); solution of NaCl, 75g/l (pH=10.5); solution of NaCl, 75g/l + solution of Na 2 SO 4 , 10 g/l (pH=10.5). The behavior of these two materials to corrosion was studied by metallographic investigations. The results are presented as microphotographs evidencing the occurrence of pitting corrosion first on material of the tubular plate, in the presence of medium particularly aggressive and on the material of the tubes. The aim of this study is to establish the corrosion mechanism as well as the formation of the oxide layer on the carbon steel in crack simulating devices. (authors)
Corrosion behavior of Ni-based structural materials for electrolytic reduction in lithium molten salt

Energy Technology Data Exchange (ETDEWEB)

Cho, Soo Haeng, E-mail: nshcho1@kaeri.re.kr [Korea Atomic Energy Research Institute, 1045 Daedeokdaero Yuseong-gu, Daejeon 305-353 (Korea, Republic of); Park, Sung Bin [Korea Atomic Energy Research Institute, 1045 Daedeokdaero Yuseong-gu, Daejeon 305-353 (Korea, Republic of); Lee, Jong Hyeon, E-mail: jonglee@cnu.ac.kr [Graduate School of Green Energy Technology, Chungnam National University, 79 Daehak-ro, Yuseong-gu, Daejeon 305-764 (Korea, Republic of); Hur, Jin Mok; Lee, Han Soo [Korea Atomic Energy Research Institute, 1045 Daedeokdaero Yuseong-gu, Daejeon 305-353 (Korea, Republic of)

2011-05-01

In this study, the corrosion behavior of new Ni-based structural materials was studied for electrolytic reduction after exposure to LiCl-Li{sub 2}O molten salt at 650 deg. C for 24-216 h under an oxidizing atmosphere. The new alloys with Ni, Cr, Al, Si, and Nb as the major components were melted at 1700 deg. C under an inert atmosphere. The melt was poured into a preheated metallic mold to prepare an as-cast alloy. The corrosion products and fine structures of the corroded specimens were characterized by scanning electron microscope (SEM), Energy Dispersive X-ray Spectroscope (EDS), and X-ray diffraction (XRD). The corrosion products of as cast and heat treated low Si/high Ti alloys were Cr{sub 2}O{sub 3}, NiCr{sub 2}O{sub 4}, Ni, NiO, and (Al,Nb,Ti)O{sub 2}; those of as cast and heat treated high Si/low Ti alloys were Cr{sub 2}O{sub 3}, NiCr{sub 2}O{sub 4}, Ni, and NiO. The corrosion layers of as cast and heat treated low Si/high Ti alloys were continuous and dense. However, those of as cast and heat treated high Si/low Ti alloys were discontinuous and cracked. Heat treated low Si/high Ti alloy showed the highest corrosion resistance among the examined alloys. The superior corrosion resistance of the heat treated low Si/high Ti alloy was attributed to the addition of an appropriate amount of Si, and the metallurgical evaluations were performed systematically.
Microstructural characterization and electrochemical corrosion behavior of Incoloy 800 in sulphate and chloride solutions

International Nuclear Information System (INIS)

Mansur, Fabio Abud; Schvartzman, Monica Maria de Abreu Mendonca; Campos, Wagner Reis da Costa; Aguiar, Antonio Eugenio de; Chaim, Marcos Souza

2011-01-01

Corrosion has been the major cause of tube failures in steam generators (SG) tubes in nuclear power plants. Problems have resulted from impurities in the secondary water systems which are originated from leaks of cooling water. It is important to understand the compatibility of steam generator tube materials with the environment. This study presents the microstructural characterization and electrochemical behavior of the Incoloy 800 in sodium chloride and sodium sulphate aqueous solutions at 80 degree C. Potentiodynamic anodic polarization, cyclic polarization and open circuit potential (OCP) measurements were the electrochemical techniques applied in this work. The pitting resistance of Incoloy 800 in chloride plus sulphate mixtures were also examined. Experiments performed in solutions with different concentrations of Cl- and SO 4 2- ions in solution (200 ppb, 500 ppb, 1ppm, 5 ppm, 50 ppm and 100 ppm) showed that this concentrations range had no substantial effect on the anodic behavior of the alloy. After polarization no localized corrosion was found on the samples. (author)
Localized Corrosion Behavior of Type 304SS with a Silica Layer Under Atmospheric Corrosion Environments

International Nuclear Information System (INIS)

E. Tada; G.S. Frankel

2006-01-01

The U.S. Department of Energy (DOE) has proposed a potential repository for spent nuclear fuel and high-level radioactive waste at the Yucca Mountain site in Nevada. [I] The temperature could be high on the waste packages, and it is possible that dripping water or humidity could interact with rock dust particulate to form a thin electrolyte layer with concentrated ionic species. Under these conditions, it is possible that highly corrosion-resistant alloys (CRAs) used as packages to dispose the nuclear waste could suffer localized corrosion. Therefore, to better understand long-term corrosion performance of CRAs in the repository, it is important to investigate localized corrosion under a simulated repository environment. We measured open circuit potential (OCP) and galvanic current (i g ) for silica-coated Type 304SS during drying of salt solutions under controlled RH environments to clarify the effect of silica layer as a dust layer simulant on localized corrosion under atmospheric environments. Type 304SS was used as a relatively susceptible model CRA instead of the much more corrosion resistant alloys, such as Alloy 22, that are being considered as, waste package materials
Evaluation of the corrosion behavior of the al-356 alloy in NaCl solutions

Directory of Open Access Journals (Sweden)

Mauricio Vásquez Rendón

2011-01-01

Full Text Available Cellular metals are a new class of materials with promising applications and a unique combination of physical, chemical and mechanical properties. The Al-356 alloy is used to manufacture metal foams from NaCl preforms. Despite the usefulness of these materials, their performance may be affected by corrosion due to residual salt. This paper reports the study of the behavior of the Al-356 alloy in chloride solutions by electrochemical techniques in rotating disk electrode. The cathodic reaction of oxygen reduction is the crucial stage of process dissolution of the material, which shows that is the oxygen transport which limits the corrosion process.
Study of the corrosion behavior of magnesium alloy weldings in NaCl solutions by gravimetric tests

Directory of Open Access Journals (Sweden)

Segarra, José A.

2015-09-01

Full Text Available In this article, the corrosion behavior of commercial AZ31 welded plates in aqueous chloride media was investigated by means of gravimetric techniques and Neutral Salt Spray tests (NSS. The AZ31 samples tested were welded using Gas Tugsten Arc Welding (GTAW and different filler materials. Material microstructures were investigated by optical microscopy to stablish the influence of those microstructures in the corrosion behavior. Gravimetric and NSS tests indicate that the use of more noble filler alloys for the sample welding, preventing the reduction of aluminum content in weld beads, does not imply a better corrosion behavior.En este artículo se ha investigado el comportamiento frente a la corrosión en medios acuosos salinos de chapas soldadas de aleación AZ31 mediante técnicas gravimétricas y ensayo en cámara de niebla salina. Las muestras estudiadas han sido soldadas mediante soldadura TIG (Tungsten Inert Gas y con diferentes materiales de aporte. En el estudio se ha empleado microscopía óptica para analizar la microestructura. Los ensayos de gravimetría y los ensayos de niebla salina indican que el empleo de materiales de aporte más nobles para soldar las muestras evitando la disminución del contenido en aluminio en los cordones, no implica un mejor comportamiento frente a la corrosión.
Corrosion and nanomechanical behaviors of plasma electrolytic oxidation coated AA7020-T6 aluminum alloy

Energy Technology Data Exchange (ETDEWEB)

Venugopal, A., E-mail: arjun_venu@hotmail.com [Materials and Metallurgy Group, Materials and Mechanical Entity, Vikram Sarabhai Space Centre, Thiruvananthapuram (India); Srinath, J. [Materials and Metallurgy Group, Materials and Mechanical Entity, Vikram Sarabhai Space Centre, Thiruvananthapuram (India); Rama Krishna, L. [International Advanced Research Centre for Powder Metallurgy and New Materials (ARCI), Balapur P.O., Hyderabad 500005 (India); Ramesh Narayanan, P.; Sharma, S.C.; Venkitakrishnan, P.V. [Materials and Metallurgy Group, Materials and Mechanical Entity, Vikram Sarabhai Space Centre, Thiruvananthapuram (India)

2016-04-13

Alumina coating was deposited on AA7020 aluminum alloy by plasma electrolytic oxidation (PEO) method. The corrosion, stress corrosion cracking (SCC) and nano-mechanical behaviors were examined by means of potentiodynamic polarization, slow strain rate test (SSRT) and nano-indentation tests. Potentiodynamic polarization (PP) was used to evaluate the corrosion resistance of the coating and slow strain rate test (SSRT) was used for evaluating the environmental cracking resistance in 3.5% NaCl solution. The mechanical properties (hardness and elastic modulus) were obtained from each indentation as a function of the penetration depth across the coating cross section. The above results were compared with similar PEO coated aluminum and magnesium alloys. Results indicated that PEO coating on AA7020 alloy significantly improved the corrosion resistance. However the environmental cracking resistance was found to be only marginal. The hardness and elastic modulus values were found to be much higher when compared to the base metal and similar PEO coated 7075 aluminum alloys. The fabricated coating also exhibited good adhesive strength with the substrate similar to other PEO coated aluminum alloys reported in the literature.
Effect of pulsed gas tungsten arc welding on corrosion behavior of Ti-6Al-4V titanium alloy

Energy Technology Data Exchange (ETDEWEB)

Balasubramanian, M. [Department of Mechanical Engineering, Maamallan Institute of Technology, Anna University, Sriperumpudur 602 105 (India)], E-mail: manianmb@rediffmail.com; Jayabalan, V. [Department of Manufacturing Engineering, Anna University, Guindy, Chennai 600 025 (India)], E-mail: jbalan@annauniv.edu; Balasubramanian, V. [Department of Manufacturing Engineering, Annamalai University, Annamalai Nagar 608 002 (India)], E-mail: visvabalu@yahoo.com

2008-07-01

Due to the excellent combination of properties such as elevated strength-to-weight ratio, high toughness and excellent resistance to corrosion, make titanium alloys attractive for many industrial applications. Advantages of pulsed current welding frequently reported in literature include refinement of fusion zone grain size, etc. Hence, in this investigation an attempt has been made to study the effect of pulsed current Gas Tungsten Arc (GTA) welding parameters on corrosion behavior of Ti-6Al-4V titanium alloy. Pulsed current gas tungsten arc welding was used to fabricate the joints. To optimize the number of experiments to be performed, central composite design was used. The investigation revealed increase in corrosion resistance with increase in peak current and pulse frequency up to an optimum value of the same and decrease in corrosion resistance beyond that optimum point. An increase in corrosion resistance with grain refinement was also detected.
Effect of pulsed gas tungsten arc welding on corrosion behavior of Ti-6Al-4V titanium alloy

International Nuclear Information System (INIS)

Balasubramanian, M.; Jayabalan, V.; Balasubramanian, V.

2008-01-01

Due to the excellent combination of properties such as elevated strength-to-weight ratio, high toughness and excellent resistance to corrosion, make titanium alloys attractive for many industrial applications. Advantages of pulsed current welding frequently reported in literature include refinement of fusion zone grain size, etc. Hence, in this investigation an attempt has been made to study the effect of pulsed current Gas Tungsten Arc (GTA) welding parameters on corrosion behavior of Ti-6Al-4V titanium alloy. Pulsed current gas tungsten arc welding was used to fabricate the joints. To optimize the number of experiments to be performed, central composite design was used. The investigation revealed increase in corrosion resistance with increase in peak current and pulse frequency up to an optimum value of the same and decrease in corrosion resistance beyond that optimum point. An increase in corrosion resistance with grain refinement was also detected
Adsorption behavior of caffeine as a green corrosion inhibitor for copper

Energy Technology Data Exchange (ETDEWEB)

Souza, Fernando Silvio de [Grupo de Estudos de Processos Eletroquimicos e Eletroanaliticos, Departamento de Quimica, Universidade Federal de Santa Catarina, 88040-900, Florianopolis, SC (Brazil); Giacomelli, Cristiano [Departamento de Quimica, Universidade Federal de Santa Maria, Av. Roraima 1000, 97119-900, Santa Maria, RS (Brazil); Goncalves, Reinaldo Simoes [Universidade Federal do Rio Grande do Sul, Av. Bento Goncalves 9500, 91501-970, Porto Alegre, RS (Brazil); Spinelli, Almir, E-mail: almir.spinelli@ufsc.br [Grupo de Estudos de Processos Eletroquimicos e Eletroanaliticos, Departamento de Quimica, Universidade Federal de Santa Catarina, 88040-900, Florianopolis, SC (Brazil)

2012-12-01

Electrochemical and impedance experiments were carried out to evaluate the corrosion behavior of copper in aerated 0.1 mol L{sup -1} H{sub 2}SO{sub 4} solutions in the presence of three xanthine derivatives with similar chemical structures. The corrosion rate of copper was found to increase in the presence of theophylline and theobromine and decrease in the presence of caffeine. The adsorption and inhibitory effect of caffeine on copper surfaces in aerated 0.1 mol L{sup -1} H{sub 2}SO{sub 4} solutions were then investigated in detail by potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), contact angle measurements, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDS) and fluorescence experiments. The data obtained indicate that caffeine behaves as a cathodic-type inhibitor adsorbing onto the copper surface according to the Temkin isotherm, with the negative Increment G Degree-Sign {sub ads} value of - 31.1 kJ mol{sup -1} signifying a spontaneous adsorption process. The corrosion inhibition efficiency increased with caffeine concentration in the range of 1.0-10.0 mmol L{sup -1}. Furthermore, the EIS results obtained at the open-circuit potential and surface analysis (SEM, EDS and fluorescence) clearly demonstrated the adsorption of the organic compound onto the copper electrode. The contact angle measurements revealed the formation of a hydrophobic protective film. This film covers up to 72% of the total active surface, acts as a protective barrier and prevents interaction between the metal, water and oxygen molecules. - Highlights: Black-Right-Pointing-Pointer We have investigated the adsorption and corrosion inhibition of caffeine on copper surfaces. Black-Right-Pointing-Pointer Caffeine behaves as a cathodic-type inhibitor. Black-Right-Pointing-Pointer Caffeine adsorbs onto copper surface according to Temkin isotherm. Black-Right-Pointing-Pointer There exists the formation of a hydrophobic film that acts as a
Study on the Microstructure, Mechanical Properties and Corrosion Behavior of Mg-Zn-Ca Alloy Wire for Biomaterial Application

Science.gov (United States)

Zheng, Maobo; Xu, Guangquan; Liu, Debao; Zhao, Yue; Ning, Baoqun; Chen, Minfang

2018-03-01

Due to their excellent biocompatibility and biodegradability, magnesium alloy wires have attracted much attention for biomaterial applications including orthopedic K-wires and sutures in wound closure. In this study, Mg-3Zn-0.2Ca alloy wires were prepared by cold drawing combined with proper intermediate annealing process. Microstructures, texture, mechanical properties and corrosion behavior of Mg-3Zn-0.2Ca alloy wire in a simulated body fluid were investigated. The results showed that the secondary phase and average grain size of the Mg-3Zn-0.2Ca alloy were refined in comparison with the as-extruded alloy and a strong (0002)//DD basal fiber texture system was formed after multi-pass cold drawing. After the annealing, most of the basal planes were tilted to the drawing direction (DD) by about 35°, presenting the characteristics of random texture, and the texture intensity decreased. The as-annealed wire shows good mechanical properties with the ultimate tensile strength (UTS), yield strength (YS) and elongation of 253 ± 8.5 MPa, 212 ± 11.3 MPa and 9.2 ± 0.9%, respectively. Electrochemical and hydrogen evolution measurements showed that the corrosion resistance of the Mg-3Zn-0.2Ca alloy wire was improved after the annealing. The immersion test indicated that the Mg-3Zn-0.2Ca wire exhibited uniform corrosion behavior during the initial period of immersion, but then exhibited local corrosion behavior.
Humid-air and aqueous corrosion models for corrosion-allowance barrier material

International Nuclear Information System (INIS)

Lee, J.H.; Atkins, J.E.; Andrews, R.W.

1995-01-01

Humid-air and aqueous general and pitting corrosion models (including their uncertainties) for the carbon steel outer containment barrier were developed using the corrosion data from literature for a suite of cast irons and carbon steels which have similar corrosion behaviors to the outer barrier material. The corrosion data include the potential effects of various chemical species present in the testing environments. The atmospheric corrosion data also embed any effects of cyclic wetting and drying and salts that may form on the corroding specimen surface. The humid-air and aqueous general corrosion models are consistent in that the predicted humid-air general corrosion rates at relative humidities between 85 and 100% RH are close to the predicted aqueous general corrosion rates. Using the expected values of the model parameters, the model predicts that aqueous pitting corrosion is the most likely failure mode for the carbon steel outer barrier, and an earliest failure (or initial pit penetration) of the 100-mm thick barrier may occur as early as about 500 years if it is exposed continuously to an aqueous condition at between 60 and 70 degrees C
Development of an Agent-based Model to Analyze Contemporary Helium Markets

Energy Technology Data Exchange (ETDEWEB)

Riddle, Matthew E. [Argonne National Lab. (ANL), Argonne, IL (United States); Uckun, Canan [Argonne National Lab. (ANL), Argonne, IL (United States); Conzelmann, Guenter [Argonne National Lab. (ANL), Argonne, IL (United States); Macal, Charles M. [Argonne National Lab. (ANL), Argonne, IL (United States)

2016-02-01

Although U.S. helium demand has remained relatively flat since 2009, exports of helium have increased significantly since then, driven primarily by demand for electronic and semiconductor manufacturing in Asia. In the midst of this global demand shift, the Helium Act dictates a new procedure for pricing and distributing the gas through a reserve that historically functioned as a loose “oligarchy.” The new procedure requires prices to be determined by the open market through auctions and a survey of market prices, as opposed to increasing prices according to the consumer price index. Response to these changes has caused temporary shortages, price increases, and a significant increase in the development of the helium extraction technologies used to produce helium from formerly marginal sources. Technologies are being developed and refined to extract helium from formerly low-yielding natural gas fields containing much lower amounts of helium than the previously considered economic threshold of 0.3%. Combining these transformative policies with the potential for new and significant global supplies from Qatar, Algeria, and Russia could lead to new and unforeseen market behaviors and reactions from global helium markets. The objective of the project is to analyze the global helium markets.

Electrochemical corrosion behavior of MSIP Ni coating on depleted uranium surface

International Nuclear Information System (INIS)

Chen Lin; Li Kexue; Wang Qingfu; Wang Xiaohong; Guan Weijun

2014-01-01

The Ni film was prepared by magnetron sputtering ion plating to improve the corrosion resistance of depleted uranium. The corrosion resistance of the Ni film was examined by electrochemical corrosion station. The results show that the Ni film corrosion potential is -100.8 mV, whereas it is -641.2 mV for depleted uranium in 50 μg/g KCl solution. The Ni film is a barrier to protect the depleted uranium substrate avoiding the corrosive media attack. The Ni film polarization resistance and impedance are much higher, while the corrosion current density is much lower contrast with depleted uranium. None crack or flake is found through 70 h corrosion. The corrosion resistance and corrosion current keep stable. It is indicated that the corrosion resistance of depleted uranium is effectively improved after deposited Ni film by magnetron sputtering ion plating. (authors)
Effect of H{sub 2}O{sub 2} on the corrosion behavior of 304L stainless steel

Energy Technology Data Exchange (ETDEWEB)

Song, Taek Ho

1994-02-15

In connection with the safe storage of high level nuclear waste, effect of H{sub 2}O{sub 2} on the corrosion behavior of 304L stainless steel was examined. Open circuit potentials and polarization curves were measured with and without H{sub 2}O{sub 2}. The experimental results show that H{sub 2}O{sub 2} increased corrosion potential and decreased pitting potential. The passive range, therefore, decreased as H{sub 2}O{sub 2} concentration increased, indicating that pitting resistance was decreased by the existence of H{sub 2}O{sub 2} in the electrolyte. These effects of H{sub 2}O{sub 2} on corrosion of 304L stainless steel are considered to be similar to those of γ-irradiation. To compare the effects of H{sub 2}O{sub 2} with those of O{sub 2}, cathodic and anodic polarization curves were made in three types of electrolyte such as aerated, deaerated, and stirred electrolyte. The experimental results show that the effects of H{sub 2}O{sub 2} on the corrosion behavior were very similar to those of O{sub 2} such as increase of corrosion potential, decrease of pitting resistance, and increase of repassivation potential. Further, H{sub 2}O{sub 2} played much greater role in controlling cathodic reaction rate in neutral water environment. In acid and alkaline media, potential shifts by H{sub 2}O{sub 2} were restricted by the large current density of proton reduction and by the le Chatelier's principle respectively.
A Study on the Corrosion Behavior of Carbon Steel Exposed to a H2S-Containing NH4Cl Medium

Science.gov (United States)

Wang, Hai-bo; Li, Yun; Cheng, Guang-xu; Wu, Wei; Zhang, Yao-heng

2018-04-01

NH4Cl corrosion failure often occurs in the overhead systems of hydrotreaters, and this failure is always accompanied by the appearance of H2S. A combination of electrochemical and surface spectroscopic (SEM/EDS, AFM, XRD) techniques was used to investigate the effect of different factors, including the surface roughness, temperature, dissolved oxygen, pH and H2S concentration, on the corrosion behavior of carbon steel in an NH4Cl environment with the presence of H2S. The effect of H2S concentrations (at the ppm level) on the corrosion behavior of carbon steel was systematically revealed. The experimental results clearly indicated that the corrosion rate reached a minimum value at 10 ppm H2S. The steel surface was covered by a uniform corrosion product film in a 10 ppm H2S environment, and the corrosion product film was tight and protective. The ammonia from NH4Cl helped maintaining the protectiveness of the corrosion films in this environment. Dissolved oxygen mainly accelerated the cathodic reaction. The cathodic limiting current density increased with increasing temperature, and the anodic branch polarization curves were similar at different temperatures. The anodic current density decreased as the pH decreased, and the cathodic current density increased as the pH decreased. The absolute surface roughness (R a) of carbon steel increased from 132.856 nm at 72 h to 153.973 nm at 144 h, and the rougher surface resulted in a higher corrosion rate. The critical innovation in this research was that multiple influential factors were revealed in the NH4Cl environment with the presence of H2S.
A Study on the Corrosion Behavior of Carbon Steel Exposed to a H2S-Containing NH4Cl Medium

Science.gov (United States)

Wang, Hai-bo; Li, Yun; Cheng, Guang-xu; Wu, Wei; Zhang, Yao-heng

2018-05-01

NH4Cl corrosion failure often occurs in the overhead systems of hydrotreaters, and this failure is always accompanied by the appearance of H2S. A combination of electrochemical and surface spectroscopic (SEM/EDS, AFM, XRD) techniques was used to investigate the effect of different factors, including the surface roughness, temperature, dissolved oxygen, pH and H2S concentration, on the corrosion behavior of carbon steel in an NH4Cl environment with the presence of H2S. The effect of H2S concentrations (at the ppm level) on the corrosion behavior of carbon steel was systematically revealed. The experimental results clearly indicated that the corrosion rate reached a minimum value at 10 ppm H2S. The steel surface was covered by a uniform corrosion product film in a 10 ppm H2S environment, and the corrosion product film was tight and protective. The ammonia from NH4Cl helped maintaining the protectiveness of the corrosion films in this environment. Dissolved oxygen mainly accelerated the cathodic reaction. The cathodic limiting current density increased with increasing temperature, and the anodic branch polarization curves were similar at different temperatures. The anodic current density decreased as the pH decreased, and the cathodic current density increased as the pH decreased. The absolute surface roughness ( R a) of carbon steel increased from 132.856 nm at 72 h to 153.973 nm at 144 h, and the rougher surface resulted in a higher corrosion rate. The critical innovation in this research was that multiple influential factors were revealed in the NH4Cl environment with the presence of H2S.
SRB seawater corrosion project

Science.gov (United States)

Bozack, M. J.

1991-01-01

The corrosion behavior of 2219 aluminum when exposed to seawater was characterized. Controlled corrosion experiments at three different temperatures (30, 60 and 100 C) and two different environments (seawater and 3.5 percent salt solution) were designed to elucidate the initial stages in the corrosion process. It was found that 2219 aluminum is an active catalytic surface for growth of Al2O3, NaCl, and MgO. Formation of Al2O3 is favored at lower temperatures, while MgO is favored at higher temperatures. Visible corrosion products are formed within 30 minutes after seawater exposure. Corrosion characteristics in 3.5 percent salt solution are different than corrosion in seawater. Techniques utilized were: (1) scanning electron microscopy, (2) energy dispersive x-ray spectroscopy, and (3) Auger electron spectroscopy.
Corrosion-electrochemical behavior of nickel in an alkali metal carbonate melt under a chlorine-containing atmosphere

Science.gov (United States)

Nikitina, E. V.; Kudyakov, V. Ya.; Malkov, V. B.; Plaksin, S. V.

2013-08-01

The corrosion-electrochemical behavior of a nickel electrode is studied in the melt of lithium, sodium, and potassium (40: 30: 30 mol %) carbonates in the temperature range 500-600°C under an oxidizing atmosphere CO2 + 0.5O2 (2: 1), which is partly replaced by gaseous chlorine (30, 50, 70%) in some experiments. In other experiments, up to 5 wt % chloride of sodium peroxide is introduced in a salt melt. A change in the gas-phase composition is shown to affect the mechanism of nickel corrosion.
Microbially influenced corrosion of stainless steel by marine bacterium Vibrio natriegens: (I) Corrosion behavior

Energy Technology Data Exchange (ETDEWEB)

Cheng Sha; Tian Jintao [Institute of Materials Science and Engineering, Ocean University of China, Qingdao 266100 (China); Chen Shougang, E-mail: sgchen@ouc.edu.cn [Institute of Materials Science and Engineering, Ocean University of China, Qingdao 266100 (China); Lei Yanhua; Chang Xueting; Liu Tao [Institute of Materials Science and Engineering, Ocean University of China, Qingdao 266100 (China); Yin Yansheng, E-mail: yys2006@ouc.edu.cn [Institute of Materials Science and Engineering, Ocean University of China, Qingdao 266100 (China)

2009-04-30

The microbially influenced corrosion of stainless steel (SS) by marine bacterium Vibrio natriegens (V. natriegens) was investigated using surface analysis (atomic force microscopy (AFM), scanning electron microscopy (SEM), and energy dispersive X-ray analysis (EDXA)) and electrochemical techniques (the open circuit potential, electrochemical impedance spectroscopy (EIS), and potentiodynamic polarization curves ). AFM images corroborated the results from the EIS models which show biofilm attachment and subsequent detachment over time. The SEM images revealed the occurrence of micro-pitting corrosion underneath the biofilms on the metal surface after the biofilm removal. The presence of carbon, oxygen, phosphor and sulfur obtained from EDXA proved the formation of biofilm. The electrochemical results showed that the corrosion of SS was accelerated in the presence of V. natriegens based on the decrease in the resistance of the charge transfer resistance (R{sub ct}) obtained from EIS and the increase in corrosion current densities obtained from potentiodynamic polarization curves.
Comparison of Corrosion Behavior of Low-Alloy Steel Containing Copper and Antimony with 409L Stainless Steel for a Flue Gas Desulfurization System

Energy Technology Data Exchange (ETDEWEB)

Park, Sun-Ah; Shin, Su-Bin; Kim, Jung-Gu [Sungkyunkwan University, Suwon (Korea, Republic of)

2016-07-15

The corrosion behavior of low alloy steel containing Cu, Sb and 409L stainless steel was investigated for application in the low-temperature section of a flue gas desulfurization (FGD) system. The electrochemical properties were evaluated by potentiodynamic polarization testing and electrochemical impedance spectroscopy (EIS) in 16.9 vol% H{sub 2}SO{sub 4} + 0.35 vol% HCl at 60 ℃. The inclusions in these steels ere identified by electron probe microanalyzer (EPMA). The corrosion products of the steels were analyzed using scanning electron microscope (SEM) with energy dispersive spectroscopy (EDS) and transmission electron microscopy (TEM). The corrosion rate of the low alloy steel containing Cu, Sb was about 100 times lower than that of 409L stainless steel. For stainless steel without passivation, active corrosion behavior was shown. In contrast, in the low alloy steel, the Cu, Sb compounds accumulated on the surface improved the corrosion resistance by suppressing the anodic dissolution reaction.
Radiation damage in gallium-stabilized δ-plutonium with helium bubbles

Energy Technology Data Exchange (ETDEWEB)

Wu, FengChao [CAS Key Laboratory of Mechanical Behavior and Design of Materials, Department of Modern Mechanics, University of Science and Technology of China, Hefei, Anhui 230027 (China); Wang, Pei [Laboratory of Computational Physics, Institute of Applied Physics and Computational Mathematics, Beijing 100094 (China); Liu, XiaoYi [CAS Key Laboratory of Mechanical Behavior and Design of Materials, Department of Modern Mechanics, University of Science and Technology of China, Hefei, Anhui 230027 (China); Wu, HengAn, E-mail: wuha@ustc.edu.cn [CAS Key Laboratory of Mechanical Behavior and Design of Materials, Department of Modern Mechanics, University of Science and Technology of China, Hefei, Anhui 230027 (China)

2017-02-15

To understand the role of helium on self-irradiation effects in δ-plutonium, microstructure evolutions due to α-decay events near pre-existing helium bubbles in gallium-stabilized δ-plutonium are investigated using molecular dynamics simulations. Bubble promoting effect plays a dominating role in point defects production, resulting in increasing number of point defects. When lightweight helium atoms act as media, energy transfer discrepancy and altered spatial morphology of point defects induced by mass effect are revealed. The evolution of stacking faults surrounding the disordered core is studied and their binding effect on the propagation of point defects are presented. The cascade-induced bubble coalescence, resolution and re-nucleation driven by internal pressure are obtained in the investigation on helium behaviors. The intrinsic tendency in our simulated self-irradiation with helium bubbles is significant for understanding the underlying mechanism of aging in plutonium and its alloys.
Creep properties of Hastelloy X in a carburizing helium environment

International Nuclear Information System (INIS)

Nakanishi, T.; Kawakami, H.

1982-01-01

In this work, we investigate the environmental effect on the creep behavior of Hastelloy X at 900 0 C in helium and air. Since helium coolant in HTGR is expected to be carburizing and very weakly oxidizing for most metals, testings were focused on the effect of carburizing and slight oxidation. Carburization decreases secondary creep strain rate and delays tertiary creep initiation. On the other hand, the crack growth rate on the specimen surface is enhanced due to very weak oxidation in helium, therefore the tertiary creep strain rate becomes larger than that in air. The rupture time of Hastelloy X was shorter in helium when compared with in air. Stress versus rupture time curves for both environments do not deviate with each other during up to 5000 hours test, and a ratio of rupture stress in helium to that in air was about 0.9
The corrosion behavior of molybdenum and Hastelloy B in sulfur and sodium polysulfides at 623 K

International Nuclear Information System (INIS)

Brown, A.P.

1987-01-01

An experimental study was completed to determine the corrosion behavior of molybdenum and Hastelloy B, a nickel-based alloy with high molybdenum content, in sulfur and sodium polysulfides (Na/sub 2/S/sub 3/,Na/sub 2/S/sub 4/, Na/sub 2/S/sub 5/) at 623 K. In sulfur, molybdenum corrodes very slowly, with a parabolic rate constant of 3.6 x 10/sup -9/ cm s/sup -1/2/. Hastelloy B shows no measurable corrosion after 100h of exposure to sulfur. The corrosion reaction of molybdenum in Na/sub 2/S/sub 3/ is characterized by the formation of a protective film that effectively eliminates further corrosion after the first 100h of exposure. Hastelloy B, however, corrodes rapidly in Na/sub 2/S/sub 3/, with corrosion rates approaching those of pure nickel under the same conditions. After the first 4h of exposure, the kinetics for the corrosion of Hastelloy B in Na/sub 2/S/sub 3/ follows a linear rate law. The scale morphology has multiple spalled layers of NiS/sub 2/, with some crystallites of NiS/sub 2/ appearing on the leading face of the scale and between the individual scale layers. This spalling causes smaller coupons of the Hastelloy B to corrode faster than larger coupons
Effects of Helium Implantation on the Mechanical Behavior of 100nm-diameter Iron Nano-pillars

International Nuclear Information System (INIS)

Landau, Peri; Guo, Qiang; Hosemann, Peter; Wang, Yongqiang; Greer, Julia R.

2014-01-01

Ferritic and ferritic-martensitic steels are being considered for cladding in the next generation nuclear reactors as well as fusion applications and spallation source materials. For these applications, helium (He) accumulation due to the high appmHe/dpa ratio, represent a matter of concern rooted in the detrimental effects of irradiation on the mechanical performance. The investigations of the effects of ion beam irradiation on mechanical properties of iron represent a useful way to simplify the complexity of irradiation process. This study is focused on the effects of mostly He bubbles on the mechanical behavior and deformation mechanisms
Corrosion behavior of austenitic and ferritic/martensitic steels in oxygen-saturated liquid Pb-Bi eutectic at 450circC and 550circC

OpenAIRE

倉田有司; 二川正敏; 斎藤滋

2005-01-01

Static corrosion tests of various austenitic and ferritic/martensitic steels were conducted in oxygen-saturated liquid Pb-Bi at 450circC and 550circC for 3000h to study the effects of temperature and alloying elements on corrosion behavior. Oxidation, grain boundary corrosion, dissolution and penetration were observed. The corrosion depth decreases at 450circC with increasing Cr content in steels regardless of ferritic/martensitic or austenitic steels. Appreciable dissolution of Ni and Cr doe...
Corrosion behavior of austenitic stainless steel containing Ti

International Nuclear Information System (INIS)

Cha, Sueng Ok; Choe, Han Cheol; Kim, Kwan Hyu

1998-01-01

Corrosion behavior of austenitic stainless steel containing Ti has been studied by using electrochemical techniques. The samples containing Ti from 0.1 to 1.0 wt% were solutionized at 1050 .deg. C for 1hr and then sensitized at 650 .deg. C for 5hr under argon atmosphere. Microstructure and phase analysis of the samples after heat treatment and corrosion tests were carried out by using XRD. TEM, SEM and optical microscope. The amount of δ-ferrite and TiC precipitates in matrix increased as the Ti content increased. In the sensitized samples, Cr 23 C 6 precipitates were observed at γ/δ interface. Degree Of Sensitization(DOS) was lower than 1.0 in all of the solutionized samples and the sensitized samples of Ti content above 0.4% wt% whereas the sensitized samples of Ti content lower than 0.4 wt% showed DOS higher than 1.0. Intergranular attack appeared mainly at grain boundaries in the sensitized sample containing 0.1 wt% Ti and at the γ/δ interface of the higher Ti content. In the latter, however, the attack was not so severe. Pitting potential(E pit ) and repassivation potential(E rep ) of the solutionized and sensitized samples were increased with increasing Ti content. The number and size of the pits decreased with increasing Ti content in the sensitized samples. The pits nucleated at Cr 23 C 6 site and the γ/δ interface
Effect of the Crevice Former on the Corrosion Behavior of 316L Stainless Steel in Chloride-Containing Synthetic Tap Water

Science.gov (United States)

Kim, Seon-Hong; Lee, Ji-Hoon; Kim, Jung-Gu; Kim, Woo-Cheol

2018-05-01

To restrain the failure of the plate heat exchanger (PHE) in customer boiler working fluid, the effect of crevice former type on the corrosion behavior of the 316L stainless steel plate was investigated using electrochemical methods and surface analyses in chloride-containing synthetic tap water (60 °C). The localized corrosion under metal-metal crevice condition was initiated more easily than that under the metal-gasket crevice condition due to the restricted mass transport at the gasket crevice mouth. However, the anodic current under the metal-metal crevice condition was lower than that under metal-gasket crevice condition at a higher anodic potential, indicating that that the metal dissolution under EPDM crevice would be higher than that under metal crevice under the accelerated corrosion condition. Because narrow crevice gap that was formed under gasket accelerated the anodic dissolution at the crevice mouth, the perforation tendency under metal-gasket crevice condition is much higher than that under metal-metal crevice condition. As a result, the crevice geometry, especially the crevice gap, mainly affected the corrosion behavior of PHE material.
Corrosion behavior of Haynes {sup registered} 230 {sup registered} nickel-based super-alloys for integrated coal gasification combined cycle syngas plants. A plant exposure study

Energy Technology Data Exchange (ETDEWEB)

Lee, Sungkyu; Lee, Jieun; Kang, Suk-Hwan; Lee, Seung-Jong; Yun, Yongseung [Institute for Advanced Engineering (IAE), Gyeonggi-do (Korea, Republic of). Plant Engineering Center; Kim, Min Jung [Sungkyunkwan Univ, Gyeonggi-do (Korea, Republic of). Advanced Materials Technology Research Center

2015-07-01

The corrosion behavior of commercially available Haynes {sup registered} 230 {sup registered} nickel-based alloy samples was investigated by exposure to coal-gasifying integrated coal gasification combined cycle pilot plant facilities affiliated with the Institute for Advanced Engineering (2.005 MPa and 160-300 C). The morphological and microstructural analyses of the exposed samples were conducted using scanning electron microscopy and energy-dispersive X-ray spectroscopy analysis on the external surface of the recovered corrosion test samples to obtain information of the corrosion scale. These analyses based on the pre- and post-exposure corrosion test samples combined with thermodynamic Ellingham-Pourbaix stability diagrams provided preliminary insight into the mechanism of the observed corrosion behavior prevailing in the piping materials that connected the particulate removal unit and water scrubber of the integrated coal gasification combined cycle pilot plant. Uniform material wastage was observed after 46 hours of operation, and a preliminary corrosion mechanism was suggested: the observed material waste and corrosion behavior of the Haynes {sup registered} 230 {sup registered} nickel-based alloy samples cut off from the coal syngas integrated coal gasification combined cycle plant were explained by the formation of discontinuous (complex) oxide phases and subsequent chlorine-induced active oxidation under the predominantly reducing environment encountered. This contribution continues the already published studies of the Fe-Ni-Cr-Co alloy Haynes {sup registered} 556 {sup registered}.
Corrosion of Carbon Steel and Corrosion-Resistant Rebars in Concrete Structures Under Chloride Ion Attack

Science.gov (United States)

Mohamed, Nedal; Boulfiza, Mohamed; Evitts, Richard

2013-03-01

Corrosion of reinforced concrete is the most challenging durability problem that threatens reinforced concrete structures, especially structures that are subject to severe environmental conditions (i.e., highway bridges, marine structures, etc.). Corrosion of reinforcing steel leads to cracking and spalling of the concrete cover and billions of dollars are spent every year on repairing such damaged structures. New types of reinforcements have been developed to avoid these high-cost repairs. Thus, it is important to study the corrosion behavior of these new types of reinforcements and compare them to the traditional carbon steel reinforcements. This study aimed at characterizing the corrosion behavior of three competing reinforcing steels; conventional carbon steel, micro-composite steel (MMFX-2) and 316LN stainless steel, through experiments in carbonated and non-carbonated concrete exposed to chloride-laden environments. Synthetic pore water solutions have been used to simulate both cases of sound and carbonated concrete under chloride ions attack. A three-electrode corrosion cell is used for determining the corrosion characteristics and rates. Multiple electrochemical techniques were applied using a Gamry PC4™ potentiostat manufactured by Gamry Instruments (Warminster, PA). DC corrosion measurements were applied on samples subjected to fixed chloride concentration in the solution.
Corrosion/96 conference papers

International Nuclear Information System (INIS)

Anon.

1996-01-01

Topics covered by this conference include: cathodic protection in natural waters; cleaning and repassivation of building HVAC systems; worldwide opportunities in flue gas desulfurization; advancements in materials technology for use in oil and gas service; fossil fuel combustion and conversion; technology of corrosion inhibitors; computers in corrosion control--modeling and information processing; recent experiences and advances of austenitic alloys; managing corrosion with plastics; corrosion measurement technology; corrosion inhibitors for concrete; refining industry; advances in corrosion control for rail and tank trailer equipment; CO 2 corrosion--mechanisms and control; microbiologically influenced corrosion; corrosion in nuclear systems; role of corrosion in boiler failures; effects of water reuse on monitoring and control technology in cooling water applications; methods and mechanisms of scale and deposit control; corrosion detection in petroleum production lines; underground corrosion control; environmental cracking--relating laboratory results and field behavior; corrosion control in reinforced concrete structures; corrosion and its control in aerospace and military hardware; injection and process addition facilities; progress reports on the results of reinspection of deaerators inspected or repaired per RP0590 criteria; near 100% volume solids coating technology and application methods; materials performance in high temperature environments containing halides; impact of toxicity studies on use of corrosion/scale inhibitors; mineral scale deposit control in oilfield related operations; corrosion in gas treating; marine corrosion; cold climate corrosion; corrosion in the pulp and paper industry; gaseous chlorine alternatives in cooling water systems; practical applications of ozone in recirculating cooling water systems; and water reuse in industry. Over 400 papers from this conference have been processed separately for inclusion on the data base
Effects of cold work, sensitization treatment, and the combination on corrosion behavior of stainless steels in nitric acid

International Nuclear Information System (INIS)

Mayuzumi, M.; Ohta, J.; Arai, T.

1998-01-01

In a reprocessing process, spent nuclear fuels from light-water reactors are dissolved in nitric acid (HNO 3 ) to separate and recover the fissile materials such as uranium and plutonium from the radioactive fission products. Corrosion behavior of two stainless steels (SS) was investigated in nitric acid (HNO 3 ) for the effect of cold work (CW), sensitization heat treatment (Sens.), and a combination (CW + Sens.). The corrosion rate of the solution-treated type 304 SS (UNS S30400) with extra-low carbon (type 304ELC SS (UNS S30403)) increased with time and reached constant values after 1,000 h of immersion. However, constant corrosion rates were obtained for 25% Cr-20% Ni-Nb (type 310Nb SS [UNS S31040]) from the initial stage of immersion. CW mitigated corrosion of the solution-treated SS. The effect of CW was different on the two types of SS, with the sensitization heat-treated type 304 ELC SS showing higher corrosion rates and type 310Nb SS lower corrosion rates by CW. Corrosion resistance of type 310Nb SS was superior to type 304 ELC SS after all treatments. Chromium concentration of the sensitization-treated type 304 ELC SS was lower in the grain-boundary region than of the solution-treated one, although no chromium carbide precipitation was observed. This may have been the cause of intergranular corrosion enhancement by sensitization treatment
Hot corrosion behavior of plasma-sprayed partially stabilized zirconia coatings in a lithium molten salt

International Nuclear Information System (INIS)

Cho, Soo Haeng; Hong, Sun Seok; Kang, Dae Seong; Park, Byung Heong; Hur, Jin Mok; Lee, Han Soo

2008-01-01

The electrolytic reduction of spent oxide fuel involves the liberation of oxygen in a molten LiCl electrolyte, which results in a chemically aggressive environment that is too corrosive for typical structural materials. It is essential to choose the optimum material for the process equipment handling molten salt. IN713LC is one of the candidate materials proposed for application in electrolytic reduction process. In this study, Yttria-Stabilized Zirconia (YSZ) top coat was applied to a surface of IN713LC with an aluminized metallic bond coat by an optimized plasma spray process, and were investigated the corrosion behavior at 675 .deg. C for 216 hours in the molten salt LiCl-Li 2 O under an oxidizing atmosphere. The as-coated and tested specimens were examined by OM, SEM/EDS and XRD, respectively. The bare superalloy reveals obvious weight loss, and the corrosion layer formed on the surface of the bare superalloy was spalled due to the rapid scale growth and thermal stress. The top coatings showed a much better hot-corrosion resistance in the presence of LiCl-Li 2 O molten salt when compared to those of the uncoated superalloy and the aluminized bond coatings. These coatings have been found to be beneficial for increasing to the hot-corrosion resistance of the structural materials for handling high temperature lithium molten salts

Effect of surface machining on corrosion behavior of SA182-304 in simulated

International Nuclear Information System (INIS)

Zhang Zhiming; Wang Jianqiu; Han Enhou; Ke Wei

2015-01-01

Different machining processes of mechanical parts can cause surface damage layers with different levels. The surface deformed layer can affect the corrosion behavior and service life of these mechanical parts a lot during the following service process. As a result, it is a key issue for the fabrication of the mechanical parts with long life that the selection of proper machining parameters and the removal of surface damage. The purpose of this study is to study the influence of different turning parameters on the corrosion behavior of nuclear grade SA182-304 stainless steel widely used in the advanced pressured water reactors (PWRs). 6 kinds of samples with different surface state are prepared by a lathe with different machining parameters, such as the feed, cutting speed and back engagement of the cutting edge. The high temperature and high pressure immersion test of these samples in the simulated PWR primary watershows that machining processes can affect the microstructure and chemical composition of the formed surface oxide scales a lot. According to the experimental results, the proper machining parameters for the studied SA182-304 are suggested. (authors)
Influence of alkali, silicate, and sulfate content of carbonated concrete pore solution on mild steel corrosion behavior

International Nuclear Information System (INIS)

L'Hostis, V.; Huet, B.; Tricheux, L.; Idrissi, H.

2010-01-01

The increase in the rebar corrosion rate due to the concrete carbonation is the major cause of reinforced concrete degradation. The aim of this study was to investigate the corrosion behavior of mild steel rebars in simulated carbonated concrete solution. For this purpose, thermodynamic calculations, electrochemical techniques, gravimetric measurements, and surface analyses were used. Thermodynamic investigations of the nature of the interstitial solution provides an estimation of the influence of sulfate (SO 4 2- ) and alkali (Na + , K + ) content on carbonate alkalinity of the CO 2 /H 2 O open system (pCO 2 =0. 3 mbar). in this system, calcium-silicate hydrates (C-S-H) remain thermodynamically unstable and amorphous silica controls silicate aqueous content at 100 ppm. Electrochemical results highlight a decrease in the corrosion rate with increasing carbonate alkalinity and the introduction of silicate. The introduction of sulfate at fixed carbonate alkalinity shows a dual effect: at high carbonate alkalinity, the corrosion rate is increased whereas at low carbonate alkalinity, corrosion rate is decreased. Those results are supported by surface analysis. Authors conclude that silicate and sulfate release from cement hydrates and fixation of alkali on carbonated hydrates are key parameters to estimate mild steel corrosion in carbonated concrete. (authors)
Corrosion Behavior of the Stressed Sensitized Austenitic Stainless Steels of High Nitrogen Content in Seawater

Directory of Open Access Journals (Sweden)

A. Almubarak

2013-01-01

Full Text Available The purpose of this paper is to study the effect of high nitrogen content on corrosion behavior of austenitic stainless steels in seawater under severe conditions such as tensile stresses and existence of sensitization in the structure. A constant tensile stress has been applied to sensitized specimens types 304, 316L, 304LN, 304NH, and 316NH stainless steels. Microstructure investigation revealed various degrees of stress corrosion cracking. SCC was severe in type 304, moderate in types 316L and 304LN, and very slight in types 304NH and 316NH. The electrochemical polarization curves showed an obvious second current peak for the sensitized alloys which indicated the existence of second phase in the structure and the presence of intergranular stress corrosion cracking. EPR test provided a rapid and efficient nondestructive testing method for showing passivity, degree of sensitization and determining IGSCC for stainless steels in seawater. A significant conclusion was obtained that austenitic stainless steels of high nitrogen content corrode at a much slower rate increase pitting resistance and offer an excellent resistance to stress corrosion cracking in seawater.
The Effect of Deep Cryogenic Treatment on the Corrosion Behavior of Mg-7Y-1.5Nd Magnesium Alloy

Directory of Open Access Journals (Sweden)

Quantong Jiang

2017-10-01

Full Text Available The effect of quenching on the corrosion resistance of Mg-7Y-1.5Nd alloy was investigated. The as-cast alloy was homogenized at 535 °C for 24 h, followed by quenching in air, water, and liquid nitrogen. Then, all of the samples were peak-aged at 225 °C for 14 h. The microstructures were studied by scanning electron microscopy, energy-dispersive spectrometry, and X-ray diffraction. Corrosion behavior was analyzed by using weight loss rate and gas collection. Electrochemical characterizations revealed that the T4-deep cryogenic sample displayed the strongest corrosion resistance among all of the samples. A new square phase was discovered in the microstructure of the T6-deep cryogenic sample; this phase was hugely responsible for the corrosion property. Cryogenic treatment significantly improved the corrosion resistance of Mg-7Y-1.5Nd alloy.
Investigation of the behaviour of 35% nickel alloys in the presence of helium coolant impurities

International Nuclear Information System (INIS)

Dixmier, J.; Leclercq, D.; Olivier, P.; Vincent, L.; Willermoz, H.

1976-01-01

Alloys of the Incoloy 800 type containing 35% nickel are being considered for the heat exchangers of steam-cycle high-temperature reactors for electricity production. Corrosion tests at 650 and 800 0 C have been carried out at atmospheric pressure and at 50 bar on four such alloys (commercially available and specially produced ones) with different titanium and aluminium contents. It appears that the degree of intergranular attack occurring in these materials increases with the titanium and aluminium concentration. Examination with a scanning electron microscope fitted with analysers confirms the decisive role of these two elements which are actually to be found in oxidized form at the grain boundaries to the exclusion of other components of the alloy. This type of corrosion can lead in the long run to a deterioration in the alloy's mechanical characteristics at high temperature. To assess the true risk of in-service rupture, various rigs have been developed for investigating corrosion under stress conditions. The atmosphere in these rigs consists of helium, of which the impurity content is rigorously controlled. In particular, the Aida high-pressure loop installed at the Grenoble Nuclear Research Centre can accommodate a large number of test-pieces. These are either subjected to a definite tensile stress or placed in a circuit through which helium is passed at high velocity. At present experiments are being conducted at 700 and 750 0 C on an Incoloy 800 alloy corresponding to the designers' specifications. The experiments are performed at atmospheric pressure and a pressure of 50 bar with the same impurity pressures. (author)
Corrosion behaviors of Mg and its alloys with different Al contents in a modified simulated body fluid

International Nuclear Information System (INIS)

Wen Zhaohui; Wu Changjun; Dai Changsong; Yang Feixia

2009-01-01

The corrosion behaviors of pure magnesium (Mg) and three Mg alloys with different Al contents were investigated in a modified simulated body fluid (m-SBF) through immersion tests, Tafel experiments, and electrochemical impedance spectroscopic (EIS) experiments. The immersion results show that the corrosion rates (CRs) of the four samples were in an order of AZ91D ct ) of the three magnesium alloys initially increased and then decreased while the R ct of pure Mg was kept lower within 24 h. The results of a scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) show that pure Mg and three alloys were heterogeneously corroded in the m-SBF. The corrosion of pure Mg, which showed a more uniform corrosion appearance, resulted from localized corrosion over the entire surface. Alloy AZ91D (of 8.5-9.5 wt.% Al) showed relatively uniform corrosion morphology and the β-Mg 12 Al 17 precipitates in alloy AZ91D were more homogeneously and continuously distributed along the grain boundaries. Obvious corrosion pits were found on the surface of alloy AZ61 and AZ31. The corrosion pits of alloy AZ61 were shallower than those of alloy AZ31. Alloy AZ61 (of 5.8-7.2 wt.% Al) possessed more Al 8 Mn 5 and a little β-Mg 12 Al 17 presented along the grain boundary heterogeneously and discontinuously. Al 8 Mn 5 was the main phase of the AZ31 alloy (of 2.5-3.5 wt.% Al) dispersed into the matrix. In conclusion, the microstructure and the Al content in the α-Mg (Al) matrix significantly affected the corrosion properties of the alloys in the m-SBF. With the increase in Al content, the corrosion resistances of the samples were improved.
Corrosion Behavior of Ni3(Si,Ti + 2Mo in Hydrochloric Acid Solution

Directory of Open Access Journals (Sweden)

Gadang Priyotomo

2013-10-01

Full Text Available The corrosion behavior of Ni3(Si,Ti + 2Mo intermetallic compound (L12 and (L12 + Niss mixture region has been investigated using an immersion test, polarization method and surface analytical method (scanning electron microscope and energy-dispersive X-Ray spectrometry in 0.5 kmol/m3 hydrochloric acid (HCl solution at 303 K. In addition, the results obtained were compared to those of the L12 single-phase Ni3(Si,Ti intermetallic compound and C 276 alloy. It was found that Ni3(Si,Ti + 2Mo had the preferential dissolution of L12 with a lower Mo concentration compared to (L12 + Niss mixture region. From the immersion test and polarization curves, Ni3(Si,Ti + 2Mo and C276 showed the lowest corrosion resistance and the highest corrosion resistance in the solution, respectively. From this work, It implied that unlike C276, Ni3(Si,Ti +2Mo intermetallic compound was difficult to form a stable passive film in HCl solution as well as Ni3(Si,Ti in the same solution.
The combined effects of prior-corrosion and aggressive chemical environments on fatigue crack growth behavior in aluminum alloy 7075-T651

Science.gov (United States)

Mills, Thomas Brian

1997-11-01

Exfoliation corrosion is a potentially severe form of corrosion that frequently affects high-strength aluminum, particularly 2xxx- and 7xxx-series alloys. Exfoliation degrades components such as sheets, plates, and extrusions that have highly elongated grain structures. Few attempts have been made to investigate the effects of this form of corrosion on the fatigue performance of these materials, so a preliminary study was conducted to determine the effects of exfoliation corrosion on the fatigue response of quarter-inch 7075-T651 aluminum alloy plate. This was accomplished by subjecting aluminum panels to an ASTM standard corrosive solution known as EXCO then fatiguing the panels in corrosion fatigue environments of dry air, humid air, and artificial acid rain. Statistical analyses of the fatigue crack growth data suggest that prior-corrosion and corrosion fatigue are competing mechanisms that both have the potential of accelerating crack growth rates. In the dry air cases, exfoliation accelerated crack growth rates a maximum of 4.75 times over the uncorroded material at lower stress intensities such as 5 ksi surdinch. This accelerated behavior dropped off rapidly, however, and was nonexistent at higher stress intensities. Humid air increased crack velocities considerably as compared to the dry air uncorroded case, but the addition of exfoliation corrosion to the humid cases did not have a significant effect on crack growth behavior. On the other hand, specimens containing exfoliation corrosion and then exposed to artificial acid rain had significantly higher crack growth rates than their uncorroded counterparts. Finally, fractographic examinations of the specimens revealed evidence of lower energy, quasi-cleavage fracture persisting near to the exfoliated edge of specimens tested in the dry air, humid air, and artificial acid rain environments. The implications of this research are that prior-corrosion damage has the ability to significantly increase crack growth
Influence and role of ethanol minor constituents of fuel grade ethanol on corrosion behavior of carbon steel

International Nuclear Information System (INIS)

Samusawa, Itaru; Shiotani, Kazuhiko

2015-01-01

Highlights: • The pitting factors of the minor contents of ethanol are acetic acid, Cl and H 2 O. • Formic acid in ethanol promotes general corrosion. • The H 2 O content in fuel-grade-ethanol (FGE) affects the corrosion morphology. • Acetic acid generates iron acetate, which has high solubility in FGE environments. • A pitting mechanism based on the rupture of passive film is proposed. - Abstract: The influences of organic acids, chloride and water on the corrosion behavior of carbon steel in fuel grade ethanol (FGE) environments were investigated by immersion testing in simulated FGE. The roles of acetic acid, chloride and water in pitting corrosion were studied by using X-ray photoelectron spectroscopy (XPS), auger electron spectroscopy (AES) and electrochemical experiments. The results indicated that iron acetate is generated on oxide film. Iron(II) acetate shows high solubility in FGE environments. The sites where iron(II) acetate is existed become preferential anodic sites, and chloride promotes anodic dissolution at such sites
Corrosion Behavior and Strength of Dissimilar Bonding Material between Ti and Mg Alloys Fabricated by Spark Plasma Sintering

Science.gov (United States)

Pripanapong, Patchara; Kariya, Shota; Luangvaranunt, Tachai; Umeda, Junko; Tsutsumi, Seiichiro; Takahashi, Makoto; Kondoh, Katsuyoshi

2016-01-01

Ti and solution treated Mg alloys such as AZ31B (ST), AZ61 (ST), AZ80 (ST) and AZ91 (ST) were successfully bonded at 475 °C by spark plasma sintering, which is a promising new method in welding field. The formation of Ti3Al intermetallic compound was found to be an important factor in controlling the bonding strength and galvanic corrosion resistance of dissimilar materials. The maximum bonding strength and bonding efficiency at 193 MPa and 96% were obtained from Ti/AZ91 (ST), in which a thick and uniform nano-level Ti3Al layer was observed. This sample also shows the highest galvanic corrosion resistance with a measured galvanic width and depth of 281 and 19 µm, respectively. The corrosion resistance of the matrix on Mg alloy side was controlled by its Al content. AZ91 (ST) exhibited the highest corrosion resistance considered from its corrode surface after corrosion test in Kroll’s etchant. The effect of Al content in Mg alloy on bonding strength and corrosion behavior of Ti/Mg alloy (ST) dissimilar materials is discussed in this work. PMID:28773788
Corrosion Behavior and Strength of Dissimilar Bonding Material between Ti and Mg Alloys Fabricated by Spark Plasma Sintering

Directory of Open Access Journals (Sweden)

Patchara Pripanapong

2016-08-01

Full Text Available Ti and solution treated Mg alloys such as AZ31B (ST, AZ61 (ST, AZ80 (ST and AZ91 (ST were successfully bonded at 475 °C by spark plasma sintering, which is a promising new method in welding field. The formation of Ti3Al intermetallic compound was found to be an important factor in controlling the bonding strength and galvanic corrosion resistance of dissimilar materials. The maximum bonding strength and bonding efficiency at 193 MPa and 96% were obtained from Ti/AZ91 (ST, in which a thick and uniform nano-level Ti3Al layer was observed. This sample also shows the highest galvanic corrosion resistance with a measured galvanic width and depth of 281 and 19 µm, respectively. The corrosion resistance of the matrix on Mg alloy side was controlled by its Al content. AZ91 (ST exhibited the highest corrosion resistance considered from its corrode surface after corrosion test in Kroll’s etchant. The effect of Al content in Mg alloy on bonding strength and corrosion behavior of Ti/Mg alloy (ST dissimilar materials is discussed in this work.
Cryogenic filter method produces super-pure helium and helium isotopes

Science.gov (United States)

Hildebrandt, A. F.

1964-01-01

Helium is purified when cooled in a low pressure environment until it becomes superfluid. The liquid helium is then filtered through iron oxide particles. Heating, cooling and filtering processes continue until the purified liquid helium is heated to a gas.
Evolution processes of the corrosion behavior and structural characteristics of plasma electrolytic oxidation coatings on AZ31 magnesium alloy

Science.gov (United States)

Chen, Dong; Wang, Ruiqiang; Huang, Zhiquan; Wu, Yekang; Zhang, Yi; Wu, Guorui; Li, Dalong; Guo, Changhong; Jiang, Guirong; Yu, Shengxue; Shen, Dejiu; Nash, Philip

2018-03-01

Evolution processes of the corrosion behavior and structural characteristics of the plasma electrolytic oxidation (PEO) coated AZ31 magnesium alloy were investigated by using scanning electron microscope (SEM) equipped with energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), potentio-dynamic polarization curves and electrochemical impedance spectroscopy (EIS) measurements. Detached coating samples were fabricated by an electrochemical method and more details of the internal micro-structure of coatings were clearly observed on the fractured cross-section morphologies of the samples compared to general polished cross-section morphologies. Evolution mechanisms of the coating corrosion behavior in relation to the evolution of micro-structural characteristics were discussed in detail.
An optimum cold end configuration for helium liquefaction cycles

International Nuclear Information System (INIS)

Minta, M.; Smith, J.L.

1984-01-01

This chapter examines the effect of the non-ideal behavior of helium at low temperature on the performance of helium liquefaction cycles. The effect is isolated by means of a continuum model for the precooling stage. The cold end losses are due primarily to the composite effect of the non-ideality of helium at low temperatures and the heat exchanger losses, in addition to the component losses fixed by the expander/compressor efficiencies. Topics considered include continuously distributed full-pressure ratio expanders, continuously distributed full-flow expanders, the heat exchange effect (ideal gas working fluid, real gas working fluid), and cold end configuration. The cold end configuration minimizes the cycle cold end losses
Corrosion and Wear Behaviors of Cr-Doped Diamond-Like Carbon Coatings

Science.gov (United States)

Viswanathan, S.; Mohan, L.; Bera, Parthasarathi; Kumar, V. Praveen; Barshilia, Harish C.; Anandan, C.

2017-08-01

A combination of plasma-enhanced chemical vapor deposition and magnetron sputtering techniques has been employed to deposit chromium-doped diamond-like carbon (DLC) coatings on stainless steel, silicon and glass substrates. The concentrations of Cr in the coatings are varied by changing the parameters of the bipolar pulsed power supply and the argon/acetylene gas composition. The coatings have been studied for composition, morphology, surface nature, nanohardness, corrosion resistance and wear resistance properties. The changes in I D / I G ratio with Cr concentrations have been obtained from Raman spectroscopy studies. Ratio decreases with an increase in Cr concentration, and it has been found to increase at higher Cr concentration, indicating the disorder in the coating. Carbide is formed in Cr-doped DLC coatings as observed from XPS studies. There is a decrease in sp 3/ sp 2 ratios with an increase in Cr concentration, and it increases again at higher Cr concentration. Nanohardness studies show no clear dependence of hardness on Cr concentration. DLC coatings with lower Cr contents have demonstrated better corrosion resistance with better passive behavior in 3.5% NaCl solution, and corrosion potential is observed to move toward nobler (more positive) values. A low coefficient of friction (0.15) at different loads is observed from reciprocating wear studies. Lower wear volume is found at all loads on the Cr-doped DLC coatings. Wear mechanism changes from abrasive wear on the substrate to adhesive wear on the coating.
Mechanical properties and corrosion behavior of Mg-Gd-Ca-Zr alloys for medical applications.

Science.gov (United States)

Shi, Ling-Ling; Huang, Yuanding; Yang, Lei; Feyerabend, Frank; Mendis, Chamini; Willumeit, Regine; Ulrich Kainer, Karl; Hort, Norbert

2015-07-01

Magnesium alloys are promising candidates for biomedical applications. In this work, influences of composition and heat treatment on the microstructure, the mechanical properties and the corrosion behavior of Mg-Gd-Ca-Zr alloys as potential biomedical implant candidates were investigated. Mg5Gd phase was observed at the grain boundaries of Mg-10Gd-xCa-0.5Zr (x=0, 0.3, 1.2wt%) alloys. Increase in the Ca content led to the formation of additional Mg2Ca phase. The Ca additions increased both the compressive and the tensile yield strengths, but reduced the ductility and the corrosion resistance in cell culture medium. After solution heat treatment, the Mg5Gd particles dissolved in the Mg matrix. The compressive strength decreased, while the corrosion resistance improved in the solution treated alloys. After ageing at 200°C, metastable β' phase formed on prismatic planes and a new type of basal precipitates have been observed, which improved the compressive and tensile ultimate strength, but decreased the ductility. Copyright © 2015 Elsevier Ltd. All rights reserved.
Cyclic Oxidation and Hot Corrosion Behavior of Nickel-Iron-Based Superalloy

Science.gov (United States)

Chellaganesh, D.; Adam Khan, M.; Winowlin Jappes, J. T.; Sathiyanarayanan, S.

2018-01-01

The high temperature oxidation and hot corrosion behavior of nickel-iron-based superalloy are studied at 900 ° and 1000 °C. The significant role of alloying elements with respect to the exposed medium is studied in detail. The mass change per unit area was catastrophic for the samples exposed at 1000 °C and gradual increase in mass change was observed at 900 °C for both the environments. The exposed samples were further investigated with SEM, EDS and XRD analysis to study the metallurgical characteristics. The surface morphology has expressed the in situ nature of the alloy and its affinity toward the environment. The EDS and XRD analysis has evidently proved the presence of protective oxides formation on prolonged exposure at elevated temperature. The predominant oxide formed during the exposure at high temperature has a major contribution toward the protection of the samples. The nickel-iron-based superalloy is less prone to oxidation and hot corrosion when compared to the existing alloy in gas turbine engine simulating marine environment.
Microstructure and corrosion behavior of laser surface-treated AZ31B Mg bio-implant material.

Science.gov (United States)

Wu, Tso-Chang; Ho, Yee-Hsien; Joshi, Sameehan S; Rajamure, Ravi S; Dahotre, Narendra B

2017-05-01

Although magnesium and magnesium alloys are considered biocompatible and biodegradable, they suffer from poor corrosion performance in the human body environment. In light of this, surface modification via rapid surface melting of AZ31B Mg alloy using a continuous-wave Nd:YAG laser was conducted. Laser processing was performed with laser energy ranging from 1.06 to 3.18 J/mm 2 . The corrosion behavior in simulated body fluid of laser surface-treated and untreated AZ31B Mg alloy samples was evaluated using electrochemical technique. The effect of laser surface treatment on phase and microstructure evolution was evaluated using X-ray diffraction and scanning electron microscopy. Microstructure examination revealed grain refinement as well as formation and uniform distribution of Mg 17 Al 12 phase along the grain boundary for laser surface-treated samples. Evolution of such unique microstructure during laser surface treatment indicated enhancement in the corrosion resistance of laser surface-treated samples compared to untreated alloy.
Corrosion behavior and protective ability of Zn and Zn-Co electrodeposits with embedded polymeric nanoparticles

International Nuclear Information System (INIS)

Boshkov, N.; Tsvetkova, N.; Petrov, P.; Koleva, D.; Petrov, K.; Avdeev, G.; Tsvetanov, Ch.; Raichevsky, G.; Raicheff, R.

2008-01-01

The anodic behavior, corrosion resistance and protective ability of Zn and alloyed Zn-Co (∼3 wt.%) nanocomposite coatings were investigated in a model corrosion medium of 5% NaCl solution. The metallic matrix of the layers incorporates core-shell nano-sized stabilized polymeric micelles (SPMs) obtained from poly(ethylene oxide)-b-poly(propylene oxide)-b-poly(ethylene oxide) block co-polymers. The protective properties of the composite coatings were evaluated using potentiodynamic polarization technique, polarization resistance measurements and powder X-ray diffraction. The sizes and distribution of the stabilized polymeric micelles in the starting electrolytes used as well as in the metal matrices of the layers were investigated using scanning and transmission electron microscopy. The results obtained are compared to those of electrodeposited Zn and Zn-Co (∼3 wt.%) alloy coatings at identical conditions and demonstrate the enhanced protective characteristics of the Zn nanocomposites during the investigating period. The influence of the SPMs on the corrosion resistance of the nanocomposite layers is commented and discussed
Corrosion and Discharge Behaviors of Mg-Al-Zn and Mg-Al-Zn-In Alloys as Anode Materials

Directory of Open Access Journals (Sweden)

Jiarun Li

2016-03-01

Full Text Available The Mg-6%Al-3%Zn and Mg-6%Al-3%Zn-(1%, 1.5%, 2%In alloys were prepared by melting and casting. Their microstructures were investigated via metallographic and energy-dispersive X-ray spectroscopy (EDS analysis. Moreover, hydrogen evolution and electrochemical tests were carried out in 3.5 wt% NaCl solution aiming at identifying their corrosion mechanisms and discharge behaviors. The results suggested that indium exerts an improvement on both the corrosion rate and the discharge activity of Mg-Al-Zn alloy via the effects of grain refining, β-Mg17Al12 precipitation, dissolving-reprecipitation, and self-peeling. The Mg-6%Al-3%Zn-1.5%In alloy with the highest corrosion rate at free corrosion potential did not perform desirable discharge activity indicating that the barrier effect caused by the β-Mg17Al12 phase would have been enhanced under the conditions of anodic polarization. The Mg-6%Al-3%Zn-1.0%In alloy with a relative low corrosion rate and a high discharge activity is a promising anode material for both cathodic protection and chemical power source applications.

Study on corrosion behavior of candidate materials in 650℃ supercritical water

International Nuclear Information System (INIS)

Ma Shuli; Luo Ying; Zhang Qiang; Wang Hao; Qiu Shaoyu

2014-01-01

The general corrosion behavior of three candidate materials (347, HR3C and In-718) was investigated in 650 ℃/25 MPa deionized water. Morphology and composition of the surface oxide film with different exposure time were observed through FEG-SEM and EDS. The phase constitute was analyzed by GIXRD. For all the test materials, the weight loss follows typical parabolic law and the weight loss of 347 shows more than 40 times higher than that of HR3C and In-718. The oxide film of three alloys mainly consists of Ni(Cr, Fe) 2 O 4 . In-718 shows severe pitting and the oxide film of 347 appears significant spalling, while HR3C has compact oxide film. In the high temperature supercritical water, the high Cr content may enhance the general corrosion property of the alloys, while addition of Nb may be detrimental to the pitting resistance of alloys. (authors)
An evaluation of corrosion resistant alloys by field corrosion test in Japanese refuse incineration plants

International Nuclear Information System (INIS)

Kawahara, Yuuzou; Nakamura, Masanori; Shibuya, Eiichi; Yukawa, Kenichi

1995-01-01

As the first step for development of the corrosion resistant superheater tube materials of 500 C, 100 ata used in high efficient waste-to-energy plants, field corrosion tests of six conventional alloys were carried out at metal temperatures of 450 C and 550 C for 700 and 3,000 hours in four typical Japanese waste incineration plants. The test results indicate that austenitic alloys containing approximately 80 wt% [Cr+Ni] show excellent corrosion resistance. When the corrosive environment is severe, intergranular corrosion of 40∼200 microm depth occurs in stainless steel and high alloyed materials. It is confirmed quantitatively that corrosion behavior is influenced by environmental corrosion factors such as Cl concentration and thickness of deposits on tube surface, metal temperature, and flue gas temperature. The excellent corrosion resistance of high [Cr+Ni+Mo] alloys such as Alloy 625 is explained by the stability of its protective oxide, such that the time dependence of corrosion nearly obeys the parabolic rate law
Perspective on present and future alloy development efforts on austenitic stainless steels for fusion application

International Nuclear Information System (INIS)

Maziasz, P.J.

1984-01-01

The purpose of this paper is to address important questions concerning how to effect further alloy development of austenitic stainless steels for resistance, and to what extent the behavior of other properties under irradiation, such as strength/embrittlement, fatigue/irradiation creep, corrosion (under irradiation), and radiation-induced activation must be influenced. To summarize current understanding, helium has been found to have major effects on swelling and embrittlement, but several metallurgical avenues are available for significant improvement relative to type 316 stainless steel. Studies on fatigue and irradiation creep, particularly including helium effects, are preliminary but have yet to reveal engineering problems requiring additional alloy development remedies. The effects of irradiation on corrosion behavior are unknown, but higher alloy nickel contents make thermal corrosion in lithium worse. 67 refs
Corrosion-electrochemical behavior of zirconium in molten alkali metal carbonates

Science.gov (United States)

Nikitina, E. V.

2016-08-01

The corrosion and electrochemical characteristics of zirconium during its interaction with molten lithium, sodium, and potassium carbonates containing from 1 to 5 wt % additives to the salt phase are studied in a temperature range of 500-800°C using gravimetry, corrosion potential measurement, and anodic polarization. The substances decreasing the corrosion losses due to the strengthening and thickening of an oxide film (lithium, sodium, potassium hydroxides) are used as passivators. Sodium chloride, fluoride, and sulfate serve as corrosion stimulators (activators).
Helium cryogenics

CERN Document Server

Van Sciver, Steven W

2012-01-01

Twenty five years have elapsed since the original publication of Helium Cryogenics. During this time, a considerable amount of research and development involving helium fluids has been carried out culminating in several large-scale projects. Furthermore, the field has matured through these efforts so that there is now a broad engineering base to assist the development of future projects. Helium Cryogenics, 2nd edition brings these advances in helium cryogenics together in an updated form. As in the original edition, the author's approach is to survey the field of cryogenics with emphasis on helium fluids. This approach is more specialized and fundamental than that contained in other cryogenics books, which treat the associated range of cryogenic fluids. As a result, the level of treatment is more advanced and assumes a certain knowledge of fundamental engineering and physics principles, including some quantum mechanics. The goal throughout the work is to bridge the gap between the physics and engineering aspe...
Flow visualization in superfluid helium-4 using He2 molecular tracers

Science.gov (United States)

Guo, Wei

Flow visualization in superfluid helium is challenging, yet crucial for attaining a detailed understanding of quantum turbulence. Two problems have impeded progress: finding and introducing suitable tracers that are small yet visible; and unambiguous interpretation of the tracer motion. We show that metastable He2 triplet molecules are outstanding tracers compared with other particles used in helium. These molecular tracers have small size and relatively simple behavior in superfluid helium: they follow the normal fluid motion at above 1 K and will bind to quantized vortex lines below about 0.6 K. A laser-induced fluorescence technique has been developed for imaging the He2 tracers. We will present our recent experimental work on studying the normal-fluid motion by tracking thin lines of He2 tracers created via femtosecond laser-field ionization in helium. We will also discuss a newly launched experiment on visualizing vortex lines in a magnetically levitated superfluid helium drop by imaging the He2 tracers trapped on the vortex cores. This experiment will enable unprecedented insight into the behavior of a rotating superfluid drop and will untangle several key issues in quantum turbulence research. We acknowledge the support from the National Science Foundation under Grant No. DMR-1507386 and the US Department of Energy under Grant No. DE-FG02 96ER40952.
Wear and corrosion behaviors of Ti6Al4V alloy biomedical materials by silver plasma immersion ion implantation process

Energy Technology Data Exchange (ETDEWEB)

Hongxi, Liu [School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093 (China); Qian, Xu, E-mail: vipliuhx@yahoo.com.cn [Faculty of Adult Education, Kunming University of Science and Technology, Kunming 650051 (China); Xiaowei, Zhang; Chuanqi, Wang [School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093 (China); Baoyin, Tang [State Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, Harbin 150001 (China)

2012-10-30

In order to improve the wear resistance and anti-corrosion behaviors of Ti6Al4V (TC4) alloy, polished samples were implanted with silver (Ag) ions by plasma immersion ion implantation (PIII) technique. The phase composition and element concentration-depth distribution in modified layer were characterized by X-ray diffraction (XRD) and Auger electron spectrum (AES). Corrosion resistance, microhardness, friction and wear behaviors of PIII-TC4 alloy changed with the Ag ion implantation dose. XRD analysis reveals that the surface modified layer consists of Ag and a small amount of TiAg phases. AES results show that Ag atomic peak concentration is 9.88%, about 14.4 nm from the surface. The maximum nanohardness and elastic modulus of PIII-TC4 alloy increases by 62.5% and 54.5%, respectively. The lowest friction coefficient reduces from 0.78 to 0.2. The test result of potentiodynamic polarization in 3.5% NaCl saturated solution indicates that the sample of Ag ion dose at 1.0 Multiplication-Sign 10{sup 17} ions/cm{sup 2} has the best corrosion resistance with the lowest corrosion current density and the least porosity.
The study of tribological and corrosion behavior of plasma nitrided 34CrNiMo6 steel under hot and cold wall conditions

International Nuclear Information System (INIS)

Maniee, A.; Mahboubi, F.; Soleimani, R.

2014-01-01

Highlights: • 34CrNiMo6 steel was plasma nitrided under hot and cold wall conditions. • The amount of ε phase in hot wall condition was more than that of cold wall condition. • Wear resistance of hot wall nitrided samples was more than cold wall treated ones. • Hot wall nitriding provides better corrosion behavior than cold wall nitriding. - Abstract: This paper reports on a comparative study of tribological and corrosion behavior of plasma nitrided 34CrNiMo6 low alloy steel under modern hot wall condition and conventional cold wall condition. Plasma nitriding was carried out at 500 °C and 550 °C with a 25% N 2 + 75% H 2 gas mixture for 8 h. The wall temperature of the chamber in hot wall condition was set to 400 °C. The treated specimens were characterized by using scanning electron microscopy (SEM), X-ray diffraction (XRD), microhardness and surface roughness techniques. The wear test was performed by pin-on-disc method. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) tests were also used to evaluate the corrosion resistance of the samples. The results demonstrated that in both nitriding conditions, wear and corrosion resistance of the treated samples decrease with increasing temperature from 500 °C to 550 °C. Moreover, nitriding under hot wall condition at the same temperature provided slightly better tribological and corrosion behavior in comparison with cold wall condition. In consequence, the lowest friction coefficient, and highest wear and corrosion resistance were found on the sample treated under hot wall condition at 500 °C, which had the maximum surface hardness and ε-Fe 2–3 N phase
A Theoretical Model for Metal Corrosion Degradation

Directory of Open Access Journals (Sweden)

David V. Svintradze

2010-01-01

Full Text Available Many aluminum and stainless steel alloys contain thin oxide layers on the metal surface which greatly reduce the corrosion rate. Pitting corrosion, a result of localized breakdown of such films, results in accelerated dissolution of the underlying metal through pits. Many researchers have studied pitting corrosion for several decades and the exact governing equation for corrosion pit degradation has not been obtained. In this study, the governing equation for corrosion degradation due to pitting corrosion behavior was derived from solid-state physics and some solutions and simulations are presented and discussed.
Hydrogen and helium trapping in tungsten deposition layers formed by RF plasma sputtering

International Nuclear Information System (INIS)

Kazunari Katayama; Kazumi Imaoka; Takayuki Okamura; Masabumi Nishikawa

2006-01-01

Understanding of tritium behavior in plasma facing materials is an important issue for fusion reactor from viewpoints of fuel control and radiation safety. Tungsten is used as a plasma facing material in the divertor region of ITER. However, investigation of hydrogen isotope behavior in tungsten deposition layer is not sufficient so far. It is also necessary to evaluate an effect of helium on a formation of deposition layer and an accumulation of hydrogen isotopes because helium generated by fusion reaction exists in fusion plasma. In this study, tungsten deposition layers were formed by sputtering method using hydrogen and helium RF plasma. An erosion rate and a deposition rate of tungsten were estimated by weight measurement. Hydrogen and helium retention were investigated by thermal desorption method. Tungsten deposition was performed using a capacitively-coupled RF plasma device equipped with parallel-plate electrodes. A tungsten target was mounted on one electrode which is supplied with RF power at 200 W. Tungsten substrates were mounted on the other electrode which is at ground potential. The plasma discharge was continued for 120 hours where pressure of hydrogen or helium was controlled to be 10 Pa. The amounts of hydrogen and helium released from deposition layers was quantified by a gas chromatograph. The erosion rate of target tungsten under helium plasma was estimated to be 1.8 times larger than that under hydrogen plasma. The deposition rate on tungsten substrate under helium plasma was estimated to be 4.1 times larger than that under hydrogen plasma. Atomic ratio of hydrogen to tungsten in a deposition layer formed by hydrogen plasma was estimated to be 0.17 by heating to 600 o C. From a deposition layer formed by helium plasma, not only helium but also hydrogen was released by heating to 500 o C. Atomic ratios of helium and hydrogen to tungsten were estimated to be 0.080 and 0.075, respectively. The trapped hydrogen is probably impurity hydrogen
Study on transition behavior of corrosion related environment near disposal site

International Nuclear Information System (INIS)

Masuda, K.; Nakanishi, T.; Kato, O.; Wada, R.

2005-01-01

Full text of publication follows: Disposal vessels are desired to stand for a certain period of time to stabilize radioactive wastes containing heat-generating substances. Besides, in case of wastes containing irradiated metal, which is a source of long-lived 14 C, long-term capability to enclose such long-life species is desired to the vessels. Since endurance of vessels is very affected by surrounding environment, evaluation of long-term environmental transition is important. In this study, we focused on the behavior of red-ox conditions and pH by reactive transport modeling in order to obtain fundamental knowledge about long-term transition of corrosion-related environment around metal vessels or metal-containing radioactive wastes. A two-dimensional reactive transport simulation was applied to a modeled repository site with engineering barrier system including cement and bentonite, etc., in consideration of following chemical models: - The metal corrosion rate was modeled to consider its effect on red-ox conditions. - The corrosion rate of carbon steel was modeled as kinetic reaction rate of production of ferrous ion and electrons as a function of pH and oxygen concentration, based on the experimental results observed under highly-controlled reducing conditions (1). - Formation of corrosion products was modeled by solubility products of iron oxides, such as magnetite, according to analytical results by in-situ XPS (2). - Cement composition and its reaction with groundwater were modeled by chemical equilibrium of primary and secondary minerals, for example, calcium silicates with several C/S ratios to consider the long-term transition of pH with cement degradations. According to the simulation results, the variation of red-ox conditions and pH around the disposal vessels has been estimated. Main component of cement composition slowly changes to calcium silicate having lower C/S ratios, resulting in decrease of pH. Although it depends on the bentonite efficiency
Characterization of the corrosion behavior of an austenitic stainless steel for biomedical applications coated with Ti N, Ti CN And DLC PVD coatings

International Nuclear Information System (INIS)

Antunes, Renato Altobelli

2006-01-01

Metallic biomaterials must present a combination of properties such as corrosion resistance, biocompatibility and mechanical resistance. Austenitic stainless steels, especially AISI 316L combine these properties with the easy of fabrication at low cost. However, they are prone to corrosion in physiological solutions. Furthermore, their corrosion products may lead to infectious ou allergenic reactions in the tissues around the implant device. In the present work, coatings produced by physical vapour deposition (PVD) methods have been applied on the surface of a 316L stainless steel to increase its corrosion resistance and biocompatibility. Three thin films were tested: titanium nitride (TiN), titanium carbonitride (TiCN) and diamond-like carbon (DLC). These materials present high hardness, wear resistance and intrinsic biocompatibility that are key features when considering biomedical applications. The characterization of the electrochemical behavior of the stainless steel coated with the three different films showed that the presence of surface defects are deleterious to the corrosion resistance of the substrate. These defects were observed using scanning electron microscopy. The evolution of the electrochemical behavior of the coated steel was explained through a mechanism based on the experimental results obtained using electrochemical impedance spectroscopy. Two different passivation treatments were carried out on the stainless steel surface, either in sulfuric or nitric acid solutions, to increase its corrosion resistance. The results suggested que these treatments were not efficient, but may be modified to improve its performance. The electronic properties of the passive films of the non-passivated and passivated stainless steel were studied using the Mott-Schottky approach. The films presented a duplex character. Below the flat band potential the behavior is typical of a highly doped type-p semiconductor. Above the flat band potential is typical of a highly
Impact of neutron irradiation on thermal helium desorption from iron

Energy Technology Data Exchange (ETDEWEB)

Hu, Xunxiang, E-mail: hux1@ornl.gov [Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States); Field, Kevin G. [Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States); Taller, Stephen [University of Michigan, Ann Arbor, MI 48109 (United States); Katoh, Yutai [Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States); Wirth, Brian D. [Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States); University of Tennessee, Knoxville, TN 37996 (United States)

2017-06-15

The synergistic effect of neutron irradiation and transmutant helium production is an important concern for the application of iron-based alloys as structural materials in fission and fusion reactors. In this study, we investigated the impact of neutron irradiation on thermal helium desorption behavior in high purity iron. Single crystalline and polycrystalline iron samples were neutron irradiated in HFIR to 5 dpa at 300 °C and in BOR-60 to 16.6 dpa at 386 °C, respectively. Following neutron irradiation, 10 keV He ion implantation was performed at room temperature on both samples to a fluence of 7 × 10{sup 18} He/m{sup 2}. Thermal desorption spectrometry (TDS) was conducted to assess the helium diffusion and clustering kinetics by analyzing the desorption spectra. The comparison of He desorption spectra between unirradiated and neutron irradiated samples showed that the major He desorption peaks shift to higher temperatures for the neutron-irradiated iron samples, implying that strong trapping sites for He were produced during neutron irradiation, which appeared to be nm-sized cavities through TEM examination. The underlying mechanisms controlling the helium trapping and desorption behavior were deduced by assessing changes in the microstructure, as characterized by TEM, of the neutron irradiated samples before and after TDS measurements.
Study on the corrosion assessment of overpack welds-III (Joint research)

International Nuclear Information System (INIS)

Mitsui, Hiroyuki; Takahashi, Rieko; Otsuki, Akiyoshi; Asano, Hidekazu; Taniguchi, Naoki; Yui, Mikazu

2006-12-01

There is some possibility that the corrosion resistance of overpack welds is different from that of base metal due to the differences of material properties. In this study, corrosion behavior of welded joint for carbon steel was compared with base metal using the specimens taken from welded joint model fabricated by TIG, MAG and EBW respectively. The corrosion tests were performed for following four items. Passivation behavior and corrosion type. Propagation of general corrosion, pitting corrosion and crevice corrosion under aerobic condition. Stress corrosion cracking susceptibility. Propagation of general corrosion and hydrogen embrittlement under anaerobic condition. The results of these corrosion tests indicated that the corrosion resistance of welded metal by TIG and MAG was inferior to base metal for general corrosion, pitting corrosion and crevice corrosion. It was implied that the filler materials used for welding affected the corrosion resistance. No deterioration of corrosion resistance was observed in any corrosion modes for EBW, which does not need filler material. The susceptibility to stress corrosion cracking of welded metal and heat affected zone was lower than that of base metal. (author)
Helium release from neutron-irradiated Li{sub 2}O single crystals

Energy Technology Data Exchange (ETDEWEB)

Yamaki, Daiju; Tanifuji, Takaaki; Noda, Kenji [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment

1998-03-01

Helium release behavior in post-irradiation heating tests was investigated for Li{sub 2}O single crystals which had been irradiated with thermal neutrons in JRR-4 and JRR-2, and fast neutrons in FFTF. It is clarified that the helium release curves from JRR-4 and JRR-2 specimens consists of only one broad peak. From the dependence of the peak temperatures on the neutron fluence and the crystal diameter, and the comparison with the results obtained for sintered pellets, it is considered that the helium generated in the specimen is released through the process of bulk diffusion with trapping by irradiation defects such as some defect clusters. For the helium release from FFTF specimens, two broad peaks were observed in the release curves. It is considered to suggest that two different diffusion paths exist for helium migration in the specimen, that is, bulk diffusion and diffusion through the micro-crack due to the heavy irradiation. In addition, helium bubble formation after irradiation due to the high temperature over 800K is suggested. (J.P.N.)
Comparison of corrosion behavior of EUROFER and CLAM steels in flowing Pb–15.7Li

Energy Technology Data Exchange (ETDEWEB)

Konys, J., E-mail: juergen.konys@kit.edu [Karlsruhe Institute of Technology, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Krauss, W. [Karlsruhe Institute of Technology, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Zhu, Z.; Huang, Q. [Institute of Nuclear Energy Safety Technology, Chinese Academy of Sciences, Hefei, Anhui 230031 (China)

2014-12-15

Ferritic martensitic steels are envisaged to be applied as structural materials in HCLL blanket systems. Their compatibility with the liquid breeder, which is in direct contact with the structural alloy, will be essential for reliable and safe operation of the designed blankets. Formerly performed corrosion tests of RAFM steels in PICOLO loop of KIT were mainly done at high flow velocities, e.g., 0.22 m/s and delivered severe attack with material loss rates above 400 μm/yr at 823 K. Meanwhile, flow velocities for corrosion testing have been reduced into the “cm range” to be near fusion relevant conditions. Among the international ITER-partners, many varieties of RAFM steels have been developed and manufactured within the last decade, e.g., the so-called Chinese Low Activation Martensitic steel (CLAM). In this paper, the long term corrosion behavior of EUROFER and CLAM steel in flowing Pb–15.7Li will be presented at a flow velocity of about 0.10 m/s and compared with earlier obtained results of RAFM steels exposed at other operation parameters of PICOLO loop. The observed corrosion attack is near 220 μm/yr and fits well to predictions made by MATLIM-modeling for low flow velocities in the turbulent flow regime.
Corrosion process studies in a nuclear waste container

International Nuclear Information System (INIS)

Guasp, Ruben A.; Lanzani, Liliana A.; Coronel, Pascual; Bruzzoni, Pablo; Semino, Carlos J.

1999-01-01

Latest results on corrosion behavior studies on high activity nuclear waste container are reported. Corrosion evaluation on lead base alloys and modeling to predict carbon steel external container cover generalized corrosion, are the main issues of these studies. (author)
Liquid helium

CERN Document Server

Atkins, K R

1959-01-01

Originally published in 1959 as part of the Cambridge Monographs on Physics series, this book addresses liquid helium from the dual perspectives of statistical mechanics and hydrodynamics. Atkins looks at both Helium Three and Helium Four, as well as the properties of a combination of the two isotopes. This book will be of value to anyone with an interest in the history of science and the study of one of the universe's most fundamental elements.
Effects of Welding Parameters on Strength and Corrosion Behavior of Dissimilar Galvanized Q&P and TRIP Spot Welds

Directory of Open Access Journals (Sweden)

Pasquale Russo Spena

2017-12-01

Full Text Available This study investigates the effects of the main welding parameters on mechanical strength and corrosion behavior of galvanized quenching and partitioning and transformation induced plasticity spot welds, which are proposed to assemble advanced structural car elements for the automotive industry. Steel sheets have been welded with different current, clamping force, and welding time settings. The quality of the spot welds has been assessed through lap-shear and salt spray corrosion tests, also evaluating the effects of metal expulsion on strength and corrosion resistance of the joints. An energy dispersive spectrometry elemental mapping has been used to assess the damage of the galvanized zinc coating and the nature of the corrosive products. Welding current and time have the strongest influence on the shear strength of the spot welds, whereas clamping force is of minor importance. However, clamping force has the primary effect on avoiding expulsion of molten metal from the nugget during the joining process. Furthermore, clamping force has a beneficial influence on the corrosion resistance because it mainly hinders the permeation of the corrosive environment towards the spot welds. Although the welded samples can exhibit high shear strength also when a metal expulsion occurs, this phenomenon should be avoided because it enhances the damage and vaporization of the protective zinc coating.
Influence of calcareous deposit on corrosion behavior of Q235 carbon steel with sulfate-reducing bacteria

Science.gov (United States)

Zhang, Jie; Li, Xiaolong; Wang, Jiangwei; Xu, Weichen; Duan, Jizhou; Chen, Shougang; Hou, Baorong

2017-12-01

Cathodic protection is a very effective method to protect metals, which can form calcareous deposits on metal surface. Research on the interrelationship between fouling organism and calcareous deposits is very important but very limited, especially sulfate-reducing bacteria (SRB). SRB is a kind of very important fouling organism that causes microbial corrosion of metals. A study of the influence of calcareous deposit on corrosion behavior of Q235 carbon steel in SRB-containing culture medium was carried out using electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM) and surface spectroscopy (EDS). The calcareous deposit was formed with good crystallinity and smooth surface under the gradient current density of -30 μA cm-2 in natural seawater for 72 h. Our results can help elucidate the formation of calcareous deposits and reveal the interrelationship between SRB and calcareous deposits under cathodic protection. The results indicate that the corrosion tendency of carbon steel was obviously affected by Sulfate-reducing Bacteria (SRB) metabolic activity and the calcareous deposit formed on the surface of carbon steel under cathodic protection was favourable to reduce the corrosion rate. Calcareous deposits can promote bacterial adhesion before biofilm formation. The results revealed the interaction between biofouling and calcareous deposits, and the anti-corrosion ability was enhanced by a kind of inorganic and organic composite membranes formed by biofilm and calcareous deposits.

Relationship between Corrosion Level of Rebar Embedded in Concrete, Corrosion Potential and Current Density Measured by Non-destructive Test Method

International Nuclear Information System (INIS)

Chung, Lan; Cho, Seung Ho; Roh, Young Sook; Kim, Joong Koo

2004-01-01

The purpose of this study is to identify corrosion mechanism and develop qualitative measurement method of corrosion level. Fist of all, structural behavior of each different level of corrosion states have been evaluated. And mathematical models that can predict corrosion level in terms of electric potential and corrosion intensity are proposed. Corrosion rate in reinforcing bar was investigated in this study using accelerated corrosion method due to electric potential differences based on Faradays law. Total 288 measurement spots were designed in terms of corrosion rates, diameter of reinforcing bars, and concrete cover thickness. Corrosion current densities and corrosion potentials of concrete were measured on these specimens using Gecor device. This study suggested the relationship between corrosion levels, and measured electric current density as follows
Effects of cell size and macrosegregation on the corrosion behavior of a dilute Pb-Sb alloy

Energy Technology Data Exchange (ETDEWEB)

Rosa, Daniel M.; Spinelli, Jose E.; Osorio, Wislei R.; Garcia, Amauri [Department of Materials Engineering, State University of Campinas-UNICAMP, P.O. Box 6122, 13083-970 Campinas, Sao Paulo (Brazil)

2006-11-08

The aim of this study was to examine the effect of cooling rate on the cellular growth of a Pb-0.85wt%Sb alloy and to evaluate the influences of cell size and of the corresponding macrosegregation profile on the resultant corrosion behavior. In order to obtain the as-cast samples a water-cooled unidirectional solidification system was used. Such experimental set-up has permitted the development of a clear cellular structural array even for relative high cooling rates and has allowed a wide range of solidification conditions to be analyzed. Macrostructural and microstructural aspects along the casting were characterized by optical microscopy and scanning electron microscope (SEM) techniques. The electrochemical impedance spectroscopy technique and potentiodynamic curves (Tafel extrapolation) were used to analyze the corrosion resistance of samples collected along the casting length and immersed in a 0.5M H{sub 2}SO{sub 4} solution at 25{sup o}C. It was found that the corrosion rate decreases with increasing cell spacing and that the pre-programming of microstructure cell size can be used as an alternative way to produce as-cast components of Pb-Sb alloys, such as battery grids, with better corrosion resistance. (author)
Effect of antimony on the corrosion behavior of low-alloy steel for flue gas desulfurization system

International Nuclear Information System (INIS)

Le, D.P.; Ji, W.S.; Kim, J.G.; Jeong, K.J.; Lee, S.H.

2008-01-01

The alloying effect of Sb in a new low-alloy steel for the purpose of FGD materials was investigated by potentiodynamic polarization, linear polarization resistance measurement, electrochemical impedance spectroscopy (EIS) and weight loss measurements in an aggressive solution of 16.9 vol.% H 2 SO 4 + 0.35 vol.% HCl (modified green death solution) at 60 deg. C, pH -0.3. All measurements confirmed the marked improvement in the corrosion behavior of the low-alloy steel via the addition of a small amount of Sb, particularly for the 0.10Sb steel. Pitting corrosion was detected by scanning electron microscopy (SEM) on the surface of blank steel and 0.05Sb steel, but not 0.10Sb steel, after weight loss measurements. X-ray photoelectron spectroscopy (XPS) analysis of the corroded surfaces after EIS and linear polarization measurements showed that the decrease in corrosion rates was due to the formation of a protective Sb 2 O 5 oxide film on the surface of the Sb-containing steels. Moreover, the addition of 0.10% Sb stimulated the development of high corrosion inhibiting, Cu-containing compounds which further inhibited the anodic and cathodic reactions
Microstructure, mechanical property, corrosion behavior, and in vitro biocompatibility of Zr-Mo alloys.

Science.gov (United States)

Zhou, F Y; Wang, B L; Qiu, K J; Li, L; Lin, J P; Li, H F; Zheng, Y F

2013-02-01

In this study, the microstructure, mechanical properties, corrosion behaviors, and in vitro biocompatibility of Zr-Mo alloys as a function of Mo content after solution treatment were systemically investigated to assess their potential use in biomedical application. The experimental results indicated that Zr-1Mo alloy mainly consisted of an acicular structure of α' phase, while ω phase formed in Zr-3Mo alloy. In Zr-5Mo alloy, retained β phase and a small amount of precipitated α phase were observed. Only the retained β phase was obtained in Zr-10Mo alloy. Zr-1Mo alloy exhibited the greatest hardness, bending strength, and modulus among all experimental Zr-Mo alloys, while β phase Zr-10Mo alloy had a low modulus. The results of electrochemical corrosion indicated that adding Mo into Zr improved its corrosion resistance which resulted in increasing the thermodynamic stability and passivity of zirconium. The cytotoxicity test suggested that the extracts of the studied Zr-Mo alloys produced no significant deleterious effect to fibroblast cells (L-929) and osteoblast cells (MG 63), indicating an excellent in vitro biocompatibility. Based on these facts, certain Zr-Mo alloys potentially suitable for different biomedical applications were proposed. Copyright © 2012 Wiley Periodicals, Inc.
AC impedance spectroscopy study of the corrosion behavior of an AZ91 magnesium alloy in 0.1 M sodium sulfate solution

International Nuclear Information System (INIS)

Chen, Jian; Wang, Jianqiu; Han, Enhou; Dong, Junhua; Ke, Wei

2007-01-01

The corrosion behavior of an AZ91 magnesium alloy in 0.1 M sodium sulfate solution at the corrosion potential (E corr ) was investigated using electrochemical impedance spectroscopy (EIS), environmental scanning electron microscopy (ESEM), energy dispersive X-ray spectroscopy (EDS), and X-ray photoelectron spectroscopy (XPS). The results showed that when the immersion time was less than 18th, general corrosion occurred on the surface and the main corrosion products were hydroxides and sulfates. The film coverage effect was the main mechanism for the corrosion process of AZ91 alloy. At this stage, the matrix had a better corrosion resistance. With the increasing immersion time, pitting occurred on the surface. At this stage, the corrosion process was controlled by three surface state variables: the area fraction θ 1 of the region controlled by the formation of Mg(OH) 2 , the area fraction θ 2 of the region controlled by the precipitation of MgAl 2 (SO 4 ) 4 .2H 2 O, and the metastable Mg + concentration C m
The corrosion behavior of CVI SiC matrix in SiC{sub f}/SiC composites under molten fluoride salt environment

Energy Technology Data Exchange (ETDEWEB)

Wang, Hongda [Structural Ceramics and Composites Engineering Research Center, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); School of Graduate, University of Chinese Academy of Sciences, Beijing 100049 (China); Feng, Qian [Analysis and Testing Center, Donghua University, Shanghai 201600 (China); Wang, Zhen, E-mail: jeff@mail.sic.ac.cn [Structural Ceramics and Composites Engineering Research Center, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); Zhou, Haijun; Kan, Yanmei; Hu, Jianbao [Structural Ceramics and Composites Engineering Research Center, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); Dong, Shaoming, E-mail: smdong@mail.sic.ac.cn [Structural Ceramics and Composites Engineering Research Center, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China); State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China)

2017-04-15

High temperature corrosion behavior and microstructural evolution of designed chemical-vapor-infiltrated SiC matrix in SiC fiber reinforced SiC ceramic matrix composites in 46.5LiF-11.5NaF-42.0KF (mol. %) eutectic salt at 800 °C for various corrosion time was studied. Worse damage was observed as extending the exposure time, with the mass loss ratio increasing from 0.716 wt. % for 50 h to 5.914 wt. % for 500 h. The mass loss rate showed a trend of first decrease and then increase with the extended corrosion exposure. Compared with the near-stoichiometric SiC matrix layers, the O-contained boundaries between deposited matrix layers and the designed Si-rich SiC matrix layers were much less corrosion resistant and preferentially corroded. Liner relationship between the mass loss ratio and the corrosion time obtained from 50 h to 300 h indicated that the corrosion action was reaction-control process. Further corrosion would lead to matrix layer exfoliation and higher mass loss ratio.
Corrosion fatigue behavior of high strength brass in aqueous solutions

Energy Technology Data Exchange (ETDEWEB)

Hamada, A.S.; Kassem, M.A.; Ramadan, R.M.; El-Zeky, M.A. [Suez Canal Univ., Dept. of Metallurgy and Materials Engineering (Egypt)

2000-07-01

Corrosion fatigue behavior of British Standard high strength brass, CZ 127 has been studied in various environments, 3.5%NaC1 solution and 3.5%NaC1 containing 1000ppm ammonia by applying the reverse bending technique, strain-controlled cyclic, at 67 cycles/min. Characteristics of the produced alloy were studied using differential thermal analysis with applying its results in heat treating of the alloy; metallographic examinations; hardness measurements; X-ray; and electrochemical behavior of the unstressed alloy. CZ 127 was fatigued at three different conditions, solution treated, peak aged, and over aged at a fixed strain amplitude, 0.03 5. Solution treated alloy gave the best fatigue properties in all environments tested among the other materials. Results of the alloy studied were compared with that obtained of 70/30 {alpha}-brass. Fracture surface of the fatigued alloy was examined using optical microscope and scanning electron microscope equipped with EDX. (author)
Corrosion fatigue behavior of high strength brass in aqueous solutions

International Nuclear Information System (INIS)

Hamada, A.S.; Kassem, M.A.; Ramadan, R.M.; El-Zeky, M.A.

2000-01-01

Corrosion fatigue behavior of British Standard high strength brass, CZ 127 has been studied in various environments, 3.5%NaC1 solution and 3.5%NaC1 containing 1000ppm ammonia by applying the reverse bending technique, strain-controlled cyclic, at 67 cycles/min. Characteristics of the produced alloy were studied using differential thermal analysis with applying its results in heat treating of the alloy; metallographic examinations; hardness measurements; X-ray; and electrochemical behavior of the unstressed alloy. CZ 127 was fatigued at three different conditions, solution treated, peak aged, and over aged at a fixed strain amplitude, 0.03 5. Solution treated alloy gave the best fatigue properties in all environments tested among the other materials. Results of the alloy studied were compared with that obtained of 70/30 α-brass. Fracture surface of the fatigued alloy was examined using optical microscope and scanning electron microscope equipped with EDX. (author)
The corrosion rate and the hydrogen absorption behavior of titanium under reducing condition-III. Research document

International Nuclear Information System (INIS)

Suzuki, H.; Taniguchi, N.; Kawakami, S.

2005-03-01

Titanium is one of the candidate materials for overpacks as a high corrosion resistance metal. At the initial stage of repository, oxidizing condition will be given around the overpack because oxygen will be brought from the ground. The oxygen will be consumed by the reaction with impurities in buffer material or corrosion of overpack, and reducing condition will be achieved around the overpack. With the changing of redox condition, the water reduction becomes to dominate the cathodic reaction accompanying hydrogen generation. Crevice corrosion and hydrogen embrittlement are main causes of the damage of long term integrity of titanium overpack. However, it is not known about the corrosion resistance and hydrogen absorption behavior of titanium under reduction condition. In this study, the completely sealed ampoule test and the immersion test of titanium in aqueous solution and bentonite was carried out. In order to obtain reliable data about the hydrogen generation rate and the ratio of hydrogen absorption in titanium. From the result of 3 years immersion tests, corrosion rate of titanium were estimated to be in the order of 10 -2 ∼10 -1 μm/y in the aqueous solution, and 10 -3 ∼10 -2 μm/y in bentonite. This value is almost the same as the last report. Almost all the hydrogen generated by corrosion was absorbed in titanium in the immersion tests in completely sealed ampoule. In the examination that changed each parameter, it was suggested that the amount of the hydrogen absorption become 2∼3 times in 1M HCO 3- and pH13. (author)
CALCULATED REGENERATOR PERFORMANCE AT 4 K WITH HELIUM-4 AND HELIUM-3

International Nuclear Information System (INIS)

Radebaugh, Ray; Huang Yonghua; O'Gallagher, Agnes; Gary, John

2008-01-01

The helium-4 working fluid in regenerative cryocoolers operating with the cold end near 4 K deviates considerably from an ideal gas. As a result, losses in the regenerator, given by the time-averaged enthalpy flux, are increased and are strong functions of the operating pressure and temperature. Helium-3, with its lower boiling point, behaves somewhat closer to an ideal gas in this low temperature range and can reduce the losses in 4 K regenerators. An analytical model is used to find the fluid properties that strongly influence the regenerator losses as well as the gross refrigeration power. The thermodynamic and transport properties of helium-3 were incorporated into the latest NIST regenerator numerical model, known as REGEN3.3, which was used to model regenerator performance with either helium-4 or helium-3. With this model we show how the use of helium-3 in place of helium-4 can improve the performance of 4 K regenerative cryocoolers. The effects of operating pressure, warm-end temperature, and frequency on regenerators with helium-4 and helium-3 are investigated and compared. The results are used to find optimum operating conditions. The frequency range investigated varies from 1 Hz to 30 Hz, with particular emphasis on higher frequencies
The Effect of superficial cracks of the concrete on the behavior and corrosion rate of steel rebars in Persian Golf (Booshehr)

International Nuclear Information System (INIS)

Afshar, A.; Rajabi, A.

2001-01-01

The presence of superficial cracks in concrete increases the diffusion of destructive agents into concrete and the corrosion of rebars will take place. In the present work, the effects of cracks width on the behavior and corrosion rate of steel rebars in the concrete containing cements type I and II at Persian Gulf water have been studied. The results show that the corrosion rate of steel rebars in the concrete with cracks width less than 0.4 mm is negligible, but with increasing the cracks width to 0.7 mm, the corrosion rate increase rapidly. Also, the corrosion gate of gebars in the concrete containing cement type I is more than that of cement type II. The visual inspection of the surface area of gebars shows that the corroded area is 6-7 times of the crack width and length
INVESTIGATIONS ON THE CORROSION OF CONSTRUCTIONAL ...

African Journals Online (AJOL)

BCSE

The corrosion behavior of three constructional steels used in Senegal, S235, .... the attack is deep and the pits propagate in depth with a high current density. ..... Equivalent electrical circuit parameters for the corrosion process of S355 and ...
Properties of vanadium-base alloys irradiated in the Dynamic Helium Charging Experiment*1

Science.gov (United States)

Chung, H. M.; Loomis, B. A.; Smith, D. L.

1996-10-01

One property of vanadium-base alloys that is not well understood in terms of their potential use a fusion reactor structural materials, is the effect of simultaneous generation of helium and neutron damage. In the present Dynamic Helium Charging Experiment (DHCE), helium was produced uniformly in the specimen at linear rates of ≈ 0.4 to 4.2 appm helium/dpa by the decay of tritium during irradiation to 18-31 dpa at 425-600°C in Li-filled capsules in a sodium-cooled fast reactor. This paper presents results of postirradiation examination and tests of microstructure and mechanical properties of V5Ti, V3Ti1Si, V8Cr6Ti, and V4Cr4Ti (the latter alloy has been identified as the most promising candidate vanadium alloy). Effects of helium on tensile strength and ductility were insignificant after irradiation and testing at > 420°C. However, postirradiation ductilities at irradiation. Ductile—brittle transition behavior of the DHCE specimens was also determined from bend tests and fracture appearance of transmission electron microscopy (TEM) disks and broken tensile specimens. No brittle behavior was observed at temperatures > - 150°C in DHCE specimens. Predominantly brittle-cleavage fracture morphologies were observed only at - 196°C in some specimens that were irradiated to 31 dpa at 425°C during the DHCE. For the helium generation rates in this experiment (≈ 0.4-4.2 appm He/dpa), grain-boundary coalescence of helium microcavities was negligible and intergranular fracture was not observed.
Microstructure, mechanical property and corrosion behavior of interpenetrating (HA + β-TCP)/MgCa composite fabricated by suction casting

International Nuclear Information System (INIS)

Wang, X.; Dong, L.H.; Li, J.T.; Li, X.L.; Ma, X.L.; Zheng, Y.F.

2013-01-01

The novel interpenetrating (HA + β-TCP)/MgCa composites were fabricated by infiltrating MgCa alloy into porous HA + β-TCP using suction casting technique. The microstructure, mechanical properties and corrosion behaviors of the composites have been evaluated by means of scanning electron microscopy (SEM), X-ray diffraction (XRD), mechanical testing, electrochemical and immersion tests. It was shown that the composites had compact structure and the interfacial bonding between MgCa alloy and HA + β-TCP scaffolds was very well. The ultimate compressive strength of the composites was about 500–1000 fold higher than that of the original porous scaffolds, and it still retained quarter-half of the strength of the bulk MgCa alloy. The electrochemical and immersion tests indicated that the corrosion resistance of the composites was better than that of the MgCa matrix alloy, and the corrosion products of the composite surface were mainly Mg(OH) 2 , HA and Ca 3 (PO 4 ) 2 . Meanwhile, the mechanical and corrosive properties of the (HA + β-TCP)/MgCa composites were adjustable by the choice of HA content. - Highlights: • The composites were fabricated by infiltrating MgCa alloy into porous HA + β-TCP. • The microstructure, mechanical and corrosion properties were investigated. • It showed composites had compact structures and good interfacial bonding. • The mechanical and corrosive properties can be adjustable by the HA content. • The corrosion mechanism of the composite has been explained
High temperature tensile properties of 316 stainless steel implanted with helium

International Nuclear Information System (INIS)

Hasegawa, Akira; Yamamoto, Norikazu; Shiraishi, Haruki

1993-01-01

Helium embrittlement is one of the problems in structural materials for fusion reactors. Recently, martensitic steels have been developed which have a good resistance to high-temperature helium embrittlement, but the mechanism has not yet been clarified. In this paper, tensile behaviors of helium implanted austenitic stainless steels, which are sensitive to the helium embrittlement, were studied and compared with those of martensitic steels under the same experimental conditions, and the effect of microstructure on helium embrittlement was discussed. Helium was implanted by 300 appm at 573-623 K to miniature tensile speciments of 316 austenitic steels using a cyclotron accelerator. Solution annealed (316SA) and 20% cold worked (316CW) specimens were used. Post-implantation tensile tests were carried out at 573, 873 and 973 K. Yield stress at 573 K increased with the helium implantation in 316SA and 316CW, but the yield stress changes of 316SA at 873 and 973 K were different from that of 316CW. Black-dots were observed in the as-implanted specimen and bubbles were observed in the speciments tensile-tested at 873 and 973 K. Intergranular fracture was observed at only 973 K in both of the 316SA and 316CW specimens. Therefore, cold work did not suppress the high-temperature helium embrittlement under this experimental condition. The difference in the influence of helium on type 316 steel and 9Cr martensitic steels were discussed. Test temperature change of reduction in are showed clearly that helium embrittlement did not occur in 9Cr martensitic steels but occurred in 316 austenitic steels. Fine microstructures of 9Cr martensitic steels should suppress helium embrittlement at high temperatures. (author)
New helium spectrum variable and a new helium-rich star

International Nuclear Information System (INIS)

Walborn, N.R.

1974-01-01

HD 184927, known previously as a helium-rich star, has been found to have a variable helium spectrum; the equivalent widths of five He I lines are larger by an average of 46 percent on a 1974 spectrogram than on one obtained with the same equipment in 1970. HD 186205 has been found to be a new, pronounced helium-rich star. (auth)
Anomalous dissolution of metals and chemical corrosion

Directory of Open Access Journals (Sweden)

DRAGUTIN M. DRAZIC

2005-03-01

Full Text Available An overview is given of the anomalous behavior of some metals, in particular Fe and Cr, in acidic aqueous solutions during anodic dissolution. The anomaly is recognizable by the fact that during anodic dissolutionmore material dissolves than would be expected from the Faraday law with the use of the expected valence of the formed ions. Mechanical disintegration, gas bubble blocking, hydrogen embrittlement, passive layer cracking and other possible reasons for such behavior have been discussed. It was shown, as suggested by Kolotyrkin and coworkers, that the reason can be, also, the chemical reaction in which H2O molecules with the metal form metal ions and gaseous H2 in a potential independent process. It occurs simultaneously with the electrochemical corrosion process, but the electrochemical process controls the corrosion potential. On the example of Cr in acid solution itwas shown that the reason for the anomalous behavior is dominantly chemical dissolution, which is considerably faster than the electrochemical corrosion, and that the increasing temperature favors chemical reaction, while the other possible reasons for the anomalous behavior are of negligible effect. This effect is much smaller in the case of Fe, but exists. The possible role of the chemical dissolution reacton and hydrogen evolution during pitting of steels and Al and stress corrosion cracking or corrosion fatigue are discussed.
Corrosion and carburization behavior of Al-rich surface layer on Ni-base alloy in supercritical-carbon dioxide environment

Energy Technology Data Exchange (ETDEWEB)

Lee, Ho Jung, E-mail: leehojung@kaist.ac.kr; Kim, Sung Hwan, E-mail: sciencetom@kaist.ac.kr; Kim, Hyunmyung, E-mail: h46kim@kaist.ac.kr; Jang, Changheui, E-mail: chjang@kaist.ac.kr

2016-12-01

Highlights: • Al-rich layer was developed on Alloy 600 by Al deposition and EB remelting. • When exposed to S-CO{sub 2} at 600 °C, mostly Cr{sub 2}O{sub 3} with transition Al{sub 2}O{sub 3} was formed. • Carburized region of amorphous C layer was observed at the oxide/matrix interface. • α-Al{sub 2}O{sub 3} was formed after pre-oxidation which resulted in superior resistance. - Abstract: In order to improve the corrosion and carburization resistance in a high-temperature supercritical-carbon dioxide (S-CO{sub 2}) environment, an Al-rich surface layer was developed on Alloy 600 by Al deposition and a subsequent high energy electron beam (EB) remelting. As a result of the EB surface treatment, an Al enriched (5–7 wt.%) micro-alloying zone (40 μm) was produced. When the EB surface-treated Alloy 600 was corroded in S-CO{sub 2} at 600 °C (20 MPa) for 500 h, the surface oxide layer mostly consisted of chromia (Cr{sub 2}O{sub 3}) with small amount of transition alumina (Al{sub 2}O{sub 3}). In addition, a carburized region of an amorphous C layer inter-mixed with the alumina was observed at the oxide/matrix interface. Meanwhile, when the EB surface-treated specimen was pre-oxidized in helium at 900 °C, α-alumina layer was formed on the surface, which showed superior corrosion and carburization resistance in S-CO{sub 2} environment. Therefore, it could be said that the presence of Al-rich surface layer alone is not enough to provide sufficient corrosion and carburization resistance in S-CO{sub 2} environment at 600 °C, unless pre-oxidation at higher temperature is applied to form a more protective α-alumina on the surface.
Testing and prediction of erosion-corrosion for corrosion resistant alloys used in the oil and gas production industry

Science.gov (United States)

Rincon, Hernan E.

The corrosion behavior of CRAs has been thoroughly investigated and documented in the public literature by many researchers; however, little work has been done to investigate erosion-corrosion of such alloys. When sand particles are entrained in the flow, the degradation mechanism is different from that observed for sand-free corrosive environment. There is a need in the oil and gas industry to define safe service limits for utilization of such materials. The effects of flow conditions, sand rate, pH and temperature on the erosion-corrosion of CRAs were widely studied. An extensive experimental work was conducted using scratch tests and flow loop tests using several experimental techniques. At high erosivity conditions, a synergistic effect between erosion and corrosion was observed. Under the high sand rate conditions tested, erosivity is severe enough to damage the passive layer protecting the CRA thereby enhancing the corrosion rate. In most cases there is likely a competition between the rates of protective film removal due to mechanical erosion and protective film healing. Synergism occurs for each of the three alloys examined (13Cr and Super13Cr and 22Cr); however, the degree of synergism is quite different for the three alloys and may not be significant for 22Cr for field conditions where erosivities are typically much lower that those occurring in the small bore loop used in this research. Predictions of the corrosion component of erosion-corrosion based on scratch test data compared reasonably well to test results from flow loops for the three CRAs at high erosivity conditions. Second order behavior appears to be an appropriate and useful model for representing the repassivation process of CRAs. A framework for a procedure to predict penetration rates for erosion-corrosion conditions was developed based on the second order model behavior observed for the re-healing process of the passive film of CRAs and on computational fluid dynamics (CFD) simulations
Corrosion behaviors of SMART materials in the ammonia atmosphere

International Nuclear Information System (INIS)

Baek, J. H.; Lee, M. H.; Choi, B. S.; Kim, J. P.; Jung, Y. H.; Lee, D. J.

1999-01-01

The corrosion characteristics of the zirconium-based alloy(Low-Sn Zircaloy-4) and titanium-based alloys(PT-7M and ASTM Gr.2), which would be used for fuel cladding tube and steam generator tube in the SMART, were investigated at 360 deg C, 400 deg C, 500 deg C, and 520 deg C in the ammonia atmosphere. In all test conditions, the resistance to uniform and nodular corrosion of zirconium-based alloy was inferior to that of titanium-based alloys. In the case of 360 deg C test, the corrosion rate of zirconium-based alloy decreased slightly with increasing the ammonia concentration, while that of titanium-based alloys increased. The test results above 400 deg C showed that the corrosion resistance of PT-7M alloys was superior to that of ASTM Gr.2 alloy and was not influenced from the variation of ammonia concentration

Effects of dextrose and lipopolysaccharide on the corrosion behavior of a Ti-6Al-4V alloy with a smooth surface or treated with double-acid-etching.

Science.gov (United States)

Faverani, Leonardo P; Assunção, Wirley G; de Carvalho, Paulo Sérgio P; Yuan, Judy Chia-Chun; Sukotjo, Cortino; Mathew, Mathew T; Barao, Valentim A

2014-01-01

Diabetes and infections are associated with a high risk of implant failure. However, the effects of such conditions on the electrochemical stability of titanium materials remain unclear. This study evaluated the corrosion behavior of a Ti-6Al-4V alloy, with a smooth surface or conditioned by double-acid-etching, in simulated body fluid with different concentrations of dextrose and lipopolysaccharide. For the electrochemical assay, the open-circuit-potential, electrochemical impedance spectroscopy, and potentiodynamic test were used. The disc surfaces were characterized by scanning electron microscopy and atomic force microscopy. Their surface roughness and Vickers microhardness were also tested. The quantitative data were analyzed by Pearson's correlation and independent t-tests (α = 0.05). In the corrosion parameters, there was a strong lipopolysaccharide correlation with the Ipass (passivation current density), Cdl (double-layer capacitance), and Rp (polarization resistance) values (pdextrose and lipopolysaccharide was correlated with the Icorr (corrosion current density) and Ipass (pdextrose and lipopolysaccharide. The combination of dextrose and lipopolysaccharide affected the corrosion behavior of the Ti-6Al-4V alloy surface treated with double-acid-etching. However, no dose-response corrosion behavior could be observed. These results suggest a greater susceptibility to corrosion of titanium implants in diabetic patients with associated infections.
Corrosion behaviors of Mg and its alloys with different Al contents in a modified simulated body fluid

Energy Technology Data Exchange (ETDEWEB)

Wen Zhaohui [Department of Ultrasound, First Affiliated Hospital of Harbin Medical University, Harbin 150001 (China); Wu Changjun, E-mail: wucj163@126.co [Department of Ultrasound, First Affiliated Hospital of Harbin Medical University, Harbin 150001 (China); Dai Changsong, E-mail: changsd@hit.edu.c [School of Chemistry Engineering and Technology, Harbin Institute of Technology, Harbin 150001 (China); Yang Feixia [School of Chemistry Engineering and Technology, Harbin Institute of Technology, Harbin 150001 (China)

2009-11-20

The corrosion behaviors of pure magnesium (Mg) and three Mg alloys with different Al contents were investigated in a modified simulated body fluid (m-SBF) through immersion tests, Tafel experiments, and electrochemical impedance spectroscopic (EIS) experiments. The immersion results show that the corrosion rates (CRs) of the four samples were in an order of AZ91D < AZ61 < AZ31 < pure Mg after immersion for 1 day. With an increase in immersion time, their corrosion rates decreased and then a stable stage was reached after 16 days. The order of CRs of the four samples changed to AZ91D < pure Mg < AZ61 < AZ31 after immersion for 24 days. The results of EIS experiments indicate that the charge transfer resistance (R{sub ct}) of the three magnesium alloys initially increased and then decreased while the R{sub ct} of pure Mg was kept lower within 24 h. The results of a scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) show that pure Mg and three alloys were heterogeneously corroded in the m-SBF. The corrosion of pure Mg, which showed a more uniform corrosion appearance, resulted from localized corrosion over the entire surface. Alloy AZ91D (of 8.5-9.5 wt.% Al) showed relatively uniform corrosion morphology and the {beta}-Mg{sub 12}Al{sub 17} precipitates in alloy AZ91D were more homogeneously and continuously distributed along the grain boundaries. Obvious corrosion pits were found on the surface of alloy AZ61 and AZ31. The corrosion pits of alloy AZ61 were shallower than those of alloy AZ31. Alloy AZ61 (of 5.8-7.2 wt.% Al) possessed more Al{sub 8}Mn{sub 5} and a little {beta}-Mg{sub 12}Al{sub 17} presented along the grain boundary heterogeneously and discontinuously. Al{sub 8}Mn{sub 5} was the main phase of the AZ31 alloy (of 2.5-3.5 wt.% Al) dispersed into the matrix. In conclusion, the microstructure and the Al content in the {alpha}-Mg (Al) matrix significantly affected the corrosion properties of the alloys in the m-SBF. With the increase
[Effect of fluoride concentration on the corrosion behavior of cobalt-chromium alloy fabricated by two different technology processes].

Science.gov (United States)

Qiuxia, Yang; Ying, Yang; Han, Xu; Di, Wu; Ke, Guo

2016-02-01

This study aims to determine the effect of fluoride concentration on the corrosion behavior of cobalt-chromium alloy fabricated by two different technology processes in a simulated oral environment. A total of 15 specimens were employed with selective laser melting (SLM) and another 15 for traditional casting (Cast) in cobalt-chromium alloy powders and blocks with the same material composition. The corrosion behavior of the specimens was studied by potentiodynamic polarization test under different oral environments with varying solubilities of fluorine (0, 0.05%, and 0.20% for each) in acid artificial saliva (pH = 5.0). The specimens were soaked in fluorine for 24 h, and the surface microstructure was observed under a field emission scanning electron microscope after immersing the specimens in the test solution at constant temperature. The corrosion potential (Ecorr) value of the cobalt-chromium alloy cast decreased with increasing fluoride concentration in acidic artificial saliva. The Ecorr, Icorr, and Rp values of the cobalt-chromium alloy fabricated by two different technology processes changed significantly when the fluoride concentration was 0.20% (P technology processes exhibited a statistically significant difference. The Icorr value of the cobalt-chromium alloy cast was higher than that in the SLM group cobalt-chromium alloy when the fluoride concentration was 0.20% (P technology processes. The corrosion resistance of the cobalt-chromium alloy cast was worse than that of the SLM group cobalt-chromium alloy when the fluoride concentration was 0.20%.
Effect of Thermomechanical Processing and Crystallographic Orientation on the Corrosion Behavior of API 5L X70 Pipeline Steel

Science.gov (United States)

Ohaeri, Enyinnaya; Omale, Joseph; Eduok, Ubong; Szpunar, Jerzy

2018-04-01

This work presents the electrochemical response of X70 pipeline steel substrates thermomechanically processed at different conditions. The WE sample was hot rolled at a temperature range of 850 °C to 805 °C and cooled at a rate of 42.75 °C/s. Another sample WD was hot rolled from 880 °C to 815 °C and cooled at a faster rate of 51.5 °C/s. Corrosion tests were conducted electrochemically by potentiodynamic polarization in hydrogen-charged and non-hydrogen-charged environments. A lower corrosion rate was measured with hydrogen charging due to the rapid formation of corrosion product film on pipeline substrate, but WE specimen emerged as the most susceptible to corrosion with and without hydrogen charging. Variations in thermomechanical rolling conditions influenced grain orientation, protective film properties, corrosion, and cracking behavior on both specimens. Cracks were seen in both specimens after hydrogen charging, but specimen WE experienced a more intense deterioration of protective corrosion product film and subsequent cracking. A large part of specimen WD retained its protective corrosion product film after the polarization test, and sites where spalling occurred resulted in pitting with less cracking. Despite weak crystallographic texture noticed in both specimens, WD showed a higher intensity of corrosion-resistant 111||ND-oriented grains, while WE showed a more random distribution of 111||ND-, 011||ND-, and 001||ND-oriented grains with a lower intensity.
Effect of Thermomechanical Processing and Crystallographic Orientation on the Corrosion Behavior of API 5L X70 Pipeline Steel

Science.gov (United States)

Ohaeri, Enyinnaya; Omale, Joseph; Eduok, Ubong; Szpunar, Jerzy

2018-06-01

This work presents the electrochemical response of X70 pipeline steel substrates thermomechanically processed at different conditions. The WE sample was hot rolled at a temperature range of 850 °C to 805 °C and cooled at a rate of 42.75 °C/s. Another sample WD was hot rolled from 880 °C to 815 °C and cooled at a faster rate of 51.5 °C/s. Corrosion tests were conducted electrochemically by potentiodynamic polarization in hydrogen-charged and non-hydrogen-charged environments. A lower corrosion rate was measured with hydrogen charging due to the rapid formation of corrosion product film on pipeline substrate, but WE specimen emerged as the most susceptible to corrosion with and without hydrogen charging. Variations in thermomechanical rolling conditions influenced grain orientation, protective film properties, corrosion, and cracking behavior on both specimens. Cracks were seen in both specimens after hydrogen charging, but specimen WE experienced a more intense deterioration of protective corrosion product film and subsequent cracking. A large part of specimen WD retained its protective corrosion product film after the polarization test, and sites where spalling occurred resulted in pitting with less cracking. Despite weak crystallographic texture noticed in both specimens, WD showed a higher intensity of corrosion-resistant 111|| ND-oriented grains, while WE showed a more random distribution of 111|| ND-, 011|| ND-, and 001|| ND-oriented grains with a lower intensity.
Corrosion and electrochemical behavior of boron/aluminum composites

International Nuclear Information System (INIS)

Pohlman, S.L.

1976-01-01

The results of an investigation to determine the importance of galvanic corrosion as a mechanism for the interfacial attack in boron/aluminium composites are reported. The results indicated that galvanic corrosion occurred between the aluminium matrix and the aluminium boride intermetallic formed during fabrication at the matrix/filament interface. Electric current measurements revealed that the aluminium matrix was preferentially attacked and the interfacial boride was cathodically protected. 18 references
Analysis of helium purification system capability during water ingress accident in RDE

Science.gov (United States)

Sriyono; Kusmastuti, Rahayu; Bakhri, Syaiful; Sunaryo, Geni Rina

2018-02-01

The water ingress accident caused by steam generator tube rupture (SGTR) in RDE (Experimental Power Reactor) must be anticipated. During the accident, steam from secondary system diffused and mixed with helium gas in the primary coolant. To avoid graphite corrosion in the core, steam will be removed by Helium purification system (HPS). There are two trains in HPS, first train for normal operation and the second for the regeneration and accident. The second train is responsible to clean the coolant during accident condition. The second train is equipped with additional component, i.e. water cooler, post accident blower, and water separator to remove this mixture gas. During water ingress, the water release from rupture tube is mixed with helium gas. The water cooler acts as a steam condenser, where the steam will be separated by water separator from the helium gas. This paper analyses capability of HPS during water ingress accident. The goal of the research is to determine the time consumed by HPS to remove the total amount of water ingress. The method used is modelling and simulation of the HPS by using ChemCAD software. The BDBA and DBA scenarios will be simulated. In BDBA scenario, up to 110 kg of water is assumed to infiltrate to primary coolant while DBA is up to 35 kg. By using ChemCAD simulation, the second train will purify steam ingress maximum in 0.5 hours. The HPS of RDE has a capability to anticipate the water ingress accident.
Corrosion performance of several metals in plutonium nitrate solution

International Nuclear Information System (INIS)

Takeda, Seiichiro; Nagai, Takayuki; Yasu, Shozo; Koizumi, Tsutomu

1995-01-01

Corrosion behavior of several metals exposed in plutonium nitrate solution was studied. Plutonium nitrate solution with the plutonium concentration ranging from 0.01 to 300 g/l was used as a corrosive medium. Specimens tested were type 304 ULC (304 ULC) stainless steel, type 310 Nb (310 Nb) stainless steel, titanium (Ti), titanium-5% tantalum alloy (Ti-5Ta), and zirconium (Zr). Corrosion behavior of these metals in plutonium nitrate solution was evaluated through examining electrochemical characteristics and corrosion rates obtained by weight loss measurement. From the results of the corrosion tests, it was found that the corrosion rate of stainless steels i.e. 304 ULC and 310 Nb, increases by the presence of plutonium in nitric acid solution. The corrosion potential of the stainless steels shifted linearly towards the noble direction as the concentration of plutonium increases. It is thought that the shifts in corrosion potential of the stainless steels to the noble direction results an increase in anodic current and, hence, corrosion rate. Valve metals, i.e. Ti, Ti-5Ta and Zr, showed good corrosion resistance over the whole range of plutonium concentration examined here. (author)
Role of expanders in helium liquefaction cycles: Parametric studies using Collins cycle

International Nuclear Information System (INIS)

Thomas, Rijo Jacob; Ghosh, Parthasarathi; Chowdhury, Kanchan

2011-01-01

Large scale helium liquefaction/refrigeration plant is a key subsystem of fusion devices. Performance of these plants is dependent on a number of geometric and operating parameters of its constituting components such as compressors, heat exchangers, expanders, valves, etc. Expander has been chosen as the subject matter of analyses in the present study. As the sensible cold of helium vapor is lost in liquefiers, the expanders in liquefaction cycles have to provide more refrigeration than those in refrigeration cycles. The expander parameters such as rate of mass flow, operating pressure, inlet temperature, etc. are inter-dependent, and hence, it is difficult to predict the system behavior with variation of a particular parameter. This necessitates the use of process simulators. Parametric studies have been performed on Collins helium liquefaction cycle using Aspen HYSYS. Collins cycle has all the basic characteristics of a large-scale helium liquefier and the results of this study may be extrapolated to understand the behavior of large scale helium liquefiers. The study shows that the maximum liquid production is obtained when 80% of the compressor flow is diverted through the expanders and it is equally distributed between the two expanders. The relationships between the liquid production and the isentropic efficiency of expanders are almost linear and both the higher and lower temperature expanders exhibit similar trends.
Role of expanders in helium liquefaction cycles: Parametric studies using Collins cycle

Energy Technology Data Exchange (ETDEWEB)

Thomas, Rijo Jacob, E-mail: rijojthomas@gmail.com [Cryogenic Engineering Centre, Indian Institute of Technology, Kharagpur, West Bengal 721302 (India); Ghosh, Parthasarathi; Chowdhury, Kanchan [Cryogenic Engineering Centre, Indian Institute of Technology, Kharagpur, West Bengal 721302 (India)

2011-06-15

Large scale helium liquefaction/refrigeration plant is a key subsystem of fusion devices. Performance of these plants is dependent on a number of geometric and operating parameters of its constituting components such as compressors, heat exchangers, expanders, valves, etc. Expander has been chosen as the subject matter of analyses in the present study. As the sensible cold of helium vapor is lost in liquefiers, the expanders in liquefaction cycles have to provide more refrigeration than those in refrigeration cycles. The expander parameters such as rate of mass flow, operating pressure, inlet temperature, etc. are inter-dependent, and hence, it is difficult to predict the system behavior with variation of a particular parameter. This necessitates the use of process simulators. Parametric studies have been performed on Collins helium liquefaction cycle using Aspen HYSYS. Collins cycle has all the basic characteristics of a large-scale helium liquefier and the results of this study may be extrapolated to understand the behavior of large scale helium liquefiers. The study shows that the maximum liquid production is obtained when 80% of the compressor flow is diverted through the expanders and it is equally distributed between the two expanders. The relationships between the liquid production and the isentropic efficiency of expanders are almost linear and both the higher and lower temperature expanders exhibit similar trends.
Effects of nitrogen in shielding gas on microstructure evolution and localized corrosion behavior of duplex stainless steel welding joint

Science.gov (United States)

Zhang, Zhiqiang; Jing, Hongyang; Xu, Lianyong; Han, Yongdian; Zhao, Lei; Zhou, Chao

2017-05-01

The effects of nitrogen addition in shielding gas on microstructure evolution and localized corrosion behavior of duplex stainless steel (DSS) welds were studied. N2-supplemented shielding gas facilitated the primary austenite formation, suppressed the Cr2N precipitation in weld root, and increased the microhardnesses of weld metal. Furthermore, N2-supplemented shielding gas increased pitting resistance equivalent number (PREN) of austenite, but which decreased slightly PREN of ferrite. The modified double loop electrochemical potentiokinetic reactivation in 2 M H2SO4 + 1 M HCl was an effective method to study the localized corrosion of the different zones in the DSS welds. The adding 2% N2 to pure Ar shielding gas improved the localized corrosion resistance in the DSS welds, which was due to compensation for nitrogen loss and promoting nitrogen further solution in the austenite phases, suppression of the Cr2N precipitation in the weld root, and increase of primary austenite content with higher PREN than the ferrite and secondary austenite. Secondary austenite are prone to selective corrosion because of lower PREN compared with ferrite and primary austenite. Cr2N precipitation in the pure Ar shielding weld root and heat affected zone caused the pitting corrosion within the ferrite and the intergranular corrosion at the ferrite boundary. In addition, sigma and M23C6 precipitation resulted in the intergranular corrosion at the ferrite boundary.
A nonlinear model for AC induced corrosion

Directory of Open Access Journals (Sweden)

N. Ida

2012-09-01

Full Text Available The modeling of corrosion poses particular difficulties. The understanding of corrosion as an electrochemical process has led to simple capacitive-resistive models that take into account the resistance of the electrolytic cell and the capacitive effect of the surface potential at the interface between conductors and the electrolyte. In some models nonlinear conduction effects have been added to account for more complex observed behavior. While these models are sufficient to describe the behavior in systems with cathodic protection, the behavior in the presence of induced AC currents from power lines and from RF sources cannot be accounted for and are insufficient to describe the effects observed in the field. Field observations have shown that a rectifying effect exists that affects the cathodic protection potential and this effect is responsible for corrosion in the presence of AC currents. The rectifying effects of the metal-corrosion interface are totally missing from current models. This work proposes a nonlinear model based on finite element analysis that takes into account the nonlinear behavior of the metal-oxide interface and promises to improve modeling by including the rectification effects at the interface.
DPC materials and corrosion environments.

Energy Technology Data Exchange (ETDEWEB)

Ilgen, Anastasia Gennadyevna; Bryan, Charles R.; Teich-McGoldrick, Stephanie; Hardin, Ernest

2014-10-01

After an exposition of the materials used in DPCs and the factors controlling material corrosion in disposal environments, a survey is given of the corrosion rates, mechanisms, and products for commonly used stainless steels. Research needs are then identified for predicting stability of DPC materials in disposal environments. Stainless steel corrosion rates may be low enough to sustain DPC basket structural integrity for performance periods of as long as 10,000 years, especially in reducing conditions. Uncertainties include basket component design, disposal environment conditions, and the in-package chemical environment including any localized effects from radiolysis. Prospective disposal overpack materials exist for most disposal environments, including both corrosion allowance and corrosion resistant materials. Whereas the behavior of corrosion allowance materials is understood for a wide range of corrosion environments, demonstrating corrosion resistance could be more technically challenging and require environment-specific testing. A preliminary screening of the existing inventory of DPCs and other types of canisters is described, according to the type of closure, whether they can be readily transported, and what types of materials are used in basket construction.
Helium the disappearing element

CERN Document Server

Sears, Wheeler M

2015-01-01

The subject of the book is helium, the element, and its use in myriad applications including MRI machines, particle accelerators, space telescopes, and of course balloons and blimps. It was at the birth of our Universe, or the Big Bang, where the majority of cosmic helium was created; and stellar helium production continues. Although helium is the second most abundant element in the Universe, it is actually quite rare here on Earth and only exists because of radioactive elements deep within the Earth. This book includes a detailed history of the discovery of helium, of the commercial industry built around it, how the helium we actually encounter is produced within the Earth, and the state of the helium industry today. The gas that most people associate with birthday party balloons is running out. “Who cares?” you might ask. Well, without helium, MRI machines could not function, rockets could not go into space, particle accelerators such as those used by CERN could not operate, fiber optic cables would not...
Behavior of copper corrosion products in water loops of heat-exchange units

International Nuclear Information System (INIS)

Zarembo, V.I.; Kritskii, V.G.; Slobodov, A.A.; Puchkov, L.V.

1989-01-01

This communication is dedicated to an examination of copper corrosion products (CP) in the conditions of real aqueous-chemical regime (ACR) parameters. The deposition of these CP in steam-generating zones (up to 85% of their total amount) stimulate local types of corrosion. The solubility in Cu CP (Cu 2 O, CuO, Cu(OH) 2 )-water (H 2 O)-gas (H 2 , O 2 )-conditioning additives (HCl, KOH) systems was determined by computer modeling according to the minimum Gibbs energy criterion on the basis of selected and matched thermodynamic constants for various chemical forms of copper under standard conditions. As a result of the authors' calculations they obtained the solubilities in water of CuO, Cu 2 O and Cu(OH) 2 when changing the dosage of active gases from 0 to 10 -2 mole/kg of water, of acid or equal to that of saturated vapor of pure water. Thus, they were able to monitor the behavior of copper CP in conditions modeling those of real ACR in operating heat exchange units, including in conditions deviating from the standard
Hydrogen permeation and corrosion behavior of high strength steel MCM 430 in cyclic wet-dry SO2 environment

International Nuclear Information System (INIS)

Nishimura, Rokuro; Shiraishi, Daisuke; Maeda, Yasuaki

2004-01-01

Hydrogen permeation caused by corrosion under a cyclic wet (2 h)-dry (10 h) SO 2 condition was investigated for a high strength steel of MCM 430 by using an electrochemical technique in addition to the corrosion behavior obtained from weight loss measurement and the determination of corrosion products by using X-ray diffraction method. The hydrogen content converted from hydrogen permeation current density was observed in both wet and dry periods. The origin of proton was estimated to be from (1) the hydrolysis of ferrous ions, (2) the oxidation of ferrous ions and ferrous hydroxide, and (3) hydrolysis of SO 2 and formation of FeSO 4 , but not from the dissociation of H 2 O. With respect to the determination of the corrosion products consisting of inner (adherent) and outer (not adherent) layers, the outer layer is composed of α-FeOOH, amorphous phase and γ-FeOOH, where α-FeOOH increases with the increase in the wet-dry cycle, and amorphous phase shows the reverse trend. The corrosion product in the inner layer is mainly Fe 3 O 4 with them. On the basis of the results obtained, the role of the dry or wet period, the effect of SO 2 and the corrosion process during the cyclic wet-dry periods were discussed
Corrosion behavior of spent MTR fuel elements in a drowned salt mine repository

International Nuclear Information System (INIS)

Brodda, B.G.; Fachinger, J.

1995-01-01

Spent MTR fuel from German Material Test Reactors will not be reprocessed, but stored in a final salt repository in the deep geologic underground. Fuel elements will be placed in POLLUX containers, which are assumed to resist the corrosive attack of an accidentally formed concentrated salt brine for about 500 years. After a container failure the brine would contact the fuel element, corrode the aluminum plating and possibly leach radionuclides from the fuel. A source term for the calculation of radionuclide mobilization results from the investigation of the behavior of MTR fuel in this scenario, which has to be considered for the long-term safety analysis of a deep mined rock salt repository. Experiments with the different plating materials show that the considered aluminum alloys will not resist the corrosive attack of a brine solution, especially in the presence of iron, under the conditions in a drowned salt mine repository. Although differences in the corrosion rates of about two orders of magnitude were observed when applying different parameter sets, the deterioration must be considered to be almost instantaneous in geological terms. Radionuclides are mobilized from irradiated MTR fuel, when the meat of the fuel element becomes accessible to the brine solution. It seems, however, that the radionuclides are effectively trapped by the aluminum hydroxide formed, as the activity concentrations in the brine solution soon reach a constant level with the progressing corrosion of the cladding aluminum. In the presence of iron a more significant initial release was observed, but also in this case an equilibrium activity seems to be reached as a consequence of radionuclide trapping
Pitting Corrosion Behavior of 304 SS and 316 SS Alloys in Aqueous Chloride and Bromide Solutions

Directory of Open Access Journals (Sweden)

Ibtehal Kareem Shakir

2018-01-01

Full Text Available The importance of the present work falls on the pitting corrosion behavior investigation of 304 SS and 316 SS alloys in 3.5 wt% of aqueous solution bearing with chloride and bromide anion at different solutions temperature range starting from (20-50oC due to the pitting corrosion tremendous effect on the economic, safety and materials loss due to leakage. The impact of solution temperatures on the pitting corrosion resistance at 3.5wt% (NaCl and NaBr solutions for the 304 SS and 316 SS has been investigated utilizing the cyclic polarization techniques at the potential range -400 to1000 mV vs. SCE at 40 mV/sec scan rate followed by the surface characterization employing Scanning Electron Microscope. The results show that a significant decline in the pitting corrosion potential Ep values of both stainless steel alloys in chloride and bromide solution during temperature increase attributed to the pitting corrosion potential decreased arises from the modification of the passive film properties. The surface examination using optical microscope and scanning electron microscope prove the occurring of higher pitting density over 304 SS in chloride solution than that observed in bromide solution with a non-circular lacy cover pitfall out at the center and falls inside the pits hall in comparison to the isolated circular lacy cover pit formed on 316 SS in 3.5wt% NaBr solution at 50 oC.
Corrosion behavior of beryllium copper and other nonmagnetic alloys in simulated drilling environments

International Nuclear Information System (INIS)

Cribb, W.R.; Booker, J.; Kane, R.D.; Turn, J.C.

1984-01-01

Beryllium copper (BeCu) alloys are known to exhibit high strength and good electrical conductivity. Other attractive properties, low magnetic susceptibility and resistance to galling, make these alloys strong contenders for use as drill collars and instrument housings in drilling equipment. Environmental cracking and corrosion tests were conducted in autoclaves at 66, 121 and 149 C (150, 250 and 300 F) in environments as severe as 10% H 2 S, 20% CO 2 balance N 2 . The results indicate Brush Alloy 25 adequately resists environmental cracking for these conditions, whereas certain nonmagnetic stainless steel cracked. Brush Alloy 25 exhibits acceptable corrosion rates at or below temperatures of 149 C (300 F) in environments with up to 1% H 2 S. Acceptable rates were also observed for environments containing up to 10% H 2 S at 66 C (150 F). The alloy showed this similar acceptable behavior in billet or tube form regardless of the aging treatment
Corrosion behavior of Ti-13Nb-13Zr alloy used as a biomaterial

International Nuclear Information System (INIS)

Niemeyer, T.C.; Grandini, C.R.; Pinto, L.M.C.; Angelo, A.C.D.; Schneider, S.G.

2009-01-01

Titanium alloys were developed as an alternative to stainless steels and have been extensively used as biomaterials ever since. One of these alloys is Ti-13Nb-13Zr (TNZ), a near-beta phase alloy containing elements with excellent biocompatibility. The main advantage of the TNZ alloy, compared to other titanium alloys, such as Ti-6Al-4V and Ti-6Al-7Nb, widely used as biomaterials, is its low elasticity modulus, closer to that of bone, and the absence of aluminum and vanadium, which have been reported to cause long-term adverse effects. In this paper, the corrosion and electrochemical behavior of TNZ alloy (as cast and after oxygen charge) was studied in a PBS solution. The results showed that, with the oxygen load, there is a significant reduction of the anodic current in almost the whole potential spam explored in this work, meaning that the corrosion rate decreases when the doping is performed.

Liquid helium target

International Nuclear Information System (INIS)

Fujii, Y.; Kitami, T.; Torikoshi, M.

1984-12-01

A liquid helium target system has been built and used for the experiment on the reaction 4 He(γ, p). The target system has worked satisfactorily; the consumption rate of liquid helium is 360 ml/h and the cryogenic system retains liquid helium for about ten hours. The structure, operation and performance of the target system are reported. (author)
Corrosion behavior of pyroclore-rich titanate ceramics for plutonium disposition; impurity effects

International Nuclear Information System (INIS)

Bakel, A. J.

1999-01-01

The baseline ceramic contains Ti, U, Ca, Hf, Gd, and Ce, and is made up of only four phases, pyrochlore, zirconolite, rutile, and brannerite. The impurities present in the three other ceramics represent impurities expected in the feed, and result in different phase distributions. The results from 3 day, 90 C MCC-1 tests with impurity ceramics were significantly different than the results from tests with the baseline ceramic. Overall, the addition of impurities to these titanate ceramics alters the phase distributions, which in turn, affects the corrosion behavior
Effects of lipopolysaccharides on the corrosion behavior of Ni-Cr and Co-Cr alloys.

Science.gov (United States)

Yu, Weiqiang; Qian, Chao; Weng, Weimin; Zhang, Songmei

2016-08-01

Lipopolysaccharides (LPS) are constituents of gingival crevicular fluid and may affect the base metal alloys used in metal ceramic crowns. The role of LPS in base metal alloys is currently unknown. The purpose of this in vitro study was to evaluate the effects of gram-negative bacterial LPS on the electrochemical behavior of Ni-Cr and Co-Cr alloys. Alloy specimens were divided into 4 groups according to Escherichia coli LPS concentration (0, 0.15, 15, and 150 μg/mL) in acidic saliva (pH 5). Open circuit potential (OCP) and potentiodynamic polarization behavior were examined using a computer-controlled potentiostat. Metal ions released from the 2 alloys were measured by immersion in LPS-free solution and 150 μg/mL LPS solution and analyzed by inductively coupled plasma atomic emission spectrometry (ICP-AES). Data were evaluated using 1-way ANOVA (α=.05). Compared with control groups, medium LPS concentration (15 μg/mL) accelerated Ni-Cr alloy corrosion (Palloy corrosion (Pcorrosion current density, and polarization resistance parameters. After immersion in high LPS concentrations (150 μg/mL), a slight increase in Ni ion release (P >.05) was observed for the Ni-Cr alloy, while a more significant Co ion release (Palloy. LPS negatively affected the electrochemical behavior of both the Ni-Cr and Co-Cr alloys. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.
The effect of β-FeOOH on the corrosion behavior of low carbon steel exposed in tropic marine environment

International Nuclear Information System (INIS)

Ma Yuantai; Li Ying; Wang Fuhui

2008-01-01

The atmospheric corrosion performance of carbon steel exposed in Wanning area, which located in the south part of China with tropic marine environment characters, was studied at different exposure periods (up to 2 years). To investigate the effect of β-FeOOH on the corrosion behavior of carbon steel in high chloride ion environment, rust layer was analyzed by using infrared spectroscopy, scanning electron microscope, X-ray diffraction, and the rusted steel was measured by electrochemical impedance spectroscopy method. The weight loss test indicated that the corrosion rate of carbon steel sharply increased during 6 months' exposure and gradually reduced after longer exposure. The results of rust analysis revealed that the underlying corrosion performance of the carbon steel was dependent on the inherent properties of the rust layers formed under different conditions such as composition and structure. Among all the iron oxide, β-FeOOH exerted significant influence. The presence of a monolayer of the rust as well as β-FeOOH accelerated the corrosion process during the initial exposure stage. EIS data implied that β-FeOOH in the inner layer was gradually consumed and transformed to γ-Fe 2 O 3 in the wet-dry cycle, which was beneficial to protect the substrate and reduced the corrosion rate
Thermodynamics of inclusion formation and its influence on the corrosion behavior of Cu bearing duplex stainless steels

International Nuclear Information System (INIS)

Jeon, Soon-Hyeok; Kim, Soon-Tae; Lee, In-Sung; Park, Yong-Soo; Park, Joo-Hyun; Kim, Kwang-Tae; Kim, Ji-Soo

2011-01-01

To elucidate the thermodynamics of inclusion formation and its influence on the corrosion behavior of Cu bearing duplex stainless steels, potentiodynamic and potentiostatic polarization tests, a SEM-EDS analysis of inclusions, and thermodynamic calculations of the formation of inclusions were carried out. While the resistance to general corrosion of the noble copper contained alloy-1.5Cu in a deaerated 2 M H 2 SO 4 was higher than that of the alloy-BASE, the resistance to pitting corrosion of copper contained alloy-1.5Cu in a deaerated 0.5 N HCl + 1 N NaCl and 30 mass% NaCl was lower than that of the alloy-BASE due to an increase of interface areas between inclusions and matrix acting as preferential pit initiation sites. The thermodynamic calculation for the formation of Cr-containing oxide inclusions was in good agreement with the experimental results. (author)
Damage behavior in helium-irradiated reduced-activation martensitic steels at elevated temperatures

Energy Technology Data Exchange (ETDEWEB)

Luo, Fengfeng [Key Laboratory of Artificial Micro- and Nano-Structures of Ministry of Education, Hubei Nuclear Solid Physics Key Laboratory and School of Physics and Technology, Wuhan University, Wuhan 430072 (China); Guo, Liping, E-mail: guolp@whu.edu.cn [Key Laboratory of Artificial Micro- and Nano-Structures of Ministry of Education, Hubei Nuclear Solid Physics Key Laboratory and School of Physics and Technology, Wuhan University, Wuhan 430072 (China); Chen, Jihong; Li, Tiecheng; Zheng, Zhongcheng [Key Laboratory of Artificial Micro- and Nano-Structures of Ministry of Education, Hubei Nuclear Solid Physics Key Laboratory and School of Physics and Technology, Wuhan University, Wuhan 430072 (China); Yao, Z. [Department of Mechanical and Materials Engineering, Queen’s University, Kingston K7L 3N6, ON (Canada); Suo, Jinping [State Key Laboratory of Mould Technology, Institute of Materials Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074 (China)

2014-12-15

Dislocation loops induced by helium irradiation at elevated temperatures in reduced-activation martensitic steels were investigated using transmission electron microscopy. Steels were irradiated with 100 keV helium ions to 0.8 dpa between 300 K and 723 K. At irradiation temperatures T{sub irr} ⩽ 573 K, small defects with both Burger vectors b = 1/2〈1 1 1〉 and b = 〈1 0 0〉 were observed, while at T{sub irr} ⩾ 623 K, the microstructure was dominated by large convoluted interstitial dislocation loops with b = 〈1 0 0〉. Only small cavities were found in the steels irradiated at 723 K.
Electrochemical Corrosion Behavior of Oxidation Layer on Fe30Mn5Al Alloy

Directory of Open Access Journals (Sweden)

ZHU Xue-mei

2017-08-01

Full Text Available The Fe30Mn5Al alloy was oxidized at 800℃ in air for 160h, the oxidation-induced layer about 15μm thick near the scale-metal interface was induced to transform to ferrite and become enriched in Fe and depletion in Mn. The effect of the oxidation-induced Mn depletion layer on the electrochemical corrosion behavior of Fe30Mn5Al alloy was evaluated. The results show that in 1mol·L-1 Na2SO4 solution, the anodic polarization curve of the Mn depletion layer exhibits self-passivation, compared with Fe30Mn5Al austenitic alloy, and the corrosion potential Evs SCE is increased to -130mV from -750mV and the passive current density ip is decreased to 29μA/cm2 from 310μA/cm2. The electrochemical impedance spectroscopy(EIS of the Mn depletion layer has the larger diameter of capacitive arc, the higher impedance modulus|Z|, and the wider phase degree range, and the fitted polarization resistant Rt is increased to 9.9kΩ·cm2 from 2.7kΩ·cm2 by using an equivalent electric circuit of Rs-(Rt//CPE. The high insulation of the Mn depletion layer leads to an improved corrosion resistance of Fe30Mn5Al austenitic alloy.
Dynamic Recrystallization Behavior and Corrosion Resistance of a Dual-Phase Mg-Li Alloy

Directory of Open Access Journals (Sweden)

Gang Liu

2018-03-01

Full Text Available The hot deformation and dynamic recrystallization behavior of the dual-phase Mg-9Li-3Al-2Sr-2Y alloy had been investigated using a compression test. The typical dual-phase structure was observed, and average of grain size of as-homogenized alloy is about 110 µm. It mainly contains β-Li, α-Mg, Al4Sr and Al2Y phases. The dynamic recrystallization (DRX kinetic was established based on an Avrami type equation. The onset of the DRX process occurred before the peak of the stress–strain flow curves. It shows that the DRX volume fraction increases with increasing deformation temperature or decreasing strain rate. The microstructure evolution during the hot compression at various temperatures and strain rates had been investigated. The DRX grain size became larger with the increasing testing temperature or decreasing strain rate because the higher temperature or lower strain rate can improve the migration of DRX grain boundaries. The fully recrystallized microstructure can be achieved in a small strain due to the dispersed island-shape α-Mg phases, continuous the Al4Sr phases and spheroidal Al2Y particles, which can accelerate the nucleation. The continuous Al4Sr phases along the grain boundaries are very helpful for enhancing the corrosion resistance of the duplex structured Mg-Li alloy, which can prevent the pitting corrosion and filiform corrosion.
Dynamic Recrystallization Behavior and Corrosion Resistance of a Dual-Phase Mg-Li Alloy.

Science.gov (United States)

Liu, Gang; Xie, Wen; Wei, Guobing; Yang, Yan; Liu, Junwei; Xu, Tiancai; Xie, Weidong; Peng, Xiaodong

2018-03-09

The hot deformation and dynamic recrystallization behavior of the dual-phase Mg-9Li-3Al-2Sr-2Y alloy had been investigated using a compression test. The typical dual-phase structure was observed, and average of grain size of as-homogenized alloy is about 110 µm. It mainly contains β-Li, α-Mg, Al₄Sr and Al₂Y phases. The dynamic recrystallization (DRX) kinetic was established based on an Avrami type equation. The onset of the DRX process occurred before the peak of the stress-strain flow curves. It shows that the DRX volume fraction increases with increasing deformation temperature or decreasing strain rate. The microstructure evolution during the hot compression at various temperatures and strain rates had been investigated. The DRX grain size became larger with the increasing testing temperature or decreasing strain rate because the higher temperature or lower strain rate can improve the migration of DRX grain boundaries. The fully recrystallized microstructure can be achieved in a small strain due to the dispersed island-shape α-Mg phases, continuous the Al₄Sr phases and spheroidal Al₂Y particles, which can accelerate the nucleation. The continuous Al₄Sr phases along the grain boundaries are very helpful for enhancing the corrosion resistance of the duplex structured Mg-Li alloy, which can prevent the pitting corrosion and filiform corrosion.
The Corrosion Behavior of Cold-Rolled 304 Stainless Steel In Salt Spray Environments

International Nuclear Information System (INIS)

Chiang, M.F.; Young, M.C.; Huang, J.Y.

2011-01-01

Saline corrosion is one of the major degradation mechanisms for stainless steel type 304 (SS304) dry storage cask during the spent fuel interim storage period. Slow strain rate test (SSRT) and neutral salt spray test (NSS) were performed at 85 degrees Celsius and 200 degrees Celsius with 0.5 wt% sodium chloride mist sprayed on the cold-rolled SS304 specimens of different degrees of reduction in this study. The weight changes of the NSS specimens tested at 85 degrees Celsius for 2000 hours differed greatly from those at 200 degrees Celsius. The weight loss of NSS specimens was not significant at 85 degrees Celsius but the weight gain decreased gradually with increasing the cold-rolled reduction. The yield strength (YS) and ultimate tensile stress (UTS) values obtained from the SSRT tests for lightly cold-rolled specimens in the salt spray environment at 85 degrees Celsius and 200 degrees Celsius are slightly lower than in air. But for those with 20% reductions, the specimen strengths were no longer changed by the saline corrosion. The preliminary results demonstrated that the quality and performance of cold-rolled SS304 is acceptable for fabrication of dry storage casks. However, more work on the corrosion behavior of cold-rolled stainless steel in the saline atmosphere is needed to better understand its long-term performance.
A liquid helium saver

International Nuclear Information System (INIS)

Avenel, O.; Der Nigohossian, G.; Roubeau, P.

1976-01-01

A cryostat equipped with a 'liquid helium saver' is described. A mass flow rate M of helium gas at high pressure is injected in a counter-flow heat exchanger extending from room to liquid helium temperature. After isenthalpic expansion through a calibrated flow impedance this helium gas returns via the low pressure side of the heat exchanger. The helium boil-off of the cryostat represents a mass flow rate m, which provides additional precooling of the incoming helium gas. Two operating regimes appear possible giving nearly the same efficiency: (1) high pressure (20 to 25 atm) and minimum flow (M . L/W approximately = 1.5) which would be used in an open circuit with helium taken from a high pressure cylinder; and (2) low pressure (approximately = 3 atm), high flow (M . L/W > 10) which would be used in a closed circuit with a rubber diaphragm pumping-compressing unit; both provide a minimum theoretical boil-off factor of about 8%. Experimental results are reported. (U.K.)
The effect of quench rate on the microstructure, mechanical properties, and corrosion behavior of U-6 Wt Pct Nb

International Nuclear Information System (INIS)

Eckelmeyer, K.H.; Romiy, A.D.; Weirick, L.J.

1984-01-01

The effect of cooling rate on microstructure, mechanical behavior, corrosion resistance, and subsequent age hardenability is discussed. Cooling rates in excess of 20 Ks -1 cause the parent γ-phase to transform martensitically to a niobium supersaturated variant of the α-phase. This phase exhibits low hardness and strength, high ductility, good corrosion resistance, and age hardenability. As cooling rate decreases from 10 Ks -1 to 0.2 Ks -1 , microstructural changes (consistent with spinodal decomposition) occur to an increasing extent. These changes produce increases in hardness and strength and decreases in ductility, corrosion resistance, and age hardenability. At cooling rates less than 0.2 Ks -1 the parent phase undergoes cellular decomposition to a coarse two-phase lamellar microstructure which exhibits intermediate strength and ductility, reduced corrosion resistance, and no age hardenability. An analysis of the cooling rates indicates that fully martensitic microstructures can be obtained in plates as thick as 50 mm
Modeling of helium bubble nucleation and growth in neutron irradiated boron doped RAFM steels

International Nuclear Information System (INIS)

Dethloff, Christian; Gaganidze, Ermile; Svetukhin, Vyacheslav V.; Aktaa, Jarir

2012-01-01

Reduced activation ferritic/martensitic (RAFM) steels are promising candidates for structural materials in future fusion technology. In addition to other irradiation defects, the transmuted helium is believed to strongly influence material hardening and embrittlement behavior. A phenomenological model based on kinetic rate equations is developed to describe homogeneous nucleation and growth of helium bubbles in neutron irradiated RAFM steels. The model is adapted to different 10 B doped EUROFER97 based heats, which already had been studied in past irradiation experiments. Simulations yield bubble size distributions, whereby effects of helium generation rate, surface energy, helium sinks and helium density are investigated. Peak bubble diameters under different conditions are compared to preliminary microstructural results on irradiated specimens. Helium induced hardening was calculated by applying the Dispersed Barrier Hardening model to simulated cluster size distributions. Quantitative microstructural investigations of unirradiated and irradiated specimens will be used to support and verify the model.
Modeling of helium bubble nucleation and growth in neutron irradiated boron doped RAFM steels

Energy Technology Data Exchange (ETDEWEB)

Dethloff, Christian, E-mail: christian.dethloff@kit.edu [Karlsruhe Institute of Technology (KIT), Institute for Applied Materials, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Gaganidze, Ermile [Karlsruhe Institute of Technology (KIT), Institute for Applied Materials, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Svetukhin, Vyacheslav V. [Ulyanovsk State University, Leo Tolstoy Str. 42, 432970 Ulyanovsk (Russian Federation); Aktaa, Jarir [Karlsruhe Institute of Technology (KIT), Institute for Applied Materials, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany)

2012-07-15

Reduced activation ferritic/martensitic (RAFM) steels are promising candidates for structural materials in future fusion technology. In addition to other irradiation defects, the transmuted helium is believed to strongly influence material hardening and embrittlement behavior. A phenomenological model based on kinetic rate equations is developed to describe homogeneous nucleation and growth of helium bubbles in neutron irradiated RAFM steels. The model is adapted to different {sup 10}B doped EUROFER97 based heats, which already had been studied in past irradiation experiments. Simulations yield bubble size distributions, whereby effects of helium generation rate, surface energy, helium sinks and helium density are investigated. Peak bubble diameters under different conditions are compared to preliminary microstructural results on irradiated specimens. Helium induced hardening was calculated by applying the Dispersed Barrier Hardening model to simulated cluster size distributions. Quantitative microstructural investigations of unirradiated and irradiated specimens will be used to support and verify the model.
Corrosion behavior of Fe3Al intermetallics with addition of lithium, cerium and nickel in 2.5 % SO2+N2 at 900 degree centigrade

International Nuclear Information System (INIS)

Luna-Ramirez, A.; Porcayo-Calderon, J.; Martinez-Villafane, A.; Gonzalez-Rodriguez, J. G.; Chaon-Nava, J. G.

2012-01-01

The corrosion behavior of Fe 3 Al-type intermetallic alloys with addition of 1 at. % cerium, lithium and nickel at high temperature has been studied. The various alloys were exposed to an environment composed of 2.5 % SO 2 +N 2 at 900 degree centigrade for 48 h. For all the intermetallic tested, the corrosion kinetics showed a parabolic behavior. The alloy, which showed less corrosion rate, was the Fe3AlNi alloy, being Fe 3 AlCeLi the alloy with the highest corrosion rate. For the various alloys, energy dispersive X-ray spectroscopy analysis, EDS, on the developed scale only detected aluminum, oxygen, and traces of iron and cerium, suggesting the formation of alumina as main component. The intermetallic alloys showed oxide cracking and spalling. The intermetallic chemical composition played an important role in defining the oxide scale morphology and the extent of damage. (Author) 39 refs.
Corrosion behavior of metals and alloys in marine-industrial environment

Directory of Open Access Journals (Sweden)

Mariappan Natesan, Subbiah Selvaraj, Tharmakkannu Manickam and Gopalachari Venkatachari

2008-01-01

Full Text Available This work deals with atmospheric corrosion to assess the degrading effects of air pollutants on ferrous and non-ferrous metals and alloys, which are mostly used as engineering materials. An exposure study was conducted in the Tuticorin port area located on the east coast of South India, in the Gulf of Mannar with Sri Lanka to the southeast. Common engineering materials, namely mild steel, galvanized iron, Zn, Al, Cu and Cu–Zn alloys (Cu–27Zn, Cu–30Zn and Cu–37Zn, were used in the investigation. The site was chosen where the metals are exposed to marine and industrial atmospheres. Seasonal 1 to 12 month corrosion losses of these metals and alloys were determined by a weight loss method. The weight losses showed strong corrosion of mild steel, galvanized iron, Cu and Zn and minor effect on Al and Cu–Zn alloys. Linear regression analysis was conducted to study the mechanism of corrosion. The composition of corrosion products formed on the metal surfaces was identified by x-ray diffraction and Fourier transform infrared spectroscopy.
Natural analogues of nuclear waste glass corrosion

International Nuclear Information System (INIS)

Abrajano, T.A. Jr.; Ebert, W.L.; Luo, J.S.

1999-01-01

This report reviews and summarizes studies performed to characterize the products and processes involved in the corrosion of natural glasses. Studies are also reviewed and evaluated on how well the corrosion of natural glasses in natural environments serves as an analogue for the corrosion of high-level radioactive waste glasses in an engineered geologic disposal system. A wide range of natural and experimental corrosion studies has been performed on three major groups of natural glasses: tektite, obsidian, and basalt. Studies of the corrosion of natural glass attempt to characterize both the nature of alteration products and the reaction kinetics. Information available on natural glass was then compared to corresponding information on the corrosion of nuclear waste glasses, specifically to resolve two key questions: (1) whether one or more natural glasses behave similarly to nuclear waste glasses in laboratory tests, and (2) how these similarities can be used to support projections of the long-term corrosion of nuclear waste glasses. The corrosion behavior of basaltic glasses was most similar to that of nuclear waste glasses, but the corrosion of tektite and obsidian glasses involves certain processes that also occur during the corrosion of nuclear waste glasses. The reactions and processes that control basalt glass dissolution are similar to those that are important in nuclear waste glass dissolution. The key reaction of the overall corrosion mechanism is network hydrolysis, which eventually breaks down the glass network structure that remains after the initial ion-exchange and diffusion processes. This review also highlights some unresolved issues related to the application of an analogue approach to predicting long-term behavior of nuclear waste glass corrosion, such as discrepancies between experimental and field-based estimates of kinetic parameters for basaltic glasses
Natural analogues of nuclear waste glass corrosion.

Energy Technology Data Exchange (ETDEWEB)

Abrajano, T.A. Jr.; Ebert, W.L.; Luo, J.S.

1999-01-06

This report reviews and summarizes studies performed to characterize the products and processes involved in the corrosion of natural glasses. Studies are also reviewed and evaluated on how well the corrosion of natural glasses in natural environments serves as an analogue for the corrosion of high-level radioactive waste glasses in an engineered geologic disposal system. A wide range of natural and experimental corrosion studies has been performed on three major groups of natural glasses: tektite, obsidian, and basalt. Studies of the corrosion of natural glass attempt to characterize both the nature of alteration products and the reaction kinetics. Information available on natural glass was then compared to corresponding information on the corrosion of nuclear waste glasses, specifically to resolve two key questions: (1) whether one or more natural glasses behave similarly to nuclear waste glasses in laboratory tests, and (2) how these similarities can be used to support projections of the long-term corrosion of nuclear waste glasses. The corrosion behavior of basaltic glasses was most similar to that of nuclear waste glasses, but the corrosion of tektite and obsidian glasses involves certain processes that also occur during the corrosion of nuclear waste glasses. The reactions and processes that control basalt glass dissolution are similar to those that are important in nuclear waste glass dissolution. The key reaction of the overall corrosion mechanism is network hydrolysis, which eventually breaks down the glass network structure that remains after the initial ion-exchange and diffusion processes. This review also highlights some unresolved issues related to the application of an analogue approach to predicting long-term behavior of nuclear waste glass corrosion, such as discrepancies between experimental and field-based estimates of kinetic parameters for basaltic glasses.
Canada's helium output rising fast

Energy Technology Data Exchange (ETDEWEB)

1966-12-01

About 12 months from now, International Helium Limited will be almost ready to start up Canada's second helium extraction plant at Mankota, in Saskatchewan's Wood Mountain area about 100 miles southwest of Moose Jaw. Another 80 miles north is Saskatchewan's (and Canada's) first helium plant, operated by Canadian Helium and sitting on a gas deposit at Wilhelm, 9 miles north of Swift Current. It contains almost 2% helium, some COD2U, and the rest nitrogen. One year in production was apparently enough to convince Canadian Helium that the export market (it sells most of its helium in W. Europe) can take a lot more than it's getting. Construction began this summer on an addition to the Swift Current plant that will raise its capacity from 12 to 36MMcf per yr when it goes on stream next spring. Six months later, International Helium's 40 MMcf per yr plant to be located about 4 miles from its 2 Wood Mountain wells will double Canada's helium output again.
Corrosion behavior of dissimilar weld joint of 316L and alloy 182 filler metal with different post-weld heat treatments in saline environments

Energy Technology Data Exchange (ETDEWEB)

Garcia, Joao H.N.; Santos, Neice F.; Esteves, Luiza; Campos, Wagner R.C.; Rabello, Emerson G., E-mail: joao.garcia@cdtn.br, E-mail: nfs@cdtn.br, E-mail: luiza.esteves@cdtn.br, E-mail: wrcc@cdtn.br, E-mail: egr@cdtn.br [Centro de Desenvolvimento da Tecnologia Nuclear (SEIES/CDTN/CNEN-MG), Belo Horizonte, MG (Brazil). Serviço de Integridade Estrutural

2017-11-01

Austenitic stainless steel and nickel alloys are widely used in nuclear reactors components and other plants of energy generation, chemical and petrochemical industries, due to their high corrosion resistance. These metals require post weld heat treatment (PWHT) to relieve stresses from the welding processes, although it can lead to a degradation of the weld microstructure. The aim of this work was to evaluate the influence of different PWHT on corrosion behavior of a dissimilar weld joint of two AISI 316L austenitic stainless steel plates with nickel alloy as filler material in saline environments. The material was submitted to heat treatments for three hours at 600, 700 and 800 °C. The weld joint was examined by optical microscopy to determine the effects of PWHT in the microstructure. The corrosion behavior of the samples before and after heat treatment was evaluated using cyclic potentiodynamic polarization (CPP) in sodium chloride solutions (19% v/v) and pH 4.0 at room temperature. Metallographic analyses showed that delta ferrite dissolute with PWHT temperature increase. CPP curves demonstrated an increase of pitting corrosion resistance as the PWHT temperature increases, although the pit size has been increased. The heat treated weld joint at 600 °C showed corrosion resistance close to the as welded material. (author)

Diffusion of helium and nucleation-growth of helium-bubbles in metallic materials

International Nuclear Information System (INIS)

Zhang Chonghong; Chen Keqin; Wang Yinshu

2001-01-01

Studies of diffusion and aggregation behaviour of helium in metallic materials are very important to solve the problem of helium embrittlement in structural materials used in the environment of nuclear power. Experimental studies on helium diffusion and aggregation in austenitic stainless steels in a wide temperature range have been performed in authors' research group and the main results obtained are briefly summarized. The mechanism of nucleation-growth of helium-bubbles has been discussed and some problems to be solved are also given
Carburization of austenitic alloys by gaseous impurities in helium

International Nuclear Information System (INIS)

Lai, G.Y.; Johnson, W.R.

1980-03-01

The carburization behavior of Alloy 800H, Inconel Alloy 617 and Hastelloy Alloy X in helium containing various amounts of H 2 , CO, CH 4 , H 2 O and CO 2 was studied. Corrosion tests were conducted in a temperature range from 649 to 1000 0 C (1200 to 1832 0 F) for exposure time up to 10,000 h. Four different helium environments, identified as A, B, C, and D, were investigated. Concentrations of gaseous impurities were 1500 μatm H 2 , 450 μatm CO, 50 μatm CH 4 and 50 μatm H 2 O for Environment A; 200 μatm H 2 , 100 μatm CO, 20 μatm CH 4 , 50 μatm H 2 O and 5 μatm CO 2 for Environment B; 500 μatm H 2 , 50 μatm CO, 50 μatm CH 4 and 2 O for Environment C; and 500 μatm H 2 , 50 μatm CO, 50 μatm CH 4 and 1.5 μatm H 2 O for Environment D. Environments A and B were characteristic of high-oxygen potential, while C and D were characteristic of low-oxygen potential. The results showed that the carburization kinetics in low-oxygen potential environments (C and D) were significantly higher, approximately an order of magnitude higher at high temperatures, than those in high-oxygen potential environments (A and B) for all three alloys. Thermodynamic analyses indicated no significant differences in the thermodynamic carburization potential between low- and high-oxygen potential environments. It is thus believed that the enhanced carburization kinetics observed in the low-oxygen potential environments were related to kinetic effects. A qualitatively mechanistic model was proposed to explain the enhanced kinetics. The present results further suggest that controlling the oxygen potential of the service environment can be an effective means of reducing carburization of alloys
Coupling a Supercritical Carbon Dioxide Brayton Cycle to a Helium-Cooled Reactor.

Energy Technology Data Exchange (ETDEWEB)

Middleton, Bobby [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Pasch, James Jay [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Kruizenga, Alan Michael [Sandia National Lab. (SNL-CA), Livermore, CA (United States); Walker, Matthew [Sandia National Lab. (SNL-CA), Livermore, CA (United States)

2016-01-01

This report outlines the thermodynamics of a supercritical carbon dioxide (sCO₂) recompression closed Brayton cycle (RCBC) coupled to a Helium-cooled nuclear reactor. The baseline reactor design for the study is the AREVA High Temperature Gas-Cooled Reactor (HTGR). Using the AREVA HTGR nominal operating parameters, an initial thermodynamic study was performed using Sandia's deterministic RCBC analysis program. Utilizing the output of the RCBC thermodynamic analysis, preliminary values of reactor power and of Helium flow rate through the reactor were calculated in Sandia's HelCO₂ code. Some research regarding materials requirements was then conducted to determine aspects of corrosion related to both Helium and to sCO₂ , as well as some mechanical considerations for pressures and temperatures that will be seen by the piping and other components. This analysis resulted in a list of materials-related research items that need to be conducted in the future. A short assessment of dry heat rejection advantages of sCO₂> Brayton cycles was also included. This assessment lists some items that should be investigated in the future to better understand how sCO₂ Brayton cycles and nuclear can maximally contribute to optimizing the water efficiency of carbon free power generation
Corrosion of carbon steel in neutral water

International Nuclear Information System (INIS)

Kawai, Noboru; Iwahori, Toru; Kurosawa, Tatsuo

1983-01-01

The initial corrosion behavior of materials used in the construction of heat exchanger and piping system of BWR nuclear power plants and thermal power plants have been examined in neutral water at 30, 50, 100, 160, 200, and 285 deg C with two concentrations of dissolved oxygen in the water. In air-saturated water, the corrosion rate of carbon steel was so higher than those in deaerated conditions and the maximum corrosion rate was observed at 200 deg C. The corrosion rate in deaerated water gradually increased with increasing the water temperature. Low alloy steel (2.25 Cr, 1Mo) exhibited good corrosion resistance compared with the corrosion of carbon steel under similar testing conditions. Oxide films grown on carbon steel in deaerated water at 50, 100, 160, 200, and 285 deg C for 48 and 240 hrs were attacked by dissolved oxygen in room temperature water respectively. However the oxide films formed higher than about 160 deg C showed more protective. The electrochemical behavior of carbon steel with oxide films was also similar to the effect of temperature on the stability of oxide films. (author)
Mechanical Behavior of Stainless Steel Fiber-Reinforced Composites Exposed to Accelerated Corrosion

Science.gov (United States)

O’Brien, Caitlin; McBride, Amanda; E. Zaghi, Arash; Burke, Kelly A.; Hill, Alex

2017-01-01

Recent advancements in metal fibers have introduced a promising new type of stainless steel fiber with high stiffness, high failure strain, and a thickness corrosion. The main goal of this study is to compare the impact of corrosion on the mechanical properties of steel fiber-reinforced composites with those of conventional types of stainless steel. By providing experimental evidences, this study may promote the application of steel fiber-reinforced composite as a viable alternative to conventional metals. Samples of steel fiber-reinforced polymer and four different types of stainless steel were subjected to 144 and 288 h of corrosion in ferric chloride solution to simulate accelerated corrosion conditions. The weight losses due to corrosion were recorded. The corroded and control samples were tested under monotonic tensile loading to measure the ultimate stresses and strains. The effect of corrosion on the mechanical properties of the different materials was evaluated. The digital image correlation (DIC) technique was used to investigate the failure mechanism of the corrosion-damaged specimens. Overall, steel fiber-reinforced composites had the greatest corrosion resistance. PMID:28773132
Electrochemical corrosion testing of metal waste forms

International Nuclear Information System (INIS)

Abraham, D. P.; Peterson, J. J.; Katyal, H. K.; Keiser, D. D.; Hilton, B. A.

1999-01-01

Electrochemical corrosion tests have been conducted on simulated stainless steel-zirconium (SS-Zr) metal waste form (MWF) samples. The uniform aqueous corrosion behavior of the samples in various test solutions was measured by the polarization resistance technique. The data show that the MWF corrosion rates are very low in groundwaters representative of the proposed Yucca Mountain repository. Galvanic corrosion measurements were also conducted on MWF samples that were coupled to an alloy that has been proposed for the inner lining of the high-level nuclear waste container. The experiments show that the steady-state galvanic corrosion currents are small. Galvanic corrosion will, hence, not be an important mechanism of radionuclide release from the MWF alloys
Investigation of the Effects of Solution Temperature on the Corrosion Behavior of Austenitic Low-Nickel Stainless Steels in Citric Acid using Impedance and Polarization Measurements

Directory of Open Access Journals (Sweden)

Mulimbayan Francis M.

2015-01-01

Full Text Available Stainless steels may be classified according to alloy microstructure – ferritic, austenitic, martensitic, duplex, and precipitation hardening grades. Among these, austenitic grade has the largest contribution to market due to the alloy’s numerous industrial and domestic applications. In this study, the corrosion behavior of low-Nickel stainless steel in citric acid was investigated using potentiodynamic polarization techniques and Electrochemical Impedance Spectroscopy (EIS. The corrosion current density which is directly related to corrosion rate was extracted from the generated anodic polarization curve. Increasing the temperature of the citric acid resulted to increased corrosion current densities indicating higher corrosion rates at initial corrosion condition. EIS was performed to generate Nyquist plots whose shape and size depicts the corrosion mechanism and corrosion resistance of the alloy in citric acid, respectively. All the generated Nyquist plots have depressed semi-circle shapes implying that corrosion process takes place with charge-transfer as the rate-determining step. Based from the extracted values of polarization resistance (Rp, the temperature of the solution has negative correlation with the corrosion resistance of the studied alloy.
Dictionary corrosion and corrosion control

International Nuclear Information System (INIS)

1985-01-01

This dictionary has 13000 entries in both languages. Keywords and extensive accompanying information simplify the choice of word for the user. The following topics are covered: Theoretical principles of corrosion; Corrosion of the metals and alloys most frequently used in engineering. Types of corrosion - (chemical-, electro-chemical, biological corrosion); forms of corrosion (superficial, pitting, selective, intercrystalline and stress corrosion; vibrational corrosion cracking); erosion and cavitation. Methods of corrosion control (material selection, temporary corrosion protection media, paint and plastics coatings, electro-chemical coatings, corrosion prevention by treatment of the corrosive media); Corrosion testing methods. (orig./HP) [de
Corrosion Behavior and Durability of Low-Alloy Steel Rebars in Marine Environment

Science.gov (United States)

Liu, Ming; Cheng, Xuequn; Li, Xiaogang; Yue, Pan; Li, Jun

2016-11-01

The corrosion resistance of Cr-modified low-alloy steels and HRB400 carbon steel was estimated using the open-circuit potential, potentiodynamic polarization, electrochemical impedance spectroscopic, and weight loss methods in simulated concrete pore solution. Results show that Cr-modified steels exhibit a higher corrosion resistance with a higher critical chloride level (CTL), lower corrosion current density, and higher impedance than carbon steel. The CTL of the steels significantly reduces with increasing temperature. Weight loss measurement shows that the Cr-modified steels exhibit low corrosion rates and small corrosion pitting. The primary constituents of the corrosion scales are Fe2O3, Fe3O4, β-FeOOH, γ-FeOOH, and α-FeOOH. A large amount of α-FeOOH could be detected in the Cr-modified steel corrosion products. Moreover, the Cr-modified steels demonstrate a higher durability than HRB400 carbon steel.
System design description of forced-convection molten-salt corrosion loops MSR-FCL-3 and MSR-FCL-4

International Nuclear Information System (INIS)

Huntley, W.R.; Silverman, M.D.

1976-11-01

Molten-salt corrosion loops MSR-FCL-3 and MSR-FCL-4 are high-temperature test facilities designed to evaluate corrosion and mass transfer of modified Hastelloy N alloys for future use in Molten-Salt Breeder Reactors. Salt is circulated by a centrifugal sump pump to evaluate material compatibility with LiF-BeF 2 -ThF 4 -UF 4 fuel salt at velocities up to 6 m/s (20 fps) and at salt temperatures from 566 to 705 0 C (1050 to 1300 0 F). The report presents the design description of the various components and systems that make up each corrosion facility, such as the salt pump, corrosion specimens, salt piping, main heaters, salt coolers, salt sampling equipment, and helium cover-gas system, etc. The electrical systems and instrumentation and controls are described, and operational procedures, system limitations, and maintenance philosophy are discussed
Stress corrosion cracking behavior of Nd:YAG laser-treated aluminum alloy 7075

International Nuclear Information System (INIS)

Yue, T.M.; Yan, L.J.; Chan, C.P.

2006-01-01

Nd-YAG laser surface treatment was conducted on 7075-T651 aluminum alloy with the aim of improving the stress corrosion cracking resistance of the alloy. Laser surface treatment was performed under two different gas environments, air and nitrogen. After the laser treatment, coarse constituent particles were removed and fine cellular/dendritic structures had formed. In addition, for the N 2 -treated specimen, an AlN phase was detected. The results of the stress corrosion test showed that after 30 days of immersion, the untreated specimen had been severely attacked by corrosion, with intergranular cracks having formed along the planar grain boundaries of the specimen. For the air-treated specimen, some relatively long stress corrosion cracks and a small number of relatively large corrosion pits were found. The cracks mainly followed the interdendritic boundaries; the fusion boundary was found to be acting as an arrestor to corrosion attacks. In contrast, only few short stress corrosion cracks appeared in the N 2 -treated specimen, indicating an improvement in corrosion initiation resistance. The superior corrosion resistance was attributed to the formation of the AlN phase in the surface of the laser-melted layer, which is an electrical insulator. The electrochemical impedance measurements taken during the stress corrosion test showed that the film resistance of the laser-treated specimens was always higher than that of the untreated specimen, with the N 2 -treated specimen showing the highest resistance
Effect of Molybdenum on the Corrosion Behavior of High-Entropy Alloys CoCrFeNi2 and CoCrFeNi2Mo0.25 under Sodium Chloride Aqueous Conditions

Directory of Open Access Journals (Sweden)

Alvaro A. Rodriguez

2018-01-01

Full Text Available The corrosion behavior of high-entropy alloys (HEAs CoCrFeNi2 and CoCrFeNi2Mo0.25 was investigated in 3.5 wt. percent sodium chloride (NaCl at 25°C by electrochemical methods. Their corrosion parameters were compared to those of HASTELLOY® C-276 (UNS N10276 and stainless steel 316L (UNS 31600 to assess the suitability of HEAs for potential industrial applications in NaCl simulating seawater type environments. The corrosion rates were calculated using corrosion current determined from electrochemical experiments for each of the alloys. In addition, potentiodynamic polarization measurements can indicate active, passive, and transpassive behavior of the metal as well as potential susceptibility to pitting corrosion. Cyclic voltammetry (CV can confirm the alloy susceptibility to pitting corrosion. Electrochemical impedance spectroscopy (EIS elucidates the corrosion mechanism under studied conditions. The results of the electrochemical experiments and scanning electron microscopy (SEM analyses of the corroded surfaces revealed general corrosion on alloy CoCrFeNi2Mo0.25 and HASTELLOY C-276 and pitting corrosion on alloy CoCrFeNi2 and stainless steel 316L.
Molten salt corrosion behavior of structural materials in LiCl-KCl-UCl3 by thermogravimetric study

Science.gov (United States)

Rao, Ch Jagadeeswara; Ningshen, S.; Mallika, C.; Mudali, U. Kamachi

2018-04-01

The corrosion resistance of structural materials has been recognized as a key issue in the various unit operations such as salt purification, electrorefining, cathode processing and injection casting in the pyrochemical reprocessing of spent metallic nuclear fuels. In the present work, the corrosion behavior of the candidate materials of stainless steel (SS) 410, 2.25Cr-1Mo and 9Cr-1Mo steels was investigated in molten LiCl-KCl-UCl3 salt by thermogravimetric analysis under inert and reactive atmospheres at 500 and 600 °C, for 6 h duration. Insignificant weight gain (less than 1 mg/cm2) in the inert atmosphere and marginal weight gain (maximum 5 mg/cm2) in the reactive atmosphere were observed at both the temperatures. Chromium depletion rates and formation of Cr-rich corrosion products increased with increasing temperature of exposure in both inert and reactive atmospheres as evidenced by SEM and EDS analysis. The corrosion attack by LiCl-KCl-UCl3 molten salt, under reactive atmosphere for 6 h duration was more in the case of SS410 than 9Cr-1Mo steel followed by 2.25Cr-1Mo steel at 500 °C and the corrosion attack at 600 °C followed the order: 9Cr-1Mo steel >2.25Cr-1Mo steel > SS410. Outward diffusion of the minor alloying element, Mo was observed in 9Cr-1Mo and 2.25Cr-1Mo steels at both temperatures under reactive atmosphere. Laser Raman spectral analysis of the molten salt corrosion tested alloys under a reactive atmosphere at 500 and 600 °C for 6 h revealed the formation of unprotected Fe3O4 and α-as well as γ-Fe2O3. The results of the present study facilitate the selection of structural materials for applications in the corrosive molten salt environment at high temperatures.
Microstructure, Tensile Properties, and Corrosion Behavior of Die-Cast Mg-7Al-1Ca- xSn Alloys

Science.gov (United States)

Wang, Feng; Dong, Haikuo; Sun, Shijie; Wang, Zhi; Mao, Pingli; Liu, Zheng

2018-02-01

The microstructure, tensile properties, and corrosion behavior of die-cast Mg-7Al-1Ca- xSn ( x = 0, 0.5, 1.0, and 2.0 wt.%) alloys were studied using OM, SEM/EDS, tensile test, weight loss test, and electrochemical test. The experimental results showed that Sn addition effectively refined grains and intermetallic phases and increased the amount of intermetallic phases. Meanwhile, Sn addition to the alloys suppressed the formation of the (Mg,Al)2Ca phase and resulted in the formation of the ternary CaMgSn phase and the binary Mg2Sn phase. The Mg-7Al-1Ca-0.5Sn alloy exhibited best tensile properties at room temperature, while Mg-7Al-1Ca-1.0Sn alloy exhibited best tensile properties at elevated temperature. The corrosion resistance of studied alloys was improved by the Sn addition, and the Mg-7Al-1Ca-0.5Sn alloy presented the best corrosion resistance.
Mechanical damage and corrosion in the primary system purification cooler

International Nuclear Information System (INIS)

Sainz, R.A.; Fiorini, R.H.; Semino, C.J.

1987-01-01

Through the routine measurements of tritium activity and isotopic content in the exchanger's cooling water, a loss of heavy water was detected. During the decommissioning programmed for October 1986, the equipment was dismantled and the tubes losses were identified through helium fugue tests; subsequently, a 100% inspection of the tubes by atmospheric currents were performed, verifying reductions exceeding 50% of the original width in 70 tubes of the first section at the top plate level. These indications were verified through the study of the two extracted tubes, one of them observing a passing failure where marks appeared at all levels of the support and corrosion plates through splits at the top plates level. The corrosion causes were due to the low cooling flow which results from the primary system's reduction regarding the purification flow design, thus permitting the deposits accumulation. (Author)
Behavior of W-based materials in hot helium gas

Czech Academy of Sciences Publication Activity Database

Matějíček, Jiří; Vilémová, Monika; Hadraba, Hynek; Di Gabriele, F.; Kuběna, Ivo; Kolíbalová, E.; Michalička, J.; Čech, J.; Jäger, Aleš

2016-01-01

Roč. 9, December (2016), s. 405-410 ISSN 2352-1791. [International Conference of Fusion Reactor Material (ICFRM-17) /17./. Aachen, 11.10.2015-16.10.2015] R&D Projects: GA ČR(CZ) GA14-12837S Institutional support: RVO:61389021 ; RVO:68081723 ; RVO:68378271 Keywords : tungsten * helium * fusion materials Subject RIV: JG - Metallurgy; JG - Metallurgy (UFM-A); JG - Metallurgy (FZU-D) http://dx.doi.org/10.1016/j.nme.2016.03.009
Creep behavior of 8Cr2WVTa martensitic steel designed for fusion DEMO reactor. An assessment on helium embrittlement resistance

International Nuclear Information System (INIS)

Yamamoto, Norikazu; Murase, Yoshiharu; Nagakawa, Johsei; Shiba, Kiyoyuki

2001-01-01

Mechanical response against transmutational helium production, alternatively susceptibility to helium embrittlement, in a nuclear fusion reactor was examined on 8Cr2WVTa martensitic steel, a prominent structural candidate for advanced fusion systems. In order to simulate DEMO (demonstrative) reactor environments, helium was implanted into the material at 823 K with concentrations up to 1000 appmHe utilizing an α-beam from a cyclotron. Creep rupture properties were subsequently determined at the same temperature and were compared with those of the material without helium. It has been proved that helium caused no meaningful deterioration in terms of both the creep lifetime and rupture elongation. Furthermore, failure occurred completely in a transgranular and ductile manner even after high concentration helium introduction and there was no symptom of grain boundary decohesion which very often arises in helium bearing materials. These facts would mirror preferable resistance of this steel toward helium embrittlement. (author)
Effect of a helium environment on the mechanical properties of HTGR primary system metals

International Nuclear Information System (INIS)

Chow, J.G.Y.; Soo, P.; Sabatini, R.L.

1978-01-01

Creep and high cycle fatigue tests have been carried out on Incoloy 800H and Hastelloy X in a helium environment containing 40 μ atm of H 2 O, 200 μ atm H 2 , 40 μ atm CO, 20 μ atm CH 4 and 10 μ atm CO 2 . The creep behavior of Incoloy 800H does not appear to show significant differences from that measured in air. However, the Hastelloy X at the maximum test temperature studied (871 0 C, 1600 0 F) shows behavior which is inferior. With respect to high cycle fatigue, the Incoloy 800H is weaker in the helium environment at a test temperature of 649 0 C (1200 0 F). At 760 0 C (1400 0 F) the strength in helium is higher but there is a tendency to lose strength more rapidly than for the air tests as the test time increases. Hastelloy X tested at 871 0 C (1600 0 F) also shows higher strength in helium for short test times but for extended tests the strengths in air and helium become similar. Scanning electron microprobe analyses have been carried out to correlate the strength measurements with surface oxidation characteristics and internal structural changes
Corrosion behavior of AISI 4130 steel alloy in ethylene glycol–water mixture in presence of molybdate

International Nuclear Information System (INIS)

Danaee, I.; Niknejad Khomami, M.; Attar, A.A.

2012-01-01

The electrochemical behavior of steel alloy in ethylene glycol–water mixture with different concentrations was investigated by polarization curves, AC impedance measurements, current transient and atomic force microscopy. The results obtained showed that corrosion rate was decreased with increasing ethylene glycol concentration. The effect of molybdate as inhibitor was studied and high inhibition efficiency was obtained. It was found that surface passivation was occurred in presence of inhibitor. The inhibiting effect of the molybdate was explained on the basis of the competitive adsorption between the inorganic anions and the aggressive Cl − ions and the adsorption isotherm basically obeys the Langmuir adsorption isotherm. Thermodynamic parameters for steel corrosion and inhibitor adsorption were determined and reveal that the adsorption process is spontaneous. Also phenomenon of both physical and chemical adsorption is proposed. -- Highlights: ► Corrosion rate was decreased with increasing ethylene glycol concentration. ► High inhibition efficiency was obtained for molybdate. ► Surface passivation was occurred in presence of inhibitor. ► The adsorption isotherm basically obeys the Langmuir adsorption isotherm.
Helium-filled proportional counter and its operation mechanism at low temperatures

CERN Document Server

Isozumi, Y; Kishimoto, S

2002-01-01

The operation mechanism of helium-filled proportional counter (HFPC) at about 4.2 K is explained. Unstable behavior of HFPC is caused by releasing secondary-electron from the cathode by four kinds of active particles such as He sub n sup + , non-resonance photon from excited helium atom, non-resonance photon from He sub 2 sup * (A sup 1 Su sup +) and He sub 2 sup m (a sup 3 Su sup +). On experiments of HFPC behavior at low temperature, the following facts were observed; 1) main charge formation process in the electron avalanche is direct ionization by electron without Hornbeck-Molnar process. Accordingly, the gas amplification factor becomes small at low temperature. 2) Stable helium cation is He sub 2 sup + at room temperature, but cluster at low temperature. Large after-pulse is observed in output signal depends on cluster ion. The probability of secondary-electron emission decreased. The gas gain increased with increasing anode voltage. 3) By decreasing reaction rate of atom and molecule collision at low t...

A STUDY OF CORROSION AND STRESS CORROSION CRACKING OF CARBON STEEL NUCLEAR WASTE STORAGE TANKS

International Nuclear Information System (INIS)

BOOMER, K.D.

2007-01-01

The Hanford reservation Tank Farms in Washington State has 177 underground storage tanks that contain approximately 50 million gallons of liquid legacy radioactive waste from cold war plutonium production. These tanks will continue to store waste until it is treated and disposed. These nuclear wastes were converted to highly alkaline pH wastes to protect the carbon steel storage tanks from corrosion. However, the carbon steel is still susceptible to localized corrosion and stress corrosion cracking. The waste chemistry varies from tank to tank, and contains various combinations of hydroxide, nitrate, nitrite, chloride, carbonate, aluminate and other species. The effect of each of these species and any synergistic effects on localized corrosion and stress corrosion cracking of carbon steel have been investigated with electrochemical polarization, slow strain rate, and crack growth rate testing. The effect of solution chemistry, pH, temperature and applied potential are all considered and their role in the corrosion behavior will be discussed
Understanding corrosion behavior of Mg-Zn-Ca alloys from subcutaneous mouse model: effect of Zn element concentration and plasma electrolytic oxidation.

Science.gov (United States)

Jang, Yongseok; Tan, Zongqing; Jurey, Chris; Xu, Zhigang; Dong, Zhongyun; Collins, Boyce; Yun, Yeoheung; Sankar, Jagannathan

2015-03-01

Mg-Zn-Ca alloys are considered as suitable biodegradable metallic implants because of their biocompatibility and proper physical properties. In this study, we investigated the effect of Zn concentration of Mg-xZn-0.3Ca (x=1, 3 and 5wt.%) alloys and surface modification by plasma electrolytic oxidation (PEO) on corrosion behavior in in vivo environment in terms of microstructure, corrosion rate, types of corrosion, and corrosion product formation. Microstructure analysis of alloys and morphological characterization of corrosion products were conducted using x-ray computed tomography (micro-CT) and scanning electron microscopy (SEM). Elemental composition and crystal structure of corrosion products were determined using x-ray diffraction (XRD) and electron dispersive x-ray spectroscopy (EDX). The results show that 1) as-cast Mg-xZn-0.3Ca alloys are composed of Mg matrix and a secondary phase of Ca2Mg6Zn3 formed along grain boundaries, 2) the corrosion rate of Mg-xZn-0.3Ca alloys increases with increasing concentration of Zn in the alloy, 3) corrosion rates of alloys treated by PEO sample are decreased in in vivo environment, and 4) the corrosion products of these alloys after in vivo tests are identified as brucite (Mg(OH)2), hydroxyapatite (Ca10(PO4)6(OH)2), and magnesite (MgCO3·3H2O). Copyright © 2014 Elsevier B.V. All rights reserved.
Effect of organic acids traces on the carbon steel corrosion behavior

International Nuclear Information System (INIS)

Stefanescu, D.; Radulescu; Mogosan, S.

2009-01-01

There are many different ways in which organic matter may get in water-steam cycles. One important pathway is constituted by organic matter admitted into the system by chemical make-up water under standard operation conditions (without inverse osmosis). The high molecular weight organic matter, in particularly polysaccharides are broken in organic acids, in particular acetic and formic acid. This paper presents an overview of the investigations undertaken referring to the behavior SA106 gr. B mild steel in secondary circuit aqueous environment contaminated with formic and acetic acid traces. The samples were filmed in static autoclaves in operation conditions of secondary circuit, in contaminated environment and after that they were investigated using metallographic microscopy and SEM. In addition, an electrochemical technique videlicet impedance spectroscopy (EIS) was used to investigate the corrosion behavior of SA106 gr. B carbon steel in secondary circuit medium contaminated with formic and acetic acid traces. (authors)
Corrosion Behavior of a Surface Modified Inconel 713LC in a Hot Lithium Molten Salt

International Nuclear Information System (INIS)

Cho, Soo Haeng; Lim, Jong Ho; Seo, Chung Seok; Jung, Ki Jung; Park, Seoung Won

2005-01-01

The Li-reduction process involves the chemical reduction of spent fuel oxides by liquid lithium metal in a molten LiCl salt bath at 650 .deg. C followed by a separate electrochemical reduction of the lithium oxide (Li 2 O), which builds up in the salt bath. This process requires a high purity inert gas atmosphere inside a remote hot cell nuclear facility to prevent an unwanted Li oxidation and fires during the handling of the chemically active Li metal. In light of the limitations of the Li-reduction process, a direct electrolytic reduction technology is being developed by KAERI to enhance the process safety and economic viability. The electrolytic reduction of spent oxide fuel involves the liberation of the oxygen in a molten LiCl electrolyte, which results in a chemically aggressive environment that is too corrosive for typical structural materials. Even so, the electrochemical process vessel must be resilient at 650 .deg. C in the presence of oxygen to enable high processing rates and an extended service life. But, the mechanism and the rate of the corrosion of the metals in a LiCl-Li 2 O molten salt under an oxidation condition are not clear. In the present work, the corrosion behavior and corrosion mechanism of a surface modified Inconel 713LC have been studied in the molten salt of LiCl-Li 2 O under an oxidation condition
Corrosion behavior of low-alloy steel in the presence of Desulfotomaculum sp

International Nuclear Information System (INIS)

Cetin, Demet; Aksu, Mehmet Levent

2009-01-01

The objective of this study was to determine the effect of sulfate-reducing Desulfotomaculum sp. bacteria isolated from a crude oil field on the corrosion of low-alloy steel. The corrosion rate and mechanism were determined with the use of Tafel slopes, mass loss method and electrochemical impedance spectroscopy (EIS). The formation of the biofilm and the corrosion products on the steel surface was determined with scanning electron microscopy (SEM) micrographs and energy dispersive X-ray spectra (EDS) analysis. It was observed from the Tafel plots that the corrosion potential exhibited a cathodic shift that verifies an increase in the corrosion rates. The semicircles tended to open at lower frequencies in the Nyquist plots which indicates the rupture of the protective film. The corrosion current density reached its maximum value at the 14th hour after the inoculation and decreased afterwards. This was attributed to the accumulation of corrosion products on the surface.
Dynamics of Superfluid Helium in Low-Gravity

Science.gov (United States)

Frank, David J.

1997-01-01

This report summarizes the work performed under a contract entitled 'Dynamics of Superfluid Helium in Low Gravity'. This project performed verification tests, over a wide range of accelerations of two Computational Fluid Dynamics (CFD) codes of which one incorporates the two-fluid model of superfluid helium (SFHe). Helium was first liquefied in 1908 and not until the 1930s were the properties of helium below 2.2 K observed sufficiently to realize that it did not obey the ordinary physical laws of physics as applied to ordinary liquids. The term superfluidity became associated with these unique observations. The low temperature of SFHe and it's temperature unifonrmity have made it a significant cryogenic coolant for use in space applications in astronomical observations with infrared sensors and in low temperature physics. Superfluid helium has been used in instruments such as the Shuttle Infrared Astronomy Telescope (IRT), the Infrared Astronomy Satellite (IRAS), the Cosmic Background Observatory (COBE), and the Infrared Satellite Observatory (ISO). It is also used in the Space Infrared Telescope (SIRTF), Relativity Mission Satellite formally called Gravity Probe-B (GP-B), and the Test of the Equivalence Principle (STEP) presently under development. For GP-B and STEP, the use of SFHE is used to cool Superconducting Quantum Interference Detectors (SQUIDS) among other parts of the instruments. The Superfluid Helium On-Orbit Transfer (SHOOT) experiment flown in the Shuttle studied the behavior of SFHE. This experiment attempted to get low-gravity slosh data, however, the main emphasis was to study the low-gravity transfer of SFHE from tank to tank. These instruments carried tanks of SFHE of a few hundred liters to 2500 liters. The capability of modeling the behavior of SFHE is important to spacecraft control engineers who must design systems that can overcome disturbances created by the movement of the fluid. In addition instruments such as GP-B and STEP are very
Comparison of the corrosion behavior of austenitic and ferritic/martensitic steels exposed to static liquid Pb Bi at 450 and 550 °C

Science.gov (United States)

Kurata, Y.; Futakawa, M.; Saito, S.

2005-08-01

Static corrosion tests of various steels were conducted in oxygen-saturated liquid Pb-Bi eutectic at 450 °C and 550 °C for 3000 h to study the effects of temperature and alloying elements on corrosion behavior in liquid Pb-Bi. Corrosion depth decreases at 450 °C with increasing Cr content in steels regardless of ferritic/martensitic steels or austenitic steels. Appreciable dissolution of Ni and Cr does not occur in the three austenitic steels at 450 °C. Corrosion depth of ferritic/martensitic steels also decreases at 550 °C with increasing Cr content in steels whereas corrosion depth of austenitic steels, JPCA and 316SS becomes larger due to ferritization caused by dissolution of Ni at 550 °C than that of ferritic/martensitic steels. An austenitic stainless steel containing about 5%Si exhibits fine corrosion resistance at 550 °C because the protective Si oxide film is formed and prevents dissolution of Ni and Cr.
Comparison of the corrosion behavior of austenitic and ferritic/martensitic steels exposed to static liquid Pb-Bi at 450 and 550 deg. C

International Nuclear Information System (INIS)

Kurata, Y.; Futakawa, M.; Saito, S.

2005-01-01

Static corrosion tests of various steels were conducted in oxygen-saturated liquid Pb-Bi eutectic at 450 deg. C and 550 deg. C for 3000 h to study the effects of temperature and alloying elements on corrosion behavior in liquid Pb-Bi. Corrosion depth decreases at 450 deg. C with increasing Cr content in steels regardless of ferritic/martensitic steels or austenitic steels. Appreciable dissolution of Ni and Cr does not occur in the three austenitic steels at 450 deg. C. Corrosion depth of ferritic/martensitic steels also decreases at 550 deg. C with increasing Cr content in steels whereas corrosion depth of austenitic steels, JPCA and 316SS becomes larger due to ferritization caused by dissolution of Ni at 550 deg. C than that of ferritic/martensitic steels. An austenitic stainless steel containing about 5%Si exhibits fine corrosion resistance at 550 deg. C because the protective Si oxide film is formed and prevents dissolution of Ni and Cr
Corrosion study in molten fluoride salt

International Nuclear Information System (INIS)

Keny, S.J.; Kumbhar, A.G.; Rangarajan, S.; Gupta, V.K.; Maheshwari, N.K.; Vijayan, P.K.

2013-01-01

Corrosion behaviors of two alloys viz. Inconel 625 and Inconel 617 were tested in molten fluoride salts of lithium, sodium and potassium (FLiNaK) in the temperature range of 550-750 ℃ in a nickel lined Inconel vessel. Electrochemical polarization (Tafel plot) technique was used for this purpose. For both alloys, the corrosion rate was found to increase sharply beyond 650 ℃ . At 600 ℃ , Inconel 625 showed a decreasing trend in the corrosion rate over a period of 24 hours, probably due to changes in the surface conditions. After fifteen days, re-testing of Inconel 625 in the same melt showed an increase in the corrosion rate. Inconel 625 was found to be more corrosion resistant than Inconel 617. (author)
Orion A helium abundance

International Nuclear Information System (INIS)

Tsivilev, A.P.; Ershov, A.A.; Smirnov, G.T.; Sorochenko, R.L.

1986-01-01

The 22.4-GHz (H,He)66-alpha and 36.5-GHz (H,He)56-alpha radio recombination lines have been observed at several Jaffe-Pankonin positions in the central part of the Orion A source. The measured relative abundance of ionized helium increases with distance, averaging 11.6 percent at peripheral points. The observed behavior is interpreted by a blister-type model nebula, which implies that Orion A has a true He abundance of 12 percent, is moving with a radial velocity of 5 km/sec, and is expanding. 18 references
Combined Effect of Alternating Current Interference and Cathodic Protection on Pitting Corrosion and Stress Corrosion Cracking Behavior of X70 Pipeline Steel in Near-Neutral pH Environment

Directory of Open Access Journals (Sweden)

Liwei Wang

2018-03-01

Full Text Available Influence of alternating current (AC on pitting corrosion and stress corrosion cracking (SCC behavior of X70 pipeline steel in the near-neutral pH environment under cathodic protection (CP was investigated. Both corrosion and SCC are inhibited by −0.775 VSCE CP without AC interference. With the superimposition of AC current (1–10 mA/cm2, the direct current (DC potential shifts negatively under the CP of −0.775 VSCE and the cathodic DC current decreases and shifts to the anodic direction. Under the CP potential of −0.95 VSCE and −1.2 VSCE, the applied AC current promotes the cathodic reaction and leads to the positive shift of DC potential and increase of cathodic current. Local anodic dissolution occurs attributing to the generated anodic current transients in the positive half-cycle of the AC current, resulting in the initiation of corrosion pits (0.6–2 μm in diameter. AC enhances the SCC susceptibility of X70 steel under −0.775 VSCE CP, attributing to the promotion of anodic dissolution and hydrogen evolution. Even an AC current as low as 1 mA/cm2 can enhance the SCC susceptibility.
Corrosion behavior of HPT-deformed TiNi alloys in cell culture medium

Science.gov (United States)

Shri, D. N. Awang; Tsuchiya, K.; Yamamoto, A.

2017-09-01

In recent years there are growing interest in fabrication of bulk nanostructured metals and alloys by using severe plastic deformation (SPD) techniques as new alternative in producing bulk nanocrystalline materials. These techniques allows for processing of bulk, fully dense workpiece with ultrafine grains. Metal undergoes SPD processing in certain techniques such as high pressure torsion (HPT), equal-channel angular pressing (ECAP) or multi-directional forging (MDF) are subjected to extensive hydrostatic pressure that may be used to impart a very high strain to the bulk solid without the introduction of any significant change in overall dimension of the sample. The change in the structure (small grain size and high-volume fraction of grain boundaries) of the material may result in the corrosion behavior different from that of the coarse-grained material. Electrochemical measurements were done to understand the corrosion behavior of TiNi alloys before and after HPT deformation. The experiment was carried out using standard three electrode setup (a sample as working electrode; a platinum wire as a counter electrode and a saturated calomel electrode in saturated KCl as a reference electrode) with the surface area of 26.42 mm2 exposed to the EMEM+10% FBS cell culture medium. The measurements were performed in an incubator with controlled environment at 37 °C and 5% CO2, simulating the cell culture condition. The potential of the specimen was monitored over 1 hour, and the stabilized potential was used as the open-circuit potential (EOCP). Potentiodynamic curves were scanned in the potential range from -0.5 V to 1.5 V relative to the EOCP, at a rate of 0.5 mV/s. The result of OCP-time measurement done in the cell culture medium shows that the OCP of HPT-deformed samples shifts towards to the more positive rather than that of BHPT samples. The OCP of deformed samples were ennobled to more than +70 mV for Ti-50mol%. The shift of OCP towards the nobler direction
A study of corrosion behavior of Ni-22Cr-13Mo-3W alloy under hygroscopic salt deposits on hot surface

International Nuclear Information System (INIS)

Badwe, Sunil; Raja, K.S.; Misra, M.

2006-01-01

Alloy 22, a nickel base Ni-22Cr-13Mo-3W alloy has an excellent corrosion resistance in oxidizing and reducing environments. Most of the corrosion studies on Alloy 22 have been conducted using conventional chemical or electrochemical methods. In the present investigation, the specimen was directly heated instead of heating the electrolyte, thereby simulating the nuclear waste package container temperature profile. Corrosion behavior of Alloy 22 and evaporation conditions of water diffusing on the container were evaluated using the newly devised heated electrode corrosion test (HECT) method in simulated acidified water (SAW) and simulated concentrated water (SCW) environments. In this method, the concentration of the environment varied with test duration. The corrosion rate of Alloy 22 was not affected by the continuous increase in ionic strength of the SAW (pH 3) environment. Passivation kinetics was faster with increase in concentration of the electrolytes. The major difference between the conventional test and HECT was the aging characteristics of the passive film of Alloy 22. The heated electrode corrosion test can be used for evaluating materials for construction of heat transfer equipments such as evaporators
Effect of silicon carbide addition on the corrosion behavior of powder metallurgy Cu−30Zn brass in a 3.5 wt% NaCl solution

Energy Technology Data Exchange (ETDEWEB)

Almomani, Mohammed Ali, E-mail: maalmomani7@just.edu.jo [Department of Industrial Engineering, Jordan University of Science and Technology, P. O. Box 3030, Irbid 22110 (Jordan); Tyfour, Wa' il Radwan, E-mail: wrtyfou@just.edu.jo [Department of Industrial Engineering, Jordan University of Science and Technology, P. O. Box 3030, Irbid 22110 (Jordan); Nemrat, Mohammed Hani, E-mail: mohammednemrat@yahoo.com [Department of Mechanical Engineering, Institute of Applied Technology, Abu Dhabi (United Arab Emirates)

2016-09-15

A study was made to evaluate the corrosion behavior when Cu−30Zn alloy is reinforced with different weight fractions of silicon carbide (SiC) particles in a simulated sea solution (3.5 wt% NaCl aqueous solution). The composites were produced via powder metallurgy (PM) route. For the sake of comparison, the corrosion behaviors of unreinforced and reinforced alloy were examined. Electrochemical measurements (potentiodynamic testing) showed that the corrosion rate of the composites decreased with increase of SiC weight percentages, as a result of weak microgalvanic couple between reinforcement particles and Cu−30Zn matrix, and the low possibility of intermetallic phases formation. ANOVA test indicated that the variations of corrosion rate of the composites upon changing weight percentages of SiC particles are statistically significant. Polarization curves showed that the passive film tends to be less stable, and the potential difference between passivation and free corrosion points increased with increase of SiC weight percentages, as SiC cathodically protect the matrix material by sacrificial anodic dissolution of crevice regions about reinforcement particles. Scanning Electron Microscope (SEM) images of the sample's surfaces before and after testing are in agreement with the electrochemical results. - Highlights: • Effect of adding SiC on both uniform and localized corrosion of Cu−30Zn alloy is studied. • Reinforcing Cu−30Zn with nonconductive SiC particles decreases its tendency to uniform and localized corrosion. • Reinforcement particles cathodically protect the matrix material, and retard pit propagation to the matrix.
Aqueous corrosion study on U-Zr alloy

International Nuclear Information System (INIS)

Pal, Titas; Venkatesan, V.; Kumar, Pradeep; Khan, K.B.; Kumar, Arun

2009-01-01

In low power or research reactor, U-Zr alloy is a potential candidate for dispersion fuel. Moreover, Zirconium has a low thermal-neutron cross section and uranium alloyed with Zr has excellent corrosion resistance and dimensional stability during thermal cycling. In the present study aqueous corrosion behavior of U-Zr alloy samples was studied in autoclave at 200 deg C temperature. Corrosion rate was determined from weight loss with time. (author)
Corrosion and impedance studies on magnesium alloy in oxalate solution

International Nuclear Information System (INIS)

Fekry, A.M.; Tammam, Riham H.

2011-01-01

Highlights: → Corrosion behavior of AZ91E alloy was investigated in 0.1 M Na 2 C 2 O 4 containing different additives as Br - , Cl - or Silicate. → The corrosion rate of 0.1 M oxalate solution containing silicate ion is lower than the blank (0.1 M Na 2 C 2 O 4 ). This was confirmed by scanning electron microscope (SEM) observations. → For the other added ions Br - or Cl - , the corrosion rate is higher than the blank. - Abstract: Corrosion behavior of AZ91E alloy was investigated in oxalate solution using potentiodynamic polarization and electrochemical impedance measurements (EIS). The effect of oxalate concentration was studied, where the corrosion rate increases with increasing oxalate concentration. The effect of added ions (Br - , Cl - or SiO 3 2- ) on the electrochemical behavior of magnesium alloy in 0.1 M Na 2 C 2 O 4 solution at 298 K, was investigated. It was found that the corrosion rate of 0.1 M oxalate solution containing silicate ion is lower than the blank (0.1 M Na 2 C 2 O 4 ). This was confirmed by scanning electron microscope (SEM) observations. However, for the other added ions Br - or Cl - , the corrosion rate is higher than the blank.
Effect of working pressure on corrosion behavior of nitrogen doped diamond-like carbon thin films deposited by DC magnetron sputtering.

Science.gov (United States)

Khun, N W; Liu, E

2011-06-01

Nitrogen doped diamond-like carbon thin films were deposited on highly conductive p-silicon(100) substrates using a DC magnetron sputtering deposition system by varying working pressure in the deposition chamber. The bonding structure, adhesion strength, surface roughness and corrosion behavior of the films were investigated by using X-ray photoelectron spectroscopy, micro-Raman spectroscopy, micro-scratch test, atomic force microscopy and potentiodynamic polarization test. A 0.6 M NaCl electrolytic solution was used for the corrosion tests. The optimum corrosion resistance of the films was found at a working pressure of 7 mTorr at which a good balance between the kinetics of the sputtered ions and the surface mobility of the adatoms promoted a microstructure of the films with fewer porosities.
Tritium Decay Helium-3 Effects in Tungsten

Energy Technology Data Exchange (ETDEWEB)

Shimada, M. [Idaho National Lab. (INL), Idaho Falls, ID (United States); Merrill, B. J. [Idaho National Lab. (INL), Idaho Falls, ID (United States)

2016-06-01

A critical challenge for long-term operation of ITER and beyond to a Demonstration reactor (DEMO) and future fusion reactor will be the development of plasma-facing components (PFCs) that demonstrate erosion resistance to steady-state/transient heat fluxes and intense neutral/ion particle fluxes under the extreme fusion nuclear environment, while at the same time minimizing in-vessel tritium inventories and permeation fluxes into the PFC’s coolant. Tritium will diffuse in bulk tungsten at elevated temperatures, and can be trapped in radiation-induced trap site (up to 1 at. % T/W) in tungsten [1,2]. Tritium decay into helium-3 may also play a major role in microstructural evolution (e.g. helium embrittlement) in tungsten due to relatively low helium-4 production (e.g. He/dpa ratio of 0.4-0.7 appm [3]) in tungsten. Tritium-decay helium-3 effect on tungsten is hardly understood, and its database is very limited. Two tungsten samples (99.99 at. % purity from A.L.M.T. Co., Japan) were exposed to high flux (ion flux of 1.0x1022 m-2s-1 and ion fluence of 1.0x1026 m-2) 0.5%T2/D2 plasma at two different temperatures (200, and 500°C) in Tritium Plasma Experiment (TPE) at Idaho National Laboratory. Tritium implanted samples were stored at ambient temperature in air for more than 3 years to investigate tritium decay helium-3 effect in tungsten. The tritium distributions on plasma-exposed was monitored by a tritium imaging plate technique during storage period [4]. Thermal desorption spectroscopy was performed with a ramp rate of 10°C/min up to 900°C to outgas residual deuterium and tritium but keep helium-3 in tungsten. These helium-3 implanted samples were exposed to deuterium plasma in TPE to investigate helium-3 effect on deuterium behavior in tungsten. The results show that tritium surface concentration in 200°C sample decreased to 30 %, but tritium surface concentration in 500°C sample did not alter over the 3 years storage period, indicating possible tritium
The corrosion Characteristics and Behaviors of the Ti-2.19Al-2.35Zr alloy

International Nuclear Information System (INIS)

Kim, Tae Hoon; Kang, Chang Sun; Baek, Jong Hyuk; Kim, Hyun Gil; Choi, Byoung Kwon; Jeong, Yong Hwan

2007-01-01

Ti-2.19Al-2.35Zr alloy is being considered as a steam generator tube material for the advanced pressurized water reactor (PWR) which is being developed by KAERI for the purpose of seawater desalination as well as a small scale electricity production. The main operational environment of SMART differs somewhat from that of a commercial PWR. That is, a heat-exchange tube is always exposed to a high temperature/pressure condition and an ammonia water chemistry is designed as a pH controlling agent without an addition of boric acid. The excellent mechanical and corrosion resistance properties are required for the steam generator tube material in SMART. Thus Ti-2.19Al-2.35Zr alloy was studied to investigate of the corrosion characteristics and behaviors of the Ti- 2.19Al-2.35Zr alloy in a simulated-SMART loop
Effect of Chromium on Corrosion Behavior of P110 Steels in CO2-H2S Environment with High Pressure and High Temperature

Directory of Open Access Journals (Sweden)

Jianbo Sun

2016-03-01

Full Text Available The novel Cr-containing low alloy steels have exhibited good corrosion resistance in CO2 environment, mainly owing to the formation of Cr-enriched corrosion film. In order to evaluate whether it is applicable to the CO2 and H2S coexistence conditions, the corrosion behavior of low-chromium steels in CO2-H2S environment with high pressure and high temperature was investigated using weight loss measurement and surface characterization. The results showed that P110 steel suffered localized corrosion and both 3Cr-P110 and 5Cr-P110 steels exhibited general corrosion. However, the corrosion rate of 5Cr-P110 was the highest among them. The corrosion process of the steels was simultaneously governed by CO2 and H2S. The outer scales on the three steels mainly consisted of FeS1−x crystals, whereas the inner scales on Cr-containing steels comprised of amorphous FeS1−x, Cr(OH3 and FeCO3, in contrast with the amorphous FeS1−x and FeCO3 mixture film of P110 steel. The more chromium the steel contains, the more chromium compounds the corrosion products contain. The addition of chromium in steels increases the uniformity of the Cr-enriched corrosion scales, eliminates the localized corrosion, but cannot decrease the general corrosion rates. The formation of FeS1−x may interfere with Cr-enriched corrosion scales and lowering the corrosion performance of 3Cr-P110 and 5Cr-P110 steels.

Some links on this page may take you to non-federal websites. Their policies may differ from this site.