Heat treatment control of Bi-2212 coils: I. Unravelling the complex dependence of the critical current density of Bi-2212 wires on heat treatment

Science.gov (United States)

Shen, Tengming; Li, Pei; Ye, Liyang

2018-01-01

A robust and reliable heat treatment is crucial for developing superconducting magnets from several superconductors especially Bi-2212. An improper heat treatment may significantly reduce the critical current density Jc of a Bi-2212 superconducting coil, even to zero, since the Jc of Bi-2212 wires is sensitive to parameters of its heat treatment (partial melt processing). To provide an essential database for heat treating Bi-2212 coils, the dependence of Jc on heat treatment is studied systematically in 11 industrial Bi-2212 wires, revealing several common traits shared between these wires and outlier behaviors. The dependence of the Jc of Bi-2212 on heat treatment is rather complex, with many processing parameters affecting Jc, including the peak processing temperature Tp, the time at the peak temperature tp, the time in the melt tmelt, the rate at which Bi-2212 melt is initially cooled CR1, the rate at which the solidification of Bi-2212 melt occurs CR2, and the temperature Tq at which the cooling rate switches from CR1 to CR2. The role of these parameters is analyzed and clarified, in the perspective of heat treating a coil. Practical advices on heat treatment design are given. The ability of a Bi-2212 coil to follow the prescribed recipe decreases with increasing coil sizes. The size of a coil that can be properly heat treated is determined.

Lowcost automated control for steel heat treatments

International Nuclear Information System (INIS)

Zambaldi, Edimilson; Magalhães, Ricardo R.; Barbosa, Bruno H.G.; Silva, Sandro P. da; Ferreira, Danton D.

2017-01-01

Highlights: • Control the furnace temperature measured by thermocouple and adjusts it. • Activating the furnace resistors through Pulse Width Modulation. • Appling heat treatments to steels by a low-cost controller. - Abstract: The aim of this paper is to propose a low cost, automated furnace control system for the heat treatment of steel. We used an open source electronic prototyping platform to control the furnace temperature, thus reducing human interaction during the heat process. The platform can be adapted to non-controlled commercial furnaces, which are often used by small businesses. A Proportional-Integral-Derivative (PID) controller was implemented to regulate the furnace temperature based on a defined heat treatment cycle. The embedded system activates the furnace resistors through Pulse Width Modulation (PWM), allowing for control of electrical power supplied to the furnace. Hardening and tempering were performed on standard steel samples using a traditional method (visual inspection without temperature control) as well the embedded system with PID feedback control. The results show that the proposed system can reproduce an arbitrary heat treatment curve with accuracy and provide the desired final hardness as inferred through metallographic analysis. In addition, we observed a 6% saving in energy consumption using the proposed control system. Furthermore, the estimated cost to implement the system is 42% lower than a commercial controller model implemented in commercial furnaces.

Mortality of insect life stages during simulated heat treatment

Science.gov (United States)

. Heat treatment for insect disinfestation uses elevated air temperatures that are lethal to stored-product insects. Heat treatment has been demonstrated in our research to offer a reduced-risk alternative to fumigation or residual pesticide use in empty bins. Heat is also compatible with organic gr...

Plasma treatment of heat-resistant materials

International Nuclear Information System (INIS)

Vlasov, V A; Kosmachev, P V; Skripnikova, N K; Bezukhov, K A

2015-01-01

Refractory lining of thermal generating units is exposed to chemical, thermal, and mechanical attacks. The degree of fracture of heat-resistant materials depends on the chemical medium composition, the process temperature and the material porosity. As is known, a shortterm exposure of the surface to low-temperature plasma (LTP) makes possible to create specific coatings that can improve the properties of workpieces. The aim of this work is to produce the protective coating on heat-resistant chamotte products using the LTP technique. Experiments have shown that plasma treatment of chamotte products modifies the surface, and a glass-ceramic coating enriched in mullite is formed providing the improvement of heat resistance. For increasing heat resistance of chamotte refractories, pastes comprising mixtures of Bacor, alumina oxide, and chamot were applied to their surfaces in different ratios. It is proved that the appropriate coating cannot be created if only one of heat-resistant components is used. The required coatings that can be used and recommended for practical applications are obtained only with the introduction of powder chamot. The paste composition of 50% chamot, 25% Bacor, and 25% alumina oxide exposed to plasma treatment, has demonstrated the most uniform surface fusion. (paper)

Heat Treatment of Tools in Light Industry

Science.gov (United States)

Petukhov, V. A.

2005-09-01

Heat treatment processes for some tools (knitting needles, travelers for thimbles of spinning and doubling frames, thread-forming spinnerets) used for the production of cloths, hosiery, and other articles) in the knitting and textile industries are considered. Problems of the choice of steel and the kind and parameters of heat treatment are discussed in connection with the special features of tool design and operating conditions.

49 CFR 179.300-10 - Postweld heat treatment.

Science.gov (United States)

2010-10-01

... 49 Transportation 2 2010-10-01 2010-10-01 false Postweld heat treatment. 179.300-10 Section 179.300-10 Transportation Other Regulations Relating to Transportation PIPELINE AND HAZARDOUS MATERIALS... Postweld heat treatment. After welding is complete, steel tanks and all attachments welded thereto, must be...

7 CFR 58.236 - Pasteurization and heat treatment.

Science.gov (United States)

2010-01-01

... 7 Agriculture 3 2010-01-01 2010-01-01 false Pasteurization and heat treatment. 58.236 Section 58... Service 1 Operations and Operating Procedures § 58.236 Pasteurization and heat treatment. All milk and... is handled according to sanitary conditions approved by the Administrator. (a) Pasteurization. (1...

Failures of tool steels after heat treatments

International Nuclear Information System (INIS)

Nunez-Gonzalez, G.

1990-01-01

The main objective of the work was to determine the most common defects occuring in tool steels of the AISI D-2, S-1, 0-1 and W-2 series during thermal treatment. Defects were evaluated by metallographic analyses, a method used to determine and recognize micro structural defects and their origin in order to be able to eliminate and correct some of the stages that are caused by heat treatment. Results show a large number of defects due to irregularities during thermal heating such as excess or lack of temperature, heating time, and atmosphere, rectifying and handling in service and, to a lesser extent, poor design. In conclusion, with the results obtained for each of the thermal treatments it is necessary to define, particularly the values each of these variables should have since they affect the material properties. (Author)

Using geothermal energy to heat a portion of a formation for an in situ heat treatment process

Science.gov (United States)

Pieterson, Roelof; Boyles, Joseph Michael; Diebold, Peter Ulrich

2010-06-08

Methods of using geothermal energy to treat subsurface formations are described herein. Methods for using geothermal energy to treat a subsurface treatment area containing or proximate to hydrocarbons may include producing geothermally heated fluid from at least one subsurface region. Heat from at least a portion of the geothermally heated fluid may be transferred to the subsurface treatment area to heat the subsurface treatment area. At least some hydrocarbon fluids may be produced from the formation.

Examination of heat treatments at preservation of grape must

Directory of Open Access Journals (Sweden)

Péter Korzenszky

2014-02-01

Full Text Available Heat treatment is a well-known process in food preservation. It is made to avoid and to slow down food deterioration. The process was developed by Louise Pasteur French scientist to avoid late among others wine further fermentation. The different heat treatments influence the shelf life in food production. In our article we present the process of grape must fermentation, as grape must is the base material of wine production. The treatment of harvested fresh grape juice has a big influence on end product quality. It is our experiments we examined the same grape must with four different methods in closed and in open spaces to determine CO2 concentration change. There are four different methods for treatment of grape juice: boiling, microwave treatment, treatment by water bath thermostat and a control without treatment. As a result of the comparison it can be stated that the heat treatment delays the start of fermentation, thereby increasing shelf life of grape must. However, no significant differences were found between two fermentation of heat-treated grape must by the microwave and water-bath thermostat. The different heat treatment of grape must base materials was done at the laboratory in Faculty of Mechanical Engineering of Szent István University. The origin of the table grapes used for the examination was Gödöllő-hillside. Normal 0 21 false false false HU X-NONE X-NONE

Effect of heat treatment on carbon steel pipe welds

International Nuclear Information System (INIS)

Mohamad Harun.

1987-01-01

The heat treatment to improve the altered properties of carbon steel pipe welds is described. Pipe critical components in oil, gasification and nuclear reactor plants require adequate room temperature toughness and high strength at both room and moderately elevated temperatures. Microstructure and microhardness across the welds were changed markedly by the welding process and heat treatment. The presentation of hardness fluctuation in the welds can produce premature failure. A number of heat treatments are suggested to improve the properties of the welds. (author) 8 figs., 5 refs

Heat Treatment and Properties of Iron and Steel

National Research Council Canada - National Science Library

Digges, Thomas

1966-01-01

.... Chemical compositions, heat treatments, and some properties and uses are presented for structural steels, tool steels, stainless and heat-resisting steels, precipitation-hardenable stainless steels...

Thermoluminescent determination of prehistoric heat treatment of chert artifacts

International Nuclear Information System (INIS)

Melcher, C.L.; Zimmerman, D.W.

1977-01-01

In recent years archeologists have become interested in the extent to which prehistoric peoples heat-treated chert prior to shaping it into tools. Thermoluminescent determination of the radiation dose accumulated by an artifact since it was formed or last heated provides a simple, reliable test for such heat treatment. This test can be applied to single artifacts without the need for raw source material for comparison. Results on 25 artifacts from four sites indicate that, for many chert sources, color and luster are not useful indicators of heat treatment by prehistoric peoples

Investigation of anodic oxide coatings on zirconium after heat treatment

International Nuclear Information System (INIS)

Sowa, Maciej; Dercz, Grzegorz; Suchanek, Katarzyna; Simka, Wojciech

2015-01-01

Highlights: • Oxide layers prepared via PEO of zirconium were subjected to heat treatment. • Surface characteristics were determined for the obtained oxide coatings. • Heat treatment led to the partial destruction of the anodic oxide layer. • Pitting corrosion resistance of zirconium was improved after the modification. - Abstract: Herein, results of heat treatment of zirconium anodised under plasma electrolytic oxidation (PEO) conditions at 500–800 °C are presented. The obtained oxide films were investigated by means of SEM, XRD and Raman spectroscopy. The corrosion resistance of the zirconium specimens was evaluated in Ringer's solution. A bilayer oxide coatings generated in the course of PEO of zirconium were not observed after the heat treatment. The resulting oxide layers contained a new sublayer located at the metal/oxide interface is suggested to originate from the thermal oxidation of zirconium. The corrosion resistance of the anodised metal was improved after the heat treatment

Efficacy of heat treatment for disinfestation of concrete grain silos

Science.gov (United States)

Field experiments were conducted in 2007 and 2008 to evaluate heat treatment for disinfestations of empty concrete elevator silos. A Mobile Heat Treatment Unit was used to introduce heat into silos to attain target conditions of 50°C for at least 6 h. Ventilated plastic containers with a capacity of...

Saving energy resources during heat treatment - the most important problem of the branch

Energy Technology Data Exchange (ETDEWEB)

Zadernovskiy, V V; Firger, I V

1980-01-01

Natural gas fired thermal furnaces expend significantly less fuel than electric furnaces with an equal quality of metal heating. An important reserve in power reserve economy is the use of the forging heat in an article for heat treatment (TOB), where besides the power resources, metal is also saved as a result of the reduction in the volume of heating means and production spaces. From the experience in the progressive enterprises of the branch, in a number of cases it is possible to combine heating for plastic deformation with heating for primary or secondary heat treatment. Other measures are examined which save power resources in heat treatment: the use of thermal furnaces for aerodynamic heating, the use of local heat treatment, the reduction in the duration of the heat treatment processes, savings in the power carriers during heat treatment in furnaces with a roll out hearth. Fibrous refractory materials are being used more and more as fettling materials in the construction of thermal furnaces.

New Nomenclatures for Heat Treatments of Additively Manufactured Titanium Alloys

Science.gov (United States)

Baker, Andrew H.; Collins, Peter C.; Williams, James C.

2017-07-01

The heat-treatment designations and microstructure nomenclatures for many structural metallic alloys were established for traditional metals processing, such as casting, hot rolling or forging. These terms do not necessarily apply for additively manufactured (i.e., three-dimensionally printed or "3D printed") metallic structures. The heat-treatment terminology for titanium alloys generally implies the heat-treatment temperatures and their sequence relative to a thermomechanical processing step (e.g., forging, rolling). These designations include: β-processing, α + β-processing, β-annealing, duplex annealing and mill annealing. Owing to the absence of a thermomechanical processing step, these traditional designations can pose a problem when titanium alloys are first produced via additive manufacturing, and then heat-treated. This communication proposes new nomenclatures for heat treatments of additively manufactured titanium alloys, and uses the distinct microstructural features to provide a correlation between traditional nomenclature and the proposed nomenclature.

Technical project of complex fast cycle heat treatment of hydrogenous coal preparation

OpenAIRE

Moiseev, V. A.; Andrienko, V. G.; Pileckij, V. G.; Urvancev, A. I.; Gvozdyakov, Dmitry Vasilievich; Gubin, Vladimir Evgenievich; Matveev, Aleksandr Sergeevich; Savostiyanova, Ludmila Viktorovna

2015-01-01

Problems of heat-treated milled hydrogenous coal preparation site creation in leading fast cycle heat treatment complex were considered. Conditions for effective use of electrostatic methods of heat-treated milled hydrogenous coal preparation were set. Technical project of heat treatment of milled hydrogenous coal preparation site was developed including coupling of working equipment complex on fast heat treatment and experimental samples of equipment being designed for manufacturing. It was ...

Effects of heat treatment on the mechanical properties of kenaf fiber

Energy Technology Data Exchange (ETDEWEB)

Carada, Paulo Teodoro D. L. [Master’s student in the Graduate School of Science and Engineering, Mechanical Engineering, Doshisha University, 1-3 Tatara Miyakodani, Kyotanabe City, Kyoto Prefecture, 610-0394 (Japan); Fujii, Toru; Okubo, Kazuya [Professor in the Faculty of Science and Engineering, Department of Mechanical and Systems Engineering, Doshisha University, 1-3 Tatara Miyakodani, Kyotanabe City, Kyoto Prefecture, 610-0394 (Japan)

2016-05-18

Natural fibers are utilized in various ways. One specific application of it, is in the field natural fiber composite (NFC). Considerable amount of researches are conducted in this field due to rising concerns in the harmful effects of synthetic materials to the environment. Additionally, these researches are done in order to overcome the drawbacks which limit the wide use of natural fiber. A way to improve NFC is to look into the reinforcing component (natural fiber). Treatments, which are classified as mechanical or chemical in nature, can be done in order to improve the performance of the natural fiber. The aim of this study is to assess the effects of heat treatment in the mechanical properties of kenaf fiber. In addition, the response of mechanical properties after exposure to high moisture environment of heat-treated kenaf fibers was observed. Heat treatment was done for one hour with the following heating temperatures: 140, 160, 180, and 200 °C. X-ray diffraction analysis was done to calculate the crystallinity index of kenaf fibers after heat treatment. The results showed that increase in tensile strength can be attained when kenaf fibers are heat treated at 140 °C. However, the tensile modulus showed inconsistency with respect to heat treatment temperature. The computed crystallinity index of the fiber matched the tensile strength observed in non-treated and heat-treated kenaf fibers. The results obtained in this study can be used for applications where heat treatment on kenaf fibers is needed.

Effect of heat treatment on structure and magnetic properties

Indian Academy of Sciences (India)

Fe46Co35Ni19/CNTs nanocomposites have been prepared by an easy two-step route including adsorption and heat treatment processes. We investigated the effect of heat treatment conditions on structure, morphology, nanoparticle sizes and magnetic properties of the Fe46Co35Ni19 alloy nanoparticles attached on the ...

Heat treatment of cathodic arc deposited amorphous hard carbon films

Energy Technology Data Exchange (ETDEWEB)

Anders, S.; Ager, J.W. III; Brown, I.G. [and others

1997-02-01

Amorphous hard carbon films of varying sp{sup 2}/sp{sup 3} fractions have been deposited on Si using filtered cathodic are deposition with pulsed biasing. The films were heat treated in air up to 550 C. Raman investigation and nanoindentation were performed to study the modification of the films caused by the heat treatment. It was found that films containing a high sp{sup 3} fraction sustain their hardness for temperatures at least up to 400 C, their structure for temperatures up to 500 C, and show a low thickness loss during heat treatment. Films containing at low sp{sup 3} fraction graphitize during the heat treatment, show changes in structure and hardness, and a considerable thickness loss.

Fabrication techniques to eliminate postweld heat treatment

International Nuclear Information System (INIS)

Lochhead, J.C.

1978-01-01

Postweld heat treatments to reduce residual stresses (stress relief operations) have been a common practice in the pressure vessel industry for a large number of years. A suitable heat treatment operation can, in particular for low alloy steels, have additional beneficial effects, i.e. a reduction in peak hardness values in the heat-affected zone, an improvement in weld metal properties, and a lowering of the adverse effects of the welding process on the mechanical properties of the parent material adjacent to the weld metal. However, continuing studies in the field of brittle fracture, improved parent materials, and more sophisticated nondestructive testing techniques have led to the elimination of such a practice in ever-increasing thickness ranges and types of material. For instance, the recently issued BS 5500 compared with BS 1113 (1969) lifts the thickness limit requiring stress relief in certain circumstances from 19 to 35mm for C steels. With respect to materials the CEGB has stated that as a result of successful operational experience it will no longer be necessary to postweld heat treat butt welds in 2 1/4 Cr-1Mo tubes of certain dimensions. Despite this trend, over a period of years a number of instances have arisen where, because of some factor, postweld heat treatment, although perhaps desirable, is not possible. This Paper describes several such examples. It must be noted that the examples quoted consist of relatively important and major items. It has been necessary within the confines of this Paper to condense the reports. It is hoped that no significant factors have been omitted. (author)

Effect of heat treatment temperature on binder thermal conductivities

International Nuclear Information System (INIS)

Wagner, P.

1975-12-01

The effect of heat treatment on the thermal conductivities of a pitch and a polyfurfuryl alcohol binder residue was investigated. Graphites specially prepared with these two binders were used for the experiments. Measured thermal conductivities were treated in terms of a two-component system, and the binder thermal conductivities were calculated. Both binder residues showed increased thermal conductivity with increased heat treatment temperature

Impact of Heat-Shock Treatment on Yellowing of Pak Choy Leaves

Institute of Scientific and Technical Information of China (English)

WANG Xiang-yang; SHEN Lian-qing; YUAN Hai-na

2004-01-01

The physiological mechanism of maintaining the green colour of pak choy leaves (Brassica rapa var chinensis) with heat-shock treatment was studied. Chlorophyll in the outer leaves of pak choy degraded rapidly during storage at ambient temperature (20 ± 2℃), a slight yellow appeared. Heat-shock treatment (46- 50℃) had a mild effect on maintaining the green colour of outer leaves. Normal chlorophyll degradation was associated with a binding of chlorophyll with chlorophyll-binding-protein preceding chlorophyll breakdown.Heat-shock treatment was found to reduce the binding-capacity between chlorophyllbinding-protein and chlorophyll. In the chlorophyll degradation pathway, pheide dioxygenase was synthesized during leaf senescence which was considered to be a key enzyme in chlorophyll degradation. Activity of this enzyme was reduced following heat-shock treatment, which might explain the observed reduction in chlorophyll breakdown. Two groups of heat-shock proteins were detected in treated leaves, the first group containing proteins from 54KDa to 74 Kda, and the second group contained proteins from 15 KDa to 29KDa. Heat-shock treatment was also found to retard the decline of glucose and fructose (the main energy substrates) of outer leaves.

Effects of heat treatment on the radiosensitivity of Salmonellae

International Nuclear Information System (INIS)

Choi, E.H.; Yang, J.S.; Lee, S.R.

1978-01-01

When the food poisoning bacteria Salmonella enteritidis and S. typhimurium were treated with radiation (cobalt-60 γ-rays) and heat (10 minutes at 45 0 C or 50 0 C), their sterilizing effect was revealed differently depending on the order of treatments. Post-irradiation heating showed a synergistic effect whereas pre-irradiation heating revealed the opposite effect and the effects differed slightly with heating temperature. (author)

Novel magnetic heating probe for multimodal cancer treatment.

Science.gov (United States)

Kan-Dapaah, Kwabena; Rahbar, Nima; Soboyejo, Wole

2015-05-01

Multifunctional materials consisting of polymers and magnetic nanoparticles (MNPs) are highly sought after in the field of biomedical engineering. These materials offer new opportunities for the development of novel cancer treatment modalities that can increase the efficacy of cancer therapy. In this paper, a novel probe for multimodal cancer treatment is proposed and analyzed. The probe is essentially a cannula with two main parts: a distal heat generating tip made of a magnetic nanocomposite and a proximal insulated shaft. A description of the concept and functional operations of the probe is presented. In an effort to assess its feasibility, the authors evaluated the ability of probe tip (made of PMMA-Fe3O4 nanocomposite) to generate heat in biological tissue using alternating magnetic field (AMF) parameters (field strength and frequency) that are acceptable for human use. Heat generation by MNPs was determined using the linear response theory. The effects of Fe3O4 volume fraction on heat generation as well as treatment time on the thermal dose were studied. The finite element method model was tested for its validity using an analytical model. Lesions were revealed to have an ellipsoidal shape and their sizes were affected by treatment time. However, their shapes remained unchanged. The comparison with the analytical model showed reasonably a good agreement to within 2%. Furthermore, the authors' numerical predictions also showed reasonable agreement with the experimental results previously reported in the literature. The authors' predictions demonstrate the feasibility of their novel probe to achieve reasonable lesion sizes, during hyperthermic or ablative heating using AMF parameters (field strength and frequency) that are acceptable for human use.

Heat treatment giving a stable high temperature micro-structure in cast austenitic stainless steel

Science.gov (United States)

Anton, Donald L.; Lemkey, Franklin D.

1988-01-01

A novel micro-structure developed in a cast austenitic stainless steel alloy and a heat treatment thereof are disclosed. The alloy is based on a multicomponent Fe-Cr-Mn-Mo-Si-Nb-C system consisting of an austenitic iron solid solution (.gamma.) matrix reinforced by finely dispersed carbide phases and a heat treatment to produce the micro-structure. The heat treatment includes a prebraze heat treatment followed by a three stage braze cycle heat treatment.

Shelf-life extension of bread by heat and irradiation treatment [Bangladesh

International Nuclear Information System (INIS)

Begum, F.; Siddique, A.K.; Choudhury, N.; Mollah, R.A.

1994-01-01

Bread slices were given irradiation treatment 0.5, 1.0, 1.5, and 2.0 KGy and heat treatment at 60 deg. C for 20 min to control mould growth. Mould growth was reladed at ambient temperature by 3, 4, 6 and 8 days after 0.5, 1.0, 1.5 and 2.0 KGy treatments, respectively, compared to 2 days in case of control sample and 3 days for heat treatment alone. Combination of heat with irradiation at 0.5, 1.0, 1.5 and 2.0 KGy retarded mould growth up to 4, 6, 7 an 9 days, respectively. Organoleptically, the irradiated bread slices were acceptable up to 3 to 6 days depending on the treatment. The combination method treated slices were acceptable up to 8 days. The application of radiation dose exceeding 2.0 KGy caused off flavour. Mild heat treatment and radiation in combination resulted in a synergistic antifungal effect and enhanced shelf-life of bread

Review of thermo-physical properties, wetting and heat transfer characteristics of nanofluids and their applicability in industrial quench heat treatment.

Science.gov (United States)

Ramesh, Gopalan; Prabhu, Narayan Kotekar

2011-04-14

The success of quenching process during industrial heat treatment mainly depends on the heat transfer characteristics of the quenching medium. In the case of quenching, the scope for redesigning the system or operational parameters for enhancing the heat transfer is very much limited and the emphasis should be on designing quench media with enhanced heat transfer characteristics. Recent studies on nanofluids have shown that these fluids offer improved wetting and heat transfer characteristics. Further water-based nanofluids are environment friendly as compared to mineral oil quench media. These potential advantages have led to the development of nanofluid-based quench media for heat treatment practices. In this article, thermo-physical properties, wetting and boiling heat transfer characteristics of nanofluids are reviewed and discussed. The unique thermal and heat transfer characteristics of nanofluids would be extremely useful for exploiting them as quench media for industrial heat treatment.

Review of thermo-physical properties, wetting and heat transfer characteristics of nanofluids and their applicability in industrial quench heat treatment

Directory of Open Access Journals (Sweden)

Ramesh Gopalan

2011-01-01

Full Text Available Abstract The success of quenching process during industrial heat treatment mainly depends on the heat transfer characteristics of the quenching medium. In the case of quenching, the scope for redesigning the system or operational parameters for enhancing the heat transfer is very much limited and the emphasis should be on designing quench media with enhanced heat transfer characteristics. Recent studies on nanofluids have shown that these fluids offer improved wetting and heat transfer characteristics. Further water-based nanofluids are environment friendly as compared to mineral oil quench media. These potential advantages have led to the development of nanofluid-based quench media for heat treatment practices. In this article, thermo-physical properties, wetting and boiling heat transfer characteristics of nanofluids are reviewed and discussed. The unique thermal and heat transfer characteristics of nanofluids would be extremely useful for exploiting them as quench media for industrial heat treatment.

Milk protein-gum tragacanth mixed gels: effect of heat-treatment sequence.

Science.gov (United States)

Hatami, Masoud; Nejatian, Mohammad; Mohammadifar, Mohammad Amin; Pourmand, Hanieh

2014-01-30

The aim of this study was to investigate the role of the heat-treatment sequence of biopolymer mixtures as a formulation parameter on the acid-induced gelation of tri-polymeric systems composed of sodium caseinate (Na-caseinate), whey protein concentrate (WPC), and gum tragacanth (GT). This was studied by applying four sequences of heat treatment: (A) co-heating all three biopolymers; (B) heating the milk-protein dispersion and the GT dispersion separately; (C) heating the dispersion containing Na-caseinate and GT together and heating whey protein alone; and (D) co-heating whey protein with GT and heating Na-caseinate alone. According to small-deformation rheological measurements, the strength of the mixed-gel network decreased in the order: C>B>D>A samples. SEM micrographs show that the network of sample C is much more homogenous, coarse and dense than sample A, while the networks of samples B and D are of intermediate density. The heat-treatment sequence of the biopolymer mixtures as a formulation parameter thus offers an opportunity to control the microstructure and rheological properties of mixed gels. Copyright © 2013 Elsevier Ltd. All rights reserved.

Heat Treatment of Gas-Atomized Powders for Cold Spray Deposition

Science.gov (United States)

Story, William A.; Brewer, Luke N.

2018-02-01

This communication demonstrates the efficacy of heat treatment on the improved deposition characteristics of aluminum alloy powders. A novel furnace was constructed for solutionizing of feedstock powders in an inert atmosphere while avoiding sintering. This furnace design achieved sufficiently high cooling rates to limit re-precipitation during powder cooling. Microscopy showed homogenization of the powder particle microstructures after heat treatment. Cold spray deposition efficiency with heat-treated powders substantially increased for the alloys AA2024, AA6061, and AA7075.

Calculation and Designing of Up-to-Date Gas-Flame Plants for Metal Heating and Heat Treatment

Directory of Open Access Journals (Sweden)

V. I. Тimoshpolsky

2008-01-01

Full Text Available An analysis of development trends in the CIS machine-building industry and current status of the heating and heat treatment furnaces of main machine-building enterprises of the Republic of Belarus as of the 1st quarter of 2008 is given in the paper.The paper presents the most efficient engineering solutions from technological and economic point of view that concern calculation and designing of up-to-date gas-flame plants which are to be applied for modernization of the current heating and heat treatment furnaces of the machine-building enterprises in the Republic of Belarus.A thermo-technical calculation of main indices of the up-to-date gas-flame plant has been carried out in the paper.

Study of heat treatment parameters for large-scale hydraulic steel gate track

Directory of Open Access Journals (Sweden)

Ping-zhou Cao

2013-10-01

Full Text Available In order to enhance external hardness and strength, a large-scale hydraulic gate track should go through heat treatment. The current design method of hydraulic gate wheels and tracks is based on Hertz contact linear elastic theory, and does not take into account the changes in mechanical properties of materials caused by heat treatment. In this study, the heat treatment parameters were designed and analyzed according to the bearing mechanisms of the wheel and track. The quenching process of the track was simulated by the ANSYS program, and the temperature variation, residual stress, and deformation were obtained and analyzed. The metallurgical structure field after heat treatment was predicted by the method based on time-temperature-transformation (TTT curves. The results show that the analysis method and designed track heat treatment process are feasible, and can provide a reference for practical projects.

Irradiation in combination of heat treatment of mango puree

International Nuclear Information System (INIS)

Noomhorm, A.; Apintanapong, M.

1996-01-01

The effect of irradiation with heat combination treatment on the shelf life and quality of mango puree was studied. Thermal inactivation of polyphenol oxidase enzyme at 80 degree C and 15 min. was used as a measure of adequacy of pre-heat treatment. Irradiation of mango puree after heat treatment at dosage of 0, 2, 4, 6 and 8 kGy showed no change in mc, pH, acidity, and TSS but during storage, growth of microorganisms brought changes in these values. Irradiation in combination with low temperature (5 degree C) reduced discoloration and darkening rate during storage. Irradiation dose from 0 to 8 kGy resulted in log linear reductions in microorganism levels but at 6 and 8 kGy, there was no growth of microorganisms. Products irradiated at 8 kGy showed no microorganism growth at both temperatures

Ultrasonic evaluation of heat treatment for stress relief in steel

International Nuclear Information System (INIS)

Bittencourt, Marcelo de S.Q.; Lamy, Carlos A.; Goncalves Filho, Orlando J.A.; Payao Filho, Joao da C.

2000-01-01

Residual stresses in materials arise due to the manufacturing processes. As a consequence, in the nuclear area some components must suffer a stress relief treatment according to strict criteria. Although these treatments are carefully carried on, concern with nuclear safety is constantly growing. This work proposes a nondestructive ultrasonic method to guarantee the efficiency of the heat treatment. It was used a short peened steel plate with tensile and compressive stresses which was submitted to a stress relief treatment. The results show that the proposed ultrasonic method could be used to confirm the efficiency of the stress relief heat treatment. (author)

Online Adaptive Hyperthermia Treatment Planning During Locoregional Heating to Suppress Treatment-Limiting Hot Spots.

Science.gov (United States)

Kok, H Petra; Korshuize-van Straten, Linda; Bakker, Akke; de Kroon-Oldenhof, Rianne; Geijsen, Elisabeth D; Stalpers, Lukas J A; Crezee, Johannes

2017-11-15

Adequate tumor temperatures during hyperthermia are essential for good clinical response, but excessive heating of normal tissue should be avoided. This makes locoregional heating using phased array systems technically challenging. Online application of hyperthermia treatment planning could help to improve the heating quality. The aim of this study was to evaluate the clinical benefit of online treatment planning during treatment of pelvic tumors heated with the AMC-8 locoregional hyperthermia system. For online adaptive hyperthermia treatment planning, a graphical user interface was developed. Electric fields were calculated in a preprocessing step using our in-house-developed finite-difference-based treatment planning system. This allows instant calculation of the temperature distribution for user-selected phase-amplitude settings during treatment and projection onto the patient's computed tomographic scan for online visualization. Online treatment planning was used for 14 treatment sessions in 8 patients to reduce the patients' reports of hot spots while maintaining the same level of tumor heating. The predicted decrease in hot spot temperature should be at least 0.5°C, and the tumor temperature should decrease less than 0.2°C. These predictions were compared with clinical data: patient feedback about the hot spot and temperature measurements in the tumor region. In total, 17 hot spot reports occurred during the 14 sessions, and the alternative settings predicted the hot spot temperature to decrease by at least 0.5°C, which was confirmed by the disappearance of all 17 hot spot reports. At the same time, the average tumor temperature was predicted to change on average -0.01°C (range, -0.19°C to 0.34°C). The measured tumor temperature change was on average only -0.02°C (range, -0.26°C to 0.31°C). In only 2 cases the temperature decrease was slightly larger than 0.2°C, but at most it was 0.26°C. Online application of hyperthermia treatment planning is

Desensitization of stainless steels by laser surface heat-treatment

Energy Technology Data Exchange (ETDEWEB)

Nakao, Yoshikuni; Nishimoto, Kazutoshi

1987-11-01

Laser heating was applied for the desensitization heat-treatment of the surface layer in the sensitized HAZ of Type 304 stainless steel. The degree of sensitization was examined by EPR technique and the 10 % oxalic acid electrolytic etch test. The CO/sub 2/ laser with maximum power of 1.5 kW was used for heat-treatment. Time-Temperature-Desensitization diagram (TTDS diagram) for sensitized Type 304 stainless steels were developed by calculation assuming the chromium diffusion control for desensitization which might occur when the chromium depleted zone was healed up due to dissolution of chromium carbide and chromium diffusion from the matrix being heated at the solution annealing temperatures. TTDS diagrams calculated agree fairly well with ones determined by corrosion tests. Laser irradiation conditions (e.g., Laser power, beam diameter and traveling velocity) required for desensitization of sensitized Type 304 stainless steels were calculated using additivity rule from the TTDS diagram calculated and theoretical thermal curve of laser heating derived from the heat conduction theory. After laser beam irradiated under an optimum condition predicted by calculation, the sensitized HAZ of Type 304 stainless steel restored complete resistance to intergranular corrosion.

Online Adaptive Hyperthermia Treatment Planning During Locoregional Heating to Suppress Treatment-Limiting Hot Spots

NARCIS (Netherlands)

Kok, H. Petra; Korshuize-van Straten, Linda; Bakker, Akke; de Kroon-Oldenhof, Rianne; Geijsen, Elisabeth D.; Stalpers, Lukas J. A.; Crezee, Johannes

2017-01-01

Adequate tumor temperatures during hyperthermia are essential for good clinical response, but excessive heating of normal tissue should be avoided. This makes locoregional heating using phased array systems technically challenging. Online application of hyperthermia treatment planning could help to

A Study of Ballast Water Treatment Using Engine Waste Heat

Science.gov (United States)

Balaji, Rajoo; Yaakob, Omar; Koh, Kho King; Adnan, Faizul Amri bin; Ismail, Nasrudin bin; Ahmad, Badruzzaman bin; Ismail, Mohd Arif bin

2018-05-01

Heat treatment of ballast water using engine waste heat can be an advantageous option complementing any proven technology. A treatment system was envisaged based on the ballast system of an existing, operational crude carrier. It was found that the available waste heat could raise the temperatures by 25 °C and voyage time requirements were found to be considerable between 7 and 12 days to heat the high volumes of ballast water. Further, a heat recovery of 14-33% of input energies from exhaust gases was recorded while using a test rig arrangement representing a shipboard arrangement. With laboratory level tests at temperature ranges of around 55-75 °C, almost complete species mortalities for representative phytoplankton, zooplankton and bacteria were observed while the time for exposure varied from 15 to 60 s. Based on the heat availability analyses for harvesting heat from the engine exhaust gases(vessel and test rig), heat exchanger designs were developed and optimized using Lagrangian method applying Bell-Delaware approaches. Heat exchanger designs were developed to suit test rig engines also. Based on these designs, heat exchanger and other equipment were procured and erected. The species' mortalities were tested in this mini-scale arrangement resembling the shipboard arrangement. The mortalities realized were > 95% with heat from jacket fresh water and exhaust gases alone. The viability of the system was thus validated.

Functional Properties of Glutinous Rice Flour by Dry-Heat Treatment.

Directory of Open Access Journals (Sweden)

Yang Qin

Full Text Available Glutinous rice flour (GRF and glutinous rice starch (GRS were modified by dry-heat treatment and their rheological, thermal properties and freeze-thaw stability were evaluated. Compared with the native GRF and GRS, the water-holding ability of modified GRF and GRS were enhanced. Both the onset and peak temperatures of the modified samples increased while the endothermic enthalpy change decreased significantly (p < 0.05. Meanwhile, dry heating remarkably increased the apparent viscosities of both GRF and GRS. Importantly, compared with GRS samples, the storage modulus (G' and loss modulus (G" values of modified GRF increased more greatly and the tanδ values decreased more remarkably, indicating that the dry-heat treatment showed more impact on the GRF and a higher viscoelasticity compared with GRS. Our results suggest the dry-heat treatment of GRF is a more effective method than that of GRS, which omits the complex and tedious process for purifying GRS, and thereby has more practical applications in the food industry.

Functional Properties of Glutinous Rice Flour by Dry-Heat Treatment.

Science.gov (United States)

Qin, Yang; Liu, Chengzhen; Jiang, Suisui; Cao, Jinmiao; Xiong, Liu; Sun, Qingjie

2016-01-01

Glutinous rice flour (GRF) and glutinous rice starch (GRS) were modified by dry-heat treatment and their rheological, thermal properties and freeze-thaw stability were evaluated. Compared with the native GRF and GRS, the water-holding ability of modified GRF and GRS were enhanced. Both the onset and peak temperatures of the modified samples increased while the endothermic enthalpy change decreased significantly (p < 0.05). Meanwhile, dry heating remarkably increased the apparent viscosities of both GRF and GRS. Importantly, compared with GRS samples, the storage modulus (G') and loss modulus (G") values of modified GRF increased more greatly and the tanδ values decreased more remarkably, indicating that the dry-heat treatment showed more impact on the GRF and a higher viscoelasticity compared with GRS. Our results suggest the dry-heat treatment of GRF is a more effective method than that of GRS, which omits the complex and tedious process for purifying GRS, and thereby has more practical applications in the food industry.

Simulation of Distortion and Residual Stress Development During Heat Treatment of Steel Castings

Energy Technology Data Exchange (ETDEWEB)

Beckermann, Christoph; Carlson, Kent

2011-07-22

Heat treatment and associated processing, such as quenching, are critical during high strength steel casting production. These processes must be managed closely to prevent thermal and residual stresses that may result in distortion, cracking (particularly after machining), re-work, and weld repair. The risk of casting distortion limits aggressive quenching that can be beneficial to the process and yield an improved outcome. As a result of these distortions, adjustments must be made to the casting or pattern design, or tie bars must be added. Straightening castings after heat treatments can be both time-consuming and expensive. Residual stresses may reduce a casting's overall service performance, possibly resulting in catastrophic failure. Stress relieving may help, but expends additional energy in the process. Casting software is very limited in predicting distortions during heat treatment, so corrective measures most often involve a tedious trial-and-error procedure. An extensive review of existing heat treatment residual stress and distortion modeling revealed that it is vital to predict the phase transformations and microstructure of the steel along with the thermal stress development during heat treatment. After reviewing the state-of-the-art in heat treatment residual stress and distortion modeling, an existing commercial code was selected because of its advanced capabilities in predicting phase transformations, the evolving microstructure and related properties along with thermal stress development during heat treatment. However, this software was developed for small parts created from forgings or machined stock, and not for steel castings. Therefore, its predictive capabilities for heat treatment of steel castings were investigated. Available experimental steel casting heat treatment data was determined to be of insufficient detail and breadth, and so new heat treatment experiments were designed and performed, casting and heat treating modified versions

Industrial heat treatment of R-HPDC A356 automotive brake callipers

CSIR Research Space (South Africa)

Chauke, L

2012-10-01

Full Text Available Heat treatment of rheo-high pressure die cast (R-HPDC) A356 brake callipers has produced good mechanical properties on the laboratory scale. An industrial heat treatment is required to evaluate the applicability and conformance of the R-HPDC A356...

THE INFLUENCE OF PRE-HEAT TREATMENT ON WHITE CAST IRONS PLASTICITY

Directory of Open Access Journals (Sweden)

T. M. Myronova

2013-11-01

Full Text Available Purpose. The development of heat treatment modes of white cast irons for structure changes in their eutectic constituent, namely in disturbing the monolithic structure of ledeburite colonies cementite structure and eutectic net continuity. Also the mentioned heat treatment modes are targeted to the eutectic net shift for the most suitable position from the point of plastic deforming. Methodology. The hypoeutectic white cast irons with 2.92…3.35 % carbon content and additionally alloyed by 3.18 % vanadium have been used as the research materials. The mentioned alloys have been pre-heat treated and hot twist tested. Findings. The research results showed that the carbide net breaking by plastic deforming leads to cast irons mechanical properties increasing but has difficulties in implementation due to the white cast irons low plasticity. The influence of different pre-heat treatment modes on structure and plasticity of white hypoeutectic cast irons have been investigated. They include the isotherm soaking under the different temperatures as well as multiply soakings and thermo-cycling. The influence of eutectic level, as well as pre heat treatment modes on different composition white cast irons hot plasticity have been investigated. Originality. It was determined that the heat treatment, which leads to double α→γ recrystallization under 860 – 950 °С and reperlitization under 720-680 °С results in significant increase of plasticity, as well as in un-alloyed and alloyed by vanadium white cast irons. It takes place due to carbide matrix phase separation in ledeburite colonies by new phase boundaries forming especially due to carbide transformations under vanadium alloying. Practical value. The implementation of pre-heat treatment with phase recrystallization resulted in hypoeutectic white cast irons plasticity increasing. The obtained level of cast iron plasticity corresponds to the one of carbide class steels, which ensures the successful

Improvement of high temperature fatigue lifetime in AZ91 magnesium alloy by heat treatment

International Nuclear Information System (INIS)

Mokhtarishirazabad, Mehdi; Azadi, Mohammad; Hossein Farrahi, Gholam; Winter, Gerhard; Eichlseder, Wilfred

2013-01-01

In the present paper, an improvement in high temperature fatigue properties of the AZ91 magnesium alloy with rare earth elements has been obtained by a typical heat treatment, denoted by T6. For this objective, out-of-phase thermo-mechanical fatigue, room temperature and high temperature low cycle fatigue tests are performed to compare lifetimes. Several rare earth elements are initially added to the AZ91 alloy during a gravity casting process in permanent molds. Also, the type of the heat treatment is examined. Results of specimens with only the solution (the T4 heat treatment) and the solution with the ageing process (the T6 heat treatment) are compared under isothermal fatigue loadings. Microstructural investigations are carried out, before and after fatigue experiments to demonstrate the heat treatment effect. Results showed that both low cycle fatigue and thermo-mechanical fatigue of the alloy at high temperatures increases tremendously after the T6 heat treatment. This behavior attributes to the variation of the ductility, which was a result of microstructural changes during the heat treatment and the varying temperature in fatigue tests

Improvement of high temperature fatigue lifetime in AZ91 magnesium alloy by heat treatment

Energy Technology Data Exchange (ETDEWEB)

Mokhtarishirazabad, Mehdi [School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran (Iran, Islamic Republic of); Azadi, Mohammad, E-mail: m_azadi@ip-co.com [Fatigue and Wear Workgroup, Irankhodro Powertrain Company (IPCO), Tehran (Iran, Islamic Republic of); Hossein Farrahi, Gholam [School of Mechanical Engineering, Sharif University of Technology, Tehran (Iran, Islamic Republic of); Winter, Gerhard; Eichlseder, Wilfred [Chair of Mechanical Engineering, University of Leoben, Leoben (Austria)

2013-12-20

In the present paper, an improvement in high temperature fatigue properties of the AZ91 magnesium alloy with rare earth elements has been obtained by a typical heat treatment, denoted by T6. For this objective, out-of-phase thermo-mechanical fatigue, room temperature and high temperature low cycle fatigue tests are performed to compare lifetimes. Several rare earth elements are initially added to the AZ91 alloy during a gravity casting process in permanent molds. Also, the type of the heat treatment is examined. Results of specimens with only the solution (the T4 heat treatment) and the solution with the ageing process (the T6 heat treatment) are compared under isothermal fatigue loadings. Microstructural investigations are carried out, before and after fatigue experiments to demonstrate the heat treatment effect. Results showed that both low cycle fatigue and thermo-mechanical fatigue of the alloy at high temperatures increases tremendously after the T6 heat treatment. This behavior attributes to the variation of the ductility, which was a result of microstructural changes during the heat treatment and the varying temperature in fatigue tests.

Gas injection to inhibit migration during an in situ heat treatment process

Science.gov (United States)

Kuhlman, Myron Ira; Vinegar; Harold J.; Baker, Ralph Sterman; Heron, Goren

2010-11-30

Methods of treating a subsurface formation are described herein. Methods for treating a subsurface treatment area in a formation may include introducing a fluid into the formation from a plurality of wells offset from a treatment area of an in situ heat treatment process to inhibit outward migration of formation fluid from the in situ heat treatment process.

Simulations of Precipitate Microstructure Evolution during Heat Treatment

Science.gov (United States)

Wu, Kaisheng; Sterner, Gustaf; Chen, Qing; Jou, Herng-Jeng; Jeppsson, Johan; Bratberg, Johan; Engström, Anders; Mason, Paul

Precipitation, a major solid state phase transformation during heat treatment processes, has for more than one century been intensively employed to improve the strength and toughness of various high performance alloys. Recently, sophisticated precipitation reaction models, in assistance with well-developed CALPHAD databases, provide an efficient and cost-effective way to tailor precipitate microstructures that maximize the strengthening effect via the optimization of alloy chemistries and heat treatment schedules. In this presentation, we focus on simulating precipitate microstructure evolution in Nickel-base superalloys under arbitrary heat treatment conditions. The newly-developed TC-PRISMA program has been used for these simulations, with models refined especially for non-isothermal conditions. The effect of different cooling profiles on the formation of multimodal microstructures has been thoroughly examined in order to understand the underlying thermodynamics and kinetics. Meanwhile, validations against several experimental results have been carried out. Practical issues that are critical to the accuracy and applicability of the current simulations, such as modifications that overcome mean-field approximations, compatibility between CALPHAD databases, selection of key parameters (particularly interfacial energy and nucleation site densities), etc., are also addressed.

Heat treatment trials for ITER toroidal field coils

International Nuclear Information System (INIS)

Matsui, Kunihiro; Hemmi, Tsutomu; Koizumi, Norikiyo; Nakajima, Hideo; Kimura, Satoshi; Nakamoto, Kazunari

2012-01-01

Cable-in-conduit (CIC) conductors using Nb 3 Sn strands are used in ITER toroidal fields (TF) coils. Heat treatment generates thermal strain in CIC conductors because of the difference in thermal expansion between the Nb 3 Sn strands and the stainless-steel jacket. The elongation/shrinkage of the TF conductor may make it impossible to insert a wound TF conductor into the groove of a radial plate. In addition, it is expected that the deformation of the winding due to heat treatment-based release of the residual force in the jacket may also make it impossible to insert the winding in the groove, and that correcting the winding geometry to allow insertion of the winding may influence the superconducting performance of the TF conductor. The authors performed several trials using heat treatment as the part of activities in Phase II of TF coil procurement aiming to resolve the above-mentioned technical issues, and evaluated the elongations of 0.064, 0.074 and 0.072% for the straight and curved conductors and 1/3-scale double-pancake (DP) winding, respectively. It was confirmed that correction if the deformed winding did not influence the superconducting performance of the conductor. (author)

Impact Toughness and Heat Treatment for Cast Aluminum

Science.gov (United States)

Lee, Jonathan A (Inventor)

2016-01-01

A method for transforming a cast component made of modified aluminum alloy by increasing the impact toughness coefficient using minimal heat and energy. The aluminum alloy is modified to contain 0.55%-0.60% magnesium, 0.10%-0.15% titanium or zirconium, less than 0.07% iron, a silicon-tomagnesium product ratio of 4.0, and less than 0.15% total impurities. The shortened heat treatment requires an initial heating at 1,000deg F. for up to I hour followed by a water quench and a second heating at 350deg F. to 390deg F. for up to I hour. An optional short bake paint cycle or powder coating process further increase.

Effect of heat treatment operations on the Rm tensile strength of silumins

Directory of Open Access Journals (Sweden)

J. Pezda

2010-10-01

Full Text Available Owing to good technological properties, low weight and good corrosion resistance, aluminum-silicon alloys are widely used as a material for cast machinery components. State of macro- and microstructure of a castings manufactured from Al-Si alloys, which is determined by a shape and distribution of hardening phases, segregation of alloying constituents and impurities, as well as distribution of porosity, create conditions to obtainment of proper mechanical properties. These properties can be improved through modification of the alloy and performed heat treatment operations. The paper presents effect of modification and heat treatment process on the Rm tensile strength of a selected silumins (EN AB-AlSi9Cu3(Fe, EN AB-AlSi12CuNiMg, EN AB-AlSi17Cu1Ni1Mg. Investigated alloys were put to treatments of refining and modification, and next to heat treatment. Temperature range of the heat treatment operations was determined on base of curves from the ATD method. Obtained results illustrate registered curves of melting and solidification from the ATD method and strength tests. On base of performed initial tests one determined parameters of the heat treatment process (temperature and duration of solutionig and ageing treatments enabling obtainment of improved Rm tensile strength of the investigated alloys.

A new paradigm for heat treatment of alloys

Energy Technology Data Exchange (ETDEWEB)

Ustinovshikov, Y., E-mail: ust@ftiudm.ru

2014-11-25

Highlights: • The sign of the ordering energy in alloys varies with the temperature. • Each temperature of heating leads to formation of its characteristic microstructure. • Quenching of alloys is a totally unnecessary and useless operation. - Abstract: The article considers the consequences in the field of heat treatment of alloys that could follow the introduction of the concept of phase transition ordering-phase separation into common use. By example of the Fe{sub 50}Cr{sub 50} alloy, industrial carbon tool steel and Ni{sub 88}Al{sub 12} alloy, it is shown that this transition occurs at a temperature, which is definite for each system, that the change of the sign of the chemical interaction between component atoms reverses the direction of diffusion fluxes in alloys, which affects changes in the type of microstructures. The discovery of this phase transition dramatically changes our understanding of the solid solution, changes the ideology of alloy heat treatment. It inevitably leads to the conclusion about the necessity of carrying out structural studies with the help of TEM in order to adjust the phase diagrams of the systems where this phase transition has been discovered. Conclusions have been made that quenching of alloys from the so-called region of the solid solution, which is usually performed before tempering (aging) is a completely unnecessary and useless operation, that the final structure of the alloy is formed during tempering (aging) no matter what the structure was before this heat treatment.

Study on Spheroidization and Related Heat Treatments of Medium Carbon Alloy Steels

Directory of Open Access Journals (Sweden)

Harisha S. R.

2018-01-01

Full Text Available The importance of medium carbon steels as engineering materials is reflected by the fact that out of the vast majority of engineering grade ferrous alloys available and used in the market today, a large proportion of them are from the family of medium carbon steels. Typically medium carbon steels have a carbon range of 0.25 to 0.65% by weight, and a manganese content ranging from 0.060 to 1.65% by weight. Medium carbon steels are more resistive to cutting, welding and forming as compared to low carbon steels. From the last two decades a number of research scholars reported the use of verity of heat treatments to tailor the properties of medium carbon steels. Spheroidizing is the novel industrial heat treatment employed to improve formability and machinability of medium/high carbon low alloy steels. This exclusive study covers procedure, the effects and possible outcomes of various heat treatments on medium carbon steels. In the present work, other related heat treatments like annealing and special treatments for property alterations which serve as pretreatments for spheroidizing are also reviewed. Medium carbon steels with property alterations by various heat treatment processes are finding increased responsiveness in transportation, aerospace, space, underwater along with other variegated fields. Improved tribological and mechanical properties consisting of impact resistance, stiffness, abrasion and strength are the main reasons for the increased attention of these steels in various industries. In the present scenario for the consolidation of important aspects of various heat treatments and effects on mechanical properties of medium carbons steel, a review of different research papers has been attempted. This review may be used as a guide to provide practical data for heat treatment industry, especially as a tool to enhance workability and tool life.

Grain Refinement of Low Carbon Martensitic Steel by Heat Treatment

Directory of Open Access Journals (Sweden)

N. V. Kolebina

2015-01-01

Full Text Available The low-carbon steels have good corrosion and technological properties. Hot deformation is the main operation in manufacturing the parts from these steels. So one of the important properties of the material is a property of plasticity. The grain size significantly influences on the ductility properties of steel. The grain size of steel depends on the chemical composition of the crystallization process, heat treatment, and steel machining. There are plenty methods to have grain refinement. However, taking into account the large size of the blanks for the hydro turbine parts, the thermal cycling is an advanced method of the grain refinement adaptable to streamlined production. This work experimentally studies the heat treatment influence on the microstructure of the low-carbon 01X13N04 alloy steel and proposes the optimal regime of the heat treatment to provide a significantly reduced grain size. L.M. Kleiner, N.P. Melnikov and I.N. Bogachyova’s works focused both on the microstructure of these steels and on the influence of its parameters on the mechanical properties. The paper focuses mainly on defining an optimal regime of the heat treatment for grain refinement. The phase composition of steel and temperature of phase transformation were defined by the theoretical analysis. The dilatometric experiment was done to determine the precise temperature of the phase transformations. The analysis and comparison of the experimental data with theoretical data and earlier studies have shown that the initial sample has residual stress and chemical heterogeneity. The influence of the heat treatment on the grain size was studied in detail. It is found that at temperatures above 950 ° C there is a high grain growth. It is determined that the optimal number of cycles is two. The postincreasing number of cycles does not cause further reducing grain size because of the accumulative recrystallization process. Based on the results obtained, the thermal cycling

Influence of heat treatment on magnesium alloys meant to automotive industry

NARCIS (Netherlands)

Popescu, G.; Moldovan, P.; Bojin, D.; Sillekens, W.H.

2009-01-01

The paper presents a study concerning the heat treatment realized on magnesium alloys, from AZ80 and ZK60 class. These alloys are destined to replace the conventional ferrous and aluminum alloys in automotive industry. It was realized the heat treatment, T5 - artificially aging, and it were

Heat treatment of a direct composite resin: influence on flexural strength

Directory of Open Access Journals (Sweden)

Caroline Lumi Miyazaki

2009-09-01

Full Text Available The purpose of this study was to evaluate the flexural strength of a direct composite, for indirect application, that received heat treatment, with or without investment. One indirect composite was used for comparison. For determination of the heat treatment temperature, thermogravimetric analysis (TGA and differential scanning calorimetry (DSC were performed, considering the initial weight loss temperature and glass transition temperature (Tg. Then, after photoactivation (600 mW/cm² - 40 s, the specimens (10 x 2 x 2 mm were heat-treated following these conditions: 170ºC for 5, 10 or 15 min, embedded or not embedded in investment. Flexural strength was assessed as a means to evaluate the influence of different heat treatment periods and investment embedding on mechanical properties. The data were analyzed by ANOVA and Tukey's test (α = 0.05. TGA showed an initial weight loss temperature of 180ºC and DSC showed a Tg value of 157°C. Heat treatment was conducted in an oven (Flli Manfredi, Italy, after 37°C storage for 48 h. Flexural strength was evaluated after 120 h at 37°C storage. The results showed that different periods and investment embedding presented similar statistical values. Nevertheless, the direct composite resin with treatments presented higher values (178.7 MPa compared to the indirect composite resin (146.0 MPa and the same direct composite submitted to photoactivation only (151.7 MPa. Within the limitations of this study, it could be concluded that the heat treatment increased the flexural strength of the direct composite studied, leading to higher mechanical strength compared to the indirect composite.

Evaluation of carbon diffusion in heat treatment of H13 tool steel under different atmospheric conditions

Directory of Open Access Journals (Sweden)

Maziar Ramezani

2015-04-01

Full Text Available Although the cost of the heat treatment process is only a minor portion of the total production cost, it is arguably the most important and crucial stage on the determination of material quality. In the study of the carbon diffusion in H13 steel during austenitization, a series of heat treatment experiments had been conducted under different atmospheric conditions and length of treatment. Four austenitization atmospheric conditions were studied, i.e., heat treatment without atmospheric control, heat treatment with stainless steel foil wrapping, pack carburization heat treatment and vacuum heat treatment. The results showed that stainless steel foil wrapping could restrict decarburization process, resulting in a constant hardness profile as vacuum heat treatment does. However, the tempering characteristic between these two heat treatment methods is different. Results from the gas nitrided samples showed that the thickness and the hardness of the nitrided layer is independent of the carbon content in H13 steel.

Effects of heat treatment temperature on morphology and properties of opal crystal

International Nuclear Information System (INIS)

Duan Tao; China Academy of Engineering Physics, Mianyang; Peng Tongjiang; Chen Jiming; Tang Yongjian

2008-01-01

The monodispersed SiO 2 microspheres were synthesized by reactant mixed equally. The colloid crystal templates were assemblied by vertical sedimentation method in ethanol at certain temperatures, and the effects of the heat treatment temperature on the morphology and the properties of opal colloid crystals were investigated. SEM, TCr-DSC results indicate SiO 2 colloid templates should be heat treated at 700-800 degree C, enhancing the conglutination and mechanistic intensity of opal templates. UV-Vis analysis result indicates that the heat treatment process can remove the photonic band gap location of the opal colloid crystals, and with the heat treatment temperature increasing gradually, blue shift occurs and the gap narrows. (authors)

Heat treatment effect on ductility of nickel-base alloys

International Nuclear Information System (INIS)

Burnakov, K.K.; Khasin, G.A.; Danilov, V.F.; Oshchepkov, B.V.; Listkova, A.I.

1979-01-01

Causes of low ductility of the KhN75MBTYu and KhN78T alloys were studied along with the heat treatment effects. Samples were tested at 20, 900, 1100, 1200 deg C. Large amount of inclusions was found in intercrystalline fractures of the above low-ductile alloys. The inclusions of two types took place: (α-Al 2 O 3 , FeO(Cr 2 O 3 xAl 2 O 3 )) dendrite-like ones and large-size laminated SiO 2 , FeO,(CrFe) 2 O 3 inclusions situated as separate colonies. Heat treatment of the alloys does not increase high-temperature impact strength and steel ductility. The heating above 1000 deg C leads to a partial dissolution and coagulation of film inclusions which results in an impact strength increase at room temperature

Heat Treatment of Cr- and Cr-V ledeburitic tool steels

Directory of Open Access Journals (Sweden)

Peter Jurči

2014-11-01

Full Text Available Cr- and Cr-V ledeburitic cold work tool steels belong to the most important tool materials for large series manufacturing. To enable high production stability, the tools must be heat treated before use. This overview paper brings a comprehensive study on the heat treatment of these materials, starting from the soft annealing and finishing with the tempering. Also, it describes the impact of any step of the heat treatment on the most important structural and mechanical characteristics, like the hardness, the toughness and the wear resistance. The widely used AIS D2- steel (conventionally manufactured and Vanadis 6 (PM are used as examples in most cases.

Dimensional Behavior of Matrix Graphite Compacts during Heat Treatments for HTGR Fuel Element Fabrication

International Nuclear Information System (INIS)

Lee, Young-Woo; Yeo, Seunghwan; Cho, Moon Sung

2015-01-01

The carbonization is a process step where the binder that is incorporated during the matrix graphite powder preparation step is evaporated and the residue of the binder is carbonized during the heat treatment at about 1073 K. This carbonization step is followed by the final high temperature heat treatment where the carbonized compacts are heat treated at 2073-2173 K in vacuum for a relatively short time (about 2 hrs). In order to develop a fuel compact fabrication technology, and for fuel matrix graphite to meet the required material properties, it is essential to investigate the relationship among the process parameters of the matrix graphite powder preparation, the fabrication parameters of fuel element green compact and the heat treatments conditions, which has a strong influence on the further steps and the material properties of fuel element. In this work, the dimensional changes of green compacts during the carbonization and final heat treatment are evaluated when compacts have different densities from different pressing conditions and different final heat treatment temperatures are employed, keeping other process parameters constant, such as the binder content, carbonization time, temperature and atmosphere (two hours ant 1073K and N2 atmosphere). In this work, the dimensional variations of green compacts during the carbonization and final heat treatment are evaluated when compacts have different densities from different pressing conditions and different final heat treatment temperatures are employed

Stone heat treatment in the Early Mesolithic of southwestern Germany: Interpretation and identification.

Directory of Open Access Journals (Sweden)

Patrick Schmidt

Full Text Available The Early Mesolithic of southwestern Germany, the so-called Beuronian (9600-7100 BC, is a period of important transformations in the way people lived, in their subsistence and in the stone tools they produced. One of the perhaps most spectacular re-inventions of that time is heat treatment of stones prior to their manufacture into tools. Although heat treatment has been understood as one of the defining characteristics of the Beuronian of southwestern Germany, and although its existence has been known for almost 30 years now, relatively few systematic studies on it are available. In this paper, we present such a study, aiming to shed light on two questions: (1 what technique and heating parameters were used in the Beuronian and (2 how reliable are the macroscopic proxies traditionally used to identify heat treatment in this context? We investigate these questions using a non-destructive archaeometric technique for measuring past heating temperatures of heat-treated stones and a quantitative surface roughness analysis aiming to understand the relations between surface aspect and heat treatment. These methods are applied to 46 Jurassic chert artefacts from the site Helga-Abri located in the Swabian Alb region of southwestern Germany. Our results document that an opportunistic low-investment procedure was used to heat stone, probably relying on the use of the above-ground part of regular camp-fires. We also found that the traditionally used macroscopic criteria, such as colour and surface gloss, cannot be unambiguously used to identify heat treatment in assemblages made from Jurassic chert. These findings have important implications for our understanding of the Beuronian lithic chaîne opératoire in terms of the investment in time and resources necessary, and for the refinement of archaeological techniques used to identify heat treatment in the Mesolithic of the Swabian Alb.

Stone heat treatment in the Early Mesolithic of southwestern Germany: Interpretation and identification.

Science.gov (United States)

Schmidt, Patrick; Spinelli Sanchez, Océane; Kind, Claus-Joachim

2017-01-01

The Early Mesolithic of southwestern Germany, the so-called Beuronian (9600-7100 BC), is a period of important transformations in the way people lived, in their subsistence and in the stone tools they produced. One of the perhaps most spectacular re-inventions of that time is heat treatment of stones prior to their manufacture into tools. Although heat treatment has been understood as one of the defining characteristics of the Beuronian of southwestern Germany, and although its existence has been known for almost 30 years now, relatively few systematic studies on it are available. In this paper, we present such a study, aiming to shed light on two questions: (1) what technique and heating parameters were used in the Beuronian and (2) how reliable are the macroscopic proxies traditionally used to identify heat treatment in this context? We investigate these questions using a non-destructive archaeometric technique for measuring past heating temperatures of heat-treated stones and a quantitative surface roughness analysis aiming to understand the relations between surface aspect and heat treatment. These methods are applied to 46 Jurassic chert artefacts from the site Helga-Abri located in the Swabian Alb region of southwestern Germany. Our results document that an opportunistic low-investment procedure was used to heat stone, probably relying on the use of the above-ground part of regular camp-fires. We also found that the traditionally used macroscopic criteria, such as colour and surface gloss, cannot be unambiguously used to identify heat treatment in assemblages made from Jurassic chert. These findings have important implications for our understanding of the Beuronian lithic chaîne opératoire in terms of the investment in time and resources necessary, and for the refinement of archaeological techniques used to identify heat treatment in the Mesolithic of the Swabian Alb.

Influence of Heat Treatments on Carotenoid Content of Cherry Tomatoes

OpenAIRE

D'Evoli, Laura; Lombardi-Boccia, Ginevra; Lucarini, Massimo

2013-01-01

Tomatoes and tomato products are rich sources of carotenoids—principally lycopene, followed by β-carotene and lutein. The aim of this work was to study the effect of heat treatment on carotenoid content in cherry tomatoes. Raw and canned products were sampled and analysed; furthermore whole, skin and pulp fractions of cherry tomatoes were analysed when raw and home-processed, in order to better understand heat treatment effects. Lycopene content in canned tomatoes was two-fold higher than in ...

Optimisation of the T6 heat treatment of rheocast alloy A356

CSIR Research Space (South Africa)

Moller, H

2007-11-01

Full Text Available popular solution heat treatment employed for SSM processed A356 is 6 hours at 540oC (i.e. similar to that used for permanent mould cast A356)6,7,9. Only limited work has been performed on the optimisation of the solution heat treatment of SSM processed... was not adequately studied by either Dewhirst8 or Rosso and Actis Grande5. The optimum artificial aging heat treatment proposed in both papers5,8 is 180oC for 4 hours. This was also confirmed in this work, but importantly, this applies only when natural aging...

Assembly for melting and heat treatment

International Nuclear Information System (INIS)

Blumenfeld, M.

1976-11-01

Laboratory scale production of alloys having a precise alloying materials content and the exact heat treatment of metallurgical specimens are discussed. The design and assembly of two relevant instruments are described. These instruments include a laboratory vacuum induction furnace and a specially designed glass lathe, that enables even an unskilled operator to encapsulate and seal metallurgical specimens in glass capsules. (author)

Experimental heat treatment of silcrete implies analogical reasoning in the Middle Stone Age.

Science.gov (United States)

Wadley, Lyn; Prinsloo, Linda C

2014-05-01

Siliceous rocks that were not heated to high temperatures during their geological formation display improved knapping qualities when they are subjected to controlled heating. Experimental heat treatment of South African silcrete, using open fires of the kind used during the Middle Stone Age, shows that the process needed careful management, notwithstanding recent arguments to the contrary. Silcrete blocks fractured when heated on the surface of open fires or on coal beds, but were heated without mishap when buried in sand below a fire. Three silcrete samples, a control, a block heated underground with maximum temperature between 400 and 500 °C and a block heated in an open fire with maximum temperature between 700 and 800 °C, were analysed with X-ray powder diffraction (XRD), X-ray fluorescence (XRF), optical microscopy, and both Fourier transform infrared (FTIR) and Raman spectroscopy. The results show that the volume expansion during the thermally induced α- to β-quartz phase transformation and the volume contraction during cooling play a major role in the heat treatment of silcrete. Rapid heating or cooling through the phase transformation at 573 °C will cause fracture of the silcrete. Successful heat treatment requires controlling surface fire temperatures in order to obtain the appropriate underground temperatures to stay below the quartz inversion temperature. Heat treatment of rocks is a transformative technology that requires skilled use of fire. This process involves analogical reasoning, which is an attribute of complex cognition. Copyright © 2014 Elsevier Ltd. All rights reserved.

Effect of heat treatment on the microstructure and properties of Ni based soft magnetic alloy.

Science.gov (United States)

Li, Chunhong; Ruan, Hui; Chen, Dengming; Li, Kejian; Guo, Donglin; Shao, Bin

2018-04-20

A Ni-based alloy was heat treated by changing the temperature and ambient atmosphere of the heat treatment. Morphology, crystal structure, and physical performance of the Ni-based alloy were characterized via SEM, XRD, TEM, and PPMS. Results show that due to the heat treatment process, the grain growth of the Ni-based alloy and the removal of impurities and defects are promoted. Both the orientation and stress caused by rolling are reduced. The permeability and saturation magnetization of the alloy are improved. The hysteresis loss and coercivity are decreased. Higher heat treatment temperature leads to increased improvement of permeability and saturation magnetization. Heat treatment in hydrogen is more conducive to the removal of impurities. At the same temperature, the magnetic performance of the heat-treated alloy in hydrogen is better than that of an alloy with heat treatment in vacuum. The Ni-based alloy shows an excellent magnetic performance on 1,373 K heat treatment in hydrogen atmosphere. In this process, the µ m , B s , P u , and H c of the obtained alloy are 427 mHm -1 , 509 mT, 0.866 Jm -3 , and 0.514 Am -1 , respectively. At the same time, the resistivity of alloy decreases and its thermal conductivity increases in response to heat treatment. © 2018 Wiley Periodicals, Inc.

Effects of heat treatment on some physical properties of Douglas fir (Pseudotsuga menziesii) wood

Science.gov (United States)

Xianjun Li; Zhiyong Cai; Qunying Mou; Yiqiang Wu; Yuan Liu

2011-01-01

In this study the effect of heat treatment on some physical properties of Douglas fir (Pseudotsuga menziesii) was investigated. Wood specimens were subjected to heat treatment at 160, 180, 200 and 220°C for 1, 2, 3 and 4h. The results show that heat treatment resulted in a darkened color, decreased moisture performance and increased dimensional stability of...

Effect of heat treatment changes on swelling treatment of coal; Sekitan no bojun shori sayo ni oyobosu netsushori henka no eikyo

Energy Technology Data Exchange (ETDEWEB)

Satsuka, T.; Mashimo, K.; Wainai, T. [Nihon University, Tokyo (Japan). College of Science and Technology

1996-10-28

Discussions were given on effects of heat treatment at relatively low temperatures as a pretreatment for coal liquefaction on coal swelling and hydrogenolysis reaction. Taiheiyo coal was heated to 200{degree}C for one hour as a pretreatment. The attempted heating methods consisted of four steps of rapid heating (6.7{degree}C/min)quenching (20{degree}C/min), rapid heating/natural cooling (0.7{degree}C/min), heating (1.0{degree}C/min)/quenching, and heating/natural cooling. The swelling treatment was composed of adding methanol benzene into heat treated coal, and leaving it at room temperature for 24 hours. The hydrogenolysis was carried out by using a tetralin solvent and at an initial hydrogen pressure of 20 kg/cm{sup 2} and a temperature of 350{degree}C and for a time of one hour. Hydrogenolysis conversion in the heat treated coal was found lower than that of the original coal because of generation of liquefaction inactive components due to thermal polymerization. When the heat treated coal is swollen by using the solvent, gas yield from the hydrogenolysis reaction decreased due to gas suppression effect, and the conversion was lower than that of the original coal. Heat treatment suggests densification of the coal structure. Swollen coal shows no conspicuous difference in the heat treatment methods against the hydrogenolysis due to the swelling effect. 3 refs., 5 figs., 1 tab.

A novel laboratory scale method for studying heat treatment of cake flour

OpenAIRE

Chesterton, AKS; Wilson, David Ian; Sadd, PI; Moggridge, Geoffrey Dillwyn

2014-01-01

A lab-scale method for replicating the time–temperature history experienced by cake flours undergoing heat treatment was developed based on a packed bed configuration. The performance of heat-treated flours was compared with untreated and commercially heat-treated flour by test baking a high ratio cake formulation. Both cake volume and AACC shape measures were optimal after 15 min treatment at 130 °C, though their values varied between harvests. Separate oscillatory rheometry tests of cake ba...

Influence of heat treatment on the microstructure and mechanical properties of Alloy 718 base metal and weldments

International Nuclear Information System (INIS)

Mills, W.J.

1979-06-01

Effect of heat treatment on the metallurgical structure and tensile properties of three heats of Alloy 718 base metal and an Alloy 718 GTA weldment were characterized. Heat treatments employed were the conventional (ASTM A637) precipitation treatment and a modified precipitation treatment designed to improve the toughness of the weldments. The GTA weldments were characterized in the as-welded condition. Light microscopy, thin foil, and surface replica electron microscopy revealed that the microstructure of this superalloy was sensitive to heat treatment and heat-to-heat variations. The modified aging treatment resulted in a larger grain size and a more homogeneous microstructure than the conventional treatments. The morphology of the primary strengthening γ phase was found to be finer and more closely spaced in the conventionally treated condition. Room and elevated temperature tensile testing revealed that the strength of the conventionally treated alloy was generally superior to that of the modified material. The conventional aging treatment resulted in greater heat-to-heat variations in tensile properties. This behavior was correlated with variations in the microstructure resulting from the precipitation heat treatments. The precipitate morphology of the GTA weldments was sensitive to heat treatment. The Laves phase was present in the interdendritic regions of both heat-treated welds. The modified aging treatment reduced the amount of Laves phase present in the weld zone. Room and elevated temperature tensile properties of the precipitation hardened weldments were relatively insensitive to heat treatment, suggesting that reduction in Laves phase from the weld zone had essentially no effect on tensile properties. As-welded GTA weldments exhibited lower strength levels and higher ductility values than heat-treated welds

A Study on Infrared Local Heat Treatment for AA5083 to Improve Formability and Automotive Part Forming

Science.gov (United States)

Lee, Eun-Ho; Yang, Dong-Yol; Ko, SeJin

2017-10-01

Automotive industries are increasingly employing aluminum alloys for auto parts to reduce vehicle weight. However, the low formability of aluminum alloys has been an obstacle to their application. To resolve the formability problem, some studies involving heat treatments under laboratory conditions have been reported. However, for industrial applications, the heat treatment sequence, heating energy efficiency, and a commercial part test should be studied. This work shows an infrared (IR) local heat treatment, heating only small areas where the heat treatment is required, for an aluminum alloy to improve the formability with a reduction of heating energy. The experiment shows that the formability drastically increases when the aluminum alloy is heat treated between two forming stages, referred to as intermediate heat treatment. The microstructures of the test pieces are evaluated to identify the cause of the increase in the formability. For an industrial application, an aluminum tailgate, which cannot be manufactured without heat treatment, was successfully manufactured by the IR local heat treatment with a reduction of energy. A simulation was also conducted with a stress-based forming limit diagram, which is not affected by the strain path and heat treatment histories. The simulation gives a good prediction of the formability improvement.

Effect of heat moisture treatment and annealing on physicochemical ...

African Journals Online (AJOL)

Red sorghum starch was physically modified by annealing and heat moisture treatment. The swelling power and solubility increased with increasing temperature range (60-90°), while annealing and heatmoisture treatment decreased swelling power and solubility of starch. Solubility and swelling were pH dependent with ...

Heat treatments of TiAl-Cr-V casting alloy

International Nuclear Information System (INIS)

Pu, Z.J.; Ma, J.L.; Wu, K.H.

1995-01-01

The need to investigate various kinds of fine microstructure based on casting TiAl alloy led to development of a multiple-stage heat treatment procedure. The first stage required the transformation of as-cast lamellar structure into near-gamma structure, followed by required transformation of near-gamma structure into various kinds of fine microstructure. The as-cast lamellar structure can be changed into near-gamma structure by annealing the alloy at 1,200 C for at least 50 hours. During the annealing process, two mechanisms are involved in transforming the lamellar structure into a near-gamma structure. One is the discontinuous coarsening (DC) process, and the other is the continuous coarsening (CC) process. With the near-gamma structure as an initial structure, the alloy being heat-treated in the γ + α and in the α fields can produce various kinds of microstructure with fine grain size. These microstructure significantly differ from the microstructure produced by heat-treating the deformed lamellar structure. Results of the investigation show that careful control of the time of the heat-treatment process in the single a field can produce a fine fully lamellar structure

Evaluation of heat treatment schedules for emerald ash borer (Coleoptera: Buprestidae).

Science.gov (United States)

Myers, Scott W; Fraser, Ivich; Mastro, Victor C

2009-12-01

The thermotolerance of the emerald ash borer, Agrilus planipennis Fairmaire (Coleoptera: Buprestidae), was evaluated by subjecting larvae and prepupae to a number of time-temperature regimes. Three independent experiments were conducted during 2006 and 2007 by heating emerald ash borer infested firewood in laboratory ovens. Heat treatments were established based on the internal wood temperature. Treatments ranged from 45 to 65 degrees C for 30 and 60 min, and the ability of larvae to pupate and emerge as adults was used to evaluate the success of each treatment. A fourth experiment was conducted to examine heat treatments on exposed prepupae removed from logs and subjected to ambient temperatures of 50, 55, and 60 degrees C for 15, 30, 45, and 60 min. Results from the firewood experiments were consistent in the first experiment. Emergence data showed emerald ash borer larvae were capable of surviving a temperatures-time combination up to 60 degrees C for 30 min in wood. The 65 degrees C for 30 min treatment was, however, effective in preventing emerald ash borer emergence on both dates. Conversely, in the second experiment using saturated steam heat, complete mortality was achieved at 50 and 55 degrees C for both 30 and 60 min. Results from the prepupae experiment showed emerald ash borer survivorship in temperature-time combinations up to 55 degrees C for 30 min, and at 50 degrees C for 60 min; 60 degrees C for 15 min and longer was effective in preventing pupation in exposed prepupae. Overall results suggest that emerald ash borer survival is variable depending on heating conditions, and an internal wood temperature of 60 degrees C for 60 min should be considered the minimum for safe treatment for firewood.

Heat treatment evaluation of steel ASTM A-131 grade A by X-Ray diffraction

Energy Technology Data Exchange (ETDEWEB)

Ferreira Junior, Francisco; Feio, Luciana Gaspar; Costa, Ednelson Silva; Rodrigues, Lino Alberto Soares; Braga, Eduardo Magalhaes, E-mail: juniorferrer93@gmail.com [Universidade Federal do Pará (UFPA), Belém, PA (Brazil)

2016-07-01

Full text: This study evaluates the residual stress of naval steel ASTM A-131 grade A before and after heat treatment. Residual stresses were determined by the technique of X-ray diffraction (XRD). Before heat treatment the residual stress measurements were made at 36 (thirty six) points distributed in a specimen with dimensions of 400 mm long, 200 mm wide and 95 mm thick, then the plate under analysis was brought to the oven for the implementation of heat treatment. To check the performance of the heat treatment, the plate was again subjected to XRD measurements of the same points previously measured in order to compare the residual stresses. As result, there was a reduction of residual stresses with the application of heat treatment. References: [1] COLPAERT, H. Metalografia dos Produtos Siderurgicos Comuns. 4 Edição. Editora Blucher. Saõ Paulo, SP, 2008. [2] HILL, R. Princípios de Metalurgia Física, 1992. (author)

Evaluation of the Characteristics of the Aluminum Alloy Casting Material by Heat Treatment

International Nuclear Information System (INIS)

Lee, Syung Yul; Park, Dong Hyun; Won, Jong Pil; Kim, Yun Hae; Lee, Myung Hoon; Moon, Kyung Man; Jeong, Jae Hyun

2012-01-01

Aluminum is on active metal, but it is well known that its oxide film plays a role as protective barrier which is comparatively stable in air and neutral aqueous solution. Thus, aluminum alloys have been widely applied in architectural trim, cold and hot-water storage vessels and piping etc., furthermore, the aluminum alloy of AC8A have been widely used in mold casting material of engine piston because of its properties of temperature and wear resistance. In recent years, the oil price is getting higher and higher, thus the using of low quality oil has been significantly increased in engines of ship and vehicle. Therefore it is considered that evaluation of corrosion resistance as well as wear resistance of AC8A material is also important to improve its property and prolong its lifetime. In this study, the effect of solution and tempering heat treatment to corrosion and wear resistance is investigated with electrochemical method and measurement of hardness. The hardness decreased with solution heat treatment compared to mold casting condition, but its value increased with tempering heat treatment and exhibited the highest value of hardness with tempering heat treatment temperature at 190 .deg. C for 24hrs. Furthermore, corrosion resistance increased with decreasing of the hardness, and decreased with increasing of the hardness reversely. As a result, it is suggested that the optimum heat treatment to improve both corrosion and wear resistance is tempering heat treatment temperature at 190 .deg. C for 16hrs

Improvement of stress-rupture life of GTD-111 by second solution heat treatment

International Nuclear Information System (INIS)

Yang, Caixiong; Xu, Yulai; Zhang, Zixing; Nie, Heng; Xiao, Xueshan; Jia, Guoqing; Shen, Zhi

2013-01-01

Highlights: ► The second solution heat treatment promoted the solution of γ–γ′ eutectic into γ matrix. ► The volume fraction of γ′ increases significantly after adding the second solution heat treatment. ► The improved stress-rupture life is primarily due to the increased volume fraction of γ′ phase. -- Abstract: An added second solution heat treatment was conducted to investigate its effects on the microstructures and stress-rupture properties of GTD-111. The microstructures were analyzed by scanning electron microscope after each step of heat treatments. The stress-rupture life of GTD-111 dramatically increases from about 180 to 288 h at 871 °C/310 MPa after adding a second solution heat treatment. The added second solution heat treatment promoted the solution of γ–γ′ eutectic into γ matrix, and facilitated the nucleation and precipitate of the secondary γ′ particles. The distribution of γ′ phase becomes much denser, the width of γ matrix channel is also reduced, and the volume fraction of γ′ phase significantly increases from about 29.3% to 44.2%. The improved stress-rupture life is primarily due to the increased volume fraction of γ′ phase. The carbides mainly consist of MC and a small amount of M 23 C 6 , which may prevent the dislocation moving and/or grain boundary sliding, and further improve the stress-rupture properties of GTD-111.

In situ post-weld heat treatment on martensitic stainless steel turbine runners using a robotic induction heating process to control temperature distribution

Science.gov (United States)

Boudreault, E.; Hazel, B.; Côté, J.; Godin, S.

2014-03-01

A new robotic heat treatment process is developed. Using this solution it is now possible to perform local heat treatment on large steel components. Crack, cavitation and erosion repairs on turbine blades and Pelton buckets are among the applications of this technique. The proof of concept is made on a 13Cr-4Ni stainless steel designated "CA6NM". This alloy is widely used in the power industry for modern system components. Given the very tight temperature tolerance (600 to 630 °C) for post-weld heat treatment on this alloy, 13Cr-4Ni stainless steel is very well suited for demonstrating the possibilities of this process. To achieve heat treatment requirements, an induction heating system is mounted on a compact manipulator named "Scompi". This robot moves a pancake coil in order to control the temperature distribution. A simulator using thermal finite element analysis is first used for path planning. A feedback loop adjusts parameters in function of environmental conditions.

In situ post-weld heat treatment on martensitic stainless steel turbine runners using a robotic induction heating process to control temperature distribution

International Nuclear Information System (INIS)

Boudreault, E; Hazel, B; Côté, J; Godin, S

2014-01-01

A new robotic heat treatment process is developed. Using this solution it is now possible to perform local heat treatment on large steel components. Crack, cavitation and erosion repairs on turbine blades and Pelton buckets are among the applications of this technique. The proof of concept is made on a 13Cr-4Ni stainless steel designated C A6NM . This alloy is widely used in the power industry for modern system components. Given the very tight temperature tolerance (600 to 630 °C) for post-weld heat treatment on this alloy, 13Cr-4Ni stainless steel is very well suited for demonstrating the possibilities of this process. To achieve heat treatment requirements, an induction heating system is mounted on a compact manipulator named S compi . This robot moves a pancake coil in order to control the temperature distribution. A simulator using thermal finite element analysis is first used for path planning. A feedback loop adjusts parameters in function of environmental conditions

Heat treatment of the EN AC-AlSi9Cu3(Fe alloy

Directory of Open Access Journals (Sweden)

J. Pezda

2010-04-01

Full Text Available Silumins are widely used in automotive, aviation and shipbuilding industries; as having specific gravity nearly three times lower than specific gravity of cast iron the silumins can be characterized by high mechanical properties. Additionally, they feature good casting properties, good machinability and good thermal conductivity. i.e. properties as required for machinery components operating in high temperatures and at considerable loads. Mechanical properties of the silumins can be upgraded, implementing suitably selected heat treatment. In the paper is presented an effect of modification and heat treatment processes on mechanical properties of the EN AC-AlSi9Cu3(Fe alloy. Investigated alloy has undergone typical processes of modification and refining, and next heat treatment. Temperature range of the heat treatment operations was determined on base of curves from the ATD method. Obtained results concern registered melting and solidification curves from the ATD method and strength tests. On base of the performed tests one has determined range of the heat treatment parameters which would assure obtainment of the best possible mechanical properties of the EN AC-AlSi9Cu3(Fe alloy.

Effect of alkali and heat treatments for bioactivity of TiO{sub 2} nanotubes

Energy Technology Data Exchange (ETDEWEB)

Kim, Seo young, E-mail: mast6269@nate.com [Dept. of Dental Biomaterials and Institute of Bio degradable material, Institute of Oral Bioscience and BK21 plus project, School of Dentistry, Chonbuk National University, Jeonju, 561-756 (Korea, Republic of); Kim, Yu kyoung, E-mail: yk0830@naver.com [Dept. of Dental Biomaterials and Institute of Bio degradable material, Institute of Oral Bioscience and BK21 plus project, School of Dentistry, Chonbuk National University, Jeonju, 561-756 (Korea, Republic of); Park, Il song, E-mail: ilsong@jbnu.ac.kr [Division of Advanced Materials Engineering, Research Center for Advanced Materials Development and Institute of Biodegradable Materials, Chonbuk National University, Jeonju 561-756 (Korea, Republic of); Jin, Guang chun, E-mail: jingc88@126.com [Oral Medical College, Beihua University, Jilin City 132013 (China); Bae, Tae sung, E-mail: bts@jbnu.ac.kr [Dept. of Dental Biomaterials and Institute of Bio degradable material, Institute of Oral Bioscience and BK21 plus project, School of Dentistry, Chonbuk National University, Jeonju, 561-756 (Korea, Republic of); Lee, Min ho, E-mail: mh@jbnu.ac.kr [Dept. of Dental Biomaterials and Institute of Bio degradable material, Institute of Oral Bioscience and BK21 plus project, School of Dentistry, Chonbuk National University, Jeonju, 561-756 (Korea, Republic of)

2014-12-01

Highlights: • TiO{sub 2} nanotubes formed via anodization were treated by alkali and heat. • The surface roughness was increased after alkali treatment (p < 0.05). • After alkali and heat treatment, the wettability was better than before treatment. • Alkali treated TiO{sub 2} nanotubes were shown higher HAp formation in SBF. • Heat treatment affected on the attachment of cells for alkali treated nanotubes. - Abstract: In this study, for improving the bioactivity of titanium used as an implant material, alkali and heat treatments were carried out after formation of the nanotubes via anodization. Nanotubes with uniform length, diameter, and thickness were formed by anodization. The alkali and heat-treated TiO{sub 2} nanotubes were covered with the complex network structure, and the Na compound was generated on the surface of the specimens. In addition, after 5 and 10 days of immersion in the SBF, the crystallized OCP and HAp phase was significantly increased on the surface of the alkali-treated TiO{sub 2} nanotubes (PNA) and alkali and heat-treated TiO{sub 2} nanotubes (PNAH) groups. Cell proliferation was decreased due to the formation of amorphous sodium titanate (Na{sub 2}TiO{sub 3}) layer on the surface of the PNA group. However, anatase and crystalline sodium titanate were formed on the surface of the PNAH group after heat treatment at 550 °C, and cell proliferation was improved. Thus, PNA group had higher HAp forming ability in the simulated body fluid. Additional heat treatment affected on enhancement of the bioactivity and the attachment of osteoblasts for PNA group.

EFFECT OF HEAT TREATMENT ON SOYBEAN PROTEIN SOLUBILITY

Directory of Open Access Journals (Sweden)

RODICA CĂPRIŢĂ

2007-05-01

Full Text Available The use of soybean products in animal feeds is limited due to the presence of antinutritional factors (ANF. Proper heat processing is required to destroy ANF naturally present in raw soybeans and to remove solvent remaining from the oil extraction process. Over and under toasting of soybean causes lower nutritional value. Excessive heat treatment causes Maillard reaction which affects the availability of lysine in particular and produces changes to the chemical structure of proteins resulting in a decrease of the nutritive value. The objective of this study was to evaluate the effect of heating time on the protein solubility. The investigation of the heating time on protein solubility in soybean meal (SBM revealed a negative correlation (r = -0.9596. Since the urease index is suitable only for detecting under processed SBM, the protein solubility is an important index for monitoring SBM quality.

Computerized property prediction and process planning in heat treatment of steels

Energy Technology Data Exchange (ETDEWEB)

Gergely, M. (Steel Advisory Centre for Industrial Technologies (SACIT), Budapest (Hungary)); Somogyi, S. (Steel Advisory Centre for Industrial Technologies (SACIT), Budapest (Hungary)); Kohlheb, R. (Steel Advisory Centre for Industrial Technologies (SACIT), Budapest (Hungary))

1994-01-01

Recent years have seen widespread interest in the establishment of prediction methods, based on phenomenological description and computer simulation of transformation processes during heat treatment, and in the introduction of software for technological planning. The steady development of this approach is aimed at meeting the requirement of metallurgists, design engineers dealing with material selection and dimensioning, and technologists planning heat treatment processes. Research in this field of computer simulation has been concentrated so far on two main areas of interest: . Modelling of transformation processes and the prediction of microstructures and/or properties, . Developing program packages to help solve concrete tasks such as material selection, on-line process control and monitoring, and the design of heat-treating operations. During the last two decades in the field of heat treatment, various mathematical models with different accuracy and complexity have been developed. In this paper, an attempt is made to outline some important results in computer simulation and computerized property prediction without aiming at completeness. The topic is restricted to quenched and tempered, and case-hardened steels. (orig.)

Suppression of outgassing from spindt-type cold-cathode by heat treatment

International Nuclear Information System (INIS)

Miyo, Yasuhiko; Ogiwara, Norio; Saidoh, Masahiro; Hayashi, Naoki; Turuta, Kouichi.

1995-01-01

In Spindt type cold cathode electron source (hereafter, referred to as FEA), field emission is used for extracting electrons. It was made clear that the FEA is an excellent electron source that never causes gas release by heating peripheral parts. But the gas release form the FEA was confirmed though it was slight accompanying the extraction of current. This gas release becomes a problem when pressure measurement is carried out by using the FEA in ultrahigh or extremely high vacuum. If the gas release occurs by the effect of the heat generation at the tip of an emitter accompanying the extraction of electron current, it is possible to reduce the gas release by carrying out the heat treatment of the FEA was attempted, and as the result, it was elucidated that by the heat treatment at 400degC, the gas release form the FEA was able to be suppressed. However, a new problem that the insulation between gate and emitter deteriorated and broke during the extraction of current occurred. The experimental method and the results of the reduction of gas release by heat treatment and the observation of the broken FEA with a scanning electron microscope are reported. Also the problem that in the FEA which was heat-treated at 400degC, the current has decreased from 500 μA to 100 μA in about 100 hours occurred. As to these problems, it is necessary to continue the experiment further. (K.I.)

Heat treatment of large-sized welded rotors of steam turbines for atomic power stations

Energy Technology Data Exchange (ETDEWEB)

Kutasov, R F; Mukhina, M P; Tustanovskii, A S

1977-01-01

The heat treatment of a welded rotor of grade 25Kh2NMFA steel for steam turbines of nuclear power plants was considered. A following heat treatment schedule was suggested: charging the rotor in to a furnace at 100-150 deg C, heating to 200-250 deg C and holding for 12 hrs; slow heating (10 deg C/h) to 400-450 deg C and holding for 12 hrs; slow heating to 630-640 deg C and holding for 50 hrs, cooling at a rate of 5 deg C/h down to 100 deg C, holding for 20 hrs and cooling with the furnace open. The proposed heat treatment schedule of a duration of 356 hrs ensures a temperature gradient throughout the cross section and the length of the rotor of not more than +-5 deg C, least deviations of geometric dimensions and makes possible machining finish to within 0-0.02 mm. Described are the particularities of the design of a roll-out hearth electric chamber furnace, measuring 13000x5500x5000 mm and built for the purpose of carrying out said heat treatment. The power rating of the furnace is 2850 kW.

Effects of Mead Wort Heat Treatment on the Mead Fermentation Process and Antioxidant Activity.

Science.gov (United States)

Czabaj, Sławomir; Kawa-Rygielska, Joanna; Kucharska, Alicja Z; Kliks, Jarosław

2017-05-14

The effects of mead wort heat treatment on the mead fermentation process and antioxidant activity were tested. The experiment was conducted with the use of two different honeys (multiflorous and honeydew) collected from the Lower Silesia region (Poland). Heat treatment was performed with the use of a traditional technique (gently boiling), the more commonly used pasteurization, and without heat treatment (control). During the experiment fermentation dynamics were monitored using high performance liquid chromatography with refractive index detection (HPLC-RID). Total antioxidant capacity (TAC) and total phenolic content (TPC) were estimated for worts and meads using UV/Vis spectrophotometric analysis. The formation of 5-hydroxymethylfurfural (HMF) was monitored by HPLC analyses. Heat treatment had a great impact on the final antioxidant capacity of meads.

Development of the heat treatment system for the 40 T hybrid magnet superconducting outsert.

Science.gov (United States)

Chen, W G; Chen, Z M; Chen, Z Y; Huang, P C; He, P; Zhu, J W

2011-10-01

The heat treatment of Nb(3)Sn coil with the glass fabric insulation is one of the key and critical processes for the outsert solenoids of the 40 T hybrid magnet, which could be wound with cable-in-conduit conductors using the insulation-wind-and-react technique. The manufacturing of the large vertical type vacuum/Ar atmosphere-protection heat treatment system has been completed and recently installed in the High Magnetic Filed Laboratory, Chinese Academy of Sciences. The heat treatment system composed mainly the furnace, the purging gas supply system, the control system, the gas impurities monitoring system, and so on. At present, the regulation and testing of the heat treatment system has been successfully finished, and all of technical parameters meet or exceed specifications.

Microstructure and mechanical properties of reactor pressure vessel mock-up material treated by intercritical heat treatment

International Nuclear Information System (INIS)

Kim, M. C.; Lee, B. S.; Hong, J. H.; Lee, H. J.; Park, S. D.; Kim, K. B.; Yoon, J. H.; Kim, J. S.; Oh, J. M.

2003-12-01

The mechanical properties and microstructures of base metal and weld HAZ (Heat-Affected Zone) of a Mn-Mo-Ni low alloy steels treated by intercritical heat treatment were investigated to evaluate effects of intercritical heat treatment on mechanical properties. In order to clarify the effects of intercritical heat treatment, two types of specimen were prepared by CHT(Conventional Heat Treatment) and IHT(CHT+Intercritical Heat Treatment). Tensile test, charpy impact test and vickers hardness test were carried out to evaluate the mechanical properties. It is found that impact toughness and hardness were improved by intercritical heat treatment. Mean size of precipitates and effective grain were quantitatively analysed as microstructural factors. It is found that precipitate size was decreased and shape of precipitate was spherodized by intercritical heat treatment and grain size was also decreased. So, it is thought that these microstructural changes cause the improvement of mechanical properties by intercritical heat treatment. The simulated specimen using a Gleeble thermal simulator system was used to evaluate the mechanical properties of HAZ. It is well known that IRHAZ and SRHAZ have lower toughness than base metal. However, in the case of IHT, impact toughness of IRHAZ and SRHAZ were slightly higher than that of base metal. It is obvious that this improvement of fracture toughness in IRHAZ and SRHAZ region was closely related to the microstructural changes, such as spheroidization of precipitate and decreases of precipitate size and grain size

THE HEAT TREATMENT ANALYSIS OF E110 CASE HARDENING STEEL

Directory of Open Access Journals (Sweden)

MAJID TOLOUEI-RAD

2016-03-01

Full Text Available This paper investigates mechanical and microstructural behaviour of E110 case hardening steel when subjected to different heat treatment processes including quenching, normalizing and tempering. After heat treatment samples were subjected to mechanical and metallographic analysis and the properties obtained from applying different processes were analysed. The heat treatment process had certain effects on the resultant properties and microstructures obtained for E110 steel which are described in details. Quenching produced a martensitic microstructure characterized by significant increase in material’s hardness and a significant decreased in its impact energy. Annealed specimens produced a coarse pearlitic microstructure with minimal variation in hardness and impact energy. For normalized samples, fine pearlitic microstructure was identified with a moderate increase in hardness and significant reduction in impact energy. Tempering had a significant effect on quenched specimens, with a substantial rise in material ductility and reduction of hardness with increasing tempering temperature. Furthermore, Results provide additional substantiation of temper embrittlement theory for low-carbon alloys, and indicate potential occurrence of temper embrittlement for fine pearlitic microstructures.

UV-Heat Treatments for the Control of Foodborne Microbial Pathogens in Chicken Broth

Directory of Open Access Journals (Sweden)

M. Gouma

2015-01-01

Full Text Available This investigation established the process criteria for using UV-C light and mild heat (UV-H treatment to inactivate 5-Log10 cycles (performance criterion of common foodborne pathogen populations, Escherichia coli, Salmonella Typhimurium, Listeria monocytogenes, and Staphylococcus aureus, when inoculated in chicken broth. To define the target microorganism and the proper UV-H treatment conditions (including UV dose, treatment time, and temperature that would achieve the stated performance criterion, mathematical equations based on Geeraerd’s model were developed for each microorganism. For the sake of comparison, inactivation equations for heat treatments were also performed on the same chicken broth and for the same microorganisms. L. monocytogenes was the most UV-H resistant microorganism at all temperatures, requiring a UV dose between 6.10 J/mL (5.6 min and 2.26 J/mL (2.09 min to achieve 5-Log10 reductions. In comparison with UV treatments at room temperatures, the combination of UV and mild heat allowed both the UV dose and treatment time to be reduced by 30% and 63% at 55°C and 60°C, respectively. Compared to heat treatments, the UV-H process reduced the heating time for 5-Log10 reductions of all the investigated microorganisms in chicken broth from 20-fold to 2-fold when the operating temperature varied from 53 to 60°C.

Study of critical dependence of stable phases in Nitinol on heat treatment using electrical resistivity probe

International Nuclear Information System (INIS)

Uchil, J.; Mohanchandra, K.P.; Kumara, K.G.; Mahesh, K.K.

1998-01-01

Phase transformations in 40% cold-worked Nitinol as a function of heat treatment have been studied using electrical resistivity variation with temperature. The stabilisation of austenitic, rhombohedral and martensitic phases is shown to critically depend on the temperatures of heat treatment by the analysis of temperature dependence of electrical resistivity in heating and cooling parts of the cycle. Characteristic values of electrical resistivity of the stable phases are determined. The R-phase has been found to form continuously with increasing heat-treatment temperature starting from room temperature and to suddenly disappear beyond heat-treatment at 683 K. The observed presence or absence of R-phase is confirmed by heat capacity measurements as a function of temperature. (orig.)

Modeling heat and mass transfer in the heat treatment step of yerba maté processing

Directory of Open Access Journals (Sweden)

J. M. Peralta

2007-03-01

Full Text Available The aim of this research was to estimate the leaf and twig temperature and moisture content of yerba maté branches (Ilex paraguariensis Saint Hilaire during heat treatment, carried out in a rotary kiln dryer. These variables had to be estimated (modeling the heat and mass transfer due to the difficulty of experimental measurement in the dryer. For modeling, the equipment was divided into two zones: the flame or heat treatment zone and the drying zone. The model developed fit well with the experimental data when water loss took place only in leaves. In the first zone, leaf temperature increased until it reached 135°C and then it slowly decreased to 88°C at the exit, despite the gas temperature, which varied in this zone from 460°C to 120°C. Twig temperature increased in the two zones from its inlet temperature (25°C up to 75°C. A model error of about 3% was estimated based on theoretical and experimental data on leaf moisture content.

Effects of Heat-treatments on the Mechanical Strength of Coated YSZ: An Experimental Assessment

DEFF Research Database (Denmark)

Toftegaard, Helmuth Langmaack; Sørensen, Bent F.; Linderoth, Søren

2009-01-01

The mechanical strength of thin, symmetric sandwich specimens consisting of a dense yttria-stabilized zirconia (YSZ) substrate coated with a porous NiO–YSZ layer at both major faces was investigated. Specimens were loaded in uniaxial tension to failure following heat treatments at various...... temperatures. In comparison with the YSZ material, the failure strength of coated specimens was found to increase for heat treatments at 1100°C, but decreased again with further increased heat-treatment temperatures....

Influence of Heat Treatment on Mercury Cavitation Resistance of Surface Hardened 316LN Stainless Steel

Energy Technology Data Exchange (ETDEWEB)

Pawel, Steven J [ORNL; Hsu, Julia [Massachusetts Institute of Technology (MIT)

2010-11-01

The cavitation-erosion resistance of carburized 316LN stainless steel was significantly degraded but not destroyed by heat treatment in the temperature range 500-800 C. The heat treatments caused rejection of some carbon from the carburized layer into an amorphous film that formed on each specimen surface. Further, the heat treatments encouraged carbide precipitation and reduced hardness within the carburized layer, but the overall change did not reduce surface hardness fully to the level of untreated material. Heat treatments as short as 10 min at 650 C substantially reduced cavitation-erosion resistance in mercury, while heat treatments at 500 and 800 C were found to be somewhat less detrimental. Overall, the results suggest that modest thermal excursions perhaps the result of a weld made at some distance to the carburized material or a brief stress relief treatment will not render the hardened layer completely ineffective but should be avoided to the greatest extent possible.

Uninterrupted heat-treatment of starch raw materials

Energy Technology Data Exchange (ETDEWEB)

Bronshtein, D Z

1958-01-01

A setup is presented, with a Rekord grinder, a Khronos scale, and other equipment of Soviet manufacture, in which oats, rye, wheat, and other grains are treated at 42 to 45 degrees prior to their use as raw materials in the ethanol industry. These materials are analyzed with respect to H/sub 2/O, starch, bulk, weight, screen analysis, and the final ethanol yields/ton of such raw materials. In a three year run in plant, this heat-treatment was advantageous, as compared to the former treatment of the starch materials.

Uninterrupted heat-treatment of starch raw materials

Energy Technology Data Exchange (ETDEWEB)

Bronshtein, D Z

1958-01-01

A setup is presented, with a Rekord grinder, a Khronos scale, and other equipment of Soviet manufacture, in which oats, rye, wheat, and other grains are treated at 42 to 45/sup 0/ prior to their use as raw materials in the ethanol industry. These materials are analyzed with respect to H/sub 2/O, starch, bulk weight, screen analysis, and the final ethanol yields/ton of such raw materials. In a three year run in a plant, this heat-treatment was advantageous, as compared to the former treatment of the starch materials.

The effect of heat treatment on phosphorus segregation in a submerged-arc weld metal

International Nuclear Information System (INIS)

Beere, W.B.; Buswell, J.T.

1999-01-01

Intergranular fracture (IGF) has been observed in carbon-manganese steels after irradiation or high temperature exposure for prolonged periods. The effect is associated with an increase in the ductile-brittle transition temperature and has been related to phosphorus diffusion to grain boundaries. Phosphorus also diffuses thermally at the temperatures used for post-weld heat treatments such that in principle, the slightly different heat treatments given to different parts of a large vessel could lead to differing grain boundary phosphorus coverage and hence susceptibility to IGF. The effect of typical heat treatments on phosphorus coverage has been investigated using a finite difference model based on a theory that has been fitted to a wide range of constant temperature data. Regardless of previous history, the grain boundary coverage of phosphorus was predicted to depend on the final anneal and cooling rate. These differed insufficiently in the typical heat treatments to produce significant differences in segregation. It was concluded that the ductile-brittle transition temperature in submerged-arc welds would be unaffected in vessels that had seen typical post-weld heat treatments

Synthesis of Mo5SiB2 based nanocomposites by mechanical alloying and subsequent heat treatment

International Nuclear Information System (INIS)

Abbasi, A.R.; Shamanian, M.

2011-01-01

Research highlights: → α-Mo-Mo 5 SiB 2 nanocomposite was produced after 20 h milling of Mo-Si-B powders. → Heat treatment of 5 h MAed powders led to the formation of boride phases. → Heat treatment of 10 h MAed powders led to the formation of Mo 5 SiB 2 phase. → By increasing heat treatment time, quantity of Mo 5 SiB 2 phase increased. → 5 h heat treatment of 20 h MAed powders led to the formation of Mo 5 SiB 2 -based composite. - Abstract: In this study, systematic investigations were conducted on the synthesis of Mo 5 SiB 2 -based alloy by mechanical alloying and subsequent heat treatment. In this regard, Mo-12.5 mol% Si-25 mol% B powder mixture was milled for different times. Then, the mechanically alloyed powders were heat treated at 1373 K for 1 h. The phase transitions and microstructural evolutions of powder particles during mechanical alloying and heat treatment were studied by X-ray diffractometry and scanning electron microscopy. The results showed that the phase evolutions during mechanical alloying and subsequent heat treatment are strongly dependent on milling time. After 10 h of milling, a Mo solid solution was formed, but, no intermetallic phases were detected at this stage. However, an α-Mo-Mo 5 SiB 2 nanocomposite was formed after 20 h of milling. After heat treatment of 5 h mechanically alloyed powders, small amounts of MoB and Mo 2 B were detected and α-Mo-MoB-Mo 2 B composite was produced. On the other hand, heat treatment of 10 h and 20 h mechanically alloyed powders led to the formation of an α-Mo-Mo 5 SiB 2 -MoSi 2 -Mo 3 Si composite. At this point, there is a critical milling time (10 h) for the formation of Mo 5 SiB 2 phase after heat treatment wherein below that time, boride phase and after that time, Mo 5 SiB 2 phase are formed. In the case of 20 h mechanically alloyed powders, by increasing heat treatment time, not only the quantity of α-Mo was reduced and the quantity of Mo 5 SiB 2 was increased, but also new boride

Effect of heat treatment upon the fatigue-crack growth behavior of Alloy 718 weldments

International Nuclear Information System (INIS)

James, L.A.; Mills, W.J.

1981-05-01

Gas-tungsten-arc weldments in Alloy 718 were studied in fatigue-crack growth test conducted at five temperatures over the range 24--649 degree C. In general, crack growth rates increased with increasing temperature, and weldments given the ''conventional'' post-weld heat-treatment generally exhibited crack growth rates that were higher than for weldments given the ''modified'' (INEL) heat-treatment. Limited testing in the as-welded condition revealed crack growth rates significantly lower than observed for the heat-treated cases, and this was attributed to residual stresses. Three different heats of filler wire were utilized, and no heat-to-heat variations were noted. 23 refs., 9 figs., 6 tabs

Effect of heat treatment temperature on microstructure

Indian Academy of Sciences (India)

The results of electrochemical performance measurements for the HCSs as anode material for lithium ion batteries indicate that the discharge capacity of the HCSs is improved after heat treatment at 800°C compared with the as-prepared HCSs and have a maximum value of 357 mAh/g and still retains 303 mAh/g after 40 ...

Numerical analysis of heat treatment of TiCN coated AA7075 aluminium alloy

Science.gov (United States)

Srinath, M. K.; Prasad, M. S. Ganesha

2018-04-01

The Numerical analysis of heat treatments of TiCN coated AA7075 aluminium alloys is presented in this paper. The Convection-Diffusion-Reaction (CDR) equation with solutions in the Streamlined-Upward Petrov-Galerkin (SUPG) method for different parameters is provided for the understanding of the process. An experimental process to improve the surface properties of AA-7075 aluminium alloy was attempted through the coatings of TiCN and subsequent heat treatments. From the experimental process, optimized temperature and time was obtained which gave the maximum surface hardness and corrosion resistance. The paper gives an understanding and use of the CDR equation for application of the process. Expression to determine convection, diffusion and reaction parameters are provided which is used to obtain the overall expression of the heat treatment process. With the substitution of the optimized temperature and time, the governing equation may be obtained. Additionally, the total energy consumed during the heat treatment process is also developed to give a mathematical formulation of the energy consumed.

Effect of heat treatment on the grooving corrosion resistance of ERW pipes

International Nuclear Information System (INIS)

Lee, Jong Kwon; Lee, Jae Young; Lim, Soo Hyun; Park, Ji Hwan; Seo, Bo Min; Kim, Seon Hwa

2002-01-01

The v-sharp grooving corrosion of ERW(electrical resistance welding) steel pipes limited their wide application in the industry in spite of their high productivity and efficiency. The grooving corrosion is caused mainly by the different microstructures between the matrix and weld that is formed during the rapid heating and cooling cycle in welding. By this localized corrosion reaction of pipes, it evolves economic problems such as the early damage of industrial facilities and pipe lines of apartment, and water pollution. Even though the diminishing of sulfur content is most effective to decrease the susceptibility of grooving corrosion, it requires costly process. In this study, improvement of grooving corrosion resistance was pursuited by post weld heat treatment in the temperature range between 650 .deg. C and 950 .deg. C. Also, the effect of heat input in the welding was investigated. By employing chromnoamperometry and potentiodynamic experiment, the corrosion rate and grooving corrosion index(α) were obtained. It was found that heat treatment could improve the grooving corrosion resistance. Among them, the heat treated at 900 .deg. C and 950 .deg. C had excellent grooving corrosion resistance. The index of heat treated specimen at 900 .deg. C and 950 .deg. C were 1.0, 1.2, respectively, which are almost immune to the grooving corrosion. Potential difference after the heat treatment, between base and weld metal was decreased considerably. While the as-received one measured 61∼71 mV, that of the 900 .deg. C heat treated steel pipe measured only 10mV. The results were explained and discussed

THE EFFECT OF HEAT TREATMENT ON THE DURABILITY OF BAMBOO Gigantochloa scortechinii

Directory of Open Access Journals (Sweden)

Norashikin Kamarudin

2012-07-01

Full Text Available Bamboo signifies as one of the fastest growing plants and it can be used for various products. In tropical countries such as Indonesia and Malaysia, bamboo is abundantly available at reasonable prices, therefore it is used for numerous purposes. However, as lignocellulosic material, bamboo is susceptible to fungal and insect attacks. Heat treatment is an option to improve bamboo's durability. The objective of this study was to improve the durability of bamboo using hot oil palm treatment. A Malaysian grown bamboo species, Buluh Semantan (Gigantochloa scortechinii, as a study material was soaked in hot oil palm for various temperatures and soaking time, before being inoculated with the basidiomycete Coriolus versicolor in an agar block test. The results demonstrated that the longer the heating time, the more improved the durability of bamboo. Altering the temperature in the palm oil treatment produced varying results. Bamboo blocks that heated in hot oil palm at 100°C for 60 minutes shows considerably less weight eduction that indicates less fungal attack. Overall, the higher the temperature, the better the durability of bamboo. Please indicates what the meaning of heat treatment in this experiment, it is not clear.

Reactions of lactose during heat treatment of milk : a quantitative study

NARCIS (Netherlands)

Berg, H.E.

1993-01-01

The kinetics of the chemical reactions of lactose during heat treatment of milk were studied. Skim milk and model solutions resembling milk were heated. Reaction products were determined and the influence of varying lactose, casein and fat concentration on the formation of these products

Investigation of heat treatment conditions of structural material for blanket fabrication process

International Nuclear Information System (INIS)

Hirose, Takanori; Suzuki, Satoshi; Akiba, Masato; Shiba, Kiyoyuki; Sawai, Tomotsugu; Jitsukawa, Shiro

2004-01-01

This paper presents recent results of thermal hysteresis effects on ceramic breeder blanket structural material. Reduced activation ferritic/martensitic (RAF) steel is the leading candidates for the first wall structural materials of breeding blankets. RAF steel demonstrates superior resistance to high dose neutron irradiation, because the steel has tempered martensite structure which contains the number of sink site for radiation defects. This microstructure obtained by two-step heat treatment, first is normalizing at temperature above 1200 K and the second is tempering at temperature below 1100 K. Recent study revealed the thermal hysteresis has significant impacts on the post-irradiation mechanical properties. The breeding blanket has complicated structure, which consists of tungsten armor and thin first wall with cooling pipe. The blanket fabrication requires some high temperature joining processes. Especially hot isostatic pressing (HIP) is examined as a near-net-shape fabrication process for this structure. The process consists of heating above 1300 K and isostatic pressing at the pressure above 150 MPa followed by tempering. Moreover ceramics pebbles are packed into blanket module and the module is to be seamed by welding followed by post weld heat treatment in the final assemble process. Therefore the final microstructural features of RAFs strongly depend on the blanket fabrication process. The objective of this work is to evaluate the effects of thermal hysteresis corresponding to blanket fabrication process on RAFs microstructure in order to establish appropriate blanket fabrication process. Japanese RAFs F82H (Fe-0.1C-8Cr-2W-0.2V-0.05Ta) was investigated by metallurgical method after isochronal heat treatment up to 1473 K simulating high temperature bonding process. Although F82H showed significant grain growth after conventional solid HIP conditions (1313 K x 2 hr.), this coarse grained microstructure was refined by the post HIP normalizing at

THE EFFECTS OF INTERCRITICAL HEAT TREATMENTS ON THE ...

African Journals Online (AJOL)

Effect of intercritical heat treatment on 0.14wt%C 0.56wt%Mn 0.13wt%Si struc- ... Table 1: Chemical composition of the steel used (wt. %) with its critical temperature (calculated). C. Mn. Si. Ni. S ... primary austenitic grain size hardening and.

Effect of Cold Drawing and Heat Treatment on the Microstructure of Invar36 Alloy Wire

International Nuclear Information System (INIS)

Han, Seung Youb; Jang, Seon Ah; Eun, Hee-Chul; Choi, Jung-Hoon; Lee, Ki Rak; Park, Hwan Seo; Ahn, Do-Hee; Kim, Soo Young; Kim, Jea Youl; Shin, Sang Yong

2016-01-01

In this study, the effect of cold drawing and heat treatment on the microstructure of Invar36 alloy wire was investigated. Invar36 alloy wire is used as a transmission line core material, and is required to have high strength. The diameter of the Invar36 alloy wire specimens were reduced from 16 mm to 4.3 mm after three cold drawing and two heat treatment processes, thereby increasing tensile strength. Specimens were taken after each of the cold drawing and heat treatment processes, and their microstructure and tensile properties were analyzed. The Invar36 alloy wire had a γ-(Fe, Ni) phase matrix before the cold drawing and heat treatment processes. After the cold drawing processes, {220} and {200} textures were mainly achieved. After the heat treatment processes, a {200} recrystallization γ-(Fe, Ni) phase was formed with fine carbides. The recrystallization γ-(Fe, Ni) phase grains had low dislocation density, so they probably accommodated a large amount of deformation during the cold drawing processes.

Effect of Cold Drawing and Heat Treatment on the Microstructure of Invar36 Alloy Wire

Energy Technology Data Exchange (ETDEWEB)

Han, Seung Youb; Jang, Seon Ah; Eun, Hee-Chul; Choi, Jung-Hoon; Lee, Ki Rak; Park, Hwan Seo; Ahn, Do-Hee [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Kim, Soo Young; Kim, Jea Youl [RandD Center, KOS Ltd., Yangsan (Korea, Republic of); Shin, Sang Yong [University of Ulsan, Ulsan (Korea, Republic of)

2016-10-15

In this study, the effect of cold drawing and heat treatment on the microstructure of Invar36 alloy wire was investigated. Invar36 alloy wire is used as a transmission line core material, and is required to have high strength. The diameter of the Invar36 alloy wire specimens were reduced from 16 mm to 4.3 mm after three cold drawing and two heat treatment processes, thereby increasing tensile strength. Specimens were taken after each of the cold drawing and heat treatment processes, and their microstructure and tensile properties were analyzed. The Invar36 alloy wire had a γ-(Fe, Ni) phase matrix before the cold drawing and heat treatment processes. After the cold drawing processes, {220} and {200} textures were mainly achieved. After the heat treatment processes, a {200} recrystallization γ-(Fe, Ni) phase was formed with fine carbides. The recrystallization γ-(Fe, Ni) phase grains had low dislocation density, so they probably accommodated a large amount of deformation during the cold drawing processes.

Effect of grinding and heat treatment on the mechanical behavior of zirconia ceramic

Directory of Open Access Journals (Sweden)

Gabriela Freitas RAMOS

2016-01-01

Full Text Available Abstract The present study investigated the effect of grinding on roughness, flexural strength, and reliability of a zirconia ceramic before and after heat treatment. Seven groups were tested (n = 15: a control group (labeled CG, untreated, and six groups of samples ground with diamond discs, simulating diamond burs, with grits of 200 µm (G80; 160 µm (G120, and 25 µm (G600, either untreated or heat-treated at 1200°C for 2 h (labeled A. Yttria tetragonal zirconia polycrystal discs were manufactured, ground, and submitted to roughness and crystalline phase analyses before the biaxial flexural strength test. There was no correlation between roughness (Ra and Rz and flexural strength. The reliability of the materials was not affected by grinding or heat treatment, but the characteristic strength was higher after abrasion with diamond discs, irrespective of grit size. The X-ray diffraction data showed that grinding leads to a higher monoclinic (m phase content, whereas heat treatment produces reverse transformation, leading to a fraction of m-phase in ground samples similar to that observed in the control group. However, after heat treatment, only the G80A samples presented strength similar to that of the control group, while the other groups showed higher strength values. When zirconia pieces must be adjusted for clinical use, a smoother surface can be obtained by employing finer-grit diamond burs. Moreover, when the amount of monoclinic phase is related to the degradation of zirconia, the laboratory heat treatment of ground pieces is indicated for the reverse transformation of zirconia crystals.

Effect of Pressure and Heat Treatments on the Compressive Strength of Reactive Powder Concrete

Directory of Open Access Journals (Sweden)

Helmi Masdar

2018-01-01

Full Text Available This paper presents the corresponding compressive strength of RPC with variable pressure combined with heating rate, heating duration, and starting time of heating. The treatments applied were 8 MPa static pressure on fresh RPC prims and heat curing at 240 °C in an oven. The compressive strength test was conducted at 7-d and 28-d. The images of RPC morphology were captured on the surface of a fractured specimen using Scanning Electron Microscopy in Secondary Electron detector mode to describe pore filing mechanism after treatments. The results show that a heating rate at 50 °C/hr resulted in the highest compressive strength about 40 % more than those at 10 or 100 °C/hr. A heating duration of 48 hours led to the maximum compressive strength. Heat curing applied 2 days after casting resulted in the maximum compressive. Heat curing had a signicant effect on the compresssive strength due to the acceleration of both reactions (hydration and pozzolanic and the degree of transformation from tobermorite to xonotlite. It is concluded that the optimum condition of treatments is both pressure and heat curing at 2-day after casting with a rate of 50 °C/hr for 48 hours.

Effect of heat treatment regime on structural lamination in ferritic-austenitic steels

International Nuclear Information System (INIS)

Sizov, R.A.; Zakharova, M.I.; Novikov, I.I.; Bannykh, O.A.

1983-01-01

The effect of preliminary thermal treatment on lamination and viscosity of EhP-53 and KO-3 steels after durable aging at the temperature of 350 is studied. It is shown that preliminary heat treatment considerably affects lamination processes in the result of aging of 0Kh18G8N2T steel. The lowest rate of lamination and higher impact strength after aging at 350 deg C for 4500 hours corresponds to the following heat treatment: 10 hour aging at 650 deg C with cooling in the air, then quenching in water from 950 deg C after aging for 30 min and the following tempering (650 deg C, 5 hours). Unlike the 0Kh18G8N2T steel, lamination parameters of steel 0Kh22N6T practically do not change after the application of heat treatment. Nevertherless, taking into account results of impact strength, it is advisable to have thermal treatment according to the regime: quenching in water at 950 deg C after aging for 30 min

Effect of Heat Treatment on the Lycopene Content of Tomato Puree ...

African Journals Online (AJOL)

Effect of Heat Treatment on the Lycopene Content of Tomato Puree. MI Mohammed, DI Malami. Abstract. Lycopene is a powerful antioxidant. Epidemiological studies have associated its consumption with numerous health benefits. In this study the effects of heating on lycopene were investigated by exposing tomato ...

Effect of heat treatment duration on tribological behavior of electroless Ni-(high)P coatings

Science.gov (United States)

Biswas, A.; Das, S. K.; Sahoo, P.

2016-09-01

Electroless nickel coating occurs through an autocatalytic chemical reaction and without the aid of electricity. From tribological perspective, it is recommended due to its high hardness, wear resistance, lubricity and corrosion resistance properties. In this paper electroless Ni-P coatings with high phosphorous weight percentages are developed on mild steel (AISI 1040) substrates. The coatings are subjected to heat treatment at 300°C and 500°C for time durations up to 4 hours. The effect of heat treatment duration on the hardness as well as tribological properties is discussed in detail. Hardness is measured in a micro hardness tester while the tribological tests are carried out on a pin-on-disc tribotester. Wear is reported in the form of wear rates of the sample subjected to the test. As expected, heat treatment of electroless Ni-P coating results in enhancement in its hardness which in turn increases its wear resistance. The present study also finds that duration of heat treatment has quite an effect on the properties of the coating. Increase in heat treatment time in general results in increase in the hardness of the coating. Coefficient of friction is also found to be lesser for the samples heat treated for longer durations (4 hour). However, in case of wear, similar trend is not observed. Instead samples heat treated for 2 to 3 hour display better wear resistance compared to the same heat treated for 4 hour duration. The microstructure of the coating is also carried out to ensure about its proper development. From scanning electron microscopy (SEM), the coating is found to possess the conventional nodular structure while energy dispersive X-ray analysis (EDX) shows that the phosphorous content in the coating to be greater than 9%. This means that the current coating belongs to the high phosphorous category. From X-ray diffraction analysis (XRD), it is found that coating is amorphous in as-deposited condition but transforms into a crystalline structure with

Flexible and stable heat energy recovery from municipal wastewater treatment plants using a fixed-inverter hybrid heat pump system

International Nuclear Information System (INIS)

Chae, Kyu-Jung; Ren, Xianghao

2016-01-01

Highlights: • Specially designed fixed-inverter hybrid heat pump system was developed. • Hybrid operation performed better at part loads than single inverter operation. • The applied heat pump can work stably over a wide range of heat load variations. • Heat energy potential of treated effluent was better than influent. • The heat pump’s COP from the field test was 4.06 for heating and 3.64 for cooling. - Abstract: Among many options to improve energy self-sufficiency in sewage treatment plants, heat extraction using a heat pump holds great promise, since wastewater contains considerable amounts of thermal energy. The actual heat energy demand at municipal wastewater treatment plants (WWTPs) varies widely with time; however, the heat pumps typically installed in WWTPs are of the on/off controlled fixed-speed type, thus mostly run intermittently at severe part-load conditions with poor efficiency. To solve this mismatch, a specially designed, fixed-inverter hybrid heat pump system incorporating a fixed-speed compressor and an inverter-driven, variable-speed compressor was developed and tested in a real WWTP. In this hybrid configuration, to improve load response and energy efficiency, the base-heat load was covered by the fixed-speed compressor consuming relatively less energy than the variable-speed type at nominal power, and the remaining varying load was handled by the inverter compressor which exhibits a high load-match function while consuming relatively greater energy. The heat pump system developed reliably extracted heat from the treated effluent as a heat source for heating and cooling purposes throughout the year, and actively responded to the load changes with a high measured coefficient of performance (COP) of 4.06 for heating and 3.64 for cooling. Moreover, this hybrid operation yielded a performance up to 15.04% better on part loads than the single inverter operation, suggesting its effectiveness for improving annual energy saving when

Effect of heat treatment on antimycotic activity of Sahara honey

Directory of Open Access Journals (Sweden)

Moussa Ahmed

2014-11-01

Full Text Available Objective: To evaluate the influence of the temperature on honey colour, polyphenol contents and antimycotic capacity and to evaluate the correlation between these parameters. Methods: Sahara honey were heated up to 25, 50, 75 and 100 °C for 15, 30 and 60 min, and their colour intensity, polyphenol contents and antimycotic capacity. The Folin-Ciocalteu test was used to determine the total polyphenol contents (TPC. The antimycotic activity was evaluated both by agar diffusion method and micro wells dilution method against the Candida albicans (C. albicans and Candida glabrata (C. glabrata. Results: Initial values for TPC in Sahara honey ranged from 0.55 to 1.14 mg of gallic acid per kg of honey, with the average value of 0.78 mg of gallic acid per kg of honey. The TPC values after heat-treatment were 0.54 to 1.54 with the average value of 1.49 mg. The minimal inhibitory concentrations before heat-treatment of Sahara honey against C. albicans and C. glabrata ranged from 3.06%-12.5% and 50% respectively. After heat-treatment the minimal inhibitory concentrations between 12.5% and 50% for C. albicans and C. glabrata, respectively. The diameters of inhibition zones of Sahara honey with 50% concentration varied from (12.67-15.00 mm by C. albicans to (14.33-15.67 mm by C. glabrata. The diameters of inhibition zones after heat-treatment at 25 and 50 °C for 15.30 and 60 min ranged from (2.00-18.67 mm by C. albicans to (8.00-16.67 mm by C. glabrata. Statistically significant relations between the TPC and the colour intensity of Sahara honey (r=0.99, P<0.05. Furthermore, the results showed that the TPC and colour is not correlated with the antimycotic capacity. Conclusions: To our knowledge this is the first report on the antimycotic capacity of Sahara honey.

Effect of heat treatment duration on phase separation of sodium borosilicate glass, containing copper

International Nuclear Information System (INIS)

Shejnina, T.G.; Gutner, S.Kh.; Anan'in, N.I.

1989-01-01

The effect of heat treatment duration on phase separation of sodium borosilicate (SBS) glass, containing copper is studied. It is stated that phase separation close to equilibrium one is attained under 12 hours of heat treatment of SBS glass containing copper

The Effect of Heat Treatments and Coatings on the Outgassing Rate of Stainless Steel Chambers

Energy Technology Data Exchange (ETDEWEB)

Mamum, Md Abdullah A. [Old Dominion Univ., Norfolk, VA (United States); Elmustafa, Abdelmageed A, [Old Dominion Univ., Norfolk, VA (United States); Stutzman, Marcy L. [JLAB, Newport News, VA (United States); Adderley, Philip A. [JLAB, Newport News, VA (United States); Poelker, Matthew [JLAB, Newport News, VA (United States)

2014-03-01

The outgassing rates of four nominally identical 304L stainless steel vacuum chambers were measured to determine the effect of chamber coatings and heat treatments. One chamber was coated with titanium nitride (TiN) and one with amorphous silicon (a-Si) immediately following fabrication. One chamber remained uncoated throughout, and the last chamber was first tested without any coating, and then coated with a-Si following a series of heat treatments. The outgassing rate of each chamber was measured at room temperatures between 15 and 30 deg C following bakes at temperatures between 90 and 400 deg C. Measurements for bare steel showed a significant reduction in the outgassing rate by more than a factor of 20 after a 400 deg C heat treatment (3.5 x 10{sup 12} TorrL s{sup -1}cm{sup -2} prior to heat treatment, reduced to 1.7 x 10{ sup -13} TorrL s{sup -1}cm{sup -2} following heat treatment). The chambers that were coated with a-Si showed minimal change in outgassing rates with heat treatment, though an outgassing rate reduced by heat treatments prior to a-Si coating was successfully preserved throughout a series of bakes. The TiN coated chamber exhibited remarkably low outgassing rates, up to four orders of magnitude lower than the uncoated stainless steel. An evaluation of coating composition suggests the presence of elemental titanium which could provide pumping and lead to an artificially low outgassing rate. The outgassing results are discussed in terms of diffusion-limited versus recombination-limited processes.

Local total and radiative heat-transfer coefficients during the heat treatment of a workpiece in a fluidised bed

International Nuclear Information System (INIS)

Gao, W.M.; Kong, L.X.; Hodgson, P.D.

2006-01-01

The heat-transfer coefficients around a workpiece immersed in an electrically heated heat treatment fluidised bed were studied. A suspension probe designed to simulate a workpiece of complex geometry was developed to measure local total and radiative heat-transfer coefficients at a high bed temperature. The probe consisted of an energy-storage region separated by insulation from the fluidised bed, except for the measuring surface, and a multi-thermocouple measurement system. Experiments in the fluidised bed were performed for a fluidising medium of 120-mesh alumina, a wide temperature range of 110-1050 deg. C and a fluidising number range of 1.18-4.24. It was found that the workpiece surface temperature has a more significant effect on heat transfer than the bed temperature. The total heat-transfer coefficient at the upper surface of the workpiece sharply decreased at the start of heating, and then steadily increased as heating progressed, while a sharp decrease became a rapid increase and then a slow increase for the radiative heat-transfer coefficient. A great difference in the heat-transfer coefficients around the workpiece was observed

Microbial safety control of compost material with cow dung by heat treatment.

Science.gov (United States)

Gong, Chun-ming

2007-01-01

Various kinds of pathogenic bacteria derived from the intestinal tract of animals exist in compost material like cow dung. In order to sterilize the pathogenic bacteria completely in compost material, the cow dung was put into a heat treatment machine in pilot plan, and harmless condition in short time was examined. The results indicated, pathogenic indicator bacteria such as coliform bacteria, fecal coliform, Escherichia coli and salmonella were all 106 cfu/g dw at the beginning, died rapidly when cow dung temperature rose to above 50 degrees C, and not detected at 54-68 degrees C for 6-24 h heat treatment. Coliform bacteria and salmonella in heated cow dung were not detected by re-growth culture and enrichment culture examination. Moreover, it was hardly influenced on the fermentation ability of composting microbe, organic decomposition bacteria. During heat treatment, the mesophile decreased rapidly and the thermophile stabilized or increased, and the most of composting microbe were bacillus in cow dung by fluorescence microscope, this indicated that bacillus was dominator and composting microbe in composting process.

Influence of Heat Treatments on Carotenoid Content of Cherry Tomatoes

Directory of Open Access Journals (Sweden)

Laura D'Evoli

2013-07-01

Full Text Available Tomatoes and tomato products are rich sources of carotenoids—principally lycopene, followed by β-carotene and lutein. The aim of this work was to study the effect of heat treatment on carotenoid content in cherry tomatoes. Raw and canned products were sampled and analysed; furthermore whole, skin and pulp fractions of cherry tomatoes were analysed when raw and home-processed, in order to better understand heat treatment effects. Lycopene content in canned tomatoes was two-fold higher than in raw tomatoes (11.60 mg/100 g versus 5.12 mg/100 g. Lutein and β-carotene were respectively 0.15 mg/100 g and 0.75 mg/100 g in canned tomatoes versus 0.11 mg/100 g and 1.00 mg/100 g in raw tomatoes. For home-processed tomatoes, β-carotene and lutein showed a content decrease in all thermally treated products. This decrease was more evident for β-carotene in the skin fraction (−17%, while for lutein it was greater in the pulp fraction (−25%. Lycopene presented a different pattern: after heat treatment its concentration increased both in the whole and in pulp fractions, while in the skin fraction it decreased dramatically (−36%. The analysis of the isomers formed during the thermal treatment suggests that lycopene is rather stable inside the tomato matrix.

Influence of Heat Treatments on Carotenoid Content of Cherry Tomatoes.

Science.gov (United States)

D'Evoli, Laura; Lombardi-Boccia, Ginevra; Lucarini, Massimo

2013-07-31

Tomatoes and tomato products are rich sources of carotenoids-principally lycopene, followed by β-carotene and lutein. The aim of this work was to study the effect of heat treatment on carotenoid content in cherry tomatoes. Raw and canned products were sampled and analysed; furthermore whole, skin and pulp fractions of cherry tomatoes were analysed when raw and home-processed, in order to better understand heat treatment effects. Lycopene content in canned tomatoes was two-fold higher than in raw tomatoes (11.60 mg/100 g versus 5.12 mg/100 g). Lutein and β-carotene were respectively 0.15 mg/100 g and 0.75 mg/100 g in canned tomatoes versus 0.11 mg/100 g and 1.00 mg/100 g in raw tomatoes. For home-processed tomatoes, β-carotene and lutein showed a content decrease in all thermally treated products. This decrease was more evident for β-carotene in the skin fraction (-17%), while for lutein it was greater in the pulp fraction (-25%). Lycopene presented a different pattern: after heat treatment its concentration increased both in the whole and in pulp fractions, while in the skin fraction it decreased dramatically (-36%). The analysis of the isomers formed during the thermal treatment suggests that lycopene is rather stable inside the tomato matrix.

The influence of distal-end heat treatment on deflection of nickel-titanium archwire.

Science.gov (United States)

Silva, Marcelo Faria da; Pinzan-Vercelino, Célia Regina Maia; Gurgel, Júlio de Araújo

2016-01-01

The aim of this in vitro study was to evaluate the deflection-force behavior of nickel-titanium (NiTi) orthodontic wires adjacent to the portion submitted to heat treatment. A total of 106 segments of NiTi wires (0.019 x 0.025-in) and heat-activated NiTi wires (0.016 x 0.022-in) from four commercial brands were tested. The segments were obtained from 80 archwires. For the experimental group, the distal portion of each segmented archwire was subjected to heat treatment (n = 40), while the other distal portion of the same archwire was used as a heating-free control group (n = 40). Deflection tests were performed in a temperature-controlled universal testing machine. Unpaired Student's t-tests were applied to determine if there were differences between the experimental and control groups for each commercial brand and size of wire. Statistical significance was set at p wire. Heat treatment applied to the distal ends of rectangular NiTi archwires does not permanently change the elastic properties of the adjacent portions.

Effect of nitrite on the microbiological stability of canned Vienna sausages preserved by mild heat treatment or combinations of heat and irradiation

International Nuclear Information System (INIS)

Farkas, J.; Zukal, E.; Incze, K.

1973-01-01

Keeping quality of Vienna sausages packed in No. 1/5 cans (ca 200 g) with salt brine and heat treated with F 0 values in the range of 0.25-0.55 was studied as a function of sodium nitrate addition. In uninoculated cans the heat requirement of preservation proved to be about 0.3 F 0 in the presence of 300 ppm NaNO 2 . A heat treatment of 0.55 F 0 and 200 ppm NaNO 2 resulted in higher microbiological stability of cans inoculated with 2x10 4 /tin Clostridium sporogenes spores than a heat treatment of 1.9 F 0 without nitrite addition. The effect of the combination of heat treatment of 0.35-0.55 F 0 and 0.45 Mrad of gamma irradiation was also studied with inoculated cans. The combination of irradiation plus heat resulted in a higher microbiological stability of the samples than the reversed order of the treatments, but this synergistic effect could not be proved in all experiments. The addition of 200 ppm NaNO 2 was not as effective in increasing the shelf-life of combination treated samples as with the solely heat treated ones. In a medium composed of a 50% extract of Vienna sausages (pH 6.4, asub(w) 0.96) and inoculated with 10 5 per ml Clostridium sporogenes spores 100 ppm or more NaNO 2 was required to ensure microbiological stability of samples heat treated with F 0 0.4. In the range of the permitted concentration level for canned meat products, sodium nitrite did not influence the heat resistance of Clostridium sporogenes, but inhibited the germination of the surviving spores. (F.J.)

Influence of heat treatment on physicochemical and rheological characteristics of natural yogurts

Directory of Open Access Journals (Sweden)

Juliana Aparecida Célia

2017-08-01

Full Text Available The aim of this study was to assess the influence of heat treatment on physicochemical and rheological characteristics of natural yogurts, as well as the influence of lyophilization process on natural yogurts after reconstitution. In the first experiment, three yogurt treatments were processed, as follows: Treatment 1, yogurt produced with raw refrigerated milk; Treatment 2, yogurt produced with refrigerated pasteurized milk; and Treatment 3, yogurt produced with UHT (ultra-high temperature milk, in addition to analyses of fat, protein, moisture, titratable acidity, and pH. The shelf life of yogurts at 1, 8, 15, 22, and 29 days of storage, as well as pH, acidity, syneresis, viscosity, viable lactic bacteria, and total coliforms were also assessed. In the second experiment, yogurts were submitted to lyophilization process, performed by scanning electron microscopy analysis and subsequently in those reconstituted, in addition to being assessed the physicochemical, rheological, and viable lactic bacteria characteristics. The results found in the first experiment showed that heat treatment was positive for viscosity, syneresis, and lactic bacteria, being viable until the 15th day of storage only for yogurts submitted to heat treatment. In the second experiment, lyophilization preserved the physicochemical characteristics of yogurts, but the number of initial lactic bacteria was different, also negatively affecting yogurt viscosity.

Induction heat treatment of laser welds

DEFF Research Database (Denmark)

Bagger, Claus; Olsen, Flemming Ove; Sørensen, Joakim Ilsing

2003-01-01

of an induction coil. A number of systematic laboratory tests were then performed in order to study the effects of the coil on bead-on-plate laser welded samples. In these tests, important parameters such as coil current and distance between coil and sample were varied. Temperature measurements were made...... the laser beam as close as possible. After welding, the samples were quality assessed according to ISO 13.919-1 and tested for hardness. The metallurgical phases are analysed and briefly described. A comparison between purely laser welded samples and induction heat-treated laser welded samples is made......In this paper, a new approach based on induction heat-treatment of flat laser welded sheets is presented. With this new concept, the ductility of high strength steels GA260 with a thickness of 1.8 mm and CMn with a thickness of 2.13 mm is believed to be improved by prolonging the cooling time from...

Heat Treatment of Buckypaper for Use in Volatile Organic Compounds Sampling

Directory of Open Access Journals (Sweden)

Jonghwa Oh

2016-01-01

Full Text Available Three types of buckypapers (BPs, two of them fabricated with arc discharge (AD single-walled carbon nanotubes (SWNTs (acetone-cleaned AD BP and methanol-cleaned AD BP and one with high-pressure carbon monoxide (HiPco SWNTs (HiPco BP, were heat-treated at different conditions to find the specific conditions for each type that improve the adsorption properties. Based on thermogravimetric analysis (TGA data, three heat treatment conditions were designed for the AD BPs and another three conditions for the HiPco BPs. Also, changes in weight and physical integrity before and after the heat treatment were considered. Heating at 300°C for 90 minutes was selected for acetone-cleaned AD BP, in which the BP kept its physical integrity and yielded a relatively high Brunauer, Emmett, and Teller (BET surface area (970 ± 18 m2/g, while methanol-cleaned AD BP was excluded because of its physical change. For HiPco BP, a condition of 300°C heating for 30 minutes was chosen as a relatively higher surface area (933 ± 54 m2/g and less weight loss (5% were observed.

Relaxation of residual stress in MMC after combined plastic deformation and heat treatment

International Nuclear Information System (INIS)

Bruno, G.; Ceretti, M.; Girardin, E.; Giuliani, A.; Manescu, A.

2004-01-01

Neutron Diffraction shows that plastic pre-deformation and heat treatments have opposite effects on the residual stress in Al-SiC p composites. The thermal micro residual stress is relaxed or even reversed by pre-strains above 0.2%, but restored by heat treatments. The sense of relaxation changes above 400 deg. C (the mixing temperature)

Degradation of Anthocyanin Content in Sour Cherry Juice During Heat Treatment

Directory of Open Access Journals (Sweden)

Lilla Szalóki-Dorkó

2015-01-01

Full Text Available Sour cherry juices made from two sour cherry cultivars (Érdi bőtermő and Kántorjánosi 3, were investigated to determine their total anthocyanin content and half-life of anthocyanins during heat treatment at different temperatures (70, 80 and 90 °C for 4 h. Before the heat treatment, Érdi bőtermő juice had higher anthocyanin concentration (812 mg/L than Kántorjánosi 3 juice (513 mg/L. The greatest heat sensitivity of anthocyanins was measured at 90 °C, while the treatments at 80 and 70 °C caused lower thermal degradation. The loss of anthocyanins in Érdi bőtermő juice after treatment was 38, 29 and 18 %, respectively, while in Kántorjánosi 3 juice losses of 46, 29 and 19 % were observed, respectively. At 90 °C sour cherry Érdi bőtermő juice had higher half-life (t1/2 of anthocyanins, while the Kántorjánosi 3 juice had higher t1/2 values at 70 °C. Cyanidin-3-glucosyl-rutinoside was present in higher concentrations in both cultivars (Érdi bőtermő: 348 and Kántorjánosi 3: 200 mg/L than cyanidin-3-rutinoside (177 and 121 mg/L before treatment. However, during the experiment, cyanidin-3-rutinoside was proved to be more resistant to heat. Comparing the two varieties, both investigated pigment compounds were more stable in Kántorjánosi 3 than in Érdi bőtermő. Degradation rate of anthocyanins was cultivar-dependent characteristic, which should be taken into account in the food production.

Investigation of heat distribution during magnetic heating treatment using a polyurethane–ferrofluid phantom-model

International Nuclear Information System (INIS)

Henrich, F.; Rahn, H.; Odenbach, S.

2014-01-01

Magnetic heating treatment can be used as an adjuvant treatment for cancer therapy. In this therapy, magnetic nanoparticles are enriched inside the tumour and exposed to an alternating magnetic field. Due to magnetic losses the temperature in the tumour rises. The resulting temperature profile inside the tumour is useful for the therapeutic success. In this context heat transfer between tissue with nanoparticles and tissue without nanoparticles is a highly important feature which is actually not understood in detail. In order to investigate this, a phantom has been created which can be used to measure the temperature profile around a region enriched with magnetic nanoparticles. This phantom is composed of a material, which has similar thermal conductivity as human tissue. A tempered water bath surrounds the phantom to establish a constant surrounding temperature simulating the heat sink provided by the human body in a real therapeutic application. It has been found that even at a low concentration of magnetic nanoparticles around 13 mg/ml, sufficient heating of the enriched region can be achieved. Moreover it has been observed that the temperature drops rapidly in the material surrounding the enriched region. Corresponding numerical investigations provide a basis for future recalculations of the temperature inside the tumour using temperature data obtained in the surrounding tissue. - Highlights: • The temperature profile by magnetic hyperthermia was examined. • A model was built to get a deeper understanding of the temperature profile. • The temperature profile of the model inside magnetic fields was measured. • Based on the model a simulation of the temperature profile was performed. • The simulated temperature profile agreed well with the measured profile

Evaluation of carbon diffusion in heat treatment of H13 tool steel under different atmospheric conditions

OpenAIRE

Ramezani, Maziar; Pasang, Timotius; Chen, Zhan; Neitzert, Thomas; Au, Dominique

2015-01-01

Although the cost of the heat treatment process is only a minor portion of the total production cost, it is arguably the most important and crucial stage on the determination of material quality. In the study of the carbon diffusion in H13 steel during austenitization, a series of heat treatment experiments had been conducted under different atmospheric conditions and length of treatment. Four austenitization atmospheric conditions were studied, i.e., heat treatment without atmospheric contro...

Heat stroke during long-term clozapine treatment: should we be concerned about hot weather?

OpenAIRE

Hoffmann, Maurício Scopel; Oliveira, Lucas Mendes; Lobato, Maria Inês Rodrigues; Belmonte-de-Abreu, Paulo

2016-01-01

Objective To describe the case of a patient with schizophrenia on clozapine treatment who had an episode of heat stroke. Case description During a heat wave in January and February 2014, a patient with schizophrenia who was on treatment with clozapine was initially referred for differential diagnose between systemic infection and neuroleptic malignant syndrome, but was finally diagnosed with heat stroke and treated with control of body temperature and hydration. Comments This report aims to...

Preliminary heat treatment of 4KhM2Fch die steel

International Nuclear Information System (INIS)

Leonidov, V.M.; Berezkin, Y.A.; Nikitenko, E.V.

1986-01-01

To improve the machinability and preparation of the structure for hardening, die steels are given a preliminary treatment which provides a reduction in hardness as a result of separation in the structure of the carbide and ferrite phases, coagulation of the carbides, and acquisition by them of a granular form and also the obtaining of fine grains and a uniform distribution of the structural constituents. The microstructure was evaluated after etching in 4% nital on an MIM-8M microscope. The 4KhM2Fch steel was given a preliminary heat treatment of normalize and anneal. It was concluded that for 4KhM2Fch steel a preliminary heat treatment of normalizing from 950 0 C with a hold of 1.5-2 h, annealing at 750-760 0 C with a hold of 2-3 h, cooling to the isothermal temperature of 670-680 0 C with a hold of 3-4 h, and further air cooling is recommended. The structure after such a heat is granular pearlite with a rating 1-2 and a hardness of 220-250 HB

The effect of postproduction heat treatment on γ-TiAl alloys produced by the GTAW-based additive manufacturing process

Energy Technology Data Exchange (ETDEWEB)

Ma, Yan; Cuiuri, Dominic; Li, Huijun; Pan, Zengxi, E-mail: zengxi@uow.edu.au; Shen, Chen

2016-03-07

Postproduction heat treatments were carried out on additively manufactured γ-TiAl alloys that were produced by using the gas tungsten arc welding (GTAW) process. The microstructural evolution and mechanical properties of both as-fabricated and heat-treated specimens were investigated to assess the effect of different heat treatment conditions, by using optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), Neutron Diffraction and tensile tests. The results indicated that heat treatment promotes the formation of the γ phase in the majority region after heat treatment at 1200 °C for 24 h, while a fully lamellar structure was formed in the near-substrate zone. The response to heat treatment at 1060 °C/24 h was markedly different, producing a fine lamellar structure with differing sizes in the majority region and near-substrate zone. These various microstructural characteristics determined the mechanical properties of the heat-treated samples. The heat-treated samples at 1200 °C/24 h exhibited lower UTS and microhardness values but higher ductility than the as-fabricated samples without heat treatment, while the 1060 °C/24 h heat treatment resulted in higher UTS and microhardness values but lower ductility. Due to the homogenous microstructure in the majority region after each postproduction heat treatment, the tensile properties were similar for both the build direction (Z) and travel direction (Y), thereby minimising the anisotropy that is exhibited by the as-fabricated alloy prior to heat treatment.

Effect of Carbon Nanofiber Heat Treatment on Physical Properties of Polymeric Nanocomposites—Part I

Directory of Open Access Journals (Sweden)

Khalid Lafdi

2007-01-01

Full Text Available The definition of a nanocomposite material has broadened significantly to encompass a large variety of systems made of dissimilar components and mixed at the nanometer scale. The properties of nanocomposite materials also depend on the morphology, crystallinity, and interfacial characteristics of the individual constituents. In the current work, vapor-grown carbon nanofibers were subjected to varying heat-treatment temperatures. The strength of adhesion between the nanofiber and an epoxy (thermoset matrix was characterized by the flexural strength and modulus. Heat treatment to 1800C∘ demonstrated maximum improvement in mechanical properties over that of the neat resin, while heat-treatment to higher temperatures demonstrated a slight decrease in mechanical properties likely due to the elimination of potential bonding sites caused by the elimination of the truncated edges of the graphene layers. Both the electrical and thermal properties of the resulting nanocomposites increased in conjunction with the increasing heat-treatment temperature.

Heat treatment on keruing and light red meranti: The effect of heat exposure at different levels of temperature on bending strength properties

Science.gov (United States)

Noh, Nur Ilya Farhana Md; Ahmad, Zakiah

2017-11-01

Heat treatment on timbers is a process of applying heat to modify and equip the timbers with new improvised characteristics. It is environmental friendly compared to the common practice of treating timber by chemical preservatives. Malaysian hardwood timbers namely Keruing and Light Red Meranti which are in green condition were heat treated at temperature 150°C, 170°C, 190°C and 210°C, in a specially designed electronic furnace within one hour duration. The objectives were to determine the effect of heat treatment on bending strength properties of heat treated timbers in terms of Modulus of Elasticity (MOE) and Modulus of Rupture (MOR) and to examine the significance changes at each temperature level. Untreated samples for each species were used as a control sample. The results indicated that the bending strength properties for both species of timbers were affected by the heat exposure. Both MOE and MOR values for heat treated Keruing were increased when subjected to the temperature levels at 150°C, 170°C and 190°C except at 210°C. Heat treated Light Red Meranti shows the same pattern of increment on its MOE and MOR values after exposure to heat at three temperature levels applied and the values dropped at 210°C. However, for both of species, even though there were decrement occurred at 210°C, the value is still higher compared to the control sample. The increments of MOE and MOR values are an indicator that heat treatment had successfully improvised the bending strength properties of these two species of hardwood timber.

Effect of the Heat Treatment on the Graphite Matrix of Fuel Element for HTGR

International Nuclear Information System (INIS)

Lee, Chungyong; Lee, Seungjae; Suh, Jungmin; Jo, Youngho; Lee, Youngwoo; Cho, Moonsung

2013-01-01

In this paper, the cylinder-formed fuel element for the block type reactor is focused on, which consists of the large part of graphite matrix. One of the most important properties of the graphite matrix is the mechanical strength for the high reliability because the graphite matrix should be enabled to protect the TRISO particles from the irradiation environment and the impact from the outside. In this study, the three kinds of candidate graphites and Phenol as a binder were chosen and mixed with each other, formed and heated for the compressive strength test. The objective of this research is to optimize the kinds and composition of the mixed graphite and the forming process by evaluating the compressive strength before/after heat treatment (carbonization of binder). In this study, the effect of heat treatment on graphite matrix was studied in terms of the density and the compressive strength. The size (diameter and length) of pellet is increased by heat treatment. Due to additional weight reduction and swelling (length and diameter) of samples the density of graphite pellet is decreased from about 2.0 to about 1.7g/cm 3 . From the mechanical test results, the compressive strength of graphite pellets was related to the various conditions such as the contents of binder, the kinds of graphite and the heat treatment. Both the green pellet and the heat treated pellet, the compressive strength of G+S+P pellets is relatively higher than that of R+S+P pellets. To optimize fuel element matrix, the effect of Phenol and other binders, graphite composition and the heat treatment on the mechanical properties will be deeply investigated for further study

Evaluation of focused ultrasound algorithms: Issues for reducing pre-focal heating and treatment time.

Science.gov (United States)

Yiannakou, Marinos; Trimikliniotis, Michael; Yiallouras, Christos; Damianou, Christakis

2016-02-01

Due to the heating in the pre-focal field the delay between successive movements in high intensity focused ultrasound (HIFU) are sometimes as long as 60s, resulting to treatment time in the order of 2-3h. Because there is generally a requirement to reduce treatment time, we were motivated to explore alternative transducer motion algorithms in order to reduce pre-focal heating and treatment time. A 1 MHz single element transducer with 4 cm diameter and 10 cm focal length was used. A simulation model was developed that estimates the temperature, thermal dose and lesion development in the pre-focal field. The simulated temperature history that was combined with the motion algorithms produced thermal maps in the pre-focal region. Polyacrylimde gel phantom was used to evaluate the induced pre-focal heating for each motion algorithm used, and also was used to assess the accuracy of the simulation model. Three out of the six algorithms having successive steps close to each other, exhibited severe heating in the pre-focal field. Minimal heating was produced with the algorithms having successive steps apart from each other (square, square spiral and random). The last three algorithms were improved further (with small cost in time), thus eliminating completely the pre-focal heating and reducing substantially the treatment time as compared to traditional algorithms. Out of the six algorithms, 3 were successful in eliminating the pre-focal heating completely. Because these 3 algorithms required no delay between successive movements (except in the last part of the motion), the treatment time was reduced by 93%. Therefore, it will be possible in the future, to achieve treatment time of focused ultrasound therapies shorter than 30 min. The rate of ablated volume achieved with one of the proposed algorithms was 71 cm(3)/h. The intention of this pilot study was to demonstrate that the navigation algorithms play the most important role in reducing pre-focal heating. By evaluating in

Heat treatments and low temperature fracture toughness of a Ti-6A1-4V alloy

International Nuclear Information System (INIS)

Nagai, K.; Hiraga, K.; Ishikawa, K.; Ogata, T.

1984-01-01

Titanium alloy is one of the reliable structural materials for cryogenic use owing to its high strength, high specific strength and low thermal conductivity. Heat treatment is one method of controlling the normally poor fracture toughness of this alloy at ambient temperature. However, there have been few attempts to improve the low temperature fracture toughness by heat treatment. This study was conducted to elucidate the effects of heat treatments on the low temperature fracture toughness in a Ti-6A1-4V alloy. The effects of the heat treatments were as follows: the beta treatment was a very feasible method to improve the low temperature fracture properties; the alpha+beta treatment was favorable for the increment in the low temperature ductility but did not largely improve the fracture toughness; the double treatment yielded good ductility but was not useful for improving the fracture toughness

Influence of heat treatment temperature on bonding and oxidation ...

Indian Academy of Sciences (India)

Administrator

Diamond; TiO2 film; heat treatment temperature; anti-oxidation; mechanical properties. 1. Introduction. Due to its ..... figure 4a, which was due to the change of chemical envi- ronment of ... graphite, diamond, diamond-like carbon and carbon.10.

SiO2 sol-gel films after ammonia and heat two-step treatments

International Nuclear Information System (INIS)

Zhang Chunlai; Wang Biyi; Tian Dongbin; Yin Wei; Jiang Xiaodong; Yuan Xiaodong; Yan Lianghong; Zhang Hongliang; Zhao Songnan; Lv Haibing

2008-01-01

SiO 2 thin films were deposited using tetraethoxylsilane as precursor, ammonia as catalyst on K9 glass by sol-gel method. These films were post-treated by ammonia and heat. The properties of the coatings were characterized by ellipsometer, UV-vis spectrophotometry, FTIR-spectroscopy, scanning probe microscope and contact angle measurement apparatus. The resuits indicate that the thickness of the films with ammonia and heat treatment tend to decrease. Both the refractive index and water contact angle increase after ammonia treatment. However, they both decrease after heat treatment. The former increases by 0.236 for the first step, then decreases by 0.202 for the second. The latter increases to 58.92 degree, then decreases to 38.07 degree. The transmittance of the coatings turn to be better and continuously shift to short wave by UV-vis spectrophotometry. The surface becomes smoother by AFM after the two-step treatment. (authors)

Effects of heat treatments on laser welded Mg-rare earth alloy NZ30K

International Nuclear Information System (INIS)

Dai Jun; Huang Jian; Li Min; Li Zhuguo; Dong Jie; Wu Yixiong

2011-01-01

Highlights: → Firstly find the tadpole-shape precipitates in the welding joint. → The precipitation strengthening can account for 79% of the total strength. → The results can provide some insights on the application of Mg-RE alloy. - Abstract: In this study, the effects of heat treatments on the quality of laser welded Mg-rare earth alloy NZ30K were systematically studied. The microstructure and mechanical properties of joints, welded by a 15 kW high power CO 2 laser, under different heat treatments had been tested and analyzed. The results indicated that the heat treatment plays an important role in the mechanical strength of laser welded joint of NZ30K. The microstructure of samples after the solution treatment as well as aging treatment is different from that of the as-received welded joint. For solution treatment, although the microstructure is much different from that of as-received welded joint, the solution strengthening effect is not obvious. There are lots of precipitates in the fusion zone after the aging treatment, which will significantly enhance the ultimate tensile strength (UTS) and the yield tensile strength (YTS) of the welding joint. 79% of YTS is caused by precipitation strengthening. Therefore, the results implied that the UTS and YTS can be greatly improved by proper heat treatment.

Effect of heat-treatment on toughness and strength properties of C-Mn steel

International Nuclear Information System (INIS)

Mohd bin Harun; Goh Kian Seong; Jasmin binti Baba

1991-01-01

The strength and toughness of the heat-treated and tempered C-Mn are studied. Two types of heat-treatment have been carried out with the specimens in an argon gas. The variation in the fracture surfaces of the heat-treated and tempered specimens with impact test temperature is discussed also

Effect of heat treatment of toughness and strength properties of C-Mn steel

International Nuclear Information System (INIS)

Mohamad bin Harun; Goh Kian Seong; Yasmin binti Baba

1989-01-01

The strength and toughness of the heat-treated and tempered C-Mn are studied. Two type of heat-treatments have been carried out with the specimens in an argon gas. The variation in the fracture surfaces of the heat-treated and tempered specimens with impact test temperatures also is discussed. (author)

Impact of Heat Treatment on the Freezing Points of Cow and Goat Milk

Directory of Open Access Journals (Sweden)

Bohumíra Janštová

2009-01-01

Full Text Available The aim of this study was to monitor the impact of heat treatment variables on the freezing point of cow and goat milk. The freezing point (FP was established in 30 bulk tank samples of goat milk and in 30 bulk tank samples of cow milk which were subject to laboratory heat treatment at temperatures of 72 °C (A, 85 °C (B, 95 °C (C, with the same exposition times of 20 s. Freezing point measurements of raw and heat-treated milk were carried out in compliance with the Standard CTS 57 0538 by a thermistor cryoscope. The FP of raw cow milk increased with heat treatment from the initial values of -0.5252 ± 0.0114 °C (O by 0.0023 °C (A, 0.0034 °C (B and 0.0051°C (C. Changes in FP values of goat milk were detected, from its initial value of –0.5530 ± 0.0086 °C there was an increase in the FP depending on the mode of heat treatment due to pasteurization by an average of 0.0028 °C (A, 0.0036 °C (B and 0.0054 °C (C. The dynamics of the changes were similar both in goat and cow milk. Freezing point values in cow and goat milk differed (P ⪬ 0.01 when compared to the freezing point of untreated milk after the individual interventions as well as when compared between each other. An increase in the heat treatment temperature of cow and goat milk causes an increase in the freezing point (a shift towards zero. These results can be used in practice for checking the raw material in dairy industry.

Heat treatment of transparent Yb:YAG and YAG ceramics and its influence on laser performance

Science.gov (United States)

Fujioka, Kana; Mochida, Tetsuo; Fujimoto, Yasushi; Tokita, Shigeki; Kawanaka, Junji; Maruyama, Momoko; Sugiyama, Akira; Miyanaga, Noriaki

2018-05-01

Composite transparent ceramic materials are promising for improving the performance of high-average-power lasers. A combination of room-temperature bonding via surface treatment by a fast atom beam and diffusion bonding via heating, which effectively controls the ion diffusion distance near the interface, makes the laser materials suitable for a variety of oscillator/amplifier. During the heat treatment of yttrium aluminum garnet (YAG) ceramics, the Si ions in the solid solution of the sintering aid incorporated within the grains were seen to segregate at the grain boundary, resulting in an increase of scattering sites. The number density and size of the scattering sites strongly depended on the post-heating temperature rather than the heating time. Specifically, heating at 1300 °C did not affect the transmittance of the YAG ceramic, whereas both the size and number of scattering sites substantially increased with a heat treatment at 1400 °C. The laser oscillation experiment using cryogenically-cooled Yb:YAG ceramics exhibited heating temperature dependence of the slope efficiency owing to the increasing scattering loss.

A heat mathematical model of polymer composite cylinder during microwave treatment

Directory of Open Access Journals (Sweden)

S. V. Reznik

2014-01-01

Full Text Available Traditional technologies of producing epoxy based polymer composite materials (PCM require a long-term and energy consuming thermal processing. Microwave heating could be used as an alternative technology for heating work pieces made of PCM; this would allow to reduce treatment time and energy consumption significantly. A mathematical model of temperature distribution inside a cylindrical composite system during microwave treatment was investigated in this paper. The model includes a hollow PCM cylinder made of an epoxy binder and carbon fibers and a solid cylindrical mandrel. Theoretical and experimental results on the temperature state of the system were analyzed and discussed.

Phase transformation and hardness of SS 316 L steel cast alloy after heat treatment at high temperature

International Nuclear Information System (INIS)

Hidayat, S.; Prayitno, D. H.

2000-01-01

Heat treatment Study of SS 316 L cast alloy at high temperature was conducted. The alloy of SS 316 L was melted by arc melting furnace in argon atmosphere. Heat treatment of SS 316 L casting alloy was carried out in tube furnace at 1400 o C for period of 1/2, 1, and 2 hours. The optical microscopic characterization showed that SS 316 L cast has got dendritic micro structure with ferrite as the primary phase. After the heat treatment, the ferrite phase underwent gradual decrease followed by an increase of the austenite phase. The heat treatment process also resulted in the formation of the new grain boundary. The hardness examination revealed that for longer period of the heat treatment, the hardness of SS 316 L increased. (author)

The effects of heat treatment on physical and technological ...

African Journals Online (AJOL)

STORAGESEVER

2009-10-19

Oct 19, 2009 ... ween 450 and 660 m altitudes in Cide-Sehdagi (Gercek et al., 1998; Dogu ... changes continue as the temperature is increased in ... Heat treatment slows water uptake and wood cell wall absorbs ...... The Effect of Boiling Time.

Effect of heat treatment on anodic activation of aluminium by trace element indium

Energy Technology Data Exchange (ETDEWEB)

Graver, Brit [Department of Materials Science and Engineering, Norwegian University of Science and Technology, N-7491 Trondheim (Norway); Helvoort, Antonius T.J. van [Department of Physics, Norwegian University of Science and Technology, N-7491 Trondheim (Norway); Nisancioglu, Kemal, E-mail: kemal.nisancioglu@material.ntnu.n [Department of Materials Science and Engineering, Norwegian University of Science and Technology, N-7491 Trondheim (Norway)

2010-11-15

Research highlights: {yields} Indium segregation activates AlIn alloy surface anodically in chloride solution. {yields} Enrichment of In on Al surface can occur thermally by heat treatment at 300 {sup o}C. {yields} Increasing temperature homogenises indium in aluminium reducing anodic activation. {yields} Indium can activate AlIn surface by segregating through dealloying of aluminium. {yields} Anodic activation is caused by AlIn amalgam formation at aluminium surface. - Abstract: The presence of trace elements in Group IIIA-VA is known to activate aluminium anodically in chloride environment. The purpose of this paper is to investigate the surface segregation of trace element In by heat treatment and resulting surface activation. Model binary AlIn alloys, containing 20 and 1000 ppm by weight of In, were characterized after heat treatment at various temperatures by use of glow discharge optical emission spectroscopy, electron microscopy and electrochemical polarization. Heat treatment for 1 h at 300 {sup o}C gave significant segregation of discrete In particles (thermal segregation), which activated the surface. Indium in solid solution with aluminium, obtained by 1 h heat treatment at 600 {sup o}C, also activated by surface segregation of In on alloy containing 1000 ppm In, resulting from the selective dissolution of the aluminium component during anodic oxidation (anodic segregation). The effect of anodic segregation was reduced by decreasing indium concentration in solid solution; it had negligible effect at the 20 ppm level. The segregated particles were thought to form a liquid phase alloy with aluminium during anodic polarization, which in turn, together with the chloride in the solution destabilized the oxide.

The local heat treatment equipment and technology of the pipelines welded joints

International Nuclear Information System (INIS)

Korol'kov, P.M.

1998-01-01

The principal methods and equipment for local treatment of the pipe-lines weld joints in different industry branches is described. Recommendations about heat treatment equipment and technology application are given

Effect of heat treatments on machinability of gold alloy with age-hardenability at intraoral temperature.

Science.gov (United States)

Watanabe, I; Baba, N; Watanabe, E; Atsuta, M; Okabe, T

2004-01-01

This study investigated the effect of heat treatment on the machinability of heat-treated cast gold alloy with age-hardenability at intraoral temperature using a handpiece engine with SiC wheels and an air-turbine handpiece with carbide burs and diamond points. Cast gold alloy specimens underwent various heat treatments [As-cast (AC); Solution treatment (ST); High-temperature aging (HA), Intraoral aging (IA)] before machinability testing. The machinability test was conducted at a constant machining force of 0.784N. The three circumferential speeds used for the handpiece engine were 500, 1,000 and 1,500 m/min. The machinability index (M-index) was determined as the amount of metal removed by machining (volume loss, mm(3)). The results were analyzed by ANOVA and Scheffé's test. When an air-turbine handpiece was used, there was no difference in the M-index of the gold alloy among the heat treatments. The air-turbine carbide burs showed significantly (pmachinability of the gold alloy using the air-turbine handpiece. The heat treatments had a small effect on the M-index of the gold alloy machined with a SiC wheel for a handpiece engine.

Study of the Al-Si-X system by different cooling rates and heat treatment

Directory of Open Access Journals (Sweden)

Miguel Angel Suarez

2012-10-01

Full Text Available The solidification behavior of the Al-12.6% Si (A1, the hypereutectic Al-20%Si (A2 and the Al-20%Si-1.5% Fe-0.5%Mn (A3 (in wt. (% alloys, at different cooling rates is reported and discussed. The cooling rates ranged between 0.93 °C/s and 190 °C/s when cast in sand and copper wedge-shaped molds, respectively. A spheroidization heat treatment was carried out to the alloys in the as-cast condition at 540 °C for 11 hours and quench in water with a subsequent heat treatment at 170 °C for 5 hours with the purpose of improving the mechanical properties. The samples were characterized by optical microscopy, scanning electron microscopy and mechanically by tensile test, in order to evaluate the response of the heat treatment on the different starting microstructures and mechanical properties. It was found that alloys cooled at rates greater than 10.8 °C/s had a smaller particle size and better distribution, also showed a greater response to spheroidization heat treatment of all silicon (Si phases. The spheroidization heat treatment caused an increase in the ultimate tensile stress (UTS and elongation when compared with the alloys in the as-cast condition. The highest UTS value of 174 MPa was obtained for the (A1 alloy.

Effect of heat treatment of wood on the morphology, surface roughness and penetration of simulated and human blood.

Science.gov (United States)

Rekola, J; Lassila, L V J; Nganga, S; Ylä-Soininmäki, A; Fleming, G J P; Grenman, R; Aho, A J; Vallittu, P K

2014-01-01

Wood has been used as a model material for the development of novel fiber-reinforced composite bone substitute biomaterials. In previous studies heat treatment of wood was perceived to significantly increase the osteoconductivity of implanted wood material. The objective of this study was to examine some of the changing attributes of wood materials that may contribute to improved biological responses gained with heat treatment. Untreated and 140°C and 200°C heat-treated downy birch (Betula pubescens Ehrh.) were used as the wood materials. Surface roughness and the effect of pre-measurement grinding were measured with contact and non-contact profilometry. Liquid interaction was assessed with a dipping test using two manufactured liquids (simulated blood) as well as human blood. SEM was used to visualize possible heat treatment-induced changes in the hierarchical structure of wood. The surface roughness was observed to significantly decrease with heat treatment. Grinding methods had more influence on the surface contour and roughness than heat treatment. The penetration of the human blood in the 200°C heat-treated exceeded that in the untreated and 140°C heat-treated materials. SEM showed no significant change due to heat treatment in the dry-state morphology of the wood. The results of the liquid penetration test support previous findings in literature concerning the effects of heat treatment on the biological response to implanted wood. Heat-treatment has only a marginal effect on the surface contour of wood. The highly specialized liquid conveyance system of wood may serve as a biomimetic model for the further development of tailored fiber-composite materials.

Alkali-heat treatment of a low modulus biomedical Ti-27Nb alloy

International Nuclear Information System (INIS)

Zhou, Y; Wang, Y B; Zhang, E W; Cheng, Y; Xiong, X L; Zheng, Y F; Wei, S C

2009-01-01

This study focuses on the surface modification of a near β-type Ti-27 wt.% Nb alloy by alkali-heat treatment. The influence of alkali concentration, alkali-treated time and alkali-treated temperature on the microstructure and constitutional phases of the modified surface is investigated by SEM, XRD and ICP. Immersion experiments in a simulated body fluid (SBF) were carried out to examine the Ca-P phase forming ability of the modified surfaces. The SEM observation and XRD analysis revealed that a sodium titanate layer is formed after alkali-heat treatment. The morphology and Ca-P phase forming of the layer are greatly affected by the surface roughness of the samples, the alkali concentration, the alkali-treated time and alkali-treated temperature. The results of SBF immersion, which are obtained by ICP analysis, indicate that the activated sodium titanate layer prepared by alkali-heat treatment is beneficial to further improving the biocompatibility of the Ti-27 wt.% Nb alloy.

Effects of Heat Treatment on SiC-SiC Ceramic Matrix Composites

Science.gov (United States)

Knauf, Michael W.

Residual stresses resulting from the manufacturing process found within a silicon carbide/silicon carbide (SiC/SiC) ceramic matrix composite were thoroughly investigated through the use of high-energy X-ray diffraction and Raman microspectroscopy. The material system studied was a Rolls-Royce composite produced with Hi-Nicalon fibers woven into a five harness satin weave, coated with boron nitride and silicon carbide interphases, and subsequently infiltrated with silicon carbide particles and a silicon matrix. Constituent stress states were measured before, during, and after heat treatments ranging from 900 °C to 1300 °C for varying times between one and sixty minutes. Stress determination methods developed through these analyses can be utilized in the development of ceramic matrix composites and other materials employing boron-doped silicon. X-ray diffraction experiments were performed at the Argonne National Laboratory Advanced Photon Source to investigate the evolution of constituent stresses through heat treatment, and determine how stress states are affected at high temperature through in situ measurements during heat treatments up to 1250 °C for 30 minutes. Silicon carbide particles in the as-received condition exhibited a nearly isotropic stress state with average tensile stresses of approximately 300 MPa. The silicon matrix exhibited a complimentary average compressive stress of approximately 300 MPa. Strong X-ray diffraction evidence is presented demonstrating solid state boron diffusion and increased boron solubility found in silicon throughout heat treatment. While the constituent stress states did evolve through the heat treatment cycles, including approaching nearly stress-free conditions at temperatures close to the manufacturing temperature, no permanent relaxation of stress was observed. Raman spectroscopy was utilized to investigate stresses found within silicon carbide particles embedded within the matrix and the silicon matrix as an alternate

Laser heat treatment of welds for various stainless steels

Science.gov (United States)

Dontu, O.; Ganatsios, S.; Alexandrescu, N.; Predescu, C.

2008-03-01

The paper presents a study concerning the post - weld heat treatment of a duplex stainless steel. Welded joint samples were surface - treated using the same laser source adopted during welding in order to counterbalance the excess of ferrite formed in the welding process.

A previously undescribed organic residue sheds light on heat treatment in the Middle Stone Age.

Science.gov (United States)

Schmidt, Patrick; Porraz, Guillaume; Bellot-Gurlet, Ludovic; February, Edmund; Ligouis, Bertrand; Paris, Céline; Texier, Pierre-Jean; Parkington, John E; Miller, Christopher E; Nickel, Klaus G; Conard, Nicholas J

2015-08-01

South Africa has in recent years gained increasing importance for our understanding of the evolution of 'modern human behaviour' during the Middle Stone Age (MSA). A key element in the suite of behaviours linked with modern humans is heat treatment of materials such as ochre for ritual purposes and stone prior to tool production. Until now, there has been no direct archaeological evidence for the exact procedure used in the heat treatment of silcrete. Through the analysis of heat-treated artefacts from the Howiesons Poort of Diepkloof Rock Shelter, we identified a hitherto unknown type of organic residue - a tempering-residue - that sheds light on the processes used for heat treatment in the MSA. This black film on the silcrete surface is an organic tar that contains microscopic fragments of charcoal and formed as a residue during the direct contact of the artefacts with hot embers of green wood. Our results suggest that heat treatment of silcrete was conducted directly using an open fire, similar to those likely used for cooking. These findings add to the discussion about the complexity of MSA behaviour and appear to contradict previous studies that had suggested that heat treatment of silcrete was a complex (i.e., requiring a large number of steps for its realization) and resource-consuming procedure. Copyright © 2015 Elsevier Ltd. All rights reserved.

Effect of heat treatment on brewer's yeast fermentation activity

OpenAIRE

Kharandiuk, Tetiana; Kosiv, Ruslana; Palianytsia, Liubov; Berezovska, Natalia

2015-01-01

The influence of temperature treatment of brewer's yeast strain Saflager W-34/70 at temperatures of -17, 20, 25, 30, 35, 40 °C on their fermentative activity was studied. It was established that the freezing of yeast leads to a decrease of fermentation activity in directly proportional to the duration way. Fermentative activity of yeast samples can be increased by 20-24% by heat treatment at 35 °C during 15-30 minutes.

Effect of intercritical heat treatment on mechanical properties of reinforcing steel bars

International Nuclear Information System (INIS)

Abro, M.I.; Memon, R.A.; Soomro, I.A.; Aftab, U.

2017-01-01

Intercritical heat treatments attempts were made to enhance the mechanical properties of reinforcing steel bars milled from scrap metal. For this, two grades of steel bars were obtained from different steel mills and their mechanical properties that include hardness, ultimate tensile strength, and percent elongation before and after intercritical heat treatment were determined. Results indicated that 25.5 and 17.6%, improvements in UTS (Ultimate Tensile Strength) and 18.8 and 14.3% improvement in percent elongation in two grades of reinforcing steel samples containing 0.17 and 0.24% carbon respectively was achieved while heating at 750 degree C for 2h. Appreciable improvement in the mechanical properties was noted due to birth of sufficient quantity of martensite along with ferrite. (author)

Influence of Heat Treatment on Abrasive Wear Resistance of Silumin Matrix Composite Castings

Directory of Open Access Journals (Sweden)

Gawdzińska K.

2016-03-01

Full Text Available The authors attempted at examining the effect of heat treatment on abrasive wear resistance of metal composite castings. Metal matrix composites were made by infiltrating preforms created from unordered short fibers (graphite or silumin with liquid aluminium alloy AlSi12(b. Thus prepared composites were subject to solution heat treatment at a temperature of 520°C for four hours, then aging at a temperature of 220°C for four hours. Abrasion resistance of the material was tested before and after thermal treatment.

Evaluation of dry heat treatment of soft wheat flour for the production of high ratio cakes.

Science.gov (United States)

Keppler, S; Bakalis, S; Leadley, C E; Sahi, S S; Fryer, P J

2018-05-01

An accurate method to heat treat flour samples has been used to quantify the effects of heat treatment on flour functionality. A variety of analytical methods has been used such as oscillatory rheology, rheomixer, solvent retention capacity tests, and Rapid Visco Analysis (RVA) in water and in aqueous solutions of sucrose, lactic acid, and sodium carbonate. This work supports the hypothesis that heat treatment facilitates the swelling of starch granules at elevated temperature. Results furthermore indicated improved swelling ability and increased interactions of flour polymers (in particular arabinoxylans) of heat treated flour at ambient conditions. The significant denaturation of the proteins was indicated by a lack of gluten network formation after severe heat treatments as shown by rheomixer traces. Results of these analyses were used to develop a possible cake flour specification. A method was developed using response surfaces of heat treated flour samples in the RVA using i) water and ii) 50% sucrose solution. This can uniquely characterise the heat treatment a flour sample has received and to establish a cake flour specification. This approach might be useful for the characterisation of processed samples, rather than by baking cakes. Hence, it may no longer be needed to bake a cake after flour heat treatment to assess the suitability of the flour for high ratio cake production, but 2 types of RVA tests suffice. Copyright © 2018 The Authors. Published by Elsevier Ltd.. All rights reserved.

Analysis of Thermal Stresses and Strains Developing during the Heat Treatment of Windmill Shaft

Directory of Open Access Journals (Sweden)

Cebo-Rudnicka A.

2017-06-01

Full Text Available In the paper the results of evaluation of the temperature and stress fields during four cycles of the heat treatment process of the windmill shaft has been presented. The temperature field has been calculated from the solution to the heat conduction equation over the whole heat treatment cycles of the windmill shaft. To calculate the stress field an incremental method has been used. The relations between stresses and strains have been described by Prandtl-Reuss equation for the elastic-plastic body. In order to determine the changes in the temperature and stress fields during heat treatment of the windmill shaft self-developed software utilizing the Finite Element Method has been used. This software can also be used to calculate temperature changes and stress field in ingots and other axially symmetric products. In the mathematical model of heating and cooling of the shaft maximum values of the strains have been determined, which allowed to avoid the crack formation. The critical values of strains have been determined by using modified Rice and Tracy criterion.

Effect of prolonged isothermal heat treatment on the mechanical behavior of advanced NANOBAIN steel

Science.gov (United States)

Avishan, Behzad

2017-09-01

The microstructural evolution and consequent changes in strength and ductility of advanced NANOBAIN steel during prolonged isothermal heat-treatment stages were investigated. The microstructure and mechanical properties of nanostructured bainite were not expected to be influenced by extending the heat-treatment time beyond the optimum value because of the autotempering phenomenon and high tempering resistance. However, experimental results indicated that the microstructure was thermodynamically unstable and that prolonged austempering resulted in carbon depletion from high-carbon retained austenite and carbide precipitations. Therefore, austenite became thermally less stable and partially transformed into martensite during cooling to room temperature. Prolonged austempering did not lead to the typical tempering sequence of bainite, and the sizes of the microstructural constituents were independent of the extended heat-treatment times. This independence, in turn, resulted in almost constant ultimate tensile strength values. However, microstructural variations enhanced the yield strength and the hardness of the material at extended isothermal heat-treatment stages. Finally, although microstructural changes decreased the total elongation and impact toughness, considerable combinations of mechanical properties could still be achieved.

Susceptibility of Plodia interpunctella (Lepidoptera: Pyralidae) developmental stages to high temperatures used during structural heat treatments.

Science.gov (United States)

Mahroof, R; Subramanyam, B

2006-12-01

Heating the ambient air of a whole, or a portion of a food-processing facility to 50 to 60 degrees C and maintaining these elevated temperatures for 24 to 36 h, is an old technology, referred to as heat treatment. There is renewed interest in adopting heat treatments around the world as a viable insect control alternative to fumigation with methyl bromide. There is limited published information on responses of the Indian meal moth, Plodia interpunctella (Hübner), exposed to elevated temperatures typically used during heat treatments. Time-mortality relationships were determined for eggs, fifth-instars (wandering-phase larvae), pupae, and adults of P. interpunctella exposed to five constant temperatures between 44 and 52 degrees C. Mortality of each stage increased with increasing temperature and exposure time. In general, fifth-instars were the most heat-tolerant stage at all temperatures tested. Exposure for a minimum of 34 min at 50 degrees C was required to kill 99% of the fifth-instars. It is proposed that heat treatments aimed at controlling fifth-instars should be able to control all other stages of P. interpunctella.

Simple approach to carboxyl-rich materials through low-temperature heat treatment of hydrothermal carbon in air

Energy Technology Data Exchange (ETDEWEB)

Chen Zhen; Ma Lijian; Li Shuqiong; Geng Junxia; Song Qiang; Liu Jun; Wang Chunli; Wang Hang; Li Juan [College of Chemistry, Sichuan University, Key Laboratory of Radiation Physics and Technology (Sichuan University), Ministry of Education, Chengdu 610064 (China); Qin Zhi [Institute of Modern Physics, Chinese Academy of Sciences, Lanzhou 730000 (China); Li Shoujian, E-mail: sjli000616@scu.edu.cn [College of Chemistry, Sichuan University, Key Laboratory of Radiation Physics and Technology (Sichuan University), Ministry of Education, Chengdu 610064 (China)

2011-08-01

It was found that a large number of oxygen-containing functional groups (OFGs) could be created on the surface of hydrothermal carbon (HTC) by simply heating at lower temperature in air during the course of our preliminary experiments which focused on oxidation pre-treatment of pristine HTC for the purpose of grafting functionalization. Especially carboxyl groups on HTC would increase significantly, from 0.53 to 3.70 mmol/g after heat treatment at 300 deg. C. So, effects of heat-treatment on the OFGs on the carbon microsphere were deeply studied to confirm and explain the findings. Experiments involving different materials (HTC, activated carbon and glucose) were performed under varying conditions (heating temperature and time, in air or in Ar atmosphere). A reaction mechanism for newly generating carboxyl groups on HTC surface during heat-treatment process was supposed based on the results from the sample characterization using Boehm titrations, infrared spectra, X-ray photoelectron spectroscopy, energy dispersive spectrometry and elemental analysis. In addition, the as heat-treated product has excellent sorption capability for Pb{sup 2+} and Cd{sup 2+} ions.

Influence of heat treatment temperature on bonding and oxidation ...

Indian Academy of Sciences (India)

The effects of heat treatment temperature on the morphology, composition, chemical bonds, oxidation resistance and compressive strength of diamond particles coated with TiO2 films were characterized through scanning electron microscopy, Fourier transform infrared, Raman spectroscopy, X-ray diffraction analysis, X-ray ...

Application of microjet in heat treatment of aluminium bronzes

Directory of Open Access Journals (Sweden)

Z. Górny

2011-04-01

Full Text Available Mechanical properties of a CuAl10Fe4Ni4 bronze subjected to solution heat treatment and toughening were examined. In solution heattreatment, a microjet was used to raise the cooling rate. A slight increase of mechanical properties was observed.

The Microstructure And Mechanical Properties Of The AlSi17Cu5 Alloy After Heat Treatment

Directory of Open Access Journals (Sweden)

Piątkowski J.

2015-09-01

Full Text Available In the paper results of the microstructure and mechanical properties (HB, Rm and R0,2 of AlSi17Cu5 alloy, subjected by solution heat treatment (500ºC/6h/woda and aging (200ºC/16h/piec are presented. In next step the alloy was modified and heated significantly above the Tliq temperature (separately and together. It was found that the increase in the strength properties of the tested alloy after heat treatment compared to alloys without solution heat treatment and aging was due to precipitation hardening. The applied aging treatment of ingots (preceded by solution heat treatment, causes not only increase in concentration in α(Al solid solution, but also a favorable change of the primary Si crystals morphology. During stereological measurements significant size reduction and change in the morphology of hypereutectic silicon crystals ware found. This effects can be further enhanced by overheating the alloy to a temperature of 920ºC and rapid cooling before casting of the alloy.

The influence of distal-end heat treatment on deflection of nickel-titanium archwire

Directory of Open Access Journals (Sweden)

Marcelo Faria da Silva

2016-02-01

Full Text Available Objective: The aim of this in vitro study was to evaluate the deflection-force behavior of nickel-titanium (NiTi orthodontic wires adjacent to the portion submitted to heat treatment. Material and Methods: A total of 106 segments of NiTi wires (0.019 x 0.025-in and heat-activated NiTi wires (0.016 x 0.022-in from four commercial brands were tested. The segments were obtained from 80 archwires. For the experimental group, the distal portion of each segmented archwire was subjected to heat treatment (n = 40, while the other distal portion of the same archwire was used as a heating-free control group (n = 40. Deflection tests were performed in a temperature-controlled universal testing machine. Unpaired Student's t-tests were applied to determine if there were differences between the experimental and control groups for each commercial brand and size of wire. Statistical significance was set at p < 0.05. Results: There were no statistically significant differences between the tested groups with the same size and brand of wire. Conclusions: Heat treatment applied to the distal ends of rectangular NiTi archwires does not permanently change the elastic properties of the adjacent portions.

Effect of T6 heat treatment on tensile strength of EN AB-48000 alloy modified with strontium

Directory of Open Access Journals (Sweden)

J. Pezda

2011-07-01

Full Text Available Among alloys of non-ferrous metals, aluminum alloys have found their broadest application in foundry industry. Silumins are widely used in automotive, aviation and shipbuilding industries; as having specific gravity nearly three times lower than specific gravity of cast iron. The silumins can be characterized by high mechanical properties. To upgrade mechanical properties of a castings made from silumins one makes use of heat treatment, what leads to change of their structure and advantageously affects on mechanical properties of the silumins. In the paper are presented test results concerning effect of dispersion hardening on change of tensile strength of EN AB-48000 silumin modified with strontium. Investigated alloy was melted in electric resistance furnace. Temperature ranges of solution heat treatment and ageing heat treatment were selected on base of curves from ATD method, recorded for refined alloy and for modified alloy. The heat treatment resulted in change of Rm tensile strength, while performed investigations have enabled determination of temperatures and durations of solution heat treatment and ageing heat treatment, which precondition obtainment of the best tensile strength Rm of the investigated alloy.

Heat treatment of TI-6AL-4V produced by lasercusing

Directory of Open Access Journals (Sweden)

Becker, Thorsten

2015-08-01

Full Text Available LaserCUSING® is a selective laser melting (SLM process that is capable of manufacturing parts by melting powder with heat input from a laser beam. LaserCUSING demonstrates potential for producing the intricate geometries specifically required for biomedical implants and aerospace applications. One main limitation to this form of rapid prototyping is the lack of published studies on the material performance of the resulting material. Studies of the material’s performance are often complicated by dependence on several factors, including starting powder properties, laser parameters, and post-processing heat treatments. This study aims to investigate the mechanical properties of LaserCUSING-produced Ti-6Al-4V and its performance relative to the conventional wrought counterpart. A combination of conventional and LaserCUSING-tailored heat treatments is performed. The resulting microstructures are studied and linked to the properties obtained from hardness tests. The findings highlight that LaserCused Ti-6Al-4V is competitive with traditional materials, provided that optimal parameters are chosen and parts are subject to tailored post-processing. In the as-built condition, LaserCused Ti-6Al-4V displays superior strength and hardness as a result of a martensitic microstructure, and a poorer performance in ductility. However, the material performance can be improved using tailored heat treatments. Careful consideration must be given to suitable post-processing before application in critical components in the aerospace or biomedical industry can occur

Influence of heat treatment on the machinability and corrosion behavior of AZ91 Mg alloy

Directory of Open Access Journals (Sweden)

Swetha Chowdary V

2018-03-01

Full Text Available In the present study, AZ91 Mg alloy was heat treated at 410 °C for 6, 12 and 24 h to investigate the influence of heat treatment on machinability and corrosion behavior. The effect of soaking time on the amount and distribution of Mg17Al12 (β – phase was analyzed under the optical microscope. Microhardness measurements demonstrated the increased hardness with increased heat treatment soaking time, which can be attributed to the solid solution strengthening. The influence of super saturated α-grains on reducing the cutting force (Fz with respect to increased cutting speed was observed as prominent. The corrosion behavior of the heat treated specimens was studied by conducting electrochemical tests. Surprisingly, corrosion rate of heat treated samples was observed as increased compared with the base material. From the results, it is evident that the machinability of AZ91 Mg alloy can be improved by producing super saturated α-grains through heat treatment but at the cost of losing corrosion resistance. Keywords: AZ91 Mg alloy, Solid solution, Turning, Corrosion, Machinability

Technoeconomic Optimization of Waste Heat Driven Forward Osmosis for Flue Gas Desulfurization Wastewater Treatment

Energy Technology Data Exchange (ETDEWEB)

Gingerich, Daniel B [Carnegie Mellon Univ., Pittsburgh, PA (United States); Bartholomew, Timothy V [Carnegie Mellon Univ., Pittsburgh, PA (United States); Mauter, Meagan S [Carnegie Mellon Univ., Pittsburgh, PA (United States)

2017-06-26

With the Environmental Protection Agency’s recent Effluent Limitation Guidelines for Steam Electric Generators, power plants are having to install and operate new wastewater technologies. Many plants are evaluating desalination technologies as possible compliance options. However, the desalination technologies under review that can reduce wastewater volume or treat to a zero-liquid discharges standard have a significant energy penalty to the plant. Waste heat, available from the exhaust gas or cooling water from coal-fired power plants, offers an opportunity to drive wastewater treatment using thermal desalination technologies. One such technology is forward osmosis (FO). Forward osmosis utilizes an osmotic pressure gradient to passively pull water from a saline or wastewater stream across a semi-permeable membrane and into a more concentrated draw solution. This diluted draw solution is then fed into a distillation column, where the addition of low temperature waste heat can drive the separation to produce a reconcentrated draw solution and treated water for internal plant reuse. The use of low-temperature waste heat decouples water treatment from electricity production and eliminates the link between reducing water pollution and increasing air emissions from auxiliary electricity generation. In order to evaluate the feasibility of waste heat driven FO, we first build a model of an FO system for flue gas desulfurization (FGD) wastewater treatment at coal-fired power plants. This model includes the FO membrane module, the distillation column for draw solution recovery, and waste heat recovery from the exhaust gas. We then add a costing model to account for capital and operating costs of the forward osmosis system. We use this techno-economic model to optimize waste heat driven FO for the treatment of FGD wastewater. We apply this model to three case studies: the National Energy Technology Laboratory (NETL) 550 MW model coal fired power plant without carbon

Inactivation of T4-phages by heat and γ-irradiation treatment in respect to sludge hygienization

International Nuclear Information System (INIS)

Farniok, C.; Turanitz, K.; Stehlik, G.; Meyrath, J.

1977-04-01

The effects of γ-irradiation, heat treatment and combined heat/irradiation treatments on T 4 -bacteriophages were studied and evaluated in surviving fractions. To ascertain the extent of inactivation, the formation of plaque was studied in the host organism Escherichia coli K 12 D 10. A 90-minute heat treatment of the bacteriolysat at 55 0 C did not inactivate the bacteriophages, whereas the number of plaque-forming bacteriophages was decreased by 50% at 60 0 C. At 65 0 C a linear correlation of heating period and the logarithm of relative number of phages was observed. After 30 minutes exposure to 70 0 C only few bacteriophages were traced in the plaque test. By inactivation of T 4 -phages after exposure to γ-irradiation a linear correlation of irradiation dose and the logarithm of the relative number of surviving bacteriophages was found. The combined method of heat and irradiation treatments resulted in a synergistic effect. (author)

Modified heat treatment for lower temperature improvement of the mechanical properties of two ultrahigh strength low alloy steels

Science.gov (United States)

Tomita, Yoshiyuki; Okabayashi, Kunio

1985-01-01

In the previous papers, a new heat treatment for improving the lower temperature mechanical propertise of the ultrahigh strength low alloy steels was suggested by the authors which produces a mixed structure of 25 vol pct lower bainite and 75 vol pct martensite through isothermal transformation at 593 K for a short time followed by water quenching (after austenitization at 1133 K). In this paper, two commercial Japanese ultrahigh strength steels, 0.40 pct C-Ni-Cr-Mo (AISI 4340 type) and 0.40 pct C-Cr-Mo (AISI 4140 type), have been studied to determine the effect of the modified heat treatment, coupled above new heat treatment with γ ⇆ α' repctitive heat treatment, on the mechanical properties from ambient temperature (287 K) to 123 K. The results obtained for various test temperatures have been compared with those for the new heat treatment reported previously and the conventional 1133 K direct water quenching treatment. The incorporation of intermediate four cyclic γ ⇆ α' repctitive heat treatment steps (after the initial austenitization at 1133 K and oil quenching) into the new heat treatment reported previously, as compared with the conventional 1133 K direct water quenching treatment, significantly improved 0.2 pct proof stress as well as notch toughness of the 0.40 pct C-Ni-Cr-Mo ultrahigh strength steel at similar fracture ductility levels from 287 to 123 K. Also, this heat treatment, as compared with the conventional 1133 K direct water quenching treatment, significantly improved both 0.2 pct proof stress and notch toughness of the 0.40 pct C-Cr-Mo ultrahigh strength steel with increased fracture ductility at 203 K and above. The microstructure consists of mixed areas of ultrafine grained martensite, within which is the refined blocky, highly dislocated structure, and the second phase lower bainite (about 15 vol pct), which appears in acicular form and partitions prior austenite grains. This newly developed heat treatment makes it possible to modify

Effect of Heat Treatment on the Surface Properties of Activated Carbons

Directory of Open Access Journals (Sweden)

Meriem Belhachemi

2011-01-01

Full Text Available This work reports the effect of heat treatment on the porosity and surface chemistry of two series of activated carbons prepared from a local agricultural biomass material, date pits, by physical activation with carbon dioxide and steam. Both series samples were oxidized with nitric acid and subsequently heat treated under N2 at 973 K in order to study the effect of these treatments in porosity and surface functional groups of activated carbons. When the activated carbons were heat treated after oxidation the surface area and the pore volume increase for both activated carbons prepared by CO2 and steam activations. However the amount of surface oxygen complexes decreases, the samples keep the most stable oxygen surface groups evolved as CO by temperature-programmed desorption experiments at high temperature. The results show that date pits can be used as precursors to produce activated carbons with a well developed porosity and tailored oxygen surface groups.

Heart rate variability during exertional heat stress: effects of heat production and treatment.

Science.gov (United States)

Flouris, Andreas D; Bravi, Andrea; Wright-Beatty, Heather E; Green, Geoffrey; Seely, Andrew J; Kenny, Glen P

2014-04-01

We assessed the efficacy of different treatments (i.e., treatment with ice water immersion vs. natural recovery) and the effect of exercise intensities (i.e., low vs. high) for restoring heart rate variability (HRV) indices during recovery from exertional heat stress (EHS). Nine healthy adults (26 ± 3 years, 174.2 ± 3.8 cm, 74.6 ± 4.3 kg, 17.9 ± 2.8 % body fat, 57 ± 2 mL·kg·(-1) min(-1) peak oxygen uptake) completed four EHS sessions incorporating either walking (4.0-4.5 km·h(-1), 2 % incline) or jogging (~7.0 km·h(-1), 2 % incline) on a treadmill in a hot-dry environment (40 °C, 20-30 % relative humidity) while wearing a non-permeable rain poncho for a slow or fast rate of rectal temperature (T re) increase, respectively. Upon reaching a T re of 39.5 °C, participants recovered until T re returned to 38 °C either passively or with whole-body immersion in 2 °C water. A comprehensive panel of 93 HRV measures were computed from the time, frequency, time-frequency, scale-invariant, entropy and non-linear domains. Exertional heat stress significantly affected 60/93 HRV measures analysed. Analyses during recovery demonstrated that there were no significant differences between HRV measures that had been influenced by EHS at the end of passive recovery vs. whole-body cooling treatment (p > 0.05). Nevertheless, the cooling treatment required statistically significantly less time to reduce T re (p whole-body immersion in 2 °C water results in faster cooling, there were no observed differences in restoration of autonomic heart rate modulation as measured by HRV indices with whole-body cold-water immersion compared to passive recovery in thermoneutral conditions.

Effect of Annealing Heat Treatment to Characteristics of AlDC8 (Al-Si-Cu) Alloy

Energy Technology Data Exchange (ETDEWEB)

Moon, Kyung Man; Lee, Sung-Yul; Lee, Myeong Hoon; Jeong, Jae-Hyun [Korea Maritime and Ocean University, Busan (Korea, Republic of); Baek, Tae-Sil [Pohang College, Pohang (Korea, Republic of)

2015-12-15

ALDC8 (Al-Si-Cu) alloy has been often corroded with pattern of intergranular corrosion in corrosive environments. Thus, in order to improve its corrosion resistance, the effect of annealing heat treatment to corrosion resistance and hardness was investigated with parameters of heating temperatures such as 100 ℃, 200 ℃, 300 ℃, 400 ℃ and 500 ℃ for 1hr. The hardness was varied with annealing temperature and slightly decreased with annealing heat treatment. However, the relation between annealing temperature and hardness agreed not well each other. Corrosion potential was shifted to noble direction and corrosion current density was also decreased with increasing annealing temperature. Moreover, both AC impedance at 10 mHz and polarization resistance on the cyclic voltammogram curve were also increased with increasing annealing temperature. Furthermore, intergranular corrosion was somewhat observed in non heat treatment as well as annealing temperatures at 100 ℃, 200 ℃ and 300 ℃, while, intergranular corrosion was not nearly observed at annealing temperature of 400 ℃, 500 ℃. Consequently, it is considered that the annealing heat treatment of ALDC8 alloy may be an available method not only to inhibit its intergranular corrosion but also to improve its corrosion resistance.

Physical aspects of thermotherapy: A study of heat transport with a view to treatment optimisation

Science.gov (United States)

Olsrud, Johan Karl Otto

1998-12-01

Local treatment with the aim to destruct tissue by heating (thermotherapy) may in some cases be an alternative or complement to surgical methods, and has gained increased interest during the last decade. The major advantage of these, often minimally-invasive methods, is that the disease can be controlled with reduced treatment trauma and complications. The extent of thermal damage is a complex function of the physical properties of tissue, which influence the temperature distribution, and of the biological response to heat. In this thesis, methods of obtaining a well-controlled treatment have been studied from a physical point of view, with emphasis on interstitial laser-induced heating of tumours in the liver and intracavitary heating as a treatment for menorrhagia. Hepatic inflow occlusion, in combination with temperature-feedback control of the output power of the laser, resulted in well defined damaged volumes during interstitial laser thermotherapy in normal porcine liver. In addition, phantom experiments showed that the use of multiple diffusing laser fibres allows heating of clinically relevant tissue volumes in a single session. Methods for numerical simulation of heat transport were used to calculate the temperature distribution and the results agreed well with experiments. It was also found from numerical simulation that the influence of light transport on the damaged volume may be negligible in interstitial laser thermotherapy in human liver. Finite element analysis, disregarding light transport, was therefore proposed as a suitable method for 3D treatment planning. Finite element simulation was also used to model intracavitary heating of the uterus, with the purpose of providing an increased understanding of the influence of various treatment parameters on blood flow and on the depth of tissue damage. The thermal conductivity of human uterine tissue, which was used in these simulations, was measured. Furthermore, magnetic resonance imaging (MRI) was

Viscose liquid heat treatment using plate scraper heat exchanger

Directory of Open Access Journals (Sweden)

K. A. Rashkin

2012-01-01

Full Text Available The current work analyzes the use of different types of heat exchangers, depending on the technology of production. It is taken the detail analysis of the ways of applicability of various types of heat exchangers, depending on the viscosity of the processed product. It is posed the problem of the analytical determination of the required area of heat exchange with the use of differential equations of heat transfer in a moving liquid media, written in cylindrical coordinates, for symmetrical temperature distribution, without taking in account the energy dissipation.

Effect of heat treatment on bend stress relaxation of pure tungsten

International Nuclear Information System (INIS)

Sasaki, Kenta; Nogami, Shuhei; Fukuda, Makoto; Katakai, Yasuyuki; Hasegawa, Akira

2013-01-01

Highlights: • Bend stress relaxation test was performed on the pure tungsten after heat treatment for stress relief. • The BSR ratio of the heat treated specimen was larger than that of the as-received specimen at this temperature region. • Small reduction in the BSR ratio was observed at the temperatures of 500–800 °C. • The BSR ratio of the heat treated specimen decreased significantly at the temperatures of 900–1000 °C. • The BSR ratio decreased significantly in a short time below 0.1 h, and then decreased slowly. -- Abstract: Bend stress relaxation (BSR) tests at temperatures of 500, 600, 800, 900 and 1000 °C for 0.1, 0.5 and 1 h in vacuum were performed on the pure tungsten after heat treatment for stress relief at 900 °C for 1 h. The degree of stress relaxation increased with test temperature. The BSR ratio of the heat treated specimen was larger than that of the as-received specimen at this temperature region. Small reduction in the BSR ratio was observed at the temperatures of 500, 600 and 800 °C. The BSR ratio of the heat treated specimen decreased significantly at the temperatures of 900 and 1000 °C and it was close to that of the as-received specimen. The BSR ratio of the heat treated specimen and the as-received specimen exhibited similar trend of time-evolution. The stress was exponentially relaxed with increasing test time. The BSR ratio decreased significantly in a short time below 0.1 h, and then decreased slowly. Higher activation energy of stress relaxation evaluated by cross-cut method was obtained for the higher temperature

Development of shelf stable, processed, low acid food products using heat-irradiation combination treatments

International Nuclear Information System (INIS)

Minnaar, A.

1998-01-01

The amount of ionizing irradiation needed to sterilize low acid vegetable and starch products (with and without sauces) commercially impairs their sensorial and nutritive qualities, and use of thermal processes for the same purpose may also have an adverse effect on the product quality. A systematic approach to the establishment of optimized combination parameters was developed for heat-irradiation processing to produce high quality, shelf stable, low acid food products. The effects of selected heat, heat-irradiation combination and irradiation treatments on the quality of shelf stable mushrooms in brine and rice, stored at ambient temperature, were studied. From a quality viewpoint, use of heat-irradiation combination treatments favouring low irradiation dose levels offered a feasible alternative to thermally processed or radappertized mushrooms in brine. However, shelf stable rice produced by heat-irradiation combination treatments offered a feasible alternative only to radappertized rice from the standpoint of quality. The technical requirements for the heat and irradiation processing of a long grain rice cultivar from the United States of America oppose each other directly, thereby reducing the feasibility of using heat-irradiation combination processing to produce shelf stable rice. The stability of starch thickened white sauces was found to be affected severely during high dose irradiation and subsequent storage at ambient temperature. However, use of pea protein isolate as a thickener in white sauces was found to have the potential to maintain the viscosity of sauces for irradiated meat and sauce products throughout processing and storage. (author)

Comparative study of heat transfer and wetting behaviour of conventional and bioquenchants for industrial heat treatment

Energy Technology Data Exchange (ETDEWEB)

Fernandes, Peter; Prabhu, K. Narayan [Department of Metallurgical and Materials Engineering, National Institute of Technology Karnataka, Surathkal, P.O. Srinivasnagar 575 025 Mangalore, Karnataka State (India)

2008-02-15

An investigation was conducted to study the suitability of vegetable oils as bioquenchants for industrial heat treatment. The study involved the assessment of the severity of quenching and wetting behaviour of conventional and vegetable oil quench media. Quench severities of sunflower, coconut and palm oils were found to be greater than mineral oil. The quench severity of aqueous media is greater than oil media although their wettability is poor as indicated by their higher contact angles. A dimensionless contact angle parameter defined in this work is found to be a better parameter to compare the wetting behaviour with heat transfer. (author)

Effect of heat treatment on the characteristics of tool steel deposited by the directed energy deposition process

Science.gov (United States)

Park, Jun Seok; Lee, Min-Gyu; Cho, Yong-Jae; Sung, Ji Hyun; Jeong, Myeong-Sik; Lee, Sang-Kon; Choi, Yong-Jin; Kim, Da Hye

2016-01-01

The directed energy deposition process has been mainly applied to re-work and the restoration of damaged steel. Differences in material properties between the base and the newly deposited materials are unavoidable, which may affect the mechanical properties and durability of the part. We investigated the effect of heat treatment on the characteristics of tool steel deposited by the DED process. We prepared general tool steel materials of H13 and D2 that were deposited onto heat-treated substrates of H13 and D2, respectively, using a direct metal tooling process. The hardness and microstructure of the deposited steel before and after heat treatment were investigated. The hardness of the deposited H13 steel was higher than that of wrought H13 steel substrate, while that of the deposited D2 was lower than that of wrought D2. The evolution of the microstructures by deposition and heat treatment varied depending on the materials. In particular, the microstructure of the deposited D2 steel after heat treatment consisted of fine carbides in tempered martensite and it is expected that the deposited D2 steel will have isotropic properties and high hardness after heat treatment.

Aging of iron (hydr)oxides by heat treatment and effects on heavy metal binding

DEFF Research Database (Denmark)

Sørensen, Mette Abildgaard; Starckpoole, M. M.; Frenkel, A. I.

2000-01-01

their transformations caused by heat treatment prior to disposal or aging at a proper disposal site. The transformations were investigated by XRD, SEM, XANES, EXAFS, surface area measurements, pH static leaching tests, and extractions with oxalate and weak hydrochloric acid. It was found that at 600 and 900 °C the iron...... oxides were transformed to hematite, which had a greater thermodynamic stability but less surface area than the initial products. Heat treatment also caused some volatilization of heavy metals (most notably, Hg). Leaching with water at pH 9 (L/S 10, 24 h) and weak acid extraction showed that heat...

The long-term effects of a life-prolonging heat treatment on the Drosophila melanogaster transcriptome suggest that heat shock proteins extend lifespan

DEFF Research Database (Denmark)

Sarup, Pernille Merete; Sørensen, Peter; Loeschcke, Volker

2014-01-01

Heat-induced hormesis, i.e. the beneficial effect of mild heat-induced stress, increases the average lifespan of many organisms. This effect, which depends on the heat shock factor, decreases the log mortality rate weeks after the stress has ceased. To identify candidate genes that mediate......-treated flies. Several hsp70 probe sets were up-regulated 1.7–2-fold in the mildly stressed flies weeks after the last heat treatment (P shock protein, Hsp70, is reported to return to normal levels of expression shortly after heat stress. We...... conclude that the heat shock response, and Hsp70 in particular, may be central to the heat-induced increase in the average lifespan in flies that are exposed to mild heat stress early in life....

Modification of the original color of the Eucalyptus grandis wood by heat treatments

Directory of Open Access Journals (Sweden)

Rosilei Aparecida Garcia

2014-09-01

Full Text Available The objective of this study was to determine the modification of original color of Eucalyptus grandis Hill ex. Maiden wood after heat-treatment. Wood samples were heat-treated under different temperatures (180, 200, 215 and 230ºC and time conditions (15 minutes, 2 and 4 hours. Color analysis were performed on the CIE L*a*b* system by using a Color Eye XTH-X-Rite 200d spectrophotometer. All heat treatments promoted an alteration of the original color of wood. Heat-treated woods presented lower L* (lightness values than untreated wood (control, characterizing the wood darkness, mainly for more severe conditions of temperature and time. Chromatic coordinates (a* and b* showed different behaviors depending on the temperature-time combination. The modification of the original color of the wood allowed the creation of new color patterns, which can add greater value to the studied wood.

Improving the conductivity of single-walled carbon nanotubes films by heat treatment

Energy Technology Data Exchange (ETDEWEB)

Wang Jiaping [State Key Laboratory of High Performance Ceramics and Superfine Microstructures, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Superfine Microstructures, 1295 Dingxi Road, Shanghai 200050 (China); Sun Jing, E-mail: jingsun@mail.sic.ac.c [State Key Laboratory of High Performance Ceramics and Superfine Microstructures, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Superfine Microstructures, 1295 Dingxi Road, Shanghai 200050 (China); Gao Lian, E-mail: liangaoc@online.sh.c [State Key Laboratory of High Performance Ceramics and Superfine Microstructures, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Superfine Microstructures, 1295 Dingxi Road, Shanghai 200050 (China); Liu Yangqiao; Wang Yan; Zhang Jing [State Key Laboratory of High Performance Ceramics and Superfine Microstructures, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Superfine Microstructures, 1295 Dingxi Road, Shanghai 200050 (China); Kajiura, Hisashi; Li Yongming; Noda, Kazuhiro [Advanced Materials Laboratories, Sony Corporation, Atsugi Tec. No. 2, 4-16-1 Okata Atsugi, Kanagawa 243-0021 (Japan)

2009-10-19

A simple heat treatment method was applied to remove surfactants remaining in the single-walled carbon nanotubes (SWNTs) films at 300 deg. C for 5 h in air. Scanning electron microscope (SEM), transmission electron microscope (TEM), X-ray photoelectron spectroscopy (XPS) and reflected light interference microscope (RLIM) were employed to verify the elimination of surfactants. The comprehensive performance, especially the conductivity, could be improved by more than one order after heat treatment. For example, using SDBS as dispersant, the sheet resistance decreased from 782,600 OMEGA/square to 40,460 OMEGA/square with the transmittance of about 99.5% at 550 nm.

Study on mechanical properties of the laminated composite materials with compatible heat treatments

International Nuclear Information System (INIS)

Pashkov, P.O.; Pektemirov, B.G.; Yaroshenko, A.P.

1980-01-01

Considered is the behaviour during axial extension of trilament composite materials, the mechanical properties of which are formed mainly by heat treatment. Application in the composite of the materials with compatible heat treatment is most rational. It is shown that for (ATsMg+N18K8M5T+ATsMg), (KhN78+VKS+KhH78) composites, the constituents of which are relatively plastic and tightly bound with each other, the tensile strength and uniform strain are changed additively

Thermoluminescence and cathodoluminescence studies of calcite and MgO: surface defects and heat treatment

International Nuclear Information System (INIS)

Goeksu, H.Y.; Brown, L.M.

1988-01-01

Some of the problems which preclude accurate thermoluminescence (TL) dating of geologically formed calcite stem from different sample pre-treatment procedures, such as grinding, drilling or pre-heating. It has long been known that grinding can introduce spurious TL in calcite, but there have been wide differences of opinion as to the magnitude of the influence and its importance. Therefore, various grinding and acid-washing procedures have been suggested to avoid spurious thermoluminescence. Various models have been developed to explain the mechanism. We have studied the changes in thermoluminescence (TL) and cathodoluminescence (CL) properties as well as in the spectral composition of the glow from calcite and MgO due to surface defects and heat treatment. It is found that both laboratory heat treatment and surface indents give rise to changes in TL efficiency. (author)

Effect of heat treatment time on microstructure and electrical conductivity in LATP glass ceramics

Energy Technology Data Exchange (ETDEWEB)

Sonigra, Dhiren, E-mail: somans@iitb.ac.in, E-mail: ajit.kulkarni@iitb.ac.in; Soman, Swati, E-mail: somans@iitb.ac.in, E-mail: ajit.kulkarni@iitb.ac.in; Kulkarni, Ajit R., E-mail: somans@iitb.ac.in, E-mail: ajit.kulkarni@iitb.ac.in [Dept. of Metallurgical Engineering and Materials Science, IIT Bombay, Mumbai-400076 (India)

2014-04-24

Glass-ceramic is prepared by heat treatment of melt quenched 14Li{sub 2}O−9Al{sub 2}O{sub 3}−38TiO{sub 2}−39P{sub 2}O{sub 5} glass in the vicinity of crystallization temperature. Growth of ceramic phase is controlled by tuning heat treatment time at fixed temperature. Ceramic phase was identified to be LiTi{sub 2}(PO{sub 4}){sub 3} from X Ray Diffraction analysis. Microstructural evolution of this phase with hold time was observed under high resolution Scanning Electron Microscope. DC conductivity is observed to increase by 4-5 orders of magnitude in this glass-ceramic compared to parent glass. However, formation of pores and cracks with very large heat treatment time seem to hinder further increase of conductivity.

The effects of heat treatment on physical and technological ...

African Journals Online (AJOL)

STORAGESEVER

2009-10-19

Oct 19, 2009 ... surface of wood were used to evaluate the effect of heat treatment on the surface characteristics of ... Some of the products developed by thermal treat- .... boards were stored uncontrolled condition in an unheated room for .... These results can be explained with material loses in ...... Finland-state of the art.

Optimisasi Suhu Pemanasan dan Kadar Air pada Produksi Pati Talas Kimpul Termodifikasi dengan Teknik Heat Moisture Treatment (HMT (Optimization of Heating Temperature and Moisture Content on the Production of Modified Cocoyam Starch Using Heat Moisture Treatment (HMT Technique

Directory of Open Access Journals (Sweden)

I Nengah Kencana Putra

2016-12-01

Full Text Available One of the physically starch modification technique is heat-moisture treatment (HMT. This technique can increase the resistance of starch to heat, mechanical treatment, and acid during processing.  This research aimed to find out the influence of heating temperature and moisture content in the modification process of cocoyam starch  with HMT techniques on the characteristic of product, and then to determine the optimum heating temperature and moisture content in the process. The research was designed with a complete randomized design (CRD with two factors factorial experiment.  The first factor was temperature of the heating consists of 3 levels namely 100 °C, 110 °C, and 120 °C. The second factor was the moisture content of starch which consists of 4 levels, namely 15 %, 20 %, 25 %, and 30 %. The results showed that the heating temperature and moisture content significantly affected water content, amylose content and swelling power of modified cocoyam starch product, but the treatment had no significant effect on the solubility of the product. HMT process was able to change the type of cocoyam starch from type B to type C. The optimum heating temperature and water content on modified cocoyam starch production process was 110 °C and 30 % respectively. Such treatment resulted in a modified cocoyam starch with moisture content of 6.50 %, 50,14 % amylose content, swelling power of 7.90, 0.0009% solubility, paste clarity of 96.310 % T, and was classified as a type C starch.   ABSTRAK Salah satu teknik modifikasi pati secara fisik adalah teknik Heat Moisture Treatment (HMT. Teknik ini dapat meningkatkan ketahanan pati terhadap panas, perlakuan mekanik, dan asam selama pengolahan. Penelitian ini bertujuan untuk mengetahui pengaruh suhu dan kadar air pada proses modifikasi pati talas kimpul dengan teknik HMT terhadap karakteristik produk, dan selanjutnya menentukan suhu dan kadar air yang optimal dalam proses tersebut. Penelitian ini dirancang

Effect of heat treatment on CO2 adsorption of KOH-activated graphite nanofibers.

Science.gov (United States)

Meng, Long-Yue; Park, Soo-Jin

2010-12-15

In this work, graphite nanofibers (GNFs) were successfully expanded intercalating KOH followed by heat treatment in the temperature range of 700-1000 °C. The aim was to improve the CO(2) adsorption capacity of the GNFs by increasing the porosity of GNFs. The effects of heat treatment on the pore structures of GNFs were investigated by N(2) full isotherms, XRD, SEM, and TEM. The CO(2) adsorption capacity was measured by CO(2) isothermal adsorption at 25 °C and 1 atm. From the results, it was found that the activation temperature had a major influence on CO(2) adsorption capacity and textural properties of GNFs. The specific surface area, total pore volume, and mesopore volume of the GNFs increased after heat treatment. The CO(2) adsorption isotherms showed that G-900 exhibited the best CO(2) adsorption capacity with 59.2 mg/g. Copyright © 2010 Elsevier Inc. All rights reserved.

Microsegregation of heat and homogenization treatments in uranium-niobium alloys (U-Nb)

International Nuclear Information System (INIS)

Leal, J.F.

1988-01-01

In the following sections microsegration results in U-3,6 Wt% Nb and U-6,1 Wt% Nb alloys casted in noconsumable electrode arc furnace are presented. The microsegration is studied qualitatively by optical microscopy and quantitatively by electron microprobe. The degree of homogenization has been measured after 800 and 850 0 C heat treatments in tubular resistive furnace. The microstructures after heat treatments are quantitatively analysed to check effects on the casting structures, mainly the variations in solute along the dendrite arm spacing. Some solidification phenomena are then discussed on reference to theorical models of dendritic solidification, including microstructure and microsegregation. The experimental results are compared to theoretical on basis of initial and residual microsegregation after homogenization treatments. The times required for homogenization of the alloys are also discussed in function of the microsegregation from casting structures and the temperatures of the treatments. (author) [pt

Effects of Two-stage Heat Treatment on Delayed Coke and Study of Their Surface Texture Characteristics

Science.gov (United States)

Im, Ui-Su; Kim, Jiyoung; Lee, Seon Ho; Lee, Byung-Rok; Peck, Dong-Hyun; Jung, Doo-Hwan

2017-12-01

In the present study, surface texture features and chemical properties of two types of cokes, made from coal tar by either 1-stage heat treatment or 2-stage heat treatment, were researched. The relationship between surface texture characteristics and the chemical properties was identified through molecular weight distribution, insolubility of coal tar, weight loss with temperature increase, coking yield, and polarized light microscope analysis. Rapidly cleared anisotropy texture in cokes was observed in accordance with the coking temperature rise. Quinoline insolubility and toluene insolubility of coal tar increased with a corresponding increases in coking temperature. In particular, the cokes produced by the 2-stage heat treatment (2S-C) showed surface structure of needle cokes at a temperature approximately 50°C lower than the 1-stage heat treatment (1S-C). Additionally, the coking yield of 2S-C increased by approximately 14% in comparison with 1S-C.

Effect of heat treatment to sweet potato flour on dough properties and characteristics of sweet potato-wheat bread.

Science.gov (United States)

Pérez, Isela Carballo; Mu, Tai-Hua; Zhang, Miao; Ji, Lei-Lei

2017-12-01

The effect of heat treatment at 90, 100, 110 and 120 ℃ for 20 min to sweet potato flour on dough properties and characteristics of sweet potato-wheat bread was investigated. The lightness (L*) and a* of sweet potato flour samples after heat treatment were increased, while the b* were decreased significantly, as well as the particle size, volume and area mean diameter ( p sweet potato flour was observed, where the number of irregular granules increased as the temperature increased from 90 to 120 ℃. Compared with sweet potato flour samples without heat treatment and with heat treatment at 90, 100 and 120 ℃, the gelatinization temperature and enthalpy change of sweet potato flour at 110 ℃ were the lowest, which were 77.94 ℃ and 3.67 J/g, respectively ( p sweet potato flour increased significantly from 1199 ml without heat treatment to 1214 ml at 90 ℃ ( p sweet potato-wheat bread with sweet potato flour after heat treatment increased significantly, which was the largest at 90 ℃ (2.53 cm 3 /g) ( p sweet potato flour could be potentially used in wheat bread production.

Regenerative heat treatments for the extension of the creep life of the superalloy IN-738

International Nuclear Information System (INIS)

Stevens, R.A.; Flewitt, P.E.J.

1979-01-01

Uniaxial creep tests have been performed on the cast nickel-base superalloy IN-738 at 1023K and 1123K. Microstructural damage occurring during creep has been characterised using transmission electron microscopy of surface and extraction replicas. Considerable coarsening of the γ' precipitates occurs during creep causing a progressive loss of creep strength. Intermediate heat treatment of interrupted specimens regenerates a microstructure similar to the original, and on re-testing significant creep life extensions are observed. These heat treatments do not completely recover the creep life due to the development of grain boundary cavitation. Additional heat treatments were performed under a superimposed hydrostatic pressure of 138 MPa to remove these cavities. (orig.) [de

Improved corrosion resistance of aluminum brazing sheet by a post-brazing heat treatment

NARCIS (Netherlands)

Norouzi Afshar, F.; Tichelaar, F.D.; Glenn, A. M.; Taheri, P.; Sababi, M.; Terryn, H.A.; Mol, J.M.C.

2017-01-01

This work studies the influence of the microstructure on the corrosion mechanism and susceptibility of as-brazed aluminum sheet. Various microstructures are obtained using postbrazing heat treatments developed to enhance the corrosion resistance of an AA4xxx/AA3xxx brazing sheet. The heat

Effects of Induction Heat Bending and Heat Treatment on the Boric Acid Corrosion of Low Alloy Steel Pipe for Nuclear Power Plants

Energy Technology Data Exchange (ETDEWEB)

Kim, Ki-Tae; Kim, Young-Sik [Andong National University, Gyeongbuk (Korea, Republic of); Chang, Hyun-Young; Park, Heung-Bae [KEPCO EandC, Gyeongbuk (Korea, Republic of); Sung, Gi-Ho; Shin, Min-Chul [Sungil SIM Co. Ltd, Busan (Korea, Republic of)

2016-11-15

In many plants, including nuclear power plants, pipelines are composed of numerous fittings such as elbows. When plants use these fittings, welding points need to be increased, and the number of inspections also then increases. As an alternative to welding, the pipe bending process forms bent pipe by applying strain at low or high temperatures. This work investigates how heat treatment affects on the boric acid corrosion of ASME SA335 Gr. P22 caused by the induction heat bending process. Microstructure analysis and immersion corrosion tests were performed. It was shown that every area of the induction heat bent pipe exhibited a high corrosion rate in the boric acid corrosion test. This behavior was due to the enrichment of phosphorous in the ferrite phase, which occurred during the induction heat bending process. This caused the ferrite phase to act as a corrosion initiation site. However, when re-heat treatment was applied after the bending process, it enhanced corrosion resistance. It was proved that this resistance was closely related to the degree of the phosphorus segregation in the ferrite phase.

Effect of heat treatment of whole cottonseed on in vitro, in situ and in ...

African Journals Online (AJOL)

Keywords: Amino acid flow, heat treatment, protein degradation, whole cononseed. * Author to whom ... heat-treated soybearu were compared with raw soybeans, it was found that ... et al., 1985; Faldet & Sarter, 1989) while milk fat percenrage.

Influence of lactic acid and post-treatment recovery time on the heat resistance of Listeria monocytogenes.

Science.gov (United States)

Omori, Yasuo; Miake, Kiyotaka; Nakamura, Hiromi; Kage-Nakadai, Eriko; Nishikawa, Yoshikazu

2017-09-18

The aim of this study was to evaluate the effect of lactic acid (LA) with and without organic material at various post-treatment recovery times on the heat resistance of Listeria monocytogenes (Lm). LA decreased Lm numbers; however, the effect was remarkably attenuated by the presence of organic matter. Five strains of Lm were treated with LA and the listericidal effects were compared. The effect of LA varied depending on the strain, with ≥3.0% (w/w) LA required to kill the Lm strains in a short time. The heat resistance of Lm treated with LA was examined with respect to the time interval between the acid treatment and the subsequent manufacturing step. The heat resistance of Lm was shown to significantly increase during the post-treatment period. Heat tolerance (D value) increased up to 3.4-fold compared with the non-treated control bacteria. RNA sequencing and RT-PCR analyses suggested that several stress chaperones, proteins controlled by RecA and associated with high-temperature survival, were involved in the mechanism of enhanced heat resistance. These results are applicable to manufacturers when LA and heat treatment methods are utilized for the effective control of Lm in foods. Copyright © 2017 The Authors. Published by Elsevier B.V. All rights reserved.

Significance of heat-moisture treatment conditions on the pasting and gelling behaviour of various starch-rich cereal and pseudocereal flours.

Science.gov (United States)

Collar, Concha

2017-10-01

The impact of heat-moisture treatment processing conditions (15%, 25%, and 35% moisture content; 1, 3, and 5 h heating time at 120 ℃) on the viscosity pasting and gelling profiles of different grain flours matrices (barley, buckwheat, sorghum, high β-glucan barley, and wheat) was investigated by applying successive cooking and cooling cycles to rapid visco analyser canisters with highly hydrated samples (3.5:25, w:w). At a milder heat-moisture treatment conditions (15% moisture content, 1 h heating time), except for sorghum, heat-moisture treatment flours reached much higher viscosity values during earlier pasting and subsequent gelling than the corresponding native counterparts. Besides heat-moisture treatment wheat flour, the described behaviour found also for non-wheat-treated flours has not been previously reported in the literature. An increased hydrophobicity of prolamins and glutelins in low moisture-short heating time heat-moisture treatment of non-wheat flours with high protein content (12.92%-19.95%) could explain the enhanced viscosity profile observed.

Effect of heat treatment on polyphenol oxidase and peroxidase ...

African Journals Online (AJOL)

Effect of heat treatment (55°C/20 min) on polyphenol oxidase (PPO) and peroxidase (POD) activities and total phenolic compounds was investigated in Algerian dates (Deglet Nour variety) at Tamar (fully ripe) stage and in dates stored for 5 months at ambient temperature and in cold storage (10°C). Results obtained ...

Predicting outgrowth and inactivation of Clostridium perfringens in meat products during low temperature long time heat treatment

DEFF Research Database (Denmark)

Duan, Zhi; Holst Hansen, Terese; Hansen, Tina Beck

OBJECTIVE Sous-vide cooking and molecular gastronomy has started a wave of experimenting with Low Temperature Long Time (LTLT) heat treatments. Heat treatments, at temperatures as low as 50°C, have been suggested by celebrity chefs. LTLT treatments often take hours to reach to the final core...

Effects of the Solid Solution Heat Treatment on the Corrosion Resistance Property of SSC13 Cast Alloy

Energy Technology Data Exchange (ETDEWEB)

Kim, Kuk-Jin [Hi-Sten Co., Ltd., Gimhae (Korea, Republic of); Lim, Su Gun [Gyeongsang National University, Jinju (Korea, Republic of); Pak, S. J. [Gachon BioNano Research Institute, Gachon University, Sungnam (Korea, Republic of)

2015-04-15

Recently, Stainless steels have been increasingly selected as the fitting or the valve materials of water pipes as the human health issue is getting higher and higher. Therefore, the connectors attached at pipes to deliver water are exposed to more severe environments than the pipes because crevice or galvanic corrosion is apt to occur at the fittings or the valves. Effects of the solid solution annealing, cooling rate after this heat treatment, and passivation on the corrosion properties of the shell mold casted SSC13 (STS304 alloy equivalent) were studied. The heating and quenching treatment more or less reduced hardness but effectively improved corrosion resistance. It was explained by the reduction of delta ferrite contents. Independent of heat treatment, the chemical passivation treatment also lowered corrosion rate but the improvement of corrosion resistance depended on temperature and time for passivation treatment indicating that the optimum conditions for passivation treatment were the bath temperature of 34 .deg. C and operating time of 10 minutes. Therefore it is suggested that the corrosion resistance of SSC13 can be effectively improved with the heat treatment, where SSC13 is heated for 10 minutes at 1120 °C and quenched and passivation treatment, where SSC13 is passivated for at least 10 seconds at 34 °C nitric acid solution.

Influence of Heat Treatment on the Morphologies of Copper Nanoparticles Based Films by a Spin Coating Method

Directory of Open Access Journals (Sweden)

Wei Liu

2017-01-01

Full Text Available We have investigated the influence of heat treatment on the morphologies of copper nanoparticles based films on glass slides by a spin coating method. The experiments show that heat treatment can modify the sizes and morphologies of copper nanoparticles based films on glass slides. We suggest that through changing the parameters of heat treatment process may be helpful to vary the scattering and absorbing intensity of copper nanoparticles when used in energy harvesting/conversion and optical devices.

Heat treatment of processing sludge of ornamental rocks: application as pozzolan in cement matrices

Directory of Open Access Journals (Sweden)

J.G. Uliana

Full Text Available The sector of ornamental rocks produces significant volume of waste during the sawing of the blocks and demand to find ways to recycle, given its environmental impact. Considering the possibilities of use of industrial by-products as mineral admixtures, aiming at sustainable development in the construction industry, this paper aims to study the performance of the processing sludge of ornamental rocks and grinding after heat treatment, based on their potential application as partial substitute for cement. The residue was characterized, cast and milled to produce glassy material. Was analyzed the mechanical performance and pozzolanic activity with partial replacement of cement by waste in natural condition and after heat treatment in mortars for comparison. The results were promising, so it was possible to verify that after heat treatment, the treated waste is presented as a material with pozzolanic characteristics.

Examination of the influence of heat treatment on the properties of Al-Si alloys

Energy Technology Data Exchange (ETDEWEB)

Vuksanovic, D.; Rakocevic, S. [Faculty of Metallurgy, Podgorica (RS); Markovic, S. [Faculty of Technology and Metallurgy, Belgrade (RS); Petrovic, T. [Institute ' Kirilo Savic' , Belgrade (RS); Kovacevic, K. [Institute for Ferrous Metallurgy (RS); Tripkovic, S. [H.K. Petar Drapsin, Mladenovac (RS)

2007-08-15

In this paper the influence of heat treatment on the structural and mechanical properties of Al-Si alloys was investigated. Silicon content in the examined alloys was in the range 11 to 14%, the contents of the other alloying elements were in the standard range but all alloys were modified with strontium. The regime of the applied heat treatment was quenching (520 C/6h - cooling in water) + aging (205oC/7h - air cooling). The examinations were carried out at room temperature as well as at 250 C and 300 C. The obtained results showed a positive influence of the applied heat treatment on the mechanical properties of the examined alloys. The improvement of the mechanical properties can be considered as a consequence of a redistribution and change of morphology of the phases present in the structure of the alloys. (orig.)

Effect of grain orientation and heat treatment on mechanical properties of pure W

Energy Technology Data Exchange (ETDEWEB)

Noto, Hiroyuki, E-mail: noto_hiroyuki@iae.kyoto-u.ac.jp [Graduate School of Energy Science, Kyoto University, Kyoto 611-0011 (Japan); Research Fellow of Japan Society for the Promotion of Science (Japan); Taniguchi, Shuichi [Graduate School of Energy Science, Kyoto University, Kyoto 611-0011 (Japan); Kurishita, Hiroaki; Matsuo, Satoru [International Research Center for Nuclear Materials Science, Institute for Materials Research, Tohoku University, Oarai, Ibaraki 311-1313 (Japan); Ukita, Takashi; Tokunaga, Kazutoshi [Institute for Applied Mechanics, Kyushu University, Kasuga, Fukuoka 816-8580 (Japan); Kimura, Akihiko [Institute of Advanced Energy, Kyoto University, Kyoto 611-0011 (Japan)

2014-12-15

The effect of grain orientation, heat-treatment temperature and test temperature on the mechanical properties of tungsten (W), which vary depending on plastic working and fabrication process, was investigated by mechanical testing of tensile or bending. Heavily worked W samples (1.5–2.0 mm in the final thickness) exhibit degradation of fracture strength due to recrystallization embrittlement after heat-treatment at 1240 °C (temperature of diffusion bonding between W and a candidate material of the Fe base support structure). On the other hand, W samples with lower thickness reduction rates do not suffer degradation of fracture strength after heating up to around 1300 °C, and show somewhat higher fracture strength by heat-treatment below 1300 °C than the samples in the as-received state. The observed behavior is a reflection of recovery of dislocations introduced by plastic working. High temperature tensile testing of ITER grade W with an anisotropic grain structure and S-TUN with an equiaxed grain structure revealed that both W grades exhibit plastic elongation at temperatures higher than 200 °C with essentially the same temperature dependence of yield strength, which is relatively insensitive to grain orientation in the structure at 200–1300 °C.

Effect of grain orientation and heat treatment on mechanical properties of pure W

International Nuclear Information System (INIS)

Noto, Hiroyuki; Taniguchi, Shuichi; Kurishita, Hiroaki; Matsuo, Satoru; Ukita, Takashi; Tokunaga, Kazutoshi; Kimura, Akihiko

2014-01-01

The effect of grain orientation, heat-treatment temperature and test temperature on the mechanical properties of tungsten (W), which vary depending on plastic working and fabrication process, was investigated by mechanical testing of tensile or bending. Heavily worked W samples (1.5–2.0 mm in the final thickness) exhibit degradation of fracture strength due to recrystallization embrittlement after heat-treatment at 1240 °C (temperature of diffusion bonding between W and a candidate material of the Fe base support structure). On the other hand, W samples with lower thickness reduction rates do not suffer degradation of fracture strength after heating up to around 1300 °C, and show somewhat higher fracture strength by heat-treatment below 1300 °C than the samples in the as-received state. The observed behavior is a reflection of recovery of dislocations introduced by plastic working. High temperature tensile testing of ITER grade W with an anisotropic grain structure and S-TUN with an equiaxed grain structure revealed that both W grades exhibit plastic elongation at temperatures higher than 200 °C with essentially the same temperature dependence of yield strength, which is relatively insensitive to grain orientation in the structure at 200–1300 °C

Microstructure and Mechanical Properties of Inconel 625 Alloy on Low Carbon Steel by Heat Treatment after Overlay Welding

International Nuclear Information System (INIS)

Kim, Seungpil; Jang, Jaeho; Kim, Jungsoo; Kim, Byung Jun; Sohn, Keun Yong; Nam, Dae-Geun

2016-01-01

Overlay welding technique is one of methods used to improve metal mechanical properties such as strength, toughness and corrosion resistance. Generally, Inconel 625 alloy is used for overlay welding layer on low carbon steels for economic consideration. However, the method produces some problems in the microstructure of the cast structure and some defects, caused by the elevated temperatures of the overlay process. To resolve these problems, heat treatments are required. In this study, Inconel 625 alloy was welded on a low carbon steel by the overlay welding process to investigate the resulting microstructure and mechanical properties. A double heat treatment was performed to improve the mechanical properties of the welding and substrate layers. It was found that Inconel 625 alloy had an austenite microstructure after the first heat treatment, but the low carbon steel had a ferrite-pearlite microstructure after the second heat treatment. After the double heat treatment, the sample showed the optimum hardness because of grain refinement and homogenization of the microstructure.

Microstructure and Mechanical Properties of Inconel 625 Alloy on Low Carbon Steel by Heat Treatment after Overlay Welding

Energy Technology Data Exchange (ETDEWEB)

Kim, Seungpil; Jang, Jaeho; Kim, Jungsoo; Kim, Byung Jun; Sohn, Keun Yong; Nam, Dae-Geun [Korea Institute of Industrial Technology, Busan (Korea, Republic of)

2016-08-15

Overlay welding technique is one of methods used to improve metal mechanical properties such as strength, toughness and corrosion resistance. Generally, Inconel 625 alloy is used for overlay welding layer on low carbon steels for economic consideration. However, the method produces some problems in the microstructure of the cast structure and some defects, caused by the elevated temperatures of the overlay process. To resolve these problems, heat treatments are required. In this study, Inconel 625 alloy was welded on a low carbon steel by the overlay welding process to investigate the resulting microstructure and mechanical properties. A double heat treatment was performed to improve the mechanical properties of the welding and substrate layers. It was found that Inconel 625 alloy had an austenite microstructure after the first heat treatment, but the low carbon steel had a ferrite-pearlite microstructure after the second heat treatment. After the double heat treatment, the sample showed the optimum hardness because of grain refinement and homogenization of the microstructure.

Effect of heat treatment on microstructure and mechanical properties of PIP-SiC/SiC composites

Energy Technology Data Exchange (ETDEWEB)

Zhao, Shuang, E-mail: zhsh6007@126.com [Key Laboratory of Advanced Ceramic Fibres and Composites, College of Aerospace and Materials Engineering, National University of Defense Technology, Changsha 410073 (China); School of Mechanical, Aerospace, and Civil Engineering, University of Manchester, Manchester M13 9PL (United Kingdom); Zhou, Xingui; Yu, Jinshan [Key Laboratory of Advanced Ceramic Fibres and Composites, College of Aerospace and Materials Engineering, National University of Defense Technology, Changsha 410073 (China); Mummery, Paul [School of Mechanical, Aerospace, and Civil Engineering, University of Manchester, Manchester M13 9PL (United Kingdom)

2013-01-01

Continuous SiC fibre reinforced SiC matrix composites (SiC/SiC) have been studied as materials for heat resistant and nuclear applications. Thermal stability is one of the key issues for SiC/SiC composites. In this study, 3D SiC/SiC composites are fabricated via the polymer impregnation and pyrolysis (PIP) process, and then heat treated at 1400 Degree-Sign C, 1600 Degree-Sign C and 1800 Degree-Sign C in an inert atmosphere for 1 h, respectively. The effect of heat treatment on microstructure and mechanical properties of the composites is investigated. The results indicate that the mechanical properties of the SiC/SiC composites are significantly improved after heat treatment at 1400 Degree-Sign C mainly because the mechanical properties of the matrix are greatly improved due to crystallisation. With the increasing of heat treatment temperature, the properties of the composites are conversely decreased because of severe damage of the fibres and the matrix.

Enhancement of contractile force generation of artificial skeletal muscle tissues by mild and transient heat treatment.

Science.gov (United States)

Sato, Masanori; Ikeda, Kazushi; Kanno, Shota; Ito, Akira; Kawabe, Yoshinori; Kamihira, Masamichi

2014-01-01

Artificial skeletal muscle tissues composed of cells are expected to be used for applications of regenerative medicine and drug screening. Generally, however, the physical forces generated by tissue-engineered skeletal muscle are lower than those of skeletal muscle tissues found in the body. Local hyperthermia is used for many diseases including muscle injuries. It was recently reported that mild heat treatment improved skeletal muscle functions. In this study, we investigated the effects of mild heat treatment on the tissue-engineered skeletal muscle tissues in vitro. We used magnetite cationic liposomes to label C2C12 myoblast cells magnetically, and constructed densely packed artificial skeletal muscle tissues by using magnetic force. Cell culture at 39°C promoted the differentiation of myoblast cells into myotubes. Moreover, the mild and transient heat treatment improved the contractile properties of artificial skeletal muscle tissue constructs. These findings indicate that the culture method using heat treatment is a useful approach to enhance functions of artificial skeletal muscle tissue.

Research on Crack-Filling Heat Treatment and Hydrogen Permeation Test of Self-healing Tritium Permeation Barriers

Science.gov (United States)

Liu, Dawei; Wang, Yan; Zhang, Ying; Ouyang, Taoyuan; Zhou, Tong; Fang, Xuanwei; Suo, Jinping

2018-03-01

A TiC + mixture (TiC/Al2O3 (1:1 wt.%)) +Al2O3 self-healing triple layer coating (TLC) was designed and manufactured by our group, and the crack-filling heat treatment process had been roughly explored in the past. In this work, the accelerating test with a thick TiC + mixture (TiC/Al2O3 (1:1 wt.%)) double-layer coating (DLC) was carried out. The DLC coating warped when the heat treatment temperature was lower than 550 °C, which was rare in similar researches, and it crushed into fan-shaped pieces when the treatment temperature was higher than 650 °C. The two different spalling failures were explained by weight gain, porosity and stress analyses. The heating rate had a significant effect. The bonding strength and hydrogen permeation of the TLC samples were also tested. Remaining at 650 °C for 40 h was proved to be an optimal crack-filling heat treatment process, considering the hydrogen resistance.

Comparison of the effects of different heat treatment processes on rheological properties of cake and bread wheat flours.

Science.gov (United States)

Bucsella, Blanka; Takács, Ágnes; Vizer, Viktoria; Schwendener, Urs; Tömösközi, Sándor

2016-01-01

Dry and hydrothermal heat treatments are efficient for modifying the technological-functional and shelf-life properties of wheat milling products. Dry heat treatment process is commonly used to enhance the volume of cakes. Hydrothermal heat treatment makes wheat flours suitable as thickener agents. In this study, cake and bread wheat flours that differed in baking properties were exposed to dry (100 °C, 12 min) and hydrothermal (95 °C, 5 min, 5-20 l/h water) heat treatments. Rheological differences caused by the treatments were investigated in a diluted slurry and in a dough matrix. Dry heat treatment resulted in enhanced dough stability. This effect was significantly higher in the cake flour than the bread flour. Altered viscosity properties of the bread flour in the slurry matrix were also observed. The characteristics of hydrothermally treated samples showed matrix dependency: their viscosity increases in the slurry and decreases in the dough matrix. These results can support us to produce flour products with specific techno-functional properties. Copyright © 2015 Elsevier Ltd. All rights reserved.

Surface engineering and heat treatment

International Nuclear Information System (INIS)

Morton, P.H.

1991-01-01

This book is the proceedings of a Conference organised jointly by The Institute of Metals and The Centre for Exploitation of Science and Technology (CEST). It sets out to review this role and point the way to the future by collecting together a series of invited papers written by noted authorities in their fields. The opening review by CEST highlights the economic and industrial importance of Surface Engineering and is followed by a group of four articles devoted to specific branches of industry. Several technical papers then describe various aspects of the development of heat treatment over the last twenty-five years. These are followed by papers describing advances made possible by new technologies such as plasma, laser and ion beam. A separate abstract has been prepared for a paper on materials aspects of ion beam technology. (author)

Impact of Surface Potential on Apatite Formation in Ti Alloys Subjected to Acid and Heat Treatments.

Science.gov (United States)

Yamaguchi, Seiji; Hashimoto, Hideki; Nakai, Ryusuke; Takadama, Hiroaki

2017-09-24

Titanium metal (Ti) and its alloys are widely used in orthopedic and dental fields. We have previously shown that acid and heat treatment was effective to introduce bone bonding, osteoconduction and osteoinduction on pure Ti. In the present study, acid and heat treatment with or without initial NaOH treatment was performed on typical Ti-based alloys used in orthopedic and dental fields. Dynamic movements of alloying elements were developed, which depended on the kind of treatment and type of alloy. It was found that the simple acid and heat treatment enriched/remained the alloying elements on Ti-6Al-4V, Ti-15Mo-5Zr-3Al and Ti-15Zr-4Nb-4Ta, resulting in neutral surface charges. Thus, the treated alloys did not form apatite in a simulated body fluid (SBF) within 3 days. In contrast, when the alloys were subjected to a NaOH treatment prior to an acid and heat treatment, alloying elements were selectively removed from the alloy surfaces. As a result, the treated alloys became positively charged, and formed apatite in SBF within 3 days. Thus, the treated alloys would be useful in orthopedic and dental fields since they form apatite even in a living body and bond to bone.

Quality of mango nectar processed by high-pressure homogenization with optimized heat treatment.

Science.gov (United States)

Tribst, Alline Artigiani Lima; Franchi, Mark Alexandrow; de Massaguer, Pilar Rodriguez; Cristianini, Marcelo

2011-03-01

This work aimed to evaluate the effect of high-pressure homogenization (HPH) with heat shock on Aspergillus niger, vitamin C, and color of mango nectar. The nectar was processed at 200 MPa followed by heat shock, which was optimized by response surface methodology by using mango nectar ratio (45 to 70), heat time (10 to 20), and temperature (60 to 85 °C) as variables. The color of mango nectar and vitamin C retention were evaluated at the optimized treatments, that is, 200 MPa + 61.5 °C/20 min or 73.5 °C/10 min. The mathematical model indicates that heat shock time and temperature showed a positive effect in the mould inactivation, whereas increasing ratio resulted in a protective effect on A. niger. The optimized treatments did not increase the retention of vitamin C, but had positive effect for the nectar color, in particular for samples treated at 200 MPa + 61.5 °C/20 min. The results obtained in this study show that the conidia can be inactivated by applying HPH with heat shock, particularly to apply HPH as an option to pasteurize fruit nectar for industries.

On board short-time high temperature heat treatment of ballast water: a field trial under operational conditions.

Science.gov (United States)

Quilez-Badia, Gemma; McCollin, Tracy; Josefsen, Kjell D; Vourdachas, Anthony; Gill, Margaret E; Mesbahi, Ehsan; Frid, Chris L J

2008-01-01

A ballast water short-time high temperature heat treatment technique was applied on board a car-carrier during a voyage from Egypt to Belgium. Ballast water from three tanks was subjected for a few seconds to temperatures ranging from 55 degrees C to 80 degrees C. The water was heated using the vessel's heat exchanger steam and a second heat exchanger was used to pre-heat and cool down the water. The treatment was effective at causing mortality of bacteria, phytoplankton and zooplankton. The International Maritime Organization (IMO) standard was not agreed before this study was carried out, but comparing our results gives a broad indication that the IMO standard would have been met in some of the tests for the zooplankton, in all the tests for the phytoplankton; and probably on most occasions for the bacteria. Passing the water through the pump increased the kill rate but increasing the temperature above 55 degrees C did not improve the heat treatment's efficacy.

Gas Furnace with Pulsed Feeding of the Heating Agent for Volume Precision Heat Treatment of CCM Rolls

Science.gov (United States)

Moroz, V. I.; Egorova, V. M.; Gusev, S. V.

2001-05-01

A standard chamber batch furnace of the Severstal' plant has been modified for precision heat treatment of CCM rolls. The certification tests of a charge of rolls from steel 24KhM1F have shown the technical and economical advantages of the new design.

热处理与可持续发展%Heat Treatment and Sustainable Development

Institute of Scientific and Technical Information of China (English)

徐跃明; 樊东黎

2001-01-01

In the view point of sustainable development，there exist some serious problems，such as higher energy consumption，environmental pollution，oxidation and decarburization of steels，in the heat treatment industry of China．In order to keep the sustainable development of heat treatment industry in China，something must be done．First of all is to heighten sustainable development consciousness．At the same time，it is necessary to strengthen technology innovation and speed up improving traditional heat treatment industry with high technology，to develop the clean production of heat treatment and popularize the application of efficient，energy saving and none or less oxidation heat treatment technology．A great attention is still paid to the certification of ISO9000 and ISO14000 series standard and heat treatment industry standard to raise modernized and standard management level of enterprises．%从可持续发展的角度分析，我国热处理行业主要存在能耗高、环境污染严重、氧化脱碳严重3大问题。目前，热处理行业仍普遍存在节能环保意识不强，缺乏有效的管理措施，技术落后等现象。面对新的挑战，热处理要在21世纪得到持续发展，必须从“源消减”做起。首先要加强可持续发展的意识；加强技术创新，加快用高新技术改造传统热处理产业的步伐；积极发展热处理清洁生产，推广高效、节能、少无氧化热处理技术；重视ISO9000、ISO14000标准系列认证和行业达标验收工作，全面提高企业现代化、规范化管理水平。

Effects of heat treatment on mechanical properties of h13 steel

Science.gov (United States)

Guanghua, Yan; Xinmin, Huang; Yanqing, Wang; Xingguo, Qin; Ming, Yang; Zuoming, Chu; Kang, Jin

2010-12-01

Heat treatment on the mechanical properties of H13 hot working die steel for die casting is discussed. The H13 steel for die casting was treated by different temperatures of vacuum quenching, tempering, and secondary tempering to investigate its mechanical properties. Strength, plasticity, hardness, and impact toughness of the H13 hot working die steel for die casting were measured. Microstructure, grain size, and carbide particle size after heat treatment have a great impact on the mechanical properties of H13 hot working die steel for die casting. The microstructure of the H13 was analyzed by scanning electron microscopy (SEM) and by a metallographic microscope. It is found that H13 exhibits excellent mechanical properties after vacuum quenching at 1050°C and twice tempering at 600°C.

Design and performance of a new induction furnace for heat treatment of superconducting radiofrequency niobium cavities.

Science.gov (United States)

Dhakal, Pashupati; Ciovati, Gianluigi; Rigby, Wayne; Wallace, John; Myneni, Ganapati Rao

2012-06-01

Superconducting radio frequency (SRF) cavities made of high purity niobium (Nb) are the building blocks of many modern particle accelerators. The fabrication process includes several cycles of chemical and heat treatment at low (∼120 °C) and high (∼800 °C) temperatures. In this contribution, we describe the design and performance of an ultra-high-vacuum furnace which uses an induction heating system to heat treat SRF cavities. Cavities are heated by radiation from the Nb susceptor. By using an all-niobium hot zone, contamination of the Nb cavity by foreign elements during heat treatment is minimized and allows avoiding subsequent chemical etching. The furnace was operated up to 1400 °C with a maximum pressure of ∼1 × 10(-5) Torr and the maximum achievable temperature is estimated to be higher than 2000 °C. Initial results on the performance of a single cell 1.5 GHz cavity made of ingot Nb heat treated at 1200 °C using this new induction furnace and without subsequent chemical etching showed a reduction of the RF losses by a factor of ∼2 compared to cavities made of fine-grain Nb which underwent standard chemical and heat treatments.

Photosynthetic responses to heat treatments at different temperatures and following recovery in grapevine (Vitis amurensis L.) leaves.

Science.gov (United States)

Luo, Hai-Bo; Ma, Ling; Xi, Hui-Feng; Duan, Wei; Li, Shao-Hua; Loescher, Wayne; Wang, Jun-Fang; Wang, Li-Jun

2011-01-01

The electron transport chain, Rubisco and stomatal conductance are important in photosynthesis. Little is known about their combined responses to heat treatment at different temperatures and following recovery in grapevines (Vitis spp.) which are often grown in climates with high temperatures. The electron transport function of photosystem II, the activation state of Rubisco and the influence of stomatal behavior were investigated in grapevine leaves during heat treatments and following recovery. High temperature treatments included 35, 40 and 45°C, with 25°C as the control and recovery temperature. Heat treatment at 35°C did not significantly (P>0.05) inhibit net photosynthetic rate (P(n)). However, with treatments at 40 and 45°C, P(n) was decreased, accompanied by an increase in substomatal CO(2) concentration (C(i)), decreases in stomatal conductance (g(s)) and the activation state of Rubisco, and inhibition of the donor side and the reaction center of PSII. The acceptor side of PSII was inhibited at 45°C but not at 40°C. When grape leaves recovered following heat treatment, P(n), g(s) and the activation state of Rubisco also increased, and the donor side and the reaction center of PSII recovered. The increase in P(n) during the recovery period following the second 45°C stress was slower than that following the 40°C stress, and these increases corresponded to the donor side of PSII and the activation state of Rubisco. Heat treatment at 35°C did not significantly (P>0.05) influence photosynthesis. The decrease of P(n) in grape leaves exposed to more severe heat stress (40 or 45°C) was mainly attributed to three factors: the activation state of Rubisco, the donor side and the reaction center of PSII. However, the increase of P(n) in grape leaves following heat stress was also associated with a stomatal response. The acceptor side of PSII in grape leaves was responsive but less sensitive to heat stress.

Curie Temperature and Microstructural Changes Due to the Heating Treatment of Magnetic Amorphous Materials

Directory of Open Access Journals (Sweden)

Gondro J.

2016-03-01

Full Text Available Three distinct alloys: Fe86Zr7Nb1Cu1B5, Fe82Zr7Nb2Cu1B8, and Fe81Pt5Zr7Nb1Cu1B5 were characterized both magnetically and structurally. The samples, obtained with spinning roller method as a ribbons 3 mm in width and 20 μm thick, were investigated as-quenched and after each step of a multi steps heating treatment procedure. Each sample was annealed at four steps, fifteen minutes at every temperature, starting from 573K+600K up to +700K depending on type of alloy. Mössbauer spectroscopy data and transmission electron microscope (HRE M pictures confirmed that the as-quenched samples are fully amorphous. This is not changed after the first stages of treatment heating leads to a reduction of free volumes. The heating treatment has a great influence on the magnetic susceptibilities. The treatment up to 600K improves soft magnetic properties: an χ increase was observed, from about 400 to almost 1000 for the samples of alloys without Pt, and from about 200 to 450 at maximum, for the Fe81Pt5Zr7Nb1Cu1B5. Further heating, at more elevated temperatures, leads to magnetic hardening of the samples. Curie temperatures, established from the location of Hopkinson’s maxima on the χ(T curve are in very good agreement with those obtained from the data of specific magnetization, σ(T, measured in a field of 0.75T. As a critical parameter β was chosen to be equal 0.36 for these calculations, it confirmed that the alloys may be considered as ferromagnetic of Heisenberg type. Heating treatment resulted in decreasing of TC. These changes are within a range of several K.

Effect of Stabilization Heat Treatment on Time-Dependent Polarization Losses in Sintered Nd-Fe-B Permanent Magnets

Directory of Open Access Journals (Sweden)

Tuominen S.

2013-01-01

Full Text Available Some companies in the motor and generator industry utilizing sintered NdFeB magnets have adopted pre-ageing heat treatment in order to improve the stability of the magnets. The parameters of this stabilization heat treatment are based mainly on assumptions rather than on any published research results. In this work, the effects of pre-ageing treatment on the time-dependent polarization losses of two different types of commercial sintered NdFeB magnets were studied. The material showing the squarer J(H curve did not benefit from the pre-ageing treatment, since it seems to be stable under a certain critical temperature. In contrast, a stabilizing effect was observed in the material showing rounder J(H curve. After the stabilization heat treatment, the polarization of the magnets was found to be at lower level, but unchanged over a certain period of time. The length of this period depends on the temperature and the duration of the pre-ageing treatment. In addition, our analysis reveals that the stabilization heat treatment performed in an open circuit condition does not stabilize the magnet uniformly.

Regularities of texture formation in alloys undergoing phase transformations during heat treatment and plastic working

International Nuclear Information System (INIS)

Ageev, N.V.; Babarehko, A.A.

1983-01-01

Peculiarities of texture formation in metals undergoing phase transformations in the temperature range of heat treatment and hot working are investigated theoretically and experimentally. A low-temperature phase after hot working is shown to inherite a high-temperature phase texture due to definite orientation conformity during phase transformation. Strengthened heat and thermomechanical treatments, as a rule, do not destroy material texture but change it

Surface chemistry of polyacrylonitrile- and rayon-based activated carbon fibers after post-heat treatment

International Nuclear Information System (INIS)

Chiang Yuchun; Lee, C.-Y.; Lee, H.-C.

2007-01-01

Polyacrylonitrile- and rayon-based activated carbon fibers (ACFs) subject to heat treatment were investigated by means of elemental analyzer, and X-ray photoelectron spectroscopy (XPS). The total ash content of all ACFs was also analyzed. The adsorption of benzene, carbon tetrachloride and water vapor on ACFs was determined to shed light on the role of surface chemistry on gas adsorption. Results show that different precursors resulted in various elemental compositions and imposed diverse influence upon surface functionalities after heat treatment. The surface of heat-treated ACFs became more graphitic and hydrophobic. Three distinct peaks due to C, N, and O atoms were identified by XPS, and the high-resolution revealed the existence of several surface functionalities. The presence of nitride-like species, aromatic N-imines, or chemisorbed nitrogen oxides was found to be of great advantage to adsorption of water vapor or benzene, but the pyridine-N was not. Unstable complexes on the surface would hinder the fibers from adsorption of carbon tetrachloride. The rise in total ash content or hydrogen composition was of benefit to the access of water vapor. Modifications of ACFs by heat treatment have effectively improved adsorption performance

Effect of Heat Shock Treatment and Aloe Vera Coating to Chilling Injury Symptom in Tomato (Lycopersicon asculantum Mill.

Directory of Open Access Journals (Sweden)

Sutrisno

2012-04-01

Full Text Available This research was undertaken to determine the effect of length in heat shock and edible coating as pre-storage treatment to Chilling Injury (CI symptom reflected by ion leakage induced and quality properties in tomato (Lycopersicon asculantum Mill.. Heat Shock Treatment (HST was conducted at three different levels of length, which were, 20; 40 and 60 min. Edible coating was conducted using aloe vera gel. The result showed that HST and Aloe Vera Coating (AVC were more effective to reduce CI symptom at lower chilling storage. Prolong exposure to heated water may delay climacteric peak. The length of heat shock, AVC treatment and low temperature storage significantly affected the tomato quality parameter but not significantly different for each treatment except weight loss. HST for 20 min at ambient temperature was significantly different to other treatment.

Heat treatment for improvement in lower temperature mechanical properties of 0.40 pct C-Cr-Mo ultrahigh strength steel

Science.gov (United States)

Tomita, Yoshiyuki; Okabayashi, Kunio

1983-11-01

In the previous paper, it was reported that isothermal heat treatment of a commercial Japanese 0.40 pct C-Ni-Cr-Mo ultrahigh strength steel (AISI 4340 type) at 593 K for a short time followed by water quenching, in which a mixed structure of 25 vol pct lower bainite and 75 vol pct martensite is produced, results in the improvement of low temperature mechanical properties (287 to 123 K). The purpose of this paper is to study whether above new heat treatment will still be effective in commercial practice for improving low temperature mechanical properties of the ultrahigh strength steel when applied to a commercial Japanese 0.40 pct C-Cr-Mo ultrahigh strength steel which is economical because it lacks the expensive nickel component (AISI 4140 type). At and above 203 K this new heat treatment, as compared with the conventional 1133 K direct water quenching treatment, significantly improved the strength, tensile ductility, and notch toughness of the 0.40 pct C-Cr-Mo ultrahigh strength steel. At and above 203 K the new heat treatment also produced superior fracture ductility and notch toughness results at similar strength levels as compared to those obtained by using γ α' repetitive heat treatment for the same steel. However, the new heat treatment remarkably decreased fracture ductility and notch toughness of the 0.40 pct C-Cr-Mo ultrahigh strength steel below 203 K, and thus no significant improvement in the mechanical properties was noticeable as compared with the properties produced by the conventional 1133 K direct water quenching treatment and the γ α' repetitive heat treatment. This contrasts with the fact that the new heat treatment, as compared with the conventional 1133 K direct water quenching treatment and the γ α' repetitive heat treatment, dramatically improved the notch toughness of the 0.40 pct C-Ni-Cr-Mo ultrahigh strength steel, providing a better combination of strength and ductility throughout the 287 to 123 K temperature range. The difference

Hybrid fuzzy logic control of laser surface heat treatments

International Nuclear Information System (INIS)

Perez, Jose Antonio; Ocana, Jose Luis; Molpeceres, Carlos

2007-01-01

This paper presents an advanced hybrid fuzzy logic control system for laser surface heat treatments, which allows to increase significantly the uniformity and final quality of the obtained product, reducing the rejection rate and increasing the productivity and efficiency of the treatment. Basically, the proposed hybrid control structure combines a fuzzy logic controller, with a pure integral action, both fully decoupled, improving the performances of the process with a reasonable design cost, since the system nonlinearities are fully compensated by the fuzzy component of the controller, while the integral action contributes to eliminate the steady-state error

Deep heat muscle treatment: A mathematical model - I

International Nuclear Information System (INIS)

Ogulu, A.; Bestman, A.R.

1992-03-01

The flow of blood during deep heat muscle treatment is studied in this paper. We model the blood vessel as a long tube in circular section whose radius varied slowly. Under the Boussinesq approximation, we seek asymptotic series expansions for the velocity components, temperature and pressure about a small parameter, ε, characterizing the radius variation. The study reveals mathematically why physicians recommend a hot bath for cuts and physiotherapists use ice packs for bruises. (author). 5 refs, 3 figs

The Effect of Heat Treatment on the Pull-off Strength of Optionally Varnished Surfaces of Five Wood Materials

Directory of Open Access Journals (Sweden)

Musa Atar

2015-09-01

Full Text Available This study investigated the effects of heat treatment, following optional treatment with synthetic, water-based, and alkyd varnishes, on the pull-off strength of wooden materials sampled from oriental beech (Fagus orientalis L., oak (Quercus petraea Liebl., black poplar (Populus nigra L., pine (Pinus sylvestris L., and fir (Abies bornmulleriana M.. The test samples were subjected to heat treatment at temperatures of 165 °C and 175 °C for periods of 2 and 4 h with a total of 4 variations. With respect to the wood type, the samples of beech wood yielded the highest results for pull-off strength, while fir wood yielded the lowest. With respect to the varnish types, the highest pull-off strength was found in the samples of synthetic varnished beech (5,452 with a 37.2% improvement at 175 °C heat treatment for 4 h, while the lowest results were obtained in the samples of fir (0.991 with a 48.5% decrease at 175 °C heat treatment for 4 h. In conclusion, heat treatment significantly decreased the pull-off strength of the woods.

Influence of Solution Heat Treatment on Structure and Mechanical Properties of ZnAl22Cu3 Alloy

Directory of Open Access Journals (Sweden)

Michalik R.

2016-09-01

Full Text Available The influence of solution heat treatment at 385°C over 10 h with cooling in water on the structure, hardness and strength of the ZnAl22Cu3 eutectoid alloy is presented in the paper. The eutectoid ZnAl22Cu3 alloy is characterized by a dendritic structure. Dendrites are composed of a supersaturated solid solution of Al in Zn. In the interdendritic spaces a eutectoid mixture is present, with an absence of the ε (CuZn4 phase. Solution heat treatment of the ZnAl22Cu3 alloy causes the occurrence of precipitates rich in Zn and Cu, possibly ε phase. Solution heat treatment at 385°C initially causes a significant decrease of the alloy hardness, although longer solution heat treatment causes a significant increase of the hardness as compared to the as-cast alloy.

Effects of post heat-treatment on surface characteristics and adhesive bonding performance of medium density fiberboard

Science.gov (United States)

Nadir Ayrilimis; Jerrold E. Winandy

2009-01-01

A series of commercially manufactured medium density fiberboard (MDF) panels were exposed to a post-manufacture heat-treatment at various temperatures and durations using a hot press and just enough pressure to ensure firm contact between the panel and the press platens. Post-manufacture heat-treatment improved surface roughness of the exterior MDF panels. Panels...

On the conjoint influence of heat treatment and lithium content on microstructure and mechanical properties of A380 aluminum alloy

International Nuclear Information System (INIS)

Karamouz, Mostafa; Azarbarmas, Mortaza; Emamy, Masoud

2014-01-01

Highlights: • T4 heat treatment and the addition of Li modify the microstructure of alloy. • Heat treatment improves the tensile properties of non-modified and modified alloys. • Fracture surfaces of modified specimens had more ductile dimples than base alloys. - Abstract: In this study, the effects of a T4 heat treatment on the microstructure and tensile properties of an A380 aluminum alloy with and without lithium (Li) additions have been investigated. Microstructural examination was carried out using optical and scanning electron microscopy, image analysis, and X-ray diffraction (XRD) analysis methods. The results showed that when the T4 heat treatment was applied, spheroidized eutectic Si particles and fragmented β-phase particles were formed. The influence of the heat treatment on the aspect ratio and average length of Si and β phases in a non-modified alloy was more noticeable than in the Li-modified. Significant improvements in tensile properties were also observed in heat-treated samples. Additionally, a fractographical analysis showed that the fracture surfaces of the Li-modified specimens with and without heat treatment had more ductile dimple and fewer brittle cleavage surfaces

Heat treatment effect on the properties of the EhP767 maraging steel welded joints

International Nuclear Information System (INIS)

Taver, E.I.; Piskarev, M.N.; Yushchenko, K.A.; Pustovit, A.I.; Anisimova, M.S.

1977-01-01

Heat treatment effect on properties of welded joints of maraging 03Kh13N4K13M3T (EhP767) steel with yield strength over 150 kgs/mm 2 has been investigated. It is shown, that change in impact strength of aged joints at - 196 deg C depends on the amount of residual austenite and grain size. To stabilize 20-40 % residual austenite heat treatment regimes have been developed. Recommended are quenching at 1030-1050 deg C, sub-zero treatment and aging at 520 deg C for 16 hrs

Variation of Mechanical Properties of High RRR And Reactor Grade Niobium With Heat Treatments

Energy Technology Data Exchange (ETDEWEB)

Ganapati Myneni; H. Umezawa

2003-06-01

Superconducting rf cavities used as accelerating structures in particle accelerators are made from high purity niobium with residual resistance ratios greater than 250. Reactor grade niobium is also used to make wave-guide and/or end group components for these accelerating structures. The major impurities in this type of niobium are interstitially dissolved gases such as hydrogen, nitrogen, and oxygen in addition to carbon. After fabricating the niobium accelerating structures, they are subjected to heat treatments for several hours in vacuum at temperatures of up to 900 C for degassing hydrogen or up to 1400 C for improving the thermal conductivity of niobium considerably. These heat treatments are affecting the mechanical properties of niobium drastically. In this paper the variation of the mechanical properties of high purity and reactor grade niobium with heat treatments in a vacuum of {approx} 10{sup -6} Torr and temperatures from 600 C to 1250 C for periods of 10 to 6 hours are presented.

Effects of heat treatment conditions on microstructure and mechanical properties of AISI 420 steel

Energy Technology Data Exchange (ETDEWEB)

Scheuer, C.J.; Fraga, R.A.; Cardoso, R.P.; Brunatto, S.F. [Universidade Federal do Parana (UFPR), Curitiba, PR (Brazil). Departamento de Engenharia Mecanica. Grupo de Tecnologia de Fabricacao Assistida por Plasma e Metalurgia do Po

2014-07-01

The cycle control of heat treatments, on the quenching and tempering operation of AISI 420 stainless steel, is essential for improved material performance. The adequate choice of heat treatment parameters, can lead an optimization on its mechanical properties and corrosion resistance. Thus, this paper aims to investigate the effects of quenchants medium, and austenitizing and tempering temperatures, on the microstructure and mechanical properties of AISI 420 steel. Different heat treatments cycles were studied: 1) samples were austenitized at 1050°C and water, oil and air quenched; 2) samples were austenitized at range temperatures of 950-1050°C and oil quenched; and 3) as-quenched samples were tempering at range temperatures of 400-500°C. Treated samples were characterized by optical microscopy, X-ray diffractometry and hardness measurements. The samples hardness increases with increasing cooling rate (water > oil > air quenched). Water quenched samples presented crack after cooling to room temperature. Samples hardness also increases with austenitizing temperature increasing, and decreases with increasing tempering temperature. (author)

ANALYSIS OF PITTING CORROSION ON AN INCONEL 718 ALLOY SUBMITTED TO AGING HEAT TREATMENT

Directory of Open Access Journals (Sweden)

Felipe Rocha Caliari

2014-10-01

Full Text Available Inconel 718 is one of the most important superalloys, and it is mainly used in the aerospace field on account of its high mechanical strength, good resistance to fatigue and creep, good corrosion resistance and ability to operate continuously at elevated temperatures. In this work the resistance to pitting corrosion of a superalloy, Inconel 718, is analyzed before and after double aging heat treatment. The used heat treatment increases the creep resistance of the alloy, which usually is used up to 0.6 Tm. Samples were subjected to pitting corrosion tests in chloride-containing aqueous solution, according to ASTM-F746-04 and the procedure described by Yashiro et al. The results of these trials show that after heat treatment the superalloy presents higher corrosion resistance, i.e., the pitting corrosion currents of the as received surfaces are about 6 (six times bigger (~0.15 mA than those of double aged surfaces (~0.025 mA.

Enhancing the mechanical properties of electrospun polyester mats by heat treatment

Directory of Open Access Journals (Sweden)

M. Kancheva

2015-01-01

Full Text Available Microfibrous materials with a targeted design based on poly(L-lactic acid (PLA and poly(ε-caprolactone (PCL were prepared by electrospinning and by combining electrospinning and electrospraying. Several approaches were used: (i electrospinning of a common solution of the two polymers, (ii simultaneous electrospinning of two separate solutions of PLA and PCL, (iii electrospinning of PLA solution in conjunction with electrospraying of PCL solution, and (iv alternating layer-by-layer deposition by electrospinning of separate PLA and PCL solutions. The mats were heated at the melting temperature of PCL (60°", thus achieving melting of PCL fibers/particles and thermal sealing of the fibers. The mats subjected to thermal treatment were characterized by greater mean fiber diameters and reduced values of the water contact angle compared to the pristine mats. Heat treatment of the mats affected their thermal stability and led to an increase in the crystallinity degree of PLA incorporated in the mats, whereas that of PCL was reduced. All mats were characterized by enhanced mechanical properties after thermal treatment as compared to the non-treated fibrous materials.

Biochemical changes in full fat rice bran stabilized through microwave heating and irradiation treatment

International Nuclear Information System (INIS)

El-Niely, H.F.; Abaullah, M.I.

2007-01-01

The effect of microwave heating and irradiation treatments on proximate composition, lipoxygenase (LOX) activity, free fatty acid (FFA) and fatty acids profile of full fat rice bran were examined. Full fat raw rice bran (FRB) (82.7 g / kg moisture content) was heated in microwave oven at 850 W for up to 4 min or exposed to gamma irradiation up to 25 KGy then packed in polyethylene bags and stored at room temperature for 6 months. Water, protein, fat, ash and crude fiber contents did not change significantly in raw, microwave heated and irradiated samples before and after storage. An exception for this general observation was observed for the moisture content of FRB processed through microwave heating where heating FRB for 4 min dropped the level of moisture to 64.3 g / kg at zero time. Storage of both raw and processed samples had significant (P<0.05) effects on LOX activity. LOX activity of raw samples was significantly increased from its initial value by 43.5% after storage for six months. Microwave heat and irradiated samples showed deactivated LOX and samples exhibited significant changes in LOX activity could be due to treatment dosage. Meanwhile, significant change in LOX activity was observed in processed samples stored for six months. Minor changes were observed due to applied processing methods on FFA and fatty acids composition of full fat rice bran before and after storage. The results suggested that microwave heated or irradiated full fat rice bran packed in polyethylene bags can be stored at room temperature for six months without adverse effect on proximate, fatty acid composition quality and could prevent oxidative and hydrolytic rancidity. However, gamma irradiation treatment at 25 KGy was more effective in this respect. Therefore, it could be concluded that gamma irradiation contributed to optimal processing conditions for FRB stabilization

Sour gas injection for use with in situ heat treatment

Science.gov (United States)

Fowler, Thomas David [Houston, TX

2009-11-03

Systems, methods, and heaters for treating a subsurface formation are described herein. At least one method for providing acidic gas to a subsurface formation is described herein. The method may include providing heat from one or more heaters to a portion of a subsurface formation; producing fluids that include one or more acidic gases from the formation using a heat treatment process. At least a portion of one of the acidic gases may be introduced into the formation, or into another formation, through one or more wellbores at a pressure below a lithostatic pressure of the formation in which the acidic gas is introduced.

New method of processing heat treatment experiments with numerical simulation support

Science.gov (United States)

Kik, T.; Moravec, J.; Novakova, I.

2017-08-01

In this work, benefits of combining modern software for numerical simulations of welding processes with laboratory research was described. Proposed new method of processing heat treatment experiments leading to obtaining relevant input data for numerical simulations of heat treatment of large parts was presented. It is now possible, by using experiments on small tested samples, to simulate cooling conditions comparable with cooling of bigger parts. Results from this method of testing makes current boundary conditions during real cooling process more accurate, but also can be used for improvement of software databases and optimization of a computational models. The point is to precise the computation of temperature fields for large scale hardening parts based on new method of temperature dependence determination of the heat transfer coefficient into hardening media for the particular material, defined maximal thickness of processed part and cooling conditions. In the paper we will also present an example of the comparison standard and modified (according to newly suggested methodology) heat transfer coefficient data’s and theirs influence on the simulation results. It shows how even the small changes influence mainly on distribution of temperature, metallurgical phases, hardness and stresses distribution. By this experiment it is also possible to obtain not only input data and data enabling optimization of computational model but at the same time also verification data. The greatest advantage of described method is independence of used cooling media type.

Effect of Heat Treatment on Microstructure and Impact Toughness of Ti-6Al-4V Manufactured by Selective Laser Melting Process

Directory of Open Access Journals (Sweden)

Lee K.-A.

2017-06-01

Full Text Available This study manufactured Ti-6Al-4V alloy using one of the powder bed fusion 3D-printing processes, selective laser melting, and investigated the effect of heat treatment (650°C/3hrs on microstructure and impact toughness of the material. Initial microstructural observation identified prior-β grain along the building direction before and after heat treatment. In addition, the material formed a fully martensite structure before heat treatment, and after heat treatment, α and β phase were formed simultaneously. Charpy impact tests were conducted. The average impact energy measured as 6.0 J before heat treatment, and after heat treatment, the average impact energy increased by approximately 20% to 7.3 J. Fracture surface observation after the impact test showed that both alloys had brittle characteristics on macro levels, but showed ductile fracture characteristics and dimples at micro levels.

The Through Process Simulation of Mold filling, Solidification, and Heat Treatment of the Al Alloy Bending Beam Low-pressure Casting

International Nuclear Information System (INIS)

Yin, Yajun; Guo, Zhao; Wang, Huan; Liao, Dunming; Chen, Tao; Zhou, Jianxin

2015-01-01

The research on the simulation for the through process of low-pressure casting and heat treatment is conducive to combine information technology and advanced casting technology, which will help to predict the defects and mechanical properties of the castings in the through process. In this paper, we focus on the simulation for through process of low-pressure casting and heat treatment of ZL114A Bending beam. Firstly, we analyzethe distribution of the shrinkage and porosities in filling and solidification process, and simulate the distribution of stress and strain in the late solidification of casting. Then, the numerical simulation of heat treatment process for ZL114A Bending beam is realized according to the heat treatment parameters and the corresponding simulation results of temperature field, stress, strain, and aging performance are given. Finally, we verify that simulation platform for the through process of low-pressure casting and heat treatment can serve the production practice perfectly and provide technical guidance and process optimization for the through process of low-pressure casting and heat treatment. (paper)

The heat treatment of steel. A mathematical control problem

Energy Technology Data Exchange (ETDEWEB)

Hoemberg, Dietmar; Kern, Daniela

2009-07-21

The goal of this paper is to show how the heat treatment of steel can be modelled in terms of a mathematical optimal control problem. The approach is applied to laser surface hardening and the cooling of a steel slab including mechanical effects. Finally, it is shown how the results can be utilized in industrial practice by a coupling with machine-based control. (orig.)

THE EFFECT OF HEAT TREATMENT ON THE CHEMICAL AND COLOR CHANGE OF BLACK LOCUST (ROBINIA PSEUDOACACIA WOOD FLOUR

Directory of Open Access Journals (Sweden)

Yao Chen,

2012-01-01

Full Text Available The aim of this study was to investigate the effects of oxygen and moisture content (MC on the chemical and color changes of black locust (Robinia pseudoacacia wood during heat treatment. The wood flour was conditioned to different initial MCs and heated for 24 h at a constant temperature of 120ºC in either oxygen or nitrogen atmosphere. The pH values and chromaticity indexes were examined. Diffuse reflectance UV-Vis (DRUV and Fourier transform infrared (FTIR spectra were used to characterize the changes of chromophores upon heating. The study demonstrated that the pH values decreased after heat treatment, and it was lower when the heat treated was in oxygen than in nitrogen. The L* decreased significantly, while a* and b* increased. The total color difference ΔE* increased with increasing initial MC until a plateau was reached after 30% MC. The color change was greater in oxygen than in nitrogen. The hydroxyl groups decreased after heat treatment. The releases of acid and formation of quinoid compounds and carboxylic groups during heat treatment were confirmed. Discoloration of wood is due mainly to the condensation and oxidation reactions, which are accelerated by oxygen. Higher MCs are required to obtain the greatest color change of wood in inert atmosphere.

Effect of Post-Weld Heat Treatment on Creep Rupture Properties of Grade 91 Steel Heavy Section Welds

Energy Technology Data Exchange (ETDEWEB)

Li, Leijun

2012-11-02

This project will conduct a systematic metallurgical study on the effect of post-weld heat treatment (PWHT) on the creep rupture properties of P91 heavy section welds. The objective is to develop a technical guide for selecting PWHT parameters, and to predict expected creep-rupture life based on the selection of heat treatment parameters. The project consists of four interdependent tasks: Experimentally and numerically characterize the temperature fields of typical post-weld heat treatment procedures for various weld and joint configurations to be used in Gen IV systems. Characterize the microstructure of various regions, including the weld fusion zone, coarse-grain heat-affected zone, and fine-grain heat affected zone, in the welds that underwent the various welding and PWHT thermal histories. Conduct creep and creep-rupture testing of coupons extracted from actual and physically simulated welds. Establish the relationship among PWHT parameters, thermal histories, microstructure, creep, and creep-rupture properties.

Influence of sub-solvus solution heat treatment on γ′ morphological instability in a new Ni–Cr–Co-based powder metallurgy superalloy

International Nuclear Information System (INIS)

Yang, W.P.; Liu, G.Q.; Wu, K.; Hu, B.F.

2014-01-01

Highlights: • A special γ′ morphological instability in a new Ni–Cr–Co-based P/M superalloy was studied. • Three heat treatments were applied to the alloy and microstructures were observed. • Microstructure of the alloy was homogenized by sub-solvus solution heat treatment. • Sub-solvus solution heat treatment influences morphology of γ′ fan-type structures. • Sub-solvus solution heat treatment makes γ′ fan-type structures regular and stable. -- Abstract: The influence of the sub-solvus solution heat treatment on the microstructure, especially the γ′ morphology (γ′ fan-type structure), and microhardness of a new Ni–Cr–Co-based powder metallurgy superalloy was studied by means of field emission scanning electron microscopy (FESEM) and microhardness testing. The results show that sub-solvus solution heat treatment changes the microstructure of an as-forged alloy. It makes large primary γ′ phases at grain boundaries smaller and the distribution of secondary γ′ phases in the interior of the grains more homogeneous. Moreover, the grain boundaries widen because of the supplementary precipitate. The sub-solvus solution heat treatment before the super-solvus solution heat treatment does not change nucleation sites of the γ′ fan-type structures which precipitate during the super-solvus solution heat treatment. However, it influences the morphology of γ′ fan-type structures. Length distribution of the secondary γ′ dendrites in fan-type structures changes from a bimodal to a unimodal distribution, which means the lengths of the secondary γ′ dendrites become more uniform. Applying a sub-solvus solution heat treatment after the super-solvus solution heat treatment causes the secondary γ′ dendrites to be broken off in the fan-type structures and a refinement of the γ′ phases, and this improves stability of the γ′ phases

Effect of heat-treatment with raw cotton seed oil on decay resistance and dimensional stability of Beech (Fagus orientalis

Directory of Open Access Journals (Sweden)

مریم قربانی

2015-05-01

Full Text Available This research was conducted to determine the effect of heat-treatment with raw cotton seed oil on decay resistance and dimensional stability of beech according to EN113 and ASTM-D1037 standards respectively. The heat treatment with raw cotton seed oil was carried out in the cylinder at the temperatures of 130 and 170oC for 30 and 60 minutes. Oil uptake, density, volumetric swelling, water absorption and weight loss exposed to decay were measured. Oil uptake at 30 and 60 min were determined 10.5 and 13.3 Kg/cm3 respectively. Oil-heat treated samples at 30min and 130°C indicated the maximum density with 87.7% increase. According to results, oil-heat treatment improved water repellency and dimensional stability. Water absorption in 130°C and 60 minutes decreased 76% in comparison with control. Decay resistance of oil soaked samples for 60minutes was 80.2% more than control samples. Oil-heat treatment compared with oil treatment improved decay resistance, this effect was significant at 30 min. The temperature rise of oil–heat treatment at 30 minutes improved decay resistance, but the improvement under same level of temperature with increase time was not significant.

Evaluation of the Sensitization of 316L Stainless Steels After the Post Weld Heat Treatment

Energy Technology Data Exchange (ETDEWEB)

Lee, Junho; Jang, Changheui [Korea Advanced Institute of Science and Technology, Daejeon (Korea, Republic of); Lee, Kyoung Soo [Korea Hydro and Nuclear Power Co. Ltd., Daejeon (Korea, Republic of)

2014-05-15

It was observed that the PWSCC growth rate of alloy 182 was markedly decreased after PWHT. However, the PWHT of components made of stainless steels (SSs) would be limited because of the concerns about sensitization when they are exposed to temperature range of 500 to 800 .deg. C. Also, the sensitization of austenitic stainless steels could increase the susceptibility to intergrannular stress corrosion cracking. Therefore, the effect of PWHT on the sensitization behaviors of 316L SSs having predominant austenitic structure with small amount of ferrite was investigated to assess the applicability of PWHT to dissimilar weld area with austenitic stainless steels. The sensitization behaviors of two heats of 316L SSs with small amount of ferrite were investigated after heat treatment at 600, 650 and 700 .deg. C. Grain boundary sensitization was not observed in 316L SSs after the heat treatment at 600, 650 and 700 .deg. C up to 30 h. The increase in degree of sensitization (DOS) was caused by reduction of corrosion resistance in ferrite phase due to formation of chromium carbide and intermatallic phases during heat treatment. The DOS value of 316L SSs depended on the ferrite morphology. The stringer type of ferrite (316L-heat A) showed relatively higher DOS in comparison with 316L containing blocky type of ferrite (316L-heat B). It could be due to sufficient supplement of chromium in larger size of ferrite phase.

Evaluation of the Sensitization of 316L Stainless Steels After the Post Weld Heat Treatment

International Nuclear Information System (INIS)

Lee, Junho; Jang, Changheui; Lee, Kyoung Soo

2014-01-01

It was observed that the PWSCC growth rate of alloy 182 was markedly decreased after PWHT. However, the PWHT of components made of stainless steels (SSs) would be limited because of the concerns about sensitization when they are exposed to temperature range of 500 to 800 .deg. C. Also, the sensitization of austenitic stainless steels could increase the susceptibility to intergrannular stress corrosion cracking. Therefore, the effect of PWHT on the sensitization behaviors of 316L SSs having predominant austenitic structure with small amount of ferrite was investigated to assess the applicability of PWHT to dissimilar weld area with austenitic stainless steels. The sensitization behaviors of two heats of 316L SSs with small amount of ferrite were investigated after heat treatment at 600, 650 and 700 .deg. C. Grain boundary sensitization was not observed in 316L SSs after the heat treatment at 600, 650 and 700 .deg. C up to 30 h. The increase in degree of sensitization (DOS) was caused by reduction of corrosion resistance in ferrite phase due to formation of chromium carbide and intermatallic phases during heat treatment. The DOS value of 316L SSs depended on the ferrite morphology. The stringer type of ferrite (316L-heat A) showed relatively higher DOS in comparison with 316L containing blocky type of ferrite (316L-heat B). It could be due to sufficient supplement of chromium in larger size of ferrite phase

Effect of heat treatment on microstructure, mechanical properties and erosion resistance of cast 23-8-N nitronic steel

International Nuclear Information System (INIS)

Kumar, Avnish; Sharma, Ashok; Goel, S.K.

2015-01-01

Effects of heat treatment on microstructure, mechanical properties and erosion behavior of cast 23-8-N nitronic steel were studied. A series of heat treatments were carried out in the temperature range of 1180–1240 °C to observe the effect on microstructure. Optimum heat treatment cycle was obtained at 1220 °C for holding time of 150 min, which leads to dissolution of carbides, formation of equiaxed grains and twins. Heat treatment has shown improvement in tensile strength, toughness, impact strength and work hardening capacity, however at the cost of marginal reduction in hardness and yield strength. This resulted in improvement of erosion resistance of cast 23-8-N nitronic steel. The microstructures, fractured surfaces and phases were studied by optical microscopy, field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD) analysis respectively

On post-weld heat treatment cracking in tig welded superalloy ATI 718Plus

Science.gov (United States)

Asala, G.; Ojo, O. A.

The susceptibility of heat affected zone (HAZ) to cracking in Tungsten Inert Gas (TIG) welded Allvac 718Plus superalloy during post-weld heat treatment (PWHT) was studied. Contrary to the previously reported case of low heat input electron beam welded Allvac 718Plus, where HAZ cracking occurred during PWHT, the TIG welded alloy is crack-free after PWHT, notwithstanding the presence of similar micro-constituents that caused cracking in the low input weld. Accordingly, the formation of brittle HAZ intergranular micro-constituents may not be a sufficient factor to determine cracking propensity, the extent of heat input during welding may be another major factor that influences HAZ cracking during PWHT of the aerospace superalloy Allvac 718Plus.

Universal high-temperature heat treatment furnace for FBR mixed uranium and plutonium carbide fuel

International Nuclear Information System (INIS)

Handa, Muneo; Takahashi, Ichiro; Watanabe, Hitoshi

1978-10-01

A universal high-temperature heat treatment furnace for LMFBR advanced fuels was installed in Plutonium Fuel Laboratory, Oarai Research Establishment. Design, construction and performance of the apparatus are described. With the apparatus, heat treatment of the fuel under a controlled gas atmosphere and quenching of the fuel with blowing helium gas are possible. Equipment to measure impurity gas release of the fuel is also provided. Various plutonium enclosure techniques, e.g., a gas line filter with new exchange mechanics, have been developed. In performance test, results of the enclosure techniques are described. (author)

Effect of tin oxide nano particles and heat treatment on decay resistance and physical properties of beech wood (Fagus orientalis

Directory of Open Access Journals (Sweden)

Maryam Ghorbani

2014-11-01

Full Text Available This research was conducted to investigate the effect of Tin oxide nanoparticles and heat treatment on decay resistance and physical properties of beech wood. Biological and physical test samples were prepared according to EN-113 and ASTM-D4446-05 standards respectively. Samples were classified into 4 groups: control, impregnation with Tin oxide nanoparticles, heat treatment and nano-heat treatment. Impregnation with Tin oxide nano at 5000ppm concentration was carried out in the cylinder according to Bethell method. Then, samples were heated at 140, 160 and 185˚C for 2 and 4 hours. According to results, decay resistance improved with increasing time and temperature of heat treatment. Least weight loss showed 46.39% reduction in nano-heat samples treated at 180˚C for 4 hours in comparison with control at highest weight loss. Nano-heat treated samples demonstrated the maximum amount of water absorption without significant difference with control and nanoparticles treated samples. Increase in heat treatment temperature reduced water absorption so that it is revealed 47.8% reduction in heat treated samples at 180°C for 4h after 24h immersion in water. In nano-heat treated samples at 180˚C for 2h was measured least volume swelling. Volume swelling in nano-treated samples decreased 8.7 and 22.76% after 2 and 24 h immersion in comparison with the control samples respectively.

Ploidy Manipulation of Zebrafish Embryos with Heat Shock 2 Treatment

Science.gov (United States)

Baars, Destiny L.; Pelegri, Francisco

2016-01-01

Manipulation of ploidy allows for useful transformations, such as diploids to tetraploids, or haploids to diploids. In the zebrafish Danio rerio, specifically the generation of homozygous gynogenetic diploids is useful in genetic analysis because it allows the direct production of homozygotes from a single heterozygous mother. This article describes a modified protocol for ploidy duplication based on a heat pulse during the first cell cycle, Heat Shock 2 (HS2). Through inhibition of centriole duplication, this method results in a precise cell division stall during the second cell cycle. The precise one-cycle division stall, coupled to unaffected DNA duplication, results in whole genome duplication. Protocols associated with this method include egg and sperm collection, UV treatment of sperm, in vitro fertilization and heat pulse to cause a one-cell cycle division delay and ploidy duplication. A modified version of this protocol could be applied to induce ploidy changes in other animal species. PMID:28060351

Effects of heat treatment on density, dimensional stability and color ...

African Journals Online (AJOL)

The purpose of this study was to evaluate the effect of heat treatment on some physical properties and color change of Pinus nigra wood which has high industrial use potential and large growing stocks in Turkey. Wood samples which comprised the material of the study were obtained from an industrial plant. Samples were ...

Effect of Heat Treatment on the Properties of CoCrMo Alloy Manufactured by Selective Laser Melting

Science.gov (United States)

Guoqing, Zhang; Junxin, Li; Xiaoyu, Zhou; Jin, Li; Anmin, Wang

2018-05-01

To obtain medical implants with better mechanical properties, it is necessary to conduct studies on the heat treatment process of the selective laser melting (SLM) manufacturing parts. The differential scanning calorimetry method was used to study the heat treatment process of the phase transition of SLM CoCrMo alloy parts. The tensile properties were tested with a tensile test machine, the quantity of carbide precipitated after heat treatment was measured by energy-dispersive x-ray spectroscopy, and the tensile fracture morphology of the parts was investigated using SEM. The obtained results were: Mechanical properties in terms of elongation and tensile strength of CoCrMo alloy manufactured by SLM that had been heat-treated at 1200 °C for 2 h followed by cooling with water were not only higher than the national standard but also higher than the experimental results of the same batch of castings. The mechanism of fracture of parts manufactured by SLM without heat treatment was brittle fracture, whereas parts which had been heat-treated at 1200 °C for 2 h combined with water cooling and at 1200 °C for 1 h with furnace cooling suffered ductile fracture. This study provides the basis for defining the applications for which CoCrMo alloys manufactured by SLM are suitable within the field of medical implants.

Expanded heat treatment to form residual compressive hoop stress on inner surface of zirconium alloy tubing

International Nuclear Information System (INIS)

Megata, Masao

1997-01-01

A specific heat treatment process that introduces hoop stress has been developed. This technique can produce zirconium alloy tubing with a residual compressive hoop stress near the inner surface by taking advantage of the mechanical anisotropy in hexagonal close-packed zirconium crystal. Since a crystal having its basal pole parallel to the tangential direction of the tubing is easier to exhibit plastic elongation under the hoop stress than that having its basal pole parallel to the radial direction, the plastic and elastic elongation can coexist under a certain set of temperature and hoop stress conditions. The mechanical anisotropy plays a role to extend the coexistent stress range. Thus, residual compressive hoop stress is formed at the inner surface where more plastic elongation occurs during the heat treatment. This process is referred to as expanded heat treatment. Since this is a fundamental crystallographic principle, it has various applications. The application to improve PCI/SCC (pellet cladding interaction/stress corrosion cracking) properties of water reactor fuel cladding is promising. Excellent results were obtained with laboratory-scale heat treatment and an out-reactor iodine SCC test. These results included an extension of the time to SCC failure. (author)

COMPUTERIZED HEAT-TREATMENT IN A ZIMBABWEAN FACTORY

Directory of Open Access Journals (Sweden)

M. Collier

2012-01-01

Full Text Available In the context of Zimbabwe's current economic problems, parts of the manufacturing industry are turning their attention to the possibility of utilising local design talent in upgrading their manufacturing plants. This paper describes a project undertaken by the National University of Science and Technology to convert the heat-treatment process in a major manufacturing plant from semi -manual to a computerized one. The system comprises microcontroller connection to the furnaces and sensors, and communicates with a central computer on which software for a windowed user-interface is hosted. Experimental results for the system are presented, and a strategy for other companies in the same predicament is proposed.

The influence of heat treatments on several types of base-metal removable partial denture alloys.

Science.gov (United States)

Morris, H F; Asgar, K; Rowe, A P; Nasjleti, C E

1979-04-01

Four removable partial denture alloys, Vitallium (Co-Cr alloy), Dentillium P.D. (Fe-Cr alloy), Durallium L.G. (Co-Cr-Ni alloy), and Ticonium 100 (Ni-Cr alloy), were evaluated in the as-cast condition and after heat treatment for 15 minutes at 1,300 degrees, 1,600 degrees, 1,900 degrees, and 2,200 degrees F followed by quenching in water. The following properties were determined and compared for each alloy at each heat treatment condition: the yield strengths at 0.01%, 0.1%, and 0.2% offsets, the ultimate tensile strength, the percent elongation, the modulus of elasticity, and the Knoop microhardness. The results were statistically analyzed. Photomicrographs were examined for each alloy and test condition. The following conclusions were made: 1. The "highest values" were exhibited by the as-cast alloy. 2. Heat treatment of the partial denture alloys tested resulted in reductions in strength, while the elongations varied. This study demonstrates that, in practice, one should avoid (a) prolonged "heat-soaking" while soldering and (b) grinding or polishing of the casting until the alloy is "red hot". 3. Durallium L.G. was the least affected by the various heat treatment conditions. 4. Conventional reporting of the yield strength at 0.2% offset, the ultimate tensile strength, and percent elongation are not adequate to completely describe and compare the mechanical behavior of alloys. The reporting of the yield strength at 0.01% offset, in addition to the other reported properties, will provide a more complete description of the behavior of the dental alloys.

Heat treatment of nickel alloys

International Nuclear Information System (INIS)

Smith, D.F. Jr.; Clatworthy, E.F.

1975-01-01

A heat treating process is described that can be used to produce desired combinations of strength, ductility, and fabricability characteristics in heat resistant age-hardenable alloys having precipitation-hardening amounts of niobium, titanium, and/or tantalum in a nickel-containing matrix. (U.S.)

Effect of Shortened Heat Treatment on the Hardness and Microstructure of 320.0 Aluminium Alloy

Directory of Open Access Journals (Sweden)

Pezda J.

2014-06-01

Full Text Available Improvement of Al-Si alloys properties in scope of classic method is connected with change of Si precipitations morphology through: using modification of the alloy, maintaining suitable temperature of overheating and pouring process, as well as perfection of heat treatment methods. Growing requirements of the market make it necessary to search after such procedures, which would quickly deliver positive results with simultaneous consideration of economic aspects. Presented in the paper shortened heat treatment with soaking of the alloy at temperature near temperature of solidus could be assumed as the method in the above mentioned understanding of the problem. Such treatment consists in soaking of the alloy to temperature of solutioning, keeping in such temperature, and next, quick quenching in water (20 °C followed by artificial ageing. Temperature ranges of solutioning and ageing treatments implemented in the adopted testing plan were based on analysis of recorded curves from the ATD method. Obtained results relate to dependencies and spatial diagrams describing effect of parameters of the solutioning and ageing treatments on HB hardness of the investigated alloy and change of its microstructure. Performed shortened heat treatment results in precipitation hardening of the investigated 320.0 alloy, what according to expectations produces increased hardness of the material.

The effect of the combined treatment of gamma irradiation and heating on the aerobic bacterial load of white and black peppers

International Nuclear Information System (INIS)

Mohd Khan Ayob; Ismail Bahari; Osman Hassan; Verumandy Kaleswaran

1985-01-01

The effect of combined heat-irradiation treatment on the aerobic bacterial load of black and white peppers were evaluated in comparison with that of heat or irradiation treatment only. The irradiation doses applied were 0 (control), 2, 4, 6 and 8 kGy and the heating temperatures were 28 (control), 50, 60, 70 and 80 deg C. Results indicated that gamma radiation of 7 kGy and 5 kGy were capable of reducing bacterial population from 3.6 x 10 6 /g and 2.9 x 10 5 /g to 3 /g black and white peppers, respectively. Heating at drying temperature could only reduce the bacterial contaminants to 1/2 log cycle. Combined treatment of irradiation followed by heating is more effective in reducing the bacterial load, and the combined treatment of heating followed by irradiation showed similar effects as in irradiation treatment alone. (author)

Influence of Heat Treatment on the Corrosion Behavior of Purified Magnesium and AZ31 Alloy

OpenAIRE

Khalifeh, Sohrab; Burleigh, T. David

2017-01-01

Magnesium and its alloys are ideal for biodegradable implants due to their biocompatibility and their low-stress shielding. However, they can corrode too rapidly in the biological environment. The objective of this research was to develop heat treatments to slow the corrosion of high purified magnesium and AZ31 alloy in simulated body fluid at 37{\\deg}C. Heat treatments were performed at different temperatures and times. Hydrogen evolution, weight loss, PDP, and EIS methods were used to measu...

The effects of combined treatment of irradiation and heat on bacteria escherichia coli and sarcina lutea in dry condition

International Nuclear Information System (INIS)

Nikham; Hilmy, Nazly

1987-01-01

The effects of combination treatment of irradiation and heat on bacteria escherichia coli and sarcina lutea in dry condition. Investigation on the effects of combined irradiation + heat and heat + irradiation treatments have been carried out i.e. at the doses of 0; 1.0; 1.5; and 2.0 kGy with heating at 50 0 C for 10; 20; and 30 minutes on escherichia coli B/r, escherichia coli from sludge and sarcine lutea. Samples of bacteria were prepared in dry condition by using sterile fine sand as carrier. Irradiation was done in aerobic condition with RH 90% and the time range between irradiation and heating was not more than 2 hours. The results showed that the D 10 value did not give significant difference between the combined irradiation + heat, and heat + irradiation treatments for the 3 species of bacteria, compared to irradiation only (p 0.05). Doses of 1.0 and 1.5 kGy combined with heating at 50 0 C for 10 and 20 minutes gave better results compared to irradiation only. 17 refs

Measurement of heat treatment induced residual stresses by using ESPI combined with hole-drilling method

Directory of Open Access Journals (Sweden)

Jie Cheng

2010-08-01

Full Text Available In this study, residual stresses in heat treated specimen were measured by using ESPI (Electronic Speckle-Pattern Interferometry combined with the hole-drilling method. The specimen, made of SUS 304 austenitic stainless steel, was quenched and water cooled to room temperature. Numerical simulation using a hybrid FDM/FEM package was also carried out to simulate the heat treatment process. As a result, the thermal stress fields were obtained from both the experiment and the numerical simulation. By comparision of stress fields, results from the experimental method and numerical simulation well agreed to each other, therefore, it is proved that the presented experimental method is applicable and reliable for heat treatment induced residual stress measurement.

Heat treatment and aging effect on the structural and optical properties of plasma polymerized 2,6-diethylaniline thin films

International Nuclear Information System (INIS)

Matin, Rummana; Bhuiyan, A.H.

2012-01-01

The monomer, 2,6-diethylaniline has been used to deposit plasma polymerized 2,6-diethylaniline (PPDEA) thin films at room temperature on to glass substrates by a capacitively coupled parallel plate glow discharge reactor. A comparative analysis on the changes of morphological, structural and optical properties of as-deposited, heat treated and aged PPDEA thin films is ascertained. Scanning electron microscopy shows uniform and pinhole free surface of PPDEA thin films and no significant difference in the surface morphology is observed due to heat treatment. Electron dispersive X-ray and Fourier transform infrared spectroscopic investigations indicate some structural rearrangement in PPDEA thin films due to heat treatment. Differential thermal analysis, thermogravimetric analysis and differential thermogravimetric analysis suggest that the PPDEA is thermally stable up to about 580 K. The study on the optical absorption spectra of as-deposited, heat treated and aged PPDEA thin films of different thicknesses lead to the determination of the allowed direct and indirect transition energies ranging from 3.63 to 2.73 and 2.38 to 1.26 eV respectively. Urbach energy, steepness parameter and extinction coefficient are also assessed. It is observed that the optical parameters of as-deposited PPDEA thin films change due to heat treatment and do not change appreciably due to aging. - Highlights: ► Heat treatment and aging effect of plasma polymerized 2,6-diethylaniline thin films. ► The surface morphology of PPDEA is found uniform for all types of sample. ► Heat treatment introduces some elemental and structural rearrangement. ► The thermal stability is found up to about 580 K. ► Optical parameters were changed for heat treatment but not markedly for aging.

Effect of heat treatment on strength and abrasive wear behaviour of ...

Indian Academy of Sciences (India)

Administrator

Aluminum 6061 has been used as matrix material owing to its ... Mechanical properties such as microhardness, tensile strength, and abrasive wear tests have been ... heat treatment conditions, adopted Al6061–SiCp composites exhibited better microhardness and tensile ... corrosion resistance (Ramesh et al 2005).

Structural steels for power generating equipment and heat and chemical heat treatments

International Nuclear Information System (INIS)

Astaf'ev, A.A.

1979-01-01

Development of structural steels for power generating equipment and for reactor engineering, in particular, is elucidated. Noted is utilization of the 15Kh2NMFA steels for the WWER-1000 reactor vessels, the 10GN2MFA steels for steam generators, pressurizers, vessels of the automatic emergency shut down and safety system; the 00Kh12N3DL steel for cast pump vessels and main locking bars. The recommendations on heat treatment of big forgings, for instance, ensuring the necessary complex of mechanical properties are given. Diffusion chromizing with subsequent nitriding of austenitic steels which increase durability of the components in BN reactors more than 4 times, is practised on a large scale

[Effect of heat treatment on the structure of a Cu-Zn-Al-Ni system dental alloy].

Science.gov (United States)

Guastaldi, A C; Adorno, A T; Beatrice, C R; Mondelli, J; Ishikiriama, A; Lacefield, W

1990-01-01

This article characterizes the structural phases present in the copper-based metallic alloy system "Cu-Zn-Al-Ni" developed for dental use, and relates those phases to other properties. The characterization was obtained after casting (using the lost wax process), and after heat treatment. In order to obtain better corrosion resistance by changing the microstructure, the castings were submitted to 30, 45 and 60 minutes of heat treatment at the following temperatures: 750 degrees C, 800 degrees C, and 850 degrees C. The various phases were analyzed using X-ray diffraction and scanning electron microscopy (SEM). The results after heat treatment showed a phase (probably Cu3Al), that could be responsible for the improvement in the alloy's resistance to corrosion as compared to the as-cast structure.

Combined heat and gamma-irradiation treatments for the control of strawberry diseases under market conditions

International Nuclear Information System (INIS)

Brodrick, H.T.; Thomas, A.C.; Van Tonder, A.J.; Terblanche, J.C.

1977-02-01

The spoilage of strawberries under local market conditions was investigated. It was confirmed that the major losses are due to 'leak' disease caused by Rhizopus stolonifer (Ehr. ex Fr.) Lind. It was also established that further fruit losses in summer are due to anthracnose caused by the fungus Colletotrichum acutatum Simmonds. This is the first time that the latter pathogen has been isolated and identified and recognised as a problem on strawberries in South Africa. Studies with R. stolonifer in culture showed that 46 degrees Celsius for 20 min (the previous international standard heat treatment for fruit) was disappointing, while a treatment at 50 degrees Celsius for 10 min effectively inhibited spore germination. Irradiation studies with cultures of R. stolonifer and C. acutatum showed that a dose of 200 and 100 krad, respectively, resulted in excellent inhibition of spore germination. However, irradiating in nitrogen gas resulted in a tenfold reduction in the effectiveness of the irradiation treatments. The use of nitrogen during irradiation, therefore, cannot be considered, especially where an effective control of the fungal pathogens is desired. Investigations with different cultivars clearly demonstrated the synergistic effect on disease control obtained when combining heat and irradiation treatments. The combination treatment (moist heat at 50-52 degrees Celsius for 10 min plus 200 krad), besides effectively controlling both diseases in strawberries, did not adversely affect berry quality. In simulated transport tests it was shown that a minimal amount of berry softening did occur with this treatment, but this adverse effect was negligible compared with the beneficial effect obtained from disease control. In semi-commercial experiments it was shown that the combination heat and irradiation treatment effectively controlled spoilage diseases for a period of several days from picking, thus allowing sufficient time to market the fruit under local market

Effect of Heat Treatment on the Structure and Properties of Die Steel 70Kh3G2FTR

Science.gov (United States)

Krylova, S. E.; Kletsova, O. A.; Gryzunov, V. I.; Fot, A. P.; Tavtilov, I. Sh.

2018-01-01

The effect of heat treatment parameters on the properties and structural and phase composition of a promising die steel 70Kh3G2FTR for hot deformation is studied. The temperature-and-stress state of a hammer die under a heat treatment is simulated.

Dry Heat Treatment Reduces the Occurrence of Cladosporium cucumerinum, Ascochyta citrullina, and Colletotrichum orbiculare on the Surface and Interior of Cucumber Seeds

Directory of Open Access Journals (Sweden)

Yanxia Shi

2016-01-01

Full Text Available Dry heat treatment has been identified as a method for disinfecting seed-borne pathogens in vegetable seeds. This study demonstrated that three seed-borne pathogens of cucumber (Cladosporium cucumerinum that causes scabs, Ascochyta citrullina that results in gummy stem blight, and Colletotrichum orbiculare that induces anthracnose could be effectively eradicated from cucumber seeds by dry heat treatment. In vitro growth of these three pathogens was inhibited by dry heat treatment at 70 °C for 40 min. These pathogens were inactivated after exposing infected seeds to 70 °C dry heat for at least 90 min. Seed infection was significantly reduced by exposing the seeds to 70 °C dry heat for at least 40 min. Seed moisture content and germination were slightly reduced after 70 °C heat treatment for 40–120 min. Seed vigor remained at a high level after dry heat treatment at 70 °C for 90 min. In conclusion, 70 °C dry heat treatment for 90 min was determined to be the optimal method for eradication of C. cucumerinum, Didymella bryoniae, and C. orbiculare from cucumber seeds.

Assessment of heat treatment of dairy products by MALDI-TOF-MS.

Science.gov (United States)

Meltretter, Jasmin; Birlouez-Aragon, Inès; Becker, Cord-Michael; Pischetsrieder, Monika

2009-12-01

The formation of the Amadori product from lactose (protein lactosylation) is a major parameter to evaluate the quality of processed milk. Here, MALDI-TOF-MS was used for the relative quantification of lactose-adducts in heated milk. Milk was heated at a temperature of 70, 80, and 100 degrees C between 0 and 300 min, diluted, and subjected directly to MALDI-TOF-MS. The lactosylation rate of alpha-lactalbumin increased with increasing reaction temperature and time. The results correlated well with established markers for heat treatment of milk (concentration of total soluble protein, soluble alpha-lactalbumin and beta-lactoglobulin at pH 4.6, and fluorescence of advanced Maillard products and soluble tryptophan index; r=0.969-0.997). The method was also applied to examine commercially available dairy products. In severely heated products, protein pre-purification by immobilized metal affinity chromatography improved spectra quality. Relative quantification of protein lactosylation by MALDI-TOF-MS proved to be a very fast and reliable method to monitor early Maillard reaction during milk processing.

Dimensional Changes of Nb$_{3}$Sn Rutherford Cables During Heat Treatment

CERN Document Server

Rochepault, E; Ambrosio, G; Anerella, M; Ballarino, A; Bonasia, A; Bordini, B; Cheng, D; Dietderich, D R; Felice, H; Garcia Fajardo, L; Ghosh, A; Holik, E F; Izquierdo Bermudez, S; Perez, J C; Pong, I; Schmalzle, J; Yu, M

2016-01-01

In high field magnet applications, Nb$_{3}$Sn coils undergo a heat treatment step after winding. During this stage, coils radially expand and longitudinally contract due to the Nb$_{3}$Sn phase change. In order to prevent residual strain from altering superconducting performances, the tooling must provide the adequate space for these dimensional changes. The aim of this paper is to understand the behavior of cable dimensions during heat treatment and to provide estimates of the space to be accommodated in the tooling for coil expansion and contraction. This paper summarizes measurements of dimensional changes on strands, single Rutherford cables, cable stacks, and coils performed between 2013 and 2015. These samples and coils have been performed within a collaboration between CERN and the U.S. LHC Accelerator Research Program to develop Nb$_{3}$Sn quadrupole magnets for the HiLumi LHC. The results are also compared with other high field magnet projects.

Effect of heat treatment on carbon fiber surface properties and fibers/epoxy interfacial adhesion

International Nuclear Information System (INIS)

Dai Zhishuang; Zhang Baoyan; Shi Fenghui; Li Min; Zhang Zuoguang; Gu Yizhuo

2011-01-01

Carbon fiber surface properties are likely to change during the molding process of carbon fiber reinforced matrix composite, and these changes could affect the infiltration and adhesion between carbon fiber and resin. T300B fiber was heat treated referring to the curing process of high-performance carbon fiber reinforced epoxy matrix composites. By means of X-ray photoelectron spectroscopy (XPS), activated carbon atoms can be detected, which are defined as the carbon atoms conjunction with oxygen and nitrogen. Surface chemistry analysis shows that the content of activated carbon atoms on treated carbon fiber surface, especially those connect with the hydroxyl decreases with the increasing heat treatment temperature. Inverse gas chromatography (IGC) analysis reveals that the dispersive surface energy γ S d increases and the polar surface energy γ S sp decreases as the heat treatment temperature increases to 200. Contact angle between carbon fiber and epoxy E51 resin, which is studied by dynamic contact angle test (DCAT) increases with the increasing heat treatment temperature, indicating the worse wettability comparing with the untreated fiber. Moreover, micro-droplet test shows that the interfacial shear strength (IFSS) of the treated carbon fiber/epoxy is lower than that of the untreated T300B fiber which is attributed to the decrement of the content of reactive functional groups including hydrogen group and epoxy group.

PECULIARITIES OF GENERALIZATION OF SIMILAR PHENOMENA IN THE PROCESS OF FISH HEAT TREATMENT

Directory of Open Access Journals (Sweden)

V. A. Pokhol’chenko

2015-01-01

Full Text Available The theoretical presuppositions for the possibility of generalizing and similarity founding in dehydration and wet materials heating processes are studieded in this article. It is offered to carry out the given processes generalization by using dimensionless numbers of similarity. At the detailed analyzing of regularities of heat treatment processes of fish in different modes a significant amount of experienced material was successfully generalized on the basis of dimensionless simplex (similarity numbers. Using the dimensionless simplex allowed to detect a number of simple mathematical models for the studied phenomena. The generalized kinetic models of fish dehydration, the generalized dynamic models (changing moisture diffusion coefficients, the generalized kinetic models of fish heating (the temperature field changing in the products thickness, average volume and center were founded. These generalized mathematical models showed also relationship of dehydration and heating at the processes of fish semi-hot, hot smoking (drying and frying. The relationship of the results from the physical nature of the dehydration process, including a change in the binding energy of the moisture with the material to the extent of the process and the shrinkage impact on the rate of the product moisture removal is given in the article. The factors influencing the internal structure and properties of the raw material changing and retarding the dehydration processes are described there. There was a heating rate dependence of fish products on the chemical composition the geometric dimensions of the object of heating and on the coolant regime parameters. A unique opportunity is opened by using the generalized models, combined with empirically derived equations and the technique of engineering calculation of these processes, to design a rational modes of heat treatment of raw materials and to optimize the performance of thermal equipment.

Characterization by transmission electron microscopy of a JRQ steel subjected to different heat treatments

International Nuclear Information System (INIS)

Moreno G, N.

2014-01-01

In this work a study was conducted on the steel Astm A-533, Grade B, Class 1 of reference JRQ, for the purpose of carrying out a study by transmission electron microscopy on the size and distribution of precipitates in steel samples JRQ previously subjected to heat treatments. This because the reactor vessels of the nuclear power plant of Laguna Verde, are made of a steel Astm A-533 Grade B, Class 1. It is known that the neutron radiation causes damage primarily embrittlement in materials that are exposed to it. However, observable damage through mechanical tests result from microstructural defects and atomic, induced by the neutron radiation. In previous studies hardening by precipitation of a JRQ steel (provided by the IAEA) was induced by heat treatments, finding that the conditions of heat treatment that reproduce the hardness and stress mechanical properties of a steel Astm A-533, Grade B, Class 1 irradiated for 8 years to a fluence of 3.5 x 10 17 neutrons/cm 2 and to a temperature of 290 grades C are achieved with annealing treatments at 550 grades C. In the studied samples it was found that the more hardening phase both the heat treatments as the neutron radiation, is the bainite, being the ferrite practically unchanged. Which it gave the tone to believe that the ferrite is the phase that provides at level macro the mechanical properties in stress, since in the irradiated samples such properties remained unchanged with respect to the non-irradiated material, however changes were observed in material ductility, which may be attributable to the change of hardness in the bainite, which opens a possibility for modeling the micromechanical behavior of this material. (Author)

Abnormal Grain Growth in the Heat Affected Zone of Friction Stir Welded Joint of 32Mn-7Cr-1Mo-0.3N Steel during Post-Weld Heat Treatment

Directory of Open Access Journals (Sweden)

Yijun Li

2018-04-01

Full Text Available The abnormal grain growth in the heat affected zone of the friction stir welded joint of 32Mn-7Cr-1Mo-0.3N steel after post-weld heat treatment was confirmed by physical simulation experiments. The microstructural stability of the heat affected zone can be weakened by the welding thermal cycle. It was speculated to be due to the variation of the non-equilibrium segregation state of solute atoms at the grain boundaries. In addition, the pressure stress in the welding process can promote abnormal grain growth in the post-weld heat treatment.

Heat treatment device for extending the life of a pressure vessel, particularly a reactor pressure vessel

International Nuclear Information System (INIS)

Krauss, P.; Mueller, E.; Poerner, H.; Weber, R.

1979-01-01

A support body in the form of an insulating cylinder is tightly sealed by connected surfaces at its outer circumference to the inner wall of the pressure vessel. It forms an annular heating space. The heat treatment or tempering of the pressure vessel takes place with the reactor space empty and screened from the outside by ceiling bolts. Heating gas or an induction winding can be used as the means of heating. (DG) [de

Sensitivity of Austempering Heat Treatment of Ductile Irons to Changes in Process Parameters

Science.gov (United States)

Boccardo, A. D.; Dardati, P. M.; Godoy, L. A.; Celentano, D. J.

2018-03-01

Austempered ductile iron (ADI) is frequently obtained by means of a three-step austempering heat treatment. The parameters of this process play a crucial role on the microstructure of the final product. This paper considers the influence of some process parameters (i.e., the initial microstructure of ductile iron and the thermal cycle) on key features of the heat treatment (such as minimum required time for austenitization and austempering and microstructure of the final product). A computational simulation of the austempering heat treatment is reported in this work, which accounts for a coupled thermo-metallurgical behavior in terms of the evolution of temperature at the scale of the part being investigated (the macroscale) and the evolution of phases at the scale of microconstituents (the microscale). The paper focuses on the sensitivity of the process by looking at a sensitivity index and scatter plots. The sensitivity indices are determined by using a technique based on the variance of the output. The results of this study indicate that both the initial microstructure and the thermal cycle parameters play a key role in the production of ADI. This work also provides a guideline to help selecting values of the appropriate process parameters to obtain parts with a required microstructural characteristic.

Sensitivity of Austempering Heat Treatment of Ductile Irons to Changes in Process Parameters

Science.gov (United States)

Boccardo, A. D.; Dardati, P. M.; Godoy, L. A.; Celentano, D. J.

2018-06-01

Austempered ductile iron (ADI) is frequently obtained by means of a three-step austempering heat treatment. The parameters of this process play a crucial role on the microstructure of the final product. This paper considers the influence of some process parameters ( i.e., the initial microstructure of ductile iron and the thermal cycle) on key features of the heat treatment (such as minimum required time for austenitization and austempering and microstructure of the final product). A computational simulation of the austempering heat treatment is reported in this work, which accounts for a coupled thermo-metallurgical behavior in terms of the evolution of temperature at the scale of the part being investigated (the macroscale) and the evolution of phases at the scale of microconstituents (the microscale). The paper focuses on the sensitivity of the process by looking at a sensitivity index and scatter plots. The sensitivity indices are determined by using a technique based on the variance of the output. The results of this study indicate that both the initial microstructure and the thermal cycle parameters play a key role in the production of ADI. This work also provides a guideline to help selecting values of the appropriate process parameters to obtain parts with a required microstructural characteristic.

Synergistic effects of heat and irradiation treatment (thermoradiation) in the sterilization of medical products

International Nuclear Information System (INIS)

Trauth, C.A. Jr.; Sivinski, H.D.

1975-01-01

This paper describes a generic class of sterilization processes is which properly chosen combinations of radiation and heat synergistically inactivate many bacteria and viruses. Treatments with optimal combinations are shown to offer the possibility of using lower total doses and lower temperatures than would be required separately for sterilization. This results from easier elimination of heat-labile, radioresistant organisms and radiolabile, heat-resistant organisms, and from synergistic inactivation of organisms which are both radioresistant and heat resistant. These processes depend upon temperature, dose-rate, and time in fairly complex ways; therefore, an analytical framework in which they can be defined is also presented. (author)

Influence of prolonged storage process, pasteurization, and heat treatment on biologically-active human milk proteins.

Science.gov (United States)

Chang, Jih-Chin; Chen, Chao-Huei; Fang, Li-Jung; Tsai, Chi-Ren; Chang, Yu-Chuan; Wang, Teh-Ming

2013-12-01

The bioactive proteins in human milk may be influenced by prolonged storage process, pasteurization, and heat treatment. This study was conducted to evaluate the effects of these procedures. Three forms of human milk - freshly expressed, frozen at -20°C for a prolonged duration, and pasteurized milk - were collected from 14 healthy lactating mothers and a milk bank. The concentrations of major bioactive proteins (secretory immunoglobulin A, lactoferrin, lysozyme, and leptin) were quantified using enzyme-linked immunosorbent assay kits. Changes in these proteins by heat treatment at 40°C or 60°C for 30 minutes were further evaluated. The mean concentrations of lactoferrin and secretory immunoglobulin A were significantly reduced by 66% and 25.9%, respectively, in pasteurized milk compared with those in freshly-expressed milk. Heat treatment at 40°C or 60°C did not cause significant changes in lactoferrin and secretory immunoglobulin A, but there was an apparent increase in lysozyme (p = 0.016). There were no significant differences in leptin level among these three forms of milk prior to (p = 0.153) or after heat treatment (p = 0.053). Various freezing/heating/pasteurization processes applied to human milk prior to delivery to neonates could affect the concentration of immunomodulatory proteins, especially lactoferrin, secretory immunoglobulin A, and lysozyme. Leptin was unaffected by the various handling processes tested. Fresh milk was found to be the best food for neonates. Further studies are warranted to evaluate the functional activity of these proteins and their effects on infants' immunological status. Copyright © 2013. Published by Elsevier B.V.

Heat treatment of Ti6Al4V produced by Selective Laser Melting: Microstructure and mechanical properties

International Nuclear Information System (INIS)

Vrancken, Bey; Thijs, Lore; Kruth, Jean-Pierre; Van Humbeeck, Jan

2012-01-01

Highlights: ► Responses of SLM-produced and wrought Ti6Al4V to heat treatment are compared. ► Temperature is found to be the controlling parameter for treatments in the α + β range. ► Ductility could be improved by a factor of 85%, from 7.27% to 13.59%. ► An optimal heat treatment for SLM produced Ti6Al4V is proposed. - Abstract: The present work shows that optimization of mechanical properties via heat treatment of parts produced by Selective Laser Melting (SLM) is profoundly different compared to conventionally processed Ti6Al4V. In order to obtain optimal mechanical properties, specific treatments are necessary due to the specific microstructure resulting from the SLM process. SLM is an additive manufacturing technique through which components are built by selectively melting powder layers with a focused laser beam. The process is characterized by short laser-powder interaction times and localized high heat input, which leads to steep thermal gradients, rapid solidification and fast cooling. In this research, the effect of several heat treatments on the microstructure and mechanical properties of Ti6Al4V processed by SLM is studied. A comparison is made with the effect of these treatments on hot forged and subsequently mill annealed Ti6Al4V with an original equiaxed microstructure. For SLM produced parts, the original martensite α′ phase is converted to a lamellar mixture of α and β for heat treating temperatures below the β-transus (995 °C), but features of the original microstructure are maintained. Treated above the β-transus, extensive grain growth occurs and large β grains are formed which transform to lamellar α + β upon cooling. Post treating at 850 °C for 2 h, followed by furnace cooling increased the ductility of SLM parts to 12.84 ± 1.36%, compared to 7.36 ± 1.32% for as-built parts.

Heat treatment of thin NiTi filaments by electric current

Czech Academy of Sciences Publication Activity Database

Pilch, Jan; Heller, Luděk; Šittner, Petr

2010-01-01

Roč. 2, č. 1 (2010), 1-4 ISSN N R&D Projects: GA ČR GAP108/10/1296; GA AV ČR(CZ) IAA200100627 Grant - others:EC "UPWIND" -Integrated Wind Turbine Design(XE) 019945 (SES6) Institutional research plan: CEZ:AV0Z10100520 Keywords : NiTi * SMA * heat treatment * martensitic transformation Subject RIV: BM - Solid Matter Physics ; Magnetism

Heat treatment effect on impact strength of 40Kh steel

International Nuclear Information System (INIS)

Golubev, V.K.; Novikov, S.A.; Sobolev, Yu.S.; Yukina, N.A.

1984-01-01

The paper presents results of studies on the effect of heat treatment on strength and pattern of 40Kh steel impact failure. Loading levels corresponding to macroscopic spalling microdamage initiation in the material are determined for three initial states. Metallographic study on the spalling failure pattern for 40Kh steel in different initial states and data on microhardness measurement are presented

Fabrication and heat treatment of high strength Al-Cu-Mg alloy processed using selective laser melting

Science.gov (United States)

Zhang, Hu; Zhu, Haihong; Nie, Xiaojia; Qi, Ting; Hu, Zhiheng; Zeng, Xiaoyan

2016-04-01

The proposed paper illustrates the fabrication and heat treatment of high strength Al-Cu-Mg alloy produced by selective laser melting (SLM) process. Al-Cu-Mg alloy is one of the heat treatable aluminum alloys regarded as difficult to fusion weld. SLM is an additive manufacturing technique through which components are built by selectively melting powder layers with a focused laser beam. The process is characterized by short laser-powder interaction times and localized high heat input, which leads to steep thermal gradients, rapid solidification and fast cooling. In this research, 3D Al-Cu-Mg parts with relative high density of 99.8% are produced by SLM from gas atomized powders. Room temperature tensile tests reveal a remarkable mechanical behavior: the samples show yield and tensile strengths of about 276 MPa and 402 MPa, respectively, along with fracture strain of 6%. The effect of solution treatment on microstructure and related tensile properties is examined and the results demonstrate that the mechanical behavior of the SLMed Al-Cu-Mg samples can be greatly enhanced through proper heat treatment. After T4 solution treatment at 540°C, under the effect of precipitation strengthening, the tensile strength and the yield strength increase to 532 MPa and 338 MPa, respectively, and the elongation increases to 13%.

Differential effect of prior heat treatment on the thermal enhancement of radiation damage in the ear of the mouse

International Nuclear Information System (INIS)

Law, M.P.; Ahier, R.G.

1982-01-01

The effect of prior heat treatment on thermal enhancement of radiodermatitis was investigated in the ear of the mouse. Ears were heated by immersion in hot water. A priming treatment of 43.5 0 C for 30 min (H) was given at various times before a second combined treatment of hypethermia at 43.5 0 C (h) given immediately before (hX) or after (Xh) a dose of X rays (X). The effect of H was measured in two ways. The heating time h, required to cause a given enhancement of radiodermatitis was estimated by fixing X and varying the duration of h. The thermal enhancement ratio, defined as the dose of X rays alone divided by the dose of X rays with heat required to cause a given reaction, was measured by fixing h and varying X. The priming treatment H reduced the skin response to hX. This effect was such that at 24 to 96 hr after H, the heating time h, had to be increased to about 1.5 times that required without prior hyperthermia. In contrast, the priming treatment had no effect on the response to Xh

QUALITY IMPROVEMENT OF SECONDARY SILUMINS BY USING REFINING-MODIFYING, HEAT AND LASER TREATMENTS

Directory of Open Access Journals (Sweden)

I. P. Volchok

2014-10-01

Full Text Available Purpose. As a rule secondary silumins are characterized by lower quality than their primary analogues. During manufacture of alloys a large quantity of intermetallides, first of all on the basis of iron, in their structure is ignored. To achieve the optimum level of properties it is necessary to search for ways to adapt refining-modifying, heat and laser treatments to peculiarities of the structure of secondary Al-Si alloys. Methodology. The research was carried out by using standard methods of metallographic analysis, determination of foundry, mechanical and service properties of alloys according to rotatable plans of multifactor experiments. Findings. It was established, that refiningmodifying treatment is a required procedure during manufacture of secondary silumins as it permits to effectively influence the iron-containing phases' segregations by changing their morphology, size and distribution and to increase the effectiveness of further treatment in solid state. It was found that standard modes of heat treatment are not optimal for secondary silumins. Laser treatment has shown high effectiveness in increasing of strength, wear resistance, corrosion and cavitation resistance of secondary Al-Si alloys, and the increased iron content contributed to additional solid solution hardening. Originality. It was established, that after refining-modifying treatment the phase Al5SiFe, which crystallizes in the shape of long stretched plates transformed into phase Al15(FeMn3Si2 in skeletal or polyhedral shape. The relationship between iron content in secondary silumins and holding time during heat treatment that ensures optimum of mechanical properties was obtained. It was proved that the presence of ironcontaining intermetallides Al5SiFe results in the decrease of hardened layer's depth during laser treatment. It was established, that with increasing of iron concentration the corrosion rate of secondary silumins in 3 % NaCl + 0.1 % H2O2 and 10 % HCl

Influence of heat treatment on the wear life of hydraulic fracturing tools

Energy Technology Data Exchange (ETDEWEB)

Zheng, Chao; Liu, Yonghong; Wang, Hanxiang; Qin, Jie; Shen, Yang; Zhang, Shihong [China University of Petroleum, Qingdao (China)

2017-02-15

Wear phenomenon has caused severe damage or failure of fracturing tools in oil and gas industry. In this paper, influence of heat treatment on the mechanical properties and wear resistance of fracturing tool made of lamellar graphite grey cast iron were investigated. The surface composition and microstructure were characterized by X-ray diffraction (XRD) and metallographic microscope. Sliding wear tests were performed to study the tribological behavior. Tests results showed that wear rates of treated specimens decreased by 33 %. Besides, worn morphology and wear debris were analyzed using Scanning electron microscope (SEM) and Energy dispersive Xray spectra (EDS). Wear failure mechanisms of specimens were identified. Furthermore, on-site experiment results indicated that wear loss of treated samples decreased by 37.5 %. The wear life of hydraulic fracturing tools can be improved obviously by the heat treatment.

Influence of heat treatment on the wear life of hydraulic fracturing tools

International Nuclear Information System (INIS)

Zheng, Chao; Liu, Yonghong; Wang, Hanxiang; Qin, Jie; Shen, Yang; Zhang, Shihong

2017-01-01

Wear phenomenon has caused severe damage or failure of fracturing tools in oil and gas industry. In this paper, influence of heat treatment on the mechanical properties and wear resistance of fracturing tool made of lamellar graphite grey cast iron were investigated. The surface composition and microstructure were characterized by X-ray diffraction (XRD) and metallographic microscope. Sliding wear tests were performed to study the tribological behavior. Tests results showed that wear rates of treated specimens decreased by 33 %. Besides, worn morphology and wear debris were analyzed using Scanning electron microscope (SEM) and Energy dispersive Xray spectra (EDS). Wear failure mechanisms of specimens were identified. Furthermore, on-site experiment results indicated that wear loss of treated samples decreased by 37.5 %. The wear life of hydraulic fracturing tools can be improved obviously by the heat treatment

Residual stress and mechanical properties of SiC ceramic by heat treatment

International Nuclear Information System (INIS)

Yoon, H.K.; Kim, D.H.; Shin, B.C.

2007-01-01

Full text of publication follows: Silicon carbide is a compound of relatively low density, high hardness, elevated thermal stability and good thermal conductivity, resulting in good thermal shock resistance. Because of these properties, SiC materials are widely used as abrasives and refractories. In this study, SiC single and poly crystals was grown by the sublimation method using the SiC seed crystal and SiC powder as the source material. Mechanical properties of SiC single and poly crystals are carried out by using the nano-indentation method and small punch test after the heat treatment. As a result, mechanical properties of SiC poly crystal had over double than single. And SiC single and poly crystals were occurred residual stress, but residual stress was shown relaxant properties by the effect of heat treatment. (authors)

Applicability of Solid Solution Heat Treatments to Aluminum Foams

Directory of Open Access Journals (Sweden)

Miguel Rodríguez-Pérez

2012-12-01

Full Text Available Present research work evaluates the influence of both density and size on the treatability of Aluminum-based (6000 series foam-parts subjected to a typical solid solution heat treatment (water quenching. The results are compared with those obtained for the bulk alloy, evaluating the fulfilment of cooling requirements. Density of the foams was modeled by tomography analysis and the thermal properties calculated, based on validated density-scaled models. With this basis, cooling velocity maps during water quenching were predicted by finite element modeling (FEM in which boundary conditions were obtained by solving the inverse heat conduction problem. Simulations under such conditions have been validated experimentally. Obtained results address incomplete matrix hardening for foam-parts bigger than 70 mm in diameter with a density below 650 kg/m3. An excellent agreement has been found in between the predicted cooling maps and final measured microhardness profiles.

Effect of Heat Treatment Parameters on the Microstructure and Properties of Inconel-625 Superalloy

Science.gov (United States)

Sukumaran, Arjun; Gupta, R. K.; Anil Kumar, V.

2017-07-01

Inconel-625 is a solid solution-strengthened alloy used for long-duration applications at high temperatures and moderate stresses. Different heat treatment cycles (temperatures of 625-1025 °C and time of 2-6 h) have been studied to obtain optimum mechanical properties suitable for a specific application. It has been observed that room temperature strength and, hardness decreased and ductility increased with increase in heat treatment temperature. The rate of change of these properties is found to be moderate for the samples heat-treated up to 850 °C, and thereafter, it increases rapidly. It is attributed to the microstructural changes like dissolution of carbides, recrystallization and grain growth. Microstructures are found to be predominantly single-phase austenitic with the presence of fine alloy carbides. The presence of twins is observed in samples heat-treated at lower temperature, which act as nucleation sites for recrystallization at 775 °C. Beyond 850 °C, the role of carbides present in the matrix is subsided by the coarsening of recrystallized grains and finally at 1025 °C, significant dissolution of carbide results in substantial reduction in strength and increase in ductility. Elongation to an extent of >71% has been obtained in sample heat-treated at 1025 °C indicating excellent tendency for cold workability. Failure of heat-treated specimens is found to be mainly due to carbide particle-matrix decohesion which acts as locations for crack initiation.

Effects of post-weld heat treatment on microstructure and mechanical properties of TLP bonded Inconel718 superalloy

International Nuclear Information System (INIS)

Cao, J.; Wang, Y.F.; Song, X.G.; Li, C.; Feng, J.C.

2014-01-01

Transient liquid phase bonding of Inconel718 superalloy was carried out using a commercial Ni–Cr–Si–B amorphous interlayer. The interfacial microstructure of Inconel718 joints was analyzed by a scanning electron microscope and a transmission electron microscope. In particular, the effects of post-weld heat treatment on the interfacial microstructure and joining properties of Inconel718 joints were investigated in detail. The results showed that the precipitation of second phases in joints induced by post-weld heat treatment were beneficial to the improvement of joint properties. A tensile strength of 1130 MPa with an elongation percentage of 7% was achieved for a sample bonded at 1050 °C/60 min+1180 °C/60 min followed by the post-weld heat treatment

Endotoxin inactivation via steam-heat treatment in dilute simethicone emulsions used in biopharmaceutical processes.

Science.gov (United States)

Britt, Keith A; Galvin, Jeffrey; Gammell, Patrick; Nti-Gyabaah, Joseph; Boras, George; Kolwyck, David; Ramirez, José G; Presente, Esther; Naugle, Gregory

2014-01-01

Simethicone emulsion is used to regulate foaming in cell culture operations in biopharmaceutical processes. It is also a potential source of endotoxin contamination. The inactivation of endotoxins in dilute simethicone emulsions was assessed as a function of time at different steam temperatures using a Limulus amebocyte lysate kinetic chromogenic technique. Endotoxin inactivation from steam-heat treatment was fit to a four-parameter double exponential decay model, which indicated that endotoxin inactivation was biphasic, consisting of fast and slow regimes. In the fast regime, temperature-related effects were dominant. Transitioning into the slow regime, the observed temperature dependence diminished, and concentration-related effects became increasingly significant. The change in the Gibbs free energy moving through the transition state indicated that a large energy barrier must be overcome for endotoxin inactivation to occur. The corresponding Arrhenius pre-exponential factor was >10(12) s(-1) suggesting that endotoxins in aqueous solution exist as aggregates. The disorder associated with the endotoxin inactivation reaction pathway was assessed via the change in entropy moving through the transition state. This quantity was positive indicating that endotoxin inactivation may result from hydrolysis of individual endotoxin molecules, which perturbs the conformation of endotoxin aggregates, thereby modulating the biological activity observed. Steam-heat treatment decreased endotoxin levels by 1-2 logarithm (log) reduction (LRV), which may be practically relevant depending on incoming raw material endotoxin levels. Antifoam efficiency and cell culture performance were negligibly impacted following steam-heat treatment. The results from this study show that steam-heat treatment is a viable endotoxin control strategy that can be implemented to support large-scale biopharmaceutical manufacturing. © 2014 American Institute of Chemical Engineers.

Effect of Heat Treatment on the Hardness and Wear of Grinding Balls

Science.gov (United States)

Aissat, Sahraoui; Sadeddine, Abdelhamid; Bradai, Mohand Amokrane; Younes, Rassim; Bilek, Ali; Benabbas, Abderrahim

2017-09-01

The effect quenching and tempering by different regimes on Rockwell hardness and wear processes of grinding balls 50 and 70 mm in diameter made of two melts of chromium-molybdenum cast iron is studied. The heating temperature for quenching is 850, 950, and 1050°C; the tempering temperature is 250, 400, and 600°C. Iron is analyzed in an electron microscope. Diffraction patterns are obtained. A model of cast iron wear is suggested and compared to the Davis model and to experimental results. An optimum heat treatment regime is proposed.

Effect of phosphorus and heat treatment on microstructure of Al-25%Si alloy

Directory of Open Access Journals (Sweden)

Bo Dang

2017-01-01

Full Text Available It is known that phosphorus can refine the primary silicon and heat treatment can spheroidize the eutectic silicon. This paper presents an optimal combination of heat treatment processes and P refinement on hypereutectic Al-Si alloy. The optimal P addition amount, and the solution and aging temperatures for Al-25%Si alloy were obtained through the orthogonal experiment, and their modification effects were discussed. The results show that P addition has the greatest modification effect, followed by aging temperature, and the modification effect of solution temperature is the least. The optimized modification parameters are: addition of 0.6% P, solution at 540 篊 and aging at 160 篊 . In addition, the cooling curve, superheating and hardness of the alloy were also analyzed.

Treatment of Phlegm- and Heat-induced Insomnia by Acupuncture in 120 Cases

Institute of Scientific and Technical Information of China (English)

崔芮; 周德安

2003-01-01

@@ Clinical Data The 120 cases in this series were outpatients suffering from insomnia due to interior-stirring by phlegm-heat, ranging in age from 28 to 67 years. They were randomly divided into a treatment group and a control group.

Influence of heat treatment on field emission characteristics of boron nitride thin films

International Nuclear Information System (INIS)

Li Weiqing; Gu Guangrui; Li Yingai; He Zhi; Feng Wei; Liu Lihua; Zhao Chunhong; Zhao Yongnian

2005-01-01

Boron nitride (BN) nanometer thin films are synthesized on Si (1 0 0) substrates by RF reactive magnetron sputtering. Then the film surfaces are treated in the case of the base pressure below 5 x 10 -4 Pa and the temperature of 800 and 1000 deg. C, respectively. And the films are studied by Fourier transform infrared spectra (FTIR), atomic force microscopic (AFM) and field emission characteristics at different annealing temperature. The results show that the surface heat treatment makes no apparent influence on the surface morphology of the BN films. The transformations of the sample emission characteristics have to do with the surface negative electron affinity (NEA) of the films possibly. The threshold electric fields are lower for BN samples without heat-treating than the treated films, which possibly ascribed to the surface negative electron affinity effect. A threshold field of 8 V/μm and the emission current of 80 μA are obtained. The surface NEA is still presence at the heat treatment temperature of 800 deg. C and disappeared at temperature of 1000 deg. C

Influence of Microstructure and Composition Changes on Mechanical Characteristics of Aluminium Alloy After Heating and Cooling Treatment

International Nuclear Information System (INIS)

Sigit; Nuraini, E; Martoyo

1998-01-01

Influences of microstructure and chemical composition changes on mechanical characteristics of AIMg2 which were heated at 85-500 0 C and cooled with sands, water or air have been studied. Microstructure observation was carried out using optical microscope, while chemical composition determination by atomic absorption spectrophotometry (AAS). AIMg2 which has been heated at the relatively low temperature i. e, 200 0 C during 6 hours and cooled using sands showed a small change microstructure, but those will be clearly observed on the treatment at 300 0 C. The microstructure change is in agreement with the change of mechanical characteristic, I. e., the decreasing of tensile strength and hardness and increasing of elongation. After the temperature of treatment is higher than 300 0 C, the decreasing of the tensile strength was relatively constant, while the hardness increased. The microstructure of AIMg2 resulted from the heat treatment at temperature of 500 0 C was different with that of 300 0 C. Heat treatment at 500 0 C following by cooling in the sands, water or air respectively gave similar microstructure. Those also caused the change of alloying element content which was in agreement with decreasing of mechanical characteristics

Heat treatment, microstructure and mechanical properties of a C–Mn–Al–P hot dip galvanizing TRIP steel

International Nuclear Information System (INIS)

Ding, Wei; Hedström, Peter; Li, Yan

2016-01-01

Heat treatments of a hot dip galvanizing TRIP (Transformation induced plasticity) steel with chemical composition 0.20C-1.50Mn-1.2Al-0.07P(mass%) were performed in a Gleeble 3500 laboratory equipment. The heat treatment process parameters were varied to investigate the effect of intercritical annealing temperature as well as isothermal bainitic transformation (IBT) temperature and time, on the microstructure and the mechanical properties. The microstructure was investigated using scanning electron microscopy, transmission electron microscopy and x-ray diffraction, while mechanical properties were evaluated by tensile testing. Furthermore, to generate a better understanding of the phase transformations during heat treatment, dilatometry trials were conducted. The desired microstructure containing ferrite, bainite, retained austenite and martensite was obtained after the heat treatments. It was further found that the IBT is critical in determining the mechanical properties of the steel, since it controls the fraction of bainite. With increasing bainite fraction, the fraction of retained austenite increases while the fraction of martensite decreases. The mechanical properties of the steel are excellent with a tensile strength above 780 MPa (expect in one case) and elongation above 22%.

Processing and refinement of steel microstructure images for assisting in computerized heat treatment of plain carbon steel

Science.gov (United States)

Gupta, Shubhank; Panda, Aditi; Naskar, Ruchira; Mishra, Dinesh Kumar; Pal, Snehanshu

2017-11-01

Steels are alloys of iron and carbon, widely used in construction and other applications. The evolution of steel microstructure through various heat treatment processes is an important factor in controlling properties and performance of steel. Extensive experimentations have been performed to enhance the properties of steel by customizing heat treatment processes. However, experimental analyses are always associated with high resource requirements in terms of cost and time. As an alternative solution, we propose an image processing-based technique for refinement of raw plain carbon steel microstructure images, into a digital form, usable in experiments related to heat treatment processes of steel in diverse applications. The proposed work follows the conventional steps practiced by materials engineers in manual refinement of steel images; and it appropriately utilizes basic image processing techniques (including filtering, segmentation, opening, and clustering) to automate the whole process. The proposed refinement of steel microstructure images is aimed to enable computer-aided simulations of heat treatment of plain carbon steel, in a timely and cost-efficient manner; hence it is beneficial for the materials and metallurgy industry. Our experimental results prove the efficiency and effectiveness of the proposed technique.

Heat treatment, microstructure and mechanical properties of a C–Mn–Al–P hot dip galvanizing TRIP steel

Energy Technology Data Exchange (ETDEWEB)

Ding, Wei [School of Material and Metallurgy, Inner Mongolia University of Science and Technology, Baotou 014010 (China); Department of Materials Science and Engineering, KTH Royal Institute of Technology, SE-100 44 Stockholm (Sweden); Bayan Obo multimetallic resource comprehensive utilization Key lab, Inner Mongolia University of Science and Technology, Baotou 014010 (China); Hedström, Peter [Department of Materials Science and Engineering, KTH Royal Institute of Technology, SE-100 44 Stockholm (Sweden); Li, Yan [Department of Materials Science and Engineering, KTH Royal Institute of Technology, SE-100 44 Stockholm (Sweden); Bayan Obo multimetallic resource comprehensive utilization Key lab, Inner Mongolia University of Science and Technology, Baotou 014010 (China)

2016-09-30

Heat treatments of a hot dip galvanizing TRIP (Transformation induced plasticity) steel with chemical composition 0.20C-1.50Mn-1.2Al-0.07P(mass%) were performed in a Gleeble 3500 laboratory equipment. The heat treatment process parameters were varied to investigate the effect of intercritical annealing temperature as well as isothermal bainitic transformation (IBT) temperature and time, on the microstructure and the mechanical properties. The microstructure was investigated using scanning electron microscopy, transmission electron microscopy and x-ray diffraction, while mechanical properties were evaluated by tensile testing. Furthermore, to generate a better understanding of the phase transformations during heat treatment, dilatometry trials were conducted. The desired microstructure containing ferrite, bainite, retained austenite and martensite was obtained after the heat treatments. It was further found that the IBT is critical in determining the mechanical properties of the steel, since it controls the fraction of bainite. With increasing bainite fraction, the fraction of retained austenite increases while the fraction of martensite decreases. The mechanical properties of the steel are excellent with a tensile strength above 780 MPa (expect in one case) and elongation above 22%.

Influence of Heat Treatments on Electrical Properties and Microstructure of 10 % Mass Fraction of Sucrose YBCO Superconductor

International Nuclear Information System (INIS)

Khalida Salleh; Fariesha, F.; Azhan, H.; Yusainee, S.Y.

2013-01-01

The influence of different heat treatments on the superconducting properties of 10 % mass fraction of sucrose structure YBCO superconductor was investigated. X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM) equipment were used to determine the phase of superconductor and structural studies respectively at 10 % mass fraction of sucrose. The samples were prepared via solid state (SSM) and co-precipitation (CPM) reaction methods and underwent sintering and heat treatment process at 900, 930 and 960 degree Celsius respectively with mixing of C 12 H 22 O 11 sucrose during pelletization. The T C,on decreases with respect to higher heat treatment temperature. The suppression of both T C,on and T C,off indicates the destruction of superconductivity trends. The best T C,off were achieved in pure SSM and CPM samples sintered at 950 degree Celsius for 5 hours with T C,off 86 K and 91 K respectively. Comparing with pure YBCO, the 10 % mass fraction of sucrose YBCO exhibited higher critical current, I C by two times. It indicates the effect of high surface area in porous structure. The XRD results confirmed that all the samples remain in single phase, which indicates no effect of sucrose in the porous structures sample and maintaining in orthorhombic structure. Higher heat treatment at 960 degree Celsius resulted in destruction on its superconductivity behavior due to the partial melt phase on its microstructure, especially in CPM. This is due to the smaller grain size of samples which trapped more heat and causing partial melting to occur rapidly. It can be deduced that, annealing temperatures at 900 and 930 degree Celsius are the best optimum heat treatments for CPM and SSM porous superconductor, respectively. (author)

Effect of heat treatment oanas irradiation, and combined treatment on the shelf of fresh avocados (Persea americana L)

International Nuclear Information System (INIS)

Purwanto, Z.I.; Maha, Munsiah

1987-01-01

Effects of heat treatment, gamma irradiation, and combined treatments on the shelf-life of fresh avocados (Persea americana L.). Experiments to determine the effective irradiation conditions to prolong the shelf-life of fresh avocados were conducted at the centre for the Application of Isotopes washed and dried, then divided into 4 groups, namely for control (A), dipped in hot water at 40 0 C for 20 minutes (heat treatment, B), irradiated at a dose of 25 Gy (C), and combination of hot water dipping (40 0 C for 20 minutes) and irradiation at a 25 Gy (D). The samples were stored at room temperature. Evaluation on physical and chemical properties of the samples was done daily up to 10 days' storage. Parameters observed were texture, moisture and fat contents, percentage of weight loss, percentage of mature fruit, and subjective organoleptic evaluation. It was found that treated samples with and without combination treatment were still in good condition until 10 days of storage. It could be concluded that dipping in hot water, either alone or in combination with irradiation at a dose of 25 Gy could extend the shelf-life of fresh avocado up to 10 days at room temperature compared to only 5 days of the control. (author). 2 figs, 8 refs

Effect of an Intermediate Heat-treatment on a Change of the Corrosion Resistance and Hardness of a HANA-4 Outer Strip

International Nuclear Information System (INIS)

Lee, Myung Ho; Jung, Yang Il; Park, Sang Yoon; Choi, Byoung Kwon; Park, Jeong Yong; Jeong, Yong Hwan; Eom, Kyong Bo; Park, Nam Gyu; Lim, Yoon Soo

2008-01-01

KAERI (Korea Atomic Energy Research Institute) in collaboration with KNF (Korea Nuclear Fuel) undertook some researches on the applicability of HANA-4 and HANA-6 alloys for the spacer grid for a PWR (Pressurized Water Reactor) nuclear fuel. As a part of the research, KAERI studied the effect of the final heat-treatment on the mechanical and corrosion properties of a HANA-4 inner strip. The strip was manufactured with a sheet which had been intermediately heat-treated at about 580 .deg. C for 2.5-4 hours after each cold rolling before being processed into the final strip product. It was mentioned that the process with the intermediate heat treatment needed reviewing to establish an improved manufacturing process for the cold rolling. So, this work tried to check the effect of an intermediate heat-treatment on the properties of a HANA-4 strip using a specimen that was taken from a second hot rolled material before a cold-rolling. The manufacturing processes, with three different kinds of annealings, were introduced to investigate the applicable intermediate heat-treatment process. After all the cold-rolling processes, the Vickers hardness was measured for the final annealed specimens and 60 days of corrosion tests were carried out to check on the effect of the intermediate heat-treatment. Finally, an appropriate intermediate heat-treatment was proposed to improve the manufacturability of the HANA-4 strip

Heat Stroke

DEFF Research Database (Denmark)

Mørch, Sofie Søndergaard; Andersen, Johnny Dohn Holmgren; Bestle, Morten Heiberg

2017-01-01

not diagnosed until several days after admittance; hence treatment with cooling was delayed. Both patients were admitted to the intensive care unit, where they were treated with an external cooling device and received treatment for complications. Both cases ended fatally. As global warming continues, more heat......Heat stroke is an acute, life-threatening emergency characterized clinically by elevated body temperature and central nervous system dysfunction. Early recognition and treatment including aggressive cooling and management of life-threatening systemic complications are essential to reduce morbidity...... and mortality. This case report describes two Danish patients diagnosed with heat stroke syndrome during a heat wave in the summer of 2014. Both patients were morbidly obese and had several predisposing illnesses. However since heat stroke is a rare condition in areas with temperate climate, they were...

A support system in virtual reality for effective hyperthermia treatments. Heating properties of needle applicator for brain tumors

International Nuclear Information System (INIS)

Shindo, Yasuhiro; Iseki, Yuya; Nakane, Kazuya; Mimoto, Naoki; Kubo, Mitsunori; Kato, Kazuo; Takahashi, Hideaki; Uzuka, Takeo; Fujii, Yukihiko

2011-01-01

This paper describes the effectiveness of the developed simulator system for performing an effective hyperthermia treatment with a needle applicator in virtual reality (VR). The human brain is protected by the skull, which makes it difficult to non-invasively heat deep brain tumors with electromagnetic energy. Generally, needle applicators were used in clinical practice to heat brain tumors. However, some problems exist. One is that this heating method has a small heating area around the needle. In order to expand the heating area of a needle applicator, we developed a new type of needle applicator made from a shape memory alloy (SMA). The thermal properties of the SMA were checked experimentally using the developed heating system. As a result, the proposed needle applicator made of SMA is useful to create a wider heating area inside a tumor. Another problem is that medical doctors find it difficult to put a needle applicator into a target point inside of tumors. Therefore, a support system for performing an effective hyperthermia treatment is required in the clinic. In this paper, first, we constructed an anatomical 3-D model from magnetic resonance imaging (MRI) and X-ray computed tomography (CT) images by using 3-D computer aided design (CAD) software. Second, we presented the finite element method (FEM) model which is divided into non-linear elements on 3-D computer graphics (CG). Finally, we calculated temperature distributions using the 3-D FEM model with blood perfusion during hyperthermia treatments. From these results, it was found that the proposed VR system is effective for performing hyperthermia treatments. (author)

No major differences found between the effects of microwave-based and conventional heat treatment methods on two different liquid foods.

Science.gov (United States)

Géczi, Gábor; Horváth, Márk; Kaszab, Tímea; Alemany, Gonzalo Garnacho

2013-01-01

Extension of shelf life and preservation of products are both very important for the food industry. However, just as with other processes, speed and higher manufacturing performance are also beneficial. Although microwave heating is utilized in a number of industrial processes, there are many unanswered questions about its effects on foods. Here we analyze whether the effects of microwave heating with continuous flow are equivalent to those of traditional heat transfer methods. In our study, the effects of heating of liquid foods by conventional and continuous flow microwave heating were studied. Among other properties, we compared the stability of the liquid foods between the two heat treatments. Our goal was to determine whether the continuous flow microwave heating and the conventional heating methods have the same effects on the liquid foods, and, therefore, whether microwave heat treatment can effectively replace conventional heat treatments. We have compared the colour, separation phenomena of the samples treated by different methods. For milk, we also monitored the total viable cell count, for orange juice, vitamin C contents in addition to the taste of the product by sensory analysis. The majority of the results indicate that the circulating coil microwave method used here is equivalent to the conventional heating method based on thermal conduction and convection. However, some results in the analysis of the milk samples show clear differences between heat transfer methods. According to our results, the colour parameters (lightness, red-green and blue-yellow values) of the microwave treated samples differed not only from the untreated control, but also from the traditional heat treated samples. The differences are visually undetectable, however, they become evident through analytical measurement with spectrophotometer. This finding suggests that besides thermal effects, microwave-based food treatment can alter product properties in other ways as well.

No major differences found between the effects of microwave-based and conventional heat treatment methods on two different liquid foods.

Directory of Open Access Journals (Sweden)

Gábor Géczi

Full Text Available Extension of shelf life and preservation of products are both very important for the food industry. However, just as with other processes, speed and higher manufacturing performance are also beneficial. Although microwave heating is utilized in a number of industrial processes, there are many unanswered questions about its effects on foods. Here we analyze whether the effects of microwave heating with continuous flow are equivalent to those of traditional heat transfer methods. In our study, the effects of heating of liquid foods by conventional and continuous flow microwave heating were studied. Among other properties, we compared the stability of the liquid foods between the two heat treatments. Our goal was to determine whether the continuous flow microwave heating and the conventional heating methods have the same effects on the liquid foods, and, therefore, whether microwave heat treatment can effectively replace conventional heat treatments. We have compared the colour, separation phenomena of the samples treated by different methods. For milk, we also monitored the total viable cell count, for orange juice, vitamin C contents in addition to the taste of the product by sensory analysis. The majority of the results indicate that the circulating coil microwave method used here is equivalent to the conventional heating method based on thermal conduction and convection. However, some results in the analysis of the milk samples show clear differences between heat transfer methods. According to our results, the colour parameters (lightness, red-green and blue-yellow values of the microwave treated samples differed not only from the untreated control, but also from the traditional heat treated samples. The differences are visually undetectable, however, they become evident through analytical measurement with spectrophotometer. This finding suggests that besides thermal effects, microwave-based food treatment can alter product properties in other

Mild heat treatments induce long-term changes in metabolites associated with energy metabolism in Drosophila melanogaster

DEFF Research Database (Denmark)

Sarup, Pernille; Petersen, Simon Metz Mariendal; Nielsen, Niels Christian

2016-01-01

treatments on the metabolome of male Drosophila melanogaster. 10 days after the heat treatment, metabolic aging appears to be slowed down, and a treatment response with 40 % higher levels of alanine and lactate and lower levels of aspartate and glutamate were measured. All treatment effects had disappeared...

Microstructure evolution during spray rolling and heat treatment of 2124 Al

Energy Technology Data Exchange (ETDEWEB)

McHugh, K.M. [Industrial Technology Department, Idaho National Laboratory, Idaho Falls, ID 83415-2050 (United States)], E-mail: kevin.mchugh@inl.gov; Lin, Y.; Zhou, Y.; Johnson, S.B.; Delplanque, J.-P.; Lavernia, E.J. [Department of Chemical Engineering and Materials Science, University of California, Davis, CA 95616 (United States)

2008-03-25

Spray rolling is a strip-casting technology that combines elements of spray forming and twin-roll casting. It consists of atomizing molten metal with a high velocity inert gas, quenching the resultant droplets in flight, and directing the spray between mill rolls. In-flight convection heat transfer from atomized droplets and conduction heat transfer at the rolls rapidly remove the metal's latent heat. Hot deformation of the semi-solid material in the rolls results in fully consolidated, rapidly-solidified strip. Spray rolling operates at a higher solidification rate than conventional twin-roll casting and is able to process a broader range of alloys at high production rates. A laboratory-scale strip caster was constructed and used to evaluate the interplay of processing parameters and strip quality for strips up to 200 mm wide and 1.6-6.4 mm thick. This paper examines microstructure evolution during spray rolling and explores how gas-to-metal mass flow ratio influences the microstructure and mechanical properties of spray-rolled 2124 Al. The influences of solution heat treatment and cold rolling on grain structure and constituent particle spheroidization are also examined.

Effect of high temperature heat treatments on the quality factor of a large-grain superconducting radio-frequency niobium cavity

Science.gov (United States)

Dhakal, P.; Ciovati, G.; Myneni, G. R.; Gray, K. E.; Groll, N.; Maheshwari, P.; McRae, D. M.; Pike, R.; Proslier, T.; Stevie, F.; Walsh, R. P.; Yang, Q.; Zasadzinzki, J.

2013-04-01

Large-grain Nb has become a viable alternative to fine-grain Nb for the fabrication of superconducting radio-frequency cavities. In this contribution we report the results from a heat treatment study of a large-grain 1.5 GHz single-cell cavity made of “medium purity” Nb. The baseline surface preparation prior to heat treatment consisted of standard buffered chemical polishing. The heat treatment in the range 800-1400°C was done in a newly designed vacuum induction furnace. Q0 values of the order of 2×1010 at 2.0 K and peak surface magnetic field (Bp) of 90 mT were achieved reproducibly. A Q0 value of (5±1)×1010 at 2.0 K and Bp=90mT was obtained after heat treatment at 1400°C. This is the highest value ever reported at this temperature, frequency, and field. Samples heat treated with the cavity at 1400°C were analyzed by secondary ion mass spectrometry, x-ray photoelectron spectroscopy, energy dispersive x ray, point-contact tunneling, and x-ray diffraction, and revealed a complex surface composition which includes titanium oxide, increased carbon, and nitrogen content but reduced hydrogen concentration compared to a non-heat-treated sample.

Effects of post-heat treatment on microstructure and properties of laser cladded composite coatings on titanium alloy substrate

Science.gov (United States)

Li, G. J.; Li, J.; Luo, X.

2015-01-01

The composite coatings were produced on the Ti6Al4V alloy substrate by laser cladding. Subsequently, the coatings were heated at 500 °C for 1 h and 2 h and then cooled in air. Effects of post-heat treatment on microstructure, microhardness and fracture toughness of the coatings were investigated by scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive spectroscopy (EDS), optical microscopy (OM). Wear resistance of the coatings was evaluated under the dry sliding reciprocating friction condition at room temperature. The results indicated that the coatings mainly consist of a certain amount of coarse white equiaxed WC particles surrounded by the white-bright W2C, a great deal of fine dark spherical TiC particles and the matrix composed of the α(Ti), Ti2Ni and TiNi phases. Effects of the post-heat treatment on phase constituents and microstructure of the coatings were almost negligible due to the low temperature. However, the post-heat treatment could decrease the residual stress and increase fracture toughness of the coatings, and fracture toughness of the coatings was improved from 2.77 MPa m1/2 to 3.80 MPa m1/2 and 4.43 MPa m1/2 with the heat treatment for 1 h and 2 h, respectively. The mutual role would contribute to the reduction in cracking susceptibility. Accompanied with the increase in fracture toughness, microhardness of the coatings was reduced slightly. The dominant wear mechanism for all the coatings was abrasive wear, characterized by micro-cutting or micro-plowing. The heat treatment could significantly decrease the average friction coefficient and reduce the fluctuation of the friction coefficient with the change in sliding time. The appropriate heat treatment time (approximately 1 h) had a minimal effect on wear mass loss and volume loss. Moreover, the improvement in fracture toughness will also be beneficial to wear resistance of the coatings under the long service.

Effect of T6 heat treatment on damping characteristics of Al/RHA ...

Indian Academy of Sciences (India)

Abstract. In the present work, effect of T6 heat treatment on the damping behaviour of aluminum/rice husk ash .... alloy-based composites, there is dearth of information on the damping ... fication. Using the process 4, 6 and 8% by weight, RHA.

Decreased survival of prostate cancer cells in vitro by combined treatment of heat and an antioxidant inhibitor diethyldithiocarbamate (DDC).

Science.gov (United States)

Moriyama-Gonda, Nobuko; Igawa, Mikio; Shiina, Hiroaki; Urakami, Shinji; Terashima, Masaharu

2003-11-01

The aim of this study was to examine a modulation of thermotolerance by treatment with combination of heat and the antioxidant inhibitor diethyldithiocarbamate (DDC) of the PC-3 prostate cancer cells. To determine thermotolerance, cells were heated once or twice. Two 1 h exposures at 43 degrees C, with a recovery period in between, revealed better survival/recovery of cells after the second exposure than after the first (fig. 1A + 1B). Additional experiments were performed, heating cells twice (fig. 1B + 1C). First, cells were heated at 43 degrees C for 1 h and, after various recovery times (intervals) at 37 degree C, subsequently reheated at 44 degrees C for 1 h. To ensure effective cell killing, efficiency of the combined treatments of 1 mM DDC and heating at 43 or 44 degrees C for 1 h was estimated by measuring cell survival, reactive oxygen species (ROS) generation, superoxide dismutase (SOD) activity and heat shock protein 70 (hsp 70) expression. To obtain a more effective method for subsequent heat exposure, cells were heated twice after a 24 h interval in the presence or absence of 1 mM DDC. ROS generation and SOD activity immediately increased correlating with duration of heating, but their levels gently decreased with time after discontinuation of heating. On the other hand, hsp 70 levels slowly increased, also correlating with duration of heating but continued to increase with time after discontinuation of heating for a certain period. DDC administration coupled with heating at 43 or 44 degrees C significantly decreased cell survival compared to heating alone (p DDC as compared to heat alone at 43 and 44 degrees C (p DDC could have potential benefits in the treatment of prostate cancer.

Heat treatment eliminates 'Candidatus Liberibacter asiaticus' from infected citrus trees under controlled conditions.

Science.gov (United States)

Hoffman, Michele T; Doud, Melissa S; Williams, Lisa; Zhang, Mu-Qing; Ding, Fang; Stover, Ed; Hall, David; Zhang, Shouan; Jones, Lisa; Gooch, Mark; Fleites, Laura; Dixon, Wayne; Gabriel, Dean; Duan, Yong-Ping

2013-01-01

Huanglongbing (HLB) is one of the most destructive diseases of citrus worldwide. The three known causal agents of HLB are species of α-proteobacteria: 'Candidatus Liberibacter asiaticus', 'Ca. L. africanus', and 'Ca. L. americanus'. Previous studies have found distinct variations in temperature sensitivity and tolerance among these species. Here, we describe the use of controlled heat treatments to cure HLB caused by 'Ca. L. asiaticus', the most prevalent and heat-tolerant species. Using temperature-controlled growth chambers, we evaluated the time duration and temperature required to suppress or eliminate the 'Ca. L. asiaticus' bacterium in citrus, using various temperature treatments for time periods ranging from 2 days to 4 months. Results of quantitative polymerase chain reaction (qPCR) after treatment illustrate significant decreases in the 'Ca. L. asiaticus' bacterial titer, combined with healthy vigorous growth by all surviving trees. Repeated qPCR testing confirmed that previously infected, heat-treated plants showed no detectable levels of 'Ca. L. asiaticus', while untreated control plants remained highly infected. Continuous thermal exposure to 40 to 42°C for a minimum of 48 h was sufficient to significantly reduce titer or eliminate 'Ca. L. asiaticus' bacteria entirely in HLB-affected citrus seedlings. This method may be useful for the control of 'Ca. Liberibacter'-infected plants in nursery and greenhouse settings.

Influence of heat treatment on hole transfer dynamics in core-shell quantum dot/organic hole conductor hybrid films

Science.gov (United States)

Sun, Mingye; Zheng, Youjin; Zhang, Lei; Zhao, Liping; Zhang, Bing

2017-08-01

The influence of heat treatment on hole transfer (HT) processes from the CdSe/ZnS and CdSe/CdS/ZnS quantum dots (QDs) to 4,4‧,4″-Tris(carbazol-9-yl)-triphenylamine (TCTA) in QD/TCTA hybrid films has been researched with time-resolved photoluminescence (PL) spectroscopy. The PL dynamic results demonstrated a heat-treatment-temperature-dependent HT process from the core-shell CdSe QDs to TCTA. The HT rates and efficiencies can be effectively increased due to reduced distance between core-shell CdSe QDs and TCTA after heat treatment. The CdS shell exhibited a more obvious effect on HT from the core-shell CdSe QDs to TCTA than on electron transfer to TiO2, due to higher barrier for holes to tunnel through CdS shell and larger effective mass of holes in CdS than electrons. These results indicate that heat treatment would be an effective means to further optimize solid-state QD sensitized solar cells and rational design of CdS shell is significant.

Calculation of α/γ equilibria in SA508 grade 3 steels for intercritical heat treatment

International Nuclear Information System (INIS)

Lee, B.J.; Kim, H.D.; Hong, J.H.

1998-01-01

An attempt has been made to suggest an optimum temperature for intercritical heat treatment of an SA508 grade 3 steel for nuclear pressure vessels, based on thermodynamic calculation of the α/γ phase equilibria. A thermodynamic database constructed for the Fe-Mn-Ni-Mo-Cr-Si-V-Al-C-N ten-component system and an empirical criterion that the amount of reformed austenite should be around 40 pct were used for thermodynamic calculation and derivation of the optimum heat-treatment temperature, respectively. The calculated optimum temperature, 720 C, was in good agreement with an experimentally determined temperature of 725 C obtained through an independent experimental investigation of the same steel. The agreement between the calculated and measured fraction of reformed austenite during the intercritical heat treatment was also confirmed. Based on the agreement between calculation and experiment, it could be concluded that thermodynamic calculations can be successfully applied to the materials and/or process design as an additive tool to the already established technology, and that the currently constructed thermodynamic database for steel systems shows an accuracy that makes such applications possible

Statement on a heat treatment to control Agrilus planipennis

DEFF Research Database (Denmark)

Baker, R.; Candresse, T.; Dormannsné Simon, E.

2012-01-01

, to clarify its conclusion and indicate what data would be needed to assess the effectiveness of the new treatment. The Panel concluded that the new proposal is not within the scope of the opinion as the data provided by the US Authorities cannot be used to evaluate the effectiveness of the new proposed heat...

Effect of heat treatment on strength and abrasive wear behaviour of ...

Indian Academy of Sciences (India)

In the present investigation Al6061–SiCp composites was fabricated by liquid metallurgy route with percentages of SiCp varying from 4 wt% to 10 wt% in steps of 2 ... However, under identical heat treatment conditions, adopted Al6061–SiCp composites exhibited better microhardness and tensile strength reduced wear loss ...

Additive manufacturing of Co-Cr-Mo alloy: Influence of heat treatment on microstructure, tribological and electrochemical properties

Directory of Open Access Journals (Sweden)

Kedar Mallik Mantrala

2015-03-01

Full Text Available Co-Cr-Mo alloy samples, fabricated using Laser Engineered Net Shaping – a laser based additive manufacturing technology, have been subjected heat treatment to study its influence on microstructure, wear and corrosion properties. Following L9 Orthogonal array of Taguchi method, the samples were solutionized at 1200oC for 30, 45 and 60 min followed by water quenching. Ageing treatment was done at 815oC and 830oC for 2, 4 and 6 h. Heat treated samples were evaluated for their microstructure, hardness, wear resistance and corrosion resistance. The results revealed that highest hardness of 512 ± 58 Hv and wear rate of 0.90 ± 0.14 × 10-4 mm3/N.m can be achieved with appropriate post-fabrication heat treatment. ANOVA and grey relational analysis on the experimental data revealed that the samples subjected to solution treatment for 60 min, without ageing, exhibit best combination of hardness, wear and corrosion resistance.

Aesthetic value improvement of the ruby stone using heat treatment and its synergetic surface study

International Nuclear Information System (INIS)

Sahoo, Rakesh K.; Mohapatra, Birendra K.; Singh, Saroj K.; Mishra, Barada K.

2015-01-01

Highlights: • Natural ruby is heated at high temperature with metal oxide additives (PbO and ZnO) to enhance its aesthetic value. • Changes in surface characteristics of these natural rubies before and after heat treatment are compared. • The R-line peak splitting in the PL spectra and the contrary shift of the Al 2p peaks in the XPS spectra are explicated. - Abstract: The surface behavior of the natural ruby stones before and after heat treatment with metal oxide additives like: zinc oxide (ZnO) and lead oxide (PbO) have been studied. The surface appearance of the ruby stones processed with the metal oxides changed whereas the bulk densities of the stones remained within the range of 3.9–4.0 g/cm 3 . The cracks healing and pores filling by the metal oxides on the surface of the ruby have been examined using scanning electron microscopy. The chemical compositions based on the XPS survey scans are in good agreement with the expected composition. The phase and crystallinity of the ruby stones original and heat-treated were obtained from their X-ray diffraction patterns. The change in peak separation between R 1 and R 2 – peaks in photoluminescence spectra and the contrary binding energy shift of the Al 2p peaks in the X-ray photoelectron spectra have been explicated. Moreover, in this work we describe the change in surface chemical and physical characteristics of the ruby stone before and after heat treatment

A numerical study on dual-phase-lag model of bio-heat transfer during hyperthermia treatment.

Science.gov (United States)

Kumar, P; Kumar, Dinesh; Rai, K N

2015-01-01

The success of hyperthermia in the treatment of cancer depends on the precise prediction and control of temperature. It was absolutely a necessity for hyperthermia treatment planning to understand the temperature distribution within living biological tissues. In this paper, dual-phase-lag model of bio-heat transfer has been studied using Gaussian distribution source term under most generalized boundary condition during hyperthermia treatment. An approximate analytical solution of the present problem has been done by Finite element wavelet Galerkin method which uses Legendre wavelet as a basis function. Multi-resolution analysis of Legendre wavelet in the present case localizes small scale variations of solution and fast switching of functional bases. The whole analysis is presented in dimensionless form. The dual-phase-lag model of bio-heat transfer has compared with Pennes and Thermal wave model of bio-heat transfer and it has been found that large differences in the temperature at the hyperthermia position and time to achieve the hyperthermia temperature exist, when we increase the value of τT. Particular cases when surface subjected to boundary condition of 1st, 2nd and 3rd kind are discussed in detail. The use of dual-phase-lag model of bio-heat transfer and finite element wavelet Galerkin method as a solution method helps in precise prediction of temperature. Gaussian distribution source term helps in control of temperature during hyperthermia treatment. So, it makes this study more useful for clinical applications. Copyright © 2015 Elsevier Ltd. All rights reserved.

Karakteristik Fisikokimia Mie Kering Berbasis Pati Ubi Jalar Varietas Lokal Dengan Menggunakan Metode Heat Moisture Treatment

Directory of Open Access Journals (Sweden)

Zaidiyah Zaidiyah

2015-10-01

Full Text Available The effects of heat moisture treatment (110°C and pretreatment on the physicochemical properties of sweet potato dried-noodles starch based were investigated. Completely randomized design was performed which arranged by two-factor. The first factor is noodles consist of native starch and treated starch (heat moisture treatment. The second factor is a type of sweet potato local varieties which consists of three levels: orange, purple and cream flesh color, respectively. Native starch and treated starch treatment showed significant effect on water content, protein and carbohydrate/fiber. Water absorption and cooking loss of dried noodle is highly different between native (non-HMT and treated starch (HMT.

Effect of foam on temperature prediction and heat recovery potential from biological wastewater treatment.

Science.gov (United States)

Corbala-Robles, L; Volcke, E I P; Samijn, A; Ronsse, F; Pieters, J G

2016-05-15

Heat is an important resource in wastewater treatment plants (WWTPs) which can be recovered. A prerequisite to determine the theoretical heat recovery potential is an accurate heat balance model for temperature prediction. The insulating effect of foam present on the basin surface and its influence on temperature prediction were assessed in this study. Experiments were carried out to characterize the foam layer and its insulating properties. A refined dynamic temperature prediction model, taking into account the effect of foam, was set up. Simulation studies for a WWTP treating highly concentrated (manure) wastewater revealed that the foam layer had a significant effect on temperature prediction (3.8 ± 0.7 K over the year) and thus on the theoretical heat recovery potential (30% reduction when foam is not considered). Seasonal effects on the individual heat losses and heat gains were assessed. Additionally, the effects of the critical basin temperature above which heat is recovered, foam thickness, surface evaporation rate reduction and the non-absorbed solar radiation on the theoretical heat recovery potential were evaluated. Copyright © 2016 Elsevier Ltd. All rights reserved.

Artificial crystals with 3d metal and palladium particles subjected to high-temperature heat treatment

Science.gov (United States)

Rinkevich, A. B.; Nemytova, O. V.; Perov, D. V.; Samoylovich, M. I.; Kuznetsov, E. A.

2018-04-01

High-temperature heat treatment has valuable impact on the structure and physical properties of artificial crystals with 3d metal and palladium particles. Artificial crystals are obtained by means of introduction of particles into the interspherical voids of opal matrices. The magnetic properties are studied at the temperatures ranging from 2 to 300 K and in fields up to 350 kOe. Microwave properties are investigated in the millimeter frequency range. The complex dielectric permittivity of several nanocomposites is measured. The influence of heat treatment up to 960 °C on the structure of artificial crystals is clarified.

Non-lethal heat treatment of cells results in reduction of tumor initiation and metastatic potential

International Nuclear Information System (INIS)

Kim, Yoo-Shin; Lee, Tae Hoon; O'Neill, Brian E.

2015-01-01

Non-lethal hyperthermia is used clinically as adjuvant treatment to radiation, with mixed results. Denaturation of protein during hyperthermia treatment is expected to synergize with radiation damage to cause cell cycle arrest and apoptosis. Alternatively, hyperthermia is known to cause tissue level changes in blood flow, increasing the oxygenation and radiosensitivity of often hypoxic tumors. In this study, we elucidate a third possibility, that hyperthermia alters cellular adhesion and mechanotransduction, with particular impact on the cancer stem cell population. We demonstrate that cell heating results in a robust but temporary loss of cancer cell aggressiveness and metastatic potential in mouse models. In vitro, this heating results in a temporary loss in cell mobility, adhesion, and proliferation. Our hypothesis is that the loss of cellular adhesion results in suppression of cancer stem cells and loss of tumor virulence and metastatic potential. Our study suggests that the metastatic potential of cancer is particularly reduced by the effects of heat on cellular adhesion and mechanotransduction. If true, this could help explain both the successes and failures of clinical hyperthermia, and suggest ways to target treatments to those who would most benefit. - Highlights: • Non-lethal hyperthermia treatment of cancer cells is shown to cause a reduction in rates of tumor initiation and metastasis. • Dynamic imaging of cells during heat treatment shows temporary changes in cell shape, cell migration, and cell proliferation. • Loss of adhesion may lead to the observed effect, which may disproportionately impact the tumor initiating cell fraction. • Loss or suppression of the tumor initiating cell fraction results in the observed loss of metastatic potential in vivo. • This result may lead to new approaches to synergizing hyperthermia with surgery, radiation, and chemotherapy

Non-lethal heat treatment of cells results in reduction of tumor initiation and metastatic potential

Energy Technology Data Exchange (ETDEWEB)

Kim, Yoo-Shin; Lee, Tae Hoon; O' Neill, Brian E., E-mail: BEOneill@houstonmethodist.org

2015-08-14

Non-lethal hyperthermia is used clinically as adjuvant treatment to radiation, with mixed results. Denaturation of protein during hyperthermia treatment is expected to synergize with radiation damage to cause cell cycle arrest and apoptosis. Alternatively, hyperthermia is known to cause tissue level changes in blood flow, increasing the oxygenation and radiosensitivity of often hypoxic tumors. In this study, we elucidate a third possibility, that hyperthermia alters cellular adhesion and mechanotransduction, with particular impact on the cancer stem cell population. We demonstrate that cell heating results in a robust but temporary loss of cancer cell aggressiveness and metastatic potential in mouse models. In vitro, this heating results in a temporary loss in cell mobility, adhesion, and proliferation. Our hypothesis is that the loss of cellular adhesion results in suppression of cancer stem cells and loss of tumor virulence and metastatic potential. Our study suggests that the metastatic potential of cancer is particularly reduced by the effects of heat on cellular adhesion and mechanotransduction. If true, this could help explain both the successes and failures of clinical hyperthermia, and suggest ways to target treatments to those who would most benefit. - Highlights: • Non-lethal hyperthermia treatment of cancer cells is shown to cause a reduction in rates of tumor initiation and metastasis. • Dynamic imaging of cells during heat treatment shows temporary changes in cell shape, cell migration, and cell proliferation. • Loss of adhesion may lead to the observed effect, which may disproportionately impact the tumor initiating cell fraction. • Loss or suppression of the tumor initiating cell fraction results in the observed loss of metastatic potential in vivo. • This result may lead to new approaches to synergizing hyperthermia with surgery, radiation, and chemotherapy.

Effect of heat treatment on friction and wear behavior of al-6061 composite reinforced with 10% submicron Al2O3 particles

International Nuclear Information System (INIS)

AlQutub, Amro M

2009-01-01

The present research aims at investigating experimentally the effect of heat treatment on the hardness, wear behavior, and friction properties of 6061 Al composite reinforced with sub-micron Al2O3 (10% vol.) produced by powder metallurgy. Heat treatment of the as-received composite starts by the solution treatment at a temperature of 550 degree C for a period of two hours followed by quenching in chilled water and then age hardening at 175 degree C for different periods. It is illustrated that heat treatment has relatively small effect on the hardness of the composite. This can be attributed to the large interface areas between the matrix and the sub-micron alumina in the composite, which reduces the whole concentration of vacancies in the matrix. The result is reduced efficiency of age hardening. For this reason, wear and friction tests were limited to the heat treated composite with four hours aging only. A pin-on-disc tribometer was used to conduct wear and friction tests against AISI 4140 at room temperature for both as-received composite and heat treated composite (with four hours of aging) for comparison. Wear tests indicate that heat treatment has the advantage of increasing transition load to severe wear by 30% compared to as-received composite. On the other hand, at high loads heat treatment results in larger delaminated flakes on the worn surface, indicating reduced fracture toughness. This, in turn, resulted in higher wear rates compared to the as-received composite. Dry friction coefficient is practically unaffected by the heat treatment. (author)

Preparation, heat treatment, and mechanical properties of the uranium-5 weight percent chromium eutectic alloy

International Nuclear Information System (INIS)

Townsend, A.B.

1980-10-01

The eutectic alloy of uranium-5 wt % chromium (U-5Cr) was prepared from high-purity materials and cast into 1-in.-thick ingots. This material was given several simple heat treatments, the mechanical properties of these heat-treated samples were determined; and the microstructure was examined. Some data on the melting point and transformation temperatures were obtained

Heat inactivation of wine spoilage yeast Dekkera bruxellensis by hot water treatment.

Science.gov (United States)

Fabrizio, V; Vigentini, I; Parisi, N; Picozzi, C; Compagno, C; Foschino, R

2015-08-01

Cell suspensions of four Dekkera bruxellensis strains (CBS 2499, CBS 2797, CBS 4459 and CBS 4601) were subjected to heat treatment in deionized water at four different temperatures (55·0, 57·5, 60·0 and 62·5°C) to investigate their thermal resistance. The decimal reduction times at a specific temperature were calculated from the resulting inactivation curves: the D-values at 55·0°C ranged from 63 to 79·4 s, at 57·5°C from 39·6 to 46·1 s, at 60·0°C from 19·5 to 20·7 s, at 62·5°C from 10·2 to 13·7 s. The z-values were between 9·2 and 10·2°C, confirming that heat resistance is a strain-dependent character. A protocol for the sanitization of 225 l casks by immersion in hot water was set up and applied to contaminated 3-year-old barrels. The heat penetration through the staves was evaluated for each investigated temperature by positioning a thermal probe at 8 mm deep. A treatment at 60°C for an exposure time of 19 min allowed to eliminate the yeast populations up to a log count reduction of 8. Brettanomyces/Dekkera bruxellensis is the main yeast involved in red wine spoilage that occurs during ageing in barrel, generating considerable economic losses. Current sanitization protocols, performed using different chemicals, are ineffective due to the porous nature of the wood. The thermal inactivation of D. bruxellensis cells by hot water treatment proves to be efficacious and easy to perform, provided that the holding time at the killing temperature takes into account the filling time of the vessel and the time for the heat penetration into the wood structure. © 2015 The Society for Applied Microbiology.

Heat treatment effect on the mechanical properties of industrial drawn copper wires

International Nuclear Information System (INIS)

Beribeche, Abdellatif; Boumerzoug, Zakaria; Ji, Vincent

2013-01-01

In this present investigation, the mechanical properties of industrial drawn copper wires have been studied by tensile tests. The effect of prior heat treatments at 500°C on the drawn wires behavior was the main goal of this investigation. We have found that the mechanical behavior of drawn wires depends strongly on those treatments. SEM observations of the wire cross section after tensile tests have shown that the mechanism of rupture was mainly controlled by the void formation

Effect of heat treatment on the structural and optical properties of tellurite glasses doped erbium

Energy Technology Data Exchange (ETDEWEB)

Jlassi, I., E-mail: ifa.jlassi@fst.rnu.tn [Laboratoire de Physico-Chimie des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95 Hammam-Lif 2050 (Tunisia); Elhouichet, H. [Laboratoire de Physico-Chimie des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95 Hammam-Lif 2050 (Tunisia); Departement de Physique, Faculte des Sciences de Tunis, Campus ElManar 2092 (Tunisia); Hraiech, S.; Ferid, M. [Laboratoire de Physico-Chimie des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95 Hammam-Lif 2050 (Tunisia)

2012-03-15

The 75TeO{sub 2}-20ZnO-4Na{sub 2}CO{sub 3}-1Er{sub 2}O{sub 3} (in molar ratio) glass system was prepared by the conventional melt-quenching method. As such, the samples prepared were investigated by differential scanning calorimetry (DSC), X-ray diffractrometry (XRD), Raman spectroscopy and infrared luminescence. DSC analyses were carried out on our glass at different heating rates between 5 and 20 Degree-Sign C/min. The result of the annealing temperature on the spectroscopic properties of Er{sup 3+} in tellurite glasses was discussed. The activation energy, for surface crystallization, was determined graphically from a Kissinger-type plot and had a value about 897.2 kJ/mol. Crystalline phases for both {alpha}-TeO{sub 2}, {gamma}-TeO{sub 2} and Zn{sub 2}Te{sub 3}O{sub 8} system were determined by the XRD method and were confirmed by Raman spectroscopy characterizations after heat treatment. The effect of heat treatment on absorption spectra and luminescence properties in the tellurite glass was also investigated. With heat treatment, the ultraviolet absorption edge presented a redshift. As a result, the Judd-Ofelt (J-O) intensity parameters ({Omega}{sub 2}, {Omega}{sub 4}, {Omega}{sub 6}) were determined. The spontaneous emission probabilities of some relevant transitions, the branching ratio and the radiative lifetimes of several excited states of Er{sup 3+} were predicted using intensity J-O parameters. The near infrared emission that corresponds to Er{sup 3+}: {sup 4}I{sub 13/2}{yields}{sup 4}I{sub 15/2} can be significantly enhanced after heat treatment. Notably, it is found that the luminescence lifetime in the present system is much longer than that in most other glasses and glass ceramics. A comparative study on luminescence performance suggests that the obtained glass ceramic is a promising material for Er{sup 3+} doped fiber amplifiers. - Highlights: Black-Right-Pointing-Pointer Tellurite glasses were prepared by conventional melt-quenching method. Black

Application of heat treatment and hot extrusion processes to improve mechanical properties of the AZ91 alloy

Directory of Open Access Journals (Sweden)

T. Reguła

2010-04-01

Full Text Available The main aim of this paper is to evaluate the effects of hot working (extrusion and hest treatment on room temperature mechanical properties of magnesium-based AZ91 alloy. The results were compared with as-cast condition. The examined material had been obtained by gravity casting to permanent moulds and subsequently subjected to heat treatment and/or processed by extrusion at 648 K. Microstructural and mechanical properties of properly prepared specimens were studied. Rm, Rp02 and A5 were determined from tensile tests. Brinell hardness tests were also conducted. The research has shown that hot working of AZ91 alloy provides high mechanical properties unattainable by cast material subjected to heat-treatment. The investigated alloy subjected to hot working and subsequently heat-treated has doubled its strength and considerably improved the elongation - compared with the as-cast material.

Modernization and efficiency of heat treatment and heating up plants; Modernisierung und Effizienz von Thermoprozessanlagen

Energy Technology Data Exchange (ETDEWEB)

Wendt, Peter [LOI Thermprocess GmbH, Essen (Germany); Kuehn, Friedhelm [Ingenieurbuero fuer Waermebehandlung, Industrieoefen und Energieberatung, Muelheim (Germany)

2010-10-15

A goal of this contribution is to show, using examples of the thermal heat treatment industry and the thermal processing units used there (Beltype plants, routary hearth, walking hearth, walking beam, pusher type furnaces and gas carburizing plants as well as case hardening plants), which increases in efficiency within and outside of the actual thermal treatment process and the necessary thermal processing units for the order are available today. From the possibilities of the reduction of energy employment resulting from that, a high potential for the discharge of the environment can be derived. The economic effect concerning energy employment and saving possibilities will also be considered. Concluding, examples of case-hardening show which variants of a change of process present themselves partially in the future, in order to achieve substantial production increases and thus energy cost reductions. (orig.)

Preliminary study concerning the influence of combined heat and radiation treatment on the quality of some horticultural products

International Nuclear Information System (INIS)

Langerak, D.Is.; Bruurs, M.F.J.

1973-01-01

In collaboration with a canning factory a number of horticultural products were preserved by means of the combined irradiation and heating treatment. The aim was to study the influence of the parameters irradiation and heat on quality and microbiological spoilage. The products were exposed to gamma-rays with doses varying from 0 to 1 Mrad. The heat treatment varied from 5 to 40 minutes at 98 to 121 0 C; time and temperature depended on the type of product. The sterilization value (F value) was measured by means of the method of Esty and Meyer for products with pH>5. The canned products were stored afterwards at 20-55 0 C. The organoleptic test showed that the colour and texture of most products were improved by the combined treatment, provided the irradiation dose did not exceed 0.25 Mrad. Strawberries in syrup discoloured at 0.1 Mrad. For a number of products the improved colour was partially lost during storage. Flavour and taste were not generally influenced unfavourably at doses up to 0.3 Mrad (exception: strawberries). The treatment sequence did not affect distinctly the quality or microbiological spoilage. The sterilization time (F value) of the combined treatment was determined by the shortest heating period required for the tenderness of the product. (F.J.)

Intermittent cryogen spray cooling for optimal heat extraction during dermatologic laser treatment

Science.gov (United States)

Majaron, Boris; Svaasand, Lars O.; Aguilar, Guillermo; Nelson, J. Stuart

2002-09-01

Fast heat extraction is critically important to obtain the maximal benefit of cryogen spray cooling (CSC) during laser therapy of shallow skin lesions, such as port wine stain birthmarks. However, a film of liquid cryogen can build up on the skin surface, impairing heat transfer due to the relatively low thermal conductivity and higher temperature of the film as compared to the impinging spray droplets. In an attempt to optimize the cryogen mass flux, while minimally affecting other spray characteristics, we apply a series of 10 ms spurts with variable duty cycles. Heat extraction dynamics during such intermittent cryogen sprays were measured using a custom-made metal-disc detector. The highest cooling rates were observed at moderate duty cycle levels. This confirms the presence, and offers a practical way to eliminate the adverse effect of liquid cryogen build-up on the sprayed surface. On the other hand, lower duty cycles allow a substantial reduction in the average rate of heat extraction, enabling less aggressive and more efficient CSC for treatment of deeper targets, such as hair follicles.

Dual Microstructure Heat Treatment of a Nickel-Base Disk Alloy Assessed

Science.gov (United States)

Gayda, John

2002-01-01

Gas turbine engines for future subsonic aircraft will require nickel-base disk alloys that can be used at temperatures in excess of 1300 F. Smaller turbine engines, with higher rotational speeds, also require disk alloys with high strength. To address these challenges, NASA funded a series of disk programs in the 1990's. Under these initiatives, Honeywell and Allison focused their attention on Alloy 10, a high-strength, nickel-base disk alloy developed by Honeywell for application in the small turbine engines used in regional jet aircraft. Since tensile, creep, and fatigue properties are strongly influenced by alloy grain size, the effect of heat treatment on grain size and the attendant properties were studied in detail. It was observed that a fine grain microstructure offered the best tensile and fatigue properties, whereas a coarse grain microstructure offered the best creep resistance at high temperatures. Therefore, a disk with a dual microstructure, consisting of a fine-grained bore and a coarse-grained rim, should have a high potential for optimal performance. Under NASA's Ultra-Safe Propulsion Project and Ultra-Efficient Engine Technology (UEET) Program, a disk program was initiated at the NASA Glenn Research Center to assess the feasibility of using Alloy 10 to produce a dual-microstructure disk. The objectives of this program were twofold. First, existing dual-microstructure heat treatment (DMHT) technology would be applied and refined as necessary for Alloy 10 to yield the desired grain structure in full-scale forgings appropriate for use in regional gas turbine engines. Second, key mechanical properties from the bore and rim of a DMHT Alloy 10 disk would be measured and compared with conventional heat treatments to assess the benefits of DMHT technology. At Wyman Gordon and Honeywell, an active-cooling DMHT process was used to convert four full-scale Alloy 10 disks to a dual-grain microstructure. The resulting microstructures are illustrated in the

Surface Observation and Pore Size Analyses of Polypropylene/Low-Melting Point Polyester Filter Materials: Influences of Heat Treatment

Directory of Open Access Journals (Sweden)

Lin Jia-Horng

2016-01-01

Full Text Available This study proposes making filter materials with polypropylene (PP and low-melting point (LPET fibers. The influences of temperatures and times of heat treatment on the morphology of thermal bonding points and average pore size of the PP/LPET filter materials. The test results indicate that the morphology of thermal bonding points is highly correlated with the average pore size. When the temperature of heat treatment is increased, the fibers are joined first with the thermal bonding points, and then with the large thermal bonding areas, thereby decreasing the average pore size of the PP/LPET filter materials. A heat treatment of 110 °C for 60 seconds can decrease the pore size from 39.6 μm to 12.0 μm.

Effect of high temperature heat treatments on the quality factor of a large-grain superconducting radio-frequency niobium cavity

Directory of Open Access Journals (Sweden)

P. Dhakal

2013-04-01

Full Text Available Large-grain Nb has become a viable alternative to fine-grain Nb for the fabrication of superconducting radio-frequency cavities. In this contribution we report the results from a heat treatment study of a large-grain 1.5 GHz single-cell cavity made of “medium purity” Nb. The baseline surface preparation prior to heat treatment consisted of standard buffered chemical polishing. The heat treatment in the range 800–1400°C was done in a newly designed vacuum induction furnace. Q_{0} values of the order of 2×10^{10} at 2.0 K and peak surface magnetic field (B_{p} of 90 mT were achieved reproducibly. A Q_{0} value of (5±1×10^{10} at 2.0 K and B_{p}=90  mT was obtained after heat treatment at 1400°C. This is the highest value ever reported at this temperature, frequency, and field. Samples heat treated with the cavity at 1400°C were analyzed by secondary ion mass spectrometry, x-ray photoelectron spectroscopy, energy dispersive x ray, point-contact tunneling, and x-ray diffraction, and revealed a complex surface composition which includes titanium oxide, increased carbon, and nitrogen content but reduced hydrogen concentration compared to a non-heat-treated sample.

Effect of high temperature heat treatments on the quality factor of a large-grain superconducting radio-frequency niobium cavity

Energy Technology Data Exchange (ETDEWEB)

Dhakal, P.; Ciovati, G.; Myneni, G. R.; Gray, K. E.; Groll, N.; Maheshwari, P.; McRae, D. M.; Pike, R.; Proslier, T.; Stevie, F.; Walsh, R. P.; Yang, Q.; Zasadzinzki, J.

2013-04-01

Large-grain Nb has become a viable alternative to fine-grain Nb for the fabrication of superconducting radio-frequency cavities. In this contribution we report the results from a heat treatment study of a large-grain 1.5 GHz single-cell cavity made of “medium purity” Nb. The baseline surface preparation prior to heat treatment consisted of standard buffered chemical polishing. The heat treatment in the range 800–1400°C was done in a newly designed vacuum induction furnace. Q{sub 0} values of the order of 2×10{sup 10} at 2.0 K and peak surface magnetic field (B{sub p}) of 90 mT were achieved reproducibly. A Q{sub 0} value of (5±1)×10{sup 10} at 2.0 K and B{sub p}=90mT was obtained after heat treatment at 1400°C. This is the highest value ever reported at this temperature, frequency, and field. Samples heat treated with the cavity at 1400°C were analyzed by secondary ion mass spectrometry, x-ray photoelectron spectroscopy, energy dispersive x ray, point-contact tunneling, and x-ray diffraction, and revealed a complex surface composition which includes titanium oxide, increased carbon, and nitrogen content but reduced hydrogen concentration compared to a non-heat-treated sample.

Influence of heat treatments on the microstructure and tensile behaviour of selective laser melting-produced TI-6AL-4V parts

Directory of Open Access Journals (Sweden)

Ter Haar, Gerrit Matthys

2016-11-01

Full Text Available In industry, post-process heat treatments of Ti-6Al-4V are performed with the aim of improving its tensile behaviour. While heat treatments of wrought Ti6Al4V have been standardised (e.g., Aerospace Material Specification H-81200, heat treatments of selective laser melting (SLM-produced Ti-6Al-4V lacks research and understanding. Significant concern exists about SLM Ti6-Al-4V’s achievable ductility attributed to its martensitic (α’ phase. In this research, heat treatments at a range of temperatures are applied to SLM-produced Ti-6Al-4V tensile samples. Microstructural analysis (both optically and through electron backscatter diffraction was used to identify links between heat treatments and microstructure. Subsequently, uniaxial tensile tests were performed to determine the respective tensile properties of all samples. Correlations in the data show a significant loss in strength with respect to an increase in annealing temperature due to grain growth, while no noticeable trend was observed for fracture strain with regard to annealing temperatures.

Influence of heat treatment on the strength and fracture toughness of 7N01 aluminum alloy

Energy Technology Data Exchange (ETDEWEB)

Li, Bo [School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, 610031, Sichuan (China); Wang, Xiaomin, E-mail: xmwang991011@163.com [School of Life Science and Engineering, Southwest Jiaotong University, Chengdu, 610031, Sichuan (China); Chen, Hui; Hu, Jie [School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, 610031, Sichuan (China); Huang, Cui [School of Life Science and Engineering, Southwest Jiaotong University, Chengdu, 610031, Sichuan (China); Gou, Guoqing [School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, 610031, Sichuan (China)

2016-09-05

7N01 aluminum (Al) alloys are treated by five heat treatment methods as peak aging (T6), over aging (T74), high temperature and subsequently low temperature aging (HLA), retrogression and reaging (RRA) and double retrogression and reaging (DRRA). The strength and fracture toughness of the five samples are tested, and the microstructures are investigated by optical microscopy (OM), transmission electron microscopy (TEM), and scanning electron microscopy (SEM). The results show that 7N01 Al-alloy treated at T6 condition has high strength but low fracture toughness. Compared with T6 treatment, T74 and HLA treatments increase the fracture toughness by 67% and 90% respectively, while the strength decrease by 9% and 17%. RRA process is a proper treatment method for 7N01 which improves the fracture toughness without sacrificing strength. The fracture toughness of DRRA treated alloy is much lower than that of RRA. Quantitative analysis through TEM images shows that the heat treatment affects the mechanical properties of 7N01 Al-alloy highly through changing the precipitates in grains and on grain boundaries, which can be explained by the coherency strengthening mechanism and Orowan mechanism. - Highlights: • Five heat treatments which can change the properties of 7N01 Al alloy were designed. • Quantitative analysis of precipitates was employed to study the mechanism. • RRA treatment can make proper strength/toughness property balances for 7N01 Al alloy.

Influence of heat treatment on the strength and fracture toughness of 7N01 aluminum alloy

International Nuclear Information System (INIS)

Li, Bo; Wang, Xiaomin; Chen, Hui; Hu, Jie; Huang, Cui; Gou, Guoqing

2016-01-01

7N01 aluminum (Al) alloys are treated by five heat treatment methods as peak aging (T6), over aging (T74), high temperature and subsequently low temperature aging (HLA), retrogression and reaging (RRA) and double retrogression and reaging (DRRA). The strength and fracture toughness of the five samples are tested, and the microstructures are investigated by optical microscopy (OM), transmission electron microscopy (TEM), and scanning electron microscopy (SEM). The results show that 7N01 Al-alloy treated at T6 condition has high strength but low fracture toughness. Compared with T6 treatment, T74 and HLA treatments increase the fracture toughness by 67% and 90% respectively, while the strength decrease by 9% and 17%. RRA process is a proper treatment method for 7N01 which improves the fracture toughness without sacrificing strength. The fracture toughness of DRRA treated alloy is much lower than that of RRA. Quantitative analysis through TEM images shows that the heat treatment affects the mechanical properties of 7N01 Al-alloy highly through changing the precipitates in grains and on grain boundaries, which can be explained by the coherency strengthening mechanism and Orowan mechanism. - Highlights: • Five heat treatments which can change the properties of 7N01 Al alloy were designed. • Quantitative analysis of precipitates was employed to study the mechanism. • RRA treatment can make proper strength/toughness property balances for 7N01 Al alloy.

Effects of heat-moisture treatment reaction conditions on the physicochemical and structural properties of maize starch: moisture and length of heating.

Science.gov (United States)

Sui, Zhongquan; Yao, Tianming; Zhao, Yue; Ye, Xiaoting; Kong, Xiangli; Ai, Lianzhong

2015-04-15

Changes in the properties of normal maize starch (NMS) and waxy maize starch (WMS) after heat-moisture treatment (HMT) under various reaction conditions were investigated. NMS and WMS were adjusted to moisture levels of 20%, 25% and 30% and heated at 100 °C for 2, 4, 8 and 16 h. The results showed that moisture content was the most important factor in determining pasting properties for NMS, whereas the heating length was more important for WMS. Swelling power decreased in NMS but increased in WMS, and while the solubility index decreased for both samples, the changes were largely determined by moisture content. The gelatinisation temperatures of both samples increased with increasing moisture content but remained unchanged with increasing heating length. The Fourier transform infrared (FT-IR) absorbance ratio was affected to different extents by the moisture levels but remained constant with increasing the heating length. The X-ray intensities increased but relative crystallinity decreased to a greater extent with increasing moisture content. This study showed that the levels of moisture content and length of heating had significant impacts on the structural and physicochemical properties of normal and waxy maize starches but to different extents. Copyright © 2014 Elsevier Ltd. All rights reserved.

Influence of dimethyl dicarbonate on the resistance of Escherichia coli to a combined UV-Heat treatment in apple juice

Science.gov (United States)

Gouma, Maria; Gayán, Elisa; Raso, Javier; Condón, Santiago; Álvarez, Ignacio

2015-01-01

Commercial apple juice inoculated with Escherichia coli was treated with UV-C, heat (55°C) and dimethyl dicarbonate – DMDC (25, 50, and 75 mg/L)-, applied separately and in combination, in order to investigate the possibility of synergistic lethal effects. The inactivation levels resulting from each treatment applied individually for a maximum treatment time of 3.58 min were limited, reaching 1.2, 2.9, and 0.06 log10 reductions for UV, heat, and DMDC (75 mg/L), respectively. However, all the investigated combinations resulted in a synergistic lethal effect, reducing the total treatment time and UV dose, with the synergistic lethal effect being higher when larger concentrations of DMDC were added to the apple juice. The addition of 75 mg/L of DMDC prior to the combined UV-C light treatment at 55°C resulted in 5 log10 reductions after only 1.8 min, reducing the treatment time and UV dose of the combined UV-Heat treatment by 44%. PMID:26042117

Effect of the Heat Treatment on the Mechanical Property and Corrosion Resistance of CU - 7Al - 2.5Si Alloy

Energy Technology Data Exchange (ETDEWEB)

Lee, Syung-Yul; Won, Jong-Pil; Park, Dong-Hyun; Moon, Kyung-Man; Lee, Myeong-Hoon; Jeong, Jin-A [Korea Maritime and Ocean Univ., Busan (Korea, Republic of); Baek, Tae-Sil [Pohang College, Pohang (Korea, Republic of)

2014-02-15

Recently, the fuel oil of diesel engines of marine ships has been increasingly changed to heavy oil of low quality as the oil price is getting higher and higher. Therefore, the spiral gear attached at the motor of the oil purifier which plays an important role to purify the heavy oil is also easy to expose at severe environmental condition due to the purification of the heavy oil in higher temperature. Thus, the material of the spiral gear requires a better mechanical strength, wear and corrosion resistance. In this study, the heat treatment(tempering) with various holding time at temperature of 500 .deg. C was carried out to the alloy of Cu-7Al-2.5Si as centrifugal casting, and the properties of both hardness and corrosion resistance with and without heat treatment were investigated with observation of the microstructure and with electrochemical methods, such as measurement of corrosion potential, cathodic and anodic polarization curves, cyclic voltammogram, and a.c. impedance. in natural seawater solution. The α, β and γ{sub 2} phases were observed in the material in spite of no heat treatment due to quenching effect of a spin mold. However, their phases, that is, β and γ{sub 2} phases decreased gradually with increasing the holding time at a constant temperature of 500 .deg. C. The hardness more or less decreased with heat treatment, however its corrosion resistance was improved with the heat treatment. Furthermore, the longer holding time, the better corrosion resistance. In addition, when the holding time was 48hrs, its corrosion current density showed the lowest value. The pattern of corroded surface was nearly similar to that of the pitting corrosion, and this morphology was greatly observed in the case of no heat treatment. It is considered that γ{sub 2} phase at the grain boundary was corroded preferentially as an anode. However, the pattern of general corrosion exhibited increasingly due to decreasing the γ{sub 2} phase with heat treatment

Optimization of heat treatment parameters for additive manufacturing and gravity casting AlSi10Mg alloy

Science.gov (United States)

Girelli, L.; Tocci, M.; Montesano, L.; Gelfi, M.; Pola, A.

2017-11-01

Additive manufacturing of metals is a production process developed in the last few years to realize net shape components with complex geometry and high performance. AlSi10Mg is one of the most widely used aluminium alloys, both in this field and in conventional foundry processes, for its significant mechanical properties combined with good corrosion resistance. In this paper the effect of heat treatment on AlSi10Mg alloy was investigated. Solution and ageing treatments were carried out with different temperatures and times on samples obtained by direct metal laser sintering and gravity casting in order to compare their performance. Microstructural analyses and hardness tests were performed to investigate the effectiveness of the heat treatment. The results were correlated to the sample microstructure and porosity, analysed by means of optical microscopy and density measurements. It was found that, in the additive manufactured samples, the heat treatment can reduce significantly the performance of the alloy also because of the increase of porosity due to entrapped gas during the deposition technique and that the higher the solution temperature the higher the increase of such defects. A so remarkable effect was not found in the conventional cast alloy.

Effect of heat treatment and shelf life on chilling injury of mango cv. Nam Dok Mai

Directory of Open Access Journals (Sweden)

Apiradee Muangdech

2017-10-01

Full Text Available This study was aimed to investigate the effect of heat treatment and shelf life on chilling injury of mango cv.Nam Dok Mai.The heat treatment of mango pulp during storage were determined by hot air oven set at 34 and 38°C for three intervals, as 24, 48, and 72 hours, then they were subsequently stored at 5°C for 10, 20, and 30 days to determine the appropriate shelf life. The findings showed that the symptom of mango fruit after chilling injury appeared within the 30th day of storage at 5°C. Several symptoms of mango fruit after chilling injury treatment were observed, i.e., pitting, browning on the skin, water soaking, and rapid rotting of the fruits that resulted in shorter shelf life. It was found that chilling injury mangoes had lower level of total soluble solid, higher disease incidence, and lower quality of fruit when compared with normal ripe-mango fruits at 25°C. Mango fruits treated at 34°C for either 24 or 48 hours, and at 38°C for 24 hours prior to cold storage at 5°C for 10 and 20 days showed a significant reduction in the chilling injury (CI index when compared to that of non-heated fruits. On the other hand, the heat treatment did not affect fruit weight loss, firmness, color changes, and water soaking at 5°C.