  1. Metallurgy of zirconium and hafnium

    International Nuclear Information System (INIS)

    Baryshnikov, N.V.; Geger, V.Eh.; Denisova, N.D.; Kazajn, A.A.; Kozhemyakin, V.A.; Nekhamkin, L.G.; Rodyakin, V.V.; Tsylov, Yu.A.

    1979-01-01

    Considered are those properties of zirconium and of hafnium, which are of practical interest for the manufacture of these elements. Systematized are the theoretical and the practical data on the procedures for thermal decomposition of zirconia and for obtaining zirconium dioxide and hafnium dioxide by a thermal decomposition of compounds and on the hydrometallurgical methods for extracting zirconium and hafnium. Zirconium and hafnium fluorides and chlorides production procedures are described. Considered are the iodide and the electrolytic methods of refining zirconium and hafnium

  2. SEPARATING HAFNIUM FROM ZIRCONIUM

    Science.gov (United States)

    Lister, B.A.J.; Duncan, J.F.

    1956-08-21

    A dilute aqueous solution of zirconyl chloride which is 1N to 2N in HCl is passed through a column of a cation exchange resin in acid form thereby absorbing both zirconium and associated hafnium impurity in the mesin. The cation exchange material with the absorbate is then eluted with aqueous sulfuric acid of a O.8N to 1.2N strength. The first portion of the eluate contains the zirconium substantially free of hafnium.

  3. Commercial production of metal hafnium and hafnium-based products

    International Nuclear Information System (INIS)

    Negodin, D.A.; Shtutsa, M.G.; Akhtonov, S.G.; Il'enko, E.V.; Kobyzev, A.M.

    2012-01-01

    Hafnium possesses a unique complex of physical and chemical properties which allow the application of products on its basis in various industries. Joint Stock Company 'Chepetsky Mechanical Plant' is the single enterprise which produces hafnium on the territory of Russia. The manufacture of metal hafnium with the total content of zirconium and hafnium, at least, 99,8 % of weights is developed at the present time at Joint Stock Company CHMZ. The weight of melted hafnium ingots is up to 1 ton. Manufacture of wide range of products from hafnium is implemented. The plates from a hafnium with thickness of 0.60 mm which are used for emergency control cartridges of VVER-440 reactors are the most critical product. It is shown that ingots and products obtained from metal hafnium correspond to the Russian and international standards for reactor materials in chemical composition, mechanical and corrosion properties.

  4. Zirconium and hafnium

    Science.gov (United States)

    Jones, James V.; Piatak, Nadine M.; Bedinger, George M.; Schulz, Klaus J.; DeYoung,, John H.; Seal, Robert R.; Bradley, Dwight C.

    2017-12-19

    Zirconium and hafnium are corrosion-resistant metals that are widely used in the chemical and nuclear industries. Most zirconium is consumed in the form of the main ore mineral zircon (ZrSiO4, or as zirconium oxide or other zirconium chemicals. Zirconium and hafnium are both refractory lithophile elements that have nearly identical charge, ionic radii, and ionic potentials. As a result, their geochemical behavior is generally similar. Both elements are classified as incompatible because they have physical and crystallochemical properties that exclude them from the crystal lattices of most rock-forming minerals. Zircon and another, less common, ore mineral, baddeleyite (ZrO2), form primarily as accessory minerals in igneous rocks. The presence and abundance of these ore minerals in igneous rocks are largely controlled by the element concentrations in the magma source and by the processes of melt generation and evolution. The world’s largest primary deposits of zirconium and hafnium are associated with alkaline igneous rocks, and, in one locality on the Kola Peninsula of Murmanskaya Oblast, Russia, baddeleyite is recovered as a byproduct of apatite and magnetite mining. Otherwise, there are few primary igneous deposits of zirconium- and hafnium-bearing minerals with economic value at present. The main ore deposits worldwide are heavy-mineral sands produced by the weathering and erosion of preexisting rocks and the concentration of zircon and other economically important heavy minerals, such as ilmenite and rutile (for titanium), chromite (for chromium), and monazite (for rare-earth elements) in sedimentary systems, particularly in coastal environments. In coastal deposits, heavy-mineral enrichment occurs where sediment is repeatedly reworked by wind, waves, currents, and tidal processes. The resulting heavy-mineral-sand deposits, called placers or paleoplacers, preferentially form at relatively low latitudes on passive continental margins and supply 100 percent of

  5. SEPARATION OF HAFNIUM FROM ZIRCONIUM

    Science.gov (United States)

    Overholser, L.B.; Barton, C.J. Sr.; Ramsey, J.W.

    1960-05-31

    The separation of hafnium impurities from zirconium can be accomplished by means of organic solvent extraction. The hafnium-containing zirconium feed material is dissolved in an aqueous chloride solution and the resulting solution is contacted with an organic hexone phase, with at least one of the phases containing thiocyanate. The hafnium is extracted into the organic phase while zirconium remains in the aqueous phase. Further recovery of zirconium is effected by stripping the onganic phase with a hydrochloric acid solution and commingling the resulting strip solution with the aqueous feed solution. Hexone is recovered and recycled by means of scrubbing the onganic phase with a sulfuric acid solution to remove the hafnium, and thiocyanate is recovered and recycled by means of neutralizing the effluent streams to obtain ammonium thiocyanate.

  6. Calorimetric measurements on hafnium titanate

    International Nuclear Information System (INIS)

    Kandan, R.; Prabhakara Reddy, B.; Panneerselvam, G.; Nagarajan, K.

    2012-01-01

    Owing to its desirable nuclear and mechanical properties such as good absorption cross-section for thermal neutrons (105 barns), hafnium titanate (HfTiO 4 ) finds application as control rods for nuclear reactors. An accurate knowledge of the thermo physical properties of this material is necessary for design of control rod and for modeling its performance. Heat capacity is an important thermodynamic property that determines the temperature dependent variation of all other thermodynamic properties. Hence enthalpy increments of hafnium titanate (HfTiO 4 ) were measured in the temperature range 803-1663 K by employing the method of inverse drop calorimetry using high temperature differential calorimeter

  7. Hafnium carbide formation in oxygen deficient hafnium oxide thin films

    Energy Technology Data Exchange (ETDEWEB)

    Rodenbücher, C. [Forschungszentrum Jülich GmbH, Peter Grünberg Institute (PGI-7), JARA-FIT, 52425 Jülich (Germany); Hildebrandt, E.; Sharath, S. U.; Kurian, J.; Komissinskiy, P.; Alff, L. [Technische Universität Darmstadt, Institute of Materials Science, 64287 Darmstadt (Germany); Szot, K. [Forschungszentrum Jülich GmbH, Peter Grünberg Institute (PGI-7), JARA-FIT, 52425 Jülich (Germany); University of Silesia, A. Chełkowski Institute of Physics, 40-007 Katowice (Poland); Breuer, U. [Forschungszentrum Jülich GmbH, Central Institute for Engineering, Electronics and Analytics (ZEA-3), 52425 Jülich (Germany); Waser, R. [Forschungszentrum Jülich GmbH, Peter Grünberg Institute (PGI-7), JARA-FIT, 52425 Jülich (Germany); RWTH Aachen, Institute of Electronic Materials (IWE 2), 52056 Aachen (Germany)

    2016-06-20

    On highly oxygen deficient thin films of hafnium oxide (hafnia, HfO{sub 2−x}) contaminated with adsorbates of carbon oxides, the formation of hafnium carbide (HfC{sub x}) at the surface during vacuum annealing at temperatures as low as 600 °C is reported. Using X-ray photoelectron spectroscopy the evolution of the HfC{sub x} surface layer related to a transformation from insulating into metallic state is monitored in situ. In contrast, for fully stoichiometric HfO{sub 2} thin films prepared and measured under identical conditions, the formation of HfC{sub x} was not detectable suggesting that the enhanced adsorption of carbon oxides on oxygen deficient films provides a carbon source for the carbide formation. This shows that a high concentration of oxygen vacancies in carbon contaminated hafnia lowers considerably the formation energy of hafnium carbide. Thus, the presence of a sufficient amount of residual carbon in resistive random access memory devices might lead to a similar carbide formation within the conducting filaments due to Joule heating.

  8. Hafnium isotope stratigraphy of ferromanganese crusts

    Science.gov (United States)

    Lee; Halliday; Hein; Burton; Christensen; Gunther

    1999-08-13

    A Cenozoic record of hafnium isotopic compositions of central Pacific deep water has been obtained from two ferromanganese crusts. The crusts are separated by more than 3000 kilometers but display similar secular variations. Significant fluctuations in hafnium isotopic composition occurred in the Eocene and Oligocene, possibly related to direct advection from the Indian and Atlantic oceans. Hafnium isotopic compositions have remained approximately uniform for the past 20 million years, probably reflecting increased isolation of the central Pacific. The mechanisms responsible for the increase in (87)Sr/(86)Sr in seawater through the Cenozoic apparently had no effect on central Pacific deep-water hafnium.

  9. Ferroelectricity in undoped hafnium oxide

    International Nuclear Information System (INIS)

    Polakowski, Patrick; Müller, Johannes

    2015-01-01

    We report the observation of ferroelectric characteristics in undoped hafnium oxide thin films in a thickness range of 4–20 nm. The undoped films were fabricated using atomic layer deposition (ALD) and embedded into titanium nitride based metal-insulator-metal (MIM) capacitors for electrical evaluation. Structural as well as electrical evidence for the appearance of a ferroelectric phase in pure hafnium oxide was collected with respect to film thickness and thermal budget applied during titanium nitride electrode formation. Using grazing incidence X-Ray diffraction (GIXRD) analysis, we observed an enhanced suppression of the monoclinic phase fraction in favor of an orthorhombic, potentially, ferroelectric phase with decreasing thickness/grain size and for a titanium nitride electrode formation below crystallization temperature. The electrical presence of ferroelectricity was confirmed using polarization measurements. A remanent polarization P r of up to 10 μC cm −2 as well as a read/write endurance of 1.6 × 10 5 cycles was measured for the pure oxide. The experimental results reported here strongly support the intrinsic nature of the ferroelectric phase in hafnium oxide and expand its applicability beyond the doped systems

  10. Study of fine structure of deformed hafnium

    International Nuclear Information System (INIS)

    Voskresenskaya, L.A.; Petukhova, A.S.; Kovalev, K.S.

    1978-01-01

    Variations in the hafnium fine structure following the cold plastic deformation have been studied. The fine structure condition has been studied through the harmonic analysis of the profile of the X-ray diffraction line, obtained at the DRON-I installation. Received has been the dependence of the crystal lattice microdistortions value on the deformation extent for hafnium. This dependence is compared with the corresponding one for zirconium. It is found out that at all the deformations the microdistortion distribution is uniform. The microdistortion value grows with the increase in the compression. During the mechanical impact higher microdistortions of the crystal lattice occur in the hafnium rather than in zirconium

  11. Hafnium - material for chemical apparatus engineering

    International Nuclear Information System (INIS)

    Jennert, D.

    1981-01-01

    This work describes - on the background of available literature - the properties of hafnium in technical quality (DIN-material No. 2.6400) as material for chemical apparatus engineering. The occurence, refining, physical and chemical properties will be described as well as the material behavior. In conclusion, it has been found that there is, at present, sufficient information for the engineering of hafnium which has to be completed by additional investigations for special applications. (orig.) [de

  12. Determination of hafnium by atomic absorption spectrometry

    International Nuclear Information System (INIS)

    Yoshida, Isao; Kobayashi, Hiroshi; Ueno, Keihei.

    1977-01-01

    Optimum conditions for atomic absorption spectrophotometric determination of hafnium were investigated by use of a Jarrel-Ash AA-1 instrument which was equipped with a premixed gas burner slotted 50 mm in length and 0.4 mm in width. Absorption of hafnium, which was atomized in an nitrous oxide-acetylene flame, was measured on a resonance line at 307.29 nm. The absorption due to hafnium was enhanced in the presence of ammonium fluoride and iron(III) ion, as shown in Figs. 2 and 3, depending on their concentration. The highest absorption was attained by the addition of (0.15 -- 0.3)M ammonium fluoride, 0.07 M of iron(III) ion and 0.05 M of hydrochloric acid. An excess of the additives decreased the absorption. The presence of zirconium, which caused a significant interference in the ordinary analytical methods, did not affect the absorption due to hafnium, if the zirconium concentration is less than 0.2 M. A standard procedure was proposed; A sample containing a few mg of hafnium was dissolved in a 25-ml volumetric flask, and ammonium fluoride, ferric nitrate and hydrochloric acid were added so that the final concentrations were 0.3, 0.07 and 0.05 M, respectively. Atomic absorption was measured on the aqueous solution in a nitrous oxide-acetylene flame and the hafnium content was calculated from the absorbance. Sensitivity was as high as 12.5 μg of Hf/ml/l% absorption. The present method is especially recommendable to the direct determination of hafnium in samples containing zirconium. (auth.)

  13. Titanium(IV), zirconium, hafnium and thorium

    International Nuclear Information System (INIS)

    Brown, Paul L.; Ekberg, Christian

    2016-01-01

    Titanium can exist in solution in a number of oxidation states. The titanium(IV) exists in acidic solutions as the oxo-cation, TiO 2+ , rather than Ti 4+ . Zirconium is used in the ceramics industry and in nuclear industry as a cladding material in reactors where its reactivity towards hydrolysis reactions and precipitation of oxides may result in degradation of the cladding. In nature, hafnium is found together with zirconium and as a consequence of the contraction in ionic radii that occurs due to the 4f -electron shell, the ionic radius of hafnium is almost identical to that of zirconium. All isotopes of thorium are radioactive and, as a consequence of it being fertile, thorium is important in the nuclear fuel cycle. The polymeric hydrolysis species that have been reported for thorium are somewhat different to those identified for zirconium and hafnium, although thorium does form the Th 4 (OH) 8 8+ species.

  14. Gravimetric determination of hafnium through its arsenate in carbide and boride of hafnium

    International Nuclear Information System (INIS)

    Rasulbekova, R.A.; Mamedov, I.A.

    1976-01-01

    A gravimetric method of determining hafnium through hydroarsenate has been recommended. The method differs from the known ones by its simplicity and by the recalculation coefficient which is more than by 50% smaller than that used in preparing a weight form of HfO 2 . Upon development of gravimetric determination of hafnium through hydro-and pyroarsenate, an investigation has been conducted with the aim to find some physico-chemical constants of hafnium hydroarsenate. The weighed amount of hafnium hydroarsenate is dissolved in sulphuric acid (2:5). The precipitate of hafnium hydroarsenate has been studied for recording infrared absorption spectra. Thermographic analysis of the precipitate has been performed. Thermogram reveals endothermal effect at 105 deg C and exothermal at 840 deg C. Water solubility of hafnium has been determined equal to 1.75x10 6 g mol/l. The corresponding solubility product of the precipitate has been calculated which is 2.1x10 -17 . It is shown that the method possesses certain selectivity, sufficient accuracy, and is rather fast. It has been established that determination can be performed in the presence of excess amounts of ions

  15. Method of separating hafnium from zirconium

    International Nuclear Information System (INIS)

    Megy, J.A.

    1980-01-01

    English. A new anhydrous method was developed for separating zirconium and hafnium, which gives higher separation factors and is more economical than previous methods. A molten phase, comprising a solution of unseparated zirconium and hafnium and a solvent metal, is first prepared. The molten metal phase is contacted with a fused salt phase which includes a zirconium salt. Zirconium and hafnium separation is effected by mutual displacement with hafnium being transported from the molten metal phase to the fused salt phase, while zirconium is transported from the fused salt phase to the molten metal phase. The solvent metal is less electropositive than zirconium. Zinc was chosen as the solvent metal, from a group which also included cadmium, lead, bismuth, copper, and tin. The fused salt phase cations are more electropositive than zirconium and were selected from a group comprising the alkali elements, the alkaline earth elements, the rare earth elements, and aluminum. A portion of the zirconium in the molten metal phase was oxidized by injecting an oxidizing agent, chlorine, to form zirconium tetrachlorid

  16. Kinetic studies on the hafnium nad deuterium

    International Nuclear Information System (INIS)

    Bing Wenzeng; Long Xinggui; Zhu Zuliang

    2009-04-01

    Through the method of reaction rate analysis in a constant volume reactor, the time dependence of the pressure drop of the hafnium deuteride formation are studied over a temperature range 573-873 K on a metal hydride thermodynamic and kinetic parameters measuring apparatus. The rate constants of the hafnium deuteride formation, which are 0.0530 s -1 , 0.0452 s -1 , 0.0319 s -1 , 0.0261 s -1 , are calculated at a serial temperatures of 573 K, 673 K, 773 K, 873 K and the initial pressure of 13 kPa. The activation energy of the reaction is (-10.1±1.5) kJ·mol -1 . Comparing the above results with those of titanium deuteride formation on the same measuring apparatus, the kinetic mechanism of the deuteride formation of hafnium and titanium is considered different. It is concluded that the reaction rate of hafnium absorbing deuterium may be controlled by phase transformation and surface oxidation. (authors)

  17. Recovery of hafnium values from loaded extraction solvent

    International Nuclear Information System (INIS)

    Abodishish, H.A.

    1989-01-01

    This patent describes an improvement in a process for recovering high purity hafnium hydroxide from a methyl isobutyl ketone organic solvent that is substantially free of sulfate ions and contains hafnium thiocyanate and thiocyanic acid. The improvement comprising reacting the organic solvent with ammonia to produce a reaction product in the form of a methyl isobutyl ketone organic solvent that is substantially free of sulfate ions and contains ammonium thiocyanite solution and hafnium hydroxide; separating the constituents of the reaction product in accordance with their respective specific gravities to produce a hafnium hydroxide sludge as one of the separation products; and removing the liquid component of the sludge to yield a high purity hafnium hydroxide ready for calcination to hafnium oxide

  18. Flotation separation of hafnium(IV) from aqueous solutions

    International Nuclear Information System (INIS)

    Downey, D.M.; Narick, C.N.; Cohen, T.A.

    1985-01-01

    A simple, rapid method for the separation of hafnium from aqueous solutions was investigated using sup(175+181)Hf tracer. Cationic hafnium complex ions were floated from dilute acid solutions with sodium lauryl sulfate (SLS) and anionic hafnium complexes were floated from basic and oxalic acid solutions with hexadecyltrimethyl ammonium bromide (HTMAB). The conditions necessary for quantitative recovery of the metal and mechanisms of flotation are described. (author)

  19. Flotation separation of hafnium(IV) from aqueous solutions

    Energy Technology Data Exchange (ETDEWEB)

    Downey, D.M.; Narick, C.N.; Cohen, T.A.

    1985-09-01

    A simple, rapid method for the separation of hafnium from aqueous solutions was investigated using sup(175 + 181)Hf tracer. Cationic hafnium complex ions were floated from dilute acid solutions with sodium lauryl sulfate (SLS) and anionic hafnium complexes were floated from basic and oxalic acid solutions with hexadecyltrimethyl ammonium bromide (HTMAB). The conditions necessary for quantitative recovery of the metal and mechanisms of flotation are described. (author). 21 refs.; 5 figs.

  20. Titanium zirconium and hafnium coordination compounds with vanillin thiosemicarbazone

    International Nuclear Information System (INIS)

    Konunova, Ts.B.; Kudritskaya, S.A.

    1987-01-01

    Coordination compounds of titanium zirconium and hafnium tetrachlorides with vanillin thiosemicarbazone of MCl 4 x nLig composition, where n=1.5, 4 for titanium and 1, 2, 4 for zirconium and hafnium, are synthesized. Molar conductivity of ethanol solutions is measured; IR spectroscopic and thermochemical investigation are carried out. The supposition about ligand coordination via sulfur and azomethine nitrogen atoms is made. In all cases hafnium forms stable compounds than zirconium

  1. Niobium and hafnium grown on porous membranes

    International Nuclear Information System (INIS)

    Morant, C.; Marquez, F.; Campo, T.; Sanz, J.M.; Elizalde, E.

    2010-01-01

    In this work we report on a method for fabricating highly ordered nanostructures of niobium and hafnium metals by physical vapour deposition using two different templates: anodized aluminum oxide membranes (AAO) and zirconium onto AAO membranes (Zr/AAO). The growth mechanism of these metal nanostructures is clearly different depending on the material used as a template. A different morphology was obtained by using AAO or Zr/AAO templates: when the metal is deposited onto AAO membranes, nanospheres with ordered hexagonal regularity are obtained; however, when the metal is deposited onto a Zr/AAO template, highly ordered nanocones are formed. The experimental approach described in this work is simple and suitable for synthesizing nanospheres or nanoholes of niobium and hafnium metals in a highly ordered structure.

  2. Joint titrimetric determination of zirconium and hafnium

    International Nuclear Information System (INIS)

    Vazquez, Cristina; Botbol, Moises; Bianco de Salas, G.N.; Cornell de Casas, M.I.

    1980-01-01

    A method for the joint titrimetric determination of zirconium and hafnium, which are elements of similar chemical behaviour, is described. The disodic salt of the ethylendiaminetetracetic acid (EDTA) is used for titration, while xilenol orange serves as final point indicator. Prior to titration it is important to evaporate with sulfuric acid, the solution resulting from the zirconium depolymerization process, to adjust the acidity and to eliminate any interferences. The method, that allows the quick and precise determination of zirconium and hafnium in quantities comprised between 0.01 and mg, was applied to the analysis of raw materials and of intermediate and final products in the fabrication of zirconium sponge and zircaloy. (M.E.L.) [es

  3. Molten salt scrubbing of zirconium or hafnium tetrachloride

    International Nuclear Information System (INIS)

    Lee, E.D.; McLaughlin, D.F.

    1990-01-01

    This patent describes a continuous process for removing impurities of iron or aluminum chloride or both from vaporous zirconium or hafnium chloride or both. It comprises: introducing impure zirconium or hafnium chloride vapor or both into a middle portion of an absorbing column containing a molten salt phase, the molten salt phase absorbing the impurities of iron or aluminum chloride or both to produce chloride vapor stripped of zirconium or hafnium chloride; introducing sodium or potassium chloride or both into a top portion of the column; controlling the top portion of the column to between 300--375 degrees C.; heating a bottom portion of the column to 450--550 degrees C. To vaporize zirconium chloride or hafnium chloride or hafnium and zirconium chloride from the molten salt; withdrawing molten salt substantially free of zirconium and hafnium chloride from the bottom portion of the column; and withdrawing zirconium chloride or hafnium chloride or hafnium and zirconium chloride vapor substantially free of impurities of iron and aluminum chloride from the top of the column

  4. Investigation of ferromagnetism in oxygen deficient hafnium oxide thin films

    Energy Technology Data Exchange (ETDEWEB)

    Hildebrandt, Erwin; Kurian, Jose; Krockenberger, Yoshiharu; Alff, Lambert [Institut fuer Materialwissenschaft, TU Darmstadt (Germany); Suter, Andreas [PSI, Villingen (Switzerland); Wilhelm, Fabrice; Rogalev, Andrei [ESRF, Grenoble (France)

    2008-07-01

    Oxygen deficient thin films of hafnium oxide were grown on single crystal r-cut and c-cut sapphire by reactive molecular beam epitaxy. RF-activated oxygen was used for the in situ oxidation of hafnium oxide thin films. Oxidation conditions were varied substantially in order to create oxygen deficiency in hafnium oxide films intentionally. The films were characterized by X-ray and magnetic measurements. X-ray diffraction studies show an increase in lattice parameter with increasing oxygen deficiency. Oxygen deficient hafnium oxide thin films also showed a decreasing bandgap with increase in oxygen deficiency. The magnetisation studies carried out with SQUID did not show any sign of ferromagnetism in the whole oxygen deficiency range. X-ray magnetic circular dichroism measurements also confirmed the absence of ferromagnetism in oxygen deficient hafnium oxide thin films.

  5. Preparation of hafnium carbide by chemical vapor deposition

    International Nuclear Information System (INIS)

    Hertz, Dominique.

    1974-01-01

    Hard, adhesive coatings of single-phase hafnium carbide were obtained by chemical vapor reaction in an atmosphere containing hafnium tetrachloride, methane and a large excess of hydrogen. By varying the gas phase composition and temperature the zones of formation of the different solid phases were studied and the growth of elementary hafnium and carbon deposits evaluated separately. The results show that the mechanism of hafnium carbide deposition does not hardly involve phenomene of homogeneous-phase methane decomposition or tetrachloride reduction by hydrogen unless the atmosphere is very rich or very poor in methane with respect to tetrachloride. However, hydrogen acting inversely on these two reactions, affects the stoichiometry of the substance deposited. The methane decomposition reaction is fairly slow, the reaction leading to hafnium carbide deposition is faster and that of tetrachloride reduction by hydrogen is quite fast [fr

  6. Assessing hafnium on hafnia as an oxygen getter

    International Nuclear Information System (INIS)

    O'Hara, Andrew; Demkov, Alexander A.; Bersuker, Gennadi

    2014-01-01

    Hafnium dioxide or hafnia is a wide band gap dielectric used in a range of electronic applications from field effect transistors to resistive memory. In many of these applications, it is important to maintain control over oxygen stoichiometry, which can be realized in practice by using a metal layer, specifically hafnium, to getter oxygen from the adjacent dielectric. In this paper, we employ density functional theory to study the thermodynamic stability of an interface between (100)-oriented monoclinic hafnia and hafnium metal. The nudged elastic band method is used to calculate the energy barrier for migration of oxygen from the oxide to the metal. Our investigation shows that the presence of hafnium lowers the formation energy of oxygen vacancies in hafnia, but more importantly the oxidation of hafnium through the migration of oxygen from hafnia is favored energetically

  7. Properties of filmogen solutions and films of hafnium compounds

    International Nuclear Information System (INIS)

    Sviridova, A.I.

    1986-01-01

    Study on hafnium hydrolizing compound solutions, used for hafnium oxide homogeneous layer formation, is conducted. In particular, electric conductivity, acidity and refractive index were investigated depending on the sal on ether concentration and the storage time. Oxyhafnium nitrate, hafnium chloride in ethanol, dichlorodiethoxyhafnium, hafnium oxychloride were used as initial compounds. Hydrolysis of hafnium compounds in solution occurs partially; further process occurs in the thin layer on the optical element surface; final decomposition is performed under heat treatment. It is ascertained, that alcoholic-aqueous solutions of inorganic salts can be filmogen only at definite acidity, density and viscosity (1.33-2.5 cp.). It is also ascertained that refractive index values and transmission spectral boundary of coatings, produced from alkoxy compound solutions and from chloride salt solutions, are practically the same. Transmittance boundary in ultraviolet region of spectrum of oxide films produced from nitrate and chloride solutions, varies with the heating temperature increase differently

  8. Analysis of hafnium in zirconium alloys

    International Nuclear Information System (INIS)

    Kondo, Isao; Sakai, Fumiaki; Ohuchi, Yoshifusa; Nakamura, Hisashi

    1977-01-01

    It is required to analyse alloying components and impurity elements in the acceptance analysis of zirconium alloys as the material for fuel cladding tubes and pressure tubes for advanced thermal reactors. Because of extreme similarity in chemical properties between zirconium and hafnium, about 100 ppm of hafnium is usually contained in zirconium alloys. Zircaloy-2 alloy and 2.5% Nb-zirconium with the addition of hafnium had been prepared as in-house standard samples for rapid analysis. Study was made on fluorescent X-ray analysis and emission spectral analysis to establish the analytical method. By using these in-house standard samples, acceptance analysis was successfully carried out for the fuel cladding tubes for advanced thermal reactors. Sulfuric acid solution was prepared from JAERI-Z 1, 2 and 3, the standard sample for zircaloy-2 prepared by the Analytical Committee on Nuclear Fuel and Reactor Materials, JAERI, and zirconium oxide (Hf 1 ppm/Zr). Standard Hf solution was added to the sulfuric acid solution step by step, to make up a series of the standard oxide samples by the precipitation process. By the use of these standard samples, the development of the analytical method and joint analysis were made by the three-member analytical technique research group including PNC. The analytical precision for the fluorescent X-ray analysis was improved by attaching a metallic yttrium filter to the window of an X-ray tube so as to suppress the effect due to zirconium matrix. The variation factor of the joint analysis was about 10% to show good agreement, and the indication value was determined. (Kobatake, H.)

  9. Primary hafnium metal sponge and other forms, approved standard 1973

    International Nuclear Information System (INIS)

    Anon.

    1975-01-01

    A specification is presented covering virgin hafnium metal commonly designated as sponge because of its porous, sponge-like texture; it may also be in other forms such as chunklets. The specification does not cover crystal bar

  10. Investigation of colourless complexes of thorium, hafnium and zirconium

    International Nuclear Information System (INIS)

    Kiciak, S.; Stefanowicz, T.; Gontarz, H.; Swit, Z.

    1980-01-01

    The investigations conducted in the Institute of General Chemistry of Poznan Technical University in partial cooperation with Kharkhof Technical University related with thorium, hafnium and zirconium complexes are reviewed. (author)

  11. Molten salt extractive distillation process for zirconium-hafnium separation

    International Nuclear Information System (INIS)

    McLaughlin, D.F.; Stoltz, R.A.

    1989-01-01

    This patent describes an improvement in a process for zirconium-hafnium separation. It utilizes an extractive distillation column with a mixture of zirconium and hafnium tetrachlorides introduced into a distillation column having a top and bottom with hafnium enriched overheads taken from the top of the column and a molten salt solvent circulated through the column to provide a liquid phase, and with molten salt solvent containing zirconium chloride being taken from the bottom of the distillation column. The improvements comprising: utilizing a molten salt solvent consisting principally of lithium chloride and at least one of sodium, potassium, magnesium and calcium chlorides; stripping of the zirconium chloride taken from the bottom of the distillation column by electrochemically reducing zirconium from the molten salt solvent; and utilizing a pressurized reflux condenser on the top of the column to add the hafnium chloride enriched overheads to the molten salt solvent previously stripped of zirconium chloride

  12. Internal Dosimetry for Inhalation of Hafnium Tritide Aerosols

    Energy Technology Data Exchange (ETDEWEB)

    Inkret, W.C.T.; Schillaci, M.E.; Boyce, M.K.; Cheng, Y.S.; Efurd, D.W.; Little, T.T.; Miller, G.; Musgrave, J.A.; Wermer, J.R

    2001-07-01

    Metal tritides with low dissolution rates may have residence times in the lungs which are considerably longer than the biological half-time normally associated with tritium in body water, resulting in long-term irradiation of the lungs by low energy {beta} particles and bremsstrahlung X rays. Samples of hafnium tritide were placed in a lung simulant fluid to determine approximate lung dissolution rates. Hafnium hydride samples were analysed for particle size distribution with a scanning electron microscope. Lung simulant data indicated a biological dissolution half-time for hafnium tritide on the order of 10{sup 5}d. Hafnium hydride particle sizes ranged between 2 and 10 {mu}m, corresponding to activity median aerodynamic diameters of 5 to 25 {mu}m. Review of in vitro dissolution data, development of a biokinetic model, and determination of secondary limits for 1 {mu}m AMAD particles are presented and discussed. (author)

  13. New solvent extraction process for zirconium and hafnium

    International Nuclear Information System (INIS)

    Takahashi, M.; Katoh, Y.; Miyazaki, H.

    1984-01-01

    The authors' company developed a new solvent extraction process for zirconium and hafnium separation, and started production of zirconium sponge by this new process in September 1979. The process utilizes selective extraction of zirconium oxysulfate using high-molecular alkyl amine, and has the following advantages: 1. This extraction system has a separation factor as high as 10 to 20 for zirconium and hafnium in the range of suitable acid concentration. 2. In the scrubbing section, removal of all the hafnium that coexists with zirconium in the organic solvent can be effectively accomplished by using scrubbing solution containing hafnium-free zirconium sulfate. Consequently, hafnium in the zirconium sponge obtained is reduced to less than 50 ppm. 3. The extractant undergoes no chemical changes but is very stable for a long period. In particular, its solubility in water is small, about 20 ppm maximum, posing no environmental pollution problems such as are often caused by other process raffinates. At the present time, the zirconium and hafnium separation operation is very stable, and zirconium sponge made by this process can be applied satisfactorily to nuclear reactors

  14. Separation process of zirconium and hafnium

    International Nuclear Information System (INIS)

    Hure, J.; Saint-James, R.

    1955-01-01

    About the separation different processes of zirconium-hafnium, the extraction by solvent in cross-current is the most easily the process usable on an industrial scale. It uses tributyl phosphate as solvent, diluted with white spirit to facilitate the decanting. Some exploratory tests showed that nitric environment seemed the most favorable for extraction; but a lot of other factors intervene in the separation process. We studied the influence of the acidity successively, the NO 3 - ions concentration, the role of the cation coming with NO 3 - , as well as the influence of the concentration of zirconium in the solution on the separation coefficient β = α Zr / α Hf . (M.B.) [fr

  15. The interaction of fast neutrons with hafnium

    International Nuclear Information System (INIS)

    Smith, A.B.

    2002-01-01

    Elemental hafnium neutron total cross sections are measured from ∼0.75 to 4.5 MeV in steps of ∼40 keV. Differential neutron elastic-scattering cross sections are measured from ∼4.5 to 10.0 MeV in ∼0.5 MeV steps and at 40 scattering angles distributed between ∼17 and 160 deg. These data are combined with those found in the literature to construct a comprehensive experimental data base which is interpreted in terms of coupled-channels models. Physical characteristics of the resulting potentials are discussed. Comparisons are made with ENDF/B-6 (MAT 7200). A detailed report of this work is given by Smith (Smith, A., 2001. Argonne National Laboratory Report ANL/NDM-153)

  16. High temperature diffusion of hafnium in tungsten and a tungsten-hafnium carbide alloy

    International Nuclear Information System (INIS)

    Ozaki, Y.; Zee, R.H.

    1994-01-01

    Refractory metals and ceramics are used extensively in energy systems due to their high temperature properties. This is particularly important in direct conversion systems where thermal to electric conversion efficiency is a direct function of temperature. Tungsten, which has the highest melting temperature among elemental metals, does not possess sufficient creep resistance at temperature above 1,600 K. Different dispersion strengthened tungsten alloys have been developed to extend the usefulness of tungsten to higher temperatures. One of these alloys, tungsten with 0.4 mole percent of finely dispersed HfC particles (W-HfC), has the optimum properties for high temperature applications. Hafnium carbide is used as the strengthening agent due to its high chemical stability and its compatibility with tungsten. The presence of HfC particles retards the rate of grain growth as well as restricting dislocation motion. Both of which are beneficial for creep resistance. The long term behavior of this alloy depends largely on the evolution of its microstructure which is governed by the diffusion of its constituents. Data on the diffusion of carbon in tungsten and tungsten self-diffusion are available, but no direct measurements have been made on the diffusion of hafnium in tungsten. The only diffusion data available are estimated from a coarsening study and these data are highly unreliable. In this study, the diffusion behavior of hafnium in pure tungsten and in a W-HfC alloy was directly measured by means of Secondary Ion Mass Spectroscopy (SIMS). The selection of the W-HfC alloy is due to its importance in high temperature engineering applications, and its higher recrystallization temperature. The presence of HfC particles in tungsten restricts grain growth resulting in better high temperature creep resistance. The higher recrystallization temperature allows measurements to be made over a wider range of temperatures at a relatively constant grain size

  17. 40 CFR 471.90 - Applicability; description of the zirconium-hafnium forming subcategory.

    Science.gov (United States)

    2010-07-01

    ... zirconium-hafnium forming subcategory. 471.90 Section 471.90 Protection of Environment ENVIRONMENTAL... POINT SOURCE CATEGORY Zirconium-Hafnium Forming Subcategory § 471.90 Applicability; description of the zirconium-hafnium forming subcategory. This subpart applies to discharges of pollutants to waters of the...

  18. 40 CFR 421.330 - Applicability: Description of the primary zirconium and hafnium subcategory.

    Science.gov (United States)

    2010-07-01

    ... primary zirconium and hafnium subcategory. 421.330 Section 421.330 Protection of Environment ENVIRONMENTAL... CATEGORY Primary Zirconium and Hafnium Subcategory § 421.330 Applicability: Description of the primary zirconium and hafnium subcategory. The provisions of this subpart are applicable to discharges resulting...

  19. Ground-state structures of Hafnium clusters

    Energy Technology Data Exchange (ETDEWEB)

    Ng, Wei Chun; Yoon, Tiem Leong [School of Physics, Universiti Sains Malaysia, 11800 USM, Penang (Malaysia); Lim, Thong Leng [Faculty of Engineering and Technoloty, Multimedia University, Melaca Campus, 75450 Melaka (Malaysia)

    2015-04-24

    Hafnium (Hf) is a very large tetra-valence d-block element which is able to form relatively long covalent bond. Researchers are interested to search for substitution to silicon in the semi-conductor industry. We attempt to obtain the ground-state structures of small Hf clusters at both empirical and density-functional theory (DFT) levels. For calculations at the empirical level, charge-optimized many-body functional potential (COMB) is used. The lowest-energy structures are obtained via a novel global-minimum search algorithm known as parallel tempering Monte-Carlo Basin-Hopping and Genetic Algorithm (PTMBHGA). The virtue of using COMB potential for Hf cluster calculation lies in the fact that by including the charge optimization at the valence shells, we can encourage the formation of proper bond hybridization, and thus getting the correct bond order. The obtained structures are further optimized using DFT to ensure a close proximity to the ground-state.

  20. Hafnium carbide nanocrystal chains for field emitters

    International Nuclear Information System (INIS)

    Tian, Song; Li, Hejun; Zhang, Yulei; Ren, Jincui; Qiang, Xinfa; Zhang, Shouyang

    2014-01-01

    A hafnium carbide (HfC) nanostructure, i.e., HfC nanocrystal chain, was synthesized by a chemical vapor deposition (CVD) method. X-ray diffractometer, field-emission scanning electron microscope, transmission electron microscope, and energy-dispersive X-ray spectrometer were employed to characterize the product. The synthesized one-dimensional (1D) nanostructures with many faceted octahedral nanocrystals possess diameters of tens of nanometers to 500 nm and lengths of a few microns. The chain-like structures possess a single crystalline structure and preferential growth direction along the [1 0 0] crystal orientation. The growth of the chains occurred through the vapor–liquid–solid process along with a negative-feedback mechanism. The field emission (FE) properties of the HfC nanocrystal chains as the cold cathode emitters were examined. The HfC nanocrystal chains display good FE properties with a low turn-on field of about 3.9 V μm −1 and a high field enhancement factor of 2157, implying potential applications in vacuum microelectronics.

  1. Use of hafnium in control bars of nuclear reactors

    International Nuclear Information System (INIS)

    Ramirez S, J.R.; Alonso V, G.

    2003-01-01

    Recently the use of hafnium as neutron absorber material in nuclear reactors has been reason of investigation by virtue of that this material has nuclear properties as to the neutrons absorption and structural that can prolong the useful life of the control mechanisms of the nuclear reactors. In this work some of those more significant hafnium properties are presented like nuclear material. Also there are presented calculations carried out with the HELIOS code for fuel cells of uranium oxide and of uranium and plutonium mixed oxides under controlled conditions with conventional bars of boron carbide and also with similar bars to which are substituted the absorbent material by metallic hafnium, the results are presented in this work. (Author)

  2. Analytical study of zirconium and hafnium α-hydroxy carboxylates

    International Nuclear Information System (INIS)

    Terra, V.R.

    1991-01-01

    The analytical study of zirconium and hafnium α-hydroxy carboxylates was described. For this purpose dl-mandelic, dl-p-bromo mandelic, dl-2-naphthyl glycolic, and benzilic acids were prepared. These were used in conjunction with glycolic, dl-lactic, dl-2-hydroxy isovaleric, dl-2-hydroxy hexanoic, and dl-2-hydroxy dodecanoic acids in order to synthesize the zirconium(IV) and hafnium(IV) tetrakis(α-hydroxy carboxylates). The compounds were characterized by melting point determination, infrared spectroscopy, thermogravimetric analysis, calcination to oxides and X-ray diffractometry by the powder method. (C.G.C)

  3. High temperature evaporation of titanium, zirconium and hafnium carbides

    International Nuclear Information System (INIS)

    Gusev, A.I.; Rempel', A.A.

    1991-01-01

    Evaporation of cubic nonstoichiometric carbides of titanium, zirconium and hafnium in a comparatively low-temperature interval (1800-2700) with detailed crystallochemical sample certification is studied. Titanium carbide is characterized by the maximum evaporation rate: at T>2300 K it loses 3% of sample mass during an hour and at T>2400 K titanium carbide evaporation becomes extremely rapid. Zirconium and hafnium carbide evaporation rates are several times lower than titanium carbide evaporation rates at similar temperatures. Partial pressures of metals and carbon over the carbides studied are calculated on the base of evaporation rates

  4. Preparation of complexes of zirconium and hafnium tetrachlorides with phosphorus oxychloride

    International Nuclear Information System (INIS)

    McLaughlin, D.F.

    1989-01-01

    This patent describes an improvement in a method for separating hafnium tetrachloride from zirconium tetrachloride where a complex of zirconium-hafnium tetrachlorides and phosphorus oxychloride is prepared from zirconium-hafnium tetrachlorides and the complex of zirconium-hafnium tetrachlorides and phosphorus oxychloride is introduced into a distillation column, which distillation column has a reboiler connected at the bottom and a reflux condenser connected at the top and where a hafnium tetrachloride enriched stream is taken from the top of the column and a zirconium enriched tetrachloride stream is taken from the bottom of the column. The improvement comprising: prepurifying the zirconium-hafnium tetrachlorides, prior to preparation of the complex and introduction of the complex into a distillation column, to substantially eliminate iron chloride from the zirconium hafnium tetrachlorides, whereby buildup or iron chloride in the distillation column and in the reboiler is substantially eliminated and the column can be operated in a continuous, stable and efficient manner

  5. Separation process of zirconium and hafnium; Procede de separation du zirconium et du hafnium

    Energy Technology Data Exchange (ETDEWEB)

    Hure, J; Saint-James, R [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1955-07-01

    About the separation different processes of zirconium-hafnium, the extraction by solvent in cross-current is the most easily the process usable on an industrial scale. It uses tributyl phosphate as solvent, diluted with white spirit to facilitate the decanting. Some exploratory tests showed that nitric environment seemed the most favorable for extraction; but a lot of other factors intervene in the separation process. We studied the influence of the acidity successively, the NO{sub 3}{sup -} ions concentration, the role of the cation coming with NO{sub 3}{sup -}, as well as the influence of the concentration of zirconium in the solution on the separation coefficient {beta} = {alpha}{sub Zr} / {alpha}{sub Hf}. (M.B.) [French] Des differents procedes de separation zirconium-hafnium, l'extraction par solvant en contre-courant est le procede le plus facilement utilisable a l'echelle industrielle. On utilise comme solvant le phosphate de tributyle, dilue avec du white spirit pour faciliter les decantations. Des essais preliminaires ont montre que le milieu nitrique semblait le plus favorable a l'extraction; mais beaucoup d'autres facteurs interviennent dans le processus de separation. Nous avons etudie successivement l'influence de l'acidite, celle de la concentration en ions NO{sub 3}{sup -}, le role du cation accompagnant NO{sub 3}{sup -}, ainsi que l'influence de la concentration en zirconium de la solution sur le coefficient de separation {beta} = {alpha}{sub Zr} / {alpha}{sub Hf}. (MB)

  6. Separation of zirconium and hafnium using paper distribution chromatography

    International Nuclear Information System (INIS)

    Lebedeva, G.G.; Viktorova, M.E.

    1981-01-01

    A method is suggested of chromatographic separation of zirconium and hafnium in a CCl 4 -tributyl phosphate system (1:9) containing KCl as a salting-out agent in 5 M HNO 3 at 28-30 deg C. Zr and Hf are deterfmined in articiial mixtures under optimal chromatography conditions using visual colorimetry [ru

  7. X-Ray Photoemission Study of the Oxidation of Hafnium

    International Nuclear Information System (INIS)

    Chourasia, R.; Hickman, J.L.; Miller, R.L.; Nixon, G.A.; Seabolt, M.A.

    2011-01-01

    About 20 angstrom of hafnium were deposited on silicon substrates using the electron beam evaporation technique. Two types of samples were investigated. In one type, the substrate was kept at the ambient temperature. After the deposition, the substrate temperature was increased to 100, 200, and 300 degree C. In the other type, the substrate temperature was held fixed at some value during the deposition. For this type, the substrate temperatures used were 100, 200, 300, 400, 500, 550, and 600 degree C. The samples were characterized in situ by the technique of X-ray photoelectron spectroscopy. No trace of elemental hafnium is observed in the deposited overlayer. Also, there is no evidence of any chemical reactivity between the overlayer and the silicon substrate over the temperature range used. The hafnium overlayer shows a mixture of the dioxide and the suboxide. The ratio of the suboxide to dioxide is observed to be more in the first type of samples. The spectral data indicate that hafnium has a strong affinity for oxygen. The overlayer gets completely oxidized to form HfO 2 at substrate temperature around 300 degree C for the first type of samples and at substrate temperature greater than 550 degree C for the second type

  8. X-Ray Photoemission Study of the Oxidation of Hafnium

    Directory of Open Access Journals (Sweden)

    A. R. Chourasia

    2009-01-01

    Full Text Available About 20 Å of hafnium were deposited on silicon substrates using the electron beam evaporation technique. Two types of samples were investigated. In one type, the substrate was kept at the ambient temperature. After the deposition, the substrate temperature was increased to 100, 200, and 300∘C. In the other type, the substrate temperature was held fixed at some value during the deposition. For this type, the substrate temperatures used were 100, 200, 300, 400, 500, 550, and 600∘C. The samples were characterized in situ by the technique of X-ray photoelectron spectroscopy. No trace of elemental hafnium is observed in the deposited overlayer. Also, there is no evidence of any chemical reactivity between the overlayer and the silicon substrate over the temperature range used. The hafnium overlayer shows a mixture of the dioxide and the suboxide. The ratio of the suboxide to dioxide is observed to be more in the first type of samples. The spectral data indicate that hafnium has a strong affinity for oxygen. The overlayer gets completely oxidized to form HfO2 at substrate temperature around 300∘C for the first type of samples and at substrate temperature greater than 550∘C for the second type.

  9. Modelling of Zirconium and Hafnium separation using continuous annular chromatography

    International Nuclear Information System (INIS)

    Moch-Setyadji; Endang Susiantini

    2014-01-01

    Nuclear degrees of zirconium in the form of a metal alloy is the main material for fuel cladding of NPP. Zirconium is also used as sheathing UO 2 kernel in the form of ZrC as a substitute of SiC in the fuel elements of High Temperature Reactor (HTR). Difficulty separating hafnium from zirconium because it has a lot of similarities in the chemical properties of Zr and Hf. Annular chromatography is a device that can be used for separating of zirconium and hafnium to obtain zirconium nuclear grade. Therefore, it is necessary to construct the mathematical modelling that can describe the separation of zirconium and hafnium in the annular chromatography containing anion resin dowex-1X8. The aim of research is to perform separation simulation by using the equilibrium model and mass transfer coefficient resulted from research. Zr and Hf feed used in this research were 26 and 1 g/l, respectively. Height of resin (L), angular velocity (ω) and the superficial flow rate (uz) was varied to determine the effect of each parameter on the separation of Zr and Hf. By using Kd and Dv values resulted previous research. Simulation results showed that zirconium and hafnium can be separated using a continuous annular chromatography with high resin (long bed) 50 cm, superficial flow rate of 0.001 cm/s, the rotation speed of 0.006 rad/min and 20 cm diameter annular. In these conditions the results obtained zirconium concentration of 10,303.226 g/m 3 and hafnium concentration of 12.324 g/m 3 (ppm). (author)

  10. Hafnium Resonance Parameter Analysis Using Neutron Capture and Transmission Experiments

    International Nuclear Information System (INIS)

    MJ Trbovich; DP Barry; RE Slovacck; Y Danon; RC Block; JA Burke; NJ Drindak; G Leinweber; RV Ballad

    2004-01-01

    The focus of this work is to determine resonance parameters for stable hafnium isotopes in the 0.005-200 eV region, with special emphasis on the overlapping 176 Hf and 178 Hf resonances near 8 eV. The large neutron cross section of hafnium, combined with its corrosion resistance and excellent mechanical properties, make it a useful material for controlling nuclear reactions. Experiments measuring neutron capture and transmission were performed at the Rensselaer Polytechnic Institute (RPI) electron linear accelerator (LINAC) using the time of flight method. 6 Li glass scintillation detectors were used for transmission experiments at flight path lengths of 15 and 25 m. Capture experiments were done using a sixteen section NaI(Tl) multiplicity detector at a flight path length of 25 m. These experiments utilized various thicknesses of metallic and isotopically-enriched liquid samples. The liquid samples were designed to provide information on the 176 Hf and 178 Hf contributions to the 8 eV doublet without saturation. Data analysis was done using the R-matrix Bayesian code SAMMY version M6 beta. SAMMY is able to account for experimental resolution effects for each of the experimental setups at the RPI LINAC, and also can correct for multiple scattering effects in neutron capture yield data. The combined capture and transmission data analysis yielded resonance parameters for all hafnium isotopes from 0.005-200 eV. Resonance integrals were calculated along with errors for each hafnium isotope using the NJOY [1] and INTER [2] codes. The isotopic resonance integrals calculated were significantly different than previously published values; however the calculated elemental hafnium resonance integral changed very little

  11. 40 CFR 166.25 - Agency review.

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 23 2010-07-01 2010-07-01 false Agency review. 166.25 Section 166.25... Health Exemptions § 166.25 Agency review. (a) General. The Agency will review all requests as... is needed. The Agency will review the application and other available data necessary to make a...

  12. 7 CFR 1427.166 - Insurance.

    Science.gov (United States)

    2010-01-01

    ... 7 Agriculture 10 2010-01-01 2010-01-01 false Insurance. 1427.166 Section 1427.166 Agriculture... AGRICULTURE LOANS, PURCHASES, AND OTHER OPERATIONS COTTON Recourse Seed Cotton Loans § 1427.166 Insurance. The seed cotton must be insured at the full loan value against loss or damage by fire. ...

  13. 34 CFR 668.166 - Excess cash.

    Science.gov (United States)

    2010-07-01

    ... the Secretary for the costs the Secretary incurred in providing that excess cash to the institution... 34 Education 3 2010-07-01 2010-07-01 false Excess cash. 668.166 Section 668.166 Education..., DEPARTMENT OF EDUCATION STUDENT ASSISTANCE GENERAL PROVISIONS Cash Management § 668.166 Excess cash. (a...

  14. 9 CFR 166.7 - Cooking standards.

    Science.gov (United States)

    2010-01-01

    ... 9 Animals and Animal Products 1 2010-01-01 2010-01-01 false Cooking standards. 166.7 Section 166.7... HEALTH PROTECTION SWINE HEALTH PROTECTION General Provisions § 166.7 Cooking standards. (a) Garbage shall...) Garbage shall be agitated during cooking, except in steam cooking equipment, to ensure that the prescribed...

  15. 33 CFR 157.166 - Hydrocarbon emissions.

    Science.gov (United States)

    2010-07-01

    ... 33 Navigation and Navigable Waters 2 2010-07-01 2010-07-01 false Hydrocarbon emissions. 157.166 Section 157.166 Navigation and Navigable Waters COAST GUARD, DEPARTMENT OF HOMELAND SECURITY (CONTINUED... Crude Oil Washing (COW) System on Tank Vessels Cow Operations § 157.166 Hydrocarbon emissions. If the...

  16. 17 CFR 166.3 - Supervision.

    Science.gov (United States)

    2010-04-01

    ... 17 Commodity and Securities Exchanges 1 2010-04-01 2010-04-01 false Supervision. 166.3 Section 166.3 Commodity and Securities Exchanges COMMODITY FUTURES TRADING COMMISSION CUSTOMER PROTECTION RULES § 166.3 Supervision. Each Commission registrant, except an associated person who has no supervisory duties, must diligently supervise the handling b...

  17. Electronic properties of hafnium oxide: A contribution from defects and traps

    Energy Technology Data Exchange (ETDEWEB)

    Gritsenko, Vladimir A., E-mail: grits@isp.nsc.ru; Perevalov, Timofey V.; Islamov, Damir R., E-mail: damir@isp.nsc.ru

    2016-02-15

    In the present article, we give a review of modern data and latest achievements pertaining to the study of electronic properties of oxygen vacancies in hafnium oxide. Hafnium oxide is a key dielectric for use in many advanced silicon devices. Oxygen vacancies in hafnium oxide largely determine the electronic properties of the material. We show that the electronic transitions between the states due to oxygen vacancies largely determine the optical absorption and luminescent properties of hafnium oxide. We discuss the role of oxygen vacancies as traps that facilitate charge transport in hafnium oxide films. Also, we demonstrate the fact that the electrical conductivity in hafnium oxide is controlled by the phonon-assisted tunnelling of charge carriers between traps that were identified as oxygen vacancies.

  18. Method of purifying zirconium tetrachloride and hafnium tetrachloride in a vapor stream

    International Nuclear Information System (INIS)

    Snyder, T.S.; Stolz, R.A.

    1992-01-01

    This patent describes a method of purifying zirconium tetrachloride and hafnium tetrachloride in a vapor stream from a sand chlorinator in which the silicon and metals present in sand fed to the chlorinator are converted to chlorides at temperatures over about 800 degrees C. It comprises cooling a vapor stream from a sand chlorinator, the vapor stream containing principally silicon tetrachloride, zirconium tetrachloride, and hafnium tetrachloride contaminated with ferric chloride, to a temperature of from about 335 degrees C to about 600 degrees C; flowing the vapor stream through a gaseous diffusion separative barrier to produce a silicon tetrachloride-containing vapor stream concentrated in zirconium tetrachloride and hafnium tetrachloride and a silicon tetrachloride-containing vapor stream depleted in zirconium tetrachloride and hafnium tetrachloride; adsorbing the ferric chloride in the separative barrier; and recovering the silicon tetrachloride stream concentrated in zirconium tetrachloride and hafnium tetrachloride separately from the silicon tetrachloride stream depleted in zirconium tetrachloride and hafnium tetrachloride

  19. Synthesis of Hafnium-Based Ceramic Materials for Ultra-High Temperature Aerospace Applications

    Science.gov (United States)

    Johnson, Sylvia; Feldman, Jay

    2004-01-01

    This project involved the synthesis of hafnium (Hf)-based ceramic powders and Hf-based precursor solutions that were suitable for preparation of Hf-based ceramics. The Hf-based ceramic materials of interest in this project were hafnium carbide (with nominal composition HE) and hafnium dioxide (HfO2). The materials were prepared at Georgia Institute of Technology and then supplied to research collaborators Dr. Sylvia Johnson and Dr. Jay Feldman) at NASA Ames Research Center.

  20. Elaboration and characterisation of yttrium oxide and hafnium oxide powders by the sol-gel process

    International Nuclear Information System (INIS)

    Hours, T.

    1988-01-01

    The two classical sol-gel processes, colloidal and polymeric are studied for the preparation of yttrium oxide and hafnium oxide high performance powders. In the colloidal process, controlled and reproducible conditions for the preparation of yttrium oxide and hafnium oxide sols from salts or alkoxides are developed and the hydrothermal synthesis monodisperse hafnium oxide colloids is studied. The polymeric process is studied with hafnium ethyl-hexylate, hydrolysis kinetics for controlled preparation of sols and gels is investigated. Each step of preparation is detailed and powders obtained are characterized [fr

  1. Design and fabrication of hafnium tube to control the power of the irradiation test fuel in HANARO

    Energy Technology Data Exchange (ETDEWEB)

    Kim, D. H.; Lee, C. B.; Kim, Y. M.; Yang, Y. S.; Jung, Y. H

    2003-05-01

    For the irradiation test at HANARO, non-instrumentation capsule was manufactured and hafnium tube was used to control LHGR of HANARO. Hafnium tube can control the irradiation condition of HANARO similar to that of commercial reactor. Hafnium tube thickness was determined by the LHGR calculated at OR-4 irradiation hole to be installed the non-instrumented capsule. To fabricate the hafnium tube with hafnium plate, the fabrication method was determined by using the hafnium mechanical properties. And the tensile strength of hafnium was confirmed by tensile test. This report is confirmed the LHGR control at the OR-4 and the Hafnium fabrication for in used which the AFPCAP non-instrumented irradiation capsule.

  2. Pentamethylcyclopentadienyl Zirconium and Hafnium Polyhydride Complexes : Synthesis, Structure, and Reactivity

    NARCIS (Netherlands)

    Visser, Cindy; Hende, Johannes R. van den; Meetsma, Auke; Hessen, Bart; Teuben, Jan H.

    2001-01-01

    The half-sandwich zirconium and hafnium N,N-dimethylaminopropyl complexes Cp*M[(CH2)3NMe2]Cl2 (Cp* = η5-C5Me5, M = Zr, 1; Hf, 2) and Cp*M[(CH2)3NMe2]2Cl (M = Zr, 3; Hf, 4) were synthesized by mono- or dialkylation of Cp*MCl3 with the corresponding alkyllithium and Grignard reagents. Hydrogenolysis

  3. Separation of zirconium from hafnium by ion exchange

    Energy Technology Data Exchange (ETDEWEB)

    Felipe, Elaine C.B.; Palhares, Hugo G.; Ladeira, Ana Claudia Q., E-mail: elainecfelipe@yahoo.com.br, E-mail: hugopalhares@gmail.com, E-mail: ana.ladeira@cdtn.br [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2013-07-01

    Zirconium and hafnium are two of the most important metals for the nuclear industry. Hafnium occurs in all zirconium ores usually in the range 2 - 3%. However, for the most nuclear industry applications, it is necessary to use a zirconium of extremely pure level. The current work consists in the separation of zirconium and hafnium by the ion exchange method in order to obtain a zirconium concentrate of high purity. The zirconium and hafnium liquors were produced from the leaching of the Zr(OH){sub 4} and Hf(OH){sub 4} with nitric acid for 24 hours. From these two liquors it was prepared one solution containing 7.5 x 10{sup -2} mol L{sup -1} of Zr and 5.8 x 10{sup -3} mol L{sup -1} of Hf with acidity of 1 M. Ion exchange experiments were carried out in batch with the resins Dowex 50WX4, Dowex 50WX8 100, Dowex 50WX8 50, Amberlite IR-120 and Marathon C at constant temperature 28 deg C. Other variables such as, acidity and agitation were kept constant. The data were adjusted to Langmuir equation in order to calculate the maximum loading capacity (q{sub max}) of the resins, the distribution coefficient (K{sub d}) for Zr and Hf and the separation factor (α{sub Hf}{sup Zr} ). The results of maximum loading capacity (q{sub max}) for Zr and Hf, in mmol g{sup -}1, showed that the most suitable resins for columns experiments are: Dowex 50WX4 50 (q{sub max} Z{sub r} = 2.21, Hf = 0.18), Dowex 50WX8 50 (q{sub max} Zr = 1.89, Hf = 0.13) and Amberlite (q{sub max} Zr = 1.64, Hf = 0.12). However, separations factors, α{sub Hf}{sup Zr}, showed that the resins are not selective. (author)

  4. Evolution of the hafnium isotopic composition in the RBMK reactor

    International Nuclear Information System (INIS)

    Jurkevicius, A.; Remeikis, V.

    2002-01-01

    The isotopic composition of hafnium in the radial neutron flux sensor of the RBMK-1500 reactor, the rates of the neutron absorption on Hf isotopes and the neutron spectrum in the sensor were numerically modeled. The sequence SAS2 (Shielding Analysis Sequence) program from the package SCALE 4.4A and the HELIOS code system were used for calculations. It has been obtained that the overall neutron absorption rates in hafnium for the sensors located in the 2.4 % and 2.6 % enrichment uranium-erbium nuclear fuel assemblies are by 16 % and 19 % lower than in the 2.0 % enrichment uranium nuclear fuel assemblies. The overall neutron absorption rate in hafnium decreases 2.70-2.75 times due to the sensor burnup to 5800 MW d. The sensitivity of the Hf sensors to the thermal neutron flux increases twice due to the nuclear fuel assembly burnup to 3000 MW d. The corrective factors ξ d (I) at the different integral current I of the sensors and ξ td (E) at the different burnup E of the nuclear fuel assemblies were calculated. The obtained dependence ξ d (I) calculated numerically was compared to the experimental one determined by comparing signals of the fresh sensor and the sensor with the integral current I and by processing repeated calibration results of Hf sensors in RBMK-1500 reactors. The relative relationship coefficients K T (T FA ) were found for all RBMK-1500 nuclear fuel types. (author)

  5. Recovery of hafnium radioisotopes from a proton irradiated tantalum target

    International Nuclear Information System (INIS)

    Taylor, W.A.; Garcia, J.G.; Hamilton, V.T.; Heaton, R.C.; Jamriska, D.J.; Ott, M.A.; Philips, D.R.; Radzinski, S.D.

    1998-01-01

    The 178m2 Hf nucleus, with its long half-life (31 y) and high-spin isomeric state (16 + ) is desired for new and exotic nuclear physics studies. The Los Alamos Radioisotope Program irradiated a kilogram of natural tantalum at the Los Alamos Meson Physics Facility in early 1981. After fifteen years of decay, this target was ideal for the recovery of 178m2 Hf. There was more than a millicurie of 178m2 Hf produced during this irradiation and there has been a sufficient period of time for most of the other hafnium radioisotopes to decayed away. Traditionally, separation techniques for recovering hafnium isotopes from tantalum targets employ solvent extractions with reagents that are considered hazardous. These techniques are no longer condoned because they generate a mixed-waste (radioactive and hazardous components) that can not be treated for disposal. In this paper we describe a new and unique procedure for the recovery of hafnium radioisotopes from a highly radioactive, proton irradiated, tantalum target using reagents that do not contribute a hazardous waste component. (author)

  6. Zirconium and hafnium in the southeastern Atlantic States

    Science.gov (United States)

    Mertie, J.B.

    1958-01-01

    The principal source of zirconium and hafnium is zircon, though a minor source is baddeleyite, mined only in Brazil. Zircon is an accessory mineral in igneous, metamorphic, and sedimentary rocks, but rarely occurs in hardrock in minable quantities. The principal sources of zircon are therefore alluvial deposits, which are mined in many countries of five continents. The principal commercial deposits in the United States are in Florida, though others exist elsewhere in the southeastern Coastal Plain. The evidence indicates that conditions for the accumulation of workable deposits of heavy minerals were more favorable during the interglacial stages of the Pleistocene epoch than during Recent time. Therefore detrital ores of large volume and high tenor are more likely to be found in the terrace deposits than along the present beaches. Other concentrations of heavy minerals, however, are possible at favored sites close to the Fall Line where the Tuscaloosa formation rests upon the crystalline rocks of the Piedmont province. A score of heavy and semiheavy minerals occur in the detrital deposits of Florida, but the principal salable minerals are ilmenite, leucoxene, rutile, and zircon, though monazite and staurolite are saved at some mining plants. Commercial deposits of heavy minerals are generally required to have a tenor of 4 percent, though ores with a lower tenor can be mined at a profit if the content of monazite is notably high. The percentages of zircon in the concentrates ranges from 10 to 16 percent, and in eastern Florida from 13 to 15 percent. Thus the tenor in zircon of the ore-bearing sands ranges from 0.4 to 0.6 percent. The content of hafnium in zircon is immaterial for many uses, but for some purposes very high or very low tenors in hafnium are required. Alluvial zircon cannot be separated into such varieties, which, if needed, must be obtained from sources in bedrock. It thus becomes necessary to determine the Hf : Zr ratios in zircon from many kinds of

  7. On the stabilization of niobium(V) solutions by zirconium(IV) and hafnium(IV)

    DEFF Research Database (Denmark)

    Sørensen, E.; Bjerre, A.B.

    1992-01-01

    Niobium cannot be separated from zirconium or hafnium when these elements occur together in solution with common anions such as chloride and sulphate. This is ascribed to the co-polymerization of niobium(V) and the hydrolysed ionic species of zirconium(IV) and hafnium(IV) to form colloidal...

  8. Use of X-ray fluorescence analysis for the determination of hafnium in zircalloys

    International Nuclear Information System (INIS)

    Sato, I.M.; Salvador, V.L.R.; Lordello, A.R.

    1985-01-01

    The determination of hafnium at trace levels (ppm) in the presence of zirconium by X-ray fluorescence technique is presented. The samples were prepared in the form of double-layer pellets, with boric acid as the binding material. The most sensitive first order line of hafnium HfLα (0.157 nm), which is used analyticaly, has approximately 67% overlapping with second order line of zirconium ZrKα 1 , (0.079 nm). As the excitation potencial of zirconium is larger than hafnium, the best condition was selected, so that the interference of zirconium intensity would not be significant in hafnium analytical line. The method allowed the determination of hafnium above 5.0 ppm (LLd = 1.5 ppm) with an accuracy of less than 10%. (Author) [pt

  9. Preparation of complexes of zirconium and hafnium tetrachlorides with phosphorus oxychloride

    International Nuclear Information System (INIS)

    Snyder, T.S.; Stoltz, R.A.

    1989-01-01

    This patent describes an improvement in a method for separating hafnium chloride from zirconium chloride using a distillation column, with a hafnium chloride enriched vapor stream taken from the top of the column and a zirconium enriched chloride stream taken from the bottom of the column. The improvement comprising: purifying the zirconium-hafnium chloride in a molten salt purification vessel prior to or after introduction into the distillation column to substantially eliminate iron chloride from the zirconium-hafnium chloride by at least periodically removing iron chloride from the molten salt purification vessel by electrochemically plating iron onto an electrode in the molten salt purification vessel. The molten salt in the molten salt purification vessel consisting essentially of a mixture of chlorides selected from the group consisting of alkali metals, alkaline earth metals, zirconium, hafnium, aluminum, manganese, and zinc

  10. 9 CFR 166.2 - General restrictions.

    Science.gov (United States)

    2010-01-01

    ... of any of the following: Processed products; rendered products; bakery waste; candy waste; eggs... 9 Animals and Animal Products 1 2010-01-01 2010-01-01 false General restrictions. 166.2 Section 166.2 Animals and Animal Products ANIMAL AND PLANT HEALTH INSPECTION SERVICE, DEPARTMENT OF...

  11. Properties of neutron-rich hafnium high-spin isomers

    CERN Multimedia

    Tungate, G; Walker, P M; Neyens, G; Billowes, J; Flanagan, K; Koester, U H; Litvinov, Y

    It is proposed to study highly-excited multi-quasiparticle isomers in neutron-rich hafnium (Z=72) isotopes. Long half-lives have already been measured for such isomers in the storage ring at GSI, ensuring their accessibility with ISOL production. The present proposal focuses on:\\\\ (i) an on-line experiment to measure isomer properties in $^{183}$Hf and $^{184}$Hf, and\\\\ (ii) an off-line molecular breakup test using REXTRAP, to provide Hf$^{+}$ beams for future laser spectroscopy and greater sensitivity for the future study of more neutron-rich isotopes.

  12. Studies on Optical and Electrical Properties of Hafnium Oxide Nanoparticles

    Science.gov (United States)

    Jayaraman, Venkatachalam; Sagadevan, Suresh; Sudhakar, Rajesh

    2017-07-01

    In this paper, the synthesis and physico-chemical properties of hafnium oxide nanoparticles (HfO2 NPs) are analyzed and reported. The synthesis was carried out by the precipitation route by using hafnium tetrachloride (HfCl4) as precursor material with potassium hydroxide (KOH) dissolved in Millipore water. In the precipitation technique, the chemical reaction is comparatively simple, low-cost and non-toxic compared to other synthetic methods. The synthesized HfO2 NPs were characterized by using powder x-ray diffraction (PXRD), ultraviolet-visible (UV-Vis) spectroscopy, Raman analysis, and high-resolution transmission electron microscopy (HRTEM). The monoclinic structure of the HfO2 NPs was resolved utilizing x-ray diffraction (XRD). The optical properties were studied from the UV-Vis absorption spectrum. The optical band gap of the HfO2NPs was observed to be 5.1 eV. The Raman spectrum shows the presence of HfO2 NPs. The HRTEM image showed that the HfO2 NPs were of spherical shape with an average particle size of around 28 nm. The energy-dispersive x-ray spectroscopy (EDS) spectrum obviously demonstrated the presence of HfO2 NPs. Analysis and studies on the dielectric properties of the HfO2 NPs such as the dielectric constant, the dielectric loss, and alternating current (AC) conductivity were carried out at varying frequencies and temperatures.

  13. Corrosion potentials of hafnium in molten alkaline-earth metal chlorides

    International Nuclear Information System (INIS)

    Kovalik, O.Yu.; Tkhaj, V.D.

    2000-01-01

    Corrosion potentials of hafnium in molten calcium, strontium and barium chlorides are measured and their temperature dependences are determined. It is stated that the corrosion potential of hafnium becomes more electropositive with an increase of the environment temperature. If the temperature is the same the potential shifts to the interval of more electronegative values in the row of CaCl 2 , SrCl 2 , BaCl 2 which corresponds to a lesser corrosion rate in environments positioned from left to right. the comparison of hafnium corrosion potentials with previously measured values for titanium and zirconium shows that a metal activity decrease results in a more electronegative corrosion potential [ru

  14. Hafnium-Based Contrast Agents for X-ray Computed Tomography.

    Science.gov (United States)

    Berger, Markus; Bauser, Marcus; Frenzel, Thomas; Hilger, Christoph Stephan; Jost, Gregor; Lauria, Silvia; Morgenstern, Bernd; Neis, Christian; Pietsch, Hubertus; Sülzle, Detlev; Hegetschweiler, Kaspar

    2017-05-15

    Heavy-metal-based contrast agents (CAs) offer enhanced X-ray absorption for X-ray computed tomography (CT) compared to the currently used iodinated CAs. We report the discovery of new lanthanide and hafnium azainositol complexes and their optimization with respect to high water solubility and stability. Our efforts culminated in the synthesis of BAY-576, an uncharged hafnium complex with 3:2 stoichiometry and broken complex symmetry. The superior properties of this asymmetrically substituted hafnium CA were demonstrated by a CT angiography study in rabbits that revealed excellent signal contrast enhancement.

  15. Solvent extraction of zirconium and hafnium using MIBK-HSCN-HCL process

    International Nuclear Information System (INIS)

    Borges, J.A.L.; Cunha, O.G.C. da

    1985-01-01

    The separation process of zirconium and hafnium, using MIBK as extractant in a set of mixer-settler is described. The chemical analysis was done by X-ray fluorescence and emission spectrography. (Author) [pt

  16. Hafnium as a prospective absorber for VVER-1000 reactors of Ukraine

    International Nuclear Information System (INIS)

    Afanas'ev, A.A.; Konotop, Yu.F.; Odejchuk, N.L.

    2000-01-01

    Nuclear-physical parameters of hafnium having in mind its use as an absorber, are considered. Technical aspects of Hf production are exposed. Use of B 4 C/Hf absorber is twice cheaper than a standard one

  17. Spectrofluorimetric determination of hafnium and zirconium with 3,7-dihydroxyflavone

    Energy Technology Data Exchange (ETDEWEB)

    Ito, Takushi; Suzuki, Osamu; Seuzuki, Tetsuo; Murata, Akira

    1986-04-01

    The absorptive and fluorescent characteristics of the hafnium and zirconium complexes of 3-hydroxyflavone and its 12 hydroxy and methoxy derivatives have been studied. The fluorescence of the 1:1 hafnium - 3,7-dihydroxyflavone complex (lambdasub(ex.)397 nm,lambdasub(em.) 465 nm) in 3 M hydrochloric acid has been used to determine 2-40 ng ml/sup -1/ of hafnium. The fluorescence of the 1:1 zirconium - 3,7-dihydroxyflavone complex (lambdasub(ex.) 395 nm, lambda sub(em.) 465 nm) at pH 2.0 in 0.02 M sulphate solution has been used to determine 2-40 ng ml/sup -1/ of zirconium. These methods are very sensitive and can be used for the simultaneous determination of hafnium and zirconium with an error of about 5%.

  18. Electronic structure of pentacene on hafnium studied by ultraviolet photoelectron spectroscopy

    International Nuclear Information System (INIS)

    Kang, Seong Jun; Yi, Yeon Jin; Kim, Chung Yi; Whang, Chung Nam

    2005-01-01

    The electronic structure of pentacene on hafnium, which is a low work function metal, was analyzed by using ultraviolet photoelectron spectroscopy. The energy level alignment was studied by using the onset of the highest occupied molecular orbital level and the shift of the vacuum level of the pentacene layer, which was deposited on a clean hafnium surface in a stepwise manner. The measured onset of the highest occupied molecular orbital energy level was 1.52 eV from the Fermi level of hafnium. The vacuum level was shifted 0.28 eV toward higher binding energy with additional pentacene layers, which means an interfacial dipole exists at the interface between pentacene and hafnium. We confirm that a small electron injection barrier can be achieved by inserting a low work function metal in a pentacene thin-film transistor.

  19. Compositional characterization of hafnium alloy used as control rod material in nuclear reactor

    International Nuclear Information System (INIS)

    Sharma, P.K.; Bassan, M.K.T.; Avhad, D.K.; Singhal, R.K.

    2014-01-01

    Hafnium (Hf) is a heavy, steel-gray metal in the reactive metals group that is very closely related to zirconium (Zr) and forms a continuous solid-solution at all concentrations of zirconium and hafnium. Hafnium occurs naturally with zirconium at a ratio of approximately 1:50 and is produced exclusively as a co-product of nuclear-grade zirconium. It is used in a variety of applications where few substitutes are available. Thus with its relatively high thermal neutron absorption cross-section, hafnium's biggest application is as control rod material in nuclear reactors. During this work, major (Zirconium (Zr), Cobalt (Co) and Molybdenum (Mo)) and trace ((Iron (Fe), Nickel (Ni) and Titanium (Ti)) elements were measured in the bulk matrices of Hf. These materials are also associated with other impurities such as O, N, H etc.

  20. Evaluation of thermodynamic data on zirconium and hafnium halides and oxyhalides by means of transport experiments

    International Nuclear Information System (INIS)

    Dittmer, G.; Niemann, U.

    1987-01-01

    A consistent set of thermodynamic data for zirconium and hafnium halides, oxides and oxyhalides was achieved. It was found that formation enthalpies of gaseous compounds could be derived from solubility measurements together with theoretical estimations and a revision of literature data. Free energy functions were calculated employing statistical mechanics. Data for liquid and solid compounds were obtained via sublimation and vaporization data. Chemical equilibria of zirconium and hafnium with halogens are discussed. 51 refs.; 16 figs.; 14 tabs

  1. Investigation of chlorination of zirconium and hafnium and their compounds in discharge from hollow cathode

    International Nuclear Information System (INIS)

    Ioffe, R.B.; Korovin, Yu.I.

    1978-01-01

    The possibility is investigated of chlorinating various zirconium and hafnium compounds (metal, oxide, carbide) in a hot discharge from a hollow cathode with various chlorinating reagents: copper monochloride, nickel chloride, magnesium chloride, for the purpose of accelerating their entrance into the excitation zone. It has been shown thermodynamically and experimentally that chlorination of metal zirconium and hafnium and their carbides with copper monochloride in hot hollow cathode conditions provides a sharp increase in the intensity of the lines of these elements

  2. Knight shift in scandium and its alloys with hafnium and titanium

    International Nuclear Information System (INIS)

    Chachkhiani, Z.B.; Chechernikov, V.I.; Martynova, L.F.; Nidel'ko, V.I.; Chachkhiani, L.G.; Georgadze, G.S.

    1981-01-01

    Results of the investigation of NMR on 45 Sc nuclei and magnetic susceptibility of scandium and its solid solutions with titanium and hafnium are presented. It is shown that the existing hybridization of S and d zones in pure scandium and its alloys with titanium and hafnium affects the Knight shift reducing the value of the contact contribution. The temperature behaviour of the Knight shift from the temperature dependence and spin susceptibility of collectivized d electrons [ru

  3. Application of hafnium hydride control rod to large sodium cooled fast breeder reactor

    Energy Technology Data Exchange (ETDEWEB)

    Ikeda, Kazumi, E-mail: kazumi_ikeda@mfbr.mhi.co.jp [Mitsubishi FBR Systems, Inc., 34-17, Jingumae 2-Chome, Shibuya-ku, Tokyo 150-0001 (Japan); Moriwaki, Hiroyuki, E-mail: hiroyuki_moriwaki@mfbr.mhi.co.jp [Mitsubishi FBR Systems, Inc., 34-17, Jingumae 2-Chome, Shibuya-ku, Tokyo 150-0001 (Japan); Ohkubo, Yoshiyuki, E-mail: yoshiyuki_okubo@mfbr.mhi.co.jp [Mitsubishi FBR Systems, Inc., 34-17, Jingumae 2-Chome, Shibuya-ku, Tokyo 150-0001 (Japan); Iwasaki, Tomohiko, E-mail: tomohiko.iwasaki@qse.tohoku.ac.jp [Department of Quantum Science and Energy Engineering, Tohoku University, Aoba, Aramaki, Aoba-ku, Sendai-shi, Miyagi-ken 980-8579 (Japan); Konashi, Kenji, E-mail: konashi@imr.tohoku.ac.jp [Institute for Materials Research, Tohoku University, Narita-cho, Oarai-machi, Higashi-Ibaraki-gun, Ibaraki-ken 311-1313 (Japan)

    2014-10-15

    Highlights: • Application of hafnium hydride control rod to large sodium cooled fast breeder reactor. • This paper treats application of an innovative hafnium hydride control rod to a large sodium cooled fast breeder reactor. • Hydrogen absorption triples the reactivity worth by neutron spectrum shift at H/Hf ratio of 1.3. • Lifetime of the control rod quadruples because produced daughters of hafnium isotopes are absorbers. • Nuclear and thermal hydraulic characteristics of the reactor are as good as or better than B-10 enriched boron carbide. - Abstract: This study treats the feasibility of long-lived hafnium hydride control rod in a large sodium-cooled fast breeder reactor by nuclear and thermal analyses. According to the nuclear calculations, it is found that hydrogen absorption of hafnium triples the reactivity by the neutron spectrum shift at the H/Hf ratio of 1.3, and a hafnium transmutation mechanism that produced daughters are absorbers quadruples the lifetime due to a low incineration rate of absorbing nuclides under irradiation. That is to say, the control rod can function well for a long time because an irradiation of 2400 EFPD reduces the reactivity by only 4%. The calculation also reveals that the hafnium hydride control rod can apply to the reactor in that nuclear and thermal characteristics become as good as or better than 80% B-10 enriched boron carbide. For example, the maximum linear heat rate becomes 3% lower. Owing to the better power distribution, the required flow rate decreases approximately by 1%. Consequently, it is concluded on desk analyses that the long lived hafnium hydride control rod is feasible in the large sodium-cooled fast breeder reactor.

  4. Dielectric response and ac conductivity analysis of hafnium oxide nanopowder

    International Nuclear Information System (INIS)

    Karahaliou, P K; Xanthopoulos, N; Krontiras, C A; Georga, S N

    2012-01-01

    The dielectric response of hafnium oxide nanopowder was studied in the frequency range of 10 -2 -10 6 MHz and in the temperature range of 20-180 °C. Broadband dielectric spectroscopy was applied and the experimental results were analyzed and discussed using the electric modulus (M*) and alternating current (ac) conductivity formalisms. The analyses of the dc conductivity and electric modulus data revealed the presence of mechanisms which are thermally activated, both with almost the same activation energy of 1.01 eV. A fitting procedure involving the superposition of the thermally activated dc conductivity, the universal dielectric responce and the near constant loss terms has been used to describe the frequency evolution of the real part of the specific electrical conductivity. The conductivity master curve was obtained, suggesting that the time-temperature superposition principle applies for the studied system, thus implying that the conductivity mechanisms are temperature independent.

  5. Amorphous Hafnium-Indium-Zinc Oxide Semiconductor Thin Film Transistors

    Directory of Open Access Journals (Sweden)

    Sheng-Po Chang

    2012-01-01

    Full Text Available We reported on the performance and electrical properties of co-sputtering-processed amorphous hafnium-indium-zinc oxide (α-HfIZO thin film transistors (TFTs. Co-sputtering-processed α-HfIZO thin films have shown an amorphous phase in nature. We could modulate the In, Hf, and Zn components by changing the co-sputtering power. Additionally, the chemical composition of α-HfIZO had a significant effect on reliability, hysteresis, field-effect mobility (μFE, carrier concentration, and subthreshold swing (S of the device. Our results indicated that we could successfully and easily fabricate α-HfIZO TFTs with excellent performance by the co-sputtering process. Co-sputtering-processed α-HfIZO TFTs were fabricated with an on/off current ratio of ~106, higher mobility, and a subthreshold slope as steep as 0.55 V/dec.

  6. Determination of hafnium with the inductively coupled plasma (ICP)

    International Nuclear Information System (INIS)

    Wuensch, G.; Pose, K.

    1985-01-01

    The relative intensities of 198 hafnium lines in the Ar-ICP are listed. Spectral interference tables are given for the 9 analytically best lines, covering the range of +-60 pm around the Hf-lines. They include measured (not calculated) data of the interferent equivalent concentrations (IEC) and the critical concentration ratios (CCR) for 115 lines of all 34 possibly interfering elements. In many cases, these IEC- or CCR-data differ by 1 or 2 orders of magnitude from those calculated from intensities observed in the NBS-copper arc. Since no intense Hf-line is free from spectral interferences, examples are given for the calculation of the most suitable line for a known matrix. (orig.) [de

  7. Separation of zirconium--hafnium by nitride precipitation

    International Nuclear Information System (INIS)

    Anderson, R.N.; Parlee, N.A.

    1977-01-01

    A method is described for the separation of a light reactive metal (e.g., zirconium) from a heavy reactive metal (e.g., hafnium) by forming insoluble nitrides of the metals in a molten metal solvent (e.g., copper) inert to nitrogen and having a suitable density for the light metal nitride to form a separate phase in the upper portion of the solvent and for the heavy metal nitride to form a separate phase in the lower portion of the solvent. Nitriding is performed by maintaining a nitrogen-containing atmosphere over the bath. The light and heavy metals may be an oxide mixture and carbothermically reduced to metal form in the same bath used for nitriding. The nitrides are then separately removed and decomposed to form the desired separate metals. 16 claims, 1 figure

  8. Systematic investigation of electromagnetic properties of all stable hafnium isotopes

    International Nuclear Information System (INIS)

    Napiorkowski, T.J.; Choinski, J.; Czosnyka, T.; Iwanicki, J.; Kownacki, J.; Zemlo, L.; Srebrny, J.; Starosta, K.; Boer, J. de.; Gollwitzer, A.; Loewe, M.; Wuerkner, M.; Guenther, C.; Weber, T.; Hagemann, G.; Sletten, G.

    1996-01-01

    In a systematic investigation of the electromagnetic structure of hafnium stable isotopes enriched targets of 176, 177, 178, 179, 180 Hf were Coulomb exciting using: 67 MeV 19 F beam from NBITAL FN Tandem, 125 MeV 32 S beam from MP Tandem in Accelerator Laboratory LMU and TU Munich, 225 MeV 58 Ni beam from NBITAL FN Tandem plus 2 Liniac Boosters complex. Scattered particle-gamma as well as p-γ-γ coincidence were registered. A further simultaneous analysis of Coulomb excitation cross section as a function of scattering angle of 19 F, 32 S, 58 Ni projectiles should be sufficient to deduce reduced probabilities of E2 transitions in ground state band

  9. Synthesis and characterization of hafnium oxide for luminescent applications

    International Nuclear Information System (INIS)

    Guzman Mendoza, J.; Aguilar Frutis, M.A.; Flores, G. Alarcon; Garcia Hipolito, M.; Azorin Nieto, J.; Rivera Montalvo, T.; Falcony, C.

    2008-01-01

    Full text: Hafnium oxide (HfO 2 ) is a material with a wide range of possible technological applications because it's chemical and physical properties such as high melting point, high chemical stability, high refraction index, high dielectric constant and hardness near to diamond in the tetragonal phase. The large energy gap and low phonon frequencies of the HfO 2 makes it appropriate as a host matrix for been doped with rare earth activators. Efficient luminescent materials find wide application in electroluminescent flat panel displays; color plasma displays panels, scintillators, cathode ray tubes, fluorescent lamps, lasers, etc. In recent years the study of luminescent materials based on HfO 2 has been intensified. Some groups have studied the optical properties of doped and undoped HfO 2 . In this contribution, Hafnium Oxide (HfO 2 ) films were prepared using the spray pyrolysis deposition technique. The material was synthesized using chlorides as raw materials in deionised water as solvent and deposited on Corning glass substrates at temperatures from 300 deg C to 600 deg C. For substrate temperatures lower than 400 deg C, the deposited films are amorphous, while for substrate temperatures higher than 450 deg C, the monoclinic phase of HfO 2 appears. Scanning electron microscopy with microprobe analysis was use to observe the microstructure and obtain the chemical composition of the films; rough surfaces with spherical particles were appreciated. UV and low energy X Ray radiations were used in order to achieve the thermoluminescent characterization of the films as a function of the deposition temperature

  10. 36 CFR 13.166 - Temporary facilities.

    Science.gov (United States)

    2010-07-01

    ... 36 Parks, Forests, and Public Property 1 2010-07-01 2010-07-01 false Temporary facilities. 13.166... facilities. A temporary facility or structure directly and necessarily related to the taking of subsistence... facilities which shall be published annually in accordance with § 1.7 of this chapter. ...

  11. Estimation of human absorbed dose for (166)Ho-PAM: comparison with (166)Ho-DOTMP and (166)Ho-TTHMP.

    Science.gov (United States)

    Vaez-Tehrani, Mahdokht; Zolghadri, Samaneh; Yousefnia, Hassan; Afarideh, Hossein

    2016-10-01

    In this study, the human absorbed dose of holmium-166 ((166)Ho)-pamidronate (PAM) as a potential agent for the management of multiple myeloma was estimated. (166)Ho-PAM complex was prepared at optimized conditions and injected into the rats. The equivalent and effective absorbed doses to human organs after injection of the complex were estimated by radiation-absorbed dose assessment resource and methods proposed by Sparks et al based on rat data. The red marrow to other organ absorbed dose ratios were compared with these data for (166)Ho-DOTMP, as the only clinically used (166)Ho bone marrow ablative agent, and (166)Ho-TTHMP. The highest absorbed dose amounts are observed in the bone surface and bone marrow with 1.11 and 0.903 mGy MBq(-1), respectively. Most other organs would receive approximately insignificant absorbed dose. While (166)Ho-PAM demonstrated a higher red marrow to total body absorbed dose ratio than (166)Ho-1,4,7,10-tetraazacyclo dodecane-1,4,7,10 tetra ethylene phosphonic acid (DOTMP) and (166)Ho-triethylene tetramine hexa (methylene phosphonic acid) (TTHMP), the red marrow to most organ absorbed dose ratios for (166)Ho-TTHMP and (166)Ho-PAM are much higher than the ratios for (166)Ho-DOTMP. The result showed that (166)Ho-PAM has significant characteristics than (166)Ho-DOTMP and therefore, this complex can be considered as a good agent for bone marrow ablative therapy. In this work, two separate points have been investigated: (1) human absorbed dose of (166)Ho-PAM, as a potential bone marrow ablative agent, has been estimated; and (2) the complex has been compared with (166)Ho-DOTMP, as the only clinically used bone marrow ablative radiopharmaceutical, showing significant characteristics.

  12. Investigation of complexes with bone affinity using the In vivo generator system 166 Dy/166 Ho

    International Nuclear Information System (INIS)

    Pedraza L, M.

    2006-01-01

    The importance of this original research lies in the fact that it has proven that the [ 166 Dy]Dy/ 166 Ho-EDTMP in vivo generator system is a stable complex that can be used as a therapeutic radiopharmaceutical. Multiple myeloma and other hematological malignancies have been treated by myeloablative radiotherapy/chemotherapy and subsequent stem cell transplantation. Bone-seeking radiopharmaceuticals such as 166 Ho-DOTMP or 153 Sm-DTMP, have been proposed for delivering ablative radiation doses to marrow in multiple myeloma and other hematological malignancies or have shown excellent results in palliative bone metastasis pain therapy, respectively. As lanthanides have similar chemical characteristics the phosphonate with bone affinity (EDTMP) labeled with Dy/Ho can be used for marrow ablation while causing minimal irradiation to normal organs. This in vivo generator system has not been previously reported. The aim of this research was to label EDTMP (ethylene diamine tetramethylene phosphonate) with 166 Dy/ 166 Ho; to evaluate the in vitro and in vivo stability of both 166 Dy-EDTMP and 166 Ho-EDTMP complexes when the daughter 166 Ho is formed as a dysprosium decay product; to determine the bone marrow cytotoxic and genotoxic effect in mice and to evaluate, by histopathology, the myeloablative potential of the [ 166 Dy]Dy/ 166 Ho-EDTMP in vivo generator system. 166 Dy was obtained by neutron irradiation of enriched 164 Dy 2 O 3 in a TRIGA Mark III reactor. Labeling was carried out in an aqueous phosphate medium at pH 8.0 by addition of 166 DyCl 3 to EDTMP at a molar ratio 1:1.75, with >99 % radiochemical purity, as determined by thin-layer chromatography (TLC) and high-performance liquid chromatography (HPLC). In vitro studies demonstrated that 166 Dy/ 166 Ho-EDTMP is unstable after dilution in saline but stable in human serum with no translocation of the daughter nucleus subsequent to β decay of 166 Dy, which could release free 166 Ho 3+ . Biodistribution in mice

  13. Labeling of biotin with 166Dy/166Ho as a stable in vivo generator system

    International Nuclear Information System (INIS)

    Ferro-Flores, G.; Monroy-Guzman, F.; Tendilla, J.I.; Garcia-Salinas, L.; Villarreal-Barajas, J.E.; Arteaga-Murphy, C.

    2002-01-01

    Biotin (cis-tetrahydro-2-oxothieno[3,4-d]imidazoline-4-valeric acid) is a 244 Da vitamin found in low concentration in blood and tissue (vitamin H). The aim of this work was to synthesize 166 Dy/ 166 Ho-DTPA-bisBiotin to evaluate its potential as a new radiopharmaceutical for targeted radiotherapy. Dysprosium-166/ holmium-166 chloride was obtained by neutron irradiation of 20 mg of enriched Dy 2 O 3 ( 164 Dy, 99 %, from Oak Ridge NL) in a Triga Mark III reactor at a flux in the central thimble of 3.10 13 n. cm -2 s -1 for 20 h. Following irradiation, the target was allowed to decay for 2 days, then 100 μL of 12 N chloride acid were added and stirred for 1 min. To this solution was added 500 μL of injectable water and the whole was also stirred for 2 min. The average radioactive concentration was 332 MBq/ml. The biotin used in this investigation was covalently conjugated to diethylenetriamine pentaacetic acid (DTPA) through the use of the cyclic anhydride and lysine conjugate to biotin (biocytin) to produce DTPA-α,ω-bis(biocytin amide)(DTPA-bisBiotin). Sterile and apyrogenic V-vial was prepared to contain 2.0 mg (1.9 x 10 -3 mmol) of the DTPA-bisbiotin compound in 1.0 ml of 0.05 M bicarbonate buffer (pH 8.0) and then 20 μL of 166 Dy2Cl3 solution were added to the preparation. Thin Layer Chromatography aluminum cellulose sheets were utilised as the stationary phase and a ternary mixture of methanol:water:ammonium hydroxide (20:40:2) as the mobile phase. 166 Dy/ 166 Ho-DTPA-bisBiotin travelled with the solvent front R f 0.9-1.0 and the Dy +3 /Ho +3 species remained at the origin (R f = 0). The biological integrity of labelled biotin was achieved evaluating its avidity for avidin in an agarose column. Stability studies against dilution were carried out by diluting the radiocomplex solution with saline and with human serum at 310 K. After 10 min and 24 h the radiochemical purity of each 166 Dy/ 166 Ho complex solution was determined by TLC. The complex 166 Dy/ 166

  14. Preparation of 166 Dy/166 Ho-Macro aggregates as an In vivo generator system for the treatment of arthrophaties

    International Nuclear Information System (INIS)

    Aldama A, T.K.

    2003-01-01

    The present work reports the obtention of macro aggregates of hydroxides of Dysprosium-166/Holmium-166 ( 166 Dy/ 166 Ho-MH), as a generator system in vivo to be used in the treatment of arthritis rheumatoid. The 166 Dy was obtained by neutron irradiation of 166 DyO 3 (enriched to 98.45%) by 20 h in the TRIGA Mark III Reactor and 50 h of decay, to the oxide of 166 Dy/ 166 Ho formed, it was added HCl 0.12 N to obtain a final volume of 3.5 ml of solution of 166 Dy/ 166 Ho chloride. The solution of 166D yCl 3 solution was obtained with an activity of 3.502 mCi (129 MBq), appropriate for the preparation of the radiopharmaceutical 166 Dy/ 166 Ho-MH. The separation of the 166 Dy from the 166 Ho, was carried out by chromatography in an cation exchange column, gaining an appropriate separation, obtaining a 166 Dy with a radionuclide purity greater than 90%. The 166 Dy/ 166 Ho-MH were prepared by addition to the solution of 166 DyCI 3 NaOH 0.5 N low ultrasonic bath with later centrifugation, decanted and resuspension in saline solution, obtaining a radiopharmaceutical with a generator system 166 Dy/ 166 Ho with particles of size average of 3 μm, in form of 166 Dy / 166 Ho-MH. Under these conditions, it was obtained a radiochemical yield greater than 99%. The microscopic analysis and of filtration showed that the formulation doesn't present particles smaller than to 1 μm, neither greater to 50 μm, which will allow, the quick phagocytosis for the synoviocytes of the synovial membrane, and by consequence, an homogeneous distribution of the radiation dose could exist. The sedimentation velocity for the formulated suspension is of 0.04 cm/min that it will allow the administration of homogeneous activities of the radiopharmaceutical, to the no deposit in the injection devices. The studies of stability in vitro indicate us that inside the articulation, the particles won't probably reduce its size neither their radiochemical purity, for that the flight extra articular will be

  15. Pyroelectricity of silicon-doped hafnium oxide thin films

    Science.gov (United States)

    Jachalke, Sven; Schenk, Tony; Park, Min Hyuk; Schroeder, Uwe; Mikolajick, Thomas; Stöcker, Hartmut; Mehner, Erik; Meyer, Dirk C.

    2018-04-01

    Ferroelectricity in hafnium oxide thin films is known to be induced by various doping elements and in solid-solution with zirconia. While a wealth of studies is focused on their basic ferroelectric properties and memory applications, thorough studies of the related pyroelectric properties and their application potential are only rarely found. This work investigates the impact of Si doping on the phase composition and ferro- as well as pyroelectric properties of thin film capacitors. Dynamic hysteresis measurements and the field-free Sharp-Garn method were used to correlate the reported orthorhombic phase fractions with the remanent polarization and pyroelectric coefficient. Maximum values of 8.21 µC cm-2 and -46.2 µC K-1 m-2 for remanent polarization and pyroelectric coefficient were found for a Si content of 2.0 at%, respectively. Moreover, temperature-dependent measurements reveal nearly constant values for the pyroelectric coefficient and remanent polarization over the temperature range of 0 ° C to 170 ° C , which make the material a promising candidate for IR sensor and energy conversion applications beyond the commonly discussed use in memory applications.

  16. Hafnium oxide nanoparticles: toward an in vitro predictive biological effect?

    International Nuclear Information System (INIS)

    Marill, Julie; Anesary, Naeemunnisa Mohamed; Zhang, Ping; Vivet, Sonia; Borghi, Elsa; Levy, Laurent; Pottier, Agnes

    2014-01-01

    Hafnium oxide, NBTXR3 nanoparticles were designed for high dose energy deposition within cancer cells when exposed to ionizing radiation. The purpose of this study was to assess the possibility of predicting in vitro the biological effect of NBTXR3 nanoparticles when exposed to ionizing radiation. Cellular uptake of NBTXR3 nanoparticles was assessed in a panel of human cancer cell lines (radioresistant and radiosensitive) by transmission electron microscopy. The radioenhancement of NBTXR3 nanoparticles was measured by the clonogenic survival assay. NBTXR3 nanoparticles were taken up by cells in a concentration dependent manner, forming clusters in the cytoplasm. Differential nanoparticle uptake was observed between epithelial and mesenchymal or glioblastoma cell lines. The dose enhancement factor increased with increase NBTXR3 nanoparticle concentration and radiation dose. Beyond a minimum number of clusters per cell, the radioenhancement of NBTXR3 nanoparticles could be estimated from the radiation dose delivered and the radiosensitivity of the cancer cell lines. Our preliminary results suggest a predictable in vitro biological effect of NBTXR3 nanoparticles exposed to ionizing radiation

  17. Studies of high-K isomers in hafnium nuclei

    International Nuclear Information System (INIS)

    Sletten, G.; Gjoerup, N.L.

    1991-01-01

    K-isomeric states built on high-Ω Nilsson orbitals from deformation-aligned high-j levels near the Fermi surface are found to cluster in the neutron rich Hf, W and Os nuclei. It has been shown that some of the high seniority states of this type have decay properties that indicate strong mixing of configurations and that in Osmium nuclei γ-softness cause strong deviations from the well established K-selection rule. Also in the Hafnium nuclei is the expected forbiddenness in isomeric decays an order of magnitude smaller than expected from the K-selection rule. A new 9 quasiparticle isomer has been discovered in 175 Hf at I=57/2. This isomer has the anomalous decay as the dominant mode. Other lower seniority states are also identified. At spin 35/2 and 45/2 the deformation aligned states become yrast, but the structure of the yrast line to even higher spins is not yet understood. (author)

  18. Luminescent determination of zirconium and hafnium with myricetin

    International Nuclear Information System (INIS)

    Talipov, Sh.T.; Zel'tser, L.E.; Morozova, L.A.; Tashkhodzhaev, A.T.

    1978-01-01

    Reaction of formation of 3, 5, 7, 3', 4', 5' - hexaoxiflavone - myricetin complexes with zirconium and hafnium ions has been the basis for development of luminescent method of determining these elements. Optimum conditions for complexing have been determined. For Hf they are : 8-9 HCl concentration, maximum fluorescence wave length (lambda fl.)of 520 nm, wave length of exciting light (lambda el) of 436 nm, for Zr lambda fl = 536nm, lambda el = 436 nm. Stable fluorescence establishes after 25 min. for Zr and after 15 min for Hf in the presence of 40% ethanol. Usage of various camouflage agents has permitted to attain high selectivity of the method. Possibility for determination of Zr with myricetin in the presence of a 10-time excess of Hf, Cr, Cu, 50-time excess of Mo and Ti is shown. Sensitivity of Zr determination is 2.0x10 μg -2 /ml, for Hf it is 9.0x10 μg -3 and mineral waters

  19. Labeling of biotin with Dy-166/Ho-166 as a stable in vivo generator system

    International Nuclear Information System (INIS)

    Ferro-Flores, G.; Monroy-Guzman, F.; Jimenez-Varela, R.; Tendilla, J.I.; Arteaga-Murphy, C.; Pedraza-Lopez, M.

    2002-01-01

    Aim: Biotin is a vitamin found in low concentration in blood and tissue. In radioimmunodiagnosis and radioimmunotherapy practice, the pre-targeting avidin-biotin strategy has shown that target-to-nontarget radioactivity ratios can be significantly improved. In addition, the biotin content of cancerous tumors is higher than that of normal tissue and it has been found in the cellular nucleus due to a specific transfer of biotin to histones by human serum biotinidase. Because of its nuclear properties, the 166 Dy/ 166 Ho radionuclide pair can be considered as an in vivo generator system. The aim of this work was to synthesize 166 Dy/ 166 Ho-DTPA-bisBiotin to evaluate its potential as a new radiopharmaceutical for targeted radiotherapy. Material and Methods: Dysprosium-166/Holmium-166 chloride was obtained by neutron irradiation of 50 mg of 99% enriched 164 Dy 2 O 3 in a TRIGA Mark III reactor at a flux in the central thimble of 3.10 13 n. cm -2 s -1 for 20 h. Following irradiation, the target was allowed to decay for 2 days, 100 μL of 12 N chloride acid were added and the mixture stirred for 3 min. To this suspension 1.0 mL of injectable water were added and heated for 2 min at 90 0 C. The biotin used in this investigation was diethylenetriaminepentaacetic-α,ω-bis(biocytinamide)(DTPA-bisBiotin, Sigma). Sterile and apyrogenic V-vial was prepared to contain 16.0 mg (1.52 x 10 -4 mmol) of the DTPA-bisBiotin in 4.0 mL of 0.05 M bicarbonate buffer (pH 8.5), then 50 μL of the radiochloride solution were added to the preparation. TLC aluminum cellulose sheets were used as the stationary phase and a ternary mixture of methanol: water: ammonium hydroxide (20:40:2) as the mobile phase. 166 Dy/ 166 Ho-DTPA-bisBiotin traveled with the solvent front R f 0.9-1.0 and the Dy +3 /Ho +3 species remained at the origin (R f 0.0). HPLC reverse phase was also used to evaluate radiochemical purity. The biological integrity of labeled biotin was achieved evaluating its avidity for avidin

  20. Composition and microstructure of zirconium and hafnium germanates obtained by different chemical routes

    International Nuclear Information System (INIS)

    Utkin, A.V.; Prokip, V.E.; Baklanova, N.I.

    2014-01-01

    The phase composition and morphology of zirconium and hafnium germanates synthesized by ceramic and co-precipitation routes were studied. The products were characterized using high-temperature X-ray diffraction analysis (XRD), Raman spectroscopy, scanning electron microscopy (SEM) and thermal (TG/DTA) analysis. To investigate the phase composition and stoichiometry of compounds the unit cell parameters were refined by full-profile Rietveld XRD analysis. The morphology of products and its evolution during high-temperature treatment was examined by SEM analysis. It was stated that there is the strong dependence of the phase composition and morphology of products on the preparation route. The ceramic route requires a multi-stage high-temperature treatment to obtain zirconium and hafnium germanates of 95% purity or more. Also, there are strong diffusion limitations to obtain hafnium germanate Hf 3 GeO 8 by ceramic route. On the contrary, the co-precipitation route leads to the formation of nanocrystalline single phase germanates of stoichiometric composition at a relatively low temperatures (less than 1000 °C). The results of quantitative XRD analysis showed the hafnium germanates are stoichiometric compounds in contrast to zirconium germanates that form a set of solid solutions. This distinction may be related to the difference in the ion radii of Zr and Hf. - Graphical abstract: The phase composition and morphology of zirconium and hafnium germanates synthesized by ceramic and co-precipitation routes were studied. It was stated that there is the strong dependence of the phase composition and morphology of products on the preparation route. Display Omitted - Highlights: • Zr and Hf germanates were synthesized by ceramic and co-precipitation routes. • The morphology of products depends on the synthesis parameters. • Zirconium germanates forms a set of solid solutions. • Hafnium germanates are stoichiometric compounds

  1. 17 CFR 166.2 - Authorization to trade.

    Science.gov (United States)

    2010-04-01

    ... 17 Commodity and Securities Exchanges 1 2010-04-01 2010-04-01 false Authorization to trade. 166.2 Section 166.2 Commodity and Securities Exchanges COMMODITY FUTURES TRADING COMMISSION CUSTOMER PROTECTION RULES § 166.2 Authorization to trade. No futures commission merchant, introducing broker or any of their...

  2. 26 CFR 1.166-1 - Bad debts.

    Science.gov (United States)

    2010-04-01

    ... 26 Internal Revenue 2 2010-04-01 2010-04-01 false Bad debts. 1.166-1 Section 1.166-1 Internal... TAXES (CONTINUED) Itemized Deductions for Individuals and Corporations § 1.166-1 Bad debts. (a... shall be allowed in respect of bad debts owed to the taxpayer. For this purpose, bad debts shall...

  3. 26 CFR 1.166-4 - Reserve for bad debts.

    Science.gov (United States)

    2010-04-01

    ... the bad debts reserves of certain mutual savings banks, domestic building and loan associations, and... 26 Internal Revenue 2 2010-04-01 2010-04-01 false Reserve for bad debts. 1.166-4 Section 1.166-4...) INCOME TAXES (CONTINUED) Itemized Deductions for Individuals and Corporations § 1.166-4 Reserve for bad...

  4. 12 CFR 16.6 - Sales of nonconvertible debt.

    Science.gov (United States)

    2010-01-01

    ... 12 Banks and Banking 1 2010-01-01 2010-01-01 false Sales of nonconvertible debt. 16.6 Section 16.6... RULES § 16.6 Sales of nonconvertible debt. (a) The OCC will deem offers or sales of bank issued... grade; (5) Prior to or simultaneously with the sale of the debt, each purchaser receives an offering...

  5. Preparation of 166 Dy/166 Ho DTPA-bis biotin as a system of In vivo generator

    International Nuclear Information System (INIS)

    Jimenez V, M.R.

    2003-01-01

    The objective of this work was to synthesize the complex 166 Dy/ 166 Ho - diethylen triamine pentaacetic-bis Biotin ( 166 Dy/ 166 Ho DTPA-bis Biotin) to evaluate its potential as a new radiopharmaceutical in directed radiotherapy. The Dysprosium-166 was obtained for neutron irradiation of 164 Dy 2 0 3 in the TRIGA Mark III reactor. The labelled was carried out in aqueous solution to p H 8.0 for addition of 166 Dy Cl 3 to the diethylen triamine pentaacetic-α, ω-bis Biotin (DTPA-bis Biotin). The radiochemical purity was determined for HPLC and ITLC. The biological integrity of the marked biotin is evaluated by the biological recognition of the avidin for HPLC - molecular exclusion with and without avidin addition. The studies of stability in vitro were made in dilutions of saline solution to 0.9% and with human serum at 37 C incubated 1 and 24 hours. The complex 166 Dy/ 166 Ho DTPA-bis Biotin was obtained with a radiochemical purity of 99.1 ± 0.6%. The biological recognition of the complex 166 Dy/ 166 Ho DTPA-bis Biotin for the avidin it doesn't affect the labelling procedure. The studies in vitro demonstrated that the 166 Dy/ 166 Ho DTPA-bis Biotin is stable after the dilution in saline solution and in human serum that there is not translocation of the one radionuclide subsequent son to the beta decay of the 166 Dy that could produce the 166 Ho 3+ liberation. The studies of Biodistribution in healthy mice demonstrated that the one complex 166 Dy/ 166 Ho DTPA-bis Biotin have a high renal distribution. In conclusion the radiolabelled biotin in this investigation has the appropriate properties to be used as an In vivo generator system stable for directed radiotherapy. (Author)

  6. Preparation of .sup.166./sup.Ho-Macroaggregates and .sup.166./sup.Ho-Chitosan for the Radiotherapy

    Czech Academy of Sciences Publication Activity Database

    Kropáček, Martin; Melichar, František; Mirzajevová, Marcela

    2002-01-01

    Roč. 29, č. 2 (2002), s. 382 ISSN 1619-7070 R&D Projects: GA MZd NM6828; GA AV ČR KSK4055109 Keywords : Holmium-166 * 166 Ho-macroaggregates * 166 Ho-chitosan Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders

  7. Bond formation in hafnium atom implantation into SiC induced by high-energy electron irradiation

    International Nuclear Information System (INIS)

    Yasuda, H.; Mori, H.; Sakata, T.; Naka, M.; Fujita, H.

    1992-01-01

    Bilayer films of Hf (target atoms)/α-SiC (substrate) were irradiated with 2 MeV electrons in an ultra-high voltage electron microscope (UHVEM), with the electron beam incident on the hafnium layer. As a result of the irradiation, hafnium atoms were implanted into the SiC substrate. Changes in the microstructure and valence electronic states associated with the implantation were studied by a combination of UHVEM and Auger valence electron spectroscopy. The implantation process is summarized as follows. (1) Irradiation with 2 MeV electrons first induces a crystalline-to-amorphous transition in α-SiC. (2) Hafnium atoms which have been knocked-off from the hafnium layer by collision with the 2 MeV electrons are implanted into the resultant amorphous SiC. (3) The implanted hafnium atoms make preferential bonding to carbon atoms. (4) With continued irradiation, the hafnium atoms repeat the displacement along the beam direction and the subsequent bonding with the dangling hybrids of carbon and silicon. The repetition of the displacement and subsequent bonding lead to the deep implantation of hafnium atoms into the SiC substrate. It is concluded that implantation successfully occurs when the bond strength between a constituent atom of a substrate and an injected atom is stronger than that between constituent atoms of a substrate. (Author)

  8. Therapeutical radiopharmaceuticals based In vivo generator system [166 Dy] Dy/166 Ho

    International Nuclear Information System (INIS)

    Ferro F, G.; Garcia S, L.; Monroy G, F.; Tendilla, J.I.; Pedraza L, M.; Murphy, C.A. de

    2002-01-01

    At the idea to administer to a patient a molecule containing in it structure a father radionuclide, with a half life enough large which allows to the radiolabelled molecule to take up position specifically in a white tissue and decaying In vivo to the daughter radionuclide with properties potentially therapeutic, it is known as In vivo generator system. In this work the preparation and the preliminary dosimetric valuations of radiopharmaceuticals based In vivo generator system 166 Dy Dy/ 166 Ho for applications in radioimmunotherapy, in the treatment of the rheumatoid arthritis and in the bone marrow ablation (m.o.) for candidates patients to bone marrow transplant are presented. (Author)

  9. Determination of hafnium, molybdenum, and vanadium in niobium and niobium-based alloys by atomic absorption spectrometry

    International Nuclear Information System (INIS)

    Ide, Kunikazu; Kobayashi, Takeshi; Sudo, Emiko.

    1985-01-01

    The analytical procedure is as follows: Weigh 1 g of a sample and put it into a 100 cm 3 PTFE beaker. Add 5 ml of distilled water and 5 ml of hydrofluoric acid, and then heat the solution on a hot plate, adding 3 ml of nitric acid dropwise. Dilute the solution to 100 cm 3 with distilled water. When hafnium is determined, add 2 g of diammonium titanium hexafluoride ((NH 4 ) 2 TiF 6 )) before dilution. Working standard solutions are prepared by adding the stock standard solutions of hafnium, molybdenum, and vanadium into niobium solutions. When hafnium is determined, add 2 g of (NH 4 ) 2 TiF 6 and the alloying elements in amounts corresponding to those in sample solutions into the working standard solutions. The tolerable amounts of hydrofluoric acid were 2.9 M, 2.1 M, and 3.1 M and those of nitric acid were 1.0 M, 1.6 M, and 1.6 M for hafnium, molybdenum, and vanadium, respectively. It was found that (NH 4 ) 2 TiF 6 greatly increased the sensitivity for hafnium determination. Niobium showed minus effect for hafnium and plus effect for molybdenum and vanadium. The atomic absorption of molybdenum and vanadium were not influenced by the presence of 20 % of each alloying element, while the atomic absorption of hafnium was given plus effect by 20 % of zirconium, iron, cobalt, nickel, manganese, chromium or vanadium and minus effect by 20 % tungsten. The analytical values of hafnium, molybdenum, and vanadium in niobium-based alloys by this method showed a good agreement with those by X-ray fluorescence analysis. The lower limits of determination (S/N=2) were 0.05, 0.001, and 0.002 % and the relative standard deviation were 3, 1, and 1.5 % for hafnium, molybdenum, and vanadium, respectively. (author)

  10. Separation of zirconium and hafnium from acompanying elements by paper chromatography in the systems of alcohol-acid

    International Nuclear Information System (INIS)

    Lebedeva, G.G.; Viktorova, M.E.

    1980-01-01

    Solvents have been chosen and investigated which provide expressed separation of zirconium and hafnium at the analysis of mineral raw materials by paper chromatography. The systems with HNO 3 and HCl containing methyl, ethyl, propyl and butyl alcohols have been studied as mobile phases for separation of zirconium and hafnium. It has been shown that alcohol contents and solvent acidity affect the Rsub(f) value of these elements. The C 2 H 5 OH-5MHCl and C 2 H 5 OH-5MHNO 3 systems are most optimal for pre-concentration of zirconium and hafnium

  11. ENTIRELY AQUEOUS SOLUTION-GEL ROUTE FOR THE PREPARATION OF ZIRCONIUM CARBIDE, HAFNIUM CARBIDE AND THEIR TERNARY CARBIDE POWDERS

    Directory of Open Access Journals (Sweden)

    Zhang Changrui

    2016-07-01

    Full Text Available An entirely aqueous solution-gel route has been developed for the synthesis of zirconium carbide, hafnium carbide and their ternary carbide powders. Zirconium oxychloride (ZrOCl₂.8H₂O, malic acid (MA and ethylene glycol (EG were dissolved in water to form the aqueous zirconium carbide precursor. Afterwards, this aqueous precursor was gelled and transformed into zirconium carbide at a relatively low temperature (1200 °C for achieving an intimate mixing of the intermediate products. Hafnium and the ternary carbide powders were also synthesized via the same aqueous route. All the zirconium, hafnium and ternary carbide powders exhibited a particle size of ∼100 nm.

  12. Plasma spraying of zirconium carbide – hafnium carbide – tungsten cermets

    Czech Academy of Sciences Publication Activity Database

    Brožek, Vlastimil; Ctibor, Pavel; Cheong, D.-I.; Yang, S.-H.

    2009-01-01

    Roč. 9, č. 1 (2009), s. 49-64 ISSN 1335-8987 Institutional research plan: CEZ:AV0Z20430508 Keywords : Plasma spraying * cermet coatings * microhardness * zirconium carbide * hafnium carbide * tungsten * water stabilized plasma Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass

  13. Titanium, zirconium- and hafnium containing initiators in the polymerization of acrylic monomers to ''living'' polymers

    International Nuclear Information System (INIS)

    Farnham, W.B.; Hertler, W.R.

    1988-01-01

    This patent describes a process for preparing ''living'' polymer. The process comprises contacting one or more acrylic monomers under polymerizing conditions with a polymerization-initiating amount of a tetra-coordinate organotitanium, organozirconium or organo-hafnium polymerization initiator, and ''living'' polymers produced thereby

  14. Vapor pressure, heat capacities, and phase transitions of tetrakis(tert-butoxy)hafnium

    Czech Academy of Sciences Publication Activity Database

    Fulem, Michal; Růžička, K.

    2011-01-01

    Roč. 311, Dec. (2011), s. 25-29 ISSN 0378-3812 Institutional research plan: CEZ:AV0Z10100521 Keywords : tetrakis(tert-butoxy)hafnium * MO precursor * vapor pressure * heat capacity * vaporization enthalpy * enthalpy of fusion Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 2.139, year: 2011

  15. Separation of hafnium from zirconium in sulfuric acid solutions using pressurized ion exchange

    International Nuclear Information System (INIS)

    Hurst, F.J.

    1981-01-01

    High-resolution pressurized ion exchange has been used successfully to study and separate hafnium and zirconium sulfate complexes by chromatographic elution from Dowex 50W-X8 (15 to 25 μm) resin with sulfuric acid solutions. Techniques were developed to continuously monitor the column effluents for zirconium and hafnium by reaction with fluorometric and colorimetric reagents. Since neither reagent was specific for either metal ion, peak patterns were initially identified by using the stable isotopes 90 Zr and 180 Hf as fingerprints of their elution position. Distribution ratios for both zirconium and hafnium decrease as the inverse fourth power of the sulfuric acid concentration below 2N and as the inverse second power at higher acid concentration. The hafnium-to-zirconium separation factor is approximately constant (approx. 8) over the 0.5 to 3N range. Under certain conditions, an unseparated fraction was observed that was not retained by the resin. The amount of this fraction which is thought to be a polymeric hydrolysis product appears to be a function of metal and sulfuric acid concentrations. Conditions are being sought to give the highest zirconium concentration and the lowest acid concentration that can be used as a feed material for commercial scale-up in the continuous annular chromatographic (CAC) unit without formation of the polymer

  16. The corrosion behavior of hafnium in high-temperature-water environments

    Energy Technology Data Exchange (ETDEWEB)

    Rishel, D.M.; Smee, J.D.; Kammenzind, B.F.

    1999-10-01

    The high-temperature-water corrosion performance of hafnium is evaluated. Corrosion kinetic data are used to develop correlations that are a function of time and temperature. The evaluation is based on corrosion tests conducted in out-of-pile autoclaves and in out-of-flux locations of the Advanced Test Reactor (ATR) at temperatures ranging from 288 to 360 C. Similar to the corrosion behavior of unalloyed zirconium, the high-temperature-water corrosion response of hafnium exhibits three corrosion regimes: pretransition, posttransition, and spalling. In the pretransition regime, cubic corrosion kinetics are exhibited, whereas in the posttransition regime, linear corrosion kinetics are exhibited. Because of the scatter in the spalling regime data, it is not reasonable to use a best fit of the data to describe spalling regime corrosion. Data also show that neutron irradiation does not alter the corrosion performance of hafnium. Finally, the data illustrate that the corrosion rate of hafnium is significantly less than that of Zircaloy-2 and Zircaloy-4.

  17. Preparation of {sup 166} Dy/{sup 166} Ho DTPA-bis biotin as a system of In vivo generator; Preparacion de {sup 166} Dy/{sup 166} Ho DTPA-bis biotina como un sistema de generador In vivo

    Energy Technology Data Exchange (ETDEWEB)

    Jimenez V, M.R

    2003-07-01

    The objective of this work was to synthesize the complex {sup 166} Dy/{sup 166} Ho - diethylen triamine pentaacetic-bis Biotin ({sup 166} Dy/{sup 166} Ho DTPA-bis Biotin) to evaluate its potential as a new radiopharmaceutical in directed radiotherapy. The Dysprosium-166 was obtained for neutron irradiation of {sup 164} Dy{sub 2}0{sub 3} in the TRIGA Mark III reactor. The labelled was carried out in aqueous solution to p H 8.0 for addition of {sup 166} Dy Cl{sub 3} to the diethylen triamine pentaacetic-{alpha}, {omega}-bis Biotin (DTPA-bis Biotin). The radiochemical purity was determined for HPLC and ITLC. The biological integrity of the marked biotin is evaluated by the biological recognition of the avidin for HPLC - molecular exclusion with and without avidin addition. The studies of stability in vitro were made in dilutions of saline solution to 0.9% and with human serum at 37 C incubated 1 and 24 hours. The complex {sup 166} Dy/{sup 166} Ho DTPA-bis Biotin was obtained with a radiochemical purity of 99.1 {+-} 0.6%. The biological recognition of the complex {sup 166} Dy/{sup 166} Ho DTPA-bis Biotin for the avidin it doesn't affect the labelling procedure. The studies in vitro demonstrated that the {sup 166} Dy/{sup 166} Ho DTPA-bis Biotin is stable after the dilution in saline solution and in human serum that there is not translocation of the one radionuclide subsequent son to the beta decay of the {sup 166} Dy that could produce the {sup 166} Ho{sup 3+} liberation. The studies of Biodistribution in healthy mice demonstrated that the one complex {sup 166} Dy/{sup 166} Ho DTPA-bis Biotin have a high renal distribution. In conclusion the radiolabelled biotin in this investigation has the appropriate properties to be used as an In vivo generator system stable for directed radiotherapy. (Author)

  18. Preparation of {sup 166} Dy/{sup 166} Ho DTPA-bis biotin as a system of In vivo generator; Preparacion de {sup 166} Dy/{sup 166} Ho DTPA-bis biotina como un sistema de generador In vivo

    Energy Technology Data Exchange (ETDEWEB)

    Jimenez V, M R

    2003-07-01

    The objective of this work was to synthesize the complex {sup 166} Dy/{sup 166} Ho - diethylen triamine pentaacetic-bis Biotin ({sup 166} Dy/{sup 166} Ho DTPA-bis Biotin) to evaluate its potential as a new radiopharmaceutical in directed radiotherapy. The Dysprosium-166 was obtained for neutron irradiation of {sup 164} Dy{sub 2}0{sub 3} in the TRIGA Mark III reactor. The labelled was carried out in aqueous solution to p H 8.0 for addition of {sup 166} Dy Cl{sub 3} to the diethylen triamine pentaacetic-{alpha}, {omega}-bis Biotin (DTPA-bis Biotin). The radiochemical purity was determined for HPLC and ITLC. The biological integrity of the marked biotin is evaluated by the biological recognition of the avidin for HPLC - molecular exclusion with and without avidin addition. The studies of stability in vitro were made in dilutions of saline solution to 0.9% and with human serum at 37 C incubated 1 and 24 hours. The complex {sup 166} Dy/{sup 166} Ho DTPA-bis Biotin was obtained with a radiochemical purity of 99.1 {+-} 0.6%. The biological recognition of the complex {sup 166} Dy/{sup 166} Ho DTPA-bis Biotin for the avidin it doesn't affect the labelling procedure. The studies in vitro demonstrated that the {sup 166} Dy/{sup 166} Ho DTPA-bis Biotin is stable after the dilution in saline solution and in human serum that there is not translocation of the one radionuclide subsequent son to the beta decay of the {sup 166} Dy that could produce the {sup 166} Ho{sup 3+} liberation. The studies of Biodistribution in healthy mice demonstrated that the one complex {sup 166} Dy/{sup 166} Ho DTPA-bis Biotin have a high renal distribution. In conclusion the radiolabelled biotin in this investigation has the appropriate properties to be used as an In vivo generator system stable for directed radiotherapy. (Author)

  19. Reinforcement against crack propagation of PWR absorbers by development of boron-carbon-hafnium composites

    International Nuclear Information System (INIS)

    Provot, B.; Herter, P.

    2000-01-01

    In order to improve the mechanical behaviour of materials used as neutron absorbers in nuclear reactors, we have developed CERCER or CERMET composites with boron and hafnium. Thus a new composite B 4 C/HfB 2 has been especially studied. We have identified three kinds of degradation under irradiation (thermal gradient, swelling due to fission products and accidental corrosion) that induce imposed deformations cracking phenomena. Mechanical behaviour and crack propagation resistance have been studied by ball-on-three-balls and double torsion tests. A special device was developed to enable crack propagation and associated stress intensity factor measurements. Effects of structure and of a second phase are underline. First results show that these materials present crack initiation and propagation resistance much higher than pure boron carbide or hafnium diboride. We observe R-Curves effects, crack bridging or branching, crack arrests, and toughness increases that we can relate respectively to the composite structures. (author)

  20. Synthesis and characterization of hafnium oxide films for thermo and photoluminescence applications

    International Nuclear Information System (INIS)

    Guzman Mendoza, J.; Aguilar Frutis, M.A.; Flores, G. Alarcon; Garcia Hipolito, M.; Maciel Cerda, A.; Azorin Nieto, J.; Rivera Montalvo, T.; Falcony, C.

    2010-01-01

    Hafnium oxide (HfO 2 ) films were deposited by the ultrasonic spray pyrolysis process. The films were synthesized from hafnium chloride as raw material in deionized water as solvent and were deposited on corning glass substrates at temperatures from 300 to 600 deg. C. For substrate temperatures lower than 400 deg. C the deposited films were amorphous, while for substrate temperatures higher than 450 deg. C, the monoclinic phase of HfO 2 appeared. Scanning electron microscopy showed that the film's surface resulted rough with semi-spherical promontories. The films showed a chemical composition close to HfO 2 , with an Hf/O ratio of about 0.5. UV radiation was used in order to achieve the thermoluminescent characterization of the films; the 240 nm wavelength induced the best response. In addition, preliminary photoluminescence spectra, as a function of the deposition temperatures, are shown.

  1. Synthesis and characterization of Ho3+ doped hafnium oxide TLD for radiation dosimeter

    International Nuclear Information System (INIS)

    Sekar, Nandakumar; Ganesan, Bharanidharan; Sahib, Hajee Reyaz Ali; Aruna, Prakasarao; Ganesan, Singaravelu; Thamilkumar, P.; Rai, R.R.

    2017-01-01

    Cancer is a dreaded disease which is treated by Radiotherapy, Chemotherapy and Surgery. Radiotherapy plays a vital role in treatment of cancer and recently measurements of invivo radiation dosimetric in patient is of great interest due to high dose gradients in advanced technology like IMRT, IGRT etc. Hence, for the last few decades, a great degree of interest has been shown for the hafnium oxide for radiation dosimetric applications, due to its high dielectric constant, wide band gap and better interface properties such as chemical stability, conduction band offset and thermodynamic stability. In the present study, Synthesis and characterization of Ho 3+ doped Hafnium oxide were carried out and its applications towards radiation dosimeter were investigated

  2. Self-cleaning and surface chemical reactions during hafnium dioxide atomic layer deposition on indium arsenide.

    Science.gov (United States)

    Timm, Rainer; Head, Ashley R; Yngman, Sofie; Knutsson, Johan V; Hjort, Martin; McKibbin, Sarah R; Troian, Andrea; Persson, Olof; Urpelainen, Samuli; Knudsen, Jan; Schnadt, Joachim; Mikkelsen, Anders

    2018-04-12

    Atomic layer deposition (ALD) enables the ultrathin high-quality oxide layers that are central to all modern metal-oxide-semiconductor circuits. Crucial to achieving superior device performance are the chemical reactions during the first deposition cycle, which could ultimately result in atomic-scale perfection of the semiconductor-oxide interface. Here, we directly observe the chemical reactions at the surface during the first cycle of hafnium dioxide deposition on indium arsenide under realistic synthesis conditions using photoelectron spectroscopy. We find that the widely used ligand exchange model of the ALD process for the removal of native oxide on the semiconductor and the simultaneous formation of the first hafnium dioxide layer must be significantly revised. Our study provides substantial evidence that the efficiency of the self-cleaning process and the quality of the resulting semiconductor-oxide interface can be controlled by the molecular adsorption process of the ALD precursors, rather than the subsequent oxide formation.

  3. Zirconium and hafnium tetrachloride separation by extractive distillation with molten zinc chloride lead chloride solvent

    International Nuclear Information System (INIS)

    McLaughlin, D.F.; Stoltz, R.A.

    1988-01-01

    In an extractive distillation method for separating hafniuim tetrachloride from zirconium tetrachloride of the type wherein a mixture of zirconium and hafnium tetrachlorides is introduced into an extractive distillation column, which extractive distillation column has a reboiler connected at the bottom and a reflux condenser connected at the top and wherein a molten salt solvent is circulated into the reflux condenser and through the column to provide a liquid phase, and wherein molten salt solvent containing zirconium tetrachloride is taken from the reboiler and run through a stripper to remove zirconium tetrachloride product from the molten salt solvent and the stripped molten salt solvent is returned to the reflux condenser and hafnium tetrachloride enriched vapor is taken as product from the reflux condenser, the improvement is described comprising: the molten salt having a composition of at least 30 mole percent zinc chloride and at least 10 mole percent of lead chloride

  4. Preparation of hafnium metal by calciothermic reduction of HfO2

    International Nuclear Information System (INIS)

    Sharma, I.G.; Vijay, P.L.; Sehra, J.C.; Sundaram, C.V.

    1975-01-01

    Hafnium metal powder has been produced by the calciothermic reduction of hafnium oxide. The influence of various experimental parameters - such as amount of calcium in excess of stoichiometric requirement, temperature, and time of reduction - on the yield and purity of the metal has been studied. The metal powder obtained by reduction at 960 0 C (two hours) with a calcium excess of 70% analysed 600 ppm of oxygen and 147 ppm of nitrogen. A reduction efficiency of 96% has been achieved under these conditions. The refining of the powder by electron beam melting, fused salt electrolysis, and iodide process has been studied. The oxygen content in the metal could be brought down from 6900 to 148 ppm by electron beam melt-refining. (author)

  5. Holmium-166-chico intracavitary radiation therapy for cystic brain tumors

    Energy Technology Data Exchange (ETDEWEB)

    Rhee, C. H.; Lee, S. H.; Jang, J. S.; Kim, E. H.; Choi, C. W.; Hong, S. W.; Lim, S. M. [Korea Cancer Center, Seoul (Korea, Republic of)

    1997-07-01

    Holmium-166-chitosan complex (Ho-166-chico) is injected into the unresectable seven cystic brain tumors (2 cases of metastatic brain tumors from lung cancer, 1 case of recurrent trigeminal neurinoma, 3 cases of recurrent low grade cystic astrocytomas, and 1 case of craniopharyngioma). The Ommaya reservoir was installed stereotactically. The cyst volume and wall thickness were measured by MRI before Ho-166-chico injection. The thickness of the cyst wall is up to 4 mm. Ho-166-chico (555-740 MBq) injected into the cyst to result in 25 Gy of dose to a cyst wall at a depth of 4 mm. Dose to the cyst wall was estimated by Monte Carlo simulation using the EGS4 code. All Ho-166-chico injected was assumed to be uniformly distributed in the spherical cyst. After Ho-166-chico injection, the distribution of isotopes was monitored by gamma camera. Two injections were administrated in two cases, and one injection in all the others. The response was evaluated with MRI. Four of 7 cases were shrunk in size with thinning of the cyst wall, 2 of 7 cases showed growth arrest, and one case showed progression. Estimated surface dose of cyst wall was between 78 and 2566 Gy. No one showed systemic absorption of Ho-166-chico, and specific complication associated with isotope injection. Ho-166-chico intracavitary radiation therapy for cystic brain tumor may be safe, and reliable method and deserves further evaluation.

  6. 27 CFR 24.166 - Buildings or rooms.

    Science.gov (United States)

    2010-04-01

    ... 27 Alcohol, Tobacco Products and Firearms 1 2010-04-01 2010-04-01 false Buildings or rooms. 24.166... OF THE TREASURY LIQUORS WINE Construction and Equipment § 24.166 Buildings or rooms. All buildings or... afford adequate protection to the revenue. Each building or room will be constructed of substantial...

  7. 40 CFR 166.45 - Duration of crisis exemption.

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 23 2010-07-01 2010-07-01 false Duration of crisis exemption. 166.45... EXEMPTION OF FEDERAL AND STATE AGENCIES FOR USE OF PESTICIDES UNDER EMERGENCY CONDITIONS Crisis Exemptions § 166.45 Duration of crisis exemption. A crisis exemption may be authorized for: (a) Only as long as is...

  8. 7 CFR 457.166 - Blueberry crop insurance provisions.

    Science.gov (United States)

    2010-01-01

    ... 7 Agriculture 6 2010-01-01 2010-01-01 false Blueberry crop insurance provisions. 457.166 Section... CORPORATION, DEPARTMENT OF AGRICULTURE COMMON CROP INSURANCE REGULATIONS § 457.166 Blueberry crop insurance provisions. The Blueberry Crop Insurance Provisions for the 2005 and succeeding crop years are as follows...

  9. 31 CFR 16.6 - Prerequisites for issuing a complaint.

    Science.gov (United States)

    2010-07-01

    .... 16.6 Section 16.6 Money and Finance: Treasury Office of the Secretary of the Treasury REGULATIONS... defined in paragraph (b) of this section), the amount of money or the value of property or services demanded or requested in violation of § 16.3(a) does not exceed $150,000. (b) For the purposes of this...

  10. 9 CFR 166.8 - Vehicles used to transport garbage.

    Science.gov (United States)

    2010-01-01

    ... 9 Animals and Animal Products 1 2010-01-01 2010-01-01 false Vehicles used to transport garbage. 166.8 Section 166.8 Animals and Animal Products ANIMAL AND PLANT HEALTH INSPECTION SERVICE, DEPARTMENT... used to transport garbage. Vehicles used by a licensee to transport untreated garbage, except those...

  11. 40 CFR 166.7 - User notification; advertising.

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 23 2010-07-01 2010-07-01 false User notification; advertising. 166.7... § 166.7 User notification; advertising. (a) A State or Federal agency that obtains an exemption may... received) delivers or offers to deliver any pesticide, to advertise the pesticide for any use authorized by...

  12. 9 CFR 166.14 - Cleaning and disinfecting.

    Science.gov (United States)

    2010-01-01

    ... 9 Animals and Animal Products 1 2010-01-01 2010-01-01 false Cleaning and disinfecting. 166.14... AGRICULTURE SWINE HEALTH PROTECTION SWINE HEALTH PROTECTION General Provisions § 166.14 Cleaning and disinfecting. (a) Disinfectants to be used. Disinfection required under the regulations in this Part shall be...

  13. On-line separation of refractory hafnium and tantalum isotopes at the ISOCELE separator

    CERN Document Server

    Liang, C F; Obert, J; Paris, P; Putaux, J C

    1981-01-01

    By chemical evaporation technique, neutron deficient hafnium nuclei have been on-line separated at the ISOCELE facility, from the isobar rare-earth elements, in the metal-fluoride HfF/sub 3//sup +/ ion form. Half-lives of /sup 162-165/Hf have been measured. Similarly, tantalum has been selectively separated on the TaF/sub 4//sup +/ form. (4 refs) .

  14. Complexonometric determination of hafnium (4) in the presence of europium(3) or tantalum(5)

    International Nuclear Information System (INIS)

    Oziashvili, E.D.; Ehsakiya, K.E.; Sirakanyan, N.M.

    1986-01-01

    Complexonometric determination of hafnium in the presence of Ta or Eu in samples which can be decomposed by acids, i.e. in double borides has been investigated. Initial solutions are prepared by fusing with K 2 S 2 O 8 excess, the fusion was leached by hot water, H 2 SO L 4 was added and Hf was titrated by complexone 3 in the presence of xylenol orange

  15. Simplified method for gravimetric determination of zirconium or hafnium with α-hydroxy carboxylic acids

    International Nuclear Information System (INIS)

    Barbieri, R.S.; Rocha, J.C.; Terra, V.R.; Marques Netto, A.

    1989-01-01

    The conditions for gravimetric determination of zirconium or hafnium by glicoloc acids derivatives were studied by thermogravimetric analysis. The method utilized shownd that after precipitation, washing and drying of precipitates at 150 o C, the resulting solid was weighed in the form of [M (RCH(OH)COO) 4 ] (M = Zr, Hf; R + C 6 H 5 , β-C 10 H 7 , p-BrC 6 H 4 ). (author)

  16. Modified method for zirconium or hafnium gravimetric determination with glycolic acid derivatives

    International Nuclear Information System (INIS)

    Barbieri, R.S.; Rocha, J.C.; Terra, V.R.; Marques Neto, A.

    1989-01-01

    The conditions for gravimetric determination of zirconium or hafnium by glicolic acid derivatives were studied by thermogravimetric analysis. The method utilized shown that after precipitation, washing and drying of precipitates at 150 0 C, the resulting solid was weighed in the form of [M{RCH(OH)COO} 4 ] (M = Zr,Hf;R = C 6 H 5 , β-C 10 H 7 ,p-BrC 6 H 4 ). (author) [pt

  17. Electrodeposition in molten salts of metals used in nuclear industry: hafnium and uranium

    International Nuclear Information System (INIS)

    Serrano, K.

    1998-01-01

    The aim of this work is to study the electrodeposition in molten salts of metals used in nuclear industry: hafnium and uranium. The experiment is carried out in a molten alkaline halogenide medium in a temperature range between 670 and 750 degrees Celsius. The first part of this work concerns more particularly the electrochemical behaviour of the hafnium and uranium ions in the electrolytic solution. The reduction mechanisms of these ions have been studied by the use of three methods: cyclic voltametry, chrono-potentiometry and square wave voltametry. Results have shown that the process of metal deposition is difficult to explain because secondary reactions (as for instance: adsorption phenomena or cathodic deposit dissolution) occur. The uranium germination has then been studied by modelling of chrono-amperograms. The experiments have shown that the deposition is the result of the initial uranium crystal growth and depends on the electrolyte diffusion. The second part of this work deals with the implementation of hafnium and uranium deposition taking into account the preceding mechanistic studies. Depositions have all been observed by physical methods as for instance scanning electron microscopy. Particular experimental solutions (soluble anode, addition of fluoride ions to the electrolyte) have been used. The obtained deposition of hafnium is smooth and adheres very well to the substrate. The uranium depositions have been implemented with the use of a soluble anode. Uranium is deposited in a dendritic shape to the cathode. It has also been shown that the electro-kinetic parameters (temperature, uranium ions concentration, current density) have not an important influence on the dendritic morphology of the deposition. This morphology could be the consequence of particular convection movements to the surface of the cathode. (O.M.)

  18. Rhodium and Hafnium Influence on the Microstructure, Phase Composition, and Oxidation Resistance of Aluminide Coatings

    OpenAIRE

    Maryana Zagula-Yavorska; Małgorzata Wierzbińska; Jan Sieniawski

    2017-01-01

    A 0.5 μm thick layer of rhodium was deposited on the CMSX 4 superalloy by the electroplating method. The rhodium-coated superalloy was hafnized and aluminized or only aluminized using the Chemical vapour deposition method. A comparison was made of the microstructure, phase composition, and oxidation resistance of three aluminide coatings: nonmodified (a), rhodium-modified (b), and rhodium- and hafnium-modified (c). All three coatings consisted of two layers: the additive layer and the interdi...

  19. Radiation effects on the electrical properties of hafnium oxide based MOS capacitors.

    Energy Technology Data Exchange (ETDEWEB)

    Petrosky, J. C. (Air Force Institute of Technology, Wright-Patterson Air Force Base, OH); McClory, J. W. (Air Force Institute of Technology, Wright-Patterson Air Force Base, OH); Bielejec, Edward Salvador; Foster, J. C. (Air Force Institute of Technology, Wright-Patterson Air Force Base, OH)

    2010-10-01

    Hafnium oxide-based MOS capacitors were investigated to determine electrical property response to radiation environments. In situ capacitance versus voltage measurements were analyzed to identify voltage shifting as a result of changes to trapped charge with increasing dose of gamma, neutron, and ion radiation. In situ measurements required investigation and optimization of capacitor fabrication to include dicing, cleaning, metalization, packaging, and wire bonding. A top metal contact of 200 angstroms of titanium followed by 2800 angstroms of gold allowed for repeatable wire bonding and proper electrical response. Gamma and ion irradiations of atomic layer deposited hafnium oxide on silicon devices both resulted in a midgap voltage shift of no more than 0.2 V toward less positive voltages. This shift indicates recombination of radiation induced positive charge with negative trapped charge in the bulk oxide. Silicon ion irradiation caused interface effects in addition to oxide trap effects that resulted in a flatband voltage shift of approximately 0.6 V also toward less positive voltages. Additionally, no bias dependent voltage shifts with gamma irradiation and strong oxide capacitance room temperature annealing after ion irradiation was observed. These characteristics, in addition to the small voltage shifts observed, demonstrate the radiation hardness of hafnium oxide and its applicability for use in space systems.

  20. On the phase formation of sputtered hafnium oxide and oxynitride films

    International Nuclear Information System (INIS)

    Sarakinos, K.; Music, D.; Mraz, S.; Baben, M. to; Jiang, K.; Nahif, F.; Braun, A.; Zilkens, C.; Schneider, J. M.; Konstantinidis, S.; Renaux, F.; Cossement, D.; Munnik, F.

    2010-01-01

    Hafnium oxynitride films are deposited from a Hf target employing direct current magnetron sputtering in an Ar-O 2 -N 2 atmosphere. It is shown that the presence of N 2 allows for the stabilization of the transition zone between the metallic and the compound sputtering mode enabling deposition of films at well defined conditions of target coverage by varying the O 2 partial pressure. Plasma analysis reveals that this experimental strategy facilitates control over the flux of the O - ions which are generated on the oxidized target surface and accelerated by the negative target potential toward the growing film. An arrangement that enables film growth without O - ion bombardment is also implemented. Moreover, stabilization of the transition sputtering zone and control of the O - ion flux without N 2 addition is achieved employing high power pulsed magnetron sputtering. Structural characterization of the deposited films unambiguously proves that the phase formation of hafnium oxide and hafnium oxynitride films with the crystal structure of HfO 2 is independent from the O - bombardment conditions. Experimental and theoretical data indicate that the presence of vacancies and/or the substitution of O by N atoms in the nonmetal sublattice favor the formation of the cubic and/or the tetragonal HfO 2 crystal structure at the expense of the monoclinic HfO 2 one.

  1. Correlations between nuclear data and integral slab experiments: the case of hafnium; Correlations entre donnees nucleaires et experiences integrales a plaques: le cas du hafnium

    Energy Technology Data Exchange (ETDEWEB)

    Palau, J.M

    1999-07-01

    The aim of this work was to evaluate how much integral slab experiments can both reduce discrepancies between experimental results and calculations, and improve the knowledge of hafnium isotopes neutronic parameters by an adapted sensitivity and uncertainty method. A statistical approach, based on the generalized least squares method and perturbation theory, has been incorporated into our calculation system in order to deduce microscopic cross-section adjustments from observed integral measurements on this particular 'mock-up' reactor.In this study it has been established that the correlations between integral parameters and hafnium capture cross-sections enable specific variations in the region of resolved resonances at the level of multigroup and punctual cross-sections recommended data (JEF-2.2 evaluation) to be highlighted. The use of determinist methods together with Monte Carlo- type simulations enabled a depth analysis of the modelling approximations to be carried out. Furthermore, the sensitivity coefficient validation technique employed leads to a reliable assessment of the quality of the new basic nuclear data. In this instance, the adjustments proposed for certain isotope {sup 177}Hf resonance parameters reduce, after error propagation, by 3 to 5 per cent the difference between experimental results and calculations related to this absorbent's efficiency. Beyond this particular application, the qualification methodology integrated in our calculation system should enable other basic sizing parameters to be treated (chemical / geometric data or other unexplored nuclear data) to make technological requirements less stringent. (author)

  2. Correlations between nuclear data and integral slab experiments: the case of hafnium; Correlations entre donnees nucleaires et experiences integrales a plaques: le cas du hafnium

    Energy Technology Data Exchange (ETDEWEB)

    Palau, J M

    1999-07-01

    The aim of this work was to evaluate how much integral slab experiments can both reduce discrepancies between experimental results and calculations, and improve the knowledge of hafnium isotopes neutronic parameters by an adapted sensitivity and uncertainty method. A statistical approach, based on the generalized least squares method and perturbation theory, has been incorporated into our calculation system in order to deduce microscopic cross-section adjustments from observed integral measurements on this particular 'mock-up' reactor.In this study it has been established that the correlations between integral parameters and hafnium capture cross-sections enable specific variations in the region of resolved resonances at the level of multigroup and punctual cross-sections recommended data (JEF-2.2 evaluation) to be highlighted. The use of determinist methods together with Monte Carlo- type simulations enabled a depth analysis of the modelling approximations to be carried out. Furthermore, the sensitivity coefficient validation technique employed leads to a reliable assessment of the quality of the new basic nuclear data. In this instance, the adjustments proposed for certain isotope {sup 177}Hf resonance parameters reduce, after error propagation, by 3 to 5 per cent the difference between experimental results and calculations related to this absorbent's efficiency. Beyond this particular application, the qualification methodology integrated in our calculation system should enable other basic sizing parameters to be treated (chemical / geometric data or other unexplored nuclear data) to make technological requirements less stringent. (author)

  3. Correlations between nuclear data and results of integral slab experiments. Case of hafnium; Correlations entre donnees nucleaires et experiences integrales a plaques: le cas du hafnium

    Energy Technology Data Exchange (ETDEWEB)

    Palau, J M

    1997-10-22

    The aim of this thesis was to evaluate how much integral slab experiments can both reduce discrepancies between experimental results and calculations, and improve the knowledge of hafnium isotopes neutronic parameters by an adapted sensitivity and uncertainty method. A statistical approach, based on the generalized least squares method and perturbation theory, has been incorporated into our calculation system in order to deduce microscopic cross-section adjustments from observed integral measurements on this particular `mock-up` reactor. In this study it has been established that the correlations between integral parameters and hafnium capture cross-sections enable specific variations in the region of resolved resonances at the level of multigroup and punctual cross-sections recommended data (JEF-2.2 evaluation) to be highlighted. The use of determinist methods (APOLLO2 code) together with Monte Carlo- type simulations (TRIPOLI4 code) enabled a depth analysis of the modelling approximations to be carried out. Furthermore, the sensitivity coefficient validation technique employed leads to a reliable assessment of the quality of the new basic nuclear data. In this instance, the adjustments proposed for certain isotope {sup 177}Hf resonance parameters reduce, after error propagation, by 3 to 5 per cent the difference between experimental results and calculations related to this absorbent`s efficiency. Beyond this particular application, the qualification methodology integrated in our calculation system should enable other basic sizing parameters to be treated (chemical / geometric data or other unexplored nuclear data) to make technological requirements less stringent. (author) 128 refs.

  4. Development and characterization of ultrathin hafnium titanates as high permittivity gate insulators

    Science.gov (United States)

    Li, Min

    High permittivity or high-kappa materials are being developed for use as gate insulators for future ultrascaled metal oxide semiconductor field effect transistors (MOSFETs). Hafnium containing compounds are the leading candidates. Due to its moderate permittivity, however, it is difficult to achieve HfO2 gate structures with an EOT well below 1.0 nm. One approach to increase HfO2 permittivity is combining it with a very high-kappa material, such as TiO2. In this thesis, we systematically studied the electrical and physical characteristics of high-kappa hafnium titanates films as gate insulators. A series of HfxTi1-xO2 films with well-controlled composition were deposited using an MOCVD system. The physical properties of the films were analyzed using a variety of characterization techniques. X-ray micro diffraction indicates that the Ti-rich thin film is more immune to crystallization. TEM analysis showed that the thick stoichiometric HfTiO 4 film has an orthorhombic structure and large anisotropic grains. The C-V curves from the devices with the hafnium titanates films displayed relatively low hysteresis. In a certain composition range, the interfacial layer (IL) EOT and permittivity of HfxTi1-x O2 increases linearly with increasing Ti. The charge is negative for HfxTi1-xO2/IL and positive for Si/IL interface, and the magnitude increases as Hf increases. For ultra-thin films (less than 2 nm EOT), the leakage current increases with increasing HE Moreover, the Hf-rich sample has weaker temperature dependence of the current. In the MOSFET devices with the hafnium titanates films, normal transistor characteristics were observed, also electron mobility degradation. Next, we investigated the effects that different pre-deposition surface treatments, including HF dipping, NH3 surface nitridation, and HfO2 deposition, have on the electrical properties of hafnium titanates. Surface nitridation shows stronger effect than the thin HfO2 layer. The nitrided samples displayed a

  5. Investigation of complexes with bone affinity using the In vivo generator system {sup 166} Dy/{sup 166} Ho; Investigacion de complejos con afinidad osea utilizando el Sistema de Generador in vivo {sup 166} Dy/{sup 166} Ho

    Energy Technology Data Exchange (ETDEWEB)

    Pedraza L, M

    2006-07-01

    The importance of this original research lies in the fact that it has proven that the [{sup 166}Dy]Dy/{sup 166}Ho-EDTMP in vivo generator system is a stable complex that can be used as a therapeutic radiopharmaceutical. Multiple myeloma and other hematological malignancies have been treated by myeloablative radiotherapy/chemotherapy and subsequent stem cell transplantation. Bone-seeking radiopharmaceuticals such as {sup 166}Ho-DOTMP or {sup 153}Sm-DTMP, have been proposed for delivering ablative radiation doses to marrow in multiple myeloma and other hematological malignancies or have shown excellent results in palliative bone metastasis pain therapy, respectively. As lanthanides have similar chemical characteristics the phosphonate with bone affinity (EDTMP) labeled with Dy/Ho can be used for marrow ablation while causing minimal irradiation to normal organs. This in vivo generator system has not been previously reported. The aim of this research was to label EDTMP (ethylene diamine tetramethylene phosphonate) with {sup 166}Dy/{sup 166}Ho; to evaluate the in vitro and in vivo stability of both {sup 166}Dy-EDTMP and {sup 166}Ho-EDTMP complexes when the daughter {sup 166}Ho is formed as a dysprosium decay product; to determine the bone marrow cytotoxic and genotoxic effect in mice and to evaluate, by histopathology, the myeloablative potential of the [{sup 166}Dy]Dy/{sup 166}Ho-EDTMP in vivo generator system. {sup 166}Dy was obtained by neutron irradiation of enriched {sup 164}Dy{sub 2}O{sub 3} in a TRIGA Mark III reactor. Labeling was carried out in an aqueous phosphate medium at pH 8.0 by addition of {sup 166}DyCl{sub 3} to EDTMP at a molar ratio 1:1.75, with >99 % radiochemical purity, as determined by thin-layer chromatography (TLC) and high-performance liquid chromatography (HPLC). In vitro studies demonstrated that {sup 166}Dy/{sup 166}Ho-EDTMP is unstable after dilution in saline but stable in human serum with no translocation of the daughter nucleus

  6. Low-voltage bendable pentacene thin-film transistor with stainless steel substrate and polystyrene-coated hafnium silicate dielectric.

    Science.gov (United States)

    Yun, Dong-Jin; Lee, Seunghyup; Yong, Kijung; Rhee, Shi-Woo

    2012-04-01

    The hafnium silicate and aluminum oxide high-k dielectrics were deposited on stainless steel substrate using atomic layer deposition process and octadecyltrichlorosilane (OTS) and polystyrene (PS) were treated improve crystallinity of pentacene grown on them. Besides, the effects of the pentacene deposition condition on the morphologies, crystallinities and electrical properties of pentacene were characterized. Therefore, the surface treatment condition on dielectric and pentacene deposition conditions were optimized. The pentacene grown on polystyrene coated high-k dielectric at low deposition rate and temperature (0.2-0.3 Å/s and R.T.) showed the largest grain size (0.8-1.0 μm) and highest crystallinity among pentacenes deposited various deposition conditions, and the pentacene TFT with polystyrene coated high-k dielectric showed excellent device-performance. To decrease threshold voltage of pentacene TFT, the polystyrene-thickness on high-k dielectric was controlled using different concentration of polystyrene solution. As the polystyrene-thickness on hafnium silicate decreases, the dielectric constant of polystyrene/hafnium silicate increases, while the crystallinity of pentacene grown on polystyrene/hafnium silicate did not change. Using low-thickness polystyrene coated hafnium silicate dielectric, the high-performance and low voltage operating (pentacene thin film transistor (μ: ~2 cm(2)/(V s), on/off ratio, >1 × 10(4)) and complementary inverter (DC gains, ~20) could be fabricated.

  7. Extraction of zirconium and hafnium thiocyanates by CH3COCH2CH.(CH3)2-HSCN solvent from chloride medium

    International Nuclear Information System (INIS)

    Okada, A.T.

    1982-01-01

    A zirconium-hafnium separation process for application in nuclear industry is presented. The extraction of zirconium and hafnium thiocyanates in chloride medium by hexone-HSCN solvent was studied. The extraction process was developed, varying the parameters, such as, concentrations of the metals, the thiocyanate ion, the sulphate ion and free acidity in aqueous phase. (Author) [pt

  8. Recoil and conversion electron considerations of the {sup 166}Dy/{sup 166}Ho in vivo generator

    Energy Technology Data Exchange (ETDEWEB)

    Zeevaart, J.R. [North-West Univ., Mmabatho (South Africa). CARST; Szuecs, Z. [Nesca (South African Nuclear Energy Corporation Ltd.), Pretoria (South Africa). Radiochemistry; Hungarian Academy of Sciences, Debrecen (Hungary). Inst. of Nuclear Research; Takacs, S.; Jarvis, N. [Hungarian Academy of Sciences, Debrecen (Hungary). Inst. of Nuclear Research; Jansen, D. [Nesca (South African Nuclear Energy Corporation Ltd.), Pretoria (South Africa). Radiochemistry

    2012-07-01

    The use of radionuclides as potential therapeutic radiopharmaceuticals is increasingly investigated. An important aspect is the delivery of the radionuclide to the target, i.e. the radionuclide is not lost from the chelating agent. For in vivo generators, it is not only the log K of complexation between the metal ion and the chelator that is important, but also whether the daughter radionuclide stays inside the chelator after decay of the parent radionuclide. In our previous work, we showed that the classical recoil effect is only applicable for decays with a Q value higher than 0.6 MeV (in the atomic mass range around 100). However, Zhernosekov et al. published a result for {sup 140}Nd/{sup 140}Pr (Q = 0.222 MeV) which indicated that > 95% of the daughter ({sup 140}Pr) was lost by a DOTA chelator upon decay of {sup 140}Nd. The authors ascribed this to the ''post-effect''. Their experiment was repeated with the {sup 166}Dy/{sup 166}Ho generator to ascertain whether our calculations were correct. It was found that 72% of the daughter ({sup 166}Ho) was liberated from the DOTA chelator, indicating that the 'post effect' does exist in contrast to our recoil calculations. Upon further investigation, we determined that one should not only consider recoil energy levels but also the mode of decay which was able to explain the partial recoil found for {sup 166}Dy/{sup 166}Ho. It is concluded for the {sup 166}Dy/{sup 166}Ho system that the low recoil energy of the daughter nucleus {sup 166}Ho is not a sufficient reason to rule out release of the nuclide from chelators. On the other hand, we found that the ratio of the {sup 166}Ho that gets released corresponds to the ratio of relaxation of Ho atoms via the Auger process. (orig.)

  9. Investigation of complexes with bone affinity using the In vivo generator system {sup 166} Dy/{sup 166} Ho; Investigacion de complejos con afinidad osea utilizando el Sistema de Generador in vivo {sup 166} Dy/{sup 166} Ho

    Energy Technology Data Exchange (ETDEWEB)

    Pedraza L, M

    2006-07-01

    The importance of this original research lies in the fact that it has proven that the [{sup 166}Dy]Dy/{sup 166}Ho-EDTMP in vivo generator system is a stable complex that can be used as a therapeutic radiopharmaceutical. Multiple myeloma and other hematological malignancies have been treated by myeloablative radiotherapy/chemotherapy and subsequent stem cell transplantation. Bone-seeking radiopharmaceuticals such as {sup 166}Ho-DOTMP or {sup 153}Sm-DTMP, have been proposed for delivering ablative radiation doses to marrow in multiple myeloma and other hematological malignancies or have shown excellent results in palliative bone metastasis pain therapy, respectively. As lanthanides have similar chemical characteristics the phosphonate with bone affinity (EDTMP) labeled with Dy/Ho can be used for marrow ablation while causing minimal irradiation to normal organs. This in vivo generator system has not been previously reported. The aim of this research was to label EDTMP (ethylene diamine tetramethylene phosphonate) with {sup 166}Dy/{sup 166}Ho; to evaluate the in vitro and in vivo stability of both {sup 166}Dy-EDTMP and {sup 166}Ho-EDTMP complexes when the daughter {sup 166}Ho is formed as a dysprosium decay product; to determine the bone marrow cytotoxic and genotoxic effect in mice and to evaluate, by histopathology, the myeloablative potential of the [{sup 166}Dy]Dy/{sup 166}Ho-EDTMP in vivo generator system. {sup 166}Dy was obtained by neutron irradiation of enriched {sup 164}Dy{sub 2}O{sub 3} in a TRIGA Mark III reactor. Labeling was carried out in an aqueous phosphate medium at pH 8.0 by addition of {sup 166}DyCl{sub 3} to EDTMP at a molar ratio 1:1.75, with >99 % radiochemical purity, as determined by thin-layer chromatography (TLC) and high-performance liquid chromatography (HPLC). In vitro studies demonstrated that {sup 166}Dy/{sup 166}Ho-EDTMP is unstable after dilution in saline but stable in human serum with no translocation of the daughter nucleus

  10. Nuclear level density of 166Er with static deformation

    International Nuclear Information System (INIS)

    Nasrabadi, M.N.

    2006-01-01

    The level densities of 166 Er is calculated using the microscopic theory of interacting fermions and is compared with experimental. It is concluded that the data can be reproduced with level density formalism for nuclei with static deformation

  11. Solvent extraction of titanium(IV), zirconium(IV) and hafnium(IV) salicylates using liquid ion exchangers

    Energy Technology Data Exchange (ETDEWEB)

    Sundaramurthi, N M; Shinde, V M

    1989-02-01

    A solvent extraction method is proposed for the extraction of quadrivalent titanium, zirconium an hafnium from salicylate media using liquid ion exchangers such as Aliquat 336 and trioctylamine dissolved in xylene. The optimum conditions were evaluated from a critical study of the following: pH, salicylate concentration, amine concentration, diluent and period of equilibration. The method allows the separation of titanium, zirconium and hafnium from binary mixtures containing commonly associated metal ions and is applicable to the analysis of real samples such as BCS-CRM 387 nimonic 901, BCS-CRM 243/4 ferro-titanium, BCS-CRM 307 magnesium alloy and BCS-CRM 388 zircon. Titanium is determined either with hydrogen peroxide or by atomic absorption spectrometry whereas zirconium and hafnium are determined spectrophotometrically with Alizarin Red S and Zylenol Orange, respectively. The results of both separation and analysis are reported. The method is precise, accurate and fast.

  12. Use of hafnium in control bars of nuclear reactors; Uso de hafnio en barras de control de reactores nucleares

    Energy Technology Data Exchange (ETDEWEB)

    Ramirez S, J.R.; Alonso V, G. [ININ, 52045 Ocoyoacac, Estado de Mexico (Mexico)]. e-mail: jrrs@nuclear.inin-mx

    2003-07-01

    Recently the use of hafnium as neutron absorber material in nuclear reactors has been reason of investigation by virtue of that this material has nuclear properties as to the neutrons absorption and structural that can prolong the useful life of the control mechanisms of the nuclear reactors. In this work some of those more significant hafnium properties are presented like nuclear material. Also there are presented calculations carried out with the HELIOS code for fuel cells of uranium oxide and of uranium and plutonium mixed oxides under controlled conditions with conventional bars of boron carbide and also with similar bars to which are substituted the absorbent material by metallic hafnium, the results are presented in this work. (Author)

  13. Strong influence of polymer architecture on the microstructural evolution of hafnium-alkoxide-modified silazanes upon ceramization.

    Science.gov (United States)

    Papendorf, Benjamin; Nonnenmacher, Katharina; Ionescu, Emanuel; Kleebe, Hans-Joachim; Riedel, Ralf

    2011-04-04

    The present study focuses on the synthesis and ceramization of novel hafnium-alkoxide-modified silazanes as well as on their microstructure evolution at high temperatures. The synthesis of hafnia-modified polymer-derived SiCN ceramic nanocomposites is performed via chemical modification of a polysilazane and of a cyclotrisilazane, followed by cross-linking and pyrolysis in argon atmosphere. Spectroscopic investigation (i.e., NMR, FTIR, and Raman) shows that the hafnium alkoxide reacts with the N-H groups of the cyclotrisilazane; in the case of polysilazane, reactions of N-H as well as Si-H groups with the alkoxide are observed. Consequently, scanning and transmission electron microscopy studies reveal that the ceramic nanocomposites obtained from cyclotrisilazane and polysilazane exhibited markedly different microstructures, which is a result of the different reaction pathways of the hafnium alkoxide with cyclotrisilazane and with polysilazane. Furthermore, the two prepared ceramic nanocomposites are unexpectedly found to exhibit extremely different high-temperature behavior with respect to decomposition and crystallization; this essential difference is found to be related to the different distribution of hafnium throughout the ceramic network in the two samples. Thus, the homogeneous distribution of hafnium observed in the polysilazane-derived ceramic leads to an enhanced thermal stability with respect to decomposition, whereas the local enrichment of hafnium within the matrix of the cyclotrisilazane-based sample induces a pronounced decomposition upon annealing at high temperatures. The results indicate that the chemistry and architecture of the precursor has a crucial effect on the microstructure of the resulting ceramic material and consequently on its high-temperature behavior. Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  14. Hafnium at subduction zones: isotopic budget of input and output fluxes; L'hafnium dans les zones de subduction: bilan isotopique des flux entrant et sortant

    Energy Technology Data Exchange (ETDEWEB)

    Marini, J.Ch

    2004-05-15

    Subduction zones are the primary regions of mass exchanges between continental crust and mantle of Earth through sediment subduction toward the earth's mantle and by supply of mantellic magmas to volcanic arcs. We analyze these mass exchanges using Hafnium and Neodymium isotopes. At the Izu-Mariana subduction zone, subducting sediments have Hf and Nd isotopes equivalent to Pacific seawater. Altered oceanic crust has Hf and Nd isotopic compositions equivalent to the isotopic budget of unaltered Pacific oceanic crust. At Luzon and Java subduction zones, arc lavas present Hf isotopic ratios highly radiogenic in comparison to their Nd isotopic ratios. Such compositions of the Luzon and Java arc lavas are controlled by a contamination of their sources by the subducted oceanic sediments. (author)

  15. The Polycistronic miR166k-166h Positively Regulates Rice Immunity via Post-transcriptional Control of EIN2

    Directory of Open Access Journals (Sweden)

    Raquel Salvador-Guirao

    2018-03-01

    Full Text Available MicroRNAs (miRNAs are small RNAs acting as regulators of gene expression at the post-transcriptional level. In plants, most miRNAs are generated from independent transcriptional units, and only a few polycistronic miRNAs have been described. miR166 is a conserved miRNA in plants targeting the HD-ZIP III transcription factor genes. Here, we show that a polycistronic miRNA comprising two miR166 family members, miR166k and miR166h, functions as a positive regulator of rice immunity. Rice plants with activated MIR166k-166h expression showed enhanced resistance to infection by the fungal pathogens Magnaporthe oryzae and Fusarium fujikuroi, the causal agents of the rice blast and bakanae disease, respectively. Disease resistance in rice plants with activated MIR166k-166h expression was associated with a stronger expression of defense responses during pathogen infection. Stronger induction of MIR166k-166h expression occurred in resistant but not susceptible rice cultivars. Notably, the ethylene-insensitive 2 (EIN2 gene was identified as a novel target gene for miR166k. The regulatory role of the miR166h-166k polycistron on the newly identified target gene results from the activity of the miR166k-5p specie generated from the miR166k-166h precursor. Collectively, our findings support a role for miR166k-5p in rice immunity by controlling EIN2 expression. Because rice blast is one of the most destructive diseases of cultivated rice worldwide, unraveling miR166k-166h-mediated mechanisms underlying blast resistance could ultimately help in designing appropriate strategies for rice protection.

  16. Atomic layer deposition of calcium oxide and calcium hafnium oxide films using calcium cyclopentadienyl precursor

    International Nuclear Information System (INIS)

    Kukli, Kaupo; Ritala, Mikko; Sajavaara, Timo; Haenninen, Timo; Leskelae, Markku

    2006-01-01

    Calcium oxide and calcium hafnium oxide thin films were grown by atomic layer deposition on borosilicate glass and silicon substrates in the temperature range of 205-300 o C. The calcium oxide films were grown from novel calcium cyclopentadienyl precursor and water. Calcium oxide films possessed refractive index 1.75-1.80. Calcium oxide films grown without Al 2 O 3 capping layer occurred hygroscopic and converted to Ca(OH) 2 after exposure to air. As-deposited CaO films were (200)-oriented. CaO covered with Al 2 O 3 capping layers contained relatively low amounts of hydrogen and re-oriented into (111) direction upon annealing at 900 o C. In order to examine the application of CaO in high-permittivity dielectric layers, mixtures of Ca and Hf oxides were grown by alternate CaO and HfO 2 growth cycles at 230 and 300 o C. HfCl 4 was used as a hafnium precursor. When grown at 230 o C, the films were amorphous with equal amounts of Ca and Hf constituents (15 at.%). These films crystallized upon annealing at 750 o C, showing X-ray diffraction peaks characteristic of hafnium-rich phases such as Ca 2 Hf 7 O 16 or Ca 6 Hf 19 O 44 . At 300 o C, the relative Ca content remained below 8 at.%. The crystallized phase well matched with rhombohedral Ca 2 Hf 7 O 16 . The dielectric films grown on Si(100) substrates possessed effective permittivity values in the range of 12.8-14.2

  17. A study of a production process for hafnium-free zirconium from zircon

    International Nuclear Information System (INIS)

    Ratanalert, N.

    1985-01-01

    The purpose of this experiment was to extract and purify the zirconium from zircon. The effects of time of extraction and stripping of zirconium, concentration of feed solution, concentration of hydrochloric acid in stripping process, equilibrium curve of extraction of zirconium and hafnium and equilibrium curve of stripping zirconium or scrubbing hafnium were studied from standard zirconium and hafnium. The results, subsequently were applied to the extraction procedures for zirconium from zircon. Minus 100 mesh zircon was fused with sodium hydroxide in the ratio of 1 : 6 at 700 degree C for l hour. After fusion the zirconate was leached with water and dissolved in hot concentrated hydrochloric acid. Zirconyl chloride octahydrate crystallized out when the solution was cooled. An agueons solution of zirconyl chloride was used as the feed to the hexone - thiocyanate solvent extraction process. This was prepared by dissolving zirconyl chloride octahydrate crystal in waster. This zirconium feed solution in 1 M HCl and 1 M N H 4 CNS was extracted with 2.7 m N H 4 CNS in hexone and then stripped with 3.6 M HCl the aqueous phase was got rid of thiocyanate ion by extracting with pure hexone, then the zirconium in aqueous phase was precipitated with sulfuric acid and ammonium hydroxide at pH 1.8 - 2.0 and zirconium oxide was obtained by ignition at 700 degree C. The process could be modified to improve the purity of zirconium by using cation exchange resin to get rid of thiocyanate ion after solvent extraction process

  18. Laser coating of hafnium on Ti6Al4 for biomedical applications

    CSIR Research Space (South Africa)

    Phume, L

    2012-12-01

    Full Text Available Al4V FOR BIOMEDICAL APPLICATIONS Lerato Phume 1, 2, S.L. Pityana 1, 2, C. Meacock 1, A.P.I Popoola 2 1. National Laser Centre, Council for Scientific and Industrial Research, P.O. Box 395, Pretoria, 0001, South Africa 2. Department of Chemical... and Metallurgical Engineering, Tshwane University of Technology, Private Bag X 680, Pretoria, 0001, South Africa (b) (c) (e) To investigate laser surface coating of Ti6Al4V with preplaced Hafnium powder, to determine the influence of the energy density...

  19. Improvement of aging kinetics and precipitate size refinement in Mg–Sn alloys by hafnium additions

    Energy Technology Data Exchange (ETDEWEB)

    Behdad, S. [Department of Mechanical and Materials Engineering, Florida International University, Miami, FL 33174 (United States); Zhou, L. [Department of Materials Science and Engineering and Advanced Materials Processing and Analysis Center, University of Central Florida, Orlando, FL 32816 (United States); Henderson, H.B.; Manuel, M.V. [Department of Materials Science and Engineering, University of Florida, Gainesville, FL 32611 (United States); Sohn, Y. [Department of Materials Science and Engineering and Advanced Materials Processing and Analysis Center, University of Central Florida, Orlando, FL 32816 (United States); Agarwal, A. [Department of Mechanical and Materials Engineering, Florida International University, Miami, FL 33174 (United States); Boesl, B., E-mail: bboesl@fiu.edu [Department of Mechanical and Materials Engineering, Florida International University, Miami, FL 33174 (United States)

    2016-01-10

    Two Mg–Sn alloys were microalloyed by addition of Hafnium and their age-hardening response was studied at 200 °C. Time to reach peak hardness was significantly reduced and improved by Hf addition. TEM study showed Hf clusters in the close vicinity and at the surface of Mg{sub 2}Sn precipitates, which confirms that Hf clusters act as additional nucleation centers for Mg{sub 2}Sn precipitate formation. Our results support the validity of thermokinetic criterion proposed by Mendis for selection of microalloying elements in order to refine precipitate size, accelerate aging kinetics and enhance peak hardness.

  20. Critical evaluation of the determination of zirconium and hafnium by instrumental and radiochemical neutron activation analysis

    International Nuclear Information System (INIS)

    Burger, Mario; Kraehenbuehl, Urs

    1991-01-01

    Neutron activation analysis (instrument or radiochemical) is suitable for the determination of zirconium and hafnium in samples of geochemical origin only when sufficient attention is paid to inter-fering nuclides. The size of the necessary correction for INAA depends on the composition of the sample; this problem is discussed. The radio-chemical technique which is recommended involves separation of the samples, precipitations and anion-exchange separation. Results are given for various standard reference materials and for meteorites. (author). 12 refs.; 1 fig.; 9 tabs

  1. High temperature thermodynamics of solutions of oxygen in zirconium and hafnium

    International Nuclear Information System (INIS)

    Boureau, G.; Gerdanian, P.

    1984-01-01

    The Tian-Calvet microcalorimetric method has been applied to the determination at 1323 Kelvin of ΔH(O 2 ), the partial molar enthalpy of mixing of oxygen in zirconium and in hafnium. No measurable departure from Henry's law has been found for dilute solutions (ratio oxygen over metal smaller than 0.1). For concentrated solutions repulsive interactions are found in agreement with the existence of ordered structures at lower temperatures. The domain of homogeneity of zirconium has been found larger than previously assumed. (author)

  2. Complexing of zirconium and hafnium with ortho-aminobenzoic acid and paraaminobenzoic acid

    International Nuclear Information System (INIS)

    Alekseeva, I.I.; Nemzer, I.I.; Yuranova, L.I.; Borisova, V.V.; Prozorovskaya, Z.N.

    1977-01-01

    Formation of complexes between zirconium and hafnium and ortho- and para-aminobenzoic acids has been studied by the kinetic method. It has been found that at pH=1.3-2.0 and concentrations of metals 10 -5 -10 -6 mole complex compounds are formed with composition Me:L=1:2 and 1:1 (Me=Zr, Hf; L=ortho- or para-aminobenzoic acids). Stepwise constants and overall effective constants of complex formation have been calculated

  3. Investigation of interaction of zirconium and hafnium tetrafluorides with strontium fluoride

    International Nuclear Information System (INIS)

    Ratnikova, I.D.; Korenev, Yu.M.; Novoselova, A.V.

    1980-01-01

    Diagrams of the condensated state of systems SrF 2 -EF 4 have been plotted, where E represents Zr, Hf. In these systems, three intermediate compounds of Sr 3 EF 10 , Sr 2 EF 8 and Sr EF 6 compositions are formed. All those compounds melt incongruently at temperatures of 982, 865 and 750 deg C, respectively - zirconium salt; at temperatures of 1000, 900 and 820 deg C - hafnium salts. Fluoro-metallates of composition 2:1, and 1:1, exist in two polymorphic forms. Tetrafluorides were found to dissolve in strontium fluoride: they form solid solutions having fluorite structure

  4. Near net shape processing of zirconium or hafnium metals and alloys

    International Nuclear Information System (INIS)

    Evans, S.C.

    1992-01-01

    This patent describes a process for producing a metal shape. It comprises: plasma arc melting a metal selected from zirconium, hafnium and alloys thereof comprising at least about 90 w/o of these metals to form a liquid pool; pouring the metal form the pool into a mold to form a near net shape; and reducing the metal from its near net shape to a final size while maintaining the metal temperature below the alpha-beta transition temperature throughout the size reducing step

  5. Radiopharmaceuticals of DTPA, DMSA and EDTA labeled with holmium-166

    International Nuclear Information System (INIS)

    Rahman, M.; Matsouka, H.; Takami, S.; Terunuma, K.

    2001-01-01

    DTPA, DMSA and EDTA were labelled with 166 Ho of low specific activity, 250-275mCi/mg of Ho, produced from holmium oxide by the 165 Ho(n, g) 166 Ho reaction at a neutron flux of about 10 14 n.cm -2 .s -1 . Three pH ranges were selected in the study, viz. 2-3, 3-3.5 and 5-6. The labelling reactions were studied as chloride and nitrate solutions in aqueous and saline media at 30 min and 20-24 h of reaction. DTPA was labelled over 99, DMSA at about 90 and EDTA at 100.0% with 166 Ho. The complexes were found stable at all times of investigation. A beta chromatogram scanner was used to study by TLC the labelling reactions of DTPA and DMSA with the nuclide and by PC those of EDTA. A biodistribution study in three rats injected intravenous with a saline solution of 166 HoCl 3 [DTPA] at pH5.1 showed an initial uptake in blood, kidney and lung after 30 minutes. After four hours the complex was found to have cleared from blood and lung, and localized 100% in kidney. It was stable in vivo in the kidney after 24 hours. The g spectrum analysis did not show the formation of any impurity except the four characteristic g energies of 166 Ho. (author)

  6. Thermal behaviour of hafnium diethylenetriaminepentaacetate studied using the perturbed angular correlation technique

    Energy Technology Data Exchange (ETDEWEB)

    Chain, Cecilia Y. [Universidad Nacional de La Plata (Argentina). Dept. de Fisica; Consejo Nacional de Investigaciones Cientificas y Tecnicas (CONICET), La Plata (Argentina). IFLP-CCT; Consejo Nacional de Investigaciones Cientificas y Tecnicas, Buenos Aires (Argentina); Rivas, Patricia [Consejo Nacional de Investigaciones Cientificas y Tecnicas (CONICET), La Plata (Argentina). IFLP-CCT; Consejo Nacional de Investigaciones Cientificas y Tecnicas, Buenos Aires (Argentina); Universidad Nacional de La Plata (Argentina). Facultad de Ciencias Agrarias y Forestales; Pasquevich, Alberto F. [Universidad Nacional de La Plata (Argentina). Dept. de Fisica; Consejo Nacional de Investigaciones Cientificas y Tecnicas (CONICET), La Plata (Argentina). IFLP-CCT; Comision de Investigaciones Cientificas de la Provincia de Buenos Aires (CIC-PBA) (Argentina)

    2014-07-01

    Polyaminecarboxilic ligands like diethylenetriaminepentaacetic acid form stable complexes with many heavy metal ions, excelling as cation chelants especially in the field of radiopharmacy. The aim of this work is to characterize, by using the Time Differential Perturbed Angular Correlations (TDPAC) technique, the hyperfine interactions at hafnium sites in hafnium diethylenetriaminepentaacetate and to investigate their evolution as temperature increases. TDPAC results for KHfDTPA.3H{sub 2}O obtained by chemical synthesis yield a well defined and highly asymmetric interaction of quadrupole frequency ω{sub Q} = 141 Mrad/s, which is consistent with the existence of a unique site for the metal in the crystal lattice. The thermal behaviour of the chelate is investigated by means of differential scanning calorimetry and thermogravimetrical analyses revealing that an endothermic dehydration of KHfDTPA.3H{sub 2}O takes place in one step between 80 C and 180 C. The anhydrous KHfDTPA thus arising is characterized by a fully asymmetric and well defined interaction of quadrupole frequency ω{sub Q} = 168 Mrad/s. (orig.)

  7. Rare-earth hafnium oxide materials for magnetohydrodynamic (MHD) generator application

    Energy Technology Data Exchange (ETDEWEB)

    Marchant, D. D; Bates, J. L.

    1979-01-01

    Several ceramic materials based on rare-earth hafnium oxides have been identified as potential high-temperature electrodes and low-temperature current leadouts for open cycle coal-fired MHD generator channels. The electrode-current leadouts combination must operate at temperatures between 400 and 2000K with an electrical conductivity greater than 10/sup -2/ ohm/sup -1/ cm/sup -1/. The electrodes will be exposed to flowing (linear flow rates up to 100 m/s) potassium seeded coal combustion gases (plasma core temperatures between 2400 to 3200/sup 0/K) and coal slag. During operation the electrodes must conduct direct electric current at densities near 1.5 amp/cm/sup 2/. Consequently, the electrodes must be resistant to electrochemical decompositions and interactions with both the coal slag and potassium salts (e.g., K/sub 2/SO/sub 4/, K/sub 2/CO/sub 3/). The current leadout materials are placed between the hot electrodes and the water-cooled copper structural members and must have electrical conductivities greater than 10/sup -2/ ohm/sup -1/ cm/sup -1/ between 1400 and 400/sup 0/K. The current leadouts must be thermally and electrochemically compatible with the electrode, copper, and potassium salts. Ideally, the electrodes and current leadouts should exhibit minimal ionic conductivity. The fabrication, electrical conductivity, and electrochemical corrosion of rare-earth hafnium oxide materials are discussed. (WHK)

  8. Thermal behaviour of hafnium diethylenetriaminepentaacetate studied using the perturbed angular correlation technique

    International Nuclear Information System (INIS)

    Chain, Cecilia Y.; Rivas, Patricia

    2014-01-01

    Polyaminecarboxilic ligands like diethylenetriaminepentaacetic acid form stable complexes with many heavy metal ions, excelling as cation chelants especially in the field of radiopharmacy. The aim of this work is to characterize, by using the Time Differential Perturbed Angular Correlations (TDPAC) technique, the hyperfine interactions at hafnium sites in hafnium diethylenetriaminepentaacetate and to investigate their evolution as temperature increases. TDPAC results for KHfDTPA.3H 2 O obtained by chemical synthesis yield a well defined and highly asymmetric interaction of quadrupole frequency ω Q = 141 Mrad/s, which is consistent with the existence of a unique site for the metal in the crystal lattice. The thermal behaviour of the chelate is investigated by means of differential scanning calorimetry and thermogravimetrical analyses revealing that an endothermic dehydration of KHfDTPA.3H 2 O takes place in one step between 80 C and 180 C. The anhydrous KHfDTPA thus arising is characterized by a fully asymmetric and well defined interaction of quadrupole frequency ω Q = 168 Mrad/s. (orig.)

  9. Preparation, structure and properties of hafnium compounds in the system Hf-C-N-O

    International Nuclear Information System (INIS)

    Brundiers, G.D.

    1975-08-01

    Highly dense, homogenous and single phase hafnium carbonitride samples (with low oxygen content) were prepared in the whole concentration range of the ternary cubic carbonitrides. Stoichiometric hafnium oxicarbides were also prepared within the range of solubility. The procedure involved the hot pressing of powders of HfC, HfN, Hf, Hf-Oxide and carbon at temperatures of 3,000 0 C and pressures up to 550 kpf/cm 2 using a novel technique. Small single crystals of slightly substoichiometric HfN were also repared. The densification of the powders was studied as a function of the non-metal concentration. Carbonitrides with N/Hf ratio of 0.37 were prepared in a high temperature autoclave operating at medium pressures by the reaction of HfC with nitrogen. All the samples were characterized by density measurements, chemical, X-ray and metallographic analysis and in some cases with the aid of quantitative metallography and microprobe analysis. Typical properties investigated were lattice parameter, thermal expansion, microhardness and electrical resistivity as function of the non-metal content. For specific concentrations extreme values in the properties are attained. With the aid of the valence electron concentration (VEC) parameter, the properties can be correlated with the density of states of electrons at the Fermi level. (orig./HK) [de

  10. Titrimetric determination of thiocyanate in solutions of the hafnium-zirconium separation process

    International Nuclear Information System (INIS)

    Vazquez, Cristina; Botbol, Moises; Hernandez, M.H.

    1980-01-01

    The control of the thiocyanate concentration is necessary during the process of separating hafnium from zirconium by the hexone-thiocyanate method. Said control is carried out by titrimetric determination of thiocyanate in aqueous and organic solutions containing hydrochloric acid and ammonium thiocyanate in presence or absence of zirconium and/or hafnium. The method consists in a redox volumetric analysis using a cerium (IV) salt as titrating agent, and ferroine as the final point indicator. Owing to the instability of thiocyanate in an acid medium it is necessary to know previously if the decomposition of solutions with different concentration of ammonium thiocyanate and hydrochloric acid may have an influence upon the analytic results or may even invalidate them. In order to obtain reliable results, it must be taken into account that the stability of the solutions depends on the thiocyanate concentration, the acidity and the time elapsed from the moment the sample is taken until the test is performed. The decomposition process can be slowed down by cooling the solutions. This method allows to control the plant and does not require any special equipment. (M.E.L) [es

  11. Molecular structure, vibrational, HOMO-LUMO, MEP and NBO analysis of hafnium selenite

    Science.gov (United States)

    Yankova, Rumyana; Genieva, Svetlana; Dimitrova, Ginka

    2017-08-01

    In hydrothermal condition hafnium selenite with estimated chemical composition Hf(SeO3)2·n(H2O) was obtained and characterized by powder X-Ray diffraction, IR spectroscopy and thermogravimetrical analysis. The composition of the obtained crystalline phase was established as dihydrate of tetraaqua complex of the hafnium selenite [Hf(SeO3)2(H2O)4]·2H2O. The results of the thermogravimetrical analysis are shown that the two hydrated water molecules are released in the temperature interval 80-110°C, while the four coordinated water molecules - at 210-300°C. By DFT method, with Becke's three parameter exchange-functional combined with gradient-corrected correlation functional of Lee, Yang and Parr and 6-31G(d), 6-311 + G(d,p) basis sets and LANL2DZ for Hf atom were calculated the molecular structure, vibrational frequencies and thermodynamic properties of the structure. The UV-Vis spectra and electronic properties are presented. The energy and oscillator strength calculated by time-dependent density functional theory corresponds well with the experimental ones. Molecular electrostatic potential (MEP) was performed. Mulliken population analysis on atomic charges was also calculated. The stability and intramolecular interactions are interpreted by NBO analysis.

  12. Correlations between nuclear data and results of integral slab experiments. Case of hafnium

    International Nuclear Information System (INIS)

    Palau, J.M.

    1997-01-01

    The aim of this thesis was to evaluate how much integral slab experiments can both reduce discrepancies between experimental results and calculations, and improve the knowledge of hafnium isotopes neutronic parameters by an adapted sensitivity and uncertainty method. A statistical approach, based on the generalized least squares method and perturbation theory, has been incorporated into our calculation system in order to deduce microscopic cross-section adjustments from observed integral measurements on this particular 'mock-up' reactor. In this study it has been established that the correlations between integral parameters and hafnium capture cross-sections enable specific variations in the region of resolved resonances at the level of multigroup and punctual cross-sections recommended data (JEF-2.2 evaluation) to be highlighted. The use of determinist methods (APOLLO2 code) together with Monte Carlo- type simulations (TRIPOLI4 code) enabled a depth analysis of the modelling approximations to be carried out. Furthermore, the sensitivity coefficient validation technique employed leads to a reliable assessment of the quality of the new basic nuclear data. In this instance, the adjustments proposed for certain isotope 177 Hf resonance parameters reduce, after error propagation, by 3 to 5 per cent the difference between experimental results and calculations related to this absorbent's efficiency. Beyond this particular application, the qualification methodology integrated in our calculation system should enable other basic sizing parameters to be treated (chemical / geometric data or other unexplored nuclear data) to make technological requirements less stringent. (author)

  13. Correlations between nuclear data and integral slab experiments: the case of hafnium

    International Nuclear Information System (INIS)

    Palau, J.M.

    1999-01-01

    The aim of this work was to evaluate how much integral slab experiments can both reduce discrepancies between experimental results and calculations, and improve the knowledge of hafnium isotopes neutronic parameters by an adapted sensitivity and uncertainty method. A statistical approach, based on the generalized least squares method and perturbation theory, has been incorporated into our calculation system in order to deduce microscopic cross-section adjustments from observed integral measurements on this particular 'mock-up' reactor.In this study it has been established that the correlations between integral parameters and hafnium capture cross-sections enable specific variations in the region of resolved resonances at the level of multigroup and punctual cross-sections recommended data (JEF-2.2 evaluation) to be highlighted. The use of determinist methods together with Monte Carlo- type simulations enabled a depth analysis of the modelling approximations to be carried out. Furthermore, the sensitivity coefficient validation technique employed leads to a reliable assessment of the quality of the new basic nuclear data. In this instance, the adjustments proposed for certain isotope 177 Hf resonance parameters reduce, after error propagation, by 3 to 5 per cent the difference between experimental results and calculations related to this absorbent's efficiency. Beyond this particular application, the qualification methodology integrated in our calculation system should enable other basic sizing parameters to be treated (chemical / geometric data or other unexplored nuclear data) to make technological requirements less stringent. (author)

  14. Highly substituted zirconium and hafnium cyclopentadienyl bifunctional β-diketiminate complexes – Synthesis, structure, and catalytic activity towards ethylene polymerization

    Czech Academy of Sciences Publication Activity Database

    Havlík, A.; Lamač, Martin; Pinkas, Jiří; Varga, Vojtěch; Růžička, A.; Olejník, R.; Horáček, Michal

    2015-01-01

    Roč. 786, JUN 2015 (2015), s. 71-80 ISSN 0022-328X R&D Projects: GA ČR GAP106/10/0924 Institutional support: RVO:61388955 Keywords : Zirconium * Hafnium * Cyclopentadienyl Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 2.336, year: 2015

  15. Differential perturbed angular correlation: use of physico-chemical study of some hafnium complexes derivates of hydroxy acids and EDTA

    International Nuclear Information System (INIS)

    Silveira, J.G. da.

    1981-01-01

    Measures of quadrupolar interaction to nucleus level of the metal, in some hafnium complexes are presented, including the analysis by combustion, microanalysis, infrared spectroscopy and thermogravimetry. The hyperfine interaction parameters, the temperature effects and the thermal neutrons capture effects over the irradiated Hf Y (Y = EDTA) are also studied. (author)

  16. Therapeutical radiopharmaceuticals based In vivo generator system [{sup 166} Dy] Dy/{sup 166} Ho; Radiofarmacos terapeuticos basados en un sistema de generador In vivo [{sup 166}Dy] Dy/{sup 166}Ho

    Energy Technology Data Exchange (ETDEWEB)

    Ferro F, G.; Garcia S, L.; Monroy G, F.; Tendilla, J.I. [Gerencia de Aplicaciones Nucleares en la Salud, ININ, A.P. 18-1027, 11801 Mexico D.F. (Mexico); Pedraza L, M.; Murphy, C.A. de [Departamento de Medicina Nuclear, Instituto Nacional de Pediatria, Mexico D.F. (Mexico)

    2002-07-01

    At the idea to administer to a patient a molecule containing in it structure a father radionuclide, with a half life enough large which allows to the radiolabelled molecule to take up position specifically in a white tissue and decaying In vivo to the daughter radionuclide with properties potentially therapeutic, it is known as In vivo generator system. In this work the preparation and the preliminary dosimetric valuations of radiopharmaceuticals based In vivo generator system {sup 166} Dy Dy/{sup 166} Ho for applications in radioimmunotherapy, in the treatment of the rheumatoid arthritis and in the bone marrow ablation (m.o.) for candidates patients to bone marrow transplant are presented. (Author)

  17. 166Ho-chitosan as a radiation synovectomy agent - biocompatibility study of 166Ho-chitosan in rabbits

    International Nuclear Information System (INIS)

    Kim, Sug Jun; Lee, Soo Yong; Jeon, Dae Geun; Lee Jong Seok

    1997-01-01

    Radiation synovectomy is a noninvasive therapy that has been investigated as an alternative to surgical synovectomy. It is been successfully employed in the treatment of synovitis in rheumatoid arthrits and other inflammatory arthropathies. We developed the 166 Ho-chitosan complex for possible use as a radiation synovectomy agent. Holmium is the more practical isotope based on its higher radioactivity and logner half-life. And isotope based on its higher radioactivity and logner half-life. And chitosan is ideal and suitable particles based on its soluble and biodegradable characteristics. So we investigated the biocompatibility of the 166 Ho-chitosan complex to evaluated the suitability as a radiation synovectomy agent. In this study, we performed in vivo and in vitro stability test and biodistribution test. Our results indicate that 166 Ho-chitosan may be an effective radiopharmaceutical for radiation synovectomy. (author). 30 refs., 7 tabs

  18. {sup 166}Ho-chitosan as a radiation synovectomy agent - biocompatibility study of {sup 166}Ho-chitosan in rabbits

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Sug Jun; Lee, Soo Yong; Jeon, Dae Geun; Seok, Lee Jong [Korea Cancer Center Hospital, Seoul (Korea, Republic of)

    1997-01-01

    Radiation synovectomy is a noninvasive therapy that has been investigated as an alternative to surgical synovectomy. It is been successfully employed in the treatment of synovitis in rheumatoid arthrits and other inflammatory arthropathies. We developed the {sup 166}Ho-chitosan complex for possible use as a radiation synovectomy agent. Holmium is the more practical isotope based on its higher radioactivity and logner half-life. And isotope based on its higher radioactivity and logner half-life. And chitosan is ideal and suitable particles based on its soluble and biodegradable characteristics. So we investigated the biocompatibility of the {sup 166}Ho-chitosan complex to evaluated the suitability as a radiation synovectomy agent. In this study, we performed in vivo and in vitro stability test and biodistribution test. Our results indicate that {sup 166}Ho-chitosan may be an effective radiopharmaceutical for radiation synovectomy. (author). 30 refs., 7 tabs.

  19. Cytotoxic and genotoxic effect of the [166Dy]Dy/166Ho-EDTMP in vivo generator system in mice

    International Nuclear Information System (INIS)

    Pedraza-Lopez, Martha; Ferro-Flores, Guillermina; Arteaga de Murphy, Consuelo; Morales-Ramirez, Pedro; Piedras-Ross, Josefa; Murphy-Stack, Eduardo; Hernandez-Oviedo, Omar

    2004-01-01

    Multiple myeloma and other hematological malignancies have been treated by myeloablative radiotherapy/chemotherapy and subsequent stem cell transplantation. [ 166 Dy]Dy/ 166 Ho-ethylenediaminetetramethylene phosphonate (EDTMP) forms a stable in vivo generator system with selective skeletal uptake in mice; therefore, it could work as a potential and improved agent for marrow ablation. Induced bone marrow cytotoxicity and genotoxicity are determined by the reduction of reticulocytes (RET) and elevation of micronucleated reticulocyte (MN-RET) in peripheral blood and ablation by bone marrow histological studies. The aim of this study was to determine the bone marrow cytotoxic and genotoxic effect of the [ 166 Dy]Dy/ 166 Ho-EDTMP in vivo generator system in mice and to evaluate by histopathology its myeloablative potential. Enriched 166 Dy 2 O 3 was irradiated and [ 166 Dy]DyCl 3 was added to EDTMP in phosphate buffer (pH 8.0) in a molar ratio of 1:1.75. QC was determined by TLC. Dy-EDTMP complex was prepared the same way with nonirradiated dysprosium oxide. A group of BALB/c mice were intraperitoneally injected with the radiopharmaceutical and two groups of control animals were injected with the cold complex and with 0.9% sodium chloride, respectively. A blood sample was taken at the beginning of the experiments and every 48 h for 12 days postinjection. The animals were sacrificed, organs of interest taken out and the radioactivity determined. The femur was used for histological studies. Flow cytometry analysis was used to quantify the frequency of RET and MN-RET in the blood samples. The MCNP4B Monte Carlo computer code was used for dosimetry calculations. Radiochemical purity was 99% and the mean specific activity was 1.3 MBq/mg. The RET and MN-RET frequency were statistically different in the treatment at the end of the 12-day period demonstrating cytotoxicity and genotoxicity induced by the in vivo generator system. The histology studies show that there was

  20. 40 CFR 166.49 - Public notice of crisis exemptions.

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 23 2010-07-01 2010-07-01 false Public notice of crisis exemptions... PROGRAMS EXEMPTION OF FEDERAL AND STATE AGENCIES FOR USE OF PESTICIDES UNDER EMERGENCY CONDITIONS Crisis Exemptions § 166.49 Public notice of crisis exemptions. (a) Periodic notices. At least quarterly, the...

  1. 27 CFR 40.166 - Default, prepayment of tax required.

    Science.gov (United States)

    2010-04-01

    ... 27 Alcohol, Tobacco Products and Firearms 2 2010-04-01 2010-04-01 false Default, prepayment of tax... Payment of Taxes on Tobacco Products § 40.166 Default, prepayment of tax required. Where a check or money... tax due thereunder, or where a manufacturer is otherwise in default in payment of tax on tobacco...

  2. The E166 experiment: Development of an undulator-based ...

    Indian Academy of Sciences (India)

    A longitudinal polarized positron beam is foreseen for the international linear collider (ILC). A proof-of-principle experiment has been performed in the final focus test beam at SLAC to demonstrate the production of polarized positrons for implementation at the ILC. The E166 experiment uses a 1 m long helical undulator in a ...

  3. 26 CFR 1.166-2 - Evidence of worthlessness.

    Science.gov (United States)

    2010-04-01

    ... accounting.” The words “ELECTION UNDER § 1.166-2(d)(3)” must be typed or legibly printed at the top of the... connection with its most recent examination involving the bank's loan review process, the bank's supervisory... procedure prescribed hereunder) that the bank maintains and applies loan loss classification standards that...

  4. 27 CFR 555.166 - Seizure or forfeiture.

    Science.gov (United States)

    2010-04-01

    ... 27 Alcohol, Tobacco Products and Firearms 3 2010-04-01 2010-04-01 false Seizure or forfeiture. 555... EXPLOSIVES, DEPARTMENT OF JUSTICE EXPLOSIVES COMMERCE IN EXPLOSIVES Unlawful Acts, Penalties, Seizures and Forfeitures § 555.166 Seizure or forfeiture. Any explosive materials involved or used or intended to be used...

  5. 7 CFR 400.166 - Obligations of the Corporation.

    Science.gov (United States)

    2010-01-01

    ... 7 Agriculture 6 2010-01-01 2010-01-01 false Obligations of the Corporation. 400.166 Section 400... CORPORATION, DEPARTMENT OF AGRICULTURE GENERAL ADMINISTRATIVE REGULATIONS Reinsurance Agreement-Standards for... Corporation. The Agreement will include the following among the obligations of the Corporation. (a) The...

  6. Preparation of .sup.166./sup.Ho-Macroaggregates and .sup.166./sup.Ho-chitosan for the endoradiotherapy

    Czech Academy of Sciences Publication Activity Database

    Melichar, František; Kropáček, Martin; Eigner-Henke, Kateřina; Křížová, V.; Konopková, M.; Lang, O.; Mirzajevová, Marcela

    2002-01-01

    Roč. 1, č. 2 (2002), s. 314 ISSN 1450-1147. [Abstracts of the Congress of the World Federation of Nuclear Medicine and Biology. 29.09.2002-02.10.2002, Santiago] R&D Projects: GA MZd NM6828; GA AV ČR KSK4055109 Keywords : Holmium-166 * radionuclide synovectomy Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders

  7. A thermally robust and thickness independent ferroelectric phase in laminated hafnium zirconium oxide

    Directory of Open Access Journals (Sweden)

    S. Riedel

    2016-09-01

    Full Text Available Ferroelectric properties in hafnium oxide based thin films have recovered the scaling potential for ferroelectric memories due to their ultra-thin-film- and CMOS-compatibility. However, the variety of physical phenomena connected to ferroelectricity allows a wider range of applications for these materials than ferroelectric memory. Especially mixed HfxZr1-xO2 thin films exhibit a broad compositional range of ferroelectric phase stability and provide the possibility to tailor material properties for multiple applications. Here it is shown that the limited thermal stability and thick-film capability of HfxZr1-xO2 can be overcome by a laminated approach using alumina interlayers.

  8. Surface State Capture Cross-Section at the Interface between Silicon and Hafnium Oxide

    Directory of Open Access Journals (Sweden)

    Fu-Chien Chiu

    2013-01-01

    Full Text Available The interfacial properties between silicon and hafnium oxide (HfO2 are explored by the gated-diode method and the subthreshold measurement. The density of interface-trapped charges, the current induced by surface defect centers, the surface recombination velocity, and the surface state capture cross-section are obtained in this work. Among the interfacial properties, the surface state capture cross-section is approximately constant even if the postdeposition annealing condition is changed. This effective capture cross-section of surface states is about 2.4 × 10−15 cm2, which may be an inherent nature in the HfO2/Si interface.

  9. Thermal expansion studies on Hafnium titanate (HfTiO4)

    International Nuclear Information System (INIS)

    Panneerselvam, G.; Subramanian, G.G.S.; Antony, M.P.

    2006-01-01

    The lattice thermal expansion characteristics of hafnium titanate (HfTiO 4 ) have been studied by measuring the lattice parameter as a function of temperature by high temperature X-ray diffraction technique (HT-XRD) in the temperature range 298-1973K. Percentage linear thermal expansion and mean linear thermal expansion coefficients were computed from the lattice parameter data. The thermal expansion of HfTiO 4 is highly anisotropic. The expansivity along 'a' axis is large; as compared to the expansivity along 'b' axis which is negative below 1073 K. The percentage linear thermal expansion in the temperature range 298-1973 K along a, b and c axis are 2.74, 0.901 and 1.49 respectively. Thermal expansion values obtained in the present study are in reasonable agreement with the existing thermal expansion data. (author)

  10. Density and surface tension of melts of zirconium and hafnium fluorides with lithium fluoride

    International Nuclear Information System (INIS)

    Katyshev, S.F.; Artemov, V.V.; Desyatnik, V.N.

    1988-01-01

    A study was conducted to determine the temperature dependence of the density and surface tension of melts of LiF-ZrF 4 and LiF-HfF 4 . Density and surface tension were determined by the method of maximum pressure in an argon bubble. On the basis of experimental data over the entire concentration range the molar volumes and their relative deviations from the additive molar volumes were calculated for 1100 0 K. The positive deviations of the molar volumes from additivity in the LiF-HfF 4 system (22.45%) were greater than in the LiF-ZrF 4 system (15.75%). This indicated that the reaction with lithium fluoride is intensified with the switch to the hafnium fluoride. Results also demonstrated that the fluorides are surface-active components in the molten mixtures

  11. Extraction of hafnium with chelating agents from aqueous-alcoholic solutions

    International Nuclear Information System (INIS)

    Hala, J.; Prihoda, J.

    1975-01-01

    The extraction was studied of hafnium into solutions of N-benzoyl-N-phenylhydroxylamine, 2-thenoyltrifluoroacetone and di-n-butylphosphoric acid in benzene, toluene, chloroform and tetrachloromethane from aqueous alcoholic solutions with a formal acidity of 2M-HClO 4 . Methyl-, ethyl-, n- and isopropyl- and tert-butyl alcohol were used as organic components in the mixed aqueous-organic phase. In the extraction into N-benzoyl-N-phenylhydroxylamine the presence of the alcohols resulted in synergic effects analogous to the previously described extraction by substituted benzoylpyrazolone. With the other two extractants, the effect of the alcohols was antagonistic, due to the interaction of alcohol or water with the reagent in the organic phase, and to the decrease in the reagent distribution constant. (author)

  12. Interface and oxide traps in high-κ hafnium oxide films

    International Nuclear Information System (INIS)

    Wong, H.; Zhan, N.; Ng, K.L.; Poon, M.C.; Kok, C.W.

    2004-01-01

    The origins of the interface trap generation and the effects of thermal annealing on the interface and bulk trap distributions are studied in detail. We found that oxidation of the HfO 2 /Si interface, removal of deep trap centers, and crystallization of the as-deposited film will take place during the post-deposition annealing (PDA). These processes will result in the removal of interface traps and deep oxide traps and introduce a large amount of shallow oxide traps at the grain boundaries of the polycrystalline film. Thus, trade-off has to be made in considering the interface trap density and oxide trap density when conducting PDA. In addition, the high interface trap and oxide trap densities of the HfO 2 films suggest that we may have to use the SiO 2 /HfO 2 stack or hafnium silicate structure for better device performance

  13. Wake-up effects in Si-doped hafnium oxide ferroelectric thin films

    International Nuclear Information System (INIS)

    Zhou, Dayu; Xu, Jin; Li, Qing; Guan, Yan; Cao, Fei; Dong, Xianlin; Müller, Johannes; Schenk, Tony; Schröder, Uwe

    2013-01-01

    Hafnium oxide based ferroelectric thin films have shown potential as a promising alternative material for non-volatile memory applications. This work reports the switching stability of a Si-doped HfO 2 film under bipolar pulsed-field operation. High field cycling causes a “wake-up” in virgin “pinched” polarization hysteresis loops, demonstrated by an enhancement in remanent polarization and a shift of negative coercive voltage. The rate of wake-up is accelerated by either reducing the frequency or increasing the amplitude of the cycling field. We suggest de-pinning of domains due to reduction of the defect concentration at bottom electrode interface as origin of the wake-up

  14. Atom-vacancy ordering and magnetic susceptibility of nonstoichiometric hafnium carbide

    International Nuclear Information System (INIS)

    Gusev, A.I.; Zyryanova, A.N.

    1999-01-01

    Experimental results on magnetic susceptibility of nonstoichiometric hafnium carbide HfC y (0.6 0.71 , HfC 0.78 and HfC 0.83 in the range of 870-930 K the anomalies are revealed which are associated with superstructure short-range ordering in a non-metallics sublattice. It is shown that a short-range order in HfC 0.71 and HfC 0.78 carbides corresponds to Hf 3 C 2 ordered phase, and in HfC 0.83 carbide - to Hf 6 C 5 ordered phase. HfC 0.78 carbide is found to possesses zero magnetic susceptibility in temperature range 910-980 K [ru

  15. Sub-10 nm low current resistive switching behavior in hafnium oxide stack

    Energy Technology Data Exchange (ETDEWEB)

    Hou, Y., E-mail: houyi@pku.edu.cn, E-mail: lfliu@pku.edu.cn [Institute of Microelectronics, Peking University, 100871 Beijing (China); IMEC, Kapeldreef 75, B-3001 Heverlee (Belgium); Department of Physics and Astronomy, KU Leuven, Celestijnenlaan 200D, B-3001 Heverlee (Belgium); Celano, U.; Xu, Z.; Vandervorst, W. [IMEC, Kapeldreef 75, B-3001 Heverlee (Belgium); Department of Physics and Astronomy, KU Leuven, Celestijnenlaan 200D, B-3001 Heverlee (Belgium); Goux, L.; Fantini, A.; Degraeve, R.; Youssef, A.; Jurczak, M. [IMEC, Kapeldreef 75, B-3001 Heverlee (Belgium); Liu, L., E-mail: houyi@pku.edu.cn, E-mail: lfliu@pku.edu.cn; Cheng, Y.; Kang, J. [Institute of Microelectronics, Peking University, 100871 Beijing (China)

    2016-03-21

    In this letter, a tip-induced cell relying on the conductive atomic force microscope is proposed. It is verified as a referable replica of an integrated resistive random access memory (RRAM) device. On the basis of this cell, the functionality of sub-10 nm resistive switching is confirmed in hafnium oxide stack. Moreover, the low current switching behavior in the sub-10 nm dimension is found to be more pronounced than that of a 50 × 50 nm{sup 2} device. It shows better ON/OFF ratio and low leakage current. The enhanced memory performance is ascribed to a change in the shape of the conductive filament as the device dimensions are reduced to sub-10 nm. Therefore, device downscaling provides a promising approach for the resistance optimization that benefits the RRAM array design.

  16. Solvent extraction of hafnium(IV) by dinonylnaphthalene sulfonic acid from mixed aqueous-organic media

    International Nuclear Information System (INIS)

    Hala, J.; Piperkovova, H.

    1979-01-01

    The extraction of hafnium(IV) by heptane and toluene solutions of dinonylnaphthalene sulfonic acid (HD) from mixed aqueous-organic solutions has been studied. Alcohols, ketones, carboxylic acids, cyclic ethers, dimethylsulfoxide and dimethylformamide were used as the organic component of the mixed phase. Methanol, ethanol, formic acid and dioxane increased the extractability of Hf(IV) whereas other solvents showed only an antagonistic effect. The results were discussed from the point of view of the changes in micellar structure of HD, and compared with the uptake of Hf(IV) by resinous cation exchangers. The solubilization by HD of alcohols, carboxylic acids and dimethylsulfoxide was demonstrated by using the corresponding 14 C and 35 S labelled compounds. (author)

  17. Study of bulk Hafnium oxide (HfO2) under compression

    Science.gov (United States)

    Pathak, Santanu; Mandal, Guruprasad; Das, Parnika

    2018-04-01

    Hafnium oxide (HfO2) is a technologically important material. This material has K-value of 25 and band gap 5.8 eV. A k value of 25-30 is preferred for a gate dielectric [1]. As it shows good insulating and capacitive properties, HfO2 is being considered as a replacement to SiO2 in microelectronic devices as gate dielectrics. On the other hand because of toughening mechanism due to phase transformation induced by stress field observed in these oxides, HFO2 has been a material of investigations in various configurations for a very long time. However the controversies about phase transition of HfO2 under pressure still exists. High quality synchrotron radiation has been used to study the structural phase transition of HfO2 under pressure.

  18. Separation of hafnium from zirconium in their tetrachloride solution in molten alkali metal chlorides

    Energy Technology Data Exchange (ETDEWEB)

    Salyulev, A B; Kudyakov, V Ya; Smirnov, M V; Moskalenko, N I [AN SSSR, Sverdlovsk. Inst. Ehlektrokhimii

    1984-08-01

    The coefficient of HfCl/sub 4/ and ZrCl/sub 4/ separation in the process of vapour sublimation from their solutions in molten NaCl, KCl, CsCl, NaCl-KCl and NaCl-CsCl equimolar mixtures is found to vary in the series from approximately 1.10 to approximately 1.22 and practically not to depend on the temperature (in the 600-910 deg) range and concentration (2-25 mol.% ZrCl/sub 4/+HfCl/sub 4/). HfCl/sub 4/ and ZrCl/sub 4/ are shown to form almost perfect solutions with each other, which in their turn form imperfect solutions with molten alkali metal chlorides, with the strength of hafnium complex chloride anions increasing higher than that of zirconium in the series from NaCl to CsCl.

  19. Separation of hafnium from zirconium in their tetrachloride solution in molten alkali metal chlorides

    International Nuclear Information System (INIS)

    Salyulev, A.B.; Kudyakov, V.Ya.; Smirnov, M.V.; Moskalenko, N.I.

    1984-01-01

    The coefficient of HfCl 4 and ZrCl 4 separation in the process of vapour sublimation from their solutions in molten NaCl, KCl, CsCl, NaCl-KCl and NaCl-CsCl equimolar mixtures is found to vary in the series from approximately 1.10 to approximately 1.22 and practically not to depend on the temperature (in the 600-910 deg) range and concentration (2-25 mol.% ZrCl 4 +HfCl 4 ). HfCl 4 and ZrCl 4 are shown to form almost perfect solutions with each other, which in their turn form imperfect solutions with molten alkali metal chlorides, with the strength of hafnium complex chloride anions increasing higher than that of zirconium in the series from NaCl to CsCl

  20. Influence of plastic deformation on nitriding of a molybdenum-hafnium alloy

    International Nuclear Information System (INIS)

    Lakhtin, Yu.M.; Kogan, Ya.D.; Shashkov, D.P.; Likhacheva, T.E.

    1982-01-01

    The influence of a preliminary plastic strain on the structure and properties of molybdenum alloy with 0.2 wt.% Hf upon nitriding in the ammonia medium at 900-1200 deg C during 1-6 h is investigated. The study of microhardness distribution across the nitrided layer thickness has shown that with increase of the degree of preliminary plastic strain up to 50 % the nitrided layer hardness decreases and with further reduction growth up to 90 % - increases. Nitriding sharply (hundred times) increases wear resistance of molybdenum alloy with hafnium addition. At the reduction degree 25 % the wear resistance is less than at other values of percentage reduction in area owing to the minimum thickness of the nitride zone. The alloy strained before nitriding by 25 % has shown the best results during heat resistance testing

  1. Hafnium at subduction zones: isotopic budget of input and output fluxes

    International Nuclear Information System (INIS)

    Marini, J.Ch.

    2004-05-01

    Subduction zones are the primary regions of mass exchanges between continental crust and mantle of Earth through sediment subduction toward the earth's mantle and by supply of mantellic magmas to volcanic arcs. We analyze these mass exchanges using Hafnium and Neodymium isotopes. At the Izu-Mariana subduction zone, subducting sediments have Hf and Nd isotopes equivalent to Pacific seawater. Altered oceanic crust has Hf and Nd isotopic compositions equivalent to the isotopic budget of unaltered Pacific oceanic crust. At Luzon and Java subduction zones, arc lavas present Hf isotopic ratios highly radiogenic in comparison to their Nd isotopic ratios. Such compositions of the Luzon and Java arc lavas are controlled by a contamination of their sources by the subducted oceanic sediments. (author)

  2. Rapid screening of nuclear grade zirconium silicate without separation of hafnium from the bulk matrix

    International Nuclear Information System (INIS)

    Venkatesh, Manisha; Sharma, P.K.; Avhad, D.K.; Basu, H.; Singhal, R.K.; Reddy, A.V.R.

    2014-01-01

    Zirconium silicate, also zirconium orthosilicate, (ZrSiO 4 ) is a chemical compound, and occurs in nature as zircon, a silicate mineral. The concentration of Hafnium in nuclear grade Zirconium must be less than 0.2% w/w of Zr. In view of this it must be accurately chemically characterized before issuing a certification for export under non nuclear category. As the chemistry of Zr and Hf is similar, it is difficult to separate Hf by direct wet chemical method. During this work, concentration of Hf in zirconium silicate was measured by Field Portable X-ray Fluorescence (FPXRF) and results obtained were validated by using detailed chemical method. FPXRF spectrometry has become a common analytical technique for on-site screening and fast turnaround analysis of contaminant elements in environmental samples

  3. Conservation and diversification of the miR166 family in soybean and potential roles of newly identified miR166s.

    Science.gov (United States)

    Li, Xuyan; Xie, Xin; Li, Ji; Cui, Yuhai; Hou, Yanming; Zhai, Lulu; Wang, Xiao; Fu, Yanli; Liu, Ranran; Bian, Shaomin

    2017-02-01

    microRNA166 (miR166) is a highly conserved family of miRNAs implicated in a wide range of cellular and physiological processes in plants. miR166 family generally comprises multiple miR166 members in plants, which might exhibit functional redundancy and specificity. The soybean miR166 family consists of 21 members according to the miRBase database. However, the evolutionary conservation and functional diversification of miR166 family members in soybean remain poorly understood. We identified five novel miR166s in soybean by data mining approach, thus enlarging the size of miR166 family from 21 to 26 members. Phylogenetic analyses of the 26 miR166s and their precursors indicated that soybean miR166 family exhibited both evolutionary conservation and diversification, and ten pairs of miR166 precursors with high sequence identity were individually grouped into a discrete clade in the phylogenetic tree. The analysis of genomic organization and evolution of MIR166 gene family revealed that eight segmental duplications and four tandem duplications might occur during evolution of the miR166 family in soybean. The cis-elements in promoters of MIR166 family genes and their putative targets pointed to their possible contributions to the functional conservation and diversification. The targets of soybean miR166s were predicted, and the cleavage of ATHB14-LIKE transcript was experimentally validated by RACE PCR. Further, the expression patterns of the five newly identified MIR166s and 12 target genes were examined during seed development and in response to abiotic stresses, which provided important clues for dissecting their functions and isoform specificity. This study enlarged the size of soybean miR166 family from 21 to 26 members, and the 26 soybean miR166s exhibited evolutionary conservation and diversification. These findings have laid a foundation for elucidating functional conservation and diversification of miR166 family members, especially during seed development or

  4. Extraction of hafnium by 1-phenyl-3-methyl-4-benzoyl-5-pyralozone from aqueous-alcoholic solutions

    International Nuclear Information System (INIS)

    Hala, J.; Prihoda, J.

    1975-01-01

    Extraction of hafnium by 1-phenyl-3-methyl-4-benzoyl-5-pyrazolone (HL) in benzene, toluene, chloroform and tetrachloromethane from aqueous-alcoholic solutions of the formal acidity of 2M-HClO 4 was studied. Methyl, ethyl, n- and isopropyl, tert-butyl and allyl alcohol as well as ethylene glycol monomethyl ether and propylene glycol were used as organic components of the mixed aqueous-organic phase. Their presence in some cases resulted in a synergic increase in the distribution ratio of hafnium. The increase is interpreted using the results of a slope analysis and measurements of the alcohol distribution and the relative permittivity of the organic phase. It is suggested that HfL 4 molecules were solvated by alcohol molecules in the organic phase. At high alcohol concentration synergism changed into antagonism. This was caused by changes in the distribution of HL and its interaction with the alcohol in the organic phase. (author)

  5. Hafnium isotope evidence for a transition in the dynamics of continental growth 3.2 Gyr ago.

    Science.gov (United States)

    Næraa, T; Scherstén, A; Rosing, M T; Kemp, A I S; Hoffmann, J E; Kokfelt, T F; Whitehouse, M J

    2012-05-30

    Earth's lithosphere probably experienced an evolution towards the modern plate tectonic regime, owing to secular changes in mantle temperature. Radiogenic isotope variations are interpreted as evidence for the declining rates of continental crustal growth over time, with some estimates suggesting that over 70% of the present continental crustal reservoir was extracted by the end of the Archaean eon. Patterns of crustal growth and reworking in rocks younger than three billion years (Gyr) are thought to reflect the assembly and break-up of supercontinents by Wilson cycle processes and mark an important change in lithosphere dynamics. In southern West Greenland numerous studies have, however, argued for subduction settings and crust growth by arc accretion back to 3.8 Gyr ago, suggesting that modern-day tectonic regimes operated during the formation of the earliest crustal rock record. Here we report in situ uranium-lead, hafnium and oxygen isotope data from zircons of basement rocks in southern West Greenland across the critical time period during which modern-like tectonic regimes could have initiated. Our data show pronounced differences in the hafnium isotope-time patterns across this interval, requiring changes in the characteristics of the magmatic protolith. The observations suggest that 3.9-3.5-Gyr-old rocks differentiated from a >3.9-Gyr-old source reservoir with a chondritic to slightly depleted hafnium isotope composition. In contrast, rocks formed after 3.2 Gyr ago register the first additions of juvenile depleted material (that is, new mantle-derived crust) since 3.9 Gyr ago, and are characterized by striking shifts in hafnium isotope ratios similar to those shown by Phanerozoic subduction-related orogens. These data suggest a transitional period 3.5-3.2 Gyr ago from an ancient (3.9-3.5 Gyr old) crustal evolutionary regime unlike that of modern plate tectonics to a geodynamic setting after 3.2 Gyr ago that involved juvenile crust generation by plate

  6. Results for heterogeneous poisoning of the critical HTR-test facility KAHTER using absorber elements containing hafnium and boron

    International Nuclear Information System (INIS)

    Drueke, V.; Filges, D.; Nabi, R.; Neef, R.D.; Paul, N.; Schaal, H.

    1979-10-01

    Experiments and checking computations for investigating the initial-core poisoning of the pebble bed high temperature reactor are described. Following the example of the THTR-300, THTR absorber elements poisoned with hafnium/boron were added to the THTR fuel- and graphite elements of the KAHTER core. Three different hafnium-boron poisoned core loadings, corresponding to 2.7, 5.3 and 8% reactivity compensation, were used in the experiments. For purposes of comparison, two cores exclusively boron poisoned were also studied. The poisoning of these cores correspond to 2.7 and 8% reactivity compensation. The experiments and checking computations should serve to test the accuracy of the theoretical models and data sets in modeling the reactivity effects of absorber poisoned elements in the THTR. In particular, the applicability of the nuclear data of hafnium and the treatment of resonance calculations should be verified. In addition, to determining critical masses and ksub(eff), special emphasis was placed in the experiments on the exact determination of all reactivity effects. In some cases, repeated loading of a configuration also provided a measure of the reproducibility of ksub(eff). The experiments were checked computationally using the GAMTEREX code package and the program system RSYST. These two computation packages contain different data bases, - although the hafnium data are identical -, and the computing models differ in certain phases of the calculations. Both code systems compute ksub(eff) values to within the present accuracy requirements, whereas the program system RSYST gives better agreement with experimental measurements. (orig.) 891 RW/orig. 892 RDG [de

  7. Automated production of no carrier added holmium-166

    International Nuclear Information System (INIS)

    Izard, M.E.; Dadchova, E.

    1996-01-01

    Full text: An automated system has been developed to produce no carrier added 166 Ho from the decay of 166 Dy produced by neutron activation of 164 Dy 2 O 3 . Targets consisting of 5-10 mg of 164 Dy 2 O 3 are irradiated in HIFAR at 5 x 10 13 n.s -1 .cm -2 for 12h then allowed to cool for 2 days. The irradiation can is then transferred to the automated system located in a 'hot' cell in the radiopharmaceutical research building. A two dimension robotic arm encompassing a grab and motorized screwdriver is used to open the irradiation can. A second arm carrying a teflon tube introduces 9M HCI into the can to dissolve the target. A second tube carries the dissolved target via a peristaltic pump to a heated vial where it is evaporated to dryness under a flow of N 2 . A Peltier cooled trap is used to prevent release of HCl fumes into the cell. A motorized syringe pump dispenses 1 mL of 0.1 M HNO 3 to redissolve the digest which is then transferred by peristaltic pump via a hollow fibre filter and auto injector into an Aminex- A5 HPLC column. 166 Dy is eluted from the column in 0.132 M α-HIBA into a heated cyclone flask and evaporated to dryness under a stream of N 2 heated to about 50 deg C. After two days the evaporated Dy/ 166 Ho digest is dissolved in another 1 mL of 0.1 M HNO 3 and injected onto the HPLC column. 166 Ho is collected in 20-25 mL of α-HIBA and evaporated to dryness as before at about 400 C to ensure complete decomposition of the α-HIBA. The product is finally dissolved in about I mL of 0.1 M HCI and pumped through a 0.22 μM filter to a product vial

  8. Ion-bombardment-induced reduction in vacancies and its enhanced effect on conductivity and reflectivity in hafnium nitride films

    Energy Technology Data Exchange (ETDEWEB)

    Gu, Zhiqing; Wang, Jiafu; Hu, Chaoquan; Zhang, Xiaobo; Dang, Jianchen; Gao, Jing; Zheng, Weitao [Jilin University, School of Materials Science and Engineering, Key Laboratory of Mobile Materials, MOE, and State Key Laboratory of Superhard Materials, Changchun (China); Zhang, Sam [Nanyang Technological University, School of Mechanical and Aerospace Engineering, Singapore (Singapore); Wang, Xiaoyi [Chinese Academy of Sciences, Key Laboratory of Optical System Advanced Manufacturing Technology, Changchun Institute of Optics, Fine Mechanics and Physics, Changchun (China); Chen, Hong [Jilin University, Department of Control Science and Engineering, Changchun (China)

    2016-08-15

    Although the role of ion bombardment on electrical conductivity and optical reflectivity of transition metal nitrides films was reported previously, the results were controversial and the mechanism was not yet well explored. Here, we show that proper ion bombardment, induced by applying the negative bias voltage (V{sub b}), significantly improves the electrical conductivity and optical reflectivity in rocksalt hafnium nitride films regardless of level of stoichiometry (i.e., in both near-stoichiometric HfN{sub 1.04} and over-stoichiometric HfN{sub 1.17} films). The observed improvement arises from the increase in the concentration of free electrons and the relaxation time as a result of reduction in nitrogen and hafnium vacancies in the films. Furthermore, HfN{sub 1.17} films have always much lower electrical conductivity and infrared reflectance than HfN{sub 1.04} films for a given V{sub b}, owing to more hafnium vacancies because of larger composition deviation from HfN exact stoichiometry (N:Hf = 1:1). These new insights are supported by good agreement between experimental results and theoretical calculations. (orig.)

  9. 25 CFR 166.1000 - Who owns the records associated with this part?

    Science.gov (United States)

    2010-04-01

    ... 25 Indians 1 2010-04-01 2010-04-01 false Who owns the records associated with this part? 166.1000 Section 166.1000 Indians BUREAU OF INDIAN AFFAIRS, DEPARTMENT OF THE INTERIOR LAND AND WATER GRAZING PERMITS Records § 166.1000 Who owns the records associated with this part? (a) Records are the property of...

  10. 40 CFR 166.50 - Reporting and recordkeeping requirements for crisis exemption.

    Science.gov (United States)

    2010-07-01

    ... requirements for crisis exemption. 166.50 Section 166.50 Protection of Environment ENVIRONMENTAL PROTECTION... EMERGENCY CONDITIONS Crisis Exemptions § 166.50 Reporting and recordkeeping requirements for crisis... a crisis exemption must be immediately reported to the Agency. (b) Final reports. (1) A report...

  11. Phylogenetic analysis reveals conservation and diversification of micro RNA166 genes among diverse plant species.

    Science.gov (United States)

    Barik, Suvakanta; SarkarDas, Shabari; Singh, Archita; Gautam, Vibhav; Kumar, Pramod; Majee, Manoj; Sarkar, Ananda K

    2014-01-01

    Similar to the majority of the microRNAs, mature miR166s are derived from multiple members of MIR166 genes (precursors) and regulate various aspects of plant development by negatively regulating their target genes (Class III HD-ZIP). The evolutionary conservation or functional diversification of miRNA166 family members remains elusive. Here, we show the phylogenetic relationships among MIR166 precursor and mature sequences from three diverse model plant species. Despite strong conservation, some mature miR166 sequences, such as ppt-miR166m, have undergone sequence variation. Critical sequence variation in ppt-miR166m has led to functional diversification, as it targets non-HD-ZIPIII gene transcript (s). MIR166 precursor sequences have diverged in a lineage specific manner, and both precursors and mature osa-miR166i/j are highly conserved. Interestingly, polycistronic MIR166s were present in Physcomitrella and Oryza but not in Arabidopsis. The nature of cis-regulatory motifs on the upstream promoter sequences of MIR166 genes indicates their possible contribution to the functional variation observed among miR166 species. Copyright © 2013 Elsevier Inc. All rights reserved.

  12. 40 CFR 166.32 - Reporting and recordkeeping requirements for specific, quarantine, and public health exemptions.

    Science.gov (United States)

    2010-07-01

    ... requirements for specific, quarantine, and public health exemptions. 166.32 Section 166.32 Protection of... AGENCIES FOR USE OF PESTICIDES UNDER EMERGENCY CONDITIONS Specific, Quarantine, and Public Health Exemptions § 166.32 Reporting and recordkeeping requirements for specific, quarantine, and public health...

  13. 40 CFR 166.20 - Application for a specific, quarantine, or public health exemption.

    Science.gov (United States)

    2010-07-01

    ..., or public health exemption. 166.20 Section 166.20 Protection of Environment ENVIRONMENTAL PROTECTION... EMERGENCY CONDITIONS Specific, Quarantine, and Public Health Exemptions § 166.20 Application for a specific, quarantine, or public health exemption. (a) General information required in an application for a specific...

  14. 29 CFR 1952.166 - Where the plan may be inspected.

    Science.gov (United States)

    2010-07-01

    ... copied during normal business hours at the following locations: Office of State Programs, Occupational... 29 Labor 9 2010-07-01 2010-07-01 false Where the plan may be inspected. 1952.166 Section 1952.166..., DEPARTMENT OF LABOR (CONTINUED) APPROVED STATE PLANS FOR ENFORCEMENT OF STATE STANDARDS Iowa § 1952.166 Where...

  15. 33 CFR 165.166 - Safety Zone: Macy's July 4th Fireworks, East River, NY.

    Science.gov (United States)

    2010-07-01

    ... Fireworks, East River, NY. 165.166 Section 165.166 Navigation and Navigable Waters COAST GUARD, DEPARTMENT... § 165.166 Safety Zone: Macy's July 4th Fireworks, East River, NY. (a) Regulated area. The following area...) in length, carrying persons for the purpose of viewing the fireworks, may take position in an area...

  16. Ocular brachytherapy with a holmium-166 irradiator device

    Energy Technology Data Exchange (ETDEWEB)

    Mourao, Arnaldo P. [Centro Federal de Educacao Tecnoloica de Minas Gerais (CEFET-MG), Belo Horizonte, MG (Brazil). Nucleo de Engenharia Hospitalar], e-mail: aprata@des.cefetmg.br; Campos, Tarcisio P.R. [Universidade Federal de Minas Gerais (UFMG), Belo Horizonte, MG (Brazil). Programa de Pos-graduacao em Ciencias e Tecnicas Nucleares], e-mail: campos@nuclear.ufmg.br

    2009-07-01

    The ocular brachytherapy is a method that allows controlling ocular tumors. However, the irradiation of the ocular area in high doses can bring damages mainly to the surrounding healthy tissue, such as lens, retina and bone tissue of the orbital area in growth phase. Brachytherapy in comparison to teletherapy allows a large reduction of the absorbed doses in the adjacent tissues avoiding deleterious effects. Various types of radionuclides can be applied to ocular brachytherapy. Those radionuclides shall be encapsulated and placed juxtaposed to the sclera, back to the tumor. Herein, a new device was developed to encapsulate the radioactive material. It can easily place back of the eyeball. A computational model of the ocular area was developed in order to simulate the spatial dose distribution promoted by the holmium-166 nuclide distributed inside the irradiator device. The simulations addressed a device placed on the surface of the sclera, rotated 90 deg taken at the normal axis forward to the lens. The simulation was carried on the code Monte Carlo MCNP5. The computational simulation generates the spatial dose distribution in the treated volume. All continuous beta and the discrete gamma and X-ray spectra emitted by the holmium-166 were incorporated on simulations. The results allow comparing the space dose distribution to other types of sources used for the same end. The sclera absorbed dose, the maximum apical tumor dose, as well as on the tumor base were investigated. Indeed, the tumor thickness defines the conditions of irradiation. The holmium-166 dose distribution provides a tool to propose a better and optimized protocol for ocular brachytherapy. (author)

  17. Ocular brachytherapy with a holmium-166 irradiator device

    International Nuclear Information System (INIS)

    Mourao, Arnaldo P.; Campos, Tarcisio P.R.

    2009-01-01

    The ocular brachytherapy is a method that allows controlling ocular tumors. However, the irradiation of the ocular area in high doses can bring damages mainly to the surrounding healthy tissue, such as lens, retina and bone tissue of the orbital area in growth phase. Brachytherapy in comparison to teletherapy allows a large reduction of the absorbed doses in the adjacent tissues avoiding deleterious effects. Various types of radionuclides can be applied to ocular brachytherapy. Those radionuclides shall be encapsulated and placed juxtaposed to the sclera, back to the tumor. Herein, a new device was developed to encapsulate the radioactive material. It can easily place back of the eyeball. A computational model of the ocular area was developed in order to simulate the spatial dose distribution promoted by the holmium-166 nuclide distributed inside the irradiator device. The simulations addressed a device placed on the surface of the sclera, rotated 90 deg taken at the normal axis forward to the lens. The simulation was carried on the code Monte Carlo MCNP5. The computational simulation generates the spatial dose distribution in the treated volume. All continuous beta and the discrete gamma and X-ray spectra emitted by the holmium-166 were incorporated on simulations. The results allow comparing the space dose distribution to other types of sources used for the same end. The sclera absorbed dose, the maximum apical tumor dose, as well as on the tumor base were investigated. Indeed, the tumor thickness defines the conditions of irradiation. The holmium-166 dose distribution provides a tool to propose a better and optimized protocol for ocular brachytherapy. (author)

  18. Nano-scale Radiotherapy-NBTXR3 Hafnium Oxide Nanoparticles as Promising Cancer Therapy

    International Nuclear Information System (INIS)

    Maggiorella, L.; Barouch, G.; Devaux, C.; Pottier, A.; Levy, L.; Deutsch, E.; Bourhis, J.; Borghi, E.

    2011-01-01

    Complete text of publication follows: Background: There is considerable interest in approaches that could improve the therapeutic window of radiotherapy, which represents a crucial modality of treatment in oncology. We present the rationale for designing NBTXR3 nanoparticles activated by radiotherapy and validate the concept. We performed the Monte Carlo calculations for the first time based on the 'local model' simulation that showed a dose enhancement of radiation to tumour cells of approximately nine-fold. NBTXR3 was shown to deposit high energy when the ionizing radiation source is 'on' and to have chemically inert behavior in cellular and subcellular systems demonstrated by very good systemic tolerance, thus decreasing potential health hazards. Material and Methods: We used conventional methods, implemented in different ways, to explore interactions of high Z matter and ionizing radiation with biological systems. In addition, microtomography was performed to explore the nanoparticle volume occupancy inside the tumour and its persistence overtime in mouse tumour models. The antitumour activity of NBTXR3 and tolerance were evaluated in Ewing tumour (A673) and fibrosarcoma (HT1080) using high energy source. Results and Conclusion: We created and developed NBTXR3 nanoparticles with a crystalline hafnium oxide core which provide high electron density structure and inert behavior in biological media. NBTXR3 nanoparticles' characteristics, size, charge and shape, allow for efficient interaction with biological entities, cell membrane binding and cellular uptake. The nanoparticles were shown to form clusters at the subcellular level in tumour models. Of most importance, we show NBTXR3 intra-tumour bioavailability with dispersion of nanoparticles in the three dimensions and persistence within the tumour structure, supporting the use of NBTXR3 as effective antitumour therapeutic agent. Antitumour activity of NBTXR3 showed marked advantage in terms of survival, tumour

  19. Hafnium-doped hydroxyapatite nanoparticles with ionizing radiation for lung cancer treatment.

    Science.gov (United States)

    Chen, Min-Hua; Hanagata, Nobutaka; Ikoma, Toshiyuki; Huang, Jian-Yuan; Li, Keng-Yuan; Lin, Chun-Pin; Lin, Feng-Huei

    2016-06-01

    Recently, photodynamic therapy (PDT) is one of the new clinical options by generating cytotoxic reactive oxygen species (ROS) to kill cancer cells. However, the optical approach of PDT is limited by tissue penetration depth of visible light. In this study, we propose that a ROS-enhanced nanoparticle, hafnium-doped hydroxyapatite (Hf:HAp), which is a material to yield large quantities of ROS inside the cells when the nanoparticles are bombarded with high penetrating power of ionizing radiation. Hf:HAp nanoparticles are generated by wet chemical precipitation with total doping concentration of 15mol% Hf(4+) relative to Ca(2+) in HAp host material. The results show that the HAp particles could be successfully doped with Hf ions, resulted in the formation of nano-sized rod-like shape and with pH-dependent solubility. The impact of ionizing radiation on Hf:HAp nanoparticles is assessed by using in-vitro and in-vivo model using A549 cell line. The 2',7'-dichlorofluorescein diacetate (DCFH-DA) results reveal that after being exposed to gamma rays, Hf:HAp could significantly lead to the formation of ROS in cells. Both cell viability (WST-1) and cytotoxicity (LDH) assay show the consistent results that A549 lung cancer cell lines are damaged with changes in the cells' ROS level. The in-vivo studies further demonstrate that the tumor growth is inhibited owing to the cells apoptosis when Hf:HAp nanoparticles are bombarded with ionizing radiation. This finding offer a new therapeutic method of interacting with ionizing radiation and demonstrate the potential of Hf:HAp nanoparticles in tumor treatment, such as being used in a palliative treatment after lung surgical procedure. Photodynamic therapy (PDT) is one of the new clinical options by generating cytotoxic reactive oxygen species (ROS) to kill cancer cells. Unfortunately, the approach of PDT is usually limited to the treatment of systemic disease and deeper tumor, due to the limited tissue penetration depth of visible

  20. Characterization of hafnium oxide resistive memory layers deposited on copper by atomic layer deposition

    Energy Technology Data Exchange (ETDEWEB)

    Briggs, B.D.; Bishop, S.M. [SUNY College of Nanoscale Science and Engineering, 255 Fuller Road, Albany, NY 12203 (United States); Leedy, K.D. [Air Force Research Laboratory, 2241 Avionics Circle, Wright Patterson Air Force Base, Dayton, OH 45433 (United States); Cady, N.C., E-mail: ncady@albany.edu [SUNY College of Nanoscale Science and Engineering, 255 Fuller Road, Albany, NY 12203 (United States)

    2014-07-01

    Hafnium oxide-based resistive memory devices have been fabricated on copper bottom electrodes. The HfO{sub x} active layers in these devices were deposited by atomic layer deposition (ALD) at 250 °C with tetrakis(dimethylamido)hafnium(IV) as the metal precursor and an O{sub 2} plasma as the reactant. Depth profiles of the HfO{sub x} by X-ray photoelectron spectroscopy and secondary ion mass spectroscopy revealed a copper concentration on the order of five atomic percent throughout the HfO{sub x} film. In addition to the Cu doped HfO{sub x}, a thin layer (20 nm) of Cu{sub x}O is present at the surface. This surface layer is believed to have formed during the ALD process, and greatly complicates the analysis of the switching mechanism. The resistive memory structures fabricated from the ALD HfO{sub x} exhibited non-polar resistive switching, independent of the top metal electrode (Ni, Pt, Al, Au). Resistive switching current voltage (I–V) curves were analyzed using Schottky emission and ionic hopping models to gain insight into the physical mechanisms underpinning the device behavior. During the forming process it was determined that, at voltages in excess of 2.5 V, an ionic hopping model is in good agreement with the I–V data. The extracted ion hopping distance ∼ 4 Å was within the range of interatomic spacing of HfO{sub 2} during the forming process consistent with ionic motion of Cu{sup 2+} ions. Lastly the on state I–V data was dominated at larger voltages by Schottky emission with an estimated barrier height of ∼ 0.5 eV and a refractive index of 2.59. The consequence of the Schottky emission analysis indicates the on state resistance to be a product of a Pt/Cu{sub 2}O/Cu filament(s)/Cu{sub 2}O/Cu structure. - Highlights: • HfO{sub 2} was grown via atomic layer deposition at 250 and 100 °C on Cu substrates. • A Cu{sub 2}O surface layer and Cu doping were observed in post-deposition of HfO{sub 2}. • Resistive memory devices were fabricated and

  1. Experimental dosimetry of Ho-166 bioglass seed polymer-protected

    Energy Technology Data Exchange (ETDEWEB)

    Nogueira, Luciana B.; Campos, Tarcisio P.R. [Universidade Federal de Minas Gerais (UFMG), Belo Horizonte, MG (Brazil). Dept. de Engenharia Nuclear. Programa de Pos-Graduacao em Ciencias e Tecnicas Nucleares

    2011-07-01

    This study aims to develop experimental dosimetry of Ho-166 bio glass seed for brachytherapy studies using GAFCHROMIC EBT2 radio chromium films. The methodology consists of placement of radio chromium films in a compressed breast phantom, along with bio glass polymer-protected seeds of [Si: Ca: Ho] and [Si: Ca: Ho: Zr]. The bio glass seeds were encapsulated with polyvinyl alcohol, before being activated and used in the study. The bio glass seeds were introduced into the breast phantom, along with radio chromium films for a period of 2 hours. After the exposure time, radio chromium films were removed from phantom and digitized for analysis in ImageDIG 2.0 program, which quantifies the intensity of RGB (Red, Green, Blue). The dose calculation was evaluated by Monte Carlo technique. Experimental and theoretical data were used to calibrate the dose distribution. The results were plotted on graphs and dose iso curves were obtained. As conclusion it is possible to perform dosimetry in Ho-166 seed brachytherapy using radio chromium films, limited to a short exposure time and small activity. (author)

  2. Experimental dosimetry of Ho-166 bioglass seed polymer-protected

    International Nuclear Information System (INIS)

    Nogueira, Luciana B.; Campos, Tarcisio P.R.

    2011-01-01

    This study aims to develop experimental dosimetry of Ho-166 bio glass seed for brachytherapy studies using GAFCHROMIC EBT2 radio chromium films. The methodology consists of placement of radio chromium films in a compressed breast phantom, along with bio glass polymer-protected seeds of [Si: Ca: Ho] and [Si: Ca: Ho: Zr]. The bio glass seeds were encapsulated with polyvinyl alcohol, before being activated and used in the study. The bio glass seeds were introduced into the breast phantom, along with radio chromium films for a period of 2 hours. After the exposure time, radio chromium films were removed from phantom and digitized for analysis in ImageDIG 2.0 program, which quantifies the intensity of RGB (Red, Green, Blue). The dose calculation was evaluated by Monte Carlo technique. Experimental and theoretical data were used to calibrate the dose distribution. The results were plotted on graphs and dose iso curves were obtained. As conclusion it is possible to perform dosimetry in Ho-166 seed brachytherapy using radio chromium films, limited to a short exposure time and small activity. (author)

  3. Biodistribution and excretion of radioactivity after the administration of 166Ho-chitosan complex (DW-166HC) into the prostate of rat

    International Nuclear Information System (INIS)

    Seong, Seung Kyoo; Ryu, Jei Man; Bae, Eun Jeong; Shin, Dong Hyuk; Shigematsu, Akiyo; Hatori, Yasuhiko; Nishigaki, Junko; Kwak, Cheol; Lee, Sang Eun; Park, Kyong Bae

    2005-01-01

    The objective of this study was to determine the fate of the 166 Ho-chitosan complex (DW-166HC) in rats by examining its absorption, distribution and excretion after administration into the prostate. About 100 μCi of DW-166HC [containing 0.1875 mg of Ho(NO 3 ) 3 .5H 2 O and 0.25 mg of chitosan] was administered intraprostatically. The level of radioactivity in blood, urinary and faecal excretion, and radioactivity distribution were examined. To determine the effect of chitosan in DW-166HC, 166 Ho nitrate alone [0.1875 mg of Ho(NO 3 ) 3 .5H 2 O] was administered into the prostate of male rats, and radioactivity distribution was examined using whole-body autoradiography. After administration of DW-166HC into the prostate, cumulative urinary and faecal excretion over the period 0-72 h was 0.35% and 0.11%, respectively. The radioactivity at the administration site was extremely high at all time points up to 144 h (>98% of injected dose). The small amount of radioactivity which did transfer from the administration site distributed mainly to the liver, spleen, kidney cortex and bone. Compared with the DW-166HC group, the group that received 166 Ho nitrate alone displayed three- to fourfold higher levels of radioactivity in the main tissues, including liver, spleen, kidney cortex and bone, at 24 h after administration (P<0.05). (orig.)

  4. Recoil Induced Room Temperature Stable Frenkel Pairs in a-Hafnium Upon Thermal Neutron Capture

    Science.gov (United States)

    Butz, Tilman; Das, Satyendra K.; Dey, Chandi C.; Ghoshal, Shamik

    2013-11-01

    Ultrapure hafnium metal (110 ppm zirconium) was neutron activated with a thermal neutron flux of 6:6 · 1012 cm-2s-1 in order to obtain 181Hf for subsequent time differential perturbed angular correlation (TDPAC) experiments using the nuclear probe 181Hf(β-) 181Ta. Apart from the expected nuclear quadrupole interaction (NQI) signal for a hexagonal close-packed (hcp) metal, three further discrete NQIs were observed with a few percent fraction each. The TDPAC spectra were recorded for up to 11 half lives with extreme statistical accuracy. The fitted parameters vary slightly within the temperature range between 248 K and 373 K. The signals corresponding to the three additional sites completely disappear after `annealing' at 453 K for one minute. Based on the symmetry of the additional NQIs and their temperature dependencies, they are tentatively attributed to Frenkel pairs produced by recoil due to the emission of a prompt 5:694 MeV -ray following thermal neutron capture and reported by the nuclear probe in three different positions. These Frenkel pairs are stable up to at least 373 K.

  5. The energy landscape of glassy dynamics on the amorphous hafnium diboride surface

    Science.gov (United States)

    Nguyen, Duc; Mallek, Justin; Cloud, Andrew N.; Abelson, John R.; Girolami, Gregory S.; Lyding, Joseph; Gruebele, Martin

    2014-11-01

    Direct visualization of the dynamics of structural glasses and amorphous solids on the sub-nanometer scale provides rich information unavailable from bulk or conventional single molecule techniques. We study the surface of hafnium diboride, a conductive ultrahigh temperature ceramic material that can be grown in amorphous films. Our scanning tunneling movies have a second-to-hour dynamic range and single-point current measurements extend that to the millisecond-to-minute time scale. On the a-HfB2 glass surface, two-state hopping of 1-2 nm diameter cooperatively rearranging regions or "clusters" occurs from sub-milliseconds to hours. We characterize individual clusters in detail through high-resolution (single cluster vertical displacements, we can reconstruct the local free energy landscape of individual clusters, complete with activation barrier height, a reaction coordinate in nanometers, and the shape of the free energy landscape basins between which hopping occurs. The experimental images are consistent with the compact shape of α-relaxors predicted by random first order transition theory, whereas the rapid hopping rate, even taking less confined motion at the surface into account, is consistent with β-relaxations. We make a proposal of how "mixed" features can show up in surface dynamics of glasses.

  6. Characteristics of laser produced plasmas of hafnium and tantalum in the 1-7 nm region

    Science.gov (United States)

    Li, Bowen; Otsuka, Takamitsu; Sokell, Emma; Dunne, Padraig; O'Sullivan, Gerry; Hara, Hiroyuki; Arai, Goki; Tamura, Toshiki; Ono, Yuichi; Dinh, Thanh-Hung; Higashiguchi, Takeshi

    2017-11-01

    Soft X-ray (SXR) spectra from hafnium and tantalum laser produced plasmas were recorded in the 1-7 nm region using two Nd:YAG lasers with pulse lengths of 170 ps and 10 ns, respectively, operating at a range of power densities. The maximum focused peak power density was 2. 3 × 1014 W cm-2 for 170 ps pulses and 1. 8 × 1012 W cm-2 for 10 ns pulses, respectively. Two intense quasicontinuous intensity bands resulting from n = 4 - n = 4 and n = 4 - n = 5 unresolved transition arrays (UTAs) dominate both sets of experimental spectra. Comparison with calculations performed with the Cowan suite of atomic structure codes as well as consideration of previous experimental and theoretical results aided identification of the most prominent features in the spectra. For the 10 ns spectrum, the highest ion stage that could be identified from the n = 4 - n = 5 arrays were lower than silver-like Hf25+ and Ta26+ (which has a 4 d 104 f ground configuration) indicating that the plasma temperature attained was too low to produce ions with an outermost 4 d subshell, while for the 170 ps plasmas the presence of significantly higher stages was deduced and lines due to 4 d-5 p transitions were clearly evident. Furthermore, we show an enhancement of emission from tantalum using dual laser irradiation, and the effect of pre-pulse durations and delay times between two pulses are demonstrated.

  7. Ferroelectric transistors with monolayer molybdenum disulfide and ultra-thin aluminum-doped hafnium oxide

    Science.gov (United States)

    Yap, Wui Chung; Jiang, Hao; Liu, Jialun; Xia, Qiangfei; Zhu, Wenjuan

    2017-07-01

    In this letter, we demonstrate ferroelectric memory devices with monolayer molybdenum disulfide (MoS2) as the channel material and aluminum (Al)-doped hafnium oxide (HfO2) as the ferroelectric gate dielectric. Metal-ferroelectric-metal capacitors with 16 nm thick Al-doped HfO2 are fabricated, and a remnant polarization of 3 μC/cm2 under a program/erase voltage of 5 V is observed. The capability of potential 10 years data retention was estimated using extrapolation of the experimental data. Ferroelectric transistors based on embedded ferroelectric HfO2 and MoS2 grown by chemical vapor deposition are fabricated. Clockwise hysteresis is observed at low program/erase voltages due to slow bulk traps located near the 2D/dielectric interface, while counterclockwise hysteresis is observed at high program/erase voltages due to ferroelectric polarization. In addition, the endurances of the devices are tested, and the effects associated with ferroelectric materials, such as the wake-up effect and polarization fatigue, are observed. Reliable writing/reading in MoS2/Al-doped HfO2 ferroelectric transistors over 2 × 104 cycles is achieved. This research can potentially lead to advances of two-dimensional (2D) materials in low-power logic and memory applications.

  8. Silicon-doped hafnium oxide anti-ferroelectric thin films for energy storage

    Science.gov (United States)

    Ali, Faizan; Liu, Xiaohua; Zhou, Dayu; Yang, Xirui; Xu, Jin; Schenk, Tony; Müller, Johannes; Schroeder, Uwe; Cao, Fei; Dong, Xianlin

    2017-10-01

    Motivated by the development of ultracompact electronic devices as miniaturized energy autonomous systems, great research efforts have been expended in recent years to develop various types of nano-structural energy storage components. The electrostatic capacitors characterized by high power density are competitive; however, their implementation in practical devices is limited by the low intrinsic energy storage density (ESD) of linear dielectrics like Al2O3. In this work, a detailed experimental investigation of energy storage properties is presented for 10 nm thick silicon-doped hafnium oxide anti-ferroelectric thin films. Owing to high field induced polarization and slim double hysteresis, an extremely large ESD value of 61.2 J/cm3 is achieved at 4.5 MV/cm with a high efficiency of ˜65%. In addition, the ESD and the efficiency exhibit robust thermal stability in 210-400 K temperature range and an excellent endurance up to 109 times of charge/discharge cycling at a very high electric field of 4.0 MV/cm. The superior energy storage performance together with mature technology of integration into 3-D arrays suggests great promise for this recently discovered anti-ferroelectric material to replace the currently adopted Al2O3 in fabrication of nano-structural supercapacitors.

  9. Hafnium Films and Magnetic Shielding for TIME, A mm-Wavelength Spectrometer Array

    Science.gov (United States)

    Hunacek, J.; Bock, J.; Bradford, C. M.; Butler, V.; Chang, T.-C.; Cheng, Y.-T.; Cooray, A.; Crites, A.; Frez, C.; Hailey-Dunsheath, S.; Hoscheit, B.; Kim, D. W.; Li, C.-T.; Marrone, D.; Moncelsi, L.; Shirokoff, E.; Steinbach, B.; Sun, G.; Trumper, I.; Turner, A.; Uzgil, B.; Weber, A.; Zemcov, M.

    2018-04-01

    TIME is a mm-wavelength grating spectrometer array that will map fluctuations of the 157.7-μm emission line of singly ionized carbon ([CII]) during the epoch of reionization (redshift z ˜ 5-9). Sixty transition-edge sensor (TES) bolometers populate the output arc of each of the 32 spectrometers, for a total of 1920 detectors. Each bolometer consists of gold absorber on a ˜ 3 × 3 mm silicon nitride micro-mesh suspended near the corners by 1 × 1 × 500 μm silicon nitride legs targeting a photon-noise-dominated NEP ˜ 1 × 10^{-17} W/√{Hz} . Hafnium films are explored as a lower-T_c alternative to Ti (500 mK) for TIME TESs, allowing thicker support legs for improved yield. Hf T_c is shown to vary between 250 and 450 mK when varying the resident Ar pressure during deposition. Magnetic shielding designs and simulations are presented for the TIME first-stage SQUIDs. Total axial field suppression is predicted to be 5 × 10^7.

  10. Tuning the magnetic properties of pure hafnium by high pressure torsion

    International Nuclear Information System (INIS)

    Cepeda-Jiménez, C.M.; Beltrán, J.I.; Hernando, A.; García, M.A.; Ynduráin, F.; Zhilyaev, A.; Pérez-Prado, M.T.

    2017-01-01

    This work demonstrates that room temperature (RT) ferromagnetism might be triggered in pure hafnium (Hf), a classic paramagnet, by severe plastic deformation (SPD) via high pressure torsion (HPT). The origin of this phenomenon is elucidated by a combined approach including density functional theory (DFT) calculations and transmission electron microscopy (TEM). In particular, it is shown that the elastic lattice distorsions induced in pure Hf as a consequence of grain refinement down to the nanocrystalline regime by HPT lead to the development of a new monoclinic crystalline structure that exhibits a spontaneous magnetization at RT. DFT calculations are utilized to prove that local stretching of the original pure Hf hexagonal close packed (hcp) lattice along specific pyramidal directions, due to the presence of internal stresses in the deformed nanostructure, may give rise to the emergence of the monoclinic phase, which is endowed with a net magnetic moment. An excellent agreement is found between DFT calculations and experimental TEM observations, which provide a first evidence of the presence of the pure Hf monoclinic crystal lattice. This work shows that SPD may constitute a viable, yet widely unexplored, strategy to tune the magnetic properties and, in particular, to induce RT ferromagnetism in bulk non-magnetic metals.

  11. In-Pile Experiment of a New Hafnium Aluminide Composite Material to Enable Fast Neutron Testing in the Advanced Test Reactor

    Energy Technology Data Exchange (ETDEWEB)

    Donna Post Guillen; Douglas L. Porter; James R. Parry; Heng Ban

    2010-06-01

    A new hafnium aluminide composite material is being developed as a key component in a Boosted Fast Flux Loop (BFFL) system designed to provide fast neutron flux test capability in the Advanced Test Reactor. An absorber block comprised of hafnium aluminide (Al3Hf) particles (~23% by volume) dispersed in an aluminum matrix can absorb thermal neutrons and transfer heat from the experiment to pressurized water cooling channels. However, the thermophysical properties, such as thermal conductivity, of this material and the effect of irradiation are not known. This paper describes the design of an in-pile experiment to obtain such data to enable design and optimization of the BFFL neutron filter.

  12. Comparing particles for radiosynovectomy labeled with Ho-166

    International Nuclear Information System (INIS)

    Argueelles, M.G.; Luppi Berlanga, I.S.; Torres, E.A.; Pereyra Molina, V.

    2002-01-01

    Aim: Three types of microparticles containing Ho-166 were investigated as potential agents for radiation synovectomy. These are: hydroxyapatite (HA), ferric hydroxide macro-aggregates (FHMA) and polymeric micro-spheres (PM). Labeling was performed by three different methods: coprecipitation, two steps labeling using citrate and irradiation of Ho-165 complexed to acetylacetone (AcAc) incorporated into poly-L-lactic acid spheres (PLA) by the solvent evaporation technique. Material and methods: a coprecipitation technique of holmium hydroxide and ferric hydroxide was used in order to obtain 166 Ho-FHMA. Particle size was determined by optical microscopy and selective filtration (1.2 - 100 μm). Obtainment efficiency of FHMA was always higher than 90%. Radiochemical purity was checked by thin layer chromatography using ITLC/SG and EDTA solution as solvent. In vitro stability studies were performed by incubating labelled particles in either saline, or EDTA solution. Hydroxyapatite particles were prepared from the reaction of calcium nitrate and ammonia phosphate at high pH. By strong heating of the precipitate at 800 0 C, the product becomes largely anhydrous and hardened. The yield of the hydroxyapatite synthesis was always greater than 80%. Particle size range was studied using light microscopy. Labeling was done in two steps: 166Ho-citrate was prepared by adding sufficient citric acid to the 166 Ho-Cl 3 solution. The radioactive solution was added to the particulate suspension stirring continuously. Radiolabelled particles were rinsed and separated by centrifugation. Stable Ho-165, complexed to acetylacetone (AcAc), was incorporated into PLA spheres by the solvent evaporation technique. The particle size distribution of the micro-spheres was determined by electronic microscopy. A X-ray fluorescence technique was used to determine the percentage of 165 Ho-AcAc incorporated in the microspheres by studying standards and prepared PLA spheres. Stability studies were

  13. Preparation of {sup 166} Dy/{sup 166} Ho-Macro aggregates as an In vivo generator system for the treatment of arthrophaties; Preparacion de {sup 166} Dy/{sup 166} Ho-Macro agregados como un sistema de generador In vivo para el tratamiento de artropatias

    Energy Technology Data Exchange (ETDEWEB)

    Aldama A, T.K

    2003-07-01

    The present work reports the obtention of macro aggregates of hydroxides of Dysprosium-166/Holmium-166 ({sup 166} Dy/{sup 166} Ho-MH), as a generator system in vivo to be used in the treatment of arthritis rheumatoid. The {sup 166} Dy was obtained by neutron irradiation of {sup 166} DyO{sub 3} (enriched to 98.45%) by 20 h in the TRIGA Mark III Reactor and 50 h of decay, to the oxide of {sup 166} Dy/{sup 166} Ho formed, it was added HCl 0.12 N to obtain a final volume of 3.5 ml of solution of {sup 166} Dy/{sup 166} Ho chloride. The solution of {sup 166D}yCl{sub 3} solution was obtained with an activity of 3.502 mCi (129 MBq), appropriate for the preparation of the radiopharmaceutical {sup 166} Dy/{sup 166} Ho-MH. The separation of the {sup 166} Dy from the {sup 166} Ho, was carried out by chromatography in an cation exchange column, gaining an appropriate separation, obtaining a {sup 166} Dy with a radionuclide purity greater than 90%. The {sup 166} Dy/{sup 166} Ho-MH were prepared by addition to the solution of {sup 166} DyCI{sub 3} NaOH 0.5 N low ultrasonic bath with later centrifugation, decanted and resuspension in saline solution, obtaining a radiopharmaceutical with a generator system {sup 166} Dy/ {sup 166} Ho with particles of size average of 3 {mu}m, in form of {sup 166} Dy / {sup 166} Ho-MH. Under these conditions, it was obtained a radiochemical yield greater than 99%. The microscopic analysis and of filtration showed that the formulation doesn't present particles smaller than to 1 {mu}m, neither greater to 50 {mu}m, which will allow, the quick phagocytosis for the synoviocytes of the synovial membrane, and by consequence, an homogeneous distribution of the radiation dose could exist. The sedimentation velocity for the formulated suspension is of 0.04 cm/min that it will allow the administration of homogeneous activities of the radiopharmaceutical, to the no deposit in the injection devices. The studies of stability in vitro indicate us that inside

  14. Preparation of {sup 166} Dy/{sup 166} Ho-Macro aggregates as an In vivo generator system for the treatment of arthrophaties; Preparacion de {sup 166} Dy/{sup 166} Ho-Macro agregados como un sistema de generador In vivo para el tratamiento de artropatias

    Energy Technology Data Exchange (ETDEWEB)

    Aldama A, T K

    2003-07-01

    The present work reports the obtention of macro aggregates of hydroxides of Dysprosium-166/Holmium-166 ({sup 166} Dy/{sup 166} Ho-MH), as a generator system in vivo to be used in the treatment of arthritis rheumatoid. The {sup 166} Dy was obtained by neutron irradiation of {sup 166} DyO{sub 3} (enriched to 98.45%) by 20 h in the TRIGA Mark III Reactor and 50 h of decay, to the oxide of {sup 166} Dy/{sup 166} Ho formed, it was added HCl 0.12 N to obtain a final volume of 3.5 ml of solution of {sup 166} Dy/{sup 166} Ho chloride. The solution of {sup 166D}yCl{sub 3} solution was obtained with an activity of 3.502 mCi (129 MBq), appropriate for the preparation of the radiopharmaceutical {sup 166} Dy/{sup 166} Ho-MH. The separation of the {sup 166} Dy from the {sup 166} Ho, was carried out by chromatography in an cation exchange column, gaining an appropriate separation, obtaining a {sup 166} Dy with a radionuclide purity greater than 90%. The {sup 166} Dy/{sup 166} Ho-MH were prepared by addition to the solution of {sup 166} DyCI{sub 3} NaOH 0.5 N low ultrasonic bath with later centrifugation, decanted and resuspension in saline solution, obtaining a radiopharmaceutical with a generator system {sup 166} Dy/ {sup 166} Ho with particles of size average of 3 {mu}m, in form of {sup 166} Dy / {sup 166} Ho-MH. Under these conditions, it was obtained a radiochemical yield greater than 99%. The microscopic analysis and of filtration showed that the formulation doesn't present particles smaller than to 1 {mu}m, neither greater to 50 {mu}m, which will allow, the quick phagocytosis for the synoviocytes of the synovial membrane, and by consequence, an homogeneous distribution of the radiation dose could exist. The sedimentation velocity for the formulated suspension is of 0.04 cm/min that it will allow the administration of homogeneous activities of the radiopharmaceutical, to the no deposit in the injection devices. The studies of stability in vitro indicate us that inside the

  15. Rapid formation of nanocrystalline HfO2 powders from amorphous hafnium hydroxide under ultrasonically assisted hydrothermal treatment

    International Nuclear Information System (INIS)

    Meskin, Pavel E.; Sharikov, Felix Yu.; Ivanov, Vladimir K.; Churagulov, Bulat R.; Tretyakov, Yury D.

    2007-01-01

    Peculiarities of hafnium hydroxide hydrothermal decomposition were studied by in situ heat flux calorimetry for the first time. It was shown that this process occurs in one exothermal stage (ΔH = -17.95 kJ mol -1 ) at 180-250 deg. C resulting in complete crystallization of amorphous phase with formation of pure monoclinic HfO 2 . It was found that the rate of m-HfO 2 formation can be significantly increased by combining hydrothermal treatment with simultaneous ultrasonic activation

  16. Development of a PET tracer for imaging EGFR tyrosine kinase: evaluation of the suitability of PKI166

    International Nuclear Information System (INIS)

    Kernchen, R.; Brust, P.; Krause, M.; Baumann, M.

    2002-01-01

    The suitability of PKI166 for the development of a PET tracer for imaging EGFR tyrosine kinase was investigated. Binding studies using EGFR positive tumour tissue and tritiated PKI166 as the radioligand indicated a low binding affinity of PKI166 to the target tissue. PKI166 is therefore not recommended for PET tracer development. (orig.)

  17. The energy landscape of glassy dynamics on the amorphous hafnium diboride surface

    International Nuclear Information System (INIS)

    Nguyen, Duc; Girolami, Gregory S.; Mallek, Justin; Cloud, Andrew N.; Abelson, John R.; Lyding, Joseph; Gruebele, Martin

    2014-01-01

    Direct visualization of the dynamics of structural glasses and amorphous solids on the sub-nanometer scale provides rich information unavailable from bulk or conventional single molecule techniques. We study the surface of hafnium diboride, a conductive ultrahigh temperature ceramic material that can be grown in amorphous films. Our scanning tunneling movies have a second-to-hour dynamic range and single-point current measurements extend that to the millisecond-to-minute time scale. On the a-HfB 2 glass surface, two-state hopping of 1–2 nm diameter cooperatively rearranging regions or “clusters” occurs from sub-milliseconds to hours. We characterize individual clusters in detail through high-resolution (<0.5 nm) imaging, scanning tunneling spectroscopy and voltage modulation, ruling out individual atoms, diffusing adsorbates, or pinned charges as the origin of the observed two-state hopping. Smaller clusters are more likely to hop, larger ones are more likely to be immobile. HfB 2 has a very high bulk glass transition temperature T g , and we observe no three-state hopping or sequential two-state hopping previously seen on lower T g glass surfaces. The electronic density of states of clusters does not change when they hop up or down, allowing us to calibrate an accurate relative z-axis scale. By directly measuring and histogramming single cluster vertical displacements, we can reconstruct the local free energy landscape of individual clusters, complete with activation barrier height, a reaction coordinate in nanometers, and the shape of the free energy landscape basins between which hopping occurs. The experimental images are consistent with the compact shape of α-relaxors predicted by random first order transition theory, whereas the rapid hopping rate, even taking less confined motion at the surface into account, is consistent with β-relaxations. We make a proposal of how “mixed” features can show up in surface dynamics of glasses

  18. Materials properties of hafnium and zirconium silicates: Metal interdiffusion and dopant penetration studies

    Science.gov (United States)

    Quevedo Lopez, Manuel Angel

    Hafnium and Zirconium based gate dielectrics are considered potential candidates to replace SiO2 or SiON as the gate dielectric in CMOS processing. Furthermore, the addition of nitrogen into this pseudo-binary alloy has been shown to improve their thermal stability, electrical properties, and reduce dopant penetration. Because CMOS processing requires high temperature anneals (up to 1050°C), it is important to understand the diffusion properties of any metal associated with the gate dielectric in silicon at these temperatures. In addition, dopant penetration from the doped polysilicon gate into the Si channel at these temperatures must also be studied. Impurity outdiffusion (Hf, Zr) from the dielectric, or dopant (B, As, P) penetration through the dielectric into the channel region would likely result in deleterious effects upon the carrier mobility. In this dissertation extensive thermal stability studies of alternate gate dielectric candidates ZrSixOy and HfSixO y are presented. Dopant penetration studies from doped-polysilicon through HfSixOy and HfSixOyNz are also presented. Rutherford Backscattering Spectroscopy (RBS), Heavy Ion RBS (HI-RBS), X-ray Photoelectron Spectroscopy (XPS), High Resolution Transmission Electron Microscopy (HR-TEM), and Time of Flight and Dynamic Secondary Ion Mass Spectroscopy (ToF-SIMS, D-SIMS) methods were used to characterize these materials. The dopant diffusivity is calculated by modeling of the dopant profiles in the Si substrate. In this disseration is reported that Hf silicate films are more stable than Zr silicate films, from the metal interdiffusion point of view. On the other hand, dopant (B, As, and P) penetration is observed for HfSixO y films. However, the addition of nitrogen to the Hf - Si - O systems improves the dopant penetration properties of the resulting HfSi xOyNz films.

  19. Protective coatings of hafnium dioxide by atomic layer deposition for microelectromechanical systems applications

    Energy Technology Data Exchange (ETDEWEB)

    Berdova, Maria, E-mail: maria.berdova@aalto.fi [Aalto University, Department of Materials Science and Engineering, 02150, Espoo (Finland); Wiemer, Claudia; Lamperti, Alessio; Tallarida, Grazia; Cianci, Elena [Laboratorio MDM, IMM CNR, Via C. Olivetti 2, 20864, Agrate Brianza, MB (Italy); Lamagna, Luca; Losa, Stefano; Rossini, Silvia; Somaschini, Roberto; Gioveni, Salvatore [STMicroelectronics, Via C. Olivetti 2, 20864, Agrate Brianza, MB (Italy); Fanciulli, Marco [Laboratorio MDM, IMM CNR, Via C. Olivetti 2, 20864, Agrate Brianza, MB (Italy); Università degli studi di Milano Bicocca, Dipartimento di Scienza dei Materiali, 20126, Milano (Italy); Franssila, Sami, E-mail: sami.franssila@aalto.fi [Aalto University, Department of Materials Science and Engineering, 02150, Espoo (Finland)

    2016-04-15

    Graphical abstract: - Highlights: • Atomic layer deposition of HfO{sub 2} from (CpMe){sub 2}Hf(OMe)Me or Hf(NMeEt){sub 4} and ozone for potential applications in microelectromechanical systems. • ALD HfO{sub 2} protects aluminum substrates from degradation in moist environment and at the same time retains good reflectance properties of the underlying material. • The resistance of hafnium dioxide to moist environment is independent of chosen precursors. - Abstract: This work presents the investigation of HfO{sub 2} deposited by atomic layer deposition (ALD) from either HfD-CO4 or TEMAHf and ozone for microelectromechanical systems (MEMS) applications, in particular, for environmental protection of aluminum micromirrors. This work shows that HfO{sub 2} films successfully protect aluminum in moist environment and at the same time retain good reflectance properties of underlying material. In our experimental work, the chemical composition, crystal structure, electronic density and roughness of HfO{sub 2} films remained the same after one week of humidity treatment (relative humidity of 85%, 85 °C). The reflectance properties underwent only minor changes. The observed shift in reflectance was only from 80–90% to 76–85% in 400–800 nm spectral range when coated with ALD HfO{sub 2} films grown with Hf(NMeEt){sub 4} and no shift (remained in the range of 68–83%) for films grown from (CpMe){sub 2}Hf(OMe)Me.

  20. 25 CFR 166.220 - What are the basic steps for acquiring a permit through negotiation?

    Science.gov (United States)

    2010-04-01

    ... 25 Indians 1 2010-04-01 2010-04-01 false What are the basic steps for acquiring a permit through negotiation? 166.220 Section 166.220 Indians BUREAU OF INDIAN AFFAIRS, DEPARTMENT OF THE INTERIOR LAND AND WATER GRAZING PERMITS Permit Requirements Obtaining A Permit § 166.220 What are the basic steps for acquiring a permit through negotiation? The...

  1. 25 CFR 166.219 - How do I acquire a permit through negotiation?

    Science.gov (United States)

    2010-04-01

    ... 25 Indians 1 2010-04-01 2010-04-01 false How do I acquire a permit through negotiation? 166.219 Section 166.219 Indians BUREAU OF INDIAN AFFAIRS, DEPARTMENT OF THE INTERIOR LAND AND WATER GRAZING PERMITS Permit Requirements Obtaining A Permit § 166.219 How do I acquire a permit through negotiation? (a) Permits may be negotiated and granted by th...

  2. Study of hafnium (IV) oxide nanoparticles synthesized by polymerized complex and polymer precursor derived sol-gel methods

    KAUST Repository

    Ramos-Gonzá lez, R.; Garcí a-Cerda, L. A.; Alshareef, Husam N.; Gnade, Bruce E.; Quevedo-Ló pez, Manuel Angel Quevedo

    2010-01-01

    This work reports the preparation and characterization of hafnium (IV) oxide (HfO2) nanoparticles grown by derived sol-gel routes that involves the formation of an organic polymeric network. A comparison between polymerized complex (PC) and polymer precursor (PP) methods is presented. For the PC method, citric acid (CA) and ethylene glycol (EG) are used as the chelating and polymerizable reagents, respectively. In the case of PP method, poly(acrylic acid) (PAA) is used as the chelating reagent. In both cases, different precursor gels were prepared and the hafnium (IV) chloride (HfCl4) molar ratio was varied from 0.1 to 1.0 for the PC method and from 0.05 to 0.5 for the PP method. In order to obtain the nanoparticles, the precursors were heat treated at 500 and 800 °C. The thermal characterization of the precursor gels was carried out by thermogravimetric analysis (TGA) and the structural and morphological characterization by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The XRD patterns of the samples obtained by both methods shows the formation of HfO2 at 500 °C with monoclinic crystalline phase. The PC method exhibited also the cubic phase. Finally, the HfO2 nanoparticles size (4 to 11 nm) was determined by TEM and XRD patterns. © (2010) Trans Tech Publications.

  3. Study of hafnium (IV) oxide nanoparticles synthesized by polymerized complex and polymer precursor derived sol-gel methods

    KAUST Repository

    Ramos-González, R.

    2010-03-01

    This work reports the preparation and characterization of hafnium (IV) oxide (HfO2) nanoparticles grown by derived sol-gel routes that involves the formation of an organic polymeric network. A comparison between polymerized complex (PC) and polymer precursor (PP) methods is presented. For the PC method, citric acid (CA) and ethylene glycol (EG) are used as the chelating and polymerizable reagents, respectively. In the case of PP method, poly(acrylic acid) (PAA) is used as the chelating reagent. In both cases, different precursor gels were prepared and the hafnium (IV) chloride (HfCl4) molar ratio was varied from 0.1 to 1.0 for the PC method and from 0.05 to 0.5 for the PP method. In order to obtain the nanoparticles, the precursors were heat treated at 500 and 800 °C. The thermal characterization of the precursor gels was carried out by thermogravimetric analysis (TGA) and the structural and morphological characterization by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The XRD patterns of the samples obtained by both methods shows the formation of HfO2 at 500 °C with monoclinic crystalline phase. The PC method exhibited also the cubic phase. Finally, the HfO2 nanoparticles size (4 to 11 nm) was determined by TEM and XRD patterns. © (2010) Trans Tech Publications.

  4. Complexation behaviour of DADCA and DAPDA with dysprosium-166/holmium-166 parent daughter system and its potential for use in radioimmunotherapy

    International Nuclear Information System (INIS)

    Orsini, S.; University of Technology, Broadway, NSW; Di Bartolo, N.; Smith, S.; Baker, T.

    1998-01-01

    Full text: A novel approach for the delivery of therapeutic doses from 166 Ho to cancerous tissue is via the decay of its parent, 166 Dy. When designing radioimmunoconjugte, a crucial question is to determine whether the ligand used in the radiolabeling process is capable of holding the 166 Ho on decay of the parent, 166 Dy. In this study, two pendant arm macrocycles 1, 10-Diaza-4, 7, 13, 16-tetraoxacyclooctadecane-N, N'-diacetic acid, (DACDA) and 1, 10-Diaza-4, 7, 13-trioxacyclopentadecane-N, N'-diacetic acid, (DAPDA) that were reported to forms reasonably stable complexes with Dy and Ho, were synthesised. The synthesis of the two pendant arm macrocycles was first attempted using methods outlined by Chang and Rowland. The yields obtained through this method were low (10 % for both ligands) and it was considered important to investigate alternative approaches to the synthesis. The new method involved an alkylation reaction in the presence of acetonitrile and sodium bicarbonate. The method took considerably less time and the yields increased to 88 %. The ligands were characterised using 1 H NMR, 13 C NMR and mass spectrometry. The chemical and radiolytic stabilities of 166 Dy and 166 Ho complexes of the two ligands were investigated at pH = 5 and the ligands potential for use in the in vivo generator system evaluated

  5. Anti-invasive and antiangiogenic effects of MMI-166 on malignant glioma cells

    International Nuclear Information System (INIS)

    Nakabayashi, Hiromichi; Yawata, Toshio; Shimizu, Keiji

    2010-01-01

    The constitutive overexpression of matrix metalloproteinases (MMPs) is frequently observed in malignant tumours. In particular, MMP-2 and MMP-9 have been reported to be closely associated with invasion and angiogenesis in malignant gliomas. Our study aimed to evaluate the antitumour effects of MMI-166 (Nalpha-[4-(2-Phenyl-2H- tetrazole-5-yl) phenyl sulfonyl]-D-tryptophan), a third generation MMP inhibitor, on three human glioma cell lines (T98G, U87MG, and ONS12) in vitro and in vivo. The effects of MMI-166 on the gelatinolytic activity was analysed by gelatine zymography. The anti-invasive effect of MMI-166 was analysed by an in vitro invasion assay. An in vitro angiogenesis assay was also performed. In vitro growth inhibition of glioma cells by MMI-166 was determined by the MTT assay. The effect of MMI-166 on an orthotropic implantation model using athymic mice was also evaluated. Gelatine zymography revealed that MMP-2 and MMP-9 activities were suppressed by MMI-166. The invasion of glioma cells was suppressed by MMI-166. The angiogenesis assay showed that MMI-166 had a suppressive effect on glioma cell-induced angiogenesis. However, MMI-166 did not suppress glioma cell proliferation in the MTT assay. In vivo, MMI-166 suppressed tumour growth in athymic mice implanted orthotropically with T98G cells and showed an inhibitory effect on tumour-induced angiogenesis and tumour growth. This is the first report of the effect of a third generation MMP inhibitor on malignant glioma cells. These results suggest that MMI-166 may have potentially suppressive effects on the invasion and angiogenesis of malignant gliomas

  6. Quarry detection monitoring wells completion report WP-166

    International Nuclear Information System (INIS)

    1991-09-01

    The purpose of this report is to document the activities undertaken during implementation of Work Package 166, Quarry Detection Monitoring Wells, for the Weldon Spring Site Remedial action project, Weldon Spring, Missouri. The subcontract specifications should be consulted for specific details regarding this work effort. Analytical parameters for soil samples collected for all but one borehole were analyzed for uranium, thorium, cyanide, nitroaromatics, and all Hazardous Substance List parameters including volatiles, semivolatiles, pesticides, polychlorinated biphenyls (PCBs) and metals. No soil samples were collected at other borehole as per specifications. With Z exceptions, uranium results for all boreholes sampled were at background levels. Nitroaromatics and cyanide were not detected in any of the samples collected. Volatile and semivolatile organics were not detected in the soil samples collected from the boreholes, with the exception of common lab contaminants such as methylene chloride, toluene, acetone, and pathalates. All metals results were either within their natural background ranges or below the detection limit of the instrument. PCB's were not detected within any of the boreholes. Pesticides detected (aldrin and methoxychlor) at one borehole near the surface may be attributed to previous spraying of pesticides on the highway right-of-way. In conclusion, the analytical results show that only uranium was detected in significant quantities; all other results were below the detection limit, very near the detection limit, or within natural background ranges. 1 fig

  7. 25 CFR 1000.166 - What are the phases of the negotiation process?

    Science.gov (United States)

    2010-04-01

    ... 25 Indians 2 2010-04-01 2010-04-01 false What are the phases of the negotiation process? 1000.166 Section 1000.166 Indians OFFICE OF THE ASSISTANT SECRETARY, INDIAN AFFAIRS, DEPARTMENT OF THE INTERIOR ANNUAL FUNDING AGREEMENTS UNDER THE TRIBAL SELF-GOVERNMENT ACT AMENDMENTS TO THE INDIAN SELF-DETERMINATION AND EDUCATION ACT Negotiation Process...

  8. 25 CFR 166.901 - How will the BIA select an agriculture intern?

    Science.gov (United States)

    2010-04-01

    ... 25 Indians 1 2010-04-01 2010-04-01 false How will the BIA select an agriculture intern? 166.901... PERMITS Agriculture Education, Education Assistance, Recruitment, and Training § 166.901 How will the BIA select an agriculture intern? (a) The purpose of the agriculture intern program is to ensure the future...

  9. 46 CFR 166.10 - Course of study for engineering students.

    Science.gov (United States)

    2010-10-01

    ... 46 Shipping 7 2010-10-01 2010-10-01 false Course of study for engineering students. 166.10 Section... AND APPROVAL OF NAUTICAL SCHOOL SHIPS § 166.10 Course of study for engineering students. The course of study for engineering students shall include (a) all the instruction necessary to fully equip the...

  10. 25 CFR 166.608 - What types of insurance may be required?

    Science.gov (United States)

    2010-04-01

    ... Bonding and Insurance Requirements § 166.608 What types of insurance may be required? We may require liability or casualty insurance (such as for fire, hazard, or flood), depending upon the activity conducted... 25 Indians 1 2010-04-01 2010-04-01 false What types of insurance may be required? 166.608 Section...

  11. 40 CFR 166.24 - Public notice of receipt of application and opportunity for public comment.

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 23 2010-07-01 2010-07-01 false Public notice of receipt of application and opportunity for public comment. 166.24 Section 166.24 Protection of Environment ENVIRONMENTAL... of the applicant's description of the emergency conditions including the pest and the site or crop to...

  12. 33 CFR 166.200 - Shipping safety fairways and anchorage areas, Gulf of Mexico.

    Science.gov (United States)

    2010-07-01

    ... anchorage areas, Gulf of Mexico. 166.200 Section 166.200 Navigation and Navigable Waters COAST GUARD... the erection of structures therein to provide safe approaches through oil fields in the Gulf of Mexico... for Fairway Anchorages in the Gulf of Mexico. Structures may be placed within an area designated as a...

  13. 25 CFR 166.223 - Can I use a permit as collateral for a loan?

    Science.gov (United States)

    2010-04-01

    ... 25 Indians 1 2010-04-01 2010-04-01 false Can I use a permit as collateral for a loan? 166.223... PERMITS Permit Requirements Permit (leasehold) Mortgage § 166.223 Can I use a permit as collateral for a loan? We may approve a permit containing a provision that authorizes the permittee to encumber the...

  14. DXD Motif-Dependent and -Independent Effects of the Chlamydia trachomatis Cytotoxin CT166

    Directory of Open Access Journals (Sweden)

    Miriam Bothe

    2015-02-01

    Full Text Available The Gram-negative, intracellular bacterium Chlamydia trachomatis causes acute and chronic urogenital tract infection, potentially leading to infertility and ectopic pregnancy. The only partially characterized cytotoxin CT166 of serovar D exhibits a DXD motif, which is important for the enzymatic activity of many bacterial and mammalian type A glycosyltransferases, leading to the hypothesis that CT166 possess glycosyltransferase activity. CT166-expressing HeLa cells exhibit actin reorganization, including cell rounding, which has been attributed to the inhibition of the Rho-GTPases Rac/Cdc42. Exploiting the glycosylation-sensitive Ras(27H5 antibody, we here show that CT166 induces an epitope change in Ras, resulting in inhibited ERK and PI3K signaling and delayed cell cycle progression. Consistent with the hypothesis that these effects strictly depend on the DXD motif, CT166 with the mutated DXD motif causes neither Ras-ERK inhibition nor delayed cell cycle progression. In contrast, CT166 with the mutated DXD motif is still capable of inhibiting cell migration, suggesting that CT166 with the mutated DXD motif cannot be regarded as inactive in any case. Taken together, CT166 affects various fundamental cellular processes, strongly suggesting its importance for the intracellular survival of chlamydia.

  15. Therapeutic application of new holmium-166 chitosan complex in malignant and benign diseases

    International Nuclear Information System (INIS)

    Park, K.B.; Kim, Y.M.; Shin, B.C.; Kim, J.R.; Ryu, J.M.; Lim, S.M.

    1998-01-01

    The new holmium-166 chitosan complex ( 166 Ho-CHICO, DW- 166 HC) was prepared by reacting the aqueous acidic solution of chitosan with 166 Ho(NO 3 ) 3 at room temperature with quantitative labelling yield. The progress of the reaction and labelling yield were determined by instant this layer chromatography using silicic acid impregnated glass fiber (ITLC-SA) and developing solvent of MeOH:H 2 O:HAC (49:49:2). The high labelling yield of more than 99% was obtained by reacting chitosan solution (35 mg/4 ml) with 166 Ho(NO 3 ) 3 in which 7 mg of 165 Ho+ 166 Ho were contained as a maximum content. The labelling yield was highly dependent on the pH of the chitosan solution. The optimal labelling could be obtained at pH 2.5∼3.5 The characteristics of 166 Ho-CHICO were similar to those of chitosan, which is biocompatible, biodegradable, non-toxic, soluble and viscous in acidic condition but geltatinuous at pH 6.0 and precipitating in alkaline conditions. 166 Ho-CHICO can be easily prepared by reconstituting freeze-dried chitosan (kit A) with 166 Ho(NO 3 ) 3 solution (kit B) just prior to use. After intrahepatic administration of 166 Ho-CHICO to male rats, the radioactivity concentrations in blood were low and the cumulative urinary and fecal excretion over a period of 0 to 72 hours were 0.53% and 0.54%, respectively. the radioactivity concentration in tissues and the whole-body autoradiography images showed that most of the administered radioactivity was localized at the administered site, and only slight radioactivity was detected from the liver, spleen, lungs, and bones. An autoradiograph after intratumoral administration of 166 Ho-CHICO showed that radioactivity was localized at the administered site of the lesion without distribution to other organs and tissues. A biodistribution study in normal rabbits with 166 Ho-CHICO showed that most of the radioactivities were retained in the knee joint with negligible extra leakage at 72 hours after intra

  16. Corrosion resistant surface for vanadium nitride and hafnium nitride layers as function of grain size

    Science.gov (United States)

    Escobar, C. A.; Caicedo, J. C.; Aperador, W.

    2014-01-01

    In this research it was studied vanadium nitride (VN) and hafnium nitride (HfN) film, which were deposited onto silicon (Si (100)) and AISI 4140 steel substrates via r.f. magnetron sputtering technique in Ar/N2 atmosphere with purity at 99.99% for both V and Hf metallic targets. Both films were approximately 1.2±0.1 μm thick. The crystallography structures that were evaluated via X-ray diffraction analysis (XRD) showed preferential orientations in the Bragg planes VN (200) and HfN (111). The chemical compositions for both films were characterized by EDX. Atomic Force Microscopy (AFM) was used to study the morphology; the results reveal grain sizes of 78±2 nm for VN and 58±2 nm for HfN and roughness values of 4.2±0.1 nm for VN and 1.5±0.1 nm for HfN films. The electrochemical performance in VN and HfN films deposited onto steel 4140 were studied by Tafel polarization curves and impedance spectroscopy methods (EIS) under contact with sodium chloride at 3.5 wt% solution, therefore, it was found that the corrosion rate decreased about 95% in VN and 99% for HfN films in relation to uncoated 4140 steel, thus demonstrating, the protecting effect of VN and HfN films under a corrosive environment as function of morphological characteristics (grain size). VN(grain size)=78±2.0 nm, VN(roughness)=4.2±0.1 nm, VN(corrosion rate)=40.87 μmy. HfN(grain size)=58±2.0 nm, HfN(roughness)=1.5±0.1 nm, HfN(corrosion rate)=0.205 μmy. It was possible to analyze that films with larger grain size, can be observed smaller grain boundary thus generating a higher corrosion rate, therefore, in this work it was found that the HfN layer has better corrosion resistance (low corrosion rate) in relation to VN film which presents a larger grain size, indicating that the low grain boundary in (VN films) does not restrict movement of the Cl- ion and in this way the corrosion rate increases dramatically.

  17. Synthesis and characterization of hafnium carbide microcrystal chains with a carbon-rich shell via CVD

    International Nuclear Information System (INIS)

    Tian, Song; Li, Hejun; Zhang, Yulei; Liu, Sen; Fu, Yangxi; Li, Yixian; Qiang, Xinfa

    2013-01-01

    Graphical abstract: Novel HfC microcrystal chains have been synthesized via a catalyst-assisted chemical vapor deposition process. SEM results show the chains have a periodically changing diameter and a nanoscale sharpening tip. Analysis of TEM/SAED/EELS/EDX data shows the single-crystal chains grow along a [0 0 1] direction and consist of a HfC core and a thin carbon-rich shell with embedded HfC nanocrystallites surrounding the core. This work achieves the controllable preparation of nanoscale HfC sharpening tips for application as a point electron emission source and facilitates the application of HfC ultrafast laser-triggered tips in attosecond science. Highlights: •HfC microcrystal chains were synthesized by a catalyst-assisted CVD. •The chains grow along a [0 0 1] direction and have a periodically changing diameter. •Single-crystal HfC core is sheathed by a thin carbon-rich shell. •A growth mechanism model is proposed to explain the growth of microcrystal chians. •This work achieves the controllable preparation of nanoscale HfC sharpening tips. -- Abstract: Novel hafnium carbide (HfC) microcrystal chains, with a periodically changing diameter and a nanoscale sharpening tip at the chain end, have been synthesized via a catalyst-assisted chemical vapor deposition (CVD) process. The as-synthesized chains with many octahedral microcrystals have diameters of between several hundreds of nm and 6 μm and lengths of ∼500 μm. TEM diffraction studies show that the chains are single-crystalline HfC and preferentially grow along a [0 0 1] crystal orientation. TEM/EELS/EDX analysis proves the chains are composed of a HfC core and a thin (several tens of nm to 100 nm) carbon-rich shell with the embedded HfC nanocrystallites (typically below 10 nm) surrounding the core. The growth mechanism model for the chains based on the vapor–liquid–solid process, the vapor–solid process, and the HfC crystal growth characteristics is discussed

  18. Hafnium in peralkaline and peraluminous boro-aluminosilicate glass, and glass subcomponents: a solubility study

    International Nuclear Information System (INIS)

    Davis, Linda L.; Darab, John G.; Qian, Maoxu; Zhao, Donggao; Palenik, Christopher S.; Li, Hong; Strachan, Denis M.; Li, Liyu

    2003-01-01

    A relationship between the solubility of hafnia (HfO2) and the host glass composition was explored by determining the solubility limits of HfO2 in peralkaline and peraluminous borosilicate glasses in the system SiO2-Al2O3-B2O3-Na2O, and in glasses in the system SiO2-Na2O-Al2O3 in air at 1450 C. The only Hf-bearing phase to crystallize in the peralkaline borosilicate melts is hafnia, while in the boron-free melts sodium-hafnium silicates crystallize. All peraluminous borosilicate melts crystallize hafnia, but the slightly peraluminous glasses also have sector-zoned hafnia crystals that contain Al and Si. The more peraluminous borosilicate glasses also crystallize a B-containing mullite. The general morphology of the hafnia crystals changes as peralkalinity (Na2O/(Na2O+Al2O3)) decreases, as expected in melts with increasing viscosity. In all of the glasses with Na2O > Al2O3, the solubility of hafnia is linearly and positively correlated with Na2O/(Na2O + Al2O3) or Na2O - Al2O3 (excess sodium), despite the presence of 5 to 16 mol% B2O3. The solubility of hafnia is higher in the sodium-aluminum borosilicate glasses than in the sodium-aluminosilicate glasses, suggesting that the boron is enhancing the effect that excess sodium has on the incorporation of Hf into the glass structure. The results of this solubility study are compared to other studies of high-valence cation solubility in B-free silicate melts. From this, for peralkaline B-bearing glasses, it is shown that, although the solubility limits are higher, the solution behavior of hafnia is the same as in B-free silicate melts previously studied. By comparison, also, it is shown that in peraluminous melts, there must be a different solution mechanism for hafnia: different than for peralkaline sodium-aluminum borosilicate glasses and different than for B-free silicate melts studied by others

  19. Nano-crystals of cerium–hafnium binary oxide: Their size-dependent structure

    Energy Technology Data Exchange (ETDEWEB)

    Raitano, Joan M. [Department of Applied Physics and Applied Mathematics, Materials Science and Engineering Program, Columbia University, New York, NY 10027 (United States); Khalid, Syed [National Synchrotron Light Source, Brookhaven National Laboratory, Upton, NY 11973 (United States); Marinkovic, Nebojsa [Chemical Engineering Department, Columbia University, 500 W 120th St, Mudd 801, New York, NY 10027 (United States); Chan, Siu-Wai, E-mail: sc174@columbia.edu [Department of Applied Physics and Applied Mathematics, Materials Science and Engineering Program, Columbia University, New York, NY 10027 (United States)

    2015-09-25

    Highlights: • (1 − x)CeO{sub 2}–xHfO{sub 2} was precipitated (0 < x < 1) and calcined in air. • For x ⩽ 0.14, crystallites ⩽140 nm in size exhibit only the fluorite structure. • This low hafnia solubility is attributable to no auto-reduction (Ce{sup 3+} = 0). • The low solubility is also due to the high temperature required for homogenization. • Coarsening is lessened as Hf{sup 4+} ions slow cation diffusion in these crystallites. - Abstract: Cerium oxide (CeO{sub 2}, “ceria”) and hafnium oxide (HfO{sub 2}, “hafnia”) were aqueously co-precipitated and subsequently calcined to allow for homogenization. The size of the (1−x)CeO{sub 2}–xHfO{sub 2} crystallites, determined by the Scherrer equation, varied from 140 nm for x = 0 to 15 nm for x = 0.73. For x ⩽ 0.14, only cubic structures are visible in X-ray diffractograms, and the lattice parameters are consistent with the values expected for structurally cubic solid solutions of hafnia in ceria. At x = 0.26, tetragonal and monoclinic phases nucleated with the former not being observed in the bulk phase diagram for ceria–hafnia. Therefore, the solubility limit of the cubic structure is between x = 0.14 and x = 0.26 for 40–61 nm crystallites, the sizes of these respective compositions. More specifically, for the 40 nm crystallites of x = 0.26 (1 − x)CeO{sub 2}–xHfO{sub 2}, 15% of the hafnia remains in a structurally cubic solid solution with ceria based on the observed cubic lattice parameter. The compositional domain for the cubic fluorite structure in this study is narrower than other nanostructured (1 − x)CeO{sub 2}–xHfO{sub 2} studies, especially studies with crystallite sizes less than 10 nm, but wider than observed in the bulk and helps to expand the size regime over which the relationship between crystallite size and phase stability is known. The extent of this cubic-structure domain is mainly attributable to the intermediate crystallite size and the roughly zero Ce{sup 3

  20. A search for long-lived radionuclides produced by fast-neutron irradiations of copper, silver, europium, terbium, and hafnium

    International Nuclear Information System (INIS)

    Meadows, J.W.; Smith, D.L.; Ikeda, Y.; Konno, C.

    1990-01-01

    Identical sample packets, each containing samples of elemental copper, silver, europium, terbium, and hafnium, as well as titanium, iron and nickel as dosimeters, have been irradiated in three distinct accelerator neutron fields (at Argonne National Laboratory and Los Alamos National Laboratory in the U.S.A., and Japan Atomic Energy Research Institute, Tokai, Japan) as part of an interlaboratory research collaboration to search for the production of long-lived radionuclides for fusion waste disposal applications. This paper is a progress report on this project. To date, we have detected the following activities, and have obtained preliminary experimental cross section values for several of these: Ag-106m,108m,110m; Eu-150m,152g,154; Tb-158,160; and Hf-175,178m2,179m2,181. (author). 11 refs, 1 fig., 4 tabs

  1. Improved DC performance of AlGaN/GaN high electron mobility transistors using hafnium oxide for surface passivation

    International Nuclear Information System (INIS)

    Liu, Chang; Chor, Eng Fong; Tan, Leng Seow

    2007-01-01

    Improved DC performance of AlGaN/GaN high electron mobility transistors (HEMTs) have been demonstrated using reactive-sputtered hafnium oxide (HfO 2 ) thin film as the surface passivation layer. Hall data indicate a significant increase in the product of sheet carrier concentration (n s ) and electron mobility (μ n ) in the HfO 2 -passivated HEMTs, compared to the unpassivated HEMTs. This improvement in electron carrier characteristics gives rise to a 22% higher I Dmax and an 18% higher g mmax in HEMTs with HfO 2 passivation relative to the unpassivated devices. On the other hand, I gleak of the HEMTs decreases by nearly one order of magnitude when HfO 2 passivation is applied. In addition, drain current is measured in the subthreshold regime. Compared to the unpassivated HEMTs, HfO 2 -passivated HEMTs exhibit a much smaller off-state I D , indicating better turn-off characteristics

  2. About the structure and stability of complex carbonates of thorium (IV), cerium (IV), zirconium (IV), hafnium (IV)

    International Nuclear Information System (INIS)

    Dervin, Jacqueline

    1972-01-01

    This research thesis addressed the study of complex carbonates of cations of metals belonging to the IV A column, i.e. thorium (IV), zirconium (IV), hafnium (IV), and also cerium (IV) and uranium (VI), and more particularly focused on ionic compounds formed in solution, and also on the influence of concentration and nature of cations on stability and nature of the formed solid. The author first presents methods used in this study, discusses their precision and scope of validity. She reports the study of the formation of different complex ions which have been highlighted in solution, and the determination of their formation constants. She reports the preparation and study of the stability domain of solid complexes. The next part reports the use of thermogravimetric analysis, IR spectrometry, and crystallography for the structural study of these compounds

  3. Tribo-electrochemical characterization of hafnium multilayer systems deposited on nitride/vanadium nitride AISI 4140 steel

    Science.gov (United States)

    Mora, M.; Vera, E.; Aperador, W.

    2016-02-01

    In this work is presented the synergistic behaviour among corrosion/wear (tribocorrosion) of the multilayer coatings hafnium nitride/vanadium nitride [HfN/VN]n. The multilayers were deposited on AISI 4140 steel using the technique of physical vapor deposition PVD magnetron sputtering, the tests were performed using a pin-on-disk tribometer, which has an adapted potentiostat galvanostat with three-electrode electrochemical cell. Tribocorrosive parameters such as: Friction coefficient between the coating and the counter body (100 Cr6 steel ball); Polarization resistance by means of electrochemical impedance spectroscopy technique and corrosion rate by polarization curves were determined. It was observed an increase in the polarization resistance, a decrease in the corrosion rate and a low coefficient of friction in comparison with the substrate, due to an increase on the number of bilayers.

  4. Tribo-electrochemical characterization of hafnium multilayer systems deposited on nitride/vanadium nitride AISI 4140 steel

    International Nuclear Information System (INIS)

    Mora, M; Vera, E; Aperador, W

    2016-01-01

    In this work is presented the synergistic behaviour among corrosion/wear (tribocorrosion) of the multilayer coatings hafnium nitride/vanadium nitride [HfN/VN]n. The multilayers were deposited on AISI 4140 steel using the technique of physical vapor deposition PVD magnetron sputtering, the tests were performed using a pin-on-disk tribometer, which has an adapted potentiostat galvanostat with three-electrode electrochemical cell. Tribocorrosive parameters such as: Friction coefficient between the coating and the counter body (100 Cr6 steel ball); Polarization resistance by means of electrochemical impedance spectroscopy technique and corrosion rate by polarization curves were determined. It was observed an increase in the polarization resistance, a decrease in the corrosion rate and a low coefficient of friction in comparison with the substrate, due to an increase on the number of bilayers. (paper)

  5. Animal experiments and clinical trials of {sup 166}Ho-chitosan for various cancers

    Energy Technology Data Exchange (ETDEWEB)

    Lim, Sang Moo; Choi, C W; Kim, E H; Woo, K S; Chung, W S; Lee, J I; Park, S Y; Son, Y S; Lee, S H; Kim, S J; Kim, B G; Kim, J H; Lee, C H [Korea Cancer Center Hospital, Seoul (Korea, Republic of)

    1997-07-01

    {sup 166}Ho is a good therapeutic radionuclide because of its suitable half-life (26.8 hours), high beta energy and 6% gamma ray for imaging. Chitosan is a kind of N-glucosamine with 400 to 500 kD MW, which chelates metal ions and degrades slowly in vivo. As a preclinical studies, we performed cytotoxic effect of {sup 166}Ho-chitosan in a variety of cancer cell lines derived from stomach or ovarian cancer based on MTT assay and HTCA method. To evaluated the absorbed dose to the cavitary wall from {sup 166}Ho-chitosan, intraperitoneal administration of {sup 166}Ho-chitosan in the rat and simulation of energy transfer from the beta particles to the cavity wall using the Monte Carlo code EGS4 was done, and used as a standard for the planning therapy. Intracavitary {sup 166}Ho-chitosan therapy were tried in peritoneal metastatic ovarian and stomach cancers and cystic brain tumors. Intraarterial injection in inoperable primary liver cancer was also tried. As a radiation synovectomy agent, biocompatibility study in the knee joints of rabbits were performed. {sup 166}Ho-chitosan showed synergistic effects with 5-FU or cisplatin in vitro. 97-99% of {sup 166}Ho-chitosan was localized within the peritoneal cavity, and more than 90% of {sup 166}Ho-chitosan was attached to the peritoneal wall. Partial response were observed in 4 among 5 patients with ovarian cancer without severe toxicity. In the cystic brain tumor, 5 of 8 cysts were shrunken in size with thinning of the wall, 2 out of 8 showed growth retardation. In the primary liver cancer, radioactivity was distributed in the teritory of selected hepatic arterial branch, and partial responses were observed in 2 cases. In the knee joints of the rabbits, more than 98% of {sup 166}Ho-chitosan remained in the joint cavity and was stable upto 1 week. 49 refs., 22 tabs. (author)

  6. The interfacial orientation relationship of oxide nanoparticles in a hafnium-containing oxide dispersion-strengthened austenitic stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Miao, Yinbin, E-mail: miao2@illinois.edu [Department of Nuclear, Plasma and Radiological Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); Mo, Kun [Nuclear Engineering Division, Argonne National Laboratory, Lemont, IL 60493 (United States); Cui, Bai [Department of Mechanical and Materials Engineering, University of Nebraska-Lincoln, Lincoln, NE 68588 (United States); Department of Material Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); Chen, Wei-Ying [Department of Nuclear, Plasma and Radiological Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); Miller, Michael K.; Powers, Kathy A. [Center for Nanophase Materials Sciences, Oak Ridge National Laboratory, Oak Ridge, TN 37830 (United States); McCreary, Virginia; Gross, David [Department of Material Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); Almer, Jonathan [X-ray Science Division, Argonne National Laboratory, Lemont, IL 60493 (United States); Robertson, Ian M. [Department of Material Science and Engineering, University of Wisconsin-Madison, Madison, WA 53706 (United States); Department of Material Science and Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States); Stubbins, James F. [Department of Nuclear, Plasma and Radiological Engineering, University of Illinois at Urbana-Champaign, Urbana, IL 61801 (United States)

    2015-03-15

    This work reports comprehensive investigations on the orientation relationship of the oxide nanoparticles in a hafnium-containing austenitic oxide dispersion-strengthened 316 stainless steel. The phases of the oxide nanoparticles were determined by a combination of scanning transmission electron microscopy–electron dispersive X-ray spectroscopy, atom probe tomography and synchrotron X-ray diffraction to be complex Y–Ti–Hf–O compounds with similar crystal structures, including bixbyite Y{sub 2}O{sub 3}, fluorite Y{sub 2}O{sub 3}–HfO{sub 2} solid solution and pyrochlore (or fluorite) Y{sub 2}(Ti,Hf){sub 2−x}O{sub 7−x}. High resolution transmission electron microscopy was used to characterize the particle–matrix interfaces. Two different coherency relationships along with one axis-parallel relation between the oxide nanoparticles and the steel matrix were found. The size of the nanoparticles significantly influences the orientation relationship. The results provide insight into the relationship of these nanoparticles with the matrix, which has implications for interpreting material properties as well as responses to radiation. - Highlights: • The oxide nanoparticles in a hafnium-containing austenitic ODS were characterized. • The nanoparticles are Y–Hf–Ti–O enriched phases according to APT and STEM–EDS. • Two coherency and an axis-parallel orientation relationships were found by HR-TEM. • Particle size has a prominent effect on the orientation relationship (OR). • Formation mechanism of the oxide nanoparticles was discussed based on the ORs.

  7. Evaluation of samarium-153 and holmium-166-EDTMP in the normal baboon model

    Energy Technology Data Exchange (ETDEWEB)

    Louw, W.K.A.; Dormehl, I.C.; Rensburg, A.J. van; Hugo, N.; Alberts, A.S.; Forsyth, O.E.; Beverley, G.; Sweetlove, M.A.; Marais, J.; Loetter, M.G.; Aswegen, A. van

    1996-11-01

    Bone-seeking radiopharmaceuticals such as ethylenediaminetetramethylene phosphonate (EDTMP) complexes of samarium-153 and holmium-166 are receiving considerable attention for therapeutic treatment of bone metastases. In this study, using the baboon experimental model, multicompartmental analysis revealed that with regard to pharmacokinetics, biodistribution, and skeletal localisation, {sup 166}Ho-EDTMP was significantly inferior to {sup 153}Sm-EDTMP and {sup 99m}Tc-MDP. A more suitable {sup 166}Ho-bone-seeking agent should thus be sought for closer similarity to {sup 153}Sm-EDTMP to exploit fully the therapeutic potential of its shorter half-life and more energetic beta radiation.

  8. Development of Therapeutic Modality of Esophageal Cancer Using Ho-166 Stent

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Jong Doo; Park, Kwang Kyun; Lee, Min Geol [Yonsei University Medical College, Seoul (Korea, Republic of); Park, Kyung Bae [Korea Atomic Energy Research Institute, Taejon (Korea, Republic of)

    1997-09-01

    The prognosis of esophageal cancer is poor due absence of serosa which prevent local invasion to the surrounding organs such as aorta, mediastinum, trachea, and bronchi. We developed a Ho-166 Coated Radioactive Self-Expandable Metallic Stent which is a new herapeutic device in the treatment of esophageal cancer and underwent an animal experiment in mongrel dogs. We observed mucosal destruction by 4-6 mCi of Ho-166 without serious complications such as perforation of esophageal wall. Therefore, Ho-166 coated self-expandable stent appears to be an effective therapeutic device in the palliative treatment of esophageal cancer. 17 refs., 4 figs. (author)

  9. Cytotoxic and genotoxic effect of the [{sup 166}Dy]Dy/{sup 166}Ho-EDTMP in vivo generator system in mice

    Energy Technology Data Exchange (ETDEWEB)

    Pedraza-Lopez, Martha [Departamento de Medicina Nuclear, Instituto Nacional de Ciencias Medicas y Nutricion, Salvador Zubiran, Delegacion Tlalpan, Mexico DF 14000 (Mexico); Ferro-Flores, Guillermina [Instituto Nacional de Investigaciones Nucleares, Carretera Mexico-Toluca, Ocoyoacac, Estado de Mexico, CP 52045 (Mexico); Arteaga de Murphy, Consuelo [Departamento de Medicina Nuclear, Instituto Nacional de Ciencias Medicas y Nutricion, Salvador Zubiran, Delegacion Tlalpan, Mexico DF 14000 (Mexico)]. E-mail: consuelo_murphy@yahoo.com.mx; Morales-Ramirez, Pedro [Instituto Nacional de Investigaciones Nucleares, Carretera Mexico-Toluca, Ocoyoacac, Estado de Mexico, CP 52045 (Mexico); Piedras-Ross, Josefa [Departamento de Medicina Nuclear, Instituto Nacional de Ciencias Medicas y Nutricion, Salvador Zubiran, Delegacion Tlalpan, Mexico DF 14000 (Mexico); Murphy-Stack, Eduardo [Hospital Santaelena, Mexico DF (Mexico); Hernandez-Oviedo, Omar [Escuela Superior de Fisica y Matematicas, IPN, Mexico DF (Mexico)

    2004-11-01

    Multiple myeloma and other hematological malignancies have been treated by myeloablative radiotherapy/chemotherapy and subsequent stem cell transplantation. [{sup 166}Dy]Dy/{sup 166}Ho-ethylenediaminetetramethylene phosphonate (EDTMP) forms a stable in vivo generator system with selective skeletal uptake in mice; therefore, it could work as a potential and improved agent for marrow ablation. Induced bone marrow cytotoxicity and genotoxicity are determined by the reduction of reticulocytes (RET) and elevation of micronucleated reticulocyte (MN-RET) in peripheral blood and ablation by bone marrow histological studies. The aim of this study was to determine the bone marrow cytotoxic and genotoxic effect of the [{sup 166}Dy]Dy/{sup 166}Ho-EDTMP in vivo generator system in mice and to evaluate by histopathology its myeloablative potential. Enriched {sup 166}Dy{sub 2}O{sub 3} was irradiated and [{sup 166}Dy]DyCl{sub 3} was added to EDTMP in phosphate buffer (pH 8.0) in a molar ratio of 1:1.75. QC was determined by TLC. Dy-EDTMP complex was prepared the same way with nonirradiated dysprosium oxide. A group of BALB/c mice were intraperitoneally injected with the radiopharmaceutical and two groups of control animals were injected with the cold complex and with 0.9% sodium chloride, respectively. A blood sample was taken at the beginning of the experiments and every 48 h for 12 days postinjection. The animals were sacrificed, organs of interest taken out and the radioactivity determined. The femur was used for histological studies. Flow cytometry analysis was used to quantify the frequency of RET and MN-RET in the blood samples. The MCNP4B Monte Carlo computer code was used for dosimetry calculations. Radiochemical purity was 99% and the mean specific activity was 1.3 MBq/mg. The RET and MN-RET frequency were statistically different in the treatment at the end of the 12-day period demonstrating cytotoxicity and genotoxicity induced by the in vivo generator system. The

  10. Genotoxic and cytotoxic damage by the therapeutic radiopharmaceutical [166Dy]Dy/166Ho-EDTMP as in vivo generator system

    International Nuclear Information System (INIS)

    Pedraza L, M.; Piedras R, J.; Ferro F, G.; Morales R, P.; Murphy S, E.; Hernandez O, O.

    2005-01-01

    In patients with leukemias and multiple myeloma, the cure can be obtained to inclination of a bone marrow transplant (m.o.), for that which one is used a combination of external radiotherapy and chemotherapy with the consequent toxicity to healthy organs. The complex [ 166 Dy]Dy/ 166 Ho-ethylenediaminetetramethylenephosphonate ([ 166 Dy]Dy/ 166 Ho-EDTMP) it forms a generator system in vivo stable with bony selective likeness in mice therefore, this it could work as a therapeutic radiopharmaceutical for bone marrow ablation. The objective of this original work was to determine the genotoxic and cytotoxic damage produced by the [ 166 Dy]Dy/ 166 Ho-EDTMP like a generator system in vivo by means of the reticulocytes reduction (RET) and micronucleus elevation in reticulocytes (RET-MN) in peripheral blood and to evaluate its myeloablative potential for histopathologic studies. It was irradiated 166 Dy 2 O 3 enriched and it was add in form 166 DyCI 3 to the EDTMP in a softening media of phosphates (pH 8), the optimal molar relationship 166 Dy: EDTMP was 1.7:1 and the radiochemical purity was evaluated by ITLC. The Dy:EDTMP complexes, non radioactive, its were prepared in the same way with non irradiated dysprosium oxide. A group of BALB/c mice was injected intraperitoneally with the radiopharmaceutical and two groups of control mice were injected with the non radioactive complex and with sodium chloride 0.9% respectively. Before injecting each one of the solutions it was take a basal sample of peripheral blood of the mouse tail and each 48 h post-injection during 12 d. The animals were sacrificed to obtain the organs of interest and to determine the radioactivity in each one. The femur was used for the histopathologic studies. The quantification of the frequency of RET and RET-MN was carried out by flow cytometry of the sanguine samples and the Monte Carlo code MCNP4B for the dosimetry calculations was used. The radiochemical purity was 99% and in average the specific

  11. Magnetic Resonance Imaging-Based Radiation-Absorbed Dose Estimation of Ho-166 Microspheres in Liver Radioembolization

    NARCIS (Netherlands)

    Seevinck, Peter R.; van de Maat, Gerrit H.; de Wit, Tim C.; Vente, Maarten A. D.; Nijsen, Johannes F. W.; Bakker, Chris J. G.

    2012-01-01

    Purpose: To investigate the potential of magnetic resonance imaging (MRI) for accurate assessment of the three-dimensional Ho-166 activity distribution to estimate radiation-absorbed dose distributions in Ho-166-loaded poly (L-lactic acid) microsphere (Ho-166-PLLA-MS) liver radioembolization.

  12. Technical cooperation for the wider uses of Ho-166 therapeutic agents in European countries

    CERN Document Server

    Park, K B; Choi, S M; Han, K H; Hong, Y D; Park, W W; Shin, B C

    2002-01-01

    Czech has put their priority in developing the radiopharmaceuticals based on reactor produced Ho-166 and a related fabrication will be extended to other EU conturies including Germany, France, etc after a development of project. The collaboration will be based on the mutual agreement for developing the between research institutes, industries and academic institutes and further researches should be followed by the issue of developing radiopharmaceuticals using Ho-166. To strengthen the collaboration, detailed discussions for the practical collaboration have been made through the visitation to the research institution of each counter part. For implementing the collaboration between NPI and KAERI, an institutional basis technical cooperation agreement(TCA) will be concluded. Furthermore, agreement for the substantial collaboration on Ho-166 related researches will be made after the conclusion of the TCA. It will accelerate the commercialization of KAERI developed Ho-166 therapeutic agents into other European cou...

  13. CD166/ALCAM expression is characteristic of tumorigenicity and invasive and migratory activities of pancreatic cancer cells.

    Directory of Open Access Journals (Sweden)

    Kenji Fujiwara

    Full Text Available CD166, also known as activated leukocyte cell adhesion molecule (ALCAM, is expressed by various cells in several tissues including cancer. However, the role of CD166 in malignant tumors is controversial, especially in pancreatic cancer. This study aimed to clarify the role and significance of CD166 expression in pancreatic cancer.We performed immunohistochemistry and flow cytometry to analyze the expression of CD166 in surgical pancreatic tissues and pancreatic cancer cell lines. The differences between isolated CD166+ and CD166- pancreatic cancer cells were analyzed by invasion and migration assays, and in mouse xenograft models. We also performed quantitative RT-PCR and microarray analyses to evaluate the expression levels of CD166 and related genes in cultured cells.Immunohistochemistry revealed high expression of CD166 in pancreatic cancer tissues (12.2%; 12/98 compared with that in normal pancreas controls (0%; 0/17 (p = 0.0435. Flow cytometry indicated that CD166 was expressed in 33.8-70.2% of cells in surgical pancreatic tissues and 0-99.5% of pancreatic cancer cell lines. Invasion and migration assays demonstrated that CD166- pancreatic cancer cells showed stronger invasive and migratory activities than those of CD166+ cancer cells (p<0.05. On the other hand, CD166+ Panc-1 cells showed a significantly stronger colony formation activity than that of CD166- Panc-1 cells (p<0.05. In vivo analysis revealed that CD166+ cells elicited significantly greater tumor growth than that of CD166- cells (p<0.05 in both subcutaneous and orthotopic mouse tumor models. mRNA expression of the epithelial-mesenchymal transition activator Zeb1 was over-expressed in CD166- cells (p<0.001. Microarray analysis showed that TSPAN8 and BST2 were over-expressed in CD166+ cells, while BMP7 and Col6A1 were over-expressed in CD166- cells.CD166+ pancreatic cancer cells are strongly tumorigenic, while CD166- pancreatic cancer cells exhibit comparatively stronger

  14. Animal experiments and clinical trials of 166Ho-Chitosan for various cancers

    International Nuclear Information System (INIS)

    Lim, S.M.; Choi, C.W.; Park, S.Y.; Lee, S.H.; Lee, B.H.; Park, K.B.

    1998-01-01

    166 Ho-Chitosan is a complex of 166 Ho and N-glucosamine with 400 to 500 kD MW, which chelates metal ions and degrades slowly in vivo. In mice, 166 H-Chitosan administered intraperitoneally was uniformly bound to the peritoneal wall (94%), and the surface dose calculated by Monte Carlo simulation (EGS 4 code) was 81 Gy/uCi/cm 2 . 166 Ho-Chitosan was administered intraperitoneally as an adjunct in the treatment of ovarian cancer with diffuse spread of malignant cells in the peritoneal surfaces including the diaphragm. 97-99% of 166 Ho-Chitosan was localized within the peritoneal cavity, and more than 90% of 166 Ho-Chitosan was attached to the peritoneal wall. Partial response were observed in 4 among 5 patients with ovarian cancer without severe toxicity. Intracavitary radiation therapy with 166 Ho-Chitosan in the cystic brain tumor, 5 or 8 cysts were shrunken in size with thinning of the wall, 2 out of 8 showed growth retardation. For large or multiple primary liver cancers, which were inoperable and resistent to chemotherapy. 166 Ho-Chitosan was used for intraarterial injection, because this solution became gel with neutral pH. In the primary liver cancer, radioactivity was distributed in the territory of selected hepatic arterial branch, and partial responses were observed in 2 cases. For the large solitary liver tumor, which was not operable due to its location, direct intratumoral injection of the radioisotope had a limited response. 18 FDG PET was a useful tool to follow up those radionuclide therapy, and guide to plan the next therapy. In one case of the large single metastatic stomach cancer in the liver, 18 FDG PET was done two weeks after intratumoral injection of 166 Ho-Chitosan, which showed cold defects matched with distribution of 166 Ho-Chitosan, and second injection was guided by PET image. Various methods of the administration of 166 Ho-Chitosan could be used for the treatment of the cancers. (author)

  15. 166 Ho-HA Evaluation as therapeutic agent for rheumatoid arthritis treatment

    International Nuclear Information System (INIS)

    Chandia, M; Errazu, X; Mendoza, P; Troncoso, F; Jofre, J; Sierralta, P

    2003-01-01

    Aim: Rheumatoid arthritis is a limiting disease having, among its pathological features, the inflammation of synovial tissue with progressive and later destruction of the articulation. This lead to joint deformation and loss of its function, generating pain and reducing the mobility of the affected articulation. The aim was to evaluate 166 Ho-Hydroxyapatite ( 166 Ho-HA) as potential radiopharmaceutical for the syntomatic treatment of chronic and acute arthritis Materials and Methods: 166 Holmiun was produced by irradiation of Ho 2 O 3 at La Reina Research Reactor, Nuclear Chilean Energy Commission. Hydroxyapatite was in-house synthetized. Its labelling and quality controls follows the internationally accepted procedures. An antigen arthritis was induced to eight New Zealand rabbits with the 166 Ho-HA radiochemical being administred thereafter in two dosage modalities (single and double). The compound therapeutic efficiency was evaluated based upon clinical improvement and images from the inflamated articulation using 67 Ga citrate before and after 166 Ho-HA injection. Results: The radiochemical purity of the innoculated compound was greater than 98% as measured under sterility conditions. Clinically, an inflamation reduction (2 cm), appetite improvement and general well being was observed. The 166 Ho-HA distribution and localization was monitored using gamma camera images taken at 4 and 24 h. There was no evidence of extraarticular leakage. From the 67 Ga citrate imaging, the acute group shows an overall improvement of well being corresponding to a lesser uptake at the inflamated articulation, regarding to the chronic group. The 166 Ho-HA double dosis, compared to the single dosis, suggest a reduced uptake of 67 Ga citrate at the inflamated tissue, meaning an increased therapeutic effect. Conclusions: 166 Ho-HA is usefull as therapeutic agent for the syntomatic treatment of rheumatoideal arthritis as shown by imaging and clinical examination (author)

  16. 166Ho-HA evaluation as therapeutic agent for rheumatoid arthritis treatment

    International Nuclear Information System (INIS)

    Chandia, M.C.; Errazu, X.C.; Pinto, L.N.; Godoy, N.O.; Avila, M.J.; Mendoza, P.; Mendoza, J.; Jofre, J.; Sirraalta, P.

    2002-01-01

    Aim: Rheumatoid arthritis is a limiting disease having, among its pathological features, the inflammation of synovial tissue with progressive and later destruction of the articulation. This leads to joint deformation and loss of its function, generating pain and reducing the mobility of the affected articulation. The aim was to evaluate 166 Ho-Hydroxyapatite ( 166 Ho-HA) as potential radiopharmaceutical for the symptomatic treatment of chronic and acute arthritis. Materials and Methods: Holmiun-166 was produced by irradiation of Ho 2 O 3 at La Reina Research Reactor, Nuclear Chilean Energy Commission. Hydroxyapatite was in-house synthesized. Its labelling and quality controls follows the internationally accepted procedures. An antigen's arthritis was induced to eight New Zealand rabbits with the 166 Ho-HA radiochemical being administered thereafter in two dosage modalities (single and double). The compound therapeutic efficiency was evaluated based upon clinical improvement and images from the inflamated articulation using 67 Ga citrate before and after 166 Ho-HA injection. Results: The radiochemical purity of the inoculated compound was greater than 98% as measured under sterility conditions. Clinically, an inflammation reduction (2 cm), appetite improvement and general well being was observed. The 166 Ho-HA distribution and localization was monitored using gamma camera images taken at 4 and 24 h. There was no evidence of extra articular leakage. From the 67 Ga citrate imaging, the acute group shows an overall improvement of well being corresponding to a lesser uptake at the inflamated articulation, regarding to the chronic group. The 166 Ho-HA double doses, compared to the single doses, suggest a reduced uptake of 67 Ga citrate at the inflamated tissue, meaning an increased therapeutic effect. Conclusions: 166 Ho-HA is useful as therapeutic agent for the symptomatic treatment of rheumatoid arthritis as shown by imaging and clinical examination

  17. Study on preparation of 166Ho-Chitosan oriented in the treatment of liver cancer

    International Nuclear Information System (INIS)

    Dang Ho Hong Quang; Duong Van Dong; Bui Van Cuong; Nguyen Thanh Binh; Nguyen Thanh Nhan; Nguyen Dinh Lam; Nguyen Thi Thu

    2017-01-01

    This study describes the process for the preparation and quality control of 166 Ho-Chitosan product. The labeling conditions of chitosan with 166 Ho radioisotope were carried out such as the concentration of chitosan, pH, temperature and reaction time to create 166 Ho-Chitosan compositions. Product quality inspection 166 Ho-Chitosan on the criteria as nuclide purity, radiochemical purity, tested for sterility and bacterial endotoxin. The results of survey showed that 166 Ho labeled with chitosan were completed in 1% acetic acid, 3 mCi: 30 mg ratio at pH = 3, marking time at room temperature for 30 minutes. The results of quality test have shown radionuclide purity ≥ 99%, radiochemical purity ≥ 98%, meeting the criteria for the aseptic and bacterial endotoxin according to IV Vietnam pharmacopoeia. From the above mentioned, 166 Ho-Chitosan compositions meet the quality criteria of the radiopharmaceuticals, therefore, it can be used in pre-clinical research and its application in clinical treatment. (author)

  18. Implantation of titanium, chromium, yttrium, molybdenum, silver, hafnium, tantalum, tungsten and platinum ions generated by a metal vapor vacuum ion source into 440C stainless steel

    International Nuclear Information System (INIS)

    Sasaki, Jun; Hayashi, Kazunori; Sugiyama, Kenji; Ichiko, Osami; Hashiguchi, Yoshihiro

    1992-01-01

    Titanium, yttrium, molybdenum, silver, chromium, hafnium, tantalum, tungsten and platinum ions generated by a metal vapor vacuum arc (MEVVA) ion source were implanted into 440C stainless steel in the dose region 10 17 ions cm -2 with extraction voltages of up to 70 kV. Glow discharge spectroscopy (GDS), friction coefficient, and Vickers microhardness of the specimens were studied. Grooves made by friction tests were investigated by electron probe microanalysis (EPMA). GDS showed incorporation of carbon in the yttrium, hafnium, tantalum, tungsten and platinum implanted specimens, as well as titanium implanted samples. A large amount of oxygen was observed in the yttrium implanted specimen. The friction coefficient was measured by reciprocating sliding of an unimplanted 440C ball without lubricant at a load of 0.245 N. The friction decreased and achieved a stable state after implantation of titanium, hafnium and tantalum. The friction coefficient of the platinum implanted specimen showed a gradual decrease after several cycles of sliding at high friction coefficient. The yttrium implanted sample exhibited a decreased but slightly unstable friction coefficient. Results from EPMA showed that the implanted elements, which gave decreased friction, remained even after sliding of 200 cycles. Implantation of chromium, molybdenum, silver and tungsten did not provide a decrease in friction and the implants were gone from the wear grooves after the sliding tests. (orig.)

  19. Studies on therapeutic method of liver cancer(hapatocellular carcinome)by Holmium-166 radionuclide

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Jong Tae; Yoo, H. S.; Kim, M. J.; Han, K. H.; Park, C. I. [Yonsei University Medical College, Seoul (Korea, Republic of)

    1997-07-01

    As the study of radioactive nuclide, Holmium-166 in the treatment of liver cancer(hepatocellular carcinoma), this study was performed under the base of animal experimental. Using dog liver, percutaneous injection of Ho-166 MAA or chitosan with premade dose was done under the ultrasound guidance. Continuously the same procedure as previous one was performed in the skin hapatoma, which was developed by the injection of hepatocellular carcinoma cell in the nude mouse, In case of injected normal liver of dog, imaging study including ultrasound, CT and MRI was done in order to evaluate effect of Ho-166 and pathologic reaction. The result showed well defined nectosis of normal liver as well as skin hepatoma. The area of nectosis is dependent on the dose of injected Ho-166. Generally, pathologic reaction is tissue coagulation nectosis, Ho-166 particles, fibrosis and hemorrhage. In the clinical study, 50 patients with hapatoma was selected for this study under the agreement of patient. Under ultrasound guidance percutaneous injection of Ho-166 Maa or chitosan to tumor was performed and follow-up study was extended from 6 to 12 month. The result showed that 64% of patient were completely treated. Overall, the effect of treatment could be obtained in 41 patient (82%) among 50 hepatoma patient. Conclusively Ho-166 is thought to be a compromising agent in the treatment of hepatocellular carcinoma and one of therapeutic modality, if it is established internally and world-wide. In the future, the popular percutaneous ethanol injection method will be replaced to this method. 19 refs., 1 tabs., 14 figs. (author)

  20. Study on the preparation of 166Ho-patch for a skin cancer treatment

    International Nuclear Information System (INIS)

    Kim, Y. M.; Kim, K. H.; Han, K. H.; Park, E. W.; Shin, B. C.; Park, K. B.; Lee, J. D.

    1998-01-01

    Radioactive patch containing holmium-166 has been developed for skin cancer treatment, and then applied to animal model and patients with malignant skin cancer. 165Ho-Patch prepared by dissolving polyurethane and 165 Ho(NO 3 ) 3 ·5H 2 O in mixing solvent of DMF and THF and casting on aluminium dish was irradiated in ''HANARO'' reactor ( Φth = 1.25 X 1013 n/cm 2 '·sec, power = 15 MW), which results in preparing 166 Ho-Patch emitting β energy of Max. 1.86 MeV (51 %), 1.78 MeV (48 %), mean 0.67 MeV and low γ energy. The 166 Ho-Patch specially designed was applied to the superficial skin cancers. Their efficacy and safety have been investigated for several months. Radioactive patch was ready to prepare by post-irradiation without special danger by radioactive material. Skin tumor could be successfully treated with 166 Ho-Patch in animal model and patients. In animal model and patients, the world's first noninvasive 166Ho-Patch readily prepared by post-irradiation proved to be safe and effective in treatment for skin cancer

  1. Standardization Of 166mHo Using Merlin Gerin Ionization Chamber System

    International Nuclear Information System (INIS)

    Nazaroh; Chandra; Hermawan; Juita Erni

    2000-01-01

    Standardization of 166m Ho using Merlin Gerin ionization chamber system has been carried out. Solution of 166m Ho was obtained from ETL-Japan. Activity measurement of 166m Ho was done before and after preparation. The result of activity measurement by P3KRBiN before preparation was (134.47±0.4) kBq/g, and after preparation was (131.98±1.85) kBq/g, at reference time, 1 March 1999. The ETL's result was (130.4±0.4) kBq/g, at the same reference time. The difference between P3KRBiN's (without uncertainty) and ETL's measurement result was 1.2% and if the uncertainty was included, both measurements was agreed

  2. Development of radioactive 166Ho-coated balloon and its dose estimation

    International Nuclear Information System (INIS)

    Park, K. B.; Kim, K. H.; Hong, Y. D.; Park, E. W.

    2000-01-01

    The use of balloon with radioisotope is a promising method to prevent restenosis after transluminal coronary arterial angioplasty or stent implantation. In this study, we have developed a new radioactive coated balloon, which is prepared by coating the surface of existing balloon with 166 Ho instead of being filled with beta sources which emit high energy beta-particles for the purpose of the delivery of sufficient radiation to the vessel wall. To estimate the safety of 166 Ho-coated balloon, leaching test and radiation resistance test of the balloon were performed. The absorbed dose distributions around the 166 Ho-coated balloon were estimated by means of Monte Carlo simulation and the initial activities for optimal therapeutic regimen were determined on the basis of this results

  3. Isomer decay spectroscopy of 164Sm and 166Gd: midshell collectivity around N=100.

    Science.gov (United States)

    Patel, Z; Söderström, P-A; Podolyák, Zs; Regan, P H; Walker, P M; Watanabe, H; Ideguchi, E; Simpson, G S; Liu, H L; Nishimura, S; Wu, Q; Xu, F R; Browne, F; Doornenbal, P; Lorusso, G; Rice, S; Sinclair, L; Sumikama, T; Wu, J; Xu, Z Y; Aoi, N; Baba, H; Bello Garrote, F L; Benzoni, G; Daido, R; Fang, Y; Fukuda, N; Gey, G; Go, S; Gottardo, A; Inabe, N; Isobe, T; Kameda, D; Kobayashi, K; Kobayashi, M; Komatsubara, T; Kojouharov, I; Kubo, T; Kurz, N; Kuti, I; Li, Z; Matsushita, M; Michimasa, S; Moon, C-B; Nishibata, H; Nishizuka, I; Odahara, A; Şahin, E; Sakurai, H; Schaffner, H; Suzuki, H; Takeda, H; Tanaka, M; Taprogge, J; Vajta, Zs; Yagi, A; Yokoyama, R

    2014-12-31

    Excited states in the N=102 isotones 166Gd and 164Sm have been observed following isomeric decay for the first time at RIBF, RIKEN. The half-lives of the isomeric states have been measured to be 950(60) and 600(140) ns for 166Gd and 164Sm, respectively. Based on the decay patterns and potential energy surface calculations, including β6 deformation, a spin and parity of 6- has been assigned to the isomeric states in both nuclei. Collective observables are discussed in light of the systematics of the region, giving insight into nuclear shape evolution. The decrease in the ground-band energies of 166Gd and 164Sm (N=102) compared to 164Gd and 162Sm (N=100), respectively, presents evidence for the predicted deformed shell closure at N=100.

  4. Isomer Decay Spectroscopy of Sm 164 and Gd 166 : Midshell Collectivity Around N =100

    Science.gov (United States)

    Patel, Z.; Söderström, P.-A.; Podolyák, Zs.; Regan, P. H.; Walker, P. M.; Watanabe, H.; Ideguchi, E.; Simpson, G. S.; Liu, H. L.; Nishimura, S.; Wu, Q.; Xu, F. R.; Browne, F.; Doornenbal, P.; Lorusso, G.; Rice, S.; Sinclair, L.; Sumikama, T.; Wu, J.; Xu, Z. Y.; Aoi, N.; Baba, H.; Bello Garrote, F. L.; Benzoni, G.; Daido, R.; Fang, Y.; Fukuda, N.; Gey, G.; Go, S.; Gottardo, A.; Inabe, N.; Isobe, T.; Kameda, D.; Kobayashi, K.; Kobayashi, M.; Komatsubara, T.; Kojouharov, I.; Kubo, T.; Kurz, N.; Kuti, I.; Li, Z.; Matsushita, M.; Michimasa, S.; Moon, C.-B.; Nishibata, H.; Nishizuka, I.; Odahara, A.; Şahin, E.; Sakurai, H.; Schaffner, H.; Suzuki, H.; Takeda, H.; Tanaka, M.; Taprogge, J.; Vajta, Zs.; Yagi, A.; Yokoyama, R.

    2014-12-01

    Excited states in the N =102 isotones Gd 166 and Sm 164 have been observed following isomeric decay for the first time at RIBF, RIKEN. The half-lives of the isomeric states have been measured to be 950(60) and 600(140) ns for Gd 166 and Sm 164 , respectively. Based on the decay patterns and potential energy surface calculations, including β6 deformation, a spin and parity of 6- has been assigned to the isomeric states in both nuclei. Collective observables are discussed in light of the systematics of the region, giving insight into nuclear shape evolution. The decrease in the ground-band energies of Gd 166 and Sm 164 (N =102 ) compared to Gd 164 and Sm 162 (N =100 ), respectively, presents evidence for the predicted deformed shell closure at N =100 .

  5. Mechanistic Studies of Hafnium-Pyridyl Amido-Catalyzed 1-Octene Polymerization and Chain Transfer Using Quench-Labeling Methods.

    Science.gov (United States)

    Cueny, Eric S; Johnson, Heather C; Anding, Bernie J; Landis, Clark R

    2017-08-30

    Chromophore quench-labeling applied to 1-octene polymerization as catalyzed by hafnium-pyridyl amido precursors enables quantification of the amount of active catalyst and observation of the molecular weight distribution (MWD) of Hf-bound polymers via UV-GPC analysis. Comparison of the UV-detected MWD with the MWD of the "bulk" (all polymers, from RI-GPC analysis) provides important mechanistic information. The time evolution of the dual-detection GPC data, concentration of active catalyst, and monomer consumption suggests optimal activation conditions for the Hf pre-catalyst in the presence of the activator [Ph 3 C][B(C 6 F 5 ) 4 ]. The chromophore quench-labeling agents do not react with the chain-transfer agent ZnEt 2 under the reaction conditions. Thus, Hf-bound polymeryls are selectively labeled in the presence of zinc-polymeryls. Quench-labeling studies in the presence of ZnEt 2 reveal that ZnEt 2 does not influence the rate of propagation at the Hf center, and chain transfer of Hf-bound polymers to ZnEt 2 is fast and quasi-irreversible. The quench-label techniques represent a means to study commercial polymerization catalysts that operate with high efficiency at low catalyst concentrations without the need for specialized equipment.

  6. An Auger electron spectroscopy study on the anodization process of high-quality thin-film capacitors made of hafnium

    International Nuclear Information System (INIS)

    Noya, Atsushi; Sasaki, Katsutaka; Umezawa, Toshiji

    1989-01-01

    Formation process of the anodic oxide film of hafnium for use as a thin-film capacitor has been examined by the current-voltage characteristics of the anodization and the in-depth analysis of formed oxide using Auger electron spectroscopy. It is found that the oxide growth obeys three different rate laws such as the linear rate law at first and next the parabolic rate law during the constant current anodization, and then the reciprocal logarithmic rate law during the constant voltage anodization following after the constant current process. From the Auger electron spectroscopy analysis, it is found that the shape of the compositional depth profile of the grown oxide film varies associating with the rate law of oxidation obeyed. The variation of depth profile correlating with the rate law is discussed with respect to each elementary process such as the transport and/or the reaction of chemical species interpreted from the over-all behavior of anodization process. It is revealed that the stoichiometric film having an interface with sharp transition, which is favorable for obtaining excellent electrical properties of the capacitor, can be obtained under the condition that the phase-boundary reaction is the rate-determining step of the anodization. The constant voltage anodization process also satisfies such circumstances and therefore can be favorable method for preparing highquality thin-film capacitors. (author)

  7. Evaluation and Enhancement of the Oxygen Reduction Reaction Activity on Hafnium Oxide Nanoparticles Assisted by L(+)-lysine

    International Nuclear Information System (INIS)

    Chisaka, Mitsuharu; Itagaki, Noriaki

    2016-01-01

    Evaluation of the oxygen reduction reaction (ORR) on oxide compounds is difficult owing to the insulating nature of oxides. In this study, various amounts of L(+)-lysine were added to the precursor dispersion for the hydrothermal synthesis of hafnium oxide nanoparticles on reduced graphene oxide sheets (HfO_x–rGO) to coat the HfO_x catalysts with layers of carbon, thereby increasing the conductivity and number of active sites. When the mass ratio of L(+)-lysine to GO, R, was above 26, carbon layers were formed and the amount monotonically increased with increasing R, as noted by cyclic voltammogrametry. X-ray photoelectron spectroscopy and rotating disk electrode analyses revealed that pyrolysis produced ORR-active oxygen defects, whose formation was proposed to involve carbothermal reduction. When 53 ≤ R ≤ 210, HfO_x–rGO contained a similar amount of oxygen defects and ORR activity, as represented by an onset potential of 0.9 V versus the reversible hydrogen electrode in 0.1 mol dm"−"3 H_2SO_4. However, the number of active sites depended on R due to the amount of L(+)-lysine-derived carbon layers that increased both the number of active sites and resistivity towards oxygen diffusion.

  8. IER-297 CED-2: Final Design for Thermal/Epithermal eXperiments with Jemima Plates with Polyethylene and Hafnium

    Energy Technology Data Exchange (ETDEWEB)

    Nelson, A. J. [Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States); Percher, C. M. [Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States); Zywiec, W. J. [Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States); Heinrichs, D. P. [Lawrence Livermore National Lab. (LLNL), Livermore, CA (United States)

    2018-01-11

    This report presents the final design (CED-2) for IER-297, and focuses on 15 critical configurations using highly enriched uranium (HEU) Jemima plates moderated by polyethylene with and without hafnium diluent. The goal of the U.S. Nuclear Criticality Safety Program’s Thermal/Epithermal eXperiments (TEX) is to design and conduct new critical experiments to address high priority nuclear data needs from the nuclear criticality safety and nuclear data communities, with special emphasis on intermediate energy (0.625 eV – 100 keV) assemblies that can be easily modified to include various high priority diluent materials. The TEX (IER 184) CED-1 Report [1], completed in 2012, demonstrated the feasibility of meeting the TEX goals with two existing NCSP fissile assets, plutonium Zero Power Physics Reactor (ZPPR) plates and highly enriched uranium (HEU) Jemima plates. The first set of TEX experiments will focus on using the plutonium ZPPR plates with polyethylene moderator and tantalum diluents.

  9. Cation exchange resins labeled with holmium-166 for treatment of liver malignancy

    International Nuclear Information System (INIS)

    Costa, Renata F.; Osso Junior, Joao A.

    2008-01-01

    The increasing interest in new therapeutic radiopharmaceuticals is prompting investigators to utilize isotopes with more focused capabilities for treating various tumors, reducing the negative effects on neighboring healthy cells. Local radionuclide therapy using radioactive microspheres is a promising therapy for non-operable group of patients suffering from liver malignancies. Many publications have shown the success of this technique. The emphasis in the present work is the resin-based microspheres labeled with 166 Ho. The production of 166 Ho is feasible in the IEA-R1 Reactor at IPEN-CNEN/SP, because it does not need high power and high neutron fluxes. Samples of Ho 2 O 3 were irradiated in selected positions of the nuclear reactor IEA-R1 at IPEN/CNEN-SP. The neutron flux was 1.0 x10 13 n.s -1 .cm -2 for 1 hour. The dissolution of Ho 2 O 3 was studied with different volumes of 0.1M HCl and also varying the heating temperature. The AG50W-X8 200-400 mesh and CM Sephadex C-25 cation exchange resins were labeled with 166 Ho. The retention of 166 Ho in the resins was studied and also its stability. The results of the dissolution experiments of Ho 2 O 3 showed that there is a direct relation between the increasing volumes needed to dissolve higher masses, and also the positive effect of raising the temperature. The results show very good retention of 166 Ho in both columns, even when high volumes of 0.1M HCl are passed through the column containing the resins and its good stability towards saline solution, PBS solution and glucose.Although the resins employed in this work did not have the right particle size (20-50μm), the chemical behavior showed the very good labeling of the resins with 166 Ho, and its stability. (author)

  10. New therapeutic agent for radiation synovectomy - preparation of {sup 166}Ho-EDTMP-HA particle

    Energy Technology Data Exchange (ETDEWEB)

    Bai, H.; Jin, X.; Du, J.; Wang, F.; Chen, D.; Fan, H.; Cheng, Z.; Zhang, J. [China Institute of Atomic Energy, Beijing (Switzerland). Isotope Department

    1997-10-01

    In order to prepare new therapeutical agent for radiation synovectomy, Hydroxyapatite (HA) was labelled with {sup 166}Ho by EDTMP that had high affinity to HA particles. Radiolabelling of HA particles was divided into two steps, {sup 166}Ho-EDTMP was prepared first; then mixed with HA particles completely and vibrated for 15 minutes on the micromixer at room temperature, washed 3 times with deionized water. Radiolabelling particle was separated from free {sup 166}Ho via centrifugation to determine its radiolabelling efficiency. {sup 166}Ho-EDTMP-HA and {sup 166}Ho-EDTMP were injected into knee joint of normal rabbits respectively, every group was killed at different time postinjection, took out major organ and collected urine and blood, then weighted and determined their radio counts. HA particles, as a natural component of bone was known to have good compatibility with soft tissue and biodegrade into calcium and phosphate in vivo. It was readily prepared from common chemical and formed into particles of desired size range in a controlled process, it had high stability in vitro and vivo. Radiolabelling of HA particle with {sup 166}Ho by EDTMP was simple to perform and provides an excellent labelling yield that was more than 95% under the optimal labelling condition. The optimal labelling condition at room temperature was pH 6.0-8.0 and vibration time 15 minutes. The absorbed capacity of HA particle was 5 mg Ho/g HA particle and size of radiolabelling particle was at range of 2-5,{mu}m that is suitable for therapy of radiation synovectomy. {sup 166}Ho-EDTMP-HA particle demonstrated high in vitro stability in either normal saline or 1% BSA solution, but instability under extremely acidic condition (pH 1-2). The control studies performed with {sup 166}Ho-EDTMP not bound to HA particle provided information on the distribution of radioactivity that would occur upon leakage of the radiochemical compound from joint. Its short half-life, its extremely low leakage from the

  11. {sup 166} Ho-EDTMP in detecting bone metastases: preliminary results

    Energy Technology Data Exchange (ETDEWEB)

    Achando, S.S.; Fernandes, L.; Herrerias, R.; Muramoto, E.; Almeida, M.A.T.; Pereira, N.S. de; Mengatti, J. [Instituto de Pesquisas Energeticas e Nucleares (IPEN), Sao Paulo, SP (Brazil)

    1995-12-31

    Holmium-166-EDTMP (ethylene-dimine-tetra methylene phosphonic acid) due to its promising biological properties, has proved to be a palliating therapeutic agent for bone cancer in human beings. In a basic medium, {sup 166} Ho-EDTMP can be readily prepared with a complexing molar ratio EDTMP/Ho 4.34. The radiochemical purity of the complex was higher than 98%. The biodistribution in rats and mice, showed a high skeletal uptake, a fast blood clearance and a low soft tissue uptake and a lesion to normal bone ratio equal to 2. (author). 3 refs., 4 tabs.

  12. Isomer Decay Spectroscopy of Sm-164 and Gd-166: Midshell Collectivity Around N=100

    OpenAIRE

    Patel, Z; Soederstroem, P-A; Podolyak, Z; Regan, PH; Walker, PM; Watanabe, H; Ideguchi, E; Simpson, GS; Liu, HL; Nishimura, S; Wu, Q; Xu, FR; Browne, F; Doornenbal, P; Lorusso, G

    2014-01-01

    © 2014 American Physical Society. Excited states in the N=102 isotones Gd166 and Sm164 have been observed following isomeric decay for the first time at RIBF, RIKEN. The half-lives of the isomeric states have been measured to be 950(60) and 600(140) ns for Gd166 and Sm164, respectively. Based on the decay patterns and potential energy surface calculations, including β6 deformation, a spin and parity of 6- has been assigned to the isomeric states in both nuclei. Collective observables are disc...

  13. Our first clinical experience with radiosynoviorthesis by means of (166)Ho-holmium-boro-macroaggregates.

    Science.gov (United States)

    Kraft, Otakar; Kasparek, R; Ullmann, V; Melichar, F; Kropacek, M; Mirzajevov, M

    2005-01-01

    In this paper, we evaluate the therapeutic and adverse effects of the application of 166-holmium-boro-macroaggregates (HMBA) in radiosynovectomy (RSO) of the knees. We assessed the efficacy and safety of (166)Ho-HBMA in a prospective clinical trial in patients suffering from chronic synovitis. An effective component of radiopharmaceutical (166)Ho-boro-macroaggregates is radionuclide (166)Ho which has both beta-emission and gamma-emission. The physical half-life time of 166 Ho is 26.8 hours. After application of the radiopharmaceutical into a joint cavity, the effect of beta-emission causes radiation necrosis of pathologically changed (inflamed) synovial membrane. From 15th April 2005, we have started RSO of knees by means of new radiopharmaceutical (166)Ho-boro-macroaggregates in patients with gonarthrosis, rheumatoid arthritis, chronic synovitis, psoriatic arthritis, gout arthropathy. Seventeen intra-articular injections were performed in fifteen patients receiving a mean activity of 972 MBq (range: 904-1,057 MBq) (166)Ho-HMBA. The patients were hospitalized for three days. Side effects were evaluated during hospital stay and after 6-8 weeks. Static scintigraphy of knee joints and measurements of blood radioactivity were performed. Therapeutic effects were evaluated after 6-8 weeks. In 2 hours and 2 days after application, we proved, by means of knee and inguinal scintigraphy, only insignificant radiopharmaceutical leakage from the joint cavity to the inguinal lymph nodes in four patients. In treated patients, no serious adverse effects occurred. Nine patients were without complaints; 4 patients had slight knee exsudation and 2 patients had great exsudation. Therapeutic effects after 6-8 weeks were as follows: 2 patients were without pain, 9 with lower pain, 3 with the same pain and 1 patient with increased pain. Joint motion was improved in 7 patients, remained the same in 7 patients and was impaired in 1 patient. Analgesics consumption was lower in 5 patients

  14. New therapeutic agent for radiation synovectomy - preparation of 166Ho-EDTMP-HA particle

    International Nuclear Information System (INIS)

    Bai, H.; Jin, X.; Du, J.; Wang, F.; Chen, D.; Fan, H.; Cheng, Z.; Zhang, J.

    1997-01-01

    In order to prepare new therapeutical agent for radiation synovectomy, Hydroxyapatite (HA) was labelled with 166 Ho by EDTMP that had high affinity to HA particles. Radiolabelling of HA particles was divided into two steps, 166 Ho-EDTMP was prepared first; then mixed with HA particles completely and vibrated for 15 minutes on the micromixer at room temperature, washed 3 times with deionized water. Radiolabelling particle was separated from free 166 Ho via centrifugation to determine its radiolabelling efficiency. 166 Ho-EDTMP-HA and 166 Ho-EDTMP were injected into knee joint of normal rabbits respectively, every group was killed at different time postinjection, took out major organ and collected urine and blood, then weighted and determined their radio counts. HA particles, as a natural component of bone was known to have good compatibility with soft tissue and biodegrade into calcium and phosphate in vivo. It was readily prepared from common chemical and formed into particles of desired size range in a controlled process, it had high stability in vitro and vivo. Radiolabelling of HA particle with 166 Ho by EDTMP was simple to perform and provides an excellent labelling yield that was more than 95% under the optimal labelling condition. The optimal labelling condition at room temperature was pH 6.0-8.0 and vibration time 15 minutes. The absorbed capacity of HA particle was 5 mg Ho/g HA particle and size of radiolabelling particle was at range of 2-5,μm that is suitable for therapy of radiation synovectomy. 166 Ho-EDTMP-HA particle demonstrated high in vitro stability in either normal saline or 1% BSA solution, but instability under extremely acidic condition (pH 1-2). The control studies performed with 166 Ho-EDTMP not bound to HA particle provided information on the distribution of radioactivity that would occur upon leakage of the radiochemical compound from joint. Its short half-life, its extremely low leakage from the joint and its even distribution throughout

  15. Trap state passivation improved hot-carrier instability by zirconium-doping in hafnium oxide in a nanoscale n-metal-oxide semiconductor-field effect transistors with high-k/metal gate

    International Nuclear Information System (INIS)

    Liu, Hsi-Wen; Tsai, Jyun-Yu; Liu, Kuan-Ju; Lu, Ying-Hsin; Chang, Ting-Chang; Chen, Ching-En; Tseng, Tseung-Yuen; Lin, Chien-Yu; Cheng, Osbert; Huang, Cheng-Tung; Ye, Yi-Han

    2016-01-01

    This work investigates the effect on hot carrier degradation (HCD) of doping zirconium into the hafnium oxide high-k layer in the nanoscale high-k/metal gate n-channel metal-oxide-semiconductor field-effect-transistors. Previous n-metal-oxide semiconductor-field effect transistor studies demonstrated that zirconium-doped hafnium oxide reduces charge trapping and improves positive bias temperature instability. In this work, a clear reduction in HCD is observed with zirconium-doped hafnium oxide because channel hot electron (CHE) trapping in pre-existing high-k bulk defects is the main degradation mechanism. However, this reduced HCD became ineffective at ultra-low temperature, since CHE traps in the deeper bulk defects at ultra-low temperature, while zirconium-doping only passivates shallow bulk defects.

  16. Genotoxic and cytotoxic damage by the therapeutic radiopharmaceutical [{sup 166}Dy]Dy/{sup 166}Ho-EDTMP as in vivo generator system; Dano genotoxico y citotoxico por el radiofarmaco terpeutico [{sup 166}Dy]Dy/{sup 166}Ho-EDTMP como sistema de generador in vivo

    Energy Technology Data Exchange (ETDEWEB)

    Pedraza L, M; Piedras R, J [Instituto Nacional de Ciencias Medicas y Nutricion, Salvador Zubiran. Vasco. de Quiroga 15, 14000 Mexico D.F. (Mexico); Ferro F, G; Morales R, P [ININ, Km. 36.5 Carretera Mexico-Toluca, Ocoyoacac, 52045 Estado de Mexico (Mexico); Murphy S, E [Hospital Santaelena, Mexico D.F. (Mexico); Hernandez O, O [Escuela Superior de Fisica y Matematicas, IPN, Mexico D.F. (Mexico)

    2005-07-01

    In patients with leukemias and multiple myeloma, the cure can be obtained to inclination of a bone marrow transplant (m.o.), for that which one is used a combination of external radiotherapy and chemotherapy with the consequent toxicity to healthy organs. The complex [{sup 166}Dy]Dy/{sup 166}Ho-ethylenediaminetetramethylenephosphonate ([{sup 166}Dy]Dy/{sup 166}Ho-EDTMP) it forms a generator system in vivo stable with bony selective likeness in mice therefore, this it could work as a therapeutic radiopharmaceutical for bone marrow ablation. The objective of this original work was to determine the genotoxic and cytotoxic damage produced by the [{sup 166}Dy]Dy/{sup 166}Ho-EDTMP like a generator system in vivo by means of the reticulocytes reduction (RET) and micronucleus elevation in reticulocytes (RET-MN) in peripheral blood and to evaluate its myeloablative potential for histopathologic studies. It was irradiated {sup 166}Dy{sub 2}O{sub 3} enriched and it was add in form {sup 166}DyCI{sub 3} to the EDTMP in a softening media of phosphates (pH 8), the optimal molar relationship {sup 166}Dy: EDTMP was 1.7:1 and the radiochemical purity was evaluated by ITLC. The Dy:EDTMP complexes, non radioactive, its were prepared in the same way with non irradiated dysprosium oxide. A group of BALB/c mice was injected intraperitoneally with the radiopharmaceutical and two groups of control mice were injected with the non radioactive complex and with sodium chloride 0.9% respectively. Before injecting each one of the solutions it was take a basal sample of peripheral blood of the mouse tail and each 48 h post-injection during 12 d. The animals were sacrificed to obtain the organs of interest and to determine the radioactivity in each one. The femur was used for the histopathologic studies. The quantification of the frequency of RET and RET-MN was carried out by flow cytometry of the sanguine samples and the Monte Carlo code MCNP4B for the dosimetry calculations was used. The

  17. Preparation and Quality Control of 166Ho Labelled Polylactic Acid Microspheres for radiotherapy

    Czech Academy of Sciences Publication Activity Database

    Kropáček, Martin; Melichar, František; Klejzarová, Michaela; Ventruba, Jiří; Tomeš, Marek; Mirzajevová, Marcela

    2007-01-01

    Roč. 2, č. 332 (2007), s. 34-34 ISSN 1619-7070 R&D Projects: GA AV ČR 1QS100480501 Institutional research plan: CEZ:AV0Z10480505 Keywords : polylactic acid microspheres * 166Ho * liver tumour therapy Subject RIV: FR - Pharmacology ; Medidal Chemistry

  18. Radiosynoviorthesis of Knees by Means of 166Ho-Holmium-Boro-Macroaggregates

    Czech Academy of Sciences Publication Activity Database

    Kraft, O.; Kašpárek, R.; Ullmann, V.; Melichar, František; Kropáček, Martin; Mirzajevová, Marcela

    2007-01-01

    Roč. 22, č. 2 (2007), s. 296-302 ISSN 1084-9785 R&D Projects: GA AV ČR 1QS100480501 Institutional research plan: CEZ:AV0Z10480505 Keywords : radiosynoviorthesis * radionuclide synovectomy * 166Ho Subject RIV: FR - Pharmacology ; Medidal Chemistry Impact factor: 1.725, year: 2007

  19. 25 CFR 166.903 - How can I get an agriculture scholarship?

    Science.gov (United States)

    2010-04-01

    ... scholarships must reapply annually to continue to receive funding beyond the initial award period. Students who... degree-granting program at an accredited college or university. (g) Graduate scholarships are available... 25 Indians 1 2010-04-01 2010-04-01 false How can I get an agriculture scholarship? 166.903 Section...

  20. 38 CFR 17.166 - Dental services for hospital or nursing home patients and domiciled members.

    Science.gov (United States)

    2010-07-01

    ... 38 Pensions, Bonuses, and Veterans' Relief 1 2010-07-01 2010-07-01 false Dental services for... Veterans' Relief DEPARTMENT OF VETERANS AFFAIRS MEDICAL Dental Services § 17.166 Dental services for... domiciliary care pursuant to the provisions of §§ 17.46 and 17.47, will be furnished such dental services as...

  1. Isomer-delayed gamma-ray spectroscopy of neutron-rich 166Tb

    Directory of Open Access Journals (Sweden)

    Gurgi L.A.

    2017-01-01

    Full Text Available This short paper presents the identification of a metastable, isomeric-state decay in the neutron-rich odd-odd, prolate-deformed nucleus 166Tb. The nucleus of interest was formed using the in-flight fission of a 345 MeV per nucleon 238U primary beam at the RIBF facility, RIKEN, Japan. Gamma-ray transitions decaying from the observed isomeric states in 166Tb were identified using the EURICA gamma-ray spectrometer, positioned at the final focus of the BigRIPS fragments separator. The current work identifies a single discrete gamma-ray transition of energy 119 keV which de-excites an isomeric state in 166Tb with a measured half-life of 3.5(4 μs. The multipolarity assignment for this transition is an electric dipole and is made on the basis internal conversion and decay lifetime arguments. Possible two quasi-particle Nilsson configurations for the initial and final states which are linked by this transition in 166Tb are made on the basis of comparison with Blocked BCS Nilsson calculations, with the predicted ground state configuration for this nucleus arising from the coupling of the v(1-/2[521] and π(3+/2 Nilsson orbitals.

  2. Preparation and Quality Control of 166-Ho--Macroaggregates for Radiosynoviorthesis

    Czech Academy of Sciences Publication Activity Database

    Kropáček, Martin; Melichar, František; Šrank, Jiří; Mirzajevová, Marcela; Klejzarová, Michaela; Kraft, O.; Kašpárek, R.; Záhlava, J.; Chodacki, A.

    2007-01-01

    Roč. 22, Č. 3 (2007), s. 450-452 ISSN 1084-9785 R&D Projects: GA AV ČR 1QS100480501 Institutional research plan: CEZ:AV0Z10480505 Keywords : radiosynoviorthesis * Holmium-166 * radionuclide synovectomy Subject RIV: FR - Pharmacology ; Medidal Chemistry Impact factor: 1.725, year: 2007

  3. 49 CFR 176.166 - Transport of Class 1 (explosive) materials on passenger vessels.

    Science.gov (United States)

    2010-10-01

    ... 49 Transportation 2 2010-10-01 2010-10-01 false Transport of Class 1 (explosive) materials on....166 Transport of Class 1 (explosive) materials on passenger vessels. (a) Only the following Class 1 (explosive) materials may be transported as cargo on passenger vessels: (1) Division 1.4 (explosive...

  4. 75 FR 13329 - Implications of Financial Accounting System (FAS) 166 on SBA Guaranteed Loan Programs

    Science.gov (United States)

    2010-03-19

    ... SMALL BUSINESS ADMINISTRATION [Docket No. SBA-2010-0005] Implications of Financial Accounting... from the public on: (1) The effect that the accounting changes mandated by the Financial Accounting Standards Board (FASB) in Financial Accounting Standard (FAS) 166 have on SBA Lender and investor...

  5. 25 CFR 166.311 - Is an Indian agricultural resource management plan required?

    Science.gov (United States)

    2010-04-01

    ... holistic management objectives; and (5) Identify actions to be taken to reach established objectives. (c... 25 Indians 1 2010-04-01 2010-04-01 false Is an Indian agricultural resource management plan... WATER GRAZING PERMITS Land and Operations Management Management Plans and Environmental Compliance § 166...

  6. George de Hevesy (1885-1966). Discoverer of hafnium, founder of radioanalytical chemistry and X-ray fluorescence analysis and father of nuclear medicine

    International Nuclear Information System (INIS)

    Niese, Siegfried

    2017-01-01

    George de Hevesy known as discoverer of hafnium, founder of radioanalytical chemistry and X-ray fluorescence analysis and father of nuclear medicine has done important research work in inorganic, physical and radioanalytical and physiological chemistry as well as in geochemistry, radiation biology and medicine. When he must flee for political reasons from a country he must change his colleagues, his equipments, and the topic of his work. It is extremely surprising that he could receive important results under such circumstances even at an advanced age. (author)

  7. A spanish mineral of zirconium and hafnium. Separation of the two elements by liquid-liquid extraction, using tributyl phosphate as chelating agent

    International Nuclear Information System (INIS)

    Ruiz Sanchez, F.; Cruz Castillo, F. de la; Fernandez Cellini, R.

    1962-01-01

    The zirconium and Hafnium oxides are obtained from a Spanish mineral of zircon with an average contest of 55% in ZrO 2 -HfO 2 . An alkaline fusion to open the mineral, followed by a purification by crystallization as (Zr O-Hf O)Cl 2 H 2 O or as (Zr-Hf) (SO 4 ) 2 . 4H 2 O, is used. A discussion of the best experimental conditions for opening the mineral and of the purification method is made. (Author) 45 refs

  8. Clinical effects of transcatheter hepatic arterial embolization with holmium-166 poly(l-lactic acid) microspheres in healthy pigs

    Energy Technology Data Exchange (ETDEWEB)

    Vente, M.A.D.; Nijsen, J.F.W.; Wit, T.C. de; Schip, A.D. van het [University Medical Center Utrecht, Department of Nuclear Medicine, P.O. Box 85500, Utrecht (Netherlands); Seppenwoolde, J.H.; Seevinck, P.R. [University Medical Center Utrecht, Image Sciences Institute, Utrecht (Netherlands); Krijger, G.C. [Delft University of Technology, Department of Radiation, Radionuclides and Reactors, Faculty of Applied Sciences, Delft (Netherlands); Huisman, A. [University Medical Center Utrecht, Department of Clinical Chemistry and Haematology, Utrecht (Netherlands); Zonnenberg, B.A. [University Medical Center Utrecht, Department of Internal Medicine, Utrecht (Netherlands); Ingh, T.S.G.A.M. van den [TCCI Consultancy B.V., P.O. Box 85032, Utrecht (Netherlands)

    2008-07-15

    The aim of this study is to evaluate the toxicity of holmium-166 poly(l-lactic acid) microspheres administered into the hepatic artery in pigs. Healthy pigs (20-30 kg) were injected into the hepatic artery with holmium-165-loaded microspheres ({sup 165}HoMS; n = 5) or with holmium-166-loaded microspheres ({sup 166}HoMS; n = 13). The microspheres' biodistribution was assessed by single-photon emission computed tomography and/or MRI. The animals were monitored clinically, biochemically, and ({sup 166}HoMS group only) hematologically over a period of 1 month ({sup 165}HoMS group) or over 1 or 2 months ({sup 166}HoMS group). Finally, a pathological examination was undertaken. After microsphere administration, some animals exhibited a slightly diminished level of consciousness and a dip in appetite, both of which were transient. Four lethal adverse events occurred in the {sup 166}HoMS group due either to incorrect administration or comorbidity: inadvertent delivery of microspheres into the gastric wall (n = 2), preexisting gastric ulceration (n = 1), and endocarditis (n = 1). AST levels were transitorily elevated post-{sup 166}HoMS administration. In the other blood parameters, no abnormalities were observed. Nuclear scans were acquired from all animals from the {sup 166}HoMS group, and MRI scans were performed if available. In pigs from the {sup 166}HoMS group, atrophy of one or more liver lobes was frequently observed. The actual radioactivity distribution was assessed through ex vivo {sup 166m}Ho measurements. It can be concluded that the toxicity profile of HoMS is low. In pigs, hepatic arterial embolization with {sup 166}HoMS in amounts corresponding with liver-absorbed doses of over 100 Gy, if correctly administered, is not associated with clinically relevant side effects. This result offers a good perspective for upcoming patient trials. (orig.)

  9. Clinical study of liver cancer (Hepatocellular carcinoma) by 166 Ho-CHICO

    Energy Technology Data Exchange (ETDEWEB)

    Lee, J. T.; Yoo, H. S.; Lee, J. D.; Lee, D. Y.; Kim, E. K.; Yoo, N. C.; Shin, S. J.; Han, K. H. [Yonsei University, Seoul (Korea); Park, K. B. [Korea Atomic Energy Research Institute, Taejeon (Korea)

    2000-04-01

    As having used Ho-166 Chitosan complex, this study was designed for the development of new therapeutic agent in the treatment of liver cancer (hepatocellular carcinoma). During the period of 3 years from April 1, 1997 to March 31, 2000, this project was successfully performed on the base of clinical experience with percutaneous Ho-166 CHICO injection in the treatment of liver cancer'. In order to evaluate the biodistribution and effect of Ho-166 CHICO was performed in 50 patients, who had the progressed liver cancer with range of 3-10cm in diameter. After the administration of the complex materials, we evaluated the therapeutic effect as well as complication by the follow-up study that included laboratory examination, radioactivity counting and various imaging modalities. 1) In animal experiment, radioactivity of target liver was ranged between 27-33% of total body one, urine excretion between 0.17-0.24 %. White blood cell and platelet counts start diminishing within 7 days and at maximum within 4 weeks after administration of complex materials. In tissue changes of target liver was revealed no significant change in the tumor dose of Ho-166, but periportal fibrosis and massive tissue necrosis in the high ones. 2) In clinical study, total necrosis of tumor is 66%, partial 10% and non-response 24% among 50 patients' liver cancer. The most important complication were leukopenia and thrombocytopenia (82%), the remained was abdominal pain(34%), skin reaction(12%), bile duct obstruction(10%), liver abscess(6%) etc. Conclusively intraarterial injection of Ho-166 CHICO was effective in the treatment of larger and progressed liver cancer. 19 refs., 14 figs., 8 tabs. (Author)

  10. Effects of Intraluminal Irradiation with Holmium-166 for TIPS Stenosis: Experimental Study in a Swine Model

    Energy Technology Data Exchange (ETDEWEB)

    Park, Ji Seon; Oh, Joo Hyeong; Kim, Deog Yoon; Park, Yong Koo; Kim, Soo Joong [Kyung Hee University Medical Center, Seoul (Korea, Republic of); Park, Sang Joon [Kang Dong Sacred Heart Hospital, Hallym University, Seoul (Korea, Republic of)

    2007-04-15

    We wanted to evaluate the effectiveness of intraluminal irradiation with Holmium-166 ({sup 166}Ho) for reducing the pseudointimal hyperplasia (PIH) in the transjugular intrahepatic portosystemic shunt (TIPS) tract in a swine model. TIPS was performed in 12 domestic pigs, after the creation of portal hypertension by intraportal injection of a mixture of N-butyl-2- cyanoacrylate (NBCA) and lipiodol. Five pigs first underwent intraluminal irradiation (30 Gy) in the parenchymal tract with using a {sup 166}Ho solution-filled balloon catheter, and this was followed by the placement of a nitinol stent in the TIPS tract. For the seven control pigs, the balloon was filled with saline and contrast media mixture. Two weeks later, follow-up portography and histological analysis were performed. TIPS was successfully performed in all twelve pigs with achieving artificially induced portal hypertension. Portography performed two weeks after TIPS showed the patent tracts in the TIPS tracts that were irradiated with {sup 166}Ho (5/5, 100%), whereas either completely (5/6, 83.3%) or partially (1/6, 16.7%) occluded TIPS were seen in the seven pigs of the nonirradiated control group, except in one pig that experienced periprocedural death due to bleeding. Histological analysis showed a statistically significant difference for the maximal PIH (irradiated: 32.8%, nonirradiated: 76.0%, p < 0.001) between the two groups. Intraluminal irradiation with 30 Gy of {sup 166}Ho for TIPS significantly improved the TIPS patency in a swine model of portal hypertension during a 2- week period of follow-up.

  11. Production, Quality Control and Biological Evaluation of 166Ho-PDTMP as a Possible Bone Palliation Agent

    Directory of Open Access Journals (Sweden)

    Samaneh Zolghadri

    2013-05-01

    Full Text Available Objective(s:In this study, 166Ho-1,2-propylene di-amino tetra(methy1enephosphonicAcid (166Ho-PDTMP complex  was prepared as a bone palliation agent. Materials and Methods:The complex was successfully prepared using an in-house synthesized EDTMP ligand and 166HoCl3. Ho-166 chloride was obtained by thermal neutron irradiation (1 × 1013 n.cm-2.s-1 of natural Ho(NO33 samples  followed by radiolabeling and stability studies. Biodistribution in wild type rats was also peformed. Results: The complex was prepared with thespecific activity of 278 GBq/mg and high radiochemical purity (>99%, checked by ITLC. 166Ho-PDTMP complex was stabilized in the final preparation and in the presence of human serum (>90% up to 72 hr. The biodistribution of 166Ho-PDTMP in wild-type rats demonstrated significant bone uptake was up to 48 hr compared to 166HoCl3. Conclusion: The produced 166Ho-PDTMP properties suggest a possible new bone palliative therapeutic to overcome the metastatic bone pains.  

  12. Safety analysis of holmium-166 microsphere scout dose imaging during radioembolisation work-up. A cohort study

    Energy Technology Data Exchange (ETDEWEB)

    Braat, Arthur J.A.T.; Prince, Jip F.; Rooij, Rob van; Bruijnen, Rutger C.G.; Bosch, Maurice A.A.J. van den; Lam, Marnix G.E.H. [University Medical Center Utrecht, Department of Radiology and Nuclear Medicine, Utrecht (Netherlands)

    2018-03-15

    Radioembolisation is generally preceded by a scout dose of technetium-99m-macroaggregated albumin to estimate extrahepatic shunting of activity. Holmium-166 microspheres can be used as a scout dose (±250 MBq) and as a therapeutic dose. The general toxicity of a holmium-166 scout dose ({sup 166}Ho-SD) and safety concerns of an accidental extrahepatic deposition of {sup 166}Ho-SD were investigated. All patients who received a {sup 166}Ho-SD in our institute were reviewed for general toxicity and extrahepatic depositions. The absorbed dose in extrahepatic tissue was calculated on SPECT/CT and correlated to clinical toxicities. In total, 82 patients were included. No relevant clinical toxicity occurred. Six patients had an extrahepatic deposition of {sup 166}Ho-SD (median administered activity 270 MBq). The extrahepatic depositions (median activity 3.7 MBq) were located in the duodenum (3x), gastric fundus, falciform ligament and the lesser curvature of the stomach, and were deposited in a median volume of 15.3 ml, which resulted in an estimated median absorbed dose of 3.6 Gy (range 0.3-13.8 Gy). No adverse events related to the extrahepatic deposition of the {sup 166}Ho-SD occurred after a median follow-up of 4 months (range 1-12 months). These results support the safety of 250 MBq {sup 166}Ho-SD in a clinical setting. (orig.)

  13. 25 CFR 166.100 - What special tribal policies will we apply to permitting on Indian agricultural lands?

    Science.gov (United States)

    2010-04-01

    ... preferences in permits advertised for bid under § 166.221 of this part, by allowing prospective Indian operators to match the highest responsible bid (unless the tribal law or leasing policy specifies some other... THE INTERIOR LAND AND WATER GRAZING PERMITS Tribal Policies and Laws Pertaining to Permits § 166.100...

  14. 78 FR 24235 - 166th Meeting of the Advisory Council on Employee Welfare and Pension Benefit Plans; Notice of...

    Science.gov (United States)

    2013-04-24

    ... DEPARTMENT OF LABOR Employee Benefits Security Administration 166th Meeting of the Advisory Council on Employee Welfare and Pension Benefit Plans; Notice of Meeting Pursuant to the authority... 166th open meeting of the Advisory Council on Employee Welfare and Pension Benefit Plans (also known as...

  15. Evidence for the involvement of Ala 166 in coupling Na(+) to sugar transport through the human Na(+)/glucose cotransporter

    DEFF Research Database (Denmark)

    Meinild, A K; Loo, D D; Hirayama, B A

    2001-01-01

    . The affinity for Na(+) was unchanged compared to that of hSGLT1, whereas the sugar affinity was reduced and sugar specificity was altered. There was a reduction in the turnover rate of the transporter, and in contrast to that of hSGLT1, the turnover rate depended on the sugar molecule. Exposure of A166C......We mutated residue 166, located in the putative Na(+) transport pathway between transmembrane segments 4 and 5 of human Na(+)/glucose cotransporter (hSGLT1), from alanine to cysteine (A166C). A166C was expressed in Xenopus laevis oocytes, and electrophysiological methods were used to assay function...... to MTSEA and MTSET, but not MTSES, abolished sugar transport. Accessibility of A166C to alkylating reagents was independent of protein conformation, indicating that the residue is always accessible from the extracellular surface. Sugar and phlorizin did not protect the residue from being alkylated...

  16. Dosimetric intercomparison of permanent Ho-166 seed's implants and HDR Ir-192 brachytherapy in breast cancer.

    Science.gov (United States)

    de Campos, Tarcisio Passos Ribeiro; Nogueira, Luciana Batista; Trindade, Bruno; Cuperschmid, Ethel Mizrahy

    2016-01-01

    To provide a comparative dosimetric analysis of permanent implants of Ho(166)-seeds and temporary HDR Ir(192)-brachytherapy through computational simulation. Brachytherapy with Ir(192)-HDR or LDR based on temporary wires or permanent radioactive seed implants can be used as dose reinforcement for breast radiation therapy. Permanent breast implants have not been a practical clinical routine; although, I(125) and Pd(103)-seeds have already been reported. Biodegradable Ho(166)-ceramic-seeds have been addressed recently. Simulations of implants of nine Ho(166)-seeds and equivalent with HDR Ir(192)-brachytherapy were elaborated in MCNP5, shaped in a computational multivoxel simulator which reproduced a female thorax phantom. Spatial dose rate distributions and dose-volume histograms were generated. Protocol's analysis involving exposure time, seed's activities and dose were performed. Permanent Ho(166)-seed implants presented a maximum dose rate per unit of contained activity (MDR) of 1.1601 μGy h(-1) Bq(-1); and, a normalized MDR in standard points (8 mm, equidistant to 03-seeds - SP1, 10 mm - SP2) of 1.0% (SP1) and 0.5% (SP2), respectively. Ir(192)-brachytherapy presented MDR of 4.3945 × 10(-3) μGy h(-1) Bq(-1); and, 30% (SP1), and 20% (SP2). Therefore, seed's implant activities of 333 MBq (Ho(166)) and 259 GBq (Ir(192)) produced prescribed doses of 58 Gy (SP1; 5d) and 56 Gy (SP1, 5 fractions, 6 min), respectively. Breast Ho(166)-implants of 37-111 MBq are attractive due to the high dose rate near 6-10 mm from seeds, equivalent to Ir(192)-brachytherapy of 259 GBq (3 fractions, 6 min) providing similar dose in standard points at a week; however, with spatial dose distribution better confined. The seed positioning can be adjusted for controlling the breast tumor, in stages I and II, in flat and deep tumors, without any breast volumetric limitation.

  17. Chilean experience in production of therapeutic radiopharmaceuticals labelled with 153Sm and 166Ho

    International Nuclear Information System (INIS)

    Chandia, M.; Gil, M.G.; Tomicic, M.; Araya, G.; Olea, E.; Chong, G.

    1998-01-01

    153 Samarium ( 153 Sm) and 166 Holmium ( 166 Ho) were produced at the Nuclear Center of La Reina Research Reactor, Chilean Nuclear Energy Commission. 153 Sm-EDTMP (Ethylenediaminetetramethylene Phosphonate) used for clinical trial of therapy for painful skeletal metastases and labeled particles such as 166 Ho-FHMA (ferric hydroxide macroagregattes) and 153 Sm-HAP (hydroxiapatite particles) used for radiation synevectomy, were labeled. Radionuclide purity of both radionuclides was analyzed by gamma spectrometry using a multichannel gamma spectrometer. Radiochemical labeled reaction parameters of 153 Sm-EDTMP such as: Sm/EDTMP molar ratio, 153 Sm specific activity, labeled pH and temperature, were determined in order to get high radiolabeling yields. Radiochemical Quality Controls of 153 Sm-EDTMP using different chromatographic systems were carried out in order to determine labeling yields. Bodistribution studies were achieved in mice by dissection of animals and by autoradiography of histological slices in rats, after 2h post injection. 153 Sm-HAP and 166 Ho-FHMA labeled particles were prepared using the methods described. Radiochemical purity, in case of radiolabeled particles was carried out by centrifugation, measuring activity in the supernatant and in particles pellet. Physical parameters, such as particle size and range of the radiopharmaceuticals based on particles labeling were evaluated in order to determine the ideal conditions to obtain particles size range between 10 - 40μ. In vitro labeling stability for over seven days and wash out activity by incubation in human synovial fluid after 6 and 24h post labeling, was also studied. 153 Sm-EDTMP was easily labeled with a Radiochemical purity over 99.5% and stable for over 7 days. Biodistribution studies in mice give more than 50% of ID uptake in bone and less than 0,1% in liver this was correlated by autoradiographic image. 153 Sm-HAP and 166 Ho-FHMA were also labeling obtaining radiochemical purity over 95

  18. A fast response hafnium selective polymeric membrane electrode based on N,N'-bis(α-methyl-salicylidene)-dipropylenetriamine as a neutral carrier

    International Nuclear Information System (INIS)

    Rezaei, B.; Meghdadi, S.; Zarandi, R. Fazel

    2008-01-01

    In this study a new hafnium selective sensor was fabricated from polyvinylchloride (PVC) matrix membrane containing neutral carrier N,N'-bis(α-methyl-salicylidene)-dipropylenetriamine (Mesaldpt) as a new ionophore, sodium tetraphenyl borate (NaTPB) as anionic discriminator and dioctyl phthalate (DOP) as plasticizing solvent mediator in tetrahydrofuran solvent. The electrode exhibits Nernstian response for Hf 4+ (Hafnium(IV)) over a wide concentration range (2.0 x 10 -7 to 1.0 x 10 -1 M) with the determination coefficient of 0.9966 and slope of 15.1 ± 0.1 mV decades -1 . The limit of detection is 1.9 x 10 -7 M. The electrode has a fast response time of 18 s and a working pH range of 4-8. The proposed membrane shows excellent discriminating ability towards Hf 4+ ion with regard to several alkali, alkaline earth transition and heavy metal ions. It can be used over a period of 1.5 months with good reproducibility. It is successfully applied for direct determination of Hf 4+ in solutions by standard addition method for real sample analysis

  19. A fast response hafnium selective polymeric membrane electrode based on N,N'-bis({alpha}-methyl-salicylidene)-dipropylenetriamine as a neutral carrier

    Energy Technology Data Exchange (ETDEWEB)

    Rezaei, B. [Department of Chemistry, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of)], E-mail: rezaei@cc.iut.ac.ir; Meghdadi, S.; Zarandi, R. Fazel [Department of Chemistry, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of)

    2008-08-30

    In this study a new hafnium selective sensor was fabricated from polyvinylchloride (PVC) matrix membrane containing neutral carrier N,N'-bis({alpha}-methyl-salicylidene)-dipropylenetriamine (Mesaldpt) as a new ionophore, sodium tetraphenyl borate (NaTPB) as anionic discriminator and dioctyl phthalate (DOP) as plasticizing solvent mediator in tetrahydrofuran solvent. The electrode exhibits Nernstian response for Hf{sup 4+} (Hafnium(IV)) over a wide concentration range (2.0 x 10{sup -7} to 1.0 x 10{sup -1} M) with the determination coefficient of 0.9966 and slope of 15.1 {+-} 0.1 mV decades{sup -1}. The limit of detection is 1.9 x 10{sup -7} M. The electrode has a fast response time of 18 s and a working pH range of 4-8. The proposed membrane shows excellent discriminating ability towards Hf{sup 4+} ion with regard to several alkali, alkaline earth transition and heavy metal ions. It can be used over a period of 1.5 months with good reproducibility. It is successfully applied for direct determination of Hf{sup 4+} in solutions by standard addition method for real sample analysis.

  20. Our first clinical experience with radiosynoviorthesis by means of 166Ho-holmium-boro-macroaggregates

    International Nuclear Information System (INIS)

    Kraft, O.; Ullmann, V.; Kasparek, R.; Melichar, F.; Kropacek, M.; Mirzajevova, M.

    2005-01-01

    In this paper, we evaluate the therapeutic and adverse effects of the application of 166- holmium-boro-macroaggregates (HMBA) in radiosynovectomy (RSO) of the knees. We assessed the efficacy and safety of 166H o-HBMA in a prospective clinical trial in patients suffering from chronic synovitis. An effective component of radiopharmaceutical 166H o-boro-macroaggregates is radionuclide 166H o which has both b-emission and g-emission. The physical half-life time of 166H o is 26.8 hours. After application of the radiopharmaceutical into a joint cavity, the effect of b-emission causes radiation necrosis of pathologically changed (inflamed) synovial membrane. From 15 april 2005, we have started RSO of knees by means of new radiopharmaceutical 166H o-boro-macroaggregates in patients with gonarthrosis, rheumatoid arthritis, chronic synovitis, psoriatic arthritis, gout arthropathy. Seventeen intra-articular injections were performed in fifteen patients receiving a mean activity of 972 MBq (range: 904.1057 MBq) 166H o-HMBA. The patients were hospitalized for three days. Side effects were evaluated during hospital stay and after 6.8 weeks. Static scintigraphy of knee joints and measurements of blood radioactivity were performed. Therapeutic effects were evaluated after 6.8 weeks. In 2 hours and 2 days after application, we proved, by means of knee and inguinal scintigraphy, only insignificant radiopharmaceutical leakage from the joint cavity to the inguinal lymph nodes in four patients. In treated patients, no serious adverse effects occurred. Nine patients were without complaints; 4 patients had slight knee exudation and 2 patients had great exudation. Therapeutic effects after 6.8 weeks were as follows: 2 patients were without pain, 9 with lower pain, 3 with the same pain and 1 patient with increased pain. Joint motion was improved in 7 patients, remained the same in 7 patients and was impaired in 1 patient. Analgesics consumption was lower in 5 patients, the same in 9

  1. Calcium phosphate holmium-166 ceramic to addition in bone cement: synthesis and characterization

    Energy Technology Data Exchange (ETDEWEB)

    Donanzam, Blanda A.; Campos, Tarcisio P.R., E-mail: campos@nuclear.ufmg.b [Universidade do Federal de Minas Gerais (DEN/UFMG), Belo Horizonte, MG (Brazil). Escola de Engenharia. Dept. de Engenharia Nuclear; Dalmazio, Ilza; Valente, Eduardo S., E-mail: id@cdtn.b, E-mail: valente@cdtn.b [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2011-07-01

    Spine metastases are a common and painful complication of cancer. The treatment often consists of bone cement injection (vertebroplasty or kyphoplasty) within vertebral body for vertebrae stabilization, followed by external beam radiation therapy. Recently, researchers introduced the concept of radioactive bone cement for spine tumors therapy. Then, investigations about bioactive and radioactive materials became interesting. In this study, we present the synthesis of calcium phosphate incorporated holmium (CaP-Ho) via sol-gel technique, and its characterization by XRD, FT-IR, NA and SEM. Results showed a multiphasic bioceramic composed mainly of hydroxyapatite, {beta}-tricalcium phosphate, holmium phosphate and traces of calcium pyrophosphate. Furthermore, the nuclide Ho-166 was the major radioisotope produced. Despite that, the radioactive bioceramic CaP-{sup 166}Ho must be investigated in clinical trials to assure its efficacy and safety on spine tumors treatment (author)

  2. Calcium phosphate holmium-166 ceramic to addition in bone cement: synthesis and characterization

    International Nuclear Information System (INIS)

    Donanzam, Blanda A.; Campos, Tarcisio P.R.

    2011-01-01

    Spine metastases are a common and painful complication of cancer. The treatment often consists of bone cement injection (vertebroplasty or kyphoplasty) within vertebral body for vertebrae stabilization, followed by external beam radiation therapy. Recently, researchers introduced the concept of radioactive bone cement for spine tumors therapy. Then, investigations about bioactive and radioactive materials became interesting. In this study, we present the synthesis of calcium phosphate incorporated holmium (CaP-Ho) via sol-gel technique, and its characterization by XRD, FT-IR, NA and SEM. Results showed a multiphasic bioceramic composed mainly of hydroxyapatite, β-tricalcium phosphate, holmium phosphate and traces of calcium pyrophosphate. Furthermore, the nuclide Ho-166 was the major radioisotope produced. Despite that, the radioactive bioceramic CaP- 166 Ho must be investigated in clinical trials to assure its efficacy and safety on spine tumors treatment (author)

  3. Study of intraarticular application of 166-Holmium IHPP in healthy hares

    International Nuclear Information System (INIS)

    Szentesi, M.; Koernyei, J.; Antalffi, M.; Toerkoe, J.; Toth, G.Y.; Janoki, G.Y.; Balogh, L.

    2002-01-01

    Radiosynoviorthesis non invasive therapy in rheumatoid arthritis is an alternative of surgical synovectomy. This method was applied first by Fellinger in 1952, and since then it has been practiced all over the world. The leakage of traditionally applied isotopes is cca. 4-10%, and the whole body dose is 10 rads. The objective of our work is to produce a nuclear medication with a minimum radioactive load, of short half-life and ideal molecule size for the treatment of radiosynoviorthesis / 166- Holmium IHPP / and the study of its effect on healthy hares. The first results have been already reported on previously. 166-Holmium IHPP has the features of: half-life of 26.9 hr, the maximum soft-tissue penetration of a beta particle 1.84 MeV, emitted from 166-Ho 8.4 mm. With an average of 3.3 mm. Methods applied: Biodistribution analysis, gamma camera analysis, biochemical and histological tests with photo- and electro microscope were carried out on healthy New Zealand hares 6, 24, 72, 168 hours after radiosynoviorthesis. Results: All the testing methods applied showed that 97 /96,1-98,2/ % remained on the spot of the injection and the 2/3 of the small percentage released leakage: is excreted by the liver and the other 1/3 of it with the urine.The hematological and biochemical parameters did not show differences. During histological examination moderate level acute radioarthritis in the knee joint treated was observed (6-24 hours after the injection), then moderate level subacute radioarthritis with slight degeneration in the synovial membrane and in the synovial fluid. It was only the electro microscopic examination that did show a minimal degeneration in the cartilage and in the menisci, but it got regenerated in 168 hours. Conclusion: The examination carried out has proved that 166-Ho -IHPP can be effectively applied in radiosynoviorthesis. Clinical testing has started

  4. Preparation and Quality Control of 166Ho-Boro-Macroaggregates for Radiosynoviorthesis

    Czech Academy of Sciences Publication Activity Database

    Kropáček, Martin; Melichar, František; Šrank, Jiří; Mirzajevová, Marcela; Klejzarová, Michaela; Kraft, O.; Kašpárek, R.; Záhlava, J.; Chodacki, A.

    2006-01-01

    Roč. 33, Suppl. 2 (2006), S327-S328 ISSN 1619-7070. [Annual Congress of the European Association of Nuclear Medicine. 01.10.2006-03.10.2006, Athens] R&D Projects: GA AV ČR(CZ) IQS10480501 Institutional research plan: CEZ:AV0Z10480505 Keywords : 166Ho- Boro -Macroaggregate * Radiosynoviorthesis Subject RIV: CH - Nuclear ; Quantum Chemistry

  5. Beta dosimetry in intraperitoneal administration of 166Ho-chitosan complex

    International Nuclear Information System (INIS)

    Kim, E. H.; Lim, S. M.; Park, K. B.

    1998-01-01

    Intraperitoneal administration of radioisotopes is suggested to treat the metastatic ovarian cancer in the peritoneal cavity. Administering beta-emitting radioisotopes into the peritoneal cavity allows the maximum energy delivery to the cancerous cells of the peritoneal wall surface while sparing the normal cells located in deep site of the peritoneal wall. In this study, dose estimates of the peritoneal wall are provided to be used for prescribing the amount of 166 Ho-chitosan complex administered. The 166 Ho-chitosan complex diffused in the peritoneal fluid may attach to the peritoneal wall surface. The attachment fraction of 166 Ho-chitosan complex to the peritoneal wall surface is obtained by simulating the ascites with Fischer rats. Both volume source in the peritoneal fluid and the surface source over the peritoneal wall surface are counted for the contribution to the peritoneal wall dose. The Monte Carlo code EGS4 is used to simulate the energy transfer of the beta particles emitted from 166 Ho. A plane geometrical model of semi-infinite volume describes the peritoneal cavity and the peritoneal wall. A semi-infinite plane of 10 μm in thickness at every 1 mm of depth in the peritoneal wall is taken as the target in dose estimation. Greater than 98 percents of attachment fraction has been observed from the experiments with Fischer rats. Given 1.3 μCi/cm 2 and 2.4 μCi/ml of uniform activity density, absorbed dose is 123 Gy, 8.59 Gy, 3.00 Gy, 1.03 Gy, and 327 Gy at 0 mm, 1 mm, 2 mm, 3 mm, and 4 mm in depth to the peritoneal wall, respectively

  6. Metallorganic chemical vapor deposition and atomic layer deposition approaches for the growth of hafnium-based thin films from dialkylamide precursors for advanced CMOS gate stack applications

    Science.gov (United States)

    Consiglio, Steven P.

    To continue the rapid progress of the semiconductor industry as described by Moore's Law, the feasibility of new material systems for front end of the line (FEOL) process technologies needs to be investigated, since the currently employed polysilicon/SiO2-based transistor system is reaching its fundamental scaling limits. Revolutionary breakthroughs in complementary-metal-oxide-semiconductor (CMOS) technology were recently announced by Intel Corporation and International Business Machines Corporation (IBM), with both organizations revealing significant progress in the implementation of hafnium-based high-k dielectrics along with metal gates. This announcement was heralded by Gordon Moore as "...the biggest change in transistor technology since the introduction of polysilicon gate MOS transistors in the late 1960s." Accordingly, the study described herein focuses on the growth of Hf-based dielectrics and Hf-based metal gates using chemical vapor-based deposition methods, specifically metallorganic chemical vapor deposition (MOCVD) and atomic layer deposition (ALD). A family of Hf source complexes that has received much attention recently due to their desirable properties for implementation in wafer scale manufacturing is the Hf dialkylamide precursors. These precursors are room temperature liquids and possess sufficient volatility and desirable decomposition characteristics for both MOCVD and ALD processing. Another benefit of using these sources is the existence of chemically compatible Si dialkylamide sources as co-precursors for use in Hf silicate growth. The first part of this study investigates properties of MOCVD-deposited HfO2 and HfSixOy using dimethylamido Hf and Si precursor sources using a customized MOCVD reactor. The second part of this study involves a study of wet and dry surface pre-treatments for ALD growth of HfO2 using tetrakis(ethylmethylamido)hafnium in a wafer scale manufacturing environment. The third part of this study is an investigation of

  7. {sup 166} Ho-HA Evaluation as therapeutic agent for rheumatoid arthritis treatment; Evaluacion de {sup 166}Ho-Ha como agente terapeutico en el tratamiento de la artritis reumatoidea

    Energy Technology Data Exchange (ETDEWEB)

    Chandia, M; Errazu, X [Comision Chilena de Energia Nuclear, Santiago (Chile); Mendoza, P [Departamento de Medicina Nuclear, Hospital Militar, Santiago (Chile); Troncoso, F [Comision Chilena de Energia Nuclear, Santiago (Chile); Jofre, J; Sierralta, P [Departamento de Medicina Nuclear, Hospital Militar, Santiago (Chile)

    2003-01-01

    Aim: Rheumatoid arthritis is a limiting disease having, among its pathological features, the inflammation of synovial tissue with progressive and later destruction of the articulation. This lead to joint deformation and loss of its function, generating pain and reducing the mobility of the affected articulation. The aim was to evaluate {sup 166}Ho-Hydroxyapatite ({sup 166} Ho-HA) as potential radiopharmaceutical for the syntomatic treatment of chronic and acute arthritis Materials and Methods: {sup 166}Holmiun was produced by irradiation of Ho{sub 2}O{sub 3} at La Reina Research Reactor, Nuclear Chilean Energy Commission. Hydroxyapatite was in-house synthetized. Its labelling and quality controls follows the internationally accepted procedures. An antigen arthritis was induced to eight New Zealand rabbits with the {sup 166}Ho-HA radiochemical being administred thereafter in two dosage modalities (single and double). The compound therapeutic efficiency was evaluated based upon clinical improvement and images from the inflamated articulation using {sup 67}Ga citrate before and after {sup 166} Ho-HA injection. Results: The radiochemical purity of the innoculated compound was greater than 98% as measured under sterility conditions. Clinically, an inflamation reduction (2 cm), appetite improvement and general well being was observed. The {sup 166} Ho-HA distribution and localization was monitored using gamma camera images taken at 4 and 24 h. There was no evidence of extraarticular leakage. From the {sup 67}Ga citrate imaging, the acute group shows an overall improvement of well being corresponding to a lesser uptake at the inflamated articulation, regarding to the chronic group. The {sup 166}Ho-HA double dosis, compared to the single dosis, suggest a reduced uptake of {sup 67}Ga citrate at the inflamated tissue, meaning an increased therapeutic effect. Conclusions: {sup 166} Ho-HA is usefull as therapeutic agent for the syntomatic treatment of rheumatoideal arthritis

  8. Insurgency in Ancient Times: The Jewish Revolts Against the Seleucid and Roman Empires, 166 BC-73 AD

    National Research Council Canada - National Science Library

    Sorrells, William T

    2005-01-01

    This monograph examines two insurgencies conducted by the Jews in ancient times: the Maccabee Revolt against the Seleucid Empire from 166-164 BC, and the Revolt against the Roman Empire from 66-70 AD...

  9. Isolation and expression analysis of four HD-ZIP III family genes targeted by microRNA166 in peach.

    Science.gov (United States)

    Zhang, C H; Zhang, B B; Ma, R J; Yu, M L; Guo, S L; Guo, L

    2015-10-30

    MicroRNA166 (miR166) is known to have highly conserved targets that encode proteins of the class III homeodomain-leucine zipper (HD-ZIP III) family, in a broad range of plant species. To further understand the relationship between HD-ZIP III genes and miR166, four HD-ZIP III family genes (PpHB14, PpHB15, PpHB8, and PpREV) were isolated from peach (Prunus persica) tissue and characterized. Spatio-temporal expression profiles of the genes were analyzed. Genes of the peach HD-ZIP III family were predicted to encode five conserved domains. Deduced amino acid sequences and tertiary structures of the four peach HD-ZIP III genes were highly conserved, with corresponding genes in Arabidopsis thaliana. The expression level of four targets displayed the opposite trend to that of miR166 throughout fruit development, with the exception of PpHB14 from 35 to 55 days after full bloom (DAFB). This finding indicates that miR166 may negatively regulate its four targets throughout fruit development. As for leaf and phloem, the same trend in expression level was observed between four targets and miR166 from 75 to 105 DAFB. However, the opposite trend was observed for the transcript level between four targets and miR166 from 35 to 55 DAFB. miRNA166 may negatively regulate four targets in some but not all developmental stages for a given tissue. The four genes studied were observed to have, exactly or generally, the same change tendency as individual tissue development, a finding that suggests genes of the HD-ZIP III family in peach may have complementary or cooperative functions in various tissues.

  10. Cell Adhesion Molecule CD166/ALCAM Functions Within the Crypt to Orchestrate Murine Intestinal Stem Cell HomeostasisSummary

    Directory of Open Access Journals (Sweden)

    Nicholas R. Smith

    2017-05-01

    Full Text Available Background & Aims: Intestinal epithelial homeostasis is maintained by active-cycling and slow-cycling stem cells confined within an instructive crypt-based niche. Exquisite regulating of these stem cell populations along the proliferation-to-differentiation axis maintains a homeostatic balance to prevent hyperproliferation and cancer. Although recent studies focus on how secreted ligands from mesenchymal and epithelial populations regulate intestinal stem cells (ISCs, it remains unclear what role cell adhesion plays in shaping the regulatory niche. Previously we have shown that the cell adhesion molecule and cancer stem cell marker, CD166/ALCAM (activated leukocyte cell adhesion molecule, is highly expressed by both active-cycling Lgr5+ ISCs and adjacent Paneth cells within the crypt base, supporting the hypothesis that CD166 functions to mediate ISC maintenance and signal coordination. Methods: Here we tested this hypothesis by analyzing a CD166–/– mouse combined with immunohistochemical, flow cytometry, gene expression, and enteroid culture. Results: We found that animals lacking CD166 expression harbored fewer active-cycling Lgr5+ ISCs. Homeostasis was maintained by expansion of the transit-amplifying compartment and not by slow-cycling Bmi1+ ISC stimulation. Loss of active-cycling ISCs was coupled with deregulated Paneth cell homeostasis, manifested as increased numbers of immature Paneth progenitors due to decreased terminal differentiation, linked to defective Wnt signaling. CD166–/– Paneth cells expressed reduced Wnt3 ligand expression and depleted nuclear β-catenin. Conclusions: These data support a function for CD166 as an important cell adhesion molecule that shapes the signaling microenvironment by mediating ISC–niche cell interactions. Furthermore, loss of CD166 expression results in decreased ISC and Paneth cell homeostasis and an altered Wnt microenvironment. Keywords: Intestinal Stem Cell, Homeostasis

  11. Prognostic value of CD166 expression in cancers of the digestive system: a systematic review and meta-analysis.

    Directory of Open Access Journals (Sweden)

    Chao Ni

    Full Text Available Many studies have reported the prognostic predictive value of CD166 as a cancer stem cell marker in cancers of the digestive system; however, its predictive value remains controversial. Here, we investigate the correlation between CD166 positivity in digestive system cancers and clinicopathological features using meta-analysis.A comprehensive search in PubMed and ISI Web of Science through March of 2013 was performed. Only articles containing CD166 antigen immunohistochemical staining in cancers of the digestive system were included,including pancreatic cancer, esophageal cancer, gastric cancer and colorectal cancer. Data comparing 3- and 5-year overall survival along with other clinicopathological features were collected.Nine studies with 2553 patients who met the inclusion criteria were included for the analysis. The median rate of CD166 immunohistochemical staining expression was 56% (25.4%-76.3%. In colorectal cancer specifically, the results of a fixed-effects model indicated that CD166-positive expression was an independent marker associated with a smaller tumor burden (T category; RR = 0.93, 95%, CI: 0.88-0.98 but worse spread to nearby lymph nodes (N category; RR = 1.17, 95% CI: 1.05-1.30. The 5-year overall survival rate was showed relationship with cytoplasmic positive staining of CD166 (RR = 1.47 95% 1.21-1.79, but no significant association was found in the pool or any other stratified analysis with 3- or 5- year overall survival rate.Based on the published studies, different cellular location of CD166 has distinct prognostic value and cytoplasmic positive expression is associated with worse prognosis outcome. Besides, our results also find CD166 expression indicate advanced T category and N-positive status in colorectal cancer specifically.

  12. Gamma spectrometry and chemical characterization of bioactive glass seeds with Holmium-166 for oncological implants

    International Nuclear Information System (INIS)

    Valente, Eduardo S.

    2009-01-01

    Bioactive glass seeds synthesized by the sol-gel technique with Si:Ho:Ca composition with natural holmium incorporated were irradiated in the TRIGA type nuclear reactor IPR-R1 at 100kW, in the central thimble where the thermal neutron flux is 2.8x10 12 n/cm 2 .s and the epithermal neutron flux is 2.6 X 10 11 n/cm 2 .s . After an 8 hour irradiation time, with an induced activity close to 110MBq/seed, a set of seeds was submitted to Gamma Spectrometry Analysis in a counting system with an HPGe detector, ORTEC electronic instrumentation and a Camberra Multichannel Analyser, to determine all radionuclides present on the sample as well as its individual activities. Special attention was paid on the discrimination of Si, 40 Ca, 44 Ca, C and Ho as the other expected elements like 48 Ca, 2 H and 18 O were present in traces or have very short half-lives. The second sample was submitted to Plasma spectrometry to determine the 166 Ho concentration in weight. The third sample was submitted to an X-ray spectrometry in a JEOL-JXA-8900RL equipment to determine its qualitative chemical composition, in order to evaluate impurities and nominal composition. It was determined that most of the activity, after decaying of short half-life elements, was due to 166 Ho present on the sample, with a well characterized β and gamma spectra. The homogeneity of the seeds was tested on the X-ray spectrometry, and verified that there is no discrepancy in composition from distinct seeds or in a same seed. The results are relevant on the investigation of the viability of producing 166 Ho radioactive seeds for oncological implants. (author)

  13. Edaravone prevents neurotoxicity of mutant L166P DJ-1 in Parkinson's disease.

    Science.gov (United States)

    Li, Bing; Yu, Dawei; Xu, Zhiying

    2013-10-01

    Parkinson's disease (PD), which is estimated to affect approximately 1 % of the population over the age of 65, is the second most common neurodegenerative disorder after Alzheimer's disease. It was reported that pathogenic mutations in DJ-1 lead to autosomal recessive early-onset familial Parkinsonism. The L166P mutant of DJ-1 is the most commonly studied loss-of-function mutation in early onset familial PD, but the underlying mechanisms are still unknown. Edaravone is a powerful free radical scavenger used in clinical treatment for cerebral ischemic stroke. In the present study, we investigated the effects of edaravone on the neurotoxicity in PD-induced isoforms of DJ-1 containing the mutation L166P. Our results indicated that edaravone was able to significantly attenuate oxidative stress and improve mitochondrial function. Furthermore, edaravone was found to reduce apoptosis in Neuro2a cells through modulation of mitochondria-dependent apoptosis pathways. Interestingly, our result also demonstrated that edaravone was able to up-regulate VMAT2 expression in N2a cells in a dose-dependent manner. Our findings enhance the understanding of the neuro-protective effects of edaravone in cell models and suggest that edaravone offers significant protection in a PD-related in vitro model.

  14. Production and investigation of tungsten α emitters including the new isotopes, 165W and 166W

    International Nuclear Information System (INIS)

    Toth, K.S.; Schmidt-Ott, W.; Bingham, C.R.; Ijaz, M.A.

    1975-01-01

    Neutron-deficient tungsten isotopes were produced by bombarding an enriched 156 Dy target with 16 O ions accelerated in the Oak Ridge isochronous cyclotron. A gas-jet-capillary system was used to transport product nuclei to an area where their α-decay properties could be investigated. The data of Eastham and Grant concerning 162 , 163 , 164 W were confirmed. In addition, two new weak α groups were observed. On the basis of excitation functions, 14 N + 156 Dy cross bombardments, and α-decay energy systematics they were assigned to the new isotopes 165 W and 166 W. Their decay properties are as follows: (1) 165 W, E/sub alpha/ = 4.909 plus-or-minus 0.005 MeV, T 1 / 2 = 5.1 plus-or-minus 0.5 sec, and (2) 166 W, E/sub alpha/ = 4.739 plus-or-minus 0.005 MeV, T 1 / 2 = 16 plus-or-minus 3 sec

  15. PRODUCTION OF HAFNIUM METAL

    Science.gov (United States)

    Elger, G.W.; Boubel, R.W.

    1963-01-01

    This patent deals with a process of producing pure Hf metal from oxygen- contaminated gaseous Hf chloride. The oxygen compounds in the chioride gas are halogenated by contacting the gas at elevated temperature with Cl/sub 2/ in the presence of C. The Hf chloride, still in gaseous form, is contacted with molten Mg whereby Hf metal is formed and condensed on the Mg. (AEC)

  16. PKI 166 induced redox signalling and apoptosis through activation of p53, MAP kinase and caspase pathway in epidermoid carcinoma.

    Science.gov (United States)

    Das, Subhasis; Dey, Kaushik Kumar; Bharti, Rashmi; MaitiChoudhury, Sujata; Maiti, Sukumar; Mandal, Mahitosh

    2012-01-01

    Cellular redox changes have emerged as a pivotal and proximal event in cancer. PKI 166 is used to determine the effects of redox sensitive inhibition of EGFR, metastasis and apoptosis in epidermoid carcinoma. Cytotoxicity study of PKI 166 (IC50 1.0 microM) treated A431 cells were performed by MTT assay for 48 and 72 hrs. Morphological analysis of PKI 166 treated A431 cells for 48 hrs. revealed the cell shrinkage, loss of filopodia and lamellipodia by phase contrast and SEM images in dose dependent manner. It has cytotoxic effects through inhibiting cellular proliferation, leads to the induction of apoptosis, as increased fraction of sub-G1 phase of the cell cycle, chromatin condensation and DNA ladder. It inhibited cyclin-D1 and cyclin-E expression and induced p53, p21 expression in dose dependent manner. Consequently, an imbalance of Bax/Bcl-2 ratio triggered caspase cascade and subsequent cleavage of PARP, thereby shifting the balance in favour of apoptosis. PKI 166 treatment actively stimulated reactive oxygen species (ROS) and mitochondrial membrane depolarization. It inhibited some metastatic properties of A431 cells supressing colony formation by soft agar assay and inhibition of MMP 9 activity by gelatin zymography and western blot analysis. PKI 166 inhibited growth factor induced phosphorylation of EGFR, Akt, MAPK, JNK and colony formation in A431 cells. Thus the inhibition of proliferation was associated with redox regulation of the caspase cascade, EGFR, Akt/PI3K, MAPK/ ERK and JNK pathway. On the other hand, increased antioxidant activity leads to decreased ROS generation inhibit the anti-proliferative and apoptotic properties of PKI 166 in A431 cells. These observations indicated PKI 166 induced redox signalling dependent inhibition of cell proliferation, metastatic properties and induction of apoptotic potential in epidermoid carcinoma.

  17. Effects of oxygen partial pressure and annealing temperature on the residual stress of hafnium oxide thin-films on silicon using synchrotron-based grazing incidence X-ray diffraction

    Energy Technology Data Exchange (ETDEWEB)

    Biswas, Debaleen [Saha Institute of Nuclear Physics, 1/AF Bidhannagar, Kolkata 700 064 (India); Sinha, Anil Kumar [ISU, Raja Ramanna Centre for Advanced Technology, Indore 452 013 (India); Homi Bhabha National Institute, BARC, Mumbai 400 094 (India); Chakraborty, Supratic, E-mail: supratic.chakraborty@saha.ac.in [Saha Institute of Nuclear Physics, 1/AF Bidhannagar, Kolkata 700 064 (India)

    2016-10-30

    Highlights: • Residual stress estimation thin hafnium oxide film with thickness of <10 nm. • A mathematical expression is proposed for stress estimation of thin-film using GIXRD. • Residual stress varies with argon content in Ar/O{sub 2} plasma and annealing temperature. • Variation of stress is explained by IL swelling and enhanced structural relaxation. - Abstract: Synchrotron radiation-based grazing incidence X-ray diffraction (GI-XRD) technique is employed here to estimate the residual stress of < 10 nm thin hafnium oxide film deposited on Si (100) substrate at different argon/oxygen ratios using reactive rf sputtering. A decrease in residual stress, tensile in nature, is observed at higher annealing temperature for the samples deposited with increasing argon ratio in the Ar/O{sub 2} plasma. The residual stress of the films deposited at higher p{sub Ar} (Ar:O{sub 2} = 4:1) is also found to be decreased with increasing annealing temperature. But the stress is more or less constant with annealing temperature for the films deposited at lower Ar/O{sub 2} (1:4) ratio. All the above phenomena can be explained on the basis of swelling of the interfacial layer and enhanced structural relaxation in the presence of excess Hf in hafnium oxide film during deposition.

  18. Structural and functional characterization of human apolipoprotein E 72-166 peptides in both aqueous and lipid environments

    Directory of Open Access Journals (Sweden)

    Chou Chi-Yuan

    2011-01-01

    Full Text Available Abstract Backgrounds There are three apolipoprotein E (apoE isoforms involved in human lipid homeostasis. In the present study, truncated apoE2-, apoE3- and apoE4-(72-166 peptides that are tailored to lack domain interactions are expressed and elucidated the structural and functional consequences. Methods & Results Circular dichroism analyses indicated that their secondary structure is still well organized. Analytical ultracentrifugation analyses demonstrated that apoE-(72-166 produces more complicated species in PBS. All three isoforms were significantly dissociated in the presence of dihexanoylphosphatidylcholine. Dimyristoylphosphatidylcholine turbidity clearance assay showed that apoE4-(72-166 maintains the highest lipid-binding capacity. Finally, only apoE4-(72-166 still maintained significant LDL receptor binding ability. Conclusions Overall, apoE4-(72-166 peptides displayed a higher lipid-binding and comparable receptor-binding ability as to full-length apoE. These findings provide the explanation of diverged functionality of truncated apoE isoforms.

  19. Synthesis, characterization, and in vitro evaluation of a radio-metal organic framework composed of in vivo generator {sup 166}Dy/{sup 166}Ho and DOTMP as a novel agent for bone marrow ablation

    Energy Technology Data Exchange (ETDEWEB)

    Vosoghi, Sara; Shirvani-Arani, Simindokht; Bahrami-Samani, Ali; Salek, Nafise; Mirerezaei, Ehsan; Jalilian, Amir Reza [Nuclear Science and Technology Research Institute (NSTRI), Tehran (Iran, Islamic Republic of)

    2016-07-01

    In this study, the MOF concept contributed to the preparation of a novel, bone-ablating agent composed of Cu(II) using the in vivo generator {sup 166}Dy/{sup 166}Ho and 1,4,7,10-tetraazacyclododecane-1,4,7,10-tetramethylene phosphonic acid (DOTMP). The product was characterized (IR, elemental analysis: CHN, ICM-MS, PIXE, DLS, XRD) and quality-controlled (radio-thin layer chromatography (RTLC)). The stability and in vitro hydroxyapatite binding was checked up to one week at 37 C in human serum. Radio-MOF crystals and colloidal radio-MOF particles were obtained by varying the synthesizing conditions (including pH and temperature), and they had similar IR patterns and similar elemental analysis results. The estimated chemical formula was [1Lu-1Cu-1Cl-1DOTMP] for both. The final product was synthesized at pH = 8 while stirring at room temperature using {sup 166}Dy/{sup 166}Ho-nitrate, CuCl{sub 2}, and DOTMP (yield > 99%, RTLC). Dynamic light scattering (DLS) measurements showed particles in the size range of 60 to 100 nm for the resultant radio-MOF particles (RMP). In vitro binding experiments showed acceptable bone-seeking affinity of the prepared formula even after one week of storage in human serum at 37 C. Importantly, this is the first study of the use of the MOF concept to provide a highly-stable organometallic compound containing {sup 166}Dy/{sup 166}Ho in vivo generator for bone marrow ablation.

  20. Remote detection of methane with a 1.66-microm diode laser.

    Science.gov (United States)

    Uehara, K; Tai, H

    1992-02-20

    High-sensitivity real-time remote detection of methane in air with a 1.66-microm distributed-feedback diode laser operating at room temperature is demonstrated by laboratory simulations. The laser current was modulated at a high frequency of ~5 MHz, and the laser-center frequency was locked onto a methane-absorption line. The laser light directed toward the probed region was received after one-way transmission or further reflection from a topographic target. The methane absorption was detected by the second-harmonic component in the optical-power variation. The minimum-detectable concentration-path-length product in the transmission scheme was 0.3 part in 10(6) m for a signal averaging time of 1.3 s. In the reflection scheme, the amount of methane could be measured from the ratio of the fundamental and second-harmonic signal intensities independently of the received power.

  1. Fotometría de grupos compactos de galaxias: Shakhbazian 37, 45, 166, 331 y 362

    Science.gov (United States)

    Campos, J. M.; Calderón, J. H.; Gimeno, N. G.; Díaz, R. J.

    Continuando con la fotometría CCD de Grupos de Galaxias Compactos de Shakhbazyan (SCGG) en este trabajo se presentan nuevos resultados preliminares sobre los grupos Shakbazyan 37, 45, 166, 331 y 362. EL objeto del proyecto es contribuir al estudio de las propiedades físicas de tales grupos y contribuir a las bases de datos para mejora de las estadísticas. Los datos fueron adquiridos con el Telescopio JKT del Observatorio Norte Europeo. El análisis de las imágenes en las bandas I y B como del índice de color B-I permitió reidentificar las galaxias catalogadas, resultando las mismas muy enrojecidas y verificando que predominan las galaxias tempranas, resultados consistentes con los obtenidos para otros grupos y por otros autores.

  2. Chlamydia and sudden infant death syndrome. A study of 166 SIDS and 30 control cases

    DEFF Research Database (Denmark)

    Banner, Jytte; Lundemose, A G; Gregersen, M

    1990-01-01

    .04). Chlamydia trachomatis is an agent of pneumonia in 1-4 month-old infants who have acquired the disease from an infected cervix during birth, but other chlamydia species are also capable of causing pneumonia. The lung sections of the 32 chlamydia positive SIDS cases did not show typical histological signs......Chlamydia inclusions could be demonstrated by an immunofluorescence assay in formalin-fixed lung sections in 32 of 166 cases (19.4%) of Sudden Infant Death Syndrome (SIDS) and in the lungs of only 1 of 30 infants with a known cause of death (3.3%). The difference is statistically significant (P = 0...... of pneumonia. Even though chlamydia inclusions were detected in the lungs of 32 SIDS cases a causal relation between chlamydia infection and SIDS could not be demonstrated....

  3. Closure Report for Corrective Action Unit 166: Storage Yards and Contaminated Materials, Nevada Test Site, Nevada

    Energy Technology Data Exchange (ETDEWEB)

    NSTec Environmental Restoration

    2009-08-01

    Corrective Action Unit (CAU) 166 is identified in the Federal Facility Agreement and Consent Order (FFACO) as 'Storage Yards and Contaminated Materials' and consists of the following seven Corrective Action Sites (CASs), located in Areas 2, 3, 5, and 18 of the Nevada Test Site: CAS 02-42-01, Condo Release Storage Yd - North; CAS 02-42-02, Condo Release Storage Yd - South; CAS 02-99-10, D-38 Storage Area; CAS 03-42-01, Conditional Release Storage Yard; CAS 05-19-02, Contaminated Soil and Drum; CAS 18-01-01, Aboveground Storage Tank; and CAS 18-99-03, Wax Piles/Oil Stain. Closure activities were conducted from March to July 2009 according to the FF ACO (1996, as amended February 2008) and the Corrective Action Plan for CAU 166 (U.S. Department of Energy, National Nuclear Security Administration Nevada Site Office, 2007b). The corrective action alternatives included No Further Action and Clean Closure. Closure activities are summarized. CAU 166, Storage Yards and Contaminated Materials, consists of seven CASs in Areas 2, 3, 5, and 18 of the NTS. The closure alternatives included No Further Action and Clean Closure. This CR provides a summary of completed closure activities, documentation of waste disposal, and confirmation that remediation goals were met. The following site closure activities were performed at CAU 166 as documented in this CR: (1) At CAS 02-99-10, D-38 Storage Area, approximately 40 gal of lead shot were removed and are currently pending treatment and disposal as MW, and approximately 50 small pieces of DU were removed and disposed as LLW. (2) At CAS 03-42-01, Conditional Release Storage Yard, approximately 7.5 yd{sup 3} of soil impacted with lead and Am-241 were removed and disposed as LLW. As a BMP, approximately 22 ft{sup 3} of asbestos tile were removed from a portable building and disposed as ALLW, approximately 55 gal of oil were drained from accumulators and are currently pending disposal as HW, the portable building was removed and

  4. Closure Report for Corrective Action Unit 166: Storage Yards and Contaminated Materials, Nevada Test Site, Nevada

    International Nuclear Information System (INIS)

    2009-01-01

    Corrective Action Unit (CAU) 166 is identified in the Federal Facility Agreement and Consent Order (FFACO) as 'Storage Yards and Contaminated Materials' and consists of the following seven Corrective Action Sites (CASs), located in Areas 2, 3, 5, and 18 of the Nevada Test Site: CAS 02-42-01, Condo Release Storage Yd - North; CAS 02-42-02, Condo Release Storage Yd - South; CAS 02-99-10, D-38 Storage Area; CAS 03-42-01, Conditional Release Storage Yard; CAS 05-19-02, Contaminated Soil and Drum; CAS 18-01-01, Aboveground Storage Tank; and CAS 18-99-03, Wax Piles/Oil Stain. Closure activities were conducted from March to July 2009 according to the FF ACO (1996, as amended February 2008) and the Corrective Action Plan for CAU 166 (U.S. Department of Energy, National Nuclear Security Administration Nevada Site Office, 2007b). The corrective action alternatives included No Further Action and Clean Closure. Closure activities are summarized. CAU 166, Storage Yards and Contaminated Materials, consists of seven CASs in Areas 2, 3, 5, and 18 of the NTS. The closure alternatives included No Further Action and Clean Closure. This CR provides a summary of completed closure activities, documentation of waste disposal, and confirmation that remediation goals were met. The following site closure activities were performed at CAU 166 as documented in this CR: (1) At CAS 02-99-10, D-38 Storage Area, approximately 40 gal of lead shot were removed and are currently pending treatment and disposal as MW, and approximately 50 small pieces of DU were removed and disposed as LLW. (2) At CAS 03-42-01, Conditional Release Storage Yard, approximately 7.5 yd 3 of soil impacted with lead and Am-241 were removed and disposed as LLW. As a BMP, approximately 22 ft 3 of asbestos tile were removed from a portable building and disposed as ALLW, approximately 55 gal of oil were drained from accumulators and are currently pending disposal as HW, the portable building was removed and disposed as LLW, and

  5. Cytotoxic effect of the Her-2/Her-1 inhibitor PKI-166 on renal cancer cells expressing the connexin 32 gene.

    Science.gov (United States)

    Fujimoto, Eriko; Yano, Tomohiro; Sato, Hiromi; Hagiwara, Kiyokazu; Yamasaki, Hiroshi; Shirai, Sumiko; Fukumoto, Keiko; Hagiwara, Hiromi; Negishi, Etsuko; Ueno, Koichi

    2005-02-01

    We have reported that connexin (Cx) 32 acts as a tumor suppressor gene in renal cancer cells partly due to Her-2 inactivation. Here, we determined if a Her-2/Her-1 inhibitor (PKI-166) can enhance the tumor-suppressive effect of Cx32 in Caki-2 cells from human renal cell carcinoma. The expression of Cx32 in Caki-2 cells was required for PKI-166-induced cytotoxic effect at lower doses. The cyctotoxicity was dependent on the occurrence of apoptosis and partly mediated by Cx32-driven gap junction intercellular communications. These results suggest that PKI-166 further supports the tumor-suppressive effect of the Cx32 gene in renal cancer cells through the induction of apoptosis.

  6. PWR Blowdown Heat Transfer Separate-Effects Program. Thermal-Hydraulic Test Facility experimental data report for test 166S

    International Nuclear Information System (INIS)

    Clemons, V.D.; White, M.D.; Hedrick, R.A.

    1978-01-01

    Reduced instrument responses are presented for Thermal-Hydraulic Test Facility (THTF) test 166S, which is part of the ORNL Pressurized-Water Reactor (PWR) Blowdown Heat Transfer Separate-Effects Program. The objective of the program is to investigate the thermal-hydraulic phenomenon governing the energy transfer and transport processes that occur during a loss-of-coolant accident in a PWR system. Test 166S was conducted to obtain thermal-hydraulic and CHF information in THTF bundle 1 with an intact hot leg. The primary purpose of this report is to make the reduced instrument responses during tests 166S available. These are presented in graphical form in engineering units and have been analyzed only to the extent necessary to ensure reasonableness and consistency

  7. Extended study on oxidation behaviors of UN0.68 and UN1.66 by XPS

    Science.gov (United States)

    Luo, Lizhu; Hu, Yin; Pan, Qifa; Long, Zhong; Lu, Lei; Liu, Kezhao; Wang, Xiaolin

    2018-04-01

    The surface oxidation behaviors of UN0.68 and UN1.66 thin films are investigated by X-ray photoelectron spectroscopy (XPS), and the traditional U4f/N1s, O1s, valence band spectra as well as the unconventional U4d and U5d spectra are collected for the understanding of their oxidation behavior in-depth. Similar asymmetrical peak shape of the U4f spectra to uranium is observed for both uranium nitrides, despite of a slight shift to higher energy side for UN1.66 clean surface. However, significant difference among the corresponding spectra of UN0.68 and UN1.66 during oxidation reveals the distinctive properties of each own. The coexistence of UO2-x, UO2 and UO2-x.Ny on UN0.68 surface results in the peculiar features of U4f spectra as well as the others within the XPS energy scale, where peaks of the oxidized species firstly shift to higher energy side compared to the clean surface, and then return closely towards those of stoichiometric UO2. For UN1.66, the generation of U-N-O ternary compounds on the surface is identified with the symmetrical U4f peaks at 379.9eV and 390.8 eV, which locate intermediate between UO2 and UN1.66, and gradually expanding to higher energy side during the progressive oxidation. Furthermore, the formation of N-O species on UN1.66 surface is also detected as an oxidation product. The metallic character of UN1.66 is identified by the intense signal at Fermi level, which is greatly suppressed by the increasing oxygen exposure and implies the weakening metallic properties of the as-generated U-N-O compounds. Higher uranium oxides, such as UO3 and U4O9, are deduced to be the final oxidation products, and a multistage mechanism for UN1.66 following the exposure to oxygen is discussed.

  8. Contribution towards ALD and MOCVD of rare earth oxides and hafnium oxide. From precursor evaluation to process development and thin film characterization

    International Nuclear Information System (INIS)

    Xu, Ke

    2013-01-01

    elements for ALD applications. A possible synthesis route is the salt metatheses route. It could be expected that the monodentate guanidine ligand would provide increased reactivity towards water, where the bulky guanidine ligands will shield the RE center providing self-limiting growth behavior. In Chapter 4 and 7, ALD of rare earth oxides and hafnium oxide using corresponding guanidinate precursors are in detail investigated. According to the measurements, these processes are true ALD processes with broad ALD windows, high growth per cycle in the saturated area. Furthermore, the rare earth guanidinate and hafnium guanidinate precursors exhibit matching ALD window in the temperature range of 200 - 225 C. This motivated us to deposite trinary oxide thin films (HfREOx) using corresponding precursor combinations.

  9. Actin re-organization induced by Chlamydia trachomatis serovar D--evidence for a critical role of the effector protein CT166 targeting Rac.

    Directory of Open Access Journals (Sweden)

    Jessica Thalmann

    Full Text Available The intracellular bacterium Chlamydia trachomatis causes infections of urogenital tract, eyes or lungs. Alignment reveals homology of CT166, a putative effector protein of urogenital C. trachomatis serovars, with the N-terminal glucosyltransferase domain of clostridial glucosylating toxins (CGTs. CGTs contain an essential DXD-motif and mono-glucosylate GTP-binding proteins of the Rho/Ras families, the master regulators of the actin cytoskeleton. CT166 is preformed in elementary bodies of C. trachomatis D and is detected in the host-cell shortly after infection. Infection with high MOI of C. trachomatis serovar D containing the CT166 ORF induces actin re-organization resulting in cell rounding and a decreased cell diameter. A comparable phenotype was observed in HeLa cells treated with the Rho-GTPase-glucosylating Toxin B from Clostridium difficile (TcdB or HeLa cells ectopically expressing CT166. CT166 with a mutated DXD-motif (CT166-mut exhibited almost unchanged actin dynamics, suggesting that CT166-induced actin re-organization depends on the glucosyltransferase motif of CT166. The cytotoxic necrotizing factor 1 (CNF1 from E. coli deamidates and thereby activates Rho-GTPases and transiently protects them against TcdB-induced glucosylation. CNF1-treated cells were found to be protected from TcdB- and CT166-induced actin re-organization. CNF1 treatment as well as ectopic expression of non-glucosylable Rac1-G12V, but not RhoA-G14A, reverted CT166-induced actin re-organization, suggesting that CT166-induced actin re-organization depends on the glucosylation of Rac1. In accordance, over-expression of CT166-mut diminished TcdB induced cell rounding, suggesting shared substrates. Cell rounding induced by high MOI infection with C. trachomatis D was reduced in cells expressing CT166-mut or Rac1-G12V, and in CNF1 treated cells. These observations indicate that the cytopathic effect of C. trachomatis D is mediated by CT166 induced Rac1 glucosylation

  10. Radioactive ceramic seeds with Ho-166 and Sm-153 with perspective of use in brachytherapy

    International Nuclear Information System (INIS)

    Valente, Eduardo Sarmento

    2010-01-01

    This work aimed to characterize physically, chemically and radioactively ceramics seeds with holmium and samarium embedded in ceramic matrix produced by sol-gel route. Biological response of HeLa cells was investigated macroscopically in vitro under the exposure to β radiation of Ho-166 and Sm-153. The dispersal of radioactive material in simulated body fluid (SBF) was made and the dose rate and total dose deposited in the volume delimited by the range of β particles in the water was calculated. The methodology used in physical, chemical and nuclear characterization was based on the following techniques: atomic emission spectrometry, neutron activation analysis, gamma spectrometry, X-ray fluorescence spectrometry and X-rays diffraction. In addition to the solubility in SBF, an in vivo pilot study assessed the dispersion of radioactive seeds implanted in rabbit muscle tissue. Four experiments were prepared to investigate the biological response in vitro, in which radioactive seeds were placed directly in contact with the cells in confluent culture flasks. The first two were done with seed's activity of 3.7 MBq (0.1 mCi) for the Sm-153 and 11.1 MBq (0.3 mCi) for Ho-166. There were no concerns with spatial positioning for seeds in those early experiments. The subsequent experiments were performed with activity ranging from 37 MBq (1 mCi) and 111 MBq (3 mCi) and with defined position of the seeds in the flask. The results showed the presence of halos with maximum diameter of 8 mm around the seeds where there was a drastic reduction in the number of viable cells as a result of the effects of β radiation. The calculation of dose deposited in water as well as the dose rate calculation of during handling of the seeds for an implant followed the methodology established by MIRD. These calculations found dose rates ranging from 7 to 19 Gy/h and integrated doses between 93 and 730 Gy, due to β radiation, for 6 half-lives of radioisotopes Sm-153 and Ho-166. The dose

  11. Radiosynoviorthesis of knees by means of 166Ho-holmium-boro-macroaggregates.

    Science.gov (United States)

    Kraft, Otakar; Kaspárek, Richard; Ullmann, Vojtech; Melichar, Frantisek; Kropácek, Martin; Mirzajevova, Marcela

    2007-04-01

    The aim of this study was to evaluate adverse and therapeutic effects of applicated holmium-boro-macroaggregates (HBMAs) in the radiosynoviorthesis (RSO) of knees in patients suffering from chronic synovitis. We started RSO of the knees by means of a new radiopharmaceutical (RF) HBMA in patients with gonarthrosis, rheumatoid arthritis, chronic synovitis, psoriatic arthritis, and gout arthropathy. Seventeen (17) intra-articular injections were performed in 15 patients who were receiving a mean activity of 972 MBq (range, 904-1057) of 166Ho-HBMA. Patient inclusion to the study followed a series of inclusion and exclusion criterions. The patients were hospitalized for 3 days. Side-effects were evaluated during their hospital stay and again after 6-8 weeks. Static scintigraphy of knee joints and measurements of blood radioactivity were performed. Therapeutic effects were evaluated after 6-8 weeks and at 6 months. In 2 hours and 2 days following the application, we proved, by means of knee and inguinal scintigraphy, only insignificant radiopharmaceutical leakage from the joint cavity to the inguinal lymph nodes in 4 patients. In the treated patients, no serious adverse effects occurred. Nine (9) patients were without complaints, 4 patients had slight knee exudation, and 2 patients had great exudation. Therapeutic effects were as follows: 2 patients were without pain, 9 were with lower pain, 3 were with the same pain, and 1 patient was with increased pain. Joint motion was improved in 7 patients, remained the same in 7 patients, and was impaired in 1 patient. Analgesics consumption was lower in 5 patients, the same in 9 patients, and greater in 1 patient. Knee exudation was absent in 2 patients, lower in 4 patients, the same in 6 patients, and greater in 3 patients. In 3 patients it was necessary to do surgical RSO. This RF can extend the range of clinically used radiopharmaceuticals for RSO and to supplement space between 90Y with high energy and 186Re with 169Er with

  12. Dosimetric effectiveness in implants with distinct HO166-seed distribution in prostate

    International Nuclear Information System (INIS)

    Braga, Viviane V. B.; Campos, Tarcísio P. R.

    2017-01-01

    Currently, there is a need to produce new therapeutic techniques for the treatment of prostate tumors, considering the high incidence of the disease and significant morbidity rates associated with surgery and radiotherapy. Simulations in brachytherapy produce essential information about the efficiency and dosimetric efficacy compared to other techniques. Computational simulation by Monte Carlo method has been used to evaluate the absorbed dose and effective dose in radiotherapy and radiology. Virtual, analytical or voxelized phantoms are useful in the internal assessment of the spatial distribution of absorbed dose. This study estimated the efficiency of dosimetry by parameters of merit generated from volumetric distributions of absorbed doses simulating various spatial distributions of Ho-166 seeds in a prostate model. A computer model of voxels was developed, using the code SISCODES (Computational System for Dosimetry by Neutrons and Photons by Stochastic Methods applied to radiology and radiotherapy), representative of a real physical simulator predefined as a calibration method. The virtual model reproduced a cubic box, filled with muscle equivalent tissue (TE), where a 5-cm diameter ball with TE-prostate was positioned 2-cm from the air interface. A Ho-166 seed distribution, produced by 16 filet-implants distributed regularly (10-mm pitch) containing 04 separate 8-mm seeds, was employed. Two pitch were considered: 9 and 10 mm, with same distance between seed in a fillet. Based on SISCODE database of chemical composition of tissues and nuclear data, The code allowed the association of nuclear and chemical data to the voxels of the model, by the selection of the tissue of each voxel, as well as the positioning of the sources and their spatial distribution and spectra. The code MCNP5 simulated the transport of photons and electrons in the model, generating the energy deposited per unit mass in each voxel for photons in MeV.g-1 and energy absorbed in MeV for beta

  13. Dosimetric effectiveness in implants with distinct HO166-seed distribution in prostate

    Energy Technology Data Exchange (ETDEWEB)

    Braga, Viviane V. B.; Campos, Tarcísio P. R., E-mail: Vitoriabraga06@gmail.com, E-mail: tprcampos@yahoo.com.br [Universidade Federal de Minas Gerais (UFMG), Belo Horizonte, MG (Brazil). Departamento de Engenharia Nuclear

    2017-07-01

    Currently, there is a need to produce new therapeutic techniques for the treatment of prostate tumors, considering the high incidence of the disease and significant morbidity rates associated with surgery and radiotherapy. Simulations in brachytherapy produce essential information about the efficiency and dosimetric efficacy compared to other techniques. Computational simulation by Monte Carlo method has been used to evaluate the absorbed dose and effective dose in radiotherapy and radiology. Virtual, analytical or voxelized phantoms are useful in the internal assessment of the spatial distribution of absorbed dose. This study estimated the efficiency of dosimetry by parameters of merit generated from volumetric distributions of absorbed doses simulating various spatial distributions of Ho-166 seeds in a prostate model. A computer model of voxels was developed, using the code SISCODES (Computational System for Dosimetry by Neutrons and Photons by Stochastic Methods applied to radiology and radiotherapy), representative of a real physical simulator predefined as a calibration method. The virtual model reproduced a cubic box, filled with muscle equivalent tissue (TE), where a 5-cm diameter ball with TE-prostate was positioned 2-cm from the air interface. A Ho-166 seed distribution, produced by 16 filet-implants distributed regularly (10-mm pitch) containing 04 separate 8-mm seeds, was employed. Two pitch were considered: 9 and 10 mm, with same distance between seed in a fillet. Based on SISCODE database of chemical composition of tissues and nuclear data, The code allowed the association of nuclear and chemical data to the voxels of the model, by the selection of the tissue of each voxel, as well as the positioning of the sources and their spatial distribution and spectra. The code MCNP5 simulated the transport of photons and electrons in the model, generating the energy deposited per unit mass in each voxel for photons in MeV.g-1 and energy absorbed in MeV for beta

  14. 25 CFR 166.910 - What happens if I do not fulfill my obligation to the BIA?

    Science.gov (United States)

    2010-04-01

    ... GRAZING PERMITS Agriculture Education, Education Assistance, Recruitment, and Training § 166.910 What... under agriculture education programs with an obligated service requirement, and who does not accept employment or unreasonably terminates employment must repay us in accordance with the following table: If you...

  15. 17 CFR 230.166 - Exemption from section 5(c) for certain communications in connection with business combination...

    Science.gov (United States)

    2010-04-01

    ...) for certain communications in connection with business combination transactions. 230.166 Section 230... only to communications relating to business combinations. The exemption does not apply to...) Communications. In a registered offering involving a business combination transaction, any communication made in...

  16. Arginine Coordination in Enzymatic Phosphoryl Transfer: Evaluation of the Effect of Arg166 Mutations in Escherichia Coli Alkaline Phosphatase

    International Nuclear Information System (INIS)

    O'Brien, P.J.; Lassila, J.K.; Fenn, T.D.; Zalatan, J.G.; Herschlag, D.

    2008-01-01

    Arginine residues are commonly found in the active sites of enzymes catalyzing phosphoryl transfer reactions. Numerous site-directed mutagenesis experiments establish the importance of these residues for efficient catalysis, but their role in catalysis is not clear. To examine the role of arginine residues in the phosphoryl transfer reaction, we have measured the consequences of mutations to arginine 166 in Escherichia coli alkaline phosphatase on hydrolysis of ethyl phosphate, on individual reaction steps in the hydrolysis of the covalent enzyme-phosphoryl intermediate, and on thio substitution effects. The results show that the role of the arginine side chain extends beyond its positive charge, as the Arg166Lys mutant is as compromised in activity as Arg166Ser. Through measurement of individual reaction steps, we construct a free energy profile for the hydrolysis of the enzyme-phosphate intermediate. This analysis indicates that the arginine side chain strengthens binding by ∼3 kcal/mol and provides an additional 1-2 kcal/mol stabilization of the chemical transition state. A 2.1 (angstrom) X-ray diffraction structure of Arg166Ser AP is presented, which shows little difference in enzyme structure compared to the wild-type enzyme but shows a significant reorientation of the bound phosphate. Altogether, these results support a model in which the arginine contributes to catalysis through binding interactions and through additional transition state stabilization that may arise from complementarity of the guanidinum group to the geometry of the trigonal bipyramidal transition state

  17. Effect of Advanced Plasma Source bias voltage on properties of HfO2 films prepared by plasma ion assisted electron evaporation from metal hafnium

    International Nuclear Information System (INIS)

    Zhu, Meiping; Yi, Kui; Arhilger, Detlef; Qi, Hongji; Shao, Jianda

    2013-01-01

    HfO 2 films, using metal hafnium as starting material, are deposited by plasma-ion assisted electron evaporation with different Advanced Plasma Source (APS) bias voltages. The refractive index and extinction coefficient are calculated, the chemical state and composition, as well as the stress and aging behavior is investigated. Laser induced damage threshold (LIDT) and damage mechanism are also evaluated and discussed. Optical, structural, mechanical and laser induced damage properties of HfO 2 films are found to be sensitive to APS bias voltage. The film stress can be tuned by varying the APS bias voltage. Damage morphologies indicate the LIDT of the HfO 2 films at 1064 nm and 532 nm are dominated by the nodular-defect density in coatings, while the 355 nm LIDT is dominated by the film absorption. HfO 2 films with higher 1064 nm LIDT than samples evaporated from hafnia are achieved with bias voltage of 100 V. - Highlights: • HfO 2 films are evaporated with different Advanced Plasma Source (APS) bias voltages. • Properties of HfO 2 films are sensitive to APS bias voltage. • With a bias voltage of 100 V, HfO 2 coatings without any stress can be achieved. • Higher 1064 nm laser induced damage threshold is achieved at a bias voltage of 100 V

  18. Design of an Extractive Distillation Column for the Environmentally Benign Separation of Zirconium and Hafnium Tetrachloride for Nuclear Power Reactor Applications

    Directory of Open Access Journals (Sweden)

    Le Quang Minh

    2015-09-01

    Full Text Available Nuclear power with strengthened safety regulations continues to be used as an important resource in the world for managing atmospheric greenhouse gases and associated climate change. This study examined the environmentally benign separation of zirconium tetrachloride (ZrCl4 and hafnium tetrachloride (HfCl4 for nuclear power reactor applications through extractive distillation using a NaCl-KCl molten salt mixture. The vapor–liquid equilibrium behavior of ZrCl4 and HfCl4 over the molten salt system was correlated with Raoult’s law. The molten salt-based extractive distillation column was designed optimally using a rigorous commercial simulator for the feasible separation of ZrCl4 and HfCl4. The molten salt-based extractive distillation approach has many potential advantages for the commercial separation of ZrCl4 and HfCl4 compared to the conventional distillation because of its milder temperatures and pressure conditions, smaller number of required separation trays in the column, and lower energy requirement for separation, while still taking the advantage of environmentally benign feature by distillation. A heat-pump-assisted configuration was also explored to improve the energy efficiency of the extractive distillation process. The proposed enhanced configuration reduced the energy requirement drastically. Extractive distillation can be a promising option competing with the existing extraction-based separation process for zirconium purification for nuclear power reactor applications.

  19. A silicon doped hafnium oxide ferroelectric p–n–p–n SOI tunneling field–effect transistor with steep subthreshold slope and high switching state current ratio

    Directory of Open Access Journals (Sweden)

    Saeid Marjani

    2016-09-01

    Full Text Available In this paper, a silicon–on–insulator (SOI p–n–p–n tunneling field–effect transistor (TFET with a silicon doped hafnium oxide (Si:HfO2 ferroelectric gate stack is proposed and investigated via 2D device simulation with a calibrated nonlocal band–to–band tunneling model. Utilization of Si:HfO2 instead of conventional perovskite ferroelectrics such as lead zirconium titanate (PbZrTiO3 and strontium bismuth tantalate (SrBi2Ta2O9 provides compatibility to the CMOS process as well as improved device scalability. By using Si:HfO2 ferroelectric gate stack, the applied gate voltage is effectively amplified that causes increased electric field at the tunneling junction and reduced tunneling barrier width. Compared with the conventional p–n–p–n SOI TFET, the on–state current and switching state current ratio are appreciably increased; and the average subthreshold slope (SS is effectively reduced. The simulation results of Si:HfO2 ferroelectric p–n–p–n SOI TFET show significant improvement in transconductance (∼9.8X enhancement at high overdrive voltage and average subthreshold slope (∼35% enhancement over nine decades of drain current at room temperature, indicating that this device is a promising candidate to strengthen the performance of p–n–p–n and conventional TFET for a switching performance.

  20. L2₁ and XA Ordering Competition in Hafnium-Based Full-Heusler Alloys Hf₂VZ (Z = Al, Ga, In, Tl, Si, Ge, Sn, Pb).

    Science.gov (United States)

    Wang, Xiaotian; Cheng, Zhenxiang; Wang, Wenhong

    2017-10-20

    For theoretical designing of full-Heusler based spintroinc materials, people have long believed in the so-called Site Preference Rule (SPR). Very recently, according to the SPR, there are several studies on XA-type Hafnium-based Heusler alloys X₂YZ, i.e., Hf₂VAl, Hf₂CoZ (Z = Ga, In) and Hf₂CrZ (Z = Al, Ga, In). In this work, a series of Hf₂-based Heusler alloys, Hf₂VZ (Z = Al, Ga, In, Tl, Si, Ge, Sn, Pb), were selected as targets to study the site preferences of their atoms by first-principle calculations. It has been found that all of them are likely to exhibit the L2₁-type structure instead of the XA one. Furthermore, we reveal that the high values of spin-polarization of XA-type Hf₂VZ (Z = Al, Ga, In, Tl, Si, Ge, Sn, Pb) alloys have dropped dramatically when they form the L2₁-type structure. Also, we prove that the electronic, magnetic, and physics nature of these alloys are quite different, depending on the L2₁-type or XA-type structures.

  1. Holmium-166m: multi-gamma standard to determine the activity of radionuclides in semiconductor detectors

    International Nuclear Information System (INIS)

    Bernardes, Estela Maria de Oliveira

    2001-01-01

    The efficiency and calibration curves as function of gamma-ray energy for a germanium detector are usually established by using many standard gamma ray sources of radionuclides decaying with few gamma rays or radionuclides having complex decay scheme, as 152 Eu or 133 Ba. But these radionuclides cannot be used alone, because they have a few gamma lines with high intensity and these lines have a irregular distribution in the energy spectrum. 166m Ho is found to be a convenient single source for such calibration, because it decays by β - with subsequent emission of about 40 strong and well distributed gamma lines between 80 and 1500 keV. Moreover, its long half - life (1200 years) and X-rays characteristics between 40 and 50 keV makes it a good standard for calibration of germanium detectors. However, it is necessary to know with accuracy and precision the gamma ray intensities of their main lines, due to the fact that literature has showed discrepant values. Then, a methodology to determine the emission probability of its main lines is proposed by means of combined use of gamma spectrometry and coincidence 4πβ -γ techniques. The experimental results show consistence to the others authors, with lower or compatible uncertainties. (author)

  2. Clinical trial of {sup 166}Ho-CHICO in the treatment of rheumatoid knee synovitis

    Energy Technology Data Exchange (ETDEWEB)

    Kim, S. Y.; Yoo, D. H.; Bae, S. C.; Lee, I. H.; Jung, S. S.; Jun, J. B.; Kim, T. H.; Kim, S. S. [Hanyang Univ., Seoul (Korea)

    2000-03-01

    The untreated, chronic synovial inflammation leads to pannus formation and eventual destruction of the articular cartilage. In cases where medical therapy was unsuccessful, surgical of radiation synovectomy over surgical synovectomy are (1) greater destruction of diseased synovium, (2) reduced Potential for blood clots and infection, (3) no requirement for anesthesia, and (4) less costly and less time consuming. Recently KAERI developed Dy-165 HMA, which was characterized by the absence of iron and a higher concentration of dysprosium. And then more recently KAERI also developed {sup 16H}o-CHICO, which was characterized by relatively longer half-life (26.8 hr), more biological due to organic nature of chitosan, more even spatial distribution due to colloidal solution, and more absorbable to synovium than Dy-165 HMA. These long-term follow-up results indicate that the {sup 166}Ho-CHICO is an effective and safe agent for radiation synovectomy for knee synovitis in patients with rheumatoid arthritis as well as the other chronic arthritides. But further large scaled and controlled study are required. 16 refs. (Author)

  3. EVA1A/TMEM166 Regulates Embryonic Neurogenesis by Autophagy

    Directory of Open Access Journals (Sweden)

    Mengtao Li

    2016-03-01

    Full Text Available Self-renewal and differentiation of neural stem cells is essential for embryonic neurogenesis, which is associated with cell autophagy. However, the mechanism by which autophagy regulates neurogenesis remains undefined. Here, we show that Eva1a/Tmem166, an autophagy-related gene, regulates neural stem cell self-renewal and differentiation. Eva1a depletion impaired the generation of newborn neurons, both in vivo and in vitro. Conversely, overexpression of EVA1A enhanced newborn neuron generation and maturation. Moreover, Eva1a depletion activated the PIK3CA-AKT axis, leading to the activation of the mammalian target of rapamycin and the subsequent inhibition of autophagy. Furthermore, addition of methylpyruvate to the culture during neural stem cell differentiation rescued the defective embryonic neurogenesis induced by Eva1a depletion, suggesting that energy availability is a significant factor in embryonic neurogenesis. Collectively, these data demonstrated that EVA1A regulates embryonic neurogenesis by modulating autophagy. Our results have potential implications for understanding the pathogenesis of neurodevelopmental disorders caused by autophagy dysregulation.

  4. Bone marrow ablation with Ho-166 pharmaceuticals as preparation for bone marrow transplants

    International Nuclear Information System (INIS)

    Parks, N.J.; Kawakami, T.; Avila, M.; White, R.; Cain, G.; Moore, P.F.

    1991-01-01

    Bone marrow ablation is required preparation for leukemia patients where bone marrow transplantation is to be the therapeutic modality. Presently, the total body irradiation that is used produces appreciable morbidity in terms of radiation sickness, but an evenly distributed dose to marrow. The authors have shown in Beagles that bone-seeking radiolanthanide (Ho-166, t 1/2 = 25 h, 1.8 MeB beta, carrier added) phosphonic acid chelates can be used to completely ablate bone marrow with little morbidity. The research plan, incorporating bone marrow ablation with bone-seeking radionuclides and in vitro purging of aspirated leukemic marrow for use in autologous marrow transplants, is presented. Phosphonic acid complexes of Sm-153 also localize in the skeleton and have found use in the palliation of bone pain. However, the dose distribution is uneven because these radiopharmaceuticals distribute according to available surface; 2-4 times the skeletal average in trabecular vs cortical bone. Thus, the marrow dose can vary. The authors' research group and the Radiation Interactions Division of NIST have announced the discovery that beta radiation-induced excited electrons are trapped in the hydroxyapatite mineral of bone and provide a potential direct dosimetric method for marrow dose when combined with routine bone marrow (and included bone) biopsies. The overall research plan sets the hypothesis that reduced morbidity marrow ablation can be successfully followed by bone marrow transplantation (BMT) with autologous marrow purged in vitro by antibody-targeted alpha emitters

  5. 25 CFR 166.814 - How will the BIA determine the value of the products or property illegally used or removed?

    Science.gov (United States)

    2010-04-01

    ... the BIA determine the value of the products or property illegally used or removed? We will determine the value of the products or property illegally used or removed based upon a valuation of similar... property illegally used or removed? 166.814 Section 166.814 Indians BUREAU OF INDIAN AFFAIRS, DEPARTMENT OF...

  6. Advance of activities report of the contract CFE-PLV/166/90. Second four-monthly; Reporte de avance de actividades del contrato CFE-PLV/166/90. Segundo cuatrimestre

    Energy Technology Data Exchange (ETDEWEB)

    Perusquia C, R.; Alonso V, G.; Hernandez M, J.L.; Montes T, J.L. [ININ, 52045 Ocoyoacac, Estado de Mexico (Mexico)

    1992-09-15

    In this report a relationship of finished activities of the Global Program of Fuel Management inside the reactor carried out by the ININ under the contract ININ/CFE 1990-1991 (CFE-PLV/166/90) is presented. Those areas of activities are: 1. Nuclear Data Bank area. 2. Static Simulation of the Reactor area. 3. Reload Optimization area. 4. Analysis of Transitory Events of the Reactor area. (Author)

  7. Mobile spine chordoma: results of 166 patients from the AOSpine Knowledge Forum Tumor database.

    Science.gov (United States)

    Gokaslan, Ziya L; Zadnik, Patricia L; Sciubba, Daniel M; Germscheid, Niccole; Goodwin, C Rory; Wolinsky, Jean-Paul; Bettegowda, Chetan; Groves, Mari L; Luzzati, Alessandro; Rhines, Laurence D; Fisher, Charles G; Varga, Peter Pal; Dekutoski, Mark B; Clarke, Michelle J; Fehlings, Michael G; Quraishi, Nasir A; Chou, Dean; Reynolds, Jeremy J; Williams, Richard P; Kawahara, Norio; Boriani, Stefano

    2016-04-01

    A chordoma is an indolent primary spinal tumor that has devastating effects on the patient's life. These lesions are chemoresistant, resistant to conventional radiotherapy, and moderately sensitive to proton therapy; however, en bloc resection remains the preferred treatment for optimizing patient outcomes. While multiple small and largely retrospective studies have investigated the outcomes following en bloc resection of chordomas in the sacrum, there have been few large-scale studies on patients with chordomas of the mobile spine. The goal of this study was to review the outcomes of surgically treated patients with mobile spine chordomas at multiple international centers with respect to local recurrence and survival. This multiinstitutional retrospective study collected data between 1988 and 2012 about prognosis-predicting factors, including various clinical characteristics and surgical techniques for mobile spine chordoma. Tumors were classified according to the Enneking principles and analyzed in 2 treatment cohorts: Enneking-appropriate (EA) and Enneking-inappropriate (EI) cohorts. Patients were categorized as EA when the final pathological assessment of the margin matched the Enneking recommendation; otherwise, they were categorized as EI. Descriptive statistics were used to summarize the data (Student t-test, chi-square, and Fisher exact tests). Recurrence and survival data were analyzed using Kaplan-Meier survival curves, log-rank tests, and multivariate Cox proportional hazard modeling. A total of 166 patients (55 female and 111 male patients) with mobile spine chordoma were included. The median patient follow-up was 2.6 years (range 1 day to 22.5 years). Fifty-eight (41%) patients were EA and 84 (59%) patients were EI. The type of biopsy (p mobile spine.

  8. Advance of activities report of the contract CFE-PLV/166/90. Second four-monthly

    International Nuclear Information System (INIS)

    Perusquia C, R.; Alonso V, G.; Hernandez M, J.L.; Montes T, J.L.

    1992-09-01

    In this report a relationship of finished activities of the Global Program of Fuel Management inside the reactor carried out by the ININ under the contract ININ/CFE 1990-1991 (CFE-PLV/166/90) is presented. Those areas of activities are: 1. Nuclear Data Bank area. 2. Static Simulation of the Reactor area. 3. Reload Optimization area. 4. Analysis of Transitory Events of the Reactor area. (Author)

  9. Impedance Characterization of the Capacitive field-Effect pH-Sensor Based on a thin-Layer Hafnium Oxide Formed by Atomic Layer Deposition

    Directory of Open Access Journals (Sweden)

    Michael LEE

    2014-05-01

    Full Text Available As a sensing element, silicon dioxide (SiO2 has been applied within ion-sensitive field effect transistors (ISFET. However, a requirement of increasing pH-sensitivity and stability has observed an increased number of insulating materials that obtain high-k gate being applied as FETs. The increased high-k gate reduces the required metal oxide layer and, thus, the fabrication of thin hafnium oxide (HfO2 layers by atomic layer deposition (ALD has grown with interest in recent years. This metal oxide presents advantageous characteristics that can be beneficial for the advancements within miniaturization of complementary metal oxide semiconductor (CMOS technology. In this article, we describe a process for fabrication of HfO2 based on ALD by applying water (H2O as the oxygen precursor. As a first, electrochemical impedance spectroscopy (EIS measurements were performed with varying pH (2-10 to demonstrate the sensitivity of HfO2 as a potential pH sensing material. The Nyquist plot demonstrates a high clear shift of the polarization resistance (Rp between pH 6-10 (R2 = 0.9986, Y = 3,054X + 12,100. At acidic conditions (between pH 2-10, the Rp change was small due to the unmodified oxide gate (R2 = 0.9655, Y = 2,104X + 4,250. These preliminary results demonstrate the HfO2 substrate functioned within basic to neutral conditions and establishes a great potential for applying HfO2 as a dielectric material for future pH measuring FET sensors.

  10. Synergistic effect of carbon nanotube as sintering aid and toughening agent in spark plasma sintered molybdenum disilicide-hafnium carbide composite

    Energy Technology Data Exchange (ETDEWEB)

    Mukherjee, Biswajyoti; Asiq Rahman, O.S.; Sribalaji, M [Materials Science and Engineering, Indian Institute of Technology Patna, Bihta Kanpa Road, Bihta, Patna, Bihar 801103 (India); Bakshi, Srinivasa Rao [Department of Metallurgical and Materials Engineering, Indian Institute of Technology Madras, Chennai 600036 (India); Keshri, Anup Kumar, E-mail: anup@iitp.ac.in [Materials Science and Engineering, Indian Institute of Technology Patna, Bihta Kanpa Road, Bihta, Patna, Bihar 801103 (India)

    2016-12-15

    Hafnium carbide (HfC) along with sintering aids was consolidated at a relatively lower temperature i.e. 1600 °C (i.e. T=~0.41 T{sub m}) under a uniaxial load of 50 MPa by spark plasma sintering. Two different sintering aids such as molybdenum disilicide (MoSi{sub 2}) and carbon nanotube (CNT) were added to enhance the densification and lower the extent of grain growth in the sintered pellets. Density of the sintered pellet increased from 96.0±0.8% in HfC +5 wt% MoSi{sub 2} (HM) to 99.0±0.5% with the addition of 2 wt% CNT in HfC+5 wt% MoSi{sub 2} (HMC) at sintering temperature of 1600 °C. Further, the extent of grain growth drastically reduced from 204% in HM to 50% in HMC. Analysis of linear shrinkage during densification revealed that CNT addition increased densification rate and decreased the time required to reach the density of 99.0±0.5% at 1600 °C. Increased densification and lower degree of grain growth could be due to the synergistic effect offered by the CNT, which are as follows: (i) Lubrication effect of CNT, (ii) Lower activation energy for grain boundary diffusion (iii) Reduction in liquid phase sintering temperature and (iv) Grain boundary pinning. Fracture toughness of the sintered HM and HMC composite was obtained using indentation technique. By the addition of 2 wt% CNT in HM, drastic increase of 91% in fracture toughness was seen. This significant improvement in fracture toughness was due to the enhanced densification and relatively lower grain size of HMC. Also crack bridging, crack deflection, crack arrest, CNT and graphene sheet pull-out and swording played major role in toughening of HMC pellet.

  11. Technical Note: A simulation study on the feasibility of radiotherapy dose enhancement with calcium tungstate and hafnium oxide nano- and microparticles.

    Science.gov (United States)

    Sherck, Nicholas J; Won, You-Yeon

    2017-12-01

    To assess the radiotherapy dose enhancement (RDE) potential of calcium tungstate (CaWO 4 ) and hafnium oxide (HfO 2 ) nano- and microparticles (NPs). A Monte Carlo simulation study was conducted to gauge their respective RDE potentials relative to that of the broadly studied gold (Au) NP. The study was warranted due to the promising clinical and preclinical studies involving both CaWO 4 and HfO 2 NPs as RDE agents in the treatment of various types of cancers. The study provides a baseline RDE to which future experimental RDE trends can be compared to. All three materials were investigated in silico with the software Penetration and Energy Loss of Positrons and Electrons (PENELOPE 2014) developed by Francesc Salvat and distributed in the United States by the Radiation Safety Information Computational Center (RSICC) at Oak Ridge National Laboratory. The work utilizes the extensively studied Au NP as the "gold standard" for a baseline. The key metric used in the evaluation of the materials was the local dose enhancement factor (DEF loc ). An additional metric used, termed the relative enhancement ratio (RER), evaluates material performance at the same mass concentrations. The results of the study indicate that Au has the strongest RDE potential using the DEF loc metric. HfO 2 and CaWO 4 both underperformed relative to Au with lower DEF loc of 2-3 × and 4-100 ×, respectively. The computational investigation predicts the RDE performance ranking to be: Au > HfO 2 > CaWO 4 . © 2017 American Association of Physicists in Medicine.

  12. Feasibility of Endovascular Radiation Therapy Using Holmium-166 Filled Balloon Catheter in a Swine Hemodialysis Fistula Model: Preliminary Results

    Energy Technology Data Exchange (ETDEWEB)

    Won, Jong Yun; Lee, Kwang Hun; Lee, Do Yun [Dept. of Radiology, Research Institute of Radiological Science, Yensei University College of Medicine, Seoul (Korea, Republic of); Kim, Myoung Soo [Dept. of Radiology, Yensei University College of Medicine, Seoul (Korea, Republic of); Kang, Byung Chul [Dept. of Radiology, Internal Medicine, EwhaWoman' s University School of Medicine, Seoul (Korea, Republic of); Kim, Seung Jung [Dept. of Internal Medicine, EwhaWoman' s University School of Medicine, Seoul (Korea, Republic of)

    2011-08-15

    To describe how to make a swine hemodialysis fistula model and report our initial experience to test the feasibility of endovascular radiation therapy with Holmium-166 filled balloon catheters. The surgical formation of arterio-venous fistula (AVF) was performed by end-to-side anastomosis of the bilateral jugular vein and carotid artery of 6 pigs. After 4 weeks, angiograms were taken and endovascular radiation was delivered to the venous side of AVF with Holmium-166 filled balloon catheters. Pigs were sacrificed 4 weeks after the radiation and AVFs were harvested for histological examination. All animals survived without any morbidity during the experimental periods. The formation of fistula on the sides of necks was successful in 11 of the 12 pigs (92%). One AVF failed from the small jugular vein. On angiograms, 4 of the 11 AVFs showed total occlusion or significant stenosis and therefore, endovascular radiation could not be performed. Of 7 eligible AVFs, five underwent successful endovascular radiation and two AVFs did not undergo radiation for the control. Upon histologic analysis, one non-radiated AVF showed total occlusion and others showed intimal thickening from the neointimal hyperplasia. Formation of the swine carotid artery-jugular vein hemodialysis fistula model was successful. Endovascular radiation using a Holmium-166 filled balloon catheter was safe and feasible.

  13. Plant phenolics and absorption features in vegetation reflectance spectra near 1.66 μm

    Science.gov (United States)

    Kokaly, Raymond F.; Skidmore, Andrew K

    2015-01-01

    Past laboratory and field studies have quantified phenolic substances in vegetative matter from reflectance measurements for understanding plant response to herbivores and insect predation. Past remote sensing studies on phenolics have evaluated crop quality and vegetation patterns caused by bedrock geology and associated variations in soil geochemistry. We examined spectra of pure phenolic compounds, common plant biochemical constituents, dry leaves, fresh leaves, and plant canopies for direct evidence of absorption features attributable to plant phenolics. Using spectral feature analysis with continuum removal, we observed that a narrow feature at 1.66 μm is persistent in spectra of manzanita, sumac, red maple, sugar maple, tea, and other species. This feature was consistent with absorption caused by aromatic C-H bonds in the chemical structure of phenolic compounds and non-hydroxylated aromatics. Because of overlapping absorption by water, the feature was weaker in fresh leaf and canopy spectra compared to dry leaf measurements. Simple linear regressions of feature depth and feature area with polyphenol concentration in tea resulted in high correlations and low errors (% phenol by dry weight) at the dry leaf (r2 = 0.95, RMSE = 1.0%, n = 56), fresh leaf (r2 = 0.79, RMSE = 2.1%, n = 56), and canopy (r2 = 0.78, RMSE = 1.0%, n = 13) levels of measurement. Spectra of leaves, needles, and canopies of big sagebrush and evergreens exhibited a weak absorption feature centered near 1.63 μm, short ward of the phenolic compounds, possibly consistent with terpenes. This study demonstrates that subtle variation in vegetation spectra in the shortwave infrared can directly indicate biochemical constituents and be used to quantify them. Phenolics are of lesser abundance compared to the major plant constituents but, nonetheless, have important plant functions and ecological significance. Additional research is needed to advance our understanding of the

  14. Evaluation of the therapeutic effect of hydroxyapatite particles labeled with Ho166 in rats with acute and chronic arthritis

    International Nuclear Information System (INIS)

    Mendoza Lopez, Patricia

    2002-01-01

    The therapeutic effect of an intraarticular injection of hydroxyapatite particles labeled with Holmium-166 ( Ho 166 HA) was evaluated. For this evaluation 72 antigen-induced arthritis rats; the arthritis was induced by an intraarticular injection of a suspension of ovoalbumin and Freund's adjuvant complete. The 72 rats were divided in three groups: control group, acute arthritis group and chronic arthritis group. The evaluation of the therapeutic effect was achieved by the measuring of the perimeter of the arthritic knee joint in different days after the intraarticular injection of 0,5 μCi of Ho 166 -HA (day 0, 4, 9, 14, 19, 30). Also a biological distribution study was done at 4, 24 and 48 hours in different organs, through the counting of its radiation. The results of the biological distribution showed that a very high percent of the injected activity remains inside the joint, with minimal activity in other organs, which indicates that the extra articular leakage is very low. The evaluation of the articular perimeter, demonstrated that Ho 166 -HA has a therapeutic effect , which was shown by comparing the control group (6.42 ±0.43 cm right knee; 6.14 ±0.31 cm left knee) with the acute arthritis group (5.11 ±0.3 cm right knee; 4.95 ±0.39 cm left knee) with significantly statistical values (p≤0,01); also the control group was compared with the chronic arthritis group (5.6 ±0.56 cm right knee; 5.47 ±0.51 cm left knee), with significantly statistical values (p≤0,01). This therapeutic effect was evident too when evaluating the measure of the articular perimeter in acute and chronic arthritis groups through the time with significantly statistical values (p≤0,01). In conclusion the hydroxyapatite particles labeled with Holmium-166 are biologically stable in vivo and have a therapeutic effect in the treatment of acute and chronic arthritis in rats [es

  15. Experimental and clinical studies on the intraarterial injection of holmium-166 chitosan complex in the treatment of hepatocellular carcinoma

    International Nuclear Information System (INIS)

    Lee, Jong Tae; Kim, Eun Kyung; Won, Jong Yoon; Lee, Do Yun; Lee, Jong Doo; Yoo, Hyung Sik; Yoo, Nae Choon; Park, Kyung Bae

    2001-01-01

    The purposes of this study were to evaluate the biodistribution and effect of Ho-166 radionuclide by intra-arterial injection of the Ho-166 chitosan complex in dogs and to assess the clinical efficacy and side effects of this complex in the treatment of hepatocellular carcinoma (HCC). In an experimental study, 20 mCi of Ho-166 chitosan complex was injected into the left hepatic artery of six adult dogs. The distribution of radioactivity in each organ was calculated using a gamma camera scan at regular intervals. A beta ray radioactivity count (cpm) of blood and urine was performed periodically, and hematologic and hepatic function were regularly assessed. At 4, 8 and 12 weeks after intra-arterial injection, bone marrow and liver were pathologically evaluated. Twenty-five patients with a single, nodular HCC mass 3-9 cm in diameter were treated by intra-arterial injection of Ho-166 chitosan complex, and immediately after the procedure a gamma camera scan was obtained. A beta ray radioactivity count(CPM) of blood was performed periodically, hematologic and hepatic function were regularly evaluated, and CT scans and angiograms were obtained 3 months after the procedure. On the basis of the CT and angiographic findings, the treatment effects were classified as complete (CR), partial (PR) or non-response(NR). In the animal study, blood radioactivity peaked immediately in each organ per whole body was 25% in the left lobe of the liver, 7% in the right lobe, 3% in the lung, 1.4-3% in the bladder, and 2% in bone. WBC and platelet counts declined maximally at 3-4 weeks and recovered at 12 weeks the cellularity of bone marrow was 25% at 4 weeks and 55% at 12 weeks, findings which correlated well with the observed hematologic changes. In the clinical study of 25 HCC patients, CR was achieved in 17 (68%) cases, PR in 5 (20%) and NR in 3 (12%). At gamma camera imaging immediately after treatment, tumor radioactivity was localized in 76% of cases. In six cases (24%) WBC and

  16. Thermodynamic and kinetic studies in the systems alkali chloride-zinconium (or hafnium) tetrachloride: Part I. Vapour pressure measurements over hexachloro compounds and use of vapour pressure data in fractional decomposition

    International Nuclear Information System (INIS)

    Ray, H.S.; Bhat, B.G.; Reddy, G.S.; Biswas, A.K.

    1978-01-01

    A molten tin isoteniscope has been used to measure the vapour pressures over ZrCl 4 , HfCl 4 and the hexachlore zirconates (M 2 ZrCl 6 ) and the hexachloro hafnates (M 2 HfCl 6 ) of four alkali metals (M = Na,K,Rb,Cs). The method of preparation of these compounds and the effect of small amounts of residual alkali chlorides on the their vapour pressure are discussed. The pressure-temperature plots are examined in the light of some theoretical postulates. A scheme for separation of hafnium from zirconoium by multistage fractional decomposition of the hexachlore compounds of any alkali metal is described. The scheme, which is analogous to rectification in liquid-vapour systems, employs a countercurrent flow of Zr(Hf)Cl 4 in a gas stream and a moving bed of alkali chlorides. The separation is based on the difference in the dissociation equilibrium for zirconium and hafnium compounds. Stage calculations for such a scheme and the main conclusions of a computational work are presented. (author)

  17. Gastro-duodenal perforations: conventional plain film, US and CT findings in 166 consecutive patients

    International Nuclear Information System (INIS)

    Grassi, Roberto; Romano, Stefania; Pinto, Antonio; Romano, Luigia

    2004-01-01

    Introduction: Gastro-duodenal perforations may be suspected in patients with history of ulceration, who present with acute pain and abdominal wall rigidity, but radiological findings in these cases may be unable to confirm a clinical diagnosis. The aim of our study was to report our experience in the diagnosis of gastro-duodenal perforation by conventional radiography, US and CT examinations. Material and methods: We retrospectively reviewed medical records of 166 consecutive patients who presented in the last 2 years to our institutions with symptoms of acute abdomen and submitted to surgery at the Emergency Unit of the ''A.Cardarelli'' Hospital of Naples with a surgical finding of perforated gastro-duodenal ulcer. The evidence of free intraperitoneal air on abdominal plain film was considered as a direct or suggestive finding of perforation. Evidence of intraperitoneal free fluid and/or reduced intestinal peristalsis at sonographic examination were considered indirect signs of gastro-duodenal perforation. Evidence of free peritoneal gas at CT was considered as a direct evidence of gastro-duodenal perforation. Results: Twenty patients underwent immediate surgery with no preoperative imaging evaluation, in 10 of them the site of perforation was found in a juxta-pyloric region and in the others at level of duodenum. In 146 patients submitted to serial radiological investigations before surgery, the site of perforation was in 56 (38.3%) duodenal, in 52 (35.6%) juxta-pyloric, in 28 (19.1%) gastric and in 10 (6.8%) pyloric. The cause of perforation was in all cases gastric or duodenal ulceration, in seven cases involving pancreatic parenchyma. In 110 (75.4%) patients with direct findings of perforation, in 94 cases (85.5%) the correct diagnosis was established on abdominal plain film, in two (1.8%) with radiographic and sonographic examinations and in 14 (12.7%) on CT findings. In 36 (24,6%) patients with no direct findings of perforation, only 24 (16,4%) of them

  18. Gastro-duodenal perforations: conventional plain film, US and CT findings in 166 consecutive patients

    Energy Technology Data Exchange (ETDEWEB)

    Grassi, Roberto; Romano, Stefania E-mail: stefromano@libero.it; Pinto, Antonio; Romano, Luigia

    2004-04-01

    Introduction: Gastro-duodenal perforations may be suspected in patients with history of ulceration, who present with acute pain and abdominal wall rigidity, but radiological findings in these cases may be unable to confirm a clinical diagnosis. The aim of our study was to report our experience in the diagnosis of gastro-duodenal perforation by conventional radiography, US and CT examinations. Material and methods: We retrospectively reviewed medical records of 166 consecutive patients who presented in the last 2 years to our institutions with symptoms of acute abdomen and submitted to surgery at the Emergency Unit of the ''A.Cardarelli'' Hospital of Naples with a surgical finding of perforated gastro-duodenal ulcer. The evidence of free intraperitoneal air on abdominal plain film was considered as a direct or suggestive finding of perforation. Evidence of intraperitoneal free fluid and/or reduced intestinal peristalsis at sonographic examination were considered indirect signs of gastro-duodenal perforation. Evidence of free peritoneal gas at CT was considered as a direct evidence of gastro-duodenal perforation. Results: Twenty patients underwent immediate surgery with no preoperative imaging evaluation, in 10 of them the site of perforation was found in a juxta-pyloric region and in the others at level of duodenum. In 146 patients submitted to serial radiological investigations before surgery, the site of perforation was in 56 (38.3%) duodenal, in 52 (35.6%) juxta-pyloric, in 28 (19.1%) gastric and in 10 (6.8%) pyloric. The cause of perforation was in all cases gastric or duodenal ulceration, in seven cases involving pancreatic parenchyma. In 110 (75.4%) patients with direct findings of perforation, in 94 cases (85.5%) the correct diagnosis was established on abdominal plain film, in two (1.8%) with radiographic and sonographic examinations and in 14 (12.7%) on CT findings. In 36 (24,6%) patients with no direct findings of perforation, only 24

  19. Production, quality control, biodistribution assessment and preliminary dose evaluation of {sup 166}Ho-alendronate as a bone marrow ablative agent

    Energy Technology Data Exchange (ETDEWEB)

    Fakhari, Ashraf [Tehran University of Medical Sciences (Iran, Islamic Republic of). Dept. of Radiopharmacy; Jalilian, Amir Reza; Yousefnia, Hassan; Zolghadri, Samaneh; Samani, Ali Bahrami; Akbari, Mahmoud Reza; Deha, Fariba Johari [Nuclear Science and Technology Research Institute (NSTRI), Tehran (Iran, Islamic Republic of); Shafiee-Ardestani, Mahdi; Khalaj, Ali [Tehran University of Medical Sciences (Iran, Islamic Republic of). Dept. of Medicinal Chemistry

    2015-07-01

    In this study, production, quality control and biodistribution studies of {sup 166}Ho-alendronate have been presented and followed by dosimetric evaluation for human based on biodistribution data in wild-type rats. {sup 166}Ho chloride was obtained by thermal neutron irradiation of natural {sup 165}Ho(NO{sub 3}){sub 3} samples. {sup 166}Ho-alendronate complex was prepared by adding the desired amount of alkaline alendronate solution (0.2 mL, 150 mg/mL) to 3-5 mCi of the {sup 166}HoCl{sub 3} solution. Radiochemical purity of the complex was monitored by instant thin layer chromatography (ITLC). {sup 166}Ho-alendronate complex was prepared in high radiochemical purity (> 99%, ITLC) and specific activity of 4.4 GBq/mmol. Stability studies of the complex in the final preparation and in the presence of human serum were performed up to 48 h. The major accumulation of the radio-complex was in the bone tissues followed by absorbed dose evaluation of each human organ by RADAR software used for modelling the radiation dose delivered. The final preparation was administered to wild-type rats and biodistribution of the complex was performed 2-48 h post injection showing major accumulation of the complex in the bone tissue. The highest absorbed dose for {sup 166}Ho-alendronate is observed in bone surface and red marrow with 2.670 and 1.880 mSv/MBq; respectively. These findings suggest that {sup 166}Ho-alendronate has considerable characteristics compared to {sup 166}Ho-DOTMP and can be a possible candidate for bone marrow ablation in patients with multiple myeloma.

  20. Production of microspheres labeled with holmium-166 for liver cancer therapy: the preliminary experience at IPEN/CNEN-SP

    International Nuclear Information System (INIS)

    Costa, Renata F.; Azevedo, Mariangela B.M.; Nascimento, Nanci; Sene, Frank F.; Martinelli, Jose R.; Osso Junior, Joao A.

    2009-01-01

    Microspheres labeled with therapeutic radionuclides for malignancies of liver are widely used in many countries. The internal radionuclide therapy uses a permanently implanted device, such as Therasphere R or SIR-Spheres R , or a biodegradable device that provides structural support for the radionuclide of choice and causes the tumor reduction. Three different types of material supports have been investigated, i.e., biodegradable polymer-based, glass-based and resin-based microspheres. Nowadays there is a project concerning the labeling of these 3 materials with 166 Ho being developed at IPEN-CNEN/SP and coordinated by the Radiopharmacy Directory. 166 Ho(t 1/2 =26.8 h) is a beta minus emitter (E max =1.84 MeV), with right properties for radiotherapy and can be produced with the low power Brazilian Nuclear Reactor IEA-R1m. The aim of this work is to describe the stage of development of this project. The initial experience used resin-based microspheres, a cation exchange resin labeled with 166 Ho, it showed the essential characteristics for liver therapy. Preliminary results of the preparation of glass-based microspheres labeled with 165 Ho showed that 5% of Ho 2 O 3 was incorporated in an aluminosilicate glass, through the process of spheronization by flame, which produced spherical microspheres with 20-40μm particle size. The preparation of biodegradable material, polymer-based microspheres, is in its initial stage and the objective is to prepare and label with 165 Ho different polymer-based microspheres. These combined efforts have been done to offer a national radiotherapeutic product for the the Brazilian nuclear medicine community at fair value and also to offer a viable possibility of treatment for patients affected by liver malignancies. (author)

  1. Production of microspheres labeled with holmium-166 for liver cancer therapy: the preliminary experience at IPEN/CNEN-SP

    Energy Technology Data Exchange (ETDEWEB)

    Costa, Renata F.; Azevedo, Mariangela B.M.; Nascimento, Nanci; Sene, Frank F.; Martinelli, Jose R.; Osso Junior, Joao A., E-mail: renatafcosta@usp.b [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

    2009-07-01

    Microspheres labeled with therapeutic radionuclides for malignancies of liver are widely used in many countries. The internal radionuclide therapy uses a permanently implanted device, such as Therasphere{sup R} or SIR-Spheres{sup R}, or a biodegradable device that provides structural support for the radionuclide of choice and causes the tumor reduction. Three different types of material supports have been investigated, i.e., biodegradable polymer-based, glass-based and resin-based microspheres. Nowadays there is a project concerning the labeling of these 3 materials with {sup 166}Ho being developed at IPEN-CNEN/SP and coordinated by the Radiopharmacy Directory. {sup 166}Ho(t{sub 1/2}=26.8 h) is a beta minus emitter (E{sub max}=1.84 MeV), with right properties for radiotherapy and can be produced with the low power Brazilian Nuclear Reactor IEA-R1m. The aim of this work is to describe the stage of development of this project. The initial experience used resin-based microspheres, a cation exchange resin labeled with {sup 166}Ho, it showed the essential characteristics for liver therapy. Preliminary results of the preparation of glass-based microspheres labeled with {sup 165}Ho showed that 5% of Ho{sub 2}O{sub 3} was incorporated in an aluminosilicate glass, through the process of spheronization by flame, which produced spherical microspheres with 20-40mum particle size. The preparation of biodegradable material, polymer-based microspheres, is in its initial stage and the objective is to prepare and label with {sup 165}Ho different polymer-based microspheres. These combined efforts have been done to offer a national radiotherapeutic product for the the Brazilian nuclear medicine community at fair value and also to offer a viable possibility of treatment for patients affected by liver malignancies. (author)

  2. Evolution of E 2 transition strength in deformed hafnium isotopes from new measurements on 172Hf,174Hf, and 176Hf

    Science.gov (United States)

    Rudigier, M.; Nomura, K.; Dannhoff, M.; Gerst, R.-B.; Jolie, J.; Saed-Samii, N.; Stegemann, S.; Régis, J.-M.; Robledo, L. M.; Rodríguez-Guzmán, R.; Blazhev, A.; Fransen, Ch.; Warr, N.; Zell, K. O.

    2015-04-01

    Background: The available data for E 2 transition strengths in the region between neutron-deficient hafnium and platinum isotopes are far from complete. More and precise data are needed to enhance the picture of structure evolution in this region and to test state-of-the-art nuclear models. In a simple model, the maximum collectivity is expected at the middle of the major shell. However, for actual nuclei, particularly in heavy-mass regions, which should be highly complex, this picture may no longer be the case, and one should use a more realistic nuclear-structure model. We address this point by studying the spectroscopy of Hf as a representative case. Purpose: We remeasure the 21+ half-lives of 172,174,176Hf, for which there is some disagreement in the literature. The main goal is to measure, for the first time, the half-lives of higher-lying states of the rotational band. The new results are compared to a theoretical calculation for absolute transition strengths. Method: The half-lives were measured using γ -γ and conversion-electron-γ delayed coincidences with the fast timing method. For the determination of half-lives in the picosecond region, the generalized centroid difference method was applied. For the theoretical calculation of the spectroscopic properties, the interacting boson model is employed, whose Hamiltonian is determined based on microscopic energy-density functional calculations. Results: The measured 21+ half-lives disagree with results from earlier γ -γ fast timing measurements, but are in agreement with data from Coulomb excitation experiments and other methods. Half-lives of the 41+ and 61+ states were measured, as well as a lower limit for the 81+ states. Conclusions: This work shows the importance of a mass-dependent effective boson charge in the interacting boson model for the description of E 2 transition rates in chains of nuclei. It encourages further studies of the microscopic origin of this mass dependence. New experimental

  3. Augmented growth inhibition of B16-BL6 melanoma by combined treatment with a selective matrix metalloproteinase inhibitor, MMI-166, and cytotoxic agents.

    Science.gov (United States)

    Hojo, Kanji; Maki, Hideo; Sawada, Takuko Yamada; Maekawa, Ryuji; Yoshioka, Takayuki

    2002-01-01

    MMI-166 is a selective matrix metalloproteinase (MMP) inhibitor. The purpose of this study was to evaluate the antitumor efficacy of the combined treatment of MMI-166 with paclitaxel or carboplatin. Mice bearing B16-BL6 melanoma were treated p.o. with MMI-166 from 1 day after tumor inoculation. The mice were administered i.v. with either paclitaxel or carboplatin at the maximum tolerated dose (MTD). MMI-166 monotherapy inhibited in vivo growth of the B16-BL6 tumor to an extent similar to that of paclitaxel or carboplatin monotherapy. When MMI-166 was combined with paclitaxel or carboplatin, the antitumor efficacy was significantly (p B16-BL6 tumor cells nor does it augment the cytotoxicity of paclitaxel or carboplatin. These results indicate that augmented antitumor activity of the combination treatment was not simply due to the augmentation of direct cytotoxic activity, but was rather an additive effect of the antitumor activities of different mechanisms. They suggest the effectiveness of a combination therapy of MMI-166 with paclitaxel or carboplatin in clinical therapy.

  4. Corrective Action Investigation Plan for Corrective Action Unit 166: Storage Yards and Contaminated Materials, Nevada Test Site, Nevada

    International Nuclear Information System (INIS)

    David Strand

    2006-01-01

    Corrective Action Unit 166 is located in Areas 2, 3, 5, and 18 of the Nevada Test Site, which is 65 miles northwest of Las Vegas, Nevada. Corrective Action Unit (CAU) 166 is comprised of the seven Corrective Action Sites (CASs) listed below: (1) 02-42-01, Cond. Release Storage Yd - North; (2) 02-42-02, Cond. Release Storage Yd - South; (3) 02-99-10, D-38 Storage Area; (4) 03-42-01, Conditional Release Storage Yard; (5) 05-19-02, Contaminated Soil and Drum; (6) 18-01-01, Aboveground Storage Tank; and (7) 18-99-03, Wax Piles/Oil Stain. These sites are being investigated because existing information on the nature and extent of potential contamination is insufficient to evaluate and recommend corrective action alternatives. Additional information will be obtained by conducting a corrective action investigation (CAI) before evaluating corrective action alternatives and selecting the appropriate corrective action for each CAS. The results of the field investigation will support a defensible evaluation of viable corrective action alternatives that will be presented in the Corrective Action Decision Document. The sites will be investigated based on the data quality objectives (DQOs) developed on February 28, 2006, by representatives of the Nevada Division of Environmental Protection; U.S. Department of Energy, National Nuclear Security Administration Nevada Site Office; Stoller-Navarro Joint Venture; and Bechtel Nevada. The DQO process was used to identify and define the type, amount, and quality of data needed to develop and evaluate appropriate corrective actions for CAU 166. Appendix A provides a detailed discussion of the DQO methodology and the DQOs specific to each CAS. The scope of the CAI for CAU 166 includes the following activities: (1) Move surface debris and/or materials, as needed, to facilitate sampling. (2) Conduct radiological surveys. (3) Perform field screening. (4) Collect and submit environmental samples for laboratory analysis to determine if

  5. Deleterious effects on MDAMB-231 breast adenocarcinoma cell lineage submitted to Ho-166 radioactive seeds at very low activity

    Energy Technology Data Exchange (ETDEWEB)

    Falcao, Patricia L.; Campos, Tarcisio P.R., E-mail: campos@nuclear.ufmg.br [Universidade Federal de Minas Gerais (UFMG), Belo Horizonte, MG (Brazil). Dept. de Engenharia Nuclear; Sarmento, Eduardo V. [Centro de Desenvolvimento de Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil); Cuperschmid, Ethel M. [Universidade Federal de Minas Gerais (CEMEMOR/UFMG), Belo Horizonte, BR (Brazil). Fac. de Medicina. Centro de Memoria da Medicina

    2011-07-01

    Herein, the deleterious effect of ionizing radiation provided by Ho-166 radioactive seeds at low activity were addressed, based on experimental in vitro assays at the MDA MB231 cell lineage, a breast adenocarcinoma, compared to PBMC - peripheral blood cells. The methodology involves of the MDBMB-231 and PBMC expansion in culture in suitable environment in 30mm well plates and T-25 flasks. Seeds were synthesized with Ho-165 incorporated and characterized previously. Activation was processed at IPR1 reactor at the peripheral table, at 8h exposition. Three groups of seeds were tested: 0,34 mCi, 0,12 mCi activity, and control group. Such seeds were placed on culture and held to a period of 05 half-lives of the radionuclide. The biological responses at these exposure were documented by inverse microscopic photographic in time. Also, MTT essay were performed. A fast response in producing deleterious effects at cancer cell was observed even if for the low activity seeds. Also, a biological response dependent to a radial distance of the seed was observed. At conclusion, viability clonogenic control of MDAMB231 is identified at the exposition to Ho-166 ceramic seeds, even if at low activity of 0,1 to 0,3mCi. (author)

  6. Deleterious effects on MDAMB-231 breast adenocarcinoma cell lineage submitted to Ho-166 radioactive seeds at very low activity

    International Nuclear Information System (INIS)

    Falcao, Patricia L.; Campos, Tarcisio P.R.; Cuperschmid, Ethel M.

    2011-01-01

    Herein, the deleterious effect of ionizing radiation provided by Ho-166 radioactive seeds at low activity were addressed, based on experimental in vitro assays at the MDA MB231 cell lineage, a breast adenocarcinoma, compared to PBMC - peripheral blood cells. The methodology involves of the MDBMB-231 and PBMC expansion in culture in suitable environment in 30mm well plates and T-25 flasks. Seeds were synthesized with Ho-165 incorporated and characterized previously. Activation was processed at IPR1 reactor at the peripheral table, at 8h exposition. Three groups of seeds were tested: 0,34 mCi, 0,12 mCi activity, and control group. Such seeds were placed on culture and held to a period of 05 half-lives of the radionuclide. The biological responses at these exposure were documented by inverse microscopic photographic in time. Also, MTT essay were performed. A fast response in producing deleterious effects at cancer cell was observed even if for the low activity seeds. Also, a biological response dependent to a radial distance of the seed was observed. At conclusion, viability clonogenic control of MDAMB231 is identified at the exposition to Ho-166 ceramic seeds, even if at low activity of 0,1 to 0,3mCi. (author)

  7. Targeting of liver tumour in rats by selective delivery of holmium-166 loaded microspheres: a biodistribution study

    Energy Technology Data Exchange (ETDEWEB)

    Nijsen, F.; Rook, D.; Zonnenberg, B.; Klerk, J. de; Rijk, P. van; Schip, F. van het [Dept. of Nuclear Medicine, University Medical Center, Utrecht (Netherlands); Brandt, C. [Animal Inst., Utrecht Univ. (Netherlands); Meijer, R. [Dept. of Radiology, Univ. Medical Center, Utrecht (Netherlands); Dullens, H. [Dept. of Pathology, Univ. Medical Center, Utrecht (Netherlands); Hennink, W. [Dept. of Pharmaceutics, Utrecht Univ. (Netherlands)

    2001-06-01

    Intra-arterial administration of beta-emitting particles that become trapped in the vascular bed of a tumour and remain there while delivering high doses, represents a unique approach in the treatment of both primary and metastatic liver tumours. Studies on selective internal radiation therapy of colorectal liver metastases using yttrium-90 glass microspheres have shown encouraging results. This study describes the biodistribution of 40-{mu}m poly lactic acid microspheres loaded with radioactive holmium-166, after intra-arterial administration into the hepatic artery of rats with implanted liver tumours. Radioactivity measurements showed >95% retention of injected activity in the liver and its resident tumour. The average activity detected in other tissues was {<=}0.1%ID/g, with incidental exceptions in the lungs and stomach. Very little {sup 166}Ho activity was detected in kidneys (<0.1%ID/g), thereby indicating the stability of the microspheres in vivo. Tumour targeting was very effective, with a mean tumour to liver ratio of 6.1{+-}2.9 for rats with tumour (n=15) versus 0.7{+-}0.5 for control rats (n=6; P<0.001). These ratios were not significantly affected by the use of adrenaline. Histological analysis showed that five times as many large (>10) and medium-sized (4-9) clusters of microspheres were present within tumour and peritumoural tissue, compared with normal liver. Single microspheres were equally dispersed throughout the tumour, as well as normal liver parenchyma. (orig.)

  8. Epidermal growth factor receptor inhibitor PKI-166 governs cardiovascular protection without beneficial effects on the kidney in hypertensive 5/6 nephrectomized rats.

    Science.gov (United States)

    Ulu, Nadir; Mulder, Gemma M; Vavrinec, Peter; Landheer, Sjoerd W; Duman-Dalkilic, Basak; Gurdal, Hakan; Goris, Maaike; Duin, Marry; van Dokkum, Richard P E; Buikema, Hendrik; van Goor, Harry; Henning, Robert H

    2013-06-01

    Transactivation of epidermal growth factor receptor (EGFR) signaling by G protein-coupled receptors has been implicated in several cardiovascular (CV) conditions, including hypertension, heart failure, and cardiac and vascular hypertrophy. However, the therapeutic potential of EGFR inhibition in these conditions is currently unknown. The main objective of the present study was to investigate cardiac, vascular, and renal effects of EGFR inhibition by 4-[4-[[(1R)-1-phenylethyl]amino]-7H-pyrrolo[2,3-d]pyrimidin-6-yl]phenol (PKI-166) in the hypertensive chronic kidney disease model. Rats underwent 5/6 nephrectomy (5/6Nx) and were treated with PKI-166, lisinopril or vehicle from week 6 after disease induction until week 12. Sham animals received either PKI-166 or vehicle. Treatment with PKI-166 did not affect the development of the characteristic renal features in 5/6Nx, including proteinuria, diminished creatinine clearance, and increased glomerulosclerosis, whereas these were attenuated by lisinopril. Despite absence of effects on progressive renal damage, PKI-166 attenuated the progression of hypertension and maintained cardiac function (left ventricle end-diastolic pressure) to a similar extent as lisinopril. Also, PKI-166 attenuated the increase in phosphorylated EGFR in the heart as induced by 5/6Nx. Moreover, PKI-166 and lisinopril restored the impaired contraction of isolated thoracic aortic rings to phenylephrine and angiotensin II and impaired myogenic constriction of small mesenteric arteries in 5/6Nx rats. Blockade of the EGFR displays a CV benefit independent of limiting the progression of renal injury. Our findings extend the evidence on EGFR signaling as a target in CV disorders.

  9. 6-Peroxo-6-zirconium crown and its hafnium analogue embedded in a triangular polyanion: [M6(O2)6(OH)6(gamma-SiW10O36)3]18- (M = Zr, Hf).

    Science.gov (United States)

    Bassil, Bassem S; Mal, Sib Sankar; Dickman, Michael H; Kortz, Ulrich; Oelrich, Holger; Walder, Lorenz

    2008-05-28

    We have synthesized and structurally characterized the unprecedented peroxo-zirconium(IV) containing [Zr6(O2)6(OH)6(gamma-SiW10O36)3]18- (1). Polyanion 1 comprises a cyclic 6-peroxo-6-zirconium core stabilized by three decatungstosilicate units. We have also prepared the isostructural hafnium(IV) analogue [Hf6(O2)6(OH)6(gamma-SiW10O36)3]18- (2). We investigated the acid/base and redox properties of 1 by UV-vis spectroscopy and electrochemistry studies. Polyanion 1 represents the first structurally characterized Zr-peroxo POM with side-on, bridging peroxo units. The simple, one-pot synthesis of 1 and 2 involving dropwise addition of aqueous hydrogen peroxide could represent a general procedure for incorporating peroxo groups into a large variety of transition metal and lanthanide containing POMs.

  10. Hafnium and neodymium isotopes and REY distribution in the truly dissolved, nanoparticulate/colloidal and suspended loads of rivers in the Amazon Basin, Brazil

    Science.gov (United States)

    Merschel, Gila; Bau, Michael; Schmidt, Katja; Münker, Carsten; Dantas, Elton L.

    2017-09-01

    Radiogenic isotopes in river sediments and river waters have been widely used in provenance studies, as these samples naturally integrate the geology/chemistry of the entire catchment. While the Hf and Nd isotope systems are coupled during igneous processes, they are decoupled during supergene processes at the Earth's surface, which is reflected by the isotope composition of riverine sediments. We present the first data for both Hf and Nd isotope compositions of the dissolved (0.2 μm-filtrates rich in nanoparticles and colloids, NPCs) and the truly dissolved (1 kDa-ultrafiltrates) load of rivers. Hafnium and Nd isotope compositions and concentrations of the Rare Earths and Yttrium (REY) and Hf were determined for suspended particles (>0.2 μm) as well as for the dissolved and the truly dissolved load of the Rio Solimões, the Amazon's largest tributary draining the Andes, and of the Rio Negro, an organic NPC- and particle-rich river draining the rainforest of northern Amazonia. We also analyzed the Nd isotope compositions of suspended sediments and 0.2 μm-filtered water samples from the Amazon River and its tributaries Rio Tapajos, Rio Xingu and Rio Jari. Our novel results clearly show that the decoupling of the Hf and Nd isotope systems is related to incongruent weathering processes on the continent, as this decoupling can already be observed in the different Hf and Nd pools, i.e. in the particulate, the NPC-dominated dissolved and the truly dissolved load of rivers. In the Rio Negro and Rio Solimões, a strong particle size-dependent difference in Hf isotope composition is observed. Values of εHf become more radiogenic as filter poresize decreases, which can be related to the density- and size-dependent distribution of Hf-rich minerals, e.g. zircons, and their absence from the truly dissolved pool. In contrast, the Nd isotope composition of Amazonian river waters reflects that of their catchment geology. Tributaries draining the Precambrian Brazilian and

  11. A comparison of conventional and computer-assisted semen analysis (CRISMAS software) using samples from 166 young Danish men

    DEFF Research Database (Denmark)

    Vested, Anne; Ramlau-Hansen, Cecilia; Bonde, Jens P

    2011-01-01

    The aim of the present study was to compare assessments of sperm concentration and sperm motility analysed by conventional semen analysis with those obtained by computer-assisted semen analysis (CASA) (Copenhagen Rigshospitalet Image House Sperm Motility Analysis System (CRISMAS) 4.6 software......) using semen samples from 166 young Danish men. The CRISMAS software identifies sperm concentration and classifies spermatozoa into three motility categories. To enable comparison of the two methods, the four motility stages obtained by conventional semen analysis were, based on their velocity...... classifications, divided into three stages, comparable to the three CRISMAS motility categories: rapidly progressive (A), slowly progressive (B) and non-progressive (C+D). Differences between the two methods were large for all investigated parameters (P sperm concentration...

  12. Optical vector network analysis of ultranarrow transitions in 166Er3+ : 7LiYF4 crystal.

    Science.gov (United States)

    Kukharchyk, N; Sholokhov, D; Morozov, O; Korableva, S L; Cole, J H; Kalachev, A A; Bushev, P A

    2018-02-15

    We present optical vector network analysis (OVNA) of an isotopically purified Er166 3+ :LiYF 4 7 crystal. The OVNA method is based on generation and detection of a modulated optical sideband by using a radio-frequency vector network analyzer. This technique is widely used in the field of microwave photonics for the characterization of optical responses of optical devices such as filters and high-Q resonators. However, dense solid-state atomic ensembles induce a large phase shift on one of the optical sidebands that results in the appearance of extra features on the measured transmission response. We present a simple theoretical model that accurately describes the observed spectra and helps to reconstruct the absorption profile of a solid-state atomic ensemble as well as corresponding change of the refractive index in the vicinity of atomic resonances.

  13. Analytic Electron Trajectories in an Extremely Relativistic Helical Wiggler an Application to the Proposed SLAC E166 Experiment.

    CERN Document Server

    ThomasDonohue, John

    2004-01-01

    The proposed experiment SLAC E166 intends to generate circularly polarized gamma rays of energy 10 MeV by passing a 15 GeV electron beam through a meter long wiggler with approximately 400 periods. Using an analytic model formulated by Rullier and me, I present calculations of electron trajectories. At this extremely high energy the trajectories are described quite well by the model, and an extremely simple picture emerges, even for trajectories that that fail to encircle the axis of the wiggler. Our calculations are successfully compared with standard numerical integration of the Lorentz force equations of motion. In addition, the calculation of the spectrum and angular distribution of the radiated photons is easily carried out.

  14. Radioactive metallic stent for palliative treatment of esopageal cancer using Ho-166: an experimental study in canine model

    Energy Technology Data Exchange (ETDEWEB)

    Won, J. H.; Lee, J. D. [College of Medicine, Yonsei Univ., Seoul (Korea, Republic of); Wang, H. J.; Lim, H. E.; Park, C. H. [College of Medicine, Ajou Univ., Inchon (Korea, Republic of); Park, K. B. [KAERI, Taejon (Korea, Republic of)

    1999-07-01

    Self-expandable metallic stents are widely used for palliative treatment of esophageal cancer, however, tumor overgrowth and short survaval limit its long-term effect. The purpose of this study is to evaluate tissue response of the radiation effect in normal canine esophagus whether metallic stents coated with radioactive H-166 is effective for patients survival and preservation of stent patency longer than stents without radioactive materials. Ho-166 was incorporated within polyurethan (50{mu}) and coated over the outer surface of self-expandable metallic stents. Metallic stents with radioactivity of 4.0-7.8mCi (Group A), 1.0-1.8 mCi (Group B) and 0.5-0.7mCi (Group C) were placed in normal mid-esophagus in twelve dogs (Group A), five (Group B) and another five dogs (Group C) respectively, and the stents were tightly anchored by surgery to prevent migration. Estimated radiation dose was 6-70 Gy in Group C. Fluoroscopy confirmed stents in esophagus without migration for at least two days. The dogs were sacrified at two or three months later and histopathologic examinations were performed. In group A, mid-esophagus stricture, mucosal ulceration were found in all specimens. Severe fibrosis and degeneration of muscular propria, upper one half were found in three and complete fibrosis of esophageal wall, however, esophageal perforation was found but muscular layer was intact. In group C, no histological changes was demonstrated in three but submucosal inflammation with intact mucosa in two. In therapeutic dose level (group B), radioactive metallic stent showed radiation effect within esophageal wall without complication which might give additional palliative effect in malignant espohageal stricture.

  15. Purification of a 166mHo solution by successive high-performance liquid chromatography and gravitational chromatography for half-life determination

    International Nuclear Information System (INIS)

    Florence Gueguen; Helene Isnard; Carole Bresson; Celine Caussignac; Guillaume Stadelmann; Anthony Nonell; Sebastien Mialle; Karsten Kossert; Frederic Chartier

    2014-01-01

    A methodology to purify a 166m Ho solution has been developed by a combination of activity and mass concentration measurements in order to further determine the 166m Ho half-life. The isobaric interference at m/q ≃ 166 requires Ho purification from non-natural Er with a high purification degree due to the large amount of Ho as opposed to Er. The Ho/Er separation was achieved using high-performance liquid chromatography on a semi-preparative column followed by purification on gravitational chromatography. The efficiency of the separation was evaluated after precise determination of the Er isotopic composition. The purification methodology enabled to separate Ho from Er. (author)

  16. Zirconium Zr and hafnium Hf

    International Nuclear Information System (INIS)

    Busev, A.I.; Tiptsova, V.G.; Ivanov, V.M.

    1978-01-01

    The basic methods for extracting and determining Zr(4) and Hf(4) are described. Diantipyrinemethane and its alkyl homologs selectively extract Zr and Hf from HNO 3 solutions in the presence of nitrates. Zr is selectively extracted with tetraethyldiamide of heptyl phosphoric acid (in benzene) as well as with 2-thenoyltrifluoroacetone (in an acid). The latter reagents is suitable for rapid determination of 95 Zr in a mixture with 95 Nb and other fragments. The complexometric determination of Zr is based on formation of a stable complex of Zr with EDTA. The titration is carried out in the presence of n-sulfobenzene-azo-pyrocatechol, eriochrome black T. The determination is hindered by Hf, fluoride-, phosphate-, oxalate- and tartrate-ions. The method is used for determining Zr in zircon and eudialyte ore. Zr is determined photometrically with the aid of xylenol orange, arsenazo 3 and pyrocatechol violet (in phosphorites). Hf is determined in the presence of Zr photometrically with the aid of xylenol orange or methyl-thymol blue. The method is based on Zr being masked with hydrogen peroxide in the presence of sulfate-ions

  17. Cathodoluminescence of Irradiated Hafnium Dioxide

    Science.gov (United States)

    2011-03-01

    Martin and Michael Rhoby for their hard work in fixing assorted problems that cropped up during the course of my thesis work. Emily A. Purcell...Cathodoluminescence Microscopy of Inorganic Solids. New York: Plenum Press, 1990. [13] D. Drouin, A. R. Couture, D. Joly , X. Tastet, V. Aimez and R. Gauvin

  18. Alkali metal hafnium oxide scintillators

    Science.gov (United States)

    Bourret-Courchesne, Edith; Derenzo, Stephen E.; Taylor, Scott Edward

    2018-05-08

    The present invention provides for a composition comprising an inorganic scintillator comprising an alkali metal hafnate, optionally cerium-doped, having the formula A2HfO3:Ce; wherein A is an alkali metal having a valence of 1, such as Li or Na; and the molar percent of cerium is 0% to 100%. The alkali metal hafnate are scintillators and produce a bright luminescence upon irradiation by a suitable radiation.

  19. Studies on the production and utilization of radioisotopes - Treatment of= skin cancer with Ho-166 skin patch in an animal model

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jae Rok [Korea Atomic Energy Research Institute, Taejon (Korea, Republic of); Lee, Jong Doo [Yonsei University, Seoul (Korea, Republic of)

    1995-07-01

    Skin cancers were developed in 8 ICR mice and 2 hairless mice by topical application of chemical compound (TDA and NPO) for 35 wks. Specially designed= Ho-166 skin patches were applied over the skin cancer for 1-2 hrs to deliver 8000 rads to the tumors. Complete, destruction of tumors as well as regeneration of epithelium were observed after the treatment. In conclusion, Ho-166 patch is a useful treatment modality in superficial skin cancers. 10 refs., 4 tabs., 4 figs. (author)

  20. Corrective Action Decision Document for Corrective Action Unit 166: Storage Yards and Contaminated Materials, Nevada Test Site, Nevada with Errata Sheet

    Energy Technology Data Exchange (ETDEWEB)

    Grant Evenson

    2007-03-01

    This Corrective Action Decision Document (CADD) has been prepared for Corrective Action Unit (CAU) 166, Storage Yards and Contaminated Materials, in accordance with the Federal Facility Agreement and Consent Order (1996). The corrective action sites (CASs) are located in Areas 2, 3, 5, and 18 of the Nevada Test Site, Nevada. Corrective Action Unit 166 is comprised of the following CASs: • 02-42-01, Cond. Release Storage Yd - North • 02-42-02, Cond. Release Storage Yd - South • 02-99-10, D-38 Storage Area • 03-42-01, Conditional Release Storage Yard • 05-19-02, Contaminated Soil and Drum • 18-01-01, Aboveground Storage Tank • 18-99-03, Wax Piles/Oil Stain The purpose of this CADD is to identify and provide the rationale for the recommendation of a corrective action alternative (CAA) for the seven CASs within CAU 166. Corrective action investigation (CAI) activities were performed from July 31, 2006, through February 28, 2007, as set forth in the CAU 166 Corrective Action Investigation Plan (NNSA/NSO, 2006).

  1. Growth inhibitory effects of the dual ErbB1/ErbB2 tyrosine kinase inhibitor PKI-166 on human prostate cancer xenografts.

    Science.gov (United States)

    Mellinghoff, Ingo K; Tran, Chris; Sawyers, Charles L

    2002-09-15

    Experiments with human prostate cancer cell lines have shown that forced overexpression of the ErbB2-receptor tyrosine kinase (RTK) promotes androgen-independent growth and increases androgen receptor-transcriptional activity in a ligand-independent fashion. To investigate the relationship between ErbB-RTK signaling and androgen in genetically unmanipulated human prostate cancer, we performed biochemical and biological studies with the dual ErbB1/ErbB2 RTK inhibitor PKI-166 using human prostate cancer xenograft models with isogenic sublines reflecting the transition from androgen-dependent to androgen-independent growth. In the presence of low androgen concentrations, PKI-166 showed profound growth-inhibitory effects on tumor growth, which could be partially reversed by androgen add-back. At physiological androgen concentrations, androgen withdrawal greatly enhanced the ability of PKI-166 to retard tumor growth. The level of extracellular signal-regulated kinase activation correlated with the response to PKI-166 treatment, whereas the expression levels of ErbB1 and ErbB2 did not. These results suggest that ErbB1/ErbB2 RTKs play an important role in the biology of androgen-independent prostate cancer and provide a rationale for clinical evaluation of inhibitors targeted to this pathway.

  2. Studies on the preparation of ferric-hydroxide macro aggregate and hydroxyapatite particles labelled with Sm-153, Ho-166 and/or Dy-165 for radiation synovectomy

    International Nuclear Information System (INIS)

    Le Van So; Pham Ngoc Dien; Truong Hong Nghia; Nguyen Thi Thu; Nguyen Cong Duc; Vo Thji Cam Hoa; Bui Van Cuong

    2004-01-01

    The modified methods for the preparation of Hydroxyapatite particle (HA) and Ferric Hydroxide Macro Aggregated (FHMA of high stability and uniformity in particle size and of good geometrical shape suitable for production of radiolabeled carrier for radiation synovectomy purpose were developed. 165 Dy, 166 Ho and/or 153 Sm labeled HA and FHMA were produced using a simple labelling method. (author)

  3. 25 CFR 166.307 - Will the grazing capacity be increased if I graze adjacent trust or non-trust rangelands not...

    Science.gov (United States)

    2010-04-01

    ... § 166.307 Will the grazing capacity be increased if I graze adjacent trust or non-trust rangelands not... trust or non-trust rangeland in common with the permitted land. Grazing capacity will be established... 25 Indians 1 2010-04-01 2010-04-01 false Will the grazing capacity be increased if I graze...

  4. Brachytherapy using holmium-166 liquid balloon system for in-stent restenosis: 6 months clinical and angiographic follow-up

    Energy Technology Data Exchange (ETDEWEB)

    Kim, M. H.; Kim, S. K.; Cha, K. S.; Kim, Y. D.; Lee, H. S.; Kang, D. Y. [Donga University College of Medicine, Busan (Korea, Republic of)

    2002-07-01

    In western country, 3 systems of brachytherapy using commercial radioactive source has been established. However, brachytherapy using holmium-166 liquid balloon system (HLBS) for the patient with stent restenosis has not been studied enough. 30 patients (male 23, mean age 58.9 7.7) were enrolled. Target dose was 15 Gy at 1 mm distance from the intimal surface. Clinical diagnoses of the study patients included stable angina 10 and unstable angina 20 patients. Target lesion included LAD 19, LCx 5 and RCA 6 arteries. Pre-brachytherapy treatment included cutting balloon angioplasty in 25, rotational atherectomy in 5 patients. Fractionation and stepping was done in 6 patients each. Follow-up angiography was done in 19 patients. Of them, 4 cases developed angiographic restenosis (21%) including 3 cases of total occlusion. 6 month MACE (major adverse cardiac event) occurred in 5 patients including one sudden cardiac death in a patient with 80 year-old, triple-vessel diseased patient. Vascular brachytherapy using HLBS is a safe and effective treatment modality for in-stent restenosis showing acceptable angiographic and clinical result.

  5. Embedding of $^{163}$Ho and $^{166m}$ Ho in the energy absorbers of low temperature metallic magnetic calorimeters

    CERN Multimedia

    The calorimetric measurement of the $^{163}$Ho electron capture spectrum is a promising tool to investigate the electron neutrino mass. A suitable method to embed the source in the detectors is the ion-implantation. This process has already been used to embed $^{163}$Ho ions in micro-fabricated low temperature metallic magnetic prototypes. The $^{163}$Ho electron capture spectrum obtained with these first prototypes is presently the most precise with an energy resolution of $\\Delta$$\\textit{E}$$_{FWHM}$ = 7.6 eV. In order to test the performance of the new generation of low temperature metallic magnetic calorimeters, we propose to perform a $^{163}$Ho ion-implantation on the new chip having two arrays consisting of 32 pixels each. An activity of about 1 Bq per pixel is required. With this new detector array we will be able to achieve a better energy resolution and to acquire a higher statistics which allows for studying the $^{163}$Ho spectral shape. We propose also to perform an ion-implantation of $^{166m}$...

  6. The Concordance and Heritability of Type 2 Diabetes in 34,166 Twin Pairs From International Twin Registers

    DEFF Research Database (Denmark)

    Willemsen, G.; Ward, K. J.; Bell, C. G.

    2015-01-01

    studies worldwide need to pool their resources. The Discordant Twin (DISCOTWIN) consortium was established for this goal. Here, we describe the DISCOTWIN Consortium and present an analysis of type 2 diabetes (T2D) data in nearly 35,000 twin pairs. Seven twin cohorts from Europe (Denmark, Finland, Norway...... and medication use, fasting glucose and insulin measures, or medical records. The prevalence of T2D ranged from 2.6% to 12.3% across the cohorts depending on age, body mass index (BMI), and national diabetes prevalence. T2D discordance rate was lower for MZ (5.1%, range 2.9-11.2%) than for same-sex dizygotic (DZ......, the Netherlands, Spain, Sweden, and the United Kingdom) and one from Australia investigated the rate of discordance for T2D in same-sex twin pairs aged 45 years and older. Data were available for 34,166 same-sex twin pairs, of which 13,970 were MZ, with T2D diagnosis based on self-reported diagnosis...

  7. 166 ORIGINAL ARTICLE

    African Journals Online (AJOL)

    boaz

    This study evaluated the inhibitory effects of Phyllanthus amarus extracts on Staphylococcus aureus, Streptococcus pneumoniae,. Streptococcus pyogenes, Pseudomonas aeruginosa and Candida albicans. These effects were compared with those of ampicillin, gentamicin and pefloxacin. Phytochemical analysis showed ...

  8. Pages 166- 173.pmd

    African Journals Online (AJOL)

    Administrator

    The logistic regression model to predict neonatal mortality had a good fit (AUC: 0.8507, misclassification rate: 13.6%) ... intensive care units, principal component analysis, logistic regression, ... between cost of neonatal care and length of stay.

  9. 166Ho and 90Y labeled 6D2 monoclonal antibody for targeted radiotherapy of melanoma: Comparison with 188Re radiolabel

    International Nuclear Information System (INIS)

    Thompson, S.; Ballard, B.; Jiang, Z.; Revskaya, E.; Sisay, N.; Miller, W.H.; Cutler, C.S.; Dadachova, E.; Francesconi, L.C.

    2014-01-01

    Introduction: An approach to radioimmunotherapy (RIT) of metastatic melanoma is the targeting of melanin pigment with monoclonal antibodies (mAbs) to melanin radiolabeled with therapeutic radionuclides. The proof of principle experiments were performed using a melanin-binding antibody 6D2 of IgM isotype radiolabeled with a β emitter 188 Re and demonstrated the inhibition of tumor growth. In this study we investigated the efficacy of 6D2 antibody radiolabeled with two other longer lived β emitters 90 Y and 166 Ho in treatment of experimental melanoma, with the objective to find a possible correlation between the efficacy and half-life of the radioisotopes which possess high energy β (E max > 1.5 MeV) emission properties. Methods: 6D2 was radiolabeled with longer lived β emitters 90 Y and 166 Ho in treatment of experimental melanoma in A2058 melanoma tumor-bearing nude mice. The immunoreactivity of the radiolabeled 6D2 mAb, its in vitro binding to the MNT1 human melanoma cells, the biodistribution and therapy in A2058 human melanoma bearing nude mice as well as dosimetry calculations were performed. Results: When labeled with the longer lived 90 Y radionuclide, the 6D2 mAb did not produce any therapeutic effect in tumor bearing mice while the reduction of the tumor growth by 166 Ho-6D2 was very similar to the previously reported therapy results for 188 Re-6D2. In addition, 166 Ho-labeled mAb produced the therapeutic effect on the tumor without any toxic effects while the administration of the 90 Y-labeled radioconjugate was toxic to mice with no appreciable anti-tumor effect. Conclusions: 166 Ho-labeled mAb to melanin produced some therapeutic effect on the tumor without any toxic effects while the administration of the 90 Y-labeled radioconjugate was toxic to mice with no appreciable anti-tumor effect. We concluded that the serum half-life of the 6D2 carrier antibody matched well the physical half-life of 166 Ho to deliver the tumoricidal absorbed dose to the

  10. Population Screening and Prevention Strategies for Thalassemias and other Hemoglobinopathies of Eastern India: Experience of 18,166 cases.

    Science.gov (United States)

    Chatterjee, Tridip; Chakravarty, Amit; Chakravarty, Sudipa

    2015-01-01

    We evaluated population screening programs (1999-2011), conducted by the Thalassaemia Foundation, Kolkata, India, for the first time in Eastern India in different districts of West Bengal, for prevention of thalassemia comprising screening of heterozygotes and β-thalassemia intermedia (β-TI) cases [β(+), β(++), β(0)/β(+), β(E)/β(E) (codon 26 or HBB: c.79G > A), Hb-E-β-thalassemia (Hb E-β-thal)]. Among 18,166 cases, we found 2092 heterozygotes and 2245 β-TI individuals (who had no information about their disorders). Results were evaluated with standard hematological analyses including erythrocyte indices, hemoglobin (Hb) typing and quantification. Participants were divided into five groups (children, pre-marriage cases, pre-pregnancy cases, affected family members, pregnant women). The objectives of this evaluation were to fix cut-off values of red blood cells (RBCs), mean corpuscular volume (MCV), mean corpuscular Hb (MCH), red blood cell distribution width (RDW) and Hb A2, as the standard World Health Organization (WHO) guidelines were not strictly followed in mass-scale screening programs. We have observed many dilemmas in considering the status of the thalassemia subject, due to presence of some other clinical conditions such as iron deficiency anemia, α-thalassemia (α-thal), δ-thalassemia (δ-thal), clinically silent Hb variants, and some cases of non hemoglobinopathies (such as pregnancy) along with thalassemia. The MCV values varied greatly in different conditions of hemoglobinopathies, whereas MCH provided a more stable measurement. We found an MCH value of <27.0 pg is a suitable cut-off point for screening in this population. Participants with an MCH of <27.0 pg should be investigated further to confirm or exclude a diagnosis of β-thal trait.

  11. Activated leucocyte cell adhesion molecule (ALCAM/CD166) regulates T cell responses in a murine model of food allergy.

    Science.gov (United States)

    Kim, Y S; Kim, M N; Lee, K E; Hong, J Y; Oh, M S; Kim, S Y; Kim, K W; Sohn, M H

    2018-05-01

    Food allergy is a major public health problem. Studies have shown that long-term interactions between activated leucocyte cell adhesion molecule (ALCAM/CD166) on the surface of antigen-presenting cells, and CD6, a co-stimulatory molecule, influence immune responses. However, there are currently no studies on the functions of ALCAM in food allergy. Therefore, we aimed to identify the functions of ALCAM in ovalbumin (OVA)-induced food allergy using ALCAM-deficient mice. Wild-type (WT) and ALCAM-deficient (ALCAM -/- ) mice were sensitized intraperitoneally and with orally fed OVA. The mice were killed, and parameters related to food allergy and T helper type 2 (Th2) immune responses were analysed. ALCAM serum levels increased and mRNA expression decreased in OVA-challenged WT mice. Serum immunoglobulin (Ig)E levels, Th2 cytokine mRNA and histological injuries were higher in OVA-challenged WT mice than in control mice, and these were attenuated in ALCAM -/- mice. T cell proliferation of total cells, CD3 + CD4 + T cells and activated T cells in immune tissues were diminished in OVA-challenged ALCAM -/- mice. Proliferation of co-cultured T cells and dendritic cells (DCs) was decreased by the anti-CD6 antibody. In addition, WT mice sensitized by adoptive transfer of OVA-pulsed ALCAM -/- BM-derived DCs showed reduced immune responses. Lastly, serum ALCAM levels were higher in children with food allergy than in control subjects. In this study, serum levels of ALCAM were elevated in food allergy-induced WT mice and children with food allergy. Moreover, immune responses and T cell activation were attenuated in OVA-challenged ALCAM -/- mice. These results indicate that ALCAM regulates food allergy by affecting T cell activation. © 2018 British Society for Immunology.

  12. Cobalt(II), nickel(II), copper(II), zinc(II) and hafnium(IV) complexes of N'-(furan-3-ylmethylene)-2-(4-methoxyphenylamino)acetohydrazide.

    Science.gov (United States)

    Emam, Sanaa M; El-Saied, Fathy A; Abou El-Enein, Saeyda A; El-Shater, Heba A

    2009-03-01

    Cobalt(II), nickel(II), copper(II), zinc(II) and hafnium(IV) complexes of furan-2-carbaldehyde 4-methoxy-N-anilinoacetohydrazone were synthesized and characterized by elemental and thermal (TG and DTA) analyses, IR, UV-vis and (1)H NMR spectra as well as magnetic moment and molar conductivity. Mononuclear complexes are obtained with 1:1 molar ratio except complexes 3 and 9 which are obtained with 1:2 molar ratios. The IR spectra of ligand and metal complexes reveal various modes of chelation. The ligand behaves as a neutral bidentate one and coordination occurs via the carbonyl oxygen atom and azomethine nitrogen atom. The ligand behaves also as a monobasic tridentate one and coordination occurs through the enolic oxygen atom, azomethine nitrogen atom and the oxygen atom of furan ring. Moreover, the ligand behaves as a neutral tridentate and coordination occurs via the carbonyl oxygen, azomethine nitrogen and furan oxygen atoms as well as a monobasic bidentate and coordination occurs via the enolic oxygen atom and azomethine nitrogen atom. The electronic spectra and magnetic moment measurements reveal that all complexes possess octahedral geometry except the copper complex 10 possesses a square planar geometry. The thermal studies showed the type of water molecules involved in metal complexes as well as the thermal decomposition of some metal complexes.

  13. Determination of hafnium at the 10−4% level (relative to zirconium content) using neutron activation analysis, inductively coupled plasma mass spectrometry and inductively coupled plasma atomic emission spectrometry

    International Nuclear Information System (INIS)

    Smolik, Marek; Polkowska-Motrenko, Halina; Hubicki, Zbigniew; Jakóbik-Kolon, Agata; Danko, Bożena

    2014-01-01

    Graphical abstract: -- Highlights: •We worked out ICP-MS method of Hf determination in Zr and Zr compounds. •We used NAA method as reference one. •We obtained pure zirconium matrix by ion exchange (Diphonix ® resin). •These permit to determine ≥1 × 10 −4 % Hf in Zr sample by ICP MS with good precision and accuracy. -- Abstract: Hafnium at the very low level of 1–8 ppm (in relation to zirconium) was determined in zirconium sulfate solutions (originating from investigations of the separation of ca. 44 ppm Hf from zirconium by means of the ion exchange method) by using three independent methods: inductively coupled plasma mass spectrometry (ICP MS), neutron activation analysis (NAA) and inductively coupled plasma atomic emission spectrometry (ICP-AES). The results of NAA and ICP MS determinations were consistent with each other across the entire investigated range (the RSD of both methods did not exceed 38%). The results of ICP-AES determination were more diverse, particularly at less than 5 ppm Hf (RSD was significantly higher: 29–253%). The ion exchange method exploiting Diphonix ® resin proved sufficient efficiency in Zr–Hf separation when the initial concentration ratio of the elements ([Zr] 0 /[Hf] 0 ) ranged from 1200 to ca. 143,000

  14. Expression Levels of Activated Leukocyte Cell Adhesion Molecule (ALCAM/CD166 in Primary Breast Carcinoma and Distant Breast Cancer Metastases

    Directory of Open Access Journals (Sweden)

    M. Ihnen

    2010-01-01

    Full Text Available Introduction: Activated Leukocyte Cell Adhesion Molecule (ALCAM/CD166 gained increasing attention regarding tumorprogression and metastatic spread in breast cancer. The aim of this study was to examine ALCAM expression levels in primary breast cancer and distant metastases of the same patient within 29 autopsy cases to better understand the underlying mechanisms of metastases and the role of adhesion molecules in this process.

  15. The structure of the 168Er nucleus and the 166Er(t,p) 168 Er reaction in terms of the sdg interacting boson model

    Science.gov (United States)

    Akiyama, Y.; Heyde, K.; Arima, A.; Yoshinaga, N.

    1986-05-01

    Extending the interacting boson model by incorporating besides s and d, also the g-boson, we can describe the population of positive parity states of 168Er in the 166Er(t,P) 168Er reaction rather well. In particular, the excitation of I,Kπi = 4,3 +1; 2,2 +2; 0,0 +3 and 0,0 +4 states is much improved over the sd-IBM approach.

  16. Development of radiolabelled compound using reactor producted RI - Evaluation of Ho-166 endovascular therapy to prevent restenosis after PTCA or stenting for occlusive coronary artery disease

    Energy Technology Data Exchange (ETDEWEB)

    Park, Chan Hee; Choi, Byung Il; Kim, Han Soo [Ajou University, Suwon (Korea)

    2000-04-01

    Occlusive coronary artery disease is managed successfully by percutaneous transfemoral coronary angioplasty (PTCA) or stenting with 95% success rate. However, restenosis after PTCA is not uncommon and the reported incidence of reocclusion is about 30 {approx} 40%. Therefore, the objective of the research was to develop endovascular brachytherapy using liquid form of Ho-166 in order to inhibit neointimal hyperplasia responsible for restenosis following PTCA or stenting. Our research was carried out in 3 stages: First stage - The effectiveness of radiation was confirmed by using animal model. Following over-sized balloon injury to rat carotid artery and porcine coronary artery, various external radiation doses were delivered. Second stage - For radiation dose distribution within the coronary artery and its surrounding tissues, Gafchromic film was used. In vitro dose distribution of Ho-166 utilizing water phantom and Gafchromic film was measured. Third stage - None uniform dose distribution from Ho-166 within the balloon caused by small air bubbles was eliminated by negative suction method. More accurate dose distribution was also possible using newly developed micrometer by our physicist. Limited number of human trial was performed without adverse effect. 40 refs. (Author)

  17. Clinical trial of {sup 165}Dy-HMA and {sup 166}Ho-CHICO in the treatment of Rheumatoid knee synovitis

    Energy Technology Data Exchange (ETDEWEB)

    Kim, S. Y.; Yoo, D. H.; Bae, S. C.; Jun, J. B. [Hanyang University, Seoul (Korea, Republic of); Lim, S. M.; Hong, S. W.; Lee, S. Y.; Cheon, D. G.; Kim, S. J. [Korea Cancer Center Hospital, Seoul (Korea, Republic of)

    1997-07-01

    The untreated, chronic synovial inflammation leads to pannus formation and eventual destruction of the articular cartilage. In cases where medical therapy was unsuccessful, surgical or radiation synovectomy is necessary especially in the knee joints. The advantages of radiation synovectomy over surgical synovectomy are (1) greater destruction of diseased synovium, (2) reduced potential for blood clots and infection, (3) no requirement for anesthesia, and (4) less costly and less time consuming. Recently KAERI developed Dy-165 HMA, which was characterized by the absence of iron and a higher concentration of dysprosium. And then more recently KAERI also developed {sup 166}Ho-CHICO, which was characterized by relatively longer half-life(26.8 hr), more biological due to organic nature of chitosan, more even spatial distribution due to colloidal solution and more absorbable to synovium than Dy-165 HMA. We studied to evaluate the efficacy and safety of radiation synovectomy with Dy-165 HMA and {sup 166}Ho-CHICO in chronic rheumatoid synovitis with knee. The present study indicates that the Dy-165 HMA and {sup 166}Ho-CHICO are an effective and safe agent for radiation synovectomy. But further large scaled long-term follow up study and controlled study with steroid only are required. 15 refs. (author)

  18. Wüstite in the fusion crust of Almahata Sitta sulfide-metal assemblage MS-166: Evidence for oxygen in metallic melts

    Science.gov (United States)

    Horstmann, Marian; Humayun, Munir; Harries, Dennis; Langenhorst, Falko; Chabot, Nancy L.; Bischoff, Addi; Zolensky, Michael E.

    2013-05-01

    Meteorite fusion crusts form during the passage of a meteoroid through the Earth's atmosphere and are highly oxidized intergrowths as documented by the presence of e.g., oxides. The porous and irregular fusion crust surrounding the Almahata Sitta sulfide-metal assemblage MS-166 was found highly enriched in wüstite (Fe1-xO). Frictional heating of the outer portions of the assemblage caused partial melting of predominantly the Fe-sulfide and minor amounts of the outer Ni-rich portions of the originally zoned metal in MS-166. Along with melting significant amounts of oxygen were incorporated into the molten fusion crust and mainly FeS was oxidized and desulfurized to form wüstite. Considerable amounts of FeS were lost due to ablation, whereas the cores of the large metal grains appear largely unmelted leaving behind metal grains and surrounding wüstite-rich material (matte). Metal grains along with the surrounding matte typically form an often highly porous framework of globules interconnected with the matte. Although textures and chemical composition suggest that melting of Fe,Ni metal occurred only partially (Ni-rich rims), there is a trace elemental imprint of siderophile element partitioning influenced by oxygen in the metallic melt as indicated by the behavior of W and Ga, the two elements significantly affected by oxygen in a metallic melt. It is remarkable that MS-166 survived the atmospheric passage as troilite inclusions in iron meteorites are preferentially destroyed.

  19. Standardization of radionuclides multi-gamma emitters 166mHo and 72Ga and determination of its gamma intensities by decay

    International Nuclear Information System (INIS)

    Moreira, Denise Simoes

    2005-01-01

    In the present work, the multi-gamma emitters 166m Ho and 72 Ga have been measured by 4πβ-γ coincidence technique. The calibration system is composed of a 4π gas-flow proportional counter coupled to a pair of NaI(Tl) crystals. Both radionuclides were measured by using two gamma discrimination windows, namely (629.9 + 834.2) keV and (2201.6 + 2507.7) keV for 72 Ga and 184.4 keV and (711.7 + 830.5) keV for 166m Ho. The methodology recently developed by LMN (Laboratorio de Metrologia Nuclear) for simulating all detection processes in a 4π(β,X)-γ coincidence system by means of the Monte Carlo technique was applied to the measurements of both radionuclides, and the predict behavior extrapolation curve was compared with the experimental data. The results obtained were in good agreement within the experimental uncertainty. The emission probabilities per decay of the most intense y-ray in the decay of 166m Ho and 72 Ga were measured by means HPGe spectrometer system, which was previously calibrated with standard sources of 57 Co, 60 Co, 54 Mn, 133 Ba, 24 Na, 152E u and 241 Am previously standardized in the 4πβ-γ system. All the uncertainties evolved were treated rigorously, by means of covariance analysis. (author)

  20. An Ultrahigh Resolution Structure of TEM-1 β-Lactamase Suggests a Role for Glu166 as the General Base in Acylation

    International Nuclear Information System (INIS)

    Minasov, George; Wang, Xiaojun; Shoichet, Brian K.

    2002-01-01

    Although TEM-1 β-lactamase is among the best studied enzymes, its acylation mechanism remains controversial. To investigate this problem, the structure of TEM-1 in complex with an acylation transition-state analogue was determined at ultrahigh resolution (0.85 (angstrom)) by X-ray crystallography. The quality of the data was such as to allow for refinement to an R-factor of 9.1% and an R free of 11.2%. In the resulting structure, the electron density features were clear enough to differentiate between single and double bonds in carboxylate groups, to identify multiple conformations that are occupied by residues and loops, and to assign 70% of the protons in the protein. Unexpectedly, even at pH 8.0 where the protein was crystallized, the active site residue Glu166 is clearly protonated. This supports the hypothesis that Glu166 is the general base in the acylation half of the reaction cycle. This structure suggests that Glu166 acts through the catalytic water to activate Ser70 for nucleophilic attack on the β-lactam ring of the substrate. The hydrolytic mechanism of class A β-lactamases, such as TEM-1, appears to be symmetrical, as are the serine proteases. Apart from its mechanistic implications, this atomic resolution structure affords an unusually detailed view of the structure, dynamics, and hydrogen-bonding networks of TEM-1, which may be useful for the design of inhibitors against this key antibiotic resistance target.

  1. Inhibition of primary roots and stimulation of lateral root development in Arabidopsis thaliana by the rhizobacterium Serratia marcescens 90-166 is through both auxin-dependent and -independent signaling pathways.

    Science.gov (United States)

    Shi, Chun-Lin; Park, Hyo-Bee; Lee, Jong Suk; Ryu, Sangryeol; Ryu, Choong-Min

    2010-03-01

    The rhizobacterium Serratia marcescens strain 90-166 was previously reported to promote plant growth and induce resistance in Arabidopsis thaliana. In this study, the influence of strain 90-166 on root development was studied in vitro. We observed inhibition of primary root elongation, enhanced lateral root emergence, and early emergence of second order lateral roots after inoculation with strain 90-166 at a certain distance from the root. Using the DR5::GUS transgenic A. thaliana plant and an auxin transport inhibitor, N-1-naphthylphthalamic acid, the altered root development was still elicited by strain 90-166, indicating that this was not a result of changes in plant auxin levels. Intriguingly, indole-3-acetic acid, a major auxin chemical, was only identified just above the detection limit in liquid culture of strain 90-166 using liquid chromatography-mass spectrometry. Focusing on bacterial determinants of the root alterations, we found that primary root elongation was inhibited in seedlings treated with cell supernatant (secreted compounds), while lateral root formation was induced in seedlings treated with lysate supernatant (intracellular compounds). Further study revealed that the alteration of root development elicited by strain 90-166 involved the jasmonate, ethylene, and salicylic acid signaling pathways. Collectively, our results suggest that strain 90-166 can contribute to plant root development via multiple signaling pathways.

  2. A spanish mineral of zirconium and hafnium. Separation of the two elements by liquid-liquid extraction, using tributyl phosphate as chelating agent; Beneficio de un mineral espanol de circonio-hafnio. Separacion de ambos elementos por extraccion liquido-liquido, empleando fosfato de tributilo como agente de quelacion

    Energy Technology Data Exchange (ETDEWEB)

    Ruiz Sanchez, F; Cruz Castillo, F. de la; Fernandez Cellini, R

    1962-07-01

    The zirconium and Hafnium oxides are obtained from a Spanish mineral of zircon with an average contest of 55% in ZrO{sub 2}-HfO{sub 2}. An alkaline fusion to open the mineral, followed by a purification by crystallization as (Zr O-Hf O)Cl{sub 2} H{sub 2}O or as (Zr-Hf) (SO{sub 4}){sub 2}. 4H{sub 2}O, is used. A discussion of the best experimental conditions for opening the mineral and of the purification method is made. (Author) 45 refs.

  3. Neutron Diffraction Studies of a Class A beta-Lactamase Toho-1 E166A/R274N/R276N Triple Mutant

    International Nuclear Information System (INIS)

    Blakeley, Matthew P.; Chen, Yu; Afonine, Pavel

    2010-01-01

    beta-Lactam antibiotics have been used effectively over several decades against many types of bacterial infectious diseases. However, the most common cause of resistance to the beta-lactam antibiotics is the production of beta-lactamase enzymes that inactivate beta-lactams by rapidly hydrolyzing the amide group of the beta-lactam ring. Specifically, the class A extended-spectrum beta-lactamases (ESBLs) and inhibitor-resistant enzymes arose that were capable of hydrolyzing penicillins and the expanded-spectrum cephalosporins and monobactams in resistant bacteria, which lead to treatment problems in many clinical settings. A more complete understanding of the mechanism of catalysis of these ESBL enzymes will impact current antibiotic drug discovery efforts. Here, we describe the neutron structure of the class A, CTX-M-type ESBL Toho-1 E166A/R274N/R276N triple mutant in its apo form, which is the first reported neutron structure of a beta-lactamase enzyme. This neutron structure clearly reveals the active-site protonation states and hydrogen-bonding network of the apo Toho-1 ESBL prior to substrate binding and subsequent acylation. The protonation states of the active-site residues Ser70, Lys73, Ser130, and Lys234 in this neutron structure are consistent with the prediction of a proton transfer pathway from Lys73 to Ser130 that is likely dependent on the conformation of Lys73, which has been hypothesized to be coupled to the protonation state of Glu166 during the acylation reaction. Thus, this neutron structure is in agreement with a proposed mechanism for acylation that identifies Glu166 as the general base for catalysis.

  4. Corrective Action Investigation Plan for Corrective Action Unit 166: Storage Yards and Contaminated Materials, Nevada Test Site, Nevada, Rev. No.: 0

    Energy Technology Data Exchange (ETDEWEB)

    David Strand

    2006-06-01

    Corrective Action Unit 166 is located in Areas 2, 3, 5, and 18 of the Nevada Test Site, which is 65 miles northwest of Las Vegas, Nevada. Corrective Action Unit (CAU) 166 is comprised of the seven Corrective Action Sites (CASs) listed below: (1) 02-42-01, Cond. Release Storage Yd - North; (2) 02-42-02, Cond. Release Storage Yd - South; (3) 02-99-10, D-38 Storage Area; (4) 03-42-01, Conditional Release Storage Yard; (5) 05-19-02, Contaminated Soil and Drum; (6) 18-01-01, Aboveground Storage Tank; and (7) 18-99-03, Wax Piles/Oil Stain. These sites are being investigated because existing information on the nature and extent of potential contamination is insufficient to evaluate and recommend corrective action alternatives. Additional information will be obtained by conducting a corrective action investigation (CAI) before evaluating corrective action alternatives and selecting the appropriate corrective action for each CAS. The results of the field investigation will support a defensible evaluation of viable corrective action alternatives that will be presented in the Corrective Action Decision Document. The sites will be investigated based on the data quality objectives (DQOs) developed on February 28, 2006, by representatives of the Nevada Division of Environmental Protection; U.S. Department of Energy, National Nuclear Security Administration Nevada Site Office; Stoller-Navarro Joint Venture; and Bechtel Nevada. The DQO process was used to identify and define the type, amount, and quality of data needed to develop and evaluate appropriate corrective actions for CAU 166. Appendix A provides a detailed discussion of the DQO methodology and the DQOs specific to each CAS. The scope of the CAI for CAU 166 includes the following activities: (1) Move surface debris and/or materials, as needed, to facilitate sampling. (2) Conduct radiological surveys. (3) Perform field screening. (4) Collect and submit environmental samples for laboratory analysis to determine if

  5. Regulation of MIR165/166 by class II and class III homeodomain leucine zipper proteins establishes leaf polarity

    DEFF Research Database (Denmark)

    Merelo, Paz; Ram, Hathi; Caggiano, Monica Pia

    2016-01-01

    A defining feature of plant leaves is their flattened shape. This shape depends on an antagonism between the genes that specify adaxial (top) and abaxial (bottom) tissue identity; however, the molecular nature of this antagonism remains poorly understood. Class III homeodomain leucine zipper (HD-...... show that class III and class II HD-ZIP proteins act together to repress MIR165/166 via a conserved cis-element in their promoters. Organ morphology and tissue patterning in plants, therefore, depend on a bidirectional repressive circuit involving a set of miRNAs and its targets....

  6. The Measurement of the Evaporation Residues Excitation Functions in the Fusion Reactions 144Sm (40Ar,xn) and 166Er(40Ar,xn)

    Science.gov (United States)

    Chernysheva, E. V.; Rodin, A. M.; Belozerov, A. V.; Dmitriev, S. N.; Gulyaev, A. V.; Gulyaeva, A. V.; Itkis, M. G.; Novoselov, A. S.; Oganessian, Yu. Ts.; Salamatin, V. S.; Stepantsov, S. V.; Vedeneev, V. Yu.; Yukhimchuk, S. A.; Krupa, L.; Kliman, J.; Motycak, S.; Sivacek, I.

    2015-06-01

    The evaporation residues excitation functions for the reactions 40Ar+144Sm→184Hg and 40Ar+166Er→206Rn were measured at the energies below and above the Coulomb barrier (Elab=142-207 MeV) using a mass-separator MASHA. The experimental data were compared with theoretical calculations using a Channel Coupling Model. The influence of experimental beam energy spread on the excitation functions was taking into account. It was found that structure of xn-cross sections correlate strongly with the nuclear structure of colliding nuclei.

  7. Structure of the /sup 168/Er nucleus and the /sup 166/Er(t,p)/sup 168/Er reaction in terms of the sdg interacting boson model

    Energy Technology Data Exchange (ETDEWEB)

    Akiyama, Y.; Heyde, K.; Arima, A.; Yoshinaga, N.

    1986-05-29

    Extending the interacting boson model by incorporating besides s and d, also the g-boson, we can describe the population of positive parity states of /sup 168/Er in the /sup 166/Er(t,P)/sup 168/Er reaction rather well. In particular, the excitation of I,Ksub(i)sup(..pi..) = 4,3/sub 1//sup +/; 2,2/sub 2//sup +/; 0,0/sub 3//sup +/ and 0,0/sub 4//sup +/ states is much improved over the sd-IBM appraoch.

  8. Phenomenological descriptions of the Yrast bands in sup(160,162,164,166)Yb nuclei band crossings and moments of inertia

    International Nuclear Information System (INIS)

    El Zaiki, M.I.; Nafie, H.O.; Abd El Mageed, K.E.

    1992-01-01

    Two methods of calculations have been used to fit the previously presented data on rotationally aligned quasiparticle bands in sup(160,162,164,166)Yb. Backbendings of moment of inertia of the Yrast states can be reproduced reasonably well. The energy levels and the effective moment of inertia for both gs and s-band are calculated and compared with the experimental data. Band crossing interpretations are discussed for each nucleus. The interaction strength calculations are presented. (author). 17 refs., 7 figs., 4 tabs

  9. Design Studies for Flux and Polarization Measurements of Photons and Positrons for SLAC Proposal E166: An experiment to test polarized positron production in the FFTB (LCC-0107)

    Energy Technology Data Exchange (ETDEWEB)

    Woods, M

    2003-10-02

    We present results from design studies carried out to investigate measurements of the flux, spectrum and polarization of undulator photons for SLAC Proposal E166. A transmission Compton polarimeter is considered for measuring the photon circular polarization. We also present results for measuring the flux and spectrum of positrons produced by the undulator photons in an 0.5X{sub 0} Titanium target. And we present some considerations for use of a transmission Compton polarimeter to measure the circular polarization of bremsstrahlung photons emitted by the polarized positrons in a thin radiator.

  10. Efficient UV-emitting X-ray phosphors: octahedral Zr(PO4)6 luminescence centers in potassium hafnium-zirconium phosphates K2Hf1-xZrx(PO4)2 and KHf2(1-x)Zr2x(PO4)3

    International Nuclear Information System (INIS)

    Torardi, C.C.; Miao, C.R.; Li, J.

    2003-01-01

    Potassium hafnium-zirconium phosphates, K 2 Hf 1-x Zr x (PO 4 ) 2 and KHf 2(1-x) Zr 2x (PO 4 ) 3 , are broad-band UV-emitting phosphors. At room temperature, they have emission peak maxima at approximately 322 and 305 nm, respectively, under 30 kV peak molybdenum X-ray excitation. Both phosphors demonstrate luminescence efficiencies that make them up to ∼60% as bright as commercially available CaWO 4 Hi-Plus. The solid-state and flux synthesis conditions, and X-ray excited UV luminescence of these two phosphors are discussed. Even though the two compounds have different atomic structures, they contain zirconium in the same active luminescence environment as that found in highly efficient UV-emitting BaHf 1-x Zr x (PO 4 ) 2 . All the three materials have hafnium and zirconium in octahedral coordination via oxygen-atom corner sharing with six separate PO 4 tetrahedra. This octahedral Zr(PO 4 ) 6 moiety appears to be an important structural element for efficient X-ray excited luminescence, as are the edge-sharing octahedral TaO 6 chains for tantalate emission

  11. Differential gene expression in Xylella fastidiosa 9a5c during co-cultivation with the endophytic bacterium Methylobacterium mesophilicum SR1.6/6.

    Science.gov (United States)

    Dourado, Manuella Nóbrega; Santos, Daiene Souza; Nunes, Luiz Roberto; Costa de Oliveira, Regina Lúcia Batista da; de Oliveira, Marcus Vinicius; Araújo, Welington Luiz

    2015-12-01

    Xylella fastidiosa, the causal agent of citrus variegated chlorosis (CVC), colonizes plant xylem, reducing sap flow, and inducing internerval chlorosis, leaf size reduction, necrosis, and harder and smaller fruits. This bacterium may be transmitted from plant to plant by sharpshooter insects, including Bucephalogonia xanthopis. The citrus endophytic bacterium Methylobacterium mesophilicum SR1.6/6 colonizes citrus xylem and previous studies showed that this strain is also transferred from plant to plant by B. xanthopis (Insecta), suggesting that this endophytic bacterium may interact with X. fastidiosa in planta and inside the insect vector during co-transmission by the same insect vector. To better understand the X. fastidiosa behavior in the presence of M. mesophilicum, we evaluated the X. fastidiosa transcriptional profile during in vitro interaction with M. mesophilicum SR1.6/6. The results showed that during co-cultivation, X. fastidiosa down-regulated genes related to growth and up-regulated genes related to energy production, stress, transport, and motility, suggesting the existence of a specific adaptive response to the presence of M. mesophilicum in the culture medium. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  12. Risk factors associated with short-term outcome and development of perioperative complications in dogs undergoing surgery because of gastric dilatation-volvulus: 166 cases (1992-2003).

    Science.gov (United States)

    Beck, Jennifer J; Staatz, Andrew J; Pelsue, Davyd H; Kudnig, Simon T; MacPhail, Catriona M; Seim, Howard B; Monnet, Eric

    2006-12-15

    To evaluate risk factors associated with death and development of perioperative complications in dogs undergoing surgery for treatment of gastric dilatation-volvulus (GDV). Retrospective case series. 166 dogs. Records of dogs with confirmed GDV that underwent surgery were reviewed. Logistic regression was performed to identify factors associated with development of complications (ie, hypotension, arrhythmias, gastric necrosis necessitating gastrectomy, disseminated intravascular coagulation, peritonitis, sepsis, postoperative dilatation, postoperative vomiting, and incisional problems) and with short-term outcome (ie, died vs survived to the time of suture removal). Short-term mortality rate was 16.2% (27/166). Risk factors significantly associated with death prior to suture removal were clinical signs for > 6 hours prior to examination, combined splenectomy and partial gastrectomy, hypotension at any time during hospitalization, peritonitis, sepsis, and disseminated intravascular coagulation. Partial gastrectomy was not a significant risk factor for death but was for peritonitis, disseminated intravascular coagulation, sepsis, and arrhythmias. Age, gastrectomy, and disseminated intravascular coagulation were risk factors for development of hypotension. Use of a synthetic colloid or hypertonic saline solution was associated with a significantly decreased risk of hypotension. Results suggest that the prognosis for dogs undergoing surgery because of GDV is good but that certain factors are associated with an increased risk that dogs will develop perioperative complications or die.

  13. EXAMINATION OF THE MASS-DEPENDENT Li DEPLETION HYPOTHESIS BY THE Li ABUNDANCES OF THE VERY METAL-POOR DOUBLE-LINED SPECTROSCOPIC BINARY G166-45

    International Nuclear Information System (INIS)

    Aoki, Wako; Ito, Hiroko; Tajitsu, Akito

    2012-01-01

    The Li abundances of the two components of the very metal-poor ([Fe/H] –2.5) double-lined spectroscopic binary G166-45 (BD+26°2606) are determined separately based on high-resolution spectra obtained with the Subaru Telescope High Dispersion Spectrograph and its image slicer. From the photometric colors and the mass ratio, the effective temperatures of the primary and secondary components are estimated to be 6350 ± 100 K and 5830 ± 170 K, respectively. The Li abundance of the primary (A(Li) = 2.23) agrees well with the Spite plateau value, while that of the secondary is slightly lower (A(Li) = 2.11). Such a discrepancy of the Li abundances between the two components is previously found in the extremely metal-poor, double-lined spectroscopic binary CS 22876-032; however, the discrepancy in G166-45 is much smaller. The results agree with the trends found for Li abundance as a function of effective temperature (and of stellar mass) of main-sequence stars with –3.0 eff ∼ 5800 K is not particularly large in this metallicity range. The significant Li depletion found in CS 22876-032B is a phenomenon only found in the lowest metallicity range ([Fe/H] < –3).

  14. INFRACŢIUNILE PREVĂZUTE LA ART.164 ŞI 166 CP RM: ASPECTE TEORETICE ŞI PRACTICE

    Directory of Open Access Journals (Sweden)

    Sergiu BRÎNZA

    2015-11-01

    Full Text Available Analiza efectuată în cadrul acestui articol are ca obiect caracteristicile juridico-penale ale infracţiunilor specificate la art.164 şi 166 CP RM. Se argumentează că, în cazul infracţiunii specificate la art.164 CP RM, constrângerea fizică se poate concretiza în: 1 vătămarea intenţionată gravă, medie sau uşoară a integrităţii corporale ori a sănătăţii; 2 violenţa care nu implică un prejudiciu cauzat sănătăţii. În continuare, se arată că oricare din tipurile de arme menţionate în Legea privind regimul armelor şi al muniţiilor cu destinaţie civilă pot fi aplicate ca mijloace de săvârşire a infracţiunii prevă-zute la lit.g alin.(2 art.164 CP RM. Or, legiuitorul nu a stabilit nicio limitare a tipurilor de arme ce pot fi aplicate la răpirea unei persoane. Contează doar ca armele să fie utilizabile în vederea anihilării unei persoane. Nu în ultimul rând, în legătură cu infracţiunile prevăzute la art.166 CP RM, se relevă că, în condiţiile Republicii Moldova, care se confruntă cu fenomenul separatismului, restrângerea libertăţii persoanei are un caracter ilegal şi atunci când este exercitată de autorităţile neconstituţionale care controlează partea de est a ţării.THE OFFENCES REFERRED TO AT ART.164. AND 166 PC RM: THEORETICAL AND PRACTICAL ASPECTS The analysis performed in this article covers the legal-penal characteristics of the offences specified in art.164 and 166 PC RM. It is argued that, with regard to the offence specified in art.164 PC RM, the physical constraint may result in: 1 intentional grave, ordinary or easy battery or health harm; 2 violence without any health harm. Further, it is shown that any of the types of weapons mentioned in Law on weapons and ammunition destined for civil usage can be applied as means of committing the offence referred to at lett.g par.(2 art.164 PC RM. Or, the legislature did not set any limitation on the types of weapons that can be

  15. Investigation of the two-quasiparticle bands in the doubly-odd nucleus 166Ta using a particle-number conserving cranked shell model

    Science.gov (United States)

    Zhang, ZhenHua

    2016-07-01

    The high-spin rotational properties of two-quasiparticle bands in the doubly-odd 166Ta are analyzed using the cranked shell model with pairing correlations treated by a particle-number conserving method, in which the blocking effects are taken into account exactly. The experimental moments of inertia and alignments and their variations with the rotational frequency hω are reproduced very well by the particle-number conserving calculations, which provides a reliable support to the configuration assignments in previous works for these bands. The backbendings in these two-quasiparticle bands are analyzed by the calculated occupation probabilities and the contributions of each orbital to the total angular momentum alignments. The moments of inertia and alignments for the Gallagher-Moszkowski partners of these observed two-quasiparticle rotational bands are also predicted.

  16. Job strain and tobacco smoking: an individual-participant data meta-analysis of 166,130 adults in 15 European studies.

    Directory of Open Access Journals (Sweden)

    Katriina Heikkilä

    Full Text Available Tobacco smoking is a major contributor to the public health burden and healthcare costs worldwide, but the determinants of smoking behaviours are poorly understood. We conducted a large individual-participant meta-analysis to examine the extent to which work-related stress, operationalised as job strain, is associated with tobacco smoking in working adults.We analysed cross-sectional data from 15 European studies comprising 166,130 participants. Longitudinal data from six studies were used. Job strain and smoking were self-reported. Smoking was harmonised into three categories never, ex- and current. We modelled the cross-sectional associations using logistic regression and the results pooled in random effects meta-analyses. Mixed effects logistic regression was used to examine longitudinal associations. Of the 166,130 participants, 17% reported job strain, 42% were never smokers, 33% ex-smokers and 25% current smokers. In the analyses of the cross-sectional data, current smokers had higher odds of job strain than never-smokers (age, sex and socioeconomic position-adjusted odds ratio: 1.11, 95% confidence interval: 1.03, 1.18. Current smokers with job strain smoked, on average, three cigarettes per week more than current smokers without job strain. In the analyses of longitudinal data (1 to 9 years of follow-up, there was no clear evidence for longitudinal associations between job strain and taking up or quitting smoking.Our findings show that smokers are slightly more likely than non-smokers to report work-related stress. In addition, smokers who reported work stress smoked, on average, slightly more cigarettes than stress-free smokers.

  17. Coulomb excitation of /sup 182/ /sup 184/ /sup 186/W and /sup 166/Er with /sup 4/He and /sup 16/O ions

    Energy Technology Data Exchange (ETDEWEB)

    McGowan, F K; Milner, W T; Sayer, R O; Robinson, R L; Stelson, P H [Oak Ridge National Lab., Tenn. (USA)

    1977-10-10

    The Coulomb excitation reaction induced by /sup 4/He ions selectively excites 2/sup +/ and 3/sup -/ states by direct E2 and E3 Coulomb excitation. In this paper, new results are presented from ..gamma..-ray spectroscopy with 15 MeV /sup 4/He ions on a natural abundance target of W. In particular, a 3/sup -/ state in each isotope, /sup 182/ /sup 184/ /sup 186/W, was observed by direct E3 excitation. In addition to obtaining B(Elambda, 0 ..-->.. J = lambda for excitation of each state, information on the reduced transition probabilities for the different decay modes of these states is given. The Coulomb excitation probabilities of the 2'/sup +/ states at 786 keV in /sup 166/Er and at 737 keV in /sup 186/W were measured with /sup 16/O and /sup 4/He ions by the backscattered particle-gamma coincidence method in order to determine the static electric quadrupole moment Qsub(2'). For /sup 166/Er, Qsub(2')=2.11+-0.37 e.b which is in agreement with (Qsub(2'))sub(rot) and for /sup 186/W, Qsub(2')=1.17+-0.30 e.b which is in agreement with Kumar-Baranger model calculations and is significantly smaller than (Qsub(2'))sub(rot). This deviation of the measured Qsub(2') from (Qsub(2'))sub(rot) implies in the framework of the Kumar-Baranger calculations a strong coupling between ..beta..- and ..gamma..-vibrational bands. On the other hand, the observed upper limit for B(E2, 2'' ..-->.. 2') does not confirm this implication.

  18. Molecular gas in the H II-region complex RCW 166: Possible evidence for an early phase of cloud-cloud collision prior to the bubble formation

    Science.gov (United States)

    Ohama, Akio; Kohno, Mikito; Fujita, Shinji; Tsutsumi, Daichi; Hattori, Yusuke; Torii, Kazufumi; Nishimura, Atsushi; Sano, Hidetoshi; Yamamoto, Hiroaki; Tachihara, Kengo; Fukui, Yasuo

    2018-05-01

    Young H II regions are an important site for the study of O star formation based on distributions of ionized and molecular gas. We reveal that two molecular clouds at ˜48 km s-1 and ˜53 km s-1 are associated with the H II regions G018.149-00.283 in RCW 166 by using the JCMT CO High-Resolution Survey (COHRS) of the 12CO(J = 3-2) emission. G018.149-00.283 comprises a bright ring at 8 μm and an extended H II region inside the ring. The ˜48 km s-1 cloud delineates the ring, and the ˜53 km s-1 cloud is located within the ring, indicating a complementary distribution between the two molecular components. We propose a hypothesis that high-mass stars within G018.149-00.283 were formed by triggering during cloud-cloud collision at a projected velocity separation of ˜5 km s-1. We argue that G018.149-00.283 is in an early evolutionary stage, ˜0.1 Myr after the collision according to the scheme detailed by Habe and Ohta (1992, PASJ, 44, 203), which will be followed by a bubble formation stage like RCW 120. We also suggest that nearby H II regions N21 and N22 are candidates for bubbles possibly formed by cloud-cloud collision. Inoue and Fukui (2013, ApJ, 774, L31) showed that the interface gas becomes highly turbulent and realizes a high-mass accretion rate of 10-3-10-4 M⊙ yr-1 by magnetohydrodynamical numerical simulations, which offers an explanation of the O-star formation. The fairly high frequency of cloud-cloud collision in RCW 166 is probably due to the high cloud density in this part of the Scutum arm.

  19. Passive behaviour of zirconium, hafnium and niobium

    International Nuclear Information System (INIS)

    Hornkjoel, S.

    1990-01-01

    The paper deals mainly with the results of stationary and transient polarization measurements together with capacitance measurements on passive electrodes of Zr, Hf and Nb over the entire pH-scale. The passive current densities are exstremely low, and essentially both pH and potential independent, exept for Nb at high pH. The extrapolated potential of zero inverse capacitance seems to be different from the extrapolated potential of zero film thickness for Zr and Hf, but not for Nb. The potential versus time curves at constant current show a downwards bending for Zr and Hf. It is shown that the pitting potentials of Zr and Hf are dependent of the concentration of halide ions and the type of halide ion, but not on pH. It is also shown that the pitting induction is second-order stimulated by chloride ions and first-order hindered by sulphate ions. Results from electron transfer reactions on passive niobium are reported. 9 refs

  20. Nanomechanical properties of hafnium nitride coating

    International Nuclear Information System (INIS)

    Chen Yao; Laha, Tapas; Balani, Kantesh; Agarwal, Arvind

    2008-01-01

    Nanomechanical properties of plasma-sprayed HfN coating with and without hot isostatic pressing (HIP) treatment were evaluated using nanoindentation. For HIPed HfN coating, the elastic modulus (E) and yield strength increase whereas the hardness (H), H/E ratio and fraction of the elastic work decrease. HIPed HfN coating shows a larger pile-up around the indent as compared to as-sprayed HfN. HIPing causes densification and improvement in inter-splat bonding which subsequently lead to increase in nanomechanical properties

  1. High-pressure torsion of hafnium

    International Nuclear Information System (INIS)

    Edalati, Kaveh; Horita, Zenji; Mine, Yoji

    2010-01-01

    Pure Hf (99.99%) is processed by high-pressure torsion (HPT) under pressures of 4 and 30 GPa to form an ultrafine-grained structure with a gain size of ∼180 nm. X-ray diffraction analysis shows that, unlike Ti and Zr, no ω phase formation is detected after HPT processing even under a pressure of 30 GPa. A hydride formation is detected after straining at the pressure of 4 GPa. The hydride phase decomposes either by application of a higher pressure as 30 GPa or by unloading for prolong time after HPT processing. Microhardness, tensile and bending tests show that a high hardness (360 Hv) and an appreciable ductility (8%) as well as high tensile and bending strength (1.15 and 2.75 GPa, respectively) are achieved following the high-pressure torsion.

  2. Early enriched environment exposure protects spatial memory and accelerates amyloid plaque formation in APP(Swe/PS1(L166P mice.

    Directory of Open Access Journals (Sweden)

    Francesca Montarolo

    Full Text Available Enriched environment exposure improves several aspects of cognitive performance in Alzheimer's disease patients and in animal models and, although the role of amyloid plaques is questionable, several studies also assessed their response to enriched environment, with contrasting results. Here we report that rearing APP(Swe/PS1(L166P mice in an enriched environment since birth rescued the spatial memory impairment otherwise present at 6 months of age. At the same time, the exposure to the enriched environment caused a transient acceleration of plaque formation, while there was no effect on intracellular staining with the 6E10 antibody, which recognizes β-amyloid, full length amyloid precursor protein and its C-terminal fragments. The anticipation of plaque formation required exposure during early development, suggesting an action within critical periods for circuits formation. On the other hand, chronic neuronal activity suppression by tetrodotoxin decreased the number of plaques without affecting intracellular amyloid. These results indicate that enriched environment exposure since early life has a protective effect on cognitive deterioration although transiently accelerates amyloid deposition. In addition, the effects of the enriched environment might be due to increased neuronal activity, because plaques were reduced by suppression of electrical signaling by tetrodotoxin.

  3. Determination of the biodistribution and biokinetics of radiopharmaca like 166Ho-ferric-hydroxide or 153Sm-EDTMP used for therapeutic treatment by energy dispersive measurements

    International Nuclear Information System (INIS)

    Fischer, H.; Poljanc, K.; Aiginger, H.; Pruefert, U.; Granegger, S.; Ofluoglu, S.; Pirich, Ch.; Sinzinger, H.; Dudczak, R.; Steger, F.

    2003-01-01

    The activity distribution of beta-emitting radionuclides in the human body and the respective therapeutic dose distribution in the target and the unwanted leakage in the other organs was determined by measurement of corresponding gamma-lines. The measurement was done by scanning in a whole-body counter in the General Hospital Vienna. It is possible to localize activity and dose distribution by means of the detected activity profiles of the four detectors. Two typical treatments are reported: the treatment of synovitis using radiation of 166 Ho-Ferric-Hydroxide (characteristic gamma-line: 81 keV) and radionuclide therapy focused at the palliative treatment of bone metastases with 153 Sm-EDTMP, a bone seeking beta-emitting radionuclide (characteristic gamma-line: 103 keV). For the determination of the applied dose, the leakage and the quality assurance spectroscopic data of a clinical whole-body counter can be a useful tool for controlling and monitoring in health care. (authors)

  4. Measurement of the positron polarization at an helical undulator based positron source for the international linear collider ILC. The E-166 experiment at SLAC

    Energy Technology Data Exchange (ETDEWEB)

    Karim, Laihem

    2008-06-05

    A helical undulator based polarized positron source is forseen at a future International Linear Collider (ILC). The E-166 experiment has tested this scheme using a one meter long, short-period, pulsed helical undulator installed in the Final Focus Test Beam (FFTB) at SLAC. A low-emittance 46.6 GeV electron beam passing through this undulator generated circularly polarized photons with energies up to about 8 MeV. The generated photons of several MeV with circular polarization are then converted in a relatively thin target to generate longitudinally polarized positrons. Measurements of the positron polarization have been performed at 5 different energies of the positrons. In addition electron polarization has been determined for one energy point. For a comparison of the measured asymmetries with the expectations detailed simulations were necessary. This required upgrading GEANT4 to include the dominant polarization dependent interactions of electrons, positrons and photons in matter. The measured polarization of the positrons agrees with the expectations and is for the energy point with the highest polarization at 6MeV about 80%. (orig.)

  5. Delay in weight bearing in surgically treated tibial shaft fractures is associated with impaired healing: a cohort analysis of 166 tibial fractures.

    Science.gov (United States)

    Houben, I B; Raaben, M; Van Basten Batenburg, M; Blokhuis, T J

    2018-04-09

    The relation between timing of weight bearing after a fracture and the healing outcome is yet to be established, thereby limiting the implementation of a possibly beneficial effect for our patients. The current study was undertaken to determine the effect of timing of weight bearing after a surgically treated tibial shaft fracture. Surgically treated diaphyseal tibial fractures were retrospectively studied between 2007 and 2015. The timing of initial weight bearing (IWB) was analysed as a predictor for impaired healing in a multivariate regression. Totally, 166 diaphyseal tibial fractures were included, 86 cases with impaired healing and 80 with normal healing. The mean age was 38.7 years (range 16-89). The mean time until IWB was significantly shorter in the normal fracture healing group (2.6 vs 7.4 weeks, p bearing is independently associated with impaired fracture healing in surgically treated tibial shaft fractures. Unlike other factors such as fracture type or soft tissue condition, early resumption of weight bearing can be influenced by the treating physician and this factor therefore has a direct clinical relevance. This study indicates that early resumption of weight bearing should be the treatment goal in fracture fixation. 3b.

  6. Power Macintosh 7300/166

    CERN Document Server

    1997-01-01

    The Power Macintosh 7300 was released in 1997 and was the same case as the Power Macintosh 7600. Its main evolution is that it was equipped with a faster processor. It also had a bigger hard drive (2 GB) and a faster CD-ROM drive (12x to 8x). In return, Apple chose to remove the audiovisual connections that were present on all its predecessors of the range 7x00.

  7. 166 - 169_Yakubu and Babatunde

    African Journals Online (AJOL)

    User

    Yakubu, I.* and Babatunde, B. H.. Department of Geography Bayero University, PMB 3011, Kano. *Corresponding author: ibyakubu2006@yahoo.com. ABSTRACT. Soil nutrient decline has become a major issue of concern to researchers in the semi-arid region of. Nigeria. This condition is further exacerbated by worsening ...

  8. Physical activity attenuates the influence of FTO variants on obesity risk: a meta-analysis of 218,166 adults and 19,268 children.

    Directory of Open Access Journals (Sweden)

    Tuomas O Kilpeläinen

    2011-11-01

    Full Text Available The FTO gene harbors the strongest known susceptibility locus for obesity. While many individual studies have suggested that physical activity (PA may attenuate the effect of FTO on obesity risk, other studies have not been able to confirm this interaction. To confirm or refute unambiguously whether PA attenuates the association of FTO with obesity risk, we meta-analyzed data from 45 studies of adults (n = 218,166 and nine studies of children and adolescents (n = 19,268.All studies identified to have data on the FTO rs9939609 variant (or any proxy [r(2>0.8] and PA were invited to participate, regardless of ethnicity or age of the participants. PA was standardized by categorizing it into a dichotomous variable (physically inactive versus active in each study. Overall, 25% of adults and 13% of children were categorized as inactive. Interaction analyses were performed within each study by including the FTO×PA interaction term in an additive model, adjusting for age and sex. Subsequently, random effects meta-analysis was used to pool the interaction terms. In adults, the minor (A- allele of rs9939609 increased the odds of obesity by 1.23-fold/allele (95% CI 1.20-1.26, but PA attenuated this effect (p(interaction  = 0.001. More specifically, the minor allele of rs9939609 increased the odds of obesity less in the physically active group (odds ratio  = 1.22/allele, 95% CI 1.19-1.25 than in the inactive group (odds ratio  = 1.30/allele, 95% CI 1.24-1.36. No such interaction was found in children and adolescents.The association of the FTO risk allele with the odds of obesity is attenuated by 27% in physically active adults, highlighting the importance of PA in particular in those genetically predisposed to obesity.

  9. hCLE/C14orf166 associates with DDX1-HSPC117-FAM98B in a novel transcription-dependent shuttling RNA-transporting complex.

    Directory of Open Access Journals (Sweden)

    Alicia Pérez-González

    Full Text Available hCLE/C14orf166 is a nuclear and cytoplasmic protein that interacts with the RNAP II, modulates nuclear RNA metabolism and is present in cytoplasmic RNA granules involved in localized translation. Here we have studied whether hCLE shares common interactors in the nucleus and the cytosol, which could shed light on its participation in the sequential phases of RNA metabolism. Nuclear and cytoplasmic purified hCLE-associated factors were identified and proteins involved in mRNA metabolism, motor-related proteins, cytoskeletal and translation-related factors were found. Purified hCLE complexes also contain RNAs and as expected some hCLE-interacting proteins (DDX1, HSPC117, FAM98B were found both in the nucleus and the cytoplasm. Moreover, endogenous hCLE fractionates in protein complexes together with DDX1, HSPC117 and FAM98B and silencing of hCLE down-regulates their nuclear and cytosolic accumulation levels. Using a photoactivatable hCLE-GFP protein, nuclear import and export of hCLE was observed indicating that hCLE is a shuttling protein. Interestingly, hCLE nuclear import required active transcription, as did the import of DDX1, HSPC117 and FAM98B proteins. The data indicate that hCLE probably as a complex with DDX1, HSPC117 and FAM98B shuttles between the nucleus and the cytoplasm transporting RNAs suggesting that this complex has a prominent role on nuclear and cytoplasmic RNA fate.

  10. Photofission cross-section ratio measurement of {sup 235}U/{sup 238}U using monoenergetic photons in the energy range of 9.0–16.6 MeV

    Energy Technology Data Exchange (ETDEWEB)

    Krishichayan, E-mail: krishi@tunl.duke.edu [Department of Physics, Duke University, Durham, NC 27708 (United States); Triangle Universities Nuclear Laboratory, Durham, NC 27708 (United States); Bhike, Megha; Finch, S.W.; Howell, C.R. [Department of Physics, Duke University, Durham, NC 27708 (United States); Triangle Universities Nuclear Laboratory, Durham, NC 27708 (United States); Tonchev, A.P. [Nuclear and Chemical Sciences Division, Lawrence Livermore National Laboratory, Livermore, CA 94550 (United States); Tornow, W. [Department of Physics, Duke University, Durham, NC 27708 (United States); Triangle Universities Nuclear Laboratory, Durham, NC 27708 (United States)

    2017-05-11

    Photofission cross-section ratios of {sup 235}U and {sup 238}U have been measured using monoenergetic photon beams at the HIγS facility of TUNL. These measurements have been performed in small energy steps between 9.0 and 16.6 MeV using a dual-fission ionization chamber. Measured cross-section ratios are compared with the previous experimental data as well as with the recent evaluated nuclear data library ENDF.

  11. Avaliação de 166 ETEs em operação no país, compreendendo diversas tecnologias. Parte 1: análise de desempenho Evaluation of 166 treatment plants operating in Brazil, comprising several technologies. Part 1: performance analysis

    Directory of Open Access Journals (Sweden)

    Sílvia M. A. Corrêa Oliveira

    2005-12-01

    Full Text Available O trabalho apresenta uma análise de desempenho de 166 estações de tratamento de esgotos urbanos em operação nos estados de Minas Gerais e de São Paulo. Foram investigadas seis modalidades de tratamento diferentes, compreendendo os processos: (a fossa séptica seguida de filtro anaeróbio, (b lagoas facultativas, (c lagoas anaeróbias seguidas por lagoas facultativas, (d lodos ativados, (e reatores UASB operando isoladamente e (f reatores UASB seguidos por pós-tratamento. A avaliação considerou as concentrações efluentes e as eficiências de remoção dos constituintes DBO, DQO, SST, NTK, PT e coliformes (organismos termotolerantes, que foram comparadas com valores típicos reportados na literatura técnica. Em geral, o desempenho na remoção de matéria orgânica esteve dentro do esperado. As eficiências de remoção de SST estiveram abaixo, enquanto a remoção de coliformes foi maior que a descrita na literatura. A remoção de nutrientes foi baixa, já que nenhuma das modalidades analisadas foi projetada com este objetivo.The paper analyses the performance of 166 wastewater treatment plants operating in Brazil. Six different treatment technologies have been investigated, comprising the following processes: septic tank + anaerobic filter, facultative pond, anaerobic pond + facultative pond, activated sludge, UASB reactors alone, UASB reactors followed by post-treatment. The objective of the research was to evaluate the effluent quality and the removal efficiencies of the parameters BOD, COD, TSS, coliforms, TKN and phosphorus. The paper compares the effluent quality and the removal efficiencies with typical values reported by the technical literature. In general, the performance in the removal of organic matter was as expected. TSS removal efficiencies were lower than reported, but coliform removal was higher than described in the literature. Nutrient removal was low, but none of the treatment processes have been designed with

  12. Separation of zirconium and hafnium; Separation du zirconium et de l'hafnium

    Energy Technology Data Exchange (ETDEWEB)

    Saint-James, D [Commissariat a l' Energie Atomique, Saclay (France).Centre d' Etudes Nucleaires

    1959-07-01

    This account is more chemical than metallurgical in character. The reason for this is that so-called 'nuclear metal' must fulfil standards of purity which only chemical processes can attain. This paper must therefore be considered as a preliminary study, from which the metallurgists can form an idea of the treatments leading to the production of the metal. (author) [French] Cet expose a un caractere chimique plutot que metallurgique. La raison en est que le metal dit 'nucleaire' a des exigences de purete que seuls des processus chimiques peuvent satisfaire. Il faut donc considerer cet expose comme un preliminaire, permettant de donner une idee aux metallurgistes des traitements qui aboutissent a l'elaboration du metal. (auteur)

  13. Neuraxial blocks and spinal haematoma: Review of 166 case reports published 1994-2015. Part 1: Demographics and risk-factors.

    Science.gov (United States)

    Lagerkranser, Michael

    2017-04-01

    Bleeding into the vertebral canal causing a spinal haematoma (SH) is a rare but serious complication to central neuraxial blocks (CNB). Of all serious complications to CNBs such as meningitis, abscess, cardiovascular collapse, and nerve injury, neurological injury associated with SH has the worst prognosis for permanent harm. Around the turn of the millennium, the first guidelines were published that aimed to reduce the risk of this complication. These guidelines are based on known risk factors for SH, rather than evidence from randomised, controlled trials (RCTs). RCTs, and therefore meta-analysis of RCTs, are not appropriate for identifying rare events. Analysing published case reports of rare complications may at least reveal risk factors and can thereby improve management of CNBs. The aims of the present review were to analyse case reports of SH after CNBs published between 1994 and 2015, and compare these with previous reviews of case reports. MEDLINE and EMBASE were used for identifying case reports published in English, German, or Scandinavian languages, using appropriate search terms. Reference lists were also scrutinised for case reports. Twenty different variables from each case were specifically searched for and filled out on an Excel spreadsheet, and incidences were calculated using the number of informative reports as denominator for each variable. Altogether 166 case reports on spinal haematoma after CNB published during the years between 1994 and 2015 were collected. The annual number of case reports published during this period almost trebled compared with the two preceding decades. This trend continued even after the first guidelines on safe practice of CNBs appeared around year 2000, although more cases complied with such guidelines during the second half of the observation period (2005-2015) than during the first half. Three types of risk factors dominated: (1) Patient-related risk factors such as haemostatic and spinal disorders, (2) CNB

  14. Measurement of thermal neutron cross-section and resonance integral for the 165Ho(n,γ) 166gHo reaction using electron linac-based neutron source

    Science.gov (United States)

    Nguyen, Van Do; Pham, Duc Khue; Kim, Tien Thanh; Kim, Guinyun; Lee, Manwoo; Kim, Kyung Sook; Kang, Heung-Sik; Cho, Moo-Hyun; Ko, In Soo; Namkung, Won

    2011-01-01

    The thermal neutron cross-section and the resonance integral of the 165Ho(n,γ) 166gHo reaction have been measured by the activation method using a 197Au(n,γ) 198Au monitor reaction as a single comparator. The high-purity natural Ho and Au foils with and without a cadmium shield case of 0.5 mm thickness were irradiated in a neutron field of the Pohang neutron facility. The induced activities in the activated foils were measured with a calibrated p-type high-purity Ge detector. The correction factors for the γ-ray attenuation ( Fg), the thermal neutron self-shielding ( Gth), the resonance neutron self-shielding ( Gepi) effects, and the epithermal neutron spectrum shape factor ( α) were taken into account. The thermal neutron cross-section for the 165Ho(n,γ) 166gHo reaction has been determined to be 59.7 ± 2.5 barn, relative to the reference value of 98.65 ± 0.09 barn for the 197Au(n,γ) 198Au reaction. By assuming the cadmium cut-off energy of 0.55 eV, the resonance integral for the 165Ho(n,γ) 166gHo reaction is 671 ± 47 barn, which is determined relative to the reference value of 1550 ± 28 barn for the 197Au(n,γ) 198Au reaction. The present results are, in general, good agreement with most of the previously reported data within uncertainty limits.

  15. Luminescence properties of a single-component Na0.34Ca0.66Al1.66Si2.34O8:Ce3+, Sm3+ phosphor with tunable color tone for UV-pumped LEDs

    Science.gov (United States)

    Wang, Lei; Dong, Jie; Cui, Cai'e.; Tian, Yue; Huang, Ping

    2015-08-01

    A series of single-phase Na0.34Ca0.66Al1.66Si2.34O8:Ce3+, Sm3+ (NCASO) phosphors have been synthesized via a high temperature solid-state reaction method. The samples were studied based on photoluminescence (PL), photoluminescence excitation (PLE) spectra and fluorescence decay patterns. The obtained PLE exhibited a strong excitation band in the UV region between 250 and 380 nm. Under 340 nm excitation, NCASO:Ce3+, Sm3+ phosphor showed a broad emission band at 414 nm of Ce3+ and four emission bands from 550 nm to 725 nm of Sm3+. Spectra demonstrate nonradiative energy transfers (ET) occur from Ce3+-Sm3+. The analysis based on Inokuti-Hirayama model indicates that the ET is governed by electric dipole-dipole interaction. Moreover, the emitting colors can be adjusting from blue to white by proper tuning of the relative composition of Ce3+/Sm3+. These results show that NCASO:Ce3+, Sm3+ phosphors can be used as a potential single-phased white-emitting candidate for UV WLEDs.

  16. Intercomparison Of Activity Measurements Of Co-58, Y-88, Ho-166m, Tc-99m, dan I-131 Between P3KRBiN and Laboratory Within BATAN And Hospitals

    International Nuclear Information System (INIS)

    Nazaroh; Ermi-Juita; Hermawan-Candra

    2003-01-01

    One way to maintain traceability and to keep consistency of the measurement result of radioactivity was intercomparison program. According with Surat Keputusan Kepala BATAN No.73/KA/IV/99, one of tasks and functions of standardization laboratory is to coordinate an intercomparison program of radioactivity measurement. In the year of 2000, intercomparison program of activity measurements between P3KRBiN and 10 laboratories within BATAN and 12 hospitals were carried out. For intercomparison of Co-58, Y-88, and Ho-166m, there were 3 laboratories within BATAN which have more than 50% difference compared with P3KRBiN measurements and for intercomparison of Tc-99m, dan I-131, there were 2 Dose-Calibrators belongs to hospitals which have more than 30% difference compared with P3KRBiN measurements. From that result it can be concluded that intercomparison of activity measurements are very important and needs continuously to maintain traceability and to keep consistency of measurement result. (author)

  17. Vegetation - Central Mojave Desert [ds166

    Data.gov (United States)

    California Natural Resource Agency — The Department of Defense and the other desert managers are developing and organizing scientific information needed to better manage the natural resources of the...

  18. 40 CFR 166.3 - Definitions.

    Science.gov (United States)

    2010-07-01

    ... pollinating insect, or any pest predator, parasite, pathogen or other biological control agent which functions naturally or as part of an integrated pest management program to control another pest. Emergency condition... for control of the pest under the conditions of the emergency; and (2) No economically or...

  19. 9 CFR 166.15 - State status.

    Science.gov (United States)

    2010-01-01

    ..., Iowa, Kansas, Kentucky, Louisiana, Mississippi, Nebraska, New York, North Dakota, Oregon, South... enforcement responsibility under the Act: Alabama, Arizona, California, Colorado, Florida, Georgia, Hawaii, Idaho, Illinois, Indiana, Iowa, Michigan, Minnesota, Mississippi, Missouri, Montana, Nebraska, Nevada...

  20. 75 FR 166 - Postal Product Price Changes

    Science.gov (United States)

    2010-01-04

    ... POSTAL REGULATORY COMMISSION [Docket No. CP2009-49; Order No. 371] Postal Product Price Changes...-filed Postal Service request to change prices for a Global Plus 2 contract. This notice provides an...: On December 21, 2009, the Postal Service filed a notice that prices for the Global Plus 2 contract at...

  1. Search Results | Page 166 | IDRC - International Development ...

    International Development Research Centre (IDRC) Digital Library (Canada)

    In the Arab world, gender inequality in the labour market persists through occupational segregation, wage gaps, higher unemployment rates, ... Gender and Migration : a Women's Movement Perspective on Negotiating Rights (India). Women's ...

  2. Publications | Page 166 | IDRC - International Development ...

    International Development Research Centre (IDRC) Digital Library (Canada)

    Home · Resources ... Policy brief on young women's political participation (open access) ... Development to push for programs that will tackle the barriers that limit ... institutes and research organizations conducted across 13 states of India.

  3. 21 CFR 166.110 - Margarine.

    Science.gov (United States)

    2010-04-01

    ... these, whose origin is vegetable or rendered animal carcass fats, or any form of oil from a marine... used in whole or in part, the animal source shall be identified in conjunction with the word milk in...

  4. 21 CFR 211.166 - Stability testing.

    Science.gov (United States)

    2010-04-01

    ... record of such data shall be maintained. Accelerated studies, combined with basic stability information on the components, drug products, and container-closure system, may be used to support tentative expiration dates provided full shelf life studies are not available and are being conducted. Where data from...

  5. Uma Investigação na Complementaridade do Fluxo de Caixa e do Balanço Financeiro após a Aprovação da NBCASP 16.6 para o Setor Público

    Directory of Open Access Journals (Sweden)

    Marcleide Maria Macêdo Pederneiras

    2013-09-01

    Full Text Available Este estudo teve por objetivo analisar os ganhos informacionais gerados pela obrigatoriedade na elaboração da Demonstração de Fluxo de Caixa para o setor público após a aprovação da NBCASP 16.6, pois com a mudança o setor público passa a elaborar duas demonstrações com informações financeiras que podem levar ao usuário da Contabilidade Pública a questionar a real necessidade da elaboração destes dois demonstrativos conjuntamente. Para a realização deste estudo foi utilizado o método indutivo, onde foi elaborado um caso prático partindo do Balanço Financeiro do Estado de Pernambuco, através do qual se elaborou a Demonstração de Fluxo de Caixapara comparar as informações geradas por cada demonstrativo. Houve limitação em relação ao caso prático por os municípios ainda não estarem elaborando tais demonstrativos. Após a análise dos demonstrativos concluiu-se que ambos os demonstrativos são importantes para a tomada de decisão dos gestores e que tais demonstrativos são complementares, gerando informações diferentes, havendo, portanto, um ganho informacional para os usuários da contabilidade pública.

  6. Hafnium isotope ratios of nine GSJ reference samples

    International Nuclear Information System (INIS)

    Hanyu, Takeshi; Nakai, Shun'ichi; Tatsuta, Riichiro

    2005-01-01

    176 Hf/ 177 Hf ratios of nine geochemical reference rocks from the Geological Survey of Japan, together with BIR-1 and BCR-2, were determined using multi-collector inductively coupled plasma mass spectrometry. Our data for BIR-1, BCR-2 and JB-1 are in agreement with those previously reported, demonstrating the appropriateness of the chemical procedure and isotopic measurement employed in this study. The reference rocks have a wide range of 176 Hf/ 177 Hf covering the field defined by various volcanic rocks, such as mid-ocean ridge basalts, ocean island basalts, and subduction related volcanic rocks. They are therefore suitable as rock standards for Hf isotope measurement of geological samples. (author)

  7. Control of the hafnium content in Co samples by SSMS

    International Nuclear Information System (INIS)

    Lukaszew, R.A.; Cretella, R.F.

    1989-01-01

    The production of 60 Co requires a strict control of the chemical composition of the cobalt before irradiation in order to avoid the activation of some undesirable elements and to constrain the presence of slow neutron poisons. A methodology by SSMS for the survey analysis of metallic Co prior to its irradiation in the nuclear reactor at Embalse (Cdba., Argentina) is described. The low detection limit attained for Hf (below 0.5 ppm) is outlined. The results obtained for some other impurities without a standard reference are compared with atomic emission spectrographic data and show satisfactory agreement. (orig.)

  8. Production of long-lived hafnium isomers in reactor irradiations

    Czech Academy of Sciences Publication Activity Database

    Adam, Jindřich

    -, - (2006), s. 48-56 ISSN 1574-1818 R&D Projects: GA MŠk 1P04LA213 Institutional research plan: CEZ:AV0Z10480505 Keywords : production * Hf Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders

  9. Hafnium Isotopic Variations in Central Atlantic Intraplate Volcanism

    Science.gov (United States)

    Geldmacher, J.; Hanan, B. B.; Hoernle, K.; Blichert-Toft, J.

    2008-12-01

    Although one of the geochemically best investigated volcanic regions on Earth, almost no Hf isotopic data have been published from the broad belt of intraplate seamounts and islands in the East Atlantic between 25° and 36° N. This study presents 176Hf/177Hf ratios from 61 representative samples from the Canary, Selvagen and Madeira Islands and nearby large seamounts, encompassing the full range of different evolutionary stages and geochemical endmembers. The majority of samples have mafic, mainly basaltic compositions with Mg-numbers within or near the range of magmas in equilibrium with mantle olivine (68-75). No correlation was found between Mg-number and 176Hf/177Hf ratios in the data set. In comparison to observed Nd isotope variations published for this volcanic province (6 ɛNd units), 176Hf/177Hf ratios span a larger range (14 ɛHf units). Samples from the Madeira archipelago have the most radiogenic compositions (176Hf/177Hfm= 0.283132-0.283335), widely overlapping the field for central Atlantic N-MORB. They form a relatively narrow, elongated trend (stretching over >6 ɛHf units) between a radiogenic MORB-like endmember and a composition located on the Nd-Hf mantle array. In contrast, all Canary Islands samples plot below the mantle array (176Hf/177Hfm = 0.282943-0.283067) and, despite being from an archipelago that stretches over a much larger geographic area, form a much denser cluster with less compositional variation (~4 ɛHf units). All samples from the seamounts NE of the Canaries, proposed to belong to the same Canary hotspot track (e.g. Geldmacher et al., 2001, JVGR 111; Geldmacher et al., 2005, EPSL 237), fall within the Hf isotopic range of this cluster. The cluster largely overlaps the composition of the proposed common mantle endmember 'C' (Hanan and Graham, 1996, Science 272) but spans a space between a more radiogenic (depleted) composition and a HIMU-type endmember. Although samples of Seine and Unicorn seamounts, attributed to the Madeira hotspot track, show less radiogenic Hf and Nd isotope ratios than Madeira, their isotopic compositions lie along an extension of the Madeira trend in plots of Hf versus Sr, Nd, Pb isotopes. The new Hf isotope ratios confirm the existence of at least two geochemically distinct volcanic provinces (Canary and Madeira) in the East Atlantic as previously proposed.

  10. Electric field cycling behavior of ferroelectric hafnium oxide.

    Science.gov (United States)

    Schenk, Tony; Schroeder, Uwe; Pešić, Milan; Popovici, Mihaela; Pershin, Yuriy V; Mikolajick, Thomas

    2014-11-26

    HfO2 based ferroelectrics are lead-free, simple binary oxides with nonperovskite structure and low permittivity. They just recently started attracting attention of theoretical groups in the fields of ferroelectric memories and electrostatic supercapacitors. A modified approach of harmonic analysis is introduced for temperature-dependent studies of the field cycling behavior and the underlying defect mechanisms. Activation energies for wake-up and fatigue are extracted. Notably, all values are about 100 meV, which is 1 order of magnitude lower than for conventional ferroelectrics like lead zirconate titanate (PZT). This difference is mainly atttributed to the one to two orders of magnitude higher electric fields used for cycling and to the different surface to volume ratios between the 10 nm thin films in this study and the bulk samples of former measurements or simulations. Moreover, a new, analog-like split-up effect of switching peaks by field cycling is discovered and is explained by a network model based on memcapacitive behavior as a result of defect redistribution.

  11. Elastic and Thermodynamic Properties of Zirconium and Hafnium ...

    Indian Academy of Sciences (India)

    65

    Here Rh3V is chosen as the parent binary compound and the doping ..... Grüneisen parameter ζ [44] are two key quantities in solid state problems due to their .... The authors wish to thank DRDO (ER & IPR), New Delhi for the financial support.

  12. Electronic structure of hafnium: A Compton profile study

    Indian Academy of Sciences (India)

    To extract the true Compton profile from the raw data, the raw data were cor- rected for ... For the present sample and experimental conditions, the contribution of .... are in better agreement with the simple renormalized free atom calculations for.

  13. Hafnium(IV) complexation with oxalate at variable temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Friend, Mitchell T.; Wall, Nathalie A. [Washington State Univ., Pullmanm, WA (United States). Dept. of Chemistry

    2017-08-01

    Appropriate management of fission products in the reprocessing of spent nuclear fuel (SNF) is crucial in developing advanced reprocessing schemes. The addition of aqueous phase complexing agents can prevent the co-extraction of these fission products. A solvent extraction technique was used to study the complexation of Hf(IV) - an analog to fission product Zr(IV) - with oxalate at 15, 25, and 35 C in 1 M HClO{sub 4} utilizing a {sup 175+181}Hf radiotracer. The mechanism of the solvent extraction system of 10{sup -5} M Hf(IV) in 1 M HClO{sub 4} to thenoyltrifluoroacetone (TTA) in toluene demonstrated a 4{sup th}-power dependence in both TTA and H{sup +}, with Hf(TTA){sub 4} the only extractable species. The equilibrium constant for the extraction of Hf(TTA){sub 4} was determined to be log K{sub ex}=7.67±0.07 (25±1 C, 1 M HClO{sub 4}). The addition of oxalate to the aqueous phase decreased the distribution ratio, indicating aqueous Hf(IV)-oxalate complex formation. Polynomial fits to the distribution data identified the formation of Hf(ox){sup 2+} and Hf(ox){sub 2(aq)} and their stability constants were measured at 15, 25, and 35 C in 1 M HClO{sub 4}. van't Hoff analysis was used to calculate Δ{sub r}G, Δ{sub r}H, and Δ{sub r}S for these species. Stability constants were observed to increase at higher temperature, an indication that Hf(IV)-oxalate complexation is endothermic and driven by entropy.

  14. Iron(3) chloride interaction with zirconium and hafnium tetrahalides

    International Nuclear Information System (INIS)

    Berdonosov, S.; Kharisov, B.I.; Melikhov, I.V.

    1988-01-01

    Using FeCl 3 , labelled with 36 Cl radionuclide, it is shown, that during reaction between FeCl 3 and MCl (M=Zr, Hf) resulting in Cl 2 splitting-off and FeMCl 6 formation, chlorine is splitted from MCl 4 . From the analysis of Moessbauer spectra and visual observations it follows, that reaction between FeCl 3 and MBr 4 starts at 50 deg C temperature, whereupon bromine and FeMCl 3 Br 3 compounds are formed. Considerations about the possible mechanism of reactions between FeCl 3 and MCl 4 or MBr 4 are proposed

  15. Cesium hafnium chloride scintillator coupled with an avalanche photodiode photodetector

    Czech Academy of Sciences Publication Activity Database

    Kurosawa, S.; Kodama, S.; Yokota, Y.; Horiai, T.; Yamaji, A.; Shoji, Y.; Král, Robert; Pejchal, Jan; Ohashi, Y.; Kamada, K.; Nikl, Martin; Yoshikawa, A.

    2017-01-01

    Roč. 12, Feb (2017), s. 1-8, č. článku C02042. ISSN 1748-0221 Grant - others:AV ČR(CZ) JSPS-17-18 Program:Bilaterální spolupráce Institutional support: RVO:68378271 Keywords : gamma detectors * scintillators and scintillating fibres * scintillators * scintillation and light emission processes Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 1.220, year: 2016

  16. Spectroscopy of very neutron-deficient hafnium and tungsten isotopes

    Energy Technology Data Exchange (ETDEWEB)

    Dracoulis, G D; Fabricius, B; Davidson, P M [Australian National Univ., Canberra, ACT (Australia). Dept. of Nuclear Physics; Macchiavelli, A O; Oliviera, J; Burde, J; Stephens, F; Deleplanque, M A [Lawrence Berkeley Lab., CA (United States)

    1992-08-01

    Level schemes of the very neutron-deficient isotopes {sup 158}Hf and {sup 162}W have been identified, and that for {sup 164}W extended. Alignment of the H{sub 9/2} neutrons is suggested. (author). 12 refs., 7 figs.

  17. Neutron Detection Utilizing Gadolinium Doped Hafnium Oxide Films

    National Research Council Canada - National Science Library

    Blasy, Bryan D

    2008-01-01

    ... retains monoclinic local symmetery for all levels of doping. Current as a function of voltage experiments identified the films as having poor diode characteristics with high leakage current in the forward bias region...

  18. Crystal structures of superconducting sodium intercalates of hafnium nitride chloride

    International Nuclear Information System (INIS)

    Oro-Sole, J.; Frontera, C.; Beltran-Porter, D.; Lebedev, O.I.; Van Tendeloo, G.; Fuertes, A.

    2006-01-01

    Sodium intercalation compounds of HfNCl have been prepared at room temperature in naphtyl sodium solutions in tetrahydrofuran and their crystal structure has been investigated by Rietveld refinement using X-ray powder diffraction data and high-resolution electron microscopy. The structure of two intercalates with space group R3-bar m and lattice parameters a=3.58131(6)A, c=57.752(6)A, and a=3.58791(8)A, c=29.6785(17)A is reported, corresponding to the stages 2 and 1, respectively, of Na x HfNCl. For the stage 2 phase an ordered model is presented, showing two crystallographically independent [HfNCl] units with an alternation of the Hf-Hf interlayer distance along the c-axis, according with the occupation by sodium atoms of one out of two van der Waals gaps. Both stages 1 and 2 phases are superconducting with critical temperatures between 20 and 24K, they coexist in different samples with proportions depending on the synthesis conditions, and show a variation in c spacing that can be correlated with the sodium stoichiometry. High-resolution electron microscopy images of the host and intercalated samples show bending of the HfNCl bilayers as well as stacking faults in some regions, which coexist in the same crystal with ordered domains

  19. Elastic and thermodynamic properties of zirconium- and hafnium ...

    Indian Academy of Sciences (India)

    2018-02-02

    Feb 2, 2018 ... ties. The volume optimization curves (both LDA and GGA) for binary Rh3V, Rh3Zr and Rh3Hf compounds are shown in ... the strength of covalent bonding of the given material. ..... Bulk modulus is correlated with binding energy or cohesive energy of atoms, since it is a measure of average atomic bond.

  20. Experiment for a measurement of the charge radius of the proton at the S-DALINAC and investigation of the fine structure of giant resonances in {sup 28}Si, {sup 48}Ca and {sup 166}Er with the help of the wavelet analysis; Experiment zur Messung des Ladungsradius des Protons am S-DALINAC und Untersuchung der Feinstruktur von Riesenresonanzen in {sup 28}Si, {sup 48}Ca und {sup 166}Er mit Hilfe der Waveletanalyse

    Energy Technology Data Exchange (ETDEWEB)

    Pysmenetska, Inna

    2009-07-22

    The present thesis consists of two parts. In the first part a novel experimental method for the measurement of the proton root-mean-square radius at the S-DALINAC is presented. A setup based on semiconductor detectors is realized. In contrast to previous experiments it allows a simultaneous measurement of the momentum transfer dependence of the elastic electron scattering cross section. A possible suppression of the significant electron and bremsstrahlung background observed in a test experiment was investigated with the help of different methods, such as {delta}E-E telescopes, the time of flight method with a pulsed beam and pulse shape discrimination. The combination of these methods allows a reduction of the background at all scattering angles, which should allow a successful measurement. The response of the detector system was studied with the help of Monte-Carlo simulations with an emphasis on the dependence of the expected accuracy of different parameters. The second part of this work describes an investigation of the fine structure of giant resonances in {sup 28}Si, {sup 48}Ca and {sup 166}Er with the help of a wavelet analysis. The discrete wavelet transform was used for a background determination in spectra of the iso vector E1 and the M2 giant resonances in {sup 48}Ca. This allows the extraction of 1{sup -} und 2{sup -} level densities in the excitation energy region of the respective resonances with the help of a fluctuation analysis. A fluctuation analysis of the fine structure of the isoscalar E2 resonance in {sup 166}Er allows the extraction of the coherent widths of the 2{sup +} states. In the excitation energy region E{sub x}=10-16 MeV widths between 30 and 80 eV are found. The fine structure of the giant resonances is furthermore specified by characteristic scales. In this thesis scales in {sup 28}Si and {sup 48}Ca are extracted with the help of the above mentioned wavelet transform. In {sup 28}Si the isovector E1 and isoscalar E2 resonances were

  1. Separation of magnesium from magnesium chloride and zirconium and/or hafnium subchlorides in the production of zirconium and/or hafnium sponge metal

    International Nuclear Information System (INIS)

    Abodishish, H.A.M.; Adams, R.J.; Kearl, S.R.

    1992-01-01

    This patent describes the producing of a refractory metal wherein a sponge refractory metal is produced as an intermediate product by the use of magnesium with the incidental production of magnesium chloride, and wherein residual magnesium is separated from the magnesium chloride and from refractory metal to a vacuum distillation step which fractionally distills the magnesium, the magnesium chloride, and the metal sub-chlorides; the steps of: recovering fractionally distilled vapors of magnesium chloride and metal sub-chlorides from a sponge refractory metal; separately condensing the vapors as separately recovered; and recycling the separately recovered magnesium at a purity of at least about 96%

  2. 32 CFR 644.166 - Authority and applicability.

    Science.gov (United States)

    2010-07-01

    ... 10, United States Code, as amended by section 707 of the Act of Congress approved October 27, 1971... parcel of real property before or after its acquisition is authorized by law, if he considers it suitable... options to the Committees on Armed Services of the Senate and House of Representatives. (b) Applicability...

  3. 7 CFR 989.166 - Reserve tonnage generally.

    Science.gov (United States)

    2010-01-01

    ... Agreements and Orders; Fruits, Vegetables, Nuts), DEPARTMENT OF AGRICULTURE RAISINS PRODUCED FROM GRAPES..., with or without chemicals, prior to or during the drying process, for purposes other than to expedite drying, or that have been produced from seedless varieties of grapes other than Thompson Seedless (i.e...

  4. Dicty_cDB: VSI166 [Dicty_cDB

    Lifescience Database Archive (English)

    Full Text Available KK Translated Amino Acid sequence (All Frames) Frame A: QKHKTIYKYQHCYFLQIFFLTHYHTKFFLILFNTHTFKKK--- ---gxxxxxxxxxxxxxfxxxfffxxx...ppxffffffspxff*kkkkkxxxxfffxtpxxf ffxxkkkk Frame B: knikqstniniaifykfff*hittpsfs*fylthill...kkk--- ---GXXXXXXXKXXXXFFXXFFFXXXXPPXFFFFFFPPXFFKKKKKKXFXXFFFXPXXXF FXPXKKKK Frame C: kt*nnlqistllfftnfffntl...phqvflnfi*htyf*kk--- ---xxxxxxxxxxxxxffxxfffxxxppxfffffffpplflkkkkkkxfxfffxnpxxxf

  5. 40 CFR 417.166 - Pretreatment standards for new sources.

    Science.gov (United States)

    2010-07-01

    ... GUIDELINES AND STANDARDS SOAP AND DETERGENT MANUFACTURING POINT SOURCE CATEGORY Manufacture of Liquid... standard shall be: (1) For normal liquid detergent operations the following values pertain: Pollutant or...

  6. 19 CFR 191.166 - Destruction of merchandise.

    Science.gov (United States)

    2010-04-01

    ... THE TREASURY (CONTINUED) DRAWBACK Distilled Spirits, Wines, or Beer Which Are Unmerchantable or Do Not... drawback claimant who proposes to destroy rather than export the distilled spirits, wine, or beer shall state that fact on Customs Form 7551. (b) Action by Customs. Distilled spirits, wine, or beer returned...

  7. 9 CFR 166.1 - Definitions in alphabetical order.

    Science.gov (United States)

    2010-01-01

    ..., preparation, cooking or consumption of food, except that such term shall not include waste from ordinary..., preparation, cooking or consumption of food that has been ground and heated to a minimum temperature of 230 °F... cooked as a food for swine and which are fenced in or otherwise constructed so that swine are unable to...

  8. 17 CFR 166.5 - Dispute settlement procedures.

    Science.gov (United States)

    2010-04-01

    ... or directly connected with any transaction for the purchase or sale of any commodity for future... notice must be given at the time when the Commission registrant notifies the customer of an intention to...

  9. 76 FR 166 - Fresh and Chilled Atlantic Salmon From Norway

    Science.gov (United States)

    2011-01-03

    ... and demand conditions or business cycle for the Domestic Like Product that have occurred in the United... Official, at 202-205-3088. Limited disclosure of business proprietary information (BPI) under an... Subject Merchandise, a U.S. or foreign trade or business association, or another interested party...

  10. 27 CFR 46.166 - Dealing in tobacco products.

    Science.gov (United States)

    2010-04-01

    ... packages, provided the products remain in the packages until removed by the customer or in the presence of the customer. Where a vending machine is used, tobacco products must similarly be vended in proper... consumption in the United States unless such articles are removed from their export packaging and repackaged...

  11. What we do | Page 166 | IDRC - International Development ...

    International Development Research Centre (IDRC) Digital Library (Canada)

    The overarching goal of Gender Evaluation Methodology (GEM) Phase II is to ... Culture and the Exercise of Decision Making by Women in West Africa ... political and social decision-making, and weak participation of women at the local, ...

  12. The E166 experiment: Development of an undulator-based ...

    Indian Academy of Sciences (India)

    K-factor is about 0.19 which leads to a parabolic distribution for the first harmonic with a cut-off ... magnetization, an asymmetry in the transmitted photon rate is observed. The ... [1] G Moortgat-Pick and H M Steiner, EPJdirect C, vol. 1, C6 ...

  13. Our first clinical experience with radiosynoviorthesis by means of 166

    Czech Academy of Sciences Publication Activity Database

    Kraft, O.; Kašpárek, R.; Ullmann, V.; Melichar, František; Kropáček, Martin; Mirzajevová, Marcela

    2005-01-01

    Roč. 8, č. 2 (2005), s. 131-134 ISSN 1506-9680 R&D Projects: GA AV ČR(CZ) 1QS100480501 Institutional research plan: CEZ:AV0Z10480505 Keywords : holmium * radiotherapy Subject RIV: CH - Nuclear ; Quantum Chemistry

  14. MILITARY MEDICINE: International Journal of AMSUS. Volume 166, Number 9

    Science.gov (United States)

    2001-09-01

    General, U.S. Army: Memorandum to Major Walter Reed. Washington, DC, fiebre amarilla " Anales de la Ciencir Medicas, Flsicas y Naturales de la Habana May 29... Fiebre Am- It is, we think, important to observe that of the 9 failures to arilla, Estudio Clinico Patologico y Etiologico, reprint, Habana, infect, the

  15. 40 CFR 82.166 - Reporting and recordkeeping requirements.

    Science.gov (United States)

    2010-07-01

    ... operators of appliances must maintain on-site and report to EPA Headquarters at the address listed in § 82... signed by an authorized company official. (o) The owners or operators of appliances must maintain on-site...

  16. 49 CFR 1.66 - Delegations to Maritime Administrator.

    Science.gov (United States)

    2010-10-01

    ... delegated to the Administrator of the National Oceanic and Atmospheric Administration relating to the... the functions vested in the Secretary by section 3(d) of the Act to Prevent Pollution from Ships (33 U...) Carry out the functions vested in the Secretary by the Oil Pollution Act of 1990 (August 18, 1990; Pub...

  17. All projects related to | Page 166 | IDRC - International Development ...

    International Development Research Centre (IDRC) Digital Library (Canada)

    2017-01-24

    Malnutrition remains a serious problem in both Vietnam and Thailand, particularly in the uplands, home to most of the ethnic minorities. End Date: January 24, 2017. Topic: MALNUTRITION, FOOD SHORTAGE, WOMEN, CHILDREN, RESOURCES DEVELOPMENT, SURVEYS, INTERVIEWS, POLICY MAKING, Capacity ...

  18. 166 Spatialization of Time and Temporalization of Space: A Critical ...

    African Journals Online (AJOL)

    Ngozi Ezenwa-Ohaeto

    changing and this made some people to take time to be equivalent to .... and these facts are seen as the very essence of time. He argued that .... against our conventional belief about time. Is there no time? ..... space and whatever is false of space is also false of time. .... them as co-existing in orderly manner with a simple.

  19. Quantitative microanalysis of hafnium - zirconium system by X-ray fluorescence

    International Nuclear Information System (INIS)

    Majid, C.A.; Hussain, M.A.; Saeed, K.

    1986-01-01

    X-ray fluorescence technique has been used for the analysis of Hf in the presence of Zr by developing a method. In this method the spectral interference of Hf lines by Zr is eliminated completely and the Hf detection is accomplished using the most efficient Li line of its L-series. The principle of the method is based on the extinction properties of crystals for some orders of reflection. Ge(III) is used as the analyzing crystal. This method can be used accurately to detect Hf in any concentration of Zr at least from about 20 ppm to 100%. Also no information about the expected range of the analyte sample, is required in advance. (authors)

  20. X-Ray fluorescence of microquantities of hafnium in zirconium by precipitation as thin film

    International Nuclear Information System (INIS)

    Vigoda de Leyt, Dora; Caridi, A.F.; Deibe, Jorge

    1988-01-01

    The importance of Zr and Hf in the nuclear industry represents and increasing need for the development of reliable chemical methods to determine Hf traces in Zr matrix. A precipitation method in amoniacal medium was developed. A thin film is obtained where matrix effects are absent or minimized. Hf in the range of 5-70.10 -9 Kg in a 5.10 -6 Kg Zr matrix was studied. Fluorescence Hf Lα and Hf Lβ X-rays are excited by a W-anode tube 17 kV-25mA and 50kV-25mA. Radiation scattered by the tube was used as internal standard. Bartlett criterion was used for the regression analysis. Determination limit was fixed in 5±4. 10 -9 Kg Hf at a 95 % probability. (Author) [es