Sample records for graphitic carbon particles

  1. A graphite foam reinforced by graphite particles

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, J.J.; Wang, X.Y.; Guo, L.F.; Wang, Y.M.; Wang, Y.P.; Yu, M.F.; Lau, K.T.T. [DongHua University, Shanghai (China). College of Material Science and Engineering

    2007-11-15

    Graphite foam was obtained after carbonization and graphitization of a pitch foam formed by the pyrolysis of coal tar based mesophase pitch mixed with graphite particles in a high pressure and temperature chamber. The graphite foam possessed high mechanical strength and exceptional thermal conductivity after adding the graphite particles. Experimental results showed that the thermal conductivity of modified graphite foam reached 110W/m K, and its compressive strength increased from 3.7 MPa to 12.5 MPa with the addition of 5 wt% graphite particles. Through the microscopic observation, it was also found that fewer micro-cracks were formed in the cell wall of the modified foam as compared with pure graphite foam. The graphitization degree of modified foam reached 84.9% and the ligament of graphite foam exhibited high alignment after carbonization at 1200{sup o}C for 3 h and graphitization at 3000{sup o}C for 10 min.

  2. Mesoporous silica particles modified with graphitic carbon: interaction with human red blood cells and plasma proteins

    Energy Technology Data Exchange (ETDEWEB)

    Martinez, Diego Stefani Teodoro; Franqui, Lidiane Silva; Bettini, Jefferson; Strauss, Mathias, E-mail: diego.martinez@lnnano.cnpem.br [Centro Nacional de Pesquisa em Energia e Materiais (CNPEM), Campinas, SP (Brazil); Damasceno, Joao Paulo Vita; Mazali, Italo Odone [Universidade Estadual de Campinas (UNICAMP), SP (Brazil)

    2016-07-01

    Full text: In this work the interaction of the mesoporous silica particles (SBA-15, ∼700 nm) modified with graphitic carbon (SBA-15/C) on human red blood cells (hemolysis) and plasma proteins (protein corona formation) is studied. XPS and CHN analysis showed that the carbon content on the SBA-15/C samples varied from 2 to 10% and was tuned by the functionalization step. The formed carbon structures where associated to graphitic nanodomains coating the pores surface as verified by Raman spectroscopy and {sup 13}C NMR. Advanced TEM/EELS analysis showed that the carbon structures are distributed along the SBA-15 mesopores. SAXS and textural analyses were used to confirm that the porous structure of the silica support is kept after the modification procedure and to calculate the number of graphitic carbon stacked layers coating the mesopores. After incubation of SBA-15 with human red blood cells (RBCs), it was observed a dose-dependent hemolytic effect, probably, due to binding of the material silanol-rich surface to the phosphatidylcholine molecules from the RBC membrane. The graphitic carbon modifications have mitigated this effect, indicating that the graphitic carbon coating protected the silanol groups of the particle surface hindering the hemolysis. Considering the protein corona formation, selective biomolecular interaction of proteins was observed for the different materials using gel electrophoresis (SDS-PAGE) analysis. Besides, graphitic carbon modification decreased the amount of proteins on the corona. Together, the in vitro hemolysis and protein corona assays are promising biological models to understand the influence of silica surface functionalization on their bionano-interactions. Finally, our work contributes to the development of fundamental research on such nanomaterials chemistry in the emerging field of nanobioscience and nanotoxicology. (author)

  3. Raman spectroscopy of carbon nano-particles synthesized by laser ablation of graphite in water

    Energy Technology Data Exchange (ETDEWEB)

    Cardenas, J. F.; Cadenbach, T.; Costa V, C.; Paz, J. L. [Escuela Politecnica Nacional, Departamento de Fisica, Apdo. 17-12-866, Ladron de Guevara E11-253, EC 170109, Quito (Ecuador); Zhang, Z. B.; Zhang, S. L. [Institutionen for teknikvetenskaper, Fasta tillstandets elektronik, Angstromlaboratoriet, Lagerhyddsvagen, 1 Box 534, 751-21 Uppsala (Sweden); Debut, A.; Vaca, A. V., E-mail: cardenas9291@gmail.com [Centro de Nanociencia y Nanotecnologia, Universidad de las Fuerzas Armadas ESPE, Sangolqui (Ecuador)

    2017-11-01

    Carbon nanoparticles (CNPs) have been synthesized by laser ablation of polycrystalline graphite in water using a pulsed Nd:YAG laser (1064 nm) with a width of 8 ns. Structural and mesoscopic characterization of the CNPs in the supernatant by Raman spectroscopy provide evidence for the presence of mainly two ranges of particle sizes: 1-5 nm and 10-50 nm corresponding to amorphous carbon and graphite Nps, respectively. These results are corroborated by complementary characterization using atomic force microscopy (AFM) and transmission electron microscopy (Tem). In addition, large (10-100 μm) graphite particles removed from the surface are essentially unmodified (in structure and topology) by the laser as confirmed by Raman analysis. (Author)

  4. Carbon-14 Graphitization Chemistry

    Science.gov (United States)

    Miller, James; Collon, Philippe; Laverne, Jay

    2014-09-01

    Accelerator Mass Spectrometry (AMS) is a process that allows for the analysis of mass of certain materials. It is a powerful process because it results in the ability to separate rare isotopes with very low abundances from a large background, which was previously impossible. Another advantage of AMS is that it only requires very small amounts of material for measurements. An important application of this process is radiocarbon dating because the rare 14C isotopes can be separated from the stable 14N background that is 10 to 13 orders of magnitude larger, and only small amounts of the old and fragile organic samples are necessary for measurement. Our group focuses on this radiocarbon dating through AMS. When performing AMS, the sample needs to be loaded into a cathode at the back of an ion source in order to produce a beam from the material to be analyzed. For carbon samples, the material must first be converted into graphite in order to be loaded into the cathode. My role in the group is to convert the organic substances into graphite. In order to graphitize the samples, a sample is first combusted to form carbon dioxide gas and then purified and reduced into the graphite form. After a couple weeks of research and with the help of various Physics professors, I developed a plan and began to construct the setup necessary to perform the graphitization. Once the apparatus is fully completed, the carbon samples will be graphitized and loaded into the AMS machine for analysis.

  5. Effect of starting microstructure upon the nucleation sites and distribution of graphite particles during a graphitising anneal of an experimental medium-carbon machining steel

    Energy Technology Data Exchange (ETDEWEB)

    Inam, A., E-mail: aqil.ceet@pu.edu.pk; Brydson, R., E-mail: mtlrmdb@leeds.ac.uk; Edmonds, D.V., E-mail: d.v.edmonds@leeds.ac.uk

    2015-08-15

    The potential for using graphite particles as an internal lubricant during machining is considered. Graphite particles were found to form during graphitisation of experimental medium-carbon steel alloyed with Si and Al. The graphite nucleation sites were strongly influenced by the starting microstructure, whether ferrite–pearlite, bainite or martensite, as revealed by light and electron microscopy. Favourable nucleation sites in the ferrite–pearlite starting microstructure were, not unexpectedly, found to be located within pearlite colonies, no doubt due to the presence of abundant cementite as a source of carbon. In consequence, the final distribution of graphite nodules in ferrite–pearlite microstructures was less uniform than for the bainite microstructure studied. In the case of martensite, this study found a predominance of nucleation at grain boundaries, again leading to less uniform graphite dispersions. - Highlights: • Metallography of formation of graphite particles in experimental carbon steel. • Potential for using graphite in steel as an internal lubricant during machining. • Microstructure features expected to influence improved machinability studied. • Influence of pre-anneal starting microstructure on graphite nucleation sites. • Influence of pre-anneal starting microstructure on graphite distribution. • Potential benefit is new free-cutting steel compositions without e.g. Pb alloying.

  6. Graphite suspension in carbon dioxide

    International Nuclear Information System (INIS)

    Roche, R.

    1965-01-01

    Since 1963 the Atomic Division of SNECMA has been conducting, under a contract with the CEA, an experimental work with a two-component fluid comprised of carbon dioxide and small graphite particles. The primary purpose was the determination of basic engineering information pertaining to the stability and the flowability of the suspension. The final form of the experimental loop consists mainly of the following items: a light-phase compressor, a heavy-phase pump, an electrical-resistance type heater section, a cooling heat exchanger, a hairpin loop, a transparent test section and a separator. During the course of the testing, it was observed that the fluid could be circulated quite easily in a broad range of variation of the suspension density and velocity - density from 30 to 170 kg/m 3 and velocity from 2 to 24 m/s. The system could be restarted and circulation maintained without any difficulty, even with the heavy-phase pump alone. The graphite did not have a tendency to pack or agglomerate during operation. No graphite deposition was observed on the wall of the tubing. A long period run (250 hours) has shown the evolution of the particle dimensions. Starting with graphite of surface area around 20 m 2 /g (graphite particles about 1 μ), the powder surface area reaches an asymptotic value of 300 m 2 /g (all the particles less than 0.3 μ). Moisture effect on flow stability, flow distribution between two parallel channels, pressure drop in straight tubes, recompression ratio in diffusers were also investigated. (author) [fr

  7. Glassy carbon coated graphite for nuclear applications

    International Nuclear Information System (INIS)

    Delpeux S; Cacciaguerra T; Duclaux L

    2005-01-01

    glassy carbon presents a good adhesion appear smooth and non porous, therefore suggesting that glassy carbon deposition is an interesting route to shut off the open porosity on the surface of graphite pieces. Nevertheless, numbers of parameters have to be better understood: i.e. the optimal protocol to impregnate graphite by the resin, the role of the interface and the possibilities to control the resin shrinkage by adding additives (i.e. carbon black, graphite particles, carbon char,...) to the glassy carbon precursor. (authors)

  8. Glassy carbon coated graphite for nuclear applications

    Energy Technology Data Exchange (ETDEWEB)

    Delpeux, S.; Cacciaguerra, T.; Duclaux, L. [Orleans Univ., CRMD, CNRS, 45 (France)

    2005-07-01

    of the graphite substrate. The deposit regions where glassy carbon presents a good adhesion appear smooth and non porous, therefore suggesting that glassy carbon deposition is an interesting route to shut off the open porosity on the surface of graphite pieces (Fig 3). Nevertheless, numbers of parameters have to be better understood: i.e. the optimal protocol to impregnate graphite by the resin, the role of the interface and the possibilities to control the resin shrinkage by adding additives (i.e. carbon black, graphite particles, carbon char..) to the glassy carbon precursor. (authors)

  9. Erosion of common structural materials and the degradation of suspended particles in flowing suspension of graphite powder in carbon dioxide gas

    International Nuclear Information System (INIS)

    Garton, D.A.; Hawes, R.I.; Rose, P.W.

    1968-06-01

    Experiments have been performed to examine the erosion of common materials of construction by a flowing suspension of graphite powder in carbon dioxide gas and the degradation of the graphite powder in the suspension. The suspension was circulated through a stainless steel loop at a pressure of 200 p.s.i.g. and bulk fluid temperature of 100-150 deg. C. No change in the weight of pins of mild steel, stainless steel and zircaloy, which were placed across the flow stream in a region where the velocity approached 100 ft./sec, could be detected after 350 hours of circulation. Examination of micro-photographs of the cross sections of the specimens showed no change in the structure of the metals. Considerable erosion of graphite pins producing a 6% decrease in the weight was observed under similar conditions. Detailed spectrographic analysis of the suspended powder taken at various times during the experiment showed no noticeable increase in the impurity content which could be attributed to erosion of the test specimens. A considerable increase in the tungsten, tin and cobalt concentration was observed and this is attributed to wear of the pump seal surfaces. The mean particle size of the suspended graphite powder was observed to decrease rapidly from 5 microns to 3 microns after only a few hours of circulation in the loop. After this initial period there was little further change in the particle size, the mean diameter being 2.85 microns after 167 hours of circulation. (author)

  10. Graphite

    Science.gov (United States)

    Robinson, Gilpin R.; Hammarstrom, Jane M.; Olson, Donald W.; Schulz, Klaus J.; DeYoung,, John H.; Seal, Robert R.; Bradley, Dwight C.

    2017-12-19

    Graphite is a form of pure carbon that normally occurs as black crystal flakes and masses. It has important properties, such as chemical inertness, thermal stability, high electrical conductivity, and lubricity (slipperiness) that make it suitable for many industrial applications, including electronics, lubricants, metallurgy, and steelmaking. For some of these uses, no suitable substitutes are available. Steelmaking and refractory applications in metallurgy use the largest amount of produced graphite; however, emerging technology uses in large-scale fuel cell, battery, and lightweight high-strength composite applications could substantially increase world demand for graphite.Graphite ores are classified as “amorphous” (microcrystalline), and “crystalline” (“flake” or “lump or chip”) based on the ore’s crystallinity, grain-size, and morphology. All graphite deposits mined today formed from metamorphism of carbonaceous sedimentary rocks, and the ore type is determined by the geologic setting. Thermally metamorphosed coal is the usual source of amorphous graphite. Disseminated crystalline flake graphite is mined from carbonaceous metamorphic rocks, and lump or chip graphite is mined from veins in high-grade metamorphic regions. Because graphite is chemically inert and nontoxic, the main environmental concerns associated with graphite mining are inhalation of fine-grained dusts, including silicate and sulfide mineral particles, and hydrocarbon vapors produced during the mining and processing of ore. Synthetic graphite is manufactured from hydrocarbon sources using high-temperature heat treatment, and it is more expensive to produce than natural graphite.Production of natural graphite is dominated by China, India, and Brazil, which export graphite worldwide. China provides approximately 67 percent of worldwide output of natural graphite, and, as the dominant exporter, has the ability to set world prices. China has significant graphite reserves, and

  11. Graphitization in Carbon MEMS and Carbon NEMS

    Science.gov (United States)

    Sharma, Swati

    Carbon MEMS (CMEMS) and Carbon NEMS (CNEMS) are an emerging class of miniaturized devices. Due to the numerous advantages such as scalable manufacturing processes, inexpensive and readily available precursor polymer materials, tunable surface properties and biocompatibility, carbon has become a preferred material for a wide variety of future sensing applications. Single suspended carbon nanowires (CNWs) integrated on CMEMS structures fabricated by electrospinning of SU8 photoresist on photolithographially patterned SU8 followed by pyrolysis are utilized for understanding the graphitization process in micro and nano carbon materials. These monolithic CNW-CMEMS structures enable the fabrication of very high aspect ratio CNWs of predefined length. The CNWs thus fabricated display core---shell structures having a graphitic shell with a glassy carbon core. The electrical conductivity of these CNWs is increased by about 100% compared to glassy carbon as a result of enhanced graphitization. We explore various tunable fabrication and pyrolysis parameters to improve graphitization in the resulting CNWs. We also suggest gas-sensing application of the thus fabricated single suspended CNW-CMEMS devices by using the CNW as a nano-hotplate for local chemical vapor deposition. In this thesis we also report on results from an optimization study of SU8 photoresist derived carbon electrodes. These electrodes were applied to the simultaneous detection of traces of Cd(II) and Pb(II) through anodic stripping voltammetry and detection limits as low as 0.7 and 0.8 microgL-1 were achieved. To further improve upon the electrochemical behavior of the carbon electrodes we elucidate a modified pyrolysis technique featuring an ultra-fast temperature ramp for obtaining bubbled porous carbon from lithographically patterned SU8. We conclude this dissertation by suggesting the possible future works on enhancing graphitization as well as on electrochemical applications

  12. Tunable Graphitic Carbon Nano-Onions Development in Carbon Nanofibers for Multivalent Energy Storage

    Energy Technology Data Exchange (ETDEWEB)

    Schwarz, Haiqing L. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)

    2016-01-01

    We developed a novel porous graphitic carbon nanofiber material using a synthesis strategy combining electrospinning and catalytic graphitization. RF hydrogel was used as carbon precursors, transition metal ions were successfully introduced into the carbon matrix by binding to the carboxylate groups of a resorcinol derivative. Transition metal particles were homogeneously distributed throughout the carbon matrix, which are used as in-situ catalysts to produce graphitic fullerene-like nanostructures surrounding the metals. The success design of graphitic carbons with enlarged interlayer spacing will enable the multivalent ion intercalation for the development of multivalent rechargeable batteries.

  13. Nanostructured carbon films with oriented graphitic planes

    International Nuclear Information System (INIS)

    Teo, E. H. T.; Kalish, R.; Kulik, J.; Kauffmann, Y.; Lifshitz, Y.

    2011-01-01

    Nanostructured carbon films with oriented graphitic planes can be deposited by applying energetic carbon bombardment. The present work shows the possibility of structuring graphitic planes perpendicular to the substrate in following two distinct ways: (i) applying sufficiently large carbon energies for deposition at room temperature (E>10 keV), (ii) utilizing much lower energies for deposition at elevated substrate temperatures (T>200 deg. C). High resolution transmission electron microscopy is used to probe the graphitic planes. The alignment achieved at elevated temperatures does not depend on the deposition angle. The data provides insight into the mechanisms leading to the growth of oriented graphitic planes under different conditions.

  14. Technique for production of graphite-carbon products

    Energy Technology Data Exchange (ETDEWEB)

    Antonov, A.N.; Bentsianovskaya, I.A.; Filatova, V.A.; Nabokov, V.S.; Nestor, V.P.; Zil' bergleyt, I.M.

    1982-01-01

    The technique for producing carbon-graphite products that includes filtration under a pressure of 0.1-015 MPa (through graphite stock) of an aqueous carbon material with the addition of surfactant, drying, and subsequent thermal treatment, is simplified and made less lengthy. Oxidized graphite is utilized with a prior addition of 1-10% water-soluble organic substance into the suspension -molasses, hemicellulose, sugar or polyacrylamide. A 0.03-1.5% suspension of oxidized graphite is utilized, with a particle size of 0.02-0.1 mkm. Thermal processing is done in a carbon fill, at a rate of 10-20 degrees/hour to 700-800/sup 0/, maintained 2-3 hours.

  15. Sealing nuclear graphite with pyrolytic carbon

    International Nuclear Information System (INIS)

    Feng, Shanglei; Xu, Li; Li, Li; Bai, Shuo; Yang, Xinmei; Zhou, Xingtai

    2013-01-01

    Pyrolytic carbon (PyC) coatings were deposited on IG-110 nuclear graphite by thermal decomposition of methane at ∼1830 °C. The PyC coatings are anisotropic and airtight enough to protect IG-110 nuclear graphite against the permeation of molten fluoride salts and the diffusion of gases. The investigations indicate that the sealing nuclear graphite with PyC coating is a promising method for its application in Molten Salt Reactor (MSR)

  16. Nucleation and growth characteristics of graphite spheroids in bainite during graphitization annealing of a medium carbon steel

    International Nuclear Information System (INIS)

    Gao, J.X.; Wei, B.Q.; Li, D.D.; He, K.

    2016-01-01

    The evolution of microstructure in bainite during graphitization annealing at 680 °C of Jominy-quenched bars of an Al-Si bearing medium carbon (0.4C wt%) steel has been studied and compared with that in martensite by using light, scanning and transmission electron microscopy. The results show that the graphitization process in bainite is different from that in martensite in many aspects such as the initial carbon state, the behavior of cementite, the nucleation-growth feature and kinetics of formation of graphite spheroids during graphitization annealing, and the shape, size and distribution of these graphite spheroids. The fact that the graphitization in bainite can produce more homogeneous graphite spheroids with more spherical shape and finer size in a shorter annealing time without the help of preexisting coring particles implies that bainite should be a better starting structure than martensite for making graphitic steel. - Highlights: • This article presents a microstructural characterization of formation of graphite spheroids in bainite. • Nucleation and growth characteristics of graphite spheroids formed in bainite and martensite are compared. • Bainite should be a better starting structure for making graphitic steel as results show.

  17. The electrochemical properties of graphite and carbon

    International Nuclear Information System (INIS)

    Yeager, E.; Gupta, S.; Molla, J.A.

    1983-01-01

    Carbon and graphite are often used as supports for electrocatalysts, but also have an electrocatalytic function in such electrode reactions as O 2 reduction in alkaline electrolytes, Cl 2 generation in brine and SOCl 2 reduction in lithium-thionyl chloride batteries. These catalytic functions involve specific chemical functional groups bound to the carbon and graphite surfaces. The factors controlling O 2 reduction with various types of carbon electrodes of both low and high surface area are reviewed. Of particular importance is the role of hydrogen peroxide. The role of the functionality of the carbon in the electrocatalysis will be discussed

  18. Electronic structure of incident carbon ions on a graphite surface

    International Nuclear Information System (INIS)

    Kiuchi, Masato; Takeuchi, Takae; Yamamoto, Masao.

    1997-01-01

    The electronic structure of an incident carbon ion on a graphite surface is discussed on the basis of ab initio molecular orbital calculations. A carbon cation forms a covalent bond with the graphite, and a carbon nonion is attracted to the graphite surface through van der Waals interaction. A carbon anion has no stable state on a graphite surface. The charge effects of incident ions become clear upon detailed examination of the electronic structure. (author)

  19. Dependence of strength on particle size in graphite

    International Nuclear Information System (INIS)

    Kennedy, E.P.; Kennedy, C.R.

    The strength to particle size relationship for specially fabricated graphites has been demonstrated and rationalized using fracture mechanics. In the past, similar studies have yielded empirical data using only commercially available material. Thus, experimental verification of these relationships has been difficult. However, the graphites of this study were fabricated by controlling the particle size ranges for a series of isotropic graphites. All graphites that were evaluated had a constant 1.85 g/cm 3 density. Thus, particle size was the only variable. This study also considered the particle size effect on other physical properties; coefficient of thermal expansion (CTE), electrical resistivity, fracture strain, and Young's modulus

  20. Enhancing thermal conductivity of fluids with graphite nanoparticles and carbon nanotube

    Science.gov (United States)

    Zhang, Zhiqiang [Lexington, KY; Lockwood, Frances E [Georgetown, KY

    2008-03-25

    A fluid media such as oil or water, and a selected effective amount of carbon nanomaterials necessary to enhance the thermal conductivity of the fluid. One of the preferred carbon nanomaterials is a high thermal conductivity graphite, exceeding that of the neat fluid to be dispersed therein in thermal conductivity, and ground, milled, or naturally prepared with mean particle size less than 500 nm, and preferably less than 200 nm, and most preferably less than 100 nm. The graphite is dispersed in the fluid by one or more of various methods, including ultrasonication, milling, and chemical dispersion. Carbon nanotubes with graphitic structure is another preferred source of carbon nanomaterial, although other carbon nanomaterials are acceptable. To confer long term stability, the use of one or more chemical dispersants is preferred. The thermal conductivity enhancement, compared to the fluid without carbon nanomaterial, is proportional to the amount of carbon nanomaterials (carbon nanotubes and/or graphite) added.

  1. An Experiment on the Carbonization of Fuel Compact Matrix Graphite for HTGR

    International Nuclear Information System (INIS)

    Lee, Young Woo; Kim, Joo Hyoung; Cho, Moon Sung

    2012-01-01

    The fuel element for HTGR is manufactured by mixing coated fuel particles with matrix graphite powder and forming into either pebble type or cylindrical type compacts depending on their use in different HTGR cores. The coated fuel particle, the so-called TRISO particle, consists of 500-μm spherical UO 2 particles coated with the low density buffer Pyrolytic Carbon (PyC) layer, the inner and outer high density PyC layer and SiC layer sandwiched between the two inner and outer PyC layers. The coated TRISO particles are mixed with a properly prepared matrix graphite powder, pressed into a spherical shape or a cylindrical compact, and finally heat-treated at about 1800 .deg. C. These fuel elements can have different sizes and forms of compact. The basic steps for manufacturing a fuel element include preparation of graphite matrix powder, over coating the fuel particles, mixing the fuel particles with a matrix powder, carbonizing green compact, and the final high-temperature heat treatment of the carbonized fuel compact. The carbonization is a process step where the binder that is incorporated during the matrix graphite powder preparation step is evaporated and the residue of the binder is carbonized during the heat treatment at about 1073 K, In order to develop a fuel compact fabrication technology, and for fuel matrix graphite to meet the required material properties, it is of extreme importance to investigate the relationship among the process parameters of the matrix graphite powder preparation, fabrication parameters of fuel element green compact and the carbonization condition, which has a strong influence on further steps and the material properties of fuel element. In this work, the carbonization behavior of green compact samples prepared from the matrix graphite powder mixtures with different binder materials was investigated in order to elucidate the behavior of binders during the carbonization heat treatment by analyzing the change in weight, density and its

  2. Synthesis of graphitic carbon nitride by reaction of melamine and uric acid

    International Nuclear Information System (INIS)

    Dante, Roberto C.; Martin-Ramos, Pablo; Correa-Guimaraes, Adriana; Martin-Gil, Jesus

    2011-01-01

    Highlights: → Graphitic carbon nitrides by CVD of melamine and uric acid on alumina. → The building blocks of carbon nitrides are heptazine nuclei. → Composite particles with alumina core and carbon nitride coating. - Abstract: Graphitic carbon nitrides were synthesized starting from melamine and uric acid. Uric acid was chosen because it thermally decomposes, and reacts with melamine by condensation at temperatures in the range of 400-600 deg. C. The reagents were mixed with alumina and subsequently the samples were treated in an oven under nitrogen flux. Alumina favored the deposition of the graphitic carbon nitrides layers on the exposed surface. This method can be assimilated to an in situ chemical vapor deposition (CVD). Infrared (IR) spectra, as well as X-ray diffraction (XRD) patterns, are in accordance with the formation of a graphitic carbon nitride with a structure based on heptazine blocks. These carbon nitrides exhibit poor crystallinity and a nanometric texture, as shown by transmission electron microscopy (TEM) analysis. The thermal degradation of the graphitic carbon nitride occurs through cyano group formation, and involves the bridging tertiary nitrogen and the bonded carbon, which belongs to the heptazine ring, causing the ring opening and the consequent network destruction as inferred by connecting the IR and X-ray photoelectron spectroscopy (XPS) results. This seems to be an easy and promising route to synthesize graphitic carbon nitrides. Our final material is a composite made of an alumina core covered by carbon nitride layers.

  3. Effect of graphite target power density on tribological properties of graphite-like carbon films

    Science.gov (United States)

    Dong, Dan; Jiang, Bailing; Li, Hongtao; Du, Yuzhou; Yang, Chao

    2018-05-01

    In order to improve the tribological performance, a series of graphite-like carbon (GLC) films with different graphite target power densities were prepared by magnetron sputtering. The valence bond and microstructure of films were characterized by AFM, TEM, XPS and Raman spectra. The variation of mechanical and tribological properties with graphite target power density was analyzed. The results showed that with the increase of graphite target power density, the deposition rate and the ratio of sp2 bond increased obviously. The hardness firstly increased and then decreased with the increase of graphite target power density, whilst the friction coefficient and the specific wear rate increased slightly after a decrease with the increasing graphite target power density. The friction coefficient and the specific wear rate were the lowest when the graphite target power density was 23.3 W/cm2.

  4. Improvement on the electrochemical characteristics of graphite anodes by coating of the pyrolytic carbon using tumbling chemical vapor deposition

    International Nuclear Information System (INIS)

    Han, Young-Soo; Lee, Jai-Young

    2003-01-01

    The electrochemical characteristics of graphite coated with pyrolytic carbon materials using tumbling chemical vapor deposition (CVD) process have been studied for the active material of anodes in lithium ion secondary batteries. Coating of pyrolytic carbons on the surface of graphite particles, which tumble in a rotating reactor tube, was performed through the pyrolysis of liquid propane gas (LPG). The surface morphology of these graphite particles coated with pyrolytic carbon has been observed with scanning electron microscopy (SEM). The surface of graphite particles can well be covered with pyrolytic carbon by tumbling CVD. High-resolution transmission electron microscopy (HRTEM) image of these carbon particles shows that the core part is highly ordered carbon, while the shell part is disordered carbon. We have found that the new-type carbon obtained from tumbling CVD has a uniform core (graphite)-shell (pyrolytic carbon) structure. The electrochemical property of the new-type carbons has been examined using a charge-discharge cycler. The coating of pyrolytic carbon on the surface of graphite can effectively reduce the initial irreversible capacity by 47.5%. Cyclability and rate-capability of theses carbons with the core-shell structure are much better than those of bare graphite. From electrochemical impedance spectroscopy (EIS) spectra, it is found that the coating of pyrolytic carbon on the surface of graphite causes the decrease of the contact resistance in the carbon electrodes, which means the formation of solid electrolyte interface (SEI) layer is suppressed. We suggest that coating of pyrolytic carbon by the tumbling CVD is an effective method in improving the electrochemical properties of graphite electrodes for lithium ion secondary batteries

  5. Coating of graphite flakes with MgO/carbon nanocomposite via gas state reaction

    Energy Technology Data Exchange (ETDEWEB)

    Sharif, M., E-mail: Sharif_m@metaleng.iust.ac.i [Iran University of Science and Technology, Tehran (Iran, Islamic Republic of); Faghihi-Sani, M.A. [Sharif University of Technology, Tehran (Iran, Islamic Republic of); Golestani-Fard, F. [Iran University of Science and Technology, Tehran (Iran, Islamic Republic of); Saberi, A. [Tabriz University (Iran, Islamic Republic of); Soltani, Ali Khalife [Iran University of Science and Technology, Tehran (Iran, Islamic Republic of)

    2010-06-18

    Coating of graphite flakes with MgO/carbon nanocomposite was carried out via gaseous state reaction between mixture of Mg metal, CO gas and graphite flakes at 1000 {sup o}C. XRD and FE-SEM analysis of coating showed that the coating was comprised of MgO nano particles and amorphous carbon distributed smoothly and covered the graphite surface evenly. Thermodynamic calculations were employed to predict the reaction sequences as well as phase stability. The effect of coating on water wettability and oxidation resistance of graphite was studied using contact angle measurement and TG analysis, respectively. It was demonstrated that the reaction between Mg and CO could result in MgO/C nanocomposite deposition. The coating improved water wettability of graphite and also enhanced the oxidation resistance of graphite flakes significantly. Also the graphite coating showed significant phenolic resin-wettabilty owing to high surface area of such hydrophilic nano composite coating. The importance of graphite coating is explained with emphasis on its potential application in graphite containing refractories.

  6. Coating of graphite flakes with MgO/carbon nanocomposite via gas state reaction

    International Nuclear Information System (INIS)

    Sharif, M.; Faghihi-Sani, M.A.; Golestani-Fard, F.; Saberi, A.; Soltani, Ali Khalife

    2010-01-01

    Coating of graphite flakes with MgO/carbon nanocomposite was carried out via gaseous state reaction between mixture of Mg metal, CO gas and graphite flakes at 1000 o C. XRD and FE-SEM analysis of coating showed that the coating was comprised of MgO nano particles and amorphous carbon distributed smoothly and covered the graphite surface evenly. Thermodynamic calculations were employed to predict the reaction sequences as well as phase stability. The effect of coating on water wettability and oxidation resistance of graphite was studied using contact angle measurement and TG analysis, respectively. It was demonstrated that the reaction between Mg and CO could result in MgO/C nanocomposite deposition. The coating improved water wettability of graphite and also enhanced the oxidation resistance of graphite flakes significantly. Also the graphite coating showed significant phenolic resin-wettabilty owing to high surface area of such hydrophilic nano composite coating. The importance of graphite coating is explained with emphasis on its potential application in graphite containing refractories.

  7. Graphite suspension in carbon dioxide; Suspension de graphite dans le gaz carbonique

    Energy Technology Data Exchange (ETDEWEB)

    Roche, R [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires; Moussez, C; Rouvillois, X; Brevet, R [Societe Nationale d' Etude et de Construction de Moteurs d' Aviation (SNECMA), 75 - Paris (France)

    1965-07-01

    Since 1963 the Atomic Division of SNECMA has been conducting, under a contract with the CEA, an experimental work with a two-component fluid comprised of carbon dioxide and small graphite particles. The primary purpose was the determination of basic engineering information pertaining to the stability and the flowability of the suspension. The final form of the experimental loop consists mainly of the following items: a light-phase compressor, a heavy-phase pump, an electrical-resistance type heater section, a cooling heat exchanger, a hairpin loop, a transparent test section and a separator. During the course of the testing, it was observed that the fluid could be circulated quite easily in a broad range of variation of the suspension density and velocity - density from 30 to 170 kg/m{sup 3} and velocity from 2 to 24 m/s. The system could be restarted and circulation maintained without any difficulty, even with the heavy-phase pump alone. The graphite did not have a tendency to pack or agglomerate during operation. No graphite deposition was observed on the wall of the tubing. A long period run (250 hours) has shown the evolution of the particle dimensions. Starting with graphite of surface area around 20 m{sup 2}/g (graphite particles about 1 {mu}), the powder surface area reaches an asymptotic value of 300 m{sup 2}/g (all the particles less than 0.3 {mu}). Moisture effect on flow stability, flow distribution between two parallel channels, pressure drop in straight tubes, recompression ratio in diffusers were also investigated. (author) [French] Depuis 1963 la Division Atomique de la SNECMA conduit, dans le cadre d'un contrat avec le Commissariat A l'Energie Atomique, l'etude experimentale d'une suspension de fines particules de graphite dans le gaz carbonique. L'objectif principal est d'obtenir des informations d'ordre mecanique et technologique sur la mise en oeuvre de l'ecoulement de ce fluide diphase. Le circuit experimental comprend principalement: un

  8. Carbon Nanotubes Growth by CVD on Graphite Fibers

    Science.gov (United States)

    Zhu, Shen; Su, Ching-Hua; Cochrane, J. C.; Lehoczky, S. L.; Muntele, I.; Ila, D.; Curreri, Peter A. (Technical Monitor)

    2002-01-01

    Due to the superior electrical and mechanical properties of carbon nanotubes (CNT), synthesizing CNT on various substances for electronics devices and reinforced composites have been engaged in many efforts for applications. This presentation will illustrate CNT synthesized on graphite fibers by thermal CVD. On the fiber surface, iron nanoparticles as catalysts for CNT growth are coated. The growth temperature ranges from 600 to 1000 C and the pressure ranges from 100 Torr to one atmosphere. Methane and hydrogen gases with methane content of 10% to 100% are used for the CNT synthesis. At high growth temperatures (greater than or equal to 900 C), the rapid inter-diffusion of the transition metal iron on the graphite surface results in the rough fiber surface without any CNT grown on it. When the growth temperature is relative low (650-800 C), CNT with catalytic particles on the nanotube top ends are fabricated on the graphite surface. (Methane and hydrogen gases with methane content of 10% to 100% are used for the CNT synthesis.) (By measuring the samples) Using micro Raman spectroscopy in the breath mode region, single-walled or multi-walled CNT (MWCNT), depending on growth concentrations, are found. Morphology, length and diameter of these MWCNT are determined by scanning electron microscopy and Raman spectroscopy. The detailed results of syntheses and characterizations will be discussed in the presentation.

  9. Topological Characterization of Carbon Graphite and Crystal Cubic Carbon Structures.

    Science.gov (United States)

    Siddiqui, Wei Gao Muhammad Kamran; Naeem, Muhammad; Rehman, Najma Abdul

    2017-09-07

    Graph theory is used for modeling, designing, analysis and understanding chemical structures or chemical networks and their properties. The molecular graph is a graph consisting of atoms called vertices and the chemical bond between atoms called edges. In this article, we study the chemical graphs of carbon graphite and crystal structure of cubic carbon. Moreover, we compute and give closed formulas of degree based additive topological indices, namely hyper-Zagreb index, first multiple and second multiple Zagreb indices, and first and second Zagreb polynomials.

  10. High-performance supercapacitors based on hierarchically porous graphite particles

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Zheng; Wen, Jing; Yan, Chunzhu; Rice, Lynn; Sohn, Hiesang; Lu, Yunfeng [Department of Chemical and Biomolecular Engineering, University of California, Los Angeles, CA 90095 (United States); Shen, Meiqing [School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300072 (China); Cai, Mei [General Motor R and D Center, Warren, MI 48090 (United States); Dunn, Bruce [Department of Materials Science and Engineering, University of California, Los Angeles, CA 90095 (United States)

    2011-07-15

    Hierarchically porous graphite particles are synthesized using a continuous, scalable aerosol approach. The unique porous graphite architecture provides the particles with high surface area, fast ion transportation, and good electronic conductivity, which endows the resulting supercapacitors with high energy and power densities. This work provides a new material platform for high-performance supercapacitors with high packing density, and is adaptable to battery electrodes, fuel-cell catalyst supports, and other applications. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  11. New insights into canted spiro carbon interstitial in graphite

    Science.gov (United States)

    EL-Barbary, A. A.

    2017-12-01

    The self-interstitial carbon is the key to radiation damage in graphite moderator nuclear reactor, so an understanding of its behavior is essential for plant safety and maximized reactor lifetime. The density functional theory is applied on four different graphite unit cells, starting from of 64 carbon atoms up to 256 carbon atoms, using AIMPRO code to obtain the energetic, athermal and mechanical properties of carbon interstitial in graphite. This study presents first principles calculations of the energy of formation that prove its high barrier to athermal diffusion (1.1 eV) and the consequent large critical shear stress (39 eV-50 eV) necessary to shear graphite planes in its presence. Also, for the first time, the gamma surface of graphite in two dimensions is calculated and found to yield the critical shear stress for perfect graphite. Finally, in contrast to the extensive literature describing the interstitial of carbon in graphite as spiro interstitial, in this work the ground state of interstitial carbon is found to be canted spiro interstitial.

  12. Spherical cauliflower-like carbon dust formed by interaction between deuterium plasma and graphite target and its internal structure

    Energy Technology Data Exchange (ETDEWEB)

    Ohno, N. [Department of Energy Engineering and Science, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya 464-8603 (Japan)], E-mail: ohno@ees.nagoya-u.ac.jp; Yoshimi, M. [Department of Energy Engineering and Science, Graduate School of Engineering, Nagoya University, Furo-cho, Chikusa-ku, Nagoya 464-8603 (Japan); Tokitani, M. [National Institute for Fusion Science, Oroshi 322-6, Toki 509-5292 (Japan); Takamura, S. [Department of Electronics, Aichi Institute of Technology, Yakusa-cho, Toyota 470-0392 (Japan); Tokunaga, K.; Yoshida, N. [Research Institute for Applied Mechanics, Kyushu University, Kasuga, Fukuoka 816-8580 (Japan)

    2009-06-15

    Simulated experiments to produce carbon dust particles with cauliflower structure have been performed in a liner plasma device, NAGDIS-II by exposing high density deuterium plasma to a graphite sample (IG-430U). Formation of carbon dust depends on the surface temperature and the incident ion energy. At a surface temperature 600-700 K, a lot of isolated spherical dust particles are observed on the graphite target. The internal structure of an isolated dust particle was observed with Focused Ion Beam (FIB) system and Transmission Electron Microscope (TEM) in detail. FIB analysis clearly shows there exist honey-combed cell structure with thin carbon walls in the dust particle and the dust particle grows from the graphite surface. TEM image also shows that the dust particle is made of amorphous carbon with crystallized grains with diameters of 10-50 nm.

  13. Graphitic Carbon Foam Structural Cores and Multifunctional Applications

    Data.gov (United States)

    National Aeronautics and Space Administration — Graphitic carbon foams include a family of material forms and products with mechanical, thermal, and electrical properties that are tailor-able over a wide range....

  14. Effect of thermal annealing on property changes of neutron-irradiated non-graphitized carbon materials and nuclear graphite

    International Nuclear Information System (INIS)

    Matsuo, Hideto

    1991-06-01

    Changes in dimension of non-graphitized carbon materials and nuclear graphite, and the bulk density, electrical resistivity, Young's modulus and thermal expansivity of nuclear graphite were studied after neutron irradiation at 1128-1483 K and the successive thermal annealing up to 2573 K. Carbon materials showed larger and anisotropic dimensional shrinkage than that of nuclear graphite after the irradiation. The irradiation-induced dimensional shrinkage of carbon materials decreased during annealing at temperatures from 1773 to 2023 K, followed by a slight increase at higher temperatures. On the other hand, the irradiated nuclear graphite hardly showed the changes in length, density and thermal expansivity under the thermal annealing, but the electrical resistivity and Young's modulus showed a gradual decrease with annealing temperature. It has been clarified that there exists significant difference in the effect of thermal annealing on irradiation-induced dimensional shrinkage between graphitized nuclear graphite and non-graphitized carbon materials. (author)

  15. Graphitic carbon nitride based nanocomposites: a review

    Science.gov (United States)

    Zhao, Zaiwang; Sun, Yanjuan; Dong, Fan

    2014-11-01

    Graphitic carbon nitride (g-C3N4), as an intriguing earth-abundant visible light photocatalyst, possesses a unique two-dimensional structure, excellent chemical stability and tunable electronic structure. Pure g-C3N4 suffers from rapid recombination of photo-generated electron-hole pairs resulting in low photocatalytic activity. Because of the unique electronic structure, the g-C3N4 could act as an eminent candidate for coupling with various functional materials to enhance the performance. According to the discrepancies in the photocatalytic mechanism and process, six primary systems of g-C3N4-based nanocomposites can be classified and summarized: namely, the g-C3N4 based metal-free heterojunction, the g-C3N4/single metal oxide (metal sulfide) heterojunction, g-C3N4/composite oxide, the g-C3N4/halide heterojunction, g-C3N4/noble metal heterostructures, and the g-C3N4 based complex system. Apart from the depiction of the fabrication methods, heterojunction structure and multifunctional application of the g-C3N4-based nanocomposites, we emphasize and elaborate on the underlying mechanisms in the photocatalytic activity enhancement of g-C3N4-based nanocomposites. The unique functions of the p-n junction (semiconductor/semiconductor heterostructures), the Schottky junction (metal/semiconductor heterostructures), the surface plasmon resonance (SPR) effect, photosensitization, superconductivity, etc. are utilized in the photocatalytic processes. Furthermore, the enhanced performance of g-C3N4-based nanocomposites has been widely employed in environmental and energetic applications such as photocatalytic degradation of pollutants, photocatalytic hydrogen generation, carbon dioxide reduction, disinfection, and supercapacitors. This critical review ends with a summary and some perspectives on the challenges and new directions in exploring g-C3N4-based advanced nanomaterials.

  16. Preparation and characterization of flake graphite/silicon/carbon spherical composite as anode materials for lithium-ion batteries

    International Nuclear Information System (INIS)

    Lai Jun; Guo Huajun; Wang Zhixing; Li Xinhai; Zhang Xiaoping; Wu Feixiang; Yue Peng

    2012-01-01

    Highlights: ► Flake graphite/silicon/carbon composite is synthesized via spray drying. ► Flake graphite of ∼0.5 μm and glucose are used to prepare the composite. ► The as-prepared composite shows spherical and porous appearance. ► The composite shows nearly the same cycleability as commercial graphite in 20 cycles. ► The composite shows a reversible capacity of 552 mAh/g at the 20th cycle. - Abstract: Using nano-Si, glucose and flake graphite of ∼0.5 μm as raw materials, flake graphite/silicon/carbon composite is successfully synthesized via spray drying and subsequent pyrolysis. The samples are characterized by XRD, SEM, TEM and electrochemical measurements. The composite is composed of flake graphite, nano-Si and amorphous glucose-pyrolyzed carbon and presents good spherical appearance. Some micron pores arising from the decomposition of glucose exist on the surface of the composite particles. The composite has a high reversible capacity of 602.7 mAh/g with an initial coulombic efficiency of 69.71%, and shows nearly the same cycleability as the commercial graphite in 20 cycles. Both the glucose-pyrolyzed carbon and the micron pores play important roles in improving the cycleability of the composite. The flake graphite/silicon/carbon composite electrode is a potential alternative to graphite for high energy-density lithium ion batteries.

  17. Carburization in fluidized bed of carbon-graphite materials

    Energy Technology Data Exchange (ETDEWEB)

    Murav' ev, V I

    1977-01-01

    A study has been made of the diffusion saturation with carbon of the surface of titanium alloy VT1-1, molybdenum and 08KP steel with respect to the type of carbographitic materials, methods of pseudoliquefaction and heating in the temperature interval 800 to 1100/sup 0/ deg C. Used as the carburizing materials have been charcoal, acetylene black, charcoal carburizer, graphitized particles, pyrobenzene. The maximum carburizing effect is shown to be possessed by charcoal, the minimum effect - by acetylene black. Carburization in the pseudoliquid layer is 5 to 7 times as intensive as in the case of gas cementation and in a solid carburizer. No oxidation of the materials and hydrogenation of titanium has been observed in the temperature interval under study.

  18. Graphitized biogas-derived carbon nanofibers as anodes for lithium-ion batteries

    International Nuclear Information System (INIS)

    Cuesta, Nuria; Cameán, Ignacio; Ramos, Alberto; García, Ana B.

    2016-01-01

    The electrochemical performance as potential anodes for lithium-ion batteries of graphitized biogas-derived carbon nanofibers (BCNFs) is investigated by galvanostatic cycling versus Li/Li + at different electrical current densities. These graphitic nanomaterials have been prepared by high temperature treatment of carbon nanofibers produced in the catalytic decomposition of biogas. At low current density, they deliver specific capacities comparable to that of oil-derived micrometric graphite, the capacity retention values being mostly in the range 70-80% and cycling efficiency ∼ 100%. A clear tendency of the anode capacity to increase alongside the BCNFs crystal thickness was observed. Besides the degree of graphitic tri-dimensional structural order, the presence of loops between the adjacent edges planes on the graphene layers, the mesopore volume and the active surface area of the graphitized BCNFs were found to influence on battery reversible capacity, capacity retention along cycling and irreversible capacity. Furthermore, provided that the development of the crystalline structure is comparable, the graphitized BCNFs studied show better electrochemical rate performance than micrometric graphite. Therefore, this result can be associated with the nanometric particle size as well as the larger surface area of the BCNFs which, respectively, reduces the diffusion time of the lithium ions for the intercalation/de-intercalation processes, i.e. faster charge-discharge rate, and increases the contact area at the anode active material/electrolyte interface which may improve the Li + ions access, i.e. charge transfer reaction.

  19. Carbon nanostructures obtained by underwater arc discharge of graphite electrodes: Synthesis and characterization

    International Nuclear Information System (INIS)

    Darias Gonzalez, J. G.; Hernandez Tabare, L.; Herrera Palma, V.; Sierra Trujillo, J. S.; Desdin Garcia, L. F.; Codorniu Pujals, D.; Bermudez Martinez, A.; Arias de Fuentes, O.; Maury Toledo, A.

    2015-01-01

    In the present work, the application of the method of underwater arc discharge of graphite electrodes for obtaining several carbon nano structures is described. The analysis of the obtained products by Transmission Electron Microscopy (TEM), Scanning Electron Microscopy (SEM), Raman spectroscopy, Atomic Force Microscopy (AFM) and X-Ray Diffraction (XRD) showed that the samples collected from the material floating on the water surface were composed mainly by polyhedral onion-like particles, while those taken from the precipitate were a mixture multi walled nano-tubes, onion-like particles and other graphitic structures. The main features of the obtained nano structures are discussed. (Author)

  20. Graphitic Nitrogen Triggers Red Fluorescence in Carbon Dots.

    Science.gov (United States)

    Holá, Kateřina; Sudolská, Mária; Kalytchuk, Sergii; Nachtigallová, Dana; Rogach, Andrey L; Otyepka, Michal; Zbořil, Radek

    2017-12-26

    Carbon dots (CDs) are a stable and highly biocompatible fluorescent material offering great application potential in cell labeling, optical imaging, LED diodes, and optoelectronic technologies. Because their emission wavelengths provide the best tissue penetration, red-emitting CDs are of particular interest for applications in biomedical technologies. Current synthetic strategies enabling red-shifted emission include increasing the CD particle size (sp 2 domain) by a proper synthetic strategy and tuning the surface chemistry of CDs with suitable functional groups (e.g., carboxyl). Here we present an elegant route for preparing full-color CDs with well-controllable fluorescence at blue, green, yellow, or red wavelengths. The two-step procedure involves the synthesis of a full-color-emitting mixture of CDs from citric acid and urea in formamide followed by separation of the individual fluorescent fractions by column chromatography based on differences in CD charge. Red-emitting CDs, which had the most negative charge, were separated as the last fraction. The trend in the separation, surface charge, and red-shift of photoluminescence was caused by increasing amount of graphitic nitrogen in the CD structure, as was clearly proved by XPS, FT-IR, Raman spectroscopy, and DFT calculations. Importantly, graphitic nitrogen generates midgap states within the HOMO-LUMO gap of the undoped systems, resulting in significantly red-shifted light absorption that in turn gives rise to fluorescence at the low-energy end of the visible spectrum. The presented findings identify graphitic nitrogen as another crucial factor that can red-shift the CD photoluminescence.

  1. Graphite and carbon/carbon components for hot gas ducts

    International Nuclear Information System (INIS)

    Popp, G.; Gruber, U.; Boeder, H.; Janssen, K.

    1984-01-01

    The large coal reserves in the Federal Republic of Germany and the uncertainty of the future energy situation on the world market make it appear sound policy to devote some thought to the gasification of coal. For certain chemical processes, moreover, it would be advantageous to have a reasonably priced source of process heat available. In the Federal Republic of Germany this process heat shall be produced in a high-temperature nuclear reactor (HTR), the primary heating temperatures being in the range between 950 deg. C and 1050 deg. C. One serious problem in utilisation of high temperature heat is the resistance of the construction materials. Ceramic materials with high temperature resistance are considered. The material includes graphite and CC carbon fibre reinforced carbon. As a result of the project promoted by Ministerium fur Wirtschaft (Federal Republic of Germany) it has been demonstrated that both CC and graphite manufactured by SIGRI GmbH are well suited for use in high temperature reactors

  2. Influence of Particle Size on Properties of Expanded Graphite

    Directory of Open Access Journals (Sweden)

    Kurajica, S

    2010-02-01

    Full Text Available Expanded graphite has been applied widely in thermal insulation, adsorption, vibration damping, gasketing, electromagnetic interference shielding etc. It is made by intercalation of natural flake graphite followed by thermal expansion. Intercalation is a process whereby an intercalant material is inserted between the graphene layers of a graphite crystal. Exfoliation, a huge unidirectional expansion of the starting intercalated flakes, occurs when the graphene layers are forced apart by the sudden decomposition and vaporization of the intercalated species by thermal shock. Along with production methodologies, such as the intercalation process and heat treatment, the raw material characteristics, especially particle size, strongly influence the properties of the final product.This report evaluates the influence of the particle size of the raw material on the intercalation and expansion processes and consequently the properties of the exfoliated graphite. Natural crystalline flake graphite with wide particle diameter distribution (between dp = 80 and 425 µm was divided into four size-range portions by sieving. Graphite was intercalated via perchloric acid, glacial acetic acid and potassium dichromate oxidation and intercalation procedure. 5.0 g of graphite, 7.0 g of perchloric acid, 4.0 g of glacial acetic acid and 2.0 g of potassium dichromate were placed in glass reactor. The mixture was stirred with n = 200 min–1 at temperature of 45 °C during 60 min. Then it was filtered and washed with distilled water until pH~6 and dried at 60 °C during 24 h. Expansion was accomplished by thermal shock at 1000 °C for 1 min. The prepared samples were characterized by means of exfoliation volume measurements, simultaneous differential thermal analysis and thermo-gravimetry (DTA/TGA, X-ray diffraction (XRD, Fourier transform infrared spectroscopy (FTIR, BET measurements and scanning electron microscopy (SEM.X-ray diffraction indicated a change of distance

  3. Improved graphite matrix for coated-particle fuel

    International Nuclear Information System (INIS)

    Schell, D.H.; Davidson, K.V.

    1978-10-01

    An experimental process was developed to incorporate coated fuel particles in an extruded graphite matrix. This structure, containing 41 vol% particles, had a high matrix density, >1.6 g/cm 3 , and a matrix conductivity three to four times that of a pitch-injected fuel rod at 1775 K. Experiments were conducted to determine the uniformity of particle loadings in extrusions. Irradiation specimens were supplied for five tests in the High-Fluence Isotope Reactor at the Oak Ridge National Laboratory

  4. Controlled synthesis of graphitic carbon-encapsulated α-Fe2O3 nanocomposite via low-temperature catalytic graphitization of biomass and its lithium storage property

    International Nuclear Information System (INIS)

    Wu, Feng; Huang, Rong; Mu, Daobin; Wu, Borong; Chen, Yongjian

    2016-01-01

    Highlights: • Facile synthesis of graphitic carbon/α-Fe 2 O 3 nano-sized anode composite. • In situ low temperature catalytic graphitization of biomass material. • Onion-like graphitic carbon layers conformally encapsulating around α-Fe 2 O 3 core. • High lithium storage properties, especially, outstanding cycle performance. - Abstract: A delicate structure of graphitic carbon-encapsulated α-Fe 2 O 3 nanocomposite is in situ constructed via “Absorption–Catalytic graphitization–Oxidation” strategy, taking use of biomass matter of degreasing cotton as carbon precursor and solution reservoir. With the assistance of the catalytic graphitization effect of iron core, onion-like graphitic carbon (GC) shell is made directly from the biomass at low temperature (650 °C). The nanosized α-Fe 2 O 3 particles would effectively mitigate volumetric strain and shorten Li + transport path during charge/discharge process. The graphitic carbon shells may promote charge transfer and protect active particles from directly exposing to electrolyte to maintain interfacial stability. As a result, the as-prepared α-Fe 2 O 3 @GC composite displays an outstanding cycle performance with a reversible capacity of 1070 mA h g −1 after 430 cycles at 0.2C, as well as a good rate capability of ∼ 950 mA h g −1 after 100 cycles at 1C and ∼ 850 mA h g −1 even up to 200 cycles at a 2C rate.

  5. Large-scale preparation of hollow graphitic carbon nanospheres

    International Nuclear Information System (INIS)

    Feng, Jun; Li, Fu; Bai, Yu-Jun; Han, Fu-Dong; Qi, Yong-Xin; Lun, Ning; Lu, Xi-Feng

    2013-01-01

    Hollow graphitic carbon nanospheres (HGCNSs) were synthesized on large scale by a simple reaction between glucose and Mg at 550 °C in an autoclave. Characterization by X-ray diffraction, Raman spectroscopy and transmission electron microscopy demonstrates the formation of HGCNSs with an average diameter of 10 nm or so and a wall thickness of a few graphenes. The HGCNSs exhibit a reversible capacity of 391 mAh g −1 after 60 cycles when used as anode materials for Li-ion batteries. -- Graphical abstract: Hollow graphitic carbon nanospheres could be prepared on large scale by the simple reaction between glucose and Mg at 550 °C, which exhibit superior electrochemical performance to graphite. Highlights: ► Hollow graphitic carbon nanospheres (HGCNSs) were prepared on large scale at 550 °C ► The preparation is simple, effective and eco-friendly. ► The in situ yielded MgO nanocrystals promote the graphitization. ► The HGCNSs exhibit superior electrochemical performance to graphite.

  6. Large-scale preparation of hollow graphitic carbon nanospheres

    Energy Technology Data Exchange (ETDEWEB)

    Feng, Jun; Li, Fu [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061 (China); Bai, Yu-Jun, E-mail: byj97@126.com [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061 (China); State Key laboratory of Crystal Materials, Shandong University, Jinan 250100 (China); Han, Fu-Dong; Qi, Yong-Xin; Lun, Ning [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials, Ministry of Education, Shandong University, Jinan 250061 (China); Lu, Xi-Feng [Lunan Institute of Coal Chemical Engineering, Jining 272000 (China)

    2013-01-15

    Hollow graphitic carbon nanospheres (HGCNSs) were synthesized on large scale by a simple reaction between glucose and Mg at 550 Degree-Sign C in an autoclave. Characterization by X-ray diffraction, Raman spectroscopy and transmission electron microscopy demonstrates the formation of HGCNSs with an average diameter of 10 nm or so and a wall thickness of a few graphenes. The HGCNSs exhibit a reversible capacity of 391 mAh g{sup -1} after 60 cycles when used as anode materials for Li-ion batteries. -- Graphical abstract: Hollow graphitic carbon nanospheres could be prepared on large scale by the simple reaction between glucose and Mg at 550 Degree-Sign C, which exhibit superior electrochemical performance to graphite. Highlights: Black-Right-Pointing-Pointer Hollow graphitic carbon nanospheres (HGCNSs) were prepared on large scale at 550 Degree-Sign C Black-Right-Pointing-Pointer The preparation is simple, effective and eco-friendly. Black-Right-Pointing-Pointer The in situ yielded MgO nanocrystals promote the graphitization. Black-Right-Pointing-Pointer The HGCNSs exhibit superior electrochemical performance to graphite.

  7. Graphitization kinetics of fluidized-bed pyrolytic carbons

    International Nuclear Information System (INIS)

    Beatty, R.L.

    1975-08-01

    Graphitization of 12 fluidized-bed pyrocarbons was studied as a function of heat-treatment time and temperature (1350 to 3000 0 C) to investigate the effect of initial microstructure on the graphitization process. The term ''graphitization'' is defined to include any thermally induced structural change, whether or not any layer stacking order is attained. A broad range of CVD microstructures was prepared at temperatures from 1150 to 1900 0 C and various propylene and methane concentrations. The twelve carbons spanned a wide range of graphitizabilities, primarily as a function of deposition temperature. Hydrocarbon concentration was of much less importance except for deposition at 1900 0 C. Hydrogen content of the as-deposited carbons decreased with increasing temperature of deposition, and initial graphitization behavior of the low-temperature carbons appeared to be related to hydrogen content and evolution. Rates of change in the parameters varied widely throughout the range of heat-treatment times (HTt) and temperatures (HTT) for the different carbons showing differences between the more graphitizable or ''soft'' carbons from the nongraphitizing or ''hard'' carbons. ΔH for nongraphitizing carbons was 175 +- 15 kcal below 1950 0 C, 240 +- 35 kcal at 1950 to 2700 0 C, and 330 +- 20 kcal above 2700 0 C. For graphitizing carbons deposited at 1150 0 C, values near 245 kcal were obtained from anti chi data for the HTT range 1350 to 1650 0 C, while densification data yielded values of about 160 kcal in the same range. The behaviors observed for graphitizable carbons above 2000 0 C are consistent with literature. Different kinetic behaviors below 2000 0 C were shown to be due to different initial microstructures as well as to different parameters measured. (U.S.)

  8. Preparation of nanoporous carbons from graphite nanofibres

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Byung-Joo [Department of Green Chemistry and Environmental Biotechnology, University of Science and Technology, PO Box 107, Yuseong, Daejeon 305-600 (Korea, Republic of); Park, Soo-Jin [Department of Chemistry, Inha University, 253, Nam-gu, Incheon 402-751 (Korea, Republic of)

    2006-09-14

    In this study we manufactured highly porous graphite nanofibres (GNFs) by physical activation in order to develop promising energy storage materials. The activation was performed at activation temperatures in the range of 800-1050 deg. C. The pore structures of the porous GNFs were analysed using N{sub 2}/77 K adsorption isotherms. After the activation, the porous GNFs showed a decrease in diameter and scratches on their surfaces, resulting from surface oxidation and the opening of the graphitic layers, respectively. It was found that the specific surface area of the porous GNFs prepared at 1050 deg. C was more than 2000 m{sup 2} g{sup -1} without loss of their fibre shape or serious increase in electrical resistivity. This result indicates that porous GNFs prepared under optimal conditions can have a much higher specific surface area and are promising materials for energy storage technologies.

  9. New anode material for lithium-ion cells produced by catalytic graphitization of glassy carbon at 1000 degrees C

    Energy Technology Data Exchange (ETDEWEB)

    Skowronski, J.M. [Poznan Univ. of Technology, Poznan (Poland). Inst. of Chemistry and Technical Electrochemistry; Central Lab. of Batteries and Cells, Poznan (Poland); Knofczynski, K. [Central Lab. of Batteries and Cells, Poznan (Poland)

    2006-10-15

    This study investigated the conversion of glassy carbon into graphite at relatively low temperature of 1000 degrees C under ambient pressure using iron powder as the catalyst. The composite product of reaction was a graphite and turbostratic carbon whose use was then examined in terms of application in lithium-ion cells. Glassy, hard carbon spheres of 10 to 15 {iota}m were prepared from phenolic resin in a nitrogen atmosphere and then subjected to heat treatment with an iron powder mixture. After cooling down to ambient temperature, the carbon/iron mixture was treated with diluted HCl solution to remove metallic additives. The modified carbon was then washed with distilled water until chloride ions disappeared in a filtrate. All samples were characterized using XRD analysis. Working electrodes for electrochemical measurements were made by mixing carbons with PVDF. Cyclic voltammograms recorded for unmodified and modified carbons were consistent with XRD measurements. SEM analysis revealed that the process of graphitization begins at the external regions of glassy carbon spheres where erosion occurs when the carbon reacts with iron particles. The surface destruction of carbon spheres progresses into the interior of the spheres, resulting in their collapse followed by the transformation into pallets resembling a stack of graphite sheets. It was noted that not all unorganized carbon was conversed to graphite. Rather, only 50 per cent of turbostratic carbon existed in the product of heat treatment. The product of graphitization appeared to be a promising material for the preparation of anodes for lithium-ion cells. The discharge capacity for carbon produced by catalytic treatment was found to be approximately 5 times higher, while the discharge/charge reversibility was 23 per cent higher than values obtained for untreated carbon. The study showed that the uptake of lithium ions by the original carbon depends on the insertion/deinsertion mechanism of hard carbon as well

  10. Carbon-14 in neutron-irradiated graphite for graphite-moderated reactors. Joint research

    Energy Technology Data Exchange (ETDEWEB)

    Fujii, Kimio [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment; Matsuo, Hideto [Radioactive Waste Management and Nuclear Facility Decommissioning Technology Center, Tokyo (Japan)

    2002-12-01

    The graphite moderated gas cooled reactor operated by the Japan Atomic Power Company was stopped its commercial operation on March 1998, and the decommissioning process has been started. Graphite material is often used as the moderator and the reflector materials in the core of the gas cooled reactor. During the operation, a long life nuclide of {sup 14}C is generated in the graphite by several transmutation reactions. Separation of {sup 14}C isotope and the development of the separation method have been recognized to be critical issues for the decommissioning of the reactor core. To understand the current methodologies for the carbon isotope separation, literature on the subject was surveyed. Also, those on the physical and chemical behavior of {sup 14}C were surveyed. This is because the larger part of the nuclides in the graphite is produced from {sup 14}N by (n,p) reaction, and the location of them in the material tends to be different from those of the other carbon atoms. This report summarizes the result of survey on the open literature about the behavior of {sup 14}C and the separation methods, including the list of the literature on these subjects. (author)

  11. Development of a rotating graphite carbon disk stripper

    Science.gov (United States)

    Hasebe, Hiroo; Okuno, Hiroki; Tatami, Atsushi; Tachibana, Masamitsu; Murakami, Mutsuaki; Kuboki, Hironori; Imao, Hiroshi; Fukunishi, Nobuhisa; Kase, Masayuki; Kamigaito, Osamu

    2018-05-01

    Highly oriented graphite carbon sheets (GCSs) were successfully used as disk strippers. An irradiation test conducted in 2015 showed that GCS strippers have the longest lifetime and exhibit improved stripping and transmission efficiencies. The problem of disk deformation in previously used Be-disk was solved even with higher beam intensity.

  12. Carbon nanostructures and graphite-coated metal nanostructures ...

    Indian Academy of Sciences (India)

    Under certain conditions, pyrolysis of ruthenocene gives rise to graphite coated ruthenium nanoparticles as well as worm-like carbon structures. Pyrolysis of mixtures of ruthenocene and ferrocene gives rise to nanoparticles or nanorods of FeRu alloys, the composition depending upon the composition of the original mixture.

  13. Graphitic Carbon-Based Nanostructures for Energy and Environmental Applications

    Science.gov (United States)

    Chan, Ka Long Donald

    This thesis focuses on the synthesis and characterization of graphitic carbonbased photocatalytic nanostructures for energy and environmental applications. The preparation of carbon- and oxygen-rich graphitic carbon nitride with enhanced photocatalytic hydrogen evolution property was investigated. Composite materials based on graphene quantum dots were also prepared. These composites were used for photocatalytic degradation of organic pollutants and photoelectrocatalytic disinfection. The first part of this thesis describes a facile method for the preparation of carbon- and oxygen-rich graphitic carbon nitride by thermal condensation. Incorporation of carbon and oxygen enhanced the photoresponse of carbon nitride in the visible-light region. After exfoliation, the product was c.a. 45 times more active than bulk graphitic carbon nitride in photocatalytic hydrogen evolution under visible-light irradiation. In the second part, a simple approach to enhance the photocatalytic activity of red phosphorus was developed. Mechanical ball milling was applied to reduce the size of red phosphorus and to deposit graphene quantum dots (GQDs) onto red phosphorus. The product exhibited high visible-light-driven photocatalytic performance in the photodegradation of Rhodamine B. The incorporation of GQDs in titanium dioxide could also extend the absorption spectrum of TiO2 into the visible-light range. The third part of this thesis reports on the fabrication of a visible-light-driven composite photocatalyst of TiO2 nanotube arrays (TNAs) and GQDs. Carboxyl-containing GQDs were covalently coupled to amine-modified TNAs. The product exhibited enhanced photocurrent and high photoelectrocatalytic performance in the inactivation of E. coli under visible-light irradiation. The role of various reactive species in the photoelectrocatalytic process was investigated.

  14. Numerical modelling of adsorption of metallic particles on graphite substrate via molecular dynamics simulation

    International Nuclear Information System (INIS)

    Rafii-Tabar, H.

    1998-01-01

    A computer-based numerical modelling of the adsorption process of gas phase metallic particles on the surface of a graphite substrate has been performed via the application of molecular dynamics simulation method. The simulation related to an extensive STM-based experiment performed in this field, and reproduces part of the experimental results. Both two-body and many-body inter-atomic potentials have been employed. A Morse-type potential describing the metal-carbon interactions at the interface was specially formulated for this modelling. Intercalation of silver in graphite has been observed as well as the correct alignments of monomers, dimers and two-dimensional islands on the surface. (author)

  15. Retention and effective diffusion of model metabolites on porous graphitic carbon.

    Science.gov (United States)

    Lunn, Daniel B; Yun, Young J; Jorgenson, James W

    2017-12-29

    The study of metabolites in biological samples is of high interest for a wide range of biological and pharmaceutical applications. Reversed phase liquid chromatography is a common technique used for the separation of metabolites, but it provides little retention for polar metabolites. An alternative to C18 bonded phases, porous graphitic carbon has the ability to provide significant retention for both non-polar and polar analytes. The goal of this work is to study the retention and effective diffusion properties of porous graphitic carbon, to see if it is suitable for the wide injection bands and long run times associated with long, packed capillary-scale separations. The retention of a set of standard metabolites was studied for both stationary phases over a wide range of mobile phase conditions. This data showed that porous graphitic carbon benefits from significantly increased retention (often >100 fold) under initial gradient conditions for these metabolites, suggesting much improved ability to focus a wide injection band at the column inlet. The effective diffusion properties of these columns were studied using peak-parking experiments with the standard metabolites under a wide range of retention conditions. Under the high retention conditions, which can be associated with retention after injection loading for gradient separations, D eff /D m ∼0.1 for both the C18-bonded and porous graphitic carbon columns. As C18 bonded particles are widely, and successfully utilized for long gradient separations without issue of increasing peak width from longitudinal diffusion, this suggests that porous graphitic carbon should be amenable for long runtime gradient separations as well. Copyright © 2017 Elsevier B.V. All rights reserved.

  16. Preparation and characterization of flake graphite/silicon/carbon spherical composite as anode materials for lithium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Lai Jun [School of Metallurgical Science and Engineering, Central South University, Changsha 410083 (China); Guo Huajun, E-mail: Lai_jun_@126.com [School of Metallurgical Science and Engineering, Central South University, Changsha 410083 (China); Wang Zhixing; Li Xinhai; Zhang Xiaoping; Wu Feixiang; Yue Peng [School of Metallurgical Science and Engineering, Central South University, Changsha 410083 (China)

    2012-07-25

    Highlights: Black-Right-Pointing-Pointer Flake graphite/silicon/carbon composite is synthesized via spray drying. Black-Right-Pointing-Pointer Flake graphite of {approx}0.5 {mu}m and glucose are used to prepare the composite. Black-Right-Pointing-Pointer The as-prepared composite shows spherical and porous appearance. Black-Right-Pointing-Pointer The composite shows nearly the same cycleability as commercial graphite in 20 cycles. Black-Right-Pointing-Pointer The composite shows a reversible capacity of 552 mAh/g at the 20th cycle. - Abstract: Using nano-Si, glucose and flake graphite of {approx}0.5 {mu}m as raw materials, flake graphite/silicon/carbon composite is successfully synthesized via spray drying and subsequent pyrolysis. The samples are characterized by XRD, SEM, TEM and electrochemical measurements. The composite is composed of flake graphite, nano-Si and amorphous glucose-pyrolyzed carbon and presents good spherical appearance. Some micron pores arising from the decomposition of glucose exist on the surface of the composite particles. The composite has a high reversible capacity of 602.7 mAh/g with an initial coulombic efficiency of 69.71%, and shows nearly the same cycleability as the commercial graphite in 20 cycles. Both the glucose-pyrolyzed carbon and the micron pores play important roles in improving the cycleability of the composite. The flake graphite/silicon/carbon composite electrode is a potential alternative to graphite for high energy-density lithium ion batteries.

  17. In situ synthesized Li2S@porous carbon cathode for graphite/Li2S full cells using ether-based electrolyte

    International Nuclear Information System (INIS)

    Wang, Ning; Zhao, Naiqin; Shi, Chunsheng; Liu, Enzuo; He, Chunnian; He, Fang; Ma, Liying

    2017-01-01

    Graphical abstract: A facile method is proposed to prepare lithium sulfide@porous carbon composites (Li 2 S@PC) by in-situ reaction of lithium sulfate (Li 2 SO 4 ) and the pyrolytic carbon from glucose. We assembled graphite-Li 2 S@PC full-cells using the obtained Li 2 S@PC composites as the cathode, graphite as the anode and DOL/DME with LiNO 3 additive as the electrolyte. Display Omitted -- Highlights: •A simple synthesis method was proposed to form Li 2 S@porous carbon composites. •Graphite-Li 2 S full-cells were constructed in DME-based electrolyte. •A novel method was proposed to activate the full cells. -- Abstract: Lithium-sulfur (Li-S) batteries have been recognized as one of the promising next-generation energy storage devices owing to their high energy density, low cost and eco-friendliness. As for cathode’s performance, the main challenges for developing highly-efficient and long-life Li-S batteries are to retard the polysulfides diffusion into electrolyte and the reaction with metallic lithium (Li). Especially, the safety issues, derived from metallic Li in anode, must be overcome. Herein, we fabricated lithium sulfide@porous carbon composites (Li 2 S@PC) by an in-situ reaction between the lithium sulfate (Li 2 SO 4 ) and the pyrolytic carbon from glucose. The nanosized Li 2 S particles were uniformly distributed in the carbon matrix, which not only significantly improve electronic conductivity of the electrode but also effectively trap the dissolved polysulfides. Furthermore, on the basis of the graphite’s electrochemical features in ether-based electrolyte, we assembled graphite-Li 2 S@PC full cells using the obtained Li 2 S@PC composites as the cathode, graphite as the anode and the DOL/DME with LiNO 3 additive as the electrolyte. A unique strategy was proposed to activate the full-cells in descending order using constant voltage and current to charge the cut-off voltage. This Li-S full cell exhibits stable cycling performance at 0.5 C over

  18. Microstructure, elastic and inelastic properties of partially graphitized biomorphic carbons

    Science.gov (United States)

    Orlova, T. S.; Kardashev, B. K.; Smirnov, B. I.; Gutierrez-Pardo, A.; Ramirez-Rico, J.; Martinez-Fernandez, J.

    2015-03-01

    The microstructural characteristics and amplitude dependences of the Young's modulus E and internal friction (logarithmic decrement δ) of biocarbon matrices prepared by beech wood carbonization at temperatures T carb = 850-1600°C in the presence of a nickel-containing catalyst have been studied. Using X-ray diffraction and electron microscopy, it has been shown that the use of a nickel catalyst during carbonization results in a partial graphitization of biocarbons at T carb ≥ 1000°C: the graphite phase is formed as 50- to 100-nm globules at T carb = 1000°C and as 0.5- to 3.0-μm globules at T carb = 1600°C. It has been found that the measured dependences E( T carb) and δ( T carb) contain three characteristic ranges of variations in the Young's modulus and logarithmic decrement with a change in the carbonization temperature: E increases and δ decreases in the ranges T carb 1300°C; in the range 1000 biocarbons carbonized in the presence of nickel correlates with the evolution of their microstructure. The largest values of E are obtained for samples with T carb = 1000 and 1600°C. However, the samples with T carb = 1600°C exhibit a higher susceptibility to microplasticity due to the presence of a globular graphite phase that is significantly larger in size and total volume.

  19. Milling Behavior of Matrix Graphite Powders with Different Binder Materials in HTGR Fuel Element Fabrication: I. Variation in Particle Size Distribution

    International Nuclear Information System (INIS)

    Lee, Young Woo; Cho, Moon Sung

    2011-01-01

    The fuel element for HTGR is manufactured by mixing coated fuel particles with matrix graphite powder and forming into either pebble type or cylindrical type compacts depending on their use in different HTGR cores. The coated fuel particle, the so-called TRISO particle, consists of 500-μm spherical UO 2 particles coated with the low density buffer Pyrolytic Carbon (PyC) layer, the inner and outer high density PyC layer and SiC layer sandwiched between the two inner and outer PyC layers. The coated TRISO particles are mixed with a matrix graphite powder properly prepared and pressed into a spherical shape or a cylindrical compact finally heat-treated at about 1900 .deg. C. These fuel elements can have different sizes and forms of compact. The basic steps for manufacturing a fuel element include preparation of graphite matrix powder, overcoating the fuel particles, mixing the fuel particles with a matrix powder, carbonizing green compact, and the final high-temperature heat treatment of the carbonized fuel compact. In order to develop a fuel compact fabrication technology, it is important to develop a technology to prepare the matrix graphite powder (MGP) with proper characteristics, which has a strong influence on further steps and the material properties of fuel element. In this work, the milling behavior of matrix graphite powder mixture with different binder materials and their contents was investigated by analyzing the change in particle size distribution with different milling time

  20. Electrical conductivity of compacts of graphene, multi-wall carbon nanotubes, carbon black, and graphite powder

    NARCIS (Netherlands)

    Marinho, B.; Gomes Ghislandi, M.; Tkalya, E.; Koning, C.E.; With, de G.

    2012-01-01

    The electrical conductivity of different carbon materials (multi-walled carbon nanotubes, graphene, carbon black and graphite), widely used as fillers in polymeric matrices, was studied using compacts produced by a paper preparation process and by powder compression. Powder pressing assays show that

  1. A Nanoporous Carbon/Exfoliated Graphite Composite For Supercapacitor Electrodes

    Science.gov (United States)

    Rosi, Memoria; Ekaputra, Muhamad P.; Iskandar, Ferry; Abdullah, Mikrajuddin; Khairurrijal

    2010-12-01

    Nanoporous carbon was prepared from coconut shells using a simple heating method. The nanoporous carbon is subjected to different treatments: without activation, activation with polyethylene glycol (PEG), and activation with sodium hydroxide (NaOH)-PEG. The exfoliated graphite was synthesized from graphite powder oxidized with zinc acetate (ZnAc) and intercalated with polyvinyl alcohol (PVA) and NaOH. A composite was made by mixing the nanoporous carbon with NaOH-PEG activation, the exfoliated graphite and a binder of PVA solution, grinding the mixture, and annealing it using ultrasonic bath for 1 hour. All of as-synthesized materials were characterized by employing a scanning electron microscope (SEM), a MATLAB's image processing toolbox, and an x-ray diffractometer (XRD). It was confirmed that the composite is crystalline with (002) and (004) orientations. In addition, it was also found that the composite has a high surface area, a high distribution of pore sizes less than 40 nm, and a high porosity (67%). Noting that the pore sizes less than 20 nm are significant for ionic species storage and those in the range of 20 to 40 nm are very accessible for ionic clusters mobility across the pores, the composite is a promising material for the application as supercapacitor electrodes.

  2. The effect of iron catalyzed graphitization on the textural properties of carbonized cellulose : Magnetically separable graphitic carbon bodies for catalysis and remediation

    NARCIS (Netherlands)

    Hoekstra, Jacco; Beale, Andrew M.; Soulimani, Fouad; Versluijs-Helder, Marjan; Van De Kleut, Dirk; Koelewijn, Jacobus M.; Geus, John W.; Jenneskens, Leonardus W.

    2016-01-01

    Whereas pyrolysis of pristine microcrystalline cellulose spheres yields nonporous amorphous carbon bodies, pyrolysis of microcrystalline cellulose spheres loaded with iron salts leads to the formation of magnetically separable mesoporous graphitic carbon bodies. The microcrystalline cellulose

  3. Comparative inhalation toxicity of multi-wall carbon nanotubes, graphene, graphite nanoplatelets and low surface carbon black.

    Science.gov (United States)

    Ma-Hock, Lan; Strauss, Volker; Treumann, Silke; Küttler, Karin; Wohlleben, Wendel; Hofmann, Thomas; Gröters, Sibylle; Wiench, Karin; van Ravenzwaay, Bennard; Landsiedel, Robert

    2013-06-17

    Carbon nanotubes, graphene, graphite nanoplatelets and carbon black are seemingly chemically identical carbon-based nano-materials with broad technological applications. Carbon nanotubes and carbon black possess different inhalation toxicities, whereas little is known about graphene and graphite nanoplatelets. In order to compare the inhalation toxicity of the mentioned carbon-based nanomaterials, male Wistar rats were exposed head-nose to atmospheres of the respective materials for 6 hours per day on 5 consecutive days. Target concentrations were 0.1, 0.5, or 2.5 mg/m3 for multi-wall carbon nanotubes and 0.5, 2.5, or 10 mg/m3 for graphene, graphite nanoplatelets and low-surface carbon black. Toxicity was determined after end of exposure and after three-week recovery using broncho-alveolar lavage fluid and microscopic examinations of the entire respiratory tract. No adverse effects were observed after inhalation exposure to 10 mg/m3 graphite nanoplatelets or relatively low specific surface area carbon black. Increases of lavage markers indicative for inflammatory processes started at exposure concentration of 0.5 mg/m3 for multi-wall carbon nanotubes and 10 mg/m3 for graphene. Consistent with the changes in lavage fluid, microgranulomas were observed at 2.5 mg/m3 multi-wall carbon nanotubes and 10 mg/m3 graphene. In order to evaluate volumetric loading of the lung as the key parameter driving the toxicity, deposited particle volume was calculated, taking into account different methods to determine the agglomerate density. However, the calculated volumetric load did not correlate to the toxicity, nor did the particle surface burden of the lung. The inhalation toxicity of the investigated carbon-based materials is likely to be a complex interaction of several parameters. Until the properties which govern the toxicity are identified, testing by short-term inhalation is the best option to identify hazardous properties in order to avoid unsafe applications or select

  4. Comparative inhalation toxicity of multi-wall carbon nanotubes, graphene, graphite nanoplatelets and low surface carbon black

    Science.gov (United States)

    2013-01-01

    Background Carbon nanotubes, graphene, graphite nanoplatelets and carbon black are seemingly chemically identical carbon-based nano-materials with broad technological applications. Carbon nanotubes and carbon black possess different inhalation toxicities, whereas little is known about graphene and graphite nanoplatelets. Methods In order to compare the inhalation toxicity of the mentioned carbon-based nanomaterials, male Wistar rats were exposed head-nose to atmospheres of the respective materials for 6 hours per day on 5 consecutive days. Target concentrations were 0.1, 0.5, or 2.5 mg/m3 for multi-wall carbon nanotubes and 0.5, 2.5, or 10 mg/m3 for graphene, graphite nanoplatelets and low-surface carbon black. Toxicity was determined after end of exposure and after three-week recovery using broncho-alveolar lavage fluid and microscopic examinations of the entire respiratory tract. Results No adverse effects were observed after inhalation exposure to 10 mg/m3 graphite nanoplatelets or relatively low specific surface area carbon black. Increases of lavage markers indicative for inflammatory processes started at exposure concentration of 0.5 mg/m3 for multi-wall carbon nanotubes and 10 mg/m3 for graphene. Consistent with the changes in lavage fluid, microgranulomas were observed at 2.5 mg/m3 multi-wall carbon nanotubes and 10 mg/m3 graphene. In order to evaluate volumetric loading of the lung as the key parameter driving the toxicity, deposited particle volume was calculated, taking into account different methods to determine the agglomerate density. However, the calculated volumetric load did not correlate to the toxicity, nor did the particle surface burden of the lung. Conclusions The inhalation toxicity of the investigated carbon-based materials is likely to be a complex interaction of several parameters. Until the properties which govern the toxicity are identified, testing by short-term inhalation is the best option to identify hazardous properties in

  5. Structure and properties of carbon black particles

    Science.gov (United States)

    Xu, Wei

    Structure and properties of carbon black particles were investigated using atomic force microscopy, gas adsorption, Raman spectroscopy, and X-ray diffraction. Supplementary information was obtained using TEM and neutron scattering. The AFM imaging of carbon black aggregates provided qualitative visual information on their morphology, complementary to that obtained by 3-D modeling based on TEM images. Our studies showed that carbon black aggregates were relatively flat. The surface of all untreated carbon black particles was found to be rough and its fractal dimension was 2.2. Heating reduced the roughness and fractal dimension for all samples heat treated at above 1300 K to 2.0. Once the samples were heat treated rapid cooling did not affect the surface roughness. However, rapid cooling reduced crystallite sizes, and different Raman spectra were obtained for carbon blacks of various history of heat treatment. By analyzing the Raman spectra we determined the crystallite sizes and identified amorphous carbon. The concentration of amorphous carbon depends on hydrogen content. Once hydrogen was liberated at increased temperature, the concentration of amorphous carbon was reduced and crystallites started to grow. Properties of carbon blacks at high pressure were also studied. Hydrostatic pressure did not affect the size of the crystallites in carbon black particles. The pressure induced shift in Raman frequency of the graphitic component was a result of increased intermolecular forces and not smaller crystallites. Two methods of determining the fractal dimension, the FHH model and the yardstick technique based on the BET theory were used in the literature. Our study proved that the FHH model is sensitive to numerous assumptions and leads to wrong conclusions. On the other hand the yardstick method gave correct results, which agreed with the AFM results.

  6. Electrophoretic deposition of carbon nanotubes on a carbon fiber surface with different index graphitization

    International Nuclear Information System (INIS)

    Almeida, E.C.; Baldan, M.R.; Ferreira, N.G.; Edwards, E.R.

    2009-01-01

    Full text: The purpose of this work is to examine the electrophoretic deposition of carbon nanotubes powder on carbon fibers, produced at different heat treatments temperatures. Besides, a systematic study of the effects of graphitization index from substrate on the structure and morphology of CNTs has been available. Carbon fibers were produced from polyacrylonitrile at three different heat treatments temperatures, 1000, 1500 and 2000 deg C. The carbon fibers microstructure or its graphitization index may be controlled by the heat treatments temperatures. The electrophoretic deposition of carbon nanotubes was obtained with the powder of carbon nanotubes dispersed in water by ultrasonication to obtain dispersions of 0.05 mg/mL. The carbon fibers were immersed in the nanotube dispersion, and a positive potential of 10 V/cm was applied. Morphology and microstructure of carbon nanotubes on carbon fibers were obtained by scanning electron microscopy, Raman spectroscopy and X-ray photoelectron spectroscopy. (author)

  7. High-resolution optical microscopy of carbon and graphite

    International Nuclear Information System (INIS)

    Cook, W.H.; Allen, M.D.; Leslie, B.C.; Gray, R.J.

    1975-01-01

    The ceramographic preparation of carbonaceous materials varying in crystalline quality, amorphous carbon to well crystallized graphite, is described. In a two-step process, using alumina and diamond polishing compounds, one can prepare more samples, obtain a substantial saving in man hours, avoid rounding material around pores, and obtain flatter surfaces than were obtainable with earlier, conventional methods. Improved resolution of microstructural details is achieved without impregnation with epoxy resins or other materials to support the porous structures. Use of rotatable, half-wave retardation (sensitive tint) enhances the microstructural definition in both color and black and white. These innovations were extensively used as part of the examination of nuclear grades of graphite before and after exposure to fast neutrons at temperatures from 650 to 1100 0 C; typical examples are discussed. (auth)

  8. Carbon nanostructure formation driven by energetic particles

    International Nuclear Information System (INIS)

    Zhu Zhiyuan; Gong Jinlong; Zhu Dezhang

    2006-01-01

    Carbon nanostructures, especially carbon nanotubes (CNTs), have been envisaged to be the building blocks of a variety of nanoscale devices and materials. The inherent nanometer-size and ability of being either metallic or semiconductive of CNTs lead to their application in nanoelectronics. Excellent mechanical characteristics of CNTs suggest their use as structural reinforcements. However, to fully exploit the potential applications, effective means of tailoring CNT properties must be developed. Irradiation of materials with energetic particles beams (ions and electrons) is a standard and important tool for modifying material properties. Irradiation makes it possible to dope the samples, to create local amorphous region or vice versa, recrystallize the lattice and even drive a phase transition. In this paper, we report our results of (1) phase transfromation from carbon nanotubes to nanocrystalline diamond driven by hydrogen plasma, (2) onion-like nanostructure from carbon nanotubes driven by ion beams of several tens keV, and (3) amorphous carbon nanowire network formation by ion beam irradiation. Structural phase transformation from multiwalled carbon nanotubes to nanocrystalline diamond by hydrogen plasma post-treatment was carried out. Ultrahigh equivalent diamond nucleation density of more than 1011 nuclei/cm 2 was obtained. The diamond formation and growth mechanisms were proposed to be the consequence of the formation of sp3 bonded amorphous carbon clusters. The hydrogen chemisorption on curved graphite network and the energy deposited on CNTs by continuous impingement of activated molecular or atomic hydrogen are responsible for the formation of amorphous carbon matrix. Diamond nucleates and grows in the way similar to that of diamond chemical vapor deposition processes on amorphous carbon films. Furthermore, single crystalline diamond nanorods of 4-8 nm in diameter and up to 200 nm in length have been successfully synthesized by hydrogen plasma post

  9. Fe_3C@carbon nanocapsules/expanded graphite as anode materials for lithium ion batteries

    International Nuclear Information System (INIS)

    Huang, You-Guo; Lin, Xi-Le; Zhang, Xiao-Hui; Pan, Qi-Chang; Yan, Zhi-Xiong; Wang, Hong-Qiang; Chen, Jian-Jun; Li, Qing-Yu

    2015-01-01

    ABSTRACT: Fe_3C@carbonnanocapsules(*)/expanded graphite composite was successfully prepared by a new and facile method, including mix of starting materials and heat treatment of the precursor. It is featured by unique 3-D structure, where expanded graphite acts as scaffold to ensure a continuous entity, and Fe_3C particles coated by carbon nanocapsules are embedded intimately. The Fe_3C nanoparticles encased in carbon nanocapsules act as catalyst in the modification of SEI film during the cycles. The interesting 3-D architecture which aligns the conductivity paths in the planar direction with expanded graphite and in the axial direction with carbon nanocapsules minimizes the resistance and enhances the reversible capacity. The prepared composite exhibits a high reversible capacity and excellent rate performance as an anode material for lithium ion batteries. The composite maintains a reversible capacity of 1226.2 mAh/g after 75 cycles at 66 mA/g. When the current density increases to 200 mA/g, the reversible capacity maintains 451.5 mAh/g. The facile synthesis method and excellent electrochemical performances make the composite expected to be one of the most potential anode material for lithium ion batteries.

  10. Protection of nuclear graphite toward fluoride molten salt by glassy carbon deposit

    International Nuclear Information System (INIS)

    Bernardet, V.; Gomes, S.; Delpeux, S.; Dubois, M.; Guerin, K.; Avignant, D.; Renaudin, G.; Duclaux, L.

    2009-01-01

    Molten salt reactor represents one of the promising future Generation IV nuclear reactors families where the fuel, a liquid molten fluoride salt, is circulating through the graphite reactor core. The interactions between nuclear graphite and fluoride molten salt and also the graphite surface protection were investigated in this paper by powder X-ray diffraction, micro-Raman spectroscopy and scanning electron microscopy coupled with X-ray microanalysis. Nuclear graphite discs were covered by two kinds of protection deposit: a glassy carbon coating and a double coating of pyrolitic carbon/glassy carbon. Different behaviours have been highlighted according to the presence and the nature of the coated protection film. Intercalation of molten salt between the graphite layers did not occur. Nevertheless the molten salt adhered more or less to the surface of the graphite disc, filled more or less the graphite surface porosity and perturbed more or less the graphite stacking order at the disc surface. The behaviour of unprotected graphite was far to be satisfactory after two days of immersion of graphite in molten salt at 500 deg. C. The best protection of the graphite disc surface, with the maximum of inertness towards molten salt, has been obtained with the double coating of pyrolitic carbon/glassy carbon

  11. Effect of the graphite electrode material on the characteristics of molten salt electrolytically produced carbon nanomaterials

    International Nuclear Information System (INIS)

    Kamali, Ali Reza; Schwandt, Carsten; Fray, Derek J.

    2011-01-01

    The electrochemical erosion of a graphite cathode during the electrolysis of molten lithium chloride salt may be used for the preparation of nano-structured carbon materials. It has been found that the structures and morphologies of these carbon nanomaterials are dependent on those of the graphite cathodes employed. A combination of tubular and spherical carbon nanostructures has been produced from a graphite with a microstructure of predominantly planar micro-sized grains and a minor fraction of more irregular nano-sized grains, whilst only spherical carbon nanostructures have been produced from a graphite with a microstructure of primarily nano-sized grains. Based on the experimental results, a best-fit regression equation is proposed that relates the crystalline domain size of the graphite reactants and the carbon products. The carbon nanomaterials prepared possess a fairly uniform mesoporosity with a sharp peak in pore size distribution at around 4 nm. The results are of crucial importance to the production of carbon nanomaterials by way of the molten salt electrolytic method. - Highlights: → Carbon nanomaterials are synthesised by LiCl electrolysis with graphite electrodes. → The degree of crystallinity of graphite reactant and carbon product are related. → A graphite reactant is identified that enables the preparation of carbon nanotubes. → The carbon products possess uniform mesoporosity with narrow pore size distribution.

  12. Friction and wear of carbon-graphite materials for high-energy brakes

    Science.gov (United States)

    Bill, R. C.

    1978-01-01

    Caliper type brake simulation experiments were conducted on seven different carbon graphite materials formulations against a steel disk material and against a carbon graphite disk material. The effects of binder level, boron carbide (B4C) additions, SiC additions, graphite fiber additions, and graphite cloth reinforcement on friction and wear behavior were investigated. Reductions in binder level, additions of B4C, and additions of SiC each resulted in increased wear. The wear rate was not affected by the addition of graphite fibers. Transition to severe wear and high friction was observed in the case of graphite-cloth-reinforced carbon sliding against a disk of similar composition. The transition was related to the disruption of a continuous graphite shear film that must form on the sliding surfaces if low wear is to occur.

  13. Friction and wear of carbon-graphite materials for high energy brakes

    Science.gov (United States)

    Bill, R. C.

    1975-01-01

    Caliper-type brakes simulation experiments were conducted on seven different carbon-graphite material formulations against a steel disk material and against a carbon-graphite disk material. The effects of binder level, boron carbide (B4C) additions, graphite fiber additions, and graphite cloth reinforcement on friction and wear behavior were investigated. Reductions in binder level and additions of B4C each resulted in increased wear. The wear rate was not affected by the addition of graphite fibers. Transition to severe wear and high friction was observed in the case of graphite-cloth-reinforced carbon sliding against a disk of similar composition. This transition was related to the disruption of a continuous graphite shear film that must form on the sliding surfaces if low wear is to occur. The exposure of the fiber structure of the cloth constituent is believed to play a role in the shear film disruption.

  14. Special graphites; Graphites speciaux

    Energy Technology Data Exchange (ETDEWEB)

    Leveque, P [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1964-07-01

    A large fraction of the work undertaken jointly by the Commissariat a l'Energie Atomique (CEA) and the Pechiney Company has been the improvement of the properties of nuclear pile graphite and the opening up of new fields of graphite application. New processes for the manufacture of carbons and special graphites have been developed: forged graphite, pyro-carbons, high density graphite agglomeration of graphite powders by cracking of natural gas, impervious graphites. The physical properties of these products and their reaction with various oxidising gases are described. The first irradiation results are also given. (authors) [French] Ameliorer les proprietes du graphite nucleaire pour empilements et ouvrir de nouveaux domaines d'application au graphite constituent une part importante de l'effort entrepris en commun par le Commissariat a l'Energie Atomique (CEA) et la compagnie PECHINEY. Des procedes nouveaux de fabrication de carbones et graphites speciaux ont ete mis au point: graphite forge, pyrocarbone, graphite de haute densite, agglomeration de poudres de graphite par craquage de gaz naturel, graphites impermeables. Les proprietes physiques de ces produits ainsi que leur reaction avec differents gaz oxydants sont decrites. Les premiers resultats d'irradiation sont aussi donnes. (auteurs)

  15. All-Carbon Electrode Consisting of Carbon Nanotubes on Graphite Foil for Flexible Electrochemical Applications

    Directory of Open Access Journals (Sweden)

    Je-Hwang Ryu

    2014-03-01

    Full Text Available We demonstrate the fabrication of an all-carbon electrode by plasma-enhanced chemical vapor deposition for use in flexible electrochemical applications. The electrode is composed of vertically aligned carbon nanotubes that are grown directly on a flexible graphite foil. Being all-carbon, the simple fabrication process and the excellent electrochemical characteristics present an approach through which high-performance, highly-stable and cost-effective electrochemical applications can be achieved.

  16. Effect of graphite particle size and content on the formation mechanism of detonation polycrystalline diamond

    Science.gov (United States)

    Tong, Y.; Cao, Y.; Liu, R.; Shang, S. Y.; Huang, F. L.

    2018-03-01

    The formation mechanism of detonation polycrystalline diamond (DPD) generated from the detonation of a mixed RDX/graphite explosive is investigated. It is found experimentally that the DPD conversion rate decreases with both the content and the particle size of the graphite. Moreover, the particle sizes of the generated DPD powder are analyzed, which shows that, with the decrease in the graphite particle size, the mean number diameter of DPD decreases, but the mean volume diameter increases. In addition, with the help of scanning electron microscopy, it is observed that the in situ phase change occurs in the graphite particles, by which the small particles combine to form numerous large DPD particles. Based on both the experimental data and the classical ZND detonation model, we divide such a DPD synthesis process into two stages: In the first stage, the in situ phase change from graphite to diamond is dominant, supplemented by some coalescence growth at high pressure and temperature, which is affected mainly by the detonation performance of the mixed explosive under consideration. In the second stage, the graphitization of DPD caused by the residual heat is dominant, which is affected mainly by the unloading rate of the particle temperature.

  17. Fabrication and electrochemical behavior of single-walled carbon nanotube/graphite-based electrode

    International Nuclear Information System (INIS)

    Moghaddam, Abdolmajid Bayandori; Ganjali, Mohammad Reza; Dinarvand, Rassoul; Razavi, Taherehsadat; Riahi, Siavash; Rezaei-Zarchi, Saeed; Norouzi, Parviz

    2009-01-01

    An electrochemical method for determining the dihydroxybenzene derivatives on glassy carbon (GC) has been developed. In this method, the performance of a single-walled carbon nanotube (SWCNT)/graphite-based electrode, prepared by mixing SWCNTs and graphite powder, was described. The resulting electrode shows an excellent behavior for redox of 3,4-dihydroxybenzoic acid (DBA). SWCNT/graphite-based electrode presents a significant decrease in the overvoltage for DBA oxidation as well as a dramatic improvement in the reversibility of DBA redox behavior in comparison with graphite-based and glassy carbon (GC) electrodes. In addition, scanning electron microscopy (SEM) and atomic force microscopy (AFM) procedures performed for used SWCNTs

  18. Photoemission studies of fluorine functionalized porous graphitic carbon

    Science.gov (United States)

    Ganegoda, Hasitha; Jensen, David S.; Olive, Daniel; Cheng, Lidens; Segre, Carlo U.; Linford, Matthew R.; Terry, Jeff

    2012-03-01

    Porous graphitic carbon (PGC) has unique properties desirable for liquid chromatography applications when used as a stationary phase. The polar retention effect on graphite (PREG) allows efficient separation of polar and non-polar solutes. Perfluorinated hydrocarbons however lack polarizabilty and display strong lipo- and hydrophobicity, hence common lipophilic and hydrophilic analytes have low partition coefficiency in fluorinated stationary phases. Attractive interaction between fluorinated stationary phase and fluorinated analytes results in strong retention compared to non-fluorinated analytes. In order to change the selectivities of PGC, it is necessary to develop a bonded PGC stationary phase. In this study, we have synthesized perfluorinated, PGC using hepatadecafluoro-1-iodooctane, under different temperature conditions. Surface functionalization of the raw material was studied using photoelectron spectroscopy (PES). Results indicate the existence of fluorine containing functional groups, -CF, -CF2 along with an intercalated electron donor species. Multiple oxygen functional groups were also observed, likely due to the presence of oxygen in the starting material. These oxygen species may be responsible for significant modifications to planer and tetrahedral carbon ratios.

  19. Photoemission studies of fluorine functionalized porous graphitic carbon

    Energy Technology Data Exchange (ETDEWEB)

    Ganegoda, Hasitha; Olive, Daniel; Cheng, Lidens; Segre, Carlo U.; Terry, Jeff [Department of Physics, Illinois Institute of Technology, Chicago, Illinois 60616 (United States); Jensen, David S.; Linford, Matthew R. [Department of Chemistry and Biochemistry, Brigham Young University, Provo, Utah 84602 (United States)

    2012-03-01

    Porous graphitic carbon (PGC) has unique properties desirable for liquid chromatography applications when used as a stationary phase. The polar retention effect on graphite (PREG) allows efficient separation of polar and non-polar solutes. Perfluorinated hydrocarbons however lack polarizabilty and display strong lipo- and hydrophobicity, hence common lipophilic and hydrophilic analytes have low partition coefficiency in fluorinated stationary phases. Attractive interaction between fluorinated stationary phase and fluorinated analytes results in strong retention compared to non-fluorinated analytes. In order to change the selectivities of PGC, it is necessary to develop a bonded PGC stationary phase. In this study, we have synthesized perfluorinated, PGC using hepatadecafluoro-1-iodooctane, under different temperature conditions. Surface functionalization of the raw material was studied using photoelectron spectroscopy (PES). Results indicate the existence of fluorine containing functional groups, -CF, -CF{sub 2} along with an intercalated electron donor species. Multiple oxygen functional groups were also observed, likely due to the presence of oxygen in the starting material. These oxygen species may be responsible for significant modifications to planer and tetrahedral carbon ratios.

  20. Late-time particle emission from laser-produced graphite plasma

    Energy Technology Data Exchange (ETDEWEB)

    Harilal, S. S.; Hassanein, A.; Polek, M. [School of Nuclear Engineering, Center for Materials Under Extreme Environment, Purdue University, West Lafayette, Indiana 47907 (United States)

    2011-09-01

    We report a late-time ''fireworks-like'' particle emission from laser-produced graphite plasma during its evolution. Plasmas were produced using graphite targets excited with 1064 nm Nd: yttrium aluminum garnet (YAG) laser in vacuum. The time evolution of graphite plasma was investigated using fast gated imaging and visible emission spectroscopy. The emission dynamics of plasma is rapidly changing with time and the delayed firework-like emission from the graphite target followed a black-body curve. Our studies indicated that such firework-like emission is strongly depended on target material properties and explained due to material spallation caused by overheating the trapped gases through thermal diffusion along the layer structures of graphite.

  1. Late-time particle emission from laser-produced graphite plasma

    International Nuclear Information System (INIS)

    Harilal, S. S.; Hassanein, A.; Polek, M.

    2011-01-01

    We report a late-time ''fireworks-like'' particle emission from laser-produced graphite plasma during its evolution. Plasmas were produced using graphite targets excited with 1064 nm Nd: yttrium aluminum garnet (YAG) laser in vacuum. The time evolution of graphite plasma was investigated using fast gated imaging and visible emission spectroscopy. The emission dynamics of plasma is rapidly changing with time and the delayed firework-like emission from the graphite target followed a black-body curve. Our studies indicated that such firework-like emission is strongly depended on target material properties and explained due to material spallation caused by overheating the trapped gases through thermal diffusion along the layer structures of graphite.

  2. Voronoi-Tessellated Graphite Produced by Low-Temperature Catalytic Graphitization from Renewable Resources.

    Science.gov (United States)

    Zhao, Leyi; Zhao, Xiuyun; Burke, Luke T; Bennett, J Craig; Dunlap, Richard A; Obrovac, Mark N

    2017-09-11

    A highly crystalline graphite powder was prepared from the low temperature (800-1000 °C) graphitization of renewable hard carbon precursors using a magnesium catalyst. The resulting graphite particles are composed of Voronoi-tessellated regions comprising irregular sheets; each Voronoi-tessellated region having a small "seed" particle located near their centroid on the surface. This suggests nucleated outward growth of graphitic carbon, which has not been previously observed. Each seed particle consists of a spheroidal graphite shell on the inside of which hexagonal graphite platelets are perpendicularly affixed. This results in a unique high surface area graphite with a high degree of graphitization that is made with renewable feedstocks at temperatures far below that conventionally used for artificial graphites. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  3. Contributions for the international conference on carbon and graphite CARBON '88

    International Nuclear Information System (INIS)

    Delle, W.

    1988-08-01

    This report is the compilation of three papers prepared by the Kernforschungsanlage Juelich GmbH (KFA) in collaboration with other partners for the International Conference CARBON '88. The topics were as follows: 1.) Fracture toughness of fast neutron irradiated graphite (W. Delle, H. Derz, G. Kleist, H. Nickel, W. Thiele); 2.) The irradiation creep characteristics of graphite to high fluences (C.R. Kennedy, M. Cundy, G. Kleist); and 3.) New silicon carbide materials starting with the Coat-Mix procedure (H.K. Luhleich, K. Bach, F.J. Dias, M. Kampel, F. Koch, H. Nickel). (orig./MM)

  4. Direct synthesis of sp-bonded carbon chains on graphite surface by femtosecond laser irradiation

    International Nuclear Information System (INIS)

    Hu, A.; Rybachuk, M.; Lu, Q.-B.; Duley, W. W.

    2007-01-01

    Microscopic phase transformation from graphite to sp-bonded carbon chains (carbyne) and nanodiamond has been induced by femtosecond laser pulses on graphite surface. UV/surface enhanced Raman scattering spectra and x-ray photoelectron spectra displayed the local synthesis of carbyne in the melt zone while nanocrystalline diamond and trans-polyacetylene chains form in the edge area of gentle ablation. These results evidence possible direct 'writing' of variable chemical bonded carbons by femtosecond laser pulses for carbon-based applications

  5. Special graphites

    International Nuclear Information System (INIS)

    Leveque, P.

    1964-01-01

    A large fraction of the work undertaken jointly by the Commissariat a l'Energie Atomique (CEA) and the Pechiney Company has been the improvement of the properties of nuclear pile graphite and the opening up of new fields of graphite application. New processes for the manufacture of carbons and special graphites have been developed: forged graphite, pyro-carbons, high density graphite agglomeration of graphite powders by cracking of natural gas, impervious graphites. The physical properties of these products and their reaction with various oxidising gases are described. The first irradiation results are also given. (authors) [fr

  6. Photothermal cancer therapy using graphitic carbon–coated magnetic particles prepared by one-pot synthesis

    Directory of Open Access Journals (Sweden)

    Lee HJ

    2014-12-01

    Full Text Available Hyo-Jeong Lee,1 Jakkid Sanetuntikul,2 Eun-Sook Choi,1 Bo Ram Lee,1 Jung-Hee Kim,1 Eunjoo Kim,1 Sangaraju Shanmugam2 1Nano and Bio Research Division, 2Department of Energy Systems Engineering, Daegu Gyeongbuk Institute of Science and Technology, Daegu, Republic of Korea Abstract: We describe here a simple synthetic strategy for the fabrication of carbon-coated Fe3O4 (Fe3O4@C particles using a single-component precursor, iron (III diethylenetriaminepentaacetic acid complex. Physicochemical analyses revealed that the core of the synthesized particles consists of ferromagnetic Fe3O4 material ranging several hundred nanometers, embedded in nitrogen-doped graphitic carbon with a thickness of ~120 nm. Because of their photothermal activity (absorption of near-infrared [NIR] light, the Fe3O4@C particles have been investigated for photothermal therapeutic applications. An example of one such application would be the use of Fe3O4@C particles in human adenocarcinoma A549 cells by means of NIR-triggered cell death. In this system, the Fe3O4@C can rapidly generate heat, causing >98% cell death within 10 minutes under 808 nm NIR laser irradiation (2.3 W cm-2. These Fe3O4@C particles provided a superior photothermal therapeutic effect by intratumoral delivery and NIR irradiation of tumor xenografts. These results demonstrate that one-pot synthesis of carbon-coated magnetic particles could provide promising materials for future clinical applications and encourage further investigation of this simple method. Keywords: graphitic carbon–encapsulated magnetic nanoparticles, iron oxide, one-pot synthesis, photothermal cancer therapy

  7. Method to produce carbon-cladded nuclear fuel particles

    International Nuclear Information System (INIS)

    Sturge, D.W.; Meaden, G.W.

    1978-01-01

    In the method charges of micro-spherules of fuel element are designed to have two carbon layers, whereby a one aims to achieve a uniform granulation (standard measurement). Two drums are used for this purpose connected behind one another. The micro-spherules coated with the first layer (phenolformaldehyde resin coated graphite particles) leave the first drum and enter the second one. Following the coating with a second layer, the micro-spherules are introduced into a grain size separator. The spherules that are too small are directly recycled into the second drum and those ones that are too large are recycled into the first drum after removing the graphite layers. The method may also be applied to metal cladded particles to manufacture cermet fuels. (RW) [de

  8. Mechanical activation of graphite in air: A way to advanced carbon nanomaterials

    Energy Technology Data Exchange (ETDEWEB)

    Baklanova, O.N., E-mail: baklanova@ihcp.ru; Drozdov, V.A.; Lavrenov, A.V.; Vasilevich, A.V.; Muromtsev, I.V.; Trenikhin, M.V.; Arbuzov, A.B.; Likholobov, V.A.; Gorbunova, O.V.

    2015-10-15

    A high-energy planetary mill AGO-2 was used for mechanical activation of synthetic graphite with the particle size of 25–30 μm and specific surface area S{sub BET} = 3.0 m{sup 2}/g in air for 1–60 min at a 100 g acceleration of milling bodies. The X-ray diffraction, Raman spectroscopy and electron microscopy studies showed that the 60 min mechanical activation of graphite decreases the number of graphene layers in graphite crystallites to 8–12 and induces their turbostratic disorder. The size of graphite particles decreases to 6.9 μm after 30 min of mechanical activation and increases to 12.1 μm when the time of mechanical activation is extended to 60 min. Similar changes are observed for the true density of graphite: after 60 min of mechanical activation it becomes equal to 2.48 ⋅ 10{sup 3} kg/m{sup 3}, which is by 10% higher than the true density of graphite not subjected to such treatment. The specific adsorption surface of graphite (S{sub BET}) reaches its maximum values, 427–460 m{sup 2}/g, after 7–12 min of mechanical activation. A further increase in the activation time to 30–60 min decreases S{sub BET} of graphite to 230–250 m{sup 2}/g. Due to attrition of steel milling bodies caused by mechanical activation, iron is accumulated in the samples and its content exceeds 5%. Iron is distributed uniformly in the graphite as the 30–100 and 3–5 nm particles of hematite and iron carbide. The IR spectroscopy study revealed the formation of 0.8 mEq/g of the hydroxyl, phenolic, lactone and carbonyl groups on the graphite surface in the course of mechanical activation. - Highlights: • Graphite was mechanically activated in air at a 100 g acceleration of milling bodies. • The amount of graphenes in graphite crystallites decreases to 8–12. • Graphite transforms into a nanocrystalline X-ray amorphous state. • A metal–graphite composite with the 30–100 and 3–5 nm iron particles is formed. • Oxygen-containing groups in the amount of

  9. Investigation of carbon near the graphite-diamond-liquid triple point

    International Nuclear Information System (INIS)

    Prawer, S.; Jamieson, D.N.

    1992-01-01

    Pulsed laser irradiation is used to heat deeply buried damage layers in diamond. Over a small range of laser powers, damage annealing, formation of buried graphitic layers, and melting of diamond followed by its conversion upon cooling into graphite are observed. The diagnostics employed are Channeling Contrast Microscopy, optical absorption, surface profilometry, and scanning and optical microscopies. The results are explained in terms of the behaviour of carbon under high internal pressures close to the diamond-graphite-liquid carbon triple point in the phase diagram. 17 refs., 3 figs

  10. Potassium vapor assisted preparation of highly graphitized hierarchical porous carbon for high rate performance supercapacitors

    Science.gov (United States)

    Liu, Zheng; Zeng, Ying; Tang, Qunli; Hu, Aiping; Xiao, Kuikui; Zhang, Shiying; Deng, Weina; Fan, Binbin; Zhu, Yanfei; Chen, Xiaohua

    2017-09-01

    Ultrahigh graphitized carbon microspheres with rich hierarchical pores (AGHPCM-1) have been successfully synthesized through the one-step activation-carbonization strategy (OACS) with porous sulfonated poly-divinylbenzene as the carbon precursor, iron as the hard template and catalyst, and potassium hydroxide (KOH) as activation agent. Through the XRD, TEM, Raman and BET analysis, AGHPCM-1 shows very high graphitization degree and rich micro-, meso- and macro-pores. More importantly, the mechanism for KOH to improve the graphitization degree of carbon materials in OACS has been illustrated by the thermodynamical theory. The tremendous heat releasing from the reaction between the catalyst precursor of Fe2O3 and potassium vapor plays a key role in the formation of graphitized carbon. It may provide a general direction to prepare highly graphitized porous carbon at a moderate temperature. Integrating the advantages of high graphitization degree and rich hierarchical porous structure, the AGHPCM-1 exhibits an excellent rate performance with a response to up to the high current density of 150 A g-1 and high scan rate of 2000 mV s-1. No obvious capacitance decay can be observed after 10000 charge/discharge cycles even at the high current density of 20 A g-1.

  11. Suppressing propylene carbonate decomposition by coating graphite electrode foil with silver

    International Nuclear Information System (INIS)

    Gao, J.; Zhang, H.P.; Fu, L.J.; Zhang, T.; Wu, Y.P.; Takamura, T.; Wu, H.Q.; Holze, R.

    2007-01-01

    A method has been developed to suppress the decomposition of propylene carbonate (PC) by coating graphite electrode foil with a layer of silver. Results from electrochemical impedance measurements show that the Ag-coated graphite electrode presents lower charge transfer resistance and faster diffusion of lithium ions in comparison with the virginal one. Cyclic voltammograms and discharge-charge measurements suggest that the decomposition of propylene carbonate and co-intercalation of solvated lithium ions are prevented, and lithium ions can reversibly intercalate into and deintercalate from the Ag-coated graphite electrode. These results indicate that Ag-coating is a good way to improve the electrochemical performance of graphitic carbon in PC-based electrolyte solutions

  12. Texture formation in iron particles using mechanical milling with graphite as a milling aid

    Energy Technology Data Exchange (ETDEWEB)

    Motozuka, S.; Hayashi, K. [Department of Mechanical Engineering, Gifu National College of Technology, 2236-2 Kamimakuwa, Motosu, Gifu 501-0495 (Japan); Tagaya, M. [Department of Materials Science and Technology, Nagaoka University of Technology, 1603-1 Kamitomioka, Nagaoka, Niigata 940-2188 (Japan); Morinaga, M. [Toyota Physical and Chemical Research Institute, 41-1, Yokomichi, Nagakute, Aichi 480-1192 (Japan)

    2015-09-15

    Crystallographically anisotropic platelet iron particles were successfully prepared using a conventional ball mill with addition of graphite (Gp) particles. The morphological and structural changes resulting from the milling were investigated using scanning electron microscopy and X-ray diffraction. The spherical iron particles were plastically deformed into platelet shapes during the milling. Simultaneously, it is suggested that the size of the Gp particles decreased and adhered as nanoparticles on the surface of the iron particles. The adhered Gp particles affected the plastic deformation behavior of the iron particles: the (001) planes of α-iron were oriented parallel to the particle face, and no preferred in-plane orientation was observed. This study not only details the preparation of soft magnetic metal particles that crystallographically oriented to enhance their magnetic properties but also provides new insight into the activities of the well-established and extensively studied mechanical milling method.

  13. Texture formation in iron particles using mechanical milling with graphite as a milling aid

    International Nuclear Information System (INIS)

    Motozuka, S.; Hayashi, K.; Tagaya, M.; Morinaga, M.

    2015-01-01

    Crystallographically anisotropic platelet iron particles were successfully prepared using a conventional ball mill with addition of graphite (Gp) particles. The morphological and structural changes resulting from the milling were investigated using scanning electron microscopy and X-ray diffraction. The spherical iron particles were plastically deformed into platelet shapes during the milling. Simultaneously, it is suggested that the size of the Gp particles decreased and adhered as nanoparticles on the surface of the iron particles. The adhered Gp particles affected the plastic deformation behavior of the iron particles: the (001) planes of α-iron were oriented parallel to the particle face, and no preferred in-plane orientation was observed. This study not only details the preparation of soft magnetic metal particles that crystallographically oriented to enhance their magnetic properties but also provides new insight into the activities of the well-established and extensively studied mechanical milling method

  14. Synthesis of partially graphitic ordered mesoporous carbons with high surface areas

    Energy Technology Data Exchange (ETDEWEB)

    Gao, Wenjun; Wan, Ying [Department of Chemistry, Key Laboratory of Resource Chemistry of Ministry of Education, Shanghai Normal University, Shanghai 200234 (China); Dou, Yuqian; Zhao, Dongyuan [Department of Chemistry, Shanghai Key Laboratory of Molecular Catalysis and Innovative Materials, Fudan University, Shanghai 200433 (China)

    2011-01-01

    Graphitic carbons with ordered mesostructure and high surface areas (of great interest in applications such as energy storage) have been synthesized by a direct triblock-copolymer-templating method. Pluronic F127 is used as a structure-directing agent, with a low-molecular-weight phenolic resol as a carbon source, ferric oxide as a catalyst, and silica as an additive. Inorganic oxides can be completely eliminated from the carbon. Small-angle XRD and N{sub 2} sorption analysis show that the resultant carbon materials possess an ordered 2D hexagonal mesostructure, uniform bimodal mesopores (about 1.5 and 6 nm), high surface area ({proportional_to}1300 m{sup 2}/g), and large pore volumes ({proportional_to}1.50 cm{sup 3}/g) after low-temperature pyrolysis (900 C). All surface areas come from mesopores. Wide-angle XRD patterns demonstrate that the presence of the ferric oxide catalyst and the silica additive lead to a marked enhancement of graphitic ordering in the framework. Raman spectra provide evidence of the increased content of graphitic sp{sup 2} carbon structures. Transmission electron microscopy images confirm that numerous domains in the ordered mesostructures are composed of characteristic graphitic carbon nanostructures. The evolution of the graphitic structure is dependent on the temperature and the concentrations of the silica additive, and ferric oxide catalyst. Electrochemical measurements performed on this graphitic mesoporous carbon when used as an electrode material for an electrochemical double layer capacitor shows rectangular-shaped cyclic voltammetry curves over a wide range of scan rates, even up to 200 mV/s, with a large capacitance of 155 F/g in KOH electrolyte. This method can be widely applied to the synthesis of graphitized carbon nanostructures. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  15. Positron annihilation study of graphite, glassy carbon and C60/C70 fullerene

    International Nuclear Information System (INIS)

    Hasegawa, Masayuki; Kajino, Masahiro; Yamaguchi, Sadae; Iwata, Tadao; Kuramoto, Eiichi; Takenaka, Minoru.

    1992-01-01

    ACAR (Angular Correlation of Annihilation Radiation) and positron lifetime measurements have been made on, HOPG (Highly Oriented Pyrolytic Graphite), isotropic fine-grained graphite, glassy carbons and C 60 /C 70 powder. HOPG showed marked bimodality along the c-axis and anisotropy in ACAR momentum distribution, which stem from characteristic annihilation between 'interlayer' positrons and π-electrons in graphite. ACAR curves of the isotropic graphite and glassy carbons are even narrower than that of HOPG perpendicular to the c-axis. Positron lifetime of 420 and 390 - 480 psec, much longer than that of 221 psec in HOPG, were observed for the isotropic graphite and glassy carbons respectively, which are due to positron trapping in structural voids in them. Positron lifetime and ACAR width (FWHM) can be well correlated to void sizes (1.7 to 5.0 nm) of glassy carbons which have been determined by small angle neutron (SAN) scattering measurements. ACAR curves and positron lifetime of C 60 /C 70 powder agree well with those of glassy carbons. This shows that positron wave functions extend, as in the voids of glassy carbons, much wider than open spaces of the octahedral interstices of the face-centered cubic (FCC) structure of C 60 crystal and strongly suggests positron trapping in the 'soccer ball' vacancy. Possible positron states in the carbon materials are discussed with a simple model of void volume-trapping. Preliminary results on neutron irradiation damage in HOPG are also presented. (author)

  16. Substitution of Acetylene Black by Using Modified Flake Graphite Applied in Activated Carbon Supercapacitors

    Directory of Open Access Journals (Sweden)

    Zhao Peng

    2018-01-01

    Full Text Available Flake graphite was mechanically modified at different times in N-methyl pyrrolidone under normal pressure. The results of the scanning electron microscopy, X-ray diffraction, and transmission electron microscopy suggested that the structure of the flake graphite was modified. The crystallinity of the flake graphite, and many defects were introduced into the material. The evaluation of capacitor performance by cyclic voltammetry, galvanostatic charge/discharge tests, and electrochemical impedance spectroscopy was also performed. Results showed that the electrochemical performance of flake graphite was strongly enhanced, particularly when it was exfoliated for 6 h. Moreover, the electrochemical capacitive properties of activated carbon were obviously enhanced through the substitution of acetylene black by flake graphite modified for 6 h.

  17. Effects of Particle Size and Surface Chemistry on the Dispersion of Graphite Nanoplates in Polypropylene Composites

    Directory of Open Access Journals (Sweden)

    Raquel M. Santos

    2018-02-01

    Full Text Available Carbon nanoparticles tend to form agglomerates with considerable cohesive strength, depending on particle morphology and chemistry, thus presenting different dispersion challenges. The present work studies the dispersion of three types of graphite nanoplates (GnP with different flake sizes and bulk densities in a polypropylene melt, using a prototype extensional mixer under comparable hydrodynamic stresses. The nanoparticles were also chemically functionalized by covalent bonding polymer molecules to their surface, and the dispersion of the functionalized GnP was studied. The effects of stress relaxation on dispersion were also analyzed. Samples were removed along the mixer length, and characterized by microscopy and dielectric spectroscopy. A lower dispersion rate was observed for GnP with larger surface area and higher bulk density. Significant re-agglomeration was observed for all materials when the deformation rate was reduced. The polypropylene-functionalized GnP, characterized by increased compatibility with the polymer matrix, showed similar dispersion effects, albeit presenting slightly higher dispersion levels. All the composites exhibit dielectric behavior, however, the alternate current (AC conductivity is systematically higher for the composites with larger flake GnP.

  18. Growth of carbon nanotubes in arc plasma treated graphite disc: microstructural characterization and electrical conductivity study

    Science.gov (United States)

    Nayak, B. B.; Sahu, R. K.; Dash, T.; Pradhan, S.

    2018-03-01

    Circular graphite discs were treated in arc plasma by varying arcing time. Analysis of the plasma treated discs by field emission scanning electron microscope revealed globular grain morphologies on the surfaces, but when the same were observed at higher magnification and higher resolution under transmission electron microscope, growth of multiwall carbon nanotubes of around 2 nm diameter was clearly seen. In situ growth of carbon nanotube bundles/bunches consisting of around 0.7 nm tube diameter was marked in the case of 6 min treated disc surface. Both the untreated and the plasma treated graphite discs were characterized by X-ray diffraction, energy dispersive spectra of X-ray, X-ray photoelectron spectroscopy, transmission electron microscopy, micro Raman spectroscopy and BET surface area measurement. From Raman spectra, BET surface area and microstructure observed in transmission electron microscope, growth of several layers of graphene was identified. Four-point probe measurements for electrical resistivity/conductivity of the graphite discs treated under different plasma conditions showed significant increase in conductivity values over that of untreated graphite conductivity value and the best result, i.e., around eightfold increase in conductivity, was observed in the case of 6 min plasma treated sample exhibiting carbon nanotube bundles/bunches grown on disc surface. By comparing the microstructures of the untreated and plasma treated graphite discs, the electrical conductivity increase in graphite disc is attributed to carbon nanotubes (including bundles/bunches) growth on disc surface by plasma treatment.

  19. Simple synthesis of mesoporous FeNi/graphitic carbon nanocomposite catalysts and study on their activities in catalytic cracking of toluene

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Yangang, E-mail: ygwang8136@gmail.com [Department of Environmental Science and Engineering, University of Shanghai for Science and Technology, Shanghai 200093 (China); Chen, Yuting; Yao, Mingcui [Department of Environmental Science and Engineering, University of Shanghai for Science and Technology, Shanghai 200093 (China); Qin, Hengfei; Kang, Shifei; Li, Xi [Department of Environmental Science and Engineering, Fudan University, Shanghai 200433 (China); Zuo, Yuanhui; Zhang, Xiaodong [Department of Environmental Science and Engineering, University of Shanghai for Science and Technology, Shanghai 200093 (China); Cui, Li-Feng, E-mail: lifeng.cui@gmail.com [Department of Environmental Science and Engineering, University of Shanghai for Science and Technology, Shanghai 200093 (China)

    2015-11-01

    Mesoporous FeNi alloy/graphitic carbon nanocomposite catalysts with different Fe/Ni molar ratios have been synthesized through a simple solid–liquid grinding/templating method using mesoporous silica SBA-15 as the template. Metal nitrates and natural soybean oil were respectively used as the magnetic particle precursors and carbon source, which can be infiltrated into the silica template after simple impregnation, grinding and subsequent heat treatment. X-ray diffraction, nitrogen adsorption–desorption, transmission electron microscopy and thermogravimetric analysis techniques were used to characterize the samples. It is observed that high contents of FeNi alloy nanoparticles with the sizes of 3–6 nm are well dispersed into the walls of graphitic mesoporous carbon matrix, and the resulting nanocomposites have a uniform mesostructure with a high specific surface area and large pore volume. Because of these properties, the obtained FeNi/graphitic carbon nanocomposites can be used as novel catalysts for the catalytic cracking of toluene and exhibit a higher activity and stability than FeNi/commercial activated carbon (AC) catalyst. After a period of 810 min reaction at 700 °C, the toluene conversion on the FeNi/graphitic carbon nanocomposites can be maintained at a level of more than 75% and this value is 2.5 times as high as that of the FeNi/AC catalyst. - Highlights: • Mesoporous FeNi alloy/graphitic carbon nanocomposites (FeNi/GCN) were synthesized. • High contents of FeNi alloy nanoparticles are well embedded into the graphitic carbon walls. • The obtained FeNi/GCN catalysts have a high surface area and uniform mesostructure. • The FeNi/GCN catalysts exhibited excellent catalytic performance in the cracking of toluene.

  20. Large-strain Soft Sensors Using Elastomers Blended with Exfoliated/Fragmented Graphite Particles

    Energy Technology Data Exchange (ETDEWEB)

    Park, Sungmin; Nam, Gyungmok; Kim, Jonghun; Yoon, Sang-Hee [Inha Univ., Incheon (Korea, Republic of)

    2016-09-15

    An elastic polymer (e.g., PDMS) blended with EFG particles is a promising conductive composite for fabricating soft sensors that can detect an object's deformation up to or more than 50 %. Here, we develop large-strain, sprayable soft sensors using a mixture of PDMS and EFG particles, which are used as a host elastomer and electrically conductive particles, respectively. A solution for a conductive composite mixture is prepared by the microwave-assisted graphite exfoliation, followed by ultrasonication-induced fragmentation of the exfoliated graphite and ultrasonic blending of PDMS and EFG. Using the prepared solutions for composite and pure PDMS, 1-, 2-, and 3-axis soft sensors are fabricated by airbrush stencil technique where composite mixture and pure PDMS are materials for sensing and insulating layers, respectively. We characterize the soft strain sensors after investigating the effect of PDMS/EFG wt % on mechanical compliance and electrical conductance of the conductive composite.

  1. Scanning transmission electron microscopy analysis of Ge(O)/(graphitic carbon nitride) nanocomposite powder

    Energy Technology Data Exchange (ETDEWEB)

    Kawasaki, Masahiro [JEOL USA Inc., 11 Dearborn Road, Peabody, MA 01960 (United States); Sompetch, Kanganit [Department of Chemistry and Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Sarakonsri, Thapanee, E-mail: tsarakonsri@gmail.com [Department of Chemistry and Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Shiojiri, Makoto [Kyoto Institute of Technology, Kyoto 606-8585 (Japan); School of Science and Engineering, University of Toyama, Toyama 930-8555 (Japan)

    2015-12-15

    Analytical electron microscopy has revealed the structure of particles that were synthesized by chemical reaction of GeO{sub 2} with NaBH{sub 4} in the basic solution including graphitic carbon nitride (g-C{sub 3}N{sub 4}) powders. The g-C{sub 3}N{sub 4} was arranged by recrystallization of melamine at 600 °C under N{sub 2} gas atmosphere. The samples were dried at 60 °C or 180 °C for 4 h. The g-C{sub 3}N{sub 4} was observed as lamellae of several ten nm or less in size and had an amorphous-like structure with a distorted lattice in an area as small as a few hundred pm in size. The reaction product was Ge(O) particles as fine as several nm in size and composed of Ge and O atoms. Most of the particles must be of GeO{sub 2−x} with the amorphous-like structure that has also a distorted lattice in an area of a few hundred pm in size. In the sample dried at 60 °C, the particles were found to be dispersed in a wide area on the g-C{sub 3}N{sub 4} lamella. It is hard to recognize those particles in TEM images. The particles in the sample dried at 180 °C became larger and were easily observed as isolated lumps. Hence, these powders can be regarded as GeO{sub 2}/g-C{sub 3}N{sub 4} or Ge/GeO{sub 2}/g-C{sub 3}N{sub 4} nanocomposites, and expected to be applicable to anode materials for high energy Li-ion batteries due to Ge catalysis effect, accordingly. - Graphical abstract: STEM analysis of Ge(O)/(graphitic carbon nitride) nanocomposite powder. - Highlights: • Graphitic (g)-C{sub 3}N{sub 4} powder was prepared at 600 °C by recrystallization of melamine. • Ge(O) was prepared by chemical reaction in a solution including the g-C{sub 3}N{sub 4} powders. • The products can be regarded as GeO{sub 2}/g-C{sub 3}N{sub 4} or Ge/GeO{sub 2}/g-C{sub 3}N{sub 4} nanocomposites. • GeO{sub 2} was amorphous several-nm particles and g-C{sub 3}N{sub 4} was amorphous lamella of several 10 nm in size. • We expect them to be applicable for high energy Li-ion battery anode

  2. Tritium retention properties of tungsten, graphite and co-deposited carbon film

    International Nuclear Information System (INIS)

    Nobuta, Y.; Hatano, Y.; Matsuyama, M.; Abe, S.; Akamaru, S.; Yamauchi, Y.; Hino, T.; Suzuki, S.; Akiba, M.

    2014-01-01

    DT + ion irradiation was performed on polycrystalline tungsten, graphite and carbon film and both the amount of retained tritium and the reduction of retained tritium after preservation in vacuum were investigated using an IP technique and BIXS. In addition, the relationship between the retention properties of tritium and the microstructure of graphite and carbon film were studied with Raman spectroscopy. The amount of retained tritium in tungsten was smaller than in both graphite and carbon film. After 1 keV of DT + irradiation, graphite showed no reduction of the amount of retained tritium after six months preservation while that of carbon film decreased by approximately 20% after 40 days preservation. It was suggested that this difference might be associated with differences in the microstructure between graphite and carbon film. In tungsten, the amount of retained tritium decreased to approximately half after 18 days preservation. As the incident energy of implanted tritium to tungsten increased, the decrease in tritium retention during preservation became slower. Tungsten's properties of releasing tritium while preserved in vacuum would be a useful tool for the reduction/removal of retained tritium

  3. Theory and simulation of epitaxial rotation. Light particles adsorbed on graphite

    DEFF Research Database (Denmark)

    Vives, E.; Lindgård, P.-A.

    1993-01-01

    We present a theory and Monte Carlo simulations of adsorbed particles on a corrugated substrate. We have focused on the case of rare gases and light molecules, H-2 and D2, adsorbed on graphite. The competition between the particle-particle and particle-substrate interactions gives rise to frustra...... found a modulated 4 x 4 structure. Energy, structure-factor intensities, peak positions, and epitaxial rotation angles as a function of temperature and coverage have been determined from the simulations. Good agreement with theory and experimental data is found.......We present a theory and Monte Carlo simulations of adsorbed particles on a corrugated substrate. We have focused on the case of rare gases and light molecules, H-2 and D2, adsorbed on graphite. The competition between the particle-particle and particle-substrate interactions gives rise...... between the commensurate and incommensurate phase for the adsorbed systems. From our simulations and our theory, we are, able to understand the gamma phase of D2 as an ordered phase stabilized by disorder. It can be described as a 2q-modulated structure. In agreement with the experiments, we have also...

  4. Report on the study of erosion and H-recycle/inventory of carbon/graphite

    International Nuclear Information System (INIS)

    Haasz, A.A.; Davis, J.W.

    1990-04-01

    This study investigated the erosion and hydrogen retention capacity of graphite under plasma exposure by performing controlled plasma simulation experiments using a low-energy high-flux mass analyzed ion accelerator. The authors studied radiation-enhanced sublimation (RES) of graphite, the effect of ion angle of incidence on physical sputtering, the effect of oxygen on hydrocarbon formation during O 2 /H 2 impact, chemical erosion of boron carbide, and the effect of thermal atoms on self-sputtering of graphite. The flux dependence of RES is nearly linear (power of .91) for the extended flux range of 10 13 - 10 17 H + /cm 2 s. Physical sputtering yields were enhanced for off-normal angles of incidence, especially for highly-oriented polished surfaces. Oxygen did not appear to have an effect on the hydrocarbon formation rate; however, some erosion through CO formation was observed. Although large transients were observed in hydrocarbon production in B 4 C, steady-state levels were typically about two orders of magnitude below the erosion rate of graphite. To investigate carbon self-sputtering, thermal H 0 atoms were added to impacting C + ions, simulating a condition existing in the tokamak plasma edge. This led to a synergistic enhancement of the chemical erosion process. For C + /H+0 flux ratios of less than about 10 -1 the chemical erosion yield exceeds unity. Work on hydrogen retention concentrated on the study of H + trapping in different types of graphites as a function of flux and fluence of incident H + . The amount of H trapped in the near-surface region of graphite reaches a saturation level, a function of graphite temperature and impacting H + energy. The amount of H trapped in graphite beyond the ion range was found to increase with increasing fluence and varied for different graphites tested. It seems that hydrogen diffuses through grain boundaries and open porosity in the material until trapped by available carbon bonds

  5. Comparison of the tribology performance of nano-diesel soot and graphite particles as lubricant additives

    International Nuclear Information System (INIS)

    Zhang, Zu-chuan; Cai, Zhen-bing; Peng, Jin-fang; Zhu, Min-hao

    2016-01-01

    The tribology behavior of exhaust diesel soot as a lubricant additive was investigated and then compared with that of a selection of commercial nano-graphite particles. Specifically, 0.01 wt% particles were dispersed in PAO4 oil with 1 wt% sorbitan monooleate (Span 80) as a dispersing agent, and wear tests based on the ball against plate mode were conducted at various temperatures. Different analytical techniques (e.g. transmission electron, scanning electron and infrared microscopy; energy dispersive x-ray and Raman spectroscopy; and charge measurement) were employed to characterize the chemistry and morphology of the additives and their tribology performance. The oil containing only 0.01 wt% diesel soot clearly improved wear resistance over 60 °C. In particular, at 100 °C the wear rate decreased by approximately 90% compared to the function of base oil. In the same test conditions, diesel soot exhibited better anti-wear performance than nano-graphite at high temperatures. The potential measure showed that the nano-graphite had positive charge and the diesel soot had negative charge. Electrochemical action may play an important role in the lubricant mechanisms of diesel soot and graphite as oil additives. (paper)

  6. Blackbody Radiation and the Carbon Particle

    Directory of Open Access Journals (Sweden)

    Robitaille P.-M.

    2008-07-01

    Full Text Available Since the days of Kirchhoff, blackbody radiation has been considered to be a uni- versal process, independent of the nature and shape of the emitter. Nonetheless, in promoting this concept, Kirchhoff did require, at the minimum, thermal equilibrium with an enclosure. Recently, the author stated (P.-M. Robitaille, IEEE Trans. Plasma Sci. , 2003, v. 31(6, 1263–1267; P.-M. Robitaille, Progr. in Phys. , 2006, v. 2, 22–23, that blackbody radiation is not universal and has called for a return to Stewart’s law (P.-M. Robitaille, Progr. in Phys. , 2008, v. 3, 30–35. In this work, a historical analysis of thermal radiation is presented. It is demonstrated that soot, or lampblack, was the standard for blackbody experiments throughout the 1800s. Furthermore, graphite and carbon black continue to play a central role in the construction of blackbody cavities. The advent of universality is reviewed through the writings of Pierre Prevost, Pierre Louis Dulong, Alexis Therese Petit, Jean Baptiste Joseph Fourier, Simeon Denis Pois- son, Frederick Herve de la Provostaye, Paul Quentin Desain, Balfour Stewart, Gustav Robert Kirchhoff, and Max Karl Ernst Ludwig Planck. These writings illustrate that blackbody radiation, as experimentally produced in cavities and as discussed theoreti- cally, has remained dependent on thermal equilibrium with at least the smallest carbon particle. Finally, Planck’s treatment of Kirchhoff’s law is examined in detail and the shortcomings of his derivation are outlined. It is shown once again, that universality does not exist. Only Stewart’s law of thermal emission, not Kirchhoff’s, is fully valid.

  7. Blackbody Radiation and the Carbon Particle

    Directory of Open Access Journals (Sweden)

    Pierre-Marie Robitaille

    2008-07-01

    Full Text Available Since the days of Kirchhoff, blackbody radiation has been considered to be a universal process, independent of the nature and shape of the emitter. Nonetheless, in promoting this concept, Kirchhoff did require, at the minimum, thermal equilibrium with an enclosure. Recently, the author stated (P.-M. Robitaille, IEEE Trans. Plasma Sci., 2003, v.31(6, 1263-1267; P.-M. Robitaille, Progr. in Phys., 2006, v.2, 22-23, that blackbody radiation is not universal and has called for a return to Stewart's law (P.-M. Robitaille, Progr. in Phys., 2008, v.3, 30-35. In this work, a historical analysis of thermal radiation is presented. It is demonstrated that soot, or lampblack, was the standard for blackbody experiments throughout the 1800s. Furthermore, graphite and carbon black continue to play a central role in the construction of blackbody cavities. The advent of universality is reviewed through the writings of Pierre Prevost, Pierre Louis Dulong, Alexis Therese Petit, Jean Baptiste Joseph Fourier, Simeon Denis Poisson, Frederick Herve de la Provostaye, Paul Quentin Desain, Balfour Stewart, Gustav Robert Kirchhoff, and Max Karl Ernst Ludwig Planck. These writings illustrate that blackbody radiation, as experimentally produced in cavities and as discussed theoretically, has remained dependent on thermal equilibrium with at least the smallest carbon particle. Finally, Planck's treatment of Kirchhoff's law is examined in detail and the shortcomings of his derivation are outlined. It is shown once again, that universality does not exist. Only Stewart's law of thermal emission, not Kirchhoff's, is fully valid.

  8. Functionalization/passivation of porous graphitic carbon with di-tert-amylperoxide

    Energy Technology Data Exchange (ETDEWEB)

    Jensen, David S.; Gupta, Vipul; Olsen, Rebecca E.; Miller, Alex T.; Davis, Robert C.; Ess, Daniel; Zhu, Zihua; Vail, Michael A.; Dadson, Andrew; Linford, Matthew R.

    2011-11-18

    Porous graphitic carbon (PGC) particles were functionalized/passivated in situ in packed beds at elevated temperature with neat di-tert-amylperoxide (DTAP) in a column oven. The performance of these particles for high performance liquid chromatography (HPLC) was assayed before and after this chemistry with the following analytes: benzene, toluene, ethyl benzene, n-propyl benzene, n-butyl benzene, p-xylene, phenol, 4-methylphenol, phenetole, 3,5-xylenol, and anisole. After the first functionalization/passivation, the retention factors, k, of these compounds decreased by about 5% and the number of theoretical plates (N) increased by ca. 15%. These values of k then remained roughly constant after a second functionalization/ passivation but a further increase in N was noticed. In addition, after each of the reactions, the peak asymmetries decreased by ca. 15%, for a total of ca. 30%. The columns were then subjected twice to methanol at 100 C for 5 h at 1 mL/min. After these stability tests, the values of k remained roughly constant, the number of plates increased, which is favorable, and the asymmetries rose and then declined, where they remained below the initial values for the unfunctionalized columns. Functionalized and unfunctionalized particles were characterized by scanning electron microscopy and BET measurements, which showed no difference between the functionalized and unfunctionalized materials, and X-ray photoelectron spectroscopy and time-of-flight secondary ion mass spectrometry (ToF-SIMS), where ToF-SIMS suggested some chemical differences between the functionalized and unfunctionalized materials. In particular ToF-SIMS suggested that the expected five-carbon fragments from DTAP exist at higher concentrations on DTAP-functionalized PGC. First principle calculations on model graphitic surfaces suggest that the first addition of a DTAP radical to the surface proceeds in an approximately isothermal or slightly favorable fashion, but that subsequent DTAP

  9. Temperature dependence of the thermal expansion of neutron-irradiated pyrolytic carbon and graphite

    International Nuclear Information System (INIS)

    Matsuo, Hideto

    1988-01-01

    The effects of neutron irradiation and annealing on the temperature dependence of the linear thermal expansion of pyrolytic carbon and graphite were investigated after irradiation at 930-1280 0 C to a maximum neutron fluence of 2.84 x 10 25 m -2 (E > 29 fJ). After irradiation, little change in the thermal expansion of pyrolytic graphite was observed. However, as-deposited pyrolytic carbon showed an increase in thermal expansion in the perpendicular direction, a decrease in the direction parallel to the deposition plane, and also an increase in the anisotropy of the thermal expansion. Annealing at 2000 0 C did not cause any effective changes for irradiated specimens of either as-deposited pyrolytic carbon or pyrolytic graphite. (author)

  10. From spent graphite to amorphous sp2+sp3 carbon-coated sp2 graphite for high-performance lithium ion batteries

    Science.gov (United States)

    Ma, Zhen; Zhuang, Yuchan; Deng, Yaoming; Song, Xiaona; Zuo, Xiaoxi; Xiao, Xin; Nan, Junmin

    2018-02-01

    Today, with the massive application of lithium ion batteries (LIBs) in the portable devices and electric vehicles, to supply the active materials with high-performances and then to recycle their wastes are two core issues for the development of LIBs. In this paper, the spent graphite (SG) in LIBs is used as raw materials to fabricate two comparative high-capacity graphite anode materials. Based on a microsurgery-like physical reconstruction, the reconstructed graphite (RG) with a sp2+sp3 carbon surface is prepared through a microwave exfoliation and subsequent spray drying process. In contrast, the neural-network-like amorphous sp2+sp3 carbon-coated graphite (AC@G) is synthesized using a self-reconfigurable chemical reaction strategy. Compared with SG and commercial graphite (CG), both RG and AC@G have enhanced specific capacities, from 311.2 mAh g-1 and 360.7 mAh g-1 to 409.7 mAh g-1 and 420.0 mAh g-1, at 0.1C after 100 cycles. In addition, they exhibit comparable cycling stability, rate capability, and voltage plateau with CG. Because the synthesis of RG and AC@G represents two typical physical and chemical methods for the recycling of SG, these results on the sp2+sp3 carbon layer coating bulk graphite also reveal an approach for the preparation of high-performance graphite anode materials derived from SG.

  11. Strongly Localized Image States of Spherical Graphitic Particles

    Directory of Open Access Journals (Sweden)

    Godfrey Gumbs

    2014-01-01

    Full Text Available We investigate the localization of charged particles by the image potential of spherical shells, such as fullerene buckyballs. These spherical image states exist within surface potentials formed by the competition between the attractive image potential and the repulsive centripetal force arising from the angular motion. The image potential has a power law rather than a logarithmic behavior. This leads to fundamental differences in the nature of the effective potential for the two geometries. Our calculations have shown that the captured charge is more strongly localized closest to the surface for fullerenes than for cylindrical nanotube.

  12. Significance of Graphitic Surfaces in Aurodicyanide Adsorption by Activated Carbon: Experimental and Computational Approach

    Science.gov (United States)

    Bhattacharyya, Dhiman; Depci, Tolga; Prisbrey, Keith; Miller, Jan D.

    Despite tremendous developments in industrial use of activated carbon (AC) for gold adsorption, specific aurodicyanide [Au(CN)2-] adsorption sites on the carbon have intrigued researchers. The graphitic structure of AC has been well established. Previously radiochemical and now, XPS and Raman characterizations have demonstrated higher site-specific gold adsorption on graphitic edges. Morphological characterizations have revealed the presence of slit-pores (5-10 Å). Molecular-dynamics-simulation (MDS) performed on graphitic slit-pores illustrated gold-cyanide ion-pair preferentially adsorbs on edges. Ab-initio simulations predicted lower barrier for electron sharing in pores with aurodic yanide, indicating tighter bonding than graphitic surface and was well supported by Gibbs energy calculations too. Interaction energy as function of the separation distance indicated tighter bonding of gold cyanide to the graphite edges than water molecules. Selective adsorption of aurodicyanide ion-pair seems to be related to low polarity of gold complex and its accommodation at graphitic edges.

  13. Process for purifying graphite

    International Nuclear Information System (INIS)

    Clausius, R.A.

    1985-01-01

    A process for purifying graphite comprising: comminuting graphite containing mineral matter to liberate at least a portion of the graphite particles from the mineral matter; mixing the comminuted graphite particles containing mineral matter with water and hydrocarbon oil to form a fluid slurry; separating a water phase containing mineral matter and a hydrocarbon oil phase containing grahite particles; and separating the graphite particles from the hydrocarbon oil to obtain graphite particles reduced in mineral matter. Depending upon the purity of the graphite desired, steps of the process can be repeated one or more times to provide a progressively purer graphite

  14. Nanoscale Electrochemistry of sp(2) Carbon Materials: From Graphite and Graphene to Carbon Nanotubes.

    Science.gov (United States)

    Unwin, Patrick R; Güell, Aleix G; Zhang, Guohui

    2016-09-20

    Carbon materials have a long history of use as electrodes in electrochemistry, from (bio)electroanalysis to applications in energy technologies, such as batteries and fuel cells. With the advent of new forms of nanocarbon, particularly, carbon nanotubes and graphene, carbon electrode materials have taken on even greater significance for electrochemical studies, both in their own right and as components and supports in an array of functional composites. With the increasing prominence of carbon nanomaterials in electrochemistry comes a need to critically evaluate the experimental framework from which a microscopic understanding of electrochemical processes is best developed. This Account advocates the use of emerging electrochemical imaging techniques and confined electrochemical cell formats that have considerable potential to reveal major new perspectives on the intrinsic electrochemical activity of carbon materials, with unprecedented detail and spatial resolution. These techniques allow particular features on a surface to be targeted and models of structure-activity to be developed and tested on a wide range of length scales and time scales. When high resolution electrochemical imaging data are combined with information from other microscopy and spectroscopy techniques applied to the same area of an electrode surface, in a correlative-electrochemical microscopy approach, highly resolved and unambiguous pictures of electrode activity are revealed that provide new views of the electrochemical properties of carbon materials. With a focus on major sp(2) carbon materials, graphite, graphene, and single walled carbon nanotubes (SWNTs), this Account summarizes recent advances that have changed understanding of interfacial electrochemistry at carbon electrodes including: (i) Unequivocal evidence for the high activity of the basal surface of highly oriented pyrolytic graphite (HOPG), which is at least as active as noble metal electrodes (e.g., platinum) for outer

  15. Carbon fuel particles used in direct carbon conversion fuel cells

    Science.gov (United States)

    Cooper, John F.; Cherepy, Nerine

    2012-10-09

    A system for preparing particulate carbon fuel and using the particulate carbon fuel in a fuel cell. Carbon particles are finely divided. The finely dividing carbon particles are introduced into the fuel cell. A gas containing oxygen is introduced into the fuel cell. The finely divided carbon particles are exposed to carbonate salts, or to molten NaOH or KOH or LiOH or mixtures of NaOH or KOH or LiOH, or to mixed hydroxides, or to alkali and alkaline earth nitrates.

  16. Carbon Fuel Particles Used in Direct Carbon Conversion Fuel Cells

    Science.gov (United States)

    Cooper, John F.; Cherepy, Nerine

    2008-10-21

    A system for preparing particulate carbon fuel and using the particulate carbon fuel in a fuel cell. Carbon particles are finely divided. The finely dividing carbon particles are introduced into the fuel cell. A gas containing oxygen is introduced into the fuel cell. The finely divided carbon particles are exposed to carbonate salts, or to molten NaOH or KOH or LiOH or mixtures of NaOH or KOH or LiOH, or to mixed hydroxides, or to alkali and alkaline earth nitrates.

  17. Superparamagnetism in carbon-coated Co particles produced by the Kratschmer carbon arc process

    Science.gov (United States)

    McHenry, M. E.; Majetich, S. A.; Artman, J. O.; Degraef, M.; Staley, S. W.

    1994-04-01

    A process based on the Kratschmer-Huffman carbon arc method of preparing fullerenes has been used to generate carbon-coated cobalt and cobalt carbide nanocrystallites. Magnetic nanocrystallites are extracted from the soot with a gradient field technique. For Co/C composites, structural characterization by x-ray diffraction and high-resolution transmission electron microscopy reveals the presence of a fcc Co phase, graphite, and a minority Co2C phase. The majority of Co nanocrystals exists as nominally spherical particles, 0.5-5 nm in radius. Hysteretic and temperature-dependent magnetic response, in randomly and magnetically aligned powder samples frozen in epoxy reveals fine-particle magnetism associated with monodomain Co particles. The magnetization exhibits a unique functional dependence on H/T, and hysteresis below a blocking temperature, TB~=160 K. Below TB, the temperature dependence of the coercivity is given by Hc=Hci[1-(T/TB)1/2], with Hci~=450 Oe.

  18. A process for the production of a scale-proof and corrosion-resistant coating on graphite and carbon bodies

    Science.gov (United States)

    Fitzer, E.

    1981-01-01

    A process for the production of a corrosion resistant coating on graphite and carbon bodies is described. The carbon or graphite body is coated or impregnated with titanium silicide under the addition of a metal containing wetting agent in a nitrogen free atmosphere, so that a tight coating is formed.

  19. Anodic polarization of carbon graphite electrodes in chloride fluoride melts zirconium containing

    International Nuclear Information System (INIS)

    Lyapustin, A.A.; Kanashin, Yu.P.; Nichkov, I.F.; Smyshlyaev, V.Yu.

    1985-01-01

    Polarization of carbon graphite anodes in zircorium containing chloride fluoride melts of the KCl-K 2 ZrF 6 -KF composition at molar ratios [F]:[Zr] being equal to 6, 12, 18, 24, 30 has been studied. K 2 ZrF 6 concentration constitutes 25; 18.9; 15.2; 12.7; 11.8% (by mass), correspondingly. Vitreous carbon (VC-2500), high purity graphite and graphite EhG-0 have been used as anodic materials. Anodic polarization curves have been obtained under electrotype steady-state conditions at 973, 1023, 1073 K. Influence of concentration of fluorine ions in melt on polarization of carbon graphite anodes is shown. Content growth of fluorine ions in melt leads to shift of steady-state anode potentials to their negative values regardless a graphite mark. The most con siderable potential shift on 0.5 V takes plase at molar ratio [F]:[Zr] increasing from 6 to 12. Temperature increase, as measurements showed, doesn't influence greatly on polarization curve shape

  20. Synthesis of metal free ultrathin graphitic carbon nitride sheet for photocatalytic dye degradation of Rhodamine B under visible light irradiation

    Science.gov (United States)

    Rahman, Shakeelur; Momin, Bilal; Higgins M., W.; Annapure, Uday S.; Jha, Neetu

    2018-04-01

    In recent times, low cost and metal free photocatalyts driven under visible light have attracted a lot of interest. One such photo catalyst researched extensively is bulk graphitic carbon nitride sheets. But the low surface area and weak mobility of photo generated electrons limits its photocatalytic performance in the visible light spectrum. Here we present the facile synthesis of ultrathin graphitic carbon nitride using a cost effective melamine precursor and its application in highly efficient photocatalytic dye degradation of Rhodamine B molecules. Compared to bulk graphitic carbon nitride, the synthesized ultrathin graphitic carbon nitride shows an increase in surface area, a a decrease in optical band gap and effective photogenerated charge separation which facilitates the harvest of visible light irradiation. Due to these optimal properties of ultrathin graphitic carbon nitride, it shows excellent photocatalytic activity with photocatalytic degradation of about 95% rhodamine B molecules in 1 hour.

  1. Nitrogen-Rich Polyacrylonitrile-Based Graphitic Carbons for Hydrogen Peroxide Sensing

    Directory of Open Access Journals (Sweden)

    Brandon Pollack

    2017-10-01

    Full Text Available Catalytic substrate, which is devoid of expensive noble metals and enzymes for hydrogen peroxide (H2O2, reduction reactions can be obtained via nitrogen doping of graphite. Here, we report a facile fabrication method for obtaining such nitrogen doped graphitized carbon using polyacrylonitrile (PAN mats and its use in H2O2 sensing. A high degree of graphitization was obtained with a mechanical treatment of the PAN fibers embedded with carbon nanotubes (CNT prior to the pyrolysis step. The electrochemical testing showed a limit of detection (LOD 0.609 µM and sensitivity of 2.54 µA cm−2 mM−1. The promising sensing performance of the developed carbon electrodes can be attributed to the presence of high content of pyridinic and graphitic nitrogens in the pyrolytic carbons, as confirmed by X-ray photoelectron spectroscopy. The reported results suggest that, despite their simple fabrication, the hydrogen peroxide sensors developed from pyrolytic carbon nanofibers are comparable with their sophisticated nitrogen-doped graphene counterparts.

  2. Electrochemical properties of carbon nanocoils and hollow graphite fibers as anodes for rechargeable lithium ion batteries

    International Nuclear Information System (INIS)

    Wang, Liyong; Liu, Zhanjun; Guo, Quangui; Wang, Guizhen; Yang, Jinhua; Li, Peng; Wang, Xianglei; Liu, Lang

    2016-01-01

    Carbon nanocoils (CNCs) have been used as anode materials for preparation of lithium ion batteries. As pure carbon material without any chemical modification, the graphitized CNCs anode exhibited larger capacities with good Coulombic efficiency, a higher rate capability, and better reversibility than the hollow graphite fibers (HGFs) anode. The excellent performance of the CNCs was possibly ascribed to the special structure and the high degree of graphitization. As a result, the CNCs anode exhibited high reversible capacity of 385.5 mA h g"−"1 at 50 mA g"−"1, 104.7% reversible capacity retention after 105 cycles, and superior reversible capability of 177.4 mA h g"−"1 at 1 A g"−"1 after 100 cycles. This result indicated that CNCs could be an attractive choice as anode material for high-energy density and high-power lithium-ion batteries.

  3. Sample distillation/graphitization system for carbon pool analysis by accelerator mass spectrometry (AMS)

    International Nuclear Information System (INIS)

    Pohlman, J.W.; Knies, D.L.; Grabowski, K.S.; DeTurck, T.M.; Treacy, D.J.; Coffin, R.B.

    2000-01-01

    A facility at the Naval Research Laboratory (NRL), Washington, DC, has been developed to extract, trap, cryogenically distill and graphitize carbon from a suite of organic and inorganic carbon pools for analysis by accelerator mass spectrometry (AMS). The system was developed to investigate carbon pools associated with the formation and stability of methane hydrates. However, since the carbon compounds found in hydrate fields are ubiquitous in aquatic ecosystems, this apparatus is applicable to a number of oceanographic and environmental sample types. Targeted pools are dissolved methane, dissolved organic carbon (DOC), dissolved inorganic carbon (DIC), solid organic matrices (e.g., seston, tissue and sediments), biomarkers and short chained (C 1 -C 5 ) hydrocarbons from methane hydrates. In most instances, the extraction, distillation and graphitization events are continuous within the system, thus, minimizing the possibility of fractionation or contamination during sample processing. A variety of methods are employed to extract carbon compounds and convert them to CO 2 for graphitization. Dissolved methane and DIC from the same sample are sparged and cryogenically separated before the methane is oxidized in a high temperature oxygen stream. DOC is oxidized to CO 2 by 1200 W ultraviolet photo-oxidation lamp, and solids oxidized in sealed, evacuated tubes. Hydrocarbons liberated from the disassociation of gas hydrates are cryogenically separated with a cryogenic temperature control unit, and biomarkers separated and concentrated by preparative capillary gas chromatography (PCGC). With this system, up to 20 samples, standards or blanks can be processed per day

  4. Formation of carbon nanotubes in the graphite surface by Ar ion sputtering

    International Nuclear Information System (INIS)

    Wang Zhenxia; Zhu Fuying; Wang Wenmin; Yu Guoqing; Ruan Meiling; Zhang Huiming; Zhu Jingping

    1998-01-01

    The authors have investigated structures and topography features of sputtered graphite surface using scanning electron microscopy (SEM) and transmission electron microscopy (TEM), and demonstrated that carbon nanotubes can be grown up by sputtered-atom deposition on a protrusion of topography feature

  5. On the Crystallization of Compacted and Chunky Graphite from Liquid Multicomponent Iron-Carbon-Silicon-Based Melts

    Science.gov (United States)

    Stefanescu, D. M.; Huff, R.; Alonso, G.; Larrañaga, P.; De la Fuente, E.; Suarez, R.

    2016-08-01

    Extensive SEM work was carried out on deep-etched specimens to reveal the evolution of compacted and chunky graphite in magnesium-modified multicomponent Fe-C-Si alloys during early solidification and at room temperature. The findings of this research were then integrated in the current body of knowledge to produce an understanding of the crystallization of compacted and chunky graphite. It was confirmed that growth from the liquid for both compacted and chunky graphite occurs radially from a nucleus, as foliated crystals and dendrites. The basic building blocks of the graphite aggregates are hexagonal faceted graphite platelets with nanometer height and micrometer width. Thickening of the platelets occurs through growth of additional graphene layers nucleated at the ledges of the graphite prism. Additional thickening resulting in complete joining of the platelets may occur from the recrystallization of the amorphous carbon that has diffused from the liquid through the austenite, once the graphite aggregate is enveloped in austenite. With increasing magnesium levels, the foliated graphite platelets progressively aggregate along the c-axis forming clusters. The clusters that have random orientation, eventually produce blocky graphite, as the spaces between the parallel platelets disappear. This is typical for compacted graphite irons and tadpole graphite. The chunky graphite aggregates investigated are conical sectors of graphite platelets stacked along the c-axis. The foliated dendrites that originally develop radially from a common nucleus may aggregate along the c-axis forming blocky graphite that sometimes exhibits helical growth. The large number of defects (cavities) observed in all graphite aggregates supports the mechanism of graphite growth as foliated crystals and dendrites.

  6. Modifications of Graphite and Multiwall Carbon Nanotubes in the Presence of Urea

    Science.gov (United States)

    Duraia, El-Shazly M.; Fahami, Abbas; Beall, Gary W.

    2018-02-01

    The effect of high-energy ball milling on two carbon allotropes, graphite and multiwall carbon nanotubes (MWCNT) in the presence of urea has been studied. Samples were investigated using Raman spectroscopy, x-ray diffraction, scanning electron microscope (SEM) and x-ray photoelectron spectroscopy (XPS). Nitrogen-doped graphene has been successfully synthesized via a simple scalable mechanochemistry method using urea and graphite powder precursors. XPS results revealed the existence of the different nitrogen atoms configurations including pyridine, pyrrodic and graphitic N. SEM observations showed that the graphene nanosheets morphology become more wrinkles folded and crumbled as the milling time increased. The ID/IG ratio also increased as the milling time rose. The presence of both D' and G + D bands at 1621 cm-1 and 2940 cm-1, respectively, demonstrated the nitrogen incorporation in the graphene lattice Two factors contribute to the used urea: first it helps to exfoliate graphite into graphene, and second it preserves the graphitic structure from damage during the milling process as well as acting as a solid-state nitrogen source. Based on the phase analysis, the d-spacing of MWCNT samples in the presence of urea decreased due to the mechanical force in the milling process as the milling time increased. On the other hand, in the graphite case, due to its open flat surface, the graphite (002) peak shifts toward lower two theta as the milling time increase. Such findings are important and could be used for large-scale production of N-doped graphene, diminishing the use of either dangerous chemicals or sophisticated equipment.

  7. Mechanical and tribological properties of acrylonitrile–butadiene rubber filled with graphite and carbon black

    International Nuclear Information System (INIS)

    Wang, Lei Lei; Zhang, Li Qun; Tian, Ming

    2012-01-01

    Highlights: ► Graphite/carbon black/rubber micro- and nano-composites were prepared. ► Nanocomposites showed better mechanical properties and wear resistance. ► The effect of load and sliding speed on friction and wear is significant. ► Graphite lubricant film can reduce friction coefficient and wear rate. -- Abstract: In this work, acrylonitrile–butadiene rubber (NBR)/expanded graphite (EG)/carbon black (CB) micro- and nanocomposites were prepared by two different methods, and the resulting mechanical and tribological properties were compared with those of NBR/CB composites. Meanwhile, the effects of graphite dispersion and loading content, as well as the applied load and sliding velocity on the tribological behavior of the above composites under dry friction condition were also evaluated. The worn surfaces were analyzed by scanning electron microscopy (SEM) to disclose wear mechanism. As expected, the better the dispersion of graphite, the more remarkable enhancement on tensile and dynamic mechanical properties, and the greater reduction in the coefficient of friction (COF) and specific wear rate (W s ). It was found that a small amount of EG could effectively decrease COF and W s of NBR/CB composites because of the formation of graphite lubricant films. The COF and W s of NBR/CB/EG composites show a decreasing trend with a rise in applied load and sliding velocity. NBR/CB/EG nanocomposite always shows a stable wearing process with relatively low COF and W s . It is thought that well-dispersed graphite nano-sheets were beneficial to the formation of a fine and durable lubricant film.

  8. KPF{sub 6} dissolved in propylene carbonate as an electrolyte for activated carbon/graphite capacitors

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Hongyu [State Key Laboratory of Electroanalytical Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, 5625 Renmin Street, Changchun 130022 (China); Yoshio, Masaki [Advanced Research Center, Saga University, 1341 Yoga-machi, Saga 840-0047 (Japan)

    2010-02-15

    KPF{sub 6} dissolved in propylene carbonate (PC) has been proposed as an electrolyte for activated carbon (AC)/graphite capacitors. The electrochemical performance of AC/graphite capacitor has been tested in XPF{sub 6}-PC or XBF{sub 4}-PC electrolytes (X stands for alkali or quaternary alkyl ammonium cations). The AC/graphite capacitor using KPF{sub 6}-PC electrolyte shows an excellent cycle-ability compared with other electrolytes containing alkali ions. The big decomposition of the PC solvent at the AC negative electrode is considerably suppressed in the case of KPF{sub 6}-PC, which fact has been correlated with the mild solvation of K{sup +} by PC solvent. The relationship between the ionic radius of cation and the corresponding specific capacitance of AC negative electrode also proves that PC-solvated K{sup +} ions are adsorbed on AC electrode instead of naked K{sup +} ions. (author)

  9. Degradation of Carbon Fiber Reinforced Polymer and Graphite by Laser Heating

    Science.gov (United States)

    2016-08-01

    Education and Training Command In Partial Fulfillment of the Requirements for the Degree of Doctor of Philosophy Nicholas C. Herr, BS, MS Captain...ensuring good thermal contact between the sample and its holder (by using sample powders, pellets, or thin films ). The sample temperature is also...carbon nanotube and carbon-containing thin- film manufacturing [82–84] as well as cleaning graphite surfaces in experimental fusion reactors [83

  10. Chemistry of carbon nanomaterials: Uses of lithium nanotube salts in organic syntheses and functionalization of graphite

    Science.gov (United States)

    Chattopadhyay, Jayanta

    The effective utilization of carbon nanomaterials, such as single-walled carbon nanotubes (SWNTs) and graphite, has been hindered due to difficulties (poor solubility, poly-dispersity) in processing. Therefore, a high degree of sidewall functionalization, either covalent or non-covalent, is often required to overcome these difficulties as the functionalized nanomaterials exhibit better solubility (either in organic solvents or in water), dispersity, manipulation, and processibility. This thesis presents a series of convenient and efficient organic synthetic routes to functionalize carbon nanomaterials. Carbon nanotube salts, prepared by treating SWNTs with lithium in liquid ammonia, react readily with aryl halides to yield aryl-functionalized SWNTs. These arylated SWNTs are soluble in methanol and water upon treatment with oleum. Similarly, SWNTs can be covalently functionalized by different heteroatoms (nitrogen, oxygen, and sulfur). Using the reductive alkylation approach, a synthetic scheme is designed to prepare long chain carboxylic acid functionalized SWNTs [SWNTs-(RCOOH)] that can react with (1) amine-terminated polyethylene glycol (PEG) chains to yield water-soluble biocompatible PEGylated SWNTs that are likely to be useful in a variety of biomedical applications; (2) polyethyleneimine (PEI) to prepare a SWNTs-PEI based adsorbent material that shows a four-fold improvement in the adsorption capacity of carbon dioxide over commonly used materials, making it useful for regenerable carbon dioxide removal in spaceflight; (3) chemically modified SWNTs-(RCOOH) to permit covalent bonding to the nylon matrix, thus allowing the formation of nylon 6,10 and nylon 6,10/SWNTs-(RCOOH) nanocomposites. Furthermore, we find that the lithium salts of carbon nanotubes serve as a source of electrons to induce polymerization of simple alkenes and alkynes onto the surface of carbon nanotubes. In the presence of sulfide/disulfide bonds, SWNT salts can initiate the single electron

  11. Three-dimensional interconnected porous graphitic carbon derived from rice straw for high performance supercapacitors

    Science.gov (United States)

    Jin, Hong; Hu, Jingpeng; Wu, Shichao; Wang, Xiaolan; Zhang, Hui; Xu, Hui; Lian, Kun

    2018-04-01

    Three-dimensional interconnected porous graphitic carbon materials are synthesized via a combination of graphitization and activation process with rice straw as the carbon source. The physicochemical properties of the three-dimensional interconnected porous graphitic carbon materials are characterized by Nitrogen adsorption/desorption, Fourier-transform infrared spectroscopy, X-ray diffraction, Raman spectroscopy, Scanning electron microscopy and Transmission electron microscopy. The results demonstrate that the as-prepared carbon is a high surface area carbon material (a specific surface area of 3333 m2 g-1 with abundant mesoporous and microporous structures). And it exhibits superb performance in symmetric double layer capacitors with a high specific capacitance of 400 F g-1 at a current density of 0.1 A g-1, good rate performance with 312 F g-1 under a current density of 5 A g-1 and favorable cycle stability with 6.4% loss after 10000 cycles at a current density of 5 A g-1 in the aqueous electrolyte of 6M KOH. Thus, rice straw is a promising carbon source for fabricating inexpensive, sustainable and high performance supercapacitors' electrode materials.

  12. "Bricks and mortar" self-assembly approach to graphitic mesoporous carbon nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Fulvio, P. F.; Mayes, R.; Wang, X. Q.; Mahurin, S., M.; Bauer, J. C.; Presser, V.; McDonough, J.; Gogotsi, Y.; Dai, S.

    2011-04-20

    Mesoporous carbon materials do not have sufficient ordering at the atomic scale to exhibit good electronic conductivity. To date, mesoporous carbons having uniform mesopores and high surface areas have been prepared from partially-graphitizable precursors in the presence of templates. High temperature thermal treatments above 2000 °C, which are usually required to increase conductivity, result in a partial or total collapse of the mesoporous structures and reduced surface areas induced by growth of graphitic domains, limiting their applications in electric double layer capacitors and lithium-ion batteries. In this work, we successfully implemented a “brick-and-mortar” approach to obtain ordered graphitic mesoporous carbon nanocomposites with tunable mesopore sizes below 850 °C without using graphitization catalysts or high temperature thermal treatments. Phenolic resin-based mesoporous carbons act as mortar to highly conductive carbon blacks and carbon onions (bricks). The capacitance and resistivity of final materials can be tailored by changing the mortar to brick ratios.

  13. Plasmon mediated enhancement and tuning of optical emission properties of two dimensional graphitic carbon nitride nanosheets.

    Science.gov (United States)

    Bayan, Sayan; Gogurla, Narendar; Midya, Anupam; Singha, Achintya; Ray, Samit K

    2017-12-01

    We demonstrate surface plasmon induced enhancement and tunablilty in optical emission properties of two dimensional graphitic carbon nitride (g-C 3 N 4 ) nanosheets through the attachment of gold (Au) nanoparticles. Raman spectroscopy has revealed surface enhanced Raman scattering that arises due to the combined effect of the charge transfer process and localized surface plasmon induced enhancement in electromagnetic field, both occurring at the nanoparticle-nanosheet interface. Photoluminescence studies suggest that at an optimal concentration of nanoparticles, the emission intensity can be enhanced, which is maximum within the 500-525 nm region. Further, the fabricated electroluminescent devices reveal that the emission feature can be tuned from bluish-green to red (∼160 nm shift) upon attaching Au nanoparticles. We propose that the π*→π transition in g-C 3 N 4 can trigger surface plasmon oscillation in Au, which subsequently increases the excitation process in the nanosheets and results in enhanced emission in the green region of the photoluminescence spectrum. On the other hand, electroluminescence of g-C 3 N 4 can induce plasmon oscillation more efficiently and thus can lead to red emission from Au nanoparticles through the radiative damping of particle plasmons. The influence of nanoparticle size and coverage on the emission properties of two dimensional g-C 3 N 4 , nanosheets has also been studied in detail.

  14. Visible-light-driven dynamic cancer therapy and imaging using graphitic carbon nitride nanoparticles.

    Science.gov (United States)

    Heo, Nam Su; Lee, Sun Uk; Rethinasabapathy, Muruganantham; Lee, Eun Zoo; Cho, Hye-Jin; Oh, Seo Yeong; Choe, Sang Rak; Kim, Yeonho; Hong, Won G; Krishnan, Giribabu; Hong, Won Hi; Jeon, Tae-Joon; Jun, Young-Si; Kim, Hae Jin; Huh, Yun Suk

    2018-09-01

    Organic graphitic carbon nitride nanoparticles (NP-g-CN), less than 30 nm in size, were synthesized and evaluated for photodynamic therapy (PDT) and cell imaging applications. NP-g-CN particles were prepared through an intercalation process using a rod-like melamine-cyanuric acid adduct (MCA) as the molecular precursor and a eutectic mixture of LiCl-KCl (45:55 wt%) as the reaction medium for polycondensation. The nano-dimensional NP-g-CN penetrated the malignant tumor cells with minimal hindrance and effectively generated reactive oxygen species (ROS) under visible light irradiation, which could ablate cancer cells. When excited by visible light irradiation (λ > 420 nm), NP-g-CN introduced to HeLa and cos-7 cells generated a significant amount of ROS and killed the cancerous cells selectively. The cytotoxicity of NP-g-CN was manipulated by altering the light irradiation and the BP-g-CN caused more damage to the cancer cells than normal cells at low concentrations. As a potential non-toxic organic nanomaterial, the synthesized NP-g-CN are biocompatible with less cytotoxicity than toxic inorganic materials. The combined effects of the high efficacy of ROS generation under visible light irradiation, low toxicity, and bio-compatibility highlight the potential of NP-g-CN for PDT and imaging without further modification. Copyright © 2018 Elsevier B.V. All rights reserved.

  15. Near-field thermal radiation between hyperbolic metamaterials: Graphite and carbon nanotubes

    Energy Technology Data Exchange (ETDEWEB)

    Liu, X. L.; Zhang, R. Z.; Zhang, Z. M., E-mail: zhuomin.zhang@me.gatech.edu [G. W. Woodruff School of Mechanical Engineering, Georgia Institute of Technology, Atlanta, Georgia 30332 (United States)

    2013-11-18

    The near-field radiative heat transfer for two hyperbolic metamaterials, namely, graphite and vertically aligned carbon nanotubes (CNTs), is investigated. Graphite is a naturally existing uniaxial medium, while CNT arrays can be modeled as an effective anisotropic medium. Different hyperbolic modes can be separately supported by these materials in certain infrared regions, resulting in a strong enhancement in near-field heat transfer. It is predicted that the heat flux between two CNT arrays can exceed that between SiC plates at any vacuum gap distance and is about 10 times higher with a 10 nm gap.

  16. Friction and wear studies of graphite and a carbon-carbon composite in air and in helium

    International Nuclear Information System (INIS)

    Li, C.C.; Sheehan, J.E.

    1980-10-01

    Sliding friction and wear tests were conducted on a commercial isotropic graphite and a carbon-carbon composite in air, purified helium, and a helium environment containing controlled amounts of impurities simulating the primary coolant chemistry of a high-temperature gas-cooled reactor (HTGR). The friction and wear characteristics of the materials investigated were stable and were found to be very sensitive to the testing temperature. In general, friction and wear decreased with increasing temperature in the range from ambient to 950 0 C. This temperature dependence is concluded to be due to chemisorption of impurities to form lubricating films and oxidation at higher temperatures, which reduce friction and wear. Graphite and carbon-carbon composites are concluded to be favorable candidate materials for high-temperature sliding service in helium-cooled reactors

  17. Carbide Coatings for Nickel Alloys, Graphite and Carbon/Carbon Composites to be used in Fluoride Salt Valves

    Energy Technology Data Exchange (ETDEWEB)

    Nagle, Denis [Johns Hopkins Univ., Baltimore, MD (United States); Zhang, Dajie [Johns Hopkins Univ., Baltimore, MD (United States)

    2015-10-22

    The focus of this research was concerned with developing materials technology that supports the evolution of Generation IV Advanced High Temperature Reactor (AHTR) concepts. Specifically, we investigate refractory carbide coatings for 1) nickel alloys, and 2) commercial carbon-carbon composites (CCCs). Numerous compelling reasons have driven us to focus on carbon and carbide materials. First, unlike metals, the strength and modulus of CCCs increase with rising temperature. Secondly, graphite and carbon composites have been proven effective for resisting highly corrosive fluoride melts such as molten cryolite [Na₃AlF₆] at ~1000°C in aluminum reduction cells. Thirdly, graphite and carbide materials exhibit extraordinary radiation damage tolerance and stability up to 2000°C. Finally, carbides are thermodynamically more stable in liquid fluoride salt than the corresponding metals (i.e. Cr and Zr) found in nickel based alloys.

  18. Noncovalently functionalized graphitic mesoporous carbon as a stable support of Pt nanoparticles for oxygen reduction

    Energy Technology Data Exchange (ETDEWEB)

    Shao, Yuyan; Zhang, Sheng; Kou, Rong; Wang, Chongmin; Viswanathan, Vilayanur; Liu, Jun; Wang, Yong; Lin, Yuehe [Pacific Northwest National Laboratory, Richland, WA 99352 (United States); Wang, Xiqing; Dai, Sheng [Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States)

    2010-04-02

    We report a durable electrocatalyst support, highly graphitized mesoporous carbon (GMPC), for oxygen reduction in polymer electrolyte membrane (PEM) fuel cells. GMPC is prepared through graphitizing the self-assembled soft-template mesoporous carbon (MPC) under high temperature. Heat-treatment at 2800 C greatly improves the degree of graphitization while most of the mesoporous structures and the specific surface area of MPC are retained. GMPC is then noncovalently functionalized with poly(diallyldimethylammonium chloride) (PDDA) and loaded with Pt nanoparticles by reducing Pt precursor (H{sub 2}PtCl{sub 6}) in ethylene glycol. Pt nanoparticles of {proportional_to}3.0 nm in diameter are uniformly dispersed on GMPC. Compared to Pt supported on Vulcan XC-72 carbon black (Pt/XC-72), Pt/GMPC exhibits a higher mass activity towards oxygen reduction reaction (ORR) and the mass activity retention (in percentage) is improved by a factor of {proportional_to}2 after 44 h accelerated degradation test under the potential step (1.4-0.85 V) electrochemical stressing condition which focuses on support corrosion. The enhanced activity and durability of Pt/GMPC are attributed to the graphitic structure of GMPC which is more resistant to corrosion. These findings demonstrate that GMPC is a promising oxygen reduction electrocatalyst support for PEM fuel cells. The approach reported in this work provides a facile, eco-friendly promising strategy for synthesizing stable metal nanoparticles on hydrophobic support materials. (author)

  19. Carbon isotope geothermometry of graphite-bearing marbles from Central Dronning Maud Land, East Antarctica

    International Nuclear Information System (INIS)

    Wand, U.; Muehle, K.

    1988-01-01

    In order to estimate the peak metamorphic temperatures in high-grade regional metamorphic marbles from central Dronning Maud Land (East Antarctica), 13 C/ 12 C isotope ratios have been measured for coexisting carbonate and graphite pairs. The δ 13 C values of carbonates (calcite ± dolomite) and graphite vary from -0.1 to +4.6 permill (PDB) and from -3.3 to +1.7 permill, respectively. The isotopic fractionation between carbonate and graphite ranges from 2.9 to 4.0 permill and is similar to the Δ 13 C (carb-gr) values observed in other East Antarctic and non-Antarctic granulite-facies marbles. The metamorphic temperatures calculated using the equation of VALLEY and O'NEIL (1981) for calcite-graphite pairs are predominantly in the range 700 0 - 800 0 C (x n=5 ± s = 730 0 ± 30 0 C) and agree well with metamorphic temperatures derived from mineral chemical studies in this East Antarctic region. (author)

  20. Recompressed exfoliated graphite articles

    Science.gov (United States)

    Zhamu, Aruna; Shi, Jinjun; Guo, Jiusheng; Jang, Bor Z

    2013-08-06

    This invention provides an electrically conductive, less anisotropic, recompressed exfoliated graphite article comprising a mixture of (a) expanded or exfoliated graphite flakes; and (b) particles of non-expandable graphite or carbon, wherein the non-expandable graphite or carbon particles are in the amount of between about 3% and about 70% by weight based on the total weight of the particles and the expanded graphite flakes combined; wherein the mixture is compressed to form the article having an apparent bulk density of from about 0.1 g/cm.sup.3 to about 2.0 g/cm.sup.3. The article exhibits a thickness-direction conductivity typically greater than 50 S/cm, more typically greater than 100 S/cm, and most typically greater than 200 S/cm. The article, when used in a thin foil or sheet form, can be a useful component in a sheet molding compound plate used as a fuel cell separator or flow field plate. The article may also be used as a current collector for a battery, supercapacitor, or any other electrochemical cell.

  1. Conversion from dose-to-graphite to dose-to-water in an 80 MeV/A carbon ion beam.

    Science.gov (United States)

    Rossomme, S; Palmans, H; Shipley, D; Thomas, R; Lee, N; Romano, F; Cirrone, P; Cuttone, G; Bertrand, D; Vynckier, S

    2013-08-21

    Based on experiments and numerical simulations, a study is carried out pertaining to the conversion of dose-to-graphite to dose-to-water in a carbon ion beam. This conversion is needed to establish graphite calorimeters as primary standards of absorbed dose in these beams. It is governed by the water-to-graphite mass collision stopping power ratio and fluence correction factors, which depend on the particle fluence distributions in each of the two media. The paper focuses on the experimental and numerical determination of this fluence correction factor for an 80 MeV/A carbon ion beam. Measurements have been performed in the nuclear physics laboratory INFN-LNS in Catania (Sicily, Italy). The numerical simulations have been made with a Geant4 Monte Carlo code through the GATE simulation platform. The experimental data are in good agreement with the simulated results for the fluence correction factors and are found to be close to unity. The experimental values increase with depth reaching 1.010 before the Bragg peak region. They have been determined with an uncertainty of 0.25%. Different numerical results are obtained depending on the level of approximation made in calculating the fluence correction factors. When considering carbon ions only, the difference between measured and calculated values is maximal just before the Bragg peak, but its value is less than 1.005. The numerical value is close to unity at the surface and increases to 1.005 near the Bragg peak. When the fluence of all charged particles is considered, the fluence correction factors are lower than unity at the surface and increase with depth up to 1.025 before the Bragg peak. Besides carbon ions, secondary particles created due to nuclear interactions have to be included in the analysis: boron ions ((10)B and (11)B), beryllium ions ((7)Be), alpha particles and protons. At the conclusion of this work, we have the conversion of dose-to-graphite to dose-to-water to apply to the response of a graphite

  2. Self-assembly of graphitic carbon nitride nanosheets–carbon nanotube composite for electrochemical simultaneous determination of catechol and hydroquinone

    International Nuclear Information System (INIS)

    Zhang, Hanqiang; Huang, Yihong; Hu, Shirong; Huang, Qitong; Wei, Chan; Zhang, Wuxiang; Yang, Weize; Dong, Peihui; Hao, Aiyou

    2015-01-01

    Graphical abstract: Schematic diagram of hydrothermal synthesis graphitic carbon nitride nanosheets-carbon nanotube composite and theirs application for electrochemical sensing catechol and hydroquinone. - Highlights: • Self-assembly of graphitic carbon nitride nanosheets-carbon nanotube composite. • CNNS-CNT show more stronger conductivity than CNNS and CNT. • CNNS-CNT has been performed for detection of catechol and hydroquinone. • The probe was applied to detect practical samples with satisfactory results. - Abstract: In this paper, three-dimensional (3D) graphitic carbon nitride nanosheets-carbon nanotube (CNNS-CNT) composite was synthesized via hydrothermal reaction of 2D CNNS and 1D CNT-COOH by π-π stacking and electrostatic interactions. This CNNS-CNT composite was characterized by transmission electron microscope, scanning electron microscope, x-ray diffraction and fourier-transform infrared. In addition, the CNNS-CNT composite displayed excellent conductivity comparing with CNNS and CNT-COOH monomer. This composite was applied for electrochemical simultaneous determination of catechol (CC) and hydroquinone (HQ) with good sensitivity, wide linear range and low detection limit. In addition, this CNNS-CNT composite modified electrode was also applied to detect practical samples with satisfactory results

  3. Laser surface graphitization to control friction of diamond-like carbon coatings

    Science.gov (United States)

    Komlenok, Maxim S.; Kononenko, Vitaly V.; Zavedeev, Evgeny V.; Frolov, Vadim D.; Arutyunyan, Natalia R.; Chouprik, Anastasia A.; Baturin, Andrey S.; Scheibe, Hans-Joachim; Shupegin, Mikhail L.; Pimenov, Sergei M.

    2015-11-01

    To study the role of laser surface graphitization in the friction behavior of laser-patterned diamond-like carbon (DLC) films, we apply the scanning probe microscopy (SPM) in the lateral force mode (LFM) which allows to obtain simultaneously the lateral force and topography images and to determine local friction levels in laser-irradiated and original surface areas. Based on this approach in the paper, we report on (1) laser surface microstructuring of hydrogenated a-C:H and hydrogen-free ta-C films in the regime of surface graphitization using UV laser pulses of 20-ns duration and (2) correlation between the structure and friction properties of the laser-patterned DLC surface on micro/nanoscale using SPM/LFM technique. The SPM/LFM data obtained for the surface relief gratings of graphitized microstructures have evidenced lower friction forces in the laser-graphitized regions. For the hydrogenated DLC films, the reversible frictional behavior of the laser-graphitized micropatterns is found to take place during LFM imaging at different temperatures (20 and 120 °C) in ambient air. It is revealed that the lateral force distribution in the laser-graphitized areas is shifted to higher friction levels (relative to that of the unirradiated surface) at temperature 120 °C and returned back to the lower friction during the sample cooling to 20 °C, thus confirming an influence of adsorbed water layers on the nanofriction properties of laser-graphitized micropatterns on the film surface.

  4. Hierarchical mesoporous/microporous carbon with graphitized frameworks for high-performance lithium-ion batteries

    Directory of Open Access Journals (Sweden)

    Yingying Lv

    2014-11-01

    Full Text Available A hierarchical meso-/micro-porous graphitized carbon with uniform mesopores and ordered micropores, graphitized frameworks, and extra-high surface area of ∼2200 m2/g, was successfully synthesized through a simple one-step chemical vapor deposition process. The commercial mesoporous zeolite Y was utilized as a meso-/ micro-porous template, and the small-molecule methane was employed as a carbon precursor. The as-prepared hierarchical meso-/micro-porous carbons have homogeneously distributed mesopores as a host for electrolyte, which facilitate Li+ ions transport to the large-area micropores, resulting a high reversible lithium ion storage of 1000 mA h/g and a high columbic efficiency of 65% at the first cycle.

  5. Contribution to the study of the reactivity of pre-graphitic carbons

    International Nuclear Information System (INIS)

    Barrillon, Eric

    1963-01-01

    This research thesis relates to studies of the gasification of solid fuels. After having reported the study of raw materials used for the production of graphite, the author reports the study of a mixing of petroleum coke and coal tar pitch. The author focuses of the intermediary stage of graphite elaboration which is used as an anode in the production of aluminium by electrolytic process. Pitch cokes and petroleum cokes are used as raw materials to study the order of reaction of carbon with carbon dioxide. After having shown that the shape of curves giving the gasification rate related to carbon anhydride with respect to wear was a characteristic of a given type of coke, the author reports some measurements of oxi-reactivity in order to check whether the shape of these curves remains the same when changing the reaction gas

  6. Density separation of combustion-derived soot and petrogenic graphitic black carbon: Quantification and isotopic characterization

    International Nuclear Information System (INIS)

    Veilleux, M-H; Gelinas, Y; Dickens, A F; Brandes, J

    2009-01-01

    The black carbon continuum is composed of a series of carbon-rich components derived from combustion or metamorphism and characterized by contrasting environmental behavior and susceptibility to oxidation. In this work, we present a micro-scale density fractionation method that allows isolating the small quantities of soot-like and graphitic material usually found in natural samples. Organic carbon and δ 13 C mass balance calculations were used to quantify the relative contributions of the two fractions to thermally-stable organic matter from a series of aquatic sediments. Varying proportions of soot-like and graphitic material were found in these samples, with large variations in δ 13 C signatures suggesting important differences in their origin and/or dynamics in the environment.

  7. Synthesis of ultrathin nitrogen-doped graphitic carbon nanocages as advanced electrode materials for supercapacitor.

    Science.gov (United States)

    Tan, Yueming; Xu, Chaofa; Chen, Guangxu; Liu, Zhaohui; Ma, Ming; Xie, Qingji; Zheng, Nanfeng; Yao, Shouzhuo

    2013-03-01

    Synthesis of nitrogen-doped carbons with large surface area, high conductivity, and suitable pore size distribution is highly desirable for high-performance supercapacitor applications. Here, we report a novel protocol for template synthesis of ultrathin nitrogen-doped graphitic carbon nanocages (CNCs) derived from polyaniline (PANI) and their excellent capacitive properties. The synthesis of CNCs involves one-pot hydrothermal synthesis of Mn3O4@PANI core-shell nanoparticles, carbonization to produce carbon coated MnO nanoparticles, and then removal of the MnO cores by acidic treatment. The CNCs prepared at an optimum carbonization temperature of 800 °C (CNCs-800) have regular frameworks, moderate graphitization, high specific surface area, good mesoporosity, and appropriate N doping. The CNCs-800 show high specific capacitance (248 F g(-1) at 1.0 A g(-1)), excellent rate capability (88% and 76% capacitance retention at 10 and 100 A g(-1), respectively), and outstanding cycling stability (~95% capacitance retention after 5000 cycles) in 6 M KOH aqueous solution. The CNCs-800 can also exhibit great pseudocapacitance in 0.5 M H2SO4 aqueous solution besides the large electrochemical double-layer capacitance. The excellent capacitance performance coupled with the facile synthesis of ultrathin nitrogen-doped graphitic CNCs indicates their great application potential in supercapacitors.

  8. Chemical Composition of the Graphitic Black Carbon Fraction in Riverine and Marine Sediments at Submicron Scales using Carbon X-ray Spectromicroscopy

    International Nuclear Information System (INIS)

    Haberstroh, P.; Brandes, J.; Gelinas, Y.; Dickens, A.; Wirick, S.; Cody, G.

    2006-01-01

    The chemical composition of the graphitic black carbon (GBC) fraction of marine organic matter was explored in several marine and freshwater sedimentary environments along the west coast of North America and the Pacific Ocean. Analysis by carbon x-ray absorption near edge structure (C-XANES) spectroscopy and scanning transmission x-ray microscopy (STXM) show the GBC-fraction of Stillaguamish River surface sediments to be dominated by more highly-ordered and impure forms of graphite, together forming about 80% of the GBC, with a smaller percent of an aliphatic carbon component. Eel River Margin surface sediments had very little highly-ordered graphite, and were instead dominated by amorphous carbon and to a lesser extent, impure graphite. However, the GBC of surface sediments from the Washington State Slope and the Mexico Margin were composed almost solely of amorphous carbon. Pre-anthropogenic, highly-oxidized deep-sea sediments from the open Equatorial Pacific Ocean contained over half their GBC in different forms of graphite as well as highly-aliphatic carbon, low aromatic/highly-acidic aliphatic carbon, low aromatic/highly aliphatic carbon, and amorphous forms of carbon. Our results clearly show the impact of graphite and amorphous C phases in the BC fraction in modern riverine sediments and nearby marine shelf deposits. The pre-anthropogenic Equatorial Pacific GBC fraction is remarkable in the existence of highly-ordered graphite

  9. Synthesis of diamondlike carbon particles in/on a water substrate by laser irradiation

    International Nuclear Information System (INIS)

    Hidai, Hirofumi; Tokura, Hitoshi

    2005-01-01

    We proposed two-particle synthesis techniques using a liquid as a substrate. First, utilizing liquid instead of solid substrates, particle synthesis is expected on the liquid surface. Particles sink into the liquid before the particles grow into film, because of liquid fluidity. Second, the excitation of a gas dissolved in water was also attempted. An ArF excimer laser beam was focused in a chamber. The 60% volume of the chamber was filled with water, in which methane was dissolved and the remaining space of the chamber was filled with methane gas. As a result, diamondlike carbon particles could be synthesized in water. The particles synthesized from methane in the gas phase were 50-200 nm in diameter, and the particles synthesized from methane dissolved in water were 200-700 nm in diameter, and no structural differences were observed between the particles of two different diameters. Energy-dispersive spectroscopy, Raman spectroscopy analysis, and high-resolution transmission electron microscopy observations revealed that particles contained a diamondlike carbon component and that graphite was attached to them. These particles were harder than graphite particles

  10. Contribution to the study of the reactivity of graphite with respect to carbon dioxide and air

    International Nuclear Information System (INIS)

    Jacquet, M.

    1959-09-01

    The oxidation of nuclear-quality graphite by air and carbon dioxide has been studied at temperatures at which the reaction becomes measurable. These experiments have been carried out on graphites differing in the concentration and nature of their ash, and in their mode of preparation. The reaction velocities measured have been compared in an attempt to correlate these two factors. Ten types of graphite have thus been studied. Since the oxidation reactions are of the type gas-solid, their velocities have also been compared to the BET surface areas of the graphite studied and to the diameter distribution of the pores of this surface. The conclusion is that, even for these low impurity contents, the law relating the reaction velocity to the surface is masked by the impurities which appear to behave as preferential reaction sites. This has been shown by carrying out successive purifications on various types of graphite, which treatment results in an important decrease in the reactivity of all the samples studied. (author) [fr

  11. Hypergravity synthesis of graphitic carbon nanomaterial in glide arc plasma

    NARCIS (Netherlands)

    Šperka, J.; Soucek, P.; van Loon, J.J.W.A.; Dowson, A.; Schwarz, C.; Krause, J.; Butenko, Y.; Kroesen, G.; Kudrle, V.

    2014-01-01

    A nanostructured carbon material was synthesized using a methane/helium glide arc plasma under standard and increased gravity. Material analysis performed on samples collected from an effluent gas filter showed that the deposited material was present in the form of carbon nanoparticles. They

  12. Multi-walled Carbon Nanotubes/Graphite Nanosheets Modified Glassy Carbon Electrode for the Simultaneous Determination of Acetaminophen and Dopamine.

    Science.gov (United States)

    Zhang, Susu; He, Ping; Zhang, Guangli; Lei, Wen; He, Huichao

    2015-01-01

    Graphite nanosheets prepared by thermal expansion and successive sonication were utilized for the construction of a multi-walled carbon nanotubes/graphite nanosheets based amperometric sensing platform to simultaneously determine acetaminophen and dopamine in the presence of ascorbic acid in physiological conditions. The synergistic effect of multi-walled carbon nanotubes and graphite nanosheets catalyzed the electrooxidation of acetaminophen and dopamine, leading to a remarkable potential difference up to 200 mV. The as-prepared modified electrode exhibited linear responses to acetaminophen and dopamine in the concentration ranges of 2.0 × 10(-6) - 2.4 × 10(-4) M (R = 0.999) and 2.0 × 10(-6) - 2.0 × 10(-4) M (R = 0.998), respectively. The detection limits were down to 2.3 × 10(-7) M for acetaminophen and 3.5 × 10(-7) M for dopamine (S/N = 3). Based on the simple preparation and prominent electrochemical properties, the obtained multi-walled carbon nanotubes/graphite nanosheets modified electrode would be a good candidate for the determination of acetaminophen and dopamine without the interference of ascorbic acid.

  13. Electrochemical and anticorrosion behaviors of hybrid functionalized graphite nano-platelets/tripolyphosphate in epoxy-coated carbon steel

    International Nuclear Information System (INIS)

    Mohammadi, Somayeh; Shariatpanahi, Homeira; Taromi, Faramarz Afshar; Neshati, Jaber

    2016-01-01

    Highlights: • FGNP was combined with TPP to obtain a hybrid nano-particle. • TEM image showed uniform distribution of the hybrid nanoparticles in epoxy coating. • FGNP is a substrate for linking of TPP anions by hydrogen bonding. • FGNP as an accelerator, provides rapid iron phosphate passive film formation. • The hybrid nano-particle can provide long-term corrosion protection. - Abstract: Functionalized graphite nano-platelets (FGNP) were combined with tripolyphosphate (TPP) to gain a hybrid nano-particle (FGNP-TPP) with homogenous dispersion in epoxy, resulting in an excellent anti-corrosion coating for carbon steel substrate. Characterization analyses of the hybrid nano-particle were performed by FT-IR, SEM, XRD and TEM. TPP was linked to FGNP nano-particles by hydrogen bondings. Different epoxy coatings formulated with 1 wt.% of FGNP, FGNP-TPP and TPP were evaluated. Electrochemical investigations, salt spray and pull-off tests showed that the hybrid nano-particle can provide long-term corrosion protection compared to FGNP and TPP due to synergistic effect between FGNP as an accelerator and TPP as a corrosion inhibitor to produce a uniform and stable iron-phosphate passive film with high surface coverage.

  14. Electrochemical and anticorrosion behaviors of hybrid functionalized graphite nano-platelets/tripolyphosphate in epoxy-coated carbon steel

    Energy Technology Data Exchange (ETDEWEB)

    Mohammadi, Somayeh, E-mail: somaye.mohammadi32@aut.ac.ir [Department of Chemistry, Amirkabir University of Technology, Tehran (Iran, Islamic Republic of); Shariatpanahi, Homeira [Corrosion Department, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745-4163, Tehran (Iran, Islamic Republic of); Taromi, Faramarz Afshar [Department of Polymer Engineering, Amirkabir University of Technology, Tehran (Iran, Islamic Republic of); Neshati, Jaber [Corrosion Department, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745-4163, Tehran (Iran, Islamic Republic of)

    2016-08-15

    Highlights: • FGNP was combined with TPP to obtain a hybrid nano-particle. • TEM image showed uniform distribution of the hybrid nanoparticles in epoxy coating. • FGNP is a substrate for linking of TPP anions by hydrogen bonding. • FGNP as an accelerator, provides rapid iron phosphate passive film formation. • The hybrid nano-particle can provide long-term corrosion protection. - Abstract: Functionalized graphite nano-platelets (FGNP) were combined with tripolyphosphate (TPP) to gain a hybrid nano-particle (FGNP-TPP) with homogenous dispersion in epoxy, resulting in an excellent anti-corrosion coating for carbon steel substrate. Characterization analyses of the hybrid nano-particle were performed by FT-IR, SEM, XRD and TEM. TPP was linked to FGNP nano-particles by hydrogen bondings. Different epoxy coatings formulated with 1 wt.% of FGNP, FGNP-TPP and TPP were evaluated. Electrochemical investigations, salt spray and pull-off tests showed that the hybrid nano-particle can provide long-term corrosion protection compared to FGNP and TPP due to synergistic effect between FGNP as an accelerator and TPP as a corrosion inhibitor to produce a uniform and stable iron-phosphate passive film with high surface coverage.

  15. Development of a dry-mechanical graphite separation process and elimination of the separated carbon for the reprocessing of spherical HTR fuel elements

    International Nuclear Information System (INIS)

    Kronschnabel, H.

    1982-01-01

    Due to the C-14 distribution the separation of the particle-free outer region of the spherical HTR fuel element with subsequent solidification of the separated carbon makes it possible to reduce by half the remaining C-14 inventory in the inner particle region to be further treated. Separation of the particle-free outer region by a newly developed sphere-peeling milling machine, conditioning the graphite into compacts and in-situ cementation into a salt-mine are the basic elements of this head-end process variation. An annual cavern volume of approx. 2000 m 3 will be needed to ultimately store the graphite of the particle-free outer region, which corresponds to a reprocessing capacity of 50 GWsub(e) installed HTR power. The brush-disintegration of the remaining inner particle region and the resulting peel-brush-preparation are capable of separating 95% of the graphite without any heavy metal losses. With the mentioned reprocessing capacity an annual cavern volume of approx. 16.500 m 3 is required. (orig.) [de

  16. Honeycomb-like graphitic ordered macroporous carbon prepared by pyrolysis of ammonium bicarbonate

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Liancheng [Key Laboratory of Colloid and Interface Chemistry, Shandong University, Jinan, Shandong 250100 (China); Zhang, Junhao, E-mail: jhzhang6@mail.ustc.edu.cn [Key Laboratory of Colloid and Interface Chemistry, Shandong University, Jinan, Shandong 250100 (China); School of Biology and Chemical Engineering, Jiangsu University of Science and Technology, Zhenjiang, Jiangsu 212003 (China); Xu, Liqiang; Qian, Yitai [Key Laboratory of Colloid and Interface Chemistry, Shandong University, Jinan, Shandong 250100 (China)

    2011-10-15

    Graphical abstract: Honeycomb-like graphitic macroporous carbon (HGMC) with big pores centered at 1-3 {mu}m, has been prepared by controlling the reaction temperature and amount of NH{sub 4}HCO{sub 3} at 550 {sup o}C in a sealed reaction system. Possible formation processes of HGMC are discussed on the experimental results. It is believed that the in situ formed MgO microparticles play a template role during the preparation of HGMC. Highlights: {yields} Honeycomb-like graphitic carbon was synthesized at 550 {sup o}C. {yields} The honeycomb-like graphitic carbon is macroposous structures. {yields} The formed MgO microparticles play a template role during the HGMC formation. {yields} The method can be expended to synthesize other porous or hollow carbon material. -- Abstract: Honeycomb-like graphitic macroporous carbon (HGMC) was synthesized by means of pyrolysis of NH{sub 4}HCO{sub 3} using Mg powder as reductant in an autoclave at 550 {sup o}C. The characterization of structure and morphology was carried out by X-ray diffraction (XRD), Raman spectrum, field-emission scanning electron microscopy (FESEM), and (High-resolution) transmission electron microscope [(HR)TEM]. The results of nitrogen adsorption-desorption indicate that the products are macropore materials with the pore size of 1-3 {mu}m, and the Brunauer-Emett-Teller (BET) surface area was 14 m{sup 2}/g. As a typical morphology, the possible growth process of HGMC was also investigated and discussed. The experimental results show that the in situ formed MgO microparticles play a template role during the HGMC formation.

  17. Honeycomb-like graphitic ordered macroporous carbon prepared by pyrolysis of ammonium bicarbonate

    International Nuclear Information System (INIS)

    Wang, Liancheng; Zhang, Junhao; Xu, Liqiang; Qian, Yitai

    2011-01-01

    Graphical abstract: Honeycomb-like graphitic macroporous carbon (HGMC) with big pores centered at 1-3 μm, has been prepared by controlling the reaction temperature and amount of NH 4 HCO 3 at 550 o C in a sealed reaction system. Possible formation processes of HGMC are discussed on the experimental results. It is believed that the in situ formed MgO microparticles play a template role during the preparation of HGMC. Highlights: → Honeycomb-like graphitic carbon was synthesized at 550 o C. → The honeycomb-like graphitic carbon is macroposous structures. → The formed MgO microparticles play a template role during the HGMC formation. → The method can be expended to synthesize other porous or hollow carbon material. -- Abstract: Honeycomb-like graphitic macroporous carbon (HGMC) was synthesized by means of pyrolysis of NH 4 HCO 3 using Mg powder as reductant in an autoclave at 550 o C. The characterization of structure and morphology was carried out by X-ray diffraction (XRD), Raman spectrum, field-emission scanning electron microscopy (FESEM), and (High-resolution) transmission electron microscope [(HR)TEM]. The results of nitrogen adsorption-desorption indicate that the products are macropore materials with the pore size of 1-3 μm, and the Brunauer-Emett-Teller (BET) surface area was 14 m 2 /g. As a typical morphology, the possible growth process of HGMC was also investigated and discussed. The experimental results show that the in situ formed MgO microparticles play a template role during the HGMC formation.

  18. Evaluation of w values for carbon beams in air, using a graphite calorimeter.

    Science.gov (United States)

    Sakama, Makoto; Kanai, Tatsuaki; Fukumura, Akifumi; Abe, Kyoko

    2009-03-07

    Despite recent progress in carbon therapy, accurate values for physical data such as the w value in air or stopping power ratios for ionization chamber dosimetry have not been obtained. The absorbed dose to graphite obtained with the graphite calorimeter was compared with that obtained using the ionization chambers following the IAEA protocol in order to evaluate the w values in air for mono-energetic carbon beams of 135, 290, 400 and 430 MeV/n. Two cylindrical chambers (PTW type 30001 and PTW type 30011, Farmer) and two plane-parallel chambers (PTW type 23343, Markus and PTW type 34001, Roos) calibrated by the absorbed dose to graphite and exposure to the (60)Co photon beam were used. The comparisons to our calorimeter measurements revealed that, using the ionization chambers, the absorbed dose to graphite comes out low by 2-6% in this experimental energy range and with these chamber types and calibration methods. In the therapeutic energy range, the w values in air for carbon beams indicated a slight energy dependence; we, however, assumed these values to be constant for practical use because of the large uncertainty and unknown perturbation factors of the ionization chambers. The w values in air of the carbon beams were evaluated to be 35.72 J C(-1) +/- 1.5% in the energy range used in this study. This value is 3.5% larger than that recommended by the IAEA TRS 398 for heavy-ion beams. Using this evaluated result, the absorbed dose to water in the carbon beams would be increased by the same amount.

  19. Graphitic carbon nitride nanosheets doped graphene oxide for electrochemical simultaneous determination of ascorbic acid, dopamine and uric acid

    International Nuclear Information System (INIS)

    Zhang, Hanqiang; Huang, Qitong; Huang, Yihong; Li, Feiming; Zhang, Wuxiang; Wei, Chan; Chen, Jianhua; Dai, Pingwang; Huang, Lizhang; Huang, Zhouyi; Kang, Lianping; Hu, Shirong; Hao, Aiyou

    2014-01-01

    Graphical abstract: Schematic drawing of electrochemical oxidize AA, DA and UA on graphitic carbon nitride nanosheets-graphene oxide composite modified electrode. - Highlights: • Synthesize g-C 3 N 4 , GO and CNNS-GO composite. • CNNS-GO composite was the first time for simultaneous determination of AA, DA and UA. • CNNS-GO/GCE displays fantastic selectivity and sensitivity for AA, DA and UA. • CNNS-GO/GCE was applied to detect real sample with satisfactory results. - Abstract: Graphitic carbon nitride nanosheets with a graphite-like structure have strong covalent bonds between carbon and nitride atoms, and nitrogen atoms in the carbon architecture can accelerate the electron transfer and enhance electrical properties effectually. The graphitic carbon nitride nanosheets-graphene oxide composite was synthesized. And the electrochemical performance of the composite was investigated by cyclic voltammetry and differential pulse voltammetry ulteriorly. Due to the synergistic effects of layer-by-layer structures by π-π stacking or charge-transfer interactions, graphitic carbon nitride nanosheets-graphene oxide composite can improved conductivity, electro-catalytic and selective oxidation performance. The proposed graphitic carbon nitride nanosheets-graphene oxide composite modified electrode was employed for simultaneous determination of ascorbic acid, dopamine and uric acid in their mixture solution, it exhibited distinguished sensitivity, wide linear range and low detection limit. Moreover, the modified electrode was applied to detect urine and dopamine injection sample, and then the samples were spiked with certain concentration of three substances with satisfactory recovery results

  20. Graphitic Carbon Materials Tailored for the Rapid Adsorption of Biomolecules

    Science.gov (United States)

    Pescatore, Nicholas A.

    Sepsis is an overactive inflammatory response to an infection, with 19 million cases estimated worldwide and causing organ dysfunction if left untreated. Three pro-inflammatory cytokines are seen from literature review as vital biomarkers for sepsis and are interleukin-6 (IL-6), interleukin-8 (IL-8) and tumor necrosis factor-alpha (TNF-alpha), which have the potential to be removed by hemoperfusion. This thesis examines carbon nanomaterials for their adsorption capabilities in the search for an optimal material for blood cleansing hemoperfusion application, such as mediating the effects of sepsis. Non-porous and porous carbon polymorphs and their properties are investigated in this thesis for their protein adsorption capabilities. Polymer-derived mesoporous carbons were compared to non-porous graphene nanoplatelets (GNP's) to observe changes in adsorption capacity for cytokines between porous and non-porous materials. GNP's were functionalized via high temperature vacuum annealing, air oxidation, acid oxidation and amination treatments to understand the effect of surface chemistry on adsorption. For practical use in a hemoperfusion column, polymer-derived carbon beads and composite materials such as cryogel and PTFE-GNP composites were designed and tested for their adsorption capacity. At concentrations of IL-6, IL-8, and TNF-alpha seen in septic patients, these cytokines were completely removed from the blood after 5 minutes of incubation with GNP's. Overall, a low-cost, scalable carbon adsorbent was found to provide a novel approach of rapidly removing pro-inflammatory cytokines from septic patients.

  1. Creating high yield water soluble luminescent graphene quantum dots via exfoliating and disintegrating carbon nanotubes and graphite flakes.

    Science.gov (United States)

    Lin, Liangxu; Zhang, Shaowei

    2012-10-21

    We have developed an effective method to exfoliate and disintegrate multi-walled carbon nanotubes and graphite flakes. With this technique, high yield production of luminescent graphene quantum dots with high quantum yield and low oxidization can be achieved.

  2. Silver Nanoparticles and Graphitic Carbon Through Thermal Decomposition of a Silver/Acetylenedicarboxylic Salt

    Directory of Open Access Journals (Sweden)

    Komninou Philomela

    2009-01-01

    Full Text Available Abstract Spherically shaped silver nanoparticles embedded in a carbon matrix were synthesized by thermal decomposition of a Ag(I/acetylenedicarboxylic acid salt. The silver nanoparticles, which are formed either by pyrolysis at 300 °C in an autoclave or thermolysis in xylene suspension at reflux temperature, are acting catalytically for the formation of graphite layers. Both reactions proceed through in situ reduction of the silver cations and polymerization of the central acetylene triple bonds and the exact temperature of the reaction can be monitored through DTA analysis. Interestingly, the thermal decomposition of this silver salt in xylene partly leads to a minor fraction of quasicrystalline silver, as established by HR-TEM analysis. The graphitic layers covering the silver nanoparticles are clearly seen in HR-TEM images and, furthermore, established by the presence of sp2carbon at the Raman spectrum of both samples.

  3. Preparation and evaluation of coal extracts as precursors for carbon and graphite products

    Energy Technology Data Exchange (ETDEWEB)

    Zondlo, J.W.; Stiller, A.W.; Stansberry, P.G. [West Virginia Univ., Morgantown, WV (United States)] [and others

    1996-08-01

    A coal extraction process coupled with coal hydrotreatment has been shown capable of producing suitable precursors for a variety of commercially important carbon and graphite products. The N-methylpyrolidone (NMP) extracts of hydrotreated coals have been analytically and chemically characterized and shown to have properties acceptable for use as binder and impregnation pitch. Mesophase formation studies have demonstrated their capability for producing both needle and anode grade coke as well as precursors for mesophase pitch fibers. A graphite artifact has been produced using a coal extract as a binder and coke derived from the extract as a filler. Further evaluation of the extract materials is being carried out by industrial members of the Carbon Products Consortium.

  4. A fluorescent sensor for selective detection of cyanide using mesoporous graphitic carbon(IV) nitride.

    Science.gov (United States)

    Lee, Eun Zoo; Lee, Sun Uk; Heo, Nam-Su; Stucky, Galen D; Jun, Young-Si; Hong, Won Hi

    2012-04-25

    A turn-on fluorescence sensor, Cu(2+)-c-mpg-C(3)N(4), was developed for detection of CN(-) in aqueous solution by simply mixing cubic mesoporous graphitic carbon nitride (c-mpg-C(3)N(4)) and aqueous solution of Cu(NO(3))(2). The highly sensitive detection of CN(-) with a detection limit of 80 nM is not only possible in aqueous solution but also in human blood serum.

  5. Synthesis and photocatalytic properties of graphitic carbon nitride nanofibers using porous anodic alumina templates

    Science.gov (United States)

    Suchitra, S. M.; Udayashankar, N. K.

    2017-12-01

    In the present study, we describe an effective method for the synthesis of Graphitic carbon nitride (GCN) nanostructures using porous anodic alumina (AAO) membrane as template by simple thermal condensation of cyanamide. Synthesized nanostructure was fully analysed by various techniques to detect its crystalline nature, morphology, luminescent properties followed by the evaluation of its photocatalytic activity in the degradation of Methylene blue dye. Structural analysis of synthesized GCNNF was systematically carried out using x-ray powder diffraction (XRD) and scanning electron microscope (SEM), and. The results confirmed the growth of GCN inside the nanochannels of anodic alumina templates. Luminescent properties of GCNNF were studied using photoluminescence (PL) spectroscopy. PL analysis showed the presence of a strong emission peak in the wavelength range of 350-600 nm in blue region. GCNNF displays higher photocatalytic performance in the photodegradation of methylene blue compare to the bulk GCN. Highlights 1. In the present paper, we report the synthesis of graphitic carbon nitride nanofibers (GCNNF) using porous anodic aluminium oxide membranes as templates through thermal condensation of cyanamide at 500 °C. 2. The synthesis of Graphitic carbon nitride nanofibers using porous andic alumina template is the efficient approach for increasing crystallinity and surface area. 3. The high surface area of graphitic carbon nitride nanofibers has a good impact on novel optical and photocatalytic properties of the bulkGCN. 4. AAO templating of GCN is one of the versatile method to produce tailorable GCN nanostructures with higher surface area and less number of structural defects. 5. Towards photocatalytic degradation of dyes, the tuning of physical properties is very essential thing hence we are succeeded in achieving better catalytic performance of GCN nanostructures by making use of AAO templates.

  6. Activation of peroxymonosulfate by graphitic carbon nitride loaded on activated carbon for organic pollutants degradation

    International Nuclear Information System (INIS)

    Wei, Mingyu; Gao, Long; Li, Jun; Fang, Jia; Cai, Wenxuan; Li, Xiaoxia; Xu, Aihua

    2016-01-01

    Highlights: • Supported g-C_3N_4 on AC catalysts with different loadings were prepared. • The metal free catalysts exhibited high efficiency for dyes degradation with PMS. • The catalyst presented a long-term stability for multiple runs. • The C=O groups played a key role in the oxidation process. - Abstract: Graphitic carbon nitride supported on activated carbon (g-C_3N_4/AC) was prepared through an in situ thermal approach and used as a metal free catalyst for pollutants degradation in the presence of peroxymonosulfate (PMS) without light irradiation. It was found that g-C_3N_4 was highly dispersed on the surface of AC with the increase of surface area and the exposition of more edges and defects. The much easier oxidation of C species in g-C_3N_4 to C=O was also observed from XPS spectra. Acid Orange 7 (AO7) and other organic pollutants could be completely degraded by the g-C_3N_4/AC catalyst within 20 min with PMS, while g-C_3N_4+PMS and AC+PMS showed no significant activity for the reaction. The performance of the catalyst was significantly influenced by the amount of g-C_3N_4 loaded on AC; but was nearly not affected by the initial solution pH and reaction temperature. In addition, the catalysts presented good stability. A nonradical mechanism accompanied by radical generation (HO· and SO_4·"−) in AO7 oxidation was proposed in the system. The C=O groups play a key role in the process; while the exposure of more N-(C)_3 group can further increase its electron density and basicity. This study can contribute to the development of green materials for sustainable remediation of aqueous organic pollutants.

  7. Porous graphitic materials obtained from carbonization of organic ...

    Indian Academy of Sciences (India)

    features such as pore diameter, hierarchical porous archi- tectures, surface ... bon xerogels seem to be promising candidates for liquid ... co-solvent to increase the solubility of furfural, whilst the .... 100 nm, thus Vt means the total volume of pores below c.a. ..... Wang Z, Zhang X, Liu X, Lv M, Yang K and Meng J 2011 Carbon.

  8. Graphite crystals grown within electromagnetically levitated metallic droplets

    International Nuclear Information System (INIS)

    Amini, Shaahin; Kalaantari, Haamun; Mojgani, Sasan; Abbaschian, Reza

    2012-01-01

    Various graphite morphologies were observed to grow within the electromagnetically levitated nickel–carbon melts, including primary flakes and spheres, curved surface graphite and eutectic flakes, as well as engulfed and entrapped particles. As the supersaturated metallic solutions were cooled within the electromagnetic (EM) levitation coil, the primary graphite flakes and spheres formed and accumulated near the periphery of the droplet due to EM circulation. The primary graphite islands, moreover, nucleated and grew on the droplet surface which eventually formed a macroscopic curved graphite crystal covering the entire liquid. Upon further cooling, the liquid surrounding the primary graphite went under a coupled eutectic reaction while the liquid in the center formed a divorced eutectic due to EM mixing. This brought about the formation of graphite fine flakes and agglomerated particles close to the surface and in the center of the droplet, respectively. The graphite morphologies, growth mechanisms, defects, irregularities and growth instabilities were interpreted with detailed optical and scanning electron microscopies.

  9. Charge Modulation in Graphitic Carbon Nitride as a Switchable Approach to High-Capacity Hydrogen Storage.

    Science.gov (United States)

    Tan, Xin; Kou, Liangzhi; Tahini, Hassan A; Smith, Sean C

    2015-11-01

    Electrical charging of graphitic carbon nitride nanosheets (g-C4 N3 and g-C3 N4 ) is proposed as a strategy for high-capacity and electrocatalytically switchable hydrogen storage. Using first-principle calculations, we found that the adsorption energy of H2 molecules on graphitic carbon nitride nanosheets is dramatically enhanced by injecting extra electrons into the adsorbent. At full hydrogen coverage, the negatively charged graphitic carbon nitride achieves storage capacities up to 6-7 wt %. In contrast to other hydrogen storage approaches, the storage/release occurs spontaneously once extra electrons are introduced or removed, and these processes can be simply controlled by switching on/off the charging voltage. Therefore, this approach promises both facile reversibility and tunable kinetics without the need of specific catalysts. Importantly, g-C4 N3 has good electrical conductivity and high electron mobility, which can be a very good candidate for electron injection/release. These predictions may prove to be instrumental in searching for a new class of high-capacity hydrogen storage materials. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  10. Irradiation-induced defects in graphite and glassy carbon studied by positron annihilation

    International Nuclear Information System (INIS)

    Hasegawa, M.; Kajino, M.; Kuwahara, H.; Yamaguchi, S.; Kuramoto, E.; Takenaka, M.

    1992-01-01

    ACAR and positron lifetime measurements have been made on, HOPG, isotropic fine-grained graphites, glassy carbons and C 60 /C 70 . HOPG showed a marked bimodal ACAR distribution along the c-axis. By irradiation of 1.0 X 10 19 fast neutrons/cm 2 remarkable narrowing in the ACAR curves and disappearance of the bimodal distribution were observed. Lifetime in HOPG increased from 225 psec to 289 psec (positron-lifetime in vacancies and their small clusters) by the irradiation. The irradiation on isotropic graphites and glassy carbons, however, gave slight narrowing in ACAR curves and decrease in lifetimes (360 psec → 300psec). This suggests irradiation-induced vacancy trapping in crystallites. In C 60 /C 70 powder two lifetime components were detected: τ 1 =177psec, τ 2 =403psec (I 2 =58%). The former is less than the bulk lifetime of HOPG, while the latter being very close to lifetimes in the isotropic graphites and glassy carbons. This and recent 2D-ACAR study of HOPG surface [15] strongly suggest free and defect surface states around ''soccer ball'' cages

  11. A high-performance carbon nanoparticle-decorated graphite felt electrode for vanadium redox flow batteries

    International Nuclear Information System (INIS)

    Wei, L.; Zhao, T.S.; Zhao, G.; An, L.; Zeng, L.

    2016-01-01

    Highlights: • Propose a carbon nanoparticle-decorated graphite felt electrode for VRFBs. • The energy efficiency is up to 84.8% at 100 mA cm"−"2. • The new electrode allows the peak power density to reach 508 mW cm"−"2. - Abstract: Increasing the performance of vanadium redox flow batteries (VRFBs), especially the energy efficiency and power density, is critically important to reduce the system cost to a level for widespread commercialization. Unlike conventional VRFBs with flow-through structure, in this work we create a VRFB featuring a flow-field structure with a carbon nanoparticle-decorated graphite felt electrode for the battery. This novel structure, exhibiting a significantly reduced ohmic loss through reducing electrode thickness, an increased surface area and improved electrocatalytic activity by coating carbon nanoparticles, allows the energy efficiency up to 84.8% at a current density of as high as 100 mA cm"−"2 and the peak power density to reach a value of 508 mW cm"−"2. In addition, it is demonstrated that the battery with this proposed structure exhibits a substantially improved rate capability and capacity retention as opposed to conventional flow-through structured battery with thick graphite felt electrodes.

  12. Graphitic carbon nitride/graphene oxide/reduced graphene oxide nanocomposites for photoluminescence and photocatalysis

    Energy Technology Data Exchange (ETDEWEB)

    Aleksandrzak, Malgorzata, E-mail: malgorzata.aleksandrzak@o2.pl; Kukulka, Wojciech; Mijowska, Ewa

    2017-03-15

    Highlights: • Graphitic carbon nitride modified with graphene nanostructures. • Influence of graphene nanostructures size in photocatalytic properties of g-C{sub 3}N{sub 4}. • Improved photocatalysis resulted from up-converted photoluminescence. - Abstract: The study presents a modification of graphitic carbon nitride (g-C{sub 3}N{sub 4}) with graphene oxide (GO) and reduced graphene oxide (rGO) and investigation of photoluminescent and photocatalytic properties. The influence of GO and rGO lateral sizes used for the modification was investigated. The nanomaterials were characterized with atomic force microscopy (AFM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), diffuse reflectance UV–vis spectroscopy (DR-UV-vis) and photoluminescence spectroscopy (PL). PL revealed that pristine graphitic carbon nitride and its nanocomposites with GO and rGO emitted up-converted photoluminescence (UCPL) which could contribute to the improvement of photocatalytic activity of the materials. The photoactivity was evaluated in a process of phenol decomposition under visible light. A hybrid composed of rGO nanoparticles (rGONPs, 4–135 nm) exhibited the highest photoactivity compared to rGO with size of 150 nm–7.2 μm and graphene oxide with the corresponding sizes. The possible reason of the superior photocatalytic activity is the most enhanced UCPL of rGONPs, contributing to the emission of light with higher energy than the incident light, resulting in improved photogeneration of electron-hole pairs.

  13. Carbon Raman Spectroscopy of 36 Inter-Planetary Dust Particles

    Science.gov (United States)

    Busemann, H.; Nittler, L. R.; Davidson, J.; Franchi, I. A.; Messenger, S.; Nakamura-Messenger, K.; Palma, R. L.; Pepin, R. O.

    2009-01-01

    Carbon Raman spectroscopy is a useful tool to determine the degree of order of organic material (OM) in extra-terrestrial matter. As shown for meteoritic OM [e.g., 2], peak parameters of D and G bands are a measure of thermal alteration, causing graphitization (order), and amorphization, e.g. during protoplanetary irradiation, causing disorder. Th e most pristine interplanetary dust particles (IDPs) may come from comets. However, their exact provenance is unknown. IDP collection during Earth?s passage through comet Grigg-Skjellerup?s dust stream ("GSC" collectors) may increase the probability of collecting fresh IDPs from a known, cometary source. We used Raman spectroscopy to compare 21 GSC-IDPs with 15 IDPs collected at different periods, and found that the variation among GSC-IDPs is larger than among non-GSC IDPs, with the most primitive IDPs being mostly GSC-IDPs.

  14. Proceedings of the conference on electrochemistry of carbon allotropes: Graphite, fullerenes and diamond

    Energy Technology Data Exchange (ETDEWEB)

    Kinoshita, K. [ed.] [Lawrence Berkeley National Lab., CA (United States); Scherson, D. [ed.] [Case Western Reserve Univ., Cleveland, OH (United States)

    1998-02-01

    This conference provided an opportunity for electrochemists, physicists, materials scientists and engineers to meet and exchange information on different carbon allotropes. The presentations and discussion among the participants provided a forum to develop recommendations on research and development which are relevant to the electrochemistry of carbon allotropes. The following topics which are relevant to the electrochemistry of carbon allotropes were addressed: Graphitized and disordered carbons, as Li-ion intercalation anodes for high-energy-density, high-power-density Li-based secondary batteries; Carbons as substrate materials for catalysis and electrocatalysis; Boron-doped diamond film electrodes; and Electrochemical characterization and electrosynthesis of fullerenes and fullerene-type materials. Abstracts of the presentations are presented.

  15. Highly sensitive piezo-resistive graphite nanoplatelet-carbon nanotube hybrids/polydimethylsilicone composites with improved conductive network construction.

    Science.gov (United States)

    Zhao, Hang; Bai, Jinbo

    2015-05-13

    The constructions of internal conductive network are dependent on microstructures of conductive fillers, determining various electrical performances of composites. Here, we present the advanced graphite nanoplatelet-carbon nanotube hybrids/polydimethylsilicone (GCHs/PDMS) composites with high piezo-resistive performance. GCH particles were synthesized by the catalyst chemical vapor deposition approach. The synthesized GCHs can be well dispersed in the matrix through the mechanical blending process. Due to the exfoliated GNP and aligned CNTs coupling structure, the flexible composite shows an ultralow percolation threshold (0.64 vol %) and high piezo-resistive sensitivity (gauge factor ∼ 10(3) and pressure sensitivity ∼ 0.6 kPa(-1)). Slight motions of finger can be detected and distinguished accurately using the composite film as a typical wearable sensor. These results indicate that designing the internal conductive network could be a reasonable strategy to improve the piezo-resistive performance of composites.

  16. Mass-producible method for preparation of a carbon-coated graphite@plasma nano-silicon@carbon composite with enhanced performance as lithium ion battery anode

    International Nuclear Information System (INIS)

    Chen, Hedong; Wang, Zhoulu; Hou, Xianhua; Fu, Lijun; Wang, Shaofeng; Hu, Xiaoqiao; Qin, Haiqing; Wu, Yuping

    2017-01-01

    Carbon-coated core-shell structure artificial graphite@plasma nano-silicon@carbon (AG@PNSi@C) composite, applying as lithium ion battery anode material, has been prepared via spray drying method. The plasma nano-silicon (<100 nm), which contained amorphous silicon, was synthesized by radio frequency induction plasma system with the high temperatures processing capability and high quench rates. The artificial graphite in the composite acts as the core which supports the particle and provides electroconductivity, while PNSi attached on the surface of the core, enhances the specific capacity of the composite. The as prepared composite shows superior performance as anode in lithium-ion batteries, regarding to the initial Coulombic efficiency and cycle life. The initial Coulombic efficiency of AG@PNSi@C electrode is 81.0% with a discharge capacity of 553 mAh g −1 and a recharge capacity of 448 mAh g −1 . During cycling, AG@PNSi@C exhibits excellent performance with a very low capacity fading that the discharge capacity maintains 498.2 mAh g −1 and 449.4 mAh g −1 after 250 cycles and 500 cycles. AG@PNSi@C also shows enhanced resistance against high current density. Besides the remarkable electrochemical performances, the facile and mass-producible synthesis process makes the AG@PNSi@C composite very promising for its application in lithium-ion batteries.

  17. Image Analysis of a Negatively Curved Graphitic Sheet Model for Amorphous Carbon

    Science.gov (United States)

    Bursill, L. A.; Bourgeois, Laure N.

    High-resolution electron micrographs are presented which show essentially curved single sheets of graphitic carbon. Image calculations are then presented for the random surface schwarzite-related model of Townsend et al. (Phys. Rev. Lett. 69, 921-924, 1992). Comparison with experimental images does not rule out the contention that such models, containing surfaces of negative curvature, may be useful for predicting some physical properties of specific forms of nanoporous carbon. Some difficulties of the model predictions, when compared with the experimental images, are pointed out. The range of application of this model, as well as competing models, is discussed briefly.

  18. Structures, origin and evolution of various carbon phases in the ureilite Northwest Africa 4742 compared with laboratory-shocked graphite

    Science.gov (United States)

    Le Guillou, C.; Rouzaud, J. N.; Remusat, L.; Jambon, A.; Bourot-Denise, M.

    2010-07-01

    Mineralogical structures of carbon phases within the ureilite North West Africa 4742, a recent find, are investigated at various scales by high-resolution transmission electron microscopy (HRTEM), Raman microspectrometry and X-ray diffraction. Ureilites are the most carbon-rich of all meteorites, containing up to 6 wt.% carbon. Diamond, graphite and so-called "amorphous carbon" are typically described, but their crystallographic relationships and respective thermal histories remain poorly constrained. We especially focus on the origin of "amorphous carbon" and graphite, as well as their relationship with diamond. Two aliquots of carbon-bearing material were extracted: the insoluble organic matter (IOM) and the diamond fraction. We also compare the observed structures with those of laboratory-shocked graphite. Polycrystalline diamond aggregates with mean coherent domains of about 40 nm are reported for the first time in a ureilite and TEM demonstrates that all carbon phases are crystallographically related at the nanometre scale. Shock features show that diamond is produced from graphite through a martensitic transition. This observation demonstrates that graphite was present when the shock occurred and is consequently a precursor of diamond. The structure of what is commonly described as the "amorphous carbon" has been identified. It is not completely amorphous but only disordered and consists of nanometre-sized polyaromatic units surrounding the diamond. Comparison with laboratory-shocked graphite, partially transformed into diamond, indicates that the disordered carbon could be the product of diamond post-shock annealing. As diamond is the carrier of noble gases, whereas graphite is noble gas free, graphite cannot be the sole diamond precursor. This implies a multiple-stage history. A first generation of diamond could have been synthesized from a noble gas rich precursor or environment by either a shock or a condensation process. Thermally-induced graphitization

  19. Pore-Width-Dependent Preferential Interaction of sp2 Carbon Atoms in Cyclohexene with Graphitic Slit Pores by GCMC Simulation

    Directory of Open Access Journals (Sweden)

    Natsuko Kojima

    2011-01-01

    Full Text Available The adsorption of cyclohexene with two sp2 and four sp3 carbon atoms in graphitic slit pores was studied by performing grand canonical Monte Carlo simulation. The molecular arrangement of the cyclohexene on the graphitic carbon wall depends on the pore width. The distribution peak of the sp2 carbon is closer to the pore wall than that of the sp3 carbon except for the pore width of 0.7 nm, even though the Lennard-Jones size of the sp2 carbon is larger than that of the sp3 carbon. Thus, the difference in the interactions of the sp2 and sp3 carbon atoms of cyclohexene with the carbon pore walls is clearly observed in this study. The preferential interaction of sp2 carbon gives rise to a slight tilting of the cyclohexene molecule against the graphitic wall. This is suggestive of a π-π interaction between the sp2 carbon in the cyclohexene molecule and graphitic carbon.

  20. Floatability study of graphite ore from southeast Sulawesi (Indonesia)

    Science.gov (United States)

    Florena, Fenfen Fenda; Syarifuddin, Fahmi; Hanam, Eko Sulistio; Trisko, Nici; Kustiyanto, Eko; Enilisiana, Rianto, Anton; Arinton, Ghenadi

    2016-02-01

    Graphite ore obtained from Kolaka Regency, South East Sulawesi, Indonesia have been succesfully investigated for beneficiation by froth flotation technique. Preliminary study have been done to determine the minerals types, fixed carbon content and liberation size of the graphite. Graphite is naturally floatable due to its hydrophobic property. Some suitable reagents are usually added to increase effectiveness of recovery. In this article, enrichment of graphite by froth flotation was studied by investigating the effect of reagents concentrations, rotation speed and particle size on the carbon grade and recovery of the concentrate. The carbon grade increased from 3.00% to 60.00% at the optimum flotation conditions.

  1. Graphitic Carbon Nitride as a Catalyst Support in Fuel Cells and Electrolyzers

    International Nuclear Information System (INIS)

    Mansor, Noramalina; Miller, Thomas S.; Dedigama, Ishanka; Jorge, Ana Belen; Jia, Jingjing; Brázdová, Veronika; Mattevi, Cecilia; Gibbs, Chris; Hodgson, David; Shearing, Paul R.; Howard, Christopher A.; Corà, Furio; Shaffer, Milo; Brett, Daniel J.L.

    2016-01-01

    Highlights: • Graphitic carbon nitride (gCN) describes many materials with different structures. • gCNs can exhibit excellent mechanical, chemical and thermal resistance. • A major obstacle for pure gCN catalyst supports is limited electronic conductivity. • Composite/Hybrid gCN structures show excellent performance as catalyst supports. • gCNs have great potential for use in fuel calls and water electrolyzers. - Abstract: Electrochemical power sources, such as polymer electrolyte membrane fuel cells (PEMFCs), require the use of precious metal catalysts which are deposited as nanoparticles onto supports in order to minimize their mass loading and therefore cost. State-of-the-art/commercial supports are based on forms of carbon black. However, carbon supports present disadvantages including corrosion in the operating fuel cell environment and loss of catalyst activity. Here we review recent work examining the potential of different varieties of graphitic carbon nitride (gCN) as catalyst supports, highlighting their likely benefits, as well as the challenges associated with their implementation. The performance of gCN and hybrid gCN-carbon materials as PEMFC electrodes is discussed, as well as their potential for use in alkaline systems and water electrolyzers. We illustrate the discussion with examples taken from our own recent studies.

  2. Aligned carbon nanotube, graphene and graphite oxide thin films via substrate-directed rapid interfacial deposition

    Science.gov (United States)

    D'Arcy, Julio M.; Tran, Henry D.; Stieg, Adam Z.; Gimzewski, James K.; Kaner, Richard B.

    2012-05-01

    A procedure for depositing thin films of carbon nanostructures is described that overcomes the limitations typically associated with solution based methods. Transparent and conductively continuous carbon coatings can be grown on virtually any type of substrate within seconds. Interfacial surface tension gradients result in directional fluid flow and film spreading at the water/oil interface. Transparent films of carbon nanostructures are produced including aligned ropes of single-walled carbon nanotubes and assemblies of single sheets of chemically converted graphene and graphite oxide. Process scale-up, layer-by-layer deposition, and a simple method for coating non-activated hydrophobic surfaces are demonstrated.A procedure for depositing thin films of carbon nanostructures is described that overcomes the limitations typically associated with solution based methods. Transparent and conductively continuous carbon coatings can be grown on virtually any type of substrate within seconds. Interfacial surface tension gradients result in directional fluid flow and film spreading at the water/oil interface. Transparent films of carbon nanostructures are produced including aligned ropes of single-walled carbon nanotubes and assemblies of single sheets of chemically converted graphene and graphite oxide. Process scale-up, layer-by-layer deposition, and a simple method for coating non-activated hydrophobic surfaces are demonstrated. Electronic supplementary information (ESI) available: Droplet coalescence, catenoid formation, mechanism of film growth, scanning electron micrographs showing carbon nanotube alignment, flexible transparent films of SWCNTs, AFM images of a chemically converted graphene film, and SEM images of SWCNT free-standing thin films. See DOI: 10.1039/c2nr00010e

  3. Effect of carbon black on electrical and rheological properties of graphite nanoplatelets/poly(ethylene-butyl acrylate composites

    Directory of Open Access Journals (Sweden)

    H. Oxfall

    2015-01-01

    Full Text Available The effect of adding carbon black on the electrical and rheological properties of graphite nanoplatelets/poly(ethylene-butyl acrylate copolymer composites produced via melt or solution mixing was studied. By adding a small amount of low- or high-structured carbon black to the nanocomposite, the electrical percolation threshold decreased and the final conductivity (at higher filler contents increased. The effect on the percolation threshold was significantly stronger in case of the high-structured carbon black where replacing 10 wt% of the total filler content with carbon black instead of graphite nanoplatelets reduced the electrical percolation threshold from 6.9 to 4.6 vol%. Finally, the solution mixing process was found to be more efficient leading to a lower percolation threshold. For the composites containing high-structured carbon black, graphite nanoplatelets and their hybrids there was a quite reasonable correlation between the electrical and rheological percolation thresholds.

  4. Graphite nanoplatelets and carbon nanotubes based polyethylene composites: Electrical conductivity and morphology

    International Nuclear Information System (INIS)

    Haznedar, Galip; Cravanzola, Sara; Zanetti, Marco; Scarano, Domenica; Zecchina, Adriano; Cesano, Federico

    2013-01-01

    Graphite nanoplatelets (GNPs) and/or multiwalled-carbon nanotubes (MWCNTs)/low density polyethylene (LDPE) composites have been obtained either via melt-mixing or solvent assisted methods. Electrical properties of samples obtained through the above mentioned methods are compared and the conductance values as function of filler fraction are discussed. The corresponding percolation thresholds are evaluated. Conductivity maps images are acquired under low-potentials scanning electron microscopy (0.3 KV) and the relationship between the obtained conductivity images and electric properties is highlighted. The synergistic role of CNTs (1D) and GNPs (2D) in improving the conductive properties of the polymer composites has been shown. - Highlights: • Graphite nanoplatelets (GNPs) and GNPs/MWCNT LDPE composites. • Low potential SEM conductivity maps. • Conducting paths between 1D and 2D C-structures (synergistic effect) are obtained. • Composites based on hybrid 1D/2D combinations show lower percolation thresholds

  5. Metallic electrical transport in inter-graphitic planes of an individual tubular carbon nanocone

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Q; Gao, R X; Qu, S L [Department of Optics and Electronics Science, Harbin Institute of Technology at Wei Hai, Weihai 264209 (China); Li, J J; Gu, C Z [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100080 (China)], E-mail: wq19750505@tom.com

    2009-04-08

    Tubular carbon cones (TCCs) with a herring-bone-like graphitic structure are synthesized on gold wire via the bias-assisted hot filament chemical vapor deposition (HFCVD) method. The electrical transport properties of an individual TCC are studied in the temperature range from 300 to 500 K by using a double probe scanning electron microscopy (DPSEM) in situ electrical measurement system. The high-resistance I-V characteristics of W-TCC-Au back-to-back double junctions show that electrons tunnel through the W-TCC junction, while thermoionic transport through the Au-TCC junction contributes to low-resistance properties. Temperature dependence of the electrical characteristics indicates that inter-graphitic-plane electrical transport in TCC is metallic.

  6. Activated Flake Graphite Coated with Pyrolysis Carbon as Promising Anode for Lithium Storage

    International Nuclear Information System (INIS)

    Chen, Jun; Zou, Guoqiang; Zhang, Yan; Song, Weixin; Hou, Hongshuai; Huang, Zhaodong; Liao, Hanxiao; Li, Simin; Ji, Xiaobo

    2016-01-01

    A facile route to improve the lithium-storage properties of flake graphite (FG) is proposed through coating pyrolysis carbon from polyvinylidene fluoride (PVDF) assisted by KOH activation. The interplanar distance between the graphene sheets of activated PVDF/FG is enlarged, effectively suppressing the electrode deformation during lithium (de)-intercalation. More edge and porous structures of PVDF/FG arising from KOH activation on graphite flakes contribute to improved electron and ion transport, leading to great improvement in its rate and cycling performances. The initial specific capacity of the activated PVDF/FG is 476.6 mAh g −1 at 50 mA g −1 and when the current increases to 1000 mA g −1 , the value still retains 142.6 mAh g −1 .

  7. Percolation transition in carbon composite on the basis of fullerenes and exfoliated graphite

    Science.gov (United States)

    Berezkin, V. I.; Popov, V. V.

    2018-01-01

    The electrical conductivity of a carbon composite on the basis of C60 fullerenes and exfoliated graphite is investigated in the range of relative contents of components from 0 to 100%. The samples are obtained by the thermal treatment of the initial dispersed mixtures in vacuum in the diffusion-adsorption process and their further cold pressing. The resistivity of the samples gradually increases with an increase in the fraction of fullerenes, and a sharp transition from the conductive state to the dielectric one is observed after achieving certain concentrations of C60. The interpretation of the results within the percolation theory makes it possible to evaluate the percolation threshold (expressed as a relative content of graphite) as equal to 4.45 wt % and the critical conductivity index as equal to 1.85 (which is typical for three-dimensional twocomponent disordered media including those having pores).

  8. Electrochemical insertion in solid media of alkali cations in carbonated host structures (polyacetylene, fullerene and graphite)

    International Nuclear Information System (INIS)

    Lemont, Sylvain

    1994-01-01

    This research thesis reports the investigation of electrochemical insertion of alkali cations in different host carbon containing structures (polyacetylene, fullerene, graphite). After a recall of the main characteristics of the three considered compounds, the author reports a bibliographical survey, describes the different compounds which can be used as solid electrolytes and explains the choice of the studied compounds with respect to their phase diagrams, ionic conductivity, electrochemical stability range. He describes the experimental methods, discusses the results obtained by intercalation of alkali cations (Li + , Na + , K + ) in polyacetylene. He discusses the electrochemical and structural results obtained on intercalation compounds of lithium and sodium ions in fullerene. The structures of several phases have been obtained by electron diffraction. Preliminary studies of electron energy loss spectrometry (EELS) are reported. The last part compares the results obtained on two types of graphite: pellets and spherules [fr

  9. Activation of peroxymonosulfate by graphitic carbon nitride loaded on activated carbon for organic pollutants degradation

    Energy Technology Data Exchange (ETDEWEB)

    Wei, Mingyu; Gao, Long; Li, Jun [School of Environmental Engineering, Wuhan Textile University, Wuhan 430073 (China); Fang, Jia [School of Chemistry and Chemical Engineering, Wuhan Textile University, Wuhan 430073 (China); Cai, Wenxuan [School of Environmental Engineering, Wuhan Textile University, Wuhan 430073 (China); Li, Xiaoxia [School of Chemistry and Chemical Engineering, Wuhan Textile University, Wuhan 430073 (China); Xu, Aihua, E-mail: xahspinel@sina.com [School of Environmental Engineering, Wuhan Textile University, Wuhan 430073 (China); Engineering Research Center for Clean Production of Textile Dyeing and Printing, Ministry of Education, Wuhan 430073 (China)

    2016-10-05

    Highlights: • Supported g-C{sub 3}N{sub 4} on AC catalysts with different loadings were prepared. • The metal free catalysts exhibited high efficiency for dyes degradation with PMS. • The catalyst presented a long-term stability for multiple runs. • The C=O groups played a key role in the oxidation process. - Abstract: Graphitic carbon nitride supported on activated carbon (g-C{sub 3}N{sub 4}/AC) was prepared through an in situ thermal approach and used as a metal free catalyst for pollutants degradation in the presence of peroxymonosulfate (PMS) without light irradiation. It was found that g-C{sub 3}N{sub 4} was highly dispersed on the surface of AC with the increase of surface area and the exposition of more edges and defects. The much easier oxidation of C species in g-C{sub 3}N{sub 4} to C=O was also observed from XPS spectra. Acid Orange 7 (AO7) and other organic pollutants could be completely degraded by the g-C{sub 3}N{sub 4}/AC catalyst within 20 min with PMS, while g-C{sub 3}N{sub 4}+PMS and AC+PMS showed no significant activity for the reaction. The performance of the catalyst was significantly influenced by the amount of g-C{sub 3}N{sub 4} loaded on AC; but was nearly not affected by the initial solution pH and reaction temperature. In addition, the catalysts presented good stability. A nonradical mechanism accompanied by radical generation (HO· and SO{sub 4}·{sup −}) in AO7 oxidation was proposed in the system. The C=O groups play a key role in the process; while the exposure of more N-(C){sub 3} group can further increase its electron density and basicity. This study can contribute to the development of green materials for sustainable remediation of aqueous organic pollutants.

  10. Microwave absorbing property of silicone rubber composites with added carbonyl iron particles and graphite platelet

    International Nuclear Information System (INIS)

    Xu, Yonggang; Zhang, Deyuan; Cai, Jun; Yuan, Liming; Zhang, Wenqiang

    2013-01-01

    Silicone rubber composites filled with carbonyl iron particles (CIPs) and graphite platelet (GP) were prepared using non-coating or coating processes. The complex permittivity and permeability of the composites were measured using a vector network analyzer in the frequency range of 1–18 GHz and dc electric conductivity was measured by the standard four-point contact method. The results showed that CIPs/GP composites fabricated in the coating process had the highest permittivity and permeability due to the particle orientation and interactions between the two absorbents. The coating process resulted in a decreased effective eccentricity of the absorbents, and the dc conductivity increased according to Neelakanta's equations. The reflection loss (RL) value showed that the composites had an excellent absorbing property in the L-band, minimum −11.85 dB at 1.5 mm and −15.02 dB at 2 mm. Thus, GP could be an effective additive in preparing thin absorbing composites in the L-band. - Highlights: ► The added GP increased the permittivity and permeability of composites filled with CIPs. ► The enhancement was owing to interactions of the two absorbents and the fabrication process. ► The coating process decreased the effective eccentricity of the particles, and increased the conductivity of the composites. ► The composites to which CIPs/GP were added in coating process had excellent absorbing properties in the L-band.

  11. Hierarchical porous nitrogen-doped partial graphitized carbon monoliths for supercapacitor

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Yifeng; Du, Juan; Liu, Lei; Wang, Guoxu; Zhang, Hongliang; Chen, Aibing, E-mail: chen-ab@163.com [Hebei University of Science and Technology, College of Chemical and Pharmaceutical Engineering (China)

    2017-03-15

    Porous carbon monoliths have attracted great interest in many fields due to their easy availability, large specific surface area, desirable electronic conductivity, and tunable pore structure. In this work, hierarchical porous nitrogen-doped partial graphitized carbon monoliths (N–MC–Fe) with ordered mesoporous have been successfully synthesized by using resorcinol-formaldehyde as precursors, iron salts as catalyst, and mixed triblock copolymers as templates via a one-step hydrothermal method. In the reactant system, hexamethylenetetramine (HMT) is used as nitrogen source and one of the carbon precursors under hydrothermal conditions instead of using toxic formaldehyde. The N–MC–Fe show hierarchically porous structures, with interconnected macroporous and ordered hexagonally arranged mesoporous. Nitrogen element is in situ doped into carbon through decomposition of HMT. Iron catalyst is helpful to improve the graphitization degree and pore volume of N–MC–Fe. The synthesis strategy is user-friendly, cost-effective, and can be easily scaled up for production. As supercapacitors, the N–MC–Fe show good capacity with high specific capacitance and good electrochemical stability.

  12. High resolution transmission electron microscopic study of nanoporous carbon consisting of curved single graphite sheets

    International Nuclear Information System (INIS)

    Bourgeois, L.N.; Bursill, L.A.

    1997-01-01

    A high resolution transmission electron microscopic study of a nanoporous carbon rich in curved graphite monolayers is presented. Observations of very thin regions. including the effect of tilting the specimen with respect to the electron beam, are reported. The initiation of single sheet material on an oriented graphite substrate is also observed. When combined with image simulations and independent measurements of the density (1.37g cm -3 ) and sp 3 /sp 2 +sp 2 bonding fraction (0.16), these observations suggest that this material is a two phase mixture containing a relatively low density aggregation of essentially capped single shells like squat nanotubes and polyhedra, plus a relatively dense 'amorphous' carbon structure which may be described using a random-Schwarzite model. Some negatively-curved sheets were also identified in the low density phase. Finally, some discussion is offered regarding the growth mechanisms responsible for this nanoporous carbon and its relationship with the structures of amorphous carbons across a broad range of densities, porosities and sp 3 /sp 2 +sp 3 bonding fractions

  13. Development of electrically heated rods with resistive element of graphite or carbon/carbon composites for simulating transients in nuclear reactors

    International Nuclear Information System (INIS)

    Polidoro, H.A.

    1987-01-01

    Thermo-hydraulic problems, in nuclear plants are normally analysed by the use of electrically heated rods. The direct or indirect heater rods are limited in their use because, for high temperatures and high heat flux, the heating element temperature approach its melting point. The use of platinum or tantalum is not economically viable. Graphite and carbon/carbon composites are alternative materials because they are good electrical conductors and have good mechanical properties at high temperatures. Graphite and carbon/carbon composites were used to make heating elements for testing by indirect heating. The swaging process used to reduce the cladding diameter prevented the fabrication of graphite heater rods. Carbon/carbon composite used to make heating elements gave good results up to a heat flux of 100 W/cm 2 . It is easy to verify that this value can be exceeded if the choice of the complementary materials for insulator and cladding improved. (author) [pt

  14. Nitrogen–doped graphitized carbon shell encapsulated NiFe nanoparticles: A highly durable oxygen evolution catalyst

    Energy Technology Data Exchange (ETDEWEB)

    Du, Lei; Luo, Langli; Feng, Zhenxing; Engelhard, Mark; Xie, Xiaohong; Han, Binghong; Sun, Junming; Zhang, Jianghao; Yin, Geping; Wang, Chongmin; Wang, Yong; Shao, Yuyan

    2017-09-01

    Oxygen evolution reaction (OER) plays a crucial role in various energy conversion devices such as water electrolyzers and metal–air batteries. Precious metal catalysts such as Ir, Ru and their oxides are usually used for enhanced reaction kinetics but are limited by their scarce resource. The challenges associated with alternative non–precious metal catalysts such as transition metal oxides and (oxy)hydroxides etc. are their low electronic conductivity and poor durability. Here, we report OER catalysts of NiFe nanoparticles encapsulated by nitrogen–doped graphitized carbon shells derived from bimetallic metal–organic frameworks (MOFs) precursors. The optimal OER catalyst shows excellent activity (360 mV overpotential at 10 mA cm–2GEO) and durability (no obvious degradation after 20 000 cycles). The electron-donation from Fe and tuned electronic structure of metal cores by Ni are revealed to be primary contributors to the enhanced OER activity. We further demonstrated that the structure and morphology of encapsulating carbon shells, which are the key factors influencing the durability, are facilely controlled by chemical state of precursors. Severe metal particle growth probably caused by oxidation of carbon shells and encapsulated nanoparticles is believed to the main mechanism for activity degradation in these catalysts.

  15. Fe-Catalyzed Synthesis of Porous Carbons Spheres with High Graphitization Degree for High-Performance Supercapacitors

    Science.gov (United States)

    Zhu, Jun; Shi, Hongwei; Zhuo, Xin; Hu, Yalin

    2017-10-01

    We have developed a facile and efficient Fe-catalyzed method for fabrication of porous carbons spheres with high graphitization degree (GNPCs) using glucose as carbon precursor at relatively low carbonization temperature. GNPCs not only have relatively large accessible ion surface area to accommodate greater capacity but also high graphitization degree to accelerate ion diffusion. As a typical application, we demonstrate that GNPCs exhibit excellent electrochemical performance for use in supercapacitors, with high specific capacity of 150.6 F g-1 at current density of 1 A g-1 and good rate capability and superior cycling stability over 10,000 cycles, confirming their potential application for energy storage. Moreover, it is believed that this method offers a new strategy for synthesis of porous carbons with high graphitization degree.

  16. Evaluation of plasma disruption simulating short pulse laser irradiation experiments on boronated graphites and CFCs [carbon fibre composites

    International Nuclear Information System (INIS)

    Stad, R.C.L. van der; Klippel, H.T.; Kraaij, G.J.

    1992-12-01

    New experimental and numerical results from disruption heat flux simulations in the millisecond range with laser beams are discussed. For a number of graphites, boronated graphites and carbon fibre composites, the effective enthalpy of ablation is determined as 30 ± 3 MJ/kg, using laser pulses of about -.3 ms. The numerical results predict the experimental results rather well. No effect of boron doping on the ablation enthalpy is found. (author). 9 refs., 4 figs., 1 tab

  17. Adsorption and manipulation of carbon onions on highly oriented pyrolytic graphite studied with atomic force microscopy

    International Nuclear Information System (INIS)

    Zhou Jianfeng; Shen Ziyong; Hou Shimin; Zhao Xingyu; Xue Zengquan; Shi Zujin; Gu Zhennan

    2007-01-01

    Carbon onions produced by DC arc discharge method were deposited on highly oriented pyrolytic graphite (HOPG) surface and their adsorption and manipulation was studied using an atomic force microscopy (AFM). Well-dispersed adsorption of carbon onions on HOPG surface was obtained and aggregations of onions were not observed. The van der Waals interaction between the onion and HOPG surface and that between two onions, were calculated and discussed using Hamaker's theory. The manipulation of adsorbed onions on HOPG surface was realized using the AFM in both the raster mode and the vector mode. The controllability and precision of two manipulation modes were compared and the vector mode manipulation was found superior, and is a useful technique for the construction of nano-scale devices based on carbon onions

  18. Graphitic carbon nitride: Synthesis, characterization and photocatalytic decomposition of nitrous oxide

    International Nuclear Information System (INIS)

    Praus, Petr; Svoboda, Ladislav; Ritz, Michal; Troppová, Ivana; Šihor, Marcel; Kočí, Kamila

    2017-01-01

    Graphitic carbon nitride (g-C_3N_4) was synthetized by condensation of melamine at the temperatures of 400–700 °C in air for 2 h and resulting products were characterized and finally tested for the photocatalytic decomposition of nitrous oxide. The characterization methods were elemental analysis, UV–Vis diffuse reflectance spectroscopy (DRS), photoluminescence (PL), Fourier transform infrared (FTIR) and Raman spectroscopy, measurement of specific surface area (SSA), X-ray powder diffraction (XRD), scanning (SEM) and transmission (TEM) electron microscopy. The XRD patterns, FTIR and Raman spectra proved the presence of g-C_3N_4 at above 550 °C but the optimal synthesis temperature of 600–650 °C was found. Under these conditions graphitic carbon nitride of the overall empirical composition of C_6N_9H_2 was formed. At lower temperatures g-C_3N_4 with a higher content of hydrogen was formed but at higher temperatures g-C_3N_4 was decomposed. At the temperatures above 650 °C, its exfoliation was observed. The photocatalytic experiments showed that the activity of all the samples synthetized at 400–700 °C was very similar, that is, within the range of experimental error (5 %). The total conversion of N_2O reached about 43 % after 14 h. - Highlights: • Graphitic carbon nitride (g-C_3N_4) was thermally synthetized from melamine in the range of 400–700 °C. • The optimal temperature was determined at 600–650 °C. • All synthesis products were properly characterized by physico-chemical methods. • Exfoliation of g-C_3N_4 at above 600 °C was observed. • g-C_3N_4 was used for the photocatalytic decomposition of N_2O.

  19. Wettability of graphitic-carbon and silicon surfaces: MD modeling and theoretical analysis

    International Nuclear Information System (INIS)

    Ramos-Alvarado, Bladimir; Kumar, Satish; Peterson, G. P.

    2015-01-01

    The wettability of graphitic carbon and silicon surfaces was numerically and theoretically investigated. A multi-response method has been developed for the analysis of conventional molecular dynamics (MD) simulations of droplets wettability. The contact angle and indicators of the quality of the computations are tracked as a function of the data sets analyzed over time. This method of analysis allows accurate calculations of the contact angle obtained from the MD simulations. Analytical models were also developed for the calculation of the work of adhesion using the mean-field theory, accounting for the interfacial entropy changes. A calibration method is proposed to provide better predictions of the respective contact angles under different solid-liquid interaction potentials. Estimations of the binding energy between a water monomer and graphite match those previously reported. In addition, a breakdown in the relationship between the binding energy and the contact angle was observed. The macroscopic contact angles obtained from the MD simulations were found to match those predicted by the mean-field model for graphite under different wettability conditions, as well as the contact angles of Si(100) and Si(111) surfaces. Finally, an assessment of the effect of the Lennard-Jones cutoff radius was conducted to provide guidelines for future comparisons between numerical simulations and analytical models of wettability

  20. Electrochemical characteristics of Shewanella loihica on carbon nanotubes-modified graphite surfaces

    International Nuclear Information System (INIS)

    Zhang, Xiaoming; Epifanio, Monica; Marsili, Enrico

    2013-01-01

    Highlights: • We deposited CNT coatings on graphite electrode by electrophoretic deposition. • CNT coating increased extracellular electron transfer in Shewanella loihica biofilms. • Thick electroactive biofilms hinder the electroactivity of CNT coatings. -- Abstract: High specific surface and electrocatalytic activity of the electrode surface favour extracellular electron transfer from electrochemically active biofilms to polarized electrodes. We coated layer-by-layer carbon nanotubes (CNTs) on graphite electrodes through electrophoretic deposition, thus increasing the electrocatalytic activity. After determining the optimal number of CNT layers through electrochemical methods, we grew Shewanella loihica PV-4 biofilms on the CNT-coated electrodes to quantify the increase in extracellular electron transfer rate compared with unmodified electrodes. Current density on CNT-modified electrodes was 1.7 times higher than that observed on unmodified electrodes after 48 h from inoculation. Rapid microbial cells attachment on CNT-coated electrodes, as determined from scanning electronic microscopy, explained the rapid increase of the current. Also, the CNT reduced the charge transfer resistance of the graphite electrodes, as measured by Electrochemical Impedance Spectroscopy. However, the electrocatalytic activity of the CNT-coated electrode decreased as the biofilm grew thicker and covered the CNT-coating. These result confirmed that surface-modified electrodes improve the electron transfer rate in thin biofilms (<5 μm), but are not feasible for power production in microbial fuel cells, where the biofilm thickness is much higher

  1. Roll-to-Roll Laser-Printed Graphene-Graphitic Carbon Electrodes for High-Performance Supercapacitors.

    Science.gov (United States)

    Kang, Sangmin; Lim, Kyungmi; Park, Hyeokjun; Park, Jong Bo; Park, Seong Chae; Cho, Sung-Pyo; Kang, Kisuk; Hong, Byung Hee

    2018-01-10

    Carbon electrodes including graphene and thin graphite films have been utilized for various energy and sensor applications, where the patterning of electrodes is essentially included. Laser scribing in a DVD writer and inkjet printing were used to pattern the graphene-like materials, but the size and speed of fabrication has been limited for practical applications. In this work, we devise a simple strategy to use conventional laser-printer toner materials as precursors for graphitic carbon electrodes. The toner was laser-printed on metal foils, followed by thermal annealing in hydrogen environment, finally resulting in the patterned thin graphitic carbon or graphene electrodes for supercapacitors. The electrochemical cells made of the graphene-graphitic carbon electrodes show remarkably higher energy and power performance compared to conventional supercapacitors. Furthermore, considering the simplicity and scalability of roll-to-roll (R2R) electrode patterning processes, the proposed method would enable cheaper and larger-scale synthesis and patterning of graphene-graphitic carbon electrodes for various energy applications in the future.

  2. Uranium Oxide Aerosol Transport in Porous Graphite

    Energy Technology Data Exchange (ETDEWEB)

    Blanchard, Jeremy; Gerlach, David C.; Scheele, Randall D.; Stewart, Mark L.; Reid, Bruce D.; Gauglitz, Phillip A.; Bagaasen, Larry M.; Brown, Charles C.; Iovin, Cristian; Delegard, Calvin H.; Zelenyuk, Alla; Buck, Edgar C.; Riley, Brian J.; Burns, Carolyn A.

    2012-01-23

    The objective of this paper is to investigate the transport of uranium oxide particles that may be present in carbon dioxide (CO2) gas coolant, into the graphite blocks of gas-cooled, graphite moderated reactors. The transport of uranium oxide in the coolant system, and subsequent deposition of this material in the graphite, of such reactors is of interest because it has the potential to influence the application of the Graphite Isotope Ratio Method (GIRM). The GIRM is a technology that has been developed to validate the declared operation of graphite moderated reactors. GIRM exploits isotopic ratio changes that occur in the impurity elements present in the graphite to infer cumulative exposure and hence the reactor’s lifetime cumulative plutonium production. Reference Gesh, et. al., for a more complete discussion on the GIRM technology.

  3. Scaled-Up Production and Transport Applications of Graphitic Carbon Nanomaterials

    Science.gov (United States)

    Saviers, Kimberly R.

    Graphitic carbon nanomaterials enhance the performance of engineered systems for energy harvesting and storage. However, commercial availability remains largely cost-prohibitive due to technical barriers to mass production. This thesis examines both the scaled-up production and energy transport applications of graphitic materials. Cost driven-production of graphitic petals is developed, carbon nanotube array thermal interface materials enhance waste heat energy harvesting, and microsupercapacitors are visually examined using a new electroreflectance measurement method. Graphitic materials have previously been synthesized using batch-style processing methods with small sample sizes, limiting their commercial viability. In order to increase production throughput, a roll-to-roll radio-frequency plasma chemical vapor deposition method is employed to continuously deposit graphitic petals on carbon fiber tow. In consideration of a full production framework, efficient and informative characterization methods in the form of electrical resistance and electrochemical capacitance are highlighted. To co-optimize the functional characteristics of the material, the processing conditions are comprehensively varied using a data-driven predictive design of experiments method. Repeatable and reliable production of graphitic materials will enable a host of creative graphene-based devices to emerge into the marketplace. Two such applications are discussed in the remaining chapters. Waste heat is most efficiently harvested at high temperatures, such as vehicle exhaust systems near 600°C. However, the resistance to heat flux at the interfaces between the harvesting device and its surroundings is detrimental to the system-level performance. To study the performance of thermal interface materials up to 700°C, a reference bar measurement method was designed. Design considerations are discussed and compared to past implementations, particularly regarding radiation heat flux and thermal

  4. Adsorption behavior of perfluorinated sulfonic acid ionomer on highly graphitized carbon nanofibers and their thermal stabilities

    DEFF Research Database (Denmark)

    Andersen, Shuang Ma; Borghei, Maryam; Dhiman, Rajnish

    2014-01-01

    A systematic adsorption study of perfluorinated sulfonic acid Nafion® ionomer on ribbon type highly graphitized carbon nanofibers (CNFs) was carried out using 19 fluorine nuclear magnetic resonance spectroscopy. Based on the values obtained for the equilibrium constant (Keq., derived from Langmuir....... The ionomer is probably adsorbed via the polar sulfonic group on hydrophilic Vulcan, whereas, it is adsorbed primarily via hydrophobic -CF2- backbone on the highly hydrophobic pristine CNFs. Ionomer adsorption behavior is gradually altered from apolar to polar group adsorption for the acid modified CNFs...

  5. A simple method for the preparation of activated carbon fibers coated with graphite nanofibers.

    Science.gov (United States)

    Kim, Byung-Joo; Park, Soo-Jin

    2007-11-15

    A simple method is described for the preparation of activated carbon fibers (ACFs) coated with graphite nanofibers (GNFs). Low-pressure-plasma mixed-gas (Ar/O2) treatment of the ACFs led to the growth of GNFs on their surface. The growth was greater at higher power inputs, and from TEM observations the GNFs were seen to be of herringbone type. It was found that the N2 adsorption capacity of the ACFs did not sharply decrease, and that volume resistivity of the ACFs enhanced as a result of this treatment.

  6. Changes in porosity of graphite caused by radiolytic gasification by carbon dioxide

    International Nuclear Information System (INIS)

    Murdie, Neil; Edwards, I.A.S.; Marsh, Harry

    1986-01-01

    Methods have been developed to study porosity in nuclear grade graphite. The changes induced during the radiolytic gasification of graphite in carbon dioxide have been investigated. Porosity in radiolytically gasified graphite (0-22.8% wt. loss) was examined by optical microscopy and scanning electron microscopy (SEM). Each sample was vacuum impregnated with a slow-setting resin containing a fluorescent dye. Optical microscopy was used to study pores >2 μm 2 c.s.a. A semi-automatic image analysis system linked to the optical microscope enabled pore parameter data including cross-sectional areas, perimeters, Feret's diameters and shape factors, to be collected. The results showed that radiolytic gasification produced a large increase in the number of pores 2 c.s.a. New open pores 2 c.s.a. were developed by gasification of existing open porosity into the closed porosity ( 2 c.s.a.) within the binder-coke. Open pores, 2-100 μm 2 c.s.a., which were gasified within the coarse-grained mosaics of the binder-coke. In the gasification process to 22.8% wt. loss, the apparent open pore volume increased from 6.6 to 33.8% and the apparent closed pore volumes decreased from approx. 3% to 0.1%. The increase in apparent open porosity from 6.6% (virgin) to 33.8% resulted from gasification within original open porosity and by the opening and development of closed porosity. There was no evidence for creation of porosity from within the 'bulk' graphite, it being developed from existing fine porosity. The structure of pores > 100 μm 2 c.s.a. showed no change because of the inhibition of oxidation by deposition of carbonaceous species from the CH 4 inhibitor. Such species diffuse to the pore wall and are sacrificially oxidised. (author)

  7. On the Deposition Equilibrium of Carbon Nanotubes or Graphite in the Reforming Processes of Lower Hydrocarbon Fuels

    Directory of Open Access Journals (Sweden)

    Zdzisław Jaworski

    2017-11-01

    Full Text Available The modeling of carbon deposition from C-H-O reformates has usually employed thermodynamic data for graphite, but has rarely employed such data for impure filamentous carbon. Therefore, electrochemical data for the literature on the chemical potential of two types of purified carbon nanotubes (CNTs are included in the study. Parameter values determining the thermodynamic equilibrium of the deposition of either graphite or CNTs are computed for dry and wet reformates from natural gas and liquefied petroleum gas. The calculation results are presented as the atomic oxygen-to-carbon ratio (O/C against temperature (200 to 100 °C for various pressures (1 to 30 bar. Areas of O/C for either carbon deposition or deposition-free are computed, and indicate the critical O/C values below which the deposition can occur. Only three types of deposited carbon were found in the studied equilibrium conditions: Graphite, multi-walled CNTs, and single-walled CNTs in bundles. The temperature regions of the appearance of the thermodynamically stable forms of solid carbon are numerically determined as being independent of pressure and the analyzed reactants. The modeling indicates a significant increase in the critical O/C for the deposition of CNTs against that for graphite. The highest rise in the critical O/C, of up to 290% at 30 bar, was found for the wet reforming process.

  8. Deposition of pyrolytic carbon from methane in the pores of artificial graphites. Influence of the temperature (1961); Depot de carbone pyrolytique dans les pores de graphites artificiels a partir de methane. Influence de la temperature (1961)

    Energy Technology Data Exchange (ETDEWEB)

    Blanchard, R; Bochirol, L; Moreau, C; Philippot, J [Commissariat a l' Energie Atomique, Grenoble (France). Centre d' Etudes Nucleaires

    1961-07-01

    it is shown that below 1000 deg. C the carbon formed by the decomposition of methane is deposited at a depth of up to several centimetres in the porosity of graphitic supports; the probable mechanism of these reactions is given. (authors) [French] On montre qu'en dessous de 1000 deg. C le depot de carbone par decomposition de methane se produit jusqu'a une profondeur de plusieurs dizaines de millimetres dans la porosite de supports graphites, et l'on indique le mecanisme probable de ces reactions. (auteurs)

  9. Effects of atmospheric air plasma treatment of graphite and carbon felt electrodes on the anodic current from Shewanella attached cells.

    Science.gov (United States)

    Epifanio, Monica; Inguva, Saikumar; Kitching, Michael; Mosnier, Jean-Paul; Marsili, Enrico

    2015-12-01

    The attachment of electrochemically active microorganisms (EAM) on an electrode is determined by both the chemistry and topography of the electrode surface. Pre-treatment of the electrode surface by atmospheric air plasma introduces hydrophilic functional groups, thereby increasing cell attachment and electroactivity in short-term experiments. In this study, we use graphite and carbon felt electrodes to grow the model EAM Shewanella loihica PV-4 at oxidative potential (0.2 V vs. Ag/AgCl). Cell attachment and electroactivity are measured through electrodynamic methods. Atmospheric air plasma pre-treatment increases cell attachment and current output at graphite electrodes by 25%, while it improves the electroactivity of the carbon felt electrodes by 450%. Air plasma pre-treatment decreased the coulombic efficiency on both carbon felt and graphite electrodes by 60% and 80%, respectively. Microbially produced flavins adsorb preferentially at the graphite electrode, and air plasma pre-treatment results in lower flavin adsorption at both graphite and carbon felt electrodes. Results show that air plasma pre-treatment is a feasible option to increase current output in bioelectrochemical systems. Copyright © 2015 Elsevier B.V. All rights reserved.

  10. Behavior of LASL-made graphite, ZrC, and ZrC-containing coated particles in irradiation tests HT-28 and HT-29

    International Nuclear Information System (INIS)

    Reiswig, R.D.; Wagner, P.; Hollabaugh, C.M.; White, R.W.; O'Rourke, J.A.; Davidson, K.V.; Schell, D.H.

    1976-01-01

    Three types of materials, extruded graphite, hot-pressed ZrC, and particles with ZrC coatings, were irradiated in ORNL High Fluence Isotope Reactor Irradiation tests HT-28 and HT-29. The ZrC seemed unaffected. The graphite changed in dimensions, x-ray diffraction parameters, and thermal conductivity. The four types of coated particles tested all resisted the irradiation well, except one set of particles with double-graded C-ZrC-C coats. Overall, the results were considered encouraging for use of ZrC and extruded graphite fuel matrices. 16 fig

  11. Artificial graphites

    International Nuclear Information System (INIS)

    Maire, J.

    1984-01-01

    Artificial graphites are obtained by agglomeration of carbon powders with an organic binder, then by carbonisation at 1000 0 C and graphitization at 2800 0 C. After description of the processes and products, we show how the properties of the various materials lead to the various uses. Using graphite enables us to solve some problems, but it is not sufficient to satisfy all the need of the application. New carbonaceous material open application range. Finally, if some products are becoming obsolete, other ones are being developed in new applications [fr

  12. Graphitic carbon in a nanostructured titanium oxycarbide thin film to improve implant osseointegration

    International Nuclear Information System (INIS)

    Zanoni, R.; Ioannidu, C.A.; Mazzola, L.; Politi, L.; Misiano, C.; Longo, G.; Falconieri, M.; Scandurra, R.

    2015-01-01

    A nanostructured coating layer on titanium implants, able to improve their integration into bones and to protect against the harsh conditions of body fluids, was obtained by Ion Plating Plasma Assisted, a method suitable for industrial applications. A titanium carbide target was attached under vacuum to a magnetron sputtering source powered with a direct current in the 500–1100 W range, and a 100 W radio frequency was applied to the sample holder. The samples produced at 900 W gave the best biological response in terms of overexpression of some genes of proteins involved in bone turnover. We report the characterization of a reference and of an implant sample, both obtained at 900 W. Different micro/nanoscopic techniques evidenced the morphology of the substrates, and X-ray Photoelectron Spectroscopy was used to disclose the surface composition. The layer is a 500 nm thick hard nanostructure, composed of 60% graphitic carbon clustered with 15% TiC and 25% Ti oxides. - Highlights: • Nanostructured TiC protective layers were produced on Ti samples for prostheses. • Ion Plating Plasma-Assisted Deposition from TiC targets was used on Ti samples. • A model of the surface layer has been drawn from XPS, Raman, AFM, FIB/SEM, TEM. • The layer is mainly composed of graphitic carbon in addition to TiC and Ti oxides

  13. Combination Carbon Nanotubes with Graphene Modified Natural Graphite and Its Electrochemical Performance

    Directory of Open Access Journals (Sweden)

    DENG Ling-feng

    2017-04-01

    Full Text Available The CNTs/rGO/NG composite lithiumion battery anode material was synthesized by thermal reducing, using graphene oxide (GO and carbon nanotubes (CNTs as precursors for a 5 ∶ 3 proportion. The morphology, structure, and electrochemical performance of the composite were characterized by scanning electron microscopy(SEM, X-ray diffractometry(XRD, Fourier transform infrared spectra (FTIR and electrochemical measurements. The results show that reduced graphene oxide and carbon nanotubes form a perfect three-dimensional network structure on the surface of natural graphite. CNTs/rGO/NG composite has good rate performance and cycle life,compared with pure natural graphite.The initial discharge capacity of designed anode is 479mAh/g at 0.1C, the reversible capacity up to 473mAh/g after 100 cycles,the capacity is still 439.5mAh/g, the capacity retention rate is 92%,and the capacity is 457, 433, 394mAh/g at 0.5, 1, 5C, respectively.

  14. Aligned Carbon Nanotube Arrays Bonded to Solid Graphite Substrates: Thermal Analysis for Future Device Cooling Applications

    Directory of Open Access Journals (Sweden)

    Betty T. Quinton

    2018-05-01

    Full Text Available Carbon nanotubes (CNTs are known for high thermal conductivity and have potential use as nano-radiators or heat exchangers. This paper focuses on the thermal performance of carpet-like arrays of vertically aligned CNTs on solid graphite substrates with the idea of investigating their behavior as a function of carpet dimensions and predicting their performance as thermal interface material (TIM for electronic device cooling. Vertically aligned CNTs were grown on highly oriented pyrolytic graphite (HOPG substrate, which creates a robust and durable all-carbon hierarchical structure. The multi-layer thermal analysis approach using Netzsch laser flash analysis system was used to evaluate their performance as a function of carpet height, from which their thermal properties can be determined. It was seen that the thermal resistance of the CNT array varies linearly with CNT carpet height, providing a unique way of decoupling the properties of the CNT carpet from its interface. This data was used to estimate the thermal conductivity of individual multi-walled nanotube strands in this carpet, which was about 35 W/m-K. The influence of CNT carpet parameters (aerial density, diameter, and length on thermal resistance of the CNT carpet and its potential advantages and limitations as an integrated TIM are discussed.

  15. Standard Test Methods for Properties of Continuous Filament Carbon and Graphite Fiber Tows

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    1999-01-01

    1.1 These test methods cover the preparation and tensile testing of resin-impregnated and consolidated test specimens made from continuous filament carbon and graphite yarns, rovings, and tows to determine their tensile properties. 1.2 These test methods also cover the determination of the density and mass per unit length of the yarn, roving, or tow to provide supplementary data for tensile property calculation. 1.3 These test methods include a procedure for sizing removal to provide the preferred desized fiber samples for density measurement. This procedure may also be used to determine the weight percent sizing. 1.4 These test methods include a procedure for determining the weight percent moisture adsorption of carbon or graphite fiber. 1.5 The values stated in SI units are to be regarded as the standard. The values in parentheses are for information only. 1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of t...

  16. Facile synthesis and enhanced visible-light photocatalysis of graphitic carbon nitride composite semiconductors.

    Science.gov (United States)

    Li, Huiquan; Liu, Yuxing; Gao, Xing; Fu, Cong; Wang, Xinchen

    2015-04-13

    The semiconductor heterojunction has been an effective architecture to enhance photocatalytic activity by promoting photogenerated charge separation. Here, graphitic carbon nitride (CN) and B-modified graphitic carbon nitride (CNB) composite semiconductors were fabricated by a facile calcination process using cheap, sustainable, and easily available sodium tetraphenylboron and urea as precursors. The synthetic CN-CNB-25 semiconductor with a suitable CNB content showed the highest visible-light activity. Its degradation ratio for methyl orange and phenol was more than twice that of CN and CNB and its H2 evolution rate was ∼3.4 and ∼1.8 times higher than that of CN and CNB, respectively. It also displayed excellent stability and reusability. The enhanced activity of CN-CNB-25 was attributed predominantly to the efficient separation of photoinduced electrons and holes. This paper describes a visible-light-responsive CN composite semiconductor with great potential in environmental and energy applications. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  17. Graphitic carbon in a nanostructured titanium oxycarbide thin film to improve implant osseointegration

    Energy Technology Data Exchange (ETDEWEB)

    Zanoni, R., E-mail: robertino.zanoni@uniroma1.it [Dipartimento di Chimica, Università di Roma ‘La Sapienza’ p.le Aldo Moro 5, 00185 Rome (Italy); Ioannidu, C.A.; Mazzola, L.; Politi, L. [Dipartimento di Scienze Biochimiche, Università di Roma ‘La Sapienza’, p.le Aldo Moro 5, 00185 Rome (Italy); Misiano, C. [Romana Film Sottili, Anzio, Rome (Italy); Longo, G. [Istituto Superiore di Sanità, Viale Regina Elena 299, 00161 Rome (Italy); Ecole Polytechnique Fédérale de Lausanne, SB IPSB LPMV, BSP 409 (Cubotron UNIL), R.te de la Sorge, CH-1015 Lausanne (Switzerland); Falconieri, M. [ENEA, Unità Tecnica Applicazioni delle Radiazioni, via Anguillarese 301, 00123 Rome (Italy); Scandurra, R. [Dipartimento di Scienze Biochimiche, Università di Roma ‘La Sapienza’, p.le Aldo Moro 5, 00185 Rome (Italy)

    2015-01-01

    A nanostructured coating layer on titanium implants, able to improve their integration into bones and to protect against the harsh conditions of body fluids, was obtained by Ion Plating Plasma Assisted, a method suitable for industrial applications. A titanium carbide target was attached under vacuum to a magnetron sputtering source powered with a direct current in the 500–1100 W range, and a 100 W radio frequency was applied to the sample holder. The samples produced at 900 W gave the best biological response in terms of overexpression of some genes of proteins involved in bone turnover. We report the characterization of a reference and of an implant sample, both obtained at 900 W. Different micro/nanoscopic techniques evidenced the morphology of the substrates, and X-ray Photoelectron Spectroscopy was used to disclose the surface composition. The layer is a 500 nm thick hard nanostructure, composed of 60% graphitic carbon clustered with 15% TiC and 25% Ti oxides. - Highlights: • Nanostructured TiC protective layers were produced on Ti samples for prostheses. • Ion Plating Plasma-Assisted Deposition from TiC targets was used on Ti samples. • A model of the surface layer has been drawn from XPS, Raman, AFM, FIB/SEM, TEM. • The layer is mainly composed of graphitic carbon in addition to TiC and Ti oxides.

  18. Enhancement of the Rate Capability of LiFePO4 by a New Highly Graphitic Carbon-Coating Method.

    Science.gov (United States)

    Song, Jianjun; Sun, Bing; Liu, Hao; Ma, Zhipeng; Chen, Zhouhao; Shao, Guangjie; Wang, Guoxiu

    2016-06-22

    Low lithium ion diffusivity and poor electronic conductivity are two major drawbacks for the wide application of LiFePO4 in high-power lithium ion batteries. In this work, we report a facile and efficient carbon-coating method to prepare LiFePO4/graphitic carbon composites by in situ carbonization of perylene-3,4,9,10-tetracarboxylic dianhydride during calcination. Perylene-3,4,9,10-tetracarboxylic dianhydride containing naphthalene rings can be easily converted to highly graphitic carbon during thermal treatment. The ultrathin layer of highly graphitic carbon coating drastically increased the electronic conductivity of LiFePO4. The short pathway along the [010] direction of LiFePO4 nanoplates could decrease the Li(+) ion diffusion path. In favor of the high electronic conductivity and short lithium ion diffusion distance, the LiFePO4/graphitic carbon composites exhibit an excellent cycling stability at high current rates at room temperature and superior performance at low temperature (-20 °C).

  19. Inter-diffusion of carbon into niobium coatings deposited on graphite

    International Nuclear Information System (INIS)

    Barzilai, S.; Raveh, A.; Frage, N.

    2006-01-01

    The inter-diffusion of carbon (originating from a graphite substrate) into a niobium coating and the fabrication of its carbides by heat treatment in the temperature range of 1073-1773 K was studied. The thickness of the Nb 2 C and Nbc phases formed after heat treatment as well as the inter-diffusion coefficients for the formation of the carbide layers were also studied. It was found that the carbide layer growth displayed parabolic behavior patterns inherent in the growth rate constants (K) of Nb 2 C and NbC layers. By assuming that the inter-diffusion coefficients are independent of concentration, it was possible to determine the inter-diffusion coefficients of carbon D c into Nb 2 C and NbC layers as a function of temperature

  20. Analysis of the cytotoxicity of carbon-based nanoparticles, diamond and graphite, in human glioblastoma and hepatoma cell lines

    DEFF Research Database (Denmark)

    Zakrzewska, Karolina Ewa; Samluk, Anna; Wierzbicki, Mateusz

    2015-01-01

    carbon based nanoparticles, diamond and graphite, on glioblastoma and hepatoma cells were compared. First, we confirmed previous results that diamond nanoparticles are practically nontoxic. Second, graphite nanoparticles exhibited a negative impact on glioblastoma, but not on hepatoma cells. The studied...... carbon nanoparticles could be a potentially useful tool for therapeutics delivery to the brain tissue with minimal side effects on the hepatocytes. Furthermore, we showed the influence of the nanoparticles on the stable, fluorescently labeled tumor cell lines and concluded that the labeled cells...

  1. Carbon-Supported Iron Oxide Particles

    DEFF Research Database (Denmark)

    Meaz, T.; Mørup, Steen; Koch, C. Bender

    1996-01-01

    A carbon black ws impregnated with 6 wt% iron using an aqueous solution of iron nitrate. The impregnated carbon was initially dried at 125 C. The effect of heating of the iron oxide phase was investigated at temperatures between 200 and 600 C using Mossbauer spectroscopy. All heat treatments were...... done in an oxygen-containing atmosphere. Ferrihydrite is formed and is stable at and below a temperature of 300 C. At 600 C small particles of maghemite is the dominant iron oxide. A transformation reaction is suggested....

  2. The effect of bed particle size and deposit morphology on the filtration of magnetite through granular graphite beds

    International Nuclear Information System (INIS)

    Barbieri, R.R.; Bercovich, E.J.; Liberman, S.J.

    1980-01-01

    Graphite filters are of great interest for water purification in nuclear power reactors' primary systems due to their possible operation at high temperature. The influence of the bed particle size on the retention of magnetite from aqueous suspensions at room temperature was studied. The filtration coefficient changes from 0.0 to 0.18 as the mean graphite particle diameter decreases from 1.2 to 0. mm. As the retention increases, there is also an increase in the differential pressure across the bed, so both effects must be considered in order to optimize filter's operation. The specific effective volume of the deposit was calculated with the Blake-Kozeny equation and the experimental specific volumes. These are much larger than the specific volume of solid magnetite. From the results, information regarding the morphology of the deposit in the filter is obtained. (M.E.L) [es

  3. Highly Graphitic Carbon Nanofibers Web as a Cathode Material for Lithium Oxygen Batteries

    Directory of Open Access Journals (Sweden)

    Hyungkyu Han

    2018-01-01

    Full Text Available The lithium oxygen battery is a promising energy storage system due to its high theoretical energy density and ability to use oxygen from air as a “fuel”. Although various carbonaceous materials have been widely used as a cathode material due to their high electronic conductivity and facial processability, previous studies mainly focused on the electrochemical properties associated with the materials (such as graphene and carbon nanotubes and the electrode configuration. Recent reports demonstrated that the polarization associated with cycling could be significantly increased by lithium carbonates generated from the reaction between the carbon cathode and an electrolyte, which indicates that the physicochemical properties of the carbon cathode could play an important role on the electrochemical performances. However, there is no systematic study to understand these phenomena. Here, we systematically explore the electrochemical properties of carbon nanofibers (CNF webs with different graphitization degree as a cathode for Li oxygen batteries. The physicochemical properties and electrochemical properties of CNF webs were carefully monitored before and after cycling. CNF webs are prepared at 1000, 1200 and 1400 °C. CNF web pyrolyzed at 1400 °C shows lowered polarization and improved cycle retention compared to those of CNF webs pyrolyzed at 1000 and 1200 °C.

  4. Graphite Carbon-Supported Mo2C Nanocomposites by a Single-Step Solid State Reaction for Electrochemical Oxygen Reduction.

    Science.gov (United States)

    Huang, K; Bi, K; Liang, C; Lin, S; Wang, W J; Yang, T Z; Liu, J; Zhang, R; Fan, D Y; Wang, Y G; Lei, M

    2015-01-01

    Novel graphite-molybdenum carbide nanocomposites (G-Mo2C) are synthesized by a typical solid state reaction with melamine and MoO3 as precursors under inert atmosphere. The characterization results indicate that G-Mo2C composites are composed of high crystallization and purity of Mo2C and few layers of graphite carbon. Mo2C nanoparticles with sizes ranging from 5 to 50 nm are uniformly supported by surrounding graphite layers. It is believed that Mo atom resulting from the reduction of MoO3 is beneficial to the immobilization of graphite carbon. Moreover, the electrocatalytic performances of G-Mo2C for ORR in alkaline medium are investigated by cyclic voltammetry (CV), rotating disk electrode (RDE) and chronoamperometry test with 3M methanol. The results show that G-Mo2C has a considerable catalytic activity and superior methanol tolerance performance for the oxygen reduction reaction (ORR) benefiting from the chemical interaction between the carbide nanoparticles and graphite carbon.

  5. Carbon Papers and Aerogels Based on Graphene Layers and Chitosan: Direct Preparation from High Surface Area Graphite.

    Science.gov (United States)

    Barbera, Vincenzina; Guerra, Silvia; Brambilla, Luigi; Maggio, Mario; Serafini, Andrea; Conzatti, Lucia; Vitale, Alessandra; Galimberti, Maurizio

    2017-12-11

    In this work, carbon papers and aerogels based on graphene layers and chitosan were prepared. They were obtained by mixing chitosan (CS) and a high surface area nanosized graphite (HSAG) in water in the presence of acetic acid. HSAG/CS water dispersions were stable for months. High resolution transmission electron microscopy revealed the presence of few graphene layers in water suspensions. Casting or lyophilization of such suspensions led to the preparation of carbon paper and aerogel, respectively. In X-ray spectra of both aerogels and carbon paper, peaks due to regular stacks of graphene layers were not detected: graphene with unaltered sp 2 structure was obtained directly from graphite without the use of any chemical reaction. The composites were demonstrated to be electrically conductive thanks to the graphene. Chitosan thus makes it possible to obtain monolithic carbon aerogels and flexible and free-standing graphene papers directly from a nanosized graphite by avoiding oxidation to graphite oxide and successive reduction. Strong interaction between polycationic chitosan and the aromatic substrate appears to be at the origin of the stability of HSAG/CS adducts. Cation-π interaction is hypothesized, also on the basis of X-ray photoelectron spectroscopy findings. This work paves the way for the easy large-scale preparation of carbon papers through a method that has a low environmental impact and is based on a biosourced polymer, graphene, and water.

  6. Modeling to study the role of catalyst in the formation of graphitic shells during carbon nanofiber growth subjected to reactive plasma

    Science.gov (United States)

    Gupta, Ravi; Gupta, Neha; Sharma, Suresh C.

    2018-04-01

    An analytical model to study the role of a metal catalyst nanofilm in the nucleation, growth, and resulting structure of carbon nanofibers (CNFs) in low-temperature hydrogen diluted acetylene plasma has been developed. The model incorporates the nanostructuring of thin catalyst films, growth of CNF, restructuring of catalyst nanoparticles during growth, and its repercussion on the resulting structure (alignment of rolled graphene sheets around catalyst nanoparticles) by taking into account the plasma sheath formalization, kinetics of neutrals and positively charged species in the reactive plasma, flux of plasma species onto the catalyst front surface, and numerous surface reactions for carbon generation. In order to examine the influence of the catalyst film on the growth of CNFs, the numerical solutions of the model equations have been obtained for experimentally determined initial conditions and glow discharge plasma parameters. From the solutions obtained, we found that nanostructuring of thin films leads to the formation of small nanoparticles with high surface number density. The CNF nucleates over these small-sized nanoparticles grow faster and attain early saturation because of the quick poisoning of small-sized catalyst particles, and contain only a few graphitic shells. However, thick nanofilms result in shorter CNFs with large diameters composed of many graphitic shells. Moreover, we found that the inclination of graphitic shells also depends on the extent up to which the catalyst can reconstruct itself during the growth. The small nanoparticles show much greater elongation along the growth axis and also show a very small difference between their tip and base diameter during the growth due to which graphitic shells align at very small angles as compared to the larger nanoparticles. The present study is useful to synthesize the thin and more extended CNFs/CNTs having a smaller opening angle (inclination angle of graphene layers) as the opening angle has a

  7. Solid-phase extraction of polar pesticides from environmental water samples on graphitized carbon and Empore-activated carbon disks and on-line coupling to octadecyl-bonded silica analytical columns.

    NARCIS (Netherlands)

    Slobodník, J.; Oztekizan, O.; Lingeman, H.; Brinkman, U.A.T.

    1996-01-01

    The suitability of Empore-activated carbon disks (EACD), Envi-Carb graphitized carbon black (GCB) and CPP-50 graphitized carbon for the trace enrichment of polar pesticides from water samples was studied by means of off-line and on-line solid-phase extraction (SPE). In the off-line procedure, 0.5-2

  8. MnO{sub 2}-wrapped hollow graphitized carbon nanosphere electrode for supercapacitor

    Energy Technology Data Exchange (ETDEWEB)

    Lv, Jing; Yang, Xing; Zhou, Haiyan; Kang, Liping; Lei, Zhibin [Key Laboratory of Applied Surface and Colloid Chemistry (Shaanxi Normal University), Ministry of Education, Xi’an 710062 (China); School of Materials Science and Engineering, Shaanxi Normal University, Xi’an 710062 (China); Liu, Zong-Huai, E-mail: zhliu@snnu.edu.cn [Key Laboratory of Applied Surface and Colloid Chemistry (Shaanxi Normal University), Ministry of Education, Xi’an 710062 (China); School of Materials Science and Engineering, Shaanxi Normal University, Xi’an 710062 (China)

    2016-01-15

    Highlights: • MnO{sub 2}/HGC nanospheres are prepared by a cooperative template wrapping method. • MnO{sub 2}/HGC nanospheres possess large specific surface area. • MnO{sub 2}/HGC nanospheres are benefit for transmission of ions and electrons. • MnO{sub 2}/HGC electrodes exhibit a high specific capacitance. - Abstract: MnO{sub 2}-wrapped hollow graphitized carbon nanospheres (MnO{sub 2}/HGC) electrodes are prepared by a cooperative template wrapping method. hollow Graphitized carbon nanospheres (HGC) are firstly obtained by carbonizing phenolic resin followed by etching the SiO{sub 2} template, then the MnO{sub 2} ultrathin nanoplates are coated on the surfaces of the HGC nanospheres through a redox reaction between KMnO{sub 4} and HGC nanospheres. The as-prepared MnO{sub 2}/HGC hollow nanospheres possess porous structure and large specific surface area (∼230 m{sup 2} g{sup −1}). The specific capacitances of MnO{sub 2}/HGC nanosphere electrodes with different mass ratios of MnO{sub 2} to HGC are about 340–380 F g{sup −1} at a scan rate of 5 mV s{sup −1} in Na{sub 2}SO{sub 4} solution, and shows relative good cycling performance of the initial capacitance after 1000 cycles. The good specific capacitance is ascribed to the novel hollow nanosphere structure, which possesses high surface-to-volume ratio, and makes it easy for the mass diffusion of electrolyte and transmission of ions and electrons and also maintains the mechanical integrality.

  9. Graphitic carbon nitride: Synthesis, characterization and photocatalytic decomposition of nitrous oxide

    Energy Technology Data Exchange (ETDEWEB)

    Praus, Petr, E-mail: petr.praus@vsb.cz [Institute of Environmental Technology, VŠB-Technical University of Ostrava, 17. Listopadu 15/2172, Ostrava 708 33 (Czech Republic); Department of Chemistry, Faculty of Metallurgy and Materials Engineering, VŠB-Technical University of Ostrava, 17. Listopadu 15/2172, Ostrava 708 33 (Czech Republic); Svoboda, Ladislav [Institute of Environmental Technology, VŠB-Technical University of Ostrava, 17. Listopadu 15/2172, Ostrava 708 33 (Czech Republic); Department of Chemistry, Faculty of Metallurgy and Materials Engineering, VŠB-Technical University of Ostrava, 17. Listopadu 15/2172, Ostrava 708 33 (Czech Republic); Ritz, Michal [Department of Chemistry, Faculty of Metallurgy and Materials Engineering, VŠB-Technical University of Ostrava, 17. Listopadu 15/2172, Ostrava 708 33 (Czech Republic); Troppová, Ivana; Šihor, Marcel; Kočí, Kamila [Institute of Environmental Technology, VŠB-Technical University of Ostrava, 17. Listopadu 15/2172, Ostrava 708 33 (Czech Republic)

    2017-06-01

    Graphitic carbon nitride (g-C{sub 3}N{sub 4}) was synthetized by condensation of melamine at the temperatures of 400–700 °C in air for 2 h and resulting products were characterized and finally tested for the photocatalytic decomposition of nitrous oxide. The characterization methods were elemental analysis, UV–Vis diffuse reflectance spectroscopy (DRS), photoluminescence (PL), Fourier transform infrared (FTIR) and Raman spectroscopy, measurement of specific surface area (SSA), X-ray powder diffraction (XRD), scanning (SEM) and transmission (TEM) electron microscopy. The XRD patterns, FTIR and Raman spectra proved the presence of g-C{sub 3}N{sub 4} at above 550 °C but the optimal synthesis temperature of 600–650 °C was found. Under these conditions graphitic carbon nitride of the overall empirical composition of C{sub 6}N{sub 9}H{sub 2} was formed. At lower temperatures g-C{sub 3}N{sub 4} with a higher content of hydrogen was formed but at higher temperatures g-C{sub 3}N{sub 4} was decomposed. At the temperatures above 650 °C, its exfoliation was observed. The photocatalytic experiments showed that the activity of all the samples synthetized at 400–700 °C was very similar, that is, within the range of experimental error (5 %). The total conversion of N{sub 2}O reached about 43 % after 14 h. - Highlights: • Graphitic carbon nitride (g-C{sub 3}N{sub 4}) was thermally synthetized from melamine in the range of 400–700 °C. • The optimal temperature was determined at 600–650 °C. • All synthesis products were properly characterized by physico-chemical methods. • Exfoliation of g-C{sub 3}N{sub 4} at above 600 °C was observed. • g-C{sub 3}N{sub 4} was used for the photocatalytic decomposition of N{sub 2}O.

  10. X-ray photoelectron spectroscopy of graphitic carbon nanomaterials doped with heteroatoms

    Directory of Open Access Journals (Sweden)

    Toma Susi

    2015-01-01

    Full Text Available X-ray photoelectron spectroscopy (XPS is one of the best tools for studying the chemical modification of surfaces, and in particular the distribution and bonding of heteroatom dopants in carbon nanomaterials such as graphene and carbon nanotubes. Although these materials have superb intrinsic properties, these often need to be modified in a controlled way for specific applications. Towards this aim, the most studied dopants are neighbors to carbon in the periodic table, nitrogen and boron, with phosphorus starting to emerge as an interesting new alternative. Hundreds of studies have used XPS for analyzing the concentration and bonding of dopants in various materials. Although the majority of works has concentrated on nitrogen, important work is still ongoing to identify its precise atomic bonding configurations. In general, care should be taken in the preparation of a suitable sample, consideration of the intrinsic photoemission response of the material in question, and the appropriate spectral analysis. If this is not the case, incorrect conclusions can easily be drawn, especially in the assignment of measured binding energies into specific atomic configurations. Starting from the characteristics of pristine materials, this review provides a practical guide for interpreting X-ray photoelectron spectra of doped graphitic carbon nanomaterials, and a reference for their binding energies that are vital for compositional analysis via XPS.

  11. Green synthesis of graphitic carbon nitride nanodots using sodium chloride template

    Energy Technology Data Exchange (ETDEWEB)

    Yuan, Bo [National University of Defense Technology, College of Science (China); Zou, Xianshuai; Yan, Tingnan; Fei, Junjie [Xiangtan University, College of Chemistry (China); Chu, Zengyong, E-mail: chuzy@nudt.edu.cn [National University of Defense Technology, College of Science (China)

    2016-05-15

    Graphitic carbon nitride (g-C{sub 3}N{sub 4}) nanodots are simply prepared by a thermal treatment of dicyandiamide (DCDA) confined within NaCl templates. Cyano groups are introduced to the nanodots due to the catalytic effect of NaCl. NaCl could facilitate the polymerization of DCDA at lower temperatures, but will promote the decomposition when the temperature is above 550 °C. Thermal treatment at 600 °C for 30 min is the optimal condition for the scalable synthesis of g-C{sub 3}N{sub 4} nanodots with an average diameter of ~9 nm. g-C{sub 3}N{sub 4} nanodots have a higher band gap of 3.1 eV, which can emit bright blue light due to the decreased diameter, the introduction of cyano groups, and the incorporation of some sodium ions. The residue sodium ions and the cyano groups might lead to the local distortion of the graphitic crystals, or act as recombination centers for the enhanced photoluminescence.Graphical Abstract.

  12. Synthesis of Carbon Dots with Multiple Color Emission by Controlled Graphitization and Surface Functionalization.

    Science.gov (United States)

    Miao, Xiang; Qu, Dan; Yang, Dongxue; Nie, Bing; Zhao, Yikang; Fan, Hongyou; Sun, Zaicheng

    2018-01-01

    Multiple-color-emissive carbon dots (CDots) have potential applications in various fields such as bioimaging, light-emitting devices, and photocatalysis. The majority of the current CDots to date exhibit excitation-wavelength-dependent emissions with their maximum emission limited at the blue-light region. Here, a synthesis of multiple-color-emission CDots by controlled graphitization and surface function is reported. The CDots are synthesized through controlled thermal pyrolysis of citric acid and urea. By regulating the thermal-pyrolysis temperature and ratio of reactants, the maximum emission of the resulting CDots gradually shifts from blue to red light, covering the entire light spectrum. Specifically, the emission position of the CDots can be tuned from 430 to 630 nm through controlling the extent of graphitization and the amount of surface functional groups, COOH. The relative photoluminescence quantum yields of the CDots with blue, green, and red emission reach up to 52.6%, 35.1%, and 12.9%, respectively. Furthermore, it is demonstrated that the CDots can be uniformly dispersed into epoxy resins and be fabricated as transparent CDots/epoxy composites for multiple-color- and white-light-emitting devices. This research opens a door for developing low-cost CDots as alternative phosphors for light-emitting devices. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  13. Alkaline electrochemical advanced oxidation process for chromium oxidation at graphitized multi-walled carbon nanotubes.

    Science.gov (United States)

    Xue, Yudong; Zheng, Shili; Sun, Zhi; Zhang, Yi; Jin, Wei

    2017-09-01

    Alkaline electrochemical advanced oxidation processes for chromium oxidation and Cr-contaminated waste disposal were reported in this study. The highly graphitized multi-walled carbon nanotubes g-MWCNTs modified electrode was prepared for the in-situ electrochemical generation of HO 2 - . RRDE test results illustrated that g-MWCNTs exhibited much higher two-electron oxygen reduction activity than other nanocarbon materials with peak current density of 1.24 mA cm -2 , %HO 2 - of 77.0% and onset potential of -0.15 V (vs. Hg/HgO). It was originated from the highly graphitized structure and good electrical conductivity as illustrated from the Raman, XRD and EIS characterizations, respectively. Large amount of reactive oxygen species (HO 2 - and ·OH) were in-situ electro-generated from the two-electron oxygen reduction and chromium-induced alkaline electro-Fenton-like reaction. The oxidation of Cr(III) was efficiently achieved within 90 min and the conversion ratio maintained more than 95% of the original value after stability test, offering an efficient and green approach for the utilization of Cr-containing wastes. Copyright © 2017 Elsevier Ltd. All rights reserved.

  14. Carbon nanostructures reduced from graphite oxide as electrode materials for supercapacitors

    Directory of Open Access Journals (Sweden)

    Yurii M. Shulga

    2015-03-01

    Full Text Available In this review we present information about obtaining and properties of carbon nanomaterials (graphite oxide, grapheme oxide, reduced graphene oxide, which are used as electrodes for supercapacitors (SC. This review describes methods of obtaining graphite oxide, followed by separation of graphene oxide and reducing graphene oxide by thermal, photochemical and chemical methods. Information on the composition and concentration of functional groups in graphene oxide and the elemental composition is described in detail. Results of the analysis of еру physical, electrochemical, thermal and optical properties of the graphene oxide and its derivatives are shown. The ratio of oxygen-containing functional groups was estimated by XPS. The presence of partial surface reduction is found. Hydroge-containing functional groups are characterized by IR spectroscopy. Method of estimating the size of graphene crystallites by Raman spectroscopy is shown. Mass loss upon heating is analyzed by thermogravimetry. The gassing of graphene oxide at thermal and photochemical reduction is studied by mass spectrometry. The difference between the abovementioned reduction methods is clearly demonstrated by the difference in the composition of the evolved gases. Also the chemical method of graphene oxide reduction with hydrazine is described. Review considers the literature data which illustrate the most interesting, from the Authors׳ point of view, aspects of that field of research.

  15. Method of producing exfoliated graphite, flexible graphite, and nano-scaled graphene platelets

    Science.gov (United States)

    Zhamu, Aruna; Shi, Jinjun; Guo, Jiusheng; Jang, Bor Z.

    2010-11-02

    The present invention provides a method of exfoliating a layered material (e.g., graphite and graphite oxide) to produce nano-scaled platelets having a thickness smaller than 100 nm, typically smaller than 10 nm. The method comprises (a) dispersing particles of graphite, graphite oxide, or a non-graphite laminar compound in a liquid medium containing therein a surfactant or dispersing agent to obtain a stable suspension or slurry; and (b) exposing the suspension or slurry to ultrasonic waves at an energy level for a sufficient length of time to produce separated nano-scaled platelets. The nano-scaled platelets are candidate reinforcement fillers for polymer nanocomposites. Nano-scaled graphene platelets are much lower-cost alternatives to carbon nano-tubes or carbon nano-fibers.

  16. Visible Light Neural Stimulation on graphitic-Carbon Nitride/Graphene Photocatalytic Fibers

    DEFF Research Database (Denmark)

    Zhang, Zhongyang; Xu, Ruodan; Wang, Zegao

    2017-01-01

    conversion, was for the first time investigated. Specifically, g-C3N4 was combined with graphene oxide (GO) in a 3D manner on the surfaces of electrospun polycaprolactone/gelatin (PG) fibers and functioned as a biocompatible interface for visible-light stimulating neuronal differentiation. The enhanced......Light stimulation allows remote and spatiotemporally accurate operation that has been applied as effective, non-invasive means of therapeutic interventions. Here, visible light neural stimulation of graphitic carbon nitride (g-C3N4), an emerging photocatalyst with visible-light optoelectronic...... was confirmed by the Lactate Dehydrogenase (LDH) assay, live dead staining and colorimetric cell viability assay CCK-8. Under a bidaily, monochromatic light stimulation at a wavelength of 450 nm at 10mW/cm2, a 18.5-fold increase of neurite outgrowth of PC12 was found on g-C3N4 coated fibers; while AA reduced GO...

  17. Supercapacitors based on 3D network of activated carbon nanowhiskers wrapped-on graphitized electrospun nanofibers

    Science.gov (United States)

    He, Shuijian; Chen, Linlin; Xie, Chencheng; Hu, Huan; Chen, Shuiliang; Hanif, Muddasir; Hou, Haoqing

    2013-12-01

    Due to their cycling stability and high power density, the supercapacitors bridge the power/energy gap between traditional dielectric capacitors and batteries/fuel cells. Electrode materials are key components for making high performance supercapacitors. An activated carbon nanowhiskers (ACNWs) wrapped-on graphitized electrospun nanofiber (GENF) network (ACNWs/GENFN) with 3D porous structure is prepared as a new type of binder-free electrode material for supercapacitors. The supercapacitor based on the ACNWs/GENFN composite material displays an excellent performance with a specific capacitance of 176.5 F g-1 at current density of 0.5 A g-1, an ultrahigh power density of 252.8 kW kg-1 at current density of 800 A g-1 and an outstanding cycling stability of no capacitance loss after 10,000 charge/discharge cycles.

  18. Fabrication and Testing of Carbon Fiber, Graphite-Epoxy Panels for Submillimeter Telescope Use

    Science.gov (United States)

    Rieger, H.; Helwig, G.; Parks, R. E.; Ulich, B. L.

    1983-12-01

    An experimental carbon-fiber, graphite-epoxy, aluminum Flexcore sandwich panel roughly 1-m square was made by Dornier System, Friedrichshafen, West Germany. The panel was a pre-prototype of the panels to be used in the dish of the 10-m diameter Sub-Millimeter Telescope, a joint project of the Max-Planck-Institute fur Radioastronomie, Bonn, West Germany, and Steward Observatory, the University of Arizona in Tucson. This paper outlines the fabrication process for the panel and indicates the surface accuracy of the panel replication process. To predict the behavior of the panel under various environmental loads, the panel was modeled structurally using anisotropic elements for the core material. Results of this analysis along with experimental verification of these predictions are also given.

  19. Metal-free hybrids of graphitic carbon nitride and nanodiamonds for photoelectrochemical and photocatalytic applications.

    Science.gov (United States)

    Zhou, Li; Zhang, Huayang; Guo, Xiaochen; Sun, Hongqi; Liu, Shaomin; Tade, Moses O; Wang, Shaobin

    2017-05-01

    Graphitic carbon nitride (g-C 3 N 4 ) has been considered as a metal-free, cost-effective, eco-friendly and efficient catalyst for various photoelectrochemical applications. However, compared to conventional metal-based photocatalysts, its photocatalytic activity is still low because of the low mobility of carriers restricted by the polymer nature. Herein, a series of hybrids of g-C 3 N 4 (GCN) and nanodiamonds (NDs) were synthesized using a solvothermal method. The photoelectrochemical performance and photocatalytic efficiency of the GCN/NDs were investigated by means of the generation of photocurrent and photodegradation of methylene blue (MB) solutions under UV-visible light irradiations. In this study, the sample of GCN/ND-33% derived from 0.1g GCN and 0.05g NDs displayed the highest photocatalytic activity and the strongest photocurrent density. The mechanism of enhanced photoelectrochemical and photocatalytic performances was also discussed. Copyright © 2017 Elsevier Inc. All rights reserved.

  20. Nickel Oxide and Nickel Co-doped Graphitic Carbon Nitride Nanocomposites and its Octylphenol Sensing Application

    KAUST Repository

    Gong, Wanyun

    2015-11-16

    Nickel oxide and nickel co-doped graphitic carbon nitride (NiO-Ni-GCN) nanocomposites were successfully prepared by thermal treatment of melamine and NiCl2 6H2O. NiO-Ni-GCN nanocomposites showed superior electrochemical catalytic activity for the oxidation of octylphenol to pure GCN. A detection method of octylphenol in environmental water samples was developed based at NiO-Ni-GCN nanocomposites modified electrode under infrared light irradiation. Differential pulse voltammetry was used as the analytic technique of octylphenol, exhibiting stable and specific concentration-dependent oxidation signal in the presence of octylphenol in the range of 10nM to 1μM and 1μM to 50μM, with a detection limit of 3.3nM (3S/N). © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  1. Mechanical behaviour of cyclic olefin copolymer/exfoliated graphite nanoplatelets nanocomposites foamed through supercritical carbon dioxide

    Directory of Open Access Journals (Sweden)

    A. Biani

    2016-12-01

    Full Text Available A cycloolefin copolymer matrix was melt mixed with exfoliated graphite nanoplatelets (xGnP and the resulting nanocomposites were foamed by supercritical carbon dioxide. The density of the obtained foams decreased with the foaming pressure. Moreover, xGnP limited the cell growth during the expansion process thus reducing the cell diameter (from 1.08 to 0.22 mm with an XGnP amount of 10 wt% at 150 bar and increasing the cell density (from 12 to 45 cells/mm2 with a nanofiller content of 10 wt% at 150 bar. Electron microscopy observations of foams evidenced exfoliation and orientation of the nanoplatelets along the cell walls. Quasi-static compressive tests and tensile creep tests on foams clearly indicated that xGnP improved the modulus (up to a factor of 10 for a xGnP content of 10 wt% and the creep stability.

  2. Nickel Oxide and Nickel Co-doped Graphitic Carbon Nitride Nanocomposites and its Octylphenol Sensing Application

    KAUST Repository

    Gong, Wanyun; Zou, Jing; Zhang, Sheng; Zhou, Xin; Jiang, Jizhou

    2015-01-01

    Nickel oxide and nickel co-doped graphitic carbon nitride (NiO-Ni-GCN) nanocomposites were successfully prepared by thermal treatment of melamine and NiCl2 6H2O. NiO-Ni-GCN nanocomposites showed superior electrochemical catalytic activity for the oxidation of octylphenol to pure GCN. A detection method of octylphenol in environmental water samples was developed based at NiO-Ni-GCN nanocomposites modified electrode under infrared light irradiation. Differential pulse voltammetry was used as the analytic technique of octylphenol, exhibiting stable and specific concentration-dependent oxidation signal in the presence of octylphenol in the range of 10nM to 1μM and 1μM to 50μM, with a detection limit of 3.3nM (3S/N). © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  3. Free vibration of fully functionally graded carbon nanotube reinforced graphite/epoxy laminates

    Science.gov (United States)

    Kuo, Shih-Yao

    2018-03-01

    This study provides the first-known vibration analysis of fully functionally graded carbon nanotube reinforced hybrid composite (FFG-CNTRHC) laminates. CNTs are non-uniformly distributed to reinforce the graphite/epoxy laminates. Some CNT distribution functions in the plane and thickness directions are proposed to more efficiently increase the stiffening effect. The rule of mixtures is modified by considering the non-homogeneous material properties of FFG-CNTRHC laminates. The formulation of the location dependent stiffness matrix and mass matrix is derived. The effects of CNT volume fraction and distribution on the natural frequencies of FFG-CNTRHC laminates are discussed. The results reveal that the FFG layout may significantly increase the natural frequencies of FFG-CNTRHC laminate.

  4. Graphitic carbon nitride nanosheet electrode-based high-performance ionic actuator

    Science.gov (United States)

    Wu, Guan; Hu, Ying; Liu, Yang; Zhao, Jingjing; Chen, Xueli; Whoehling, Vincent; Plesse, Cédric; Nguyen, Giao T. M.; Vidal, Frédéric; Chen, Wei

    2015-01-01

    Ionic actuators have attracted attention due to their remarkably large strain under low-voltage stimulation. Because actuation performance is mainly dominated by the electrochemical and electromechanical processes of the electrode layer, the electrode material and structure are crucial. Here, we report a graphitic carbon nitride nanosheet electrode-based ionic actuator that displays high electrochemical activity and electromechanical conversion abilities, including large specific capacitance (259.4 F g−1) with ionic liquid as the electrolyte, fast actuation response (0.5±0.03% in 300 ms), large electromechanical strain (0.93±0.03%) and high actuation stability (100,000 cycles) under 3 V. The key to the high performance lies in the hierarchical pore structure with dominant size actuation performance. PMID:26028354

  5. Influence of porewidening duration on the template assisted growth of graphitic carbon nitride nanostructures

    Science.gov (United States)

    Suchitra, S. M.; Udayashankar, N. K.

    2018-01-01

    Porous anodic aluminium oxide (AAO) membranes with a highly ordered pore arrangement are typically used as ideal templates for the synthesis of numerous nanostructured materials. Highly ordered templates gained significant attraction due to the fact that they are readily fabricated through self-organised simple anodization process. In this paper, the effect of different pore-widening treatments on the quality of the pores of the AAO templates prepared with different electrolytes were inspected. Results confirmed that, without altering the interpore distance different pore dimensions and diameters of the AAO templates can be easily achieved by chemical pore widening process at room temperature. Also, graphitic carbon nitride nanorods of different dimension have been fabricated from AAO template after porewidening process. These nanostructures are widely used in case of metal free visible light driven photo catalysis, photo degradation of organic pollutants, photo electric conversion and water splitting applications.

  6. Metastable carbon in two chondritic porous interplanetary dust particles

    International Nuclear Information System (INIS)

    Rietmeijer, F.J.M.; Mackinnon, I.D.R.

    1987-01-01

    An analytical electron microscope study is presented on carbonaceous material in two chondritic porous aggregates, W7029* A and W7010* A2, from the Johnson Space Center Cosmic Dust Collection. The finding of well-ordered carbon-2H (lonsdaleite) in the two aggregates suggests that a record of hydrocarbon carbonization may be preserved in these materials. This carbon is a metastable phase resulting from hydrous pyrolysis below 300-350 0 C and may be a precursor to poorly graphitized carbons in primitive extra terrestrial materials. (UK)

  7. Formation of long carbon chain molecules during laser vaporization of graphite

    International Nuclear Information System (INIS)

    Heath, J.R.; Zhang, Q.; O'Brien, S.C.; Curl, R.F.; Kroto, H.W.; Smalley, R.E.

    1987-01-01

    Graphite is laser vaporized into a He carrier gas containing various simple molecules such as H 2 , H 2 O, NH 3 , and CH 3 CN, supersonically expanded, and skimmed into a molecular beam, and the beam is interrogated by photoionization time-of-flight mass spectrometry. Without added reactants in the He carrier gas, C/sub n/ species up to n = 130 are readily observed. Two distributions separated at about n = 40 appear to be present with the low n species the focus of this work. In the presence of added reagents, new species appear as a result of reaction. These are satisfactorily explained on the basis that a significant proportion of the C/sub n/ species initially formed are reactive radicals with linear carbon chain structures which can readily add H, N, or CN at the ends to form relatively stable polyynes or cyanopolyynes. Some of the cyanopolyynes detected have also been observed in the interstellar medium, and circumstellar carbon condensation processes in the atmospheres of carbon-rich stars similar to those studied here are suggested as possible synthetic sources

  8. Growth dynamics of carbon-metal particles and nanotubes synthesized by CO2 laser vaporization

    Science.gov (United States)

    Kokai, F.; Takahashi, K.; Yudasaka, M.; Iijima, S.

    To study the growth of carbon-Co/Ni particles and single-wall carbon nanotubes (SWNTs) by 20 ms CO2 laser-pulse irradiation of a graphite-Co/Ni (1.2 at.%) target in an Ar gas atmosphere (600 Torr), we used emission imaging spectroscopy and shadowgraphy with a temporal resolution of 1.67 ms. Wavelength-selected emission images showed that C2 emission was strong in the region close to the target (within 2 cm), while for the same region the blackbody radiation from the large clusters or particles increased with increasing distance from the target. Shadowgraph images showed that the viscous flow of carbon and metal species formed a mushroom or a turbulent cloud spreading slowly into the Ar atmosphere, indicating that particles and SWNTs continued to grow as the ejected material cooled. In addition, emission imaging spectroscopy at 1200 °C showed that C2 and hot clusters and particles with higher emission intensities were distributed over much wider areas. We discuss the growth dynamics of the particles and SWNTs through the interaction of the ambient Ar with the carbon and metal species released from the target by the laser pulse.

  9. Rheological and electrical properties of hybrid nanocomposites of epoxy resins filled with graphite nanoplatelets and carbon black.

    Science.gov (United States)

    Truong, Quang-Trung; Lee, Seon-Suk; Lee, Dai-Soo

    2011-02-01

    Graphite nanoplatelets (GNP) were prepared by microwave irradiation of natural graphites intercalated with ferric chloride in nitromethane (GIC). Intercalated structure of GIC was confirmed by X-ray diffraction patterns. SEM images of GIC after microwave irradiation showed the exfoliation of GIC, the formation of GNPs. Hybrid nanocomposites of bisphenol-A type epoxy resins filled with GNP and a conductive carbon black (CB) were prepared and rheological and electrical properties of the nanocomposites were investigated. Viscosity and electrical surface resistivity of the nanocomposites showed minima at certain mixtures of GNP and CB in the epoxy resins.

  10. Amorphous calcium carbonate particles form coral skeletons

    Science.gov (United States)

    Mass, Tali; Giuffre, Anthony J.; Sun, Chang-Yu; Stifler, Cayla A.; Frazier, Matthew J.; Neder, Maayan; Tamura, Nobumichi; Stan, Camelia V.; Marcus, Matthew A.; Gilbert, Pupa U. P. A.

    2017-09-01

    Do corals form their skeletons by precipitation from solution or by attachment of amorphous precursor particles as observed in other minerals and biominerals? The classical model assumes precipitation in contrast with observed “vital effects,” that is, deviations from elemental and isotopic compositions at thermodynamic equilibrium. Here, we show direct spectromicroscopy evidence in Stylophora pistillata corals that two amorphous precursors exist, one hydrated and one anhydrous amorphous calcium carbonate (ACC); that these are formed in the tissue as 400-nm particles; and that they attach to the surface of coral skeletons, remain amorphous for hours, and finally, crystallize into aragonite (CaCO3). We show in both coral and synthetic aragonite spherulites that crystal growth by attachment of ACC particles is more than 100 times faster than ion-by-ion growth from solution. Fast growth provides a distinct physiological advantage to corals in the rigors of the reef, a crowded and fiercely competitive ecosystem. Corals are affected by warming-induced bleaching and postmortem dissolution, but the finding here that ACC particles are formed inside tissue may make coral skeleton formation less susceptible to ocean acidification than previously assumed. If this is how other corals form their skeletons, perhaps this is how a few corals survived past CO2 increases, such as the Paleocene-Eocene Thermal Maximum that occurred 56 Mya.

  11. Brazing graphite to graphite

    International Nuclear Information System (INIS)

    Peterson, G.R.

    1976-01-01

    Graphite is joined to graphite by employing both fine molybdenum powder as the brazing material and an annealing step that together produce a virtually metal-free joint exhibiting properties similar to those found in the parent graphite. Molybdenum powder is placed between the faying surfaces of two graphite parts and melted to form molybdenum carbide. The joint area is thereafter subjected to an annealing operation which diffuses the carbide away from the joint and into the graphite parts. Graphite dissolved by the dispersed molybdenum carbide precipitates into the joint area, replacing the molybdenum carbide to provide a joint of graphite

  12. Hard carbon coated nano-Si/graphite composite as a high performance anode for Li-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Jeong, Sookyung; Li, Xiaolin; Zheng, Jianming; Yan, Pengfei; Cao, Ruiguo; Jung, Hee Joon; Wang, Chong M.; Liu, Jun; Zhang, Jiguang

    2016-08-27

    With the ever increasing demands on Li-ion batteries with higher energy densities, alternative anode with higher reversible capacity is required to replace the conventional graphite anode. Here, we demonstrate a cost-effective hydrothermal-carbonization approach to prepare the hard carbon coated nano-Si/graphite (HC-nSi/G) composite as a high performance anode for Li-ion batteries. In this hierarchical structured composite, the hard carbon coating layer not only provides an efficient pathway for electron transfer, but also alleviates the volume variation of silicon during charge/discharge processes. The HC-nSi/G composite electrode shows excellent electrochemical performances including a high specific capacity of 878.6 mAh g-1 based on the total weight of composite, good rate performance and a decent cycling stability, which is promising for practical applications.

  13. Further investigation on boric acid catalytic graphitization of polyacrylonitrile carbon fibers: Mechanism and mechanical properties

    International Nuclear Information System (INIS)

    Wen, Ya; Lu, Yonggen; Xiao, Hao; Qin, Xianying

    2012-01-01

    Highlights: ► The modulus of carbon fiber was improved by boric acid at the temperature range of 1500–2900 °C. ► 2300 °C is a key temperature degree from which the boron began to benefit fiber strength. ► The fiber strength was affected by the boron reaction and related to the boron states. -- Abstract: Catalytic graphitization of polyacrylonitrile based carbon fibers by boric acid doping was studied and the dependence of fiber tensile strength on the boron content and temperature was discussed. It was found that there existed a key temperature point for the boron to take effect. When the fibers were modified with 7.0 wt.% boric acid solution, with increasing temperature, the tensile strength was lower than that of the unmodified ones below 2300 °C, but a reverse thing happened above 2300 °C. Moreover, when being heated at 2500 °C, the modified fibers showed an increasing tensile modulus and strength with increasing boron content till maximums of 404 GPa and 2.46 GPa, 26% and 16% higher than those of unmodified ones. The mechanical properties of the fibers were affected by the interaction of carbon and boron, and also related with boron states. The decomposition of boron acid and its interaction with carbon brought defects on fiber surface, degrading the mechanical properties below 1300 °C. With further heat treatment, the boron diffused into the fibers and divided into two states: substitutional and interstitial. At a temperature over 2300 °C with an appreciate boron content, the substitutional would be formed predominantly, which removed the structural defects and relaxed the distortions, so as to benefit the mechanical properties.

  14. Facile fabrication of ordered mesoporous graphitic carbon nitride for RhB photocatalytic degradation

    Energy Technology Data Exchange (ETDEWEB)

    Luo, Lei; Zhang, Anfeng [State Key Laboratory of Fine Chemicals, PSU-DUT Joint Center for Energy Research, School of Chemical Engineering, Dalian University of Technology, Dalian 116024 (China); Janik, Michael J. [EMS Energy Institute, PSU-DUT Joint Center for Energy Research and Department of Energy & Mineral Engineering, Pennsylvania State University, University Park, PA 16802 (United States); Li, Keyan [State Key Laboratory of Fine Chemicals, PSU-DUT Joint Center for Energy Research, School of Chemical Engineering, Dalian University of Technology, Dalian 116024 (China); Song, Chunshan [State Key Laboratory of Fine Chemicals, PSU-DUT Joint Center for Energy Research, School of Chemical Engineering, Dalian University of Technology, Dalian 116024 (China); EMS Energy Institute, PSU-DUT Joint Center for Energy Research and Department of Energy & Mineral Engineering, Pennsylvania State University, University Park, PA 16802 (United States); Guo, Xinwen, E-mail: guoxw@dlut.edu.cn [State Key Laboratory of Fine Chemicals, PSU-DUT Joint Center for Energy Research, School of Chemical Engineering, Dalian University of Technology, Dalian 116024 (China)

    2017-02-28

    Highlights: • Ordered mesoporous graphitic carbon nitrides with S{sub BET} = 279.3 m{sup 2}/g were prepared. • Enhanced photocatalytic activity and reusability were presented. • Improved S{sub BET} and charge carrier separation efficiency contribute to the activity. - Abstract: Ordered mesoporous graphitic carbon nitrides were prepared by directly condensing the uniform mixtures of melamine and KIT-6. After removal of the KIT-6 sacrificial template, the carbon nitrides were characterized with TEM, N{sub 2} physical adsorption, XRD, FT-IR, XPS, UV–vis and PL spectrometries, and tested for their RhB photocatalytic degradation activity. Together, these characterizations confirmed the as-prepared tunable mesoporous materials with enhanced charge separation efficiency and superior photocatalytic performance. Compared with a conventional bulk g-C{sub 3}N{sub 4}, ordered mesoporous g-C{sub 3}N{sub 4} exhibits a larger specific surface area of 279.3 m{sup 2}/g and a pore size distribution about 4.0 nm and 13.0 nm. Meanwhile, the reduced bandgap energy of 2.77 eV and lower photogenerated electron-hole pair recombination frequency were evidenced by UV–Vis and PL spectra. The RhB photocatalytic degradation activity maximizes with a mass ratio of KIT-6/melamine of 80% (KCN80), and the kinetic constant reaches 0.0760 min{sup −1} which is 16 times higher than that of the bulk sample. Reusability of KCN80 was demonstrated by a lack of evident deactivation after three consecutive reaction periods. The direct condensation of the KIT-6 and melamine mixture does not require pre-casting of the precursor into the pore system of the templates. Owing to its high product yield, improved S{sub BET}, reduced bandgap energy and limited charge recombination, the facile-prepared ordered mesoporous g-C{sub 3}N{sub 4} is a practical candidate for further modification.

  15. Understanding the crack formation of graphite particles in cycled commercial lithium-ion batteries by focused ion beam - scanning electron microscopy

    Science.gov (United States)

    Lin, Na; Jia, Zhe; Wang, Zhihui; Zhao, Hui; Ai, Guo; Song, Xiangyun; Bai, Ying; Battaglia, Vincent; Sun, Chengdong; Qiao, Juan; Wu, Kai; Liu, Gao

    2017-10-01

    The structure degradation of commercial Lithium-ion battery (LIB) graphite anodes with different cycling numbers and charge rates was investigated by focused ion beam (FIB) and scanning electron microscopy (SEM). The cross-section image of graphite anode by FIB milling shows that cracks, resulted in the volume expansion of graphite electrode during long-term cycling, were formed in parallel with the current collector. The crack occurs in the bulk of graphite particles near the lithium insertion surface, which might derive from the stress induced during lithiation and de-lithiation cycles. Subsequently, crack takes place along grain boundaries of the polycrystalline graphite, but only in the direction parallel with the current collector. Furthermore, fast charge graphite electrodes are more prone to form cracks since the tensile strength of graphite is more likely to be surpassed at higher charge rates. Therefore, for LIBs long-term or high charge rate applications, the tensile strength of graphite anode should be taken into account.

  16. Graphitized Carbon: A Promising Stable Cathode Catalyst Support Material for Long Term PEMFC Applications.

    Science.gov (United States)

    Mohanta, Paritosh Kumar; Regnet, Fabian; Jörissen, Ludwig

    2018-05-28

    Stability of cathode catalyst support material is one of the big challenges of polymer electrolyte membrane fuel cells (PEMFC) for long term applications. Traditional carbon black (CB) supports are not stable enough to prevent oxidation to CO₂ under fuel cell operating conditions. The feasibility of a graphitized carbon (GC) as a cathode catalyst support for low temperature PEMFC is investigated herein. GC and CB supported Pt electrocatalysts were prepared via an already developed polyol process. The physical characterization of the prepared catalysts was performed using transmission electron microscope (TEM), X-ray Powder Diffraction (XRD) and inductively coupled plasma optical emission spectrometry (ICP-OES) analysis, and their electrochemical characterizations were conducted via cyclic voltammetry(CV), rotating disk electrode (RDE) and potential cycling, and eventually, the catalysts were processed using membrane electrode assemblies (MEA) for single cell performance tests. Electrochemical impedance spectroscopy (EIS) and scanning electrochemical microscopy (SEM) have been used as MEA diagonostic tools. GC showed superior stability over CB in acid electrolyte under potential conditions. Single cell MEA performance of the GC-supported catalyst is comparable with the CB-supported catalyst. A correlation of MEA performance of the supported catalysts of different Brunauer⁻Emmett⁻Teller (BET) surface areas with the ionomer content was also established. GC was identified as a promising candidate for catalyst support in terms of both of the stability and the performance of fuel cell.

  17. Defect induced tuning of photoluminescence property in graphitic carbon nitride nanosheets through synthesis conditions

    Energy Technology Data Exchange (ETDEWEB)

    Das, D. [School of Materials Science and Nanotechnology, Jadavpur University, Kolkata 700032 (India); Banerjee, D., E-mail: nilju82@gmail.com [School of Materials Science Engineering Indian Institute of Engineering Science and Technology, Shibpur, Howrah (India); Pahari, D. [School of Materials Science Engineering Indian Institute of Engineering Science and Technology, Shibpur, Howrah (India); Ghorai, U.K. [Department of Industrial Chemistry & Swami Vivekananda Research centre, Ramakrishna Mission Vidyamandira, Belur Math, Howrah 711202 (India); Sarkar, S.; Das, N.S. [School of Materials Science and Nanotechnology, Jadavpur University, Kolkata 700032 (India); Chattopadhyay, K.K., E-mail: kalyan_chattopadhyay@yahoo.com [School of Materials Science and Nanotechnology, Jadavpur University, Kolkata 700032 (India); Thin Film and Nanoscience Laboratory, Department of Physics, Jadavpur University, Kolkata 700032 (India)

    2017-05-15

    Synthesis of layered sheet like graphitic carbon nitride by pyrolysis of urea at different temperatures has been reported. The proper phase formation has been confirmed by X-ray diffraction study whereas field emission scanning and transmission electron microscope characterized the morphology of the material. Fourier transform infrared and Raman spectroscopy revealed the presence of different bonds in the sample. Thermal gravimetric analysis has been used to study the thermal stability of the material. Energy dispersive X-ray analysis further revealed the elemental composition of carbon and nitrogen in a proper stoichiometric ratio. Excitation dependent photoluminescence spectra of the as prepared samples have been studied in detail. It has been shown that synthesis condition can tailor the amount of defects present in the synthesized samples that in turn can change the photoluminescence properties of the material. The fluorescence spectra of the as prepared samples have been used to detect copper ions present in the sample. It has also been shown that the presence of defects which is mainly N-H functional groups can change the decay characteristics of the carrier in these samples which in turn changes the PL spectra.

  18. Electrical Properties of Cement-Based Composites with Carbon Nanotubes, Graphene, and Graphite Nanofibers.

    Science.gov (United States)

    Yoo, Doo-Yeol; You, Ilhwan; Lee, Seung-Jung

    2017-05-08

    This study was conducted to evaluate the effect of the carbon-based nanomaterial type on the electrical properties of cement paste. Three different nanomaterials, multi-walled carbon nanotubes (MWCNTs), graphite nanofibers (GNFs), and graphene (G), were incorporated into the cement paste at a volume fraction of 1%. The self-sensing capacity of the cement composites was also investigated by comparing the compressive stress/strain behaviors by evaluating the fractional change of resistivity (FCR). The electrical resistivity of the plain cement paste was slightly reduced by adding 1 vol % GNFs and G, whereas a significant decrease of the resistivity was achieved by adding 1 vol % MWCNTs. At an identical volume fraction of 1%, the composites with MWCNTs provided the best self-sensing capacity with insignificant noise, followed by the composites containing GNFs and G. Therefore, the addition of MWCNTs was considered to be the most effective to improve the self-sensing capacity of the cement paste. Finally, the composites with 1 vol % MWCNTs exhibited a gauge factor of 113.2, which is much higher than commercially available strain gauges.

  19. Electrical Properties of Cement-Based Composites with Carbon Nanotubes, Graphene, and Graphite Nanofibers

    Directory of Open Access Journals (Sweden)

    Doo-Yeol Yoo

    2017-05-01

    Full Text Available This study was conducted to evaluate the effect of the carbon-based nanomaterial type on the electrical properties of cement paste. Three different nanomaterials, multi-walled carbon nanotubes (MWCNTs, graphite nanofibers (GNFs, and graphene (G, were incorporated into the cement paste at a volume fraction of 1%. The self-sensing capacity of the cement composites was also investigated by comparing the compressive stress/strain behaviors by evaluating the fractional change of resistivity (FCR. The electrical resistivity of the plain cement paste was slightly reduced by adding 1 vol % GNFs and G, whereas a significant decrease of the resistivity was achieved by adding 1 vol % MWCNTs. At an identical volume fraction of 1%, the composites with MWCNTs provided the best self-sensing capacity with insignificant noise, followed by the composites containing GNFs and G. Therefore, the addition of MWCNTs was considered to be the most effective to improve the self-sensing capacity of the cement paste. Finally, the composites with 1 vol % MWCNTs exhibited a gauge factor of 113.2, which is much higher than commercially available strain gauges.

  20. The Effect of Hydrogen on the Mechanical Properties of Cast Irons and ADI with Various Carbon Equivalent and Graphite Morphology

    International Nuclear Information System (INIS)

    Cho, Yong Gi; Lee, Kyung Sub

    1989-01-01

    The effect of hydrogen on the mechanical properties of cast irons, flake, CV graphite cast iron ductile iron and ADI have been investigated. The effects of various carbon equivalent, graphite morphology and matrix have been analyzed to determine the predominant factor which influences on the hydrogen embrittlement. The effect of various carbon equivalent on the embrittlement was little in the similar graphite morphology. The embrittlement of ferrite matrix changed by heat treatment was less than that of pearlite matrix. In the case of ADI, the tendency of hydrogen embrittlement of lower bainite matrix was less remarkable than that of upper banite matrix. As the result of hydrogen charging, the tendency of interface decohesion between matrix-graphite was increased in flake G.C.I., and the trend from ductile fracture mode to brittle fracture mode was observed in CV G.C.I and ductile iron. Lower bainite in ADI showed the ductile fracture mode. Hydrogen solubility of lower bainite was higher than that of upper bainite

  1. Transformation of Graphitic and Amorphous Carbon Dust to Complex Organic Molecules in a Massive Carbon Cycle in Protostellar Nebulae

    Science.gov (United States)

    Nuth, Joseph A., III; Johnson, Natasha M.

    2012-01-01

    More than 95% of silicate minerals and other oxides found in meteorites were melted, or vaporized and recondensed in the Solar Nebula prior to their incorporation into meteorite parent bodies. Gravitational accretion energy and heating via radioactive decay further transformed oxide minerals accreted into planetesimals. In such an oxygen-rich environment the carbonaceous dust that fell into the nebula as an intimate mixture with oxide grains should have been almost completely converted to CO. While some pre-collapse, molecular-cloud carbonaceous dust does survive, much in the same manner as do pre-solar oxide grains, such materials constitute only a few percent of meteoritic carbon and are clearly distinguished by elevated D/H, N-15/N-16, C-13/C-12 ratios or noble gas patterns. Carbonaceous Dust in Meteorites: We argue that nearly all of the carbon in meteorites was synthesized in the Solar Nebula from CO and that this CO was generated by the reaction of carbonaceous dust with solid oxides, water or OH. It is probable that some fraction of carbonaceous dust that is newly synthesized in the Solar Nebula is also converted back into CO by additional thermal processing. CO processing might occur on grains in the outer nebula through irradiation of CO-containing ice coatings or in the inner nebula via Fischer-Tropsch type (FTT) reactions on grain surfaces. Large-scale transport of both gaseous reaction products and dust from the inner nebula out to regions where comets formed would spread newly formed carbonaceous materials throughout the solar nebula. Formation of Organic Carbon: Carbon dust in the ISM might easily be described as inorganic graphite or amorphous carbon, with relatively low structural abundances of H, N, O and S . Products of FTT reactions or organics produced via irradiation of icy grains contain abundant aromatic and aliphatic hydrocarbons. aldehydes, keytones, acids, amines and amides.. The net result of the massive nebular carbon cycle is to convert

  2. From Core to Capture: Graphite Management by Gasification and Carbon Capture & Storage (CCS)

    International Nuclear Information System (INIS)

    Goodwin, J.; Bradbury, D.; Black, S.; Tomlinson, T.; Livesey, B.; Robinson, J.; Lindberg, M.; Newton, C.; Jones, A.; Wickham, A.

    2016-01-01

    Radioactive graphite waste arises principally from the moderators of graphite/gas-cooled reactors at the end of life of the reactors. Commercial power producing reactors (for example, Magnox, AGR and RBMK) have graphite moderators, each containing several thousand tonnes of graphite, with the UK having the largest inventory of over 90,000 tonnes. Additionally, there are smaller quantities of graphite arising from other sources such as fuel element components. The current long term strategy for management of reactor graphite in the UK is for these wastes to be conditioned for disposal followed by transfer to a geological disposal facility (GDF). With this baseline position, these wastes will account for about 30% of the ILW inventory in a GDF. As the volume of the graphite waste is so large, it is not currently economic to retrieve and process the graphite in advance of the availability of a geological disposal facility. Recent work by the NDA has ascribed a much smaller “incremental” volume of 2% due to graphite, calculated on the basis that the GDF has to be a certain size anyway in order to dissipate the decay heat from high level waste

  3. Carbon Fiber Damage in Particle Beam

    CERN Document Server

    Dehning, B; Kroyer, T; Meyer, M; Sapinski, M

    2011-01-01

    Carbon fibers are commonly used as moving targets in beam wire scanners. The heating of the fiber due to energy loss of the particles travelling through is simulated with Geant4. The heating induced by the beam electromagnetic field is estimated with ANSYS. The heat transfer and sublimation processes are modelled. Due to the model nonlinearity, a numerical approach based on discretization of the wire movement is used to solve it for particular beams. Radiation damage to the fiber is estimated with SRIM. The model is tested with available SPS and LEP data and a dedicated damage test on the SPS beam is performed followed by a post-mortem analysis of the wire remnants. Predictions for the LHC beams are made.

  4. Impedance aspect of charge storage at graphite and glassy carbon electrodes in potassium hexacyanoferrate (II redox active electrolyte

    Directory of Open Access Journals (Sweden)

    Katja Magdić

    2016-04-01

    Full Text Available Different types of charge storage mechanisms at unmodified graphite vs. glassy carbon electrodes in acid sulphate supporting solution containing potassium hexacyanoferrate (II redox active electrolyte, have been revealed by electrochemical impedance spectroscopy and supported by cyclic voltammetry experiments. Reversible charge transfer of Fe(CN63-/4- redox reaction detected by assessment of CVs of glassy carbon electrode, is in impedance spectra indicated by presence of bulk diffusion impedance and constant double-layer/pseudocapacitive electrode impedance compared to that measured in the pure supporting electrolyte. Some surface retention of redox species detected by assessment of CVs of graphite electrode is in impedance spectra indicated by diffusion impedance coupled in this case by diminishing of double-layer/pseudo­capacitive impedance compared to that measured in the pure supporting electrolyte. This phenomenon is ascribed to contribution of additional pseudocapacitive impedance generated by redox reaction of species confined at the electrode surface.

  5. Rapid synthesis of graphitic carbon nitride powders by metathesis reaction between CaCN2 and C2Cl6

    International Nuclear Information System (INIS)

    Pang Linlin; Bi Jianqiang; Bai Yujun; Qi Yongxin; Zhu Huiling; Wang Chengguo; Wu Jiwei; Lu Chengwei

    2008-01-01

    Carbon nitride powders were rapidly synthesized at low temperature via the chemical metathesis reaction between CaCN 2 and C 2 Cl 6 . X-ray diffraction results confirm the formation of crystalline graphitic carbon nitride. Besides the dominant morphology of nanoparticles, flakes, nanorods, hollow and solid spheres can be observed by transmission electron microscopy. The absorption peaks of C-N, C=N and s-triazine rings, as well as the absence of C≡N peak in the infrared spectra, further verify the formation of graphite-like sp 2 -bonded structure with planar networks. Elemental analysis gives an atomic ratio of N/C around 0.3. X-ray photoelectron spectra exhibit the existence of chemical bonding between C and N

  6. Metal-functionalized single-walled graphitic carbon nitride nanotubes: a first-principles study on magnetic property

    Directory of Open Access Journals (Sweden)

    Shenoy Vivek

    2011-01-01

    Full Text Available Abstract The magnetic properties of metal-functionalized graphitic carbon nitride nanotubes were investigated based on first-principles calculations. The graphitic carbon nitride nanotube can be either ferromagnetic or antiferromagnetic by functionalizing with different metal atoms. The W- and Ti-functionalized nanotubes are ferromagnetic, which are attributed to carrier-mediated interactions because of the coupling between the spin-polarized d and p electrons and the formation of the impurity bands close to the band edges. However, Cr-, Mn-, Co-, and Ni-functionalized nanotubes are antiferromagnetic because of the anti-alignment of the magnetic moments between neighboring metal atoms. The functionalized nanotubes may be used in spintronics and hydrogen storage.

  7. Wear Characteristics of Hybrid Composites Based on Za27 Alloy Reinforced With Silicon Carbide and Graphite Particles

    Directory of Open Access Journals (Sweden)

    S. Mitrović

    2014-06-01

    Full Text Available The paper presents the wear characteristics of a hybrid composite based on zinc-aluminium ZA27 alloy, reinforced with silicon-carbide and graphite particles. The tested sample contains 5 vol.% of SiC and 3 vol.% Gr particles. Compocasting technique has been used to prepare the samples. The experiments were performed on a “block-on-disc” tribometer under conditions of dry sliding. The wear volumes of the alloy and the composite were determined by varying the normal loads and sliding speeds. The paper contains the procedure for preparation of sample composites and microstructure of the composite material and the base ZA27 alloy. The wear surface of the composite material was examined using the scanning electronic microscope (SEM and energy dispersive spectrometry (EDS. Conclusions were obtained based on the observed impact of the sliding speed, normal load and sliding distance on tribological behaviour of the observed composite.

  8. Growth of Hexagonal Columnar Nanograin Structured SiC Thin Films on Silicon Substrates with Graphene–Graphitic Carbon Nanoflakes Templates from Solid Carbon Sources

    Directory of Open Access Journals (Sweden)

    Wanshun Zhao

    2013-04-01

    Full Text Available We report a new method for growing hexagonal columnar nanograin structured silicon carbide (SiC thin films on silicon substrates by using graphene–graphitic carbon nanoflakes (GGNs templates from solid carbon sources. The growth was carried out in a conventional low pressure chemical vapor deposition system (LPCVD. The GGNs are small plates with lateral sizes of around 100 nm and overlap each other, and are made up of nanosized multilayer graphene and graphitic carbon matrix (GCM. Long and straight SiC nanograins with hexagonal shapes, and with lateral sizes of around 200–400 nm are synthesized on the GGNs, which form compact SiC thin films.

  9. High Resolution Angle Resolved Photoemission Studies on Quasi-Particle Dynamics in Graphite

    Energy Technology Data Exchange (ETDEWEB)

    Leem, C.S.

    2010-06-02

    We obtained the spectral function of the graphite H point using high resolution angle resolved photoelectron spectroscopy (ARPES). The extracted width of the spectral function (inverse of the photo-hole lifetime) near the H point is approximately proportional to the energy as expected from the linearly increasing density of states (DOS) near the Fermi energy. This is well accounted by our electron-phonon coupling theory considering the peculiar electronic DOS near the Fermi level. And we also investigated the temperature dependence of the peak widths both experimentally and theoretically. The upper bound for the electron-phonon coupling parameter is 0.23, nearly the same value as previously reported at the K point. Our analysis of temperature dependent ARPES data at K shows that the energy of phonon mode of graphite has much higher energy scale than 125K which is dominant in electron-phonon coupling.

  10. Facile synthesis of nanorod-type graphitic carbon nitride/Fe2O3 composite with enhanced photocatalytic performance

    International Nuclear Information System (INIS)

    Wang, Jiangpeng; Li, Changqing; Cong, Jingkun; Liu, Ziwei; Zhang, Hanzhuo; Liang, Mei; Gao, Junkuo; Wang, Shunli; Yao, Juming

    2016-01-01

    Here we report a facile synthesis of nanorod-type graphitic carbon nitride/Fe 2 O 3 composite (Fe 2 O 3 -g-C 3 N 4 ) by using Fe-melamine supramolecular framework as precursor. The chemical and optical properties of the nanocomposites are well-characterized. The Fe 2 O 3 -g-C 3 N 4 nanocomposite demonstrated excellent photocatalytic activities under visible light due to the efficient utilization of sunlight and the construction of Z-scheme electron transfer pathway. The results indicated that it could be a promising approach for the preparation of efficient g-C 3 N 4 nanocomposites photocatalysts by using metal-melamine supramolecular framework as precursors. - Graphical abstract: Nanorod-type graphitic carbon nitride/Fe 2 O 3 composite (Fe 2 O 3 -g-C 3 N 4 ) was synthesized by using Fe-melamine supramolecular framework as precursor. The Fe 2 O 3 -g-C 3 N 4 nanocomposite demonstrated excellent photocatalytic activities under visible light. Display Omitted - Highlights: • Nanorod-type graphitic carbon nitride/Fe 2 O 3 composite (Fe 2 O 3 -g-C 3 N 4 ) was synthesized. • Fe 2 O 3 -g-C 3 N 4 showed strong optical absorption in the visible-light region. • The Fe 2 O 3 -g-C 3 N 4 nanocomposite demonstrated excellent photocatalytic activities.

  11. Hydrogen storage in carbon nanofibres for defence applications : the influence of growth parameters on graphitic quality and storage capacity

    Energy Technology Data Exchange (ETDEWEB)

    Turpin, M.; Mellor, I. [Morgan Materials Technology Ltd., Worcestershire (United Kingdom); Shatwell, R.A.; Prentice, C. [QinetiQ Farnborough, Hampshire (United Kingdom); Browning, D.J. [QinetiQ Haslar, Gosport, Hampshire (United Kingdom); Lakeman, J.B. [Dstl Portsdown, Cosham, Hampshire (United Kingdom); Gerrard, M.L.; Mortimer, R.J. [Loughborough Univ. of Technology, Loughborough, Leicestershire (United Kingdom). Dept. of Chemistry

    2002-07-01

    The results of a study on hydrogen storage in carbon or graphite nanofibres (GNFs) were presented. Graphite nanofibres used in hydrogen storage treatment were synthesized at 600 degrees C by passing ethylene over a series of Fe:Ni:Cu catalysts. It was shown that while hydrogen storage can occur for up to 6.5 wt per cent, this number can vary depending on the method of preparation and heat treatment. Hydrogen storage requires an effective method, such as Raman spectroscopy, for characterising the product. Transmission Electron Microscopy also helped in the optimisation of the process to produce highly graphitic nanofibres. The main role of heat treatment is to remove carbon from the surface of the GNFs, allowing access to the graphene planes. Hydrogen storage experiments were conducted at 120 bar, using a bespoke apparatus with differential pressure. A detailed error analysis was performed on the uptake measurement system. The rate of penetration by hydrogen into a layer of carbon capping graphene planes is found to be negligible. It is concluded that hydrogen adsorption will not be observed unless the layer is removed. A maximum uptake of 4.2 wt per cent was achieved, increasing to more than 6.5 wt per cent following heat treatment at 1000 degrees C. 32 refs., 3 tabs., 7 figs.

  12. Controlling wear failure of graphite-like carbon film in aqueous environment: Two feasible approaches

    International Nuclear Information System (INIS)

    Wang Yongxin; Wang Liping; Xue Qunji

    2011-01-01

    Friction and wear behaviors of graphite-like carbon (GLC) films in aqueous environment were investigated by a reciprocating sliding tribo-meter with ball-on-disc contact. Film structures and wear scars were studied by scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) and a non-contact 3D surface profiler. A comprehensive wear model of the GLC film in aqueous environment was established, and two feasible approaches to control critical factor to the corresponding wear failure were discussed. Results showed that wear loss of GLC films in aqueous environment was characterized by micro-plough and local delamination. Due to the significant material loss, local delamination of films was critical to wear failure of GLC film in aqueous environment if the film was not prepared properly. The initiation and propagation of micro-cracks within whole films closely related to the occurrence of the films delamination from the interface between interlayer and substrate. The increase of film density by adjusting the deposition condition would significantly reduce the film delamination from substrate, meanwhile, fabricating a proper interlayer between substrate and GLC films to prevent the penetration of water molecules into the interface between interlayer and substrate could effectively eliminate the delamination.

  13. Heavily Graphitic-Nitrogen Self-doped High-porosity Carbon for the Electrocatalysis of Oxygen Reduction Reaction

    Science.gov (United States)

    Feng, Tong; Liao, Wenli; Li, Zhongbin; Sun, Lingtao; Shi, Dongping; Guo, Chaozhong; Huang, Yu; Wang, Yi; Cheng, Jing; Li, Yanrong; Diao, Qizhi

    2017-11-01

    Large-scale production of active and stable porous carbon catalysts for oxygen reduction reaction (ORR) from protein-rich biomass became a hot topic in fuel cell technology. Here, we report a facile strategy for synthesis of nitrogen-doped porous nanocarbons by means of a simple two-step pyrolysis process combined with the activation of zinc chloride and acid-treatment process, in which kidney bean via low-temperature carbonization was preferentially adopted as the only carbon-nitrogen sources. The results show that this carbon material exhibits excellent ORR electrocatalytic activity, and higher durability and methanol-tolerant property compared to the state-of-the-art Pt/C catalyst for the ORR, which can be mainly attributed to high graphitic-nitrogen content, high specific surface area, and porous characteristics. Our results can encourage the synthesis of high-performance carbon-based ORR electrocatalysts derived from widely-existed natural biomass.

  14. Stable Carbon Isotope Ratio (δ13C Measurement of Graphite Using EA-IRMS System

    Directory of Open Access Journals (Sweden)

    Andrius Garbaras

    2015-06-01

    Full Text Available δ13C values in non-irradiated natural graphite were measured. The measurements were carried out using an elemental analyzer combined with stable isotope ratio mass spectrometer (EA-IRMS. The samples were prepared with ground and non-ground graphite, the part of which was mixed with Mg (ClO42. The best combustion of graphite in the oxidation furnace of the elemental analyzer was achieved when the amount of pulverized graphite ranged from 200 to 490 µg and the mass ratio C:Mg(ClO42 was approximately 1:10. The method for the graphite burning avoiding the isotope fractionation is proposed.DOI: http://dx.doi.org/10.5755/j01.ms.21.2.6873

  15. A general salt-templating method to fabricate vertically aligned graphitic carbon nanosheets and their metal carbide hybrids for superior lithium ion batteries and water splitting.

    Science.gov (United States)

    Zhu, Jixin; Sakaushi, Ken; Clavel, Guylhaine; Shalom, Menny; Antonietti, Markus; Fellinger, Tim-Patrick

    2015-04-29

    The synthesis of vertically aligned functional graphitic carbon nanosheets (CNS) is challenging. Herein, we demonstrate a general approach for the fabrication of vertically aligned CNS and metal carbide@CNS composites via a facile salt templating induced self-assembly. The resulting vertically aligned CNS and metal carbide@CNS structures possess ultrathin walls, good electrical conductivity, strong adhesion, excellent structural robustness, and small particle size. In electrochemical energy conversion and storage such unique features are favorable for providing efficient mass transport as well as a large and accessible electroactive surface. The materials were tested as electrodes in a lithium ion battery and in electrochemical water splitting. The vertically aligned nanosheets exhibit remarkable lithium ion storage properties and, concurrently, excellent properties as electrocatalysts for hydrogen evolution.

  16. High-resolution transmission electron microscopy studies of graphite materials prepared by high-temperature treatment of unburned carbon concentrates from combustion fly ashes

    Energy Technology Data Exchange (ETDEWEB)

    Miguel Cabielles; Jean-Nol Rouzaud; Ana B. Garcia [Instituto Nacional del Carbn (INCAR), Oviedo (Spain)

    2009-01-15

    High-resolution transmission electron microscopy (HRTEM) has been used in this work to study the microstructural (structure and microtexture) changes occurring during the high-temperature treatment of the unburned carbon concentrates from coal combustion fly ashes. Emphasis was placed on two aspects: (i) the development of graphitic carbon structures and (ii) the disordered carbon forms remaining in the graphitized samples. In addition, by coupling HRTEM with energy-dispersive spectroscopy, the transformations with the temperature of the inorganic matter (mainly iron- and silicon-based phases) of the unburned carbon concentrates were evidenced. The HRTEM results were compared to the averaged structural order of the materials as evaluated by X-ray diffraction (XRD) and Raman spectroscopy. As indicated by XRD and Raman parameters, more-ordered materials were obtained from the unburned carbon concentrates with higher mineral/inorganic matter, thus inferring the catalytic effect of some of their components. However, the average character of the information provided by these instrumental techniques seems to be inconclusive in discriminating between carbon structures with different degrees of order (stricto sensu graphite, graphitic, turbostratic, etc.) in a given graphitized unburned carbon. Unlike XRD and Raman, HRTEM is a useful tool for imaging directly the profile of the polyaromatic layers (graphene planes), thus allowing the sample heterogeneity to be looked at, specifically the presence of disordered carbon phases. 49 refs., 9 figs., 3 tabs.

  17. Preparation of pyrolytic carbon coating on graphite for inhibiting liquid fluoride salt and Xe135 penetration for molten salt breeder reactor

    International Nuclear Information System (INIS)

    Song, Jinliang; Zhao, Yanling; He, Xiujie; Zhang, Baoliang; Xu, Li; He, Zhoutong; Zhang, DongSheng; Gao, Lina; Xia, Huihao; Zhou, Xingtai; Huai, Ping; Bai, Shuo

    2015-01-01

    Highlights: • Rough laminar pyrolytic carbon coating (RLPyC) is prepared by a fixed-bed method. • The salt-infiltration into IG-110 is 13.5%, less than 0.01% of RLPyC under 1.5 atm. • The helium diffusion coefficient of RLPyC coated graphite is 2.16 × 10 −8 cm 2 /s. • The coated graphite can inhibit the liquid fluoride salt and Xe 135 penetration. - Abstract: A fixed-bed deposition method was used to prepare rough laminar pyrolytic carbon coating (RLPyC) on graphite for inhibiting liquid fluoride salt and Xe 135 penetration during use in molten salt breeder reactor. The RLPyC coating possessed a graphitization degree of 44% and had good contact with graphite substrate. A high-pressure reactor was constructed to evaluate the molten salt infiltration in the isostatic graphite (IG-110, TOYO TANSO CO., LTD.) and RLPyC coated graphite under 1.01, 1.52, 3.04, 5.07 and 10.13 × 10 5 Pa for 12 h. Mercury injection and molten-salt infiltration experiments indicated the porosity and the salt-infiltration amount of 18.4% and 13.5 wt% under 1.52 × 10 5 Pa of IG-110, which was much less than 1.2% and 0.06 wt% under 10.13 × 10 5 Pa of the RLPyC, respectively. A vacuum device was constructed to evaluate the Xe 135 penetration in the graphite. The helium diffusion coefficient of RLPyC coated graphite was 2.16 × 10 −12 m 2 /s, much less than 1.21 × 10 −6 m 2 /s of the graphite. Thermal cycle experiment indicated the coatings possessed excellent thermal stability. The coated graphite could effectively inhibit the liquid fluoride salt and Xe 135 penetration

  18. An investigation of heat exchanger fouling in dust suspension cooling systems using graphite powder and carbon dioxide gas

    International Nuclear Information System (INIS)

    Garton, D.A.; Hawes, R.I.; Rose, P.W.

    1966-01-01

    Some experiments have been performed to study the fouling of heat exchanger surfaces where heat is being transferred from a heated fluid to a cooled surface. The fluid studied was a suspension of 4-5 microns mean diameter graphite powder in carbon dioxide gas at near atmospheric pressures. The solids loading range covered was from 5 to 30 lb. graphite/lb. carbon dioxide, and gas Reynolds numbers from 6000 to 16000. Temperature gradients across the cooler of from 20 to 120 deg. C were obtained. The heat transfer ratio is correlated to show the dependence upon the solids loading ratio of the suspension, the gas Reynolds number and the temperature gradient across the cooler. The results have demonstrated that stringent precautions are necessary to ensure complete dryness of the graphite powder and the loop flow surfaces before any quantitative fouling data can be obtained, as the presence of entrained moisture will accelerate the deposition of material on the cold walls of the heat exchanger and can result in plugging. The heat transfer coefficient showed no obvious dependency upon either the gas Reynolds number or the temperature gradient across the cooler over the range investigated. The measured heat transfer coefficient was considerably lower than that obtained when the heat is transferred from a hot wall to a cooler fluid. At a solids loading of 30 lb, graphite/lb. carbon dioxide, the heat transfer coefficient was only 50% of that for heat transfer from a heated wall. At solids loadings below 7 lb/lb., the heat transfer was less than that for a gas alone. (author)

  19. Oxidation kinetics of innovative carbon materials with respect to severe air ingress accidents in HTRs and graphite disposal or processing

    International Nuclear Information System (INIS)

    Schloegel, Baerbel

    2010-01-01

    Currently future nuclear reactor concepts of the Fourth Generation (Gen IV) are under development. To some extend they apply with new, innovative materials developed just for this purpose. This thesis work aims at a concept of Generation IV Very High Temperature Reactors (VHTR) in the framework of the European project RAPHAEL (ReActor for Process heat, Hydrogen And ELectricity generation). The concept named ANTARES (AREVA New Technology based on advanced gas-cooled Reactors for Energy Supply) was developed by AEVA NP. It is a helium cooled, graphite moderated modular reactor for electricity and hydrogen production, by providing the necessary process heat due to its high working temperature. Particular attention is given here to oxidation kinetics of newly developed carbon materials (NBG-17) with still unknown but needed information in context of severe air ingress accident in VHTR's. Special interest is paid to the Boudouard reaction, the oxidation of carbon by CO 2 . In case of an air ingress accident, carbon dioxide is produced in the primary reaction of atmospheric oxygen with reflector graphite. From there CO 2 could flow into the reactor core causing further damage by conversion into CO. The purpose of this thesis is to ascertain if and to what degree this could happen. First of all oxidation kinetic data of the Boudouard reaction with NBG-17 is determined by experiments in a thermo gravimetric facility. The measurements are evaluated and converted into a common formula and a Langmuir-Hinshelwood similar oxidation kinetic equation, as input for the computer code REACT/THERMIX. This code is then applied to analyse severe air ingress accidents for several air flow rates. The results are discussed for two accident situations, in which a certain graphite burn off is achieved. All cases show much more damage to the graphite bottom reflector than to the reactor core. Thus the bottom reflector will lose its structural integrity much earlier than the core itself will

  20. The influence of conductive additives and inter-particle voids in carbon EDLC electrodes

    Energy Technology Data Exchange (ETDEWEB)

    Pandolfo, A.G.; Wilson, G.J.; Huynh, T.D.; Hollenkamp, A.F. [CSIRO - Energy Technology, Bayview Avenue, Clayton, Vic 3168 (Australia)

    2010-10-15

    Through the interpretation of porosity and intrusion data, and correlation to the electrochemical response, this study has confirmed that are not only carbon blacks (CBs) very effective in improving the electrical connectivity of a carbon electrode coating, but they also significantly modify the porosity of the electrode coating and thereby also influence ionic diffusion. CBs are more effective conductive fillers than graphites in EDLC electrodes. The highly branched structure of CBs allows multiple electrical contact points and results in a lower electrode electronic resistance. CBs can decrease inter-particle porosity (both volume and size) and introduce additional porosity that is characteristic of the type of carbon employed. It is observed that electrode coatings prepared from a carbon slurry have a highly macroporous structure and that electrolyte accessibility to individual activated carbon particles is unlikely to be the limiting factor to accessing capacitance. Electrochemical testing has confirmed the strong relationship between bulk electrode resistance and the accessibility of capacitance at different rates. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

  1. Environmentally-friendly oxygen-free roasting/wet magnetic separation technology for in situ recycling cobalt, lithium carbonate and graphite from spent LiCoO{sub 2}/graphite lithium batteries

    Energy Technology Data Exchange (ETDEWEB)

    Li, Jia; Wang, Guangxu; Xu, Zhenming, E-mail: zmxu@sjtu.edu.cn

    2016-01-25

    Highlights: • The idea of “waste + waste → resources.” was used on this study. • Based on thermodynamic analysis, the possible reaction between LiCoO{sub 2} and graphite was obtained. • The residues of oxygen-free roasting are cobalt, lithium carbonate and graphite. • The recovery rate of Co and Li is 95.72% and 98.93% after wet magnetic separation. • It provides the rationale for environmental-friendly recycling spent LIBs in industrial-scale. - Abstract: The definite aim of the present paper is to present some novel methods that use oxygen-free roasting and wet magnetic separation to in situ recycle of cobalt, Lithium Carbonate and Graphite from mixed electrode materials. The in situ recycling means to change waste into resources by its own components, which is an idea of “waste + waste → resources.” After mechanical scraping the mixed electrode materials enrich powders of LiCoO{sub 2} and graphite. The possible reaction between LiCoO{sub 2} and graphite was obtained by thermodynamic analysis. The feasibility of the reaction at high temperature was studied with the simultaneous thermogravimetry analysis under standard atmospheric pressure. Then the oxygen-free roasting/wet magnetic separation method was used to transfer the low added value mixed electrode materials to high added value products. The results indicated that, through the serious technologies of oxygen-free roasting and wet magnetic separation, mixture materials consist with LiCoO{sub 2} and graphite powders are transferred to the individual products of cobalt, Lithium Carbonate and Graphite. Because there is not any chemical solution added in the process, the cost of treating secondary pollution can be saved. This study provides a theoretical basis for industrial-scale recycling resources from spent LIBs.

  2. Azide photochemistry for facile modification of graphitic surfaces: preparation of DNA-coated carbon nanotubes for biosensing

    International Nuclear Information System (INIS)

    Moghaddam, Minoo J; Yang Wenrong; Bojarski, Barbara; Gengenbach, Thomas R; Gao Mei; Zareie, Hadi; McCall, Maxine J

    2012-01-01

    A facile, two-step method for chemically attaching single-stranded DNA to graphitic surfaces, represented here by carbon nanotubes, is reported. In the first step, an azide-containing compound, N-5-azido-nitrobenzoyloxy succinimide (ANB-NOS), is used to form photo-adducts on the graphitic surfaces in a solid-state photochemical reaction, resulting in active ester groups being oriented for the subsequent reactions. In the second step, pre-synthesized DNA strands bearing a terminal amine group are coupled in an aqueous solution with the active esters on the photo-adducts. The versatility of the method is demonstrated by attaching pre-synthesized DNA to surfaces of carbon nanotubes in two platforms—as vertically-aligned multi-walled carbon nanotubes on a solid support and as tangled single-walled carbon nanotubes in mats. The reaction products at various stages were characterized by x-ray photoelectron spectroscopy. Two different assays were used to check that the DNA strands attached to the carbon nanotubes were able to bind their partner strands with complementary base sequences. The first assay, using partner DNA strands tethered to gold nanoparticles, enabled the sites of DNA attachment to the carbon nanotubes to be identified in TEM images. The second assay, using radioactively labelled partner DNA strands, quantified the density of functional DNA strands attached to the carbon nanotubes. The diversity of potential applications for these DNA-modified carbon-nanotube platforms is exemplified here by the successful use of a DNA-modified single-walled carbon-nanotube mat as an electrode for the specific detection of metal ions. (paper)

  3. Effect of iron and chromium on the graphitization behaviour of sulfur-containing carbon

    International Nuclear Information System (INIS)

    Tyumentsev, V.A.; Belenkov, E.A.; Saunina, S.I.; Podkopaev, S.A.; Shvejkin, G.P.

    1998-01-01

    Process of transition of carbonaceous material, containing structurally incorporated sulfur, into graphite and impact of iron and chromium additions are studied. It is established that carbonaceous material, containing more than 1.5 mass % S and also 1.5 mass % Cr 2 O 3 is heterogeneous after thermal treatment at 1300-1600 deg C. It consists of large and sufficiency complete areas of coherent scattering having graphite structure and ultra-dispersed matrix. The number of graphite crystals formed in the presence of dispersed iron within this temperature range, decreases by two times [ru

  4. The Role of Cesium Cation in Controlling Interphasial Chemistry on Graphite Anode in Propylene Carbonate-Rich Electrolytes

    Energy Technology Data Exchange (ETDEWEB)

    Xiang, Hongfa; Mei, Donghai; Yan, Pengfei; Bhattacharya, Priyanka; Burton, Sarah D.; Cresce, Arthur V.; Cao, Ruiguo; Engelhard, Mark H.; Bowden, Mark E.; Zhu, Zihua; Polzin, Bryant; Wang, Chong M.; Xu, Kang; Zhang, Jiguang; Xu, Wu

    2015-09-10

    Propylene carbonate (PC) is seldom used in lithium-ion batteries (LIBs) due to its sustained co-intercalation into graphene structure and the eventual graphite exfoliation, despite potential advantages it brings, such as wider liquid range and lower cost. Here we discover that cesium cation (Cs+), originally used to suppress dendrite growth of Li metal anode, directs the formation of solid electrolyte interphase (SEI) on graphitic anode in PC-rich electrolytes through preferential solvation. Effective suppression of PC-decomposition and graphite-exfoliation was achieved when the ratio of ethylene carbonate (EC)/PC in electrolytes was so adjusted that the reductive decomposition of Cs+-(EC)m (1≤m≤2) complex precedes that of Li+-(PC)n (3≤n≤5). The interphase directed by Cs+ is stable, ultrathin and compact, leading to significant improvements in LIB performances. In a broader context, the accurate tailoring of SEI chemical composition by introducing a new solvation center represents a fundamental breakthrough in manipulating interfacial reactions processes that once were elusive.

  5. Electrospun N-doped Hierarchical Porous Carbon Nanofiber with Improved Graphitization Degree for High Performance Lithium Ion Capacitor.

    Science.gov (United States)

    Li, Baohua; Shi, Ruiying; Han, Cuiping; Xu, Xiaofu; Qing, Xianying; Xu, Lei; Li, Hongfei; Li, Junqin; Wong, Ching-Ping

    2018-05-14

    Lithium ion capacitor (LIC) has been regarded as a promising device to combine the merits of lithium ion batteries and supercapacitors, which can meet the requirements for both high energy and power density. The development of advanced electrode is the key. Herein, we demonstrate the bottom-up synthesis of activated carbon nanofiber (a-PANF) with hierarchical porous structure and high graphitization degree. Electrospinning is employed to prepare interconnected fiber network with macropores and ferric acetylacetonate is introduced as both mesopore creating agent and graphitic catalyst to increase the graphitization degree. Furthermore, chemical activation enlarges the specific surface area by producing rich micropores. Half cell evaluation of the as-prepared a-PANF displays a discharge capacity of 80 mAh g-1 at 0.1 A g-1 within 2~4.5 V and no capacity fading after 1000 cycles at 2 A g-1, which is significantly higher than conventional activated carbon. Furthermore, the as-assembled LIC with a-PANF cathode and Fe3O4 anode achieves a superior energy density of 124.6 Wh kg-1 at a specific power of 93.8 W kg-1, and remains 103.7 Wh kg-1 at 4687.5 W kg-1, demonstrating the promising application of a-PANF as potential electrode candidates for efficient energy storage systems. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  6. A novel route to graphite-like carbon supporting SnO{sub 2} with high electron transfer and photocatalytic activity

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Xianjie; Liu, Fenglin; Liu, Bing [Hubei Collaborative Innovation Center for Advanced Organochemical Materials, Hubei University, Wuhan 430062 (China); Ministry of Education Key Laboratory for the Synthesis and Applications of Organic Functional Molecules, Hubei University, Wuhan 430062 (China); Tian, Lihong, E-mail: tian7978@hubu.edu.cn [Hubei Collaborative Innovation Center for Advanced Organochemical Materials, Hubei University, Wuhan 430062 (China); Ministry of Education Key Laboratory for the Synthesis and Applications of Organic Functional Molecules, Hubei University, Wuhan 430062 (China); Hu, Wei; Xia, Qinghua [Hubei Collaborative Innovation Center for Advanced Organochemical Materials, Hubei University, Wuhan 430062 (China); Ministry of Education Key Laboratory for the Synthesis and Applications of Organic Functional Molecules, Hubei University, Wuhan 430062 (China)

    2015-04-28

    Highlights: • Mesoporous nanocomposites that graphite-like carbon supporting SnO{sub 2} are prepared by solvothermal method combined with a post- calcination. • The polyvinylpyrrolidone not only promotes the nucleation and crystallization but also provides the carbon source in the process. • The graphite-like carbon hinders the recombination of photogenerated electron and holes efficiently. • The mesoporous carbon–SnO{sub 2} nanocomposite shows high photocatalytic activity on the degradation of Rhodamine B and glyphosate under simulated sunlight. - Abstract: Mesoporous graphite-like carbon supporting SnO{sub 2} (carbon–SnO{sub 2}) nanocomposites were prepared by a modified solvothermal method combined with a post-calcination at 500 °C under a nitrogen atmosphere. The polyvinylpyrrolidone not only promotes the nucleation and crystallization, but also provides the carbon source in the process. The results of scanning electron microscopy and transmission electron microscopy show a uniform distribution of SnO{sub 2} nanoparticles on the graphite- like carbon surface. Raman and X-ray photoelectron spectra indicate the presence of strong C–Sn interaction between SnO{sub 2} and graphite-like carbon. Photoelectrochemical measurements confirm that the effective separation of electron–hole pairs on the carbon–SnO{sub 2} nanocomposite leads to a high photocatalytic activity on the degradation of Rhodamine B and glyphosate under simulated sunlight irradiation. The nanocomposite materials show a potential application in dealing with the environmental and industrial contaminants under sunlight irradiation.

  7. Amperometric sensor for detection of bisphenol A using a pencil graphite electrode modified with polyaniline nanorods and multiwalled carbon nanotubes

    International Nuclear Information System (INIS)

    Poorahong, S.; Thammakhet, C.; Numnuam, A.; Kanatharana, P.; Thavarungkul, P.; Limbut, W.

    2012-01-01

    We report on a simple and highly sensitive amperometric method for the determination of bisphenol A (BPA) using pencil graphite electrodes modified with polyaniline nanorods and multiwalled carbon nanotubes. The modified electrodes display enhanced electroactivity for the oxidation of BPA compared to the unmodified pencil graphite electrode. Under optimized conditions, the sensor has a linear response to BPA in the 1. 0 and 400 μM concentration range, with a limit of detection of 10 nM (at S/N = 3). The modified electrode also has a remarkably stable response, and up to 95 injections are possible with a relative standard deviation of 4. 2% at 100 μM of BPA. Recoveries range from 86 to 102% for boiling water spiked with BPA from four brands of baby bottles. (author)

  8. Nitrogen-Doped Carbon Nanotube/Graphite Felts as Advanced Electrode Materials for Vanadium Redox Flow Batteries.

    Science.gov (United States)

    Wang, Shuangyin; Zhao, Xinsheng; Cochell, Thomas; Manthiram, Arumugam

    2012-08-16

    Nitrogen-doped carbon nanotubes have been grown, for the first time, on graphite felt (N-CNT/GF) by a chemical vapor deposition approach and examined as an advanced electrode for vanadium redox flow batteries (VRFBs). The unique porous structure and nitrogen doping of N-CNT/GF with increased surface area enhances the battery performance significantly. The enriched porous structure of N-CNTs on graphite felt could potentially facilitate the diffusion of electrolyte, while the N-doping could significantly contribute to the enhanced electrode performance. Specifically, the N-doping (i) modifies the electronic properties of CNT and thereby alters the chemisorption characteristics of the vanadium ions, (ii) generates defect sites that are electrochemically more active, (iii) increases the oxygen species on CNT surface, which is a key factor influencing the VRFB performance, and (iv) makes the N-CNT electrochemically more accessible than the CNT.

  9. Uncovering the local inelastic interactions during manufacture of ductile cast iron: How the substructure of the graphite particles can induce residual stress concentrations in the matrix

    DEFF Research Database (Denmark)

    Andriollo, Tito; Hellström, Kristina; Sonne, Mads Rostgaard

    2018-01-01

    Recent X-ray diffraction (XRD) measurements have revealed that plastic deformation and a residual elastic strain field can be present around the graphite particles in ductile cast iron after manufacturing, probably due to some local mismatch in thermal contraction. However, as only one component...... of the elastic strain tensor could be obtained from the XRD data, the shape and magnitude of the associated residual stress field have remained unknown. To compensate for this and to provide theoretical insight into this unexplored topic, a combined experimental-numerical approach is presented in this paper...... the graphite particles and the matrix during manufacturing of the industrial part considered in the XRD study. The model indicates that, besides the vis- coplastic deformation of the matrix, the effect of the inelastic deformation of the graphite has to be considered to explain the magnitude of the XRD strain...

  10. Nitrite electrochemical sensor based on prussian blue/single-walled carbon nanotubes modified pyrolytic graphite electrode

    CSIR Research Space (South Africa)

    Adekunle, AS

    2011-09-01

    Full Text Available Nitrite, NO2- (in neutral), and NO (in acidic media) were used as analytical probe to investigate the electrocatalytic properties of Prussian blue nanoparticles (PB) modified edge plane pyrolytic graphite (EPPG) electrode. Results indicate...

  11. Development of graphite carbon nitride based fluorescent immune sensor for detection of alpha fetoprotein

    Science.gov (United States)

    Li, Yike; Dong, Lingyu; Wang, Xiangfeng; Liu, Yuan; Liu, Hailing; Xie, Mengxia

    2018-05-01

    A novel fluorescent immunosensor for determination of alpha fetoprotein (AFP) in serum samples has been developed based on the nano graphite carbon nitride (g-C3N4) as fluorophore and immunomagnetic beads (MBs) as separation material. The bulk g-C3N4 was obtained by thermal polymerization of melamine, and then carboxylated and exfoliated to acquire the carboxylated nano g-C3N4 (c-n-g-C3N4), which has been characterized and the results showed that it had excellent fluorescent properties. The antibodies of AFP (Ab1, Ab2) were conjugated to the MBs and the c-n-g-C3N4, respectively. In assay of AFP detection, the magnetic part of the immunosensor, MBs-Ab1, would form the sandwich type complex with the signal part of the sensor, c-n-g-C3N4-Ab2. The developed immunosensor could simplify the process of separation due to the MBs. The results illustrated that proposed approach held a good linearity between the fluorescence intensity of the sensor and the AFP concentration ranging from 5-600 ng/mL with the limit of detection as low as 0.43 ng/mL, and its spiking recoveries ranged from 98.2% to 105.9% with RSD from 2.1% to 3.5%. The fabricated fluorescent immunosensor possesses the merits of good sensitivity, excellent selectivity, high biocompatibility and low cost, and the results provide a novel clue to develop immunosensor for determination of the biomarkers in complex matrices.

  12. Resonance energy transfer based electrochemiluminescence and fluorescence sensing of riboflavin using graphitic carbon nitride quantum dots

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Huan [Key Laboratory of Bioelectrochemistry & Environmental Analysis of Gansu Province, College of Chemistry & Chemical Engineering, Northwest Normal University, Lanzhou, Gansu 730070 (China); The Phytochemistry Key Laboratory of Tibetan Plateau of Qinghai Province, College of Pharmacy, Qinghai Nationalities University, Xining, Qinghai 810007 (China); Ma, Qin; Wang, Yanfeng; Wang, Caihe; Qin, Dongdong; Shan, Duoliang; Chen, Jing [Key Laboratory of Bioelectrochemistry & Environmental Analysis of Gansu Province, College of Chemistry & Chemical Engineering, Northwest Normal University, Lanzhou, Gansu 730070 (China); Lu, Xiaoquan, E-mail: luxq@nwnu.edu.cn [Key Laboratory of Bioelectrochemistry & Environmental Analysis of Gansu Province, College of Chemistry & Chemical Engineering, Northwest Normal University, Lanzhou, Gansu 730070 (China)

    2017-06-22

    Graphitic carbon nitride quantum dots (g-CNQDs) are rarely used in the field of electrochemiluminescence. In this paper, g-CNQDs have a strong and stable electrochemiluminescence (ECL) signal generated in the presence of co-reactant K{sub 2}S{sub 2}O{sub 8}. The ECL signal of g-CNQDs was quenched by the mechanism of resonance energy transfer (RET) between donor g-CNQDs and receptor riboflavin (RF) that is proved by UV-vis absorption spectroscopy, electrochemiluminescence and fluorescence emission spectroscopy analysis technology. Therefore, we achieved detection of the riboflavin content in the drug tablets of vitamin B{sub 2} using ECL and FL. The determination results of ECL showed that the riboflavin content of the drug vitamin B{sub 2} (VB{sub 2}) tablets was consistent with the fluorescence (FL) analysis, with wider linear range of 0.02–11 μM and lower minimum detection limit of 0.63 nM (S/N = 3) than FL. Hence, the riboflavin content in human serum was further detected using ECL. The relative standard deviation is less than 6.5%, with an acceptable recovery of 95.33%–104.22%, which means that this sensor has potential applications in the actual sample analysis. As a new ECL luminary, g-CNQDs have opened a new field for the development and application of ECL sensor. - Highlights: • G-CNQDs proposed as a new luminophore for ECL. • ECL signal was strong and stable in the presence of co-reactant K{sub 2}S{sub 2}O{sub 8}. • Based on the resonance energy transfer between g-CNQDs and riboflavin. • ECL has wider linear range and lower detection limit than FL.

  13. Resonance energy transfer based electrochemiluminescence and fluorescence sensing of riboflavin using graphitic carbon nitride quantum dots

    International Nuclear Information System (INIS)

    Wang, Huan; Ma, Qin; Wang, Yanfeng; Wang, Caihe; Qin, Dongdong; Shan, Duoliang; Chen, Jing; Lu, Xiaoquan

    2017-01-01

    Graphitic carbon nitride quantum dots (g-CNQDs) are rarely used in the field of electrochemiluminescence. In this paper, g-CNQDs have a strong and stable electrochemiluminescence (ECL) signal generated in the presence of co-reactant K 2 S 2 O 8 . The ECL signal of g-CNQDs was quenched by the mechanism of resonance energy transfer (RET) between donor g-CNQDs and receptor riboflavin (RF) that is proved by UV-vis absorption spectroscopy, electrochemiluminescence and fluorescence emission spectroscopy analysis technology. Therefore, we achieved detection of the riboflavin content in the drug tablets of vitamin B 2 using ECL and FL. The determination results of ECL showed that the riboflavin content of the drug vitamin B 2 (VB 2 ) tablets was consistent with the fluorescence (FL) analysis, with wider linear range of 0.02–11 μM and lower minimum detection limit of 0.63 nM (S/N = 3) than FL. Hence, the riboflavin content in human serum was further detected using ECL. The relative standard deviation is less than 6.5%, with an acceptable recovery of 95.33%–104.22%, which means that this sensor has potential applications in the actual sample analysis. As a new ECL luminary, g-CNQDs have opened a new field for the development and application of ECL sensor. - Highlights: • G-CNQDs proposed as a new luminophore for ECL. • ECL signal was strong and stable in the presence of co-reactant K 2 S 2 O 8 . • Based on the resonance energy transfer between g-CNQDs and riboflavin. • ECL has wider linear range and lower detection limit than FL.

  14. In situ synthesis of cylindrical spongy polypyrrole doped protonated graphitic carbon nitride for cholesterol sensing application.

    Science.gov (United States)

    Shrestha, Bishnu Kumar; Ahmad, Rafiq; Shrestha, Sita; Park, Chan Hee; Kim, Cheol Sang

    2017-08-15

    Herein, we demonstrate the exfoliation of bulk graphitic carbon nitrides (g-C 3 N 4 ) into ultra-thin (~3.4nm) two-dimensional (2D) nanosheets and their functionalization with proton (g-C 3 N 4 H + ). The layered semiconductor g-C 3 N 4 H + nanosheets were doped with cylindrical spongy shaped polypyrrole (CSPPy-g-C 3 N 4 H + ) using chemical polymerization method. The as-prepared nanohybrid composite was utilized to fabricate cholesterol biosensors after immobilization of cholesterol oxidase (ChOx) at physiological pH. Large specific surface area and positive charge nature of CSPPy-g-C 3 N 4 H + composite has tendency to generate strong electrostatic attraction with negatively charged ChOx, and as a result they formed stable bionanohybrid composite with high enzyme loading. A detailed electrochemical characterization of as-fabricated biosensor electrode (ChOx-CSPPy-g-C 3 N 4 H + /GCE) exhibited high-sensitivity (645.7 µAmM -1 cm -2 ) in wide-linear range of 0.02-5.0mM, low detection limit (8.0μM), fast response time (~3s), long-term stability, and good selectivity during cholesterol detection. To the best of our knowledge, this novel nanocomposite was utilized for the first time for cholesterol biosensor fabrication that resulted in high sensing performance. Hence, this approach opens a new prospective to utilize CSPPy-g-C 3 N 4 H + composite as cost-effective, biocompatible, eco-friendly, and superior electrocatalytic as well as electroconductive having great application potentials that could pave the ways to explore many other new sensors fabrication and biomedical applications. Copyright © 2017 Elsevier B.V. All rights reserved.

  15. Enhanced visible-light-driven photocatalytic performance of porous graphitic carbon nitride

    Energy Technology Data Exchange (ETDEWEB)

    Chang, Fei, E-mail: feichang@usst.edu.cn [School of Environment and Architecture, University of Shanghai for Science and Technology, Shanghai 200093 (China); Li, Chenlu; Luo, Jieru; Xie, Yunchao; Deng, Baoqing [School of Environment and Architecture, University of Shanghai for Science and Technology, Shanghai 200093 (China); Hu, Xuefeng, E-mail: xfhu@yic.ac.cn [Key Laboratory of Coastal Environmental Processes and Ecological Remediation, Yantai Institute of Coastal Zone Research, Chinese Academy of Sciences, Yantai, Shandong 264003 (China)

    2015-12-15

    Graphical abstract: - Highlights: • Porous g-C{sub 3}N{sub 4} samples were fabricated by a facile pyrolysis method. • As-prepared porous g-C{sub 3}N{sub 4} samples showed remarkably enhanced photocatalytic performance. • Holes and radicals ·O{sub 2}{sup −} exerted dominant roles on the photocatalytic process. - Abstract: In this study, a series of porous graphitic carbon nitride (g-C{sub 3}N{sub 4}) materials were fabricated through a direct pyrolysis of protonated melamine by nitric acid solution. These as-prepared porous samples were characterized by a collection of analytical techniques. It was found that a proper concentration of nitric acid solution involved facilitated to generate samples in tube-like morphology with numerous pores, identified with X-ray diffraction patterns, FT-IR spectra, SEM, TEM, and BET measurements. These g-C{sub 3}N{sub 4} samples were subjected to photocatalytic degradation of dye Rhodamine B (RhB) in aqueous under visible-light irradiation. Under identical conditions, those porous g-C{sub 3}N{sub 4} samples showed significantly improved catalytic performance in comparison with the sample prepared without the introduction of nitric acid. In particularly, the best candidate, sample M1:1, showed an apparent reaction rate nearly 6.2 times that of the unmodified counterpart. The enhancement of photocatalytic performance could be attributed to the favorable porous structure with the enlarged specific surface area and the suitable electronic structure as well. In addition, ESR measurements were conducted for the sake of proposing a photocatalytic degradation mechanism.

  16. Self-floating graphitic carbon nitride/zinc phthalocyanine nanofibers for photocatalytic degradation of contaminants

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Tiefeng; Ni, Dongjing; Chen, Xia; Wu, Fei; Ge, Pengfei; Lu, Wangyang, E-mail: luwy@zstu.edu.cn; Hu, Hongguang; Zhu, ZheXin; Chen, Wenxing, E-mail: wxchen@zstu.edu.cn

    2016-11-05

    Highlights: • A facile synthetic strategy to prepare visible-light responsive electrospun nanofibers. • Self-floating nanofiber photocatalyts for the effective utilization of solar. • Possible degradation pathway of RhB and CBZ under visible light and solar irradiation. • Present a method for removing highly hazardous contaminants. - Abstract: The effective elimination of micropollutants by an environmentally friendly method has received extensive attention recently. In this study, a photocatalyst based on polyacrylonitrile (PAN)-supported graphitic carbon nitride coupled with zinc phthalocyanine nanofibers (g-C{sub 3}N{sub 4}/ZnTcPc/PAN nanofibers) was successfully prepared, where g-C{sub 3}N{sub 4}/ZnTcPc was introduced as the catalytic entity and the PAN nanofibers were employed as support to overcome the defects of easy aggregation and difficult recycling. Herein, rhodamine B (RhB), 4-chlorophenol and carbamazepine (CBZ) were selected as the model pollutants. Compared with the typical hydroxyl radical-dominated catalytic system, g-C{sub 3}N{sub 4}/ZnTcPc/PAN nanofibers displayed the targeted adsorption and degradation of contaminants under visible light or solar irradiation in the presence of high additive concentrations. According to the results of the radical scavenging techniques and the electron paramagnetic resonance technology, the degradation of target substrates was achieved by the attack of active species, including photogenerated hole, singlet oxygen, superoxide radicals and hydroxyl radicals. Based on the results of ultra-performance liquid chromatography and mass spectrometry, the role of free radicals on the photocatalytic degradation intermediates was identified and the final photocatalytic degradation products of both RhB and CBZ were some biodegradable small molecules.

  17. Mechanical and physical properties of carbon-graphite fiber-reinforced polymers intended for implant suprastructures.

    Science.gov (United States)

    Segerström, Susanna; Ruyter, I Eystein

    2007-09-01

    Mechanical properties and quality of fiber/matrix adhesion of poly(methyl methacrylate) (PMMA)-based materials, reinforced with carbon-graphite (CG) fibers that are able to remain in a plastic state until polymerization, were examined. Tubes of cleaned braided CG fibers were treated with a sizing resin. Two resin mixtures, resin A and resin B, stable in the fluid state and containing different cross-linking agents, were reinforced with CG fiber loadings of 24, 36, and 47 wt% (20, 29, and 38 vol.%). In addition, resin B was reinforced with 58 wt% (47 vol.%). After heat-polymerization, flexural strength and modulus were evaluated, both dry and after water storage. Coefficient of thermal expansion, longitudinally and in the transverse direction of the specimens, was determined. Adhesion between fibers and matrix was evaluated with scanning electron microscopy (SEM). Flexural properties and linear coefficient of thermal expansion were similar for both fiber composites. With increased fiber loading, flexural properties increased. For 47 wt% fibers in polymer A the flexural strength was 547.7 (28.12) MPa and for polymer B 563.3 (89.24) MPa when water saturated. Linear coefficient of thermal expansion was for 47 wt% CG fiber-reinforced polymers; -2.5 x 10(-6) degrees C-1 longitudinally and 62.4 x 10(-6) degrees C-1 in the transverse direction of the specimens. SEM revealed good adhesion between fibers and matrix. More porosity was observed with fiber loading of 58 wt%. The fiber treatment and the developed resin matrices resulted in good adhesion between CG fibers and matrix. The properties observed indicate a potential for implant-retained prostheses.

  18. Patterned structures of graphene and graphitic carbon and methods for their manufacture

    Energy Technology Data Exchange (ETDEWEB)

    Polsky, Ronen; Xiao, Xiaoyin; Burckel, David Bruce; Wheeler, David R.; Brozik, Susan M.; Beechem, Thomas Edwin

    2018-01-09

    A patterned graphene or graphitic body is produced by providing a three-dimensionally patterned carbonaceous body; coating the body with a catalytic metal whereby is formed a coating having an inner surface proximal the body and an outer surface distal the body; and annealing the coated body under time and temperature conditions effective to form a graphene or graphitic layer on the outer surface of the catalytic metal coating.

  19. Enhanced photovoltaic properties in graphitic carbon nanospheres networked TiO{sub 2} nanocomposite based dye sensitized solar cell

    Energy Technology Data Exchange (ETDEWEB)

    Agarwal, Radhe [Department of Physics and Institute for Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00931 (United States); Sahoo, Satyaprakash, E-mail: satya504@gmail.com [Department of Physics and Institute for Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00931 (United States); Chitturi, Venkateswara Rao [Department of Physics and Institute for Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00931 (United States); Williams, Joseph D. [Department of Biomedical and Chemical Engineering, Syracuse University, L.C. Smith College of Engineering and Computer Science, Syracuse, NY (United States); Resto, Oscar [Department of Physics and Institute for Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00931 (United States); Katiyar, Ram S., E-mail: rkatiyar@hpcf.uprrp.edu [Department of Physics and Institute for Functional Nanomaterials, University of Puerto Rico, San Juan, PR 00931 (United States)

    2015-08-25

    Highlights: • Nano size graphitic carbon nanospheres were prepared from MWCNTs. • TiO{sub 2}/GCNS composite was used as the photoanode in dye-sensitized solar cell. • An improved photovoltaic performance with GCNS–TiO{sub 2} composite was noticed. - Abstract: In this work, we report a novel carbon based TiO{sub 2} nanocomposite electron injection layer (photoanode) toward the improved performance of DSSCs. Graphitic carbon nanospheres (GCNSs) were synthesized by a unique acidic treatment of multi-wall carbon nanotubes. GCNS–TiO{sub 2} nanocomposites with different concentrations of GCNSs (ranging from 5 to 20 μL) were prepared to use as photoanodes in DSSCs. Structural and morphological properties of GCNS–TiO{sub 2} nanocomposites were analyzed by Raman spectroscopy and ultra-high resolution transmission electron microscopy techniques, respectively. A systematic increment in the short circuit current density (J{sub SC}) and open circuit voltage (V{sub OC}) of DSSC was observed by increasing GCNS concentration up to an optimal value, possibly due to the combined effect of slight rise in quasi-Fermi level and higher carrier transport rate in the resultant composite. Thus, a significant enhancement of ∼47% in the efficiency of DSSC containing GCNS–TiO{sub 2} photoanode was observed as compare to DSSC with pure TiO{sub 2} photoanode.

  20. Metal-Embedded Porous Graphitic Carbon Fibers Fabricated from Bamboo Sticks as a Novel Cathode for Lithium-Sulfur Batteries.

    Science.gov (United States)

    Zhang, Xuqing; Zhong, Yu; Xia, Xinhui; Xia, Yang; Wang, Donghuang; Zhou, Cheng'ao; Tang, Wangjia; Wang, Xiuli; Wu, J B; Tu, Jiangping

    2018-04-25

    Lithium-sulfur batteries (LSBs) are deemed to be among the most prospective next-generation advanced high-energy batteries. Advanced cathode materials fabricated from biological carbon are becoming more popular due to their unique properties. Inspired by the fibrous structure of bamboo, herein we put forward a smart strategy to convert bamboo sticks for barbecue into uniform bamboo carbon fibers (BCF) via a simple hydrothermal treatment proceeded in alkaline solution. Then NiCl 2 is used to etch the fibers through a heat treatment to achieve Ni-embedded porous graphitic carbon fibers (PGCF/Ni) for LSBs. The designed PGCF/Ni/S electrode exhibits improved electrochemical performances including high initial capacity (1198 mAh g -1 at 0.2 C), prolonged cycling life (1030 mAh g -1 at 0.2 C after 200 cycles), and improved rate capability. The excellent properties are attributed to the synergistic effect of 3D porous graphitic carbon fibers with highly conductive Ni nanoparticles embedded.

  1. Green synthesis of nitrogen-doped graphitic carbon sheets with use of Prunus persica for supercapacitor applications

    Energy Technology Data Exchange (ETDEWEB)

    Atchudan, Raji, E-mail: atchudanr@yu.ac.kr [School of Chemical Engineering, Yeungnam University, Gyeongsan 38541 (Korea, Republic of); Edison, Thomas Nesakumar Jebakumar Immanuel [School of Chemical Engineering, Yeungnam University, Gyeongsan 38541 (Korea, Republic of); Perumal, Suguna [Department of Applied Chemistry, Kyungpook National University, Daegu 41566 (Korea, Republic of); Lee, Yong Rok, E-mail: yrlee@yu.ac.kr [School of Chemical Engineering, Yeungnam University, Gyeongsan 38541 (Korea, Republic of)

    2017-01-30

    Highlights: • N-GCSs was synthesized from the unripe Prunus persica by direct hydrothermal method. • The resulting N-GCSs-2 exhibit an excellent graphitization with 9.33% of nitrogen. • N-GCSs-2 provide high C{sub s} of 176 F g{sup −1} at current density of 0.1 A g{sup −1} in 1 M H{sub 2}SO{sub 4}. • N-GCSs-2 have high capacitance retention and 20% capacity growth after 2000 cycles. • First time, N-GCSs resulted from peach via green route for flexible supercapacitors. - Abstract: Nitrogen-doped graphitic carbon sheets (N-GCSs) were prepared from the extract of unripe Prunus persica fruit by a direct hydrothermal method. The synthesized N-GCSs were examined by high resolution transmission electron microscopy (HRTEM), nitrogen adsorption-desorption isotherms, X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), and Fourier transform infrared (FT-IR) spectroscopy. HRTEM showed that the synthesized carbon sheets were graphitic with lattice fringes and an inter-layer distance of 0.36 nm. Doping with the nitrogen moiety present over the synthesized GCSs was confirmed by XPS, FT-IR spectroscopy, and energy dispersive X-ray spectroscopy elemental mapping. The fruit extract associated with hydrothermal-carbonization method is economical and eco-friendly with a single step process. The resulting carbon sheets could be modified and are promising candidates for nano-electronic applications, including supercapacitors. The synthesized N-GCSs-2 provided a high specific capacitance of 176 F g{sup −1} at a current density of 0.1 A g{sup −1}. This electrode material has excellent cyclic stability, even after 2000 cycles of charge-discharge at a current density of 0.5 A g{sup −1}.

  2. Unique graphitized mesophase carbon microbead@niobium carbide-derived carbon composites as high performance anode materials of lithium-ion battery

    International Nuclear Information System (INIS)

    Yuan, Xiulan; Cong, Ye; Yu, Yanyan; Li, Xuanke; Zhang, Jiang; Dong, Zhijun; Yuan, Guanming; Cui, Zhengwei; Li, Yanjun

    2017-01-01

    To meet the requirements of the energy storage materials for high energy density and high power density, unique niobium carbide-derived carbon (NbC-CDC) coated graphitized mesophase carbon microbead (GMCMB) composites (GMCMB@NbC-CDC) with core-shell structure were prepared by chlorinating the precursor of graphitization mesophase carbon microbead@niobium carbide. The microstructure of NbC-CDC was characterized as mainly amorphous carbon combined with short and curved sheets of graphene, and the order degree of carbon layers increases with the chlorination temperature. The composites exhibited a tunable specific surface area and micropore volume, with micropore size of 0.6∼0.7 nm. Compared with the pure GMCMB, the GMCMB@NbC-CDC composites manifested higher charge (726.9 mAh g"−"1) and discharge capacities (458.9 mAh g"−"1) at the first cycle, which was probably that Li ions could insert into not only carbon layers of GMCMB but also micropores of NbC-CDC. After 100 cycles, the discharge capacity of GMCMB@NbC-CDC chlorinated at 800 °C still kept 384.6 mAh g"−"1, which was much higher than that of the pure GMCMB (305.2 mAh g"−"1). Furthermore, the GMCMB@NbC-CDC composites presented better rate performance at higher current densities.

  3. Enhanced visible light photocatalytic degradation of Rhodamine B over phosphorus doped graphitic carbon nitride

    Energy Technology Data Exchange (ETDEWEB)

    Chai, Bo, E-mail: willycb@163.com; Yan, Juntao; Wang, Chunlei; Ren, Zhandong; Zhu, Yuchan

    2017-01-01

    Highlights: • The phosphorus doped g-C{sub 3}N{sub 4} photocatalysts are synthesized by a co-pyrolysis procedure. • The crystal phase, morphology, and optical property of P doped g-C{sub 3}N{sub 4} are characterized. • The P doped g-C{sub 3}N{sub 4} photocatalysts show the improved photocatalytic activity. • The possible mechanism for enhanced photocatalytic activity is proposed. - Abstract: Phosphorus doped graphitic carbon nitride (g-C{sub 3}N{sub 4}) was easily synthesized using ammonium hexafluorophosphate (NH{sub 4}PF{sub 6}) as phosphorus source, and ammonium thiocyanate (NH{sub 4}SCN) as g-C{sub 3}N{sub 4} precursor, through a direct thermal co-polycondensation procedure. The obtained phosphorus doped g-C{sub 3}N{sub 4} was characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), high-resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectra (FTIR), UV–vis diffuse reflectance absorption spectra (UV-DRS), photoelectrochemical measurement and photoluminescence spectra (PL). The photocatalytic activities of phosphorus doped g-C{sub 3}N{sub 4} samples were evaluated by degradation of Rhodamine B (RhB) solution under visible light irradiation. The results showed that the phosphorus doped g-C{sub 3}N{sub 4} had a superior photocatalytic activity than that of pristine g-C{sub 3}N{sub 4}, attributing to the phosphorus atoms substituting carbon atoms of g-C{sub 3}N{sub 4} frameworks to result in light harvesting enhancement and delocalized π-conjugated system of this copolymer, beneficial for the increase of photocatalytic performance. The photoelectrochemical measurements also verified that the charge carrier separation efficiency was promoted by phosphorus doping g-C{sub 3}N{sub 4}. Moreover, the tests of radical scavengers demonstrated that the holes (h{sup +}) and superoxide radicals (·O{sub 2}{sup −}) were the main active species for the

  4. Particle flux and temperature dependence of carbon impurity production from an inertially-cooled limiter in tore supra

    International Nuclear Information System (INIS)

    DeMichelis, C.; Monier-Garbet, P.; Guilhem, D.

    1998-01-01

    A visible endoscope system and an infrared camera system have been used to study the flux of carbon from an inertially-cooled graphite limiter in Tore Supra. From the variation in the carbon flux with plasma parameters new data have been obtained describing the dependence of radiation enhanced sublimation (RES) and chemical sputtering on incident ion flux. Other characteristics of RES under plasma operation conditions have also been studied. The dependence of RES on incident deuterium particle flux density is found to be in reasonable agreement with the expected particle flux scaling over a range of particle fluxes varying by a factor ∼ 25, extending the present scaling to higher flux density values. Chemical sputtering has been observed, but only in regions of the limiter with low incident deuterium fluxes. Values inferred for the chemical sputtering yield are similar to those measured with a temperature controlled test limiter in Textor. (author)

  5. Synthesis of graphitized carbon, nanodiamond and graphene supported Li4Ti5O12 and comparison of their electrochemical performance as anodes for lithium ion batteries

    Science.gov (United States)

    Yang, Shuai; Miao, Juan; Wang, Qiufen; Lu, Mengwei; Sun, Jiufang; Wen, Tao

    2016-12-01

    Graphitized carbon (GC), nanodiamond (ND) and graphene (GE) supported Li4Ti5O12 (LTO) composites have been synthesized via a solid-state reaction, respectively. The particle sizes of LTO/GC, LTO/ND and LTO/GE are smaller than pure LTO. When tested as the anode for lithium ion batteries, the discharge capacities of LTO, LTO/GC, LTO/ND and LTO/GE composites are 100.1 mAh g-1, 150.4 mAh g-1, 90.4 mAh g-1 and 218.3 mAh g-1 at the current density of 175 mA g-1 after 500 cycles. Their rate capacities retain 59.8%, 80.0%, 81.0% and 85.7% at the current density of 175 mA g-1, 438 mA g-1, 875 mA g-1 and 175 mA g-1, respectively. Moreover, the recovery rates of their rate capacities are 78.6%, 83.4%, 88.9% and 90.1% when returned to the current density of 175 mA g-1, respectively. The reasons can be attributed to the synergistic effect between GC (ND and GE) and LTO as well as the features of the different carbon supports. This strategy, with the carbon constituting a good supporting structure, is an effective way to improve the cycling performance of anode materials for lithium ion batteries.

  6. Source contributions to atmospheric fine carbon particle concentrations

    Science.gov (United States)

    Andrew Gray, H.; Cass, Glen R.

    A Lagrangian particle-in-cell air quality model has been developed that facilitates the study of source contributions to atmospheric fine elemental carbon and fine primary total carbon particle concentrations. Model performance was tested using spatially and temporally resolved emissions and air quality data gathered for this purpose in the Los Angeles area for the year 1982. It was shown that black elemental carbon (EC) particle concentrations in that city were dominated by emissions from diesel engines including both on-highway and off-highway applications. Fine primary total carbon particle concentrations (TC=EC+organic carbon) resulted from the accumulation of small increments from a great variety of emission source types including both gasoline and diesel powered highway vehicles, stationary source fuel oil and gas combustion, industrial processes, paved road dust, fireplaces, cigarettes and food cooking (e.g. charbroilers). Strategies for black elemental carbon particle concentration control will of necessity need to focus on diesel engines, while controls directed at total carbon particle concentrations will have to be diversified over a great many source types.

  7. Ignition of a Combustible Atmosphere by Incandescent Carbon Wear Particles

    Science.gov (United States)

    Buckley, Donald H.; Swikert, Max A.; Johnson, Robert L.

    1960-01-01

    A study was made to determine whether carbon wear particles from carbon elements in sliding contact with a metal surface were sufficiently hot to cause ignition of a combustible atmosphere. In some machinery, electric potential differences and currents may appear at the carbon-metal interface. For this reason the effect of these voltages and currents on the ability of carbon wear particles to cause ignition was evaluated. The test specimens used in the investigation were carbon vanes taken from a fuel pump and flat 21-inch-diameter 2 metal disks (440-C stainless steel) representing the pump housing. During each experiment a vane was loaded against a disk with a 0.5-pound force, and the disk was rotated to give a surface speed of 3140 feet per minute. The chamber of the apparatus that housed the vane and the disk was filled with a combustible mixture of air and propane. Various voltages and amperages were applied across the vane-disk interface. Experiments were conducted at temperatures of 75, 350, 400, and 450 F. Fires were produced by incandescent carbon wear particles obtained at conditions of electric potential as low as 106 volts and 0.3 ampere at 400 F. Ignitions were obtained only with carbon wear particles produced with an electric potential across the carbon-vane-disk interface. No ignitions were obtained with carbon wear particles produced in the absence of this potential; also, the potential difference produced no ignitions in the absence of carbon wear particles. A film supplement showing ignition by incandescent wear particles is available.

  8. Performance of brazed graphite, carbon-fiber composite, and TZM materials for actively cooled structures: qualification tests

    International Nuclear Information System (INIS)

    Smid, I.; Croessmann, C. D.; Watson, R. D.; Linke, J.; Cardella, A.; Bolt, H.; Reheis, N.; Kny, E.

    1995-01-01

    The divertor of a near-term fusion device has to withstand high heat fluxes, heat shocks, and erosion caused by the plasma. Furthermore, it has to be maintainable through remote techniques. Above all, a good heat removal capability across the interface (low-Z armor/heat sink) plus overall integrity after many operational cycles are needed. To meet all these requirements, an active metal brazing technique is applied to bond graphite and carbon-fiber composite materials to a heat sink consisting of a Mo-41Re coolant tube through a TZM body. Plain brazed graphite and TZM tiles are tested for their fusion-relevant properties. The interfaces appear undamaged after thermal cycling when the melting point of the braze joint is not exceeded and when the graphite armor is > 4 mm thick. High heat flux tests are performed on three actively cooled divertor targets. The braze joints show no sign of failure after exposure to thermal loads ∼ 25 % higher than the design value surface heat flux of 10 MW/m 2 . (author)

  9. Ultrathin nitrogen-doped graphitized carbon shell encapsulating CoRu bimetallic nanoparticles for enhanced electrocatalytic hydrogen evolution

    Science.gov (United States)

    Xu, You; Li, Yinghao; Yin, Shuli; Yu, Hongjie; Xue, Hairong; Li, Xiaonian; Wang, Hongjing; Wang, Liang

    2018-06-01

    Design of highly active and cost-effective electrocatalysts is very important for the generation of hydrogen by electrochemical water-splitting. Herein, we report the fabrication of ultrathin nitrogen-doped graphitized carbon shell encapsulating CoRu bimetallic nanoparticles (CoRu@NCs) and demonstrate their promising feasibility for efficiently catalyzing the hydrogen evolution reaction (HER) over a wide pH range. The resultant CoRu@NC nanohybrids possess an alloy–carbon core–shell structure with encapsulated low-ruthenium-content CoRu bimetallic alloy nanoparticles (10–30 nm) as the core and ultrathin nitrogen-doped graphitized carbon layers (2–6 layers) as the shell. Remarkably, the optimized catalyst (CoRu@NC-2 sample) with a Ru content as low as 2.04 wt% shows superior catalytic activity and excellent durability for HER in acidic, neutral, and alkaline conditions. This work offers a new method for the design and synthesis of non-platium-based electrocatalysts for HER in all-pH.

  10. Stabilization of amorphous calcium carbonate by controlling its particle size

    NARCIS (Netherlands)

    Nudelman, F.; Sonmezler, E.; Bomans, P.H.H.; With, de G.; Sommerdijk, N.A.J.M.

    2010-01-01

    Amorphous calcium carbonate (ACC) nanoparticles of different size are prepared using a flow system. Post-synthesis stabilization with a layer of poly[(a,ß)-DL-aspartic acid] leads to stabilization of the ACC, but only for particles

  11. Single particle composition measurements of artificial Calcium Carbonate aerosols

    Science.gov (United States)

    Zorn, S. R.; Mentel, T. F.; Schwinger, T.; Croteau, P. L.; Jayne, J.; Worsnop, D. R.; Trimborn, A.

    2012-12-01

    Mineral dust, with an estimated total source from natural and anthropogenic emissions of up to 2800 Tg/yr, is one of the two largest contributors to total aerosol mass, with only Sea salt having a similar source strength (up to 2600 Tg/yr). The composition of dust particles varies strongly depending on the production process and, most importantly, the source location. Therefore, the composition of single dust particles can be used both to trace source regions of air masses as well as to identify chemical aging processes. Here we present results of laboratory studies on generating artificial calcium carbonate (CaCO3) particles, a model compound for carbonaceous mineral dust particles. Particles were generated by atomizing an aqueous hydrogen carbonate solution. Water was removed using a silica diffusion dryer., then the particles were processed in an oven at temperatures up to 900°C, converting the hydrogen carbonate to its anhydrous form. The resulting aerosol was analyzed using an on-line single particle laser ablation aerosol particle time-of-flight mass spectrometer (LAAPTOF). The results confirm the conversion to calcium carbonate, and validate that the produced particles indeed can be used as a model compound for carbonaceous dust aerosols.

  12. Effects of Propylene Carbonate Content in CsPF6-Containing Electrolytes on the Enhanced Performances of Graphite Electrode for Lithium-Ion Batteries

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, Jianming; Yan, Pengfei; Cao, Ruiguo; Xiang, Hongfa; Engelhard, Mark H.; Polzin, Bryant; Wang, Chong M.; Zhang, Jiguang; Xu, Wu

    2016-02-10

    Cesium salt has been demonstrated as an efficient electrolyte additive in suppressing the lithium (Li) dendrite formation and directing the formation of an ultrathin and stable solid electrolyte interphase (SEI) even in propylene carbonate (PC)-ethylene carbonate (EC)-based electrolytes. Here, we further investigate the effect of PC content in the presence of CsPF6 additive (0.05 M) on the performances of graphite electrode in Li||graphite half cells and in graphite||LiNi0.80Co0.15Al0.05O2 (NCA) full cells. It is found that the performance of graphite electrode is also affected by PC content even though CsPF6 additive is present in the electrolytes. An optimal PC content of 20% by weight in the solvent mixtures is identified. The enhanced electrochemical performance of graphite electrode is attributed to the synergistic effects of the Cs+ additive and the PC solvent. The formation of a robust, ultrathin and compact SEI layer containing lithium-enriched species on the graphite electrode, directed by Cs+, effectively suppresses the PC co-intercalation and thus prevents the graphite exfoliation. This SEI layer is only permeable for de-solvated Li+ ions and allows fast Li+ ion transport through it, which therefore largely alleviates the Li dendrite formation on graphite electrode during lithiation even at high current densities. The presence of low-melting-point PC solvent also enables the sustainable operation of the graphite||NCA full cells under a wide spectrum of temperatures. The fundamental findings of this work shed light on the importance of manipulating/maintaining the electrode/electrolyte interphasial stability in a variety of energy storage devices.

  13. Pt coating on flame-generated carbon particles

    International Nuclear Information System (INIS)

    Choi, In Dae; Lee, Dong Geun

    2008-01-01

    Carbon black, activated carbon and carbon nanotube have been used as supporting materials for precious metal catalysts used in fuel cell electrodes. One-step flame synthesis method is used to coat 2-5nm Pt dots on flame-generated carbon particles. By adjusting flame temperature, gas flow rates and resident time of particles in flame, we can obtain Pt/C nano catalyst-support composite particles. Additional injection of hydrogen gas facilitates pyrolysis of Pt precursor in flame. The size of as-incepted Pt dots increases along the flame due to longer resident time and sintering in high temperature flame. Surface coverage and dispersion of the Pt dots is varied at different sampling heights and confirmed by Transmission Electron Microscopy (TEM), Energy Dispersive Spectra (EDS) and X-Ray Diffraction (XRD). Crystallinity and surface bonding groups of carbon are investigated through X-ray Photoelectron Spectroscoy (XPS) and Raman spectroscopy

  14. Electropolymerization of 3-aminophenol on carbon graphite surface: Electric and morphologic properties

    International Nuclear Information System (INIS)

    Franco, Diego L.; Afonso, Andre S.; Vieira, Sabrina N.; Ferreira, Lucas F.; Goncalves, Rafael A.; Brito-Madurro, Ana G.; Madurro, Joao M.

    2008-01-01

    This paper reports the formation of electropolymerized films derived from 3-aminophenol on graphite electrode by cyclic voltammetry, prepared in different pH conditions. With increase of pH values, a shift of the oxidation potential of 3-aminophenol to more cathodic potentials was observed. 3-Aminophenol electrooxidation, in acid and basic media, yielded polymeric films onto graphite surface. In ferrocyanide/ferricyanide solution, the polymer produced in acid medium showed higher electron transfer efficiency. Scanning electron microscopy (SEM), atomic force microscopy (AFM), and FT-IR were used to investigate some properties of the graphite electrode modified with poly(3-aminophenol). Scanning electron microscopy showed that the morphology of the films is strongly dependent on the pH of the electropolymerization medium. FT-IR spectra of polymer films produced for either acid or basic media suggest that the monomer is polymerized by NH 2 group

  15. Electropolymerization of 3-aminophenol on carbon graphite surface: Electric and morphologic properties

    Energy Technology Data Exchange (ETDEWEB)

    Franco, Diego L.; Afonso, Andre S.; Vieira, Sabrina N.; Ferreira, Lucas F. [Institute of Chemistry, Federal University of Uberlandia, Av. Joao Naves de Avila 2121, 38400-902 Uberlandia (Brazil); Goncalves, Rafael A. [School of Mechanical Engineering, Federal University of Uberlandia, Av. Joao Naves de Avila 2121, 38400-902 Uberlandia (Brazil); Brito-Madurro, Ana G. [Institute of Chemistry, Federal University of Uberlandia, Av. Joao Naves de Avila 2121, 38400-902 Uberlandia (Brazil); Madurro, Joao M. [Institute of Chemistry, Federal University of Uberlandia, Av. Joao Naves de Avila 2121, 38400-902 Uberlandia (Brazil)], E-mail: jmadurro@ufu.br

    2008-02-15

    This paper reports the formation of electropolymerized films derived from 3-aminophenol on graphite electrode by cyclic voltammetry, prepared in different pH conditions. With increase of pH values, a shift of the oxidation potential of 3-aminophenol to more cathodic potentials was observed. 3-Aminophenol electrooxidation, in acid and basic media, yielded polymeric films onto graphite surface. In ferrocyanide/ferricyanide solution, the polymer produced in acid medium showed higher electron transfer efficiency. Scanning electron microscopy (SEM), atomic force microscopy (AFM), and FT-IR were used to investigate some properties of the graphite electrode modified with poly(3-aminophenol). Scanning electron microscopy showed that the morphology of the films is strongly dependent on the pH of the electropolymerization medium. FT-IR spectra of polymer films produced for either acid or basic media suggest that the monomer is polymerized by NH{sub 2} group.

  16. Contribution to the study of the reactivity of graphite with respect to carbon dioxide and air; Contribution a l'etude de la reactivite du graphite vis-a-vis du gaz corbonique et de l'air

    Energy Technology Data Exchange (ETDEWEB)

    Jacquet, M [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

    1959-09-15

    The oxidation of nuclear-quality graphite by air and carbon dioxide has been studied at temperatures at which the reaction becomes measurable. These experiments have been carried out on graphites differing in the concentration and nature of their ash, and in their mode of preparation. The reaction velocities measured have been compared in an attempt to correlate these two factors. Ten types of graphite have thus been studied. Since the oxidation reactions are of the type gas-solid, their velocities have also been compared to the BET surface areas of the graphite studied and to the diameter distribution of the pores of this surface. The conclusion is that, even for these low impurity contents, the law relating the reaction velocity to the surface is masked by the impurities which appear to behave as preferential reaction sites. This has been shown by carrying out successive purifications on various types of graphite, which treatment results in an important decrease in the reactivity of all the samples studied. (author) [French] On a etudie l'oxydation de graphites de qualites nucleaires par l'air et par le gaz carbonique, a des temperatures telles que la reaction commence a etre mesurable. Ces essais ont porte sur des graphites differents aux points de vue de la concentration et de la nature des cendres, et differents par le mode de preparation. Les vitesses de reaction mesurees ont ete comparees afin de tenter de les relier a ces deux facteurs. Dix qualites de graphite ont ainsi ete etudiees. Les reactions d'oxydation etant des reactions gaz-solide, les vitesses ont ete egalement comparees aux surfaces specifiques B.E.T. des echantillons de graphite etudies et a la repartition par diametres des pores de cette surface. La conclusion est que, meme a ces teneurs faibles en impuretes, la loi de variation de la vitesse de reaction en fonction de la surface est masquee par les impuretes qui paraissent jouer le role de sites privilegies de reaction comme l'ont montre les

  17. Measurements of anomalous neutron transport in bulk graphite

    International Nuclear Information System (INIS)

    Bowman, C.D.; Smith, G.A.; Vogelaar, B.; Howell, C.R.; Bilpuch, E.G.; Tornow, W.

    2003-01-01

    The neutron absorption of bulk granular graphite has been measured in a classical exponential diffusion experiment. Our first measurements of April 2002 implementing both exponential decay and pulsed die-away experiments and using the TUNL pulsed accelerator at Duke University as a neutron source indicated a capture cross section for graphite a striking factor of three lower than the measured value for carbon of 3.4 millibarns. Therefore a new exponential experiment with an improved geometry enabling greater accuracy has been performed giving an apparent cross section for carbon in the form of bulk granular graphite of less than 0.5 millibarns. This result confirms our first result and is also consistent with less than one part per million of boron in our graphite. The bulk density of the graphite is 1.02 compared with the actual particle density of 1.60 indicating a packing fraction of 0.64 or a void fraction of 0.36. We suspect that the apparent suppression of absorption in bulk graphite may be associated with the strong coherent diffraction of neutrons that dominates neutron transport in graphite. Coherent diffraction has never been taken into account in graphite reactor design and no neutron transport code including general use codes such as MCNP incorporate diffraction effects even though diffraction dominates many practical thermal neutron transport problems. (orig.)

  18. Measurements of anomalous neutron transport in bulk graphite

    Energy Technology Data Exchange (ETDEWEB)

    Bowman, C.D.; Smith, G.A. [ADNA Corp., Los Alamos, NM (United States); Vogelaar, B. [Virginia Tech., Blacksburg, VA (United States); Howell, C.R.; Bilpuch, E.G.; Tornow, W. [Triangle Univ. Nuclear Lab., Duke Univ., Durham, NC (United States)

    2003-07-01

    The neutron absorption of bulk granular graphite has been measured in a classical exponential diffusion experiment. Our first measurements of April 2002 implementing both exponential decay and pulsed die-away experiments and using the TUNL pulsed accelerator at Duke University as a neutron source indicated a capture cross section for graphite a striking factor of three lower than the measured value for carbon of 3.4 millibarns. Therefore a new exponential experiment with an improved geometry enabling greater accuracy has been performed giving an apparent cross section for carbon in the form of bulk granular graphite of less than 0.5 millibarns. This result confirms our first result and is also consistent with less than one part per million of boron in our graphite. The bulk density of the graphite is 1.02 compared with the actual particle density of 1.60 indicating a packing fraction of 0.64 or a void fraction of 0.36. We suspect that the apparent suppression of absorption in bulk graphite may be associated with the strong coherent diffraction of neutrons that dominates neutron transport in graphite. Coherent diffraction has never been taken into account in graphite reactor design and no neutron transport code including general use codes such as MCNP incorporate diffraction effects even though diffraction dominates many practical thermal neutron transport problems. (orig.)

  19. Classroom Demonstration: Combustion of Diamond to Carbon Dioxide Followed by Reduction to Graphite

    Science.gov (United States)

    Miyauchi, Takuya; Kamata, Masahiro

    2012-01-01

    An educational demonstration shows the combustion of carbon to carbon dioxide and then the reduction of carbon dioxide to carbon. A melee diamond is the source of the carbon and the reaction is carried out in a closed flask. The demonstration helps students to realize that diamonds are made of carbon and that atoms do not change or vanish in…

  20. Highly conductive bridges between graphite spheres to improve the cycle performance of a graphite anode in lithium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Hongyu [IM and T Ltd., Advanced Research Center, Saga University, Yoga-machi 1341, Saga 840-0047 (Japan); Umeno, Tatsuo; Mizuma, Koutarou [Research Center, Mitsui Mining Co. Ltd., Hibiki-machi 1-3, Wakamatsu-ku, Kitakyushu 808-0021 (Japan); Yoshio, Masaki [Advanced Research Center, Saga University, Yoga-machi 1341, Saga 840-0047 (Japan)

    2008-01-10

    Spherical carbon-coated natural graphite (SCCNG) is a promising anode material for lithium-ion batteries, but the smooth surface of graphite spheres is difficult to wet with an aqueous binder solution, and lacks electrical contacts. As a result, the cycle performance of such a graphite anode material is not satisfactory. An effective method has been introduced to tightly connect adjacent SCCNG particles by a highly conductive binder, viz. acetylene black bridges. The effect of the conductive bridges on the cyclability of SCCNG electrode has been investigated. (author)

  1. Catalytic Graphitization for Preparation of Porous Carbon Material Derived from Bamboo Precursor and Performance as Electrode of Electrical Double-Layer Capacitor

    Science.gov (United States)

    Tsubota, Toshiki; Maguchi, Yuta; Kamimura, Sunao; Ohno, Teruhisa; Yasuoka, Takehiro; Nishida, Haruo

    2015-12-01

    The combination of addition of Fe (as a catalyst for graphitization) and CO2 activation (a kind of gaseous activation) was applied to prepare a porous carbon material from bamboo powder (a waste product of superheated steam treatment). Regardless of the heat treatment temperature, many macropores were successfully formed after the heating process by removal of Fe compounds. A turbostratic carbon structure was generated in the Fe-added sample heated at 850°C. It was confirmed that the added Fe acted as a template for pore formation. Moreover, it was confirmed that the added Fe acted as a catalyst for graphitization. The resulting electrochemical performance as the electrode of an electrical double-layer capacitor, as demonstrated by cyclic voltammetry, electrochemical impedance spectroscopy, and charge-discharge testing, could be explained based on the graphitization and activation effects. Addition of Fe could affect the electrical properties of carbon material derived from bamboo.

  2. Fluidized bed reactor for working up carbon coated particles

    International Nuclear Information System (INIS)

    Marschollek, M.; Simon, W.; Walter, C.

    1981-01-01

    A fluidized bed reactor is described for working up carbon coated particles, particularly nuclear fuel particles or fertile material particles consisting essentially of a cylindrical portion connected to a conical portion. Gas supply pipes, gas distribution space and gas distribution heads are provided within the conical reactor lower portion, the gas distribution members being arranged in at least two superimposed planes and distributed symmetrically over the cross-section of the reactor

  3. Effects of Propylene Carbonate Content in CsPF 6 -Containing Electrolytes on the Enhanced Performances of Graphite Electrode for Lithium-Ion Batteries

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, Jianming; Yan, Pengfei; Cao, Ruiguo; Xiang, Hongfa [School of; Engelhard, Mark H.; Polzin, Bryant J. [Chemical Sciences and Engineering Division, Argonne National Laboratory, 9700 South Cass Avenue, Argonne, Illinois 60439, United States; Wang, Chongmin; Zhang, Ji-Guang; Xu, Wu

    2016-02-15

    The effects Of propylene carbonate (PC) content in CsPF6-containing electrolytes on the performances of graphite electrode in lithium half cells and in graphite parallel to LiNi0.80Co0.15Al0.05O2 (NCA) full cells are investigated. It is found that the performance of graphite electrode is significantly-affected by PC content in the CsPF6-containing electrolytes. An optimal PC content of 20% by weight in the solvent mixtures is identified. The enhanced electrochemical performance of graphite electrode can be attributed to the synergistic effects of the PC solvent and the Cs+ additive. The synergistic effects of Cs+ additive and appropriate amount of PC enable the formation of a robust, ultrathin, and compact solid electrolyte interphase (SEI) layer on the surface of graphite electrode, which is only permeable for desolvated Li+ ions and allows fast Li+ ion transport through it. Therefore, this SEI layer effectively suppresses the PC cointercalation and largely alleviates the Li dendrite formation on graphite electrode during lithiation even at relatively high current densities. The presence of low-melting-point PC solvent improves the sustainable operation of graphite parallel to NCA full cells under a wide temperature range. The fundamental findings also shed light On the importance of manipulating/maintaining the electrode/electrolyte interphasial stability in various energy-storage devices.

  4. Mechanical behaviour of cyclic olefin copolymer/exfoliated graphite nanoplatelets nanocomposites foamed by supercritical carbon dioxide

    Czech Academy of Sciences Publication Activity Database

    Biani, A.; Dorigato, A.; Bonani, W.; Šlouf, Miroslav; Pegoretti, A.

    2016-01-01

    Roč. 10, č. 12 (2016), s. 977-989 ISSN 1788-618X R&D Projects: GA TA ČR(CZ) TE01020118; GA MŠk(CZ) LO1507 Institutional support: RVO:61389013 Keywords : nanocomposites * foams * graphite nanoplatelets Subject RIV: CD - Macromolecular Chemistry Impact factor: 2.983, year: 2016

  5. Graphite in Science and Nuclear Technique

    OpenAIRE

    Zhmurikov, E. I.; Bubnenkov, I. A.; Dremov, V. V.; Samarin, S. I.; Pokrovsky, A. S.; Harkov, D. V.

    2013-01-01

    The monograph is devoted to the application of graphite and graphite composites in science and technology. The structure and electrical properties, the technological aspects of production of high-strength synthetic graphites, the dynamics of the graphite destruction, traditionally used in the nuclear industry are discussed. It is focuses on the characteristics of graphitization and properties of graphite composites based on carbon isotope 13C. The book is based, generally, on the original res...

  6. Liquid-phase pulsed laser ablation synthesis of graphitized carbon-encapsulated palladium core–shell nanospheres for catalytic reduction of nitrobenzene to aniline

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Yu-jin; Ma, Rory; Reddy, D. Amaranatha; Kim, Tae Kyu, E-mail: tkkim@pusan.ac.kr

    2015-12-01

    Graphical abstract: - Highlights: • Graphitized carbon-encapsulated palladium core–shell nanospheres fabricated by laser ablation. • Physical characterizations of synthesized Pd@C nanospheres. • Assessments of catalytic performance of Pd@C nanospheres for the reduction of nitrobenzene to aniline. • Significant improvement of the catalytic activity due to the graphitized carbon-layered structure and the high specific surface area. - Abstract: Graphitized carbon-encapsulated palladium (Pd) core–shell nanospheres were produced via pulsed laser ablation of a solid Pd foil target submerged in acetonitrile. The microstructural features and optical properties of these nanospheres were characterized via high resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and UV-visible spectroscopy. Microstructural analysis indicated that the core–shell nanostructures consisted of single-crystalline cubic metallic Pd spheres that serve as the core material, over which graphitized carbon was anchored as a heterogeneous shell. The absorbance spectrum of the synthesized nanostructures exhibited a broad (absorption) band at ∼264 nm; this band corresponded to the typical inter-band transition of a metallic system and resulted possibly from the absorbance of the ionic Pd{sup 2+}. The catalytic properties of the Pd and Pd@C core–shell nanostructures were investigated using the reduction of nitrobenzene to aniline by an excess amount of NaBH{sub 4} in an aqueous solution at room temperature, as a model reaction. Owing to the graphitized carbon-layered structure and the high specific surface area, the resulting Pd@C nanostructures exhibited higher conversion efficiencies than their bare Pd counterparts. In fact, the layered structure provided access to the surface of the Pd nanostructures for the hydrogenation reaction, owing to the synergistic effect between graphitized carbon and the nanostructures. Their

  7. Liquid-phase pulsed laser ablation synthesis of graphitized carbon-encapsulated palladium core–shell nanospheres for catalytic reduction of nitrobenzene to aniline

    International Nuclear Information System (INIS)

    Kim, Yu-jin; Ma, Rory; Reddy, D. Amaranatha; Kim, Tae Kyu

    2015-01-01

    Graphical abstract: - Highlights: • Graphitized carbon-encapsulated palladium core–shell nanospheres fabricated by laser ablation. • Physical characterizations of synthesized Pd@C nanospheres. • Assessments of catalytic performance of Pd@C nanospheres for the reduction of nitrobenzene to aniline. • Significant improvement of the catalytic activity due to the graphitized carbon-layered structure and the high specific surface area. - Abstract: Graphitized carbon-encapsulated palladium (Pd) core–shell nanospheres were produced via pulsed laser ablation of a solid Pd foil target submerged in acetonitrile. The microstructural features and optical properties of these nanospheres were characterized via high resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and UV-visible spectroscopy. Microstructural analysis indicated that the core–shell nanostructures consisted of single-crystalline cubic metallic Pd spheres that serve as the core material, over which graphitized carbon was anchored as a heterogeneous shell. The absorbance spectrum of the synthesized nanostructures exhibited a broad (absorption) band at ∼264 nm; this band corresponded to the typical inter-band transition of a metallic system and resulted possibly from the absorbance of the ionic Pd 2+ . The catalytic properties of the Pd and Pd@C core–shell nanostructures were investigated using the reduction of nitrobenzene to aniline by an excess amount of NaBH 4 in an aqueous solution at room temperature, as a model reaction. Owing to the graphitized carbon-layered structure and the high specific surface area, the resulting Pd@C nanostructures exhibited higher conversion efficiencies than their bare Pd counterparts. In fact, the layered structure provided access to the surface of the Pd nanostructures for the hydrogenation reaction, owing to the synergistic effect between graphitized carbon and the nanostructures. Their unique

  8. Graphite-based photovoltaic cells

    Science.gov (United States)

    Lagally, Max; Liu, Feng

    2010-12-28

    The present invention uses lithographically patterned graphite stacks as the basic building elements of an efficient and economical photovoltaic cell. The basic design of the graphite-based photovoltaic cells includes a plurality of spatially separated graphite stacks, each comprising a plurality of vertically stacked, semiconducting graphene sheets (carbon nanoribbons) bridging electrically conductive contacts.

  9. Commercial expanded graphite as a low-cost, long-cycling life anode for potassium-ion batteries with conventional carbonate electrolyte

    Science.gov (United States)

    An, Yongling; Fei, Huifang; Zeng, Guifang; Ci, Lijie; Xi, Baojuan; Xiong, Shenglin; Feng, Jinkui

    2018-02-01

    Design and synthesis of capable anode materials that can store the large size K+ is the key of development for potassium-ion batteries. The low-cost and commercial expanded graphite with large particles is a graphite-derived material with good conductivity and enlarged interlayer spaces to boost the potassium ion diffusion coefficient during charge/discharge process. Thus, we achieve excellent anode performance for potassium-ion batteries based on an expanded graphite. It can deliver a capacity of 263 mAh g-1 at the rate of 10 mA g-1 and the reversible capacity remains almost unchanged after 500 cycles at a high rate of 200 mA g-1 with a coulombic efficiency of around 100%. The potassium storage mechanism is investigated by the ex situ XRD technique. This excellent potassium storage performance will make the expanded graphite promising anode candidate for potassium ion batteries.

  10. Estimation of Wear Behavior of Polyphenylene Sulphide Composites Reinforced with Glass/Carbon Fibers, Graphite and Polytetrafluoroethylene, by Pin-on-disc Test

    Directory of Open Access Journals (Sweden)

    M.A.C. Besnea

    2015-03-01

    Full Text Available Wear behavior of polyphenylene sulphide composites was investigated according to load and test speed. Two types of materials were studied: first, with 40 wt% glass fiber, and second, with 10 wt% carbon fiber, 10 wt% graphite and 10 wt%. Tribological tests were performed on the universal tribometer UMT-2, using a pin-on-disc device. The friction coefficient and wear rate for the composites were analyzed. As a result of experimental tests, it was established that polymer composite with polyphenylene sulphide matrix, carbon fibers, graphite and polytetrafluorethylene exhibit good wear behavior under operating conditions.

  11. Synthesis of graphitized carbon, nanodiamond and graphene supported Li_4Ti_5O_1_2 and comparison of their electrochemical performance as anodes for lithium ion batteries

    International Nuclear Information System (INIS)

    Yang, Shuai; Miao, Juan; Wang, Qiufen; Lu, Mengwei; Sun, Jiufang; Wen, Tao

    2016-01-01

    Highlights: • We synthesized graphitized carbon, nanodiamond and graphene supported Li_4Ti_5O_1_2, respectively. • The order of the capacities is LTO/GE > LTO/GC > LTO > LTO/ND after 500 cycles. • The rate capabilities and cycling stabilities are in the order of LTO/GE > LTO/ND > LTO/GC > LTO. - Abstract: Graphitized carbon (GC), nanodiamond (ND) and graphene (GE) supported Li_4Ti_5O_1_2 (LTO) composites have been synthesized via a solid-state reaction, respectively. The particle sizes of LTO/GC, LTO/ND and LTO/GE are smaller than pure LTO. When tested as the anode for lithium ion batteries, the discharge capacities of LTO, LTO/GC, LTO/ND and LTO/GE composites are 100.1 mAh g"−"1, 150.4 mAh g"−"1, 90.4 mAh g"−"1 and 218.3 mAh g"−"1 at the current density of 175 mA g"−"1 after 500 cycles. Their rate capacities retain 59.8%, 80.0%, 81.0% and 85.7% at the current density of 175 mA g"−"1, 438 mA g"−"1, 875 mA g"−"1 and 175 mA g"−"1, respectively. Moreover, the recovery rates of their rate capacities are 78.6%, 83.4%, 88.9% and 90.1% when returned to the current density of 175 mA g"−"1, respectively. The reasons can be attributed to the synergistic effect between GC (ND and GE) and LTO as well as the features of the different carbon supports. This strategy, with the carbon constituting a good supporting structure, is an effective way to improve the cycling performance of anode materials for lithium ion batteries.

  12. Comparison on exfoliated graphene nano-sheets and triturated graphite nano-particles for mode-locking the Erbium-doped fibre lasers

    Science.gov (United States)

    Yang, Chun-Yu; Lin, Yung-Hsiang; Wu, Chung-Lun; Cheng, Chih-Hsien; Tsai, Din-Ping; Lin, Gong-Ru

    2018-06-01

    Comparisons on exfoliated graphene nano-sheets and triturated graphite nano-particles for mode-locking the Erbium-doped fiber lasers (EDFLs) are performed. As opposed to the graphite nano-particles obtained by physically triturating the graphite foil, the tri-layer graphene nano-sheets is obtained by electrochemically exfoliating the graphite foil. To precisely control the size dispersion and the layer number of the exfoliated graphene nano-sheet, both the bias of electrochemical exfoliation and the speed of centrifugation are optimized. Under a threshold exfoliation bias of 3 volts and a centrifugation at 1000 rpm, graphene nano-sheets with an average diameter of 100  ±  40 nm can be obtained. The graphene nano-sheets with an area density of 15 #/µm2 are directly imprinted onto the end-face of a single-mode fiber made patchcord connector inside the EDFL cavity. Such electrochemically exfoliated graphene nano-sheets show comparable saturable absorption with standard single-graphene and perform the self-amplitude modulation better than physically triturated graphite nano-particles. The linear transmittance and modulation depth of the inserted graphene nano-sheets are 92.5% and 53%, respectively. Under the operation with a power gain of 21.5 dB, the EDFL can be passively mode-locked to deliver a pulsewidth of 454.5 fs with a spectral linewidth of 5.6 nm. The time-bandwidth product of 0.31 is close to the transform limit. The Kelly sideband frequency spacing of 1.34 THz is used to calculate the chirp coefficient as  ‑0.0015.

  13. Uncovering the local inelastic interactions during manufacture of ductile cast iron: How the substructure of the graphite particles can induce residual stress concentrations in the matrix

    Science.gov (United States)

    Andriollo, Tito; Hellström, Kristina; Sonne, Mads Rostgaard; Thorborg, Jesper; Tiedje, Niels; Hattel, Jesper

    2018-02-01

    Recent X-ray diffraction (XRD) measurements have revealed that plastic deformation and a residual elastic strain field can be present around the graphite particles in ductile cast iron after manufacturing, probably due to some local mismatch in thermal contraction. However, as only one component of the elastic strain tensor could be obtained from the XRD data, the shape and magnitude of the associated residual stress field have remained unknown. To compensate for this and to provide theoretical insight into this unexplored topic, a combined experimental-numerical approach is presented in this paper. First, a material equivalent to the ductile cast iron matrix is manufactured and subjected to dilatometric and high-temperature tensile tests. Subsequently, a two-scale hierarchical top-down model is devised, calibrated on the basis of the collected data and used to simulate the interaction between the graphite particles and the matrix during manufacturing of the industrial part considered in the XRD study. The model indicates that, besides the viscoplastic deformation of the matrix, the effect of the inelastic deformation of the graphite has to be considered to explain the magnitude of the XRD strain. Moreover, the model shows that the large elastic strain perturbations recorded with XRD close to the graphite-matrix interface are not artifacts due to e.g. sharp gradients in chemical composition, but correspond to residual stress concentrations induced by the conical sectors forming the internal structure of the graphite particles. In contrast to common belief, these results thus suggest that ductile cast iron parts cannot be considered, in general, as stress-free at the microstructural scale.

  14. Low Secondary Electron Yield Carbon Coatings for Electron-cloud Mitigation in Modern Particle Accelerators

    CERN Document Server

    Yin Vallgren, Christina; Calatroni, Sergio; Chiggiato, Paolo; Costa Pinto, Pedro; Marques, Hugo; Neupert, Holger; Taborelli, Mauro; Vollenberg, Wilhelmus; Wevers, Ivo; Yaqub, Kashif

    2010-01-01

    Electron-cloud is one of the main limitations for particle accelerators with positively charged beams of high intensity and short bunch spacing, as the SPS at CERN. The Secondary Electron Yield (SEY) of the inner surface of the vacuum chamber is the main parameter governing the phenomenon. The effect could be eliminated by coating the vacuum chambers with a material of low SEY, which does not require bake-out and is robust against air exposure. For such a purpose amorphous carbon (a-C) coatings were produced by magnetron sputtering of graphite targets. They exhibit maximum SEY between 0.95 and 1.05 after air transfer to the measuring instrument. After 1 month of air exposure the SEY rises by 10 - 20 % of the initial values. Storage in desiccator or by packaging in Al foil makes this increase negligible. The coatings have a similar X-ray photoelectron spectroscopy (XPS) C1s spectrum for a large set of deposition parameters and exhibit an enlarged linewidth compared to HOPG graphite. The static outgassing witho...

  15. Diffusivities of Ag, Cs, Sr, and Kr in TRISO fuel particles and graphite

    Energy Technology Data Exchange (ETDEWEB)

    Collin, Blaise Paul [Idaho National Lab. (INL), Idaho Falls, ID (United States)

    2016-09-01

    Tri-structural isotropic (TRISO) coated particles have been developed and studied since the late 1950s when the concept of coated particles was invented by Roy Huddle of the United Kingdom Atomic Energy Authority. Several decades of work by half a dozen countries on fission product transport in TRISO fuel through numerous irradiation and heating experiments have led to several recommendations of transport data and to the adoption of various sets of diffusion coefficients. In 1997, the International Atomic Energy Agency (IAEA) gathered all these historical results and issued a technical document (TECDOC-978 [IAEA]) that summarizes these sets of recommended diffusion coefficients. Table 1 shows the reference literature articles for the diffusivities that have historically been recommended by the American and German TRISO fuel development programs and that are summarized in the IAEA report (see section 7 for full references of these articles).

  16. Electrochemical treatment of graphite

    Energy Technology Data Exchange (ETDEWEB)

    Podlovilin, V.I.; Egorov, I.M.; Zhernovoj, A.I.

    1983-01-01

    In the course of investigating various modes of electrochemical treatment (ECT) it has been found that graphite anode treatment begins under the ''glow mode''. A behaviour of some marks of graphite with the purpose of ECT technique development in different electrolytes has been tested. Electrolytes have been chosen of three types: highly alkaline (pH 13-14), neutral (pH-Z) and highly acidic (pH 1-2). For the first time parallel to mechanical electroerosion treatment, ECT of graphite and carbon graphite materials previously considered chemically neutral is proposed. ECT of carbon graphite materials has a number of advantages as compared with electroerrosion and mechanical ones with respect to the treatment rate and purity (ronghness) of the surface. A small quantity of sludge (6-8%) under ECT is in highly alkali electrolytes.

  17. Electrochemical treatment of graphite

    International Nuclear Information System (INIS)

    Podlovilin, V.I.; Egorov, I.M.; Zhernovoj, A.I.

    1983-01-01

    In the course of investigating various modes of electroche-- mical treatment (ECT) it has been found that graphite anode treatment begins under the ''glow mode''. A behaviour of some marks of graphite with the purpose of ECT technique development in different electrolytes has been tested. Electrolytes have been chosen of three types: highly alkaline (pH 13-14), neutral (pH-Z) and highly acidic (pH 1-2). For the first time parallel to mechanical electroerosion treatment ECT graphite and carbon graphite materials previously considered chemically neutral is proposed. ECT of carbon graphite materials has a number of advantages as compared with electroerrosion and mechanical ones this is treatment rate and purity (ronghness) of the surface. A sMall quantity of sludge (6-8%) under ECT is in highly alkali electrolytes

  18. Preparation of porous carbon particle with shell/core structure

    Directory of Open Access Journals (Sweden)

    2007-05-01

    Full Text Available Porous carbon particles with a shell/core structure have been prepared successfully by controlled precipitation of the polymer from droplets of oil-in-water emulsion, followed by curing and carbonization. The droplets of the oil phase are composed of phenolic resin (PFR, a good solvent (ethyl acetate and porogen (Poly(methyl methacrylate, PMMA. The microstructure was characterized in detail by scanning electron microscopy (SEM, transmission electron microscopy (TEM, nitrogen adsorption, and thermo gravimetric analysis (TGA. The obtained carbon particles have a capsular structure with a microporous carbon shell and a mesoporous carbon core. The BET surface area and porous volume are calculated to be 499 m2g-1 and 0.56 cm3g-1, respectively. The effects of the amount of porogen (PMMA, co-solvent (acetone and surfactant on the resultant structure were studied in detail.

  19. Direct synthesis of graphitic mesoporous carbon from green phenolic resins exposed to subsequent UV and IR laser irradiations

    Science.gov (United States)

    Sopronyi, Mihai; Sima, Felix; Vaulot, Cyril; Delmotte, Luc; Bahouka, Armel; Matei Ghimbeu, Camelia

    2016-01-01

    The design of mesoporous carbon materials with controlled textural and structural features by rapid, cost-effective and eco-friendly means is highly demanded for many fields of applications. We report herein on the fast and tailored synthesis of mesoporous carbon by UV and IR laser assisted irradiations of a solution consisting of green phenolic resins and surfactant agent. By tailoring the UV laser parameters such as energy, pulse repetition rate or exposure time carbon materials with different pore size, architecture and wall thickness were obtained. By increasing irradiation dose, the mesopore size diminishes in the favor of wall thickness while the morphology shifts from worm-like to an ordered hexagonal one. This was related to the intensification of phenolic resin cross-linking which induces the reduction of H-bonding with the template as highlighted by 13C and 1H NMR. In addition, mesoporous carbon with graphitic structure was obtained by IR laser irradiation at room temperature and in very short time periods compared to the classical long thermal treatment at very high temperatures. Therefore, the carbon texture and structure can be tuned only by playing with laser parameters, without extra chemicals, as usually required. PMID:28000781

  20. Preparation of pyrolytic carbon coating on graphite for inhibiting liquid fluoride salt and Xe{sup 135} penetration for molten salt breeder reactor

    Energy Technology Data Exchange (ETDEWEB)

    Song, Jinliang [Key Laboratory of Nuclear Radiation and Nuclear Energy Technology, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Zhao, Yanling, E-mail: jlsong1982@yeah.net [School of Materials Science and Engineering, University of Jinan, Jinan 250022 (China); He, Xiujie; Zhang, Baoliang [Key Laboratory of Nuclear Radiation and Nuclear Energy Technology, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Xu, Li [Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); He, Zhoutong; Zhang, DongSheng; Gao, Lina; Xia, Huihao; Zhou, Xingtai; Huai, Ping [Key Laboratory of Nuclear Radiation and Nuclear Energy Technology, Shanghai Institute of Applied Physics, Chinese Academy of Sciences, Shanghai 201800 (China); Bai, Shuo [Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China)

    2015-01-15

    Highlights: • Rough laminar pyrolytic carbon coating (RLPyC) is prepared by a fixed-bed method. • The salt-infiltration into IG-110 is 13.5%, less than 0.01% of RLPyC under 1.5 atm. • The helium diffusion coefficient of RLPyC coated graphite is 2.16 × 10{sup −8} cm{sup 2}/s. • The coated graphite can inhibit the liquid fluoride salt and Xe{sup 135} penetration. - Abstract: A fixed-bed deposition method was used to prepare rough laminar pyrolytic carbon coating (RLPyC) on graphite for inhibiting liquid fluoride salt and Xe{sup 135} penetration during use in molten salt breeder reactor. The RLPyC coating possessed a graphitization degree of 44% and had good contact with graphite substrate. A high-pressure reactor was constructed to evaluate the molten salt infiltration in the isostatic graphite (IG-110, TOYO TANSO CO., LTD.) and RLPyC coated graphite under 1.01, 1.52, 3.04, 5.07 and 10.13 × 10{sup 5} Pa for 12 h. Mercury injection and molten-salt infiltration experiments indicated the porosity and the salt-infiltration amount of 18.4% and 13.5 wt% under 1.52 × 10{sup 5} Pa of IG-110, which was much less than 1.2% and 0.06 wt% under 10.13 × 10{sup 5} Pa of the RLPyC, respectively. A vacuum device was constructed to evaluate the Xe{sup 135} penetration in the graphite. The helium diffusion coefficient of RLPyC coated graphite was 2.16 × 10{sup −12} m{sup 2}/s, much less than 1.21 × 10{sup −6} m{sup 2}/s of the graphite. Thermal cycle experiment indicated the coatings possessed excellent thermal stability. The coated graphite could effectively inhibit the liquid fluoride salt and Xe{sup 135} penetration.

  1. Papers about coated particles, graphitic and metallic materials for progressive high-temperature reactors at the Reactor Meeting 1978

    International Nuclear Information System (INIS)

    Rottmann, J.

    1978-09-01

    In the contributions, questions on the development, the radiation and the high-temperature behaviour and the characterization of fuel element particles are treated. Furthermore the resistance and radiation behaviour of graphitic materials are discussed. Finally, questions on the choice of high-temperature alloys for nuclear process heat facilities are discussed and the testing-equipment of the Nuclear Research Centre as well as first results of the long-time experiments are presented. The work was performed within the frame of the projects 'HTR-Fuel Element Cycle' and 'Prototype Nuclear Process Heat', which are sponsored by the Federal Ministry of Research and Technology of the Federal Republic of Germany and of the state of North-Rhine-Westfalia. Partner firms, who participate in the two projects are Gelsenberg AG, Gesellschaft fuer Hochtemperaturreaktor-Technik mbH, Hochtemperaturreaktor-Brennelement GmbH, Hochtemperatur-Reaktorbau GmbH, Kernforschungsanlage Juelich GmbH, NUKEM GmbH, SIGRI Elektrographit GmbH/Ringsdorff-Werke GmbH, Bergbauforschung GmbH und Rheinische Braunkohlenwerke AG. (orig./UA) [de

  2. Ammonia Synthesis using Ti and Nb Nitride Nano-particles Prepared by Mesoporous Graphitic C3N4

    KAUST Repository

    Kumagai, Hiromu

    2015-01-22

    TiN and NbN nanoparticles were synthesized from mesoporous graphitic C3N4 (mpg-C3N4) as a reactive template and used as the catalyst for ammonia synthesis. The obtained TiN and NbN nanoparticles possess high surface areas of 299 and 275 m2 g-1, respectively, making them attractive in the use of catalysis and support. Although most of the TiN and NbN particles show no measurable activity for ammonia formation, the nanoparticles enabled an ammonia synthesis rate of 31 μmol h-1 g-cat-1 at 673 K and 0.1 MPa of synthesis gas (N2 + 3H2) for both TiN and NbN catalysts. It is evident that the formation of nanoparticles with high nitride surface area is essential for the materials to function as catalysts in ammonia synthesis. The addition of Fe to TiN enhanced the ammonia synthesis activity, whereas it had detrimental effects on the catalytic activity of NbN. The properties of these catalysts in ammonia synthesis are discussed.

  3. Advanced High-Temperature Reactor for Production of Electricity and Hydrogen: Molten-Salt-Coolant, Graphite-Coated-Particle-Fuel

    International Nuclear Information System (INIS)

    Forsberg, C.W.

    2002-01-01

    The objective of the Advanced High-Temperature Reactor (AHTR) is to provide the very high temperatures necessary to enable low-cost (1) efficient thermochemical production of hydrogen and (2) efficient production of electricity. The proposed AHTR uses coated-particle graphite fuel similar to the fuel used in modular high-temperature gas-cooled reactors (MHTGRs), such as the General Atomics gas turbine-modular helium reactor (GT-MHR). However, unlike the MHTGRs, the AHTR uses a molten salt coolant with a pool configuration, similar to that of the PRISM liquid metal reactor. A multi-reheat helium Brayton (gas-turbine) cycle, with efficiencies >50%, is used to produce electricity. This approach (1) minimizes requirements for new technology development and (2) results in an advanced reactor concept that operates at essentially ambient pressures and at very high temperatures. The low-pressure molten-salt coolant, with its high heat capacity and natural circulation heat transfer capability, creates the potential for (1) exceptionally robust safety (including passive decay-heat removal) and (2) allows scaling to large reactor sizes [∼1000 Mw(e)] with passive safety systems to provide the potential for improved economics

  4. Investigation on particle-solid interactions

    International Nuclear Information System (INIS)

    Yano, Syukuro

    1988-08-01

    Basic processes in plasma-material interactions have been surveyed and reviewed. Problems concerned with carbon materials, which have been progressively used for the first wall and limiters in Tokamaks, are mainly discussed. Recent usage of carbon materials, basic properties and characteristics of carbon/graphite materials, desorption of gasses are described. As to the interactions of incident hydrogen isotope particles with graphite surface, data of trapping, depth profile, reemission, isotope exchange, and diffusion are reviewed and discussed. (author)

  5. The modeling and synthesis of nanodiamonds by laser ablation of graphite and diamond-like carbon in liquid-confined ambient

    Science.gov (United States)

    Basso, L.; Gorrini, F.; Bazzanella, N.; Cazzanelli, M.; Dorigoni, C.; Bifone, A.; Miotello, A.

    2018-01-01

    Nanodiamonds have attracted considerable interest for their potential applications in quantum computation, sensing, and bioimaging. However, synthesis of nanodiamonds typically requires high pressures and temperatures, and is still a challenge. Here, we demonstrate production of nanodiamonds by pulsed laser ablation of graphite and diamond-like carbon in water. Importantly, this technique enables production of nanocrystalline diamonds at room temperature and standard pressure conditions. Moreover, we propose a method for the purification of nanodiamonds from graphitic and amorphous carbon phases that do not require strong acids and harsh chemical conditions. Finally, we present a thermodynamic model that describes the formation of nanodiamonds during pulsed laser ablation. We show that synthesis of the crystalline phase is driven by a graphite-liquid-diamond transition process that occurs at the extreme thermodynamic conditions reached inside the ablation plume.

  6. Cobalt hexacyanoferrate modified multi-walled carbon nanotubes/graphite composite electrode as electrochemical sensor on microfluidic chip

    International Nuclear Information System (INIS)

    Li Xinchun; Chen Zuanguang; Zhong Yuwen; Yang Fan; Pan Jianbin; Liang Yajing

    2012-01-01

    Highlights: ► CoHCF nanoparticles modified MWCNTs/graphite electrode use for electrochemistry on electrophoresis microchip for the first time. ► Simultaneous, rapid, and sensitive electrochemical detection of hydrazine and isoniazid in real samples. ► An exemplary work of CME sensor assembly onto microchip for determination of analytes with environmental significance. ► Manifestation of the applicability and flexibility of CME sensor for electroanalysis on microfluidic chip. - Abstract: Nanomaterial-based electrochemical sensor has received significant interest. In this work, cobalt hexacyanoferrate modified multi-walled carbon nanotubes/graphite composite electrode was electrochemically prepared and exploited as an amperometric detector for microchip electrophoresis. The prepared sensor displayed rapid and sensitive response towards hydrazine and isoniazid oxidation, which was attributed to synergetic electrocatalytic effect of cobalt hexacyanoferrate and multi-walled carbon nanotubes. The sensitivity enhancement with nearly two orders of magnitude was gained, compared with the bare carbon paste electrode, with the detection limit of 0.91 μM (S/N = 3) for hydrazine. Acceptable repeatability of the microanalysis system was verified by consecutive eleven injections of hydrazine without chip and electrode treatments, the RSDs for peak current and migration time were 3.4% and 2.1%, respectively. Meanwhile, well-shaped electrophoretic peaks were observed, mainly due to fast electron transfer of electroactive species on the modified electrode. The developed microchip-electrochemistry setup was successfully applied to the determination of hydrazine and isoniazid in river water and pharmaceutical preparation, respectively. Several merits of the novel electrochemical sensor coupled with microfluidic platform, such as comparative stability, easy fabrication and high sensitivity, hold great potential for hydrazine compounds assay in the lab-on-a-chip system.

  7. Cobalt hexacyanoferrate modified multi-walled carbon nanotubes/graphite composite electrode as electrochemical sensor on microfluidic chip

    Energy Technology Data Exchange (ETDEWEB)

    Li Xinchun [School of Pharmaceutical Sciences, Sun Yat-sen University, 132 Waihuan East Road of Higher Education Mega Centre, Guangzhou 510006 (China); Chen Zuanguang, E-mail: chenzg@mail.sysu.edu.cn [School of Pharmaceutical Sciences, Sun Yat-sen University, 132 Waihuan East Road of Higher Education Mega Centre, Guangzhou 510006 (China); Zhong Yuwen, E-mail: yu0106@163.com [Center for Disease Control and Prevention of Guangdong Province, 176 Xingangxi, Guangzhou 510300 (China); Yang Fan; Pan Jianbin; Liang Yajing [School of Pharmaceutical Sciences, Sun Yat-sen University, 132 Waihuan East Road of Higher Education Mega Centre, Guangzhou 510006 (China)

    2012-01-13

    Highlights: Black-Right-Pointing-Pointer CoHCF nanoparticles modified MWCNTs/graphite electrode use for electrochemistry on electrophoresis microchip for the first time. Black-Right-Pointing-Pointer Simultaneous, rapid, and sensitive electrochemical detection of hydrazine and isoniazid in real samples. Black-Right-Pointing-Pointer An exemplary work of CME sensor assembly onto microchip for determination of analytes with environmental significance. Black-Right-Pointing-Pointer Manifestation of the applicability and flexibility of CME sensor for electroanalysis on microfluidic chip. - Abstract: Nanomaterial-based electrochemical sensor has received significant interest. In this work, cobalt hexacyanoferrate modified multi-walled carbon nanotubes/graphite composite electrode was electrochemically prepared and exploited as an amperometric detector for microchip electrophoresis. The prepared sensor displayed rapid and sensitive response towards hydrazine and isoniazid oxidation, which was attributed to synergetic electrocatalytic effect of cobalt hexacyanoferrate and multi-walled carbon nanotubes. The sensitivity enhancement with nearly two orders of magnitude was gained, compared with the bare carbon paste electrode, with the detection limit of 0.91 {mu}M (S/N = 3) for hydrazine. Acceptable repeatability of the microanalysis system was verified by consecutive eleven injections of hydrazine without chip and electrode treatments, the RSDs for peak current and migration time were 3.4% and 2.1%, respectively. Meanwhile, well-shaped electrophoretic peaks were observed, mainly due to fast electron transfer of electroactive species on the modified electrode. The developed microchip-electrochemistry setup was successfully applied to the determination of hydrazine and isoniazid in river water and pharmaceutical preparation, respectively. Several merits of the novel electrochemical sensor coupled with microfluidic platform, such as comparative stability, easy fabrication and

  8. Nuclear graphite ageing and turnaround

    International Nuclear Information System (INIS)

    Marsden, B.J.; Hall, G.N.; Smart, J.

    2001-01-01

    Graphite moderated reactors are being operated in many countries including, the UK, Russia, Lithuania, Ukraine and Japan. Many of these reactors will operate well into the next century. New designs of High Temperature Graphite Moderated Reactors (HTRS) are being built in China and Japan. The design life of these graphite-moderated reactors is governed by the ageing of the graphite core due to fast neutron damage, and also, in the case of carbon dioxide cooled reactors by the rate of oxidation of the graphite. Nuclear graphites are polycrystalline in nature and it is the irradiation-induced damage to the individual graphite crystals that determines the material property changes with age. The life of a graphite component in a nuclear reactor can be related to the graphite irradiation induced dimensional changes. Graphites typically shrink with age, until a point is reached where the shrinkage stops and the graphite starts to swell. This change from shrinkage to swelling is known as ''turnaround''. It is well known that pre-oxidising graphite specimens caused ''turnaround'' to be delayed, thus extending the life of the graphite, and hence the life of the reactor. However, there was no satisfactory explanation of this behaviour. This paper presents a numerical crystal based model of dimensional change in graphite, which explains the delay in ''turnaround'' in the pre-oxidised specimens irradiated in a fast neutron flux, in terms of crystal accommodation and orientation and change in compliance due to radiolytic oxidation. (author)

  9. Pseudocapacitive performance of electrodeposited porous Co3O4 film on electrophoretically modified graphite electrodes with carbon nanotubes

    Science.gov (United States)

    Kazazi, Mahdi; Sedighi, Ali Reza; Mokhtari, Mohammad Amin

    2018-05-01

    A facile and efficient two-step procedure was developed for the fabrication of a high-performance and binder-free cobalt oxide-carbon nanotubes (CO/CNT) pseudocapacitive electrode. First, CNTs were deposited on the surface of a chemically activated graphite sheet by cathodic electrophoretic deposition technique from their ethanolic suspension. In the next step, a thin film of cobalt oxide was electrodeposited on the CNTs coated graphite substrate by a galvanostatic method, followed by a thermal treatment in air. The structure and morphology of the prepared cobaltite electrode with and without CNT interlayer were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and nitrogen adsorption-desorption measurement. The results indicated that Co3O4 nanoparticles were uniformly attached on the surface of CNTs, to form a porous-structured CO/CNT composite electrode with a high specific surface area of 144.9 m2 g-1. Owing to the superior electrical conductivity of CNTs, high surface area and open porous structure, and improved integrity of the electrode structure, the composite electrode delivered a high areal capacitance of 4.96F cm-2 at a current density of 2 mA cm-2, a superior rate performance (64.7% capacitance retention from 2 mA cm-2 to 50 mA cm-2), as well as excellent cycling stability (91.8% capacitance retention after 2000 cycles), which are higher than those of the pure cobaltite electrode.

  10. Preparation of graphite dispersed copper composite on copper plate with CO2 laser

    Science.gov (United States)

    Yokoyama, S.; Ishikawa, Y.; Muizz, M. N. A.; Hisyamudin, M. N. N.; Nishiyama, K.; Sasano, J.; Izaki, M.

    2018-01-01

    It was tried in this work to prepare the graphite dispersed copper composite locally on a copper plate with a CO2 laser. The objectives of this study were to clear whether copper graphite composite was prepared on a copper plate and how the composite was prepared. The carbon content at the laser spot decreased with the laser irradiation time. This mainly resulted from the elimination by the laser trapping. The carbon content at the outside of the laser spot increased with time. Both the laser ablation and the laser trapping did not act on the graphite particles at the outside of the laser spot. Because the copper at the outside of the laser spot melted by the heat conduction from the laser spot, the particles were fixed by the wetting. However, the graphite particles were half-floated on the copper plate. The Vickers hardness decreased with an increase with laser irradiation time because of annealing.

  11. Liquid-phase pulsed laser ablation synthesis of graphitized carbon-encapsulated palladium core-shell nanospheres for catalytic reduction of nitrobenzene to aniline

    Science.gov (United States)

    Kim, Yu-jin; Ma, Rory; Reddy, D. Amaranatha; Kim, Tae Kyu

    2015-12-01

    Graphitized carbon-encapsulated palladium (Pd) core-shell nanospheres were produced via pulsed laser ablation of a solid Pd foil target submerged in acetonitrile. The microstructural features and optical properties of these nanospheres were characterized via high resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and UV-visible spectroscopy. Microstructural analysis indicated that the core-shell nanostructures consisted of single-crystalline cubic metallic Pd spheres that serve as the core material, over which graphitized carbon was anchored as a heterogeneous shell. The absorbance spectrum of the synthesized nanostructures exhibited a broad (absorption) band at ∼264 nm; this band corresponded to the typical inter-band transition of a metallic system and resulted possibly from the absorbance of the ionic Pd2+. The catalytic properties of the Pd and Pd@C core-shell nanostructures were investigated using the reduction of nitrobenzene to aniline by an excess amount of NaBH4 in an aqueous solution at room temperature, as a model reaction. Owing to the graphitized carbon-layered structure and the high specific surface area, the resulting Pd@C nanostructures exhibited higher conversion efficiencies than their bare Pd counterparts. In fact, the layered structure provided access to the surface of the Pd nanostructures for the hydrogenation reaction, owing to the synergistic effect between graphitized carbon and the nanostructures. Their unique structure and excellent catalytic performance render Pd@C core-shell nanostructures highly promising candidates for catalysis applications.

  12. Carbon particle induced foaming of molten sucrose for the preparation of carbon foams

    International Nuclear Information System (INIS)

    Narasimman, R.; Vijayan, Sujith; Prabhakaran, K.

    2014-01-01

    Graphical abstract: - Highlights: • An easy method for the preparation of carbon foam from sucrose is presented. • Wood derived activated carbon particles are used to stabilize the molten sucrose foam. • The carbon foams show relatively good mechanical strength. • The carbon foams show excellent CO 2 adsorption and oil absorption properties. • The process could be scaled up for the preparation of large foam bodies. - Abstract: Activated carbon powder was used as a foaming and foam setting agent for the preparation of carbon foams with a hierarchical pore structure from molten sucrose. The rheological measurements revealed the interruption of intermolecular hydrogen bonding in molten sucrose by the carbon particles. The carbon particles stabilized the bubbles in molten sucrose by adsorbing on the molten sucrose–gas interface. The carbon foams obtained at the activated carbon powder to sucrose weight ratios in the range of 0–0.25 had a compressive strength in the range of 1.35–0.31 MPa. The produced carbon foams adsorb 2.59–3.04 mmol/g of CO 2 at 760 mmHg at 273 K and absorb oil from oil–water mixtures and surfactant stabilized oil-in-water emulsions with very good selectivity and recyclability

  13. A general strategy toward graphitized carbon coating on iron oxides as advanced anodes for lithium-ion batteries.

    Science.gov (United States)

    Ding, Chunyan; Zhou, Weiwei; Wang, Bin; Li, Xin; Wang, Dong; Zhang, Yong; Wen, Guangwu

    2017-08-25

    Integration of carbon materials with benign iron oxides is blazing a trail in constructing high-performance anodes for lithium-ion batteries (LIBs). In this paper, a unique general, simple, and controllable strategy is developed toward in situ uniform coating of iron oxide nanostructures with graphitized carbon (GrC) layers. The basic synthetic procedure only involves a simple dip-coating process for the loading of Ni-containing seeds and a subsequent Ni-catalyzed chemical vapor deposition (CVD) process for the growth of GrC layers. More importantly, the CVD treatment is conducted at a quite low temperature (450 °C) and with extremely facile liquid carbon sources consisting of ethylene glycol (EG) and ethanol (EA). The GrC content of the resulting hybrids can be controllably regulated by altering the amount of carbon sources. The electrochemical results reveal remarkable performance enhancements of iron oxide@GrC hybrids compared with pristine iron oxides in terms of high specific capacity, excellent rate and cycling performance. This can be attributed to the network-like GrC coating, which can improve not only the electronic conductivity but also the structural integrity of iron oxides. Moreover, the lithium storage performance of samples with different GrC contents is measured, manifesting that optimized electrochemical property can be achieved with appropriate carbon content. Additionally, the superiority of GrC coating is demonstrated by the advanced performance of iron oxide@GrC compared with its corresponding counterpart, i.e., iron oxides with amorphous carbon (AmC) coating. All these results indicate the as-proposed protocol of GrC coating may pave the way for iron oxides to be promising anodes for LIBs.

  14. Using X-ray methods to evaluate the combustion sulfur minerals and graphitic carbon in coals and ashes

    International Nuclear Information System (INIS)

    Wertz, D.L.; Collins, L.W.

    1988-01-01

    Coals are complex mixtures of vastly different materials whose combustion kinetics may well exhibit symbiotic effects. Although the sulfur oxide gases produced during the combustion of coals may have a variety of sources, they are frequently caused by the thermal degradation of inorganic minerals to produce ''acid rain''. Since many of the minerals involved either as reactants or products in coal combustion produce well defined x-ray power diffraction (XRPD) patterns, the fate of these minerals may be followed by measuring the XRPD patterns of combustion products. Coal 1368P, a coal with an unusually high pyrite (FeS/sub 2/) fraction, has been the subject materials in our investigations of the fate of the inorganic minerals during combustion. These studies include measuring the fate of pyrite and of graphitic carbon in coal 1368P under varying combustion conditions. The results discussed in this paper were obtained by standard XRPD methods

  15. Supercapacitive evaluation of carbon black/exfoliated graphite/MnO{sub 2} ternary nanocomposite electrode by continuous cyclic voltammetry

    Energy Technology Data Exchange (ETDEWEB)

    Naderi, Hamid Reza, E-mail: hrnaderi@ut.ac.ir [Center of Excellence in Electrochemistry, Faculty of Chemistry, University of Tehran, Tehran (Iran, Islamic Republic of); Norouzi, Parviz, E-mail: norouzi@khayam.ut.ac.ir [Center of Excellence in Electrochemistry, Faculty of Chemistry, University of Tehran, Tehran (Iran, Islamic Republic of); Biosensor Research Center, Endocrinology & Metabolism Molecular-Cellular Sciences Institute, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of); Ganjali, Mohammad Reza, E-mail: ganjali@khayam.ut.ac.ir [Center of Excellence in Electrochemistry, Faculty of Chemistry, University of Tehran, Tehran (Iran, Islamic Republic of); Biosensor Research Center, Endocrinology & Metabolism Molecular-Cellular Sciences Institute, Tehran University of Medical Sciences, Tehran (Iran, Islamic Republic of)

    2015-08-01

    A new ternary nanocomposite was prepared by using MnO{sub 2}, carbon black (CB), and exfoliated graphite (EG) through a sonochemical method. In this process, the MnO{sub 2} nanoparticles was anchored on the mixture of CB and EG to maximize the specific capacitances of these materials. Structure and morphology of the CB/EG/MnO{sub 2} nanocomposites were examined by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The electrochemical properties of the CB/EG/MnO{sub 2} nanocomposites with different content of MnO{sub 2} were studied by cyclic voltammetry (CV), fast Fourier transformation continuous cyclic voltammetry (FFTCCV) technique, galvanostatic charge–discharge, and electrochemical impedance spectroscopy (EIS). The best nanocomposite electrode displayed specific capacitance of 364 F g{sup −1} at the scan rate of 2 mV s{sup −1} in 0.5 M Na{sub 2}SO{sub 4} aqueous solution, which is higher than pure MnO{sub 2} (289 F g{sup −1}). The capacitance stability of the nanocomposite electrode was studied by FFTCCV at the scan rate of 500 mV s{sup −1}. The result shows that after recording 4000 CVs, the specific capacitance of the nanocomposite decline only 5%. Furthermore, the nanocomposite electrode showed higher energy density than MnO{sub 2} electrode. - Highlights: • MnO{sub 2}/exfoliated graphite/Carbon black nanocomposites were synthesized by ultrasonic vibration. • The best nanocomposite electrode exhibits specific capacitance of 364 F g{sup −1} in 2 mV s{sup −1}. • The stability of the nanocomposite electrode was study FFTCCV technique. • The capacitance decreases only 5.2% of initial capacitance after 4000 cycles.

  16. Structures and electrochemical performances of pyrolized carbons from graphite oxides for electric double-layer capacitor

    Science.gov (United States)

    Kim, Ick-Jun; Yang, Sunhye; Jeon, Min-Je; Moon, Seong-In; Kim, Hyun-Soo; Lee, Yoon-Pyo; An, Kye-Hyeok; Lee, Young-Hee

    The structural features and the electrochemical performances of pyrolized needle cokes from oxidized cokes are examined and compared with those of KOH-activated needle coke. The structure of needle coke is changed to a single phase of graphite oxide after oxidation treatment with an acidic solution having an NaClO 3/needle coke composition ratio of above 7.5, and the inter-layer distance of the oxidized needle coke is expanded to 6.9 Å with increasing oxygen content. After heating at 200 °C, the oxidized needle coke is reduced to a graphite structure with an inter-layer distance of 3.6 Å. By contrast, a change in the inter-layer distance in KOH-activated needle coke is not observed. An intercalation of pyrolized needle coke, observed on first charge, occurs at 1.0 V. This value is lower than that of KOH-activation needle coke. A capacitor using pyrolized needle coke exhibits a lower internal resistance of 0.57 Ω in 1 kHz, and a larger capacitance per weight and volume of 30.3 F g -1 and 26.9 F ml -1, in the two-electrode system over the potential range 0-2.5 V compared with those of a capacitor using KOH-activation of needle coke. This better electrochemical performance is attributed to a distorted graphene layer structure derived from the process of the inter-layer expansion and shrinkage.

  17. Immobilization of carbon-14 from reactor graphite waste by use of self-sustaining reaction in the C-Al-TiO2 system

    International Nuclear Information System (INIS)

    Karlina, O.K.; Klimov, V.L.; Ojovan, M.I.; Pavlova, G.Yu.; Dmitriev, S.A.; Yurchenko, A.Yu.

    2005-01-01

    As a result of long-term neutron irradiation, the long-lived 14 C is produced in the reactor graphite. The exothermic self-sustaining reaction 3C(graphite) + 4Al + 3TiO 2 = 3TiC + 2Al 2 O 3 was proposed for processing of such waste. In doing so, the carbon, including the 14 C, is chemically bound in the stable TiC. The reaction products in the C-Al-TiO 2 system were investigated both by thermodynamic simulation and experimentally in the course of this work

  18. Method of producing carbon coated nano- and micron-scale particles

    Science.gov (United States)

    Perry, W. Lee; Weigle, John C; Phillips, Jonathan

    2013-12-17

    A method of making carbon-coated nano- or micron-scale particles comprising entraining particles in an aerosol gas, providing a carbon-containing gas, providing a plasma gas, mixing the aerosol gas, the carbon-containing gas, and the plasma gas proximate a torch, bombarding the mixed gases with microwaves, and collecting resulting carbon-coated nano- or micron-scale particles.

  19. Charge transfer in carbon composites based on fullerenes and exfoliated graphite

    Science.gov (United States)

    Berezkin, V. I.

    2017-07-01

    Kinetic processes have been studied in composites based on fullerenes and exfoliated graphite at the initial proportions of components from 1: 16 to 16: 1 in mass. The samples are produced by heat treatment of initial dispersed mixtures in vacuum in the diffusion-adsorption process, their further cold pressing, and annealing. It is shown that the annealing almost does not influence the conduction mechanisms and only induces additional structural defects acting as electron traps. As a whole, the results obtained at the noted proportions of components make it possible to consider the material as a compensated metallic system with a structural disorder in which the charge transfer at temperatures from 4.2 K to room temperature is controlled by quantum interference phenomena. At low temperatures, the effect of a weak localization is observed, and the electron-electron interactions take place at medium and high temperatures.

  20. Spatial distribution of carbon species in laser ablation of graphite target

    International Nuclear Information System (INIS)

    Ikegami, T.; Ishibashi, S.; Yamagata, Y.; Ebihara, K.; Thareja, R.K.; Narayan, J.

    2001-01-01

    We report on the temporal evolution and spatial distribution of C 2 and C 3 molecules produced by KrF laser ablation of a graphite target using laser induced fluorescence imaging and optical emission spectroscopy. Spatial density profiles of C 2 were measured using two-dimensional fluorescence in various pressures of different ambient (vacuum, nitrogen, oxygen, hydrogen, helium, and argon) gases at various ablation laser fluences and ablation area. A large yield of C 2 is observed in the central part of the plume and near the target surface and its density and distribution was affected by the laser fluence and ambient gas. Fluorescent C 3 was studied in Ar gas and the yield of C 3 is enhanced at higher gas pressure and longer delay times after ablation

  1. In situ catalytic synthesis of high-graphitized carbon-coated LiFePO4 nanoplates for superior Li-ion battery cathodes.

    Science.gov (United States)

    Ma, Zhipeng; Fan, Yuqian; Shao, Guangjie; Wang, Guiling; Song, Jianjun; Liu, Tingting

    2015-02-04

    The low electronic conductivity and one-dimensional diffusion channel along the b axis for Li ions are two major obstacles to achieving high power density of LiFePO4 material. Coating carbon with excellent conductivity on the tailored LiFePO4 nanoparticles therefore plays an important role for efficient charge and mass transport within this material. We report here the in situ catalytic synthesis of high-graphitized carbon-coated LiFePO4 nanoplates with highly oriented (010) facets by introducing ferrocene as a catalyst during thermal treatment. The as-obtained material exhibits superior performances for Li-ion batteries at high rate (100 C) and low temperature (-20 °C), mainly because of fast electron transport through the graphitic carbon layer and efficient Li(+)-ion diffusion through the thin nanoplates.

  2. Nitrogen–doped graphitized carbon shell encapsulated NiFe nanoparticles: A highly durable oxygen evolution catalyst

    Energy Technology Data Exchange (ETDEWEB)

    Du, Lei; Luo, Langli; Feng, Zhenxing; Engelhard, Mark; Xie, Xiaohong; Han, Binghong; Sun, Junming; Zhang, Jianghao; Yin, Geping; Wang, Chongmin; Wang, Yong; Shao, Yuyan

    2017-09-01

    Oxygen evolution reaction (OER) plays a crucial role in various energy conversion devices such as water electrolyzers and metal–air batteries. Precious metal catalysts such as Ir, Ru and their oxides are usually used for enhancing reaction kinetics but are limited by their scarce resource. The challenges associated with alternative non–precious metal catalysts such as transition metal oxides and (oxy)hydroxides etc. are their low electronic conductivity and durability. Herein, we report a highly active (360 mV overpotential at 10 mA cm–2GEO) and durable (no degradation after 20000 cycles) OER catalyst derived from bimetallic metal–organic frameworks (MOFs) precursors. This catalyst consists of NiFe nanoparticles encapsulated by nitrogen–doped graphitized carbon shells. The electron-donation/deviation from Fe and tuned electronic structure of metal cores by Ni are revealed to be primary contributors to the enhanced OER activity, whereas N concentration contributes negligibly. We further demonstrated that the structure and morphology of encapsulating carbon shells, which are the key factors influencing the durability, are facilely controlled by the chemical state of precursors.

  3. Macroporous graphitic carbon foam decorated with polydopamine as a high-performance anode for microbial fuel cell

    Science.gov (United States)

    Jiang, Hongmei; Yang, Lu; Deng, Wenfang; Tan, Yueming; Xie, Qingji

    2017-09-01

    Herein, a macroporous graphitic carbon foam (MGCF) electrode decorated with polydopamine (PDA) is used as a high-performance anode for microbial fuel cell (MFC) applications. The MGCF is facilely prepared by pyrolysis of a powder mixture comprising maltose, nickel nitrate, and ammonia chloride, without using solid porous template. The MGCF is coated with PDA by self-polymerization of dopamine in a basic solution. The MGCF can provide a large surface area for bacterial attachment, and PDA coated on the MGCF electrode can further promote bacterial adhesion resulting from the improved hydrophility, so the MGCF-PDA electrode as an anode in a MFC can show ultrahigh bacterial loading capacity. Moreover, the electrochemical oxidation of flavins at the MGCF-PDA electrode is greatly accelerated, so the extracellular electron transfer mediated by flavins is improved. As a result, the MFC equipped with a MGCF-PDA anode can show a maximum power density of 1735 mW cm-2, which is 6.7 times that of a MFC equipped with a commercial carbon felt anode, indicating a promising anode for MFC applications.

  4. Synthesis and CO2 adsorption study of modified MOF-5 with multi-wall carbon nanotubes and expandable graphite

    International Nuclear Information System (INIS)

    Ullah, Sami; Bustam, M. A.; Shariff, A. M.; Elkhalifah, Ali E. I.; Murshid, G.; Riaz, Nadia

    2014-01-01

    MOF-5 was synthesized by solvothermal method and its reactivation under anhydrous conditions. This research is conducted to investigate the effect of MOF-5 and MOF-5 modified with multi-wall carbon nanotubes (MWCNTs) and expandable graphite (EG) on the performance of CO 2 adsorption. The synthesized MOFs were characterized using Field emission scanning electron microscopy (FESEM) for surface morphology, Thermogravimetric analysis (TGA) for thermal stability, X-ray diffraction (XRD) for crystals plane, Brunauer-Emmet-Teller (BET) for surface area and CO 2 adsorption. The result had showed that the modified MOF-5 enhanced the CO 2 adsorption compared to the pure MOF-5. The increment in the CO 2 uptake capacities of MOF materials was attributed to the decrease in the pore size and enhancement of micropore volume of MOF-5 by multi-walled carbon nanotube and EG incorporation. The BET surface area of the synthesized MOF-5@MWCNTs is more than MOF-5. The CO 2 sorption capacities of MOF-5 and MOF-5@MWCNTs were observed to increase from 0.00008 to 0.00048 mol g-1 at 298 K and 1 bar. The modified MOF-5@MWCNTs resulted in the highest CO 2 adsorption followed by the modified MOF-5@ EG and lastly, MOF-5

  5. The Diversity of Carbon in Cometary Refractory Dust Particles

    Science.gov (United States)

    Wooden, D. H.

    2018-01-01

    When comparing the dark icy surfaces of outer solar system small bodies and the composition of carbonaceous chondrites derived from dark asteroids we find a significant discrepancy in the assessed amounts of elemental carbon: up to 80% amorphous carbon is used to model the dark surfaces of Kuiper Belt Objects and Centaurs whereas at most 5% of elemental carbon is found in carbonaceous chondrites. If we presume that regimes of comet nuclei formation are analogous to disk regimes where other outer solar system ice-rich bodies formed then we can turn to comet dust to gain insights into the diversity in the concentration and forms of carbon available in the outer disk. Comet dust offers important insights into the diversity in the amounts and forms of carbon that were incorporated into aggregate dust particles in the colder parts of the protoplanetary disk out of which comet nuclei accreted. Comet nuclei are amongst the most primitive bodies because they have remained cold and unequilibrated. Comet dust particles reveal the presence of forms of elemental carbon and of soluble and insoluble organic matter, and in a great diversity of concentrations from very little, e.g., Stardust samples of comet 81P/Wild 2, to 80% by volume for Ultra Carbonaceous Antarctic Micro Meteorites (UCAMMs). Cometary outbursts and/or jet activity also demonstrate variations in the concentration of carbon in the grains at different grain sizes within a single comet. We review the diversity of carbon-bearing dust grains in cometary samples, flyby measurements and deduced from remote-sensing to enrich the discussion about the diversity of carbonaceous matter available in the outer ice-rich disk at the time of comet nuclei formation.

  6. Characterization of calcium carbonate sorbent particle in furnace environment

    International Nuclear Information System (INIS)

    Lee, Kang Soo; Jung, Jae Hee; Keel, Sang In; Yun, Jin Han; Min, Tai Jin; Kim, Sang Soo

    2012-01-01

    The oxy-fuel combustion system is a promising technology to control CO 2 and NO X emissions. Furthermore, sulfation reaction mechanism under CO 2 -rich atmospheric condition in a furnace may lead to in-furnace desulfurization. In the present study, we evaluated characteristics of calcium carbonate (CaCO 3 ) sorbent particles under different atmospheric conditions. To examine the physical/chemical characteristics of CaCO 3 , which is used as a sorbent particle for in-furnace desulfurization in the oxy-fuel combustion system, they were injected into high temperature drop tube furnace (DTF). Experiments were conducted at varying temperatures, residence times, and atmospheric conditions in a reactor. To evaluate the aerosolizing characteristics of the CaCO 3 sorbent particle, changes in the size distribution and total particle concentration between the DTF inlet and outlet were measured. Structural changes (e.g., porosity, grain size, and morphology) of the calcined sorbent particles were estimated by BET/BJH, XRD, and SEM analyses. It was shown that sorbent particles rapidly calcined and sintered in the air atmosphere, whereas calcination was delayed in the CO 2 atmosphere due to the higher CO 2 partial pressure. Instead, the sintering effect was dominant in the CO 2 atmosphere early in the reaction. Based on the SEM images, it was shown that the reactions of sorbent particles could be explained as a grain–subgrain structure model in both the air and CO 2 atmospheres.

  7. The influence of buoyant forces and volume fraction of particles on the particle pushing/entrapment transition during directional solidification of Al/SiC and Al/graphite composites

    Science.gov (United States)

    Stefanescu, Doru M.; Moitra, Avijit; Kacar, A. Sedat; Dhindaw, Brij K.

    1990-01-01

    Directional solidification experiments in a Bridgman-type furnace were used to study particle behavior at the liquid/solid interface in aluminum metal matrix composites. Graphite or siliconcarbide particles were first dispersed in aluminum-base alloys via a mechanically stirred vortex. Then, 100-mm-diameter and 120-mm-long samples were cast in steel dies and used for directional solidification. The processing variables controlled were the direction and velocity of solidification and the temperature gradient at the interface. The material variables monitored were the interface energy, the liquid/particle density difference, the particle/liquid thermal conductivity ratio, and the volume fraction of particles. These properties were changed by selecting combinations of particles (graphite or silicon carbide) and alloys (Al-Cu, Al-Mg, Al-Ni). A model which considers process thermodynamics, process kinetics (including the role of buoyant forces), and thermophysical properties was developed. Based on solidification direction and velocity, and on materials properties, four types of behavior were predicted. Sessile drop experiments were also used to determine some of the interface energies required in calculation with the proposed model. Experimental results compared favorably with model predictions.

  8. Nuclear graphite waste's behaviour under disposal conditions: Study of the release and repartition of organic and inorganic forms of carbon 14 and tritium in alkaline media

    International Nuclear Information System (INIS)

    Vende, L.

    2012-01-01

    23000 tons of graphite wastes will be generated during dismantling of the first generation of French reactors (9 gas cooled reactors). These wastes are classified as Long Lived Low Level wastes (LLW-LL). As requested by the law, the French National Radioactive Waste Management Agency (Andra) is studying concepts of low-depth disposals.In this work we focus on carbon 14, the main long-lived radionuclide in graphite waste (5730 y), but also on tritium, which is the main contributor to the radioactivity in the short term. Carbon 14 and tritium may be released from graphite waste in many forms in gaseous phase ( 14 CO 2 , HT...) or in solution ( 14 CO 3 2- , HTO...). Their speciation will strongly affect their migration from the disposal site to the environment. Leaching experiments, in alkaline solution (0.1 M NaOH simulating repository conditions) have been performed on irradiated graphite, from Saint-Laurent A2 and G2 reactors, in order to quantify their release and characterize their speciation. The studies show that carbon 14 exists in both gaseous and aqueous phases. In the gaseous phase, release is weak (≤0.1%) and corresponds to oxidizable species. Carbon 14 is mainly released into liquid phase, as both inorganic and organic species. 65% of released fraction is inorganic and 35% organic carbon. Two tritiated species have been identified in gaseous phase: HTO and HT/Organically Bond Tritium. More than 90% of tritium in that phase corresponds to HT/OBT. But release is weak (≤0.1%). HTO is mainly in the liquid phase. (author)

  9. Synthesis of MnO nano-particle@Flourine doped carbon and its application in hybrid supercapacitor

    Energy Technology Data Exchange (ETDEWEB)

    Qu, Deyu; Feng, Xiaoke [Department of Chemistry, School of Chemistry, Chemical Engineering and Life Science, Wuhan University of Technology, Wuhan 430070, Hubei (China); Wei, Xi [School of Materials Science and Engineering, State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, Hubei (China); Guo, Liping [Department of Chemistry, School of Chemistry, Chemical Engineering and Life Science, Wuhan University of Technology, Wuhan 430070, Hubei (China); Cai, Haopeng, E-mail: cai_haopeng@whut.edu.cn [School of Materials Science and Engineering, State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, Hubei (China); Tang, Haolin [School of Materials Science and Engineering, State Key Laboratory of Advanced Technology for Materials Synthesis and Processing, Wuhan University of Technology, Wuhan 430070, Hubei (China); Xie, Zhizhong, E-mail: zhizhong_xie@163.com [Department of Chemistry, School of Chemistry, Chemical Engineering and Life Science, Wuhan University of Technology, Wuhan 430070, Hubei (China)

    2017-08-15

    Highlights: • A Fluorine doped carbon encapsulated MnO nanoparticle material was fabricated through a self-assembly method. • Nafion ionomers was used as the fluorine and carbon precursor. • A lithium ion supercapacitor was assemblied by using MnO@FC and porous carbon. • A stable energy density as well as superior cycling stability were demonstrated in this hybrid system. - Abstract: A flourine doped carbon materials encapsulated MnO nano-particle was synthesized through a self-assembly method. The MnO nano-crystal covered with a thin layer of graphite were achieved. This hybrid MnO/carbon materials were employed as negative electrode in a new lithium ion hybrid supercapacitor, while the electrochemical double-layer porous carbon served as positive electrode. The electrochemical performances of this hybrid device were investigated and exhibited relative high capacity upto 40 mAh g{sup −1} in an applied current of 200 mAh g{sup −1}, good rate performance as well as superior cycling stability.

  10. Evidence for Reduced, Carbon-rich Regions in the Solar Nebula from an Unusual Cometary Dust Particle

    Energy Technology Data Exchange (ETDEWEB)

    De Gregorio, Bradley T.; Stroud, Rhonda M. [Materials Science and Technology Division, Naval Research Laboratory, Code 6366, 4555 Overlook Avenue SW, Washington, DC 20375 (United States); Nittler, Larry R. [Department of Terrestrial Magnetism, Carnegie Institution of Washington, 5241 Broad Branch Road NW, Washington, DC 20015 (United States); Kilcoyne, A. L. David, E-mail: bradley.degregorio@nrl.navy.mil [Advanced Light Source, Lawrence Berkeley National Laboratory, 1 Cyclotron Road, Mailstop 7R0222, Berkeley, CA 94720 (United States)

    2017-10-20

    Geochemical indicators in meteorites imply that most formed under relatively oxidizing conditions. However, some planetary materials, such as the enstatite chondrites, aubrite achondrites, and Mercury, were produced in reduced nebular environments. Because of large-scale radial nebular mixing, comets and other Kuiper Belt objects likely contain some primitive material related to these reduced planetary bodies. Here, we describe an unusual assemblage in a dust particle from comet 81P/Wild 2 captured in silica aerogel by the NASA Stardust spacecraft. The bulk of this ∼20 μ m particle is comprised of an aggregate of nanoparticulate Cr-rich magnetite, containing opaque sub-domains composed of poorly graphitized carbon (PGC). The PGC forms conformal shells around tiny 5–15 nm core grains of Fe carbide. The C, N, and O isotopic compositions of these components are identical within errors to terrestrial standards, indicating a formation inside the solar system. Magnetite compositions are consistent with oxidation of reduced metal, similar to that seen in enstatite chondrites. Similarly, the core–shell structure of the carbide + PGC inclusions suggests a formation via FTT reactions on the surface of metal or carbide grains in warm, reduced regions of the solar nebula. Together, the nanoscale assemblage in the cometary particle is most consistent with the alteration of primary solids condensed from a C-rich, reduced nebular gas. The nanoparticulate components in the cometary particle provide the first direct evidence from comets of reduced, carbon-rich regions that were present in the solar nebula.

  11. Graphitic carbon nitride nanosheet@metal-organic framework core-shell nanoparticles for photo-chemo combination therapy

    Science.gov (United States)

    Chen, Rui; Zhang, Jinfeng; Wang, Yu; Chen, Xianfeng; Zapien, J. Antonio; Lee, Chun-Sing

    2015-10-01

    Recently, nanoscale metal-organic frameworks (NMOFs) have started to be developed as a promising platform for bioimaging and drug delivery. On the other hand, combination therapies using multiple approaches are demonstrated to achieve much enhanced efficacy. Herein, we report, for the first time, core-shell nanoparticles consisting of a photodynamic therapeutic (PDT) agent and a MOF shell while simultaneously carrying a chemotherapeutic drug for effective combination therapy. In this work, core-shell nanoparticles of zeolitic-imadazolate framework-8 (ZIF-8) as shell embedded with graphitic carbon nitride (g-C3N4) nanosheets as core are fabricated by growing ZIF-8 in the presence of g-C3N4 nanosheets. Doxorubicin hydrochloride (DOX) is then loaded into the ZIF-8 shell of the core-shell nanoparticles. The combination of the chemotherapeutic effects of DOX and the PDT effect of g-C3N4 nanosheets can lead to considerably enhanced efficacy. Furthermore, the red fluorescence of DOX and the blue fluorescence of g-C3N4 nanosheets provide the additional function of dual-color imaging for monitoring the drug release process.Recently, nanoscale metal-organic frameworks (NMOFs) have started to be developed as a promising platform for bioimaging and drug delivery. On the other hand, combination therapies using multiple approaches are demonstrated to achieve much enhanced efficacy. Herein, we report, for the first time, core-shell nanoparticles consisting of a photodynamic therapeutic (PDT) agent and a MOF shell while simultaneously carrying a chemotherapeutic drug for effective combination therapy. In this work, core-shell nanoparticles of zeolitic-imadazolate framework-8 (ZIF-8) as shell embedded with graphitic carbon nitride (g-C3N4) nanosheets as core are fabricated by growing ZIF-8 in the presence of g-C3N4 nanosheets. Doxorubicin hydrochloride (DOX) is then loaded into the ZIF-8 shell of the core-shell nanoparticles. The combination of the chemotherapeutic effects of DOX

  12. Rapid synthesis of graphitic carbon nitride powders by metathesis reaction between CaCN{sub 2} and C{sub 2}Cl{sub 6}

    Energy Technology Data Exchange (ETDEWEB)

    Pang Linlin [Key Laboratory of Liquid Structure and Heredity of Materials, Ministry of Education, Shandong University, Jinan, 250061 (China); Carbon Fiber Engineering Research Center of Shandong Province, Shandong University, Jinan 250061 (China); Bi Jianqiang [Key Laboratory of Liquid Structure and Heredity of Materials, Ministry of Education, Shandong University, Jinan, 250061 (China); Bai Yujun [Key Laboratory of Liquid Structure and Heredity of Materials, Ministry of Education, Shandong University, Jinan, 250061 (China) and Carbon Fiber Engineering Research Center of Shandong Province, Shandong University, Jinan 250061 (China)], E-mail: byj97@126.com; Qi Yongxin [Carbon Fiber Engineering Research Center of Shandong Province, Shandong University, Jinan 250061 (China); Zhu Huiling [Key Laboratory of Liquid Structure and Heredity of Materials, Ministry of Education, Shandong University, Jinan, 250061 (China); Carbon Fiber Engineering Research Center of Shandong Province, Shandong University, Jinan 250061 (China); Wang Chengguo; Wu Jiwei [Carbon Fiber Engineering Research Center of Shandong Province, Shandong University, Jinan 250061 (China); Lu Chengwei [Department of Equipment, Shandong University of Science and Technology, Jinan 250031 (China)

    2008-12-20

    Carbon nitride powders were rapidly synthesized at low temperature via the chemical metathesis reaction between CaCN{sub 2} and C{sub 2}Cl{sub 6}. X-ray diffraction results confirm the formation of crystalline graphitic carbon nitride. Besides the dominant morphology of nanoparticles, flakes, nanorods, hollow and solid spheres can be observed by transmission electron microscopy. The absorption peaks of C-N, C=N and s-triazine rings, as well as the absence of C{identical_to}N peak in the infrared spectra, further verify the formation of graphite-like sp{sup 2}-bonded structure with planar networks. Elemental analysis gives an atomic ratio of N/C around 0.3. X-ray photoelectron spectra exhibit the existence of chemical bonding between C and N.

  13. Ammonia Synthesis using Ti and Nb Nitride Nano-particles Prepared by Mesoporous Graphitic C3N4

    KAUST Repository

    Kumagai, Hiromu; Takanabe, Kazuhiro; Kubota, Jun; Domen, Kazunari

    2015-01-01

    TiN and NbN nanoparticles were synthesized from mesoporous graphitic C3N4 (mpg-C3N4) as a reactive template and used as the catalyst for ammonia synthesis. The obtained TiN and NbN nanoparticles possess high surface areas of 299 and 275 m2 g-1

  14. Facile synthesis of phosphorus doped graphitic carbon nitride polymers with enhanced visible-light photocatalytic activity

    International Nuclear Information System (INIS)

    Zhang, Ligang; Chen, Xiufang; Guan, Jing; Jiang, Yijun; Hou, Tonggang; Mu, Xindong

    2013-01-01

    Graphical abstract: - Highlights: • P-doped g-C 3 N 4 has been prepared by a one-pot green synthetic approach. • The incorporation of P resulted in favorable textural and electronic properties. • Doping with P enhanced the visible-light photocatalytic activity of g-C 3 N 4 . • A postannealing treatment further enhanced the activity of P-doped g-C 3 N 4 . • Photogenerated holes were the main species responsible for the activity. - Abstract: Phosphorus-doped carbon nitride materials were prepared by a one-pot green synthetic approach using dicyandiamide monomer and a phosphorus containing ionic liquid as precursors. The as-prepared materials were subjected to several characterizations and investigated as metal-free photocatalysts for the degradation of organic pollutants (dyes like Rhodamine B, Methyl orange) in aqueous solution under visible light. Results revealed that phosphorus-doped carbon nitride have a higher photocatalytic activity for decomposing Rhodamine B and Methyl orange in aqueous solution than undoped g-C 3 N 4 , which was attributed to the favorable textural, optical and electronic properties caused by doping with phosphorus heteroatoms into carbon nitride host. A facile postannealing treatment further improved the activity of the photocatalytic system, due to the higher surface area and smaller structural size in the postcalcined catalysts. The phosphorus-doped carbon nitride showed high visible-light photocatalytic activity, making them promising materials for a wide range of potential applications in photochemistry

  15. Nanodiamond infiltration into porous silicon through etching of solid carbon produced at different graphitization temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Miranda, C. R. B., E-mail: claudia_rbm@yahoo.com.br [Instituto Nacional de Pesquisas Espaciais-INPE, Centro de Ciencias do Sistema Terrestre-CCST, Centro de Ciencias do Sistema Terrestre-CCST (Brazil); Baldan, M. R.; Beloto, A. F.; Ferreira, N. G. [CTE/INPE, Centro de Tecnologias Espaciais (Brazil)

    2011-09-15

    Nanocrystalline diamond (NCD) was grown on the porous silicon (PS) substrate using Reticulated Vitreous Carbon (RVC) as an additional solid carbon source. RVC was produced at different heat treatment temperatures of 1300, 1500, and 2000 Degree-Sign C, resulting in samples with different turbostratic carbon organizations. The PS substrate was produced by an electrochemical method. NCD film was obtained by the chemical vapor infiltration/deposition process where a RVC piece was positioned just below the PS substrate. The PS and NCD samples were characterized by Field Emission Gun-Scanning Electron Microscopy (FEG-SEM). NCD films presented faceted nanograins with uniform surface texture covering all the pores resulting in an apparent micro honeycomb structure. Raman's spectra showed the D and G bands, as well as, the typical two shoulders at 1,150 and 1,490 cm{sup -1} attributed to NCD. X-ray diffraction analyses showed the predominant (111) diamond orientation as well as the (220) and (311) peaks. The structural organization and the heteroatom presence on the RVC surface, analyzed from X-ray photoelectron spectroscopy, showed their significant influence on the NCD growth process. The hydrogen etching released, from RVC surface, associated to carbon and/or oxygen/nitrogen amounts led to different contributions for NCD growth.

  16. Functionalized Graphitic Carbon Nitride for Metal-free, Flexible and Rewritable Nonvolatile Memory Device via Direct Laser-Writing

    Science.gov (United States)

    Zhao, Fei; Cheng, Huhu; Hu, Yue; Song, Long; Zhang, Zhipan; Jiang, Lan; Qu, Liangti

    2014-01-01

    Graphitic carbon nitride nanosheet (g-C3N4-NS) has layered structure similar with graphene nanosheet and presents unusual physicochemical properties due to the s-triazine fragments. But their electronic and electrochemical applications are limited by the relatively poor conductivity. The current work provides the first example that atomically thick g-C3N4-NSs are the ideal candidate as the active insulator layer with tunable conductivity for achieving the high performance memory devices with electrical bistability. Unlike in conventional memory diodes, the g-C3N4-NSs based devices combined with graphene layer electrodes are flexible, metal-free and low cost. The functionalized g-C3N4-NSs exhibit desirable dispersibility and dielectricity which support the all-solution fabrication and high performance of the memory diodes. Moreover, the flexible memory diodes are conveniently fabricated through the fast laser writing process on graphene oxide/g-C3N4-NSs/graphene oxide thin film. The obtained devices not only have the nonvolatile electrical bistability with great retention and endurance, but also show the rewritable memory effect with a reliable ON/OFF ratio of up to 105, which is the highest among all the metal-free flexible memory diodes reported so far, and even higher than those of metal-containing devices. PMID:25073687

  17. Graphitic carbon nitride/Cu2O heterojunctions: Preparation, characterization, and enhanced photocatalytic activity under visible light

    International Nuclear Information System (INIS)

    Tian, Yanlong; Chang, Binbin; Fu, Jie; Zhou, Baocheng; Liu, Jiyang; Xi, Fengna; Dong, Xiaoping

    2014-01-01

    As a metal-free semiconductor material, graphitic carbon nitride (C 3 N 4 ), the high recombination rate of photogenerated charges and insufficient sunlight absorption limit its solar-based photocatalytic activity. Here, we reported the heterojunctions of C 3 N 4 –Cu 2 O with a p–n junction structure, which was synthesized by a hydrothermal method. The HR-TEM result revealed an intimate interface between C 3 N 4 and Cu 2 O in the heterojunction, and UV–vis diffuse reflection spectra showed their extended spectral response in the visible region compared with pure C 3 N 4 . These excellent structural and spectral properties, as well as p–n junction structures, endowed the C 3 N 4 –Cu 2 O heterojunctions with enhanced photocatalytic activities. The possible photocatalytic mechanism that photogenerated holes as the mainly oxidant species in photocatalysis was proposed base on the trapping experiments. - Highlights: • A hydrothermal method was used to prepare C3N 4 –Cu 2 O heterojunction. • The resulting heterojunction possesses broader absorption in the visible region. • The material owns a high visible light activity and stability for dye degradation

  18. Graphite coated with manganese oxide/multiwall carbon nanotubes composites as anodes in marine benthic microbial fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Fu, Yubin, E-mail: ffyybb@ouc.edu.cn; Yu, Jian; Zhang, Yelong; Meng, Yao

    2014-10-30

    Highlights: • MnO{sub 2}/MWCNTs composites anode exhibits faster reaction kinetics. • The surfaces of MnO{sub 2}/MWCNTs composites anode exhibits better wettability. • A BMFC using the modified anode have excellent power output. - Abstract: Improving anode performance is of great significance to scale up benthic microbial fuel cells (BMFCs) for its marine application to drive oceanography instruments. In this study, manganese oxide (MnO{sub 2})/multiwall carbon nanotubes (MWCNTs) composites are prepared to be as novel anodes in the BMFCs via a direct redox reaction between permanganate ions (MnO{sub 4}{sup −}) and MWCNTs. The results indicate that the MnO{sub 2}/MWCNTs anode has a better wettability, greater kinetic activity and higher power density than that of the plain graphite (PG) anode. It is noted that the MnO{sub 2} (50% weight percent)/MWCNTs anode shows the highest electrochemical performance among them and will be a promising material for improving bioelectricity production of the BMFCs. Finally, a synergistic mechanism of electron transfer shuttle of Mn ions and their redox reactions in the interface between modified anode and bacteria biofilm are proposed to explain its excellent electrochemical performance.

  19. Diazonium modification of porous graphitic carbon with catechol and amide groups for hydrophilic interaction and attenuated reversed phase liquid chromatography.

    Science.gov (United States)

    Iverson, Chad D; Zhang, Ya; Lucy, Charles A

    2015-11-27

    Porous graphitic carbon (PGC) is an increasingly popular and attractive phase for HPLC on account of its chemical and thermal stability, and its unique separation mechanism. However, native PGC is strongly hydrophobic and in some instances excessively retentive. As part of our effort to build a library of hydrophilic covalently modified PGC phases, we functionalized PGC with catechol and amide groups by means of aryl diazonium chemistry to produce two new phases. Successful grafting was confirmed by X-ray photoelectron spectroscopy (XPS). Under HILIC conditions, the Catechol-PGC showed up to 5-fold increased retention relative to unmodified PGC and selectivity that differed from four other HILIC phases. Under reversed phase conditions, the Amide-PGC reduced the retentivity of PGC by almost 90%. The chromatographic performance of Catechol-PGC and Amide-PGC is demonstrated by separations of nucleobases, nucleosides, phenols, alkaline pharmaceuticals, and performance enhancing stimulants. These compounds had retention factors (k) ranging from 0.5 to 13. Copyright © 2015 Elsevier B.V. All rights reserved.

  20. Graphitic carbon nanospheres: A Raman spectroscopic investigation of thermal conductivity and morphological evolution by pulsed laser irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Agarwal, Radhe; Sahoo, Satyaprakash, E-mail: satya504@gmail.com, E-mail: rkatiyar@hpcf.upr.edu; Chitturi, Venkateswara Rao; Katiyar, Ram S., E-mail: satya504@gmail.com, E-mail: rkatiyar@hpcf.upr.edu [Department of Physics, University of Puerto Rico, San Juan, Puerto Rico 00936-8377 (United States)

    2015-12-07

    Graphitic carbon nanospheres (GCNSs) were prepared by a unique acidic treatment of multi-walled nanotubes. Spherical morphology with a narrow size distribution was confirmed by transmission electron microscopy studies. The room temperature Raman spectra showed a clear signature of D- and G-peaks at around 1350 and 1591 cm{sup −1}, respectively. Temperature dependent Raman scattering measurements were performed to understand the phonon dynamics and first order temperature coefficients related to the D- and G-peaks. The temperature dependent Raman spectra in a range of 83–473 K were analysed, where the D-peak was observed to show a red-shift with increasing temperature. The relative intensity ratio of D- to G-peaks also showed a significant rise with increasing temperature. Such a temperature dependent behaviour can be attributed to lengthening of the C-C bond due to thermal expansion in material. The estimated value of the thermal conductivity of GCNSs ∼0.97 W m{sup −1} K{sup −1} was calculated using Raman spectroscopy. In addition, the effect of pulsed laser treatment on the GCNSs was demonstrated by analyzing the Raman spectra of post irradiated samples.

  1. Facile preparation of a TiO2 quantum dot/graphitic carbon nitride heterojunction with highly efficient photocatalytic activity

    Science.gov (United States)

    Wang, Xing; Jiang, Subin; Huo, Xuejian; Xia, Rui; Muhire, Elisée; Gao, Meizhen

    2018-05-01

    In this article, mechanical grinding, an effortless and super-effective synthetic strategy, is used to successfully synthesize a TiO2 quantum dot (TiO2QD)/graphitic carbon nitride (g-C3N4) heterostructure. X-ray photoelectron spectroscopy results together with transmission electron microscopy reveal the formation of the TiO2QD/g-C3N4 heterostructure with strong interfacial interaction. Because of the advantages of this characteristic, the prepared heterostructure exhibits excellent properties for photocatalytic wastewater treatment. Notably, the optimum photocatalytic activity of the TiO2QD/g-C3N4 heterostructure is nearly 3.4 times higher than that of the g-C3N4 nanosheets used for the photodegradation of rhodamine B pollutant. In addition, the stability and possible degradation mechanism of the TiO2QD/g-C3N4 heterojunction are studied in detail. This method may stimulate an effective approach to synthesizing QD-sensitized semiconductor materials and facilitate their application in environmental protection.

  2. Preparation, characterization, and surface conductivity of nanocomposites with hollow graphitic carbon nanospheres as fillers in polymethylmethacrylate matrix

    Science.gov (United States)

    Zhang, Cheng; Gao, Qingshan; Zhou, Bing; Bhargava, Gaurang

    2017-08-01

    Hollow graphitized carbon nanosphere (CNS) materials with inner diameter of 20 to 50 nm and shell thickness of 10 15 nm were synthesized from the polymerization of resorcinol (R) and formaldehyde (F) in the presence of a well-characterized iron polymeric complex (IPC). The CNS with unique nanostructures was used to fabricate CNS-polymer composites by dispersing CNS as fillers in the polymer matrix. Aggregation of CNS in polymer composites is usually a challenging issue. In this work, we employed in situ polymerization method and melt-mixing method to fabricate CNS-polymethylmethacrylate (PMMA) composites and compared their difference in terms of CNS dispersion in the composites and surface electrical conductivity. Four probes technique was utilized to measure the surface electrical conductivity of the CNS-PMMA composites. The measurements on four points and four silver painted lines on the thin film of CNS-PMMA composites were compared. The in situ polymerization method was found more efficient for better CNS dispersion in PMMA matrix and lower percolation conductivity threshold compared to the melt-mixing method. The enhanced electrical conductivity for CNS-PMMA composites may be attributed to the stronger covalent CNS-PMMA bonding between the surface functional groups and the MMA moieties.

  3. Frequency dependence of electrical properties of polyvinylidene fluoride/graphite electrode waste/natural carbon black composite

    Science.gov (United States)

    Insiyanda, D. R.; Indayaningsih, N.; Prihandoko, B.; Subhan, A.; Khaerudini, D. S.; Widodo, H.; Destyorini, F.; Chaer, A.

    2018-03-01

    Polyvinylidene fluoride (PVdF) is a semi-crystalline thermoplastic material with remarkably high piezoelectric coefficient and an attractive polymer matrix for micro-composite with superior mechanical and electrical properties. The conductive filler is obtained from Graphite Electrode Waste (GEW) and Natural Carbon Black (NCB). The variation of composite content (%) of PVdF/NCB/GEW were 100/0/0, 95/5/0, 95/0/5, 95/2.5/2.5. This experiment employed dry dispersion method for material mixing. The materials were then moulded using hot press machine with compression parameters of P = 5.5 MPa, T = 150 °C, t = 60 minutes, A = 5×5×(0.2 - 0.4) cm3. The electrical conductivity properties of pure PVdF, as well as PVdF/GEW, PVdF/NCB, and PVdF/NCB/GEW composites were investigated in a frequency range of 100 to 100000 Hz. The PVdF/GEW sample obtained the highest electrical conductivity. It is concluded that GEW and NCB can be incorporated into PVdF as a conductive filler to increase the conductivity of conductive material composite without solvent.

  4. Large-scale production of graphitic carbon nitride with outstanding nitrogen photofixation ability via a convenient microwave treatment

    Energy Technology Data Exchange (ETDEWEB)

    Ma, Huiqiang [College of Chemistry, Chemical Engineering, and Environmental Engineering, Liaoning Shihua University, Fushun 113001 (China); College of Environment and Resources, Key Lab of Groundwater Resources and Environment, Ministry of Education, Jilin University, Changchun 130021 (China); Shi, Zhenyu; Li, Shuang [College of Chemistry, Chemical Engineering, and Environmental Engineering, Liaoning Shihua University, Fushun 113001 (China); Liu, Na, E-mail: Naliujlu@163.com [College of Environment and Resources, Key Lab of Groundwater Resources and Environment, Ministry of Education, Jilin University, Changchun 130021 (China)

    2016-08-30

    Highlights: • Microwave method for synthesizing g-C{sub 3}N{sub 4} with N{sub 2} photofixation ability is reported. • Nitrogen vacancies play the important role on the nitrogen photofixation ability. • The present process is a convenient method for large-scale production of g-C{sub 3}N{sub 4}. - Abstract: A convenient microwave treatment for synthesizing graphitic carbon nitride (g-C{sub 3}N{sub 4}) with outstanding nitrogen photofixation ability under visible light is reported. X-ray diffraction (XRD), N{sub 2} adsorption, UV–vis spectroscopy, SEM, N{sub 2}-TPD, EPR, photoluminescence (PL) and photocurrent measurements were used to characterize the prepared catalysts. The results indicate that microwave treatment can form many irregular pores in as-prepared g-C{sub 3}N{sub 4}, which causes the increased surface area and separation rate of electrons and holes. More importantly, microwave treatment causes the formation of many nitrogen vacancies in as-prepared g-C{sub 3}N{sub 4}. These nitrogen vacancies not only serve as active sites to adsorb and activate N{sub 2} molecules but also promote interfacial charge transfer from catalysts to N{sub 2} molecules, thus significantly improving the nitrogen photofixation ability. Moreover, the present process is a convenient method for large-scale production of g-C{sub 3}N{sub 4} which is significantly important for the practical application.

  5. Large-scale production of graphitic carbon nitride with outstanding nitrogen photofixation ability via a convenient microwave treatment

    International Nuclear Information System (INIS)

    Ma, Huiqiang; Shi, Zhenyu; Li, Shuang; Liu, Na

    2016-01-01

    Highlights: • Microwave method for synthesizing g-C_3N_4 with N_2 photofixation ability is reported. • Nitrogen vacancies play the important role on the nitrogen photofixation ability. • The present process is a convenient method for large-scale production of g-C_3N_4. - Abstract: A convenient microwave treatment for synthesizing graphitic carbon nitride (g-C_3N_4) with outstanding nitrogen photofixation ability under visible light is reported. X-ray diffraction (XRD), N_2 adsorption, UV–vis spectroscopy, SEM, N_2-TPD, EPR, photoluminescence (PL) and photocurrent measurements were used to characterize the prepared catalysts. The results indicate that microwave treatment can form many irregular pores in as-prepared g-C_3N_4, which causes the increased surface area and separation rate of electrons and holes. More importantly, microwave treatment causes the formation of many nitrogen vacancies in as-prepared g-C_3N_4. These nitrogen vacancies not only serve as active sites to adsorb and activate N_2 molecules but also promote interfacial charge transfer from catalysts to N_2 molecules, thus significantly improving the nitrogen photofixation ability. Moreover, the present process is a convenient method for large-scale production of g-C_3N_4 which is significantly important for the practical application.

  6. Functionalized Graphitic Carbon Nitride for Metal-free, Flexible and Rewritable Nonvolatile Memory Device via Direct Laser-Writing

    Science.gov (United States)

    Zhao, Fei; Cheng, Huhu; Hu, Yue; Song, Long; Zhang, Zhipan; Jiang, Lan; Qu, Liangti

    2014-07-01

    Graphitic carbon nitride nanosheet (g-C3N4-NS) has layered structure similar with graphene nanosheet and presents unusual physicochemical properties due to the s-triazine fragments. But their electronic and electrochemical applications are limited by the relatively poor conductivity. The current work provides the first example that atomically thick g-C3N4-NSs are the ideal candidate as the active insulator layer with tunable conductivity for achieving the high performance memory devices with electrical bistability. Unlike in conventional memory diodes, the g-C3N4-NSs based devices combined with graphene layer electrodes are flexible, metal-free and low cost. The functionalized g-C3N4-NSs exhibit desirable dispersibility and dielectricity which support the all-solution fabrication and high performance of the memory diodes. Moreover, the flexible memory diodes are conveniently fabricated through the fast laser writing process on graphene oxide/g-C3N4-NSs/graphene oxide thin film. The obtained devices not only have the nonvolatile electrical bistability with great retention and endurance, but also show the rewritable memory effect with a reliable ON/OFF ratio of up to 105, which is the highest among all the metal-free flexible memory diodes reported so far, and even higher than those of metal-containing devices.

  7. Influence of the Surfactant Nature on the Occurrence of Self-Assembly between Rubber Particles and Thermally Reduced Graphite Oxide during the Preparation of Natural Rubber Nanocomposites

    Directory of Open Access Journals (Sweden)

    Héctor Aguilar-Bolados

    2015-01-01

    Full Text Available The natural rubber (NR latex consists of polymer particles charged negatively due to the adsorbed phospholipids and proteins molecules. The addition of stable aqueous suspension of thermally reduced graphite oxide (TRGO stabilized by ionic surfactants to NR latex can favor the occurrence of interaction between the stabilized TRGO and NR particles. Herein, the use of two surfactants of different nature, namely, sodium dodecyl sulfate (SDS and dodecyltrimethylammonium bromide (DTAB, for the preparation of (TRGO/NR nanocomposites, is reported. Zeta potential and particle size measurements indicated that the use of DTAB as cationic surfactant results in the flocculation of NR particles and promoted the formation of ion-pair interactions between TRGO and the proteins and/or phospholipids present on the NR surface. This indicates that the use of DTAB can promote a self-assembly phenomenon between TRGO with adsorbed DTAB molecules and NR particles. The occurrence of self-assembly phenomenon allows obtaining homogenous dispersion of TRGO particles in the polymer matrix. The TRGO/NR nanocomposites prepared by the use of DTAB exhibited superior mechanical properties and excellent electrical conductivities reaching values of stress at 500% strain of 3.02 MPa and 10−4 S/cm, respectively.

  8. Reversible Assembly of Graphitic Carbon Nitride 3D Network for Highly Selective Dyes Absorption and Regeneration.

    Science.gov (United States)

    Zhang, Yuye; Zhou, Zhixin; Shen, Yanfei; Zhou, Qing; Wang, Jianhai; Liu, Anran; Liu, Songqin; Zhang, Yuanjian

    2016-09-27

    Responsive assembly of 2D materials is of great interest for a range of applications. In this work, interfacial functionalized carbon nitride (CN) nanofibers were synthesized by hydrolyzing bulk CN in sodium hydroxide solution. The reversible assemble and disassemble behavior of the as-prepared CN nanofibers was investigated by using CO2 as a trigger to form a hydrogel network at first. Compared to the most widespread absorbent materials such as active carbon, graphene and previously reported supramolecular gel, the proposed CN hydrogel not only exhibited a competitive absorbing capacity (maximum absorbing capacity of methylene blue up to 402 mg/g) but also overcame the typical deficiencies such as poor selectivity and high energy-consuming regeneration. This work would provide a strategy to construct a 3D CN network and open an avenue for developing smart assembly for potential applications ranging from environment to selective extraction.

  9. Graphitic Carbon Nitride Nanosheets-Based Ratiometric Fluorescent Probe for Highly Sensitive Detection of H2O2 and Glucose.

    Science.gov (United States)

    Liu, Jin-Wen; Luo, Ying; Wang, Yu-Min; Duan, Lu-Ying; Jiang, Jian-Hui; Yu, Ru-Qin

    2016-12-14

    Graphitic carbon nitride (g-C 3 N 4 ) nanosheets, an emerging graphene-like carbon-based nanomaterial with high fluorescence and large specific surface areas, hold great potential for biosensor applications. Current g-C 3 N 4 nanosheets based fluorescent biosensors majorly rely on single fluorescent intensity reading through fluorescence quenching interactions between the nanosheets and metal ions. Here we report for the first time the development of a novel g-C 3 N 4 nanosheets-based ratiometric fluorescence sensing strategy for highly sensitive detection of H 2 O 2 and glucose. With o-phenylenediamine (OPD) oxidized by H 2 O 2 in the presence of horseradish peroxidase (HRP), the oxidization product can assemble on the g-C 3 N 4 nanosheets through hydrogen bonding and π-π stacking, which effectively quenches the fluorescence of g-C 3 N 4 while delivering a new emission peak. The ratiometric signal variations enable robust and sensitive detection of H 2 O 2 . On the basis of the glucose converting into H 2 O 2 through the catalysis of glucose oxidase, the g-C 3 N 4 -based ratiometric fluorescence sensing platform is also exploited for glucose assay. The developed strategy is demonstrated to give a detection limit of 50 nM for H 2 O 2 and 0.4 μM for glucose, at the same time, it has been successfully used for glucose levels detection in human serum. This strategy may provide a cost-efficient, robust, and high-throughput platform for detecting various species involving H 2 O 2 -generation reactions for biomedical applications.

  10. Dual-Layer Oxidation-Protective Plasma-Sprayed SiC-ZrB2/Al2O3-Carbon Nanotube Coating on Graphite

    Science.gov (United States)

    Ariharan, S.; Sengupta, Pradyut; Nisar, Ambreen; Agnihotri, Ankur; Balaji, N.; Aruna, S. T.; Balani, Kantesh

    2017-02-01

    Graphite is used in high-temperature gas-cooled reactors because of its outstanding irradiation performance and corrosion resistance. To restrict its high-temperature (>873 K) oxidation, atmospheric-plasma-sprayed SiC-ZrB2-Al2O3-carbon nanotube (CNT) dual-layer coating was deposited on graphite substrate in this work. The effect of each layer was isolated by processing each component of the coating via spark plasma sintering followed by isothermal kinetic studies. Based on isothermal analysis and the presence of high residual thermal stress in the oxide scale, degradation appeared to be more severe in composites reinforced with CNTs. To avoid the complexity of analysis of composites, the high-temperature activation energy for oxidation was calculated for the single-phase materials only, yielding values of 11.8, 20.5, 43.5, and 4.5 kJ/mol for graphite, SiC, ZrB2, and CNT, respectively, with increased thermal stability for ZrB2 and SiC. These results were then used to evaluate the oxidation rate for the composites analytically. This study has broad implications for wider use of dual-layer (SiC-ZrB2/Al2O3) coatings for protecting graphite crucibles even at temperatures above 1073 K.

  11. Microporous polystyrene particles for selective carbon dioxide capture.

    Science.gov (United States)

    Kaliva, Maria; Armatas, Gerasimos S; Vamvakaki, Maria

    2012-02-07

    This study presents the synthesis of microporous polystyrene particles and the potential use of these materials in CO(2) capture for biogas purification. Highly cross-linked polystyrene particles are synthesized by the emulsion copolymerization of styrene (St) and divinylbenzene (DVB) in water. The cross-link density of the polymer is varied by altering the St/DVB molar ratio. The size and the morphology of the particles are characterized by scanning and transmission electron microscopy. Following supercritical point drying with carbon dioxide or lyophilization from benzene, the polystyrene nanoparticles exhibit a significant surface area and permanent microporosity. The dried particles comprising 35 mol % St and 65 mol % DVB possess the largest surface area, ∼205 m(2)/g measured by Brunauer-Emmett-Teller and ∼185 m(2)/g measured by the Dubinin-Radushkevich method, and a total pore volume of 1.10 cm(3)/g. Low pressure measurements suggest that the microporous polystyrene particles exhibit a good separation performance of CO(2) over CH(4), with separation factors in the range of ∼7-13 (268 K, CO(2)/CH(4) = 5/95 gas mixture), which renders them attractive candidates for use in gas separation processes.

  12. Effective Thermal Conductivity of Graphite Materials with Cracks

    Science.gov (United States)

    Pestchaanyi, S. E.; Landman, I. S.

    The dependence of effective thermal diffusivity on temperature caused by volumetric cracks is modelled for macroscopic graphite samples using the three-dimensional thermomechanics code Pegasus-3D. At high off-normal heat loads typical of the divertor armour, thermostress due to the anisotropy of graphite grains is much larger than that due to the temperature gradient. Numerical simulation demonstrated that the volumetric crack density both in fine grain graphites and in the CFC matrix depends mainly on the local sample temperature, not on the temperature gradient. This allows to define an effective thermal diffusivity for graphite with cracks. The results obtained are used to explain intense cracking and particle release from carbon based materials under electron beam heat load. Decrease of graphite thermal diffusivity with increase of the crack density explains particle release mechanism in the experiments with CFC where a clear energy threshold for the onset of particle release has been observed in J. Linke et al. Fusion Eng. Design, in press, Bazyler et al., these proceedings. Surface temperature measurement is necessary to calibrate the Pegasus-3D code for simulation of ITER divertor armour brittle destruction.

  13. The Surface Interface Characteristics of Vertically Aligned Carbon Nanotube and Graphitic Carbon Fiber Arrays Grown by Thermal and Plasma Enhanced Chemical Vapor Deposition

    Science.gov (United States)

    Delzeit, Lance; Nguyen, Cattien; Li, Jun; Han, Jie; Meyyappan, M.

    2002-01-01

    The development of nano-arrays for sensors and devices requires the growth of arrays with the proper characteristics. One such application is the growth of vertically aligned carbon nanotubes (CNTs) and graphitic carbon fibers (GCFs) for the chemical attachment of probe molecules. The effectiveness of such an array is dependent not only upon the effectiveness of the probe and the interface between that probe and the array, but also the array and the underlaying substrate. If that array is a growth of vertically aligned CNTs or GCFs then the attachment of that array to the surface is of the utmost importance. This attachment provides the mechanical stability and durability of the array, as well as, the electrical properties of that array. If the detection is to be acquired through an electrical measurement, then the appropriate resistance between the array and the surface need to be fabricated into the device. I will present data on CNTs and GCFs grown from both thermal and plasma enhanced chemical vapor deposition. The focus will be on the characteristics of the metal film from which the CNTs and GCFs are grown and the changes that occur due to changes within the growth process.

  14. An ultrasensitive electrochemiluminescent immunosensor based on graphene oxide coupled graphite-like carbon nitride and multiwalled carbon nanotubes-gold for the detection of diclofenac.

    Science.gov (United States)

    Hu, Liuyi; Zheng, Jing; Zhao, Kang; Deng, Anping; Li, Jianguo

    2018-03-15

    In this study, a novel competition-type electrochemiluminescent (ECL) immunosensor for detecting diclofenac (DCF) was fabricated with graphene oxide coupled graphite-like carbon nitride (GO-g-C 3 N 4 ) as signal probe for the first time. The ECL intensity of carboxylated g-C 3 N 4 was significantly enhanced after being combined with graphene oxide (GO) which exhibited excellent charge-transport property. The sensing platform was constructed by multiwalled carbon nanotubes and gold nanoparticles (MWCNTs-AuNPs), which not only provided an effective matrix for immobilizing a large amount of coating antigen but also facilitated the electronic transmission rate to enhance the ECL intensity. Based on the synergistic effect of GO-g-C 3 N 4 and MWCNTs-AuNPs composite, the proposed sensor showed high sensitivity, good stability, and wide linearity for the detection of DCF in the range of 0.005-1000ngmL -1 with a detection limit of 1.7pgmL -1 . Furthermore, the developed immunoassay has been applied to real samples with satisfactory results. Therefore, this work provided a promising method for the detection of DCF and other small molecular compounds in the future. Copyright © 2017 Elsevier B.V. All rights reserved.

  15. Change of properties after oxidation of IG-11 graphite by air and CO2 gas

    International Nuclear Information System (INIS)

    Lim, Yun-Soo; Chi, Se-Hwan; Cho, Kwang-Yun

    2008-01-01

    Artificial graphite is typically manufactured by carbonization of a shaped body of a kneaded mixture using granular cokes as a filler and pitch as a binder. It undergoes a pitch impregnation process if necessary and finally applying graphitization heat treatment. The effect of thermal oxidation in air or a CO 2 atmosphere on IG-11 graphite samples is investigated in this study. The results show a localized oxidation process that progressively reveals the large coke particles with increasing level of overall weight loss in air. The surface of the graphite was peeled off and no change was found in the specific gravity after air oxidation. However, the specific gravity of graphite was continuously decreased by CO 2 oxidation. The decrease in the specific gravity by CO 2 oxidation was due to CO 2 gas that progressed from the surface to the interior. The pore shape after CO 2 oxidation differed from that under air oxidation

  16. Characterization of calcium carbonate sorbent particle in furnace environment

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Kang Soo [Aerosol and Particle Technology Laboratory, Department of Mechanical Engineering, KAIST 291 Daehak-ro, Yuseong-gu, Daejeon, 305-701 (Korea, Republic of); Jung, Jae Hee [Environment Sensor System Research Center, KIST 39-1 Hawolgok-dong, Seongbuk-gu, Seoul, 136-791 (Korea, Republic of); Keel, Sang In; Yun, Jin Han; Min, Tai Jin [Environmental Systems Research Division, KIMM 104 Sinseongno, Yuseong-gu, Daejeon, 305-343 (Korea, Republic of); Kim, Sang Soo, E-mail: sskim@kaist.ac.kr [Aerosol and Particle Technology Laboratory, Department of Mechanical Engineering, KAIST 291 Daehak-ro, Yuseong-gu, Daejeon, 305-701 (Korea, Republic of)

    2012-07-01

    The oxy-fuel combustion system is a promising technology to control CO{sub 2} and NO{sub X} emissions. Furthermore, sulfation reaction mechanism under CO{sub 2}-rich atmospheric condition in a furnace may lead to in-furnace desulfurization. In the present study, we evaluated characteristics of calcium carbonate (CaCO{sub 3}) sorbent particles under different atmospheric conditions. To examine the physical/chemical characteristics of CaCO{sub 3}, which is used as a sorbent particle for in-furnace desulfurization in the oxy-fuel combustion system, they were injected into high temperature drop tube furnace (DTF). Experiments were conducted at varying temperatures, residence times, and atmospheric conditions in a reactor. To evaluate the aerosolizing characteristics of the CaCO{sub 3} sorbent particle, changes in the size distribution and total particle concentration between the DTF inlet and outlet were measured. Structural changes (e.g., porosity, grain size, and morphology) of the calcined sorbent particles were estimated by BET/BJH, XRD, and SEM analyses. It was shown that sorbent particles rapidly calcined and sintered in the air atmosphere, whereas calcination was delayed in the CO{sub 2} atmosphere due to the higher CO{sub 2} partial pressure. Instead, the sintering effect was dominant in the CO{sub 2} atmosphere early in the reaction. Based on the SEM images, it was shown that the reactions of sorbent particles could be explained as a grain-subgrain structure model in both the air and CO{sub 2} atmospheres.

  17. In vitro cytotoxicity evaluation of nano-carbon particles with different sp{sup 2}/sp{sup 3} ratios

    Energy Technology Data Exchange (ETDEWEB)

    Li, S.S.; Wu, B.J.; Deng, Q.Y. [Key Laboratory for Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Guo, Y.B. [The Third People' s Hospital of Chengdu, Sichuan 610031 (China); Leng, Y.X., E-mail: yxleng@263.net [Key Laboratory for Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China); Huang, N. [Key Laboratory for Advanced Technologies of Materials, Ministry of Education, School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu, Sichuan 610031 (China)

    2017-06-01

    Graphitization occurs during the long-term service of a diamond-like carbon (DLC) modified artificial joint. Then, DLC wear debris, which are carbon particles with different sp{sup 2}/sp{sup 3} ratios and sizes ranging from the nano- to micro-meter scale produced. In this paper, to promote the application of DLC coating for artificial joint modification, the cytotoxicity of DLC debris (nano-carbon particles, NCs) with different sp{sup 2}/sp{sup 3} ratios was studied. The microstructure and physical characteristics of NCs with different sp{sup 2}/sp{sup 3} ratios were investigated by Raman spectroscopy, X-ray photoelectron spectroscopy (XPS), Transmission Electron Microscope (TEM) and Dynamic Light Scattering (DLS). Meanwhile, osteoblasts and macrophages were applied to characterize the cytotoxicity of the NCs. In vitro cytotoxicity assay results indicated that cells incubated with NCs of different sp{sup 2}/sp{sup 3} ratios had greater osteogenic capacity, and these particles caused a weaker immune response in comparison with CoCrMo particles. Taken together, the results indicated that NCs with different sp{sup 2}/sp{sup 3} ratios presented a good cytocompatibility than CoCrMo particles. But no significant differences were observed among NCs with different sp{sup 2}/sp{sup 3} ratios. The better cytocompatibility of NCs is mainly attributable to their surface charge. - Highlights: • NCs with different sp{sup 2}/sp{sup 3} ratios have been successfully prepared by annealing treatment. • NCs with different sp{sup 2}/sp{sup 3} ratios show good osteogenic capacity and lower immune response. • The good cytocompatibility of NCs is mainly dependent on its surface charge.

  18. Graphene quantum dots, graphene oxide, carbon quantum dots and graphite nanocrystals in coals

    Science.gov (United States)

    Dong, Yongqiang; Lin, Jianpeng; Chen, Yingmei; Fu, Fengfu; Chi, Yuwu; Chen, Guonan

    2014-06-01

    Six coal samples of different ranks have been used to prepare single-layer graphene quantum dots (S-GQDs). After chemical oxidation and a series of centrifugation separation, every coal could be treated into two fractions, namely, CoalA and CoalB. According to the characterization results of TEM, AFM, XRD, Raman and FTIR, CoalA was revealed to be mainly composed of S-GQDs, which have an average height of about 0.5 nm and an average plane dimension of about 10 nm. The obtained S-GQDs showed excitation-dependent fluorescence and excellent electrochemiluminescence. CoalB was found to be some other carbon-based nanomaterials (CNMs), including agglomerated GQDs, graphene oxide, carbon quantum dots and agglomerated carbon nanocrystals. Generally, low-ranked coals might be more suitable for the preparation of S-GQDs. The production yield of S-GQDs from the six investigated coals decreased from 56.30% to 14.66% when the coal rank increased gradually. In contrast, high-ranked coals had high production yield of CoalB and might be more suitable for preparing other CNMs that were contained in CoalB, although those CNMs were difficult to separate from each other in our experiment.Six coal samples of different ranks have been used to prepare single-layer graphene quantum dots (S-GQDs). After chemical oxidation and a series of centrifugation separation, every coal could be treated into two fractions, namely, CoalA and CoalB. According to the characterization results of TEM, AFM, XRD, Raman and FTIR, CoalA was revealed to be mainly composed of S-GQDs, which have an average height of about 0.5 nm and an average plane dimension of about 10 nm. The obtained S-GQDs showed excitation-dependent fluorescence and excellent electrochemiluminescence. CoalB was found to be some other carbon-based nanomaterials (CNMs), including agglomerated GQDs, graphene oxide, carbon quantum dots and agglomerated carbon nanocrystals. Generally, low-ranked coals might be more suitable for the preparation of

  19. Improved sensitivity and selectivity of uric acid voltammetric sensing with mechanically grinded carbon/graphite electrodes

    Czech Academy of Sciences Publication Activity Database

    Hasoň, Stanislav; Vetterl, Vladimír; Jelen, František; Fojta, Miroslav

    2009-01-01

    Roč. 54, č. 6 (2009), s. 1864-1873 ISSN 0013-4686 R&D Projects: GA AV ČR(CZ) KAN200040651; GA ČR(CZ) GA203/07/1195; GA MŠk(CZ) LC06035; GA ČR(CZ) GA202/08/1688; GA AV ČR(CZ) IAA400040804 Institutional research plan: CEZ:AV0Z50040507; CEZ:AV0Z50040702 Keywords : grinded carbon electrodes * voltammetry * uric acid Subject RIV: AQ - Safety, Health Protection, Human - Machine Impact factor: 3.325, year: 2009

  20. Purification and preparation of graphite oxide from natural graphite

    Energy Technology Data Exchange (ETDEWEB)

    Panatarani, C., E-mail: c.panatarani@phys.unpad.ac.id; Muthahhari, N.; Joni, I. Made [Instrumentation Systems and Functional Material Processing Laboratory, Department of Physics, Faculty of Mathematics and Natural Sciences, Universitas Padjadjaran, Padjadjaran University, Jl. Raya Bandung-Sumedang KM 21, Jatinangor, 45363, Jawa Barat (Indonesia); Rianto, Anton [Grafindo Nusantara Ltd., Belagio Mall Lantai 2, Unit 0 L3-19, Kawasan Mega Kuningan, Kav. B4 No.3, Jakarta Selatan (Indonesia)

    2016-03-11

    Graphite oxide has attracted much interest as a possible route for preparation of natural graphite in the large-scale production and manipulation of graphene as a material with extraordinary electronic properties. Graphite oxide was prepared by modified Hummers method from purified natural graphite sample from West Kalimantan. We demonstrated that natural graphite is well-purified by acid leaching method. The purified graphite was proceed for intercalating process by modifying Hummers method. The modification is on the reaction time and temperature of the intercalation process. The materials used in the intercalating process are H{sub 2}SO{sub 4} and KMNO{sub 4}. The purified natural graphite is analyzed by carbon content based on Loss on Ignition test. The thermo gravimetricanalysis and the Fouriertransform infrared spectroscopy are performed to investigate the oxidation results of the obtained GO which is indicated by the existence of functional groups. In addition, the X-ray diffraction and energy dispersive X-ray spectroscopy are also applied to characterize respectively for the crystal structure and elemental analysis. The results confirmed that natural graphite samples with 68% carbon content was purified into 97.68 % carbon content. While the intercalation process formed a formation of functional groups in the obtained GO. The results show that the temperature and reaction times have improved the efficiency of the oxidation process. It is concluded that these method could be considered as an important route for large-scale production of graphene.

  1. Chemical properties of various organic electrolytes for lithium rechargeable batteries. Pt. 1.. Characterization of passivating layer formed on graphite in alkyl carbonate solutions

    Energy Technology Data Exchange (ETDEWEB)

    Mori, Shoichiro; Asahina, Hitoshi; Suzuki, Hitoshi; Yonei, Ayako; Yokoto, Kiyomi [Tsukuba Research Center, Mitsubishi Chemical Corporation, Ibaraki (Japan)

    1997-09-01

    The characteristics and reaction mechanisms of the passivating film formed on the surface of graphite were investigated in ethylene carbonate-diethyl carbonate solutions containing LiClO{sub 4}, LiPF{sub 6} and LiN(SO{sub 2}CF{sub 3}){sub 2}. The electron consumption resulting on the irreversible capacity of graphite was almost equivalent to that used in the one-electron reduction of Li{sup +} found in the film. The electrochemical reactions in the first discharge process may be divided into the following steps: (i) `initial film formation step` from 1.4 to 0.55 V; (ii) `main film formation step` from 0.55 to 0.2 V, and (iii) `lithium intercalation step from 0.2 to 0.0 V. Most of the passivating film is formed together with the lithium intercalation reaction at step (ii). The passivating film formed at this step contained a significant amount of organic film such as EtOCO{sub 2}Li, (CH{sub 2}OCO{sub 2}Li){sub 2}, etc. Through the consecutive formation of passivating film at steps (i) and (ii), lithium intercalation into graphite proceeds smoothly without further decomposition of organic electrolyte. (orig.)

  2. Fluidized bed reactor for processing particles coated with carbon

    International Nuclear Information System (INIS)

    Marschollek, M.; Simon, W.; Walter, C.

    1978-01-01

    The carbon coating of production returns of these particles first has to be removed before the heavy metal core released can be reprocessed. For reasons of criticality, removal of burnt-up particles downwards must be possible in the fluidized bed reactor even if the reactor diameter is greater than 800 mm, and the material temperatures must not exceed 650 0 C. It consists of an upper cylindrical and a lower conical part, where, according to the invention, the gas distributor heads in the conical part are situated in several planes above one another for the fluidisation and combustion gas and where they are evently distributed over the reactor crossection, so that an even flow profile is achieved over the reactor cross section. (HP) [de

  3. Innershell ionization by fast protons, alpha particles and carbon ions

    International Nuclear Information System (INIS)

    Dijk, J.H. van.

    1984-01-01

    The subject of this thesis is the study of inner-shell excitations of atoms induced by fast charged particle collisions. A new method is described for measuring the spectrum of delta-electrons emitted by 208 Pb after excitation by 15 MeV protons or 50 MeV alpha particles. Experimental equipment is described. Results of both experiments are presented and compared with PWBA models and with calculations based on a semi-classical approximation. The small-impact-parameter ionization probabilities obtained are then compared with literature. Also small-impact-parameter measurements done with 100 MeV carbon ions are described. Besides K-shell measurements, the author also presents L-subshell ionization probability results for Pb. An appendix is added in which energy straggling problems in solid targets are treated. (Auth./G.J.P.)

  4. Synthesis of carbon-13 labelled carbonaceous deposits and their evaluation for potential use as surrogates to better understand the behaviour of the carbon-14-containing deposit present in irradiated PGA graphite

    Energy Technology Data Exchange (ETDEWEB)

    Payne, L., E-mail: liam.payne@bristol.ac.uk [Interface Analysis Centre, HH Wills Physics Laboratory, University of Bristol, BS8 1TL (United Kingdom); Walker, S.; Bond, G. [Centre for Materials Science, University of Central Lancashire, PR1 2HE (United Kingdom); Eccles, H. [John Tyndall Institute for Nuclear Research, School of Computing, Engineering and Physical Sciences, University of Central Lancashire, PR1 2HE (United Kingdom); Heard, P.J.; Scott, T.B. [Interface Analysis Centre, HH Wills Physics Laboratory, University of Bristol, BS8 1TL (United Kingdom); Williams, S.J. [Radioactive Waste Management, B587, Curie Avenue, Harwell Oxford, Didcot, OX11 0RH (United Kingdom)

    2016-03-15

    The present work has used microwave plasma chemical vapour deposition to generate suitable isotopically labelled carbonaceous deposits on the surface of Pile Grade A graphite for use as surrogates for studying the behaviour of the deposits observed on irradiated graphite extracted from UK Magnox reactors. These deposits have been shown elsewhere to contain an enhanced concentration of {sup 14}C compared to the bulk graphite. A combination of Raman spectroscopy, ion beam milling with scanning electron microscopy and secondary ion mass spectrometry were used to determine topography and internal morphology in the formed deposits. Direct comparison was made against deposits found on irradiated graphite samples trepanned from a Magnox reactor core and showed a good similarity in appearance. This work suggests that the microwave plasma chemical vapour deposition technique is of value in producing simulant carbon deposits, being of sufficiently representative morphology for use in non-radioactive surrogate studies of post-disposal behaviour of {sup 14}C-containing deposits on some irradiated Magnox reactor graphite.

  5. Laminated exfoliated graphite composite-metal compositions for fuel cell flow field plate or bipolar plate applications

    Science.gov (United States)

    Zhamu, Aruna; Shi, Jinjun; Guo, Jiusheng; Jang, Bor Z

    2014-05-20

    An electrically conductive laminate composition for fuel cell flow field plate or bipolar plate applications. The laminate composition comprises at least a thin metal sheet having two opposed exterior surfaces and a first exfoliated graphite composite sheet bonded to the first of the two exterior surfaces of the metal sheet wherein the exfoliated graphite composite sheet comprises: (a) expanded or exfoliated graphite and (b) a binder or matrix material to bond the expanded graphite for forming a cohered sheet, wherein the binder or matrix material is between 3% and 60% by weight based on the total weight of the first exfoliated graphite composite sheet. Preferably, the first exfoliated graphite composite sheet further comprises particles of non-expandable graphite or carbon in the amount of between 3% and 60% by weight based on the total weight of the non-expandable particles and the expanded graphite. Further preferably, the laminate comprises a second exfoliated graphite composite sheet bonded to the second surface of the metal sheet to form a three-layer laminate. Surface flow channels and other desired geometric features can be built onto the exterior surfaces of the laminate to form a flow field plate or bipolar plate. The resulting laminate has an exceptionally high thickness-direction conductivity and excellent resistance to gas permeation.

  6. Increasing the Fine Flaky Graphite Recovery in Flotation via a Combined MultipleTreatments Technique of Middlings

    Directory of Open Access Journals (Sweden)

    Weijun Peng

    2017-11-01

    Full Text Available As the residual flaky graphite ores become miscellaneous and fine, a single treatment technique for the middlings from the flotation process of graphite ore cannot efficiently recover the valuable graphite in the multistage grinding-flotation technology. In the study, the existence form of graphite and relationship of graphite with the associated gangue minerals were estimated by optical microscope analysis. The results indicated that the fine flaky graphite particles embedded with gangue minerals like a honeycomb, making it difficult to be beneficiated using the typical flotation technique. A combination technique of individual process and concentrated returning for the treatment of middlings was used to increase the graphite recovery based on the co-existing relationship between graphite and gangue minerals in the middlings. The graphite recovery of the final concentrate upgraded from 51.81% to 91.14% at a fixed carbon (FC content of 92.01% by a beneficiation process consisted of once coarse (94.41% passing 74 μm and rougher, five stages regrinding and six stages cleaning. The proposed treatment technique for middlings is of great significance to increase the recovery of fine flaky graphite.

  7. Glass-Graphite Composite Materials

    International Nuclear Information System (INIS)

    Mayzan, M.Z.H.; Lloyd, J.W.; Heath, P.G.; Stennett, M.C.; Hyatt, N.C.; Hand, R.J.

    2016-01-01

    A summary is presented of investigations into the potential of producing glass-composite materials for the immobilisation of graphite or other carbonaceous materials arising from nuclear power generation. The methods are primarily based on the production of base glasses which are subsequently sintered with powdered graphite or simulant TRISO particles. Consideration is also given to the direct preparation of glass-graphite composite materials using microwave technology. Production of dense composite wasteforms with TRISO particles was more successful than with powdered graphite, as wasteforms containing larger amounts of graphite were resistant to densification and the glasses tried did not penetrate the pores under the pressureless conditions used. Based on the results obtained it is concluded that the production of dense glassgraphite composite wasteforms will require the application of pressure. (author)

  8. Silver/iron oxide/graphitic carbon composites as bacteriostatic catalysts for enhancing oxygen reduction in microbial fuel cells

    Science.gov (United States)

    Ma, Ming; You, Shijie; Gong, Xiaobo; Dai, Ying; Zou, Jinlong; Fu, Honggang

    2015-06-01

    Biofilms from anode heterotrophic bacteria are inevitably formed over cathodic catalytic sites, limiting the performances of single-chamber microbial fuel cells (MFCs). Graphitic carbon (GC) - based nano silver/iron oxide (AgNPs/Fe3O4/GC) composites are prepared from waste pomelo skin and used as antibacterial oxygen reduction catalysts for MFCs. AgNPs and Fe3O4 are introduced in situ into the composites by one-step carbothermal reduction, enhancing their conductivity and catalytic activity. To investigate the effects of Fe species on the antibacterial and catalytic properties, AgNPs/Fe3O4/GC is washed with sulfuric acid (1 mol L-1) for 0.5 h, 1 h, and 5 h and marked as AgNPs/Fe3O4/GC-x (x = 0.5 h, 1 h and 5 h, respectively). A maximum power density of 1712 ± 35 mW m-2 is obtained by AgNPs/Fe3O4/GC-1 h, which declines by 4.12% after 17 cycles. Under catalysis of all AgNP-containing catalysts, oxygen reduction reaction (ORR) proceeds via the 4e- pathway, and no toxic effects to anode microorganisms result from inhibiting the cathodic biofilm overgrowth. With the exception of AgNPs/Fe3O4/GC-5 h, the AgNPs-containing composites exhibit remarkable power output and coulombic efficiency through lowering proton transfer resistance and air-cathode biofouling. This study provides a perspective for the practical application of MFCs using these efficient antibacterial ORR catalysts.

  9. Analysis of non-phthalates plasticizers on porous graphitic carbon by supercritical fluid chromatography using evaporative light scattering detection.

    Science.gov (United States)

    Vaccher, Claude; Decaudin, Bertrand; Sautou, Valérie; Lecoeur, Marie

    2014-09-12

    The analysis of several plasticizers, widely used in the production of medical devices, was investigated on porous graphitic carbon (PGC) stationary phase in supercritical fluid chromatography (SFC) with an evaporative light scattering detector (ELSD). Due to strong interaction of compounds with the PGC support, solvents of strong eluotropic strength were added to the CO2 supercritical fluid. The effect of alkyl chain (pentane, hexane, heptane) and chlorinated (CH2Cl2, CHCl3, CCl4) solvents was studied on the retention and on the ELSD detection of plasticizers. A co-solvent mixture composed of CHCl3/heptane, eluted under gradient mode, allowed a significant improvement of the ELSD response compared to the use of each solvent individually. Then, a central composite design (CCD) was implemented to optimize both the separation and the detection of plasticizers. The parameters involved were the outlet pressure, the gradient slope, the co-solvent composition and the drift tube temperature of the ELSD. After optimization, baseline separation of plasticizers was achieved in 7min and best signal-to-noise ratios were obtained with outlet pressure and drift tube temperature of ELSD set at 200bar and 31°C, respectively. The co-solvent mixture was also composed of CHCl3/heptane (35/65 v/v) and a gradient from 15 to 60% of co-solvent in 2.2min was employed. The results demonstrated that CCD is a powerful tool for the optimization of SFC/ELSD method and the response surface model analysis can provide statistical understandings of the significant factors required to achieve optimal separation and ELSD sensitivity. Copyright © 2014 Elsevier B.V. All rights reserved.

  10. Corrosion behaviour of the AlSi6Cu4 alloy and cast AlSi6Cu4-graphite particles composite

    Directory of Open Access Journals (Sweden)

    S. Holecek

    2009-04-01

    Full Text Available The corrosion behaviour of the AlSi6Cu4 alloy as a composite matrix and of composites with 8% vol. of graphite particles was investigated. The corrosion experiments were performed over a range of elevated temperatures and were carried out in sea water (3.5%NaCl solution. We have focused our attention to the determination of the mode of corrosion attack and to the determination of the rate ofcorrosion and other corrosion characteristics. Both as-cast and annealed matrix and composite specimens were tested, as well as the99.9% as-cast aluminium for comparison. Corrosion behaviour of the materials was assessed by the corrosion potential (Ec and bypotentiodynamic (polarization curves. As expected, composite is less corrosion resistant than the matrix alloy. In addition to pitting,a severe galvanic corrosion occurs as a result of galvanic couple aluminium/graphite formation. Corrosion potentials imply that examinedmaterials would be sufficiently resistant in non or slightly oxidizing solutions without dissolved oxygen. All studied materials corrode very slowly at potentials negative to corrosion potential, while at potentials positive to corrosion potential the corrosion rate goes up by 1 or 2 orders.

  11. Characteristics of activated carbon remove sulfur particles against smog.

    Science.gov (United States)

    Ge, Shengbo; Liu, Zhenling; Furuta, Yuzo; Peng, Wanxi

    2017-09-01

    Sulfur particles, which could cause diseases, were the main powder of smog. And activated carbon had the very adsorption characteristics. Therefore, five sulfur particles were adsorbed by activated carbon and were analyzed by FT-IR. The optimal adsorption time were 120 min of Na 2 SO 3 , 120 min of Na 2 S 2 O 8 , 120 min of Na 2 SO 4 , 120 min of Fe 2 (SO 4 ) 3 and 120 min of S. FT-IR spectra showed that activated carbon had the eight characteristic absorption of S-S stretch, H 2 O stretch, O-H stretch, -C-H stretch, conjugated C 000000000000 000000000000 000000000000 111111111111 000000000000 111111111111 000000000000 000000000000 000000000000 O stretch or CC stretch, CH 2 bend, C-O stretch and acetylenic C-H bend vibrations at 3850 cm -1 , 3740 cm -1 , 3430 cm -1 , 2920 cm -1 , 1630 cm -1 , 1390 cm -1 , 1110 cm -1 and 600 cm -1 , respectively. For Na 2 SO 3 , the peaks at 2920 cm -1 , 1630 cm -1 , 1390 cm -1 and 1110 cm -1 achieved the maximum at 20 min. For Na 2 S 2 O 8 , the peaks at 3850 cm -1 , 3740 cm -1 and 2920 cm -1 achieved the maximum at 60 min. The peaks at 1390 cm -1 , 1110 cm -1 and 600 cm -1 achieved the maximum at 40 min. For Na 2 SO 4 , the peaks at 3430 cm -1 , 2920 cm -1 , 1630 cm -1 , 1390 cm -1 , 1110 cm -1 and 600 cm -1 achieved the maximum at 60 min. For Fe 2 (SO 4 ) 3 , the peaks at 1390 cm -1 , 1110 cm -1 and 600 cm -1 achieved the maximum at 20 min. For S, the peaks at 1630 cm -1 , 1390 cm -1 and 600 cm -1 achieved the maximum at 120 min. It provided that activated carbon could remove sulfur particles from smog air to restrain many anaphylactic diseases.

  12. Graphitic encapsulation of MgO and Fe3C nanoparticles in the reaction of iron pentacarbonyl with magnesium

    International Nuclear Information System (INIS)

    Dyjak, Sławomir; Cudziło, Stanisław; Polański, Marek; Budner, Bogusław; Bystrzycki, Jerzy

    2013-01-01

    A simple method to produce highly ordered carbon nanostructures by combustion synthesis is presented. Graphite-encapsulated magnesium oxide, iron carbide nanoparticles and carbon nanobelts were synthesized by the one-step reduction of iron pentacarbonyl with magnesium. High-resolution transmission electron microscopy analysis of the products revealed nanocrystalline MgO and Fe 3 C particles surrounded by a well-crystallized, tight graphite film. The possible formation mechanism is presented and discussed. - Highlights: • We present a simple method to produce highly ordered carbon nanostructures by combustion synthesis. • The cubic MgO particles are completely coated by tight graphitic shells. • The mechanism of formation a distant carbon film on MgO surface has been discussed. • The presented method can be applied to synthesis of other core-shell structures

  13. Flexible, highly graphitized carbon aerogels based on bacterial cellulose/lignin: Catalyst-free synthesis and its application in energy storage devices

    KAUST Repository

    Xu, Xuezhu

    2015-04-15

    Currently, most carbon aerogels are based on carbon nanotubes (CNTs) or graphene, which are produced through a catalyst-assisted chemical vapor deposition method. Biomass based organic aerogels and carbon aerogels, featuring low cost, high scalability, and small environmental footprint, represent an important new research direction in (carbon) aerogel development. Cellulose and lignin are the two most abundant natural polymers in the world, and the aerogels based on them are very promising. Classic silicon aerogels and available organic resorcinol-formaldehyde (RF) or lignin-resorcinol-formaldehyde (LRF) aerogels are brittle and fragile; toughening of the aerogels is highly desired to expand their applications. This study reports the first attempt to toughen the intrinsically brittle LRF aerogel and carbon aerogel using bacterial cellulose. The facile process is catalyst-free and cost-effective. The toughened carbon aerogels, consisting of blackberry-like, core-shell structured, and highly graphitized carbon nanofibers, are able to undergo at least 20% reversible compressive deformation. Due to their unique nanostructure and large mesopore population, the carbon materials exhibit an areal capacitance higher than most of the reported values in the literature. This property makes them suitable candidates for flexible solid-state energy storage devices. Besides energy storage, the conductive interconnected nanoporous structure can also find applications in oil/water separation, catalyst supports, sensors, and so forth. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  14. Study of Coating Geometries and Photoluminescence Properties of Metal Nanoparticles/Graphite Composites

    Directory of Open Access Journals (Sweden)

    Pasquale Barone

    2014-01-01

    Full Text Available In this work we present the results of a study of growth and characterization of metal nanoparticles (Ag, Au, and Co/carbon surfaces. The nanoparticles grew by laser ablation technique and their dimensions were controlled by light scattering study and AFM microscopy before their insertion on graphite surface. Nanoparticles appear randomly disposed on carbon surfaces aggregating to form big particles only in the case of silver. The different behavior of metal nanoparticles on carbon surface was explained in terms of different metal wetting of surface, in agreement with previous theoretical results of He et al. Chemical information, obtained by X-ray photoelectron spectroscopy, indicated that the doping process is a simple physisorption while the interfacial interaction between particles and carbon layers causes local defects in graphite structure and the appearance of a strong photoluminescence signal for all composites. Moreover, the visible optical absorption decreases about 10% indicating the progressive metallization of carbon surface.

  15. Pt nanoparticles embedded on reduced graphite oxide with excellent electrocatalytic properties

    Energy Technology Data Exchange (ETDEWEB)

    Saravanan, Gengan, E-mail: saravanan3che@gmail.com [Central University of Tamil Nadu, Department of Chemistry, Thiruvarur, 610101 (India); Mohan, Subramanian, E-mail: sanjnamohan@yahoo.com [EMFT Division, CSIR-Central Electrochemical Research Institute, Tamilnadu, Karaikudi 630 006 (India)

    2016-11-15

    Graphical abstract: RGO/Nano Pt: This study explore the electrocatalytic oxidation performance of reduced graphite oxide (RGO) anchored with nano Pt. This graphene composite reveal superior electrooxidation performance that is associated with the flexible RGO matrix and the uniform distribution of Pt particles, which enhances surface area, fast electron transfer, uniform particle size distribution; consequently, the RGO matrix provides more stability to Pt particles during electrooxidation process. Display Omitted - Highlights: • Greener electrochemical method applied to prepare well-dispersed Pt-rGO. • Pt-rGO large surface area excellent charge transfer better catalytic activity. • Low-cost highly efficient carbon-based electrodes for direct formic acid fuel cell. • rGO an excellent support to anchor Pt nanoparticles on its surface. • Pt-rGO distinctly enhanced current density towards formic acid electrooxidation. - Abstract: Economically viable electrochemical approach has been developed for the synthesis of Pt nanoparticles through electrodeposition technique on the surface of Reduced Graphite Oxide (RGO). Pt nanoparticles embedded Reduced Graphite Oxide on Glassy Carbon Electrode are employed (Pt-rGO/GCE) for electrooxidation of formic acid. Scanning Electron Microscopy (SEM) image and Transmission Electron Microscopy (TEM) image shows that reduced graphite oxide act as an excellent support to anchor the Pt nanoparticles. Cyclic voltammetry results confirmed that Pt-rGO/GCE enhanced current density as many folds than that of bare platinum electrode for electrooxidation of formic acid. X-ray diffraction (XRD) patterns for Pt-graphene composites illustrate that peaks at 69.15 and 23° for Pt (220) and graphene carbon (002) respectively. {sup 13}C NMR spectrum of the electrochemically reduced graphite oxide resonance contains only one peak at 133 ppm which retains graphitic sp{sup 2} carbon and does not contain any oxygenated carbon and the carbonyl

  16. Improved adaptability of polyaryl-ether-ether-ketone with texture pattern and graphite-like carbon film for bio-tribological applications

    Science.gov (United States)

    Ren, Siming; Huang, Jinxia; Cui, Mingjun; Pu, Jibin; Wang, Liping

    2017-04-01

    With the development of surface treatment technology, an increasing number of bearings, seals, dynamic friction drive or even biomedical devices involve a textured surface to improve lubrication and anti-wear. The present investigation has been conducted in order to evaluate the friction and wear behaviours of textured polyaryl-ether-ether-ketone (PEEK) coated with a graphite-like carbon (GLC) film sliding against stainless steel pin in biological medium. Compared with pure PEEK, the PEEK coated with GLC film shows excellent tribological performance with a low friction of 0.08 and long lifetime (wear volumes are about 3.78 × 10-4 mm3 for un-textured one and 2.60 × 10-4 mm3 for textured GLC film after 36,000 s of sliding) under physiological saline solution. In particular, the GLC film with appropriate dimple area density is effective to improve friction reduction and wear resistance properties of PEEK substrate under biological solution, which is attributed to the entrapment of wear debris in the dimples to inhibit the graphitization and the fluid dynamic pressure effect derived from the texture surface to increase the thickness in elastohydrodynamic lubrication (EHL) film during sliding motions. Moreover, the friction coefficient of GLC film under physiological saline solution decreases with the increase in the applied load. With the increasing applied load, the texture surface is responsible for accounting the improved wear resistance and a much lower graphitization of the GLC film during whole test.

  17. Continuous Carbon Nanotube-Ultrathin Graphite Hybrid Foams for Increased Thermal Conductivity and Suppressed Subcooling in Composite Phase Change Materials.

    Science.gov (United States)

    Kholmanov, Iskandar; Kim, Jaehyun; Ou, Eric; Ruoff, Rodney S; Shi, Li

    2015-12-22

    Continuous ultrathin graphite foams (UGFs) have been actively researched recently to obtain composite materials with increased thermal conductivities. However, the large pore size of these graphitic foams has resulted in large thermal resistance values for heat conduction from inside the pore to the high thermal conductivity graphitic struts. Here, we demonstrate that the effective thermal conductivity of these UGF composites can be increased further by growing long CNT networks directly from the graphite struts of UGFs into the pore space. When erythritol, a phase change material for thermal energy storage, is used to fill the pores of UGF-CNT hybrids, the thermal conductivity of the UGF-CNT/erythritol composite was found to increase by as much as a factor of 1.8 compared to that of a UGF/erythritol composite, whereas breaking the UGF-CNT bonding in the hybrid composite resulted in a drop in the effective room-temperature thermal conductivity from about 4.1 ± 0.3 W m(-1) K(-1) to about 2.9 ± 0.2 W m(-1) K(-1) for the same UGF and CNT loadings of about 1.8 and 0.8 wt %, respectively. Moreover, we discovered that the hybrid structure strongly suppresses subcooling of erythritol due to the heterogeneous nucleation of erythritol at interfaces with the graphitic structures.

  18. Self-assembly graphitic carbon nitride quantum dots anchored on TiO_2 nanotube arrays: An efficient heterojunction for pollutants degradation under solar light

    International Nuclear Information System (INIS)

    Su, Jingyang; Zhu, Lin; Geng, Ping; Chen, Guohua

    2016-01-01

    Highlights: • Carbon nitride quantum dots (CNQDs) were decorated onto TiO_2 nanotube arrays (NTAs). • The CNQDs/TiO_2 NTAs exhibits much improved photoelectrochemical activity. • The heterojunction displays efficient removal efficiencies for RhB and phenol. • Pollutants degradation mechanism over CNQDs/TiO_2 NTAs was clarified. - Abstract: In this study, an efficient heterojunction was constructed by anchoring graphitic carbon nitride quantum dots onto TiO_2 nanotube arrays through hydrothermal reaction strategy. The prepared graphitic carbon nitride quantum dots, which were prepared by solid-thermal reaction and sequential dialysis process, act as a sensitizer to enhance light absorption. Furthermore, it was demonstrated that the charge transfer and separation in the formed heterojunction were significantly improved compared with pristine TiO_2. The prepared heterojunction was used as a photoanode, exhibiting much improved photoelectrochemical capability and excellent photo-stability under solar light illumination. The photoelectrocatalytic activities of prepared heterojunction were demonstrated by degradation of RhB and phenol in aqueous solution. The kinetic constants of RhB and phenol degradation using prepared photoelectrode are 2.4 times and 4.9 times higher than those of pristine TiO_2, respectively. Moreover, hydroxyl radicals are demonstrated to be dominant active radicals during the pollutants degradation.

  19. A Study Of Physical Properties Of Matrix Graphite Particle's Distribution As Ras Materials On 900oC Baking Stage Temperature

    International Nuclear Information System (INIS)

    Sajekti, Kasilani Noor; Dahroni, Imam; Nawangsih, Endang

    2000-01-01

    To aim's the physical characteristic of matrix graphite materials the physical basic characteristics were necessary prepared. Investigation of calsine cokes particle size distribution effect on 900 o C temperature baking stage had been done. The calsine coke and tar pitch were crushed and sieved, to get a particle size 63; 90; 106 and 125 μm, making pellet by mixed with 33% weight of tar pitch, than grilled at 900 o C during 30 minutes. Grilled products: physical (bulk density, electrical resistivity), mechanics (hardness, compressive strength) and micro's (surface area, total and pore radius) were analyzed. From the 9 samples, 3 samples in fulfilled condition with mixed particle size of calsine cokes 63 and 106 μm and the best weight ratio between calsine coke and tar pitch were 2/3:4/3 to 1. The physical properties yield were 1.19 g/mL bulk density, the electrical resistivity 2.63 Ωcm, the hardness 5.90 kg/mm 2 , the compressive strength 1600 Newton, the density (N 2 adsorbate) 2.89 g/mL, the specific surface area 8.08 mm 2 /g,the total pore /volume 1.48% and the average pore radius 12.60 Angstrom

  20. The preparation of polytrifluorochloroethylene (PCTFE) micro-particles and application on treating bearing steel surfaces to improve the lubrication effect for copper-graphite (Cu/C)

    Science.gov (United States)

    Lu, Hailin; Zhang, Pengpeng; Ren, Shanshan; Guo, Junde; Li, Xing; Dong, Guangneng

    2018-01-01

    Contact mechanical seal is a normal technology applied on middle axis of liquid rocket turbo pump, and the kinetic and static seal rings contact low temperature rocket propellant. Copper-graphite (Cu/C) composite as an excellent self-lubrication material was widely used in aerospace industry, this study took Cu/C as ball and bearing steel as disk to investigate the tribology properties, and distilled water were used to simulate the lox tribology performances. This study prepared polytrifluorochloroethylene (PCTFE) micro-particles which were coated on the oxide surfaces of bearing steel disk at temperature of 150 °C. The tribology results showed that the oxide surfaces treated with micro PCTFE particles have lower fiction coefficient and lower wear rate than original disk in water, and the wear morphology revealed that the treated surfaces obviously had less Cu/C composite transfer film than original disk. Meanwhile SEM, EDS, XRD, XPS and light microscope etc revealed that PCTFE micro-particles could associate with the oxide surfaces and caused higher water contact angle, due to the properties of the fluorine-containing composite may cause the good lubrication effect in water. Thus this technology shows great potential to enhance tribological performances for aerospace industry on a large scale.

  1. Catalytic Metal Free Production of Large Cage Structure Carbon Particles: A Candidate for Hydrogen Storage

    Science.gov (United States)

    Kimura, Yuki; Nuth, Joseph A., III; Ferguson, Frank T.

    2005-01-01

    We will demonstrate that carbon particles consisting of large cages can be produced without catalytic metal. The carbon particles were produced in CO gas as well as by introduction of 5% methane gas into the CO gas. The gas-produced carbon particles were able to absorb approximately 16.2 wt% of hydrogen. This value is 2.5 times higher than the 6.5 wt% goal for the vehicular hydrogen storage proposed by the Department of Energy in the USA. Therefore, we believe that this carbon particle is an excellent candidate for hydrogen storage for fuel cells.

  2. Measurement and investigation of effects of coal tar pitch fractions in nuclear graphite properties

    International Nuclear Information System (INIS)

    Fatemi, K.; Fatoorehchian, S.; Ahari Hashemi, F.; Ahmadi, Sh.

    2003-01-01

    Coal tar pitch has a complex chemical structure. Determination of α, β, γ fractions, is one of the methods to get information about its properties. In graphite fabrication it plays a role as a binder for coke particles. During the thermal treatment it carbonizes and changes to a secondary coke. This has considerable affects on the graphite properties. In this paper, determination of α, β, γ-1 fraction in three different types of pitches have been carried out. Graphite specimens have been fabricated by using these pitches and anisotropy coke in laboratory scale. The graphite properties have been compared with the nuclear graphite prototype. The comparison of the results showed that the density and compression strength are appreciable while the anisotropy factor of properties is about one. The linear thermal expansion in graphite from Iranian pitch had a better, result, where it stands in the nuclear range of usage. As a result, our studies showed that the graphite properties are affected by properties of pitch fractions, where it can be used as a proper sample for the graphite fabrication

  3. Dissociation of carbon dioxide and creation of carbon particles and films at room temperature

    Energy Technology Data Exchange (ETDEWEB)

    Fukuda, Takahiro [Bio-Nano Electronics Research Centre, Toyo University, 2100 Kujirai, Kawagoe Saitama 350-8585 (Japan); Maekawa, Toru [Bio-Nano Electronics Research Centre, Toyo University, 2100 Kujirai, Kawagoe Saitama 350-8585 (Japan); Hasumura, Takashi [Bio-Nano Electronics Research Centre, Toyo University, 2100 Kujirai, Kawagoe Saitama 350-8585 (Japan); Rantonen, Nyrki [Bio-Nano Electronics Research Centre, Toyo University, 2100 Kujirai, Kawagoe Saitama 350-8585 (Japan); Ishii, Koji [Bio-Nano Electronics Research Centre, Toyo University, 2100 Kujirai, Kawagoe Saitama 350-8585 (Japan); Nakajima, Yoshikata [Bio-Nano Electronics Research Centre, Toyo University, 2100 Kujirai, Kawagoe Saitama 350-8585 (Japan); Hanajiri, Tatsuro [Bio-Nano Electronics Research Centre, Toyo University, 2100 Kujirai, Kawagoe Saitama 350-8585 (Japan); Yoshida, Yoshikazu [Bio-Nano Electronics Research Centre, Toyo University, 2100 Kujirai, Kawagoe Saitama 350-8585 (Japan); Whitby, Raymond [School of Pharmacy and Biomolecular Sciences, University of Brighton, Cockroft Building, Lewes Road, Brighton BN2 4GJ (United Kingdom); Mikhalovsky, Sergey [School of Pharmacy and Biomolecular Sciences, University of Brighton, Cockroft Building, Lewes Road, Brighton BN2 4GJ (United Kingdom)

    2007-09-15

    As fluids approach their gas-liquid critical points, the physical properties such as the specific heat and compressibility diverge due to the formation of large molecular clusters. Incident light cannot penetrate near-critical fluids because of the large clusters, a phenomenon known as critical opalescence. In this paper, we irradiate near-critical carbon dioxide (ncCO{sub 2}), the critical temperature and pressure of which are 31.0{sup 0}C and 7.38 MPa, with a laser beam of 213, 266, 355 and 532 nm wavelength and show that CO{sub 2} is dissociated and particles are produced when the system is set so close to the critical point that critical opalescence occurs in the case of 213 and 266 nm wavelength, whereas no particles are produced when the temperature is made to deviate from the critical value. We also apply a dc electric field to ncCO{sub 2} during irradiation with a laser beam of 213 and 266 nm wavelength and find that particles are formed on both anode and cathode. As the intensity of the electric field increases, films are formed on the electrodes. Electron diffraction patterns and energy-dispersive x-ray, Auger electron, x-ray photoelectron and Raman spectroscopic analyses show that the particles and films are composed of amorphous carbon.

  4. Dissociation of carbon dioxide and creation of carbon particles and films at room temperature

    Science.gov (United States)

    Fukuda, Takahiro; Maekawa, Toru; Hasumura, Takashi; Rantonen, Nyrki; Ishii, Koji; Nakajima, Yoshikata; Hanajiri, Tatsuro; Yoshida, Yoshikazu; Whitby, Raymond; Mikhalovsky, Sergey

    2007-09-01

    As fluids approach their gas-liquid critical points, the physical properties such as the specific heat and compressibility diverge due to the formation of large molecular clusters. Incident light cannot penetrate near-critical fluids because of the large clusters, a phenomenon known as critical opalescence. In this paper, we irradiate near-critical carbon dioxide (ncCO2), the critical temperature and pressure of which are 31.0°C and 7.38 MPa, with a laser beam of 213, 266, 355 and 532 nm wavelength and show that CO2 is dissociated and particles are produced when the system is set so close to the critical point that critical opalescence occurs in the case of 213 and 266 nm wavelength, whereas no particles are produced when the temperature is made to deviate from the critical value. We also apply a dc electric field to ncCO2 during irradiation with a laser beam of 213 and 266 nm wavelength and find that particles are formed on both anode and cathode. As the intensity of the electric field increases, films are formed on the electrodes. Electron diffraction patterns and energy-dispersive x-ray, Auger electron, x-ray photoelectron and Raman spectroscopic analyses show that the particles and films are composed of amorphous carbon.

  5. Dissociation of carbon dioxide and creation of carbon particles and films at room temperature

    International Nuclear Information System (INIS)

    Fukuda, Takahiro; Maekawa, Toru; Hasumura, Takashi; Rantonen, Nyrki; Ishii, Koji; Nakajima, Yoshikata; Hanajiri, Tatsuro; Yoshida, Yoshikazu; Whitby, Raymond; Mikhalovsky, Sergey

    2007-01-01

    As fluids approach their gas-liquid critical points, the physical properties such as the specific heat and compressibility diverge due to the formation of large molecular clusters. Incident light cannot penetrate near-critical fluids because of the large clusters, a phenomenon known as critical opalescence. In this paper, we irradiate near-critical carbon dioxide (ncCO 2 ), the critical temperature and pressure of which are 31.0 0 C and 7.38 MPa, with a laser beam of 213, 266, 355 and 532 nm wavelength and show that CO 2 is dissociated and particles are produced when the system is set so close to the critical point that critical opalescence occurs in the case of 213 and 266 nm wavelength, whereas no particles are produced when the temperature is made to deviate from the critical value. We also apply a dc electric field to ncCO 2 during irradiation with a laser beam of 213 and 266 nm wavelength and find that particles are formed on both anode and cathode. As the intensity of the electric field increases, films are formed on the electrodes. Electron diffraction patterns and energy-dispersive x-ray, Auger electron, x-ray photoelectron and Raman spectroscopic analyses show that the particles and films are composed of amorphous carbon

  6. Hydrogen storage in graphite nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Park, C.; Tan, C.D.; Hidalgo, R.; Baker, R.T.K.; Rodriguez, N.M. [Northeastern Univ., Boston, MA (United States). Chemistry Dept.

    1998-08-01

    Graphite nanofibers (GNF) are a type of material that is produced by the decomposition of carbon containing gases over metal catalyst particles at temperatures around 600 C. These molecularly engineered structures consist of graphene sheets perfectly arranged in a parallel, perpendicular or at angle orientation with respect to the fiber axis. The most important feature of the material is that only edges are exposed. Such an arrangement imparts the material with unique properties for gas adsorption because the evenly separated layers constitute the most ordered set of nanopores that can accommodate an adsorbate in the most efficient manner. In addition, the non-rigid pore walls can also expand so as to accommodate hydrogen in a multilayer conformation. Of the many varieties of structures that can be produced the authors have discovered that when gram quantities of a selected number of GNF are exposed to hydrogen at pressures of {approximately} 2,000 psi, they are capable of adsorbing and storing up to 40 wt% of hydrogen. It is believed that a strong interaction is established between hydrogen and the delocalized p-electrons present in the graphite layers and therefore a new type of chemistry is occurring within these confined structures.

  7. Sensitive detection of cyclophosphamide using DNA-modified carbon paste, pencil graphite and hanging mercury drop electrodes.

    Science.gov (United States)

    Palaska, P; Aritzoglou, E; Girousi, S

    2007-05-15

    The interaction of cyclophosphamide (CP) with calf thymus double-stranded DNA (dsDNA) and thermally denatured single-stranded DNA (ssDNA) immobilized at the carbon paste (CPE) and pencil graphite electrodes (PGE), was studied electrochemically based on oxidation signals of guanine and adenine using differential pulse voltammetry (DPV). As a result of the interaction of CP with DNA, the voltammetric signals of guanine and adenine increased in the case of dsDNA while a slight increase was observed in ssDNA. The effect of experimental parameters such as the interaction time between CP and DNA forms and the concentration of CP, were studied using DPV with CPE and PGE. Additionally, reproducibility and detection limits were determined using both electrodes. A comparison of the analytical performance between CPE and PGE was done. Our results showed that these two different DNA biosensors could be used for the sensitive, rapid and cost effective detection of CP itself as well as of CP-DNA interaction. Furthermore, the interaction of CP with dsDNA and ssDNA was studied in solution and at the electrode surface by means of alternating current voltammetry (ACV) in 0.3M NaCl and 50mM sodium phosphate buffer (pH 8.5) supporting electrolyte, using a hanging mercury drop electrode (HMDE) as working electrode. The conclusions of this study were mainly based on tensammetric peaks I (at -1.183V) and II (-1.419V) of DNA. This study involved the interaction of CP with surface-confined and solution phase DNA where experimental parameters, such as the concentration of CP and the interaction time, were studied. By increasing the concentration of CP, an increase of peak II was observed in both ds and ssDNA, while an increase of peak I was observed only in the case of dsDNA. An overall conclusion of the study using HMDE was that the interaction of CP with surface-confined DNA significantly differed from that with solution phase DNA. The increase of peaks I and II was lower in the case of

  8. Experience with graphite in JET

    International Nuclear Information System (INIS)

    Pick, M.A.; Celentano, G.; Deksnis, E.; Dietz, K.J.; Shaw, R.; Sonnenberg, K.; Walravens, M.

    1987-01-01

    During the current operational period of JET more than 50% of the internal area of the machine is covered in graphite tiles. This includes the 15 m 2 of carbon tiles installed in the new toroidal limiter, the 40 poloidal belts of graphite tiles covering the U-joints and bellows as well as a two metre high ring (-- 20 m 2 ) or carbon tiles on the inner wall of the Torus. A ring of tiles in the equatorial plane (3 tiles high) consists of carbon-carbon fibre tiles. Test bed results indicated that the fine grained graphite tiles cracked at ∼ 1 kW/cm 2 for 2s of irradiation whereas the carbon-carbon fibre tiles were able to sustain a flux, limited by the irradiation facility, of 3.5 kW for 3s without any damage. The authors report on the generally positive experience they have had had with the installed graphite during the present and previous in-vessel configurations. This includes the physical integrity of the tiles under severe conditions such as high energy run-away electron beams, plasma disruptions and high heat fluxes. They report on the importance of the precise positioning of the inner wall and x-point tiles at the very high power fluxes of JET and the effect of deviations on both graphite and carbon-fibre tiles

  9. In-situ development of carbon nanotubes network and graphitic carbon by catalytic modification of phenolic resin binder in Al2O3–MgO–C refractories

    Directory of Open Access Journals (Sweden)

    Atul V. Maldhure

    2017-09-01

    Full Text Available In-situ formation of cross-linked carbon nanotubes network reinforced the refractory matrix and helps to improve the mechanical properties at elevated temperature. In this paper, the effect of modified phenol-formaldehyde (PF resin binder on the various mechanical properties of alumina–magnesia–carbon (AMC refractories was investigated. Initially, PF resin was modified by adding a different proportion of nickel catalyst. The AMC specimens (with the 7% carbon were prepared by using 5% of modified PF resin. The pressed samples were cured at 180 °C for 24 h and characterized by XRD, Raman spectroscopy, and FE-SEM. The characterisation shows that, in-situ formation of graphitic carbon and carbon nanotubes network in the specimens due to modification of PF resin. In-situ formation of phases leads to enhancement of density and mechanical properties of refractory at elevated temperature due to the reinforcing effect.

  10. A microstructurally based fracture model for nuclear graphite

    International Nuclear Information System (INIS)

    Burchell, T.D.

    1991-01-01

    This paper reports the physical basis of, and assumptions behind, a fracture model for nuclear graphites. Microstructurally related inputs, such as filler particle size, filler particle fracture toughness (K Ic ), density, pore size distribution, number of pores and specimen geometry (size and volume), are utilized in the model. The model has been applied to two graphites, Great Lakes Carbon Corporation grade H-451 and Toyo Tanso grade IG-110. For each graphite, the predicted tensile failure probabilities are compared with experimental data generated using ASTM Standard C-749 tensile test specimens. The predicted failure probabilities are in close agreement with the experimental data, particularly in the case of the H-451. The model is also shown to qualitatively predict the influence on the failure probabilities of changes in filler particle size, density, pore size, pore size distribution, number of pores and specimen geometry (stressed volume). The good performance is attributed to the sound physical basis of the model, which recognizes the dominant role of porosity in controlling crack initiation and propagation during graphite fracture. 8 refs., 12 figs., 1 tab

  11. Composite carbon foam electrode

    Science.gov (United States)

    Mayer, Steven T.; Pekala, Richard W.; Kaschmitter, James L.

    1997-01-01

    Carbon aerogels used as a binder for granularized materials, including other forms of carbon and metal additives, are cast onto carbon or metal fiber substrates to form composite carbon thin film sheets. The thin film sheets are utilized in electrochemical energy storage applications, such as electrochemical double layer capacitors (aerocapacitors), lithium based battery insertion electrodes, fuel cell electrodes, and electrocapacitive deionization electrodes. The composite carbon foam may be formed by prior known processes, but with the solid particles being added during the liquid phase of the process, i.e. prior to gelation. The other forms of carbon may include carbon microspheres, carbon powder, carbon aerogel powder or particles, graphite carbons. Metal and/or carbon fibers may be added for increased conductivity. The choice of materials and fibers will depend on the electrolyte used and the relative trade off of system resistivty and power to system energy.

  12. Electrochemical deposition of carbon films on titanium in molten LiCl–KCl–K2CO3

    International Nuclear Information System (INIS)

    Song, Qiushi; Xu, Qian; Wang, Yang; Shang, Xujing; Li, Zaiyuan

    2012-01-01

    Electrodeposition of carbon films on the oxide-scale-coated titanium has been performed in a LiCl–KCl–K 2 CO 3 melt, which are characterized by scanning electron microscopy, Raman spectroscopy and X-ray diffraction analysis. The electrochemical process of carbon deposition is investigated by cyclic voltammetry on the graphite, titanium and oxide-scale-coated titanium electrodes. The particle-size-gradient carbon films over the oxide-scale-coated titanium can be achieved by electrodeposition under the controlled potentials for avoiding codeposition of lithium carbide. The deposited carbon films are comprised of micron-sized ‘quasi-spherical’ carbon particles with graphitized and amorphous phases. The cyclic voltammetry behavior on the graphite, titanium and oxide-scale-coated titanium electrodes shows that CO 3 2− ions are reduced most favorably on the graphite for the three electrodes. Lithium ions can discharge under the less negative potential on the electrode containing carbon compared with titanium electrode because of the formation of lithium carbide from the reaction between lithium and carbon. - Highlights: ► Carbon films are prepared on oxide-scale-coated titanium in a LiCl–KCl–K 2 CO 3 melt. ► The films comprise micron-size ‘quasi-spherical’ carbon particles. ► The films present particle-size-gradient. ► The particles contain graphitized and amorphous phases. ► The prepared carbon films are more electrochemically active than graphite.

  13. Covalently coupled hybrid of graphitic carbon nitride with reduced graphene oxide as a superior performance lithium-ion battery anode

    Science.gov (United States)

    Fu, Yongsheng; Zhu, Junwu; Hu, Chong; Wu, Xiaodong; Wang, Xin

    2014-10-01

    An in situ chemical synthetic approach has been designed for the fabrication of a covalently coupled hybrid consisting of graphitic carbon nitride (g-C3N4) with reduced graphene oxide (rGO) with differing g-C3N4/rGO ratio. The epoxy groups of graphene oxide (GO) undergo a nucleophilic substitution reaction with dicyandiamide (C2H4N4) to form the C2H4N4-GO composite via a covalent C-N bond, and then both the in situ polymerization of C2H4N4 and the thermal reduction of GO can be achieved at higher temperatures, forming the covalently coupled g-C3N4-rGO. FT-IR, CP-MAS NMR and XPS analyses, clearly revealed a covalent interaction between the g-C3N4 and rGO sheets. The g-C3N4-rGO exhibits an unprecedented high, stable and reversible capacity of 1525 mA h g-1 at a current density of 100 mA g-1 after 50 cycles. Even at a large current density of 1000 mA g-1, a reversible capacity of 943 mA h g-1 can still be retained. The superior electrochemical performance of g-C3N4-rGO is attributed to the specific characteristics of the unique nanostructure of g-C3N4-rGO and the concerted effects of g-C3N4 and rGO, including covalent interactions between the two moieties, the good conductivity and high special surface area of the nanocomposite, as well as the template effect of the planar amino group of g-C3N4 for the dispersed decoration of Li+ ions.An in situ chemical synthetic approach has been designed for the fabrication of a covalently coupled hybrid consisting of graphitic carbon nitride (g-C3N4) with reduced graphene oxide (rGO) with differing g-C3N4/rGO ratio. The epoxy groups of graphene oxide (GO) undergo a nucleophilic substitution reaction with dicyandiamide (C2H4N4) to form the C2H4N4-GO composite via a covalent C-N bond, and then both the in situ polymerization of C2H4N4 and the thermal reduction of GO can be achieved at higher temperatures, forming the covalently coupled g-C3N4-rGO. FT-IR, CP-MAS NMR and XPS analyses, clearly revealed a covalent interaction between

  14. Performance Study of Graphite Anode Slurry in Lithium-ion Flow Battery by Ball Milling

    Directory of Open Access Journals (Sweden)

    FENG Cai-mei

    2018-02-01

    Full Text Available Graphite anode slurry of lithium-ion flow battery was prepared by the method of ball milling. The morphology, conductivity, specific capacity and cycle performance of graphite anode slurry were studied. Results show that the addition of conductive carbon material can improve the suspension stability of the electrode slurry; the ball milling process can not only improve the suspension stability but also reduce the resistivity of the mixed powders of graphite and conductive carbon materials, the ball milling effect is satisfactory when the mass ratio of the balls and the solid particles is 5:1, but too high ratio of the milling ball and the solid materials can destroy the layer structure of the graphite and affect the stability of the slurry. Increasing the fraction of the graphite and conductive carbon materials can form stable electrical network structure in the slurry and improve the reversible capacity; at the premise of keeping the flowability of the electrode slurry, the reversible specific capacity can be more than 40mAh/g. The capacity loss of graphite anode slurry mainly occurs in the first charging-discharging process, as the increase of the cycles, the capacity loss rate decreases, the capacity goes stable after 5 cycles.

  15. The Impact of Alkaliphilic Biofilm Formation on the Release and Retention of Carbon Isotopes from Nuclear Reactor Graphite.

    Science.gov (United States)

    Rout, S P; Payne, L; Walker, S; Scott, T; Heard, P; Eccles, H; Bond, G; Shah, P; Bills, P; Jackson, B R; Boxall, S A; Laws, A P; Charles, C; Williams, S J; Humphreys, P N

    2018-03-13

    14 C is an important consideration within safety assessments for proposed geological disposal facilities for radioactive wastes, since it is capable of re-entering the biosphere through the generation of 14 C bearing gases. The irradiation of graphite moderators in the UK gas-cooled nuclear power stations has led to the generation of a significant volume of 14 C-containing intermediate level wastes. Some of this 14 C is present as a carbonaceous deposit on channel wall surfaces. Within this study, the potential of biofilm growth upon irradiated and 13 C doped graphite at alkaline pH was investigated. Complex biofilms were established on both active and simulant samples. High throughput sequencing showed the biofilms to be dominated by Alcaligenes sp at pH 9.5 and Dietzia sp at pH 11.0. Surface characterisation revealed that the biofilms were limited to growth upon the graphite surface with no penetration of the deeper porosity. Biofilm formation resulted in the generation of a low porosity surface layer without the removal or modification of the surface deposits or the release of the associated 14 C/ 13 C. Our results indicated that biofilm formation upon irradiated graphite is likely to occur at the pH values studied, without any additional release of the associated 14 C.

  16. Vinylene carbonate and tris(trimethylsilyl) phosphite hybrid additives to improve the electrochemical performance of spinel lithium manganese oxide/graphite cells at 60 °C

    International Nuclear Information System (INIS)

    Koo, Bonjae; Lee, Jeongmin; Lee, Yongwon; Kim, Jun Ki; Choi, Nam-Soon

    2015-01-01

    Highlights: •The combination of tris(trimethylsilyl) phosphite and vinylene carbonate improves the electrochemical performance of lithium manganese oxide/graphite cells at 60 °C. •Removal of hydrogen fluoride and water by tris(trimethylsilyl) phosphite suppresses manganese dissolution from lithium manganese oxide. -- Abstract: The organophosphorus compounds tris(trimethylsilyl) phosphite (TMSP) and vinylene carbonate (VC) have been considered for use as functional additives to improve the electrochemical performance of Li 1.1 Mn 1.86 Mg 0.04 O 4 (LMO)/graphite full cells. Our investigation reveals that the combination of VC and TMSP as additives enhances the cycling properties and storage performance of full cells at 60 °C. The unique functions of the TMSP additive in the VC electrolyte are investigated via ex situ X-ray photoelectron spectroscopy (XPS) and 19 F nuclear magnetic resonance (NMR) measurements. The TMSP additive effectively eliminates trace water and hydrogen fluoride (HF) and produces a protective film on the LMO cathode that alleviates manganese dissolution at 60 °C

  17. Microwave-assisted preparation of carbon nanofiber-functionalized graphite felts as electrodes for polymer-based redox-flow batteries

    Science.gov (United States)

    Schwenke, A. M.; Janoschka, T.; Stolze, C.; Martin, N.; Hoeppener, S.; Schubert, U. S.

    2016-12-01

    A simple and fast microwave-assisted protocol to functionalize commercially available graphite felts (GFs) with carbon nanofibers (CNFs) for the application as electrode materials in redox-flow batteries (RFB) is demonstrated. As catalyst for the CNF synthesis nickel acetate is applied and ethanol serves as the carbon source. By the in-situ growth of CNFs, the active surface of the electrodes is increased by a factor of 50, which is determined by the electrochemical double layer capacities of the obtained materials. Furthermore, the morphology of the CNF-coating is investigated by scanning electron microscopy. Subsequently, the functionalized electrodes are applied in a polymer-based redox-flow battery (pRFB) using a TEMPO- and a viologen polymer as active materials. Due to the increased surface area as compared to an untreated graphite felt electrode, the current rating is improved by about 45% at 80 mA cm-2 and, furthermore, a decrease in overpotentials is observed. Thus, using this microwave-assisted synthesis approach, CNF-functionalized composite electrodes are prepared with a very simple protocol suitable for real life applications and an improvement of the overall performance of the polymer-based redox-flow battery is demonstrated.

  18. The influence of transport phenomena on the fluidized bed combustion of a single carbon particle

    NARCIS (Netherlands)

    Prins, W.; van Swaaij, Willibrordus Petrus Maria

    1990-01-01

    The burning rate and temperature of the carbon particles are known to affect the efficiency of a fluidized bed combustor, and also the emission levels of undesired noxious components. The main results of an extensive study on the fluidized bed combustion behaviour of a single carbon particle [1] are

  19. Research on the phenomenon of graphitization. Crystallographic study - Study of bromine sorption

    International Nuclear Information System (INIS)

    Maire, Jacques

    1967-01-01

    This research thesis reports the study of the mechanism of graphitization of carbon by using X-ray diffraction analysis and the physical and chemical study of lamellar reactions between carbon and bromine. The author first presents generalities and results of preliminary studies (meaning of graphitization, presentation of the various carbon groups and classes), and then reports the study of the graphitization of compact carbons (soft carbons). More precisely, he reports the crystallographic study of partially graphitized carbons: methods and principles, experimental results and their analysis, discussion of the graphitization mechanism. In the next part, the author reports the study of bromine sorption on carbons: experimental method, isotherms of a natural graphite and of a graphitized carbon, structure of carbon-bromine complexes, isotherms of graphitizable carbons and of all other carbons, distribution of bromine layers in partially graphitized carbons, bromine sorption and Fermi level

  20. One new route to optimize the oxidation resistance of TiC/hastelloy (Ni-based alloy) composites applied for intermediate temperature solid oxide fuel cell interconnect by increasing graphite particle size

    Science.gov (United States)

    Qi, Qian; Liu, Yan; Wang, Lujie; Zhang, Hui; Huang, Jian; Huang, Zhengren

    2017-09-01

    TiC/hastelloy composites with suitable thermal expansion and excellent electrical conductivity are promising candidates for IT-SOFC interconnect. In this paper, the TiC/hastelloy composites are fabricated by in-situ reactive infiltration, and the oxidation resistance of composites is optimized by increasing graphite particle size. Results show that the increase of graphite particles size from 1 μm to 40 μm reduces TiC particle size from 2.68 μm to 2.22 μm by affecting the formation process of TiC. Moreover, the decrease of TiC particles size accelerates the fast formation of dense and continuous TiO2/Cr2O3 oxide layer, which bring down the mass gain (800 °C/100 h) from 2.03 mg cm-2 to 1.18 mg cm-2. Meanwhile, the coefficient of thermal expansion decreases from 11.15 × 10-6 °C-1 to 10.80 × 10-6 °C-1, and electrical conductivity maintains about 5800 S cm-1 at 800 °C. Therefore, the decrease of graphite particle size is one simple and effective route to optimize the oxidation resistance of composites, and meantime keeps suitable thermal expansion and good electrical conductivity.

  1. Synthesis of graphitized carbon, nanodiamond and graphene supported Li{sub 4}Ti{sub 5}O{sub 12} and comparison of their electrochemical performance as anodes for lithium ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Shuai; Miao, Juan, E-mail: miaojuan@hpu.edu.cn; Wang, Qiufen, E-mail: grp2009wqf@163.com; Lu, Mengwei; Sun, Jiufang; Wen, Tao

    2016-12-15

    Highlights: • We synthesized graphitized carbon, nanodiamond and graphene supported Li{sub 4}Ti{sub 5}O{sub 12}, respectively. • The order of the capacities is LTO/GE > LTO/GC > LTO > LTO/ND after 500 cycles. • The rate capabilities and cycling stabilities are in the order of LTO/GE > LTO/ND > LTO/GC > LTO. - Abstract: Graphitized carbon (GC), nanodiamond (ND) and graphene (GE) supported Li{sub 4}Ti{sub 5}O{sub 12} (LTO) composites have been synthesized via a solid-state reaction, respectively. The particle sizes of LTO/GC, LTO/ND and LTO/GE are smaller than pure LTO. When tested as the anode for lithium ion batteries, the discharge capacities of LTO, LTO/GC, LTO/ND and LTO/GE composites are 100.1 mAh g{sup −1}, 150.4 mAh g{sup −1}, 90.4 mAh g{sup −1} and 218.3 mAh g{sup −1} at the current density of 175 mA g{sup −1} after 500 cycles. Their rate capacities retain 59.8%, 80.0%, 81.0% and 85.7% at the current density of 175 mA g{sup −1}, 438 mA g{sup −1}, 875 mA g{sup −1} and 175 mA g{sup −1}, respectively. Moreover, the recovery rates of their rate capacities are 78.6%, 83.4%, 88.9% and 90.1% when returned to the current density of 175 mA g{sup −1}, respectively. The reasons can be attributed to the synergistic effect between GC (ND and GE) and LTO as well as the features of the different carbon supports. This strategy, with the carbon constituting a good supporting structure, is an effective way to improve the cycling performance of anode materials for lithium ion batteries.

  2. Curling and closure of graphitic networks under electron-beam irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Ugarte, D [Ecole Polytechnique Federale, Lausanne (Switzerland)

    1992-10-22

    The discovery of buckminsterfullerene (C[sub 60]) and its production in macroscopic quantities has stimulated a great deal of research. More recently, attention has turned towards other curved graphitic networks, such as the giant fullerenes (C[sub n], n > 100) and carbon nanotubes. A general mechanism has been proposed in which the graphitic sheets bend in an attempt to eliminate the highly energetic dangling bonds present at the edge of the growing structure. Here, I report the response of carbon soot particles and tubular graphitic structures to intense electron-beam irradiation in a high-resolution electron microscope; such conditions resemble a high-temperature regime, permitting a degree of structural fluidity. With increased irradiation, there is a gradual reorganization of the initial material into quasi-spherical particles composed of concentric graphitic shells. This lends weight to the nucleation scheme proposed for fullerenes, and moreover, suggests that planar graphite may not be the most stable allotrope of carbon in systems of limited size. (Author).

  3. Hybrid-Particle-In-Cell Simulation of Backsputtered Carbon Transport in the Near-Field Plume of a Hall Thruster

    Science.gov (United States)

    Choi, Maria; Yim, John T.; Williams, George J.; Herman, Daniel A.; Gilland, James H.

    2018-01-01

    Magnetic shielding has eliminated boron nitride erosion as the life limiting mechanism in a Hall thruster but has resulted in erosion of the front magnetic field pole pieces. Recent experiments show that the erosion of graphite pole covers, which are added to protect the magnetic field pole pieces, causes carbon to redeposit on other surfaces, such as boron nitride discharge channel and cathode keeper surfaces. As a part of the risk-reduction activities for Advanced Electric Propulsion System thruster development, this study models transport of backsputtered carbon from the graphite front pole covers and vacuum facility walls. Fluxes, energy distributions, and redeposition rates of backsputtered carbon on the anode, discharge channel, and graphite cathode keeper surfaces are predicted.

  4. Structural analysis of polycrystalline (graphitized) materials

    International Nuclear Information System (INIS)

    Efremenko, M.M.; Kravchik, A.E.; Osmakov, A.S.

    1993-01-01

    Specific features of the structure of polycrystal carbon materials (CM), characterized by high enough degree of structural perfection and different genesis are analyzed. From the viewpoint of fine and supercrystallite structure analysis of the most characteristic groups of graphitized CM: artificial graphites, and natural graphites, as well, has been carried out. It is ascertained that in paracrystal CM a monolayer of hexagonally-bound carbon atoms is the basic element of the structure, and in graphitized CM - a microlayer. The importance of the evaluation of the degree of three-dimensional ordering of the microlayer is shown

  5. Single particle inclusive spectra resulting from the collision of relativistic protons, deuterons, alpha particles, and carbon ions with nuclei

    International Nuclear Information System (INIS)

    Papp, J.

    1975-05-01

    The yields of positive and negative particles resulting from the collision of 1.05 GeV/nucleon and 2.1 GeV/nucleon protons, deuterons, alpha particles, and 1.05 GeV/nucleon carbon nuclei with various targets have been measured. Single particle inclusive cross sections for production of π + , π - , p, d, 3 H, 3 He, and 4 He at 2.5 0 (lab) were obtained. How the results bear on the concepts of limiting fragmentation and scaling, the structure of the alpha particle and deuteron, and the possibility of ''coherent'' production of pions by heavy ions are discussed. (U.S.)

  6. Coordinated Isotopic and TEM Studies of Presolar Graphites from Murchison

    Science.gov (United States)

    Croat, T. K.; Stadermann, F. J.; Zinner, E.; Bernatowicz, T. J.

    2004-03-01

    TEM and NanoSIMS investigations of the same presolar Murchison KFC graphites revealed high Zr, Mo, and Ru content in refractory carbides within the graphites. Along with isotopically light carbon, these suggest a low-metallicity AGB source.

  7. Influence of adhesion to activated carbon particles on the viability of waterborne pathogenic bacteria under flow

    NARCIS (Netherlands)

    van der Mei, Henny C.; Atema-Smit, Jelly; Jager, Debbie; Langworthy, Don E.; Collias, Dimitris I.; Mitchell, Michael D.; Busscher, Henk J.

    2008-01-01

    In rural areas around the world, people often rely on water filtration plants using activated carbon particles for safe water supply. Depending on the carbon surface, adhering microorganisms die or grow to form a biofilm. Assays to assess the efficacy of activated carbons in bacterial removal do not

  8. Effect of the Heat Treatment on the Graphite Matrix of Fuel Element for HTGR

    International Nuclear Information System (INIS)

    Lee, Chungyong; Lee, Seungjae; Suh, Jungmin; Jo, Youngho; Lee, Youngwoo; Cho, Moonsung

    2013-01-01

    In this paper, the cylinder-formed fuel element for the block type reactor is focused on, which consists of the large part of graphite matrix. One of the most important properties of the graphite matrix is the mechanical strength for the high reliability because the graphite matrix should be enabled to protect the TRISO particles from the irradiation environment and the impact from the outside. In this study, the three kinds of candidate graphites and Phenol as a binder were chosen and mixed with each other, formed and heated for the compressive strength test. The objective of this research is to optimize the kinds and composition of the mixed graphite and the forming process by evaluating the compressive strength before/after heat treatment (carbonization of binder). In this study, the effect of heat treatment on graphite matrix was studied in terms of the density and the compressive strength. The size (diameter and length) of pellet is increased by heat treatment. Due to additional weight reduction and swelling (length and diameter) of samples the density of graphite pellet is decreased from about 2.0 to about 1.7g/cm 3 . From the mechanical test results, the compressive strength of graphite pellets was related to the various conditions such as the contents of binder, the kinds of graphite and the heat treatment. Both the green pellet and the heat treated pellet, the compressive strength of G+S+P pellets is relatively higher than that of R+S+P pellets. To optimize fuel element matrix, the effect of Phenol and other binders, graphite composition and the heat treatment on the mechanical properties will be deeply investigated for further study

  9. Associations between fine particle, coarse particle, black carbon and hospital visits in a Chinese city.

    Science.gov (United States)

    Wang, Xi; Chen, Renjie; Meng, Xia; Geng, Fuhai; Wang, Cuicui; Kan, Haidong

    2013-08-01

    China is one of the countries with the highest ambient particle levels in the world; however, there have been no epidemiologic studies examining the effects of fine particle (PM2.5), coarse particle (PM10-2.5) and black carbon (BC) simultaneously on morbidity outcomes. In this study, we conducted a time-series analysis to evaluate the acute effects of PM2.5, PM10-2.5, and BC on daily hospital visits in Shanghai, China. During our study period, the mean daily concentrations of PM2.5, PM10-2.5 and BC were 53.9 μg/m(3), 38.4 μg/m(3) and 3.9 μg/m(3), respectively. We found significant associations of PM2.5, PM 10-2.5, and BC with daily hospital visits. An inter-quartile range increase of the average concentrations of the current and previous days in PM2.5, PM10-2.5 and BC was associated with a 1.88% (95% CI: 0.69% to 3.06%), a 1.30% (95% CI: 0.25% to 2.34%) and a 1.33% (95% CI: 0.34% to 2.32%) increase in emergency-room visits, respectively. For outpatient visits, the corresponding estimated changes were -2.44% (95% CI: -6.62% to 1.74%), 1.09% (95% CI: -2.72% to 4.90%) and 3.34% (95% CI: 0.10% to 6.57%) respectively. The effects of BC were more robust than the effects of PM2.5 and PM10-2.5 in two-pollutant models. To our knowledge, this is the first study in China, or even in Asian developing countries, to report the effect of PM2.5, PM10-2.5, and BC simultaneously on morbidity. Our findings also suggest that BC could serve as a valuable air quality indicator that reflects the health risks of airborne particles. Copyright © 2013 Elsevier B.V. All rights reserved.

  10. Nitrogen-doped graphitic hierarchically porous carbon nanofibers obtained via bimetallic-coordination organic framework modification and their application in supercapacitors.

    Science.gov (United States)

    Yao, Yuechao; Liu, Peng; Li, Xiaoyan; Zeng, Shaozhong; Lan, Tongbin; Huang, Haitao; Zeng, Xierong; Zou, Jizhao

    2018-05-17

    Herein, N-doped graphitic hierarchically porous carbon nanofibers (NGHPCF) were prepared by electrospinning the composite of bimetallic-coordination metal-organic frameworks and polyacrylonitrile, followed by a pyrolysis and acid wash process. Control over the N content, specific surface area, and degree of graphitization of NGHPCF materials has been realized by adjusting the Co/Zn metal coordination content as well as the pyrolysis temperature. The obtained NGHPCF with a high specific surface area (623 m2 g-1) and nitrogen content (13.83 wt%) exhibit a high capacitance of 326 F g-1 at 0.5 A g-1. In addition, the capacitance of 170 F g-1 is still maintained at a high current density (40 A g-1); this indicates a high capacitance retention capability. Furthermore, a superb energy density (9.61 W h kg-1) is obtained with a high power density (62.4 W kg-1) using an organic electrolyte. These results fully illustrate that the prepared NGHPCF binder-free electrodes are promising candidates for high-performance supercapacitors.

  11. Comparison of mechanical and friction properties of composite materials based on AlMg2 containing nano-dimensional particles of crystalline graphite and nanofibers of gamma oxide of aluminum

    Science.gov (United States)

    Aborkin, A. V.; Babin, D. M.; Soboĺkov, A. V.

    2018-04-01

    The method of mechanical synthesis in a planetary ball mill was used for production of composite powders based on the AlMg2 alloy containing 1 wt. % of nanosized particles of crystalline graphite or γ-Al2O3. The resulting powders are consolidated by the sintering under pressure. Using the methods of X-ray diffraction analysis, scanning and transmission electron microscopy, the structural-phase composition of bulk composite materials was studied. Comparative analysis of the microhardness, the conditional yield stress at compression, and the friction coefficient of bulk composite materials is carried out. It has been found out that the mechanical properties of composites reinforced with γ-Al2O3 nanofibers are higher than when reinforcing with nanoscale particles of crystalline graphite.

  12. Characterization of radiation damage induced by swift heavy ions in graphite

    Energy Technology Data Exchange (ETDEWEB)

    Hubert, Christian

    2016-05-15

    Graphite is a classical material in neutron radiation environments, being widely used in nuclear reactors and power plants as a moderator. For high energy particle accelerators, graphite provides ideal material properties because of the low Z of carbon and its corresponding low stopping power, thus when ion projectiles interact with graphite is the energy deposition rather low. This work aims to improve the understanding of how the irradiation with swift heavy ions (SHI) of kinetic energies in the range of MeV to GeV affects the structure of graphite and other carbon-based materials. Special focus of this project is given to beam induced changes of thermo-mechanical properties. For this purpose the Highly oriented pyrolytic graphite (HOPG) and glassy carbon (GC) (both serving as model materials), isotropic high density polycrystalline graphite (PG) and other carbon based materials like carbon fiber carbon composites (CFC), chemically expanded graphite (FG) and molybdenum carbide enhanced graphite composites (MoC) were exposed to different ions ranging from {sup 131}Xe to {sup 238}U provided by the UNILAC accelerator at GSI in Darmstadt, Germany. To investigate structural changes, various in-situ and off-line measurements were performed including Raman spectroscopy, x-ray diffraction and x-ray photo-electron spectroscopy. Thermo-mechanical properties were investigated using the laser-flash-analysis method, differential scanning calorimetry, micro/nano-indentation and 4-point electrical resistivity measurements. Beam induced stresses were investigated using profilometry. Obtained results provided clear evidence that ion beam-induced radiation damage leads to structural changes and degradation of thermal, mechanical and electrical properties of graphite. PG transforms towards a disordered sp2 structure, comparable to GC at high fluences. Irradiation-induced embrittlement is strongly reducing the lifetime of most high-dose exposed accelerator components. For

  13. Nanodiamond graphitization: a magnetic resonance study

    International Nuclear Information System (INIS)

    Panich, A M; Shames, A I; Sergeev, N A; Olszewski, M; McDonough, J K; Mochalin, V N; Gogotsi, Y

    2013-01-01

    We report on the first nuclear magnetic resonance (NMR) and electron paramagnetic resonance (EPR) study of the high-temperature nanodiamond-to-onion transformation. 1 H, 13 C NMR and EPR spectra of the initial nanodiamond samples and those annealed at 600, 700, 800 and 1800 ° C were measured. For the samples annealed at 600 to 800 ° C, our NMR data reveal the early stages of the surface modification, as well as a progressive increase in sp 2 carbon content with increased annealing temperature. Such quantitative experimental data were recorded for the first time. These findings correlate with EPR data on the sensitivity of the dangling bond EPR line width to air content, progressing with rising annealing temperature, that evidences consequent graphitization of the external layers of the diamond core. The sample annealed at 1800 ° C shows complete conversion of nanodiamond particles into carbon onions. (paper)

  14. Thermal conductivity of partially graphitized biocarbon obtained by carbonization of medium-density fiberboard in the presence of a Ni-based catalyst

    Science.gov (United States)

    Orlova, T. S.; Parfen'eva, L. S.; Smirnov, B. I.; Gutierrez-Pardo, A.; Ramirez-Rico, J.

    2016-01-01

    The thermal conductivity k and resistivity ρ of biocarbon matrices, prepared by carbonizing medium-density fiberboard at T carb = 850 and 1500°C in the presence of a Ni-based catalyst (samples MDF-C( Ni)) and without a catalyst (samples MDF-C), have been measured for the first time in the temperature range of 5-300 K. X-ray diffraction analysis has revealed that the bulk graphite phase arises only at T carb = 1500°C. It has been shown that the temperature dependences of the thermal conductivity of samples MDFC- 850 and MDF-C-850(Ni) in the range of 80-300 K are to each other and follow the law of k( T) ˜ T 1.65, but the use of the Ni-catalyst leads to an increase in the thermal conductivity by a factor of approximately 1.5, due to the formation of a greater fraction of the nanocrystalline phase in the presence of the Ni-catalyst at T carb = 850°C. In biocarbon MDF-C-1500 prepared without a catalyst, the dependence is k( T) ˜ T 1.65, and it is controlled by the nanocrystalline phase. In MDF-C-1500(Ni), the bulk graphite phase formed increases the thermal conductivity by a factor of 1.5-2 compared to the thermal conductivity of MDF-C-1500 in the entire temperature range of 5-300 K; k( T = 300 K) reaches the values of ˜10 W m-1 K-1, characteristic of biocarbon obtained without a catalyst only at high temperatures of T carb = 2400°C. It has been shown that MDF-C-1500(Ni) in the temperature range of 40‒300 K is characterized by the dependence, k( T) ˜ T 1.3, which can be described in terms of the model of partially graphitized biocarbon as a composite of an amorphous matrix with spherical inclusions of the graphite phase.

  15. Particles of spilled oil-absorbing carbon in contact with water

    Science.gov (United States)

    Muradov, Nazim [Melbourne, FL

    2011-03-29

    Hydrogen generator coupled to or integrated with a fuel cell for portable power applications. Hydrogen is produced via thermocatalytic decomposition (cracking, pyrolysis) of hydrocarbon fuels in oxidant-free environment. The apparatus can utilize a variety of hydrocarbon fuels, including natural gas, propane, gasoline, kerosene, diesel fuel, crude oil (including sulfurous fuels). The hydrogen-rich gas produced is free of carbon oxides or other reactive impurities, so it could be directly fed to any type of a fuel cell. The catalysts for hydrogen production in the apparatus are carbon-based or metal-based materials and doped, if necessary, with a sulfur-capturing agent. Additionally disclosed are two novel processes for the production of two types of carbon filaments, and a novel filamentous carbon product. Carbon particles with surface filaments having a hydrophobic property of oil film absorption, compositions of matter containing those particles, and a system for using the carbon particles for cleaning oil spills.

  16. Molecular Characterization of Brown Carbon in Biomass Burning Aerosol Particles

    Energy Technology Data Exchange (ETDEWEB)

    Lin, Peng; Aiona, Paige K.; Li, Ying; Shiraiwa, Manabu; Laskin, Julia; Nizkorodov, Sergey A.; Laskin, Alexander

    2016-11-01

    Emissions from biomass burning are a significant source of brown carbon (BrC) in the atmosphere. In this study, we investigate the molecular composition of freshly-emitted biomass burning organic aerosol (BBOA) samples collected during test burns of selected biomass fuels: sawgrass, peat, ponderosa pine, and black spruce. We characterize individual BrC chromophores present in these samples using high performance liquid chromatography coupled to a photodiode array detector and a high-resolution mass spectrometer. We demonstrate that both the overall BrC absorption and the chemical composition of light-absorbing compounds depend significantly on the type of biomass fuels and burning conditions. Common BrC chromophores in the selected BBOA samples include nitro-aromatics, polycyclic aromatic hydrocarbon derivatives, and polyphenols spanning a wide range of molecular weights, structures, and light absorption properties. A number of biofuel-specific BrC chromophores are observed, indicating that some of them may be used as potential markers of BrC originating from different biomass burning sources. On average, ~50% of the light absorption above 300 nm can be attributed to a limited number of strong BrC chromophores, which may serve as representative light-absorbing species for studying atmospheric processing of BrC aerosol. The absorption coefficients of BBOA are affected by solar photolysis. Specifically, under typical atmospheric conditions, the 300 nm absorbance decays with a half-life of 16 hours. A “molecular corridors” analysis of the BBOA volatility distribution suggests that many BrC compounds in the fresh BBOA have low volatility (<1 g m-1) and will be retained in the particle phase under atmospherically relevant conditions.

  17. Carbon isotope ratios of organic matter in Bering Sea settling particles. Extremely high remineralization of organic carbon derived from diatoms

    International Nuclear Information System (INIS)

    Yasuda, Saki; Akagi, Tasuku; Naraoka, Hiroshi; Kitajima, Fumio; Takahashi, Kozo

    2016-01-01

    The carbon isotope ratios of organic carbon in settling particles collected in the highly-diatom-productive Bering Sea were determined. Wet decomposition was employed to oxidize relatively fresh organic matter. The amount of unoxidised organic carbon in the residue following wet decomposition was negligible. The δ 13 C of organic carbon in the settling particles showed a clear relationship against SiO 2 /CaCO 3 ratio of settling particles: approximately -26‰ and -19‰ at lower and higher SiO 2 /CaCO 3 ratios, respectively. The δ 13 C values were largely interpreted in terms of mixing of two major plankton sources. Both δ 13 C and compositional data can be explained consistently only by assuming that more than 98% of diatomaceous organic matter decays and that organic matter derived from carbonate-shelled plankton may remain much less remineralized. A greater amount of diatom-derived organic matter is discovered to be trapped with the increase of SiO 2 /CaCO 3 ratio of the settling particles. The ratio of organic carbon to inorganic carbon, known as the rain ratio, therefore, tends to increase proportionally with the SiO 2 /CaCO 3 ratio under an extremely diatom-productive condition. (author)

  18. Unique Fe2P Nanoparticles Enveloped in Sandwichlike Graphited Carbon Sheets as Excellent Hydrogen Evolution Reaction Catalyst and Lithium-Ion Battery Anode.

    Science.gov (United States)

    Zhang, Yan; Zhang, Huijuan; Feng, Yangyang; Liu, Li; Wang, Yu

    2015-12-09

    The novel Fe2P nanoparticles encapsulated in sandwichlike graphited carbon envelope nanocomposite (Fe2P/GCS) that can be first applied in hydrogen evolution reaction (HER) as well as lithium-ion batteries (LIBs) has been designed and fabricated. The unique sandwiched Fe2P/GCS is characterized with several prominent merits, including large specific surface area, nanoporous structure, excellent electronic conductivity, enhanced structural integrity and so on. All of these endow the Fe2P/GCS with brilliant electrochemical performance. When used as a HER electrocatalyst in acidic media, the harvested Fe2P/GCS demonstrates low onset overpotential and Tafel slope as well as particularly outstanding durability. Moreover, as an anode material for LIBs, the sandwiched Fe2P/GCS presents high specific capacity and excellent cyclability and rate capability. As a consequence, the acquired Fe2P/GCS is a promising material for energy applications, especially HER and LIBs.

  19. Morphology and Optical Properties of Black-Carbon Particles Relevant to Engine Emissions

    Science.gov (United States)

    Michelsen, H. A.; Bambha, R.; Dansson, M. A.; Schrader, P. E.

    2013-12-01

    Black-carbon particles are believed to have a large influence on climate through direct radiative forcing, reduction of surface albedo of snow and ice in the cryosphere, and interaction with clouds. The optical properties and morphology of atmospheric particles containing black carbon are uncertain, and characterization of black carbon resulting from engines emissions is needed. Refractory black-carbon particles found in the atmosphere are often coated with unburned fuel, sulfuric acid, water, ash, and other combustion by-products and atmospheric constituents. Coatings can alter the optical and physical properties of the particles and therefore change their optical properties and cloud interactions. Details of particle morphology and coating state can also have important effects on the interpretation of optical diagnostics. A more complete understanding of how coatings affect extinction, absorption, and incandescence measurements is needed before these techniques can be applied reliably to a wide range of particles. We have investigated the effects of coatings on the optical and physical properties of combustion-generated black-carbon particles using a range of standard particle diagnostics, extinction, and time-resolved laser-induced incandescence (LII) measurements. Particles were generated in a co-flow diffusion flame, extracted, cooled, and coated with oleic acid. The diffusion flame produces highly dendritic soot aggregates with similar properties to those produced in diesel engines, diffusion flames, and most natural combustion processes. A thermodenuder was used to remove the coating. A scanning mobility particle sizer (SMPS) was used to monitor aggregate sizes; a centrifugal particle mass analyzer (CPMA) was used to measure coating mass fractions, and transmission electron microscopy (TEM) was used to characterize particle morphologies. The results demonstrate important differences in optical measurements between coated and uncoated particles.

  20. Cyclic fatigue-crack propagation, stress-corrosion, and fracture-toughness behavior in pyrolytic carbon-coated graphite for prosthetic heart valve applications.

    Science.gov (United States)

    Ritchie, R O; Dauskardt, R H; Yu, W K; Brendzel, A M

    1990-02-01

    Fracture-mechanics tests were performed to characterize the cyclic fatigue, stress-corrosion cracking, and fracture-toughness behavior of a pyrolytic carbon-coated graphite composite material used in the manufacture of cardiac valve prostheses. Testing was carried out using compact tension C(T) samples containing "atomically" sharp precracks, both in room-temperature air and principally in a simulated physiological environment of 37 degrees C Ringer's lactate solution. Under sustained (monotonic) loads, the composite exhibited resistance-curve behavior, with a fracture toughness (KIc) between 1.1 and 1.9 MPa square root of m, and subcritical stress-corrosion crack velocities (da/dt) which were a function of the stress intensity K raised to the 74th power (over the range approximately 10(-9) to over 10(-5) m/s). More importantly, contrary to common perception, under cyclic loading conditions the composite was found to display true (cyclic) fatigue failure in both environments; fatigue-crack growth rates (da/dN) were seen to be a function of the 19th power of the stress-intensity range delta K (over the range approximately 10(-11) to over 10(-8) m/cycle). As subcritical crack velocities under cyclic loading were found to be many orders of magnitude faster than those measured under equivalent monotonic loads and to occur at typically 45% lower stress-intensity levels, cyclic fatigue in pyrolytic carbon-coated graphite is reasoned to be a vital consideration in the design and life-prediction procedures of prosthetic devices manufactured from this material.

  1. Degree of functionalization and stability of fluorine groups fixed to carbon nanotubes and graphite nanoplates by CF{sub 4} microwave plasma

    Energy Technology Data Exchange (ETDEWEB)

    Abdelkader-Fernández, V.K.; Morales-Lara, F. [Departamento de Química Inorgánica, Facultad de Ciencias, Universidad de Granada, 18071 Granada (Spain); Melguizo, M.; García-Gallarín, C.; López-Garzón, R.; Godino-Salido, M.L. [Departamento de Química Inorgánica y Orgánica, Facultad de Ciencias Experimentales, Universidad de Jaén, 23071 Jaén (Spain); López-Garzón, F.J., E-mail: flopez@ugr.es [Departamento de Química Inorgánica, Facultad de Ciencias, Universidad de Granada, 18071 Granada (Spain); Domingo-García, M.; Pérez-Mendoza, M.J. [Departamento de Química Inorgánica, Facultad de Ciencias, Universidad de Granada, 18071 Granada (Spain)

    2015-12-01

    Highlights: • The surface area of GNPs and MWCNTs determines the degree of fluorination by plasma. • Fluorine is bound to carbon atoms in up to eight chemical environments. • The stability of the fluorine groups varies in a wide range of temperature. • The electronic properties of MWCNTs are changed as a consequence of fluorination. • The textural characteristics of the materials are not changed after fluorination. - Abstract: The fluorination of graphite nanoplates (GNPs) and multi-wall carbon nanotubes (MWCNTs) by CF{sub 4} cold plasma is reported. The aim is to analyze the influence of the textural characteristics in the degree of fluorination and in the thermal stability of the fluorine groups. We have used thermal programmed desorption which clearly discriminates the nature of the desorbing species and their stability. The degree of fluorination of both materials is similar up to 20 min of treatment and then it decreases in GNPs at longer treatments. Nevertheless, the fluorine content in MWCNTs keeps increasing after 45 min. This different evolution of the fluorination degree with the time is related to the surface areas. The fluorine bonding is produced not only in defects and irregularities but also on the external graphene sheets of both materials, and it results in up to eight different chemical environments having different thermal stabilities from 150 °C up to temperatures higher than 900 °C. The fluorination increases the electronic states near the Fermi level of the nanotubes whereas it does not affect the electronic properties of graphite nanoplates. It is shown that no intercalation compounds are formed and that the textural characteristics of the materials remain unchanged after fluorination.

  2. N/S/B-doped graphitized carbon encased Fe species as a highly active and durable catalyst towards oxygen reduction reaction.

    Science.gov (United States)

    Li, Guang-Lan; Cheng, Guang-Chun; Chen, Wen-Wen; Liu, Cai-Di; Yuan, Li-Fang; Yang, Bei-Bei; Hao, Ce

    2018-03-15

    Exploring cost-effective, high-performance and durable non-precious metal catalysts is of great significance for the acceleration of sluggish oxygen reduction reaction (ORR). Here, we report an intriguing heteroatom-doped graphitized carbon encased Fe species composite by introducing N, S and B sequentially. The experimental approach was designed ingeniously for that the FeCl 3 ·6H 2 O could catalyze thiourea to synthesize N, S co-doped carbon materials which would further react with H 3 BO 3 and NH 3 (emerged at the heat-treatment process) to prepare N, S and B co-doped carbon materials (Fe-N/S/B-C). The Fe-N/S/B-C exhibits an impressive ORR activity for its half-wave potential of -0.1 V, which is 36 mV or 19 mV higher than that of the corresponding single or dual doped counterparts (Fe-N-C or Fe-N/S-C) and 31 mV positive than that of Pt/C catalyst, respectively. Further chronoamperometric measurement and accelerated aging test confirm the excellent electrochemical durability of Fe-N/S/B-C with the stable core-shell structure. The remarkable ORR performance and facile preparation method enable Fe-N/S/B-C as a potential candidate in electrochemical energy devices. Copyright © 2017 Elsevier Inc. All rights reserved.

  3. Self-sensing piezoresistive cement composite loaded with carbon black particles

    KAUST Repository

    Monteiro, André O.; Cachim, Paulo B.; Da Costa, Pedro M. F. J.

    2017-01-01

    Strain sensors can be embedded in civil engineering infrastructures to perform real-time service life monitoring. Here, the sensing capability of piezoresistive cement-based composites loaded with carbon black (CB) particles is investigated. Several

  4. Characterization and observation of water-based nanofluids quench medium with carbon particle content variation

    Science.gov (United States)

    Yahya, S. S.; Harjanto, S.; Putra, W. N.; Ramahdita, G.; Kresnodrianto, Mahiswara, E. P.

    2018-05-01

    Recently, nanofluids have been widely used in heat treatment industries as quench medium with better quenching performance. The thermal conductivity of nanofluids is higher compared to conventional quench medium such as polymer, water, brine, and petroleum-based oil. This characteristic can be achieved by mixing high thermal conductivity particles in nanometer scale with a fluid as base. In this research, carbon powder and distilled water were used as nanoparticles and base respectively. The carbon source used in this research was laboratory grade carbon powder, and activated carbon as a cheaper alternative source. By adjusting the percentage of dispersed carbon particles, thermal conductivity of nanofluids could be controlled as needed. To obtain nanoscale carbon particles, planetary ball mill was used to grind laboratory-grade carbon and active carbon powder to further decrease its particle size. This milling method will provide nanoparticles with lower production cost. Milling speed and duration were set at 500 rpm and 15 hours. Scanning electron microscope (SEM) and Energy Dispersive X-Ray (EDX) were carried out respectively to determine the particle size, material identification, particle morphology. The carbon nanoparticle content in nanofluids quench mediums for this research were varied at 0.1, 0.3, and 0.5 % vol. Furthermore, these mediums were used to quench AISI 1045 carbon steel samples which had been annealed at 1000 °C. Hardness testing and metallography observation were then conducted to check the effect of different quench medium in steel samples. Preliminary characterizations showed that the carbon particle dimension after milling was hundreds of nanometers, or still in sub-micron range. Therefore, the milling process parameters are need to be optimized further. EDX observation in laboratory-grade carbon powder showed that the powder was pure carbon as expected for, but in activated carbon has some impurities. The nanofluid itself, however, was

  5. Preparation and structure of carbon encapsulated copper nanoparticles

    International Nuclear Information System (INIS)

    Hao Chuncheng; Xiao Feng; Cui Zuolin

    2008-01-01

    Carbon-encapsulated copper nanoparticles were synthesized by a modified arc plasma method using methane as carbon source. The particles were characterized in detail by transmission electron microscope, high-resolution transmission electron microscopy, selected-area electron diffraction, X-ray diffraction, thermogravimetric and differential scanning calorimetry. The encapsulated copper nanoparticles were about 30 nm in diameter with 3-5 nm graphitic carbon shells. The outside graphitic carbon layers effectively prevented unwanted oxidation of the copper inside. The effect of the ratio of He/CH 4 on the morphologies and the formation of the carbon shell were investigated

  6. High temperature soldering of graphite

    International Nuclear Information System (INIS)

    Anikin, L.T.; Kravetskij, G.A.; Dergunova, V.S.

    1977-01-01

    The effect is studied of the brazing temperature on the strength of the brazed joint of graphite materials. In one case, iron and nickel are used as solder, and in another, molybdenum. The contact heating of the iron and nickel with the graphite has been studied in the temperature range of 1400-2400 ged C, and molybdenum, 2200-2600 deg C. The quality of the joints has been judged by the tensile strength at temperatures of 2500-2800 deg C and by the microstructure. An investigation into the kinetics of carbon dissolution in molten iron has shown that the failure of the graphite in contact with the iron melt is due to the incorporation of iron atoms in the interbase planes. The strength of a joint formed with the participation of the vapour-gas phase is 2.5 times higher than that of a joint obtained by graphite recrystallization through the carbon-containing metal melt. The critical temperatures are determined of graphite brazing with nickel, iron, and molybdenum interlayers, which sharply increase the strength of the brazed joint as a result of the formation of a vapour-gas phase and deposition of fine-crystal carbon

  7. Study on CO{sub 2} absorption enhancement by adding active carbon particles into MEA solution

    Energy Technology Data Exchange (ETDEWEB)

    Qian, Juan; Sun, Rui; Ma, Lian; Sun, Shaozeng [Harbin Institute of Technology, Harbin (China). School of Energy Science and Engineering

    2013-07-01

    The chemical absorption of CO{sub 2} is generally recognized as the most efficient post-combustion technology of CO{sub 2} separation at present. A study on CO{sub 2} absorption enhancement by adding small particles of active carbon into MEA solution is investigated within a self-designed glass stirring tank. Experiments of different particle loadings and different particle sizes have been conducted. When active carbon particle concentration is fewer, compared to the absorption rate of CO{sub 2} gas absorbed by MEA aqueous solution, the role of active carbon adsorption CO{sub 2} gas is negligible. The enhancement efficiency of CO{sub 2} absorption could be improved by 10% to the upmost in this liquid-particle system.

  8. Stable Carbon Fractionation In Size Segregated Aerosol Particles Produced By Controlled Biomass Burning

    Science.gov (United States)

    Masalaite, Agne; Garbaras, Andrius; Garbariene, Inga; Ceburnis, Darius; Martuzevicius, Dainius; Puida, Egidijus; Kvietkus, Kestutis; Remeikis, Vidmantas

    2014-05-01

    Biomass burning is the largest source of primary fine fraction carbonaceous particles and the second largest source of trace gases in the global atmosphere with a strong effect not only on the regional scale but also in areas distant from the source . Many studies have often assumed no significant carbon isotope fractionation occurring between black