Ion-exchange composite membranes pore-filled with sulfonated poly(ether ether ketone) and Engelhard titanosilicate-10 for improved performance of vanadium redox flow batteries

Science.gov (United States)

Kim, Jihoon; Lee, Yongkyu; Jeon, Jae-Deok; Kwak, Seung-Yeop

2018-04-01

A series of ion-exchange membranes for vanadium redox flow batteries (VRBs) are prepared by filling the pores of a poly(tetrafluoroethylene) (PTFE) substrate with sulfonated poly(ether ether ketone) (SPEEK) and microporous Engelhard titanosilicate-10 (ETS-10). The effects of ETS-10 incorporation and PTFE reinforcement on membrane properties and VRB single-cell performance are investigated using various characterization tools. The results show that these composite membranes exhibit improved mechanical properties and reduced vanadium-ion permeabilities owing to the interactions between ETS-10 and SPEEK, the suppressed swelling of PTFE, and the unique ETS-10 framework. The composite membrane with 3 wt% ETS-10 (referred to as "SE3/P") exhibits the best membrane properties and highest ion selectivity. The VRB system with the SE3/P membrane exhibits higher cell capacity, higher cell efficiency, and lower capacity decay than that with a Nafion membrane. These results indicate that this composite membrane has potential as an alternative to Nafion in VRB systems.

Fuel cell performance of pendent methylphenyl sulfonated poly(ether ether ketone ketone)s

Science.gov (United States)

Zhang, Hanyu; Stanis, Ronald J.; Song, Yang; Hu, Wei; Cornelius, Chris J.; Shi, Qiang; Liu, Baijun; Guiver, Michael D.

2017-11-01

Meta- and para-linked homopolymers bearing 3-methylphenyl (Me) pendent groups were postsulfonated to create sulfonated poly(ether ether ketone ketone) (SPEEKK) backbone isomers, which are referred to as Me-p-SPEEKK and Me-m-SPEEKK. Their thermal and oxidative stability, mechanical properties, dimensional stability, methanol permeability, and proton conductivity are characterized. Me-p-SPEEKK and Me-m-SPEEKK proton conductivities at 100 °C are 116 and 173 mS cm-1, respectively. Their methanol permeabilities are 3.3-3.9 × 10-7 cm2 s-1, and dimensional swelling at 100 °C is 16.4-17.5%. Me-p-SPEEKK and Me-m-SPEEKK were fabricated into membrane electrode assemblies (MEAs), and electrochemical properties were evaluated within a direct methanol fuel cell (DMFC) and proton-exchange membrane fuel cell (PEMFC). When O2 is used as the oxidant at 80 °C and 100% RH, the maximum power density of Me-m-SPEEKK reaches 657 mW cm-2, which is higher than those of Nafion 115 (552 mW cm-2). DMFC performance is 85 mW cm-2 at 80 °C with 2.0 M methanol using Me-p-SPEEKK due to its low MeOH crossover. In general, these electrochemical results are comparable to Nafion. These ionomer properties, combined with a potentially less expensive and scalable polymer manufacturing process, may broaden their potential for many practical applications.

Mass transport of direct methanol fuel cell species in sulfonated poly(ether ether ketone) membranes

International Nuclear Information System (INIS)

Silva, V.S.; Ruffmann, B.; Vetter, S.; Boaventura, M.; Mendes, A.M.; Madeira, L.M.; Nunes, S.P.

2006-01-01

Homogeneous membranes based on sulfonated poly(ether ether ketone) (sPEEK) with different sulfonation degrees (SD) were prepared and characterized. In order to perform a critical analysis of the SD effect on the polymer barrier and mass transport properties towards direct methanol fuel cell species, proton conductivity, water/methanol pervaporation and nitrogen/oxygen/carbon dioxide pressure rise method experiments are proposed. This procedure allows the evaluation of the individual permeability coefficients in hydrated sPEEK membranes with different sulfonation degrees. Nafion[reg] 112 was used as reference material. DMFC tests were also performed at 50 deg. C. It was observed that the proton conductivity and the permeability towards water, methanol, oxygen and carbon dioxide increase with the sPEEK sulfonation degree. In contrast, the SD seems to not affect the nitrogen permeability coefficient. In terms of selectivity, it was observed that the carbon dioxide/oxygen selectivity increases with the sPEEK SD. In contrast, the nitrogen/oxygen selectivity decreases. In terms of barrier properties for preventing the DMFC reactants loss, the polymer electrolyte membrane based on the sulfonated poly(ether ether ketone) with SD lower or equal to 71%, although having slightly lower proton conductivity, presented much better characteristics for fuel cell applications compared with the well known Nafion[reg] 112. In terms of the DMFC tests of the studied membranes at low temperature, the sPEEK membrane with SD = 71% showed to have similar performance, or even better, as that of Nafion[reg] 112. However, the highest DMFC overall efficiency was achieved using sPEEK membrane with SD = 52%

Thermal Stability of Sulfonated Poly(Ether Ether Ketone) Films: on the Role of Protodesulfonation

OpenAIRE

Koziara, Beata; Kappert, Emiel; Ogieglo, Wojciech; Nijmeijer, Dorothea C.; Hempenius, Mark A.; Benes, Nieck Edwin

2016-01-01

Thin film and bulk, sulfonated poly(ether ether ketone) (SPEEK) have been subjected to a thermal treatment at 160–250 °C for up to 15 h. Exposing the films to 160 °C already causes partial desulfonation, and heating to temperatures exceeding 200 °C results in increased conjugation in the material, most likely via a slight cross-linking by H-substitution. It is well-known that the sulfonate proton plays a major role in the desulfonation reactions, and exchanging the protons with other cations ...

Accelerated simulations of aromatic polymers: application to polyether ether ketone (PEEK)

Science.gov (United States)

Broadbent, Richard J.; Spencer, James S.; Mostofi, Arash A.; Sutton, Adrian P.

2014-10-01

For aromatic polymers, the out-of-plane oscillations of aromatic groups limit the maximum accessible time step in a molecular dynamics simulation. We present a systematic approach to removing such high-frequency oscillations from planar groups along aromatic polymer backbones, while preserving the dynamical properties of the system. We consider, as an example, the industrially important polymer, polyether ether ketone (PEEK), and show that this coarse graining technique maintains excellent agreement with the fully flexible all-atom and all-atom rigid bond models whilst allowing the time step to increase fivefold to 5 fs.

Analysis of electron-irradiated poly-ether ether ketone by X-ray photoelectron spectroscopy

International Nuclear Information System (INIS)

Oyabu, Matashige; Kobayashi, Yoshinori; Seguchi, Tadao; Sasuga, Tsuneo; Kudoh, Hisaaki.

1995-01-01

Organic polymers used in atomic power plants or space are damaged by ionizing irradiation. Radicals produced by irradiation cause oxidation, chain scission and crosslinking, all of which lead to degradation of the material. In this paper, the surface of electron-irradiated poly-ether ether ketone (PEEK) was studied by X-ray photoelectron spectroscopy (XPS). The irradiation in air was found to oxidize the PEEK surface producing carboxyl groups, the content of which dependant on the dose. Carboxyl groups were not produced in helium gas. Quantitative spectral analysis indicated that the aromatic structure might be decomposed. Some comparison was made between the semicrystalline and amorphous samples. The oxygen content resulting from irradiation, of semicrystalline PEEK increased more than that of amorphous PEEK. (author)

Nanocomposite Based on Functionalized Gold Nanoparticles and Sulfonated Poly(ether ether ketone Membranes: Synthesis and Characterization

Directory of Open Access Journals (Sweden)

Iole Venditti

2017-03-01

Full Text Available Gold nanoparticles, capped by 3-mercapto propane sulfonate (Au-3MPS, were synthesized inside a swollen sulfonated poly(ether ether ketone membrane (sPEEK. The formation of the Au-3MPS nanoparticles in the swollen sPEEK membrane was observed by spectroscopic and microscopic techniques. The nanocomposite containing the gold nanoparticles grown in the sPEEK membrane, showed the plasmon resonance λmax at about 520 nm, which remained stable over a testing period of three months. The size distribution of the nanoparticles was assessed, and the sPEEK membrane roughness, both before and after the synthesis of nanoparticles, was studied by AFM. The XPS measurements confirm Au-3MPS formation in the sPEEK membrane. Moreover, AFM experiments recorded in fluid allowed the production of images of the Au-3MPS@sPEEK composite in water at different pH levels, achieving a better understanding of the membrane behavior in a water environment; the dynamic hydration process of the Au-3MPS@sPEEK membrane was investigated. These preliminary results suggest that the newly developed nanocomposite membranes could be promising materials for fuel cell applications.

The Influence of Operation Temperature of the Characteristic of Sulfonated Polyether-Ether Ketone Electrolyte Membrane

International Nuclear Information System (INIS)

Sri Handayani; Eniya Listiani Dewi

2008-01-01

Recently, high temperature Direct Methanol Fuel Cell (DMFC) has been receiving great attention, because provide faster reaction kinetic, the enhance electrode kinetics, reduced size and reduce Pt-based catalyst poisoning by CO. But at high temperature, it will decrease the membrane performance i.e. low proton conductivity affected by humidification and high methanol crossover as happening to Nafion-117 membrane (commercial membrane). To solve this problems, sulfonated polyether-ether ketone and composite (silica additive) as electrolyte membrane at high temperature DMFC was tried to use. In this research, sPEEK with sulfonation degree (SD) 47 % and 68 % and addition silica 3 wt % were used as electrolyte membranes. Proton conductivity and methanol permeability of these membranes were measured at various temperatures (25, 50, 90 and 140 C ). Proton conductivity of membranes were measured by standard bridge impedance spectroscopy (LCR-meter, HIOKI 3522-50) and it was found about 0.01-0.04 S/cm. Methanol permeability of membranes were investigated by diffusion cell and gave the result about 10 - 6 - 10 - 7cm 2 /s. The best sPEEK membrane was sPEEK membrane with SD 68 % and the addition of silica 3 wt%, signed by highest selectivity value (ratio proton conductivity to methanol permeability). Therefore, electrolyte membrane based sulfonated polyether-ether ketone (SD 68 %) with silica could be used at high temperature which give promising as solid electrolyte membrane in application high temperature DMFC. (author)

A novel sulfonated poly(ether ether ketone) and cross-linked membranes for fuel cells

Energy Technology Data Exchange (ETDEWEB)

Li, Hongtao; Zhang, Gang; Wu, Jing; Zhao, Chengji; Zhang, Yang; Shao, Ke; Han, Miaomiao; Lin, Haidan; Zhu, Jing; Na, Hui [Alan G MacDiarmid Institute, College of Chemistry, Jilin University, Qianjin Street 2699, Changchun 130012, Jilin (China)

2010-10-01

A novel poly(ether ether ketone) (PEEK) containing pendant carboxyl groups has been synthesized by a nucleophilic polycondensation reaction. Sulfonated polymers (SPEEKs) with different ion exchange capacity are then obtained by post-sulfonation process. The structures of PEEK and SPEEKs are characterized by both FT-IR and {sup 1}H NMR. The properties of SPEEKs as candidates for proton exchange membranes are studied. The cross-linking reaction is performed at 140 C using poly(vinyl alcohol) (PVA) as the cross-linker. In comparison with the non-cross-linked membranes, some properties of the cross-linked membranes are significantly improved, such as water uptake, methanol resistance, mechanical and oxidative stabilities, while the proton conductivity decreases. The effect of PVA content on proton conductivity, water uptake, swelling ratio, and methanol permeability is also investigated. Among all the membranes, SPEEK-C-8 shows the highest selectivity of 50.5 x 10{sup 4} S s cm{sup -3}, which indicates that it is a suitable candidate for applications in direct methanol fuel cells. (author)

Electrochemical investigation of sulfonated poly(ether ether ketone)/clay nanocomposite membranes for moderate temperature fuel cell applications

Energy Technology Data Exchange (ETDEWEB)

Hasani-Sadrabadi, Mohammad Mahdi [Polymer Engineering Department, Amirkabir University of Technology, Tehran (Iran); Biomedical Engineering Department, Amirkabir University of Technology, Tehran (Iran); Dashtimoghadam, Erfan; Sarikhani, Kaveh [Polymer Engineering Department, Amirkabir University of Technology, Tehran (Iran); Majedi, Fatemeh S. [Biomedical Engineering Department, Amirkabir University of Technology, Tehran (Iran); Khanbabaei, Ghader [Polymer Science and Technology Division, Research Institute of Petroleum Industry, Tehran (Iran)

2010-05-01

In the present study, polyelectrolyte membranes based on partially sulfonated poly(ether ether ketone) (sPEEK) with various degrees of sulfonation are prepared. The optimum degree of sulfonation is determined according to the transport properties and hydrolytic stability of the membranes. Subsequently, various amounts of the organically modified montmorillonite (MMT) are introduced into the sPEEK matrices via the solution intercalation technique. The proton conductivity and methanol permeability measurements of the fabricated composite membranes reveal a high proton to methanol selectivity, even at elevated temperatures. Membrane based on sPEEK and 1 wt% of MMT, as the optimum nanoclay composition, exhibits a high selectivity and power density at the concentrated methanol feed. Moreover, it is found that the optimum nanocomposite membrane not only provides higher performance compared to the neat sPEEK and Nafion {sup registered} 117 membranes, but also exhibits a high open circuit voltage (OCV) at the elevated methanol concentration. Owing to the high proton conductivity, reduced methanol permeability, high power density, convenient processability and low cost, sPEEK/MMT nanocomposite membranes could be considered as the alternative membranes for moderate temperature direct methanol fuel cell applications. (author)

Characterization of melt-blended graphene – poly(ether ether ketone) nanocomposite

International Nuclear Information System (INIS)

Tewatia, Arya; Hendrix, Justin; Dong, Zhizhong; Taghon, Meredith; Tse, Stephen; Chiu, Gordon; Mayo, William E.; Kear, Bernard; Nosker, Thomas; Lynch, Jennifer

2017-01-01

Using a high shear melt-processing method, graphene-reinforced polymer matrix composites (G-PMCs) were produced with good distribution and particle–matrix interaction of bi/trilayer graphene at 2 wt. % and 5 wt. % in poly ether ether ketone (2Gn-PEEK and 5Gn-PEEK). The morphology, structure, thermal properties, and mechanical properties of PEEK, 2Gn-PEEK and 5 Gn-PEEK were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), thermal gravimetric analysis (TGA), flexural mechanical testing, and dynamic mechanical analysis (DMA). Addition of graphene to PEEK induces surface crystallization, increased percent crystallinity, offers a composite that is thermally stable until 550 °C and enhances thermomechanical properties. Results show that graphene was successfully melt-blended within PEEK using this method.

Characterization of melt-blended graphene – poly(ether ether ketone) nanocomposite

Energy Technology Data Exchange (ETDEWEB)

Tewatia, Arya; Hendrix, Justin [Department of Materials Science and Engineering, Rutgers University, 607 Taylor Road, Piscataway, NJ, 08854 (United States); Dong, Zhizhong [Department of Mechanical Engineering, Rutgers University, 98 Brett Road, Piscataway, NJ 08854 (United States); Taghon, Meredith [Department of Materials Science and Engineering, Rutgers University, 607 Taylor Road, Piscataway, NJ, 08854 (United States); Tse, Stephen [Department of Mechanical Engineering, Rutgers University, 98 Brett Road, Piscataway, NJ 08854 (United States); Chiu, Gordon; Mayo, William E.; Kear, Bernard; Nosker, Thomas [Department of Materials Science and Engineering, Rutgers University, 607 Taylor Road, Piscataway, NJ, 08854 (United States); Lynch, Jennifer, E-mail: jklynch@rci.rutgers.edu [Department of Materials Science and Engineering, Rutgers University, 607 Taylor Road, Piscataway, NJ, 08854 (United States)

2017-02-15

Using a high shear melt-processing method, graphene-reinforced polymer matrix composites (G-PMCs) were produced with good distribution and particle–matrix interaction of bi/trilayer graphene at 2 wt. % and 5 wt. % in poly ether ether ketone (2Gn-PEEK and 5Gn-PEEK). The morphology, structure, thermal properties, and mechanical properties of PEEK, 2Gn-PEEK and 5 Gn-PEEK were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry (DSC), thermal gravimetric analysis (TGA), flexural mechanical testing, and dynamic mechanical analysis (DMA). Addition of graphene to PEEK induces surface crystallization, increased percent crystallinity, offers a composite that is thermally stable until 550 °C and enhances thermomechanical properties. Results show that graphene was successfully melt-blended within PEEK using this method.

Study of sulfonated polyether ether ketone with pendant lithiated fluorinated sulfonic groups as ion conductive binder in lithium-ion batteries

Science.gov (United States)

Wei, Zengbin; Xue, Lixin; Nie, Feng; Sheng, Jianfang; Shi, Qianru; Zhao, Xiulan

2014-06-01

In an attempt to reduce the Li+ concentration polarization and electrolyte depletion from the electrode porous space, sulfonated polyether ether ketone with pendant lithiated fluorinated sulfonic groups (SPEEK-FSA-Li) is prepared and attempted as ionic conductivity binder. Sulfonated aromatic poly(ether ether ketone) exhibits strong adhesion and chemical stability, and lithiated fluorinated sulfonic side chains help to enhance the ionic conductivity and Li+ ion diffusion due to the charge delocalization over the sulfonic chain. The performances are evaluated by cyclic voltammetry, electrochemical impedance spectroscopy, charge-discharge cycle testing, 180° peel testing, and compared with the cathode prepared with polyvinylidene fluoride binder. The electrode prepared with SPEEK-FSA-Li binder forms the relatively smaller resistances of both the SEI and the charge transfer of lithium ion transport. This is beneficial to lithium ion intercalation and de-intercalation of the cathode during discharging-charging, therefore the cell prepared with SPEEK-FSA-Li shows lower charge plateau potential and higher discharge plateau potential. Compared with PVDF, the electrode with ionic binder shows smaller decrease in capacity with the increasing of cycle rate. Meanwhile, adhesion strength of electrode prepared with SPEEK-FSA-Li is more than five times greater than that with PVDF.

Craniofacial reconstruction using patient-specific implants polyether ether ketone with computer-assisted planning.

Science.gov (United States)

Manrique, Oscar J; Lalezarzadeh, Frank; Dayan, Erez; Shin, Joseph; Buchbinder, Daniel; Smith, Mark

2015-05-01

Reconstruction of bony craniofacial defects requires precise understanding of the anatomic relationships. The ideal reconstructive technique should be fast as well as economical, with minimal donor-site morbidity, and provide a lasting and aesthetically pleasing result. There are some circumstances in which a patient's own tissue is not sufficient to reconstruct defects. The development of sophisticated software has facilitated the manufacturing of patient-specific implants (PSIs). The aim of this study was to analyze the utility of polyether ether ketone (PEEK) PSIs for craniofacial reconstruction. We performed a retrospective chart review from July 2009 to July 2013 in patients who underwent craniofacial reconstruction using PEEK-PSIs using a virtual process based on computer-aided design and computer-aided manufacturing. A total of 6 patients were identified. The mean age was 46 years (16-68 y). Operative indications included cancer (n = 4), congenital deformities (n = 1), and infection (n = 1). The mean surgical time was 3.7 hours and the mean hospital stay was 1.5 days. The mean surface area of the defect was 93.4 ± 43.26 cm(2), the mean implant cost was $8493 ± $837.95, and the mean time required to manufacture the implants was 2 weeks. No major or minor complications were seen during the 4-year follow-up. We found PEEK implants to be useful in the reconstruction of complex calvarial defects, demonstrating a low complication rate, good outcomes, and high patient satisfaction in this small series of patients. Polyether ether ketone implants show promising potential and warrant further study to better establish the role of this technology in cranial reconstruction.

Organic monolith frits encased in polyether ether ketone tubing with improved durability for liquid chromatography.

Science.gov (United States)

Park, Sin Young; Cheong, Won Jo

2015-09-01

This study introduces a preparation method for polymer-encased monolith frits with improved durability for liquid chromatography columns. The inner surface of the polyether ether ketone tubing is pretreated with sulfuric acid in the presence of catalysts (vanadium oxide and sodium sulfate). The tubing was rinsed with water and acetone, flushed with nitrogen, and treated with glycidyl methacrylate. After washing, the monolith reaction mixture composed of lauryl methacrylate, ethylene glycol dimethacrylate, initiator, and porogenic solvent was filled in the tubing and subjected to in situ polymerization. The tubing was cut into thin slices and used as frits for microcolumns. To check their durability, the frit slices were placed in a vial and a heavy impact was applied on the vial by a vortex mixer for various periods. The frits made in the presence of catalysts were found to be more durable than those made without catalysts. Furthermore, when the monolith-incorporated tubing was used as a chromatography column, the column prepared in the presence of catalysts resulted in a better separation efficiency. The separation performance of the columns installed with the polyether ether ketone encased monolith frits was comparable to that of the columns installed with the commercial stainless-steel screen frits. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Implant Failure After Motec Wrist Joint Prosthesis Due to Failure of Ball and Socket-Type Articulation-Two Patients With Adverse Reaction to Metal Debris and Polyether Ether Ketone.

Science.gov (United States)

Karjalainen, Teemu; Pamilo, Konsta; Reito, Aleksi

2018-04-21

We describe 2 cases of articulation-related failures resulting in revision surgery after a Motec total wrist arthroplasty: one with an adverse reaction to metal debris and the other with an adverse reaction to polyether ether ketone. In the first patient, blood cobalt and chrome levels were elevated and magnetic resonance imaging showed clear signs of a pseudotumor. The other patient had an extensive release of polyether ether ketone particles into the surrounding synovia due to adverse wear conditions in the cup, leading to the formation of a fluid-filled cyst sac with a black lining and diffuse lymphocyte-dominated inflammation in the synovia. We recommend regular follow-up including x-rays, monitoring of cobalt and chrome ion levels, and a low threshold for cross-sectional imaging in patients who have undergone total wrist arthroplasty with a Motec joint prosthesis. Wear-related problems can also develop in implants in which polyether ether ketone is the bulk material. Copyright © 2018 American Society for Surgery of the Hand. Published by Elsevier Inc. All rights reserved.

Influence of Silica/Sulfonated Polyether-Ether Ketone as Polymer Electrolyte Membrane for Hydrogen Fueled Proton Exchange Membrane Fuel Cells

Directory of Open Access Journals (Sweden)

Sri Handayani

2011-12-01

Full Text Available The operation of non-humidified condition of proton exchange membrane fuel cell (PEMFC using composite sPEEK-silica membrane is reported. Sulfonated membrane of PEEK is known as hydrocarbon polyelectrolyte membrane for PEMFC and direct methanol fuel cell (DMFC. The state of the art of fuel cells is based on the perluorosulfonic acid membrane (Nafion. Nafion has been the most used in both PEMFC and DMFC due to good performance although in low humidified condition showed poor current density. Here we reported the effect of silica in hydrocarbon sPEEK membrane that contributes for a better water management system inside the cell, and showed 0.16 W/cm2 of power density which is 78% higher than that of non-silica modified [Keywords: composite membrane, polyether-ether ketone, silica, proton exchange membrane fuel cell].

Preparation of poly(ether ether ketone)-based polymer electrolytes for fuel cell membranes using grafting technique

International Nuclear Information System (INIS)

Hasegawa, Shin; Suzuki, Yasuyuki; Maekawa, Yasunari

2008-01-01

Poly(ether ether ketone) (PEEK)-based polymer electrolyte membranes (PEMs) was successfully prepared by radiation grafting of a styrene monomer into PEEK films and the consequent selective sulfonation of the grafting chains in the film state. Using milder sulfonation, the sulfonation reactions proceeded at the grafted chains in preference to the phenylene rings of PEEK main chains; as a result, the grafted films could successfully transform to a PEM with conductivity of more than 0.1 S/cm. The ion exchange capacity (IEC) and conductivity of the grafted PEEK electrolyte membranes were controlled to the ranges of 1.2-2.9 mmol/g and 0.03-0.18 S/cm by changing the grafting degree. It should be noted that this is the first example of directly transforming super-engineering plastic films into a PEM using radiation grafting

Proton-conducting membranes based on benzimidazole-containing sulfonated poly(ether ether ketone) compared with their carboxyl acid form

Energy Technology Data Exchange (ETDEWEB)

Li, Hongtao; Wu, Jing; Zhao, Chengji; Zhang, Gang; Zhang, Yang; Shao, Ke; Xu, Dan; Lin, Haidan; Han, Miaomiao; Na, Hui [Alan G MacDiarmid Institute, College of Chemistry, Jilin University, Changchun 130012 (China)

2009-10-15

A series of sulfonated poly(ether ether ketone) containing pendant carboxyl (C-SPEEKs) have been synthesized using a nucleophilic polycondesation reaction. A condensation reaction between 1,2-diaminobenzene and carboxyl resulted in a new series of copolymers containing benzimidazole groups (SPEEK-BIms). The expected structures of the sulfonated copolymers are confirmed by {sup 1}H NMR. The dependence of ion exchange capacity, water uptake, proton conductivity and methanol diffusion coefficient of SPEEK-BIm membranes has been studied and compared with their carboxyl acid form. The results suggest that the introduction of benzimidazole groups may be responsible for many excellent properties of the membranes for fuel cell. It is noticeable that the markedly improved oxidative stability is benefit for the application of membrane. (author)

Local deformation behavior of surface porous polyether-ether-ketone.

Science.gov (United States)

Evans, Nathan T; Torstrick, F Brennan; Safranski, David L; Guldberg, Robert E; Gall, Ken

2017-01-01

Surface porous polyether-ether-ketone has the ability to maintain the tensile monotonic and cyclic strength necessary for many load bearing orthopedic applications while providing a surface that facilitates bone ingrowth; however, the relevant deformation behavior of the pore architecture in response to various loading conditions is not yet fully characterized or understood. The focus of this study was to examine the compressive and wear behavior of the surface porous architecture using micro Computed Tomography (micro CT). Pore architectures of various depths (~0.5-2.5mm) and pore sizes (212-508µm) were manufactured using a melt extrusion and porogen leaching process. Compression testing revealed that the pore architecture deforms in the typical three staged linear elastic, plastic, and densification stages characteristic of porous materials. The experimental moduli and yield strengths decreased as the porosity increased but there was no difference in properties between pore sizes. The porous architecture maintained a high degree of porosity available for bone-ingrowth at all strains. Surface porous samples showed no increase in wear rate compared to injection molded samples, with slight pore densification accompanying wear. Copyright © 2016 Elsevier Ltd. All rights reserved.

Crosslinked poly(vinyl alcohol)/sulfonated poly(ether ether ketone) blend membranes for fuel cell applications - Surface energy characteristics and proton conductivity

Energy Technology Data Exchange (ETDEWEB)

Kanakasabai, P.; Vijay, P.; Deshpande, Abhijit P.; Varughese, Susy [Department of Chemical Engineering, Indian Institute of Technology Madras, Chennai 600 036 (India)

2011-02-01

Ionic polymers, their blends and composites are considered potential candidates for application as electrolytes in fuel cells. While developing new materials for membranes, it is important to understand the interactions of these electrolytic materials with electrodes/catalysts and with reactants/products. Some of these interactions can be understood by estimating the surface energy and wettability of the membrane materials. In this work, polyvinyl alcohol with varying degrees of sulfonation and its blend with sulfonated poly(ether ether ketone) are prepared and studied for their wettability characteristics using goniometry. The surface energy and its components are estimated using different approaches and compared. Properties such as the ion-exchange capacity, the proton conductivity and the water sorption/desorption behaviour are also investigated to understand the relationship with wettability and surface energy and its components. Among the different methods, the van Oss acid-base and the modified Berthelot approaches yield comparable estimates for the total surface energy. (author)

Polyether ether ketone implants achieve increased bone fusion when coated with nano-sized hydroxyapatite

DEFF Research Database (Denmark)

Johansson, Pär; Jimbo, Ryo; Naito, Yoshihito

2016-01-01

Polyether ether ketone (PEEK) possesses excellent mechanical properties similar to those of human bone and is considered the best alternative material other than titanium for orthopedic spine and trauma implants. However, the deficient osteogenic properties and the bioinertness of PEEK limit its...... fields of application. The aim of this study was to limit these drawbacks by coating the surface of PEEK with nano-scaled hydroxyapatite (HA) minerals. In the study, the biological response to PEEK, with and without HA coating, was investigated. Twenty-four screw-like and apically perforated implants...

Low-temperature direct heterogeneous bonding of polyether ether ketone and platinum.

Science.gov (United States)

Fu, Weixin; Shigetou, Akitsu; Shoji, Shuichi; Mizuno, Jun

2017-10-01

Direct heterogeneous bonding between polyether ether ketone (PEEK) and Pt was realized at the temperatures lower than 150°C. In order to create sufficient bondability to diverse materials, the surface was modified by vacuum ultraviolet (VUV) irradiation, which formed hydrate bridges. For comparison, direct bonding between surfaces atomically cleaned via Ar fast atom bombardment (FAB) was conducted in a vacuum. The VUV irradiation was found to be effective for creating an ultrathin hydrate bridge layer from the residual water molecules in the chamber. Tight bonds were formed through dehydration of the hydrate bridges by heating at 150°C, which also contributed to enhancing interdiffusion across the interface. The VUV-modified surfaces showed bondability as good as that of the FAB-treated surfaces, and the VUV-modified samples had shear strengths at the same level as those of FAB-treated surfaces. This technology will be of practical use in the packaging of lightweight, flexible biomedical devices. Copyright © 2017 Elsevier B.V. All rights reserved.

Rheological, mechanical and tribological properties of carbon-nanofibre reinforced poly (ether ether ketone composites

Directory of Open Access Journals (Sweden)

Volker Altstaedt

2003-12-01

Full Text Available Poly(ether ether ketone nanocomposites containing vapour-grown carbon nanofibres (CNF were produced using standard polymer processing techniques. At high shear rates no significant increase in resin viscosity was observed. Nevertheless, the addition of the CNFs results in a higher melt strength at 360°C. Electron microscopy confirmed the homogeneous dispersion and alignment of nanofibres in the polymer matrix. Evaluation of the mechanical composite properties revealed a linear increase in tensile stiffness and strength with nanofibre loading fractions up to 15 wt% whilst matrix ductility was maintained up to 10 wt%. An interpretation of the composite performance by short-fibre theory resulted in rather low intrinsic stiffness properties of the vapour-grown CNF. Differential scanning calorimetry was used to investigate crystallization kinetics and degree of crystallinity. The CNFs were found not to act as nucleating sites. Furthermore, unidirectional sliding tests against two different counterpart materials (100Cr6 martensitic bearing steel, X5CrNi18-10 austenitic stainless steel were performed. The carbon nanofibres were found to reduce the wear rate of PEEK significantly.

Mechanical properties of orthodontic wires covered with a polyether ether ketone tube.

Science.gov (United States)

Shirakawa, Nobukazu; Iwata, Toshio; Miyake, Shinjiro; Otuka, Takero; Koizumi, So; Kawata, Toshitugu

2018-03-21

To evaluate the esthetics and frictional force of an orthodontic wire passed through a newly designed tube made of a polyether ether ketone (PEEK) resin. Two types of standard PEEK tubes were prepared at 0.5 × 0.6ф and 0.8 × 0.9ф, and different archwires were passed through the tubes. Color values were determined according to brightness and hues. Friction was assessed with different bracket-wire combinations, and surface roughness was determined by stereomicroscopy before and after the application of friction. The PEEK tube showed a color difference that was almost identical to that of coated wires conventionally used in clinical practice, indicating a sufficient esthetic property. The result of the friction test showed that the frictional force was greatly reduced by passing the archwire through the PEEK tube in almost all of the archwires tested. Use of the new PEEK tube demonstrated a good combination of esthetic and functional properties for use in orthodontic appliances.

Properties investigation of sulfonated poly(ether ether ketone)/polyacrylonitrile acid-base blend membrane for vanadium redox flow battery application.

Science.gov (United States)

Li, Zhaohua; Dai, Wenjing; Yu, Lihong; Liu, Le; Xi, Jingyu; Qiu, Xinping; Chen, Liquan

2014-11-12

Acid-base blend membrane prepared from sulfonated poly(ether ether ketone) (SPEEK) and polyacrylonitrile (PAN) was detailedly evaluated for vanadium redox flow battery (VRFB) application. SPEEK/PAN blend membrane exhibited dense and homogeneous cross-section morphology as scanning electron microscopy and energy-dispersive X-ray spectroscopy images show. The acid-base interaction of ionic cross-linking and hydrogen bonding between SPEEK and PAN could effectively reduce water uptake, swelling ratio, and vanadium ion permeability, and improve the performance and stability of blend membrane. Because of the good balance of proton conductivity and vanadium ion permeability, blend membrane with 20 wt % PAN (S/PAN-20%) showed higher Coulombic efficiency (96.2% vs 91.1%) and energy efficiency (83.5% vs 78.4%) than Nafion 117 membrane at current density of 80 mA cm(-2) when they were used in VRFB single cell. Besides, S/PAN-20% membrane kept a stable performance during 150 cycles at current density of 80 mA cm(-2) in the cycle life test. Hence the SPEEK/PAN acid-base blend membrane could be used as promising candidate for VRFB application.

Effect of chemical etching on the Cu/Ni metallization of poly (ether ether ketone)/carbon fiber composites

International Nuclear Information System (INIS)

Di Lizhi; Liu Bin; Song Jianjing; Shan Dan; Yang Dean

2011-01-01

Poly(ether ether ketone)/carbon fiber composites (PEEK/Cf) were chemical etched by Cr 2 O 3 /H 2 SO 4 solution, electroless plated with copper and then electroplated with nickel. The effects of chemical etching time and temperature on the adhesive strength between PEEK/Cf and Cu/Ni layers were studied by thermal shock method. The electrical resistance of some samples was measured. X-ray photoelectron spectroscopy (XPS) was used to analyze the surface composition and functional groups. Scanning electron microscopy (SEM) was performed to observe the surface morphology of the composite, the chemical etched sample, the plated sample and the peeled metal layer. The results indicated that C=O bond increased after chemical etching. With the increasing of etching temperature and time, more and more cracks and partially exposed carbon fibers appeared at the surface of PEEK/Cf composites, and the adhesive strength increased consequently. When the composites were etched at 60 deg. C for 25 min and at 70-80 deg. C for more than 15 min, the Cu/Ni metallization layer could withstand four thermal shock cycles without bubbling, and the electrical resistivity of the metal layer of these samples increased with the increasing of etching temperature and time.

Fatigue data for polyether ether ketone (PEEK) under fully-reversed cyclic loading.

Science.gov (United States)

Shrestha, Rakish; Simsiriwong, Jutima; Shamsaei, Nima

2016-03-01

In this article, the data obtained from the uniaxial fully-reversed fatigue experiments conducted on polyether ether ketone (PEEK), a semi-crystalline thermoplastic, are presented. The tests were performed in either strain-controlled or load-controlled mode under various levels of loading. The data are categorized into four subsets according to the type of tests, including (1) strain-controlled fatigue tests with adjusted frequency to obtain the nominal temperature rise of the specimen surface, (2) strain-controlled fatigue tests with various frequencies, (3) load-controlled fatigue tests without step loadings, and (4) load-controlled fatigue tests with step loadings. Accompanied data for each test include the fatigue life, the maximum (peak) and minimum (valley) stress-strain responses for each cycle, and the hysteresis stress-strain responses for each collected cycle in a logarithmic increment. A brief description of the experimental method is also given.

Repairing a Facial Cleft by Polyether-Ether-Ketone Implant Combined With Titanium Mesh.

Science.gov (United States)

Deng, Yuan; Tang, Weiwei; Li, Zhengkang

2018-05-15

The Tessier Number 4 cleft is one of the rarest, most complex craniofacial anomalies that presents difficulties in surgical treatment. In this article, we report a case of simultaneous facial depression, eye displacement, and medial canthus deformity. In this case, the maxillary bony defect was reconstructed using computer-assisted design computer-assisted manufacturing (CAD-CAM) polyether-ether-ketone (PEEK) material, and the orbital floor defect was repaired with AO prefabricated titanium mesh. Additionally, the medial canthus was modified with canthopexy and a single Z-plasty flap. Owing to its relative rarity and varied clinical presentations, no definitive operative methods have been accepted for Tessier No. 4 facial cleft. This study presents the combination of CAD-CAM manufactured PEEK material and titanium mesh as an alternative approach for reconstructing the bony defect of Tessier No. 4 facial clefts.

L-Arginine modified multi-walled carbon nanotube/sulfonated poly(ether ether ketone) nanocomposite films for biomedical applications

Science.gov (United States)

Kaya, Hatice; Bulut, Osman; Kamali, Ali Reza; Ege, Duygu

2018-06-01

Favorable implant-tissue interactions are crucial to achieve successful osseointegration of the implants. Poly(ether ether ketone) (PEEK) is an interesting alternative to titanium in orthopedics because of its low cost, high biocompatibility and comparable mechanical properties with cancellous bone. Despite these advantages; however, the untreated surface of PEEK fails to osseointegrate due to its bioinert and hydrophobic behavior. This paper deals with the surface modification of PEEK with a novel method. For this, PEEK was first treated with concentrated sulfuric acid to prepare sulfonated PEEK (SPEEK) films using a solvent casting method. Then, 1 and 2 wt% multi-walled carbon nanotube was incorporated into SPEEK to form nanocomposite films. The samples were characterized with Fourier Transform Infrared Spectroscopy (FTIR) and Scanning Electron Microscopy. After successful preparation of the nanocomposite films, L-arginine was covalently conjugated on the nanocomposite films to further improve their surface properties. Subsequently, the samples were characterized using X-ray Photoemission Spectroscopy (XPS), water contact angle measurements and Atomic Force Microscopy (AFM) and Dynamic Mechanical Thermal Analysis (DMTA). Finally, cell culture studies were carried out by using Alamar Blue assay to evaluate the biocompatibility of the films. The results obtained indicate the successful preparation of L-arginine-conjugated MWCNT/SPEEK nanocomposite films. The modified surface shows potential to improve implants' mechanical and biological performances.

Allergic Reaction to Polyether Ether Ketone Following Cross-Reactivity to Epoxy Resin.

Science.gov (United States)

Kofler, Lukas; Wambacher, Markus; Schweinzer, Katrin; Scherl, Maritta; Kofler, Heinz

Polyether ether ketone (PEEK) is a thermoplastic polymer frequently used in engineering but also in medical devices. Only 1 case of allergic reaction to PEEK used as an implanted medical device has been reported so far; however, the route of sensitization remained unclear. Here we report on a 62-year-old male patient with a preknown, severe type IV allergy to epoxy resin. He reported strong pain in his shoulder after implantation of a PEEK-containing device after a rotator cuff injury. For testing, the device was implanted in a small pouch subcutaneously on the abdomen. The patient reported massive pain starting 8 hours after the implantation, strictly limited to the procedural area and showing perifocal erythema. A possible explanation of the sensitization mode is the source material for PEEK and epoxy resin, as both are mainly based on bisphenols. An allergic reaction to PEEK with preknown epoxy resin sensitization has not been reported so far. As epoxy resins are a frequent cause of occupational contact dermatitis and PEEK is widely used for medical and nonmedical devices, we believe that this is of great clinical relevance.

Friedel-Crafts Crosslinked Highly Sulfonated Polyether Ether Ketone (SPEEK) Membranes for a Vanadium/Air Redox Flow Battery.

Science.gov (United States)

Merle, Géraldine; Ioana, Filipoi Carmen; Demco, Dan Eugen; Saakes, Michel; Hosseiny, Seyed Schwan

2013-12-30

Highly conductive and low vanadium permeable crosslinked sulfonated poly(ether ether ketone) (cSPEEK) membranes were prepared by electrophilic aromatic substitution for a Vanadium/Air Redox Flow Battery (Vanadium/Air-RFB) application. Membranes were synthesized from ethanol solution and crosslinked under different temperatures with 1,4-benzenedimethanol and ZnCl2 via the Friedel-Crafts crosslinking route. The crosslinking mechanism under different temperatures indicated two crosslinking pathways: (a) crosslinking on the sulfonic acid groups; and (b) crosslinking on the backbone. It was observed that membranes crosslinked at a temperature of 150 °C lead to low proton conductive membranes, whereas an increase in crosslinking temperature and time would lead to high proton conductive membranes. High temperature crosslinking also resulted in an increase in anisotropy and water diffusion. Furthermore, the membranes were investigated for a Vanadium/Air Redox Flow Battery application. Membranes crosslinked at 200 °C for 30 min with a molar ratio between 2:1 (mol repeat unit:mol benzenedimethanol) showed a proton conductivity of 27.9 mS/cm and a 100 times lower VO2+ crossover compared to Nafion.

A new interpretation of SAXS peaks in sulfonated poly(ether ether ketone) (sPEEK) membranes for fuel cells.

Science.gov (United States)

Mendil-Jakani, H; Zamanillo Lopez, I; Legrand, P M; Mareau, V H; Gonon, L

2014-06-21

The structure of a commercial sulfonated poly(ether ether ketone) (sPEEK) membrane was analyzed by Small-Angle X-Ray Scattering (SAXS) for different water uptakes obtained after immersion in liquid water at various temperatures. For low membrane swelling, the SAXS profile displays only a wide-angle peak in the 0.2-0.3 Å(-1) region. As the membrane swells, two supplementary correlation peaks arise and shift towards small angles, which are the signature of a structural evolution of the membrane, whereas the wide angle peak remains stable. The SAXS spectra of sPEEK membranes can thus display three correlation peaks simultaneously. Therefore we propose a new interpretation of these SAXS spectra which conclude that the two small angle peaks are attributed to the so-called matrix and ionomer peaks and the wide-angle peak is ascribed to the mean separation distance between sulfonic acid groups grafted onto the polymer backbone. This peak attribution implies that the sPEEK nano-phase separation is triggered by an immersion in hot water (ionomer peak apparition). Our new peak attribution was confirmed by studying the impact of temperature, electron density contrast and ionic exchange capacity.

Sulfonated Holey Graphene Oxide (SHGO) Filled Sulfonated Poly(ether ether ketone) Membrane: The Role of Holes in the SHGO in Improving Its Performance as Proton Exchange Membrane for Direct Methanol Fuel Cells.

Science.gov (United States)

Jiang, Zhong-Jie; Jiang, Zhongqing; Tian, Xiaoning; Luo, Lijuan; Liu, Meilin

2017-06-14

Sulfonated holey graphene oxides (SHGOs) have been synthesized by the etching of sulfonated graphene oxides with concentrated HNO 3 under the assistance of ultrasonication. These SHGOs could be used as fillers for the sulfonated aromatic poly(ether ether ketone) (SPEEK) membrane. The obtained SHGO-incorporated SPEEK membrane has a uniform and dense structure, exhibiting higher performance as proton exchange membranes (PEMs), for instance, higher proton conductivity, lower activation energy for proton conduction, and comparable methanol permeability, as compared to Nafion 112. The sulfonated graphitic structure of the SHGOs is believed to be one of the crucial factors resulting in the higher performance of the SPEEK/SHGO membrane, since it could increase the local density of the -SO 3 H groups in the membrane and induce a strong interfacial interaction between SHGO and the SPEEK matrix, which improve the proton conductivity and lower the swelling ratio of the membrane, respectively. Additionally, the proton conductivity of the membrane could be further enhanced by the presence of the holes in the graphitic planes of the SHGOs, since it provides an additional channel for transport of the protons. When used, direct methanol fuel cell with the SPEEK/SHGO membrane is found to exhibit much higher performance than that with Nafion 112, suggesting potential use of the SPEEK/SHGO membrane as the PEMs.

Effects of microstructural inclusions on fatigue life of polyether ether ketone (PEEK).

Science.gov (United States)

Simsiriwong, Jutima; Shrestha, Rakish; Shamsaei, Nima; Lugo, Marcos; Moser, Robert D

2015-11-01

In this study, the effects of microstructural inclusions on fatigue life of polyether ether ketone (PEEK) was investigated. Due to the versatility of its material properties, the semi-crystralline PEEK polymer has been increasingly adopted in a wide range of applications particularly as a biomaterial for orthopedic, trauma, and spinal implants. To obtain the cyclic behavior of PEEK, uniaxial fully-reversed strain-controlled fatigue tests were conducted at ambient temperature and at 0.02 mm/mm to 0.04 mm/mm strain amplitudes. The microstructure of PEEK was obtained using the optical and the scanning electron microscope (SEM) to determine the microstructural inclusion properties in PEEK specimen such as inclusion size, type, and nearest neighbor distance. SEM analysis was also conducted on the fracture surface of fatigue specimens to observe microstructural inclusions that served as the crack incubation sites. Based on the experimental strain-life results and the observed microstructure of fatigue specimens, a microstructure-sensitive fatigue model was used to predict the fatigue life of PEEK that includes both crack incubation and small crack growth regimes. Results show that the employed model is applicable to capture microstructural effects on fatigue behavior of PEEK. Copyright © 2015 Elsevier Ltd. All rights reserved.

Highly stable ionic-covalent cross-linked sulfonated poly(ether ether ketone) for direct methanol fuel cells

Science.gov (United States)

Lei, Linfeng; Zhu, Xingye; Xu, Jianfeng; Qian, Huidong; Zou, Zhiqing; Yang, Hui

2017-05-01

A novel ionic cross-linked sulfonated poly(ether ether ketone) containing equal content of sulfonic acid and pendant tertiary amine groups (TA-SPEEK) has been initially synthesized for the application in direct methanol fuel cells (DMFCs). By adjusting the ratio of p-xylene dibromide to tertiary amine groups of TA-SPEEK, a series of ionic-covalent cross-linked membranes (C-SPEEK-x) with tunable degree of cross-linking are prepared. Compared with the pristine membrane, the ionic and ionic-covalent cross-linked proton exchange membranes (PEMs) exhibit reduced methanol permeability and improved mechanical properties, dimensional and oxidative stability. The proton conductivity and methanol selectivity of protonated TA-SPEEK and C-SPEEK-x at 25 °C is up to 0.109 S cm-1 and 3.88 × 105 S s cm-3, respectively, which are higher than that of Nafion 115. The DMFC incorporating C-SPEEK-25 exhibits a maximum power density as high as 35.3 mW cm-2 with 4 M MeOH at 25 °C (31.8 mW cm-2 for Nafion 115). Due to the highly oxidative stability of the membrane, no obvious performance degradation of the DMFC is observed after more than 400 h operation, indicating such cost-effective ionic-covalent cross-linked membranes have substantial potential as alternative PEMs for DMFC applications.

The Effect of Core and Veneering Design on the Optical Properties of Polyether Ether Ketone.

Science.gov (United States)

Zeighami, S; Mirmohammadrezaei, S; Safi, M; Falahchai, S M

2017-12-01

This study aimed to evaluate the effect of core shade and core and veneering thickness on color parameters and translucency of polyether ether ketone (PEEK). Sixty PEEK discs (0.5 and 1 mm in thickness) with white and dentine shades were veneered with A2 shade indirect composite resin with 0.5, 1 and 1.5 mm thickness (n=5). Cores without the veneering material served as controls for translucency evaluation. Color parameters were measured by a spectroradiometer. Color difference (ΔE₀₀) and translucency parameters (TP) were computed. Data were analyzed using one-way ANOVA and Tukey's test (for veneering thickness) and independent t-test (for core shade and thickness) via SPSS 20.0 (p⟨0.05). Regarding the veneering thickness, white cores of 0.5 mm thickness showed significant differences in all color parameters. In white cores of 1 mm thickness and dentine cores of 0.5 and 1 mm thickness, there were statistically significant differences only in L∗, a∗ and h∗. The mean TP was significantly higher in all white cores of 1 mm thickness than dentine cores of 1 mm. Considering ΔE₀₀=3.7 as clinically unacceptable, only three groups had higher mean ΔE₀₀ values. Core shade, core thickness, and the veneering thickness affected the color and translucency of PEEK restorations. Copyright© 2017 Dennis Barber Ltd.

Preliminary Study of the Use of Sulphonated Polyether Ether Ketone (SPEEK as Proton Exchange Membrane for Microbial Fuel Cell (MFC

Directory of Open Access Journals (Sweden)

Dani Permana

2018-02-01

Full Text Available Sulfonated polyether ether ketone (SPEEK was utilized as a proton exchange membrane (PEM in Microbial Fuel Cell (MFC. The SPEEK performance in producing electricity had been observed in MFC using wastewater and glucose as substrates. The MFC with catering and tofu wastewater produced maximum power density about 0.31 mW/m2 and 0.03 mW/m2, respectively, lower that of MFC with tapioca average power density of 39.4 W/m2 over 48 h. The power density boosted because of the presence of Saccharomyces cerevisiae as inoculum. The study using of S. cerevisiae and Acetobacter acetii, separately, were also conducted in with glucose as substrate. The MFC produced an average power densities were 7.3 and 6.4 mW/m2 for S. cerevisiae and A. acetii, respectively. The results of this study indicated that SPEEK membrane has the potential usage in MFCs and can substitute the commercial membrane, Nafion. Article History: Received: Juni 14th 2017; Received: Sept 25th 2017; Accepted: December 16th 2017; Available online How to Cite This Article: Putra, H.E., Permana, D and Djaenudin, D. (2018 Preliminary Study of the Use of Sulfonated Polyether Ether Ketone (SPEEK as Proton Exchange Membrane for Microbial Fuel Cell (MFC. International Journal of Renewable Energy Development, 7(1, 7-12. https://doi.org/10.14710/ijred.7.1.7-12

Preparation of graphite intercalation compounds containing oligo and polyethers

Science.gov (United States)

Zhang, Hanyang; Lerner, Michael M.

2016-02-01

Layered host-polymer nanocomposites comprising polymeric guests between inorganic sheets have been prepared with many inorganic hosts, but there is limited evidence for the incorporation of polymeric guests into graphite. Here we report for the first time the preparation, and structural and compositional characterization of graphite intercalation compounds (GICs) containing polyether bilayers. The new GICs are obtained by either (1) reductive intercalation of graphite with an alkali metal in the presence of an oligo or polyether and an electrocatalyst, or (2) co-intercalate exchange of an amine for an oligo or polyether in a donor-type GIC. Structural characterization of products using powder X-ray diffraction, Raman spectroscopy, and thermal analyses supports the formation of well-ordered, first-stage GICs containing alkali metal cations and oligo or polyether bilayers between reduced graphene sheets.Layered host-polymer nanocomposites comprising polymeric guests between inorganic sheets have been prepared with many inorganic hosts, but there is limited evidence for the incorporation of polymeric guests into graphite. Here we report for the first time the preparation, and structural and compositional characterization of graphite intercalation compounds (GICs) containing polyether bilayers. The new GICs are obtained by either (1) reductive intercalation of graphite with an alkali metal in the presence of an oligo or polyether and an electrocatalyst, or (2) co-intercalate exchange of an amine for an oligo or polyether in a donor-type GIC. Structural characterization of products using powder X-ray diffraction, Raman spectroscopy, and thermal analyses supports the formation of well-ordered, first-stage GICs containing alkali metal cations and oligo or polyether bilayers between reduced graphene sheets. Electronic supplementary information (ESI) available: Domain size, additional Raman spectra info, compositional calculation, and packing fractions. See DOI: 10.1039/c5

Effect of degree of sulfonation and casting solvent on sulfonated poly(ether ether ketone) membrane for vanadium redox flow battery

Science.gov (United States)

Xi, Jingyu; Li, Zhaohua; Yu, Lihong; Yin, Bibo; Wang, Lei; Liu, Le; Qiu, Xinping; Chen, Liquan

2015-07-01

The properties of sulfonated poly(ether ether ketone) (SPEEK) membranes with various degree of sulfonation (DS) and casting solvent are investigated for vanadium redox flow battery (VRFB). The optimum DS of SPEEK membrane is firstly confirmed by various characterizations such as physicochemical properties, ion selectivity, and VRFB single-cell performance. Subsequently the optimum casting solvent is selected for the optimum DS SPEEK membrane within N,N‧-dimethylformamide (DMF), N,N‧-dimethylacetamide (DMAc), N-methyl-2-pyrrolidone (NMP), and dimethylsulfoxide (DMSO). The different performance of SPEEK membranes prepared with various casting solvents can be attributed to the different interaction between solvent and -SO3H group of SPEEK. In the VRFB single-cell test, the optimum SPEEK membrane with DS of 67% and casting solvent of DMF (S67-DMF membrane) exhibits higher VRFB efficiencies and better cycle-life performance at 80 mA cm-2. The investigation of various DS and casting solvent will be effective guidance on the selection and modification of SPEEK membrane towards VRFB application.

Friedel–Crafts Crosslinked Highly Sulfonated Polyether Ether Ketone (SPEEK Membranes for a Vanadium/Air Redox Flow Battery

Directory of Open Access Journals (Sweden)

Géraldine Merle

2013-12-01

Full Text Available Highly conductive and low vanadium permeable crosslinked sulfonated poly(ether ether ketone (cSPEEK membranes were prepared by electrophilic aromatic substitution for a Vanadium/Air Redox Flow Battery (Vanadium/Air-RFB application. Membranes were synthesized from ethanol solution and crosslinked under different temperatures with 1,4-benzenedimethanol and ZnCl2 via the Friedel–Crafts crosslinking route. The crosslinking mechanism under different temperatures indicated two crosslinking pathways: (a crosslinking on the sulfonic acid groups; and (b crosslinking on the backbone. It was observed that membranes crosslinked at a temperature of 150 °C lead to low proton conductive membranes, whereas an increase in crosslinking temperature and time would lead to high proton conductive membranes. High temperature crosslinking also resulted in an increase in anisotropy and water diffusion. Furthermore, the membranes were investigated for a Vanadium/Air Redox Flow Battery application. Membranes crosslinked at 200 °C for 30 min with a molar ratio between 2:1 (mol repeat unit:mol benzenedimethanol showed a proton conductivity of 27.9 mS/cm and a 100 times lower VO2+ crossover compared to Nafion.

Friedel–Crafts Crosslinked Highly Sulfonated Polyether Ether Ketone (SPEEK) Membranes for a Vanadium/Air Redox Flow Battery

Science.gov (United States)

Merle, Géraldine; Ioana, Filipoi Carmen; Demco, Dan Eugen; Saakes, Michel; Hosseiny, Seyed Schwan

2014-01-01

Highly conductive and low vanadium permeable crosslinked sulfonated poly(ether ether ketone) (cSPEEK) membranes were prepared by electrophilic aromatic substitution for a Vanadium/Air Redox Flow Battery (Vanadium/Air-RFB) application. Membranes were synthesized from ethanol solution and crosslinked under different temperatures with 1,4-benzenedimethanol and ZnCl2 via the Friedel–Crafts crosslinking route. The crosslinking mechanism under different temperatures indicated two crosslinking pathways: (a) crosslinking on the sulfonic acid groups; and (b) crosslinking on the backbone. It was observed that membranes crosslinked at a temperature of 150 °C lead to low proton conductive membranes, whereas an increase in crosslinking temperature and time would lead to high proton conductive membranes. High temperature crosslinking also resulted in an increase in anisotropy and water diffusion. Furthermore, the membranes were investigated for a Vanadium/Air Redox Flow Battery application. Membranes crosslinked at 200 °C for 30 min with a molar ratio between 2:1 (mol repeat unit:mol benzenedimethanol) showed a proton conductivity of 27.9 mS/cm and a 100 times lower VO2+ crossover compared to Nafion. PMID:24957118

High strength, surface porous polyether-ether-ketone for load-bearing orthopaedic implants

Science.gov (United States)

Evans, Nathan T.; Torstrick, F. Brennan; Lee, Christopher S.D.; Dupont, Kenneth M.; Safranski, David L.; Chang, W. Allen; Macedo, Annie E.; Lin, Angela; Boothby, Jennifer M.; Whittingslow, Daniel C.; Carson, Robert A.; Guldberg, Robert E.; Gall, Ken

2015-01-01

Despite its widespread clinical use in load-bearing orthopaedic implants, polyether-ether-ketone (PEEK) is often associated with poor osseointegration. In this study, a surface porous PEEK material (PEEK-SP) was created using a melt extrusion technique. The porous layer thickness was 399.6±63.3 µm and possessed a mean pore size of 279.9±31.6 µm, strut spacing of 186.8±55.5 µm, porosity of 67.3±3.1%, and interconnectivity of 99.9±0.1%. Monotonic tensile tests showed that PEEK-SP preserved 73.9% of the strength (71.06±2.17 MPa) and 73.4% of the elastic modulus (2.45±0.31 GPa) of as-received, injection molded PEEK. PEEK-SP further demonstrated a fatigue strength of 60.0 MPa at one million cycles, preserving 73.4% of the fatigue resistance of injection molded PEEK. Interfacial shear testing showed the pore layer shear strength to be 23.96±2.26 MPa. An osseointegration model in the rat revealed substantial bone formation within the pore layer at 6 and 12 weeks via µCT and histological evaluation. Ingrown bone was more closely apposed to the pore wall and fibrous tissue growth was reduced in PEEK-SP when compared to non-porous PEEK controls. These results indicate that PEEK-SP could provide improved osseointegration while maintaining the structural integrity necessary for load-bearing orthopaedic applications. PMID:25463499

Dihydrogenimidazole modified silica-sulfonated poly(ether ether ketone) hybrid materials as electrolyte membranes for direct ethanol fuel cells

Energy Technology Data Exchange (ETDEWEB)

Roelofs, Kimball S.; Hirth, Thomas [Fraunhofer Institute for Interfacial Engineering and Biotechnology, Nobelstr. 12, 70569 Stuttgart (Germany); Schiestel, Thomas, E-mail: Thomas.Schiestel@igb.fraunhofer.de [Fraunhofer Institute for Interfacial Engineering and Biotechnology, Nobelstr. 12, 70569 Stuttgart (Germany)

2011-05-25

The present study reports on dihydrogenimidazole modified inorganic-organic mixed matrix membranes for possible application as a proton exchange membrane in direct ethanol fuel cells. The polymeric phase consisted mainly of sulfonated poly(ether ether ketone) (sPEEK) with a sulfonation degree of 55%. The inorganic phase was built up from hydrophilic fumed silica particles interconnected with partially hydrolyzed and condensed tetraethoxysilane with a total inorganic loading of 27.3%. This inorganic phase was further modified with N-(3-triethoxysilylpropyl)-4,5-dihydroimidazole (DHIM), which consists of an hydrolyzable inorganic part and a functional organic group. The influence of the modifier on the mixed matrix system was studied by means of various modifier concentrations in various aqueous-ethanolic systems (water, 2 M and 4 M ethanol). Modifier concentration and ethanol concentration of the ethanol-water mixture exhibited significant but opposite effects on the liquid uptake of the mixed matrix membranes. The proton conductivity as well as the proton diffusion coefficient as a function of modifier content showed a linear decrease. The proton conductivity as a function of temperature showed Arrhenius behavior and the activation energy of the mixed matrix membranes was 43.9 {+-} 2.6 kJ mol{sup -1}. High selectivity of proton diffusion coefficient to ethanol permeability coefficient was obtained with high modifier concentrations. At low modifier concentrations, this selectivity was dominated by ethanol permeation and at high modifier concentrations by proton diffusion. The main electrolyte properties can be optimized by setting the DHIM content in mixed matrix membrane. With this approach, tailor-made membranes can be prepared for possible application in direct ethanol fuel cells.

Dihydrogenimidazole modified silica-sulfonated poly(ether ether ketone) hybrid materials as electrolyte membranes for direct ethanol fuel cells

International Nuclear Information System (INIS)

Roelofs, Kimball S.; Hirth, Thomas; Schiestel, Thomas

2011-01-01

The present study reports on dihydrogenimidazole modified inorganic-organic mixed matrix membranes for possible application as a proton exchange membrane in direct ethanol fuel cells. The polymeric phase consisted mainly of sulfonated poly(ether ether ketone) (sPEEK) with a sulfonation degree of 55%. The inorganic phase was built up from hydrophilic fumed silica particles interconnected with partially hydrolyzed and condensed tetraethoxysilane with a total inorganic loading of 27.3%. This inorganic phase was further modified with N-(3-triethoxysilylpropyl)-4,5-dihydroimidazole (DHIM), which consists of an hydrolyzable inorganic part and a functional organic group. The influence of the modifier on the mixed matrix system was studied by means of various modifier concentrations in various aqueous-ethanolic systems (water, 2 M and 4 M ethanol). Modifier concentration and ethanol concentration of the ethanol-water mixture exhibited significant but opposite effects on the liquid uptake of the mixed matrix membranes. The proton conductivity as well as the proton diffusion coefficient as a function of modifier content showed a linear decrease. The proton conductivity as a function of temperature showed Arrhenius behavior and the activation energy of the mixed matrix membranes was 43.9 ± 2.6 kJ mol -1 . High selectivity of proton diffusion coefficient to ethanol permeability coefficient was obtained with high modifier concentrations. At low modifier concentrations, this selectivity was dominated by ethanol permeation and at high modifier concentrations by proton diffusion. The main electrolyte properties can be optimized by setting the DHIM content in mixed matrix membrane. With this approach, tailor-made membranes can be prepared for possible application in direct ethanol fuel cells.

Bio-functionalisation of polyether ether ketone using plasma immersion ion implantation

Science.gov (United States)

Wakelin, Edgar; Yeo, Giselle; Kondyurin, Alexey; Davies, Michael; McKenzie, David; Weiss, Anthony; Bilek, Marcela

2015-12-01

Plasma immersion ion implantation (PIII) is used here to improve the surface bioactivity of polyether ether ketone (PEEK) by modifying the chemical and mechanical properties and by introducing radicals. Modifications to the chemical and mechanical properties are characterised as a function of ion fluence (proportional to treatment time) to determine the suitability of the treated surfaces for biological applications. Radical generation increases with treatment time, where treatments greater than 400 seconds result in a high concentration of long-lived radicals. Radical reactions are responsible for oxidation of the surface, resulting in a permanent increase in the polar surface energy. The nano-scale reduced modulus was found to increase with treatment time at the surface from 4.4 to 5.2 GPa. The macromolecular Young's modulus was also found to increase, but by an amount corresponding to the volume fraction of the ion implanted region. The treated surface layer exhibited cracking under cyclical loads, associated with an increased modulus due to dehydrogenation and crosslinking, however it did not show any sign of delamination, indicating that the modified layer is well integrated with the substrate - a critical factor for bioactive surface coatings to be used in-vivo. Protein immobilisation on the PIII treated surfaces was found to saturate after 240 seconds of treatment, indicating that there is room to tune surface mechanical properties for specific applications without affecting the protein coverage. Our findings indicate that the modification of the chemical and mechanical properties by PIII treatments as well as the introduction of radicals render PEEK well suited for use in orthopaedic implantable devices.

High-strength, surface-porous polyether-ether-ketone for load-bearing orthopedic implants.

Science.gov (United States)

Evans, Nathan T; Torstrick, F Brennan; Lee, Christopher S D; Dupont, Kenneth M; Safranski, David L; Chang, W Allen; Macedo, Annie E; Lin, Angela S P; Boothby, Jennifer M; Whittingslow, Daniel C; Carson, Robert A; Guldberg, Robert E; Gall, Ken

2015-02-01

Despite its widespread clinical use in load-bearing orthopedic implants, polyether-ether-ketone (PEEK) is often associated with poor osseointegration. In this study, a surface-porous PEEK material (PEEK-SP) was created using a melt extrusion technique. The porous layer was 399.6±63.3 μm thick and possessed a mean pore size of 279.9±31.6 μm, strut spacing of 186.8±55.5 μm, porosity of 67.3±3.1% and interconnectivity of 99.9±0.1%. Monotonic tensile tests showed that PEEK-SP preserved 73.9% of the strength (71.06±2.17 MPa) and 73.4% of the elastic modulus (2.45±0.31 GPa) of as-received, injection-molded PEEK. PEEK-SP further demonstrated a fatigue strength of 60.0 MPa at one million cycles, preserving 73.4% of the fatigue resistance of injection-molded PEEK. Interfacial shear testing showed the pore layer shear strength to be 23.96±2.26 MPa. An osseointegration model in the rat revealed substantial bone formation within the pore layer at 6 and 12 weeks via microcomputed tomography and histological evaluation. Ingrown bone was more closely apposed to the pore wall and fibrous tissue growth was reduced in PEEK-SP when compared to non-porous PEEK controls. These results indicate that PEEK-SP could provide improved osseointegration while maintaining the structural integrity necessary for load-bearing orthopedic applications. Copyright © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Improved adaptability of polyaryl-ether-ether-ketone with texture pattern and graphite-like carbon film for bio-tribological applications

Science.gov (United States)

Ren, Siming; Huang, Jinxia; Cui, Mingjun; Pu, Jibin; Wang, Liping

2017-04-01

With the development of surface treatment technology, an increasing number of bearings, seals, dynamic friction drive or even biomedical devices involve a textured surface to improve lubrication and anti-wear. The present investigation has been conducted in order to evaluate the friction and wear behaviours of textured polyaryl-ether-ether-ketone (PEEK) coated with a graphite-like carbon (GLC) film sliding against stainless steel pin in biological medium. Compared with pure PEEK, the PEEK coated with GLC film shows excellent tribological performance with a low friction of 0.08 and long lifetime (wear volumes are about 3.78 × 10-4 mm3 for un-textured one and 2.60 × 10-4 mm3 for textured GLC film after 36,000 s of sliding) under physiological saline solution. In particular, the GLC film with appropriate dimple area density is effective to improve friction reduction and wear resistance properties of PEEK substrate under biological solution, which is attributed to the entrapment of wear debris in the dimples to inhibit the graphitization and the fluid dynamic pressure effect derived from the texture surface to increase the thickness in elastohydrodynamic lubrication (EHL) film during sliding motions. Moreover, the friction coefficient of GLC film under physiological saline solution decreases with the increase in the applied load. With the increasing applied load, the texture surface is responsible for accounting the improved wear resistance and a much lower graphitization of the GLC film during whole test.

Morphology Effect on Proton Dynamics in Nafion® 117 and Sulfonated Polyether Ether Ketone

Science.gov (United States)

Leong, Jun Xing; Diño, Wilson Agerico; Ahmad, Azizan; Daud, Wan Ramli Wan; Kasai, Hideaki

2016-09-01

We report results of our experimental and theoretical studies on the dynamics of proton conductivity in Nafion® 117 and self-fabricated sulfonated polyether ether ketone (SPEEK) membranes. Knowing that the presence of water molecules in the diffusion process results in a lower energy barrier, we determined the diffusion barriers and corresponding tunneling probabilities of Nafion® 117 and SPEEK system using a simple theoretical model that excludes the medium (water molecules) in the initial calculations. We then propose an equation that relates the membrane conductivity to the tunneling probability. We recover the effect of the medium by introducing a correction term into the proposed equation, which takes into account the effect of the proton diffusion distance and the hydration level. We have also experimentally verified that the proposed equation correctly explain the difference in conductivity between Nafion® 117 and SPEEK. We found that membranes that are to be operated in low hydration environments (high temperatures) need to be designed with short diffusion distances to enhance and maintain high conductivity.

Preparation, characterization and in vitro response of bioactive coatings on polyether ether ketone.

Science.gov (United States)

Durham, John W; Allen, Matthew J; Rabiei, Afsaneh

2017-04-01

Polyether ether ketone (PEEK) is a highly heat-resistant thermoplastic with excellent strength and elastic modulus similar to human bone, making it an attractive material for orthopedic implants. However, the hydrophobic surface of PEEK implants induces fibrous encapsulation which is unfavorable for stable implant anchorage. In this study, PEEK was coated via ion-beam-assisted deposition (IBAD) using a two-layer design of yttria-stabilized zirconia (YSZ) as a heat-protection layer, and hydroxyapatite (HA) as a top layer to improve osseointegration. Microstructural analysis of the coatings showed a dense, uniform columnar grain structure in the YSZ layer and no delamination from the substrate. The HA layer was found to be amorphous and free of porosities in its as-deposited state. Subsequent heat treatment via microwave energy followed by autoclaving crystallized the HA layer, confirmed by SEM and XRD analysis. An in vitro study using MC3T3 preosteoblast cells showed improved bioactivity in heat-treated sample groups. Cell proliferation, differentiation, and mineralization were analyzed by MTT assay and DNA content, osteocalcin expression, and Alizarin Red S (AR-S) content, respectively. Initial cell growth was increased, and osteogenic maturation and mineralization were accelerated most on coatings that underwent a combined microwave and autoclave heat treatment process as compared to uncoated PEEK and amorphous HA surfaces. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 105B: 560-567, 2017. © 2015 Wiley Periodicals, Inc.

Etched poly(ether ether ketone) jacket stir bar with detachable dumbbell-shaped structure for stir bar sorptive extraction.

Science.gov (United States)

Zhou, Wei; Wang, Chenlu; Wang, Xuemei; Chen, Zilin

2018-06-08

Development of stir bar sorptive extraction (SBSE) device with high stability and extraction efficiency is critical and challenging by date. In this work, etched poly(ether ether ketone) (PEEK) tube with high mechanical strength and large specific surface area was used as jacket for SBSE device. By etching with concentrated sulfuric acid, the smooth outer surface of PEEK become porous with plenty of micro holes, which was beneficial for coating of sorbents and significantly improved the extraction performance. After functionalized by bio-polydopamine method, strong hydrophobic p-naphtholbenzein molecular was immobilized onto the chemical resistant PEEK surface (PNB@E-PEEK) as stationary phase. We also firstly developed a simple detachable dumbbell-shaped structure for improving the workability of PEEK jacket stir bar. The dumbbell-shaped construction can eliminate the friction between stir bar and container, and the design of detachable structure make elution can be accomplished easier with small amount of organic solvent. It was interesting that the developed detachable dumbbell-shaped PNB@E-PEEK stir bar showed exceptional stability and extraction efficiency for SBSE enrichment of multiple analytes including several Sudan dyes, triazines, polycyclic aromatic hydrocarbons (PAHs), alkaloids and flavonoid. By coupling with high performance liquid chromatography-ultraviolet detection (HPLC-UV), PNB@E-PEEK stir bar based SBSE-HPLC-UV method was applied for the analysis of common Sudan dye pollutants. The method showed low limits of detection (0.02-0.03 ng/mL), good linearity (R 2  ≥ 0.9979) and good reproducibility (relative standard deviation ≤ 7.96%). It has been successfully applied to determine three dye pollutants in tap and lake water. Copyright © 2018 Elsevier B.V. All rights reserved.

Sulfonated poly(ether ether ketone)/poly(vinyl alcohol) sensitizing system for solution photogeneration of small Ag, Au, and Cu crystallites.

Science.gov (United States)

Korchev, A S; Shulyak, T S; Slaten, B L; Gale, W F; Mills, G

2005-04-28

Illumination of air-free aqueous solutions containing sulfonated poly(ether ether ketone) and poly(vinyl alcohol) with 350 nm light results in benzophenone ketyl radicals of the polyketone. The polymer radicals form with a quantum yield 0.02 and decay with a second-order rate constant 6 orders of magnitude lower than that of typical alpha-hydroxy radicals. Evidence is presented that the polymeric benzophenone ketyl radicals reduce Ag+, Cu2+, and AuCl4- to metal particles of nanometer dimensions. Decreases in the reduction rates with increasing Ag(I), Cu(II), and Au(III) concentrations are explained using a kinetic model in which the metal ions quench the excited state of the polymeric benzophenone groups, which forms the macromolecular radicals. Quenching is fastest for Ag+, whereas Cu2+ and AuCl4- exhibit similar rate constants. Particle formation becomes more complex as the number of equivalents needed to reduce the metal ions increases; the Au(III) system is an extreme case where the radical reactions operate in parallel with secondary light-initiated and thermal reduction channels. For each metal ion, the polymer-initiated photoreactions produce crystallites possessing distinct properties, such as a very strong plasmon in the Ag case or the narrow size distribution exhibited by Au particles.

Origin of mechanical modifications in poly (ether ether ketone)/carbon nanotube composite

International Nuclear Information System (INIS)

Pavlenko, Ekaterina; Puech, Pascal; Bacsa, Wolfgang; Boyer, François; Olivier, Philippe; Sapelkin, Andrei; King, Stephen; Heenan, Richard; Pons, François; Gauthier, Bénédicte; Cadaux, Pierre-Henri

2014-01-01

Variations in the hardness of a poly (ether ether ketone) beam electrically modified with multi-walled carbon nanotubes (MWCNT, 0.5%-3%) are investigated. It is shown that both rupture and hardness variations correlate with the changes in carbon nanotube concentration when using micro indentation and extended Raman imaging. Statistical analysis of the relative spectral intensities in the Raman image is used to estimate local tube concentration and polymer crystallinity. We show that the histogram of the Raman D band across the image provides information about the amount of MWCNTs and the dispersion of MWCNTs in the composite. We speculate that we have observed a local modification of the ordering between pure and modified polymer. This is partially supported by small angle neutron scattering measurements, which indicate that the agglomeration state of the MWCNTs is the same at the concentrations studied.

Origin of mechanical modifications in poly (ether ether ketone)/carbon nanotube composite

Energy Technology Data Exchange (ETDEWEB)

Pavlenko, Ekaterina; Puech, Pascal; Bacsa, Wolfgang, E-mail: wolfgang.bacsa@cemes.fr [CEMES-CNRS and University of Toulouse, 29 Jeanne Marvig, 31055 Toulouse (France); Boyer, François; Olivier, Philippe [Université de Toulouse, Institut Clément Ader, I.U.T. Université Paul Sabatier - 133C Avenue de Rangueil - B.P. 67701, 31077 Toulouse CEDEX 4 (France); Sapelkin, Andrei [School of Physics and Astronomy, Queen Mary, University of London, Mile End Road, E1 4NS London (United Kingdom); King, Stephen; Heenan, Richard [ISIS Facility, Rutherford Appleton Laboratory, Chilton, OX11 0QX Didcot (United Kingdom); Pons, François; Gauthier, Bénédicte; Cadaux, Pierre-Henri [AIRBUS FRANCE (B.E. M and P Toulouse), 316 Route de Bayonne, 31060 Toulouse (France)

2014-06-21

Variations in the hardness of a poly (ether ether ketone) beam electrically modified with multi-walled carbon nanotubes (MWCNT, 0.5%-3%) are investigated. It is shown that both rupture and hardness variations correlate with the changes in carbon nanotube concentration when using micro indentation and extended Raman imaging. Statistical analysis of the relative spectral intensities in the Raman image is used to estimate local tube concentration and polymer crystallinity. We show that the histogram of the Raman D band across the image provides information about the amount of MWCNTs and the dispersion of MWCNTs in the composite. We speculate that we have observed a local modification of the ordering between pure and modified polymer. This is partially supported by small angle neutron scattering measurements, which indicate that the agglomeration state of the MWCNTs is the same at the concentrations studied.

Effect of cesium salt of tungstophosphoric acid (Cs-TPA) on the properties of sulfonated polyether ether ketone (SPEEK) composite membranes for fuel cell applications

Energy Technology Data Exchange (ETDEWEB)

Dogan, Hacer; Inan, Tuelay Y.; Unveren, Elif [The Scientific and Technological Research Council of Turkey (TUeBiTAK), Marmara Research Center, Chemistry Institute, P.K. 21, 41470 Gebze-Kocaeli (Turkey); Kaya, Metin [DEMIRDOeKUeM A.S. 4 Eyluel Mah, ismet inoenue Cad. No:245 Bozueyuek/Bilecik (Turkey)

2010-08-15

We have prepared composite membranes for fuel cell applications. Cesium salt of tungstophosphoric acid (Cs-TPA) particles was synthesized by aqueous solutions of tungstophosphoric acid and cesium hydroxide and, Cs-TPA particles and sulfonated (polyether ether ketone) (SPEEK) with two sulfonation degrees (DS), 60 and 70%have been used. We examined both the effects of Cs-TPA in SPEEK membranes as functions of sulfonation degrees of SPEEK and the content of Cs-TPA. The performance of the composite membranes was evaluated in terms of water uptake, ion exchange capacity, proton conductivity, chemical stability, hydrolytic stability, thermal stability and methanol permeability. The morphology of the membranes was investigated with SEM micrographs. Increasing sulfonation degree of SPEEK from 60 to 70 caused agglomeration of the Cs-TPA particles. The methanol permeability was reduced to 4.7 x 10{sup -7} cm{sup 2}/s for SPEEK (DS: 60%)/Cs-TPA membrane with 10 wt.% Cs-TPA concentration, and acceptable proton conductivity of 1.3 x 10{sup -1} S/cm was achieved at 80 C under 100% RH. The weight loss at 900 C increased with the addition of inorganic particles, as expected. The hydrolytic stability of the SPEEK/Cs-TPA based composite membranes was improved with the incorporation of the Cs-TPA particles into the matrix. We also noted that SPEEK60/Cs-TPA composite membranes were hydrolytically more stable than SPEEK70/Cs-TPA composite membranes. On the other hand, Methanol, water vapor, and hydrogen permeability values of SPEEK60 composite membranes were found to be lower than that of Nafion {sup registered}. (author)

Microbial desalination cell with sulfonated sodium poly(ether ether ketone) as cation exchange membranes for enhancing power generation and salt reduction.

Science.gov (United States)

Moruno, Francisco Lopez; Rubio, Juan E; Atanassov, Plamen; Cerrato, José M; Arges, Christopher G; Santoro, Carlo

2018-06-01

Microbial desalination cell (MDC) is a bioelectrochemical system capable of oxidizing organics, generating electricity, while reducing the salinity content of brine streams. As it is designed, anion and cation exchange membranes play an important role on the selective removal of ions from the desalination chamber. In this work, sulfonated sodium (Na + ) poly(ether ether ketone) (SPEEK) cation exchange membranes (CEM) were tested in combination with quaternary ammonium chloride poly(2,6-dimethyl 1,4-phenylene oxide) (QAPPO) anion exchange membrane (AEM). Non-patterned and patterned (varying topographical features) CEMs were investigated and assessed in this work. The results were contrasted against a commercially available CEM. This work used real seawater from the Pacific Ocean in the desalination chamber. The results displayed a high desalination rate and power generation for all the membranes, with a maximum of 78.6±2.0% in salinity reduction and 235±7mWm -2 in power generation for the MDCs with the SPEEK CEM. Desalination rate and power generation achieved are higher with synthesized SPEEK membranes when compared with an available commercial CEM. An optimized combination of these types of membranes substantially improves the performances of MDC, making the system more suitable for real applications. Copyright © 2018 The Authors. Published by Elsevier B.V. All rights reserved.

Polyether ether ketone implants achieve increased bone fusion when coated with nano-sized hydroxyapatite: a histomorphometric study in rabbit bone.

Science.gov (United States)

Johansson, Pär; Jimbo, Ryo; Naito, Yoshihito; Kjellin, Per; Currie, Fredrik; Wennerberg, Ann

2016-01-01

Polyether ether ketone (PEEK) possesses excellent mechanical properties similar to those of human bone and is considered the best alternative material other than titanium for orthopedic spine and trauma implants. However, the deficient osteogenic properties and the bioinertness of PEEK limit its fields of application. The aim of this study was to limit these drawbacks by coating the surface of PEEK with nano-scaled hydroxyapatite (HA) minerals. In the study, the biological response to PEEK, with and without HA coating, was investigated. Twenty-four screw-like and apically perforated implants in the rabbit femur were histologically evaluated at 3 weeks and 12 weeks after surgery. Twelve of the 24 implants were HA coated (test), and the remaining 12 served as uncoated PEEK controls. At 3 weeks and 12 weeks, the mean bone-implant contact was higher for test compared to control (P<0.05). The bone area inside the threads was comparable in the two groups, but the perforating hole showed more bone area for the HA-coated implants at both healing points (P<0.01). With these results, we conclude that nano-sized HA coating on PEEK implants significantly improved the osteogenic properties, and in a clinical situation this material composition may serve as an implant where a rapid bone fusion is essential.

Evaluation of atmospheric solid analysis probe ionization coupled to ion mobility mass spectrometry for characterization of poly(ether ether ketone) polymers

Energy Technology Data Exchange (ETDEWEB)

Cossoul, Emilie; Hubert-Roux, Marie; Sebban, Muriel [Normandie Université, COBRA, UMR6014 and FR3038, Université de Rouen, INSA de Rouen, CNRS, IRCOF, 1 rue Tesnière, 76821 Mont-Saint-Aignan Cedex (France); Churlaud, Florence [Arkema, Centre d’Etude de Recherche et Développement, 27470 Serquigny (France); Oulyadi, Hassan [Normandie Université, COBRA, UMR6014 and FR3038, Université de Rouen, INSA de Rouen, CNRS, IRCOF, 1 rue Tesnière, 76821 Mont-Saint-Aignan Cedex (France); Afonso, Carlos, E-mail: carlos.afonso@univ-rouen.fr [Normandie Université, COBRA, UMR6014 and FR3038, Université de Rouen, INSA de Rouen, CNRS, IRCOF, 1 rue Tesnière, 76821 Mont-Saint-Aignan Cedex (France)

2015-01-26

Highlights: • Solvent free approach. • Production of intact small oligomers of PEEK with ASAP ionization. • Comparison of the MS/MS spectra from M{sup +}· and [M + H]{sup +} precursor ions. • Identification of end-groups using tandem mass spectrometry. - Abstract: Recently, the interest of the coupling between atmospheric solid analysis probe (ASAP) and ion mobility–mass spectrometry has been revealed in the field of polymers. This method associates a direct ionization technique with a bi-dimensional separation method. Poly(ether ether ketones) (PEEK) belong to the family of the poly(aryl ether ketones) (PAEK) which are high performance aromatic polymers usually used in aerospace, electronics and nuclear industries. PEEK are important commercial thermoplastics with excellent chemical resistance and good mechanical properties. Because of their low solubility, few structural characterization studies of PEEK have been reported. In mass spectrometry, only MALDI-TOF analyses for polymer synthesis monitoring have been described with the use of strong acids such as sulfuric acid. This work demonstrates that ASAP is particularly efficient for analysis of PEEK in a solvent free approach with the production of intact small oligomers (n ≤ 2). Five types of PEEK oligomers with different end-groups were evidenced. With MALDI-TOF, the same end-groups with almost the same relative abundance were obtained which support the hypothesis that the oligomers detected in ASAP are intact small oligomers and not fragments or pyrolysis products. This is particularly interesting as generally the ASAP analysis of polymers yields pyrolysis products with the loss of end-group information. The end-groups assignments have been confirmed by tandem mass spectrometry (MS/MS) experiments on the M{sup +}· molecular ions, which allowed highlighting some specific neutral or radical losses as well as two diagnostic product ions. Thus, ASAP-IM/MS/MS proves to be a fast and efficient

Computed-tomography modeled polyether ether ketone (PEEK) implants in revision cranioplasty.

Science.gov (United States)

O'Reilly, Eamon B; Barnett, Sam; Madden, Christopher; Welch, Babu; Mickey, Bruce; Rozen, Shai

2015-03-01

Traditional cranioplasty methods focus on pre-operative or intraoperative hand molding. Recently, CT-guided polyether ether ketone (PEEK) plate reconstruction enables precise, time-saving reconstruction. This case series aims to show a single institution experience with use of PEEK cranioplasty as an effective, safe, precise, reusable, and time-saving cranioplasty technique in large, complex cranial defects. We performed a 6-year retrospective review of cranioplasty procedures performed at our affiliated hospitals using PEEK implants. A total of nineteen patients underwent twenty-two cranioplasty procedures. Pre-operative, intra-operative, and post-operative data was collected. Nineteen patients underwent twenty-two procedures. Time interval from injury to loss of primary cranioplasty averaged 57.7 months (0-336 mo); 4.0 months (n=10, range 0-19) in cases of trauma. Time interval from primary cranioplasty loss to PEEK cranioplasty was 11.8 months for infection (n=11, range 6-25 mo), 12.2 months for trauma (n=5, range 2-27 mo), and 0.3 months for cosmetic or functional reconstructions (n=3, range 0-1). Similar surgical techniques were used in all patients. Drains were placed in 11/22 procedures. Varying techniques were used in skin closure, including adjacent tissue transfer (4/22) and free tissue transfer (1/22). The PEEK plate required modification in four procedures. Three patients had reoperation following PEEK plate reconstruction. Cranioplasty utilizing CT-guided PEEK plate allows easy inset, anatomic accuracy, mirror image aesthetics, simplification of complex 3D defects, and potential time savings. Additionally, it's easily manipulated in the operating room, and can be easily re-utilized in cases of intraoperative course changes or infection. Copyright © 2014 British Association of Plastic, Reconstructive and Aesthetic Surgeons. Published by Elsevier Ltd. All rights reserved.

State of the water in crosslinked sulfonated poly(ether ether ketone). Two-dimensional differential scanning calorimetry correlation mapping

Energy Technology Data Exchange (ETDEWEB)

Al Lafi, Abdul G. [Department of Chemistry, Atomic Energy Commission, Damascus, P.O. Box 6091 (Syrian Arab Republic); Hay, James N., E-mail: cscientific9@aec.org.sy [The School of Metallurgy and Materials, College of Physical Sciences and Engineering, University of Birmingham, Edgbaston, Birmingham B15 2TT (United Kingdom)

2015-07-20

Highlights: • 2D-DSC mapping was applied to analyze the heat flow responses of hydrated crosslinked sPEEK. • Two types of loosely bond water were observed. • The first was bond to the sulfonic acid groups and increased with ion exchange capacity. • The second was attributed to the polar groups introduced by ions irradiation and increased with crosslinking degree. • DSC combined with 2D mapping provides a powerful tool for polymer structural determination. - Abstract: This paper reports the first application of two-dimensional differential scanning calorimetry correlation mapping, 2D-DSC-CM to analyze the heat flow responses of sulphonated poly(ether ether ketone), sPEEK, films having different ion exchange capacity and degrees of crosslinks. With the help of high resolution and high sensitivity of 2D-DSC-CM, it was possible to locate two types of loosely bound water within the structure of crosslinked sPEEK. The first was bound to the sulfonic acid groups and dependent on the ion exchange capacity of the sPEEK. The second was bound to other polar groups, either introduced by irradiation with ions and dependent on the crosslinking degree or present in the polymer such as the carbonyl groups or terminal units. The results suggest that the ability of the sulfonic acid groups in the crosslinked sPEEK membranes to adsorb water molecules is increased by crosslinking, probably due to the better close packing efficiency of the crosslinked samples. DSC combined with 2D correlation mapping provides a fast and powerful tool for polymer structural determination.

The in vivo response to a novel Ti coating compared with polyether ether ketone: evaluation of the periphery and inner surfaces of an implant.

Science.gov (United States)

Walsh, William Robert; Pelletier, Matthew H; Christou, Chris; He, Jiawei; Vizesi, Frank; Boden, Scott D

2018-02-26

compared with PEEK. Histology showed newly formed woven bone tracked along the surface of the titanium in the apertures. The PEEK interface presented the typical nonreactive fibrous tissue inside the apertures at 4 weeks and some focal contact with bone on the outside at 4 weeks and 8 weeks. Micro-CT and histology demonstrated bone ongrowth to the surfaces coated with NM where the newly formed bone tracked along the thin titanium-coated surfaces. Polyether ether ketone surfaces presented the nonreactive fibrous tissue at the interface as previously reported in preclinical scenarios. Copyright © 2018. Published by Elsevier Inc.

Bilateral Malar Reconstruction Using Patient-Specific Polyether Ether Ketone Implants in Treacher-Collins Syndrome Patients With Absent Zygomas.

Science.gov (United States)

Sainsbury, David C G; George, Alan; Forrest, Christopher R; Phillips, John H

2017-03-01

The authors performed bilateral malar reconstruction using polyether ether ketone implants in 3 patients with Treacher-Collins syndrome with absent, as opposed to hypoplastic, zygomata. These patient-specific implants were fabricated using computed-aided design software reformatted from three-dimensional bony preoperative computed tomography images. The first time the authors performed this procedure the implant compressed the globe resulting in temporary anisocoria that was quickly recognized intraoperatively. The implant was immediately removed and the patient made a full-recovery with no ocular disturbance. The computer-aided design and manufacturing process was adjusted to include periorbital soft-tissue boundaries to aid in contouring the new implants. The same patient, and 2 further patients, subsequently underwent malar reconstruction using this soft tissue periorbital boundary fabrication process with an additional 2 mm relief removed from the implant's orbital surface. These subsequent procedures were performed without complication and with pleasing aesthetic results. The authors describe their experience and the salutary lessons learnt.

The surface modifications of multi-walled carbon nanotubes for multi-walled carbon nanotube/poly(ether ether ketone) composites

International Nuclear Information System (INIS)

Cao, Zongshuang; Qiu, Li; Yang, Yongzhen; Chen, Yongkang; Liu, Xuguang

2015-01-01

Graphical abstract: Multi-walled carbon nanotube/poly(ether ether ketone) (MWCNT/PEEK) composites incorporating surface modified multi-walled carbon nanotubes (MWCNTs) as fillers were fabricated in a solution blending method in order to explore the dynamic mechanical and tribological properties of MWCNT/PEEK composites systematically. It is evident that surface modifications of MWCNTs have a significant impact on dispersibility of MWCNTs in PEEK, dynamic mechanical and tribological properties of MWCNT/PEEK composites. Typically, a clear effect of surface modifications of MWCNTs on tribological properties of MWCNT/PEEK composites was observed. A significant reduction in frictional coefficient of MWCNT/PEEK composites with the MWCNTs modified with ethanolamine has been achieved and the self-lubricating film on their worn surfaces was also observed. - Highlights: • The dispersibility of surface modified MWCNTs in PEEK has been studied. • MWCNTs modified with ethanolamine have showed a good dispersion in PEEK. • Surface modifications of MWCNTs have a significant impact on both dynamic mechanical and tribological properties of MWCNT/PEEK composites. - Abstract: The effects of surface modifications of multi-walled carbon nanotubes (MWCNTs) on the morphology, dynamic mechanical and tribological properties of multi-walled carbon nanotube/poly(ether ether ketone) (MWCNT/PEEK) composites have been investigated. MWCNTs were treated with mixed acids to obtain acid-functionalized MWCNTs. Then the acid-functionalized MWCNTs were modified with ethanolamine (named e-MWCNTs). The MWCNT/PEEK composites were prepared by a solution-blending method. A more homogeneous distribution of e-MWCNTs within the composites was found with scanning electron microscopy. Dynamic mechanical analysis demonstrated a clear increase in the storage modulus of e-MWCNT/PEEK composites because of the improved interfacial adhesion strength between e-MWCNTs and PEEK. Furthermore, the presence of e

The surface modifications of multi-walled carbon nanotubes for multi-walled carbon nanotube/poly(ether ether ketone) composites

Energy Technology Data Exchange (ETDEWEB)

Cao, Zongshuang [Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan University of Technology, Taiyuan 030024 (China); Research Center of Advanced Material Science and Technology, Taiyuan University of Technology, Taiyuan 030024 (China); Qiu, Li [Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan University of Technology, Taiyuan 030024 (China); College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China); Yang, Yongzhen, E-mail: yyztyut@126.com [Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan University of Technology, Taiyuan 030024 (China); Research Center of Advanced Material Science and Technology, Taiyuan University of Technology, Taiyuan 030024 (China); Chen, Yongkang, E-mail: y.k.chen@herts.ac.uk [Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan University of Technology, Taiyuan 030024 (China); University of Hertfordshire, School of Engineering and Technology, Hatfield, Hertfordshire AL10 9AB (United Kingdom); Liu, Xuguang [Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan University of Technology, Taiyuan 030024 (China); College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024 (China)

2015-10-30

Graphical abstract: Multi-walled carbon nanotube/poly(ether ether ketone) (MWCNT/PEEK) composites incorporating surface modified multi-walled carbon nanotubes (MWCNTs) as fillers were fabricated in a solution blending method in order to explore the dynamic mechanical and tribological properties of MWCNT/PEEK composites systematically. It is evident that surface modifications of MWCNTs have a significant impact on dispersibility of MWCNTs in PEEK, dynamic mechanical and tribological properties of MWCNT/PEEK composites. Typically, a clear effect of surface modifications of MWCNTs on tribological properties of MWCNT/PEEK composites was observed. A significant reduction in frictional coefficient of MWCNT/PEEK composites with the MWCNTs modified with ethanolamine has been achieved and the self-lubricating film on their worn surfaces was also observed. - Highlights: • The dispersibility of surface modified MWCNTs in PEEK has been studied. • MWCNTs modified with ethanolamine have showed a good dispersion in PEEK. • Surface modifications of MWCNTs have a significant impact on both dynamic mechanical and tribological properties of MWCNT/PEEK composites. - Abstract: The effects of surface modifications of multi-walled carbon nanotubes (MWCNTs) on the morphology, dynamic mechanical and tribological properties of multi-walled carbon nanotube/poly(ether ether ketone) (MWCNT/PEEK) composites have been investigated. MWCNTs were treated with mixed acids to obtain acid-functionalized MWCNTs. Then the acid-functionalized MWCNTs were modified with ethanolamine (named e-MWCNTs). The MWCNT/PEEK composites were prepared by a solution-blending method. A more homogeneous distribution of e-MWCNTs within the composites was found with scanning electron microscopy. Dynamic mechanical analysis demonstrated a clear increase in the storage modulus of e-MWCNT/PEEK composites because of the improved interfacial adhesion strength between e-MWCNTs and PEEK. Furthermore, the presence of e

Lithium diffusion in polyether ether ketone and polyimide stimulated by in situ electron irradiation and studied by the neutron depth profiling method

Science.gov (United States)

Vacik, J.; Hnatowicz, V.; Attar, F. M. D.; Mathakari, N. L.; Dahiwale, S. S.; Dhole, S. D.; Bhoraskar, V. N.

2014-10-01

Diffusion of lithium from a LiCl aqueous solution into polyether ether ketone (PEEK) and polyimide (PI) assisted by in situ irradiation with 6.5 MeV electrons was studied by the neutron depth profiling method. The number of the Li atoms was found to be roughly proportional to the diffusion time. Regardless of the diffusion time, the measured depth profiles in PEEK exhibit a nearly exponential form, indicating achievement of a steady-state phase of a diffusion-reaction process specified in the text. The form of the profiles in PI is more complex and it depends strongly on the diffusion time. For the longer diffusion time, the profile consists of near-surface bell-shaped part due to Fickian-like diffusion and deeper exponential part.

Development and characterization of poli composites (ether ether ketone)(PEEK)(Hydroxyapatite(HA)

International Nuclear Information System (INIS)

Ferreira, V.P.; Santos, F.S.F.; Sa, M.D. de; Fook, M.V.L.

2016-01-01

The objective of this work was to develop PEEK / HA composites, combining the biological activity of the ceramic phase with the properties of the polymer phase, the materials used in this research were Poly (ether-ether-ketone) (PEEK) and Hydroxyapatite (HA) (50, 60, 70 and 80% m / v HA), this material was subjected to a load of two tons followed by a thermal treatment at 390 ° for a period of 30 minutes. Then they were characterized by FTIR, DRX and MO. In the physical-chemical characterization of FTIR and XRD, it was not possible to identify significant alterations. In the FTIR spectra of the composites, there is no formation of new identifiable chemical bonds. In the composites XRD diffractograms a profile similar to the ceramic phase was observed, with peaks increasing in intensity and narrowing proportional to the increase of the hydroxyapatite concentration in the composites. In optical microscopy it is possible to observe surfaces with heterogeneous morphology, with signs of roughness and in the cross section we observe a heterogeneous aspect, rich in regions with large agglomerates and lighter particles. Considering the processing aspects, the technique proved to be effective for the development of PEEK /HA composites. (author)

The interaction of adipose-derived human mesenchymal stem cells and polyether ether ketone.

Science.gov (United States)

Wang, Weiwei; Kratz, Karl; Behl, Marc; Yan, Wan; Liu, Yue; Xu, Xun; Baudis, Stefan; Li, Zhengdong; Kurtz, Andreas; Lendlein, Andreas; Ma, Nan

2015-01-01

Polyether ether ketone (PEEK) as a high-performance, thermoplastic implant material entered the field of medical applications due to its structural function and commercial availability. In bone tissue engineering, the combination of mesenchymal stem cells (MSCs) with PEEK implants may accelerate the bone formation and promote the osseointegration between the implant and the adjacent bone tissue. In this concept the question how PEEK influences the behaviour and functions of MSCs is of great interest. Here the cellular response of human adipose-derived MSCs to PEEK was evaluated and compared to tissue culture plate (TCP) as the reference material. Viability and morphology of cells were not altered when cultured on the PEEK film. The cells on PEEK presented a high proliferation activity in spite of a relatively lower initial cell adhesion rate. There was no significant difference on cell apoptosis and senescence between the cells on PEEK and TCP. The inflammatory cytokines and VEGF secreted by the cells on these two surfaces were at similar levels. The cells on PEEK showed up-regulated BMP2 and down-regulated BMP4 and BMP6 gene expression, whereas no conspicuous differences were observed in the committed osteoblast markers (BGLAP, COL1A1 and Runx2). With osteoinduction the cells on PEEK and TCP exhibited a similar osteogenic differentiation potential. Our results demonstrate the biofunctionality of PEEK for human MSC cultivation and differentiation. Its clinical benefits in bone tissue engineering may be achieved by combining MSCs with PEEK implants. These data may also provide useful information for further modification of PEEK with chemical or physical methods to regulate the cellular processes of MSCs and to consequently improve the efficacy of MSC-PEEK based therapies.

Wear resistance of poly(2-methacryloyloxyethyl phosphorylcholine)-grafted carbon fiber reinforced poly(ether ether ketone) liners against metal and ceramic femoral heads.

Science.gov (United States)

Yamane, Shihori; Kyomoto, Masayuki; Moro, Toru; Hashimoto, Masami; Takatori, Yoshio; Tanaka, Sakae; Ishihara, Kazuhiko

2018-04-01

Younger, active patients who undergo total hip arthroplasty (THA) have increasing needs for wider range of motion and improved stability of the joint. Therefore, bearing materials having not only higher wear resistance but also mechanical strength are required. Carbon fiber-reinforced poly(ether ether ketone) (CFR-PEEK) is known as a super engineering plastic that has great mechanical strength. In this study, we focused on poly(2-methacryloyloxyethyl phosphorylcholine) (PMPC)-grafted CFR-PEEK and investigated the effects of PMPC grafting and the femoral heads materials on the wear properties of CFR-PEEK liners. Compared with untreated CFR-PEEK, the PMPC-grafted CFR-PEEK surface revealed higher wettability and lower friction properties under aqueous circumstances. In the hip simulator wear test, wear particles generated from the PMPC-grafted CFR-PEEK liners were fewer than those of the untreated CFR-PEEK liners. There were no significant differences in the size and the morphology of the wear particles between the differences of PMPC-grafting and the counter femoral heads. Zirconia-toughened alumina (ZTA) femoral heads had significantly smoother surfaces compared to cobalt-chromium-molybdenum alloy femoral heads after the hip simulator test. Thus, we conclude that the bearing combination of the PMPC-grafted CFR-PEEK liner and ZTA head is expected to be a lifelong bearing interface in THA. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 1028-1037, 2018. © 2017 Wiley Periodicals, Inc.

Synthesis of New Polyether Ether Ketone Derivatives with Silver Binding Site and Coordination Compounds of Their Monomers with Different Silver Salts

Directory of Open Access Journals (Sweden)

Jérôme Girard

2016-05-01

Full Text Available Polyether ether ketone (PEEK is a well-known polymer used for implants and devices, especially spinal ones. To overcome the biomaterial related infection risks, 4-4′-difluorobenzophenone, the famous PEEK monomer, was modified in order to introduce binding sites for silver ions, which are well known for their antimicrobial activity. The complexation of these new monomers with different silver salts was studied. Crystal structures of different intermediates were obtained with a linear coordination between two pyridine groups and the silver ions in all cases. The mechanical and thermal properties of different new polymers were characterized. The synthesized PEEKN5 polymers showed similar properties than the PEEK ones whereas the PEEKN7 polymers showed similar thermal properties but the mechanical properties are not as good as the ones of PEEK. To improve these properties, these polymers were complexed with silver nitrate in order to “cross-link” with silver ions. The presence of ionic silver in the polymer was then confirmed by thermogravimetric analysis (TGA and X-ray powder diffraction (XRPD. Finally, a silver-based antimicrobial compound was successfully coated on the surface of PEEKN5.

Mechanical Properties Optimization of Poly-Ether-Ether-Ketone via Fused Deposition Modeling.

Science.gov (United States)

Deng, Xiaohu; Zeng, Zhi; Peng, Bei; Yan, Shuo; Ke, Wenchao

2018-01-30

Compared to the common selective laser sintering (SLS) manufacturing method, fused deposition modeling (FDM) seems to be an economical and efficient three-dimensional (3D) printing method for high temperature polymer materials in medical applications. In this work, a customized FDM system was developed for polyether-ether-ketone (PEEK) materials printing. The effects of printing speed, layer thickness, printing temperature and filling ratio on tensile properties were analyzed by the orthogonal test of four factors and three levels. Optimal tensile properties of the PEEK specimens were observed at a printing speed of 60 mm/s, layer thickness of 0.2 mm, temperature of 370 °C and filling ratio of 40%. Furthermore, the impact and bending tests were conducted under optimized conditions and the results demonstrated that the printed PEEK specimens have appropriate mechanical properties.

Poly-ethers from Winogradskyella poriferorum: Antifouling potential, time-course study of production and natural abundance

KAUST Repository

Dash, Swagatika

2011-08-01

A sponge-associated bacterium, Winogradskyella poriferorum strain UST030701-295T was cultured up to 100l for extraction of antifouling bioactive compounds. Five poly-ethers were isolated and partially characterized based on nuclear magnetic resonance (NMR) spectroscopy and mass spectrometry (MS); two of them showed inhibitory effects on biofilm formation of marine bacteria and larval settlement of macro-foulers but did not produce any adverse effects on the phenotypes of zebra fish embryos at a concentration of 5μgml -1. The effect of culture duration on the production of the poly-ethers and the bioactivity of the relevant extracts was monitored over a period of 12days. The total crude poly-ether production increased from day 2 to day 5 and the highest bioactivity was observed on day 3. The poly-ethers were found to be localized in the cellular fraction of the extracts, implying their natural occurrence. The potent bioactivity of these poly-ethers together with their high natural abundance in bacteria makes them promising candidates as ingredients in antifouling applications. © 2011 Elsevier Ltd.

Increasing the proton conductivity of sulfonated polyether ether ketone by incorporating graphene oxide: Morphology effect on proton dynamics

Science.gov (United States)

Leong, Jun Xing; Diño, Wilson Agerico; Ahmad, Azizan; Daud, Wan Ramli Wan; Kasai, Hideaki

2018-03-01

We synthesized graphene oxide-sulfonated polyether ether ketone (GO-SPEEK) composite membrane and compare its proton conductivity with that of Nafion® 117 and SPEEK membranes. From experimental measurements, we found that GO-SPEEK has better proton conductivity (σGO-SPEEK = 3.8 × 10-2 S cm-1) when compared to Nafion® 117 (σNafion = 2.4 × 10-2 S cm-1) and SPEEK (σSPEEK = 2.9 × 10-3 S cm-1). From density functional theory (DFT-) based total energy calculations, we found that GO-SPEEK has the shortest proton diffusion distance among the three membranes, yielding the highest tunneling probability. Hence, GO-SPEEK exhibits the highest conductivity. The short proton diffusion distance in GO-SPEEK, as compared to Nafion® 117 and SPEEK, can be attributed to the presence of oxygenated functional groups of GO in the polymer matrix. This also explains why GO-SPEEK requires the lowest hydration level to reach its maximum conductivity. Moreover, we have successfully shown that the proton conductivity σ is related to the tunneling probability T, i.e., σ = σ‧ exp(-1/T). We conclude that the proton diffusion distance and hydration level are the two most significant factors that determine the membrane’s good conductivity. The distance between ionic sites of the membrane should be small to obtain good conductivity. With this short distance, lower hydration level is required. Thus, a membrane with short separation between the ionic sites can have enhanced conductivity, even at low hydration conditions.

Mechanical Properties Optimization of Poly-Ether-Ether-Ketone via Fused Deposition Modeling

Directory of Open Access Journals (Sweden)

Xiaohu Deng

2018-01-01

Full Text Available Compared to the common selective laser sintering (SLS manufacturing method, fused deposition modeling (FDM seems to be an economical and efficient three-dimensional (3D printing method for high temperature polymer materials in medical applications. In this work, a customized FDM system was developed for polyether-ether-ketone (PEEK materials printing. The effects of printing speed, layer thickness, printing temperature and filling ratio on tensile properties were analyzed by the orthogonal test of four factors and three levels. Optimal tensile properties of the PEEK specimens were observed at a printing speed of 60 mm/s, layer thickness of 0.2 mm, temperature of 370 °C and filling ratio of 40%. Furthermore, the impact and bending tests were conducted under optimized conditions and the results demonstrated that the printed PEEK specimens have appropriate mechanical properties.

Sulfonated carbon black-based composite membranes for fuel cell

Indian Academy of Sciences (India)

Composite membranes were then prepared using S–C as fillers and sulfonated poly(ether ether ketone) (SPEEK) as polymer matrix with three different sulfonation degrees (DS = 60, 70 and 82%). Structure and properties of the composite membranes were characterized by FTIR, TGA, scanning electron microscopy, proton ...

Polyether ether ketone implants achieve increased bone fusion when coated with nano-sized hydroxyapatite: a histomorphometric study in rabbit bone

Directory of Open Access Journals (Sweden)

Johansson P

2016-04-01

Full Text Available Pär Johansson,1 Ryo Jimbo,1 Yoshihito Naito,2 Per Kjellin,3 Fredrik Currie,3 Ann Wennerberg1 1Department of Prosthodontics, Faculty of Odontology, Malmö University, Malmö, Sweden; 2Oral Implant Center, Tokushima University Hospital, Tokushima, Japan; 3Promimic AB, Stena Center, Göteborg, Sweden Abstract: Polyether ether ketone (PEEK possesses excellent mechanical properties similar to those of human bone and is considered the best alternative material other than titanium for orthopedic spine and trauma implants. However, the deficient osteogenic properties and the bioinertness of PEEK limit its fields of application. The aim of this study was to limit these drawbacks by coating the surface of PEEK with nano-scaled hydroxyapatite (HA minerals. In the study, the biological response to PEEK, with and without HA coating, was investigated. Twenty-four screw-like and apically perforated implants in the rabbit femur were histologically evaluated at 3 weeks and 12 weeks after surgery. Twelve of the 24 implants were HA coated (test, and the remaining 12 served as uncoated PEEK controls. At 3 weeks and 12 weeks, the mean bone–implant contact was higher for test compared to control (P<0.05. The bone area inside the threads was comparable in the two groups, but the perforating hole showed more bone area for the HA-coated implants at both healing points (P<0.01. With these results, we conclude that nano-sized HA coating on PEEK implants significantly improved the osteogenic properties, and in a clinical situation this material composition may serve as an implant where a rapid bone fusion is essential. Keywords: HA, PEEK, osseointegration, histology, orthopedics, in vivo

Mechanical properties and chemical stability of pivalolactone-based poly(ether ester)s

NARCIS (Netherlands)

Tijsma, E.J.; Tijsma, E.J.; van der Does, L.; Bantjes, A.; Bantjes, A.; Vulic, I.

1994-01-01

The processing, mechanical and chemical properties of poly(ether ester)s, prepared from pivalolactone (PVL), 1,4-butanediol (4G) and dimethyl terephthalate (DMT), were studied. The poly(ether ester)s could easily be processed by injection moulding, owing to their favourable rheological and thermal

Evaluation of crystallization kinetics of poly (ether-ketone-ketone and poly (ether-ether-ketone by DSC

Directory of Open Access Journals (Sweden)

Gibran da Cunha Vasconcelos

2010-08-01

Full Text Available The poly (aryl ether ketones are used as matrices in advanced composites with high performance due to its high thermal stability, excellent environmental performance and superior mechanical properties. Most of the physical, mechanical and thermodynamic properties of semi-crystalline polymers depend on the degree of crystallinity and morphology of the crystalline regions. Thus, a study on the crystallization process promotes a good prediction of how the manufacturing parameters affect the developed structure, and the properties of the final product. The objective of this work was to evaluate the thermoplastics polymers PEKK e PEEK by DSC, aiming to obtain the relationship between kinetics, content, nucleation and geometry of the crystalline phases, according to the parameters of the Avrami and Kissinger models. The analysis of the Avrami exponents obtained for the studied polymers indicates that both showed the formation of crystalline phases with heterogeneous nucleation and growth geometry of the type sticks or discs, depending on the cooling conditions. It was also found that the PEEK has a higher crystallinity than PEKK.

Poly(ionic liquids)-coated stainless-steel wires packed into a polyether ether ketone tube for in-tube solid-phase microextraction.

Science.gov (United States)

Feng, Juanjuan; Wang, Xiuqin; Tian, Yu; Luo, Chuannan; Sun, Min

2017-12-01

An in-tube solid-phase microextraction device was developed by packing poly(ionic liquids)-coated stainless-steel wires into a polyether ether ketone tube. An anion-exchange process was performed to enhance the extraction performance. Surface properties of poly(ionic liquids)-coated stainless-steel wires were characterized by scanning electron microscopy and energy dispersive X-ray spectrometry. The extraction device was connected to high-performance liquid chromatography equipment to build an online enrichment and analysis system. Ten polycyclic aromatic hydrocarbons were used as model analytes, and important conditions including extraction time and desorption time were optimized. The enrichment factors from 268 to 2497, linear range of 0.03-20 μg/L, detection limits of 0.010-0.020 μg/L, extraction and preparation repeatability with relative standard deviation less than 1.8 and 19%, respectively were given by the established online analysis method. It has been used to detect polycyclic aromatic hydrocarbons in environmental samples, with the relative recovery (5, 10 μg/L) in the range of 85.1-118.9%. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Effect of Polyether Ether Ketone on Therapeutic Radiation to the Spine: A Pilot Study.

Science.gov (United States)

Jackson, J Benjamin; Crimaldi, Anthony J; Peindl, Richard; Norton, H James; Anderson, William E; Patt, Joshua C

2017-01-01

Cadaveric model. To compare the effect of PEEK versus conventional implants on scatter radiation to a simulated tumor bed in the spine SUMMARY OF BACKGROUND DATA.: Given the highly vasculature nature of the spine, it is the most common place for bony metastases. After surgical treatment of a spinal metastasis, adjuvant radiation therapy is typically administered. Radiation dosing is primarily limited by toxicity to the spinal cord. The scatter effect caused by metallic implants decreases the accuracy of dosing and can unintentionally increase the effective dose seen by the spinal cord. This represents a dose-limiting factor for therapeutic radiation postoperatively. A cadaveric thorax specimen was utilized as a metastatic tumor model with two separate three-level spine constructs (one upper thoracic and one lower thoracic). Each construct was examined independently. All four groups compared included identical posterior instrumentation. The anterior constructs consisted of either: an anterior polyether ether ketone (PEEK) cage, an anterior titanium cage, an anterior bone cement cage (polymethyl methacrylate), or a control group with posterior instrumentation alone. Each construct had six thermoluminescent detectors to measure the radiation dose. The mean dose was similar across all constructs and locations. There was more variability in the upper thoracic spine irrespective of the construct type. The PEEK construct had a more uniform dose distribution with a standard deviation of 9.76. The standard deviation of the others constructs was 14.26 for the control group, 19.31 for the titanium cage, and 21.57 for the cement (polymethyl methacrylate) construct. The PEEK inter-body cage resulted in a significantly more uniform distribution of therapeutic radiation in the spine when compared with the other constructs. This may allow for the application of higher effective dosing to the tumor bed for spinal metastases without increasing spinal cord toxicity with either

Microwave sintering of poly-ether-ether-ketone (PEEK) based coatings deposited on metallic substrate

International Nuclear Information System (INIS)

Zhang, G.; Leparoux, S.; Liao, H.; Coddet, C.

2006-01-01

In this paper, the feasibility of microwave (MW) sintering PEEK (poly-ether-ether-ketone) based coatings was investigated. Three coatings were studied: pure PEEK, micron-SiC and nano-SiC particles filled (wt.10%) PEEK coatings. The results indicate that, for the two composite coatings, the SiC particles distributed in the polymer matrix, as a good MW susceptor, could be heated preferentially by MW radiation. Consequently, the polymer matrix was heated by these particles

PEEK (polyether-ether-ketone)-coated nitinol wire: Film stability for biocompatibility applications

Science.gov (United States)

Sheiko, Nataliia; Kékicheff, Patrick; Marie, Pascal; Schmutz, Marc; Jacomine, Leandro; Perrin-Schmitt, Fabienne

2016-12-01

High quality biocompatible poly-ether-ether-ketone (PEEK) coatings were produced on NiTi shape memory alloy wires using dipping deposition from colloidal aqueous PEEK dispersions after substrate surface treatment. The surface morphology and microstructure were investigated by Scanning Electron Microscopy at every step of the process from the as-received Nitinol substrate to the ultimate PEEK-coated NiTi wire. Nanoscratch tests were carried out to access the adhesive behavior of the polymer coated film to the NiTi. The results indicate that the optimum process conditions in cleaning, chemical etching, and electropolishing the NiTi, were the most important and determining parameters to be achieved. Thus, high quality PEEK coatings were obtained on NiTi wires, straight or curved (even with a U-shape) with a homogeneous microstructure along the wire length and a uniform thickness of 12 μm without any development of cracks or the presence of large voids. The biocompatibility of the PEEK coating film was checked in fibrobast cultured cells. The coating remains stable in biological environment with negligible Ni ion release, no cytotoxicity, and no delamination observed with time.

Photodegradation of poly(ether sulphone). Part 2

DEFF Research Database (Denmark)

Norrman, K.; Krebs, Frederik C

2004-01-01

The photodegradation of poly(ether sulphone) (PES) was investigated systematically by time-of-flight SIMS (ToF-SIMS) and x-ray photoelectron spectroscopy (XPS). The effect of varying the irradiation dose, wavelength and the atmosphere was studied along with mechanistic photooxidation studies using...

Characterization of a poly(ether urethane)-based controlled release membrane system for delivery of ketoprofen

International Nuclear Information System (INIS)

Macocinschi, Doina; Filip, Daniela; Vlad, Stelian; Oprea, Ana Maria; Gafitanu, Carmen Anatolia

2012-01-01

Highlights: ► Ketoprofen incorporation in poly(ether urethane) microporous membrane. ► Moisture sorption properties of as-cast membrane. ► Drug release mechanisms in function of pH and composition of membranes. - Abstract: A poly(ether urethane) based on polytetrahydrofuran containing hydroxypropyl cellulose for biomedical applications was tested for its biocompatibility. Ketoprofen was incorporated (3% and 6%) in the polyurethane matrix as an anti-inflammatory drug. Kinetic and drug release mechanisms were studied. The pore size and pore size distribution of the polyurethane membranes were investigated by scanning electron microscopy. Surface tension characteristics as well as moisture sorption properties such as diffusion coefficients and equilibrium moisture contents of the membrane material were studied. It was found that kinetics and release mechanisms are in function of medium pH, composition of polymer–drug system, pore morphology and pore size distribution. Prolonged nature of release of ketoprofen is assured by low amount of drug in polyurethane membrane and physiological pH.

Glycerol etherification with TBA: high yield to poly-ethers using a membrane assisted batch reactor.

Science.gov (United States)

Cannilla, Catia; Bonura, Giuseppe; Frusteri, Leone; Frusteri, Francesco

2014-05-20

In this work, a novel approach to obtain high yield to poly-tert-butylglycerolethers by glycerol etherification reaction with tert-butyl alcohol (TBA) is proposed. The limit of this reaction is the production of poly-ethers, which inhibits the formation of poly-ethers potentially usable in the blend with conventional diesel for transportation. The results herein reported demonstrate that the use of a water permselective membrane offers the possibility to shift the equilibrium toward the formation of poly-ethers since the water formed during reaction is continuously and selectively removed from the reaction medium by the recirculation of the gas phase. Using a proper catalyst and optimizing the reaction conditions, in a single experiment, a total glycerol conversion can be reached with a yield to poly-ethers close to 70%, which represents data never before reached using TBA as reactant. The approach here proposed could open up new opportunities for all catalytic reactions affected by water formation.

Anhydrous proton exchange membrane of sulfonated poly(ether ether ketone) enabled by polydopamine-modified silica nanoparticles

International Nuclear Information System (INIS)

Wang, Jingtao; Bai, Huijuan; Zhang, Haoqin; Zhao, Liping; Chen, Huiling; Li, Yifan

2015-01-01

Highlights: • The concept of acid/base pairs was employed to design anhydrous PEMs. • Polydopamine-modified silica particles were uniformly dispersed in SPEEK membrane. • The membranes displayed enhancement in both stability and anhydrous proton conductivity. - Abstract: Novel anhydrous proton exchange membrane is (PEM) facilely prepared by embedding dopamine-modified silica nanoparticles (DSiOis 2 ) into sulfonated poly (ether ether ketone) (SPEEK) polymer matrix. DSiO 2 bearing -NH 2 /-NH- groups are synthesized inspired by the bioadhesion principle, which are uniformly dispersed within SPEEK membrane due to the good interfacial compatibility. The interfacial electrostatic attractions render unique rearrangement of the nanophase-separated structure and the chain packing of the resultant hybrid membranes. As a result, the thermal and mechanical stabilities as well as structural stability of the hybrid membranes are enhanced when compared to SPEEK control membrane. On the other hand, induced by the attractions, acid–base pairs are formed at the SPEEK/DSiOarewere 2 interface, where fast proton transfer via Grotthuss mechanism is expected. These features confer much higher proton conductivities on the DSiO 2 -filled membranes under both hydrated and anhydrous conditions, compared to those of the SPEEK control membrane and SiO 2 -filled membranes. Particularly, the hybrid membrane with 15 wt% DSiO 2 achieve the highest conductivities of 4.52achieveachieved × 10 −3 S cm −1 at 120 °C under anhydrous condition, which is much higher than the SPEEK control membrane and the commercial Nafion membrane (0.1iswas × 10 −3 S cm −1 ). The membrane with 9 wt% DSiO 2 show an open cell potential of 0.98showshowed V and an optimum power density of 111.7 mW cm −2 , indicative of its potential application in fuel cell under anhydrous condition

Poly(ether ester amide)s for tissue engineering

NARCIS (Netherlands)

Deschamps, A.A.; van Apeldoorn, Aart A.; de Bruijn, Joost Dick; Grijpma, Dirk W.; Feijen, Jan

2003-01-01

Poly(ether ester amide) (PEEA) copolymers based on poly(ethylene glycol) (PEG), 1,4-butanediol and dimethyl-7,12-diaza-6,13-dione-1,18-octadecanedioate were evaluated as scaffold materials for tissue engineering. A PEEA copolymer based on PEG with a molecular weight of 300 g/mol and 25 wt% of soft

The failure of poly (ether ether ketone) in high speed contacts

Science.gov (United States)

Briscoe, B. J.; Stuart, B. H.; Sebastian, S.; Tweedale, P. J.

1993-04-01

The paper describes an experimental study, with an associated analysis incorporating supplementary data, of the anti-boundary lubricating action of an alkane-aliphatic carboxylic acid lubricant system in a poly (ether ether ketone)-mild steel contact. The experiments involve progressively increasing the load in a contact formed between a polymer plate and a rotating steel shaft and estimating the frictional work dissipated. Scuffing is identified when a rapid increase in frictional work is noted at a characteristic normal load. It is shown that the additive induces premature scuffing. Subsidiary data is provided using Raman spectroscopy and hardness probes, and confirms that certain additives such as decanoic acid and dodecylamine will induce surface plasticization in poly (ether ether ketone). The trends in the frictional data have been interpreted using the adhesive model of friction in conjunction with temperature-dependent interfacial theology and bulk mechanical property data. It is proposed that the scuffing process is induced prematurely as a consequence of excessive additive-induced subsurface plasticization. Restricted surface plasticization in this system provides an enhanced self-lubricating capacity.

Impaction durability of porous polyether-ether-ketone (PEEK) and titanium-coated PEEK interbody fusion devices.

Science.gov (United States)

Torstrick, F Brennan; Klosterhoff, Brett S; Westerlund, L Erik; Foley, Kevin T; Gochuico, Joanna; Lee, Christopher S D; Gall, Ken; Safranski, David L

2018-05-01

Various surface modifications, often incorporating roughened or porous surfaces, have recently been introduced to enhance osseointegration of interbody fusion devices. However, these topographical features can be vulnerable to damage during clinical impaction. Despite the potential negative impact of surface damage on clinical outcomes, current testing standards do not replicate clinically relevant impaction loading conditions. The purpose of this study was to compare the impaction durability of conventional smooth polyether-ether-ketone (PEEK) cervical interbody fusion devices with two surface-modified PEEK devices that feature either a porous structure or plasma-sprayed titanium coating. A recently developed biomechanical test method was adapted to simulate clinically relevant impaction loading conditions during cervical interbody fusion procedures. Three cervical interbody fusion devices were used in this study: smooth PEEK, plasma-sprayed titanium-coated PEEK, and porous PEEK (n=6). Following Kienle et al., devices were impacted between two polyurethane blocks mimicking vertebral bodies under a constant 200 N preload. The posterior tip of the device was placed at the entrance between the polyurethane blocks, and a guided 1-lb weight was impacted upon the anterior face with a maximum speed of 2.6 m/s to represent the strike force of a surgical mallet. Impacts were repeated until the device was fully impacted. Porous PEEK durability was assessed using micro-computed tomography (µCT) pre- and postimpaction. Titanium-coating coverage pre- and postimpaction was assessed using scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy. Changes to the surface roughness of smooth and titanium-coated devices were also evaluated. Porous PEEK and smooth PEEK devices showed minimal macroscopic signs of surface damage, whereas the titanium-coated devices exhibited substantial visible coating loss. Quantification of the porous PEEK deformation

Effects of poly-ether B on proteome and phosphoproteome expression in biofouling Balanus amphitrite cyprids

KAUST Repository

Dash, Swagatika

2012-04-01

Biofouling is ubiquitous in marine environments, and the barnacle Balanus amphitrite is one of the most recalcitrant and aggressive biofoulers in tropical waters. Several natural antifoulants that were claimed to be non-toxic have been isolated in recent years, although the mechanism by which they inhibit fouling is yet to be investigated. Poly-ether B has shown promise in the non-toxic inhibition of larval barnacle attachment. Hence, in this study, multiplex two-dimensional electrophoresis (2-DE) was applied in conjunction with mass spectrometry to investigate the effects of poly-ether B on barnacle larvae at the molecular level. The cyprid proteome response to poly-ether B treatment was analyzed at the total proteome and phosphoproteome levels, with 65 protein and 19 phosphoprotein spots found to be up- or down-regulated. The proteins were found to be related to energy-metabolism, oxidative stress, and molecular chaperones, thus indicating that poly-ether B may interfere with the redox-regulatory mechanisms governing the settlement of barnacle larvae. The results of this study demonstrate the usefulness of the proteomic technique in revealing the working mechanisms of antifouling compounds. © 2012 Copyright Taylor and Francis Group, LLC.

A study to compare the efficacy of polyether ether ketone rod device with titanium devices in posterior spinal fusion in a canine model.

Science.gov (United States)

Wang, Nanxiang; Xie, Huanxin; Xi, Chunyang; Zhang, Han; Yan, Jinglong

2017-03-09

The benefits of posterior lumbar fusion surgery with orthotopic paraspinal muscle-pediculated bone flaps are well established. However, the problem of non-union due to mechanical support is not completely resolved. The aim of the study was to compare the efficacy of polyether ether ketone (PEEK) rod device with conventional titanium devices in the posterior lumbar fusion surgery with orthotopic paraspinal muscle-pediculated bone flaps. This was a randomized controlled study with an experimental animal model. Thirty-two mongrel dogs were randomly divided into two groups-control group (n = 16), which received the titanium device and the treatment group (n = 16), which received PEEK rods. The animals were sacrificed 8 or 16 weeks after surgery. Lumbar spines of dogs in both groups were removed, harvested, and assessed for radiographic, biomechanical, and histological changes. Results in the current study indicated that there was no significant difference in the lumbar spine of the control and treatment groups in terms of radiographic, manual palpation, and gross examination. However, certain parameters of biomechanical testing showed significant differences (p < 0.05) in stiffness and displacement, revealing a better fusion (treatment group showed decreased stiffness with decreased displacement) of the bone graft. Similarly, the histological analysis also revealed a significant fusion mass in both treatment and control groups (p < 0.05). These findings revealed that fixation using PEEK connecting rod could improve the union of the bone graft in the posterior lumbar spine fusion surgery compared with that of the titanium rod fixation.

PEEK (polyether-ether-ketone)-coated nitinol wire: Film stability for biocompatibility applications

Energy Technology Data Exchange (ETDEWEB)

Sheiko, Nataliia [Institut Charles Sadron, C.N.R.S. UPR 22, Université de Strasbourg, 23 rue du Loess, BP 84047, 67034 Strasbourg Cedex 2 (France); Kékicheff, Patrick, E-mail: patrick.kekicheff@ics-cnrs.unistra.fr [Institut Charles Sadron, C.N.R.S. UPR 22, Université de Strasbourg, 23 rue du Loess, BP 84047, 67034 Strasbourg Cedex 2 (France); Marie, Pascal; Schmutz, Marc; Jacomine, Leandro [Institut Charles Sadron, C.N.R.S. UPR 22, Université de Strasbourg, 23 rue du Loess, BP 84047, 67034 Strasbourg Cedex 2 (France); Perrin-Schmitt, Fabienne [Faculté de Médecine, INSERM, UMR-S 1121, “Biomaterials and Bioengineering”, Université de Strasbourg, 11 rue Humann, 67085 Strasbourg Cedex (France)

2016-12-15

Highlights: • A thin (12 μm) homogeneous PEEK film without any defects or voids is deposited on NiTi wires. • The coating remains stable in biological environment with negligible Ni ion release and no cytotoxicity. • Large pressure (>2 GPa) can only disrupt the coating film as shown by nanoscratch tests. • Coated spring wires sustain mechanical stress in continuous cycles of axial compression/stretching for >7 million cycles. - Abstract: High quality biocompatible poly-ether-ether-ketone (PEEK) coatings were produced on NiTi shape memory alloy wires using dipping deposition from colloidal aqueous PEEK dispersions after substrate surface treatment. The surface morphology and microstructure were investigated by Scanning Electron Microscopy at every step of the process from the as-received Nitinol substrate to the ultimate PEEK-coated NiTi wire. Nanoscratch tests were carried out to access the adhesive behavior of the polymer coated film to the NiTi. The results indicate that the optimum process conditions in cleaning, chemical etching, and electropolishing the NiTi, were the most important and determining parameters to be achieved. Thus, high quality PEEK coatings were obtained on NiTi wires, straight or curved (even with a U-shape) with a homogeneous microstructure along the wire length and a uniform thickness of 12 μm without any development of cracks or the presence of large voids. The biocompatibility of the PEEK coating film was checked in fibrobast cultured cells. The coating remains stable in biological environment with negligible Ni ion release, no cytotoxicity, and no delamination observed with time.

PEEK (polyether-ether-ketone)-coated nitinol wire: Film stability for biocompatibility applications

International Nuclear Information System (INIS)

Sheiko, Nataliia; Kékicheff, Patrick; Marie, Pascal; Schmutz, Marc; Jacomine, Leandro; Perrin-Schmitt, Fabienne

2016-01-01

Highlights: • A thin (12 μm) homogeneous PEEK film without any defects or voids is deposited on NiTi wires. • The coating remains stable in biological environment with negligible Ni ion release and no cytotoxicity. • Large pressure (>2 GPa) can only disrupt the coating film as shown by nanoscratch tests. • Coated spring wires sustain mechanical stress in continuous cycles of axial compression/stretching for >7 million cycles. - Abstract: High quality biocompatible poly-ether-ether-ketone (PEEK) coatings were produced on NiTi shape memory alloy wires using dipping deposition from colloidal aqueous PEEK dispersions after substrate surface treatment. The surface morphology and microstructure were investigated by Scanning Electron Microscopy at every step of the process from the as-received Nitinol substrate to the ultimate PEEK-coated NiTi wire. Nanoscratch tests were carried out to access the adhesive behavior of the polymer coated film to the NiTi. The results indicate that the optimum process conditions in cleaning, chemical etching, and electropolishing the NiTi, were the most important and determining parameters to be achieved. Thus, high quality PEEK coatings were obtained on NiTi wires, straight or curved (even with a U-shape) with a homogeneous microstructure along the wire length and a uniform thickness of 12 μm without any development of cracks or the presence of large voids. The biocompatibility of the PEEK coating film was checked in fibrobast cultured cells. The coating remains stable in biological environment with negligible Ni ion release, no cytotoxicity, and no delamination observed with time.

A tricalcium phosphate/polyether ether ketone anchor bionic fixation device for anterior cruciate ligament reconstruction: Safety and efficacy in a beagle model.

Science.gov (United States)

Mao, Genwen; Qin, Zili; Li, Zheng; Li, Xiang; Qiu, Yusheng; Bian, Weiguo

2018-05-02

The goal of this study was to develop a bionic fixation device based on the use of a tricalcium phosphate/polyether ether ketone anchor and harvesting of the ulnar carpal flexor muscle tendon for application as a ligament graft in a beagle anterior cruciate ligament (ACL) reconstruction model, with the goal of accelerating the ligament graft-to-bone tunnel healing and providing a robust stability through exploration of this new kind of autologous ligament graft. The safety and efficacy of this fixation device were explored 3 and 6 months after surgery in a beagle ACL reconstruction model using biomechanical tests and comprehensive histological observation. The data were compared using a two-tailed Student's t test and a paired t test. A p value <0.05 was defined as statistically significant. All the models were successfully established. This fixation device possessed the excellent mechanical properties for ACL reconstruction. A comprehensive histological observation revealed that a cartilage layer was visible in the transition zone between the tendon and bone interface at both 3 and 6 months postoperation. The trabecular of the new bone was observed six months after surgery and was found to be similar to a direct connection. This fixation technique provided not only a robust primary mechanical fixation but also a bionic fixation for long-term knee joint stability by accelerating the healing of the tendon to the bone tunnel, showing a high potential for use in clinical practice. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2018. © 2018 Wiley Periodicals, Inc.

Residual stress of particulate polymer composites with reduced thermal expansion

International Nuclear Information System (INIS)

Nishino, T; Kotera, M; Sugiura, Y

2009-01-01

Thermal expansion behavior was investigated for tangusten zirconium phosphate (Zr 2 (WO 4 )(PO 4 ) 2 (ZWP)) particulate filled poly(ether ether ketone) (PEEK) composite. ZWP is known as ceramic filler with a negative thermal expansion. By incorporating ZWP with 40 volume %, the linear thermal expansion coefficient of the PEEK composite was reduced to almost same value (2.53 X 10 -5 K -1 ) with that of aluminum. This decrease was found to be quite effective for the decrease of the residual stress at the interface between aluminum plate and the composite.

Poly (ether ether ketone) membranes for fuel cells

International Nuclear Information System (INIS)

Marrero, Jacqueline C.; Gomes, Ailton de S.; Filho, Jose C.D.; Hui, Wang S.; Oliveira, Vivianna S. de

2015-01-01

Polymeric membranes were developed using a SPEEK polymer matrix (sulphonated poly (ether ether ketone)), containing hygroscopic particles of zirconia (Zr) (incorporated by sol-gel method), for use as electrolyte membranes in fuel cells. SPEEK with different sulfonation degrees were used: 63 and 86%. The thermal analysis (TGA and DSC) was carried out to characterize the membranes and electrochemical impedance spectroscopy (EIS) was carried out to evaluating the proton conductivity of the membranes. Additional analysis were underway in order to characterize these membranes, which include: X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) in order to evaluate the influence of zirconia and sulfonation degree on the properties of the membranes. (author)

Sulfonated poly(ether sulfone)s containing pyridine moiety for PEMFC.

Science.gov (United States)

Jang, Hohyoun; Islam, Md Monirul; Lim, Youngdon; Hossain, Md Awlad; Cho, Younggil; Joo, Hyunho; Kim, Whangi; Jeon, Heung-Seok

2014-10-01

Sulfonated poly(ether sulfone)s with varied degree of sulfonation (DS) were prepared via post-sulfonation of synthesized pyridine based poly(ether sulfone) (PPES) using concentrated sulfuric acid as sulfonating agent. The DS was varied with different mole ratio of 4,4'-(2,2-diphenylethenylidene)diphenol, DHTPE in the polymer unit. PPES copolymers were synthesized by direct polycondensation of pyridine unit with bis-(4-fluorophenyl)-sulfone, 4, 4'-sulfonyldiphenol and DHTPE. The structure of the resulting PPES copolymer membranes with different sulfonated units were studied by 1H NMR spectroscopy and thermogravimetric analysis (TGA). Sorption experiments were conducted to observe the interaction of sulfonated polymer with water. The ion exchange capacity (IEC) and proton conductivity were evaluated according to the increase of DS. The water uptake (WU) of the resulting membranes was in the range of 17-58%, compared to that of Nafion 211 28%. The membranes provided proton conductivities of 65-95 mS/cm in contrast to 103 mS/cm of Nafion 211.

Chemical Composition and Cytotoxic Activities of Petroleum Ether ...

African Journals Online (AJOL)

Methods: The composition of petroleum ether extract was analyzed by gas ... acids, sterides, pregnanones, terpenes, alkaloids, alkenes, alcohols, ketones, aldehydes and other compounds. .... and mass spectra with those obtained from the.

Process for making propenyl ethers and photopolymerizable compositions containing them

Science.gov (United States)

Crivello, James V.

1996-01-01

Propenyl ether monomers of formula V A(OCH.dbd.CHCH.sub.3).sub.n wherein n is an integer from one to six and A is selected from cyclic ethers, polyether and alkanes are disclosed. The monomers are readily polymerized in the presence of cationic photoinitiators, when exposed to actinic radiation, to form poly(propenyl ethers) that are useful for coatings, sealants, varnishes and adhesives. Compositions for preparing polymeric coatings comprising the compounds of formula V together with particular cationic photoinitiators are also disclosed, as are processes for making the monomers from allyl halides and readily available alcohols. The process involves rearranging the resulting allyl ethers to propenyl ethers.

In vivo and in vitro degradation of poly(ether ester) block copolymers based on poly(ethylene glycol) and poly(butylene terephthalate

NARCIS (Netherlands)

Deschamps, A.A.; van Apeldoorn, Aart A.; Hayen, H.; de Bruijn, Joost Dick; Karst, U.; Grijpma, Dirk W.; Feijen, Jan

2004-01-01

Two in vivo degradation studies were performed on segmented poly(ether ester)s based on polyethylene glycol (PEG) and poly(butylene terephthalate) (PBT) (PEOT/PBT). In a first series of experiments, the in vivo degradation of melt-pressed discs of different copolymer compositions were followed up

Composite electrolytes composed of Cs-substituted phosphotungstic acid and sulfonated poly(ether-ether ketone) for fuel cell systems

Energy Technology Data Exchange (ETDEWEB)

Oh, Song-Yul, E-mail: ms089203@tutms.tut.ac.jp [Department of Materials Science, Toyohashi University of Technology, 1-1 Hibarigaoka, Tempaku-cho, Toyohashi, Aichi 441-8580 (Japan); Yoshida, Toshihiro; Kawamura, Go [Department of Materials Science, Toyohashi University of Technology, 1-1 Hibarigaoka, Tempaku-cho, Toyohashi, Aichi 441-8580 (Japan); Muto, Hiroyuki [Department of Materials Science and Engineering, Kurume National College of Technology, 1-1-1 Komorino, Kurume, Fukuoka 830-8555 (Japan); Sakai, Mototsugu [Department of Materials Science, Toyohashi University of Technology, 1-1 Hibarigaoka, Tempaku-cho, Toyohashi, Aichi 441-8580 (Japan); Matsuda, Atsunori, E-mail: matsuda@tutms.tut.ac.jp [Department of Materials Science, Toyohashi University of Technology, 1-1 Hibarigaoka, Tempaku-cho, Toyohashi, Aichi 441-8580 (Japan)

2010-10-15

Composite electrolytes composed of cesium hydrogen sulfate containing phosphotungstic acids (CsHSO{sub 4}-H{sub 3}PW{sub 12}O{sub 40}) and sulfonated poly(ether-ether ketone) (SPEEK) were prepared by casting the corresponding precursor for application in fuel cells. Partially Cs-substituted phosphotungstic acids (Cs{sub x}H{sub 3-x}PW{sub 12}O{sub 40}) were formed in the CsHSO{sub 4}-H{sub 3}PW{sub 12}O{sub 40} system by mechanochemical treatment. SPEEK was prepared from PEEK by sulfonation using concentrated sulfuric acid. Flexible composite electrolytes were obtained and their electrochemical properties were markedly improved with the addition of Cs{sub x}H{sub 3-x}PW{sub 12}O{sub 40}, into the SPEEK matrix. A maximum power density of 213 mW cm{sup -2} was obtained from the single cell test for 50H{sub 3}PW{sub 12}O{sub 40}-50CsHSO{sub 4} in SPEEK (1/5 by weight) composite electrolyte at 80 deg. C and at 80 RH%. Electrochemical properties and transmission electron microscopy (TEM) results suggest that three-dimensional cluster particles were formed and homogeneously distributed in the SPEEK matrix. The mechanochemically synthesized Cs{sub x}H{sub 3-x}PW{sub 12}O{sub 40} incorporated into the SPEEK matrix increased the number of protonate sites in the electrolyte. The composite electrolytes were successfully formed with Cs{sub x}H{sub 3-x}PW{sub 12}O{sub 40}, which consist of hydrogen bonding between surface of inorganic solid acids and not only -HSO{sub 4}{sup -} dissociated from CsHSO{sub 4} but also -SO{sub 3}H groups in the SPEEK.

Development and characterization of poli composites (ether ether ketone)(PEEK)(Hydroxyapatite(HA); Desenvolvimento e caracterizacao de compositos poli (eter-eter-cetona)(PEEK)/Hidroxiapatita(HA)

Energy Technology Data Exchange (ETDEWEB)

Ferreira, V.P.; Santos, F.S.F.; Sa, M.D. de; Fook, M.V.L., E-mail: valeriap.ferreira@hotmail.com [Universidade Federal de Campina Grande (UFCG), PB (Brazil). Centro de Ciencias e Tecnologia. Programa de Pos-Graduacao em Ciencia e Engenharia de Materiais

2016-07-01

The objective of this work was to develop PEEK / HA composites, combining the biological activity of the ceramic phase with the properties of the polymer phase, the materials used in this research were Poly (ether-ether-ketone) (PEEK) and Hydroxyapatite (HA) (50, 60, 70 and 80% m / v HA), this material was subjected to a load of two tons followed by a thermal treatment at 390 ° for a period of 30 minutes. Then they were characterized by FTIR, DRX and MO. In the physical-chemical characterization of FTIR and XRD, it was not possible to identify significant alterations. In the FTIR spectra of the composites, there is no formation of new identifiable chemical bonds. In the composites XRD diffractograms a profile similar to the ceramic phase was observed, with peaks increasing in intensity and narrowing proportional to the increase of the hydroxyapatite concentration in the composites. In optical microscopy it is possible to observe surfaces with heterogeneous morphology, with signs of roughness and in the cross section we observe a heterogeneous aspect, rich in regions with large agglomerates and lighter particles. Considering the processing aspects, the technique proved to be effective for the development of PEEK /HA composites. (author)

Standard practice for infrared flash thermography of composite panels and repair patches used in aerospace applications

CERN Document Server

American Society for Testing and Materials. Philadelphia

2007-01-01

1.1 This practice describes a procedure for detecting subsurface flaws in composite panels and repair patches using Flash Thermography (FT), in which an infrared (IR) camera is used to detect anomalous cooling behavior of a sample surface after it has been heated with a spatially uniform light pulse from a flash lamp array. 1.2 This practice describes established FT test methods that are currently used by industry, and have demonstrated utility in quality assurance of composite structures during post-manufacturing and in-service examinations. 1.3 This practice has utility for testing of polymer composite panels and repair patches containing, but not limited to, bismaleimide, epoxy, phenolic, poly(amide imide), polybenzimidazole, polyester (thermosetting and thermoplastic), poly(ether ether ketone), poly(ether imide), polyimide (thermosetting and thermoplastic), poly(phenylene sulfide), or polysulfone matrices; and alumina, aramid, boron, carbon, glass, quartz, or silicon carbide fibers. Typical as-fabricate...

Biaxial deformation behaviour of poly-ether-ether-ketone

Science.gov (United States)

Turner, Josh; Menary, Gary; Martin, Peter

2018-05-01

The biaxial tensile properties of thin poly-ether-ether-ketone (PEEK) films are presented. Investigation into the biaxial mechanical behaviour of PEEK films will provide a preliminary insight into the anticipated stress/strain response, and potential suitability, to the possible fabrication of thin walled parts through stretch blow moulding and thermoforming processes - with the multi-axial state of strain imposed onto the heated thermoplastic sheet representative of the expected strain history experienced during these material forming processes. Following identification of the prospective forming temperature window, the biaxial mechanical behaviour of the material is characterized under differing modes of deformation, at a nominal strain rate of 1 s-1. The temperature dependence is outlined within - with an appreciable increase in flow behaviour correlated with specimen temperature exceeding its glass transition temperature (Tg).

Titanium and polyether ether ketone (PEEK) patient-specific sub-periosteal implants: two novel approaches for rehabilitation of the severely atrophic anterior maxillary ridge.

Science.gov (United States)

Mounir, M; Atef, M; Abou-Elfetouh, A; Hakam, M M

2018-05-01

The aim of this study was to assess two new protocols for single-stage rehabilitation of the severely atrophic maxillary ridge using customized porous titanium or polyether ether ketone (PEEK) sub-periosteal implants. Ten patients with a severely atrophic anterior maxillary alveolar ridge were divided randomly into two groups (five patients in each) to receive customized sub-periosteal implants fabricated via CAD/CAM technology: group 1, porous titanium implants; group 2, PEEK implants. Prosthetic loading with fixed acrylic bridges was performed 1 month postoperative. The implants were followed-up for 12 months and evaluated for the presence of any sign of radiographic bone resorption, mobility, infection, prosthetic fracture, or implant exposure. The immediate postoperative period was uneventful except for one case complicated by wound dehiscence in group 1. At 12 months, all implants were functionally stable and the patients were comfortable with the prostheses. No signs of radiographic bone resorption, mobility, infection, or prosthetic fracture were observed. Within the limitations of this study, the application of customized porous titanium and PEEK sub-periosteal implants produced through CAD/CAM technology appears to be an acceptable method for single-stage prosthetic rehabilitation of the severely atrophic edentulous anterior maxilla. This study was awarded the best case study at the academy of osseintegration annual meeting 2017, Orlando, Florida. Copyright © 2017 International Association of Oral and Maxillofacial Surgeons. Published by Elsevier Ltd. All rights reserved.

Dispersibility and chemical bonds between multi-walled carbon nanotubes and poly(ether ether ketone) in nanocomposite fibers

International Nuclear Information System (INIS)

Yanmei, Jin; Haihui, Liu; Ning, Wang; Lichen, Hou; Xing-Xiang, Zhang

2012-01-01

A series of multi-walled carbon nanotubes (MWNTs)/poly(ether ether ketone)(PEEK) nanocomposite fibers were fabricated by mixing, melt extruding PEEK with different loadings and species of MWNTs, and melt-spun the blended chips. Nanocomposite fibers were heat-stretched and heat-treated. The morphology and dispersibility of MWNTs in nanocomposite fibers were observed using a field emission environmental scanning electron microscope (FESEM) and a transmission electron microscope (TEM). The thermal and crystallization behavior of nanocomposite fibers were characterized using differential scanning calorimetry (DSC) and an X-ray diffractometer (XRD). Mechanical properties were tested using a tensile strength tester. MWNTs tend to aggregate when the loading exceeds 0.8 wt%. Functional groups on MWNTs improve the hydrophobicity and the dispersibility of MWNTs in PEEK matrix. The enhancement of mechanical properties depends on the loading and species of functional groups. The most effectively reinforced effect is in the sequence, carboxylic MWNTs (MWNT–COOH) > hydroxyl MWNTs (MWNT–OH) > MWNTs, which can be explained by the strong hydrogen bonding and the affinity between MWNT–COOH and PEEK, MWNT–OH and PEEK, and possible formation of a chemical bond between MWNT–COOH and PEEK. A nanocomposite fiber with excellent mechanical property was fabricated using 0.8 wt% MWNT–COOH as filler. The Young's modulus is 1.7 GPa; and the stress is 648 MPa. -- Highlights: ► Functional groups on MWNTs improve their hydrophobility and dispersability. ► Mechanical properties depend on the content and species of the functional groups. ► The reinforced effect is in the sequence, carboxylic MWNTs > hydroxyl MWNTs > MWNTs. ► The strength behavior was result of hydrogen bond, affinity and chemical bond. ► Dispersability of MWNTs in matrix was analyzed by calculating solubility parameter.

Poly(ether amide) segmented block copolymers with adipicacid based tetra amide segments

NARCIS (Netherlands)

Biemond, G.J.E.; Feijen, Jan; Gaymans, R.J.

2007-01-01

Poly(tetramethylene oxide)-based poly(ether ester amide)s with monodisperse tetraamide segments were synthesized. The tetraamide segment was based on adipic acid, terephthalic acid, and hexamethylenediamine. The synthesis method of the copolymers and the influence of the tetraamide concentration,

Effects of wear particles of polyether-ether-ketone and cobalt-chromium-molybdenum on CD4- and CD8-T-cell responses.

Science.gov (United States)

Du, Zhe; Wang, Shujun; Yue, Bing; Wang, Ying; Wang, You

2018-02-16

T-cells, second only to macrophages, are often considered as the potential cells involved in debris-related failure of arthroplasty. Here, we assessed the effects of particulate wear debris on T-cells and inflammatory reactions. Blood samples from 25 donors were incubated with polyether-ether-ketone (PEEK) and cobalt-chromium-molybdenum (CoCrMo) particles generated by custom cryo-milling and pulverization. The T-cell phenotypes were assessed using immunostaining and flow cytometry. For the in vivo study, 0.1 mL of each particle suspension (approximately 1.0 × 10 8 wear particles) was injected into murine knee joints; the synovium and spleen were collected one week after the operation for histological examination and immunofluorescence staining. The T-cell responses observed included low-level activation of Th1, Th2, Th17, and CD8+ pathways after 72 h of co-culture of the particles with peripheral blood mononuclear cells. Obvious CD8+ T-cell responses were observed in local synovium and peripheral spleen, with higher inflammatory cytokine expression in the CoCrMo group. Relatively minor cytotoxic and immunological reactions were observed in vitro , with PEEK and CoCrMo particle-induced immune responses being primarily mediated by CD8+ T-cells, rather than CD4+ T-cells, in vivo . Overall, PEEK wear particles induced fewer inflammatory reactions than CoCrMo particles. This study verified that PEEK was suitable as a potential alternative for metals in total knee replacements in terms of the immunological reaction to PEEK particles, and shed light on the effects of wear particles from polymer and metal-based implants on immune responses.

Influence of Layer Thickness and Raster Angle on the Mechanical Properties of 3D-Printed PEEK and a Comparative Mechanical Study between PEEK and ABS.

Science.gov (United States)

Wu, Wenzheng; Geng, Peng; Li, Guiwei; Zhao, Di; Zhang, Haibo; Zhao, Ji

2015-09-01

Fused deposition modeling (FDM) is a rapidly growing 3D printing technology. However, printing materials are restricted to acrylonitrile butadiene styrene (ABS) or poly (lactic acid) (PLA) in most Fused deposition modeling (FDM) equipment. Here, we report on a new high-performance printing material, polyether-ether-ketone (PEEK), which could surmount these shortcomings. This paper is devoted to studying the influence of layer thickness and raster angle on the mechanical properties of 3D-printed PEEK. Samples with three different layer thicknesses (200, 300 and 400 μm) and raster angles (0°, 30° and 45°) were built using a polyether-ether-ketone (PEEK) 3D printing system and their tensile, compressive and bending strengths were tested. The optimal mechanical properties of polyether-ether-ketone (PEEK) samples were found at a layer thickness of 300 μm and a raster angle of 0°. To evaluate the printing performance of polyether-ether-ketone (PEEK) samples, a comparison was made between the mechanical properties of 3D-printed polyether-ether-ketone (PEEK) and acrylonitrile butadiene styrene (ABS) parts. The results suggest that the average tensile strengths of polyether-ether-ketone (PEEK) parts were 108% higher than those for acrylonitrile butadiene styrene (ABS), and compressive strengths were 114% and bending strengths were 115%. However, the modulus of elasticity for both materials was similar. These results indicate that the mechanical properties of 3D-printed polyether-ether-ketone (PEEK) are superior to 3D-printed ABS.

Proton conductivity and fuel cell property of composite electrolyte consisting of Cs-substituted heteropoly acids and sulfonated poly(ether-ether ketone)

Energy Technology Data Exchange (ETDEWEB)

Oh, S.Y.; Yoshida, T.; Kawamura, G.; Sakai, M.; Matsuda, A. [Department of Materials Science, Toyohashi University of Technology, 1-1 Hibarigaoka, Tempaku-cho, Toyohashi, Aichi 441-8580 (Japan); Muto, H. [Department of Materials Science and Engineering, Kurume National College of Technology, 1-1-1 Komorino, Kurume, Fukuoka 830-8555 (Japan)

2010-09-15

Inorganic-organic composite electrolytes were fabricated from partially Cs{sup +}-substituted heteropoly acids (Cs-HPAs) and sulfonated poly(ether-ether ketone) (SPEEK) for application in fuel cells. Heteropoly acids, such as phosphotungstic acid (H{sub 3}PW{sub 12}O{sub 40}:WPA), and silicotungstic acid (H{sub 4}SiW{sub 12}O{sub 40}:WSiA), were mechanochemically treated with cesium hydrogen sulfate (CsHSO{sub 4}) to obtain the form of Cs-HPAs. SPEEK was prepared from PEEK by sulfonation using concentrated sulfuric acid. Water durability and surface structure of HPAs were modified by introducing Cs{sup +} into HPAs. Flexible and hot water stable composite electrolytes were obtained, and their electrochemical properties were markedly improved with the addition of Cs-HPAs into the SPEEK matrix. Maximum power densities of 245 and 247 mW cm{sup -2} were obtained for 50WPA.50CsHSO{sub 4} and 50WSiA.50CsHSO{sub 4} in SPEEK (1/5 by weight) composite electrolytes, respectively, from single cell tests at 80 C and 80 RH%. These results suggest that a three-dimensional proton-conductive path was formed among homogeneously distributed Cs-HPAs particles in the SPEEK matrix. The Cs-HPAs incorporated into the SPEEK matrix increased the number of protonate sites in the electrolyte. These observations imply that the mechanochemically synthesized Cs-HPAs, which consist of hydrogen bondings between Cs-HPAs and -HSO{sub 4}{sup -}, dissociated from CsHSO{sub 4}, are promising materials as inorganic fillers in inorganic-organic composite. (author)

Sulfonated poly(tetramethydiphenyl ether ether ketone) membranes for vanadium redox flow battery application

Energy Technology Data Exchange (ETDEWEB)

Mai, Zhensheng; Bi, Cheng; Dai, Hua [PEMFC Key Materials and Technology Laboratory, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Zhongshan Road 457, Dalian 116023 (China); Graduate University of the Chinese Academy of Sciences, Beijing 100039 (China); Zhang, Huamin; Li, Xianfeng [PEMFC Key Materials and Technology Laboratory, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Zhongshan Road 457, Dalian 116023 (China)

2011-01-01

Sulfonated poly(tetramethydiphenyl ether ether ketone) (SPEEK) with various degree of sulfonation is prepared and first used as ion exchange membrane for vanadium redox flow battery (VRB) application. The vanadium ion permeability of SPEEK40 membrane is one order of magnitude lower than that of Nafion 115 membrane. The low cost SPEEK membranes exhibit a better performance than Nafion at the same operating condition. VRB single cells with SPEEK membranes show very high energy efficiency (>84%), comparable to that of the Nafion, but at much higher columbic efficiency (>97%). In the self-discharge test, the duration of the cell with the SPEEK membrane is two times longer than that with Nafion 115. The membrane keeps a stable performance after 80-cycles charge-discharge test. (author)

Crosslinked poly(ether block amide) composite membranes for organic solvent nanofiltration applications

KAUST Repository

Aburabie, Jamaliah; Peinemann, Klaus-Viktor.

2016-01-01

Poly(ether block amide) – Pebax® – based membranes are well described for gas separation applications. But only a few publications exist for their application in pressure driven liquid applications like ultrafiltration and nanofiltration. Here we use the commercially available Pebax® 1657 for the preparation of membranes for the filtration of organic solvents. Porous polyacrylonitrile membranes were coated with Pebax® 1657 which was then crosslinked. Toluene diisocyanate (TDI) was used as a crosslinker agent for the coating. Reaction time and crosslinker concentration were optimized for the aimed application. The Pebax® coating and the impact of the TDI on the resulting crosslinked membranes were investigated by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and differential scanning calorimetry (DSC). SEM analysis shows a uniform thin coating of the PEBAX that covers the pores of the PAN membranes. FTIR and DSC analysis confirm the crosslinking reaction. Crosslinked Pebax® membranes show high stability toward ethanol propanol, acetone and even dimethylformamide (DMF). In the case of DMF applications, the standard PAN was replaced by crosslinked PAN developed in our laboratory. In order to increase the membranes permeances, graphene oxide (GO) nanosheets were incorporated in the Pebax® coating. These GO containing membranes showed strongly increased permeances for selected solvents. © 2016 Elsevier B.V.

Crosslinked poly(ether block amide) composite membranes for organic solvent nanofiltration applications

KAUST Repository

Aburabie, Jamaliah

2016-10-01

Poly(ether block amide) – Pebax® – based membranes are well described for gas separation applications. But only a few publications exist for their application in pressure driven liquid applications like ultrafiltration and nanofiltration. Here we use the commercially available Pebax® 1657 for the preparation of membranes for the filtration of organic solvents. Porous polyacrylonitrile membranes were coated with Pebax® 1657 which was then crosslinked. Toluene diisocyanate (TDI) was used as a crosslinker agent for the coating. Reaction time and crosslinker concentration were optimized for the aimed application. The Pebax® coating and the impact of the TDI on the resulting crosslinked membranes were investigated by Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM) and differential scanning calorimetry (DSC). SEM analysis shows a uniform thin coating of the PEBAX that covers the pores of the PAN membranes. FTIR and DSC analysis confirm the crosslinking reaction. Crosslinked Pebax® membranes show high stability toward ethanol propanol, acetone and even dimethylformamide (DMF). In the case of DMF applications, the standard PAN was replaced by crosslinked PAN developed in our laboratory. In order to increase the membranes permeances, graphene oxide (GO) nanosheets were incorporated in the Pebax® coating. These GO containing membranes showed strongly increased permeances for selected solvents. © 2016 Elsevier B.V.

Poly-ethers from Winogradskyella poriferorum: Antifouling potential, time-course study of production and natural abundance

KAUST Repository

Dash, Swagatika; Nogata, Yasuyuki; Zhou, Xiaojian; Zhang, Yifan; Xü , Ying; Guo, Xian Rong; Zhang, Xixiang; Qian, Peiyuan

2011-01-01

A sponge-associated bacterium, Winogradskyella poriferorum strain UST030701-295T was cultured up to 100l for extraction of antifouling bioactive compounds. Five poly-ethers were isolated and partially characterized based on nuclear magnetic

XPS investigations on the UV-laser ablation mechanism of poly(ether imide)

Energy Technology Data Exchange (ETDEWEB)

Wambach, J; Kunz, T; Schnyder, B; Koetz, R; Wokaun, A [Paul Scherrer Inst. (PSI), Villigen (Switzerland)

1999-08-01

UV-Laser ablated samples of poly(ether imide) [Kapton{sup TM}] were studied with small-spot XPS. Applying fluences above the threshold level (0.167 J/cm{sup 2}) resulted in the expected behaviour of a decline of both nitrogen and oxygen. Below the threshold level a hint for an altered ablation mechanism was found. (author) 1 fig., 5 refs.

Mechanical properties of alumina-PEEK unidirectional composite - Compression, shear, and tension

Science.gov (United States)

Kriz, R. D.; Mccolskey, J. D.

1990-01-01

An Al2O3 (alumina)-fiber composite with high strain to failure was fabricated with a thermal plastic PEEK (poly-ether-ether-ketone). The Al2O3-PEEK composite shows a marked improvement over thermally setting composite in that it absorbs 150 percent more elastic-strain energy at 76 K than at room temperature. This increase in fracture toughness at low temperatures can provide improved fatigue performance for thermal isolation straps at low temperature. Other mechanical property results suggest improvements for applications where graphite-epoxy materials are presently being used at low temperatures and where light weight is not a critical issue.

Enhanced osteoblast responses to poly ether ether ketone surface modified by water plasma immersion ion implantation.

Science.gov (United States)

Wang, Heying; Lu, Tao; Meng, Fanhao; Zhu, Hongqin; Liu, Xuanyong

2014-05-01

Poly ether ether ketone (PEEK) offers a set of characteristics superior for human implants; however, its application is limited by the bio-inert surface property. In this work, PEEK surface was modified using single step plasma immersion ion implantation (PIII) treatment with a gas mixture of water vapor as a plasma resource and argon as an ionization assistant. Field emission scanning electron microscopy, atomic force microscopy and X-ray photoelectron spectroscopy were used to investigate the microstructure and composition of the modified PEEK surface. The water contact angle and zeta-potential of the surfaces were also measured. Osteoblast precursor cells MC3T3-E1 and rat bone mesenchymal stem cells were cultured on the PEEK samples to evaluate their cytocompatibility. The obtained results show that the hydroxyl groups as well as a "ravined structure" are constructed on water PIII modified PEEK. Compared with pristine PEEK, the water PIII treated PEEK is more favorable for osteoblast adhesion, spreading and proliferation, besides, early osteogenic differentiation indicated by the alkaline phosphatase activity is also up-regulated. Our study illustrates enhanced osteoblast responses to the PEEK surface modified by water PIII, which gives positive information in terms of future biomedical applications. Copyright © 2014 Elsevier B.V. All rights reserved.

Effects of poly-ether B on proteome and phosphoproteome expression in biofouling Balanus amphitrite cyprids

KAUST Repository

Dash, Swagatika; Chandramouli, Kondethimmanahalli; Zhang, Yu; Qian, Pei Yuan

2012-01-01

in recent years, although the mechanism by which they inhibit fouling is yet to be investigated. Poly-ether B has shown promise in the non-toxic inhibition of larval barnacle attachment. Hence, in this study, multiplex two-dimensional electrophoresis (2-DE

Poly (ether ether ketone) derivatives: Synthetic route and characterization of nitrated and sulfonated polymers

International Nuclear Information System (INIS)

Conceicao, T.F.; Bertolino, J.R.; Barra, G.M.O.; Pires, A.T.N.

2009-01-01

Nitrated and sulfonated poly (ether ether ketone) [SNPEEK] samples were prepared through sulfonation of nitrated PEEK (NPEEK) at different temperatures resulting in polymers with distinct sulfonation degrees (SD). The sulfonation occurred preferentially in the hydroquinone segment even after 81% of this moiety had been nitrated. Sulfonation in the benzophenone moiety was achieved only in 16% of this segment at the reaction temperature of 80 deg. C. The substitution degree was obtained through the TG curves, and values were in agreement with 1 H NMR data when SD is much higher as ND (nitration degree). The highest SD obtained was 72%. Membranes of the sulfonated and nitrated PEEK (SNPEEK) were prepared by casting and showed good ductility depending on the substitution degree, with proton conductivity in the order of 10 -2 S cm -1 , an important characteristic in some applications, such as in fuel cells

Poly (ether ether ketone) derivatives: Synthetic route and characterization of nitrated and sulfonated polymers

Energy Technology Data Exchange (ETDEWEB)

Conceicao, T.F.; Bertolino, J.R. [Grupo de Estudo em Materiais Polimericos-Departamento de Quimica, Universidade Federal de Santa Catarina, Florianopolis, SC (Brazil); Barra, G.M.O. [Departamento de Engenharia Mecanica, Universidade Federal de Santa Catarina, Florianopolis, SC (Brazil); Pires, A.T.N. [Grupo de Estudo em Materiais Polimericos-Departamento de Quimica, Universidade Federal de Santa Catarina, Florianopolis, SC (Brazil)], E-mail: alfredotiburcio@pq.cnpq.br

2009-03-01

Nitrated and sulfonated poly (ether ether ketone) [SNPEEK] samples were prepared through sulfonation of nitrated PEEK (NPEEK) at different temperatures resulting in polymers with distinct sulfonation degrees (SD). The sulfonation occurred preferentially in the hydroquinone segment even after 81% of this moiety had been nitrated. Sulfonation in the benzophenone moiety was achieved only in 16% of this segment at the reaction temperature of 80 deg. C. The substitution degree was obtained through the TG curves, and values were in agreement with {sup 1}H NMR data when SD is much higher as ND (nitration degree). The highest SD obtained was 72%. Membranes of the sulfonated and nitrated PEEK (SNPEEK) were prepared by casting and showed good ductility depending on the substitution degree, with proton conductivity in the order of 10{sup -2} S cm{sup -1}, an important characteristic in some applications, such as in fuel cells.

Hardness and wear properties of boron-implanted poly(ether-ether-ketone) and poly-ether-imide

International Nuclear Information System (INIS)

Lee Youngchul; Lee, E.H.; Mansur, L.K.

1992-01-01

The effects of boron beam irradiation on the hardness, friction, and wear of polymer surfaces were investigated. Typical high-performance thermoplastics, poly(ether-ether-ketone) (PEEK) and a poly-ether-imide (Ultem) were studied after 200 keV boron ion beam treatment at ambient temperature to doses of 2.3x10 14 , 6.8x10 14 , and 2.2x10 15 ions cm -2 . The hardnesses of pristine and boron-implanted materials were characterized by a conventional Knoop method and a load-depth sensing nanoindentation technique. Both measurements showed a significant increase in hardness with increasing dose. The increase in hardness was also found to depend on the penetration depth of the diamond indenter. Wear and friction properties were characterized by a reciprocating sliding friction tester with an SAE 52100 high-carbon, chrome steel ball at 0.5 and 1 N normal loads. Wear and frictional properties varied in a complex fashion with polymer type and dose, but not much with normal load. A substantial reduction in friction coefficient was observed for PEEK at the highest dose but no reduction was observed for Ultem. The wear damage was substantially reduced at the highest dose for both Ultem and PEEK. For the system studied, the highest dose, 2.2x10 15 ions cm -2 , appears to be optimum in improving wear resistance for both PEEK and Ultem. (orig.)

Enhanced response of microbial fuel cell using sulfonated poly ether ether ketone membrane as a biochemical oxygen demand sensor

Energy Technology Data Exchange (ETDEWEB)

Ayyaru, Sivasankaran; Dharmalingam, Sangeetha, E-mail: sangeetha@annauniv.edu

2014-03-01

Graphical abstract: - Highlights: • Sulfonated poly ether ether ketone (SPEEK) membrane in SCMFC used to determine the BOD. • The biosensor produces a good linear relationship with the BOD concentration up to 650 ppm. • This sensing range was 62.5% higher than that of Nafion{sup ®}. • SPEEK exhibited one order lesser oxygen permeability than Nafion{sup ®}. • Nafion{sup ®} shows high anodic internal resistance (67 Ω) than the SPEEK (39 Ω). - Abstract: The present study is focused on the development of single chamber microbial fuel cell (SCMFC) using sulfonated poly ether ether ketone (SPEEK) membrane to determine the biochemical oxygen demand (BOD) matter present in artificial wastewater (AW). The biosensor produces a good linear relationship with the BOD concentration up to 650 ppm when using artificial wastewater. This sensing range was 62.5% higher than that of Nafion{sup ®}. The most serious problem in using MFC as a BOD sensor is the oxygen diffusion into the anode compartment, which consumes electrons in the anode compartment, thereby reducing the coulomb yield and reducing the electrical signal from the MFC. SPEEK exhibited one order lesser oxygen permeability than Nafion{sup ®}, resulting in low internal resistance and substrate loss, thus improving the sensing range of BOD. The system was further improved by making a double membrane electrode assembly (MEA) with an increased electrode surface area which provide high surface area for electrically active bacteria.

Tissue engineering of bovine articular cartilage within porous poly(ether ester) copolymer scaffolds with different structures

NARCIS (Netherlands)

Mahmood, Tahir A.; Shastri, V. Prasad; van Blitterswijk, Clemens; Langer, Robert; Riesle, J.U.

2005-01-01

The potential of porous poly(ether ester) scaffolds made from poly(ethylene glycol) terephthalate: poly(butylene terephthalate) (PEGT:PBT) block copolymers produced by various methods to enable cartilaginous tissue formation in vitro was studied. Scaffolds were fabricated by two different processes:

Hydrophilization of poly(ether ether ketone) films by surface-initiated atom transfer radical polymerization

DEFF Research Database (Denmark)

Fristrup, Charlotte Juel; Jankova Atanasova, Katja; Hvilsted, Søren

2010-01-01

Surface-Initiated Atom Transfer Radical Polymerization (SI-ATRP) has been exploited to hydrophilize PEEK. The ketone groups on the PEEK surface were reduced to hydroxyl groups which were converted to bromoisobutyrate initiating sites for SI-ATRP. The modification steps were followed by contact...... angle measurements and XPS. Moreover, ATR FTIR has been used to confirm the formation of initiating groups. Grafting of PEGMA from PEEK was performed in aqueous solution. The presence of the PPEGMA grafts on PEEK was revealed by the thermograms from TGA whereas investigations with AFM rejected changes...

Amphiphilic poly(ether ester amide) multiblock copolymers as biodegradable matrices for the controlled release of proteins

NARCIS (Netherlands)

Bezemer, J.M.; Oude Weme, P.; Grijpma, Dirk W.; Dijkstra, Pieter J.; van Blitterswijk, Clemens; Feijen, Jan

2000-01-01

Amphiphilic poly(ether ester amide) (PEEA) multiblock copolymers were synthesized by polycondensation in the melt from hydrophilic poly(ethylene glycol) (PEG), 1,4-dihydroxybutane and short bisester-bisamide blocks. These amide blocks were prepared by reaction of 1,4-diaminobutane with dimethyl

Synthesis and Characterization of Sulfonated Graphene Oxide Reinforced Sulfonated Poly (Ether Ether Ketone (SPEEK Composites for Proton Exchange Membrane Materials

Directory of Open Access Journals (Sweden)

Ning Cao

2018-03-01

Full Text Available As a clean energy utilization device, full cell is gaining more and more attention. Proton exchange membrane (PEM is a key component of the full cell. The commercial-sulfonated, tetrafluoroethylene-based fluoropolymer-copolymer (Nafion membrane exhibits excellent proton conductivity under a fully humidified environment. However, it also has some disadvantages in practice, such as high fuel permeability, a complex synthesis process, and high cost. To overcome these disadvantages, a low-cost and novel membrane was developed. The sulfonated poly (ether ether ketone (SPEEK was selected as the base material of the proton exchange membrane. Sulfonated graphene (SG was cross-linked with SPEEK through the elimination reaction of hydrogen bonds. It was found that the sulfonic acid groups and hydrophilic oxygen groups increased obviously in the resultant membrane. Compared with the pure SPEEK membrane, the SG-reinforced membrane exhibited better proton conductivity and methanol permeability prevention. The results indicate that the SG/SPEEK could be applied as a new proton exchange membrane in fuel cells.

Rheology and mechanics of polyether(ether)ketone - Polyetherimide blends for composites in aeronautics

Science.gov (United States)

Rosa, Mattia; Grassia, Luigi; D'Amore, Alberto; Carotenuto, Claudia; Minale, Mario

2016-05-01

In the present work rheological and mechanical properties of PEEK-PEI blends were investigated. Besides the pure components, blends with PEI concentration ranging from 10% to 90% in mass were considered. Oscillatory experiments in controlled atmosphere were conducted at different frequencies and temperatures. The frequency responses at different temperatures allowed using the TTS principle to reconstruct the master curves. All systems showed a shear thinning behavior and a flux index increasing with the percentage of PEI. The zero-shear viscosity was computed with the implementation of the Cross model and showed a decreasing behavior with the percentage of PEI. The relaxation time estimated from the crossover value of storage and loss moduli didn't change significantly with blend composition, suggesting the non-sensibility of the elasticity of the system. Lastly, tensile tests were executed to investigate the dependence of Young modulus in the different blends.

Design and synthesis of chalcone-based macrocyclic polyethers

Directory of Open Access Journals (Sweden)

Subrata Jana

2015-12-01

Full Text Available A series of chalcone-based macrocyclic ethers have been synthesized. These macrocyclic ethers contain polyether as well as extended conjugation to the benzene ring to function as fluorescent sensor for cations. The modeling studies show that the chalcone part of the receptors remains partially out of plane from the polyether part and the keto moiety of the receptors always directed outwardly in the receptor itself. This may be changed during the recognition of metal ions. The tendency of the fluorophore, to be out of plane, increases with increasing the ring size.

High-k 3D-barium titanate foam/phenolphthalein poly(ether sulfone)/cyanate ester composites with frequency-stable dielectric properties and extremely low dielectric loss under reduced concentration of ceramics

Science.gov (United States)

Zheng, Longhui; Yuan, Li; Guan, Qingbao; Liang, Guozheng; Gu, Aijuan

2018-01-01

Higher dielectric constant, lower dielectric loss and better frequency stability have been the developing trends for high dielectric constant (high-k) materials. Herein, new composites have been developed through building unique structure by using hyperbranched polysiloxane modified 3D-barium titanate foam (BTF) (BTF@HSi) as the functional fillers and phenolphthalein poly(ether sulfone) (cPES)/cyanate ester (CE) blend as the resin matrix. For BTF@HSi/cPES/CE composite with 34.1 vol% BTF, its dielectric constant at 100 Hz is as high as 162 and dielectric loss is only 0.007; moreover, the dielectric properties of BTF@HSi/cPES/CE composites exhibit excellent frequency stability. To reveal the mechanism behind these attractive performances of BTF@HSi/cPES/CE composites, three kinds of composites (BTF/CE, BTF/cPES/CE, BTF@HSi/CE) were prepared, their structure and integrated performances were intensively investigated and compared with those of BTF@HSi/cPES/CE composites. Results show that the surface modification of BTF is good for preparing composites with improved thermal stability; while introducing flexible cPES to CE is beneficial to fabricate composites with good quality through effectively blocking cracks caused by the stress concentration, and then endowing the composites with good dielectric properties at reduced concentration of ceramics.

Preparation and DMFC performance of a sulfophenylated poly(arylene ether ketone) polymer electrolyte membrane

Energy Technology Data Exchange (ETDEWEB)

Liu Baijun, E-mail: liubj@jlu.edu.c [College of Chemistry, Jilin University, Changchun 130012 (China); Hu Wei [College of Chemistry, Jilin University, Changchun 130012 (China); Kim, Yu Seung [Los Alamos National Laboratory, Electronic and Electrochemical Materials and Devices, Los Alamos, NM 87545 (United States); Zou Haifeng [College of Chemistry, Jilin University, Changchun 130012 (China); Robertson, Gilles P. [Institute for Chemical Process and Environmental Technology, National Research Council, Ottawa, Ontario K1A 0R6 (Canada); Jiang Zhenhua [College of Chemistry, Jilin University, Changchun 130012 (China); Guiver, Michael D. [Institute for Chemical Process and Environmental Technology, National Research Council, Ottawa, Ontario K1A 0R6 (Canada); Department of Energy Engineering, Hanyang University, 17 Haengdang-dong, Seongdong-gu, Seoul 133-791 (Korea, Republic of)

2010-04-15

A sulfonated poly(aryl ether ether ketone ketone) (PEEKK) having a well-defined rigid homopolymer-like chemical structure was synthesized from a readily prepared PEEKK by post-sulfonation with concentrated sulfuric acid at room temperature within several hours. The polymer electrolyte membrane (PEM) cast from the resulting polymer exhibited an excellent combination of thermal resistance, oxidative and dimensional stability, low methanol fuel permeability and high proton conductivity. Furthermore, membrane electrode assemblies (MEAs) were successfully fabricated and good direct methanol fuel cell (DMFC) performance was observed. At 2 M MeOH feed, the current density at 0.5 V reached 165 mA/cm, which outperformed our reported similarly structured analogues and MEAs derived from comparative Nafion membranes.

Preparation and characterization of poly (methyl methacrylate) and sulfonated poly (ether ether ketone) blend ultrafiltration membranes for protein separation applications

International Nuclear Information System (INIS)

Arthanareeswaran, G.; Thanikaivelan, P.; Raajenthiren, M.

2009-01-01

Poly (methyl methacrylate) (PMMA) and poly (methyl methacrylate)/sulfonated poly (ether ether ketone) (SPEEK) blend membranes were prepared by phase inversion technique in various composition using N,N'-dimethylformamide as solvent. The prepared membranes were characterized in terms of pure water flux, water content, porosity and thermal stability. The addition of SPEEK to the casting solution resulted in membranes with high pure water flux, water content, porosity and slightly low thermal stability. The cross sectional views of the blend membranes under electron microscope confirm the porosity and water flux results. The effect of the addition of SPEEK into the PMMA matrix on the extent of bovine serum albumin (BSA) separation was studied. It was found that the permeate flux increased significantly while the rejection of BSA from aqueous solution reduced moderately during ultrafiltration (UF) process. The effect was attributed to the increase in porosity and charge of the membrane due to the addition of SPEEK into the PMMA blend solution

Preliminary Investigation of Poly-Ether-Ether-Ketone Based on Fused Deposition Modeling for Medical Applications

Directory of Open Access Journals (Sweden)

Feng Zhao

2018-02-01

Full Text Available Poly-ether-ether-ketone (PEEK fabricated by fused deposition modeling for medical applications was evaluated in terms of mechanical strength and in vitro cytotoxicity in this study. Orthogonal experiments were firstly designed to investigate the significant factors on tensile strength. Nozzle temperature, platform temperature, and the filament diameter were tightly controlled for improved mechanical strength performance. These sensitive parameters affected the interlayer bonding and solid condition in the samples. Fourier transform infrared (FTIR spectrometry analysis was secondly conducted to compare the functional groups in PEEK granules, filaments, and printed parts. In vitro cytotoxicity test was carried out at last, and no toxic substances were introduced during the printing process.

Effects of atomic oxygen irradiation on the surface properties of phenolphthalein poly(ether sulfone)

International Nuclear Information System (INIS)

Pei Xianqiang; Li Yan; Wang Qihua; Sun Xiaojun

2009-01-01

To study the effects of low earth orbit environment on the surface properties of polymers, phenolphthalein poly(ether sulfone) (PES-C) blocks were irradiated by atomic oxygen in a ground-based simulation system. The surface properties of the pristine and irradiated blocks were studied by attenuated total-reflection FTIR (FTIR-ATR), X-ray photoelectron spectroscopy (XPS), scanning electron microscope (SEM). It was found that atomic oxygen irradiation induced the destruction of PES-C molecular chains, including the scission and oxidation of PES-C molecular chains, as evidenced by FTIR and XPS results. The scission of PES-C molecular chains decreased the relative concentration of C in the surface, while the oxidation increased the relative concentration of O in the surface. The changes in surface chemical structure and composition also changed the surface morphology of the block, which shifted from smooth structure before irradiation to 'carpet-like' structure after irradiation

Stress shielding and fatigue limits of poly-ether-ether-ketone dental implants.

Science.gov (United States)

Lee, Woo-Taek; Koak, Jai-Young; Lim, Young-Jun; Kim, Seong-Kyun; Kwon, Ho-Beom; Kim, Myung-Joo

2012-05-01

The poly-ether-ether-ketone (PEEK) polymer is of great interest as an alternative to titanium in orthopedics because of its biocompatibility and low elastic modulus. This study evaluated the fatigue limits of PEEK and the effects of the low elastic modulus PEEK in relation to existing dental implants. Compressive loading tests were performed with glass fiber-reinforced PEEK (GFR-PEEK), carbon fiber-reinforced PEEK (CFR-PEEK), and titanium rods. Among these tests, GFR-PEEK fatigue tests were performed according to ISO 14801. For the finite element analysis, three-dimensional models of dental implants and bone were constructed. The implants in the test groups were coated with a 0.5-mm thick and 5-mm long PEEK layer on the upper intrabony area. The strain energy densities (SED) were calculated, and the bone resorption was predicted. The fatigue limits of GFR-PEEK were 310 N and were higher than the static compressive strength of GFR-PEEK. The bone around PEEK-coated implants showed higher levels of SED than the bone in direct contact with the implants, and the wider diameter and stiffer implants showed lower levels of SED. The compressive strength of the GFR-PEEK and CFR-PEEK implants ranged within the bite force of the anterior and posterior dentitions, respectively, and the PEEK implants showed adequate fatigue limits for replacing the anterior teeth. Dental implants with PEEK coatings and PEEK implants may reduce stress shielding effects. Dental implant application of PEEK polymer-fatigue limit and stress shielding. Copyright © 2012 Wiley Periodicals, Inc.

Energetic effects of ether and ketone functional groups in 9,10-dihydroanthracene compound

International Nuclear Information System (INIS)

Freitas, Vera L.S.; Gomes, Jose R.B.; Ribeiro da Silva, Maria D.M.C.

2010-01-01

The energetic effects caused by replacing one of the methylene groups in the 9,10-dihydroanthracene by ether or ketone functional groups yielding xanthene and anthrone species, respectively, were determined from direct comparison of the standard (p o = 0.1 MPa) molar enthalpies of formation in the gaseous phase, at T = 298.15 K, of these compounds. The experimental static-bomb combustion calorimetry and Calvet microcalorimetry and the computational G3(MP2)//B3LYP method were used to get the standard molar gas-phase enthalpies of formation of xanthene, (41.8 ± 3.5) kJ . mol -1 , and anthrone, (31.4 ± 3.2) kJ . mol -1 . The enthalpic increments for the substitution of methylene by ether and ketone in the parent polycyclic compound (9,10-dihydroanthracene) are -(117.9 ± 5.5) kJ . mol -1 and -(128.3 ± 5.4) kJ . mol -1 , respectively.

Modified silyl-terminated polyether polymer blends with bisphenol A diglycidyl ether epoxy for adhesive applications

International Nuclear Information System (INIS)

Bitenieks, J; Meri, R Merijs; Zicans, J; Berzins, R; Umbraško, J; Rekners, U

2016-01-01

Modified silyl-terminated polyether polymer (MS Polymer) was blended with bisphenol A diglycidyl ether (DGEBPA) epoxy at MS Polymer/epoxy ratio from 30/70 to 70/30. MS Polymer/epoxy systems were examined for two-component adhesive formulation with additional fillers. Applicability of the MS Polymer/epoxy system at the ratio of the components 60/40 is demonstrated for the development of adhesive formulation. Rheological analysis of the components A and B shows suitable viscosity values for development of two- component adhesives formulation. Curing dynamics as well as tensile stress-strain properties and Shore A hardness of the chosen adhesive formulation are reasonable for the development of MS Polymer/epoxy type adhesive. (paper)

Biofilm behavior on sulfonated poly(ether-ether-ketone) (sPEEK)

Energy Technology Data Exchange (ETDEWEB)

Montero, Juan F.D. [Center for Research on Dental Implants (CEPID), School of Dentistry (ODT), Federal University of Santa Catarina - UFSC, Florianópolis, SC 88040-900 (Brazil); Tajiri, Henrique A.; Barra, Guilherme M.O.; Fredel, Márcio C. [Department of Mechanical Engineering (EMC), Federal University of Santa Catarina (UFSC), Florianópolis, SC 88040-900 (Brazil); Benfatti, Cesar A.M.; Magini, Ricardo S. [Center for Research on Dental Implants (CEPID), School of Dentistry (ODT), Federal University of Santa Catarina - UFSC, Florianópolis, SC 88040-900 (Brazil); Pimenta, Andréa L. [Integrated Laboratories Technologies (InteLAB), Dept. Chemical Engineering (EQA), Federal University of Santa Catarina - UFSC, Florianópolis, SC 88040-970 (Brazil); Department of Biologie, Université de Cergy Pontoise, 2, Av. Adolphe Chauvin, 95302 Cergy Pontoise (France); Souza, Júlio C.M., E-mail: julio.c.m.souza@ufsc.br [Center for Research on Dental Implants (CEPID), School of Dentistry (ODT), Federal University of Santa Catarina - UFSC, Florianópolis, SC 88040-900 (Brazil); Center for Microelectromechanical Systems (CMEMS), Dept. Mechanical Engineering (DEM), Campus Azurém, 4800-058 Guimarães (Portugal)

2017-01-01

Poly(ether-ether-ketone) (PEEK) has also shown to be very attractive for incorporating therapeutic compounds thanks to a sulfonation process which modifies the material structure resulting in a sulfonated-PEEK (sPEEK). Concerning biomedical applications, the objective of this work was to evaluate the influence of different sulfonation degree of sPEEK on the biofilm growth. PEEK samples were functionalized by using sulphuric acid (98%) and then dissolved into dimethyl-sulfoxide. A dip coating technique was used to synthesize sPEEK thin films. The sulfonation degree of the materials was analyzed by FT-IR, H NMR, TG and IEC. The surfaces were characterized by scanning electron microscopy, profilometry and contact angle analyses. Subsequently, the biofilm formation on sulfonated-PEEK based on Streptococcus mutans and Enterococcus faecalis was measured by spectrophotometry, colony forming units (CFU mL{sup −1}) and SEM. Results obtained from thermal and chemical analyses showed an intensification in sulfonation degree for sPEEK at 2 and 2.5 h. The E. faecalis or S. mutans biofilm growth revealed statistically significant differences (p < 0.05) between 2 and 3 h sulfonation groups. A significant decrease (p < 0.05) in CFU mL{sup −1} was recorded for S. mutans or E. faecalis biofilm grown on 2.5 or 3 h sPEEK. Regarding the thermal-chemical and microbiologic analyses, the sulfonation degree of sPEEK ranging from 2 up to 3 h was successful capable to decrease the biofilm growth. That revealed an alternative strategy to embed anti-biofilm and therapeutic compounds into PEEK avoiding infections in biomedical applications. - Highlights: • PEEK can be dissolved to incorporate therapeutic compounds. • High sulfonation degree on sPEEK affected the biofilm growth. • The sulfonation degree must be controlled to maintain the properties of sPEEK.

Biofilm behavior on sulfonated poly(ether-ether-ketone) (sPEEK)

International Nuclear Information System (INIS)

Montero, Juan F.D.; Tajiri, Henrique A.; Barra, Guilherme M.O.; Fredel, Márcio C.; Benfatti, Cesar A.M.; Magini, Ricardo S.; Pimenta, Andréa L.; Souza, Júlio C.M.

2017-01-01

Poly(ether-ether-ketone) (PEEK) has also shown to be very attractive for incorporating therapeutic compounds thanks to a sulfonation process which modifies the material structure resulting in a sulfonated-PEEK (sPEEK). Concerning biomedical applications, the objective of this work was to evaluate the influence of different sulfonation degree of sPEEK on the biofilm growth. PEEK samples were functionalized by using sulphuric acid (98%) and then dissolved into dimethyl-sulfoxide. A dip coating technique was used to synthesize sPEEK thin films. The sulfonation degree of the materials was analyzed by FT-IR, H NMR, TG and IEC. The surfaces were characterized by scanning electron microscopy, profilometry and contact angle analyses. Subsequently, the biofilm formation on sulfonated-PEEK based on Streptococcus mutans and Enterococcus faecalis was measured by spectrophotometry, colony forming units (CFU mL −1 ) and SEM. Results obtained from thermal and chemical analyses showed an intensification in sulfonation degree for sPEEK at 2 and 2.5 h. The E. faecalis or S. mutans biofilm growth revealed statistically significant differences (p < 0.05) between 2 and 3 h sulfonation groups. A significant decrease (p < 0.05) in CFU mL −1 was recorded for S. mutans or E. faecalis biofilm grown on 2.5 or 3 h sPEEK. Regarding the thermal-chemical and microbiologic analyses, the sulfonation degree of sPEEK ranging from 2 up to 3 h was successful capable to decrease the biofilm growth. That revealed an alternative strategy to embed anti-biofilm and therapeutic compounds into PEEK avoiding infections in biomedical applications. - Highlights: • PEEK can be dissolved to incorporate therapeutic compounds. • High sulfonation degree on sPEEK affected the biofilm growth. • The sulfonation degree must be controlled to maintain the properties of sPEEK.

In situ synthesized Li2S@porous carbon cathode for graphite/Li2S full cells using ether-based electrolyte

International Nuclear Information System (INIS)

Wang, Ning; Zhao, Naiqin; Shi, Chunsheng; Liu, Enzuo; He, Chunnian; He, Fang; Ma, Liying

2017-01-01

Graphical abstract: A facile method is proposed to prepare lithium sulfide@porous carbon composites (Li 2 S@PC) by in-situ reaction of lithium sulfate (Li 2 SO 4 ) and the pyrolytic carbon from glucose. We assembled graphite-Li 2 S@PC full-cells using the obtained Li 2 S@PC composites as the cathode, graphite as the anode and DOL/DME with LiNO 3 additive as the electrolyte. Display Omitted -- Highlights: •A simple synthesis method was proposed to form Li 2 S@porous carbon composites. •Graphite-Li 2 S full-cells were constructed in DME-based electrolyte. •A novel method was proposed to activate the full cells. -- Abstract: Lithium-sulfur (Li-S) batteries have been recognized as one of the promising next-generation energy storage devices owing to their high energy density, low cost and eco-friendliness. As for cathode’s performance, the main challenges for developing highly-efficient and long-life Li-S batteries are to retard the polysulfides diffusion into electrolyte and the reaction with metallic lithium (Li). Especially, the safety issues, derived from metallic Li in anode, must be overcome. Herein, we fabricated lithium sulfide@porous carbon composites (Li 2 S@PC) by an in-situ reaction between the lithium sulfate (Li 2 SO 4 ) and the pyrolytic carbon from glucose. The nanosized Li 2 S particles were uniformly distributed in the carbon matrix, which not only significantly improve electronic conductivity of the electrode but also effectively trap the dissolved polysulfides. Furthermore, on the basis of the graphite’s electrochemical features in ether-based electrolyte, we assembled graphite-Li 2 S@PC full cells using the obtained Li 2 S@PC composites as the cathode, graphite as the anode and the DOL/DME with LiNO 3 additive as the electrolyte. A unique strategy was proposed to activate the full-cells in descending order using constant voltage and current to charge the cut-off voltage. This Li-S full cell exhibits stable cycling performance at 0.5 C over

Novel sulfonated poly (ether ether keton)/polyetherimide acid-base blend membranes for vanadium redox flow battery applications

International Nuclear Information System (INIS)

Liu, Shuai; Wang, Lihua; Ding, Yue; Liu, Biqian; Han, Xutong; Song, Yanlin

2014-01-01

Highlights: • SPEEK/PEI acid-base blend membranes are prepared for VRB applications. • The acid-base blend membranes have much lower vanadium ion permeability. • The energy efficiency of SPEEK/PEI maintain around 86.9% after 50 cycles. - Abstract: Novel acid-base blend membranes composed of sulfonated poly (ether ether ketone) (SPEEK) and polyetherimide (PEI) were prepared for vanadium redox flow battery (VRB). The blend membranes were characterized by Fourier transform infrared spectroscopy (FT-IR) and scanning electronic microscopy (SEM). The ion exchange capacity (IEC), proton conductivity, water uptake, vanadium ion permeability and mechanical properties were measured. As a result, the acid-base blend membranes exhibit higher water uptake, IEC and lower vanadium ion permeability compared to Nafion117 membranes and all these properties decrease with the increase of PEI. In VRB single cell test, the VRB with blend membranes shows lower charge capacity loss, higher coulombic efficiency (CE) and energy efficiency (EE) than Nafion117 membrane. Furthermore, the acid-base blend membranes present stable performance up to 50 cycles with no significant decline in CE and EE. All experimental results indicate that the SPEEK/PEI (S/P) acid-base blend membranes show promising prospects for VRB

Enhanced osteogenic activity of poly ether ether ketone using calcium plasma immersion ion implantation.

Science.gov (United States)

Lu, Tao; Qian, Shi; Meng, Fanhao; Ning, Congqin; Liu, Xuanyong

2016-06-01

As a promising implantable material, poly ether ether ketone (PEEK) possesses similar elastic modulus to that of cortical bones yet suffers from bio-inertness and poor osteogenic properties, which limits its application as orthopedic implants. In this work, calcium is introduced onto PEEK surface using calcium plasma immersion ion implantation (Ca-PIII). The results obtained from scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) confirm the modified layer with varying contents of calcium are formed on PEEK surfaces. Water contact angle measurements reveal the increasing hydrophobicity of both Ca-PIII treated surfaces. In vitro cell adhesion, viability assay, alkaline phosphatase activity and collagen secretion analyses disclose improved the adhesion, proliferation, and osteo-differentiation of rat bone mesenchymal stem cells (bMSCs) on Ca-PIII treated surfaces. The obtained results indicate that PEEK surface with enhanced osteogenic activity can be produced by calcium incorporation. Copyright © 2016 Elsevier B.V. All rights reserved.

Treatment of two different water resources in desalination and microbial fuel cell processes by poly sulfone/Sulfonated poly ether ether ketone hybrid membrane

International Nuclear Information System (INIS)

Ghasemi, Mostafa; Wan Daud, Wan Ramli; Alam, Javed; Ilbeygi, Hamid; Sedighi, Mehdi; Ismail, Ahmad Fauzi; Yazdi, Mohammad H.; Aljlil, Saad A.

2016-01-01

The PS (Polysulfone)/SPEEK (sulfonated poly ether ether ketone) hybrid membranes were fabricated and modified with low and high DS (degrees of sulfonation) for the desalination of brackish water and proton exchange membrane in microbial fuel cell. The results illustrated that SPEEK has changed the morphology of membranes and increase their hydrophilicity. PS/SPEEK with lower DS (29%) had the rejection percentage of 62% for NaCl and 68% for MgSO_4; while it was 67% and 81% for PS/SPEEK (76%) at 4 bars. Furthermore, the water flux for PS at 10 bar was 12.41 L m"−"2 h"−"1. It was four times higher for PS/SPEEK (29%) which means 49.5 L m"−"2 h"−"1 and 13 times higher for PS/SPEEK (76%) with means 157.76 L m"−"2 h"−"1. However, in MFC (microbial fuel cell), the highest power production was 97.47 mW/m"2 by PS/SPEEK (29%) followed by 41.42 mW/m"2 for PS/SPEEK (76%), and 9.4 mW/m"2 for PS. This revealed that the sulfonation of PEEK (poly ether ether ketone) made it a better additive for PS for desalination, because it created a membrane with higher hydrophilicity, better pore size and better for salt rejection. Although for the separator, the degree of sulfonation was limited; otherwise it made a membrane to transfer some of the unwanted ions. - Highlights: • Fabrication of a composite membrane for desalination and MFC. • PS/SPEEK (76%) had the lowest contact angle (48.8) and highest hydrophilicity than PS and PS/SPEEK (29%). • PS/SPEEK (29%) was the best separator for use in MFC. • PS/SPEEK (76%) had the highest flux (61.3 L m"−"2 h"−"1) for desalination.

Structuring of poly ether ether ketone by ArF excimer laser radiation in different atmospheres

International Nuclear Information System (INIS)

Feng, Y.; Gottmann, J.; Kreutz, E.W.

2003-01-01

Structuring of poly ether ether ketone (PEEK) by 193 nm ArF excimer laser radiation has been investigated. Experiments were carried out in different atmospheres (air, vacuum, Ar, O 2 ) in order to study its influence on the quality of the structures and the formation of the debris. Repetition rate makes little effect on the ablation rate and roughness of the structure in presence of any kind of atmosphere, indicating for the structuring of PEEK by ArF laser radiation a large window of processing. The roughness at the bottom of the structures and the morphology of the side walls are strongly affected by the properties of the atmosphere. The smallest roughness is achieved at 0.6 J/cm 2 for all kinds of processing gases. Debris around the structures can be diminished by structuring in vacuum. Plasma expansion speed has been measured by using high speed photography

Investigation of phonon transport and thermal boundary conductance at the interface of functionalized SWCNT and poly (ether-ketone)

Energy Technology Data Exchange (ETDEWEB)

Huang, Haoxiang; Kumar, Satish, E-mail: satish.kumar@me.gatech.edu [G.W. Woodruff School of Mechanical Engineering, Georgia Institute of Technology, Atlanta, Georgia 30332 (United States); Chen, Liang [School of Energy and Power Engineering, Xi' an Jiaotong University, Xi' an, Shaanxi (China); Varshney, Vikas [Materials and Manufacturing Directorate, Air Force Research Laboratory, Wright-Patterson Air Force Base, Dayton, Ohio 45433 (United States); Universal Technology Corporation, Dayton, Ohio 45432 (United States); Roy, Ajit K. [Materials and Manufacturing Directorate, Air Force Research Laboratory, Wright-Patterson Air Force Base, Dayton, Ohio 45433 (United States)

2016-09-07

Carbon nanostructures such as carbon nanotube (CNT), graphene, and carbon fibers can be used as fillers in amorphous polymers to improve their thermal properties. In this study, the effect of covalent bonding of CNT with poly(ether ketone) (PEK) on interfacial thermal interactions is investigated using non-equilibrium molecular dynamics simulations. The number of covalent bonds between (20, 20) CNT and PEK is varied in the range of 0–80 (0%–6.25%), and the thermal boundary conductance is computed. The analysis reveals that covalent functionalization of CNT atoms can enhance the thermal boundary conductance by an order of magnitude compared to the non-functionalized CNT-PEK interface at a high degree of CNT functionalization. Besides strengthening the thermal coupling, covalent functionalization is also shown to modify the phonon spectra of CNT. The transient spectral energy analysis shows that the crosslinks cause faster energy exchange from CNT to PEK in different frequency bands. The oxygen atom of hydroxyl group of PEK contributes energy transfer in the low frequency band, while aromatic and carbonyl carbon atoms play a more significant role in high frequency bands. In addition, by analyzing the relaxation time of the spectral temperature of different frequency bands of CNT, it is revealed that with increasing number of bonds, both lower frequency vibrational modes and higher frequency modes efficiently couple across the CNT-PEK interface and contribute in thermal energy transfer from CNT to the matrix.

Graft-crosslinked copolymers based on poly(arylene ether ketone)-gc-sulfonated poly(arylene ether sulfone) for PEMFC applications.

Science.gov (United States)

Zhang, Xuan; Hu, Zhaoxia; Luo, Linqiang; Chen, Shanshan; Liu, Jianmei; Chen, Shouwen; Wang, Lianjun

2011-07-15

Novel poly(arylene ether ketone) polymers with fluorophenyl pendants and phenoxide-terminated wholly sulfonated poly(arylene ether sulfone) oligomers are prepared via Ni(0)-catalyzed and nucleophilic polymerization, respectively, and subsequently used as starting materials to obtain graft-crosslinked membranes as polymer electrolyte membranes. The phenoxide-terminated sulfonated moieties are introduced as hydrophilic parts as well as crosslinking units. The chemical structure and morphology of the obtained membranes are confirmed by (1) H NMR and tapping-mode AFM. The properties required for fuel cell applications, including water uptake and dimensional change, as well as proton conductivity, are investigated. AFM results show a clear nanoscale phase-separation microstructure of the obtained membranes. The membranes show good dimensional stability and reasonably high proton conductivities under 30-90% relative humidity. The anisotropic proton conductivity ratios (σ(formula see text) ) of the membranes in water are in the range 0.65-0.92, and increase with an increase in hydrophilic block length. The results indicate that the graft-crosslinked membranes are promising candidates for applications as polymer electrolyte membranes. Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Interaction of thrombocytes with poly(ether imide): The influence of processing.

Science.gov (United States)

Braune, S; Lange, M; Richau, K; Lützow, K; Weigel, T; Jung, F; Lendlein, A

2010-01-01

The processing of polymers for blood contacting devices can have a major influence on surface properties. In this study, we fabricated poly(ether imide) (PEI) membranes and films to investigate the effects of the processing on physicochemical surface properties by atomic force microscopy (AFM), scanning electron microscopy, contact angle as well as zeta potential measurements. A static platelet adhesion test was performed to analyze the thrombogenicity of both devices. While contact angle measurements showed similar levels of hydrophobicity and zeta potential values were equivalent, mean surface roughness as well as surface energies in the dispersive part were found to be increased for the PEI membrane. The static platelet adhesion test showed a significantly decreased number of adherent platelets per surface area on the PEI film (178.98 ± 102.70/45000 μm2) compared to the PEI membrane (504 ± 314.27/45000μm2) and, consequently, revealed evidence for higher thrombogenicity of the PEI membrane. This study shows that processing can have a significant effect on platelet adhesion to biomaterials, even though, molar weight was identical. Thrombogenicity of polymer-based cardiovascular devices, therefore, have to be evaluated at the final product level, following the entire processing procedure.

On the PEEK composites reinforced by surface-modified nano-silica

International Nuclear Information System (INIS)

Lai, Y.H.; Kuo, M.C.; Huang, J.C.; Chen, M.

2007-01-01

The nano-sized silica fillers reinforced poly(ether ether ketone) (PEEK) composites were fabricated by means of compression molding technique. The nano-sized silica, measuring 30 nm in size, was firstly modified by surface pretreatment with stearic acid. The performances and properties of the resulting PEEK/SiO 2 nanocomposites were examined in terms of tensile loading, hardness, dynamic mechanical analysis (DMA), thermomechanical analysis (TMA), thermogravimetry analysis (TGA), differential scanning calorimetry (DSC), X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The modified nano-silica was seen to disperse more uniformly than the unmodified counterpart. The XRD patterns of the modified silica reinforced PEEK composites reveal a systematic shift toward higher angles, suggesting the smaller d-spacing of the PEEK crystallites. The coefficient of thermal expansion (CTE) becomes lowered when the content of the nano-silica increases. Furthermore, the CTE of the modified silica filled PEEK nanocomposites shows the higher CTE values. A logic model is proposed. The increment of the dynamic modulus for the PEEK nanocomposites is up to 40% at elevated temperatures from 100 to 250 deg. C, indicating the apparent improvement of elevated temperature mechanical properties

Quantitative radiographic analysis of fiber reinforced polymer composites.

Science.gov (United States)

Baidya, K P; Ramakrishna, S; Rahman, M; Ritchie, A

2001-01-01

X-ray radiographic examination of the bone fracture healing process is a widely used method in the treatment and management of patients. Medical devices made of metallic alloys reportedly produce considerable artifacts that make the interpretation of radiographs difficult. Fiber reinforced polymer composite materials have been proposed to replace metallic alloys in certain medical devices because of their radiolucency, light weight, and tailorable mechanical properties. The primary objective of this paper is to provide a comparable radiographic analysis of different fiber reinforced polymer composites that are considered suitable for biomedical applications. Composite materials investigated consist of glass, aramid (Kevlar-29), and carbon reinforcement fibers, and epoxy and polyether-ether-ketone (PEEK) matrices. The total mass attenuation coefficient of each material was measured using clinical X-rays (50 kev). The carbon fiber reinforced composites were found to be more radiolucent than the glass and kevlar fiber reinforced composites.

Poly (ether ether ketone) membranes for fuel cells; Membranas de poli (eter eter cetona) sulfonado para celulas a combustivel

Energy Technology Data Exchange (ETDEWEB)

Marrero, Jacqueline C.; Gomes, Ailton de S.; Filho, Jose C.D., E-mail: jacquecosta@gmail.com [Universidade Federal do Rio de Janeiro (UFRJ), Rio de Janeiro, RJ (Brazil); Hui, Wang S. [Universidade de Sao Paulo (USP), Sao Paulo, SP (Brazil); Oliveira, Vivianna S. de [Escola Tecnica Rezende-Rammel, Rio de Janeiro, RJ (Brazil)

2015-07-01

Polymeric membranes were developed using a SPEEK polymer matrix (sulphonated poly (ether ether ketone)), containing hygroscopic particles of zirconia (Zr) (incorporated by sol-gel method), for use as electrolyte membranes in fuel cells. SPEEK with different sulfonation degrees were used: 63 and 86%. The thermal analysis (TGA and DSC) was carried out to characterize the membranes and electrochemical impedance spectroscopy (EIS) was carried out to evaluating the proton conductivity of the membranes. Additional analysis were underway in order to characterize these membranes, which include: X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) in order to evaluate the influence of zirconia and sulfonation degree on the properties of the membranes. (author)

Synthesis and Properties of Poly(ether sulfone)s with Clustered Sulfonic Groups for PEMFC Applications under Various Relative Humidity.

Science.gov (United States)

Lee, Shih-Wei; Chen, Jyh-Chien; Wu, Jin-An; Chen, Kuei-Hsien

2017-03-22

Novel sulfonated poly(ether sulfone) copolymers (S4PH-x-PSs) based on a new aromatic diol containing four phenyl substituents at the 2, 2', 6, and 6' positions of 4,4'-diphenyl ether were synthesized. Sulfonation was found to occur exclusively on the 4 position of phenyl substituents by NMR spectroscopy. The ion exchange capacity (IEC) values can be controlled by adjusting the mole percent (x in S4PH-x-PS) of the new diol. The fully hydrated sulfonated poly(ether sulfone) copolymers had good proton conductivity in the range 0.004-0.110 S/cm at room temperature. The surface morphology of S4PH-x-PSs and Nafion 212 was investigated by atomic force microscopy (tapping-mode) and related to the percolation limit and proton conductivity. Single H 2 /O 2 fuel cell based on S4PH-40-PS loaded with 0.25 mg/cm 2 catalyst (Pt/C) exhibited a peak power density of 462.6 mW/cm 2 , which was close to that of Nafion 212 (533.5 mW/cm 2 ) at 80 °C with 80% RH. Furthermore, fuel cell performance of S4PH-35-PS with various relative humidity was investigated. It was confirmed from polarization curves that the fuel cell performance of S4PH-35-PS was not as high as that of Nafion 212 under fully hydrated state due to higher interfacial resistance between S4PH-35-PS and electrodes. While under low relative humidity (53% RH) at 80 °C, fuel cells based on S4PH-35-PS showed higher peak power density (234.9 mW/cm 2 ) than that (214.0 mW/cm 2 ) of Nafion 212.

Identification of Important Process Variables for Fiber Spinning of Protein Nanotubes Generated from Waste Materials

Science.gov (United States)

2012-01-11

PEEK Polyether ether ketone POM Polarized optical microscopy PT Phosphate-Tris (spinning buffer) SDS-PAGE Sodium dodecyl sulfate...the form of a gas such as water, ammonia, carbon monoxide, hydrogen cyanide , carbon dioxide and nitrogen. Carbonization is carried out at... steel . Therefore, spider silk fibers possess the desirable mechanical properties for lightweight, high-performance fiber, and composite applications

Preparation and characterization of electrospun poly(phthalazinone ether nitrile ketone) membrane with novel thermally stable properties

Energy Technology Data Exchange (ETDEWEB)

Wang, Gang; Zhang, Hao; Qian, Bingqing [Carbon Research Laboratory, Liaoning Key Lab for Energy Materials and Chemical Engineering, State Key Lab of Fine Chemicals, Dalian University of Technology, Dalian 116024 (China); Wang, Jinyan, E-mail: wangjinyan@dlut.edu.cn [Department of Polymer Science and Materials, Dalian University of Technology, Dalian 116024 (China); Jian, Xigao [Department of Polymer Science and Materials, Dalian University of Technology, Dalian 116024 (China); Qiu, Jieshan, E-mail: jqiu@dlut.edu.cn [Carbon Research Laboratory, Liaoning Key Lab for Energy Materials and Chemical Engineering, State Key Lab of Fine Chemicals, Dalian University of Technology, Dalian 116024 (China)

2015-10-01

Highlights: • Poly (phthalazinone ether nitrile ketone) (PPENK) was used to successfully prepare nanofiber membranes by electrospinning. • Electrospun membrane exhibits a good thermostability. • Electrospun membrane. - Abstract: Electrospun nanofibrous membranes have several applications because of their excellent properties, such as high porosity, small fiber diameter, and large surface area. However, high-temperature resistant electrospun membranes remain a challenge because of the absence of precursors that offer spinnability, scalability, and superior thermal stability. In this study, poly(phthalazinone ether nitrile ketone) (PPENK) was used to successfully prepare nanofiber membranes by electrospinning. Electrospun PPENK membranes were characterized by scanning electron microscopy, differential scanning calorimetry, Fourier transform infrared spectroscopy, and tensile stress–strain tests. Results indicated that the prepared electrospun membranes had a very high glass transition temperature, superior chemical resistance, and excellent mechanical strength. These desirable properties broaden their potential application in membranes and treatment of various hot fluid streams without strict temperature control.

Novel sulfonated poly (ether ether ketone)/phosphonic acid-functionalized titania nanohybrid membrane by an in situ method for direct methanol fuel cells

Science.gov (United States)

Wu, Hong; Cao, Ying; Li, Zhen; He, Guangwei; Jiang, Zhongyi

2015-01-01

Sulfonated poly (ether ether ketone)/phosphonic acid-functionalized titania nanohybrid membranes are prepared by an in situ method using titanium tetrachloride (TiCl4) as inorganic precursor and amino trimethylene phosphonic acid (ATMP) as modifier. Phosphonic acid-functionalized titania nanoparticles with a uniform particle size of ∼50 nm are formed and dispersed homogeneously in the SPEEK matrix with good interfacial compatibility. Accordingly, the nanohybrid membranes display remarkably enhanced proton conduction property due to the incorporation of additional sites for proton transport and the formation of well-connected channels by bridging the hydrophilic domains in SPEEK matrix. The nanohybrid membrane with 6 wt. % of phosphonic acid-functionalized titania nanoparticles exhibits the highest proton conductivity of 0.334 S cm-1 at 65 °C and 100% RH, which is 63.7% higher than that of pristine SPEEK membrane. Furthermore, the as-prepared nanohybrid membranes also show elevated thermal and mechanical stabilities as well as decreased methanol permeability.

Anti-fouling behavior of hyperbranched polyglycerol-grafted poly(ether sulfone) hollow fiber membranes for osmotic power generation.

Science.gov (United States)

Li, Xue; Cai, Tao; Chung, Tai-Shung

2014-08-19

To sustain high performance of osmotic power generation by pressure-retarded osmosis (PRO) processes, fouling on PRO membranes must be mitigated. This is especially true for the porous support of PRO membranes because its porous structure is very prone to fouling by feeding river water. For the first time, we have successfully designed antifouling PRO thin-film composite (TFC) membranes by synthesizing a dendritic hydrophilic polymer with well-controlled grafting sites, hyperbranched polyglycerol (HPG), and then grafting it on poly(ether sulfone) (PES) hollow fiber membrane supports. Compared to the pristine PES membranes, polydopamine modified membranes, and conventional poly(ethylene glycol) (PEG)-grafted membranes, the HPG grafted membranes show much superior fouling resistance against bovine serum albumin (BSA) adsorption, E. coli adhesion, and S. aureus attachment. In high-pressure PRO tests, the PES TFC membranes are badly fouled by model protein foulants, causing a water flux decline of 31%. In comparison, the PES TFC membrane grafted by HPG not only has an inherently higher water flux and a higher power density but also exhibits better flux recovery up to 94% after cleaning and hydraulic pressure impulsion. Clearly, by grafting the properly designed dendritic polymers to the membrane support, one may substantially sustain PRO hollow fiber membranes for power generation.

Metal/graphite-composite materials for fusion device

International Nuclear Information System (INIS)

Kneringer, G.; Kny, E.; Fischer, W.; Reheis, N.; Staffler, R.; Samm, U.; Winter, J.

1995-01-01

The utilization of graphite as a structural material depends to an important extent on the availability of a joining technique suitable for the production of reliable large scale metal/graphite-composites. This study has been conducted to evaluate vacuum brazes and procedures for graphite and metals which can be used in fusion applications up to about 1500 degree C. The braze materials included: AgCuTi, CuTi, NiTi, Ti, ZrTi, Zr. Brazing temperatures ranged from 850 degree C to 1900 degree C. The influence of graphite quality on wettability and pore-penetration of the braze has been investigated. Screening tests of metal/graphite-assemblies with joint areas exceeding some square-centimeters have shown that they can only successfully be produced when graphite is brazed to a metal, such as tungsten or molybdenum with a coefficient of thermal expansion closely matching that of graphite. Therefore all experimental work on evaluation of joints has been concentrated on molybdenum/graphite brazings. The tensile strength of molybdenum/graphite-composites compares favorably with the tensile strength of bulk graphite from room temperature close to the melting temperature of the braze. In electron beam testing the threshold damage line for molybdenum/graphite-composites has been evaluated. Results show that even composites with the low melting AgCuTi-braze are expected to withstand 10 MW/m 2 power density for at least 10 3 cycles. Limiter testing in TEXTOR shows that molybdenum/graphite-segments with 3 mm graphite brazed on molybdenum-substrate withstand severe repeated TEXTOR plasma discharge conditions without serious damage. Results prove that actively cooled components on the basis of a molybdenum/graphite-composite can sustain a higher heat flux than bulk graphite alone. (author)

Epoxide hydrolase-lasalocid a structure provides mechanistic insight into polyether natural product biosynthesis.

Science.gov (United States)

Wong, Fong T; Hotta, Kinya; Chen, Xi; Fang, Minyi; Watanabe, Kenji; Kim, Chu-Young

2015-01-14

Biosynthesis of some polyether natural products involves a kinetically disfavored epoxide-opening cyclic ether formation, a reaction termed anti-Baldwin cyclization. One such example is the biosynthesis of lasalocid A, an ionophore antibiotic polyether. During lasalocid A biosynthesis, an epoxide hydrolase, Lsd19, converts the bisepoxy polyketide intermediate into the tetrahydrofuranyl-tetrahydropyran product. We report the crystal structure of Lsd19 in complex with lasalocid A. The structure unambiguously shows that the C-terminal domain of Lsd19 catalyzes the intriguing anti-Baldwin cyclization. We propose a general mechanism for epoxide selection by ionophore polyether epoxide hydrolases.

Epoxide hydrolase Lsd19 for polyether formation in the biosynthesis of lasalocid A: direct experimental evidence on polyene-polyepoxide hypothesis in polyether biosynthesis.

Science.gov (United States)

Shichijo, Yoshihiro; Migita, Akira; Oguri, Hiroki; Watanabe, Mami; Tokiwano, Tetsuo; Watanabe, Kenji; Oikawa, Hideaki

2008-09-17

Polyether metabolites are an important class of natural products. Although their biosynthesis, especially construction of polyether skeletons, attracted organic chemists for many years, no experimental data on the enzymatic polyether formation has been obtained. In this study, a putative epoxide hydrolase gene lsd19 found on the biosynthetic gene cluster of an ionophore polyether lasalocid was cloned and successfully overexpressed in Escherichia coli. Using the purified Lsd19, a proposed substrate, bisepoxyprelasalocid, and its synthesized analogue were successfully converted into lasalocid A and its derivative via a 6-endo-tet cyclization mode. On the other hand, treatment of the bisepoxide with trichloroacetic acid gave isolasalocid A via a 5-exo-tet cyclization mode. Therefore, the enzymatic conversion observed in this study unambiguously showed that the bisepoxyprelasalocid is an intermediate of the lasalocid biosynthesis and that Lsd19 catalyzes the sequential cyclic ether formations involving an energetically disfavored 6-endo-tet cyclization. This is the first example of the enzymatic epoxide-opening reactions leading to a polyether natural product.

Property Enhancement Effects of Side-Chain-Type Naphthalene-Based Sulfonated Poly(arylene ether ketone) on Nafion Composite Membranes for Direct Methanol Fuel Cells.

Science.gov (United States)

Wang, Baolong; Hong, Lihua; Li, Yunfeng; Zhao, Liang; Zhao, Chengji; Na, Hui

2017-09-20

Nafion/SNPAEK-x composite membranes were prepared by blending raw Nafion and synthesized side-chain-type naphthalene-based sulfonated poly(arylene ether ketone) with a sulfonation degree of 1.35 (SNPAEK-1.35). The incorporation of SNPAEK-1.35 polymer with ion exchange capacity (IEC) of 2.01 mequiv·g -1 into a Nafion matrix has the property enhancement effects, such as increasing IECs, improving proton conductivity, enhancing mechanical properties, reducing methanol crossover, and improving single cell performance of Nafion. Morphology studies show that Nafion/SNPAEK-x composite membranes exhibit a well-defined microphase separation structure depending on the contents of SNPAEK-1.35 polymer. Among them, Nafion/SNPAEK-7.5% with a bicontinuous morphology exhibits the best comprehensive properties. For example, it shows the highest proton conductivities of 0.092 S cm -1 at 25 °C and 0.163 S cm -1 at 80 °C, which are higher than those of recast Nafion with 0.073 S cm -1 at 25 °C and 0.133 S cm -1 at 80 °C, respectively. Nafion/SNPAEK-5.0% and Nafion/SNPAEK-7.5% membranes display an open circuit voltage of 0.77 V and a maximum power density of 47 mW cm -2 at 80 °C, which are much higher than those of recast Nafion of 0.63 V and 24 mW cm -2 under the same conditions. Nafion/SNPAEK-5.0% membrane also has comparable tensile strength (12.7 MPa) to recast Nafion (13.7 MPa), and higher Young's modulus (330 MPa) than that of recast Nafion (240 MPa). By combining their high proton conductivities, comparable mechanical properties, and good single cell performance, Nafion/SNPAEK-x composite membranes have the potential to be polymer electrolyte materials for direct methanol fuel cell applications.

Effect of surface finishing on friction and wear of Poly-Ether-Ether-Ketone (PEEK under oil lubrication

Directory of Open Access Journals (Sweden)

Thiago Fontoura de Andrade

Full Text Available Abstract The tribological properties of poly-ether-ether-ketone (PEEK containing 30% of carbon fiber were studied in an oil-lubricated environment and different surface finishing of the metallic counterbody. Four different finishing processes, commonly used in the automotive industry, were chosen for this study: turning, grinding, honing and polishing. The test system used was tri-pin on disc with pins made of PEEK and counterbody made of steel; they were fully immersed in ATF Dexron VI oil. Some test parameters were held constant, such as the apparent pressure of 2 MPa, linear velocity of 2 m/s, oil temperature at 85 °C, and the time - 120 minutes. The lubrication regime for the apparent pressure of 1 MPa to 7 MPa range was also studied at different sliding speeds. A direct correlation was found between the wear rate, friction coefficient and the lubrication regime, wherein wear under hydrodynamic lubrication was, on average, approximately 5 times lower, and the friction coefficient 3 times lower than under boundary lubrication.

Reinforcement of poly ether sulphones (PES) with exfoliated graphene oxide for aerospace applications

International Nuclear Information System (INIS)

Balasubramanian, K

2012-01-01

Composite materials have been used for aerospace for some time now and have gained virtually 100% acceptance as the materials of choice. Speciality polymers like poly ether sulphones (PES), poly ether ether ketones(PEEK), poly ether imides (PEI) are highly preferred materials as plastic matrix due to their superior temperature performance, excellent wear and friction resistance, excellent dimensional accuracy, high tensile strength, high modulus, precise machinability and chemical resistance. In recent years nanoadditives like single and multiwall carbon nanotubes, graphenes and graphene oxides(GO) are finding huge market potential in aerospace and automobile industries. But manufacture related factors such as particle/ matrix interphases, surface activation, mixing process, particle agglomeration, particle size and shape may lead to different property effects. In this research GO/PES composites were prepared by high shear melt blending technique. GO monolayers were exfoliated from natural graphite flake and dispersed homogeneously in PES matrix for the GO content ranging between 0.5 to 2.0 volume percentage with a high shear twin screw batch mixer. These melt blended nanocomposites were injection moulded for mechanical property validation of tensile strength, flexural modulus and impact resistance. Addition of 0.5 volume percentage of GO enhanced the tensile strength and flexural modulus by 40% and 90% respectively. The results show that addition of GO to PES increase mechanical properties due to the formation of continuous network, good dispersion and strong interfacial interactions. The strong interfacial interactions were accounted for the increase in glass transition temperature. Also there was a significant improvement in the impact resistance of the PES/ GO nanocomposite. The injection moulded samples were tested for stealth performance by measuring the electromagnetic shielding property.

Influence of Metal-Coated Graphite Powders on Microstructure and Properties of the Bronze-Matrix/Graphite Composites

Science.gov (United States)

Zhao, Jian-hua; Li, Pu; Tang, Qi; Zhang, Yan-qing; He, Jian-sheng; He, Ke

2017-02-01

In this study, the bronze-matrix/x-graphite (x = 0, 1, 3 and 5%) composites were fabricated by powder metallurgy route by using Cu-coated graphite, Ni-coated graphite and pure graphite, respectively. The microstructure, mechanical properties and corrosive behaviors of bronze/Cu-coated-graphite (BCG), bronze/Ni-coated-graphite (BNG) and bronze/pure-graphite (BPG) were characterized and investigated. Results show that the Cu-coated and Ni-coated graphite could definitely increase the bonding quality between the bronze matrix and graphite. In general, with the increase in graphite content in bronze-matrix/graphite composites, the friction coefficients, ultimate density and wear rates of BPG, BCG and BNG composites all went down. However, the Vickers microhardness of the BNG composite would increase as the graphite content increased, which was contrary to the BPG and BCG composites. When the graphite content was 3%, the friction coefficient of BNG composite was more stable than that of BCG and BPG composites, indicating that BNG composite had a better tribological performance than the others. Under all the values of applied loads (10, 20, 40 and 60N), the BCG and BNG composites exhibited a lower wear rate than BPG composite. What is more, the existence of nickel in graphite powders could effectively improve the corrosion resistance of the BNG composite.

Role of post-sulfonation of poly(ether ether sulfone) in proton conductivity and chemical stability of its proton exchange membranes for fuel cell

Energy Technology Data Exchange (ETDEWEB)

Unveren, Elif Erdal; Erdogan, Tuba; Inan, Tulay Y. [Chemistry Institute, TUBITAK Marmara Research Center, 41470, Gebze, Kocaeli (Turkey); Celebi, Serdar S. [Professor Emeritus, Chemical Engineering Department, Hacettepe University, 06800, Beytepe, Ankara (Turkey)

2010-04-15

Commercially available poly(ether ether sulfone), PEES, was directly sulfonated using concentrated sulfuric acid at low temperatures by minimizing degradation during sulfonation. The sulfonation reaction was performed in the temperature range of 5-25 C. Sulfonated polymers were characterized by FTIR, {sup 1}H NMR spectroscopy and ion exchange capacity (IEC) measurements. Degradation during sulfonation was investigated by measuring intrinsic viscosity, glass transition temperature and thermal decomposition temperature of sulfonated polymers. Sulfonated PEES, SPEES, membranes were prepared by solvent casting method and characterized in terms of IEC, proton conductivity and water uptake. The effect of sulfonation conditions on chemical stability of membranes was also investigated via Fenton test. Optimum sulfonation condition was determined to be 10 C with conc. H{sub 2}SO{sub 4} based on the characteristics of sulfonated polymers and also the chemical stability of their membranes. SPEES membranes exhibited proton conductivity up to 185.8 mS cm{sup -1} which is higher than that of Nafion 117 (133.3 mS cm{sup -1}) measured at 80 C and relative humidity 100%. (author)

Isotopic shifts in chemical exchange systems. 1. Large isotope effects in the complexation of Na+ isotopes by macrocyclic polyethers

International Nuclear Information System (INIS)

Knoechel, A.; Wilken, R.D.

1981-01-01

The complexation of 24 Na + and 22 Na + by 18 of the most widely used macrocyclic polyethers (crown ethers and monocyclic and bicyclic aminopolyethers) has been investigated in view of possible equilibrium isotope shifts. Solvated salts and polyether complexes were distributed differently into two phases and isotope ratios determined in both phases. Chloroform/water systems were shown to be particularly suitable to the investigations allowing favorable distribution for Na + and 13 of the 18 polyethers employed. With crown ethers 24 Na + enrichment varied from nonsignficant values (for large crown ethers) up to 3.1 +- 0.4% (18-crown-6). In the case of bicyclic aminopolyethers, ligands with cages of optimum size to accommodate Na + showed 24 Na + enrichment between O (nonsignificant) (2.2/sub B/2./sub B/) and 5.2 +- 1.8% (2.2.1). In contrast, for 2.2.2. and its derivatives, being too large for Na + , 22 Na + enrichment varying from O (nonsignificant) (2.2.2.p) up to 5.4 +- 0.5% (2.2.2.) has been observed. These values are remarkably high. They are explained by different bonding in solvate structure and polyether complex by using the theoretical approach of Bigeleisen

Influence of structure of crown ethers on their radiation stability

International Nuclear Information System (INIS)

Grigor'ev, E.I.; Myasoedova, T.G.; Nesterov, S.V.; Trakhtenberg, L.I.

1988-01-01

Primary products of γ-radiolysis of crown ethers with the same size of the macrocyclic ring and different substituents were studied by EPR and mass spectrometry. It was shown that introduction of substituents into the polyether ring increases the radiation stability of crown ethers due to intramolecular transfer of energy from the polyether ring to a substituent

Thermodynamic parameters for polyether adducts with neutral molecules

International Nuclear Information System (INIS)

Spencer, J.N.; Zafar, A.I.; Ganunis, T.F.

1992-01-01

Using calorimetry, thermodynamic parameters for the interaction of neutral molecules with polyether adducts are determined. When compared to its analogous acyclic ether, no macrocyclic effect is observed for 12-crown-4. The ether's collective oxygen atoms' action determines interaction with acetonitrile and malononitrile, with dimethyltin dichloride having a specific oxygen-binding site. 14 refs., 1 tab

Metal/graphite - composites in fusion engineering

International Nuclear Information System (INIS)

Staffler, R.; Kneringer, G.; Kny, E.; Reheis, N.

1995-01-01

Metal/graphite composites have been well known in medical industry for many years. X-ray tubes used in modern radiography, particulary in computerized tomography are equipped with rotating targets able to absorb a maximum of heat in a given time. Modern rotating targets consist of a refractory metal/graphite composite. Today the use of graphite as a plasma facing material is one predominant concept in fusion engineering. Depending on the thermal load, the graphite components have to be directly cooled (i.e. divertor plates) or inertially cooled (i.e. firstwall tiles). In case of direct cooling a metallurgical joining such as high temperature brazing between graphite and a metalic cooling structure shows the most promising results /1/. Inertially cooled graphite tiles have to be joined to a metallic backing plate in order to get a stable attachment to the supporting structure. The main requirements on the metallic partner of a metal/graphite composite and in the first wall area are: high melting point, high thermal strength, high thermal conductivity, low vapour pressure and a thermal expansion matching that of graphite. These properties are typical for the refractory metals such as molybdenum, tungsten and their alloys. (author)

Glass-Graphite Composite Materials

International Nuclear Information System (INIS)

Mayzan, M.Z.H.; Lloyd, J.W.; Heath, P.G.; Stennett, M.C.; Hyatt, N.C.; Hand, R.J.

2016-01-01

A summary is presented of investigations into the potential of producing glass-composite materials for the immobilisation of graphite or other carbonaceous materials arising from nuclear power generation. The methods are primarily based on the production of base glasses which are subsequently sintered with powdered graphite or simulant TRISO particles. Consideration is also given to the direct preparation of glass-graphite composite materials using microwave technology. Production of dense composite wasteforms with TRISO particles was more successful than with powdered graphite, as wasteforms containing larger amounts of graphite were resistant to densification and the glasses tried did not penetrate the pores under the pressureless conditions used. Based on the results obtained it is concluded that the production of dense glassgraphite composite wasteforms will require the application of pressure. (author)

SILICOMB PEEK Kirigami cellular structures: mechanical response and energy dissipation through zero and negative stiffness

International Nuclear Information System (INIS)

Virk, K; Marsh, M; Monti, A; Trehard, T; Hazra, K; Boba, K; Remillat, C D L; Scarpa, F; Farrow, I R

2013-01-01

The work describes the manufacturing, testing and parametric analysis of cellular structures exhibiting zero Poisson’s ratio-type behaviour, together with zero and negative stiffness effects. The cellular structures are produced in flat panels and curved configurations, using a combination of rapid prototyping techniques and Kirigami (Origami and cutting) procedures for PEEK (Polyether Ether Ketone) thermoplastic composites. The curved cellular configurations show remarkable large deformation behaviours, with zero and negative stiffness regimes depending also on the strain rate applied. These unusual stiffness characteristics lead to a large increase of energy absorption during cyclic tests. (paper)

A primary study into graphene/polyether ether ketone (PEEK) nanocomposite for laser sintering

Science.gov (United States)

Chen, Binling; Berretta, Silvia; Evans, Ken; Smith, Kaylie; Ghita, Oana

2018-01-01

This paper proposes two methods of preparation of graphene/PEEK powders for Laser Sintering (LS) and investigates their behaviour in relation to their microstructure and their properties. Thin composite films were fabricated in an attempt to replicate the thin layer formation of the powder bed process. Both methods of composite powder preparation (wet and dry) led to enhanced mechanical performance of the composite films at 0.1 and 0.5 wt% graphene nano-platelets (GNP) concentrations. The TEM images show that the GNP act as a nucleation point in crystallisation of PEEK, being at the centre of the spherulites. The hot stage microscopy reveals a 20 s delay in the onset of GNP/PEEK nanocomposite coalescence in comparison with plain PEEK. This is a very important observation for laser sintering, as it will influence the build strategy and specific parameters (e.g. time between layers deposition, multiple exposures). The excellent electrical conductivity properties of graphene were noticeable in the nanocomposite films at concentrations above 1 wt% GNP.

Polyether complexes of groups 13 and 14.

Science.gov (United States)

Swidan, Ala'aeddeen; Macdonald, Charles L B

2016-07-21

Notable aspects of the chemistry of complexes of polyether ligands including crown ethers, cryptands, glycols, glymes, and related polyether ligands with heavier group 13 and 14 elements are reviewed with a focus on results from 2005 to the present. The majority of reported polyether complexes contain lead(ii) and thallium(i) but recent breakthroughs in regard to the preparation of low oxidation state reagents of the lighter congeners have allowed for the generation of complexes containing indium(i), gallium(i), germanium(ii), and even silicon(ii). The important roles of ligand size, donor types, and counter anions in regard to the chemical properties of the polyether complexes is highlighted. A particular focus on the structural aspects of the numerous coordination complexes provides a rationale for some of the spectacular contributions that such compounds have made to Modern Main Group Chemistry.

Metal/graphite - composites in fusion engineering

International Nuclear Information System (INIS)

Staffler, R.; Kneringer, G.; Kny, E.; Reheis, N.

1989-01-01

Metal/graphite composites have been well known in medical industry for many years. X-ray tubes used in modern radiography, particularly in computerized tomography are equipped with rotating targets able to absorb a maximum of heat in a given time. Modern rotating targets consist of a refractory metal/graphite composite. Today the use of graphite as a plasma facing material is one predominant concept in fusion engineering. Depending on the thermal load, the graphite components have to be directly cooled (i.e. divertor plates) or inertially cooled (i.e. firstwall tiles). In case of direct cooling a metallurgical joining such as high temperature brazing between graphite and a metallic cooling structure shows the most promising results /1/. Inertially cooled graphite tiles have to be joined to a metallic backing plate in order to get a stable attachment to the supporting structure. The main requirements on the metallic partner of a metal/graphite composite used in the first wall area are: high melting point, high thermal strength, high thermal conductivity, low vapor pressure and a thermal expansion matching that of graphite. These properties are typical for the refractory metals such as molybdenum, tungsten and their alloys. 4 refs., 13 figs., 1 tab

Pyroelectric composite for detection of X-ray intensity

International Nuclear Information System (INIS)

Sakamoto, Walter Katsumi; Estevam, Giuliano Pierre; Carvalho, Aparecido Augusto de; Pontes, Wesley; Paula, Mauro Henrique de

2010-01-01

Composite material obtained with modified lead titanate (Pz34) ferroelectric ceramic and polyether-ether-ketone (PEEK) polymer matrix was used as sensitive component to measure X-ray intensity in a novel detection system. The sensing element works as a thermal transducer, converting a non-quantified thermal flux into an output measurable quantity of electrical voltage. The samples were obtained up to 60 vol.% of ceramic, by hot pressing the mixture of Pz34 and PEEK powders at 368 deg C and applying 12 MPa pressure for 2.0 h. The sensor response varies from 2.70 V to 0.80 V in the energy fluence rate range of 6.30 to 37.20 W/m 2 . The absorbed incident energy was analyzed as a function of the ionizing energy. Furthermore, by measuring the pyroelectric activity of the composite film it was observed that there is no degradation of the sensor after the irradiation. (author)

Effect of expanded graphite and PEI-co-Silicon Rubber on the thermo mechanical, morphological as well as rheological properties of in situ composites based on poly (ether imide) and liquid crystalline polymer

Energy Technology Data Exchange (ETDEWEB)

Hatui, Goutam, E-mail: hatui.goutam@gmail.com; Malas, Asish, E-mail: malasasish@gmail.com; Bhattacharya, Pallab; Dhibar, Saptarshi, E-mail: saptaaus2007@gmail.com; Kundu, Mrinal Kanti, E-mail: kanti.mrinal19@gmail.com; Kumar Das, Chapal, E-mail: chapal12@yahoo.co.in

2015-01-15

Highlights: • PEI/LCP/ PEI-co-Silicon Rubber/EG and PEI/LCP/MWCNT nano composites are prepared by melt blending method. • The dispersions of acid modified expanded graphite were improved in presence of PEI-co-Silicon Rubber. • Thermal stability was found to be highest for PLGC composite. • Storage modulus and Young’s modulus showed an upward trend with incorporation of only EG and EG in presence of PEI-co-Silicon Rubber. • Among the nano composites PLGC has highest viscosity. - Abstract: Nanocomposites of polyether imide (PEI) and liquid crystalline polymer (LCP) with either MWCNT, Expanded Graphite (EG) or in combination of both EG and PEI-co-Silicon Rubber were prepared by melt blending process. The compatibility between the polymeric phases (PEI and LCP) was observed to be increased by the addition of PEI-co-Silicon Rubber while the only MWCNT added system (PLC) resulted in smaller LCP droplets. A continuous morphology was produced in presence of both PEI-co-Silicon Rubber and EG both added system (PLGR). This was due to the compatibilizing effect of PEI-co-Silicon Rubber. FTIR analysis revealed interaction between PEI and LCP in presence of PEI-co-Silicon Rubber. Remarkable increment of storage modulus was observed with the addition of EG and PEI-co-Silicon Rubber. Transmission Electron Microscope (TEM) analysis showed better dispersion of multiple graphene layers of EG in presence of PEI-co-Silicon Rubber compatibilized system. Tensile and Young’s modulus both were highest for EG/ PEI-co-Silicon Rubber added system. This is due to flexible compatibilizing effect of PEI-co-Silicon Rubber which delayed the detachment of LCP domain from the PEI matrix and thus detains the fracture.

Effect of expanded graphite and PEI-co-Silicon Rubber on the thermo mechanical, morphological as well as rheological properties of in situ composites based on poly (ether imide) and liquid crystalline polymer

International Nuclear Information System (INIS)

Hatui, Goutam; Malas, Asish; Bhattacharya, Pallab; Dhibar, Saptarshi; Kundu, Mrinal Kanti; Kumar Das, Chapal

2015-01-01

Highlights: • PEI/LCP/ PEI-co-Silicon Rubber/EG and PEI/LCP/MWCNT nano composites are prepared by melt blending method. • The dispersions of acid modified expanded graphite were improved in presence of PEI-co-Silicon Rubber. • Thermal stability was found to be highest for PLGC composite. • Storage modulus and Young’s modulus showed an upward trend with incorporation of only EG and EG in presence of PEI-co-Silicon Rubber. • Among the nano composites PLGC has highest viscosity. - Abstract: Nanocomposites of polyether imide (PEI) and liquid crystalline polymer (LCP) with either MWCNT, Expanded Graphite (EG) or in combination of both EG and PEI-co-Silicon Rubber were prepared by melt blending process. The compatibility between the polymeric phases (PEI and LCP) was observed to be increased by the addition of PEI-co-Silicon Rubber while the only MWCNT added system (PLC) resulted in smaller LCP droplets. A continuous morphology was produced in presence of both PEI-co-Silicon Rubber and EG both added system (PLGR). This was due to the compatibilizing effect of PEI-co-Silicon Rubber. FTIR analysis revealed interaction between PEI and LCP in presence of PEI-co-Silicon Rubber. Remarkable increment of storage modulus was observed with the addition of EG and PEI-co-Silicon Rubber. Transmission Electron Microscope (TEM) analysis showed better dispersion of multiple graphene layers of EG in presence of PEI-co-Silicon Rubber compatibilized system. Tensile and Young’s modulus both were highest for EG/ PEI-co-Silicon Rubber added system. This is due to flexible compatibilizing effect of PEI-co-Silicon Rubber which delayed the detachment of LCP domain from the PEI matrix and thus detains the fracture

Dielectric relaxations and conduction mechanisms in polyether-clay composite polymer electrolytes under high carbon dioxide pressure.

Science.gov (United States)

Kitajima, Shunsuke; Bertasi, Federico; Vezzù, Keti; Negro, Enrico; Tominaga, Yoichi; Di Noto, Vito

2013-10-21

The composite material P(EO/EM)-Sa consisting of synthetic saponite (Sa) dispersed in poly[ethylene oxide-co-2-(2-methoxyethoxy)ethyl glycidyl ether] (P(EO/EM)) is studied by "in situ" measurements using broadband electrical spectroscopy (BES) under pressurized CO2 to characterize the dynamic behavior of conductivity and the dielectric relaxations of the ion host polymer matrix. It is revealed that there are three dielectric relaxation processes associated with: (I) the dipolar motions in the short oxyethylene side chains of P(EO/EM) (β); and (II) the segmental motion of the main chains comprising the polyether components (αfast, αslow). αslow is attributed to the slow α-relaxation of P(EO/EM) macromolecules, which is hindered by the strong coordination interactions with the ions. Two conduction processes are observed, σDC and σID, which are attributed, respectively, to the bulk conductivity and the interdomain conductivity. The temperature dependence of conductivity and relaxation processes reveals that αfast and αslow are strongly correlated with σDC and σID. The "in situ" BES measurements under pressurized CO2 indicate a fast decrease in σDC at the initial CO2 treatment time resulting from the decrease in the concentration of polyether-M(n+) complexes, which is driven by the CO2 permeation. The relaxation frequency (fR) of αslow at the initial CO2 treatment time increases and shows a steep rise with time with the same behavior of the αfast mode. It is demonstrated that the interactions between polyether chains of P(EO/EM) and cations in the polymer electrolyte layers embedded in Sa are probably weakened by the low permittivity of CO2 (ε = 1.08). Thus, the formation of ion pairs in the polymer electrolyte domains of P(EO/EM)-Sa occurs, with a corresponding reduction in the concentration of ion carriers.

Fluorinated poly(ether sulfone) ionomers with disulfonated naphthyl pendants for proton exchange membrane applications

Science.gov (United States)

Hu, Zhaoxia; Lu, Yao; Zhang, Xulve; Yan, Xiaobo; Li, Na; Chen, Shouwen

2018-06-01

Proton exchange membranes based on fluorinated poly(ether sulfone)s with disulfonated naphthyl pendants (sSPFES) have been successfully prepared by post functionalization through polymeric SNAr reaction. Copolymer structure was confirmed by H-nuclear magnetic resonance spectroscopy and Fourier transform infrared spectroscopy, the physico-chemical properties of the sSPFES membranes were evaluated by thermogravimetric analysis, gel permeation chromatography, electro-chemical impedance spectroscopy, atomic force microscopy, Fenton, water-swelling and fuel cell test. The pendant grafting degree was controlled by varying the feeding amount of the disulfonaphthols, resulting in the ion exchange capacity about 1.28-1.73 mmol/g. The obtained sSPFES membranes were thermal stable, mechanical ductile, and exhibited dimensional change less than 17%, water uptake below 70%, and proton conductivity as high as 0.17-0.28 S/cm at 90°C in water. In a single H2/O2 fuel cell test at 80°C, the sSPFES-B-3.2 membrane (1.61 mmol/g) showed the maximum power output of 593-658 mW/cm2 at 60%-80% relative humidity, indicating their rather promising potential for fuel cell applications.

Pseudomacrocyclic effect in extraction processes of metal salts by polyethers from nitric acid solutions

International Nuclear Information System (INIS)

Yakshin, V.V.; Vilkova, O.M.; Kotlyar, S.A.; Kamalov, G.L.

1997-01-01

Comparison of macrocyclic (ME) and pseudmacrocyclic effects (PME), originating by conduct of the metal salt extraction processes (Cs, Sr, In, Zr, Cd, etc) from nitric acid solutions through linear and cyclic polyethers, containing 5 or 6 atoms of ether oxygen and having close molecular masses (290-360), is carried out. It is shown that ordinary ethers practically do not extract the studied metals from nitric acid solutions. By transfer from linear polyethers to their macrocyclic analogs the ME impact is expressed clearly enough: the separation coefficient value grows by tens and hundred times. At the some time the PME role in the extraction processes of metal nitrates through crown-ethers with alkyl and groups is expressed less clearly

Modification of poly(ether ether ketone) by ion irradiation

Czech Academy of Sciences Publication Activity Database

Hnatowicz, Vladimír; Havránek, Vladimír; Bočan, Jiří; Macková, Anna; Vacík, Jiří; Švorčík, V.

2008-01-01

Roč. 266, č. 2 (2008), s. 283-287 ISSN 0168-583X R&D Projects: GA MŠk(CZ) LC06041 Institutional research plan: CEZ:AV0Z10480505 Keywords : PEEK * ion beam modification * polymer degradation Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders Impact factor: 0.999, year: 2008

Crosslinked poly(ether ether ketone): cost-effective proton exchange ...

Indian Academy of Sciences (India)

2018-02-02

Feb 2, 2018 ... such as their high cost, poor proton conductivity and high fuel permeability at temperature above 80. ◦. C, which stimu- lated the ..... swells or becomes water soluble and loses its dimensional sta- bility. The water uptake of the ...

SPEEK-MO{sub 2} (M = Zr, Sn) composite membranes for direct ethanol fuel cell: an inorganic modification of proton conductive

Energy Technology Data Exchange (ETDEWEB)

Kawaguti, Carla A.; Gomes, Ailton S. [Universidade Federal do Rio de Janeiro (UFRJ), RJ (Brazil). Inst. de Macromoleculas Eloisa Mano], e-mail: kawagutica@gmail.com

2007-07-01

Organic-inorganic composite membranes based on sulfonated poly(ether ether ketone) (SPEEK) for application in the direct ethanol fuel cell (DEFC) were synthesized. Particle of sulfated zirconia/tin oxide (SO{sub 4}{sup 2-}/ZrO{sub 2}, SnO{sub 2}, SO{sub 3}-/SnO{sub 2}) was synthesized by sol-gel method, and composite membranes with different oxide and different oxide contents were prepared from a mixture of SO{sub 4}{sup 2-}/ZrO{sub 2} or SnO{sub 2} or SO{sub 3}-/SnO{sub 2} powder and SPEEK solution. The physico-chemical properties of the membranes were studied by water or ethanol solution uptake measurements, scanning electron microscopy (SEM), the membrane's water and ethanol permeabilities were evaluated in pervaporation experiments and the conductivity determined by impedance spectroscopy. The ethanol permeabilities were decreased by inorganic modification. At several temperatures analysed, all SPEEK-MO{sub 2} composite exhibited better ethanol solution uptake than water uptake and this sorption is decreased when inorganic particles are add. A reduction of the proton conductivity by the inorganic modification was observed. (author)

Structures and Performance of Graphene/Polyimide Composite Graphite Fibers

Directory of Open Access Journals (Sweden)

LI Na

2017-09-01

Full Text Available Dry-wet spinning process was used to gain graphene oxide/polyimide composite fibers, then graphene/polyimide composite carbon and graphite fibers were obtained through carbonized and graphitized. Different graphene oxide contents of the composite carbon and graphite fibers were measured by thermal gravimetric analysis, Raman, mechanical properties, electrical properties,SEM and so on. The results show that when the GO content is 0.3%(mass fraction,the same below, the thermal property of the graphene oxide/polyimide composite fibers is the best. The mechanical and electrical properties are obriously improved by the addition of GO, graphitization degree also increases. When the composite carbon fibers are treated at 2800℃, GO content increases to 2.0%, the thermal conductivity of the composite graphite fibers reaches 435.57W·m-1·K-1 and cross-section structures of carbon fibers are more compact.

Low vanadium ion permeabilities of sulfonated poly(phthalazinone ether ketone)s provide high efficiency and stability for vanadium redox flow batteries

Science.gov (United States)

Chen, Liyun; Zhang, Shouhai; Chen, Yuning; Jian, Xigao

2017-07-01

A series of novel sulfonated poly(phthalazinone ether ketone)s containing pendant phenyl moieties (SPPEK-Ps) are synthesized and thoroughly characterized. The chemical structures of the polymers are confirmed by 1H NMR and FTIR analysis. The physicochemical properties and single cell performance of SPPEK-P membranes are systematically evaluated, revealing that the membranes are thermally, chemically and mechanically stable. The area resistances of SPPEK-P-90 and SPPEK-P-100 are 0.75 Ω cm2 and 0.34 Ω cm2, respectively. SPPEK-P membranes are impermeable to the bulky hydrated VO2+ ion and exhibited low V3+ ion permeability (SPPEK-P-90, 2.53 × 10-5 cm min-1) (Nafion 115 membrane: 9.0 × 10-4 cm min-1). Tests of SPPEK-P-90 in vanadium redox flow batteries (VRFBs) demonstrate a comparable columbic efficiency (CE) and energy efficiency (EE) to that of Nafion 115, where the CE is 98% and the EE is 83% at 60 mA cm-2. Moreover, the SPPEK-P-90 membrane exhibits stable performance in cell over 100 charge-discharge cycles (∼450 h).

Molecular motions of non-crystalline poly(aryl ether-ether-ketone) PEEK and influence of electron beam irradiation

International Nuclear Information System (INIS)

Sasuga, T.; Hagiwara, M.

1985-01-01

The dynamic mechanical relaxation of non-crystalline poly(aryl ether-ether-ketone) PEEK and the one irradiated with electron beam were studied. The three distinct γ, β, α' relaxation maxima were observed in unirradiated PEEK from low to high temperature. It was revealed from the study on the irradiation effects that three different molecular processes are overlapped in γ relaxation peak, i.e., molecular motion of water bound to main chain, local motion of main chain, and local mode of the aligned and/or oriented moiety. The β relaxation connected with the glass transition occurred at 150 deg C and it shifted to higher temperature by irradiation. The α' relaxation which can be attributed to rearrangement of molecular chain due to crystallization was observed in unirradiated PEEK approx. 180 deg C and its magnitude decreased with the increase in irradiation dose. This effect indicates the formation of structures inhibiting crystallization such as crosslinking and/or short branching during irradiation. A new relaxation, β', appeared in the temperature range of 40 deg to 100 deg C by irradiation and its magnitude increased with dose. This relaxation was attributed to rearrangement of molecular chain from loosened packing around chain ends, which were introduced into the non-crystalline region by chain scission under irradiation, to more rigid molecular packing. (author)

Bromine intercalated graphite for lightweight composite conductors

KAUST Repository

Amassian, Aram

2017-07-20

A method of fabricating a bromine-graphite/metal composite includes intercalating bromine within layers of graphite via liquid-phase bromination to create brominated-graphite and consolidating the brominated-graphite with a metal nanopowder via a mechanical pressing operation to generate a bromine-graphite/metal composite material.

Environmentally benign graphite intercalation compound composition for exfoliated graphite, flexible graphite, and nano-scaled graphene platelets

Science.gov (United States)

Zhamu, Aruna; Jang, Bor Z.

2014-06-17

A carboxylic-intercalated graphite compound composition for the production of exfoliated graphite, flexible graphite, or nano-scaled graphene platelets. The composition comprises a layered graphite with interlayer spaces or interstices and a carboxylic acid residing in at least one of the interstices, wherein the composition is prepared by a chemical oxidation reaction which uses a combination of a carboxylic acid and hydrogen peroxide as an intercalate source. Alternatively, the composition may be prepared by an electrochemical reaction, which uses a carboxylic acid as both an electrolyte and an intercalate source. Exfoliation of the invented composition does not release undesirable chemical contaminants into air or drainage.

The roles of geometry and topology structures of graphite fillers on thermal conductivity of the graphite/aluminum composites

Energy Technology Data Exchange (ETDEWEB)

Zhou, C.; Chen, D.; Zhang, X.B. [State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, Shanghai 200240 (China); Chen, Z., E-mail: zhe.chen@sjtu.edu.cn [State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, Shanghai 200240 (China); Zhong, S.Y.; Wu, Y. [State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, Shanghai 200240 (China); Ji, G. [Unité Matériaux et Transformations, CNRS UMR 8207, Université Lille 1, Villeneuve d' Ascq 59655 (France); Wang, H.W. [State Key Laboratory of Metal Matrix Composites, Shanghai Jiao Tong University, Shanghai 200240 (China)

2015-02-20

Various graphite fillers, such as graphite particles, graphite fibers, graphite flakes and porous graphite blocks, have been successfully incorporated into an Al alloy by squeeze casting in order to fabricate graphite/Al composites with enhanced thermal conductivity (TC). Microstructural characterization by X-ray diffraction and scanning electron microscopy has revealed a tightly-adhered, clean and Al{sub 4}C{sub 3}-free interface between the graphite fillers and the Al matrix in all the as-fabricated composites. Taking the microstructural features into account, we generalized the corresponding predictive models for the TCs of these composites with the effective medium approximation and the Maxwell mean-field scheme, which both show good agreement with the experimental data. The roles of geometry and topology structures of graphite fillers on the TCs of the composites were further discussed. - Highlights: • The thermal enhancement of various graphite fillers with different topology structures. • Predictive models for the thermal conductivity of different topology structures. • Oriented flakes alignment has the high potentials for thermal enhancement.

Fabrication and Physical Properties of Titanium Nitride/Hydroxyapatite Composites on Polyether Ether Ketone by RF Magnetron Sputtering Technique

Science.gov (United States)

Nupangtha, W.; Boonyawan, D.

2017-09-01

Titanium nitride (TiN) coatings have been used very successfully in a variety of applications because of their excellent properties, such as the high hardness meaning good wear resistance and also used for covering medical implants. Hydroxyapatite is a bioactive ceramic that contributes to the restoration of bone tissue, which together with titanium nitride may contribute to obtaining a superior composite in terms of mechanical and bone tissue interaction matters. This paper aims to explain how to optimize deposition conditions for films synthesis on PEEK by varying sputtering parameters such as nitrogen flow rate and direction, deposition time, d-s (target-to-substrate distance) and 13.56 MHz RF power. The plasma conditions used to deposit films were monitored by the optical emission spectroscopy (OES). Titanium nitride/Hydroxyapatite composite films were performed by gas mixture with nitrogen and argon ratio of 1:3 and target-to-substrate distance at 8 cm. The gold colour, as-deposited film was found on PEEK with high hardness and higher surface energy than uncoated PEEK. X-ray diffraction characterization study was carried to study the crystal structural properties of these composites.

Dielectric Properties of Polyether Sulfone/Bismaleimide Resin Composite Based on Nanolumina Modified by Super-Critical Ethanol

Science.gov (United States)

Chen, Yufei; Li, Zhichao; Teng, Chengjun; Li, Fangliang; Han, Yang

2016-11-01

Nano-alumina was chemically modified with super-critical ethanol enabling a surface active coating. Modified nano-alumina was incorporated in polymer blends based on thermoplastic polyether sulfone and thermosetting bismaleimide resin to produce novel nanocomposites designated as SCE-Al2O3/PES-MBAE. In the SCE-Al2O3/PES-MBAE nano-composites, the matrix was originally formed from 4,4'-diamino diphenyl methane bismaleimide (MBMI) using the diluents of 3,3'-diallyl bisphenol A (BBA) and bisphenol-A diallyl ether (BBE), while polyether sulfone (PES) was used as toughening agent along with super-critically modified nano-alumina (SCE-Al2O3) as filler material. The content of SCE-Al2O3 was varied from 0 wt.% to 6 wt.%. The nano-composites were characterized for their morphological, spectroscopic and dielectric properties. Fourier transform infrared spectroscopy (FT-IR) indicated that ethanol molecules had adhered to the surface of the nano-Al2O3 in super-critical state. A reaction between MBMI and allyl compound occurred and SCE-Al2O3 was doped into the polymer matrix. Volume resistivity of the composite initially increased and then decreased. The modification due to SCE-Al2O3 could overcome the undesirable impact of PES by using a bare minimum level of SCE-Al2O3. The dielectric constant ( ɛ) and dielectric loss (tan δ) as in the case of volume resistivity were initially increased and then decreased with the content of SCE-Al2O3 in the composite. The dielectric constant, dielectric loss and dielectric strength of SCE-Al2O3 (4 wt.%)/PES (5 wt.%)-MBAE nano-composite were 3.53 (100 Hz), 1.52 × 10-3 (100 Hz) and 15.66 kV/mm, respectively, which indicated that the dielectric properties of the composite fulfilled the basic requirements of electrical and insulating material. It was evident from the morphological analysis that the SCE-Al2O3 was evenly dispersed at the nanoscale; for example, the size of SCE-Al2O3 in SCE-Al2O3 (4 wt.%)/PES (5 wt.%)-MBAE measured less than 50 nm.

On solvent extraction of metals by macrocyclic polyethers

International Nuclear Information System (INIS)

Ionov, V.P.

1984-01-01

The Ksub(γ) parameter characterizing effective ion charges in ionic associates of metal salts is suggested; these charges parallel with other factors determine the metals extraction by macrocyclic polyethers (crown-ethers). The dependence of metal extraction constant on the Ksub(γ) parameter is discussed. It is shown that the less effective cation charge of alkali metal ionic associates, the more probable its entering the crown-ether cavity. The synergetic crown-ethers extraction is bound as well with Ksub(γ) of metal salts. The differences in the cation extraction constants having the same ionic radius are explained with account of different values of Ksub(γ) parameters of these salts

Phase behavior in blends of ethylene oxide-propylene oxide copolymer and poly(ether sulfone) studied by modulated-temperature DSC and NMR relaxometry.

Science.gov (United States)

Van Lokeren, Luk; Gotzen, Nicolaas-Alexander; Pieters, Ronny; Van Assche, Guy; Biesemans, Monique; Willem, Rudolph; Van Mele, Bruno

2009-01-01

The state diagram of a blend consisting of a copolymer containing ethylene oxide and propylene oxide, P(EO-ran-PO), and poly(ether sulfone), PES, is constructed by using modulated-temperature differential scanning calorimetry (MTDSC), T(2) NMR relaxometry, and light scattering. The apparent heat capacity signal in MTDSC is used for the characterization of polymer miscibility and morphology development. T(2) NMR relaxometry is used to detect the onset of phase separation, which is in good agreement with the onset of phase separation in the apparent heat capacity from MTDSC and the cloud-point temperature as determined from light scattering. The coexistence curve can be constructed from T(2) values at various temperatures by using a few blends with well-chosen compositions. These T(2) values also allow the detection of the boundary between the demixing zones with and without interference of partial vitrification and are in good agreement with stepwise quasi-isothermal MTDSC heat capacity measurements. Important interphases are detected in the heterogeneous P(EO-ran-PO)/PES blends.

High polymer-based composite containers for the disposal/storage of high radioactive waste

International Nuclear Information System (INIS)

Miedema, I.

2001-01-01

Spent fuel disposal is one of the hottest topics in nuclear news, getting considerable amount of media coverage around the world. Canada as well as many other countries with nuclear electric generation plants has therefore been pushed to develop policy on this issue. One of the proposed and most widely supported strategies is to dispose of this so-called waste permanently in deep underground vaults. Through the use of engineered barriers including vault seals, vault composition, backfill and sophisticated containers this radioactive matter is isolated from the natural environment. According to a design developed by Atomic Energy of Canada, the seclusion must be maintained for approximately 500 years, which is a representative length of time it takes for the radioactive elements to decay to natural background levels. The purpose of the current study is to determine the feasibility of using poly(ether ether ketone), an advanced polymer, and continuous carbon fibre in a consolidated composite as a principal container component. Feasibility was determined by simulating the ultimate radioactive environment that the containers will be exposed to by exposing test specimens to neutron and gamma radiation fields at various temperatures (20 o C - 75 o C) for a variety of time intervals. (author)

Preparation and characterization of sulfonated amine-poly(ether sulfone)s for proton exchange membrane fuel cell

Energy Technology Data Exchange (ETDEWEB)

Seo, Dong-Wan; Lim, Young-Don; Lee, Soon-Ho; Jeong, Young-Gi; Kim, Whan-Gi [Department of Applied Chemistry/RIC-ReSEM, Konkuk University, Chungju-si, Chungbuk 380-701 (Korea, Republic of); Hong, Tae-Whan [Department of Materials Sci and Engineering/RIC-ReSEM, Chungju National University, Chungju, Chungbuk (Korea, Republic of)

2010-12-15

Sulfonated amine-poly(ether sulfone)s (S-APES)s were prepared by nitration, reduction and sulfonation of poly(ether sulfone) (ultrason {sup registered} -S6010). Poly(ether sulfone) was reacted with ammonium nitrate and trifluoroacetic anhydride to produce the nitrated poly(ether sulfone), and was followed by reduction using tin(II)chloride and sodium iodide as reducing agents to give the amino-poly(ether sulfone). The S-APES was obtained by reaction of 1,3-propanesultone and the amino-poly(ether sulfone) (NH{sub 2}-PES) with sodium methoxide. The different degrees of nitration and reduction of poly(ether sulfone) were successfully synthesized by an optimized process. The reduction of nitro group to amino was done quantitatively, and this controlled the contents of the sulfonic acid group. The films were converted from salt to acid forms with dilute hydrochloric acid. Different contents of sulfonated unit of the S-APES were studied by FT-IR, {sup 1}H NMR spectroscopy, differential scanning calorimetry (DSC), and thermo gravimetric analysis (TGA). Sorption experiments were conducted to observe the interaction of sulfonated polymers with water and methanol. The ion exchange capacity (IEC), a measure of proton conductivity, was evaluated. The S-APES membranes exhibit conductivities (25 C) from 1.05 x 10{sup -3} to 4.83 x 10{sup -3} S/cm, water swell from 30.25 to 66.50%, IEC from 0.38 to 0.82 meq/g, and methanol diffusion coefficients from 3.10 x 10{sup -7} to 4.82 x 10{sup -7} cm{sup 2}/S at 25 C. (author)

Great isotope effects in compounding of sodium isotopes by macrocyclic polyether

International Nuclear Information System (INIS)

Knoechel, A.; Wilken, R.D.

1978-01-01

Isotope effects appear in the compounding of the two sodium isotopes 24 Na + and 22 Na + with macrocyclic polyethers, whose value was determined for the 13 best known polyethers. A radiometric process was used for determining the different half life periods of the nuclides used. To separate the compound and non-compound types, these were distributed between water and chloroform. The isotope ratio in the chloroform phase was compared with the output isotope ratio and the separation facfor determined from this. When using crown ethers, there was enrichment of 24 Na + by a significant amount (large crown ether) up to 3.1 +- 0.4% for 18 crown 6. The remarkably high results can be correlated by Biegeleisen's theory with other chemical conditions. There is a report on the first results of transferring these conditions to the H + /T + system. (orig.) [de

Surface analysis of graphite fiber reinforced polyimide composites

Science.gov (United States)

Messick, D. L.; Progar, D. J.; Wightman, J. P.

1983-01-01

Several techniques have been used to establish the effect of different surface pretreatments on graphite-polyimide composites. Composites were prepared from Celion 6000 graphite fibers and the polyimide LARC-160. Pretreatments included mechanical abrasion, chemical etching and light irradiation. Scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) were used in the analysis. Contact angle of five different liquids of varying surface tensions were measured on the composites. SEM results showed polymer-rich peaks and polymer-poor valleys conforming to the pattern of the release cloth used durng fabrication. Mechanically treated and light irradiated samples showed varying degrees of polymer peak removal, with some degradation down to the graphite fibers. Minimal changes in surface topography were observed on concentrations of surface fluorine even after pretreatment. The light irradiation pretreatment was most effective at reducing surface fluorine concentrations whereas chemical pretreatment was the least effective. Critical surface tensions correlated directly with the surface fluorine to carbon ratios as calculated from XPS.

Considerations of the Effects of Naphthalene Moieties on the Design of Proton-Conductive Poly(arylene ether ketone) Membranes for Direct Methanol Fuel Cells.

Science.gov (United States)

Wang, Baolong; Hong, Lihua; Li, Yunfeng; Zhao, Liang; Wei, Yuxue; Zhao, Chengji; Na, Hui

2016-09-14

Novel sulfonated poly(arylene ether ketones) (SDN-PAEK-x), consisting of dual naphthalene and flexible sulfoalkyl groups, were prepared via polycondensation, demethylation, and sulfobutylation grafting reaction. Among them, SDN-PAEK-1.94 membrane with the highest ion exchange capacity (IEC = 2.46 mequiv·g(-1)) exhibited the highest proton conductivity, which was 0.147 S· cm(-1) at 25 °C and 0.271 S·cm(-1) at 80 °C, respectively. The introduction of dual naphthalene moieties is expected to achieve much enhanced properties compared to those of sulfonated poly(arylene ether ketones) (SNPAEK-x), consisting of single naphthalene and flexible sulfoalkyl groups. Compared with SNPAEK-1.60 with a similar IEC, SDN-PAEK-1.74 membrane showed higher proton conductivity, higher IEC normalized conductivity, and higher effective proton mobility, although it had lower analytical acid concentration. The SDN-PAEK-x membranes with IECs higher than 1.96 mequiv·g(-1) also exhibited higher proton conductivity than that of recast Nafion membrane. Furthermore, SDN-PAEK-1.94 displayed a better single cell performance with a maximum power density of 60 mW·cm(-2) at 80 °C. Considering its high proton conductivity, excellent single cell performance, good mechanical stabilities, low membrane swelling, and methanol permeability, SDN-PAEK-x membranes are promising candidates as alternative polymer electrolyte membranes to Nafion for direct methanol fuel cell applications.

Carbide coated fibers in graphite-aluminum composites

Science.gov (United States)

Imprescia, R. J.; Levinson, L. S.; Reiswig, R. D.; Wallace, T. C.; Williams, J. M.

1975-01-01

The NASA-supported program at the Los Alamos Scientific Laboratory (LASL) to develop carbon fiber-aluminum matrix composites is described. Chemical vapor deposition (CVD) was used to uniformly deposit thin, smooth, continuous coats of TiC on the fibers of graphite tows. Wet chemical coating of fibers, followed by high-temperature treatment, was also used, but showed little promise as an alternative coating method. Strength measurements on CVD coated fiber tows showed that thin carbide coats can add to fiber strength. The ability of aluminum alloys to wet TiC was successfully demonstrated using TiC-coated graphite surfaces. Pressure-infiltration of TiC- and ZrC-coated fiber tows with aluminum alloys was only partially successful. Experiments were performed to evaluate the effectiveness of carbide coats on carbon as barriers to prevent reaction between alluminum alloys and carbon. Initial results indicate that composites of aluminum and carbide-coated graphite are stable for long periods of time at temperatures near the alloy solidus.

Electricity generation and removal performance of a microbial fuel cell using sulfonated poly (ether ether ketone) as proton exchange membrane to treat phenol/acetone wastewater.

Science.gov (United States)

Wu, Hao; Fu, Yu; Guo, Chunyu; Li, Yanbo; Jiang, Nanzhe; Yin, Chengri

2018-07-01

The microbial fuel cell (MFC) has emerged as a promising technology for wastewater treatment and energy recovery, but the expensive cost of proton exchange membranes (PEMs) is a problem that need to be solved. In this study, a two-chamber MFC based on our self-made PEM sulfonated poly (ether ether ketone) membrane was set up to treat phenol/acetone wastewater and synchronously generate power. The maximum output voltage was 240-250 mV. Using phenol and acetone as substrates, the power generation time in an operation cycle was 289 h. The MFC exhibited good removal performance, with no phenol or acetone detected, respectively, when the phenol concentration was lower than 50 mg/L and the acetone concentration was lower than 100 mg/L. This study provides a cheap and eco-friendly way to treat phenol/acetone wastewater and generate useful energy by MFC technology. Copyright © 2018 Elsevier Ltd. All rights reserved.

Graphite-graphite oxide composite electrode for vanadium redox flow battery

International Nuclear Information System (INIS)

Li Wenyue; Liu Jianguo; Yan Chuanwei

2011-01-01

Highlights: → A new composite electrode is designed for vanadium redox flow battery (VRB). → The graphite oxide (GO) is used as electrode reactions catalyst. → The excellent electrode activity is attributed to the oxygen-containing groups attached on the GO surface. → A catalytic mechanism of the GO towards the redox reactions is presumed. - Abstract: A graphite/graphite oxide (GO) composite electrode for vanadium redox battery (VRB) was prepared successfully in this paper. The materials were characterized with X-ray diffraction, X-ray photoelectron spectroscopy and scanning electron microscopy. The specific surface area was measured by the Brunauer-Emmett-Teller method. The redox reactions of [VO 2 ] + /[VO] 2+ and V 3+ /V 2+ were studied with cyclic voltammetry and electrochemical impedance spectroscopy. The results indicated that the electrochemical performances of the electrode were improved greatly when 3 wt% GO was added into graphite electrode. The redox peak currents of [VO 2 ] + /[VO] 2+ and V 3+ /V 2+ couples on the composite electrode were increased nearly twice as large as that on the graphite electrode, and the charge transfer resistances of the redox pairs on the composite electrode are also reduced. The enhanced electrochemical activity could be ascribed to the presence of plentiful oxygen functional groups on the basal planes and sheet edges of the GO and large specific surface areas introduced by the GO.

Graphite and boron carbide composites made by hot-pressing

International Nuclear Information System (INIS)

Miyazaki, K.; Hagio, T.; Kobayashi, K.

1981-01-01

Composites consisting of graphite and boron carbide were made by hot-pressing mixed powders of coke carbon and boron carbide. The change of relative density, mechanical strength and electrical resistivity of the composites and the X-ray parameters of coke carbon were investigated with increase of boron carbide content and hot-pressing temperature. From these experiments, it was found that boron carbide powder has a remarkable effect on sintering and graphitization of coke carbon powder above the hot-pressing temperature of 2000 0 C. At 2200 0 C, electrical resistivity of the composite and d(002) spacing of coke carbon once showed minimum values at about 5 to 10 wt% boron carbide and then increased. The strength of the composite increased with increase of boron carbide content. It was considered that some boron from boron carbide began to diffuse substitutionally into the graphite structure above 2000 0 C and densification and graphitization were promoted with the diffusion of boron. Improvements could be made to the mechanical strength, density, oxidation resistance and manufacturing methods by comparing with the properties and processes of conventional graphites. (author)

Gamma-radiolysis of benzosubstituted crown ethers

International Nuclear Information System (INIS)

Grigor'ev, E.I.; Nesterov, S.V.; Mikhalitsyna, O.V.; Trakhtenberg, L.I.; Myasoedova, T.G.

1992-01-01

The products of gamma-radiolysis of benzosubstituted crown ethers, which are distiguished by the size of polyether ring, and alkylsubstituted DB18C6 are studied by the methods of ESR and mass-spectrometry. A mechanism of the radiolysis of the radiolysis of the studied compounds in the solid phase is proposed. It is shown that the prinicple radiolysis process is the rupture of C-O bond resulting in the stabilization of H atoms from group -CH 2 - of polyether ring is realized with a lower probability

Bromine intercalated graphite for lightweight composite conductors

KAUST Repository

Amassian, Aram; Patole, Archana

2017-01-01

A method of fabricating a bromine-graphite/metal composite includes intercalating bromine within layers of graphite via liquid-phase bromination to create brominated-graphite and consolidating the brominated-graphite with a metal nanopowder via a

Effect of surface modification of fly ash on the mechanical, thermal, electrical and morphological properties of polyetheretherketone composites

International Nuclear Information System (INIS)

Parvaiz, M. Rahail; Mohanty, Smita; Nayak, Sanjay K.; Mahanwar, P.A.

2011-01-01

Research highlights: → Preparation of high performance poly (ether ether ketone) (PEEK)/fly ash (FA) composites. → Characterization studies like DMTA, MDSC, FTIR and SEM have been carried out. → Addition of modified FA, decrease T c by 58 deg. C, due to the hindrance in PEEK molecular mobility during the cooling crystallization process. → Modified fly ash filled PEEK composites exhibit higher tensile strength and modulus than the unmodified ones. - Abstract: Poly (ether ether ketone) (PEEK)/fly ash (FA) composites were prepared using melt blending technique. To improve the interfacial interaction of fly ash with the PEEK matrix, fly ash was chemically modified with calcium hydroxide, at different concentration. Various characterization studies like dynamic mechanical thermal analysis (DMTA), modulated differential scanning calorimetry (MDSC) and scanning electron microscopy (SEM) have been carried out to evaluate the storage modulus, tan δ, crystallinity, and morphology in the composites. SEM micrographs showed more uniform dispersion and interaction in the modified composites than unmodified counterpart. Surface modified fly ash improved the interfacial adhesion between fly ash and PEEK which is confirmed also through improved mechanical strength. The dynamic modulus of PEEK composites exhibited over 133% increment at 100-250 deg. C, indicating improvement of elevated temperature mechanical properties. The modified fly ash reinforcements also showed improvement in glass-transition and crystallization temperature.

Preparation and Characterization of Graphite Waste/CeO2 Composites

Science.gov (United States)

Kusrini, E.; Utami, C. S.; Nasruddin; Prasetyanto, E. A.; Bawono, Aji A.

2018-03-01

In this research, the chemical modification of graphite waste with CeO2 was developed and characterized. Graphite waste was pretreated with mechanical to obtain the size 200 mesh (75 μm), and thermal methods at 110°C oven for 6 hours. Here, we demonstrate final properties of graphite before modification (GBM), activated graphite (GA) and graphite/CeO2 composite with variation of 0.5, 1 and 2 g of CeO2 (G0.5; G1; G2). The effect of CeO2 concentration was observed. The presence of cerium in modified graphite samples (G0.5; G1; G2) were analyzed using SEM-EDX. The results show that the best surface area was found in G2 is 26.82 m2/g. The presence of CeO2 onto graphite surface does not significantly increase the surface area of composites.

Free volume study on the miscibility of PEEK/PEI blend using positron annihilation and dynamic mechanical thermal analysis

International Nuclear Information System (INIS)

Ramani, R; Alam, S

2015-01-01

High performance polymer blend of poly(ether ether ketone) (PEEK) and poly(ether imide) (PEI) was examined for their free volume behaviour using positron annihilation lifetime spectroscopy and dynamic mechanical thermal analysis methods. The fractional free volume obtained from PALS shows a negative deviation from linear additivity rule implying good miscibility between PEEK and PEI. The dynamic modulus and loss tangent were obtained for the blends at three different frequencies 1, 10 and 100 Hz at temperatures close to and above their glass transition temperature. Applying Time-Temperature-Superposition (TTS) principle to the DMTA results, master curves were obtained at a reference temperature T o and the WLF coefficients c 0 1 and c 0 2 were evaluated. Both the methods give similar results for the dependence of fractional free volume on PEI content in this blend. The results reveal that free volume plays an important role in determining the visco-elastic properties in miscible polymer blends. (paper)

Preparation and characterization of polymer blend based on sulfonated poly (ether ether ketone) and polyetherimide (SPEEK/PEI) as proton exchange membranes for fuel cells

Energy Technology Data Exchange (ETDEWEB)

Hashim, Nordiana; Ali, Ab Malik Marwan [Ionic Material and Devices Research Laboratory, Institute of Science, Universiti Teknologi MARA, 40450 Shah Alam (Malaysia); Lepit, Ajis; Rasmidi, Rosfayanti [Faculty of Applied Sciences, Universiti Teknologi MARA Sabah, Beg Berkunci 71, 88997 Kota Kinabalu (Malaysia); Subban, Ri Hanum Yahaya [Faculty of Applied Sciences, Universiti Teknologi MARA, 40450 Shah Alam (Malaysia); Institute of Science, Universiti Teknologi MARA, 40450 Shah Alam (Malaysia); Yahya, Muhd Zu Azhan [Faculty of Defence Science & Technology, Universiti Pertahanan Nasional Malaysia, 57000 Kuala Lumpur (Malaysia)

2015-08-28

Blends of sulfonated poly (ether ether ketone) (SPEEK) and polyetherimide (PEI) were prepared in five different weight ratios using N-methyl-2-pyrrolidone (NMP) as solvent by the solution cast technique. The degree of sulfonation (DS) of the sulfonated PEEK was determined from deuterated dimethyl sulfoxide (DMSO-d{sub 6}) solution of the purified polymer using {sup 1}H NMR method. The properties studied in the present investigation includes conductivity, water uptake, thermal stability and structure analysis of pure SPEEK as well as SPEEK-PEI polymer blend membranes. The experimental results show that the conductivity of the membranes increased with increase in temperature from 30 to 80°C, except for that of pure SPEEK membrane which increased with temperature from 30 to 60°C while its conductivity decreased with increasing temperature from 60 to 80°C. The conductivity of 70wt.%SPEEK-30wt.%PEI blend membrane at 80% relative humidity (RH) is found to be 1.361 × 10{sup −3} Scm{sup −1} at 30°C and 3.383 × 10{sup −3} Scm{sup −1} at 80°C respectively. It was also found that water uptake and thermal stability of the membranes slightly improved upon blending with PEI. Structure analysis was carried out using Fourier Transform Infrared (FTIR) spectroscopy which revealed considerable interactions between sulfonic acid group of SPEEK and imide groups of PEI. Modification of SPEEK by blending with PEI shows good potential for improving the electrical and physical properties of proton exchange membranes.

Quaternized adamantane-containing poly(aryl ether ketone) anion exchange membranes for vanadium redox flow battery applications

Science.gov (United States)

Zhang, Bengui; Zhang, Shouhai; Weng, Zhihuan; Wang, Guosheng; Zhang, Enlei; Yu, Ping; Chen, Xiaomeng; Wang, Xinwei

2016-09-01

Quaternized adamantane-containing poly(aryl ether ketone) anion exchange membranes (QADMPEK) are prepared and investigated for vanadium redox flow batteries (VRFB) application. The bulky, rigid and highly hydrophobic adamantane segment incorporated into the backbone of membrane material makes QADMPEK membranes have low water uptake and swelling ratio, and the as-prepared membranes display significantly lower permeability of vanadium ions than that of Nafion117 membrane. As a consequence, the VRFB cell with QADMPEK-3 membrane shows higher coulombic efficiency (99.4%) and energy efficiency (84.0%) than those for Nafion117 membrane (95.2% and 80.5%, respectively) at the current density of 80 mA cm-2. Furthermore, at a much higher current density of 140 mA cm-2, QADMPEK membrane still exhibits better coulombic efficiency and energy efficiency than Nafion117 membrane (coulombic efficiency 99.2% vs 96.5% and energy efficiency 76.0% vs 74.0%). Moreover, QADMPEK membranes show high stability in in-situ VRFB cycle test and ex-situ oxidation stability test. These results indicate that QADMPEK membranes are good candidates for VRFB applications.

Preparation and characterization of flake graphite/silicon/carbon spherical composite as anode materials for lithium-ion batteries

International Nuclear Information System (INIS)

Lai Jun; Guo Huajun; Wang Zhixing; Li Xinhai; Zhang Xiaoping; Wu Feixiang; Yue Peng

2012-01-01

Highlights: ► Flake graphite/silicon/carbon composite is synthesized via spray drying. ► Flake graphite of ∼0.5 μm and glucose are used to prepare the composite. ► The as-prepared composite shows spherical and porous appearance. ► The composite shows nearly the same cycleability as commercial graphite in 20 cycles. ► The composite shows a reversible capacity of 552 mAh/g at the 20th cycle. - Abstract: Using nano-Si, glucose and flake graphite of ∼0.5 μm as raw materials, flake graphite/silicon/carbon composite is successfully synthesized via spray drying and subsequent pyrolysis. The samples are characterized by XRD, SEM, TEM and electrochemical measurements. The composite is composed of flake graphite, nano-Si and amorphous glucose-pyrolyzed carbon and presents good spherical appearance. Some micron pores arising from the decomposition of glucose exist on the surface of the composite particles. The composite has a high reversible capacity of 602.7 mAh/g with an initial coulombic efficiency of 69.71%, and shows nearly the same cycleability as the commercial graphite in 20 cycles. Both the glucose-pyrolyzed carbon and the micron pores play important roles in improving the cycleability of the composite. The flake graphite/silicon/carbon composite electrode is a potential alternative to graphite for high energy-density lithium ion batteries.

Dynamic characteristics of polymer faced tilting pad journal bearings

DEFF Research Database (Denmark)

Simmons, Gregory F.; Cerda Varela, Alejandro Javier; Santos, Ilmar

2014-01-01

Dynamic characteristics of polymer faced tilting pad journal bearings are presented. Investigations are conducted using a single pad, load on pad configuration over a range of shaft speeds and loads. Two polyether ether ketone (PEEK) faced pads, one polytetrafluoroethylene (PTFE) faced pad and two...

Radiation-induced grafting of vinylbenzyl chloride onto a poly(ether ether ketone) film

International Nuclear Information System (INIS)

Hwang, Mi-Lim; Song, Ju-Myung; Ko, Beom-Seok; Sohn, Joon-Yong; Nho, Young-Chang; Shin, Junhwa

2012-01-01

In this study, the effects of various irradiation conditions including solvent, monomer concentration, total dose, and dose rate on the radiation grafting of a VBC monomer onto a PEEK aromatic hydrocarbon film for the preparation of a PVBC-grafted PEEK (PEEK-g-PVBC) film were investigated. The results show that the desired PVBC-grafted PEEK film can be prepared using a simultaneous irradiation grafting method, and that the degree of grafting (DOG) of the film is largely influenced by the irradiation conditions. Among the applied solvents, halogenated solvents, dichloromethane and chloroform, were found to be suitable for grafting. The successful preparation of the grafted film was confirmed using analytical instruments such as FT-IR, TGA, and SEM-EDX.

Preparation and characterization of flake graphite/silicon/carbon spherical composite as anode materials for lithium-ion batteries

Energy Technology Data Exchange (ETDEWEB)

Lai Jun [School of Metallurgical Science and Engineering, Central South University, Changsha 410083 (China); Guo Huajun, E-mail: Lai_jun_@126.com [School of Metallurgical Science and Engineering, Central South University, Changsha 410083 (China); Wang Zhixing; Li Xinhai; Zhang Xiaoping; Wu Feixiang; Yue Peng [School of Metallurgical Science and Engineering, Central South University, Changsha 410083 (China)

2012-07-25

Highlights: Black-Right-Pointing-Pointer Flake graphite/silicon/carbon composite is synthesized via spray drying. Black-Right-Pointing-Pointer Flake graphite of {approx}0.5 {mu}m and glucose are used to prepare the composite. Black-Right-Pointing-Pointer The as-prepared composite shows spherical and porous appearance. Black-Right-Pointing-Pointer The composite shows nearly the same cycleability as commercial graphite in 20 cycles. Black-Right-Pointing-Pointer The composite shows a reversible capacity of 552 mAh/g at the 20th cycle. - Abstract: Using nano-Si, glucose and flake graphite of {approx}0.5 {mu}m as raw materials, flake graphite/silicon/carbon composite is successfully synthesized via spray drying and subsequent pyrolysis. The samples are characterized by XRD, SEM, TEM and electrochemical measurements. The composite is composed of flake graphite, nano-Si and amorphous glucose-pyrolyzed carbon and presents good spherical appearance. Some micron pores arising from the decomposition of glucose exist on the surface of the composite particles. The composite has a high reversible capacity of 602.7 mAh/g with an initial coulombic efficiency of 69.71%, and shows nearly the same cycleability as the commercial graphite in 20 cycles. Both the glucose-pyrolyzed carbon and the micron pores play important roles in improving the cycleability of the composite. The flake graphite/silicon/carbon composite electrode is a potential alternative to graphite for high energy-density lithium ion batteries.

Preparation and characterization of proton exchange poly (ether sulfone)s membranes grafted propane sulfonic acid on pendant phenyl groups

International Nuclear Information System (INIS)

Lim, Youngdon; Seo, Dongwan; Hossain, Md. Awlad; Lee, Soonho; Lim, Jinseong; Jang, Hohyoun; Hong, Taehoon; Kim,; Kim, Whangi

2014-01-01

Poly(ether sulfone)s containing hexaphenyl (PHP) was prepared by 1,2-bis(4-hydroxyphenyl)-3,4,5,6-tetraphenylbenzene, 4,4-hydroxyphenylsulfone, and 4,4-fluorophenylsulfone, followed bromination on phenyl groups to produce brominated PHP (Br-PHP). Grafted sulfonated poly(ether sulfone)s containing hexaphenyl (GSPHP) were prepared from Br-PHP and 3-bromopropane sulfonic acid with potassium salt and copper powder. The salt form was converted to free acid using 1 M sulfuric acid solution. All these membranes were cast from dimethylacetamide (DMAc). The structural properties of the synthesized polymers were investigated by 1 H-NMR spectroscopy. The membranes were studied with regard to ion exchange capacity (IEC), water uptake, Fenton test, and proton conductivity. These grafted polymer membranes were compared with normal sulfonated poly(ether sulfone)s and Nafion

A study of new anhydrous, conducting membranes based on composites of aprotic ionic liquid and cross-linked SPEEK for fuel cell application

International Nuclear Information System (INIS)

Malik, Rajender Singh; Verma, Pawan; Choudhary, Veena

2015-01-01

Highlights: • New composite membranes based on SPEEK/EG/IL were fabricated. • Composite membranes exhibit good thermal stability than neat SPEEK and XSPEEK membrane. • Proton conductivity of all composite membranes increased with temperature and amount of ionic liquid. • Proton conductivity was measured under anhydrous condition in the temperature ranging from 30–140 °C. - Abstract: The present study describe the preparation and characterisation of anhydrous proton conducting composite membranes based on sulfonated poly(ether ether ketone) [SPEEK–degree of sulfonation 70–72%]/ethylene glycol [EG]/ionic liquid by solution casting method using water: ethanol (50:50) as solvent. For this purpose several composite membranes were prepared by mixing solution of SPEEK/ethylene glycol (67:33 wt %) in water:ethanol with varying amounts of 1-butyl-3-methyl-imidazolium trifluromethanesulfonate [bmim][OTf] ionic liquid. The cross-linking of SPEEK was carried out by thermal treatment i.e. by heating in vacuum oven at 80 °C (2 h), 100 °C (2 h), 120 °C (2 h) and 135 °C for 16 h. Ethylene glycol was used as a cross-linker for SPEEK to reduce the leaching out of ionic liquid and enhance the mechanical strength of SPEEK membranes. The membranes were characterized for thermal [thermogravimetry analysis], structural [FTIR–ATR], proton conductivity, morphology (XRD, SEM) and leaching out of ionic liquid with water. FTIR studies clearly showed the interactions between SPEEK, EG and ionic liquid. The proton conductivity and dynamic mechanical properties of the composite membranes were investigated at elevated temperature and under anhydrous conditions. Proton conductivity of all the membranes measured in the temperature range of 30–140 °C under anhydrous conditions was in the range of 10 −3 Scm −1 which showed an increase with increase in temperature and amount of ionic liquid

Electrical and thermal properties of graphite/polyaniline composites

Energy Technology Data Exchange (ETDEWEB)

Bourdo, Shawn E., E-mail: sxbourdo@ualr.edu [Center for Integrative Nanotechnology Sciences, University of Arkansas at Little Rock, 2801 South University Avenue, Little Rock, AR 72204 (United States); Warford, Brock A.; Viswanathan, Tito [Department of Chemistry, University of Arkansas at Little Rock, 2801 South University Avenue, Little Rock, AR 72204 (United States)

2012-12-15

A composite of a carbon allotrope (graphite) and an inherently conducting polymer, polyaniline (PANI), has been prepared that exhibits an electrical conductivity greater than either of the two components. An almost 2-fold increase in the bulk conductivity occurs when only a small mass fraction of polyaniline exists in the composite (91% graphite/ 9% polyaniline, by mass). This increase in dc electrical conductivity is curious since in most cases a composite material will exhibit a conductivity somewhere between the two individual components, unless a modification to the electronic nature of the material occurs. In order to elucidate the fundamental electrical properties of the composite we have performed variable temperature conductivity measurements to better understand the nature of conduction in these materials. The results from these studies suggest a change in the mechanism of conduction as the amount of polyaniline is increased in the composite. Along with superior electrical properties, the composites exhibit an increase in thermal stability as compared to the graphite. - Graphical abstract: (Left) Room temperature electrical conductivity of G-PANI composites at different mass ratios. (Right) Electrical conductivity of G-PANI composites at temperatures from 5 K to 300 K. Highlights: Black-Right-Pointing-Pointer Composites of graphite and polyaniline have been synthesized with unique electrical and thermal properties. Black-Right-Pointing-Pointer Certain G-PANI composites are more conductive and more thermally stable than graphite alone. Black-Right-Pointing-Pointer G-PANI composites exhibit a larger conductivity ratio with respect to temperature than graphite alone.

Thermophysical properties estimation of paraffin/graphite composite phase change material using an inverse method

International Nuclear Information System (INIS)

Lachheb, Mohamed; Karkri, Mustapha; Albouchi, Fethi; Mzali, Foued; Nasrallah, Sassi Ben

2014-01-01

Highlights: • Preparation of paraffin/graphite composites by uni-axial compression technique. • Measurement of thermophysical properties of paraffin/graphite using the periodic method. • Measurement of the experimental densities of paraffin/graphite composites. • Prediction of the effective thermal conductivity using analytical models. - Abstract: In this paper, two types of graphite were combined with paraffin in an attempt to improve thermal conductivity of paraffin phase change material (PCM): Synthetic graphite (Timrex SFG75) and graphite waste obtained from damaged Tubular graphite Heat Exchangers. These paraffin/graphite phase change material (PCM) composites are prepared by the cold uniaxial compression technique and the thermophysical properties were estimated using a periodic temperature method and an inverse technique. Results showed that the thermal conductivity and thermal diffusivity are greatly influenced by the graphite addition

Adhesive properties and adhesive joints strength of graphite/epoxy composites

Science.gov (United States)

Rudawska, Anna; Stančeková, Dana; Cubonova, Nadezda; Vitenko, Tetiana; Müller, Miroslav; Valášek, Petr

2017-05-01

The article presents the results of experimental research of the adhesive joints strength of graphite/epoxy composites and the results of the surface free energy of the composite surfaces. Two types of graphite/epoxy composites with different thickness were tested which are used to aircraft structure. The single-lap adhesive joints of epoxy composites were considered. Adhesive properties were described by surface free energy. Owens-Wendt method was used to determine surface free energy. The epoxy two-component adhesive was used to preparing the adhesive joints. Zwick/Roell 100 strength device were used to determination the shear strength of adhesive joints of epoxy composites. The strength test results showed that the highest value was obtained for adhesive joints of graphite-epoxy composite of smaller material thickness (0.48 mm). Statistical analysis of the results obtained, the study showed statistically significant differences between the values of the strength of the confidence level of 0.95. The statistical analysis of the results also showed that there are no statistical significant differences in average values of surface free energy (0.95 confidence level). It was noted that in each of the results the dispersion component of surface free energy was much greater than polar component of surface free energy.

Dry Sliding Wear Behavior of Spark Plasma Sintered Fe-Based Bulk Metallic Glass/Graphite Composites

Directory of Open Access Journals (Sweden)

Xiulin Ji

2016-09-01

Full Text Available Bulk metallic glass (BMG and BMG-graphite composites were fabricated using spark plasma sintering at the sintering temperature of 575 °C and holding time of 15 min. The sintered composites exhibited partial crystallization and the presence of distributed porosity and graphite particles. The effect of graphite reinforcement on the tribological properties of the BMG/graphite composites was investigated using dry ball-on-disc sliding wear tests. The reinforcement of graphite resulted in a reduction in both the wear rate and the coefficient of friction as compared to monolithic BMG samples. The wear surfaces of BMG/graphite composites showed regions of localized wear loss due to microcracking and fracture, as was also the case with the regions covered with graphite-rich protective film due to smearing of pulled off graphite particles.

Absorption infrared spectra of interaction products of cyclic polyethers 18-crown-6 and dibenzo-18-crown-6 with uranyl dinitrate hexahydrate

International Nuclear Information System (INIS)

Chumaevskij, N.A.; Belomestnykh, V.I.; Razgonyaeva, G.A.; Shabel'nik, K.S.; Afanas'eva, E.E.

1988-01-01

Using the method of IR spectroscopy it is established that during interaction of uranyl nitrate hexahydrate (UNH) with crown-ethers under investigation macrocycles adhere to UO 2 2+ via hydrogen bonds between water molecules and oxygen of polyethers. Interaction of UNH with the above-mentioned crowns leads to conformational rearrangement of cycles of polyethers and improvement of their symmetry, reflecting in noticeable simplification of IR spectra of interaction products as compared to spectra of initial cyclic polyethers

Method of producing exfoliated graphite composite compositions for fuel cell flow field plates

Energy Technology Data Exchange (ETDEWEB)

Zhamu, Aruna; Shi, Jinjun; Guo, Jiusheng; Jang, Bor Z

2014-04-08

A method of producing an electrically conductive composite composition, which is particularly useful for fuel cell bipolar plate applications. The method comprises: (a) providing a supply of expandable graphite powder; (b) providing a supply of a non-expandable powder component comprising a binder or matrix material; (c) blending the expandable graphite with the non-expandable powder component to form a powder mixture wherein the non-expandable powder component is in the amount of between 3% and 60% by weight based on the total weight of the powder mixture; (d) exposing the powder mixture to a temperature sufficient for exfoliating the expandable graphite to obtain a compressible mixture comprising expanded graphite worms and the non-expandable component; (e) compressing the compressible mixture at a pressure within the range of from about 5 psi to about 50,000 psi in predetermined directions into predetermined forms of cohered graphite composite compact; and (f) treating the so-formed cohered graphite composite to activate the binder or matrix material thereby promoting adhesion within the compact to produce the desired composite composition. Preferably, the non-expandable powder component further comprises an isotropy-promoting agent such as non-expandable graphite particles. Further preferably, step (e) comprises compressing the mixture in at least two directions. The method leads to composite plates with exceptionally high thickness-direction electrical conductivity.

Mesostructure of graphite composite and its lifetime

OpenAIRE

Zhmurikov, Evgenij

2015-01-01

This review is devoted to the application of graphite and graphite composites in science and technology. Structure and electrical properties, as so technological aspects of producing of high strength artificial graphite and dynamics of its destruction are considered. These type of graphite are traditionally used in the nuclear industry. Generally, the review relies, on the original results and concentrates on actual problems of application and testing of graphite materials in modern nuclear p...

Bias voltage dependence of molecular orientation of dialkyl ketone and fatty acid alkyl ester at the liquid–graphite interface

Energy Technology Data Exchange (ETDEWEB)

Hibino, Masahiro, E-mail: hibino@mmm.muroran-it.ac.jp [Department of Applied Sciences, Muroran Institute of Technology, 27-1 Mizumoto-cho, Muroran 050-8585 (Japan); Tsuchiya, Hiroshi [Department of Applied Physics, Nagoya University, Furo-cho, Chikusa-ku, Nagoya 464-8601 (Japan)

2014-10-30

Graphical abstract: - Highlights: • Self-assembled monolayers (SAMs) of 18-pentatriacontanone (as ketone) and stearyl stearate (as ester) were formed on a graphite surface at the liquid–solid interface. • Orientations of the molecules in SAMs on the substrate were studied by scanning tunneling microscopy. • A perpendicular carbon skeleton-plane orientation with the CO pointing up on the surface is favorable for a substrate with negative charge and vice versa. - Abstract: Molecular orientations of self-assembled 18-pentatriacontanone (as ketone) and stearyl stearate (as ester) monolayers adsorbed on a graphite surface were studied by scanning tunneling microscopy (STM) at the liquid–solid interface. At a positive sample bias, the central areas of the dialkyl ketone and fatty acid alkyl ester molecules in the STM images appeared as two bright regions on both sides of a dim spot and a bright region on one side of a dim spot, whereas at a negative sample bias, the areas appeared dim. This contrast variation indicates that a perpendicular carbon skeleton-plane orientation with the CO pointing down on the surface is favorable for a substrate with positive charge and vice versa because of the greater electronegativity of the oxygen atom. Upon the bias voltage reversal, the delay time for the STM image contrast change in the region was observed on a time scale of minutes. The difference between the delay time lengths for the direction of bias polarity change indicates that the perpendicular configuration with CO pointing up is more stable than that with CO pointing down. These results indicate that the use of an electric field along a direction vertical to the monolayer on the substrate provides control over the orientations of the molecules between two stable states at the liquid–solid interface.

Replication of Micro pillars by PEEK injection moulding with CrN coated Ni tool

DEFF Research Database (Denmark)

Zhang, Yang; Hansen, Hans Nørgaard; Sørensen, Søren

2015-01-01

A micro-structured nickel insert was investigatedfor polyether ether ketone (PEEK) injection moulding. Themicro-features were circular holes 4 μm in diameter and2 μm deep, with a 2-μm edge-to-edge distance. Six thousand moulding cycles were operated. Half of the insert was coatedby approximately...

Modulation of the gene expression of annulus fibrosus-derived stem cells using poly(ether carbonate urethane)urea scaffolds of tunable elasticity.

Science.gov (United States)

Zhu, Caihong; Li, Jun; Liu, Chen; Zhou, Pinghui; Yang, Huilin; Li, Bin

2016-01-01

Annulus fibrosus (AF) injuries commonly lead to substantial deterioration of the intervertebral disc (IVD). While tissue engineering has recently evolved into a promising approach for AF regeneration, it remains challenging due to the cellular, biochemical, and mechanical heterogeneity of AF tissue. In this study, we explored the use of AF-derived stem cells (AFSCs) to achieve diversified differentiation of cells for AF tissue engineering. Since the differentiation of stem cells relies significantly on the elasticity of the substrate, we synthesized a series of biodegradable poly(ether carbonate urethane)urea (PECUU) materials whose elasticity approximated that of native AF tissue. When AFSCs were cultured on electrospun PECUU fibrous scaffolds, the gene expression of collagen-I in the cells increased with the elasticity of scaffold material, whereas the expression of collagen-II and aggrecan genes showed an opposite trend. At the protein level, the content of collagen-I gradually increased with substrate elasticity, while collagen-II and GAG contents decreased. In addition, the cell traction forces (CTFs) of AFSCs gradually decreased with scaffold elasticity. Such substrate elasticity-dependent changes of AFSCs were similar to the gradual transition in the genetic, biochemical, and biomechanical characteristics of cells from inner to outer regions of native AF tissue. Together, findings from this study indicate that AFSCs, depending on the substrate elasticity, have strong tendencies to differentiate into various types of AF-like cells, thereby providing a solid foundation for the tissue engineering applications of AFSCs. Repairing the annulus fibrosus (AF) of intervertebral disc (IVD) is critical for the treatment of disc degeneration disease, but remains challenging due to the significant heterogeneity of AF tissue. Previously, we have identified rabbit AF-derived stem cells (AFSCs), which are AF tissue-specific and hold promise for AF regeneration. In this

Nitrile crosslinked polyphenyl-quinoxaline/graphite fiber composites

Science.gov (United States)

Alston, W. B.

1976-01-01

Studies were performed to reduce the 600 F thermoplasticity of polyphenylquinoxaline (PPQ) matrix resins by introducing crosslinking by the reaction of terminal nitrile groups. Seven solvents and solvent mixtures were studied as the crosslinking catalysts and used to fabricate crosslinked PPQ/HMS graphite fiber composites. The room temperature and 600 F composite mechanical properties after short time and prolonged 600 F air exposure and the 600 F composite weight loss were determined and compared to those properties of high molecular weight, linear PPQ/HMS graphite fiber composites.

The effect of polyether functional polydimethylsiloxane on surface and thermal properties of waterborne polyurethane

Science.gov (United States)

Zheng, Guikai; Lu, Ming; Rui, Xiaoping

2017-03-01

Waterborne polyurethanes (WPU) modified with polyether functional polydimethylsiloxane (PDMS) were synthesized by pre-polymerization method using isophorone diisocyanate (IPDI) and 1,4-butanediol (BDO) as hard segments and polybutylene adipate glycol (PBA) and polyether functional PDMS as soft segments. The effect of polyether functional PDMS on phase separation, thermal properties, surface properties including surface composition, morphology and wettability were investigated by FTIR, contact angle measurements, ARXPS, SEM-EDS, AFM, TG and DSC. The results showed that the compatibility between urethane hard segment and PDMS modified with polyether was good, and there was no distinct phase separation in both bulk and surface of WPU films. The degradation temperature and low temperature flexibility increased with increasing amounts of polyether functional PDMS. The enrichment of polyether functional PDMS with low surface energy on the surface imparted excellent hydrophobicity to WPU films.

Laminated exfoliated graphite composite-metal compositions for fuel cell flow field plate or bipolar plate applications

Science.gov (United States)

Zhamu, Aruna; Shi, Jinjun; Guo, Jiusheng; Jang, Bor Z

2014-05-20

An electrically conductive laminate composition for fuel cell flow field plate or bipolar plate applications. The laminate composition comprises at least a thin metal sheet having two opposed exterior surfaces and a first exfoliated graphite composite sheet bonded to the first of the two exterior surfaces of the metal sheet wherein the exfoliated graphite composite sheet comprises: (a) expanded or exfoliated graphite and (b) a binder or matrix material to bond the expanded graphite for forming a cohered sheet, wherein the binder or matrix material is between 3% and 60% by weight based on the total weight of the first exfoliated graphite composite sheet. Preferably, the first exfoliated graphite composite sheet further comprises particles of non-expandable graphite or carbon in the amount of between 3% and 60% by weight based on the total weight of the non-expandable particles and the expanded graphite. Further preferably, the laminate comprises a second exfoliated graphite composite sheet bonded to the second surface of the metal sheet to form a three-layer laminate. Surface flow channels and other desired geometric features can be built onto the exterior surfaces of the laminate to form a flow field plate or bipolar plate. The resulting laminate has an exceptionally high thickness-direction conductivity and excellent resistance to gas permeation.

Nanostructured Polyelectrolytes Based on SPEEK/TiO2 for Direct Ethanol Fuel Cells (DEFCs)

OpenAIRE

Dutra Filho, José Carlos; Santos, Tamirys Rodrigues dos; Gomes, Aílton de Souza

2014-01-01

Proton-conducting hybrid membranes consisting of poly(ether ether ketone) sulfonated (SPEEK) and titanium oxide (TiO2) were prepared using the sol-gel technique for application in direct ethanol fuel cells. The effect from TiO2 incorporation on membrane properties such as ethanol uptake, pervaporation and proton conductivity was investigated. The uptake and permeated flux decreased with increasing content of TiO2. The ethanol permeability was about one order of magnitude smaller than Nafion® ...

Laser surface modification of PEEK

Energy Technology Data Exchange (ETDEWEB)

Riveiro, A., E-mail: ariveiro@uvigo.es [Applied Physics Department, University of Vigo ETSII, Lagoas-Marcosende, 9, Vigo 36310 (Spain); Centro Universitario de la Defensa, Escuela Naval Militar, Plaza de Espana 2, 36920 Marin (Spain); Soto, R.; Comesana, R.; Boutinguiza, M.; Val, J. del; Quintero, F.; Lusquinos, F.; Pou, J. [Applied Physics Department, University of Vigo ETSII, Lagoas-Marcosende, 9, Vigo 36310 (Spain)

2012-09-15

Highlights: Black-Right-Pointing-Pointer Role of laser irradiation wavelength on the surface modification of PEEK (polyether-ether-ketone) was investigated. Black-Right-Pointing-Pointer Adequate processing conditions to improve wettability, roughness, and cell adhesion characteristics are determined. Black-Right-Pointing-Pointer A design of experiments (DOE) methodology was performed. Black-Right-Pointing-Pointer UV (355 nm) radiation is the most promising laser radiation for improving the adhesive surface properties of PEEK. - Abstract: Polyether-ether-ketone (PEEK) is a synthetic thermoplastic polymer with excellent mechanical and chemical properties, which make it attractive for the field of reconstructive surgery. Nevertheless, this material has a poor interfacial biocompatibility due to its large chemical stability which induces poor adhesive bonding properties. The possibilities of enhancing the PEEK adhesive properties by laser treatments have been explored in the past. This paper presents a systematic approach to discern the role of laser irradiation wavelength on the surface modification of PEEK under three laser wavelengths ({lambda} = 1064, 532, and 355 nm) with the aim to determine the most adequate processing conditions to increase the roughness and wettability, the main parameters affecting cell adhesion characteristics of implants. Overall results show that the ultraviolet ({lambda} = 355 nm) laser radiation is the most suitable one to enhance surface wettability of PEEK.

Characterization of {sup 14}C in neutron irradiated NBG-25 nuclear graphite

Energy Technology Data Exchange (ETDEWEB)

LaBrier, Daniel, E-mail: labrdani@isu.edu; Dunzik-Gougar, Mary Lou

2014-05-01

Recent studies suggest that the highest concentration of {sup 14}C contamination present in reactor-irradiated graphite exists on the surfaces and within near-surface layers. Surface-sensitive analysis techniques (XPS, ToF-SIMS, SEM/EDS and Raman) were employed to determine the chemical nature of {sup 14}C on irradiated NBG-25 (nuclear grade) graphite surfaces. Several {sup 14}C precursor species are identified on the surfaces of irradiated NBG-25; the quantities of these species decrease at sub-surface depths, which further suggests that {sup 14}C formation is predominantly a surface-concentrated phenomenon. The elevated presence of several surface oxide complexes on irradiated NBG-25 surfaces are attributed directly to neutron irradiation. Larger numbers of oxide bonds were found on irradiated NBG-25 surfaces (when compared to unirradiated samples) in the form of interlattice (e.g. ether) and dangling (e.g. carboxylate and ketone) bonds; the quantities of these bond types also decrease with increasing sub-surface depths.

Transition from glass to graphite in manufacture of composite aircraft structure

Science.gov (United States)

Buffum, H. E.; Thompson, V. S.

1978-01-01

The transition from fiberglass reinforced plastic composites to graphite reinforced plastic composites is described. Structural fiberglass design and manufacturing background are summarized. How this experience provides a technology base for moving into graphite composite secondary structure and then to composite primary structure is considered. The technical requirements that must be fulfilled in the transition from glass to graphite composite structure are also included.

A study on wear behaviour of Al/6101/graphite composites

Directory of Open Access Journals (Sweden)

Pardeep Sharma

2017-03-01

Full Text Available The current research work scrutinizes aluminium alloy 6101-graphite composites for their mechanical and tribological behaviour in dry sliding environments. The orthodox liquid casting technique had been used for the manufacturing of composite materials and imperilled to T6 heat treatment. The content of reinforcement particles was taken as 0, 4, 8, 12 and 16 wt.% of graphite to ascertain it is prospective as self-lubricating reinforcement in sliding wear environments. Hardness, tensile strength and flexural strength of cast Al6101 metal matrix and manufactured composites were evaluated. Hardness, tensile strength and flexural strength decreases with increasing volume fraction of graphite reinforcement as compared to cast Al6101 metal matrix. Wear tests were performed on pin on disc apparatus to assess the tribological behaviour of composites and to determine the optimum volume fraction of graphite for its minimum wear rate. Wear rate reduces with increase in graphite volume fraction and minimum wear rate was attained at 4 wt.% graphite. The wear was found to decrease with increase in sliding distance. The average co-efficient of friction also reduces with graphite addition and its minimum value was found to be at 4 wt.% graphite. The worn surfaces of wear specimens were studied through scanning electron microscopy. The occurrence of 4 wt.% of graphite reinforcement in the composites can reveal loftier wear possessions as compared to cast Al6101 metal matrix.

Study on paraffin/expanded graphite composite phase change thermal energy storage material

International Nuclear Information System (INIS)

Zhang Zhengguo; Fang Xiaoming

2006-01-01

A paraffin/expanded graphite composite phase change thermal energy storage material was prepared by absorbing the paraffin into an expanded graphite that has an excellent absorbability. In such a composite, the paraffin serves as a latent heat storage material and the expanded graphite acts as the supporting material, which prevents leakage of the melted paraffin from its porous structure due to the capillary and surface tension forces. The inherent structure of the expanded graphite did not change in the composite material. The solid-liquid phase change temperature of the composite PCM was the same as that of the paraffin, and the latent heat of the paraffin/expanded graphite composite material was equivalent to the calculated value based on the mass ratio of the paraffin in the composite. The heat transfer rate of the paraffin/expanded graphite composite was obviously higher than that of the paraffin due to the combination with the expanded graphite that had a high thermal conductivity. The prepared paraffin/expanded graphite composite phase change material had a large thermal storage capacity and improved thermal conductivity and did not experience liquid leakage during its solid-liquid phase change

The breakdown of vinyl ethers as a two-center synchronous reaction

Science.gov (United States)

Pokidova, T. S.; Shestakov, A. F.

2009-11-01

The experimental data on the molecular decomposition of vinyl ethers of various structures to alkanes and the corresponding aldehydes or ketones in the gas phase were analyzed using the method of intersecting parabolas. The enthalpies and kinetic parameters of decomposition were calculated for 17 reactions. The breakdown of ethers is a two-center concerted reaction characterized by a very high classical potential barrier to the thermally neutral reaction (180-190 kJ/mol). The kinetic parameters (activation energies and rate constants) of back reactions of the formation of vinyl ethers in the addition of aldehydes or ketones to alkanes were calculated using the method of intersecting parabolas. The factors that influenced the activation energy of the decomposition and formation of ethers were discussed. Quantum-chemical calculations of several vinyl ether decomposition reactions were performed. Ether formation reactions were compared with the formation of unsaturated alcohols as competitive reactions, which can occur in the interaction of carbonyl compounds with alkenes.

Development of design data for graphite reinforced epoxy and polyimide composites

Science.gov (United States)

Scheck, W. G.

1974-01-01

Processing techniques and design data were characterized for a graphite/epoxy composite system that is useful from 75 K to 450 K, and a graphite/polyimide composite system that is useful from 75 K to 589 K. The Monsanto 710 polyimide resin was selected as the resin to be characterized and used with the graphite fiber reinforcement. Material was purchased using the prepreg specification for the design data generation for both the HT-S/710 and HM-S/710 graphite/polyimide composite system. Lamina and laminate properties were determined at 75 K, 297 K, and 589 K. The test results obtained on the skin-stringer components proved that graphite/polyimide composites can be reliably designed and analyzed much like graphite/epoxy composites. The design data generated in the program includes the standard static mechanical properties, biaxial strain data, creep, fatigue, aging, and thick laminate data.

Influence of polyether ring size and of the nature of substituents on the yields of paramagnetic centers in γ-irradiated mono- and dibenzosubstituted crown ethers at 77 K

International Nuclear Information System (INIS)

Nesterov, S.V.; Panov, O.Yu.

1998-01-01

Intermediates stabilized in γ-irradiated mono- and dibenzosubstituted crown ethers are studied by ESR spectroscopy at 77 K. PhO · radicals and radicals with H-atom abstraction from polyether ring are the main products at low temperature γ-radiolysis. The nature of radicals produced in radiolysis and the yield of radicals, G R , depend on macroring size and on the number of aromatic substituents. Negative deviation from additive rule in function of G R versus ε of substituents is an evidence of efficient transfer of adsorbed energy to the π-system of aromatic group. (author)

Sulfonated poly(ether ether ketone) based membranes for direct ethanol fuel cells

OpenAIRE

Roelofs, K.S.

2010-01-01

The decreasing availability of fossil fuels and the increasing impact of greenhouse gases on the environment lead to an extensive development of more efficient or renewable energy sources. The direct alcohol fuel cell (DAFC) as a portable energy source is a promising and fast growing technology which meets these demands. Up to now, methanol is mostly studied as a fuel for these devices, however, applying ethanol has some evident advantages over methanol. The major challenges in direct ethanol...

Composite perfluorohydrocarbon membranes, their preparation and use

Energy Technology Data Exchange (ETDEWEB)

Ding, Yong; Bikson, Benjamin

2017-04-04

Composite porous hydrophobic membranes are prepared by forming a perfluorohydrocarbon layer on the surface of a preformed porous polymeric substrate. The substrate can be formed from poly (aryl ether ketone) and a perfluorohydrocarbon layer can be chemically grafted to the surface of the substrate. The membranes can be utilized for a broad range of fluid separations, such as microfiltration, nanofiltration, ultrafiltration as membrane contactors for membrane distillation and for degassing and dewatering of fluids. The membranes can further contain a dense ultra-thin perfluorohydrocarbon layer superimposed on the porous poly (aryl ether ketone) substrate and can be utilized as membrane contactors or as gas separation. membranes for natural gas treatment and gas dehydration.

Partial molar volumes of organic solutes in water. XXVII. Two aliphatic polyethers (triglyme, tetraglyme) at temperatures T = 298–573 K and pressures up to 30 MPa

International Nuclear Information System (INIS)

Cibulka, Ivan

2016-01-01

Highlights: • Standard molar volumes of two linear aliphatic polyethers in water are presented. • Data were obtained in the range T from (298 to 573) K and p up to 30 MPa. • Data combined with those obtained previously are analyzed and compared with standard molar volumes of cyclic ethers. - Abstract: Densities of dilute aqueous solutions of two linear aliphatic polyethers: 2,5,8,11-tetraoxadodecane (triethylene glycol dimethyl ether, triglyme) and 2,5,8,11,14-pentaoxapentadecane (tetraethylene glycol dimethyl ether, tetraglyme), measured in the temperature range from (298 to 573) K and at pressures up to 30 MPa using an automated flow vibrating-tube densimeter are reported. Standard molar volumes were evaluated from the measured data. The present values complement previous measurements performed for the title polyethers at atmospheric pressure in the temperature range from (278 to 343) K and extend the knowledge to temperature and pressure ranges in which the data on standard molar volumes for lower members of the homologous series (monoglyme, diglyme) are already available.

Effect of High Energy Radiation on Mechanical Properties of Graphite Fiber Reinforced Composites. M.S. Thesis

Science.gov (United States)

Naranong, N.

1980-01-01

The flexural strength and average modulus of graphite fiber reinforced composites were tested before and after exposure to 0.5 Mev electron radiation and 1.33 Mev gamma radiation by using a three point bending test (ASTM D-790). The irradiation was conducted on vacuum treated samples. Graphite fiber/epoxy (T300/5208), graphite fiber/polyimide (C6000/PMR 15) and graphite fiber/polysulfone (C6000/P1700) composites after being irradiated with 0.5 Mev electron radiation in vacuum up to 5000 Mrad, show increases in stress and modulus of approximately 12% compared with the controls. Graphite fiber/epoxy (T300/5208 and AS/3501-6), after being irradiated with 1.33 Mev gamma radiation up to 360 Mrads, show increases in stress and modulus of approximately 6% at 167 Mrad compared with the controls. Results suggest that the graphite fiber composites studied should withstand the high energy radiation in a space environment for a considerable time, e.g., over 30 years.

Graphite fiber/copper composites prepared by spontaneous infiltration

Science.gov (United States)

Wang, Hongbao; Tao, Zechao; Li, Xiangfen; Yan, Xi; Liu, Zhanjun; Guo, Quangui

2018-05-01

The major bottleneck in developing graphite fiber reinforced copper (GF/Cu) composites is the poor wettability of Cu/graphite system. Alloying element of chromium (Cr) is introduced to improve the wettability of liquid copper on graphite. Sessile drop method experiments illustrate that the contact angle of liquid Cu-Cr (1.0 wt.%) alloy on graphite substrate decreases to 43° at 1300 °C. The improvement of wettability is related to the formation of chromium carbide layer at interface zone. Based on the wetting experiment, a spontaneous infiltration method for preparing GF/Cu composites is proposed. Unidirectional GF preforms are infiltrated by Cu-Cr alloys without external pressure in a tubular furnace. Results reveal that the GF preform can be fully infiltrated by Cu-Cr alloy (8 wt.%) spontaneously when fiber volume fraction is 40%. The coefficient of thermal expansion (CTE) of GF/Cu-Cr (8.0 wt.%) composites is 4.68 × 10-6/K along the longitudinal direction.

Measurements of print-through in graphite fiber epoxy composites

Science.gov (United States)

Jaworske, Donald A.; Jeunnette, Timothy T.; Anzic, Judith M.

1989-01-01

High-reflectance accurate-contour mirrors are needed for solar dynamic space power systems. Graphite fiber epoxy composites are attractive candidates for such applications owing to their high modulus, near-zero coefficient of thermal expansion, and low mass. However, mirrors prepared from graphite fiber epoxy composite substrates often exhibit print-through, a distortion of the surface, which causes a loss in solar specular reflectance. Efforts to develop mirror substrates without print-through distortion require a means of quantifying print-through. Methods have been developed to quantify the degree of print-through in graphite fiber epoxy composite specimens using surface profilometry.

Langmuir and Langmuir-Blodgett films of multifunctional, amphiphilic polyethers with cholesterol moieties.

Science.gov (United States)

Reuter, Sascha; Hofmann, Anna M; Busse, Karsten; Frey, Holger; Kressler, Jörg

2011-03-01

Langmuir films of multifunctional, hydrophilic polyethers containing a hydrophobic cholesterol group (Ch) were studied by surface pressure-mean molecular area (π-mmA) measurements and Brewster angle microscopy (BAM). The polyethers were either homopolymers or diblock copolymers of linear poly(glycerol) (lPG), linear poly(glyceryl glycidyl ether) (lPGG), linear poly(ethylene glycol) (lPEG), or hyperbranched poly(glycerol) (hbPG). Surface pressure measurements revealed that the homopolymers lPG and hbPG did not stay at the water surface after spreading and solvent evaporation, in contrast to lPEG. Because of the incorporation of the Ch group in the polymer structure, stable Langmuir films were formed by Ch-lPG(n), Ch-lPGG(n), and Ch-hbPG(n). The Ch-hbPG(n), Ch-lPEG(n), Ch-lPEG(n)-b-lPG(m), Ch-lPEG(n)-b-lPGG(m), and Ch-lPEG(n)-b-hbPG(m) systems showed an extended plateau region assigned to a phase transition involving the Ch groups. Typical hierarchically ordered morphologies of the LB films on hydrophilic substrates were observed for all Ch-initiated polymers. All LB films showed that Ch of the Ch-initiated homopolymers is able to crystallize. This strong tendency of self-aggregation then triggers further dewetting effects of the respective polyether entities. Fingerlike morphologies are observed for Ch-lPEG(69), since the lPEG(69) entity is able to undergo crystallization after transfer onto the silicon substrate.

SEM/XPS analysis of fractured adhesively bonded graphite fibre surface resin-rich/graphite fibre composites

Science.gov (United States)

Devilbiss, T. A.; Wightman, J. P.; Progar, D. J.

1988-01-01

Samples of graphite fiber-reinforced polyimide were fabricated allowing the resin to accumulate at the composite surface. These surface resin-rich composites were then bonded together and tested for lap shear strength both before and after thermal aging. Lap shear strength did not appear to show a significant improvement over that previously recorded for resin-poor samples and was shown to decrease with increasing aging time and temperature.

Protein Compatible Polymer Brushes on Polymeric Substrates Prepared by Surface-Initiated Transfer Radica Polymerization

DEFF Research Database (Denmark)

Fristrup, Charlotte Juel; Eskimergen, Rüya; Burkrinsky, J.T.

2008-01-01

have been made with model systems of poly(ether ether ketone) (PEEK) films as they can easily be functionalized [1]. Moreover, the inert material polypropylene has successfully beel! activated using a photochemical method [2]. Different polymers including PEG-like matenals have been investigated...... as coating materials. ATR FTIR, water contact angle measurements, Thermal Gravimetric Analysis (TGA), and X-ray Photoelectron Spectroscopy (XPS) confirmed that hydrophilic polymers have been grafted from the surface. The surface topography which was evaluated by Atomic Force Microscopy (AFM) did not change...

Cation-exchange membranes: comparison of homopolymer, block copolymer, and heterogeneous membranes

Czech Academy of Sciences Publication Activity Database

Schauer, Jan; Llanos, J.; Žitka, Jan; Hnát, J.; Bouzek, K.

2012-01-01

Roč. 124, SI 1 (2012), E66-E72 ISSN 0021-8995 R&D Projects: GA MŠk(CZ) 7E08005 EU Projects: European Commission(XE) 212903 - WELTEMP Institutional research plan: CEZ:AV0Z40500505 Keywords : cation-exchange membranes * poly(phenylene oxide) * poly(ether ketones ) Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 1.395, year: 2012

In Situ Preparation of Polyether Amine Functionalized MWCNT Nanofiller as Reinforcing Agents

Directory of Open Access Journals (Sweden)

Ayber Yıldrım

2014-01-01

Full Text Available In situ preparation of polyether amine functionalized cross-linked multiwalled carbon nanotube (MWCNT nanofillers may improve the thermal and mechanical properties of the composites in which they are used as reinforcing agents. The reduction and functionalization of MWCNT using ethylenediamine in the presence of polyether amine produced stitched MWCNT's due to the presence of two amine (–NH2 functionalities on both sides of the polymer. Polyether amine was chosen to polymerize the carboxylated MWCNT due to its potential to form bonds with the amino groups and carboxyl groups of MWCNT which produces a resin used as polymeric matrix for nanocomposite materials. The attachment of the polyether amine (Jeffamine groups was verified by TGA, FT-IR, XRD, SEM, and Raman spectroscopy. The temperature at which the curing enthalpy is maximum, observed by DSC, was shifted to higher values by adding functionalized MWCNT. SEM images show the polymer formation between MWCNT sheets.

Microstructural characteristics, mechanical and wear behaviour of aluminium matrix hybrid composites reinforced with alumina, rice husk ash and graphite

Directory of Open Access Journals (Sweden)

Kenneth Kanayo Alaneme

2015-09-01

Full Text Available The microstructural characteristics, mechanical and wear behaviour of Aluminium matrix hybrid composites reinforced with alumina, rice husk ash (RHA and graphite were investigated. Alumina, RHA and graphite mixed in varied weight ratios were utilized to prepare 10 wt% hybrid reinforced Al-Mg-Si alloy based composites using two-step stir casting. Hardness, tensile properties, scanning electron microscopy, and wear tests were used to characterize the composites produced. The results show that Hardness decreases with increase in the weight ratio of RHA and graphite in the composites; and with RHA content greater than 50%, the effect of graphite on the hardness becomes less significant. The tensile strength for the composites containing o.5wt% graphite and up to 50% RHA was observed to be higher than that of the composites without graphite. The toughness values for the composites containing 0.5wt% graphite were in all cases higher than that of the composites without graphite. The % Elongation for all composites produced was within the range of 10–13% and the values were invariant to the RHA and graphite content. The tensile fracture surface morphology in all the composites produced was identical characterized with the presence of reinforcing particles housed in ductile dimples. The composites without graphite exhibited greater wear susceptibility in comparison to the composite grades containing graphite. However the wear resistance decreased with increase in the graphite content from 0.5 to 1.5 wt%.

Preparation and characterization of stearic acid/expanded graphite composites as thermal energy storage materials

International Nuclear Information System (INIS)

Fang, Guiyin; Li, Hui; Chen, Zhi; Liu, Xu

2010-01-01

Stearic acid/expanded graphite composites with different mass ratios were prepared by absorbing liquid stearic acid into the expanded graphite. In the composite materials, the stearic acid was used as the phase change material for thermal energy storage, and the expanded graphite acted as the supporting material. Fourier transformation infrared spectroscopy, X-ray diffraction, scanning electron microscopy and thermal diffusivity measurement were used to determine the chemical structure, crystalline phase, microstructure and thermal diffusivity of the composites, respectively. The thermal properties and thermal stability were investigated by differential scanning calorimetry and thermogravimetric analysis. The thermal analysis results indicated that the materials exhibited the same phase transition characteristics as the stearic acid and their latent heats were approximately the same as the values calculated based on the weight fraction of the stearic acid in the composites. The microstructural analysis results showed that the stearic acid was well absorbed in the porous network of the expanded graphite, and there was no leakage of the stearic acid from the composites even when it was in the molten state.

A reliability based stress-life evaluation of aluminium-graphite particulate composites

International Nuclear Information System (INIS)

Achutha, M.V.; Sridhara, B.K.; Abdul Budan, D.

2008-01-01

Fatigue tests were conducted on sand cast aluminium-graphite composite specimens on Rotating Beam Fatigue Testing Machine with three different stress levels. Aluminium-graphite (LM 25-5% graphite) composite was processed by closed mould sand casting method. Three-stress level fatigue test program was planned for carrying out fatigue experiments. Three different stress levels selected for fatigue experiments were a fraction of ultimate tensile strength. Statistical design of fatigue experiments was carried out to determine the sample size at each stress level. Experimental results are presented in the form of stress-life (S-N) curves and reliability-stress-life (R-S-N) curves, which are helpful for designers. The S-N curve of the aluminium-graphite composite was compared with its matrix alloy LM 25. Comparison revealed that the fatigue behaviour of the aluminium-graphite composite is superior to that of the matrix alloy

Side-chain sulfonated poly(ether sulfone)s for PEM applications

Energy Technology Data Exchange (ETDEWEB)

Meier-Haack, J.; Butwilowski, W.; Quetschke, A.; Vogel, C. [Leibniz Institute of Polymer Research Dresden, Dresden (Germany)

2010-07-01

Copoly(arylene ether sulfone)s from bis-(4-fluoro phenyl)sulfone (DFDPhS), bis(4-trimethylsiloxy phenyl)sulfone (DHDPhS), and 2,5-diphenylhydroquinone trimethylsilylether (Bis-TMS-DPhHQ) were obtained by nucleophilic displacement polycondensation with high molecular weights (M{sub n} up to 70,000 g/mol; {eta}{sub inh} up to 0.93 dl/g) and narrow molecular weight distributions (2.1 - 2.9). All copolymers showed a single glass-transition temperature (T{sub g}) around 230 C. Upon sulfonation with concentrated sulfuric acid, the T{sub g}s (from samples in the protonated form) were shifted to higher temperatures (+ 35 {+-} 5 C). NMR spectra and the determined ion-exchange capacities (IEC; 1.46 - 2.05 mmol/g), which were close to the theoretical values, indicating that only the pendant phenyl rings of the 2,5- diphenylhydroquinone moieties in the polymer backbone were sulfonated. Membranes prepared from N-methyl- 2-pyrrolidone (NMP) solutions were transparent and soft. The water-uptake at room temperature increased from 30% to 80% with increasing IEC. Samples from random copolymers with an IEC {>=} 1.8 mmol/g were soluble in water at 90 C. While the proton conductivity of the low IEC samples (random copolymer) (1.46 mmol/g) was lower than that of Nafion {sup registered}, the conductivities of the high IEC samples were superior to Nafion {sup registered}. In general membranes from blockcopolymers showed lower water-uptake, higher dimensional stability and higher proton conductivities as compared to samples from random copolymers with similar monomer composition and ion-exchange capacities. (orig.)

Decoupling ion conductivity and fluid permeation through optimizing hydrophilic channel morphology

Energy Technology Data Exchange (ETDEWEB)

Chu, Peter Po-Jen, E-mail: pjchu@cc.ncu.edu.tw; Fang, Yu-Shin; Tseng, Yu-Chen [Department of Chemistry, National Central University, No. 300, Jhongda Rd., Jhongli City, Taoyuan County 32001, Taiwan (R.O.C.) (China)

2016-05-18

Approaches to improve membrane ion conductivity usually leads to higher degree of swelling, more serious fuel cross-over and often sacrificed membrane mechanical strength. Preserving all three main membrane properties is a tough challenge in searching high ion conducting fuel cell membrane. The long standing dilemma is resolved by decoupling ion conduction and fluid permeation property by creating optimized channel morphology using external electric field poling. Success of this approach is demonstrated in the proton conducting membrane composed of poly(ether sulfones) (PES) and sulfonated poly(ether ether ketone) (sPEEK, degree of sulfonation=50%) composites prepared under electric field poling condition. The external field enhanced the aromatic chain ordering from both sPEEK and PES and improved the miscibility. This induced interaction is conducive to the formation of more densely packed amorphous domains that eventually leads to preferentially ordered hydrophilic proton conducting channels having a average dimension (3 nm) smaller than that in generic sPEEK or Nafion. The narrower but more ordered channel displayed much lower methanol permeability (3.17×10{sup −7} cm{sup 2}/s), and lower swelling ratio (31.20%), while the conductivity (~10{sup −1} S/cm) is higher than that of Nafion, or sPEEK at higher (64%) degree of sulfonation. The composite is chemically stable and highly durable with improved membrane mechanical strength. Nearly 50% increase of DMFC power output is observed using this membrane, and the best power density is recorded at 155 mA/cm{sup 2} (80 °C, 1M Methanol).

Enhancement of Hybrid SPEEK Based Polymer–Cyclodextrin-Silica Inorganic Membrane for Direct Methanol Fuel Cell Application

Directory of Open Access Journals (Sweden)

Tutuk Djoko Kusworo

2017-06-01

  Keywords: Direct Methanol Fuel Cell, Poly(ether ether ketone, cyclodextrin-silica, sulfonation, ionic conductivity. Article History: Received January 18th 2017; Received in revised form April 21st 2017; Accepted June 22nd 2017; Available online How to Cite This Article: Kusworo, T.D., Hakim, M.F. and Hadiyanto, H. (2017 Enhancement of Hybrid SPEEK Based Polymer–Cyclodextrin-Silica Inorganic Membrane for Direct Methanol Fuel Cell Application. International Journal of Renewable Energy Development, 6(2, 165-170. https://doi.org/10.14710/ijred.6.2.165-170

Ion-conductive properties of polyether-based composite electrolytes filled with mesoporous silica, alumina and titania

International Nuclear Information System (INIS)

Tominaga, Yoichi; Endo, Masanori

2013-01-01

Composite polymer electrolytes were prepared consisting of amorphous polyether, Li salt and mesoporous inorganic filler, and we investigated their ion-conductive properties. We synthesized three types of filler, mesoporous silica, alumina and titania (MP-Si, Al, Ti), and characterized their structural and physicochemical properties using SEM, TEM, SAXS and BET surface area measurements. From these measurements, we confirmed that MP fillers have well-defined arrays of mesoporous and hexagonal structures. Dependence on the MP filler content of the glass transition temperature (T g ) revealed that the addition of filler to original polyether-salt electrolyte causes T g decrease, to due to the dissociation of aggregated ions such as triples or crystalline complex domains. The MP-Ti composites had the greatest ionic conductivity (1.4 × 10 −5 S/cm, 7.5 wt% at 30 °C) of all samples, and the values were more than double that of the original. The addition of MP-Ti also increased the lithium transference number, because the electrolyte/filler interface provided active sites that increase mobile Li ions and conducting paths so as to enhance the mobility

Thioether-Bearing Hyperbranched Polyether Polyols with Methionine-Like Side-Chains: A Versatile Platform for Orthogonal Functionalization.

Science.gov (United States)

Seiwert, Jan; Herzberger, Jana; Leibig, Daniel; Frey, Holger

2017-01-01

The synthesis of thioether-bearing hyperbranched polyether polyols based on an AB/AB 2 type copolymerization (cyclic latent monomers) is introduced. The polymers are prepared by anionic ring-opening multibranching copolymerization of glycidol and 2-(methylthio)ethyl glycidyl ether (MTEGE), which is conveniently accessible in a single etherification step. Slow monomer addition provides control over molecular weights. Moderate dispersities (Đ = 1.48-1.85) are obtained, given the hyperbranched structure. In situ 1 H NMR copolymerization kinetics reveal reactivity ratios of r G = 3.7 and r MTEGE = 0.27. Using slow monomer addition, copolymer composition can be systematically varied, allowing for the adjustment of the hydroxyl/thioether ratio, the degree of branching (DB = 0.36-0.48), thermal properties, and cloud point temperatures in aqueous solution in the range of 29-75 °C. Thioether oxidation to sulfoxides enables to tailor the copolymers' solubility profile. Use of these copolymers as a versatile, multifunctional platform for orthogonal modification is highlighted. The methyl sulfide groups can be selectively alkoxylated, using propylene oxide, allyl glycidyl ether, or furfuryl glycidyl ether, resulting in functional hyperbranched polyelectrolytes. Reaction of the alcohol groups with benzyl isocyanate demonstrates successful orthogonal functionalization. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Graphite oxide/β-Ni(OH)2 composites for application in supercapacitors

Science.gov (United States)

Singh, Arvinder; Chandra, Amreesh

2013-06-01

Graphite oxide/β-Ni(OH)2 composites have been investigated as electrode material in supercapacitors. Phase formation of electrode material is investigated using diffraction measurements. Particle shape-size studies show deposition of β-Ni(OH)2 nanoparticles on graphite oxide (GO) sheets. Electrochemical performance of GO/β-Ni(OH)2 composite in supercapacitors is discussed based on the analysis of electrochemical impedance spectroscopy (EIS), cyclic voltammetry (CV) and galvanostatic charge-discharge studies. Excellent energy density of ˜53 Wh/kg in 1M Na2SO4 aqueous electrolyte is reported at power density of ˜1364W/kg. The significance of results is discussed in the paper.

Graphite intercalated polyaniline composite with superior anticorrosive and hydrophobic properties, as protective coating material on steel surfaces

Energy Technology Data Exchange (ETDEWEB)

Rathnayake, R.M.N.M. [National Institute of Fundamental Studies, Kandy (Sri Lanka); Graduate School of Engineering, Toyota Technological Institute, 2-12-1 Hisakata, Tempaku, Nagoya 468-8511 (Japan); Mantilaka, M.M.M.G.P.G. [Sri Lanka Institute of Nanotechnology, Nanotechnology and Science Park, Mahenwatte, Pitipana, Homagama (Sri Lanka); Hara, Masanori; Huang, Hsin-Hui [Graduate School of Engineering, Toyota Technological Institute, 2-12-1 Hisakata, Tempaku, Nagoya 468-8511 (Japan); Wijayasinghe, H.W.M.A.C., E-mail: athula@ifs.ac.lk [National Institute of Fundamental Studies, Kandy (Sri Lanka); Yoshimura, Masamichi [Graduate School of Engineering, Toyota Technological Institute, 2-12-1 Hisakata, Tempaku, Nagoya 468-8511 (Japan); Pitawala, H.M.T.G.A. [Department of Geology, University of Peradeniya, Peradeniya (Sri Lanka)

2017-07-15

Highlights: • In this paper, it has been utilized a novel method to prepare a new composite material of PANI/NPG graphite composite, using NPG vein graphite variety. • It is found that the composite works as an anti-corrosive coating on steel surfaces. Further, the prepared composite shows good hydrophobic ability, which is very useful in preventing corrosion on metal surfaces. • The prepared PANI/NPG composite material shows a significantly high corrosion resistance compared to alkyd resin/PANI coatings or alkyd resin coatings, on steel surfaces. - Abstract: Solid polymer composite systems are widely being used for potential technological applications in secondary energy sources and electrochromic devices. In this study, we synthesized and characterized a composite material composed of polyaniline (PANI) and natural needle platy (NPG) vein graphite. Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), cyclic voltammetry (CV), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), micro-Raman analysis, thermogravimetric and differential thermal analysis (TGA/DTA), transmission electron microscopy (TEM) were used to study the structural and electrochemical properties of the prepared PANI/NPG graphite composite. XPS, FTIR, and micro-Raman analysis confirmed the existence of relevant functional groups and bonding in the prepared PANI/NPG composite material. The composite shows a very low corrosion rate, approximately 29 μm per year, and high hydrophobicity on steel surfaces, which helps to prevent the corrosion due to O{sub 2} penetration towards the metal surface. It indicates that the composite can be used as a high potential surface coating material to anticorrosion. The specific capacitance of PANI/NPG composite is 833.3 F g{sup −1}, which is higher than that of PANI. This synergistic electrical performance result proves the prepared PANI/NPG graphite composite as a suitable protective coating material for steel

Actinide/crown ether chemistry

International Nuclear Information System (INIS)

Benning, M.M.

1988-01-01

A structural survey of actinide/crown ether compounds was conducted in order to investigate the solid state chemistry of these complexes. Several parameters - the metal size, crown type, counterion, solvent systems and reaction and crystallization conditions - were varied to correlate their importance in complexation. Under atmospheric conditions, two types of complexes were isolated, those containing only hydrogen-bonded crown interactions and instances where the crown interacts directly with the metal center. In both cases, water seems to play a very important role. When coordinated to the metal, water molecules exhibit the necessary donor properties required for the formation of hydrogen-bonded contacts. The water molecules also provide fierce competition with the crown ethers for metal-binding sites and in most cases prohibit the formation of complexes in which direct metal-ligand association exists. The results of this study indicate that direct interaction between the metal atoms and the crown ethers, in the presence of water, can only occur with polyether conformations which limit the steric replusions within the metal coordination sphere

Through-thickness thermal conductivity enhancement of graphite film/epoxy composite via short duration acidizing modification

Science.gov (United States)

Wang, Han; Wang, Shaokai; Lu, Weibang; Li, Min; Gu, Yizhou; Zhang, Yongyi; Zhang, Zuoguang

2018-06-01

Graphite films have excellent in-plane thermal conductivity but extremely low through-thickness thermal conductivity because of their intrinsic inter-layer spaces. To improve the inter-layer heat transfer of graphite films, we developed a simple interfacial modification with a short duration mixed-acid treatment. The effects of the mixture ratio of sulfuric and nitric acids and treatment time on the through-thickness thermal properties of graphite films were studied. The modification increased the through-thickness thermal conductivity by 27% and 42% for the graphite film and its composite, respectively. X-ray photoelectron spectroscopy, X-ray powder diffraction, and scanning electron microscopy results indicated that the acidification process had two competing effects: the positive contribution made by the enhanced interaction between the graphite layers induced by the functional groups and the negative effect from the destruction of the graphite layers. As a result, an optimal acidification method was found to be sulfuric/nitric acid treatment with a mixture ratio of 3:1 for 15 min. The resultant through-thickness thermal conductivity of the graphite film could be improved to 0.674 W/mK, and the corresponding graphite/epoxy composite shows a through-thickness thermal conductivity of 0.587 W/mK. This method can be directly used for graphite films and their composite fabrication to improve through-thickness thermal conductivity.

Preparation and tribological properties of self-lubricating TiO2/graphite composite coating on Ti6Al4V alloy

International Nuclear Information System (INIS)

Mu, Ming; Zhou, Xinjian; Xiao, Qian; Liang, Jun; Huo, Xiaodi

2012-01-01

Highlights: ► A TiO 2 /graphite composite coating is produced on Ti alloy by one-step PEO process. ► The TiO 2 /graphite composite coating exhibits excellent self-lubricating behavior. ► The self-lubricating composite coating improves the wear resistance by comparison to the conventional PEO coating. - Abstract: One-step plasma electrolytic oxidation (PEO) process in a graphite-dispersed phosphate electrolyte was used to prepare a graphite-containing oxide composite coating on Ti6Al4V alloy. The composition and microstructure of the oxide coatings produced in the phosphate electrolytes with and without addition of graphite were analyzed by X-ray diffractometer (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). The tribological properties of the uncoated Ti6Al4V alloy and oxide coatings were evaluated using a reciprocating ball-on-disk tribometer. Results showed that the graphite-containing oxide composite coating can be successfully produced on Ti6Al4V alloy in the graphite-dispersed phosphate electrolyte using PEO process. The graphite-containing oxide composite coating registered much lower friction coefficient and wear rate than the uncoated Ti6Al4V alloy and the oxide coating without graphite under dry sliding condition, exhibiting excellent self-lubricating property.

Sulfonation degree effect on ion-conducting SPEEK-titanium oxide membranes properties

Energy Technology Data Exchange (ETDEWEB)

Marrero, Jacqueline Costa; Gomes, Ailton de Souza; Dutra Filho, José Carlos, E-mail: jacquecosta@gmail.com [Universidade Federal do Rio de Janeiro (IMA/UFRJ), RJ (Brazil). Instituto de Macromoléculas Professora Eloisa Mano; Hui, Wang Shu [Universidade de São Paulo (USP), São Paulo, SP (Brazil). Departamento de Engenharia Metalúrgica e de Materiais; Oliveira, Vivianna Silva de [Escola Técnica Rezende Rammel (ETRR), Rio de Janeiro, RJ (Brazil)

2017-07-01

Polymeric membranes were developed using a SPEEK (sulfonated poly(ether ether ketone)) polymer matrix, containing titanium oxide (TiO{sub 2}) (incorporated by sol-gel method). SPEEK with different sulfonation degrees (SD): 63% and 50% were used. The influence of sulfonation degree on membrane properties was investigated. The thermal analysis (TGA and DTGA) and X-ray diffraction (XRD) were carried out to characterize the membranes and electrochemical impedance spectroscopy (EIS) was carried out to evaluate the proton conductivity of the membranes. The proton conductivities in water were of 3.25 to 37.08 mS.cm{sup -1}. Experimental data of impedance spectroscopy were analyzed with equivalent circuits using the Zview software, and the results showed that, the best fitted was at 80 °C. (author)

Estudo das propriedades térmicas de filmes poliméricos compostos de Speek, derivados do benzoimidazol e ácido fosfotúngstico Thermal properties of Speek-based polymeric films containing benzimidazole derivatives and fosfotungstic acid

Directory of Open Access Journals (Sweden)

Fabrício Celso

2008-06-01

Full Text Available Filmes poliméricos foram desenvolvidos a partir de poli (éter éter cetona sulfonado (SPEEK, derivados do benzoimidazol e ácido fosfotúngstico (HPW. Neste trabalho foi realizado um estudo utilizando a análise termogravimétrica com o objetivo de avaliar a estabilidade térmica e determinar as condições de temperatura a que podem ser submetidos os filmes produzidos, tendo em vista a aplicação de tais filmes como membranas em células a combustível. Os resultados obtidos mostram que a estabilidade térmica é afetada pela composição dos filmes. A maioria dos filmes se mostrou estável até 140 °C.Polymeric films were developed from sulfonated poly(ether ether ketone (SPEEK, benzimidazole derivatives and phosphotungstic acid (HPW. In this study, thermogravimetric analysis was performed with the aim of evaluating the temperature conditions to which polymeric films can be submitted. The results showed that thermal stability depended on film composition and the majority of the tested films showed to be stable up to 140 °C.

Synthesis and characterization of biodegradable aliphatic copolyesters with hydrophilic soft segments

Directory of Open Access Journals (Sweden)

JASNA DJONLAGIC

2004-12-01

Full Text Available In this study, the synthesis, structure and physical properties of two series of segmented poly(ester-ethers based on poly(butylene succinate and two different types of polyethers were investigated. The poly(ester-ethers were synthesized by transesterification reaction of dimethyl succinate, 1,4-butanediol and poly(ethylene oxide (PEO, Mn = 1000 g/mol in the first series, and poly(tetramethylene oxide (PTMO, Mn = 1000 g/mol in the second. The mass fraction of soft segments was varied between 10 and 50 mass. %. The effect of the introduction of two different polyether soft segments on the structure, thermal and rheological properties were investigated. The composition of the poly(ester-ethers, determined from their 1H-NMR spectra, showed that incorporation of soft polyether segments was successfully performed by the transesterification reaction in bulk. The molecular weight was estimated from solution viscosity measurements and complex dynamic viscosities. The thermal properties investigated by DSC indicated that the presence of soft segments lowers the melting and crystallization temperature of the hard phase, as well as the degree of crystallinity. Dynamical mechanical analysis was used to investigate the influence of composition on the rheological behavior of the segmented poly(ester-ethers. The results obtained from an enzymatic degradation test performed on some of the synthesized polymers showed that the biodegradability is enhanced with increasing hydrophilicity.

Chemical vapor deposition of tantalum on graphite cloth for making hot pressed fiber reinforced carbide-graphite composite

International Nuclear Information System (INIS)

Hollabaugh, C.M.; Davidson, K.V.; Radosevich, C.L.; Riley, R.E.; Wallace, T.C.

1977-01-01

Conditions for the CVD of a uniform coating of Ta on fibers of a woven graphite cloth were established. The effect of gas composition, pressure, and temperature were investigated, and the conditions that gave the desired results are presented. Several layers of the coated cloth were hot pressed to produce a TaC--C composite having uniformly dispersed, fine-grained TaC in graphite. Three compositions were hot pressed: 15, 25, and 40 volume percent carbide. 8 figures, 2 tables

Composites of aluminum alloy and magnesium alloy with graphite showing low thermal expansion and high specific thermal conductivity

Science.gov (United States)

Oddone, Valerio; Boerner, Benji; Reich, Stephanie

2017-12-01

High thermal conductivity, low thermal expansion and low density are three important features in novel materials for high performance electronics, mobile applications and aerospace. Spark plasma sintering was used to produce light metal-graphite composites with an excellent combination of these three properties. By adding up to 50 vol.% of macroscopic graphite flakes, the thermal expansion coefficient of magnesium and aluminum alloys was tuned down to zero or negative values, while the specific thermal conductivity was over four times higher than in copper. No degradation of the samples was observed after thermal stress tests and thermal cycling. Tensile strength and hardness measurements proved sufficient mechanical stability for most thermal management applications. For the production of the alloys, both prealloyed powders and elemental mixtures were used; the addition of trace elements to cope with the oxidation of the powders was studied.

Differences in interfacial bond strengths of graphite fiber-epoxy resin composites

Science.gov (United States)

Needles, H. L.

1985-01-01

The effect of epoxy-size and degree of cure on the interfacial bonding of an epoxy-amine-graphite fiber composite system is examined. The role of the fiber-resin interface in determining the overall mechanical properties of composites is poorly understood. A good interfacial adhesive bond is required to achieve maximum stress transfer to the fibers in composites, but at the same time some form of energy absorbing interfacial interaction is needed to achieve high fracture toughening. The incompatibility of these two processes makes it important to understand the nature and basic factors involved at the fiber-resin interface as stress is applied. The mechanical properties including interlaminar shear values for graphite fiber-resin composites are low compared to glass and boron-resin composites. These differences have been attributed to poor fiber-matrix adhesion. Graphite fibers are commonly subjected to post-treatments including application of organic sizing in order to improve their compatibility with the resin matrix and to protect the fiber tow from damage during processing and lay-up. In such processes, sized graphite fiber tow is impregnated with epoxy resin and then layed-up i nto the appropriate configuration. Following an extended ambient temperature cure, the graphite-resin composite structure is cured at elevated temperature using a programmed temperature sequence to cure and then cool the product.

Electrochemical performance of SnO{sub 2}/modified graphite composite material as anode of lithium ion battery

Energy Technology Data Exchange (ETDEWEB)

Wang, Hong-Qiang [Guangxi Key Laboratory of Low Carbon Energy Materials, School of Chemical and Pharmaceutical Sciences, Guangxi Normal University, Guilin 541004 (China); Hubei Key Laboratory for Processing and Application of Catalytic Materials, Huanggang Normal University, Huanggang 438000 (China); Yang, Guan-Hua; Huang, You-Guo; Zhang, Xiao-Hui; Yan, Zhi-Xiong [Guangxi Key Laboratory of Low Carbon Energy Materials, School of Chemical and Pharmaceutical Sciences, Guangxi Normal University, Guilin 541004 (China); Li, Qing-Yu, E-mail: liqingyu62@126.com [Guangxi Key Laboratory of Low Carbon Energy Materials, School of Chemical and Pharmaceutical Sciences, Guangxi Normal University, Guilin 541004 (China)

2015-11-01

In this report, we synthesized SnO{sub 2}/modified graphite anode composite material by a simple reflux method using SnCl{sub 4}·5H{sub 2}O as tin source and modified graphite as carbon source. The as-obtained composite was investigated with the help of X-ray diffraction (XRD), scanning electron microscopy (SEM) and galvanostatic cycling tests. The results show that the composite has a wave-shaped fold structure and the SnO{sub 2} nanoparticles on it have an average size of about 50 nm. Compared to pure modified graphite, the SnO{sub 2}/modified graphite exhibits a better electrochemical performance with a reversible specific capacity of 581.7 mAh g{sup −1} after 80 cycles, owing to high mechanical stress and elasticity of modified graphite could hinder the volume effect of SnO{sub 2} nanoparticles during the Li{sup +} insertion/extraction process. All these favourable characters reveal that the composite is a great potential anode material in high-performance lithium ion batteries. - Highlights: • A simple synthetic method of SnO{sub 2}/modified graphite composite as anode. • The as-prepared composite with layered structure alleviates the huge reunion of SnO{sub 2}. • The composite exhibits a good capacity retention rate of 85.8% after 25 cycles.

Synthesis and Crosslinking of Polyether-Based Main Chain Benzoxazine Polymers and Their Gas Separation Performance

Directory of Open Access Journals (Sweden)

Muntazim Munir Khan

2018-02-01

Full Text Available The poly(ethylene glycol-based benzoxazine polymers were synthesized via a polycondensation reaction between Bisphenol-A, paraformaldehyde, and poly(ether diamine/(Jeffamine®. The structures of the polymers were confirmed by proton nuclear magnetic resonance spectroscopy (1H-NMR, indicating the presence of a cyclic benzoxazine ring. The polymer solutions were casted on the glass plate and cross-linked via thermal treatment to produce tough and flexible films without using any external additives. Thermal properties and the crosslinking behaviour of these polymers were studied by thermogravimetric analysis (TGA and differential scanning calorimetry (DSC. Single gas (H2, O2, N2, CO2, and CH4 transport properties of the crosslinked polymeric membranes were measured by the time-lag method. The crosslinked PEG-based polybenzoxazine membranes show improved selectivities for CO2/N2 and CO2/CH4 gas pairs. The good separation selectivities of these PEG-based polybenzoxazine materials suggest their utility as efficient thin film composite membranes for gas and liquid membrane separation technology.

Fracto-emission from graphite/epoxy composites

Science.gov (United States)

Dickinson, J. T.

1983-01-01

Fracto-emission (FE) is the emission of particles and photons during and following crack propagation. Electrons (EE), positive ions (PIE), and excited and ground state neutrals (NE) were observed. Results of a number of experiments involving principally graphite/epoxy composites and Kevlar single fibers are presented. The physical processes responsible for EE and PIE are discussed as well as FE from fiber- and particulate-reinforced composites.

Mechanical properties of aluminium based metal matrix composites reinforced with graphite nanoplatelets

Energy Technology Data Exchange (ETDEWEB)

Alam, Syed Nasimul, E-mail: syedn@nitrkl.ac.in; Kumar, Lailesh

2016-06-14

In this work Al-matrix composites reinforced by exfoliated graphite nanoplatelets (xGnP) is fabricated by powder metallurgy route and their microstructure, mechanical properties and sliding wear behaviour were investigated. Here, xGnP has been synthesized from the thermally exfoliated graphite produced from a graphite intercalation compound (GIC) through rapid evaporation of the intercalant at an elevated temperature. The xGnP synthesized was characterized using scanning electron microscope (SEM), high-resolution transmission electron microscope (HRTEM), x-ray diffraction (XRD), atomic force microscopy (AFM), x-ray photoelectron spectroscopy (XPS), differential scanning calorimetry and thermogravimetric analysis (DSC/TGA), Raman spectroscopy and Fourier transform infrared spectroscopy (FTIR). The Al and xGnP powder mixtures were consolidated under a load of 565 MPa followed by sintering at 550 °C for 2 h in an inert atmosphere. Al-1, 2, 3 and 5 wt% xGnP nanocomposites were developed. Results of the wear test show that there was a significant improvement in the wear resistance of the composites up to the addition of 3 wt% of xGnP in the Al matrix. The hardness of the various Al-xGnP composites also shows improvement upto the addition of 1 wt% xGnP beyond which there was a decrease in the hardness of the composites. The tensile strength of the Al-xGnP composites continuously reduced with the addition of xGnP due to the formation of Al{sub 4}C{sub 3} particles at the interface of the Al and xGnP in the composite.

Fabrication and testing of fire resistant graphite composite panels

Science.gov (United States)

Roper, W. D.

1986-01-01

Eight different graphite composite panels were fabricated using four different resin matrices. The resin matrices included Hercules 71775, a blend of vinylpolystyrpyridine and bismaleimide, H795, a bismaleimide, Cycom 6162, a phenolic, and PSP 6022m, a polystyrylpyridine. Graphite panels were fabricated using fabric or unidirectional tape. Described are the processes for preparing these panels and some of their mechanical, thermal and flammability properties. Panel properties are compared with state-of-the-art epoxy fiberglass composite panels.

Nanostructured Al/Al4C3 composites reinforced with graphite or fullerene and manufactured by mechanical milling and spark plasma sintering

International Nuclear Information System (INIS)

Robles Hernández, F.C.; Calderon, H.A.

2012-01-01

Highlights: ► Fullerene mix (C 60 + C 70 + soot) is effective to manufacture nanostructured Al/Al 4 C 3 . ► Carbon in the fullerene mix is more reactive with Al that that present in graphite. ► A complete transformation of carbon into Al 4 C 3 is observed in the Al/fullerene. ► Milling and sintering conditions preserve the nanostructured nature of the composites. ► Hardness improvement: 375% Al/graphite and 582% for Al/fullerene composites. - Abstract: Nanostructured Al matrix composites with reinforcements of graphite or fullerene (C 60 + C 70 + soot) have been produced by mechanical milling and spark plasma sintering (SPS). X-ray diffraction and transmission electron microscopy show that C 60 + C 70 withstand longer mechanical milling/alloying times than graphite. Fullerene is a good control agent during mechanical alloying resulting in a denser Al/fullerene composite when compared to the Al/graphite one. A refinement mechanism that takes place during mechanical alloying of fullerene and graphite is experimentally found and correspondingly discussed. Such a mechanism plays a major role in the amorphization of graphite. The larger surface area of the fullerene mix after milling promotes a better interaction with Al and hence allows its complete transformation into Al 4 C 3 during the SPS process. The sintered products show an increase in hardness for the Al/fullerene composite of 6 times and only 4 times for the Al/graphite composite. The SPS technique shows to be an excellent method to transform the fullerene into Al 4 C 3 while preserving its nanostructured nature.

Porosity Effect on Thermal Properties of Al-12 wt % Si/Graphite Composites

Directory of Open Access Journals (Sweden)

José-Miguel Molina

2017-02-01

Full Text Available The effect of porosity on the thermal conductivity and the coefficient of thermal expansion of composites obtained by infiltration of Al-12 wt % Si alloy into graphite particulate preforms has been determined. Highly irregular graphite particles were used to fabricate the preforms. The thermal conductivity of these composites gradually increases with the applied infiltration pressure given the inherent reduction in porosity. A simple application of the Hasselman-Johnson model in a two-step procedure (that accounts for the presence of both graphite particles and voids randomly dispersed in a metallic matrix offers a good estimation of the experimental results. As concerns the coefficient of thermal expansion, the results show a slight increase with saturation being approximately in the range 14.6–15.2 × 10−6 K−1 for a saturation varying from 86% up to 100%. Results lie within the standard Hashin-Strikman bounds.

Porosity Effect on Thermal Properties of Al-12 wt % Si/Graphite Composites.

Science.gov (United States)

Molina, José-Miguel; Rodríguez-Guerrero, Alejandro; Louis, Enrique; Rodríguez-Reinoso, Francisco; Narciso, Javier

2017-02-14

The effect of porosity on the thermal conductivity and the coefficient of thermal expansion of composites obtained by infiltration of Al-12 wt % Si alloy into graphite particulate preforms has been determined. Highly irregular graphite particles were used to fabricate the preforms. The thermal conductivity of these composites gradually increases with the applied infiltration pressure given the inherent reduction in porosity. A simple application of the Hasselman-Johnson model in a two-step procedure (that accounts for the presence of both graphite particles and voids randomly dispersed in a metallic matrix) offers a good estimation of the experimental results. As concerns the coefficient of thermal expansion, the results show a slight increase with saturation being approximately in the range 14.6-15.2 × 10 -6 K -1 for a saturation varying from 86% up to 100%. Results lie within the standard Hashin-Strikman bounds.

Investigations on Mechanical Behaviour of Micro Graphite Particulates Reinforced Al-7Si Alloy Composites

Science.gov (United States)

Nagaraj, N.; Mahendra, K. V.; Nagaral, Madeva

2018-02-01

Micro particulates reinforced metal matrix composites are finding wide range of applications in automotive and sports equipment manufacturing industries. In the present study, an attempt has been made to develop Al-7Si-micro graphite particulates reinforced composites by using liquid melt method. 3 and 6 wt. % of micro graphite particulates were added to the Al-7Si base matrix. Microstructural characterization was done by using scanning electron microscope and energy dispersive spectroscope. Mechanical behaviour of Al-7Si-3 and 6 wt. % composites were evaluated as per ASTM standards. Scanning electron micrographs revealed the uniform distribution of micro graphite particulates in the Al-7Si alloy matrix. EDS analysis confirmed the presence of B and C elements in graphite reinforced composites. Further, it was noted that ultimate tensile and yield strength of Al-7Si alloy increased with the addition of 3 and 6wt. % of graphite particulates. Hardness of graphite reinforced composites was lesser than the base matrix.

Polyether matrices for lithium generators; Matrices polyethers pour generateurs au lithium

Energy Technology Data Exchange (ETDEWEB)

Alloin, F.; Sanchez, J.Y. [Laboratoire d`Electrochimie et de Physicochimie des Materiaux et des Interfaces, 38 - Saint-Martin-d`Heres (France)

1996-12-31

The use of solvating polymers of polyether type is an interesting solution for the manufacturing of high capacity lithium batteries with lithium metal anodes and which can operate at T > 50 deg. C. These operating conditions are perfectly compatible with electric-powered vehicle and stationary battery applications. In order to improve the ionic conductivity of polymer electrolytes, new aprotic and amorphous polyether lattices have been synthesized having a good conductivity but also good thermal, mechanical and electrochemical stabilities. Two type of 3-D polyether lattices obtained by reticulation of linear pre-polymers have been selected as host polymers: unsaturated poly-condensate and unsaturated co-polyethers. (J.S.) 18 refs.

Polyether matrices for lithium generators; Matrices polyethers pour generateurs au lithium

Energy Technology Data Exchange (ETDEWEB)

Alloin, F; Sanchez, J Y [Laboratoire d` Electrochimie et de Physicochimie des Materiaux et des Interfaces, 38 - Saint-Martin-d` Heres (France)

1997-12-31

The use of solvating polymers of polyether type is an interesting solution for the manufacturing of high capacity lithium batteries with lithium metal anodes and which can operate at T > 50 deg. C. These operating conditions are perfectly compatible with electric-powered vehicle and stationary battery applications. In order to improve the ionic conductivity of polymer electrolytes, new aprotic and amorphous polyether lattices have been synthesized having a good conductivity but also good thermal, mechanical and electrochemical stabilities. Two type of 3-D polyether lattices obtained by reticulation of linear pre-polymers have been selected as host polymers: unsaturated poly-condensate and unsaturated co-polyethers. (J.S.) 18 refs.

Enzymatic catalysis of anti-Baldwin ring closure in polyether biosynthesis.

Science.gov (United States)

Hotta, Kinya; Chen, Xi; Paton, Robert S; Minami, Atsushi; Li, Hao; Swaminathan, Kunchithapadam; Mathews, Irimpan I; Watanabe, Kenji; Oikawa, Hideaki; Houk, Kendall N; Kim, Chu-Young

2012-03-04

Polycyclic polyether natural products have fascinated chemists and biologists alike owing to their useful biological activity, highly complex structure and intriguing biosynthetic mechanisms. Following the original proposal for the polyepoxide origin of lasalocid and isolasalocid and the experimental determination of the origins of the oxygen and carbon atoms of both lasalocid and monensin, a unified stereochemical model for the biosynthesis of polyether ionophore antibiotics was proposed. The model was based on a cascade of nucleophilic ring closures of postulated polyepoxide substrates generated by stereospecific oxidation of all-trans polyene polyketide intermediates. Shortly thereafter, a related model was proposed for the biogenesis of marine ladder toxins, involving a series of nominally disfavoured anti-Baldwin, endo-tet epoxide-ring-opening reactions. Recently, we identified Lsd19 from the Streptomyces lasaliensis gene cluster as the epoxide hydrolase responsible for the epoxide-opening cyclization of bisepoxyprelasalocid A to form lasalocid A. Here we report the X-ray crystal structure of Lsd19 in complex with its substrate and product analogue to provide the first atomic structure-to our knowledge-of a natural enzyme capable of catalysing the disfavoured epoxide-opening cyclic ether formation. On the basis of our structural and computational studies, we propose a general mechanism for the enzymatic catalysis of polyether natural product biosynthesis. © 2012 Macmillan Publishers Limited. All rights reserved

Crown ether derivatives of EDTA: Pt. 6

International Nuclear Information System (INIS)

Liu Zhongqun; Qin Shengying; Chen Shaojin; Tan Lin

1988-01-01

EDTA-diaminodibenzo-18-crown-6 (cis- and trans-) condensation polymer is a new compound of crown ether derivatives of EDTA. In this paper the adsorption behaviors of U(IV) and U(VI) on this polymer from chloride solutions and effects of hydrochloric acid concentrations, salting-out agents and organic solvents on distribution coefficient (K d ) of uranium are investigated. Adsorption mechanism of uranyl ion (UO 2 2+ ) on this polymer was studied with IR spectra and by means of the adsorption behaviors of compounds of similar structure. Experimental results show that both polyether section and carboxyl groups in EDTA-diaminodibenzo-18-crown-6 take part in complexation with uranyl ion and synergistic effect appeared

Some metal-graphite and metal-ceramic composites for use as high energy brake lining materials

Science.gov (United States)

Bill, R. C.

1974-01-01

Materials were studied as candidates for development as potential new aircraft brake lining materials. These families were (1) copper-graphite composites; (2) nickel-graphite composites; (3) copper - rare-earth-oxide (gadolinium oxide (Gd2O3) or lanthanum oxide (La2O3)) composites and copper - rare-earth-oxide (La2O3) - rare-earth-fluoride (lanthanum fluoride (LaF3)) composites; (4) nickel - rare-earth-oxide composites and nickel - rare-earth-oxide - rare-earth-fluoride composites. For comparison purposes, a currently used metal-ceramic composite was also studied. Results showed that the nickel-Gd2O3 and nickel-La2O3-LaF3 composites were comparable or superior in friction and wear performance to the currently used composite and therefore deserve to be considered for further development.

Composition of secondary alcohols, ketones, alkanediols, and ketols in Arabidopsis thaliana cuticular waxes

Science.gov (United States)

Wen, Miao; Jetter, Reinhard

2009-01-01

Arabidopsis wax components containing secondary functional groups were examined (i) to test the biosynthetic relationship between secondary alcohols and ketols and (ii) to determine the regiospecificity and substrate preference of the enzyme involved in ketol biosynthesis. The stem wax of Arabidopsis wild type contained homologous series of C27 to C31 secondary alcohols (2.4 μg cm−2) and C28 to C30 ketones (6.0 μg cm−2) dominated by C29 homologues. In addition, compound classes containing two secondary functional groups were identified as C29 diols (∼0.05 μg cm−2) and ketols (∼0.16 μg cm−2). All four compound classes showed characteristic isomer distributions, with functional groups located between C-14 and C-16. In the mah1 mutant stem wax, diols and ketols could not be detected, while the amounts of secondary alcohols and ketones were drastically reduced. In two MAH1-overexpressing lines, equal amounts of C29 and C31 secondary alcohols were detected. Based on the comparison of homologue and isomer compositions between the different genotypes, it can be concluded that biosynthetic pathways lead from alkanes to secondary alcohols, and via ketones or diols to ketols. It seems plausible that MAH1 is the hydroxylase enzyme involved in all these conversions in Arabidopsis thaliana. PMID:19346242

Graphite nanoplatelets and carbon nanotubes based polyethylene composites: Electrical conductivity and morphology

International Nuclear Information System (INIS)

Haznedar, Galip; Cravanzola, Sara; Zanetti, Marco; Scarano, Domenica; Zecchina, Adriano; Cesano, Federico

2013-01-01

Graphite nanoplatelets (GNPs) and/or multiwalled-carbon nanotubes (MWCNTs)/low density polyethylene (LDPE) composites have been obtained either via melt-mixing or solvent assisted methods. Electrical properties of samples obtained through the above mentioned methods are compared and the conductance values as function of filler fraction are discussed. The corresponding percolation thresholds are evaluated. Conductivity maps images are acquired under low-potentials scanning electron microscopy (0.3 KV) and the relationship between the obtained conductivity images and electric properties is highlighted. The synergistic role of CNTs (1D) and GNPs (2D) in improving the conductive properties of the polymer composites has been shown. - Highlights: • Graphite nanoplatelets (GNPs) and GNPs/MWCNT LDPE composites. • Low potential SEM conductivity maps. • Conducting paths between 1D and 2D C-structures (synergistic effect) are obtained. • Composites based on hybrid 1D/2D combinations show lower percolation thresholds

A rare allergy to a polyether dental impression material.

Science.gov (United States)

Mittermüller, Pauline; Szeimies, Rolf-Markus; Landthaler, Michael; Schmalz, Gottfried

2012-08-01

Polyether impression materials have been used in dentistry for more than 40 years. Allergic reactions to these materials such as reported in the 1970s ceased after replacement of a catalyst. Very recently, however, patients have started to report symptoms that suggest a new allergic reaction from polyether impression materials. Here, we report on the results of allergy testing with polyether impression materials as well as with its components. Eight patients with clinical symptoms of a contact allergy (swelling, redness or blisters) after exposure to a polyether impression material were subjected to patch tests, two of them additionally to a prick test. A further patient with atypical symptoms of an allergy (nausea and vomiting after contact with a polyether impression material in the oral cavity) but with a history of other allergic reaction was also patch tested. The prick tests showed no immediate reactions in the two patients tested. In the patch tests, all eight patients with typical clinical symptoms showed positive reactions to the mixed polyether impression materials, to the base paste or to a base paste component. The patient with the atypical clinical symptoms did not show any positive patch test reactions. Polyether impression materials may evoke type IV allergic reactions. The causative agent was a component of the base paste. In consideration of the widespread use of this impression material (millions of applications per year) and in comparison to the number of adverse reactions from other dental materials, the number of such allergic reactions is very low. In very scarce cases, positive allergic reactions to polyether impression materials are possible.

Sulfonated poly(fluorenyl ether ketone nitrile) electrolyte membrane with high proton conductivity and low water uptake

Energy Technology Data Exchange (ETDEWEB)

Tian, S.H.; Wang, S.J.; Xiao, M.; Meng, Y.Z. [State Key Laboratory of Optoelectronic Materials and Technologies/Institute of Optoelectronic and Functional Composite Materials, Sun Yat-sen University, Guangzhou 510275 (China); Shu, D. [School of Chemistry and Environmental, South China Normal University, Guangzhou 510006 (China)

2010-01-01

High molecular weight sulfonated poly(fluorenyl ether ketone nitrile)s with different equivalent weight (EW) from 681 to 369 g mequiv.{sup -1} are synthesized by the nucleophilic substitution polycondensation of various amounts of sulfonated difluorobenzophenone (SDFBP) and 2,6-difluorobenzonitrile (DFBN) with bisphenol fluorene (BPF). The synthesized copolymers are characterized by {sup 1}H NMR, FT-IR, TGA, and DSC techniques. The membranes cast from the corresponding copolymers exhibit superior thermal stability, good oxidative stability and high proton conductivity, but low water uptake due to the strong nitrile dipole interchain interactions that combine to limit swelling. Among all the membranes, the membrane with EW of 441 g mequiv.{sup -1} shows optimum properties of both high proton conductivity of 41.9 mS cm{sup -1} and low water uptake of 42.6%. Accordingly, That membrane is fabricated into a membrane electrode assembly (MEA) and evaluated in a single proton exchange membrane fuel cell (PEMFC). The experimental results indicate its similar cell performance as that of Nafion {sup registered} 117 at 70 C, but much better cell performance at higher temperatures. At the potential of 0.6 V, the current density of fuel cell using the prepared membrane and Nafion {sup registered} 117 is 0.46 and 0.25 A cm{sup -2}, respectively. The highest current density of the former reaches as high as 1.25 A cm{sup -2}. (author)

Thermophysical properties and microstructure of graphite flake/copper composites processed by electroless copper coating

International Nuclear Information System (INIS)

Liu, Qian; He, Xin-Bo; Ren, Shu-Bin; Zhang, Chen; Ting-Ting, Liu; Qu, Xuan-Hui

2014-01-01

Highlights: • GF–copper composites were fabricated using a sparking plasma sintering, which involves coating GF with copper, using electroless plating technique. • The oriented graphite flake distributed homogeneously in matrix. • With the increase of flake graphite from 44 to 71 vol.%, the basal plane thermal conductivity of composites increases from 445 to 565 W m −1 K −1 and the thermal expansion of composites decreases from 8.1 to 5.0. • The obtained composites are suitable for electronic packaging materials. -- Abstract: This study focuses on the fabrication of thermal management material for power electronics applications using graphite flake reinforced copper composites. The manufacturing route involved electroless plating of copper on the graphite flake and further spark plasma sintering of composite powders. The relative density of the composites with 44–71 vol.% flakes achieved up to 98%. Measured thermal conductivities and coefficients of thermal expansion of composites ranged from 455–565 W m −1 K −1 and 8 to 5 ppm K −1 , respectively. Obtained graphite flake–copper composites exhibit excellent thermophysical properties to meet the heat dispersion and matching requirements of power electronic devices to the packaging materials

Mechanical and thermophysical properties of graphite/polyimide composite materials

Science.gov (United States)

Rummler, D. R.; Clark, R. K.

1979-01-01

An on-going program to characterize advanced composites for up to 50,000 hours of exposure to simulated supersonic cruise environments is summarized. Results are presented for up to 25,000 hours of thermal exposure and 10,000 hours of flight simulation at temperatures up to 560K (550 F) with emphasis on HTS/710 graphite/polyimide composite material. Results to date indicate that the maximum use temperature for HTS/710 may be reduced to 505K (450 F) for long-time (1000 hours) application such as the supersonic transport. Preliminary thermophysical properties data for HTS/PMR15 graphite/polyimide were generated. These data include thermal conductivity, thermal expansion, and specific heat from 115K (-252 F) to 590K (600 F) and emittance at room temperature and 590K (600 F). The purpose in generating these data was to validate use of state-of-the-art property measurement methods for advanced graphite fiber reinforced resin matrix composites. Based on results to this point, thermal expansion measurements for composites are most difficult to perform. A high degree of caution in conducting thermal expansion tests and analyzing results is required to produce reliable data.

Poly (fluorenyl ether ketone) ionomers containing separated hydrophilic multiblocks used in fuel cells as proton exchange membranes

Energy Technology Data Exchange (ETDEWEB)

Hu, H.; Xiao, M.; Wang, S.J.; Meng, Y.Z. [State Key Laboratory of Optoelectronic Materials and Technologies, Sun Yat-Sen University, Guangzhou 510275 (China); The Key Laboratory of Low-carbon Chemistry and Energy Conservation of Guangdong Province, Sun Yat-Sen University, Guangzhou 510275 (China)

2010-01-15

A series of sulfonated poly(fluorenyl ether ketone) with different hydrophilic block lengths were synthesized via a two-step one-pot polymerization from 9,9'-bis(4-Hydroxypheyl) fluorine, 3,3'-disulfonated-4,4'-difluorobenzophenone, and 4,4'-difluorobenzophenone. The resulting sulfonated block polymers with high inherent viscosity (0.8-1.37 dL/g) were very soluble in polar organic solvents and can form flexible and transparent membranes by casting from their solutions. Transmission electron microscope (TEM) was used to examine the microstructure of the membranes and the results revealed that significant hydrophilic/hydrophobic microphase separation was produced. The effects of the multiblock structure and/or length were investigated by comparison of the properties of the multiblock copolymer and the corresponding random structure. The multiblock structure can provide enhanced proton transport, especially under partially hydrated conditions. The as-made membranes can also exhibit better oxidative stability and single cell performance than random copolymer. The multiblock structure design method provides a useful way to prepare proton exchange membrane used in PEM fuel cells. (author)

Manufacture of nano graphite oxides derived from aqueous glucose solutions and in-situ synthesis of magnetite–graphite oxide composites

Energy Technology Data Exchange (ETDEWEB)

Liu, Xiang, E-mail: liuxiang@ahut.edu.cn; Zhao, Tiantian; Liu, Pengpeng; Cui, Ping, E-mail: cokecp@sohu.com; Hu, Peng

2015-03-01

A “bottom up” approach of manufacturing graphite oxides (GOs) derived from aqueous glucose solutions by virtue of an environmentally-friendly process and the way of in-situ synthesizing magnetite–GOs composites are described in this work in detail. The dehydrations among glucose molecules under hydrothermal condition result in the initial carbon quantum dots and ultimate GOs. The structural information of the GOs is obtained by the infrared, ultraviolet–visible and X-ray photoelectron spectra. The magnetite–GOs composites were obtained by a one-pot method under the same hydrothermal conditions as the one of preparing GOs. The composites perform high activities in catalytic degradation of Rhodamine B in the presence of hydrogen peroxides without extra heating or pH adjusting. Both the GOs and the magnetite–GOs composites are also assured by measurements of transmission electron microscope and X-ray powder diffraction. - Highlights: • Graphite oxides are made from aqueous glucose solutions by hydrothermal reaction. • A way of in-situ synthesizing composites of magnetite–graphite oxides is depicted. • The composites perform high activities in catalytic degradation of Rhodamine B.

Hydrophilization of Poly(ether ether ketone) Films by Surface-initiated Atom Transfer Radical Polymerization

DEFF Research Database (Denmark)

Fristrup, Charlotte Juel; Eskimergen, Rüya; Burkrinsky, J.T.

2008-01-01

and confirmed by ATR FTIR, water contact ang;le, and Thermal Gravimetric Analysis (TGA). The surface topography was evaluated by "Atomic Force Microscopy (AFM). X-ray Photoelectron Spectroscopy (XPS) has been used to investigate the degree of functionalization. The performed modification allowed for successful...

Posterior lumbar interbody fusion using non resorbable poly-ether-ether-ketone versus resorbable poly-L-lactide-co-D,L-lactide fusion devices. Clinical outcome at a minimum of 2-year follow-up.

Science.gov (United States)

Jiya, Timothy U; Smit, T; van Royen, B J; Mullender, M

2011-04-01

Previous papers on resorbable poly-L-lactide-co-D,L-lactide (PLDLLA) cages in spinal fusion have failed to report adequately on patient-centred clinical outcome measures. Also comparison of PLDLLA cage with a traditionally applicable counterpart has not been previously reported. This is the first randomized prospective study that assesses clinical outcome of PLDLLA cage compared with a poly-ether-ether-ketone (PEEK) implant. Twenty-six patients were randomly assigned to undergo instrumented posterior lumbar interbody fusion (PLIF) whereby either a PEEK cage or a PLDLLA cage was implanted. Clinical outcome based on visual analogue scale scores for leg pain and back pain, as well as Oswestry Disability Index (ODI) and SF-36 questionnaires were documented and analysed. When compared with preoperative values, all clinical parameters have significantly improved in the PEEK group at 2 years after surgery with the exception of SF-36 general health, SF-36 mental health and SF-36 role emotional scores. No clinical parameter showed significant improvement at 2 years after surgery compared with preoperative values in the PLDLLA patient group. Only six patients (50%) in the PLDLLA group showed improvement in the VAS scores for leg and back pain as well as the ODI, as opposed to 10 patients (71%) in the PEEK group. One-third of the patients in the PLDLLA group actually reported worsening of their pain scores and ODI. Three cases of mild to moderate osteolysis were seen in the PLDLLA group. Following up on our preliminary report, these 2-year results confirm the superiority of the PEEK implant to the resorbable PLDLLA implant in aiding spinal fusion and alleviating symptoms following PLIF in patients with degenerative spondylolisthesis associated with either canal stenosis or foramen stenosis or both and emanating from a single lumbar segment.

Thermophysical properties and microstructure of graphite flake/copper composites processed by electroless copper coating

Energy Technology Data Exchange (ETDEWEB)

Liu, Qian; He, Xin-Bo; Ren, Shu-Bin; Zhang, Chen; Ting-Ting, Liu; Qu, Xuan-Hui, E-mail: quxh@ustb.edu.cn

2014-02-25

Highlights: • GF–copper composites were fabricated using a sparking plasma sintering, which involves coating GF with copper, using electroless plating technique. • The oriented graphite flake distributed homogeneously in matrix. • With the increase of flake graphite from 44 to 71 vol.%, the basal plane thermal conductivity of composites increases from 445 to 565 W m{sup −1} K{sup −1} and the thermal expansion of composites decreases from 8.1 to 5.0. • The obtained composites are suitable for electronic packaging materials. -- Abstract: This study focuses on the fabrication of thermal management material for power electronics applications using graphite flake reinforced copper composites. The manufacturing route involved electroless plating of copper on the graphite flake and further spark plasma sintering of composite powders. The relative density of the composites with 44–71 vol.% flakes achieved up to 98%. Measured thermal conductivities and coefficients of thermal expansion of composites ranged from 455–565 W m{sup −1} K{sup −1} and 8 to 5 ppm K{sup −1}, respectively. Obtained graphite flake–copper composites exhibit excellent thermophysical properties to meet the heat dispersion and matching requirements of power electronic devices to the packaging materials.

Nano Structured Activated Carbon for Hydrogen Storge. Project Final Technical Report (May 2, 2005-Dec. 31, 2012)

Energy Technology Data Exchange (ETDEWEB)

Cabasso, Israel; Yuan, Youxin

2013-02-27

Development of a nanostructured synthetic carbons materials that have been synthesized by thermal-decomposition of aromatic rich polyether such as poly(ether ether ketone) (PEEK) is reported. These polymers based nanostructured carbons efficacious for gas adsorption and storage and have Brunauer-Emmett-Teller (BET) surface area of more than 3000 m2/g, and with average pore diameter of < 2nm. Surface-area, pore characteristics, and other critical variables for selecting porous materials of high gas adsorption capacities are presented. Analysis of the fragments evolved under various carbonization temperatures, and the correlation between the activation and carbonization temperatures provides a mechanistic perspective of the pore evolution during activation. Correlations between gas (N2 and H2) adsorption capacity and porous texture of the materials have been established. The materials possess excellent hydrogen storage properties, with hydrogen storage capacity up to 7.4 wt% (gravimetric) and ~ 45 g H2 L-1 (volumetric) at -196oC and 6.0 MPa.

Thermal fatigue of refractory metal/graphite composites for fusion applications

International Nuclear Information System (INIS)

Smid, I; Nickel, H.; Kny, E.; Reheis, N.

1995-01-01

Reactor grade graphite and molybdenum (TZM) were brazed with different high temperature brazes. The resulting composite tiles had a size of 50 mm x 50 mm with a graphite thickness of 10 mm and a TZM thickness of 5 mm. The brazed composites have been tested in electron beam simulation for their thermal fatigue properties. The parameters of these tests were chosen to match NET design specifications for normal operation and 'slow' peak energy deposition. The resulting damages and microstructural changes on the graphites and the brazes are discussed. Additional information is supplied on X-ray diffraction data proving the presence of different phases in the brazes. Finally the influence of a hydrogen plasma on the adaptability of the investigated brazes in fusion devices is discussed. (author)

A Nanoporous Carbon/Exfoliated Graphite Composite For Supercapacitor Electrodes

Science.gov (United States)

Rosi, Memoria; Ekaputra, Muhamad P.; Iskandar, Ferry; Abdullah, Mikrajuddin; Khairurrijal

2010-12-01

Nanoporous carbon was prepared from coconut shells using a simple heating method. The nanoporous carbon is subjected to different treatments: without activation, activation with polyethylene glycol (PEG), and activation with sodium hydroxide (NaOH)-PEG. The exfoliated graphite was synthesized from graphite powder oxidized with zinc acetate (ZnAc) and intercalated with polyvinyl alcohol (PVA) and NaOH. A composite was made by mixing the nanoporous carbon with NaOH-PEG activation, the exfoliated graphite and a binder of PVA solution, grinding the mixture, and annealing it using ultrasonic bath for 1 hour. All of as-synthesized materials were characterized by employing a scanning electron microscope (SEM), a MATLAB's image processing toolbox, and an x-ray diffractometer (XRD). It was confirmed that the composite is crystalline with (002) and (004) orientations. In addition, it was also found that the composite has a high surface area, a high distribution of pore sizes less than 40 nm, and a high porosity (67%). Noting that the pore sizes less than 20 nm are significant for ionic species storage and those in the range of 20 to 40 nm are very accessible for ionic clusters mobility across the pores, the composite is a promising material for the application as supercapacitor electrodes.

[Effect of phenolic ketones on ethanol fermentation and cellular lipid composition of Pichia stipitis].

Science.gov (United States)

Yang, Jinlong; Cheng, Yichao; Zhu, Yuanyuan; Zhu, Junjun; Chen, Tingting; Xu, Yong; Yong, Qiang; Yu, Shiyuan

2016-02-01

Lignin degradation products are toxic to microorganisms, which is one of the bottlenecks for fuel ethanol production. We studied the effects of phenolic ketones (4-hydroxyacetophenone, 4-hydroxy-3-methoxy-acetophenone and 4-hydroxy-3,5-dimethoxy-acetophenone) derived from lignin degradation on ethanol fermentation of xylose and cellular lipid composition of Pichia stipitis NLP31. Ethanol and the cellular fatty acid of yeast were analyzed by high performance liquid chromatography (HPLC) and gas chromatography/mass spectrometry (GC/MS). Results indicate that phenolic ketones negatively affected ethanol fermentation of yeast and the lower molecular weight phenolic ketone compound was more toxic. When the concentration of 4-hydroxyacetophenone was 1.5 g/L, at fermentation of 24 h, the xylose utilization ratio, ethanol yield and ethanol concentration decreased by 42.47%, 5.30% and 9.76 g/L, respectively, compared to the control. When phenolic ketones were in the medium, the ratio of unsaturated fatty acids to saturated fatty acids (UFA/SFA) of yeast cells was improved. When 1.5 g/L of three aforementioned phenolic ketones was added to the fermentation medium, the UFA/SFA ratio of yeast cells increased to 3.03, 3.06 and 3.61, respectively, compared to 2.58 of the control, which increased cell membrane fluidity and instability. Therefore, phenolic ketones can reduce the yeast growth, increase the UFA/SFA ratio of yeast and lower ethanol productivity. Effectively reduce or remove the content of lignin degradation products is the key to improve lignocellulose biorefinery.

The enzymology of polyether biosynthesis.

Science.gov (United States)

Liu, Tiangang; Cane, David E; Deng, Zixin

2009-01-01

Polyether ionophore antibiotics are a special class of polyketides widely used in veterinary medicine, and as food additives in animal husbandry. In this article, we review current knowledge about the mechanism of polyether biosynthesis, and the genetic and biochemical strategies used for its study. Several clear differences distinguish it from traditional type I modular polyketide biosynthesis: polyether backbones are assembled by modular polyketide synthases but are modified by two key enzymes, epoxidase and epoxide hydrolase, to generate the product. All double bonds involved in the oxidative cyclization in the polyketide backbone are of E geometry. Chain release in the polyether biosynthetic pathway requires a special type II thioesterase which specifically hydrolyzes the polyether thioester. All these discoveries should be very helpful for a deep understanding of the biosynthetic mechanism of this class of important natural compounds, and for the targeted engineering of polyether derivatives.

Tribological characterization of Al7075–graphite composites fabricated by mechanical alloying and hot extrusion

International Nuclear Information System (INIS)

Deaquino-Lara, R.; Soltani, N.; Bahrami, A.; Gutiérrez-Castañeda, E.; García-Sánchez, E.; Hernandez-Rodríguez, M.A.L.

2015-01-01

Highlights: • Al7075–graphite composites were synthesized by mechanical alloying and hot extrusion. • Effects of graphite content and milling time on the mechanical and wear properties of fabricated composites were analyzed. • Microstructure and worn surfaces of samples were studied by transmission and scanning electron microscope. • The friction coefficient, wear rate and debris thickness of fabricated composite were investigated. - Abstract: Aluminum matrix composites (AMCs) are candidate materials for aerospace and automotive industry owing to their large elastic modulus, improved strength and low wear rate. A simple method for fabrication of Al7075–graphite composites produced by mechanical alloying (MI) and hot extrusion is described in this paper. Effects of milling time (0–10 h) and graphite concentration (0–1.5 wt.%) on friction, hardness and wear resistance of the AMC were investigated. Wear resistance was determined by the pin-on-disk wear method using 20 and 40 N normal loads at a 0.367 m/s sliding velocity. The worn surfaces were examined by scanning electron microscopy (SEM) to identify distinct topographical features for elucidation of the prevailing wear mechanisms. Experimental results indicated considerable improvement in AMC hardness and wear resistance by adding 1.5% G (wt.) and 10 h of milling, showing homogenous distribution of the reinforcement particles in the Al-base metal-matrix composite. It was found that abrasion is the dominant wear mechanism in all extruded composites, whilst a combination of adhesion and delamination seems to be the governing mechanism for the 7075 aluminum alloy

Thermal fatigue of refractory metal / graphite composites for fusion applications

International Nuclear Information System (INIS)

Smid, I.; Nickel, H.

1989-01-01

Reactor grade graphite and molybdenum (TZM) were brazed with different high temperature brazes. The resulting composite tiles had a size of 50 mm x 50 mm with a graphite thickness of 10 mm and a TZM thickness of 5mm. The brazed composites have been tested in electron beam simulation for their thermal fatigue properties. The parameters of these tests were chosen to match NET design specifications for normal operation and 'slow' peak energy deposition. The resulting damages and microstructural changes on the graphites and the brazes are discussed. Additional information is supplied on X-ray diffraction data proving the presence of different phases in the brazes. Finally the influence of a hydrogen plasma on the adaptability of the investigated brazes in fusion devices is discussed. 12 refs., 4 tabs., 4 figs. (Author)

High-Temperature Graphite/Phenolic Composite

Science.gov (United States)

Seal, Ellis C.; Bodepudi, Venu P.; Biggs, Robert W., Jr.; Cranston, John A.

1995-01-01

Graphite-fiber/phenolic-resin composite material retains relatively high strength and modulus of elasticity at temperatures as high as 1,000 degrees F. Costs only 5 to 20 percent as much as refractory materials. Fabrication composite includes curing process in which application of full autoclave pressure delayed until after phenolic resin gels. Curing process allows moisture to escape, so when composite subsequently heated in service, much less expansion of absorbed moisture and much less tendency toward delamination. Developed for nose cone of external fuel tank of Space Shuttle. Other potential aerospace applications for material include leading edges, parts of nozzles, parts of aircraft engines, and heat shields. Terrestrial and aerospace applications include structural firewalls and secondary structures in aircraft, spacecraft, and ships. Modified curing process adapted to composites of phenolic with other fiber reinforcements like glass or quartz. Useful as high-temperature circuit boards and electrical insulators.

Structures and properties of naturally occurring polyether antibiotics.

Science.gov (United States)

Rutkowski, Jacek; Brzezinski, Bogumil

2013-01-01

Polyether ionophores represent a large group of natural, biologically active substances produced by Streptomyces spp. They are lipid soluble and able to transport metal cations across cell membranes. Several of polyether ionophores are widely used as growth promoters in veterinary. Polyether antibiotics show a broad spectrum of bioactivity ranging from antibacterial, antifungal, antiparasitic, antiviral, and tumour cell cytotoxicity. Recently, it has been shown that some of these compounds are able to selectively kill cancer stem cells and multidrug-resistant cancer cells. Thus, they are recognized as new potential anticancer drugs. The biological activity of polyether ionophores is strictly connected with their molecular structure; therefore, the purpose of this paper is to present an overview of their formula, molecular structure, and properties.

Synthesis and Characterization of Poly (ether imide)s Containing Phthalazinone and Isopropyl Moieties

Institute of Scientific and Technical Information of China (English)

无

2001-01-01

A novel poly(ether imide)s containing phthalazinone and isopropyl moieties derived from 2-(4-aminophenyl)-4-[4-(4-aminophenoxy)phenyl]-phthalazin-l-one and bisphenol-A diphthalic anhydride was synthesized by one-step solution condensation polymerization in m-cresol. The polymer was characterized by FTIR, NMR, molecular weights, glass transition temperature,thermal degradation temperature and WAXD.

Biosynthetic machinery of ionophore polyether lasalocid: enzymatic construction of polyether skeleton.

Science.gov (United States)

Minami, Atsushi; Oguri, Hiroki; Watanabe, Kenji; Oikawa, Hideaki

2013-08-01

Diversity of natural polycyclic polyethers originated from very simple yet versatile strategy consisting of epoxidation of linear polyene followed by epoxide opening cascade. To understand two-step enzymatic transformations at molecular basis, a flavin containing monooxygenase (EPX) Lsd18 and an epoxide hydrolase (EH) Lsd19 were selected as model enzymes for extensive investigation on substrate specificity, catalytic mechanism, cofactor requirement and crystal structure. This pioneering study on prototypical lasalocid EPX and EH provides insight into detailed mechanism of ionophore polyether assembly machinery and clarified remaining issues for polyether biosynthesis. Copyright © 2013 Elsevier Ltd. All rights reserved.

Immunological evaluation of polystyrene and poly(ether imide) cell culture inserts with different roughness.

Science.gov (United States)

Roch, Toralf; Krüger, Anne; Kratz, Karl; Ma, Nan; Jung, Friedrich; Lendlein, Andreas

2012-01-01

For the successful clinical and biological application of polymers, their interaction with cells, tissues, and body fluids has to be well characterized. In order to investigate how the physical, chemical, and mechanical properties of candidate biomaterials influence cell behaviours, the testing sample is usually placed in commercially available cell culture plates. Thus, not only the testing sample itself but also the culture dish material might influence the cell behaviour. Therefore, an insert system was created to exclude this influence and allow investigations of the testing material solely. In this study micropatterned inserts prepared from polystyrene (PS) as well as from poly(ether imide) (PEI) with three different roughness levels of i) Rq = 0.29 μm (PS) and 0.23 μm (PEI); ii) Rq = 3.47 μm (PS) and 3.92 μm (PEI); and iii) Rq = 22.16 μm [corrected] (PS) and 22.65 μm (PEI) were explored with regard of their immuno-compatibility including the determination of potential contaminations with endotoxins or other microbial products. The endotoxin levels of the inserts were determined to be less than 0.07 EU/mL, which is well below the U.S. Food and Drug Administration limit of 0.5 EU/mL and the survival of murine macrophages cultured in the inserts was not impaired. Activation of early immune mechanisms such as complement activation and the generation of reactive oxygen species could not be observed. All tested materials had no influence on the cytokine secretion from cells of whole human blood. The investigated inserts were immuno-compatible and apparently free of contaminations with microbial products. The roughness of the inserts had no stimulatory or inhibitory effect on early immune mechanisms. Conclusively, the 24-well plate insert systems introduced in this study allow investigating the interactions of tailored surface properties such as roughness with many other cell types, without the disadvantage of the standard commercially available culture

Elastic representation surfaces of unidirectional graphite/epoxy composites

International Nuclear Information System (INIS)

Kriz, R.D.; Ledbetter, H.M.

1985-01-01

Unidirectional graphite/epoxy composites exhibit high elastic anisotropy and unusual geometrical features in their elastic-property polar diagrams. From the five-component transverse-isotropic elastic-stiffness tensor we compute and display representation surfaces for Young's modulus, torsional modulus, linear compressibility, and Poisson's ratios. Based on Christoffel-equation solutions, we describe some unusual elastic-wave-surface topological features. Musgrave considered in detail the differences between phase-velocity and group-velocity surfaces arising from high elastic anisotropy. For these composites, we find effects similar to, but more dramatic than, Musgrave's. Some new, unexpected results for graphite/epoxy include: a shear-wave velocity that exceeds a longitudinal velocity in the plane transverse to the fiber; a wave that changes polarization character from longitudinal to transverse as the propagation direction sweeps from the fiber axis to the perpendicular axis

Polyimide-polyether mixed conductors as switchable materials for electrochromic devices

Energy Technology Data Exchange (ETDEWEB)

Michot, C; Baril, D; Armand, M [Laboratoire d` Ionique et d` Electrochimie du Solide, ENSEEG, Institut National Polytechnique de Grenoble, Saint-Martin d` Heres (France)

1995-12-01

A new family of redox-active polymers have been obtained by polycondensation of {alpha},{omega}-diamino oligopolyethers with various aromatic tetracarboxylic acid anhydrides. The polyether blocks retain the usual cation co-ordination ability leading to solid-state ionic conduction while the relatively large electron affinity of the bis-imide moieties formed in the block polymers allows the reversible formation of stable radical anions ({sup -} and {sup 2-}) in the range 2-2.6 V vs. Li. Either slow-scan or microelectrode voltammetry indicate that the totality of the redox centres in such materials are readily accessible for all polyether spacer lengths tested (6-22 ether fragments), suggesting both a fast electron-exchange mechanism between anion radicals and a tendency for self assembly (stacking) of the planar aromatic groups. When increasing the number of atoms in the aromatic ring, the peak separation became smaller (benzene>naphthalene>perylene), resulting ultimately in simultaneous 2-electrons injection. These materials, due to the high coloration efficiency of the reduced state and their ready processability in thin films are excellent candidate for the realisation of laminated solid-state electrochromic devices

Polyether-polyester graft copolymer

Science.gov (United States)

Bell, Vernon L. (Inventor)

1987-01-01

Described is a polyether graft polymer having improved solvent resistance and crystalline thermally reversible crosslinks. The copolymer is prepared by a novel process of anionic copolymerization. These polymers exhibit good solvent resistance and are well suited for aircraft parts. Previous aromatic polyethers, also known as polyphenylene oxides, have certain deficiencies which detract from their usefulness. These commercial polymers are often soluble in common solvents including the halocarbon and aromatic hydrocarbon types of paint thinners and removers. This limitation prevents the use of these polyethers in structural articles requiring frequent painting. In addition, the most popular commercially available polyether is a very high melting plastic. This makes it considerably more difficult to fabricate finished parts from this material. These problems are solved by providing an aromatic polyether graft copolymer with improved solvent resistance and crystalline thermally reversible crosslinks. The graft copolymer is formed by converting the carboxyl groups of a carboxylated polyphenylene oxide polymer to ionic carbonyl groups in a suitable solvent, reacting pivalolactone with the dissolved polymer, and adding acid to the solution to produce the graft copolymer.

Covalent attachment of polymeric monolith to polyether ether ketone (PEEK) tubing.

Science.gov (United States)

Lv, Chunguang; Heiter, Jaana; Haljasorg, Tõiv; Leito, Ivo

2016-08-17

A new method of reproducible preparation of vinylic polymeric monolithic columns with a key step of covalently anchoring the monolith to PEEK surface is described. In order to chemically attach the polymer monolith to the tube wall, methacrylate functional groups were introduced onto PEEK surface by a three-step procedure, including surface etching, surface reduction and surface methacryloylation. The chemical state of the modified tubing surface was characterized by attenuated total reflectance infrared (ATR-IR) spectroscopy. It was found that the etching step is the key to successfully modifying the PEEK tubing surface. Poly(styrene-co-divinylbenzene) monoliths were in situ synthesized by thermally initiated free radical copolymerization within the confines of surface-vinylized PEEK tubings of dimensions close to ones conventionally used in HPLC and UHPLC (1.6 mm internal diameter, 10.0-12.5 cm length). Adhesion test was done by measuring the operating pressure drop, which the prepared stationary phases can withstand. Good pressure resistance, up to 140 bar/10 cm (flow rate 0.5 mL min(-1), acetonitrile as a mobile phase), indicates strong bonding of monolith to the tubing wall. The monolithic material was proven to have a permeability of 1.7 × 10 (-14) m(2), applying acetonitrile-water 70:30 (v/v) as a mobile phase. The column performance was reproducible from column to column and was evaluated via the isocratic separation of a series of alkylbenzenes in the reversed-phase mode (acetonitrile-water 70:30, v/v). The numbers of plates per meter at optimal flow rate were found to be between 26 000 and 32 000 for the different analytes. Copyright © 2016 Elsevier B.V. All rights reserved.

Synthesis and Process Optimization of Electrospun PEEK-Sulfonated Nanofibers by Response Surface Methodology

Directory of Open Access Journals (Sweden)

Carlo Boaretti

2015-07-01

Full Text Available In this study electrospun nanofibers of partially sulfonated polyether ether ketone have been produced as a preliminary step for a possible development of composite proton exchange membranes for fuel cells. Response surface methodology has been employed for the modelling and optimization of the electrospinning process, using a Box-Behnken design. The investigation, based on a second order polynomial model, has been focused on the analysis of the effect of both process (voltage, tip-to-collector distance, flow rate and material (sulfonation degree variables on the mean fiber diameter. The final model has been verified by a series of statistical tests on the residuals and validated by a comparison procedure of samples at different sulfonation degrees, realized according to optimized conditions, for the production of homogeneous thin nanofibers.

Intermediates in monensin biosynthesis: A late step in biosynthesis of the polyether ionophore monensin is crucial for the integrity of cation binding

Directory of Open Access Journals (Sweden)

Wolfgang Hüttel

2014-02-01

Full Text Available Polyether antibiotics such as monensin are biosynthesised via a cascade of directed ring expansions operating on a putative polyepoxide precursor. The resulting structures containing fused cyclic ethers and a lipophilic backbone can form strong ionophoric complexes with certain metal cations. In this work, we demonstrate for monensin biosynthesis that, as well as ether formation, a late-stage hydroxylation step is crucial for the correct formation of the sodium monensin complex. We have investigated the last two steps in monensin biosynthesis, namely hydroxylation catalysed by the P450 monooxygenase MonD and O-methylation catalysed by the methyl-transferase MonE. The corresponding genes were deleted in-frame in a monensin-overproducing strain of Streptomyces cinnamonensis. The mutants produced the expected monensin derivatives in excellent yields (ΔmonD: 1.13 g L−1 dehydroxymonensin; ΔmonE: 0.50 g L−1 demethylmonensin; and double mutant ΔmonDΔmonE: 0.34 g L−1 dehydroxydemethylmonensin. Single crystals were obtained from purified fractions of dehydroxymonensin and demethylmonensin. X-ray structure analysis revealed that the conformation of sodium dimethylmonensin is very similar to that of sodium monensin. In contrast, the coordination of the sodium ion is significantly different in the sodium dehydroxymonensin complex. This shows that the final constitution of the sodium monensin complex requires this tailoring step as well as polyether formation.

Intermediates in monensin biosynthesis: A late step in biosynthesis of the polyether ionophore monensin is crucial for the integrity of cation binding.

Science.gov (United States)

Hüttel, Wolfgang; Spencer, Jonathan B; Leadlay, Peter F

2014-01-01

Polyether antibiotics such as monensin are biosynthesised via a cascade of directed ring expansions operating on a putative polyepoxide precursor. The resulting structures containing fused cyclic ethers and a lipophilic backbone can form strong ionophoric complexes with certain metal cations. In this work, we demonstrate for monensin biosynthesis that, as well as ether formation, a late-stage hydroxylation step is crucial for the correct formation of the sodium monensin complex. We have investigated the last two steps in monensin biosynthesis, namely hydroxylation catalysed by the P450 monooxygenase MonD and O-methylation catalysed by the methyl-transferase MonE. The corresponding genes were deleted in-frame in a monensin-overproducing strain of Streptomyces cinnamonensis. The mutants produced the expected monensin derivatives in excellent yields (ΔmonD: 1.13 g L(-1) dehydroxymonensin; ΔmonE: 0.50 g L(-1) demethylmonensin; and double mutant ΔmonDΔmonE: 0.34 g L(-1) dehydroxydemethylmonensin). Single crystals were obtained from purified fractions of dehydroxymonensin and demethylmonensin. X-ray structure analysis revealed that the conformation of sodium dimethylmonensin is very similar to that of sodium monensin. In contrast, the coordination of the sodium ion is significantly different in the sodium dehydroxymonensin complex. This shows that the final constitution of the sodium monensin complex requires this tailoring step as well as polyether formation.

Molecular dynamics simulations of polyethers and a quaternary ammonium ionic liquid as CO2 absorbers

Science.gov (United States)

Cardoso, Piercarlo Fortunato; Fernandez, Juan S. L. C.; Lepre, Luiz Fernando; Ando, Rômulo Augusto; Costa Gomes, Margarida F.; Siqueira, Leonardo J. A.

2018-04-01

The properties of mixtures of butyltrimethylammonium bis(trifluoromethylsulfonyl)imide, [N4111][NTf2], with poly(ethyleneglycol) dimethyl ether, PEO, were described as a function of PEO chain size by molecular dynamics simulations. Both PEO chain size and mixture composition revealed to play a significant role in determining the structure and the dynamics of the fluids. The remarkably higher viscosity observed for mixtures composed by 0.25 mole fraction of PEO was attributed to the increase in the gauche population of OCCO dihedral of the polyether of longer chains. The negative solvation enthalpy (ΔsolH < 0) and entropy (ΔsolS < 0) revealed a favorable CO2 absorption by the neat and mixture systems. The CO2 absorption was higher in neat PEO, particularly considering longer chains. The gas solubility in the mixtures presented intermediate values in comparison to the neat PEO and neat ionic liquid. The CO2 solutions had their structures discussed in the light of the calculated radial and spatial distribution functions.

In situ polymerization of monomers for polyphenylquinoxaline-graphite fiber composites

Science.gov (United States)

Serafini, T. T.; Delvigs, P.; Vannucci, R. D.

1974-01-01

In situ polymerization of monomers was used to prepare graphite-fiber-reinforced polyphenylquinoxaline composites. Six different monomer combinations were investigated. Composite mechanical property retention characteristics were determined at 316 C (600 F) over an extended time period.

Graphite oxide and molybdenum disulfide composite for hydrogen evolution reaction

Science.gov (United States)

Niyitanga, Theophile; Jeong, Hae Kyung

2017-10-01

Graphite oxide and molybdenum disulfide (GO-MoS2) composite is prepared through a wet process by using hydrolysis of ammonium tetrathiomolybdate, and it exhibits excellent catalytic activity of the hydrogen evolution reaction (HER) with a low overpotential of -0.47 V, which is almost two and three times lower than those of precursor MoS2 and GO. The high performance of HER of the composite attributes to the reduced GO supporting MoS2, providing a conducting network for fast electron transport from MoS2 to electrodes. The composite also shows high stability after 500 cycles, demonstrating a synergistic effect of MoS2 and GO for efficient HER.

Polyether ionophores-promising bioactive molecules for cancer therapy.

Science.gov (United States)

Huczyński, Adam

2012-12-01

The natural polyether ionophore antibiotics might be important chemotherapeutic agents for the treatment of cancer. In this article, the pharmacology and anticancer activity of the polyether ionophores undergoing pre-clinical evaluation are reviewed. Most of polyether ionophores have shown potent activity against the proliferation of various cancer cells, including those that display multidrug resistance (MDR) and cancer stem cells (CSC). The mechanism underlying the anticancer activity of ionophore agents can be related to their ability to form complexes with metal cations and transport them across cellular and subcellular membranes. Increasing evidence shows that the anticancer activity of polyether ionophores may be a consequence of the induction of apoptosis leading to apoptotic cell death, arresting cell cycle progression, induction of the cell oxidative stress, loss of mitochondrial membrane potential, reversion of MDR, synergistic anticancer effect with other anticancer drugs, etc. Continued investigation of the mechanisms of action and development of new polyether ionophores and their derivatives may provide more effective therapeutic drugs for cancer treatments. Copyright © 2012 Elsevier Ltd. All rights reserved.

Measurements of the thermophysical properties of graphite composites for a neutron target converter

Energy Technology Data Exchange (ETDEWEB)

Zhmurikov, E.I. [Budker Institute of Nuclear Physics, 690090 Novosibirsk, SB RAS (Russian Federation); Savchenko, I.V.; Stankus, S.V.; Yatsuk, O.S. [Kutateladze Institute of Thermal Physics, 690090 Novosibirsk, SB RAS (Russian Federation); Tecchio, L.B., E-mail: tecchio@lnl.infn.it [Laboratori Nazionali di Legnaro-Istituto Nazionale di Fisica Nucleare, Legnaro (Italy)

2012-05-11

The thermo-physical characteristics of both nuclear, industrial graphite, such as MPG-6 from NIIGRAFIT or SGL composite from SGL Carbon Group, and the first synthesized graphite composite based on a carbon {sup 13}S isotope have been measured from room temperature to 1675 K by laser flash method on an LFA-427 setup from Netzsch (Germany). The results obtained are compared to the previous data of X-Ray analysis and high-resolution electron microscopy and can be used in thermal calculations of the design of a neutron converter graphite target.

Measurements of the thermophysical properties of graphite composites for a neutron target converter

International Nuclear Information System (INIS)

Zhmurikov, E.I.; Savchenko, I.V.; Stankus, S.V.; Yatsuk, O.S.; Tecchio, L.B.

2012-01-01

The thermo-physical characteristics of both nuclear, industrial graphite, such as MPG-6 from NIIGRAFIT or SGL composite from SGL Carbon Group, and the first synthesized graphite composite based on a carbon 13 S isotope have been measured from room temperature to 1675 K by laser flash method on an LFA-427 setup from Netzsch (Germany). The results obtained are compared to the previous data of X-Ray analysis and high-resolution electron microscopy and can be used in thermal calculations of the design of a neutron converter graphite target.

Graphite nanoreinforcements in polymer nanocomposites

Science.gov (United States)

Fukushima, Hiroyuki

Nanocomposites composed of polymer matrices with clay reinforcements of less than 100 nm in size, are being considered for applications such as interior and exterior accessories for automobiles, structural components for portable electronic devices, and films for food packaging. While most nanocomposite research has focused on exfoliated clay platelets, the same nanoreinforcement concept can be applied to another layered material, graphite, to produce nanoplatelets and nanocomposites. Graphite is the stiffest material found in nature (Young's Modulus = 1060 GPa), having a modulus several times that of clay, but also with excellent electrical and thermal conductivity. The key to utilizing graphite as a platelet nanoreinforcement is in the ability to exfoliate this material. Also, if the appropriate surface treatment can be found for graphite, its exfoliation and dispersion in a polymer matrix will result in a composite with not only excellent mechanical properties but electrical properties as well, opening up many new structural applications as well as non-structural ones where electromagnetic shielding and high thermal conductivity are requirements. In this research, a new process to fabricate exfoliated nano-scale graphite platelets was established (Patent pending). The size of the resulted graphite platelets was less than 1 um in diameter and 10 nm in thickness, and the surface area of the material was around 100 m2/g. The reduction of size showed positive effect on mechanical properties of composites because of the increased edge area and more functional groups attached with it. Also various surface treatment techniques were applied to the graphite nanoplatelets to improve the surface condition. As a result, acrylamide grafting treatment was found to enhance the dispersion and adhesion of graphite flakes in epoxy matrices. The resulted composites showed better mechanical properties than those with commercially available carbon fibers, vapor grown carbon fibers

Temperature dependence of broadline NMR spectra of water-soaked, epoxy-graphite composites

Science.gov (United States)

Lawing, David; Fornes, R. E.; Gilbert, R. D.; Memory, J. D.

1981-10-01

Water-soaked, epoxy resin-graphite fiber composites show a waterline in their broadline proton NMR spectrum which indicates a state of intermediate mobility between the solid and free water liquid states. The line is still present at -42 °C, but shows a reversible decrease in amplitude with decreasing temperature. The line is isotropic upon rotation of the fiber axis with respect to the external magnetic field.

Gas storage cylinder formed from a composition containing thermally exfoliated graphite

Science.gov (United States)

Prud'Homme, Robert K. (Inventor); Aksay, Ilhan A. (Inventor)

2012-01-01

A gas storage cylinder or gas storage cylinder liner, formed from a polymer composite, containing at least one polymer and a modified graphite oxide material, which is a thermally exfoliated graphite oxide with a surface area of from about 300 m(exp 2)/g to 2600 m(exp 2)2/g.

The Continuing Saga of the Marine Polyether Biotoxins

Science.gov (United States)

Nicolaou, K. C.; Frederick, Michael O.; Aversa, Robert J.

2009-01-01

Lead-in Brevetoxin B emerged from the sea and into the laboratories of Nakanishi and Clardy who, in 1981, reported its magnificent and unprecedented structure. With its ladder-like fused polyether molecular architecture, potent toxicity, and fascinating voltage-sensitive sodium channel-based mechanism of action, it immediately captured the imagination of chemists around the world. Their synthetic escapades resulted in numerous new synthetic methods and strategies for the construction of cyclic ethers, and culminated in several impressive total syntheses of this imposing molecule and some of its equally challenging siblings that followed. Indeed, many more brevetoxin-type marine polyethers have been reported since 1981 with maitotoxin being not only the most complex and most toxic of the class, but also the largest non-polymeric natural product known to date. In this article, we begin with a brief history of these biotoxins and the phenomena that led to their isolation and highlight their biological properties and mechanism of action. We then review the chemical synthesis endeavors so far published in this long running saga, placing particular emphasis on the new synthetic methods and technologies discovered, developed and applied to their total syntheses over the last few decades. Finally, we conclude with a discussion of the, as yet unfinished, story of maitotoxin, and project into the future of this fascinating area of research. PMID:18763702

Preparation and characterization of copper-graphite composites by electrical explosion of wire in liquid.

Science.gov (United States)

Bien, T N; Gul, W H; Bac, L H; Kim, J C

2014-11-01

Copper-graphite nanocomposites containing 5 vol.% graphite were prepared by a powder metallurgy route using an electrical wire explosion (EEW) in liquid method and spark plasma sintering (SPS) process. Graphite rods with a 0.3 mm diameter and copper wire with a 0.2 mm diameter were used as raw materials for EEWin liquid. To compare, a pure copper and copper-graphite mixture was also prepared. The fabricated graphite was in the form of a nanosheet, onto which copper particles were coated. Sintering was performed at 900 degrees C at a heating rate of 30 degrees C/min for 10 min and under a pressure of 70 MPa. The density of the sintered composite samples was measured by the Archimedes method. A wear test was performed by a ball-on-disc tribometer under dry conditions at room temperature in air. The presence of graphite effectively reduced the wear of composites. The copper-graphite nanocomposites prepared by EEW had lower wear rates than pure copper material and simple mixed copper-graphite.

Preparation of graphite dispersed copper composite on copper plate with CO2 laser

Science.gov (United States)

Yokoyama, S.; Ishikawa, Y.; Muizz, M. N. A.; Hisyamudin, M. N. N.; Nishiyama, K.; Sasano, J.; Izaki, M.

2018-01-01

It was tried in this work to prepare the graphite dispersed copper composite locally on a copper plate with a CO2 laser. The objectives of this study were to clear whether copper graphite composite was prepared on a copper plate and how the composite was prepared. The carbon content at the laser spot decreased with the laser irradiation time. This mainly resulted from the elimination by the laser trapping. The carbon content at the outside of the laser spot increased with time. Both the laser ablation and the laser trapping did not act on the graphite particles at the outside of the laser spot. Because the copper at the outside of the laser spot melted by the heat conduction from the laser spot, the particles were fixed by the wetting. However, the graphite particles were half-floated on the copper plate. The Vickers hardness decreased with an increase with laser irradiation time because of annealing.

N-doped graphene/graphite composite as a conductive agent-free anode material for lithium ion batteries with greatly enhanced electrochemical performance

International Nuclear Information System (INIS)

Guanghui, Wu; Ruiyi, Li; Zaijun, Li; Junkang, Liu; Zhiguo, Gu; Guangli, Wang

2015-01-01

Graphical abstract: The study reported a novel N-doped graphene/graphite anode material for lithium ion batteries. The composite exhibits a largely enhanced electrochemical performance. The study also provides an attractive approach for the fabrication of various graphite-based materials for high power batteries. Display Omitted -- Highlights: • The paper developed a new N-doped graphene/graphite composite for lithium ion battery • The composite contains a three-dimensional graphene framework with rich of open pores • The hybrid offers a higher electrical conductivity when compared with pristine graphite • The hybrid electrode provides a greatly enhanced electrochemical performance • The study provides a prominent approach for fabrication of graphite-based materials -- ABSTRACT: Present graphite anode cannot meet the increasing requirement of electronic devices and electric vehicles due to its low specific capacity, poor cycle stability and low rate capability. The study reported a promising N-doped graphene/graphite composite as a conductive agent-free anode material for lithium ion batteries. Herein, graphite oxide and urea were dispersed in ultrapure water and partly reduced by ascorbic acid. Followed by mixing with graphite and hydrothermal treatment to produce graphene oxide/graphite hydrogel. The hydrogel was dried and finally annealed in Ar/H 2 to obtain N-doped graphene/graphite composite. The result shows that all of graphite particles was dispersed in three-dimensional graphene framework with a rich of open pores. The open pore accelerates the electrolyte transport. The graphene framework works as a conductive agent and graphite particle connector and improves the electron transfer. Electrical conductivity of the composite reaches 5912 S m −1 , which is much better than that of the pristine graphite (4018 S m −1 ). The graphene framework also acts as an expansion absorber in the anodes of lithium ion battery to relieve the large strains

New aromatic activated dihalides and bisphenol monomers for the preparation of novel poly(arylene ethers)

Science.gov (United States)

Wolfe, James F.

1993-01-01

The goal of this research program was to synthesize a series of unique monomers of type I to be utilized at NASA-Langley in the preparation of new poly(arylene ether ketones), poly(arylene ether ketosulfones), and poly(arylene ether ketophosphine oxides). These A-A and A-B monomer systems, which possess activated aryl halide and/or phenolic end groups, are accessible via condensation reactions of appropriately substituted aryl acetonitrile carbanions with activated aryl dihalides followed by oxidative decyanation.

Biomedical potentials of crown ethers: prospective antitumor agents.

Science.gov (United States)

Kralj, Marijeta; Tusek-Bozić, Ljerka; Frkanec, Leo

2008-10-01

Crown ethers are of enormous interest and importance in chemistry, biochemistry, materials science, catalysis, separation, transport and encapsulated processes, as well as in the design and synthesis of various synthetic systems with specific properties, diverse capabilities, and programmable functions. Classical crown ethers are macrocyclic polyethers that contain 3-20 oxygen atoms separated from each other by two or more carbon atoms. They are exceptionally versatile in selectively binding a range of metal ions and a variety of organic neutral and ionic species. Crown ethers are currently being studied and used in a variety of applications beyond their traditional place in chemistry. This review presents additional applications and the ever-increasing biomedical potentials of these intriguing compounds, with particular emphasis on the prospects of their relevance as anticancer agents. We believe that further research in this direction should be encouraged, as crown compounds could either induce toxicities that are different from those of conventional antitumor drugs, or complement drugs in current use, thereby providing a valuable adjunct to therapy.

Hard carbon coated nano-Si/graphite composite as a high performance anode for Li-ion batteries

Energy Technology Data Exchange (ETDEWEB)

Jeong, Sookyung; Li, Xiaolin; Zheng, Jianming; Yan, Pengfei; Cao, Ruiguo; Jung, Hee Joon; Wang, Chong M.; Liu, Jun; Zhang, Jiguang

2016-08-27

With the ever increasing demands on Li-ion batteries with higher energy densities, alternative anode with higher reversible capacity is required to replace the conventional graphite anode. Here, we demonstrate a cost-effective hydrothermal-carbonization approach to prepare the hard carbon coated nano-Si/graphite (HC-nSi/G) composite as a high performance anode for Li-ion batteries. In this hierarchical structured composite, the hard carbon coating layer not only provides an efficient pathway for electron transfer, but also alleviates the volume variation of silicon during charge/discharge processes. The HC-nSi/G composite electrode shows excellent electrochemical performances including a high specific capacity of 878.6 mAh g-1 based on the total weight of composite, good rate performance and a decent cycling stability, which is promising for practical applications.

Thermodynamic Simulation of Equilibrium Composition of Reaction Products at Dehydration of a Technological Channel in a Uranium-Graphite Reactor

Science.gov (United States)

Pavliuk, A. O.; Zagumennov, V. S.; Kotlyarevskiy, S. G.; Bespala, E. V.

2018-01-01

The problems of accumulation of nuclear fuel spills in the graphite stack in the course of operation of uranium-graphite nuclear reactors are considered. The results of thermodynamic analysis of the processes in the graphite stack at dehydration of a technological channel, fuel element shell unsealing and migration of fission products, and activation of stable nuclides in structural elements of the reactor and actinides inside the graphite moderator are given. The main chemical reactions and compounds that are produced in these modes in the reactor channel during its operation and that may be hazardous after its shutdown and decommissioning are presented. Thermodynamic simulation of the equilibrium composition is performed using the specialized code TERRA. The results of thermodynamic simulation of the equilibrium composition in different cases of technological channel dehydration in the course of the reactor operation show that, if the temperature inside the active core of the nuclear reactor increases to the melting temperature of the fuel element, oxides and carbides of nuclear fuel are produced. The mathematical model of the nonstationary heat transfer in a graphite stack of a uranium-graphite reactor in the case of the technological channel dehydration is presented. The results of calculated temperature evolution at the center of the fuel element, the replaceable graphite element, the air gap, and in the surface layer of the block graphite are given. The numerical results show that, in the case of dehydration of the technological channel in the uranium-graphite reactor with metallic uranium, the main reaction product is uranium dioxide UO2 in the condensed phase. Low probability of production of pyrophoric uranium compounds (UH3) in the graphite stack is proven, which allows one to disassemble the graphite stack without the risk of spontaneous graphite ignition in the course of decommissioning of the uranium-graphite nuclear reactor.

40 CFR 721.405 - Polyether acrylate.

Science.gov (United States)

2010-07-01

... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Polyether acrylate. 721.405 Section... § 721.405 Polyether acrylate. (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified generically as a polyether acrylate (PMN P-95-666) is subject to...

Surface modification of carbon fibers by a polyether sulfone emulsion sizing for increased interfacial adhesion with polyether sulfone

Energy Technology Data Exchange (ETDEWEB)

Yuan, Haojie [National Engineering Laboratory for Carbon Fiber Technology, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Zhang, Shouchun, E-mail: zschun@sxicc.ac.cn [National Engineering Laboratory for Carbon Fiber Technology, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001 (China); Lu, Chunxiang [National Engineering Laboratory for Carbon Fiber Technology, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001 (China)

2014-10-30

Highlights: • A polyether sulfone emulsion (PES) sizing was prepared for the first time. • The sizing enhanced the surface activity and wettability of carbon fibers. • Compared to the original sizing, the PES emulsion sizing resulted in an 18.4% increase in the interlaminar shear strength of carbon fiber/PES composites. • Important influences of emulsifier on the fiber surface and composite interface were demonstrated. • The reinforcing mechanisms are the improved fiber surface wettability and interfacial compatibility in composites. - Abstract: Interests on carbon fiber-reinforced thermoplastic composites are growing rapidly, but the challenges with poor interfacial adhesion have slowed their adoption. In this work, a polyether sulfone (PES) emulsion sizing was prepared successfully for increased interfacial adhesion of carbon fiber/PES composites. To obtain a high-quality PES emulsion sizing, the key factor, emulsifier concentration, was studied by dynamic light scattering technique. The results demonstrated that the suitable weight ratio of PES to emulsifier was 8:3, and the resulting PES emulsion sizing had an average particle diameter of 117 nm and Zeta potential of −52.6 mV. After sizing, the surface oxygen-containing functional groups, free energy and wettability of carbon fibers increased significantly, which were advantageous to promote molecular-level contact between carbon fiber and PES. Finally, short beam shear tests were performed to evaluate the interfacial adhesion of carbon fiber/PES composites. The results indicated that PES emulsion sizing played a critical role for the enhanced interfacial adhesion in carbon fiber/PES composites, and a 26% increase of interlaminar shear strength was achieved, because of the improved fiber surface wettability and interfacial compatibility between carbon fiber and PES.

Surface modification of carbon fibers by a polyether sulfone emulsion sizing for increased interfacial adhesion with polyether sulfone

International Nuclear Information System (INIS)

Yuan, Haojie; Zhang, Shouchun; Lu, Chunxiang

2014-01-01

Highlights: • A polyether sulfone emulsion (PES) sizing was prepared for the first time. • The sizing enhanced the surface activity and wettability of carbon fibers. • Compared to the original sizing, the PES emulsion sizing resulted in an 18.4% increase in the interlaminar shear strength of carbon fiber/PES composites. • Important influences of emulsifier on the fiber surface and composite interface were demonstrated. • The reinforcing mechanisms are the improved fiber surface wettability and interfacial compatibility in composites. - Abstract: Interests on carbon fiber-reinforced thermoplastic composites are growing rapidly, but the challenges with poor interfacial adhesion have slowed their adoption. In this work, a polyether sulfone (PES) emulsion sizing was prepared successfully for increased interfacial adhesion of carbon fiber/PES composites. To obtain a high-quality PES emulsion sizing, the key factor, emulsifier concentration, was studied by dynamic light scattering technique. The results demonstrated that the suitable weight ratio of PES to emulsifier was 8:3, and the resulting PES emulsion sizing had an average particle diameter of 117 nm and Zeta potential of −52.6 mV. After sizing, the surface oxygen-containing functional groups, free energy and wettability of carbon fibers increased significantly, which were advantageous to promote molecular-level contact between carbon fiber and PES. Finally, short beam shear tests were performed to evaluate the interfacial adhesion of carbon fiber/PES composites. The results indicated that PES emulsion sizing played a critical role for the enhanced interfacial adhesion in carbon fiber/PES composites, and a 26% increase of interlaminar shear strength was achieved, because of the improved fiber surface wettability and interfacial compatibility between carbon fiber and PES

Thermal and Dielectric Behavior Studies of Poly(Arylene Ether Sulfones with Sulfonated and Phosphonated Pendants

Directory of Open Access Journals (Sweden)

Shimoga D. Ganesh

2016-01-01

Full Text Available The present paper discusses the aspects of the synthesizing valeric acid based poly(ether sulfones with active carboxylic acid pendants (VALPSU from solution polymerization technique via nucleophilic displacement polycondensation reaction among 4,4′-dichlorodiphenyl sulfone (DCDPS and 4,4′-bis(4-hydroxyphenyl valeric acid (BHPA. The conditions necessary to synthesize and purify the polymer were investigated in some detail. The synthesized poly(ether sulfones comprise sulfone and ether linkages in addition to reactive carboxylic acid functionality; these active carboxylic acid functional groups were exploited to hold the phenyl sulphonic acid and phenyl phosphonic acid pendants. The phenyl sulphonic acid pendants in VALPSU were easily constructed by altering active carboxylic acid moieties by sulfanilic acid using N,N′-dicyclohexylcarbodiimide (DCC mediated mild synthetic route, whereas the latter one was built in two steps. Initially, polyphosphoric acid condensation with VALPSU by 4-bromoaniline and next straightforward palladium catalyzed synthetic route, in both of which acidic pendants are clenched by polymer backbone via amide linkage. Without impairing the primary polymeric backbone modified polymers were prepared by varying the stoichiometric ratios of respective combinations. All the polymers were physicochemically characterized and pressed into tablets; electrical contacts were established to study the dielectric properties. Finally, the influence of the acidic pendants on the dielectric properties was examined.

Aluminum-graphite composite produced by mechanical milling and hot extrusion

International Nuclear Information System (INIS)

Flores-Zamora, M.I.; Estrada-Guel, I.; Gonzalez-Hernandez, J.; Miki-Yoshida, M.; Martinez-Sanchez, R.

2007-01-01

Aluminum-graphite composites were produced by mechanical milling followed by hot extrusion. Graphite content was varied between 0 and 1 wt.%. Al-graphite mixtures were initially mixed in a shaker mill without ball, followed by mechanical milling in a High-energy simoloyer mill for 2 h under argon atmosphere. Milled powders were subsequently pressed at ∼950 MPa for 2 min, and next sintered under vacuum for 3 h at 823 K. Finally, sintered products were held for 0.5 h at 823 K and hot extruded using indirect extrusion. Tension and compression tests were carried out to determine the yield stress and maximum stress of the materials. We found that the mechanical resistance increased as the graphite content increased. Microstructural characterization was done by transmission electron microscopy. Al-O-C nanofibers and graphite nanoparticles were observed in extruded samples by transmission electron microscopy. These nanoparticles and nanofibers seemed to be responsible of the reinforcement phenomenon

Mechanical Degradation of Graphite/PVDF Composite Electrodes: A Model-Experimental Study

Energy Technology Data Exchange (ETDEWEB)

Takahashi, K; Higa, K; Mair, S; Chintapalli, M; Balsara, N; Srinivasan, V

2015-12-11

Mechanical failure modes of a graphite/polyvinylidene difluoride (PVDF) composite electrode for lithium-ion batteries were investigated by combining realistic stress-stain tests and mathematical model predictions. Samples of PVDF mixed with conductive additive were prepared in a similar way to graphite electrodes and tested while submerged in electrolyte solution. Young's modulus and tensile strength values of wet samples were found to be approximately one-fifth and one-half of those measured for dry samples. Simulations of graphite particles surrounded by binder layers given the measured material property values suggest that the particles are unlikely to experience mechanical damage during cycling, but that the fate of the surrounding composite of PVDF and conductive additive depends completely upon the conditions under which its mechanical properties were obtained. Simulations using realistic property values produced results that were consistent with earlier experimental observations.

Molecular dynamics simulation of damage cascade creation in SiC composites containing SiC/graphite interface

Energy Technology Data Exchange (ETDEWEB)

Wallace, Joseph; Chen, Di; Wang, Jing; Shao, Lin, E-mail: lshao@tamu.edu

2013-07-15

Silicon carbide composites have been investigated for their use as structural materials for advanced nuclear reactor designs. Although the composites have significantly enhanced mechanical properties and structure integrity, there is little known about the behavior of defects in the presence of a graphite-silicon carbide interface. In this study, molecular dynamics simulations have been used to model defect creation and clustering in a composite containing a SiC/graphite interface. Evolution of displacements as a function of time were studied and compared to bulk SiC. The results show that the first a few SiC atomic layers closest to the interface are easily damaged. However, beyond these first few atomic layers the system appears to be unaffected by the SiC interface.

Self-assembly of graphitic carbon nitride nanosheets–carbon nanotube composite for electrochemical simultaneous determination of catechol and hydroquinone

International Nuclear Information System (INIS)

Zhang, Hanqiang; Huang, Yihong; Hu, Shirong; Huang, Qitong; Wei, Chan; Zhang, Wuxiang; Yang, Weize; Dong, Peihui; Hao, Aiyou

2015-01-01

Graphical abstract: Schematic diagram of hydrothermal synthesis graphitic carbon nitride nanosheets-carbon nanotube composite and theirs application for electrochemical sensing catechol and hydroquinone. - Highlights: • Self-assembly of graphitic carbon nitride nanosheets-carbon nanotube composite. • CNNS-CNT show more stronger conductivity than CNNS and CNT. • CNNS-CNT has been performed for detection of catechol and hydroquinone. • The probe was applied to detect practical samples with satisfactory results. - Abstract: In this paper, three-dimensional (3D) graphitic carbon nitride nanosheets-carbon nanotube (CNNS-CNT) composite was synthesized via hydrothermal reaction of 2D CNNS and 1D CNT-COOH by π-π stacking and electrostatic interactions. This CNNS-CNT composite was characterized by transmission electron microscope, scanning electron microscope, x-ray diffraction and fourier-transform infrared. In addition, the CNNS-CNT composite displayed excellent conductivity comparing with CNNS and CNT-COOH monomer. This composite was applied for electrochemical simultaneous determination of catechol (CC) and hydroquinone (HQ) with good sensitivity, wide linear range and low detection limit. In addition, this CNNS-CNT composite modified electrode was also applied to detect practical samples with satisfactory results

Inverting the diastereoselectivity of the mukaiyama-michael addition with graphite-based catalysts

KAUST Repository

Acocella, Maria Rosaria

2014-02-07

Here, we show that graphite-based catalysts, mainly graphite oxide (GO) and exfoliated GO, are effective recyclable catalysts for a relevant stereoselective Mukaiyama-Michael addition, outperforming currently available catalysts. Moreover, the graphite-based catalysts described here invert the diastereoselectivity relative to that observed with known catalysts, with the unprecedented large prevalence of the anti diastereoisomer. This inverted diastereoselectivity is increased when the catalyst concentration is reduced and after catalyst recycling. Density functional theory calculations suggest that the selectivity is determined by two types of supramolecular interactions operating between the catalyst and the substrates at the diastereoselectivity- determining transition state, specifically, the π-stacking of b-nitrostyrene with graphite and the van der Waals interaction between the SiMe3 group of the silyl ether and the graphite. © 2013 American Chemical Society.

Graphene synthesis from graphite/Ni composite films grown by sputtering

International Nuclear Information System (INIS)

Shin, Dong Hee; Yang, Seung Bum; Shin, Dong Yeol; Kim, Chang Oh; Kim, Sung; Choi, Suk Ho; Paek, Sang Hyon

2012-01-01

Graphite/Ni composite films have been deposited on SiO 2 /Si (100) wafers by varying their graphite concentration (n G ) and thickness (t) from 2 to 12 wt% and 40 to 400 nm, respectively, in a RF sputtering system, subsequently annealed at 900 .deg. C for 4 min, and then slowly cooled to room temperature to form graphene layers on Ni surfaces. Several structural-analysis techniques reveal the optimum nG (∼8 wt%) and t (∼160 nm) of the composite films for the synthesis of fewest-layer, defect-minimized graphene. At the annealing temperature, carbon atoms diffuse out from the composite film, followed by their precipitation as graphene on the Ni layer as the carbon solubility limit in Ni is reached during the cooling period. Based on this mechanism, the optimum conditions are explained. Our approach provides an advantage in that the number of layers can be simply tuned by varying n G and t of the composite films.

(1-Adamantyl)methyl glycidyl ether: a versatile building block for living polymerization.

Science.gov (United States)

Moers, Christian; Wrazidlo, Robert; Natalello, Adrian; Netz, Isabelle; Mondeshki, Mihail; Frey, Holger

2014-06-01

(1-Adamantyl)methyl glycidyl ether (AdaGE) is introduced as a versatile monomer for oxyanionic polymerization, enabling controlled incorporation of adamantyl moieties in aliphatic polyethers. Via copolymerization with ethoxyethyl glycidyl ether (EEGE) and subsequent cleavage of the acetal protection groups of EEGE, hydrophilic linear polyglycerols with an adjustable amount of pendant adamantyl moieties are obtained. The adamantyl unit permits control over thermal properties and solubility profile of these polymers (LCST). Additionally, AdaGE is utilized as a termination agent in carbanionic polymerization, affording adamantyl-terminated polymers. Using these structures as macroinitiators for the polymerization of ethylene oxide affords amphiphilic, in-chain adamantyl-functionalized block copolymers. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Curing behaviour of epoxy resin/graphite composites containing ionic liquid

International Nuclear Information System (INIS)

Guo Baochun; Wan Jingjing; Lei Yanda; Jia Demin

2009-01-01

By adopting the isoconversional method, subtle changes in the curing activation energy (E α ) among epoxy resin/graphite composites by the inclusion of expanded graphite (EG), ionic liquid of 1-butyl-3-methyl-imidazolium hexafluorophosphate ([BMIm]PF 6 ) or their combination are shown in the whole conversion range. At lower concentrations (1 phr) of EG, compared with the E α of the neat epoxy resin, the composite with EG has a lower E α before the gelation, and a higher E α after the gelation. At higher concentrations of EG, however, in the whole conversion range, the composite with EG shows a higher E α compared with the neat epoxy resin. As the curing proceeded, a peculiar increase in E α is found in systems containing [BMIm]PF 6 . Due to the formation of hydrogen bonding between [BMIm]PF 6 and the hardener (Jeffamine), the reactivity of Jeffamine is considerably decreased, leading to a much higher E α in [BMIm]PF 6 -containing systems, especially at higher conversion. In systems containing a combination of [BMIm]PF 6 and EG, due to the interactions between EG and [BMIm]PF 6 , the shielding effect provided by the well-dispersed EG sheets constrains the formation of the hydrogen bonding between [BMIm]PF 6 and Jeffamine, leading to lowered E α compared with that for the system containing [BMIm]PF 6 only.

PNGS-A unit 4 composite graphite valve packing program

International Nuclear Information System (INIS)

Meaney, F.

1992-01-01

During the outage of Pickering 4 for retubing and rehabilitation, a composite graphite packing program was completed on 100 conventional valves and 50 nuclear valves. This paper describes component refurbishment, related maintenance, and manpower requirements. 2 figs

Radiation effect of polyether-urethane under action of different ionizing radiation

International Nuclear Information System (INIS)

Huang Wei; Chen Xiaojun; Gao Xiaoling; Xu Yunshu; Fu Yibei

2006-01-01

The research concerns in the radiation effect of γ-ray and electron beam on polyether-urethane. The thermal property and radical intensity were determined by differential thermal gravimetric analysis and electron spin resonance. The composition and content of gas products from samples irradiated by different ionizing radiation were analyzed by gas chromatography. The action mechanism of these two radiation resources of γ-ray and electron beam are same, but the means of energy deposit is different. It results in the differences of radical intensity and the thermal property of polyether-urethane as well as its gas products from the radiation decomposition. (authors)

Preparation and magnetic properties of polymer magnetic composites based on acrylate resin filled with nickel plating graphite nanosheets

Energy Technology Data Exchange (ETDEWEB)

Zhang Yi, E-mail: zhangyi520love@yahoo.com.cn [Department of Applied Chemistry, School of Science, Northwestern Polytechnical University, Xi' an 710072 (China); Qi Shuhua; Zhang Fan; Yang Yongqing; Duan Guochen [Department of Applied Chemistry, School of Science, Northwestern Polytechnical University, Xi' an 710072 (China)

2011-11-01

Nickel plating graphite nanosheets (Ni/GNs) were prepared by electroless plating method using graphite nanosheets (GNs). Then a novel polymer magnetic composites based on acrylate pressure-sensitive adhesive (acrylate PSA) filled with Ni/GNs were fabricated by solution blend method. The Ni/GNs and acrylate PSA/Ni/GNs composites were characterized by scanning electron microscope (SEM)/energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), vibrating sample magnetometer (VSM) and transmission electron microscope (TEM). All results showed that relatively uniform and compact Ni layer is successfully coated onto GNs under the given conditions, furthermore, Ni/GNs are homogeneously dispersed in acrylate PSA. The VSM results showed that the saturation magnetization of acrylate PSA/Ni/GNs composites increases with an increasing content of Ni/GNs while the coercivity decreases with an increasing content of Ni/GNs. When the content of GNs is 20 wt%, acrylate PSA/Ni/GNs composites exhibites good mechanical properties.

Preparation and magnetic properties of polymer magnetic composites based on acrylate resin filled with nickel plating graphite nanosheets

International Nuclear Information System (INIS)

Zhang Yi; Qi Shuhua; Zhang Fan; Yang Yongqing; Duan Guochen

2011-01-01

Nickel plating graphite nanosheets (Ni/GNs) were prepared by electroless plating method using graphite nanosheets (GNs). Then a novel polymer magnetic composites based on acrylate pressure-sensitive adhesive (acrylate PSA) filled with Ni/GNs were fabricated by solution blend method. The Ni/GNs and acrylate PSA/Ni/GNs composites were characterized by scanning electron microscope (SEM)/energy dispersive spectroscopy (EDS), X-ray diffraction (XRD), vibrating sample magnetometer (VSM) and transmission electron microscope (TEM). All results showed that relatively uniform and compact Ni layer is successfully coated onto GNs under the given conditions, furthermore, Ni/GNs are homogeneously dispersed in acrylate PSA. The VSM results showed that the saturation magnetization of acrylate PSA/Ni/GNs composites increases with an increasing content of Ni/GNs while the coercivity decreases with an increasing content of Ni/GNs. When the content of GNs is 20 wt%, acrylate PSA/Ni/GNs composites exhibites good mechanical properties.

An experimental study of dynamic behaviour of graphite-polycarbonatediol polyurethane composites for protective coatings

Science.gov (United States)

Gómez, C. M.; Culebras, M.; Cantarero, A.; Redondo-Foj, B.; Ortiz-Serna, P.; Carsí, M.; Sanchis, M. J.

2013-06-01

Segmented polycarbonatediol polyurethane (PUPH) has been synthesized and modified with different amounts of graphite conductive filler (from 0 to 50 wt%). Thermal and dynamical thermal analysis of the composites clearly indicates changes in the polyurethane relaxations upon addition of graphite. Broadband dielectric spectroscopy has been used to study the dielectric properties of the (PUPH) and one composite in the frequency range from 10-2 to 107 Hz and in the temperature window of -140 to 170 °C. Relaxation processes associated with different molecular motions and conductivity phenomena (Maxwell-Wagner-Sillars and electrode polarization) are discussed and related to the graphite content.

Pengerasan Pada Bahan Cetak Elastomer Polyether

OpenAIRE

Azree Zayani M.S.

2011-01-01

Bahan cetak polyether merupakan bahan elastomer yang digunakan di kedokteran gigi. Terdapat empat kelas menurut konsistensi dan viskositas yaitu (1) light body (2)medium atau regular body (3) heavy body: dan (4) Putty. Komposisi bahan cetak polyether terdiri dari pasta base dan pasta katalis. Pasta base mengandung polimer polyether, kolloidal silika sebagai bahan pengisi, dan plastisizer yaitu glikoeter atau phthalate. Pasta katalis mengandung alkil aromatik sulfonat ditambah dengan baha...

Direct transformation of silyl enol ethers into functionalized allenes.

Science.gov (United States)

Langer, P; Döring, M; Seyferth, D; Görls, H

2001-02-02

The first elimination reactions of silyl enol ethers to lithiated allenes are reported. These reactions allow a direct transformation of readily available silyl enol ethers into functionalized allenes. The action of three to four equivalents of lithium diisopropylamide (LDA) on silyl enol ethers results in the formation of lithiated allenes by initial allylic lithiation, subsequent elimination of a lithium silanolate, and finally, lithiation of the allene thus formed. Starting with amide-derived silyl imino ethers, lithiated ketenimines are obtained. A variety of reactions of the lithiated allenes with electrophiles (chlorosilanes, trimethylchlorostannane, dimethyl sulfate and ethanol) were carried out. Elimination of silanolate is observed only for substrates that contain the hindered SiMe2tBu or Si(iPr)3 moiety, but not for the SiMe3 group. The reaction of 1,1-dilithio-3,3-diphenylallene with ketones provides a convenient access to novel 1,1-di(hydroxymethyl)allenes which undergo a domino Nazarov-Friedel-Crafts reaction upon treatment with p-toluenesulfonic acid.

Influence of Moisture Absorption and Content of Graphite Filler on Electrical Property of Sensors and Transducers Enclosures and Phenomena of Electrostriction in Glass- Epoxy Composites

Directory of Open Access Journals (Sweden)

B. Shivamurthy

2008-10-01

Full Text Available In this investigation E-glass epoxy composite filled with different amount of graphite particles were prepared by compression. Plain waived E-glass cloth with density 200g / meter square was used as reinforcement. Epoxy resin LY556 mixed with Hardener HT907 and accelerator DY063 in the ratio 100:80:2 were used as matrix. The graphite of 50 particle size was used as fillers. Four types of composites were prepared with different amount of graphite fillers viz 0 %, 3 %, 6 % and 9 % with unchanged reinforcement. After subjecting the samples to water absorption up to 96 hours in steps of 24 hrs, dielectric dissipation factor (tan δ, dielectric constant and a. c. conductivity have been measured by using a LCR meter at two different frequencies (100 Hz and 1 kHz. Results show that tan δ direct constant, a.c. conductivity increases with increase in % of graphite in the composites at both high and low frequency for dry samples. Samples with 24 hrs moisture absorption showed approximately same result. After 48 hrs, tan δ values showed variations. However, the fluctuations were less at 6 % of graphite in all samples after 48 and 72 hrs of moisture absorption. Dielectric constant increases with increase in graphite % in composites at higher frequency and there was not much variation at low frequency. In all samples after 24 and 48 hrs of moisture absorption, dielectric constant decreases with increase in graphite loading. It is observed that dielectric constant increases in all samples after 72 hrs of moisture absorption as compared to dry samples. A c. conductivity increases with increase in % of graphite content in dry sample. Up to 6% a. c. conductivity increases after 24 and 48 hrs of immersion, after 72 hrs the trend is reversed. Since Fermi level is initially shifted towards the conduction band and then after 72 hrs of moisture absorption shifted towards the valence band. a. c. conductivity increases with increase in moisture content. The

The effect of polyether on the separation of pentlandite and serpentine

Directory of Open Access Journals (Sweden)

Xiaowen Zhou

2015-10-01

Full Text Available The effect of polyether on the separation of pentlandite from serpentine has been studied. In addition to flotation and sedimentation tests, electrophoresis and adsorption tests have been conducted. The flotation and sedimentation results show that serpentine impairs flotation performance of pentlandite, by adhering to the pentlandite particles. Addition of the polyether could promote the dispersion of the mixed sample of pentlandite and serpentine in alkaline conditions and significantly reduce adverse effects of serpentine on the pentlandite flotation. The electrophoresis and adsorption tests show that polyether can selectively adsorb onto pentlandite surface through hydrophobic reaction and remove serpentine slime particles from pentlandite surfaces by steric hindrance effect.

Quantifying microstructural dynamics and electrochemical activity of graphite and silicon-graphite lithium ion battery anodes

Science.gov (United States)

Pietsch, Patrick; Westhoff, Daniel; Feinauer, Julian; Eller, Jens; Marone, Federica; Stampanoni, Marco; Schmidt, Volker; Wood, Vanessa

2016-09-01

Despite numerous studies presenting advances in tomographic imaging and analysis of lithium ion batteries, graphite-based anodes have received little attention. Weak X-ray attenuation of graphite and, as a result, poor contrast between graphite and the other carbon-based components in an electrode pore space renders data analysis challenging. Here we demonstrate operando tomography of weakly attenuating electrodes during electrochemical (de)lithiation. We use propagation-based phase contrast tomography to facilitate the differentiation between weakly attenuating materials and apply digital volume correlation to capture the dynamics of the electrodes during operation. After validating that we can quantify the local electrochemical activity and microstructural changes throughout graphite electrodes, we apply our technique to graphite-silicon composite electrodes. We show that microstructural changes that occur during (de)lithiation of a pure graphite electrode are of the same order of magnitude as spatial inhomogeneities within it, while strain in composite electrodes is locally pronounced and introduces significant microstructural changes.

21 CFR 177.2430 - Polyether resins, chlorinated.

Science.gov (United States)

2010-04-01

... 21 Food and Drugs 3 2010-04-01 2009-04-01 true Polyether resins, chlorinated. 177.2430 Section 177... Components of Articles Intended for Repeated Use § 177.2430 Polyether resins, chlorinated. Chlorinated polyether resins may be safely used as articles or components of articles intended for repeated use in...

Facile synthesis and enhanced visible-light photocatalysis of graphitic carbon nitride composite semiconductors.

Science.gov (United States)

Li, Huiquan; Liu, Yuxing; Gao, Xing; Fu, Cong; Wang, Xinchen

2015-04-13

The semiconductor heterojunction has been an effective architecture to enhance photocatalytic activity by promoting photogenerated charge separation. Here, graphitic carbon nitride (CN) and B-modified graphitic carbon nitride (CNB) composite semiconductors were fabricated by a facile calcination process using cheap, sustainable, and easily available sodium tetraphenylboron and urea as precursors. The synthetic CN-CNB-25 semiconductor with a suitable CNB content showed the highest visible-light activity. Its degradation ratio for methyl orange and phenol was more than twice that of CN and CNB and its H2 evolution rate was ∼3.4 and ∼1.8 times higher than that of CN and CNB, respectively. It also displayed excellent stability and reusability. The enhanced activity of CN-CNB-25 was attributed predominantly to the efficient separation of photoinduced electrons and holes. This paper describes a visible-light-responsive CN composite semiconductor with great potential in environmental and energy applications. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Anodic stripping voltammetry using graphite composite solid electrode

Czech Academy of Sciences Publication Activity Database

Navrátil, Tomáš; Barek, J.; Kopanica, Miloslav

2009-01-01

Roč. 74, 11-12 (2009), s. 1807-1826 ISSN 0010-0765 R&D Projects: GA AV ČR IAA400400806; GA ČR GA203/07/1195; GA MŠk(CZ) LC06035 Institutional research plan: CEZ:AV0Z40400503 Keywords : Graphite composite solid electrode * voltammetry * metals Subject RIV: CG - Electrochemistry Impact factor: 0.856, year: 2009

Shape Memory Composites Based on Electrospun Poly(vinyl alcohol) Fibers and a Thermoplastic Polyether Block Amide Elastomer.

Science.gov (United States)

Shirole, Anuja; Sapkota, Janak; Foster, E Johan; Weder, Christoph

2016-03-01

The present study aimed at developing new thermally responsive shape-memory composites, that were fabricated by compacting mats of electrospun poly(vinyl alcohol) (PVA) fibers and sheets of a thermoplastic polyether block amide elastomer (PEBA). This design was based on the expectation that the combination of the rubber elasticity of the PEBA matrix and the mechanical switching exploitable through the reversible glass transition temperature (Tg) of the PVA filler could be combined to create materials that display shape memory characteristics as an emergent effect. Dynamic mechanical analyses (DMA) show that, upon introduction of 10-20% w/w PVA fibers, the room-temperature storage modulus (E') increased by a factor of 4-5 in comparison to the neat PEBA, and they reveal a stepwise reduction of E' around the Tg of PVA (85 °C). This transition could indeed be utilized to fix a temporary shape and recover the permanent shape. At low strain, the fixity was 66 ± 14% and the recovery was 98 ± 2%. Overall, the data validate a simple and practical strategy for the fabrication of shape memory composites that involves a melt compaction process and employs two commercially available polymers.

Nanostructured MnO2/exfoliated graphite composite electrode as supercapacitors

International Nuclear Information System (INIS)

Yang Yanjing; Liu Enhui; Li Limin; Huang Zhengzheng; Shen Haijie; Xiang Xiaoxia

2009-01-01

Nanostructured manganese oxides/exfoliated graphite composite (MnO 2 /EG) were synthesized via a new sol-gel route. Scanning electron microscope (SEM) was employed for surface morphology and X-ray diffraction (XRD) was used for structure characterization. Cyclic voltammetry (CV), galvanostatic charge/discharge, and the electrochemical impedance measurements were applied to investigate the electrochemical performance of the MnO 2 /EG composite electrodes. When used for electrodes of supercapacitors, the as-prepared MnO 2 /EG and the pure MnO 2 exhibited excellent capacitance characteristics in 6 mol L -1 KOH electrolyte and showed high specific capacitance values of 398 F g -1 and 326 F g -1 ,respectively, at a scan rate of 10 mV s -1 . The galvanostatic charge-discharge measurements showed approximately 0.5% loss of capacitance after 500 cycles, and charge-discharge efficiency above 99%. In addition, the synthesized nanomaterial showed a good reversibility and cycling stability.

Study on epoxy resin modified by polyether ionic liquid

Science.gov (United States)

Jin, X. C.; Guo, L. Y.; Deng, L. L.; Wu, H.

2017-06-01

Chloride 1-carboxyl polyether-3-methyl imidazole ionic liquid (PIIL) was synthesized. Then blended with epoxy resin(EP) to prepare the composite materials of PIIL/EP, which cured with aniline curing agent. The structure and curing performance of PIIL/EP were determined by FT-IR and DSC. The effects of the content of PIIL on strength of EP were studied. The results show that the PIIL was the target product. The strength was improved significantly with increase of the PIIL content. The obvious rubber elasticity of PIIL/EP after cured was showed when the content of PIIL accounts for 40% and the impact strength was up to 15.95kJ/m2.

THERMAL INSULATION PROPERTIES RESEARCH OF THE COMPOSITE MATERIAL WATER GLASS–GRAPHITE MICROPARTICLES

Directory of Open Access Journals (Sweden)

V. A. Gostev

2014-05-01

Full Text Available Research results for the composite material (CM water glass–graphite microparticles with high thermal stability and thermal insulation properties are given. A composition consisting of graphite (42 % by weight, water glass Na2O(SiO2n (50% by weight and the hardener - sodium silicofluoric Na2SiF6 (8% by weight. Technology of such composition receipt is suggested. Experimental samples of the CM with filler particles (graphite and a few microns in size were obtained. This is confirmed by a study of samples by X-ray diffraction and electron microscopy. The qualitative and quantitative phase analysis of the CM structure is done. Load limit values leading to the destruction of CM are identified. The character of the rupture surface is detected. Numerical values of specific heat and thermal conductivity are defined. Dependence of the specific heat capacity and thermal conductivity on temperature at monotonic heating is obtained experimentally. Studies have confirmed the increased thermal insulation properties of the proposed composition. CM with such characteristics can be recommended as a coating designed to reduce heat losses and resistant to high temperatures. Due to accessibility and low cost of its components the proposed material can be produced on an industrial scale.

[A survey of occupational health among polyether-exposed workers].

Science.gov (United States)

Fu, Xu-ying; Yu, Bin; Zhang, Chun-ping; Zheng, Guan-hua; Bai, Lan; Zhang, Pan-pan

2013-06-01

To investigate the occupational health of the workers simultaneously exposed to acrylonitrile, epoxyethane, epoxypropane, and styrene. A questionnaire survey was conducted in 70 front-line workers simultaneously exposed to acrylonitrile, epoxyethane, epoxypropane, and styrene (exposure group) and 50 managers (control group) in a polyether manufacturer; in addition, air monitoring at workplace and occupational health examination were also performed. The obtained data were analyzed. The female workers in exposure group and the spouses of male workers in exposure group had significantly higher spontaneous abortion rates than their counterparts in control group (P polyether-exposed working years had significantly higher mean levels of DNA damage than the control group (P polyether-exposed working years and those with not less than 20 polyether-exposed working years had significantly higher mean micronucleus rates than the control group (P polyether-exposed working years (P > 0.05); the workers with not less than 5 and less than 20 polyether-exposed working years and workers with not less than 20 polyether-exposed working years had significantly higher mean micronucleus rates than those with less than 5 polyether-exposed working years (P polyether manufacturer.

Biosynthetic conversion of thebaine to codeinone. Mechanism of ketone formation from enol ether in vivo

International Nuclear Information System (INIS)

Horn, J.S.; Paul, A.G.; Rapoport, H.

1978-01-01

Biosynthesis of the morphinan alkaloids proceeds by conversion of the enol ether or thebaine to the keto group of neopinone and thence to codeinone. To determine the mechanism of this transformation, [G- 14 C,6- 18 O]thebaine was fed to Papaver somniferum and the codeine and morphine were isolated. Comparison of the 18 O/ 14 C ratios in the codeine and morphine isolated with that of the thebaine fed showed that approximately 34% of the 18 O had been retained. Parallel feedings with [G- 14 C,6- 18 O]-codeinone demonstrated that the loss was due to nonenzymic exchange. Thus, the mechanism of enol ether cleavage in thebaine is established as cleavage of the 6-O-methyl group with retention of the 6-oxygen in the codeinone

Processing of high performance composites based on peek by aqueous suspension prepregging

Directory of Open Access Journals (Sweden)

Liliana Burakowski Nohara

2010-06-01

Full Text Available The use of polyamic acid (PAA precursor as interphase in polymer composites is one of the many applications of polyimides (PIs. In this work, composites based on poly(ether-ether-ketone (PEEK and carbon fibers were prepared using two manufacturing techniques for thermoplastic composites: hot compression molding, and aqueous polymeric suspension prepregging using PIs as interphase. Two PAAs were synthesized and used as interphases: 3,3'-4,4'-benzophenonetetracarboxylic dianhydride/oxydianiline (BTDA/ODA and pyromellitic dianhydride/oxydianiline (PMDA/ODA. The PAA/PI systems were analyzed by differential scanning calorimetry (DSC, thermogravimetry (TGA, Fourier transform infrared spectroscopy (FTIR and nuclear magnetic resonance (NMR. Results from these analyses confirmed the synthesis of these compounds. Aqueous polymeric suspension prepregging was more efficient than hot compression molding when the PMDA/ODA PAA/PI interphase was used; also, the interlaminar shear strength of composites produced using this technique was 14.5% higher than the one produced using hot compression molding.

Organic-Inorganic Graphite and Transition Metal Dichalcogenide Based Composites for 3D Printing

Science.gov (United States)

Catalan Gonzalez, Jorge Alfredo

This project was multipronged to help fuse together topics of additive manufacturing and two-dimensional (2D) layered materials, and studying the mechanical and electrical properties of the composites produced. The composites are made from the thermoplastic polymer acting as a matrix and the graphite and 2D transition metal dichalcogenides (TMDs) serving as the filler or reinforcement. Different concentrations of TMD's were added to the matrix to study the effect of composition on the mechanical and electrical properties. To shed insights into the mechanical properties, test coupons were produced as "dog bone" structures for tensile testing using the ASTM D638 type 5 standard, which were printed with the aid of a Lulzbot TAZ 6 3D printer. In the same way, two-terminal resistor-like structures were printed to test the electrical properties inherent to the composites. From the measurements conducted, polyethylene terephthalate glycol (PETG)--graphite composites had a yield strength (YS) ≈ 50 MPa, an ultimate tensile strength (UTS) ≈ 30 MPa and had a better ductility (strain to rupture ≈ 8%) compared to theacrylonitrile butadiene styrene (ABS) composite counterparts. Also, molybdenum disulfide (MoS2) had a more positive effect than tungsten disulfide (WS2), since the strength was retained while the ductility was increased at low loadings of the material. Strain levels were measured to be 30%-120% when adding 1 wt% of MoS2 and WS2. On the other hand, with high additions of MoS2 and WS2 (15 and 20 wt%) ductility was completely lost since no plastic deformation occurred during the testing. Moreover, PETG - graphite resistor-like structures were 3-dimensional (3D) printed and tested with the help of a semiconductor parameter analyzer. All samples were tested at different radius of curvatures (0 cm-1, 0.072 cm-1, 0.087 cm-1, 0.112 cm-1, 0.157 cm-1, and 0.262 cm -1) which showed a composite that was strain insensitive. The obtained average conductivity and resistivity

ZnO/graphite composites and its antibacterial activity at different conditions.

Science.gov (United States)

Dědková, Kateřina; Janíková, Barbora; Matějová, Kateřina; Čabanová, Kristina; Váňa, Rostislav; Kalup, Aleš; Hundáková, Marianna; Kukutschová, Jana

2015-10-01

The paper reports laboratory preparation, characterization and in vitro evaluation of antibacterial activity of ZnO/graphite nanocomposites. Zinc chloride and sodium carbonate served as precursors for synthesis of zinc oxide, while micromilled and natural graphite were used as the matrix for ZnO nanoparticles anchoring. During the reaction of ZnCl2 with saturated aqueous solution of Na2CO3a new compound is created. During the calcination at the temperature of 500 °C this new precursors decomposes and ZnO nanoparticles are formed. Composites ZnO/graphite with 50 wt.% of ZnO particles were prepared. X-ray powder diffraction and Raman microspectroscopy served as phase-analytical methods. Scanning electron microscopy technique was used for morphology characterization of the prepared samples and EDS mapping for visualization of elemental distribution. A developed modification of the standard microdilution test was used for in vitro evaluation of daylight induced antibacterial activity and antibacterial activity at dark conditions. Common human pathogens served as microorganism for antibacterial assay. Antibacterial activity of ZnO/graphite composites could be based on photocatalytic reaction; however there is a role of Zn(2+) ions on the resulting antibacterial activity which proved the experiments in dark condition. There is synergistic effect between Zn(2+) caused and reactive oxygen species caused antibacterial activity. Copyright © 2015 Elsevier B.V. All rights reserved.

Thermal deoxygenation of graphite oxide at low temperature

International Nuclear Information System (INIS)

Kampars, V; Legzdina, M

2015-01-01

Synthesis of graphene via the deoxygenation of the graphite oxide (GO) is a method for the large-scale production of this nanomaterial possessing exceptional mechanical, electrical and translucent properties. Graphite oxide sheet contains at least four different oxygen atoms connected to the Csp 3 and Csp 2 atoms of the sheet in the form of hydroxyl, epoxy, carboxyl or carbonyl groups. Some of these functional groups are located at the surface but others situated at the edges of the platelets. To obtain the graphene nanoplatelets or the few-layer graphene the oxygen functionalities must be removed. Exfoliation and deoxygenation can be accomplished by the use of chemical reductants or heat. Thermal deoxygenation as greener and simpler approach is more preferable over chemical reduction approach. Usually a considerable mass loss of GO observed upon heating at temperatures starting at 200 °C and is attributed to the deoxygenation process. In order to avoid the defects of the obtained graphene sheets it is very important to find the methods for lowering the deoxygenation temperature of GO. Herein, we have investigated the way treatment of the Hummer's synthesis product with acetone and methyl tert-butyl ether under ultrasonication in order to lower the thermal stability of the graphite oxide and its deoxygenation temperature. The obtained results indicate that treatment of the graphite oxide with solvents mentioned above substantially reduces the reduction and exfoliation temperature (130 °C) under ambient atmosphere. The investigation of the composition of evolved gases by hyphenated Pyr/GC/MS method at different experimental conditions under helium atmosphere shows that without the expected H 2 O, CO and CO 2 also sulphur dioxide and acetone has been released

Preparation and characterization of graphite-dispersed styrene-acrylic emulsion composite coating on magnesium alloy

Energy Technology Data Exchange (ETDEWEB)

Zhang Renhui [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Science, Lanzhou 730000 (China); Lanzhou University of Technology, College of Science, Lanzhou 730050 (China); Liang Jun, E-mail: jliang@licp.cas.cn [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Science, Lanzhou 730000 (China); Wang Qing [Lanzhou University of Technology, College of Science, Lanzhou 730050 (China)

2012-03-01

In this work, an electrically conductive, corrosion resistant graphite-dispersed styrene-acrylic emulsion composite coating on AZ91D magnesium alloy was successfully produced by the method of anodic deposition. The microstructure, composition and conductivity of the composite coating were characterized using optical microscope (OM), scanning electron microscope (SEM), X-ray diffraction (XRD), Fourier transform infrared spectrometer (FTIR) and four electrode volume resistivity instrument, respectively. The corrosion resistance of the coating was evaluated using potentiodynamic polarization measurements and salt spray tests. It is found that the graphite-dispersed styrene-acrylic emulsion composite coating was layered structure and displayed good electrical conductivity. The potentiodynamic polarization tests and salt spray tests reveal that the composite coating was successful in providing superior corrosion resistance to AZ91D magnesium alloy.

Genetic screening strategy for rapid access to polyether ionophore producers and products in actinomycetes.

Science.gov (United States)

Wang, Hao; Liu, Ning; Xi, Lijun; Rong, Xiaoying; Ruan, Jisheng; Huang, Ying

2011-05-01

Polyether ionophores are a unique class of polyketides with broad-spectrum activity and outstanding potency for the control of drug-resistant bacteria and parasites, and they are produced exclusively by actinomycetes. A special epoxidase gene encoding a critical tailoring enzyme involved in the biosynthesis of these compounds has been found in all five of the complete gene clusters of polyether ionophores published so far. To detect potential producer strains of these antibiotics, a pair of degenerate primers was designed according to the conserved regions of the five known polyether epoxidases. A total of 44 putative polyether epoxidase gene-positive strains were obtained by the PCR-based screening of 1,068 actinomycetes isolated from eight different habitats and 236 reference strains encompassing eight major families of Actinomycetales. The isolates spanned a wide taxonomic diversity based on 16S rRNA gene analysis, and actinomycetes isolated from acidic soils seemed to be a promising source of polyether ionophores. Four genera were detected to contain putative polyether epoxidases, including Micromonospora, which has not previously been reported to produce polyether ionophores. The designed primers also detected putative epoxidase genes from diverse known producer strains that produce polyether ionophores unrelated to the five published gene clusters. Moreover, phylogenetic and chemical analyses showed a strong correlation between the sequence of polyether epoxidases and the structure of encoded polyethers. Thirteen positive isolates were proven to be polyether ionophore producers as expected, and two new analogues were found. These results demonstrate the feasibility of using this epoxidase gene screening strategy to aid the rapid identification of known products and the discovery of unknown polyethers in actinomycetes.

Structural insights from boron tribromide ether cleavage into lignites and low maturity coals from the New Zealand Coal Band

DEFF Research Database (Denmark)

Glombitza, Clemens; Mangelsdorf, Kai; Horsfield, Brian

2011-01-01

structure, boron tribromide (BBr3) ether cleavage was applied to a series of lignite and coal samples of different maturity (R0 0.27–0.80%) obtained from coal mines and natural outcrops from the North and South Island of New Zealand. Terminal ether-bound alcohols rapidly decrease during diagenesis and occur...... over geological time scales. Polyether compounds were detected with chain length up to five carbon atoms. After a small decrease during the diagenetic phase these compounds occur in relatively high concentrations, even in the main catagenetic stage. This suggests that these linkage structures represent...

The Setup Design for Selective Laser Sintering of High-Temperature Polymer Materials with the Alignment Control System of Layer Deposition

Directory of Open Access Journals (Sweden)

Alexey Nazarov

2018-03-01

Full Text Available This paper presents the design of an additive setup for the selective laser sintering (SLS of high-temperature polymeric materials, which is distinguished by an original control system for aligning the device for depositing layers of polyether ether ketone (PEEK powder. The kinematic and laser-optical schemes are given. The main cooling circuits are described. The proposed technical and design solutions enable conducting the SLS process in different types of high-temperature polymer powders. The principles of the device adjustment for depositing powder layers based on an integral thermal analysis are disclosed. The PEEK sinterability was shown on the designed installation. The physic-mechanical properties of the tested 3D parts were evaluated in comparison with the known data and showed an acceptable quality.

Metal ion separations with proton-ionizable Lariat Ethers and their polymers

International Nuclear Information System (INIS)

Bartsch, R.A.

1993-01-01

The preparation of novel and specific organic complexing agents may lead to the development of new separation systems for aqueous metal ions. Thus the introduction of highly lipophilic oximes led to the current utilization of these compounds as commercial extractants for the hydrometallurgy of nonferrous metals. Crown ethers (macrocyclic polyethers) have been employed in the laboratory-scale solvent extraction of alkali-metal, alkaline-earth, and other metal cations into organic phases. Attachment of side arms to crown ethers gives lariat ethers. The presence of one or more potential coordination sites in the side arm of the lariat ether may produce substantial changes in the selectivity and efficiency of metal ion complexation. It has been demonstrated that concomitant transfer of an aqueous phase anion into the organic medium is not required for metal ion extraction. This factor is of immense importance to potential practical applications of these proton-ionizable crown ethers in which the common, hard, aqueous phase anions would be involved. Another advantage of proton-ionizable lariat ethers is the ease with which extracted metal ions may be stripped from the organic phase by shaking with aqueous mineral acid. Thus both metal ion extraction and stripping are facilitated by pendent proton-ionizable groups. Most of the hazardous metal ion species in the Hanford Site tank wastes are members of the alkali-metal, alkaline-earth, lanthanide, and actinide families. These hard metal ion species prefer association with hard donor atoms, such as oxygens. Therefore, crown and lariat ethers are well-suited for complexation with such metal ion species

Electrochemical lithiation performance and characterization of silicon-graphite composites with lithium, sodium, potassium, and ammonium polyacrylate binders.

Science.gov (United States)

Han, Zhen-Ji; Yamagiwa, Kiyofumi; Yabuuchi, Naoaki; Son, Jin-Young; Cui, Yi-Tao; Oji, Hiroshi; Kogure, Akinori; Harada, Takahiro; Ishikawa, Sumihisa; Aoki, Yasuhito; Komaba, Shinichi

2015-02-07

Poly(acrylic acid) (PAH), which is a water soluble polycarboxylic acid, is neutralized by adding different amounts of LiOH, NaOH, KOH, and ammonia (NH4OH) aqueous solutions to fix neutralization degrees. The differently neutralized polyacid, alkali and ammonium polyacrylates are examined as polymeric binders for the preparation of Si-graphite composite electrodes as negative electrodes for Li-ion batteries. The electrode performance of the Si-graphite composite depends on the alkali chemicals and neutralization degree. It is found that 80% NaOH-neutralized polyacrylate binder (a pH value of the resultant aqueous solution is ca. 6.7) is the most efficient binder to enhance the electrochemical lithiation and de-lithiation performance of the Si-graphite composite electrode compared to that of conventional PVdF and the other binders used in this study. The optimum polyacrylate binder highly improves the dispersion of active material in the composite electrode. The binder also provides the strong adhesion, suitable porosity, and hardness for the composite electrode with 10% (m/m) binder content, resulting in better electrochemical reversibility. From these results, the factors of alkali-neutralized polyacrylate binders affecting the electrode performance of Si-graphite composite electrodes are discussed.

Bacterial production of methyl ketones

Energy Technology Data Exchange (ETDEWEB)

Beller, Harry R.; Goh, Ee-Been

2017-01-31

The present invention relates to methods and compositions for increasing production of methyl ketones in a genetically modified host cell that overproduces .beta.-ketoacyl-CoAs through a re-engineered .beta.-oxidation pathway and overexpresses FadM.

Electrochemically Active Polymeric Hollow Fibers based on Poly(ether- b -amide)/Carbon Nanotubes

KAUST Repository

Cuevas, Carolina

2017-09-18

A simple and effective method to incorporate catalytic activity to a hollow fiber membrane is reported. Polyetherimide hollow fiber membranes were coated with a solution containing carboxyl-functionalized multi-walled carbon nanotubes and poly(ether-b-amide). Electron microscopy images confirmed the presence of a layer of percolating carbon nanotubes on the surface of the membranes. Cyclic voltammetry and linear swept voltammetry experiments showed that these membranes are able to drive the reactions of hydrogen evolution, and oxygen reduction, making them a cheaper, and greener substitute for platinum based cathodes in microbial bioelectrochemical systems. Water flux and molecular weight cut off experiments indicated that the electrochemically active coating layer does not affect the ultrafiltration performance of the membrane.

Electrochemically Active Polymeric Hollow Fibers based on Poly(ether- b -amide)/Carbon Nanotubes

KAUST Repository

Cuevas, Carolina; Kim, Dooli; Katuri, Krishna; Saikaly, Pascal; Nunes, Suzana Pereira

2017-01-01

A simple and effective method to incorporate catalytic activity to a hollow fiber membrane is reported. Polyetherimide hollow fiber membranes were coated with a solution containing carboxyl-functionalized multi-walled carbon nanotubes and poly(ether-b-amide). Electron microscopy images confirmed the presence of a layer of percolating carbon nanotubes on the surface of the membranes. Cyclic voltammetry and linear swept voltammetry experiments showed that these membranes are able to drive the reactions of hydrogen evolution, and oxygen reduction, making them a cheaper, and greener substitute for platinum based cathodes in microbial bioelectrochemical systems. Water flux and molecular weight cut off experiments indicated that the electrochemically active coating layer does not affect the ultrafiltration performance of the membrane.

Ketones urine test

Science.gov (United States)

Ketone bodies - urine; Urine ketones; Ketoacidosis - urine ketones test; Diabetic ketoacidosis - urine ketones test ... Urine ketones are usually measured as a "spot test." This is available in a test kit that ...

Study of wear mechanism of chopped fiber reinforced epoxy composite filled with graphite and bronze

Science.gov (United States)

Patil, Nitinchand; Prasad, Krishna

2018-04-01

The combined effect of graphite and sintered bronze with a short glass fiber reinforced epoxy composites was investigated in this work. A pin on disc wear test was carried out to study the wear behaviour and mechanism of the composites. The objective of this work is to develop an alternate friction resistance material for the application of sliding bearing. It was observed that the addition of sintered bronze improved mechanical and thermal stability of the composites as bronze has low contact resistance with graphite and has high thermal conductivity. It was observed from the test results that increased volume percentage of graphite and presence of bronze are play significant role in wear mechanism of the composites. It was observed from the scanning electronic microscopes (SEM) that the abrasive and adhesive wear mechanism was prominent in this study. It was also evident from the result that the frictional force remains stable irrespective of the applied normal load.

Radiation curable coatings containing hydroxy functional polyethers and polyesters of monoethylenic acids or hydroxy esters thereof

International Nuclear Information System (INIS)

Kaufman, M.L.

1978-01-01

Relatively water insoluble hydroxy functional monoethylenic polyethers or polyesters of monoethylenic carboxylic acids or hydroxy alkyl esters thereof are formed by adducting the monoethylenic acid or its hydroxy ester with an anhydride selected from monoepoxides, lactones, or mixtures thereof in the presence of a Lewis acid catalyst, such as BF 3 etherate, at a temperature below that at which the unsaturation is consumed, typically about 30 to 70 0 C. These adducts are of low volatility and of low toxicity and can be radiation cured in admixture with polyacrylates to form coatings having improved resistance to elevated temperature exposure

Use of graphite epoxy composites in the Solar-A Soft X-Ray Telescope

Science.gov (United States)

Jurcevich, B. K.; Bruner, M. E.

1990-01-01

This paper describes the use of composite materials in the Soft X-Ray Telescope (SXT). One of the primary structural members of the telescope is a graphite epoxy metering tube. The metering tube maintains the structural stability of the telescope during launch as well as the focal length through various environmental conditions. The graphite epoxy metering tube is designed to have a negative coefficient of thermal expansion to compensate for the positive expansion of titanium structural supports. The focus is maintained to + or - 0.001 inch by matching the CTE of the composite tube to the remaining structural elements.

Unusual selectivity-determining factors in the phosphine-free Heck arylation of allyl ethers

DEFF Research Database (Denmark)

Ambrogio, I.; Fabrizi, G.; Cacchi, S.

2008-01-01

The Heck reaction of aryl iodides and bromides with allyl ethers has been investigated. Using phosphinefree Pd(OAc)(2) in DNIF at 90 degrees C in the presence of Bu4NOAc, the reaction gave cinnamyl derivatives, usually in good to high yields, with a wide range of aryl halides. The reaction...... tolerates a variety of functional groups, including ether, amide, alcohol, aldehyde, ketone, ester, cyano, carboxylic acid, and nitro groups. Ortho-substituted arylating agents afforded moderate yields in some cases, though good to high yields were obtained with o-iodotoluene, iodovanillin, and 1...

Thermal stability and electrical conductivity in polyethers-molybdenum disulfide nanocomposites

International Nuclear Information System (INIS)

Mirabal, N.; Aguirre, P.; Santa Ana, M.A.; Benavente, E.; Gonzalez, Guillermo

2003-01-01

The intercalation of poly(ethylene oxide) (PEO), into molybdenum disulfide, like that of other electron pair donors, leads to mixed ionic-electronic conductors. At room temperature, intercalates show electrical and lithium-ion conductivities better than MoS 2 and bulk PEO composites, respectively. However, these products are known to be sensitive to temperature; indeed, in the range 80-100 deg. C an irreversible decrease of the electrical conductivity is observed. In order to investigate these features, the thermal behavior of a series of polyethers of different molecular weights (poly(ethylene glycol) (Mw 3400) and PEO with Mw in the range 10 4 -4x10 6 , pure and intercalated in MoS 2 , (Li x (MoS 2 )(polyether) y with x∼0.1 and y=1.1-1.5), was comparatively analyzed. Furthermore, the effect of thermal treatment of the sample on the electrical conductivity was studied for one of the intercalated products. Results indicate that irreversible changes, detected by both loss of weight and a significant conductivity lowering, are occurring in the range from about 100 deg. C to a temperature near to the decomposition point of the organic phase at about 350 deg. C

Improved interfacial adhesion in carbon fiber/polyether sulfone composites through an organic solvent-free polyamic acid sizing

Energy Technology Data Exchange (ETDEWEB)

Yuan, Haojie [National Engineering Laboratory for carbon fiber technology, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Zhang, Shouchun, E-mail: zschun@sxicc.ac.cn [National Engineering Laboratory for carbon fiber technology, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001 (China); Lu, Chunxiang, E-mail: chunxl@sxicc.ac.cn [National Engineering Laboratory for carbon fiber technology, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001 (China); He, Shuqing [National Engineering Laboratory for carbon fiber technology, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); An, Feng [National Engineering Laboratory for carbon fiber technology, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001 (China)

2013-08-15

An organic solvent-free polyamic acid (PAA) nanoemulsion was obtained by direct ionization of the solid PAA in deionized water, with the average particle size of 261 nm and Zeta potential of −55.1 mV, and used as a carbon fiber sizing to improve the interfacial adhesion between the carbon fiber and polyether sulfone (PES). The surface characteristics of PAA coated carbon fibers were investigated using Fourier transform infrared spectroscopy, scanning electron microscopy, atomic force microscopy and dynamic contact angle measurement. The results demonstrated that a continuous and uniform PAA sizing layer was formed on the surface of carbon fibers, and the surface energy of carbon fibers increased from 42.91 to 54.55 mN/m after sizing treatment. The single fiber pull-out testing was also performed, which showed the increased interfacial shear strength (IFSS) of carbon fiber/PES composites from 33.6 to 49.7 MPa by 47.9%. The major reasons for the improved interfacial adhesion were the increased van der Waals forces between the PES matrix and sizing layer as well as the chemical bonding between the sizing layer and carbon fiber surface. Furthermore, the PAA sizing also presented a positive effect on the interfacial adhesion of carbon fiber/PES composites under hydrothermal condition.

Improved interfacial adhesion in carbon fiber/polyether sulfone composites through an organic solvent-free polyamic acid sizing

International Nuclear Information System (INIS)

Yuan, Haojie; Zhang, Shouchun; Lu, Chunxiang; He, Shuqing; An, Feng

2013-01-01

An organic solvent-free polyamic acid (PAA) nanoemulsion was obtained by direct ionization of the solid PAA in deionized water, with the average particle size of 261 nm and Zeta potential of −55.1 mV, and used as a carbon fiber sizing to improve the interfacial adhesion between the carbon fiber and polyether sulfone (PES). The surface characteristics of PAA coated carbon fibers were investigated using Fourier transform infrared spectroscopy, scanning electron microscopy, atomic force microscopy and dynamic contact angle measurement. The results demonstrated that a continuous and uniform PAA sizing layer was formed on the surface of carbon fibers, and the surface energy of carbon fibers increased from 42.91 to 54.55 mN/m after sizing treatment. The single fiber pull-out testing was also performed, which showed the increased interfacial shear strength (IFSS) of carbon fiber/PES composites from 33.6 to 49.7 MPa by 47.9%. The major reasons for the improved interfacial adhesion were the increased van der Waals forces between the PES matrix and sizing layer as well as the chemical bonding between the sizing layer and carbon fiber surface. Furthermore, the PAA sizing also presented a positive effect on the interfacial adhesion of carbon fiber/PES composites under hydrothermal condition.

Corrosion of graphite composites in phosphoric acid fuel cells

Science.gov (United States)

Christner, L. G.; Dhar, H. P.; Farooque, M.; Kush, A. K.

1986-01-01

Polymers, polymer-graphite composites and different carbon materials are being considered for many of the fuel cell stack components. Exposure to concentrated phosphoric acid in the fuel cell environment and to high anodic potential results in corrosion. Relative corrosion rates of these materials, failure modes, plausible mechanisms of corrosion and methods for improvement of these materials are investigated.

Improvement in transdermal drug delivery performance by graphite oxide/temperature-responsive hydrogel composites with micro heater

International Nuclear Information System (INIS)

Yun, Jumi; Lee, Dae Hoon; Im, Ji Sun; Kim, Hyung-Il

2012-01-01

Transdermal drug delivery system (TDDS) was prepared with temperature-responsive hydrogel. The graphite was oxidized and incorporated into hydrogel matrix to improve the thermal response of hydrogel. The micro heater was fabricated to control the temperature precisely by adopting a joule heating method. The drug in hydrogel was delivered through a hairless mouse skin by controlling temperature. The efficiency of drug delivery was improved obviously by incorporation of graphite oxide due to the excellent thermal conductivity and the increased interfacial affinity between graphite oxide and hydrogel matrix. The fabricated micro heater was effective in controlling the temperature over lower critical solution temperature of hydrogel precisely with a small voltage less than 1 V. The cell viability test on graphite oxide composite hydrogel showed enough safety for using as a transdermal drug delivery patch. The performance of TDDS could be improved noticeably based on temperature-responsive hydrogel, thermally conductive graphite oxide, and efficient micro heater. - Graphical abstract: The high-performance transdermal drug delivery system could be prepared by combining temperature-responsive hydrogel, thermally conductive graphite oxide with improved interfacial affinity, and efficient micro heater fabricated by a joule heating method. Highlights: ► High performance of transdermal drug delivery system with an easy control of voltage. ► Improved thermal response of hydrogel by graphite oxide incorporation. ► Efficient micro heater fabricated by a joule heating method.

New Insights of Graphite Anode Stability in Rechargeable Batteries: Li-Ion Coordination Structures Prevail over Solid Electrolyte Interphases

KAUST Repository

Ming, Jun

2018-01-04

Graphite anodes are not stable in most noncarbonate solvents (e.g., ether, sulfoxide, sulfone) upon Li ion intercalation, known as an urgent issue in present Li ions and next-generation Li–S and Li–O2 batteries for storage of Li ions within the anode for safety features. The solid electrolyte interphase (SEI) is commonly believed to be decisive for stabilizing the graphite anode. However, here we find that the solvation structure of the Li ions, determined by the electrolyte composition including lithium salts, solvents, and additives, plays a more dominant role than SEI in graphite anode stability. The Li ion intercalation desired for battery operation competes with the undesired Li+–solvent co-insertion, leading to graphite exfoliation. The increase in organic lithium salt LiN(SO2CF3)2 concentration or, more effectively, the addition of LiNO3 lowers the interaction strength between Li+ and solvents, suppressing the graphite exfoliation caused by Li+–solvent co-insertion. Our findings refresh the knowledge of the well-known SEI for graphite stability in metal ion batteries and also provide new guidelines for electrolyte systems to achieve reliable and safe Li–S full batteries.

Development of time projection chamber for precise neutron lifetime measurement using pulsed cold neutron beams

Energy Technology Data Exchange (ETDEWEB)

Arimoto, Y. [High Energy Accelerator Research Organization, Ibaraki (Japan); Higashi, N. [Graduate School of Science, University of Tokyo, Tokyo (Japan); Igarashi, Y. [High Energy Accelerator Research Organization, Ibaraki (Japan); Iwashita, Y. [Institute for Chemical Research, Kyoto University, Kyoto (Japan); Ino, T. [High Energy Accelerator Research Organization, Ibaraki (Japan); Katayama, R. [Graduate School of Science, University of Tokyo, Tokyo (Japan); Kitaguchi, M. [Kobayashi-Maskawa Institute, Nagoya University, Aichi (Japan); Kitahara, R. [Graduate School of Science, Kyoto University, Kyoto (Japan); Matsumura, H.; Mishima, K. [High Energy Accelerator Research Organization, Ibaraki (Japan); Nagakura, N.; Oide, H. [Graduate School of Science, University of Tokyo, Tokyo (Japan); Otono, H., E-mail: otono@phys.kyushu-u.ac.jp [Research Centre for Advanced Particle Physics, Kyushu University, Fukuoka (Japan); Sakakibara, R. [Department of Physics, Nagoya University, Aichi (Japan); Shima, T. [Research Center for Nuclear Physics, Osaka University, Osaka (Japan); Shimizu, H.M.; Sugino, T. [Department of Physics, Nagoya University, Aichi (Japan); Sumi, N. [Faculty of Sciences, Kyushu University, Fukuoka (Japan); Sumino, H. [Department of Basic Science, University of Tokyo, Tokyo (Japan); Taketani, K. [High Energy Accelerator Research Organization, Ibaraki (Japan); and others

2015-11-01

A new time projection chamber (TPC) was developed for neutron lifetime measurement using a pulsed cold neutron spallation source at the Japan Proton Accelerator Research Complex (J-PARC). Managing considerable background events from natural sources and the beam radioactivity is a challenging aspect of this measurement. To overcome this problem, the developed TPC has unprecedented features such as the use of polyether-ether-ketone plates in the support structure and internal surfaces covered with {sup 6}Li-enriched tiles to absorb outlier neutrons. In this paper, the design and performance of the new TPC are reported in detail.

Sintering behavior and thermal conductivity of nickel-coated graphite flake/copper composites fabricated by spark plasma sintering

Science.gov (United States)

Xu, Hui; Chen, Jian-hao; Ren, Shu-bin; He, Xin-bo; Qu, Xuan-hui

2018-04-01

Nickel-coated graphite flakes/copper (GN/Cu) composites were fabricated by spark plasma sintering with the surface of graphite flakes (GFs) being modified by Ni-P electroless plating. The effects of the phase transition of the amorphous Ni-P plating and of Ni diffusion into the Cu matrix on the densification behavior, interfacial microstructure, and thermal conductivity (TC) of the GN/Cu composites were systematically investigated. The introduction of Ni-P electroless plating efficiently reduced the densification temperature of uncoated GF/Cu composites from 850 to 650°C and slightly increased the TC of the X-Y basal plane of the GF/Cu composites with 20vol%-30vol% graphite flakes. However, when the graphite flake content was greater than 30vol%, the TC of the GF/Cu composites decreased with the introduction of Ni-P plating as a result of the combined effect of the improved heat-transfer interface with the transition layer, P generated at the interface, and the diffusion of Ni into the matrix. Given the effect of the Ni content on the TC of the Cu matrix and on the interface thermal resistance, a modified effective medium approximation model was used to predict the TC of the prepared GF/Cu composites.

Novel Lead dioxide-Graphite-Polymer composite anode for electrochemical chlorine generation

Czech Academy of Sciences Publication Activity Database

Gedam, N.; Neti, R.N.; Kormunda, M.; Šubrt, Jan; Bakardjieva, Snejana

2015-01-01

Roč. 169, JUL (2015), s. 109-116 ISSN 0013-4686 Institutional support: RVO:61388980 Keywords : beta-Lead dioxide * Graphite * Polymer composite anode * Chlorine generation * Cyclic voltammetry Subject RIV: CG - Electrochemistry Impact factor: 4.803, year: 2015

Correlation between Mechanical Properties with Specific Wear Rate and the Coefficient of Friction of Graphite/Epoxy Composites

Directory of Open Access Journals (Sweden)

Mahdi Alajmi

2015-07-01

Full Text Available The correlation between the mechanical properties of Fillers/Epoxy composites and their tribological behavior was investigated. Tensile, hardness, wear, and friction tests were conducted for Neat Epoxy (NE, Graphite/Epoxy composites (GE, and Data Palm Fiber/Epoxy with or without Graphite composites (GFE and FE. The correlation was made between the tensile strength, the modulus of elasticity, elongation at the break, and the hardness, as an individual or a combined factor, with the specific wear rate (SWR and coefficient of friction (COF of composites. In general, graphite as an additive to polymeric composite has had an eclectic effect on mechanical properties, whereas it has led to a positive effect on tribological properties, whilst date palm fibers (DPFs, as reinforcement for polymeric composite, promoted a mechanical performance with a slight improvement to the tribological performance. Statistically, this study reveals that there is no strong confirmation of any marked correlation between the mechanical and the specific wear rate of filler/Epoxy composites. There is, however, a remarkable correlation between the mechanical properties and the friction coefficient of filler/Epoxy composites.

Correlation between Mechanical Properties with Specific Wear Rate and the Coefficient of Friction of Graphite/Epoxy Composites.

Science.gov (United States)

Alajmi, Mahdi; Shalwan, Abdullah

2015-07-08

The correlation between the mechanical properties of Fillers/Epoxy composites and their tribological behavior was investigated. Tensile, hardness, wear, and friction tests were conducted for Neat Epoxy (NE), Graphite/Epoxy composites (GE), and Data Palm Fiber/Epoxy with or without Graphite composites (GFE and FE). The correlation was made between the tensile strength, the modulus of elasticity, elongation at the break, and the hardness, as an individual or a combined factor, with the specific wear rate (SWR) and coefficient of friction (COF) of composites. In general, graphite as an additive to polymeric composite has had an eclectic effect on mechanical properties, whereas it has led to a positive effect on tribological properties, whilst date palm fibers (DPFs), as reinforcement for polymeric composite, promoted a mechanical performance with a slight improvement to the tribological performance. Statistically, this study reveals that there is no strong confirmation of any marked correlation between the mechanical and the specific wear rate of filler/Epoxy composites. There is, however, a remarkable correlation between the mechanical properties and the friction coefficient of filler/Epoxy composites.

Bubble Departure from Metal-Graphite Composite Surfaces and Its Effects on Pool Boiling Heat Transfer

Science.gov (United States)

Chao, David F.; Sankovic, John M.; Motil, Brian J.; Yang, W-J.; Zhang, Nengli

2010-01-01

The formation and growth processes of a bubble in the vicinity of graphite micro-fiber tips on metal-graphite composite boiling surfaces and their effects on boiling behavior are investigated. It is discovered that a large number of micro bubbles are formed first at the micro scratches and cavities on the metal matrix in pool boiling. By virtue of the non-wetting property of graphite, once the growing micro bubbles touch the graphite tips, the micro bubbles are sucked by the tips and merged into larger micro bubbles sitting on the end of the tips. The micro bubbles grow rapidly and coalesce to form macro bubbles, each spanning several tips. The necking process of a detaching macro bubble is analyzed. It is revealed that a liquid jet is produced by sudden break-off of the bubble throat. The composite surfaces not only have higher temperatures in micro- and macrolayers but also make higher frequency of the bubble departure, which increase the average heat fluxes in both the bubble growth stage and in the bubble departure period. Based on these analyses, the enhancement mechanism of pool boiling heat transfer on composite surfaces is clearly revealed.

Sequential enzymatic epoxidation involved in polyether lasalocid biosynthesis.

Science.gov (United States)

Minami, Atsushi; Shimaya, Mayu; Suzuki, Gaku; Migita, Akira; Shinde, Sandip S; Sato, Kyohei; Watanabe, Kenji; Tamura, Tomohiro; Oguri, Hiroki; Oikawa, Hideaki

2012-05-02

Enantioselective epoxidation followed by regioselective epoxide opening reaction are the key processes in construction of the polyether skeleton. Recent genetic analysis of ionophore polyether biosynthetic gene clusters suggested that flavin-containing monooxygenases (FMOs) could be involved in the oxidation steps. In vivo and in vitro analyses of Lsd18, an FMO involved in the biosynthesis of polyether lasalocid, using simple olefin or truncated diene of a putative substrate as substrate mimics demonstrated that enantioselective epoxidation affords natural type mono- or bis-epoxide in a stepwise manner. These findings allow us to figure out enzymatic polyether construction in lasalocid biosynthesis. © 2012 American Chemical Society

40 CFR 721.3710 - Polyether modified fatty acids (generic).

Science.gov (United States)

2010-07-01

... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Polyether modified fatty acids... Specific Chemical Substances § 721.3710 Polyether modified fatty acids (generic). (a) Chemical substance... Polyether modified fatty acids (PMN P-99-0435) is subject to reporting under this section for the...

Enhancement of the anticoccidial activity of polyether antibiotics in chickens by tiamulin.

Science.gov (United States)

Meingassner, J G; Schmook, F P; Czok, R; Mieth, H

1979-03-01

The anticoccidial activities of monensin and lasalocid have been studied separately and in combination with tiamulin, a new pleuromutilin derivative. Combinations of constant tiamulin concentration (.0125%) in drinking water with various levels of polyether anticoccidials (6.3 to 125 ppm) in feed and conversely of constant levels of anticoccidials with various concentrations of tiamulin were used. The prophylactic efficacy of these combined treatments in battery raised broiler chickens infected with Eimeria tenella was evaluated. Assessment of the parameters mortality, weight gain, dropping scores, lesion scores, and oocyst output showed that simultaneous application of tiamulin significantly improved the anticoccidial activity of the polyethers. As tiamulin alone is without anticoccidial activity, this phenomenon was considered to result from an interaction between tiamulin and the polyethers leading to a slower metabolic degradation of the latter. Thus tissue levels adequate for maximum anticoccidial activity would be attained with lower polyether dose levels. Experiments using isolated perfused rat liver showed that elimination of monensin was reduced by 60% in the presence of tiamulin.

Graphite in Science and Nuclear Technique

OpenAIRE

Zhmurikov, E. I.; Bubnenkov, I. A.; Dremov, V. V.; Samarin, S. I.; Pokrovsky, A. S.; Harkov, D. V.

2013-01-01

The monograph is devoted to the application of graphite and graphite composites in science and technology. The structure and electrical properties, the technological aspects of production of high-strength synthetic graphites, the dynamics of the graphite destruction, traditionally used in the nuclear industry are discussed. It is focuses on the characteristics of graphitization and properties of graphite composites based on carbon isotope 13C. The book is based, generally, on the original res...

Ketones blood test

Science.gov (United States)

Acetone bodies; Ketones - serum; Nitroprusside test; Ketone bodies - serum; Ketones - blood; Ketoacidosis - ketones blood test ... fat cells break down in the blood. This test is used to diagnose ketoacidosis . This is a ...

New Fluorinated Polymers

Science.gov (United States)

Fitch, John W., III

1997-01-01

This report summarizes progress during 1996 in our research effort along with a description of additional results associated with a TAG supplement to this grant (items 2 and 5 below). Progress is reported in five areas: 1) Polyamides Derived from [(p-HOOCC6H4)](sub 2)C(CF3)X (X= -CF3, OCH3, Cl); 2) Phosphorus-containing '12F-PEK' - Effect of Systematic Replacement of [(p-FC6H4COC6H4)](sub 2)C[(CF3)](sub 2) Monomer by [(p-FC6H4)](sub 2)(C6H5)PO; 3) Poly(ether ketone)s Derived from [(p-FC6H4COC6H4)](sub 2)(C6H5)PO; 4) New CF3-containing Organosilane Monomers and; 5) New Monomers for 12F-PEK Analogues with Improved Processability and Solubility.

Cooperative program for design, fabrication, and testing of graphite/epoxy composite helicopter shafting

Science.gov (United States)

Wright, C. C.; Baker, D. J.; Corvelli, N.; Thurston, L.; Clary, R.; Illg, W.

1971-01-01

The fabrication of UH-1 helicopter tail rotor drive shafts from graphite/epoxy composite materials is discussed. Procedures for eliminating wrinkles caused by lack of precure compaction are described. The development of the adhesive bond between aluminum end couplings and the composite tube is analyzed. Performance tests to validate the superiority of the composite materials are reported.

Polymer-derived-SiCN ceramic/graphite composite as anode material with enhanced rate capability for lithium ion batteries

Science.gov (United States)

Graczyk-Zajac, M.; Fasel, C.; Riedel, R.

2011-08-01

We report on a new composite material in view of its application as a negative electrode in lithium-ion batteries. A commercial preceramic polysilazane mixed with graphite in 1:1 weight ratio was transformed into a SiCN/graphite composite material through a pyrolytic polymer-to-ceramic conversion at three different temperatures, namely 950 °C, 1100 °C and 1300 °C. By means of Raman spectroscopy we found successive ordering of carbon clusters into nano-crystalline graphitic regions with increasing pyrolysis temperature. The reversible capacity of about 350 mAh g-1 was measured with constant current charging/discharging for the composite prepared at 1300 °C. For comparison pure graphite and pure polysilazane-derived SiCN ceramic were examined as reference materials. During fast charging and discharging the composite material demonstrates enhanced capacity and stability. Charging and discharging in half an hour lead to about 200 and 10 mAh g-1, for the composite annealed at 1300 °C and pure graphite, respectively. A clear dependence between the final material capacity and pyrolysis temperature is found and discussed with respect to possible application in batteries, i.e. practical discharging potential limit. The best results in terms of capacity recovered under 1 V and high rate capability were also obtained for samples synthesized at 1300 °C.

Graphite Composite Panel Polishing Fixture

Science.gov (United States)

Hagopian, John; Strojny, Carl; Budinoff, Jason

2011-01-01

The use of high-strength, lightweight composites for the fixture is the novel feature of this innovation. The main advantage is the light weight and high stiffness-to-mass ratio relative to aluminum. Meter-class optics require support during the grinding/polishing process with large tools. The use of aluminum as a polishing fixture is standard, with pitch providing a compliant layer to allow support without deformation. Unfortunately, with meter-scale optics, a meter-scale fixture weighs over 120 lb (.55 kg) and may distort the optics being fabricated by loading the mirror and/or tool used in fabrication. The use of composite structures that are lightweight yet stiff allows standard techniques to be used while providing for a decrease in fixture weight by almost 70 percent. Mounts classically used to support large mirrors during fabrication are especially heavy and difficult to handle. The mount must be especially stiff to avoid deformation during the optical fabrication process, where a very large and heavy lap often can distort the mount and optic being fabricated. If the optic is placed on top of the lapping tool, the weight of the optic and the fixture can distort the lap. Fixtures to support the mirror during fabrication are often very large plates of aluminum, often 2 in. (.5 cm) or more in thickness and weight upwards of 150 lb (68 kg). With the addition of a backing material such as pitch and the mirror itself, the assembly can often weigh over 250 lb (.113 kg) for a meter-class optic. This innovation is the use of a lightweight graphite panel with an aluminum honeycomb core for use as the polishing fixture. These materials have been used in the aerospace industry as structural members due to their light weight and high stiffness. The grinding polishing fixture consists of the graphite composite panel, fittings, and fixtures to allow interface to the polishing machine, and introduction of pitch buttons to support the optic under fabrication. In its

Cyclodextrin ketones as oxidation catalysts: investigation of bridged derivatives

DEFF Research Database (Denmark)

Fenger, Thomas Hauch; Marinescu, Lavinia; Bols, Mikael

2009-01-01

A series of alpha-cyclodextrin derivatives containing a 3, 4 or 5 membered ether-linked bridge between the 6A and 6D oxygen atoms, with and without a ketone, were prepared. The synthesis used perbenzylated alpha-cyclodextrin A,D-diol as a starting material upon which O-alkylation and further modi...... derivatives were also made. The 6A,6D-di-O-(propa-2-on-1,3-diyl)-6C,6F-di-O-methyl and di-O-pivaloyl derivatives were also prepared. The new compounds were analysed for catalysis of the oxidation of amines and alcohols....

Improvement in transdermal drug delivery performance by graphite oxide/temperature-responsive hydrogel composites with micro heater

Energy Technology Data Exchange (ETDEWEB)

Yun, Jumi [Department of Fine Chemical Engineering and Applied Chemistry, BK21-E2M, Chungnam National University, Daejeon 305-764 (Korea, Republic of); Lee, Dae Hoon [Environment Research Division, Korea Institute of Machinery and Materials, 171 Jang-dong, Yusong-gu, Daejeon 305-343 (Korea, Republic of); Im, Ji Sun [Department of Fine Chemical Engineering and Applied Chemistry, BK21-E2M, Chungnam National University, Daejeon 305-764 (Korea, Republic of); Kim, Hyung-Il, E-mail: hikim@cnu.ac.kr [Department of Fine Chemical Engineering and Applied Chemistry, BK21-E2M, Chungnam National University, Daejeon 305-764 (Korea, Republic of)

2012-08-01

Transdermal drug delivery system (TDDS) was prepared with temperature-responsive hydrogel. The graphite was oxidized and incorporated into hydrogel matrix to improve the thermal response of hydrogel. The micro heater was fabricated to control the temperature precisely by adopting a joule heating method. The drug in hydrogel was delivered through a hairless mouse skin by controlling temperature. The efficiency of drug delivery was improved obviously by incorporation of graphite oxide due to the excellent thermal conductivity and the increased interfacial affinity between graphite oxide and hydrogel matrix. The fabricated micro heater was effective in controlling the temperature over lower critical solution temperature of hydrogel precisely with a small voltage less than 1 V. The cell viability test on graphite oxide composite hydrogel showed enough safety for using as a transdermal drug delivery patch. The performance of TDDS could be improved noticeably based on temperature-responsive hydrogel, thermally conductive graphite oxide, and efficient micro heater. - Graphical abstract: The high-performance transdermal drug delivery system could be prepared by combining temperature-responsive hydrogel, thermally conductive graphite oxide with improved interfacial affinity, and efficient micro heater fabricated by a joule heating method. Highlights: Black-Right-Pointing-Pointer High performance of transdermal drug delivery system with an easy control of voltage. Black-Right-Pointing-Pointer Improved thermal response of hydrogel by graphite oxide incorporation. Black-Right-Pointing-Pointer Efficient micro heater fabricated by a joule heating method.

Bridged graphite oxide materials

Science.gov (United States)

Herrera-Alonso, Margarita (Inventor); McAllister, Michael J. (Inventor); Aksay, Ilhan A. (Inventor); Prud'homme, Robert K. (Inventor)

2010-01-01

Bridged graphite oxide material comprising graphite sheets bridged by at least one diamine bridging group. The bridged graphite oxide material may be incorporated in polymer composites or used in adsorption media.

Genetic Screening Strategy for Rapid Access to Polyether Ionophore Producers and Products in Actinomycetes ▿ †

Science.gov (United States)

Wang, Hao; Liu, Ning; Xi, Lijun; Rong, Xiaoying; Ruan, Jisheng; Huang, Ying

2011-01-01

Polyether ionophores are a unique class of polyketides with broad-spectrum activity and outstanding potency for the control of drug-resistant bacteria and parasites, and they are produced exclusively by actinomycetes. A special epoxidase gene encoding a critical tailoring enzyme involved in the biosynthesis of these compounds has been found in all five of the complete gene clusters of polyether ionophores published so far. To detect potential producer strains of these antibiotics, a pair of degenerate primers was designed according to the conserved regions of the five known polyether epoxidases. A total of 44 putative polyether epoxidase gene-positive strains were obtained by the PCR-based screening of 1,068 actinomycetes isolated from eight different habitats and 236 reference strains encompassing eight major families of Actinomycetales. The isolates spanned a wide taxonomic diversity based on 16S rRNA gene analysis, and actinomycetes isolated from acidic soils seemed to be a promising source of polyether ionophores. Four genera were detected to contain putative polyether epoxidases, including Micromonospora, which has not previously been reported to produce polyether ionophores. The designed primers also detected putative epoxidase genes from diverse known producer strains that produce polyether ionophores unrelated to the five published gene clusters. Moreover, phylogenetic and chemical analyses showed a strong correlation between the sequence of polyether epoxidases and the structure of encoded polyethers. Thirteen positive isolates were proven to be polyether ionophore producers as expected, and two new analogues were found. These results demonstrate the feasibility of using this epoxidase gene screening strategy to aid the rapid identification of known products and the discovery of unknown polyethers in actinomycetes. PMID:21421776

Extrusion-mixing compared with hand-mixing of polyether impression materials?

Science.gov (United States)

McMahon, Caroline; Kinsella, Daniel; Fleming, Garry J P

2010-12-01

The hypotheses tested were two-fold (a) whether altering the base:catalyst ratio influences working time, elastic recovery and strain in compression properties of a hand-mixed polyether impression material and (b) whether an extrusion-mixed polyether impression material would have a significant advantage over a hand-mixed polyether impression material mixed to the optimum base:catalyst ratio. The polyether was hand-mixed at the optimum (manufacturers recommended) base:catalyst ratios (7:1) and further groups were made by increasing or decreasing the catalyst length by 25%. Additionally specimens were also made from an extrusion-mixed polyether impression material and compared with the optimum hand-mixed base:catalyst ratio. A penetrometer assembly was used to measure the working time (n=5). Five cylindrical specimens for each hand-mixed and extrusion mixed group investigated were employed for elastic recovery and strain in compression testing. Hand-mixing polyether impression materials with 25% more catalyst than that recommended significantly decreased the working time while hand-mixing with 25% less catalyst than that recommended significantly increased the strain in compression. The extrusion-mixed polyether impression material provided similar working time, elastic recovery and strain in compression to the hand-mixed polyether mixed at the optimum base:catalyst ratio.

Nickel-Graphite Composite Compliant Interface and/or Hot Shoe Material

Science.gov (United States)

Firdosy, Samad A.; Chun-Yip Li, Billy; Ravi, Vilupanur A.; Fleurial, Jean-Pierre; Caillat, Thierry; Anjunyan, Harut

2013-01-01

Next-generation high-temperature thermoelectric-power-generating devices will employ segmented architectures and will have to reliably withstand thermally induced mechanical stresses produced during component fabrication, device assembly, and operation. Thermoelectric materials have typically poor mechanical strength, exhibit brittle behavior, and possess a wide range of coefficient of thermal expansion (CTE) values. As a result, the direct bonding at elevated temperatures of these materials to each other to produce segmented leg components is difficult, and often results in localized microcracking at interfaces and mec hanical failure due to the stresses that arise from the CTE mismatch between the various materials. Even in the absence of full mechanical failure, degraded interfaces can lead to increased electrical and thermal resistances, which adversely impact conversion efficiency and power output. The proposed solution is the insertion of a mechanically compliant layer, with high electrical and thermal conductivity, between the low- and high-temperature segments to relieve thermomechanical stresses during device fabrication and operation. This composite material can be used as a stress-relieving layer between the thermoelectric segments and/or between a thermoelectric segment and a hot- or cold-side interconnect material. The material also can be used as a compliant hot shoe. Nickel-coated graphite powders were hot-pressed to form a nickel-graphite composite material. A freestanding thermoelectric segmented leg was fabricated by brazing the compliant pad layer between the high-temperature p- Zintl and low-temperature p-SKD TE segments using Cu-Ag braze foils. The segmented leg stack was heated in vacuum under a compressive load to achieve bonding. The novelty of the innovation is the use of composite material that re duces the thermomechanical stresses en - countered in the construction of high-efficiency, high-temperature therm - o-electric devices. The

Terahertz absorption in graphite nanoplatelets/polylactic acid composites

Science.gov (United States)

Bychanok, D.; Angelova, P.; Paddubskaya, A.; Meisak, D.; Shashkova, L.; Demidenko, M.; Plyushch, A.; Ivanov, E.; Krastev, R.; Kotsilkova, R.; Ogrin, F. Y.; Kuzhir, P.

2018-04-01

The electromagnetic properties of composite materials based on poly(lactic) acid (PLA) filled with graphite nanoplatelets (GNP) were investigated in the microwave (26–37 GHz) and terahertz (0.2–1 THz) frequency ranges. The maximum of the imaginary part of the dielectric permittivity was observed close to 0.6 THz for composites with 1.5 and 3 wt.% of GNP. The experimental data of complex dielectric permittivity of GNP/PLA composites was modelled using the Maxwell-Garnett theory. The effects of fine dispersion, agglomeration, and percolation in GNP-based composites on its electromagnetic constitutive parameters, presence, and position of THz absorption peak are discussed on the basis of the modeling results and experimental data. The unique combination of conductive and geometrical parameters of GNP embedded into the PLA matrix below the percolation threshold allow us to obtain the THz-absorptive material, which may be effectively used as a 3D-printing filament.

Cs2CO3-Initiated Trifluoro-Methylation of Chalcones and Ketones for Practical Synthesis of Trifluoromethylated Tertiary Silyl Ethers

Directory of Open Access Journals (Sweden)

Cheng Dong

2017-05-01

Full Text Available It was found that 1,2-trifluoromethylation reactions of ketones, enones, and aldehydes were easily accomplished using the Prakash reagent in the presence of catalytic amounts of cesium carbonate, which represents an experimentally convenient, atom-economic process for this anionic trifluoromethylation of non-enolisable aldehydes and ketones.

High thermal conductivity of graphite fiber silicon carbide composites for fusion reactor application

International Nuclear Information System (INIS)

Snead, L.L.; Balden, M.; Causey, R.A.; Atsumi, H.

2002-01-01

The benefits of using CVI SiC/graphite fiber composites as low tritium retaining, high thermal conductivity composites for fusion applications are presented. Three-dimensional woven composites have been chemically vapor infiltrated with SiC and their thermophysical properties measured. One material used an intermediate grade graphite fiber in all directions (Amoco P55) while a second material used very high thermal conductive fiber (Amoco K-1100) in the high fiber density direction. The overall void was less than 20%. Strength as measured by four-point bending was comparable to those of SiC/SiC composite. The room temperature thermal conductivity in the high conductivity direction was impressive for both materials, with values >70 W/m K for the P-55 and >420 W/m K for the K-1100 variant. The thermal conductivity was measured as a function of temperature and exceeds the highest thermal conductivity of CVD SiC currently available at fusion relevant temperatures (>600 deg. C). Limited data on the irradiation-induced degradation in thermal conductivity is consistent with carbon fiber composite literature

Thermal expansion behaviour of high performance PEEK matrix composites

International Nuclear Information System (INIS)

Goyal, R K; Mulik, U P; Tiwari, A N; Negi, Y S

2008-01-01

The thermal expansion behaviour of high performance poly(ether-ether-ketone) (PEEK) composites reinforced with micro- (8 μm) and nano- (39 nm) sized Al 2 O 3 particles was studied. The distribution of Al 2 O 3 in the PEEK matrix was studied by scanning electron microscopy and transmission electron microscopy. The coefficient of thermal expansion (CTE) was reduced from 58 x 10 -6 deg. C -1 for pure PEEK to 22 x 10 -6 deg. C -1 at 43 vol% micro-Al 2 O 3 and to 23 x 10 -6 deg. C -1 at 12 vol% nano-Al 2 O 3 composites. For a given volume fraction, nano-Al 2 O 3 particles are more effective in reducing the CTE of composites than that of micro-Al 2 O 3 particles. This may be attributed to the much higher interfacial area or volume of nanocomposites than that of microcomposites. The upper limit and lower limit of the Schapery model separately fit closely the CTE of the micro- and nano-composites, respectively. Other models such as the rule of mixture and Kerner and Turner models were also correlated with the data

Fabrication and properties of poly(polyethylene glycol n-alkyl ether vinyl ether)s as polymeric phase change materials

International Nuclear Information System (INIS)

Pei, Dong-fang; Chen, Sai; Li, Shu-qin; Shi, Hai-feng; Li, Wei; Li, Xuan; Zhang, Xing-xiang

2016-01-01

A series of poly(polyethylene glycol n-alkyl ether vinyl ether)s (PC m E n VEs) with various lengths of alkyl chains and polyethylene glycol spacers as side chain (m = 16,18; n = 1,2) were synthesized via two steps. First, monomers-ethylene glycol hexadecyl ether vinyl ether (C 16 E 1 VE), ethylene glycol octadecyl ether vinyl ether (C 18 E 1 VE), diethylene glycol hexadecyl ether vinyl ether (C 16 E 2 VE) and diethylene glycol octadecyl ether vinyl ether (C 18 E 2 VE) were synthesized by a modified Williamson etherification. Then, four new types of phase change materials were successfully fabricated by a living cationic polymerization. Fourier transform infrared spectroscopy (FTIR), nuclear magnetic resonance spectroscopy (NMR), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC) and wide-angle X-ray diffraction (WAXD) were employed to characterize their composition, thermal properties and crystallization behavior. The results show that, the side chains of PC 16 E 1 VE, PC 18 E 1 VE, PC 16 E 2 VE and PC 18 E 2 VE are in a hexagonal lattice, and the onset temperatures for melting of PC 16 E 1 VE, PC 18 E 1 VE, PC 16 E 2 VE and PC 18 E 2 VE are 39.8 °C, 37.4 °C, 51.0 °C and 48.9 °C, the onset temperatures for crystallization are 36.7 °C, 35.2 °C, 47.4 °C and 46.3 °C, respectively. The enthalpy changes of PC 18 E 1 VE, PC 16 E 2 VE and PC 18 E 2 VE are higher than 100 J/g; on the contrary, it is 96 J/g for PC 16 E 1 VE. The enthalpy decrease is no more than 11% after 10 heating and cooling cycles. The 5 wt% mass loss temperatures of PC 18 E 1 VE, PC 16 E 2 VE and PC 18 E 2 VE are higher than 300 °C; on the contrary, it’s 283 °C for PC 16 E 1 VE. Using a weak polarity, flexible alkyl ether chain (-OCH 2 CH 2 O-) as a spacer to link the main chain and side chain is conducive to the crystallization of the alkyl side chain. These new phase change materials can be applied in heat storage, energy conservation, and environmental protection.

Facile synthesis of nanorod-type graphitic carbon nitride/Fe2O3 composite with enhanced photocatalytic performance

International Nuclear Information System (INIS)

Wang, Jiangpeng; Li, Changqing; Cong, Jingkun; Liu, Ziwei; Zhang, Hanzhuo; Liang, Mei; Gao, Junkuo; Wang, Shunli; Yao, Juming

2016-01-01

Here we report a facile synthesis of nanorod-type graphitic carbon nitride/Fe 2 O 3 composite (Fe 2 O 3 -g-C 3 N 4 ) by using Fe-melamine supramolecular framework as precursor. The chemical and optical properties of the nanocomposites are well-characterized. The Fe 2 O 3 -g-C 3 N 4 nanocomposite demonstrated excellent photocatalytic activities under visible light due to the efficient utilization of sunlight and the construction of Z-scheme electron transfer pathway. The results indicated that it could be a promising approach for the preparation of efficient g-C 3 N 4 nanocomposites photocatalysts by using metal-melamine supramolecular framework as precursors. - Graphical abstract: Nanorod-type graphitic carbon nitride/Fe 2 O 3 composite (Fe 2 O 3 -g-C 3 N 4 ) was synthesized by using Fe-melamine supramolecular framework as precursor. The Fe 2 O 3 -g-C 3 N 4 nanocomposite demonstrated excellent photocatalytic activities under visible light. Display Omitted - Highlights: • Nanorod-type graphitic carbon nitride/Fe 2 O 3 composite (Fe 2 O 3 -g-C 3 N 4 ) was synthesized. • Fe 2 O 3 -g-C 3 N 4 showed strong optical absorption in the visible-light region. • The Fe 2 O 3 -g-C 3 N 4 nanocomposite demonstrated excellent photocatalytic activities.

Rate-dependent mode I interlaminar crack growth mechanisms in graphite/epoxy and graphite/PEEK

Science.gov (United States)

Gillespie, J. W., Jr.; Carlsson, L. A.; Smiley, A. J.

1987-01-01

In this paper the mode I fracture behavior of graphite/epoxy and graphite/PEEK composites is examined over four decades of crosshead rates (0.25-250 mm/min). Straight-sided double-cantilever-beam specimens consisting of unidirectional laminates were tested at room temperature. For graphite/epoxy the load-deflection response was linear to fracture, and stable slow crack growth initiating at the highest load level was observed for all rates tested. In contrast, mode I crack growth in the graphite/PEEK material was often unstable and showed stick-slip behavior. Subcritical crack growth occurring prior to the onset of fracture was observed at intermediate displacement rates. A mechanism for the fracture behavior of the graphite/PEEK material (based on viscoelastic, plastic, and microcrack coalescence in the process zone) is proposed and related to the observed rate-dependent phenomena.

[Pollution Characteristics of Aldehydes and Ketones Compounds in the Exhaust of Beijing Typical Restaurants].

Science.gov (United States)

Cheng, Jing-chen; Cui, Tong; He, Wan-qing; Nie, Lei; Wang, Jun-ling; Pan, Tao

2015-08-01

Aldehydes and ketones compounds, as one of the components in the exhaust of restaurants, are a class of volatile organic compounds (VOCs) with strong chemical reactivity. However, there is no systematic study on aldehydes and ketones compounds in the exhaust of restaurants. To further clarify the food source emission levels of aldehydes and ketones compounds and controlling measures, to access city group catering VOCs emissions control decision-making basis, this study selected 8 Beijing restaurants with different types. The aldehydes and ketones compounds were sampled using DNPH-silica tube, and then ultra performance liquid chromatography was used for quantitative measurement. The aldehydes and ketones concentrations of reference volume condition from 8 restaurants in descending order were Roasted Duck restaurant, Chinese Style Barbecue, Home Dishes, Western Fast-food, School Canteen, Chinese Style Fast-food, Sichuan Cuisine, Huaiyang Cuisine. The results showed that the range of aldehydes and ketones compounds (C1-C9) concentrations of reference volume condition in the exhaust of restaurants was 115.47-1035.99 microg x m(-3). The composition of aldehydes and ketones compounds in the exhaust of sampled restaurants was obviously different. The percentages of C1-C3 were above 40% in the exhaust from Chinese style restaurants. Fast food might emit more C4-C9 aldehydes and ketones compounds. From the current situation of existing aldehydes and ketones compounds control, the removal efficiency of high voltage electrostatic purifiers widely used in Beijing is limited.