  1. Preparation and properties of hydrothermally stable gamma-alumina membranes

    NARCIS (Netherlands)

    Nijmeijer, Arian; Kruidhof, H.; Bredesen, Rune; Verweij, H.

    2001-01-01

    Supported mesoporous γ-Al2O3 membranes deteriorate and blister in steam-containing environments at high temperatures. This deterioration led us to the development of a new type of supported γ-Al2O3 membrane with significantly improved stability under hostile conditions. Two measures were taken to

  2. Preparation, characterization and microstructural optimization of a thin {gamma}-alumina membrane on a porous stainless steel substrate

    Energy Technology Data Exchange (ETDEWEB)

    Abedini, Sanam [Department of Mining and Metallurgical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Hafez Street, Tehran (Iran, Islamic Republic of); Parvin, Nader, E-mail: naderparvin@yahoo.com [Department of Mining and Metallurgical Engineering, Amirkabir University of Technology (Tehran Polytechnic), Hafez Street, Tehran (Iran, Islamic Republic of); Ashtari, Parviz [Nuclear Science and Technology Research Institute, Tehran (Iran, Islamic Republic of)

    2012-01-30

    Highlights: Black-Right-Pointing-Pointer A mesoporous {gamma}-Al{sub 2}O{sub 3} membrane was synthesized on conventional {alpha}-Al{sub 2}O{sub 3} substrates. Black-Right-Pointing-Pointer {gamma}-Al{sub 2}O{sub 3} membrane was potential for CO{sub 2} separation at high pressure test conditions. Black-Right-Pointing-Pointer Thus, it was required to provide the membrane layer with more strength. Black-Right-Pointing-Pointer {alpha}-Alumina substrate was substituted with porous stainless steel. Black-Right-Pointing-Pointer A stainless steel supported {alpha}-Al{sub 2}O{sub 3} membrane with better properties was synthesized. - Abstract: In this work, a supported mesoporous (MEP) {gamma}-Al{sub 2}O{sub 3} membrane was synthesized on conventional {alpha}-Al{sub 2}O{sub 3} substrates by sol-gel dip coating process. In the following, the preparation of a novel metallic-ceramic composite membrane was studied, which incorporated desirable properties of both ceramic membrane and porous metallic substrate. For this purpose, mesoporous alumina membrane layer was developed on a porous 316L stainless steel substrate. The substrate was prepared by loose powder sintering and modified by soaking-rolling and fast drying method. The prepared membranes were characterized using scanning electron microscope (SEM), field emission scanning electron microscope (FESEM), X-ray diffractometer (XRD) and N{sub 2}-adsorption/desorption measurements (BET analyses). The results revealed that a defect-free {gamma}-alumina membrane with 2.1 nm average pore size can be produced. Permeation tests with N{sub 2} gas revealed that the stainless steel substrate had 40 times more permeability than conventionally used alumina support. Additionally, single gas permeation of {gamma}-alumina membrane for CO{sub 2} and N{sub 2} was compared. It was observed that CO{sub 2} could be separated from N{sub 2} by the MEP {gamma}-Al{sub 2}O{sub 3} membrane in high pressure permeation condition, where stainless steel

  3. Attrition resistant gamma-alumina catalyst support

    Science.gov (United States)

    Singleton, Alan H.; Oukaci, Rachid; Goodwin, James G.

    2006-03-14

    A .gamma.-alumina catalyst support having improved attrition resistance produced by a method comprising the steps of treating a particulate .gamma.-alumina material with an acidic aqueous solution comprising water and nitric acid and then, prior to adding any catalytic material thereto, calcining the treated .gamma.-alumina.

  4. Fabrication of asymmetric alumina membranes

    International Nuclear Information System (INIS)

    Firouzghalb, H.; Falamaki, C.

    2010-01-01

    The effect of SrO addition on the thermal stabilization of transition aluminas with the aim of producing membrane layers (supported and unsupported) has been investigated. Al 2 O 3 -x wt.% SrO composite powders (x = 1, 3, 5, 8) were synthesized by co-precipitation of the hydroxides from solutions of AlCl 3 and Sr(NO 3 ) 2 salts using NH 4 OH as a precipitating agent. Optimum SrO dopant concentration regarding the transition aluminas stabilization effect was determined to be 5 wt.% based on XRD analysis. STA analysis showed a 30 deg. C shift versus higher temperatures in the transformation of final transitional alumina (θ-Al 2 O 3 ) to stable alpha phase due to addition of 5 wt.% SrO. The mechanism of transition aluminas thermal stabilization as a result of SrO addition is thoroughly discussed. Unsupported alumina membranes were prepared by drying boehmite sols at 600, 800, 1000 and 1100 deg. C. The effect of calcination temperature on surface area, pore size distribution of unsupported membranes containing 5 wt.% SrO has been investigated. The microstructure of unsupported and supported membranes revealed quite different. Smaller grains in the supported layers were attributed to the interaction between support and membrane.

  5. Ion adsorption parameters determined from zeta potential and titration data for a gamma-alumina nanofiltration membrane

    NARCIS (Netherlands)

    Samuel de Lint, W.B.; Benes, N.E.; Lyklema, J.; Bouwmeester, H.J.M.; Linde, van der A.J.; Wessling, M.

    2003-01-01

    Theoretical models for the prediction of nanofiltration separation performance as a function of, e.g., pH and electrolyte composition require knowledge on the ion-surface adsorption chemistry. Adsorption parameters have been extracted from electrophoretic mobility measurements on a ceramic -alumina

  6. Synthesis of Gamma-Alumina from Kankara Kaolin as Potential ...

    African Journals Online (AJOL)

    Engr Solomn Gajere

    Large specific surface area gamma-alumina (γ-Al2O3) was synthesized by hydrothermal method using Kankara kaolin as starting material. Thermal treatment of ammonium alum prepared from the filtrate of the dealuminated metakaolin was employed to obtain the alumina. Crystalline aluminum sulfate with 39 wt% Al2O3 ...

  7. Synthesis of Nano Crystalline Gamma Alumina from Waste Cans

    Directory of Open Access Journals (Sweden)

    Nada Sadoon Ahmedzeki

    2018-03-01

    Full Text Available In the present study waste aluminium cans were recycled and converted to produce alumina catalyst. These cans contain more than 98% aluminum oxide in their structure and were successfully synthesized to produce nano sized gamma alumina under mild conditions. A comprehensive study was carried out in order to examine the effect of several important parameters on maximum yield of alumina that can be produced. These parameters were reactants mole ratios (1.5, 1.5, 2, 3, 4 and 5, sodium hydroxide concentrations (10, 20, 30, 40, 50 and 55% and weights of aluminum cans (2, 4, 6, 8 and 10 g. The compositions of alumina solution were determined by Atomic absorption spectroscopy (AAS; and maximum yield of alumina solution was 96.3% obtained at 2 mole ratios of reactants, 40% sodium hydroxide concentrations and 10g of aluminum cans respectively. Gamma alumina was acquired by hydrothermal treatment of alumina solution at pH 7 and calcination temperature of 550 ºC. The prepared catalyst was characterized by X-ray diffraction (XRD, N2 adsorption/ desorption isotherms, X-ray fluorescence (XRF and atomic force microscopy (AFM. Results showed good crystallinity of alumina as described by XRD patterns, with surface area of 311.149 m2/g, 0.36 cm3/g pore volume, 5.248 nm pore size and particle size of 68.56 nm respectively.

  8. Synthesis of Gamma-Alumina from Kankara Kaolin as Potential ...

    African Journals Online (AJOL)

    In compounded zeolite catalyst it serves as the active matrix which aids the conversion of the bulkiest molecules in the feed owing to its larger pore size than zeolite. Large specific surface area gamma-alumina (γ-Al2O3) was synthesized by hydrothermal method using Kankara kaolin as starting material. Thermal treatment ...

  9. Sol-gel synthesized of nanocomposite palladium-alumina ceramic membrane for H{sub 2} permeability: Preparation and characterization

    Energy Technology Data Exchange (ETDEWEB)

    Ahmad, A.L.; Mustafa, N.N.N. [School of Chemical Engineering, Engineering Campus, Universiti Sains Malaysia, Seri Ampangan, 14300 Nibong Tebal, Penang (Malaysia)

    2007-08-15

    Palladium-alumina membrane with mesopore and narrow pore size distribution was prepared by the sol-gel method. Effect of the finely dispersed metal on the microstructure and the characteristic properties of the palladium-alumina membrane were investigated. Observations were made on membrane weight loss, morphology, pore structure, pore size, surface area, pore surface fractal and membrane's crystal structure. Autosorb analysis, X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and Fourier Transform Infrared (FTIR) analysis were employed in the membrane characterization. Autosorb analysis found that, BET surface area decreased and pore size of the membrane increased with the increasing of calcinations temperature (500-1100{sup o}C) and with the increasing of palladium amount in the membrane. FTIR and TG/DTA analysis show that the suitable temperature for calcinations of palladium-alumina membrane is at 700{sup o}C. Palladium metals are highly dispersed at calcinations temperature of 700{sup o}C as observed by TEM analysis. The fine crystallinity of the palladium and {gamma}-alumina phase was obtained after calcined at 700{sup o}C. The SEM morphology shows a smooth and free crack layer of palladium-alumina membrane after repeating the process of dipping, drying and calcinations at temperature of 700{sup o}C. The membrane also successfully coated with a good adhesion on support. The thickness of the final membrane layer was estimated as 9{mu} m. (author)

  10. Corrosion resistance characterization of porous alumina membrane supports

    Energy Technology Data Exchange (ETDEWEB)

    Dong Yingchao, E-mail: dongyc9@mail.ustc.edu.cn [Materials and Surface Science Institute (MSSI), University of Limerick, Limerick (Ireland); USTC Lab for Solid State Chemistry and Inorganic Membranes, Department of Materials Science and Engineering, University of Science and Technology of China (USTC) (China); Key Lab of Jiangxi Universities for Inorganic Membranes, National Engineering Research Center for Domestic and Building Ceramics, Jingdezhen Ceramic University (JCU) (China); Lin Bin [USTC Lab for Solid State Chemistry and Inorganic Membranes, Department of Materials Science and Engineering, University of Science and Technology of China (USTC) (China); Zhou Jianer [Key Lab of Jiangxi Universities for Inorganic Membranes, National Engineering Research Center for Domestic and Building Ceramics, Jingdezhen Ceramic University (JCU) (China); Zhang Xiaozhen [USTC Lab for Solid State Chemistry and Inorganic Membranes, Department of Materials Science and Engineering, University of Science and Technology of China (USTC) (China); Key Lab of Jiangxi Universities for Inorganic Membranes, National Engineering Research Center for Domestic and Building Ceramics, Jingdezhen Ceramic University (JCU) (China); Ling Yihan; Liu Xingqin; Meng Guangyao [USTC Lab for Solid State Chemistry and Inorganic Membranes, Department of Materials Science and Engineering, University of Science and Technology of China (USTC) (China); Hampshire, Stuart [Materials and Surface Science Institute (MSSI), University of Limerick, Limerick (Ireland)

    2011-04-15

    Tubular porous alumina ceramic membrane supports were fabricated by an extrusion-drying-sintering process and then characterized in detail in terms of corrosion resistance in both H{sub 2}SO{sub 4} and NaOH aqueous solutions. Variations in the properties of the alumina supports such as mass loss percent, mechanical strength, open porosity and pore size distribution were studied before and after corrosion under different conditions. In addition, the microstructures were analyzed using scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction before and after corrosion. The fabricated porous alumina supports offer possibilities for some potential applications as micro-filtration or ultra-filtration membrane supports, as well as in the pre-treatment of strongly acidic industrial waste-liquids. - Research highlights: {yields} Porous alumina membrane supports fabricated by extrusion-drying-sintering process. {yields} Corrosion resistance in 20 wt.% H{sub 2}SO{sub 4} and 1, 5, 10 wt.% NaOH aqueous solutions. {yields} Rapid mass loss and loss of flexural strength occurred in hot NaOH solution. {yields} Resistant to strong acid corrosion with low mass loss, low flexural strength loss. {yields} Porous alumina supports have potential for treatment of strong acid waste liquids.

  11. Synthesis of zeolite membrane (Y / α-alumina)

    International Nuclear Information System (INIS)

    Araujo, Ana Paula; Silva, Valmir Jose da; Crispin, Alana Carolyne; Rodrigues, Meiry Glaucia F.; Menezes, Romualdo R.

    2009-01-01

    The general aim of this study was to develop materials of the type: Y zeolite (hydrothermal synthesis), ceramic support (forming of powder) and zeolite membrane (rubbing). The preparation of the Y zeolite was conducted in accordance with the hydrothermal synthesis method, the time of crystallization was one day. The ceramic support was prepared by means of the forming of powder technique and subsequently subjected to sintering at a temperature of 1400 deg C/1h. The zeolite membrane (Y/α- alumina) was prepared by secondary growth method (rubbing). These materials were characterized by XRD and SEM. Obtaining Y zeolite could be confirmed by X ray diffractograms. From the images obtained by SEM, it was possible to derive from analysis that the Y zeolite is composed of a homogeneous morphology, where the particles are crowded, with uniform size. The results obtained for the ceramic support (α-alumina) showed that it displays characteristics peaks of aluminum oxide. By using micrographs it was possible to observe a heterogeneous microstructure with a compact form, without cracks upon the layers. According to the XRD, for the method of secondary growth (rubbing), it was observed that the Y zeolite which had been synthesized on the ceramic support displayed a crystalline structure. The micrography of the zeolite membrane (Y/α-alumina) showed the formation of a layer of zeolite on the ceramic support. (author)

  12. Metal–Organic Framework-Functionalized Alumina Membranes for Vacuum Membrane Distillation

    Directory of Open Access Journals (Sweden)

    Jian Zuo

    2016-12-01

    Full Text Available Nature-mimetic hydrophobic membranes with high wetting resistance have been designed for seawater desalination via vacuum membrane distillation (VMD in this study. This is achieved through molecular engineering of metal–organic framework (MOF-functionalized alumina surfaces. A two-step synthetic strategy was invented to design the hydrophobic membranes: (1 to intergrow MOF crystals on the alumina tube substrate and (2 to introduce perfluoro molecules onto the MOF functionalized membrane surface. With the first step, the surface morphology, especially the hierarchical roughness, can be controlled by tuning the MOF crystal structure. After the second step, the perfluoro molecules function as an ultrathin layer of hydrophobic floss, which lowers the surface energy. Therefore, the resultant membranes do not only possess the intrinsic advantages of alumina supports such as high stability and high water permeability, but also have a hydrophobic surface formed by MOF functionalization. The membrane prepared under an optimum condition achieved a good VMD flux of 32.3 L/m2-h at 60 °C. This study may open up a totally new approach for design of next-generation high performance membrane distillation membranes for seawater desalination.

  13. Surface modification of nanoporous alumina membranes by plasma polymerization

    Energy Technology Data Exchange (ETDEWEB)

    Losic, Dusan; Cole, Martin A; Dollmann, Bjoern; Vasilev, Krasimir; Griesser, Hans J [Ian Wark Research Institute, University of South Australia, Mawson Lakes, Adelaide, SA 5095 (Australia)], E-mail: dusan.losic@unisa.edu.au

    2008-06-18

    The deposition of plasma polymer coatings onto porous alumina (PA) membranes was investigated with the aim of adjusting the surface chemistry and the pore size of the membranes. PA membranes from commercial sources with a range of pore diameters (20, 100 and 200 nm) were used and modified by plasma polymerization using n-heptylamine (HA) monomer, which resulted in a chemically reactive polymer surface with amino groups. Heptylamine plasma polymer (HAPP) layers with a thickness less than the pore diameter do not span the pores but reduce their diameter. Accordingly, by adjusting the deposition time and thus the thickness of the plasma polymer coating, it is feasible to produce any desired pore diameter. The structural and chemical properties of modified membranes were studied by scanning electron microscopy (SEM), atomic force microscopy (AFM) and x-ray electron spectroscopy (XPS). The resultant PA membranes with specific surface chemistry and controlled pore size are applicable for molecular separation, cell culture, bioreactors, biosensing, drug delivery, and engineering complex composite membranes.

  14. Surface modification of nanoporous alumina membranes by plasma polymerization

    International Nuclear Information System (INIS)

    Losic, Dusan; Cole, Martin A; Dollmann, Bjoern; Vasilev, Krasimir; Griesser, Hans J

    2008-01-01

    The deposition of plasma polymer coatings onto porous alumina (PA) membranes was investigated with the aim of adjusting the surface chemistry and the pore size of the membranes. PA membranes from commercial sources with a range of pore diameters (20, 100 and 200 nm) were used and modified by plasma polymerization using n-heptylamine (HA) monomer, which resulted in a chemically reactive polymer surface with amino groups. Heptylamine plasma polymer (HAPP) layers with a thickness less than the pore diameter do not span the pores but reduce their diameter. Accordingly, by adjusting the deposition time and thus the thickness of the plasma polymer coating, it is feasible to produce any desired pore diameter. The structural and chemical properties of modified membranes were studied by scanning electron microscopy (SEM), atomic force microscopy (AFM) and x-ray electron spectroscopy (XPS). The resultant PA membranes with specific surface chemistry and controlled pore size are applicable for molecular separation, cell culture, bioreactors, biosensing, drug delivery, and engineering complex composite membranes

  15. Factors influencing the transport rate of short-chain alcohols through mesoporous y-alumina membranes

    NARCIS (Netherlands)

    Roy Chowdhury, Sankhanilay; Roy Chowdhury, S.; Blank, David H.A.; ten Elshof, Johan E.

    2005-01-01

    The pressure-driven transport of water, ethanol, and 1-propanol through supported -alumina membranes with different pore diameters is reported. Water and alcohols had similar permeabilities when they were transported through y-alumina membranes with average pore diameters of 4.4 and 6.0 nm, and the

  16. Studies on hydrogen separation membrane for IS process. Membrane preparation with porous α-alumina tube

    International Nuclear Information System (INIS)

    Hwang, Gab-Jin; Onuki, Kaoru; Shimizu, Saburo

    1998-01-01

    It was investigated the preparation technique of hydrogen separation membrane to enhance the decomposition ratio of hydrogen iodide in the thermochemical IS process. Hydrogen separation membranes based on porous α-alumina tubes having pore size of 100 nm and 10 nm were prepared by chemical vapor deposition using tetraethylorthosilicate (TEOS) as the Si source. In the hydrogen separation membrane, its pore was closed by the deposited silica and then the permeation of gas was affected by the hindrance diffusion. At 600degC, the selectivity ratios (H 2 /N 2 ) were 5.2 and 160 for the membranes based on porous α-alumina tube having pore size of 100 nm and 10 nm, respectively. (author)

  17. Magnetic properties of ferromagnetic nanowires embedded in nanoporous alumina membranes

    International Nuclear Information System (INIS)

    Kroell, M.; Blau, W.J.; Grandjean, D.; Benfield, R.E.; Luis, F.; Paulus, P.M.; Jongh, L.J. de

    2002-01-01

    Iron, nickel and cobalt nanowires are prepared within the pores of nanoporous alumina membranes using an electrochemical AC plating procedure. Nanowires produced in this way can be easily varied in diameter (5-250 nm) and length (up to several hundred microns). The magnetisation curves for these nanowire/alumina composites can then be determined not only as a function of the temperature but also as a function of the wire diameter and length. Conclusions regarding the magnetisation reversal processes that take place in the wires can be drawn. For Fe and Ni nanowires, we show that the magnetisation process in wires with a diameter smaller than the domain wall width is independent of the wire length and probably takes place via the formation of a small magnetic domain at the end of the wires and a subsequent propagation of the domain wall along the wire. For Co nanowires a competition between the shape anisotropy and the temperature- and size-dependent magnetocrystalline anisotropy could be observed

  18. Performance study of mullite and mullite-alumina ceramic MF membranes for oily wastewaters treatment

    DEFF Research Database (Denmark)

    Abbasi, Mohsen; Mirfendereski, Mojtaba; Fini, Mahdi Nikbakht

    2010-01-01

    In this paper, results of an experimental study on separation of oil from actual and synthetic oily wastewaters with mullite and mullite-alumina tubular ceramic membranes are presented. Mullite and mullite-alumina microfiltration (MF) symmetric membranes were synthesized from kaolin clay and α......-alumina membranes for treatment of synthetic wastewaters were investigated. In order to determine the best operating conditions, 250-3000ppm condensate gas in water emulsions was employed as synthetic oily wastewaters using mullite membrane. At the best operating conditions (3bar pressure, 1.5m/s cross flow...... velocity and 35°C temperature), performance of mullite and mullite-alumina membranes for treatment of real and synthetic wastewaters were also compared. The results for treatment of emulsions showed that the mullite ceramic membrane has the highest R (93.8%) and the lowest FR (28.97%). Also, the mullite...

  19. Ultrafast excited state deactivation of doped porous anodic alumina membranes

    International Nuclear Information System (INIS)

    Makhal, Abhinandan; Sarkar, Soumik; Pal, Samir Kumar; Yan, Hongdan; Wulferding, Dirk; Cetin, Fatih; Lemmens, Peter

    2012-01-01

    Free-standing, bi-directionally permeable and ultra-thin anodic aluminum oxide (AAO) membranes establish attractive templates (host) for the synthesis of nano-dots and rods of various materials (guest). This is due to their chemical and structural integrity and high periodicity on length scales of 5–150 nm which are often used to host photoactive nano-materials for various device applications including dye-sensitized solar cells. In the present study, AAO membranes are synthesized by using electrochemical methods and a detailed structural characterization using FEG-SEM, XRD and TGA confirms the porosity and purity of the material. Defect-mediated photoluminescence quenching of the porous AAO membrane in the presence of an electron accepting guest organic molecule (benzoquinone) is studied by means of steady-state and picosecond/femtosecond-resolved luminescence measurements. Using time-resolved luminescence transients, we have also revealed light harvesting of complexes of porous alumina impregnated with inorganic quantum dots (Maple Red) or gold nanowires. Both the Förster resonance energy transfer and the nano-surface energy transfer techniques are employed to examine the observed quenching behavior as a function of the characteristic donor–acceptor distances. The experimental results will find their relevance in light harvesting devices based on AAOs combined with other materials involving a decisive energy/charge transfer dynamics. (paper)

  20. Optical properties of alumina membranes prepared by anodic oxidation process

    International Nuclear Information System (INIS)

    Li Zhaojian; Huang Kelong

    2007-01-01

    The luminescence property of anodic alumina membranes (AAMs) with ordered nanopore arrays prepared by electrochemically anodizing aluminum in oxalic acid solutions have been investigated. Photoluminescence emission (PL) measurement shows that a blue PL band occurs in the wavelength ranges of 300-600 nm. The PL intensity and peak position of AAMs depend markedly on the excitation wavelength. A new peak located at 518 nm can be observed under a monitoring wavelength at 429 nm in the photoluminescence excitation (PLE) spectra. Convincing evidences have been presented that the PLE would be associated with the residual aluminum ions in the membrane. The PLE and PL of AAMs, as a function of anodizing times, have been discussed. It is found that the oxalic impurities incorporated in the AAMs would have important influences on the optical properties of AAMs in the initial stage of anodization. The PL and PLE spectra obtained show that there are three optical centers, of which the first is originated from the F + centers in AAMs, the second is correlated with the oxalic impurities incorporated in the AAMs, and the third is associated with the excess aluminum ions in the membrane

  1. Optical properties of alumina membranes prepared by anodic oxidation process

    Energy Technology Data Exchange (ETDEWEB)

    Li Zhaojian [College of Chemistry and Chemical Engineering, Central South University, Changsha 410083 (China)], E-mail: lizhaojian_lzj@hotmail.com; Huang Kelong [College of Chemistry and Chemical Engineering, Central South University, Changsha 410083 (China)], E-mail: klhuang@mail.csu.edu.cn

    2007-12-15

    The luminescence property of anodic alumina membranes (AAMs) with ordered nanopore arrays prepared by electrochemically anodizing aluminum in oxalic acid solutions have been investigated. Photoluminescence emission (PL) measurement shows that a blue PL band occurs in the wavelength ranges of 300-600 nm. The PL intensity and peak position of AAMs depend markedly on the excitation wavelength. A new peak located at 518 nm can be observed under a monitoring wavelength at 429 nm in the photoluminescence excitation (PLE) spectra. Convincing evidences have been presented that the PLE would be associated with the residual aluminum ions in the membrane. The PLE and PL of AAMs, as a function of anodizing times, have been discussed. It is found that the oxalic impurities incorporated in the AAMs would have important influences on the optical properties of AAMs in the initial stage of anodization. The PL and PLE spectra obtained show that there are three optical centers, of which the first is originated from the F{sup +} centers in AAMs, the second is correlated with the oxalic impurities incorporated in the AAMs, and the third is associated with the excess aluminum ions in the membrane.

  2. Ultrafast excited state deactivation of doped porous anodic alumina membranes

    Science.gov (United States)

    Makhal, Abhinandan; Sarkar, Soumik; Pal, Samir Kumar; Yan, Hongdan; Wulferding, Dirk; Cetin, Fatih; Lemmens, Peter

    2012-08-01

    Free-standing, bi-directionally permeable and ultra-thin anodic aluminum oxide (AAO) membranes establish attractive templates (host) for the synthesis of nano-dots and rods of various materials (guest). This is due to their chemical and structural integrity and high periodicity on length scales of 5-150 nm which are often used to host photoactive nano-materials for various device applications including dye-sensitized solar cells. In the present study, AAO membranes are synthesized by using electrochemical methods and a detailed structural characterization using FEG-SEM, XRD and TGA confirms the porosity and purity of the material. Defect-mediated photoluminescence quenching of the porous AAO membrane in the presence of an electron accepting guest organic molecule (benzoquinone) is studied by means of steady-state and picosecond/femtosecond-resolved luminescence measurements. Using time-resolved luminescence transients, we have also revealed light harvesting of complexes of porous alumina impregnated with inorganic quantum dots (Maple Red) or gold nanowires. Both the Förster resonance energy transfer and the nano-surface energy transfer techniques are employed to examine the observed quenching behavior as a function of the characteristic donor-acceptor distances. The experimental results will find their relevance in light harvesting devices based on AAOs combined with other materials involving a decisive energy/charge transfer dynamics.

  3. Ultrafast excited state deactivation of doped porous anodic alumina membranes

    Energy Technology Data Exchange (ETDEWEB)

    Makhal, Abhinandan; Sarkar, Soumik; Pal, Samir Kumar [Department of Chemical, Biological and Macromolecular Sciences, S N Bose National Centre for Basic Sciences, Block JD, Sector III, Salt Lake, Kolkata 700 098 (India); Yan, Hongdan; Wulferding, Dirk; Cetin, Fatih; Lemmens, Peter [Institute for Condensed Matter Physics, TU Braunschweig, Mendelssohnstrasse 3, 38106 Braunschweig (Germany)

    2012-08-03

    Free-standing, bi-directionally permeable and ultra-thin anodic aluminum oxide (AAO) membranes establish attractive templates (host) for the synthesis of nano-dots and rods of various materials (guest). This is due to their chemical and structural integrity and high periodicity on length scales of 5-150 nm which are often used to host photoactive nano-materials for various device applications including dye-sensitized solar cells. In the present study, AAO membranes are synthesized by using electrochemical methods and a detailed structural characterization using FEG-SEM, XRD and TGA confirms the porosity and purity of the material. Defect-mediated photoluminescence quenching of the porous AAO membrane in the presence of an electron accepting guest organic molecule (benzoquinone) is studied by means of steady-state and picosecond/femtosecond-resolved luminescence measurements. Using time-resolved luminescence transients, we have also revealed light harvesting of complexes of porous alumina impregnated with inorganic quantum dots (Maple Red) or gold nanowires. Both the Foerster resonance energy transfer and the nano-surface energy transfer techniques are employed to examine the observed quenching behavior as a function of the characteristic donor-acceptor distances. The experimental results will find their relevance in light harvesting devices based on AAOs combined with other materials involving a decisive energy/charge transfer dynamics. (paper)

  4. Fabrication and Characterization of Single Phase α-Alumina Membranes with Tunable Pore Diameters

    Science.gov (United States)

    Masuda, Tatsuya; Asoh, Hidetaka; Haraguchi, Satoshi; Ono, Sachiko

    2015-01-01

    Nanoporous and single phase α-alumina membranes with pore diameters tunable over a wide range of approximately 60–350 nm were successfully fabricated by optimizing the conditions for anodizing, subsequent detachment, and heat treatment. The pore diameter increased and the cell diameter shrunk upon crystallization to α-alumina by approximately 20% and 3%, respectively, in accordance with the 23% volume shrinkage resulting from the change in density associated with the transformation from the amorphous state to α-alumina. Nevertheless, flat α-alumina membranes, each with a diameter of 25 mm and a thickness of 50 μm, were obtained without thermal deformation. The α-alumina membranes exhibited high chemical resistance in various concentrated acidic and alkaline solutions as well as when exposed to high temperature steam under pressure. The Young’s modulus and hardness of the single phase α-alumina membranes formed by heat treatment at 1250 °C were notably decreased compared to the corresponding amorphous membranes, presumably because of the nodular crystallite structure of the cell walls and the substantial increase in porosity. Furthermore, when used for filtration, the α-alumina membrane exhibited a level of flux higher than that of the commercial ceramic membrane. PMID:28788005

  5. Fabrication and Characterization of Single Phase α-Alumina Membranes with Tunable Pore Diameters

    Directory of Open Access Journals (Sweden)

    Tatsuya Masuda

    2015-03-01

    Full Text Available Nanoporous and single phase α-alumina membranes with pore diameters tunable over a wide range of approximately 60–350 nm were successfully fabricated by optimizing the conditions for anodizing, subsequent detachment, and heat treatment. The pore diameter increased and the cell diameter shrunk upon crystallization to α-alumina by approximately 20% and 3%, respectively, in accordance with the 23% volume shrinkage resulting from the change in density associated with the transformation from the amorphous state to α-alumina. Nevertheless, flat α-alumina membranes, each with a diameter of 25 mm and a thickness of 50 μm, were obtained without thermal deformation. The α-alumina membranes exhibited high chemical resistance in various concentrated acidic and alkaline solutions as well as when exposed to high temperature steam under pressure. The Young’s modulus and hardness of the single phase α-alumina membranes formed by heat treatment at 1250 °C were notably decreased compared to the corresponding amorphous membranes, presumably because of the nodular crystallite structure of the cell walls and the substantial increase in porosity. Furthermore, when used for filtration, the α-alumina membrane exhibited a level of flux higher than that of the commercial ceramic membrane.

  6. Polyethyleneglycol grafting of γ-alumina membranes for solvent resistant nanofiltration

    NARCIS (Netherlands)

    Tanardi, Cheryl; Catana, Romina; Barboiu, Mihai; Ayral, André; Vankelecom, Ivo F.J.; Nijmeijer, Arian; Winnubst, Aloysius J.A.

    2016-01-01

    A method is presented for grafting mesoporous g-alumina (pore size 5 nm), supported on an a-alumina ceramic membrane, with polyethylene glycols (PEG). The grafting performance of g-Al2O3 powders with various PEG grafting agents, having different molecular weights, alkoxy groups, and ureido

  7. Absorption of Ethylene on Membranes Containing Potassium Permanganate Loaded into Alumina-Nanoparticle-Incorporated Alumina/Carbon Nanofibers.

    Science.gov (United States)

    Tirgar, Ashkan; Han, Daewoo; Steckl, Andrew J

    2018-06-06

    Ethylene is a natural aging hormone in plants, and controlling its concentration has long been a subject of research aimed at reducing wastage during packaging, transport, and storage. We report on packaging membranes, produced by electrospinning, that act as efficient carriers for potassium permanganate (PPM), a widely used ethylene oxidant. PPM salt loaded on membranes composed of alumina nanofibers incorporating alumina nanoparticles outperform other absorber systems and oxidize up to 73% of ethylene within 25 min. Membrane absorption of ethylene generated by avocados was totally quenched in 21 h, and a nearly zero ethylene concentration was observed for more than 5 days. By comparison, the control experiments exhibited a concentration of 53% of the initial value after 21 h and 31% on day 5. A high surface area of the alumina nanofiber membranes provides high capacity for ethylene absorption over a long period of time. In combination with other properties, such as planar form, flexibility, ease of handling, and lightweight, these membranes are a highly desirable component of packaging materials engineered to enhance product lifetime.

  8. Synthesis and separation properties of an α-alumina-supported high-silica MEL membrane

    NARCIS (Netherlands)

    Kosinov, N.; Hensen, E.J.M.

    2013-01-01

    A thin high-silica MEL membrane was synthesized on a porous a-alumina hollow fiber support by a secondary growth approach. The membrane quality was evaluated by permporometry, single-gas permeation and butane isomer separation. Comparison of the pervaporation performance of MEL membranes with a MFI

  9. Synthesis and characterization of alumina application in support of zeolite membrane

    International Nuclear Information System (INIS)

    Barbosa, A.S.; Rodrigues, M.G.F.

    2012-01-01

    Much interest has been aroused in process applications using zeolite membrane. The physicochemical properties of the support have a strong effect on the quality of zeolite membrane. This work is to synthesize and characterize alumina for use as a support for zeolite membrane. In this work was synthesized α-alumina: 40% alumina, 0.2% for PABA, 0.5% oleic acid and 59.3% ethyl alcohol. The mixture was ground in ball mill and placed in an oven for 24 hours at 60 °C, allowed to stand for 24h. The pressing was performed with 4 tons. The pressed material was subjected to sintering at 1400 °C/hour. The samples were characterized by EDX, XRD and SEM. The results for the media by XRD showed that they are crystalline and pure. By EDX was observed that the supports consist essentially of alumina. (author)

  10. Development of hydrophobic clay–alumina based capillary membrane for desalination of brine by membrane distillation

    Directory of Open Access Journals (Sweden)

    Rakhi Das

    2016-09-01

    Full Text Available Clay–alumina compositions of 0, 20, 40 and 55 weight percent (wt% clay and rest alumina were maintained in porous support preparation by extrusion followed by sintering at 1300 °C for 2.5 h to obtain 3 mm/2 mm (outer diameter/inner diameter capillary. 1H,1H,2H,2H-perfluorodecyltriethoxysilane (97% (C8 was used to modify the capillary surface of all compositions without any intermediate membrane layer to impart hydrophobic characteristics and compared in terms of contact angle produced by the capillaries with water and liquid entry pressure (LEPw. FTIR analysis showed that the hydrophilic surface of the capillary membranes was efficiently modified by the proposed grafting method. Capillary with 55 wt% clay produced a pore size of 1.43 micron and was considered as an ideal candidate for grafting with C8 polymer to impart surface hydrophobicity. The contact angle and LEPw value obtained for this modified membrane (C-55-M were 145° and 1 bar, respectively. The modified capillary membrane was applied for desalination of brine by air gap membrane distillation (AGMD at a feed pressure of 0.85 bar. Maximum flux obtained for C-55-M membrane was 98.66 L/m2 day at a temperature difference of 60 °C with salt rejection of 99.96%. Mass transfer coefficient of C-55-M was 16 × 10−3 mm/s at feed temperature of 70 °C.

  11. Differential Pair Distribution Function Study of the Structure of Arsenate Adsorbed on Nanocrystalline [gamma]-Alumina

    Energy Technology Data Exchange (ETDEWEB)

    Li, Wei; Harrington, Richard; Tang, Yuanzhi; Kubicki, James D.; Aryanpour, Masoud; Reeder, Richard J.; Parise, John B.; Phillips, Brian L. (SBU); (Penn)

    2012-03-15

    Structural information is important for understanding surface adsorption mechanisms of contaminants on metal (hydr)oxides. In this work, a novel technique was employed to study the interfacial structure of arsenate oxyanions adsorbed on {gamma}-alumina nanoparticles, namely, differential pair distribution function (d-PDF) analysis of synchrotron X-ray total scattering. The d-PDF is the difference of properly normalized PDFs obtained for samples with and without arsenate adsorbed, otherwise identically prepared. The real space pattern contains information on atomic pair correlations between adsorbed arsenate and the atoms on {gamma}-alumina surface (Al, O, etc.). PDF results on the arsenate adsorption sample on {gamma}-alumina prepared at 1 mM As concentration and pH 5 revealed two peaks at 1.66 {angstrom} and 3.09 {angstrom}, corresponding to As-O and As-Al atomic pair correlations. This observation is consistent with those measured by extended X-ray absorption fine structure (EXAFS) spectroscopy, which suggests a first shell of As-O at 1.69 {+-} 0.01 {angstrom} with a coordination number of 4 and a second shell of As-Al at 3.13 {+-} 0.04 {angstrom} with a coordination number of 2. These results are in agreement with a bidentate binuclear coordination environment to the octahedral Al of {gamma}-alumina as predicted by density functional theory (DFT) calculation.

  12. Modeling water flux and salt rejection of mesoporous γ-alumina and microporous organosilica membranes

    NARCIS (Netherlands)

    Farsi, A.; Boffa, V.; Qureshi, H.F.; Nijmeijer, Arian; Winnubst, Aloysius J.A.; Lykkegaard Christensen, M.

    2014-01-01

    The water and ion transport through a mesoporous γ-alumina membrane and a microporous organosilica membrane was simulated using the extended Nernst Planck equation combined with models for Donnan, steric and dielectric interfacial exclusion mechanisms. Due to the surface charge within the pore, the

  13. ZIF-8 Membranes with Improved Reproducibility Fabricated from Sputter-Coated ZnO/Alumina Supports

    KAUST Repository

    Yu, Jian; Pan, Yichang; Wang, Chongqing; Lai, Zhiping

    2015-01-01

    for reproducible fabrication of high-quality membranes. In this study, high-quality ZIF-8 membranes were prepared through hydrothermal synthesis under the partial self-conversion of sputter-coated ZnO layer on porous α-alumina supports. The reproducibility

  14. Superior thermal conductivity of transparent polymer nanocomposites with a crystallized alumina membrane

    OpenAIRE

    Md. Poostforush; H. Azizi

    2014-01-01

    The properties of novel thermoconductive and optically transparent nanocomposites have been reported. The composites were prepared by the impregnation of thermoset resin into crystallized anodic aluminum oxide (AAO). Crystallized AAO synthesized by annealing amorphous AAO membrane at 1200°C. Although through-plane thermal conductivity of nanocomposites improved up to 1.13 W•m–1•K–1 (39 vol% alumina) but their transparency was preserved (Tλ550 nm ~ 72%). Integrated annealed alumina phase, low ...

  15. Preparation and characterization of multilayer mesoporous γ-alumina membrane obtained via sol-gel using new precursors

    Directory of Open Access Journals (Sweden)

    Tafrishi R.

    2015-12-01

    Full Text Available In this paper, a mesoporous γ-alumina membrane coated on a macroporous α-alumina support via sol-gel method has been reported. A crack-free γ-alumina membrane was obtained by adding PVA to the alumina solution and optimum parameters of roughness, temperature and porosity were achieved. The support was dip-coated in different solutions using two new different solvents with different particle size distributions. Using these two solvents led to the uniform distribution of pore size in the final membrane. The alumina sols showed particle size distributions in the range of 20 to 55 nm which was measured by a DLS Zeta Sizer. X-ray diffraction technique, atomic force microscopy and scanning electron microscopy were used to characterize the membrane layer. XRD and DTA data for the γ-alumina membrane showed its thermal stability up to around 600 °C. The thickness of the mesoporous γ-alumina membrane was about 4 μm with 16 nm of surface roughness and 5 nm pore size. The resultant crack-free mesoporous membrane shows that the membrane preparation procedure was optimum. In this work, it has been investigated the performance of γ-alumina membranes for single gas permeation and separation of binary gas mixtures.

  16. Enhanced gas separation factors of microporous polymer constrained in the channels of anodic alumina membranes.

    Science.gov (United States)

    Chernova, Ekaterina; Petukhov, Dmitrii; Boytsova, Olga; Alentiev, Alexander; Budd, Peter; Yampolskii, Yuri; Eliseev, Andrei

    2016-08-08

    New composite membranes based on porous anodic alumina films and polymer of intrinsic microporosity (PIM-1) have been prepared using a spin-coating technique. According to scanning electron microscopy, partial penetration of polymer into the pores of alumina supports takes place giving rise to selective polymeric layers with fiber-like microstructure. Geometric confinement of rigid PIM-1 in the channels of anodic alumina causes reduction of small-scale mobility in polymeric chains. As a result, transport of permanent gases, such as CH4, becomes significantly hindered across composite membranes. Contrary, the transport of condensable gases (CO2, С4H10), did not significantly suffer from the confinement due to high solubility in the polymer matrix. This strategy enables enhancement of selectivity towards CO2 and C4H10 without significant loss of the membrane performance and seems to be prospective for drain and sweetening of natural gas.

  17. Superior thermal conductivity of transparent polymer nanocomposites with a crystallized alumina membrane

    Directory of Open Access Journals (Sweden)

    Md. Poostforush

    2014-04-01

    Full Text Available The properties of novel thermoconductive and optically transparent nanocomposites have been reported. The composites were prepared by the impregnation of thermoset resin into crystallized anodic aluminum oxide (AAO. Crystallized AAO synthesized by annealing amorphous AAO membrane at 1200°C. Although through-plane thermal conductivity of nanocomposites improved up to 1.13 W•m–1•K–1 (39 vol% alumina but their transparency was preserved (Tλ550 nm ~ 72%. Integrated annealed alumina phase, low refractive index mismatch between resin and alumina and formation of nano-optical fibers through the membrane resulted in such marvel combination. This report shows a great potential of these types of nanocomposites in ‘heat management’ of lightening devices.

  18. Continuous wine making by gamma-alumina-supported biocatalyst: quality of the wine and distillates.

    Science.gov (United States)

    Loukatos, P; Kiaris, M; Ligas, I; Bourgos, G; Kanellaki, M; Komaitis, M; Koutinas, A A

    2000-10-01

    The main objective of the present work was the removal of aluminum from wines produced by gamma-alumina-supported yeast cells. Reagents such as Na2CO3, NH4OH, albumin, and Ca(OH)2 were used. Calcium in the presence of albumin was effective, whereas other reagents were not so effective. Because of the improved aroma and taste of distillates produced by gamma-alumina-supported biocatalyst, volatile byproducts of distillates were analyzed. They were also assessed by sensory tests. Methanol, acetaldehyde, ethyl acetate, propanol-1, isobutyl alcohol, and amyl alcohols were determined in distillates. It was noted that the amounts of higher alcohols and amyl alcohols decreased as the temperature of fermentation dropped, leading to a product of improved quality and reduced toxicity.

  19. Membranes obtained from alumina from separation water/oil; Membranas obtidas a partir do residuo de alumina para separacao de agua/oleo

    Energy Technology Data Exchange (ETDEWEB)

    Rosas Neto, M.I.; Lira, H.L; Guimaraes, I.O; Franca, K.B., E-mail: moisesnetu@gmail.com [Universidade Federal de Campina Grande (UFCG), PB, (Brazil)

    2016-07-01

    This study aims to evaluate by flow test emulsion water/oil a membrane obtained from a crude residue of the alumina industry and see if this membrane is able to filter this emulsion within the limits specified by CONAMA. In this work, tubular membranes composed of the alumina and the residue bentonite clay were produced by extrusion and were sintered at 900, 1000 and 1100 ° C. tangential flow tests were conducted with deionized water and subsequently with an emulsion of water / oil, all done with a pressure of 1.5 bar. The results showed that membranes produced from the crude residue the alumina industry were quite efficient the emulsion's oil removal, reducing the concentration of about 100 ppm in the feed, to below 5ppm and flow rates of around 30L/h.m{sup 2}. (author)

  20. Adsorptive removal of phenolic compounds using cellulose acetate phthalate–alumina nanoparticle mixed matrix membrane

    Energy Technology Data Exchange (ETDEWEB)

    Mukherjee, Raka; De, Sirshendu, E-mail: sde@che.iitkgp.ernet.in

    2014-01-30

    Highlights: • Composite membrane of cellulose–acetate–phthalate and alumina nanoparticle is cast. • Surface charge of the membrane changes with nanoparticle concentration and pH. • Separation of phenolic compounds occurs due to adsorption. • The removal efficiency is maximum for 20% nanoparticle with 91% removal of catechol. • Transmembrane pressure drop has negligible effect on solute separation. -- Abstract: Mixed matrix membranes (MMMs) were prepared using alumina nanoparticles and cellulose acetate phthalate (CAP) by varying concentration of nanoparticles in the range of 10 to 25 wt%. The membranes were characterized by scanning electron micrograph, porosity, permeability, molecular weight cut off, contact angle, surface zeta potential, mechanical strength. Addition of nanoparticles increased the porosity, permeability of the membrane up to 20 wt% of alumina. pH at point of zero charge of the membrane was 5.4. Zeta potential of the membrane became more negative up to 20 wt% of nanoparticles. Adsorption of phenolic derivatives, catechol, paranitrophenol, phenol, orthochloro phenol, metanitrophenol, by MMMs were investigated. Variation of rejection and permeate flux profiles were studied for different solutes as a function of various operating conditions, namely, solution pH, solute concentration in feed and transmembrane pressure drop. Difference in rejection of phenolic derivatives is consequence of interplay of surface charge and adsorption by alumina. Adsorption isotherm was fitted for different solutes and effects of pH were investigated. Catechol showed the maximum rejection 91% at solution pH 9. Addition of electrolyte reduced the rejection of solutes. Transmembrane pressure drop has insignificant effects on solute rejection. Competitive adsorption reduced the rejection of individual solute.

  1. Comparative study between yeasts immobilized on alumina beads and on membranes prepared by two routes

    Directory of Open Access Journals (Sweden)

    Kiyohara Pedro K.

    2003-01-01

    Full Text Available Alumina channeled beads and rough surface membranes prepared from aqueous sols of fibrillar pseudoboehmite are able to immobilize yeasts for ethanol fermentation of sugar solutions. This paper describes comparative results of assays carried out with yeasts immobilized onto alpha-alumina beads and membranes prepared under two different conditions of processing and firing. The fermentation tests evaluated by the decrease of fermentable sugars, referred as Brix degrees per hour, indicated that the yeasts immobilized on beads had similar performance, probably because their surfaces, even being morphologically different, presented the same value of open porosity. One type of membrane (asymmetrical; precursor: pseudoboehmite; firing temperature 1,150ºC; crystal structure; alpha-alumina had better performance than the other type (asymmetrical; precursor: fibrillar pseudoboehmite plus aluminum hydroxiacetate mixture; 1,150ºC; alpha-alumina because the yeast cells entered into their porous interior through the surface slits, were immobilized and their growth was easier than on the external surface.

  2. Ultra-thin alumina and silicon nitride MEMS fabricated membranes for the electron multiplication

    Science.gov (United States)

    Prodanović, V.; Chan, H. W.; Graaf, H. V. D.; Sarro, P. M.

    2018-04-01

    In this paper we demonstrate the fabrication of large arrays of ultrathin freestanding membranes (tynodes) for application in a timed photon counter (TiPC), a novel photomultiplier for single electron detection. Low pressure chemical vapour deposited silicon nitride (Si x N y ) and atomic layer deposited alumina (Al2O3) with thicknesses down to only 5 nm are employed for the membrane fabrication. Detailed characterization of structural, mechanical and chemical properties of the utilized films is carried out for different process conditions and thicknesses. Furthermore, the performance of the tynodes is investigated in terms of secondary electron emission, a fundamental attribute that determines their applicability in TiPC. Studied features and presented fabrication methods may be of interest for other MEMS application of alumina and silicon nitride as well, in particular where strong ultra-thin membranes are required.

  3. Performance Evaluations of Ion Exchanged Zeolite Membranes on Alumina Supports

    Energy Technology Data Exchange (ETDEWEB)

    Bhave, Ramesh R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Jubin, Robert Thomas [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Spencer, Barry B. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Nair, Sankar [Georgia Inst. of Technology, Atlanta, GA (United States)

    2017-08-27

    This report describes the synthesis and evaluation of molecular sieve zeolite membranes to separate and concentrate tritiated water (HTO) from dilute HTO-bearing aqueous streams. In the first phase of this effort, several monovalent and divalent cation-exchanged silico alumino phosphate (SAPO-34) molecular sieve zeolite membranes were synthesized on disk supports and characterized with gas and vapor permeation measurements. In the second phase, Linde Type A (LTA) zeolite membranes were synthesized in disk and tubular supports. The pervaporation process performance was evaluated for the separation and concentration of tritiated water.

  4. Support influence on the properties of the alumina ceramic membranes

    International Nuclear Information System (INIS)

    Clar, C.; Scian, A.N.; Aglietti, E.F.

    2003-01-01

    The ceramic substrates used as supports for the formation of a top layer membrane must meet several requirements.Some of them are: have an average pore size and a suitable surface rugosity to obtain a homogenous top layer preventing the penetration of the membrane precursor particles into the support pores.This work analyzes the performance of the three α-Al 2 O 3 supports, with different average pore sizes and surface textures, for the formation of a membrane top layer by the dipcoating technique from colloids in suspension of aluminum basic acetate and later thermal treatment at 1000degC.The pore size distribution of the supports, the support-membrane systems and the top layer membrane was obtained by the mercury intrusion porosimetry technique.The microstructural differences of the supports and the top layer thickness were observed by MEB.It could be observed that for numerous deposits the membrane layer pore size obtained is independent on the support used and that the thickness of the last layer is lower for the greater pore size supports.The possibility of an intermediate layer between the support and the top layer was considered in every case

  5. Alumina Coating To Realize Desired Pore Characteristics Of Sintered Diatomite Membrane

    Directory of Open Access Journals (Sweden)

    Ha J.-H.

    2015-06-01

    Full Text Available Porous ceramic membranes prepared from natural materials such as diatomite, have lately attracted great interest in industrial applications due to their cost-effectiveness. In this study, we attempted to prepare an alumina coating to be deposited over a sintered diatomite-kaolin composite support layer in order to reduce the largest pore size to below 0.4 μm; such a coating could be potentially used in water treatment applications for bacterial removal.

  6. ZIF-8 Membranes with Improved Reproducibility Fabricated from Sputter-Coated ZnO/Alumina Supports

    KAUST Repository

    Yu, Jian

    2015-11-10

    Zeolitic imidazolate framework-8 (ZIF-8) membrane has shown great potential for propylene/propane separation based on molecular sieving mechanism. Although diverse synthesis strategies were applied to prepare ZIF-8 membranes, it is still a challenge for reproducible fabrication of high-quality membranes. In this study, high-quality ZIF-8 membranes were prepared through hydrothermal synthesis under the partial self-conversion of sputter-coated ZnO layer on porous α-alumina supports. The reproducibility was significantly improved, compared with that from sol-gel coated ZnO layer, due to the highly controllable sputtering deposition of ZnO precursor. The relationship between the quality of as-synthesized membrane and amount of deposited ZnO was also determined. The effect of pressure drop in C3H6/C3H8 separation on separating performance was also examined.

  7. Pore surface fractal analysis of palladium-alumina ceramic membrane using Frenkel-Halsey-Hill (FHH) model.

    Science.gov (United States)

    Ahmad, A L; Mustafa, N N N

    2006-09-15

    The alumina ceramic membrane has been modified by the addition of palladium in order to improve the H(2) permeability and selectivity. Palladium-alumina ceramic membrane was prepared via a sol-gel method and subjected to thermal treatment in the temperature range 500-1100 degrees C. Fractal analysis from nitrogen adsorption isotherm is used to study the pore surface roughness of palladium-alumina ceramic membrane with different chemical composition (nitric acid, PVA and palladium) and calcinations process in terms of surface fractal dimension, D. Frenkel-Halsey-Hill (FHH) model was used to determine the D value of palladium-alumina membrane. Following FHH model, the D value of palladium-alumina membrane increased as the calcinations temperature increased from 500 to 700 degrees C but decreased after calcined at 900 and 1100 degrees C. With increasing palladium concentration from 0.5 g Pd/100 ml H(2)O to 2 g Pd/100 ml H(2)O, D value of membrane decreased, indicating to the smoother surface. Addition of higher amount of PVA and palladium reduced the surface fractal of the membrane due to the heterogeneous distribution of pores. However, the D value increased when nitric acid concentration was increased from 1 to 15 M. The effect of calcinations temperature, PVA ratio, palladium and acid concentration on membrane surface area, pore size and pore distribution also studied.

  8. Relation Between Acid and Catalytic Properties of Chlorinated Gamma-Alumina. a 31p Mas Nmr and Ftir Investigation

    Directory of Open Access Journals (Sweden)

    Guillaume D.

    1999-07-01

    Full Text Available In this paper, we have studied the effect of chlorine on the surface properties of gamma-alumina, especially on their acid properties. The use of FTIR spectroscopy and 31P MAS NMR of adsorbed trimethylphosphine allows to propose a chlorination mechanism. To correlate the surface properties of these chlorinated gamma-alumina with their catalytic properties, we have used a model reaction, the cracking of n-heptane under reforming conditions. The analysis of the correlation between acid properties determined by 31P MAS NMR and the catalytic results (in terms of activities and selectivities allows to identify which sites are involved in the cracking reaction.

  9. Ion Transport in Organic Electrolyte Solution through the Pore Channels of Anodic Nanoporous Alumina Membranes

    International Nuclear Information System (INIS)

    Fukutsuka, Tomokazu; Koyamada, Kohei; Maruyama, Shohei; Miyazaki, Kohei; Abe, Takeshi

    2016-01-01

    Highlights: • Ion transport in organic electrolyte solution in macro- and meso-pores was focused. • Anodic nanoporous alumina membrane was used as a porous material. • The specific ion conductivities drastically decreased in macro- and meso-pores. - Abstract: For the development of high energy density lithium-ion batteries with the high rate performance, the enhancement of the ion transport in the electrolyte solutions impregnated in the porous electrodes is a key. To study the ion transport in porous electrodes, anodic nanoporous alumina (APA) self-standing membranes with macro- or meso-pores were used as model porous materials. These membranes had nearly spherical pore channels of discrete 20–68 nm in diameters. By using the geometric shape of the pores, we attempted to evaluate the specific ion conductivities of the organic electrolyte solution dissolving lithium salt simply. AC impedance spectroscopy measurement of a four-electrode cell with membranes showed one depressed semi-circle in the Nyquist plots and this semi-circle can be assigned as the ion transport resistance in the pores. The specific ion conductivities evaluated from the ion transport resistances and the geometric parameters showed very small values, even in the macro-pores, as compared with that of the bulk electrolyte solution.

  10. Morphological, Chemical Surface, and Diffusive Transport Characterizations of a Nanoporous Alumina Membrane

    Directory of Open Access Journals (Sweden)

    María I. Vázquez

    2015-12-01

    Full Text Available Synthesis of a nanoporous alumina membrane (NPAM by the two-step anodization method and its morphological and chemical surface characterization by analyzing Scanning Electron Microscopy (SEM micrographs and X-Ray Photoelectron Spectroscopy (XPS spectra is reported. Influence of electrical and diffusive effects on the NaCl transport across the membrane nanopores is determined from salt diffusion measurements performed with a wide range of NaCl concentrations, which allows the estimation of characteristic electrochemical membrane parameters such as the NaCl diffusion coefficient and the concentration of fixed charges in the membrane, by using an appropriated model and the membrane geometrical parameters (porosity and pore length. These results indicate a reduction of ~70% in the value of the NaCl diffusion coefficient through the membrane pores with respect to solution. The transport number of ions in the membrane pores (Na+ and Cl−, respectively were determined from concentration potential measurements, and the effect of concentration-polarization at the membrane surfaces was also considered by comparing concentration potential values obtained with stirred solutions (550 rpm and without stirring. From both kinds of results, a value higher than 0.05 M NaCl for the feed solution seems to be necessary to neglect the contribution of electrical interactions in the diffusive transport.

  11. Enhancing the platinum atomic layer deposition infiltration depth inside anodic alumina nanoporous membrane

    Energy Technology Data Exchange (ETDEWEB)

    Vaish, Amit, E-mail: anv@udel.edu; Krueger, Susan; Dimitriou, Michael; Majkrzak, Charles [National Institute of Standards and Technology (NIST) Center for Neutron Research, Gaithersburg, MD 20899-8313 (United States); Vanderah, David J. [Institute for Bioscience and Biotechnology Research, NIST, Rockville, Maryland 20850 (United States); Chen, Lei, E-mail: lei.chen@nist.gov [NIST Center for Nanoscale Science and Technology, Gaithersburg, Maryland 20899-8313 (United States); Gawrisch, Klaus [Laboratory of Membrane Biochemistry and Biophysics, National Institute on Alcohol Abuse and Alcoholism, National Institutes of Health, Bethesda, Maryland 20892 (United States)

    2015-01-15

    Nanoporous platinum membranes can be straightforwardly fabricated by forming a Pt coating inside the nanopores of anodic alumina membranes (AAO) using atomic layer deposition (ALD). However, the high-aspect-ratio of AAO makes Pt ALD very challenging. By tuning the process deposition temperature and precursor exposure time, enhanced infiltration depth along with conformal coating was achieved for Pt ALD inside the AAO templates. Cross-sectional scanning electron microscopy/energy dispersive x-ray spectroscopy and small angle neutron scattering were employed to analyze the Pt coverage and thickness inside the AAO nanopores. Additionally, one application of platinum-coated membrane was demonstrated by creating a high-density protein-functionalized interface.

  12. Mixed Matrix Carbon Molecular Sieve and Alumina (CMS-Al2O3) Membranes.

    Science.gov (United States)

    Song, Yingjun; Wang, David K; Birkett, Greg; Martens, Wayde; Duke, Mikel C; Smart, Simon; Diniz da Costa, João C

    2016-07-29

    This work shows mixed matrix inorganic membranes prepared by the vacuum-assisted impregnation method, where phenolic resin precursors filled the pore of α-alumina substrates. Upon carbonisation, the phenolic resin decomposed into several fragments derived from the backbone of the resin matrix. The final stages of decomposition (>650 °C) led to a formation of carbon molecular sieve (CMS) structures, reaching the lowest average pore sizes of ~5 Å at carbonisation temperatures of 700 °C. The combination of vacuum-assisted impregnation and carbonisation led to the formation of mixed matrix of CMS and α-alumina particles (CMS-Al2O3) in a single membrane. These membranes were tested for pervaporative desalination and gave very high water fluxes of up to 25 kg m(-2) h(-1) for seawater (NaCl 3.5 wt%) at 75 °C. Salt rejection was also very high varying between 93-99% depending on temperature and feed salt concentration. Interestingly, the water fluxes remained almost constant and were not affected as feed salt concentration increased from 0.3, 1 and 3.5 wt%.

  13. Porosity determination of alumina and boron carbide ceramic samples by gamma ray transmission

    International Nuclear Information System (INIS)

    Moreira, Anderson Camargo; Appoloni, Carlos Roberto

    2009-01-01

    The aim of this work is to apply the Gamma Ray Transmission (GRT), a non destructive technique, for structural characterization of ceramic samples. With this technique, the porosity of Alumina (Al 2 O 3 ) and Boron Carbide (B 4 C) ceramic samples, in tablet format, was determined. The equipment employed is constituted by a 241 Am gamma ray source (59.6 keV and 100mCi), a 2''x2'' diameter NaI (Tl) scintillation detector coupled to a standard gamma ray transmission electronic and a micrometric and automated table for sample movement. The porosity profile of the samples shows a homogeneous porosity distribution, within the spatial resolution of the employed transmission system. The mean porosity determined for Al 2 O 3 and B 4 C were 17.8±1.3% and 3.87±0.43%, respectively. A statistical treatment of these results was performed and showed that the mean porosity values determinate by the GRT are the same as those supplied by the manufacturer. (author)

  14. Grazing incidence x-ray diffraction analysis of zeolite NaA membranes on porous alumina tubes.

    Science.gov (United States)

    Kyotani, Tomohiro

    2006-07-01

    Zeolite NaA-type membranes hydrothermally synthesized on porous alumina tubes, for dehydration process, were characterized by grazing incidence 2 theta scan X-ray diffraction analysis (GIXRD). The fine structure of the membrane was studied fractionally for surface layer and for materials embedded in the porous alumina tube. The thickness of the surface layer on the porous alumina tube in the membranes used in this study was approximately 2-3 microm as determined from transmission electron microscopy with focused ion beam thin-layer specimen preparation technique (FIB-TEM). To discuss the effects of the membrane surface morphology on the GIXRD measurements, CaA-type membrane prepared by ion exchange from the NaA-type membrane and surface-damaged NaA-type membrane prepared by water leaching were also studied. For the original NaA-type membrane, 2 theta scan GIXRD patterns could be clearly measured at X-ray incidence angles (alpha) ranging from 0.1 to 2.0 deg in increments of 0.1 deg. The surface layers of the 2 - 3 microm on the porous alumina tube correspond to the alpha values up to ca. 0.2 deg. For the CaA-type and the surface-damaged NaA-type membranes, however, diffraction patterns from the surface layer could not be successfully detected and the others were somewhat broad. For all the three samples, diffraction intensities of both zeolite and alumina increased with depth (X-ray incidence angle, alpha) in the porous alumina tube region. The depth profile analysis of the membranes based on the GIXRD first revealed that amount of zeolite crystal embedded in the porous alumina tube is much larger than that in the surface layer. Thus, the 2 theta scan GIXRD is a useful method to study zeolite crystal growth mechanism around (both inside and outside) the porous alumina support during hydrothermal synthesis and to study water permeation behavior in the dehydration process.

  15. Step-by-step seeding procedure for preparing HKUST-1 membrane on porous α-alumina support.

    Science.gov (United States)

    Nan, Jiangpu; Dong, Xueliang; Wang, Wenjin; Jin, Wanqin; Xu, Nanping

    2011-04-19

    Metal-organic framework (MOF) membranes have attracted considerable attention because of their striking advantages in small-molecule separation. The preparation of an integrated MOF membrane is still a major challenge. Depositing a uniform seed layer on a support for secondary growth is a main route to obtaining an integrated MOF membrane. A novel seeding method to prepare HKUST-1 (known as Cu(3)(btc)(2)) membranes on porous α-alumina supports is reported. The in situ production of the seed layer was realized in step-by-step fashion via the coordination of H(3)btc and Cu(2+) on an α-alumina support. The formation process of the seed layer was observed by ultraviolet-visible absorption spectroscopy and atomic force microscopy. An integrated HKUST-1 membrane could be synthesized by the secondary hydrothermal growth on the seeded support. The gas permeation performance of the membrane was evaluated. © 2011 American Chemical Society

  16. Hierarchical ultrathin alumina membrane for the fabrication of unique nanodot arrays

    International Nuclear Information System (INIS)

    Wang, Yuyang; Wang, Yi; Wang, Hailong; Wang, Xinnan; Cong, Ming; Xu, Weiqing; Xu, Shuping

    2016-01-01

    Ultrathin alumina membranes (UTAMs) as evaporation masks have been a powerful tool for the fabrication of high-density nanodot arrays and have received much attention in magnetic memory devices, photovoltaics, and nanoplasmonics. In this paper, we report the fabrication of a hierarchical ultrathin alumina membrane (HUTAM) with highly ordered submicro/nanoscale channels and its application as an evaporation mask for the realization of unique non-hexagonal nanodot arrays dependent on the geometrical features of the HUTAM. This is the first report of a UTAM with a hierarchical geometry, breaking the stereotype that only limited sets of nanopatterns can be realized using the UTAM method (with typical inter-pore distance of 100 nm). The fabrication of a HUTAM is discussed in detail. An improved, longer wet etching time than previously reported is found to effectively remove the barrier layer and widen the pores of a HUTAM. A growth sustainability issue brought about by pre-patterning is discussed. Spectral comparison was made to distinguish the UTAM nanodots and HUTAM nanodots. Our results can be an inspiration for more sophisticated applications of pre-patterned anodized aluminum oxide in photocatalysis, photovoltaics, and nanoplasmonics. (paper)

  17. YSZ-Reinforced Alumina Multi-Channel Capillary Membranes for Micro-Filtration.

    Science.gov (United States)

    Wang, Bo; Lee, Melanie; Li, Kang

    2015-12-30

    The combined phase-inversion and sintering method not only produces ceramic hollow fibre membranes with much lower fabrication costs than conventional methods, but these membranes can also be designed to have greatly reduced transport resistances for filtration processes. The bottleneck of this technique is the weak mechanical property of the fibres, due to the small dimensions and the brittle nature of the ceramic materials. In this study, yttrium stabilised zirconia (YSZ) reinforced alumina seven-channel capillary microfiltration membranes were prepared with a pore size of ~230 nm and their mechanical property and permeation characteristics were studied. It is found that the addition of YSZ can effectively enhance the mechanical property of the membrane and also increase pure water permeation flux. The Al₂O₃-YSZ seven-channel capillary membranes could reach a fracture load of 23.4 N and a bending extension of 0.54 mm when being tested with a 6 cm span, to meet the requirements for most industrial microfiltration applications.

  18. Quaternized poly(vinyl alcohol)/alumina composite polymer membranes for alkaline direct methanol fuel cells

    Science.gov (United States)

    Yang, Chun-Chen; Chiu, Shwu-Jer; Chien, Wen-Chen; Chiu, Sheng-Shin

    The quaternized poly(vinyl alcohol)/alumina (designated as QPVA/Al 2O 3) nanocomposite polymer membrane was prepared by a solution casting method. The characteristic properties of the QPVA/Al 2O 3 nanocomposite polymer membranes were investigated using thermal gravimetric analysis (TGA), scanning electron microscopy (SEM), dynamic mechanical analysis (DMA), micro-Raman spectroscopy, and AC impedance method. Alkaline direct methanol fuel cell (ADMFC) comprised of the QPVA/Al 2O 3 nanocomposite polymer membrane were assembled and examined. Experimental results indicate that the DMFC employing a cheap non-perfluorinated (QPVA/Al 2O 3) nanocomposite polymer membrane shows excellent electrochemical performances. The peak power densities of the DMFC with 4 M KOH + 1 M CH 3OH, 2 M CH 3OH, and 4 M CH 3OH solutions are 28.33, 32.40, and 36.15 mW cm -2, respectively, at room temperature and in ambient air. The QPVA/Al 2O 3 nanocomposite polymer membranes constitute a viable candidate for applications on alkaline DMFC.

  19. YSZ-Reinforced Alumina Multi-Channel Capillary Membranes for Micro-Filtration

    Directory of Open Access Journals (Sweden)

    Bo Wang

    2015-12-01

    Full Text Available The combined phase-inversion and sintering method not only produces ceramic hollow fibre membranes with much lower fabrication costs than conventional methods, but these membranes can also be designed to have greatly reduced transport resistances for filtration processes. The bottleneck of this technique is the weak mechanical property of the fibres, due to the small dimensions and the brittle nature of the ceramic materials. In this study, yttrium stabilised zirconia (YSZ reinforced alumina seven-channel capillary microfiltration membranes were prepared with a pore size of ~230 nm and their mechanical property and permeation characteristics were studied. It is found that the addition of YSZ can effectively enhance the mechanical property of the membrane and also increase pure water permeation flux. The Al2O3-YSZ seven-channel capillary membranes could reach a fracture load of 23.4 N and a bending extension of 0.54 mm when being tested with a 6 cm span, to meet the requirements for most industrial microfiltration applications.

  20. Morphology of one-time coated palladium-alumina composite membrane prepared by sol-gel process and electroless plating technique

    Science.gov (United States)

    Sari, R.; Dewi, R.; Pardi; Hakim, L.; Diana, S.

    2018-03-01

    Palladium coated porous alumina ceramic membrane tube was obtained using a combination of sol-gel process and electroless plating technique. The thickness, structure and composition of palladium-alumina composite membrane were analyzed by transmission electron microscopy (TEM), scanning electron microscopy (SEM), energy-dispersive X-ray (EDX), and atomic force microscopy (AFM). Palladium particle size was 6.18 to 7.64 nm. Palladium membrane with thickness of approximately 301.5 to 815.1 nm was formed at the outer surface of the alumina layer. EDX data confirmed the formation of palladium-alumina membrane containing 45% of palladium. From this research it shows the combination of sol-gel process and electroless plating technique with one-time coating can produce a homogeneous and smoother palladium nano layer film on alumina substrate.

  1. Formation and characterization of nanotubes of La(OH)3 obtained using porous alumina membranes

    International Nuclear Information System (INIS)

    Gonzalez-Rovira, L; Sanchez-Amaya, J M; Botana, F J; Lopez-Haro, M; Hungria, A B; Boukha, Z; Bernal, S

    2008-01-01

    An electrodeposition process is used to synthesize nanotubes of a lanthanum-containing phase, employing porous alumina membranes as templates. This method should lead to the formation of La(OH) 3 nanowires, according to the previous results presented by Bocchetta et al (2007 Electrochem. Commun. 9 683-8), which can be decomposed to La 2 O 3 , as the latter shows more interest for different applications. The results obtained by means of different electron microscopy techniques indicate that this method leads to the formation of nanotubes of about 200 nm in diameter and 30-40 μm in length, instead of the nanowires proposed in the literature. Additionally, the chemical characterization demonstrates that the material synthesized is composed of lanthanum hydroxycarbonate. The presence of carbonates is found to be crucial in determining the conditions for the preparation of La 2 O 3 from the nanotubes here obtained.

  2. Formation and characterization of nanotubes of La(OH)3 obtained using porous alumina membranes

    Science.gov (United States)

    González-Rovira, L.; Sánchez-Amaya, J. M.; López-Haro, M.; Hungria, A. B.; Boukha, Z.; Bernal, S.; Botana, F. J.

    2008-12-01

    An electrodeposition process is used to synthesize nanotubes of a lanthanum-containing phase, employing porous alumina membranes as templates. This method should lead to the formation of La(OH)3 nanowires, according to the previous results presented by Bocchetta et al (2007 Electrochem. Commun. 9 683-8), which can be decomposed to La2O3, as the latter shows more interest for different applications. The results obtained by means of different electron microscopy techniques indicate that this method leads to the formation of nanotubes of about 200 nm in diameter and 30-40 µm in length, instead of the nanowires proposed in the literature. Additionally, the chemical characterization demonstrates that the material synthesized is composed of lanthanum hydroxycarbonate. The presence of carbonates is found to be crucial in determining the conditions for the preparation of La2O3 from the nanotubes here obtained.

  3. Ultrafiltro de alumina Alumina ultrafilter

    Directory of Open Access Journals (Sweden)

    M. F. de Souza

    1999-06-01

    Full Text Available Membranas de alumina AKP-50 foram preparadas sobre um substrato de alumina APC-SG de alta resistência mecânica. As membranas foram sinterizadas a 1000 °C e possuem uma distribuição estreita de poros de 40 a 90 nm, espessura média de 57 mm e taxa de fluxo de 0,4 m3/m2h. O filtro assim obtido é classificado como ultrafiltro sendo capaz de reter bactérias e alguns vírus. São quimicamente inertes e resistem a temperaturas inferiores a 1000 °C. A aderência entre as camadas permite a limpeza por contra-fluxo.Alumina ceramic membranes with unimodal pore size distribution in the 40 to 90 nm range were prepared on alumina porous substrates. The 57mm thickness membrane made from AKP-50 alumina shows 0,4 m3/m2h flow rate. The two layer substrate, prepared to have high mechanical strength, was made from commercially available APC-SG alumina. The filter made of three layers, membrane, intermediate layer and substrate, is classified as ultra-filter being able to retain bacteria and some viruses. Adherence between the three layers allows reverse washing. Filters are chemically inert and resistant to temperatures below 1000oC.

  4. Investigation of Dip-Coating Parameters Effect on The Performance of Alumina-Polydimethylsiloxane Nanofiltration Membranes for Desalination

    OpenAIRE

    Mohammad Hadi Yousefi; Mohamad Mehdi Zerafat; Majid Shokri Doodeji; Samad Sabbaghi

    2017-01-01

    The objective of this work is to investigate the effect of dip-coating parameters on the performance of Alumina-PDMS hybrid nanofiltration membranes for water desalination. Ceramic supports used in this work were prepared with a 340 nm average pore size and 34% total porosity. The aim is to determine optimum conditions of dipping time, PDMS concentration, and withdrawal speed in order to achieve high rejection and flux values. Dip-coating parameters were considered as dipping time (60 - 120 s...

  5. Effects of temperature and feed composition on catalytic dehydration of methanol to dimethyl ether over {gamma}-alumina

    Energy Technology Data Exchange (ETDEWEB)

    Freshteh Raoof; Majid Taghizadeh; Ali Eliassi; Fereydoon Yaripour [Babol University of Technology, Babol (Iran). Chemical Engineering Department

    2008-10-15

    Catalytic dehydration of methanol to dimethyl ether (DME) is performed in an adiabatic fixed bed heterogeneous reactor by using acidic {gamma}-alumina. By changing the mean average temperature of the catalyst bed (or operating temperature of the reactor) from 233 up to 303{sup o}C, changes in methanol conversion were monitored. The results showed that the conversion of methanol strongly depended on the reactor operating temperature. Also, conversion of pure methanol and mixture of methanol and water versus time were studied and the effect of water on deactivation of the catalyst was investigated. The results revealed that when pure methanol was used as the process feed, the catalyst deactivation occurred very slowly. But, by adding water to the feed methanol, the deactivation of the {gamma}-alumina was increased very rapidly; so much that, by increasing water content to 20 weight percent by weight, the catalyst lost its activity by about 12.5-fold more than in the process with pure methanol. Finally, a temperature dependent model developed to predict pure methanol conversion to DME correlates reasonably well with experimental data. 11 refs., 9 figs., 3 tabs.

  6. Electric Field Mediated Ion Transport Through Charged Mesoporous Membranes

    NARCIS (Netherlands)

    Schmuhl, R.; de Lint, W.B.S.; Keizer, Klaas; van den Berg, Albert; ten Elshof, Johan E.; Burganos, Vasilis N.; Noble, Richard D.; Asaeda, Masashi; Ayral, Andre; LeRoux, Johann D.

    2003-01-01

    The transport of ions from aqueous solutions through a stacked Au/alpha-alumina/gamma-alumina/Au membrane under the influence of a dc potential difference is reported. The membrane shows high cation permselectivity at ionic strengths of ~1 mM at pH 4.3-6.5, which is associated with a combination of

  7. Impedimetric DNA Biosensor Based on a Nanoporous Alumina Membrane for the Detection of the Specific Oligonucleotide Sequence of Dengue Virus

    Directory of Open Access Journals (Sweden)

    Chee-Seng Toh

    2013-06-01

    Full Text Available A novel and integrated membrane sensing platform for DNA detection is developed based on an anodic aluminum oxide (AAO membrane. Platinum electrodes (~50–100 nm thick are coated directly on both sides of the alumina membrane to eliminate the solution resistance outside the nanopores. The electrochemical impedance technique is employed to monitor the impedance changes within the nanopores upon DNA binding. Pore resistance (Rp linearly increases in response towards the increasing concentration of the target DNA in the range of 1 × 10−12 to 1 × 10−6 M. Moreover, the biosensor selectively differentiates the complementary sequence from single base mismatched (MM-1 strands and non-complementary strands. This study reveals a simple, selective and sensitive method to fabricate a label-free DNA biosensor.

  8. Impedimetric DNA biosensor based on a nanoporous alumina membrane for the detection of the specific oligonucleotide sequence of dengue virus.

    Science.gov (United States)

    Deng, Jiajia; Toh, Chee-Seng

    2013-06-17

    A novel and integrated membrane sensing platform for DNA detection is developed based on an anodic aluminum oxide (AAO) membrane. Platinum electrodes (~50-100 nm thick) are coated directly on both sides of the alumina membrane to eliminate the solution resistance outside the nanopores. The electrochemical impedance technique is employed to monitor the impedance changes within the nanopores upon DNA binding. Pore resistance (Rp) linearly increases in response towards the increasing concentration of the target DNA in the range of 1 × 10⁻¹² to 1 × 10⁻⁶ M. Moreover, the biosensor selectively differentiates the complementary sequence from single base mismatched (MM-1) strands and non-complementary strands. This study reveals a simple, selective and sensitive method to fabricate a label-free DNA biosensor.

  9. Fabrication of Mesoporous Silica/Alumina Hybrid Membrane Film Nanocomposites using Template Sol-Gel Synthesis of Amphiphilic Triphenylene

    Science.gov (United States)

    Lintang, H. O.; Jalani, M. A.; Yuliati, L.; Salleh, M. M.

    2017-05-01

    Herein we reported that by introducing a one-dimensional (1D) substrate with a porous structure such as anodic aluminum oxide (AAO) membrane, mesoporous silica/alumina hybrid nanocomposites were successfully fabricated by using amphiphilic triphenylene (TPC10TEG) as a template in sol-gel synthesis (TPC10TEG/silicahex). For the optical study of the nanocomposites, TPC10TEG/silicahex showed absorption peak at 264 nm due to the ordered and long-range π-π stacking of the disc-like aromatic triphenylene core. Moreover, the hexagonal arrangement of TPC10TEG/silicahex was proven based on their diffraction peaks of d 100 and d 200 at 2θ = 2.52° and 5.04° and images of transmission electron microscopy (TEM), respectively. For fabrication of mesoporous silica/alumina hybrid membrane, TPC10TEG/silicahex was drop-casted onto AAO membrane for penetration into the porous structure via gravity. X-ray diffraction (XRD) analysis on the resulted hybrid nanocomposites showed that the diffraction peaks of d 100 and d 200 of TPC10TEG/silicahex were still preserved, indicating that the hexagonal arrangements of mesoporous silica were maintained even on AAO substrate. The morphology study on the hybrid nanocomposites using TEM, scanning electron microscope (SEM) and field emission scanning electron microscope (FE-SEM) showed the successful filling of most AAO channels with the TPC10TEG/silicahex nanocomposites.

  10. Investigation of Dip-Coating Parameters Effect on The Performance of Alumina-Polydimethylsiloxane Nanofiltration Membranes for Desalination

    Directory of Open Access Journals (Sweden)

    Mohammad Hadi Yousefi

    2017-10-01

    Full Text Available The objective of this work is to investigate the effect of dip-coating parameters on the performance of Alumina-PDMS hybrid nanofiltration membranes for water desalination. Ceramic supports used in this work were prepared with a 340 nm average pore size and 34% total porosity. The aim is to determine optimum conditions of dipping time, PDMS concentration, and withdrawal speed in order to achieve high rejection and flux values. Dip-coating parameters were considered as dipping time (60 - 120 s, withdrawal speed (5 - 15 mm/s and PDMS concentration (10 - 20 wt. %. Hybrid membranes were characterized using FE-SEM and FTIR analysis techniques. Pure water flux and salt rejection were also measured to evaluate the rejection performance. Alumina-PDMS hybrid nanofiltration membranes fabricated with dipping time = 120 s, withdrawal speed = 15 mm/s and 10 wt. % PDMS exhibited the best performance giving 30.5% rejection for NaCl and 53.8% for Na2SO4.

  11. Mechanical and structural characterizations of gamma- and alpha-alumina nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Vahtrus, Mikk; Umalas, Madis [Institute of Physics, University of Tartu, Ravila 14c, 50412 Tartu (Estonia); Polyakov, Boris [Institute of Solid State Physics, University of Latvia, Kengaraga 8, LV-1063 Riga (Latvia); Dorogin, Leonid [Institute of Physics, University of Tartu, Ravila 14c, 50412 Tartu (Estonia); ITMO University, Kronverkskiy pr., 49, 197101 Saint Petersburg (Russian Federation); Saar, Rando; Tamme, Maret; Saal, Kristjan [Institute of Physics, University of Tartu, Ravila 14c, 50412 Tartu (Estonia); Lõhmus, Rünno [Institute of Physics, University of Tartu, Ravila 14c, 50412 Tartu (Estonia); Materials Technologies Competence Centre, Riia 185b, 51014 Tartu (Estonia); Vlassov, Sergei [Institute of Physics, University of Tartu, Ravila 14c, 50412 Tartu (Estonia)

    2015-09-15

    We investigate the applicability of alumina nanofibers as a potential reinforcement material in ceramic matrix compounds by comparing the mechanical properties of individual nanofibers before and after annealing at 1400 °C. Mechanical testing is performed inside a scanning electron microscope (SEM), which enables observation in real time of the deformation and fracture of the fibers under loading, thereby providing a close-up inspection of the freshly fractured area in vacuum. Improvement of both the Young's modulus and the breaking strength for annealed nanofibers is demonstrated. Mechanical testing is supplemented with the structural characterization of the fibers before and after annealing using SEM, transmission electron microscopy and X-ray diffraction methods. - Highlights: • Mechanical properties of individual alumina nanofibers were measured using in situ SEM cantilevered beam bending technique. • Improvement of mechanical properties of the alumina fibers after annealing at 1400 °C is demonstrated. • Formation of branched structures is demonstrated and their mechanical properties are studied. • XRD and electron microscopy were used for structural characterization of untreated and annealed nanofibers.

  12. Spectroscopic ellipsometry analysis of a thin film composite membrane consisting of polysulfone on a porous α-alumina support.

    Science.gov (United States)

    Ogieglo, Wojciech; Wormeester, Herbert; Wessling, Matthias; Benes, Nieck E

    2012-02-01

    Exposure of a thin polymer film to a fluid can affect properties of the film such as the density and thickness. In particular in membrane technology, these changes can have important implications for membrane performance. Spectroscopic ellipsometry is a convenient technique for in situ studies of thin films, because of its noninvasive character and very high precision. The applicability of spectroscopic ellipsometry is usually limited to samples with well-defined interfacial regions, whereas in typical composite membranes, often substantial and irregular intrusion of the thin film into the pores of a support exists. In this work, we provide a detailed characterization of a polished porous alumina membrane support, using variable-angle spectroscopic ellipsometry in combination with atomic force microscopy and mercury porosimetry. Two Spectroscopic ellipsometry optical models are presented that can adequately describe the surface roughness of the support. These models consider the surface roughness as a distinct layer in which the porosity gradually increases toward the outer ambient interface. The first model considers the porosity profile to be linear; the second model assumes an exponential profile. It is shown that the models can be extended to account for a composite membrane geometry, by deposition of a thin polysulfone film onto the support. The developed method facilitates practicability for in situ spectroscopic ellipsometry studies of nonequilibrium systems, i.e., membranes under actual permeation conditions.

  13. Biogasoline Production from Palm Oil Via Catalytic Hydrocracking over Gamma-Alumina Catalyst

    Directory of Open Access Journals (Sweden)

    Anondho Wijanarko

    2010-10-01

    Full Text Available Bio gasoline conversion from palm oil is an alternative energy resources method which can be substituted fossil fuel base energy utilization. Previous research resulted that palm oil can be converted into hydrocarbon by catalytic cracking reaction with γ-alumina catalyst. In this research, catalytic cracking reaction of palm oil by γ-alumina catalyst is done in  a stirrer batch reactor with the oil/catalyst weight ratio variation of 100:1, 75:1, and 50:1; at suhue variation of 260 to 340oC and reaction time variation of 1 to 2 hour. Post cracking reaction, bio gasoline yield could be obtained after 2 steps batch distillation. Physical property test result such as density and viscosity of this cracking reaction product and commercial gasoline tended a closed similarity. According to result of the cracking product's density, viscosity and FTIR, it  can conclude that optimum yield of the palm oil catalytic cracking reaction could be occurred when oil/catalyst weight  ratio 100:1 at 340 oC in 1.5 hour and base on this bio gasoline's FTIR, GC and GC-MS identification results, its  hydrocarbons content was resembled to the commercial  gasoline. This palm oil catalytic cracking reaction shown 11.8% (v/v in yield and 28.0% (v/v in conversion concern to feed palm oil base and produced a 61.0 octane number's biogasoline.

  14. Effect of gamma radiation on chitin-nanosilver membranes

    International Nuclear Information System (INIS)

    Singh, Rita; Singh, Durgeshwer

    2014-01-01

    Antimicrobial wound dressings are indispensable for the effective healing of skin wounds such as burns and ulcers. Various synthetic and natural polymers with good biocompatibility have been used to develop wound dressings. Chitin possesses excellent properties that are advantageous for wound dressing namely biocompatibility, biodegradability and haemostatic activity. Chitin-nanosilver membranes were developed for use as an antimicrobial dressing for wound care. For clinical applications, the wound dressing should be assuredly free of microbial contamination. Gamma irradiation has well appreciated technological advantages and is the most suitable method for the sterilization of biomedical materials. The present study was carried out to evaluate the effect of gamma radiation on the chemical and functional characteristics of the chitin-nanosilver membranes

  15. Structured Ni catalysts on porous anodic alumina membranes for methane dry reforming: NiAl 2 O 4 formation and characterization

    KAUST Repository

    Zhou, Lu

    2015-06-29

    This communication presents the successful design of a structured catalyst based on porous anodic alumina membranes for methane dry reforming. The catalyst with a strong Ni-NiAl2O4 interaction shows both excellent activity and stability. This journal is © The Royal Society of Chemistry.

  16. Structured Ni catalysts on porous anodic alumina membranes for methane dry reforming: NiAl 2 O 4 formation and characterization

    KAUST Repository

    Zhou, Lu; Guo, Y.; Basset, Jean-Marie; Kameyama, H.

    2015-01-01

    This communication presents the successful design of a structured catalyst based on porous anodic alumina membranes for methane dry reforming. The catalyst with a strong Ni-NiAl2O4 interaction shows both excellent activity and stability. This journal is © The Royal Society of Chemistry.

  17. Functionalization of {gamma}-alumina cores by polyvinylpirrolidone: properties of the resulting biocompatible nanoparticles in aqueous suspension

    Energy Technology Data Exchange (ETDEWEB)

    Fernandez, L. [Universidad Nacional del Comahue, Dpto de Quimica, Facultad de Ingenieria (Argentina); Arranz, G.; Palacio, L. [Universidad de Valladolid, Dpto. Fisica Aplicada, Facultad de Ciencias (Spain); Soria, C.; Sanchez, M.; Perez, G. [Universidad Nacional del Comahue, Dpto de Quimica, Facultad de Ingenieria (Argentina); Lozano, A. E. [UA-CSIC-UVA, Surface and Porous Materials (SMAP) (Spain); Hernandez, A.; Pradanos, P., E-mail: pradanos@termo.uva.e [Universidad de Valladolid, Dpto. Fisica Aplicada, Facultad de Ciencias (Spain)

    2009-02-15

    A biocompatible polymer has been used to functionalize 45-50 nm diameter {gamma}-alumina nanoparticles. Because the target was to use these systems in real applications, polyvinylpirrolidone (PVP) was chosen due to the characteristics of non-toxicity, biocompatibility, and feasibility of this polymer to form complexes with many cations and chemical species. This approach allows the use of these materials in medicine and food, textile, or pharmaceutical industry. The functionalization process required a previous attachment of an active group on the surface of the nanoparticles. Subsequently, a polymer chain was generated in situ, using vinyltrimethoxysilane (VTMS) and 1-vinyl-2-pyrrolidone (VP) as reactives. The morphology and topology of the nanocompound has been characterized in aqueous suspensions, attending to possible applications in this medium. The results obtained from the different techniques show that the polymer chain was successfully grafted to the nanoparticle surface, and allow an estimation of the size of the modified particle. Their electrical and conformational behavior have also been studied in different aqueous chemical environments.

  18. Synthesis and characterization of sulfonate polystyrene-lignosulfonate-alumina (SPS-LS-Al{sub 2}O{sub 3}) polyblends as electrolyte membranes for fuel cell

    Energy Technology Data Exchange (ETDEWEB)

    Gonggo, Siang Tandi, E-mail: standigonggo@yahoo.com [Chemistry Research Groups, Faculty of Teacher Training and Educational Sciences, Tadulako University (Indonesia)

    2015-09-30

    The new type of electrolyte membrane materials has been prepared by blend sulfonated polystyrene (SPS), lignosulfonate (LS), and alumina (SPS-LS-Al{sub 2}O{sub 3}) by casting polymer solution. The resulting polymer electrolyte membranes were then characterized by functional groups analysis, mechanical properties, water uptake, ion exchange capacity, and proton conductivity. SPS-LS-Al{sub 2}O{sub 3} membranes with alumina composition various have been proven qualitatively by analysis of functional groups. Increasing the Al{sub 2}O{sub 3} ratio resulted in higher ion exchange capacity (IEC), mechanical strength and proton conductivity, but water uptake decreased. The SPS-LS-Al{sub 2}O{sub 3} blend showed higher proton conductivity than Nafion 117.

  19. Grafting study of polysulfone polymeric membranes by gamma ray irradiation

    International Nuclear Information System (INIS)

    Furtado Filho, Acacio A.M.; Gomes, Ailton de S.

    2011-01-01

    Radiation-induced grafting of styrene poli sulfone films were investigated by simultaneous method in solution using gamma-ray from a radio nuclide 60 Co source. The gamma-ray energy of high intensity induced breaking of chemical bonds leading to free radical formation. The radical start a conventional polymerization sequence comparable with that obtained with a chemical catalyst acting as initiator. The effects of grafting conditions such as irradiation total dose, dose rate and addition of cross linking agent, were studied by means of morphology analysis, thermal degradation and crystallinity. After the grafting reaction, the membranes were submitted to an exhaustive extraction with solvent to remove the polystyrene homopolymer formed. The degree of grafting (DOG) was analyzed by percentage of weight increase. As a result, the reaction always follows the same pattern: DOG increases rapidly initially whilst propagation is the main reaction, then more slowly as termination becomes more frequent. (author)

  20. Stabilization of supported platinum nanoparticles on gamma-alumina catalysts by addition of tungsten

    Energy Technology Data Exchange (ETDEWEB)

    Contreras, Jose L., E-mail: jlcl@correo.azc.uam.m [Universidad Autonoma Metropolitana-Azcapotzalco. Energia, CBI, Av. Sn. Pablo 180, Col. Reynosa, 02200, Mexico, D.F. (Mexico); Universidad Autonoma Metropolitana-Iztapalapa Depto. Ingenieria de Procesos e Hidraulica, A.P. 55-534, 09340 Mexico, D.F. (Mexico); Fuentes, Gustavo A. [Universidad Autonoma Metropolitana-Iztapalapa Depto. Ingenieria de Procesos e Hidraulica, A.P. 55-534, 09340 Mexico, D.F. (Mexico); Zeifert, Beatriz; Salmones, Jose [Instituto Politecnico Nacional, ESIQIE, Av. IPN s/n Edif. 8, UPALM, Mexico, D.F. 07738 (Mexico)

    2009-08-26

    The thermal stabilization of Al{sub 2}O{sub 3} using W{sup 6+} ions has been found useful to the synthesis of Pt/Al{sub 2}O{sub 3} catalysts. The simultaneous and sequential methods were used to study the effect of W{sup 6+} upon Pt/gamma-Al{sub 2}O{sub 3} reducibility, Pt dispersion, and benzene hydrogenation. The W/Pt atomic ratios were from 0.49 to 12.4. In the first method we found that the W{sup 6+} ions delayed reduction of a fraction of Pt{sup 4+} atoms beyond 773 K. At the same time, W{sup 6+}inhibited sintering of the metallic crystallites once they were formed on the surface. For the sequential sample with a W/Pt atomic ratio of 3.28 W{sup 6+} did not inhibit the H{sub 2} reduction of Pt oxides even below of 773 K, the Pt oxides were reduced completely. After reduction at 1073 K, sequential samples impregnating Pt on WO{sub x}-gamma-Al{sub 2}O{sub 3} were more active and stable during benzene hydrogenation. TOF of the reaction did not change when the W/Pt atomic ratio, preparation technique and reduction temperature changed and its value was of 1.1 s{sup -1}. W{sup 6+} ions promoted high thermal stability of Pt crystallites when sequential catalysts were reduced at 1073 K and decreased their Lewis acidity.

  1. Growth and FIB-SEM analyses of C60 microtubes vertically synthesized on porous alumina membranes

    Science.gov (United States)

    Miyazawa, Kun'ichi; Kuriyama, Ryota; Shimomura, Shuichi; Wakahara, Takatsugu; Tachibana, Masaru

    2014-02-01

    The vertical growth of C60 microtubes (C60MTs) on anodic aluminum oxide (AAO) membranes was investigated. The C60MT size dependence on isopropyl alcohol (IPA) injection rate, into C60-saturated toluene solutions through AAO membranes, was measured. A longitudinal section of the interface between a vertically grown C60MT (V-C60MT) and a membrane was prepared by focused ion beam processing, and observed with scanning electron microscopy. No cracking was observed along the interface, suggesting good bonding. V-C60MTs exhibited spiral growth. V-C60MT planar density, wall thickness and aspect ratio all decreased with increasing IPA injection rate. The relationships among length, inner and outer diameters of V-C60MTs were also investigated by varying IPA injection rate.

  2. Capture and alignment of phi29 viral particles in sub-40 nanometer porous alumina membranes.

    Science.gov (United States)

    Moon, Jeong-Mi; Akin, Demir; Xuan, Yi; Ye, Peide D; Guo, Peixuan; Bashir, Rashid

    2009-02-01

    Bacteriophage phi29 virus nanoparticles and its associated DNA packaging nanomotor can provide for novel possibilities towards the development of hybrid bio-nano structures. Towards the goal of interfacing the phi29 viruses and nanomotors with artificial micro and nanostructures, we fabricated nanoporous Anodic Aluminum Oxide (AAO) membranes with pore size of 70 nm and shrunk the pores to sub 40 nm diameter using atomic layer deposition (ALD) of Aluminum Oxide. We were able to capture and align particles in the anodized nanopores using two methods. Firstly, a functionalization and polishing process to chemically attach the particles in the inner surface of the pores was developed. Secondly, centrifugation of the particles was utilized to align them in the pores of the nanoporous membranes. In addition, when a mixture of empty capsids and packaged particles was centrifuged at specific speeds, it was found that the empty capsids deform and pass through 40 nm diameter pores whereas the particles packaged with DNA were mainly retained at the top surface of the nanoporous membranes. Fluorescence microscopy was used to verify the selective filtration of empty capsids through the nanoporous membranes.

  3. Permeabilization assay for antimicrobial peptides based on pore-spanning lipid membranes on nanoporous alumina.

    Science.gov (United States)

    Neubacher, Henrik; Mey, Ingo; Carnarius, Christian; Lazzara, Thomas D; Steinem, Claudia

    2014-04-29

    Screening tools to study antimicrobial peptides (AMPs) with the aim to optimize therapeutic delivery vectors require automated and parallelized sampling based on chip technology. Here, we present the development of a chip-based assay that allows for the investigation of the action of AMPs on planar lipid membranes in a time-resolved manner by fluorescence readout. Anodic aluminum oxide (AAO) composed of cylindrical pores with a diameter of 70 nm and a thickness of up to 10 μm was used as a support to generate pore-spanning lipid bilayers from giant unilamellar vesicle spreading, which resulted in large continuous membrane patches sealing the pores. Because AAO is optically transparent, fluid single lipid bilayers and the underlying pore cavities can be readily observed by three-dimensional confocal laser scanning microscopy (CLSM). To assay the membrane permeabilizing activity of the AMPs, the translocation of the water-soluble dyes into the AAO cavities and the fluorescence of the sulforhodamine 101 1,2-dihexadecanoyl-sn-glycero-3-phosphoethanol-l-amine triethylammonium salt (Texas Red DHPE)-labeled lipid membrane were observed by CLSM in a time-resolved manner as a function of the AMP concentration. The effect of two different AMPs, magainin-2 and melittin, was investigated, showing that the concentrations required for membrane permeabilization and the kinetics of the dye entrance differ significantly. Our results are discussed in light of the proposed permeabilization models of the two AMPs. The presented data demonstrate the potential of this setup for the development of an on-chip screening platform for AMPs.

  4. Micropatterning of a nanoporous alumina membrane with poly(ethylene glycol) hydrogel to create cellular micropatterns on nanotopographic substrates.

    Science.gov (United States)

    Lee, Hyun Jong; Kim, Dae Nyun; Park, Saemi; Lee, Yeol; Koh, Won-Gun

    2011-03-01

    In this paper, we describe a simple method for fabricating micropatterned nanoporous substrates that are capable of controlling the spatial positioning of mammalian cells. Micropatterned substrates were prepared by fabricating poly(ethylene glycol) (PEG) hydrogel microstructures on alumina membranes with 200 nm nanopores using photolithography. Because hydrogel precursor solution could infiltrate and become crosslinked within the nanopores, the resultant hydrogel micropatterns were firmly anchored on the substrate without the use of adhesion-promoting monolayers, thereby allow tailoring of the surface properties of unpatterned nanoporous areas. For mammalian cell patterning, arrays of microwells of different dimensions were fabricated. These microwells were composed of hydrophilic PEG hydrogel walls surrounding nanoporous bottoms that were modified with cell-adhesive Arg-Gly-Asp (RGD) peptides. Because the PEG hydrogel was non-adhesive towards proteins and cells, cells adhered selectively and remained viable within the RGD-modified nanoporous regions, thereby creating cellular micropatterns. Although the morphology of cell clusters and the number of cells inside one microwell were dependent on the lateral dimension of the microwells, adhered cells that were in direct contact with nanopores were able to penetrate into the nanopores by small extensions (filopodia) for all the different sizes of microwells evaluated. Copyright © 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  5. Surface-enhanced Raman scattering of self-assembled thiol monolayers and supported lipid membranes on thin anodic porous alumina

    Directory of Open Access Journals (Sweden)

    Marco Salerno

    2017-01-01

    Full Text Available Thin anodic porous alumina (tAPA was fabricated from a 500 nm thick aluminum (Al layer coated on silicon wafers, through single-step anodization performed in a Teflon electrochemical cell in 0.4 M aqueous phosphoric acid at 110 V. Post-fabrication etching in the same acid allowed obtaining tAPA surfaces with ≈160 nm pore diameter and ≈80 nm corresponding wall thickness to be prepared. The tAPA surfaces were made SERS-active by coating with a thin (≈25 nm gold (Au layer. The as obtained tAPA–Au substrates were incubated first with different thiols, namely mercaptobenzoic acid (MbA and aminothiol (AT, and then with phospholipid vesicles of different composition to form a supported lipid bilayer (SLB. At each step, the SERS substrate functionality was assessed, demonstrating acceptable enhancement (≥100×. The chemisorption of thiols during the first step and the formation of SLB from the vesicles during the second step, were independently monitored by using a quartz crystal microbalance with dissipation monitoring (QCM-D technique. The SLB membranes represent a simplified model system of the living cells membranes, which makes the successful observation of SERS on these films promising in view of the use of tAPA–Au substrates as a platform for the development of surface-enhanced Raman spectroscopy (SERS biosensors on living cells. In the future, these tAPA–Au-SLB substrates will be investigated also for drug delivery of bioactive agents from the APA pores.

  6. A route to MFI zeolite-.alpha.-alumina composite membranes for separation of light paraffins

    Czech Academy of Sciences Publication Activity Database

    Hrabánek, Pavel; Zikánová, Arlette; Bernauer, B.; Fíla, V.; Kočiřík, Milan

    2008-01-01

    Roč. 224, 1-3 (2008), s. 76-80 ISSN 0011-9164 R&D Projects: GA ČR GA203/05/0347; GA ČR GA203/07/1443 Institutional research plan: CEZ:AV0Z40400503 Keywords : silicalite-1 * membrane * synthesis * separation Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 1.155, year: 2008

  7. Controlled Patterning of Plasmonic Dimers by Using an Ultrathin Nanoporous Alumina Membrane as a Shadow Mask.

    Science.gov (United States)

    Hao, Qi; Huang, Hao; Fan, Xingce; Yin, Yin; Wang, Jiawei; Li, Wan; Qiu, Teng; Ma, Libo; Chu, Paul K; Schmidt, Oliver G

    2017-10-18

    We report on design and fabrication of patterned plasmonic dimer arrays by using an ultrathin anodic aluminum oxide (AAO) membrane as a shadow mask. This strategy allows for controllable fabrication of plasmonic dimers where the location, size, and orientation of each particle in the dimer pairs can be independently tuned. Particularly, plasmonic dimers with ultrasmall nanogaps down to the sub-10 nm scale as well as a large dimer density up to 1.0 × 10 10 cm -2 are fabricated over a centimeter-sized area. The plasmonic dimers exhibit significant surface-enhanced Raman scattering (SERS) enhancement with a polarization-dependent behavior, which is well interpreted by finite-difference time-domain (FDTD) simulations. Our results reveal a facile approach for controllable fabrication of large-area dimer arrays, which is of fundamental interest for plasmon-based applications in surface-enhanced spectroscopy, biochemical sensing, and optoelectronics.

  8. Biofunctionalization of aqueous dispersed, alumina membrane-templated polymer nanorods for use in enzymatic chemiluminescence assays.

    Science.gov (United States)

    Mark, Sonny S; Stolper, Samuel I; Baratti, Carla; Park, Jason Y; Kricka, Larry J

    2008-09-01

    The noncovalent immobilization of alkaline phosphatase (ALP) onto aqueous dispersed nylon 6 nanorods ( approximately 310 nm mean diameter; approximately 6 microm mean length) prepared by anodic aluminum oxide (AAO) membrane templating was studied. Using multi-stacked layer-by-layer (LBL) assembly with the cationic quaternary ammonium polymer Sapphire II , the amount of ALP enzyme loaded onto the polymer nanostructures was found to be 115+/-7 microg mg(-1) nanorod. The biofunctionalized nanorods were also characterized for their chemiluminescent activity with the dioxetane substrate, CSPD . The results indicate that the kinetic parameters, K(m) and V(max), for the catalytic activity of the nanostructure-bound ALP enzyme are different from those of soluble ('free') ALP. While the K(m) value was measured to be 156 microM for free ALP, the apparent K(m) value determined for the LBL-immobilized ALP is approximately 20% lower (122 microM). Furthermore, despite the relatively high enzyme loading capacity of the nanorods, the specific activity of the bound ALP enzyme was found to be almost nine times lower than that measured for free ALP. Finally, additional experiments revealed that the catalytic activities of both free ALP and nanorod-conjugated ALP are affected similarly by changes in pH, with optimal performance levels occurring under conditions of pH 9.5. To the best of our knowledge, this study represents the first report examining the preparation of aqueous dispersed, AAO-templated polymer nanorods for potential application as enzyme scaffolds in chemiluminescent-based assay systems.

  9. Structural study on Ni nanowires in an anodic alumina membrane by using in situ heating extended x-ray absorption fine structure and x-ray diffraction techniques

    International Nuclear Information System (INIS)

    Cai Quan; Chen Xing; Chen Zhongjun; Wang Wei; Mo Guang; Wu Zhonghua; Zhang Junxi; Zhang Lide; Pan Wei

    2008-01-01

    Polycrystalline Ni nanowires have been prepared by electrochemical deposition in an anodic alumina membrane template with a nanopore size of about 60 nm. In situ heating extended x-ray absorption fine structure and x-ray diffraction techniques are used to probe the atomic structures. The nanowires are identified as being mixtures of nanocrystallites and amorphous phase. The nanocrystallites have the same thermal expansion coefficient, of 1.7 x 10 -5 K -1 , as Ni bulk; however, the amorphous phase has a much larger thermal expansion coefficient of 3.5 x 10 -5 K -1 . Details of the Ni nanowire structures are discussed in this paper

  10. Ion Adsorption Parameters Determined from Zeta Potential and Titration Data for a y-Alumina Nanofiltration Membrane

    NARCIS (Netherlands)

    de Lint, W.B.S.; Benes, Nieck Edwin; Lyklema, Johannes; Bouwmeester, Henricus J.M.; van der Linde, Ab J.; Wessling, Matthias

    2003-01-01

    Theoretical models for the prediction of nanofiltration separation performance as a function of, e.g., pH and electrolyte composition require knowledge on the ion-surface adsorption chemistry. Adsorption parameters have been extracted from electrophoretic mobility measurements on a ceramic y-alumina

  11. High-flux MFI-alumina hollow fibres: a membrane-based process for on-board CO2 capture from internal combustion vehicles

    International Nuclear Information System (INIS)

    Nicolas, C.H.

    2011-01-01

    This work focuses on the conception and development of a membrane-based process for an on-board CO 2 capture/storage application. In a first part, we simulate an on-board CO 2 capture unit based on a membrane process for the case study of a heavy vehicle (≥3500 kg). This study includes an energy analysis of the impact of gas separation and compression on the required membrane surface and module volume, as well the autonomy of the storage unit and the energy overconsumption involved in the process. In a second part, we study the influence of the hollow-fibre support quality on the final intergrowth level of nano-composite MFI-alumina membranes. Special attention is devoted to the influence of the isomorphic substitution of silica by boron and germanium, and replacement of the counter-cation (proton) by other elements, on the CO 2 /N 2 separation and permeance properties. Next, a complete chapter has been devoted to the evaluation of the thermodynamic (adsorption) and kinetic (diffusion) parameters in the CO 2 /N 2 separation. Finally, we analyze the influence of standard pollutants (water, NO x , hydrocarbons) on the CO 2 separation properties of the synthesized membranes. (author)

  12. Fluorescence studies on gamma irradiated egg lecithin liposomal membrane

    International Nuclear Information System (INIS)

    Pandey, B.N.; Mishra, K.P.

    1998-01-01

    Alterations in structure and organization of sonicated EYL liposomal vesicular membrane after irradiation was investigated by DPH fluorescence probe which is a well known reporter for the environment of hydrophobic interior of membrane. Results of present study have demonstrated that loss of DPH fluorescence in liposomal membrane is linked to free radical mediated structural alterations possibly rigidization in the lipid bilayer

  13. Characterization of modified PVDF membrane by gamma irradiation for non-potable water reuse.

    Science.gov (United States)

    Lim, Seung Joo; Kim, Tak-Hyun; Shin, In Hwan

    2015-01-01

    Poly(vinylidene fluorine) (PVDF) membranes were grafted by gamma-ray irradiation and were sulfonated by sodium sulfite to modify the surface of the membranes. The characteristics of the modified PVDF membranes were evaluated by the data of Fourier transform infrared (FT-IR), X-ray photoelectron spectroscopy (XPS), field-emission scanning electron microscope (FE-SEM), the contact angle of the membrane surface and the water permeability. From the results of FT-IR, XPS and FE-SEM, it was shown that the modified membranes were successfully grafted by gamma-ray irradiation and were sulfonated. The content of oxygen and sulfur increased with the monomer concentration, while the content of fluorine sharply decreased. The pore size of the modified membranes decreased after gamma-ray irradiation. The contact angle and the water permeability showed that the hydrophilicity of the modified membranes played a role in determining the membrane performance. The feasibility study of the modified PVDF membranes for using non-potable water reuse were carried out using a laboratory-scale microfiltration system. Grey wastewater was used as the influent in the filtration unit, and permeate quality satisfied non-potable water reuse guidelines in the Republic of Korea.

  14. Fabrication and optical properties of TiO sub 2 nanowire arrays made by sol-gel electrophoresis deposition into anodic alumina membranes

    CERN Document Server

    Lin, Y; Yuan, X Y; Xie, T; Zhang, L D

    2003-01-01

    Ordered TiO sub 2 nanowire arrays have been successfully fabricated into the nanochannels of a porous anodic alumina membrane by sol-gel electrophoretic deposition. After annealing at 500 deg. C, the TiO sub 2 nanowire arrays and the individual nanowires were characterized using scanning electron microscopy (SEM), transmission electron microscopy (TEM), selected area electron diffraction (SAED) and x-ray diffraction (XRD). SEM and TEM images show that these nanowires are dense and continuous with a uniform diameter throughout their entire length. XRD and SAED analysis together indicate that these TiO sub 2 nanowires crystallize in the anatase polycrystalline structure. The optical absorption band edge of TiO sub 2 nanowire arrays exhibits a blue shift with respect of that of the bulk TiO sub 2 owing to the quantum size effect.

  15. Effect of high carbon dioxide storage and gamma irradiation on membrane deterioration in cauliflower florets

    International Nuclear Information System (INIS)

    Voisine, R.; Hombourger, C.; Willemot, C.; Castaigne, F.; Makhlouf, J.

    1993-01-01

    Controlled atmospheres and gamma irradiation are technologies which extend storage-life of fruits and vegetables. Separate and combined effects of high CO 2 storage and gamma irradiation on cell membranes from cauliflower florets (Brassica oleracea L., Botrytis group) were investigated. Storage of the florets for 8 days at 13°C, either under 15% carbon dioxide or in air after irradiation at 2 kGy, accelerated the deterioration of microsomal membranes during storage. Both treatments caused an early loss in lipid phosphate. Irradiation enhanced the free fatty acid content of the membranes during storage and caused an extensive protein loss. When irradiation and high CO 2 storage were combined, electrolyte leakage significantly increased while protein loss was considerably reduced. The results indicate that high CO 2 and irradiation accelerate membrane degradation through different mechanisms. The combined effects of the treatments were not additive, but membrane yield was apparently reduced. CO 2 protected the membranes from protein loss induced by irradiation. The apparent increase in electrolyte leakage after irradiation may be caused by the release of ions following cell wall deterioration

  16. Luminescence enhancement of a self-organised Y.sub.2./sub.O.sub.3./sub.:Eu.sup.3+./sup. thin film-coated porous alumina membrane

    Czech Academy of Sciences Publication Activity Database

    Abdellaoui, N.; Pereira, A.; Kandri, T.; Drouard, E.; Novotný, Michal; Moine, B.; Pillonnet, A.

    2016-01-01

    Roč. 4, č. 39 (2016), s. 9212-9218 ISSN 2050-7526 R&D Projects: GA MŠk LO1409; GA ČR GA16-22092S Institutional support: RVO:68378271 Keywords : pulsed laser deposition * thin film * self- organisation * alumina membrane * luminescence * photonic structure Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 5.256, year: 2016

  17. Effect of Pore Thickness and the State of Polarization on the Optical Properties of Hexagonal Nanoarray of Au/Nanoporous Anodic Alumina Membrane

    Directory of Open Access Journals (Sweden)

    Mohamed Shaban

    2015-01-01

    Full Text Available Hexagonal nanoarrays of Au particles were deposited on nanoporous anodic alumina membrane (NAAM utilizing r.f. magnetron sputtering. The thickness of the NAAMs is adjusted by changing the second anodization time from 5 min to 20 min. The surface morphology, composition, and optical properties are characterized by using SEM, EDX, and spectrophotometer, respectively. The effects of the NAAM thickness and state of polarization on the morphological changes and on the optical properties of the fabricated nanoarrays were addressed. According to the measured optical spectra, the rate of decrease of NAAMs refractive index was found to be 3.825 × 10−4 nm−1. Using the modified Kubelka-Munk radiative transfer model, the energy gap of NAAMs was calculated from diffused reflectance and was decreased from 1.682 to 1.376 as the anodization time increased from 5 to 20 min. Also, the saturation of interference fringes is substantially enhanced, and field enhancement can be achieved due to the excitation and constructive interference of surface plasmon waves by coating NAAMs with the hexagonal nanoarrays of Au. Based on the advantages of the fabrication approach and the enhanced and controlled properties, this new generation of samples can be used as promising building blocks for nanophotonic and nanoelectronics devices.

  18. Effects of gamma-irradiation on the erythrocyte membrane: ESR, NMR and biochemical studies

    International Nuclear Information System (INIS)

    Cantafora, A.; Ceccarini, M.; Guidoni, L.; Ianzini, F.; Minetti, M.; Viti, V.

    1987-01-01

    The effects of gamma-irradiation on resealed erythrocyte ghosts have been examined with different techniques. Phospholipid analysis reveals peroxidative damage on the polyunsaturated chains of phosphatidylethanolamine. Gel electrophoresis and ESR measurements indicate modifications of the cytoskeletal proteins. 31 P nuclear magnetic resonance data show bilayer modifications that can be interpreted as changes in lipid-protein interactions. The overall picture from the present results favours interaction between lipids and proteins in the inner monolayer of the membrane. (author)

  19. GABAA [gamma-aminobutyric acid] type binding sites on membranes of spermatozoa

    International Nuclear Information System (INIS)

    Erdoe, S.L.; Wekerle, L.

    1990-01-01

    The binding of [ 3 H] gamma-aminobutyric acid (GABA) to seminal membranes of swines and rams was examined. Specific, GABA binding was demonstrated in both species, which showed the features of GABA A type receptors. The affinity of binding was similar in both species, whereas the density of seminal GABA binding sites was 5 times higher in swine. Our findings suggest that GABA may have a direct effect on spermatozoa

  20. Synthesis and characterization of mesoporous ceria/alumina nanocomposite materials via mixing of the corresponding ceria and alumina gel precursors.

    Science.gov (United States)

    Khalil, Kamal M S

    2007-03-01

    Mesoporous ceria/alumina, CeO(2)/Al(2)O(3), composites containing 10, 20 and 30% (w/w) ceria were prepared by a novel gel mixing method. In the method, ceria gel (formed via hydrolysis of ammonium cerium(IV) nitrate by aqueous ammonium carbonate solution) and alumina gel (formed via controlled hydrolysis of aluminum tri-isopropoxide) were mixed together. The mixed gel was subjected to subsequent drying and calcination for 3 h at 400, 600, 800 and 1000 degrees C. The uncalcined (dried at 110 degrees C) and the calcined composites were investigated by different techniques including TGA, DSC, FTIR, XRD, SEM and nitrogen adsorption/desorption isotherms. Results indicated that composites calcined for 3 h at 800 degrees C mainly kept amorphous alumina structure and gamma-alumina formed only upon calcinations at 1000 degrees C. On the other hand, CeO(2) was found to crystallize in the common ceria, cerinite, phase and it kept this structure over the entire calcination range (400-1000 degrees C). Therefore, high surface areas, stable surface textures, and non-aggregated nano-sized ceria dispersions were obtained. A systematic texture change based on ceria ratio was observed, however in all cases mesoporous composite materials exposing thermally stable texture and structure were obtained. The presented method produces composite ceria/alumina materials that suit different applications in the field of catalysis and membranes technology, and throw some light on physicochemical factors that determine textural morphology and thermal stability of such important composite.

  1. Characterization of commercial proton exchange membrane materials after exposure to beta and gamma radiation

    Energy Technology Data Exchange (ETDEWEB)

    Thomson, S.N.; Carson, R.; Muirhead, C.; Li, H.; Castillo, I.; Boniface, H.; Suppiah, S. [Canadian Nuclear Laboratories, Chalk River, ON (Canada); Ratnayake, A.; Robinson, J. [Tyne Engineering Inc., Burlington, ON (Canada)

    2015-03-15

    Proton Exchange Membrane (PEM) type electrolysis cells have a potential use for tritium removal and heavy water upgrading. AECL is currently exposing various commercial PEM materials to both gamma (Cobalt-60 source) and beta (tritiated water) radiation to study the effects of radiation on these materials. This paper summarizes the testing methods and results that have been collected to date. The PEM materials that are or have been exposed to radiation are: Nafion 112, 212, 117 and 1110. Membrane characterization pre- and post- exposure consists of non-destructive inspection (FTIR, SEM/XPS), mechanical (tensile strength, percentage elongation, and modulus), electrical (resistance), or chemical (ion-exchange capacity - IEC). It has appeared that the best characterization techniques to compare exposed versus unexposed membranes were IEC, ultimate tensile strength and percent elongation. These testing techniques are easy and cheap to perform. The non-destructive tests, such as SEM and FTIR did not provide particularly useful information on radiation-induced degradation. Where changes in material properties were measured after radiation exposure, they would be expected to result in poorer cell performance. However, for modest γ-radiation exposure, all membranes showed a slight decrease in cell voltage (better performance). In contrast, the one β-radiation exposed membrane did show the expected increase in cell voltage. The counterintuitive trend for γ-radiation exposed membranes is not yet understood. Based on these preliminary results, it appears that γ- and β-radiation exposures have different effects.

  2. Gamma irradiation prolongs the sea bass (Dicentrarchus labrax L) storage and delays the lipids membrane degradation

    International Nuclear Information System (INIS)

    Barkallah, Insaf; Mahjoub, Abdelmajid; Cheour, F.

    2005-01-01

    Sea bass have been submitted to gamma rays radiation at doses 0, 1, 2, 3 or 4 KGy at 0,087KGY/min rate and stored during 21 days at 1 0 C to evaluate the effects on the development of microorganisms as well as on the conservation and the degradation of membranes lipids Microbiological analysis has revealed only the presence of mesophils germs in muscles which are totally eliminated at dose 4 KGy. The presence of psychrophiles, halophiles, coliformes, fecaux and totals, Staphylococcus aureus and Clostridium sulfutoreducteurs has been noted in the visceres of sea bass. They are completely eliminated at dose 1KGy. Contents in nitrogen basic fowl (ABVT) and in trimethylamine (TMA), as well as the pH increase during storage of fish in relation with the reduction of phospholipids, the diminution of the degree of insaturation of the phospholipids and the free fat acidic fraction, and the increase of the report sterols on phospholipids. The irradiation to gamma rays allows to slow these changes and consequently reduced the deterioration of the sea bass. We conclude that the irradiation to gamma rays could have prolong the conservation of sea bass sea bass by preserving probably lipids membranes of the degradation and by inhibiting the development of microorganisms

  3. Size-Controlled AgI/Ag Heteronanowires in Highly Ordered Alumina Membranes: Superionic Phase Stabilization and Conductivity.

    Science.gov (United States)

    Zhang, Hemin; Tsuchiya, Takashi; Liang, Changhao; Terabe, Kazuya

    2015-08-12

    Nanoscaled ionic conductors are crucial for future nanodevices. A well-known ionic conductor, AgI, exhibited conductivity greater than 1 Ω(-1) cm(-1) in α-phase and transformed into poorly conducting β-/γ-phase below 147 °C, thereby limiting applications. Here, we report that transition temperatures both from the β-/γ- to α-phase (Tc↑) and the α- to β-/γ-phase (Tc↓) are tuned by AgI/Ag heteronanowires embedded in anodic aluminum oxide (AAO) membranes with 10-30 nm pores. Tc↑ and Tc↓ shift to correspondingly higher and lower temperature as pore size decreases, generating a progressively enlarged thermal hysteresis. Tc↑ and Tc↓ specifically achieve 185 and 52 °C in 10 nm pores, and the final survived conductivity reaches ∼8.3 × 10(-3) Ω(-1) cm(-1) at room temperature. Moreover, the low-temperature stabilizing α-phase (down to 21 °C, the lowest in state of the art temperatures) is reproducible and survives further thermal cycling. The low-temperature phase stabilization and enhancement conductivity reported here suggest promising applications in silver-ion-based future nanodevices.

  4. Use of gamma and UV radiation in grafting hydrogel polymers to membranes

    International Nuclear Information System (INIS)

    Baker, L.; Hill, D.J.T.; Whittaker, A.; Hunter, D.; Davis, T.P.

    1998-01-01

    Full text: Dimethylacrylamide and N-isopropylacrylamide hydrogels are useful for their ability to absorb large amounts of water and for their thermotropic response. However as membranes they do not have the mechanical properties to be applicable in industry. Therefore these hydrogels have been grafted to polyvinylidinedifluoride (PVDF) membranes using radiation. Both UV and gamma irradiation were used. In the first method the PVDF membranes were first hydroxylated by immersion in a aqueous solution of potassium peroxydisulfate (10% w/v), with nitrogen purging for two hours at 80 deg C. This was followed by immersion in an aqueous solution of riboflavine (4mg/L) and monomer (10% v/v), degassing with nitrogen and irradiation under a Mercury UV light (wavelength 240 nm) at room temperature for 15 minutes. Membranes were washed by soxhlet extraction in distilled water and oven dried. The second method of grafting hydrogels to membranes involved immersing the membrane in 10 mL of distilled water containing monomer and CuSO 4 to prevent homopolymerisation. The solution was degassed with N 2 for 3 minutes then irradiated under nitrogen using a 60 Co source for various time periods. The effect of varying monomer and CuSO 4 concentration as well as dose rate and dose were studied. Membranes were rinsed in distilled water for 24 hours and dried in an oven before characterisation. Grafting was characterised by mass change (Mettler AC 100 balance), XPS (PHI Model 560 XPS/SAM/SIMA1 multitechnique surface analysis system), SEM (Hitachi S-900 Field Emission SEM) and FTIR-ATR (Perkn Elmer System 2000 FTIR with MIRMCT detector)

  5. Effect of gamma irradiation at intermediate doses on the performance of reverse osmosis membranes

    International Nuclear Information System (INIS)

    Combernoux, Nicolas; Labed, Véronique; Schrive, Luc; Wyart, Yvan; Carretier, Emilie; Moulin, Philippe

    2016-01-01

    The goal of this study is to explain the degradation of Polyamide (PA) composite reverse osmosis membrane (RO) in function of the irradiation dose. Irradiations were performed with a gamma 60 Co source in wet conditions and under oxygen atmosphere. For different doses of 0.2 and 0.5 MGy with a constant dose rate of 0.5 kGy h −1 , RO membranes performances (NaCl retention, permeability) were studied before and after irradiation. ATR-FTIR, ion chromatography and gas chromatography were used to characterize structural modification. Results showed that the permeability of RO membranes irradiated at 0.2 MGy exhibited a small decrease, related to scissions of the PVA coating. However, retention did not change at this dose. At 0.5 MGy, permeability showed a large increase of a factor around 2 and retention began to decrease from 99% to 95%. Chromatography measurements revealed a strong link between permselectivity properties variation, ion leakage and oxygen consumption. Add to ATR-FTIR observations, these results emphasized that the cleavages of amide and ester bonds were observed at 0.5 MGy, more precisely the loss of hydrogen bonds between polyamide chains. By different analysis, modifications of the polysulfone layer occur until a dose of 0.2 MGy. - Highlights: • Irradiation of RO membranes at intermediate dose (0.2 and 0.5 MGy). • For a dose rate of 0.5 kGy h −1 RO membranes are radiation resistant until 0.2 MGy. • Cleavages of polymer bonds in the active layer at 0.5 MGy. • Decrease in permselectivity properties of the membrane at 0.5 MGy. • High oxygen consumption between 0.2 and 0.5 MGy related to the membranes degradation.

  6. Crosslinking of electrospun poly (VDF-co-HFP) nanofibrous membranes by gamma-ray irradiation

    International Nuclear Information System (INIS)

    Kim, Yun Hye; Lim, Youn Mook; Choi, Jae Hak; An, Sung Jun; Park, Jong Seok; Nho, Young Chang

    2008-01-01

    Poly (VDF-co-HFP)/PEGDMA nanofibrous membranes (NFMs) have been prepared by an electrospinning process. Since electrospun NFMs have a nanoporous structure, they have a potential application for a polymer electrolyte or a separator. Poly (VDF-co-HFP) is a polymer electrolyte binder. In order to improve their mechanical properties, poly (VDF-co-HFP)/PEGDMA NFMs were crosslinked by a gamma-ray irradiation. Then the crosslinked NFMs were characterized through an electrolyte uptake, IR structural analysis, and SEM morphological investigation

  7. Characterization of acute undifferentiated leukemia by combined analysis of plasma membrane-associated gamma-glutamyltranspeptidase and soluble terminal transferase.

    Science.gov (United States)

    Heumann, D; Losa, G; Barras, C; Morell, A; von Fliedner, V

    1985-08-01

    gamma-Glutamyltranspeptidase (gamma-GT) is a plasma membrane-associated enzyme present in blasts of certain acute leukemias. We analyzed 90 cases of undifferentiated and differentiated acute leukemias for gamma-GT, using a colorimetric assay. Blasts of all patients with common acute lymphoblastic leukemia (ALL) and T-ALL were negative for gamma-GT (less than 5 units). In contrast, gamma-GT was significantly elevated in acute myeloblastic or monoblastic leukemia blasts (P less than .001). In 16 cases of acute undifferentiated leukemia (AUL) studied, the levels of gamma-GT ranged from 0 to 93 units; in eight cases, gamma-GT was positive (greater than 5 units), and six of these had 2% to 5% Sudan black-positive leukemic cells in the blast-enriched suspension. Combined gamma-GT/TdT analysis revealed that both enzyme markers were mutually exclusive in 75% of AUL cases, suggesting that gamma-GT+/TdT-blasts are of nonlymphoid origin, and gamma-GT-/TdT+ blasts are of lymphoid origin. Two cases were devoid of both enzyme activities and could represent truly undifferentiated leukemia. Thus, combined gamma-GT/TdT analysis underlines the heterogeneity of AUL and appears to be useful in defining the lineage commitment of undifferentiated leukemic blasts.

  8. Effect of Addition of Soybean Oil and Gamma-Ray Cross-linking on the Nanoporous HDPE Membrane

    Directory of Open Access Journals (Sweden)

    Jong-Seok Park

    2012-01-01

    Full Text Available A nanoporous high-density polyethylene (HDPE membrane was prepared by a wet process. Soybean oil and dibutyl phthalate (DBP were premixed as codiluents, and gamma-rays were used for the cross-linking of HDPE. The pore volume of the nanoporous HDPE membranes with soybean oil was affected by the extracted amount of oil. The tensile strength of the membrane improved with an increasing absorbed dose up to 60 kGy, but decreased at 80 kGy due to severe degradation. The ionic conductivity of the nanoporous HDPE membrane did not really change with an increasing absorbed dose because the pores had already been formed before the gamma-ray radiation. Finally, the electrochemical stability of the HDPE membrane increased when the absorbed dose increased up to 60 kGy.

  9. Determination of porosity in supports for ceramic membranes of titanium dioxide by gamma spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Siciliano, Umberto C.C.S.; Oliveira, Elizabeth E.M.; Brandão, Luís E.B.; Carvalho, Paulo V.R., E-mail: ucsiciliano@gmail.com, E-mail: eemo@ien.gov.br, E-mail: brandao@ien.gov.br, E-mail: paulov@ien.gov.br [Instituto de Engenharia Nuclear (IEN/CNEN-RJ), Rio de Janeiro, RJ (Brazil)

    2017-07-01

    Membrane separation processes (MSP) have been widely used to fractionate, concentrate and purity solutions, such as: food industry, pharmaceutical, water desalination and for treatment of the radioactive liquid waste in the nuclear industry. The MSP are more economical than traditional methods because most of them are athermic. Increased membrane application has led to the expansion of the manufacturing technology knowledge base, resulting in membranes with high permeability, improved selectivity and long-term stability. The demand for high operating temperatures and chemical resistance have stimulated the development of inorganic structures, mainly porous ceramics. The materials most used to obtain ceramic membranes are oxides like Ab0{sub 3}, Si0{sub 2}, Zr0{sub 2} and Ti0{sub 2} or combination of these. Despite the favorable characteristics, ceramic membranes has not been applied extensively, mainly due to the difficulty of obtaining porous structures without cracks and with adequate pore size. The objective of this work is obtain a support of titanium oxide using potato starch as a pore former. The titanium oxide used is commercial, with average particle size of 0.13 μm. Three suspensions were prepared containing 0,5 and 10 % of the potato starch and the drying in spray dryer, obtaining a homogeneous and granulated powder, with flow ability suitable for compaction. The supports were uniaxial pressing with l.5 kgf.cm{sup -2} and sintering at temperatures of 1050, 1100 and 1150 °C for 1h in oven resistance. The results showed that the porosity obtained by gamma ray transmission method was approximately 50%. This value is within range for applications as membrane support. (author)

  10. Changes induced by gamma radiation in microsomal membranes of storage of garlic

    International Nuclear Information System (INIS)

    Perez, M.B.; Croci, C.A.; Aveldano, M.I.

    2003-01-01

    This study evaluates the effects of the radio inhibition process on garlic bulbs in terms of phase properties of microsomal membranes and their lipid and fatty acid composition. Garlic bulbs were irradiated with an average dose of 60 Gy of 60 Co gamma rays 30-40 days after harvest. The treatment was carried out in the facilities of the National Atomic Energy Commission (CNEA). Rough and smooth microsomal membranes were isolated by ultracentrifugation from tissues of irradiated and non-irradiated storage leaves. Wide angle X-ray diffractograms of both fractions were recorded along 270 days of storage. Lipids were separated by thin layer chromatography. The fatty acid composition of major lipid fractions was studied by gas-liquid chromatography. The diffractograms featured peaks at Bragg spacing of 4.15 Armstrong and 3.75 Armstrong, revealing the presence of a gel (crystalline) phase, while the characteristic peak of the liquid-crystalline phase (4.6 Armstrong) was not observed in both sorts of membranes. Irradiation was found to bring about modifications in the intensity of 4.15 Armstrong and 3.75 Armstrong peaks from smooth microsomal membranes, but not in the behaviour along the studied period. Data from the rough microsomal fraction were erratic. Parallel to these changes, radiation induced significant modifications in the level of smooth microsomal membrane triacylglycerols in relation to phospholipids and their fatty acids. These findings indicate that the storage leaf tissues of garlic are radiosensitive both in terms of physical and chemical properties of their microsomal membranes. From the practical point of view, these results could be the basis for the development of techniques to be applied to storage garlic to evaluate if it was irradiated. (author)

  11. Surface characterisation and photocatalytic performance of N-doped TiO{sub 2} thin films deposited onto 200 nm pore size alumina membranes by sol–gel methods

    Energy Technology Data Exchange (ETDEWEB)

    Grilli, R., E-mail: r.grilli@surrey.ac.uk [The Surface Analysis Laboratory, Faculty of Engineering and Physical Sciences, University of Surrey, Guildford, Surrey, GU2 7XH (United Kingdom); Di Camillo, D.; Lozzi, L. [Dipartimento di Scienze Fisiche e Chimiche, Università degli Studi dell' Aquila, Via Vetoio, 67010 Coppito, L' Aquila (Italy); Horovitz, I.; Mamane, H.; Avisar, D. [School of Mechanical Engineering, Faculty of Engineering, Tel Aviv University, Tel Aviv 69978 (Israel); Baker, M.A. [The Surface Analysis Laboratory, Faculty of Engineering and Physical Sciences, University of Surrey, Guildford, Surrey, GU2 7XH (United Kingdom)

    2015-06-01

    Membrane filtration is employed for water treatment and wastewater reclamation purposes, but membranes alone are unable to remove pollutant molecules and certain pathogens. Photocatalytically active N-doped TiO{sub 2} coatings have been deposited by sol–gel onto 200 nm pore size alumina membranes for water treatment applications using two different methods, via pipette droplets or spiral bar applicator. The uncoated and coated membranes were characterised by X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), X-ray diffraction (XRD) and energy dispersive X-ray spectrometry (EDX). Both coatings showed the presence of N-doped anatase, with a surface coverage between 84 and 92%, and nitrogen concentration (predominantly interstitial) of 0.9 at.%. The spiral bar applicator deposited coatings exhibit a thicker mud-cracked surface layer with limited penetration of the porous membrane, whilst the pipette deposited coatings have mostly penetrated into the bulk of the membrane and a thinner layer is present at the surface. The photocatalytic activity (PCA), measured through the degradation of carbamazepine (CBZ), under irradiation of a solar simulator was 58.6% for the pipette coating and 63.3% for the spiral bar coating. These photocatalytically active N-doped sol–gel coated membranes offer strong potential in forming the fundamental basis of a sunlight based water treatment system. - Highlights: • Sol gel N-doped TiO{sub 2} thin films were deposited on 200 nm pore size Al{sub 2}O{sub 3} membranes. • Two sol–gel methods have been compared – pipette drop and spiral bar deposition. • The coatings showed a similar microstructure and composition but different morphology. • The PCA (degradation of carbamazepine) was ∼60% for both sol–gel coatings. • The coated membranes are promising for use in a membrane based water treatment system.

  12. alumina solid electrolyte

    Indian Academy of Sciences (India)

    -β/β -alumina ceramics come from two parent phases designated as β-alumina and β ..... Acknowledgements. This work was supported by the Energy Efficiency & ... of Trade, Industry & Energy, Republic of Korea (No. 20142010102460).

  13. Influence of high energy electron irradiation and gamma irradiation on the osmotic resistance of human erythrocyte membranes

    International Nuclear Information System (INIS)

    Catana, D.; Hategan, Alina; Moraru, Rodica; Popescu, Alina; Morariu, V. V.

    1998-01-01

    The effects of 5 MeV electrons and of gamma irradiation at 0 deg. C on the osmotic fragility of human erythrocyte membranes are presented. Both electron and gamma radiation in the range 0-400 Gy induced no hemolysis indicating that the membrane modifications due to radiation interaction do not reach a critical point as to cause swelling of the cells and subsequent lysis. The osmotic stress experiments performed after irradiation showed that the gamma irradiated erythrocytes exhibited an almost similar sigmoidal behavior for all irradiation doses, whereas the electron irradiated samples showed a much larger increase in hemolysis degree and, in the case of a given electron dose (100 Gy), the hemolysis was found much smaller than for the control sample (a similar behavior of the erythrocytes was found in the case of microwave irradiation at temperatures under 0 deg. C). Our experimental data suggest that electron radiation and gamma radiation have different impacts on the erythrocyte membrane fluidity, involving, probably, the different rate of energy deposition in the samples and the direct interaction of electrons with the erythrocyte membranes. (authors)

  14. Antibacterial activity of zinc oxide-coated nanoporous alumina

    Energy Technology Data Exchange (ETDEWEB)

    Skoog, S.A. [Joint Department of Biomedical Engineering, University of North Carolina and North Carolina State University, Box 7115, Raleigh, NC 27695-7115 (United States); Bayati, M.R. [Department of Materials Science and Engineering, North Carolina State University, Box 7907, Raleigh, NC 27695-7907 (United States); Petrochenko, P.E. [Joint Department of Biomedical Engineering, University of North Carolina and North Carolina State University, Box 7115, Raleigh, NC 27695-7115 (United States); Division of Biology, Office of Science and Engineering Laboratories, Center for Devices and Radiological Health, U.S. Food and Drug Administration, Silver Spring, MD 20993 (United States); Stafslien, S.; Daniels, J.; Cilz, N. [Center for Nanoscale Science and Engineering, North Dakota State University, 1805 Research Park Drive, Fargo, ND 58102 (United States); Comstock, D.J.; Elam, J.W. [Energy Systems Division, Argonne National Laboratory, Argonne, IL 60439 (United States); Narayan, R.J., E-mail: roger_narayan@msn.com [Joint Department of Biomedical Engineering, University of North Carolina and North Carolina State University, Box 7115, Raleigh, NC 27695-7115 (United States); Department of Materials Science and Engineering, North Carolina State University, Box 7907, Raleigh, NC 27695-7907 (United States)

    2012-07-25

    Highlights: Black-Right-Pointing-Pointer Atomic layer deposition was used to deposit ZnO on nanoporous alumina membranes. Black-Right-Pointing-Pointer Scanning electron microscopy showed continuous coatings of zinc oxide nanocrystals. Black-Right-Pointing-Pointer Activity against B. subtilis, E. coli, S. aureus, and S. epidermidis was shown. - Abstract: Nanoporous alumina membranes, also known as anodized aluminum oxide membranes, are being investigated for use in treatment of burn injuries and other skin wounds. In this study, atomic layer deposition was used for coating the surfaces of nanoporous alumina membranes with zinc oxide. Agar diffusion assays were used to show activity of zinc oxide-coated nanoporous alumina membranes against several bacteria found on the skin surface, including Bacillus subtilis, Escherichia coli, Staphylococcus aureus, and Staphylococcus epidermidis. On the other hand, zinc oxide-coated nanoporous alumina membranes did not show activity against Pseudomonas aeruginosa, Enterococcus faecalis, and Candida albicans. These results suggest that zinc oxide-coated nanoporous alumina membranes have activity against some Gram-positive and Gram-negative bacteria that are associated with skin colonization and skin infection.

  15. Fabrication of Meso-Porous Gamma-Alumina Films by Sol-Gel and Gel Casting Processes for Making Moisture Sensors

    Directory of Open Access Journals (Sweden)

    Kalyan Kumar Mistry

    2007-04-01

    Full Text Available Meso-porous g-Al2O3 film may be used as a highly sensitive trace moisture sensor. The crack-free alumina film was developed using a combination of sol-gel and tape casting processes, which produce high porosity, high surface area and small pore dimensions in the range of few nano-meter at uniform distribution. Sol-gel processes are well known in nano-technology and nano-material preparation, but it is difficult to make crack-free thick or thin films using this method. Tape cast methods are used for the fabrication of flexible crack-free thick ceramic sheets. Our objective was to develop nano-structured, crack-free, transparent Al2O3 film a few microns thick, has a highly porous and stable crystallographic nature. A metallic paste was printed by screen printing on both side of the film surface for electrodes to form a sensitive element. A silver wire (dia j=0.1mm lead was connected to a grid structure electrode using a silver paste spot for fine joining. Alumina is absorbs moisture molecules into its meso-porous layer and changes its electrical characteristics according to the moisture content, its dielectric constant increase as moisture increase. Moisture molecules can be conceived of as dipoles in random state before the application of an electric field. When the dipole orientation was changed from random to an equilibrium state under the application of external field, a large change in dielectric constant was observed. The number of water molecules absorbed determines the electrical impedance of the capacitor, which in turn is proportional to water vapor pressure.

  16. {gamma} alumina- and HY zeolite-supported molybdenum catalysts: characterisation of the oxidic and sulfided phases; Catalyseurs a base de molybdene supporte sur alumine {gamma} et zeolithe HY: caracterisation des phases oxydes et sulfures

    Energy Technology Data Exchange (ETDEWEB)

    Plazenet, G

    2001-10-01

    Oxidic precursors of hydro-treatment catalysts (Co)Mo/alumina or zeolite were characterised by Raman spectroscopy, NMR and EXAFS at the Mo and Co K-edges. The formation of an Anderson-type alumino-molybdate compound upon impregnation of the support with an ammonium hepta-molybdate solution was confirmed for alumina, and also observed for the HY zeolitic support, with consumption of the amorphous alumina of the zeolite. In absence of the latter, ammonium hepta-molybdate precipitates. The species are conserved upon drying; upon calcination, the alumino-molybdate evolves into a surface aluminium molybdate type phase, whereas the hepta-molybdate transforms into MoO{sub 3}. The species formed upon impregnation are located in the inter-granular porosity whereas MoO{sub 3} vapor-condensation leads to formation of dimers located inside the zeolitic structure. The study of the cobalt-promoted precursors showed that the evolution of the molybdenum is the same in the case of co-impregnation preparation. Impregnation with cobalt-molybdate prevents the formation of the alumino-molybdate anion and thus enables the preservation of the Mo-Co interaction but, whatever the precursor, the leveling effect of the calcination-re-hydration steps was demonstrated. An EXAFS study at different sulfur coverages of the MoS{sub 2} platelets in the alumina-supported sulfided catalysts showed the limitations of EXAFS for size determination of MoS{sub 2} crystallites, a parameter that can be reached by AWAXS, which also conveys information about sheet-stacking. The EXAFS study of sulfided (Co)Mo/HY systems revealed incomplete sulfidation of the samples and the very high dispersion of the active phase. The absence of an observable Mo-Co interaction whatever the preparation of the promoted catalysts is consistent with the absence of promoting effect in toluene hydrogenation. (author)

  17. Preparation and characterization of a nickel/alumina composite membrane for high temperature hydrogen separation. Application in a membrane reactor for the dry reforming of methane; De la synthese d'une membrane composite nikel/ceramique permselective a l'hydrogene au reacteur membranaire. Application au reformage du methane

    Energy Technology Data Exchange (ETDEWEB)

    Haag, St.

    2003-11-01

    The objective of this work was to develop composite inorganic membranes based on nickel or palladium supported on a porous ceramic for high temperature hydrogen separation. These membranes were used in a membrane reactor for the dry reforming of methane in order to shift the chemical equilibrium towards the production of hydrogen and carbon monoxide. The metal layers were deposited on a tubular alumina support by electroless plating. The Ni and the Pd layers are 1 micron thick. The hydrogen permeation tests were done for high temperatures. The Pd/ceramic membrane is permselective to hydrogen and the H{sub 2}/N{sub 2} separation factor (single gas) is 60 at 400 deg C with a transmembrane pressure difference of 1 bar. With a gas mixture, the H{sub 2}/N{sub 2} separation factor is 13. This membrane is not completely dense and the transport mechanism of hydrogen through the Pd layer is mixed: solution-diffusion through the metal bulk and surface diffusion through the defects of the film. However, an embrittlement of the palladium layer under hydrogen atmosphere was observed at 500 deg C. The Ni/ceramic membrane is stable until 600 deg C, its permselectivity to hydrogen increases with the temperature. The use of a sweep gas can provide a H{sub 2}/N{sub 2} separation factor (mixture) of about 25. The main diffusion mechanism is surface diffusion through the pores. Both membranes are not catalytic. Thus, some catalysts composed of nickel and cobalt supported on MgO, SiO{sub 2} or Al{sub 2}O{sub 3} were prepared. These systems allow to reach theoretical limits of conversion calculated for a conventional fixed bed reactor. In the membrane reactor, an enhancement of the methane conversion (15-20%) is observed with both membranes due the selective removal of hydrogen during the reaction. The Ni/ceramic membrane more stable, more permeable and as selective as the palladium one is a brand new material for high temperature hydrogen separation. (author)

  18. Porous Alumina Films with Width-Controllable Alumina Stripes

    Directory of Open Access Journals (Sweden)

    Huang Shi-Ming

    2010-01-01

    Full Text Available Abstract Porous alumina films had been fabricated by anodizing from aluminum films after an electropolishing procedure. Alumina stripes without pores can be distinguished on the surface of the porous alumina films. The width of the alumina stripes increases proportionally with the anodizing voltage. And the pores tend to be initiated close to the alumina stripes. These phenomena can be ascribed to the electric field distribution in the alumina barrier layer caused by the geometric structure of the aluminum surface.

  19. Porous Alumina Films with Width-Controllable Alumina Stripes

    Science.gov (United States)

    2010-01-01

    Porous alumina films had been fabricated by anodizing from aluminum films after an electropolishing procedure. Alumina stripes without pores can be distinguished on the surface of the porous alumina films. The width of the alumina stripes increases proportionally with the anodizing voltage. And the pores tend to be initiated close to the alumina stripes. These phenomena can be ascribed to the electric field distribution in the alumina barrier layer caused by the geometric structure of the aluminum surface. PMID:21170406

  20. Effects of gamma-irradiation on the electrokinetic properties of purple membranes

    International Nuclear Information System (INIS)

    Doltchinkova, V.; Baldjiiska, M.; Stoilova, S.

    1998-01-01

    The effect of gamma-irradiation (5, 10 and 15 Gy) on the kinetic surface charge of purple membranes (PM) was followed by means of particle microelectrophoresis. The changes in electrophoretic mobility (EPM) were examined at 2, 5 and 26 h, respectively, following irradiation of native PM, and at 2, 26, 50 h and 5 days following irradiation of delipidated PM. It was concluded that the high inhomogeneity of the suspension, even after sonication, largely affects the measured zeta-potential. The 15-Gy treatment significantly increased the net negative surface charge density at 5 and 26 h after irradiation of native PM. However, the opposite effect of approximately twofold reduction of EPM values was derived from simultaneous studies concerning their delipidated form. Low irradiation doses clearly induced an enhancement of negative surface charge density at 2 h post-exposure as well as the formation of unstable structures of delipidated PM. The changes in electrokinetic properties might reflect the specific aggregate formation in both native and delipidated PM. It was suggested that the effect observed of both types of PM was mainly a structural phenomenon possibly related to the modification of functionally active residues. (orig.)

  1. Effect of gamma-radiation on the structure and function of yeast membrane

    International Nuclear Information System (INIS)

    Khare, S.; Trivedi, A.; Kesavan, P.C.; Prasad, R.

    1982-01-01

    A decrease in the influx of several amino acids was observed following gamma-irradiation of Candida albicans strain 3100. At low dose (2.5 Gy), which does not affect cell survival, a stimulation in the uptake was visible; moreover, sulphydryl loss and lipid peroxidation were also evident. With further increase in the dose of radiation, a parallel increment in the loss of sulphydryl groups and production of malonaldehyde was observed. Radioprotectors like L-cysteine and dithiothreitol were shown to shield the radiation-induced loss of sulphydryl and damage to transport and survival. Reduced glutathione, on the other hand, exhibited protection at the level of sulphydryl damage only. N-ethylmaleimide, a well known hypoxic cell radiosensitizer, enhanced the radiosensitivity with respect to survival; it, however, had no effect on amino acid transport. Oxygen enhancement of radiation damage to transport and cell survival and the radioprotection by sodium formate under these circumstances, and more so by anoxia, were demonstrated. The results indicate that the manifestation of damage to membrane structure and function precedes any observable loss of survival. (author)

  2. Characterization of the microporous HDPE film with alpha alumina

    International Nuclear Information System (INIS)

    Park, Jong Seok; Sung, Hae Jun; Gwon, Hui Jeong; Lim, Youn Mook; Nho, Young Chang

    2010-01-01

    The effects of the addition of the alpha alumina on the properties of the microporous high density polyethylene (HDPE) films were investigated. The particle size and the specific surface area of alpha alumina were 400 nm and 7.3 m 2 g -1 . The HDPE and the alpha alumina were mixed to obtain the precursor film in the twin extruder. The precursor films were uni-axially stretched up to 600% in oven 120 .deg. C and then the stretched HDPE films were irradiated by gamma rays. The pore volume of the microporous HDPE films was increased with an increasing content of the alpha alumina. The mechanical characteristics of the microporous HDPE films were increased with a content of alpha alumina up to 15%, but decreased at 20%. The electrochemical stability of the microporous HDPE film containing alpha alumia was increased with an increased irradiation dose up ti 50 kGy

  3. Sequential Vapor Infiltration Treatment Enhances the Ionic Current Rectification Performance of Composite Membranes Based on Mesoporous Silica Confined in Anodic Alumina.

    Science.gov (United States)

    Liang, Yanyan; Liu, Zhengping

    2016-12-20

    Ionic current rectification of nanofluidic diode membranes has been studied widely in recent years because it is analogous to the functionality of biological ion channels in principle. We report a new method to fabricate ionic current rectification membranes based on mesoporous silica confined in anodic aluminum oxide (AAO) membranes. Two types of mesostructured silica nanocomposites, hexagonal structure and nanoparticle stacked structure, were used to asymmetrically fill nanochannels of AAO membranes by a vapor-phase synthesis (VPS) method with aspiration approach and were further modified via sequence vapor infiltration (SVI) treatment. The ionic current measurements indicated that SVI treatment can modulate the asymmetric ionic transport in prepared membranes, which exhibited clear ionic current rectification phenomenon under optimal conditions. The ionic current rectifying behavior is derived from the asymmetry of surface conformations, silica species components, and hydrophobic wettability, which are created by the asymmetrical filling type, silica depositions on the heterogeneous membranes, and the condensation of silanol groups. This article provides a considerable strategy to fabricate composite membranes with obvious ionic current rectification performance via the cooperation of the VPS method and SVI treatment and opens up the potential of mesoporous silica confined in AAO membranes to mimic fluid transport in biological processes.

  4. Changes induced by gamma radiation in microsomal membranes of storage of garlic; Cambios provocados por la radiacion gamma en membranas microsomales de hoja de reserva de ajo

    Energy Technology Data Exchange (ETDEWEB)

    Perez, M B; Croci, C A [Universidad Nacional del Sur, Bahia Blanca (Argentina). Laboratorio de Radioisotopos; Aveldano, M I [Universidad Nacional del Sur, Bahia Blanca (Argentina). Instituto de Investigaciones Bioquimicas

    2003-07-01

    This study evaluates the effects of the radio inhibition process on garlic bulbs in terms of phase properties of microsomal membranes and their lipid and fatty acid composition. Garlic bulbs were irradiated with an average dose of 60 Gy of {sup 60}Co gamma rays 30-40 days after harvest. The treatment was carried out in the facilities of the National Atomic Energy Commission (CNEA). Rough and smooth microsomal membranes were isolated by ultracentrifugation from tissues of irradiated and non-irradiated storage leaves. Wide angle X-ray diffractograms of both fractions were recorded along 270 days of storage. Lipids were separated by thin layer chromatography. The fatty acid composition of major lipid fractions was studied by gas-liquid chromatography. The diffractograms featured peaks at Bragg spacing of 4.15 Armstrong and 3.75 Armstrong, revealing the presence of a gel (crystalline) phase, while the characteristic peak of the liquid-crystalline phase (4.6 Armstrong) was not observed in both sorts of membranes. Irradiation was found to bring about modifications in the intensity of 4.15 Armstrong and 3.75 Armstrong peaks from smooth microsomal membranes, but not in the behaviour along the studied period. Data from the rough microsomal fraction were erratic. Parallel to these changes, radiation induced significant modifications in the level of smooth microsomal membrane triacylglycerols in relation to phospholipids and their fatty acids. These findings indicate that the storage leaf tissues of garlic are radiosensitive both in terms of physical and chemical properties of their microsomal membranes. From the practical point of view, these results could be the basis for the development of techniques to be applied to storage garlic to evaluate if it was irradiated. (author)

  5. Regulation of microtubule nucleation from membranes by complexes of membrane-bound gamma-tubulin with Fyn kinase and phosphoinositide 3-kinase

    Czech Academy of Sciences Publication Activity Database

    Macůrek, Libor; Dráberová, Eduarda; Richterová, Věra; Sulimenko, Vadym; Sulimenko, Tetyana; Dráberová, Lubica; Marková, Vladimíra; Dráber, Pavel

    2008-01-01

    Roč. 416, č. 3 (2008), s. 421-430 ISSN 0264-6021 R&D Projects: GA MŠk LC545; GA ČR GA204/05/2375; GA ČR GA304/04/1273; GA MŠk(CZ) 1M0520 Institutional research plan: CEZ:AV0Z50520514 Keywords : detergent -resistant membrane * Fyn * PI3K gamma-tubulin Subject RIV: EB - Genetics ; Molecular Biology Impact factor: 4.371, year: 2008

  6. Reuse of activated alumina

    Energy Technology Data Exchange (ETDEWEB)

    Hobensack, J.E. [Martin Marietta Energy Systems, Inc., Piketon, OH (United States)

    1991-12-31

    Activated alumina is used as a trapping media to remove trace quantities of UF{sub 6} from process vent streams. The current uranium recovery method employs concentrated nitric acid which destroys the alumina pellets and forms a sludge which is a storage and disposal problem. A recently developed technique using a distilled water rinse followed by three dilute acid rinses removes on average 97% of the uranium, and leaves the pellets intact with crush strength and surface area values comparable with new material. Trapping tests confirm the effectiveness of the recycled alumina as UF{sub 6} trapping media.

  7. Complexes of membrane-associated gamma-tubulin with Fyn kinase and phosphoinositide 3-kinase in differentiating cells

    Czech Academy of Sciences Publication Activity Database

    Sulimenko, Vadym; Macůrek, Libor; Dráberová, Eduarda; Richterová, Věra; Sulimenko, Tetyana; Dráberová, Lubica; Marková, Vladimíra; Dráber, Pavel

    2009-01-01

    Roč. 276, č. 1 (2009), s. 253-253 ISSN 1742-464X. [FEBS Congress /34/. 04.07.2009-09.07.2009, Praha] R&D Projects: GA MŠk 1M0506; GA MŠk LC545; GA ČR GA204/05/2375; GA ČR GA304/04/1273 Institutional research plan: CEZ:AV0Z50520514 Keywords : detergent -resistant membrane * Fyn * PI3K gamma-tubulin Subject RIV: EB - Genetics ; Molecular Biology

  8. Experimental investigation of nano-alumina effect on the filling time ...

    African Journals Online (AJOL)

    In this research, by producing composite samples made of glass fibers and epoxy resin with different percentages of nanoparticles (Nano-alumina), the adding effect of nanoparticles of alumina Alpha and Gamma grade on filling time in the vacuum assistant resin transfer molding process (VARTM) is investigated. The grade ...

  9. Gamma-ray-induced changes in hypodermal mesocarp tissue plasma membrane of pre- and post-storage muskmelon

    International Nuclear Information System (INIS)

    Lester, G.E.; Whitaker, B.D.

    1996-01-01

    Gamma irradiation (1.0 kGy) of intact, newly harvested, mature muskmelon fruit (Cucumis melo L. var. reticulatus Naud.) appears to have an immediate deleterious effect, but also a long-term beneficial effect, on the integrity and function of the plasma membrane (PM) of hypodermal mesocarp tissue. The initial consequences of gamma irradiation included an increase in the free sterol:phospholipid ratio, resulting at least in part from deglycosylation of steryl glycosides, a decrease in the spinasterol:7-stigmastenol ratio in each of the PM steryl lipids (free sterols, steryl glycosides, and acylated steryl glycosides), and a decrease in H+-ATPase activity. Irradiation did not increase protein loss, suggesting that the decrease in H+-ATPase activity resulted from either direct inactivation of the enzyme or altered PM ordering caused by the steryl lipid modifications. The long-term beneficial effects of irradiation, observed following 10 days of commercial storage, included greater retention of total PM protein, a diminished decline in total PM phospholipids (PL) and in the PL:protein ratio, and maintenance of greater overall H-ATPase activity (activity was the same as in controls on a per mg protein basis, but there was gt 30% more protein in the PM of stored irradiated fruit). These results indicate that 1 kGy gamma irradiation administered prior to storage slowes the progression of two key parameters of senescence, PM protein loss and PL catabolism

  10. Influence of additives on the stability of the phases of alumina; Influencia de aditivos na estabilidade das fases da alumina

    Energy Technology Data Exchange (ETDEWEB)

    Rosario, D.C.C.; Gouvea, D., E-mail: deisedorosario@usp.br [Universidade de Sao Paulo (USP), SP (Brazil). Departamento de Engenharia Metalurgica e de Materiais. Laboratorio de Processos Ceramicos

    2011-07-01

    Problems with the stability of gamma alumina in catalytic reactions have been solved with the inclusion of additives during the synthesis of alumina. These additives stabilize the temperature of phase transition allowing the use of metastable alumina at high temperatures, but the mechanisms of action of additives are not well defined. It is known that each family of additive or additives behaves in different ways for this stabilization. This work aimed to study the performance of MgO and ZrO{sub 2}, respectively at different concentrations in alumina synthesized via Pechini. The samples were analyzed by DSC, X-ray diffraction, measurement of specific surface area by BET analysis, and infrared analysis. The results showed an increase in transition temperature for both additives, and a different changes for specific surface area, showing that MgO and ZrO{sub 2} work on improving the stability but with distinct mechanisms. (author)

  11. Synthesis and characterization of platinum supported on alumina doped with cerium catalyst

    International Nuclear Information System (INIS)

    Yusof Abdullah; Abd Fatah Awang Mat; Mohd Ali Sufi; Sarimah Mahat; Razali Kassim; Nurhaslinda Abdullah.

    1996-03-01

    The synthesis and characterization of gamma-alumina doped with cerium as platinum support for the automobile exhaust catalyst are described. Platinum/alumina/ceria catalyst were prepared by impregnation of hexachloroplatinic acid and sintered at 500 degree Celsius to obtain metal dispersions of 1.0 wt%. Catalyst distribution inside the powder and the effects of the addition of cerium to alumina were analyzed by the scanning electron microscopy (SEM) and x-ray fluorescence spectroscopy (XRF). The results showed that the alumina - supported catalysts contained well dispersion of the noble metal

  12. Effect of gamma irradiation on membranes of normal and pathological erythrocytes (beta-thalassemia)

    International Nuclear Information System (INIS)

    Sportelli, L.; Bonincontro, A.; Cametti, C.; Consiglio Nazionale delle Ricerche, Rome

    1987-01-01

    The influence of ionizing radiation on the membrane of human normal erythrocytes has extensively been studied and a variety of effects including changes in the cation fluxes or in non-electrolytes permeability, in membrane fluidity, in peroxidation of unsaturated lipids as well as chemical composition or structural modifications has been observed. However, only few studies deal with the effects of ionizing radiation on pathological red blood cells. In this work, we have investigated by means of electron spin resonance (ESR) spectroscopy the effects of 60 Co γ-radiation on the normal and homozygous β-thalassemic human erythrocyte membranes. (orig.)

  13. Gamma radiation grafting process for preparing separator membranes for electrochemical cells

    International Nuclear Information System (INIS)

    Agostino, V.F. D'; Lee, J.Y.

    1982-01-01

    An irradiation grafting process for preparing separator membranes for use in electrochemical cells, comprises contacting a polymeric base film with an aqueous solution of a hydrophilic monomer and a polymerization retardant; and irradiating said contacted film to form a graft membrane having low electrical resistivity and having monomer molecules uniformly grafted thereon. In the examples (meth) acrylic acid is grafted on to polyethylene, polypropylene and polytetrafluoroethylene in the presence of ferrous sulphate or cupric sulphate as polymerization retardants. (author)

  14. High alumina refractories

    International Nuclear Information System (INIS)

    Simao, L.C.; Lopes, A.B.; Galvao Filho, N.B.; Souza, R.B. de

    1989-01-01

    High alumina refractories with 92 to 96.5% Al 2 O 3 were produced using brown and white fused as aggregate. Those refractories present only alumina-α and mullite as crystalline mineralogical phase. Other physical and chemical characteristics are similar to the ones found in refractories produced in Brazil, Japan and U.S.A. The most important physical and chemical tests used for the characterization of the raw materials and refractories, complemented by those realized at high temperatures, plus X-ray Difractometry and optical microscopy are presented, besides the refractory formulation and main parameters of production [pt

  15. Membrane Potential Dynamics of Spontaneous and Visually Evoked Gamma Activity in V1 of Awake Mice

    NARCIS (Netherlands)

    Perrenoud, Q.; Pennartz, C.M.A.; Gentet, L.J.

    2016-01-01

    Cortical gamma activity (30-80 Hz) is believed to play important functions in neural computation and arises from the interplay of parvalbumin-expressing interneurons (PV) and pyramidal cells (PYRs). However, the subthreshold dynamics underlying its emergence in the cortex of awake animals remain

  16. Analysis of Gas Separated for Silica Membrane in Hydrogen Gas Production by Using Nuclear Reactor Thermal

    International Nuclear Information System (INIS)

    Pandiangan, Tumpal

    2007-01-01

    One of the hydrogen production method that have been developed is a thermo-chemical method. This method is permissible to increase thermal efficiency up to 70 % and to decrease of operational temperature from 800℃ down to 450 ℃. One of several factor that can increase of the hydrogen production thermal efficiency at the above method is to apply a separated membrane that have a relative good for permeansce and selectivity performance. It had been carried out for analyzing of time and temperature CVD (Chemical Vapouration Deposition) that is affected to permeansce and power selecting performance of the membrane. The layering membrane silica process was carried out by means of the CVD method at atmosphere pressure. The membrane silica layering that was observed was developed by a CVD method in atmospheric pressure. The silica membrane was formed at the out side surface of the alumina gamma cylinder that had been coated by alumina gamma which it has average porosity about of 0.01 mic.meter. A permeansce and separation power performance of the membrane silica that was carried out by means of CVD method at 600 ℃ on H 2 , He and N 2 are : 2 x 10 -10 , 9 x 10 -9 and 4 x 10 -7 mol Pa/m 2 s and the selected power of H 2 /N 2 = 45. The permeansce of that membrane is relative good but the selected power is relative not so good. (author)

  17. Alumina Technology Roadmap

    Energy Technology Data Exchange (ETDEWEB)

    none,

    2002-02-01

    The Alumina Technology Roadmap outlines a comprehensive long-term research and development plan that defines the industry's collective future and establishes a clear pathway forward. It emphasizes twelve high-priority R&D areas deemed most significant in addressing the strategic goals.

  18. Effect of gamma radiation on the transport of spin-labeled compounds across the erythrocyte membrane

    International Nuclear Information System (INIS)

    Gwozdzinski, K.; Bartosz, G.; Leyko, W.

    1981-01-01

    The effect of ionizing radiation on the non-electrolyte, anion and cation permeability of the erythrocyte membrane was studied by measurement of the reduction rate of appropriate nitroxyl derivatives. Irradiation of bovine erythrocytes in the dose-range of 2-50 krad resulted in a regular dose-dependent increase in the reduction rates of a cation (TEMPO-choline) and a hydrophobic non-electrolyte (TEMPO), and non-regular changes in the reduction rate of a hydrophilic non-electrolyte (TEMPOL). The permeation constant for TEMPO-choline also showed a non-regular response to radiation, similar to the response pattern of other red blood cell parameters. These results also demonstrate that the effects of radiation on the transport of various solutes can be used as a means of distinguishing between different channels of membrane transport. (orig.)

  19. Preparation of alumina microspheres

    International Nuclear Information System (INIS)

    Santos, W.R. dos; Abrao, A.

    1980-01-01

    Inorganic exchangers are widely used for adsorption and column partition chromatography. The main difficulty of using commercial alumina (in powder) for column chromatography is related to its packing, and the operations through the column become diffcult and time-consuming; also it turns to be virtually impossible to use large dimension columns. In order to eliminate these problems, a process for the preparation of alumina micro-spheres was developed as an adaptation of a similar process used to prepare nuclear fuel microspheres (UO 2 , ThO 2 ). The flowsheet of this process is presented together with the analytical results of sphericity after calcination, granulometry, density and characterization by X-ray diffractometry. Solubility tests showed that the so-prepared microspheres are well resistant to strong acids and bases; retention tests showed their efficiency, mainly to copper. (C.L.B.) [pt

  20. Uranyl sorption onto alumina

    International Nuclear Information System (INIS)

    Jacobsson, A.M.M.

    1997-01-01

    The mechanism for the adsorption of uranyl onto alumina from aqueous solution was studied experimentally and the data were modeled using a triple layer surface complexation model. The experiments were carried out at low uranium concentrations (9 x 10 -11 --5 x 10 -8 M) in a CO 2 free environment at varying electrolyte concentrations (0.01--1 M) and pH (4.5--12). The first and second acid dissociation constants, pK a1 and pK a2 , of the alumina surface were determined from potentiometric titrations to be 7.2 ± 0.6 and 11.2 ± 0.4, respectively. The adsorption of uranium was found to be independent of the electrolyte concentration. The authors therefore conclude that the uranium binds as an inner sphere complex. The results were modeled using the code FITEQL. Two reactions of uranium with the surface were needed to fit the data, one forming a uranyl complex with a single surface hydroxyl and the other forming a bridged or bidentate complex reacting with two surface hydroxyls of the alumina. There was no evidence from these experiments of site heterogeneity. The constants used for the reactions were based in part on predictions made utilizing the Hard Soft Acid Base, HSAB, theory, relating the surface complexation constants to the hydrolysis of the sorbing metal ion and the acid dissociation constants of the mineral oxide surface

  1. Gamma-irradiation and neutron effect on DNA-membrane complexes of mammalian cells

    International Nuclear Information System (INIS)

    Lapidus, I.L.; Nazarov, V.M.; Ehrtsgreber, G.

    1984-01-01

    The first results of radiobiological investigations in the biophysical channel of the JINR reactor IBR-2 are presented. Sedimentation behaviour of DNA-membrane complexes has been studied at irradiation of the Chinese hamster cells (VT9-4) in a wide dose range of 137 Cs γ-irradiation and neutrons. An earlier assumption of the authors on the role of DNA double-strand breaks in changing the relative sedimentation velocity of complexes at irradiation of cells with doses over 50 Gy has been confirmed

  2. Concanavalin A/IFN-gamma triggers autophagy-related necrotic hepatocyte death through IRGM1-mediated lysosomal membrane disruption.

    Directory of Open Access Journals (Sweden)

    Chih-Peng Chang

    Full Text Available Interferon-gamma (IFN-γ, a potent Th1 cytokine with multiple biological functions, can induce autophagy to enhance the clearance of the invading microorganism or cause cell death. We have reported that Concanavalin A (Con A can cause autophagic cell death in hepatocytes and induce both T cell-dependent and -independent acute hepatitis in immunocompetent and immunodeficient mice, respectively. Although IFN-γ is known to enhance liver injury in Con A-induced hepatitis, its role in autophagy-related hepatocyte death is not clear. In this study we report that IFN-γ can enhance Con A-induced autophagic flux and cell death in hepatoma cell lines. A necrotic cell death with increased lysosomal membrane permeabilization (LMP is observed in Con A-treated hepatoma cells in the presence of IFN-γ. Cathepsin B and L were released from lysosomes to cause cell death. Furthermore, IFN-γ induces immunity related GTPase family M member 1(IRGM1 translocation to lysosomes and prolongs its activity in Con A-treated hepatoma cells. Knockdown of IRGM1 inhibits the IFN-γ/Con A-induced LMP change and cell death. Furthermore, IFN-γ(-/- mice are resistant to Con A-induced autophagy-associated necrotic hepatocyte death. We conclude that IFN-γ enhances Con A-induced autophagic flux and causes an IRGM1-dependent lysosome-mediated necrotic cell death in hepatocytes.

  3. Study of cross-linking reactions induced by gamma rays in hybrid membranes of Bisphenol-A-Polysulfone and precipitated silica

    International Nuclear Information System (INIS)

    Furtado Filho, Acacio Antonio M.; Gomes, Ailton de S.; Lopes, Lea; Benzi, Marcia R.

    2011-01-01

    In this work the bisphenol-A-polysulfone (PSF) was sulfonated using trimethyl silyl chlorosulfonate [(CH 3 ) 3 SiSO 3 Cl] as a mild sulfonating agent in a homogeneous solution of dichloroethane. The sulfonation reaction was confirmed by acid-base titration and FTIR-spectroscopy analysis. The hybrid membranes were obtained by casting the sulfonated bisphenol-A-polysulfone (SPSF) and precipitated silica Tixosil R 333 solutions in N-N-dimethylacetamide. Cross-linking in the hybrid membranes was obtained by irradiation, with doses ranging from 5 to 30 kGy using gamma ray from a 60 Co source. The water uptake and the swelling of the membranes were estimated by measuring the change in weight between dry and wet conditions. The conductivity of the membranes in acid form was measured with the ac impedance technique using a PGSTAT30 frequency response analyzer. The hybrid cross-linked membranes have conductivity close to 10-1 S.cm -1 at 100% RH and 80 deg C. Electrochemical performances, thermo-mechanical stability and low cost make this cross-linked SPSF hybrid membrane an attractive material for fuel cells using a proton exchange membrane. (author)

  4. Bauxite Mining and Alumina Refining

    Science.gov (United States)

    Frisch, Neale; Olney, David

    2014-01-01

    Objective: To describe bauxite mining and alumina refining processes and to outline the relevant physical, chemical, biological, ergonomic, and psychosocial health risks. Methods: Review article. Results: The most important risks relate to noise, ergonomics, trauma, and caustic soda splashes of the skin/eyes. Other risks of note relate to fatigue, heat, and solar ultraviolet and for some operations tropical diseases, venomous/dangerous animals, and remote locations. Exposures to bauxite dust, alumina dust, and caustic mist in contemporary best-practice bauxite mining and alumina refining operations have not been demonstrated to be associated with clinically significant decrements in lung function. Exposures to bauxite dust and alumina dust at such operations are also not associated with the incidence of cancer. Conclusions: A range of occupational health risks in bauxite mining and alumina refining require the maintenance of effective control measures. PMID:24806720

  5. A study of the isobutane dehydrogenation in a porous membrane catalytic reactor: design, use and modelling

    Energy Technology Data Exchange (ETDEWEB)

    Casanave, D

    1996-01-26

    The aim of this study was to set up and model a catalytic fixed-bed membrane reactor for the isobutane dehydrogenation. The catalyst, developed at Catalysis Research Institute (IRC), was a silicalite-supported Pt-based catalyst. Their catalytic performances (activity, selectivity, stability) where found better adapted to the membrane reactor, when compared with commercial Pt or Cr based catalysts. The kinetic study of the reaction has been performed in a differential reactor and led to the determination of a kinetic law, suitable when the catalyst is used near thermodynamic equilibrium. The mass transfer mechanisms were determined in meso-porous and microporous membranes through both permeability and gas mixtures (iC{sub 4}/H{sub 2}/N{sub 2}) separation measurements. For the meso-porous {gamma}-alumina, the mass transfer is ensured by a Knudsen diffusion mechanism which can compete with surface diffusion for condensable gas like isobutane. The resulting permselectivity H{sub 2}/iC4 of this membrane is low ({approx} 4). For the microporous zeolite membrane, molecular sieving occurs due to steric hindrance, leading to higher permselectivity {approx}14. Catalyst/membrane associations were compared in terms of isobutane dehydrogenation performances, for both types of membranes (meso-porous and microporous) and for two different reactor configurations (co-current and counter-current sweep gas flow). The best experimental results were obtained with the zeolite membrane, when sweeping the outer compartment in a co-current flow. The equilibrium displacement observed with the {gamma}-alumina membrane was lower and mainly due to a dilution effect of the reaction mixture by the sweep gas. A mathematical model was developed, which correctly describes all the experimental results obtained with the zeolite membrane, when the co-current mode is used. (Abstract Truncated)

  6. Enriched fluoride sorption using alumina/chitosan composite

    Energy Technology Data Exchange (ETDEWEB)

    Viswanathan, Natrayasamy, E-mail: natrayasamy_viswanathan@rediffmail.com [Department of Chemistry, Anna University Tiruchirappalli - Dindigul Campus, Dindigul 624 622, Tamil Nadu (India); Meenakshi, S., E-mail: drs_meena@rediffmail.com [Department of Chemistry, Gandhigram Rural University, Gandhigram 624 302, Tamil Nadu (India)

    2010-06-15

    Alumina possesses an appreciable defluoridation capacity (DC) of 1566 mg F{sup -}/kg. In order to improve its DC, it is aimed to prepare alumina polymeric composites using the chitosan. Alumina/chitosan (AlCs) composite was prepared by incorporating alumina particles in the chitosan polymeric matrix, which can be made into any desired form viz., beads, candles and membranes. AlCs composite displayed a maximum DC of 3809 mg F{sup -}/kg than the alumina and chitosan (52 mg F{sup -}/kg). The fluoride removal studies were carried out in batch mode to optimize the equilibrium parameters viz., contact time, pH, co-anions and temperature. The equilibrium data was fitted with Freundlich and Langmuir isotherms to find the best fit for the sorption process. The calculated values of thermodynamic parameters indicate the nature of sorption. The surface characterisation of the sorbent was performed by FTIR, AFM and SEM with EDAX analysis. A possible mechanism of fluoride sorption by AlCs composite has been proposed. Suitability of AlCs composite at field conditions was tested with a field sample taken from a nearby fluoride-endemic village. This work provides a potential platform for the development of defluoridation technology.

  7. Proton adsorption onto alumina: extension of multisite complexation (MUSIC) theory

    Energy Technology Data Exchange (ETDEWEB)

    Nagashima, K.; Blum, F.D.

    1999-09-01

    The adsorption isotherm of protons onto a commercial {gamma}-alumina sample was determined in aqueous nitric acid with sodium nitrate as a background electrolyte. Three discrete regions could be discerned in the log-log plots of the proton isotherm determined at the solution pH 5 to 2. The multisite complexation (MUSIC) model was modified to analyze the simultaneous adsorption of protons onto various kinds of surface species.

  8. Long-term results of uncemented alumina acetabular implants.

    Science.gov (United States)

    Boehler, M; Knahr, K; Plenk, H; Walter, A; Salzer, M; Schreiber, V

    1994-01-01

    We report the clinical and tribological performance of 67 ceramic acetabular prostheses implanted between 1976 and 1979 without bone cement. They articulated with ceramic femoral heads mounted on mental femoral stems. After a mean elapsed period of 144 months, 59 sockets were radiographically stable but two showed early signs and six showed late signs of loosening. Four of the loose sockets have been revised. Histological analysis of the retrieved tissue showed a fibrous membrane around all the implants, with fibrocartilage in some. There was no bone ingrowth, and the fibrous membrane was up to 6 mm thick and infiltrated with lymphocytes, plasma cells, and macrophages. Intra- and extracellular birefringent wear particles were seen. Tribological analysis showed total wear rates in two retrieved alumina-on-alumina joints of 2.6 microns per year in a stable implant and 68 microns in a loose implant. Survival analysis showed a revision rate of 12.4% at 136 months.

  9. Antibacterial Activity of Zinc Oxide-Coated Nanoporous Alumina

    Science.gov (United States)

    2012-05-17

    made nanoporous alumina membranes, which were created by means of anodic oxidation of aluminum in an oxalic acid electrolyte, for treatment of skin...this study. All of the solutions were prepared using 18 M de-ionized water (lab supply) and trace metal grade nitric acid (Thermo Fisher Scientific...low production cost, repro- ducible reproduction, and facile reproduction approach for these materials. Using in vitro studies, keratinocytes (HaCaT

  10. Study of carbon-doped micro and nano sized alumina for radiation dosimetry applications

    International Nuclear Information System (INIS)

    Fontainha, C. C. P.; Alves, N.; Ferraz, W. B.; Faria, L. O.

    2017-10-01

    New materials have been widely investigated for ionizing radiation dosimetry for medical procedures. Carbon-doped doped alumina (Al 2 O 3 :C) have been proposed as thermoluminescent and photo luminescent dosimeters. In the present study nano and micro-sized alumina doped with different percentages of carbon, sintered under different atmosphere conditions, at temperatures ranging from 1300 to 1750 degrees Celsius, were sintered and their dosimetric characteristics for gamma fields were investigated. Among the investigated sample preparation methods, the micro-sized alumina doped with 0.01% of carbon and sintered at 1700 degrees Celsius under reducing atmosphere has presented the best Tl output, comparable to the best Tl sensitivities ever reported to alumina and better efficiency than the nano-sized alumina synthesized in this study. The influence of humidity in the Tl signal has been evaluated to be -4.0%. The micro-sized alumina obtained by the methodology used in this work is a suitable candidate for application in X and gamma radiation dosimetry. (Author)

  11. A clinical trial on the treatment of burns in children at the University Teaching Hospital using amniotic membrane sterilized by gamma radiation (July to December 1994)

    International Nuclear Information System (INIS)

    Katebe, K.R.C.

    1995-01-01

    About six hundred patients are admitted to the University Teaching Hospital every year. Most of the burns are from water and fire with a high mortality rate in children. This study was centred on the feasibility of using amniotic membrane for wound dressing. The method of Gamma radiation was employed to sterilize this biological tissue before utilising it on patients. The results of the study show more superior healing rate compared with other methods. There was lack of hypersensitivity reactions and reduced wound infection and good quality wound healing. The method is easy to use and has been accepted by the patients and nursing staff. (n.m.). 20 refs., tabs., 6 graphs

  12. Influence of additives on the stability of the phases of alumina

    International Nuclear Information System (INIS)

    Rosario, D.C.C.; Gouvea, D.

    2011-01-01

    Problems with the stability of gamma alumina in catalytic reactions have been solved with the inclusion of additives during the synthesis of alumina. These additives stabilize the temperature of phase transition allowing the use of metastable alumina at high temperatures, but the mechanisms of action of additives are not well defined. It is known that each family of additive or additives behaves in different ways for this stabilization. This work aimed to study the performance of MgO and ZrO 2 , respectively at different concentrations in alumina synthesized via Pechini. The samples were analyzed by DSC, X-ray diffraction, measurement of specific surface area by BET analysis, and infrared analysis. The results showed an increase in transition temperature for both additives, and a different changes for specific surface area, showing that MgO and ZrO 2 work on improving the stability but with distinct mechanisms. (author)

  13. Nanoporous alumina as templates for multifunctional applications

    Science.gov (United States)

    Sousa, C. T.; Leitao, D. C.; Proenca, M. P.; Ventura, J.; Pereira, A. M.; Araujo, J. P.

    2014-09-01

    Due to its manufacturing and size tailoring ease, porous anodic alumina (PAA) templates are an elegant physical-chemical nanopatterning approach and an emergent alternative to more sophisticated and expensive methods currently used in nanofabrication. In this review, we will describe the ground work on the fabrication methods of PAA membranes and PAA-based nanostructures. We will present the specificities of the electrochemical growth processes of multifunctional nanomaterials with diversified shapes (e.g., nanowires and nanotubes), and the fabrication techniques used to grow ordered nanohole arrays. We will then focus on the fabrication, properties and applications of magnetic nanostructures grown on PAA and illustrate their dependence on internal (diameter, interpore distance, length, composition) and external (temperature and applied magnetic field intensity and direction) parameters. Finally, the most outstanding experimental findings on PAA-grown nanostructures and their trends for technological applications (sensors, energy harvesting, metamaterials, and biotechnology) will be addressed.

  14. Comparative study of selenite adsorption on carbon based adsorbents and activated alumina.

    Science.gov (United States)

    Jegadeesan, G; Mondal, K; Lalvani, S B

    2003-08-01

    The sorption characteristics of carbon-based adsorbents such as activated carbon and chitin for the removal of selenite, Se (IV), an anionic, hazardous contaminant, are compared with those of alpha and gamma alumina. Batch experiments were conducted to determine the influence of pH, concentration of adsorbate, adsorbent loading and temperature on the sorption characteristics of the adsorbents. Generally, low pH of the solution resulted in favorable selenium removal. With the exception of activated carbon, uptakes decreased with increase in temperature. In comparison, chitin was found to be far less effective for the removal of Se (IV) from aqueous solutions. The data also showed that gamma alumina provided higher selenium removal percentages (99%) compared to alpha alumina (94%), activated carbon (87%) and chitin (49%). The selenite removal was found to decrease with increasing initial Se (IV) concentration in the solution. Adsorption capacities of the adsorbents are reported in terms of their Langmuir adsorption isotherms. The adsorption capacity (on unit mass basis) of the adsorbents for selenite is in the order: chitin (specific area (sa) = 9.58 m2 g(-1)) activated carbon (sa = 96.37 m2 g(-1)) < alpha alumina (sa = 6 m2 g(-1)) < gamma alumina (sa = 150 m2 g(-1)).

  15. Structural Study and Modification of Support Layer for Forward Osmosis Membranes

    KAUST Repository

    Shi, Meixia

    2016-01-01

    polymerization. Among the different substrates we include standard asymmetric porous membranes prepared from homopolymers, such as polysulfone. Additionally block copolymer membrane and Anodisc alumina membrane are chosen based on their exceptional structures

  16. Gelcasting polycrystalline alumina

    Energy Technology Data Exchange (ETDEWEB)

    Janney, M.A. [Oak Ridge National Lab., TN (United States)

    1997-04-01

    This work is being done as part of a CRADA with Osram-Sylvania, Inc. (OSI) OSI is a major U.S. manufacturer of high-intensity lighting. Among its products is the Lumalux{reg_sign} line of high-pressure sodium vapor arc lamps, which are used for industrial, highway, and street lighting. The key to the performance of these lamps is the polycrystalline alumina (PCA) tube that is used to contain the plasma that is formed in the electric arc. That plasma consists of ionized sodium, mercury, and xenon vapors. The key attributes of the PCA tubes are their transparency (95% total transmittance in the visible region), their refractoriness (inner wall temperature can reach 1400{degrees}C), and their chemical resistance (sodium and mercury vapor are extremely corrosive). The current efficiency of the lamps is very high, on the order of several hundred lumens / watt. (Compare - incandescent lamps -13 lumens/watt fluorescent lamps -30 lumens/watt.) Osram-Sylvania would like to explore using gelcasting to form PCA tubes for Lumalux{reg_sign} lamps, and eventually for metal halide lamps (known as quartz-halogen lamps). Osram-Sylvania, Inc. currently manufactures PCA tubes by isostatic pressing. This process works well for the shapes that they presently use. However, there are several types of tubes that are either difficult or impossible to make by isostatic pressing. It is the desire to make these new shapes and sizes of tubes that has prompted Osram-Sylvania`s interest in gelcasting. The purpose of the CRADA is to determine the feasibility of making PCA items having sufficient optical quality that they are useful in lighting applications using gelcasting.

  17. Synthesis and characterization of microporous inorganic membranes for propylene/propane separation

    Science.gov (United States)

    Ma, Xiaoli

    Membrane-based gas separation is promising for efficient propylene/propane (C3H6/C3H8) separation with low energy consumption and minimum environment impact. Two microporous inorganic membrane candidates, MFI-type zeolite membrane and carbon molecular sieve membrane (CMS) have demonstrated excellent thermal and chemical stability. Application of these membranes into C3H6/C3H 8 separation has not been well investigated. This dissertation presents fundamental studies on membrane synthesis, characterization and C3H 6/C3H8 separation properties of MFI zeolite membrane and CMS membrane. MFI zeolite membranes were synthesized on α-alumina supports by secondary growth method. Novel positron annihilation spectroscopy (PAS) techniques were used to non-destructively characterize the pore structure of these membranes. PAS reveals a bimodal pore structure consisting of intracrystalline zeolitic micropores of ~0.6 nm in diameter and irregular intercrystalline micropores of 1.4 to 1.8 nm in size for the membranes. The template-free synthesized membrane exhibited a high permeance but a low selectivity in C3H 6/C3H8 mixture separation. CMS membranes were synthesized by coating/pyrolysis method on mesoporous gamma-alumina support. Such supports allow coating of thin, high-quality polymer films and subsequent CMS membranes with no infiltration into support pores. The CMS membranes show strong molecular sieving effect, offering a high C3H 6/C3H8 mixture selectivity of ~30. Reduction in membrane thickness from 500 nm to 300 nm causes an increase in C3H8 permeance and He/N2 selectivity, but a decrease in the permeance of He, N 2 and C3H6 and C3H6/C 3H8 selectivity. This can be explained by the thickness dependent chain mobility of the polymer film resulting in final carbon membrane of reduced pore size with different effects on transport of gas of different sizes, including possible closure of C3H6-accessible micropores. CMS membranes demonstrate excellent C3H6/C 3H8 separation

  18. ATOMIC LAYER DEPOSITION OF TITANIUM OXIDE THIN FILMS ONNANOPOROUS ALUMINA TEMPLATES FOR MEDICAL APPLICATIONS

    Energy Technology Data Exchange (ETDEWEB)

    Brigmon, R.

    2009-05-05

    Nanostructured materials may play a significant role in controlled release of pharmacologic agents for treatment of cancer. Many nanoporous polymer materials are inadequate for use in drug delivery. Nanoporous alumina provides several advantages over other materials for use in controlled drug delivery and other medical applications. Atomic layer deposition was used to coat all the surfaces of the nanoporous alumina membrane in order to reduce the pore size in a controlled manner. Both the 20 nm and 100 nm titanium oxide-coated nanoporous alumina membranes did not exhibit statistically lower viability compared to the uncoated nanoporous alumina membrane control materials. In addition, 20 nm pore size titanium oxide-coated nanoporous alumina membranes exposed to ultraviolet light demonstrated activity against Escherichia coli and Staphylococcus aureus bacteria. Nanostructured materials prepared using atomic layer deposition may be useful for delivering a pharmacologic agent at a precise rate to a specific location in the body. These materials may serve as the basis for 'smart' drug delivery devices, orthopedic implants, or self-sterilizing medical devices.

  19. A novel technique for synthesizing dense alumina nanostructures

    Energy Technology Data Exchange (ETDEWEB)

    Pancholi, A [Department of Materials Science and Engineering, University of Delaware, Newark, DE 19716 (United States); Stoleru, V G [Department of Materials Science and Engineering, University of Delaware, Newark, DE 19716 (United States); Kell, C D [Department of Chemical Engineering, University of Delaware, Newark, DE 19716 (United States)

    2007-05-30

    The formation of highly ordered nanoporous alumina membranes by anodizing high-purity aluminium under optimum conditions (i.e., anodization time, electrolyte temperature, and cell voltage) in various electrolyte solutions is a well established process. In this paper we report on the formation of a wide range of alumina nanostructures, including nanotubes/nanochannels, nanoplates, and nanofibres, by using a technique that involves anodization and etching processing steps similar to the ones that yield nanopores, under slightly modified experimental conditions. The effects of the anodization voltage, time, and temperature, as well as the effects of the etching time, on the formation and the properties of the alumina nanostructures are analysed. We propose a simple analytical model to describe the formation of different types of alumina nanostructures, as a result of irreversible breakage of the pore walls for long etching times. The geometry of the nanostructures and their dimensions, ranging between 10 and 100 nm, were found to be dependent on the pore dimensions and on the location of the cleavage/breakage of the pore walls.

  20. Alumina Yield in the Bayer Process

    Science.gov (United States)

    Den Hond, R.

    The alumina industry has historically been able to reduce alumina production costs, by increasing the liquor alumina yield. To know the potential for further yield increases, the phase diagram of the ternary system Na2O-Al2O -H2O at various temperature levels was analysed. It was found that the maximum theorical precipitation alumina yield is 160 g/l, while that for digestion was calculated to be 675 g/l.

  1. Sintering behaviour of spinel–alumina composites

    Indian Academy of Sciences (India)

    % alumina dissolves in spinel (MgAl2O4) at 1600°C. Solid solubility of alumina in spinel decreases rapidly with decreasing temperature, which causes exsolution of alumina from spinel phase. Previous work of one of the authors revealed that ...

  2. Dynamic tensile response of alumina-Al composites

    International Nuclear Information System (INIS)

    Atisivan, R.; Bandyopadhyay, A.; Gupta, Y. M.

    2002-01-01

    Plate impact experiments were carried out to examine the high strain-rate tensile response of alumina-aluminum (Al) composites with tailored microstructures. A novel processing technique was used to fabricate interpenetrating phase alumina-aluminum composites with controlled microstructures. Fused deposition modeling (FDM), a commercially available rapid prototyping technique, was used to produce the controlled porosity mullite ceramic preforms. Alumina-Al composites were then processed via reactive metal infiltration of porous mullite ceramics. With this approach, both the micro as well as the macro structures can be designed via computer aided design (CAD) to tailor the properties of the composites. Two sets of dynamic tensile experiments were performed. In the first, the metal content was varied between 23 and 39 wt. percent. In the second, the microstructure was varied while holding the metal content nearly constant. Samples with higher metal content, as expected, displayed better spall resistance. For a given metal content, samples with finer metal diameter showed better spall resistance. Relationship of the microstructural parameters on the dynamic tensile response of the structured composites is discussed here

  3. Transport properties of alumina nanofluids

    International Nuclear Information System (INIS)

    Wong, Kau-Fui Vincent; Kurma, Tarun

    2008-01-01

    Recent studies have showed that nanofluids have significantly greater thermal conductivity compared to their base fluids. Large surface area to volume ratio and certain effects of Brownian motion of nanoparticles are believed to be the main factors for the significant increase in the thermal conductivity of nanofluids. In this paper all three transport properties, namely thermal conductivity, electrical conductivity and viscosity, were studied for alumina nanofluid (aluminum oxide nanoparticles in water). Experiments were performed both as a function of volumetric concentration (3-8%) and temperature (2-50 deg. C). Alumina nanoparticles with a mean diameter of 36 nm were dispersed in water. The effect of particle size was not studied. The transient hot wire method as described by Nagaska and Nagashima for electrically conducting fluids was used to test the thermal conductivity. In this work, an insulated platinum wire of 0.003 inch diameter was used. Initial calibration was performed using de-ionized water and the resulting data was within 2.5% of standard thermal conductivity values for water. The thermal conductivity of alumina nanofluid increased with both increase in temperature and concentration. A maximum thermal conductivity of 0.7351 W m -1 K -1 was recorded for an 8.47% volume concentration of alumina nanoparticles at 46.6 deg. C. The effective thermal conductivity at this concentration and temperature was observed to be 1.1501, which translates to an increase in thermal conductivity by 22% when compared to water at room temperature. Alumina being a good conductor of electricity, alumina nanofluid displays an increasing trend in electrical conductivity as volumetric concentration increases. A microprocessor-based conductivity/TDS meter was used to perform the electrical conductivity experiments. After carefully calibrating the conductivity meter's glass probe with platinum tip, using a standard potassium chloride solution, readings were taken at various

  4. Activity of adenylate cyclase in plasma membranes of pulmonary tissue remote times following nonlethal gamma-irradiation of rats

    International Nuclear Information System (INIS)

    Slozhenkina, L.V.; Ruda, V.P.; Ushakova, T.E.; Kuzin, A.M.

    1990-01-01

    Basal and stimulated activity of adenylate cyclase (cyclizing ATP-pyrophosphate lyase, E.C. 4.6.1.1., AC) in plasma membranes of pumonary tissye was being studied during a year after fractionated irradiation of rats (2 Gyx3). Basal and hormone-stimulated activity of AC was shown to vary significantly from normal 6 and 12 months after irradiation. The exposed membranes responded differently to AC activation by isoproterenol and F -

  5. Ultrasonic control of ceramic membrane fouling by particles: effect of ultrasonic factors.

    Science.gov (United States)

    Chen, Dong; Weavers, Linda K; Walker, Harold W

    2006-07-01

    Ultrasound at 20 kHz was applied to a cross-flow ultrafiltration system with gamma-alumina membranes in the presence of colloidal silica particles to systematically investigate how ultrasonic factors affect membrane cleaning. Based on imaging of the ultrasonic cavitation region, optimal cleaning occurred when the membrane was outside but close to the cavitation region. Increasing the filtration pressure increased the compressive forces driving cavitation collapse and resulted in fewer cavitation bubbles absorbing and scattering sound waves and increasing sound wave penetration. However, an increased filtration pressure also resulted in greater permeation drag, and subsequently less improvement in permeate flux compared to low filtration pressure. Finally, pulsed ultrasound with short pulse intervals resulted in permeate flux improvement close to that of continuous sonication.

  6. The characterization of ceramic alumina prepared by using additive glass beads

    Science.gov (United States)

    Suprapedi; Muljadi; Sardjono, Priyo

    2018-01-01

    The ceramic alumina has been made by using additive glass bead (5 and 10 % wt.). There are two kinds of materials, such as : gamma Alumina and glass bead. Synthesis of alumina was done by ball milling for 24 hours, then the mixed powder was dried in drying oven at 100 °C for 6 hours. Furthermore, the dried powder was mixed by using 2 % of PVA and continued with compacted to form a pellet with pressure of 50 MPA. The next step is sintering process with variation temperature of 1150, 1200, 1250, 1300 and 1400 °C and holding time for 2 hours. The characterization conducted are consist of test density, hardness, shrinkage, and microstructure. The results show that ceramic alumina with addition of 10 % wt. glass bead has the higher value of density, hardness and shrinkage than addition of 5% wt. glass bead. The highest characterization of ceramic alumina with addition 10 % glass bead was achieved at sintering temperature of 1400 °C with density 3.68 g/cm3, hardness vickers 780.40 Hv and shrinkage 15.23 %. The XRD results show that it was founds a corrundum (alpha Alumina) as dominant phase and mullite as minor phase.

  7. Beneficial effects of gamma linolenic acid supplementation on nerve conduction velocity, Na+, K+ ATPase activity, and membrane fatty acid composition in sciatic nerve of diabetic rats.

    Science.gov (United States)

    Coste, T; Pierlovisi, M; Leonardi, J; Dufayet, D; Gerbi, A; Lafont, H; Vague, P; Raccah, D

    1999-07-01

    Metabolic and vascular abnormalities are implicated in the pathogenesis of diabetic neuropathy. Two principal metabolic defects are altered lipid metabolism resulting from the impairment of delta-6-desaturase, which converts linoleic acid (LA) into gamma linolenic acid (GLA), and reduced nerve Na+, K+ ATPase activity. This reduction may be caused by a lack of incorporation of (n-6) fatty acids in membrane phospholipids. Because this ubiquitous enzyme maintains the membrane electrical potential and allows repolarization, disturbances in its activity can alter the process of nerve conduction velocity (NCV). We studied the effects of supplementation with GLA (260 mg per day) on NCV, fatty acid phospholipid composition, and Na+, K+ ATPase activity in streptozotocin-diabetic rats. Six groups of 10 rats were studied. Two groups served as controls supplemented with GLA or sunflower oil (GLA free). Two groups with different durations of diabetes were studied: 6 weeks with no supplementation and 12 weeks supplemented with sunflower oil. To test the ability of GLA to prevent or reverse the effects of diabetes, two groups of diabetic rats were supplemented with GLA, one group for 12 weeks and one group for 6 weeks, starting 6 weeks after diabetes induction. Diabetes resulted in a 25% decrease in NCV (P < 0.0001), a 45% decrease in Na+, K+ ATPase activity (P < 0.0001), and an abnormal phospholipid fatty acid composition. GLA restored NCV both in the prevention and reversal studies and partially restored Na+, K+ ATPase activity in the preventive treatment group (P < 0.0001). These effects were accompanied by a modification of phospholipid fatty acid composition in nerve membranes. Overall, the results suggest that membrane fatty acid composition plays a direct role in NCV and confirm the beneficial effect of GLA supplementation in diabetic neuropathy.

  8. Infrasonic backpulsed membrane cleaning of micro- and ...

    African Journals Online (AJOL)

    Membrane fouling is universally considered to be one of the most critical problems in the wider application of membrane filtration. In this research microfiltration and ultrafiltration membranes were fouled during a cross-flow filtration process, using yeast and alumina suspensions in a flat cell. Infrasonic backpulsing directly ...

  9. Low temperature synthesis of nano alpha-alumina powder by two-step hydrolysis

    International Nuclear Information System (INIS)

    Yan, Ting; Guo, Xiaode; Zhang, Xiang; Wang, Zhixiang; Shi, Jinqiu

    2016-01-01

    Highlights: • The nano α-Al 2 O 3 with good dispersion was prepared by two-step hydrolysis. • α-Al 2 O 3 powders were added as seed particles in the hydrolysis. • This article indicated that the glucose could impel the γ-Al 2 O 3 transformed to α-Al 2 O 3 directly. • This article indicated that the addictive of α-Al 2 O 3 seed could improve the phase transformation rate of γ-Al 2 O 3 to α-Al 2 O 3 . • In this article, the pure α-Al 2 O 3 could be obtained by calcining at 1000 °C for 1.5 h. - Abstract: The ultral fine alpha-alumina powder has been successfully synthesized via two-step hydrolysis of aluminum isopropoxide. Glucose and polyvinyl pyrrolidone were used as surfactants during the appropriate processing step. The alpha-alumina powder was used as seed particles. Several synthesis parameters, such as the amount of seeds, surfactants, and calcination temperature, were studied by X-ray diffraction (XRD), Fourier transform infrared spectra (FTIR), Thermogravimetry-differential scanning calorimetry (TG-DSC), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The experimental results showed that glucose greatly lower the phase transformation temperature of alpha-alumina by impelling the gamma-alumina transformed to alpha-alumina directly, and the seed could improve the phase transformation rate of alpha-alumina, the polyvinylpyrrolidone have an effect on preventing excessive grain growth and agglomeration of alpha-alumina powder. Comparatively well dispersed alpha-alumina powder with particle size less than 50 nm can be synthesized through this method after calcinations at 1000 °C for 2 h.

  10. Sensitivity and repair of DNA-membrane complex of E.coli B/r and E.coli B/sub(S-1) irradiated with gamma-quanta

    International Nuclear Information System (INIS)

    Morozov, I.I.; Sulimova, T.V.; Ryabchenko, N.I.; Myasnik, M.N.

    1977-01-01

    Irradiation of E. coli B/r and E. coli Bsub(S-1) with gamma-quanta (14 to 42 krad) in Tris buffer at 0 deg C causes a 85% release of DNA molecules from a DNA: membrane complex which is partly repaired on incubation of cells in Tris buffer, pH 8.1, at 37 deg C. A short-term (2 min) addition of nutrient medium to irradiated cells also rises the radioresistance of DNA: membrane complex while further treatment of bacteria under similar conditions causes no additional rejoining of DNA with membranes

  11. Controlling the transport of cations through permselective mesoporous alumina layers by manipulation of electric field and ionic strength

    NARCIS (Netherlands)

    Schmuhl, R.; Keizer, Klaas; van den Berg, Albert; ten Elshof, Johan E.; Blank, David H.A.

    2004-01-01

    The electric field-driven transport of ions through supported mesoporous γ-alumina membranes was investigated. The influence of ion concentration, ion valency, pH, ionic strength, and electrolyte composition on transport behavior was determined. The permselectivity of the membrane was found to be

  12. Beryllium Adsorption at Transition Aluminas: Implications for Environmental Science and Oxidation of Aluminum Alloys

    Energy Technology Data Exchange (ETDEWEB)

    Sergey N. Rashkeev; Michael V. Glazoff

    2010-08-01

    It is demonstrated that?gamma- and?eta- aluminas (transition Al2O3 polytypes with defect spinel structure) can effectively capture beryllium atoms. Although the bulk crystal structures of these two oxides are characterized only by slight differences in cation vacancy distributions, the interaction of Be with the two polytypes are different. For gamma- Al2O3, the Be adsorption energy is high (~ 5 eV per atom), and all Be atoms are captured and trapped at the surface - all attempts to move Be in the subsurface region result in its expulsion back to the surface. On the other hand, for ?eta- alumina Be atoms can be captured both at the surface and in octahedrally-coordinated subsurface cation vacancies. This result implies that both alumina oxides could be successfully used for Be capture out of wastewater streams related to industrial processes of aluminum and alumina production. Also, the surface adsorption mechanism of Be at?gamma- Al2O3 explains why very small additions of Be (of the order of several ppm) to Al-Mg and Al-Mg-Si casting and wrought alloys prevent run-away oxidation of these materials in molten state, as well as ingot cracking. We also discuss possibilities to use other additives (e.g., Ca and Sr) yielding the same protective effect for aluminum alloys but which are less toxic than beryllium.

  13. Bauxite Mining and Alumina Refining

    OpenAIRE

    Donoghue, A. Michael; Frisch, Neale; Olney, David

    2014-01-01

    Objective: To describe bauxite mining and alumina refining processes and to outline the relevant physical, chemical, biological, ergonomic, and psychosocial health risks. Methods: Review article. Results: The most important risks relate to noise, ergonomics, trauma, and caustic soda splashes of the skin/eyes. Other risks of note relate to fatigue, heat, and solar ultraviolet and for some operations tropical diseases, venomous/dangerous animals, and remote locations. Exposures to bauxite dust,...

  14. Production of pure sintered alumina

    International Nuclear Information System (INIS)

    Rocha, J.C. da; Huebner, H.W.

    1982-01-01

    With the aim of optimizing the sintering parameters, the strength of a large number of alumina samples was determined which were produced under widely varying sintering conditions and with different amounts of MgO content. The strength as a function of sintering time or temperature was found to go through a maximum. With increasing time, this maximum is shifted to lower temperatures, and with decreasing temperature to longer times. Data pairs of sintering times and temperatures which yeld the strength maximum were determined. The value of the strength at the maximum remains unchanged. The strength is high (= 400 MN/m 2 , at a grain size of 3 um and a porosity of 2 per cent) and comparable to foreign aluminas produced for commercial purposes, or even higher. The increase in the sintering time from 1 h to 16 h permits a reduction of the sintering temperature from 1600 to 1450 0 C without losing strength. The practical importance of this fact for a production of sintered alumina on a large scale is emphasized. (Author) [pt

  15. Enhanced H2/CH4 and H2/CO2 Separation by Carbon Molecular Sieve Membrane Coated on Titania Modified Alumina Support: Effects of TiO2 Intermediate Layer Preparation Variables on Interfacial Adhesion.

    Czech Academy of Sciences Publication Activity Database

    Tseng, H.-H.; Wang, Ch.-T.; Zhuang, G.-L.; Uchytil, Petr; Řezníčková Čermáková, Jiřina; Setničková, Kateřina

    2016-01-01

    Roč. 510, JUL 15 (2016), s. 391-404 ISSN 0376-7388 Grant - others:NSC(TW) NSC100-2221-E- 040-004-MY3 Institutional support: RVO:67985858 Keywords : carbon membrane * intermediate layer * adhesion Subject RIV: CI - Industrial Chemistry, Chemical Engineering Impact factor: 6.035, year: 2016

  16. The amphiphilic peptide adenoregulin enhances agonist binding to A1-adenosine receptors and [35S]GTP gamma S to brain membranes.

    Science.gov (United States)

    Moni, R W; Romero, F S; Daly, J W

    1995-08-01

    1. Adenoregulin is an amphilic peptide isolated from skin mucus of the tree frog, Phyllomedusa bicolor. Synthetic adenoregulin enhanced the binding of agonists to several G-protein-coupled receptors in rat brain membranes. 2. The maximal enhancement of agonist binding, and in parentheses, the concentration of adenoregulin affording maximal enhancement were as follows: 60% (20 microM) for A1-adenosine receptors, 30% (100 microM) for A2a-adenosine receptors, 20% (2 microM) for alpha 2-adrenergic receptors, and 30% (10 microM) for 5HT1A receptors. High affinity agonist binding for A1-, alpha 2-, and 5HT1A-receptors was virtually abolished by GTP gamma S in the presence of adenoregulin, but was only partially abolished in its absence. Magnesium ions increased the binding of agonists to receptors and reduced the enhancement elicited by adenoregulin. 3. The effect of adenoregulin on binding of N6-cyclohexyladenosine ([3H]CHA) to A1-receptors was relatively slow and was irreversible. Adenoregulin increased the Bmax value for [3H]CHA binding sites, and the proportion of high affinity states, and slowed the rate of [3H]CHA dissociation. Binding of the A1-selective antagonist, [3H]DPCPX, was maximally enhanced by only 13% at 2 microM adenoregulin. Basal and A1-adenosine receptor-stimulated binding of [35S]GTP gamma S were maximally enhanced 45% and 23%, respectively, by 50 microM adenoregulin. In CHAPS-solubilized membranes from rat cortex, the binding of both [3H]CHA and [3H]DPCPX were enhanced by adenoregulin. Binding of [3H]CHA to membranes from DDT1 MF-2 cells was maximally enhanced 17% at 20 microM adenoregulin. In intact DDT1 MF-2 cells, 20 microM adenoregulin did not potentiate the inhibition of cyclic AMP accumulation mediated via the adenosine A1 receptor. 4. It is proposed that adenoregulin enhances agonist binding through a mechanism involving enhancement of guanyl nucleotide exchange at G-proteins, resulting in a conversion of receptors into a high affinity state

  17. Preparation of alumina-β'

    International Nuclear Information System (INIS)

    Casarini, J.R.; Souza, D.P.F.

    1984-01-01

    Alumina - (β + β') in powder, with composition of 8.85% Na 2 0 + 0.75% Li 2 0 + 90.40% Al 2 O 3 is obtained using the zeta process. The phase transformation β→β' can be seen with powder X-ray diffraction. It was observed that the efficiency of the transformation is related to the processing and purity of the raw material. Impurities as Ca and Si difficult the phase transformation β→β'. (E.G.) [pt

  18. Effect of Aluminum Purity on the Pore Formation of Porous Anodic Alumina

    International Nuclear Information System (INIS)

    Kim, Byeol; Lee, Jin Seok

    2014-01-01

    Anodic alumina oxide (AAO), a self-ordered hexagonal array, has various applications in nanofabrication such as the fabrication of nanotemplates and other nanostructures. In order to obtain highly ordered porous alumina membranes, a two-step anodization or prepatterning of aluminum are mainly conducted with straight electric field. Electric field is the main driving force for pore growth during anodization. However, impurities in aluminum can disturb the direction of the electric field. To confirm this, we anodized two different aluminum foil samples with high purity (99.999%) and relatively low purity (99.8%), and compared the differences in the surface morphologies of the respective aluminum oxide membranes produced in different electric fields. Branched pores observed in porous alumina surface which was anodized in low-purity aluminum and the size; dimensions of the pores were found to be usually smaller than those obtained from high-purity aluminum. Moreover, anodization at high voltage proceeds to a significant level of conversion because of the high speed of the directional electric field. Consequently, anodic alumina membrane of a specific morphology, i. e., meshed pore, was produced

  19. Effect of Aluminum Purity on the Pore Formation of Porous Anodic Alumina

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Byeol; Lee, Jin Seok [Sookmyung Women' s Univ., Seoul (Korea, Republic of)

    2014-02-15

    Anodic alumina oxide (AAO), a self-ordered hexagonal array, has various applications in nanofabrication such as the fabrication of nanotemplates and other nanostructures. In order to obtain highly ordered porous alumina membranes, a two-step anodization or prepatterning of aluminum are mainly conducted with straight electric field. Electric field is the main driving force for pore growth during anodization. However, impurities in aluminum can disturb the direction of the electric field. To confirm this, we anodized two different aluminum foil samples with high purity (99.999%) and relatively low purity (99.8%), and compared the differences in the surface morphologies of the respective aluminum oxide membranes produced in different electric fields. Branched pores observed in porous alumina surface which was anodized in low-purity aluminum and the size; dimensions of the pores were found to be usually smaller than those obtained from high-purity aluminum. Moreover, anodization at high voltage proceeds to a significant level of conversion because of the high speed of the directional electric field. Consequently, anodic alumina membrane of a specific morphology, i. e., meshed pore, was produced.

  20. Ordering of Octahedral Vacancies in Transition Aluminas

    NARCIS (Netherlands)

    Wang, Yuan Go; Bronsveld, Paul M.; Hosson, Jeff Th.M. De; Djuričić, Boro; McGarry, David; Pickering, Stephen

    1998-01-01

    The microstructure of transition aluminas obtained via the dehydration of boehmite has been characterized by using transmission electron microscopy (TEM). The presence of γ-, δ-, and θ-aluminas was identified by using selected-area electron diffraction. Modifications that resulted from the

  1. Ultrasonic control of ceramic membrane fouling: Effect of particle characteristics.

    Science.gov (United States)

    Chen, Dong; Weavers, Linda K; Walker, Harold W

    2006-02-01

    In this study, the effect of particle characteristics on the ultrasonic control of membrane fouling was investigated. Ultrasound at 20 kHz was applied to a cross-flow filtration system with gamma-alumina membranes in the presence of colloidal silica particles. Experimental results indicated that particle concentration affected the ability of ultrasound to control membrane fouling, with less effective control of fouling at higher particle concentrations. Measurements of sound wave intensity and images of the cavitation region indicated that particles induced additional cavitation bubbles near the ultrasonic source, which resulted in less turbulence reaching the membrane surface and subsequently less effective control of fouling. When silica particles were modified to be hydrophobic, greater inducement of cavitation bubbles near the ultrasonic source occurred for a fixed concentration, also resulting in less effective control of fouling. Particle size influenced the cleaning ability of ultrasound, with better permeate recovery observed with larger particles. Particle size did not affect sound wave intensity, suggesting that the more effective control of fouling by large particles was due to greater lift and cross-flow drag forces on larger particles compared to smaller particles.

  2. Plasma-sprayed tantalum/alumina cermets

    International Nuclear Information System (INIS)

    Kramer, C.M.

    1977-12-01

    Cermets of tantalum and alumina were fabricated by plasma spraying, with the amount of alumina varied from 0 to 65 percent (by volume). Each of four compositions was then measured for tensile strength, elastic modulus, and coefficient of thermal expansion. In general, strength and strain to failure decreased with increasing alumina content: 62 MPa for 100 percent Ta to 19 MPa for 35 v percent Ta. A maximum of 0.1 percent strain was observed for the sprayed 100 percent Ta specimens. The coefficient of thermal expansion measured for the pure Ta was 6.2 (10 -6 )/K

  3. Mullite-alumina functionally gradient ceramics

    International Nuclear Information System (INIS)

    Pena, P.; Bartolome, J.; Requena, J.; Moya, J.S.

    1993-01-01

    Cracks free mullite-alumina Functionally Gradient Ceramics (FGC) have been obtained by sequential slip casting of Mullite-alumina slurries with different mullite/alumina ratios. These slurries were prepared with 65 % solids content and viscosities ranging from 10 to 40 mPa.s. The presence of cracks perpendicular to the FGC layers have been attributed to residual stresses developed because of the mismatch in thermal expansion between layers. The microstructure of the different layers, and de residual stress value σ R in each layer was also determined. (orig.)

  4. Double-side active TiO{sub 2}-modified nanofiltration membranes in continuous flow photocatalytic reactors for effective water purification

    Energy Technology Data Exchange (ETDEWEB)

    Romanos, G.Em., E-mail: groman@chem.demokritos.gr [Institute of Physical Chemistry, NCSR Demokritos, 153 10 Agia Paraskevi Attikis, Athens (Greece); Athanasekou, C.P.; Katsaros, F.K.; Kanellopoulos, N.K. [Institute of Physical Chemistry, NCSR Demokritos, 153 10 Agia Paraskevi Attikis, Athens (Greece); Dionysiou, D.D. [Department of Civil and Environmental Engineering, University of Cincinnati, Cincinnati, OH 45221-0071 (United States); Likodimos, V.; Falaras, P. [Institute of Physical Chemistry, NCSR Demokritos, 153 10 Agia Paraskevi Attikis, Athens (Greece)

    2012-04-15

    Highlights: Black-Right-Pointing-Pointer A novel CVD reactor for the developments of double side active TiO{sub 2} membranes. Black-Right-Pointing-Pointer Double side active TiO{sub 2} membranes efficiently photodegrade organic pollutants. Black-Right-Pointing-Pointer A photocatalytic membrane purification device for continuous flow water treatment. - Abstract: A chemical vapour deposition (CVD) based innovative approach was applied with the purpose to develop composite TiO{sub 2} photocatalytic nanofiltration (NF) membranes. The method involved pyrolytic decomposition of titanium tetraisopropoxide (TTIP) vapor and formation of TiO{sub 2} nanoparticles through homogeneous gas phase reactions and aggregation of the produced intermediate species. The grown nanoparticles diffused and deposited on the surface of {gamma}-alumina NF membrane tubes. The CVD reactor allowed for online monitoring of the carrier gas permeability during the treatment, providing a first insight on the pore efficiency and thickness of the formed photocatalytic layers. In addition, the thin TiO{sub 2} deposits were developed on both membrane sides without sacrificing the high yield rates. Important innovation was also introduced in what concerns the photocatalytic performance evaluation. The membrane efficiency to photo degrade typical water pollutants, was evaluated in a continuous flow water purification device, applying UV irradiation on both membrane sides. The developed composite NF membranes were highly efficient in the decomposition of methyl orange exhibiting low adsorption-fouling tendency and high water permeability.

  5. Influence of sintering temperature on the characteristics of a-alumina filtration tubes

    International Nuclear Information System (INIS)

    Zarina Abdul Wahid; Rafindde Ramli; Andanastuti Muchtar; Abd Wahab Mohammad

    2005-01-01

    The emerging technology of ceramic membrane filters has created a lot of impact on the materials development and separation industries. Ceramic membrane filters have been used in many separation industry applications particularly in food, dairy, beverages, biotechnology, pharmaceutical and waste treatment industries. This is due to the fact that ceramics are inert and durable and can withstand high temperatures as well as extreme chemical conditions. They also have favourable mechanical properties and lower fouling rates. In this study, ceramic filtration tubes having dimensions of 10 mm outer diameter, 6 mm inner diameter and 880 mm long were prepared from a-alumina using the extrusion technique. The effects of sintering temperature on the pore size, microstructure and porosity of the alumina tube were investigated. The optimum sintering temperature was determined based on the performance of the tubes with regards to porosity, pore size and microstructure. The alumina tubes were sintered at six different temperatures i.e. 1250 degree C, 1300 degree C, 1350 degree C, 1400 degree C, 1450 degree C and 1500 degree C. The porous structures of the alumina tubes were studied using Scanning Electron Microscope (SEM) whereas a Mercury Porosimeter was used to determine the porosity and pore size distribution. (Author)

  6. Structure, surface area and morphology of aluminas from thermal decomposition of Al(OH(CH3COO2 crystals

    Directory of Open Access Journals (Sweden)

    KIYOHARA PEDRO K.

    2000-01-01

    Full Text Available Crystalline aluminium hydroxiacetate was prepared by reaction between aluminium powder (ALCOA 123 and aqueous solution of acetic acid at 96ºC ±1ºC. The white powder of Al(OH(CH3COO2 is constituted by agglomerates of crystalline plates, having size about 10mum. The crystals were fired from 200ºC to 1550ºC, in oxidizing atmosphere and the products characterized by X-ray diffraction, scanning electron microscopy and surface area measurements by BET-nitrogen method. Transition aluminas are formed from heating at the following temperatures: gamma (300ºC; delta (750ºC; alpha (1050ºC. The aluminas maintain the original morphology of the Al(OHAc2 crystal agglomerates, up to 1050ºC, when sintering and coalescence of the alpha-alumina crystals start and proceed up to 1550ºC. High surface area aluminas are formed in the temperature range of 700ºC to 1100ºC; the maximum value of 198m²/g is obtained at 900ºC, with delta-alumina structure. The formation sequence of transition aluminas is similar to the sequence from well ordered boehmite, but with differences in the transition temperatures and in the development of high surface areas. It is suggested that the causes for these diversities between the two sequences from Al(OH Ac2 and boehmite are due to the different particle sizes, shapes and textures of the gamma-Al2O3 which acts as precursor for the sequence gamma- to alpha-Al2O3.

  7. Study of the molybdenum retention in alumina

    International Nuclear Information System (INIS)

    Wilkinson, Maria V.; Mondino, Angel V.; Manzini, Alberto

    2002-01-01

    The Argentine National Atomic Energy Commission routinely produces 99 Mo by fission of highly enriched uranium contained in targets irradiated in RA-3 reactor. The current process begins with the dissolution of the irradiated target in a basic media, considering the possibility of changing the targets, it could be convenient to dissolve them in acid media. The use of alumina as a first separation step in acid dissolution processes is already known although it is necessary to determine both the type of alumina to be used and the separation conditions. The study of molybdenum retention in alumina was performed at laboratory scale, using Mo-99 as radiotracer. Different kinds of alumina were tried, varying charge solution acidity. Influence of uranium concentration in the loading solution on molybdenum retention was also studied. (author)

  8. Everlasting Dark Printing on Alumina by Laser

    Science.gov (United States)

    Penide, J.; Quintero, F.; Arias-González, F.; Fernández, A.; del Val, J.; Comesaña, R.; Riveiro, A.; Lusquiños, F.; Pou, J.

    Marks or prints are needed in almost every material, mainly for decorative or identification purposes. Despite alumina is widely employed in many different industries, the need of printing directly on its surface is still a complex problem. In this sense, lasers have largely demonstrated their high capacities to mark almost every material including ceramics, but performing dark permanent marks on alumina is still an open challenge. In this work we present the results of a comprehensive experimental analysis on the process of marking alumina by laser. Four different laser sources were used in this study: a fiber laser (1075 nm) and three diode pumped Nd:YVO4 lasers emitting at near-infrared (1064 nm), visible (532 nm) and ultraviolet (355 nm) wavelengths, respectively. The results obtained with the four lasers were compared and physical processes involved were explained in detail. Colorimetric analyses allowed to identify the optimal parameters and conditions to produce everlasting and high contrast marks on alumina.

  9. Sintering behaviour of spinel–alumina composites

    Indian Academy of Sciences (India)

    Administrator

    College of Engineering & Ceramic Technology, Kolkata 700 010, India. †. School of .... Chemical compositions of different batches of spinel–alumina composites. Chemistry ..... sence of magnesio–aluminate spinel, Ph D Thesis, University.

  10. Control of porosity in alumina for catalytic purposes - a review; Controle de porosidade em aluminas para fins cataliticos - uma revisao

    Energy Technology Data Exchange (ETDEWEB)

    Moure, Gustavo Torres [PETROBRAS, Rio de Janeiro, RJ (Brazil). Centro de Pesquisas (CENPES). Setor de Tecnologia de Hidrorrefino, Lubrificantes e Parafinas; Morgado Junior, Edisson [PETROBRAS, Rio de Janeiro, RJ (Brazil). Centro de Pesquisas (CENPES). Setor de Tecnologia de Craqueamento Catalitico; Figueiredo, Cecilia Maria C.

    1999-12-01

    In recent years, the Alumina Group, of the Catalysts Division of CENPES, has dedicated research to develop and characterize alumina for the catalytic processes of interest to PETROBRAS. Control of the texture of the alumina and, consequently, the alumina based catalysts, is crucially important to their adequacy and performance. Knowledge of the porosity formation mechanisms in alumina was fundamental for the development of catalysts to satisfy the demand from PETROBRAS. This comprises the scope of this review. (author)

  11. Tungsten metallizing alumina--yttria ceramics

    International Nuclear Information System (INIS)

    Cowan, R.E.; Stoddard, S.D.

    1977-03-01

    The ease with which high-alumina bodies may be metallized with tungsten is improved by additions of yttria to the alumina. Mechanisms of this bonding process were studied by use of optical and electron microscopy, electron microprobe, and tensile tests. Variables studied included yttria content of the body and the firing temperature during metallizing. The study showed that a reaction between the tungsten and the yttrogarnet grain boundary phase markedly improved adherence

  12. Quest for anionic MOF membranes: Continuous sod -ZMOF membrane with Co2 adsorption-driven selectivity

    KAUST Repository

    Almaythalony, Bassem; Shekhah, Osama; Swaidan, Raja; Belmabkhout, Youssef; Pinnau, Ingo; Eddaoudi, Mohamed

    2015-01-01

    We report the fabrication of the first continuous zeolite-like metal-organic framework (ZMOF) thin-film membrane. A pure phase sod-ZMOF, sodalite topology, membrane was grown and supported on a porous alumina substrate using a solvothermal

  13. Tailoring thermal conductivity via three-dimensional porous alumina.

    Science.gov (United States)

    Abad, Begoña; Maiz, Jon; Ruiz-Clavijo, Alejandra; Caballero-Calero, Olga; Martin-Gonzalez, Marisol

    2016-12-09

    Three-dimensional anodic alumina templates (3D-AAO) are an astonishing framework with open highly ordered three-dimensional skeleton structures. Since these templates are architecturally different from conventional solids or porous templates, they teem with opportunities for engineering thermal properties. By establishing the mechanisms of heat transfer in these frameworks, we aim to create materials with tailored thermal properties. The effective thermal conductivity of an empty 3D-AAO membrane was measured. As the effective medium theory was not valid to extract the skeletal thermal conductivity of 3D-AAO, a simple 3D thermal conduction model was developed, based on a mixed series and parallel thermal resistor circuit, giving a skeletal thermal conductivity value of approximately 1.25 W·m -1 ·K -1 , which matches the value of the ordinary AAO membranes prepared from the same acid solution. The effect of different filler materials as well as the variation of the number of transversal nanochannels and the length of the 3D-AAO membrane in the effective thermal conductivity of the composite was studied. Finally, the thermal conductivity of two 3D-AAO membranes filled with cobalt and bismuth telluride was also measured, which was in good agreement with the thermal model predictions. Therefore, this work proved this structure as a powerful approach to tailor thermal properties.

  14. Tailoring thermal conductivity via three-dimensional porous alumina

    Science.gov (United States)

    Abad, Begoña; Maiz, Jon; Ruiz-Clavijo, Alejandra; Caballero-Calero, Olga; Martin-Gonzalez, Marisol

    2016-01-01

    Three-dimensional anodic alumina templates (3D-AAO) are an astonishing framework with open highly ordered three-dimensional skeleton structures. Since these templates are architecturally different from conventional solids or porous templates, they teem with opportunities for engineering thermal properties. By establishing the mechanisms of heat transfer in these frameworks, we aim to create materials with tailored thermal properties. The effective thermal conductivity of an empty 3D-AAO membrane was measured. As the effective medium theory was not valid to extract the skeletal thermal conductivity of 3D-AAO, a simple 3D thermal conduction model was developed, based on a mixed series and parallel thermal resistor circuit, giving a skeletal thermal conductivity value of approximately 1.25 W·m−1·K−1, which matches the value of the ordinary AAO membranes prepared from the same acid solution. The effect of different filler materials as well as the variation of the number of transversal nanochannels and the length of the 3D-AAO membrane in the effective thermal conductivity of the composite was studied. Finally, the thermal conductivity of two 3D-AAO membranes filled with cobalt and bismuth telluride was also measured, which was in good agreement with the thermal model predictions. Therefore, this work proved this structure as a powerful approach to tailor thermal properties. PMID:27934930

  15. Synthesis of Alumina using the solvo thermal method

    International Nuclear Information System (INIS)

    Meor Yusoff Meor Sulaiman; Masliana Muslimin

    2007-01-01

    The paper describes work done on synthesis of α- and β-alumina by using the solvo thermal technique. Synthesis of both these aluminas involves the transition reactions of the aluminium hydroxide into alumina by a dehydroxylation process. As there are many forms of transition aluminas produced during this process, x-ray diffraction (XRD) technique was used to identify α-alumina and β-alumina. After establishing the optimum conditions for the production of a single-phase α- and β-aluminas, characteristic study on the product was performed. An important parameter in establishing nano sized powders is their crystallite size and analysis of the β-alumina shows that it is a nano sized powder with a size of 28 nm while the α-alumina has a crystallite size of 200 nm. Other properties analysed include morphology, surface area and particle size. (author)

  16. Role of Gamma Radiation and Some Natural Products in Alteration of Bacterial Outer Membrane Porins Permeability for Uptake of Certain Antibiotics

    International Nuclear Information System (INIS)

    El-Bastawisy, H.S.

    2015-01-01

    Membrane permeability is the first step involved in resistance of bacteria to an antibiotic. The bacterial outer membrane proteins (OMPs) that constitute porins play role in the definition of intrinsic resistance in Gram negative bacilli that is altered under antibiotic pressure. It has been noted that the response to prolonged exposure to increasing levels of antibiotic cause major changes in the permeability of the bacterium due to down regulation of porins and over expression of efflux pumps. In this study a total of 92 bacterial isolates of different species were isolated from different sites of cancer and non cancer patients; the microorganisms were identified using API system. The susceptibility test was carried out for all the isolates to detect the multidrug resistant isolates; from this test eleven strains were selected for further studies. Antimicrobial susceptibility of the eleven strains against some selected antibiotics acting on the inhibition of cell wall synthesis before and after in vitro gamma irradiation was carried out. The obtained results showed a clear increase in the number of resistant isolates after irradiation as compared to those before irradiation. The efficacy of the citrus fruits (Citrus limon, Citrus paradise, Citrus reticulate and Citrus sinensis) was tested to improve the performance of the tested antibiotics by increasing its permeability through the porin channels. The dried crushed citrus fruits peels were decontaminated by gamma irradiation at 700 Gray; then the aqueous extract of the citrus fruits were prepared to test its antimicrobial activity against the selected bacterial strains. The obtained results revealed that the aqueous extracts of different citrus fruits peels did not show any antibacterial activities against six bacterial isolates (Acinetobacter calcoaceticus 44, Enterbacter cloacae 51, Escherichia coli 52, Pseudomonas fluorescens 64, Klebsiella pneumoniae 78 and Pseudomonas aeruginosa 90). Therefore, these six

  17. Effect of hydrothermal process for inorganic alumina sol on crystal structure of alumina gel

    Directory of Open Access Journals (Sweden)

    K. Yamamura

    2016-09-01

    Full Text Available This paper reports the effect of a hydrothermal process for alumina sol on the crystal structure of alumina gel derived from hydrothermally treated alumina sol to help push forward the development of low temperature synthesis of α-Al2O3. White precipitate of aluminum hydroxide was prepared with a homogeneous precipitation method using aluminum nitrate and urea in aqueous solution. The obtained aluminum hydroxide precipitate was peptized by using acetic acid at room temperature, which resulted in the production of a transparent alumina sol. The alumina sol was treated with a hydrothermal process and transformed into an alumina gel film by drying at room temperature. Crystallization of the alumina gel to α-Al2O3 with 900 °C annealing was dominant for a hydrothermal temperature of 100 °C and a hydrothermal time of 60 min, as production of diaspore-like species was promoted with the hydrothermal temperature and time. Excess treatments with hydrothermal processes at higher hydrothermal temperature for longer hydrothermal time prevented the alumina gel from being crystallized to α-Al2O3 because the excess hydrothermal treatments promoted production of boehmite.

  18. Alumina ceramics prepared with new pore-forming agents

    Directory of Open Access Journals (Sweden)

    Zuzana Živcová

    2008-06-01

    Full Text Available Porous ceramics have a wide range of applications at all length scales, ranging from fi ltration membranes and catalyst supports to biomaterials (scaffolds for bone ingrowths and thermally or acoustically insulating bulk materials or coating layers. Organic pore-forming agents (PFAs of biological origin can be used to control porosity, pore size and pore shape. This work concerns the characterization and testing of several less common pore-forming agents (lycopodium, coffee, fl our and semolina, poppy seed, which are of potential interest from the viewpoint of size, shape or availability. The performance of these new PFAs is compared to that of starch, which has become a rather popular PFA for ceramics during the last decade. The PFAs investigated in this work are in the size range from 5 μm (rice starch to approximately 1 mm (poppy seed, all with more or less isometric shape. The burnout behavior of PFAs is studied by thermal analysis, i.e. thermogravimetry and differential thermal analysis. For the preparation of porous alumina ceramics from alumina suspensions containing PFAs traditional slip casting (into plaster molds and starch consolidation casting (using metal molds are used in this work. The resulting microstructures are investigated using optical microscopy, combined with image analysis, as well as other methods (Archimedes method of double-weighing in water, mercury intrusion porosimetry.

  19. Shock diffraction in alumina powder

    International Nuclear Information System (INIS)

    Venz, G.; Killen, P.D.; Page, N.W.

    1996-01-01

    In order to produce complex shaped components by dynamic compaction of ceramic powders detailed knowledge of their response under shock loading conditions is required. This work attempts to provide data on release effects and shock attenuation in 1 μm and 5 μm α-alumina powders which were compacted to between 85 % and 95 % of the solid phase density by the impact of high velocity steel projectiles. As in previous work, the powder was loaded into large cylindrical dies with horizontal marker layers of a contrasting coloured powder to provide a record of powder displacement in the recovered specimens. After recovery and infiltration with a thermosetting resin the specimens were sectioned and polished to reveal the structure formed by the passage of the projectile and shock wave. Results indicate that the shock pressures generated were of the order of 0.5 to 1.4 GPa and higher, with shock velocities and sound speeds in the ranges 650 to 800 m/s and 350 to 400 m/s respectively

  20. Biosensors Based on Ultrathin Film Composite Membranes

    Science.gov (United States)

    1994-01-25

    composite membranes should have a number C •’ of potential advantages including fast response time, simplicity of construction, and applicability to a number...The support membrane for the ultrathin film composite was an Anopore ( Alltech Associates) microporous alumina filter, these membranes are 55 Pm thick...constant 02 concentration in this solution. Finally, one of the most important potential advantage of a sensor based on an ultrathin film composite

  1. High contrast laser marking of alumina

    International Nuclear Information System (INIS)

    Penide, J.; Quintero, F.; Riveiro, A.; Fernández, A.; Val, J. del; Comesaña, R.; Lusquiños, F.; Pou, J.

    2015-01-01

    Highlights: • Laser marking of alumina using near infrared (NIR) lasers was experimentally analyzed. • Color change produced by NIR lasers is due to thermally induced oxygen vacancies. • Laser marking results obtained using NIR lasers and green laser are compared. • High contrast marks on alumina were achieved. - Abstract: Alumina serves as raw material for a broad range of advanced ceramic products. These elements should usually be identified by some characters or symbols printed directly on them. In this sense, laser marking is an efficient, reliable and widely implemented process in industry. However, laser marking of alumina still leads to poor results since the process is not able to produce a dark mark, yielding bad contrast. In this paper, we present an experimental study on the process of marking alumina by three different lasers working in two wavelengths: 1064 nm (Near-infrared) and 532 nm (visible, green radiation). A colorimetric analysis has been carried out in order to compare the resulting marks and its contrast. The most suitable laser operating conditions were also defined and are reported here. Moreover, the physical process of marking by NIR lasers is discussed in detail. Field Emission Scanning Electron Microscopy, High Resolution Transmission Electron Microscopy and X-ray Photoelectron Spectroscopy were also employed to analyze the results. Finally, we propose an explanation for the differences of the coloration induced under different atmospheres and laser parameters. We concluded that the atmosphere is the key parameter, being the inert one the best choice to produce the darkest marks

  2. Synthesis of nano γ-alumina by the solvothermal technique

    International Nuclear Information System (INIS)

    Meor Yusoff Meor Sulaiman; Masliana Muslimin

    2006-01-01

    The paper describes work done on synthesis of γ-alumina by using the solvo thermal technique. Synthesis of γ-alumina involves the transition reactions of the aluminium hydroxide into alumina by a dehydroxylation process. As there are many forms of transition aluminas produced during this process, a x-ray diffraction (XRD) technique was used to identify γ-alumina and the other forms of alumina. After establishing the optimum conditions for the production of a single-phase γ-alumina, characteristic study on the product was performed. An important parameter in establishing nanosized powders is their crystallite size and analysis of the γ-alumina shows that it is a nanosized powder with a size of 28 nm. Other properties analysed include morphology, surface area and particle size. (Author)

  3. Severe wear behaviour of alumina balls sliding against diamond ...

    Indian Academy of Sciences (India)

    study, alumina ball was chosen as the counter body material to show better performance of the ... Tribology is a relatively new science that considers ... The science is applied in ... for example, in hip prosthesis, instead of existing alumina.

  4. Challenges and Strategies in the Synthesis of Mesoporous Alumina Powders and Hierarchical Alumina Monoliths

    Directory of Open Access Journals (Sweden)

    Anne Galarneau

    2012-02-01

    Full Text Available A new rapid, very simple and one-step sol-gel strategy for the large-scale preparation of highly porous γ-Al2O3 is presented. The resulting mesoporous alumina materials feature high surface areas (400 m2 g−1, large pore volumes (0.8 mL g−1 and the ��-Al2O3 phase is obtained at low temperature (500 °C. The main advantages and drawbacks of different preparations of mesoporous alumina materials exhibiting high specific surface areas and large pore volumes such as surfactant-nanostructured alumina, sol-gel methods and hierarchically macro-/mesoporous alumina monoliths have been analyzed and compared. The most reproducible synthesis of mesoporous alumina are given. Evaporation-Induced Self-Assembly (EISA is the sole method to lead to nanostructured mesoporous alumina by direct templating, but it is a difficult method to scale-up. Alumina featuring macro- and mesoporosity in monolithic shape is a very promising material for in flow applications; an optimized synthesis is described.

  5. Electrochemically produced alumina as TL detector

    International Nuclear Information System (INIS)

    Osvay, M.

    1996-01-01

    The goal of this work was to compare the TL properties of various electrochemically produced alumina layers (E-AIO) in order to investigate the effect of the electrolyte and the Mg content on the alloys. It has been found that the TL sensitivity of oxidised layers is more influenced by the type of electrolyte, than by the composition of alloy. Hard oxide layer evolved in reduction electrolyte has rather different character compared to other alumina production investigated. The effect of reducing media seems to be very important during preparation of alumina layer. One of the advantages properties of E-AIO is, that it serve a promising method to increase the measuring range of TL method above 10 kGy as well. (author)

  6. Iron films deposited on porous alumina substrates

    Energy Technology Data Exchange (ETDEWEB)

    Yamada, Yasuhiro, E-mail: yyasu@rs.kagu.tus.ac.jp; Tanabe, Kenichi; Nishida, Naoki [Tokyo University of Science (Japan); Kobayashi, Yoshio [The University of Electro-Communications (Japan)

    2016-12-15

    Iron films were deposited on porous alumina substrates using an arc plasma gun. The pore sizes (120 – 250 nm) of the substrates were controlled by changing the temperature during the anodic oxidation of aluminum plates. Iron atoms penetrated into pores with diameters of less than 160 nm, and were stabilized by forming γ-Fe, whereas α-Fe was produced as a flat plane covering the pores. For porous alumina substrates with pore sizes larger than 200 nm, the deposited iron films contained many defects and the resulting α-Fe had smaller hyperfine magnetic fields. In addition, only a very small amount of γ-Fe was obtained. It was demonstrated that the composition and structure of an iron film can be affected by the surface morphology of the porous alumina substrate on which the film is grown.

  7. Hydrogen diffusion in Pb β''-alumina

    International Nuclear Information System (INIS)

    Bates, J.B.; Dudney, N.J.; Wang, J.C.

    1985-01-01

    The mobile Na + ions in Na β''-alumina can be completely exchanged with Pb 2+ ions by treatment in molten PbCl 2 . When this exchange was carried out in the presence of air, protons in the form of OH - were introduced into the conduction layers along with lead ions. Although the concentration of OH - was low, on the order of 5 x 10 -3 per formula unit of Pb/sub 0.84/Mg/sub 0.67/Al/sub 10.33/O_1_7, the distribution of OH - after ion exchange indicated that the proton mobility in Pb β''-alumina is high. The potential use of Pb β''-alumina as a fast proton conductor that is stable at 400 0 C motivated further studies of hydrogen diffusion. In this report, the results of tracer diffusion measurements by isotope exchange will be presented

  8. Pt/Au nanoalloy supported on alumina and chlorided alumina: DFT and experimental analysis

    Science.gov (United States)

    Sharifi, N.; Falamaki, C.; Ghorbanzadeh Ahangari, M.

    2018-04-01

    Density functional theory (DFT) was used to explore the adsorption of Pt/Au nanoalloy onto a pure and chlorided γ-Al2O3(110) surface, which has been applied in numerous catalytic reactions. First, we considered the adsorption properties of Pt clusters (n ≤ 5) onto the Al2O3(110) surface to determine the most stable Pt cluster on alumina surface in reforming processes. After full structural relaxations of Pt clusters at various configurations on alumina, our computed results expressed that the minimum binding energy (‑5.67 eV) is accrued for Pt4 cluster and the distance between the nearest Pt atom in the cluster to the alumina surface is equal to 1.13 Å. Then, we investigated the binding energies, geometries, and electronic properties of adsorbed Aun clusters (n ≤ 6) on the γ-Al2O3(110) surface. Our studied showed that Au5 was the most thermodynamically stable structure on γ-Al2O3. Finally, we inspected these properties for adsorbed Au clusters onto the Pt4-decorated alumina (Aun/Pt4-alumina) system. The binding energy of the Au4/Pt4-alumina system was ‑5.01 eV, and the distance between Au4 cluster and Pt4-alumina was 1.33 Å. The Au4/Pt4alumina system was found to be the most stable nanometer-sized catalyst design. At last, our first-principles calculations predicted that the best position of embedment Cl on the Au4/Pt4-alumina.

  9. Vapour growth of Cd(Zn)Te columnar nanopixels into porous alumina

    International Nuclear Information System (INIS)

    Sochinskii, N.V.; Abellan, M.; Martin Gonzalez, M.; Saucedo, E.; Dieguez, E.; Briones, F.

    2006-01-01

    The vapour phase growth (VPG) of CdTe and Cd 1- x Zn x Te was performed in order to investigate the formation of Cd(Zn)Te columnar nanostructures, which could serve as a basis for micropixels usable for further development of X- and gamma-ray high-resolution imaging devices. The possibility to form the 'Cd(Zn)Te-in-porous alumina' nanostructures by VPG has been demonstrated. The Cd(Zn)Te crystals integrated into nanoporous alumina have shown to have photoluminescence properties compatible with those of the bulk crystals and planar epitaxial layers. Further investigations are going on to improve the structural quality of Cd(Zn)Te nanocrystals

  10. Electron-irradiation-induced phase transformation in alumina

    International Nuclear Information System (INIS)

    Chen, C.L.; Arakawa, K.; Lee, J.-G.; Mori, H.

    2010-01-01

    In this study, electron-irradiation-induced phase transformations between alumina polymorphs were investigated by high-resolution transmission electron microscopy. It was found that the electron-irradiation-induced α → κ' phase transformation occurred in the alumina under 100 keV electron irradiation. It is likely that the knock-on collision between incident electrons and Al 3+ cations is responsible for the occurrence of electron-irradiation-induced phase transformation from α-alumina to κ'-alumina.

  11. Blocking of grain reorientation in self-doped alumina materials

    International Nuclear Information System (INIS)

    Suarez, M.; Fernandez, A.; Menendez, J.L.; Ramirez-Rico, J.; Torrecillas, R.

    2011-01-01

    Alumina nanoparticles 10-20 nm in diameter were nucleated on alumina particles, 150 nm average diameter, by a colloidal route followed by calcination. It is shown that after sintering, the final grain size is up to 20% smaller due to the addition of the alumina nanoparticles. Electron backscattered diffraction analysis shows that whereas a correlation in the relative crystalline orientations between neighbouring grains exists in the pure materials, the addition of alumina nanoparticles results in a random crystalline orientation.

  12. Studies of alumina additions in zirconia - magnesia

    International Nuclear Information System (INIS)

    Muccillo, R.

    1987-01-01

    Ionic conductivity measurements have been carried out in the 500 0 C - 1000 0 C temperature range in Mg - PSZ (Partially Stabilized Zirconia) with 0.5 to 10 mol % alumina additions. All specimens were prepared by pressing followed by pre - and sintering at 1000 0 C/2h and1450 0 C/4h, respectively. Thermal histerysis of the ionic conductivity have been detected, probably due to phase changes in the Mg-PSZ samples. The results show that alumina additions up to 2.1% enhances densification with no major variations in electrical resistivity values. (Author) [pt

  13. Tritium compatibility of alumina and Fosterite

    Energy Technology Data Exchange (ETDEWEB)

    Coffin, D.O.

    1979-09-01

    Many pressure measurements are required to control processing of the fuel gases associated with fusion power reactors. Since most pressure transducers respond to changes in pressure sensitive electrical parameters, insulators will be required to withstand chronic exposures to concentrated tritium. For this investigation samples of alumina and Fosterite were exposed to concentrated tritium gas for 11 weeks. Gas phase impurities were then analyzed for clues that would indicate decomposition of the exposed materials. The only gaseous impurity resulting from these tritium exposures was tritio-methane, which is always produced when tritium is stored in stainless steel containers. There was no evidence that either alumina or Fosterite decomposed in the presence of tritium.

  14. Delayed Failure in a Shock Loaded Alumina

    International Nuclear Information System (INIS)

    Cooper, G. A.; Millett, J. C. F.; Bourne, N. K.; Dandekar, D. P.

    2006-01-01

    Manganin stress gauges have been used to measure the lateral stress in a shock-loaded alumina. In combination with known longitudinal stresses, these have been used to determine the shear strength of this material, behind the shock front. The two-step nature of the lateral stress traces shows a slow moving front behind the main shock, behind which shear strength undergoes a significant decrease. Results also show that this front decreases markedly in velocity as the HEL is crossed, suggesting that limited plasticity occurs during inelastic deformation. Finally, comparison of measured shear strengths with other aluminas shows a high degree of agreement

  15. Fabrication of Ceramic Matrix Composite Tubes Using a Porous Mullite/Alumina Matrix and Alumina/Mullite Fiber

    National Research Council Canada - National Science Library

    Radsick, Timothy

    2001-01-01

    ... or from inadequate oxide-based ones. A porous mullite/alumina matrix combined with alumina/mullite fiber reinforcement eliminates the need for an interface coating while producing a strong, tough and oxidation resistant composite...

  16. Modification of the temperatures of phase transformations of alumina by the insertion of MgO and ZrO2

    International Nuclear Information System (INIS)

    Rosario, D.C.C.; Gouvea, D.

    2010-01-01

    Due to the stability and diversity of alumina polymorph, it becomes a very interesting material for stability studies considering changes in surface energy. The gamma phase is metastable and extensively studied due its properties and applications in catalysis. Studies have been conducted with the purpose to changing the transformation temperature gamma-alpha, considering modification on surface energy of nanomaterials. Thereby, this study aims to understand the phase transition amorphous-gamma of alumina by inserting additives (MgO and ZrO 2 ), taking into account the effects on specific surface area and surface energy. The assessment of stability was performed by analysis of DTA, X-ray diffraction and measurements of specific surface area, showing an increase in surface area with additives concentration, followed by a decrease of surface energy, then stability of gamma phase. (author)

  17. Characterization of alumina using small angle neutron scattering (SANS)

    International Nuclear Information System (INIS)

    Megat Harun Al Rashidn Megat Ahmad; Abdul Aziz Mohamed; Azmi Ibrahim; Che Seman Mahmood; Edy Giri Rachman Putra; Muhammad Rawi Muhammad Zin; Razali Kassim; Rafhayudi Jamro

    2007-01-01

    Alumina powder was synthesized from an aluminium precursor and studied using small angle neutron scattering (SANS) technique and complemented with transmission electron microscope (TEM). XRD measurement confirmed that the alumina produced was high purity and highly crystalline αphase. SANS examination indicates the formation of mass fractals microstructures with fractal dimension of about 2.8 on the alumina powder. (Author)

  18. 21 CFR 73.1010 - Alumina (dried aluminum hydroxide).

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 1 2010-04-01 2010-04-01 false Alumina (dried aluminum hydroxide). 73.1010... GENERAL LISTING OF COLOR ADDITIVES EXEMPT FROM CERTIFICATION Drugs § 73.1010 Alumina (dried aluminum hydroxide). (a) Identity. (1) The color additive alumina (dried aluminum hydroxide) is a white, odorless...

  19. Ionic and molecular transport in beta- and beta''-alumina

    International Nuclear Information System (INIS)

    Bates, J.B.

    1984-03-01

    Investigations of rapid transport of cations and water molecules in the β- and β''-alumina family of superionic conductors are reviewed. Particular topics that are discussed include the Haven ratio and mixed-ion effects in β-alumina, and the influence of superlattice ordering on ionic transport in β''-alumina

  20. Study on alumina-alumina brazing for application in vacuum chambers of proton synchrotron

    International Nuclear Information System (INIS)

    Yadav, D.P.; Kaul, R.; Ganesh, P.; Shiroman, Ram; Tiwari, Pragya; Sridhar, R.; Kukreja, L.M.

    2013-01-01

    The paper describes an experimental study to standardize vacuum brazing process to obtain satisfactory high purity alumina brazed joints for application in rapid cycle proton synchrotron machine. Two different brazing routes, adopted for making alumina-alumina brazed joints, included (i) multi-step Mo-Mn metallization and brazing with BVAg-8 alloy and (ii) advanced single-step active brazing with CuSil-ABA alloy. Brazed alumina specimens, prepared by both the routes, yielded ultra high vacuum compatible, helium leak tight and bakeable joints. Active-brazed specimens exhibited satisfactory strength values in tensile and four-point bend tests. Metallized-brazed specimens, although exhibited relatively lower tensile strength than the targeted value, displayed satisfactory flexural strength in four-point bend test. The results of the study demonstrated that active brazing is the simple and cost effective alternative to conventional metallization route for producing satisfactory brazed joints for application in rapid cycle proton synchrotron machine. (author)

  1. Permeability optimization and performance evaluation of hot aerosol filters made using foam incorporated alumina suspension.

    Science.gov (United States)

    Innocentini, Murilo D M; Rodrigues, Vanessa P; Romano, Roberto C O; Pileggi, Rafael G; Silva, Gracinda M C; Coury, José R

    2009-02-15

    Porous ceramic samples were prepared from aqueous foam incorporated alumina suspension for application as hot aerosol filtering membrane. The procedure for establishment of membrane features required to maintain a desired flow condition was theoretically described and experimental work was designed to prepare ceramic membranes to meet the predicted criteria. Two best membranes, thus prepared, were selected for permeability tests up to 700 degrees C and their total and fractional collection efficiencies were experimentally evaluated. Reasonably good performance was achieved at room temperature, while at 700 degrees C, increased permeability was obtained with significant reduction in collection efficiency, which was explained by a combination of thermal expansion of the structure and changes in the gas properties.

  2. LOW TEMPERATURE SINTERING OF ALUMINA BIOCERAMIC UNDER NORMAL PRESSURE

    Institute of Scientific and Technical Information of China (English)

    2000-01-01

    Superfine alumina powder with high purity (mean particle size is less than 0. 35μm) were used as main starting material for sintering alumina ceramic. A multiple additive MgO-ZrO2 (Y2O3) was homogeneously added into the batch by the chemical coprecipitation method. Sintering of alumina bioceramic at low tempera ture (<1600C) was achieved resulting in a dense and high strength alumina ceramic with the bending strength up to 382 MPa and an improved fracture toughness. Mechanism that the multiple additives promote the sintering of alumina ceramic is discussed on the base of XRD and SEM analysis.

  3. Investigating the property profile of polyamide-alumina nanocomposite materials

    International Nuclear Information System (INIS)

    Sarwar, Muhammad Ilyas; Zulfiqar, Sonia; Ahmad, Zahoor

    2009-01-01

    Transparent sol-gel-derived nanocomposites were prepared by incorporating an alumina network into a polyamide matrix. Different amounts of aluminum butoxide were hydrolyzed and condensed to produce the alumina network. Thin composite films were characterized in terms of their optical, morphological, mechanical and thermomechanical properties. Tensile modulus, stress at both yield and break points, improved for alumina loadings of 5-10 wt.%. The glass transition temperature increased to 140 o C for nanocomposites containing 15 wt.% alumina. Scanning electron microscopy investigations indicated a uniform distribution of alumina in the polyamide matrix.

  4. Mechanical Properties of Plasma Sprayed Alumina Coatings

    Czech Academy of Sciences Publication Activity Database

    Kovářík, O.; Nohava, Jiří; Siegel, J.

    2003-01-01

    Roč. 48, č. 2 (2003), s. 129-145 ISSN 0001-7043 R&D Projects: GA ČR GA106/01/0094 Institutional research plan: CEZ:AV0Z2043910 Keywords : plasma sprayed alumina coatings, fatigue test, metalography, fractography, residual stress, microhardness, Young's modulus , four-point bending Subject RIV: BL - Plasma and Gas Discharge Physics

  5. Yield stress of alumina-zirconia suspensions

    International Nuclear Information System (INIS)

    Ramakrishnan, V.; Pradip; Malghan, S.G.

    1996-01-01

    The yield stress of concentrated suspensions of alumina, zirconia, and mixed alumina-zirconia powders was measured by the vane technique as a function of solids loading, relative amounts of alumina and zirconia, and pH. At the isoelectric point (IEP), the yield stress varied as the fourth power of the solids loading. The relative ratio of alumina and zirconia particles was important in determining the yield stress of the suspension at the IEP. The yield stress of single and mixed suspensions showed a marked variation with pH. The maximum value occurred at or near the IEP of the suspension. The effect of electrical double-layer forces on the yield stress can be described on the basis of the Derjaguin-Landau-Verwey-Overbeek (DLVO) theory. A normalized yield stress--that is, the ratio of the yield stress at a given pH to the yield stress at the IEP predicted by this model--showed good correlation with experimental data

  6. Vacuum seeding and secondary growth route to sodalite membrane

    International Nuclear Information System (INIS)

    Lee, Sung-Reol; Son, You-Hwan; Julbe, Anne; Choy, Jin-Ho

    2006-01-01

    Sodalite membrane has been successfully fabricated on tubular porous α-Al 2 O 3 supports by secondary growth method with vacuum seeding. In the seeding process, the colloidal seeding particles were agglutinated not only onto the surface of alumina support but also within the pores by vacuum sucking method. To obtain defect-free sodalite membrane, the sodalite crystals were grown directly on the alumina support in a mixture solution containing alumina and silica species under the hydrothermal reaction condition. The as-synthesized sodalite membranes were characterized by X-ray diffraction (XRD) analysis and scanning electron microscopy (SEM). The thickness and the quality of sodalite membrane could be controlled by the hydrothermal reaction time (12∼24 h) and temperature (100∼150 deg. C) under the mother solution of 5Na 2 O : 2SiO 2 : Al 2 O 3 : 1000H 2 O

  7. POROUS MEMBRANE TEMPLATED SYNTHESIS OF POLYMER PILLARED LAYER

    Institute of Scientific and Technical Information of China (English)

    Zhong-wei Niu; Dan Li; Zhen-zhong Yang

    2003-01-01

    The anodic porous alumina membranes with a definite pore diameter and aspect ratio were used as templates to synthesize polymer pillared layer structures. The pillared polymer was produced in the template membrane pores, and the layer on the template surfaces. Rigid cured epoxy resin, polystyrene and soft hydrogel were chosen to confirm the methodology. The pillars were in the form of either tubes or fibers, which were controlled by the alumina membrane pore surface wettability. The structural features were confirmed by scanning electron microscopy results.

  8. Wear of alumina on alumina total hip prosthesis - effect of lubricant on hip simulator test

    Energy Technology Data Exchange (ETDEWEB)

    Ueno, M.; Amino, H. [Kyocera Corp., Fushimi, Kyoto (Japan). Bioceram Div.; Oonishi, H. [Dept. of Orthopaedic Surgery, Artificial Joint Sect. and Biomat. Res. Lab., Osaka Minami National Hospital, Osaka (Japan); Clarke, I.C.; Good, V. [Dept. of Orthopaedic Surgery, Loma Linda Univ. Medical Center, CA (United States)

    2001-07-01

    The complex wear-friction-lubrication behavior of alumina on alumina combination in total hip prostheses (THP) was investigated using a hip joint simulator. The objectives of this study were to evaluate the effect of the ball/cup clearance and of the lubricant conditions. Alumina bearings were categorized in three diametrical clearances, 20-30, 60-70 and 90-100 micrometer, three each and wear tests were carried out with 90% bovine serum. There was no significant difference between three groups. Volumetric wear in the run-in phase for all tested nine ceramic liners averaged 0.27mm{sup 3}/million cycles and in the steady-state phase averaged 0.0042mm{sup 3}/million cycles. In addition to the 90% serum, 27% serum and saline were used as the lubricant for evaluate the effect of serum concentration on alumina on alumina wear couples. The wear test results showed that in all tested conditions the wear trends of alumina BEARING were bi-phasic and wear volume could be affected by the serum concentration. Both ''Run-in'' and ''Steady-state'' wear rates in 90% bovine serum were three times higher than those in saline. (orig.)

  9. Radiological assessment for bauxite mining and alumina refining.

    Science.gov (United States)

    O'Connor, Brian H; Donoghue, A Michael; Manning, Timothy J H; Chesson, Barry J

    2013-01-01

    Exposure Groups (SEGs). The monitoring was undertaken over 12 months, to provide annual average assessments of above-background doses, thereby reducing temporal variations, especially for radon exposures. The monitoring program concentrated on gamma and radon exposures, rather than gross alpha exposures, as past studies have shown that gross alpha exposures from inhalable dust for most of the workforce are small in comparison to combined gamma and radon exposures. The natural background determinations were consistent with data in the literature for localities near Alcoa's mining, refining and residue operations in Western Australia, and also with UNSCEAR global data. Within the mining operations, there was further consistency between the above-background dose estimates and the local geochemistry, with slight elevation of dose levels in mining pits. Conservative estimates of above-background levels for the workforce have been made using an assumption of 100% occupancy (1920 hours per year) for the SEGs considered. Total incremental composite doses for individuals were clearly less than 1.0 mSv/year when gamma, radon progeny and gross alpha exposures were considered. This is despite the activity concentration of some materials being slightly higher than the benchmark of 1 Bq/g. The results are consistent with previous monitoring and demonstrate compliance with the 1 mSv/year exemption level within mining, refining and residue operations. These results will be of value to bauxite mines and alumina refineries elsewhere in the world.

  10. Rheological Properties of Aqueous Nanometric Alumina Suspensions

    Energy Technology Data Exchange (ETDEWEB)

    Li, Chuanping [Iowa State Univ., Ames, IA (United States)

    2004-01-01

    Colloidal processing is an effective and reliable approach in the fabrication of the advanced ceramic products. Successful colloidal processing of fine ceramic powders requires accurate control of the rheological properties. The accurate control relies on the understanding the influences of various colloidal parameters on the rheological properties. Almost all research done on the rheology paid less attention to the interactions of particle and solvent. However, the interactions of the particles are usually built up through the media in which the particles are suspended. Therefore, interactions of the particle with the media, the adsorbed layers on the particle surface, and chemical and physical properties of media themselves must influence the rheology of the suspension, especially for the dense suspensions containing nanosized particles. Relatively little research work has been reported in this area. This thesis addresses the rheological properties of nanometric alumina aqueous suspensions, and paying more attention to the interactions between particle and solvent, which in turn influence the particle-particle interactions. Dense nanometric alumina aqueous suspensions with low viscosity were achieved by environmentally-benign fructose additives. The rheology of nanometric alumina aqueous suspensions and its variation with the particle volume fraction and concentration of fructose were explored by rheometry. The adsorptions of solute (fructose) and solvent (water) on the nanometric alumina particle surfaces were measured and analyzed by TG/DSC, TOC, and NMR techniques. The mobility of water molecules in the suspensions and its variation with particle volume fractions and fructose additive were determined by the 17O NMR relaxation method. The interactions between the nanometric alumina particles in water and fructose solutions were investigated by AFM. The results indicated that a large number of water layers were physically bound on the particles

  11. High energy irradiation of bacterial membrane vesicles

    International Nuclear Information System (INIS)

    De La Rosa, M.A.M.

    1977-01-01

    The interactions of membrane components and two well-defined transport systems in the E. coli ML 308-225 membrane vesicles with 60 Co gamma radiation were investigated. The results presented show that gamma radiation can monitor membrane components and functions of varying radiosensitivities. The possible application of high-energy radiation as a physical probe of membrane structure and functions is indeed promising

  12. Control of the γ-alumina to α-alumina phase transformation for an optimized alumina densification

    Energy Technology Data Exchange (ETDEWEB)

    Lamouri, S.; Hamidouche, M.; Bouaouadja, N.; Belhouchet, H.; Garnier, V.; Fantozzi, G.; Trelkat, J.F.

    2017-07-01

    In this work, we studied the aptitude to sintering green bodies using γ-Al2O3 transition alumina as raw powder. We focused on the influence of the heating rate on densification and microstructural evolution. Phase transformations from transition alumina γ→δ→θ→α-Al2O3 were studied by in situ X-rays diffraction from the ambient to 1200°C. XRD patterns revealed coexistence of various phase transformations during the heating cycle. DTA and dilatometry results showed that low heating rate leads to a significant reduction of the temperature of the α-Al2O3 alumina formation. Around 1190, 1217 and 1240°C were found when using 5, 10 and 20°C/min of heating rate, respectively. The activation energy for θ-Al2O3→α-Al2O3 transformation calculated by Kissinger and JMA equations using dilatometry method were 464.29 and 488.79kJ/mol, respectively and by DTA method were 450.72 and 475.49kJ/mol, respectively. In addition, the sintering of the green bodies with low heating rate promotes the rearrangement of the grains during θ-Al2O3→α-Al2O3 transformation, enhancing the relative density to 95% and preventing the development of a vermicular structure. (Author)

  13. Mechanical properties of ion-implanted alumina

    International Nuclear Information System (INIS)

    Pope, S.G.

    1988-01-01

    Monolithic oxide ceramics are being proposed as structural materials in continuously more-demanding applications. The demands being placed on these materials have caused concern pertaining to the continued growth of oxide structural ceramics due to limited toughness. The realization that ceramic strength and toughness can be affected by surface conditions has led to many surface-modification techniques, all striving to improve the mechanical properties of ceramics. Along these lines, the effects of ion implantation as a surface modification technique for improvement of the mechanical properties of alumina were studied. Initially, sapphire samples were implanted with elemental ion species that would produce oxide precipitates within the sapphire surface when annealed in an oxygen-containing atmosphere. Optimum conditions as determined from implantation into sapphire were then used to modify a polycrystalline alumina. Specific modifications in microhardness, indentation fracture toughness and flexure strength are reported for the parameters studied. Microstructure and phase relationships related to modified surfaces properties are also reported

  14. Microstructural evolution of alumina-zirconia nanocomposites

    International Nuclear Information System (INIS)

    Ojaimi, C.L.; Chinelatto, A.S.A.; Chinelatto, A.L.; Pallone, E.M.J.A.

    2012-01-01

    Ceramic materials have limited use due to their brittleness. The inclusion of nanosized particles in a ceramic matrix, which are called nanocomposites, and ceramic processing control by controlling the grain size and densification can aid in obtaining ceramic products of greater strength and toughness. Studies showed that the zirconia nano inclusions in the matrix of alumina favors an increase in mechanical properties by inhibiting the grain growth of the matrix and not by the mechanism of the transformation toughening phase of zirconia. In this work, the microstructural evolution of alumina nanocomposites containing 15% by volume of nanometric zirconia was studied. From the results it was possible to understand the sintering process of these nanocomposites. (author)

  15. Influence of alumina characteristics on glaze properties

    Directory of Open Access Journals (Sweden)

    Arrufat, S.

    2010-10-01

    Full Text Available Aluminium oxide is a synthetic raw material manufactured from bauxite by the Bayer process, whose Al2O3 content typically exceeds 99%. Four main types of alumina can be defined, depending on the processing used: hydrargillite Al(OH3, boehmite AlOOH, transition aluminas (calcined at low temperatures, 1000 °C, with an intermediary crystallographic structure between hydrates and alpha alumina, and α-Al2O3 (calcined at high temperatures, >1100 °C. In glaze manufacturing, α-Al2O3 is the main type of alumina used. This raw material acts as a matting agent: the matt effect depends on alumina particle size and content in the glaze. This study examines the effect of the degree of alumina calcination on glaze technical and aesthetic properties. For this purpose, aluminas with different degrees of calcination were added to a glaze formulated with a transparent frit and kaolin, in order to simplify the system to be studied. The results show that, depending on the degree of calcination, alumina particles can react with the glaze components (SiO2, CaO, and ZnO to form new crystalline phases (anorthite and gahnite. Both crystallisations extract CaO and ZnO from the glassy phase, increasing glassy phase viscosity. The variation in crystalline phases and glassy phase viscosity yields glazes with different technical and aesthetic properties.

    El óxido de aluminio es una materia prima sintética fabricada a partir de la bauxita por medio del proceso Bayer, cuyo contenido de Al2O3 supera, por regla general, el 99%. Se pueden definir cuatro tipos de alúmina, en función del tipo de proceso usado: hidrargilita Al(OH3, boehmita AlOOH, alúminas de transición (calcinadas a bajas temperaturas, 1000 °C, con una estructura cristalográfica intermedia entre los hidratos y la alfa alúmina, y la α-Al2O3 (calcinada a

  16. Mesoscale Modelling of the Response of Aluminas

    International Nuclear Information System (INIS)

    Bourne, N. K.

    2006-01-01

    The response of polycrystalline alumina to shock is not well addressed. There are several operating mechanisms that only hypothesized which results in models which are empirical. A similar state of affairs in reactive flow modelling led to the development of mesoscale representations of the flow to illuminate operating mechanisms. In this spirit, a similar effort is undergone for a polycrystalline alumina. Simulations are conducted to observe operating mechanisms at the micron scale. A method is then developed to extend the simulations to meet response at the continuum level where measurements are made. The approach is validated by comparison with continuum experiments. The method and results are presented, and some of the operating mechanisms are illuminated by the observed response

  17. CH3-ReO3 on gamma-Al2O3: understanding its structure, initiation,and reactivity in olefin metathesis

    Energy Technology Data Exchange (ETDEWEB)

    Salameh, Alain; Joubert, Jerome; Baudouin, Anne; Lukens, Wayne; Delbecq, Francoise; Sautet, Philippe; Basset, Jean Marie; Coperet,Christophe

    2007-01-20

    Me-ReO3 on gamma-alumina: understanding the structure, theinitiation and thereactivity of a highly active olefin metathesiscatalyst Heterolytic splitting of the C-H bond of the methyl group ofCH3ReO3 on AlsO reactive sites of alumina as a way to generate the activesite of CH3ReO3 supported on gamma-Al203.

  18. Effects of gamma irradiation on the plasma membrane of suspension-cultured apple cells. Rapid irreversible inhibition of H+-ATPase activity

    International Nuclear Information System (INIS)

    Dong, C.-Z.; Montillet, J.-L.; Triantaphylides, C.

    1994-01-01

    The effects of ionizing radiation, used in post-harvest treatment of fruit and vegetables. were investigated on cultured apple cells (Pyrus malus L. cv. Royal Red) on a short-term period. Irradiation (2 kGy) induced an increase of passive ion effluxes from cells and a decrease of cell capacity to regulate external pH. These alterations are likely due to effects on plasma membrane structure and function and were further investigated by studying the effects of irradiation on plasma membrane H + -ATPase activity. Plasma membrane-enriched vesicles were prepared and the H + -ATPase activity was characterized. Irradiation of the vesicles induced a dose dependent inhibition of H + -ATPase activity. The loss of enzyme activity was immediate, even at low doses (0.5 kGy), and was not reversed by the addition of 2mM dithiothreitol. This inhibition may be the result of an irreversible oxidation of enzyme sulfhydryl moieties and/or the result of changes induced within the lipid bilayer affecting the membrane-enzyme interactions. Further analysis of the H + -ATPase activity was carried out on vesicles obtained from irradiated cells confirming the previous results. In vivo recovery of activity was not observed within 5 h following the treatment, thus explaining the decrease of cell capacity to regulate external pH. This rapid irreversible inhibition of the plasma membrane H + -ATPase must be considered as one of the most important primary biochemical events occurring in irradiated plant material. (author)

  19. Grinding mechanism of zirconia toughened alumina

    International Nuclear Information System (INIS)

    Tsukuda, A.; Kondo, Y.; Yokota, K.

    1998-01-01

    In the grinding process, physical properties of ceramics affect both grinding mechanism and quality of ground surface. In this study we focused on fracture toughness of ceramics and the effect on grinding. A grinding test was carried out by single point grinding for ten different zirconia toughened alumina ceramics with different monoclinic zirconia contents. Effects of zirconia contents on the grinding mechanism and crack initiation were discussed. Copyright (1998) AD-TECH - International Foundation for the Advancement of Technology Ltd

  20. Performance characteristics of porous alumina ceramic structures

    International Nuclear Information System (INIS)

    Latella, B.A.; Liu, T.

    2000-01-01

    Porous ceramics have found a wide range of applications as filters for liquids and gases. The suitability of materials for use in these types of applications depends on the microstructure (grain size, pore size and pore volume fraction) and hence the mechanical and thermal properties. In this study alumina ceramics with different levels of porosity and controlled pore sizes were fabricated and the surface damage and fracture properties were examined. Copyright (2000) The Australian Ceramic Society

  1. In-beam dielectric properties of alumina

    International Nuclear Information System (INIS)

    Molla, J.; Ibarra, A.; Hodgson, E.R.

    1995-01-01

    The dielectric properties (permittivity and loss tangent) of a 99.7% purity alumina grade have been measured over a wide frequency range (1 kHz-15 GHz) before and after 2 MeV electron irradiation at different temperatures. The dielectric properties at 15 GHz were measured during irradiation. Both prompt and fluence effects are observed together with permanent changes which continue to evolve following irradiation. The behaviour is complex, consistent with both radiation induced electronic effects and aggregation processes. ((orig.))

  2. Separation of tungsten and rhenium on alumina

    Directory of Open Access Journals (Sweden)

    MILOVAN SM. STOILJKOVIC

    2004-09-01

    Full Text Available The conditions for the efficient separation of tungsten(VI and rhenium (VII on alumina were established. The distribution coefficients Kd for tungstate and perrhenate anions, as well as the separation factors a (a = KdWO42-/Kd ReO4- were determined using hydrochloric or nitric acid as the aqueous media. A solution of sodium chloride in the pH range 2–6 was also examined. Under all the tested experimental conditions, alumina is a much better adsorbent for tungsten than for rhenium. The obtained results indicated that the best separation of these two elements is achieved when 0.01– 0.1 mol dm-3 HCl or 1.0 mol dm-3 HNO3 are used as the aqueous media. If NaCl is used as the aqueous phase, the best separation is achieved with 0.20 mol dm-3 NaCl, pH 4–6. Under these experimental conditions, the breakthrough and saturation capacities of alumina for tungsten at pH 4 are 17 and 26 mg W/g Al2O3, respectively. With increasing pH, these values decrease. Thus, at pH 6 they are only 4 and 13 mg W/g Al2O3, respectively.

  3. High contrast laser marking of alumina

    Science.gov (United States)

    Penide, J.; Quintero, F.; Riveiro, A.; Fernández, A.; del Val, J.; Comesaña, R.; Lusquiños, F.; Pou, J.

    2015-05-01

    Alumina serves as raw material for a broad range of advanced ceramic products. These elements should usually be identified by some characters or symbols printed directly on them. In this sense, laser marking is an efficient, reliable and widely implemented process in industry. However, laser marking of alumina still leads to poor results since the process is not able to produce a dark mark, yielding bad contrast. In this paper, we present an experimental study on the process of marking alumina by three different lasers working in two wavelengths: 1064 nm (Near-infrared) and 532 nm (visible, green radiation). A colorimetric analysis has been carried out in order to compare the resulting marks and its contrast. The most suitable laser operating conditions were also defined and are reported here. Moreover, the physical process of marking by NIR lasers is discussed in detail. Field Emission Scanning Electron Microscopy, High Resolution Transmission Electron Microscopy and X-ray Photoelectron Spectroscopy were also employed to analyze the results. Finally, we propose an explanation for the differences of the coloration induced under different atmospheres and laser parameters. We concluded that the atmosphere is the key parameter, being the inert one the best choice to produce the darkest marks.

  4. Slip cast coating of alumina crucibles

    International Nuclear Information System (INIS)

    Haroun, N.A.; El-Masry, M.A.A.

    1980-01-01

    The development of a process for coating alumina crucibles with MgO protective coat in a two-step slip casting operation is described. The best milling conditions for the alumina used were wet ball milling for 24 hr. MgO had to be calcined at 1200 0 C to minimize hydration. Optimum slip casting conditions for alumina and magnesia were found to be L/S I and pH 3-6 or 9-II for the former, and L/S 3 (alcohol) and pH 8.5-10 for the latter. Sintering of Al 2 O 3 and MgO in the temperature range 1150-500 0 C was investigated. Additions of NiO and MgO lowered the sintered densities at lower temperatures but improved the densification at 1500 0 C. Near theoretical density Al 2 O 3 and MgO crucibles were obtained. A two-step slip casting technique was developed to coat Al 2 O 3 with MgO. Certain slow firing schedules could eliminate the otherwise observed coat-crucible separation and cracks. (author)

  5. Preparation and Characterization of Activated Alumina

    Science.gov (United States)

    Rabia, A. R.; Ibrahim, A. H.; Zulkepli, N. N.

    2018-03-01

    Activated alumina is a high surface area and highly porous form of aluminum oxide that can be employed for contaminant species adsorb from ether gases or liquids without changing its form. The research in getting this material has generated huge interested. Thus, this paper presented preparation of activated alumina from chemical process. Pure aluminum (99.9% pure) reacted at room temperature with an aqueous NaOH in a reactor to produce a solution of sodium aluminate (NaAlO2). This solution was passed through filter paper and the clear filtrate was neutralized with H2SO4, to pH 6, 7 or 8, resulting in the precipitation of a white gel, Al(OH)3·XH2O. The washed gel for sulfate ions were dried at 80 °C for 6 h, a 60 mesh sieve was to separate and sort them into different sizes. The samples were then calcined (burn) for 3h in a muffle furnace, in air, at a heating rate of 2 °C min-1. The prepared activated alumina was further characterized for better understanding of its physical properties in order to predict its chemical mechanism.

  6. Heterotrimeric G protein beta1gamma2 subunits change orientation upon complex formation with G protein-coupled receptor kinase 2 (GRK2) on a model membrane.

    Science.gov (United States)

    Boughton, Andrew P; Yang, Pei; Tesmer, Valerie M; Ding, Bei; Tesmer, John J G; Chen, Zhan

    2011-09-13

    Few experimental techniques can assess the orientation of peripheral membrane proteins in their native environment. Sum Frequency Generation (SFG) vibrational spectroscopy was applied to study the formation of the complex between G protein-coupled receptor (GPCR) kinase 2 (GRK2) and heterotrimeric G protein β(1)γ(2) subunits (Gβγ) at a lipid bilayer, without any exogenous labels. The most likely membrane orientation of the GRK2-Gβγ complex differs from that predicted from the known protein crystal structure, and positions the predicted receptor docking site of GRK2 such that it would more optimally interact with GPCRs. Gβγ also appears to change its orientation after binding to GRK2. The developed methodology is widely applicable for the study of other membrane proteins in situ.

  7. Influence of coprecipitation and mechanical mixture methods on the characteristics of nickel oxide-alumina composites; Influencia dos metodos de coprecipitacao e mistura mecanica nas caracteristicas de compositos oxido de niquel-alumina

    Energy Technology Data Exchange (ETDEWEB)

    Cordeiro, G.L.; Yoshito, W.K.; Ussui, V.; Lima, N.B. de; Lazar, D.R.R., E-mail: gcordeiro@usp.br [Instituto de Pesquisas Energeticas e Nucleares (CCTM/IPEN/CNEN-SP), Sao Paulo, SP (Brazil). Centro de Ciencia e Tecnologia de Materiais

    2014-07-01

    Alumina-supported nickel catalysts are currently used in the reforming process due to low cost and high activity for hydrogen production from alcohols. In this work, the effect of preparation methods on nickel oxide-alumina based materials has been investigated. Nickel content was fixed at 15 wt%. Ceramic powders were obtained by coprecipitation in ammonia medium and mechanical mixture. Coprecipitated materials were calcined in air at 750 deg C to obtain the corresponding oxides. Materials obtained by mechanical mixture were prepared by wet milling of nickel oxide and alumina powders, both synthesized by precipitation and calcination in air at 450 and 750 deg C, respectively. Powders were characterized by X-ray diffraction, nitrogen gas sorption by applying the BET method, laser diffraction, scanning electron microscopy, electrophoretic mobility measurements for zeta potential determination and infrared spectroscopy. The results showed that coprecipitation method allowed the production of mixed oxides with high surface area (232,7 ± 3,2 m{sup 2}.g{sup -1}) and normal granulometric distribution while mechanical mixture led to the formation of materials constituted by gamma alumina and nickel oxide phases, with low surface area (136,2 ± 0,5 m{sup 2}.g{sup -1}) and bimodal granulometric distribution. (author)

  8. Hydrogenation of surface carbon on alumina-supported nickel

    Energy Technology Data Exchange (ETDEWEB)

    Mccarthy, J.G.; Wise, H.

    1979-05-01

    The methanation of carbon deposited by CO or ethylene decomposition on Girdler G-65 catalyst (25Vertical Bar3< nickel, 8Vertical Bar3< alkali, mostly CaO, 4Vertical Bar3< C as graphite, on alumina) was studied by temperature-programed desorption and temperature-programed surface reaction. Four types of carbon were identified: ..cap alpha..-carbon consisted of isolated carbon atoms bonded to nickel and reacting with hydrogen at 470/sup 0/ +/- 20/sup 0/K; ..gamma..-carbon was probably a bulk carbide, most likely Ni/sub 3/C, which had a reaction peak at 550/sup 0/K; ..beta..-carbon consisted of amorphous, polymerized carbon, which had a reaction peak at 680/sup 0/K; and an unreactive crystalline graphite-like species. The ..cap alpha..-form was thermally unstable and transformed into the ..beta..-form above 600/sup 0/K. Both ..cap alpha..- and ..beta..-forms slowly converted to inert graphite above 600/sup 0/K. The evidence suggested that synthesis gas methanation proceeds by dissociative adsorption of CO as the rate-determining step which forms a very reactive carbon adatom state (..cap alpha..') which converts to the ..cap alpha..-state in the absence of hydrogen and to methane in the presence of hydrogen.

  9. Cold Spray Aluminum–Alumina Cermet Coatings: Effect of Alumina Content

    Science.gov (United States)

    Fernandez, Ruben; Jodoin, Bertrand

    2018-04-01

    Deposition behavior and deposition efficiency were investigated for several aluminum-alumina mixture compositions sprayed by cold spray. An increase in deposition efficiency was observed. Three theories postulated in the literature, explaining this increase in deposition efficiency, were investigated and assessed. Through finite element analysis, the interaction between a ceramic particle peening an impacting aluminum particle was found to be a possible mechanism to increase the deposition efficiency of the aluminum particle, but a probability analysis demonstrated that this peening event is too unlikely to contribute to the increment in deposition efficiency observed. The presence of asperities at the substrate and deposited layers was confirmed by a single-layer deposition efficiency measurement and proved to be a major mechanism in the increment of deposition efficiency of the studied mixtures. Finally, oxide removal produced by the impact of ceramic particles on substrate and deposited layers was evaluated as the complement of the other effects and found to also play a major role in increasing the deposition efficiency. It was found that the coatings retained approximately half of the feedstock powder alumina content. Hardness tests have shown a steady increase with the coating alumina content. Dry wear tests have revealed no improvement in wear resistance in samples with an alumina content lower than 22 wt.% compared to pure aluminum coatings. Adhesion strength showed a steady improvement with increasing alumina content in the feedstock powder from 18.5 MPa for pure aluminum coatings to values above 70 MPa for the ones sprayed with the highest feedstock powder alumina content.

  10. Response of exfoliated human buccal epithelium cells to combined gamma radiation, microwaves, and magnetic field exposure estimated by changes in chromatin condensation and cell membrane permeability

    Directory of Open Access Journals (Sweden)

    K. А. Kuznetsov

    2016-11-01

    Full Text Available Modulation of the biological effects produced by ionizing radiation (IR using microwave and magnetic fields has important theoretical and practical applications. Response of human buccal epithelium cells to different physical agents (single and combined exposure to 0.5–5 Gy γ-radiation (60Co; microwaves with the frequency of 36.64 GHz and power densities of 0.1 and 1 W/m2, and static magnetic field with the intensity of 25 mT has been investigated. The stress response of the cells was evaluated by counting heterochromatin granules quantity (HGQ in the cell nuclei stained with orcein. Membrane permeability was assessed by the percentage of cells stained with indigocarmine (cells with damaged membrane. The increase of heterochromatin granules quantity (HGQ, i.e. chromatin condensation was detected at the doses of 2 Gy and higher. Changes in the cell membrane permeability to indigocarmine expressed the threshold effect. Membrane permeability reached the threshold at the doses of 2–3 Gy for the cells of different donors and did not change with the increase of the dose of γ-radiation. Cells obtained from different donors revealed some individual peculiarities in their reaction to γ-radiation. The static magnetic field and microwaves applied before or after γ-radiation decreased its impact, as revealed by means of HGQ assessment.

  11. Tribological and stability investigations of alkylphosphonic acids on alumina surface

    International Nuclear Information System (INIS)

    Cichomski, M.; Kośla, K.; Grobelny, J.; Kozłowski, W.; Szmaja, W.

    2013-01-01

    Alumina substrates are commonly used for various micro-/nanoelectromechanical systems (MEMS/NEMS). For efficient and lifetime longevity of these devices, lubricant films of self-assembled monolayers (SAMs) with nanometer thickness are increasingly being employed. In the present paper, we report preparation, tribological and stability investigations of alkylphosphonic acids on the alumina surface. The alkylphosphonic acids were prepared on the alumina surface using the liquid phase deposition method. The effectiveness of modification of the alumina surface by alkylphosphonic acids was investigated using water contact angle measurements, secondary ion mass spectrometry, X-ray photoelectron and infrared spectroscopy. Frictional behavior in milinewton load range was studied by microtribometry. It is shown that surface modification of the alumina surface by alkylphosphonic acids reduces the coefficient of friction values compared to the unmodified alumina. In comparison to the non-modified alumina surface, all tested alkylphosphonic acids cause a decrease in the friction coefficients in friction tests for counterparts made from different materials, such as steel, zirconia and silicon nitride. It is also found that the alumina surface modified by alkylphosphonic acids with longer chain has a higher degree of hydrophobicity and lower coefficient of friction. The best frictional properties are obtained for the system consisting of the alumina surface modified by n-octadecylphosphonic acid and silicon nitride counterpart. Stability tests in different environmental conditions: laboratory, acidic and alkaline solutions were also monitored.

  12. Dynamical stability of the alpha and theta phases of alumina

    DEFF Research Database (Denmark)

    Lodziana, Zbigniew; Parlinski, K.

    2003-01-01

    Using density functional calculations the phonon dispersion relations, phonon density of states, and free energy of theta and alpha phases of alumina are investigated. The temperature dependence of the free energy indicates that entropy contributes to the destabilization of the alpha phase...... cations in alumina, and suggest that some other than entropic mechanism exists, which stabilizes transition aluminas up to 1400 K. The present calculations go beyond the ground state energy calculations [C. Wolverton and K.C. Hass, Phys. Rev. B 63, 24102 (2001)], and give an additional understanding...... of the stability of transition alumina at finite temperatures....

  13. Synthesis and characterization of ceramic membranes for micro filtration

    International Nuclear Information System (INIS)

    Mohammad Idrees; Lim Yan Ne; Hamdani Saidi

    1996-01-01

    This paper presents the results of a preliminary research work in the development of ceramic membranes by moulding process. The two major objectives were to determine the effect of operating parameters ori- the membrane sheet and membrane characterization. The starting material for the membrane was powdered aluminum oxide and alumina granules. Alumina granules were obtained by spray drying of mixture of alumina with additives and binders under specific conditions. The membrane sheet was produced by mould pressing at various pressures and then sintering at different temperatures. Membrane characterization was done based on microstructure using SEM, pore size distribution, density, and porosity. Strong and porous membranes were produced at pressing force of 120 -140 kN and sintering temperature of 1400 -1500 'C. Pore size and porosity obtained was in the range of 2 -10 μ m, and 13 - 48% respectively. These membranes can be used for, microfiltration at elevated temperature and under extreme environmental condition. They can also be used as porous support for the production qf composite asymmetric UF/hyperfiltration, and gas separation membranes. Further work in the refinement of' pore-size and permeation studies is envisaged

  14. Development and evaluation of alumina calcination

    International Nuclear Information System (INIS)

    Bennett, I.J.

    2000-01-01

    This thesis focuses on a number of aspects governing the transformation of gibbsite, via intermediate phases, to α-alumina. These aspects include the size and morphology of the gibbsite grains, the influence of additions of foreign elements, the effect of a mechanical treatment of the gibbsite prior to calcination, and combinations of these factors. The materials were characterised by scanning electron microscopy, X-ray diffraction and surface area measurements. For some of the calcined materials an attempt was made to sinter the powders to a dense body to investigate if any of the treatments during calcination had an effect on this process. The literature review covers the current state of understanding of the production of bulk alumina powder by the Bayer process and the phase changes seen on calcination of precursors to the stable α-alumina phase. A detailed description of the phase changes is given and the various routes and conditions necessary for the transformations to occur are considered. The transformations are examined in relation to the morphology of the crystals and the variables controlling the phase transformation route are discussed. Calcination in air showed that the size of the gibbsite grain governs the calcination route taken to reach oc-alumina. The standard gibbsites used in this work show a mixed calcination sequence transforming both via the boehmite phase, followed by the γ, δ and θ phases, and via the χ and κ phases. The formation of boehmite is attributed to retention of water vapour within the grain. Differences in morphology of the starting materials showed that for the range of materials seen, the morphology of the grain is less important than its size. The super fine material confirmed that a small grain size transforms via the non-boehmite route only, with the other gibbsites taking intermediate routes as for the standard gibbsites. Of the additions made prior to calcination, aluminium fluoride was found to reduce the

  15. Laser Surface Treatment of Sintered Alumina

    Science.gov (United States)

    Hagemann, R.; Noelke, C.; Kaierle, S.; Wesling, V.

    Sintered alumina ceramics are used as refractory materials for industrial aluminum furnaces. In this environment the ceramic surface is in permanent contact with molten aluminum resulting in deposition of oxidic material on its surface. Consequently, a lower volume capacity as well as thermal efficiency of the furnaces follows. To reduce oxidic adherence of the ceramic material, two laser-based surface treatment processes were investigated: a powder- based single-step laser cladding and a laser surface remelting. Main objective is to achieve an improved surface quality of the ceramic material considering the industrial requirements as a high process speed.

  16. Cathodoluminescence study of anodic nanochannel alumina

    Energy Technology Data Exchange (ETDEWEB)

    Guo, Q.X. [Department of Electrical and Electronic Engineering, Saga University, Honjo-1, Saga, 840-8502 (Japan)]. E-mail: guoq@cc.saga-u.ac.jp; Hachiya, Y. [Department of Electrical and Electronic Engineering, Saga University, Honjo-1, Saga, 840-8502 (Japan); Tanaka, T. [Department of Electrical and Electronic Engineering, Saga University, Honjo-1, Saga, 840-8502 (Japan); Nishio, M. [Department of Electrical and Electronic Engineering, Saga University, Honjo-1, Saga, 840-8502 (Japan); Ogawa, H. [Department of Electrical and Electronic Engineering, Saga University, Honjo-1, Saga, 840-8502 (Japan)

    2006-07-15

    Nanochannel alumina (NCA) templates with highly ordered pore arrays were prepared by anodizing pure aluminum foil in acid solutions. Cathodoluminescence measurements reveal that a blue emission band appears at around 2.8 eV and its energy position depends on measurement temperature and pore size of NCA. The shift of the blue emission band energy with temperature is ascribed to the variations of electron-phonon interactions. X-ray absorption near-edge fine structure results show that the blue emission band shift with pore size is due to the local environment change of atoms in NCA.

  17. Shockless spalling damage of alumina ceramic

    Science.gov (United States)

    Erzar, B.; Buzaud, E.

    2012-05-01

    Ceramic materials are commonly used to build multi-layer armour. However reliable test data is needed to identify correctly models and to be able to perform accurate numerical simulation of the dynamic response of armour systems. In this work, isentropic loading waves have been applied to alumina samples to induce spalling damage. The technique employed allows assessing carefully the strain-rate at failure and the dynamic strength. Moreover, specimens have been recovered and analysed using SEM. In a damaged but unbroken specimen, interactions between cracks has been highlighted illustrating the fragmentation process.

  18. Creep cavitation effects in polycrystalline alumina

    International Nuclear Information System (INIS)

    Porter, J.R.; Blumenthal, W.; Evans, A.G.

    1981-01-01

    Fine grained polycrystalline alumina has been deformed in creep at high temperatures, to examine the evolution of cavities at grain boundaries. Cavities with equilibrium and crack-like morphologies have been observed, distributed nonuniformly throughout the material. The role of these cavities during creep has been described. A transition from equilibrium to crack-like morphology has been observed and correlated with a model based on the influence of the surface to boundary diffusivity ratio and the local tensile stress. The contribution of cavitation to the creep rate and total creep strain has been analyzed and excluded as the principal cause of the observed non-linear creep rate

  19. Investigations on thermoluminescent dosimetry (TLD) with doped alumina ceramics

    International Nuclear Information System (INIS)

    Janas, R.; Huebner, K.

    1976-01-01

    Alumina ceramics doped and burned under various conditions have been investigated with regard to their suitability for thermoluminescent dosimetry. The production of ceramics is described. The properties essential for dosimetric purposes, such as glow curve, energy dose characteristics, fading, recoverability, lower detection limit and energy dependence, are indicated. The advantages and disadvantages of alumina ceramics are compared. (author)

  20. Cavity cutting efficiency of a Bioglass and alumina powder ...

    Indian Academy of Sciences (India)

    1531–1536. c Indian Academy of Sciences. ... conical in shape, whereas cavities produced by alumina and alumina + 45S5 were more ... any other material having good cutting properties is highly .... Saw, Buehler Ltd, IL, USA) at a blade speed of 3500 r.p.m. ... and the machine was run for 1min to remove any residual.

  1. Treatment of chrome plating wastewater (Cr+6) using activated alumina.

    Science.gov (United States)

    Sarkar, Sudipta; Gupta, Anirban

    2003-01-01

    Suitability of activated alumina for removal of hexavalent chromium from electroplating wastewater has been investigated. Activated alumina exhibited good sorption capacity for hexavalent chromium and pH has no pronounced effect on the sorption capacity. Both batch and column adsorption studies have been carried out and an adsorption column design indicated reasonable depth of column for practical application.

  2. Characterization of silane coated hollow sphere alumina-reinforced

    Indian Academy of Sciences (India)

    Silane coated hollow sphere alumina ceramic particles were moulded with ultra high molecular weight polyethylene (UHMWPE) to form a series of composites with alumina weight percent in the range from 15 to 50. The composites were prepared in a cylindrical mould using powder-processing technique. The composites ...

  3. Near net-shape fabrication of alumina glass composites

    NARCIS (Netherlands)

    Zhu, Q.; With, de G.; Dortmans, L.J.M.G.; Feenstra, F.

    2005-01-01

    The purpose of the present study is to fabricate alumina glass composites by melt infiltration with better dimensional control through reducing both the presintering and infiltration temperature. Main efforts were put to develop glasses that are chemically compatible with alumina. After extensive

  4. Thermal shock behavior of rare earth modified alumina ceramic composites

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Junlong; Liu, Changxia [Ludong Univ., Yantai (China). School of Transportation

    2017-05-15

    Alumina matrix ceramic composites toughened by AlTiC master alloys, diopside and rare earths were fabricated by hot-pressing and their thermal shock behavior was investigated and compared with that of monolithic alumina. Results showed that the critical thermal shock temperature (ΔT) of monolithic alumina was 400 C. However, it decreased to 300 C for alumina incorporating only AlTiC master alloys, and increased with further addition of diopside and rare earths. Improvement of thermal shock resistance was obtained for alumina ceramic composites containing 9.5 wt.% AlTiC master alloys and 0.5 wt.% rare earth additions, which was mainly attributed to the formation of elongated grains in the composites.

  5. Morphology and transmittance of porous alumina on glass substrate

    Energy Technology Data Exchange (ETDEWEB)

    Guo Peitao, E-mail: guopeitao@hotmail.com [Wuhan University of Technology. Wuhan (China); Xia Zhilin [Wuhan University of Technology. Wuhan (China); Key Laboratory of Low Dimensional Materials and Application Technology, Xiangtan University, Ministry of Education, Xiangtan (China); Xue Yiyu [Wuhan University of Technology. Wuhan (China); Huang Caihua [China Three Gorges University, Yichang (China); Zhao Lixin [Wuhan University of Technology. Wuhan (China)

    2011-02-01

    The porous optical film has higher threshold of laser-induced damage than densified films, for the study of mechanism of laser-induced damage of porous optical film with ordered pore structure. Porous anodic alumina (PAA) film with high transmittance on glass substrate has been prepared. Aluminum film was deposited on glass substrate by means of resistance and electron beam heat (EBH) evaporation. Porous alumina was prepared in oxalic acid solution under different anodizing conditions. At normal incidence, the optical transmittance spectrum over 300-1000 nm spectra region was obtained by spectrophotometer. SEM was introduced to analysis the morphology of the porous alumina film. The pore aperture increased with the increase of anodizing voltage, which resulted in a rapid decrease of the pore concentration and the optical thickness of porous alumina film. Damage morphology of porous alumina film is found to be typically defects initiated, and the defect is the pore presented on the film.

  6. Characterization and sintering of niobium-ATR alumina

    International Nuclear Information System (INIS)

    Sibuya, N.H.; Iwasaki, H.; Suzuki, C.K.; Pinatti, D.G.

    1987-01-01

    In the niobium aluminothermy a slag is produced, composed mostly of alumina and other compounds such as niobium oxide and silica. The phase composition of this ATR alumina was characterized by X-ray powder diffractometry, and afterwards this alumina was subjected to leaching processes. It was noticed that the original content of 70% α-alumina in slag rose to 95% after the calcination. ATR alumina (leached and calcined, and without any treatment) was used to make pressed bodies which were fired in air at 1200 to 1400 0 C for 1 to 10,5 hours; and in vacuum at 1550 to 1800$0C for 2 hours. Characterization was done by density measurements, X-ray diffractometry and ultrasonic analysis. Ultrasonic analysis of some vacuum fired bodies showed londitudinal velocities close to the value found in literature. Correlation of several techniques measurements disclosed the niobium oxide interference in sintering. (Author) [pt

  7. The mineralogy of bauxite for producing smelter-grade alumina

    Science.gov (United States)

    Authier-Martin, M.; Forte, G.; Ostap, S.; See, J.

    2001-12-01

    Aluminum-producing companies rely on low-cost, high-purity, smelter-grade alumina (aluminum oxide), and alumina production utilizes the bulk of bauxites mined world-wide. The mineralogy of the bauxites has a significant impact on the operation of the Bayer process for alumina production. Typically, the Bayer process produces smelter-grade alumina of 99.5% Al2O3, starting from bauxite containing 30% to 60% Al2O3. The main objective of the Bayer process is to extract the maximum amount of aluminum from the bauxite at as high an aluminate concentration in solution as possible, while limiting any troublesome side reactions. Only with a better understanding of the chemistry of the mineral species and a strict control of the operating/processing conditions can the Bayer process produce efficiently, a low cost, high-quality alumina with minimum detrimental environmental impact.

  8. Synthesis and photocatalytic properties of graphitic carbon nitride nanofibers using porous anodic alumina templates

    Science.gov (United States)

    Suchitra, S. M.; Udayashankar, N. K.

    2017-12-01

    In the present study, we describe an effective method for the synthesis of Graphitic carbon nitride (GCN) nanostructures using porous anodic alumina (AAO) membrane as template by simple thermal condensation of cyanamide. Synthesized nanostructure was fully analysed by various techniques to detect its crystalline nature, morphology, luminescent properties followed by the evaluation of its photocatalytic activity in the degradation of Methylene blue dye. Structural analysis of synthesized GCNNF was systematically carried out using x-ray powder diffraction (XRD) and scanning electron microscope (SEM), and. The results confirmed the growth of GCN inside the nanochannels of anodic alumina templates. Luminescent properties of GCNNF were studied using photoluminescence (PL) spectroscopy. PL analysis showed the presence of a strong emission peak in the wavelength range of 350-600 nm in blue region. GCNNF displays higher photocatalytic performance in the photodegradation of methylene blue compare to the bulk GCN. Highlights 1. In the present paper, we report the synthesis of graphitic carbon nitride nanofibers (GCNNF) using porous anodic aluminium oxide membranes as templates through thermal condensation of cyanamide at 500 °C. 2. The synthesis of Graphitic carbon nitride nanofibers using porous andic alumina template is the efficient approach for increasing crystallinity and surface area. 3. The high surface area of graphitic carbon nitride nanofibers has a good impact on novel optical and photocatalytic properties of the bulkGCN. 4. AAO templating of GCN is one of the versatile method to produce tailorable GCN nanostructures with higher surface area and less number of structural defects. 5. Towards photocatalytic degradation of dyes, the tuning of physical properties is very essential thing hence we are succeeded in achieving better catalytic performance of GCN nanostructures by making use of AAO templates.

  9. Catalytic combustion of propane in a membrane reactor with separate feed of reactants—I. Operation in absence of trans-membrane pressure gradients

    NARCIS (Netherlands)

    Saracco, Guido; Veldsink, Jan Willem; Versteeg, Geert F.; Swaaij, Wim P.M. van

    1995-01-01

    A pilot plant study on propane catalytic combustion in a membrane reactor with separate reactant feeds is presented. The membrane consisted of a porous alumina tube activated by insertion into its pores of a Pt/γ-Al2O3 catalyst. The role of reactants concentration and of the feed flow rates were

  10. Properties of Transition Metal Doped Alumina

    Science.gov (United States)

    Nykwest, Erik; Limmer, Krista; Brennan, Ray; Blair, Victoria; Ramprasad, Rampi

    Crystallographic texture can have profound effects on the properties of a material. One method of texturing is through the application of an external magnetic field during processing. While this method works with highly magnetic systems, doping is required to couple non-magnetic systems with the external field. Experiments have shown that low concentrations of rare earth (RE) dopants in alumina powders have enabled this kind of texturing. The magnetic properties of RE elements are directly related to their f orbital, which can have as many as 7 unpaired electrons. Since d-block elements can have as many as 5 unpaired electrons the effects of substitutional doping of 3d transition metals (TM) for Al in alpha (stable) and theta (metastable) alumina on the local structure and magnetic properties, in addition to the energetic cost, have been calculated by performing first-principles calculations based on density functional theory. This study has led to the development of general guidelines for the magnetic moment distribution at and around the dopant atom, and the dependence of this distribution on the dopant atom type and its coordination environment. It is anticipated that these findings can aid in the selection of suitable dopants help to guide parallel experimental efforts. This project was supported in part by an internship at the Army Research Laboratory, administered by the Oak Ridge Institute for Science and Education, along with a grant of computer time from the DoD High Performance Computing Modernization Program.

  11. Gamma Knife

    Science.gov (United States)

    ... News Physician Resources Professions Site Index A-Z Gamma Knife Gamma Knife® is a radiation therapy that uses computerized ... If you're scheduled for radiation therapy using Gamma Knife®, a treatment team consisting of a radiation ...

  12. Formation of self-ordered porous anodized alumina template for growing tungsten trioxide nanowires

    Science.gov (United States)

    Hussain, Tajamal; Shah, Asma Tufail; Shehzad, Khurram; Mujahid, Adnan; Farooqi, Zahoor Hussain; Raza, Muhammad Hamid; Ahmed, Mirza Nadeem; Nisa, Zaib Un

    2015-12-01

    Uniform porous anodized aluminum oxide (AAO) membrane has been synthesized by two-step anodization for fabricating tungsten trioxide (WO3) nanowires. Under assayed conditions, uniform porous structure of alumina (Al2O3) membrane with long range ordered hexagonal arrangements of nanopores was achieved. The self-assembled template possesses pores of internal diameter of 50 nm and interpore distance ( d int) of 80 nm with a thickness of about 80 µm, i.e., used for fabrication of nanostructures. WO3 nanowires have been fabricated by simple electroless deposition method inside Al2O3 nanopores. SEM images show tungsten trioxide nanowire with internal diameter of about 50 nm, similar to porous diameter of AAO template. XRD results showed that nanowires exist in cubic crystalline state with minor proportion of monoclinic phase.

  13. Evaluation of technological properties of alumina refractory systems-zirconia and zirconia-silica-alumina

    International Nuclear Information System (INIS)

    Marinho, A.R.O.; Carvalho, T.U.S.; Fagury Neto, E.; Rabelo, A.A.

    2014-01-01

    Alumina-zirconia refractories are noted for being products of excellent cost-effective, however, zirconia may limit its use due to decreasing resistance to thermal shock. This study aims to evaluate these refractories with the addition of microsilica, which can greatly improve their properties. Were used the following starting materials: calcined alumina, zirconia (stabilized and monoclinic) in amounts of 2%, 4% and 6% by weight, plus microsilica (5%w.). The powders were milled together with binder and lubricant for conformation bodies by uniaxial pressing. The samples were dried, calcined and sintered at 1400 °C/2h were characterized using the methods of Archimedes, and scanning electron microscopy (SEM), chemical analysis using energy dispersive X-ray (EDS), and mechanical flexural strength tests at room temperature. Formulations with the presence of microsilica showed satisfactory results and optimized properties. (author)

  14. Microstructural evolution of alumina-zirconia nanocomposites; Evolucao microestrutural de nanocompositos alumina-zirconia

    Energy Technology Data Exchange (ETDEWEB)

    Ojaimi, C.L.; Chinelatto, A.S.A.; Chinelatto, A.L. [Universidade Estadual de Ponta Grossa (UEPG), PR (Brazil); Pallone, E.M.J.A., E-mail: christianelago@yahoo.com.br [Universidade de Sao Paulo (USP), Pirassununga, Sao Paulo, SP (Brazil). Faculdade de Zootecnia e Engenharia de Alimentos

    2012-07-01

    Ceramic materials have limited use due to their brittleness. The inclusion of nanosized particles in a ceramic matrix, which are called nanocomposites, and ceramic processing control by controlling the grain size and densification can aid in obtaining ceramic products of greater strength and toughness. Studies showed that the zirconia nano inclusions in the matrix of alumina favors an increase in mechanical properties by inhibiting the grain growth of the matrix and not by the mechanism of the transformation toughening phase of zirconia. In this work, the microstructural evolution of alumina nanocomposites containing 15% by volume of nanometric zirconia was studied. From the results it was possible to understand the sintering process of these nanocomposites. (author)

  15. Microstructural evaluation of alumina-niobium and alumina- niobium-zircon ceramics for ballistic application

    International Nuclear Information System (INIS)

    Mota, Juliana Machado da; Lopes, Cristina Moniz Araujo; Melo, Francisco Lourenco Cristovao de

    2009-01-01

    This study aimed to evaluate the microstructural of Alumina- Niobium and Alumina- Niobium-Zircon ceramics. Samples with 3.5 x 4.5 x 34 mm dimensions were prepared by uniaxial pressure (50 MPa) followed by isostatic pressure (300 MPa). The samples were sintered at 1500 ° C for 1 hour. The ceramics obtained were characterized by scanning electron microscopy (SEM) and X-ray diffraction, to evaluate the phases and microstructures. In order to analyze the microstructure, by SEM the samples were prepared using two techniques: heat treatment (1350 ° C for 5 minutes) and thermochemical treatment (500 ° C for 8 minutes in a solution of NaOH and KOH) on polished and fractured surfaces. The results showed that despite differences between the two etchings, both were effective to analyze the microstructure. (author)

  16. Dissolution kinetics for alumina in cryolite melts. Distribution of alumina in the electrolyte of industrial aluminium cells

    Energy Technology Data Exchange (ETDEWEB)

    Kobbeltvedt, Ove

    1997-12-31

    This thesis contributes to the understanding of which factors determine the rate of dissolution of alumina added to the bath in alumina reduction cells. Knowing this may help reduce the occurrences of operation interruptions and thus make it possible to produce aluminium using less energy. When alumina powder was added to a stirred cryolite melt, the alumina dissolved in two distinct main stages. In the first stage, the dissolution rate was very high, which reflects dissolution of single alumina grains that are being dispersed in the bath upon addition. In the second stage, lumps of alumina infiltrated with bath dissolved at a rate considerably slower than that of the first stage. The formation of these alumina agglomerates is the most important contributor to slow dissolution. The parameters varied in the experiments were convection, batch size, and temperature of the bath and of the added alumina. Increased gas stirring of the bath speeded up dissolution in both stages but the size of the batch was of little significance. Increasing the bath temperature had no effect in the first stage but speeded up dissolution considerably in the second stage. Compared to adding alumina at room temperature, preheating it to a high temperature (600 {sup o}C) increased the dissolution rate in the first stage while preheating to lower temperatures (100-300 {sup o}C) decreased the dissolution rate. In the second stage, preheating slowed the dissolution. The two latter phenomena of reduced dissolution rates are ascribed to the removal of moisture from the alumina upon preheating. The bath flow and the distribution of alumina in the bath were measured in four different types of cells. It was found that if a certain asymmetry of the magnetic field traverse to the cell was present, due to the presence of risers, then loops of high velocity bath flow occurred near the short ends of the cell. Thus, alumina added near the short ends is effectively transferred away from the feeding

  17. Surface study of nano-template anodic porous alumina pre-irradiated by ArF laser

    International Nuclear Information System (INIS)

    Jaleh, B.; Saramad, S.; Farshchi-Tabrizi, M.

    2009-01-01

    Nano-porous alumina membranes have widely used as matrix for the fabrication of nanomaterials for many applications including quantum-dot arrays, magnetic storage devices and composites for catalysis, due to their remarkable hardness, thermal and anti corrupted stability, uniform pore size and high pore density. In this experiment three sets of aluminum samples were chosen for fabrication nano-porous anodic alumina. One set has select for laser cleaning before chemical treatment and the two others with and without chemical treatment without laser irradiation. Anodic aluminum oxide (AAO) films were characterized with Scanning Electron Microscope (SEM) and Atomic Force Microscope (AFM) micrograph and the SEM results were analyzed by Linear-Angular Fast Fourier Transform (LA-FFT) technique to investigate the arrangement and ordering of pores. According to these results the laser irradiated sample has much better regularity in comparison with the usual one.

  18. Mechanical behavior of alumina and alumina-feldspar based ceramics in an acetic acid (4%) environment

    International Nuclear Information System (INIS)

    Stumpf, Aisha S.G.; Bergmann, Carlos P.; Vicenzi, Juliane; Fetter, Rebecca; Mundstock, Karina S.

    2009-01-01

    This study investigates the mechanical properties of alumina-feldspar based ceramics when exposed to an aggressive environment (acetic acid 4%). Alumina ceramics containing different concentrations of feldspar (0%, 1%, 5%, 10%, or 40%) were sintered at either 1300, 1600, or 1700 o C. Flaws (of width 0%, 30%, or 50%) were introduced into the specimens using a saw. Half of these ceramic bodies were exposed to acetic acid. Their flexural strength, K IC , and porosity were measured and the fractured samples were evaluated using scanning electronic- and optical microscopy. It was found that in the ceramic bodies sintered at 1600 o C, feldspar content up to 10% improved flexural strength and K IC, and reduced porosities. Generally, it was found that acetic acid had a weakening effect on the flexural strength of samples sintered at 1700 o C but a beneficial effect on K IC of ceramics sintered at 1600 o C. It was concluded that alumina-based ceramics with feldspar content up to 10% and sintered at higher temperatures would perform better in an aggressive environment similar to oral cavity.

  19. Recovery of homogeneous polyoxometallate catalysts from aqueous and organic media by a mesoporous ceramic membrane without loss of catalytic activity.

    Science.gov (United States)

    Roy Chowdhury, Sankhanilay; Witte, Peter T; Blank, Dave H A; Alsters, Paul L; Ten Elshof, Johan E

    2006-04-03

    The recovery of homogeneous polyoxometallate (POM) oxidation catalysts from aqueous and non-aqueous media by a nanofiltration process using mesoporous gamma-alumina membranes is reported. The recovery of Q(12)[WZn(3)(ZnW(9)O(34))(2)] (Q=[MeN(n-C(8)H(17))(3)](+)) from toluene-based media was quantitative within experimental error, while up to 97 % of Na(12)[WZn(3)(ZnW(9)O(34))(2)] could be recovered from water. The toluene-soluble POM catalyst was used repeatedly in the conversion of cyclooctene to cyclooctene oxide and separated from the product mixture after each reaction. The catalytic activity increased steadily with the number of times that the catalyst had been recycled, which was attributed to partial removal of the excess QCl that is known to have a negative influence on the catalytic activity. Differences in the permeability of the membrane for different liquid media can be attributed to viscosity differences and/or capillary condensation effects. The influence of membrane pore radius on permeability and recovery is discussed.

  20. Master sintering curves of two different alumina powder compacts

    Directory of Open Access Journals (Sweden)

    Vaclav Pouchly

    2009-12-01

    Full Text Available Concept of Master Sintering Curve is a strong tool for optimizing sintering schedule. The sintering behaviour can be predicted, and sintering activation energy can be calculated with the help of few dilatometric measurements. In this paper an automatic procedure was used to calculate Master Sintering Curves of two different alumina compacts. The sintering activation energies were determined as 640 kJ/mol for alumina with particle size of 240 nm, respective 770 kJ/mol for alumina with particle size of 110 nm. The possibility to predict sintering behaviour with the help of Master Sintering Curve was verified.

  1. Effect of alumina on the dissolution rate of glasses

    International Nuclear Information System (INIS)

    Palavit, G.; Montagne, L.

    1997-01-01

    Small alumina addition to silicate glasses improves their chemical durability, but a large amount of alumina can also be beneficial to obtain a high dissolution rate. This paper describes the effect of Al 3+ on the early stage of glass alteration, in relation with its coordination in the glass and also with the reactions involved (hydrolysis and ionic exchange). We describe briefly nuclear magnetic resonance tools available to characterize the aluminum environments in the glasses. The rote of alumina on the dissolution rate of phosphate glasses is also discussed in order to show that the effect of Al 3+ is dependant upon the nature of the glass matrix. (author)

  2. Activated alumina preparation and characterization: The review on recent advancement

    Science.gov (United States)

    Rabia, A. R.; Ibrahim, A. H.; Zulkepli, N. N.

    2018-03-01

    Aluminum and aluminum based material are significant industrial materials synthesis because of their abandonment, low weight and high-quality corrosion resistance. The most advances in aluminum processing are the ability to synthesize it's under suitable chemical composition and conditions, a porous structure can be formed on the surface. Activated alumina particles (AAP) synthesized by the electrochemically process from aluminum have gained serious attention, inexpensive material that can be employed for water filtration due to its active surface. Thus, the paper present a review study based on recent progress and advances in synthesizing activated alumina, various techniques currently being used in preparing activated alumina and its characteristics are studied and summarized

  3. Plasma sprayed alumina-titania coatings

    International Nuclear Information System (INIS)

    Steeper, T.J.; Rotolico, A.J.; Nerz, J.E.; Riggs, W.L. II; Varacalle, D.J. Jr.; Wilson, G.C.

    1992-01-01

    This paper presents an experimental study of the air plasma spraying (APS) of alumina-titania powder using argon-hydrogen working gases. This powder system is being used in the fabrication of heater tubes that emulate nuclear fuel tubes for use in thermal-hydraulic testing. Experiments were conducted using a Taguchi fractional-factorial design parametric study. Operating parameters were varied around the typical spray parameters in a systematic design of experiments in order to display the range of plasma processing conditions and their effect on the resultant coatings. The coatings were characterized by hardness and electrical tests, surface profilometry, image analysis, optical metallography, and x-ray diffraction. Coating qualities are discussed with respect to dielectric strength, hardness, porosity, surface roughness, deposition efficiency, and microstructure. attempts are made to correlate the features of the coatings with the changes in operating parameters

  4. Alumina strength degradation in the elastic regime

    International Nuclear Information System (INIS)

    Furnish, Michael D.; Chhabildas, Lalit C.

    1998-01-01

    Measurements of Kanel et al. [1991] have suggested that deviatoric stresses in glasses shocked to nearly the Hugoniot Elastic Limit (HEL) relax over a time span of microseconds after initial loading. 'Failure' (damage) waves have been inferred on the basis of these measurements using time-resolved manganin normal and transverse stress gauges. Additional experiments on glass by other researchers, using time-resolved gauges, high-speed photography and spall strength determinations have also lead to the same conclusions. In the present study we have conducted transmitted-wave experiments on high-quality Coors AD995 alumina shocked to roughly 5 and 7 GPa (just below or at the HEL). The material is subsequently reshocked to just above its elastic limit. Results of these experiments do show some evidence of strength degradation in the elastic regime

  5. Compositional characterization of atomic layer deposited alumina

    Energy Technology Data Exchange (ETDEWEB)

    Philip, Anu; Thomas, Subin; Kumar, K. Rajeev [Department of Instrumentation, Cochin University of Science and Technology, Cochin-22, Kerala (India)

    2014-01-28

    As the microelectronic industry demands feature size in the order of few and sub nanometer regime, the film composition and other film properties become critical issues and ALD has emerged as the choice of industry. Aluminum oxide is a material with wide applications in electronic and optoelectronic devices and protective and ion barrier layers. Al{sub 2}O{sub 3} is an excellent dielectric because of its large band gap (8.7eV), large band offsets with silicon. We have deposited thin layers of alumina on silicon wafer (p-type) for gate dielectric applications by ALD technique and compositional characterizations of the deposited thin films were done using EDS, XPS and FTIR spectra.

  6. Compositional characterization of atomic layer deposited alumina

    International Nuclear Information System (INIS)

    Philip, Anu; Thomas, Subin; Kumar, K. Rajeev

    2014-01-01

    As the microelectronic industry demands feature size in the order of few and sub nanometer regime, the film composition and other film properties become critical issues and ALD has emerged as the choice of industry. Aluminum oxide is a material with wide applications in electronic and optoelectronic devices and protective and ion barrier layers. Al 2 O 3 is an excellent dielectric because of its large band gap (8.7eV), large band offsets with silicon. We have deposited thin layers of alumina on silicon wafer (p-type) for gate dielectric applications by ALD technique and compositional characterizations of the deposited thin films were done using EDS, XPS and FTIR spectra

  7. Rheological properties of alumina injection feedstocks

    Directory of Open Access Journals (Sweden)

    Vivian Alexandra Krauss

    2005-06-01

    Full Text Available The rheological behavior of alumina molding feedstocks containing polyethylene glycol (PEG, polyvinylbutyral (PVB and stearic acid (SA and having different powder loads were analyzed using a capillary rheometer. Some of the feedstocks showed a pseudoplastic behavior of n < 0, which can lead to the appearance of weld lines on molded parts. Their viscosity also displayed a strong dependence on the shear rate. The slip phenomenon, which can cause an unsteady front flow, was also observed. The results indicate that the feedstock containing a lower powder load displayed the best rheological behavior. The 55 vol. % powder loaded feedstock presented the best rheological behavior, thus appearing to be more suitable than the formulation containing a vol. 59% powder load, which attained viscosities exceeding 10³ Pa.s at low shear rates, indicating its unsuitability for injection molding.

  8. Two steps sintering alumina doped with niobia

    International Nuclear Information System (INIS)

    Gomes, L.B.; Hatzfeld, J.; Heck, M.; Pokorny, A.; Bergmann, C.P.

    2014-01-01

    In this work, high surface area commercial alumina was doped with niobia and sintered in two steps in order to obtain dense materials with lower processing temperatures. The powders were milled and uniaxially pressed (200 MPa). The first step of sintering took place at 1100°C for 3, 6, 9 and 12 hours, followed by the second step at 1350°C for 3 hours. The relative density, porosity and water absorption of the samples were determined by the Archimedes method. The crystalline phases were analyzed by X-ray Diffraction (XRD) and the morphology of the samples after sintering, evaluated by Scanning Electron Microscopy (SEM). The results indicate that the use of niobia combined with the two steps sintering promotes an increase in the density of the material, even at lower sintering temperatures. (author)

  9. Characterization of alumina suspensions by electroacoustics

    Energy Technology Data Exchange (ETDEWEB)

    Galassi, C.; Roncari, E.; Greenwood, R.; Piancastelli, A. [CNR, Faenza (Italy). Research Inst. for Ceramics Technology

    1997-12-31

    Using the acoustophoresis technique three different dispersants were selected to investigate the effect of the volume fraction of the suspension on the minimum amount of dispersant required to give the maximum zeta potential. No effect was detected over a volume fraction range 0.11 to 0.35. The acoustosizer was used to screen many dispersants for alumina in a relatively short time. From the viewpoint that the most stable suspensions are those with the greatest zeta potentials, then the following dispersants can be recommended: Reotan LA (0.25 mg/m{sup 2}) Dolapix CA (0.20 mg/m{sup 2}) and Dolapix PC33 (0.30 mg/m{sup 2}). Vanisperse and Borresperse are poor. Polyacrylic acid and polymethacrylic acid were better than some commercially available products. (orig.) 2 refs.

  10. Aluminum matrix composites reinforced with alumina nanoparticles

    CERN Document Server

    Casati, Riccardo

    2016-01-01

    This book describes the latest efforts to develop aluminum nanocomposites with enhanced damping and mechanical properties and good workability. The nanocomposites exhibited high strength, improved damping behavior and good ductility, making them suitable for use as wires. Since the production of metal matrix nanocomposites by conventional melting processes is considered extremely problematic (because of the poor wettability of the nanoparticles), different powder metallurgy routes were investigated, including high-energy ball milling and unconventional compaction methods. Special attention was paid to the structural characterization at the micro- and nanoscale, as uniform nanoparticle dispersion in metal matrix is of prime importance. The aluminum nanocomposites displayed an ultrafine microstructure reinforced with alumina nanoparticles produced in situ or added ex situ. The physical, mechanical and functional characteristics of the materials produced were evaluated using different mechanical tests and micros...

  11. The local strength of microscopic alumina reinforcements

    International Nuclear Information System (INIS)

    Žagar, Goran; Pejchal, Václav; Mueller, Martin G.; Rossoll, Andreas; Cantoni, Marco; Mortensen, Andreas

    2015-01-01

    We measure, using an adaptation of a method designed for ceramic ball bearings, the local strength of a brittle second phase that serves to reinforce a metal. The method uses focused ion beam milling and a nanoindentation device, and is free of artifacts commonly present in micromachined specimens. It is demonstrated on Nextel 610™ nanocrystalline alumina fibers embedded in an aluminum matrix composite. Results reveal a size effect that does not follow, across size scales, usual Weibull statistics: the fiber strength distribution differs between measurements at the microscale and macroscopic tensile testing. This implies that, in micromechanical analysis of multiphase materials, highly localized events such as the propagation of internal damage require input data that must be measured at the same, local, microscale as the event; the present work opens a path to this end.

  12. Ultra-high-density 3D DNA arrays within nanoporous biocompatible membranes for single-molecule-level detection and purification of circulating nucleic acids

    Czech Academy of Sciences Publication Activity Database

    Aramesh, M.; Shimoni, O.; Fox, K.; Karle, T.J.; Lohrmann, A.; Ostrikov, K.; Prawer, S.; Červenka, Jiří

    2015-01-01

    Roč. 7, č. 14 (2015), s. 5998-6006 ISSN 2040-3364 Institutional support: RVO:68378271 Keywords : Fourier-transform spectroscopy * alumina membranes * oligonucleotide hybridization Subject RIV: BO - Biophysics Impact factor: 7.760, year: 2015

  13. Fabrication and Molecular Transport Studies of Highly c-Oriented AFI Membranes

    KAUST Repository

    Liu, Yang; Zhang, Bing; Liu, Defei; Sheng, Ping; Lai, Zhiping

    2017-01-01

    -packed and c-oriented monolayer of plate-like seeds that is manually assembled on a porous alumina support. The straight channels in the membrane are not only aligned vertically along the membrane depth, but are also continuous without disruption. The transport

  14. Analysis and theory of gas transport in microporous sol-gel derived ceramic membranes

    NARCIS (Netherlands)

    de Lange, R.S.A.; de Lange, Rob; Keizer, Klaas; Burggraaf, Anthonie; Burggraaf, A.J.

    1995-01-01

    Sol-gel modification of mesoporous alumina membranes is a very successful technique to improve gas separation performance. Due to the formed microporous top layer, the membranes show activated transport and molecular sieve-like separation factors. This paper concentrates on the mechanism of

  15. Influence of the Si/Al ratio on the separation properties of SSZ-13 zeolite membranes

    NARCIS (Netherlands)

    Kosinov, N.; Auffret, C.; Borghuis, G.J.; Sripathi, V.G.P.; Hensen, E.J.M.

    2015-01-01

    SSZ-13 (CHA) zeolite membranes supported by a-alumina hollow fibers were prepared by a hydrothermal secondary growth method. The gel Si/Al ratio was varied between 5 and 100. The water adsorption depended strongly on the Si/Al ratio. Comparatively, ethanol adsorption varied less with membrane

  16. Finger-like voids induced by viscous fingering during phase inversion of alumina/PES/NMP suspensions

    KAUST Repository

    Wang, Bo

    2012-07-01

    The formation mechanism of phase-inversion ceramic hollow fibre membranes has not been well understood. In this paper, we report on the formation of finger-like macrovoids during non-solvent-induced phase inversion of alumina/PES/NMP suspensions. A membrane structure without such finger-like macrovoids was observed when the suspension was slowly immersed into pure ethanol or a mixture of 70. wt% NMP and 30. wt% water, whereas finger-like macrovoids occurred when the suspension was slid into the non-solvents at higher speeds. We found that the formation process of finger-like macrovoids could be fully or partially reversed when nascent membranes were taken out from water shortly after immersion, depending on the duration of the immersion. Splitting of the fingers during the formation of the macrovoids was also observed during the phase inversion of two alumina/PES/NMP suspensions. These experimental observations were not predicted by current theories of finger-like macrovoid formation in polymer membranes, but appear to mimic the well-known viscous fingering phenomenon. We therefore propose that in the phase inversion of ceramic suspensions, the viscous fingering phenomenon is an important mechanism in the formation of finger-like voids. © 2012 Elsevier B.V.

  17. Natural gas purification using supported ionic liquid membrane

    NARCIS (Netherlands)

    Althuluth, M.A.M.; Overbeek, J.P.; Wees, H.J.; Zubeir, L.F.; Haije, W.G.; Berrouk, A.S.; Peters, C.J.; Kroon, M.C.

    2015-01-01

    This paper examines the possibility of the application of a supported ionic liquid membrane (SILM) for natural gas purification. The ionic liquid (IL) 1-ethyl-3-methylimidazolium tris(pentafluoroethyl)trifluorophosphate ([emim][FAP]) was impregnated successfully in the ¿-alumina layer of a tubular

  18. Glass transition temperature of PMMA/modified alumina nanocomposite: Molecular dynamic study

    OpenAIRE

    Mohammadi, Maryam; Davoodi, Jamal; Javanbakht, Mahdi; Rezaei, Hamidreza

    2017-01-01

    In this study, the effect of alumina and modified alumina nanoparticles in a PMMA/alumina nanocomposite was investigated. To attain this goal, the glass transition behavior of poly methyl methacrylate (PMMA), PMMA/alumina and PMMA/hydroxylated alumina nanocomposites were investigated by molecular dynamic simulations (MD). All the MD simulations were performed using the Materials Studio 6.0 software package of Accelrys. To obtain the glass transition temperature, the variation of density vs. t...

  19. Study of cross-linking reactions induced by gamma rays in hybrid membranes of Bisphenol-A-Polysulfone and precipitated silica; Estudo da formacao de ligacoes cruzadas por irradiacao gama em membranas hibridas de Polissulfona Bisfenol-A e silica precipitada

    Energy Technology Data Exchange (ETDEWEB)

    Furtado Filho, Acacio Antonio M., E-mail: facacio@ctex.eb.br [Laboratorio de Quimica Militar, CTEx, Rio de Janeiro, RJ (Brazil); Gomes, Ailton de S.; Lopes, Lea; Benzi, Marcia R. [Instituto de Macromoleculas Professora Eloisa Mano, UFRJ, Rio de Janeiro, RJ (Brazil)

    2011-07-01

    In this work the bisphenol-A-polysulfone (PSF) was sulfonated using trimethyl silyl chlorosulfonate [(CH{sub 3}){sub 3}SiSO{sub 3}Cl] as a mild sulfonating agent in a homogeneous solution of dichloroethane. The sulfonation reaction was confirmed by acid-base titration and FTIR-spectroscopy analysis. The hybrid membranes were obtained by casting the sulfonated bisphenol-A-polysulfone (SPSF) and precipitated silica Tixosil{sup R} 333 solutions in N-N-dimethylacetamide. Cross-linking in the hybrid membranes was obtained by irradiation, with doses ranging from 5 to 30 kGy using gamma ray from a {sup 60}Co source. The water uptake and the swelling of the membranes were estimated by measuring the change in weight between dry and wet conditions. The conductivity of the membranes in acid form was measured with the ac impedance technique using a PGSTAT30 frequency response analyzer. The hybrid cross-linked membranes have conductivity close to 10-1 S.cm{sup -1} at 100% RH and 80 deg C. Electrochemical performances, thermo-mechanical stability and low cost make this cross-linked SPSF hybrid membrane an attractive material for fuel cells using a proton exchange membrane. (author)

  20. Study on rich alumina alkali-activated slag clay minerals cementitious materials for immobilization of radioactive waste

    International Nuclear Information System (INIS)

    Li Yuxiang; Qian Guangren; Yi Facheng; Shi Rongming; Fu Yibei; Li Lihua; Zhang Jun

    1999-01-01

    The composition and some properties of its pastes of rich alumina alkali-activated slag clay minerals (RAAASCM) cementitious materials for immobilization of radioactive waste are studied. Experimental results show that heat activated kaolinite, Xingjiang zeolite, modified attapulgite clay are better constituents of RAAASCM. RAAASCM cementitious materials pastes exhibit high strength, low porosity, fewer harmful pore, and high resistance to sulphate corrosion as well as gamma irradiation. The Sr 2+ , Cs + leaching portion of the simulated radioactive waste forms based on RAAASCM, is low

  1. Synthesis and structure of porous alumina precursors derived from n-alkylamine-AlCl3 system; Chokusa alkylamine-AlCl{sub 3} kei wo mochiiru takoshitsu alumina zenkutai no gosei to kozo

    Energy Technology Data Exchange (ETDEWEB)

    Yoshimura, M.; Machida, M.; Kijima, T. [Miyazaki Univ. (Japan)

    1998-06-01

    Alumina precursors have been prepared from AlCl3 by using n-alkylamines (C{sub n}H{sub 2n+1}NH2) as precipitant at pH 9.6 and pH 6.2, and the structure, composition, microstructure, and thermal decomposition behavior are investigated. The effects of the structure of the precursor on the decomposition behavior and on the surface area of porous alumina are also investigated. When alkylamines n{>=}6 are used, long periodicity phases are produced corresponding to larger than d=2.0nm spacing which can not be attributed to bayerite or pseudo-boehnite. Long periodicity phase is formed uniquely near the water content of about 50mass% (H2O/Al=4.5), and the spacing varies depending on the alkyl chainlength of amine. When the precipitate prepared at pH 6.2 is heated, water is desorbed at near 100degC, pseudo-baehnite phase is pyrolyzed at 300degC, and the precipitate changed into {gamma}-alumina at temperatures higher than 500degC. 16 refs., 9 figs.

  2. Characterisation of the acidity and the basicity of transition alumina by NMR and FTIR spectroscopy of adsorption of probe molecules; Caracterisation par RMN et infrarouge de molecules sondes adsorbees, de l'acidite et de la basicite d'alumines de transition

    Energy Technology Data Exchange (ETDEWEB)

    Mathonneau, E.

    2003-04-01

    This work has been devoted to characterization of the acidity and the basicity of the surface of transition alumina. Three different alumina (Alumina-{gamma}, -{delta} et -{theta} ({gamma}-Al, {delta}-Al, {theta}-Al)) have been studied by adsorption of probe molecules such trimethyl phosphine and carbon monoxide (acidity study); and tri-ethyl borane (basicity study). We emphasized that the acidity increases with an increasing pretreatment temperature where as the basicity decreases. Comparing quantitative results from the different probe molecules we could show an increasing strength acidity following: {gamma}-Al > {theta}-Al > {delta}-Al, and basicity following: {delta}-Al > {gamma}-Al > {theta}-Al. We could evaluate on a qualitative (nature and repartition) and on a quantitative point of view the impact of the transformations {gamma}-Al {yields} {delta}-Al and {gamma}-Al > {theta}-Al on the acid-basicity of the surface. We could also explain catalytic reactivity differences between alumina for the position isomerization of butene-1. (author)

  3. New Polymeric Membranes for Organic Solvent Nanofiltration

    KAUST Repository

    Aburabie, Jamaliah

    2017-05-01

    The focus of this dissertation was the development, synthesis and modification of polymers for the preparation of membranes for organic solvent nanofiltration. High chemical stability in a wide range of solvents was a key requirement. Membranes prepared from synthesized polymers as well as from commercial polymers were designed and chemically modified to reach OSN requirements. A solvent stable thin-film composite (TFC) membrane is reported, which is fabricated on crosslinked polythiosemicarbazide (PTSC) as substrate. The membranes exhibited high fluxes towards solvents like THF, DMF and DMSO ranging around 20 L/m2 h at 5 bar with a MWCO of around 1000 g/mol. Ultrafiltration PTSC membranes were prepared by non-solvent induced phase separation and crosslinked with GPTMS. The crosslinking reaction was responsible for the formation of an inorganic-type-network that tuned the membrane pore size. The crosslinked membranes acquired high solvent stability in DMSO, DMF and THF with a MWCO above 1300 g/mol. Reaction Induced Phase Separation (RIPS) was introduced as a new method for the preparation of skinned asymmetric membranes. These membranes have two distinctive layers with different morphologies both from the same polymer. The top dense layer is composed of chemically crosslinked polymer chains while the bottom layer is a porous structure formed by non-crosslinked polymer chains. Such membranes were tested for vitamin B12 in solvents after either crosslinking the support or dissolving the support and fixing the freestanding membrane on alumina. Pebax® 1657 was utilized for the preparation of composite membranes by simple coating. Porous PAN membranes were coated with Pebax® 1657 which was then crosslinked using TDI. Crosslinked Pebax® membranes show high stability towards ethanol, propanol and acetone. The membranes were also stable in DMF once crosslinked PAN supports were used. Sodium alginate polymer was investigated for the preparation of thin film composite

  4. Membrane dynamics

    DEFF Research Database (Denmark)

    Bendix, Pól Martin

    2015-01-01

    Current topics include membrane-protein interactions with regard to membrane deformation or curvature sensing by BAR domains. Also, we study the dynamics of membrane tubes of both cells and simple model membrane tubes. Finally, we study membrane phase behavior which has important implications...... for the lateral organization of membranes as wells as for physical properties like bending, permeability and elasticity...

  5. Alumina-on-Polyethylene Bearing Surfaces in Total Hip Arthroplasty.

    Science.gov (United States)

    Jung, Yup Lee; Kim, Shin-Yoon

    2010-02-11

    The long-term durability of polyethylene lining total hip arthroplasty (THA) mainly depends on periprosthetic osteolysis due to wear particles, especially in young active patients. In hip simulator study, reports revealed significant wear reduction of the alumina ceramic-on-polyethylene articulation of THA compared with metal-on-polyethylene bearing surfaces. However, medium to long-term clinical studies of THA using the alumina ceramic-on-polyethylene are few and the reported wear rate of this articulation is variable. We reviewed the advantages and disadvantages of ceramicon- polyethylene articulation in THA, hip simulator study and retrieval study for polyethylene wear, in vivo clinical results of THA using alumina ceramic-on-polyethylene bearing surfaces in the literature, and new trial alumina ceramic-onhighly cross linked polyethylene bearing surfaces.

  6. Synthesis of beta alumina from aluminum hydroxide and oxyhydroxide precursors

    CSIR Research Space (South Africa)

    Van Zyl, A

    1993-02-01

    Full Text Available Two aluminium oxyhydroxides, boehmite and pseudoboehmite, and two aluminium hydroxides, bayerite and gibbsite, have been investigated as precursors for the synthesis of the solid electrolyte, beta alumina. Reaction pathways and products have been...

  7. Significance of structure–property relationship in alumina based ...

    Indian Academy of Sciences (India)

    Unknown

    adverse environmental conditions and mechanical vibra- tions. Most ceramic ... However, even alumina insulators manufactured (for use in 25 kV railway traction ..... early showed plastic deformation and large cracks in and around the indents.

  8. Ceramic joining through reactive wetting of alumina with calcium ...

    Indian Academy of Sciences (India)

    phase analysis of the fractured joint surface clearly indicate reactive wetting of the alumina ceramics. This wetting enhances ... ally considered oxide materials for many applications. .... three cases but is more pronounced in the case of C12A7.

  9. Failure Analysis of Alumina Reinforced Aluminum Microtruss and Tube Composites

    Science.gov (United States)

    Chien, Hsueh Fen (Karen)

    The energy absorption capacity of cellular materials can be dramatically increased by applying a structural coating. This thesis examined the failure mechanisms of alumina reinforced 3003 aluminum alloy microtrusses and tubes. Alumina coatings were produced by hard anodizing and by plasma electrolytic oxidation (PEO). The relatively thin and discontinuous oxide coating at the hinge acted as a localized weak spot which triggered a chain reaction of failure, including oxide fracture, oxide spallation, oxide penetration to the aluminum core and severe local plastic deformation of the core. For the PEO microtrusses, delamination occurred within the oxide coating resulting in a global strut buckling failure mode. A new failure mode for the anodized tubes was observed: (i) axisymmetric folding of the aluminum core, (ii) longitudinal fracture, and (iii) alumina pulverization. Overall, the alumina coating enhanced the buckling resistance of the composites, while the aluminum core supported the oxide during the damage propagation.

  10. Characterization of the Uptake of Nitrogen Oxides on Alumina Adsorbents

    National Research Council Canada - National Science Library

    Pocengal, David

    1999-01-01

    ...) to quantify nitrate and nitrite (NOx) in aqueous solutions that contained NOx exposed alumina and to correlate the quantities of these surface NOx species with the quantity of gaseous NOx sorbed...

  11. Surface chloride salt formation on Space Shuttle exhaust alumina

    Science.gov (United States)

    Cofer, W. R., III; Pellett, G. L.; Sebacher, D. I.; Wakelyn, N. T.

    1984-01-01

    Aluminum oxide samples from the exhaust of Space Shuttle launches STS-1, STS-4, STS-5, and STS-6 were collected from surfaces on or around the launch pad complex and chemically analyzed. The results indicate that the particulate solid-propellant rocket motor (SRM) alumina was heavily chlorided. Concentrations of water-soluble aluminum (III) ion were large, suggesting that the surface of the SRM alumina particles was rendered soluble by prior reactions with HCl and H2O in the SRM exhaust cloud. These results suggest that Space Shuttle exhaust alumina particles are good sites for nucleation and condensation of atmospheric water. Laboratory experiments conducted at 220 C suggest that partial surface chloriding of alumina may occur in hot Space Shuttle exhaust plumes.

  12. Processing and characterization of alumina/LAS bioceramics for ...

    Indian Academy of Sciences (India)

    Administrator

    dental applications. M GUEDES1,4,*, V .... Alumina/LAS bioceramics for dental applications. 697 strength ... assessment. ... indentation load (N) and c is the median length (m) of the ... mixtures show two distinct modes, reflecting both the.

  13. Synthesis of α-Alumina (Corundum) and its Application

    International Nuclear Information System (INIS)

    Nay Thwe Kyi; Kyaw Myo Naing; Tin Tin Aye; Nyunt Wynn

    2005-09-01

    This paper described the preparation of aluminium isopropoxide from aluminium sheet at different heating times.Aluminium sheet is found to have a reaction with absolute isopropyl alcohol and mercury (II) chloride as a catalyst under nitrogen atmosphere. Aluminium isopropoxide was characterized by NMR, XRD and IR. Aluminium isopropoxide serves as a molecular precursor to derive pure alumina gel by hydrolysis under both homogeneous and heterogeneous conditions. Pyrolysis to this alumina gel transforms it into -aluminia (corundum) at 1200'C. The phase transformation during pyrolysis was characterized by XRD, SEM and TEM. The alumina (corundum) has porous crystalline nature with high surface aera, which may be used as efficient adsorbent packing material in coloumn chromatography for the seperation of vitamin A from the leaves. -alumina can be also used in catalysis

  14. Effect of chemical composition and alumina content on structure and ...

    Indian Academy of Sciences (India)

    porcelain types (Morrell 1985; Vazquez and Mejia Velasquez. 1998). By increasing ... Orlova et al found that, in alumina porcelains, opti- mum mechanical ... of high mobility of ions, acceptable electrical performance may be achieved with ...

  15. Alumina-on-Polyethylene Bearing Surfaces in Total Hip Arthroplasty

    OpenAIRE

    Jung, Yup Lee; Kim, Shin-Yoon

    2010-01-01

    The long-term durability of polyethylene lining total hip arthroplasty (THA) mainly depends on periprosthetic osteolysis due to wear particles, especially in young active patients. In hip simulator study, reports revealed significant wear reduction of the alumina ceramic-on-polyethylene articulation of THA compared with metal-on-polyethylene bearing surfaces. However, medium to long-term clinical studies of THA using the alumina ceramic-on-polyethylene are few and the reported wear rate of th...

  16. Novel Translucent and Strong Submicron Alumina Ceramics for Dental Restorations.

    Science.gov (United States)

    Zhao, M; Sun, Y; Zhang, J; Zhang, Y

    2018-03-01

    An ideal ceramic restorative material should possess excellent aesthetic and mechanical properties. We hypothesize that the high translucency and strength of polycrystalline ceramics can be achieved through microstructural tailoring. The aim of this study is to demonstrate the superior optical and mechanical properties of a new class of submicron grain-sized alumina ceramics relative to the current state-of-the-art dental ceramic materials. The translucency, the in-line transmission ( T IT ) in particular, of these submicron alumina ceramics has been examined with the Rayleigh-Gans-Debye light-scattering model. The theoretical predictions related very well with the measured T IT values. The translucency parameter ( TP) and contrast ratio ( CR) of the newly developed aluminas were measured with a reflectance spectrophotometer on a black-and-white background. For comparison, the T IT , TP, and CR values for a variety of dental ceramics, mostly measured in-house but also cited from the literature, were included. The flexural strength of the aluminas was determined with the 4-point bending test. Our findings have shown that for polycrystalline alumina ceramics, an average grain size ceramic and zirconias, including the most translucent cubic-containing zirconias. The strength of these submicron grain-sized aluminas was significantly higher than that of the cubic-containing zirconia (e.g., Zpex Smile) and lithia-based glass-ceramics (e.g., IPS e.max CAD HT). A coarse-grained alumina could also reach a translucency level comparable to that of dental porcelain. However, the relatively low strength of this material has limited its clinical indications to structurally less demanding applications, such as orthodontic brackets. With a combined high strength and translucency, the newly developed submicron grain-sized alumina may be considered a suitable material for dental restorations.

  17. Self-ordered Porous Alumina Fabricated via Phosphonic Acid Anodizing

    OpenAIRE

    Akiya, Shunta; Kikuchi, Tatsuya; Natsui, Shungo; Sakaguchi, Norihito; Suzuki, Ryosuke O.

    2016-01-01

    Self-ordered periodic porous alumina with an undiscovered cell diameter was fabricated via electrochemical anodizing in a new electrolyte, phosphonic acid (H3PO3). High-purity aluminum plates were anodized in phosphonic acid solution under various operating conditions of voltage, temperature, concentration, and anodizing time. Phosphonic acid anodizing at 150-180 V caused the self-ordering behavior of porous alumina, and an ideal honeycomb nanostructure measuring 370-440 nm in cell diameter w...

  18. Interface chemistry of nanostructured materials: ion adsorption on mesoporous alumina.

    Science.gov (United States)

    Wang, Yifeng; Bryan, Charles; Xu, Huifang; Pohl, Phil; Yang, Yi; Brinker, C Jeffrey

    2002-10-01

    This paper presents a part of our work on understanding the effect of nanoscale pore space confinement on ion sorption by mesoporous materials. Acid-base titration experiments were performed on both mesoporous alumina and alumina particles under various ionic strengths. The point of zero charge (PZC) for mesoporous alumina was measured to be approximately 9.1, similar to that for nonmesoporous alumina materials, indicating that nanoscale pore space confinement does not have a significant effect on the PZC of pore surfaces. However, for a given pH deviation from the PZC, (pH-PZC), the surface charge per mass on mesoporous alumina was as much as 45 times higher than that on alumina particles. This difference cannot be fully explained by the surface area difference between the two materials. Our titration data have demonstrated that nanoscale confinement has a significant effect, most likely via the overlap of the electric double layer (EDL), on ion sorption onto mesopore surfaces. This effect cannot be adequately modeled by existing surface complexation models, which were developed mostly for an unconfined solid-water interface. Our titration data have also indicated that the rate of ion uptake by mesoporous alumina is relatively slow, probably due to diffusion into mesopores, and complete equilibration for sorption could take 4-5 min. A molecular simulation using a density functional theory was performed to calculate ion adsorption coefficients as a function of pore size. The calculation has shown that as pore size is reduced to nanoscales (<10 nm), the adsorption coefficients of ions can vary by more than two orders of magnitude relative to those for unconfined interfaces. The prediction is supported by our experimental data on Zn sorption onto mesoporous alumina. Owing to their unique surface chemistry, mesoporous materials can potentially be used as effective ion adsorbents for separation processes and environmental cleanup.

  19. Alumina Concentration Detection Based on the Kernel Extreme Learning Machine.

    Science.gov (United States)

    Zhang, Sen; Zhang, Tao; Yin, Yixin; Xiao, Wendong

    2017-09-01

    The concentration of alumina in the electrolyte is of great significance during the production of aluminum. The amount of the alumina concentration may lead to unbalanced material distribution and low production efficiency and affect the stability of the aluminum reduction cell and current efficiency. The existing methods cannot meet the needs for online measurement because industrial aluminum electrolysis has the characteristics of high temperature, strong magnetic field, coupled parameters, and high nonlinearity. Currently, there are no sensors or equipment that can detect the alumina concentration on line. Most companies acquire the alumina concentration from the electrolyte samples which are analyzed through an X-ray fluorescence spectrometer. To solve the problem, the paper proposes a soft sensing model based on a kernel extreme learning machine algorithm that takes the kernel function into the extreme learning machine. K-fold cross validation is used to estimate the generalization error. The proposed soft sensing algorithm can detect alumina concentration by the electrical signals such as voltages and currents of the anode rods. The predicted results show that the proposed approach can give more accurate estimations of alumina concentration with faster learning speed compared with the other methods such as the basic ELM, BP, and SVM.

  20. Antimicrobial Properties of Chitosan-Alumina/f-MWCNT Nano composites

    International Nuclear Information System (INIS)

    Masheane, M.; Nthunya, L.; Malinga, S.; Masheane, M.; Nthunya, L.; Nxumalo, E.; Mhlanga, S.; Barnard, T.

    2016-01-01

    Antimicrobial chitosan-alumina/functionalized-multi walled carbon nano tube (f-MWCNT) nano composites were prepared by a simple phase inversion method. Scanning electron microscopy (SEM) analyses showed the change in the internal morphology of the composites and energy dispersive spectroscopy (EDS) confirmed the presence of alumina and f-MWCNTs in the chitosan polymer matrix. Fourier transform infrared (FTIR) spectroscopy showed the appearance of new functional groups from both alumina and f-MWCNTs, and thermogravimetric analysis (TGA) revealed that the addition of alumina and f-MWCNTs improved the thermal stability of the chitosan polymer. The presence of alumina and f-MWCNTs in the polymer matrix was found to improve the thermal stability and reduced the solubility of chitosan polymer. The prepared chitosan-alumina/f-MWCNT nano composites showed inhibition of twelve strains of bacterial strains that were tested. Thus, the nano composites show a potential for use as a biocides in water treatment for the removal of bacteria at different environmental conditions.

  1. Superhydrophobic surfaces fabricated by surface modification of alumina particles

    Science.gov (United States)

    Richard, Edna; Aruna, S. T.; Basu, Bharathibai J.

    2012-10-01

    The fabrication of superhydrophobic surfaces has attracted intense interest because of their widespread potential applications in various industrial fields. Recently, some attempts have been carried out to prepare superhydrophobic surfaces using metal oxide nanoparticles. In the present work, superhydrophobic surfaces were fabricated with low surface energy material on alumina particles with different sizes. It was found that particle size of alumina is an important factor in achieving stable superhydrophobic surface. It was possible to obtain alumina surface with water contact angle (WCA) of 156° and a sliding angle of Superhydrophobicity of the modified alumina is attributed to the combined effect of the micro-nanostructure and low surface energy of fatty acid on the surface. The surface morphology of the alumina powder and coatings was determined by FESEM. The stability of the coatings was assessed by conducting water immersion test. Effect of heat treatment on WCA of the coating was also studied. The transition of alumina from hydrophilic to superhydrophobic state was explained using Wenzel and Cassie models. The method is shown to have potential application for creating superhydrophobic surface on cotton fabrics.

  2. Study on the potential of water/oil of tubular alumina ceramics through flux and turbidity analysis; Estudo do potencial de separacao agua/oleo de membranas ceramicas tubulares de alumina atraves da analise das medidas de fluxo e turbidez

    Energy Technology Data Exchange (ETDEWEB)

    Silva, A.A; Melo, K.S. [Universidade Federal, Campina Grande, PB (Brazil)]. E-mail: adrianasilva_cg@yahoo.com.br; Maia, J.B.N.; Franca, R.V.; Silva, R.A.V.; Lira, H.L.; Carvalho, L.H. [Universidade Federal, Campina Grande, PB (Brazil). Dept. de Engenharia de Materiais]. E-mail: helio@dema.ufpb.br; Franca, K.B.; Rodrigues, M.G.F [Universidade Federal, Campina Grande, PB (Brazil). Dept. de Engenharia Quimica]. E-mail: kepler@labdes.ufpb.br

    2003-07-01

    In the last years, a considerable attention was given to the effluents composed by contaminated water with oil and the impact on the environment . The water pollution by oleaginous hydrocarbon is specially harmful to the aquatic life, decreasing the transmission of light and disturb the normal mechanism of oxygen transfer. So, to remove oil from water is an important aspect to control the pollution from several industries. The ceramic membranes act as a barrier for the emulsified oil. It has been studied enough as a medium to separate oil/ water from stable emulsions. The objective of this work is to present an evaluation of the separation potential of a tubular alumina ceramic membrane made in laboratory from Materials Engineering Department, Federal University of Campina Grande (UFCG). It was done test of flux and concentration of oil the permeate. The results showed that the membranes can be satisfactorily used in the oil/water separation. (author)

  3. Effects of Etching Time and NaOH Concentration on the Production of Alumina Nanowires Using Porous Anodic Alumina Template

    Science.gov (United States)

    Sadeghpour-Motlagh, M.; Mokhtari-Zonouzi, K.; Aghajani, H.; Kakroudi, M. Ghassemi

    2014-06-01

    In this work, two-step anodizing of commercial aluminum foil in acid oxalic solution was applied for producing alumina film. Then the anodic alumina film was etched in sodium hydroxide (NaOH) solution resulting dense and aligned alumina nanowires. This procedure leads to splitting of alumina nanotubes. Subsequently nanowires are produced. The effects of NaOH solution concentration (0.2-1 mol/L) and etching time (60-300 s) at constant temperature on characteristic of nanotubes and produced nanowires were investigated using scanning electron microscopy. The results show that an increase in NaOH solution concentration increases the rate of nanowires production and in turn the manipulation process will be more specific.

  4. A nanoporous alumina microelectrode array for functional cell–chip coupling

    International Nuclear Information System (INIS)

    Wesche, Manuel; Hüske, Martin; Yakushenko, Alexey; Brüggemann, Dorothea; Mayer, Dirk; Offenhäusser, Andreas; Wolfrum, Bernhard

    2012-01-01

    The design of electrode interfaces has a strong impact on cell-based bioelectronic applications. We present a new type of microelectrode array chip featuring a nanoporous alumina interface. The chip is fabricated in a combination of top-down and bottom-up processes using state-of-the-art clean room technology and self-assembled generation of nanopores by aluminum anodization. The electrode characteristics are investigated in phosphate buffered saline as well as under cell culture conditions. We show that the modified microelectrodes exhibit decreased impedance compared to planar microelectrodes, which is caused by a nanostructuring effect of the underlying gold during anodization. The stability and biocompatibility of the device are demonstrated by measuring action potentials from cardiomyocyte-like cells growing on top of the chip. Cross sections of the cell–surface interface reveal that the cell membrane seals the nanoporous alumina layer without bending into the sub-50 nm apertures. The nanoporous microelectrode array device may be used as a platform for combining extracellular recording of cell activity with stimulating topographical cues. (paper)

  5. Properties of single crystal beta''-aluminas

    International Nuclear Information System (INIS)

    Bates, J.B.; Brown, G.M.; Kaneda, T.; Brundage, W.E.; Wang, J.C.; Engstrom, H.

    1979-01-01

    Large single crystals of sodium beta''-alumina were grown by slow evaporation of Na 2 O at 1690 0 C from a mixture of Na 2 CO 3 , MgO, and Al 2 O 3 . Polarized Raman measurements were made on the Na β'' single crystals and on single crystals of Li, K, Rb, and Ag β'' prepared by ion exchange of Na β''. The low frequency Raman spectra of Na, K, Rb, and Ag β'' contained four or more bands due to vibrations of the mobile cations. These results were analyzed by assuming the spectra to be due to the normal modes of a defect cluster consisting of a cation vacancy surrounded by three cations. From model calculations, the Raman band of Na β'' at 33 cm -1 is assigned to the attempt mode for diffusion of Na + ions. The structure of a Ag β'' single crystal was investigated by neutron diffraction, and 20% of the Ag + ion sites were found to be vacant

  6. Coprecipitated nickel-alumina methanation catalysts

    International Nuclear Information System (INIS)

    Kruissink, E.C.

    1981-01-01

    In the last few years there has been a renewed interest in the methanation reaction CO+3H 2 =CH 4 +H 2 O. The investigations described in this thesis were performed in relation to the application of this reaction, within the framework of the so-called 'NFE' project, also called 'ADAM' and 'EVA' project. This project, which has been under investigation in West Germany for some years, aims at the investigation of the feasibility of transporting heat from a nuclear high temperature reactor by means of a chemical cycle. A promising possibility to realize such a cycle exists in applying the combination of the endothermic steam reforming of methane and the exothermic methanation reaction. This thesis describes the investigations into a certain type of methanation catalyst, viz. a coprecipitated nickel-alumina catalyst, with the aim to give more insight into the interrelationship between the preparation conditions on the one hand and catalyst properties such as activity and stability on the other hand. (Auth.)

  7. Red mud flocculation process in alumina production

    Science.gov (United States)

    Fedorova, E. R.; Firsov, A. Yu

    2018-05-01

    The process of thickening and washing red mud is a gooseneck of alumina production. The existing automated systems of the thickening process control involve stabilizing the parameters of the primary technological circuits of the thickener. The actual direction of scientific research is the creation and improvement of models and systems of the thickening process control by model. But the known models do not fully consider the presence of perturbing effects, in particular the particle size distribution in the feed process, distribution of floccules by size after the aggregation process in the feed barrel. The article is devoted to the basic concepts and terms used in writing the population balance algorithm. The population balance model is implemented in the MatLab environment. The result of the simulation is the particle size distribution after the flocculation process. This model allows one to foreseen the distribution range of floccules after the process of aggregation of red mud in the feed barrel. The mud of Jamaican bauxite was acting as an industrial sample of red mud; Cytec Industries of HX-3000 series with a concentration of 0.5% was acting as a flocculant. When simulating, model constants obtained in a tubular tank in the laboratories of CSIRO (Australia) were used.

  8. Effect of humic acid on sorption of technetium by alumina

    International Nuclear Information System (INIS)

    Kumar, S.; Rawat, N.; Kar, A.S.; Tomar, B.S.; Manchanda, V.K.

    2011-01-01

    Highlights: → Tc sorption on alumina has been studied under aerobic as well anaerobic condition over pH 3-10. → Effect of humic acid on sorption of Tc by alumina has been investigated. → Linear additive modeling and surface complexation modeling were carried out to delineate the role of humic acid in Tc(IV) sorption in ternary system of Tc(IV)-humic acid-alumina. → Sorption of humic acid onto alumina and strong complexation of Tc(IV) with humic acid were found to govern the sorption of Tc(IV) in the ternary system. - Abstract: Sorption of technetium by alumina has been studied in absence as well as in presence of humic acid using 95 Tc m as a tracer. Measurements were carried out at fixed ionic strength (0.1 M NaClO 4 ) under varying pH (3-10) as well as redox (aerobic and reducing anaerobic) conditions. Under aerobic conditions, negligible sorption of technetium was observed onto alumina both in absence and in presence of humic acid. However, under reducing conditions (simulated with [Sn(II)] = 10 -6 M), presence of humic acid enhanced the sorption of technetium in the low pH region significantly and decreased at higher pH with respect to that in absence of humic acid. Linear additive as well as surface complexation modeling of Tc(IV) sorption in presence of humic acid indicated the predominant role of sorbed humic acid in deciding technetium sorption onto alumina.

  9. Sterilization of heparinized cuprophan hemodialysis membranes

    OpenAIRE

    ten Hoopen, Hermina W.M.; Hinrichs, W.L.J.; Hinrichs, W.L.J.; Engbers, G.H.M.; Feijen, Jan

    1996-01-01

    The effects of sterilization of dry heparinized Cuprophan hemodialysis membranes by means of ethylene oxide (EtO) exposure, gamma irradiation, or steam on the anticoagulant activity and chemical characteristics of immobilized heparin and the permeability of the membrane were investigated. Sterilization did not result in a release of heparin or heparin fragments from heparinized Cuprophan. Sterilization of heparinized Cuprophan by means of EtO exposure and gamma irradiation induced a slight, i...

  10. Electroviscous Effects in Ceramic Nanofiltration Membranes.

    Science.gov (United States)

    Farsi, Ali; Boffa, Vittorio; Christensen, Morten Lykkegaard

    2015-11-16

    Membrane permeability and salt rejection of a γ-alumina nanofiltration membrane were studied and modeled for different salt solutions. Salt rejection was predicted by using the Donnan-steric pore model, in which the extended Nernst-Planck equation was applied to predict ion transport through the pores. The solvent flux was modeled by using the Hagen-Poiseuille equation by introducing electroviscosity instead of bulk viscosity. γ-Alumina particles were used for ζ-potential measurements. The ζ-potential measurements show that monovalent ions did not adsorb on the γ-alumina surface, whereas divalent ions were highly adsorbed. Thus, for divalent ions, the model was modified, owing to pore shrinkage caused by ion adsorption. The ζ-potential lowered the membrane permeability, especially for membranes with a pore radius lower than 3 nm, a ζ-potential higher than 20 mV, and an ionic strength lower than 0.01 m. The rejection model showed that, for a pore radius lower than 3 nm and for solutions with ionic strengths lower than 0.01 m, there is an optimum ζ-potential for rejection, because of the concurrent effects of electromigration and convection. Hence, the model can be used as a prediction tool to optimize membrane perm-selectivity by designing a specific pore size and surface charge for application at specific ionic strengths and pH levels. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  11. Morphological evolution of porous nanostructures grown from a single isolated anodic alumina nanochannel

    Science.gov (United States)

    Chen, Shih-Yung; Chang, Hsuan-Hao; Lai, Ming-Yu; Liu, Chih-Yi; Wang, Yuh-Lin

    2011-09-01

    Porous anodic aluminum oxide (AAO) membranes have been widely used as templates for growing nanomaterials because of their ordered nanochannel arrays with high aspect ratio and uniform pore diameter. However, the intrinsic growth behavior of an individual AAO nanochannel has never been carefully studied for the lack of a means to fabricate a single isolated anodic alumina nanochannel (SIAAN). In this study, we develop a lithographic method for fabricating a SIAAN, which grows into a porous hemispherical structure with its pores exhibiting fascinating morphological evolution during anodization. We also discover that the mechanical stress affects the growth rate and pore morphology of AAO porous structures. This study helps reveal the growth mechanism of arrayed AAO nanochannels grown on a flat aluminum surface and provides insights to help pave the way to altering the geometry of nanochannels on AAO templates for the fabrication of advanced nanocomposite materials.

  12. Morphological evolution of porous nanostructures grown from a single isolated anodic alumina nanochannel

    International Nuclear Information System (INIS)

    Chen, Shih-Yung; Wang, Yuh-Lin; Chang, Hsuan-Hao; Lai, Ming-Yu; Liu, Chih-Yi

    2011-01-01

    Porous anodic aluminum oxide (AAO) membranes have been widely used as templates for growing nanomaterials because of their ordered nanochannel arrays with high aspect ratio and uniform pore diameter. However, the intrinsic growth behavior of an individual AAO nanochannel has never been carefully studied for the lack of a means to fabricate a single isolated anodic alumina nanochannel (SIAAN). In this study, we develop a lithographic method for fabricating a SIAAN, which grows into a porous hemispherical structure with its pores exhibiting fascinating morphological evolution during anodization. We also discover that the mechanical stress affects the growth rate and pore morphology of AAO porous structures. This study helps reveal the growth mechanism of arrayed AAO nanochannels grown on a flat aluminum surface and provides insights to help pave the way to altering the geometry of nanochannels on AAO templates for the fabrication of advanced nanocomposite materials.

  13. Gamma astronomy

    International Nuclear Information System (INIS)

    Cesarsky, C.; Cesarsky, J.P.

    1986-01-01

    This article overviews the gamma astronomy research. Sources already observed, and what causes to give to them; the galactic radiation and its interpretation; techniques already used and current projects [fr

  14. Gamma Spectroscopy

    NARCIS (Netherlands)

    Niemantsverdriet, J.W.; Butz, Tilman; Ertl, G.; Knözinger, H.; Schüth, F.

    2008-01-01

    No abstract. The sections in this article are 1 Introduction 2 Mössbauer Spectroscopy 3 Time-Differential Perturbed Angular Correlations (TDPAC) 4 Conclusions and Outlook Keywords: Mössbauer spectroscopy; gamma spectroscopy; perturbed angular correlation; TDPAC

  15. Energy transfer in porous anodic alumina/rhodamine 110 nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Elhouichet, H., E-mail: habib.elhouichet@fst.rnu.tn [Laboratoire de Physico-Chimie des Materiaux Mineraux et leurs Applications, Centre National de Recherches en Sciences des Materiaux, B.P. 95, Hammam-Lif 2050 (Tunisia); Departement de Physique, Faculte des Sciences de Tunis, University of Tunis Elmanar 2092 Tunis (Tunisia); Harima, N.; Koyama, H. [Hyogo University of Teacher Education, Kato, Hyogo 673-1494 (Japan); Gaponenko, N.V. [Belarusian State University of Informatics and Radioelectronics, P. Browki St. 6, 220013 Minsk (Belarus)

    2012-09-15

    We have used porous anodic alumina (PAA) films as templates for embedding rhodamine 110 (Rh110) molecules and examined their photoluminescence (PL) properties in detail. The analysis of the polarization memory (PM) of PL strongly suggests that there is a significant energy transfer from PAA to Rh110 molecules. The effect of annealing the PAA layer on the PL properties of the nanocomposite has been studied. The results show that the energy transfer becomes more efficient in annealed PAA. - Highlights: Black-Right-Pointing-Pointer Porous anodic alumina-rhodamine 110 nanocomposites are elaborated. Black-Right-Pointing-Pointer Efficient energy transfer from the host to Rh110 molecules is evidenced from measurements of photoluminescence and degree of polarization memory spectra. Black-Right-Pointing-Pointer Thermal annealing of porous anodic alumina can improve the process of excitation transfer.

  16. Thermal and Electrical Characterization of Alumina Substrate for Microelectronic Applications

    International Nuclear Information System (INIS)

    Ahmad, S.; Ibrahim, A.; Alias, R.; Shapee, S. M.; Ambak, Z.; Zakaria, S. Z.; Yahya, M. R.; Mat, A. F. A.

    2010-01-01

    This paper reports the effect of sintering temperature on thermal and electrical properties of alumina material as substrate for microelectronic devices. Alumina materials in the form of green sheet with 1 mm thickness were sintered at 1100 deg. C, 1300 deg. C and 1500 deg. C for about 20 hours using heating and cooling rates of 2 deg. C/min. The densities were measured using densitometer and the microstructures of the samples were analyzed using SEM micrographs. Meanwhile thermal and electrical properties of the samples were measured using flash method and impedance analyzer respectively. It was found that thermal conductivity and thermal diffusivity of the substrate increases as sintering temperature increases. It was found also that the dielectric constant of alumina substrate increases as the sintering temperature increases.

  17. Thermal and Electrical Characterization of Alumina Substrate for Microelectronic Applications

    Science.gov (United States)

    Ahmad, S.; Ibrahim, A.; Alias, R.; Shapee, S. M.; Ambak, Z.; Zakaria, S. Z.; Yahya, M. R.; Mat, A. F. A.

    2010-03-01

    This paper reports the effect of sintering temperature on thermal and electrical properties of alumina material as substrate for microelectronic devices. Alumina materials in the form of green sheet with 1 mm thickness were sintered at 1100° C, 1300° C and 1500° C for about 20 hours using heating and cooling rates of 2° C/min. The densities were measured using densitometer and the microstructures of the samples were analyzed using SEM micrographs. Meanwhile thermal and electrical properties of the samples were measured using flash method and impedance analyzer respectively. It was found that thermal conductivity and thermal diffusivity of the substrate increases as sintering temperature increases. It was found also that the dielectric constant of alumina substrate increases as the sintering temperature increases.

  18. Alumina composites for oxide/oxide fibrous monoliths

    International Nuclear Information System (INIS)

    Cruse, T. A.; Polzin, B. J.; Picciolo, J. J.; Singh, D.; Tsaliagos, R. N.; Goretta, K. C.

    2000-01-01

    Most work on ceramic fibrous monoliths (FMs) has focused on the Si 3 N 4 /BN system. In an effort to develop oxidation-resistant FMs, several oxide systems have recently been examined. Zirconia-toughened alumina and alumina/mullite appear to be good candidates for the cell phase of FMs. These composites offer higher strength and toughness than pure alumina and good high-temperature stability. By combining these oxides, possibly with a weaker high-temperature oxide as the cell-boundary phase, it should be possible to product a strong, resilient FM that exhibits graceful failure. Several material combinations have been examined. Results on FM fabrication and microstructural development are presented

  19. Retrospective dosimetry with alumina substrate from electronic components

    International Nuclear Information System (INIS)

    Ekendahl, D.; Judas, L.

    2012-01-01

    Alumina substrate can be found in electronic components used in portable electronic devices. The material is radiation sensitive and can be applied in dosimetry using thermally or optically stimulated luminescence. Electronic portable devices such as mobile phones, USB flash discs, mp3 players, etc., which are worn close to the body, can represent personal dosemeters for members of the general public in situations of large-scale radiation accidents or malevolent acts with radioactive materials. This study investigated dosimetric properties of alumina substrates and aspects of using mobile phones as personal dosemeters. The alumina substrates exhibited favourable dosimetry characteristics. However, anomalous fading had to be properly corrected in order to achieve sufficient precision in dose estimate. Trial dose reconstruction performed by means of two mobile phones proved that mobile phones can be used for reconstruction of personal doses. (authors)

  20. Conductivity variations in composites of. alpha. -zirconium phosphate and alumina

    Energy Technology Data Exchange (ETDEWEB)

    Slade, R.C.T.; Knowles, J.A. (Dept. of Chemistry, Exeter Univ. (UK))

    Composite proton-conducting solid electrolytes have been formed from {alpha}-zirconium hydrogen phosphate ({alpha}-Zr(HPO{sub 4}){sub 2}.H{sub 2}O, {alpha}-ZrP) and aluminas (Al{sub 2}O{sub 3}) in varying mole ratios. Conductivity variations as a function of temperature have been characterised and compared to that for a delaminated {alpha}-ZrP (no alumina). There are no appreciable conductivity enhancements on composite formation, but conductivity for materials ca. 50 mole% in alumina can be comparable to the delaminated materials. Differential scanning calorimetry shows the composites to have different thermal properties to simple admixtures. High resolution {sup 31}P NMR studies show reaction to form aluminium phosphate at the interface between components. (orig.).

  1. Radiation silver paramagnetic centers in a beta-alumina crystal

    International Nuclear Information System (INIS)

    Badalyan, A.G.; Zhitnikov, R.A.

    1985-01-01

    Silver paramagnetic centers in a β-alumina crystal, formed after X-ray radiation at 77 K, are investigated by the EPR method. Silver enters the β-alumina crystal, substituting sodium and potassium ions in a mirror plane. Crystals with substitution from 0.1 to 100% of alkali metal ions by Ag + ions are investigated. Silver atomic centers (Ag 0 -centers), formed by electron capture with the Ag + ion, are firstly detected and investigated in the β-alumina. Hole Ag 2+ -centers are investigated and detected in crystals with high concentration of Ag + . By studying the orientation dependence of a g-factor it is established that hole capture by the Ag + ion is accompanied by Ag 2+ ion displacement from the position, Ag + being primarity taken up (Beavers-Roth or anti- Beavers-Roth) to the position between two oxygen ions in the mirror plane

  2. Pressureless sintering behavior of injection molded alumina ceramics

    Directory of Open Access Journals (Sweden)

    Liu W.

    2014-01-01

    Full Text Available The pressureless sintering behaviors of two widely used submicron alumina (MgOdoped and undoped with different solid loadings produced by injection molding have been studied systematically. Regardless of the sinterability of different powders depending on their inherent properties, solid loading plays a critical role on the sintering behavior of injection molded alumina, which greatly determines the densification and grain size, and leads to its full densification at low temperatures. As compared to the MgO-doped alumina powder, the undoped specimens exhibit a higher sinterability for its smaller particle size and larger surface area. While full densification could be achieved for MgO-doped powders with only a lower solid loading, due to the fact that MgO addition can reduce the detrimental effect of the large pore space on the pore-boundary separation.

  3. Synthesis of alumina powders by precipitation method and solvothermal treatment

    International Nuclear Information System (INIS)

    Politchuk, J.O.; Lima, N.B.; Lazar, D.R.R.; Ussui, V.; Yoshito, W.K.

    2012-01-01

    The improvement of alumina powders synthesis processes has been focused on the preparation of ceramic powders with well defined crystalline structure and with high specific surface area and nanometric particle size without formation of hard agglomerates. For this purpose the precipitation step should be studied and and also the temperature of alumina crystallization should be reduced. The aim of this study was to obtain alumina powders by hydroxide precipitation with ammonia in the presence of cationic surfactant, followed by solvothermal treatment and calcination. The powders were characterized by TG/DTA, X-ray diffraction, surface area measurements by gas adsorption (BET) and scanning electron microscopy. The results showed that powders produced by solvothermal treatment without surfactant have higher crystallinity. However the presence of CTAB enhances 240% the specific surface area compared with powders produced without this reagent (author)

  4. High field 27Al MAS NMR and TPD studies of active sites in ethanol dehydration using thermally treated transitional aluminas as catalysts

    Energy Technology Data Exchange (ETDEWEB)

    Hu, Jian Zhi; Xu, Suochang; Kwak, Ja Hun; Hu, Mary Y.; Wan, Chuan; Zhao, Zhenchao; Szanyi, Janos; Bao, Xinhe; Han, Xiuwen; Wang, Yong; Peden, Charles H. F.

    2016-04-01

    Gamma-, sigma- and theta-Al2O3 are well known metastable “transitional” alumina structural polymorphs. Upon heating, Al2O3 transitions to the so-called and Al2O3 polymorphs and finally forms the thermally stable Al2O3. The poorly developed crystallinity and co-existence of the , , and Al2O3 prior to forming all Al2O3, making it difficult to characterize the structures as well as to quantify the various phases of the transition alumina. As a result, there are significant controversies in the literatures. In this work, a detailed NMR analysis was carried out at high magnetic field on three special aluminum oxide samples where the, , , Al2O3 phases are made dominant, respectively, by controlling the synthesis conditions. The goal is to simplify, including making unambiguous, spectral assignments in 27Al MAS NMR spectra of transition alumina that have not yet been commonly agreed previously. Specifically, quantitative 1D 27Al MAS NMR was used to quantify the ratios of the different alumina structural units, 2D MQMAS 27Al MAS was used for obtaining the highest spectral resolution to guide the analysis of the 1D spectrum, and a saturation pulse sequence was integrated into the 1D NMR to select the amorphous structures, including obtain spectra where the penta-coordinate sites are observed with enhanced relative intensity. Collectively, this study uniquely assigns Al-peaks (both octahedral and tetrahedral) to the Al2O3 and the Al2O3 phases and offers a new way of understanding, including quantifying, the different structural units and sites in transition alumina samples.

  5. Cylindrical Three-Dimensional Porous Anodic Alumina Networks

    Directory of Open Access Journals (Sweden)

    Pedro M. Resende

    2016-11-01

    Full Text Available The synthesis of a conformal three-dimensional nanostructure based on porous anodic alumina with transversal nanopores on wires is herein presented. The resulting three-dimensional network exhibits the same nanostructure as that obtained on planar geometries, but with a macroscopic cylindrical geometry. The morphological analysis of the nanostructure revealed the effects of the initial defects on the aluminum surface and the mechanical strains on the integrity of the three-dimensional network. The results evidence the feasibility of obtaining 3D porous anodic alumina on non-planar aluminum substrates.

  6. Fabrication of Anodic Porous Alumina by Squaric Acid Anodizing

    OpenAIRE

    Kikuchi, Tatsuya; Yamamoto, Tsuyoshi; Natsui, Shungo; Suzuki, Ryosuke O.

    2014-01-01

    The growth behavior of anodic porous alumina formed via anodizing in a new electrolyte, squaric acid (3,4-dihydroxy-3-cyclobutene-1,2-dione), is reported for the first time. A high-purity aluminum foil was anodized in a 0.1 M squaric acid solution at 293 K and a constant applied potential of 100-150 V. Anodic oxides grew on the aluminum foil at applied potentials of 100-120 V, but a burned oxide film was formed at higher voltage. Anodic porous alumina with a cell size of approximately 200-400...

  7. Behaviour modelling of two aluminas in divergent spherical pyrotechnical experiments

    International Nuclear Information System (INIS)

    Malaise, F.; Tranchet, J.Y.; Collombet, F.

    1997-01-01

    Two pure aluminas of different characteristics have been subjected to the propagation of a longitudinal divergent spherical shock wave through pyrotechnical experiments. An approach combining a phenomenological analysis and numerical 1D-calculations is proposed to study the behaviour of these aluminas submitted to that type of wave loading. The modelling, proposed in a previous paper, is refined and gives satisfying experimentation-calculation correlations. An analysis of the influence exerted by the various encountered phenomena (plastic activity, pore closure, microcracking) is performed. The significant consequence of the activation of damage with an extension criterion is also underlined. (orig.)

  8. Comparative study on sintered alumina for ballistic shielding application

    International Nuclear Information System (INIS)

    Melo, Francisco Cristovao Lourenco de; Goncalves, Diniz Pereira

    1997-01-01

    This work presents a development of the armor made from special ceramic materials and kevlar. An experimental investigation was conducted to study the ballistic penetration resistance on three samples taken from sintered alumina: a commercial one and two formulations A and B made in IAE/CTA. The main differences between the two formulations was the grain size and bend resistance. The knowledge of the mechanisms during the penetration and perforation process allowed to apply a ductile composite laminate made form kevlar under the alumina to delay its rupture. The last ballistic test showed how a Weibull's modulii and other mechanical properties are able to improve ballistic penetration resistance. (author)

  9. Membrane fusion

    DEFF Research Database (Denmark)

    Bendix, Pól Martin

    2015-01-01

    At Stanford University, Boxer lab, I worked on membrane fusion of small unilamellar lipid vesicles to flat membranes tethered to glass surfaces. This geometry closely resembles biological systems in which liposomes fuse to plasma membranes. The fusion mechanism was studied using DNA zippering...... between complementary strands linked to the two apposing membranes closely mimicking the zippering mechanism of SNARE fusion complexes....

  10. Sterilization of heparinized cuprophan hemodialysis membranes

    NARCIS (Netherlands)

    ten Hoopen, Hermina W.M.; Hinrichs, W.L.J.; Hinrichs, W.L.J.; Engbers, G.H.M.; Feijen, Jan

    1996-01-01

    The effects of sterilization of dry heparinized Cuprophan hemodialysis membranes by means of ethylene oxide (EtO) exposure, gamma irradiation, or steam on the anticoagulant activity and chemical characteristics of immobilized heparin and the permeability of the membrane were investigated.

  11. Gamma camera

    International Nuclear Information System (INIS)

    Berninger, W.H.

    1975-01-01

    The light pulse output of a scintillator, on which incident collimated gamma rays impinge, is detected by an array of photoelectric tubes each having a convexly curved photocathode disposed in close proximity to the scintillator. Electronic circuitry connected to outputs of the phototubes develops the scintillation event position coordinate electrical signals with good linearity and with substantial independence of the spacing between the scintillator and photocathodes so that the phototubes can be positioned as close to the scintillator as is possible to obtain less distortion in the field of view and improved spatial resolution as compared to conventional planar photocathode gamma cameras

  12. HDS, HDN and HDA activities of nickel-molybdenum catalysts supported on alumina

    Energy Technology Data Exchange (ETDEWEB)

    Dominguez-Crespo, M.A. [Instituto Mexicano del Petroleo, Programa de Tratamiento de Crudo Maya. Avenida Eje Central Lazaro Cardenas No.152, Col. San Bartolo Atepehuacan, 07730, Mexico D. F. (Mexico); Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada (CICATA-Altamira, IPN) Km 14.5 Carretera Tampico-puerto Industrial 89600, Altamira, Tamaulipas (Mexico); Torres-Huerta, A.M.; Ramirez-Meneses, E. [Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada (CICATA-Altamira, IPN) Km 14.5 Carretera Tampico-puerto Industrial 89600, Altamira, Tamaulipas (Mexico); Diaz-Garcia, L. [Instituto Mexicano del Petroleo, Programa de Tratamiento de Crudo Maya. Avenida Eje Central Lazaro Cardenas No.152, Col. San Bartolo Atepehuacan, 07730, Mexico D. F. (Mexico); Arce-Estrada, E.M. [Instituto Politecnico Nacional, Departamento de Metalurgia y Materiales. A.P. 75-876, 07300 Mexico, D. F. (Mexico)

    2008-08-15

    In this work, NiMo-Al{sub 2}O{sub 3} catalysts were prepared by using different alumina precursors. The supports were impregnated by means of the spray at incipient wetness technique in both basic and acid media. Both the supports and fresh catalysts were characterized by the adsorption-desorption isotherms, Temperature-Programmed Reduction (TPR), Thermal Pyridine Adsorption-Desorption (TPD) and X-Ray Diffraction analyses (XRD). After sulfidation, the NiMoS metallic particles were characterized by Transmission Electron Microscopy (TEM). The initial analyses were performed in a trickle-bed reactor by using a real feedstock (Mexican heavy gas oil) and performing hydrotreating reactions (HDS, HDN and HDA) at three different temperatures: 613, 633 and 653 K; and 54 kg cm{sup -} {sup 2}. The catalytic activities are discussed in relation to the physicochemical properties of the NiMo catalysts, alumina phase and pH of the impregnating solution. The catalytic results show an increase in the conversion profiles with temperature. The sulfur conversion was increased from 89 to 99.25%, 91-99%, 90.8-97%, 83-95% and 78-96% when the crystal size of the support varied from 3 to 20 nm, respectively. The nitrogen and aromatic conversions were also increased in the range of 23-45 wt.%. It was found that the {gamma} phase reached a higher catalytic performance than the {eta} phase. The NiMo catalysts synthesized in a basic medium showed a better catalytic performance than that obtained with those prepared in acid solutions. The significance of the kinetic data to compare the catalysts is discussed. The maximum value of the catalytic activity was reached with the catalysts with the smallest particle sizes. (author)

  13. FAS grafted superhydrophobic ceramic membrane

    Energy Technology Data Exchange (ETDEWEB)

    Lu Jun [School of Material Science and Engineering, Jingdezhen Ceramic Institute, 333001 Jingdezhen (China); Key Laboratory of Inorganic Coating Materials, Shanghai Institute of Ceramics, CAS, 1295 DingXi Road, Shanghai 200050 (China); Yu Yun, E-mail: yunyush@mail.sic.ac.cn [Key Laboratory of Inorganic Coating Materials, Shanghai Institute of Ceramics, CAS, 1295 DingXi Road, Shanghai 200050 (China); Zhou Jianer [School of Material Science and Engineering, Jingdezhen Ceramic Institute, 333001 Jingdezhen (China); Song Lixin; Hu Xingfang [Key Laboratory of Inorganic Coating Materials, Shanghai Institute of Ceramics, CAS, 1295 DingXi Road, Shanghai 200050 (China); Larbot, Andre [Institut Europeen des Membranes, UMR 5635-CNRS, ENSCM, UMII, 1919 Route de Mende 34293, Montpellier Cedex 5 (France)

    2009-08-30

    The hydrophobic properties of {gamma}-Al{sub 2}O{sub 3} membrane have been obtained by grafting fluoroalkylsilane (FAS) on the surface of the membrane. The following grafting parameters were studied: the eroding time of the original membrane, the grafting time, the concentration of FAS solution and the multiplicity of grafting. Hydrophobicity of the membranes was characterized by contact angle (CA) measurement. The thermogravimetric analysis (TGA) was used to investigate the weight loss process (25-800 deg. C) of the fluoroalkylsilane grafted on Al{sub 2}O{sub 3} powders under different grafting conditions. The morphologies of the membranes modified under different parameters were examined by field emission scanning electron microscopy (FE-SEM) and the surface roughness (Ra) was measured using white light interferometers. A needle-like structure was observed on the membrane surface after modification, which causes the change of Ra. On the results above, we speculated a model to describe the reaction between FAS and {gamma}-Al{sub 2}O{sub 3} membrane surface as well as the formed surface morphology.

  14. Development of silica RO membranes

    International Nuclear Information System (INIS)

    Ikeda, Ayumi; Kawamoto, Takashi; Matsuyama, Emi; Utsumi, Keisuke; Nomura, Mikihiro; Sugimoto, Masaki; Yoshikawa, Masato

    2012-01-01

    Silica based membranes have been developed by using a counter diffusion CVD method. Effects of alkyl groups in the silica precursors and deposition temperatures had investigated in order to control pore sizes of the silica membranes. In this study, this type of a silica membrane was applied for RO separation. Effects of silica sources, deposition temperatures and post treatments had been investigated. Tetramethoxysilane (TMOS), Ethyltrimethoxysilane (ETMOS) and Phenyltrimethoxysilane (PhTMOS) were used as silica precursors. A counter diffusion CVD method was carried out for 90 min at 270 - 600degC on γ-alumina capillary substrates (effective length: 50 mm, φ: 4 nm: NOK Co.). O 3 or O 2 was introduced into the inside of the substrate at the O 2 rate of 0.2 L min -1 . Ion beam irradiation was carried out for a post treatment using Os at 490 MeV for 1.0 x 10 10 ions cm -2 or 3.0 x 10 10 ions cm -2 . Single gas permeance was measured by using H 2 , N 2 and SF 6 . RO tests were employed at 3.0 or 5.4 MPa for 100 mg L -1 of feed NaCl solution. First, effects of the silica sources were investigated. The total fluxes increased by increasing N 2 permeance through the silica membrane deposited by ETMOS. The maximum NaCl rejection was 28.2% at 12.2 kg m -2 h -1 of the total flux through the membrane deposited at 270degC. N 2 permeance was 9.6 x 10 -9 mol m -2 s -1 Pa -1 . While, total fluxes through the membrane deposited by using PhTMOS were smaller than those through the ETMOS membranes. The phenyl groups for the PhTMOS membrane must be important for the hydrophobic properties through the membrane. Next, effects of ion beam irradiation were tested for the TMOS membranes. Water is difficult to permeate through the TMOS membranes due to the low N 2 permeance through the membrane (3.1 x 10 -11 mol m -2 s -1 Pa -1 ). N 2 permeance increased to 7.3 x 10 -9 mol m -2 s -1 Pa -1 by the irradiation. Irradiation amounts had little effects on N 2 permeance. However, NaCl rejections

  15. Contact angle studies on anodic porous alumina.

    Science.gov (United States)

    Redón, Rocío; Vázquez-Olmos, A; Mata-Zamora, M E; Ordóñez-Medrano, A; Rivera-Torres, F; Saniger, J M

    2005-07-15

    The preparation of nanostructures using porous anodic aluminum oxide (AAO) as templates involves the introduction of dissolved materials into the pores of the membranes; one way to determine which materials are preferred to fill the pores involves the measurement of the contact angles (theta) of different solvents or test liquids on the AAOs. Thus, we present measurements of contact angles of nine solvents on four different AAO sheets by tensiometric and goniometric methods. From the solvents tested, we found dimethyl sulfoxide (DMSO) and N,N(')-dimethylformamide (DMF) to interact with the AAOs, the polarity of the solvents and the surfaces being the driving force.

  16. High-frequency characteristics of glass/ceramic composite and alumina multilayer structures

    International Nuclear Information System (INIS)

    Niwa, K.; Suzuki, H.; Yokoyama, H.; Kamechara, N.; Tsubone, K.; Tanisawa, H.; Sugiki, H.

    1990-01-01

    This paper reports the transmission characteristics of glass/ceramic composite (borosilicate glass/alumina) and alumina multilayer structures examined. The triplate stripline formed in the glass/ceramic multilayer shows low conductor and dielectric loss. Alumina multilayer, however, has twice the transmission loss at 10 GHz, because the resistivity of W in the alumina multilayer is higher than the Cu in the glass/ceramic multilayer. Crosstalk between striplines in the glass/ceramics is less than -80 dB up to 11 GHz and 9 GHz for alumina

  17. Microwave-assisted brazing of alumina ceramics for electron tube ...

    Indian Academy of Sciences (India)

    Vickers microhardness measurement indicated reliable joint performance for the microwave-assisted brazed joints during ... Alumina ceramics are used in wide range of applications due to their .... temperature were recorded by DAQSOFT software in a sep- .... Tubes: Design and Development Capabilities (MTDDC)',.

  18. State of the art: alumina ceramics for energy applications

    International Nuclear Information System (INIS)

    Hauth, W.E.; Stoddard, S.D.

    1978-01-01

    Prominent ceramic raw materials and products manufacturers were surveyed to determine the state of the art for alumina ceramic fabrication. This survey emphasized current capabilities and limitations for fabrication of large, high-density, high-purity, complex shapes. Some directions are suggested for future needs and development

  19. Multifunctional substrates of thin porous alumina for cell biosensors

    KAUST Repository

    Toccafondi, Chiara; Thorat, Sanjay B.; La Rocca, Rosanna; Scarpellini, Alice; Salerno, Marco; Dante, Silvia; Das, Gobind

    2014-01-01

    We have fabricated anodic porous alumina from thin films (100/500 nm) of aluminium deposited on technological substrates of silicon/glass, and investigated the feasibility of this material as a surface for the development of analytical biosensors aiming to assess the status of living cells. To this goal, porous alumina surfaces with fixed pitch and variable pore size were analyzed for various functionalities. Gold coated (about 25 nm) alumina revealed surface enhanced Raman scattering increasing with the decrease in wall thickness, with factor up to values of approximately 104 with respect to the flat gold surface. Bare porous alumina was employed for micro-patterning and observation via fluorescence images of dye molecules, which demonstrated the surface capability for a drug-loading device. NIH-3T3 fibroblast cells were cultured in vitro and examined after 2 days since seeding, and no significant (P > 0.05) differences in their proliferation were observed on porous and non-porous materials. The effect on cell cultures of pore size in the range of 50–130 nm—with pore pitch of about 250 nm—showed no significant differences in cell viability and similar levels in all cases as on a control substrate. Future work will address combination of all above capabilities into a single device.

  20. Grafting of alumina on SBA-15: Effect of surface roughness

    Czech Academy of Sciences Publication Activity Database

    Zukal, Arnošt; Šiklová, Helena; Čejka, Jiří

    2008-01-01

    Roč. 24, č. 17 (2008), s. 9837-9842 ISSN 0743-7463 R&D Projects: GA AV ČR KAN100400701 Institutional research plan: CEZ:AV0Z40400503 Keywords : alumina-grafted materials * SBA-15 * Nitrogen adsorption Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 4.097, year: 2008

  1. Macroporous silica–alumina composites with mesoporous walls

    Indian Academy of Sciences (India)

    Macroporous silica–alumina composites with mesopores have been prepared by employing polymethylmethacrylate beads as templates in the presence of the cationic surfactant, N-cetyl-N,N,N-trimethylammonium bromide. The Si/Al ratio in the composites has been varied between 4.5 and 48 and the occurrence of ...

  2. Improving subcritical crack growth resistance for alumina glass dental composite

    NARCIS (Netherlands)

    Zhu, Q.; With, de G.

    2005-01-01

    The improvement of subcritical crack growth (SCG) resistance for alumina glass dental composites was explored in this study. The addition of nitrogen to the glass phases in the composite was found to increase the SCG resistance, where the SCG exponent n increases from 22 for the oxide glass

  3. Electrochemical impedance spectroscopy of nanoporous anodic alumina template

    International Nuclear Information System (INIS)

    Shahzad, K.

    2010-01-01

    Room temperature EIS characterization of nanoporous anodic alumina prepared at 40 V and 60 V has been done in 0.3 M oxalic acid solution. Rapid decrease in impedance was observed for the template prepared at 40 V. EIS study of porous anodic alumina template prepared in 0.3 M oxalic acid has been done in different electrolytes. Templates prepared in 0.3 M sulfuric acid solution were also characterized for comparison. Rapid decrease in the thickness of nonporous anodic film was observed with an increase of aggressiveness of electrolyte. Temperature based systematic study of EIS measurement has been done for porous anodic alumina template at different temperatures. Formation of micropores was observed in the nanoporous anodic alumina film formed on aluminum in 0.3 M oxalic acid solution which accelerates the dissolution rate with increase of measurement temperature. In addition to these, electropolishing behavior of pure aluminum has also been studied in different electrolytes and it was observed that electropolishing conditions prior to anodization are extremely important. (author)

  4. Indentation fatigue in silicon nitride, alumina and silicon carbide ...

    Indian Academy of Sciences (India)

    Unknown

    carbide ceramics. A K MUKHOPADHYAY. Central Glass and Ceramic Research Institute, Kolkata 700 032, India. Abstract. Repeated indentation fatigue (RIF) experiments conducted on the same spot of different structural ceramics viz. a hot pressed silicon nitride (HPSN), sintered alumina of two different grain sizes viz.

  5. Synthesis and characterization of hydroxyapatite/alumina ceramic ...

    Indian Academy of Sciences (India)

    39

    In the present work, nano crystalline hydroxyapatite/alumina (HAp-Al2O3) composite was .... powder was dried in hot air oven at 80 °C for 24 hours. ... weekly, and the culture medium was changed twice in a week. 4. Results and Discussion.

  6. Dielectric properties of carbon nanofibre/alumina composites

    Czech Academy of Sciences Publication Activity Database

    Fernandez-Garcia, L.; Suarez, M.; Menéndez, J.L.; Pecharromán, C.; Nuzhnyy, Dmitry; Bovtun, Viktor; Savinov, Maxim; Kempa, Martin; Petzelt, Jan

    2013-01-01

    Roč. 57, JUN (2013), s. 380-387 ISSN 0008-6223 R&D Projects: GA ČR GAP204/12/0232; GA MŠk LD12025 Institutional support: RVO:68378271 Keywords : alumina * carbon nanofibre * dielectric and THz spectroscopy * infrared spectroscopy * percolation threshold Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 6.160, year: 2013

  7. Capillary condensation in porous alumina observed by positronium lifetime spectroscopy

    International Nuclear Information System (INIS)

    Ivanov, Eugeniu; Vata, Ion; Toderian, Stefan; Dudu, Dorin; Rusen, Ion; Stefan, Nitisor

    2008-01-01

    The PALS method based on time distribution measurements has been used to study capillary condensation of different gases adsorbed in microporous alumina powder. The isotherms exhibit features which are associated with a shifted gas-liquid transition. The sorption and desorption processes are irreversible presenting a hysteresis effect. Suggestions on some new aspects of the capillary condensation dynamics are made

  8. Multifunctional substrates of thin porous alumina for cell biosensors

    KAUST Repository

    Toccafondi, Chiara

    2014-02-27

    We have fabricated anodic porous alumina from thin films (100/500 nm) of aluminium deposited on technological substrates of silicon/glass, and investigated the feasibility of this material as a surface for the development of analytical biosensors aiming to assess the status of living cells. To this goal, porous alumina surfaces with fixed pitch and variable pore size were analyzed for various functionalities. Gold coated (about 25 nm) alumina revealed surface enhanced Raman scattering increasing with the decrease in wall thickness, with factor up to values of approximately 104 with respect to the flat gold surface. Bare porous alumina was employed for micro-patterning and observation via fluorescence images of dye molecules, which demonstrated the surface capability for a drug-loading device. NIH-3T3 fibroblast cells were cultured in vitro and examined after 2 days since seeding, and no significant (P > 0.05) differences in their proliferation were observed on porous and non-porous materials. The effect on cell cultures of pore size in the range of 50–130 nm—with pore pitch of about 250 nm—showed no significant differences in cell viability and similar levels in all cases as on a control substrate. Future work will address combination of all above capabilities into a single device.

  9. Indentation fatigue in silicon nitride, alumina and silicon carbide ...

    Indian Academy of Sciences (India)

    Repeated indentation fatigue (RIF) experiments conducted on the same spot of different structural ceramics viz. a hot pressed silicon nitride (HPSN), sintered alumina of two different grain sizes viz. 1 m and 25 m, and a sintered silicon carbide (SSiC) are reported. The RIF experiments were conducted using a Vicker's ...

  10. Fabrication of an alumina torus for thermonuclear fusion containment

    International Nuclear Information System (INIS)

    Hauth, W.E.; Blake, R.D.; Dickinson, J.M.; Rutz, H.L.; Stoddard, S.D.

    1978-05-01

    A 235-cm-diam torus has been fabricated for plasma containment during thermonuclear fusion experiments. This 30-cm-diam torus consists of sixty 99.5%-alumina segments, 80% of which are assembled by forming vacuum-tight ceramic-to-ceramic seals. Selection of sealing materials and techniques are discussed

  11. Synthesis and textural evolution of alumina particles with mesoporous structures

    International Nuclear Information System (INIS)

    Liu Xun; Peng Tianyou; Yao Jinchun; Lv Hongjin; Huang Cheng

    2010-01-01

    Alumina particles with mesostructures were synthesized through a chemical precipitation method by using different inorganic aluminum salts followed by a heterogeneous azeotropic distillation and calcination process. The obtained mesoporous γ-alumina particles were systematically characterized by the X-ray diffraction, transmission electron microscopy and nitrogen adsorption-desorption measurement. Effects of the aluminum salt counter anion, pH value and the azeotropic distillation process on the structural or textural evolution of alumina particles were investigated. It is found that Cl - in the reaction solution can restrain the textural evolution of the resultant precipitates into two-dimensional crystallized pseudoboehmite lamellae during the heterogeneous azeotropic distillation, and then transformed into γ-Al 2 O 3 particles with mesostructures after further calcination at 1173 K, whereas coexisting SO 4 2- can promote above morphology evolution and then transformed into γ-Al 2 O 3 nanofibers after calcination at 1173 K. Moreover nearly all materials retain relatively high specific surface areas larger than 100 m 2 g -1 even after calcinations at 1173 K. - Graphical abstract: Co-existing Cl - is beneficial for the formation of γ-alumina nanoparticles with mesostructures during the precipitation process. Interparticle and intraparticle mesopores can be derived from acidic solution and near neutral solution, respectively.

  12. Controlled growth of single nanowires within a supported alumina template

    DEFF Research Database (Denmark)

    Vlad, A.; Mátéfi-Tempfli, M.; Faniel, S.

    2006-01-01

    A simple technique for fabricating single nanowires with well-defined position is presented. The process implies the use of a silicon nitride mask for selective electrochemical growth of the nanowires in a porous alumina template. We show that this method allows the realization of complex nanowire...

  13. Gamma camera

    International Nuclear Information System (INIS)

    Tschunt, E.; Platz, W.; Baer, Ul; Heinz, L.

    1978-01-01

    A gamma camera has a plurality of exchangeable collimators, one of which is replaceably mounted in the ray inlet opening of the camera, while the others are placed on separate supports. Supports are swingably mounted upon a column one above the other

  14. Gamma camera

    International Nuclear Information System (INIS)

    Schlosser, P.A.; Steidley, J.W.

    1980-01-01

    The design of a collimation system for a gamma camera for use in nuclear medicine is described. When used with a 2-dimensional position sensitive radiation detector, the novel system can produce superior images than conventional cameras. The optimal thickness and positions of the collimators are derived mathematically. (U.K.)

  15. Fc gamma receptor activation induces the tyrosine phosphorylation of both phospholipase C (PLC)-gamma 1 and PLC-gamma 2 in natural killer cells

    OpenAIRE

    1992-01-01

    Crosslinking of the low affinity immunoglobulin G (IgG) Fc receptor (Fc gamma R type III) on natural killer (NK) cells initiates antibody- dependent cellular cytotoxicity. During this process, Fc gamma R stimulation results in the rapid activation of phospholipase C (PLC), which hydrolyzes membrane phosphoinositides, generating inositol-1,4,5- trisphosphate and sn-1,2-diacylglycerol as second messengers. We have recently reported that PLC activation after Fc gamma R stimulation can be inhibit...

  16. Increasing the Performance of Vacuum Membrane Distillation Using Micro-Structured Hydrophobic Aluminum Hollow Fiber Membranes

    Directory of Open Access Journals (Sweden)

    Chia-Chieh Ko

    2017-04-01

    Full Text Available This study develops a micro-structured hydrophobic alumina hollow fiber with a high permeate flux of 60 Lm−2h−1 and salt rejection over 99.9% in a vacuum membrane distillation process. The fiber is fabricated by phase inversion and sintering, and then modified with fluoroalkylsilanes to render it hydrophobic. The influence of the sintering temperature and feeding temperature in membrane distillation (MD on the characteristics of the fiber and MD performance are investigated. The vacuum membrane distillation uses 3.5 wt % NaCl aqueous solution at 70 °C at 0.03 bar. The permeate flux of 60 Lm−2h−1 is the highest, compared with reported data and is higher than that for polymeric hollow fiber membranes.

  17. Application of various types of alumina and nano--alumina sulfuric acid in the synthesis of α-aminonitriles derivatives: comparative study

    Directory of Open Access Journals (Sweden)

    A. Teimouri

    2014-09-01

    Full Text Available An efficient and green protocol for the synthesis of α-aminonitrile derivatives by one-pot reaction of different aldehydes with amines and trimethylsilyl cyanide has been developed using natural alumina, alumina sulfuric acid (ASA, nano-g-alumina, nano-g-alumina sulfuric acid (nano-g-ASA under microwave irradiation and solvent-free conditions. The advantages of methods are short reaction times, high yields, milder conditions and easy work up. The catalysts can be recovered for the subsequent reactions and reused without any appreciable loss of efficiency. DOI: http://dx.doi.org/10.4314/bcse.v28i3.13

  18. Superhydrophilicity of novel anodic alumina nanofibers films and their formation mechanism

    Science.gov (United States)

    Peng, Rong; Yang, Wulin; Fu, Licai; Zhu, Jiajun; Li, Deyi; Zhou, Lingping

    2017-06-01

    A novel anodic alumina nanofibers structure, which is different from the traditional porous anodic structure, has been quickly fabricated via anodizing in a new electrolyte, pyrophosphoric acid. The effects of the solution concentration and the anodizing time on the formation of the anodic alumina nanofibers were analyzed. The results show that the nanostructure of anodic alumina can change to the nanofiber oxide from the porous oxide by increasing the solution concentration. Prolonging the anodizing time is beneficial to obtain alumina nanofibers at high solution concentration. Growth behavior of the alumina nanofibers was also discussed by scanning electron microscopy observations. Owing to the unique hexagonal structure of anodic alumina as well as the preferential chemical dissolution between the porous anodic alumina and the anodic alumina nanotips, the slightly soluble anodic alumina nanotips could form novel alumina nanofibers during anodizing. The results show that the nanofibers-covered aluminum surface exhibits superhydrophilic property, with a near-zero water contact angle. Such alumina nanofibers with superhydrophilic property could be used for various potential applications.

  19. Nanostructural characterization of large-scale porous alumina fabricated via anodizing in arsenic acid solution

    Energy Technology Data Exchange (ETDEWEB)

    Akiya, Shunta; Kikuchi, Tatsuya, E-mail: kiku@eng.hokudai.ac.jp; Natsui, Shungo; Suzuki, Ryosuke O.

    2017-05-01

    Highlights: • Anodic porous alumina was formed in an arsenic acid solution. • Potential difference (voltage) anodizing at 340 V was achieved. • The porous alumina was slightly ordered under the appropriate conditions. • Pore sealing behavior was not observed in boiling distilled water. • The porous alumina exhibits a white photoluminescence emission under UV irradiation. - Abstract: Anodizing of aluminum in an arsenic acid solution is reported for the fabrication of anodic porous alumina. The highest potential difference (voltage) without oxide burning increased as the temperature and the concentration of the arsenic acid solution decreased, and a high anodizing potential difference of 340 V was achieved. An ordered porous alumina with several tens of cells was formed in 0.1–0.5 M arsenic acid solutions at 310–340 V for 20 h. However, the regularity of the porous alumina was not improved via anodizing for 72 h. No pore sealing behavior of the porous alumina was observed upon immersion in boiling distilled water, and it may be due to the formation of an insoluble complex on the oxide surface. The porous alumina consisted of two different layers: a hexagonal alumina layer that contained arsenic from the electrolyte and a pure alumina honeycomb skeleton. The porous alumina exhibited a white photoluminescence emission at approximately 515 nm under UV irradiation at 254 nm.

  20. Dependency of {gamma}-secretase complex activity on the structural integrity of the bilayer

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, Hua, E-mail: hzhou2@lbl.gov [Life Sciences Division, Lawrence Berkeley National Laboratory, University of California, Berkeley, CA 94720 (United States); Zhou, Shuxia; Walian, Peter J.; Jap, Bing K. [Life Sciences Division, Lawrence Berkeley National Laboratory, University of California, Berkeley, CA 94720 (United States)

    2010-11-12

    Research highlights: {yields} Partial solubilization of membranes with CHAPSO can increase {gamma}-secretase activity. {yields} Completely solubilized {gamma}-secretase is inactive. {yields} Purified {gamma}-secretase regains activity after reconstitution into lipid bilayers. {yields} A broad range of detergents can be used to successfully reconstitute {gamma}-secretase. -- Abstract: {gamma}-secretase is a membrane protein complex associated with the production of A{beta} peptides that are pathogenic in Alzheimer's disease. We have characterized the activity of {gamma}-secretase complexes under a variety of detergent solubilization and reconstitution conditions, and the structural state of proteoliposomes by electron microscopy. We found that {gamma}-secretase activity is highly dependent on the physical state or integrity of the membrane bilayer - partial solubilization may increase activity while complete solubilization will abolish it. The activity of well-solubilized {gamma}-secretase can be restored to near native levels when properly reconstituted into a lipid bilayer environment.

  1. Effects of Processing Temperatures of Nickel Plating on Capacitance Density of Alumina Film Capacitor.

    Science.gov (United States)

    Jeong, Myung-Sun; Ju, Byeong-Kwon; Lee, Jeon-Kook

    2015-06-01

    We observed the effects of nickel plating temperatures for controlling the surface morphologies of the deposited nickel layers on the alumina nano-pores. The alumina nano-channels were filled with nickel at various processing temperatures of 60-90 degrees C. The electrical properties of the alumina film capacitors were changed with processing temperatures. The electroless nickel plating (ENP) at 60 degrees C improved the nickel penetration into the alumina nano-channels due to the reduced reaction rate. Nickel layers are uniformly formed on the high aspect ratio alumina pores. Due to the uniform nickel electrode, the capacitance density of the alumina film capacitors is improved by the low leakage current, dissipation factor and equivalent series resistance. Alumina film capacitors made by ENP at 60 degrees C had a high capacitance density of 160 nF/cm2.

  2. Synthesis and structural evaluation of freeze-cast porous alumina

    Energy Technology Data Exchange (ETDEWEB)

    Souza, Douglas F., E-mail: souzadf@outlook.com [Department of Metallurgical and Materials Engineering, Federal University of Minas Gerais — UFMG, Avenida Presidente Antônio Carlos, 6627, Campus UFMG, Belo Horizonte, MG CEP: 31270-901, Escola de Engenharia, bloco 2, sala 2230 (Brazil); Nunes, Eduardo H.M., E-mail: eduardohmn@gmail.com [Department of Metallurgical and Materials Engineering, Federal University of Minas Gerais — UFMG, Avenida Presidente Antônio Carlos, 6627, Campus UFMG, Belo Horizonte, MG CEP: 31270-901, Escola de Engenharia, bloco 2, sala 2230 (Brazil); Pimenta, Daiana S.; Vasconcelos, Daniela C.L. [Department of Metallurgical and Materials Engineering, Federal University of Minas Gerais — UFMG, Avenida Presidente Antônio Carlos, 6627, Campus UFMG, Belo Horizonte, MG CEP: 31270-901, Escola de Engenharia, bloco 2, sala 2230 (Brazil); Nascimento, Jailton F.; Grava, Wilson [Petrobras/CENPES, Avenida Horácio Macedo 950, Cidade Universitária, Ilha do Fundão, Rio de Janeiro, RJ CEP:21941-915 (Brazil); Houmard, Manuel [Department of Materials Engineering and Civil Construction, Federal University of Minas Gerais — UFMG, Avenida Presidente Antônio Carlos, 6627, Campus UFMG, Belo Horizonte, MG CEP: 31270-901, Escola de Engenharia, bloco 1, sala 3304 (Brazil); Vasconcelos, Wander L., E-mail: wlv@demet.ufmg.br [Department of Metallurgical and Materials Engineering, Federal University of Minas Gerais — UFMG, Avenida Presidente Antônio Carlos, 6627, Campus UFMG, Belo Horizonte, MG CEP: 31270-901, Escola de Engenharia, bloco 2, sala 2230 (Brazil)

    2014-10-15

    In this work we fabricated alumina samples by the freeze-casting technique using tert-butanol as the solvent. The prepared materials were examined by scanning electron microscopy and X-ray microtomography. Next, they were coated with sol–gel silica films by dip-coating. Permeability tests were carried out in order to assess the permeation behavior of the materials processed in this study. We observed that the sintering time and alumina loading showed a remarkable effect on both the structural properties and flexural strength of the freeze-cast samples. Nitrogen adsorption tests revealed that the silica prepared in this study exhibited a microporous structure. It was observed that the presence of silica coatings on the alumina surface decreased the CO{sub 2} permeance by about one order of magnitude. Because of the similar kinetic diameters of nitrogen and carbon dioxide, the CO{sub 2}/N{sub 2} system showed a separation efficiency that was lower than that observed for the He/CO{sub 2} and He/N{sub 2} systems. We noticed that increasing the feed pressure improved the separation capacity of the obtained materials. - Highlights: • Porous alumina samples obtained by the freeze-casting technique • Microporous silica coating prepared by a simple sol–gel dip-coating methodology • Samples examined by SEM, μ-CT, and nitrogen sorption tests • Mechanical tests were carried out in the freeze-cast samples. • The presence of silica coatings on the alumina surface decreased the CO{sub 2} permeance.

  3. Optical performance of hybrid porous silicon-porous alumina multilayers

    Science.gov (United States)

    Cencha, L. G.; Antonio Hernández, C.; Forzani, L.; Urteaga, R.; Koropecki, R. R.

    2018-05-01

    In this work, we study the optical response of structures involving porous silicon and porous alumina in a multi-layered hybrid structure. We performed a rational design of the optimal sequence necessary to produce a high transmission and selective filter, with potential applications in chemical and biosensors. The combination of these porous materials can be used to exploit its distinguishing features, i.e., high transparency of alumina and high refractive index of porous silicon. We assembled hybrid microcavities with a central porous alumina layer between two porous silicon Bragg reflectors. In this way, we constructed a Fabry-Perot resonator with high reflectivity and low absorption that improves the quality of the filter compared to a microcavity built only with porous silicon or porous alumina. We explored a simpler design in which one of the Bragg reflectors is replaced by the aluminium that remains bound to the alumina after its fabrication. We theoretically explored the potential of the proposal and its limitations when considering the roughness of the layers. We found that the quality of a microcavity made entirely with porous silicon shows a limit in the visible range due to light absorption. This limitation is overcome in the hybrid scheme, with the roughness of the layers determining the ultimate quality. Q-factors of 220 are experimentally obtained for microcavities supported on aluminium, while Q-factors around 600 are reached for microcavities with double Bragg reflectors, centred at 560 nm. This represents a four-fold increase with respect to the optimal porous silicon microcavity at this wavelength.

  4. Advanced morphological analysis of patterns of thin anodic porous alumina

    Energy Technology Data Exchange (ETDEWEB)

    Toccafondi, C. [Istituto Italiano di Tecnologia, Department of Nanophysics, Via Morego 30, Genova I 16163 (Italy); Istituto Italiano di Tecnologia, Department of Nanostructures, Via Morego 30, Genova I 16163 (Italy); Stępniowski, W.J. [Department of Advanced Materials and Technologies, Faculty of Advanced Technologies and Chemistry, Military University of Technology, 2 Kaliskiego Str., 00-908 Warszawa (Poland); Leoncini, M. [Istituto Italiano di Tecnologia, Department of Nanostructures, Via Morego 30, Genova I 16163 (Italy); Salerno, M., E-mail: marco.salerno@iit.it [Istituto Italiano di Tecnologia, Department of Nanophysics, Via Morego 30, Genova I 16163 (Italy)

    2014-08-15

    Different conditions of fabrication of thin anodic porous alumina on glass substrates have been explored, obtaining two sets of samples with varying pore density and porosity, respectively. The patterns of pores have been imaged by high resolution scanning electron microscopy and analyzed by innovative methods. The regularity ratio has been extracted from radial profiles of the fast Fourier transforms of the images. Additionally, the Minkowski measures have been calculated. It was first observed that the regularity ratio averaged across all directions is properly corrected by the coefficient previously determined in the literature. Furthermore, the angularly averaged regularity ratio for the thin porous alumina made during short single-step anodizations is lower than that of hexagonal patterns of pores as for thick porous alumina from aluminum electropolishing and two-step anodization. Therefore, the regularity ratio represents a reliable measure of pattern order. At the same time, the lower angular spread of the regularity ratio shows that disordered porous alumina is more isotropic. Within each set, when changing either pore density or porosity, both regularity and isotropy remain rather constant, showing consistent fabrication quality of the experimental patterns. Minor deviations are tentatively discussed with the aid of the Minkowski measures, and the slight decrease in both regularity and isotropy for the final data-points of the porosity set is ascribed to excess pore opening and consequent pore merging. - Highlights: • Thin porous alumina is partly self-ordered and pattern analysis is required. • Regularity ratio is often misused: we fix the averaging and consider its spread. • We also apply the mathematical tool of Minkowski measures, new in this field. • Regularity ratio shows pattern isotropy and Minkowski helps in assessment. • General agreement with perfect artificial patterns confirms the good manufacturing.

  5. Membrane contactor/separator for an advanced ozone membrane reactor for treatment of recalcitrant organic pollutants in water

    International Nuclear Information System (INIS)

    Chan, Wai Kit; Jouët, Justine; Heng, Samuel; Yeung, King Lun; Schrotter, Jean-Christophe

    2012-01-01

    An advanced ozone membrane reactor that synergistically combines membrane distributor for ozone gas, membrane contactor for pollutant adsorption and reaction, and membrane separator for clean water production is described. The membrane reactor represents an order of magnitude improvement over traditional semibatch reactor design and is capable of complete conversion of recalcitrant endocrine disrupting compounds (EDCs) in water at less than three minutes residence time. Coating the membrane contactor with alumina and hydrotalcite (Mg/Al=3) adsorbs and traps the organics in the reaction zone resulting in 30% increase of total organic carbon (TOC) removal. Large surface area coating that diffuses surface charges from adsorbed polar organic molecules is preferred as it reduces membrane polarization that is detrimental to separation. - Graphical abstract: Advanced ozone membrane reactor synergistically combines membrane distributor for ozone, membrane contactor for sorption and reaction and membrane separator for clean water production to achieve an order of magnitude enhancement in treatment performance compared to traditional ozone reactor. Highlights: ► Novel reactor using membranes for ozone distributor, reaction contactor and water separator. ► Designed to achieve an order of magnitude enhancement over traditional reactor. ► Al 2 O 3 and hydrotalcite coatings capture and trap pollutants giving additional 30% TOC removal. ► High surface area coating prevents polarization and improves membrane separation and life.

  6. Study on the bound water of several high specific surface-area oxides (beryllia, alumina, silica-alumina)

    International Nuclear Information System (INIS)

    Rouquerol, J.

    1964-11-01

    This study is concerned with the bound water of several oxides (beryllia, alumina, silica-alumina) at different steps of their dehydration (heating temperatures between 150 and 1100 deg. C). The following techniques have been used simultaneously: Thermal analysis (a new method has been developed), nitrogen adsorption (study of the texture), Diborane hydrolysis (qualitative and quantitative analysis of surface water), Infra-red spectrography (in the absorption range of water), Nuclear magnetic resonance (in the resonance range of protons). Thanks to these different techniques, five kinds of bound water have been observed. Attention is called on the great influence of the thermal treatment conditions on the evolution of the products resulting from the decomposition of alumina α-trihydrate Al(OH) 3 and beryllium α-hydroxide, in the course of the dehydration. Moreover, the author emphasizes the peculiar properties of the two kinds of oxides (alumina and beryllia) prepared through a new method of treatment under low pressure and constant speed of decomposition. Such particular features concern mainly texture, bound water, and consequently, also catalytic activity. (author) [fr

  7. EFFECTIVE ELASTIC PROPERTIES OF ALUMINA-ZIRCONIA COMPOSITE CERAMICS - PART 4. TENSILE MODULUS OF POROUS ALUMINA AND ZIRCONIA

    Directory of Open Access Journals (Sweden)

    W. Pabst

    2004-12-01

    Full Text Available In this fourth paper of a series on the effective elastic properties of alumina-zirconia composite ceramics the influence of porosity on the effective tensile modulus of alumina and zirconia ceramics is discussed. The examples investigated are alumina and zirconia ceramics prepared from submicron powders by starch consolidation casting using two different types of starch, potato starch (median size D50 =47.2 µm and corn starch (median size D50 =13.7 µm. The dependence of effective tensile moduli E, on the porosity f, measured for porosities in the ranges of approx. 19-55 vol.% and 10-42 vol.% for alumina and zirconia, respectively, using a resonant frequency technique, was evaluated by fitting with various model relations, including newly developed ones. A detailed comparison of the fitting results suggests the superiority of the new relation E/E0 = (1 - f·(1 - f/fC, developed by the authors (with the tensile modulus of the dense ceramic material E0 and the critical porosity fC, over most other existing fit models. Only for special purposes and well-behaved data sets the recently proposed exponential relation E/E0 = exp [-Bf/(1 - f] and the well-known Phani-Niyogi relation E/E0 = (1 - f/fCN might be preferable.

  8. Alpha alumina exoemissive and thermoluminescent properties. Application to the dosimetry of ionizing radiations in case of accident

    International Nuclear Information System (INIS)

    Alessandri, M.F.

    1989-06-01

    This work consists of two parts. In the first part, a phenomenon of phototransfer in Thermostimulated Exoelectronic Emission (T.S.E.E.) is pointed out. Study of intrinsic T.S.E.E. of alpha alumina exposed to ultraviolet (U.V.) excitation of energy superior to 4 eV shows three T.S.E.E. peaks situated at 240, 325, 535 0 C (heating rate of 2 0 C.s -1 ). The phototransfer phenomenon is then characterized notably by the lowering of the U.V. excitation threshold to 3.5 eV and the increasing of T.S.E.E. response for U.V. energies between 3.5 and 6 eV. Discussion and interpretation of the results obtained are based on the perfect analogy with the phototransfer of Thermoluminescence (T.L.) observed on a similar type of alpha alumina. The second part describes the application of alpha alumina dosimetric properties to accidental irradiation dosimetry and cartography. The material is bound to a textile support to be used for clothes manufacturing for irradiation risking workers. T.S.E.E. and T.L. properties of the selected fabric have been studied. - T.S.E.E. response to a beta irradiation of strontium 90 covers the region [0.01 - 10 Gy], with a dispersion of ± 20%, a non significant thermic fading beyond 72 hours after irradiation and a very important optical fading; - the region in T.L. extends from 0.25 to 10 Gy with X irradiation (45 kV) and from 0.5 to 10 Gy with gamma irradiation of cobalt 60 and caesium 137; the dispersion is ± 20%, the thermic fading is weak and the optical fading is negligible in artificial light or does not vary any more after 5 days of sunlight exposition [fr

  9. Nanoscale Capillary Flows in Alumina: Testing the Limits of Classical Theory.

    Science.gov (United States)

    Lei, Wenwen; McKenzie, David R

    2016-07-21

    Anodic aluminum oxide (AAO) membranes have well-formed cylindrical channels, as small as 10 nm in diameter, in a close packed hexagonal array. The channels in AAO membranes simulate very small leaks that may be present for example in an aluminum oxide device encapsulation. The 10 nm alumina channel is the smallest that has been studied to date for its moisture flow properties and provides a stringent test of classical capillary theory. We measure the rate at which moisture penetrates channels with diameters in the range of 10 to 120 nm with moist air present at 1 atm on one side and dry air at the same total pressure on the other. We extend classical theory for water leak rates at high humidities by allowing for variable meniscus curvature at the entrance and show that the extended theory explains why the flow increases greatly when capillary filling occurs and enables the contact angle to be determined. At low humidities our measurements for air-filled channels agree well with theory for the interdiffusive flow of water vapor in air. The flow rate of water-filled channels is one order of magnitude less than expected from classical capillary filling theory and is coincidentally equal to the helium flow rate, validating the use of helium leak testing for evaluating moisture flows in aluminum oxide leaks.

  10. Extraction of Alumina from Red Mud for Synthesis of Mesoporous Alumina by Adding CTABr as Mesoporous Directing Agent

    Directory of Open Access Journals (Sweden)

    Eka Putra Ramdhani

    2018-05-01

    Full Text Available Mines in Bintan were producing bauxite for many years. The production process of bauxite to alumina produced much red mud. From X-ray Fluorescence (XRF, alumina content on Bintan’s red mud was 28.87 wt.%. This research was studying on the extraction alumina from red mud with reduction of hematite (Fe2O3 and desilication processes. After extraction process alumina was collected about 52.89 wt.%. Synthesis of mesoporous alumina from red mud using sol-gel method at the room temperature for 72 h with cetyltrimethylammonium bromide (CTABr as mesoporous directing agent. The CTABr/Al-salt ratio, i.e. 1.57; 4.71 and 7.85 with the sample code of AMC-1, AMC-3, AMC-5, respectively. The product was calcined at 550 °C for 6 h. The synthesized materials were characterized by X-ray Diffraction (XRD, scanning electron microscopy-energy dispersive X-ray (SEM-EDX, transmission electron microscopy (TEM, and N2 adsorption-desorption techniques. XRD pattern of AMC-1, AMC-3, and AMC-5 showed that all synthesized materials have amorphous phase. The morphology were wormhole aggregate that were showed by SEM and TEM characterization. N2 adsorption-desorption characterization showed the distribution of pore size of about 3.2 nm. The highest surface area and pore volume were obtained in solid-solid ratio CTABr/GM-AL by 1.57 (AMC-1 i.e. 241 m2/g and 0.107 cm3/g, respectively.

  11. Characterization of metallized alumina: properties. [Diamonite P-3142-1, Wesgo Al-500 alumina ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Swearengen, J.C.; Burchett, O.L., Gieske, J.H.

    1976-12-01

    The effects of metallizing and brazing on the mechanical properties of Diamonite P-3142-1 and Wesgo A1-500 alumina ceramics were evaluated. The information was required for analytical prediction of the performance of ceramic-to-metal joints formed by the metallize-braze process. Residual stresses and fracture strengths were monitored before and after metallizing treatments; micromechanical modelling and surface acoustic wave experiments were utilized to determine density, thermal expansion and elastic moduli within the metallized region of the ceramics. It was observed that the metallizing elements penetrate the ceramics to a depth of about 005 ..mu..m and measurably modify the properties to a depth of about 300 ..mu..m. The moduli and density are increased approximately five percent within the penetration zone. The thermal expansion coefficients are not modified significantly by metallizing; the warping which occurs during metallizing results from microstructural changes within the ceramics and not differential thermal contraction. Fracture toughness of the Diamonite ceramic is greater than that of the Wesgo, although the metallizing treatments increase the toughness of each. Fracture strength of the Diamonite was degraded on the metallized surface, whereas the strength of the Wesgo was essentially unchanged by metallizing. Macroscopic compressive residual stresses, which exist at the surfaces of the ceramics, do not significantly affect the fracture strengths. The implications of these results for calculations of joint performance are discussed.

  12. Carbon-coated ceramic membrane reactor for production of hydrogen via aqueous phase reforming of sorbitol

    NARCIS (Netherlands)

    Neira d'Angelo, M.F.; Ordomskiy, V.; Schouten, J.C.; Schaaf, van der J.; Nijhuis, T.A.

    2014-01-01

    Hydrogen was produced by aqueous-phase reforming (APR) of sorbitol in a carbon-on-alumina tubular membrane reactor (4 nm pore size, 7 cm long, 3 mm internal diameter) that allows the hydrogen gas to permeate to the shell side, whereas the liquid remains in the tube side. The hydrophobic nature of

  13. Gamma camera

    International Nuclear Information System (INIS)

    Reiss, K.H.; Kotschak, O.; Conrad, B.

    1976-01-01

    A gamma camera with a simplified setup as compared with the state of engineering is described permitting, apart from good localization, also energy discrimination. Behind the usual vacuum image amplifier a multiwire proportional chamber filled with trifluorine bromium methane is connected in series. Localizing of the signals is achieved by a delay line, energy determination by means of a pulse height discriminator. With the aid of drawings and circuit diagrams, the setup and mode of operation are explained. (ORU) [de

  14. Gamma irradiator

    International Nuclear Information System (INIS)

    Simonet, G.

    1986-09-01

    Fiability of devices set around reactors depends on material resistance under irradiation noticeably joints, insulators, which belongs to composition of technical, safety or physical incasurement devices. The irradiated fuel elements, during their desactivation in a pool, are an interesting gamma irradiation device to simulate damages created in a nuclear environment. The existing facility at Osiris allows to generate an homogeneous rate dose in an important volume. The control of the element distances to irradiation box allows to control this dose rate [fr

  15. Avaliação da resistência ao desgaste de aluminas nanométricas produzidas a partir da decomposição térmica de acetato de alumínio liofilizado Evaluation of wear resistance of nanometric aluminas produced by thermal decomposition of lyophilized aluminum acetate

    Directory of Open Access Journals (Sweden)

    E. Fagury Neto

    2007-12-01

    Full Text Available Ensaios de resistência ao desgaste, na modalidade pino-contra-disco com pares deslizantes, foram realizados em pinos confeccionados a partir de pós de alumina proveniente do processo de decomposição térmica de acetato de alumínio liofilizado. Pós de alumina referentes às fases alfa-Al2O3 e gama-Al2O3, com e sem aditivos de sinterização (MgO e La2O3, foram usados para confeccionar pinos de desgaste. Pinos feitos também a partir de alumina comercial (A1000 SG foram analisados e os resultados foram comparados. Os ensaios foram feitos de acordo com norma ASTM e mostraram que os pinos confeccionados a partir de alfa-Al2O3 têm elevada resistência ao desgaste, comprovada pelos ensaios de perda de massa e microscopia eletrônica. Os pinos de gama-Al2O3 tiveram desempenho intermediário e os pinos de A1000 SG mostraram resultados menos expressivos.Wear resistance tests, using the pin-on-disk test method with sliding pairs, were carried out on pins produced from alumina powders prepared by thermal decomposition of lyophilized aluminum acetate. Alumina powders of alpha-Al2O3 and gamma-Al2O3 phases, with and without sintering additives (MgO and La2O3, were used to produce wear pins. In addition, pins made of commercial alumina (A1000 SG were tested and the results compared. The tests, carried out according to the ASTM standard, indicated that the pins made with alpha-Al2O3 powder showed high wear resistance, a finding corroborated by mass loss tests and scanning electron microscopy. The gamma-Al2O3 pins showed an intermediary performance while the A1000 SG pins showed less interesting results.

  16. Gamma teletopography

    International Nuclear Information System (INIS)

    Simonet, G.

    1987-06-01

    The mapping of gamma sources radiation emission in a nuclear plant is an important safety point. A remote gamma ray mapping process was developed in SPS/CEA/SACLAY. It uses the ''pinhole camera'' principle, precursor of photography. It mainly consists of a radiation proof box, with a small orifice, containing sensitive emulsions at the opposite. A first conventional photographic type emulsion photographs the area. A second photographic emulsion shows up the gamma radiations. The superim position of the two shots gives immediate informations of the precise location of each source of radiation in the observed area. To make easier the presentation and to improve the accuracy of the results for radiation levels mapping, the obtained films are digitally processed. The processing assigns a colours scale to the various levels of observed radiations. Taking account physical data and standard parameters, it gets possible to estimate the dose rate. The device is portable. Its compactness and fully independent nature make it suitable for use anywhere. It can be adapted to a remote automatic handling system, robot... so as to avoid all operator exposure when the local dose rate is too high [fr

  17. Membrane Biophysics

    CERN Document Server

    Ashrafuzzaman, Mohammad

    2013-01-01

    Physics, mathematics and chemistry all play a vital role in understanding the true nature and functioning of biological membranes, key elements of living processes. Besides simple spectroscopic observations and electrical measurements of membranes we address in this book the phenomena of coexistence and independent existence of different membrane components using various theoretical approaches. This treatment will be helpful for readers who want to understand biological processes by applying both simple observations and fundamental scientific analysis. It provides a deep understanding of the causes and effects of processes inside membranes, and will thus eventually open new doors for high-level pharmaceutical approaches towards fighting membrane- and cell-related diseases.

  18. Study of the interactions between alumina and metallic ion in solution at the liquid/oxide interface during catalysts synthesis; Etude des interactions alumine/ion metallique en solution a l`interface oxyde/liquide lors de la preparation des catalyseurs

    Energy Technology Data Exchange (ETDEWEB)

    Mertens de Wilmars, D.

    1998-01-15

    This work concerns the formation of compounds including metal and Al(III) ions during impregnation of gamma alumina with a solution of the metal precursor. Formation of Li/Al hydroxy-carbonate (Li/Al HDC) on alumina during impregnation by a neutral or basic solution containing Li{sup +} is established. Zeta potential measurements are used to determine the ratio overlay of the alumina by HDC Li/Al. By this technique, residual positive charges are observed on HDC Li/Al surface. The formation of two different compounds including Mo(VI) and Al(III) ions during impregnation of alumina with molybdate or hepta-molybdate solution is reported here for the first time. The use of sodium molybdate solution as impregnation precursor leads to the formation of hydroxy-molybdo-luminate, while the ammonium hepta-molybdate solution forms ammonium hexa-molybdo-aluminate by contact with alumina.Dissolution kinetics of alumina in aqueous solution in absence or in presence of metal ions (Li{sup +}, K{sup +}, Zn{sup 2+}, MoO{sub 4}{sup 2-}, Mo{sub 7}O{sub 24}{sup 6-}) are investigated at different pH. Results show that the support is not inert in aqueous solution, even at neutral pH (near ZPC). The homogeneous nucleation of Li/Al HDC observed for Li/Al{sub 2}O{sub 3} system evidence the permeability of the solid/solution interface: diffusion processus through the interface is more important than previously reported. A dissolution-precipitation mechanism is proposed to account for the formation of Al(III)-containing compounds on alumina surface. Alumina dissolves when contacted with aqueous solution. When Al(III) ions concentration in solution is bigger than the sur-saturation needed for heterogenous nucleation of the Al(III) containing compounds, this one precipitates. This mechanism agrees with all our results. (author) 169 refs.

  19. A study on heat transfer characteristics of spherical and fibrous alumina nanofluids

    International Nuclear Information System (INIS)

    Kim, Chang Kyu; Lee, Gyoung-Ja; Rhee, Chang Kyu

    2012-01-01

    Highlights: ► Spherical and fibrous alumina nanoparticles were prepared by pulsed wire evaporation and hydrolysis methods. ► Fibrous alumina nanofluid exhibited higher thermal conductivity enhancement than spherical one due to entangled structure of nanofibers with high aspect-ratio. ► Decreasing rate of viscosity with temperature for fibrous alumina nanofluid was much larger than that for spherical one. - Abstract: Ethylene glycol based nanofluids containing spherical/fibrous alumina nanoparticles were synthesized by pulsed wire evaporation and hydrolysis methods. The crystallographic and morphological properties of the prepared nanoparticles were analyzed by X-ray diffraction, nitrogen gas adsorption and transmission electron microscopy. The average diameter of spherical alumina nanoparticles was about 80 nm and the alumina nanofibers exhibited a high aspect ratio (length/width). The viscosity and thermal conductivity of the spherical/fibrous alumina nanofluids were experimentally measured in the temperature range from 25 to 80 °C. For the fibrous alumina nanofluid, the increase of temperature raised thermal conductivity but lowered viscosity. On the other hand, for the spherical alumina nanofluid, both thermal conductivity and viscosity were decreased with increasing temperature. In particular, the fibrous alumina nanofluid exhibited a higher enhancement of thermal conductivity than the spherical one due to the well-connected structure between entangled nanofibers with high aspect ratio.

  20. Deuterium permeation of amorphous alumina coating on 316L prepared by MOCVD

    International Nuclear Information System (INIS)

    Li Shuai; He Di; Liu Xiaopeng; Wang Shumao; Jiang Lijun

    2012-01-01

    Highlights: ► Deuterium permeation behavior of alumina coating by MOCVD is investigated. ► The as-prepared alumina is amorphous. ► The alumina coating is dense and well adherent to substrate. ► Deuterium permeation rate of alumina coating is 2–3 orders of magnitude lower than martensitic steels. - Abstract: The deuterium permeation behavior of the alumina coating on 316L stainless steel prepared by metal organic chemical vapor deposition (MOCVD) was investigated. The alumina coating was also characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and scanning electron microscope (SEM). It was found that the as-prepared coating consisted of amorphous alumina. This alumina coating had a dense, crack-free and homogeneous morphology. Although the alumina coating was amorphous, effective suppression of deuterium permeation was demonstrated. The deuterium permeability of the alumina coating was 51–60 times less than that of the 316L stainless steel and 153–335 times less than that of the referred low activation martensitic steels at 860–960 K.

  1. Preparation and characterization of metallic supported thin Pd-Ag membranes for hydrogen separation

    OpenAIRE

    Fernandez, Ekain; Medrano, Jose Antonio; Melendez, Jon; Parco, Maria; Viviente, J.L.; van Sint Annaland, Martin; Gallucci, Fausto; Pacheco Tanaka, David A.

    2015-01-01

    This paper reports the preparation and characterization of thin-film (4-5 µm thick) Pd-Ag metallic supported membranes for high temperature applications. Various thin film membranes have been prepared by depositing a ceramic interdiffusion barrier layer prior to the simultaneous Pd-Ag electroless plating deposition. Two deposition techniques for ceramic layers (made of zirconia and alumina) have been evaluated: atmospheric plasma spraying and dip coating of a powder suspension. Initially, the...

  2. Spectroscopic and nonlinear photophysical characterization of organic octupolar-compounds supported by anodic-alumina nanotube-arrays

    International Nuclear Information System (INIS)

    Morales-Saavedra, O.G.; Ontiveros-Barrera, F.G.; Hennrich, G.; Mata-Zamora, M.E.; Rodriguez-Rosales, A.A.; Banuelos, J.G.

    2011-01-01

    Highlights: → Preparation of organic-inorganic nanostructured hybrid materials. → Insertion of octupolar compounds in alumina nanotube arrays. → Linear and nonlinear photophysical characterization of solid-state hybrid structures. → Fabrication of photonic materials. - Abstract: Amorphous anodic alumina membranes (AAM) comprising highly ordered nanometric porous arrays (porous anodic aluminas: PAA) with 1D-nanotube dimensions of ∼75 nm in diameter and 45 microns in depth were successfully prepared and used as nanostructured host networks for different functionalized octupolar chromophores (named here Oct-(n)). Atomic force microscopy (AFM) studies performed on the developed hybrid systems confirmed a homogeneous insertion of these organic molecules into the PAA nanotube-arrays. Samples with high structural quality were selected for several photophysical characterizations: Comprehensive X-ray diffraction (XRD) and optical spectroscopic characterizations performed according to UV-vis absorption, photoluminescent (PL) and Raman measurements revealed the structural and optical performance of these molecules within the PAA-confinement. Since the implemented optical chromophores were specifically functionalized for nonlinear optical (NLO) applications, the obtained Oct-(n)/PAA-based amorphous hybrids were also characterized according to cubic NLO-techniques such as third harmonic generation (THG) and the Z-Scan method. PAA-confined octupolar chromophores have shown interesting linear and NLO optical properties which have not yet been intensively investigated in bulk hybrid systems; hence, the obtained hybrid nanostructures represent a promising field of investigation in the route to functional octupolar-based materials, where different self-assembled molecular structures may be formed, giving rise to enhanced linear and NLO-properties.

  3. Study of preparation and surface morphology of self-ordered nanoporous alumina; Estudo da preparacao e da morfologia de superficie de alumina nanoporosa auto-organizada

    Energy Technology Data Exchange (ETDEWEB)

    Rodrigues, Elisa Marchezini; Martins, Maximiliano Delany, E-mail: elisamarch@gmail.com, E-mail: MG.mdm@cdtn.br [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG. (Brazil); Silva, Ronald Arreguy, E-mail: arregsilva@yahoo.com.br [Centro Universitario de Belo Horizonte (UniBH), Belo Horizonte, MG (Brazil)

    2013-07-01

    Nanoporous alumina is a typical material that exhibits self-ordered nanochannels spontaneously organized in hexagonal shape. Produced by anodizing of metallic aluminum, it has been used as a template for production of materials at the nanoscale. This work aimed to study the preparation of nanoporous alumina by anodic anodizing of metallic aluminum substrates. The nanoporous alumina was prepared following the methodology proposed by Masuda and Fukuda (1995), a two-step method consisting of anodizing the aluminum sample in the potentiostatic mode, removing the layer of aluminum oxide (alumina) formed and then repeat the anodization process under the same conditions as the first anodization. This method produces nanoporous alumina with narrow pore diameter distribution and well-ordered structure. (author)

  4. Electrochemically grown metallic nanocomb structures on nanoporous alumina templates

    International Nuclear Information System (INIS)

    Kaya, Savas; Atar, Erdem

    2011-01-01

    Electrochemical growth of metallic nanocomb structures on anodized alumina templates is described. Nanocombs originate from the orderly growth and merger of very thin (d=15±5 nm) metallic nanowires which do not completely fill much larger pores (d∼100 nm) in the alumina template (t≤3 μm). Instead, the nanowires prefer growing along the inner corners of the hexagonal pores, coalescing into a highly ordered structure as they emerge, resulting a metallic form reminiscent of the topology of the original template. We disclose here the typical processing conditions and the microstructure of this previously unknown material as observed with a scanning electron microscope (SEM) and energy dispersive x-ray (EDX) spectroscopy. It is shown that Au nanocombs have an anomalous EDX spectra and can emit electrons at a field of ∼1 kV/cm.

  5. Health monitoring technology for alumina-fiber-reinforced plastic

    International Nuclear Information System (INIS)

    Aoyama, Hiroshi; Watanabe, Hiroyuki; Terai, Motoaki

    1998-01-01

    Formally, we developed new load-support systems that consists of a biconical, alumina-fiber-reinforced plastic (ERP) structure for the superconducting magnet. Safe operation of the superconducting magnet will be jeopardized if the mechanical condition of the load-support system begins to degrade. One of the factors that evaluate the soundness of the superconducting magnet is the stiffness of the load-support system. Here, it is important to know the relation between the degradation of the stiffness and the growth of defects. For this purpose, firstly, a fatigue test of the load-support system was carried out, and the various defects (matrix cracking and delamination of FRP laminates) were observed during this fatigue testing. Finally, we proposed the application of two non-destructive-evaluation (NDE) methods for the health monitoring of alumina/epoxy load-support systems. (author)

  6. Preparation of alumina microspheres. Its application as in inorganic exchanger

    Energy Technology Data Exchange (ETDEWEB)

    Santos, W.R. dos; Abrao, A [Instituto de Pesquisas Energeticas e Nucleares, Sao Paulo (Brazil). Centro de Engenharia Quimica

    1980-01-01

    Inorganic exchangers are widely used for adsorption and column partition chromatography. The main difficulty of using commercial alumina (in powder) for column chromatography is related to its packing, and the operations through the column become diffcult and time-consuming; also it turns to be virtually impossible to use large dimension columns. In order to eliminate these problems, a process for the preparation of alumina microspheres was developed as an adaptation of a similar process used to prepare nuclear fuel microspheres (UO/sub 2/, ThO/sub 2/). The flowsheet of this process is presented together with the analytical results of sphericity after calcination, granulometry, density and characterization by X-ray diffractometry. Solubility tests showed that the so-prepared microspheres are well resistant to strong acids and bases; retention tests showed their efficiency, mainly to copper.

  7. Evaluation of technological properties of alumina refractory systems-zirconia and zirconia-silica-alumina; Avaliacao das propriedades tecnologicas de refratarios dos sistemas alumina-zirconia e alumina-zirconia-silica

    Energy Technology Data Exchange (ETDEWEB)

    Marinho, A.R.O.; Carvalho, T.U.S.; Fagury Neto, E.; Rabelo, A.A., E-mail: adriano@unifesspa.edu.br [Universidade Federal do Sul e Sudeste do Para (UFSSPA), Maraba, PA (Brazil)

    2014-07-01

    Alumina-zirconia refractories are noted for being products of excellent cost-effective, however, zirconia may limit its use due to decreasing resistance to thermal shock. This study aims to evaluate these refractories with the addition of microsilica, which can greatly improve their properties. Were used the following starting materials: calcined alumina, zirconia (stabilized and monoclinic) in amounts of 2%, 4% and 6% by weight, plus microsilica (5%w.). The powders were milled together with binder and lubricant for conformation bodies by uniaxial pressing. The samples were dried, calcined and sintered at 1400 °C/2h were characterized using the methods of Archimedes, and scanning electron microscopy (SEM), chemical analysis using energy dispersive X-ray (EDS), and mechanical flexural strength tests at room temperature. Formulations with the presence of microsilica showed satisfactory results and optimized properties. (author)

  8. MICROWAVE JOINING OF ALUMINA CERAMIC AND HYDROXYLAPATITE BIOCERAMIC

    Institute of Scientific and Technical Information of China (English)

    1999-01-01

    Microwave joining is a rapid developmental new techniqu e in recent years.This paper introduces a new microwave joining equipment which was made by our lab,succeeds in alumina ceramic-hydroxylapatite bioceramic j o in in the equipment, and analyzes the join situation of join boundary by using s canni ng electron microscope(SEM),this paper analyzes the mechanism of microwave joini ng also.

  9. Results of recent KROTOS FCI tests. Alumina vs. corium melts

    Energy Technology Data Exchange (ETDEWEB)

    Huhtiniemi, I.; Magallon, D.; Hohmann, H. [Commission of the European Communities, Ispra (Italy). Joint Research Center

    1998-01-01

    Recent results from KROTOS fuel-coolant interaction experiments are discussed. Five tests with alumina were performed under highly subcooled conditions, all of these tests resulted in spontaneous steam explosions. Additionally, four tests were performed at low subcooling to confirm, on one hand, the suppression of spontaneous steam explosions under such conditions and, on the other hand, that such a system is still triggerable using an external initiator. The other test parameters in these alumina tests included the melt superheat and the initial pressure. All the tests in the investigated superheat range (150 K - 750 K) produced a steam explosion and no evidence of the explosion suppression by the elevated initial pressure (in the limited range of 0.1 - 0.375 MPa) was observed in the alumina tests. The corium test series include a test with 3 kg of melt under both subcooled and near saturated conditions at ambient pressure. Two additional tests were performed with subcooled water; one test was performed at an elevated pressure of 0.2 MPa with 2.4 kg of melt and another test with 5.1 kg of melt at ambient pressure. None of these tests with corium produced a propagating energetic steam explosion. However, propagating low energy (about twice the energy of the trigger pulse) events were observed. All corium tests produced significantly higher water level swells during the mixing phase than the corresponding alumina tests. Present experimental evidence suggests that the water depletion in the mixing zone suppresses energetic steam explosions with corium melts at ambient pressure and in the present pour geometry. Processes that could produce such a difference in void generation are discussed. (author)

  10. Porous Alumina and Zirconia Ceramics With Tailored Thermal Conductivity

    Czech Academy of Sciences Publication Activity Database

    Gregorová, E.; Pabst, W.; Sofer, Z.; Jankovský, O.; Matějíček, Jiří

    2012-01-01

    Roč. 395, č. 1 (2012), 012022-012022 ISSN 1742-6588. [European Thermal Sciences Conference (Eurotherm)/6./. Poitiers, 04.09.2012-07.09.2012] Institutional support: RVO:61389021 Keywords : Ceramics * alumina * zirconia * porosity * thermal conductivity * pore-forming agent * oxide ceramics * starch * porosity Subject RIV: JK - Corrosion ; Surface Treatment of Materials http://iopscience.iop.org/1742-6596/395/1/012022/pdf/1742-6596_395_1_012022.pdf

  11. On the thermally activated crack propagation in alumina

    International Nuclear Information System (INIS)

    Devezas, T.C.

    1983-01-01

    Subcritical crack growth was studied in the temperature 25-100 0 C in two commercial aluminas containing different amounts of a glassy phase. The experimental method employed was that of double torsion under constant load, using a device specially built to carry out mechanical tests at constant compressive load and high temperatures. Activation enthalpies of subcritical crack growth were determined for the two materials. (Author) [pt

  12. Ion irradiation effect of alumina and its luminescence

    Energy Technology Data Exchange (ETDEWEB)

    Aoki, Yasushi; Yamamoto, Shunya; Naramoto, Hiroshi [Japan Atomic Energy Research Inst., Takasaki, Gunma (Japan). Takasaki Radiation Chemistry Research Establishment; My, N T

    1997-03-01

    The luminescence spectra of single crystalline alpha-alumina and ruby which has 0.02% of Cr{sub 2}O{sub 3} as a impurity, induced by 200 keV He{sup +} and Ar{sup +} irradiation were measured at room temperature as a function of irradiation dose. The analysis of the measured spectra showed the existence of three main luminescence features in the wavelength region of 250 to 350 nm, namely anionic color centers, F-center at 411 nm and F{sup +}-center at 330 nm and a band observed around 315 nm. As alpha-alumina was irradiated with He{sup +}, F-center and F{sup +}-center luminescence grew and decayed, but the behaviors of those were different from each other. It seems that a concentration quenching occurred on the F-center luminescence in the dose range above 1x10{sup 14} He/cm{sup 2}. Furthermore, F-center luminescence was strongly suppressed in ruby, compared with that in alumina. On the other hand, the luminescence band around 315 nm appeared only in the early stage of irradiation and did not show its growth part. The dose dependent behavior was similar to that of Cr{sup 3+} emission at 695 nm (R-line) in ruby in both cases of He{sup +} and Ar{sup +} irradiation. Based on the experimental results mentioned above, the processes of defect formation and excitation in alumina in the early stage of ion irradiation will be discussed. (author)

  13. Dependence of the Stabilization of -Alumina on the Spray Process

    Czech Academy of Sciences Publication Activity Database

    Stahr, C.Ch.; Saaro, S.; Berger, L.-M.; Herrmann, M.; Dubský, Jiří; Neufuss, Karel

    2007-01-01

    Roč. 16, 5-6 (2007), s. 822-830 ISSN 1059-9630 R&D Projects: GA ČR(CZ) GA106/05/0483 Institutional research plan: CEZ:AV0Z20430508 Keywords : -Al2O3 stabilization * alumina * chromia * solid solution * X-ray diffraction Subject RIV: JK - Corrosion ; Surface Treatment of Materials Impact factor: 1.204, year: 2007

  14. Oxidation of mullite-zirconia-alumina-silicon carbide composites

    International Nuclear Information System (INIS)

    Baudin, C.; Moya, J.S.

    1990-01-01

    This paper reports the isothermal oxidation of mullite-alumina-zirconia-silicon carbide composites obtained by reaction sintering studied in the temperature interval 800 degrees to 1400 degrees C. The kinetics of the oxidation process was related to the viscosity of the surface glassy layer as well as to the crystallization of the surface film. The oxidation kinetics was halted to T ≤ 1300 degrees C, presumably because of crystallization

  15. Efective infrared reflectivity and dielectric function of polycrystalline alumina ceramics

    Czech Academy of Sciences Publication Activity Database

    Nuzhnyy, Dmitry; Petzelt, Jan; Borodavka, Fedir; Vaněk, Přemysl; Šimek, Daniel; Trunec, D.; Maca, K.

    2017-01-01

    Roč. 254, č. 5 (2017), s. 1-8, č. článku 1600607. ISSN 0370-1972 R&D Projects: GA ČR GA15-08389S Institutional support: RVO:68378271 Keywords : alumina * ceramics * effective dielectric function * effective medium approximation * geometrical resonances * infrared reflectivity Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 1.674, year: 2016

  16. Glass properties in the yttria-alumina-silica system

    Science.gov (United States)

    Hyatt, M. J.; Day, D. E.

    1987-01-01

    The glass formation region in the yttria-alumina-silica system was investigated. Properties of glasses containing 25 to 55 wt pct yttria were measured and the effect of the composition was determined. The density, refractive index, thermal-expansion coefficient, and microhardness increased with increasing yttria content. The dissolution rate in 1N HCl increased with increasing yttria content and temperature. These glasses were also found to have high electrical resistivity.

  17. Vitrification of high-level alumina nuclear waste

    International Nuclear Information System (INIS)

    Brotzman, J.R.

    1979-01-01

    Borophosphate glass compositions have been developed for the vitrification of a high-alumina calcined defense waste. The effect of substituting SiO 2 , P 2 O 5 and CuO for B 2 O 3 on the viscosity and leach resistance was measured. The effect of the alkali to borate ratio and the Li 2 O:Na 2 O ratio on the melt viscosity and leach resistance was also measured

  18. Organized Mesoporous Alumina: Synthesis, Structure and Potential in Catalysis

    Czech Academy of Sciences Publication Activity Database

    Čejka, Jiří

    2003-01-01

    Roč. 254, - (2003), s. 327-338 ISSN 0926-860X R&D Projects: GA AV ČR IAA4040001; GA ČR GA104/02/0571; GA MŠk ME 404 Institutional research plan: CEZ:AV0Z4040901 Keywords : organized mesoporous alumina * mesoporous molecular sieves * synthesis Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 2.825, year: 2003

  19. Near-field radiative heat transfer in mesoporous alumina

    International Nuclear Information System (INIS)

    Li Jing; Feng Yan-Hui; Zhang Xin-Xin; Huang Cong-Liang; Wang Ge

    2015-01-01

    The thermal conductivity of mesoporous material has aroused the great interest of scholars due to its wide applications such as insulation, catalyst, etc. Mesoporous alumina substrate consists of uniformly distributed, unconnected cylindrical pores. Near-field radiative heat transfer cannot be ignored, when the diameters of the pores are less than the characteristic wavelength of thermal radiation. In this paper, near-field radiation across a cylindrical pore is simulated by employing the fluctuation dissipation theorem and Green function. Such factors as the diameter of the pore, and the temperature of the material are further analyzed. The research results show that the radiative heat transfer on a mesoscale is 2∼4 orders higher than on a macroscale. The heat flux and equivalent thermal conductivity of radiation across a cylindrical pore decrease exponentially with pore diameter increasing, while increase with temperature increasing. The calculated equivalent thermal conductivity of radiation is further developed to modify the thermal conductivity of the mesoporous alumina. The combined thermal conductivity of the mesoporous alumina is obtained by using porosity weighted dilute medium and compared with the measurement. The combined thermal conductivity of mesoporous silica decreases gradually with pore diameter increasing, while increases smoothly with temperature increasing, which is in good agreement with the experimental data. The larger the porosity, the more significant the near-field effect is, which cannot be ignored. (paper)

  20. Thermal and tensile properties of alumina filled PET nanocomposites

    Science.gov (United States)

    Nikam, Pravin N.; Deshpande, Vineeta D.

    2018-05-01

    In the present investigation, nanocomposites of poly(ethylene terephathalate)(PET) with different content (0 to 5 wt.%) of alumina nanoparticles (n-Al2O3) were prepared by melt-extrusion technique. Morphological characterization of samples was examined by transmission electron microscopy (TEM). Morphological analysis revealed that degree of dispersion of alumina nanoparticles (ANPs) was increased at lower content (i.e. upto 2 wt.%), which observed by TEM. Thermal and tensile measurements were carried out using and differential scanning calorimetry (DSC) and universal testing machine (UTM). The thermal analysis showed that the glass transition termperature (Tg), melting temperature (Tm), crystallization temperature (Tc) of PET/alumina nanocomposites (PNCs) were higher than neat PET (PET0). The heat enthalpy (ΔHm) of crystallization for PNCs was increased compared to PET0, which indicates that degree of crystallinity of PNCs also increased compared to PET0. The half-time (t0.5) of crystallization of PNCs were decreased compared to PET0 which indicates that the incorporation of ANPs nucleate the PET molecular chains and allowing the easily crystallization during nonisothermal process. The tensile analysis revealed that the tensile elastic modulus (i.e. Young's modulus) of PNCs increased almost linearly with increasing the content of ANPs while tensile elongation at break decreased nonlinearly. The tensile strength of PNCs increased with a 1 wt.% of ANPs whereas the higher content of ANPs decreased the tensile strength.

  1. Nanocarbon-Coated Porous Anodic Alumina for Bionic Devices

    Directory of Open Access Journals (Sweden)

    Morteza Aramesh

    2015-08-01

    Full Text Available A highly-stable and biocompatible nanoporous electrode is demonstrated herein. The electrode is based on a porous anodic alumina which is conformally coated with an ultra-thin layer of diamond-like carbon. The nanocarbon coating plays an essential role for the chemical stability and biocompatibility of the electrodes; thus, the coated electrodes are ideally suited for biomedical applications. The corrosion resistance of the proposed electrodes was tested under extreme chemical conditions, such as in boiling acidic/alkali environments. The nanostructured morphology and the surface chemistry of the electrodes were maintained after wet/dry chemical corrosion tests. The non-cytotoxicity of the electrodes was tested by standard toxicity tests using mouse fibroblasts and cortical neurons. Furthermore, the cell–electrode interaction of cortical neurons with nanocarbon coated nanoporous anodic alumina was studied in vitro. Cortical neurons were found to attach and spread to the nanocarbon coated electrodes without using additional biomolecules, whilst no cell attachment was observed on the surface of the bare anodic alumina. Neurite growth appeared to be sensitive to nanotopographical features of the electrodes. The proposed electrodes show a great promise for practical applications such as retinal prostheses and bionic implants in general.

  2. Dielectric properties of alumina/zirconia composites at millimeter wavelengths

    International Nuclear Information System (INIS)

    Molla, J.; Heidinger, R.; Ibarra, A.; Link, G.

    1994-01-01

    Alumina-zirconia composites with ZrO 2 contents up to 20% and negligible porosity were investigated at millimeter (mm) wavelengths to determine the changes appearing in the dielectric properties of pure alumina ceramics when unstabilized or partially stabilized ZrO 2 is added to improve the mechanical strength. It is demonstrated that it essential to distinguish between the contributions of the monoclinic and the tetragonal phase of zirconia (m-ZrO 2 , t-ZrO 2 ). Permittivity is raised with increasing content of either phases; the effective permittivity can be assessed by the rule of mixtures (Maxwell-Garnett formulation of the generalized Clasussius-Mossotti relation) using permittivity values of 10 for Al 2 O 3 , 14-21 for m-ZrO 2 and 40-45 for t-ZrO 2 . The permittivity data show only a small variation in the investigated range of 9-145 GHz. For the dielectric loss, there is evidence of a predominant contribution of m-ZrO 2 ; in addition, the marked increase in loss with frequency becomes sharper. The t-ZrO 2 , which is responsible for strengthening, does not show any significant influence on losses. It is therefore concluded, that ZrO 2 strengthening of alumina is feasible without affecting mm-wave losses at room temperature as long as the presence of m-ZrO 2 is avoided

  3. Environmental Sustainability of the Alumina Industry in Western Europe

    Directory of Open Access Journals (Sweden)

    Valentina Dentoni

    2014-12-01

    Full Text Available The implementation of European policies on environmental protection is enforcing some substantial modifications in the processing methods and technologies traditionally adopted in the alumina industry and, in particular, in the management of the alumina residue produced. The article analyses the evolution of the alumina production and the residue disposal practices in Western Europe. Some critical aspects regarding the legal implementation of the EU Directive on the landfill of waste are highlighted and discussed. With reference to the requirements established for the landfill of non-hazardous waste, a key point is represented by the possibility of reducing the deposit protection measures if the collection and treatment of leachate is not necessary. The flexibility introduced by the Directive is not incorporated into the Italian law; this fact may represent a major issue in the prospect of disposal conversion from wet to dry methods for companies operating in Italy, as it may endanger the economic sustainability of the plants’ upgrade, as well as the opportunity to attract outside investments.

  4. Investigation of vapor explosions with alumina droplets in sodium

    International Nuclear Information System (INIS)

    Zimmer, H.J.

    1991-02-01

    Within the analysis of severe hypothetical fast breeder accidents the consequence of a fuel-coolant interaction has to be considered i.e. the thermal interaction between hot molten fuel and sodium. Experiments have been performed to study the thermal fragmentation of a molten alumina droplet in sodium. Alumina temperatures up to 3100 K and sodium temperatures up to 1143 K were used. For the first time film boiling of alumina drops in sodium was achieved. With some droplets undergoing film boiling, the fragmentation was triggered by an externally applied pressure wave. The trigger was followed promptly by a strong reaction pressure wave if and only if a contact temperature threshold of T I =2060±160 K was exceeded. In agreement with similar experiments in which other materials were studied this threshold corresponds to an interfacial temperature close to the homogeneous nucleation temperature of the vaporising liquid. Based on the present and previous experimental results a model concept of thermal fragmentation is developed. (orig.) [de

  5. Removing Bacillus subtilis from fermentation broth using alumina nanoparticles.

    Science.gov (United States)

    Mu, Dashuai; Mu, Xin; Xu, Zhenxing; Du, Zongjun; Chen, Guanjun

    2015-12-01

    In this study, an efficient separation technology using Al2O3 nanoparticles (NPs) was developed for removing Bacillus subtilis from fermentation broth. The dosage of alumina nanoparticles used for separating B. subtilis increased during the culture process and remained stable in the stationary phase of the culture process. The pH of the culture-broth was also investigated for its effects on flocculation efficiency, and showed an acidic pH could enhance the flocculation efficiency. The attachment mechanisms of Al2O3 NPs to the B. subtilis surface were investigated, and the zeta potential analysis showed that Al2O3 NPs could attach to B. subtilis via electrostatic attachment. Finally, the metabolite content and the antibacterial effect of the fermentation supernatants were detected and did not significantly differ between alumina nanoparticle separation and centrifugation separation. Together, these results indicate a great potential for a highly efficient and economical method for removing B. subtilis from fermentation broth using alumina nanoparticles. Copyright © 2015 Elsevier Ltd. All rights reserved.

  6. Synthesis and textural evolution of alumina particles with mesoporous structures

    Science.gov (United States)

    Liu, Xun; Peng, Tianyou; Yao, Jinchun; Lv, Hongjin; Huang, Cheng

    2010-06-01

    Alumina particles with mesostructures were synthesized through a chemical precipitation method by using different inorganic aluminum salts followed by a heterogeneous azeotropic distillation and calcination process. The obtained mesoporous γ-alumina particles were systematically characterized by the X-ray diffraction, transmission electron microscopy and nitrogen adsorption-desorption measurement. Effects of the aluminum salt counter anion, pH value and the azeotropic distillation process on the structural or textural evolution of alumina particles were investigated. It is found that Cl - in the reaction solution can restrain the textural evolution of the resultant precipitates into two-dimensional crystallized pseudoboehmite lamellae during the heterogeneous azeotropic distillation, and then transformed into γ-Al 2O 3 particles with mesostructures after further calcination at 1173 K, whereas coexisting SO 42- can promote above morphology evolution and then transformed into γ-Al 2O 3 nanofibers after calcination at 1173 K. Moreover nearly all materials retain relatively high specific surface areas larger than 100 m 2 g -1 even after calcinations at 1173 K.

  7. On characterizing the mechanical properties of aluminum–alumina composites

    International Nuclear Information System (INIS)

    Gudlur, Pradeep; Boczek, Artur; Radovic, Miladin; Muliana, Anastasia

    2014-01-01

    The overall response of aluminum–alumina (Al–Al 2 O 3 ) composites depends strongly on their microstructural characteristics. We study the overall mechanical response of Al–Al 2 O 3 composites experimentally, using Resonant Ultrasound Spectroscopy (RUS) and uniaxial compressive testing. Microstructures of composite with 10% alumina volume content are constructed from the microstructural images of the composite obtained from scanning electron microscopy (SEM). The SEM images of the composite are converted to finite element (FE) meshes, which are used to solve the boundary value problem in order to determine the overall mechanical response of the Al–Al 2 O 3 composite. The responses generated from the micromechanical models are compared with the elastic modulus obtained from RUS and experimental stress–strain curves from uniaxial compression tests. Effects of processing, porosity, alumina content, thermal (residual) stress, and plastic deformation on the overall elastic modulus and response of the composites are also studied. We observed that slightly altering the processing method had a significant effect on the microstructural characteristics and in turn on the overall physical and mechanical properties of the composite. With changes in porosity by 2–3%, the elastic modulus was found to vary by 10–15 GPa approximately. We observed that the elastic moduli of the composites determined from the uniaxial compressive tests are close to those obtained from RUS

  8. Gamma teletopography

    International Nuclear Information System (INIS)

    Simonet, G.

    1986-09-01

    To set the gamma activity cartography is an important element of safety in numerous cases: intervention in hot cell, search of a radioactive source, examination of radioactive waste circuit followed by a reprocessing definition of decontamination and decommissioning processes and for all other accidents. The device presented here is like a ''black box'' with an aperture and an emulsion photosensitive to the opposite; a classical film takes photography of the place; a X-ray type emulsion gives a spot more or less contrasted and extensive corresponding to each source. Images can be processed with a microprocessor [fr

  9. A Study on the Effect of Nano Alumina Particles on Fracture Behavior of PMMA

    Directory of Open Access Journals (Sweden)

    Arezou Sezavar

    2015-04-01

    Full Text Available In the current research, the role of nano-sized alumina on deformation and fracture mechanism of Poly Methyl Methacrylate (PMMA was investigated. For this purpose, PMMA matrix nanocomposite reinforced with different wt% of alumina (i.e., 5, 10 and 15 were fabricated using the compression molding technique. Tensile properties of produced nanocomposites were studied using Zwick Z250 apparatus at cross head speed of about 5 mm/min. In order to specify the role of alumina nanoparticles on deformation and fracture mechanism of PMMA, microscopic evaluation was performed using scanning electron microscope (SEM. The achieved results prove that tensile properties of PMMA depend on alumina wt%. For example, addition of 15 wt% alumina to PMMA causes an increase of about 25% modulus of elasticity. Micrographs taken from the fracture surface of PMMA and its nanocomposites show deformation and fracture mechanism of PMMA changes as alumina is added to it.

  10. Deuterium permeation of amorphous alumina coating on 316L prepared by MOCVD

    Science.gov (United States)

    Li, Shuai; He, Di; Liu, Xiaopeng; Wang, Shumao; Jiang, Lijun

    2012-01-01

    The deuterium permeation behavior of the alumina coating on 316L stainless steel prepared by metal organic chemical vapor deposition (MOCVD) was investigated. The alumina coating was also characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and scanning electron microscope (SEM). It was found that the as-prepared coating consisted of amorphous alumina. This alumina coating had a dense, crack-free and homogeneous morphology. Although the alumina coating was amorphous, effective suppression of deuterium permeation was demonstrated. The deuterium permeability of the alumina coating was 51-60 times less than that of the 316L stainless steel and 153-335 times less than that of the referred low activation martensitic steels at 860-960 K.

  11. Role of Metal Oxides in Chemical Evolution: Interaction of Ribose Nucleotides with Alumina

    Science.gov (United States)

    Arora, Avnish Kumar; Kamaluddin

    2009-03-01

    Interaction of ribonucleotides—namely, 5‧-AMP, 5‧-GMP, 5‧-CMP, and 5‧-UMP—with acidic, neutral, and basic alumina has been studied. Purine nucleotides showed higher adsorption on alumina in comparison with pyrimidine nucleotides under acidic conditions. Adsorption data obtained followed Langmuir adsorption isotherm, and Xm and KL values were calculated. On the basis of infrared spectral studies of ribonucleotides, alumina, and ribonucleotide-alumina adducts, we propose that the nitrogen base and phosphate moiety of the ribonucleotides interact with the positive charge surface of alumina. Results of the present study may indicate the importance of alumina in concentrating organic molecules from dilute aqueous solutions in primeval seas in the course of chemical evolution on Earth.

  12. Experimental research on HEL and failure properties of alumina under impact loading

    Directory of Open Access Journals (Sweden)

    Xiao-wei Feng

    2016-06-01

    Full Text Available A series of plate impact experiments on alumina was conducted using a light gas gun in order to further investigate Hugoniot elastic limit (HEL and failure properties of alumina under shock compression. The velocity interferometer system for any reflector (VISAR was used to record the rear-free surface velocity histories of the alumina samples. According to the experimental results, the HELs of tested alumina samples with different thicknesses were measured, and the decay phenomenon of elastic wave in shocked alumina was studied. A phenomenological expression between HEL and thickness of sample was presented, and the causes of the decay phenomenon were discussed. The propagation of failure wave in shocked alumina was probed. The velocity and delayed time of failure wave propagation were obtained. The physical mechanism of the generation and propagation of failure was further discussed.

  13. Comparative study on sintered alumina for ballistic shielding application; Estudo comparativo entre aluminas sinterizadas visando aplicacao em blindagem balistica

    Energy Technology Data Exchange (ETDEWEB)

    Melo, Francisco Cristovao Lourenco de; Goncalves, Diniz Pereira [Centro Tecnico Aeroespacial (CTA), Sao Jose dos Campos, SP (Brazil). Inst. de Aeronautica e Espaco

    1997-12-31

    This work presents a development of the armor made from special ceramic materials and kevlar. An experimental investigation was conducted to study the ballistic penetration resistance on three samples taken from sintered alumina: a commercial one and two formulations A and B made in IAE/CTA. The main differences between the two formulations was the grain size and bend resistance. The knowledge of the mechanisms during the penetration and perforation process allowed to apply a ductile composite laminate made form kevlar under the alumina to delay its rupture. The last ballistic test showed how a Weibull`s modulii and other mechanical properties are able to improve ballistic penetration resistance. (author) 3 refs.

  14. Heterogeneous burnable poisons. Sinterability study in oxidizing atmosphere of alumina-gadolinia and alumina-boron carbide compounds

    International Nuclear Information System (INIS)

    Agueda, H.C.; Leiva, S.F.; Russo, D.O.

    1990-01-01

    Solid burnable poisons are used in reactors cooled by pressure light water (PLWR) with the purpose of controlling initial reactivity in the first reactor's core. The burnable poisons may be uniformly mixed with the fuel -known as 'homogeneous' poisons-; or constituting separate elements -known as heterogeneous poisons-. The purpose of this work is to present the results of two sinterability studies, performed on Al 2 O 3 -Gd 2 O 3 and Al 2 O 3 -B 4 C, where alumina acts as inert matrix, storing the absorbing elements as Gd 2 O 3 or B 4 C. The elements were sintered at an air atmosphere and additives permitting the obtention of a greater density alumina were tested at lower temperatures than the characteristic for this material, in order to determine its compatibility with the materials dealt with herein. (Author) [es

  15. Membranes of activated CD4+ T cells expressing T cell receptor (TcR) alpha beta or TcR gamma delta induce IgE synthesis by human B cells in the presence of interleukin-4

    NARCIS (Netherlands)

    Gascan, H.; Aversa, G. G.; Gauchat, J. F.; van Vlasselaer, P.; Roncarolo, M. G.; Yssel, H.; Kehry, M.; Spits, H.; de Vries, J. E.

    1992-01-01

    In the present study it is demonstrated that human B cells can be induced to switch to IgE production following a contact-mediated signal provided by activated T cell receptor (TcR) gamma delta+, CD4+ and TcR alpha beta+, CD4+ T cell clones and interleukin (IL)-4. The signal provided by these T cell

  16. Gamma knife

    International Nuclear Information System (INIS)

    Kawamoto, Shunsuke; Takakura, Kintomo

    1991-01-01

    As to the gamma knife which is the radiation surgery device developed in Sweden a quarter century ago, its principle, structure, treatment techniques, already established clinical effect and the problems being left for hereafter are described. This treatment means supplements the operation under microscopes, and at present it takes the important position in neurosurgery, but hereafter, by the interdisciplinary cooperation of neurosurgery and clinical radiobiology, the more development can be expected. The method of irradiating the radiation of high dose selectively to a target region and breaking its tissue is called radiosurgery, and the device developed for this purpose is the gamma knife. First, it was applied to functional diseases, but good results were obtained by its application to auditory nerve and brain blood vessels, and it establishes the position as the safe treatment method of the morbid state in the deep part of brains, which is difficult to reach by operation. Accompanying the recent progress of the operation of skull base part, attention is paid to its application to various tumors in skull base. On the other hand, the radiosurgery combining a cyclotron or a linear accelerator with stereotaxic brain surgery is actively tried mainly to the deformation of brain blood vessels. (K.I.)

  17. Quest for anionic MOF membranes: Continuous sod -ZMOF membrane with Co2 adsorption-driven selectivity

    KAUST Repository

    Almaythalony, Bassem

    2015-02-11

    We report the fabrication of the first continuous zeolite-like metal-organic framework (ZMOF) thin-film membrane. A pure phase sod-ZMOF, sodalite topology, membrane was grown and supported on a porous alumina substrate using a solvothermal crystallization method. The absence of pinhole defects in the film was confirmed and supported by the occurrence of quantifiable time-lags, for all studied gases, during constant volume/variable pressure permeation tests. For both pure and mixed gas feeds, the sod-ZMOF-1 membrane exhibits favorable permeation selectivity toward carbon dioxide over relevant industrial gases such as H2, N2, and CH4, and it is mainly governed by favorable CO2 adsorption.

  18. Decomposition of silica-alumina ores of Afghanistan by sulfuric acid

    International Nuclear Information System (INIS)

    Khomidi, A.K.; Mamatov, E.D.

    2016-01-01

    Present article is devoted to decomposition of silica-alumina ores of Afghanistan by sulfuric acid. Physicochemical properties of initial silica-alumina ores were studied by means of X-ray phase, differential thermal and silicate analysis. The influence of temperature, process duration and acid concentration on extraction rate of valuable components was considered. The optimal conditions of decomposition of silica-alumina ores of Afghanistan by sulfuric acid were proposed.

  19. Fabrication of a novel aluminum surface covered by numerous high-aspect-ratio anodic alumina nanofibers

    OpenAIRE

    Nakajima, Daiki; Kikuchi, Tatsuya; Natsui, Shungo; Sakaguchi, Norihito; Suzuki, Ryosuke O.

    2015-01-01

    The formation behavior of anodic alumina nanofibers via anodizing in a concentrated pyrophosphoric acid under various conditions was investigated using electrochemical measurements and SEM/TEM observations. Pyrophosphoric acid anodizing at 293 K resulted in the formation of numerous anodic alumina nanofibers on an aluminum substrate through a thin barrier oxide and honeycomb oxide with narrow walls. However, long-term anodizing led to the chemical dissolution of the alumina nanofibers. The de...

  20. Synthesis of Carbon Nanotube (CNT Composite Membranes

    Directory of Open Access Journals (Sweden)

    Dusan Losic

    2010-12-01

    Full Text Available Carbon nanotubes are attractive approach for designing of new membranes for advanced molecular separation because of their unique transport properties and ability to mimic biological protein channels. In this work the synthetic approach for fabrication of carbon nanotubes (CNTs composite membranes is presented. The method is based on growth of multi walled carbon nanotubes (MWCNT using chemical vapour deposition (CVD on the template of nanoporous alumina (PA membranes. The influence of experimental conditions including carbon precursor, temperature, deposition time, and PA template on CNT growth process and quality of fabricated membranes was investigated. The synthesis of CNT/PA composites with controllable nanotube dimensions such as diameters (30–150 nm, and thickness (5–100 µm, was demonstrated. The chemical composition and morphological characteristics of fabricated CNT/PA composite membranes were investigated by various characterisation techniques including scanning electron microscopy (SEM, energy-dispersive x-ray spectroscopy (EDXS, high resolution transmission electron microscopy (HRTEM and x-ray diffraction (XRD. Transport properties of prepared membranes were explored by diffusion of dye (Rose Bengal used as model of hydrophilic transport molecule.

  1. Investigation of self-powered gamma flux detectors with Lead(II) oxide serving as both emitter and insulator

    International Nuclear Information System (INIS)

    Shi, H.; Yue, S.; Jonkmans, G.; Sur, B.; Hilborn, J.

    2010-01-01

    The use of Lead(II) oxide as the electron-emitting component and the insulating component of self-powered flux detectors is a concept that had not been previously explored. Detectors constructed from various combinations of electrodes (stainless steel, Al, Pb, and W) and insulating materials (Al 2 O 3 and PbO) were irradiated in a 427 Gy/h gamma field. Although high gamma sensitivities were achieved, PbO did not prove to be a strong emitter of gamma-induced electrons. Nevertheless, PbO did serve as a better insulator than one that is currently in use, namely alumina. (author)

  2. Removal of Arsenic from Drinking Water Using Modified Activated Alumina

    Directory of Open Access Journals (Sweden)

    Mohammad Mosaferi

    2005-09-01

    Full Text Available Considering contamination of drinking water to arsenic in some villages ofIran. In order to develop a simple method for household water treatment in rural areas, efficiency of  modified activated alumina with iron compounds- a product of Alcan Company with trade name of AAFS-50- was studied Equilibrium batch experiments were carried out using shaker incubator and arsenic was analyzed with SDDC method. Effects of initial concentration of arsenic, adsorbent dose, oxidation state of arsenic, pH and oxidation with chlorine on adsorption were studied. Correlation coefficient of Freundlich and Laungmuier  isotherms  for As(V and As(III were 0.964 , 0.991 and 0.970, 0.978 respectively . These results show that adsorption of arsenic on modified activated alumina is compatible with both models specially Laungmuier models. Removal efficiency of As(V at 0.5 ,1 and 2 hr increased with doubling the adsorbent dose from 44.8 to 72%, 69.6 to 90.8 and 92.4 to 98% ; respectively. Experiments using different concentrations of arsenic showed that adsorption of arsenic on activated alumina are a first order reaction that is, rate of reaction is dependent on intial; concentration of arsenic. Removal efficiency for concentration of 0.250 mg/L of arsenic, with increasing of reaction time from 15 min to 60 min, increased 1.54 times and reached from 61% to 94%. During 2hrs, removal of As(V and As(III were 96% and 16% respectively. Using 1.5 mg/L Chlorine as oxidant agent, removal of As(III was increased to 94%. In the case of pH effect, rate of adsorption increased for arsenite, with increasing of pH to 8 and decreased with more increasing, so that adsorption at pH 14 was equal to pH 2. For arsenate, the most adsorption was observed at pH between 6 to 8 . These results show that by using the studied activated alumina, there will not be need for adjustment of pH and the activated alumina used in this study could have application as a safe adsorbent for removal of

  3. Laser-induced reaction alumina coating on ceramic composite

    Science.gov (United States)

    Xiao, Chenghe

    Silicon carbide ceramics are susceptible to corrosion by certain industrial furnace environments. It is also true for a new class of silicon carbide-particulate reinforced alumina-matrix composite (SiCsb(P)Alsb2Osb3) since it contains more than 55% of SiC particulate within the composite. This behavior would limit the use of SiCsb(P)Alsb2Osb3 composites in ceramic heat exchangers. Because oxide ceramics corrode substantially less in the same environments, a laser-induced reaction alumina coating technique has been developed for improving corrosion resistance of the SiCsb(P)Alsb2Osb3 composite. Specimens with and without the laser-induced reaction alumina coating were subjected to corrosion testing at 1200sp°C in an air atmosphere containing Nasb2COsb3 for 50 ˜ 200 hours. Corroded specimens were characterized via x-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive spectrometer (EDS). The uncoated SiCsbP/Alsb2Osb3 composite samples experienced an initial increase in weight during the exposure to Nasb2COsb3 at 1200sp°C due to the oxidation of residual aluminum metal in the composite. There was no significant weight change difference experienced during exposure times between 50 and 200 hours. The oxidation layer formed on the as-received composite surface consisted of Si and Alsb2Osb3 (after washing with a HF solution). The oxidation layer grew outward and inward from the original surface of the composite. The growth rate in the outward direction was faster than in the inward direction. The formation of the Si/Alsb2Osb3 oxidation layer on the as-received composite was nonuniform, and localized corrosion was observed. The coated samples experienced very little mass increase. The laser-induced reaction alumina coating effectively provided protection for the SiCsbP/Alsb2Osb3 composite by keeping the corrodents from contacting the composite and by the formation of some refractory compounds such as Nasb2OAlsb2Osb3SiOsb2 and Nasb2Alsb{22}Osb

  4. Viscosity of aqueous and cyanate ester suspensions containing alumina nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Lawler, Katherine [Iowa State Univ., Ames, IA (United States)

    2009-01-01

    The viscosities of both aqueous and cyanate ester monomer (BECy) based suspensions of alumina nanoparticle were studied. The applications for these suspensions are different: aqueous suspensions of alumina nanoparticles are used in the production of technical ceramics made by slip casting or tape casting, and the BECy based suspensions are being developed for use in an injection-type composite repair resin. In the case of aqueous suspensions, it is advantageous to achieve a high solids content with low viscosity in order to produce a high quality product. The addition of a dispersant is useful so that higher solids content suspensions can be used with lower viscosities. For BECy suspensions, the addition of nanoparticles to the BECy resin is expected to enhance the mechanical properties of the cured composite. The addition of saccharides to aqueous suspensions leads to viscosity reduction. Through DSC measurements it was found that the saccharide molecules formed a solution with water and this resulted in lowering the melting temperature of the free water according to classic freezing point depression. Saccharides also lowered the melting temperature of the bound water, but this followed a different rule. The shear thinning and melting behaviors of the suspensions were used to develop a model based on fractal-type agglomeration. It is believed that the structure of the particle flocs in these suspensions changes with the addition of saccharides which leads to the resultant viscosity decrease. The viscosity of the BECy suspensions increased with solids content, and the viscosity increase was greater than predicted by the classical Einstein equation for dilute suspensions. Instead, the Mooney equation fits the viscosity behavior well from 0-20 vol% solids. The viscosity reduction achieved at high particle loadings by the addition of benzoic acid was also investigated by NMR. It appears that the benzoic acid interacts with the surface of the alumina particle which may

  5. Reduction in Friction and Wear of Alumina Surfaces as Assisted with Surface-Adsorbing Polymers in Aqueous Solutions

    DEFF Research Database (Denmark)

    Røn, Troels; Lee, Seunghwan

    2016-01-01

    We have investigated the aqueous lubricating effects of various polymers for the sliding contacts of self-mated alumina surfaces in neutral aqueous environment. Given that isoelectric point (IEP) of alumina is ca. pH 9, polyanions can readily adsorb onto alumina surface at neutral pH via electros......We have investigated the aqueous lubricating effects of various polymers for the sliding contacts of self-mated alumina surfaces in neutral aqueous environment. Given that isoelectric point (IEP) of alumina is ca. pH 9, polyanions can readily adsorb onto alumina surface at neutral pH via...

  6. The effect of alumina nanofillers size and shape on mechanical behavior of PMMA matrix composite

    Directory of Open Access Journals (Sweden)

    Ben Hasan Somaya Ahmed

    2014-01-01

    Full Text Available Composites with the addition of alumina nanofillers show improvement in mechanical properties. The PMMA polymer was used as a matrix and two different types of nanofillers, having extremely different shapes were added in the matrix to form the composite. Reinforcements were based on alumina nanoparticles having either spherical shape or whiskers having the length to diameter ratio of 100. The influence of alumina fillers size, shape and fillers loading on mechanical properties of prepared composite were studied using the nanoindentation measurements and dynamic mechanical analysis. It was observed that both alumina whiskers and alumina spherical nanoparticles added in the PMMA matrix improved the mechanical properties of the composite but the improvement was significantly higher with alumina whisker reinforcement. The concentration of the reinforcing alumina spherical nanoparticles and alumina whiskers in PMMA matrix varied up to 5 wt. %. The best performance was obtained by the addition of 3 wt. % of alumina whiskers in the PMMA matrix with regard to mechanical properties of the obtained composite.

  7. Determination of calcium and magnesium in nuclear grade alumina by ion chromatography technique

    International Nuclear Information System (INIS)

    Hespanhol, E.C.B.; Pires, M.A.F.; Atalla, L.T.

    1987-07-01

    A simple method for solubilization of alumina and separation of magnesium and calcium from alumina matrix was developed by initial coprecipitation of those elements with iron(III) hydroxide. Calcium and magnesium were later separated from iron chloride anionic complex in a Dowex 1-X 10 anionic exchange resin. The ion chromatography tecnnique was employed for the analysis of calcium and magnesium. One hundred percent recovery for calcium and magnesium was obtained in their separation from alumina. A precision of 6% and 10% for magnesium and calcium, respectively, was obtained in alumina samples analysis which contain less than 0,02% of magnesium and less than 0,08% of calcium. (Author) [pt

  8. Fabrication of a novel aluminum surface covered by numerous high-aspect-ratio anodic alumina nanofibers

    Science.gov (United States)

    Nakajima, Daiki; Kikuchi, Tatsuya; Natsui, Shungo; Sakaguchi, Norihito; Suzuki, Ryosuke O.

    2015-11-01

    The formation behavior of anodic alumina nanofibers via anodizing in a concentrated pyrophosphoric acid under various conditions was investigated using electrochemical measurements and SEM/TEM observations. Pyrophosphoric acid anodizing at 293 K resulted in the formation of numerous anodic alumina nanofibers on an aluminum substrate through a thin barrier oxide and honeycomb oxide with narrow walls. However, long-term anodizing led to the chemical dissolution of the alumina nanofibers. The density of the anodic alumina nanofibers decreased as the applied voltage increased in the 10-75 V range. However, active electrochemical dissolution of the aluminum substrate occurred at a higher voltage of 90 V. Low temperature anodizing at 273 K resulted in the formation of long alumina nanofibers measuring several micrometers in length, even though a long processing time was required due to the low current density during the low temperature anodizing. In contrast, high temperature anodizing easily resulted in the formation and chemical dissolution of alumina nanofibers. The structural nanofeatures of the anodic alumina nanofibers were controlled by choosing of the appropriate electrochemical conditions, and numerous high-aspect-ratio alumina nanofibers (>100) can be successfully fabricated. The anodic alumina nanofibers consisted of a pure amorphous aluminum oxide without anions from the employed electrolyte.

  9. Surface area, crystal morphology and characterization of transition alumina powders from a new gibbsite precursor

    Directory of Open Access Journals (Sweden)

    Antonio Carlos Vieira Coelho

    2007-06-01

    Full Text Available A new procedure was used to prepare a microcrystalline powder constituted by thin euhedral hexagonal gibbsite plates, 0.2 to 0.6 µm in diameter and 32 nm thick. The powder, fired between 200 and 1000 °C, produced chi and kappa transition aluminas. Alpha-alumina is formed from 1000 °C and recrystallized up to 1500 °C. At 1000 °C, kappa- and alpha-alumina coexisted, but kappa-alumina could only be characterized by SAED. The details of the internal organization of the transition alumina pseudomorphs were clearly observable in TEM due to the great thinness of the I-gibbsite plates. The specific surface area varied from pristine I-gibbsite (24.9 m².g-1 to chi- and kappa transition aluminas (25.4 m².g-1 at 1000 °C to alpha-alumina (4.0 m².g-1 at 1500 °C. The maximum value of specific surface area is 347 m².g-1 in chi-alumina powder at 300 °C, a difference from Bayer gibbsite, in which the chi-alumina highest surface area is 370 m².g-1 at 400 °C.

  10. On the possibility of producing alumina ceramic with a slight electrical conductivity

    CERN Document Server

    Caspers, Fritz

    1989-01-01

    Antistatic alumina ceramic is desirable for certain particle accelerator applications. In general, highly insulating surface close to a charged particle beam must be avoided in order to prevent the formation of ion pockets and other unwanted electrical effects. For the AA vacuum chamber (UHV), an antistatic ferrite has been produced and successfully installed. The fabrication of antistatic alumina might be possible in a similar way. By using certain metal oxides in the cement, which holds the alumina particles together, a slight conductivity could be obtained after the firing and sintering process, without deteriorating the mechanical and outgassing properties of the alumina compound.

  11. CO2 Acquisition Membrane (CAM)

    Science.gov (United States)

    Mason, Larry W.; Way, J. Douglas; Vlasse, Marcus

    2003-01-01

    The objective of CAM is to develop, test, and analyze thin film membrane materials for separation and purification of carbon dioxide (CO2) from mixtures of gases, such as those found in the Martian atmosphere. The membranes are targeted toward In Situ Resource Utilization (ISRU) applications that will operate in extraterrestrial environments and support future unmanned and human space missions. A primary application is the Sabatier Electrolysis process that uses Mars atmosphere CO2 as raw material for producing water, oxygen, and methane for rocket fuel and habitat support. Other applications include use as an inlet filter to collect and concentrate Mars atmospheric argon and nitrogen gases for habitat pressurization, and to remove CO2 from breathing gases in Closed Environment Life Support Systems (CELSS). CAM membrane materials include crystalline faujasite (FAU) zeolite and rubbery polymers such as silicone rubber (PDMS) that have been shown in the literature and via molecular simulation to favor adsorption and permeation of CO2 over nitrogen and argon. Pure gas permeation tests using commercial PDMS membranes have shown that both CO2 permeance and the separation factor relative to other gases increase as the temperature decreases, and low (Delta)P(Sub CO2) favors higher separation factors. The ideal CO2/N2 separation factor increases from 7.5 to 17.5 as temperature decreases from 22 C to -30 C. For gas mixtures containing CO2, N2, and Ar, plasticization decreased the separation factors from 4.5 to 6 over the same temperature range. We currently synthesize and test our own Na(+) FAU zeolite membranes using standard formulations and secondary growth methods on porous alumina. Preliminary tests with a Na(+) FAU membrane at 22 C show a He/SF6 ideal separation factor of 62, exceeding the Knudsen diffusion selectivity by an order of magnitude. This shows that the membrane is relatively free from large defects and associated non-selective (viscous flow) transport

  12. Gamma camera

    International Nuclear Information System (INIS)

    Tschunt, E.; Platz, W.; Baer, U.; Heinz, L.

    1978-01-01

    A gamma camera has a plurality of exchangeable collimators, one of which is mounted in the ray inlet opening of the camera, while the others are placed on separate supports. The supports are swingably mounted upon a column one above the other through about 90 0 to a collimator exchange position. Each of the separate supports is swingable to a vertically aligned position, with limiting of the swinging movement and positioning of the support at the desired exchange position. The collimators are carried on the supports by means of a series of vertically disposed coil springs. Projections on the camera are movable from above into grooves of the collimator at the exchange position, whereupon the collimator is turned so that it is securely prevented from falling out of the camera head

  13. Functionalized inorganic membranes for gas separation

    Science.gov (United States)

    Ku, Anthony Yu-Chung [Rexford, NY; Ruud, James Anthony [Delmar, NY; Molaison, Jennifer Lynn [Marietta, GA; Schick, Louis Andrew ,; Ramaswamy, Vidya [Niskayuna, NY

    2008-07-08

    A porous membrane for separation of carbon dioxide from a fluid stream at a temperature higher than about 200.degree. C. with selectivity higher than Knudsen diffusion selectivity. The porous membrane comprises a porous support layer comprising alumina, silica, zirconia or stabilized zirconia; a porous separation layer comprising alumina, silica, zirconia or stabilized zirconia, and a functional layer comprising a ceramic oxide contactable with the fluid stream to preferentially transport carbon dioxide. In particular, the functional layer may be MgO, CaO, SrO, BaO, La.sub.2O.sub.3, CeO.sub.2, ATiO.sub.3, AZrO.sub.3, AAl.sub.2O.sub.4, A.sup.1FeO.sub.3, A.sup.1MnO.sub.3, A.sup.1CoO.sub.3, A.sup.1NiO.sub.3, A.sup.2HfO.sub.3, A.sup.3CeO.sub.3, Li.sub.2ZrO.sub.3, Li.sub.2SiO.sub.3, Li.sub.2TiO.sub.3 or a mixture thereof; wherein A is Mg, Ca, Sr or Ba; A.sup.1 is La, Ca, Sr or Ba; A.sup.2 is Ca, Sr or Ba; and A.sup.3 is Sr or Ba.

  14. Surface Modification of Ceramic Membranes with Thin-film Deposition Methods for Wastewater Treatment

    KAUST Repository

    Jahangir, Daniyal

    2017-12-01

    Membrane fouling, which is caused by deposition/adsorption of foulants on the surface or within membrane pores, still remains a bottleneck that hampers the widespread application of membrane bioreactor (MBR) technology for wastewater treatment. Recently membrane surface modification has proved to be a useful method in water/wastewater treatment to improve the surface hydrophilicity of membranes to obtain higher water fluxes and to reduce fouling. In this study, membrane modification was investigated by depositing a thin film of same thickness of TiO2 on the surface of an ultrafiltration alumina membrane. Various thin-film deposition (TFD) methods were employed, i.e. electron-beam evaporation, sputter and atomic layer deposition (ALD), and a comparative study of the methods was conducted to assess fouling inhibition performance in a lab-scale anaerobic MBR (AnMBR) fed with synthetic municipal wastewater. Thorough surface characterization of all modified membranes was carried out along with clean water permeability (CWP) tests and fouling behavior by bovine serum albumin (BSA) adsorption tests. The study showed better fouling inhibition performance of all modified membranes; however the effect varied due to different surface characteristics obtained by different deposition methods. As a result, ALD-modified membrane showed a superior status in terms of surface characteristics and fouling inhibition performance in AnMBR filtration tests. Hence ALD was determined to be the best TFD method for alumina membrane surface modification for this study. ALD-modified membranes were further characterized to determine an optimum thickness of TiO2-film by applying different ALD cycles. ALD treatment significantly improved the surface hydrophilicity of the unmodified membrane. Also ALD-TiO2 modification was observed to reduce the surface roughness of original alumina membrane, which in turn enhanced the anti-fouling properties of modified membranes. Finally, a same thickness of ALD

  15. PENGARUH PERBEDAAN SIFAT PENYANGGA ALUMINA TERHADAP SIFAT KATALIS HYDROTREATING BERBASIS NIKEL-MOLIBDENUM

    Directory of Open Access Journals (Sweden)

    Maria Ulfah

    2012-11-01

    Full Text Available EFFECT OF ALUMINA SUPPORT PROPERTIES ON THE NICKEL-MOLIBDENUM BASE HYDROTREATING CATALYST. Effect of surface characteristics of three species of synthesized γ-alumina (alumina-1, alumina-2 and alumina-3 on characteristics NiMo catalysts has been studied. Those aluminas are derived from boehmite Catapal B by varying rasio mol nitric acid to boehmite. A sol-gel method is used to synthesize γ-Al2O3 support. The Nitrogen adsorption, X-ray diffraction (XRD, Temperature Programmed Reduction (TPR of H2, Temperature Programmed Desorption (TPD of NH3, and mechanical strength are used to characterize the supports and catalysts. The results showed that the surface area alumina affects the formation of crystalline MoO3 in the NiMo catalyst, while γ-Al2O3-3 support which has the highest surface area (about 195 m2/g compared to the other two types of alumina (>195 m2/g does not have a crystalline MoO3. The formation of crystalline MoO3 is not influenced by the acidity alumina. Based on the results of XRD, it is  indicated that the supported alumina-3 NiMo catalyst (having the highest acid strength shows that there is no presence of crystalline MoO3. Pore size distribution of support did not change significantly after the deposition of Ni and Mo oxides. Mechanical strength of support also affects the strength NiMo catalyst. Support alumina-3 which has the highest mechanical strength gives the mechanical strength of the highest NiMo catalyst. Pengaruh sifat penyangga γ-alumina hasil pengembangan (alumina-1, alumina-2 dan alumina-3 pada karakter katalis hydrotreating nikel-molibdenum (NiMo telah dipelajari. Ketiga jenis γ-alumina diturunkan dari boehmite “Catapal B” dengan menvariasikan nisbah mol asam nitrat terhadap boehmite. Pembuatan γ-alumina menggunakan metoda sol-gel. Adsorpsi Nitrogen, X-ray difraksi (XRD, Temperature Programmed Reduction (TPR H2, Temperature Programmed Desorption (TPD NH3, dan kekuatan mekanik digunakan untuk

  16. Membrane paradigm

    International Nuclear Information System (INIS)

    Price, R.H.; Thorne, K.S.

    1986-01-01

    The membrane paradigm is a modified frozen star approach to modeling black holes, with particles and fields assuming a complex, static, boundary-layer type structure (membrane) near the event horizon. The membrane has no effects on the present or future evolution of particles and fields above itself. The mathematical representation is a combination of a formalism containing terms for the shear and bulk viscosity, surface pressure, momentum, temperature, entropy, etc., of the horizon and the 3+1 formalism. The latter model considers a family of three-dimensional spacelike hypersurfaces in one-dimensional time. The membrane model considers a magnetic field threading the hole and undergoing torque from the hole rotation. The field is cleaned by the horizon and distributed over the horizon so that ohmic dissipation is minimized. The membrane paradigm is invalid inside the horizon, but is useful for theoretically probing the properties of slowly evolving black holes

  17. Membrane processes

    Science.gov (United States)

    Staszak, Katarzyna

    2017-11-01

    The membrane processes have played important role in the industrial separation process. These technologies can be found in all industrial areas such as food, beverages, metallurgy, pulp and paper, textile, pharmaceutical, automotive, biotechnology and chemical industry, as well as in water treatment for domestic and industrial application. Although these processes are known since twentieth century, there are still many studies that focus on the testing of new membranes' materials and determining of conditions for optimal selectivity, i. e. the optimum transmembrane pressure (TMP) or permeate flux to minimize fouling. Moreover the researchers proposed some calculation methods to predict the membrane processes properties. In this article, the laboratory scale experiments of membrane separation techniques, as well their validation by calculation methods are presented. Because membrane is the "heart" of the process, experimental and computational methods for its characterization are also described.

  18. Mechanical stability of heat-treated nanoporous anodic alumina subjected to repetitive mechanical deformation

    Science.gov (United States)

    Bankova, A.; Videkov, V.; Tzaneva, B.; Mitov, M.

    2018-03-01

    We report studies on the mechanical response and deformation behavior of heat-treated nanoporous anodic alumina using a micro-balance test and experimental test equipment especially designed for this purpose. AAO samples were characterized mechanically by a three-point bending test using a micro-analytical balance. The deformation behavior was studied by repetitive mechanical bending of the AAO membranes using an electronically controlled system. The nanoporous AAO structures were prepared electrochemically from Al sheet substrates using a two-step anodizing technique in oxalic acid followed by heat treatment at 700 °C in air. The morphological study of the aluminum oxide layer after the mechanical tests and mechanical deformation was conducted using scanning electron and optical microscopy, respectively. The experimental results showed that the techniques proposed are simple and accurate; they could, therefore, be combined to constitute a method for mechanical stability assessment of nanostructured AAO films, which are important structural components in the design of MEMS devices and sensors.

  19. Aging time on the aluminum basic acetate gel and its influence on the membrane permeability

    International Nuclear Information System (INIS)

    Clar, C; Scian, A. N; Aglietti, E.F

    2003-01-01

    Alumina ceramic membranes are new materials with important applications in separation processes with low energy requirements, high selectivity and ability to work at high and low temperatures.The preparation of alumina ceramic membranes from hydrates or aluminum salts as precursors implies obtaining a system of controlled porosity with a suitable mechanical resistance as well as the densification of the material thanks to the stable phases remaining after the thermal treatment.The metal carboxylates are potential precursors for the deposition and the subsequent formation of oxides at low temperatures.Aluminum basic acetate gel was synthesised in this work from commercial pseudobohemite. The influence of the aging time on the composition, crystalline structure and transition temperatures of the phases on the carboxylate was studied by XRD and DTA-TG.From suspensions of this aged gel at different times alumina ceramic membranes were prepared by dipcoating on different α-Al 2 O 3 supports and the influence of aging on the permeability of those membranes face to N 2 was also studied. It was observed that this is a parameter to be considered as it determines the thickness, permeability and integrity of the membranes

  20. Recovery of homogeneous polyoxometallate catalysts from aqueous and organic media by a mesoporous ceramic membrane without loss of catalytic activity

    NARCIS (Netherlands)

    Roy Chowdhury, S.; Roy Chowdhury, Sankhanilay; Witte, Peter T.; Blank, David H.A.; Alsters, Paul L.; ten Elshof, Johan E.

    2006-01-01

    The recovery of homogeneous polyoxometallate (POM) oxidation catalysts from aqueous and non-aqueous media by a nanofiltration process using mesoporous γ-alumina membranes is reported. The recovery of Q12[WZn3(ZnW9O34)2] (Q=[MeN(n-C8H17)3]+) from toluene-based media was quantitative within

  1. Microwave sintering of zirconia toughened alumina at 28GHz

    International Nuclear Information System (INIS)

    Samandi, M.; Ji, H.; Miyake, S.

    1998-01-01

    Microwave radiation from a 10 kW, CW gyrotron operating at 28 GHz was employed to sinter 10% zirconia toughened alumina (ZTA) ceramic samples. It has been established that the use of millimetre wave radiation circumvents the difficulties encountered during the sintering of ceramics, i e. formation of hot spot, by radiation at industrially permissible frequency of 2.45GHz. Further, careful density measurement and microstructural characterisation of mm- wave and conventionally sintered samples by XRD, SEM and TEM has unequivocally demonstrated the effectiveness of mm-wave radiation for obtaining high density ceramics at lower sintering temperatures. Copyright (1998) Australasian Ceramic Society

  2. Techniques for detection of transition phases in calcined alumina

    International Nuclear Information System (INIS)

    Pandolfelli, V.C.; Folgueras-Dominguez, S.

    1987-01-01

    Detection of transition phases in alumina, is very important in the receiving control and calcination of aluminium hydroxide. The non alfa or transition phases difficults the processability and causes localized shrinkage on sintering compromising the dimensional and mechanical aspects of the product. In this research using refraction index, absorption of dyes, specific density, X-ray diffraction and scanning electron microscopy, analyses, are done in calcined hydroxides submited to different thermal treatments. The limits and facilities of each technique are discussed and compared. (Author) [pt

  3. Liquid-film assisted formation of alumina/niobium interfaces

    OpenAIRE

    Sugar, Joshua D.; McKeown, Joseph T.; Marks, Robert A.; Glaeser, Andreas M.

    2002-01-01

    Alumina has been joined at 1400 degrees C using niobium-based interlayers. Two different joining approaches were compared: solid-state diffusion bonding using a niobium foil as an interlayer, and liquid-film assisted bonding using a multilayer copper/niobium/copper interlayer. In both cases, a 127-(mu)m thick niobium foil was used; =1.4-(mu)m or =3-(mu)m thick copper films flanked the niobium. Room-temperature four-point bend tests showed that the introduction of a copper film had a significa...

  4. Electrochemically replicated smooth aluminum foils for anodic alumina nanochannel arrays

    International Nuclear Information System (INIS)

    Biring, Sajal; Tsai, K-T; Sur, Ujjal Kumar; Wang, Y-L

    2008-01-01

    A fast electrochemical replication technique has been developed to fabricate large-scale ultra-smooth aluminum foils by exploiting readily available large-scale smooth silicon wafers as the masters. Since the adhesion of aluminum on silicon depends on the time of surface pretreatment in water, it is possible to either detach the replicated aluminum from the silicon master without damaging the replicated aluminum and master or integrate the aluminum film to the silicon substrate. Replicated ultra-smooth aluminum foils are used for the growth of both self-organized and lithographically guided long-range ordered arrays of anodic alumina nanochannels without any polishing pretreatment

  5. Adhesion of silver films to ion-bombarded alumina

    International Nuclear Information System (INIS)

    Erck, R.A.; Fenske, G.R.

    1990-01-01

    This paper reports on silver films deposited on alumina substrates using ion bombardment. Adhesion strength was measured as a function of deposition conditions, sputter-cleaning time, and bombarding ion species, using a pull-type adhesion tester. Argon- and argon/oxygen-ion sputtering produced large increases in adhesion strength, with the greatest increases occurring for oxygen-ion bombardment. Adhesion strength increased monotonically as a function of ion sputtering time. At a given deposition rate, further enhancement of adhesion is seen with concurrent ion bombardment

  6. Diffusion and flow of water vapours in chromatographic Alumina gel

    International Nuclear Information System (INIS)

    Khan, M.; Shah, H. U.

    2005-01-01

    The kinetics of sorption of water vapours in chromatographic alumina gel was studied. Water vapours are adsorbed on the gel at temperature (15 degree C) at different constant relative pressure from 0.1-0.93 p/p. Rate constant, Effective diffusivities, Knudsen diffusivities and bulk diffusivities were determined through Fick type equation. Total pore volume is 0.498 cc g-1 and specific surface area comes to be 465 m2 g-1 as obtained by Gurvitsch rule and Kieselve's quantities respectively. An average pore radius (hydraulic) is 1.1x10/sub -7/ cm. The study of these quantities provide a strong basis for evaluating surface properties. (author)

  7. Thermal diffusivity of alumina-zirconia sintered with niobium additions

    International Nuclear Information System (INIS)

    Santos, W.N. dos; Paulin Filho, P.I.; Taylor, R.

    1994-01-01

    The effect of niobium oxide addition on the alumina-zirconia thermal diffusivity was investigated from 100 0 C to 1000 0 C by the laser flash method. It was observed that 4 to 6% addition of niobium oxide increases the thermal diffusivity when samples were sintered at 1450 0 C. This effect was due to elimination of porosity by formation of liquid please above 1420 0 C in the Al 2 O 3 - Nb 2 O 5 system. (author). 7 refs., 3 figs

  8. Preparation of 11C-labelled methanol on alumina column

    International Nuclear Information System (INIS)

    Sarkadi, E.; Kovacs, Z.; Horvath, G.

    1998-01-01

    The [ 11 C]methyl iodide is an important intermedia to synthesize 11 C-labelled radiopharmaceuticals for medical diagnostics in positron emission tomography. Recently a new method has been developed to produce [ 11 C]methanol intermedia. The advantage of this method of radiomethanol preparation is the application of an alumina column at room temperature instead of a complicated cooling unit used with the conventional reaction vessel. The yield and purity of radiomethanol was the same as in the previous methods. (K.A.)

  9. Primordial membranes

    DEFF Research Database (Denmark)

    Hanczyc, Martin M; Monnard, Pierre-Alain

    2017-01-01

    Cellular membranes, which are self-assembled bilayer structures mainly composed of lipids, proteins and conjugated polysaccharides, are the defining feature of cell physiology. It is likely that the complexity of contemporary cells was preceded by simpler chemical systems or protocells during...... the various evolutionary stages that led from inanimate to living matter. It is also likely that primitive membranes played a similar role in protocell 'physiology'. The composition of such ancestral membranes has been proposed as mixtures of single hydrocarbon chain amphiphiles, which are simpler versions...

  10. Ferromagnetic resonance investigation in permalloy magnetic antidot arrays on alumina nanoporous membranes

    Energy Technology Data Exchange (ETDEWEB)

    Rodríguez-Suárez, R.L., E-mail: rrodriguez@fis.puc.cl [Facultad de Física, Pontificia Universidad Católica de Chile, Av. Vicuña Mackenna 4860 Casilla 306, Santiago (Chile); Palma, J.L.; Burgos, E.O. [Departamento de Física, Universidad de Santiago de Chile (USACH), Avda. Ecuador 3493, 917-0124 Santiago (Chile); Michea, S. [Facultad de Física, Pontificia Universidad Católica de Chile, Av. Vicuña Mackenna 4860 Casilla 306, Santiago (Chile); Departamento de Física, Universidad de Santiago de Chile (USACH), Avda. Ecuador 3493, 917-0124 Santiago (Chile); Escrig, J.; Denardin, J.C. [Departamento de Física, Universidad de Santiago de Chile (USACH), Avda. Ecuador 3493, 917-0124 Santiago (Chile); Center for the Development of Nanoscience and Nanotechnology (CEDENNA), Avda. Ecuador 3493, 917-0124 Santiago (Chile); Aliaga, C. [Center for the Development of Nanoscience and Nanotechnology (CEDENNA), Avda. Ecuador 3493, 917-0124 Santiago (Chile); Facultad de Química y Biología, Universidad de Santiago de Chile, Casilla 40, Correo 33, Santiago (Chile)

    2014-01-15

    The magnetic properties of Ni{sub 80}Fe{sub 20} antidot arrays with hole diameters of 18 and 70 nm fabricated by a template-assisted method were investigated using the ferromagnetic resonance technique. Tuning the antidot arrays by changing the hole diameter enables control on the angular dependence of the ferromagnetic resonance field. The scanning electron microscope images reveal a quite regular hexagonal arrangement of the pores, however the angular dependence of the resonance field do not exhibit the six-fold symmetry expected for this symmetry. Micromagnetic simulations performed on a perfect hexagonal lattice, when compared with those made on our real system taken from the scanning microscope images, reveal that the presence of defects in the antidot lattice affects the ferromagnetic resonance field symmetry. - Highlights: • We use the FMR technique to investigate the magnetic properties of Py antidots. • We studied the effect of pore diameter on FMR angular measurement. • FMR field does not exhibit the six-fold symmetry. • For all angular positions there are two resonance modes always present. • Micromagnetic simulations agree with the experimental results with defects.

  11. Development of tungsten coatings for the corrosion protection of alumina-based ceramics

    International Nuclear Information System (INIS)

    Arons, R.M.; Dusek, J.T.; Hafstrom, J.W.

    1979-01-01

    A means of applying tungsten coatings to an alumina based ceramic is described. A slurry of pure tungsten was prepared and applied by brush coating or slip casting on the alumina-3 wt % Yt small crucible. The composite was fired and a very dense ceramic crucible with a crack free tungsten coating was produced

  12. A High-Purity Alumina for Use in Studies of Shock Loaded Samples

    Science.gov (United States)

    Lacina, David; Neel, Christopher

    2017-06-01

    We report the results of plate impact experiments on a potential new ``standard'' material, Coorstek Plasmapure-UC (99.9% purity) polycrystalline alumina, for use in non-conduction, impact environment, shock loading studies. This work was motivated by a desire to find a 99.9% purity alumina to replace the now unavailable Coors Vistal (99.9%) alumina, as it was hoped the Hugoniot elastic limit (HEL) of the new standard would match the 9-11 GPa value of Vistal. Shock response data, including the HEL, Hugoniot particle velocities, Hugoniot shock velocities, stress vs volume, and release wave speeds, was obtained up to 14 GPa. This data will be compared with Hugoniot curve data for other high purity alumina to contrast differences in the shock response, and is intended to be useful in impedance matching calculations. We will show that the HEL of Plasmapure-UC alumina is 5.5 GPa and speculate on causes for this lower than expected value. We will also explore why the elastic-plastic response for Plasmapure-UC alumina differs from what has been observed from other high purity alumina. The final result of this work is to recommend a well-characterized, lower purity alumina (Coorstek AD-995) as a potential new ``standard'' material.

  13. Comparative evaluation of alumina powders obtained from different routes for engineering applications

    International Nuclear Information System (INIS)

    Page, C.H.; Chatterjee, A.K.

    1991-01-01

    Alumina, the most versatile and widely used refractory ceramic oxide, has currently occupied the position of the most preferred material in engineering ceramic industry. Though limited to some extent, the experience so far has been that the selection of an inappropriat high alumina ceramic can lead to cost penalties and poor performance in service. With this in view, one of the studies undertaken at the research laboratories of The Associated Cement Cos.Ldt. (India) has been to synthesise alumina powders by various process routes and to compare their physico-mechanical, thermal, textural and microstructural characteristics so as to understand the effects emanating from the powder synthesis processes on the performance properties of alumina. Following this approach, the present paper deals with aluminas obtained from four process routes, viz. Sol-Gel, Controlled Precipitation, Pyrolysis and Aluminium salts and conventional alumina obtained by calcination of gibbsite. The properties of these four varieties of alumina are characterised with respect to chemical analysis, particle size, textural features, grindability, etc. Behaviour of these powders in green processing/shaping particularly in terms of compaction, density, binder requirements, etc. have been studied. The calcination characteristics as reflected in shrinkage, densification and crystal morphology have been examined. Finally, the physical and thermal properties of Aluminas obtained from various synthesis routes and their co-relation with various powder characteristics and compact microstrcture have been dealt with. (orig.)

  14. Morphology and thermal properties of compatibilized PA12/PP blends with boehmite alumina nanofiller inclusions

    CSIR Research Space (South Africa)

    Ogunniran, ES

    2011-12-01

    Full Text Available -1 Morphology and Thermal Properties of Compatibilized PA12/PP Blends with Boehmite Alumina Nanofiller Inclusions 1. Elijah Soba Ogunniran1, 2. Rotimi Sadiku1, 3. Suprakas Sinha Ray2,*, 4. Nyambeni Luruli3 Keywords: ? boehmite alumina; ? morphology...

  15. All cause mortality and incidence of cancer in workers in bauxite mines and alumina refineries

    NARCIS (Netherlands)

    Fritschi, Lin; Hoving, Jan Lucas; Sim, Malcolm R.; del Monaco, Anthony; Macfarlane, Ewan; McKenzie, Dean; Benke, Geza; de Klerk, Nicholas

    2008-01-01

    Bauxite is a reddish clay that is refined to produce alumina, which is then reduced to aluminium. There have been studies examining the health of workers in aluminium smelters, but not workers in bauxite mining and alumina refining. A cohort of employees of 1 large aluminium company since 1983 was

  16. Phase transformation of aluminium hydroxide to aα- alumina prepared from different aluminium salts

    International Nuclear Information System (INIS)

    Masliana Muslimin; Meor Yusoff Meor Sulaiman

    2006-01-01

    The study intends to look at the most suitable aluminium salt to produce a single-phase a-alumina by the hydrothermal method. In the process to produce alumina from the calcination of aluminium hydroxide (Al(OH) 3 ), three different aluminium salts namely aluminium sulfate (Al 2 (SO 4) 2), aluminium nitrate (A(NO 3 ) 3 ) and aluminium chloride (AlCl 3 ) were tried. The process involved the used of NH 4 OH as the precipitating medium. Aluminium hydroxide produced from each of these salts were characterised by x-ray diffraction (XRD) technique to identity the crystalline phase. Aluminium hydroxide produced by all the different aluminium salts is present as boehmite or pseudo-boehmite phase. Aluminium hydroxide produced from Al 2 (SO) 2 , Al(NO) 3 and AlCl 3 shows the transformation of the boehmite phase to a α-alumina phase at 500 0 C. On further heating, the α-alumina continuously formed at 800 o C followed soon at 1000 o C. But for the Al(NO3) 3 salts a different phase transitions occurs on heating especially at 1000 o C. Here it was observed not a single alumina phase is presence but the presence of both α and γ--alumina phases. At 1300 o C, the single α-alumina phase was formed. The study concluded that aluminium sulphate is recommended in order to obtain a single-phase α-alumina with the required characteristics. (Author)

  17. Studies on the promotion of nickel—alumina coprecipitated catalysts: I. Titanium oxide

    NARCIS (Netherlands)

    Lansink Rotgerink, H.G.J.; Mercera, P.D.L.; van Ommen, J.G.; Ross, J.R.H.

    1988-01-01

    A series of TiO2-promoted nickel—alumina catalysts has been prepared and characterized. The promoter was added in various proportions to a calcined coprecipitated nickel—alumina material by adsorption of the acetylacetonate complex of titanium, followed by further calcination and reduction. The

  18. Modification of alumina matrices through chemical etching and electroless deposition of nano-Au array for amperometric sensing

    Directory of Open Access Journals (Sweden)

    Valinčius Gintaras

    2007-01-01

    Full Text Available AbstractSimple nanoporous alumina matrix modification procedure, in which the electrically highly insulating alumina barrier layer at the bottom of the pores is replaced with the conductive layer of the gold beds, was described. This modification makes possible the direct electron exchange between the underlying aluminum support and the redox species encapsulated in the alumina pores, thus, providing the generic platform for the nanoporous alumina sensors (biosensors with the direct amperometric signal readout fabrication.

  19. Gamma camera

    International Nuclear Information System (INIS)

    Conrad, B.; Heinzelmann, K.G.

    1975-01-01

    A gamma camera is described which obviates the distortion of locating signals generally caused by the varied light conductive capacities of the light conductors in that the flow of light through each light conductor may be varied by means of a shutter. A balancing of the flow of light through each of the individual light conductors, in effect, collective light conductors may be balanced on the basis of their light conductive capacities or properties, so as to preclude a distortion of the locating signals caused by the varied light conductive properties of the light conductors. Each light conductor has associated therewith two, relative to each other, independently adjustable shutters, of which one forms a closure member and the other an adjusting shutter. In this embodiment of the invention it is thus possible to block all of the light conductors leading to a photoelectric transducer, with the exception of those light conductors which are to be balanced. The balancing of the individual light conductors may then be obtained on the basis of the output signals of the photoelectric transducer. (auth)

  20. High quality bio-oil from catalytic flash pyrolysis of lignocellulosic biomass over alumina-supported sodium carbonate

    KAUST Repository

    Imran, Ali

    2014-11-01

    Performance of a novel alumina-supported sodium carbonate catalyst was studied to produce a valuable bio-oil from catalytic flash pyrolysis of lignocellulosic biomass. Post treatment of biomass pyrolysis vapor was investigated in a catalyst fixed bed reactor at the downstream of the pyrolysis reactor. In-situ catalytic upgrading of biomass pyrolysis vapor was conducted in an entrained flow pyrolysis reactor by feeding a premixed feedstock of the catalyst and biomass. Na2CO3/gamma-Al2O3 was very effective for de-oxygenation of the pyrolysis liquid and oxygen content of the bio-oil was decreased from 47.5 wt.% to 16.4 wt.%. An organic rich bio-oil was obtained with 5.8 wt.% water content and a higher heating value of 36.1 MJ/kg. Carboxylic acids were completely removed and the bio-oil had almost a neutral pH. This bio-oil of high calorific low, low water and oxygen content may be an attractive fuel precursor. In-situ catalytic upgrading of biomass pyrolysis vapor produced a very similar quality bio-oil compared to post treatment of pyrolysis vapors, and shows the possible application of Na2CO3/gamma-Al2O3 in a commercial type reactor system such as a fluidized bed reactor. (C) 2014 Elsevier B.V. All rights reserved.

  1. Gamma ray generator

    Science.gov (United States)

    Firestone, Richard B; Reijonen, Jani

    2014-05-27

    An embodiment of a gamma ray generator includes a neutron generator and a moderator. The moderator is coupled to the neutron generator. The moderator includes a neutron capture material. In operation, the neutron generator produces neutrons and the neutron capture material captures at least some of the neutrons to produces gamma rays. An application of the gamma ray generator is as a source of gamma rays for calibration of gamma ray detectors.

  2. Measurement of the gamma field around Silene reactor

    International Nuclear Information System (INIS)

    Spurny, Frantisek; Medioni, Roger.

    1976-07-01

    A method for measuring the gamma component in the mixed field emitted by the Silene facility implanted in Valduc is investigated. Various thermoluminescent phosphors (natural LiF, 7 LiF, SO 4 Ca, Al 2 O 3 ) in containers of different sizes and types are used. The detectors results are corrected for their neutron sensitivity by using coefficients which were determined in previous studies. Alumina is shown to be the most suitable detector for this problem because of the dose ranges to be measured and its low sensitivity to neutrons. A series of measurements carried out at many points in the irradiation hall shows a good homogeneity in the gamma distribution. Results are given for different distances from the source and for a 10 17 fissions power of the reactor [fr

  3. Membranous nephropathy

    Science.gov (United States)

    ... skin-lightening creams Systemic lupus erythematosus , rheumatoid arthritis, Graves disease, and other autoimmune disorders The disorder occurs at ... diagnosis. The following tests can help determine the cause of membranous nephropathy: Antinuclear antibodies test Anti-double- ...

  4. Protein adsorption on low temperature alpha alumina films for surgical instruments

    Energy Technology Data Exchange (ETDEWEB)

    Cloud, A.N., E-mail: acloud@uark.ed [University of Arkansas, Fayetteville, AR 72701 (United States); Kumar, S. [Ian Wark Research Institute, University of South Australia, Mawson Lakes, Adelaide, SA 5095 (Australia); Kavdia, M.; Abu-Safe, H.H.; Gordon, M.H. [University of Arkansas, Fayetteville, AR 72701 (United States)

    2009-08-31

    Bulk alumina has been shown to exhibit reduced protein adsorption, a property that can be exploited for developing alumina-coated surgical instruments and devices. Alpha alumina thin films were deposited on surgical stainless steel substrates to investigate the adsorption of a model protein (BSA, bovine serum albumin). The films were deposited at 480 {sup o}C by AC inverted cylindrical magnetron sputtering. Films were obtained at 6 kW and 50% oxygen partial pressure by volume. The presence of alpha-phase alumina has been shown by transmission electron microscopy. Results indicate that there was a 50% reduction in protein adsorption for samples with the alumina coating compared to those with no coating.

  5. Study of preparation and surface morphology of self-ordered nanoporous alumina

    International Nuclear Information System (INIS)

    Rodrigues, Elisa Marchezini; Martins, Maximiliano Delany; Silva, Ronald Arreguy

    2013-01-01

    Nanoporous alumina is a typical material that exhibits self-ordered nanochannels spontaneously organized in hexagonal shape. Produced by anodizing of metallic aluminum, it has been used as a template for production of materials at the nanoscale. This work aimed to study the preparation of nanoporous alumina by anodic anodizing of metallic aluminum substrates. The nanoporous alumina was prepared following the methodology proposed by Masuda and Fukuda (1995), a two-step method consisting of anodizing the aluminum sample in the potentiostatic mode, removing the layer of aluminum oxide (alumina) formed and then repeat the anodization process under the same conditions as the first anodization. This method produces nanoporous alumina with narrow pore diameter distribution and well-ordered structure. (author)

  6. Mesoporous Alumina Microfibers In Situ Transformation from AACH Fibers and the Adsorption Performance

    Directory of Open Access Journals (Sweden)

    Xiaoqin Shi

    2014-01-01

    Full Text Available Well-dispersed mesoporous γ-alumina microfibers with high surface were prepared by thermal decomposition of the ammonium aluminum carbonate hydroxide (AACH precursors. The as-synthesized alumina retained the morphology of its precursor and exhibited memory effect. The structural, morphological, porous, and adsorptive properties of the samples were investigated by XRD, FTIR, TGA-DSC, SEM, TEM, and UV-vis spectroscopy. The prepared γ-alumina microfibers exhibited excellent ability to remove organic pollutants from waste water because of their mesoporous structures. The γ-alumina in situ converted from AACH synthesized without surfactant exhibited adsorption ability for Congo red as good as that synthesized with PEG2000 and better than PEG20000 that provided a facile method without surfactant to synthesize γ-alumina with excellent adsorption performance.

  7. Porous alumina scaffold produced by sol-gel combined polymeric sponge method

    Science.gov (United States)

    Hasmaliza, M.; Fazliah, M. N.; Shafinaz, R. J.

    2012-09-01

    Sol gel is a novel method used to produce high purity alumina with nanometric scale. In this study, three-dimensional porous alumina scaffold was produced using sol-gel polymeric sponge method. Briefly, sol gel alumina was prepared by evaporation and polymeric sponge cut to designated sizes were immersed in the sol gel followed by sintering at 1250 and 1550°C. In order to study the cell interaction, the porous alumina scaffold was sterilized using autoclave prior to Human Mesenchymal Stem Cells (HMSCs) seeding on the scaffold and the cell proliferation was assessed by alamarBlue® assay. SEM results showed that during the 21 day period, HMSCs were able to attach on the scaffold surface and the interconnecting pores while maintaining its proliferation. These findings suggested the potential use of the porous alumina produced as a scaffold for implantation procedure.

  8. High toughness alumina/aluminate: The role of hetero-interfaces

    International Nuclear Information System (INIS)

    Brito, M.E.; Yasuoka, M.; Kanzaki, S.

    1996-01-01

    Silica doped alumina/aluminate materials present a combination of high strength and high toughness not achieved before in other alumina systems, except for transformation toughened alumina. The authors have associated the increase in toughness to crack bridging by anisotropically grown alumina grains with concurrent interfacial debonding of these grains. A HREM study of grain boundaries and hetero-interface structures in this material shows the absence of amorphous phases at grain boundaries. Local Auger electron analysis of fractured surfaces revealed the coexistence of Si and La at the grain facets exposed by the noticeable intergranular fracture mode of this material. It is concluded that a certain and important degree of boundaries weakness is related to both presence of Si at the interfaces and existence of alumina/aluminate hetero-interfaces

  9. Bauxite mining and alumina refining: process description and occupational health risks.

    Science.gov (United States)

    Donoghue, A Michael; Frisch, Neale; Olney, David

    2014-05-01

    To describe bauxite mining and alumina refining processes and to outline the relevant physical, chemical, biological, ergonomic, and psychosocial health risks. Review article. The most important risks relate to noise, ergonomics, trauma, and caustic soda splashes of the skin/eyes. Other risks of note relate to fatigue, heat, and solar ultraviolet and for some operations tropical diseases, venomous/dangerous animals, and remote locations. Exposures to bauxite dust, alumina dust, and caustic mist in contemporary best-practice bauxite mining and alumina refining operations have not been demonstrated to be associated with clinically significant decrements in lung function. Exposures to bauxite dust and alumina dust at such operations are also not associated with the incidence of cancer. A range of occupational health risks in bauxite mining and alumina refining require the maintenance of effective control measures.

  10. A comparison of alumina, carbon and carbon-covered alumina as support for Ni-Mo-F additives: gas oil hydroprocessing studies

    Energy Technology Data Exchange (ETDEWEB)

    Boorman, P.M.; Kydd, R.A.; Sorensen, T.S.; Chong, K.; Lewis, J.M.; Bell, W.S. (University of Calgary, Calgary, AB (Canada). Dept. of Chemistry)

    1991-01-01

    Catalysts with 3 wt% NiO, 15 wt% MoO{sub 3} and 0-6.9 nominal wt% fluoride supported on alumina, carbon and carbon-covered alumina were studied to examine the role of fluoride and the influence of the support on hydroprocessing on Alberta gas oil. Experiments were carried out in a batch reactor at 410{degree}C and 6.9 MPa initial H{sub 2} pressure. It was found that fluoride promotion enhances cracking and hydrogenation reactions resulting in decreased aromatic and sulphur contents in the gas oil. The promotion is dependent on the type of support and is related to the strength of the fluoride-support interaction and the accessibility of the fluoride to the surface hydroxyl groups on the support. A maximum in activity at 3.6 wt% fluoride was observed for the alumina-supported catalysts whereas higher loadings of fluoride were required for carbon-covered alumina-supported catalysts to see an improvement over their carbon-supported counterparts. However, the carbon-covered alumina-supported catalysts seem to have a lower propensity for coke deposition than their alumina counterparts. 27 refs., 1 fig., 4 tabs.

  11. A comparison of alumina, carbon and carbon-covered alumina as supports for Ni-Mo-F additives: gas oil hydroprocessing studies

    Energy Technology Data Exchange (ETDEWEB)

    Boorman, P.M.; Kydd, R.A.; Sorensen, T.S.; Chong, K.; Lewis, J.M.; Bell, W.S. (Calgary Univ., AB (Canada). Dept. of Chemistry)

    1992-01-01

    Catalysts with 3 wt% NiO, 15 wt% MoO{sub 3} and 0-6.9 nominal wt% fluoride supported on alumina, carbon and carbon-covered alumina were studied to examine the role of fluoride and the influence of the support on hydroprocessing on Alberta gas oil. Experiments were carried out in a batch reactor at 410{sup o}C and 6.9 MPa initial H{sub 2} pressure. It was found that fluoride promotion enhances cracking and hydrogenation reactions resulting in decreased aromatic and sulphur contents in the gas oil. The promotion is dependent on the type of support and is related to the strength of the fluoride-support interaction and the accessibility of the fluoride to the surface hydroxyl groups on the support. A maximum in activity at 3.6 wt% fluoride was observed for the alumina-supported catalysts whereas higher loadings of fluoride were required for carbon-covered alumina-supported catalysts to see an improvement over their carbon supported counterparts. However, the carbon-covered alumina supported catalysts seem to have a lower propensity for coke deposition than their alumina counterparts. (author).

  12. Relation between sedimentation behaviour of DNA-membrane complexes and DNA single- and double-strand breaks after irradiation with gamma-rays, pulse neutrons and 12C ions

    International Nuclear Information System (INIS)

    Erzgraber, G.; Lapidus, I.L.

    1985-01-01

    The experimental data on sedimentation behaviour of DNA-membrane complexes at radiation of the Chinese hamster cells (V79-4) in a wide dose range of 127 Cs γ-rays, pulse neutrons (reactor IBR-2, Laboratory of Neutron Physics, JINR, Dubna) are accelerated 12 C ions (cyclotron U-200, Laboratory of Nuclear Reactions, JINR, Dubna) are presented An assumption on the role of DNA single- and double-strend breaks in changing the sedimentation properties of DNA-membrane complexes has been confirmed by the experiments with radiation of different quality. The possibility of estimating induction and repair of DNA breaks on the basis of dependence of the relative sedimentation velocity of complexes on the irradiation does is discussed

  13. Structural, optical and mechanical properties of amorphous and crystalline alumina thin films

    Energy Technology Data Exchange (ETDEWEB)

    Nayar, Priyanka [Department of Physics, Guru Nanak Dev University, Amritsar 143005 (India); Khanna, Atul, E-mail: akphysics@yahoo.com [Department of Physics, Guru Nanak Dev University, Amritsar 143005 (India); Kabiraj, D.; Abhilash, S.R. [Inter University Accelerator Centre, Aruna Asaf Ali Marg, New Delhi 110067 (India); Beake, Ben D.; Losset, Yannick [Micro Materials Limited, Unit 3, Wrexham Technology Park, Wrexham LL13 7YP (United Kingdom); Chen, Banghao [Chemistry and Biochemistry Department, Florida State University, Tallahassee 32306 (United States)

    2014-10-01

    Thin films of amorphous alumina of thickness 350 nm were deposited on fused silica substrates by electron beam evaporation. Amorphous films were annealed at several temperatures in the range: 400–1130 °C and changes in film crystallinity, short-range structure, optical and mechanical properties were studied. X-ray diffraction studies found that crystallization starts at 800 °C and produces γ and δ-alumina, the latter phase grows with heat treatment and the sample was mostly δ and θ-alumina after annealing at 1130 °C. The as-deposited amorphous alumina films have low hardness of 5 to 8 GPa, which increases to 11 to 12 GPa in crystalline sample. {sup 27}Al Magic Angle Spinning Nuclear Magnetic Resonance was used to study the short-range order of amorphous and crystalline alumina films and it was found that amorphous alumina film contains AlO{sub 5} and AlO{sub 4} structural units in the ratio of 1:2. The concentration of AlO{sub 5} was significantly suppressed in crystalline film, which contains 48% of Al{sup 3+} ions in AlO{sub 6}, 7% in AlO{sub 5} and 45% in AlO{sub 4} units. - Highlights: • Structure–property correlations in alumina films grown by electron-beam evaporation • Amorphous films crystallize into γ and δ-alumina on annealing in air at 800 °C. • δ and θ-alumina films are stable up to 1130 °C and do not transform to α-phase. • Amorphous alumina films contain {sup [5]}Al and {sup [4]}Al structural units in the ratio of 1:2. • {sup [5]}Al decreases whereas {sup [6]}Al concentration increases on crystallization.

  14. Oxidation of Alumina-Forming MAX Phases in Turbine Environments

    Science.gov (United States)

    Smialek, James; Garg, Anita; Harder, Bryan; Nesbitt, James; Gabb, Timothy; Gray, SImon

    2017-01-01

    Protective coatings for high temperature turbine components are based on YSZ thermal barriers and oxidation resistant, alumina-forming NiAl or NiCoCrAlY bond coats. Ti2AlC and Cr2AlC MAX phases are thus of special interest because of good oxidation resistance and CTE that can match Al2O3 and YSZ. Their alumina scales grow according to cubic kinetics due to grain growth in the scale, with initial heating dominated by fast TiO2 growth. Protective cubic kinetics are also found in high pressure burner rig tests of MAXthal 211 Ti2AlC, but with reduced rates due to volatile TiO(OH)2 formation in water vapor. YSZ-coatings on bulk Ti2AlC exhibit remarkable durability up to 1300C in furnace tests and at least a 25x life advantage compared to superalloys. At another extreme, Cr2AlC is resistant to low temperature Na2SO4 hot corrosion and exhibits thermal cycling stability bonded to a superalloy disk material. Accordingly, sputtered Cr2AlC coatings on disk specimens prevented hot corrosion detriments on LCF. Breakaway oxidation (Ti2AlC), scale spallation (Cr2AlC), interdiffusion, and processing as coatings still present serious challenges. However the basic properties of MAX phases provide some unusual opportunities for use in high temperature turbines.

  15. Scratch induced failure of plasma sprayed alumina based coatings

    International Nuclear Information System (INIS)

    Hazra, S; Bandyopadhyay, P.P.

    2012-01-01

    Highlights: ► Scratch induced failure of alumina based coatings including nanostructured is reported. ► Ceramic is deposited on bond coat instead of steel, emulating a realistic situation. ► Lateral force data is supplemented with microscopy to observe coating failure. ► The failure mechanism during scratching has been identified. ► Critical load of failure has been calculated for each bond-top coat combination. -- Abstract: A set of plasma sprayed coatings were obtained from three alumina based top coat and two bond coat powders. Scratch test was undertaken on these coatings, under constant and linearly varying load. Test results include the lateral force data and scanning electron microscope (SEM) images. Failure occurred by large area spallation of the top coat and in most cases tensile cracks appeared on the exposed bond coat. The lateral force showed an increasing trend with an increase in normal load up to a certain point and beyond this, it assumed a steady average value. The locations of coating spallation and occurrence of maximum lateral force did not coincide. A bond coat did not show a significant role in determining the scratch adhesion strength.

  16. Wet chemical synthesis of nickel supported on alumina catalysts

    International Nuclear Information System (INIS)

    Freire, Ranny Rodrigues; Costa, Talita Kenya Oliveira; Morais, Ana Carla da Fonseca Ferreira; Costa, Ana Cristina Figueiredo de Melo; Freitas, Normanda Lino de

    2016-01-01

    Heterogenic catalysts are those found to be in a different phase on the reaction when compared to the reactants and products. Preferred when compared to homogeneous catalysts due to the easiness on which the separation is processed. The objective of this study is to obtain and characterize Alumina based catalysts impregnated with Nickel (Al_2O_3), by wet impregnation. The alumina was synthesized by combustion reaction. Before and after the impregnation the catalysts were characterized by X-ray diffraction (XRD), granulometric analysis, the textural analysis will be held by nitrogen adsorption (BET), energy-dispersive X-ray spectroscopy (EDX) and scanning electron microscopy (SEM). The results show a presence of a stable crystalline phase of Al2O3 in all the studied samples and after the impregnation the second phase formed was of NiO and NiAl_2O_4. The Al_2O_3 e Ni/Al_2O_3 catalysts resulted in clusters with a medium diameter of 18.9 and 14.2 μm, respectively. The catalysts show a medium-pore characteristic (medium pore diameter between 2 and 50 nm), the superficial area to Al_2O_3 and Ni/Al_2O_3 catalysts were 8.69 m"2/g and 5.56 m"2/g, respectively. (author)

  17. Structure and Magnetic Properties of Rare Earth Doped Transparent Alumina

    Science.gov (United States)

    Limmer, Krista; Neupane, Mahesh; Chantawansri, Tanya

    Recent experimental studies of rare earth (RE) doped alumina suggest that the RE induced novel phase-dependent structural and magnetic properties. Motivated by these efforts, the effects of RE doping of alpha and theta alumina on the local structure, magnetic properties, and phase stability have been examined in this first principles study. Although a direct correlation between the magnetic field dependent materials properties observed experimentally and calculated from first principles is not feasible because of the applied field and the scale, the internal magnetic properties and other properties of the doped materials are evaluated. The RE dopants are shown to increase the substitutional site volume as well as increasingly distort the site structure as a function of ionic radii. Doping both the alpha (stable) and theta (metastable) phases enhanced the relative stability of the theta phase. The energetic doping cost and internal magnetic moment were shown to be a function of the electronic configuration of the RE-dopant, with magnetic moment directly proportional to the number of unpaired electrons and doping cost being inversely related.

  18. Synthesis of magnesium aluminate spinel by periclase and alumina chlorination

    International Nuclear Information System (INIS)

    Orosco, Pablo; Barbosa, Lucía; Ruiz, María del Carmen

    2014-01-01

    Highlights: • Use of chlorination for the synthesis of magnesium aluminate spinel. • The reagents used were alumina, periclase and chlorine. • Isothermal and non-isothermal assays were performed in air and Cl 2 –N 2 flows. • The chlorination produced magnesium aluminate spinel at 700 °C. • Selectivity of the chlorination reaction to obtain spinel is very high. - Abstract: A pyrometallurgical route for the synthesis of magnesium aluminate spinel by thermal treatment of a mechanical mixture containing 29 wt% MgO (periclase) and 71 wt% Al 2 O 3 (alumina) in chlorine atmosphere was developed and the results were compared with those obtained by calcining the same mixture of oxides in air atmosphere. Isothermal and non-isothermal assays were performed in an experimental piece of equipment adapted to work in corrosive atmospheres. Both reagents and products were analyzed by differential thermal analysis (DTA), X-ray diffraction (XRD) and X-ray fluorescence (XRF). Thermal treatment in Cl 2 atmosphere of the MgO–Al 2 O 3 mixture produces magnesium aluminate spinel at 700 °C, while in air, magnesium spinel is generated at 930 °C. The synthesis reaction of magnesium aluminate spinel was complete at 800 °C

  19. Development of new microporous silica membranes for gas separation

    International Nuclear Information System (INIS)

    Camelia Barboiu; Alejandro Mourgues; Beatrice Sala; Serge de Perthuis; Camelia Barboiu; Alejandro Mourgues; Beatrice Sala; Anne Julbe; Jose Sanchez

    2006-01-01

    This paper presents the synthesis and the application of molecular sieving ceramic membranes to purify hydrogen or helium from various gas mixtures. The membranes prepared in this work consist of an ultra-microporous silica-based separative layer produced via a sol-gel process. Ultra microporous silica containing boron is synthesized by the acid catalyzed hydrolysis and condensation of tetra-ethyl-ortho-silicate in ethanol. The layer is deposited inside a tubular asymmetric alumina support with a meso-porous y alumina inner layer. The thickness of the silica layers after treatment is about 200 nm, estimated from their cross-section SEM micrographs. Ultra-microporous membranes (with pore sizes less than 0.7 nm) are thus required to get high selectivity. Such membranes enable to carry out gas separation up to 500 deg C under a transmembrane pressure lower than 8 bars. He and H 2 permeance values close to 10 -7 mol.m -2 s -1 Pa -1 are obtained, associated with ideal selectivities α(He/CO 2 ) and α(H 2 /CO 2 ) between 10 and 20 at 300 deg C. (authors)

  20. Coupling of separation and reaction in zeolite membrane reactor for hydroisomerization of hydrocarbons

    Energy Technology Data Exchange (ETDEWEB)

    Gora, L.; Maloncy, M.L.; Jansen, J.C. [Ceramic Membrane Centre, The Pore, DelftChemTech, Delft Univ. of Technology (Netherlands)

    2004-07-01

    A zeolite membrane reactor has been developed for the hydroisomerization of hydrocarbons, in which the linear molecules are separated from branch ones on the silicalite-1 membrane prior to conversion of the permeated linear hydrocarbons to equilibrium levels on the catalyst bed. A model studies using C6 components are conduct. Separated n-C6 from 2MP (selectivity 24) is converted for 72% with 36% selectivity towards di-branched isomers (at 393 K). The results indicate that platinum containing chlorinated alumina/silicalite-1 membrane reactor has a potential in upgrading octane values and offers advantages such as higher efficiency, better process control and lower consumption of energy. (orig.)