Properties of antimony doped ZnO thin films deposited by spray pyrolysis technique

Energy Technology Data Exchange (ETDEWEB)

Sadananda Kumar, N., E-mail: sadanthara@gmail.com; Bangera, Kasturi V.; Shivakumar, G. K. [National Institute of Technology Karnataka, Surathkal, Thin Films Laboratory, Department of Physics (India)

2015-07-15

Antimony (Sb) doped zinc oxide (ZnO) thin films were deposited on the glass substrate at 450°C using spray pyrolysis technique. Effect of Sb doping on surface morphology structural, optical and electrical properties were studied. X-ray diffraction (XRD) analysis showed that both the undoped and doped ZnO thin films are polycrystalline in nature with (101) preferred orientation. SEM analysis showed a change in surface morphology of Sb doped ZnO thin films. Doping results in a marked increase in conductivity without affecting the transmittance of the films. ZnO films prepared with 3 at % Sb shows the lowest resistivity of 0.185 Ohm cm with a Hall mobility of 54.05 cm{sup 2} V{sup –1} s{sup –1}, and a hole concentration of 6.25 × 10{sup 17} cm{sup –3}.

Atomic layer deposition of Al-doped ZnO thin films

Energy Technology Data Exchange (ETDEWEB)

Tynell, Tommi; Yamauchi, Hisao; Karppinen, Maarit; Okazaki, Ryuji; Terasaki, Ichiro [Department of Chemistry, Aalto University, FI-00076 Aalto (Finland); Department of Physics, Nagoya University, Nagoya 464-8602 (Japan)

2013-01-15

Atomic layer deposition has been used to fabricate thin films of aluminum-doped ZnO by depositing interspersed layers of ZnO and Al{sub 2}O{sub 3} on borosilicate glass substrates. The growth characteristics of the films have been investigated through x-ray diffraction, x-ray reflection, and x-ray fluorescence measurements, and the efficacy of the Al doping has been evaluated through optical reflectivity and Seebeck coefficient measurements. The Al doping is found to affect the carrier density of ZnO up to a nominal Al dopant content of 5 at. %. At nominal Al doping levels of 10 at. % and higher, the structure of the films is found to be strongly affected by the Al{sub 2}O{sub 3} phase and no further carrier doping of ZnO is observed.

Neutron scintillator using Ga-doped ZnO phosphor with high detection efficiency

International Nuclear Information System (INIS)

Koyama, Shin; Kinoshita, Atsushi; Fujiwara, Akihiko; Kobayashi, Haruki; Takei, Yoshinori; Nanto, Hidehito; Katagiri, Masaki

2009-01-01

Zinc Oxide (ZnO) family phosphors as phosphor for neutron detector have prepared using Spark Plasma Sintering (SPS) method. The optical properties of ZnO phosphor prepared are investigated. The following results were obtained. Two dominant photoluminescence (PL) emission peaks at 395 nm and 495 nm were observed. The lifetime of the PL emission peak at 395 nm (UV emission band) is about 20 ns, which is suitable for neutron detection. The Ga (30 mol%)-doped ZnO phosphor exhibited an intense UV emission band without the visible emission band. The Ga-doped ZnO phosphor can be prepared at the atmospheric pressure of about 8 Pa using SPS method. It was found that the PL intensity of UV emission band is increased with improving the crystallinity of the ZnO phosphor. (author)

Enhancement of the light-scattering ability of Ga-doped ZnO thin films using SiO{sub x} nano-films prepared by atmospheric pressure plasma deposition system

Energy Technology Data Exchange (ETDEWEB)

Chang, Kow-Ming [Department of Electronics Engineering and Institute of Electronics, National Chiao Tung University, 1001 Ta Hsueh Road, Hsinchu 30010, Taiwan, ROC (China); Ho, Po-Ching, E-mail: raymondsam.ee98g@nctu.edu.tw [Department of Electronics Engineering and Institute of Electronics, National Chiao Tung University, 1001 Ta Hsueh Road, Hsinchu 30010, Taiwan, ROC (China); Ariyarit, Atthaporn [Department of Electronics Engineering and Institute of Electronics, National Chiao Tung University, 1001 Ta Hsueh Road, Hsinchu 30010, Taiwan, ROC (China); Yang, Kuo-Hui; Hsu, Jui-Mei; Wu, Chin-Jyi; Chang, Chia-Chiang [Industrial Technology Research Institute, Mechanical and Systems Research Laboratories, Hsinchu 31040, Taiwan, ROC (China)

2013-12-02

To enhance the light-trapping qualities of silicon thin-film solar cells, the use of transparent conductive oxide with high haze and high conductivity is essential. This study investigated an eco-friendly technique that used bilayer Ga-doped zinc oxide/SiO{sub x} films prepared with an atmospheric pressure plasma jet to achieve high haze and low resistivity. A minimum resistivity of 6.00 × 10{sup −4} Ω·cm was achieved at 8 at.% gallium doping. Examination of X-ray diffraction spectra showed that increased film thickness led to increased carrier concentration in GZO bilayers. The optimal bilayer GZO film achieved considerably higher haze values in the visible and NIR regions, compared with Asahi U-type fluorine doped tin oxide. - Highlights: • Ga-doped ZnO (GZO) and SiO{sub x} deposited by atmospheric pressure plasma jet (APPJ) • Deposition uses a water-based precursor and low substrate temperature (< 150 °C). • SiO{sub x} buffer layers deposited by APPJ can control haze value of Ga-doped ZnO films. • GZO/SiO{sub x} achieved the resistivity of 6.00 × 10{sup −4} Ω·cm and haze of 21.5% at 550 nm.

Electronic and atomic structure of complex defects in Al- and Ga-highly doped ZnO films

Energy Technology Data Exchange (ETDEWEB)

Menéndez-Proupin, Eduardo [Instituto de Energía Solar, Universidad Politécnica de Madrid (UPM), Ciudad Universitaria, 28040 Madrid (Spain); Departamento de Física, Facultad de Ciencias, Universidad de Chile, Las Palmeras 3425, 780-0003 Ñuñoa, Santiago (Chile); Palacios, Pablo, E-mail: pablo.palacios@upm.es [Instituto de Energía Solar, Universidad Politécnica de Madrid (UPM), Ciudad Universitaria, 28040 Madrid (Spain); Dpt. FAIAN, E.T.S.I. Aeronáutica y del Espacio, UPM, Pz. Cardenal Cisneros 3, 28040 Madrid (Spain); Wahnón, Perla [Instituto de Energía Solar, Universidad Politécnica de Madrid (UPM), Ciudad Universitaria, 28040 Madrid (Spain); Dpt. TFO, E.T.S.I. Telecomunicación, UPM, Ciudad Universitaria, 28040 Madrid (Spain)

2015-06-15

Point defects in Ga- and Al-doped ZnO thin films are studied by means of first principles electronic structure calculations. Candidate defects are identified to explain recently observed differences in electrical and spectroscopic behavior of both systems. Substitutional doping in Ga–ZnO explain the metallic behavior of the electrical properties. Complexes of interstitial oxygen with substitutional Ga can behave as acceptor and cause partial compensation, as well as gap states below the conduction band minimum as observed in photoemission experiments. Zn vacancies can also act as compensating acceptors. On the other hand, the semiconducting behavior of Al–ZnO and the small variation in the optical gap compared with pure ZnO, can be explained by almost complete compensation between acceptor Zn vacancies and substitutional Al donors. Interstitial Al can also be donor levels and can be the origin of the small band observed in photoemission experiments below the Fermi level. Combinations of substitutional Al with interstitial oxygen can act simultaneously as compensating acceptor and generator of the mentioned photoemission band. The theoretical calculations have been done using density functional theory (DFT) within the generalized gradient approximation with on-site Coulomb interaction. In selected cases, DFT calculations with semilocal-exact exchange hybrid functionals have been performed. Results explain photoelectron spectra of Ga–ZnO and Al–ZnO at the corresponding doping levels. - Highlights: • Defects in Ga- and Al-heavy-doped ZnO films are studied by quantum calculations. • Defects compatible with electrical, optical, and HAXPES spectra are proposed. • Doping efficiency is reduced by Zn vacancies and O interstitials. • HAXPES bands near the Fermi level are induced by Al{sub i}, and complexes Ga{sub Zn}-O{sub i}, and Al{sub Zn}-O{sub i}.

Physical and chemical properties of a Ga-doped ZnO crystal

International Nuclear Information System (INIS)

Stashans, Arvids; Olivos, Katia; Rivera, Richard

2011-01-01

First-principles calculations based on density functional theory and strengthened by Hartree-Fock computations have been performed to study a Ga-doped wurtzite-type ZnO crystal. The large 108-atom supercell used throughout this work allows one to model a single point defect within the periodic supercell model. Thus, the Ga impurity produced purely local effects on the properties of the material. The electronic band structure was obtained for both pure and impurity-doped materials. The occurrence of free electrons in the conduction band was observed after the incorporation of Ga, implying the Ga dopant's contribution to n-type electrical conductivity in the ZnO crystal, in agreement with known experimental data. An analysis of the charges on atoms and obtained atomic displacements in the region surrounding the defect showed that there is some alteration in the chemical bonding because of the presence of Ga atoms. In particular, the ionic bonding is strengthened in the defect's neighbourhood.

Physical and chemical properties of a Ga-doped ZnO crystal

Energy Technology Data Exchange (ETDEWEB)

Stashans, Arvids; Olivos, Katia; Rivera, Richard, E-mail: arvids@utpl.edu.e [Grupo de FisicoquImica de Materiales, Universidad Tecnica Particular de Loja, Apartado 11-01-608, Loja (Ecuador)

2011-06-01

First-principles calculations based on density functional theory and strengthened by Hartree-Fock computations have been performed to study a Ga-doped wurtzite-type ZnO crystal. The large 108-atom supercell used throughout this work allows one to model a single point defect within the periodic supercell model. Thus, the Ga impurity produced purely local effects on the properties of the material. The electronic band structure was obtained for both pure and impurity-doped materials. The occurrence of free electrons in the conduction band was observed after the incorporation of Ga, implying the Ga dopant's contribution to n-type electrical conductivity in the ZnO crystal, in agreement with known experimental data. An analysis of the charges on atoms and obtained atomic displacements in the region surrounding the defect showed that there is some alteration in the chemical bonding because of the presence of Ga atoms. In particular, the ionic bonding is strengthened in the defect's neighbourhood.

Piezoelectricity and charge trapping in ZnO and Co-doped ZnO thin films

Directory of Open Access Journals (Sweden)

Domenico D’Agostino

2017-05-01

Full Text Available Piezoelectricity and charge storage of undoped and Co-doped ZnO thin films were investigated by means of PiezoResponse Force Microscopy and Kelvin Probe Force Microscopy. We found that Co-doped ZnO exhibits a large piezoelectric response, with the mean value of piezoelectric matrix element d33 slightly lower than in the undoped sample. Moreover, we demonstrate that Co-doping affects the homogeneity of the piezoelectric response, probably as a consequence of the lower crystalline degree exhibited by the doped samples. We also investigate the nature of the interface between a metal electrode, made up of the PtIr AFM tip, and the films as well as the phenomenon of charge storage. We find Schottky contacts in both cases, with a barrier value higher in PtIr/ZnO than in PtIr/Co-doped ZnO, indicating an increase in the work function due to Co-doping.

Optoelectronic properties of doped hydrothermal ZnO thin films

KAUST Repository

Mughal, Asad J.; Carberry, Benjamin; Oh, Sang Ho; Myzaferi, Anisa; Speck, James S.; Nakamura, Shuji; DenBaars, Steven P.

2017-01-01

, or In were evaluated for their optoelectronic properties. Inductively coupled plasma atomic emission spectroscopy was used to determine the concentration of dopants within the ZnO films. While Al and Ga-doped films showed linear incorporation rates

Negative permittivity of ZnO thin films prepared from aluminum and gallium doped ceramics via pulsed-laser deposition

DEFF Research Database (Denmark)

Bodea, M. A.; Sbarcea, G.; Naik, G. V.

2013-01-01

Aluminum and gallium doped zinc oxide thin films with negative dielectric permittivity in the near infrared spectral range are grown by pulsed laser deposition. Composite ceramics comprising ZnO and secondary phase Al2O3 or Ga2O3 are employed as targets for laser ablation. Films deposited on glass...

Luminescence properties of Ag-, Ga-doped ZnO and ZnO-ZnS thin films

Energy Technology Data Exchange (ETDEWEB)

Kushnirenko, V.I.; Khomchenko, V.S.; Zavyalova, L.V. [V. Lashkarev Institute of Semiconductor Physics, NAS of Ukraine, Pr. Nauki 45, 03028 Kiev (Ukraine); Zashivailo, T.V. [National Technical University of Ukraine ' ' KPI' ' , Pr. Pobedy 37, 03056 Kiev (Ukraine)

2012-08-15

Thin films of ZnS were grown by metal-organic chemical vapor deposition (MOCVD) method under atmospheric pressure onto glass substrates. ZnO-ZnS:[Ag, Ga] and ZnO:[Ag, Ga] thin films were prepared by oxidation and Ag, Ga doping of ZnS films at temperatures of 700-775 C for 0.5-1 h. Crystalline quality and luminescent properties were investigated using X-ray diffraction (XRD), atomic force microscopy (AFM), and photoluminescence. It is found that the doped films have a polycrystalline structure without preferred orientation and consist of small grains gathered into conglomerates. The shape of photoluminescence (PL) spectra of the films depends strongly on the preparation conditions. The ZnO-ZnS:[Ag, Ga] films exhibited the blue and green emission connected with the presence of silver and oxygen, respectively. The ZnO:[Ag, Ga] films revealed the white emission originated from different defect-related transitions. The possible origin of radiative centers is discussed (copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Improved electrical conduction properties in unintentionally-doped ZnO thin films treated by rapid thermal annealing

International Nuclear Information System (INIS)

Lee, Youngmin; Lee, Choeun; Shim, Eunhee; Jung, Eiwhan; Lee, Jinyong; Kim, Deukyoung; Lee, Sejoon; Fu, Dejun; Yoon, Hyungdo

2011-01-01

The effects of thermal treatments on the electrical conduction properties for the unintentionally doped ZnO thin films were investigated. Despite the decreased carrier density in the annealed ZnO thin films, the conductivity was increased because the contribution of the effective carrier mobility to the conductivity of the unintentionally-doped ZnO thin films is greater than that of the carrier density. The resistivity exponentially decreased with increasing RTA temperature, and this result was confirmed to come from the enhanced effective carrier-mobility, which originated from the increased crystallite size in the annealed ZnO thin films.

Improved electrical conduction properties in unintentionally-doped ZnO thin films treated by rapid thermal annealing

Energy Technology Data Exchange (ETDEWEB)

Lee, Youngmin; Lee, Choeun; Shim, Eunhee; Jung, Eiwhan; Lee, Jinyong; Kim, Deukyoung; Lee, Sejoon [Dongguk University-Seoul, Seoul (Korea, Republic of); Fu, Dejun [Wuhan University, Wuhan (China); Yoon, Hyungdo [Korea Electronics Technology Institute, Seongnam (Korea, Republic of)

2011-10-15

The effects of thermal treatments on the electrical conduction properties for the unintentionally doped ZnO thin films were investigated. Despite the decreased carrier density in the annealed ZnO thin films, the conductivity was increased because the contribution of the effective carrier mobility to the conductivity of the unintentionally-doped ZnO thin films is greater than that of the carrier density. The resistivity exponentially decreased with increasing RTA temperature, and this result was confirmed to come from the enhanced effective carrier-mobility, which originated from the increased crystallite size in the annealed ZnO thin films.

Structure and Properties of Al and Ga- Doped ZnO

Science.gov (United States)

Temizer, Namik Kemal

Recently there is tremendous interest in Transparent conducting oxide (TCO) research due to the unlimited and exciting application areas. Current research is mostly focused on finding alternative low cost and sustainable materials in order to replace indium tin oxide (ITO), which caused serious concern due to the increasing cost of indium and chemical stability issues of ITO. The primary aim of this research is to develop alternative TCO materials with superior properties in order to increase the efficiency in optoelectronic applications, as well as to study the properties of these materials to fully characterize them. We have grown Al and Ga-doped ZnO films with an optimized composition under different deposition conditions in order to understand the effect of processing parameters on the film properties. We report a detailed investigation on the structure-property correlations in Ga and Al codoped ZnO films on c-sapphire substrates where the thin film microstructure varies from nanocrystalline to single crystal. We have achieved highly epitaxial films with very high optical transmittance (close to 90%) and low resistivity (˜110muO-cm) values. The films grown in an ambient oxygen partial pressure (PO2 ) of 50 mTorr and at growth temperatures from room temperature to 600°C showed semiconducting behavior, whereas samples grown at a Po2 of 1 mTorr showed metallic nature. The most striking feature is the occurrence of resistivity minima at relatively high temperatures around 110 K in films deposited at high temperatures. The structure-property correlations reveal that point defects play an important role in modifying the structural, optical, electrical and magnetic properties and such changes in physical properties are controlled predominantly by the defect content. To gain a better understanding of the conduction processes in doped ZnO thin films, we have studied the temperature variation of resistivity of some selected samples that showed some interesting behavior

Synthesis and Characterization of Molybdenum Doped ZnO Thin Films by SILAR Deposition Method

Science.gov (United States)

Radha, R.; Sakthivelu, A.; Pradhabhan, D.

2016-08-01

Molybdenum (Mo) doped zinc oxide (ZnO) thin films were deposited on the glass substrate by Successive Ionic Layer Adsorption and Reaction (SILAR) deposition method. The effect of Mo dopant concentration of 5, 6.6 and 10 mol% on the structural, morphological, optical and electrical properties of n-type Mo doped ZnO films was studied. The X-ray diffraction (XRD) results confirmed that the Mo doped ZnO thin films were polycrystalline with wurtzite structure. The field emission scanning electron microscopy (FESEM) studies shows that the surface morphology of the films changes with Mo doping. A blue shift of the optical band gap was observed in the optical studies. Effect of Mo dopant concentration on electrical conductivity was studied and it shows comparatively high electrical conductivity at 10 mol% of Mo doping concentration.

Effect of doping concentration on the conductivity and optical properties of p-type ZnO thin films

Energy Technology Data Exchange (ETDEWEB)

Pathak, Trilok Kumar [Semiconductor Research Lab, Department of Physics, Gurukula Kangri University, Haridwar (India); Kumar, Vinod, E-mail: vinod.phy@gmail.com [Department of Physics, University of the Free State, Bloemfontein (South Africa); Swart, H.C., E-mail: swarthc@ufs.ac.za [Department of Physics, University of the Free State, Bloemfontein (South Africa); Purohit, L.P., E-mail: proflppurohitphys@gmail.com [Semiconductor Research Lab, Department of Physics, Gurukula Kangri University, Haridwar (India)

2016-01-01

Nitrogen doped ZnO (NZO) thin films were synthesized on glass substrates by the sol–gel and spin coating method. Zinc acetate dihydrates and ammonium acetate were used as precursors for zinc and nitrogen, respectively. X-ray diffraction study showed that the thin films have a hexagonal wurtzite structure corresponding (002) peak for undoped and doped ZnO thin films. The transmittance of the films was above 80% and the band gap of the film varies from 3.21±0.03 eV for undoped and doped ZnO. The minimum resistivity of NZO thin films was obtained as 0.473 Ω cm for the 4 at% of nitrogen (N) doping with a mobility of 1.995 cm{sup 2}/V s. The NZO thin films showed p-type conductivity at 2 and 3 at% of N doping. The AC conductivity measurements that were carried out in the frequency range 10 kHz to 0.1 MHz showed localized conduction in the NZO thin films. These highly transparent ZnO films can be used as a possible window layer in solar cells.

Ionized zinc vacancy mediated ferromagnetism in copper doped ZnO thin films

Directory of Open Access Journals (Sweden)

Shi-Yi Zhuo

2012-03-01

Full Text Available This paper reports the origin of ferromagnetism in Cu-doped ZnO thin films. Room-temperature ferromagnetism is obtained in all the thin films when deposited at different oxygen partial pressure. An obviously enhanced peak corresponding to zinc vacancy is observed in the photoluminescence spectra, while the electrical spin resonance measurement implies the zinc vacancy is negative charged. After excluding the possibility of direct exchange mechanisms (via free carriers, we tentatively propose a quasi-indirect exchange model (via ionized zinc vacancy for Cu-doped ZnO system.

Combined effect of oxygen deficient point defects and Ni doping in radio frequency magnetron sputtering deposited ZnO thin films

Energy Technology Data Exchange (ETDEWEB)

Saha, B., E-mail: biswajit.physics@gmail.com [Thin Film and Nano Science Laboratory, Department of Physics, Jadavpur University, 700 032 Kolkata (India); Department of Physics, National Institute of Technology Agartala, Jirania 799046, Tripura (India); Das, N.S.; Chattopadhyay, K.K. [Thin Film and Nano Science Laboratory, Department of Physics, Jadavpur University, 700 032 Kolkata (India)

2014-07-01

Ni doped ZnO thin films with oxygen deficiency have been synthesized on glass substrates by radio frequency magnetron sputtering technique using argon plasma. The combined effect of point defects generated due to oxygen vacancies and Ni doping on the optical and electrical properties of ZnO thin films has been studied in this work. Ni doping concentrations were varied and the structural, optical and electrical properties of the films were studied as a function of doping concentrations. The films were characterized with X-ray diffractometer, UV–Vis–NIR spectrophotometer, X-ray photoelectron spectroscopy, atomic force microscopy and electrical conductivity measurements. Oxygen deficient point defects (Schottky defects) made the ZnO thin film highly conducting while incorporation of Ni dopant made it more functional regarding their electrical and optical properties. The films were found to have tunable electrical conductivity with Ni doping concentrations. - Highlights: • ZnO thin films prepared by radio frequency magnetron sputtering technique • Synthesis process was stimulated to introduce Schottky-type point defects. • Point defects and external doping of Ni made ZnO thin films more functional. • Point defect induced high electrical conductivity in ZnO thin film. • Significant shift in optical bandgap observed in ZnO with Ni doping concentrations.

Optical and electrical properties of transparent conducting B-doped ZnO thin films prepared by various deposition methods

International Nuclear Information System (INIS)

Nomoto, Jun-ichi; Miyata, Toshihiro; Minami, Tadatsugu

2011-01-01

B-doped ZnO (BZO) thin films were prepared with various thicknesses up to about 500 nm on glass substrates at 200 deg. C by dc or rf magnetron sputtering deposition, pulsed laser deposition (PLD), and vacuum arc plasma evaporation (VAPE) methods. Resistivities of 4-6 x 10 -4 Ω cm were obtained in BZO thin films prepared with a B content [B/(B + Zn) atomic ratio] around 1 at. % by PLD and VAPE methods: Hall mobilities above 40 cm 2 /Vs and carrier concentrations on the order of 10 20 cm -3 . All 500-nm-thick-BZO thin films prepared with a resistivity on the order of 10 -3 -10 -4 Ω cm exhibited an averaged transmittance above 80% in the wavelength range of 400-1100 nm. The resistivity in BZO thin films prepared with a thickness below about 500 nm was found to increase over time with exposure to various high humidity environments. In heat-resistance tests, the resistivity stability of BZO thin films was found to be nearly equal to that of Ga-doped ZnO thin films, so these films were judged suitable for use as a transparent electrode for thin-film solar cells.

Effect of growth interruption on the crystalline quality and electrical properties of Ga-doped ZnO thin film deposited on quartz substrate by magnetron sputtering

International Nuclear Information System (INIS)

Lee, Geun-Hyoung

2013-01-01

Ga-doped ZnO(GZO) thin films were deposited on the quartz substrate by magnetron sputtering system with growth interruption technique. As the number of interruptions and interruption time increased, the carrier concentration and Hall mobility in GZO films significantly increased. As a result, the resistivity of GZO films decreased. The optical transmittance of GZO films also increased with the number of interruption and interruption time. The transmittance showed over 90% in visual region. Atomic force microscopy measurement showed that the film surface became smoother with an increase of the number of interruption. In addition, the crystalline quality and electrical properties of GZO films were more improved when the growth interruption was employed with a temperature gradient. - Highlights: • Ga-doped ZnO thin films were deposited with growth interruption technique. • The crystallinity of the films was improved with the number of interruptions. • The crystallinity of the films was improved as the interruption time increased. • The growth interruption with a temperature gradient more improved the film quality

Ultraviolet Sensing by Al-doped ZnO Thin Films

International Nuclear Information System (INIS)

Rashid, A.R.A.; Menon, P.S.; Shaari, S.

2011-01-01

We report the fabrication and characterization of an ultraviolet photoconductive sensing by using Al-doped ZnO films. Undoped ZnO, 1 at.% and 2 at% of Al were prepared on quartz glass by sol gel method with annealing temperature of 500 degree Celsius for 1 hour. The presence of spherical shaped nanoparticles were detected for undoped ZnO by using FESEM. The absorption edge shifted to a lower wavelength by doping with Al and excitonic peak can be observed. The band gap values increased by adding Al. I-V curves reveal an improvement in electrical properties when the samples are illuminated by ultraviolet (UV) light with a wavelength of 365 nm. At 1 at.% of Al, the film have a larger increment in photocurrent response when illuminated with UV light compared to undoped ZnO and 2 at.% Al. The thin films have a longer recovery time than response time. (author)

Oxygen vacancy-induced ferromagnetism in un-doped ZnO thin films

Science.gov (United States)

Zhan, Peng; Wang, Weipeng; Liu, Can; Hu, Yang; Li, Zhengcao; Zhang, Zhengjun; Zhang, Peng; Wang, Baoyi; Cao, Xingzhong

2012-02-01

ZnO films became ferromagnetic when defects were introduced by thermal-annealing in flowing argon. This ferromagnetism, as shown by the photoluminescence measurement and positron annihilation analysis, was induced by the singly occupied oxygen vacancy with a saturated magnetization dependent positively on the amount of this vacancy. This study clarified the origin of the ferromagnetism of un-doped ZnO thin films and provides possibly an alternative way to prepare ferromagnetic ZnO films.

Probing the doping mechanisms and electrical properties of Al, Ga and In doped ZnO prepared by spray pyrolysis

KAUST Repository

Maller, Robert

2016-05-24

The measured structural, optical and electrical properties of Al, Ga and In doped ZnO films deposited using spray pyrolysis are reported over the doping range 0.1 - 3 atomic percent (at. %). Over the entire doping series highly transparent, polycrystalline thin films are prepared. Using the AC Hall effect we probe the electronic properties of our doped films separating the impact of doping on the measured charge carrier concentrations and Hall mobility, with an emphasis on the low doping, < 1 at. %, range. In this doping range highly resistive films are formed and we highlight AC Hall as a reliable and highly reproducible technique for analysing the doping mechanism. The implementation of a simple, post-deposition heat treatment of our AZO films creates typical films with charge carrier concentrations exceeding > 1019 cm-3 and electron mobilities over 10 cm2/Vs. We describe in detail the nature of the defect chemistry and the role of intrinsic defects, particularly traps, and show that despite significant variations in dopant species and grain boundary concentrations that the defect chemistry dominates the electrical characteristics.

Probing the doping mechanisms and electrical properties of Al, Ga and In doped ZnO prepared by spray pyrolysis

KAUST Repository

Maller, Robert; Porte, Yoann; Alshareef, Husam N.; McLachlan, Martyn

2016-01-01

The measured structural, optical and electrical properties of Al, Ga and In doped ZnO films deposited using spray pyrolysis are reported over the doping range 0.1 - 3 atomic percent (at. %). Over the entire doping series highly transparent, polycrystalline thin films are prepared. Using the AC Hall effect we probe the electronic properties of our doped films separating the impact of doping on the measured charge carrier concentrations and Hall mobility, with an emphasis on the low doping, < 1 at. %, range. In this doping range highly resistive films are formed and we highlight AC Hall as a reliable and highly reproducible technique for analysing the doping mechanism. The implementation of a simple, post-deposition heat treatment of our AZO films creates typical films with charge carrier concentrations exceeding > 1019 cm-3 and electron mobilities over 10 cm2/Vs. We describe in detail the nature of the defect chemistry and the role of intrinsic defects, particularly traps, and show that despite significant variations in dopant species and grain boundary concentrations that the defect chemistry dominates the electrical characteristics.

Optical and electrical properties of transparent conducting B-doped ZnO thin films prepared by various deposition methods

Energy Technology Data Exchange (ETDEWEB)

Nomoto, Jun-ichi; Miyata, Toshihiro; Minami, Tadatsugu [Optoelectronic Device System R and D Center, Kanazawa Institute of Technology, 7-1 Ohgigaoka, Nonoichi, Ishikawa 921-8501 (Japan)

2011-07-15

B-doped ZnO (BZO) thin films were prepared with various thicknesses up to about 500 nm on glass substrates at 200 deg. C by dc or rf magnetron sputtering deposition, pulsed laser deposition (PLD), and vacuum arc plasma evaporation (VAPE) methods. Resistivities of 4-6 x 10{sup -4}{Omega} cm were obtained in BZO thin films prepared with a B content [B/(B + Zn) atomic ratio] around 1 at. % by PLD and VAPE methods: Hall mobilities above 40 cm{sup 2}/Vs and carrier concentrations on the order of 10{sup 20} cm{sup -3}. All 500-nm-thick-BZO thin films prepared with a resistivity on the order of 10{sup -3}-10{sup -4}{Omega} cm exhibited an averaged transmittance above 80% in the wavelength range of 400-1100 nm. The resistivity in BZO thin films prepared with a thickness below about 500 nm was found to increase over time with exposure to various high humidity environments. In heat-resistance tests, the resistivity stability of BZO thin films was found to be nearly equal to that of Ga-doped ZnO thin films, so these films were judged suitable for use as a transparent electrode for thin-film solar cells.

Two-step deposition of Al-doped ZnO on p-GaN to form ohmic contacts

Science.gov (United States)

Su, Xi; Zhang, Guozhen; Wang, Xiao; Chen, Chao; Wu, Hao; Liu, Chang

2017-07-01

Al-doped ZnO (AZO) thin films were deposited directly on p-GaN substrates by using a two-step deposition consisting of polymer assisted deposition (PAD) and atomic layer deposition (ALD) methods. Ohmic contacts of the AZO on p-GaN have been formed. The lowest sheet resistance of the two-step prepared AZO films reached to 145 Ω/sq, and the specific contact resistance reduced to 1.47 × 10-2 Ω·cm2. Transmittance of the AZO films remained above 80% in the visible region. The combination of PAD and ALD technique can be used to prepare p-type ohmic contacts for optoelectronics.

Quenching of surface traps in Mn doped ZnO thin films for enhanced optical transparency

International Nuclear Information System (INIS)

Ilyas, Usman; Rawat, R.S.; Roshan, G.; Tan, T.L.; Lee, P.; Springham, S.V.; Zhang, Sam; Fengji Li; Chen, R.; Sun, H.D.

2011-01-01

The structural and photoluminescence analyses were performed on un-doped and Mn doped ZnO thin films grown on Si (1 0 0) substrate by pulsed laser deposition (PLD) and annealed at different post-deposition temperatures (500-800 deg. C). X-ray diffraction (XRD), employed to study the structural properties, showed an improved crystallinity at elevated temperatures with a consistent decrease in the lattice parameter 'c'. The peak broadening in XRD spectra and the presence of Mn 2p3/2 peak at ∼640 eV in X-ray Photoelectron Spectroscopic (XPS) spectra of the doped thin films confirmed the successful incorporation of Mn in ZnO host matrix. Extended near band edge emission (NBE) spectra indicated the reduction in the concentration of the intrinsic surface traps in comparison to the doped ones resulting in improved optical transparency. Reduced deep level emission (DLE) spectra in doped thin films with declined PL ratio validated the quenching of the intrinsic surface traps thereby improving the optical transparency and the band gap, essential for optoelectronic and spintronic applications. Furthermore, the formation and uniform distribution of nano-sized grains with improved surface features of Mn-doped ZnO thin films were observed in Field Emission Scanning Electron Microscopy (FESEM) images.

Pulsed laser deposited Al-doped ZnO thin films for optical applications

Directory of Open Access Journals (Sweden)

Gurpreet Kaur

2015-02-01

Full Text Available Highly transparent and conducting Al-doped ZnO (Al:ZnO thin films were grown on glass substrates using pulsed laser deposition technique. The profound effect of film thickness on the structural, optical and electrical properties of Al:ZnO thin films was observed. The X-ray diffraction depicts c-axis, plane (002 oriented thin films with hexagonal wurtzite crystal structure. Al-doping in ZnO introduces a compressive stress in the films which increase with the film thickness. AFM images reveal the columnar grain formation with low surface roughness. The versatile optical properties of Al:ZnO thin films are important for applications such as transparent electromagnetic interference (EMI shielding materials and solar cells. The obtained optical band gap (3.2–3.08 eV was found to be less than pure ZnO (3.37 eV films. The lowering in the band gap in Al:ZnO thin films could be attributed to band edge bending phenomena. The photoluminescence spectra gives sharp visible emission peaks, enables Al:ZnO thin films for light emitting devices (LEDs applications. The current–voltage (I–V measurements show the ohmic behavior of the films with resistivity (ρ~10−3 Ω cm.

Role of vacancy defects in Al doped ZnO thin films for optoelectronic devices

Science.gov (United States)

Rotella, H.; Mazel, Y.; Brochen, S.; Valla, A.; Pautrat, A.; Licitra, C.; Rochat, N.; Sabbione, C.; Rodriguez, G.; Nolot, E.

2017-12-01

We report on the electrical, optical and photoluminescence properties of industry-ready Al doped ZnO thin films grown by physical vapor deposition, and their evolution after annealing under vacuum. Doping ZnO with Al atoms increases the carrier density but also favors the formation of Zn vacancies, thereby inducing a saturation of the conductivity mechanism at high aluminum content. The electrical and optical properties of these thin layered materials are both improved by annealing process which creates oxygen vacancies that releases charge carriers thus improving the conductivity. This study underlines the effect of the formation of extrinsic and intrinsic defects in Al doped ZnO compound during the fabrication process. The quality and the optoelectronic response of the produced films are increased (up to 1.52 mΩ \\cdotcm and 3.73 eV) and consistent with the industrial device requirements.

Structural, optical and magnetic properties of Mn doped ZnO thin films prepared by pulsed laser deposition

Energy Technology Data Exchange (ETDEWEB)

Aravind, Arun, E-mail: aruncusat@gmail.com [Nanophotonic and Optoelectronic Devices Laboratory, Department of Physics, Cochin University of Science and Technology, Kochi 682 022, Kerala (India); Jayaraj, M.K., E-mail: mkj@cusat.ac.in [Nanophotonic and Optoelectronic Devices Laboratory, Department of Physics, Cochin University of Science and Technology, Kochi 682 022, Kerala (India); Kumar, Mukesh; Chandra, Ramesh [Nano Science Laboratory, Institute Instrumentation Centre, IIT Roorkee, Roorkee 247 667, Uttarakhand (India)

2012-08-01

Highlights: Black-Right-Pointing-Pointer Defect induced Raman active modes in Mn doped ZnO thin films. Black-Right-Pointing-Pointer Room temperature ferromagnetism. Black-Right-Pointing-Pointer Morphological variations of ZnO thin films with Mn doping. Black-Right-Pointing-Pointer Variation of refractive index of ZnO thin films with Mn doping. - Abstract: Zn{sub 1-x}Mn{sub x}O thin films were grown by pulsed laser deposition. The phase purity and the structure were confirmed by X-ray diffraction studies. The films have a transmittance more than 80% in the visible region. The refractive index of Zn{sub 0.90}Mn{sub 0.10}O films is found to be 1.77 at 550 nm. The presence of non-polar E{sub 2}{sup high} and E{sub 2}{sup low} Raman modes in thin films indicates that 'Mn' doping does not change the wurtzite structure of ZnO. Apart from the normal modes of ZnO the Zn{sub 1-x}Mn{sub x}O ceramic targets show two additional modes at 332 cm{sup -1} (I{sub 1}) and 524 cm{sup -1} (I{sub 2}). The broad Raman peaks (340-600 cm{sup -1}) observed Zn{sub 0.90}Mn{sub 0.10}O thin films can be deconvoluted into five peaks, denoted as P{sub 1}-P{sub 5}. The possible origins of Raman peaks in Zn{sub 1-x}Mn{sub x}O films are the structural disorder and morphological change caused by the Mn dopant. The B{sub 1}{sup low}, {sup 2}B{sub 1}{sup low}, B{sub 1}{sup high} and A{sub 1}{sup LO} modes as well as the surface phonon mode have been observed in heavily Mn-doped ZnO films. Zn{sub 0.98}Mn{sub 0.02}O thin film shows room temperature ferromagnetism. The saturation magnetic moment of the Zn{sub 0.98}Mn{sub 0.02}O thin film is 0.42{mu}{sub B}/Mn atom. The undoped ZnO film prepared under the same condition shows diamagnetic nature. At higher doping concentrations the formation of Mn clusters suppress the room temperature ferromagnetism in Zn{sub 1-x}Mn{sub x}O thin films and shows paramagnetism. XPS confirms the incorporation of Mn{sup 2+} into the ZnO lattice.

Effect of Er3+ doping on structural, morphological and photocatalytical properties of ZnO thin films

Science.gov (United States)

Bouhouche, S.; Bensouici, F.; Toubane, M.; Azizi, A.; Otmani, A.; Chebout, K.; Kezzoula, F.; Tala-Ighil, R.; Bououdina, M.

2018-05-01

In this research work, structure, microstructure, optical and photocatalytic properties of undoped and Erbium doped nanostructured ZnO thin films prepared by sol-gel dip-coating are investigated. X-ray diffraction (XRD) analysis indicates that the deposited films crystallize within the hexagonal wurtzite-type structure with a preferential growth orientation along (002) plane. Morphological observations using scanning electron microscopy (SEM) reveal important influence of Er concentration; displaying homogeneous and dense aspect for undoped to 0.3% then grid-like morphology for 0.4 and 0.5%. UV/vis/NIR transmittance spectroscopy spectra display a transmittance over 70%, and small variation in the energy gap energy 3.263–3.278 eV. Wettability test of ZnO thin films surface ranges from hydrophilic aspect for pure ZnO to hydrophobic one for Er doped ZnO, and the contact angle is found to increase from 58.7° for pure ZnO up to 98.4° for 0.4% Er doped ZnO. The photocatalytic activity measurements evaluated using the degradation of methylene blue (MB) under UV light irradiation demonstrate that undoped ZnO film shows higher photocatalytic activity compared to Er doped ZnO films, which may be attributed to the deterioration of films’crystallinity resulting in lower transmittance.

Formation of p-type ZnO thin film through co-implantation

Science.gov (United States)

Chuang, Yao-Teng; Liou, Jhe-Wei; Woon, Wei-Yen

2017-01-01

We present a study on the formation of p-type ZnO thin film through ion implantation. Group V dopants (N, P) with different ionic radii are implanted into chemical vapor deposition grown ZnO thin film on GaN/sapphire substrates prior to thermal activation. It is found that mono-doped ZnO by N+ implantation results in n-type conductivity under thermal activation. Dual-doped ZnO film with a N:P ion implantation dose ratio of 4:1 is found to be p-type under certain thermal activation conditions. Higher p-type activation levels (1019 cm-3) under a wider thermal activation range are found for the N/P dual-doped ZnO film co-implanted by additional oxygen ions. From high resolution x-ray diffraction and x-ray photoelectron spectroscopy it is concluded that the observed p-type conductivities are a result of the promoted formation of PZn-4NO complex defects via the concurrent substitution of nitrogen at oxygen sites and phosphorus at zinc sites. The enhanced solubility and stability of acceptor defects in oxygen co-implanted dual-doped ZnO film are related to the reduction of oxygen vacancy defects at the surface. Our study demonstrates the prospect of the formation of stable p-type ZnO film through co-implantation.

Influence of Ag thickness of aluminum-doped ZnO/Ag/aluminum-doped ZnO thin films

Energy Technology Data Exchange (ETDEWEB)

Wu, Hung-Wei, E-mail: hwwu@mail.ksu.edu.tw [Department of Computer and Communication, Kun Shan University, No. 949, Dawan Rd., Yongkang Dist., Tainan City 710, Taiwan (China); Yang, Ru-Yuan [Graduate Institute of Materials Engineering, National Pingtung University of Science and Technology, 1, Shuefu Rd., Neipu, Pingtung City 912, Taiwan (China); Hsiung, Chin-Min; Chu, Chien-Hsun [Department of Mechanical Engineering, National Pingtung University of Science and Technology, 1, Shuefu Rd., Neipu, Pingtung City 912, Taiwan (China)

2012-10-01

Highly conducting aluminum-doped ZnO (30 nm)/Ag (5-15 nm)/aluminum-doped ZnO (30 nm) multilayer thin films were deposited on glass substrate by rf magnetron sputtering (for top/bottom aluminum-doped ZnO films) and e-beam evaporation (for Ag film). The transmittance is more than 70% for wavelengths above 400 nm with the Ag layer thickness of 10 nm. The resistivity is 3.71 Multiplication-Sign 10{sup -4} {Omega}-cm, which can be decreased to 3.8 Multiplication-Sign 10{sup -5} {Omega}-cm with the increase of the Ag layer thickness to 15 nm. The Haacke figure of merit has been calculated for the films with the best value being 8 Multiplication-Sign 10{sup -3} {Omega}{sup -1}. It was shown that the multilayer thin films have potential for applications in optoelectronics. - Highlights: Black-Right-Pointing-Pointer High-quality Al-doped ZnO (AZO)/Ag/AZO Transparent Conducting Oxide films. Black-Right-Pointing-Pointer AZO films (30 nm) made by RF sputtering; E-beam evaporation for Ag film (5-15 nm). Black-Right-Pointing-Pointer Influence of Ag thickness on optical and electrical properties were analyzed. Black-Right-Pointing-Pointer High quality multilayer film with optimal intermediate Ag layer thickness of 10 nm. Black-Right-Pointing-Pointer 3.71 Multiplication-Sign 10{sup -4} {Omega}-cm resistivity, 91.89% transmittance at 470 nm obtained and reproducible.

Structural, optical and magnetic properties of nanocrystalline Co-doped ZnO thin films grown by sol-gel

Energy Technology Data Exchange (ETDEWEB)

Kayani, Zohra Nazir; Shah, Iqra; Zulfiqar, Bareera; Sabah, Aneeqa [Lahore College for Women Univ., Lahore (Pakistan); Riaz, Saira; Naseem, Shahzad [Univ. of the Punjab, Lahore (Pakistan). Centre of Excellence in Solid State Physics

2018-04-01

Cobalt-doped ZnO thin films have been deposited using a sol-gel route by changing the number of coats on the substrate from 6 to 18. This project deals with various film thicknesses by increasing the number of deposited coats. The effect of thickness on structural, magnetic, surface morphology and optical properties of Co-doped ZnO thin film was studied. The crystal structure of the Co-doped ZnO films was investigated by X-ray diffraction. The films have polycrystalline wurtzite hexagonal structures. A Co{sup 2+} ion takes the place of a Zn{sup 2+} ion in the lattice without creating any distortion in its hexagonal wurtzite structure. An examination of the optical transmission spectra showed that the energy band gap of the Co-doped ZnO films increased from 3.87 to 3.97 eV with an increase in the number of coatings on the substrate. Ferromagnetic behaviour was confirmed by measurements using a vibrating sample magnetometer. The surface morphology of thin films was assessed by scanning electron microscope. The grain size on the surface of thin films increased with an increase in the number of coats.

Recombination luminescence and trap levels in undoped and Al-doped ZnO thin films on quartz and GaSe (0 0 0 1) substrates

Energy Technology Data Exchange (ETDEWEB)

Evtodiev, I. [Moldova State University, 60 A. Mateevici Str., Chisinau, MD 2009, Republic of Moldova (Moldova, Republic of); Caraman, I. [Vasile Alecsandri University of Bacau, 157 Calea Marasesti, RO 600115 Bacau (Romania); Leontie, L., E-mail: lleontie@uaic.ro [Alexandru Ioan Cuza University of Iasi, Bd. Carol I, Nr. 11, RO 700506 Iasi (Romania); Rusu, D.-I. [Vasile Alecsandri University of Bacau, 157 Calea Marasesti, RO 600115 Bacau (Romania); Dafinei, A. [Faculty of Physics, University of Bucharest, Platforma Magurele, Str. Fizicienilor nr. 1, CP Mg - 11, Bucharest-Magurele, RO 76900 (Romania); Nedeff, V.; Lazar, G. [Vasile Alecsandri University of Bacau, 157 Calea Marasesti, RO 600115 Bacau (Romania)

2012-03-15

Highlights: Black-Right-Pointing-Pointer ZnO films on GaSe create electron trapping states and PL recombination levels. Black-Right-Pointing-Pointer Zn and Al diffusion in GaSe produces low-energy widening of its PL emission. Black-Right-Pointing-Pointer ZnO:Al films on GaSe lamellas are suitable for gas-discharge lamp applications. -- Abstract: Photoluminescence spectra of ZnO and ZnO:Al (1.00, 2.00 and 5.00 at.%) films on GaSe (0 0 0 1) lamellas and amorphous quartz substrates, obtained by annealing, at 700 K, of undoped and Al-doped metal films, are investigated. For all samples, the nonequilibrium charge carriers recombine by radiative band-to-band transitions with energy of 3.27 eV, via recombination levels created by the monoionized oxygen atoms, forming the impurity band laying in the region 2.00 - 2.70 eV. Al doping induces an additional recombination level at 1.13 eV above the top of the valence band of ZnO films on GaSe substrates. As a result of thermal diffusion of Zn and Al into the GaSe interface layer from ZnO:Al/GaSe heterojunction, electron trap levels located at 0.22 eV and 0.26 eV below the conduction band edge of GaSe, as well as a deep recombination level, responsible for the luminescent emission in the region 1.10 - 1.40 eV, are created.

Effect of Mg doping in ZnO buffer layer on ZnO thin film devices for electronic applications

Science.gov (United States)

Giri, Pushpa; Chakrabarti, P.

2016-05-01

Zinc Oxide (ZnO) thin films have been grown on p-silicon (Si) substrate using magnesium doped ZnO (Mg: ZnO) buffer layer by radio-frequency (RF) sputtering method. In this paper, we have optimized the concentration of Mg (0-5 atomic percent (at. %)) ZnO buffer layer to examine its effect on ZnO thin film based devices for electronic and optoelectronic applications. The crystalline nature, morphology and topography of the surface of the thin film have been characterized. The optical as well as electrical properties of the active ZnO film can be tailored by varying the concentration of Mg in the buffer layer. The crystallite size in the active ZnO thin film was found to increase with the Mg concentration in the buffer layer in the range of 0-3 at. % and subsequently decrease with increasing Mg atom concentration in the ZnO. The same was verified by the surface morphology and topography studies carried out with scanning electron microscope (SEM) and atomic electron microscopy (AFM) respectively. The reflectance in the visible region was measured to be less than 80% and found to decrease with increase in Mg concentration from 0 to 3 at. % in the buffer region. The optical bandgap was initially found to increase from 3.02 eV to 3.74 eV by increasing the Mg content from 0 to 3 at. % but subsequently decreases and drops down to 3.43 eV for a concentration of 5 at. %. The study of an Au:Pd/ZnO Schottky diode reveals that for optimum doping of the buffer layer the device exhibits superior rectifying behavior. The barrier height, ideality factor, rectification ratio, reverse saturation current and series resistance of the Schottky diode were extracted from the measured current voltage (I-V) characteristics.

Morphology evolution of hydrothermally grown ZnO nanostructures on gallium doping and their defect structures

Energy Technology Data Exchange (ETDEWEB)

Pineda-Hernandez, G. [Facultad de Ingenieria Quimica, Benemerita Universidad Autonoma de Puebla, C.P. 72570 Puebla, Pue. (Mexico); Escobedo-Morales, A., E-mail: alejandroescobedo@hotmail.com [Facultad de Ingenieria Quimica, Benemerita Universidad Autonoma de Puebla, C.P. 72570 Puebla, Pue. (Mexico); Pal, U. [Instituto de Fisica, Benemerita Universidad Autonoma de Puebla, Apdo. Postal J-48, C.P. 72570 Puebla, Pue. (Mexico); Chigo-Anota, E. [Facultad de Ingenieria Quimica, Benemerita Universidad Autonoma de Puebla, C.P. 72570 Puebla, Pue. (Mexico)

2012-08-15

In the present article, the effect of gallium doping on the morphology, structural, and vibrational properties of hydrothermally grown ZnO nanostructures has been studied. It has been observed that incorporated gallium plays an important role on the growth kinetics and hence on the morphology evolution of the ZnO crystals. Ga doping in high concentration results in the contraction of ZnO unit cell, mainly along c-axis. Although Ga has high solubility in ZnO, heavy doping promotes the segregation of Ga atoms as a secondary phase. Incorporated Ga atoms strongly affect the vibrational characteristics of ZnO lattice and induce anomalous Raman modes. Possible mechanisms of morphology evolution and origin of anomalous Raman modes in Ga doped ZnO nanostructures are discussed. -- Highlights: Black-Right-Pointing-Pointer Ga doped ZnO nanostructures were successfully grown by hydrothermal chemical route. Black-Right-Pointing-Pointer Ga doping has strong effect on the resulting morphology of ZnO nanostructures. Black-Right-Pointing-Pointer Anomalous vibrational modes in wurtzite ZnO lattice are induced by Ga doping. Black-Right-Pointing-Pointer Incorporated Ga atoms accommodate at preferential lattice sites.

Effect of Ag doping on the properties of ZnO thin films for UV stimulated emission

Science.gov (United States)

Razeen, Ahmed S.; Gadallah, A.-S.; El-Nahass, M. M.

2018-06-01

Ag doped ZnO thin films have been prepared using sol-gel spin coating method, with different doping concentrations. Structural and morphological properties of the films have been investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques. Thin films have been optically pumped and stimulated emission has been observed with strong peaks in the UV region. The UV stimulated emission is found to be due to exciton-exciton scattering, and Ag doping promoted this process by increasing the excitons concentrations in the ZnO lattice. Output-input intensity relation and peak emission, FWHM, and quantum efficiency relations with pump intensity have been reported. The threshold for which stimulated emission started has been evaluated to be about 18 MW/cm2 with quantum efficiency of about 58.7%. Mechanisms explaining the role of Ag in enhancement of stimulated emission from ZnO thin films have been proposed.

Electrodeposition of Cu-doped ZnO nanowire arrays and heterojunction formation with p-GaN for color tunable light emitting diode applications

International Nuclear Information System (INIS)

Lupan, O.; Pauporté, T.; Viana, B.; Aschehoug, P.

2011-01-01

Highlights: ► High quality copper-doped zinc oxide nanowires were electrochemically grown at low temperature. ► ZnO:Cu nanowires have been epitaxially grown on Mg-doped p-GaN single-crystalline layers. ► The (ZnO:Cu NWs)/(p-GaN:Mg) heterojunction was used to fabricate a light-emitting diode structure. ► The photo- and electroluminescence emission was red-shifted to the violet spectral region compared to pure ZnO. ► The results are of importance for band-gap engineering of ZnO and for color-tunable LED. - Abstract: Copper-doped zinc oxide (ZnO:Cu) nanowires (NWs) were electrochemically deposited at low temperature on fluor-doped tin oxide (FTO) substrates. The electrochemical behavior of the Cu–Zn system for Cu-doped ZnO electrodeposition was studied and the electrochemical reaction mechanism is discussed. The synthesized ZnO arrayed layers were investigated by using SEM, XRD, EDX, photoluminescence and Raman techniques. X-ray diffraction analysis demonstrates a decrease in the lattice parameters of Cu-doped ZnO NWs. Structural analyses show that the nanomaterial is of hexagonal structure with the Cu incorporated in ZnO NWs probably by substituting zinc in the host lattice. Photoluminescence studies on pure and Cu-doped ZnO NWs shows that the near band edge emission is red-shifted by about 5 or 12 nm depending on Cu(II) concentration in the electrolytic bath solution (3 or 6 μmol l −1 ). Cu-doped ZnO NWs have been also epitaxially grown on Mg doped p-GaN single-crystalline layers and the (ZnO:Cu NWs)/(p-GaN:Mg) heterojunction has been used to fabricate a light-emitting diode (LED) structure. The emission was red-shifted to the visible violet spectral region compared to pure ZnO. The present work demonstrates the ability of electrodeposition to produce high quality ZnO nanowires with tailored optical properties by doping. The obtained results are of great importance for further studies on bandgap engineering of ZnO, for color-tunable LED applications

Realizing luminescent downshifting in ZnO thin films by Ce doping with enhancement of photocatalytic activity

Science.gov (United States)

Narayanan, Nripasree; Deepak, N. K.

2018-04-01

ZnO thin films doped with Ce at different concentration were deposited on glass substrates by spray pyrolysis technique. XRD analysis revealed the phase purity and polycrystalline nature of the films with hexagonal wurtzite geometry and the composition analysis confirmed the incorporation of Ce in the ZnO lattice in the case of doped films. Crystalline quality and optical transmittance diminished while electrical conductivity enhanced with Ce doping. Ce doping resulted in a red-shift of optical energy gap due to the downshift of the conduction band minimum after merging with Ce related impurity bands formed below the conduction band in the forbidden gap. In the room temperature photoluminescence spectra, UV emission intensity of the doped films decreased while the intensity of the visible emission band increased drastically implying the degradation in crystallinity as well as the incorporation of defect levels capable of luminescence downshifting. Ce doping showed improvement in photocatalytic efficiency by effectively trapping the free carriers and then transferring for dye degradation. Thus Ce doped ZnO thin films are capable of acting as luminescent downshifters as well as efficient photocatalysts.

The magnetic ordering in high magnetoresistance Mn-doped ZnO thin films

KAUST Repository

Venkatesh, S.

2016-03-24

We studied the nature of magnetic ordering in Mn-doped ZnO thin films that exhibited ferromagnetism at 300 K and superparamagnetism at 5 K. We directly inter-related the magnetisation and magnetoresistance by invoking the polaronpercolation theory and variable range of hopping conduction below the metal-to-insulator transition. By obtaining a qualitative agreement between these two models, we attribute the ferromagnetism to the s-d exchange-induced spin splitting that was indicated by large positive magnetoresistance (∼40 %). Low temperature superparamagnetism was attributed to the localization of carriers and non-interacting polaron clusters. This analysis can assist in understanding the presence or absence of ferromagnetism in doped/un-doped ZnO.

The magnetic ordering in high magnetoresistance Mn-doped ZnO thin films

Energy Technology Data Exchange (ETDEWEB)

Venkatesh, S.; Baras, A.; Roqan, I. S., E-mail: Iman.roqan@kaust.edu.sa [Physical Sciences and Engineering Division, King Abdullah University of Science and Technology (KAUST), Thuwal 23955-6900 (Saudi Arabia); Lee, J.-S. [Stanford Synchrotron Radiation Lightsource, SLAC National Accelerator Laboratory, Menlo Park, California 94025 (United States)

2016-03-15

We studied the nature of magnetic ordering in Mn-doped ZnO thin films that exhibited ferromagnetism at 300 K and superparamagnetism at 5 K. We directly inter-related the magnetisation and magnetoresistance by invoking the polaron percolation theory and variable range of hopping conduction below the metal-to-insulator transition. By obtaining a qualitative agreement between these two models, we attribute the ferromagnetism to the s-d exchange-induced spin splitting that was indicated by large positive magnetoresistance (∼40 %). Low temperature superparamagnetism was attributed to the localization of carriers and non-interacting polaron clusters. This analysis can assist in understanding the presence or absence of ferromagnetism in doped/un-doped ZnO.

Characteristics of hydrogen co-doped ZnO : Al thin films

International Nuclear Information System (INIS)

Lee, S H; Lee, T S; Lee, K S; Cheong, B; Kim, W M; Kim, Y D

2008-01-01

ZnO films co-doped with H and Al (HAZO) were prepared by sputtering ZnO targets containing 1 wt% Al 2 O 3 on Corning glass at a substrate temperature of 150 deg. C with Ar and H 2 /Ar gas mixtures. The effects of hydrogen addition to Al-doped ZnO (AZO) films with low Al content on the electrical, the optical and the structural properties of the as-grown films as well as the vacuum- and air-annealed films were examined. Secondary ion mass spectroscopy analysis showed that the hydrogen concentration increased with increasing H 2 in sputter gas. For the as-deposited films, the free carrier number increased with increasing H 2 . The Hall mobility increased at low hydrogen content, reaching a maximum before decreasing with a further increase of H 2 content in sputter gas. Annealing at 300 deg. C resulted in the removal of hydrogen, causing a decrease in the carrier concentration. It was shown that hydrogen might exist as single isolated interstitial hydrogen bound with oxygen, thereby acting like an anionic dopant. Also, it was shown that the addition of hydrogen to ZnO films doped with low metallic dopant concentration could yield transparent conducting films with very low absorption loss as well as with proper electrical properties, which is suitable for thin film solar cell applications

Exploration of Al-Doped ZnO in Photovoltaic Thin Films

Science.gov (United States)

Ciccarino, Christopher; Sahiner, M. Alper

The electrical properties of Al doped ZnO-based thin films represent a potential advancement in the push for increasing solar cell efficiency. Doping with Aluminum will theoretically decrease resistivity of the film and therefore achieve this potential as a viable option in the P-N junction phase of photovoltaic cells. The n-type semi-conductive characteristics of the ZnO layer will theoretically be optimized with the addition of Aluminum carriers. In this study, Aluminum doping concentrations ranging from 1-3% by mass were produced, analyzed, and compared. Films were developed onto ITO coated glass using the Pulsed Laser Deposition technique. Target thickness was 250 nm and ellipsometry measurements showed uniformity and accuracy in this regard. Active dopant concentrations were determined using Hall Effect measurements. Efficiency measurements showed possible applications of this doped compound, with upwards of 7% efficiency measured, using a Keithley 2602 SourceMeter set-up. XRD scans showed highly crystalline structures, with effective Al intertwining of the hexagonal wurtzile ZnO molecular structure. This alone indicates a promising future of collaboration between these two materials.

Structural and Magnetic Properties of Mn doped ZnO Thin Film Deposited by Pulsed Laser Deposition

KAUST Repository

Baras, Abdulaziz

2011-07-01

Diluted magnetic oxide (DMO) research is a growing field of interdisciplinary study like spintronic devices and medical imaging. A definite agreement among researchers concerning the origin of ferromagnetism in DMO has yet to be reached. This thesis presents a study on the structural and magnetic properties of DMO thin films. It attempts to contribute to the understanding of ferromagnetism (FM) origin in DMO. Pure ZnO and Mn doped ZnO thin films have been deposited by pulsed laser deposition (PLD) using different deposition conditions. This was conducted in order to correlate the change between structural and magnetic properties. Structural properties of the films were characterized using x-ray diffraction (XRD) and scanning electron microscopy (SEM). The superconducting quantum interference device (SQUID) was used to investigate the magnetic properties of these films. The structural characterizations showed that the quality of pure ZnO and Mn doped ZnO films increased as oxygen pressure (PO) increased during deposition. All samples were insulators. In Mn doped films, Mn concentration decreased as PO increased. The Mn doped ZnO samples were deposited at 600˚C and oxygen pressure from 50-500mTorr. All Mn doped films displayed room temperature ferromagnetism (RTFM). However, at 5 K a superparamagnetic (SPM) behavior was observed in these samples. This result was accounted for by the supposition that there were secondary phase(s) causing the superparamagnetic behavior. Our findings hope to strengthen existing research on DMO origins and suggest that secondary phases are the core components that suppress the ferromagnetism. Although RTFM and SPM at low temperature has been observed in other systems (e.g., Co doped ZnO), we are the first to report this behavior in Mn doped ZnO. Future research might extend the characterization and exploration of ferromagnetism in this system.

Properties of fluorine and tin co-doped ZnO thin films deposited by sol–gel method

International Nuclear Information System (INIS)

Pan, Zhanchang; Zhang, Pengwei; Tian, Xinlong; Cheng, Guo; Xie, Yinghao; Zhang, Huangchu; Zeng, Xiangfu; Xiao, Chumin; Hu, Guanghui; Wei, Zhigang

2013-01-01

Highlights: •F and Sn co-doped ZnO thin films were synthesized by sol–gel method. •The effects of different F doping concentrations were investigated. •The co-doped nanocrystals exhibit good crystal quality. •The origin of the photoluminescence emissions was discussed. •The films showed high transmittance and low resistivity. -- Abstract: Highly transparent and conducting fluorine (F) and tin (Sn) co-doped ZnO (FTZO) thin films were deposited on glass substrates by the sol–gel processing. The structure and morphology of the films are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM) with various F doping concentrations. SEM images showed that the hexagonal ZnO crystals were well-arranged on the glass substrates and the HRTEM images indicated that the individual nanocrystals are highly oriented and exhibited a perfect lattice structure. Owing to its high carrier concentration and mobility, as well as good crystal quality, a minimum resistivity of 1 × 10 −3 Ω cm was obtained from the FTZO thin film with 3% F doping, and the average optical transmittance in the entire visible wavelength region was higher than 90%. The X-ray photoelectron spectroscopy (XPS) study confirmed the substitution of Zn 2+ by Sn ions and Room temperature photoluminescence (PL) observed for pure and FTZO thin films suggested the films exhibit a good crystallinity with a very low defect concentration

Defect induced activation of Raman silent modes in rf co-sputtered Mn doped ZnO thin films

Energy Technology Data Exchange (ETDEWEB)

Yadav, Harish Kumar [Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India); Sreenivas, K [Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India); Katiyar, R S [Department of Physics, University of Puerto Rico, San Juan, PR 00931-3343 (Puerto Rico); Gupta, Vinay [Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India)

2007-10-07

We study the influence of Mn doping on the vibrational properties of rf sputtered ZnO thin films. Raman spectra of the Mn doped ZnO samples reveal two additional vibrational modes, in addition to the host phonon modes, at 252 and 524 cm{sup -1}. The intensity of the additional modes increases continuously with Mn concentration in ZnO and can be used as an indication of Mn incorporation in ZnO. The modes are assigned to the activation of ZnO silent modes due to relaxation of Raman selection rules produced by the breakdown of the translational symmetry of the crystal lattice with the incorporation of Mn at the Zn site. Furthermore, the A{sub 1} (LO) mode is observed with very high intensity in the Raman spectra of undoped ZnO thin film and is attributed to the built-in electric field at the grain boundaries.

Defect induced activation of Raman silent modes in rf co-sputtered Mn doped ZnO thin films

International Nuclear Information System (INIS)

Yadav, Harish Kumar; Sreenivas, K; Katiyar, R S; Gupta, Vinay

2007-01-01

We study the influence of Mn doping on the vibrational properties of rf sputtered ZnO thin films. Raman spectra of the Mn doped ZnO samples reveal two additional vibrational modes, in addition to the host phonon modes, at 252 and 524 cm -1 . The intensity of the additional modes increases continuously with Mn concentration in ZnO and can be used as an indication of Mn incorporation in ZnO. The modes are assigned to the activation of ZnO silent modes due to relaxation of Raman selection rules produced by the breakdown of the translational symmetry of the crystal lattice with the incorporation of Mn at the Zn site. Furthermore, the A 1 (LO) mode is observed with very high intensity in the Raman spectra of undoped ZnO thin film and is attributed to the built-in electric field at the grain boundaries

Development of transparent conductive indium and fluorine co-doped ZnO thin films: Effect of F concentration and post-annealing temperature

Energy Technology Data Exchange (ETDEWEB)

Hadri, A. [University Mohammed V, Faculty of Sciences, Physics Department, LPM, B.P. 1014, Rabat (Morocco); Taibi, M. [University of Mohammed V, LPCMIN, Ecole Normale Superieure, Rabat (Morocco); Loghmarti, M.; Nassiri, C.; Slimani Tlemçani, T. [University Mohammed V, Faculty of Sciences, Physics Department, LPM, B.P. 1014, Rabat (Morocco); Mzerd, A., E-mail: mzerd@yahoo.fr [University Mohammed V, Faculty of Sciences, Physics Department, LPM, B.P. 1014, Rabat (Morocco)

2016-02-29

In the present work ZnO, In doped ZnO and In-F co-doped ZnO (IFZO) films were synthesized on heated glass substrates (350 °C) by the chemical spray technique. The effect of fluorine concentration on the structural, morphological, optical and electrical properties was studied. It was observed from X-ray diffraction (XRD) that the films have a polycrystalline structure and the intensity of the peaks depend on the doping and co-doping concentration. No diffraction peak related to dopants in XRD patterns along with shift in peaks angles to ZnO proved that In and F ions were doped into ZnO thin films. The Raman spectra confirm the hexagonal structure of the as-deposited films, and demonstrated an enhancement of the surface phonon mode of doped and co-doped films as compared to undoped films. The as-deposited films showed an average transmittance above 70%, in the wavelength range of 400–800 nm. A minimum electrical resistivity, in the order of 5.2 × 10{sup −} {sup 2} Ω cm was obtained for the IFZO thin film with 5 at.% F doping. Moreover, the electrical properties of doped and co-doped films were enhanced after post-deposition annealing. It was found that post-annealed thin films at 350 °C showed a decrease of one order of magnitude of the resistivity values. Such a transparent and conducting thin film can be suitable for optical and electrical applications owing to their low resistivity combined with high transmittance in the visible range. - Highlights: • Conductive transparent ZnO, IZO, IFZO thin films were deposited by spray pyrolysis. • Doping and co-doping affect morphology and optoelectrical properties. • As deposited film with high fluorine content exhibited high carrier mobility (55 cm{sup 2} V{sup −} {sup 1} s{sup −} {sup 1}). • Correlation between intrinsic defects and carrier mobility was observed. • Post-annealing in Ar atmosphere improves conductivity.

Preparation of cadmium-doped ZnO thin films by SILAR and their ...

Indian Academy of Sciences (India)

Cadmium-doped zinc oxide (Cd : ZnO) thin films were deposited from sodium zincate bath .... of complex ion on the substrate followed by reaction of the .... Intensity (a.u.). 0. 500 .... trum confirmed the presence of Zn, O and Cd elements in the.

Highly transparent and conductive Sn/F and Al co-doped ZnO thin films prepared by sol–gel method

International Nuclear Information System (INIS)

Pan, Zhanchang; Luo, Junming; Tian, Xinlong; Wu, Shoukun; Chen, Chun; Deng, Jianfeng; Xiao, Chumin; Hu, Guanghui; Wei, Zhigang

2014-01-01

Highlights: • F/Sn and Al co-doped ZnO thin films were synthesized by sol–gel method. • The co-doped nanocrystals exhibit good crystal quality. • The origin of the photoluminescence emissions was discussed. • The films showed high transmittance and low resistivity. -- Abstract: Al doped ZnO, Al–Sn co-doped ZnO and Al–F co-doped ZnO nanocrystals were successfully synthesized onto glass substrates by the sol–gel method. The structure and morphology of the films are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and high resolution transmission electron microscopy (HRTEM). The results indicated that all the films were polycrystalline with a hexagonal wurtzite structure and exhibited a c-axis preferred orientation. The electrical and optical properties were also investigated by 4-point probe device and Uv–vis spectroscopy, room temperature photoluminescence (PL) and Raman spectrum (Raman), respectively. The PL and Raman results suggested that the co-doped films with a very low defect concentration and exhibit a better crystallinity than AZO thin films. The XPS study confirmed the incorporation of Al, Sn and F ions in the ZnO lattice

Influence of Al doping on structural and optical properties of Mg–Al co-doped ZnO thin films prepared by sol–gel method

International Nuclear Information System (INIS)

Fang, Dongyu; Lin, Kui; Xue, Tao; Cui, Can; Chen, Xiaoping; Yao, Pei; Li, Huijun

2014-01-01

Highlights: • Mg–Al co-doped ZnO thin films were prepared by sol–gel spin coating method. • The effects of Al doping on structural and optical properties of AMZO thin films were investigated. • The EDS spectra confirmed presence of Mg and Al elements in AMZO thin films. • The optical band gap of AMZO thin films increased with Al doping concentration increased. • The origin of the photoluminescence emissions was discussed. -- Abstract: Mg–Al co-doped ZnO (AMZO) thin films were successfully deposited onto quartz glass substrates by sol–gel spin coating method. The structure, surface morphology, composition, optical transmittance, and photoluminescence properties of AMZO thin films were characterized through X-ray diffraction, scanning electron microscopy with energy dispersive X-ray spectroscopy (EDS), transmission electron microscopy, UV–VIS–NIR spectrophotometry, and fluorescence spectrophotometry. The results indicated that AMZO thin films exhibited preferred orientation growth along the c-axis, and the full width at half maximum of the (0 0 2) diffraction peak decreased first and subsequently increased, reaching a minimum of approximately 0.275° at 3% Al content. The calculated crystallite size increased from 30.21 nm to 40.73 nm. Al doping content increased from 1% to 3% and subsequently reached 19.33 nm for Al doping content at 5%. The change in lattice parameters was demonstrated by the c/a ratio, residual stress, bond length, and volume per unit cell. EDS analysis confirmed the presence of Mg and Al elements in ZnO thin films. The atomic percentage of Mg and Al elements was nearly equal to their nominal stoichiometry within the experimental error. In addition, the optical transmittance of AMZO thin films was over 85% in the visible region, and the optical band gap increased with increasing Al doping concentration. Room temperature photoluminescence showed ultraviolet emission peak and defect emission peak. The defect emission peak of

Effects of Annealing Temperature on Properties of Ti-Ga-Doped ZnO Films Deposited on Flexible Substrates.

Science.gov (United States)

Chen, Tao-Hsing; Chen, Ting-You

2015-11-03

An investigation is performed into the optical, electrical, and microstructural properties of Ti-Ga-doped ZnO films deposited on polyimide (PI) flexible substrates and then annealed at temperatures of 300 °C, 400 °C, and 450 °C, respectively. The X-ray diffraction (XRD) analysis results show that all of the films have a strong (002) Ga doped ZnO (GZO) preferential orientation. As the annealing temperature is increased to 400 °C, the optical transmittance increases and the electrical resistivity decreases. However, as the temperature is further increased to 450 °C, the transmittance reduces and the resistivity increases due to a carbonization of the PI substrate. Finally, the crystallinity of the ZnO film improves with an increasing annealing temperature only up to 400 °C and is accompanied by a smaller crystallite size and a lower surface roughness.

Synthesis, microstructural characterization and optical properties of undoped, V and Sc doped ZnO thin films

International Nuclear Information System (INIS)

Amezaga-Madrid, P.; Antunez-Flores, W.; Ledezma-Sillas, J.E.; Murillo-Ramirez, J.G.; Solis-Canto, O.; Vega-Becerra, O.E.; Martinez-Sanchez, R.; Miki-Yoshida, M.

2011-01-01

Research highlights: → Undoped, V and Sc doped ZnO thin films by Aerosol Assisted Chemical Vapour Deposition. → Optimum substrate temperatures of 673 K and 623 K for Sc and V doped films. → Around one third of the dopants in solution were deposited into the films. → Crystallite and grain size decreased with the increase of dopant concentration. → Optical band gap increased from 3.29 to 3.32 eV for undoped to 7 Sc/Zn at. %. - Abstract: Many semiconductor oxides (ZnO, TiO 2 , SnO 2 ) when doped with a low percentage of non-magnetic (V, Sc) or magnetic 3d (Co, Mn, Ni, Fe) cation behave ferromagnetically. They have attracted a great deal of interest due to the integration of semiconducting and magnetic properties in a material. ZnO is one of the most promising materials to carry out these tasks in view of the fact that it is optically transparent and has n or p type conductivity. Here, we report the synthesis, microstructural characterization and optical properties of undoped, V and Sc doped zinc oxide thin films. ZnO based thin films with additions of V and Sc were deposited by the Aerosol Assisted Chemical Vapour Deposition method. V and Sc were incorporated separately in the precursor solution. The films were uniform, transparent and non-light scattering. The microstructure of the films was characterized by Grazing Incidence X-ray Diffraction, Scanning Electron Microscopy, and Scanning Probe Microscopy. Average grain size and surface rms roughness were estimated by the measurement of Atomic Force Microscopy. The microstructure of doped ZnO thin films depended on the type and amount of dopant material incorporated. The optical properties were determined from specular reflectance and transmittance spectra. Results were analyzed to determine the optical constant and band gap of the films. An increase in the optical band gap with the content of Sc dopant was obtained.

Enhancing the Performance of Quantum Dot Light-Emitting Diodes Using Room-Temperature-Processed Ga-Doped ZnO Nanoparticles as the Electron Transport Layer

KAUST Repository

Cao, Sheng

2017-04-19

Colloidal ZnO nanoparticle (NP) films are recognized as efficient electron transport layers (ETLs) for quantum dot light-emitting diodes (QD-LEDs) with good stability and high efficiency. However, because of the inherently high work function of such films, spontaneous charge transfer occurs at the QD/ZnO interface in such a QD-LED, thus leading to reduced performance. Here, to improve the QD-LED performance, we prepared Ga-doped ZnO NPs with low work functions and tailored band structures via a room-temperature (RT) solution process without the use of bulky organic ligands. We found that the charge transfer at the interface between the CdSe/ZnS QDs and the doped ZnO NPs was significantly weakened because of the incorporated Ga dopants. Remarkably, the as-assembled QD-LEDs, with Ga-doped ZnO NPs as the ETLs, exhibited superior luminances of up to 44 000 cd/m2 and efficiencies of up to 15 cd/A, placing them among the most efficient red-light QD-LEDs ever reported. This discovery provides a new strategy for fabricating high-performance QD-LEDs by using RT-processed Ga-doped ZnO NPs as the ETLs, which could be generalized to improve the efficiency of other optoelectronic devices.

Effect of Co doping concentration on structural properties and optical parameters of Co-doped ZnO thin films by sol-gel dip-coating method.

Science.gov (United States)

Nam, Giwoong; Yoon, Hyunsik; Kim, Byunggu; Lee, Dong-Yul; Kim, Jong Su; Leem, Jae-Young

2014-11-01

The structural and optical properties of Co-doped ZnO thin films prepared by a sol-gel dip-coating method were investigated. X-ray diffraction analysis showed that the thin films were grown with a c-axis preferred orientation. The position of the (002) peak was almost the same in all samples, irrespective of the Co concentration. It is thus clear that Co doping had little effect on the position of the (002) peak. To confirm that Co2+ was substituted for Zn2+ in the wurtzite structure, optical measurements were conducted at room temperature by a UV-visible spectrometer. Three absorption peaks are apparent in the Co-doped ZnO thin films that do not appear for the undoped ZnO thin film. As the Co concentration was increased, absorption related to characteristic Co2+ transitions increased because three absorption band intensities and the area underneath the absorption wells between 500 and 700 nm increased with increasing Co concentration. The optical band gap and static dielectric constant decreased and the Urbach energy and extinction coefficient increased with increasing Co concentration.

Effects of Doping Concentration on the Structural and Optical Properties of Spin-Coated In-doped ZnO Thin Films Grown on Thermally Oxidized ZnO Film/ZnO Buffer Layer/Mica Substrate

Energy Technology Data Exchange (ETDEWEB)

Kim, Byunggu; Leem, Jae-Young [Inje University, Gimhae (Korea, Republic of)

2017-01-15

ZnO buffer layers were deposited on mica substrates using a sol-gel spin coating method. Then, a thin film of metallic Zn was deposited onto the ZnO buffer layer/mica substrate using a thermal evaporator, and the deposited Zn thin films were then thermally oxidized in a furnace at 500 ℃ for 2 h in air. Finally, In-doped ZnO (IZO) thin films with different In concentrations were grown on the oxidized ZnO film/ZnO buffer layer/mica substrates using the sol-gel spin-coating method. All the IZO films showed ZnO peaks with similar intensities. The full width at half maximum values of the ZnO (002) peak for the IZO thin films decreased with an increase in the In concentration to 1 at%, because the crystallinity of the films was enhanced. However, a further increase in the In concentration caused the crystal quality to degrade. This might be attributed to the fact that the higher In doping resulted in an increase in the number of ionized impurities. The Urbach energy (EU) values of the IZO thin film decreased with an increase in the In concentration to 1 at % because of the enhanced crystal quality of the films. The EU values for the IZO thin films increased with the In concentration from 1 at%to 3 at%, reflecting the broadening of localized band tail state near the conduction band edge of the films.

Effects of Doping Concentration on the Structural and Optical Properties of Spin-Coated In-doped ZnO Thin Films Grown on Thermally Oxidized ZnO Film/ZnO Buffer Layer/Mica Substrate

International Nuclear Information System (INIS)

Kim, Byunggu; Leem, Jae-Young

2017-01-01

ZnO buffer layers were deposited on mica substrates using a sol-gel spin coating method. Then, a thin film of metallic Zn was deposited onto the ZnO buffer layer/mica substrate using a thermal evaporator, and the deposited Zn thin films were then thermally oxidized in a furnace at 500 ℃ for 2 h in air. Finally, In-doped ZnO (IZO) thin films with different In concentrations were grown on the oxidized ZnO film/ZnO buffer layer/mica substrates using the sol-gel spin-coating method. All the IZO films showed ZnO peaks with similar intensities. The full width at half maximum values of the ZnO (002) peak for the IZO thin films decreased with an increase in the In concentration to 1 at%, because the crystallinity of the films was enhanced. However, a further increase in the In concentration caused the crystal quality to degrade. This might be attributed to the fact that the higher In doping resulted in an increase in the number of ionized impurities. The Urbach energy (EU) values of the IZO thin film decreased with an increase in the In concentration to 1 at % because of the enhanced crystal quality of the films. The EU values for the IZO thin films increased with the In concentration from 1 at%to 3 at%, reflecting the broadening of localized band tail state near the conduction band edge of the films.

Dopant-driven enhancements in the optoelectronic properties of laser ablated ZnO: Ga thin films

Science.gov (United States)

Hassan, Ali; Jin, Yuhua; Chao, Feng; Irfan, Muhammad; Jiang, Yijian

2018-04-01

Theoretically and experimentally evaluated optoelectronic properties of GZO (Ga-doped zinc oxide) were correlated in the present article. Density functional theory and Hubbard U (DFT + Ud + Up) first-principle calculations were used for the theoretical study. The pulsed laser deposition technique was used to fabricate GZO thin films on p-GaN, Al2O3, and p-Si substrates. X-ray diffraction graphs show single crystal growth of GZO thin films with (002) preferred crystallographic orientation. The chemical composition was studied via energy dispersive X-ray spectroscopy, and no other unwanted impurity-related peaks were found, which indicated the impurity-free thin film growth of GZO. Field emission scanning electron microscopic micrographs revealed noodle-, seed-, and granular-like structures of GZO/GaN, GZO/Al2O3, and GZO/Si, respectively. Uniform growth of GZO/GaN was found due to fewer mismatches between ZnO and GaN (0.09%). Hall effect measurements in the van der Pauw configuration were used to check electrical properties. The highest mobility (53 cm2/Vs) with a high carrier concentration was found with low laser shots (1800). A 5-fold photoluminescence enhancement in the noodle-like structure of GZO/GaN compared with GZO/Al2O3 and GZO/Si was detected. This points toward shape-driven optical properties because the noodle-like structure is more favorable for optical enhancements in GZO thin films. Theoretical (3.539 eV) and experimental (3.54 eV) values of the band-gap were also found to be comparable. Moreover, the lowest resistivity (3.5 × 10-4 Ωcm) with 80% transmittance is evidence that GZO is a successful alternate of ITO.

Influence of lithium doping on the structural and electrical characteristics of ZnO thin films

Energy Technology Data Exchange (ETDEWEB)

Johny, T. Anto [Centre for Materials for Electronics Technology (C-MET), (Department of Information Technology, Scientific Society, Ministry of Communication and Information Technology, Govt. of India), Athani - PO, Thrissur, 680 581 Kerala (India); Kumar, Viswanathan, E-mail: vkumar10@yahoo.com [Centre for Materials for Electronics Technology (C-MET), (Department of Information Technology, Scientific Society, Ministry of Communication and Information Technology, Govt. of India), Athani - PO, Thrissur, 680 581 Kerala (India); Imai, Hideyuki; Kanno, Isaku [Micro Engineering, Kyoto University, Kyoto 606-8501 (Japan)

2012-06-30

Thin films of undoped and lithium-doped Zinc oxide, (Zn{sub 1-x}Li{sub x})O; x = 0, 0.05, 0.10 and 0.20 were prepared by sol-gel method using spin-coating technique on silicon substrates [(111)Pt/Ti/SiO{sub 2}/Si)]. The influence of lithium doping on the structural, electrical and microstructural characteristics have been investigated by means of X-ray diffraction, leakage current, piezoelectric measurements and scanning electron microscopy. The resistivity of the ZnO film is found to increase markedly with low levels (x {<=} 0.05) of lithium doping thereby enhancing their piezoelectric applications. The transverse piezoelectric coefficient, e{sub 31}{sup Low-Asterisk} has been determined for the thin films having the composition (Zn{sub 0.95}Li{sub 0.05})O, to study their suitability for piezoelectric applications. - Highlights: Black-Right-Pointing-Pointer Preferentially c-axis oriented (Zn{sub 1-x}Li{sub x})O films were spin-coated on glass. Black-Right-Pointing-Pointer (Zn{sub 1-x}Li{sub x})O thin films exhibit dense columnar microstructure. Black-Right-Pointing-Pointer Low levels of lithium doping, increases the electrical resistivity of ZnO thin films. Black-Right-Pointing-Pointer (Zn{sub 1-x}Li{sub x})O thin films show high values of transverse piezoelectric coefficient, e{sup Low-Asterisk }{sub 31}.

Cation vacancies and electrical compensation in Sb-doped thin-film SnO2 and ZnO

International Nuclear Information System (INIS)

Korhonen, E; Prozheeva, V; Tuomisto, F; Bierwagen, O; Speck, J S; White, M E; Galazka, Z; Liu, H; Izyumskaya, N; Avrutin, V; Özgür, Ü; Morkoç, H

2015-01-01

We present positron annihilation results on Sb-doped SnO 2 and ZnO thin films. The vacancy types and the effect of vacancies on the electrical properties of these intrinsically n-type transparent semiconducting oxides are studied. We find that in both materials low and moderate Sb-doping leads to formation of vacancy clusters of variable sizes. However, at high doping levels cation vacancy defects dominate the positron annihilation signal. These defects, when at sufficient concentrations, can efficiently compensate the n-type doping produced by Sb. This is the case in ZnO, but in SnO 2 the concentrations appear too low to cause significant compensation. (invited article)

Cation vacancies and electrical compensation in Sb-doped thin-film SnO2 and ZnO

Science.gov (United States)

Korhonen, E.; Prozheeva, V.; Tuomisto, F.; Bierwagen, O.; Speck, J. S.; White, M. E.; Galazka, Z.; Liu, H.; Izyumskaya, N.; Avrutin, V.; Özgür, Ü.; Morkoç, H.

2015-02-01

We present positron annihilation results on Sb-doped SnO2 and ZnO thin films. The vacancy types and the effect of vacancies on the electrical properties of these intrinsically n-type transparent semiconducting oxides are studied. We find that in both materials low and moderate Sb-doping leads to formation of vacancy clusters of variable sizes. However, at high doping levels cation vacancy defects dominate the positron annihilation signal. These defects, when at sufficient concentrations, can efficiently compensate the n-type doping produced by Sb. This is the case in ZnO, but in SnO2 the concentrations appear too low to cause significant compensation.

Influences of oxygen gas flow rate on electrical properties of Ga-doped ZnO thin films deposited on glass and sapphire substrates

International Nuclear Information System (INIS)

Makino, Hisao; Song, Huaping; Yamamoto, Tetsuya

2014-01-01

The Ga-doped ZnO (GZO) films deposited on glass and c-plane sapphire substrates have been comparatively studied in order to explore the role of grain boundaries in electrical properties. The influences of oxygen gas flow rates (OFRs) during the deposition by ion-plating were examined. The dependences of carrier concentration, lattice parameters, and characteristic of thermal desorption of Zn on the OFR showed common features between glass and sapphire substrates, however, the Hall mobility showed different behavior. The Hall mobility of GZO films on glass increased with increasing OFR of up to 15 sccm, and decreased with further increasing OFR. On the other hand, the Hall mobility of GZO films on c-sapphire increased for up to 25 sccm. The role of grain boundary in polycrystalline GZO films has been discussed. - Highlights: • Ga-doped ZnO films were deposited on glass and c-sapphire by ion-plating. • The epitaxial growth on c-sapphire was confirmed by X-ray diffraction. • Dependence of Hall mobility showed different tendency between glass and sapphire. • Grain boundaries influence transport properties at high O 2 gas flow rate

Fabrication of p-type conductivity in SnO{sub 2} thin films through Ga doping

Energy Technology Data Exchange (ETDEWEB)

Tsay, Chien-Yie, E-mail: cytsay@fcu.edu.tw; Liang, Shan-Chien

2015-02-15

Highlights: • P-type Ga-doped SnO{sub 2} semiconductor films were prepared by sol-gel spin coating. • Optical bandgaps of the SnO{sub 2}:Ga films are narrower than that of the SnO{sub 2} film. • SnO{sub 2}:Ga films exhibited p-type conductivity as Ga doping content higher than 10%. • A p-n heterojunction composed of p-type SnO{sub 2}:Ga and n-type ZnO:Al was fabricated. - Abstract: P-type transparent tin oxide (SnO{sub 2}) based semiconductor thin films were deposited onto alkali-free glass substrates by a sol-gel spin-coating method using gallium (Ga) as acceptor dopant. In this study, we investigated the influence of Ga doping concentration ([Ga]/[Sn] + [Ga] = 0%, 5%, 10%, 15%, and 20%) on the structural, optical and electrical properties of SnO{sub 2} thin films. XRD analysis results showed that dried Ga-doped SnO{sub 2} (SnO{sub 2}:Ga) sol-gel films annealed in oxygen ambient at 520 °C for 1 h exhibited only the tetragonal rutile phase. The average optical transmittance of as-prepared thin film samples was higher than 87.0% in the visible light region; the optical band gap energy slightly decreased from 3.92 eV to 3.83 eV with increases in Ga doping content. Hall effect measurement showed that the nature of conductivity of SnO{sub 2}:Ga thin films changed from n-type to p-type when the Ga doping level was 10%, and when it was at 15%, Ga-doped SnO{sub 2} thin films exhibited the highest mean hole concentration of 1.70 × 10{sup 18} cm{sup -3}. Furthermore, a transparent p-SnO{sub 2}:Ga (Ga doping level of 15%)/n-ZnO:Al (Al doping level of 2%) heterojunction was fabricated on alkali-free glass. The I-V curve measurement for the p-n heterojunction diode showed a typical rectifying characteristic with a forward turn-on voltage of 0.65 V.

Probing magnetism and electronic structure of Fe-doped ZnO thin films

International Nuclear Information System (INIS)

El Amiri, A.; Moubah, R.; Lmai, F.; Abid, M.; Hassanain, N.; Hlil, E.K.; Lassri, H.

2016-01-01

Ab-initio calculations using Korringa–Kohn–Rostoker method combined with the coherent potential approximation were performed in order to study the magnetic properties of Fe-doped ZnO thin films with different Fe contents. The extracted parameters are compared with those determined experimentally. Based on total and partial densities of state curves, we demonstrate that there is a competition between p–d exchange and superexchange mechanisms leading to weak ferromagnetic and antiferromagnetic contributions, respectively. The dominant mechanism is found to be antiferromagnetic. However, with increasing Fe content the ferromagnetic contribution increases. In addition, the effect of structural defects on the magnetism of the system is reported. It is shown that both Zn and O vacancies increase ferromagnetism, which is more pronounced in case of Zn. - Highlights: • The KKR–CPA approach was used to study the magnetism of Fe-doped ZnO thin films. • There is a competition between p–d exchange and superexchange mechanisms leading to weak ferromagnetic and antiferromagnetic contributions. • Zn vacancies are more significant than the O ones for obtaining ferromagnetism.

Probing magnetism and electronic structure of Fe-doped ZnO thin films

Energy Technology Data Exchange (ETDEWEB)

El Amiri, A., E-mail: aelamiri@casablanca.ma [LPFA, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco); Moubah, R., E-mail: reda.moubah@hotmail.fr [LPMMAT, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco); Lmai, F. [LPTA, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco); Abid, M. [LPFA, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco); Hassanain, N. [Laboratoire de Physique des Matériaux, Faculté des Sciences, BP 1014 Rabat (Morocco); Hlil, E.K. [Institut Néel, CNRS et Université Joseph Fourier, BP 166, 38042 Grenoble (France); Lassri, H. [LPMMAT, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco)

2016-01-15

Ab-initio calculations using Korringa–Kohn–Rostoker method combined with the coherent potential approximation were performed in order to study the magnetic properties of Fe-doped ZnO thin films with different Fe contents. The extracted parameters are compared with those determined experimentally. Based on total and partial densities of state curves, we demonstrate that there is a competition between p–d exchange and superexchange mechanisms leading to weak ferromagnetic and antiferromagnetic contributions, respectively. The dominant mechanism is found to be antiferromagnetic. However, with increasing Fe content the ferromagnetic contribution increases. In addition, the effect of structural defects on the magnetism of the system is reported. It is shown that both Zn and O vacancies increase ferromagnetism, which is more pronounced in case of Zn. - Highlights: • The KKR–CPA approach was used to study the magnetism of Fe-doped ZnO thin films. • There is a competition between p–d exchange and superexchange mechanisms leading to weak ferromagnetic and antiferromagnetic contributions. • Zn vacancies are more significant than the O ones for obtaining ferromagnetism.

Synthesis of highly conductive thin-walled Al-doped ZnO single-crystal microtubes by a solid state method

Science.gov (United States)

Hu, Shuopeng; Wang, Yue; Wang, Qiang; Xing, Cheng; Yan, Yinzhou; Jiang, Yijian

2018-06-01

ZnO has attracted considerable attention in fundamental studies and practical applications for the past decade due to its outstanding performance in gas sensing, photocatalytic degradation, light harvesting, UV-light emitting/lasing, etc. The large-sized thin-walled ZnO (TW-ZnO) microtube with stable and rich VZn-related acceptors grown by optical vapor supersaturated precipitation (OVSP) is a novel multifunctional optoelectronic material. Unfortunately, the OVSP cannot achieve doping due to the vapor growth process. To obtain doped TW-ZnO microtubes, a solid state method is introduced in this work to achieve thin-walled Al-doping ZnO (TW-ZnO:Al) microtubes with high electrical conductivity. The morphology and microstructures of ZnO:Al microtubes are similar to undoped ones. The Al3+ ions are confirmed to substitute Zn2+ sites and Zn(0/-1) vacancies in the lattice of ZnO by EDS, XRD, Raman and temperature-dependent photoluminescence analyses. The Al dopant acting as a donor level offers massive free electrons to increase the carrier concentrations. The resistivity of the ZnO:Al microtube is reduced down to ∼10-3 Ω·cm, which is one order of magnitude lower than that of the undoped microtube. The present work provides a simple way to achieve doped ZnO tubular components for potential device applications in optoelectronics.

Growth of Cu2O on Ga-doped ZnO and their interface energy alignment for thin film solar cells

International Nuclear Information System (INIS)

Wong, L. M.; Chiam, S. Y.; Wang, S. J.; Pan, J. S.; Huang, J. Q.; Chim, W. K.

2010-01-01

Cu 2 O thin films are deposited by direct current reactive magnetron sputtering on borofloat glass and indium tin oxide (ITO) coated glass at room temperature. The effect of oxygen partial pressure on the structures and properties of Cu 2 O thin films are investigated. We show that oxygen partial pressure is a crucial parameter in achieving pure phases of CuO and Cu 2 O. Based on this finding, we fabricate heterojunctions of p-type Cu 2 O with n-type gallium doped ZnO (GZO) on ITO coated glass substrates by pulsed laser deposition for GZO thin films. The energy band alignment for thin films of Cu 2 O/GZO on ITO glass is characterized using high-resolution x-ray photoelectron spectroscopy. The energy band alignment for the Cu 2 O/GZO heterojunctions is determined to be type II with a valence band offset of 2.82 eV and shows negligible effects of variation with gallium doping. The higher conduction band of the Cu 2 O relative to that of GZO in the obtained band alignment shows that the heterojunctions are suitable for solar cell application based on energy levels consideration.

A simplified approach to the band gap correction of defect formation energies: Al, Ga, and In-doped ZnO

Science.gov (United States)

Saniz, R.; Xu, Y.; Matsubara, M.; Amini, M. N.; Dixit, H.; Lamoen, D.; Partoens, B.

2013-01-01

The calculation of defect levels in semiconductors within a density functional theory approach suffers greatly from the band gap problem. We propose a band gap correction scheme that is based on the separation of energy differences in electron addition and relaxation energies. We show that it can predict defect levels with a reasonable accuracy, particularly in the case of defects with conduction band character, and yet is simple and computationally economical. We apply this method to ZnO doped with group III elements (Al, Ga, In). As expected from experiment, the results indicate that Zn substitutional doping is preferred over interstitial doping in Al, Ga, and In-doped ZnO, under both zinc-rich and oxygen-rich conditions. Further, all three dopants act as shallow donors, with the +1 charge state having the most advantageous formation energy. Also, doping effects on the electronic structure of ZnO are sufficiently mild so as to affect little the fundamental band gap and lowest conduction bands dispersion, which secures their n-type transparent conducting behavior. A comparison with the extrapolation method based on LDA+U calculations and with the Heyd-Scuseria-Ernzerhof hybrid functional (HSE) shows the reliability of the proposed scheme in predicting the thermodynamic transition levels in shallow donor systems.

Sputter deposited gallium doped ZnO for TCO applications

Energy Technology Data Exchange (ETDEWEB)

Dietrich, Marc; Kronenberger, Achim; Polity, Angelika; Meyer, Bruno [I. Physikalisches Institut, Justus Liebig Universitaet Giessen (Germany); Blaesing, Juergen; Krost, Alois [FNW/IEP/AHE, Otto-von-Guericke Universitaet Magdeburg (Germany)

2010-07-01

Transparent conducting oxides to be used for flat panel or display applications should exhibit low electrical resistivity in line with a high optical transmission in the visible spectral range. Today indium-tin-oxide is the material which meets these requirements best. However, the limited availability of indium makes it useful to search for alternatives and ZnO doped with group III elements are promising candidates. While the Al doping in high concentrations causes problems due to the formation of insulating Al-oxides, Gallium related oxides are typically n-type conducting wide band gap semiconductors. Therefore we deposited Gallium doped ZnO thin films on quartz and sapphire substrates by radio frequency magnetron sputtering with a ZnO/Ga{sub 2}O{sub 3}(3at%) composite target. The substrate temperature and the oxygen flow during the sputtering process were varied to optimise the layer properties. Introducing oxygen to the sputtering gas allowed to vary the resistivity of the films by three orders of magnitude from about 1 {omega}cm down to less than 1 m{omega}cm.

Theoretical investigation of electronic, magnetic and optical properties of Fe doped GaN thin films

International Nuclear Information System (INIS)

Salmani, E.; Mounkachi, O.; Ez-Zahraouy, H.; Benyoussef, A.; Hamedoun, M.; Hlil, E.K.

2013-01-01

Highlights: •Magnetic and optical properties Fe-doped GaN thin films are studied using DFT. •The band gaps of GaN thin films are larger than the one of the bulk. •The layer thickness and acceptor defect can switch the magnetic ordering. -- Abstract: Using first principles calculations based on spin-polarized density functional theory, the magnetic and optical properties of GaN and Fe-doped GaN thin films with and without acceptor defect is studied. The band structure calculations show that the band gaps of GaN thin films with 2, 4 and 6 layers are larger than the one of the bulk with wurtzite structure and decreases with increasing the film thickness. In Fe doped GaN thin films, we show that layer of thickness and acceptor defect can switch the magnetic ordering from disorder local moment (DLM) to ferromagnetic (FM) order. Without acceptor defect Fe doped GaN exhibits spin glass phase in 4 layers form and ferromagnetic state for 2 layers form of the thin films, while it exhibits ferromagnetic phase with acceptor defect such as vacancies defect for 2 and 4 layers. In the FM ordering, the thin films is half-metallic and is therefore ideal for spin application. The different energy between ferromagnetic state and disorder local moment state was evaluated. Moreover, the optical absorption spectra obtained by ab initio calculations confirm the ferromagnetic stability based on the charge state of magnetic impurities

Friction and wear behavior of nitrogen-doped ZnO thin films deposited via MOCVD under dry contact

Directory of Open Access Journals (Sweden)

U.S. Mbamara

2016-06-01

Full Text Available Most researches on doped ZnO thin films are tilted toward their applications in optoelectronics and semiconductor devices. Research on their tribological properties is still unfolding. In this work, nitrogen-doped ZnO thin films were deposited on 304 L stainless steel substrate from a combination of zinc acetate and ammonium acetate precursor by MOCVD technique. Compositional and structural studies of the films were done using Rutherford Backscattering Spectroscopy (RBS and X-ray Diffraction (XRD. The frictional behavior of the thin film coatings was evaluated using a ball-on-flat configuration in reciprocating sliding under dry contact condition. After friction test, the flat and ball counter-face surfaces were examined to assess the wear dimension and failure mechanism. Both friction behavior and wear (in the ball counter-face were observed to be dependent on the crystallinity and thickness of the thin film coatings.

Defect-band mediated ferromagnetism in Gd-doped ZnO thin films

KAUST Repository

Venkatesh, S.

2015-01-07

Gd-doped ZnO thin films prepared by pulsed laser deposition with Gd concentrations varying from 0.02–0.45 atomic percent (at. %) showed deposition oxygen pressure controlled ferromagnetism. Thin films prepared with Gd dopant levels (

Effect of dopants and thermal treatment on properties of Ga-Al-ZnO thin films fabricated by hetero targets sputtering system

International Nuclear Information System (INIS)

Hong, JeongSoo; Matsushita, Nobuhiro; Kim, KyungHwan

2013-01-01

In this study, we fabricated Ga and Al doped ZnO (Ga-Al-ZnO; GAZO) thin films by using the facing targets sputtering system under various conditions such as input current and thermal treatment temperature. The properties of the as-deposited GAZO thin films were examined by four-point, UV/Vis spectrometry, X-ray diffraction, atomic force microscopy and field-emission scanning electron microscopy. The result showed that the lowest sheet resistance of the films was 59.3 ohm/sq and transmittance was about 85%. After thermal treatment, the properties of GAZO thin films were improved. The lowest sheet resistance (47.3 ohm/sq) of the GAZO thin films were obtained at thermal treatment temperature of 300 °C, considered to be the result of continuous substitutions by dopants and improved crystallinity by the thermal treatment. - Highlights: ► Ga and Al doped ZnO thin films were prepared by hetero targets sputtering system. ► Free electrons were increased due to the continuous substitutions of Ga and Al. ► Crystallinity was improved by recombination of particles with increasing of temperature

Effects of Doping with Al, Ga, and In on Structural and Optical Properties of ZnO Nanorods Grown by Hydrothermal Method

International Nuclear Information System (INIS)

Kim, Soaram; Nam, Giwoong; Park, Hyunggil; Yoon, Hyunsik; Leem, Jaeyoung; Lee, Sangheon; Kim, Jong Su; Kim, Jin Soo; Kim, Do Yeob; Kim, Sungo

2013-01-01

The structural and optical properties of the ZnO, Al-doped ZnO, Ga-doped ZnO, and In-doped ZnO nanorods were investigated using field-emission scanning electron microscopy, X-ray diffraction, photoluminescence (PL) and ultraviolet-visible spectroscopy. All the nanorods grew with good alignment on the ZnO seed layers and the ZnO nanorod dimensions could be controlled by the addition of the various dopants. For instance, the diameter of the nanorods decreased with increasing atomic number of the dopants. The ratio between the near-band-edge emission (NBE) and the deep-level emission (DLE) intensities (I NBE /I DLE ) obtained by PL gradually decreased because the DLE intensity from the nanorods gradually increased with increase in the atomic number of the dopants. We found that the dopants affected the structural and optical properties of the ZnO nanorods including their dimensions, lattice constants, residual stresses, bond lengths, PL properties, transmittance values, optical band gaps, and Urbach energies

Effects of Doping with Al, Ga, and In on Structural and Optical Properties of ZnO Nanorods Grown by Hydrothermal Method

Energy Technology Data Exchange (ETDEWEB)

Kim, Soaram; Nam, Giwoong; Park, Hyunggil; Yoon, Hyunsik; Leem, Jaeyoung [Inje Univ., Gimhae (Korea, Republic of); Lee, Sangheon; Kim, Jong Su [Yeungnam Univ., Gyeongsan (Korea, Republic of); Kim, Jin Soo [Chonbuk National Univ., Jeonju (Korea, Republic of); Kim, Do Yeob; Kim, Sungo [Clemson Univ., Clemson (United States)

2013-04-15

The structural and optical properties of the ZnO, Al-doped ZnO, Ga-doped ZnO, and In-doped ZnO nanorods were investigated using field-emission scanning electron microscopy, X-ray diffraction, photoluminescence (PL) and ultraviolet-visible spectroscopy. All the nanorods grew with good alignment on the ZnO seed layers and the ZnO nanorod dimensions could be controlled by the addition of the various dopants. For instance, the diameter of the nanorods decreased with increasing atomic number of the dopants. The ratio between the near-band-edge emission (NBE) and the deep-level emission (DLE) intensities (I{sub NBE}/I{sub DLE}) obtained by PL gradually decreased because the DLE intensity from the nanorods gradually increased with increase in the atomic number of the dopants. We found that the dopants affected the structural and optical properties of the ZnO nanorods including their dimensions, lattice constants, residual stresses, bond lengths, PL properties, transmittance values, optical band gaps, and Urbach energies.

Doping effect on the optical properties of ZnO nanostructures

Energy Technology Data Exchange (ETDEWEB)

Stoehr, M. [Frederick Seitz Materials Research Laboratory, University of Illinois,104 South Goodwin Avenue, Urbana, IL 61801 (United States); Institut Universitaire de Technologie, Universite de Haute Alsace, 61 rue Albert Camus, 68093 Mulhouse Cedex (France); Juillaguet, S. [Groupe d' Etude des Semi-conducteurs, Universite Montpellier II, Place Eugene Bataillon, 34095 Montpellier Cedex 5 (France); Kyaw, T.M.; Wen, J.G. [Institut Universitaire de Technologie, Universite de Haute Alsace, 61 rue Albert Camus, 68093 Mulhouse Cedex (France)

2007-04-15

High quality undoped and Ga{sub 2}O{sub 3} or In{sub 2}O{sub 3} doped ZnO nanostructures are grown by chemical vapor transport and condensation. The doping effect on the optical properties is investigated by photoluminescence. At room temperature, photoluminescence on Ga{sub 2}O{sub 3} doped ZnO nanostructures reveals an enhancement of the ultraviolet near band edge emission at 390 nm, while the intensity of the deep level emission at 530 nm weakens. At 5 K, an intense neutral-donor-bound exciton (D{sup 0}X) line dominates the undoped and doped ZnO photoluminescence spectra. The presence of well resolved two-electron satellite lines allow to determine the type of donors. At 5 K, the results indicate that ZnO nanostructures grown with 10% of Ga{sub 2}O{sub 3} display an excellent optical quality, proved by an intense D{sup 0}X line, a high intensity ratio between the D{sup 0}X line and the deep level emission as well as the presence of numerous phonon replicas of the main lines. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Title: Using Alignment and 2D Network Simulations to Study Charge Transport Through Doped ZnO Nanowire Thin Film Electrodes

KAUST Repository

Phadke, Sujay

2011-09-30

Factors affecting charge transport through ZnO nanowire mat films were studied by aligning ZnO nanowires on substrates and coupling experimental measurements with 2D nanowire network simulations. Gallium doped ZnO nanowires were aligned on thermally oxidized silicon wafer by shearing a nanowire dispersion in ethanol. Sheet resistances of nanowire thin films that had current flowing parallel to nanowire alignment direction were compared to thin films that had current flowing perpendicular to nanowire alignment direction. Perpendicular devices showed ∼5 fold greater sheet resistance than parallel devices supporting the hypothesis that aligning nanowires would increase conductivity of ZnO nanowire electrodes. 2-D nanowire network simulations of thin films showed that the device sheet resistance was dominated by inter-wire contact resistance. For a given resistivity of ZnO nanowires, the thin film electrodes would have the lowest possible sheet resistance if the inter-wire contact resistance was one order of magnitude lower than the single nanowire resistance. Simulations suggest that the conductivity of such thin film devices could be further enhanced by using longer nanowires. Solution processed Gallium doped ZnO nanowires are aligned on substrates using an innovative shear coating technique. Nanowire alignment has shown improvement in ZnO nanowire transparent electrode conductivity. 2D network simulations in conjunction with electrical measurements have revealed different regimes of operation of nanowire thin films and provided a guideline for improving electrical performance of nanowire electrodes. Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

The electrical, elemental, optical, and surface properties of Si-doped ZnO thin films prepared by thermionic vacuum arc

Science.gov (United States)

Mohammadigharehbagh, Reza; Özen, Soner; Yudar, Hafizittin Hakan; Pat, Suat; Korkmaz, Şadan

2017-09-01

The purpose of this work is to study the properties of Si-doped ZnO (SZO) thin films, which were prepared using the non-reactive thermionic vacuum arc technique. The analysis of the elemental, optical, and surface properties of ZnO:Si thin films was carried out using energy dispersive x-ray spectroscopy, UV-VIS spectrophotometry, atomic force microscopy, and scanning electron microscopy, respectively. The current-voltage measurement was employed in order to study the electrical properties of the films. The effect of Si doping on the physical properties of ZnO films was investigated. The film thicknesses were measured as 55 and 35 nm for glass and PET substrates, respectively. It was clearly observed from the x-ray diffraction results that the Si and ZnO peaks were present in the coated SZO films for all samples. The morphological studies showed that the deposited surfaces are homogenous, dense, and have a uniform surface, with the existence of some cracks only on the glass substrate. The elemental composition has confirmed the existence of Zn, Si, and O elements within the prepared films. Using a UV-VIS spectrophotometer, the optical parameters such as transmittance, absorbance, refractive index, and reflectance were calculated. It should be noted that the transparency and refractive indices obtained from the measurements decrease with increasing Si concentration. The obtained optical bandgap values using transmittance spectra were determined to be 3.74 and 3.84 eV for the glass and PET substrates, respectively. An increase in the bandgap results demonstrates that the Si doping concentration is comparable to the pure ZnO thin films. The current versus voltage curves revealed the ohmic nature of the films. Subsequently, the development and fabrication of excellent transparent conducting electrodes enabled the appropriate use of Si-doped ZnO thin films.

Structural and Optical Properties of Group III Doped Hydrothermal ZnO Thin Films

KAUST Repository

Mughal, Asad J.

2017-01-11

In this work, we employ a simple two-step growth technique to deposit impurity doped heteroepitaxial thin films of (0001) ZnO onto (111) MgAl2O4 spinel substrates through a combination of atomic layer deposition (ALD) and hydrothermal growth. The hydrothermal layer is doped with Al, Ga, and In through the addition of their respective nitrate salts. We evaluated the effect that varying the concentrations of these dopants has on both the structural and optical properties of these films. It was found that the epitaxial ALD layer created a ⟨111⟩MgAl2O4∥⟨0001⟩ZnO out-of-plane orientation and a ⟨1¯1¯2⟩MgAl2O4∥∥⟨011¯0⟩ZnO in-plane orientation between the film and substrate. The rocking curve line widths ranged between 0.75° and 1.80° depending on dopant concentration. The optical bandgap determined through the Tauc method was between 3.28 eV and 3.39 eV and showed a Burstein-Moss shift with increasing dopant concentration.

Structural, Morphological, and LPG Sensing Properties of Al-Doped ZnO Thin Film Prepared by SILAR

Directory of Open Access Journals (Sweden)

Shampa Mondal

2013-01-01

Full Text Available Undoped and aluminum doped zinc oxide (AZO thin films were deposited on glass substrates by successive ion layer adsorption and reaction (SILAR technique from ammonium zincate complex. The thin films are characterized by X-ray diffraction (XRD and scanning electron microscopy (SEM for their structural and morphological studies. Both undoped and Al-doped film show strong preferred c-axis orientation. The texture coefficient (TC of the film along (002 direction increases due to Al incorporation. SEM micrograph shows round shaped particles for pure ZnO. However AZO films show particles with off spherical shape and compact interconnected grains. Sensitivity of the film in presence of 80% LEL (lower explosive limit of LPG increases with temperature and is maximum at 325°C. Significantly high sensitivity of 87% with reasonably fast response was observed for 1% Al-doped ZnO (AZO film in presence of 1.6 vol% LPG at 325°C.

Study of copper doping effects on structural, optical and electrical properties of sprayed ZnO thin films

International Nuclear Information System (INIS)

Mhamdi, A.; Mimouni, R.; Amlouk, A.; Amlouk, M.; Belgacem, S.

2014-01-01

Highlights: • The sprayed Cu-doped ZnO thin layers films were well crystallised in hexagonal wurtzite phase. • Nanoncrystallites on clusters were observed whose density decreases especially at 2% Cu content. • This parallel circuit R–C represents the contribution of the grain boundaries delineating the oriented columnar microcrystallites along c-axis. - Abstract: Copper-doped zinc oxide thin films (ZnO:Cu) at different percentages (1–3%) were deposited on glass substrates using a chemical spray technique. The effect of Cu concentration on the structural, morphology and optical properties of the ZnO:Cu thin films were investigated. XRD analysis revealed that all films consist of single phase ZnO and were well crystallised in würtzite phase with the crystallites preferentially oriented towards (0 0 2) direction parallel to c-axis. The Film surface was analyzed by contact atomic force microscopy (AFM) in order to understand the effect of the doping on the surface structure. Doping by copper resulted in a slight decrease in the optical band gap energy of the films and a noticeably change in optical constants. From the spectroscopy impedance analysis we investigated the frequency relaxation phenomenon and the circuit equivalent circuit of such thin layers. Finally, all results have been discussed in terms of the copper doping concentration

An investigation on the In doping of ZnO thin films by spray pyrolysis

Science.gov (United States)

Mahesh, Devika; Kumar, M. C. Santhosh

2018-04-01

Indium doped zinc oxide (IGZO)thin films are gaining much interest owing to its commercial application as transparent conductive oxide thin films. In the current study thin films indium doped ZnO thin films have been deposited on glass substrates by chemical spray pyrolysis technique with an indium concentration of 1, 2.5 and 4% in Zinc source. The films show a peak shift in the X-Ray Diffraction patterns with varying indium doping concentration. The (101) peak was enhanced for the 2.5 % indium doped films and variation in grain size with the different doping levels was studied. The as-deposited films are uniform and shown high transparency (>90%) in the visible region. Average thicknesses of films are found to be 800nm, calculated using the envelope method. The film with 2.5 % of indium content was found to be highly conducting than the rest, since for the lower and higher concentrations the conductivity was possibly halted by the limit in carrier concentration and indium segregation in the grain boundaries respectively. The enhancement of mobility and carrier concentration was clearly seen in the optimum films.

Photovoltaic Properties of Co-doped ZnO Thin Film on Glass Substrate

International Nuclear Information System (INIS)

Sabia Aye; Zin Ma Ma; May Nwe Oo; Than Than Win; Yin Maung Maung; Ko Ko Kyaw Soe

2011-12-01

Cobalt (Co) 0.4 mol doped zinc oxide (ZnO) fine powder was prepared by solid state mixed oxide route. Phase formation and crystal structure of Co-doped ZnO (CZO) powder were examined by X-ray diffraction (XRD). Scanning Electron Microscopy (SEM) was used to observe the micro structure of Co doped ZnO powder. Energy Dispersive X-ray Fluorescent (EDXRF) technique gave the elemental content of cobalt and zinc. Co-doped ZnO film was formed on glass substrate by spin coating technique. Photovoltaic properties of CZO/glass cell were measured.

Theoretical study of the multiferroic properties in M-doped (M=Co, Cr, Mg) ZnO thin films

Energy Technology Data Exchange (ETDEWEB)

Bahoosh, S.G. [Max Planck Institute of Microstructure Physics, Weinberg 2, 06120 Halle (Germany); Apostolov, A.T. [University of Architecture, Civil Engineering and Geodesy, Faculty of Hydrotechnics, Department of Physics, 1, Hristo Smirnenski Blvd., 1046 Sofia (Bulgaria); Apostolova, I.N. [University of Forestry, Faculty of Forest Industry, 10, Kl. Ohridsky Blvd., 1756 Sofia (Bulgaria); Trimper, S. [Institute of Physics, Martin-Luther-University, D-06099 Halle (Germany); Wesselinowa, Julia M. [University of Sofia, Department of Physics, Blvd. J. Bouchier 5, 1164 Sofia (Bulgaria)

2015-01-01

The origin of multiferroism is still an open problem in ZnO. We propose a microscopic model to clarify the occurrence of multiferroism in this material. Using Green's function technique we study the influence of ion doping and size effects on the magnetization and polarization of ZnO thin films. The calculations for magnetic Co- and Cr-ions are based on the s–d model, the transverse Ising model in terms of pseudo-spins and a biquadratic magnetoelectric coupling, whereas in case of nonmagnetic Mg-ions the model takes into account the Coulomb interaction and an indirect coupling between the pseudo-spins via the conduction electrons. We show that the magnetization M exhibits a maximum for a fixed concentration of the doping ions. Furthermore M increases with decreasing film thickness N. The polarization increases with increasing concentration of the dopant and decreasing N. The results are in good agreement with the experimental data. - Highlights: • The paper analyzes the multiferroic properties of doped ZnO thin films by a microscopic model. • The magnetization exhibits a maximum at a fixed doping concentration. • The polarization increases with growing dopant concentration. • The ferroelectric transition temperature is enhanced for increasing dopant concentration.

Efficiency of Nb-Doped ZnO Nanoparticles Electrode for Dye-Sensitized Solar Cells Application

Science.gov (United States)

Anuntahirunrat, Jirapat; Sung, Youl-Moon; Pooyodying, Pattarapon

2017-09-01

The technological of Dye-sensitized solar cells (DSSCs) had been improved for several years. Due to its simplicity and low cost materials with belonging to the part of thin films solar cells. DSSCs have numerous advantages and benefits among the other types of solar cells. Many of the DSSC devices had use organic chemical that produce by specific method to use as thin film electrodes. The organic chemical that widely use to establish thin film electrodes are Zinc Oxide (ZnO), Titanium Dioxide (TiO2) and many other chemical substances. Zinc oxide (ZnO) nanoparticles had been used in DSSCs applications as thin film electrodes. Nanoparticles are a part of nanomaterials that are defined as a single particles 1-100 nm in diameter. From a few year ZnO widely used in DSSC applications because of its optical, electrical and many others properties. In particular, the unique properties and utility of ZnO structure. However the efficiency of ZnO nanoparticles based solar cells can be improved by doped various foreign impurity to change the structures and properties. Niobium (Nb) had been use as a dopant of metal oxide thin films. Using specification method to doped the ZnO nanoparticles thin film can improved the efficiencies of DSSCs. The efficiencies of Nb-doped ZnO can be compared by doping 0 at wt% to 5 at wt% in ZnO nanoparticles thin films that prepared by the spin coating method. The thin film electrodes doped with 3 at wt% represent a maximum efficiencies with the lowest resistivity of 8.95×10-4 Ω·cm.

Roughness-based monitoring of transparency and conductivity in boron-doped ZnO thin films prepared by spray pyrolysis

International Nuclear Information System (INIS)

Gaikwad, Rajendra S.; Bhande, Sambhaji S.; Mane, Rajaram S.; Pawar, Bhagwat N.; Gaikwad, Sanjay L.; Han, Sung-Hwan; Joo, Oh-Shim

2012-01-01

Graphical abstract: Display Omitted Highlights: ► We report surface roughness dependent transparency and conductivity in ZnO films. ► The surface roughness with respected to boron doping concentrations is studied. ► Boron doped and pristine Zinc oxide thin films have showed ≥95% transmittance. ► Increased carrier concentration of 9.21 × 10 21 cm −3 revealed from Hall measurement. -- Abstract: Sprayed polycrystalline ZnO and boron-doped ZnO thin films composed of spherical grains of 25–32 nm in diameters are used in roughness measurement and further correlated with the transparency and the conductivity characteristics. The surface roughness is increased up to Zn 0.98 B 0.02 O and then declined at higher boron concentrations. The sprayed ZnO films revealed ≥95% transmittance in the visible wavelength range, 1.956 × 10 −4 Ω cm electrical resistivity, 46 cm 2 /V s Hall mobility and 9.21 × 10 21 cm −3 charge carrier concentration. The X-ray photoelectron spectroscopy study has confirmed 0.15 eV binding energy change for Zn 2p 3/2 when 2 at% boron content is mixed without altering electro-optical properties substantially. Finally, using soft modeling importance of these textured ZnO over non-textured films for enhancing the solar cells performance is explored.

Exciton luminescence characteristic of ZnO. Ga scintillator for neutron detection

International Nuclear Information System (INIS)

Kinoshita, A.; Fujiwara, A.; Koyama, S.; Takei, Y.; Nanto, H.; Katagiri, Masaki

2008-01-01

ZnO family phosphors as novel phosphor materials for neutron detector have prepared using Spark Plasma Sintering method. The optical properties of ZnO phosphor prepared are investigated. The following results were obtained. Two dominant PL emission peaks at 395 nm and 495 nm were observed. The lifetime of the PL emission peak at 395 nm (UV emission band) is about 20 ns, which is suitable for neutron detection. The Ga (30 mol%)-doped ZnO phosphor exhibited an intense UV emission band without the visible emission band. The Ga-doped ZnO phosphor can be prepared at the atmospheric pressure of about 8 Pa using SPS method. It was found that the PL intensity of UV emission band is increased with improving the crystallinity of the ZnO phosphor. (author)

Structural and optical properties of Na-doped ZnO films

Science.gov (United States)

Akcan, D.; Gungor, A.; Arda, L.

2018-06-01

Zn1-xNaxO (x = 0.0-0.05) solutions have been synthesized by the sol-gel technique using Zinc acetate dihydrate and Sodium acetate which were dissolved into solvent and chelating agent. Na-doped ZnO nanoparticles were obtained from solutions to find phase and crystal structure. Na-doped ZnO films have been deposited onto glass substrate by using sol-gel dip coating system. The effects of dopant concentration on the structure, morphology, and optical properties of Na-doped ZnO thin films deposited on glass substrate are investigated. Characterization of Zn1-xNaxO nanoparticles and thin films are examined using differential thermal analysis (DTA)/thermogravimetric analysis (TGA), Scanning electron microscope (SEM) and X-Ray diffractometer (XRD). Optical properties of Zn1-xNaxO thin films were obtained by using PG Instruments UV-Vis-NIR spectrophotometer in 190-1100 nm range. The structure, morphology, and optical properties of thin films are presented.

Effect of nickel doping on the photocatalytic activity of ZnO thin films under UV and visible light

International Nuclear Information System (INIS)

Kaneva, Nina V.; Dimitrov, Dimitre T.; Dushkin, Ceco D.

2011-01-01

Nanostructured ZnO thin films with different concentrations of Ni 2+ doping (0, 1, 5, 10 and 15 wt.%) are prepared by the sol-gel method for the first time. The thin films are prepared from zinc acetate, 2-methoxyethanol and monoethanolamine on glass substrates by using dip coating method. The films comprise of ZnO nanocrystallites with hexagonal crystal structure, as revealed by X-ray diffraction. The film surface is with characteristic ganglia-like structure as observed by Scanning Electron Microscopy. Furthermore, the Ni-doped films are tested with respect to the photocatalysis in aqueous solutions of malachite green upon UV-light illumination, visible light and in darkness. The initial concentration of malachite green and the amount of catalyst are varied during the experiments. It is found that increasing of the amount of Ni 2+ ions with respect to ZnO generally lowers the photocatalytic activity in comparison with the pure ZnO films. Nevertheless, all films exhibit a substantial activity under both, UV and visible light and in darkness as well, which is promising for the development of new ZnO photocatalysts by the sol-gel method.

Giant coercivity in ferromagnetic Co doped ZnO single crystal thin film

International Nuclear Information System (INIS)

Loukya, B.; Negi, D.S.; Dileep, K.; Kumar, N.; Ghatak, Jay; Datta, R.

2013-01-01

The origin of ferromagnetism in ZnO doped with transition metal impurities has been discussed extensively and appeared to be a highly controversial and challenging topic in today's solid state physics. Magnetism observed in this system is generally weak and soft. We have grown Co:ZnO up to 30 at% Co in single crystal thin film form on c-plane sapphire. A composition dependent coercivity is observed in this system which reaches peak value at 25 at% Co, the values are 860 Oe and 1149 Oe with applied field along parallel and perpendicular to the film substrate interface respectively. This giant coercivity might pave the way to exploit this material as a magnetic semiconductor with novel logic functionalities. The findings are explained based on defect band itinerant ferromagnetism and its partial interaction with localized d electrons of Co through charge transfer. Besides large coercivity, an increase in the band gap with Co concentration has also been observed along with blue emission peak with long tail confirming the formation of extended point defect levels in the host lattice band gap. - Highlights: • Co doped ZnO ferromagnetic single crystal thin film. • Giant coercivity in Co:ZnO thin film which may help to turn this material into application. • Cathodoluminescence (CL) data showing increase in band gap with Co concentrations. • A theoretical proposal is made to explain the observed giant coercivity

Structural, electrical, and dielectric properties of Cr doped ZnO thin films: Role of Cr concentration

Energy Technology Data Exchange (ETDEWEB)

Gürbüz, Osman, E-mail: osgurbuz@yildiz.edu.tr; Okutan, Mustafa

2016-11-30

Highlights: • Magnetic material of Cr and semiconductor material of ZnO were grown by the magnetron sputtering co-sputter technique. • Perfect single crystalline structures were grown. • DC and AC conductivity with dielectric properties as a function of frequency (f = 5Hz–13 MHz) at room temperature were measured and compared. • Cr doped ZnO can be used in microwave, sensor and optoelectronic devices as the electrical conductivity increases while dielectric constant decreases with the Cr content. - Abstract: An undoped zinc oxide (ZnO) and different concentrations of chromium (Cr) doped ZnO Cr{sub x}ZnO{sub 1−x} (x = 3.74, 5.67, 8.10, 11.88, and 15.96) thin films were prepared using a magnetron sputtering technique at room temperature. These films were characterized by X-ray diffraction (XRD), High resolution scanning electron microscope (HR-SEM), and Energy dispersive X-ray spectrometry (EDS). XRD patterns of all the films showed that the films possess crystalline structure with preferred orientation along the (100) crystal plane. The average crystallite size obtained was found to be between 95 and 83 nm which was beneficial in high intensity recording peak. Both crystal quality and crystallite sizes decrease with increasing Cr concentration. The crystal and grain sizes of the all film were investigated using SEM analysis. The surface morphology that is grain size changes with increase Cr concentration and small grains coalesce together to form larger grains for the Cr{sub 11.88}ZnO and Cr{sub 15.96}ZnO samples. Impedance spectroscopy studies were carried out in the frequencies ranging from 5 Hz to 13 MHz at room temperature. The undoped ZnO film had the highest dielectric value, while dielectric values of other films decreased as doping concentrations increased. Besides, the dielectric constants decreased whereas the loss tangents increased with increasing Cr content. This was considered to be related to the reduction of grain size as Cr content in ZnO

Effect of strain on the structural and optical properties of Cu-N co-doped ZnO thin films

International Nuclear Information System (INIS)

Zhao Yue; Zhou Mintao; Li Zhao; Lv Zhiyong; Liang Xiaoyan; Min Jiahua; Wang Linjun; Shi Weimin

2011-01-01

Polycrystalline ZnO thin films co-doped with Cu and N have been obtained by chemical bath deposition. Introduction of Cu and N causes the change of strained stress in ZnO films, which subsequently affects the structural and optical properties. The dependence of structural and optical properties of the ZnO films on lattice strained stress is investigated by XRD measurement, SEM, PL spectrum, optical reflection and Raman spectrum. The result of photoluminescence of Cu-N co-doped ZnO films indicates that the UV emission peaks shift slightly towards higher energy side with decrease in tensile strain and vise versa. The blue-shift of the absorption edge and up-shift of E2 (high) mode of the films can be observed in the optical reflection and Raman spectra. - Highlights: →Cu-N co-doped ZnO is first prepared by the wet chemical method. → Stress is produced by the introduction of Cu and N atoms. → Effect of stress on the structural and optical properties of ZnO film is investigated. → Cu concentration will be used to control the structural and optical properties.

Appraisal on Textured Grain Growth and Photoconductivity of ZnO Thin Film SILAR

Directory of Open Access Journals (Sweden)

Deepu Thomas

2014-01-01

Full Text Available ZnO thin films were prepared by successive ionic layer adsorption reaction (SILAR method. The textured grain growth along c-axis in pure ZnO thin films and doped with Sn was studied. The structural analysis of the thin films was done by X-ray diffraction and surface morphology by scanning electron microscopy. Textured grain growth of the samples was measured by comparing the peak intensities. Textured grain growth and photo current in ZnO thin films were found to be enhanced by doping with Sn. ZnO thin film having good crystallinity with preferential (002 orientation is a semiconductor with photonic properties of potential benefit to biophotonics. From energy dispersive X-ray analysis, it is inferred that oxygen vacancy creation is responsible for the enhanced textured grain growth in ZnO thin films.

Morphological differences in transparent conductive indium-doped zinc oxide thin films deposited by ultrasonic spray pyrolysis

International Nuclear Information System (INIS)

Jongthammanurak, Samerkhae; Cheawkul, Tinnaphob; Witana, Maetapa

2014-01-01

In-doped ZnO thin films were deposited on glass substrates by an ultrasonic spray pyrolysis technique, using indium chloride (InCl 3 ) as a dopant and zinc acetate solution as a precursor. Increasing the [at.% In]/[at.% Zn] ratio changed the crystal orientations of thin films, from the (100) preferred orientation in the undoped, to the (101) and (001) preferred orientations in the In-doped ZnO thin films with 4 at.% and 6–8 at.%, respectively. Undoped ZnO thin film shows relatively smooth surface whereas In-doped ZnO thin films with 4 at.% and 6–8 at.% show surface features of pyramidal forms and hexagonal columns, respectively. X-ray diffraction patterns of the In-doped ZnO thin films with [at.% In]/[at.% Zn] ratios of 6–8% presented an additional peak located at 2-theta of 32.95°, which possibly suggested that a metastable Zn 7 In 2 O 10 phase was present with the ZnO phase. ZnO thin films doped with 2 at.% In resulted in a sheet resistance of ∼ 645 Ω/sq, the lowest value among thin films with [at.% In]/[at.% Zn] ratio in a range of 0–8%. The precursor molarity was changed between 0.05 M and 0.20 M at an [at.% In]/[at.% Zn] ratio of 2%. Increasing the precursor molarity in a range of 0.10 M–0.20 M resulted in In-doped ZnO thin films with the (100) preferred orientation. An In-doped ZnO thin film deposited by 0.20 M precursor showed a sheet resistance of 25 Ω/sq, and an optical transmission of 75% at 550 nm wavelength. The optical band gap estimated from the transmission result was 3.292 eV. - Highlights: • Indium-doped ZnO thin films were grown on glass using ultrasonic spray pyrolysis. • Thin films' orientations depend on In doping and Zn molarity of precursor solution. • Highly c-axis or a-axis orientations were found in the In-doped ZnO thin films. • In doping of 6–8 at.% may have resulted in ZnO and a metastable Zn 7 In 2 O 10 phases. • Increasing precursor molarity reduced sheet resistance of In-doped ZnO thin films

Effect of Sn-doped on microstructural and optical properties of ZnO thin films deposited by sol-gel method

International Nuclear Information System (INIS)

Tsay, C.-Y.; Cheng, H.-C.; Tung, Y.-T.; Tuan, W.-H.; Lin, C.-K.

2008-01-01

In this study, transparent thin films of Sn-doped ZnO (ZnO:Sn) were deposited onto alkali-free glass substrates by a sol-gel method; the effect of Sn doping on crystallinity, microstructural and optical properties was investigated. The atomic percentages of dopant in ZnO-based sols were Sn/Zn = 0, 1, 2, 3, and 5 at.%. The as-deposited films were pre-heated at 300 deg. C for 10 min and then annealed in air at 500 deg. C for 1 h. The results show that Sn-doped ZnO thin films demonstrate obviously improved surface roughness, enhanced transmittance in the 400-600 nm wavelength range and reduced average crystallite size. Among all of the annealed ZnO-based films in this study, films doped with 2 at.% Sn concentration exhibited the best properties, namely an average transmittance of 90%, an RMS roughness value of 1.92 nm and a resistivity of 9.3 x 10 2 Ω-cm

Efficient acetone sensor based on Ni-doped ZnO nanostructures prepared by spray pyrolysis technique

Science.gov (United States)

Darunkar, Swapnil S.; Acharya, Smita A.

2018-05-01

Ni-doped ZnO thin film was prepared by home-built spray pyrolysis unit for the detection of acetone at 300°C. Scanning electron microscopic (SEM) images of as-developed thin film of undoped ZnO exhibits large quantity of spherical, non-agglomerated particles with uniform size while in Ni-doped ZnO, particles are quite non-uniform in nature. The particle size estimated by using image J are obtained to be around 20-200 nm. Ni-doping effect on band gaps are determined by UV-vis optical spectroscopy and band gap of Ni-doped ZnO is found to be 3.046 eV. Nickel doping exceptionally enhances the sensing response of ZnO as compared to undoped ZnO system. The major role of the Ni-doping is to create more active sites for chemisorbed oxygen on the surface of sensor and correspondingly, to improve the sensing response. The 6 at.% of Ni-doped ZnO exhibits the highest response (92%) for 100 ppm acetone at 300 °C.

Physical properties and heterojunction device demonstration of aluminum-doped ZnO thin films synthesized at room ambient via sol-gel method

Energy Technology Data Exchange (ETDEWEB)

Karaagac, Hakan, E-mail: hkaraagac@ucdavis.edu [Department of Electrical and Computer Engineering, University of California at Davis, Davis, CA 95616 (United States); Yengel, Emre; Saif Islam, M. [Department of Electrical and Computer Engineering, University of California at Davis, Davis, CA 95616 (United States)

2012-04-25

Highlights: Black-Right-Pointing-Pointer Undoped and Al doped ZnO (AZO) thin films were successfully prepared using sol-gel technique. Black-Right-Pointing-Pointer Structural analysis has revealed that Al doping has a significant influence on preferential orientation. Black-Right-Pointing-Pointer It has been observed that wrinkles forms on the surface of films when annealed with a fast heat ramp up rate. Black-Right-Pointing-Pointer Optical analysis has revealed that that the band gap energy of ZnO thin film increases with increasing Al doping concentration. Black-Right-Pointing-Pointer The lowest resistivity is observed for 1% Al ZnO thin film, which is 2.2 Multiplication-Sign 10{sup -2} ({Omega} cm). - Abstract: ZnO and some of its ternary wide-bandgap alloys offer interesting opportunities for designing materials with tunable band gaps, strong piezoresistivity and controlled electrical conductance with high optical transparency. Synthesizing these materials on arbitrary substrates using low-cost and unconventional techniques can help in integrating semiconductors with different physical, electrical, and optical characteristics on a single substrate for heterogeneous integration of multifunctional devices. Here we report the successful synthesis of aluminum (Al) doped ZnO (AZO) thin films on soda-lime glass, silicon and fluorine doped tin oxide (FTO) pre-coated glass substrates by using sol-gel deposition method at ambient condition. X-ray diffraction (XRD) analysis revealed that varying degree of Al doping significantly impacts the crystal orientation, semiconductor bandgap and optical transparency of the film. Crystal structure of the film is also found to be strongly correlated to the characteristics of the substrate material. The impact of heating rate during post annealing process is studied and optimized in order to improve the surface morphology of the deposited films. Optical characterizations have revealed that bandgap energy of AZO films can be tuned

ZnO and Al doped ZnO thin films deposited by Spray Plasma: Effect of the growth time and Al doping on microstructural, optical and electrical properties

International Nuclear Information System (INIS)

Baba, Kamal; Lazzaroni, Claudia; Nikravech, Mehrdad

2015-01-01

Nanostructured zinc oxide (ZnO) and Al doped ZnO (ZnO:Al) thin films are deposited on glass substrate by the Spray Plasma technique. Zinc nitrate and aluminium nitrate are used as Zn and Al precursors, respectively. The effect of the growth time on structural and optical properties of undoped films is studied by X-ray diffraction, atomic force microscopy, and UV–Vis spectroscopy. The effect of Al doping on microstructural, optical and electrical characteristics of ZnO:Al films is also investigated. The results show that the grain size and the film thickness both increase with the growth time. The band gap of the layers varies from 3.17 to 3.24 eV depending on the thickness. The increase of the Al doping results in the enlargement of the peak (002) and the shift of its position to higher 2θ values. Average optical transmittance decreases from 90 to 65% with the growth time because of the thickness increase while there is no significant influence of the aluminium doping on the transmittance which is above 80% in most of the visible and near-IR range for all ZnO:Al films. The electrical properties characterized by Hall measurements show that all the deposited films exhibit high resistivity, between 4 and 10 4 Ω cm. The carrier concentration decreases from 2.10 19 to 2.10 13 cm −3 when the concentration of Al increases from 1.5 to 5 atm%. - Highlights: • The original Spray Plasma technique is used for ZnO and ZnO:Al thin film deposition. • Investigation of the effect of growth time and Al doping on the structural and optical properties • Increase of grain size and film thickness with the growth time • Optical transmittance decreases from 90 to 65% with the growth time and is above 80% for ZnO:Al films in UV–Vis-NIR range. • The peak position of the (002) plane is shifted to high 2θ values with Al doping.

Al and Fe co-doped transparent conducting ZnO thin film for mediator-less biosensing application

Directory of Open Access Journals (Sweden)

Shibu Saha

2011-12-01

Full Text Available Highly c-axis oriented Al and Fe co-doped ZnO (ZAF thin film is prepared by pulsed laser deposition. Fe introduces redox centre along with shallow donor level while Al doping enhances conductivity of ZnO, thus removing the requirement of both mediator and bottom conducting layer in bioelectrode. Model enzyme (glucose oxidase, was immobilized on surface of ZAF matrix. Cyclic voltammetry and photometric assay show that prepared bio-electrode is sensitive to glucose concentration with enhanced response of 0.18 μAmM-1cm-2 and low Km ∼ 2.01 mM. The results illustrate that ZAF is an attractive matrix for realization of miniaturized mediator-less solid state biosensor.

Identifying the influence of the intrinsic defects in Gd-doped ZnO thin-films

KAUST Repository

Flemban, Tahani H.; Sequeira, M. C.; Zhang, Z.; Venkatesh, S.; Alves, E.; Lorenz, K.; Roqan, Iman S.

2016-01-01

Gd-doped ZnO thin films were prepared using pulsed laser deposition at different oxygen pressures and varied Gd concentrations. The effects of oxygen deficiency-related defects on the Gd incorporation, optical and structural properties, were explored by studying the impact of oxygen pressure during deposition and post-growth thermal annealing in vacuum. Rutherford Backscattering Spectrometry revealed that the Gd concentration increases with increasing oxygen pressure for samples grown with the same Gd-doped ZnO target. Unexpectedly, the c-lattice parameter of the samples tends to decrease with increasing Gd concentration, suggesting that Gd-defect complexes play an important role in the structural properties. Using low-temperature photoluminescence(PL), Raman measurements and density functional theory calculations, we identified oxygen vacancies as the dominant intrinsic point defects. PL spectra show a defect band related to oxygen vacancies for samples grown at oxygen deficiency.

Identifying the influence of the intrinsic defects in Gd-doped ZnO thin-films

KAUST Repository

Flemban, Tahani H.

2016-02-08

Gd-doped ZnO thin films were prepared using pulsed laser deposition at different oxygen pressures and varied Gd concentrations. The effects of oxygen deficiency-related defects on the Gd incorporation, optical and structural properties, were explored by studying the impact of oxygen pressure during deposition and post-growth thermal annealing in vacuum. Rutherford Backscattering Spectrometry revealed that the Gd concentration increases with increasing oxygen pressure for samples grown with the same Gd-doped ZnO target. Unexpectedly, the c-lattice parameter of the samples tends to decrease with increasing Gd concentration, suggesting that Gd-defect complexes play an important role in the structural properties. Using low-temperature photoluminescence(PL), Raman measurements and density functional theory calculations, we identified oxygen vacancies as the dominant intrinsic point defects. PL spectra show a defect band related to oxygen vacancies for samples grown at oxygen deficiency.

Effect of Mg doping in the gas-sensing performance of RF-sputtered ZnO thin films

Science.gov (United States)

Vinoth, E.; Gowrishankar, S.; Gopalakrishnan, N.

2018-06-01

Thin films of Mg-free and Mg-doped (3, 10 and 20 mol%) ZnO thin films have been deposited on Si (100) substrates by RF magnetron sputtering for gas-sensing application. Preferential orientation along (002) plane with hexagonal wurtzite structure has been observed in X-ray diffraction analysis. The conductivity, resistivity, and mobility of the deposited films have been measured by Hall effect measurement. The bandgap of the films has been calculated from the UV-Vis-NIR spectroscopy. It has been found that the bandgap was increased from 3.35 to 3.91 eV with Mg content in ZnO due to the radiative recombination of excitons. The change in morphology of the grown films has been investigated by scanning electron microscope. Gas-sensing measurements have been conducted for fabricated films. The sensor response, selectivity, and stability measurement were done for the fabricated films. Though better response was found towards ethanol, methanol, and ammonia for MZ2 (Mg at 10 mol%) film and maximum gas response was observed towards ammonia. The selectivity measurement reveals maximum sensitivity about 42% for ammonia. The low response time of 123 s and recovery time of 152 s towards ammonia were observed for MZ2 (Mg at 10 mol%). Stability of the Mg-doped ZnO thin film confirmed by the continuous sensing measurements for 4 months.

Cu-Doped ZnO Thin Films Deposited by a Sol-Gel Process Using Two Copper Precursors: Gas-Sensing Performance in a Propane Atmosphere

Directory of Open Access Journals (Sweden)

Heberto Gómez-Pozos

2016-01-01

Full Text Available A study on the propane gas-sensing properties of Cu-doped ZnO thin films is presented in this work. The films were deposited on glass substrates by sol-gel and dip coating methods, using zinc acetate as a zinc precursor, copper acetate and copper chloride as precursors for doping. For higher sensitivity values, two film thickness values are controlled by the six and eight dippings, whereas for doping, three dippings were used, irrespective of the Cu precursor. The film structure was analyzed by X-ray diffractometry, and the analysis of the surface morphology and film composition was made through scanning electron microscopy (SEM and secondary ion mass spectroscopy (SIMS, respectively. The sensing properties of Cu-doped ZnO thin films were then characterized in a propane atmosphere, C3H8, at different concentration levels and different operation temperatures of 100, 200 and 300 °C. Cu-doped ZnO films doped with copper chloride presented the highest sensitivity of approximately 6 × 104, confirming a strong dependence on the dopant precursor type. The results obtained in this work show that the use of Cu as a dopant in ZnO films processed by sol-gel produces excellent catalysts for sensing C3H8 gas.

Defect characterization and magnetic properties in un-doped ZnO thin film annealed in a strong magnetic field

Science.gov (United States)

Ning, Shuai; Zhan, Peng; Wang, Wei-Peng; Li, Zheng-Cao; Zhang, Zheng-Jun

2014-12-01

Highly c-axis oriented un-doped zinc oxide (ZnO) thin films, each with a thickness of ~ 100 nm, are deposited on Si (001) substrates by pulsed electron beam deposition at a temperature of ~ 320 °C, followed by annealing at 650 °C in argon in a strong magnetic field. X-ray photoelectron spectroscopy (XPS), positron annihilation analysis (PAS), and electron paramagnetic resonance (EPR) characterizations suggest that the major defects generated in these ZnO films are oxygen vacancies. Photoluminescence (PL) and magnetic property measurements indicate that the room-temperature ferromagnetism in the un-doped ZnO film originates from the singly ionized oxygen vacancies whose number depends on the strength of the magnetic field applied in the thermal annealing process. The effects of the magnetic field on the defect generation in the ZnO films are also discussed.

Post-annealing effect on the room-temperature ferromagnetism in Cu-doped ZnO thin films

International Nuclear Information System (INIS)

Hu, Yu-Min; Kuang, Chein-Hsiun; Han, Tai-Chun; Yu, Chin-Chung; Li, Sih-Sian

2015-01-01

In this work, we investigated the structural and magnetic properties of both as-deposited and post-annealed Cu-doped ZnO thin films for better understanding the possible mechanisms of room-temperature ferromagnetism (RT-FM) in ZnO-based diluted magnetic oxides. All of the films have a c-axis-oriented wurtzite structure and display RT-FM. X-ray photoelectron spectroscopy results showed that the incorporated Cu ions in as-deposited films are in 1+ valence state merely, while an additional 2+ valence state occurs in post-annealed films. The presence of Cu 2+ state in post-annealed film accompanies a higher magnetization value than that of as-deposited film and, in particular, the magnetization curves at 10 K and 300 K of the post-annealed film separate distinctly. Since Cu 1+ ion has a filled 3d band, the RT-FM in as-deposited Cu-doped ZnO thin films may stem solely from intrinsic defects, while that in post-annealed films is enhanced due to the presence of CuO crystallites

Epitaxial growth of Sb-doped nonpolar a-plane ZnO thin films on r-plane sapphire substrates by RF magnetron sputtering

Energy Technology Data Exchange (ETDEWEB)

Chen, Hou-Guang, E-mail: houguang@isu.edu.tw [Department of Materials Science and Engineering, I-Shou University, Kaohsiung 840, Taiwan (China); Hung, Sung-Po [Department of Materials Science and Engineering, I-Shou University, Kaohsiung 840, Taiwan (China)

2014-02-15

Highlights: ► Sb-doped nonpolar a-plane ZnO layers were epitaxially grown on sapphire substrates. ► Crystallinity and electrical properties were studied upon growth condition and doping concentration. ► The out-of-plane lattice spacing of ZnO films reduces monotonically with increasing Sb doping level. ► The p-type conductivity of ZnO:Sb film is closely correlated with annealing condition and Sb doping level. -- Abstract: In this study, the epitaxial growth of Sb-doped nonpolar a-plane (112{sup ¯}0) ZnO thin films on r-plane (11{sup ¯}02) sapphire substrates was performed by radio-frequency magnetron sputtering. The influence of the sputter deposition conditions and Sb doping concentration on the microstructural and electrical properties of Sb-doped ZnO epitaxial films was investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and the Hall-effect measurement. The measurement of the XRD phi-scan indicated that the epitaxial relationship between the ZnO:Sb layer and sapphire substrate was (112{sup ¯}0){sub ZnO}//(11{sup ¯}02){sub Al{sub 2O{sub 3}}} and [11{sup ¯}00]{sub ZnO}//[112{sup ¯}0]{sub Al{sub 2O{sub 3}}}. The out-of-plane a-axis lattice parameter of ZnO films was reduced monotonically with the increasing Sb doping level. The cross-sectional transmission electron microscopy (XTEM) observation confirmed the absence of any significant antimony oxide phase segregation across the thickness of the Sb-doped ZnO epitaxial film. However, the epitaxial quality of the films deteriorated as the level of Sb dopant increased. The electrical properties of ZnO:Sb film are closely correlated with post-annealing conditions and Sb doping concentrations.

Investigation on the effect of Zr doping in ZnO thin films by spray pyrolysis

International Nuclear Information System (INIS)

Gokulakrishnan, V.; Parthiban, S.; Jeganathan, K.; Ramamurthi, K.

2011-01-01

Zirconium doped zinc oxide thin films with enhanced optical transparency were prepared on Corning 1737 glass substrates at the substrate temperature of 400 o C by spray pyrolysis method for various doping concentrations of zirconium (IV) chloride in the spray solution. The X-ray diffraction studies reveal that the films exhibit hexagonal crystal structure with polycrystalline grains oriented along (0 0 2) direction. The crystalline quality of the films is found to be deteriorating with the increase of doping concentration and acquires amorphous state for higher concentration of 8 at.% in precursor solution. The average transmittance for 5 at.% (solution) zirconium doped ZnO film is significantly increased to ∼92% in the visible region of 500-800 nm. The room temperature photoluminescence (PL) spectra of films show a band edge between 3.41 and 3.2 eV and strong blue emission at 2.8 eV irrespective of doping concentration and however intensity increases consistently with doping levels. The vacuum annealing at 400 o C reduced the resistivity of the films significantly due to the coalescence of grains and the lowest resistivity of 2 x 10 -3 Ω cm is observed for 3 at.% (solution) Zr doped ZnO films which envisages that it is a good candidate for stable TCO material.

Characterization of a new transparent-conducting material of ZnO doped ITO thin films

Science.gov (United States)

Ali, H. M.

2005-11-01

Thin films of indium tin oxide (ITO) doped with zinc oxide have the remarkable properties of being conductive yet still highly transparent in the visible and near-IR spectral ranges. The Electron beam deposi- tion technique is one of the simplest and least expensive ways of preparing. High-quality ITO thin films have been deposited on glass substrates by Electron beam evaporation technique. The effect of doping and substrate deposition temperature was found to have a significant effect on the structure, electrical and optical properties of ZnO doped ITO films. The average optical transmittance has been increased with in- creasing the substrate temperature. The maximum value of transmittance is greater than 84% in the visible region and 85% in the NIR region obtained for film with Zn/ITO = 0.13 at substrate temperature 200 °C. The dielectric constant, average excitation energy for electronic transitions (E o), the dispersion energy (E d), the long wavelength refractive index (n ), average oscillator wave length ( o) and oscillator strength S o for the thin films were determined and presented in this work.

The effects of ZnO buffer layers on the properties of phosphorus doped ZnO thin films grown on sapphire by pulsed laser deposition

International Nuclear Information System (INIS)

Kim, K-W; Lugo, F J; Lee, J H; Norton, D P

2012-01-01

The properties of phosphorus doped ZnO thin films grown on sapphire by pulsed laser deposition were examined, specifically focusing on the effects of undoped ZnO buffer layers. In particular, buffer layers were grown under different conditions; the transport properties of as-deposited and rapid thermal annealed ZnO:P films were then examined. As-deposited films showed n-type conductivity. After rapid thermal annealing, the film on buffer layer grown at a low temperature showed the conversion of carrier type to p-type for specific growth conditions while the films deposited on buffer layer grown at a high temperature remained n-type regardless of growth condition. The films deposited on buffer layer grown at a low temperature showed higher resistivity and more significant change of the transport properties upon rapid thermal annealing. These results suggest that more dopants are incorporated in films with higher defect density. This is consistent with high resolution x-ray diffraction results for phosphorus doped ZnO films on different buffer layers. In addition, the microstructure of phosphorus doped ZnO films is substantially affected by the buffer layer.

Stabilization and enhanced energy gap by Mg doping in ɛ-phase Ga2O3 thin films

Science.gov (United States)

Bi, Xiaoyu; Wu, Zhenping; Huang, Yuanqi; Tang, Weihua

2018-02-01

Mg-doped Ga2O3 thin films with different doping concentrations were deposited on sapphire substrates using laser molecular beam epitaxy (L-MBE) technique. X-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS) and ultraviolet-visible (UV-vis) absorption spectrum were used to characterize the crystal structure and optical properties of the as-grown films. Compared to pure Ga2O3 thin film, the Mg-doped thin films have transformed from the most stable β-phase into ɛ-phase. The absorption edge shifted to about 205 nm and the optical bandgap increased to ˜ 6 eV. These properties reveal that Mg-doped Ga2O3 films may have potential applications in the field of deep ultraviolet optoelectronic devices, such as deep ultraviolet photodetectors, short wavelength light emitting devices and so on.

Thermal Quenching of Photoluminescence from Er-Doped GaN Thin Films

National Research Council Canada - National Science Library

Seo, J. T; Hoemmerich, U; Lee, D. C; Heikenfeld, J; Steckl, A. J; Zavada, J. M

2002-01-01

The green (537 and 558 nm) and near infrared (1.54 micrometers) photoluminescence (PL) spectra of Er-doped GaN thin films have been investigated as a function of temperature, excitation wavelength, and pump intensity...

Defect characterization and magnetic properties in un-doped ZnO thin film annealed in a strong magnetic field

International Nuclear Information System (INIS)

Ning Shuai; Zhan Peng; Wang Wei-Peng; Li Zheng-Cao; Zhang Zheng-Jun

2014-01-01

Highly c-axis oriented un-doped zinc oxide (ZnO) thin films, each with a thickness of ∼ 100 nm, are deposited on Si (001) substrates by pulsed electron beam deposition at a temperature of ∼ 320 °C, followed by annealing at 650 °C in argon in a strong magnetic field. X-ray photoelectron spectroscopy (XPS), positron annihilation analysis (PAS), and electron paramagnetic resonance (EPR) characterizations suggest that the major defects generated in these ZnO films are oxygen vacancies. Photoluminescence (PL) and magnetic property measurements indicate that the room-temperature ferromagnetism in the un-doped ZnO film originates from the singly ionized oxygen vacancies whose number depends on the strength of the magnetic field applied in the thermal annealing process. The effects of the magnetic field on the defect generation in the ZnO films are also discussed. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

A Rapid Method for Deposition of Sn-Doped GaN Thin Films on Glass and Polyethylene Terephthalate Substrates

Science.gov (United States)

Pat, Suat; Özen, Soner; Korkmaz, Şadan

2018-01-01

We report the influence of Sn doping on microstructure, surface, and optical properties of GaN thin films deposited on glass and polyethylene terephthalate (PET) substrate. Sn-doped GaN thin films have been deposited by thermionic vacuum arc (TVA) at low temperature. TVA is a rapid deposition technology for thin film growth. Surface and optical properties of the thin films were presented. Grain size, height distribution, roughness values were determined. Grain sizes were calculated as 20 nm and 13 nm for glass and PET substrates, respectively. Nano crystalline forms were shown by field emission scanning electron microscopy. Optical band gap values were determined by optical methods and photoluminescence measurement. The optical band gap values of Sn doped GaN on glass and PET were determined to be approximately ˜3.40 eV and ˜3.47 eV, respectively. As a result, TVA is a rapid and low temperature deposition technology for the Sn doped GaN deposited on glass and PET substrate.

The Influence of Spark Plasma Sintering Temperature on the Microstructure and Thermoelectric Properties of Al,Ga Dual-Doped ZnO

DEFF Research Database (Denmark)

Han, Li; Le, Thanh Hung; Van Nong, Ngo

2013-01-01

ZnO dual-doped with Al and Ga was prepared by spark plasma sintering using different sintering temperatures. The microstructural evolution and thermoelectric properties of the samples were investigated in detail. The samples obtained with sintering temperature above 1223 K had higher relative...... of ZnO particles and microstructure evolution at different sintering temperatures were investigated by simulation of the self-Joule-heating effect of the individual particles....

Transparent conductive Ga-doped ZnO films fabricated by MOCVD

Energy Technology Data Exchange (ETDEWEB)

Behrends, Arne; Wagner, Alexander; Al-Suleiman, Mohamed Aid Mansur; Waag, Andreas; Bakin, Andrey [Institute of Semiconductor Technology, University of Technology Braunschweig, Hans-Sommer-Str. 66, 38106 Braunschweig (Germany); Lugauer, Hans-Juergen; Strassburg, Martin; Walter, Robert; Weimar, Andreas [OSRAM Opto Semiconductors GmbH, Leibnizstr. 4, 93055 Regensburg (Germany)

2012-04-15

Transparent conductive oxides (TCOs) are used for a variety of different applications, e.g., in solar cells and light emitting diodes (LEDs). Mostly, sputtering is used, which often results in a degradation of the underlying semiconductor material. In this work we report on a ''soft'' method for the fabrication of ZnO films as TCO layers by using metal organic chemical vapor deposition (MOCVD) at particularly low temperatures. The MOCVD approach has been studied focusing on the TCO key issues: fabrication temperature, morphology, optical, and electrical properties. Very smooth ZnO films with rms values down to 0.8 nm were fabricated at a substrate temperature of only 300 C. Ga-doping is well controllable even for high carrier concentrations up to 2 x 10{sup 20} cm{sup -3}, which is above the Mott-density leading to metallic-like behavior of the films. Furthermore all films show excellent optical transparency in the visible spectral range. As a consequence, our MOCVD approach is well suited for the soft fabrication of ZnO-based TCO layers. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

On the role of diluted magnetic cobalt-doped ZnO electrodes in efficiency improvement of InGaN light emitters

Energy Technology Data Exchange (ETDEWEB)

Liu, Hong-Ru; Wang, Shih-Yin [Department of Materials Science and Engineering, National Chung Hsing University, Taichung 40227, Taiwan (China); Ou, Sin-Liang [Department of Materials Science and Engineering, Da-Yeh University, Changhua 51591, Taiwan (China); Wuu, Dong-Sing, E-mail: dsw@dragon.nchu.edu.tw [Department of Materials Science and Engineering, National Chung Hsing University, Taichung 40227, Taiwan (China); Department of Materials Science and Engineering, Da-Yeh University, Changhua 51591, Taiwan (China); Advanced Optoelectronic Technology Center, National Cheng Kung University, Tainan 70101, Taiwan (China)

2016-07-11

The 120-nm-thick cobalt-doped ZnO (Co-doped ZnO, CZO) dilute magnetic films deposited by pulsed laser deposition were employed as the n-electrodes for both lateral-type blue (450 nm) and green (520 nm) InGaN light emitters. In comparison to the conventional blue and green emitters, there were 15.9% and 17.7% enhancements in the output power (@350 mA) after fabricating the CZO n-electrode on the n-GaN layer. Observations on the role of CZO n-electrodes in efficiency improvement of InGaN light emitters were performed. Based on the results of Hall measurements, the carrier mobilities were 176 and 141 cm{sup 2}/V s when the electrons passed through the n-GaN and the patterned-CZO/n-GaN, respectively. By incorporating the CZO n-electrode into the InGaN light emitters, the electrons would be scattered because of the collisions between the magnetic atoms and the electrons as the device is driven, leading to the reduction of the electron mobility. Therefore, the excessively large mobility difference between electron and hole carriers occurred in the conventional InGaN light emitter can be efficiently decreased after preparing the CZO n-electrode on the n-GaN layer, resulting in the increment of carrier recombination rate and the improvement of light output power.

On the role of diluted magnetic cobalt-doped ZnO electrodes in efficiency improvement of InGaN light emitters

International Nuclear Information System (INIS)

Liu, Hong-Ru; Wang, Shih-Yin; Ou, Sin-Liang; Wuu, Dong-Sing

2016-01-01

The 120-nm-thick cobalt-doped ZnO (Co-doped ZnO, CZO) dilute magnetic films deposited by pulsed laser deposition were employed as the n-electrodes for both lateral-type blue (450 nm) and green (520 nm) InGaN light emitters. In comparison to the conventional blue and green emitters, there were 15.9% and 17.7% enhancements in the output power (@350 mA) after fabricating the CZO n-electrode on the n-GaN layer. Observations on the role of CZO n-electrodes in efficiency improvement of InGaN light emitters were performed. Based on the results of Hall measurements, the carrier mobilities were 176 and 141 cm"2/V s when the electrons passed through the n-GaN and the patterned-CZO/n-GaN, respectively. By incorporating the CZO n-electrode into the InGaN light emitters, the electrons would be scattered because of the collisions between the magnetic atoms and the electrons as the device is driven, leading to the reduction of the electron mobility. Therefore, the excessively large mobility difference between electron and hole carriers occurred in the conventional InGaN light emitter can be efficiently decreased after preparing the CZO n-electrode on the n-GaN layer, resulting in the increment of carrier recombination rate and the improvement of light output power.

Stabilization and enhanced energy gap by Mg doping in ε-phase Ga2O3 thin films

Directory of Open Access Journals (Sweden)

Xiaoyu Bi

2018-02-01

Full Text Available Mg-doped Ga2O3 thin films with different doping concentrations were deposited on sapphire substrates using laser molecular beam epitaxy (L-MBE technique. X-ray diffraction (XRD, x-ray photoelectron spectroscopy (XPS and ultraviolet-visible (UV-vis absorption spectrum were used to characterize the crystal structure and optical properties of the as-grown films. Compared to pure Ga2O3 thin film, the Mg-doped thin films have transformed from the most stable β-phase into ε-phase. The absorption edge shifted to about 205 nm and the optical bandgap increased to ∼ 6 eV. These properties reveal that Mg-doped Ga2O3 films may have potential applications in the field of deep ultraviolet optoelectronic devices, such as deep ultraviolet photodetectors, short wavelength light emitting devices and so on.

Annealing effects on electrical and optical properties of ZnO thin-film samples deposited by radio frequency-magnetron sputtering on GaAs (001) substrates

International Nuclear Information System (INIS)

Liu, H. F.; Chua, S. J.; Hu, G. X.; Gong, H.; Xiang, N.

2007-01-01

The effects of thermal annealing on Hall-effect measurement and photoluminescence (PL) from undoped n-type ZnO/GaAs thin-film samples have been studied. The evolutions of carrier concentration, electrical resistivity, and PL spectrum at various annealing conditions reveal that the dominant mechanism that affects the electrical and PL properties is dependent on the amount of thermal energy and the ambient pressure applied during the annealing process. At low annealing temperatures, annihilation of native defects is dominant in reducing the carrier concentration and weakening the low-energy tail of the main PL peak, while the GaAs substrate plays only a minor role in carrier compensations. For the higher temperatures, diffusion of Ga atoms from the GaAs substrate into ZnO film leads to a more n-type conduction of the sample. As a result, the PL exhibits a high-energy tail due to the high-level doping

Structural, optical, and LED characteristics of ZnO and Al doped ZnO thin films

Science.gov (United States)

Sandeep, K. M.; Bhat, Shreesha; Dharmaprakash, S. M.

2017-05-01

ZnO (pristine) and Al doped ZnO (AZO) films were prepared using sol-gel spin coating method. The XRD analysis showed the enhanced compressive stress in AZO film. The presence of extended states below the conduction band edge in AZO accounts for the redshift in optical bandgap. The PL spectra of AZO showed significant blue emission due to the carrier recombination from defect states. The TRPL curves showed the dominant DAP recombination in ZnO film, whereas defect related recombination in Al doped ZnO film. Color parameters viz: the dominant wavelength, color coordinates (x,y), color purity, luminous efficiency and correlated color temperature (CCT) of ZnO and AZO films are calculated using 1931 (CIE) diagram. Further, a strong blue emission with color purity more than 96% is observed in both the films. The enhanced blue emission in AZO significantly increased the luminous efficiency (22.8%) compared to ZnO film (10.8%). The prepared films may be used as blue phosphors in white light generation.

Diffusivity, solubility and thermodynamic modelling of diffusion growth of Ga"3"+-doped LiTaO_3 thin film for integrated optics

International Nuclear Information System (INIS)

Zhang, De-Long; Zhang, Qun; Zhang, Pei; Kang, Jian; Wong, Wing-Han; Yu, Dao-Yin

2016-01-01

Graphical abstract: Diffusion growth of Ga"3"+-doped LiTaO_3(LT) thin film was studied thermodynamically. Some Ga"3"+-doped LT thin films were grown on LT surface by in-diffusion of homogeneously coated Ga_2O_3 film at the temperature range of (1273 to 1473) K. The Ga"3"+ profile in the grown thin film was analyzed by secondary ion mass spectrometry. Form the measured Ga"3"+ profiles, some thermodynamic parameters were obtained. These include diffusivity, diffusion constant, chemical activation energy, solubility, solubility constant and enthalpy of solution. These parameters are crucial to design and growth of a Ga"3"+-doped LT thin film with desired Ga"3"+ profile for integrated optics application. A thermodynamic model is suggested for the growth and verified experimentally. - Highlights: • Diffusion growth of Ga"3"+-doped LiTaO_3 thin film were studied thermodynamically. • Diffusion constant is 1.41 · 10"−"6 m"2/s and activation energy is 237.2 kJ/mol. • Solubility constant is 22.9 · 10"2"6 ions/m"3 and enthalpy of solution is 28.9 kJ/mol. • Ga"3"+ dopant has small effect on LiTaO_3 refractive index. • Ga"3"+ growth can be described by a Fick-type equation with a constant diffusivity. - Abstract: A thermodynamic study was performed on diffusion growth of Ga"3"+-doped LiTaO_3(LT) thin film for integrated optics. Some Ga"3"+-doped LT thin films were grown on LT surface by in-diffusion of homogeneously coated Ga_2O_3 film at the temperature range of (1273 to 1473) K. After growth, the refractive indices at Ga"3"+-doped and un-doped surface parts were measured by prism coupling technique and Li composition there was evaluated from the measured refractive indices. The results show that Ga"3"+ dopant has small effect on the LT index. Li_2O out-diffusion is not measurable. The Ga"3"+ profile in the grown thin film was analysed by secondary ion mass spectrometry. It is found that the grown Ga"3"+ ions follow a complementary error function profile. A

Influence Al doped ZnO nanostructure on structural and optical properties

International Nuclear Information System (INIS)

Ramelan, Ari Handono; Wahyuningsih, Sayekti; Chasanah, Uswatul; Munawaroh, Hanik

2016-01-01

The preparation of Al-doped ZnO (AZO) thin films prepared by the spin-coating method was reported. Preparation of AZO was conducted by annealing treatment at a temperature of 700°C. While the spin-coating process of AZO thin films were done at 2000 and 3000 rpm respectively. The structural properties of ZnO were determined by X- ray diffraction (XRD) analysis. ZnOnanostructure was formed after annealed at atemperature of 400°C.The morphology of ZnO was determined by Scanning Electron Microscopy (SEM) showed the irregular morphology about 30-50µm in size. Al doped on ZnO influenced the optical properties of those material. Increasing Al contain on ZnO cause of shifting to the lower wavelength. The optical properties of the ZnO as well as AZO films showed that higher reflectance on the ultraviolet region so those materials were used as anti-reflecting agent.Al addition significantly enhance the optical transparency and induce the blue-shift in optical bandgap of ZnO films.

ZnO quantum dot-doped graphene/h-BN/GaN-heterostructure ultraviolet photodetector with extremely high responsivity

Science.gov (United States)

Lu, Yanghua; Wu, Zhiqian; Xu, Wenli; Lin, Shisheng

2016-12-01

A ZnO quantum dot photo-doped graphene/h-BN/GaN-heterostructure ultraviolet photodetector with extremely high responsivity of more than 1915 A W-1 and detectivity of more than 1.02 × 1013 Jones (Jones = cm Hz1/2 W-1) has been demonstrated. The interfaced h-BN layer increases the barrier height at the graphene/GaN heterojunction, which decreases the dark current and improves the on/off current ratio of the device. The photo-doping effect increases the barrier height and carrier concentration at the graphene/h-BN/GaN heterojunction, thus the responsivity is improved from 1473 A W-1 to 1915 A W-1 and the detectivity is improved from 5.8 × 1012 to 1.0 × 1013 Jones. Moreover, all of the responsivity and detectivity values are the highest values among all the graphene-based ultraviolet photodetectors.

Effects of thin heavily Mg-doped GaN capping layer on ohmic contact formation of p-type GaN

International Nuclear Information System (INIS)

Wu, L L; Zhao, D G; Jiang, D S; Chen, P; Le, L C; Li, L; Liu, Z S; Zhang, S M; Zhu, J J; Wang, H; Zhang, B S; Yang, H

2013-01-01

The growth condition of thin heavily Mg-doped GaN capping layer and its effect on ohmic contact formation of p-type GaN were investigated. It is confirmed that the excessive Mg doping can effectively enhance the Ni/Au contact to p-GaN after annealing at 550 °C. When the flow rate ratio between Mg and Ga gas sources is 6.4% and the layer width is 25 nm, the capping layer grown at 850 °C exhibits the best ohmic contact properties with respect to the specific contact resistivity (ρ c ). This temperature is much lower than the conventional growth temperature of Mg-doped GaN, suggesting that the deep-level-defect induced band may play an important role in the conduction of capping layer. (paper)

Crystallinity Improvement of ZnO Thin Film on Different Buffer Layers Grown by MBE

Directory of Open Access Journals (Sweden)

Shao-Ying Ting

2012-01-01

Full Text Available The material and optical properties of ZnO thin film samples grown on different buffer layers on sapphire substrates through a two-step temperature variation growth by molecular beam epitaxy were investigated. The thin buffer layer between the ZnO layer and the sapphire substrate decreased the lattice mismatch to achieve higher quality ZnO thin film growth. A GaN buffer layer slightly increased the quality of the ZnO thin film, but the threading dislocations still stretched along the c-axis of the GaN layer. The use of MgO as the buffer layer decreased the surface roughness of the ZnO thin film by 58.8% due to the suppression of surface cracks through strain transfer of the sample. From deep level emission and rocking curve measurements it was found that the threading dislocations play a more important role than oxygen vacancies for high-quality ZnO thin film growth.

Atomic layer epitaxy of ZnO for applications in molecular beam epitaxy growth of GaN and InGaN

International Nuclear Information System (INIS)

Godlewski, M.; Szczerbakow, A.; Ivanov, V. Yu.; Barski, A.; Goldys, E.M.

2000-01-01

We report the successful atomic layer epitaxy growth of thin ZnO films and their use for GaN and InGaN epitaxy. The properties of ZnO epilayers, obtained by four different procedures, are analysed, as well as of GaN and InGaN films grown on ZnO-coated Si and GaAs by MBE. (author)

The Influence of Spark Plasma Sintering Temperature on the Microstructure and the Thermoelectric Properties of Al, Ga dually-doped ZnO

DEFF Research Database (Denmark)

Han, Li; Le, Thanh Hung; Van Nong, Ngo

2012-01-01

Al, Ga dually-doped ZnO was prepared by spark plasma sintering with different sintering temperatures. The microstructural evolution and thermoelectric properties of the samples were investigated in detail. The samples with a sintering temperature above 1223K obtained higher relative densities...

Electronic structure of Al- and Ga-doped ZnO films studied by hard X-ray photoelectron spectroscopy

Directory of Open Access Journals (Sweden)

M. Gabás

2014-01-01

Full Text Available Al- and Ga-doped sputtered ZnO films (AZO, GZO are semiconducting and metallic, respectively, despite the same electronic valence structure of the dopants. Using hard X-ray photoelectron spectroscopy we observe that both dopants induce a band in the electronic structure near the Fermi level, accompanied by a narrowing of the Zn 3d/O 2p gap in the valence band and, in the case of GZO, a substantial shift in the Zn 3d. Ga occupies substitutional sites, whereas Al dopants are in both substitutional and interstitial sites. The latter could induce O and Zn defects, which act as acceptors explaining the semiconducting character of AZO and the lack of variation in the optical gap. By contrast, mainly substitutional doping is consistent with the metallic-like behavior of GZO.

X-ray photoelectron spectroscopy investigations of band offsets in Ga0.02Zn0.98O/ZnO heterojunction for UV photodetectors

Science.gov (United States)

Singh, Karmvir; Rawal, Ishpal; Punia, Rajesh; Dhar, Rakesh

2017-10-01

Here, we report the valence and conduction band offset measurements in pure ZnO and the Ga0.02Zn0.98O/ZnO heterojunction by X-Ray photoelectron spectroscopy studies for UV photodetector applications. For detailed investigations on the band offsets and UV photodetection behavior of Ga0.02Zn0.98O/ZnO heterostructures, thin films of pristine ZnO, Ga-doped ZnO (Ga0.02Zn0.98O), and heterostructures of Ga-doped ZnO with ZnO (Ga0.02Zn0.98O/ZnO) were deposited using a pulsed laser deposition technique. The deposited thin films were characterized by X-ray diffraction, atomic force microscopy, and UV-Vis spectroscopy. X-ray photoelectron spectroscopy studies were carried out on all the thin films for the investigation of valence and conduction band offsets. The valence band was found to be shifted by 0.28 eV, while the conduction band has a shifting of -0.272 eV in the Ga0.02Zn0.98O/ZnO heterojunction as compared to pristine ZnO thin films. All the three samples were analyzed for photoconduction behavior under UVA light of the intensity of 3.3 mW/cm2, and it was observed that the photoresponse of pristine ZnO (19.75%) was found to increase with 2 wt. % doping of Ga (22.62%) and heterostructured thin films (29.10%). The mechanism of UV photodetection in the deposited samples has been discussed in detail, and the interaction of chemisorbed oxygen on the ZnO surface with holes generated by UV light exposure has been the observed mechanism for the change in electrical conductivity responsible for UV photoresponse on the present deposited ZnO films.

Effects of oxygen gas flow rates and Ga contents on structural properties of Ga-doped ZnO films prepared by ion-plating with a DC arc discharge

International Nuclear Information System (INIS)

Terasako, Tomoaki; Nomoto, Junichi; Makino, Hisao; Yamamoto, Naoki; Shirakata, Sho; Yamamoto, Tetsuya

2015-01-01

Structural properties of highly c-axis oriented polycrystalline Ga-doped ZnO (GZO) films prepared by ion-plating with a DC arc discharge were studied in terms of the oxygen gas flow rate (F O2 ) introduced into the chamber during the deposition process and the Ga 2 O 3 content in the GZO sintered pellet. The X-ray diffraction (XRD) measurements revealed that the GZO films have the residual compressive stress along the a-axis direction (in-plane) and the tensile stress along the c-axis direction (out-of-plane). The increase in F O2 or the increase in Ga 2 O 3 content was effective for relaxing the in-plane compressive stress induced by the so-called atomic peening effect. The positive correlation between the carrier concentration (n) and the primitive cell volume (V) would be due to the incorporation of Ga atoms substituting Zn sites (Ga Zn s) together with the generation of n-type intrinsic defects or complex defects. - Highlights: • Films of Ga-doped ZnO (GZO) films were deposited by ion-plating with a DC arc discharge. • Structural properties of GZO films were examined by X-ray diffraction measurements. • GZO films had the residual compressive stress along the a-axis direction. • There was the correlation between the carrier concentration and the cell volume.

Effects of oxygen gas flow rates and Ga contents on structural properties of Ga-doped ZnO films prepared by ion-plating with a DC arc discharge

Energy Technology Data Exchange (ETDEWEB)

Terasako, Tomoaki, E-mail: terasako.tomoaki.mz@ehime-u.ac.jp [Graduate School of Science and Engineering, Ehime University, 3 Bunkyo-cho, Matsuyama-shi, Ehime 790-8577 (Japan); Nomoto, Junichi; Makino, Hisao; Yamamoto, Naoki [Research Institute, Kochi University of Technology, 185 Miyanokuchi, Tosayamada-cho, Kami-shi, Kochi 782-8502 (Japan); Shirakata, Sho [Graduate School of Science and Engineering, Ehime University, 3 Bunkyo-cho, Matsuyama-shi, Ehime 790-8577 (Japan); Yamamoto, Tetsuya [Research Institute, Kochi University of Technology, 185 Miyanokuchi, Tosayamada-cho, Kami-shi, Kochi 782-8502 (Japan)

2015-12-01

Structural properties of highly c-axis oriented polycrystalline Ga-doped ZnO (GZO) films prepared by ion-plating with a DC arc discharge were studied in terms of the oxygen gas flow rate (F{sub O2}) introduced into the chamber during the deposition process and the Ga{sub 2}O{sub 3} content in the GZO sintered pellet. The X-ray diffraction (XRD) measurements revealed that the GZO films have the residual compressive stress along the a-axis direction (in-plane) and the tensile stress along the c-axis direction (out-of-plane). The increase in F{sub O2} or the increase in Ga{sub 2}O{sub 3} content was effective for relaxing the in-plane compressive stress induced by the so-called atomic peening effect. The positive correlation between the carrier concentration (n) and the primitive cell volume (V) would be due to the incorporation of Ga atoms substituting Zn sites (Ga{sub Zn}s) together with the generation of n-type intrinsic defects or complex defects. - Highlights: • Films of Ga-doped ZnO (GZO) films were deposited by ion-plating with a DC arc discharge. • Structural properties of GZO films were examined by X-ray diffraction measurements. • GZO films had the residual compressive stress along the a-axis direction. • There was the correlation between the carrier concentration and the cell volume.

ZnO quantum dot-doped graphene/h-BN/GaN-heterostructure ultraviolet photodetector with extremely high responsivity.

Science.gov (United States)

Lu, Yanghua; Wu, Zhiqian; Xu, Wenli; Lin, Shisheng

2016-12-02

A ZnO quantum dot  photo-doped graphene/h-BN/GaN-heterostructure ultraviolet photodetector with extremely high responsivity of more than 1915 A W -1 and detectivity of more than 1.02 × 10 13 Jones (Jones = cm Hz 1/2 W -1 ) has been demonstrated. The interfaced h-BN layer increases the barrier height at the graphene/GaN heterojunction, which decreases the dark current and improves the on/off current ratio of the device. The photo-doping effect increases the barrier height and carrier concentration at the graphene/h-BN/GaN heterojunction, thus the responsivity is improved from 1473 A W -1 to 1915 A W -1 and the detectivity is improved from 5.8 × 10 12 to 1.0 × 10 13 Jones. Moreover, all of the responsivity and detectivity values are the highest values among all the graphene-based ultraviolet photodetectors.

Title: Using Alignment and 2D Network Simulations to Study Charge Transport Through Doped ZnO Nanowire Thin Film Electrodes

KAUST Repository

Phadke, Sujay; Lee, Jung-Yong; West, Jack; Peumans, Peter; Salleo, Alberto

2011-01-01

of magnitude lower than the single nanowire resistance. Simulations suggest that the conductivity of such thin film devices could be further enhanced by using longer nanowires. Solution processed Gallium doped ZnO nanowires are aligned on substrates using

Preparation of p-type GaN-doped SnO2 thin films by e-beam evaporation and their applications in p-n junction

Science.gov (United States)

Lv, Shuliang; Zhou, Yawei; Xu, Wenwu; Mao, Wenfeng; Wang, Lingtao; Liu, Yong; He, Chunqing

2018-01-01

Various transparent GaN-doped SnO2 thin films were deposited on glass substrates by e-beam evaporation using GaN:SnO2 targets of different GaN weight ratios. It is interesting to find that carrier polarity of the thin films was converted from n-type to p-type with increasing GaN ratio higher than 15 wt.%. The n-p transition in GaN-doped SnO2 thin films was explained for the formation of GaSn and NO with increasing GaN doping level in the films, which was identified by Hall measurement and XPS analysis. A transparent thin film p-n junction was successfully fabricated by depositing p-type GaN:SnO2 thin film on SnO2 thin film, and a low leakage current (6.2 × 10-5 A at -4 V) and a low turn-on voltage of 1.69 V were obtained for the p-n junction.

AlGaN/GaN high-electron-mobility transistors with transparent gates by Al-doped ZnO

International Nuclear Information System (INIS)

Wang Chong; He Yun-Long; Zheng Xue-Feng; Ma Xiao-Hua; Zhang Jin-Cheng; Hao Yue

2013-01-01

AlGaN/GaN high-electron-mobility transistors (HEMTs) with Al-doped ZnO (AZO) transparent gate electrodes are fabricated, and Ni/Au/Ni-gated HEMTs are produced in comparison. The AZO-gated HEMTs show good DC characteristics and Schottky rectifying characteristics, and the gate electrodes achieve excellent transparencies. Compared with Ni/Au/Ni-gated HEMTs, AZO-gated HEMTs show a low saturation current, high threshold voltage, high Schottky barrier height, and low gate reverse leakage current. Due to the higher gate resistivity, AZO-gated HEMTs exhibit a current—gain cutoff frequency (f T ) of 10 GHz and a power gain cutoff frequency (f max ) of 5 GHz, and lower maximum oscillation frequency than Ni/Au/Ni-gated HEMTs. Moreover, the C—V characteristics are measured and the gate interface characteristics of the AZO-gated devices are investigated by a C—V dual sweep

Hydrogen-surfactant-assisted coherent growth of GaN on ZnO substrate

Science.gov (United States)

Zhang, Jingzhao; Zhang, Yiou; Tse, Kinfai; Zhu, Junyi

2018-01-01

Heterostructures of wurtzite based devices have attracted great research interest because of the tremendous success of GaN in light emitting diodes (LED) industry. High-quality GaN thin films on inexpensive and lattice matched ZnO substrates are both commercially and technologically desirable. Intrinsic wetting conditions, however, forbid such heterostructures as the energy of ZnO polar surfaces is much lower than that of GaN polar surfaces, resulting in 3D growth mode and poor crystal quality. Based on first-principles calculations, we propose the use of surfactant hydrogen to dramatically alter the growth mode of the heterostructures. Stable H-involved surface configurations and interfaces are investigated with the help of our newly developed modelling techniques. The temperature and chemical potential dependence of our proposed strategy, which is critical in experiments, is predicted by applying the experimental Gibbs free energy of H2. Our thermodynamic wetting condition analysis is a crucial step for the growth of GaN on ZnO, and we find that introducing H will not degrade the stability of ZnO substrate. This approach will allow the growth of high-quality GaN thin films on ZnO substrates. We believe that our new strategy may reduce the manufactory cost, improve the crystal quality, and improve the efficiency of GaN-based devices.

Low-Concentration Indium Doping in Solution-Processed Zinc Oxide Films for Thin-Film Transistors

Directory of Open Access Journals (Sweden)

Xue Zhang

2017-07-01

Full Text Available We investigated the influence of low-concentration indium (In doping on the chemical and structural properties of solution-processed zinc oxide (ZnO films and the electrical characteristics of bottom-gate/top-contact In-doped ZnO thin-film transistors (TFTs. The thermogravimetry and differential scanning calorimetry analysis results showed that thermal annealing at 400 °C for 40 min produces In-doped ZnO films. As the In content of ZnO films was increased from 1% to 9%, the metal-oxygen bonding increased from 5.56% to 71.33%, while the metal-hydroxyl bonding decreased from 72.03% to 9.63%. The X-ray diffraction peaks and field-emission scanning microscope images of the ZnO films with different In concentrations revealed a better crystalline quality and reduced grain size of the solution-processed ZnO thin films. The thickness of the In-doped ZnO films also increased when the In content was increased up to 5%; however, the thickness decreased on further increasing the In content. The field-effect mobility and on/off current ratio of In-doped ZnO TFTs were notably affected by any change in the In concentration. Considering the overall TFT performance, the optimal In doping concentration in the solution-processed ZnO semiconductor was determined to be 5% in this study. These results suggest that low-concentration In incorporation is crucial for modulating the morphological characteristics of solution-processed ZnO thin films and the TFT performance.

LPCVD homoepitaxy of Si doped β-Ga2O3 thin films on (010) and (001) substrates

Science.gov (United States)

Rafique, Subrina; Karim, Md Rezaul; Johnson, Jared M.; Hwang, Jinwoo; Zhao, Hongping

2018-01-01

This paper presents the homoepitaxy of Si-doped β-Ga2O3 thin films on semi-insulating (010) and (001) Ga2O3 substrates via low pressure chemical vapor deposition with a growth rate of ≥1 μm/h. Both high resolution scanning transmission electron microscopy and X-ray diffraction measurements demonstrated high crystalline quality homoepitaxial growth of these thin films. Atomic resolution STEM images of the as-grown β-Ga2O3 thin films on (010) and (001) substrates show high quality material without extended defects or dislocations. The charge carrier transport properties of the as-grown Si-doped β-Ga2O3 thin films were characterized by the temperature dependent Hall measurement using van der Pauw patterns. The room temperature carrier concentrations achieved for the (010) and (001) homoepitaxial thin films were ˜1.2 × 1018 cm-3 and ˜9.5 × 1017 cm-3 with mobilities of ˜72 cm2/V s and ˜42 cm2/V s, respectively.

Structural and magnetic properties of Co-doped ZnO thin films grown by ultrasonic spray pyrolysis method

Science.gov (United States)

Baghdad, R.; Lemée, N.; Lamura, G.; Zeinert, A.; Hadj-Zoubir, N.; Bousmaha, M.; Bezzerrouk, M. A.; Bouyanfif, H.; Allouche, B.; Zellama, K.

2017-04-01

Cobalt-doped ZnO thin films with several different percentage of Co from 0 up to 15 at% were synthesized via a cheap, simple and versatile method i.e. ultrasonic spray pyrolysis at atmospheric pressure and a substrate temperature of 350 °C. The structure of the as-prepared samples was characterized by X-ray diffraction (XRD), Raman spectroscopy and FTIR. The Co-doping effect is revealed by the presence of three additional peaks around 235, 470 and 538 cm-1 respect to the Raman spectra of the unsubstituted film. Fourier transform infrared spectroscopy (FTIR) put in evidence the decrease of the bond force constant f with increasing Co-doping. By ultra-violet visible near infrared (UV-Vis-NIR) spectroscopy on Co-doped samples it was possible to show the presence of additional absorption bands at approximately 570, 620 and 660 nm suggesting that Co2+ ions do not change their oxidation when substituted to zinc and the ZnO lattice does not change its wurtzite structure as well. Finally, all our samples exhibit a paramagnetic behavior without any trace of intrinsic room temperature ferromagnetism.

Carbon doped ZnO: Synthesis, characterization and interpretation

International Nuclear Information System (INIS)

Mishra, D.K.; Mohapatra, J.; Sharma, M.K.; Chattarjee, R.; Singh, S.K.; Varma, Shikha; Behera, S.N.; Nayak, Sanjeev K.; Entel, P.

2013-01-01

A novel thermal plasma in-flight technique has been adopted to synthesize nanocrystalline ZnO and carbon doped nanocrystalline ZnO matrix. Transmission electron microscopy (TEM) studies on these samples show the average particle sizes to be around 32 nm for ZnO and for carbon doped ZnO. An enhancement of saturation magnetization in nanosized carbon doped ZnO matrix by a factor of 3.8 has been found in comparison to ZnO nanoparticles at room temperature. Raman measurement clearly indicates the presence of Zn–C complexes surrounded by ZnO matrix in carbon doped ZnO. This indicates that the ferromagnetic signature in carbon doped ZnO arises from the creation of defects or the development of oxy-carbon clusters, in the carbon doped ZnO system. Theoretical studies based on density functional theory also support the experimental analyses. - Highlights: ► Synthesis of nanocrystalline ZnO and carbon doped ZnO matrix by inflight thermal plasma reactor. ► Enhancement of ferromagnetism in nanosized carbon doped ZnO in comparison to ZnO nanoparticles. ► Raman measurement indicates the presence of Zn–C complexes surrounded by ZnO matrix. ► Ferromagnetic signature in carbon doped ZnO arises from the development of oxy-carbon clusters. ► DFT supports experimental evidence of ferromagnetism in C doped ZnO nanoparticles.

Low-Temperature Processed Ga-Doped ZnO Coatings from Colloidal Inks

KAUST Repository

Della Gaspera, Enrico

2013-03-06

We present a new colloidal synthesis of gallium-doped zinc oxide nanocrystals that are transparent in the visible and absorb in the near-infrared. Thermal decomposition of zinc stearate and gallium nitrate after hot injection of the precursors in a mixture of organic amines leads to nanocrystals with tunable properties according to gallium amount. Substitutional Ga3+ ions trigger a plasmonic resonance in the infrared region resulting from an increase in the free electrons concentration. These nanocrystals can be deposited by spin coating, drop casting, and spray coating resulting in homogeneous and high-quality thin films. The optical transmission of the Ga-ZnO nanoparticle assemblies in the visible is greater than 90%, and at the same time, the near-infrared absorption of the nanocrystals is maintained in the films as well. Several strategies to improve the films electrical and optical properties have been presented, such as UV treatments to remove the organic compounds responsible for the observed interparticle resistance and reducing atmosphere treatments on both colloidal solutions and thin films to increase the free carriers concentration, enhancing electrical conductivity and infrared absorption. The electrical resistance of the nanoparticle assemblies is about 30 kΩ/sq for the as-deposited, UV-exposed films, and it drops down to 300 Ω/sq after annealing in forming gas at 450 °C, comparable with state of the art tin-doped indium oxide coatings deposited from nanocrystal inks. © 2013 American Chemical Society.

Resistive switching: An investigation of the bipolar–unipolar transition in Co-doped ZnO thin films

International Nuclear Information System (INIS)

Santos, Daniel A.A.; Zeng, Hao; Macêdo, Marcelo A.

2015-01-01

Highlights: • A purely bipolar behavior on a Co-doped ZnO thin film has been demonstrated. • We have shown what can happen if a unipolar test is performed in a purely bipolar device. • An explanation for how a sample can show a purely bipolar switching behavior was suggested. • An important open issue about resistive switching effect was put in debate. - Abstract: In order to investigate the resistive switching effect we built devices in a planar structure in which two Al contacts were deposited on the top of the film and separated by a small gap using a shadow mask. Therefore, two samples of 10% Co-doped ZnO thin films were sputtered on glass substrate. High resolution X-ray diffraction (HRXRD) revealed a highly c-axis oriented crystalline structure, without secondary phase. The high resolution scanning electron microscopy (HRSEM) showed a flat surface with good coverage and thickness about 300 nm. A Keithley 2425 semiconductor characterization system was used to perform the resistive switching tests in the bipolar and unipolar modes. Considering only the effect of compliance current (CC), the devices showed a purely bipolar behavior since an increase in CC did not induce a transition to unipolar behavior

Analysis of optical band-gap shift in impurity doped ZnO thin films by using nonparabolic conduction band parameters

International Nuclear Information System (INIS)

Kim, Won Mok; Kim, Jin Soo; Jeong, Jeung-hyun; Park, Jong-Keuk; Baik, Young-Jun; Seong, Tae-Yeon

2013-01-01

Polycrystalline ZnO thin films both undoped and doped with various types of impurities, which covered the wide carrier concentration range of 10 16 –10 21 cm −3 , were prepared by magnetron sputtering, and their optical-band gaps were investigated. The experimentally measured optical band-gap shifts were analyzed by taking into account the carrier density dependent effective mass determined by the first-order nonparabolicity approximation. It was shown that the measured shifts in optical band-gaps in ZnO films doped with cationic dopants, which mainly perturb the conduction band, could be well represented by theoretical estimation in which the band-gap widening due to the band-filling effect and the band-gap renormalization due to the many-body effect derived for a weakly interacting electron-gas model were combined and the carrier density dependent effective mass was incorporated. - Highlights: ► Optical band-gaps of polycrystalline ZnO thin films were analyzed. ► Experimental carrier concentration range covered from 10 16 to 10 21 cm −3 . ► Nonparabolic conduction band parameters were used in theoretical analysis. ► The band-filling and the band-gap renormalization effects were considered. ► The measured optical band-gap shifts corresponded well with the calculated ones

Dominant intrinsic acceptors in GaN and ZnO

Energy Technology Data Exchange (ETDEWEB)

Saarinen, K; Hautakangas, S; Tuomisto, F [Laboratory of Physics, Helsinki University of Technology, PO Box 1100, FI-02015 TKK (Finland)

2006-09-01

Positron annihilation measurements reveal negatively charged Ga vacancies in n-type GaN and Zn vacancies in n-type ZnO. Positron trapping at other negative defects is not observed, indicating that cation vacancies are the dominant acceptors in these materials. The vacancy concentrations are the same as the total acceptor densities determined in Hall experiments, confirming the dominant role of the vacancy defects. The Ga vacancy in GaN is found as the main compensating centre over the range of four orders of magnitude of intentional oxygen doping.

Dominant intrinsic acceptors in GaN and ZnO

International Nuclear Information System (INIS)

Saarinen, K; Hautakangas, S; Tuomisto, F

2006-01-01

Positron annihilation measurements reveal negatively charged Ga vacancies in n-type GaN and Zn vacancies in n-type ZnO. Positron trapping at other negative defects is not observed, indicating that cation vacancies are the dominant acceptors in these materials. The vacancy concentrations are the same as the total acceptor densities determined in Hall experiments, confirming the dominant role of the vacancy defects. The Ga vacancy in GaN is found as the main compensating centre over the range of four orders of magnitude of intentional oxygen doping

Al-doped ZnO nanofilms: Synthesis and characterization

Energy Technology Data Exchange (ETDEWEB)

Huczko, A.; Dabrowska, A. [Department of Chemistry, Warsaw University, Warsaw (Poland); Madhup, D.K. [Department of Physics, Kathmandu University, Dhulikhel (Nepal); College of Biomedical Engineering and Applied Sciences, Hadigaun, Kathmandu (Nepal); Subedi, D.P.; Chimouriya, S.P. [Department of Physics, Kathmandu University, Dhulikhel (Nepal)

2010-12-15

Al-doped and un-doped ZnO nanofilms on quartz substrate were obtained by ultrasonic spray pyrolysis of salt solutions (mole concentration of Al within 0-10%). The films were characterized by Scanning electron microscopy (SEM), X-ray diffraction (XRD), Atomic force microscopy (AFM) and UV spectroscopy to study the morphology and optical properties. The optical studies showed that the increase in Al within ZnO thin layer increases its band gap energy. The obtained value of band gap energy is very close to the determined oscillation energy. However, the dispersion energy is nearly half of band gap energy value. (Copyright copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Enhancing the Performance of Quantum Dot Light-Emitting Diodes Using Room-Temperature-Processed Ga-Doped ZnO Nanoparticles as the Electron Transport Layer

KAUST Repository

Cao, Sheng; Zheng, Jinju; Zhao, Jialong; Yang, Zuobao; Li, Chengming; Guan, Xinwei; Yang, Weiyou; Shang, Minghui; Wu, Tao

2017-01-01

-temperature (RT) solution process without the use of bulky organic ligands. We found that the charge transfer at the interface between the CdSe/ZnS QDs and the doped ZnO NPs was significantly weakened because of the incorporated Ga dopants. Remarkably, the as

Implanted ZnO thin films: Microstructure, electrical and electronic properties

International Nuclear Information System (INIS)

Lee, J.; Metson, J.; Evans, P.J.; Kinsey, R.; Bhattacharyya, D.

2007-01-01

Magnetron sputtered polycrystalline ZnO thin films were implanted using Al, Ag, Sn, Sb and codoped with TiN in order to improve the conductivity and to attempt to achieve p-type behaviour. Structural and electrical properties of the implanted ZnO thin films were examined with X-ray diffractometry (XRD), scanning electron microscopy (SEM), secondary ion mass spectrometry (SIMS), atomic force microscopy (AFM) and conductivity measurements. Depth profiles of the implanted elements varied with the implant species. Implantation causes a partial amorphisation of the crystalline structure and decreases the effective grain size of the films. One of the findings is the improvement, as a consequence of implantation, in the conductivity of initially poorly conductive samples. Heavy doping may help for the conversion of conduction type of ZnO thin films. Annealing in vacuum mitigated structural damage and stress caused by implantation, and improved the conductivity of the implanted ZnO thin films

Modulation-Doped In2O3/ZnO Heterojunction Transistors Processed from Solution

KAUST Repository

Khim, Dongyoon

2017-03-15

This paper reports the controlled growth of atomically sharp In2 O3 /ZnO and In2 O3 /Li-doped ZnO (In2 O3 /Li-ZnO) heterojunctions via spin-coating at 200 °C and assesses their application in n-channel thin-film transistors (TFTs). It is shown that addition of Li in ZnO leads to n-type doping and allows for the accurate tuning of its Fermi energy. In the case of In2 O3 /ZnO heterojunctions, presence of the n-doped ZnO layer results in an increased amount of electrons being transferred from its conduction band minimum to that of In2 O3 over the interface, in a process similar to modulation doping. Electrical characterization reveals the profound impact of the presence of the n-doped ZnO layer on the charge transport properties of the isotype In2 O3 /Li-ZnO heterojunctions as well as on the operating characteristics of the resulting TFTs. By judicious optimization of the In2 O3 /Li-ZnO interface microstructure, and Li concentration, significant enhancement in both the electron mobility and TFT bias stability is demonstrated.

Modulation-Doped In2O3/ZnO Heterojunction Transistors Processed from Solution

KAUST Repository

Khim, Dongyoon; Lin, Yen-Hung; Nam, Sungho; Faber, Hendrik; Tetzner, Kornelius; Li, Ruipeng; Zhang, Qiang; Li, Jun; Zhang, Xixiang; Anthopoulos, Thomas D.

2017-01-01

This paper reports the controlled growth of atomically sharp In2 O3 /ZnO and In2 O3 /Li-doped ZnO (In2 O3 /Li-ZnO) heterojunctions via spin-coating at 200 °C and assesses their application in n-channel thin-film transistors (TFTs). It is shown that addition of Li in ZnO leads to n-type doping and allows for the accurate tuning of its Fermi energy. In the case of In2 O3 /ZnO heterojunctions, presence of the n-doped ZnO layer results in an increased amount of electrons being transferred from its conduction band minimum to that of In2 O3 over the interface, in a process similar to modulation doping. Electrical characterization reveals the profound impact of the presence of the n-doped ZnO layer on the charge transport properties of the isotype In2 O3 /Li-ZnO heterojunctions as well as on the operating characteristics of the resulting TFTs. By judicious optimization of the In2 O3 /Li-ZnO interface microstructure, and Li concentration, significant enhancement in both the electron mobility and TFT bias stability is demonstrated.

Thin Film growth and characterization of Ti doped ZnO by RF/DC magnetron sputtering

KAUST Repository

Baseer Haider, M.

2015-01-01

Thin film Ti doped ZnO (Ti-ZnO) film were grown on sapphire (0001) substrate by RF and DC magnetron sputtering. Films were grown at a substrate temperature of 250 °C with different Ti/Zn concentration. Surface chemical study of the samples was performed by X-ray photoelectron spectroscopy to determine the stoichiometry and Ti/Zn ratio for all samples. Surface morphology of the samples were studied by atomic force microscopy. X-ray diffraction was carried out to determine the crystallinity of the film. No secondary phases of TixOy was observed. We observed a slight increase in the lattice constant with the increase in Ti concentration in ZnO. No ferromagnetic signal was observed for any of the samples. However, some samples showed super-paramagnetic phase. © 2015 Materials Research Society.

The Improvement of Electrical Characteristics of Pt/Ti Ohmic Contacts to Ga-Doped ZnO by Homogenized KrF Pulsed Excimer Laser Treatment

Science.gov (United States)

Oh, Min-Suk

2018-04-01

We investigated the effect of KrF excimer laser surface treatment on Pt/Ti ohmic contacts to Ga-doped n-ZnO ( N d = 4.3 × 1017 cm-3). The treatment of the n-ZnO surfaces by laser irradiation greatly improved the electrical characteristics of the metal contacts. The Pt/Ti ohmic layer on the laser-irradiated n-ZnO showed specific contact resistances of 2.5 × 10-4 ˜ 4.8 × 10-4 Ω cm2 depending on the laser energy density and gas ambient, which were about two orders of magnitude lower than that of the as-grown sample, 8.4 × 10-2 Ω cm2. X-ray photoelectron spectroscopy and photoluminescence measurements showed that the KrF excimer laser treatments increased the electron concentration near the surface region of the Ga-doped n-ZnO due to the preferential evaporation of oxygen atoms from the ZnO surface by the laser-induced dissociation of Zn-O bonds.

Improving the conductance of ZnO thin film doping with Ti by using a cathodic vacuum arc deposition process

International Nuclear Information System (INIS)

Wu, Chun-Sen; Lin, Bor-Tsuen; Jean, Ming-Der

2011-01-01

The Ti-doped ZnO films compared to un-doped ZnO films were deposited onto Corning XG glass substrates by using a cathodic vacuum arc deposition process in a mixture of oxygen and argon gases. The structural, electrical and optical properties of un-doped and Ti-doped ZnO films have been investigated. When the Ti target power is about 750 W, the incorporation of titanium atoms into zinc oxide films is obviously effective. Additionally, the resistivity of un-doped ZnO films is high and reduces to a value of 3.48 x 10 -3 Ω-cm when Ti is incorporated. The Ti doped in the ZnO films gave rise to the improvement of the conductivity of the films obviously. The Ti-doped ZnO films have > 85% transmittance in a range of 400-700 nm.

Effects of Sb-doping on the grain growth of Cu(In, Ga)Se2 thin films fabricated by means of single-target sputtering

International Nuclear Information System (INIS)

Zhang, Shu; Wu, Lu; Yue, Ruoyu; Yan, Zongkai; Zhan, Haoran; Xiang, Yong

2013-01-01

To investigate the effects of Sb doping on the kinetics of grain growth in Cu(In,Ga)Se 2 (CIGS) thin films during annealing, CIGS thin films were sputtered onto Mo coated substrates from a single CIGS alloy target, followed by chemical bath deposition of Sb 2 S 3 thin layers on top of CIGS layers and subsequent annealing at different temperatures for 30 min in Se vapors. X-ray diffraction results showed that CIGS thin films were obtained directly using the single-target sputtering method. After annealing, the In/Ga ratio in Sb-doped CIGS thin films remained stable compared to undoped film, possibly because Sb can promote the incorporation of Ga into CIGS. The grain growth in CIGS thin films was enhanced after Sb doping, exhibiting significantly larger grains after annealing at 400 °C or 450 °C compared to films without Sb. In particular, the effect was strikingly significant in grain growth across the film thickness, resulting in columnar grain structure in Sb-doped films. This grain growth improvement may be led by the diffusion of Sb from the front surface to the CIGS-Mo back interface, which promoted the mass transport process in CIGS thin films. - Highlights: ► Cu(In,Ga)Se 2 (CIGS) thin films made by sputtering from a single CIGS target. ► Chemical bath deposition used to introduce antimony into CIGS absorber layers. ► In/Ga ratio decreases in Sb-doped annealed films, comparatively to undoped films. ► Sb-doped CIGS films are superior to undoped films in terms of grain-growth kinetics

Doping Nitrogen in InGaZnO Thin Film Transistor with Double Layer Channel Structure.

Science.gov (United States)

Chang, Sheng-Po; Shan, Deng

2018-04-01

This paper presents the electrical characteristics of doping nitrogen in an amorphous InGaZnO thin film transistor. The IGZO:N film, which acted as a channel layer, was deposited using RF sputtering with a nitrogen and argon gas mixture at room temperature. The optimized parameters of the IGZO:N/IGZO TFT are as follows: threshold voltage is 0.5 V, field effect mobility is 14.34 cm2V-1S-1. The on/off current ratio is 106 and subthreshold swing is 1.48 V/decade. The positive gate bias stress stability of InGaZnO doping with nitrogen shows improvement compared to doping with oxygen.

Comparative investigation on cation-cation (Al-Sn) and cation-anion (Al-F) co-doping in RF sputtered ZnO thin films: Mechanistic insight

Energy Technology Data Exchange (ETDEWEB)

Mallick, Arindam; Basak, Durga, E-mail: sspdb@iacs.res.in

2017-07-15

Highlights: • Comparative study on Al, Al-Sn and Al-F doped ZnO films has been carried out. • High transparent Al-F co-doped film shows three times enhanced carrier density. • Al-F co-doped film shows larger carrier relaxation time. • Al-Sn co-doped films shows carrier transport dominated by impurity scattering. • Al-F co-doped ZnO film can be applied as transparent electrode. - Abstract: Herein, we report a comparative mechanistic study on cation-cation (Al-Sn) and cation-anion (Al-F) co-doped nanocrystalline ZnO thin films grown on glass substrate by RF sputtering technique. Through detailed analyses of crystal structure, surface morphology, microstructure, UV-VIS-NIR transmission-reflection and electrical transport property, the inherent characteristics of the co-doped films were revealed and compared. All the nanocrystalline films retain the hexagonal wurtzite structure of ZnO and show transparency above 90% in the visible and NIR region. As opposed to expectation, Al-Sn (ATZO) co-doped film show no enhanced carrier concentration consistent with the probable formation of SnO{sub 2} clusters supported by the X-ray photoelectron spectroscopy study. Most interestingly, it has been found that Al-F (AFZO) co-doped film shows three times enhanced carrier concentration as compared to Al doped and Al-Sn co-doped films attaining a value of ∼9 × 10{sup 20} cm{sup −3} due to the respective cation and anion substitution. The carrier relaxation time increases in AFZO while it decreases significantly for ATZO film consistent with the concurrence of the impurity scattering in the latter.

Optimization of Electrochemically Deposited Highly Doped ZnO Bilayers on Ga-Rich Chalcopyrite Selenide for Cost-Effective Photovoltaic Device Technology

Directory of Open Access Journals (Sweden)

Dimitra N. Papadimitriou

2016-11-01

Full Text Available High quality polycrystalline bilayers of aluminium doped ZnO (Al:ZnO were successively electrodeposited in the form of columnar structures preferentially oriented along the ( 10 1 ¯ 1 crystallographic direction from aqueous solution of zinc nitrate (Zn(NO32 at negative electrochemical potential of EC = (−0.8–(−1.2 V and moderate temperature of 80 °C on gallium rich (30% Ga chalcopyrite selenide Cu(In,GaSe2 (CIGS with chemically deposited ZnSe buffer (ZnSe/Cu(In,GaSe2/Mo/glass. The aluminium doped ZnO layer properties have initially been probed by deposition of Al:ZnO/i-ZnO bilayers directly on Mo/glass substrates. The band-gap energy of the Al:ZnO/i-ZnO reference layers was found to vary from 3.2 to 3.7 eV by varying the AlCl3 solute dopant concentration from 1 to 20 mM. The electrical resistivity of indium-pellet contacted highly doped Al:ZnO sheet of In/Al:ZnO/i-ZnO/Mo/glass reference samples was of the order ρ ~10−5 Ω·cm; the respective carrier concentration of the order 1022 cm−3 is commensurate with that of sputtered Al:ZnO layers. For crystal quality optimization of the bilayers by maintenance of the volatile selenium content of the chalcopyrite, they were subjected to 2-step annealing under successive temperature raise and N2 flux regulation. The hydrostatic compressive strain due to Al3+ incorporation in the ZnO lattice of bilayers processed successively with 5 and 12 mM AlCl3 dopant was εh = −0.046 and the respective stress σh = −20 GPa. The surface reflectivity of maximum 5% over the scanned region of 180–900 nm and the (optical band gap of Eg = 3.67 eV were indicative of the high optical quality of the electrochemically deposited (ECD Al:ZnO bilayers.

Highly transparent and conductive Al-doped ZnO nanoparticulate thin films using direct write processing

International Nuclear Information System (INIS)

Vunnam, S; Ankireddy, K; Kellar, J; Cross, W

2014-01-01

Solution processable Al-doped ZnO (AZO) thin films are attractive candidates for low cost transparent electrodes. We demonstrate here an optimized nanoparticulate ink for the fabrication of AZO thin films using scalable, low-cost direct write processing (ultrasonic spray deposition) in air at atmospheric pressure. The thin films were made via thermal processing of as-deposited films. AZO films deposited using the proposed nanoparticulate ink with further reducing in vacuum and rf plasma of forming gas exhibited optical transparency greater than 95% across the visible spectrum, and electrical resistivity of 0.5 Ω cm and it drops down to 7.0 × 10 −2 Ω cm after illuminating with UV light, which is comparable to commercially available tin doped indium oxide colloidal coatings. Various structural analyses were performed to investigate the influence of ink chemistry, deposition parameters, and annealing temperatures on the structural, optical, and electrical characteristics of the spray deposited AZO thin films. Optical micrographs confirmed the presence of surface defects and cracks using the AZO NPs ink without any additives. After adding N-(2-Aminoethyl)-3-aminopropylmethyldimethoxy silane to the ink, AZO films exhibited an optical transparency which was virtually identical to that of the plain glass substrate. (papers)

ZnO thin films and nanostructures for emerging optoelectronic applications

Science.gov (United States)

Rogers, D. J.; Teherani, F. H.; Sandana, V. E.; Razeghi, M.

2010-02-01

ZnO-based thin films and nanostructures grown by PLD for various emerging optoelectronic applications. AZO thin films are currently displacing ITO for many TCO applications due to recent improvements in attainable AZO conductivity combined with processing, cost and toxicity advantages. Advances in the channel mobilities and Id on/off ratios in ZnO-based TTFTs have opened up the potential for use as a replacement for a-Si in AM-OLED and AM-LCD screens. Angular-dependent specular reflection measurements of self-forming, moth-eye-like, nanostructure arrays grown by PLD were seen to have green gap in InGaN-based LEDs was combated by substituting low Ts PLD n-ZnO for MOCVD n-GaN in inverted hybrid heterojunctions. This approach maintained the integrity of the InGaN MQWs and gave LEDs with green emission at just over 510 nm. Hybrid n-ZnO/p-GaN heterojunctions were also seen to have the potential for UV (375 nm) EL, characteristic of ZnO NBE emission. This suggests that there was significant hole injection into the ZnO and that such LEDs could profit from the relatively high exciton binding energy of ZnO.

Magnetic Properties of Gadolinium-Doped ZnO Films and Nanostructures

KAUST Repository

Roqan, Iman S.

2016-08-29

The magnetic properties of Gd-doped ZnO films and nanostructures are important to the development of next-generation spintronic devices. Here, we elucidate the significant role played by Gd-oxygen-deficiency defects in mediating/inducing ferromagnetic coupling in in situ Gd-doped ZnO thin films deposited at low oxygen pressure by pulsed laser deposition (PLD). Samples deposited at higher oxygen pressures exhibited diamagnetic responses. Vacuum annealing was used on these diamagnetic samples (grown at a relatively high oxygen pressures) to create oxygen- deficiency defects with the aim of demonstrating reproducibility of room-temperature ferromagnetism (RTFM). Samples annealed at oxygen environment exhibited super‐ paramagnetism and blocking-temperature effects. The samples possessed secondary phases; Gd segregation led to superparamagnetism. Theoretical studies showed a shift of the 4f level of Gd to the conduction band minimum (CBM) in Gd-doped ZnO nanowires, which led to an overlap with the Fermi level, resulting in strong exchange coupling and consequently RTFM.

Determination of chemical state of Al doping element in ZnO layer

International Nuclear Information System (INIS)

Csik, A.; Toth, J.; Lovics, R.; Takats, V.; Hakl, J.; Vad, K.

2011-01-01

Complete text of publication follows. Transparent and conducting oxides (TCO) thin films are very important from the scientific and technological point of view. The coexistence of electrical conductivity and optical transparency in these materials makes it possible to use them in modern technologies: transparent electrodes for flat panel displays and photovoltaic cells, low emissivity windows, transparent thin films transistors, light emitting diodes. One of the important TCO semiconductors is the impurity-doped zinc-oxide (ZnO) layer, for example aluminium doped zinc-oxide layer (AZO), due to its unique physical and chemical properties. It has wide band gap (3.44 eV) and large exciton binding energy (60 meV). ZnO thin layers have a great interest for potential applications in optical and optoelectronic devices. Furthermore, high quality single crystal ZnO wafers has already been available as a result of new developments in ZnO growth technologies with the capability to scale up wafer size, which is an important factor for increasing efficiency of solar cells. Nonetheless, in order to enable the use of ZnO layers with enhanced electrical properties, higher conductivities can be obtained by doping with donor elements such as aluminium, gallium, indium, boron or fluorine. Investigation of p-type doping possibilities, diffusion processes and thermal stability of these layers are in the focus of interest in the interpretation of their optical and electrical properties, and the prediction of their lifetime. In our SNMS/SIMS-XPS laboratory, experiments on TCO layered structures were carried on. Depth profile and chemical state analyses of ZnO/AlO/ZnO layered structures were performed by Secondary Neutral Mass Spectrometry (SNMS) and X-ray photoelectron spectroscopy (XPS). The samples were produced by atomic layer deposition technique with the following layered structure: between a few hundred atomic layers of ZnO was an AlO atomic layer. The SNMS was used for depth

Effect of co-doping process on topography, optical and electrical properties of ZnO nanostructured

Science.gov (United States)

Mohamed, R.; Mamat, M. H.; Malek, M. F.; Ismail, A. S.; Yusoff, M. M.; Syamsir, S. A.; Khusaimi, Z.; Rusop, M.

2018-05-01

We investigated of Undoped ZnO and Magnesium (Mg)-Aluminium (Al) co-doped Zinc Oxide (MAZO) nanostructured films were prepared by sol gel spin coating technique. The surface topography was analyzed using Atomic Force Microscopy (AFM). Based on the AFM results, Root Mean Square (RMS) of MAZO films have rougher surface compared to pure ZnO films. The optical and electrical properties of thin film samples were characterized using Uv-Vis spectroscopy and two point probes, current-voltage (I-V) measurements. The transmittance spectra for both thin samples was above 80% in the visible wavelength. The MAZO film shows the highest conductivity compared to pure ZnO films. This result indicates that the improvement of carrier mobility throughout doping process and possibly contribute by extra ion charge.

Micro-patterned ZnO semiconductors for high performance thin film transistors via chemical imprinting with a PDMS stamp.

Science.gov (United States)

Seong, Kieun; Kim, Kyongjun; Park, Si Yun; Kim, Youn Sang

2013-04-07

Chemical imprinting was conducted on ZnO semiconductor films via a chemical reaction at the contact regions between a micro-patterned PDMS stamp and ZnO films. In addition, we applied the chemical imprinting on Li doped ZnO thin films for high performance TFTs fabrication. The representative micro-patterned Li doped ZnO TFTs showed a field effect mobility of 4.2 cm(2) V(-1) s(-1) after sintering at 300 °C.

Crystalline nanostructured Cu doped ZnO thin films grown at room temperature by pulsed laser deposition technique and their characterization

Energy Technology Data Exchange (ETDEWEB)

Drmosh, Qasem A. [Department of Mechanical Engineering, King Fahd University of Petroleum and Minerals, Dhahran 31261 (Saudi Arabia); Rao, Saleem G.; Yamani, Zain H. [Laser Research Group, Department of Physics, Center of Excellence in Nanotechnology, King Fahd University of Petroleum and Minerals, Dhahran 31261 (Saudi Arabia); Gondal, Mohammed A., E-mail: magondal@kfupm.edu.sa [Laser Research Group, Department of Physics, Center of Excellence in Nanotechnology, King Fahd University of Petroleum and Minerals, Dhahran 31261 (Saudi Arabia)

2013-04-01

We report structural and optical properties of Cu doped ZnO (ZnO:Cu) thin films deposited on glass substrate at room temperature by pulsed laser deposition (PLD) method without pre and post annealing contrary to all previous reports. For preparation of (ZnO:Cu) composites pure Zn and Cu targets in special geometrical arrangements were exposed to 248 nm radiations generated by KrF exciter laser. The laser energy was 200 mJ with 10 Hz frequency and 20 ns pulse width. The effect of Cu concentration on crystal structure, morphology, and optical properties were investigated by XRD, FESEM and photoluminescence spectrometer respectively. A systematic shift in ZnO (0 0 2) peak with Cu concentration observed in XRD spectra demonstrated that Cu ion has been incorporated in ZnO lattice. Uniform film with narrow size range grains were observed in FESEM images. The photoluminescence (PL) spectra measured at room temperature revealed a systematic red shift in ZnO emission peak and decrease in the band gap with the increase in Cu concentration. These results entail that PLD technique can be realized to deposit high quality crystalline ZnO and ZnO:Cu thin films without pre and post heat treatment which is normally practiced worldwide for such structures.

Low operation voltage of GaN-based LEDs with Al-doped ZnO upper contact directly on p-type GaN without insert layer

Science.gov (United States)

Chen, P. H.; Chen, Yu An; Chang, L. C.; Lai, W. C.; Kuo, Cheng Huang

2015-07-01

Al-doped ZnO (AZO) film was evaporated on double-side polished sapphire, p-GaN layers, n+-InGaN-GaN short-period superlattice (SPS) structures, and GaN-based light-emitting diodes (LEDs) by e-beam. The AZO film on the p-GaN layer after thermal annealing exhibited an extremely high transparency (98% at 450 nm) and a small specific contact resistance of 2.19 × 10-2 Ω cm2, which was almost the same as that of as-deposited AZO on n+-SPS structure. With 20 mA injection current, the forward voltages were 3.30 and 3.27 V, whereas the output powers were 4.32 and 4.07 mW for the LED with AZO on insert n+-SPS upper contact and the LED with AZO on p-GaN upper contact (without insert layer), respectively. The small specific contact resistance and low operation voltage of LED with AZO on p-GaN upper contact was achieved by rapid thermal annealing (RTA) process.

Selective growth of ZnO thin film nanostructures: Structure, morphology and tunable optical properties

Energy Technology Data Exchange (ETDEWEB)

Krishnakanth, Katturi Naga; Sunandana, C. S. [School of Physics, University of Hyderabad, Hyderabad-50046 (India); Rajesh, Desapogu, E-mail: rajesh.esapogu@gmail.com, E-mail: mperd@nus.edu.sg [School of Physics, University of Hyderabad, Hyderabad-50046 (India); Dept. of Mechanical Engineering, National University of Singapore (Singapore)

2016-05-23

The ZnO nanostructures (spherical, rod shape) have been successfully fabricated via a thermal evaporation followed by dip coating method. The pure, doped ZnO thin films were characterized by X-ray powder diffraction (XRD) and field emission scanning electron microscopy (FESEM) and UV-Vis spectroscopy, respectively. A possible growth mechanism of the spherical, rod shape ZnO nanostructures are discussed. XRD patterns revealed that all films consist of pure ZnO phase and were well crystallized with preferential orientation towards (002) direction. Doping by PVA, PVA+Cu has effective role in the enhancement of the crystalline quality and increases in the band gap.

Effect of the thin Ga2O3 layer in n+-ZnO/n-Ga2O3/p-Cu2O heterojunction solar cells

International Nuclear Information System (INIS)

Minami, Tadatsugu; Nishi, Yuki; Miyata, Toshihiro

2013-01-01

The influence of inserting a Ga 2 O 3 thin film as an n-type semiconductor layer on the obtainable photovoltaic properties in Cu 2 O-based heterojunction solar cells was investigated with a transparent conductive Al-doped ZnO (AZO) thin film/n-Ga 2 O 3 thin film/p-Cu 2 O sheet structure. It was found that this Ga 2 O 3 thin film can greatly improve the performance of Cu 2 O-based heterojunction solar cells fabricated using polycrystalline Cu 2 O sheets that had been prepared by a thermal oxidization of copper sheets. The obtained photovoltaic properties in the AZO/Ga 2 O 3 /Cu 2 O heterojunction solar cells were strongly dependent on the deposition conditions of the Ga 2 O 3 films. The external quantum efficiency obtained in AZO/Ga 2 O 3 /Cu 2 O heterojunction solar cells was found to be greater at wavelengths below approximately 500 nm than that obtained in AZO/Cu 2 O heterojunction solar cells (i.e., prepared without a Ga 2 O 3 layer) at equivalent wavelengths. This improvement of photovoltaic properties is mainly attributed to a decrease in the level of defects at the interface between the Ga 2 O 3 thin film and the Cu 2 O sheet. Conversion efficiencies over 5% were obtained in AZO/Ga 2 O 3 /Cu 2 O heterojunction solar cells fabricated using an n-Ga 2 O 3 thin-film layer prepared with a thickness of 40–80 nm at an O 2 gas pressure of approximately 1.7 Pa by a pulsed laser deposition. - Highlights: • We demonstrate high-efficiency Cu 2 O-based p-n heterojunction solar cells. • A non-doped Ga 2 O 3 thin film was used as an n-type semiconductor layer. • The Ga 2 O 3 thin film was prepared at a low temperature by a low damage deposition. • p-type Cu 2 O sheets prepared by thermal oxidization of copper sheets were used. • Conversion efficiencies over 5% were obtained in AZO/n-Ga 2 O 3 /p-Cu 2 O solar cells

Properties of Nb-doped ZnO transparent conductive thin films ...

Indian Academy of Sciences (India)

Administrator

by rf magnetron sputtering using a high quality ceramic target ... Guangxi Key Laboratory of Information Materials, Guilin University of Electronic ... films are highly textured along the c axis and perpendicular to the surface of the substrate. ... ZnO films; Nb-doped; magnetron sputtering; optical and electrical properties. 1.

Fabrication of cerium-doped β-Ga2O3 epitaxial thin films and deep ultraviolet photodetectors.

Science.gov (United States)

Li, Wenhao; Zhao, Xiaolong; Zhi, Yusong; Zhang, Xuhui; Chen, Zhengwei; Chu, Xulong; Yang, Hujiang; Wu, Zhenping; Tang, Weihua

2018-01-20

High-quality cerium-doped β-Ga 2 O 3 (Ga 2 O 3 :Ce) thin films could be achieved on (0001)α-Al 2 O 3 substrates using a pulsed-laser deposition method. The impact of dopant contents concentration on crystal structure, optical absorption, photoluminescence, and photoelectric properties has been intensively studied. X-ray diffraction analysis results have shown that Ga 2 O 3 :Ce films are highly (2¯01) oriented, and the lattice spacing of the (4¯02) planes is sensitive to the Ce doping level. The prepared Ga 2 O 3 :Ce films show a sharp absorption edge at about 250 nm, meaning a high transparency to deep ultraviolet (DUV) light. The photoluminescence results revealed that the emissions were in the violet-blue-green region, which are associated with the donor-acceptor transitions with the Ce 3+ and oxygen vacancies related defects. A simple DUV photodetector device with a metal-semiconductor-metal structure has also been fabricated based on Ga 2 O 3 :Ce thin film. A distinct DUV photoresponse was obtained, suggesting a potential application in DUV photodetector devices.

Decrease of oxygen vacancy by Zn-doped for improving solar-blind photoelectric performance in β-Ga2O3 thin films

Science.gov (United States)

Guo, Daoyou; Qin, Xinyuan; Lv, Ming; Shi, Haoze; Su, Yuanli; Yao, Guosheng; Wang, Shunli; Li, Chaorong; Li, Peigang; Tang, Weihua

2017-11-01

Highly (201) oriented Zn-doped β-Ga2O3 thin films with different dopant concentrations were grown on (0001) sapphire substrates by radio frequency magnetron sputtering. With the increase of Zn dopant concentration, the crystal lattice expands, the energy band gap shrinks, and the oxygen vacancy concentration decreases. Both the metal semiconductor metal (MSM) structure photodetectors based on the pure and Zn-doped β-Ga2O3 thin films exhibit solar blind UV photoelectric property. Compared to the pure β-Ga2O3 photodetector, the Zn-doped one exhibits a lower dark current, a higher photo/dark current ratio, a faster photoresponse speed, which can be attributed to the decreases of oxygen vacancy concentration.[Figure not available: see fulltext.

Genesis of flake-like morphology and dye-sensitized solar cell performance of Al-doped ZnO particles: a study

International Nuclear Information System (INIS)

Sengupta, D.; Mondal, B.; Mukherjee, K.

2017-01-01

In dye-sensitized solar cell (DSSC) application, the particulate morphologies of photo-anode facilitate efficient dye loading and thus lead to better photo-conversion efficiency than their thin film counterpart. However, till date, the electronic and optical properties as well as the DSSC application of Al-doped ZnO (AZO) particles as photo-anode material is studied less than thin films. Herein, phase formation behavior, morphology evolution, optical properties, and dye-sensitized solar cell performance of wet chemically prepared ZnO and AZO (dopant level: 1–4 mol%) particles are studied. It is found that Al doping modulates significantly the ZnO morphology which in turn results the maximum dye adsorption as well as best photo-conversion efficiency at optimum dopant concentration. Specifically, the nanoparticle of ZnO turns predominantly to flake-like morphology with a higher surface area when 2 mol% Al is doped. Such morphology modulation is expected, since the crystallinity, lattice parameters, and lattice strain of ZnO changes appreciably with Al doping. The variations of optical properties (absorbance, diffused reflectance, and band gap) of AZO materials as compared to primitive ZnO are also identified through UV-vis studies. An attempt is made here to correlate the structural features with the photovoltaic performances of ZnO and AZO.

Genesis of flake-like morphology and dye-sensitized solar cell performance of Al-doped ZnO particles: a study

Energy Technology Data Exchange (ETDEWEB)

Sengupta, D.; Mondal, B.; Mukherjee, K., E-mail: kalisadhanm@yahoo.com [CSIR-Central Mechanical Engineering Research Institute, Centre for Advanced Materials Processing (India)

2017-03-15

In dye-sensitized solar cell (DSSC) application, the particulate morphologies of photo-anode facilitate efficient dye loading and thus lead to better photo-conversion efficiency than their thin film counterpart. However, till date, the electronic and optical properties as well as the DSSC application of Al-doped ZnO (AZO) particles as photo-anode material is studied less than thin films. Herein, phase formation behavior, morphology evolution, optical properties, and dye-sensitized solar cell performance of wet chemically prepared ZnO and AZO (dopant level: 1–4 mol%) particles are studied. It is found that Al doping modulates significantly the ZnO morphology which in turn results the maximum dye adsorption as well as best photo-conversion efficiency at optimum dopant concentration. Specifically, the nanoparticle of ZnO turns predominantly to flake-like morphology with a higher surface area when 2 mol% Al is doped. Such morphology modulation is expected, since the crystallinity, lattice parameters, and lattice strain of ZnO changes appreciably with Al doping. The variations of optical properties (absorbance, diffused reflectance, and band gap) of AZO materials as compared to primitive ZnO are also identified through UV-vis studies. An attempt is made here to correlate the structural features with the photovoltaic performances of ZnO and AZO.

Effect of the thickness and hydrogen treatment on the properties of Ga-doped ZnO transparent conductive films

International Nuclear Information System (INIS)

Lee, Min-Jung; Lim, Jinhyong; Bang, Jungsik; Lee, Woong; Myoung, Jae-Min

2008-01-01

Combined effects of the thickness and hydrogen post-annealing treatment on the structural, electrical, and optical properties of Ga-doped ZnO (GZO) films were investigated as a potential substitute for indium tin oxide transparent conductive oxide. In the as-deposited films, microstructural evolution initially improved the crystallinity up to the thickness of 160 nm accompanying enhanced electrical and optical properties, but further thickness increase resulted in the deterioration of these properties attributable to the development of ZnGa 2 O 4 and Ga 2 O 3 phases originating from the excessive amount of the Ga dopant. Post-annealing treatment of the GZO films in a hydrogen atmosphere improved the electrical and optical properties substantially through possible reduction of the oxide phases and passivation of the surfaces and grain boundaries. In this case, electrical and optical properties remained almost similar for the thickness above 160 nm indicating that there exists a certain optimal film thickness.

Doping effect on SILAR synthesized crystalline nanostructured Cu-doped ZnO thin films grown on indium tin oxide (ITO) coated glass substrates and its characterization

Science.gov (United States)

Dhaygude, H. D.; Shinde, S. K.; Velhal, Ninad B.; Takale, M. V.; Fulari, V. J.

2016-08-01

In the present study, a novel chemical route is used to synthesize the undoped and Cu-doped ZnO thin films in aqueous solution by successive ionic layer adsorption and reaction (SILAR) method. The synthesized thin films are characterized by x-ray diffractometer (XRD), field emission scanning electron microscopy (FE-SEM), energy dispersive x-ray analysis (EDAX), contact angle goniometer and UV-Vis spectroscopic techniques. XRD study shows that the prepared films are polycrystalline in nature with hexagonal crystal structure. The change in morphology for different doping is observed in the studies of FE-SEM. EDAX spectrum shows that the thin films consist of zinc, copper and oxygen elements. Contact angle goniometer is used to measure the contact angle between a liquid and a solid interface and after detection, the nature of the films is initiated from hydrophobic to hydrophilic. The optical band gap energy for direct allowed transition ranging between 1.60-2.91 eV is observed.

Quantum corrections to temperature dependent electrical conductivity of ZnO thin films degenerately doped with Si

International Nuclear Information System (INIS)

Das, Amit K.; Ajimsha, R. S.; Kukreja, L. M.

2014-01-01

ZnO thin films degenerately doped with Si (Si x Zn 1−x O) in the concentrations range of ∼0.5% to 5.8% were grown by sequential pulsed laser deposition on sapphire substrates at 400 °C. The temperature dependent resistivity measurements in the range from 300 to 4.2 K revealed negative temperature coefficient of resistivity (TCR) for the 0.5%, 3.8%, and 5.8% doped Si x Zn 1−x O films in the entire temperature range. On the contrary, the Si x Zn 1−x O films with Si concentrations of 1.0%, 1.7%, and 2.0% showed a transition from negative to positive TCR with increasing temperature. These observations were explained using weak localization based quantum corrections to conductivity

X-ray photoelectron spectroscopy study and thermoelectric properties of Al-doped ZnO thin films

International Nuclear Information System (INIS)

Li Li; Fang Liang; Zhou Xianju; Liu Ziyi; Zhao Liang; Jiang Sha

2009-01-01

In this paper, high quality Al-doped ZnO (AZO) thin films were prepared by direct current (DC) reactive magnetron sputtering using a Zn target (99.99%) containing Al of 1.5 wt.%. The films obtained were characterized by X-ray photoelectron spectroscopy (XPS) and thermoelectric measurements. The XPS results reveal that Zn and Al exist only in oxidized state, while there are dominant crystal lattice and rare adsorbed oxygen for O in the annealed AZO thin films. The studies of thermoelectric property show a striking thermoelectric effect in the AZO thin films. On the one hand, the thermoelectromotive and magnetothermoelectromotive forces increase linearly with increasing temperature difference (ΔT). On the other hand, the thermoelectric power (TEP) decreases with the electrical resistance of the sample. But the TEP increases with the increase of temperature below 300 K, and it nearly does not change around room temperature. The experimental results also demonstrate that the annealing treatment increases TEP, while the external magnetic field degrades TEP.

Indium doped zinc oxide thin films obtained by electrodeposition

International Nuclear Information System (INIS)

Machado, G.; Guerra, D.N.; Leinen, D.; Ramos-Barrado, J.R.; Marotti, R.E.; Dalchiele, E.A.

2005-01-01

Indium doped ZnO thin films were obtained by co-electrodeposition (precursor and dopant) from aqueous solution. XRD analysis showed typical patterns of the hexagonal ZnO structure for both doped and undoped films. No diffraction peaks of any other structure such as In 2 O 3 or In(OH) 3 were found. The incorporation of In into the ZnO film was verified by both EDS and XPS measurements. The bandgap energy of the films varied from 3.27 eV to 3.42 eV, increasing with the In concentration in the solution. This dependence was stronger for the less cathodic potentials. The incorporation of In into the film occurs as both, an In donor state in the ZnO grains and as an amorphous In 2 O 3 at the grain boundaries

UV and visible photoluminescence emission intensity of undoped and In-doped ZnO thin film and photoresponsivity of ZnO:In/Si hetero-junction

International Nuclear Information System (INIS)

Zebbar, N.; Chabane, L.; Gabouze, N.; Kechouane, M.; Trari, M.; Aida, M.S.; Belhousse, S.; Hadj Larbi, F.

2016-01-01

Undoped zinc oxide (ZnO) and indium-doped (ZnO:In) thin films were grown at different temperatures (250–400 °C) on alkali-free borosilicate glass and n-Si (100) substrates by Ultrasonic Spray Pyrolysis method. The structural, compositional, optical and electrical properties of ZnO films were investigated by X-ray diffraction, Scanning Electron Microscopy, Rutherford Back Scattering Spectroscopy, Fourier Transform Infrared spectroscopy, photoluminescence (PL) and the four-point probe technique. The predominance of ultraviolet (UV) and blue emission intensities was found to be closely dependent on the resistivity of the film. The visible emission band (peaking at 432 nm) prevails for low film resistivity, ranging from 10 −2 to 1 Ω·cm. By contrast, for higher resistivity (> 1 Ω·cm), there is a predominance of the UV band (382 nm). The PL and photoresponsivity results of fabricated ZnO:In/n-Si(100) heterojunctions prepared at different temperatures are discussed. The maximum spectral response of the ZnO:8%In/Si heterojunction diode fabricated at 250 °C was about 80 mA/W at zero bias. The highlighted results are attractive for the optoelectronic applications. - Highlights: • Properties of ZnO thin films grown by Ultrasonic Spray Pyrolysis at 350 °C. • Photoluminescence emission intensity in undoped ZnO film: effect of the resistivity • Photoluminescence emission intensity of In-doped ZnO film is resistivity dependent. • The spectral response of ZnO:In/Si hetero-junction deposited in the range (250–400 °C)

UV and visible photoluminescence emission intensity of undoped and In-doped ZnO thin film and photoresponsivity of ZnO:In/Si hetero-junction

Energy Technology Data Exchange (ETDEWEB)

Zebbar, N., E-mail: nacbar2003@yahoo.fr [LCMS, Faculty of Physics, University of Sciences and Technology (USTHB), BP 32, El-Alia, Algiers (Algeria); Chabane, L. [LCMS, Faculty of Physics, University of Sciences and Technology (USTHB), BP 32, El-Alia, Algiers (Algeria); Gabouze, N. [CRTSE, 02 Bd. Frantz Fanon, BP 140, Algiers (Algeria); Kechouane, M. [LCMS, Faculty of Physics, University of Sciences and Technology (USTHB), BP 32, El-Alia, Algiers (Algeria); Trari, M. [Laboratory of Storage and Valorization of Renewable Energies, Faculty of Chemistry (USTHB), BP 32, El-Alia, Algiers (Algeria); Aida, M.S. [LCM et Interface, Faculty of Sciences, University of Constantine, 25000 (Algeria); Belhousse, S. [CRTSE, 02 Bd. Frantz Fanon, BP 140, Algiers (Algeria); Hadj Larbi, F. [MEMS & Sensors, Division Microélectronique et Nanotechnologie, Centre de Développement des Technologies Avancées (CDTA), BP 17, Baba Hassen, Algiers (Algeria)

2016-04-30

Undoped zinc oxide (ZnO) and indium-doped (ZnO:In) thin films were grown at different temperatures (250–400 °C) on alkali-free borosilicate glass and n-Si (100) substrates by Ultrasonic Spray Pyrolysis method. The structural, compositional, optical and electrical properties of ZnO films were investigated by X-ray diffraction, Scanning Electron Microscopy, Rutherford Back Scattering Spectroscopy, Fourier Transform Infrared spectroscopy, photoluminescence (PL) and the four-point probe technique. The predominance of ultraviolet (UV) and blue emission intensities was found to be closely dependent on the resistivity of the film. The visible emission band (peaking at 432 nm) prevails for low film resistivity, ranging from 10{sup −2} to 1 Ω·cm. By contrast, for higher resistivity (> 1 Ω·cm), there is a predominance of the UV band (382 nm). The PL and photoresponsivity results of fabricated ZnO:In/n-Si(100) heterojunctions prepared at different temperatures are discussed. The maximum spectral response of the ZnO:8%In/Si heterojunction diode fabricated at 250 °C was about 80 mA/W at zero bias. The highlighted results are attractive for the optoelectronic applications. - Highlights: • Properties of ZnO thin films grown by Ultrasonic Spray Pyrolysis at 350 °C. • Photoluminescence emission intensity in undoped ZnO film: effect of the resistivity • Photoluminescence emission intensity of In-doped ZnO film is resistivity dependent. • The spectral response of ZnO:In/Si hetero-junction deposited in the range (250–400 °C)

Effect of Al and Fe doping in ZnO on magnetic and magneto-transport properties

International Nuclear Information System (INIS)

Kumar, Santosh; Deepika; Tripathi, Malvika; Vaibhav, Pratyush; Kumar, Aman; Kumar, Ritesh; Choudhary, R.J.; Phase, D.M.

2016-01-01

The structural, magnetic and magneto-transport of undoped ZnO, Zn_0_._9_7Al_0_._0_3O, Zn_0_._9_5Fe_0_._0_5O and Zn_0_._9_2Al_0_._0_3Fe_0_._0_5O thin films grown on Si(100) substrate using pulsed laser deposition were investigated. The single phase nature of the films is confirmed by X-ray diffraction and Raman spectroscopy measurements. The possibility of Fe metal cluster in Fe doped/co-doped films is ruled out by Fe 2p core level photoelectron spectra. From O 1s core level spectra it is observed that oxygen vacancy is present in all the films. The undoped ZnO film shows magnetic ordering below ∼175 K, whereas Fe doped/codoped samples show magnetic ordering even at 300 K. The Al doped sample reveals paramagnetic behavior. The magneto-transport measurements suggest that the mobile carriers undergo exchange interaction with local magnetic moments. - Highlights: • Al, Fe, Al–Fe co-doped and undoped films of ZnO are deposited on Si by PLD. • Single phase (002) oriented Wurtzite ZnO phase is formed for all films. • Fe doped and Fe–Al co-doped ZnO films reveal magnetic hysteresis at 300 K. • Negative magnetoresistance is observed in undoped and Fe–Al co-doped ZnO film. • It is apparent that charge carriers are coupled with the local magnetic moment.

Effect of Al and Fe doping in ZnO on magnetic and magneto-transport properties

Energy Technology Data Exchange (ETDEWEB)

Kumar, Santosh, E-mail: skphysics@yahoo.co.in [Department of Physics, College of Commerce, Arts & Science, Patna 800020, Bihar (India); Deepika [Department of Physics, College of Commerce, Arts & Science, Patna 800020, Bihar (India); Tripathi, Malvika [UGC DAE, Consortium for scientific research, Indore 452001, Madhya Pradesh (India); Vaibhav, Pratyush [Jaypee University of Engineering and Technology, Guna 473226, Madhya Pradesh (India); Kumar, Aman [Indian Institute of Technology, Roorkee (India); Kumar, Ritesh [Department of Physics, College of Commerce, Arts & Science, Patna 800020, Bihar (India); Choudhary, R.J., E-mail: ram@csr.res.in [UGC DAE, Consortium for scientific research, Indore 452001, Madhya Pradesh (India); Phase, D.M. [UGC DAE, Consortium for scientific research, Indore 452001, Madhya Pradesh (India)

2016-12-01

The structural, magnetic and magneto-transport of undoped ZnO, Zn{sub 0.97}Al{sub 0.03}O, Zn{sub 0.95}Fe{sub 0.05}O and Zn{sub 0.92}Al{sub 0.03}Fe{sub 0.05}O thin films grown on Si(100) substrate using pulsed laser deposition were investigated. The single phase nature of the films is confirmed by X-ray diffraction and Raman spectroscopy measurements. The possibility of Fe metal cluster in Fe doped/co-doped films is ruled out by Fe 2p core level photoelectron spectra. From O 1s core level spectra it is observed that oxygen vacancy is present in all the films. The undoped ZnO film shows magnetic ordering below ∼175 K, whereas Fe doped/codoped samples show magnetic ordering even at 300 K. The Al doped sample reveals paramagnetic behavior. The magneto-transport measurements suggest that the mobile carriers undergo exchange interaction with local magnetic moments. - Highlights: • Al, Fe, Al–Fe co-doped and undoped films of ZnO are deposited on Si by PLD. • Single phase (002) oriented Wurtzite ZnO phase is formed for all films. • Fe doped and Fe–Al co-doped ZnO films reveal magnetic hysteresis at 300 K. • Negative magnetoresistance is observed in undoped and Fe–Al co-doped ZnO film. • It is apparent that charge carriers are coupled with the local magnetic moment.

Effects of intermittent atomization on the properties of Al-doped ZnO thin films deposited by aerosol-assisted chemical vapor deposition

Energy Technology Data Exchange (ETDEWEB)

Liu, Linjie; Wang, Lixin [Hebei Key Laboratory of Applied Chemistry, Yanshan University, Qinhuangdao 066004 (China); Qin, Xiujuan, E-mail: qinxj@ysu.edu.cn [Hebei Key Laboratory of Applied Chemistry, Yanshan University, Qinhuangdao 066004 (China); Cui, Li [Hebei Key Laboratory of Applied Chemistry, Yanshan University, Qinhuangdao 066004 (China); Shao, Guangjie [Hebei Key Laboratory of Applied Chemistry, Yanshan University, Qinhuangdao 066004 (China); State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China)

2016-04-30

Al-doped ZnO (AZO) thin films were prepared on glass substrates with different atomization interval times by aerosol-assisted chemical vapor deposition method. The structure, morphology, and optical and electrical properties were investigated by X-ray diffractometer, atomic force microscope, UV-vis double beam spectrophotometer and 4 point probe method. ZnO thin films exhibited strong growth orientation along the (002) plane and the crystalline was affected by the atomization interval time. All the films had high transmittance and the films with interval times of 2 min and 4 min had good haze values for the transparent conducting oxide silicon solar cell applications. The AZO thin film had the best optical and electrical properties when the atomization interval time was 4 min. This is very important for the optoelectronic device applications. The surface morphology of AZO films depended on the atomization interval time. - Highlights: • Intermittent atomization is proved to be an effective measure. • Atomization interval time has an important influence on the crystallinity of films. • The surface morphology of ZnO films depends on atomization interval time. • Different hazes can be obtained by changing the atomization interval time.

Effects of intermittent atomization on the properties of Al-doped ZnO thin films deposited by aerosol-assisted chemical vapor deposition

International Nuclear Information System (INIS)

Liu, Linjie; Wang, Lixin; Qin, Xiujuan; Cui, Li; Shao, Guangjie

2016-01-01

Al-doped ZnO (AZO) thin films were prepared on glass substrates with different atomization interval times by aerosol-assisted chemical vapor deposition method. The structure, morphology, and optical and electrical properties were investigated by X-ray diffractometer, atomic force microscope, UV-vis double beam spectrophotometer and 4 point probe method. ZnO thin films exhibited strong growth orientation along the (002) plane and the crystalline was affected by the atomization interval time. All the films had high transmittance and the films with interval times of 2 min and 4 min had good haze values for the transparent conducting oxide silicon solar cell applications. The AZO thin film had the best optical and electrical properties when the atomization interval time was 4 min. This is very important for the optoelectronic device applications. The surface morphology of AZO films depended on the atomization interval time. - Highlights: • Intermittent atomization is proved to be an effective measure. • Atomization interval time has an important influence on the crystallinity of films. • The surface morphology of ZnO films depends on atomization interval time. • Different hazes can be obtained by changing the atomization interval time.

Ga-doped ZnO films deposited with varying sputtering powers and substrate temperatures by pulsed DC magnetron sputtering and their property improvement potentials

International Nuclear Information System (INIS)

Lee, Sanghun; Cheon, Dongkeun; Kim, Won-Jeong; Ham, Moon-Ho; Lee, Woong

2012-01-01

Ga-doped ZnO (GZO) transparent conductive oxide (TCO) films were deposited on glass substrates by pulsed DC magnetron sputtering with varying sputtering power and substrate temperature while fixing the Ga concentration in the sputtering target. The application of higher sputtering power by pulsed DC magnetrons sputtering at a moderate temperature of 423 K results in increased carrier concentration and mobility which accompanied improved doping efficiency and crystalline quality. Substrate temperature was found to be the more dominant parameter in controlling the electrical properties and crystallinity, while the sputtering power played synergistic auxiliary roles. Electrical and optical properties of the GZO TCO films fulfilled requirements for transparent electrodes, despite relatively low substrate temperature (423 K) and small thickness (100 nm). In an attempt to improve the electrical properties of the GZO films by hydrogen-treatment, it was observed that the substitutional Ga plays the complex role of carrier generator as donor and carrier suppressor deactivating the oxygen vacancy simultaneously, which would complicate the property improvement by increasing doping efficiency.

Study of ytterbium doping effects on structural, mechanical and opto-thermal properties of sprayed ZnO thin films using the Boubaker Polynomials Expansion Scheme (BPES)

Energy Technology Data Exchange (ETDEWEB)

Amlouk, A. [Unite de physique des dispositifs a semi-conducteurs, Faculte des sciences de Tunis, Universite de Tunis El Manar, 2092 Tunis (Tunisia); Boubaker, K., E-mail: mmbb11112000@yahoo.f [Unite de physique des dispositifs a semi-conducteurs, Faculte des sciences de Tunis, Universite de Tunis El Manar, 2092 Tunis (Tunisia); Amlouk, M. [Unite de physique des dispositifs a semi-conducteurs, Faculte des sciences de Tunis, Universite de Tunis El Manar, 2092 Tunis (Tunisia); Bouhafs, M. [Unite de Recherche MA2I, Ecole Nationale d' Ingenieurs de Tunis, B.P. 37 Le Belvedere, 1002 Tunis (Tunisia)

2009-10-19

In this work, ZnO thin films have been grown on glass substrates by using a solution of propanol (C{sub 3}H{sub 8}O), water (H{sub 2}O) and zinc acetate (Z{sub n}(CH{sub 3}CO{sub 2}){sub 2}) in acidified medium (pH 5). The obtained films were n doped with ytterbium (Yb) at the rates of 100, 200 and 300 ppm. The structural features of the doped films were investigated using XRD, atomic force microscopy and scanning electronic microscopy techniques. XRD analysis shows a strong (0 0 2) X-ray diffraction line for increasing Yb-doping amounts. This c-axis preferential orientation of ZnO crystallites is naturally required to use this oxide as transparent conductor in optoelectronic applications. Atomic force microscopy (AFM) analysis shows an enhancement in the surface roughness of the doped ZnO:Yb thin films. Optical measurements were performed in 300-1800 nm domain via transmittance T(lambda) and reflectance R(lambda) spectra. Conjoint optical and thermal properties were deduced from the optical measurements in reference to the Amlouk-Boubaker opto-thermal expansivity psi{sub AB}. Optically relevant ytterbium doping effects have been discussed. Finally, mechanical measurements have been carried out using Vickers standard disposal. The results confirmed the structural and functional changes that several recent studies attributed to ytterbium doping.

Influence of annealing temperature on optical properties of Al doped ZnO nanoparticles via sol-gel methods

Science.gov (United States)

Rashid, Affa Rozana Abd; Hazwani, Tuan Nur; Mukhtar, Wan Maisarah; Taib, Nur Athirah Mohd

2018-06-01

Zinc oxide (ZnO) thin films have become technologically important materials due to their wide range of electrical and optical properties. The characteristics can be further adjusted by adequate doping processes. The effect of dopant concentration of Al, heating treatment and annealing in reducing atmosphere on the optical properties of the thin films is discussed. Undoped and aluminum-doped zinc oxide (AZO) thin films are prepared by the sol-gel method. Zinc acetate dihydrate, 2-methoxyethanol and monoethanolamine are used as precursor, solvent and stabilizer. In the case of AZO, aluminum nitrate nanohydrate is added to the precursor solution with an atomic percentage equal to 0 %, 1 %, 2 % and 3 % of Al. The multi thin layers are transformed into ZnO upon annealing at 450 °C and 500 °C. The optical properties such as transmittance, absorbance, band gap and refractive index of the thin films have been investigated by using UV-Visible Spectroscopy (UV-Vis). The results show that the effect of aluminium dopant concentration on the optical properties is depend on the post-heat treatment of the films. By doping with Al, the transmittance spectra in visible range increased and widen the band gap of ZnO which might due to Burstein-moss effects.

Performance of Cr-doped ZnO for acetone sensing

Energy Technology Data Exchange (ETDEWEB)

Al-Hardan, N.H., E-mail: naif_imen@ukm.my [Institute of Microengineering and Nanoelectronics (IMEN), Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor (Malaysia); Abdullah, M.J.; Aziz, A. Abdul [School of Physics, Universiti Sains Malaysia, 11800 USM, Penang (Malaysia)

2013-04-01

Zinc oxide (ZnO) doped with chromium (Cr) was synthesized by reactive co-sputtering for gas sensing applications. The effect of varying the contents of Cr (from 1 to 4 at%) on the ZnO gas sensor response was studied. X-ray diffraction analysis reveals the high orientation of c-axis of the prepared films. The optimum operating temperature of the undoped ZnO was 400 °C and shifted to 300 °C for the Cr-doped ZnO under the acetone vapour. The 1% Cr doping ZnO gas sensor was most sensitive for the acetone vapour. The ability of the 1% Cr-doped ZnO to produce repeatable results under different acetone vapour concentrations was tested. The timing properties of the doped Cr ZnO gas sensor were 70 and 95 s for the rise and recovery time respectively.

p-type ZnO films with solid-source phosphorus doping by molecular-beam epitaxy

International Nuclear Information System (INIS)

Xiu, F.X.; Yang, Z.; Mandalapu, L.J.; Liu, J.L.; Beyermann, W. P.

2006-01-01

Phosphorus-doped p-type ZnO films were grown on r-plane sapphire substrates using molecular-beam epitaxy with a solid-source GaP effusion cell. X-ray diffraction spectra and reflection high-energy electron diffraction patterns indicate that high-quality single crystalline (1120) ZnO films were obtained. Hall and resistivity measurements show that the phosphorus-doped ZnO films have high hole concentrations and low resistivities at room temperature. Photoluminescence (PL) measurements at 8 K reveal a dominant acceptor-bound exciton emission with an energy of 3.317 eV. The acceptor energy level of the phosphorus dopant is estimated to be 0.18 eV above the valence band from PL spectra, which is also consistent with the temperature dependence of PL measurements

Hydrogen absorption in thin ZnO films prepared by pulsed laser deposition

International Nuclear Information System (INIS)

Melikhova, O.; Čížek, J.; Lukáč, F.; Vlček, M.; Novotný, M.; Bulíř, J.; Lančok, J.; Anwand, W.; Brauer, G.; Connolly, J.; McCarthy, E.; Krishnamurthy, S.; Mosnier, J.-P.

2013-01-01

Highlights: ► Thin ZnO films and high quality ZnO crystal were electrochemically doped with hydrogen. ► Hydrogen absorbed in ZnO causes plastic deformation both in ZnO crystal and thin films. ► In ZnO crystal a sub-surface region with very high density of defects was formed. ► Moreover, plastic deformation causes specific surface modification of ZnO crystal. ► In ZnO films hydrogen-induced plastic deformation introduced defects in the whole film. -- Abstract: ZnO films with thickness of ∼80 nm were grown by pulsed laser deposition (PLD) on MgO (1 0 0) single crystal and amorphous fused silica (FS) substrates. Structural studies of ZnO films and a high quality reference ZnO single crystal were performed by slow positron implantation spectroscopy (SPIS). It was found that ZnO films exhibit significantly higher density of defects than the reference ZnO crystal. Moreover, the ZnO film deposited on MgO substrate exhibits higher concentration of defects than the film deposited on amorphous FS substrate most probably due to a dense network of misfit dislocations. The ZnO films and the reference ZnO crystal were subsequently loaded with hydrogen by electrochemical cathodic charging. SPIS characterizations revealed that absorbed hydrogen introduces new defects into ZnO

Hydrogen absorption in thin ZnO films prepared by pulsed laser deposition

Energy Technology Data Exchange (ETDEWEB)

Melikhova, O., E-mail: oksivmel@yahoo.com [Charles University in Prague, Faculty of Mathematics and Physics, V Holesovickach 2, CZ-180 00 Praha 8 (Czech Republic); Čížek, J.; Lukáč, F.; Vlček, M. [Charles University in Prague, Faculty of Mathematics and Physics, V Holesovickach 2, CZ-180 00 Praha 8 (Czech Republic); Novotný, M.; Bulíř, J.; Lančok, J. [Institute of Physics, Academy of Sciences of the Czech Republic, Na Slovance 2, 182 21 Prague (Czech Republic); Anwand, W.; Brauer, G. [Institut für Strahlenphysik, Helmholtz-Zentrum Dresden-Rossendorf, PO Box 510 119, D-01314 Dresden (Germany); Connolly, J.; McCarthy, E.; Krishnamurthy, S.; Mosnier, J.-P. [National Centre for Plasma Science and Technology, School of Physical Sciences, Glasnevin, Dublin 9 (Ireland)

2013-12-15

Highlights: ► Thin ZnO films and high quality ZnO crystal were electrochemically doped with hydrogen. ► Hydrogen absorbed in ZnO causes plastic deformation both in ZnO crystal and thin films. ► In ZnO crystal a sub-surface region with very high density of defects was formed. ► Moreover, plastic deformation causes specific surface modification of ZnO crystal. ► In ZnO films hydrogen-induced plastic deformation introduced defects in the whole film. -- Abstract: ZnO films with thickness of ∼80 nm were grown by pulsed laser deposition (PLD) on MgO (1 0 0) single crystal and amorphous fused silica (FS) substrates. Structural studies of ZnO films and a high quality reference ZnO single crystal were performed by slow positron implantation spectroscopy (SPIS). It was found that ZnO films exhibit significantly higher density of defects than the reference ZnO crystal. Moreover, the ZnO film deposited on MgO substrate exhibits higher concentration of defects than the film deposited on amorphous FS substrate most probably due to a dense network of misfit dislocations. The ZnO films and the reference ZnO crystal were subsequently loaded with hydrogen by electrochemical cathodic charging. SPIS characterizations revealed that absorbed hydrogen introduces new defects into ZnO.

Comparative effects of indium/ytterbium doping on, mechanical and gas-sensitivity-related morphological, properties of sprayed ZnO compounds

International Nuclear Information System (INIS)

Boukhachem, A.; Fridjine, S.; Amlouk, A.; Boubaker, K.; Bouhafs, M.; Amlouk, M.

2010-01-01

In this study, conducting and transparent indium-doped zinc oxide (ZnO) thin films have been deposited on glass substrates by the micro-spray technique. First, zinc oxide layers were obtained by spaying a solution of propanol and zinc acetate in acidified medium. Alternatively, some of the obtained films were doped with indium (In) at the molar rates of: 1%, 2% and 3%. In addition to the classical structural investigated using XRD, AFM and SEM techniques, microhardness Vickers (Hv) measurements have been carried out along with comparative morphological prospecting. The specific gases sensitivity-related surface morphology of the doped ZnO compounds was favorably different from that of the non-doped ones, and showed a thin overlay structure. Results were compared to those recorded for similar ytterbium-doped material.

Efficiencies of Eu{sup 3+} ions and hydrogen atoms as donors in ZnO thin films

Energy Technology Data Exchange (ETDEWEB)

Akazawa, Housei, E-mail: akazawa.housei@lab.ntt.co.jp [NTT Device Innovation Center, NTT Corporation, 3-1 Morinosato Wakamiya, Atsugi, Kanagawa 243-0198 (Japan)

2016-09-15

The donor efficiencies of Eu{sup 3+} ions and hydrogen atoms in ZnO crystalline films were investigated with reference to that of Ga{sup 3+} ions. It was found that Eu{sup 3+} ions acted as extrinsic donors in ZnO:Eu films, yielding a resistivity of 1.8 × 10{sup −3} Ω cm at a doping level of 1 at. %. This value is comparable to one for intrinsic donors in undoped ZnO films. The conductivity was maintained as the deposition temperature was increased to 200 °C, and this is evidence for the contribution of extrinsic donors. Deposition of Ga-doped and Eu-doped ZnO films in an H{sub 2}O gas flow produced oxyhydrogenated ZnO:(Ga, H) and ZnO:(Eu, H) films in which the Ga{sup 3+} and Eu{sup 3+} donors were deactivated by oxidization. Nevertheless, hydrogen donors contributed to electrical conduction yielding a resistivity of 1 × 10{sup −2} Ω cm. Postannealing in an H{sub 2} gas ambient alleviated the excessive oxidization of the films and thereby reactivated the donor action of Ga{sup 3+} and Eu{sup 3+} ions, causing the resistivity to recover to 10{sup −3} Ω cm for ZnO:(Ga, H) and 10{sup −2} Ω cm for ZnO:(Eu, H). In contrast, vacuum annealing of ZnO:(Ga, H) and ZnO:(Eu, H) films increased resistivity through removal of hydrogen donors while not affecting the oxidized condition of the samples.

Epitaxial GaN around ZnO nanopillars

Energy Technology Data Exchange (ETDEWEB)

Fikry, Mohamed; Scholz, Ferdinand [Institut fuer Optoelektronik, Universitaet Ulm, Albert-Einstein-Allee 45, 89081 Ulm (Germany); Madel, Manfred; Tischer, Ingo; Thonke, Klaus [Institut fuer Quantenmaterie, Universitaet Ulm, Albert-Einstein-Allee 45, 89081 Ulm (Germany)

2011-07-01

We report on an investigation of the epitaxial quality of GaN layers overgrown coaxially around ZnO nanopillars. In a first step, regularly arranged ZnO nanopillars were grown using pre-patterning by e-beam lithography or self-organized hexagonal polystyrene sphere masks. Alternatively, ZnO pillars were also successfully grown on top of GaN pyramids. In a second step, GaN layers were grown around the ZnO pillars by Metal Organic Vapor Phase Epitaxy. At growth temperatures above 800 C, the ZnO pillars are dissolved by the hydrogen carrier gas leaving hollow GaN nanotubes. Characterization involved photoluminescence (PL), scanning electron microscopy and cathodoluminescence. The fair quality of the deposited GaN layers is confirmed by a sharp low temperature PL peak at 3.48 eV attributed to the donor bound exciton emission. Further peaks at 3.42 eV and 3.29 eV show the possible existence of basal plane and prismatic stacking faults.

doped ZnO thick film resistors

Indian Academy of Sciences (India)

The characterization and ethanol gas sensing properties of pure and doped ZnO thick films were investigated. Thick films of pure zinc oxide were prepared by the screen printing technique. Pure zinc oxide was almost insensitive to ethanol. Thick films of Al2O3 (1 wt%) doped ZnO were observed to be highly sensitive to ...

Boron doped nanostructure ZnO films deposited by ultrasonic spray pyrolysis

Energy Technology Data Exchange (ETDEWEB)

Karakaya, Seniye, E-mail: seniyek@ogu.edu.tr; Ozbas, Omer

2015-02-15

Highlights: • Nanostructure undoped and boron doped ZnO films were deposited by USP technique. • Influences of doping on the surface and optical properties of the ZnO films were investigated. • XRD spectra of the films exhibited a variation in crystalline quality depending on the B content. - Abstract: ZnO is an II–VI compound semiconductor with a wide direct band gap of 3.3 eV at room temperature. Doped with group III elements (B, Al or Ga), it becomes an attractive candidate to replace tin oxide (SnO{sub 2}) or indium tin oxide (ITO) as transparent conducting electrodes in solar cell devices and flat panel display due to competitive electrical and optical properties. In this work, ZnO and boron doped ZnO (ZnO:B) films have been deposited onto glass substrates at 350 ± 5 °C by a cost-efficient ultrasonic spray pyrolysis technique. The optical, structural, morphological and electrical properties of nanostructure undoped and ZnO:B films have been investigated. Electrical resistivity of films has been analyzed by four-probe technique. Optical properties and thicknesses of the films have been examined in the wavelength range 1200–1600 nm by using spectroscopic ellipsometry (SE) measurements. The optical constants (refractive index (n) and extinction coefficient (k)) and the thicknesses of the films have been fitted according to Cauchy model. The optical method has been used to determine the band gap value of the films. Transmission spectra have been taken by UV spectrophotometer. It is found that both ZnO and ZnO:B films have high average optical transmission (≥80%). X-ray diffraction (XRD) patterns indicate that the obtained ZnO has a hexagonal wurtzite type structure. The morphological properties of the films were studied by atomic force microscopy (AFM). The surface morphology of the nanostructure films is found to depend on the concentration of B. As a result, ZnO:B films are promising contender for their potential use as transparent window layer and

Development of natively textured surface hydrogenated Ga-doped ZnO-TCO thin films for solar cells via magnetron sputtering

International Nuclear Information System (INIS)

Wang, Fei; Chen, Xin-liang; Geng, Xin-hua; Zhang, De-kun; Wei, Chang-chun; Huang, Qian; Zhang, Xiao-dan; Zhao, Ying

2012-01-01

Highlights: ► Natively textured surface hydrogenated gallium-doped zinc oxide (HGZO) thin films have been deposited via magnetron sputtering on glass substrates. ► The directly deposited HGZO thin films present rough crater-type surface morphology. ► Typical HGZO thin film exhibits a high electron mobility of 41.3 cm 2 /V s and a relative low sheet resistance of ∼7.0 Ω. ► These HGZO thin films have high optical transmittances in the visible and near infrared region (∼380–1100 nm). ► A gradient H 2 growth method for fabricating HGZO thin films has been proposed in magnetron sputtering process. - Abstract: The main purposes are to obtain high quality transparent conductive oxide (TCO) based on zinc oxide (ZnO) thin films with high optical transparency in the visible and near infrared spectral range, high electrical conductivity and good light-scattering capability to enhance the path of the light inside the Si-based thin film solar cells. Natively textured surface hydrogenated gallium-doped ZnO (HGZO) thin films have been deposited via pulsed direct current (DC) magnetron sputtering on glass substrates at a substrate temperature of 553 K. These natively textured HGZO thin films exhibit high optical transmittance (over 80%) in the visible and near infrared region (λ = 380–1100 nm) and excellent electrical properties. The optimized HGZO thin film with crater-type textured surface obtained at the hydrogen flow rate of ∼2.0 sccm exhibits a high electron mobility of 41.3 cm 2 /V s and a relatively low sheet resistance of ∼7.0 Ω. The influences of hydrogen flow rates on the surface morphology, electrical and optical properties of HGZO thin films were investigated in detail. In addition, we put forward a method of gradient H 2 growth technique for fabricating HGZO thin films so as to obtain rough surface structure with good light-scattering capability and high electrical conductivity. “Crater-like” surface feature size and optical transmittance

Ga+ focused-ion-beam implantation-induced masking for H2 etching of ZnO films

International Nuclear Information System (INIS)

Fang, Hsin-Chiao; Huang, Jun-Han; Chu, Wen-Huei; Liu, Chuan-Pu

2010-01-01

Gallium implantation of ZnO by a focused-ion beam is used to create a mask for ZnO dry etching with hydrogen. Effects of Ga + fluence on the etch stop properties and the associated mechanisms are investigated. The fluence of 2.8 x 10 16 cm -2 is determined to be optimum to render the best mask quality. While lower fluences would cause less etching selectivity, higher fluences would cause erosion of the surface and particles to be precipitated on the surface after H 2 treatment at high temperature. In contrast to the commonly adopted gallium oxide formation on Si, transmission electron microscopy analysis reveals that, for the fluences ≤ 2.8 x 10 16 cm -2 , Ga + ions are incorporated as dopants into ZnO without any second phases or precipitates, indicating the Ga-doped ZnO layer behaves as a mask for H 2 etching due to the higher electronegativity of Ga + towards oxygen. However, for the fluences ≥ 4.6 x 10 16 cm -2 , the surface particles are responsible for the etch stop and are identified as ZnGa 2 O 4 . We finally demonstrate a complicated pattern of 'NCKU' on ZnO by using this technique. The study not only helps clarify the related mechanisms, but also suggests a feasible extension of the etch stop process that can be applied to more functional material.

Study on Crystallographic Properties of Li Doped ZnO Thin Films

International Nuclear Information System (INIS)

Khine Khine Linn; Than Than Win; Yin Maung Maung; Ko Ko Kyaw Soe

2008-03-01

Li-doped ZnO film is prepared on highly polished Si substrate. The process temperature are range from 400 0 C to 600 0 C and maintained 1 hr for homogenization. According to the experimental results, it is significant that the growth chemistry is quite feasible and expected to be crystalline at above-mentioned temperatures.

Highly doped ZnO films deposited by spray-pyrolysis. Design parameters for optoelectronic applications

Energy Technology Data Exchange (ETDEWEB)

Garcés, F.A., E-mail: felipe.garces@santafe-conicet.gov.ar [Instituto de Física del Litoral (UNL-CONICET), Güemes 3450, Santa Fe S3000GLN (Argentina); Budini, N. [Instituto de Física del Litoral (UNL-CONICET), Güemes 3450, Santa Fe S3000GLN (Argentina); Schmidt, J.A.; Arce, R.D. [Instituto de Física del Litoral (UNL-CONICET), Güemes 3450, Santa Fe S3000GLN (Argentina); Facultad de Ingeniería Química, Universidad Nacional del Litoral, Santiago del Estero 2829, Santa Fe S3000AOM (Argentina)

2016-04-30

Synthesis and preparation of ZnO films are relevant subjects for obtaining transparent and conducting layers with interesting applications in optoelectronics and photovoltaics. Optimization of parameters such as dopant type and concentration, deposition time and substrate temperature is important for obtaining ZnO layers with optimal properties. In this work we present a study about the induced effects of deposition time on optical and electrical properties of ZnO thin films. These films were deposited by spray pyrolysis of a suitable Zn precursor, obtained through the sol–gel method. The deposition time has direct incidence on internal stress in the crystal structure, generating defects that may affect transparency and electrical transport into the layers. We performed mosaicity measurements, through X-ray diffraction, and used it as a tool to get an insight on structural characteristics and homogeneity of ZnO layers. Also, through this technique, we analyzed thickness and doping effects on crystallinity and carrier transport properties. - Highlights: • Al-doped ZnO films with high conductivity and moderate Hall mobility were obtained. • Mosaicity between crystalline domains increased with film thickness. • Lattice parameters a and c diminished linearly as a function of Al concentration. • First steps for developing porous silicon/doped ZnO heterojunctions were presented.

Highly doped ZnO films deposited by spray-pyrolysis. Design parameters for optoelectronic applications

International Nuclear Information System (INIS)

Garcés, F.A.; Budini, N.; Schmidt, J.A.; Arce, R.D.

2016-01-01

Synthesis and preparation of ZnO films are relevant subjects for obtaining transparent and conducting layers with interesting applications in optoelectronics and photovoltaics. Optimization of parameters such as dopant type and concentration, deposition time and substrate temperature is important for obtaining ZnO layers with optimal properties. In this work we present a study about the induced effects of deposition time on optical and electrical properties of ZnO thin films. These films were deposited by spray pyrolysis of a suitable Zn precursor, obtained through the sol–gel method. The deposition time has direct incidence on internal stress in the crystal structure, generating defects that may affect transparency and electrical transport into the layers. We performed mosaicity measurements, through X-ray diffraction, and used it as a tool to get an insight on structural characteristics and homogeneity of ZnO layers. Also, through this technique, we analyzed thickness and doping effects on crystallinity and carrier transport properties. - Highlights: • Al-doped ZnO films with high conductivity and moderate Hall mobility were obtained. • Mosaicity between crystalline domains increased with film thickness. • Lattice parameters a and c diminished linearly as a function of Al concentration. • First steps for developing porous silicon/doped ZnO heterojunctions were presented.

Effect of a Ga-doped ZnO thin film with a ZTO buffer layer fabricated by using pulsed DC magnetron sputter for dye-sensitized solar cells

Energy Technology Data Exchange (ETDEWEB)

Song, Sang-Woo; Lee, Kyung-Ju; Roh, Ji-Hyung; Park, On-Jeon; Kim, Hwan-Sun; Moon, Byung-Moo [Korea University, Seoul (Korea, Republic of); Ji, Min-Woo [Yonsei University, Seoul (Korea, Republic of)

2014-08-15

The electrical property of a Ga-doped ZnO(GZO) thin film is well known to be similar that of commercialized fluorine-doped tin oxide(FTO). However GZO is limited for use at high process temperatures for solar cells because of its unstable resistivity at temperatures above 300 .deg. C. A GZO thin film compared to zinc tin oxide(ZTO)-GZO multilayer can be used at high process temperatures. A GZO thin film was deposited on glass by using pulsed DC magnetron sputter. Then, a ZTO buffer layer was deposited on the GZO surface. During the deposition, the working pressure was 5 mTorr (Z-1 glass) and 1 mTorr (Z-2 glass). Dye-sensitized solar cells (DSSCs) were fabricated using Z-1, Z-2 and commercialized FTO glasses. Z-2 showed a conversion efficiency of 4.265%, which was enhanced by 0.399% compared to that of the DSSCs using FTO(3.784%). The conversion efficiency for Z-1 (3.889%) was a little higher than that of FTO. Thus, the ZTO-GZO electrode showed better characteristics than those obtained using the FTO electrode, which can be attributed to the reduced charge recombination and series resistance.

Activities towards p-type doping of ZnO

International Nuclear Information System (INIS)

Brauer, G; Kuriplach, J; Ling, C C; Djurisic, A B

2011-01-01

Zinc oxide (ZnO) is an interesting and promising semiconductor material for many potential applications, e.g. in opto-electronics and for sensor devices. However, its p-type doping represents a challenging problem, and the physical reasons of its mostly n-type conductivity are not perfectly clear at present. Efforts to achieve p-type conductivity by ion implantation are reviewed, and ways to achieve p-type ZnO nanorods and thin films through various growth conditions are summarized. Then, issues associated with the preparation of Schottky contacts is discussed in some detail as this is a requirement of the device formation process. Finally, the possible incorporation of hydrogen and nitrogen into structural defects, which can act as trapping sites for positrons, is discussed in the context of experimental and theoretical positron results and the estimated H and N content in a variety of ZnO materials.

Activities towards p-type doping of ZnO

Energy Technology Data Exchange (ETDEWEB)

Brauer, G [Institut fuer Ionenstrahlphysik und Materialforschung, Forschungszentrum Dresden-Rossendorf, Postfach 510119, D-01314 Dresden (Germany); Kuriplach, J [Department of Low Temperature Physics, Charles University, V Holetovickach 2, CZ-18000 Prague (Czech Republic); Ling, C C; Djurisic, A B, E-mail: g.brauer@fzd.de [Department of Physics, University of Hong Kong, Pokfulam Road (Hong Kong)

2011-01-10

Zinc oxide (ZnO) is an interesting and promising semiconductor material for many potential applications, e.g. in opto-electronics and for sensor devices. However, its p-type doping represents a challenging problem, and the physical reasons of its mostly n-type conductivity are not perfectly clear at present. Efforts to achieve p-type conductivity by ion implantation are reviewed, and ways to achieve p-type ZnO nanorods and thin films through various growth conditions are summarized. Then, issues associated with the preparation of Schottky contacts is discussed in some detail as this is a requirement of the device formation process. Finally, the possible incorporation of hydrogen and nitrogen into structural defects, which can act as trapping sites for positrons, is discussed in the context of experimental and theoretical positron results and the estimated H and N content in a variety of ZnO materials.

Positron annihilation spectroscopy in doped p-type ZnO

Science.gov (United States)

Majumdar, Sayanee; Sanyal, D.

2011-07-01

Positron annihilation lifetime (PAL) spectroscopy has been used to investigate the vacancy type defect of the Li and N doped ZnO. The mono-vacancies, shallow -vacancies and open volume defects have been found in both the Li and N doped ZnO. The mono-vacancies, shallow-vacancies and open volume defects increase in N-doped ZnO as the size of N is quite high compared to Li. Positron annihilation study showed that the doping above 1-3% Li and 3-4% N in ZnO are not required in order to achieve low resistivity, high hole concentration and good mobility.

Polarity in GaN and ZnO: Theory, measurement, growth, and devices

Science.gov (United States)

Zúñiga-Pérez, Jesús; Consonni, Vincent; Lymperakis, Liverios; Kong, Xiang; Trampert, Achim; Fernández-Garrido, Sergio; Brandt, Oliver; Renevier, Hubert; Keller, Stacia; Hestroffer, Karine; Wagner, Markus R.; Reparaz, Juan Sebastián; Akyol, Fatih; Rajan, Siddharth; Rennesson, Stéphanie; Palacios, Tomás; Feuillet, Guy

2016-12-01

The polar nature of the wurtzite crystalline structure of GaN and ZnO results in the existence of a spontaneous electric polarization within these materials and their associated alloys (Ga,Al,In)N and (Zn,Mg,Cd)O. The polarity has also important consequences on the stability of the different crystallographic surfaces, and this becomes especially important when considering epitaxial growth. Furthermore, the internal polarization fields may adversely affect the properties of optoelectronic devices but is also used as a potential advantage for advanced electronic devices. In this article, polarity-related issues in GaN and ZnO are reviewed, going from theoretical considerations to electronic and optoelectronic devices, through thin film, and nanostructure growth. The necessary theoretical background is first introduced and the stability of the cation and anion polarity surfaces is discussed. For assessing the polarity, one has to make use of specific characterization methods, which are described in detail. Subsequently, the nucleation and growth mechanisms of thin films and nanostructures, including nanowires, are presented, reviewing the specific growth conditions that allow controlling the polarity of such objects. Eventually, the demonstrated and/or expected effects of polarity on the properties and performances of optoelectronic and electronic devices are reported. The present review is intended to yield an in-depth view of some of the hot topics related to polarity in GaN and ZnO, a fast growing subject over the last decade.

Effect of Al-doped on physical properties of ZnO Thin films grown by spray pyrolysis on SnO2: F/glass

Directory of Open Access Journals (Sweden)

Castagné M.

2012-06-01

Full Text Available Transparent conducting thin films of aluminum-doped zinc oxide (ZnO:Al have been deposited on SnO2:F/glass by the chemical spray technique, starting from zinc acetate (CH3CO22Zn.2H2O and aluminum chloride AlCl3. The effect of changing the aluminum-to-zinc ratio y from 0 to 3 at.%, has been thoroughly investigated. It was found that the optical and electrical properties of Al doped ZnO films improved with the addition of aluminum in the spray solution until y=2%. At this Al doping percentage, the thin layers have a resistivity equal to 4.1 × 10−4 Ω.cm and a transmittance of about 90 % in the region [600-1000] nm. XRD patterns confirm that the films have polycristalline nature and a wurtzite (hexagonal structure which characterized with (100, (002 and (101 principal orientations. The undoped films have (002 as the preferred orientation but Al doped ones have (101 as the preferred orientation. Beyond y= 1%, peak intensities decrease considerably.

Ga vacancy induced ferromagnetism enhancement and electronic structures of RE-doped GaN

International Nuclear Information System (INIS)

Zhong Guohua; Zhang Kang; He Fan; Ma Xuhang; Lu Lanlan; Liu Zhuang; Yang Chunlei

2012-01-01

Because of their possible applications in spintronic and optoelectronic devices, GaN dilute magnetic semiconductors (DMSs) doped by rare-earth (RE) elements have attracted much attention since the high Curie temperature was obtained in RE-doped GaN DMSs and a colossal magnetic moment was observed in the Gd-doped GaN thin film. We have systemically studied the GaN DMSs doped by RE elements (La, Ce-Yb) using the full-potential linearized augmented plane wave method within the framework of density functional theory and adding the considerations of the electronic correlation and the spin-orbital coupling effects. We have studied the electronic structures of DMSs, especially for the contribution from f electrons. The origin of magnetism, magnetic interaction and the possible mechanism of the colossal magnetic moment were explored. We found that, for materials containing f electrons, electronic correlation was usually strong and the spin-orbital coupling was sometimes crucial in determining the magnetic ground state. It was found that GaN doped by La was non-magnetic. GaN doped by Ce, Nd, Pm, Eu, Gd, Tb and Tm are stabilized at antiferromagnetic phase, while GaN doped by other RE elements show strong ferromagnetism which is suitable materials for spintronic devices. Moreover, we have identified that the observed large enhancement of magnetic moment in GaN is mainly caused by Ga vacancies (3.0μB per Ga vacancy), instead of the spin polarization by magnetic ions or originating from N vacancies. Various defects, such as substitutional Mg for Ga, O for N under the RE doping were found to bring a reduction of ferromagnetism. In addition, intermediate bands were observed in some systems of GaN:RE and GaN with intrinsic defects, which possibly opens the potential application of RE-doped semiconductors in the third generation high efficiency photovoltaic devices.

The role of Al, Ba, and Cd dopant elements in tailoring the properties of c-axis oriented ZnO thin films

Energy Technology Data Exchange (ETDEWEB)

Ali, Dilawar [Department of Physics GC University, Lahore 54000 (Pakistan); Center for Advanced Studies in Physics, GC University Lahore, Lahore 54000 (Pakistan); Butt, M.Z., E-mail: mzakriabutt@gmail.com [Center for Advanced Studies in Physics, GC University Lahore, Lahore 54000 (Pakistan); Arif, Bilal [Department of Physics, Faculty of Arts and Sciences, Firat University, 23169 Elazig (Turkey); Al-Ghamdi, Ahmed A. [Department of Physics, Faculty of Sciences, King Abdul Aziz University, Jeddah (Saudi Arabia); Yakuphanoglu, Fahrettin [Department of Physics, Faculty of Arts and Sciences, Firat University, 23169 Elazig (Turkey); Department of Physics, Faculty of Sciences, King Abdul Aziz University, Jeddah (Saudi Arabia)

2017-02-01

Highly c-axis oriented un-doped ZnO and Al-, Ba-, and Cd-doped ZnO thin films were successfully deposited on glass substrate employing sol-gel spin coating method. XRD analysis showed that all thin films possess hexagonal wurtzite structure with preferred orientation along c-axis. Field emission scanning electron microscope (FESEM) was used to study the morphology of thin films. The morphology consists of spherical and non-spherical shape grains. EDX analysis confirms the presence of O, Zn, Al, Ba, and Cd in the relevant thin films. The optical properties of thin films were studied using UV–Vis spectrometer. All thin films possess more than 85% optical transmittance in the visible region. Blue shift in optical band gap E{sub g} has been observed on doping with Al, whereas doping with Ba and Cd resulted in red shift of E{sub g}. Urbach energy E{sub u} of all doped ZnO thin films was found to have excellent correlation with their band gap energy E{sub g}. Moreover, E{sub g} increases while E{sub u} decreases on the increase in crystallite size D. Optical parameters E{sub g} and E{sub u} as well as structural parameters lattice strain and stacking fault probability also show excellent correlation with the B-factor or the mean-square amplitude of atomic vibrations of the dopant elements. Electrical conductivity measurement of the thin films was carried out using two-point probe method. The electrical conductivity was found to increase with the increase in crystallite orientation along c-axis.

Luminescence evolution of porous GaN thin films prepared via UV-assisted electrochemical etching

International Nuclear Information System (INIS)

Cheah, S.F.; Lee, S.C.; Ng, S.S.; Yam, F.K.; Abu Hassan, H.; Hassan, Z.

2015-01-01

Porous gallium nitride (GaN) thin films with different surface morphologies and free carriers properties were fabricated from Si-doped GaN thin films using ultra-violet assisted electrochemical etching approach under various etching voltages. Fluctuation of luminescence signals was observed in the photoluminescence spectra of porous GaN thin films. Taking advantage of the spectral sensitivity of infrared attenuated total reflection spectroscopy on semiconductor materials, roles of free carriers and porous structure in controlling luminescence properties of GaN were investigated thoroughly. The results revealed that enhancement in luminescence signal is not always attained upon porosification. Although porosification is correlated to the luminescence enhancement, however, free carrier is the primary factor to enhance luminescence intensity. Due to unavoidable significant reduction of free carriers from Si-doped GaN in the porosification process, control of etching depth (i.e., thickness of porous layer formed from the Si-doped layer) is critical in fabricating porous GaN thin film with enhanced luminescence response. - Highlights: • Various pore morphologies with free carrier properties are produced by Si-doped GaN. • Free carriers are important to control the luminescence signal of porous GaN. • Enhancement of luminescence signal relies on the pore depth of Si-doped layer

Strain-free GaN thick films grown on single crystalline ZnO buffer layer with in situ lift-off technique

International Nuclear Information System (INIS)

Lee, S. W.; Minegishi, T.; Lee, W. H.; Goto, H.; Lee, H. J.; Lee, S. H.; Lee, Hyo-Jong; Ha, J. S.; Goto, T.; Hanada, T.; Cho, M. W.; Yao, T.

2007-01-01

Strain-free freestanding GaN layers were prepared by in situ lift-off process using a ZnO buffer as a sacrificing layer. Thin Zn-polar ZnO layers were deposited on c-plane sapphire substrates, which was followed by the growth of Ga-polar GaN layers both by molecular beam epitaxy (MBE). The MBE-grown GaN layer acted as a protecting layer against decomposition of the ZnO layer and as a seeding layer for GaN growth. The ZnO layer was completely in situ etched off during growth of thick GaN layers at low temperature by hydride vapor phase epitaxy. Hence freestanding GaN layers were obtained for the consecutive growth of high-temperature GaN thick layers. The lattice constants of freestanding GaN agree with those of strain-free GaN bulk. Extensive microphotoluminescence study indicates that strain-free states extend throughout the high-temperature grown GaN layers

On single doping and co-doping of spray pyrolysed ZnO films: Structural, electrical and optical characterisation

International Nuclear Information System (INIS)

Vimalkumar, T.V.; Poornima, N.; Jinesh, K.B.; Kartha, C. Sudha; Vijayakumar, K.P.

2011-01-01

In this paper we present studies on ZnO thin films (prepared using Chemical Spray pyrolysis (CSP) technique) doped in two different ways; in one set, 'single doping' using indium was done while in the second set, 'co-doping' using indium and fluorine was adopted. In the former case, effect of in-situ as well as ex-situ doping using In was analyzed. Structural (XRD studies), electrical (I-V measurements) and optical characterizations (through absorption, transmission and photoluminescence studies) of the films were done. XRD analysis showed that, for spray-deposited ZnO films, ex-situ doping using Indium resulted in preferred (0 0 2) plane orientation, while in-situ doping caused preferred orientation along (1 0 0), (0 0 2), (1 0 1) planes; however for higher percentage of in-situ doping, orientation of grains changed from (0 0 2) plane to (1 0 1) plane. The co-doped films had (0 0 2) and (1 0 1) planes. Lowest resistivity (2 x 10 -3 Ω cm) was achieved for the films, doped with 1% Indium through in-situ method. Photoluminescence (PL) emissions of ex-situ doped and co-doped samples had two peaks; one was the 'near band edge' emission (NBE) and the other was the 'blue-green' emission. But interestingly the PL emission of in-situ doped samples exhibited only the 'near band edge' emission. Optical band gap of the films increased with doping percentage, in all cases of doping.

Mg-doped ZnO thin films deposited by the atomic layer chemical vapor deposition for the buffer layer of CIGS solar cell

Energy Technology Data Exchange (ETDEWEB)

Li, Zhao-Hui [Department of Electronics Engineering, Gachon University, Soojung-gu, Seongnam city 461-701, Gyunggi-do (Korea, Republic of); Center for Photovoltaic and Solar Energy, Shenzhen Institutes of Advanced Technology, Chinese Academy of Sciences, Shenzhen city 518055 (China); Cho, Eou-Sik [Department of Electronics Engineering, Gachon University, Soojung-gu, Seongnam city 461-701, Gyunggi-do (Korea, Republic of); Kwon, Sang Jik, E-mail: sjkwon@gachon.ac.kr [Department of Electronics Engineering, Gachon University, Soojung-gu, Seongnam city 461-701, Gyunggi-do (Korea, Republic of)

2014-09-30

Highlights: • Mg-doped ZnO film as CIGS buffer was prepared by ALD process. • The grain size of ZnO-like hexagonal phase decreased with Mg content. • The transmittance and crystallinity increased but the band gap decreased with temperature. - Abstract: Mg-doped ZnO [(Zn, Mg)O] thin films were prepared by atomic layer chemical vapor deposition (ALCVD) process with different Mg content, using diethyl zinc, biscyclopentadienyl magnesium, and water as the metal and oxygen sources, respectively. The ratio of Mg to Zn was varied by changing the pulse ratio of MgCp{sub 2} to DEZn precursor to study its effect on the properties of (Zn, Mg)O thin films. From the experimental results, it was shown that the grain size of the ZnO-like hexagonal phase (Zn, Mg)O decreased as the Mg content increased. But the transmittance and optical band gap of (Zn, Mg)O films increased with the increase of the Mg content. In addition, the effect of the substrate temperature on the properties of (Zn, Mg)O films was also investigated. The deposition rate, transmittance, and crystallinity of (Zn, Mg)O films increased as the substrate temperature increased. But its band gap decreased slightly with the increase of substrate temperature.

Effect of growth temperature on the epitaxial growth of ZnO on GaN by ALD

Science.gov (United States)

Särkijärvi, Suvi; Sintonen, Sakari; Tuomisto, Filip; Bosund, Markus; Suihkonen, Sami; Lipsanen, Harri

2014-07-01

We report on the epitaxial growth of ZnO on GaN template by atomic layer deposition (ALD). Diethylzinc (DEZn) and water vapour (H2O) were used as precursors. The structure and the quality of the grown ZnO layers were studied with scanning electron microscope (SEM), X-ray diffraction (XRD), photoluminescence (PL) measurements and positron annihilation spectroscopy. The ZnO films were confirmed epitaxial, and the film quality was found to improve with increasing deposition temperature in the vicinity of the threshold temperature of two dimensional growth. We conclude that high quality ZnO thin films can be grown by ALD. Interestingly only separate Zn-vacancies were observed in the films, although ZnO thin films typically contain fairly high density of surface pits and vacancy clusters.

Synthesis and characterization of Mn-doped ZnO column arrays

International Nuclear Information System (INIS)

Yang Mei; Guo Zhixing; Qiu Kehui; Long Jianping; Yin Guangfu; Guan Denggao; Liu Sutian; Zhou Shijie

2010-01-01

Mn-doped ZnO column arrays were successfully synthesized by conventional sol-gel process. Effect of Mn/Zn atomic ratio and reaction time were investigated, and the morphology, tropism and optical properties of Mn-doped ZnO column arrays were characterized by SEM, XRD and photoluminescence (PL) spectroscopy. The result shows that a Mn/Zn atomic ratio of 0.1 and growth time of 12 h are the optimal condition for the preparation of densely distributed ZnO column arrays. XRD analysis shows that Mn-doped ZnO column arrays are highly c-axis oriented. As for Mn-doped ZnO column arrays, obvious increase of photoluminescence intensity is observed at the wavelength of ∼395 nm and ∼413 nm, compared to pure ZnO column arrays.

Mn doped GaN thin films and nanoparticles

Czech Academy of Sciences Publication Activity Database

Šofer, Z.; Sedmidubský, D.; Huber, Š.; Hejtmánek, Jiří; Macková, Anna; Fiala, R.

2012-01-01

Roč. 9, 8-9 (2012), s. 809-824 ISSN 1475-7435 R&D Projects: GA ČR GA104/09/0621 Institutional research plan: CEZ:AV0Z10100521; CEZ:AV0Z10480505 Keywords : GaN nanoparticles * GaN thin films * manganese * transition metals * MOVPE * ion implantations Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.087, year: 2012

Structural, optical and magnetic characterization of Ru doped ZnO nanorods

International Nuclear Information System (INIS)

Kumar, Sanjeev; Kaur, Palvinder; Chen, C.L.; Thangavel, R.; Dong, C.L.; Ho, Y.K.; Lee, J.F.; Chan, T.S.; Chen, T.K.; Mok, B.H.; Rao, S.M.; Wu, M.K.

2014-01-01

Graphical abstract: Ruthenium (Ru = 0%, 1% and 2%) doped nano-crystalline zinc oxide (ZnO) nanorods were synthesized by using well-known sol–gel technique. X-ray diffraction (XRD) results show that Ru (0%, 1% and 2%) doped ZnO nanorods crystallized in the wurtzite structure having space group C 3v (P6 3 mc). Williamson and Hall plot reveal that in the nanoscale dimensions, incorporation of Ru induced the tensile strain in ZnO host matrix. Photoluminescence (PL) and Raman studies of Ru doped ZnO nanorods show the formation of singly ionized oxygen vacancies which may account for the observed room temperature ferromagnetism (RTFM) in 2% Ru doped ZnO. X-ray absorption spectroscopy (XAS) reveals that Ru replace the Zn atoms in the host lattice and maintain the crystal symmetry with slightly lattice distortion. Highlights: • Ru doped ZnO nanorods crystallized in the wurtzite structure having space group C 3v (P6 3 mc). • PL and Raman studies show the formation of singly ionized oxygen vacancies in 2% Ru doped ZnO. • XAS reveals that Ru replace the Zn atoms in the host lattice with slightly lattice distortion. • Doping of Ru in ZnO nanostructures gives rise to RTFM ordering. -- Abstract: Ruthenium (Ru = 0%, 1% and 2%) doped nano-crystalline zinc oxide (ZnO) nanorods were synthesized by using well-known sol–gel technique. X-ray diffraction (XRD) results show that Ru (0%, 1% and 2%) doped ZnO nanorods crystallized in the wurtzite structure having space group C 3v (P6 3 mc). Williamson and Hall plot reveal that in the nanoscale dimensions, incorporation of Ru induced the tensile strain in ZnO host matrix. Photoluminescence (PL) and Raman studies of Ru doped ZnO nanorods show the formation of singly ionized oxygen vacancies which may account for the observed room temperature ferromagnetism (RTFM) in 2% Ru doped ZnO. X-ray absorption spectroscopy (XAS) reveals that Ru replace the Zn atoms in the host lattice and maintain the crystal symmetry with slightly lattice

Enhanced room temperature ferromagnetism in electrodeposited Co-doped ZnO nanostructured thin films by controlling the oxygen vacancy defects

Energy Technology Data Exchange (ETDEWEB)

Simimol, A. [Nanomaterials Research Lab, Surface Engineering Division, CSIR-National Aerospace Laboratories, Post Bag No. 1779, Bangalore 560017 (India); Department of Physics, National Institute of Technology Calicut, Calicut 673601 (India); Anappara, Aji A. [Department of Physics, National Institute of Technology Calicut, Calicut 673601 (India); Greulich-Weber, S. [Department of Physics, Nanophotonic Materials, Faculty of Science, University of Paderborn, 33095 Paderborn (Germany); Chowdhury, Prasanta [Nanomaterials Research Lab, Surface Engineering Division, CSIR-National Aerospace Laboratories, Post Bag No. 1779, Bangalore 560017 (India); Barshilia, Harish C., E-mail: harish@nal.res.in

2015-06-07

We report the growth of un-doped and cobalt doped ZnO nanostructures fabricated on FTO coated glass substrates using electrodeposition method. A detailed study on the effects of dopant concentration on morphology, structural, optical, and magnetic properties of the ZnO nanostructures has been carried out systematically by varying the Co concentration (c.{sub Co}) from 0.01 to 1 mM. For c.{sub Co }≤ 0.2 mM, h-wurtzite phase with no secondary phases of Co were present in the ZnO nanostructures. For c.{sub Co} ≤ 0.2 mM, the photoluminescence spectra exhibited a decrease in the intensity of ultraviolet emission as well as band-gap narrowing with an increase in dopant concentration. All the doped samples displayed a broad emission in the visible range and its intensity increased with an increase in Co concentration. It was found that the defect centers such as oxygen vacancies and zinc interstitials were the source of the visible emission. The X-ray photoelectron spectroscopy studies revealed, Co was primarily in the divalent state, replacing the Zn ion inside the tetrahedral crystal site of ZnO without forming any cluster or secondary phases of Co. The un-doped ZnO nanorods exhibited diamagnetic behavior and it remained up to a c.{sub Co} of 0.05 mM, while for c.{sub Co }> 0.05 mM, the ZnO nanostructures exhibited ferromagnetic behavior at room temperature. The coercivity increased to 695 G for 0.2 mM Co-doped sample and then it decreased for c.{sub Co }> 0.2 mM. Our results illustrate that up to a threshold concentration of 0.2 mM, the strong ferromagnetism is due to the oxygen vacancy defects centers, which exist in the Co-doped ZnO nanostructures. The origin of strong ferromagnetism at room temperature in Co-doped ZnO nanostructures is attributed to the s-d exchange interaction between the localized spin moments resulting from the oxygen vacancies and d electrons of Co{sup 2+} ions. Our findings provide a new insight for tuning the

Mott transition in Ga-doped Mg{sub x}Zn{sub 1-x}O: A direct observation

Energy Technology Data Exchange (ETDEWEB)

Wei Wei; Nori, Sudhakar [Department of Materials Science and Engineering, North Carolina State University, Raleigh, NC (United States); Jin Chunming [Department of Biomedical Engineering, University of North Carolina and North Carolina State University, Campus Box 7115, Raleigh, NC 27695-7115 (United States); Narayan, Jagdish [Department of Materials Science and Engineering, North Carolina State University, Raleigh, NC (United States); Narayan, Roger J., E-mail: roger_narayan@unc.edu [Department of Biomedical Engineering, University of North Carolina and North Carolina State University, Campus Box 7115, Raleigh, NC 27695-7115 (United States); Ponarin, Dmtri; Smirnov, Alex [Department of Chemistry, North Carolina State University, Raleigh, NC (United States)

2010-07-25

This paper reports the direct evidence for Mott transition in Ga-doped Mg{sub x}Zn{sub 1-x}O thin films. Highly transparent Ga-doped Mg{sub x}Zn{sub 1-x}O thin films were grown on c-plane sapphire substrates using pulsed laser deposition. 0.1 at.%, 0.5 at.% and 1 at.% Ga-doped Mg{sub 0.1}Zn{sub 0.9}O films were selected for resistivity measurements in the temperature range from 250 K to 40 mK. The 0.1 at.% Ga-doped Mg{sub 0.1}Zn{sub 0.9}O thin film showed typical insulator-like behavior and the 1 at.% Ga-doped Mg{sub 0.1}Zn{sub 0.9}O thin film showed typical metal-like behavior. The 0.5 at.% Ga-doped Mg{sub 0.1}Zn{sub 0.9}O film showed increasing resistivity with decreasing temperature; resistivity was saturated with a value of 1.15 x 10{sup -2} {Omega} cm at 40 mK, which is characteristic of the metal-insulator transition region. Temperature-dependent conductivity {sigma}(T) in the low temperature range revealed that the electron-electron scattering is the dominant dephasing mechanism. The inelastic scattering time is found to vary as T{sup -3/2}.

Influence of Al concentration and annealing temperature on structural, optical, and electrical properties of Al co-doped ZnO thin films

International Nuclear Information System (INIS)

Gürbüz, Osman; Kurt, İsmail; Çalışkan, Serkan; Güner, Sadık

2015-01-01

Highlights: • RF magnetron sputtering technique seems to be very efficient method for fabrication of Al doped ZnO (AZO) films. • Long range single crystalline structure improves with annealing process. • Optical properties became much better after annealing process especially for the AZO films that include high Al concentration. • Much greater conductivity with increasing Al concentration and annealing process. • AZO films have potential applicability in spintronic devices. - Abstract: The pure ZnO and Al-doped ZnO (AZO) thin films (thickness: 200 nm) were prepared on both side polished silica (SiO 2 ) substrates via RF magnetron sputtering at room temperature by using 2.5 inches high-purity ZnO (99.9%) and Al (99.9%) targets. The samples were annealed at 300 °C, 400 °C and 500 °C for 45 min in N 2 ambient in quartz annealing furnace system, respectively. We investigated the effects of various Al concentrations and annealing treatment on the structural, electrical, and optical properties of films. The preferred crystallization was observed along c axis (single (0 0 2) diffraction peak) from substrate surface assigning the single crystalline Würtzite lattice for pure ZnO and AZO thin films. Although increasing Al concentration decreases the order of crystallization of as-grown films, annealing process increases the long range crystal order. The crystallite sizes vary between minimum 12.98 nm and maximum 20.79 nm for as-grown and annealed samples. The crystallite sizes decrease with increasing Al concentration but increase with increasing annealing temperature as general trend. The grain size and porosity of films change with annealing treatment. The smaller grains coalesce together to form larger grains for many films. However, a reverse behavior is seen for Al 2.23 ZnO and Al 12.30 ZnO samples. That is, Al concentration plays critical role as well as temperature on grain size. Low percent optical transmittance (T%) is observed due to higher Al

Microstructure and optical properties of nanocrystalline ZnO and ZnO:(Li or Al) thin films

Energy Technology Data Exchange (ETDEWEB)

Oral, A. Yavuz [Department of Materials Science and Engineering, Gebze Institute of Technology, Gebze 41400 (Turkey)]. E-mail: aoral@gyte.edu.tr; Bahsi, Z. Banu [Department of Materials Science and Engineering, Gebze Institute of Technology, Gebze 41400 (Turkey); Aslan, M. Hasan [Department of Physics, Gebze Institute of Technology, Gebze 41400 (Turkey)

2007-03-15

Zinc oxide thin films (ZnO, ZnO:Li, ZnO:Al) were deposited on glass substrates by a sol-gel technique. Zinc acetate, lithium acetate, and aluminum chloride were used as metal ion sources in the precursor solutions. XRD analysis revealed that Li doped and undoped ZnO films formed single phase zincite structure in contrast to Al:ZnO films which did not fully crystallize at the annealing temperature of 550 deg. C. Crystallized films had a grain size under 50 nm and showed c-axis grain orientation. All films had a very smooth surface with RMS surface roughness values between 0.23 and 0.35 nm. Surface roughness and optical band tail values increased by Al doping. Compared to undoped ZnO films, Li doping slightly increased the optical band gap of the films.

Fabrication of the heterojunction diode from Y-doped ZnO thin films on p-Si substrates by sol-gel method

Science.gov (United States)

Sharma, Sanjeev K.; Singh, Satendra Pal; Kim, Deuk Young

2018-02-01

The heterojunction diode of yttrium-doped ZnO (YZO) thin films was fabricated on p-Si(100) substrates by sol-gel method. The post-annealing process was performed at 600 °C in vacuum for a short time (3 min) to prevent inter-diffusion of Zn, Y, and Si atoms. X-ray diffraction (XRD) pattern of as-grown and annealed (600 °C in vacuum) films showed the preferred orientation along the c-axis (002) regardless of dopant concentrations. The uniform surface microstructure and the absence of other metal/oxide peaks in XRD pattern confirmed the excellence of films. The increasing bandgap and carrier concentration of YZO thin films were interpreted by the BM shift, that is, the Fermi level moves towards the conduction band edge. The current-voltage characteristics of the heterojunction diode, In/n-ZnO/p-Si/Al, showed a rectification behavior. The turn-on voltage and ideality factor of n-ZnO/p-Si and n-YZO/p-Si were observed to be 3.47 V, 2.61 V, and 1.97, 1.89, respectively. Y-dopant in ZnO thin films provided more donor electrons caused the shifting of Fermi-energy level towards the conduction band and strengthen the interest for heterojunction diodes.

Thermal activation of nitrogen acceptors in ZnO thin films grown by MOCVD

Energy Technology Data Exchange (ETDEWEB)

Dangbegnon, J.K.; Talla, K.; Botha, J.R. [Department of Physics, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth (South Africa)

2010-06-15

Nitrogen doping in ZnO is inhibited by spontaneous formation of compensating defects. Perfect control of the nitrogen doping concentration is required, since a high concentration of nitrogen could induce the formation of donor defects involving nitrogen. In this work, the effect of post-growth annealing in oxygen ambient on ZnO thin films grown by Metalorganic Chemical Vapor Deposition, using NO as both oxidant and nitrogen dopant, is studied. After annealing at 700 C and above, low-temperature photoluminescence shows the appearance of a transition at {proportional_to}3.23 eV which is interpreted as pair emission involving a nitrogen acceptor. A second transition at {proportional_to}3.15 eV is also discussed. This work suggests annealing as a potential means for p-type doping using nitrogen (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Room temperature ferromagnetism in Cu doped ZnO

Science.gov (United States)

Ali, Nasir; Singh, Budhi; Khan, Zaheer Ahmed; Ghosh, Subhasis

2018-05-01

We report the room temperature ferromagnetism in 2% Cu doped ZnO films grown by RF magnetron sputtering in different argon and oxygen partial pressure. X-ray photoelectron spectroscopy was used to ascertain the oxidation states of Cu in ZnO. The presence of defects within Cu-doped ZnO films can be revealed by electron paramagnetic resonance. It has been observed that saturated magnetic moment increase as we increase the zinc vacancies during deposition.

Synthesis and characterization of three-dimensional transition metal ions doped zinc oxide based dilute magnetic semiconductor thin films

Science.gov (United States)

Samanta, Kousik

Dilute magnetic semiconductors (DMS), especially 3d-transition metal (TM) doped ZnO based DMS materials are the most promising candidates for optoelectronics and spintronics applications; e.g. in spin light emitting diode (SLED), spin transistors, and spin field effect transistors (SFET), etc. In the present dissertation, thin films of Zn1-xTMxO (TM = Co2+, Cu2+, and Mn2+) were grown on (0001) oriented Al2O3 substrates by pulsed laser deposition (PLD) technique. The films were highly c-axis oriented, nearly single crystalline, and defects free for a limited concentration of the dilution of transition metal ions. In particular, we have obtained single crystalline phases of Zn1-xTMxO thin films for up to 10, 3, and 5 stoichiometric percentages of Co2+, Cu2+, and Mn2+ respectively. Raman micro-probe system was used to understand the structural and lattice dynamical properties at different physical conditions. The confinement of optical phonons in the disorder lattice was explained by alloy potential fluctuation (APF) using a spatial correlation (SC) model. The detailed analysis of the optical phonon behavior in disorder lattice confirmed the substitution of the transition metal ions in Zn 2+ site of the ZnO host lattice. The secondary phases of ZnCo 2O4, CuO, and ZnMn2O4 were detected in higher Co, Cu, and Mn doped ZnO thin films respectively; where as, XRD did not detect these secondary phases in the same samples. Room temperature ferromagnetism was observed in Co2+ and Cu2+ ions doped ZnO thin films with maximum saturation magnetization (Ms) of 1.0 and 0.76 muB respectively. The origin of the observed ferromagnetism in Zn1-xCoxO thin films was tested by the controlled introduction of shallow donors (Al) in Zn0.9-x Co0.1O:Alx (x = 0.005 and 0.01) thin films. The saturation magnetization for the 10% Co-doped ZnO (1.0 muB /Co) at 300K reduced (˜0.25 muB/Co) due to Al doping. The observed ferromagnetism and the reduction due to Al doping can be explained by the Bound

Photoluminescence quenching and enhanced spin relaxation in Fe doped ZnO nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Ovhal, Manoj M.; Santhosh Kumar, A. [Department of Materials Engineering, Defence Institute of Advanced Technology, Girinagar, Pune 411025 (India); Khullar, Prerna [School of Materials Science and Technology, Indian Institute of Technology (Banaras Hindu University), Varanasi 221005 (India); Kumar, Manjeet [Department of Materials Engineering, Defence Institute of Advanced Technology, Girinagar, Pune 411025 (India); Abhyankar, A.C., E-mail: ashutoshabhyankar@gmail.com [Department of Materials Engineering, Defence Institute of Advanced Technology, Girinagar, Pune 411025 (India)

2017-07-01

Cost-effective ultrasonically assisted precipitation method is utilized to synthesize Zinc oxide (ZnO) nanoparticles (NPs) at room temperature and the effect of Iron (Fe) doping on structural, optical and spin relaxation properties also presented. As-synthesized pure and Fe doped ZnO NPs possess a perfect hexagonal growth habit of wurtzite zinc oxide, along the (101) direction of preference. With Fe doping, ‘c/a’ ratio and compressive lattice strain in ZnO NPs are found to reduce and increase, respectively. Raman studies demonstrate that the E{sub 1} longitudinal optical (LO) vibrational mode is very weak in pure which remarkably enhanced with Fe doping into ZnO NPs. The direct band gap energy (E{sub g}) of the ZnO NPs has been increased from 3.02 eV to 3.11 eV with Fe doping. A slight red-shift observed with strong green emission band, in photoluminescence spectra, is strongly quenched in 6 wt.% Fe doped ZnO NPs. The field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM) reveals spherical shape of ZnO NPs with 60–70 nm, which reduces substantially on Fe doping. The energy dispersive X-ray spectrum and elemental mapping confirms the homogeneous distribution of Fe in ZnO NPs. Moreover, the specific relaxation rate (R{sub 2sp} = 1/T{sub 2}) has been measured using Carr-Purcell-Meiboom-Gill (CPMG) method and found to be maximum in 6 wt.% Fe doped ZnO NPs. Further, the correlation of structural, optical and dynamic properties is proposed. - Highlights: • Pure ZnO and Fe doped ZnO NPs were successfully prepared by cost effective ultrasonically assisted precipitation method. • The optical band gap of ZnO has been enhanced form 3.02–3.11 eV with Fe doping. • PL quenching behaviour has been observed with Fe{sup 3+} ions substitution in ZnO lattice. • Specific relaxation rate (R{sub 2sp} = 1/T{sub 2}) has been varied with Fe doping and found to be maximum in 6 wt.% Fe doped ZnO NPs.

Enhanced Doping Efficiency of Al-Doped ZnO by Atomic Layer Deposition Using Dimethylaluminum Isopropoxide as an Alternative Aluminum Precursor

NARCIS (Netherlands)

Wu, Y.; Potts, S.E.; Hermkens, P.M.; Knoops, H.C.M.; Roozeboom, F.; Kessels, W.M.M.

2013-01-01

Atomic layer deposition offers the unique opportunity to control, at the atomic level, the 3D distribution of dopants in highly uniform and conformal thin films. Here, it is demonstrated that the maximum doping efficiency of Al in ZnO can be improved from ∼10% to almost 60% using dimethylaluminum

Preparation and characterization of Ce-doped ZnO nanofibers by an electrospinning method

Directory of Open Access Journals (Sweden)

Jong-Pil Kim

2011-02-01

Full Text Available ZnO and Ce-doped ZnO Nanofibers on (111 Pt/SiO2/Si substrates were produced using an electrospinning technique. The as-prepared composite fibres were subjected to high-temperature calcination to produce inorganic fibers. After calcining at a temperature of 500 °C, the average diameter of the ZnO and Ce-doped ZnO nanofibers were determined to be 170 nm and 225 nm, respectively. The average grain size of the ZnO and Ce-doped ZnO nanofibers were about 50 nm and 57 nm, respectively. The microstructure, chemical bonding state and photoluminescence of the produced ZnO and Ce-doped ZnO nanofibers were investigated. The Ce-doped ZnO nanofiber can be assigned to the presence of Ce ions on substitutional sites of Zn ions and the Ce3+ state from X-ray photoelectron spectra. Compared with PL spectra of ZnO nanofibers, the peak position of the UV emission of the Ce-doped ZnO nanofibers is sharply suppressed while the green emission band is highly enhanced.

Synthesis, characterization and electrochemical behavior of Sb-doped ZnO microsphere film

Energy Technology Data Exchange (ETDEWEB)

Li, Qian [Department of Materials Science and Engineering, State Key Laboratory of Silicon Materials, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou, 310027 (China); Cheng, Kui, E-mail: chengkui@zju.edu.cn [Department of Materials Science and Engineering, State Key Laboratory of Silicon Materials, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou, 310027 (China); Weng, Wenjian, E-mail: wengwj@zju.edu.cn [Department of Materials Science and Engineering, State Key Laboratory of Silicon Materials, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou, 310027 (China); The Shanghai Institute of Ceramics, Chinese Academy of Sciences, 1295 Dingxi Road, Shanghai, 200050 (China); Du, Piyi; Han, Gaorong [Department of Materials Science and Engineering, State Key Laboratory of Silicon Materials, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou, 310027 (China)

2013-10-01

Sb-doped ZnO microsphere film was fabricated by a carboxylate ion assisted hydrothermal route coupled with a post-calcination process. The structure, chemical composition and optical band gap of the Sb-doped ZnO microsphere film were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, inductively couple plasma optical emission spectroscopy and UV–visible spectrophotometry, and compared with the un-doped ZnO microsphere film. The results suggest that the formation of zinc–antimony tartrate complex species during hydrothermal growth is the key to realize Sb-doped ZnO microstructures, and the present hydrothermal method with post-calcination is an effective way to dope Sb into ZnO. Furthermore, the Sb-doped ZnO microsphere film based electrochemical biosensor exhibits a good sensing performance for the detection of hydrogen peroxide, with a sensitivity of 271 μA mM{sup −1} cm{sup −2} which is more than three times higher than that of the un-doped ZnO biosensor. - Highlights: • Sb-doped ZnO microsphere (SZM) films were grown by hydrothermal deposition. • Carboxylate ions were used to form complex during hydrothermal growth. • The formation of Zn–Sb tartrate complex is the key to realize SZM. • The biosensors based on SZM film are feasible and sensitive to detect H{sub 2}O{sub 2}. • The Sb doping could improve the electrochemical property of ZnO.

Explanation of ferromagnetism origin in C-doped ZnO by first principle calculations

International Nuclear Information System (INIS)

El Amiri, A.; Lassri, H.; Hlil, E.K.; Abid, M.

2015-01-01

By ab-initio calculations, we systematically study possible source of ferromagnetism C-doped ZnO compound. The electronic structure and magnetic properties of C-doped ZnO with / without ZnO host and C defects were investigated using the Korringa–Kohn–Rostoker (KKR) method combined with coherent potential approximation (CPA). We show that Zn vacancy and presence of C defects (substitutional, interstitial or combination of both) induce the ferromagnetism in C-doped ZnO. From density of state (DOS) analysis, we show that p–p interaction between C atoms and/or C and O atoms is the mechanism of ferromagnetic coupling in C-doped ZnO. - Highlights: • We study the effect of ZnO host and C defects on ferromagnetism in C-doped ZnO. • Details of KKR method calculations performed to investigate both magnetic and electronic structures. • Magnetic moments, total and partial DOS for C-doped ZnO are well calculated and discussed. • Based on DOS calculations we interpret a origin of ferromagnetism in C-doped ZnO. • Mechanism of ferromagnetic coupling is well proposed

Explanation of ferromagnetism origin in C-doped ZnO by first principle calculations

Energy Technology Data Exchange (ETDEWEB)

El Amiri, A., E-mail: aelamiri@casablanca.ma [Laboratoire de Physique Fondamentale et Appliquée (LPFA), Faculté des Sciences Ain Chock, Université Hassan II, B.P. 5366 Mâarif, Casablanca, Maroc (Morocco); Lassri, H. [Laboratoire de Physique des Matériaux, Micro-électronique, Automatique et Thermique (LPMMAT). Faculté des Sciences Ain Chock, Université Hassan II, B.P. 5366 Mâarif, Casablanca, Maroc (Morocco); Hlil, E.K. [Institut Néel, CNRS et Université Joseph Fourier, BP 166, 38042 Grenoble (France); Abid, M. [Laboratoire de Physique Fondamentale et Appliquée (LPFA), Faculté des Sciences Ain Chock, Université Hassan II, B.P. 5366 Mâarif, Casablanca, Maroc (Morocco)

2015-01-15

By ab-initio calculations, we systematically study possible source of ferromagnetism C-doped ZnO compound. The electronic structure and magnetic properties of C-doped ZnO with / without ZnO host and C defects were investigated using the Korringa–Kohn–Rostoker (KKR) method combined with coherent potential approximation (CPA). We show that Zn vacancy and presence of C defects (substitutional, interstitial or combination of both) induce the ferromagnetism in C-doped ZnO. From density of state (DOS) analysis, we show that p–p interaction between C atoms and/or C and O atoms is the mechanism of ferromagnetic coupling in C-doped ZnO. - Highlights: • We study the effect of ZnO host and C defects on ferromagnetism in C-doped ZnO. • Details of KKR method calculations performed to investigate both magnetic and electronic structures. • Magnetic moments, total and partial DOS for C-doped ZnO are well calculated and discussed. • Based on DOS calculations we interpret a origin of ferromagnetism in C-doped ZnO. • Mechanism of ferromagnetic coupling is well proposed.

Synthesis and characterization of ZnO and Ni doped ZnO nanorods by thermal decomposition method for spintronics application

International Nuclear Information System (INIS)

Saravanan, R.; Santhi, Kalavathy; Sivakumar, N.; Narayanan, V.; Stephen, A.

2012-01-01

Zinc oxide nanorods and diluted magnetic semiconducting Ni doped ZnO nanorods were prepared by thermal decomposition method. This method is simple and cost effective. The decomposition temperature of acetate and formation of oxide were determined by TGA before the actual synthesis process. The X-ray diffraction result indicates the single phase hexagonal structure of zinc oxide. The transmission electron microscopy and scanning electron microscopy images show rod like structure of ZnO and Ni doped ZnO samples with the diameter ∼ 35 nm and the length in few micrometers. The surface analysis was performed using X-ray photoelectron spectroscopic studies. The Ni doped ZnO exhibits room temperature ferromagnetism. This diluted magnetic semiconducting Ni doped ZnO nanorods finds its application in spintronics. - Highlights: ► The method used is very simple and cost effective compared to all other methods for the preparation DMS materials. ► ZnO and Ni doped ZnO nanorods ► Ferromagnetism at room temperature

Fabrication of nanostructured Al-doped ZnO thin film for methane sensing applications

Energy Technology Data Exchange (ETDEWEB)

Shafura, A. K., E-mail: shafura@ymail.com; Azhar, N. E. I.; Uzer, M.; Mamat, M. H. [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA, 40450 Shah Alam, Selangor (Malaysia); Sin, N. D. Md. [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA, 40450 Shah Alam, Selangor (Malaysia); Faculty of Electrical Engineering, Universiti Teknologi MARA Cawangan Johor, Kampus Pasir Gudang, 81750 Masai, Johor (Malaysia); Saurdi, I. [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA, 40450 Shah Alam, Selangor (Malaysia); Faculty of Electrical Engineering, Universiti Teknologi MARA Sarawak, Kampus Kota Samarahan Jalan Meranek, Sarawak (Malaysia); Shuhaimi, A. [Dimensional Materials Research Centre (LDMRC), Department of Physics, Faculty of Science, University ofMalaya, 50603 Kuala Lumpur (Malaysia); Alrokayan, Salman A. H.; Khan, Haseeb A. [Research Chair of Targeting and Treatment Cancer Using Nanoparticles, Department Of Biochemistry, College Of Science, King Saud University, P.O: 2454 Riyadh 11451 (Saudi Arabia); Rusop, M., E-mail: nanouitm@gmail.com [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA, 40450 Shah Alam, Selangor (Malaysia); NANO-SciTech Centre (NST), Institute of Science, Universiti Teknologi MARA, 40450 Shah Alam, Selangor (Malaysia)

2016-07-06

CH{sub 4} gas sensor was fabricated using spin-coating method of the nanostructured ZnO thin film. Effect of annealing temperature on the electrical and structural properties of the film was investigated. Dense nanostructured ZnO film are obtained at higher annealing temperature. The optimal condition of annealing temperature is 500°C which has conductivity and sensitivity value of 3.3 × 10{sup −3} S/cm and 11.5%, respectively.

A review of the growth, doping, and applications of β-Ga2O3 thin films

Science.gov (United States)

Razeghi, Manijeh; Park, Ji-Hyeon; McClintock, Ryan; Pavlidis, Dimitris; Teherani, Ferechteh H.; Rogers, David J.; Magill, Brenden A.; Khodaparast, Giti A.; Xu, Yaobin; Wu, Jinsong; Dravid, Vinayak P.

2018-03-01

β-Ga2O3 is emerging as an interesting wide band gap semiconductor for solar blind photo detectors (SBPD) and high power field effect transistors (FET) because of its outstanding material properties including an extremely wide bandgap (Eg 4.9eV) and a high breakdown field (8 MV/cm). This review summarizes recent trends and progress in the growth/doping of β-Ga2O3 thin films and then offers an overview of the state-of-the-art in SBPD and FET devices. The present challenges for β-Ga2O3 devices to penetrate the market in real-world applications are also considered, along with paths for future work.

Nucleation, Growth Mechanism, and Controlled Coating of ZnO ALD onto Vertically Aligned N-Doped CNTs.

Science.gov (United States)

Silva, R M; Ferro, M C; Araujo, J R; Achete, C A; Clavel, G; Silva, R F; Pinna, N

2016-07-19

Zinc oxide thin films were deposited on vertically aligned nitrogen-doped carbon nanotubes (N-CNTs) by atomic layer deposition (ALD) from diethylzinc and water. The study demonstrates that doping CNTs with nitrogen is an effective approach for the "activation" of the CNTs surface for the ALD of metal oxides. Conformal ZnO coatings are already obtained after 50 ALD cycles, whereas at lower ALD cycles an island growth mode is observed. Moreover, the process allows for a uniform growth from the top to the bottom of the vertically aligned N-CNT arrays. X-ray photoelectron spectroscopy demonstrates that ZnO nucleation takes place at the N-containing species on the surface of the CNTs by the formation of the Zn-N bonds at the interface between the CNTs and the ZnO film.

Characterization of n and p-type ZnO thin films grown by pulsed filtered cathodic vacuum arc system

International Nuclear Information System (INIS)

Kavak, H.; Erdogan, E.N.; Ozsahin, I.; Esen, R.

2010-01-01

Full text : Semiconductor ZnO thin films with wide band gap attract much interest due to their properties such as chemical stability in hydrogen plasma, high optical transparency in the visible and nearinfrared region. Due to these properties ZnO oxide is a promising materials for electronic or optoelectronic applications such as solar cell (as an antireflecting coating and a transparent conducting material), gas sensors, surface acoustic wave devices. The purpose of this research is to improve the properties of n and p-type ZnO thin films for device applications. Polycrystalline ZnO is naturally n-type and very difficult to dope to make p-type. Therefore nowadays hardly produced p-type ZnO attracts a lot of attention. Nitrogen considered as the best dopant for p-type ZnO thin films.The transparent, conductive and very precise thickness controlled n and p-type semiconducting nanocrystalline ZnO thin films were prepared by pulsed filtered cathodic vacuum arc deposition (PFCVAD) method. Structural, optical and electrical properties of these films were investigated. And also photoluminescence properties of these films were investigated. Transparent p-type ZnO thin films were produced by oxidation of PFCVAD deposited zinc nitride. Zinc nitride thin films were deposited with various thicknesses and under different oxygen pressures on glass substrates. Zinc nitride thin films, which were deposited at room temperatures, were amorphous and the optical transmission was below 70%. For oxidation zinc nitride, the sample was annealed in air starting from 350 degrees Celsium up to 550 degrees Celsium for one hour duration. These XRD patterns imply that zinc nitride thin films converted to zinc oxide thin films with the same hexagonal crystalline structures of ZnO. The optical measurements were made for each annealing temperature and the optical transmissions of ZnO thin films were found better than 90 percent in visible range after annealing over 350 degrees Celsium. By

A highly selective and wide range ammonia sensor—Nanostructured ZnO:Co thin film

International Nuclear Information System (INIS)

Mani, Ganesh Kumar; Rayappan, John Bosco Balaguru

2015-01-01

Graphical abstract: - Highlights: • Cobalt doped nanostructured ZnO thin films were spray deposited on glass substrates. • Co-doped ZnO film was highly selective towards ammonia than ethanol, methanol, etc. • The range of ammonia detection was improved significantly by doping cobalt in ZnO. - Abstract: Ammonia sensing characteristics of undoped and cobalt (Co)-doped nanostructured ZnO thin films were investigated. Polycrystalline nature with hexagonal wurtzite structure and high crystalline quality with dominant (0 0 2) plane orientation of Co-doped ZnO film were confirmed by the X-ray diffractogram. Scanning electron micrographs of the undoped film demonstrated the uniform deposition of sphere-shaped grains. But, smaller particles with no clear grain boundaries were observed for Co-doped ZnO thin film. Band gap values were found to be 3.26 eV and 3.22 eV for undoped and Co-doped ZnO thin films. Ammonia sensing characteristics of Co-doped ZnO film at room temperature were investigated in the concentration range of 15–1000 ppm. Variation in the sensing performances of Co-doped and pure ZnO thin films has been analyzed and compared

Atomic layer deposition of B-doped ZnO using triisopropyl borate as the boron precursor and comparison with Al-doped ZnO

NARCIS (Netherlands)

Garcia - Alonso, D.; Potts, S.E.; Helvoirt, van C.A.A.; Verheijen, M.A.; Kessels, W.M.M.

2015-01-01

Doped ZnO films are an important class of transparent conductive oxides, with many applications demanding increased growth control and low deposition temperatures. Therefore, the preparation of B-doped ZnO films by atomic layer deposition (ALD) at 150 °C was studied. The B source was triisopropyl

Recent progress on doped ZnO nanostructures for visible-light photocatalysis

International Nuclear Information System (INIS)

Samadi, Morasae; Zirak, Mohammad; Naseri, Amene; Khorashadizade, Elham; Moshfegh, Alireza Z.

2016-01-01

Global environmental pollution and energy supply demand have been regarded as important concerns in recent years. Metal oxide semiconductor photocatalysts is a promising approach to apply environmental remediation as well as fuel generation from water splitting and carbon dioxide reduction. ZnO nanostructures have been shown promising photocatalytic activities due to their non-toxic, inexpensive, and highly efficient nature. However, its wide band gap hinders photo-excitation for practical photocatalytic applications under solar light as an abundant, clean and safe energy source. To overcome this barrier, many strategies have been developed in the last decade to apply ZnO nanostructured photocatalysts under visible light. In this review, we have classified different approaches to activate ZnO as a photocatalyst in visible-light spectrum. Utilization of various nonmetals, transition metals and rare-earth metals for doping in ZnO crystal lattice to create visible-light-responsive doped ZnO photocatalysts is discussed. Generation of localized energy levels within the gap in doped ZnO nanostructures has played an important role in effective photocatalytic reaction under visible-light irradiation. The effect of dopant type, ionic size and its concentration on the crystal structure, electronic property and morphology of doped ZnO with a narrower band gap is reviewed systematically. Finally, a comparative study is performed to evaluate two classes of metals and nonmetals as useful dopants for ZnO nanostructured photocatalysts under visible light. - Highlights: • Metals and nonmetals used as a dopant to shift ZnO band gap toward visible-light. • Modification of electronic structure played a crucial role in doped ZnO activity. • Correlation between dopant's characteristics and ZnO visible activity was reviewed. • Photo-degradation of doped ZnO was studied and compared for different dopants.

Recent progress on doped ZnO nanostructures for visible-light photocatalysis

Energy Technology Data Exchange (ETDEWEB)

Samadi, Morasae; Zirak, Mohammad [Department of Physics, Sharif University of Technology, P.O. Box 11555-9161, Tehran (Iran, Islamic Republic of); Naseri, Amene [Institute for Nanoscience and Nanotechnology, Sharif University of Technology, P.O. Box 11365-8639, Tehran (Iran, Islamic Republic of); Khorashadizade, Elham [Department of Physics, Sharif University of Technology, P.O. Box 11555-9161, Tehran (Iran, Islamic Republic of); Moshfegh, Alireza Z., E-mail: moshfegh@sharif.edu [Department of Physics, Sharif University of Technology, P.O. Box 11555-9161, Tehran (Iran, Islamic Republic of); Institute for Nanoscience and Nanotechnology, Sharif University of Technology, P.O. Box 11365-8639, Tehran (Iran, Islamic Republic of)

2016-04-30

Global environmental pollution and energy supply demand have been regarded as important concerns in recent years. Metal oxide semiconductor photocatalysts is a promising approach to apply environmental remediation as well as fuel generation from water splitting and carbon dioxide reduction. ZnO nanostructures have been shown promising photocatalytic activities due to their non-toxic, inexpensive, and highly efficient nature. However, its wide band gap hinders photo-excitation for practical photocatalytic applications under solar light as an abundant, clean and safe energy source. To overcome this barrier, many strategies have been developed in the last decade to apply ZnO nanostructured photocatalysts under visible light. In this review, we have classified different approaches to activate ZnO as a photocatalyst in visible-light spectrum. Utilization of various nonmetals, transition metals and rare-earth metals for doping in ZnO crystal lattice to create visible-light-responsive doped ZnO photocatalysts is discussed. Generation of localized energy levels within the gap in doped ZnO nanostructures has played an important role in effective photocatalytic reaction under visible-light irradiation. The effect of dopant type, ionic size and its concentration on the crystal structure, electronic property and morphology of doped ZnO with a narrower band gap is reviewed systematically. Finally, a comparative study is performed to evaluate two classes of metals and nonmetals as useful dopants for ZnO nanostructured photocatalysts under visible light. - Highlights: • Metals and nonmetals used as a dopant to shift ZnO band gap toward visible-light. • Modification of electronic structure played a crucial role in doped ZnO activity. • Correlation between dopant's characteristics and ZnO visible activity was reviewed. • Photo-degradation of doped ZnO was studied and compared for different dopants.

Enhancing the electron transfer and band potential tuning with long-term stability of ZnO based dye-sensitized solar cells by gallium and tellurium as dual-doping

International Nuclear Information System (INIS)

Akin, Seckin; Erol, Erdinc; Sonmezoglu, Savas

2017-01-01

A series of ZnO nanoparticles with Ga and Te dual-doping were successfully synthesized by using a facile sol–gel route, and their performance as the photoanode material in DSSCs was employed for the first time. The effects of simultaneously Ga–Te dopants into ZnO host (Ga x Te 1-x ZnO where the values of x ranging from 0 to 1 mol % with increments of 0.25 mol %) on the structural, optical, morphological, and compositional properties of the resulting samples were characterized via XRD, Raman, UV–vis–NIR spectrometer, PL, BET, AFM, FE–SEM, EDX, and XPS measurements. The incorporation of Ga–Te enlarges the surface area of the photoanodes, leading to higher dye-loading capability. Moreover, the PL intensity of pure ZnO drastically decreases by Ga–Te dopants, which demonstrates the reduction of oxygen vacancies, indicating the slow recombination of photoinduced charge carriers. Owing to the doping effect of Ga–Te, the energy conversion efficiencies of the DSSCs based on these photoanodes lie in the range of 4.79–7.08%, which is higher than that of pure ZnO (3.53%). This improvement of efficiency can be mainly ascribed to the combined effects of faster electron transport rate, retarded charge recombination, enhanced dye adsorption capability, longer electron lifetime as well as shifted negatively of conduction band edge in dual-doped ZnO films. Furthermore, it is noteworthy that after 1200 h, the degraded Ga 0.25 Te 0.75 ZnO device still shows 86% of their initial efficiency. This study provides a strategy for constructing self-powered systems using a device such as Ga x Te 1-x ZnO based DSSC described here for the first time.

Temperature dependent thermoelectric properties of chemically derived gallium zinc oxide thin films

KAUST Repository

Barasheed, Abeer Z.; Sarath Kumar, S. R.; Alshareef, Husam N.

2013-01-01

In this study, the temperature dependent thermoelectric properties of sol-gel prepared ZnO and 3% Ga-doped ZnO (GZO) thin films have been explored. The power factor of GZO films, as compared to ZnO, is improved by nearly 17% at high temperature. A stabilization anneal, prior to thermoelectric measurements, in a strongly reducing Ar/H2 (95/5) atmosphere at 500°C was found to effectively stabilize the chemically derived films, practically eliminating hysteresis during thermoelectric measurements. Subtle changes in the thermoelectric properties of stabilized films have been correlated to oxygen vacancies and excitonic levels that are known to exist in ZnO-based thin films. The role of Ga dopants and defects, formed upon annealing, in driving the observed complex temperature dependence of the thermoelectric properties is discussed. © The Royal Society of Chemistry 2013.

Enhanced Light Scattering by Preferred Orientation Control of Ga Doped ZnO Films Prepared through MOCVD

Directory of Open Access Journals (Sweden)

Long Giang Bach

2016-01-01

Full Text Available We have explored the effective approach to fabricate GZO/ZnO films that can make the pyramidal surface structures of GZO films for effective light scattering by employing a low temperature ZnO buffer layer prior to high temperature GZO film growth. The GZO thin films exhibit the typical preferred growth orientations along the (002 crystallographic direction at deposition temperature of 400°C and SEM showed that column-like granule structure with planar surface was formed. In contrast, GZO films with a pyramidal texture surface were successfully developed by the control of (110 preferred orientation. We found that the light diffuse transmittance of the film with a GZO (800 nm/ZnO (766 nm exhibited 13% increase at 420 nm wavelength due to the formed large grain size of the pyramidal texture surface. Thus, the obtained GZO films deposited over ZnO buffer layer have high potential for use as front TCO layers in Si-based thin film solar cells. These results could develop the potential way to fabricate TCO based ZnO thin film using MOCVD or sputtering techniques by depositing a low temperature ZnO layer to serve as a template for high temperature GZO film growth. The GZO films exhibited satisfactory optoelectric properties.

Optical and structural properties of individual Co-doped ZnO microwires

Science.gov (United States)

Kolomys, O. F.; Strelchuk, V. V.; Rarata, S. V.; Hayn, R.; Savoyant, A.; Giovannelli, F.; Delorme, F.; Tkach, V.

2018-06-01

The Co-doped ZnO microwires (MWs) were grown using the optical furnace method. We used Scanning electron microscopy (SEM), polarized micro-Raman spectroscopy, photoluminescence (PL) and optical absorption spectroscopy to systematic investigation of the optical and structural properties of Co-doped ZnO MWs. The SEM analysis reveals that Co-doped ZnO MWs has hexagonal facets and cavity inside. The EDS results confirmed the presence and non-uniform distribution of Co impurities in the samples. Co doping of ZnO MWs leads to the decreased intensity, drastically broadening and high-energy shift of the NBE PL band. The red emission band at 1.85 eV originates from 2E(2G) → 4A2 (4F) intra-3d-transition of Co2+ in the ZnO lattice has been observed. The intense structured absorption bands within the near infrared ranges 3800-4800 and 5500-9000 cm-1 are caused by electronic spin-allowed transitions 4T2(F) ← 4A2(F) and 4T1(F) ← 4A2(F) of the tetrahedrally coordinated Co2+ (3 d7) ions substituting Zn2+ ions in Co-doped ZnO MWs. Micro-Raman studies of Co doped ZnO MWs show doping/disorder induced additional modes as compared to the undoped sample. The resonant enhancement of the additional local Co-related A1-symmetry Raman mode is observed in the parallel polarization geometry y(z , z) ybar . For the Co doped ZnO MWs, the enhancement of the additional Co-related local vibration mode with an increase in the excitation photon energy is also observed in the Raman spectra.

Hydrogen absorption in thin ZnO films prepared by pulsed laser deposition

Czech Academy of Sciences Publication Activity Database

Melikhova, O.; Čížek, J.; Lukáč, F.; Vlček, M.; Novotný, Michal; Bulíř, Jiří; Lančok, Ján; Anwand, W.; Brauer, G.; Connolly, J.; McCarthy, E.; Krishnamurthy, S.; Mosnier, J.-P.

2013-01-01

Roč. 580, suppl. 1 (2013), S40-S43 ISSN 0925-8388 R&D Projects: GA ČR(CZ) GAP108/11/0958 Institutional support: RVO:68378271 Keywords : defects * hydrogen * positron annihilation * thin films * ZnO Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.726, year: 2013

Effect of hydrogen doping on the properties of Al and F co-doped ZnO films for thin film silicon solar cell applications

Energy Technology Data Exchange (ETDEWEB)

Wang, Fang-Hsing, E-mail: fansen@dragon.nchu.edu.tw; Yang, Tung-Hsin

2016-04-30

Aluminum and fluorine co-doped zinc oxide (AFZO) thin films were prepared in Ar + H{sub 2} atmospheres by rf magnetron sputtering at room temperature. The structural, electrical, and optical properties of the prepared films were investigated using X-ray diffraction, scanning electron microscopy, atomic force microscopy, Hall-effect measurement, X-ray photoelectron spectroscopy, and ultraviolet–visible spectrometry, and their dependence on deposition atmosphere (i.e. H{sub 2} / (H{sub 2} + Ar) ratio) was studied. The resulting films showed a (0 0 2) diffraction peak, indicating a typical wurtzite structure, and the optimal film crystallinity was obtained with the H{sub 2} / (H{sub 2} + Ar) ratio of 3%. The electrical resistivity of AFZO films decreased to 9.16 × 10{sup −4} Ω-cm, which was lower than ZnO:Al and ZnO:F films due to double doping effect of Al and F. The resistivity further decreased to below 5 × 10{sup −4} Ω-cm for the AFZO film with the H{sub 2} / (H{sub 2} + Ar) ratio of 3%–5%. All the films regardless of hydrogen content displayed high transmittances (> 92%) in the visible wavelength range. Applying the developed AFZO films as front transparent electrodes, amorphous Si thin film solar cells were fabricated and the open-circuit voltage, fill factor, and efficiency of the cell with the hydrogenated AFZO film were improved in contrast to those without the hydrogenated film. - Highlights: • H{sub 2} doping improves optoelectronic properties of Al, F co-doped ZnO (AFZO) films. • Resistivity of AFZO films decreases to 4.4 × 10{sup −4} Ω-cm with the 3% H{sub 2}/(Ar + H{sub 2}) ratio. • AFZO films show high average visible transmittances of above 92%. • Efficiency of a-Si thin film solar cells is improved by AFZO:H as front electrode.

Ultraviolet electroluminescence from nitrogen-doped ZnO-based heterojuntion light-emitting diodes prepared by remote plasma in situ atomic layer-doping technique.

Science.gov (United States)

Chien, Jui-Fen; Liao, Hua-Yang; Yu, Sheng-Fu; Lin, Ray-Ming; Shiojiri, Makoto; Shyue, Jing-Jong; Chen, Miin-Jang

2013-01-23

Remote plasma in situ atomic layer doping technique was applied to prepare an n-type nitrogen-doped ZnO (n-ZnO:N) layer upon p-type magnesium-doped GaN (p-GaN:Mg) to fabricate the n-ZnO:N/p-GaN:Mg heterojuntion light-emitting diodes. The room-temperature electroluminescence exhibits a dominant ultraviolet peak at λ ≈ 370 nm from ZnO band-edge emission and suppressed luminescence from GaN, as a result of the decrease in electron concentration in ZnO and reduced electron injection from n-ZnO:N to p-GaN:Mg because of the nitrogen incorporation. The result indicates that the in situ atomic layer doping technique is an effective approach to tailoring the electrical properties of materials in device applications.

Effects of Post- Heat Treatment of Nanocrystalline ZnO Thin Films deposited on Zn-Deposited FTO Substrates

Energy Technology Data Exchange (ETDEWEB)

Kim, Ikhyun; Kim, Younggyu; Nam, Giwoong; Leem, Jae-Young [Inje University, Gimhae (Korea, Republic of)

2015-10-15

The effects of heat-treatment temperature on the structural and optical properties of ZnO thin films were investigated with field-effect scanning electron microscopy (SEM), X-ray diffraction analysis, and photoluminescence (PL) measurements. The ZnO thin films were grown on Zn-deposited fluorine-doped tin oxide substrates by sol-gel spin coating. The SEM images of the samples showed that their surfaces had a mountain-chain-like structure. The film annealed at 400 ℃ had the highest degree of alignment along the c-axis, and its residual stress was close to zero. The PL spectra of the ZnO thin films consisted of sharp near-band-edge emissions (NBE) and broad deep-level emissions (DLE) in the visible range. The DLE peaks exhibited a green-to-red shift with an increase in the temperature. The highest INBE/IDLE ratio was observed in the film annealed at 400 ℃. Thus, the optimal temperature for growing high-quality ZnO thin films on Zn-deposited FTO substrates is 400 ℃.

Synthesis and characterization of porous structured ZnO thin film for dye sensitized solar cell applications

Energy Technology Data Exchange (ETDEWEB)

Marimuthu, T.; Anandhan, N., E-mail: anandhan-kn@rediffmail.com; Mummoorthi, M. [School of Physics, Alagappa University, Karaikudi – 630 003 (India); Dharuman, V. [Department of Bioelectronics and Biosensors, Alagappa University, Karaikudi – 630 003 (India)

2016-05-23

Zinc oxide (ZnO) and zinc oxide/eosin yellow (ZnO/EY) thin films were potentiostatically deposited onto fluorine doped tin oxide (FTO) glass substrate. Effect of eosin yellow dye on structural, morphological and optical properties was studied. X-ray diffraction patterns, micro Raman spectra and photoluminescence (PL) spectra reveal hexagonal wurtzite structure with less atomic defects in 101 plane orientation of the ZnO/EY film. Scanning electron microscopy (SEM) images show flower for ZnO and porous like structure for ZnO/EY thin film, respectively. DSSC was constructed and evaluated by measuring the current density verses voltage curve.

Synthesis of Doped and non-Doped Nano MgO Ceramic Membranes

Directory of Open Access Journals (Sweden)

Shiraz Labib

2013-12-01

Full Text Available Doped and non-doped MgO coated thin films on alumina substrates were prepared using a chelating sol-gel method under controlled conditions to prepare nanomaterials with unprecedented properties. The effect of doping of ZnO on thermal, surface and structural properties was investigated using DTA-TG, BET and XRD respectively. Also microstructural studies and coating thickness measurements of MgO thin film were conducted using SEM. An increase in the thermal stability of MgO with increasing ZnO doping percent was observed. The increase of ZnO doping percent showed a marked decrease in the average particle size of MgO powder as a result of the replacement of some Mg2+ by Zn2+ which has similar ionic radius as Mg2+. This decrease in particle size of MgO was also related to the decrease of the degree of MgO crystalinity. The increase of ZnO doping also showed a marked decrease in coating thickness values of the prepared membranes. This decrease was related to the  mechanism of ZnO doping into a MgO crystal lattice.

Effects of a highly Si-doped GaN current spreading layer at the n+-GaN/multi-quantum-well interface on InGaN/GaN blue-light-emitting diodes

International Nuclear Information System (INIS)

Kim, C. S.; Cho, H. K.; Choi, R. J.; Hahn, Y. B.; Lee, H. J.; Hong, C. H.

2004-01-01

Highly Si-doped GaN thin current spreading layer (CSL) with various carrier concentrations were inserted before the n + -GaN/multi-quantum-well (MQW) interface controlled by the growth rate and the modulated Si-doping in InGaN/GaN blue light-emitting diodes (LEDs), and their effects were investigated by using capacitance-voltage (C-V), current-voltage (I-V), and output power measurements. The LEDs with a highly Si-doped CSL show enhanced I-V characteristics and increased output power with increasing carrier concentration up to some critical point in the CSL. This means that proper high Si-doping in some limited area before the interface may enhance the device performance through the current spreading effect.

Magnetic behavior of Co–Mn co-doped ZnO nanoparticles

International Nuclear Information System (INIS)

Li, Hengda; Liu, Xinzhong; Zheng, Zhigong

2014-01-01

Here, we report on systematic studies of the magnetic properties of Co and Mn co-doped ZnO nanoparticles prepared by a sol–gel technique. The effect of the concentration of the doping ions on the magnetic properties of Co and Mn co-doped ZnO nanoparticles is presented. X-ray diffraction characterizations (XRD) of co-doped ZnO nanoparticles are all wurtzite structure. The Zn 0.96 Co 0.02 Mn 0.02 O nanoparticles and Zn 0.94 Co 0.02 Mn 0.04 O nanoparticles display ferromagnetic behavior at room temperature. Superconducting quantum interference device (SQUID) magnetometer figures show that with the concentration of the Mn ions increased, the saturation magnetic moment (M s ) increased, and the magnetic is probably due to the co-doping of the Mn ions. Our results demonstrate that the Mn ions doping concentration play an important role in the ferromagnetic properties of Co–Mn co-doped ZnO nanoparticles at room temperature. - Highlights: • The effect of the doping ions on the magnetic properties is presented. • The magnetic is probably due to the co-doping of the Mn ions. • The Mn ions concentration play an important role in the ferromagnetic properties

A study of Eu incorporated ZnO thin films: An application of Al/ZnO:Eu/p-Si heterojunction diode

Energy Technology Data Exchange (ETDEWEB)

Turgut, G. [Department of Basic Sciences, Faculty of Science, Erzurum Technical University, Erzurum, 25240 (Turkey); Duman, S., E-mail: sduman@atauni.edu.tr [Department of Physics, Faculty of Science, Ataturk University, Erzurum, 25240 (Turkey); Sonmez, E. [Department of Physics, Faculty of K.K. Education, Ataturk University, Erzurum, 25240 (Turkey); Ozcelik, F.S. [Department of Physics, Faculty of Science, Ataturk University, Erzurum, 25240 (Turkey)

2016-04-15

Highlights: • Eu incorporated ZnO thin films were grown by sol–gel spin coating. • The influence of Eu contribution on features of ZnO was investigated. • Al/ZnO:Eu/p-Si heterojunction diodes were also fabricated. • The diode parameters were calculated from I–V measurements. - Abstract: In present work, the pure and europium (Eu) incorporated zinc oxide (ZnO) thin films were deposited with sol-gel spin coating by using zinc acetate dehydrate and Eu (III) chloride salts. The coated films were examined by means of XRD, AFM and UV/VIS spectrophotometer. The ZnO hexagonal wurtzite nanoparticles with (002) preferential direction were observed for all films. The values of crystallite size, micro-strain and surface roughness continuously increased from 21 nm, 1.10 × 10{sup −3} and 2.43 nm to the values of 35.56 nm, 1.98 × 10{sup −3} and 28.99 nm with Eu doping, respectively. The optical band gap value of the pure ZnO initially increased from 3.296 eV to 3.328 eV with Eu doping up to 2 at.% doping level, then it started to decrease with more Eu content. The electrical features of Al/n-ZnO:Eu/p-Si heterojunction diodes were inquired by current-voltage (I–V) measurements at the room temperature.

Y-Doped ZnO Nanorods by Hydrothermal Method and Their Acetone Gas Sensitivity

Directory of Open Access Journals (Sweden)

Peng Yu

2013-01-01

Full Text Available Pure and yttrium- (Y- doped (1 at%, 3 at%, and 7 at% ZnO nanorods were synthesized using a hydrothermal process. The crystallography and microstructure of the synthesized samples were characterized by X-ray diffraction (XRD, scanning electron microscopy (SEM, and energy dispersive X-ray spectroscopy (EDX. Comparing with pure ZnO nanorods, Y-doped ZnO exhibited improved acetone sensing properties. The response of 1 at% Y-doped ZnO nanorods to 100 ppm acetone is larger than that of pure ZnO nanorods. The response and recovery times of 1 at% Y-doped ZnO nanorods to 100 ppm acetone are about 30 s and 90 s, respectively. The gas sensor based on Y-doped ZnO nanorods showed good selectivity to acetone in the interfere gases of ammonia, benzene, formaldehyde, toluene, and methanol. The formation mechanism of the ZnO nanorods was briefly analyzed.

Morphological transition of ZnO nanostructures influenced by magnesium doping

International Nuclear Information System (INIS)

Premkumar, T.; Zhou, Y.S.; Gao, Y.; Baskar, K.; Jiang, L.; Lu, Y.F.

2012-01-01

Wurtzite zinc oxide (ZnO) nanochains have been synthesized through high-pressure pulsed laser deposition. The chain-like ZnO nanostructures were obtained from magnesium (Mg) doped ZnO targets, whereas vertically aligned nanorods were obtained from primitive ZnO targets. The Mg doping has influenced the morphological transition of ZnO nanostructures from nanorods to nanochains. The field emission scanning electron microscope images revealed the growth of beaded ZnO nanochains. The ZnO nanochains of different diameters 40 and 120 nm were obtained. The corresponding micro-Raman spectra showed strong E 2H mode of ZnO, which confirmed the good crystallinity of the nanochains. In addition to near band edge emission at 3.28 eV, ZnO nanochains show broad deep level emission at 2.42 eV than that of ZnO nanorods.

Comparative study about Al-doped zinc oxide thin films deposited by Pulsed Electron Deposition and Radio Frequency Magnetron Sputtering as Transparent Conductive Oxide for Cu(In,Ga)Se{sub 2}-based solar cells

Energy Technology Data Exchange (ETDEWEB)

Pattini, F., E-mail: pattini@imem.cnr.it [IMEM-CNR, Institute of Materials for Electronics and Magnetism, Parco Area delle Scienze 37/A, 43124 Parma (Italy); Annoni, F.; Bissoli, F.; Bronzoni, M. [IMEM-CNR, Institute of Materials for Electronics and Magnetism, Parco Area delle Scienze 37/A, 43124 Parma (Italy); Garcia, J.P. [Delft University of Technology, Faculty of Applied Sciences, Delft Product and Process Design Institute, Julianalaan 67, 2628 BC Delft (Netherlands); Gilioli, E.; Rampino, S. [IMEM-CNR, Institute of Materials for Electronics and Magnetism, Parco Area delle Scienze 37/A, 43124 Parma (Italy)

2015-05-01

In this study, a comparison between Al-doped ZnO (AZO) as Transparent Conductive Oxide for Cu(In,Ga)Se{sub 2}-based solar cells grown by Pulsed Electron Deposition (PED) and Radio Frequency Magnetron Sputtering (RFMS) was performed. PED yielded polycrystalline [002] mono-oriented thin films with low electrical resistivity and high optical transparency with heater temperatures ranging from room temperature (RT) to 250 °C. The electrical resistivity of these films can be tuned by varying the heater temperature, reaching a minimum value of 3.5 × 10{sup −4} Ωcm at 150 °C and an average transmittance over 90% in the visible range. An AZO film grown at RT was deposited by PED on an actual Cu(In,Ga)Se{sub 2}-based solar cell, resulting to an efficiency value of 15.2% on the best device. This result clearly shows that PED is a suitable technique for growing ZnO-based thin films for devices/applications where low deposition temperature is required. On the other hand, an optimized AZO thin film front contact for thin film solar cells was studied and fabricated via RFMS. The parameters of this technique were tweaked to obtain highly conductive and transparent AZO thin films. The lowest resistivity value of 3.7 × 10{sup −4} Ωcm and an average transmittance of 86% in the 400-1100 nm wavelength range was obtained with a heater temperature of 250 °C. A thick sputtered AZO film was deposited at RT onto an identical cell used for PED-grown AZO, reaching the highest conversion efficiency value of 14.7%. In both cases, neither antireflection coatings nor pure ZnO layer was used. - Highlights: • Pulsed Electron Deposition (PED) lets high quality films grow at low temperature. • Al:ZnO (AZO) thin films grown by PED present high optical and electrical quality. • AZO electrical resistivity can be tuned from 10{sup −4} to 10{sup −2} Ωcm in proper condition. • Cu(In,Ga)Se{sub 2}-based simplified solar cells achieved efficiency of 15.2% for PED-grown AZO.

Effect of cobalt doping on the mechanical properties of ZnO nanowires

Energy Technology Data Exchange (ETDEWEB)

Vahtrus, Mikk; Šutka, Andris [Institute of Physics, University of Tartu, W. Ostwaldi 1, 50412 Tartu (Estonia); Polyakov, Boris [Institute of Solid State Physics, University of Latvia, Kengaraga 8, LV-1063 Riga (Latvia); Oras, Sven; Antsov, Mikk [Institute of Physics, University of Tartu, W. Ostwaldi 1, 50412 Tartu (Estonia); Doebelin, Nicola [RMS Foundation, Bischmattstrasse 12, Bettlach 2544 (Switzerland); Institute of Geological Sciences, University of Bern, Baltzerstrasse 1–3, Bern 3012 (Switzerland); Lõhmus, Rünno; Nõmmiste, Ergo [Institute of Physics, University of Tartu, W. Ostwaldi 1, 50412 Tartu (Estonia); Vlassov, Sergei, E-mail: vlassovs@ut.ee [Institute of Physics, University of Tartu, W. Ostwaldi 1, 50412 Tartu (Estonia)

2016-11-15

In this work, we investigate the influence of doping on the mechanical properties of ZnO nanowires (NWs) by comparing the mechanical properties of pure and Co-doped ZnO NWs grown in similar conditions and having the same crystallographic orientation [0001]. The mechanical characterization included three-point bending tests made with atomic force microscopy and cantilever beam bending tests performed inside scanning electron microscopy. It was found that the Young's modulus of ZnO NWs containing 5% of Co was approximately a third lower than that of the pure ZnO NWs. Bending strength values were comparable for both materials and in both cases were close to theoretical strength indicating high quality of NWs. Dependence of mechanical properties on NW diameter was found for both doped and undoped ZnO NWs. - Highlights: •Effect of Co doping on the mechanical properties of ZnO nanowires is studied. •Co substitutes Zn atoms in ZnO crystal lattice. •Co addition affects crystal lattice parameters. •Co addition results in significantly decreased Young's modulus of ZnO. •Bending strength for doped and undoped wires is close to the theoretical strength.

GaN and ZnO nanostructures

Energy Technology Data Exchange (ETDEWEB)

Fuendling, Soenke; Soekmen, Uensal; Behrends, Arne; Al-Suleiman, Mohamed Aid Mansur; Merzsch, Stephan; Li, Shunfeng; Bakin, Andrey; Wehmann, Hergo-Heinrich; Waag, Andreas [Institut fuer Halbleitertechnik, Technische Universitaet Braunschweig, Braunschweig (Germany); Laehnemann, Jonas; Jahn, Uwe; Trampert, Achim; Riechert, Henning [Paul-Drude-Institut fuer Festkoerperelektronik, Berlin (Germany)

2010-10-15

GaN and ZnO are both wide band gap semiconductors with interesting properties concerning optoelectronic and sensor device applications. Due to the lack or the high costs of native substrates, alternatives like sapphire, silicon, or silicon carbide are taken, but the resulting lattice and thermal mismatches lead to increased defect densities which reduce the material quality. In contrast, nanostructures with high aspect ratio have lower defect densities as compared to layers. In this work, we give an overview on our results achieved on both ZnO as well as GaN based nanorods. ZnO nanostructures were grown by a wet chemical approach as well as by VPT on different substrates - even on flexible polymers. To compare the growth results we analyzed the structures by XRD and PL and show possible device applications. The GaN nano- and microstructures were grown by metal organic vapor phase epitaxy either in a self-organized process or by selective area growth for a better control of shape and material composition. Finally we take a look onto possible device applications, presenting our attempts, e.g., to build LEDs based on GaN nanostructures. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

Magnetoresistance of magnetically doped ZnO films

Energy Technology Data Exchange (ETDEWEB)

Behan, A J; Mokhtari, A; Blythe, H J; Fox, A M; Gehring, G A [Department of Physics and Astronomy, University of Sheffield, Sheffield S3 7RH (United Kingdom); Ziese, M, E-mail: G.A.Gehring@sheffield.ac.u [Division of Superconductivity and Magnetism, University of Leipzig, D-04103, Leipzig (Germany)

2009-08-26

Magnetoresistance measurements have been made at 5 K on doped ZnO thin films grown by pulsed laser deposition. ZnCoO, ZnCoAlO and ZnMnAlO samples have been investigated and compared to similar films containing no transition metal dopants. It is found that the Co-doped samples with a high carrier concentration have a small negative magnetoresistance, irrespective of their magnetic moment. On decreasing the carrier concentration, a positive contribution to the magnetoresistance appears and a further negative contribution. This second, negative contribution, which occurs at very low carrier densities, correlates with the onset of ferromagnetism due to bound magnetic polarons suggesting that the negative magnetoresistance results from the destruction of polarons by a magnetic field. An investigation of the anisotropic magnetoresistance showed that the orientation of the applied magnetic field, relative to the sample, had a large effect. The results for the ZnMnAlO samples showed less consistent trends.

VLS-grown diffusion doped ZnO nanowires and their luminescence properties

International Nuclear Information System (INIS)

Roy, Pushan Guha; Dutta, Amartya; Das, Arpita; Bhattacharyya, Anirban; Sen, Sayantani; Pramanik, Pallabi

2015-01-01

Zinc Oxide (ZnO) nanowires were deposited by vapor–liquid–solid (VLS) method on to aluminum doped ZnO (AZO) thin films grown by sol-gel technique. For various device applications, current injection into such nanowires is critical. This is expected to be more efficient for ZnO nanowires deposited on to AZO compared to those deposited on to a foreign substrate such as silicon. In this work we compare the morphological and optical properties of nanowires grown on AZO with those grown under similar conditions on silicon (Si) wafers. For nanowires grown on silicon, diameters around 44 nm with heights around 2.2 μm were obtained. For the growth on to AZO, the diameters were around 90 nm while the heights were around 520 nm. Room temperature photoluminescence (RT-PL) measurements show improved near band-edge emission for nanowires grown on to AZO, indicating higher material quality. This is further established by low temperature photoluminescence (LT-PL) measurements where excitonic transitions with width as small as 14 meV have been obtained at 4 K for such structures. Electron energy loss spectroscopy (EELS) studies indicate the presence of Al in the nanowires, indicating a new technique for introduction of dopants into these structures. These results indicate that ZnO nanowires on sol-gel grown AZO thin films show promise in the development of various optoelectronic devices. (paper)

Effect of different sol concentrations on the properties of nanocrystalline ZnO thin films grown on FTO substrates by sol-gel spin-coating

International Nuclear Information System (INIS)

Kim, Ikhyun; Kim, Younggyu; Nam, Giwoong; Kim, Dongwan; Park, Minju; Kim, Haeun; Lee, Wookbin; Leem, Jaeyoung; Kim, Jongsu; Kim, Jin Soo

2014-01-01

Nanocrystalline ZnO thin films grown on fluorine-doped tinoxide (FTO) substrates were fabricated using the spin-coating method. The structural and the optical properties of the ZnO thin films prepared using different sol concentrations were investigated by using field-emission scanning electron microscopy (FE-SEM), X-ray diffractometry (XRD), photoluminescence (PL) measurements, and ultraviolet-visible (UV-vis) spectrometry. The surface morphology of the ZnO thin films, as observed in the SEM images, exhibited a mountain-chain structure. XRD results indicated that the thin films were preferentially orientated along the direction of the c-axis and that the grain size of the ZnO thin films increased with increasing sol concentration. The PL spectra showed a strong ultraviolet emission peak at 3.22 eV and a broad orange emission peak at 2.0 eV. The intensities of deep-level emission (DLE) gradually increased with increasing sol concentration from 0.4 to 1.0 M. The transmittance spectra of the ZnO thin films showed that the ZnO thin films were transparent (∼85%) in the visible region and exhibited sharp absorption edges at 375 nm. Thus, The Urbach energy of ZnO thin films decreased with increasing sol concentration.

Influence of Te and Se doping on ZnO films growth by SILAR method

Science.gov (United States)

Güney, Harun; Duman, Ćaǧlar

2016-04-01

The AIP Successive ionic layer adsorption and reaction (SILAR) is an economic and simple method to growth thin films. In this study, SILAR method is used to growth Selenium (Se) and Tellurium (Te) doped zinc oxide (ZnO) thin films with different doping rates. For characterization of the films X-ray diffraction (XRD), absorbance and scanning electron microscopy (SEM) are used. XRD results are showed well-defined strongly (002) oriented crystal structure for all samples. Also, absorbance measurements show, Te and Se concentration are proportional and inversely proportional with band gap energy, respectively. SEM measurements show that the surface morphology and thickness of the material varied with Se and/or Te and varying concentrations.

Influence of Te and Se doping on ZnO films growth by SILAR method

International Nuclear Information System (INIS)

Güney, Harun; Duman, Çağlar

2016-01-01

The AIP Successive ionic layer adsorption and reaction (SILAR) is an economic and simple method to growth thin films. In this study, SILAR method is used to growth Selenium (Se) and Tellurium (Te) doped zinc oxide (ZnO) thin films with different doping rates. For characterization of the films X-ray diffraction (XRD), absorbance and scanning electron microscopy (SEM) are used. XRD results are showed well-defined strongly (002) oriented crystal structure for all samples. Also, absorbance measurements show, Te and Se concentration are proportional and inversely proportional with band gap energy, respectively. SEM measurements show that the surface morphology and thickness of the material varied with Se and/or Te and varying concentrations.

Influence of Te and Se doping on ZnO films growth by SILAR method

Energy Technology Data Exchange (ETDEWEB)

Güney, Harun, E-mail: harunguney25@hotmail.com [Department of Electric and Energy, Vocation High School, Ağrı İbrahim Çeçen University (Turkey); Duman, Çağlar, E-mail: caglarduman@erzurum.edu.tr [Department of Electrical and Electronic Engineering, Faculty of Engineering, Erzurum Technical University (Turkey)

2016-04-18

The AIP Successive ionic layer adsorption and reaction (SILAR) is an economic and simple method to growth thin films. In this study, SILAR method is used to growth Selenium (Se) and Tellurium (Te) doped zinc oxide (ZnO) thin films with different doping rates. For characterization of the films X-ray diffraction (XRD), absorbance and scanning electron microscopy (SEM) are used. XRD results are showed well-defined strongly (002) oriented crystal structure for all samples. Also, absorbance measurements show, Te and Se concentration are proportional and inversely proportional with band gap energy, respectively. SEM measurements show that the surface morphology and thickness of the material varied with Se and/or Te and varying concentrations.

Mn-doped ZnO nanocrystals synthesized by sonochemical method: Structural, photoluminescence, and magnetic properties

Energy Technology Data Exchange (ETDEWEB)

Othman, A.A., E-mail: aaelho@yahoo.com [Assiut University, Faculty of Science, Department of Physics, Assiut 71516 (Egypt); Osman, M.A. [Assiut University, Faculty of Science, Department of Physics, Assiut 71516 (Egypt); Ibrahim, E.M.M. [Sohag University, Faculty of Science, Department of Physics, Sohag 82524 (Egypt); Ali, Manar A.; Abd-Elrahim, A.G. [Assiut University, Faculty of Science, Department of Physics, Assiut 71516 (Egypt)

2017-05-15

Highlights: • Mn-doped ZnO nanostructures were synthesized by the sonochemical method. • Structural, morphological, optical, photoluminescence and magnetic properties were investigated. • Mn-doped ZnO nanostructures reveal a blue shift of the optical band gap. • Photoluminescence spectra of Mn-doped ZnO nanostructures show quenching in the emission intensity. • Mn-doped ZnO nanostructures exhibit ferromagnetic ordering at room temperature. - Abstract: This work reports the synthesis of Mn-doped ZnO nanostructures using ice-bath assisted sonochemical technique. The impact of Mn-doping on structural, morphological, optical, and magnetic properties of ZnO nanostructures is studied. The morphological study shows that the lower doped samples possess mixtures of nanosheets and nanorods while the increase in Mn content leads to improvement of an anisotropic growth in a preferable orientation to form well-defined edge rods at Mn content of 0.04. UV–vis absorption spectra show that the exciton peak in the UV region is blue shifted due to Mn incorporation into the ZnO lattice. Doping ZnO with Mn ions leads to a reduction in the PL intensity due to a creation of more non-radiative recombination centers. The magnetic measurements show that the Mn-doped ZnO nanostructures exhibit ferromagnetic ordering at room temperature, as well as variation of the Mn content can significantly affect the ferromagnetic behavior of the samples.

Room temperature ferromagnetism in Co doped ZnO within an optimal doping level of 5%

International Nuclear Information System (INIS)

Mohapatra, J.; Mishra, D.K.; Mishra, Debabrata; Perumal, A.; Medicherla, V.R.R.; Phase, D.M.; Singh, S.K.

2012-01-01

Highlights: ► Zn 1−x Co x O ((0 ≤ x ≤ 0.1)) system synthesized by solid state reaction technique. ► Observation of room temperature ferromagnetism for 3 and 5% Co doped ZnO. ► XPS and EPMA studies predict the occurrence of segregated CoO clusters. ► Suppresses ferromagnetic ordering in higher doping percentage of Co (>5%). -- Abstract: We report on the structural, micro-structural and magnetic properties of Zn 1−x Co x O (0 ≤ x ≤ 0.1) system. Electron probe micro-structural analysis on 5% Co doped ZnO indicates the presence of segregated cobalt oxide which is also confirmed from the Co 2p core level X-ray photoelectron spectrum. The presence of oxygen defects in lower percentage of Co doped ZnO (≤5%) enhances the carrier mediated exchange interaction and thereby enhancing the room-temperature ferromagnetic behaviour. Higher doping percentage of cobalt (>5%) creates weak link between the grains and suppresses the carrier mediated exchange interaction. This is the reason why room temperature ferromagnetism is not observed in 7% and 10% Co doped ZnO.

Structural, magnetic and electronic structure properties of Co doped ZnO nanoparticles

International Nuclear Information System (INIS)

Kumar, Shalendra; Song, T.K.; Gautam, Sanjeev; Chae, K.H.; Kim, S.S.; Jang, K.W.

2015-01-01

Highlights: • XRD and HR-TEM results show the single phase nature of Co doped ZnO nanoparticles. • XMCD and dc magnetization results indicate the RT-FM in Co doped ZnO nanoparticles. • Co L 3,2 NEXAFS spectra infer that Co ions are in 2+ valence state. • O K edge NEXAFS spectra show that O vacancy increases with Co doping in ZnO. - Abstract: We reported structural, magnetic and electronic structure studies of Co doped ZnO nanoparticles. Doping of Co ions in ZnO host matrix has been studied and confirmed using various methods; such as X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), energy dispersed X-ray (EDX), high resolution transmission electron microscopy (HR-TEM), Fourier transform infrared spectroscopy (FT-IR), near edge X-ray absorption fine structure (NEXAFS) spectroscopy, magnetic hysteresis loop measurements and X-ray magnetic circular dichroism (XMCD). From the XRD and HR-TEM results, it is observed that Co doped ZnO nanoparticles have single phase nature with wurtzite structure and exclude the possibility of secondary phase formation. FE-SEM and TEM micrographs show that pure and Co doped nanoparticles are nearly spherical in shape. O K edge NEXAFS spectra indicate that O vacancies increase with Co doping. The Co L 3,2 edge NEXAFS spectra revealed that Co ions are in 2+ valence state. DC magnetization hysteresis loops and XMCD results clearly showed the intrinsic origin of temperature ferromagnetism in Co doped ZnO nanoparticles

Al-doped ZnO seed layer-dependent crystallographic control of ZnO nanorods by using electrochemical deposition

Energy Technology Data Exchange (ETDEWEB)

Son, Hyo-Soo; Choi, Nak-Jung [Department of Nano-Optical Engineering, Korea Polytechnic University, Siheung 429-793 (Korea, Republic of); Kim, Kyoung-Bo [Department of Metallurgical and Materials Engineering, Inha Technical College, Incheon 402-752 (Korea, Republic of); Kim, Moojin [Department of Renewable Energy, Jungwon University, Goesan-gun, Chungbuk 367-805 (Korea, Republic of); Lee, Sung-Nam, E-mail: snlee@kpu.ac.kr [Department of Nano-Optical Engineering, Korea Polytechnic University, Siheung 429-793 (Korea, Republic of)

2016-10-15

Highlights: • Polar and semipolar ZnO NRs were successfully achieved by hydrothermal synthesis. • Semipolar and polar ZnO NRs were grown on ZnO and AZO/m-sapphire, respectively. • Al % of AZO/m-sapphire enhanced the lateral growth rate of polar ZnO NRs. - Abstract: We investigated the effect of an Al-doped ZnO film on the crystallographic direction of ZnO nanorods (NRs) using electrochemical deposition. From high-solution X-ray diffraction measurements, the crystallographic plane of ZnO NRs grown on (1 0 0) ZnO/m-plane sapphire was (1 0 1). The surface grain size of the (100) Al-doped ZnO (AZO) film decreased with increasing Al content in the ZnO seed layer, implying that the Al dopant accelerated the three-dimensional (3D) growth of the AZO film. In addition, it was found that with increasing Al doping concentration of the AZO seed layer, the crystal orientation of the ZnO NRs grown on the AZO seed layer changed from [1 0 1] to [0 0 1]. With increasing Al content of the nonpolar (1 0 0) AZO seed layer, the small surface grains with a few crystallographic planes of the AZO film changed from semipolar (1 0 1) ZnO NRs to polar (0 0 1) ZnO NRs due to the increase of the vertical [0 0 1] growth rate of the ZnO NRs owing to excellent electrical properties.

Preparation of manganese-doped ZnO thin films and their ...

Indian Academy of Sciences (India)

Various physical and chemical techniques that has been used to deposit Mn:ZnO thin films .... appearance and Mn-doped films were slightly brownish with a good adherence to the ..... shows a constantly decreasing trend with increasing man-.

Control of N/N2 species ratio in NO plasma for p-type doping of ZnO

International Nuclear Information System (INIS)

Chen Xingyou; Zhang Zhenzhong; Jiang Mingming; Wang Shuangpeng; Li Binghui; Shan Chongxin; Liu Lei; Zhao Dongxu; Shen Dezhen; Yao Bin

2011-01-01

Nitrogen-doped ZnO thin films were grown on c-plane sapphire (Al 2 O 3 ) substrates via plasma-assisted molecular beam epitaxy using plasma activated nitric oxide (NO) as the oxygen source and dopant. X-ray diffraction measurements indicate that a small NO flux benefits the crystal quality of the thin films. Hall effect measurements indicate that the electron density of the ZnO films decreases gradually with decreasing NO flux, and the conduction reverses to p-type at a certain flux. Optical emission spectra indicate that the N atom content in the NO plasma increases with decreasing NO flux, and the origin of this is discussed. X-ray photoelectron spectroscopy measurements demonstrate that the number of N atom occupied O sites in the ZnO lattice increases correspondingly.

Electronic structure, magnetic and structural properties of Ni doped ZnO nanoparticles

International Nuclear Information System (INIS)

Kumar, Shalendra; Vats, Prashant; Gautam, S.; Gupta, V.P.; Verma, K.D.; Chae, K.H.; Hashim, Mohd; Choi, H.K.

2014-01-01

Highlights: • XRD, and HR-TEM results show the single phase nature of Ni doped ZnO nanoparticles. • dc magnetization results indicate the RT-FM in Ni doped ZnO nanoparticles. • Ni L 3,2 edge NEXAFS spectra infer that Ni ions are in +2 valence state. • O K edge NEXAFS spectra show that O vacancy increases with Ni doping in ZnO. - Abstract: We report structural, magnetic and electronic structural properties of Ni doped ZnO nanoparticles prepared by auto-combustion method. The prepared nanoparticles were characterized by using X-ray diffraction (XRD), high resolution transmission electron microscopy (HR-TEM), near edge X-ray absorption fine structure (NEXAFS) spectroscopy, and dc magnetization measurements. The XRD and HR-TEM results indicate that Ni doped ZnO nanoparticles have single phase nature with wurtzite lattice and exclude the presence of secondary phase. NEXAFS measurements performed at Ni L 3,2 -edges indicates that Ni ions are in +2 valence state and exclude the presence of Ni metal clusters. O K-edge NEXAFS spectra indicate an increase in oxygen vacancies with Ni-doping, while Zn L 3,2 -edge show the absence of Zn-vacancies. The magnetization measurements performed at room temperature shows that pure and Ni doped ZnO exhibits ferromagnetic behavior

Optoelectronic Characterization of Ta-Doped ZnO Thin Films by Pulsed Laser Deposition.

Science.gov (United States)

Koo, Horng-Show; Peng, Jo-Chi; Chen, Mi; Chin, Hung-I; Chen, Jaw-Yeh; Wu, Maw-Kuen

2015-11-01

Transparent conductive oxide of Ta-doped ZnO (TZO) film with doping amount of 3.0 wt% have been deposited on glass substrates (Corning Eagle XG) at substrate temperatures of 100 to 500 degrees C by the pulsed laser deposition (PLD) technique. The effect of substrate temperature on the structural, optical and electronic characteristics of Ta-doped ZnO (TZO) films with 3.0 wt% dopant of tantalum oxide (Ta2O5) was measured and demonstrated in terms of X-ray diffraction (XRD), ultraviolet-visible spectrometer (UV-Vis), four-probe and Hall-effect measurements. X-ray diffraction pattern shows that TZO films grow in hexagonal crystal structure of wurtzite phase with a preferred orientation of the crystallites along (002) direction and exhibits better physical characteristics of optical transmittance, electrical conductivity, carrier concentration and mobility for the application of window layer in the optoelectronic devices of solar cells, OLEDs and LEDs. The lowest electrical resistivity (ρ) and the highest carrier concentration of the as-deposited film deposited at 300 degrees C are measured as 2.6 x 10(-3) Ω-cm and 3.87 x 10(-20) cm(-3), respectively. The highest optical transmittance of the as-deposited film deposited at 500 degrees C is shown to be 93%, compared with another films deposited below 300 degrees C. It is found that electrical and optical properties of the as-deposited TZO film are greatly dependent on substrate temperature during laser ablation deposition.

Thickness-dependent magneto-optical effects in hole-doped GaS and GaSe multilayers: a first-principles study

Science.gov (United States)

Li, Fei; Zhou, Xiaodong; Feng, Wanxiang; Fu, Botao; Yao, Yugui

2018-04-01

Recently, two-dimensional (2D) GaS and GaSe nanosheets were successfully fabricated and the measured electronic, mechanical, and optoelectronic properties are excellent. Here, using the first-principles density functional theory, we investigate the magnetic, optical, and magneto-optical (MO) Kerr and Faraday effects in hole-doped GaS and GaSe multilayers. GaS and GaSe monolayers (MLs) manifest ferromagnetic ground states by introducing even a small amount of hole doping, whereas the magnetism in GaS and GaSe multilayers are significantly different under hole doping. Our results show that ferromagnetic states can be easily established in GaS bilayers and trilayers under proper hole doping, however, most of GaSe multilayers are more favorable to nonmagnetic states. The magnetic moments in GaS multilayers are weakened remarkably with the increasing of thin film thickness and are negligible more than three MLs. This leads to the thickness dependence of MO Kerr and Faraday effects. Furthermore, the MO effects strongly depend on the doping concentration and therefore are electrically controllable by adjusting the number of holes via gate voltage. The substrate effects on the MO properties are also discussed. Combining the unique MO and other interesting physical properties make GaS and GaSe a superior 2D material platform for semiconductor MO and spintronic nanodevices.

Spectroscopic and magnetic properties of Mn doped GaN epitaxial films grown by plasma assisted molecular beam epitaxy

International Nuclear Information System (INIS)

Vidyasagar, R.; Lin, Y.-T.; Tu, L.-W.

2012-01-01

Graphical abstract: We report here that micro-Raman scattering spectrum for Mn doped GaN thin film has displayed a new peak manifested at 578 cm −1 , by which it is attributed to interior LVM originated by the incorporation of Mn ions in place of Ga sites. Mn doped GaN thin film also showed the typical negative magnetoresistance up to ∼50 K, revealing that the film showed magnetic ordering of spins below 50 K. Display Omitted Highlights: ► GaN and Mn doped GaN single phase wurtzite structures grown by PAMBE. ► The phase purity of the epilayers investigated by HRXRD, HRSEM and EDX. ► The red shift in near band edge emission has been observed using micro-PL. ► A new peak related LVM at 578 cm −1 in micro-Raman scattering measurements confirmed Mn doped into GaN. ► Negative-magnetoresistance investigations have showed that the film has T c −1 , which is attributed to the vacancy-related local vibrational mode of Mn occupying the Ga site. Temperature dependent negative magnetoresistance measurements provide a direct evidence of magnetic ordering below 50 K for the Mn doped GaN thin film.

Comparative study of zinc oxide and aluminum doped zinc oxide transparent thin films grown by direct current magnetron sputtering

International Nuclear Information System (INIS)

Suchea, M.; Christoulakis, S.; Katsarakis, N.; Kitsopoulos, T.; Kiriakidis, G.

2007-01-01

Pure and aluminum (Al) doped zinc oxide (ZnO and ZAO) thin films have been grown using direct current (dc) magnetron sputtering from pure metallic Zn and ceramic ZnO targets, as well as from Al-doped metallic ZnAl2at.% and ceramic ZnAl2at.%O targets at room temperature (RT). The effects of target composition on the film's surface topology, crystallinity, and optical transmission have been investigated for various oxygen partial pressures in the sputtering atmosphere. It has been shown that Al-doped ZnO films sputtered from either metallic or ceramic targets exhibit different surface morphology than the undoped ZnO films, while their preferential crystalline growth orientation revealed by X-ray diffraction remains always the (002). More significantly, Al-doping leads to a larger increase of the optical transmission and energy gap (E g ) of the metallic than of the ceramic target prepared films

Tungsten-doped ZnO nanocomposite: Synthesis, characterization, and highly active photocatalyst toward dye photodegradation

Energy Technology Data Exchange (ETDEWEB)

Moafi, Hadi Fallah, E-mail: Fallah.m@guilan.ac.ir [Department of Chemistry, Faculty of Science, University of Guilan, P.O. Box 1914, Rasht (Iran, Islamic Republic of); Zanjanchi, Mohammad Ali; Shojaie, Abdollah Fallah [Department of Chemistry, Faculty of Science, University of Guilan, P.O. Box 1914, Rasht (Iran, Islamic Republic of)

2013-05-15

A series of W-doped ZnO nanocomposite with different W contents were synthesized by sol–gel method and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), diffuse reflectance spectroscopy (DRS), X-ray photoelectron spectroscopy (XPS), inductively coupled plasma (ICP) and BET surface area measurement. The XRD results revealed that all the W-doped samples showed a hexagonal wurtzite structure. The results of EDS and XPS revealed that W was doped into ZnO structure. The particle size of doped ZnO is much smaller as compared to that of pure ZnO. The photocatalytic activity of undoped ZnO and W-doped ZnO was evaluated by the photodegradation of methylene blue in aqueous solution. The results show that the photocatalytic activity of the W-doped ZnO is much higher than that of undoped ZnO and the optimum percentage of doped W is 4 mol%. The enhanced photocatalytic activity of the W-ZnO samples may be related to the narrowing of the band gap, increase in the charge separation efficiency, particle size reduction and increase of the surface area. Highlights: ► W-doped ZnO nanocomposites were synthesized by a sol–gel method. ► The XRD results revealed that all the materials consisting of wurtzite structure. ► The sizes of the W-ZnO nanocomposite are 5–10 nm, obtained from TEM image. ► With W doping into ZnO photoinduced charge separation rate has been enhanced. ► Photocatalytic activity of the W-ZnO is much higher than that of undoped ZnO.

Tungsten-doped ZnO nanocomposite: Synthesis, characterization, and highly active photocatalyst toward dye photodegradation

International Nuclear Information System (INIS)

Moafi, Hadi Fallah; Zanjanchi, Mohammad Ali; Shojaie, Abdollah Fallah

2013-01-01

A series of W-doped ZnO nanocomposite with different W contents were synthesized by sol–gel method and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), diffuse reflectance spectroscopy (DRS), X-ray photoelectron spectroscopy (XPS), inductively coupled plasma (ICP) and BET surface area measurement. The XRD results revealed that all the W-doped samples showed a hexagonal wurtzite structure. The results of EDS and XPS revealed that W was doped into ZnO structure. The particle size of doped ZnO is much smaller as compared to that of pure ZnO. The photocatalytic activity of undoped ZnO and W-doped ZnO was evaluated by the photodegradation of methylene blue in aqueous solution. The results show that the photocatalytic activity of the W-doped ZnO is much higher than that of undoped ZnO and the optimum percentage of doped W is 4 mol%. The enhanced photocatalytic activity of the W-ZnO samples may be related to the narrowing of the band gap, increase in the charge separation efficiency, particle size reduction and increase of the surface area. Highlights: ► W-doped ZnO nanocomposites were synthesized by a sol–gel method. ► The XRD results revealed that all the materials consisting of wurtzite structure. ► The sizes of the W-ZnO nanocomposite are 5–10 nm, obtained from TEM image. ► With W doping into ZnO photoinduced charge separation rate has been enhanced. ► Photocatalytic activity of the W-ZnO is much higher than that of undoped ZnO

Doping of ZnO nanowires using phosphorus diffusion from a spin-on doped glass source

International Nuclear Information System (INIS)

Bocheux, A.; Robin, I. C.; Bonaimé, J.; Hyot, B.; Feuillet, G.; Kolobov, A. V.; Fons, P.; Mitrofanov, K. V.; Tominaga, J.; Tamenori, Y.

2014-01-01

In this article, we report on ZnO nanowires that were phosphorus doped using a spin on dopant glass deposition and diffusion method. Photoluminescence measurements suggest that this process yields p-doped ZnO. The spatial location of P atoms was studied using x-ray near-edge absorption structure spectroscopy and it is concluded that the doping is amphoteric with P atoms located on both Zn and O sites

Single and couple doping ZnO nanocrystals characterized by positron techniques

Science.gov (United States)

Pasang, Tenzin; Namratha, Keerthiraj; Guagliardo, Paul; Byrappa, Kullaiah; Ranganathaiah, Chikkakuntappa; Samarin, S.; Williams, J. F.

2015-04-01

Zinc oxide (ZnO) nanocrystals have been synthesized using a mild hydrothermal process using low temperatures and pressures with the advantages of free growth catalyst, low cost and alternative technology. Positron annihilation lifetime spectroscopy and coincidence Doppler broadening (CDB) spectroscopic methods have been used to investigate the roles of single- and co-dopants and native defects of the ZnO nanocrystals controlled by the synthesis process. It is shown that single Ag1+ and Pd2+ dopants occupy interstitial sites of the ZnO lattice and single Ru3+ doping replaces Zn vacancies substitutionally with a significant effect on the CDB momentum ratio curves when compared using ZnO as the reference spectrum. The co-doping of the ZnO lattice with (Sn4+ + Co2+) shows similar CDB ratios as Ru3+ single-doping. Also co-doping with (Ag1+ + Pd2+) or (Ag1+ + W6+) shows significant decreases in the band gap energy up to about 12.6% compared to single doping. The momentum ratio curves, referenced to undoped ZnO, indicate dopants in interstitial and substitutional sites. The presence of transition metal ions interstitially will trap electrons which resist the recombination of electrons and in turn affect the conductivity of the material.

Single and couple doping ZnO nanocrystals characterized by positron techniques

International Nuclear Information System (INIS)

Pasang, Tenzin; Namratha, Keerthiraj; Byrappa, Kullaiah; Guagliardo, Paul; Ranganathaiah, Chikkakuntappa; Samarin, S; Williams, J F

2015-01-01

Zinc oxide (ZnO) nanocrystals have been synthesized using a mild hydrothermal process using low temperatures and pressures with the advantages of free growth catalyst, low cost and alternative technology. Positron annihilation lifetime spectroscopy and coincidence Doppler broadening (CDB) spectroscopic methods have been used to investigate the roles of single- and co-dopants and native defects of the ZnO nanocrystals controlled by the synthesis process. It is shown that single Ag 1+ and Pd 2+ dopants occupy interstitial sites of the ZnO lattice and single Ru 3+ doping replaces Zn vacancies substitutionally with a significant effect on the CDB momentum ratio curves when compared using ZnO as the reference spectrum. The co-doping of the ZnO lattice with (Sn 4+ + Co 2+ ) shows similar CDB ratios as Ru 3+ single-doping. Also co-doping with (Ag 1+ + Pd 2+ ) or (Ag 1+ + W 6+ ) shows significant decreases in the band gap energy up to about 12.6% compared to single doping. The momentum ratio curves, referenced to undoped ZnO, indicate dopants in interstitial and substitutional sites. The presence of transition metal ions interstitially will trap electrons which resist the recombination of electrons and in turn affect the conductivity of the material. (paper)

Fabrication and characterization of Pd/Cu doped ZnO/Si and Ni/Cu doped ZnO/Si Schottky diodes

Energy Technology Data Exchange (ETDEWEB)

Agarwal, Lucky; Singh, Brijesh Kumar; Tripathi, Shweta [Department of Electronics & Communication Engineering, Motilal Nehru National Institute of Technology, Allahabad 211004 (India); Chakrabarti, P., E-mail: pchakrabarti.ece@iitbhu.ac.in [Department of Electronics & Communication Engineering, Motilal Nehru National Institute of Technology, Allahabad 211004 (India); Department of Electronics Engineering, Indian Institute of Technology (Banaras Hindu University), Varanasi 221005 (India)

2016-08-01

In this paper, fabrication and characterization of copper doped ZnO (Cu doped ZnO) based Schottky devices have been reported. Cu doped ZnO thin films have been deposited on p-Si (100) samples by the sol-gel spin coating method. X-Ray diffraction (XRD) and atomic force microscopy (AFM) studies have been done in order to evaluate the structural and morphological properties of the film. The optical properties of the film have been determined by using variable angle ellipsometry. Further, Seebeck measurement of the deposited Cu doped ZnO film leads to positive Seebeck coefficient confirming the p-type conductivity of the sample. The resistivity and acceptor concentration of the film has also been evaluated using four probe measurement system. Pd and Ni metals have been deposited on separate Cu doped ZnO thin film samples using low cost thermal evaporation method to form Schottky contacts. The electrical characterization of the Schottky diode has been performed by semiconductor device analyzer (SDA). Electrical parameters such as barrier height, ideality factor, reverse saturation current and rectification ratio have also been determined for the as-prepared Schottky diode using conventional thermionic emission model and Cheung's method. - Highlights: • Fabrication of sol-gel derived Cu doped ZnO (p-type) Schottky contact proposed. • The p-type Conductivity of the sample confirmed by Seebeck Measurement. • Pd and Ni deposited on Cu doped ZnO film to form Schottky contacts. • Cu doped ZnO expected to emerge as a potential material for thin film solar cells.

Fabrication and characterization of Pd/Cu doped ZnO/Si and Ni/Cu doped ZnO/Si Schottky diodes

International Nuclear Information System (INIS)

Agarwal, Lucky; Singh, Brijesh Kumar; Tripathi, Shweta; Chakrabarti, P.

2016-01-01

In this paper, fabrication and characterization of copper doped ZnO (Cu doped ZnO) based Schottky devices have been reported. Cu doped ZnO thin films have been deposited on p-Si (100) samples by the sol-gel spin coating method. X-Ray diffraction (XRD) and atomic force microscopy (AFM) studies have been done in order to evaluate the structural and morphological properties of the film. The optical properties of the film have been determined by using variable angle ellipsometry. Further, Seebeck measurement of the deposited Cu doped ZnO film leads to positive Seebeck coefficient confirming the p-type conductivity of the sample. The resistivity and acceptor concentration of the film has also been evaluated using four probe measurement system. Pd and Ni metals have been deposited on separate Cu doped ZnO thin film samples using low cost thermal evaporation method to form Schottky contacts. The electrical characterization of the Schottky diode has been performed by semiconductor device analyzer (SDA). Electrical parameters such as barrier height, ideality factor, reverse saturation current and rectification ratio have also been determined for the as-prepared Schottky diode using conventional thermionic emission model and Cheung's method. - Highlights: • Fabrication of sol-gel derived Cu doped ZnO (p-type) Schottky contact proposed. • The p-type Conductivity of the sample confirmed by Seebeck Measurement. • Pd and Ni deposited on Cu doped ZnO film to form Schottky contacts. • Cu doped ZnO expected to emerge as a potential material for thin film solar cells.

Optically active centers in Eu implanted, Eu in situ doped GaN, and Eu doped GaN quantum dots

International Nuclear Information System (INIS)

Bodiou, L.; Braud, A.; Doualan, J.-L.; Moncorge, R.; Park, J. H.; Munasinghe, C.; Steckl, A. J.; Lorenz, K.; Alves, E.; Daudin, B.

2009-01-01

A comparison is presented between Eu implanted and Eu in situ doped GaN thin films showing that two predominant Eu sites are optically active around 620 nm in both types of samples with below and above bandgap excitation. One of these sites, identified as a Ga substitutional site, is common to both types of Eu doped GaN samples despite the difference in the GaN film growth method and in the doping technique. High-resolution photoluminescence (PL) spectra under resonant excitation reveal that in all samples these two host-sensitized sites are in small amount compared to the majority of Eu ions which occupy isolated Ga substitutional sites and thus cannot be excited through the GaN host. The relative concentrations of the two predominant host-sensitized Eu sites are strongly affected by the annealing temperature for Eu implanted samples and by the group III element time opening in the molecular beam epitaxy growth. Red luminescence decay characteristics for the two Eu sites reveal different excitation paths. PL dynamics under above bandgap excitation indicate that Eu ions occupying a Ga substitutional site are either excited directly into the 5 D 0 level or into higher excited levels such as 5 D 1 , while Eu ions sitting in the other site are only directly excited into the 5 D 0 level. These differences are discussed in terms of the spectral overlap between the emission band of a nearby bound exciton and the absorption bands of Eu ions. The study of Eu doped GaN quantum dots reveals the existence of only one type of Eu site under above bandgap excitation, with Eu PL dynamics features similar to Eu ions in Ga substitutional sites

Sonochemical synthesis of Dy-doped ZnO nanostructures and their photocatalytic properties

Energy Technology Data Exchange (ETDEWEB)

Yayapao, Oranuch [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Thongtem, Titipun, E-mail: ttpthongtem@yahoo.com [Department of Chemistry, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Phuruangrat, Anukorn, E-mail: phuruangrat@hotmail.com [Department of Materials Science and Technology, Faculty of Science, Prince of Songkla University, Hat Yai, Songkhla 90112 (Thailand); Thongtem, Somchai [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand)

2013-11-05

Highlights: •Undoped and Dy-doped ZnO used as photocatalysts. •They were synthesized by sonochemistry. •The promising materials for treatment of organic pollutants. -- Abstract: Dy-doped ZnO nanostructures were synthesized by a sonochemical method. The concentration effect of Dy on their phase, morphology, optical properties and photocatalytic activities was investigated. XRD patterns indicated that the as-synthesized 0–3% Dy-doped ZnO was hexagonal wurtzite structure. SEM and TEM show that the products were nanorods with their growth direction along the c axis. The photoluminescence spectrum of 3% Dy-doped ZnO, applied by Gaussian analysis, consists of three emission peaks at 376 nm, 448 nm and 487 nm. The photocatalytic activities of the as-synthesized products were determined from the degradation of methylene blue (C{sub 16}H{sub 18}N{sub 3}SCl) by UV radiation. In this research, the 3% Dy-doped ZnO showed the highest photocatalytic activity.

Sonochemical synthesis of Dy-doped ZnO nanostructures and their photocatalytic properties

International Nuclear Information System (INIS)

Yayapao, Oranuch; Thongtem, Titipun; Phuruangrat, Anukorn; Thongtem, Somchai

2013-01-01

Highlights: •Undoped and Dy-doped ZnO used as photocatalysts. •They were synthesized by sonochemistry. •The promising materials for treatment of organic pollutants. -- Abstract: Dy-doped ZnO nanostructures were synthesized by a sonochemical method. The concentration effect of Dy on their phase, morphology, optical properties and photocatalytic activities was investigated. XRD patterns indicated that the as-synthesized 0–3% Dy-doped ZnO was hexagonal wurtzite structure. SEM and TEM show that the products were nanorods with their growth direction along the c axis. The photoluminescence spectrum of 3% Dy-doped ZnO, applied by Gaussian analysis, consists of three emission peaks at 376 nm, 448 nm and 487 nm. The photocatalytic activities of the as-synthesized products were determined from the degradation of methylene blue (C 16 H 18 N 3 SCl) by UV radiation. In this research, the 3% Dy-doped ZnO showed the highest photocatalytic activity

Room temperature ferromagnetism in Mg-doped ZnO nanoparticles

International Nuclear Information System (INIS)

Singh, Jaspal; Vashihth, A.; Gill, Pritampal Singh; Verma, N. K.

2015-01-01

Zn 1-x Mg x O (x = 0, 0,10) nanoparticles were successfully synthesized using sol-gel method. X-ray diffraction (XRD) confirms that the synthesized nanoparticles possess wurtzite phase having hexagonal structure. Morphological analysis was carried out using transmission electron microscopy (TEM) which depicts the spherical morphology of ZnO nanoparticles. Energy dispersive spectroscopy (EDS) showed the presence of Mg in ZnO nanoparticles. Electron spin resonance (ESR) signal was found to be decreasing with increasing of Mg-doping concentration. The room temperature ferromagnetism was observed in undoped and Mg-doped ZnO nanoparticles. The increase of Mg-doping concentration resulted in decrease of saturation magnetization value which could be attributed to decrease of oxygen vacancies present in host nanoparticles

Design and characterization of Ga-doped indium tin oxide films for pixel electrode in liquid crystal display

International Nuclear Information System (INIS)

Choi, J.H.; Kang, S.H.; Oh, H.S.; Yu, T.H.; Sohn, I.S.

2013-01-01

Indium tin oxide (ITO) thin films doped with various metal atoms were investigated in terms of phase transition behavior and electro-optical properties for the purpose of upgrading ITO and indium zinc oxide (IZO) films, commonly used for pixel electrodes in flat panel displays. We explored Ce, Mg, Zn, and Ga atoms as dopants to ITO by the co-sputtering technique, and Ga-doped ITO films (In:Sn:Ga = 87.4:6.7:5.9 at.%) showed the phase transition behavior at 210 °C within 20 min with high visible transmittance of 91% and low resistivity of 0.22 mΩ cm. The film also showed etching rate similar to amorphous ITO, and no etching residue on glass surfaces. These results were confirmed with the film formed from a single Ga-doped ITO target with slightly different compositions (In:Sn:Ga = 87:9:4 at.%). Compared to the ITO target, Ga-doped ITO target left 1/4 less nodules on the target surface after sputtering. These results suggest that Ga-doped ITO films could be an excellent alternative to ITO and IZO for pixel electrodes in thin film transistor liquid crystal display (TFT-LCD). - Highlights: ► We report Ga-doped In–Sn–O films for a pixel electrode in liquid crystal display. ► Ga-doped In–Sn–O films show phase transition behavior at 210 °C. ► Ga-doped In–Sn–O films show high wet etchability and low resistivity

Polycrystalline ZnO: B grown by LPCVD as TCO for thin film silicon solar cells

International Nuclear Information System (INIS)

Fay, Sylvie; Steinhauser, Jerome; Nicolay, Sylvain; Ballif, Christophe

2010-01-01

Conductive zinc oxide (ZnO) grown by low pressure chemical vapor deposition (LPCVD) technique possesses a rough surface that induces an efficient light scattering in thin film silicon (TF Si) solar cells, which makes this TCO an ideal candidate for contacting such devices. IMT-EPFL has developed an in-house LPCVD process for the deposition of nanotextured boron doped ZnO films used as rough TCO for TF Si solar cells. This paper is a general review and synthesis of the study of the electrical, optical and structural properties of the ZnO:B that has been performed at IMT-EPFL. The influence of the free carrier absorption and the grain size on the electrical and optical properties of LPCVD ZnO:B is discussed. Transport mechanisms at grain boundaries are studied. It is seen that high doping of the ZnO grains facilitates the tunnelling of the electrons through potential barriers that are located at the grain boundaries. Therefore, even if these potential barriers increase after an exposition of the film to a humid atmosphere, the heavily doped LPCVD ZnO:B layers show a remarkable stable conductivity. However, the introduction of diborane in the CVD reaction induces also a degradation of the intra-grain mobility and increases over-proportionally the optical absorption of the ZnO:B films. Hence, the necessity to finely tune the doping level of LPCVD ZnO:B films is highlighted. Finally, the next challenges to push further the optimization of LPCVD ZnO:B films for thin film silicon solar cells are discussed, as well as some remarkable record cell results achieved with LPCVD ZnO:B as front electrode.

Growth and characterization of semi-insulating carbon-doped/undoped GaN multiple-layer buffer

International Nuclear Information System (INIS)

Kim, Dong-Seok; Won, Chul-Ho; Kang, Hee-Sung; Kim, Young-Jo; Kang, In Man; Lee, Jung-Hee; Kim, Yong Tae

2015-01-01

We have proposed a new semi-insulating GaN buffer layer, which consists of multiple carbon-doped and undoped GaN layer. The buffer layer showed sufficiently good semi-insulating characteristics, attributed to the depletion effect between the carbon-doped GaN and the undoped GaN layers, even though the thickness of the carbon-doped GaN layer in the periodic structure was designed to be very thin to minimize the total carbon incorporation into the buffer layer. The AlGaN/AlN/GaN heterostructure grown on the proposed buffer exhibited much better electrical and structural properties than that grown on the conventional thick carbon-doped semi-insulating GaN buffer layer, confirmed by Hall measurement, x-ray diffraction, and secondary ion mass spectrometry. The fabricated device also showed excellent buffer breakdown characteristics. (paper)

Studies on morphology, electrical and optical characteristics of Al-doped ZnO thin films grown by atomic layer deposition

Science.gov (United States)

Chen, Li; Chen, Xinliang; Zhou, Zhongxin; Guo, Sheng; Zhao, Ying; Zhang, Xiaodan

2018-03-01

Al doped ZnO (AZO) films deposited on glass substrates through the atomic layer deposition (ALD) technique are investigated with various temperatures from 100 to 250 °C and different Zn : Al cycle ratios from 20 : 0 to 20 : 3. Surface morphology, structure, optical and electrical properties of obtained AZO films are studied in detail. The Al composition of the AZO films is varied by controlling the ratio of Zn : Al. We achieve an excellent AZO thin film with a resistivity of 2.14 × 10‑3 Ω·cm and high optical transmittance deposited at 150 °C with 20 : 2 Zn : Al cycle ratio. This kind of AZO thin films exhibit great potential for optoelectronics device application. Project supported by the State Key Development Program for Basic Research of China (Nos. 2011CBA00706, 2011CBA00707) and the Tianjin Applied Basic Research Project and Cutting-Edge Technology Research Plan (No. 13JCZDJC26900).

Al-Doped ZnO Monolayer as a Promising Transparent Electrode Material: A First-Principles Study

Directory of Open Access Journals (Sweden)

Mingyang Wu

2017-03-01

Full Text Available Al-doped ZnO has attracted much attention as a transparent electrode. The graphene-like ZnO monolayer as a two-dimensional nanostructure material shows exceptional properties compared to bulk ZnO. Here, through first-principle calculations, we found that the transparency in the visible light region of Al-doped ZnO monolayer is significantly enhanced compared to the bulk counterpart. In particular, the 12.5 at% Al-doped ZnO monolayer exhibits the highest visible transmittance of above 99%. Further, the electrical conductivity of the ZnO monolayer is enhanced as a result of Al doping, which also occurred in the bulk system. Our results suggest that Al-doped ZnO monolayer is a promising transparent conducting electrode for nanoscale optoelectronic device applications.

Properties of Al- and Ga-doped thin zinc oxide films treated with UV laser radiation

Science.gov (United States)

Al-Asedy, Hayder J.; Al-Khafaji, Shuruq A.; Bakhtiar, Hazri; Bidin, Noriah

2018-03-01

This paper reports the Nd:YAG laser irradiation treated modified properties of aluminum (Al) and gallium (Ga) co-doped zinc oxide (ZnO) (AGZO) films prepared on Si-substrate via combined sol-gel and spin-coating method. The impact of varying laser energy (150-200 mJ) on the structure, morphology, electrical and optical properties of such AGZO films were determined. Laser-treated samples were characterized using various analytical tools. Present techniques could achieve a high-quality polycrystalline films compared with those produced via conventional high temperature processing. AGZO films irradiated with third harmonics UV radiation (355 nm) from Nd:YAG laser source revealed very low resistivity of 4.02 × 10- 3 Ω cm. The structural properties grain size was calculated firm the X-ray diffraction spectra using the Scherrer equation that increased from 12.7 to 22.5 nm as the annealing laser energy increased from (150-200) mJ. The differences in crystallinity and orientation are explained in terms of the thermal effect caused by laser irradiation. (FESEM) images have been demonstrated that Nd:YAG laser annealing can significantly improve the crystallinity level, densification, and surface flatness of sol-gel derived AGZO thin films that occurred as a result of laser processing. Synthesized AGZO films displayed favorable growth orientation along (101) lattice direction. AGZO films with energy band gap of 3.37-3.41 eV were obtained. Results on the crystallinity, surface morphology, roughness, bonding vibration, absorption, photoluminescence, and resistivity of the laser-irradiated films were analyzed and discussed.

Characteristics of sputtered Al-doped ZnO films for transparent electrodes of organic thin-film transistor

International Nuclear Information System (INIS)

Park, Yong Seob; Kim, Han-Ki

2011-01-01

Aluminum-doped ZnO (AZO) thin-films were deposited with various RF powers at room temperature by radio frequency (RF) magnetron sputtering method. The electrical properties of the AZO film were improved with the increasing RF power. These results can be explained by the improvement of the crystallinity in the AZO film. We fabricated the organic thin-film transistor (OTFT) of the bottom gate structure using pentacene active and poly-4-vinyl phenol gate dielectric layers on the indium tin oxide gate electrode, and estimated the device properties of the OTFTs including drain current-drain voltage (I D -V D ), drain current-gate voltage (I D -V G ), threshold voltage (V T ), on/off ratio and field effect mobility. The AZO film that grown at 160 W RF power exhibited low resistivity (1.54 x 10 -3 Ω.cm), high crystallinity and uniform surface morphology. The pentacene thin-film transistor using the AZO film that's fabricated at 160 W RF power exhibited good device performance such as the mobility of 0.94 cm 2 /V s and the on/off ratio of ∼ 10 5 . Consequently, the performance of the OTFT such as larger field-effect carrier mobility was determined the conductivity of the AZO source/drain (S/D) electrode. AZO films prepared at room temperature by the sputtering method are suitable for the S/D electrodes in the OTFTs.

Sodium doping in ZnO crystals

Science.gov (United States)

Parmar, N. S.; Lynn, K. G.

2015-01-01

ZnO bulk single crystals were doped with sodium by thermal diffusion. Positron annihilations spectroscopy confirms the filling of zinc vacancies, to >6 μm deep in the bulk. Secondary-ion mass spectrometry measurement shows the diffusion of sodium up to 8 μm with concentration (1-3.5) × 1017 cm-3. Broad photoluminescence excitation peak at 3.1 eV, with onset appearance at 3.15 eV in Na:ZnO, is attributed to an electronic transition from a NaZn level at ˜(220-270) meV to the conduction band. Resistivity in Na doped ZnO crystals increases up to (4-5) orders of magnitude at room temperature.

The Effects of Zr Doping on the Optical, Electrical and Microstructural Properties of Thin ZnO Films Deposited by Atomic Layer Deposition

Directory of Open Access Journals (Sweden)

Stephania Herodotou

2015-10-01

Full Text Available Transparent conducting oxides (TCOs, with high optical transparency (≥85% and low electrical resistivity (10−4 Ω·cm are used in a wide variety of commercial devices. There is growing interest in replacing conventional TCOs such as indium tin oxide with lower cost, earth abundant materials. In the current study, we dope Zr into thin ZnO films grown by atomic layer deposition (ALD to target properties of an efficient TCO. The effects of doping (0–10 at.% Zr were investigated for ~100 nm thick films and the effect of thickness on the properties was investigated for 50–250 nm thick films. The addition of Zr4+ ions acting as electron donors showed reduced resistivity (1.44 × 10−3 Ω·cm, increased carrier density (3.81 × 1020 cm−3, and increased optical gap (3.5 eV with 4.8 at.% doping. The increase of film thickness to 250 nm reduced the electron carrier/photon scattering leading to a further reduction of resistivity to 7.5 × 10−4 Ω·cm and an average optical transparency in the visible/near infrared (IR range up to 91%. The improved n-type properties of ZnO: Zr films are promising for TCO applications after reaching the targets for high carrier density (>1020 cm−3, low resistivity in the order of 10−4 Ω·cm and high optical transparency (≥85%.

Effects of O2 plasma post-treatment on ZnO: Ga thin films grown by H2O-thermal ALD

Science.gov (United States)

Lee, Yueh-Lin; Chuang, Jia-Hao; Huang, Tzu-Hsuan; Ho, Chong-Long; Wu, Meng-Chyi

2013-03-01

Transparent conducting oxides have been widely employed in optoelectronic devices using the various deposition methods such as sputtering, thermal evaporator, and e-gun evaporator technologies.1-3 In this work, gallium doped zinc oxide (ZnO:Ga) thin films were grown on glass substrates via H2O-thermal atomic layer deposition (ALD) at different deposition temperatures. ALD-GZO thin films were constituted as a layer-by-layer structure by stacking zinc oxides and gallium oxides. Diethylzinc (DEZ), triethylgallium (TEG) and H2O were used as zinc, gallium precursors and oxygen source, respectively. Furthermore, we investigated the influences of O2 plasma post-treatment power on the surface morphology, electrical and optical property of ZnO:Ga films. As the result of O2 plasma post-treatment, the characteristics of ZnO:Ga films exhibit a smooth surface, low resistivity, high carrier concentration, and high optical transmittance in the visible spectrum. However, the transmittance decreases with O2 plasma power in the near- and mid-infrared regions.

Structure of Ga2O3(ZnO)6: a member of the homologous series Ga2O3(ZnO)m

International Nuclear Information System (INIS)

Michiue, Yuichi; Kanke, Yasushi; Kimizuka, Noboru

2008-01-01

The structure of Ga 2 O 3 (ZnO) 6 was determined using singlecrystal X-ray diffraction techniques in the space group Cmcm. The metal ion sublattice resembles some of the Zn ions in the wurtzite ZnO structure. The oxygen ion sublattice in Ga 2 O 3 (ZnO) 6 also resembles some of the O ions in ZnO. Structural relationships between Ga 2 O 3 (ZnO) 6 and ZnO are discussed, illustrating the process for obtaining the centrosymmetric Ga 2 O 3 (ZnO) 6 structure from the noncentrosymmetric ZnO. Structures of phases in the homologous series Ga 2 O 3 (ZnO) m are predicted on the basis of the structural data for Ga 2 O 3 (ZnO) 6 . The structures of even m are constructed by simply extending the structure units seen in Ga 2 O 3 (ZnO) 6 , while those of odd m consist of structure units which are of different types from those used for even m. (orig.)

Control of N/N{sub 2} species ratio in NO plasma for p-type doping of ZnO

Energy Technology Data Exchange (ETDEWEB)

Chen Xingyou [Key Laboratory of Excited State Processes and Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 3888 Dongnanhu Road, Changchun, 130033 (China); Graduate School of the Chinese Academy of Sciences, Beijing 100049 (China); Zhang Zhenzhong; Jiang Mingming; Wang Shuangpeng; Li Binghui; Shan Chongxin; Liu Lei; Zhao Dongxu; Shen Dezhen [Key Laboratory of Excited State Processes and Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 3888 Dongnanhu Road, Changchun, 130033 (China); Yao Bin [State Key Laboratory of Superhard Materials and College of Physics, Jilin University, Changchun 130023 (China)

2011-09-01

Nitrogen-doped ZnO thin films were grown on c-plane sapphire (Al{sub 2}O{sub 3}) substrates via plasma-assisted molecular beam epitaxy using plasma activated nitric oxide (NO) as the oxygen source and dopant. X-ray diffraction measurements indicate that a small NO flux benefits the crystal quality of the thin films. Hall effect measurements indicate that the electron density of the ZnO films decreases gradually with decreasing NO flux, and the conduction reverses to p-type at a certain flux. Optical emission spectra indicate that the N atom content in the NO plasma increases with decreasing NO flux, and the origin of this is discussed. X-ray photoelectron spectroscopy measurements demonstrate that the number of N atom occupied O sites in the ZnO lattice increases correspondingly.

Radio-frequency magnetron sputtering and wet thermal oxidation of ZnO thin film

International Nuclear Information System (INIS)

Liu, H. F.; Chua, S. J.; Hu, G. X.; Gong, H.; Xiang, N.

2007-01-01

The authors studied the growth and wet thermal oxidation (WTO) of ZnO thin films using a radio-frequency magnetron sputtering technique. X-ray diffraction reveals a preferred orientation of [1010]ZnO(0002)//[1120]Al 2 O 3 (0002) coexisted with a small amount of ZnO (1011) and ZnO (1013) crystals on the Al 2 O 3 (0001) substrate. The ZnO (1011) and ZnO (1013) crystals, as well as the in-plane preferred orientation, are absent from the growth of ZnO on the GaAs(001) substrate. WTO at 550 deg. C improves the crystalline and the photoluminescence more significantly than annealing in air, N 2 and O 2 ambient; it also tends to convert the crystal from ZnO (1011) and ZnO (1013) to ZnO (0002). The evolution of the photoluminescence upon WTO and annealing reveals that the green and orange emissions, centered at 520 and 650 nm, are likely originated from oxygen vacancies and oxygen interstitials, respectively; while the 420 nm emission, which is very sensitive to the postgrowth thermal processing regardless of the substrate and the ambient gas, is likely originated from the surface-state related defects

Transparent conductive ZnO layers on polymer substrates: Thin film deposition and application in organic solar cells

Energy Technology Data Exchange (ETDEWEB)

Dosmailov, M. [Institute of Applied Physics, Johannes Kepler University Linz, A-4040 Linz (Austria); Leonat, L.N. [Linz Institute for Organic Solar Cells (LIOS)/Institute of Physical Chemistry, Johannes Kepler University Linz, A-4040 Linz (Austria); Patek, J. [Institute of Applied Physics, Johannes Kepler University Linz, A-4040 Linz (Austria); Roth, D.; Bauer, P. [Institute of Experimental Physics, Johannes Kepler University Linz, A-4040 Linz (Austria); Scharber, M.C.; Sariciftci, N.S. [Linz Institute for Organic Solar Cells (LIOS)/Institute of Physical Chemistry, Johannes Kepler University Linz, A-4040 Linz (Austria); Pedarnig, J.D., E-mail: johannes.pedarnig@jku.at [Institute of Applied Physics, Johannes Kepler University Linz, A-4040 Linz (Austria)

2015-09-30

Aluminum doped ZnO (AZO) and pure ZnO thin films are grown on polymer substrates by pulsed-laser deposition and the optical, electrical, and structural film properties are investigated. Laser fluence, substrate temperature, and oxygen pressure are varied to obtain transparent, conductive, and stoichiometric AZO layers on polyethylene terephthalate (PET) that are free of cracks. At low fluence (1 J/cm{sup 2}) and low pressure (10{sup −3} mbar), AZO/PET samples of high optical transmission in the visible range, low electrical sheet resistance, and high figure of merit (FOM) are produced. AZO films on fluorinated ethylene propylene have low FOM. The AZO films on PET substrates are used as electron transport layer in inverted organic solar cell devices employing P3HT:PCBM as photovoltaic polymer-fullerene bulk heterojunction. - Highlights: • Aluminum doped and pure ZnO thin films are grown on polyethylene terephthalate. • Growth parameters laser fluence, temperature, and gas pressure are optimized. • AZO films on PET have high optical transmission and electrical conductance (FOM). • Organic solar cells on PET using AZO as electron transport layer are made. • Power conversion efficiency of these OSC devices is measured.

High mobility and low operating voltage ZnGaO and ZnGaLiO transistors with spin-coated Al2O3 as gate dielectric

International Nuclear Information System (INIS)

Xia, D X; Xu, J B

2010-01-01

Spin-coated alumina serving as a gate dielectric in thin film transistors shows interesting dielectric properties for low-voltage applications, despite a moderate capacitance. With Ga singly doped and Ga, Li co-doped ZnO as the active channel layers, typical mobilities of 4.7 cm 2 V -1 s -1 and 2.1 cm 2 V -1 s -1 are achieved, respectively. At a given gate bias, the operation current is much smaller than the previously reported values in low-voltage thin film transistors, primarily relying on the giant-capacitive dielectric. The reported devices combine advantages of high mobility, low power consumption, low cost and ease of fabrication. In addition to the transparent nature of both the dielectric and semiconducting active channels, the superior electrical properties of the devices may provide a new avenue for future transparent electronics. (fast track communication)

Facile synthesis of cobalt-doped zinc oxide thin films for highly efficient visible light photocatalysts

Energy Technology Data Exchange (ETDEWEB)

Altintas Yildirim, Ozlem, E-mail: ozlemaltintas@gmail.com [Department of Metallurgical and Materials Engineering, Selcuk University, Konya (Turkey); Arslan, Hanife; Sönmezoğlu, Savaş [Department of Metallurgical and Materials Engineering, Karamanoglu Mehmetbey University, Karaman (Turkey); Nanotechnology R& D Laboratory, Karamanoglu Mehmetbey University, Karaman (Turkey)

2016-12-30

Highlights: • Photocatalytically active Co-ZnO thin film was obtained by sol-gel method. • Co{sup 2+} doping narrowed the band gap of pure ZnO to an extent of 3.18 eV. • Co-ZnO was effective in MB degradation under visible light. • Optimum dopant content to show high performance was 3 at.%. - Abstract: Cobalt-doped zinc oxide (Co:ZnO) thin films with dopant contents ranging from 0 to 5 at.% were prepared using the sol–gel method, and their structural, morphological, optical, and photocatalytic properties were characterized. The effect of the dopant content on the photocatalytic properties of the films was investigated by examining the degradation behavior of methylene blue (MB) under visible light irradiation, and a detailed investigation of their photocatalytic activities was performed by determining the apparent quantum yields (AQYs). Co{sup 2+} ions were observed to be substitutionally incorporated into Zn{sup 2+} sites in the ZnO crystal, leading to lattice parameter constriction and band gap narrowing due to the photoinduced carriers produced under the visible light irradiation. Thus, the light absorption range of the Co:ZnO films was improved compared with that of the undoped ZnO film, and the Co:ZnO films exhibited highly efficient photocatalytic activity (∼92% decomposition of MB after 60-min visible light irradiation for the 3 at.% Co:ZnO film). The AQYs of the Co:ZnO films were greatly enhanced under visible light irradiation compared with that of the undoped ZnO thin film, demonstrating the effect of the Co doping level on the photocatalytic activity of the films.

Structural and magnetic Properties of Mn, Co, Ni doped ZnO ...

African Journals Online (AJOL)

It is abundant, cost effective, non-toxic and also it is used in many bio-medical applications. ... The XRD of Mn-doped ZnO nanocrystals shows hexagonal structure. ... The TM doped ZnO nanocrystals shows weak ferromagnetic properties at ...

Formation of Ga2O3 by the oxidation of p-type GaN thin films

Energy Technology Data Exchange (ETDEWEB)

Pinnisch, Melanie; Reppin, Daniel; Stehr, Jan; Laufer, Andreas; Hofmann, Detlev M.; Meyer, Bruno K. [1. Physikalisches Institut, Justus-Liebig-University, Giessen (Germany)

2010-07-01

Both GaN and Ga{sub 2}O{sub 3} are wide band gap semiconductors with energies of 3.45 eV and 4.9 eV, respectively. While GaN can be achieved p- or n-type conducting by doping, Ga{sub 2}O{sub 3} is n-type or high resistive dependent on the presence of oxygen vacancies. We studied the conversion of p-type Mg doped GaN thin films to Ga{sub 2}O{sub 3} by thermal treatments in the temperature range from 600 C to 1200 C and in different atmospheres. Changes of the film properties were studied by means of X-ray diffraction, photo-electron spectroscopy and atomic force microscopy. Optical and magnetic resonance methods were used to investigate the evolution of the dopands and defects.

Optoelectronic and thermoelectric properties in Ga doped {beta}- PbS{sub 2} nanostructured thin films

Energy Technology Data Exchange (ETDEWEB)

Geethu, R.; Jacob, Rajani [Thin Film Research Lab, U.C. College, Aluva, Cochin, Kerala (India); Shripathi, T.; Okram, G.S.; Ganesan, V.; Tripathi, Shilpa; Fatima, Anees [UGC-DAE CSR, Khandwa Road, Indore-452 001, Madhya Pradesh (India); Sreenivasan, P.V. [Department of Chemistry, U.C. College, Aluva, Cochin, Kerala (India); Urmila, K.S.; Pradeep, B. [Solid State Physics Laboratory, Cochin University of Science and Technology, Cochin, Kerala (India); Philip, Rachel Reena, E-mail: reenatara@rediffmail.com [Thin Film Research Lab, U.C. College, Aluva, Cochin, Kerala (India)

2012-06-15

Lead sulphide nanostructured thin films were grown on soda lime glass substrates by chemical bath deposition. The films were then doped with gallium using vacuum evaporation technique. X-ray diffraction (XRD) established the structural type of the host films to be tetragonal {beta}-PbS{sub 2} with average grain size of the order of 15 nm. The nanostructure of films was further confirmed from scanning electron and atomic force micrographs. The shift in the binding energies of the 4f and 4d states of lead, 2p state of sulphur and the 2p states of Ga from their elemental binding energy values, determined from X-ray photoelectron spectroscopy (XPS), indicated intact chemical bonding in the compound. Compositional analysis showed about 0.01% doping of Ga into PbS{sub 2}. Low temperature thermopower measurements indicated p-type conductivity for the films with Fermi level positioned at about 0.017 eV above the maxima of valence band. Optical absorption studies in conjunction with photo sensitivity measurements established its pertinence in junction formation in photovoltaic applications due to the blue shift in the band gap to 2.37 eV and the increased photoconductivity of the films.

Mn{sup 2+} ions distribution in doped sol–gel deposited ZnO films

Energy Technology Data Exchange (ETDEWEB)

Stefan, Mariana, E-mail: mstefan@infim.ro [National Institute of Materials Physics, P.O. Box MG-7, 077125 Magurele (Romania); Ghica, Daniela; Nistor, Sergiu V.; Maraloiu, Adrian V. [National Institute of Materials Physics, P.O. Box MG-7, 077125 Magurele (Romania); Plugaru, Rodica [National Institute for R & D in Microtechnologies (IMT), Erou Iancu Nicolae Str. 126A, 077190 Bucharest (Romania)

2017-02-28

Highlights: • Several Mn{sup 2+} centers observed by EPR in sol–gel ZnO films. • Mn{sup 2+} ions localized at Zn{sup 2+} sites in ZnO grains and disordered ZnO phase. • Sixfold coordinated Mn{sup 2+} ions localized in inter-grain region. • Aggregated Mn in insular-like regions between ZnO grains in the ZnO:5%Mn film. • Aggregated Mn phase presence and distribution observed by EPR and EDX-STEM. - Abstract: The localization and distribution of the Mn{sup 2+} ions in two sol–gel deposited ZnO films doped with different manganese concentrations were investigated by electron paramagnetic resonance spectroscopy and analytical transmission electron microscopy. In the lightly doped sample the Mn{sup 2+} ions are mainly localized substitutionally at isolated tetrahedrally coordinated Zn{sup 2+} sites in both crystalline ZnO nanograins (34%) and surrounding disordered ZnO (52%). In the highly doped ZnO film, a much smaller proportion of manganese substitutes Zn{sup 2+} in the crystalline and disordered ZnO (10%). The main amount (85%) of manganese aggregates in a secondary phase as an insular-like distribution between the ZnO nanograins. The remaining Mn{sup 2+} ions (14% and 5% at low and high doping levels, respectively) are localized at isolated, six-fold coordinated sites, very likely in the disordered intergrain region. Annealing at 600 °C induced changes in the Mn{sup 2+} ions distribution, reflecting the increase of the ZnO crystallization degree, better observed in the lightly doped sample.

The crystallization and physical properties of Al-doped ZnO nanoparticles

Energy Technology Data Exchange (ETDEWEB)

Chen, K.J. [Institute of Microelectronics and Department of Electrical Engineering, Center for Micro/Nano Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan (China); Fang, T.H. [Institute of Mechanical and Electromechanical Engineering, National Formosa University, Yunlin 632, Taiwan (China); Hung, F.Y. [Institute of Nanotechnology and Microsystems Engineering, Center for Micro/Nano Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan (China)], E-mail: fyhung@mail.mse.ncku.edu.tw; Ji, L.W. [Institute of Mechanical and Electromechanical Engineering, National Formosa University, Yunlin 632, Taiwan (China); Chang, S.J.; Young, S.J. [Institute of Microelectronics and Department of Electrical Engineering, Center for Micro/Nano Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan (China); Hsiao, Y.J. [Department of Materials Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan (China)

2008-07-15

Un-doped Al (0-9 at.%) nanoparticles and doped ZnO powders were prepared by the sol-gel method. The nanoparticles were heated at 700-800 deg. C for 1 h in air and then analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), Raman spectra and photoluminescence (PL). The results of un-doped (ZnO) and Al-doped ZnO (AZO) nanoparticles were also compared to investigate the structural characteristics and physical properties. XRD patterns of AZO powders were similar to those of ZnO powders, indicating that micro-Al ions were substituted for Zn atoms and there were no variations in the structure of the ZnO nanoparticles. From the XRD and SEM data, the grain size of the AZO nanoparticles increased from 34.41 to 40.14 nm when the annealing temperature was increased. The Raman intensity of the AZO nanoparticles (Al = 5 at.%) increased when the annealing temperature was increased. Increasing the degree of crystalline not only reduced the residual stress, but also improved the physical properties of the nanoparticles.

The crystallization and physical properties of Al-doped ZnO nanoparticles

International Nuclear Information System (INIS)

Chen, K.J.; Fang, T.H.; Hung, F.Y.; Ji, L.W.; Chang, S.J.; Young, S.J.; Hsiao, Y.J.

2008-01-01

Un-doped Al (0-9 at.%) nanoparticles and doped ZnO powders were prepared by the sol-gel method. The nanoparticles were heated at 700-800 deg. C for 1 h in air and then analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), Raman spectra and photoluminescence (PL). The results of un-doped (ZnO) and Al-doped ZnO (AZO) nanoparticles were also compared to investigate the structural characteristics and physical properties. XRD patterns of AZO powders were similar to those of ZnO powders, indicating that micro-Al ions were substituted for Zn atoms and there were no variations in the structure of the ZnO nanoparticles. From the XRD and SEM data, the grain size of the AZO nanoparticles increased from 34.41 to 40.14 nm when the annealing temperature was increased. The Raman intensity of the AZO nanoparticles (Al = 5 at.%) increased when the annealing temperature was increased. Increasing the degree of crystalline not only reduced the residual stress, but also improved the physical properties of the nanoparticles

Characterization of Mn doped ZnO nanopowder

Energy Technology Data Exchange (ETDEWEB)

Schlenker, Eva; Bakin, Andrey; Al-Suleiman, Mohamed; Wehmann, Hergo-Heinrich; Waag, Andreas [Institute of Semiconductor Technology, TU Braunschweig (Germany); Schmid, Herbert; Mader, Werner [Institute for Inorganic Chemistry, University Bonn (Germany); Bremers, Heiko; Hangleiter, Andreas [Institute of Applied Physics, TU Braunschweig (Germany)

2008-07-01

In the quest of materials for spintronic applications, diluted magnetic semiconductors recently attracted much attention. The main challenge is finding a ferromagnetic material with Curie temperature T{sub c}>300 K whose magnetic properties can be controlled electrically. The interest was particularly focused on Zn(TM)O since theoretical calculations predict that ZnO containing Mn could exhibit ferromagnetism with T{sub c} above room temperature. In the present study, the structural and magnetic properties of Mn doped ZnO nanopowder are investigated and compared to undoped ZnO crystals. Doping of ZnO with Mn results in increased lattice constants as revealed by XRD. However, an inhomogeneous distribution of the Mn dopants within the nanopowder was revealed by energy-dispersive X-ray and electron energy-loss spectroscopy. Magnetic properties are investigated by means of SQUID measurements on aggregates of powder particles as well as by MFM to study the behavior of single grains. The MFM image differs significantly from the topography as imaged by AFM and suggests the existence of long-ranging magnetic signals emerging from the sample.

Suppression of temperature instability in InGaZnO thin-film transistors by in situ nitrogen doping

International Nuclear Information System (INIS)

Raja, Jayapal; Jang, Kyungsoo; Yi, Junsin; Balaji, Nagarajan

2013-01-01

We have investigated the effect of nitrogen doping on the behavior of hysteresis curve and its suppression of temperature instability in amorphous InGaZnO thin-film transistors (a-IGZO TFTs). The in situ nitrogen doping reduced the temperature induced abnormal sub threshold leakage current and traps generation. Large falling-rate (F R ) ∼ 0.26 eV V −1 , low activation energy (E a ) ∼ 0.617 eV and a small hysteresis compared to the pure a-IGZO TFTs, shows the best immunity to thermal instability. This is mainly attributed to the reduction of interface trap density and oxygen vacancies due to the passivation of defects and/dangling bonds. (paper)

Advanced properties of Al-doped ZnO films with a seed layer approach for industrial thin film photovoltaic application

International Nuclear Information System (INIS)