  1. Crystal growth and characterization of europium doped lithium strontium iodide scintillator as an ionizing radiation detector

    Science.gov (United States)

    Uba, Samuel

    High performance detectors used in the detection of ionizing radiation is critical to nuclear nonproliferation applications and other radiation detectors applications. In this research we grew and tested Europium doped Lithium Strontium Iodide compound. A mixture of lithium iodide, strontium iodide and europium iodide was used as the starting materials for this research. Congruent melting and freezing temperature of the synthesized compound was determined by differential scanning calorimetry (DSC) using a Setaram Labsys Evo DSC-DTA instrument. The melting temperatures were recorded at 390.35°C, 407.59°C and freezing temperature was recorded at 322.84°C from a graph of heat flow plotted against temperature. The synthesized material was used as the charge for the vertical Bridgeman growth, and a 6.5 cm and 7.7cm length boule were grown in a multi-zone transparent Mullen furnace. A scintillating detector of thickness 2.53mm was fabricated by mechanical lapping in mineral oil, and scintillating response and timing were obtained to a cesium source using CS-137 isotope. An energy resolution (FWHM over peak position) of 12.1% was observed for the 662keV full absorption peak. Optical absorption in the UV-Vis wavelength range was recorded for the grown crystal using a U-2900 UV/VIS Spectrophotometer. Absorption peaks were recorded at 194nm, 273nm, and 344nm from the absorbance spectrum, various optical parameters such as absorption coefficient, extinction coefficient, refractive index, and optical loss were derived. The optical band gap energy was calculated using Tauc relation expression at 1.79eV.

  2. Chloride, bromide and iodide scintillators with europium doping

    Science.gov (United States)

    Zhuravleva, Mariya; Yang, Kan

    2014-08-26

    A halide scintillator material is disclosed where the halide may comprise chloride, bromide or iodide. The material is single-crystalline and has a composition of the general formula ABX.sub.3 where A is an alkali, B is an alkali earth and X is a halide which general composition was investigated. In particular, crystals of the formula ACa.sub.1-yEu.sub.yI.sub.3 where A=K, Rb and Cs were formed as well as crystals of the formula CsA.sub.1-yEu.sub.yX.sub.3 (where A=Ca, Sr, Ba, or a combination thereof and X=Cl, Br or I or a combination thereof) with divalent Europium doping where 0.ltoreq.y.ltoreq.1, and more particularly Eu doping has been studied at one to ten mol %. The disclosed scintillator materials are suitable for making scintillation detectors used in applications such as medical imaging and homeland security.

  3. Barium iodide and strontium iodide crystals andd scintillators implementing the same

    Science.gov (United States)

    Payne, Stephen A; Cherepy, Nerine J; Hull, Giulia E; Drobshoff, Alexander D; Burger, Arnold

    2013-11-12

    In one embodiment, a material comprises a crystal comprising strontium iodide providing at least 50,000 photons per MeV. A scintillator radiation detector according to another embodiment includes a scintillator optic comprising europium-doped strontium iodide providing at least 50,000 photons per MeV. A scintillator radiation detector in yet another embodiment includes a scintillator optic comprising SrI.sub.2 and BaI.sub.2, wherein a ratio of SrI.sub.2 to BaI.sub.2 is in a range of between 0:1 A method for manufacturing a crystal suitable for use in a scintillator includes mixing strontium iodide-containing crystals with a source of Eu.sup.2+, heating the mixture above a melting point of the strontium iodide-containing crystals, and cooling the heated mixture near the seed crystal for growing a crystal. Additional materials, systems, and methods are presented.

  4. Influence of organic solvent treatment on elasticoluminescent property of europium-doped strontium aluminates

    International Nuclear Information System (INIS)

    Fujio, Yuki; Xu, Chao-Nan; Terasaki, Nao; Ueno, Naohiro

    2014-01-01

    The influence of an organic solvent treatment on elasticoluminescent (ELS) characteristics of mechanoluminescent (ML) sensor using the composite film consisting of an ELS material and epoxy resin was investigated. We used strontium aluminate doped with a small amount of europium (SrAl 2 O 4 :Eu, SAOE) as an ELS material in this study. After evaluating the ELS characteristics of the fabricated ML sensors using SAOE treated with/without various organic solvents, SAOE treated with methanol and ethanol showed lower ELS intensities than that of untreated SAOE. In contrast, the ELS response curves against strain for the ML sensors using SAOE treated with acetone and toluene, overlapped with that of untreated SAOE. From the characterization of SAOE treated with alcohols, such as methanol and ethanol, we can hypothesize that poor ELS characteristics is due to the degradation of the SAOE grain surfaces by the hydrolyze reaction of SAOE with hydroxyl group of alcohol. Thus, on the basis of the obtained results, we can conclude that the selection of organic solvent used in the preparation of SAOE film is of considerable importance in the development of ML sensor with a highly-reliable ELS characteristic. -- Highlights: • Influence of organic solution treatment on the sensing characteristics of a mechanoluminescent (ML) sensor using SrAl 2 O 4 :Eu has been investigated. • An alcohol treatment of SAOE powder has considerable effect on its ML characteristic. • There is almost no influence of acetone and toluene treatments on ML characteristics

  5. Trivalent europium-doped strontium molybdate red phosphors in white light-emitting diodes: Synthesis, photophysical properties and theoretical calculations

    International Nuclear Information System (INIS)

    Yang, W.-Q.; Liu, H.-G.; Liu, G.-K.; Lin, Y.; Gao, M.; Zhao, X.-Y.; Zheng, W.-C.; Chen, Y.; Xu, J.; Li, L.-Z.

    2012-01-01

    Eu 3+ -doped strontium molybdate red phosphors (Sr 1−x MoO 4 :Eu x (x = 0.01–0.2)) for white light-emitting diodes (LED) were synthesized by the solid-state reaction method. The fluorescent intensities of the as-prepared phosphors were remarkably improved. The excitation and emission spectra demonstrate that these phosphors can be effectively excited by the near-UV light (395 nm) and blue light (466 nm). Their emitted red light peaks are located at 613 nm, and the highest quantum yield value (η) of the as-grown red phosphor, which is 95.85%, is much higher than that of commercial red phosphor (77.53%). These red phosphors plus commercial yellow powers (1:10) were successfully packaged with the GaN-based blue chips on a piranha frame by epoxy resins. The encapsulated white LED lamps show high performance of the CIE chromaticity coordinates and color temperatures. Moreover, to explain the fluorescent spectra of these phosphors, a complete 3003 × 3003 energy matrix was successfully built by an effective operator Hamiltonian including free ion and crystal field interactions. For the first time, the fluorescent spectra for Eu 3+ ion at the tetragonal (S 4 ) Sr 2+ site of SrMoO 4 crystal were calculated from a complete diagonalization (of energy matrix) method. The fitting values are close to the experimental results.

  6. Spectral characteristics of europium-doped lead iodide

    International Nuclear Information System (INIS)

    Novosad, I.S.; Novosad, S.S.

    2013-01-01

    Optical absorption and x-ray luminescence spectra and thermally stimulated luminescence curves of a PbI 2 :EuCl 3 crystal grown by the Stockbarger method were investigated in the temperature range 85-295 K. It was presumed based on results of EPR spectral studies that the europium ions in this material existed in the divalent state and replaced matrix cations. An intense broad non-elementary band at 780 nm in addition to a weak band with a maximum in the range 512-520 nm were observed in the PbI 2 :Eu 2+ x-ray luminescence spectrum at 85 K. The intensity of the long-wavelength emission increased slightly upon increasing the crystal temperature from 85 to 130 K and was quenched in several stages upon increasing the temperature further to 220 K. The maximum shifted to 740 nm. It was proposed based on an analysis of the obtained data and results of a study of the luminescence properties of PbI 2 and PbI 2 :Mn 2+ crystals that the non-elementary emission band of the PbI 2 :Eu 2+ crystal at 780 nm could be represented as a superposition of three individual Gaussian bands with maxima near 715, 740, and 800 nm that were due to centers characteristic of the matrix and additional centers that were formed by Eu ions through association with intrinsic and dopant oxygen-containing defects, respectively. Doping PbI 2 with Eu 2+ ions did not affect the spectrum of matrix trapping levels. The nature of emission and trapping centers and luminescence excitation mechanisms of PbI 2 :Eu 2+ were discussed. (authors)

  7. Investigations of white light emitting europium doped zinc oxide nanoparticles

    International Nuclear Information System (INIS)

    Ashtaputre, S S; Nojima, A; Marathe, S K; Matsumura, D; Ohta, T; Tiwari, R; Dey, G K; Kulkarni, S K

    2008-01-01

    Europium doped zinc oxide nanoparticles have been synthesized using a chemical route. The amount of doped europium was varied which shows the changes in the photoluminescence (PL) intensity. The post synthesis annealing effect on the properties of ZnO nanoparticles has also been investigated. In general, PL is broad and a white light is emitted which originates from ZnO and the intra-4f transitions of Eu 3+ ions. The x-ray diffraction patterns do not show any Eu-related peaks for as-synthesized ZnO nanoparticles as well as for annealed samples. X-ray absorption spectroscopy reveals that europium ions are present on the surface of the core of ZnO and inside the shell of zinc hydroxide [Zn(OH 2 )] after annealing

  8. Europium-doped calcium titanate: Optical and structural evaluations

    Energy Technology Data Exchange (ETDEWEB)

    Mazzo, Tatiana Martelli; Pinatti, Ivo Mateus [INCTMN, LIEC, Departamento de Química, Universidade Federal de São Carlos, P.O. Box 676, 13565-905 São Carlos, SP (Brazil); Macario, Leilane Roberta [INCTMN, LIEC, Instituto de Química, Universidade Estadual Paulista, P.O. Box 355, 14800-900 Araraquara, SP (Brazil); Avansi, Waldir [Centro de Ciências Exatas e de Tecnologia, Departamento de Física, Universidade Federal de São Carlos, Jardim Guanabara, 13565-905 São Carlos, SP (Brazil); Moreira, Mario Lucio [Instituto de Física e Matemática, Universidade Federal de Pelotas, P.O. Box 354, Campus do Capão do Leão, 96001-970 Pelotas, RS (Brazil); Rosa, Ieda Lucia Viana, E-mail: ilvrosa@ufscar.br [INCTMN, LIEC, Departamento de Química, Universidade Federal de São Carlos, P.O. Box 676, 13565-905 São Carlos, SP (Brazil); Mastelaro, Valmor Roberto [Instituto de Física de São Carlos, Departamento de Física e Ciência dos Materiais, Universidade de São Paulo, P.O. Box 369, Av Trabalhador São Carlense 400, 13560-970 São Carlos, SP (Brazil); Varela, José Arana; Longo, Elson [INCTMN, LIEC, Instituto de Química, Universidade Estadual Paulista, P.O. Box 355, 14800-900 Araraquara, SP (Brazil)

    2014-02-05

    Highlights: • CaTiO{sub 3}:Eu{sup 3+} were obtained using low temperatures and very short reactional times. • The Eu{sup 3+} changes the local order–disorder of the [TiO{sub 6}] and [CaO{sub 12}] clusters. • Lifetime decay curves reveal two sites of symmetry of the Eu{sup 3+} in the CT matrix. • CaTiO{sub 3}:Eu{sup 3+} exhibit the strongest luminescent intensity and pure red color. -- Abstract: Pure Calcium Titanate (CT-pure) and Europium doped Calcium Titanate Ca{sub 1−x}Eu{sub x}TiO{sub 3} (x = 0.5%, 1.0% and 2.0% molar ratio of Eu{sup 3+} ions) powders were synthesized by hydrothermal microwave method (HTMW) at 140 °C for 8 min. The HTMW method appears to be an efficient method to prepare the luminescence materials using low temperatures and very short reactional times. In addition it is possible to determine specific correlations imposed by TiCl{sub 4} replacement by titanium isopropoxide [Ti(OC{sub 3}H{sub 7}){sub 4}] changing the reaction character and resulting in two different options of europium doping CT syntesis. To evaluate the influence of the structural order–disorder among the reactions and different properties of these materials, the following techniques were used for characterization. XANES spectroscopy that revealed that the introduction of Eu{sup 3+} ions into the CT lattice induces to significant changes in the local order–disorder around both, [TiO{sub 6}] and [CaO{sub 12}], complex clusters. PL spectra show Eu{sup 3+} emission lines ascribed to the Eu{sup 3+} transitions from {sup 5}D{sub 0} excited states to {sup 7}F{sub J} (J = 0, 1–4) fundamental states in CT:Eu{sup 3+} powders excited at 350 and 394 nm.

  9. Europium-Doped Lanthanum Hafnate Nanoparticles: Structure, Photoluminescence, and Radioluminescence

    Science.gov (United States)

    Wahid, Kareem; Pokhrel, Madhab; Mao, Yuanbing

    Due to their novel physical properties, nanostructured phosphors are of interest for radiation-based imaging and therapeutics. Herein, the structural and luminescent properties of europium-doped lanthanum hafnate (La2Hf2O7:xmol%Eu3+, x = 0 - 35) nanoparticles are investigated for use as scintillators. X-ray diffraction, Raman spectroscopy, and scanning electron microscopy confirm samples prepared through a combined co-precipitation and low-temperature molten salt synthetic process homogenously form spherical nanocrystals of 36 nm in the ordered pyrochlore phase. Ultraviolet and X-ray excitation of these samples induce strong red emissions in the 580 - 590 and 612 - 630 nm range corresponding to the 5D0->7 F1 magnetic dipole and 5D0->7 F2 electric dipole transitions of Eu3+. Optical response and quantum yield are optimized at 5% Eu3+; a proposed trade-off between quenching mechanisms (defect-states/cross-relaxation) and dopant concentration is discussed. Owing to their high density, large effective atomic number, and bright luminescence, these La2Hf2O7:xmol%Eu3+ nanoparticles warrant further investigation for scintillator applications. The authors thank the support from the Defense Threat Reduction Agency of the U.S. Department of Defense (award #HDTRA1- 10-1-0114).

  10. Systematic investigation and in vitro biocompatibility studies on mesoporous europium doped hydroxyapatite

    OpenAIRE

    Popa Cristina; Ciobanu Carmen; Iconaru Simona; Stan Miruna; Dinischiotu Anca; Negrila Constantin; Motelica-Heino Mikael; Guegan Regis; Predoi Daniela

    2014-01-01

    International audience; This paper reports a systematic investigation on europium doped hydroxyapatite (Eu:HAp). In this work, a set of complementary techniques Fourier Transform Infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM) and, Brunauer-Emmett-Teller (BET) technique was used to allowing a proper understanding of Eu:HAp. The XPS analysis confirmed the substitution of Ca ions by Eu ions in Eu:HAp samples. Eu:HAp and pure HAp show ...

  11. Tailoring the properties of europium-doped potassium calcium iodide scintillators through defect engineering

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Yuntao; Rutstrom, Daniel J.; Zhuravleva, Mariya; Loyd, Matthew [Scintillation Materials Research Center, University of Tennessee, Knoxville, TN (United States); Department of Materials Science and Engineering, University of Tennessee, Knoxville, TN (United States); Li, Qi [Physical Science Division, IBM Thomas J Watson Research Center, Yorktown Heights, NY (United States); Department of Computer Science, University of Illinois, Urbana-Champaign, IL (United States); Stand, Luis [Scintillation Materials Research Center, University of Tennessee, Knoxville, TN (United States); Department of Materials Science and Engineering, University of Tennessee, Knoxville, TN (United States); Bredesen Center for Interdisciplinary Research and Graduate Education, University of Tennessee, Knoxville, TN (United States); Koschan, Merry [Scintillation Materials Research Center, University of Tennessee, Knoxville, TN (United States); Melcher, Charles L. [Scintillation Materials Research Center, University of Tennessee, Knoxville, TN (United States); Department of Materials Science and Engineering, University of Tennessee, Knoxville, TN (United States); Bredesen Center for Interdisciplinary Research and Graduate Education, University of Tennessee, Knoxville, TN (United States); Departments of Nuclear Engineering, University of Tennessee, Knoxville, TN (United States)

    2018-02-15

    Codoping is an effective approach for precise control of point defects in many advanced materials, and can be used to optimize their function. This paper reports an effort toward tailoring the scintillation properties of metal halides through defect engineering. A study of aliovalent codoping of the KCaI{sub 3}:Eu{sup 2+} single-crystalline scintillators is performed, through which it is discovered that a simultaneous suppression of X-ray induced afterglow and improvement of gamma-ray energy resolution can be successfully achieved via Zr{sup 4+} codoping. The afterglow level is reduced by more than twofold with Zr{sup 4+} codoping. The energy resolution of a 5 mm cubic KCaI{sub 3}:Eu{sup 2+} sample is improved from 3.25 to 2.7% at 662 keV, and 6.5 to 5.73% at 122 keV upon Zr{sup 4+} codoping. Physical explanations for the improvements are revealed from our investigations into both the electronic structure and thermodynamics of the defects by using thermoluminescence techniques and density functional theory calculations. The codoped Zr{sup 4+} ions prefer to form interstitials acting as shallow electron traps. The {Zr_C_a+V_C_a} complex can co-exist with Zr{sub i} interstitials as shallow hole traps under certain condition, which are able to trap holes temporarily. (copyright 2017 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  12. Luminescence variations in europium-doped silicon-substituted hydroxyapatite nanobiophosphor via three different methods

    Energy Technology Data Exchange (ETDEWEB)

    Thang, Cao Xuan; Pham, Vuong-Hung, E-mail: vuong.phamhung@hust.edu.vn

    2015-07-15

    Highlights: • Europium doped silicon-substituted hydroxyapatite was synthesized by wet chemical synthesis method. • Morphology of nanoparticles depended on the synthesized method. • Photoluminescence intensity of the sample increases with the increasing of Si substitutions, Eu dopants and thermal annealing. - Abstract: This paper reports the first attempt for the synthesis of europium-doped Si-substituted hydroxyapatite (HA) nanostructure to achieve strong and stable luminescence of nanobiophosphor, particularly, by addition of different Eu dopants, Si substitutions, and application of optimum annealing temperatures of up to 1000 °C. The nanobiophosphor was synthesized by the coprecipitation, microwave, and hydrothermal methods. The nanoparticles demonstrated a nanowire to a spindle-like morphology, which was dependent on the method of synthesis. The photoluminescence (PL) intensity of the sample increases with the increase in Si substitutions and Eu dopants. The luminescent nanoparticles also showed the typical luminescence of Eu{sup 3+} centered at 610 nm, which was more efficient for the annealed Eu-doped Si-HA nanoparticles than for the as-synthesized nanoparticles. Among the different synthesis methods, the hydrothermal method reveals the best light emission represented by high PL intensity and narrow PL spectra. These results suggest the potential application of Eu-doped Si-HA in stable and biocompatible nanophosphors for light emission and nanomedicine.

  13. Europium-doped amorphous calcium phosphate porous nanospheres: preparation and application as luminescent drug carriers

    Directory of Open Access Journals (Sweden)

    Zhang Kui-Hua

    2011-01-01

    Full Text Available Abstract Calcium phosphate is the most important inorganic constituent of biological tissues, and synthetic calcium phosphate has been widely used as biomaterials. In this study, a facile method has been developed for the fabrication of amorphous calcium phosphate (ACP/polylactide-block-monomethoxy(polyethyleneglycol hybrid nanoparticles and ACP porous nanospheres. Europium-doping is performed to enable photoluminescence (PL function of ACP porous nanospheres. A high specific surface area of the europium-doped ACP (Eu3+:ACP porous nanospheres is achieved (126.7 m2/g. PL properties of Eu3+:ACP porous nanospheres are investigated, and the most intense peak at 612 nm is observed at 5 mol% Eu3+ doping. In vitro cytotoxicity experiments indicate that the as-prepared Eu3+:ACP porous nanospheres are biocompatible. In vitro drug release experiments indicate that the ibuprofen-loaded Eu3+:ACP porous nanospheres show a slow and sustained drug release in simulated body fluid. We have found that the cumulative amount of released drug has a linear relationship with the natural logarithm of release time (ln(t. The Eu3+:ACP porous nanospheres are bioactive, and can transform to hydroxyapatite during drug release. The PL properties of drug-loaded nanocarriers before and after drug release are also investigated.

  14. Characterization of photoluminescent europium doped yttrium oxide thin-films prepared by metallorganic chemical vapor deposition

    International Nuclear Information System (INIS)

    McKittrick, J.; Bacalski, C.F.; Hirata, G.A.; Hubbard, K.M.; Pattillo, S.G.; Salazar, K.V.; Trkula, M.

    1998-01-01

    Europium doped yttrium oxide, (Y 1-x Eu x ) 2 O 3 , thin-films were deposited on silicon and sapphire substrates by metallorganic chemical vapor deposition (MOCVD). The films were grown in a MOCVD chamber reacting yttrium and europium tris(2,2,6,6-tetramethyl-3,5,-heptanedionates) precursors in an oxygen atmosphere at low pressures (5 Torr) and low substrate temperatures (500--700 C). The films deposited at 500 C were flat and composed of nanocrystalline regions of cubic Y 2 O 3 , grown in a textured [100] or [110] orientation to the substrate surface. Films deposited at 600 C developed from the flat, nanocrystalline morphology into a plate-like growth morphology oriented in the [111] with increasing deposition time. Monoclinic Y 2 O 3 :Eu 3+ was observed in x-ray diffraction for deposition temperatures ≥600 C on both (111) Si and (001) sapphire substrates. This was also confirmed by the photoluminescent emission spectra

  15. Study on Europium-Doped Hydroxyapatite Nanoparticles by Fourier Transform Infrared Spectroscopy and Their Antimicrobial Properties

    Directory of Open Access Journals (Sweden)

    Simona-Liliana Iconaru

    2013-01-01

    Full Text Available Fourier transform infrared spectroscopy (FT-IR analysis was conducted on europium-doped hydroxyapatite, Ca10-xEux(PO46(OH2 nanocrystalline powders (Eu:HAp with 0≤xEu≤0.2. Antimicrobial studies were also performed for the first time on Eu:HAp. The antimicrobial properties of Eu:HAp nanoparticles with 0≤xEu≤0.2 on Gram-negative (E. coli ATCC 25922, Pseudomonas aeruginosa 1397 and Gram-positive (Staphylococcus aureus 0364, Enterococcus faecalis ATCC 29212 bacteria systems and a species of fungus (Candida albicans ATCC 10231 were reported. Our study demonstrates that the antimicrobial activity of Eu:HAp nanoparticles is dependent on the europium concentration.

  16. Synthesis, Structure, and Luminescent Properties of Europium-Doped Hydroxyapatite Nanocrystalline Powders

    International Nuclear Information System (INIS)

    Ciobanu, C.S.; Iconaru, S.L.; Predoi, D.; Massuyeau, F.; Constantin, L.V.; Costescu, A.

    2012-01-01

    The luminescent europium-doped hydroxyapatite (Eu:HAp, Ca 10-x Eu x (PO 4 ) 6 (OH) 2 ) with 0>x>0.2 nanocrystalline powders was synthesized by coprecipitation. The structural, morphological, and textural properties were well characterized by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The vibrational studies were performed by Fourier transform infrared, Raman, and photoluminescence spectroscopies. The X-ray diffraction analysis revealed that hydroxyapatite is the unique crystalline constituent of all the samples, indicating that Eu has been successfully inserted into the HAp lattice. Eu doping inhibits HAp crystallization, leading to a decrease of the average crystallite size from around 20 nm in the undoped sample to around 7 nm in the sample with the highest Eu concentration. Furthermore, the samples show the characteristic 5 D 0 → 7 F 0 transition observed at 578 nm related to Eu 3+ ions distributed on Ca 2+ sites of the apatitic structure

  17. Red light emission from europium doped zinc sodium bismuth borate glasses

    Science.gov (United States)

    Hegde, Vinod; Viswanath, C. S. Dwaraka; Upadhyaya, Vyasa; Mahato, K. K.; Kamath, Sudha D.

    2017-12-01

    Zinc sodium bismuth borate (ZNBB) glasses doped with different concentrations of europium were prepared by conventional melt quenching method and characterized through the measurements of density, refractive index, X-ray diffraction (XRD), Fourier Transform Infrared (FTIR) spectra, optical absorption, luminescence and radiative lifetimes. FTIR spectra showed seven characteristic peaks of bismuth and borate functional groups in the range of 400-1600 cm-1. The optical band gap and bonding parameters have been calculated from absorption spectra. Photoluminescence spectra recorded in the visible region with 394 nm excitation are used to calculate the Judd-Ofelt (JO) intensity parameters (Ω2 and Ω4). The JO intensity parameters have been used to calculate the radiative parameters such as branching ratio (β), stimulated emission cross-section (σse), transition probability (A) for the fluorescent level of 5D0→7F2. Decay rates through single exponential are used to calculate the lifetime (τm) of the meta-stable state 5D0 of (Eu3+ ion) these glasses. The radiative parameters measured for all these glasses show 0.7 mol% europium doped zinc sodium bismuth borate glass 5D0→7F2 transition has the potential for red laser applications. The quality of the colour emitted by the present glasses are estimated quantitatively by CIE chromaticity coordinates, which confirms the suitability of these glasses as a red emitting material for field emission technologies and LEDs.

  18. Synthesis, Structure, and Luminescent Properties of Europium-Doped Hydroxyapatite Nanocrystalline Powders

    Directory of Open Access Journals (Sweden)

    Carmen Steluta Ciobanu

    2012-01-01

    Full Text Available The luminescent europium-doped hydroxyapatite (Eu:HAp, Ca10−xEux(PO46(OH2 with 0≤x≤0.2 nanocrystalline powders was synthesized by coprecipitation. The structural, morphological, and textural properties were well characterized by X-ray diffraction, scanning electron microscopy, and transmission electron microscopy. The vibrational studies were performed by Fourier transform infrared, Raman, and photoluminescence spectroscopies. The X-ray diffraction analysis revealed that hydroxyapatite is the unique crystalline constituent of all the samples, indicating that Eu has been successfully inserted into the HAp lattice. Eu doping inhibits HAp crystallization, leading to a decrease of the average crystallite size from around 20 nm in the undoped sample to around 7 nm in the sample with the highest Eu concentration. Furthermore, the samples show the characteristic 5D0→7F0 transition observed at 578 nm related to Eu3+ ions distributed on Ca2+ sites of the apatitic structure.

  19. Modified magnetic and optical properties of manganese nanoparticles incorporated europium doped magnesium borotellurite glass

    Energy Technology Data Exchange (ETDEWEB)

    Aziz, Siti Maisarah; Sahar, M.R., E-mail: mrahim057@gmail.com; Ghoshal, S.K.

    2017-02-01

    This paper reports the modified optical and magnetic properties of europium (Eu{sup 3+}) ions doped and Manganese nanoparticles (NPs) embedded Magnesium Borotellurite glass synthesized via melt quenching method. The influence of varying Mn NPs concentrations on the magnetic, absorption and emission properties of such glass samples are determined. Stables, transparent and amorphous glasses are obtained. The observed modification of the electronic polarizability is interpreted in terms of the generation of non-bridging oxygen (NBO) and bridging oxygen (BO) in the amorphous network. TEM images manifested the growth of Mn NPs with average diameter 11±1 nm. High-resolution TEM reveals that the lattice spacing of manganese nanoparticles is 0.308 nm at (112) plane. The emission spectra revealed four prominent peaks centered at 587 nm, 610 nm, 651 nm and 700 nm assigned to the transition from {sup 5}D{sub 0} →{sup 7}F{sub J} (J=1, 2, 3, 4) states of Eu{sup 3+} ion. A significant drop in the luminescence intensity due to the incorporation of Mn NPs is ascribed to the enhanced energy transfer from the Eu{sup 3+} ion to NPs. Prepared glass systems exhibited paramagnetic behavior. - Highlights: • The europium doped magnesium borotellurite glasses embedded Mn NPs prepared using the conventional melt-quenching method. • The TEM result reveals the size of Mn NPs while its planar spacing has been determined by HRTEM. • The luminescence properties of TeO{sub 2}–B{sub 2}O{sub 3}–MgO–Eu{sub 2}O{sub 3}–Mn{sub 3}O{sub 4} glasses have been investigated as effect of Mn NPs content. • The magnetization measurement of glass sample is carried out using vibrating sample magnetometer (VSM)

  20. Size-dependent cytotoxicity of europium doped NaYF4 nanoparticles in endothelial cells

    International Nuclear Information System (INIS)

    Chen, Shizhu; Zhang, Cuimiao; Jia, Guang; Duan, Jianlei; Wang, Shuxiang; Zhang, Jinchao

    2014-01-01

    Lanthanide-doped sodium yttrium fluoride (NaYF 4 ) nanoparticles exhibit novel optical properties which make them be widely used in various fields. The extensive applications increase the chance of human exposure to these nanoparticles and thus raise deep concerns regarding their riskiness. In the present study, we have synthesized europium doped NaYF 4 (NaYF 4 :Eu 3+ ) nanoparticles with three diameters and used endothelial cells (ECs) as a cell model to explore the potential toxic effect. The cell viability, cytomembrane integrity, cellular uptake, intracellular localization, intracellular reactive oxygen species (ROS), mitochondrial membrane potential (MMP), apoptosis detection, caspase-3 activity and expression of inflammatory gene were studied. The results indicated that these nanoparticles could be uptaken into ECs and decrease the cell viability, induce the intracellular lactate dehydrogenase (LDH) release, increase the ROS level, and decrease the cell MMP in a size-dependent manner. Besides that, the cells were suffered to apoptosis with the caspase-3 activation, and the inflammation specific gene expressions (ICAM1 and VCAM1) were also increased. Our results suggest that the damage pathway may be related to the ROS generation and mitochondrial damage. The results provide novel evidence to elucidate their toxicity mechanisms and may be helpful for more rational applications of these compounds in the future. - Highlights: • NaYF 4 :Eu 3+ nanoparticles with three diameters have been synthesized. • NaYF 4 :Eu 3+ nanoparticles could be uptaken by endothelial cells (ECs). • NaYF 4 :Eu 3+ nanoparticles show a significant cytotoxicity on ECs. • The size of NaYF 4 :Eu 3+ nanoparticles may be important to their toxicology effect

  1. A microwave-assisted solution combustion synthesis to produce europium-doped calcium phosphate nanowhiskers for bioimaging applications.

    Science.gov (United States)

    Wagner, Darcy E; Eisenmann, Kathryn M; Nestor-Kalinoski, Andrea L; Bhaduri, Sarit B

    2013-09-01

    Biocompatible nanoparticles possessing fluorescent properties offer attractive possibilities for multifunctional bioimaging and/or drug and gene delivery applications. Many of the limitations with current imaging systems center on the properties of the optical probes in relation to equipment technical capabilities. Here we introduce a novel high aspect ratio and highly crystalline europium-doped calcium phosphate nanowhisker produced using a simple microwave-assisted solution combustion synthesis method for use as a multifunctional bioimaging probe. X-ray diffraction confirmed the material phase as europium-doped hydroxyapatite. Fluorescence emission and excitation spectra and their corresponding peaks were identified using spectrofluorimetry and validated with fluorescence, confocal and multiphoton microscopy. The nanowhiskers were found to exhibit red and far red wavelength fluorescence under ultraviolet excitation with an optimal peak emission of 696 nm achieved with a 350 nm excitation. Relatively narrow emission bands were observed, which may permit their use in multicolor imaging applications. Confocal and multiphoton microscopy confirmed that the nanoparticles provide sufficient intensity to be utilized in imaging applications. Copyright © 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  2. Enhancement in red emission at room temperature from europium doped ZnO nanowires by 1,10 phenanthroline-europium interface induced resonant excitations

    Directory of Open Access Journals (Sweden)

    Soumen Dhara

    2017-02-01

    Full Text Available We show that europium doped ZnO nanowires after surface modification with organic ligand, 1,10 phenanthroline (phen leads to strong red emission at 613 nm which is a characteristic emission from the atomic levels of Eu3+. Surface modification with phen leads to formation of phenanthroline-europium interface on the surface of the nanowires due to attachment of Eu3+ ions. After an optimized surface modification with phen, intensity of both the UV emission (band edge and red emission improved by two orders of magnitude at room temperature. We observed multiple energy transfer pathways to the energy levels of Eu3+ ions through the phenanthroline-europium interface, which found to be very effective to the significant enhancement of emission from the dopant Eu3+. This study shows a new insight in to the energy transfer process from phen to the europium doped ZnO system.

  3. Structural and photocatalytic properties of iron- and europium-doped TiO2 nanoparticles obtained under hydrothermal conditions

    International Nuclear Information System (INIS)

    Diamandescu, L.; Vasiliu, F.; Tarabasanu-Mihaila, D.; Feder, M.; Vlaicu, A.M.; Teodorescu, C.M.; Macovei, D.; Enculescu, I.; Parvulescu, V.; Vasile, E.

    2008-01-01

    Iron- and europium-doped (≤1 at.%) TiO 2 nanoparticles powders have been synthesized by a hydrothermal route at 200 deg. C, starting with TiCl 4 , FeCl 3 .6H 2 O and EuCl 3 .6H 2 O. The structure, morphology and optical peculiarities were investigated by means of X-ray diffraction (XRD), transmission electron microscopy (TEM), extended X-ray absorption fine structure (EXAFS), Moessbauer spectroscopy and UV-vis measurements. The photocatalytic performance was analysed in the photodegradation reaction of phenol. Rietveld refinements of XRD patterns reveal that the as-prepared samples consist in iron- and europium-doped TiO 2 in the tetragonal anatase structural shape, with particle size as low as 15 nm. By means of Moessbauer spectroscopy on both 57 Fe and 151 Eu isotopes as well as by EXAFS analyses, the presence of Fe 3+ and/or Eu 3+ ions in the nanosized powders has been evidenced. It was found that iron and europium ions can substitute for titanium in the anatase structure. From the UV-vis reflection spectra, by using the transformed Kubelka-Munk functions, the band gap energy (E g ) of the hydrothermal samples has been determined in comparison with that of Degussa P-25 photocatalyst. A decrease of E g from 2.9 eV found for Degussa photocatalyst to 2.8 eV for the titania doped with 1 at.% Fe has been evidenced, indicating a valuable absorption shift (∼20 nm) towards visible light region. However, the best photocatalytic activity in the photodegradation reaction of phenol was evidenced for the hydrothermal sample, TiO 2 : 1 at.% Fe, 0.5 at.% Eu, in both UV and visible light regions. The photocatalytic activities of iron-doped and iron-europium-codoped samples are high and practically the same only in visible light. The photocatalytic properties in correlation with the structural and optical peculiarities of the hydrothermal samples are discussed

  4. Structural and optical analysis on europium doped AZrO{sub 3} (A=Ba, Ca, Sr) phosphor for display devices application

    Energy Technology Data Exchange (ETDEWEB)

    Dubey, Vikas, E-mail: jsvikasdubey@gmail.com [Department of Physics, Bhilai Institute of Technology Raipur, 493661 (India); Tiwari, Neha [Department of Physics, Govt. Model Science College, Jabalpur (India)

    2016-05-06

    Behavior displayed by europium doped AZrO{sub 3} phosphor which was synthesized by solid state reaction method. For synthesis of BaZrO{sub 3}, SrZrO{sub 3} and CaZrO{sub 3} phosphor with fixed concentration of europium ion was calcination at 1000°C and sintered at 1300°C following intermediate grinding. Synthesized sample was characterized by X-ray diffraction analysis and crystallite sized was calculated by Scherer’s formula. From PL spectra of prepared phosphors shows intense emission centred at 612nm (red emission) with high intensity for SrZrO{sub 3}:Eu{sup 3+}. For europium doped BaZrO{sub 3} and CaZrO{sub 3} (613nm) phosphor shows less intense PL spectra as compared to SrZrO{sub 3}:Eu{sup 3+}. The strong emission peak of AZrO{sub 3}:Eu{sup 3+} phosphor is due to forced electric dipole transition of {sup 5}D{sub 0} to {sup 7}F{sub 2} centered at 612 and 613nm. It is characteristic red emission for europium ion. The excitation spectra of AZrO{sub 3}:Eu{sup 3+} phosphor mainly consists of the charge transfer and (CTB) of Eu{sup 3+} located in 200–350 nm centred at 254nm. The present phosphors can act as single host for red light emission in display devices. The CIE coordinates were calculated by Spectrophotometric method using the spectral energy distribution of the AZrO{sub 3}:Eu{sup 3+} sample.

  5. Chloride, bromide and iodide scintillators with europium

    Science.gov (United States)

    Zhuravleva, Mariya; Yang, Kan

    2016-09-27

    A halide scintillator material is disclosed where the halide may comprise chloride, bromide or iodide. The material is single-crystalline and has a composition of the general formula ABX.sub.3 where A is an alkali, B is an alkali earth and X is a halide which general composition was investigated. In particular, crystals of the formula ACa.sub.1-yEu.sub.yI.sub.3 where A=K, Rb and Cs were formed as well as crystals of the formula CsA.sub.1-yEu.sub.yX.sub.3 (where A=Ca, Sr, Ba, or a combination thereof and X=Cl, Br or I or a combination thereof) with divalent Europium doping where 0.ltoreq.y.ltoreq.1, and more particularly Eu doping has been studied at one to ten mol %. The disclosed scintillator materials are suitable for making scintillation detectors used in applications such as medical imaging and homeland security.

  6. Potassium Iodide

    Science.gov (United States)

    ... certain other liquids including low-fat white or chocolate milk, flat soda, orange juice, raspberry syrup, or ... Potassium iodide may cause side effects. Tell your doctor if any of these symptoms are severe or do not go away: swollen glands metallic taste in the ...

  7. STRONTIUM PRECIPITATION

    Science.gov (United States)

    McKenzie, T.R.

    1960-09-13

    A process is given for improving the precipitation of strontium from an aqueous phosphoric-acid-containing solution with nickel or cobalt ferrocyanide by simultaneously precipitating strontium or calcium phosphate. This is accomplished by adding to the ferrocyanide-containing solution calcium or strontium nitrate in a quantity to yield a concentration of from 0.004 to 0.03 and adjusting the pH of the solution to a value of above 8.

  8. Electro regeneration of iodide loaded resin. Contributed Paper RD-18

    International Nuclear Information System (INIS)

    Kumar, Ratnesh; Kumar, T.; Sree Kumar, B.; Seshadri, K.S.; Paul, Biplob

    2014-01-01

    Spent resins generated in the nuclear reactor contain essentially cationic activities due to Cesium, Strontium, Cobalt, and anionic activities due to Iodide, Iodate etc with activity loading to the extent of 0.1 Cim -3 and a surface dose of the order of 5 R. It is necessary to convert the spent resin into innocuous, reusable forms. An attempt has been made to regenerate Iodide containing spent resin into OH - electrolytically by using the OH - produced at the cathode compartment of an electrolytic cell. Results show that the regeneration of the spent resin containing Iodide could be completely accomplished electrolytically more efficiently than by addition of alkali. (author)

  9. dl-Alaninium iodide

    Directory of Open Access Journals (Sweden)

    Kevin Lamberts

    2012-06-01

    Full Text Available The crystal structure of dl-alanine hydroiodide (1-carboxyethanaminium iodide, C3H8NO2+·I−, is that of an organic salt consisting of N-protonated cations and iodide anions. The compound features homochiral helices of N—H...O hydrogen-bonded cations in the [010] direction; neighbouring chains are related by crystallographic inversion centers and hence show opposite chirality. The iodide counter-anions act as hydrogen-bond acceptors towards H atoms of the ammonium and carboxy groups, and cross-link the chains along [100]. Thus, an overall two-dimensional network is formed in the ab plane. No short contacts occur between iodide anions.

  10. Study of strontium and cesium migration in fractured crystalline rock

    International Nuclear Information System (INIS)

    Gustafsson, E.; Klockars, C.E.

    1984-01-01

    The purpose of this investigation has been to study the retardation and dilution of non-active strontium and cesium relative to a non-absorbing substance (iodide) in a well-defined fracture zone in the Finnsjoen field research area. The investigation was carried out in a previously tracer-tested fracture zone. The study has encompassed two separate test runs with prolonged injection of strontium and iodide and of cesium and iodide. The test have shown that: - Strontium is not retarded, but rather absorbed to about 40% at equilibrium. - At injection stop, 36.3% of the injected mass of strontium has been absorbed and there is no deabsorption. -Cesium is retarded a factor of 2-3 and absorbed to about 30% at equilibrium. - At injection stop, 39.4% of the injected mass of cesium has been absorbed. Cesium is deabsorbed after injection stop (400h) and after 1300 hours, only 22% of the injected mass of cesium is absorbed. (author)

  11. Calcium phosphate cements with strontium halides as radiopacifiers.

    Science.gov (United States)

    López, Alejandro; Montazerolghaem, Maryam; Engqvist, Håkan; Ott, Marjam Karlsson; Persson, Cecilia

    2014-02-01

    High radiopacity is required to monitor the delivery and positioning of injectable implants. Inorganic nonsoluble radiopacifiers are typically used in nondegradable bone cements; however, their usefulness in resorbable cements is limited due to their low solubility. Strontium halides, except strontium fluoride, are ionic water-soluble compounds that possess potential as radiopacifiers. In this study, we compare the radiopacity, mechanical properties, composition, and cytotoxicity of radiopaque brushite cements prepared with strontium fluoride (SrF2 ), strontium chloride (SrCl2 ·6H2 O), strontium bromide (SrBr2 ), or strontium iodide (SrI2 ). Brushite cements containing 10 wt % SrCl2 ·6H2 O, SrBr2 , or SrI2 exhibited equal to or higher radiopacity than commercial radiopaque cements. Furthermore, the brushite crystal lattice in cements that contained the ionic radiopacifiers was larger than in unmodified cements and in cements that contained SrF2 , indicating strontium substitution. Despite the fact that the strontium halides increased the solubility of the cements and affected their mechanical properties, calcium phosphate cements containing SrCl2 ·6H2 O, SrBr2 , and SrI2 showed no significant differences in Saos-2 cell viability and proliferation with respect to the control. Strontium halides: SrCl2 ·6H2 O, SrBr2 , and SrI2 may be potential candidates as radiopacifiers in resorbable biomaterials although their in vivo biocompatibility, when incorporated into injectable implants, is yet to be assessed. Copyright © 2013 Wiley Periodicals, Inc.

  12. Barium iodide and strontium iodide crystals and scintillators implementing the same

    Science.gov (United States)

    Payne, Stephen A.; Cherepy, Nerine; Pedrini, Christian; Burger, Arnold

    2016-09-13

    In one embodiment, a crystal includes at least one metal halide; and an activator dopant comprising ytterbium. In another general embodiment, a scintillator optic includes: at least one metal halide doped with a plurality of activators, the plurality of activators comprising: a first activator comprising europium, and a second activator comprising ytterbium. In yet another general embodiment, a method for manufacturing a crystal suitable for use in a scintillator includes mixing one or more salts with a source of at least one dopant activator comprising ytterbium; heating the mixture above a melting point of the salt(s); and cooling the heated mixture to a temperature below the melting point of the salts. Additional materials, systems, and methods are presented.

  13. Measurements of cesium and strontium diffusion in biotite gneiss

    International Nuclear Information System (INIS)

    Skagius, K.; Neretnieks, I.

    1988-01-01

    A significant retardation of radionuclides transported by flowing water from an underground repository can be expected if the nuclides are able to diffuse into the water filled micropores in the rock. This diffusion into the pores will also increase the surface available to interactions between the nuclides in the ground water and the rock material, such as sorption. To calculate the retardation, it is necessary to know the sorption properties and the diffusivities in the rock matrix for the radionuclides. Diffusion experiments with cesium and strontium in biotite gneiss samples have been performed. Both the transport of strontium and cesium through rock samples and the concentration profiles of cesium and strontium inside rock samples have been determined. The result shows that diffusion of cesium and strontium occurs in the rock material. A diffusion model has been used to evaluate the diffusivity. Both pore diffusion and surface diffusion had to be included in the model to give good agreement with the experimental data. If surface diffusion is not included in the model, the effective pore diffusivity that gives the best fit to the experimental data is found to be higher than expected from earlier measurement of iodide diffusion in the same type of rock material. This indicates that the diffusion of cesium and strontium (sorbing components) in rock material is caused by both pore diffusion and surface diffusion acting in parallel

  14. Diffusion measurements of cesium and strontium in biotite gneiss

    International Nuclear Information System (INIS)

    Skagius, K.; Neretnieks, I.

    1985-01-01

    A significant retardation of radionuclides transported by flowing water from an underground repository can be expected if the nuclides are able to diffuse into the water filled micropores in the rock. This diffusion into the pores will also increase the surface available to interaction between the nuclides in the groundwater and the rock material, such as sorption. To calculate the retardation it is necessary to know the sorption properties and the diffusivities in the rock matrix for the radionuclides. Diffusion experiments with cesium and strontium in biotite gneiss samples have been performed. Both the transport of strontium and cesium through rock samples and the concentration profiles of cesium and strontium inside rock samples have been determined. The result show that diffusion of cesium and strontium occurs in the rock material. A diffusion model has been used to evaluate the diffusivity. Both pore diffusion and surface diffusion had to be included in the model to give good agreement with the experimental data. If surface diffusion is not included in the model, the effective pore diffusivity that gives the best fit to the experimental data is found to be higher than expected from earlier measurements of iodide diffusion in the same type of rock material. This indicates that the diffusion of cesium and strontium (sorbing components) in rock material is caused by both pore diffusion and surface diffusion acting in parallel. (author)

  15. Potassium iodide stockpiling

    International Nuclear Information System (INIS)

    Krimm, R.W.

    1983-01-01

    After examination by the Federal Emergency Management Agency (FEMA) and other federal agencies of federal policy on the use and distribution of potassium iodide (KI) as a thyroid-blocking agent for use in off-site preparedness around commercial nuclear powerplants, FEMA believes the present shelf life of KI is too short, that the minimum ordering quantities are an obstacle to efficient procurement, and that the packaging format offered by the drug industry does not meet the wishes of state and local government officials. FEMA has asked assistance from the Food and Drug Administration in making it possible for those states wishing to satisfy appropriate requirements to do so at the minimum cost to the public. Given an appropriate packaging and drug form, there appears to be no reason for the federal government to have further involvement in the stockpiling of KI

  16. Rubidium-strontium method

    International Nuclear Information System (INIS)

    Dubansky, A.

    1980-01-01

    The rubidium-strontium geological dating method is based on the determination of the Rb and Sr isotope ratio in rocks, mainly using mass spectrometry. The method is only practical for silicate minerals and rocks, potassium feldspars and slates. Also described is the rubidium-strontium isochrone method. This, however, requires a significant amount of experimental data and an analysis of large quantities of samples, often of the order of tons. The results are tabulated of rubidium-strontium dating of geological formations in the Czech Socialist Republic. (M.S.)

  17. Photostriction of strontium ruthenate

    KAUST Repository

    Wei, Tzu-Chiao; Wang, Hsin-Ping; Liu, Heng-Jui; Tsai, Dung-Sheng; Ke, Jr-Jian; Wu, Chung-Lun; Yin, Yu-Peng; Zhan, Qian; Lin, Gong-Ru; Chu, Ying-Hao; He, Jr-Hau

    2017-01-01

    Transition metal oxides with a perovskite crystal structure exhibit a variety of physical properties associated with the lattice. Among these materials, strontium ruthenate (SrRuO3) displays unusually strong coupling of charge, spin and lattice

  18. Mercuric iodide sensor technology

    International Nuclear Information System (INIS)

    James, R.B.; Anderson, R.J.; Schlesinger, T.E.

    1996-09-01

    This report describes the improvement in the performance and the manufacturing yield of mercuric iodide detectors achieved by identifying the dominant impurities, carrier traps, and processing steps limiting device performance. Theoretical studies of electron and hole transport in this material set fundamental limits on detector performance and provided a standard against which to compare experimental results. Spectroscopy techniques including low temperature photoluminescence and thermally stimulated current spectroscopy were applied to characterize the deep level traps in this material. Traps and defects that can be introduced into the detector during growth, from the contact, and during the various steps in detector fabrication were identified. Trap energy levels and their relative abundances were determined. Variations in material quality and detector performance at the micron scale were investigated to understand the distribution in electric field in large volume detectors suitable for gamma-ray spectroscopy. Surface aging and contact degradation was studied extensively by techniques including atomic force microscopy, transmission electron microscopy, and variable angle spectroscopic ellipsometry. Preferred handling and processing procedures for maximizing detector performance and yield were established. The manufacturing yield of high resolution gamma-ray detectors was improved from a few percent to more than 30%

  19. Iodide transport and breast cancer.

    Science.gov (United States)

    Poole, Vikki L; McCabe, Christopher J

    2015-10-01

    Breast cancer is the second most common cancer worldwide and the leading cause of cancer death in women, with incidence rates that continue to rise. The heterogeneity of the disease makes breast cancer exceptionally difficult to treat, particularly for those patients with triple-negative disease. To address the therapeutic complexity of these tumours, new strategies for diagnosis and treatment are urgently required. The ability of lactating and malignant breast cells to uptake and transport iodide has led to the hypothesis that radioiodide therapy could be a potentially viable treatment for many breast cancer patients. Understanding how iodide is transported, and the factors regulating the expression and function of the proteins responsible for iodide transport, is critical for translating this hypothesis into reality. This review covers the three known iodide transporters - the sodium iodide symporter, pendrin and the sodium-coupled monocarboxylate transporter - and their role in iodide transport in breast cells, along with efforts to manipulate them to increase the potential for radioiodide therapy as a treatment for breast cancer. © 2015 Society for Endocrinology.

  20. Strontium-82/rubidium-82 generator

    International Nuclear Information System (INIS)

    Gennaro, G.P.; Haney, P.S.

    1986-01-01

    Hydroxylapatite, a compound having the formula: M 10 (PO 4 ) 6 (OH) 2 wherein M is calcium, strontium, barium, lead, iron, sodium, potassium, zinc, cadmium, magnesium, aluminium or a rare earth metal, is provided as a support medium for strontium-82 in a strontium-82/rubidium-82 parent-daughter radionuclide generator

  1. Thermoluminescence of strontium tetraborate

    International Nuclear Information System (INIS)

    Santiago, M.; Caselli, E.; Lester, M.

    1999-01-01

    The thermoluminescent properties of crystalline strontium tetraborate are reported. Without activators it has an efficiency comparable to that of TLD-700 powder. Its fading after 40 days amount to less than 2%. The isometric plot shows that most of the emitted light is concentrated at wavelengths ranging from 350 to 450 nm, which accounts partially for the high efficiency. (author)

  2. Analysis of radioactive strontium

    International Nuclear Information System (INIS)

    1977-01-01

    In environmental radiation survey, radioactive strontium has been analyzed in compliance with the manual ''Analyzing methods for radioactive strontium'' published in 1960 by the Science and Technology Agency, Japan, and revised in 1963. However, in a past decade, progress and development in analyzing methods and measuring equipments have been significant, therefore the manual was revised in 1974. Major revisions are as follows. (1) Analysis of 90 Sr with long half life was changed to the main theme and that of 89 Sr with short half life became a subordinate one. (2) Measuring criteria and sampling volume were revised. (3) Sample collection method was unified. (4) Analyzing method for soil was improved to NaOH-HCl method which has good recovery rate. (5) 90 Y separation method of simple operation was added for sea water analysis besides EDTA and fuming nitric acid methods. (6) Flame spectrometry for quantitative analysis of stable strontium was revised to atomic absorption spectrometry. The contents of the manual comprises 11 chapters describing introduction, measuring criteria for 90 Sr ( 89 Sr), rain and dust, land water, sea water, soil, sea bottom and river bottom sediments (changed from human urine and human bones), crops, milk (the previous one chapter was divided into two), marine organisms, and everyday foods, respectively. (Wakatsuki, Y.)

  3. Auger recombination in sodium iodide

    Science.gov (United States)

    McAllister, Andrew; Kioupakis, Emmanouil; Åberg, Daniel; Schleife, André

    2014-03-01

    Scintillators are an important tool used to detect high energy radiation - both in the interest of national security and in medicine. However, scintillator detectors currently suffer from lower energy resolutions than expected from basic counting statistics. This has been attributed to non-proportional light yield compared to incoming radiation, but the specific mechanism for this non-proportionality has not been identified. Auger recombination is a non-radiative process that could be contributing to the non-proportionality of scintillating materials. Auger recombination comes in two types - direct and phonon-assisted. We have used first-principles calculations to study Auger recombination in sodium iodide, a well characterized scintillating material. Our findings indicate that phonon-assisted Auger recombination is stronger in sodium iodide than direct Auger recombination. Computational resources provided by LLNL and NERSC. Funding provided by NA-22.

  4. Iodide uptake by negatively charged clay interlayers?

    Science.gov (United States)

    Miller, Andrew; Kruichak, Jessica; Mills, Melissa; Wang, Yifeng

    2015-09-01

    Understanding iodide interactions with clay minerals is critical to quantifying risk associated with nuclear waste disposal. Current thought assumes that iodide does not interact directly with clay minerals due to electrical repulsion between the iodide and the negatively charged clay layers. However, a growing body of work indicates a weak interaction between iodide and clays. The goal of this contribution is to report a conceptual model for iodide interaction with clays by considering clay mineral structures and emergent behaviors of chemical species in confined spaces. To approach the problem, a suite of clay minerals was used with varying degrees of isomorphic substitution, chemical composition, and mineral structure. Iodide uptake experiments were completed with each of these minerals in a range of swamping electrolyte identities (NaCl, NaBr, KCl) and concentrations. Iodide uptake behaviors form distinct trends with cation exchange capacity and mineral structure. These trends change substantially with electrolyte composition and concentration, but do not appear to be affected by solution pH. The experimental results suggest that iodide may directly interact with clays by forming ion-pairs (e.g., NaI(aq)) which may concentrate within the interlayer space as well as the thin areas surrounding the clay particle where water behavior is more structured relative to bulk water. Ion pairing and iodide concentration in these zones is probably driven by the reduced dielectric constant of water in confined space and by the relatively high polarizability of the iodide species. Copyright © 2015 Elsevier Ltd. All rights reserved.

  5. The evolution of hydrogen and iodine by the decomposition of ammonium iodide and hydrogen iodide

    International Nuclear Information System (INIS)

    Ishikawa, Hiroshi; Nakane, Masanori; Ishii, Eiichi; Uehara, Itsuki; Miyake, Yoshizo

    1977-01-01

    As a fundamental study on thermochemical production of hydrogen from water, the evolution of hydrogen and iodine from ammonium iodide and hydrogen iodide was investigated. Hydrogen was evolved by the reaction of nickel with ammonium iodide or with hydrogen iodide, and the resulting nickel(II) iodide was decomposed thermally at 600 -- 700 0 C to form nickel. First, the iodination of powdered nickel with ammonium iodide was studied by heating their powder mixture. The maximum yield of hydrogen was obtained at a temperature near 430 0 C. The iodination of powdered nickel with gaseous ammonium iodide or with dry hydrogen iodide gas was also investigated. In this case, coating of nickel particles with a layer of resulting nickel(II) iodide prevented further conversion of nickel and lowered the reaction rate. Such a retardation effect was appreciably lessened by use of carrier. When nickel was supported on such a carrier as ''isolite'', the nickel was converted into nickel(II) iodide easily. In a reaction temperature from 400 to 500 0 C, the rate of reaction between nickel and hydrogen iodide increased slightly with the elevation of the reaction temperature. In the case of ammonium iodide, the reaction rate was higher than that for hydrogen iodide and decreased apparently with the elevation of the reaction temperature, because ammonium iodide decomposed to ammonia and hydrogen iodide. Tests using a fixed bed reactor charged with 8 -- 10 mesh ''isolite''-nickel (30 wt%) were also carried out. The maximum yield of hydrogen was about 80% for ammonium iodide at 430 0 C of reaction temperature and 60% for hydrogen iodide at 500 0 C. (auth.)

  6. Synthesis and characterization of europium doped LiF phosphor

    Energy Technology Data Exchange (ETDEWEB)

    Villalobos, M. L.; Vallejo, M. A.; Sosa A, M. [Universidad de Guanajuato, Division de Ciencias e Ingenierias, Loma del Bosque No. 103, Lomas del Campestre, 37150 Leon, Guanajuato (Mexico); Diaz T, L. A., E-mail: villaloboscm2010@licifug.ugto.mx [Centro de Investigaciones en Optica, A. C., Loma del Bosque No. 115, Lomas del Campestre, 37150 Leon, Guanajuato (Mexico)

    2015-10-15

    LiF with different dopants has been one of the most investigated materials to use as thermoluminescent dosimeter. In this paper, we present the preparation method, the characterization and the thermoluminescent response of Eu doped LiF irradiated with X-rays. Pure and Eu doped LiF samples with different dopant concentration (0, 0.25, 0.5, 0.75 and 1 % mol) were synthesized using the precipitation method. The samples were structurally characterized by X-ray diffraction (XRD), the diffraction patterns showed a main cubic crystalline structure and a secondary hexagonal structure. The photoluminescence spectrum exhibited four well defined peaks characteristic of the Eu{sup 3+} ion. Thermoluminescent (Tl) glow curves of x-ray irradiated samples showed a well-defined single peak around 200 degrees C, except for the pure and 0.25% Eu doped samples. (Author)

  7. Iodide uptake by negatively charged clay interlayers?

    International Nuclear Information System (INIS)

    Miller, Andrew; Kruichak, Jessica; Mills, Melissa; Wang, Yifeng

    2015-01-01

    Understanding iodide interactions with clay minerals is critical to quantifying risk associated with nuclear waste disposal. Current thought assumes that iodide does not interact directly with clay minerals due to electrical repulsion between the iodide and the negatively charged clay layers. However, a growing body of work indicates a weak interaction between iodide and clays. The goal of this contribution is to report a conceptual model for iodide interaction with clays by considering clay mineral structures and emergent behaviors of chemical species in confined spaces. To approach the problem, a suite of clay minerals was used with varying degrees of isomorphic substitution, chemical composition, and mineral structure. Iodide uptake experiments were completed with each of these minerals in a range of swamping electrolyte identities (NaCl, NaBr, KCl) and concentrations. Iodide uptake behaviors form distinct trends with cation exchange capacity and mineral structure. These trends change substantially with electrolyte composition and concentration, but do not appear to be affected by solution pH. The experimental results suggest that iodide may directly interact with clays by forming ion-pairs (e.g., NaI (aq) ) which may concentrate within the interlayer space as well as the thin areas surrounding the clay particle where water behavior is more structured relative to bulk water. Ion pairing and iodide concentration in these zones is probably driven by the reduced dielectric constant of water in confined space and by the relatively high polarizability of the iodide species. - Highlights: • Iodide sorption experiments were completed with a diverse array of clay minerals. • Iodide uptake trended with CEC and swamping electrolyte identity and concentration. • Results can be explained by considering the formation of ion pairs in clay interlayers

  8. High-resolution stratigraphy with strontium isotopes.

    Science.gov (United States)

    Depaolo, D J; Ingram, B L

    1985-02-22

    The isotopic ratio of strontium-87 to strontium-86 shows no detectable variation in present-day ocean water but changes slowly over millions of years. The strontium contained in carbonate shells of marine organisms records the ratio of strontium-87 to strontium-86 of the oceans at the time that the shells form. Sedimentary rocks composed of accumulated fossil carbonate shells can be dated and correlated with the use of high precision measurements of the ratio of strontium-87 to strontium-86 with a resolution that is similar to that of other techniques used in age correlation. This method may prove valuable for many geological, paleontological, paleooceanographic, and geochemical problems.

  9. Strontium-90 - ED 4309

    International Nuclear Information System (INIS)

    Ammerich, M.; Frot, P.; Gambini, D.; Gauron, C.; Moureaux, P.; Herbelet, G.; Lahaye, T.; Le Guen, B.; Pihet, P.; Rannou, A.; Vidal, E.

    2012-12-01

    This sheet presents the characteristics of strontium-90, its origin, and its radio-physical and biological properties. It briefly describes its use in nuclear medicine. It indicates its dosimetric parameters for external exposure, cutaneous contamination, and internal exposure due to acute contamination or to chronic contamination. It indicates and comments the various exposure control techniques: ambient dose rate measurement, surface contamination measurement, atmosphere contamination. It addresses the means of protection: premise design, protection against external exposure and against internal exposure. It describes how areas are delimited and controlled within the premises: regulatory areas, controls to be performed. It addresses the personnel classification, training and medical survey. It addresses the issue of wastes and effluents. It briefly recalls the administrative procedures related to the authorization and declaration of possession and use of sealed and unsealed sources. It indicates regulatory aspects related to the transport of strontium-90, describes what is to be done in case of incident or accident (for the different types of contamination or exposure)

  10. Strontium-90 fluoride data sheet

    Energy Technology Data Exchange (ETDEWEB)

    Fullam, H.T.

    1981-06-01

    This report is a compilation of available data and appropriate literature references on the properties of strontium-90 fluoride and nonradioactive strontium fluoride. The objective of the document is to compile in a single source pertinent data to assist potential users in the development, licensing, and use of /sup 90/SrF/sub 2/-fueled radioisotope heat sources for terrestrial power conversion and thermal applications. The report is an update of the Strontium-90 Fluoride Data Sheet (BNWL-2284) originally issued in April 1977.

  11. 21 CFR 172.375 - Potassium iodide.

    Science.gov (United States)

    2010-04-01

    ... Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND HUMAN SERVICES (CONTINUED) FOOD FOR HUMAN CONSUMPTION (CONTINUED) FOOD ADDITIVES PERMITTED FOR DIRECT ADDITION TO FOOD FOR HUMAN CONSUMPTION Special Dietary and Nutritional Additives § 172.375 Potassium iodide. The food additive potassium iodide may be...

  12. Interaction of simple indium iodides with silver- and aluminium iodides

    International Nuclear Information System (INIS)

    Denisov, Yu.N.; Halova, N.S.; Fedorov, P.I.

    1976-01-01

    Fusibility diagrams of the systems InI-AlI 3 , InI-AgI, InI 2 -AgI, and InI 2 -AlI 3 have been studied. In the system InI-AlI 3 a compound InAlI 4 has been detected having a melting point 194 deg C and two lamination regions. In the system InI-AgI two compounds In 2 AgI 3 and InAgI 2 are formed which melt incongruently at 272 deg and 220 deg C, respectively. The formation of the compounds has been confirmed by X-ray phase analysis. Specific electroconductivity of a number of alloys of the system InI-AlI 3 has been studied. The systems of eutectic type formed by diiodide of indium with iodides of silver and aluminium have been studied by thermal and X-ray analysis and by measuring electroconductivity

  13. Double photoionization of strontium

    Energy Technology Data Exchange (ETDEWEB)

    Sokell, Emma; Grimm, Michael; Sheridan, Paul, E-mail: emma.sokell@ucd.i [School of Physics, University College Dublin, Belfield, Dublin 4 (Ireland)

    2010-02-01

    Resonant triple-differential cross-section (TDCS) measurements have been used to study the double photoionization process in strontium. Two sets of measurements were made at the photon energy of the 4p {yields} 4d resonance. The coplanar geometry was used and the fixed analyser, positioned at -90{sup 0} to the main axis of polarization of the photons, detected electrons with {approx}65% of the available excess energy. The mutual angle between the two electrons had a range just short of 90 {yields} 270{sup 0}. The TDCS exhibit unexpected lobes at a mutual angle of 180{sup 0}. Comparison with other measurements made with the same geometry but with different sharings of the available energy indicate that these TDCS all show the unexpected lobe. Some possible explanations for the lobe are considered.

  14. Isotope exchange of strontium and molybdate ions in strontium polymolybdates

    International Nuclear Information System (INIS)

    Atun, G.

    2002-01-01

    The heterogeneous isotopic exchange reactions in strontium polymolybdates of Sr 2+ and MoO 4 2- ions in the strontium nitrate and sodium molybdate solutions have been studied using 90 Sr and 99 Mo as tracers. Electrometric methods have been used to study the compositions of strontium molybdates obtained by adding strontium chloride to a progressively acidified solution of sodium molybdate. It has been found that the exchange fraction increases with increasing chain length of strontium polymolybdate. The exchange equilibrium constant (K ex ) has been calculated between 298 and 348 K as well as ΔG deg, ΔH deg and ΔS deg. The results indicate that Sr 2+ cations have a much higher affinity for exchangers than MoO 4 2- anions. By fitting the data to the Dubinin-Radushkevich (D-R) isotherm it has been shown that the exchange capacity (X m ) for both ions is affected by the ion adsorption process at low temperatures and by the ion exchange process at high temperatures. At high concentrations, the recrystallization process contributes to on the cation exchange but is ineffective on the anion exchange mechanism. (author)

  15. Dynamic iodide trapping by tumor cells expressing the thyroidal sodium iodide symporter

    International Nuclear Information System (INIS)

    Dingli, David; Bergert, Elizabeth R.; Bajzer, Zeljko; O'Connor, Michael K.; Russell, Stephen J.; Morris, John C.

    2004-01-01

    The thyroidal sodium iodide symporter (NIS) in combination with various radioactive isotopes has shown promise as a therapeutic gene in various tumor models. Therapy depends on adequate retention of the isotope in the tumor. We hypothesized that in the absence of iodide organification, isotope trapping is a dynamic process either due to slow efflux or re-uptake of the isotope by cells expressing NIS. Iodide efflux is slower in ARH-77 and K-562 cells expressing NIS compared to a thyroid cell line. Isotope retention half times varied linearly with the number of cells expressing NIS. With sufficient NIS expression, iodide efflux is a zero-order process. Efflux kinetics in the presence or absence of perchlorate also supports the hypothesis that iodide re-uptake occurs and contributes to the retention of the isotope in tumor cells. Iodide organification was insignificant. In vivo studies in tumors composed of mixed cell populations confirmed these observations

  16. Kinetic Isotope Effects in the Reduction of Methyl Iodide

    DEFF Research Database (Denmark)

    Holm, Torkil

    1999-01-01

    a Grignard reagent to methyl iodide, and for reduction of methyl iodide with tributyltin hydride or with gaseous hydrogen iodide. Very small KIE's were found for electron transfer to methyl iodide from magnesium in ether or from sodium in ammonia. The reason may be that these reactions are transport...

  17. Polymeric strontium ranelate nonahydrate

    Directory of Open Access Journals (Sweden)

    Kenny Stahl

    2011-04-01

    Full Text Available The title compound, poly[[μ-aqua-tetraaqua{μ-5-[bis(carboxylatomethylamino]-3-carboxylatomethyl-4-cyanothiophene-2-carboxylato}distrontium(II] tetrahydrate], [Sr2(C12H6N2O8S(H2O5]·3.79H2O, crystallizes with nine- and eight-coordinated Sr2+ cations. They are bound to seven of the eight ranelate O atoms and five of the water molecules. The SrO8 and SrO9 polyhedra are interconnected by edge-sharing, forming hollow layers parallel to (011. The layers are, in turn, interconnected by ranelate anions, forming a metal–organic framework (MOF structure with channels along the a axis. The four water molecules not coordinated to strontium are located in these channels and hydrogen bonded to each other and to the ranelates. Part of the water H atoms are disordered. The compound dehydrates very easily and 0.210 (4 water molecules out of nine were lost during crystal mounting causing additional disorder in the water structure.

  18. Photostriction of strontium ruthenate

    KAUST Repository

    Wei, Tzu-Chiao

    2017-04-24

    Transition metal oxides with a perovskite crystal structure exhibit a variety of physical properties associated with the lattice. Among these materials, strontium ruthenate (SrRuO3) displays unusually strong coupling of charge, spin and lattice degrees of freedom that can give rise to the photostriction, that is, changes in the dimensions of material due to the absorption of light. In this study, we observe a photon-induced strain as high as 1.12% in single domain SrRuO3, which we attribute to a nonequilibrium of phonons that are a result of the strong interaction between the crystalline lattice and electrons excited by light. In addition, these light-induced changes in the SrRuO3 lattice affect its electrical resistance. The observation of both photostriction and photoresistance in SrRuO3 suggests the possibility of utilizing the mechanical and optical functionalities of the material for next-generation optoelectronics, such as remote switches, light-controlled elastic micromotors, microactuators and other optomechanical systems.

  19. Methyl Iodide Decomposition at BWR Conditions

    International Nuclear Information System (INIS)

    Pop, Mike; Bell, Merl

    2012-09-01

    Based on favourable results from short-term testing of methanol addition to an operating BWR plant, AREVA has performed numerous studies in support of necessary Engineering and Plant Safety Evaluations prior to extended injection of methanol. The current paper presents data from a study intended to provide further understanding of the decomposition of methyl iodide as it affects the assessment of methyl iodide formation with the application of methanol at BWR Plants. This paper describes the results of the decomposition testing under UV-C light at laboratory conditions and its effect on the subject methyl iodide production evaluation. The study as to the formation and decomposition of methyl iodide as it is effected by methanol addition is one phase of a larger AREVA effort to provide a generic plant Safety Evaluation prior to long-term methanol injection to an operating BWR. Other testing phases have investigated the compatibility of methanol with fuel construction materials, plant structural materials, plant consumable materials (i.e. elastomers and coatings), and ion exchange resins. Methyl iodide is known to be very unstable, typically preserved with copper metal or other stabilizing materials when produced and stored. It is even more unstable when exposed to light, heat, radiation, and water. Additionally, it is known that methyl iodide will decompose radiolytically, and that this effect may be simulated using ultra-violet radiation (UV-C) [2]. In the tests described in this paper, the use of a UV-C light source provides activation energy for the formation of methyl iodide. Thus is similar to the effect expected from Cherenkov radiation present in a reactor core after shutdown. Based on the testing described in this paper, it is concluded that injection of methanol at concentrations below 2.5 ppm in BWR applications to mitigate IGSCC of internals is inconsequential to the accident conditions postulated in the FSAR as they are related to methyl iodide formation

  20. Prevention of organic iodide formation in BWR's

    International Nuclear Information System (INIS)

    Karjunen, T.; Laitinen, T.; Piippo, J.; Sirkiae, P.

    1996-01-01

    During an accident, many different forms of iodine may emerge. Organic iodides, such as methyl iodide and ethyl iodide, are relatively volatile, and thus their appearance leads to increased concentration of gaseous iodine. Since organic iodides are also relatively immune to most accident mitigation measures, such as sprays and filters, they can affect the accident source term significantly even when only a small portion of iodine is in organic form. Formation of organic iodides may not be limited by the amount of organic substances available. Excessive amounts of methane can be produced, for example, during oxidation of boron carbide, which is used in BWR's as a neutron absorber material. Another important source is cable insulation. In a BWR, a large quantity of cables is placed below the pressure vessel. Thus a large quantity of pyrolyse gases will be produced, should the vessel fail. Organic iodides can be formed as a result of many different reactions, but at least in certain conditions the main reaction takes place between an organic radical produced by radiolysis and elemental iodine. A necessary requirement for prevention of organic iodide production is therefore that the pH in the containment water pools is kept high enough to eliminate formation of elemental iodine. In a typical BWR the suppression pool water is usually unbuffered. As a result, the pH may be dominated by chemicals introduced during an accident. If no system for adding basic chemicals is operable, the main factor affecting pool water pH may be hydrochloric acid released during cable degradation. Should this occur, the conditions could be very favorable for production of elemental iodine and, consequently, formation of organic iodides. Although high pH is necessary for iodine retention, it could have also adverse effects. High pH may, for example, accelerate corrosion of containment materials and alter the characteristics of the solid corrosion products. (author) 6 figs., 1 tab., 13 refs

  1. In Vitro Bioavailability Study of an Antiviral Compound Enisamium Iodide

    OpenAIRE

    Eleonore Haltner-Ukomadu; Svitlana Gureyeva; Oleksii Burmaka; Andriy Goy; Lutz Mueller; Grygorii Kostyuk; Victor Margitich

    2018-01-01

    An investigation into the biopharmaceutics classification and a study of the in vitro bioavailability (permeability and solubility) of the antiviral compound enisamium iodide (4-(benzylcarbamoyl)-1-methylpyridinium iodide) were carried out. The solubility of enisamium iodide was determined in four different buffers. Apparent intestinal permeability (Papp) of enisamium iodide was assessed using human colon carcinoma (Caco-2) cells at three concentrations. The solubility of enisamium iodide in ...

  2. Strontium 90 fallout prediction

    International Nuclear Information System (INIS)

    Sarmiento, J.L.; Gwinn, E.

    1986-01-01

    An empirical formula is developed for predicting monthly sea level strontium 90 fallout (F) in the northern hemisphere as a function of time (t), precipitation rate (P), latitude (phi), longitude (lambda), and the sea level concentration of stronium 90 in air (C): F(lambda, phi, t) = C(t, phi)[v /sub d/(phi) + v/sub w/(lambda, phi, t)], where v/sub w/(lambda, phi, t) = a(phi)[P(lambda, phi, t)/P/sub o/]/sup b//sup (//sup phi//sup )/ is the wet removal, v/sub d/(phi) is the dry removal and P 0 is 1 cm/month. The constants v/sub d/, a, and b are determined as functions of latitude by fitting land based observations. The concentration of 90 Sr in air is calculated as a function of the deseasonalized concentration at a reference latitude (C-bar/sub r//sub e//sub f/), the ratio of the observations at the latitude of interest to the reference latitude (R), and a function representing the seasonal trend in the air concentration (1 + g): C-bar(t, phi) = C/sub r//sub e//sub f/(t)R(phi)[1 + g(m, phi)]; m is the month. Zonal trends in C are shown to be relatively small. This formula can be used in conjuction with precipitation observations and/or estimates to predict fallout in the northern hemisphere for any month in the years 1954 to 1974. Error estimates are given; they do not include uncertainty due to errors in precipitation data

  3. Immobilisation of strontium, nickel and iodide by a sulphate-resisting Portland cement

    International Nuclear Information System (INIS)

    Wieland, E.; Tits, J.; Spieler, P.; Dobler, J.-P.

    1998-01-01

    The interaction of Sr(II), Ni(II) and I(-I) with sulphate-resisting Portland cement was investigated under highly alkaline conditions. Batch-sorption studies were performed by contacting HTS cement (haute teneur en silice, sulphate-resisting Portland cement, Lafarge, France) with artificial cement pore water (ACW). The composition of ACW was 0.18 M KOH, 0.114 M NaOH and 1.2 mM Ca(OH) 2 . 85 Sr, 63 Ni and 125 I were used as tracers. In the experiments with Sr(II) and Ni(II), isosaccharinic acid (ISA) was added to ACW at 10 -5 M to 10 -2 M in order to study the effect of complexing ligands on radionuclide retention. The stability of the tracer solutions and the cement suspensions were first assessed. Moreover, the inventory of the stable elements were determined in cement and cement pore water. We then studied the kinetics of the radionuclide-cement interaction process and measured the dependence of the distribution ratio (R d ) on the concentration of ISA and on the concentration of cement particles (S:L ratio). In the case of 63 Ni and 125 I a strong decrease in the distribution ratio (R d ) with increasing S:L ratio was observed. There is strong indication that the inventory of the stable fraction of an element present in cement pore water accounts for the retention of the radioisotope fraction. The results further indicate that phase transformations may occur in non-pre-equilibrated cement systems (non-equilibrium conditions) which affect 63 Ni uptake by HTS cement. The distribution ratios measured on HTS cement were compared with values obtained from measurements on important cement components (portlandite, CSH/C(A)SH-phases)

  4. Method to remove methyl iodide131 gas

    International Nuclear Information System (INIS)

    Deitz, V.R.; Blachly, C.H.

    1977-01-01

    A two-stage impregnation process for charcoal is presented which is to be used for radioactive iodine or methyl iodide removal from the waste gas of a nuclear reactor. In the first stage, the coal is treated at pH 10 with an aqueous mixture of a salt of iodic acid (hypoiodite, iodate, or periodate) with iodine or iodide. In the second stage, impregnation with a tertiary amine occurs. The concentrations are chosen so that the charcoal will take up between 0.5 and 4% by weight of iodine. (UWI) [de

  5. Factors affecting the retention of methyl iodide by iodide-impregnated carbon

    International Nuclear Information System (INIS)

    Hyder, M.L.; Malstrom, R.A.

    1991-01-01

    This paper comprises two sets of studies of methyl iodide retention by iodide-impregnated carbon. In the first of these, the retention of the methyl iodide on the carbon surface and its subsequent evolution were observed directly by a technique of combustion and phosphorescence. In the second, the methyl iodide retention in a standard test was compared with surface area measurements and the concentration of unreacted iodine. A correlation among these parameters was identified and characterized. Carbon quality was varied through the selection of used material with differing service histories. Air from the Savannah River Site reactor buildings is vented through carbon beds for control of radioiodine before release to the atmosphere. The carbon used is North American Carbon Co. type GX-176 coconut shell carbon impregnated with 1% triethylenedimaine (TEDA) and 2% potassium iodide by weight. Replacement intervals for the carbon have been as long as thirty months. Analysis of samples withdrawn at much shorter times has shown that the TEDA is lost after a few months, and the performance of the carbon for methyl iodide retention is dependent on the iodide impregnant. Efficient methyl iodide retention is not a requirement for carbon in this service; however, methyl iodide retention as measured by the ASTM Test D3803 (method B) has been found to correlate well with other desirable properties of the carbon such as radiation stability. The studies undertaken here were intended to shed light on the changes taking place in this carbon during long-term service and to provide a basis for simpler measurements of carbon quality

  6. Simulating the Transfer of Strontium-90 from Soil to Leafy Vegetables by Using Strontium-88

    OpenAIRE

    Kuke, Ding; Shujuan, Liu; Yingxue, He; Dong, Yan; Fengshou, Zhang; Shuifeng, Wang; Jinghua, Guo; Wei, Zhang; Xin, Wang; Xiaoyan, Jiang

    2016-01-01

    The transfer, from soil to Chinese cabbage and spinach, of radioactive strontium-90 released as a result of accidents in nuclear power stations was studied using a stable isotope of strontium, namely nuclide strontium-88 (88Sr). The study led to an experimental model for assessing the hazard of radionuclide strontium-90 (90Sr) entering the food chain and for predicting the risk to food safety. Chinese cabbage and spinach were grown in pots in a greenhouse and irrigated with deionized water co...

  7. Combined transuranic-strontium extraction process

    Science.gov (United States)

    Horwitz, E. Philip; Dietz, Mark L.

    1992-01-01

    The transuranic (TRU) elements neptunium, plutonium and americium can be separated together with strontium from nitric acid waste solutions in a single process. An extractant solution of a crown ether and an alkyl(phenyl)-N,N-dialkylcarbanylmethylphosphine oxide in an appropriate diluent will extract the TRU's together with strontium, uranium and technetium. The TRU's and the strontium can then be selectively stripped from the extractant for disposal.

  8. Ion exchange of strontium on synthetic hydroxyapatite

    International Nuclear Information System (INIS)

    Lazic, S.; Vukovic, Z.

    1991-01-01

    Adsorption of strontium ions on synthetic hydroxyapatite was examined using both batch and column methods. The apatite was prepared from aqueous solutions and characterized by standard analytical methods. The sample obtained had characteristics of well crystallized stoichiometric hydroxyapatite. The experimental data for sorption of strontium can be very well fitted with Langmuir's adsorption isotherm. It was found that sorption occurs by an ion exchange reaction between strontium ions in solution and calcium ions in apatite. (author) 14 refs.; 5 figs.; 1 tab

  9. Kinetics of strontium sorption in calcium phosphate

    International Nuclear Information System (INIS)

    Bacic, S.; Komarov, V.F.; Vukovic, Z.

    1989-01-01

    Kinetics of strontium sorption by highly dispersed solids: tricalcium phosphate (Ca 3 (PO 4 ) 2 , TCP) and hydroxyapatite (Ca 5 (PO 4 ) 3 )H, HAP) were investigated. Analysis of sorption data was made taking into consideration composition and morphology of ultra micro particles. Conclusion is that the isomorphous strontium impurity is structurally sensitive element for calcium phosphate. It was determined that the beginning of strontium desorption corresponds to the beginning of transformation of the TCP - HAP (author)

  10. Strontium sorption on Savannah River Plant soils

    International Nuclear Information System (INIS)

    Hoeffner, S.L.

    1984-12-01

    A laboratory study of strontium-85 sorption was conducted using Savannah River Plant soil and groundwater from the low-level waste burial ground. Systematic variation of soil and water composition indicates that strontium sorption is most strongly a function of pH. Changes in clay content and in K + , Ca 2+ , or Mg 2+ concentrations influence strontium sorption indirectly through the slight pH changes which result. The ions Na + , Cl - , and NO 3 - have no effect. Ferrous ion, added to groundwater to simulate the conditions of water at the bottom of waste trenches, did not account for low strontium sorption observed with some trench waters

  11. Optimization of a Strontium Aluminate

    Energy Technology Data Exchange (ETDEWEB)

    Bone, Alexandria N. [Maryville College, TN (United States)

    2017-08-01

    Strontium aluminate with Eu2+ and Dy3+ has been at the forefront of emerging applications for storage phosphors since its discovery in 1996. In this study, the emission intensity and luminescence lifetime of SrAl2O4: Eu2+, Dy3+ were enhanced by partial substitution of Ca2+ into Sr2+ sites in the matrix.

  12. Potassium iodide capsule treatment of feline sporotrichosis.

    Science.gov (United States)

    Reis, Erica G; Gremião, Isabella D F; Kitada, Amanda A B; Rocha, Raphael F D B; Castro, Verônica S P; Barros, Mônica B L; Menezes, Rodrigo C; Pereira, Sandro A; Schubach, Tânia M P

    2012-06-01

    Sporotrichosis is a mycosis caused by Sporothrix schenckii. The most affected animal is the cat; it has played an important role in the zoonotic transmission of this disease, especially in Rio de Janeiro, Brazil, since 1998. In order to evaluate the treatment of feline sporotrichosis with potassium iodide, an observational cohort was conducted in 48 cats with sporotrichosis at Instituto de Pesquisa Clínica Evandro Chagas, Fiocruz. All cats received potassium iodide capsules, 2.5 mg/kg to 20 mg/kg q24h. The cure rate was 47.9%, treatment failure was 37.5%, treatment abandonment was 10.4% and death was 4.2%. Clinical adverse effects were observed in 52.1% of the cases. Thirteen cats had a mild increase in hepatic transaminase levels during the treatment, six of them presented clinical signs suggestive of hepatotoxicity. Compared to previous studies with itraconazole and iodide in saturated solution, potassium iodide capsules are an alternative for feline sporotrichosis treatment.

  13. Potentiometric determination of iodides in urine

    International Nuclear Information System (INIS)

    Gikolaev, B.A.; Primakova, L.N.; Rakhman'ko, E.M.

    1996-01-01

    Variants of potentiometric method: determination using a calibrations plot, the Gran method, and the double addition method are considered. The method of double additions of the test solution to the reference one is suggested as the most favorable method of determining iodides in urine under clinical laboratory conditions. Refs. 5, tabs. 2

  14. Inclusion complexation of tetrabutylammonium iodide by cyclodextrins

    Indian Academy of Sciences (India)

    Biswajit Datta

    Host-guest inclusion complex of an ionic solid (tetrabutyl ammonium iodide) with α- and β- cyclodextrin has been ... tions.2 CDs are cyclic oligomer of α-D-glucose having numerous of ... of locating at the interface of two phases (liquid–liquid.

  15. Developments in mercuric iodide gamma ray imaging

    Energy Technology Data Exchange (ETDEWEB)

    Patt, B E; Beyerle, A G; Dolin, R C; Ortale, C [EG and G Energy Measurements, Inc., Goleta, CA (USA). Santa Barbara Operations

    1989-11-01

    A mercuric iodide (HgI{sub 2}) gamma ray imaging array and camera system previously described have been characterized for spatial and energy resolution. Based on these data a new camera is being developed to more fully exploit the potential of the array. Characterization results and design criteria for the new camera will be presented. (orig.).

  16. 21 CFR 184.1265 - Cuprous iodide.

    Science.gov (United States)

    2010-04-01

    ... the following specific limitations: Category of food Maximum treatment level in food Functional use... 21 Food and Drugs 3 2010-04-01 2009-04-01 true Cuprous iodide. 184.1265 Section 184.1265 Food and Drugs FOOD AND DRUG ADMINISTRATION, DEPARTMENT OF HEALTH AND HUMAN SERVICES (CONTINUED) FOOD FOR HUMAN...

  17. Iodide-trapping defect of the thyroid

    International Nuclear Information System (INIS)

    Pannall, P.R.; Steyn, A.F.; Van Reenen, O.

    1978-01-01

    We describe a grossly hypothyroid 50-year-old woman, mentally retarded since birth. On the basis of her history of recurrent goitre, absence of 131 I neck uptake and a low saliva/plasma 131 I ratio, congenital hypothyroidism due to a defect of the iodide-trapping mechanism was diagnosed. Other family members studied did not have the defect

  18. Electrosorption of tetraalkylammonium ions on silver iodide

    NARCIS (Netherlands)

    Keizer, de A.

    1981-01-01

    The object of the present investigations was to study the ef fect of the adsorption of charged organic ions on electrically charged, solid-liquid interfaces. To that end, symmetrical quater nary ammonium ions were adsorbed on a silver iodide-electrolyte interface at various

  19. Electronic and optical properties of lead iodide

    DEFF Research Database (Denmark)

    Ahuja, R.; Arwin, H.; Ferreira da Silva, A.

    2002-01-01

    The electronic properties and the optical absorption of lead iodide (PbI2) have been investigated experimentally by means of optical absorption and spectroscopic ellipsometry, and theoretically by a full-potential linear muffin-tin-orbital method. PbI2 has been recognized as a very promising...

  20. Vapor pressure of selected organic iodides

    Czech Academy of Sciences Publication Activity Database

    Fulem, M.; Růžička, K.; Morávek, P.; Pangrác, Jiří; Hulicius, Eduard; Kozyrkin, B.; Shatunov, V.

    2010-01-01

    Roč. 55, č. 11 (2010), 4780-4784 ISSN 0021-9568 R&D Projects: GA ČR GA203/08/0217 Institutional research plan: CEZ:AV0Z10100521 Keywords : vapor pressure * static method * organic iodides Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.089, year : 2010

  1. Electrochemical reaction rates in a dye sentisised solar cell - the iodide/tri-iodide redox system

    DEFF Research Database (Denmark)

    Bay, Lasse; West, Keld; Winter-Jensen, Bjørn

    2006-01-01

    The electrochemical reaction rate of the redox couple iodide / tri-iodide in acetonitrile is characterised by impedance spectroscopy. Different electrode materials relevant for the function of dye-sensitised solar cells (DSSC) are investigated. Preferably, the reaction with the iodide / tri......-iodide couple should be fast at the counter electrode, i.e. this electrode must have a high catalytic activity towards the redox couple, and the same reaction must be slow on the photo electrode. The catalytic activity is investigated for platinum, poly(3,4-ethylenedioxythiophene) (PEDOT), polypyrrole (PPy......), and polyaniline (PANI) - all deposited onto fluorine doped tin oxide (FTO) glass. Both Pt and PEDOT are found to have sufficiently high catalytic activities for practical use as counter electrode in DSSC. The reaction resistance on FTO and anatase confirmed the beneficial effect of a compact anatase layer on top...

  2. Simulating the Transfer of Strontium-90 from Soil to Leafy Vegetables by Using Strontium-88.

    Science.gov (United States)

    Kuke, Ding; Shujuan, Liu; Yingxue, He; Dong, Yan; Fengshou, Zhang; Shuifeng, Wang; Jinghua, Guo; Wei, Zhang; Xin, Wang; Xiaoyan, Jiang

    The transfer, from soil to Chinese cabbage and spinach, of radioactive strontium-90 released as a result of accidents in nuclear power stations was studied using a stable isotope of strontium, namely nuclide strontium-88 ( 88 Sr). The study led to an experimental model for assessing the hazard of radionuclide strontium-90 ( 90 Sr) entering the food chain and for predicting the risk to food safety. Chinese cabbage and spinach were grown in pots in a greenhouse and irrigated with deionized water containing known quantities of strontium. Based on the strontium content of that water, the plants were divided into five groups (treatments) and strontium content of the soil, and 30-day-old plants were determined by inductively coupled plasma atomic emission spectroscopy instrument (ICP-AES). Data on the strontium content of soil and plants enabled the development of a model using MATLAB, a mathematical software package, which included curve fitting and problem solving using regression equations and differential equations. Although strontium curves for leaves, stems, and roots of Chinese cabbage were not exactly the same, all showed a non-linear increase when compared with the increase in the content of strontium in soil. Strontium curves for leaves, stems, and roots of spinach were very similar and showed an initial increase followed by a decrease. Strontium concentrations in both Chinese cabbage and spinach were initially related to the concentrations of sodium and sulfur, the next two relevant nuclides being calcium and magnesium. The relationship between calcium and strontium in Chinese cabbage was different from that in spinach. By using 88 Sr to simulate the transfer of radionuclide 90 Sr from soil to a crop, the relevant data required to deal with accidental release of strontium can be obtained using a fitting curve and regression equations, thereby providing some experimental basis for evaluating the potential hazards posed by such accidents to the food chain.

  3. Strontium 90 in Swedish dairy milk 1978

    International Nuclear Information System (INIS)

    Gillberg-Wickman, M.; Oestergren, I.

    1980-01-01

    The contamination of strontium-90 in Swedish milk during 1978 is practically the same as in 1977. The country-wide mean ratio of strontium-90 to calcium in milk is 0.12 Bq 90 Sr(gCa) -1 , based on monthly determinations of samples obtained from 8 dairy plants situated throughout the country. (author)

  4. Iodide adsorption on the surface of chemically pretreated clinoptilolite

    International Nuclear Information System (INIS)

    Chmielewska-Horvatova, E.; Lesny, J.

    1995-01-01

    The possibility to use the monoionic Ag +- form (eventually Hg +- and Hg 2+ -forms) of clinoptilolite of domestic origin for radioactive iodide elimination from waters has been studied. The capacity of the monoforms of clinoptilolite towards iodide exceeds many times that of the capacity of clinoptilolite in natural form. Due to the low solubility product of AgI, Hg 2 I 2 and HgI 2 iodides generate precipitates on the zeolite surface. Rtg analyses of the silver form of clinoptilolite after sorption of iodide demonstrate the formation of new crystals on the zeolite surface. The influence of interfering anions on the adsorption capacity of silver clinoptilolite towards iodide was investigated, too. Kinetic curves of iodide desorption from the surface of silver and mercury clinoptilolite were compared. Simultaneously, adsorption isotherms for the systems aqueous iodide solution/Ag-, Hg-clinoptilolite were determined. (author) 6 refs.; 7 figs.; 4 tabs

  5. Removal efficiency of water purifier and adsorbent for iodine, cesium, strontium, barium and zirconium in drinking water.

    Science.gov (United States)

    Sato, Itaru; Kudo, Hiroaki; Tsuda, Shuji

    2011-01-01

    The severe incident of Fukushima Daiichi Nuclear Power Station has caused radioactive contamination of environment including drinking water. Radioactive iodine, cesium, strontium, barium and zirconium are hazardous fission products because of the high yield and/or relatively long half-life. In the present study, 4 pot-type water purifiers and several adsorbents were examined for the removal effects on these elements from drinking water. Iodide, iodate, cesium and barium were removed by all water purifiers with efficiencies about 85%, 40%, 75-90% and higher than 85%, respectively. These efficiencies lasted for 200 l, which is near the recommended limits for use of filter cartridges, without decay. Strontium was removed with initial efficiencies from 70% to 100%, but the efficiencies were slightly decreased by use. Zirconium was removed by two models, but hardly removed by the other models. Synthetic zeolite A4 efficiently removed cesium, strontium and barium, but had no effect on iodine and zirconium. Natural zeolite, mordenite, removed cesium with an efficiency as high as zeolite A4, but the removal efficiencies for strontium and barium were far less than those of zeolite A4. Activated carbon had little removal effects on these elements. In case of radioactive contamination of tap water, water purifiers may be available for convenient decontamination of drinking water in the home.

  6. Complex crystals formed in the aqueous solution of copper(I) iodide and sodium iodide

    International Nuclear Information System (INIS)

    Sugasaka, Kazuhiko; Fujii, Ayako

    1977-01-01

    Crystals of different crystal habits were separated from the copper(I) iodide and sodium iodide solution and the thermal changes of the composition of copper(I) iodide and sodium iodide complexes were studied by chemical analysis, thermal analysis and X-ray diffractometry. Granular and columnar crystals were determined to be copper(I) iodide and sodium iodide dihydrate by X-ray diffraction analysis, respectively. Needle crystal (A) which was separated from the solution at 25 0 C was assumed to be Na 2 CuI 3 .6H 2 O. (A) was stable in its appearance in the air, but the X-ray diffraction pattern of (A) changed. Needle crystal (B) which was recrystallized at 10 0 C from mother liquor after the separation of crystal (A) was assumed to be NaCuI 2 .4H 2 O. (B) was hygroscopic and decomposed to precipitate copper(I) iodide with moisture in the air. (A) and (B) were found to change by heating and or drying, respectively, as follows: Na 2 CuI 3 .6H 2 O → (-2H 2 O, 80 0 C) → 2NaI.2H 2 O + CuI → (-4H 2 O, 160 0 C) → 2NaI + CuI → (+1/2O 2 , 450 0 C) → 2NaI + CuO + 1/2I 2 , NaCuI 2 .4H 2 O → (-4H 2 O, Dried) → NaI + CuI. (auth.)

  7. Adsorption of methyl iodide on charcoal

    International Nuclear Information System (INIS)

    Hidajat, K.; Aracil, J.; Kenney, C.N.

    1990-01-01

    The adsorption of non-radioactive methyl iodide has been measured experimentally over a range of conditions of concentration, and temperature on an activated charcoal. This is of interest since methyl iodide is formed from iodine fission products in gas cooled nuclear reactors. A mathematical model has also been developed which describes the rate of adsorption, under isothermal and linear adsorption isotherm conditions in a recycle adsorber. This model takes into account the resistance to adsorption caused by the surface adsorption, as well as the external and internal mass transfer resistances. The solution to the model for the recycle adsorber was obtained using a semidiscretisation method to reduce the partial differential equations to a system of stiff ordinary differential equations, and the resulting differential equations solved by a standard numerical technique. (author)

  8. Clinical value of sodium iodide symporter

    International Nuclear Information System (INIS)

    Li Qian

    2003-01-01

    The sodium iodide symptorter (NIS) is a membrane glycoprotein that mediates iodide uptake in the thyroid gland and several extrathyroidal tissues. In addition to thyroid tissues, the expression of NIS is found in stomach, prostate, placenta and so on. Radioiodine-concentrating activity in thyroid tissues has allowed the use of radioiodine as a diagnostic and therapeutic agent for patients with thyroid disorders. However, some extrathyroid tissues also take up radioiodine, contributing to unwanted side effects of radioiodine therapy. Now that the molecule of NIS has been cloned and characterized, it may be possible to develop novel strategies to differentially modulate NIS expression and activity, enhancing it in target tissues and impeding it in others. It is also important to explore the use of NIS as an imaging reporter gene to monitor the expression profile of the transgene in transgenic mouse animal models and in patients undergoing gene therapy clinical trials

  9. Strontium-90 measurements in Switzerland

    International Nuclear Information System (INIS)

    Friedli, C.; Geering, J.J.; Lerch, P.

    1988-01-01

    Strontium-90 contamination in Switzerland has been measured since the sixties. The determination of 90 Sr in human vertebrae, milk-teeth, milk and wine have shown a maximum activity between 1964 and 1966. Since 1976, the survey has been extended to the food chain. After the Chernobyl accident, the measurements indicated a significative 90 Sr contamination in the Tessin and the north-east of Switzerland. The partition of 90 Sr in wheat has been determined and transfer factors are given for the milk - cheese - whey chain

  10. Methyl iodide tests on used adsorbents

    International Nuclear Information System (INIS)

    Kovach, J.L.

    1993-01-01

    This paper discusses the history of events leading to the current problems in radioiodine test conditions. These radioiodine tests are performed in the adsorbent media from both safety and non-safety related Nuclear Air Treatment Systems (NATS). The main problem addressed is that currently there are still numerous plant technical specifications for NATS which reference outdated test protocols for the surveillance testing of the radioactive methyl iodide performance of the adsorbents. Recommendations for correcting the test condition problems are presented. 7 refs

  11. Strontium metabolism and mechanism of interaction with mineralized tissues

    International Nuclear Information System (INIS)

    Wadkins, C.L.; Fu Peng, C

    1981-01-01

    This paper examines the administration of strontium to birds and mammals which results in limited incorporation into skeletal tissue, depressed intestinal calcium absorption, and development of rachitic bone lesions. Comparison of radiostrontium and radiocalcium incorporation by intact animals reveals discrimination against strontium in favor of calcium. Comparison of the Sr 85 - Ca 2+ and Ca 45 - Ca 2+ exchange reveals discrimination against strontium in favor of calcium. Thus, this system manifests product specificity, strontium inhibition, strontium exchange, and discrimination observed with intact animals

  12. Fixation of Radioactive Strontium in Soil

    DEFF Research Database (Denmark)

    Gregers-Hansen, Birte

    1964-01-01

    of the other long-lived fission products. Much work2–5 has, therefore, been concerned with the possibility of bringing down the strontium-90 uptake by plants through ploughing or through the addition of lime or fertilizer to the soil. Another factor, the effect of ageing on the availability of strontium, has...... been considered6,7. In general, these methods appear to be of little practical value, except for deep ploughing and the liming of acid soils, both of which will reduce the strontium uptake by a factor of 3–4....

  13. Ceria and strontium titanate based electrodes

    DEFF Research Database (Denmark)

    2010-01-01

    A ceramic anode structure obtainable by a process comprising the steps of: (a) providing a slurry by dispersing a powder of an electronically conductive phase and by adding a binder to the dispersion, in which said powder is selected from the group consisting of niobium-doped strontium titanate......, vanadium-doped strontium titanate, tantalum-doped strontium titanate, and mixtures thereof, (b) sintering the slurry of step (a), (c) providing a precursor solution of ceria, said solution containing a solvent and a surfactant, (d) impregnating the resulting sintered structure of step (b...

  14. Strontium clusters: electronic and geometry shell effects

    DEFF Research Database (Denmark)

    Lyalin, Andrey G.; Solov'yov, Ilia; Solov'yov, Andrey V.

    2008-01-01

    charged strontium clusters consisting of up to 14 atoms, average bonding distances, electronic shell closures, binding energies per atom, and spectra of the density of electronic states (DOS). It is demonstrated that the size-evolution of structural and electronic properties of strontium clusters...... is governed by an interplay of the electronic and geometry shell closures. Influence of the electronic shell effects on structural rearrangements can lead to violation of the icosahedral growth motif of strontium clusters. It is shown that the excessive charge essentially affects the optimized geometry...

  15. Sorption isolation of strontium from seawater

    International Nuclear Information System (INIS)

    Avramenko, V.A.; Zheleznov, V.V.; Kaplun, E.V.; Sokol'nitskaya, T.A.; Yukhkam, A.A.

    2001-01-01

    Sorption isolation of strontium from seawater is considered and prospects of use of selective adsorbents for purification of seawater or liquid radioactive wastes mixed with seawater from 90 Sr are discussed. Comparative analysis of sorptive properties of adsorbents of different nature is done. It is shown that sorption-reagent materials developed by authors can to afford effective separation of 90 Sr from seawater. Possible mechanism of strontium sorption by these adsorbents is considered. The prospect of their use for purification of liquid radioactive wastes from strontium is shown [ru

  16. Products of the reaction between methylene iodide and tertiary arsines

    International Nuclear Information System (INIS)

    Gigauri, R.D.; Arabuli, L.G.; Machaidze, Z.I.; Rusiya, M.Sh.

    2005-01-01

    Iodides of iodomethylenetrialkyl(aryl) arsonium were synthesized with high yields as a result of interaction between methylene iodide and tertiary arsines. Exchange reactions of the iodides prepared with lead(II) nitrate in water-alcohol solutions gave rise to formation of iodomethylenetrialkyl(aryl) arsonium nitrates. All the products prepared were characterized by data of elementary analysis, IR spectroscopy, conductometry and melting points measurements [ru

  17. Effect of nitrogen and oxygen on radiolysis of iodide solution

    Energy Technology Data Exchange (ETDEWEB)

    Karasawa, H; Endo, M [Hitachi Ltd., Power and Industrial System R+D Divisions, Ibaraki (Japan)

    1996-12-01

    The effect of nitrogen and oxygen on radiolysis of iodide solution was examined. Direct decomposition of nitrogen by {gamma}-radiation produced nitric acid to decrease a water pH. This resulted in the iodine formation in the radiolysis of iodide solution. Hydrogen peroxide was produced by the radiolysis of water containing oxygen. This worked a reducing agent to suppress the formation of iodine in the radiolysis of iodide solution. In the analytical model, fourteen iodine species were considered and reaction scheme consisted in 124 reactions. The analytical model could estimate the oxidation state of iodide ions. (author) 4 figs., 4 refs.

  18. In Vitro Bioavailability Study of an Antiviral Compound Enisamium Iodide

    Directory of Open Access Journals (Sweden)

    Eleonore Haltner-Ukomadu

    2018-01-01

    Full Text Available An investigation into the biopharmaceutics classification and a study of the in vitro bioavailability (permeability and solubility of the antiviral compound enisamium iodide (4-(benzylcarbamoyl-1-methylpyridinium iodide were carried out. The solubility of enisamium iodide was determined in four different buffers. Apparent intestinal permeability (Papp of enisamium iodide was assessed using human colon carcinoma (Caco-2 cells at three concentrations. The solubility of enisamium iodide in four buffer solutions from pH 1.2 to 7.5 is about 60 mg/mL at 25 °C, and ranges from 130 to 150 mg/mL at 37 °C, depending on the pH. Based on these results, enisamium iodide can be classified as highly soluble. Enisamium iodide demonstrated low permeability in Caco-2 experiments in all tested concentrations of 10–100 μM with permeability coefficients between 0.2 × 10−6 cm s−1 and 0.3 × 10−6 cm s−1. These results indicate that enisamium iodide belongs to class III of the Biopharmaceutics Classification System (BCS due to its high solubility and low permeability. The bioavailability of enisamium iodide needs to be confirmed in animal and human studies.

  19. Separation of cesium and strontium with zeolites

    Energy Technology Data Exchange (ETDEWEB)

    Kanno, T; Hashimoto, H [Tohoku Univ., Sendai (Japan). Research Inst. of Mineral Dressing and Metallurgy

    1976-06-01

    The basic studies of separation of cesium and strontium were made with specimens of zeolite, which are synthetic zeolites A, X and Y; synthetic mordenite; natural mordenite; and clinoptilolite. Ammonium chloride was used as eluent, because it was considered to be a most appropriate eluent in alkaline chlorides. Cesium was easily eluted from the zeolites A and X by ammonium chloride solution, but it was difficult to elute from the synthetic mordenite, natural mordenite and clinoptilolite by ammonium chloride solution, but it was difficult to elute from the zeolites A and X. The zeolite Y is the only one zeolite among these zeolites from which both of cesium and strontium were easily eluted by ammonium chloride solution. Strontium could be separated from cesium with zeolites by formation of Sr-EDTA chelate at pH above 11. In this process, cesium was only exchanged in zeolite column, but strontium flow out from it.

  20. Separation of cesium and strontium with zeolites

    International Nuclear Information System (INIS)

    Kanno, Takuji; Hashimoto, Hiroyuki

    1976-01-01

    The basic studies of separation of cesium and strontium were made with specimens of zeolite, which are synthetic zeolites A, X and Y; synthetic mordenite; natural mordenite; and clinoptilolite. Ammonium chloride was used as eluent, because it was considered to be a most appropriate eluent in alkaline chlorides. Cesium was easily eluted from the zeolites A and X by ammonium chloride solution, but it was difficult to elute from the synthetic mordenite, natural mordenite and clinoptilolite by ammonium chloride solution, but it was difficult to elute from the zeolites A and X. The zeolite Y is the only one zeolite among these zeolites from which both of cesium and strontium were easily eluted by ammonium chloride solution. Strontium could be separated from cesium with zeolites by formation of Sr-EDTA chelate at pH above 11. In this process, cesium was only exchanged in zeolite column, but strontium flow out from it. (auth.)

  1. Dielectric behaviour of strontium tartrate single crystals

    Indian Academy of Sciences (India)

    Unknown

    dielectric loss (tan δ) as functions of frequency and temperature. Ion core type ... Since the data on dielectric properties of strontium tartrate trihydrate (STT) do not ... through 'AE' make 15-amp dimmerstat, the rate of heating was maintained ...

  2. Hanford waste encapsulation: strontium and cesium

    International Nuclear Information System (INIS)

    Jackson, R.R.

    1976-06-01

    The strontium and cesium fractions separated from high radiation level wastes at Hanford are converted to the solid strontium fluoride and cesium chloride salts, doubly encapsulated, and stored underwater in the Waste Encapsulation and Storage Facility (WESF). A capsule contains approximately 70,000 Ci of 137 Cs or 70,000 to 140,000 Ci of 90 Sr. Materials for fabrication of process equipment and capsules must withstand a combination of corrosive chemicals, high radiation dosages and frequently, elevated temperatures. The two metals selected for capsules, Hastelloy C-276 for strontium fluoride and 316-L stainless steel for cesium chloride, are adequate for prolonged containment. Additional materials studies are being done both for licensing strontium fluoride as source material and for second generation process equipment

  3. Strontium Diibuprofenate Dihydrate, Strontium Malonate Sesquihydrate, Strontium Diascorbate Dihydrate and Strontium 2-Oxidobenzoate Hydrate at 120 K

    DEFF Research Database (Denmark)

    Stahl, Kenny; Andersen, Jens Enevold Thaulov; Cristgau, Stephan

    2006-01-01

    -sharing to form chains. The Sr coordination chains are packed into layers, which are stacked by van der Waals interactions. Poly[-aqua-diaquadi--malonato-distrontium(II)], [Sr2(C3H2O4)2(H2O)3]n, crystallizes with nine-coordinated Sr atoms three-dimensionally interconnected into a framework structure. One...... of the two crystallographically independent water molecules is located on a twofold axial site. catena-Poly[[diaqua(ascorbato)strontium(II)]--ascorbato], [Sr(C6H7O6)2(H2O)2]n, crystallizes with isolated eight-coordinated Sr polyhedra. One of the ascorbate ligands bridges two Sr atoms, forming zigzag...

  4. Determination of radioactive strontium in seawater

    International Nuclear Information System (INIS)

    Grahek, Zeljko; Rozmaric Macefat, Martina

    2005-01-01

    This paper describes the procedures of isolating strontium and yttrium from seawater that enable the determination of 89,90 Sr. In one procedure, strontium is directly isolated from seawater on the column filled with Sr resin by binding of strontium to the resin from 3 M HNO 3 in a seawater, and successive elution with HNO 3 . In others, strontium is precipitated from seawater with (NH 4 ) 2 CO 3 , followed by isolation on a Sr column or an anion exchange column. It is shown that strontium precipitation is optimal with concentration of 0.3 M (NH 4 ) 2 CO 3 at pH = 11. In these conditions, 100% Y, 78% Sr, 80% Ca and 50% Mg are precipitated. Strontium is bound on to Sr column from 5 to 8 M HNO 3 , separated from other elements by elution with 3 M HNO 3 and 0.05 M HNO 3 . Strontium and yttrium are bound on to anion exchange column from alcoholic solutions of nitric acid. The optimum mixture of alcohols for sample binding is a mixture of ethanol and methanol with the volume ratio 1:3. Strontium and yttrium are separated from Mg, Ca, K, and other elements by elution with 0.25 M HNO 3 in the mixture of ethanol and methanol. After the separation, yttrium and strontium are eluted from the column with water or methanol. In the procedure of direct isolation from 1 l of the sample, the average recovery of 50% was obtained. In the remaining two procedures, the strontium recovery was about 60% for the Sr column and 65% for anion exchange column. Recovery of yttrium is about 70% for the anion exchange column. It turned out that the procedure with the Sr resin (direct isolation and isolation after precipitation) is simpler and faster in the phase of the isolation on the column in comparison with the procedure with the anion exchanger. The procedure with the anion exchanger, however, enables the simultaneous isolation of yttrium and strontium and rapid determination of 89,90 Sr. These procedures were tested by determination of 89,90 Sr on liquid scintillation counter and Cherenkov

  5. Analysis for iodide in groundwater by x-ray fluorescence spectrometry after collection as silver iodide on activated charcoal

    International Nuclear Information System (INIS)

    Howe, P.T.

    1980-01-01

    The report describes the determination of microgram quantities of iodide in water by X-ray fluorescence spectrometry. The iodide is concentrated by precipitation as silver iodide on activated charcoal. If a 60-mL sample is available, a concentration of 0.12 mg/L can be detected. Precision (2σ) at the 1-mg/L level is +- 0.08 mg/L. (auth)

  6. Strontium-90 migration in Hanford sediments, USA

    International Nuclear Information System (INIS)

    Steefel, C.I.; Yang, L.; Carroll, S.A.; Roberts, S.; Zachara, J.M.; Yabusaki, S.B.

    2005-01-01

    Full text of publication follows: Strontium-90 is an important risk-driving contaminant at the Hanford site in eastern Washington, USA. Disposal operations at the Hanford 100-N area released millions of liters of reactor cooling water containing high concentrations of strontium-90 into the vadose zone immediately adjacent to the Columbia River. The effectiveness of pump-and-treat methods for remediation have been questioned, largely because the strontium is strongly sorbed on subsurface sediments via ion exchange reactions and co-precipitation in carbonates. In addition, groundwater monitoring wells show a fluctuating seasonal behavior in which high strontium-90 concentrations correlate with high Columbia River stage, even while average concentrations remain approximately constant. A series of fully saturated reactive transport column experiments have been conducted to investigate the important controls on strontium migration in Hanford groundwater [1]. The experiments were designed to investigate the multicomponent cation exchange behavior of strontium in competition with the cations Na + , Ca +2 , and Mg +2 , the concentration of which differs between river water and groundwater. Reactive transport modeling of the experiments indicates that the Sr +2 selectivity coefficient becomes larger with increasing NaNO 3 concentration, a behavior also shown by the divalent cations Ca +2 and Mg +2 . A new set of column experiments investigates the effect of wetting and drying cycles on strontium- 90 sorption and migration by considering episodic flow in Hanford sediments. In addition, the effect of fluctuating aquifer chemistry as a result of changes in the Columbia River stage on Sr +2 sorption is addressed. Modeling of multicomponent reactive transport under variably saturated conditions is used to interpret the results of the episodic flow/chemistry experiments. [1] Experimental and modeling studies of the migration behavior of strontium in Hanford sediments, USA. C

  7. Production of Molecular Iodine and Tri-iodide in the Frozen Solution of Iodide: Implication for Polar Atmosphere.

    Science.gov (United States)

    Kim, Kitae; Yabushita, Akihiro; Okumura, Masanori; Saiz-Lopez, Alfonso; Cuevas, Carlos A; Blaszczak-Boxe, Christopher S; Min, Dae Wi; Yoon, Ho-Il; Choi, Wonyong

    2016-02-02

    The chemistry of reactive halogens in the polar atmosphere plays important roles in ozone and mercury depletion events, oxidizing capacity, and dimethylsulfide oxidation to form cloud-condensation nuclei. Among halogen species, the sources and emission mechanisms of inorganic iodine compounds in the polar boundary layer remain unknown. Here, we demonstrate that the production of tri-iodide (I3(-)) via iodide oxidation, which is negligible in aqueous solution, is significantly accelerated in frozen solution, both in the presence and the absence of solar irradiation. Field experiments carried out in the Antarctic region (King George Island, 62°13'S, 58°47'W) also showed that the generation of tri-iodide via solar photo-oxidation was enhanced when iodide was added to various ice media. The emission of gaseous I2 from the irradiated frozen solution of iodide to the gas phase was detected by using cavity ring-down spectroscopy, which was observed both in the frozen state at 253 K and after thawing the ice at 298 K. The accelerated (photo-)oxidation of iodide and the subsequent formation of tri-iodide and I2 in ice appear to be related with the freeze concentration of iodide and dissolved O2 trapped in the ice crystal grain boundaries. We propose that an accelerated abiotic transformation of iodide to gaseous I2 in ice media provides a previously unrecognized formation pathway of active iodine species in the polar atmosphere.

  8. Evaluating iodide recycling inhibition as a novel molecular initiating event for thyroid axis disruption

    Science.gov (United States)

    The enzyme iodotyrosine deiodinase (dehalogenase, IYD) catalyzes iodide recycling and promotes iodide retention in thyroid follicular cells. Loss of function or chemical inhibition of IYD reduces available iodide for thyroid hormone synthesis, which leads to hormone insufficiency...

  9. Kinetics of isotopic exchange between strontium polymolybdate and strontium ions in aqueous solution

    International Nuclear Information System (INIS)

    Atun, Gulten; Bilgin, Binay; Kilislioglu, Ayben

    2002-01-01

    A heterogeneous isotopic exchange reaction of strontium polymolybdate in strontium chloride solution was studied using 90 Sr as a tracer. The effects of low and high strontium chloride concentration on the rate and mechanism of the isotopic exchange reaction were investigated. It was found that, at high concentrations, the rate is independent of strontium concentration, but, at low concentrations, the rate is proportional to the strontium concentration. These results support a hypothesis that, at low concentrations, the rate is controlled by film diffusion, whereas at high concentrations it is controlled by particle diffusion. Experiments were performed at 293, 303 and 313 K. Activation energy of isotopic exchange reaction and thermodynamic parameters ΔH*, ΔS*, and ΔG* were calculated using the Arrhenius and Eyring equations. The results also indicated that recrystallization is a predominant factor in the present exchange reaction

  10. Kinetics of isotopic exchange between strontium polymolybdate and strontium ions in aqueous solution

    Energy Technology Data Exchange (ETDEWEB)

    Atun, Gulten E-mail: gultena@istanbul.edu.tr; Bilgin, Binay; Kilislioglu, Ayben

    2002-06-01

    A heterogeneous isotopic exchange reaction of strontium polymolybdate in strontium chloride solution was studied using {sup 90}Sr as a tracer. The effects of low and high strontium chloride concentration on the rate and mechanism of the isotopic exchange reaction were investigated. It was found that, at high concentrations, the rate is independent of strontium concentration, but, at low concentrations, the rate is proportional to the strontium concentration. These results support a hypothesis that, at low concentrations, the rate is controlled by film diffusion, whereas at high concentrations it is controlled by particle diffusion. Experiments were performed at 293, 303 and 313 K. Activation energy of isotopic exchange reaction and thermodynamic parameters {delta}H*, {delta}S*, and {delta}G* were calculated using the Arrhenius and Eyring equations. The results also indicated that recrystallization is a predominant factor in the present exchange reaction.

  11. Photoluminescence Enhancement in Formamidinium Lead Iodide Thin Films

    NARCIS (Netherlands)

    Fang, Hong-Hua; Wang, Feng; Adjokatse, Sampson; Zhao, Ni; Loi, Maria Antonietta

    2016-01-01

    Formamidinium lead iodide (FAPbI(3)) has a broader absorption spectrum and better thermal stability than the most famous methylammonium lead iodide, thus exhibiting great potential for photovoltaic applications. In this report, the light-induced photoluminescence (PL) evolution in FAPbI(3) thin

  12. The iodine/iodide redox couple at a platinum electrode

    NARCIS (Netherlands)

    Dane, L.M.; Janssen, L.J.J.; Hoogland, J.G.

    1968-01-01

    The I/iodide redox couple was studied on Pt in 0.5M H2SO4 by measuring the impedance as a function of frequency. From these measurements, the exchange c.d. j0 was derived according to Sluyters. The dependence of j0 on the reversible potential and the I and the iodide concns. was established. By

  13. Amino acid-assisted synthesis of strontium hydroxyapatite bone ...

    Indian Academy of Sciences (India)

    Strontium-incorporated calcium phosphates show potential in biomedical application, particularly the doped stron- tium may ... shows that the addition of glycine plays an important role in reducing the particle size of strontium hydroxyapatite.

  14. Reduced-graphene-oxide-and-strontium-titanate-based double ...

    Indian Academy of Sciences (India)

    GO)/strontium titanate were pre- ... R-GO and strontium titanate were synthesized and characterized before ... Microwave absorption capabilities of the composite absorbers were investigated using a .... was backed with a conducting metal sheet.

  15. Measurement of strontium 90 in the rain fall-out

    International Nuclear Information System (INIS)

    Suratman; Soedyartomo; Suhartono.

    1976-01-01

    The procedure of radioactivity measurement of strontium 90 in the rain fallout as well as the measurement of the fallout gross beta activity have been studied. In the preliminary study strontium 90 is separated from other cations especially fission products by fuming nitric acid, and radioactivity measurement is carried out in the form of strontium oxalate. Data of radioactivity measurement of strontium 90 and the gross beta activity in the fallout are given. (author)

  16. Ferroelastic Fingerprints in Methylammonium Lead Iodide Perovskite

    KAUST Repository

    Hermes, Ilka M.

    2016-02-12

    Methylammonium lead iodide (MAPbI3) perovskite materials show an outstanding performance in photovoltaic devices. However, certain material properties, especially the possible ferroic behavior, remain unclear. We observed distinct nanoscale periodic domains in the piezoresponse of MAPbI3(Cl) grains. The structure and the orientation of these striped domains indicate ferroelasticity as their origin. By correlating vertical and lateral piezoresponse force microscopy experiments performed at different sample orientations with x-ray diffraction, the preferred domain orientation was suggested to be the a1-a2-phase. The observation of these ferroelastic fingerprints appears to strongly depend on the film texture and thus the preparation route. The formation of the ferroelastic twin domains could be induced by internal strain during the cubic-tetragonal phase transition.

  17. Distribution of strontium in milk component

    International Nuclear Information System (INIS)

    Rosskopfova, O.; Galambos, M.; Rajec, P.

    2011-01-01

    The distribution of strontium between the milk components, i.e., serum, casein micelles, whey and hydroxyapatite was determined. The sorption on hydroxyapatite was investigated using batch method and radiotracer technique. The aqueous phase comprised of either milk or whey. The sorption of strontium on hydroxyapatite depended on the method of its preparation and on the composition of the aqueous phase. The sorption of strontium was increased with an increase of pH. The presence of citrate species resulted in decrease of the sorption of strontium on hydroxyapatite. The sorption of 85 Sr on hydroxyapatite decreased with the increasing concentration of Ca 2+ ions. Addition of Ca 2+ ions to milk resulted in milk pH decrease. The decrease in pH value after calcium addition to milk is related to exchanges between added calcium and micellar H + . The average value of strontium sorption on casein micelles in milk with presence of hydroxyapatite was (47.3 ± 5.6) %. The average value of sorption of 85 Sr on casein micelles in milk without the addition of hydroxyapatite was (68.9 ± 2.2) %. (author)

  18. Growth and characterization of pure and lithium doped strontium ...

    Indian Academy of Sciences (India)

    TECS

    Abstract. The effect of lithium ion as dopant on the size and transparency of strontium tartrate tetrahydrate. (SrC4H4O6⋅4H2O) crystals are presented in this paper. Growth of single crystals of undoped and lithium doped strontium tartrate tetrahydrate by controlled diffusion of strontium nitrate into the gel charged with.

  19. Growth of strontium oxalate crystals in agar–agar gel

    Indian Academy of Sciences (India)

    Growth of strontium oxalate crystals in agar–agar gel. P V DALAL. ∗ and K B SARAF. Postgraduate Department of Physics, Pratap College, Amalner 425 401, India. MS received 16 March 2008; revised 5 April 2010. Abstract. Single crystals of strontium oxalate have been grown by using strontium chloride and oxalic acid in.

  20. Rapid determination of strontium-89 and strontium-90 in food and environmental samples by Cerenkov counting

    International Nuclear Information System (INIS)

    Melin, Judith; Suomela, Jorma

    1995-01-01

    The method has been developed for emergency situations. Minimum detectable concentrations of 5 Bq/liter, kilogram of strontium-89 and strontium-90 respectively is achievable in the presence of nuclides considered to be released under accidental conditions. Result on the strontium-89 and strontium-90 content in a sample can be obtained within 12 hours. One technician can easily handle 8-10 samples during a working day of eight hours. The determination of the strontium isotopes is accomplished by monitoring the Cerenkov radiation from strontium-89 and yttrium-90 in a liquid scintillation counter. The latter is the daughter product of strontium-90. Prior to the Cerenkov counting the sample is separated from interfering nuclides by oxalate precipitation, chromate precipitation and HDEHP-extraction. The method has to be further improved and evaluated with respect to different soil types such as forest mineral soil layers, agricultural soils and pastures. Furthermore, the decontamination procedure should be evaluated for a sample containing freshly irradiated uranium. (author)

  1. Study of radiation formation of methyl-iodide Part 2

    International Nuclear Information System (INIS)

    Bartonicek, B.; Schweiner, Z.; Bednar, J.; Hladky, E.

    1975-01-01

    Purified methane, ethylene, iodine, methyl iodide, ethyl iodide and hydrogen iodide were irradiated and/or pyrolyzed in Pyrex ampoules by 60 Co-γ-radiation at temperatures between 150 and 450 deg C. The results on radiolysis and pyrolysis were as follows: 1., The most thermally stable product is hydrogen iodide in which already at 450 deg C essen-tially all originally present iodine appears. 2., The radiolytic formation of methyl iodide and hydrogen iodide is positively influenced by the rise in temperature, This and the absolute values of yields indicate a chain mechanism of radiolytic (and pyrolytic) decomposition of the mixture. 3., The ratio of equilibrium concentrations [HI]/[CH 3 I] increases with increasing temperature of pyrolysis showing that HI is the end product of the thermal chain reaction. Methyl iodide is likely to contribute (by its thermal decomposition) to the initiation and propagation of this chain reaction. 4., The negligible temperature dependence of G(H 2 ) and the absence of molecular hydrogen among the products of pyrolytic decomposition of methane-iodine mixtures shows, that (up to 450 deg C) H atoms do not play any role in the thermal chain decomposition of these mixtures. (K.A.)

  2. Flavonoid rutin increases thyroid iodide uptake in rats.

    Directory of Open Access Journals (Sweden)

    Carlos Frederico Lima Gonçalves

    Full Text Available Thyroid iodide uptake through the sodium-iodide symporter (NIS is not only an essential step for thyroid hormones biosynthesis, but also fundamental for the diagnosis and treatment of different thyroid diseases. However, part of patients with thyroid cancer is refractory to radioiodine therapy, due to reduced ability to uptake iodide, which greatly reduces the chances of survival. Therefore, compounds able to increase thyroid iodide uptake are of great interest. It has been shown that some flavonoids are able to increase iodide uptake and NIS expression in vitro, however, data in vivo are lacking. Flavonoids are polyhydroxyphenolic compounds, found in vegetables present in human diet, and have been shown not only to modulate NIS, but also thyroperoxidase (TPO, the key enzyme in thyroid hormones biosynthesis, besides having antiproliferative effect in thyroid cancer cell lines. Therefore, we aimed to evaluate the effect of some flavonoids on thyroid iodide uptake in Wistar rats in vivo. Among the flavonoids tested, rutin was the only one able to increase thyroid iodide uptake, so we decided to evaluate the effect of this flavonoid on some aspects of thyroid hormones synthesis and metabolism. Rutin led to a slight reduction of serum T4 and T3 without changes in serum thyrotropin (TSH, and significantly increased hypothalamic, pituitary and brown adipose tissue type 2 deiodinase and decreased liver type 1 deiodinase activities. Moreover, rutin treatment increased thyroid iodide uptake probably due to the increment of NIS expression, which might be secondary to increased response to TSH, since TSH receptor expression was increased. Thus, rutin might be useful as an adjuvant in radioiodine therapy, since this flavonoid increased thyroid iodide uptake without greatly affecting thyroid function.

  3. Strontium and fluorine in tuatua shells

    International Nuclear Information System (INIS)

    Trompetter, W.J.; Coote, G.E.

    1993-01-01

    This report describes the research to date on the elemental distributions of strontium, calcium, and fluorine in a collection of 24 tuatua shells (courtesy of National Museum). Variations in elemental concentrations were measured in the shell cross-sections using a scanning proton microprobe (PIXE and PIGME). In this paper we report the findings to date, and present 2-D measurement scans as illustrative grey-scale pictures. Our results support the hypothesis that increased strontium concentrations are deposited in the shells during spawning, and that fluorine concentration is proportional to growth rate. (author). 15 refs.; 13 figs.; 1 appendix

  4. Printed Barium Strontium Titanate capacitors on silicon

    Energy Technology Data Exchange (ETDEWEB)

    Sette, Daniele [Univ. Grenoble Alpes, F-38000 Grenoble (France); CEA, LETI, MINATEC Campus, F-38054 Grenoble (France); Luxembourg Institute of Science and Technology LIST, Materials Research and Technology Department, L-4422 Belvaux (Luxembourg); Kovacova, Veronika [Univ. Grenoble Alpes, F-38000 Grenoble (France); CEA, LETI, MINATEC Campus, F-38054 Grenoble (France); Defay, Emmanuel, E-mail: emmanuel.defay@list.lu [Univ. Grenoble Alpes, F-38000 Grenoble (France); CEA, LETI, MINATEC Campus, F-38054 Grenoble (France); Luxembourg Institute of Science and Technology LIST, Materials Research and Technology Department, L-4422 Belvaux (Luxembourg)

    2015-08-31

    In this paper, we show that Barium Strontium Titanate (BST) films can be prepared by inkjet printing of sol–gel precursors on platinized silicon substrate. Moreover, a functional variable capacitor working in the GHz range has been made without any lithography or etching steps. Finally, this technology requires 40 times less precursors than the standard sol–gel spin-coating technique. - Highlights: • Inkjet printing of Barium Strontium Titanate films • Deposition on silicon substrate • Inkjet printed silver top electrode • First ever BST films thinner than 1 μm RF functional variable capacitor that has required no lithography.

  5. Surface adsorption in strontium chloride ammines

    DEFF Research Database (Denmark)

    Ammitzbøll, Andreas L.; Lysgaard, Steen; Klukowska, Agata

    2013-01-01

    An adsorbed state and its implications on the ab- and desorption kinetics of ammonia in strontium chloride ammine is identified using a combination of ammonia absorption measurements, thermogravimetric analysis, and density functional theory calculations. During thermogravimetric analysis, ammonia...... desorption originating from the adsorbed state is directly observed below the bulk desorption temperature, as confirmed by density functional theory calculations. The desorption enthalpy of the adsorbed state of strontium chloride octa-ammine is determined with both techniques to be around 37-39 k...

  6. Deposition of strontium and calcium in snail shell

    Energy Technology Data Exchange (ETDEWEB)

    Rosenthal, Jr, G M; Nelson, D J; Gardiner, D A

    1965-07-03

    The relative effects of strontium and calcium concentrations in the environment on their uptake and incorporation into snail shell were investigated. /sup 45/Ca and /sup 85/Sr were used as tracers and specific activities were used to determine deposition. Data are presented in tables and graphs. Deposition of both calcium and strontium in the snail shell depended primarily on the respective concentrations of these elements in the immediate environment. A slight effect of strontium on calcium deposition was observed. There was found to be a minimum strontium deposition for various combinations of strontium and calcium in the environment. It was concluded that strontium uptake is more closely associated with environmental strontium concentrations than with calcium concentrations.

  7. 21 CFR 520.763b - Dithiazanine iodide powder.

    Science.gov (United States)

    2010-04-01

    ... therapy for adult worms. (2) The drug is contraindicated in animals sensitive to dithiazanine iodide and...) ANIMAL DRUGS, FEEDS, AND RELATED PRODUCTS ORAL DOSAGE FORM NEW ANIMAL DRUGS § 520.763b Dithiazanine...

  8. Measurement of strontium-89 and strontium-90 in environmental waters. A tentative reference method

    International Nuclear Information System (INIS)

    1976-03-01

    A tentative reference method for the measurement of 89 Sr and 90 Sr in environmental waters is described. Samples of environmental water sources are collected, preserved with acid-strontium carrier, and analyzed for 89 Sr and/or 90 Sr. The isotopes are separated from the sample water by precipitating with stable strontium carrier as carbonate. The strontium carbonate is dissolved, 90 Sr separated, the strontium reprecipitated as carbonate, filtered, and counted for the combined 89 Sr and 90 Sr activity. The 90 y is allowed to grow in from the 90 y activity; the strontium carbonate is redissolved; the 90 y is separated, precipitated, and counted for the 90 Sr determination. The 89 Sr activity is then determined by difference of the total 89 Sr and 90 y and the separate 90 Sr activities. Recoveries are determined from the added and found (recovered) strontium carrier. Counting efficiencies are determined with prepared standard reference samples. Results are reported in pCi/liter

  9. Calcium and Strontium in Swedish Waters and Fish, and Accumulation of Strontium-90

    Energy Technology Data Exchange (ETDEWEB)

    Agnedal, P O

    1966-04-15

    The purpose of this study has been to investigate the correlation between calcium and strontium in fish in relation to the concentration of these elements in the water. An investigation of the uptake of strontium-90 has also been made and permissible levels of strontium-90 in the water is calculated based upon the uptake in fish muscle tissues. Lakes with calcium concentrations between 2 - 63 mg/l have been studied and samples from the Baltic coastal water are also included. Three fish species are studied, viz. pike (Esox lucius (L.)), perch (Perca fluviatilis (L.)) and roach (Leuciscus rutilus (L.)). Bones, muscle tissues and skin + scales have been analysed. Strontium-90 measurements have been made showing an increase in both water and fish. Calculations show that in water with about 2 mg Ca/l a 10-fold increase of the existing strontium-90 level might give strontium-90 concentrations in fish muscle tissues close to what is permissible. In lakes with calcium concentrations 20 - 40 mg/l the permissible levels for drinking water will be exceeded before the fish consumption would have to be restricted.

  10. Calcium and Strontium in Swedish Waters and Fish, and Accumulation of Strontium-90

    International Nuclear Information System (INIS)

    Agnedal, P.O.

    1966-04-01

    The purpose of this study has been to investigate the correlation between calcium and strontium in fish in relation to the concentration of these elements in the water. An investigation of the uptake of strontium-90 has also been made and permissible levels of strontium-90 in the water is calculated based upon the uptake in fish muscle tissues. Lakes with calcium concentrations between 2 - 63 mg/l have been studied and samples from the Baltic coastal water are also included. Three fish species are studied, viz. pike (Esox lucius (L.)), perch (Perca fluviatilis (L.)) and roach (Leuciscus rutilus (L.)). Bones, muscle tissues and skin + scales have been analysed. Strontium-90 measurements have been made showing an increase in both water and fish. Calculations show that in water with about 2 mg Ca/l a 10-fold increase of the existing strontium-90 level might give strontium-90 concentrations in fish muscle tissues close to what is permissible. In lakes with calcium concentrations 20 - 40 mg/l the permissible levels for drinking water will be exceeded before the fish consumption would have to be restricted

  11. Prevention of organic iodide formation in BWR`s

    Energy Technology Data Exchange (ETDEWEB)

    Karjunen, T [Finnish Centre for Radiation and Nuclear Safety, Helsinki (Finland); Laitinen, T; Piippo, J; Sirkiae, P [VTT Manufacturing Technology (Finland)

    1996-12-01

    During an accident, many different forms of iodine may emerge. Organic iodides, such as methyl iodide and ethyl iodide, are relatively volatile, and thus their appearance leads to increased concentration of gaseous iodine. Since organic iodides are also relatively immune to most accident mitigation measures, such as sprays and filters, they can affect the accident source term significantly even when only a small portion of iodine is in organic form. Formation of organic iodides may not be limited by the amount of organic substances available. Excessive amounts of methane can be produced, for example, during oxidation of boron carbide, which is used in BWR`s as a neutron absorber material. Another important source is cable insulation. In a BWR, a large quantity of cables is placed below the pressure vessel. Thus a large quantity of pyrolyse gases will be produced, should the vessel fail. Organic iodides can be formed as a result of many different reactions, but at least in certain conditions the main reaction takes place between an organic radical produced by radiolysis and elemental iodine. A necessary requirement for prevention of organic iodide production is therefore that the pH in the containment water pools is kept high enough to eliminate formation of elemental iodine. In a typical BWR the suppression pool water is usually unbuffered. As a result, the pH may be dominated by chemicals introduced during an accident. If no system for adding basic chemicals is operable, the main factor affecting pool water pH may be hydrochloric acid released during cable degradation. Should this occur, the conditions could be very favorable for production of elemental iodine and, consequently, formation of organic iodides. Although high pH is necessary for iodine retention, it could have also adverse effects. High pH may, for example, accelerate corrosion of containment materials and alter the characteristics of the solid corrosion products. (author) 6 figs., 1 tab., 13 refs.

  12. Accelerated degradation of methyl iodide by agrochemicals.

    Science.gov (United States)

    Zheng, Wei; Papiernik, Sharon K; Guo, Mingxin; Yates, Scott R

    2003-01-29

    The fumigant methyl iodide (MeI, iodomethane) is considered a promising alternative to methyl bromide (MeBr) for soil-borne pest control in high-cash-value crops. However, the high vapor pressure of MeI results in emissions of a significant proportion of the applied mass into the ambient air, and this may lead to pollution of the environment. Integrating the application of certain agrochemicals with soil fumigation provides a novel approach to reduce excessive fumigant emissions. This study investigated the potential for several agrochemicals that are commonly used in farming operations, including fertilizers and nitrification inhibitors, to transform MeI in aqueous solution. The pseudo-first-order hydrolysis half-life (t(1/2)) of MeI was approximately 108 d, while the transformation of MeI in aqueous solutions containing selected agrochemicals was more rapid, with t(1/2) agrochemicals on the rate of MeI degradation in soil was also determined. Adsorption to soil apparently reduced the availability of some nitrification inhibitors in the soil aqueous phase and lowered the degradation rate in soil. In contrast, addition of the nitrification inhibitors thiourea and allylthiourea to soil significantly accelerated the degradation of MeI, possibly due to soil surface catalysis. The t(1/2) of MeI was 300 h).

  13. Resonant double photoionisation spectroscopy of strontium

    Energy Technology Data Exchange (ETDEWEB)

    Sokell, E; Grimm, M; Sheridan, P, E-mail: emma.sokell@ucd.i, E-mail: paul.sheridan@ucd.i [School of Physics, University College Dublin, Belfield, Dublin 4 (Ireland)

    2009-11-01

    Resonant triple-differential cross-section (TDCS) measurements on atomic strontium on the 4p {yields} 4d resonance are presented. All of these TDCS measurements display unexpected lobes at a mutual emission angle for the two electrons of 180{sup o}. Possible explanations for these lobes are explored.

  14. Strontium Removal: Full-Scale Ohio Demonstrations

    Science.gov (United States)

    The objectives of this presentation are to present a brief overview of past bench-scale research to evaluate the impact lime softening on strontium removal from drinking water and present full-scale drinking water treatment studies to impact of lime softening and ion exchange sof...

  15. The coprecipitation of strontium with hydroxyapatite

    International Nuclear Information System (INIS)

    Fujino, Osamu

    1975-01-01

    The distribution behavior of the strontium ion between hydroxyapatite and the parent solution was investigated. The hydroxyapatite was formed by the extremely slow addition of diammonium hydrogenphosphate to solutions of calcium and strontium nitrate buffered with ethylenediamine at 80 0 C. The precipitate yielded a typical X-ray diffraction pattern of hydroxyapatite and had a composition in which the Ca/P molar ratio was 1.67 at pH 6.80. The strontium ion was coprecipitated in the apatite, obeying the Doerner and Hoskins logarithnmic distribution law. The distribution coefficient was scarcely affected by the strontium concentration on the pH value in the parent solution, and had a value of 0.26+-0.02 at 80 0 C. On the other hand, the apparent distribution coefficient was a little affected by such organic anions as acetate, citrate, lactate, glycinate, and glutamate ions. The lattice constants of the precipitates prepared in the research were measured in order to confirm the formation of the solid solutions. (auth.)

  16. Infrared characterization of strontium titanate thin films

    International Nuclear Information System (INIS)

    Almeida, B.G.; Pietka, A.; Mendes, J.A.

    2004-01-01

    Strontium titanate thin films have been prepared at different oxygen pressures with various post-deposition annealing treatments. The films were deposited by pulsed laser ablation at room temperature on Si(0 0 1) substrates with a silica buffer layer. Infrared reflectance measurements were performed in order to determine relevant film parameters such as layer thicknesses and chemical composition. The infrared reflectance spectra were fitted by using adequate dielectric function forms for each layer. The fitting procedure provided the extraction of the dielectric functions of the strontium titanate film, the silica layer and the substrate. The as-deposited films are found to be amorphous, and their infrared spectra present peaks corresponding to modes with high damping constants. As the annealing time and temperature increases the strontium titanate layer becomes more ordered so that it can be described by its SrTiO 3 bulk mode parameters. Also, the silica layer grows along with the ordering of the strontium titanate film, due to oxidation during annealing

  17. Cesium and Strontium Separation Technologies Literature Review

    Energy Technology Data Exchange (ETDEWEB)

    T. A. Todd; T. A. Todd; J. D. Law; R. S. Herbst

    2004-03-01

    Integral to the Advanced Fuel Cycle Initiative (AFCI) Program’s proposed closed nuclear fuel cycle, the fission products cesium and strontium in the dissolved spent nuclear fuel stream are to be separated and managed separately. A comprehensive literature survey is presented to identify cesium and strontium separation technologies that have the highest potential and to focus research and development efforts on these technologies. Removal of these high-heat-emitting fission products reduces the radiation fields in subsequent fuel cycle reprocessing streams and provides a significant short-term (100 yr) heat source reduction in the repository. This, along with separation of actinides, may provide a substantial future improvement in the amount of fuel that could be stored in a geologic repository. The survey and review of the candidate cesium and strontium separation technologies are presented herein. Because the AFCI program intends to manage cesium and strontium together, technologies that simultaneously separate both elements are of the greatest interest, relative to technologies that separate only one of the two elements.

  18. Strontium ranelate in the treatment of osteoporosis

    African Journals Online (AJOL)

    2006-11-05

    Nov 5, 2006 ... postmenopausal women (mean age 69 years) with osteoporosis or osteopenia. Strontium ranelate significantly decreased markers of bone resorption and increased biomarkers of formation. Spinal BMD increased by 14%, while vertebral fractures decreased by 49% within the first year, a reduction that was.

  19. Flavonoids, Thyroid Iodide Uptake and Thyroid Cancer-A Review.

    Science.gov (United States)

    Gonçalves, Carlos F L; de Freitas, Mariana L; Ferreira, Andrea C F

    2017-06-12

    Thyroid cancer is the most common malignant tumor of the endocrine system and the incidence has been increasing in recent years. In a great part of the differentiated carcinomas, thyrocytes are capable of uptaking iodide. In these cases, the main therapeutic approach includes thyroidectomy followed by ablative therapy with radioiodine. However, in part of the patients, the capacity to concentrate iodide is lost due to down-regulation of the sodium-iodide symporter (NIS), the protein responsible for transporting iodide into the thyrocytes. Thus, therapy with radioiodide becomes ineffective, limiting therapeutic options and reducing the life expectancy of the patient. Excessive ingestion of some flavonoids has been associated with thyroid dysfunction and goiter. Nevertheless, studies have shown that some flavonoids can be beneficial for thyroid cancer, by reducing cell proliferation and increasing cell death, besides increasing NIS mRNA levels and iodide uptake. Recent data show that the flavonoids apingenin and rutin are capable of increasing NIS function and expression in vivo. Herein we review literature data regarding the effect of flavonoids on thyroid cancer, besides the effect of these compounds on the expression and function of the sodium-iodide symporter. We will also discuss the possibility of using flavonoids as adjuvants for therapy of thyroid cancer.

  20. Flavonoids, Thyroid Iodide Uptake and Thyroid Cancer—A Review

    Science.gov (United States)

    Gonçalves, Carlos F. L.; de Freitas, Mariana L.; Ferreira, Andrea C. F.

    2017-01-01

    Thyroid cancer is the most common malignant tumor of the endocrine system and the incidence has been increasing in recent years. In a great part of the differentiated carcinomas, thyrocytes are capable of uptaking iodide. In these cases, the main therapeutic approach includes thyroidectomy followed by ablative therapy with radioiodine. However, in part of the patients, the capacity to concentrate iodide is lost due to down-regulation of the sodium-iodide symporter (NIS), the protein responsible for transporting iodide into the thyrocytes. Thus, therapy with radioiodide becomes ineffective, limiting therapeutic options and reducing the life expectancy of the patient. Excessive ingestion of some flavonoids has been associated with thyroid dysfunction and goiter. Nevertheless, studies have shown that some flavonoids can be beneficial for thyroid cancer, by reducing cell proliferation and increasing cell death, besides increasing NIS mRNA levels and iodide uptake. Recent data show that the flavonoids apingenin and rutin are capable of increasing NIS function and expression in vivo. Herein we review literature data regarding the effect of flavonoids on thyroid cancer, besides the effect of these compounds on the expression and function of the sodium-iodide symporter. We will also discuss the possibility of using flavonoids as adjuvants for therapy of thyroid cancer. PMID:28604619

  1. Aqueous-gas phase partitioning and hydrolysis of organic iodides

    International Nuclear Information System (INIS)

    Glowa, G.A.; Wren, J.C.

    2003-01-01

    The volatility and decomposition of organic iodides in a reactor containment building are important parameters to consider when assessing the potential consequences of a nuclear reactor accident. However, there are few experimental data available for the volatilities (often reported as partition coefficients) or few rate constants regarding the decomposition (via hydrolysis) of organic iodides. The partition coefficients and hydrolysis rate constants of eight organic iodides, having a range of molecular structures, have been measured in the current studies. This data, and data accumulated in the literature, have been reviewed and discussed to provide guidelines for appropriate organization of organic iodides for the purpose of modelling iodine behaviour under postulated nuclear reactor accident conditions. After assessment of the partition coefficients and their temperature dependences of many classes of organic compounds, it was found that organic iodides could be divided into two categories based upon their volatility relative to molecular iodine. Similarly, hydrolysis rates and their temperature dependences are assigned to the two categories of organic iodides. (author)

  2. Electrochemical reaction rates in a dye-sensitised solar cell - the iodide/tri-iodide redox system

    DEFF Research Database (Denmark)

    Bay, L.; West, K.; Winther-Jensen, B.

    2006-01-01

    The electrochemical reaction rate of the redox couple iodide/tri-iodide in acetonitrile is characterised by impedance spectroscopy. Different electrode materials relevant for the function of dye-sensitised solar cells (DSSC) are investigated. Preferably, the reaction with the iodide....../tri-iodide couple should be fast at the counter electrode, i.e. this electrode must have a high catalytic activity towards the redox couple, and the same reaction must be slow on the photo electrode. The catalytic activity is investigated for platinum, poly(3,4-ethylenedioxythiophene) (PEDOT), polypyrrole (PPy......), and polyaniline (PANI)-all deposited onto fluorine-doped tin oxide (FTO) glass. Both Pt and PEDOT are found to have sufficiently high catalytic activities for practical use as counter electrodes in DSSC. The reaction resistance on FTO and anatase confirmed the beneficial effect of a compact anatase layer on top...

  3. Effects of calcium and magnesium on strontium distribution coefficients

    Science.gov (United States)

    Bunde, R.L.; Rosentreter, J.J.; Liszewski, M.J.; Hemming, C.H.; Welhan, J.

    1997-01-01

    The effects of calcium and magnesium on the distribution of strontium between a surficial sediment and simulated wastewater solutions were measured as part of an investigation to determine strontium transport properties of surficial sediment at the Idaho National Engineering Laboratory (INEL), Idaho. The investigation was conducted by the U.S. Geological Survey and Idaho State University, in cooperation with the U.S. Department of Energy. Batch experimental techniques were used to determine strontium linear sorption isotherms and distribution coefficients (K(d)'s) using simulated wastewater solutions prepared at pH 8.0??0.1 with variable concentrations of calcium and magnesium. Strontium linear sorption isotherm K(d)'s ranged from 12??1 to 85??3 ml/g, increasing as the concentration of calcium and magnesium decreased. The concentration of sorbed strontium and the percentage of strontium retained by the sediment were correlated to aqueous concentrations of strontium, calcium, and magnesium. The effect of these cation concentrations on strontium sorption was quantified using multivariate least-squares regression techniques. Analysis of data from these experiments indicates that increased concentrations of calcium and magnesium in wastewater discharged to waste disposal ponds at the INEL increases the availability of strontium for transport beneath the ponds by decreasing strontium sorption to the surficial sediment.

  4. Formamidinium iodide: crystal structure and phase transitions

    Directory of Open Access Journals (Sweden)

    Andrey A. Petrov

    2017-04-01

    Full Text Available At a temperature of 100 K, CH5N2+·I− (I, crystallizes in the monoclinic space group P21/c. The formamidinium cation adopts a planar symmetrical structure [the r.m.s. deviation is 0.002 Å, and the C—N bond lengths are 1.301 (7 and 1.309 (8 Å]. The iodide anion does not lie within the cation plane, but deviates from it by 0.643 (10 Å. The cation and anion of I form a tight ionic pair by a strong N—H...I hydrogen bond. In the crystal of I, the tight ionic pairs form hydrogen-bonded zigzag-like chains propagating toward [20-1] via strong N—H...I hydrogen bonds. The hydrogen-bonded chains are further packed in stacks along [100]. The thermal behaviour of I was studied by different physicochemical methods (thermogravimetry, differential scanning calorimetry and powder diffraction. Differential scanning calorimetry revealed three narrow endothermic peaks at 346, 387 and 525 K, and one broad endothermic peak at ∼605 K. The first and second peaks are related to solid–solid phase transitions, while the third and fourth peaks are attributed to the melting and decomposition of I. The enthalpies of the phase transitions at 346 and 387 K are estimated as 2.60 and 2.75 kJ mol−1, respectively. The X-ray powder diffraction data collected at different temperatures indicate the existence of I as the monoclinic (100–346 K, orthorhombic (346–387 K and cubic (387–525 K polymorphic modifications.

  5. Isomorfic Substitutions of Calcium by Strontium in Calcium Hydroxyapatite

    International Nuclear Information System (INIS)

    Christensen, Hilbert

    1962-12-01

    By means of homogeneous precipitation it has been possible to synthesize crystalline solid solutions of calcium strontium hydroxyapatite from aqueous solutions. The lattice constants for the solid solutions were measured in the range Ca 9 Sr(PO 4 ) 6 (OH) 2 - CaSr 9 (PO 4 ) 6 (OH) 2 . The investigations show that the discrimination of strontium against calcium is considerably smaller than reported elsewhere (1). Strontium is preferentially built into the c-axis direction of the apatite lattice

  6. Strontium isotope stratigraphy of the Pelotas Basin

    Energy Technology Data Exchange (ETDEWEB)

    Zerfass, Geise de Santana dos Anjos, E-mail: geise.zerfass@petrobras.com.br [Petroleo Brasileiro S.A. (PETROBRAS/CENPES/PDGEO/BPA), Rio de Janeiro, RJ (Brazil). Centro de Pesquisas e Desenvolvimento Leopoldo Americo Miguez de Mello; Chemale Junior, Farid, E-mail: fchemale@unb.br [Universidade de Brasilia (UnB), DF (Brazil). Instituto de Geociencias; Moura, Candido Augusto Veloso, E-mail: candido@ufpa.br [Universidade Federal do Para (UFPA), Belem, PA (Brazil). Centro de Geociencias. Dept. de Geoquimica e Petrologia; Costa, Karen Badaraco, E-mail: karen.costa@usp.br [Instituto Oceanografico, Sao Paulo, SP (Brazil); Kawashita, Koji, E-mail: koji@usp.br [Unversidade de Sao Paulo (USP), SP (Brazil). Centro de Pesquisas Geocronologicas

    2014-07-01

    Strontium isotope data were obtained from foraminifera shells of the Pelotas Basin Tertiary deposits to facilitate the refinement of the chronostratigraphic framework of this section. This represents the first approach to the acquisition of numerical ages for these strata. Strontium isotope stratigraphy allowed the identification of eight depositional hiatuses in the Eocene-Pliocene section, here classified as disconformities and a condensed section. The reconnaissance of depositional gaps based on confident age assignments represents an important advance considering the remarkably low chronostratigraphic resolution in the Cenozoic section of the Pelotas Basin. The recognition of hiatuses that match hiatuses is based on biostratigraphic data, as well as on global events. Furthermore, a substantial increase in the sedimentation rate of the upper Miocene section was identified. Paleotemperature and productivity trends were identified based on oxygen and carbon isotope data from the Oligocene-Miocene section, which are coherent with worldwide events, indicating the environmental conditions during sedimentation. (author)

  7. Strontium isotopic study of sediment from the Ross Sea

    International Nuclear Information System (INIS)

    Kovach, J.; Faure, G.

    1977-01-01

    A preliminary report summarizing the results of a study of the strontium-87/strontium-86 ratios and of the rubidium and strontium concentrations of the fine-grained (less than 150 microns) noncarbonate fractions of sediment samples from core E32-25 raised from a depth of 327 fathoms in the Ross Sea at 78 0 31.0'S 164 0 24.7'W was presented. The strontium-87/strontium-86 ratios of the samples analyzed range from 0.7119 to 0.7220. Rubidium and strontium concentrations range, respectively, from 126 to 164 parts per million and from 113 to 174 parts per million. The observed strontium-87/strontium-86 ratios and strontium concentrations in sediment samples from core E32-25 fit a hyperbolic curve. These ratios can be used to estimate the concentrations of volcanogenic detritus in the sediment samples. The results of this study provide additional baseline data for anticipated future studies of sediment cores to be recovered from beneath the Ross Ice Shelf by the Ross Ice Shelf Project. 1 figure

  8. Removal of Strontium from Drinking Water by Conventional ...

    Science.gov (United States)

    The United States Environmental Protection Agency Contaminant Candidate List 3 lists strontium as a contaminant for potential regulatory consideration in drinking water. There is very little data available on strontium removal from drinking water. As a result, there is an immediate need to perform treatment studies. The objective of this work is to evaluate the effectiveness of conventional and lime-soda ash softening treatments to remove strontium from surface and ground waters. Conventional drinking water treatment with aluminum and iron coagulants were able to achieve 12% and 5.9% strontium removal at best, while lime softening removed as much as 78% from natural strontium-containing ground water. Systematic fundamental experiments showed that strontium removal during the lime-soda ash softening was related to pH, calcium concentration and dissolved inorganic carbon concentration. Final strontium concentration was also directly associated with initial strontium concentration. Precipitated solids showed well-formed crystals or agglomerates of mixed solids, two polymorphs of calcium carbonate (vaterite and calcite), and strontianite, depending on initial water quality conditions. X-ray diffraction analysis suggested that strontium likely replaced calcium inside the crystal lattice and was likely mainly responsible for removal during lime softening. To inform the public.

  9. Lanthanide doped strontium-barium cesium halide scintillators

    Science.gov (United States)

    Bizarri, Gregory; Bourret-Courchesne, Edith; Derenzo, Stephen E.; Borade, Ramesh B.; Gundiah, Gautam; Yan, Zewu; Hanrahan, Stephen M.; Chaudhry, Anurag; Canning, Andrew

    2015-06-09

    The present invention provides for a composition comprising an inorganic scintillator comprising an optionally lanthanide-doped strontium-barium, optionally cesium, halide, useful for detecting nuclear material.

  10. System of lithium, sodium, and strontium bromides

    International Nuclear Information System (INIS)

    Litvinova, G.N.; Yagub'yan, E.S.; Bukhalova, G.A.

    1988-01-01

    The visual-polythermal and partially differential thermal methods of analysis have been applied to investigate the meltability diagram of the Li 2 Br 2 -Na 2 Br 2 -SrBr 2 ternary system. Three fields of crystallization belonging to strontium bromide, to the compound LiSr 2 Br 5 and solid solutions of lithium and sodium bromides are found. Two points complying with nonvariant equilibria are discovered

  11. A new method for the preparation of strontium titanate and strontium hypovanadate

    International Nuclear Information System (INIS)

    Balasubramanian, M.R.

    1985-01-01

    Strontium titanate has been a prized chemical by virtue of its dielectric, photoelectric and surface properties. The compound crystallises with the cubic perovskite structure. Till now only two techniques (and a few variants therein) have been employed for its synthesis, one of them is a solid state reaction between SrCO 3 and TiO 2 at 1100deg, and the other is a coprecipitation of strontium titanyl oxalate followed by calcination at 850deg. As ternary oxides, such as copper chromite, have been prepared by complex formation, the author found it interesting to apply this method to the preparation of strontium titanate. The most easily accessible and versatile complexing agent, EDTA, was used. (author)

  12. Standard free energy of formation of iron iodide

    Science.gov (United States)

    Khandkar, A.; Tare, V. B.; Wagner, J. B., Jr.

    1983-01-01

    An experiment is reported where silver iodide is used to determine the standard free energy of formation of iron iodide. By using silver iodide as a solid electrolyte, a galvanic cell, Ag/AgI/Fe-FeI2, is formulated. The standard free energy of formation of AgI is known, and hence it is possible to estimate the standard free energy of formation of FeI2 by measuring the open-circuit emf of the above cell as a function of temperature. The free standard energy of formation of FeI2 determined by this method is -38784 + 24.165T cal/mol. It is estimated that the maximum error associated with this method is plus or minus 2500 cal/mol.

  13. Study on gold concentrate leaching by iodine-iodide

    Science.gov (United States)

    Wang, Hai-xia; Sun, Chun-bao; Li, Shao-ying; Fu, Ping-feng; Song, Yu-guo; Li, Liang; Xie, Wen-qing

    2013-04-01

    Gold extraction by iodine-iodide solution is an effective and environment-friendly method. In this study, the method using iodine-iodide for gold leaching is proved feasible through thermodynamic calculation. At the same time, experiments on flotation gold concentrates were carried out and encouraging results were obtained. Through optimizing the technological conditions, the attained high gold leaching rate is more than 85%. The optimum process conditions at 25°C are shown as follows: the initial iodine concentration is 1.0%, the iodine-to-iodide mole ratio is 1:8, the solution pH value is 7, the liquid-to-solid mass ratio is 4:1, the leaching time is 4 h, the stirring intensity is 200 r/mim, and the hydrogen peroxide consumption is 1%.

  14. Thermoluminescence of europium-doped zinc oxide exposed to beta particle irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Iriqui R, J. L.; Cruz V, C. [Universidad de Sonora, Departamento de Investigacion en Polimeros y Materiales, Apdo. Postal 130, 83000 Hermosillo, Sonora (Mexico); Bernal, R. [Universidad de Sonora, Departamento de Investigacion en Fisica, Apdo. Postal 5-088, 83000 Hermosillo, Sonora (Mexico); Castano, V. M., E-mail: jorgeiriqui@gimmunison.com [UNAM, Instituto de Fisica, Centro de Fisica Aplicada y Tecnologia Avanzada, Apdo. Postal 1-1010, 76000 Queretaro, Qro. (Mexico)

    2015-10-15

    Full text: Zn O is a promising material for a range of optoelectronics applications, due to its direct wide band gap (E{sub g} ∼3.3 eV at 300 K) and large exciton binding energy (60 MeV). Its applications include UV light emitters, varistors, surface acoustic wave devices, piezoelectric transducers, and chemical and gas sensing. Rare-earth activation of phosphors has long been seen as an effective process since coupling energy into the rare-earth-ion site, either by ionization, charge exchange or a resonance energy process, results in light production. It is reported that Europium modifies the response thermoluminescence (Tl) for pure zinc oxide, when is irradiated with X-ray, created a peak at 365 degrees C. In this work, Zn O:Eu phosphors were synthesized by a chemical method. Some samples were exposed to beta particle irradiation for doses ranging from 1 up to 100 Gy. Tl response as a function of dose is linear throughout the studied dose range. The glow curve exhibits three maxima, centered at 176, 279 and 340 degrees C. The reusability studies obtained after ten repeated cycles of annealing irradiation readout for the Zn O:Eu shows that the variation in the Tl response is ten percent and tends to stabilization. The results indicate that these new Zn O:Eu phosphors are promising detectors and dosimeters for beta radiation. The structural and morphological characterization was carried out by X-ray diffraction and scanning electron microscopy, respectively. (Author)

  15. Perspective: Toward efficient GaN-based red light emitting diodes using europium doping

    Science.gov (United States)

    Mitchell, Brandon; Dierolf, Volkmar; Gregorkiewicz, Tom; Fujiwara, Yasufumi

    2018-04-01

    While InGaN/GaN blue and green light-emitting diodes (LEDs) are commercially available, the search for an efficient red LED based on GaN is ongoing. The realization of this LED is crucial for the monolithic integration of the three primary colors and the development of nitride-based full-color high-resolution displays. In this perspective, we will address the challenges of attaining red luminescence from GaN under current injection and the methods that have been developed to circumvent them. While several approaches will be mentioned, a large emphasis will be placed on the recent developments of doping GaN with Eu3+ to achieve an efficient red GaN-based LED. Finally, we will provide an outlook to the future of this material as a candidate for small scale displays such as mobile device screens or micro-LED displays.

  16. Europium doping in monoclinic KYb(WO{sub 4}){sub 2} crystal

    Energy Technology Data Exchange (ETDEWEB)

    Loiko, P.A. [Física i Cristallografia de Materials i Nanomaterials (FiCMA-FiCNA), Universitat Rovira i Virgili (URV), Campus Sescelades, c/ Marcellí Domingo, s/n., Tarragona, Spain E-43007 (Spain); Center for Optical Materials and Technologies (COMT), Belarusian National Technical University, 65/17 Nezavisimosti Ave., Minsk 220013 (Belarus); Vilejshikova, E.V. [Center for Optical Materials and Technologies (COMT), Belarusian National Technical University, 65/17 Nezavisimosti Ave., Minsk 220013 (Belarus); Mateos, X., E-mail: xavier.mateos@urv.cat [Física i Cristallografia de Materials i Nanomaterials (FiCMA-FiCNA), Universitat Rovira i Virgili (URV), Campus Sescelades, c/ Marcellí Domingo, s/n., Tarragona, Spain E-43007 (Spain); Serres, J.M. [Física i Cristallografia de Materials i Nanomaterials (FiCMA-FiCNA), Universitat Rovira i Virgili (URV), Campus Sescelades, c/ Marcellí Domingo, s/n., Tarragona, Spain E-43007 (Spain); Dunina, E.B.; Kornienko, A.A. [Vitebsk State Technological University, 72 Moskovskaya Ave., Vitebsk 210035 (Belarus); Yumashev, K.V. [Center for Optical Materials and Technologies (COMT), Belarusian National Technical University, 65/17 Nezavisimosti Ave., Minsk 220013 (Belarus); Aguiló, M.; Díaz, F. [Física i Cristallografia de Materials i Nanomaterials (FiCMA-FiCNA), Universitat Rovira i Virgili (URV), Campus Sescelades, c/ Marcellí Domingo, s/n., Tarragona, Spain E-43007 (Spain)

    2017-03-15

    We report on a detailed spectroscopic study of Eu{sup 3+} ions in the monoclinic KYb(WO{sub 4}){sub 2} crystal. The polarized room and low-temperature absorption spectra are measured. The maximum σ{sub abs} corresponding to the {sup 7}F{sub 1} → {sup 5}D{sub 1} transition is 1.32×10{sup –20} cm{sup 2} at 534.2 nm with a bandwidth of 0.7 nm (for E||N{sub m}). The Stark sub-levels of the excited mulitplets are determined. A Judd-Ofelt analysis is applied to the Eu{sup 3+}:KYb(WO{sub 4}){sub 2} crystal to determine the probability of spontaneous transitions, radiative lifetimes and luminescence branching ratios. Within the strong configuration interaction (SCI) approximation, the intensity parameters are Ω{sub 2}=4.757, Ω{sub 4}=2.295, Ω{sub 6}=1.644 [10{sup –20} cm{sup 2}] and Δ{sub f}=50160 cm{sup –1}. The radiative lifetime of the {sup 5}D{sub 0} state is 351 µs. The maximum stimulated-emission cross-section corresponding to the {sup 7}F{sub 1} → {sup 5}D{sub 1} transition is 1.44×10{sup –20} cm{sup 2} at 703.2 nm (for E||N{sub m}). Under UV excitation, the Eu{sup 3+}:KYb(WO{sub 4}){sub 2} crystal provides intense red photoluminescence with CIE coordinates, x=0.675, y=0.325.

  17. Solvothermally synthesized europium-doped CdS nanorods: applications as phosphors

    International Nuclear Information System (INIS)

    Kumar, Sunil; Jindal, Zinki; Kumari, Nitu; Verma, Narendra Kumar

    2011-01-01

    To exploit the photoluminescent behavior of CdS at nanoscale with different doping concentration of europium—a rare earth element, we report the synthesis of Eu-doped CdS nanorods by using low temperature solvothermal process by using ethylenediamine. The outcomes can have future applications as phosphors, photovoltaic cells, lasers, light emitting diodes, bio-imaging, and sensors. The doping was confirmed by electron dispersive spectroscopy supported by X-ray diffraction. From scanning electron microscopy and transmission electron microscopy analysis it was observed that the average diameter of the Cd 1−x Eu x S nanorods is about 10–12 nm having lengths in the range of 50–100 nm. UV–Visible spectroscopy study was carried out to determine the band gap of the nanorods and the absorbance peaks showed blue shift with respect to the bulk CdS. The blue shift was also observed as the doping concentration of Eu increases. From photoluminescence (PL) studies at λ ex = 450 nm, peaks at 528 and 540 nm were observed due to CdS, peak at 570 nm is due to defects related transitions, while the peak at 613 nm is due to Eu. As the doping concentration of Eu is increased the intensity of the luminescent peak at 613 nm is increased. Thermogravimetric analysis showed the nanorods are thermally stable up to 300 °C. The traces of impurities adsorbed on the nanorods were confirmed by Fourier transform infrared spectroscopy.

  18. Two-dimensional high spatial-resolution dosimeter using europium doped potassium chloride: a feasibility study

    International Nuclear Information System (INIS)

    Li, H Harold; Yang, Deshan; Xiao, Zhiyan; Driewer, Joseph P; Han, Zhaohui; Low, Daniel A

    2014-01-01

    Recent research has shown that KCl:Eu 2+  has great potential for use in megavoltage radiation therapy dosimetry because this material exhibits excellent storage performance and is reusable due to strong radiation hardness. This work reports the authors’ attempts to fabricate 2D KCl:Eu 2+  storage phosphor films (SPFs) using both a physical vapor deposition (PVD) method and a tape casting method. X-ray diffraction analysis showed that a 10 µm thick PVD sample was composed of highly crystalline KCl. No additional phases were observed, suggesting that the europium activator had been completely incorporated into the KCl matrix. Photostimulated luminescence and photoluminescence spectra suggested that F (Cl − ) centers were the electron storage centers post x-ray irradiation and that Eu 2+  cations acted as luminescence centers in the photostimulation process. The 150 µm thick casted KCl:Eu 2+  SPF showed sub-millimeter spatial-resolution. Monte Carlo simulations further demonstrated that the admixture of 20% KCl:Eu 2+  and 80% low Z polymer binder exhibited almost no energy-dependence in a 6 MV beam. KCl:Eu 2+  pellet samples showed a large dynamic range from 0.01 cGy to 60 Gy dose-to-water, and saturated at approximately 500 Gy as a result of KCl's intrinsic high radiation hardness. Taken together, this work provides strong evidence that KCl:Eu 2+ -based SPF with associated readout apparatus could result in a novel electronic film system that has all the desirable features associated with classic radiographic film and, importantly, water equivalence and the capability of permanent identification of each detector. (paper)

  19. Nitrogen and europium doped TiO2 anodized films with applications in photocatalysis

    International Nuclear Information System (INIS)

    Chi, Choong-Soo; Choi, Jinwook; Jeong, Yongsoo; Lee, Oh Yeon; Oh, Han-Jun

    2011-01-01

    Micro-arc oxidation method is a useful process for mesoporous titanium dioxide films. In order to improve the photocatalytic activity of the TiO 2 film, N-Eu co-doped titania catalyst was synthesized by micro-arc oxidation in the H 2 SO 4 /Eu(NO 3 ) 3 mixture solution. The specific surface area and the roughness of the anodic titania film fabricated in the H 2 SO 4 /Eu(NO 3 ) 3 electrolyte, were increased compared to that of the anodic TiO 2 film prepared in H 2 SO 4 solution. The absorbance response of N-Eu titania film shows a higher adsorption onset toward visible light region, and the incorporated N and Eu ions during anodization as a dopant in the anodic TiO 2 film significantly enhanced the photocatalytic activity for dye degradation. After dye decomposition test for 3 h, dye removal rates for the anodic TiO 2 film were 60.7% and 90.1% for the N-Eu doped titania film. The improvement of the photocatalytic activity was ascribed to the synergistic effects of the surface enlargement and the new electronic state of the TiO 2 band gap by N and Eu co-doping.

  20. TL process in europium doped alkaline earth sulphate phosphors- a review

    International Nuclear Information System (INIS)

    Bhatt, B.C.

    2003-01-01

    CaSO 4 doped with the rare earth (RE) ion dysprosium or thulium is used routinely as a thermoluminescent dosimeter (TLD) to monitor personal exposure to x- and γ-radiation. The CaSO 4 :Eu phosphor is potentially important for radio photoluminescence (RPL) and ultraviolet (UV) dosimetry. Eu 3+ → Eu 2+ conversion is suggested to play a pivotal role in UV and γ-ray induced thermoluminescence. However, there is disagreement among different workers on the mechanism of gamma and UV induced TL in this phosphor system. This paper will review the work reported on CaSO 4 :Eu and make effects to project overall picture on this phosphor system. (author)

  1. Preparation method and thermal properties of samarium and europium-doped alumino-phosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Sava, B.A., E-mail: savabogdanalexandru@yahoo.com [National Institute of Research and Development for Optoelectronics, Department for Optospintronics, 409 Atomistilor Street, P.O. Box MG – 5, RO-77125 Magurele (Romania); Elisa, M., E-mail: astatin18@yahoo.com [National Institute of Research and Development for Optoelectronics, Department for Optospintronics, 409 Atomistilor Street, P.O. Box MG – 5, RO-77125 Magurele (Romania); Boroica, L., E-mail: boroica_lucica@yahoo.com [National Institute for Lasers, Plasma and Radiation Physics, 77125 Magurele (Romania); Monteiro, R.C.C., E-mail: rcm@fct.unl.pt [Center of Materials Research/Institute for Nanostructures, Nanomodelling and Nanofabrication, (CENIMAT/I3N), Department of Materials Sciences, Faculty of Sciences and Technology, Universidade Nova de Lisboa, 2829-516 Caparica (Portugal)

    2013-12-01

    Highlights: • Improved preparation method of rare-earth-doped phosphate glasses was done. • Working and annealing temperatures were lower than for undoped phosphate glass. • Doped glass viscosity is also lower and has quasi-linear variation with temperature. • Exothermic peak appears at about 555 °C and 685 °C, due to devitrification in glass. -- Abstract: The present work investigates alumino-phosphate glasses from Li{sub 2}O–BaO–Al{sub 2}O{sub 3}–La{sub 2}O{sub 3}–P{sub 2}O{sub 5} system containing Sm{sup 3+} and Eu{sup 3+} ions, prepared by two different ways: a wet raw materials mixing route followed by evaporation and melt-quenching, and by remelting of shards. The linear thermal expansion coefficient measured by dilatometry is identical for both rare-earth-doped phosphate glasses. Comparatively to undoped phosphate glass the linear thermal expansion coefficient increases with 2 × 10{sup −7} K{sup −1} when dopants are added. The characteristic temperatures very slowly decrease but can be considered constant with atomic weight, atomic number and f electrons number of the doping ions in the case of T{sub g} (vitreous transition temperature) and T{sub sr} (high annealing temperature) but slowly increase in the case of T{sub ir} (low annealing temperature–strain point) and very slowly increase, being practically constant in the case of T{sub D} (dilatometric softening temperature). Comparatively to undoped phosphate glass the characteristic temperatures of Sm and Eu-doped glasses present lower values. The higher values of electrical conductance for both doped glasses, comparatively to usual soda-lime-silicate glass, indicate a slightly reduced stability against water. The viscosity measurements, showed a quasi-linear variation with temperature the mean square deviation (R{sup 2}) being ranged between 0.872% and 0.996%. The viscosity of doped glasses comparatively to the undoped one is lower at the same temperature. Thermogravimetric analysis did not show notable mass change for any of doped samples. DSC curves for both rare-earth-doped phosphate glasses, as bulk and powdered samples, showed T{sub g} values in the range 435–450 °C. Bulk samples exhibited a very weak exothermic peak at about 685 °C, while powdered samples showed two weak exothermic peaks at about 555 °C and 685 °C due to devitrification of the glasses. Using designed melting and annealing programs, the doped glasses were improved regarding bubbles and cords content and strain elimination.

  2. Spectroscopic investigation on europium doped heavy metal borate glasses for red luminescent application

    Energy Technology Data Exchange (ETDEWEB)

    Hegde, Vinod; Wagh, Akshatha; Kamath, Sudha D. [Manipal University, Department of Physics, Manipal Institute of Technology, Manipal (India); Hegde, Hemanth [Manipal University, Department of Chemistry, Manipal Institute of Technology, Manipal (India); Vishwanath, C.S.D. [Sri Venkateswara University, Department of Physics, Tirupati (India)

    2017-05-15

    The present study explores a new borate family glasses based on 10ZnO-5Na{sub 2}O-10Bi{sub 2}O{sub 3}-(75 - x) B{sub 2}O{sub 3}-xEu{sub 2}O{sub 3} (x = 0, 0.1, 0.5, 1, 1.5, 2, 3 mol%) composition, synthesized by rapid melt quench technique. Prepared glasses were subjected to the density and refractive index measurements and their values were used to calculate other physical properties of the glass matrix as a function of Eu{sup 3+} concentration. XRD confirmed amorphous nature of the glasses. FTIR spectra in the absorption mode were recorded in the 400-4000 cm{sup -1} region to identify different functional groups in the glass matrix. Deconvoluted FTIR spectra showed increase in BO{sub 4} units with rise in europium content which confirmed the 'network strengthener' role of europium ions by creating bridging oxygens (BOs). Optical properties were investigated for their luminescence behavior through various spectroscopic techniques such as UV-Vis-NIR absorption, excitation, emission, decay profiles, and color measurements at room temperature. Lasing properties of the glasses like total radiative life time, branching ratio, emission cross section, and optical gain were obtained from the calculated Judd-Ofelt (Ω{sub 2},Ω{sub 4}) intensity parameters. From the measured values of emission, cross sections, branching ratios, life times, strong photoluminescence features, and CIE chromaticity coordinates, 0.5 mol% of Eu{sup 3+} ions doped ZnNaBiB glasses showed optimum performance and are potential candidate for red light generation at 613 nm. (orig.)

  3. Characteristics of Un doped and Europium-doped SrI2 Scintillator Detectors

    International Nuclear Information System (INIS)

    Sturm, Benjamin; Cherepy, Nerine; Drury, Owen; Thelin, P.; Fisher, S.E.; O'Neal, S.P.; Payne, Stephen A.; Burger, Arnold; Boatner, Lynn A.; Ramey, Joanne Oxendine; Shah, Kanai; Hawrami, Rastgo

    2012-01-01

    High energy resolution gamma-ray detectors that can be formed into relatively large sizes while operating at room temperature offer many advantages for national security applications. We are working toward that goal through the development of SrI 2 (Eu) scintillator detectors, which routinely provide ;10 cm 3 . In this study, we have tested pure, undoped SrI 2 to gain a better understanding of the scintillation properties and spectroscopic performance achievable without activation. An undoped crystal grown from 99.999% pure SrI 2 pellets was tested for its spectroscopic performance, its light yield, and uniformity of scintillation light collection as a function of gamma-ray interaction position relative to the crystal growth direction. Undoped SrI 2 was found to provide energy resolution of 5.3% at 662 keV, and the light collection nonuniformity varied by only 0.72% over the length of the crystal. Measurements of both a 3% Eu-doped and the undoped SrI 2 crystal were carried out in the SLYNCI facility and indicate differences in their light yield non-proportionality. The surprisingly good scintillation properties of the pure SrI 2 crystal suggests that with high-purity feedstock, further reduction of the Eu concentration can be made to grow larger crystals while not adversely impacting the spectroscopic performance.

  4. Experimental studies of caesium iodide aerosol condensation: theoretical interpretation

    International Nuclear Information System (INIS)

    Beard, A.M.; Benson, C.G.; Horton, K.D.; Buckle, E.R.

    1990-07-01

    Caesium iodide is predicted to be a significant source of fission product aerosols during the course of a severe accident in a pressurised water reactor (PWR). The nucleation and growth of caesium iodide aerosols have been studied using a plume chamber and the results compared with theoretical values calculated using the approach developed by Buckle for aerosol nucleation. The morphology of the particles was studied using scanning electron microscopy (SEM) and transmission optical microscopy (TOM), whilst the particle size distributions were determined from differential mobility (DMPS) and aerodynamic (APS) measurements. (author)

  5. Influence of granular strontium chloride as additives on some ...

    Indian Academy of Sciences (India)

    Influence of granular strontium chloride as additives on some electrical and mechanical properties for pure polyvinyl alcohol. A B Elaydy M Hafez ... Keywords. Polyvinyl-alcohol (PVA); granular strontium chloride, SrCl2; a.c. electrical conductivity; dielectric constant; dielectric loss; Young's modulus; creep relaxation curve.

  6. Thermal reactions of some calcium, strontium, and barium chromates

    International Nuclear Information System (INIS)

    Piekarska-Piesse, B.; Gontarz, Z.; Ostrowski, A.; Kucharski, R.

    2000-01-01

    Thermal decomposition of calcium chromates and solid state reactions of barium and strontium chromates(VI) with barium and strontium hydroxides and carbonates, as well as the reduction of chromates by carbon and hydrogen, have been investigated. The mechanisms of individual stages of the thermal decomposition have been proposed on the basis of morphological classification. (author)

  7. Strontium-90 and cesium-137 in powdered milk

    International Nuclear Information System (INIS)

    1977-01-01

    Japan Chemical Analysis Center has analysed the strontium-90 and cesium-137 content in powdered milk. The samples were purchased on the open market in Tokyo from the powdered milk producers. The analysis of Strontium-90 and Cesium-137 content was carried out using the method recommended by Science and Technology Agency. (author)

  8. Reduced-graphene-oxide-and-strontium-titanate-based double

    Indian Academy of Sciences (India)

    Microwave-absorbing materials based on reduced graphene oxide (r-GO)/ strontium titanate were prepared by embedding in epoxy matrix. R-GO and strontium titanate were synthesized and characterized before composite fabrication. Microstructures of the constituent elements were studied by scanning electron ...

  9. Thermal conductivity reduction in oxygen-deficient strontium titanates

    NARCIS (Netherlands)

    Yu, Choongho; Scullin, Matthew L.; Huijben, Mark; Ramesh, Ramamoorthy; Majumdar, Arun

    2008-01-01

    We report significant thermal conductivity reduction in oxygen-deficient lanthanum-doped strontium titanate (Sr1−xLaxTiO3−δ) films as compared to unreduced strontium titanates. Our experimental results suggest that the oxygen vacancies could have played an important role in the reduction. This could

  10. 40 CFR 721.10011 - Barium calcium manganese strontium oxide.

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Barium calcium manganese strontium... Specific Chemical Substances § 721.10011 Barium calcium manganese strontium oxide. (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified as barium calcium...

  11. Uptake behavior of titanium molybdophosphate for cesium and strontium

    International Nuclear Information System (INIS)

    Yavari, R.; Ahmadi, S.J.; Huang, Y.D.

    2010-01-01

    This study investigates uptake of cesium and strontium from aqueous solution similar to nuclear waste on three samples of titanium molybdophosphate (TMP) synthesized under various conditions. Effects of concentration of sodium nitrate, pH and contact time on the uptake of cesium and strontium have been studied by bath method. The results showed that TMP has high affinity toward cesium and strontium at pH > 2 and relatively low concentration of sodium nitrate. Kinetic data indicated that cesium uptake process to achieve equilibrium was faster than strontium. Cesium and strontium breakthrough curves were examined at 25 deg C using column packed with H 3 O + form of TMP and breakthrough curves showed symmetrical S-shaped profiles. At the same time, the calculated breakthrough capacity for cesium was higher than strontium. The results of desorption studies showed that over 99% of cesium and strontium was washed out of column by using 4 M NH 4 Cl solution. This study suggests that TMP can have great potential applications for the removal of strontium and specially cesium from nuclear waste solution. (author)

  12. Electronic properties and Compton profiles of silver iodide

    Indian Academy of Sciences (India)

    We have carried out an extensive study of electronic properties of silver iodide in - and -phases. The theoretical Compton profiles, energy bands, density of states and anisotropies in momentum densities are computed using density functional theories. We have also employed full-potential linearized augmented ...

  13. Effects of Potassium Iodide on Low Avid Immunological Reactions ...

    African Journals Online (AJOL)

    In identical test conditions keeping appropriate control, the following ... Abstract. Background: Selective in‑vivo anti‑fungal action of potassium iodide (KI) is an enigma, but .... mechanism of action of the drug against selective infections. In fact, if ...

  14. Research on solubility characteristics of gaseous methyl iodide

    International Nuclear Information System (INIS)

    Zhou Yanmin; Sun Zhongning; Gu Haifeng; Wang Junlong

    2014-01-01

    With the deionized water as the absorbent, the solubility characteristics of the gaseous methyl iodide were studied under different temperature and pressure conditions, using a dynamic measuring method. The results show that within the range of experiment parameters, namely temperature is below 80℃ and pressure is lower than 0.3 MPa, the physical dissolution process of gaseous methyl iodide in water obeys Henry's law. The solubility coefficient under different temperature and pressure conditions was calculated based on the measurement results. Further research indicates that at atmospheric pressure, the solubility coefficient of methyl iodide in water decreases exponentially with the increase of temperature. While the pressure changes from 0.1 MPa to 0.3 MPa with equal interval, the solubility coefficient also increases linearly. The variation of the solubility coefficient with temperature under different pressure conditions all decreases exponentially. An equation is given to calculate the solubility coefficient of methyl iodide under different pressure and temperature conditions. (authors)

  15. Gravimetric determination of cadmium with o-phenanthroline and iodide

    International Nuclear Information System (INIS)

    Yoshida, Hitoshi; Mizuno, Kazunori; Taga, Mitsuhiko; Hikime, Seiichiro

    1976-01-01

    Cadmium forms insoluble mixed ligand complex with o-phenanthroline and iodide ions. By using the complex a new gravimetric method for the determination of cadmium was investigated. The recommended analytical procedure is as follows: Adjust pH value of a solution containing 5 to 45 mg cadmium to 4 with 3 M acetic acid-sodium acetate buffer solution. Add over threefold moles of potassium iodide to the solution and heat to just before boiling. To the solution add 0.1% ascorbic acid solution and then 0.1 M o-phenanthroline solution drop by drop in excess with stirring, and cool the mixture to room temperature. Filter the precipitates and wash first with 0.01% potassium iodide solution and then with water. Dry the precipitates at 110 0 C for two hours and weigh as Cd(o-phen) 2 I 2 (I). The gravimetric factor of the complex for cadmium is 0.1547. Chemical composition of the precipitate is variable when o-phenanthroline is added less than twofold moles to cadmium. Adding the o-phenanthroline solution 2.4-fold moles against cadmium, the ternary complex (I) precipitates quantitatively. Though a large excess of iodide ion in the solution contaminated the precipitate, the contamination was avoided when precipitation was carryed out at high temperature and in the presence of ascorbic acid. By the presented procedure 5 to 45 mg of cadmium are determined with a standard deviation of 0 C. (JPN)

  16. Kinetic method for determination of iodide ion ultramicroamounts

    International Nuclear Information System (INIS)

    Barkauskas, Yu.K.; Ramanauskas, Eh.I.

    1980-01-01

    A kinetic method for iodides ultramicroamount determination from their catalytic effect on oxidation of malachite green with chloramine B in the presence of acetone at pH 5.78+-0.3 is developed. The induction period of the reaction is determined from a change in the redox potential of the system. The induction period is proportional to the iodides concentration. Determination limit of iodides is equal to 4 μg iodide per 100 l of solution. More than 10 5 -multiple amounts of K + , Na + , NH 4+ , Ba 2 + , Al 3 + , Cu 2 + , Mg 2 + , SO 4 2 - , Cl - , MoO 4 2 - , NO 3- , ClO 3- , IO 3- , IO 4- , ClO 4- , BrO 3- ; 10 5 -10 3 -multiple amounts of Cr 3 + , Fe 3 + , Sn 2 + , S 2 - , MnO 4- , NO 2- etc. do not interfere with the determination, while 10-multiple amounts of SCN, 0.2-multiple quantities of Ag + , Hg 2 2 + do

  17. Confinement Effects in Low-Dimensional Lead Iodide Perovskite Hybrids

    NARCIS (Netherlands)

    Kamminga, Machteld E.; Fang, Honghua; Filip, Marina R.; Giustino, Feliciano; Baas, Jacobus; Blake, Graeme R.; Loi, Maria Antonietta; Palstra, Thomas T. M.

    2016-01-01

    We use a layered solution crystal growth technique to synthesize high-quality single crystals of phenylalkylammonium lead iodide organic/inorganic hybrid compounds. Single-crystal X-ray diffraction reveals low-dimensional structures consisting of inorganic sheets separated by bilayers of the organic

  18. Temperature Dependent Charge Carrier Dynamics in Formamidinium Lead Iodide Perovskite

    NARCIS (Netherlands)

    Gelvez Rueda, M.C.; Renaud, N.; Grozema, F.C.

    2017-01-01

    The fundamental opto-electronic properties of organic-inorganic hybrid perovskites are strongly affected by their structural parameters. These parameters are particularly critical in formamidinium lead iodide (FAPbI3), in which its large structural disorder leads to a non-perovskite

  19. Detection of apoptotic cells using propidium iodide staining

    NARCIS (Netherlands)

    Newbold, Andrea; Martin, Ben P.; Cullinane, Carleen; Bots, Michael

    2014-01-01

    Flow cytometry assays are often used to detect apoptotic cells in in vitro cultures. Depending on the experimental model, these assays can also be useful in evaluating apoptosis in vivo. In this protocol, we describe a propidium iodide (PI) flow cytometry assay to evaluate B-cell lymphomas that have

  20. Calcium versus strontium handling by the heart muscle.

    Science.gov (United States)

    Hendrych, Michal; Olejnickova, Veronika; Novakova, Marie

    2016-01-01

    Calcium plays a crucial role in numerous processes in living systems, from both intracellular and intercellular signalling to blood clotting. Calcium can be replaced by strontium in various intracellular processes due to high level of their similarity and strontium thus may serve as a valuable tool for different experimental studies. On the other hand, strontium is also used in clinical medicine and is commonly taken to the human body with food and water. The negative cardiac side effects of strontium therapy of osteoporosis and bone metastases are well known, but still not fully explained. This fact explains enhanced interest in this element and its impact on human body. This article reviews effects of calcium and strontium on several biochemical and physiological processes, with special emphasis on cardiac muscle.

  1. Strontium 90 in silts of the Dnieper cascade water reservoirs

    International Nuclear Information System (INIS)

    Romanenko, V.D.; Kuz'menko, M.I.; Matvienko, L.P.; Klenus, V.G.; Nasvit, O.I.

    1989-01-01

    The change of strontium-90 content in water and silts of the Dnieper cascade water reservoirs was analyzed. It was shown, that decrease of strontium-90 content in water in time connected basically with ion exchange adsorption of strontium-90 by residues. A high sorption ability of residues made it possible for radioisotopes to reduce sharply their concentration along depth of soils. The highest concentration of radioisotopes was in the upper layers, enriched by silt. It was ascertained, that strontium-90 migration along depth of residues took place rapidly in the Kiev's water reservoir. Down the cascade strontium-90 content reduced in lower layers of residues as well as in upper layers. 4 tabs

  2. Strontium Promotes Cementoblasts Differentiation through Inhibiting Sclerostin Expression In Vitro

    Directory of Open Access Journals (Sweden)

    Xingfu Bao

    2014-01-01

    Full Text Available Cementogenesis, performed by cementoblasts, is important for the repair of root resorption caused by orthodontic treatment. Based on recent studies, strontium has been applied for osteoporosis treatment due to its positive effect on osteoblasts. Although promising, the effect of strontium on cementoblasts is still unclear. So the aim of this research was to clarify and investigate the effect of strontium on cementogenesis via employing cementoblasts as model. A series of experiments including MTT, alkaline phosphatase activity, gene analysis, alizarin red staining, and western blot were carried out to evaluate the proliferation and differentiation of cementoblasts. In addition, expression of sclerostin was checked to analyze the possible mechanism. Our results show that strontium inhibits the proliferation of cementoblasts with a dose dependent manner; however, it can promote the differentiation of cementoblasts via downregulating sclerostin expression. Taking together, strontium may facilitate cementogenesis and benefit the treatment of root resorption at a low dose.

  3. FY-2015 Methyl Iodide Deep-Bed Adsorption Test Report

    Energy Technology Data Exchange (ETDEWEB)

    Soelberg, Nicholas Ray [Idaho National Lab. (INL), Idaho Falls, ID (United States); Watson, Tony Leroy [Idaho National Lab. (INL), Idaho Falls, ID (United States)

    2015-09-30

    Nuclear fission produces fission and activation products, including iodine-129, which could evolve into used fuel reprocessing facility off-gas systems, and could require off-gas control to limit air emissions to levels within acceptable emission limits. Deep-bed methyl iodide adsorption testing has continued in Fiscal Year 2015 according to a multi-laboratory methyl iodide adsorption test plan. Updates to the deep-bed test system have also been performed to enable the inclusion of evaporated HNO3 and increased NO2 concentrations in future tests. This report summarizes the result of those activities. Test results showed that iodine adsorption from gaseous methyl iodide using reduced silver zeolite (AgZ) resulted in initial iodine decontamination factors (DFs, ratios of uncontrolled and controlled total iodine levels) under 1,000 for the conditions of the long-duration test performed this year (45 ppm CH3I, 1,000 ppm each NO and NO2, very low H2O levels [3 ppm] in balance air). The mass transfer zone depth exceeded the cumulative 5-inch depth of 4 bed segments, which is deeper than the 2-4 inch depth estimated for the mass transfer zone for adsorbing I2 using AgZ in prior deep-bed tests. The maximum iodine adsorption capacity for the AgZ under the conditions of this test was 6.2% (6.2 g adsorbed I per 100 g sorbent). The maximum Ag utilization was 51%. Additional deep-bed testing and analyses are recommended to (a) expand the data base for methyl iodide adsorption and (b) provide more data for evaluating organic iodide reactions and reaction byproducts for different potential adsorption conditions.

  4. FY-2015 Methyl Iodide Deep-Bed Adsorption Test Report

    International Nuclear Information System (INIS)

    Soelberg, Nicholas Ray; Watson, Tony Leroy

    2015-01-01

    Nuclear fission produces fission and activation products, including iodine-129, which could evolve into used fuel reprocessing facility off-gas systems, and could require off-gas control to limit air emissions to levels within acceptable emission limits. Deep-bed methyl iodide adsorption testing has continued in Fiscal Year 2015 according to a multi-laboratory methyl iodide adsorption test plan. Updates to the deep-bed test system have also been performed to enable the inclusion of evaporated HNO 3 and increased NO 2 concentrations in future tests. This report summarizes the result of those activities. Test results showed that iodine adsorption from gaseous methyl iodide using reduced silver zeolite (AgZ) resulted in initial iodine decontamination factors (DFs, ratios of uncontrolled and controlled total iodine levels) under 1,000 for the conditions of the long-duration test performed this year (45 ppm CH3I, 1,000 ppm each NO and NO 2 , very low H 2 O levels [3 ppm] in balance air). The mass transfer zone depth exceeded the cumulative 5-inch depth of 4 bed segments, which is deeper than the 2-4 inch depth estimated for the mass transfer zone for adsorbing I 2 using AgZ in prior deep-bed tests. The maximum iodine adsorption capacity for the AgZ under the conditions of this test was 6.2% (6.2 g adsorbed I per 100 g sorbent). The maximum Ag utilization was 51%. Additional deep-bed testing and analyses are recommended to (a) expand the data base for methyl iodide adsorption and (b) provide more data for evaluating organic iodide reactions and reaction byproducts for different potential adsorption conditions.

  5. Nondestructive measurement of environmental radioactive strontium

    Directory of Open Access Journals (Sweden)

    Saiba Shuntaro

    2014-03-01

    Full Text Available The Fukushima Daiichi nuclear power plant accident was triggered by the 2011 Great East Japan Earthquake. The main radioactivity concerns after the accident are I-131 (half-life: 8.0 days, Cs-134 (2.1 years, Cs-137 (30 years, Sr-89 (51 days, and Sr-90 (29 years. We are aiming to establish a new nondestructive measurement and detection technique that will enable us to realize a quantitative evaluation of strontium radioactivity without chemical separation processing. This technique is needed to detect radiation contained in foods, environmental water, and soil, to prevent us from undesired internal exposure to radiation.

  6. Strontium-90 and promethium-147 recovery

    International Nuclear Information System (INIS)

    Hoisington, J.E.; McDonell, W.R.

    1982-01-01

    Strontium-90 and promethium-147 are fission product radionuclides with potential for use as heat source materials in high reliability, non-interruptible power supplies. Interest has recently been expressed in their utilization for Department of Defense (DOD) applications. This memorandum summarizes the current inventories, the annual production rates, and the possible recovery of Sr-90 and Pm-147 from nuclear materials production operations at Hanford and Savannah River. Recovery of these isotopes from LWR spend fuel utilizing the Barnwell Nuclear Fuels Plant (BNFP) is also considered. Unit recovery costs at each site are provided

  7. Kinetic method for determination of iodide ion ultramicroamounts. Kineticheskij sposob opredeleniya ul'tramikrokolichestv iodid-ionov

    Energy Technology Data Exchange (ETDEWEB)

    Barkauskas, Yu K; Ramanauskas, Eh I

    1980-04-03

    A kinetic method for iodides ultramicroamount determination from their catalytic effect on oxidation of malachite green with chloramine B in the presence of acetone at pH 5.78+-0.3 is developed. The induction period of the reaction is determined from a change in the redox potential of the system. The induction period is proportional to the iodides concentration. Determination limit of iodides is equal to 4 ..mu..g iodide per 100 l of solution. More than 10/sup 5/-multiple amounts of K/sup +/, Na/sup +/, NH/sub 4//sup +/, Ba/sup 2 +/, Al/sup 3 +/, Cu/sup 2 +/, Mg/sup 2 +/, SO/sub 4//sup 2 -/, Cl/sup -/, MoO/sub 4//sup 2 -/, NO/sub 3//sup -/, ClO/sub 3//sup -/, IO/sub 3//sup -/, IO/sub 4//sup -/, ClO/sub 4//sup -/, BrO/sub 3//sup -/; 10/sup 5/-10/sup 3/-multiple amounts of Cr/sup 3 +/, Fe/sup 3 +/, Sn/sup 2 +/, S/sup 2 -/, MnO/sub 4//sup -/, NO/sub 2//sup -/ etc. do not interfere with the determination, while 10-multiple amounts of SCN, 0.2-multiple quantities of Ag/sup +/, Hg/sub 2//sup 2 +/ do.

  8. Investigation of strontium accumulation on ovariectomized Sprague–Dawley rat tibia by micro-PIXE

    Energy Technology Data Exchange (ETDEWEB)

    Li, X.; Li, Y. [Institute of Modern Physics, Fudan University, Shanghai 200433 (China); Jin, W. [Institute of Radiation Medicine, Fudan University, Shanghai 200032 (China); Zheng, Y.; Rong, C.; Lyu, H. [Institute of Modern Physics, Fudan University, Shanghai 200433 (China); Shen, H., E-mail: haoshen@fudan.edu.cn [Institute of Modern Physics, Fudan University, Shanghai 200433 (China)

    2014-08-01

    Strontium ranelate is a newly developed drug effective in osteoporosis treatment by depressing bone resorption and maintaining bone formation. Strontium accumulation and distribution are determined in bones of rat after strontium ranelate administration by using micro-PIXE. The investigated rats are divided into four groups: (A) control, (B) ovariectomized, (C) ovariectomized followed with strontium chloride, (D) ovariectomized followed with strontium ranelate. It was found that strontium ranelate would result in increasing trabecular volume and decreasing bone resorption to treat osteoporosis. There are similar contours of calcium and strontium in two-dimensional images, while the strontium is not evenly distributed in the bone. It supports the conclusion that strontium has an affinity for bone and it is capable of replacing calcium atoms as a part of the strontium mechanism in the osteoporosis treatment. The results related to biochemistry are also discussed.

  9. Leaching of strontium sulfide from produced clinker in conversion furnace

    International Nuclear Information System (INIS)

    Ghorbanian, S. A.; Salehpour, A. R.; Radpour, S. R.

    2009-01-01

    Iran is rich in mineral resources one of which is mineral Celestine. Basing on current estimations, the capacity of mineral Celestine is over two million tons, 75-95% of which is strontium sulfate. However; in industries such as Color cathode Ray Tubes, pyrochemical processes, ceramics, paint production, zinc purification processes; strontium sulfate is not a direct feed, rather it is largely consumed in the form of strontium carbonate. Two conventional methods are used to produce strontium carbonate from the sulfate; that is direct reaction and black ash methods. Strontium sulfide, as an intermediate component has a key role in black ash process including strontium sulfate reduction by coke, hence producing and leaching the strontium sulfide by hot water. Finally the reaction of strontium sulfate with sodium carbonate lead to strontium carbonate. In this paper, a system was designed to analyze and optimize the process parameters of strontium sulfide production which is less expensive and available solvent in water. Fundamentally, when strontium sulfide becomes in contact with strontium sulfate; Sr(SH) 2 , and Sr(OH) 2 , are produced. The solubility of strontium sulfide depends on water temperature and the maximum solubility achieved at 90 d egree C . The results showed that in the experimental scale, at water to SrS ratio of 6; they sediment for 45 minutes at 95 d egree C in five operational stages; the separation of 95 and 97.1 percent of imported SrS is possible in effluent of fourth and fifth stages, respectively. Thus; four leaching stages could be recommended for pilot scale plants. Also, the results show that at water to SrS ratio of 8, 40 minutes sedimentation at 85-95 d egree C in one operational stage, the separation of 95 percent separation of inputted SrS, is possible. Solvent leaching process is continued till no smell of sulfur components is felt. It could be used as a key role to determine the number of leaching stages in experiments. Finally, the

  10. Laser Stabilization with Laser Cooled Strontium

    DEFF Research Database (Denmark)

    Christensen, Bjarke Takashi Røjle

    The frequency stability of current state-of-the-art stabilized clock lasers are limited by thermal fluctuations of the ultra-stable optical reference cavities used for their frequency stabilization. In this work, we study the possibilities for surpassing this thermal limit by exploiting the nonli......The frequency stability of current state-of-the-art stabilized clock lasers are limited by thermal fluctuations of the ultra-stable optical reference cavities used for their frequency stabilization. In this work, we study the possibilities for surpassing this thermal limit by exploiting...... the nonlinear effects from coupling of an optical cavity to laser cooled atoms having a narrow transition linewidth. Here, we have realized such a system where a thermal sample of laser cooled strontium-88 atoms are coupled to an optical cavity. The strontium-88 atoms were probed on the narrow 1S0-3P1 inter......-combination line at 689 nm in a strongly saturated regime. The dynamics of the atomic induced phase shift and absorption of the probe light were experimentally studied in details with the purpose of applications to laser stabilization. The atomic sample temperature was in the mK range which brought this system out...

  11. Sodium iodide symporter: Its role in nuclear oncology

    International Nuclear Information System (INIS)

    Chung, June-Key

    2004-01-01

    Full text: Thyroid iodide uptake is basic to the clinical applications of radioiodine in diagnosis and therapy. Iodide uptake occurs across the membrane of thyroid follicular cells via an active transporter process mediated by the sodium/iodide symporter (NIS). The recent cloning of the gene encoding NIS enabled better characterization of the molecular mechanisms underlying the iodide transport, thus opening the way to clarify and expand its role in medicine. NIS contains 13 transmembrane segments, and its gene encodes a glycoprotein of 643 amino acids. Decreased NIS expression levels account for the reduced iodide uptake in thyroid carcinomas. We found that thyroid cancer patients with positive immunostaining for NIS responded to I-131 therapy better than did the patients with negative immunostaining. Thus, NIS gene can be used for radionuclide gene therapy. Targeted expression of functional NIS in cancer cells would enable these cells to concentrate iodide from plasma and would, therefore, offer the possibility of radioiodine therapy. We and others have shown that gene transfer of NIS into a variety of cell types confers increased radioiodine uptake up to several hundred-fold that of controls. There is great interest in exploring the possibility of NIS gene transfer to facilitate radioiodine therapy for non-thyroidal human cancers including hepatoma, prostate, breast, colon cancers as well as thyroid cancer. Recently, several approaches such as, targeted gene transfer, thyroid peroxidase gene co-transfection, retinoic acid treatment and Re-188 therapy instead of I-131, have been tried to improve this novel gene therapy. Imaging reporter gene is useful in non-invasively determining the location, duration and magnitude of transgene expression in living animal. Conventionally, HSV-tk and dopaminergic receptor (D2R) genes have been presented as possible imaging reporter genes. We proved that NIS could serve as an alternative imaging reporter gene. NIS has many

  12. A study on characteristic of selective membrane for strontium analysis

    Energy Technology Data Exchange (ETDEWEB)

    Moon, Seung Hyun; Choi, Young Woo [Kwang-ju Institute of Science and Technology, Kwangju (Korea)

    1999-04-01

    In this study, supported liquid membranes (SLMs) using crown ether were prepared in order to separate strontium ion selectively from a calcium contained solution However, at the higher than 3 N nitric acid concentration of a strip solution, stability of a SLM was declined remarkably owing to the hasty loss of carrier impregnated in supporter and, on account of this phenomena, facilitated transports were not accomplished. And DC18C6 as a neutral carrier affected remarkably the selectivity of strontium and the factor determining permeabilities of metal ions was as a role of DNNS. Consequently, in order to be a optimal SLM for the high permeability and the stable selectivity of strontium, concentration of DC18C6 and DNNS should be 0.1 M and 25 mM, respectively and, at this condition, the relative removal ratio of strontium to calcium was 93.3%. And the change of calcium concentration in the feed solution affected the permeability of strontium. In particular, when the ratio of strontium to calcium concentration in the feed solution was in the range of 1/5 - 1/50, strontium could be separated selectively at stable permeabilities. (author). 17 refs., 19 figs., 3 tabs.

  13. Strontium-90 and cesium-137 in freshwater from May 1984

    International Nuclear Information System (INIS)

    1984-01-01

    Strontium-90 and cesium-137 in freshwater measured in May 1984 are given in pCi/l. The sampling point is 1, Kasumigaura-Lake (Ibaraki). Collection and pretreatment of samples, preparation of samples for analysis, separation of strontium-90 and cesium-137, determination of stable strontium, calcium and potassium, and counting are described. The sample was passed through a cation exchange column. After the radiochemical separation, the mounted precipitates were counted for activity using low background beta counters normally for 60 minutes. (Mori, K.)

  14. Crystallization of carbonate hydroxyapatite in the presence of strontium ranelate

    Science.gov (United States)

    Izmailov, R. R.; Golovanova, O. A.

    2015-11-01

    The influence of strontium ranelate on the crystallization of carbonate hydroxyapatite from a prototype of synovial fluid of humans has been investigated. The synthesis products are studied by IR Fourier spectroscopy, X-ray diffraction, and differential thermal analysis. The amount of strontium in the samples is determined by atomic emission analysis. The sizes of crystallites in the synthesized phases are calculated from the Selyakov-Scherrer formula; the lattice parameters are also determined. The phases obtained are found to be species of calcium-deficient strontium-containing carbonate hydroxyapatite of mixed A and B types. Schemes of chemical reactions occurring during heat treatment are proposed.

  15. Isomorfic Substitutions of Calcium by Strontium in Calcium Hydroxyapatite

    Energy Technology Data Exchange (ETDEWEB)

    Christensen, Hilbert

    1962-12-15

    By means of homogeneous precipitation it has been possible to synthesize crystalline solid solutions of calcium strontium hydroxyapatite from aqueous solutions. The lattice constants for the solid solutions were measured in the range Ca{sub 9}Sr(PO{sub 4}){sub 6}(OH){sub 2} - CaSr{sub 9}(PO{sub 4}){sub 6}(OH){sub 2}. The investigations show that the discrimination of strontium against calcium is considerably smaller than reported elsewhere (1). Strontium is preferentially built into the c-axis direction of the apatite lattice.

  16. Behaviour of organic iodides under pwr accident conditions

    International Nuclear Information System (INIS)

    Alm, M.

    1982-01-01

    Laboratory experiments were performed to study the behaviour of radioactive methyl iodide under PWR loss-of-coolant conditions. The pressure relief equipment consisted of an autoclave for simulating the primary circuit and of an expansion vessel for simulating the conditions after a rupture in the reactor coolant system. After pressure relief, the composition of the CH 3 sup(127/131)I-containing steam-air mixture within the expansion vessel was analysed at 80 0 C over a period of 42 days. On the basis of the values measured and of data taken from the literature, both qualitative and quantitative assessments have been made as to the behaviour of radioactive methyl iodide in the event of loss-of-coolant accidents. (author)

  17. Strontium D-Glutamate Hexahydrate and Strontium Di(hydrogen L-glutamate) Pentahydrate

    DEFF Research Database (Denmark)

    Christgau, Stephan; Odderhede, Jette; Stahl, Kenny

    2005-01-01

    Sr(C5H7NO4)] center dot 6H(2)O, ( I), and [Sr(C5H8NO4)(2)] center dot 5H(2)O, (II), both crystallize with similar strontium - glutamate - water layers. In ( I), the neutral layers are connected through hydrogen bonds by water molecules, while in ( II), the positively charged layers are connected...... through hydrogen bonds and electrostatic interactions by interleaving layers of hydrogen glutamate anions and water molecules....

  18. Growth of mercuric iodide single crystals from dimethylsulfoxide

    International Nuclear Information System (INIS)

    Carlston, R.C.

    1976-01-01

    Dimethylsulfoxide is used as a solvent for the growth of red mercuric iodide (HgI 2 ) crystals for use in radiation detectors. The hygroscopic property of the solvent allows controlled amounts of water to enter into the solvent phase and diminish the large solubility of HgI 2 so that the precipitating solid collects as well-defined euhedral crystals which grow into a volume of several cc

  19. 1-(3-Iodopropyl-4-methylquinolin-1-ium Iodide

    Directory of Open Access Journals (Sweden)

    Todor Deligeorgiev

    2015-11-01

    Full Text Available A solvent-free “one-pot” synthetic approach to 1-(3-iodopropyl-4-methylquinolin-1-ium iodide is reported in the present work. The title compound is derived from N-alkylation of 4-methylquinoline with 1,3-diiodopropane proceeded at room temperature. The target quinolinium salt is obtained in a highly pure form. It’s structure was evaluated by 1H-NMR, 13C-NMR, and DEPT135 spectra.

  20. FY-2016 Methyl Iodide Higher NOx Adsorption Test Report

    Energy Technology Data Exchange (ETDEWEB)

    Soelberg, Nicholas Ray [Idaho National Lab. (INL), Idaho Falls, ID (United States); Watson, Tony Leroy [Idaho National Lab. (INL), Idaho Falls, ID (United States)

    2016-09-01

    Deep-bed methyl iodide adsorption testing has continued in Fiscal Year 2016 under the Department of Energy (DOE) Fuel Cycle Technology (FCT) Program Offgas Sigma Team to further research and advance the technical maturity of solid sorbents for capturing iodine-129 in off-gas streams during used nuclear fuel reprocessing. Adsorption testing with higher levels of NO (approximately 3,300 ppm) and NO2 (up to about 10,000 ppm) indicate that high efficiency iodine capture by silver aerogel remains possible. Maximum iodine decontamination factors (DFs, or the ratio of iodine flowrate in the sorbent bed inlet gas compared to the iodine flowrate in the outlet gas) exceeded 3,000 until bed breakthrough rapidly decreased the DF levels to as low as about 2, when the adsorption capability was near depletion. After breakthrough, nearly all of the uncaptured iodine that remains in the bed outlet gas stream is no longer in the form of the original methyl iodide. The methyl iodide molecules are cleaved in the sorbent bed, even after iodine adsorption is no longer efficient, so that uncaptured iodine is in the form of iodine species soluble in caustic scrubber solutions, and detected and reported here as diatomic I2. The mass transfer zone depths were estimated at 8 inches, somewhat deeper than the 2-5 inch range estimated for both silver aerogels and silver zeolites in prior deep-bed tests, which had lower NOx levels. The maximum iodine adsorption capacity and silver utilization for these higher NOx tests, at about 5-15% of the original sorbent mass, and about 12-35% of the total silver, respectively, were lower than for trends from prior silver aerogel and silver zeolite tests with lower NOx levels. Additional deep-bed testing and analyses are recommended to expand the database for organic iodide adsorption and increase the technical maturity if iodine adsorption processes.

  1. Photochemical versus biological production of methyl iodide during Meteor 55

    Science.gov (United States)

    Richter, U.; Wallace, D.

    2003-04-01

    The flux of methyl iodide from sea to air represents the largest flux of iodine from the ocean to the atmosphere. Surface water concentrations and hence fluxes are particularly high in tropical regions. This flux may be responsible for the enrichment of iodine in the marine aerosol and may contribute to important processes in the marine boundary layer, including particle formation. Methyl iodide is commonly referred to as a biogenic gas, with both macroalgae and phytoplankton identified as important sources. On the other hand experimental and field data have shown the importance of photochemical production that is not necessarily associated directly with biological activity. During the Meteor cruise 55 along 11°N in the tropical Atlantic Ocean, a series of experiments were conducted to examine the biological vs. photochemical production of methyl iodide. A total of eight separate experiments were conducted. Production of CH3I in quartz glass flasks during 24 hour incubations (dark and natural sunlight) was measured under three experimental treatments: untreated seawater, filtered seawater (0.1 um pore size filter to exclude most phytoplankton and bacteria), and seawater that was poisoned with mercuric chloride. There were two clear findings from these experiments: (1) methyl iodide production was significantly higher in all the incubations that were exposed to the light than in the dark incubations; (2) there was no significant difference between CH3I production under the three experimental treatments. These results argue very strongly for the primary importance of photochemical production of CH3I as opposed to biogenic production at least for the tropical open ocean surface waters. Further experiments are required to investigate the reactants involved, their sources, the wavelength and depth dependence of production, etc. as well as (possibly related) sink processes.

  2. Synthesis and evaluation of iodide uptake inhibitors in thyroid gland

    International Nuclear Information System (INIS)

    Lacotte, Pierre

    2012-01-01

    This work was intended to discover small organic molecules acting as iodide uptake inhibitors in thyroid cells. These compounds can indeed be derivatized into biochemical probes for further characterization of proteins involved in iodide transport mechanisms. On the long term, these inhibitors also appear as attractive drug candidates for treatment of thyroid pathologies or radioprotection against iodine isotopes. A similar strategy was adopted for both of the two inhibitor families. First, we synthesized a chemical library of around 100 analogues; we measured their IC50 against iodide uptake in FRTL-5 cells to get structure-activity relationships. Absolute configuration of stereo-genic centers was also investigated, and a preferential stereochemistry was found to be responsible for activity. From this basis, around twenty 'second-generation' analogues were synthesized by combining fragments contributing to biological activity. Biological evaluation indicated that nine were very potent inhibitors, with IC50 ≤ 6 nM and satisfying physicochemical properties required for drug candidates. Finally, one photoactivatable biotinylated probe was developed in each family and used for photoaffinity labeling. Several specifically labeled proteins are still under identification and constitute new potential therapeutic targets. (author)

  3. The sodium iodide symporter: its implications for imaging and therapy

    International Nuclear Information System (INIS)

    Spitzweg, C.

    2007-01-01

    The sodium iodide symporter (NIS) is an intrinsic plasma membrane glycoprotein that mediates the active transport of iodide in the thyroid gland and a number of extrathyroidal tissues, in particular lactating mammary gland. In addition to its key function in thyroid physiology, NIS-mediated iodide accumulation allows diagnostic thyroid scintigraphy as well as therapeutic radioiodine application in benign and malignant thyroid disease. NIS therefore represents one of the oldest targets for molecular imaging and therapy. Based on the effective administration of radioiodine that has been used for over 60 years in the management of follicular cell-derived thyroid cancer, cloning and characterization of the NIS gene has paved the way for the development of a novel cytoreductive gene therapy strategy based on targeted NIS expression in thyroidal and nonthyroidal cancer cells followed by therapeutic application of 131 I or alternative radionuclides, including 188 Re and 211 At. In addition, the possibility of direct and non-invasive imaging of functional NIS expression by 123 I- and 99m Tc-scintigraphy or 124 I-PET-imaging allows the application of NIS as a novel reporter gene. In conclusion, the dual role of NIS as diagnostic and therapeutic gene and the detection of extra-thyroidal endogenous NIS expression in breast cancer open promising perspectives in nuclear medicine and molecular oncology for diagnostic and therapeutic application of NIS outside the thyroid gland. (orig.)

  4. Enhanced iodide sequestration by 3-biphenyl-5,6-dihydroimidazo 2,1-b thiazole in sodium/iodide sym-porter (NIS)-expressing cells

    International Nuclear Information System (INIS)

    Lecat-Guillet, N.; Ambroise, Y.

    2008-01-01

    The ability of the sodium/iodide sym-porter (NIS) to take up iodide has long provided the basis for cyto-reductive gene therapy and cancer treatment with radio-iodide. One of the major limitations of this approach is that radio-iodide retention in NIS-expressing cells is not sufficient for their destruction. We identified and characterized a small organic molecule capable of increasing iodide retention in HEK293 cells permanently transfected with human NIS cDNA (hNIS-HEK293) and in the rat thyroid-derived cell line FRTL-5. In the presence of 3-biphenyl-4'-yl-5,6-dihydroimidazo[2,1-b)thiazole (ISA1), the transmembrane iodide concentration gradient was increased up to 4.5-fold. Our experiments indicate that the imidazo-thiazole derivative acts either by inhibiting anion efflux mechanisms, or by promoting the relocation of iodide into subcellular compartments. This new compound is not only an attractive chemical tool to investigate the mechanisms of iodide flux at the cellular level, but also opens promising perspectives in the treatment of cancer after NIS gene transfer. (authors)

  5. Behavior of radioactive organic iodide in an atmosphere of High Temperature Gas-cooled Reactor

    International Nuclear Information System (INIS)

    Saeki, Masakatsu; Nakashima, Mikio; Sagawa, Chiaki; Masaki, Nobuyuki; Hirabayashi, Takakuni; Aratono, Yasuyuki

    1990-06-01

    Formation and decomposition behavior of radioactive organic iodide have been studied in an atmosphere of High Temperature Gas-cooled Reactor (High Temperature Engineering Test Reactor, HTTR). Na 125 I was chosen for radioactive iodine source instead of CsI diffusing from coated fuel particles. Na 125 I adsorbed on graphite was heated in pure He and He containing O 2 or H 2 O atmosphere. The results obtained are as follows. It was proved that organic iodide was formed with organic radicals released from graphite even in He atmosphere. Thus, the interchange rate of inorganic iodide with organic iodide was remarkably decreased with prolonged preheat-treatment period at 1000degC. Organic iodide formed was easily decomposed by its recirculation into hot reaction tube kept at 900degC. When organic iodide was passed through powdered graphite bed, more than 70% was decomposed at 90degC. Oxygen and water vapour intermixed in He suppressed the interchange rate of inorganic iodide with organic iodide. These results suggest that organic iodide rarely exists in the pressure vessel under normal operating condition of HTTR, and, under hypothetical accident condition of HTTR, organic iodide fraction never exceeds the value used for a safety assessment of light water reactor. (author)

  6. Laccase-catalyzed oxidation of iodide and formation of organically bound iodine in soils.

    Science.gov (United States)

    Seki, Miharu; Oikawa, Jun-ichi; Taguchi, Taro; Ohnuki, Toshihiko; Muramatsu, Yasuyuki; Sakamoto, Kazunori; Amachi, Seigo

    2013-01-02

    Laccase oxidizes iodide to molecular iodine or hypoiodous acid, both of which are easily incorporated into natural soil organic matter. In this study, iodide sorption and laccase activity in 2 types of Japanese soil were determined under various experimental conditions to evaluate possible involvement of this enzyme in the sorption of iodide. Batch sorption experiment using radioactive iodide tracer ((125)I(-)) revealed that the sorption was significantly inhibited by autoclaving (121 °C, 40 min), heat treatment (80 and 100 °C, 10 min), γ-irradiation (30 kGy), N(2) gas flushing, and addition of reducing agents and general laccase inhibitors (KCN and NaN(3)). Interestingly, very similar tendency of inhibition was observed in soil laccase activity, which was determined using 2,2'-azino-bis(3-ethylbenzothiazoline-6-sulfonate) (ABTS) as a substrate. The partition coefficient (K(d): mL g(-1)) for iodide and specific activity of laccase in soils (Unit g(-1)) showed significant positive correlation in both soil samples. Addition of a bacterial laccase with an iodide-oxidizing activity to the soils strongly enhanced the sorption of iodide. Furthermore, the enzyme addition partially restored iodide sorption capacity of the autoclaved soil samples. These results suggest that microbial laccase is involved in iodide sorption on soils through the oxidation of iodide.

  7. Strontium-90 and cesium-137 in tea (Japanese tea)

    International Nuclear Information System (INIS)

    1982-01-01

    Strontium-90 and cesium-137 in tea (Japanese tea) were determined. Five hundred grams of manufactured green tea was collected from six sampling locations in Japan. The results are shown in a table. (Namekawa, K.)

  8. Reaction of strontium zirconate with refractory borides and carbides

    International Nuclear Information System (INIS)

    Bowker, J.C.; Lane, J.E.

    1990-01-01

    The chemical compatibility of the potential oxide ceramic matrix material, strontium zirconate, and several different potential nonoxide ceramic reinforcement materials was studied by elevated temperature reaction. Results are presented in this paper

  9. Cation interdiffusion in polycrystalline calcium and strontium titanate

    International Nuclear Information System (INIS)

    Butler, E.P.; Jain, H.; Smyth, D.M.

    1991-01-01

    This paper discusses a method that has been developed to study bulk lattice interdiffusion between calcium and strontium titanate by fabrication of a diffusion couple using cosintering. The measured interdiffusion coefficients, D(C), indicate that strontium impurity diffusion in calcium titanate occurs at a faster rate than calcium impurity diffusion in strontium titanate. These interdiffusion coefficients are composition independent when the concentration of the calcium cation exceeds that of the strontium cation; otherwise D(C) is strongly composition dependent. Investigations into the effect of cation nonstoichiometry give results that are consistent with a defect incorporation reaction in which excess TiO 2 , within the solid solubility limit, produces A-site cation vacancies as compensating defects. The interdiffusion coefficients increase with increasing concentrations of TiO 2 , so it is concluded that interdiffusion of these alkaline-earth cations in their titanates occurs via a vacancy mechanism

  10. A combined cesium-strontium extraction/recovery process

    International Nuclear Information System (INIS)

    Horwitz, E.P.; Dietz, M.L.; Jensen, M.P.

    1996-01-01

    A new solvent extraction process for the simultaneous extraction of cesium and strontium from acidic nitrate media is described. This process uses a solvent formulation comprised of 0.05 M di-t-butylcyclohexano-18-crown-6 (DtBuCH18C6), 0.1 M Crown 100' (a proprietary, cesium-selective derivative of dibenzo-18-crown-6), 1.2 M tributyl phosphate (TBP), and 5% (v/v) lauryl nitrile in an isoparaffinic hydrocarbon diluent. Distribution ratios for cesium and strontium from 4 M nitric acid are 4.13 and 3.46, respectively. A benchtop batch countercurrent extraction experiment indicates that >98% of the cesium and strontium initially present in the feed solution can be removed in only four extraction stages. Through proper choice of extraction and strip conditions, extracted cesium and strontium can be recovered either together or individually

  11. Strontium removal jar test dataset for all figures and tables.

    Data.gov (United States)

    U.S. Environmental Protection Agency — The datasets where used to generate data to demonstrate strontium removal under various water quality and treatment conditions. This dataset is associated with the...

  12. Strontium-90 Error Discovered in Subcontract Laboratory Spreadsheet. Topical Report

    International Nuclear Information System (INIS)

    Brown, D.D.; Nagel, A.S.

    1999-07-01

    West Valley Demonstration Project health physicists and environment scientists discovered a series of errors in a subcontractor's spreadsheet being used to reduce data as part of their strontium-90 analytical process

  13. Adsorption of strontium (II) metal ions using phosphonate ...

    Indian Academy of Sciences (India)

    Chelation is a process wherein metalions and a polymer/matrix are bound together ... waste: evaporation, chemical precipitation/flocculation, solid-phase separation ... sary to remove strontium from the waste streams before it is discharged to ...

  14. Secondary laser cooling of strontium-88 atoms

    Energy Technology Data Exchange (ETDEWEB)

    Strelkin, S. A.; Khabarova, K. Yu., E-mail: kseniakhabarova@gmail.com; Galyshev, A. A.; Berdasov, O. I.; Gribov, A. Yu.; Kolachevsky, N. N.; Slyusarev, S. N. [Federal State Unitary Enterprise “All-Russia Research Institute for Physicotechnical and Radio Engineering Measurements” (VNIIFTRI) (Russian Federation)

    2015-07-15

    The secondary laser cooling of a cloud of strontium-88 atoms on the {sup 1}S{sub 0}–{sup 3}P{sub 1} (689 nm) intercombination transition captured into a magneto-optical trap has been demonstrated. We describe in detail the recapture of atoms from the primary trap operating on the strong {sup 1}S{sub 0}–{sup 1}P{sub 1} (461 nm) transition and determine the recapture coefficient κ, the number of atoms, and their temperature in the secondary trap as a function of experimental parameters. A temperature of 2 µK has been reached in the secondary trap at the recapture coefficient κ = 6%, which confirms the secondary cooling efficiency and is sufficient to perform metrological measurements of the {sup 1}S{sub 0}–{sup 3}P{sub 1} (698 nm) clock transition in an optical lattice.

  15. Electrochemistry of silver iodide the capacity of the double layer at the silver iodide-water interface

    NARCIS (Netherlands)

    Lyklema, J.; Overbeek, J.Th.G.

    1961-01-01

    A method is described for obtaining differential double layer capacities on silver iodide. Especially the influence of the nature and concentration of indifferent electrolytes was investigated, viz., the nitrates of Li·, K·, Rb·, NH4·, H·, Tl·, Mg··, Ba··, Co··, Cd··, Pb··, La···, Th····, the

  16. Porous allograft bone scaffolds: doping with strontium.

    Directory of Open Access Journals (Sweden)

    Yantao Zhao

    Full Text Available Strontium (Sr can promote the process of bone formation. To improve bioactivity, porous allograft bone scaffolds (ABS were doped with Sr and the mechanical strength and bioactivity of the scaffolds were evaluated. Sr-doped ABS were prepared using the ion exchange method. The density and distribution of Sr in bone scaffolds were investigated by inductively coupled plasma optical emission spectrometry (ICP-OES, X-ray photoelectron spectroscopy (XPS, and energy-dispersive X-ray spectroscopy (EDS. Controlled release of strontium ions was measured and mechanical strength was evaluated by a compressive strength test. The bioactivity of Sr-doped ABS was investigated by a simulated body fluid (SBF assay, cytotoxicity testing, and an in vivo implantation experiment. The Sr molar concentration [Sr/(Sr+Ca] in ABS surpassed 5% and Sr was distributed nearly evenly. XPS analyses suggest that Sr combined with oxygen and carbonate radicals. Released Sr ions were detected in the immersion solution at higher concentration than calcium ions until day 30. The compressive strength of the Sr-doped ABS did not change significantly. The bioactivity of Sr-doped material, as measured by the in vitro SBF immersion method, was superior to that of the Sr-free freeze-dried bone and the Sr-doped material did not show cytotoxicity compared with Sr-free culture medium. The rate of bone mineral deposition for Sr-doped ABS was faster than that of the control at 4 weeks (3.28 ± 0.23 µm/day vs. 2.60 ± 0.20 µm/day; p<0.05. Sr can be evenly doped into porous ABS at relevant concentrations to create highly active bone substitutes.

  17. Strontium isotopic stratigraphy utilizing authigenic dolomites in hemipelagic sediments

    Energy Technology Data Exchange (ETDEWEB)

    Baker, P.A. (Duke Univ., Durham, NC (USA)); Kastner, M. (Scripps Institute of Oceanography, La Jolla, CA (USA)); Elderfield, H. (Univ. of Cambridge (England))

    1990-05-01

    Authigenic dolomites commonly occur in organic-rich, continental margin marine sediments. These dolomites play a key role in the age dating of stratigraphic sections. The dolomites often are the only lithology amenable to paleomagnetic stratigraphy; they preserve siliceous microfossils against diagenetic; recrystallization, and provide useful strontium isotopic stratigraphic ages. Several potential sources of error frequently are unique to the use of authigenic dolomites in the strontium isotope methods. (1) The dolomites occur as cements of the host lithology, hence, they are not a pure phase. Potentially important contaminants during analysis include gypsum clay minerals, feldspars, and iron and manganese oxides. Strontium may occur as a structural substituent ion in these minerals or as a surface-adsorbed ion. Various leaching techniques have been tested to isolate dolomitic strontium. Purer dolomites and strontium-enriched dolomites often can be selected to ease these problems. (2) The dolomites form after the deposition of the host sediment, therefore, they record the diagenetic age not the depositional age. The stable isotopic composition of the dolomites can aid in selection of early formed samples. (3) The dolomites record pore-water strontium isotope compositions, not seawater isotopic compositions. This problem is also minimized by choosing dolomites formed near the sediment-water interface. (4) The dolomites formed near the sediment-water interface originated as rotodolomites and undergo subsequent burial diagenesis, creating a potential for later strontium isotope exchange. This problem is minimized by selecting fresh samples from the interior of nearly impermeable beds and nodules. Results from the Miocene Monterey Formation of California and from the Eocene through Pliocene Pisco basin of Peru show that authigenic dolomites can provide useful strontium isotopic age estimates.

  18. Separation of fission strontium from nuclear fuels by ammonium molybdatophosphate

    International Nuclear Information System (INIS)

    Hermann, A.

    1984-01-01

    The separation of fission strontium from solutions of prolonged cooled nuclear fuel has been performed using ammoniummolybdatophosphate (AMP) columns. The sorption mechanism of bivalent ions of AMP has been investigated by column and batch experiments. A pure ion exchange of Sr 2+ for two H + or NH 4 + ions has been established. Conditions for the sepasorption and elution of fission strontium and other fission products on AMP columns are described. (author)

  19. Strontium ranelate for preventing and treating postmenopausal osteoporosis.

    Science.gov (United States)

    O'Donnell, S; Cranney, A; Wells, G A; Adachi, J D; Reginster, J Y

    2006-10-18

    Strontium ranelate is a new treatment for osteoporosis therefore, its benefits and harms need to be known. To determine the efficacy and safety of strontium ranelate for the treatment and prevention of postmenopausal osteoporosis. We searched MEDLINE (1996 to March 2005), EMBASE (1996 to week 9 2005), the Cochrane Library (1996 to Issue 1 2005), reference lists of relevant articles and conference proceedings from the last two years. Additional data was sought from authors. We included randomized controlled trials (RCTs) of at least one year duration comparing strontium ranelate versus placebo reporting fracture incidence, bone mineral density (BMD), health related quality of life or safety in postmenopausal women. Treatment (versus prevention) population was defined as women with prevalent vertebral fractures and/or lumbar spine BMD T score gastritis or death. Additional data suggests that the risk of vascular and nervous system side-effects is slightly increased with taking 2 g of strontium ranelate daily over three to four years. There is silver level evidence (www.cochranemsk.org) to support the efficacy of strontium ranelate for the reduction of fractures (vertebral and to a lesser extent non-vertebral) in postmenopausal osteoporotic women and an increase in BMD in postmenopausal women with/without osteoporosis. Diarrhea may occur however, adverse events leading to study withdrawal were not significantly increased with taking 2 g of strontium ranelate daily. Potential vascular and neurological side-effects need to be further explored.

  20. Flame Spectrophotometric Determination of Strontium in Water and Biological Material

    Energy Technology Data Exchange (ETDEWEB)

    Joensson, G

    1964-10-15

    A flame spectrophotometric method has been developed for the determination of strontium in biological material and water samples. Strontium is determined in the presence of calcium at a wavelength of 4607 A. The intensity of the strontium emission from the sample is increased if n-butanol is added to a solution of the sample in water. With a 6 vol% solution of n-butanol in water, an optimum intensity of 3.5 times that obtained with pure water solution is obtained. Anions and alkali metals which might interfere with the flame spectrophotometric determination are separated from the sample by a simple ion exchange operation. The method allows determination of strontium in solutions down to 0.1{mu}g/ml. In this case the standard deviation is 3.1 % and with a strontium concentration of 1 {mu}g/ml the deviation is 0.9 %. This method has been used for the determination of strontium in samples of varying composition such as bone, meat and skin from fishes, samples of human bones, shell-fish, milk, and water, in which case Sr quantities of 5{mu}g were determined with an analytical error of less than 5 % and Sr{sub q}uantities greater than 10 {mu}g with an error of less than 3 %.

  1. Strontium-90 (90Sr) determination using liquid scintillation counting

    International Nuclear Information System (INIS)

    Cheberle, L.T.V.; Rosa, M.M.L.; Ferreira, M.T.; Taddei, M.H.T.

    2015-01-01

    This procedure describes a method for separation and measurement of strontium 90 Sr in water, soils, and biological samples. Water samples may be concentrated using evaporation or calcium phosphate coprecipitation. Soils and biological materials must be dissolved using wet digestion. Tracers and carriers must be added before the attack. Radioactive strontium is separated employing a specific resin before determination by liquid scintillation counting using the double energetic window method. The resin is used to concentrate strontium from samples. Stable strontium is used to monitor method yields and correct results to improve precision and accuracy. The presence of elemental strontium in the sample may bias the gravimetric yield determination. If it is suspected that natural strontium is present in the sample, its concentration should be determined by a suitable means (ICP), and the yield calculation properly modified. Sr-Spec resin with an 8M HNO 3 load solution is used to effectively remove 140 Ba and 40 K isotopes, as well as other interferences from the matrix. Tetravalent plutonium, neptunium, cerium and ruthenium, however, are not removed using nitric acid. The radiochemical procedure was tested using PROCORAD intercomparison exercises and PNI samples. (author)

  2. Flame Spectrophotometric Determination of Strontium in Water and Biological Material

    International Nuclear Information System (INIS)

    Joensson, G.

    1964-10-01

    A flame spectrophotometric method has been developed for the determination of strontium in biological material and water samples. Strontium is determined in the presence of calcium at a wavelength of 4607 A. The intensity of the strontium emission from the sample is increased if n-butanol is added to a solution of the sample in water. With a 6 vol% solution of n-butanol in water, an optimum intensity of 3.5 times that obtained with pure water solution is obtained. Anions and alkali metals which might interfere with the flame spectrophotometric determination are separated from the sample by a simple ion exchange operation. The method allows determination of strontium in solutions down to 0.1μg/ml. In this case the standard deviation is 3.1 % and with a strontium concentration of 1 μg/ml the deviation is 0.9 %. This method has been used for the determination of strontium in samples of varying composition such as bone, meat and skin from fishes, samples of human bones, shell-fish, milk, and water, in which case Sr quantities of 5μg were determined with an analytical error of less than 5 % and Sr q uantities greater than 10 μg with an error of less than 3 %

  3. Electrodeposition as an alternate method for preparation of environmental samples for iodide by AMS

    Energy Technology Data Exchange (ETDEWEB)

    Adamic, M.L., E-mail: Mary.Adamic@inl.gov [Idaho National Laboratory, P.O. Box 1625, Idaho Falls, ID 83402 (United States); Lister, T.E.; Dufek, E.J.; Jenson, D.D.; Olson, J.E. [Idaho National Laboratory, P.O. Box 1625, Idaho Falls, ID 83402 (United States); Vockenhuber, C. [Laboratory of Ion Beam Physics, ETH Zurich, Otto-Stern-Weg 5, 8093 Zurich (Switzerland); Watrous, M.G. [Idaho National Laboratory, P.O. Box 1625, Idaho Falls, ID 83402 (United States)

    2015-10-15

    This paper presents an evaluation of an alternate method for preparing environmental samples for {sup 129}I analysis by accelerator mass spectrometry (AMS) at Idaho National Laboratory. The optimal sample preparation method is characterized by ease of preparation, capability of processing very small quantities of iodide, and ease of loading into a cathode. Electrodeposition of iodide on a silver wire was evaluated using these criteria. This study indicates that the electrochemically-formed silver iodide deposits produce ion currents similar to those from precipitated silver iodide for the same sample mass. Precipitated silver iodide samples are usually mixed with niobium or silver powder prior to loading in a cathode. Using electrodeposition, the silver is already mixed with the sample and can simply be picked up with tweezers, placed in the sample die, and pressed into a cathode. The major advantage of this method is that the silver wire/electrodeposited silver iodide is much easier to load into a cathode.

  4. Electrodeposition as an alternate method for preparation of environmental samples for iodide by AMS

    International Nuclear Information System (INIS)

    Adamic, M.L.; Lister, T.E.; Dufek, E.J.; Jenson, D.D.; Olson, J.E.; Vockenhuber, C.; Watrous, M.G.

    2015-01-01

    This paper presents an evaluation of an alternate method for preparing environmental samples for "1"2"9I analysis by accelerator mass spectrometry (AMS) at Idaho National Laboratory. The optimal sample preparation method is characterized by ease of preparation, capability of processing very small quantities of iodide, and ease of loading into a cathode. Electrodeposition of iodide on a silver wire was evaluated using these criteria. This study indicates that the electrochemically-formed silver iodide deposits produce ion currents similar to those from precipitated silver iodide for the same sample mass. Precipitated silver iodide samples are usually mixed with niobium or silver powder prior to loading in a cathode. Using electrodeposition, the silver is already mixed with the sample and can simply be picked up with tweezers, placed in the sample die, and pressed into a cathode. The major advantage of this method is that the silver wire/electrodeposited silver iodide is much easier to load into a cathode.

  5. The Strontium Isotope Record of Zavkhan Terrane Carbonates: Strontium Isotope Stability Through the Ediacaran-Cambrian Transition

    OpenAIRE

    Petach, Tanya N.

    2015-01-01

    First order trends in the strontium isotopic (87Sr/86Sr) composition of seawater are controlled by radiogenic inputs from the continent and non-radiogenic inputs from exchange at mid-ocean ridges. Carbonates precipitated in seawater preserve trace amounts of strontium that record this isotope ratio and therefore record the relative importance of mid-ocean ridge and weathering chemical inputs to sea water composition. It has been proposed that environmental changes during the Ediacaran-Cambria...

  6. Discovery of aryl-tri-fluoroborates as potent sodium/iodide sym-porter (NIS) inhibitors

    International Nuclear Information System (INIS)

    Lecat-Guillet, N.; Ambroise, Y.

    2008-01-01

    The structure-based design of sodium/iodide sym-porter (NIS) inhibitors identified new active compounds. The organo-tri-fluoroborate shown was found to inhibit iodide uptake with an IC50 value of 0.4 μM on rat-derived thyroid cells. The biological activity is rationalized by the presence of the BF3 - ion as a minimal binding motif for substrate recognition at the iodide binding site. (authors)

  7. Discovery of aryl-tri-fluoroborates as potent sodium/iodide sym-porter (NIS) inhibitors

    Energy Technology Data Exchange (ETDEWEB)

    Lecat-Guillet, N.; Ambroise, Y. [CEA, DSV, Dept Bioorgan Chem and Isotop Labelling, Inst Biol and Technol, iBiTecS, F-91191 Gif Sur Yvette (France)

    2008-07-01

    The structure-based design of sodium/iodide sym-porter (NIS) inhibitors identified new active compounds. The organo-tri-fluoroborate shown was found to inhibit iodide uptake with an IC50 value of 0.4 {mu}M on rat-derived thyroid cells. The biological activity is rationalized by the presence of the BF3{sup -} ion as a minimal binding motif for substrate recognition at the iodide binding site. (authors)

  8. Strontium-90 at the Hanford Site and its ecological implications

    International Nuclear Information System (INIS)

    RE Peterson; TM Poston

    2000-01-01

    Strontium-90, a radioactive contaminant from historical operations at the U.S. Department of Energy (DOE) Hanford Site, enters the Columbia River at several locations associated with former plutonium production reactors at the Site. Strontium-90 is of concern to humans and the environment because of its moderately long half-life (29.1 years), its potential for concentrating in bone tissue, and its relatively high energy of beta decay. Although strontium-90 in the environment is not a new issue for the Hanford Site, recent studies of near-river vegetation along the shoreline near the 100 Areas raised public concern about the possibility of strontium-90-contaminated groundwater reaching the riverbed and fall chinook salmon redds. To address these concerns, DOE asked Pacific Northwest National Laboratory (PNNL) to prepare this report on strontium-90, its distribution in groundwater, how and where it enters the river, and its potential ecological impacts, particularly with respect to fall chinook salmon. The purpose of the report is to characterize groundwater contaminants in the near-shore environment and to assess the potential for ecological impact using salmon embryos, one of the most sensitive ecological indicators for aquatic organisms. Section 2.0 of the report provides background information on strontium-90 at the Hanford Site related to historical operations. Public access to information on strontium-90 also is described. Section 3.0 focuses on key issues associated with strontium-90 contamination in groundwater that discharges in the Hanford Reach. The occurrence and distribution of fall chinook salmon redds in the Hanford Reach and characteristics of salmon spawning are described in Section 4.0. Section 5.0 describes the regulatory standards and criteria used to set action levels for strontium-90. Recommendations for initiating additional monitoring and remedial action associated with strontium-90 contamination at the Hanford Site are presented in Section 6

  9. Strontium-90 at the Hanford Site and its ecological implications

    Energy Technology Data Exchange (ETDEWEB)

    RE Peterson; TM Poston

    2000-05-22

    Strontium-90, a radioactive contaminant from historical operations at the U.S. Department of Energy (DOE) Hanford Site, enters the Columbia River at several locations associated with former plutonium production reactors at the Site. Strontium-90 is of concern to humans and the environment because of its moderately long half-life (29.1 years), its potential for concentrating in bone tissue, and its relatively high energy of beta decay. Although strontium-90 in the environment is not a new issue for the Hanford Site, recent studies of near-river vegetation along the shoreline near the 100 Areas raised public concern about the possibility of strontium-90-contaminated groundwater reaching the riverbed and fall chinook salmon redds. To address these concerns, DOE asked Pacific Northwest National Laboratory (PNNL) to prepare this report on strontium-90, its distribution in groundwater, how and where it enters the river, and its potential ecological impacts, particularly with respect to fall chinook salmon. The purpose of the report is to characterize groundwater contaminants in the near-shore environment and to assess the potential for ecological impact using salmon embryos, one of the most sensitive ecological indicators for aquatic organisms. Section 2.0 of the report provides background information on strontium-90 at the Hanford Site related to historical operations. Public access to information on strontium-90 also is described. Section 3.0 focuses on key issues associated with strontium-90 contamination in groundwater that discharges in the Hanford Reach. The occurrence and distribution of fall chinook salmon redds in the Hanford Reach and characteristics of salmon spawning are described in Section 4.0. Section 5.0 describes the regulatory standards and criteria used to set action levels for strontium-90. Recommendations for initiating additional monitoring and remedial action associated with strontium-90 contamination at the Hanford Site are presented in Section 6

  10. Method of removing alkyl iodides or mixtures of iodine and alkyl iodides from a gas phase and an aqueous solution phase by utilizing ion exchange resins

    International Nuclear Information System (INIS)

    Shimizu, Hiroshi; Mizuuchi, Noboru; Yokoyama, Fumio.

    1967-01-01

    Alkyl iodides and mixtures of iodine and alkyl iodides are removed from a gas phase and an aquous solution phase by using solely an anion exchange resin containing a tertiary amine or together with an anion exchange resin containing quarternary ammonium compound. The resin containing the quarternary ammonium compound is employed mainly to remove iodine, and the resin containing the tertiary amine serves mainly to remove alkyl iodides. The method can be applied to collecting a majority of the methyl iodide as well as the radioactive iodine produced in the atmosphere of a reactor in case of a fuel accident. In embodiments, it is desirable to maintain the sufficient moisture content of the anion exchange resins at a sufficient moisture level so as not to reduce the migration speed of the iodine and alkyl iodides. The iodine and alkyl iodide can be produced with high efficiency and stability independently of the relative humidity of the gas phase. In examples, a solution which consists of 20.5 mg/l of iodine and 42.2mg/l of methyl iodide flew through a column of Amberite IRA-93 alone or blended with IRA-900 at a speed of 15 /hr. respectively. The resins were able to treat 400 times their equivalent in water. (Iwakiri, K.)

  11. Autoradiolytic decomposition and reductant-free sodium sup 124 I- and sup 123 I-iodide

    Energy Technology Data Exchange (ETDEWEB)

    Sajjad, M.; Lambrecht, R.M.; Bakr, S.A. (King Faisal Specialist Hospital and Research Centre, Riyadh (Saudi Arabia). Radionuclide and Cyclotron Operations)

    1990-01-01

    The presence of salts and metal cations in {sup 124}I- and {sup 123}I-sodium iodide solutions separated from {sup 124}Te targets promots autoradiolytic decomposition of iodide to several different iodine species dependent upon the chemical environment. The stabilization of the radioiodine as iodide by removal of trace salts and trace metal cations and in the absence of reducing agents is described. The high specific activity {sup 123}I- and {sup 124}I-iodide is suitable for labeling antibodies, proteins and radiopharmaceuticals. (orig.).

  12. Mercuric Iodide Anticoincidence Shield for Gamma-Ray Spectrometer, Phase I

    Data.gov (United States)

    National Aeronautics and Space Administration — We propose to utilize a new detector material, polycrystalline mercuric iodide, for background suppression by active anticoincidence shielding in gamma-ray...

  13. Mercuric Iodide Anticoincidence Shield for Gamma-Ray Spectrometer, Phase II

    Data.gov (United States)

    National Aeronautics and Space Administration — We utilize a new detector material, polycrystalline mercuric iodide, for background suppression by active anticoincidence shielding in gamma-ray spectrometers. Two...

  14. Temperature dependent energy levels of methylammonium lead iodide perovskite

    Science.gov (United States)

    Foley, Benjamin J.; Marlowe, Daniel L.; Sun, Keye; Saidi, Wissam A.; Scudiero, Louis; Gupta, Mool C.; Choi, Joshua J.

    2015-06-01

    Temperature dependent energy levels of methylammonium lead iodide are investigated using a combination of ultraviolet photoemission spectroscopy and optical spectroscopy. Our results show that the valence band maximum and conduction band minimum shift down in energy by 110 meV and 77 meV as temperature increases from 28 °C to 85 °C. Density functional theory calculations using slab structures show that the decreased orbital splitting due to thermal expansion is a major contribution to the experimentally observed shift in energy levels. Our results have implications for solar cell performance under operating conditions with continued sunlight exposure and increased temperature.

  15. Temperature dependent energy levels of methylammonium lead iodide perovskite

    Energy Technology Data Exchange (ETDEWEB)

    Foley, Benjamin J.; Marlowe, Daniel L.; Choi, Joshua J., E-mail: jjc6z@virginia.edu, E-mail: mgupta@virginia.edu, E-mail: scudiero@wsu.edu [Department of Chemical Engineering, University of Virginia, Charlottesville, Virginia 22904 (United States); Sun, Keye; Gupta, Mool C., E-mail: jjc6z@virginia.edu, E-mail: mgupta@virginia.edu, E-mail: scudiero@wsu.edu [Department of Electrical and Computer Engineering, University of Virginia, Charlottesville, Virginia 22904 (United States); Saidi, Wissam A. [Department of Mechanical Engineering and Materials Science, University of Pittsburgh, Pittsburgh, Pennsylvania 15261 (United States); Scudiero, Louis, E-mail: jjc6z@virginia.edu, E-mail: mgupta@virginia.edu, E-mail: scudiero@wsu.edu [Chemistry Department and Materials Science and Engineering Program, Washington State University, Pullman, Washington 99164 (United States)

    2015-06-15

    Temperature dependent energy levels of methylammonium lead iodide are investigated using a combination of ultraviolet photoemission spectroscopy and optical spectroscopy. Our results show that the valence band maximum and conduction band minimum shift down in energy by 110 meV and 77 meV as temperature increases from 28 °C to 85 °C. Density functional theory calculations using slab structures show that the decreased orbital splitting due to thermal expansion is a major contribution to the experimentally observed shift in energy levels. Our results have implications for solar cell performance under operating conditions with continued sunlight exposure and increased temperature.

  16. Growth and fabrication of large size sodium iodide crystal scintillator

    International Nuclear Information System (INIS)

    Sabharwal, S.C.; Karandikar, S.C.; Mirza, T.; Ghosh, B.; Deshpande, R.Y.

    1979-01-01

    The growth of 80 - 135 mm dia. Sodium iodide crystals activated with thallium is described in the present report. The growth is effected in a glazed porcelain crucible in a protective ambient of dry nitrogen. The technical details of the equipment developed have been fully described. The results of measurements on the rate of growth of crystal and the optimization of different growth parameters are reported. The dependence of various factors upon the performance characteristics of the scintillator detectors made using these crystals is also discussed. The energy resolution obtained for a typical detector of dimensions 76 mm dia x 76 mm ht. is 10 percent. (auth.)

  17. 1-(Ferrocen-1-ylmethyl-3-methylimidazol-3-ium iodide

    Directory of Open Access Journals (Sweden)

    Vincent O. Nyamori

    2012-12-01

    Full Text Available The structure of the title compound, [Fe(C5H5(C10H12N2]I, consists of a 1-(ferrocen-1-ylmethyl-3-methylimidazolium cation which is counter-balanced by an iodide anion. The cyclopentadienyl (Cp rings of the ferrocene unit have a slightly staggered conformation skewed from an ideal eclipsed conformation by an angle of 3.5 (6°. The interplanar angle between the Cp and the imidazole ring is 67.94 (2°.

  18. Syntheses with isotopically labelled carbon. Methyl iodide, formaldehyde and cyanide

    International Nuclear Information System (INIS)

    Finn, R.D.; Boothe, T.E.; Vora, M.M.; Hildner, J.C.; Emran, A.M.; Kothari, P.J.

    1984-01-01

    Many of the uniquely labelled synthetic precursors currently employed in the design of sophisticated radiolabelled compounds have their origins in the field of hot atom chemistry. Particularly, the development during the past few years of automated, on-line synthetic procedures which combine the nuclear reaction, hot atom and classical chemistry, and rapid purification methods has allowed the incorporation of useful radionuclides into suitable compounds of chemical and biochemical interest. The application of isotopically labelled methyl iodide, formaldehyde, and cyanide anion as synthetic intermediates in research involving human physiology and nuclear medicine, as well as their contributions to other scientific methodology, is reviewed. (author)

  19. Migration of strontium-90 from a strontium-90 fluoride deep ocean source

    International Nuclear Information System (INIS)

    Yabusaki, S.

    1981-06-01

    A hypothetical rupture of a heat source capsule on the ocean floor is analyzed for strontium-90 migration and attenuation. The evolution of the three-dimensional contaminant plume is simulated by a modified version of the Okubo-Pritchard radially symmetrical, diffusion velocity dispersion model. Results from this study indicate that released solutes are confined vertically to a layer near the level of introduction. Along the plume centerline, however, water quality is affected for considerably distances downstream from the source, with the maximum effect occurring after one year

  20. Optical lattice clock with strontium atoms; Horloge a reseau optique a atomes de strontium

    Energy Technology Data Exchange (ETDEWEB)

    Baillard, X.; Le Targat, R.; Fouche, M.; Brusch, A.; Westergaard, Ph.G.; Lecallier, A.; Lodewyck, J.; Lemonde, P. [Observatoire de Paris, LNE-SYRTE, Systemes de Reference Temps Espace, 75 (France)

    2009-07-01

    Optical lattice clocks, which were first imagined in 2000, should allow one to achieve unprecedented performances in the domain of atomic clocks. We present here the Strontium lattice clock, developed at LNE-SYRTE. The principle, in particular trapping atoms in the Lamb-Dicke regime and the notion of magic wavelength, is first explained. We then present the results obtained for the {sup 87}Sr isotope, with a frequency accuracy of 2,6.10{sup -15}, and the {sup 88}Sr isotope, with. which we perform the first frequency measurement of an optical lattice clock with bosonic atoms. (authors)

  1. Effect of competing cations on strontium sorption to surficial sediments

    International Nuclear Information System (INIS)

    Bunde, R.L.; Rosentreter, J.J.

    1995-01-01

    The following study was conducted to determine strontium distribution coefficients (K d 'S) of a surficial sediment at the Idaho National Engineering Laboratory (INEL), Idaho. Batch experimental techniques were used to determine K d 's which describe the partitioning of a solute between the solution and solid phase. A surficial sediment was mixed with synthesized aqueous solutions designed to chemically simulate wastewater disposed to infiltrations ponds near the Idaho Chemical Processing Plant at the INEL with respect to major ionic character and pH. The effects of variable concentrations of competing cations (sodium, potassium, calcium and magnesium) on strontium sorption were investigated at a fixed pH of 8.00. The pH of the natural system shows no appreciable variation, whereas a marked variability in cation concentration has been noted. Strontium sorption was impacted to a greater degree by the concentration of calcium and magnesium in solution than by the presence of sodium or potassium. However, extreme sodium solution concentrations of 1.0 to 5.0 g/L dramatically reduced strontium sorption. In all cases, strontium K d 's decreased as the concentration of calcium and magnesium in solution increased. Linear isotherm model K d 's ranged from 12.0 to 84.7 mL/g. Analysis of data from these experiments indicated that moderate concentrations of calcium and magnesium (less than 40 mg/L) and high concentrations of sodium (1.0 to 5.0 g/L) in wastewater increase strontium mobility by decreasing the sorption of strontium on surficial sediments beneath infiltration ponds at the INEL

  2. Radiopaque strontium fluoroapatite glass-ceramics

    Directory of Open Access Journals (Sweden)

    Wolfram eHöland

    2015-10-01

    Full Text Available The controlled precipitation of strontium fluoroapatite crystals, was studied in four base glass compositions derived from the SiO2 – Al2O3 – Y2O3 – SrO – Na2O – K2O/Rb2O/Cs2O – P2O5 – F system. The crystal phase formation of these glasses and the main properties of the glass-ceramics, such as thermal and optical properties and radiopacity were compared with a fifth, a reference glass-ceramic. The reference glass-ceramic was characterized as Ca-fluoroapatite glass-ceramic. The four strontium fluoroapatite glass-ceramics showed the following crystal phases: a Sr5(PO43F – leucite, KAlSi2O6 , b Sr5(PO43F – leucite, KAlSi2O6, and nano-sized NaSrPO4 c Sr5(PO43F – pollucite, CsAlSiO4 , and nano-sized NaSrPO4, d Sr5(PO43F – Rb-leucite, RbAlSi2O6, and nano-sized NaSrPO4.The proof of crystal phase formation was possible by X-ray diffraction (XRD. The microstructures, which were studied using scanning electron microscopy (SEM demonstrated a uniform distribution of the crystals in the glass matrix. The Sr-fluoroapatites were precipitated based on an internal crystallization process, and the crystals demonstrated a needlelike morphology. The study of the crystal growth of needlelike Sr-fluoroapatites gave a clear evidence of an Ostwald ripening mechanism.The formation of leucite, pollucite and Rb-leucite was based on a surface crystallization mechanism. Therefore, a twofold crystallization mechanism was successfully applied to develop these types of glass-ceramics. The main focus of this study was the controlled development of glass-ceramics exhibiting high radiopacity in comparison to the reference glass-ceramic. This goal could be achieved with all four glass-ceramics with the preferred development of the Sr-fluoroapatite – pollucite-type glass-ceramic. In addition to this main development, it was possible to control the thermal properties. Especially the Rb-leucite containing glass-ceramic showed the highest coefficient of thermal

  3. Mechanoluminescence of Dy doped strontium aluminate nanophosphors

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, Ravi, E-mail: rvsharma65@gmail.com [Department of Physics, Govt. Arts and Commerce Girls College, Raipur, C.G. 492001 (India); Bisen, D.P. [School of Studies in Physics and Astrophysics, Pt. Ravishankar Shukla University, Raipur, C.G. 492010 (India); Chandra, B.P. [Department of Postgraduate Studies and Research in Physics and Electronics, Rani Durgavati University, Jabalpur 482001 (India)

    2015-12-15

    Nanosized strontium aluminate phosphors activated with Dy{sup 3+} were prepared by a combustion method. Nanophosphor was prepared by this method at reaction temperatures as low as 600 °C. Powder X-ray diffraction (XRD), scanning electron microscope analysis was used to characterize the prepared product. The monoclinic phase was observed in the XRD pattern. The particle size of the samples was calculated around 35 nm. The SEM images show irregular shape of the prepared nanophosphor. Two peaks were found in the mechanoluminescence (ML) response curve plotted between time and ML intensity. The H{sub 3}BO{sub 3} added strontium aluminate phosphors activated with Dy show more bright ML peak as compared to the powders of SrAl{sub 2}O{sub 4}:Dy{sup 3+} without H{sub 3}BO{sub 3.} It was found that the PL and ML intensity increases with increasing concentration of Dy, it becomes maximum for 3% of Dy. The photoluminescence emission shows two intense fluorescence transitions peaks at 498 nm and 583 nm, {sup 4}F{sub 9/2}→{sup 6}H{sub 15/2} in the blue and {sup 4}F{sub 9/2}→{sup 6}H{sub 13/2} in the yellow-orange wavelength region. - Highlights: • Combustion synthesis route is used to prepare the SrAl{sub 2}O{sub 4}: Dy {sup 3+} nanophosphors. • The size of the synthesized sample was found to be in the nano-meter range. • The mechanoluminescence of SrAl{sub 2}O{sub 4}:Dy {sup 3+} nanophosphors is studied. • The photoluminescence of SrAl{sub 2}O{sub 4}: Dy {sup 3+} nanophosphors showed blue-shift as compared to bulk. • Effect of H{sub 3}BO{sub 3} on the mechanoluminescence of SrAl{sub 2}O{sub 4}:Dy{sup 3+} was studied.

  4. Stable strontium isotopic ratios from archaeological organic remains from the Thorsberg peat bog

    DEFF Research Database (Denmark)

    Nosch, Marie-Louise Bech; von Carnap-Bornheim, Claus; Grupe, Gisela

    2007-01-01

    Pilot study analysing stable strontium isotopic ratios from Iron Age textile and leather finds from the Thorsberg peat bog.......Pilot study analysing stable strontium isotopic ratios from Iron Age textile and leather finds from the Thorsberg peat bog....

  5. Flotation separation of strontium via phosphate precipitation.

    Science.gov (United States)

    Thanh, Luong H V; Liu, J C

    2017-06-01

    Flotation separation of strontium (Sr) from wastewater via phosphate precipitation was investigated. While 37.33% of Sr precipitated at highly alkaline pH in the absence of PO 4 3- , it completely precipitated as Sr 3 (PO 4 ) 2 at a molar ratio ([PO 4 3- ]:[Sr 2+ ]) of 0.62 at a lower pH value. The presence of Ca 2+ hindered Sr precipitation, yet it could be overcome by increasing the PO 4 3- dose. Sodium dodecyl sulfate (SDS) was a better collector for dispersed air flotation of Sr 3 (PO 4 ) 2 than cetyl trimethyl ammonium bromide, or mixed collector systems of SDS and saponin. The highest separation efficiency of 97.5% was achieved at an SDS dose of 40 mg/L. The main mechanism in the precipitate flotation is adsorption of anionic SDS on the positively charged surface of colloidal Sr 3 (PO 4 ) 2 via electrostatic interaction. SDS enhanced the aggregation of Sr 3 (PO 4 ) 2 precipitates as the size increased from 1.65 to 28.0 μm, which was beneficial to separation as well.

  6. Optical lattice clock with Strontium atoms

    International Nuclear Information System (INIS)

    Baillard, X.

    2008-01-01

    This thesis presents the latest achievements regarding the optical lattice clock with Strontium atoms developed at LNE-SYRTE. After a review of the different types of optical clocks that are currently under development, we stress on the concept of optical lattice clock which was first imagined for Sr 87 using the 1 S 0 → 3 P 0 transition. We exhibit the features of this atom, in particular the concept of magic wavelength for the trap, and the achievable performances for this kind of clock. The second part presents the experimental aspects, insisting particularly on the ultra-stable laser used for the interrogation of the atoms which is a central part of the experiment. Among the latest improvements, an optical pumping phase and an interrogation phase using a magnetic field have been added in order to refine the evaluation of the Zeeman effect. Finally, the last part presents the experimental results. The last evaluation of the clock using Sr 87 atoms allowed us to reach a frequency accuracy of 2.6*10 -15 and a measurement in agreement with the one made at JILA (Tokyo university) at the 10 -15 level. On another hand, thanks to recent theoretical proposals, we made a measurement using the bosonic isotope Sr 88 by adapting the experimental setup. This measurement represents the first evaluation for this type of clock, with a frequency accuracy of 7*10 -14 . (author)

  7. Selective gettering of hydrogen in high pressure metal iodide lamps

    International Nuclear Information System (INIS)

    Kuus, G.

    1976-01-01

    One of the main problems in the manufacture of high pressure gas discharge lamps is the elimination of gaseous impurities from their arc tubes. Long degassing processes of all the lamp components are necessary in order to produce lamps with a low ignition voltage and good maintenance of the radiation properties. The investigation described deals with a selective getter place in the arc tube which can replace the long degassing process. The getter consists of a piece of yttrium encapsulated in thin tantalum foil. By this way it is possible to use the gettering action of tantalum and yttrium without having reaction between the metal iodide of the arc tube and yttrium. Yttrium is used because this metal can adsorb a large quantity of hydrogen even at a temperature of 1000 0 C. Hydrogen forms the main gaseous impurity in the high pressure metal iodide lamp. For this reason the adsorption properties like adsorption rate and capacity of the tantalum--yttrium getter for hydrogen are examined, and the results obtained from lamp experiments are given

  8. Organic iodide capture using a zeolite dry filtration

    International Nuclear Information System (INIS)

    Park, Sanggil; Sung, Joonyoung; Kim, Gi-ppeum; Lee, Jaeyoung

    2017-01-01

    An organic iodide, especially, methyl iodide (CH 3 I) would generated non-negligibly from a severe accident in a nuclear power plant. This CH 3 I will be dangerous for human when it was inhaled, it is highly toxic and causes a serious nerve disorder. Even it is a major contributor to a thyroid cancer. In order to prevent its environmental release, it is required to decontaminate using a filtration system. For the removal of CH 3 I from the release gases, wet-type is not ideal due to a high re-volatile characteristics of CH 3 I. It may become volatile after dissolving in a pool and forms CH 3 I again at the surface of water pool. Therefore, a dry-filtration should be installed to remove the CH 3 I. In this study, we preliminary investigate the characteristics of zeolite filtration methods for the removal of CH 3 I. We used both silver ion exchanged ZSM-5-zeolite (Ag+-ZSM-5) to study the effect of silver ion for the removal of iodine from CH 3 I. In summary, the CH 3 I capture tests using a silver ion exchanged zeolite was conducted in the coupled TGAGC test set-up. The mass change of the sample and concentration of CH 3 I were measured. The samples were investigated by the SEM/EDS to see its surface characteristics.

  9. Interruption with the Migration of Iodide by GR(CT)

    International Nuclear Information System (INIS)

    Min, J. H.; Lee, J. K.; Jeong, J. T.

    2012-01-01

    The purpose of this study is to understand the influence of green rust on the migration of iodide. GR(CT) would be major corrosion product of iron near the seawater or saline layer in underground. The GR(CT) may play an important role in the retardation of the iodide migration in a deep geological environment due to it's anionic exchange reaction. In underground radioactive waste repository, the corrosion of iron canisters would be proceed as follows; Fe(II) and/or Fe(III) dissolved from iron containers → Fe(II)(OH) 2 and/or Fe(III)(OH) 3 → Green rust → Lepidocrocite or Magnetite → Goetite etc. Generally, the green rust has known to exist in environments close to the Fe(Π)/Fe(ΠΙ) transition zone or between the oxidized layer and reduced layer in the underground. As anion exchanger and strong reducer, the green rusts can affect the migration of anions, reactions involving green rusts were poorly studied in relation to the safety assessment of radioactive waste repository

  10. Nuclear detonation, thyroid cancer and potassium iodide prophylaxis

    Directory of Open Access Journals (Sweden)

    Viroj Wiwanitkit

    2011-01-01

    Full Text Available The recent nuclear disaster at Japan has raised global concerns about effects of radioactive leakage in the environment, associated hazards, and how they can be prevented. In this article, we have tried to explain about the guidelines laid down by World Health Organization for a potassium iodide prophylaxis following a nuclear disaster, and its mechanism of action in preventing thyroid cancer. Data was collected mainly from the studies carried out during the Chernobyl disaster of Russia in 1986 and the hazardous effects especially on the thyroid gland were studied. It was seen that radioactive iodine leakage from the nuclear plants mainly affected the thyroid gland, and especially children were at a higher risk at developing the cancers. Potassium Iodide prophylaxis can be administered in order to prevent an increase in the incidence of thyroid cancers in the population of an area affected by a nuclear disaster. However, one has to be cautious while giving it, as using it without indication has its own risks.

  11. Accumulation of strontium 90 and cesium 137 in some hydrobionts

    International Nuclear Information System (INIS)

    Boyadzhiev, A.; Keslev, D.; Kerteva, A.; Novakova, E.

    1974-01-01

    Factors responsible for the accumulation of strontium 90 and cesium 137 in some plant organisms, characteristic for fishes in Bulgarian fresh-water reservoirs and in Black Seawater, were examined. The investigated samples were taken during spring, summer and autumn-winter seasons 1967/1968. Each sample burnt to ashes at 450 0 C was examined for strontium 90 and cesium 137 content as well as stable isotopes of calcuim and potassium. Accumulation factors for strontium 90 and cesium 137 were significantly higher in freshwater hydrobionts than in seawater hydrobionts. This could be explained by variations in the concentration of stable isotopes of calcium and potassium from freshwater reservoirs and from seawater. Potassium and calcium concentrations were relatively constant in seawater while in freshwater they were significantly variable. Accumulation factors for these radionuclides increased according to the amount of rain and the altitude above sea level. Strontium 90 was deposited mostly in fins, less in scales and least in the meat of fishes; cesium 137 was mainly deposited in the meat and less in the other parts of fishes. The highest accumulation factors for strontium 90 were determined in fishes and for cesium 137 in plant organisms. The most convenient plant and fish species for tracing radioactive contamination of freshwater reservoirs and in the Black Sea were indicated. (A.B.)

  12. A process for the development of strontium hydroxyapatite

    International Nuclear Information System (INIS)

    Zahra, N.; Fayyaz, M.; Iqbal, W.; Irfan, M.; Alam, S.

    2013-01-01

    A procedure for the preparation of Strontium Hydroxyapatite is adapted to produce high purity and better homogeneity ceramic with good Crystallinity. The strontium substituted bone cement has potential for use in orthopedic surgeries. Ionic Strontium (Sr) in humans shares the same physiological pathway as calcium and can be deposited in the mineral structure of the bone. In the present study, a novel concept of preparing Sr-contained Hydroxyapatite bone cement by using a precipitation method is proposed to get an ideal biomaterial that possesses potential degradability and more excellent pharmacological effect. Chemical analysis, Fourier Transform Infra Red analysis and Thermogravimetric/ Differential Scanning Calorimetric studies were conducted on prepared Strontium Hydroxyapatite sample to characterize the incorporation of 15 percentage Sr2+ into the crystal lattice of Hydroxyapatite. Strontium was quantitatively incorporated into Hydroxyapatite where its substitution for calcium provoked a linear shift of the infrared absorption bands of the hydroxyl and phosphate groups. Thus, the formation of Sr-HAp was confirmed by Chemical Analysis, FT-IR and TGA/DSC results. (author)

  13. Investigation of Varied Strontium-Transuranic Precipitation Chemistries for Crossflow

    International Nuclear Information System (INIS)

    Nash, C.A.

    2000-01-01

    Precipitation chemistries for strontium and transuranic (TRU) removal have been tested for crossflow filterability and lanthanide removal with simulants of Hanford tank 241-AN-107 supernate. This is the initial work indicating the usefulness of a strontium and permanganate precipitation process as applied to the Hanford River Protection Project. Precipitations with both ferric and ferrous iron were shown to be at least two orders of magnitude less filterable than a 0.1 gpm/ft target average flux that was desired at the time. A precipitate from a strontium nitrate strike alone was found to filter easily and to make the desired average flux. Other chemistries tested included precipitant of lanthanum(III), nickel (II), calcium (II), and a redox chemistry using sodium permanganate. Of these chemistries a strontium and permanganate strike including calcium provided the highest filter flux compared to the other chemistries. It showed the most promise in lanthanide removal as well. This work provides a promising direction for further work to achieve both acceptable filterability and decontamination for Envelope C wastes to be treated by the Hanford River Protection Project. The work reported here was originally intended to satisfy needs for crossflow filter testing of a strontium and ferric precipitation method for treating Envelope C using a 241-AN-107 simulant

  14. Method for strontium isolation from high-mineralized water

    International Nuclear Information System (INIS)

    Evzhanov, Kh.; Andriyasova, G.M.

    1983-01-01

    A method to isolate strontium from high-mineralized waters containing sodium, magnesium, calcium and strontium chlorides, which differ from the prototype method in a considerable decrease in energy consumption with the preservation of a high degree of Sr, Mg and Ca isolation selectivity, has been suggested. According to the method suggested mineralized waters are treated with alkali (NaOH) in the amount of 95-97% of stoichiometry by magnesium, then after separation of magnesium hydroxide precipitate mother liquor is treated with sodium carbonate in the amount of 50-60% of stoichiometry by calcium. After separation of calcium carbonate precipitate mother liquor is treated with NaOH in the amount of 130-135% of stoichiometry by calcium. After separation of calcium hydroxide precipitate from mother liquor by means of sodium carbonate introduction strontium carbonate is isolated. The degree of strontium extraction in the form of SrCO 3 constitutes 90.5% of its content in the initial solution. The method presented can be used for strontium separation from natural and waste waters

  15. A process for the development of strontium hydroxyapatite

    International Nuclear Information System (INIS)

    Zahra, N; Fayyaz, M; Iqbal, W; Irfan, M; Alam, S

    2014-01-01

    A procedure for the preparation of Strontium Hydroxyapatite is adapted to produce high purity and better homogeneity ceramic with good Crystallinity. The strontium substituted bone cement has potential for use in orthopedic surgeries. Ionic Strontium (Sr) in humans shares the same physiological pathway as calcium and can be deposited in the mineral structure of the bone. In the present study, a novel concept of preparing Sr-contained Hydroxyapatite bone cement by using a precipitation method is proposed to get an ideal biomaterial that possesses potential degradability and more excellent pharmacological effect. Chemical analysis, Fourier Transform Infra Red analysis and Thermogravimetric/ Differential Scanning Calorimetric studies were conducted on prepared Strontium Hydroxyapatite sample to characterize the incorporation of 15% Sr 2 + into the crystal lattice of Hydroxyapatite. Strontium was quantitatively incorporated into Hydroxyapatite where its substitution for calcium provoked a linear shift of the infrared absorption bands of the hydroxyl and phosphate groups. Thus, the formation of Sr-HAp was confirmed by Chemical Analysis, FT-IR and TGA/DSC results

  16. A process for the development of strontium hydroxyapatite

    Science.gov (United States)

    Zahra, N.; Fayyaz, M.; Iqbal, W.; Irfan, M.; Alam, S.

    2014-06-01

    A procedure for the preparation of Strontium Hydroxyapatite is adapted to produce high purity and better homogeneity ceramic with good Crystallinity. The strontium substituted bone cement has potential for use in orthopedic surgeries. Ionic Strontium (Sr) in humans shares the same physiological pathway as calcium and can be deposited in the mineral structure of the bone. In the present study, a novel concept of preparing Sr-contained Hydroxyapatite bone cement by using a precipitation method is proposed to get an ideal biomaterial that possesses potential degradability and more excellent pharmacological effect. Chemical analysis, Fourier Transform Infra Red analysis and Thermogravimetric/ Differential Scanning Calorimetric studies were conducted on prepared Strontium Hydroxyapatite sample to characterize the incorporation of 15% Sr2+ into the crystal lattice of Hydroxyapatite. Strontium was quantitatively incorporated into Hydroxyapatite where its substitution for calcium provoked a linear shift of the infrared absorption bands of the hydroxyl and phosphate groups. Thus, the formation of Sr-HAp was confirmed by Chemical Analysis, FT-IR and TGA/DSC results.

  17. Spectroscopy and Laser-SNMS on stable and radioactive strontium

    Energy Technology Data Exchange (ETDEWEB)

    Bosco, Hauke; Walther, Clemens [Institut fuer Radiooekologie und Strahlenschutz, Leibniz Universitaet Hannover (Germany); Franzmann, Michael [Institut fuer Radiooekologie und Strahlenschutz, Leibniz Universitaet Hannover (Germany); Institut fuer Physik, Johannes Gutenberg Universitaet Mainz (Germany); Kron, Tobias; Wendt, Klaus [Institut fuer Physik, Johannes Gutenberg Universitaet Mainz (Germany)

    2016-07-01

    Nuclear accidents as experienced e.g. in Chernobyl or Fukushima and nuclear weapon tests released considerable activity levels and a variety of medium to long-lived radionuclides into the environment. Strontium-90 appears as a significant share of the fission products in spent nuclear fuel and correspondingly in any possible release. Due to its chemical properties it is subject to long range transport through the environment and can cause considerable dose to man when entering the food chain. Correspondingly, the investigation of speciation and migration channels is of major relevance. A radioanalytical approach is severely hampered by the low beta energy of the strontium-90 decay and the need to separate strontium-90 from the secular equilibrated daughter yttrium-90. Hence, application of a mass spectrometric method without chemical separation of the elements is a promising alternative for low-level investigation of strontium-90. Application of the new Laser-SNMS system at IRS Hannover could well suit those needs. It applies three Ti:Sa lasers for resonant ionization of neutral atoms produced by primary ion sputtering in a SIMS together with a time-of-flight mass analysis which provides high spatial resolution. The analytical measurements are preceded by spectroscopic studies on the level structure of strontium to develop a most efficient ionization scheme.

  18. Investigation of Varied Strontium-Transuranic Precipitation Chemistries for Crossflow

    Energy Technology Data Exchange (ETDEWEB)

    Nash, C.A.

    2000-07-27

    Precipitation chemistries for strontium and transuranic (TRU) removal have been tested for crossflow filterability and lanthanide removal with simulants of Hanford tank 241-AN-107 supernate. This is the initial work indicating the usefulness of a strontium and permanganate precipitation process as applied to the Hanford River Protection Project. Precipitations with both ferric and ferrous iron were shown to be at least two orders of magnitude less filterable than a 0.1 gpm/ft target average flux that was desired at the time. A precipitate from a strontium nitrate strike alone was found to filter easily and to make the desired average flux. Other chemistries tested included precipitant of lanthanum(III), nickel (II), calcium (II), and a redox chemistry using sodium permanganate. Of these chemistries a strontium and permanganate strike including calcium provided the highest filter flux compared to the other chemistries. It showed the most promise in lanthanide removal as well. This work provides a promising direction for further work to achieve both acceptable filterability and decontamination for Envelope C wastes to be treated by the Hanford River Protection Project. The work reported here was originally intended to satisfy needs for crossflow filter testing of a strontium and ferric precipitation method for treating Envelope C using a 241-AN-107 simulant.

  19. Development of w/o microemulsion for transdermal delivery of iodide ions.

    Science.gov (United States)

    Lou, Hao; Qiu, Ni; Crill, Catherine; Helms, Richard; Almoazen, Hassan

    2013-03-01

    The objective of this study was to develop a water-in-oil (w/o) microemulsion which can be utilized as a transdermal delivery for iodide ions. Several w/o microemulsion formulations were prepared utilizing Span 20, ethanol, Capryol 90®, and water. The selected formulations had 5%, 10%, 15%, 20%, and a maximum of 23% w/w water content. Potassium iodide (KI) was incorporated in all formulations at 5% w/v. Physicochemical characterizations were conducted to evaluate the structure and stability. These studies included: mean droplet size, pH, viscosity, conductivity, and chemical stability tests. In vitro human skin permeation studies were conducted to evaluate the diffusion of the iodide ion through human skin. The w/o microemulsion formulations were stable and compatible with iodide ions with water content ranging from 5% to 23% w/w. The addition of KI influenced the physicochemical properties of microemulsion as compared to blank microemulsion formulations. In vitro human skin permeation studies indicated that selected formulations improved iodide ion diffusion significantly as compared to control (KI solution; P valuemicroemulsion. Span 20, ethanol and Capryol 90 protected the iodide ions against oxidation and formed a stable microemulsion. It is worth to note that according to Hofmeister series, iodide ions tend to lower the interfacial tension between water and oil and consequently enhance overall stability. This work illustrates that microemulsion system can be utilized as a vehicle for the transdermal administration of iodide.

  20. Radiolytic formation of organic iodides from organic compounds released from ripolin paint

    International Nuclear Information System (INIS)

    Attia, S.; Evans, G.J.

    2002-01-01

    The impact of a serious nuclear reactor accident is governed to a large extent by the possible release of airborne organic iodides to the environment. This research examines the identification and behavior of organic iodides formed in the containment due to the release of organic compounds from Ripolin paint, into the aqueous phase, following a nuclear reactor accident. A bench scale apparatus installed in the irradiation chamber of a Gammacell was used to analyze the formation of organic iodides. Iodo-organics, transferred to the gas phase above irradiated aqueous samples, were analyzed using a Thermal Desorption method coupled with gas chromatography and mass spectrometry. Detailed studies of the identity of the organic compounds released and the organic iodides formed were conducted. The effects of parameters such as irradiation dose were also examined. All the organic iodides formed, under radiolytic conditions, were identified as iodo-alkanes. The organic compounds that were released from the Ripolin paint, such as methyl isobutyl ketone, were found to decompose, by a series of reactions, to produce the organic iodides. The precursor organic compounds and the organic iodides formed were observed to consist of the same alkyl group. These results indicate that organic compounds released from surface paints directly influence the formation of radiolytic organic iodide. (author)

  1. Structural templating in a nonplanar phthalocyanine using single crystal copper iodide

    OpenAIRE

    Rochford, L. A. (Luke A.); Ramadan, Alexandra J.; Keeble, Dean S.; Ryan, Mary P.; Heutz, Sandrine; Jones, T. S. (Tim S.)

    2015-01-01

    Solution-grown copper iodide crystals are used as substrates for the templated growth of the nonplanar vanadyl phthalocyanine using organic molecular beam deposition. Structural characterization reveals a single molecular orientation produced by the (111) Miller plane of the copper iodide crystals. These fundamental measurements show the importance of morphology and structure in templating interactions for organic electronics applications.

  2. A model for additive transport in metal halide lamps containing mercury and dysprosium tri-iodide

    NARCIS (Netherlands)

    Beks, M.L.; Haverlag, M.; Mullen, van der J.J.A.M.

    2008-01-01

    The distribution of additives in a metal halide lamp is examined through numerical modelling. A model for a lamp containing sodium iodide additives has been modified to study a discharge containing dysprosium tri-iodide salts. To study the complex chemistry the method of Gibbs minimization is used

  3. Extraction method for the determination of inorganic iodides in Rose Bengal labelled with 131I

    International Nuclear Information System (INIS)

    Lengyel, J.; Krtil, J.; Vecernik, J.

    1982-01-01

    An extraction method for the determination of inorganic iodides in Rose Bengal preparations labelled with 131 I is described. The method is based on the quantitative extraction of Rose Bengal into chloroform from acidic medium while the inorganic iodides remain in the aqueous phase. The method is simple, rapid, and reproducible. (author)

  4. Oxygen-hydrogen fuel cell with an iodine-iodide cathode - A concept

    Science.gov (United States)

    Javet, P.

    1970-01-01

    Fuel cell uses a porous cathode through which is fed a solution of iodine in aqueous iodide solution, the anode is a hydrogen electrode. No activation polarization appears on the cathode because of the high exchange-current density of the iodine-iodide electrode.

  5. Placental transfer of calcium and strontium and of their radionuclides

    International Nuclear Information System (INIS)

    Griessl, I.; Stieve, F.E.

    1987-11-01

    The first part of the report deals with the occurrence and the chemistry of strontium and its radioisotopes, and the second part discusses the calcium and the strontium metabolism in man. General information on the biology and physiology of the human skeleton is given in part 3, whereas part 4 again discusses the calcium and strontium metabolism in man, however with particular emphasis on the conditions during pregnancy and lactation. Part 5 presents an evaluation of the literature in this subject field, concentrating on results obtained with experimental animals such as cows, swine, dogs, guinea pigs, rats, and mice, and discusses the applicability of these findings to the conditions in man. An annex presents data on the yttrium metabolism in man and animal. (MG) [de

  6. Bulgarian regional patterns of contamination by global fallout (strontium 90)

    International Nuclear Information System (INIS)

    Boyadzhiev, A.; Shopov, N.; Simova, G.; Andreev, E.; Mikha lov, M.G.

    1980-01-01

    For selected districts in the country, mean annual atmospheric precipitation rates were related to strontium-90 contents in milk over the period 1970-1977. Strontium-90 in milk was determined by the method of Popov, using Va-Z-310 counters for activity measurements. The impact of annual precipitation means was examined by monofactorial spread analysis, with sites distributed into three groups according to precipitation rates observed over longer time periods: up to 650 l/m 2 from 650 to 750 l/m 2 ; and above 750 L/M 2 . Values of coefficient F were estimated, representing the ratio of group to random spreads. These figures were compared with critical values in Student's tables for 0.05 significance level. The F data indicated a definite alternative relationship to exist between strontium-90 amounts in mils and annual precipitation rates, which is prognostically meaningful from the strandpoint of radiological protection of the population

  7. Strontium titanate thin film deposition - structural and electronical characterization

    Energy Technology Data Exchange (ETDEWEB)

    Hanzig, Florian; Hanzig, Juliane; Stoecker, Hartmut; Mehner, Erik; Abendroth, Barbara; Meyer, Dirk C. [TU Bergakademie Freiberg, Institut fuer Experimentelle Physik (Germany); Franke, Michael [TU Bergakademie Freiberg, Institut fuer Elektronik- und Sensormaterialien (Germany)

    2012-07-01

    Strontium titanate is on the one hand a widely-used model oxide for solids which crystallize in perovskite type of structure. On the other hand, with its large band-gap energy and its mixed ionic and electronic conductivity, SrTiO{sub 3} is a promising isolating material in metal-insulator-metal (MIM) structures for resistive switching memory cells. Here, we used physical vapour deposition methods (e. g. electron-beam and sputtering) to produce strontium titanate layers. Sample thicknesses were probed with X-ray reflectometry (XRR) and spectroscopic ellipsometry (SE). Additionally, layer densities and dielectric functions were quantified with XRR and SE, respectively. Using infrared spectroscopy free electron concentrations were obtained. Phase and element composition analysis was carried out with grazing incidence X-ray diffraction and X-ray photoelectron spectroscopy. Subsequent temperature treatment of samples lead to crystallization of the initially amorphous strontium titanate.

  8. Iodine K-edge EXAFS analysis of iodide ion-cyclodextrin inclusion complexes in aqueous solution

    International Nuclear Information System (INIS)

    Kaneko, T; Ueda, M; Nagamatsu, S; Konishi, T; Fujikawa, T; Mizumaki, M

    2009-01-01

    We study the structure of inclusion complexes of α-, β-, γ-cyclodextrin with mono-iodide ion in aqueous solution by means of iodine K-edge EXAFS spectroscopy. The analysis is based on the assumption that two kinds of iodide ions exist in KI-cyclodextrin aqueous solution i.e. hydrated mono-iodide ions and one-one mono-iodide-cyclodextrin inclusion complexes. In KI-α-cyclodextrin system, iodine K-edge EXAFS analyse show that the average coordination number of the oxygen atoms in water molecules in the first hydration shell decreases as the fraction of included ions increases. This result suggests that dehydration process accompanies the formation of the inclusion complex. This is not found in the case of β-cyclodextrin, indicating that in this case the iodide ions are included together with the whole first hydration shell.

  9. Determination of nanogram amounts of iodide by electrochemical isotope dilution analysis

    International Nuclear Information System (INIS)

    Gabrielsson, A.-B.; Beronius, P.

    1976-01-01

    A known quantity of iodide in ethanol as solvent was labelled with 131 I-and subsequently diluted with a predetermined amount of inactive iodide. Specific activities before and after the isotope dilution were established by anodically depositing small fractions of the halide in each sample on rotating silver micro electrodes and determining the activities of the electrodeposits. The lowest concentration of iodide used in any analysis was 1.10 -5 M. Further deposition studies revealed that iodide can be deposited with 1 100% current efficiency on the rotating silver micro electrode for concentration down to 2.4.10 -6 M. Electrodeposition studies for still lower concentrations have not yet been undertaken. These results suggest that amounts of iodide ion down to about 10 ng, and possibly still smaller quantitites, might be determined with the method developed. Amounts from 42 ng to 1 μg can be determined with an error of 2.5%. (T.G.)

  10. Evaluation of optimal silver amount for the removal of methyl iodide on silver-impregnated adsorbents

    International Nuclear Information System (INIS)

    Park, G.I.; Cho, I.H.; Kim, J.H.; Oh, W.Z.

    2001-01-01

    The adsorption characteristics of methyl iodide generated from the simulated off-gas stream on various adsorbents such as silver-impregnated zeolite (AgX), zeocarbon and activated carbon were investigated. An extensive evaluation was made on the optimal silver impregnation amount for the removal of methyl iodide at temperatures up to 300 deg. C. The degree of adsorption efficiency of methyl iodide on silver-impregnated adsorbent is strongly dependent on impregnation amount and process temperature. A quantitative comparison of adsorption efficiencies on three adsorbents in a fixed bed was investigated. The influence of temperature, methyl iodide concentration and silver impregnation amount on the adsorption efficiency is closely related to the pore characteristics of adsorbents. It shows that the effective impregnation ratio was about 10wt%, based on the degree of silver utilization for the removal of methyl iodide. The practical applicability of silver-impregnated zeolite for the removal of radioiodine generated from the DUPIC process was consequently proposed. (author)

  11. Colorimetric sensing of iodide based on triazole-acetamide functionalized gold nanoparticles

    International Nuclear Information System (INIS)

    Lee, I-Lin; Sung, Yi-Ming; Wu, Shu-Pao; Wu, Chien-Hou

    2014-01-01

    We have modified gold nanoparticles (AuNPs) with triazole acetamide to obtain a material for the sensitive and selective colorimetric determination of iodide. The functionalized AuNPs were prepared by a reductive single chemical step using a Cu(I)-catalyzed click reaction. The presence of iodide ions induces the aggregation of these AuNPs and results in a color change from wine-red to purple. The iodide-induced aggregation can be detected visually with bare eyes, but also by photometry. The detection limit is as low as 15 nM. The method displays excellent selectivity for iodide over other anions due to the selective interaction with the amido groups of the triazole. The method was applied to the determination of iodide in spiked lake waters. (author)

  12. Strontium effects on root dentin tubule occlusion and nanomechanical properties.

    Science.gov (United States)

    Saeki, Kuniko; Marshall, Grayson W; Gansky, Stuart A; Parkinson, Charles R; Marshall, Sally J

    2016-02-01

    Dentin hypersensitivity often is treated by promotion of dentin tubule occlusion. In this in vitro study we evaluated nanomechanical properties and degree of tubule occlusion conferred to sound and demineralized human root dentin following treatment with a 10% (w/w) strontium acetate solution and its relation to the treatment duration and delivery method. 24 human cervical root dentin disks (8 groups of 3) were polished through 0.25 μm. 12 disks were subjected to an acid challenge (1% citric acid, pH 3.8) for 2 min. The specimens were incubated in artificial saliva, treated by soaking or brushing with deionized (DI) water or a solution of 10% strontium acetate for 2 min twice a day for 28 days. The occlusion percent and nanomechanical properties were determined at the baseline, 5, 14 and 28 days. Cross-sectioned specimens were prepared to evaluate the depth affected by strontium acetate / dentin interaction by SEM. Statistical analysis was performed using linear mixed effects models. A 10% strontium acetate treatment over 5-28 days significantly increased tubule occlusion for normal root dentin and to a lesser extent for demineralized dentin and increased the AFM based nanomechanical properties of demineralized dentin. Brushing was more effective than soaking in recovery of properties of demineralized dentin when treated with strontium. No difference in tubuleocclusion was found between the two delivery methods. Strontium acetate itself proved to have the ability to occlude dentin tubules and result in small changes in the mechanical properties of dentin. Copyright © 2015 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  13. Radiopaque Strontium Fluoroapatite Glass-Ceramics

    Science.gov (United States)

    Höland, Wolfram; Schweiger, Marcel; Dittmer, Marc; Ritzberger, Christian

    2015-01-01

    The controlled precipitation of strontium fluoroapatite crystals was studied in four base glass compositions derived from the SiO2–Al2O3–Y2O3–SrO–Na2O–K2O/Rb2O/Cs2O–P2O5–F system. The crystal phase formation of these glasses and the main properties of the glass-ceramics, such as thermal and optical properties and radiopacity were compared with a fifth, a reference glass-ceramic. The reference glass-ceramic was characterized as Ca-fluoroapatite glass-ceramic. The four strontium fluoroapatite glass-ceramics showed the following crystal phases: (a) Sr5(PO4)3F – leucite, KAlSi2O6, (b) Sr5(PO4)3F – leucite, KAlSi2O6, and nano-sized NaSrPO4, (c) Sr5(PO4)3F – pollucite, CsAlSi2O6, and nano-sized NaSrPO4, and (d) Sr5(PO4)3F – Rb-leucite, RbAlSi2O6, and nano-sized NaSrPO4. The proof of crystal phase formation was possible by X-ray diffraction. The microstructures, which were studied using scanning electron microscopy, demonstrated a uniform distribution of the crystals in the glass matrix. The Sr-fluoroapatites were precipitated based on an internal crystallization process, and the crystals demonstrated a needle-like morphology. The study of the crystal growth of needle-like Sr-fluoroapatites gave a clear evidence of an Ostwald ripening mechanism. The formation of leucite, pollucite, and Rb-leucite was based on a surface crystallization mechanism. Therefore, a twofold crystallization mechanism was successfully applied to develop these types of glass-ceramics. The main focus of this study was the controlled development of glass-ceramics exhibiting high radiopacity in comparison to the reference glass-ceramic. This goal could be achieved with all four glass-ceramics with the preferred development of the Sr-fluoroapatite – pollucite-type glass-ceramic. In addition to this main development, it was possible to control the thermal properties. Especially the Rb-leucite containing glass-ceramic showed the highest coefficient of thermal

  14. Radiopaque Strontium Fluoroapatite Glass-Ceramics.

    Science.gov (United States)

    Höland, Wolfram; Schweiger, Marcel; Dittmer, Marc; Ritzberger, Christian

    2015-01-01

    The controlled precipitation of strontium fluoroapatite crystals was studied in four base glass compositions derived from the SiO2-Al2O3-Y2O3-SrO-Na2O-K2O/Rb2O/Cs2O-P2O5-F system. The crystal phase formation of these glasses and the main properties of the glass-ceramics, such as thermal and optical properties and radiopacity were compared with a fifth, a reference glass-ceramic. The reference glass-ceramic was characterized as Ca-fluoroapatite glass-ceramic. The four strontium fluoroapatite glass-ceramics showed the following crystal phases: (a) Sr5(PO4)3F - leucite, KAlSi2O6, (b) Sr5(PO4)3F - leucite, KAlSi2O6, and nano-sized NaSrPO4, (c) Sr5(PO4)3F - pollucite, CsAlSi2O6, and nano-sized NaSrPO4, and (d) Sr5(PO4)3F - Rb-leucite, RbAlSi2O6, and nano-sized NaSrPO4. The proof of crystal phase formation was possible by X-ray diffraction. The microstructures, which were studied using scanning electron microscopy, demonstrated a uniform distribution of the crystals in the glass matrix. The Sr-fluoroapatites were precipitated based on an internal crystallization process, and the crystals demonstrated a needle-like morphology. The study of the crystal growth of needle-like Sr-fluoroapatites gave a clear evidence of an Ostwald ripening mechanism. The formation of leucite, pollucite, and Rb-leucite was based on a surface crystallization mechanism. Therefore, a twofold crystallization mechanism was successfully applied to develop these types of glass-ceramics. The main focus of this study was the controlled development of glass-ceramics exhibiting high radiopacity in comparison to the reference glass-ceramic. This goal could be achieved with all four glass-ceramics with the preferred development of the Sr-fluoroapatite - pollucite-type glass-ceramic. In addition to this main development, it was possible to control the thermal properties. Especially the Rb-leucite containing glass-ceramic showed the highest coefficient of thermal expansion (CTE). These

  15. Linking loss of sodium-iodide symporter expression to DNA damage

    International Nuclear Information System (INIS)

    Lyckesvärd, Madeleine Nordén; Kapoor, Nirmal; Ingeson-Carlsson, Camilla; Carlsson, Therese; Karlsson, Jan-Olof; Postgård, Per; Himmelman, Jakob; Forssell-Aronsson, Eva; Hammarsten, Ola; Nilsson, Mikael

    2016-01-01

    Radiotherapy of thyroid cancer with I-131 is abrogated by inherent loss of radioiodine uptake due to loss of sodium iodide symporter (NIS) expression in poorly differentiated tumor cells. It is also known that ionizing radiation per se down-regulates NIS (the stunning effect), but the mechanism is unknown. Here we investigated whether loss of NIS-mediated iodide transport may be elicited by DNA damage. Calicheamicin, a fungal toxin that specifically cleaves double-stranded DNA, induced a full scale DNA damage response mediated by the ataxia-telangiectasia mutated (ATM) kinase in quiescent normal thyrocytes. At sublethal concentrations (<1 nM) calicheamicin blocked NIS mRNA expression and transepithelial iodide transport as stimulated by thyrotropin; loss of function occurred at a much faster rate than after I-131 irradiation. KU-55933, a selective ATM kinase inhibitor, partly rescued NIS expression and iodide transport in DNA-damaged cells. Prolonged ATM inhibition in healthy cells also repressed NIS-mediated iodide transport. ATM-dependent loss of iodide transport was counteracted by IGF-1. Together, these findings indicate that NIS, the major iodide transporter of the thyroid gland, is susceptible to DNA damage involving ATM-mediated mechanisms. This uncovers novel means of poor radioiodine uptake in thyroid cells subjected to extrinsic or intrinsic genotoxic stress. - Highlights: • DNA damage inhibits polarized iodide transport in normal thyroid cells. • Down-regulation of NIS expression is mediated by activation of the ATM kinase. • Long-term ATM inhibition also represses NIS-mediated iodide transport. • IGF-1 rescues NIS expression and iodide transport in DNA-damaged cells.

  16. Linking loss of sodium-iodide symporter expression to DNA damage

    Energy Technology Data Exchange (ETDEWEB)

    Lyckesvärd, Madeleine Nordén [Sahlgrenska Cancer Center, University of Gothenburg, Göteborg (Sweden); Department of Medical Chemistry and Cell Biology, University of Gothenburg, Göteborg (Sweden); Kapoor, Nirmal [Department of Medical Chemistry and Cell Biology, University of Gothenburg, Göteborg (Sweden); Ingeson-Carlsson, Camilla; Carlsson, Therese [Sahlgrenska Cancer Center, University of Gothenburg, Göteborg (Sweden); Department of Medical Chemistry and Cell Biology, University of Gothenburg, Göteborg (Sweden); Karlsson, Jan-Olof [Department of Medical Chemistry and Cell Biology, University of Gothenburg, Göteborg (Sweden); Postgård, Per; Himmelman, Jakob; Forssell-Aronsson, Eva [Department of Radiation Physics, University of Gothenburg, Göteborg (Sweden); Hammarsten, Ola [Department of Clinical Chemistry, University of Gothenburg, Göteborg (Sweden); Nilsson, Mikael, E-mail: mikael.nilsson@gu.se [Sahlgrenska Cancer Center, University of Gothenburg, Göteborg (Sweden); Department of Medical Chemistry and Cell Biology, University of Gothenburg, Göteborg (Sweden)

    2016-05-15

    Radiotherapy of thyroid cancer with I-131 is abrogated by inherent loss of radioiodine uptake due to loss of sodium iodide symporter (NIS) expression in poorly differentiated tumor cells. It is also known that ionizing radiation per se down-regulates NIS (the stunning effect), but the mechanism is unknown. Here we investigated whether loss of NIS-mediated iodide transport may be elicited by DNA damage. Calicheamicin, a fungal toxin that specifically cleaves double-stranded DNA, induced a full scale DNA damage response mediated by the ataxia-telangiectasia mutated (ATM) kinase in quiescent normal thyrocytes. At sublethal concentrations (<1 nM) calicheamicin blocked NIS mRNA expression and transepithelial iodide transport as stimulated by thyrotropin; loss of function occurred at a much faster rate than after I-131 irradiation. KU-55933, a selective ATM kinase inhibitor, partly rescued NIS expression and iodide transport in DNA-damaged cells. Prolonged ATM inhibition in healthy cells also repressed NIS-mediated iodide transport. ATM-dependent loss of iodide transport was counteracted by IGF-1. Together, these findings indicate that NIS, the major iodide transporter of the thyroid gland, is susceptible to DNA damage involving ATM-mediated mechanisms. This uncovers novel means of poor radioiodine uptake in thyroid cells subjected to extrinsic or intrinsic genotoxic stress. - Highlights: • DNA damage inhibits polarized iodide transport in normal thyroid cells. • Down-regulation of NIS expression is mediated by activation of the ATM kinase. • Long-term ATM inhibition also represses NIS-mediated iodide transport. • IGF-1 rescues NIS expression and iodide transport in DNA-damaged cells.

  17. Linearity and Reversibility of Iodide Adsorption on Sediments from Hanford, Washington Under Water Saturated Conditions

    International Nuclear Information System (INIS)

    Um, Wooyong; Serne, R. Jeffrey; Krupka, Kenneth M.

    2004-01-01

    A series of adsorption and desorption experiments were completed to determine the linearity of iodide adsorption, as a function of concentration, and its reversibility onto sediment for geochemical conditions germane to the proposed disposal of low-level radioactive waste by the U.S. Department of Energy's Immobilized Low Activity Waste (ILAW) program at the Hanford Site in southeastern Washington. Iodine-129 is predicted to be one of the top three long-term risk drivers based on past performance assessment conducted for the eventual disposal of the low-level portion of radioactive wastes currently stored in underground storage tanks at Hanford, because iodide exhibits little adsorption affinity to mineral surfaces resulting in high mobility in the subsurface environment. Adsorption experiments, conducted with Hanford formation sediments and groundwater spiked with dissolved 125I (as an analog tracer for 129I), indicated that iodide adsorption was very low at pH 7.5 and could be represented by a linear isotherm up to a total concentration of 100 mg/L dissolved iodide. The linearity of iodide adsorption up to concentrations of 100 mg/L validates the use of the linear Kd construct in transport models to predict the fate and transport of 129I in subsurface systems at Hanford. The results of desorption experiments indicated that up to 60% of adsorbed iodide was readily desorbed after 14 days by the same groundwater solution. Iodide adsorption was considered to be partially reversible or weakly binding on the sediments. Even though small amount of initial iodide is retarded by adsorption reactions at mineral-water interfaces, the weak adsorption affinity results in release of iodide when iodide free pore waters and ground waters contact the contaminated sediments in the vadose zone and aquifer systems

  18. Strontium cobaltite oxygen sponge catalyst and methods of use

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Ho Nyung; Jeen, Hyoungjeen; Choi, Woo Seok; Biegalski, Michael; Folkman, Chad M.; Tung, I-Cheng; Fong, Dillon D.; Freeland, John W.; Shin, Dongwon; Ohta, Hiromichi; Chisholm, Matthew F.

    2017-01-24

    Rapid, reversible redox activity may be accomplished at significantly reduced temperatures, as low as about 200.degree. C., from epitaxially stabilized, oxygen vacancy ordered SrCoO.sub.2.5 and thermodynamically unfavorable perovskite SrCoO.sub.3-.delta.. The fast, low temperature redox activity in SrCoO.sub.3-.delta. may be attributed to a small Gibbs free energy difference between the two topotactic phases. Epitaxially stabilized thin films of strontium cobaltite provide a catalyst adapted to rapidly transition between oxidation states at substantially low temperatures. Methods of transitioning a strontium cobaltite catalyst from a first oxidation state to a second oxidation state are described.

  19. ADSORPTION OF STRONTIUM IONS FROM WATER ON MODIFIED ACTIVATED CARBONS

    Directory of Open Access Journals (Sweden)

    Mihai Ciobanu

    2016-12-01

    Full Text Available Adsorption of strontium ions from aqueous solutions on active carbons CAN-7 and oxidized CAN-8 has been studied. It has been found that allure of the adsorption isotherms for both studied active carbons are practically identical. Studies have shown that the adsorption isotherms for strontium ions from aqueous solutions are well described by the Langmuir and Dubinin-Radushkevich equations, respectively. The surface heterogeneity of activated carbons CAN-7 and oxidized CAN-8 has been assessed by using Freundlich equation.

  20. Conductivity and thermodynamic characteristic of superionic transition in strontium chloride

    International Nuclear Information System (INIS)

    Voronin, B.M.; Prisyazhnyj, V.D.

    1989-01-01

    Electric conductivity of strontium polycrystalline chloride in the wide temperature range including melting point is measured. Reciprocally caused anomalous behaviour of kinetic and thermodynamic properties, which relates to peculiarities of salt transition to a superionic state is established in the region of high temperatures. Thermodynamic functions corresponding to crystal anion sublattice disordering are determined and characterized. Comparative analysis of data on strontium chloride and other structural-like salts testifies about step-by-step washing-out character of superionic transition, and the depth of transition (the degree of disordering) reached at melting points relates regularly to relative sizes of cations and anions in the fluorite lattice

  1. Spectrographic determination of strontium in yttrium-90 solutions

    International Nuclear Information System (INIS)

    Roca, M.; Capdevila, C.

    1970-01-01

    The copper spark method has been used for determining strontium in the concentration range 1-100 g/ml in yttrium-90 solutions containing 0,5 % or thereabouts of ammonium citrate. The influence of the citric acid as well as the ammonium citrate with regard to 2N HCL solutions has been studied: the citric acid enhances the line intensities of strontium. The employment of either barium or lanthanum as reference element compensates for this enhancement. Because of the increase in sensitivity mentioned above, the study of influence of the citric acid has been extended and several impurities usually determined in radioisotope solutions have been considered. (Author) 4 refs

  2. Dielectric loss of strontium titanate thin films

    Science.gov (United States)

    Dalberth, Mark Joseph

    1999-12-01

    Interest in strontium titanate (STO) thin films for microwave device applications continues to grow, fueled by the telecommunications industry's interest in phase shifters and tunable filters. The optimization of these devices depends upon increasing the phase or frequency tuning and decreasing the losses in the films. Currently, the dielectric response of thin film STO is poorly understood through lack of data and a theory to describe it. We have studied the growth of STO using pulsed laser deposition and single crystal substrates like lanthanum aluminate and neodymium gallate. We have researched ways to use ring resonators to accurately measure the dielectric response as a function of temperature, electric field, and frequency from low radio frequencies to a few gigahertz. Our films grown on lanthanum aluminate show marked frequency dispersion in the real part of the dielectric constant and hints of thermally activated loss behavior. We also found that films grown with conditions that optimized the dielectric constant showed increased losses. In an attempt to simplify the system, we developed a technique called epitaxial lift off, which has allowed us to study films removed from their growth substrates. These free standing films have low losses and show obvious thermally activated behavior. The "amount of tuning," as measured by a figure of merit, KE, is greater in these films than in the films still attached to their growth substrates. We have developed a theory that describes the real and imaginary parts of the dielectric constant. The theory models the real part using a mean field description of the ionic motion in the crystal and includes the loss by incorporating the motion of charged defects in the films.

  3. Crystal structure of strontium dinickel iron orthophosphate

    Directory of Open Access Journals (Sweden)

    Said Ouaatta

    2015-10-01

    Full Text Available The title compound, SrNi2Fe(PO43, synthesized by solid-state reaction, crystallizes in an ordered variant of the α-CrPO4 structure. In the asymmetric unit, two O atoms are in general positions, whereas all others atoms are in special positions of the space group Imma: the Sr cation and one P atom occupy the Wyckoff position 4e (mm2, Fe is on 4b (2/m, Ni and the other P atom are on 8g (2, one O atom is on 8h (m and the other on 8i (m. The three-dimensional framework of the crystal structure is built up by [PO4] tetrahedra, [FeO6] octahedra and [Ni2O10] dimers of edge-sharing octahedra, linked through common corners or edges. This structure comprises two types of layers stacked alternately along the [100] direction. The first layer is formed by edge-sharing octahedra ([Ni2O10] dimer linked to [PO4] tetrahedra via common edges while the second layer is built up from a strontium row followed by infinite chains of alternating [PO4] tetrahedra and FeO6 octahedra sharing apices. The layers are held together through vertices of [PO4] tetrahedra and [FeO6] octahedra, leading to the appearance of two types of tunnels parallel to the a- and b-axis directions in which the Sr cations are located. Each Sr cation is surrounded by eight O atoms.

  4. Strontium stable isotope behaviour accompanying basalt weathering

    Science.gov (United States)

    Burton, K. W.; Parkinson, I. J.; Gíslason, S. G. R.

    2016-12-01

    The strontium (Sr) stable isotope composition of rivers is strongly controlled by the balance of carbonate to silicate weathering (Krabbenhöft et al. 2010; Pearce et al. 2015). However, rivers draining silicate catchments possess distinctly heavier Sr stable isotope values than their bedrock compositions, pointing to significant fractionation during weathering. Some have argued for preferential release of heavy Sr from primary phases during chemical weathering, others for the formation of secondary weathering minerals that incorporate light isotopes. This study presents high-precision double-spike Sr stable isotope data for soils, rivers, ground waters and estuarine waters from Iceland, reflecting both natural weathering and societal impacts on those environments. The bedrock in Iceland is dominantly basaltic, d88/86Sr ≈ +0.27, extending to lighter values for rhyolites. Geothermal waters range from basaltic Sr stable compositions to those akin to seawater. Soil pore waters reflect a balance of input from primary mineral weathering, precipitation and litter recycling and removal into secondary phases and vegetation. Rivers and ground waters possess a wide range of d88/86Sr compositions from +0.101 to +0.858. Elemental and isotope data indicate that this fractionation primarily results from the formation or dissolution of secondary zeolite (d88/86Sr ≈ +0.10), but also carbonate (d88/86Sr ≈ +0.22) and sometimes anhydrite (d88/86Sr ≈ -0.73), driving the residual waters to heavier or lighter values, respectively. Estuarine waters largely reflect mixing with seawater, but are also be affected by adsorption onto particulates, again driving water to heavy values. Overall, these data indicate that the stability and nature of secondary weathering phases, exerts a strong control on the Sr stable isotope composition of silicate rivers. [1] Krabbenhöft et al. (2010) Geochim. Cosmochim. Acta 74, 4097-4109. [2] Pearce et al. (2015) Geochim. Cosmochim. Acta 157, 125-146.

  5. Horizontal Ampoule Growth and Characterization of Mercuric Iodide at Controlled Gas Pressures for X-Ray and Gamma Ray Spectrometers

    International Nuclear Information System (INIS)

    Douglas, S.; McGregor Elsa; Ariesanti Bridget Corcoran

    2004-01-01

    The project developed a new method for producing high quality mercuric iodide crystals of x-ray and gamma spectrometers. Included are characterization of mercuric iodide crystal properties as a function of growth environment and fabrication and demonstration of room-temperature-operated high-resolution mercuric iodide spectrometers

  6. Polarographic determination of indium and thallium iodides in phosphor tablets

    International Nuclear Information System (INIS)

    Babich, G.A.; Dzhurka, G.F.; Kozhushko, G.M.; Kravtsova, K.F.; Magda, V.I.

    1984-01-01

    The technique of polarographic determination of indium and thallium iodides in phosphor tablets without preliminary separation of elements was developed. Mercury-dropping electrode was used as an indicator, and saturated calomel electrode was used as an auxiliary electrode. A recording of reduction currents was performed in the potential interval from -0.25 up to 1.15 V at potential sweep speed of 200 mV/min. Optimum conditions of sample acidic decomposition and polarography were presented. A solution of ethylene diamine (0.5 M), of ammonia (0.25 M) and of potassium chloride (0.05 M) served as a background electrolyte. The suggested technique allows one to determine component contents in tablets with a satisfactory accuracy. A period of one tablet analysis constitutes 1.5 h

  7. Mercuric iodide crystals obtained by solvent evaporation using ethanol

    International Nuclear Information System (INIS)

    Ugucioni, J.C.; Ghilardi Netto, T.; Mulato, M.

    2010-01-01

    Millimeter-sized mercuric iodide crystals were fabricated by the solvent evaporation technique using pure ethanol as a solvent. Three different conditions for solution evaporation were tested: (i) in the dark at room temperature; (ii) in the presence of light at room temperature and (iii) in an oven at 40 deg. C. Morphology, structure, optical and electrical properties were investigated using several techniques. Crystals fabricated in the dark show better properties and stability than others, possibly because the larger the energy of the system, the larger the number of induced growth defects. The crystals fabricated in the dark have adequate structure for higher resistivity and activation energy close to half the optical band-gap, as desired. With proper encapsulation these crystals might be good candidates for the development of ionizing radiation sensors.

  8. Direct photometric determination of fluorides in potassium chloride and iodide

    International Nuclear Information System (INIS)

    Dedkova, V.P.; Savvin, S.B.

    1985-01-01

    An attempt is made to apply the technique of determining fluorides with xylenol orange and sulfochlorophenol S as being the most sensitive in the analysis of of fiber optics. It is known that an increase of the sensitivity of the determination can be achieved on increasing the sample size of the substance to be analyzed, and the length of the absorbing layer. However, a high salt background may have a strong influence on the course of the reaction, and a supplementary of this effect is mad. Potassium chloride and iodide were selected as model compounds. A direct photometric procedure is proposed for determining fluorides in the samples, with a determination limit of 5 x 10 -6 %. Such a low determination limit is achieved by increasing the sample weight to 3 g, by increasing the length of the absorbing layer in the cell to 50 mm, and by using a highly sensitive reaction for determining fluorides with zirconium and xylenol orange

  9. Electrical and photomechanical effects of plastic deformation of mercuric iodide

    International Nuclear Information System (INIS)

    Marschall, J.; Milstein, F.; Gerrish, V.

    1991-01-01

    The effects of bulk plastic deformation of mercuric iodide (HgI 2 ), upon some of the electronic properties relevant to the performance of HgI 2 as a radiation detector were examined experimentally. Hole lifetimes, as well as hole and electron mobilities, were measured at various stages of sample deformation. Hole lifetimes were found to decrease by a factor of 2 under strains of several percent; carrier mobilities varied within experimental error, except during creep loading where electron and hole mobilities decreased by about 65 % and 25 %, respectively. Additionally, dark current measurements were made on specimens with varying degrees of accumulated plastic damage caused by c plane shear. Dark current values did not strongly reflect the extent of bulk plastic damage in deformed specimens. 16 refs., 4 figs., 1 tab

  10. Rapid sonochemical preparation of shape-selective lead iodide

    International Nuclear Information System (INIS)

    Huang, Baojun; He, Qin; Fa, Wenjun; Li, Pinjiang; Zhang, Yange; Zheng, Zhi

    2012-01-01

    Graphical abstract: SEM morphologies of various PbI2 products obtained with the iodine concentration of 6.7 g/L and irradiation time of 1 minute at the reaction temperatures of 35 °C (a), 25 °C (b), and 15 °C (c). Highlights: ► PbI 2 with various morphologies were rapidly formed at room temperature. ► We could well control the morphologies of PbI 2 by changing reaction conditions. ► The PbI 2 films could better resist rolling in a liquid media. -- Abstract: Lead iodide (PbI 2 ) films/crystals with various nano/micro morphologies (e.g., Nanoflake, block and microrod) were rapidly synthesized by taking advantage of a simple sonochemical method. The PbI 2 crystals with uniform nanoflake structures could be fabricated directly on lead foils with the irradiation time as short as 36 s via interfacial reaction between lead foils and elemental iodine in ethanol at ambient temperature. It was found experimentally that the morphologies of the resulting thin films/crystals could be well controlled by the adjustment of several parameters including irradiation time, reaction solvents, iodine concentration, ultrasonic power, and reaction temperature. Most importantly, the resultant PbI 2 films are stable enough to resist rolling under the drastic ultrasound irradiation in a liquid media. This method is believed to be the fastest way for in situ fabrication of morphology-controlled semiconductor films on various metal substrates for subsequent applications related to the other metal iodide or metal sulfide semiconductor films.

  11. Novel Pharmaceutical Strontium Malonate Influence on Calcium and Strontium Adsorption by Dog Femur and by Dog Teeth in a Four-Week Toxicity Study

    DEFF Research Database (Denmark)

    Raffalt, Anders Christer; Christgau, Stephan; Andersen, Jens Enevold Thaulov

    of osteoporosis. As part of this development the compound was administered in doses of 0 (placebo), 300, 1000 and 3000 mg/kg/day to beagle dogs for a period of 4 weeks. We measured the incorporation of strontium in bone, marrow and teeth in this study. Analysis by inductively coupled plasma mass spectrometry...... marginally higher incorporation of strontium suggesting that saturation levels were reached with the lowest dose level. There was no gender difference in strontium incorporation. Correlations of strontium levels with Sr/Ca-ratio and other important biological parameters were investigated....

  12. Evaluation of quaternary ammonium halides for removal of methyl iodide from flowing air streams

    International Nuclear Information System (INIS)

    Freeman, W.P.; Mohacsi, T.G.; Kovach, J.L.

    1985-01-01

    The quaternary ammonium halides of several tertiary amines were used as impregnants on activated carbon and were tested for methyl iodide penetration in accordance with test Method A, ASTM D3803, 1979, ''Standard Test Methods for Radio-iodine Testing of Nuclear Grade Gas Phase Adsorbents''. The results suggest that the primary removal mechanism for methyl iodide-131 is isotopic exchange with the quaternary ammonium halide. For example, a 5 wt% impregnation of each of the tetramethyl, tetraethyl, tetrapropyl and tetrabutyl ammonium iodides on activated carbon yielded percent penetrations of 0.47, 0.53, 0.78, and 0.08 respectively when tested according to Method A of ASTM D3803. A sample impregnated with 5% tetramethyl ammonium hydroxide gave a methyl iodide penetration of 64.87%, thus supporting the isotopic exchange mechanism for removal. It has been a generally held belief that the success of tertiary amines as impregnants for radioiodine removal is a result of their ability to complex with the methyl iodide. The results of the work indicates that the superiority of the tertiary amines similar to triethylene diamine and quinuclidine, when compared to their straight chain analogs, is a result of their ease in reacting with methyl iodide-127 to form the quaternary ammonium iodide followed by isotopic exchange

  13. Thermal behaviour of strontium tartrate single crystals grown in gel

    Indian Academy of Sciences (India)

    Unknown

    Keywords. Strontium tartrate; dopant; effect of magnetic field; thermal behaviour. 1. Introduction ... tals of such type of compounds cannot be grown by either slow evaporation or ... is observed under a stereo binocular microscope (Carl. Zeiss) and ... a depth of 1⋅8 cm due to the diffusion of the top solution. After about a week ...

  14. New Composite Sorbents for Caesium and Strontium Ions Sorption

    Directory of Open Access Journals (Sweden)

    Mykola Kartel

    2017-06-01

    Full Text Available Composite lignocellulose-inorganic sorbents derived from plant residues of agriculture and food industry, modified with ferrocyanides of d-metals and hydrated antimony pentoxide were prepared. Caesium and strontium ions removal from water was tested by radiotracer method. Sorption of heavy metal ions, methylene blue, gelatin, vitamin B12 was also studied.

  15. Thermal behaviour of strontium tartrate single crystals grown in gel

    Indian Academy of Sciences (India)

    Thermal behaviour of strontium tartrate crystals grown with the aid of sodium metasilicate gel is investigated using thermogravimetry (TG) and differential thermal analysis (DTA). Effect of magnetic field and dopant (Pb)2+ on the crystal stability is also studied using thermal analysis. This study reveals that water molecules are ...

  16. Strontium adsorption and penetration in kaolinite at low Sr

    NARCIS (Netherlands)

    Ning, Zigong; Ishiguro, Munehide; Koopal, Luuk K.; Sato, Tsutomu; Kashiwagi, Junichi

    2017-01-01

    Behavior of radioactive strontium (Sr2+) in contaminated soils is an important issue in relation to nuclear power plant accidents. The Sr2+ adsorption on kaolinite and its migration in a kaolinite soil were investigated because toxic effects of radioactive Sr2+ have been found to be very severe for

  17. Study of sorption processes of strontium on the synthetic hydroxyapatite

    International Nuclear Information System (INIS)

    Rosskopfova, O.; Galambos, M.; Rajec, P.

    2011-01-01

    The sorption of strontium on synthetic hydroxyapatite was investigated using batch method and radiotracer technique. The hydroxyapatite samples were prepared by a wet precipitation process followed by calcination of calcium phosphate that precipitated from aqueous solution. Also, commercial hydroxyapatites were used. The sorption of strontium on hydroxyapatite depended on the method of preparation and it was pH independent ranging from 4 to 9 as a result of buffering properties of hydroxyapatite. The distribution coefficient K d was significantly decreased with increasing concentration of Sr 2+ and Ca 2+ ions in solution with concentration above 1 x 10 -3 mol dm -3 . The percentage strontium sorption for commercial and by wet method prepared hydroxyapatite was in the range of 83-96%, while calcined hydroxyapatite was ranging from 10 to 30%. The experimental data for sorption of strontium have been interpreted in the term of Langmuir isotherm. The sorption of Sr 2+ ions was performed by ion-exchange with Ca 2+ cations on the crystal surface of hydroxyapatite. Although calcined hydroxyapatite is successfully used as biomaterial for hard tissues repair, it is not used for the treatment of liquid wastes. (author)

  18. Coherent normalization of finger strontium XRF measurements: feasibility and limitations

    Energy Technology Data Exchange (ETDEWEB)

    Zamburlini, M; Pejovic-Milic, A; Chettle, D R [Medical Physics and Applied Radiation Sciences, McMaster University, Hamilton, L8S 4K1 (Canada)

    2008-08-07

    A non-invasive in vivo x-ray fluorescence (XRF) method of measuring bone strontium concentrations has previously been reported as a potential diagnostic tool able to detect strontium concentration in the finger and ankle bones. The feasibility of coherent normalization for {sup 125}I-source-based finger bone strontium x-ray fluorescence (XRF) measurements is assessed here by theoretical considerations and Monte Carlo simulations. Normalization would have several advantages, among which are the correction for the signal attenuation by the overlying soft tissue, and intersubject variability in the bone size and shape. The coherent normalization of bone strontium XRF measurements presents several challenges dictated by the behaviour of the coherent cross section and mass attenuation coefficient at the energies involved. It was found that the coherent normalization alone with either 22.1 keV or 35.5 keV photons was not successful in correcting for the overlying soft tissue attenuation. However, it was found that the coherent peak at 35.5 keV was able to correct effectively for variability in the finger bone size between people. Thus, it is suggested that, if the overlying soft tissue thickness can be obtained by means of an independent measurement, the 35.5 keV peak can be used to correct for the bone size, with an overall accuracy of the normalization process of better than 10%. (note)

  19. Phonons in face-centred cubic calcium and strontium

    International Nuclear Information System (INIS)

    Singh, S.P.; Rathore, R.P.S.

    1984-01-01

    The axially symmetric and unpaired forces are employed to analyse the phonon dispersion and elastic behaviour of face centred cubic calcium and strontium which have so far not been studied adequately. The model with three parameters predicts the results which agree marvellously with the recently measured data. (author)

  20. Substitution of strontium for calcium in glass ionomer cements (Part ...

    African Journals Online (AJOL)

    Objectives: To investigate the effects of substituting strontium for calcium in fluoroaluminosilicate glass on the mechanical and ion-releasing properties of high-viscosity glass ionomer cements. Design: An exploratory, laboratory-based study. Setting: Dental biomaterials research laboratory, Dental Physical Sciences Unit, ...

  1. Strontium-90 content of human bone collected in 1967

    International Nuclear Information System (INIS)

    Jeanmaire, L.; Patti, F.

    1969-01-01

    This report follows report CEA-R-3381 and presents the strontium 90 content of human bones collected in 1967 in the Paris area. The main trend is much the same as during 1966; contamination levels are falling down in infants up to 5 year old. Beyond this age, the values are the same or experience a slight increase. (authors) [fr

  2. Effect of selected foodstuffs on strontium 89 metabolism in rats

    International Nuclear Information System (INIS)

    Keslev, D.; Jotov, M.

    1975-01-01

    The influence of a variety of food products used in human nutrition on strontium-89 cumulation in rat organism is studied. To this end the animals were fed for a week with meat, beans, maize, white and brown bread, cabbage, milk or potatoes prepared so as to be edible by man. Then for additional 15 days the animals were fed the same diet + a daily oral dose of 2 μCi strontium-89. On the 16th day radionuclide activity in the thigh bone was measured. Beans was the food product exerting optimal limiting effect on strontium deposition (reduction factor (RF) 17), milk and ranking next (RF 13, resp. 6.5). All other products showed approximately equal efforts (RF 1.4 - 1.8). The different calcium content of each of these food products is responsible for their different effectiveness. Together with the discrimination which the living organism displays in the presence of calcium, other constituents of the food products which form complexes with strontium and prevent its deposition in the bones are equally essential. (Ch.K.)

  3. Quaternary system of lithium, potassium, calcium and strontium fluorides

    International Nuclear Information System (INIS)

    Garkushin, I.K.; Voronin, K.Yu.; Dibirov, M.A.; Miftakhov, T.T.

    1996-01-01

    Four-component system of lithium, potassium, calcium and strontium fluorides is studied by differential thermal analysis. A low-melting eutectic composition is revealed, specific fusion heat of the composition is experimentally determined, its thermal properties are calculated. 8 refs., 5 figs., 1 tab

  4. Influence of strontium on the cubic to ordered hexagonal phase

    Indian Academy of Sciences (India)

    ... Refresher Courses · Symposia · Live Streaming. Home; Journals; Bulletin of Materials Science; Volume 23; Issue 6. Influence of strontium on the cubic to ordered hexagonal phase transformation in barium magnesium niobate. M Thirumal A K Ganguli. Phase Transitions Volume 23 Issue 6 December 2000 pp 495-498 ...

  5. Strontium-90 and cesium-137 in fresh water

    International Nuclear Information System (INIS)

    1978-01-01

    Japan Chemical Analysis Center has analysed the strontium-90 and Cesium-137 contents in fresh water from 7 prefectures in Japan by the commission of Science and Technology Agency of Japanese Government. The method described in ''Radioactivity Survey Data in Japan No. 43 (NIRS-RSD-43, 1977) was applied to the analysis of these two radionuclides in samples. (author)

  6. Membrane-based separation technologies for cesium, strontium, and technetium

    International Nuclear Information System (INIS)

    Kafka, T.

    1996-01-01

    This work is one of two parallel projects that are part of an ESP task to develop high-capacity, selective, solid extractants for cesium, strontium, and technetium from nuclear wastes. In this subtask, Pacific Northwest National Laboratory (PNNL) is collaborating with 3M, St. Paul, Minnesota, working in cooperation with IBC Advanced Technologies, American Fork, Utah

  7. Rubidium-strontium and uranium-lead isotopic age studies

    International Nuclear Information System (INIS)

    Loveridge, W.D.

    1980-01-01

    Rubidium-strontium whole rock isochron ages and initial 87 Sr/ 86 Sr ratios and uranium-lead ages on zircon from suites of samples selected from localities across Canada are presented. Descriptions of the geological probelms and interpretations of the measured ages are included. Laboratory age determination methods and techniques are described or referenced. (auth)

  8. Effects of strontium ranelate on spinal osteoarthritis progression

    DEFF Research Database (Denmark)

    Bruyere, O; Delferriere, D; Roux, C

    2008-01-01

    OBJECTIVE: The aim of this study was to determine whether a 3-year treatment with strontium ranelate could delay the progression of spinal osteoarthritis (OA). METHODS: This study was a post-hoc analysis of pooled data from the Spinal Osteoporosis Therapeutic Intervention (SOTI) and TReatment...

  9. Dielectric Strontium Zirconate Sprayed by a Plasma Torch.

    Czech Academy of Sciences Publication Activity Database

    Ctibor, Pavel; Sedláček, J.; Janata, Marek

    2017-01-01

    Roč. 10, č. 4 (2017), s. 225-230 ISSN 2008-2134 Institutional support: RVO:61389021 Keywords : Plasma spraying * Electrical properties * Strontium Zirconate * Insulators Subject RIV: JH - Ceramics, Fire-Resistant Materials and Glass OBOR OECD: Ceramics www.pccc.icrc.ac.ir/Articles/18/1/18/1010/

  10. Substitution of strontium for calcium in glass ionomer cements (Part ...

    African Journals Online (AJOL)

    Substitution of strontium for calcium in glass ionomer cements (Part 1): Glass synthesis and characterisation, and the effects on the cement handling variables and ... acid to form glass ionomer cements, whose properties were investigated at different time points: working and setting times were determined by rheometry; and, ...

  11. Parametric Study on the Organic Iodide Behavior during a Severe Accident

    International Nuclear Information System (INIS)

    Ryu, Myung Hyun; Kim, Han Chul; Kim, Do Sam

    2011-01-01

    Iodine is a major contributor to the potential health risk for the public following a severe accident from a nuclear power plant. Most of metal-iodides, the major form of iodine that enters the containment, can be readily dissolved in the sump water and result in iodide ions. These will be oxidized to form volatile I 2 through a large number of reactions such as radiolysis and hydrolysis. The organic radicals, made from organics such as paint in the sump water, react with iodine to produce organic iodides. Volatile iodine moves from the sump water to the atmosphere mainly by diffusion and natural convection, and react with surfaces and air radiolysis products (ARPs). Painted surfaces act as a sink for I 2 and as a source for organic iodides through adsorption and desorption. ARPs react with I 2 to form iodine oxides, which leads to the decrease of I 2 and organic iodides. Among the large number of iodine species, organic iodides have been extensively studied recently due to their volatility and very low retention. Qualified tools for modeling these phenomena have been developed and validated by several experiments such as EPICUR, PARIS and OECD-BIP. While mechanistic codes model a large number of reactions and species, semiempirical codes such as IODE or IMOD treat major ones. KINS developed a simple iodine model, RAIM (Radio-active iodine chemistry model), based on the IMOD methodology in order to deal with organic iodides conveniently, coupling with an integrated severe-accident analysis code. There are a number of mechanisms that affect the behavior of organic iodides. In this study, effects of pH of the aqueous phase, temperature, radiation dose rate, surface area of organic paints, initial iodine loads that are known to be important to organic iodide formation were studied analytically with RAIM, and also theoretically

  12. Parametric Study on the Organic Iodide Behavior during a Severe Accident

    Energy Technology Data Exchange (ETDEWEB)

    Ryu, Myung Hyun; Kim, Han Chul; Kim, Do Sam [Korea Institute of Nuclear Safety, Daejeon (Korea, Republic of)

    2011-10-15

    Iodine is a major contributor to the potential health risk for the public following a severe accident from a nuclear power plant. Most of metal-iodides, the major form of iodine that enters the containment, can be readily dissolved in the sump water and result in iodide ions. These will be oxidized to form volatile I{sub 2} through a large number of reactions such as radiolysis and hydrolysis. The organic radicals, made from organics such as paint in the sump water, react with iodine to produce organic iodides. Volatile iodine moves from the sump water to the atmosphere mainly by diffusion and natural convection, and react with surfaces and air radiolysis products (ARPs). Painted surfaces act as a sink for I{sub 2} and as a source for organic iodides through adsorption and desorption. ARPs react with I{sub 2} to form iodine oxides, which leads to the decrease of I{sub 2} and organic iodides. Among the large number of iodine species, organic iodides have been extensively studied recently due to their volatility and very low retention. Qualified tools for modeling these phenomena have been developed and validated by several experiments such as EPICUR, PARIS and OECD-BIP. While mechanistic codes model a large number of reactions and species, semiempirical codes such as IODE or IMOD treat major ones. KINS developed a simple iodine model, RAIM (Radio-active iodine chemistry model), based on the IMOD methodology in order to deal with organic iodides conveniently, coupling with an integrated severe-accident analysis code. There are a number of mechanisms that affect the behavior of organic iodides. In this study, effects of pH of the aqueous phase, temperature, radiation dose rate, surface area of organic paints, initial iodine loads that are known to be important to organic iodide formation were studied analytically with RAIM, and also theoretically

  13. Thyroid iodide compartments and their implication in the rat thyroid iodine organification

    International Nuclear Information System (INIS)

    Bastiani, P.; Simon, C.

    1982-01-01

    To estimate the relative participation of transported and intrathyroidally generated iodide (internal iodide) in the iodination of newly synthesized and preexisting thyroglobulin (Tg) in the rat thyroid, the specific radioactivities (SRAs) of thyroid iodide, Tg, lysosomal iodine, and plasma hormones were followed for 92 h after radioactive iodide injection in intact or hypophysectomized rats. In control rats, the SRA of Tg and lysosomal iodine reached a maximum at 12 h. However, the SRA of lysosomal iodide was always smaller than that of Tg. In contrast, the SRA of hormonal iodide attained a maximum at 48 h. Thus, newly labeled iodine is endocytosed and mixed inside the lysosomes with older previously iodinated molecules; hormone secretion is mainly due to old labeled iodine (i.e. iodine with a high SRA from 48-96 h). These results are consistent with the presence of least two Tg compartments, with different turnover rates and hormone contents. On the other hand, in hypophysectomized rats, the SRA of Tg, lysosomes, and hormones showed only one maximum, at 24 h. Furthermore, the SRAs of Tg and lysosomes were similar at each time interval. It is inferred that in such rats, the old labeled iodine compartment is strongly reduced, and that inside the lysosomes, newly labeled iodine is predominant. Since in hypophysectomized rats, the recycling of iodide is abolished, it is concluded that in normal rats: 1) transported iodide is organified mainly by direct iodination of newly synthesized Tg, independently of TSH, and 2) internal iodide is organified mainly by delayed iodination of preexisting Tg, this process being TSH dependent

  14. Solvent effect on the rate and equilibrium of reaction between 10-phenylphenoxarsine and methyl iodide

    International Nuclear Information System (INIS)

    Gavrilov, V.I.; Gumerov, N.S.; Rakhmatullin, R.R.

    1990-01-01

    Effect of solvent nature on nucleophilic capacity of three-coordinated arsenic and the equilibrium state of 10-phenylphenoxarsine (PA) reaction with methyl iodide are studied. Kinetic investigations are carried out by the conductometry at 24,35,45 deg C. It is established that quaternization of PA with methyl iodide when substituting a solvent (ketone for alcohol) increases 3-14 times with simultaneous growth of the activation energy value. When transforming from aprotic solvents to protic ones PA interaction equilibrium with methyl iodide shifts to the side of arsonic salt formation

  15. The method of determination of micro quantities of labeled iodide in carrier free Na125 solution

    International Nuclear Information System (INIS)

    Kholbaev, A.Kh.; Shilin, E.A.

    1996-01-01

    The method of determination of microquantities of labelled iodide in Na 125 carrier-free solution was elaborated. This method permits to increase the sensitivity and radiation protection of the determination of labeled iodide. It includes oxidation of iodide by iodate in diluted sulphuric acid with molar concentration 0,03-0,04 mole/l. The extraction of I 2 is made by toluene. The coloured solution is made and optical density is measured at λ=640 nm at the 10 mm optical path .(A.A.D.)

  16. Effect of strontium ranelate on bone mineral: Analysis of nanoscale compositional changes.

    Science.gov (United States)

    Rossi, André L; Moldovan, Simona; Querido, William; Rossi, Alexandre; Werckmann, Jacques; Ersen, Ovidiu; Farina, Marcos

    2014-01-01

    Strontium ranelate has been used to prevent bone loss and stimulate bone regeneration. Although strontium may integrate into the bone crystal lattice, the chemical and structural modifications of the bone when strontium interacts with the mineral phase are not completely understood. The objective of this study was to evaluate apatite from the mandibles of rats treated with strontium ranelate in the drinking water and compare its characteristics with those from untreated rats and synthetic apatites with and without strontium. Electron energy loss near edge structures from phosphorus, carbon, calcium and strontium were obtained by electron energy loss spectroscopy in a transmission electron microscope. The strontium signal was detected in the biological and synthetic samples containing strontium. The relative quantification of carbon by analyzing the CK edge at an energy loss of ΔE = 284 eV showed an increase in the number of carbonate groups in the bone mineral of treated rats. A synthetic strontium-containing sample used as control did not exhibit a carbon signal. This study showed physicochemical modifications in the bone mineral at the nanoscale caused by the systemic administration of strontium ranelate. Copyright © 2013 Elsevier Ltd. All rights reserved.

  17. Microwave-assisted fabrication of strontium doped apatite coating on Ti6Al4V

    Energy Technology Data Exchange (ETDEWEB)

    Zhou, Huan, E-mail: huanzhou@cczu.edu.cn [Institute of Biomedical Engineering and Health Sciences, Changzhou University, Changzhou, Jiangsu 213164 (China); Kong, Shiqin [Institute of Biomedical Engineering and Health Sciences, Changzhou University, Changzhou, Jiangsu 213164 (China); School of Materials Science and Engineering, Changzhou University, Changzhou, Jiangsu 213164 (China); Pan, Yan; Zhang, Zhiguo [Institute of Biomedical Engineering and Health Sciences, Changzhou University, Changzhou, Jiangsu 213164 (China); Deng, Linhong, E-mail: dlh@cczu.edu.cn [Institute of Biomedical Engineering and Health Sciences, Changzhou University, Changzhou, Jiangsu 213164 (China)

    2015-11-01

    Strontium has been shown to be a beneficial dopant to calcium phosphates when incorporated at nontoxic level. In the present work we studied the possibility of solution derived doping strontium into calcium phosphate coatings on titanium alloy Ti6Al4V based implants by a recently reported microwave-assisted method. By using this method strontium doped calcium phosphate nuclei were deposited to pretreated titanium alloy surface dot by dot to compose a crack-free coating layer. The presence of strontium in solution led to reduced roughness of the coating and finer nucleus size formed. In vitro study found that proliferation and differentiation of osteoblast cells seeded on the coating were influenced by strontium content in coatings, showing an increasing followed by a decreasing behavior with increasing substitution of calcium by strontium. It is suggested that this new microwave-assisted strontium doped calcium phosphate coatings may have great potential in implant modification. - Highlights: • Strontium doped calcium phosphate coating is deposited with microwave irradiation. • Increase of strontium reduces coating roughness and results in finer nucleus size. • Proliferation and differentiation of osteoblasts depend on doped strontium content.

  18. Dissolved strontium and calcium levels in the tropical Indian Ocean

    Science.gov (United States)

    Steiner, Zvi; Sarkar, Amit; Turchyn, Alexandra

    2017-04-01

    Measurements of seawater alkalinity and dissolved calcium concentrations along oceanic transects are often used to calculate calcium carbonate precipitation and dissolution rates. Given that the distribution coefficient of strontium in CaCO3 varies greatly between different groups of organisms, adding precise measurements of dissolved strontium concentrations provides opportunities to also track relative contributions of these different groups to the regional CaCO3 cycle. However, there are several obstacles to this approach. These obstacles include unresolved systematic discrepancies between seawater calcium and alkalinity data, very large analytical noise around the calcium concentration measurements and the unconstrained role of acantharia (radiolarian precipitating SrSO4 skeletons) in the marine strontium cycle. During the first cruise of the second International Indian Ocean Expedition (IIOE-2) water samples were collected along 67°E from 9°N to 5°S to explore the dissolution rate of calcium carbonate in the water. The dissolution rate can be calculated by combining measurements of water column potential alkalinity with calcium and strontium concentrations measured by ICP-OES and calcium concentration measurements using isotope dilution thermal ionization mass spectrometry (ID-TIMS). CaCO3 mineral saturation state calculated using pH and total alkalinity suggests that along 67°E, the aragonite saturation horizon lays at depth of 500 m on both sides of the equator. Across the cruise transect, dissolved strontium concentrations increase by 2-3% along the thermocline suggesting rapid recycling of strontium rich phases. This is particularly evident just below the thermocline at 8-9°N and below 1000 m water depth, south of the equator. The deep, southern enrichment in strontium does not involve a change in the Sr/Ca ratio, suggesting that this strontium enrichment is related to CaCO3 dissolution. In contrast, in the intermediate waters of the northern part of

  19. Feasibility Study for the Reduction of Perchlorate, Iodide, and Other Aqueous Anions

    National Research Council Canada - National Science Library

    Clewell, Rebecca A; Tsui, David T; Mattie, David R

    1999-01-01

    Cyclic Voltammetry (CV) was used as a technique to determine the feasibility of the use of a coulometric detector in the determination of perchlorate, iodide, and various other anions commonly found in drinking water...

  20. Capture of organic iodides from nuclear waste by metal-organic framework-based molecular traps

    KAUST Repository

    Li, Baiyan; Dong, Xinglong; Wang, Hao; Ma, Dingxuan; Tan, Kui; Jensen, Stephanie; Deibert, Benjamin J.; Butler, Joseph; Cure, Jeremy; Shi, Zhan; Thonhauser, Timo; Chabal, Yves J.; Han, Yu; Li, Jing

    2017-01-01

    capture from nuclear waste. The capture mechanism was investigated by experimental and theoretical methods.Capturing radioactive organic iodides from nuclear waste is important for safe nuclear energy usage, but remains a significant challenge. Here, Li

  1. The iodide sym-porter (NIS): new perspectives in nuclear oncology

    International Nuclear Information System (INIS)

    Pourcher, Th.; Lindenthal, S.; Basquin, C.; Ferhat, O.; Marsault, R.; Carrier, P.; Koulibaly, M.; Bussiere, F.; Darcourt, J.

    2005-01-01

    The sodium iodide sym-porter (NIS) is the plasma membrane protein that mediates uptake of iodide in the thyroid and other organs such as the stomach and the salivary gland. The cloning of its cDNA allows the targeting of NIS expression into any cell using gene therapy. This enables iodide uptake and thus NIS can be used as reporter imaging for live animals. More intriguingly, this new technique has potential using radio-iodide therapy to selectively destroy tumour cells. These two approaches employ common techniques in nuclear medicine. Many experiments on cultured cells and on animals have been carried out; they established clearly the advantages of this genetically targeted radiotherapy. Recent studies employing this therapy on multiple myeloma cell lines implanted in mice or on hepato-carcinoma-bearing rats, resulted in important tumour remission. However, additional studies on NIS regulation and the use of alternative radioisotopes transported by NIS are required to further develop this promising approach. (author)

  2. Functionalized metal organic frameworks for effective capture of radioactive organic iodides

    KAUST Repository

    Li, Baiyan; Dong, Xinglong; Wang, Hao; Ma, Dingxuan; Tan, Kui; Shi, Zhan; Chabal, Yves J.; Han, Yu; Li, Jing

    2017-01-01

    Highly efficient capture of radioactive organic iodides (ROIs) from off-gas mixtures remains a substantial challenge for nuclear waste treatment. Current materials utilized for ROI sequestration suffer from low capacity, high cost (e.g. use of noble

  3. Leaching of iodine from composites based on epoxy resin and lead iodide

    International Nuclear Information System (INIS)

    Kalinin, N.N.; Elizarova, A.N.

    1988-01-01

    The scope for using solid composites obtained by incorporating dry powdery lead iodide and its aqueous suspension into epoxy resin for prolonged immobilization of iodine-129 under monitorable storage conditions has been assessed by a study of leaching of iodine

  4. Removal efficiency of radioactive methyl iodide on TEDA-impregnated activated carbons

    International Nuclear Information System (INIS)

    Gonzalez-Garcia, C.M.; Gonzalez, J.F.; Roman, S.

    2011-01-01

    Activated carbons were prepared by different series of carbon dioxide and steam activation from walnut shells for their optimal use as radioactive methyl iodide adsorbents in Nuclear Plants. The knowledge of the most favourable textural characteristics of the activated carbons was possible by the previous study of the commercial activated carbon currently used for this purpose. In order to increase their methyl iodide affinity, the effect of triethylenediamine impregnation was studied at 5 and 10 wt.%. The results obtained indicated that in both cases the adsorption efficiency is markedly improved by the addition of impregnant, which allows the adsorbate uptake to occur not only by physical adsorption, via non-specific interactions (as in non-impregnated carbons) but also by the specific interaction of triethylenediamine with radioactive methyl iodide. Methyl iodide retention efficiencies up to 98.1% were achieved. (author)

  5. Production of high quality sodium iodide preparations labelled with carrier free iodine-125

    International Nuclear Information System (INIS)

    Abdukayumov, M.N.; Chistyakov, P.G.; Shilin, E.A.

    2001-01-01

    Work is related to the problem of high-quality Sodium Iodide preparation production and to the choice of the peptids iodination methods with the purpose of control test developing to determine the Biological activity of the above mentioned preparation

  6. Kinetics of [123I]iodide uptake and discharge by perchlorate in studies of inhibition of iodide binding by antithyroid drugs

    International Nuclear Information System (INIS)

    McCruden, D.C.; Connell, J.M.C.; Alexander, W.D.; Hilditch, T.E.

    1985-01-01

    Thyroidal binding of iodide was studied by kinetic analysis of [ 123 ]iodide uptake and its discharge by perchlorate in 80 hyperthyroid subjects receiving antithyroid drug therapy. Five dosage regimens ranging from 5 mg carbimazole twice daily to 15 mg methimazole twice daily were studied. Binding inhibition was estimated at 5-7 h after drug as an index of the mean effect of the 12 hourly regimen. In all cases, except one in the lowest dose group, binding was found to be markedly reduced with mean binding rates ranging from 0.002 to 0.020 min -1 (normal > 0.15 min -1 ). The net clearance of iodide in the lowest dose group was reduced to a mean value near the upper limit of the euthyroid range, whereas in the highest dose group it lay at the lower limit of the euthyroid range. These results were reflected in the serum thyroid hormone response. There was a reducing incidence of inadequate control of hyperthyroidism and an increasing incidence of hypothyroidism with increasing thiourylene dose. The exit rate constant of free iodide for the various doses showed values from 0.048 to 0.055 min -1 . Correpsonding mean values for the discharge rate constant after perchlorate were 0.087 to 0.105 min -1 . This suggests that perchlorate increases the rate of iodide release from the thyroid gland. Studies at a later interval after drug (12-14 h) showed no change in discharge rate constant. This leads to the conclusion that perchlorate may further inhibit iodide binding in subjects receiving antithyroid drug therapy. (author)

  7. Method for ion exchange purification of sodium iodide solution from heavy metals and potassium microimpurities

    International Nuclear Information System (INIS)

    Smirnov, G.I.; Kachur, N.Ya.; Kostromina, O.N.; Ogorodnikova, A.A.; Khajnakov, S.A.

    1990-01-01

    A method of deep ion exchange purification of sodium iodide solution from heavy metals (iron, nickel, copper, lead) and potassium microimpurities is developed. The method includes multiple sorption of microimpurities on titanium phosphate with their subsequent desorption by sorbent processing with a solution with a solution of 3-6 N nitric acid, first, and then with a neutral solution of 2 % sodium thiosulfate. The given method permits to increase the purification degree of sodium iodide solution by 25-30 %. 2 tabs

  8. Radiolysis of cesium iodide solutions at 35 and 85 deg C

    International Nuclear Information System (INIS)

    Lucas, M.

    1981-09-01

    An aqueous solution of cesium iodide was irradiated by the gamma rays from a cobalt 60 source with a dose rate of 0.4 Mrad/hr. At 35 deg C the iodide I - is oxidized in molecular iodine I 2 but at 85 deg C the iodate IO 3 - is obtained. The aim of this work is the study of aerosols behaviour released in accidental situation of a PWR in presence of steam [fr

  9. Permeation of iodide from iodine-enriched yeast through porcine intestine.

    Science.gov (United States)

    Ryszka, Florian; Dolińska, Barbara; Zieliński, Michał; Chyra, Dagmara; Dobrzański, Zbigniew

    2013-01-01

    Iodine deficiency is a common phenomenon, threatening the whole global human population. Recommended daily intake of iodine is 150 μg for adults and 250 μg for pregnant and breastfeeding women. About 50% of human population can be at risk of moderate iodine deficiency. Due to this fact, increased iodine supplementation is recommended, through intake of iodized mineral water and salt iodization. The aim of this study was to investigate permeation and absorption of iodide from iodine bioplex (experimental group) in comparison with potassium iodide (controls). Permeation and absorption processes were investigated in vitro using a porcine intestine. The experimental model was based on a standard Franz diffusion cell (FD-Cell). The iodine bioplex was produced using Saccharomyces cerevisiae yeast and whey powder: iodine content - 388 μg/g, total protein - 28.5%, total fat - 0.9%., glutamic acid - 41.2%, asparaginic acid - 29.4%, lysine - 24.8%; purchased from: F.Z.N.P. Biochefa, Sosnowiec, Poland. Potassium iodide was used as controls, at 388 μg iodine concentration, which was the same as in iodine-enriched yeast bioplex. A statistically significant increase in iodide permeation was observed for iodine-enriched yeast bioplex in comparison with controls - potassium iodide. After 5h the total amount of permeated iodide from iodine-enriched yeast bioplex was 85%, which is ~ 2-fold higher than controls - 37%. Iodide absorption was by contrast statistically significantly higher in controls - 7.3%, in comparison with 4.5% in experimental group with iodine-enriched yeast bioplex. Presented results show that iodide permeation process dominates over absorption in case of iodine-enriched yeast bioplex.

  10. Predistribution of potassium iodide--the Tennessee experience

    International Nuclear Information System (INIS)

    Fowinkle, E.W.; Sell, S.H.; Wolle, R.H.

    1983-01-01

    Tennessee public health officials made a decision to predistribute potassium iodide tablets (KI) to householders in the vicinity of a nuclear power plant. The tablets would be stored until needed in the event of a radiation emergency. The officials believed that it was important to have the option available as a means of protecting nearby residents. KI, ingested before or soon after exposure to radioactive iodine, can act as a thyroid blocker to protect the gland from accepting further iodine and, therefore, the radiation. A pilot project was undertaken to deliver, door to door, a package that contained KI tablets in sufficient quantity to supply a starter dose to each member of households within a 5-mile radius of the Sequoyah nuclear power plant near Chattanooga. The package consisted of a vial of 14 130-mg tablets and a package insert from the manufacturer enclosed in a larger vial with a childproof cap. Home visitors who delivered the vials were professionals from the local public health departments, especially trained to answer questions about the project. About 66 percent of 5,591 homes accepted the medication. Extensive coverage of the project by information media was helpful in explaining local emergency plans as well as the KI distribution to the public

  11. Silver iodide sodalite for "1"2"9I immobilisation

    International Nuclear Information System (INIS)

    Vance, E.R.; Gregg, D.J.; Grant, C.; Stopic, A.; Maddrell, E.R.

    2016-01-01

    Silver iodide sodalite was initially synthesised as a fine-grained major phase in a nominally stoichiometric composition following hot isostatic pressing at 850 °C with 100 MPa and its composition, Ag_4Al_3Si_3O_1_2I, was approximately verified by scanning electron microscopy. An alternative preparative method yielded a more dense and stoichiometric AgI sodalite on sintering and HIPing. As found for AgI, the I is released from AgI sodalite much more readily in reducing water than in ordinary water. Thus in normal PCT-B tests, the I release was <0.3 g/L in water, but it was ∼70 g/L under highly reducing conditions. This is an important point with regard to can material if HIPing is used for consolidation. - Highlights: • Dense AgI sodalite has been produced by hot isostatic pressing. • The stoichiometry of AgI sodalite has been confirmed by scanning electron microscopy. • Good I immobilisation in AgI sodalite exposed to water containing Cu or Ni metal powders was determined. • AgI sodalite exposed to water containing Fe powders decomposed and released significant quantities of iodine.

  12. In situ nucleophilic substitutional growth of methylammonium lead iodide polycrystals.

    Energy Technology Data Exchange (ETDEWEB)

    Acik, Muge [Argonne National Lab. (ANL), Argonne, IL (United States). Center for Nanoscale Materials and Nanoscience and Technology Division; Alam, Todd M. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States). Dept. of Organic Materials Science; Guo, Fangmin [Argonne National Lab. (ANL), Argonne, IL (United States). Advanced Photon Source (APS) and X-ray Science Division; Ren, Yang [Argonne National Lab. (ANL), Argonne, IL (United States). Advanced Photon Source (APS) and X-ray Science Division; Lee, Byeongdu [Argonne National Lab. (ANL), Argonne, IL (United States). Advanced Photon Source (APS) and X-ray Science Division; Rosenberg, Richard A. [Argonne National Lab. (ANL), Argonne, IL (United States). Advanced Photon Source (APS) and X-ray Science Division; Mitchell, JF [Argonne National Lab. (ANL), Argonne, IL (United States). Materials Science Division; Kinaci, Alper [Argonne National Lab. (ANL), Argonne, IL (United States). Center for Nanoscale Materials and Nanoscience and Technology Division; Chan, Maria [Argonne National Lab. (ANL), Argonne, IL (United States). Center for Nanoscale Materials and Nanoscience and Technology Division; Darling, Seth B. [Argonne National Lab. (ANL), Argonne, IL (United States). Center for Nanoscale Materials and Nanoscience and Technology Division; Univ. of Chicago, IL (United States). Inst. for Molecular Engineering

    2017-01-01

    Methylammonium lead iodide (MAPbIx) perovskites are organic-inorganic semiconductors that serve as the light-harvesting component of the photovoltaics, and are desirable with their long diffusion length yielding power conversion efficiencies of ≥22%. Conventional techniques grow perovskites by spin coating precursors on an oxide or a polymer substrate followed by annealing, however, use of high boiling point solvents and high temperatures hinder device stability and performance. Through a one-step, acid-catalyzed nucleophilic-substitutional crystal growth in polar protic solvents, we show evidence for the substrate- and annealing- free production of MAPbIx polycrystals that are metallic-lead-free with negligibly small amount of PbI2 precipitation (<10%). On the basis of this chemical composition, we have devised an in situ growth of highly air (upto ~1.5 months) and thermally-stable (≤300°C), tetragonal-phased, variable-sized polycrystals (~100 nm-10 μm) amendable for large-area deposition, and ultimately, large-scale manufacturing. This method is encouraging for stable optoelectronic devices, and leads to energy-efficient and low-cost processing.

  13. Slow hot carrier cooling in cesium lead iodide perovskites

    Science.gov (United States)

    Shen, Qing; Ripolles, Teresa S.; Even, Jacky; Ogomi, Yuhei; Nishinaka, Koji; Izuishi, Takuya; Nakazawa, Naoki; Zhang, Yaohong; Ding, Chao; Liu, Feng; Toyoda, Taro; Yoshino, Kenji; Minemoto, Takashi; Katayama, Kenji; Hayase, Shuzi

    2017-10-01

    Lead halide perovskites are attracting a great deal of interest for optoelectronic applications such as solar cells, LEDs, and lasers because of their unique properties. In solar cells, heat dissipation by hot carriers results in a major energy loss channel responsible for the Shockley-Queisser efficiency limit. Hot carrier solar cells offer the possibility to overcome this limit and achieve energy conversion efficiency as high as 66% by extracting hot carriers. Therefore, fundamental studies on hot carrier relaxation dynamics in lead halide perovskites are important. Here, we elucidated the hot carrier cooling dynamics in all-inorganic cesium lead iodide (CsPbI3) perovskite using transient absorption spectroscopy. We observe that the hot carrier cooling rate in CsPbI3 decreases as the fluence of the pump light increases and the cooling is as slow as a few 10 ps when the photoexcited carrier density is 7 × 1018 cm-3, which is attributed to phonon bottleneck for high photoexcited carrier densities. Our findings suggest that CsPbI3 has a potential for hot carrier solar cell applications.

  14. Kinetics of the thermal decomposition of nickel iodide

    International Nuclear Information System (INIS)

    Nakajima, Hayato; Shimizu, Saburo; Onuki, Kaoru; Ikezoe, Yasumasa; Sato, Shoichi

    1984-01-01

    Thermal decomposition kinetics of NiI 2 under constant I 2 partial pressure was studied by thermogravimetry. The reaction is considered as a reaction step of the thermochemical hydrogen production process in the Ni-I-S system. At temperatures from 775K to 869K and under I 2 pressures from 0 to 960Pa, the decomposition started at the NiI 2 pellet surface and the reactant-product interface moved interior at a constant rate until the decomposed fraction, α, reached 0.6. The overall reaction rate at a constant temperature can be expressed as the difference of the constant decomposition (forward) rate, which is proportional to the equilibrium dissociation pressure of NiI 2 , and the iodide formation (backward) rate, which is proportional to the I 2 pressure. The apparent activation energy of the decomposition was 147 kJ.mol -1 , which is very close to the heat of reaction, 152 kJ.mol -1 calculated from the equilibrium dissociation pressure. The electron microscopic observations, revealed that the reaction product obtained by decomposing NiI 2 under pure He atomosphere was composed of relatively well grown cubic Ni crystals. Whereas, the decomposed product obtained under I 2 -He mixture was composed of larger but disordered crystals. (author)

  15. Persistent photovoltage in methylammonium lead iodide perovskite solar cells

    Directory of Open Access Journals (Sweden)

    A. Baumann

    2014-08-01

    Full Text Available We herein perform open circuit voltage decay (OCVD measurements on methylammonium lead iodide (CH3NH3PbI3 perovskite solar cells to increase the understanding of the charge carrier recombination dynamics in this emerging technology. Optically pulsed OCVD measurements are conducted on CH3NH3PbI3 solar cells and compared to results from another type of thin-film photovoltaics, namely, the two reference polymer–fullerene bulk heterojunction solar cell devices based on P3HT:PC60BM and PTB7:PC70BM blends. We observe two very different time domains of the voltage transient in the perovskite solar cell with a first drop on a short time scale that is similar to the decay in the studied organic solar cells. However, 65%–70% of the maximum photovoltage persists on much longer timescales in the perovskite solar cell than in the organic devices. In addition, we find that the recombination dynamics in all time regimes are dependent on the starting illumination intensity, which is also not observed in the organic devices. We then discuss the potential origins of these unique behaviors.

  16. Radiation damage resistance in mercuric iodide X-ray detectors

    Energy Technology Data Exchange (ETDEWEB)

    Patt, B E; Dolin, R C; Devore, T M; Markakis, J M [EG and G Energy Measurements, Inc., Goleta, CA (USA); Iwanczyk, J S; Dorri, N [Xsirius, Inc., Marina del Rey, CA (USA); Trombka, J [National Aeronautics and Space Administration, Greenbelt, MD (USA). Goddard Space Flight Center

    1990-12-20

    Mercuric iodide (HgI{sub 2}) radiation detectors show great potential as ambient-temperature solid-state detectors for X-rays, gamma rays and visible light, with parameters that are competitive with existing technologies. In a previous experiment, HgI{sub 2} detectors irradiated with 10 MeV protons/cm{sup 2} exhibited no damage. The 10 MeV protons represent only the low range of the spectrum of energies that are important. An experiment has been conducted at the Saturne accelerator facility at Saclay, France, to determine the susceptibility of these detectors to radiation damage by high-energy (1.5 GeV) protons. The detectors were irradiated to a fluence of 10{sup 8} protons/cm{sup 2}. This fluence is equivalent to the cosmic radiation expected in a one-year period in space. The resolution of the detectors was measured as a function of the integral dose. No degradation in the response of any of the detectors or spectrometers was seen. It is clear from this data that HgI{sub 2} has extremely high radiation-damage resistance, exceeding that of most other semiconductor materials used for radiation detectors. Based on the results shown to date, HgI{sub 2} detectors are suitable for applications in which they may be exposed to high integral dose levels. (orig.).

  17. A selective iodide ion sensor electrode based on functionalized ZnO nanotubes.

    Science.gov (United States)

    Ibupoto, Zafar Hussain; Khun, Kimleang; Willander, Magnus

    2013-02-04

    In this research work, ZnO nanotubes were fabricated on a gold coated glass substrate through chemical etching by the aqueous chemical growth method. For the first time a nanostructure-based iodide ion selective electrode was developed. The ZnO nanotubes were functionalized with miconazole ion exchanger and the electromotive force (EMF) was measured by the potentiometric method. The iodide ion sensor exhibited a linear response over a wide range of concentrations (1 × 10-6 to 1 × 10-1 M) and excellent sensitivity of -62 ± 1 mV/decade. The detection limit of the proposed sensor was found to be 5 × 10-7 M. The effects of pH, temperature, additive, plasticizer and stabilizer on the potential response of iodide ion selective electrode were also studied. The proposed iodide ion sensor demonstrated a fast response time of less than 5 s and high selectivity against common organic and the inorganic anions. All the obtained results revealed that the iodide ion sensor based on functionalized ZnO nanotubes may be used for the detection of iodide ion in environmental water samples, pharmaceutical products and other real samples.

  18. A Selective Iodide Ion Sensor Electrode Based on Functionalized ZnO Nanotubes

    Directory of Open Access Journals (Sweden)

    Magnus Willander

    2013-02-01

    Full Text Available In this research work, ZnO nanotubes were fabricated on a gold coated glass substrate through chemical etching by the aqueous chemical growth method. For the first time a nanostructure-based iodide ion selective electrode was developed. The ZnO nanotubes were functionalized with miconazole ion exchanger and the electromotive force (EMF was measured by the potentiometric method. The iodide ion sensor exhibited a linear response over a wide range of concentrations (1 × 10−6 to 1 × 10−1 M and excellent sensitivity of –62 ± 1 mV/decade. The detection limit of the proposed sensor was found to be 5 × 10−7 M. The effects of pH, temperature, additive, plasticizer and stabilizer on the potential response of iodide ion selective electrode were also studied. The proposed iodide ion sensor demonstrated a fast response time of less than 5 s and high selectivity against common organic and the inorganic anions. All the obtained results revealed that the iodide ion sensor based on functionalized ZnO nanotubes may be used for the detection of iodide ion in environmental water samples, pharmaceutical products and other real samples.

  19. Studies of selected transuranium and lanthanide tri-iodides under pressure using absorption spectrophotometry

    International Nuclear Information System (INIS)

    Haire, R.G.; Young, J.P.; Peterson, J.R.; Tennessee Univ., Knoxville; Benedict, U.

    1987-01-01

    The anhydrous tri-iodides of plutonium, americium and curium under pressure have been investigated using absorption spectrophotometry. These initial studies on plutonium and curium tri-iodides together with the published data for americium tri-iodide show that the rhombohedral form of these compounds (BiI 3 -type structure) can be converted to the orthorhombic form (PuBr 3 -type structure) by applying pressure at room temperature. Absorption spectrophotometry can often differentiate between two crystallographic forms of a material and has been used in the present high-pressure studies to monitor the effects of pressure on the tri-iodides. A complication in these studies of the tri-iodides is a significant shift of their absorption edges with pressure from the near UV to the visible spectral region. With curium tri-iodide this shift causes interference with the major f-f absorption peaks and precludes identification by absorption spectrophotometry of the high pressure phase of CmI 3 . (orig.)

  20. Mechanistic aspects of ingested chlorine dioxide on thyroid function: impact of oxidants on iodide metabolism

    International Nuclear Information System (INIS)

    Bercz, J.P.; Jones, L.L.; Harrington, R.M.; Bawa, R.; Condie, L.

    1986-01-01

    Toxicological studies dealing with recent findings of health effects of drinking water disinfectants are reviewed. Experiments with monkeys and rodents indicate that the biological activity of ingested disinfectants is expressed via their chemical interaction with the mucosal epithelia, secretory products, and nutritional contents of the alimentary tract. Evidence exists that a principal partner of this redox interaction is the iodide of nutritional origin that is ubiquitous in the gastrointestinal tract. Thus the observation that subchronic exposure to chlorine dioxide (ClO 2 ) in drinking water decreases serum thyroxine levels in mammalian species can be best explained with changes produced in the chemical form of the bioavailable iodide. Ongoing and previously reported mechanistic studies indicate that oxidizing agents such as chlorine-based disinfectants oxidize the basal iodide content of the gastrointestinal tract. The resulting reactive iodine species readily attaches to organic matter by covalent bonding. Evidence suggests that the extent to which such iodinated organics are formed is proportional to the magnitude of the electromotive force and stoichiometry of the redox couple between iodide and the disinfectant. Because the extent of thyroid uptake of the bioavailable iodide does not decrease during ClO 2 ingestion, it seems that ClO 2 does not cause iodide deficiency of sufficient magnitude to account for the decease in hormonogenesis. Absorption of one or more of iodinated molecules, e.g., nutrient, hormones, or cellular constituents of the alimentary tract having thyromimetic or thyroid inhibitory properties, is a better hypothesis for the effects seen

  1. Modelling iodide – iodate speciation in atmospheric aerosol: Contributions of inorganic and organic iodine chemistry

    Directory of Open Access Journals (Sweden)

    S. Pechtl

    2007-01-01

    Full Text Available The speciation of iodine in atmospheric aerosol is currently poorly understood. Models predict negligible iodide concentrations but accumulation of iodate in aerosol, both of which is not confirmed by recent measurements. We present an updated aqueous phase iodine chemistry scheme for use in atmospheric chemistry models and discuss sensitivity studies with the marine boundary layer model MISTRA. These studies show that iodate can be reduced in acidic aerosol by inorganic reactions, i.e., iodate does not necessarily accumulate in particles. Furthermore, the transformation of particulate iodide to volatile iodine species likely has been overestimated in previous model studies due to negligence of collision-induced upper limits for the reaction rates. However, inorganic reaction cycles still do not seem to be sufficient to reproduce the observed range of iodide – iodate speciation in atmospheric aerosol. Therefore, we also investigate the effects of the recently suggested reaction of HOI with dissolved organic matter to produce iodide. If this reaction is fast enough to compete with the inorganic mechanism, it would not only directly lead to enhanced iodide concentrations but, indirectly via speed-up of the inorganic iodate reduction cycles, also to a decrease in iodate concentrations. Hence, according to our model studies, organic iodine chemistry, combined with inorganic reaction cycles, is able to reproduce observations. The presented chemistry cycles are highly dependent on pH and thus offer an explanation for the large observed variability of the iodide – iodate speciation in atmospheric aerosol.

  2. Lead iodide X-ray and gamma-ray spectrometers for room and high temperature operation

    International Nuclear Information System (INIS)

    Hermon, H.; James, R.B.; Lund, J.

    1998-01-01

    In this study the authors report on the results of the investigation of lead iodide material properties. The effectiveness of a zone refining purification method on the material purity is determined by ICP-MS and ICP-OES and correlated to the electrical and physical material properties. They show that this zone refining method is very efficient in removing impurities from lead iodide, and they also determine the segregation coefficient for some of these impurities. Triple axis X-ray diffraction (TAD) analysis has been used to determine the crystalline perfection of the lead iodide after applying various cutting, etching and fabrication methods. The soft lead iodide crystal was found to be damaged when cleaved by a razor blade, but by using a diamond wheel saw, followed by etching, the crystallinity of the material was much improved, as observed by TAD. Low temperature photoluminescence also indicates an improvement in the material properties of the purified lead iodide. Electrical properties of lead iodide such as carrier mobility, were calculated based on carrier-phonon scattering. The results for the electrical properties were in good agreement with the experimental data

  3. Optical lattice clock with Strontium atoms; Horloge a reseau optique a atomes de strontium

    Energy Technology Data Exchange (ETDEWEB)

    Baillard, X

    2008-01-15

    This thesis presents the latest achievements regarding the optical lattice clock with Strontium atoms developed at LNE-SYRTE. After a review of the different types of optical clocks that are currently under development, we stress on the concept of optical lattice clock which was first imagined for Sr{sup 87} using the {sup 1}S{sub 0} {yields} {sup 3}P{sub 0} transition. We exhibit the features of this atom, in particular the concept of magic wavelength for the trap, and the achievable performances for this kind of clock. The second part presents the experimental aspects, insisting particularly on the ultra-stable laser used for the interrogation of the atoms which is a central part of the experiment. Among the latest improvements, an optical pumping phase and an interrogation phase using a magnetic field have been added in order to refine the evaluation of the Zeeman effect. Finally, the last part presents the experimental results. The last evaluation of the clock using Sr{sup 87} atoms allowed us to reach a frequency accuracy of 2.6*10{sup -15} and a measurement in agreement with the one made at JILA (Tokyo university) at the 10{sup -15} level. On another hand, thanks to recent theoretical proposals, we made a measurement using the bosonic isotope Sr{sup 88} by adapting the experimental setup. This measurement represents the first evaluation for this type of clock, with a frequency accuracy of 7*10{sup -14}. (author)

  4. Strontium isotope geochemistry of soil and playa deposits near Yucca Mountain, Nevada

    International Nuclear Information System (INIS)

    Marshall, B.D.; Mahan, S.A.

    1994-01-01

    The isotopic composition of strontium contained in the carbonate fractions of soils provides an excellent tracer which can be used to test models for their origin. This paper reports data on surface coatings and cements, eolian sediments, playas and alluvial fan soils which help to constrain a model for formation of the extensive calcretes and fault infillings in the Yucca Mountain region. The playas contain carbonate with a wide range of strontium compositions; further work will be required to fully understand their possible contributions to the pedogenic carbonate system. Soils from an alluvial fan to the west of Yucca Mountain show that only small amounts of strontium are derived from a fan draining a carbonate terrane have strontium component. Although much evidence points to an eolian source for at least some of the strontium in the pedogenic carbonates near Yucca Mountain, an additional component or past variation of strontium composition in the eolian source is required to model the pedogenic carbonate system

  5. A facile one-pot hydrothermal method to prepare europium-doped titania hollow phosphors and their sensitized luminescence properties

    Energy Technology Data Exchange (ETDEWEB)

    Feng Xuan; Yang Ling; Zhang Nianchun [Department of Chemistry and Institute of Nanochemistry, Jinan University, 601 Western Huangpu Road, Guangzhou 510632 (China); Liu Yingliang, E-mail: tliuyl@jnu.edu.c [Department of Chemistry and Institute of Nanochemistry, Jinan University, 601 Western Huangpu Road, Guangzhou 510632 (China)

    2010-09-17

    Research highlights: {yields} The strongest emission intensity was observed with TiO{sub 2}:Eu{sub 0.2} hollow spheres and TiO{sub 2}:Eu{sub 0.2} hollow spheres calcining at 550 {sup o}C. Moreover, the strongest excitation of TiO{sub 2}:Eu{sub 0.2} hollow spheres transferred from 400 to 500 {sup o}C and the effective nonradiative energy transfer from the TiO{sub 2} hollow spheres host matrix to Eu{sup 3+} ions crystal field states was realized due to changes of crystalline field in the environment around Eu{sup 3+} ions occupying Ti{sup 4+} sites. The proposed energy transfer mechanism was that UV light is absorbed in the band of TiO{sub 2} hollow spheres crystal and then the energy is relaxed to the defect states of TiO{sub 2} host. The energy can transfer to the crystal states of Eu{sup 3+} ions ({sup 7}F{sub j}, j = 0, 1, 2, 3 and 4), which results in efficient photoluminescence. The fluorescent intensity of TiO{sub 2}:Eu{sub 0.2} hollow spheres was 2.2 times as strong as that of TiO{sub 2}:Eu{sub 0.2} bulk material. - Abstract: Monodisperse europium-activated titania hollow phosphors had been synthesized by a facile one-pot hydrothermal method using carbon spheres as hard templates. Samples were characterized by X-ray powder diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy, energy dispersive spectrometer and photoluminescence spectrum. The strongest emission intensity was observed with TiO{sub 2}:Eu{sub 0.2} hollow spheres and TiO{sub 2}:Eu{sub 0.2} hollow spheres calcining at 550 {sup o}C. Moreover, the strongest excitation of TiO{sub 2}:Eu{sub 0.2} hollow spheres transferred from 400 to 500 {sup o}C and the effective nonradiative energy transfer from the TiO{sub 2} hollow spheres host matrix to Eu{sup 3+} ions crystal field states was realized due to changes of crystalline field in the environment around Eu{sup 3+} ions occupying Ti{sup 4+} sites. The proposed energy transfer mechanism was that UV light is absorbed in the band of TiO{sub 2} hollow spheres crystal and then the energy is relaxed to the defect states of TiO{sub 2} host. The energy can transfer to the crystal states of Eu{sup 3+} ions ({sup 7}F{sub j}, j = 0, 1, 2, 3 and 4), which results in efficient photoluminescence. The fluorescent intensity of TiO{sub 2}:Eu{sub 0.2} hollow spheres was 2.2 times as strong as that of TiO{sub 2}:Eu{sub 0.2} bulk material.

  6. TH-C-19A-12: Two-Dimensional High Spatial-Resolution Dosimeter Using Europium Doped Potassium Chloride

    International Nuclear Information System (INIS)

    Li, H; Yang, D; Xiao, Z; Driewer, J; Han, Z; Low, D

    2014-01-01

    Purpose: Recent research has shown that KCl:Eu2+ has great potential for use in megavoltage radiation therapy dosimetry because this material exhibits excellent storage performance and is reusable due to strong radiation hardness. This work reports our attempts to fabricate 2D KCl:Eu2+ storage phosphor films (SPFs) using both a physical vapor deposition (PVD) method and a tape casting method. Methods: A thin layer of KCl:Eu2+ was deposited on a substrate of borosilicate glass (e.g., laboratory slides) with a PVD system. For tape casting, a homogenous suspension containing storage phosphor particles, liquid vehicle and polymer binder was formed and subsequently cast by doctor-blade onto a polyethylene terephthalate substrate to form a 150 μm thick SPF. Results: X ray diffraction analysis showed that a 10 μm thick PVD sample was composed of highly crystalline KCl. No additional phases were observed, suggesting that the europium activator had completed been incorporated into the KCl matrix. Photostimulated luminescence and photoluminescence spectra suggested that F (Cl−) centers were the electron storage centers post x ray irradiation and that Eu2+ cations acted as luminescence centers in the photostimulation process. The 150 μm thick casted KCl:Eu2+ SPF showed sub-millimeter spatial resolution. Monte Carlo simulations further demonstrated that the admixture of 20% KCl:Eu2+ and 80% low Z polymer binder exhibited almost no energy dependence in a 6 MV beam. KCl:Eu2+ pellet samples showed a large dynamic range from 0.01 cGy to 60 Gy dose-to-water, and saturated at approximately 500 Gy as a Result of its intrinsic high radiation hardness. Conclusions: This discovery research provides strong evidence that KCl:Eu2+ based SPF with associated readout apparatus could Result in a novel electronic film system that has all the desirable features associated with classic radiographic film and, importantly, water equivalence and the capability of permanent identification of each detector. This work was supported in part by NIH Grant No. R01CA148853. The authors would like to thank Paul Leblans (AGFA Healthcare, Belgium) for many helpful discussions on this topic

  7. Simple preparation of fluorescent composite films based on cerium and europium doped LaF3 nanoparticles

    Science.gov (United States)

    Secco, Henrique de L.; Ferreira, Fabio F.; Péres, Laura O.

    2018-03-01

    The combination of materials to form hybrids with unique properties, different from those of the isolated components, is a strategy used to prepare functional materials with improved properties aiming to allow their application in specific fields. The doping of lanthanum fluoride with other rare earth elements is used to obtain luminescent particles, which may be useful to the manufacturing of electronic devices' displays and biological markers, for instance. The application of the powder of nanoparticles has limitations in some fields; to overcome this, the powder may be incorporated in a suitable polymeric matrix. In this work, lanthanum fluoride nanoparticles, undoped and doped with cerium and europium, were synthesized through the co-precipitation method in aqueous solution. Aiming the formation of solid state films, composites of nanoparticles in an elastomeric matrix, the nitrile rubber (NBR), were prepared. The flexibility and the transparency of the matrix in the regions of interest are advantages for the application of the luminescent composites. The composites were applied as films using the casting and the spin coating techniques and luminescent materials were obtained in the samples doped with europium and cerium. Scanning electron microscopy images showed an adequate dispersion of the particles in the matrix in both film formation techniques. Aggregates of the particles were detected in the samples which may affect the uniformity of the emission of the composites.

  8. Gamma ray spectroscopy employing divalent europium-doped alkaline earth halides and digital readout for accurate histogramming

    Science.gov (United States)

    Cherepy, Nerine Jane; Payne, Stephen Anthony; Drury, Owen B.; Sturm, Benjamin W.

    2016-02-09

    According to one embodiment, a scintillator radiation detector system includes a scintillator, and a processing device for processing pulse traces corresponding to light pulses from the scintillator, where the processing device is configured to: process each pulse trace over at least two temporal windows and to use pulse digitization to improve energy resolution of the system. According to another embodiment, a scintillator radiation detector system includes a processing device configured to: fit digitized scintillation waveforms to an algorithm, perform a direct integration of fit parameters, process multiple integration windows for each digitized scintillation waveform to determine a correction factor, and apply the correction factor to each digitized scintillation waveform.

  9. Advances in the synthesis of new Europium doped CaSO4 phosphors and their thermoluminescence characterization

    International Nuclear Information System (INIS)

    Bernal, R.; Garcia-Haro, A.R.; Machi, L.; Brown, F.; Perez-Salas, R.; Castano, V.M.; Cruz-Vazquez, C.

    2008-01-01

    Novel self-agglomerating Eu doped CaSO 4 phosphors were synthesized by a cheap, easy, and environmental friendly chemical route. Pellet-shaped sintered samples were obtained without any binding material, and exposed to beta particle irradiation. The thermoluminescence (TL) response in the 0.08-2.6 Gy dose range increased linearly as the radiation dose increased. Glow curves exhibit the most intense maximum close to 200 deg. C, and two much less intense maxima at 250 and 330 deg. C when a 5 deg. C/s heating rate is used. No TL peaks shift is observed when dose changes, which is characteristic of first order kinetics TL processes. The whole glow curve displays a remarkable stability under storage at room temperature. The main peak intensity is 2.5 times greater than that of the TLD-100. The method here reported can be used to synthesize CaSO 4 with other dopants

  10. Photovoltaic Performance Enhancement of Silicon Solar Cells Based on Combined Ratios of Three Species of Europium-Doped Phosphors

    Directory of Open Access Journals (Sweden)

    Wen-Jeng Ho

    2018-05-01

    Full Text Available This paper presents a scheme for the enhancement of silicon solar cells in terms of luminescent emission band and photovoltaic performance. The proposed devices are coated with an luminescent down-shifting (LDS layer comprising three species of europium (Eu-doped phosphors mixed within a silicate film (SiO2 using a spin-on film deposition. The three species of phosphor were mixed at ratios of 0.5:1:1.5, 1:1:1, or 1.5:1:0.5 in weight percentage (wt %. The total quantity of Eu-doped phosphors in the silicate solution was fixed at 3 wt %. The emission wavelengths of the Eu-doped phosphors were as follows: 518 nm (specie-A, 551 nm (specie-B, and 609 nm (specie-C. We examined the extended luminescent emission bands via photoluminescence measurements at room temperature. Closely matching the luminescent emission band to the high responsivity band of the silicon semiconductor resulted in good photovoltaic performance. Impressive improvements in efficiency were observed in all three samples: 0.5:1:1.5 (20.43%, 1:1:1 (19.67%, 1.5:1:0.5 (16.81%, compared to the control with a layer of pure SiO2 (13.80%.

  11. Gamma ray spectroscopy employing divalent europium-doped alkaline earth halides and digital readout for accurate histogramming

    Science.gov (United States)

    Cherepy, Nerine Jane; Payne, Stephen Anthony; Drury, Owen B; Sturm, Benjamin W

    2014-11-11

    A scintillator radiation detector system according to one embodiment includes a scintillator; and a processing device for processing pulse traces corresponding to light pulses from the scintillator, wherein pulse digitization is used to improve energy resolution of the system. A scintillator radiation detector system according to another embodiment includes a processing device for fitting digitized scintillation waveforms to an algorithm based on identifying rise and decay times and performing a direct integration of fit parameters. A method according to yet another embodiment includes processing pulse traces corresponding to light pulses from a scintillator, wherein pulse digitization is used to improve energy resolution of the system. A method in a further embodiment includes fitting digitized scintillation waveforms to an algorithm based on identifying rise and decay times; and performing a direct integration of fit parameters. Additional systems and methods are also presented.

  12. Photovoltaic Performance Enhancement of Silicon Solar Cells Based on Combined Ratios of Three Species of Europium-Doped Phosphors.

    Science.gov (United States)

    Ho, Wen-Jeng; You, Bang-Jin; Liu, Jheng-Jie; Bai, Wen-Bin; Syu, Hong-Jhang; Lin, Ching-Fuh

    2018-05-18

    This paper presents a scheme for the enhancement of silicon solar cells in terms of luminescent emission band and photovoltaic performance. The proposed devices are coated with an luminescent down-shifting (LDS) layer comprising three species of europium (Eu)-doped phosphors mixed within a silicate film (SiO₂) using a spin-on film deposition. The three species of phosphor were mixed at ratios of 0.5:1:1.5, 1:1:1, or 1.5:1:0.5 in weight percentage (wt %). The total quantity of Eu-doped phosphors in the silicate solution was fixed at 3 wt %. The emission wavelengths of the Eu-doped phosphors were as follows: 518 nm (specie-A), 551 nm (specie-B), and 609 nm (specie-C). We examined the extended luminescent emission bands via photoluminescence measurements at room temperature. Closely matching the luminescent emission band to the high responsivity band of the silicon semiconductor resulted in good photovoltaic performance. Impressive improvements in efficiency were observed in all three samples: 0.5:1:1.5 (20.43%), 1:1:1 (19.67%), 1.5:1:0.5 (16.81%), compared to the control with a layer of pure SiO₂ (13.80%).

  13. TH-C-19A-12: Two-Dimensional High Spatial-Resolution Dosimeter Using Europium Doped Potassium Chloride

    Energy Technology Data Exchange (ETDEWEB)

    Li, H; Yang, D; Xiao, Z [Washington University School of Medicine, St. Louis, MO (United States); Driewer, J [University of Nebraska Medical Center, Omaha, NE (United States); Han, Z [Brigham and Womens Hospital and Harvard Medical School, Boston, MA (United States); Low, D [UCLA, Los Angeles, CA (United States)

    2014-06-15

    Purpose: Recent research has shown that KCl:Eu2+ has great potential for use in megavoltage radiation therapy dosimetry because this material exhibits excellent storage performance and is reusable due to strong radiation hardness. This work reports our attempts to fabricate 2D KCl:Eu2+ storage phosphor films (SPFs) using both a physical vapor deposition (PVD) method and a tape casting method. Methods: A thin layer of KCl:Eu2+ was deposited on a substrate of borosilicate glass (e.g., laboratory slides) with a PVD system. For tape casting, a homogenous suspension containing storage phosphor particles, liquid vehicle and polymer binder was formed and subsequently cast by doctor-blade onto a polyethylene terephthalate substrate to form a 150 μm thick SPF. Results: X ray diffraction analysis showed that a 10 μm thick PVD sample was composed of highly crystalline KCl. No additional phases were observed, suggesting that the europium activator had completed been incorporated into the KCl matrix. Photostimulated luminescence and photoluminescence spectra suggested that F (Cl−) centers were the electron storage centers post x ray irradiation and that Eu2+ cations acted as luminescence centers in the photostimulation process. The 150 μm thick casted KCl:Eu2+ SPF showed sub-millimeter spatial resolution. Monte Carlo simulations further demonstrated that the admixture of 20% KCl:Eu2+ and 80% low Z polymer binder exhibited almost no energy dependence in a 6 MV beam. KCl:Eu2+ pellet samples showed a large dynamic range from 0.01 cGy to 60 Gy dose-to-water, and saturated at approximately 500 Gy as a Result of its intrinsic high radiation hardness. Conclusions: This discovery research provides strong evidence that KCl:Eu2+ based SPF with associated readout apparatus could Result in a novel electronic film system that has all the desirable features associated with classic radiographic film and, importantly, water equivalence and the capability of permanent identification of each detector. This work was supported in part by NIH Grant No. R01CA148853. The authors would like to thank Paul Leblans (AGFA Healthcare, Belgium) for many helpful discussions on this topic.

  14. Distribution of strontium in DB18K6 and DTBDB18K6 systems

    International Nuclear Information System (INIS)

    Usarov, Z.O.; Khujaev, S.

    2007-01-01

    Distributions of strontium in DB18K6 and DTBDB18K6 crown-ethers in chloroform were investigated for extraction of strontium from water solutions of nitric acid. Nitrate solutions with various pH were considered. In both crown-ethers the most extraction of strontium was observed for the moderate pH values. Equilibrium of extraction process is reached for comparatively short time and is occurred to be 20 min (authors)

  15. An optimization on strontium separation model for fission products (inactive trace elements) using artificial neural networks

    International Nuclear Information System (INIS)

    Moosavi, K.; Setayeshi, S.; Maragheh, M.Gh.; Ahmadi, S.J.; Kardan, M.R.; Banaem, L.M.

    2009-01-01

    In this study, an experimental design using artificial neural networks for an optimization on the strontium separation model for fission products (inactive trace elements) is investigated. The goal is to optimize the separation parameters to achieve maximum amount of strontium that is separated from the fission products. The result of the optimization method causes a proper purity of Strontium-89 that was separated from the fission products. It is also shown that ANN may be establish a method to optimize the separation model.

  16. Investigation of the elution by seawater of caesium and strontium from loaded clinoptilolite

    International Nuclear Information System (INIS)

    Harder, B.R.; Mitchell, I.H.; Smyth, M.J.

    1985-07-01

    Simple investigations of the elution of caesium and strontium from loaded clinoptilolite are described. The clinoptilolite was loaded to levels expected in the British Nuclear Fuels plc SIXEP plant and contacted with seawater at approx. 15 C. (The elution time was measured until about 99% of the caesium and strontium had been eluted.) It was found that 99% of the caesium was eluted in 35 hours but the strontium (with more variable results) took at least 400 hours for 99% elution. (author)

  17. Migration Behaviour of Strontium in Czech Bentonite Clay

    Directory of Open Access Journals (Sweden)

    Lucie Baborova

    2016-09-01

    Full Text Available The study deals with sorption and diffusion behaviour of strontium in Czech bentonite B75. The study is a part of a research on reactive transport of radioactive contaminants in barrier materials of a deep geological repository of radioactive waste in the Czech Republic. Series of sorption and diffusion experiments with Sr and non-activated Ca bentonite B75 produced in the Czech Republic were performed in two background solutions (CaCl2 and NaCl. On the basis of sorption batch experiments the kinetics of strontium sorption on bentonite was assessed and the sorption isotherms for various experimental conditions were obtained. As a result of performed diffusion experiments the parameters of diffusion (i.e. effective diffusion coefficient De and apparent diffusion coefficient Da were determined. The observed discrepancies between sorption characteristics obtained from the sorption and diffusion experiments are discussed.

  18. Strontium isotopic geochemistry of intrusive rocks, Puerto Rico, Greater Antilles

    International Nuclear Information System (INIS)

    Jones, L.M.; Kesler, S.E.

    1980-01-01

    The strontium isotope geochemistry is given for three Puerto Rican intrusive rocks: the granodioritic Morovis and San Lorenzo plutons and the Rio Blanco stock of quartz dioritic composition. The average calculated initial 87 Sr/ 86 Sr ratios are 0.70370, 0.70355 and 0.70408, respectively. In addition, the San Lorenzo data establish a whole-rock isochron of 71 +- 2 m.y., which agrees with the previously reported K-Ar age of 73 m.y. Similarity of most of the intrusive rocks in the Greater Antilles with respect to their strontium isotopic geochemistry regardless of their major element composition indicates that intrusive magmas with a wide range of composition can be derived from a single source material. The most likely source material, in view of the available isotopic data, is the mantle wedge overlying the subduction zone. (orig.)

  19. Strontium-90 and cesium-137 in service water

    International Nuclear Information System (INIS)

    1979-01-01

    Prefectural public health laboratories and institutes and Japan Chemical Analysis Center have analysed the contents of strontium-90 and cesium-137 in service water under the commission of Science and Technology Agency. At each prefectural public health laboratories and institutes, 100 literes of service water (8 prefectures, water from the intake of each station of water works) and tap water (32 prefectures) were collected as sample twice a year. The samples were filtrated with large filter papers after addition and mixture of both some carries. The filtration was then applied on a column filled the sodium cation exchange resin, and all the cations were absorbed on it. These resin and filter papers were collected at Japan Chemical Analysis Center. At Japan Chemical Analysis Center, these collected samples were radiochemically analysed for strontium-90 and cesium-137 using the method applied for the analysis of rain and dry fallout materials. (author)

  20. Determination of lithium, rubidium and strontium in foodstuffs

    International Nuclear Information System (INIS)

    Evans, W.H.; Read, J.I.

    1985-01-01

    For the determination of total lithium, rubidium and strontium in foodstuffs the organic matter is destroyed by a wet-oxidation procedure. Both lithium and rubidium are measured by flame atomic-emission spectrophotometry, rubidium with the addition of a radiation buffer and strontium is measured by flame atomic-absorption spectrophotometry using the same radiation buffer. The optimum conditions for measurement are described and interferences noted. The accuracy of the method was assessed by measuring the recovery of these metals from foodstuff homogenates and values for standard reference materials are listed, for comparison with certified levels where these exist. From the results obtained standard deviations were calculated and derived limits of detection and confidence intervals are given. (author)

  1. Strontium-90 and cesium-137 in total diet

    International Nuclear Information System (INIS)

    1977-01-01

    Under the commission of Science and Technology Agency, Japan Chemical Analysis Center has analysed total diet samples collected from 30 prefectures (2 times per year), and determined to content of strontium-90 and cesium-137 in these samples. Each Prefectural public health laboratories and institutes have collected all the daily regular diet consumed for five persons, namely three meals and other eating between meals, for radiochemical analysis in polyethylene containers. These samples were collected to Japan Chemical Analysis Center after carbonization without smoke rising in the large stainless dish. At Japan Chemical Analysis Center, these samples were asked in an electric muffle furnance. And the ask to which both some carriers and hydrochloric acid were added, was destroyed under heating. The nuclides were dissolved into hydrochloric acid and filtrated, after it was added with nitric acid and heated to dryness. The filtrates was analysed for strontium-90 and cesium-137 using the method recommended by Science and Technology Agency. (author)

  2. Hydrogen iodide processing section in a thermochemical water-splitting iodine-sulfur process using a multistage hydrogen iodide decomposer

    International Nuclear Information System (INIS)

    Ohashi, Hirofumi; Sakaba, Nariaki; Imai, Yoshiyuki; Kubo, Shinji; Sato, Hiroyuki; Tachibana, Yukio; Kunitomi, Kazuhiko; Kato, Ryoma

    2009-01-01

    A multistage hydrogen iodide (HI) decomposer (repetition of HI decomposition reaction and removal of product iodine by a HIx solution) in a thermochemical water-splitting iodine-sulfur process for hydrogen production using high-temperature heat from the high-temperature gas-cooled reactor was numerically evaluated, especially in terms of the flow rate of undecomposed HI and product iodine at the outlet of the decomposer, in order to reduce the total heat transfer area of heat exchangers for the recycle of undecomposed HI and to eliminate components for the separation. A suitable configuration of the multistage HI decomposer was countercurrent rather than concurrent, and the HIx solution from an electro-electro dialysis at a low temperature was a favorable feed condition for the multistage HI decomposer. The flow rate of undecomposed HI and product iodine at the outlet of the multistage HI decomposer was significantly lower than that of the conventional HI decomposer, because the conversion was increased, and HI and iodine were removed by the HIx solution. Based on this result, an alternative HI processing section using the multistage HI decomposer and eliminating some recuperators, coolers, and components for the separation was proposed and evaluated. The total heat transfer area of heat exchangers in the proposed HI processing section could be reduced to less than about 1/2 that in the conventional HI processing section. (author)

  3. Sea water strontium isotopes, acid rain, and the cretaceous-tertiary boundary

    International Nuclear Information System (INIS)

    MacDougall, J.D.

    1988-01-01

    A large bolide impact at the end of the Cretaceous would have produced significant amounts of nitrogen oxides by shock heating of the atmosphere. The resulting acid precipitation would have increased continental weathering greatly and could be an explanation for the observed high ratio of strontium-87 to strontium-86 in sea water at about this time, due to the dissolution of large amounts of strontium from the continental crust. Spikes to high values in the sea water strontium isotope record at other times may reflect similar episodes. 17 references, 1 figure, 1 table

  4. [Effects of strontium in drinking water on the growth of school-age children].

    Science.gov (United States)

    Tao, Y; Cao, S; Xu, F; Li, J

    1999-09-30

    An epidemiological study on the effect of strontium in drinking water on body shape development, bone age, prevalence of caries and dental fluorosis was carried out. The results show: there is a certain promotion on the development of bone age of school-age children, especially of girls, and there is no obvious impact on body shape developing when the concentration of strontium in drinking water is only 10 mg/L. The correlation between strontium in drinking water and the prevalence of caries in children could not get a conclusive evidence in this paper. A further epidemiological investigation is necessary if the role of strontium against caries should be proved.

  5. Strontium-90 in ion-exchange resin used in the Australian FIEFS network

    International Nuclear Information System (INIS)

    Wise, K.N.

    1977-10-01

    In order to determine monthly strontium-90 fallout deposited at the eight Australian monitoring stations, account must be taken of the level of strontium-90 contamination of the ion-exchange resin as prepared for use in the FIEFS. This procedure has always been important in monitoring strontium-90 fallout deposit in Australia because the level of strontium-90 contamination of ion-exchange resin, supplied by manufacturers in the Northern Hemisphere, has remained of the same order of magnitude as the monthly fallout deposit in the Southern Hemisphere

  6. Seawater strontium isotopes, acid rain, and the Cretaceous-Tertiary boundary

    Science.gov (United States)

    Macdougall, J. D.

    1988-01-01

    A large bolide impact at the end of the Cretaceous would have produced significant amounts of nitrogen oxides by shock heating of the atmosphere. The resulting acid precipitation would have increased continental weathering greatly and could be an explanation for the observed high ratio of strontium-87 to strontium-86 in seawater at about this time, due to the dissolution of large amounts of strontium from the continental crust. Spikes to high values in the seawater strontium isotope record at other times may reflect similar episodes.

  7. Strontium eluting graphene hybrid nanoparticles augment osteogenesis in a 3D tissue scaffold

    Science.gov (United States)

    Kumar, Sachin; Chatterjee, Kaushik

    2015-01-01

    The objective of this work was to prepare hybrid nanoparticles of graphene sheets decorated with strontium metallic nanoparticles and demonstrate their advantages in bone tissue engineering. Strontium-decorated reduced graphene oxide (RGO_Sr) hybrid nanoparticles were synthesized by the facile reduction of graphene oxide and strontium nitrate. X-ray diffraction, transmission electron microscopy, and atomic force microscopy revealed that the hybrid particles were composed of RGO sheets decorated with 200-300 nm metallic strontium particles. Thermal gravimetric analysis further confirmed the composition of the hybrid particles as 22 wt% of strontium. Macroporous tissue scaffolds were prepared by incorporating RGO_Sr particles in poly(ε-caprolactone) (PCL). The PCL/RGO_Sr scaffolds were found to elute strontium ions in aqueous medium. Osteoblast proliferation and differentiation was significantly higher in the PCL scaffolds containing the RGO_Sr particles in contrast to neat PCL and PCL/RGO scaffolds. The increased biological activity can be attributed to the release of strontium ions from the hybrid nanoparticles. This study demonstrates that composites prepared using hybrid nanoparticles that elute strontium ions can be used to prepare multifunctional scaffolds with good mechanical and osteoinductive properties. These findings have important implications for designing the next generation of biomaterials for use in tissue regeneration.The objective of this work was to prepare hybrid nanoparticles of graphene sheets decorated with strontium metallic nanoparticles and demonstrate their advantages in bone tissue engineering. Strontium-decorated reduced graphene oxide (RGO_Sr) hybrid nanoparticles were synthesized by the facile reduction of graphene oxide and strontium nitrate. X-ray diffraction, transmission electron microscopy, and atomic force microscopy revealed that the hybrid particles were composed of RGO sheets decorated with 200-300 nm metallic strontium

  8. Strontium Localization in Bone Tissue Studied by X-Ray Absorption Spectroscopy

    DEFF Research Database (Denmark)

    Frankær, Christian Grundahl; Raffalt, Anders Christer; Ståhl, Kenny

    2014-01-01

    Strontium has recently been introduced as a pharmacological agent for the treatment and prevention of osteoporosis. We determined the localization of strontium incorporated into bone matrix from dogs treated with Sr malonate by X-ray absorption spectroscopy. A new approach for analyzing the X...... highly ordered sites, and at least 30 % is located at less ordered sites where only the first solvation shell is resolved, suggesting that strontium is sur- rounded by only oxygen atoms similar to Sr2? in solution. Strontium was furthermore shown to be absorbed in collagen in which it obtains a higher...

  9. Reduction in the absorption and retention of strontium in rats

    Energy Technology Data Exchange (ETDEWEB)

    Slat, B; Kostial, K; Harrison, G E

    1971-12-01

    Rats were fed a stock diet supplemented with calcium phosphate and sodium alginate, both separately and simultaneously, over a period of 4-5 months. Observations were made at intervals on the growth rate and on visual and histological abnormalities in some body tissues. No toxic effects were observed. The absorption and skeletal retention of calcium for rats on the combined supplements remained almost unchanged but the absorption and retention of strontium was reduced 7-fold.

  10. Strontium borate glass: potential biomaterial for bone regeneration

    OpenAIRE

    Pan, H. B.; Zhao, X. L.; Zhang, X.; Zhang, K. B.; Li, L. C.; Li, Z. Y.; Lam, W. M.; Lu, W. W.; Wang, D. P.; Huang, W. H.; Lin, K. L.; Chang, J.

    2009-01-01

    Boron plays important roles in many life processes including embryogenesis, bone growth and maintenance, immune function and psychomotor skills. Thus, the delivery of boron by the degradation of borate glass is of special interest in biomedical applications. However, the cytotoxicity of borate glass which arises with the rapid release of boron has to be carefully considered. In this study, it was found that the incorporation of strontium into borate glass can not only moderate the rapid relea...

  11. Extraction of cesium and strontium from nuclear waste

    Science.gov (United States)

    Davis, Jr., Milton W.; Bowers, Jr., Charles B.

    1988-01-01

    Cesium is extracted from acidified nuclear waste by contacting the waste with a bis 4,4'(5) [1-hydroxy-2-ethylhexyl]benzo 18-crown-6 compound and a cation exchanger in a matrix solution. Strontium is extracted from acidified nuclear waste by contacting the waste with a bis 4,4'(5') [1-hydroxyheptyl]cyclohexo 18-crown-6 compound, and a cation exchanger in a matrix solution.

  12. Applications of Random Nonlinear Photonic Crystals Based on Strontium Tetraborate

    Directory of Open Access Journals (Sweden)

    Alexandre I. Zaitsev

    2012-10-01

    Full Text Available Properties of strontium tetraborate (SBO and features of as-grown anti-parallel domains are summarized. From the point of view of nonlinear optics, these domains form nonlinear photonic crystals (NPC. Applications of NPC to the deep ultraviolet generation and fs pulse diagnostics are described. NPC and SBO are prospective media for the creation of a widely tunable source of fs pulses in the vacuum ultraviolet and for autocorrelation diagnostics of broadly tunable sources.

  13. Electrical behaviour of strontium-doped lanthanum manganite interfaces

    DEFF Research Database (Denmark)

    Koch, Søren; Hendriksen, P.V.; Jacobsen, Torben

    2005-01-01

    The contact resistance of strontium-doped lanthanum manganite (LSM) contact pairs is investigated by polarisation analysis at different temperatures and atmospheres. The ceramic contacts have a high contact resistance, and strongly nonlinear current–voltage behaviour is observed at low temperatur....... The nonlinear behaviour is ascribed to the presence of energy barriers at the contact interface. Generally, point contacts showed a more linear behaviour than plane contact interfaces....

  14. Strontium-rubidium infusion pump with in-line dosimetry

    International Nuclear Information System (INIS)

    Barker, S.L.; Loberg, M.D.

    1986-01-01

    A strontium-rubidium infusion system is described which consists of: (a) means for generating rubidium 82 in a solution which can be infused into a patient; (b) means for infusing the solution into a patient; (c) means for measuring the radioactivity present in the solution as it is infused into the patient; and (d) means for controlling the means for infusing in response to the amount of radioactivity which has been infused into the patient

  15. Practical aspects of the environmental behavior of strontium isotopes

    International Nuclear Information System (INIS)

    Madelmont, Claude; Bittel, Robert; Daburon, Francois.

    1977-03-01

    The practical aspects of contamination patterns of the food chain by strontium isotopes are reviewed - plants with special emphasis on the consequences of irrigation (contamination level at equilibrium); dairy products and the adjustement of a general model to regional conditions (a table of quantitative parameters for some French regions is included); marine and freshwater products. One should keep in mind that transfer parameters may change with time and cannot be assessed definitively [fr

  16. Iodide behaviour in hard clay rocks under controlled physico-chemical conditions at different concentrations

    International Nuclear Information System (INIS)

    Frasca, B.; Savoye, S.; Wittebroodt, C.; Leupin, O.X.; Descostes, M.; Grenut, B.; Meier, P.; Michelot, J.L.

    2010-01-01

    Document available in extended abstract form only. With a half-life of 1.6 10 7 years, its high mobility and its potential to accumulate in the biosphere, iodine-129 is considered, from safety assessment calculations for radioactive waste repositories, to be one of the main radiological dose contributors. Based on the findings of previous studies, iodide, especially at low concentrations, seems to be migrating at a slower rate in clay rock than Cl-36. The cause of this retardation regarding the diffusion of iodide versus chloride is not yet understood but several hypotheses are point towards sorption on natural organic matter (NOM), pyrite or redox reactions. Oxidation of iodide would form IO 3 - which is known to have a higher sorption affinity on several soils and sediment samples than iodide. The present project aims at exploring the effect on the iodide behaviour of two parameters: (i) the initial concentration of iodide and (ii) the amount of NOM contained in the argillite samples. Such an investigation is carried out on Tournemire argillite by means of both batch and through-diffusion experiments. The main challenge is to exclude as much as possible the occurrence of any experimental artefact that could induce iodide uptake (oxygen contamination, dissolution/precipitation of carbonate phases). Regarding redox conditions and rock equilibrium, all the experiments were carried out under physico-chemical conditions as close as possible to those prevailing in field. Using a glove box with an atmosphere of N 2 /CO 2 (respectively 99.6% and 0.4%), we preserved the experiments from oxygen and maintained the calculated in-situ carbonate equilibrium. At first, four through-diffusion experiments with the non-sorbing tracers HTO and Cl-36 were performed to allow the diffusive parameters of each sample to be defined. Afterwards, iodide was injected in the diffusion cells at four different concentrations (10 -6 M to 10 -3 M). Thus, the comparison of the incoming fluxes of

  17. Literature survey of strontium-89/90 analysis

    International Nuclear Information System (INIS)

    Kwakman, P.J.M.

    1994-08-01

    At the RIVM Laboratory of Radiation Research (LSO), the determination of strontium-89/90 in grass and milk samples using fuming nitric acid is a bottle neck in the routine monitoring programme, mainly due to the use of hazardous chemicals. In recent scientific articles, a number of alternatives have been described. This report gives an overview of the latest developments in this field and compares the pros and cons of these methods. The most promising method appears to be the 'Sr-spec' method developed by EIChrom Industries. In this method, an ion-exchanger is used for sorption of cations from the sample solution and, subsequently, a crown ether on a polymer support is applied for the selective complexation of bivalent strontium ions in the presence of other interfering bivalent ions. An important advantage is that the hazardous fuming nitric acid can be omitted and that the total number of chemical separation steps can be largely reduced. The possibility of a routine application of the 'Sr-spec' method for the determination of strontium-89/90 in grass and milk at RIVM/LSO is proposed. 2 tabs., 1 appendix, 23 refs

  18. Microwave-hydrothermal synthesis of barium strontium titanate nanoparticles

    International Nuclear Information System (INIS)

    Simoes, A.Z.; Moura, F.; Onofre, T.B.; Ramirez, M.A.; Varela, J.A.; Longo, E.

    2010-01-01

    Research highlights: → Barium strontium titanate nanoparticles were obtained by the Hydrothemal microwave technique (HTMW) → This is a genuine technique to obtain nanoparticles at low temperature and short times → Barium strontium titanate free of carbonates with tetragonal structure was grown at 130 o C. - Abstract: Hydrothermal-microwave method (HTMW) was used to synthesize crystalline barium strontium titanate (Ba 0.8 Sr 0.2 TiO 3 ) nanoparticles (BST) in the temperature range of 100-130 o C. The crystallization of BST with tetragonal structure was reached at all the synthesis temperatures along with the formation of BaCO 3 as a minor impurity at lower syntheses temperatures. Typical FT-IR spectra for tetragonal (BST) nanoparticles presented well defined bands, indicating a substantial short-range order in the system. TG-DTA analyses confirmed the presence of lattice OH- groups, commonly found in materials obtained by HTMW process. FE/SEM revealed that lower syntheses temperatures led to a morphology that consisted of uniform grains while higher syntheses temperature consisted of big grains isolated and embedded in a matrix of small grains. TEM has shown BST nanoparticles with diameters between 40 and 80 nm. These results show that the HTMW synthesis route is rapid, cost effective, and could serve as an alternative to obtain BST nanoparticles.

  19. Strontium borate glass: potential biomaterial for bone regeneration.

    Science.gov (United States)

    Pan, H B; Zhao, X L; Zhang, X; Zhang, K B; Li, L C; Li, Z Y; Lam, W M; Lu, W W; Wang, D P; Huang, W H; Lin, K L; Chang, J

    2010-07-06

    Boron plays important roles in many life processes including embryogenesis, bone growth and maintenance, immune function and psychomotor skills. Thus, the delivery of boron by the degradation of borate glass is of special interest in biomedical applications. However, the cytotoxicity of borate glass which arises with the rapid release of boron has to be carefully considered. In this study, it was found that the incorporation of strontium into borate glass can not only moderate the rapid release of boron, but also induce the adhesion of osteoblast-like cells, SaOS-2, thus significantly increasing the cyto-compatibility of borate glass. The formation of multilayers of apatite with porous structure indicates that complete degradation is optimistic, and the spread of SaOS-2 covered by apatite to form a sandwich structure may induce bone-like tissue formation at earlier stages. Therefore, such novel strontium-incorporated borosilicate may act as a new generation of biomaterial for bone regeneration, which not only renders boron as a nutritious element for bone health, but also delivers strontium to stimulate formation of new bones.

  20. Assessment of strontium in the Savannah River Site environment

    International Nuclear Information System (INIS)

    Carlton, W.H.; Evans, A.G.; Geary, L.A.; Murphy, C.E. Jr.; Strom, R.N.

    1992-01-01

    This document on strontium is published as a part of the Radiological Assessment Program (RAP). It is the sixth in a series of eight documents on individual radioisotopes released to the environment as a result of SRS (Savannah River Site) operations. Strontium exists in the environment as a result of above-ground nuclear weapons tests, the Chernobyl accident, the destruction of satellite Cosmos 954, small releases from reactors and reprocessing plants, and the operation of industrial, medical, and educational facilities. Strontium has been produced at SRS during the operation of 5 production reactors. About 300 curies of radiostrontium were released into streams in the late 50s and 60s, primarily from leaking fuel elements in reactor storage basins. Smaller quantities were released from the fuel reprocessing operations. About 400 Ci were released to seepage basins. A much smaller quantity, about 2 Ci, was released to the atmosphere. The overall radiological impact of SRS releases on the offsite maximum individual can be characterized by total doses of 6.2 mrem (atmospheric) and 1.4 mrem (liquid), compared with a dose of 12,960 mrem from non-SRS sources during the same period of time. Radiostrontium releases have resulted in a negligible risk to the environment and the population it supports

  1. Assessment of strontium in the Savannah River Site environment

    Energy Technology Data Exchange (ETDEWEB)

    Carlton, W.H.; Evans, A.G.; Geary, L.A.; Murphy, C.E. Jr.; Strom, R.N.

    1992-12-31

    This document on strontium is published as a part of the Radiological Assessment Program (RAP). It is the sixth in a series of eight documents on individual radioisotopes released to the environment as a result of SRS (Savannah River Site) operations. Strontium exists in the environment as a result of above-ground nuclear weapons tests, the Chernobyl accident, the destruction of satellite Cosmos 954, small releases from reactors and reprocessing plants, and the operation of industrial, medical, and educational facilities. Strontium has been produced at SRS during the operation of 5 production reactors. About 300 curies of radiostrontium were released into streams in the late 50s and 60s, primarily from leaking fuel elements in reactor storage basins. Smaller quantities were released from the fuel reprocessing operations. About 400 Ci were released to seepage basins. A much smaller quantity, about 2 Ci, was released to the atmosphere. The overall radiological impact of SRS releases on the offsite maximum individual can be characterized by total doses of 6.2 mrem (atmospheric) and 1.4 mrem (liquid), compared with a dose of 12,960 mrem from non-SRS sources during the same period of time. Radiostrontium releases have resulted in a negligible risk to the environment and the population it supports.

  2. A glucose bio-battery prototype based on a GDH/poly(methylene blue) bioanode and a graphite cathode with an iodide/tri-iodide redox couple.

    Science.gov (United States)

    Wang, Jen-Yuan; Nien, Po-Chin; Chen, Chien-Hsiao; Chen, Lin-Chi; Ho, Kuo-Chuan

    2012-07-01

    A glucose bio-battery prototype independent of oxygen is proposed based on a glucose dehydrogenase (GDH) bioanode and a graphite cathode with an iodide/tri-iodide redox couple. At the bioanode, a NADH electrocatalyst, poly(methylene blue) (PMB), which can be easily grown on the electrode (screen-printed carbon paste electrode, SPCE) by electrodeposition, is harnessed and engineered. We find that carboxylated multi-walled carbon nanotubes (MWCNTs) are capable of significantly increasing the deposition amount of PMB and thus enhancing the PMB's electrocatalysis of NADH oxidation and the glucose bio-battery's performance. The choice of the iodide/tri-iodide redox couple eliminates the dependence of oxygen for this bio-battery, thus enabling the bio-battery with a constant current-output feature similar to that of the solar cells. The present glucose bio-battery prototype can attain a maximum power density of 2.4 μW/cm(2) at 25 °C. Crown Copyright © 2012. Published by Elsevier Ltd. All rights reserved.

  3. THERAPY OF GRAVES’ DISEASE WITH SODIUM IODIDE-131

    Directory of Open Access Journals (Sweden)

    I Wayan Hartadi Noor

    2013-11-01

    Full Text Available Normal 0 false false false EN-US X-NONE X-NONE MicrosoftInternetExplorer4 Graves’ disease is the most common form of thyrotoxicosis, with a peak incidence in the 20-40 year of age group. Females are involved about five times more commonly than male. The easiest sign to recognize patients with Graves’ disease is the present of Graves’ ophthalmopathy. The diagnosis of Graves’ disease may sometimes base only on a physical examination and a medical history. Diffuse thyroid enlargement and sign of thyrotoxicosis, mainly ophthalmopathy and to lesser extent dermopathy, usually adequate for diagnosis. TSH test combined with FT4 test is usually the first laboratory test performs in these patients. The patients suffered Graves’ disease can be treated with antithyroid drug therapy or undergo subtotal Thyroidectomy. Another therapy is by using sodium iodide-131, where this therapy has advantages including easy administration, effectiveness, low expense, and absence of pain. /* Style Definitions */ table.MsoNormalTable {mso-style-name:"Table Normal"; mso-tstyle-rowband-size:0; mso-tstyle-colband-size:0; mso-style-noshow:yes; mso-style-priority:99; mso-style-qformat:yes; mso-style-parent:""; mso-padding-alt:0in 5.4pt 0in 5.4pt; mso-para-margin:0in; mso-para-margin-bottom:.0001pt; mso-pagination:widow-orphan; font-size:11.0pt; font-family:"Calibri","sans-serif"; mso-ascii-font-family:Calibri; mso-ascii-theme-font:minor-latin; mso-fareast-font-family:"Times New Roman"; mso-fareast-theme-font:minor-fareast; mso-hansi-font-family:Calibri; mso-hansi-theme-font:minor-latin; mso-bidi-font-family:"Times New Roman"; mso-bidi-theme-font:minor-bidi;}

  4. Carbamazepine (Tegretol) inhibits in vivo iodide uptake and hormone synthesis in rat thyroid glands

    International Nuclear Information System (INIS)

    Villa, S.M.; Alexander, N.M.

    1987-01-01

    Decreased serum concentrations of T3 and T4 occur in patients treated with the anticonvulsant drug carbamazepine (CBZ), but with rare exception, these patients remain euthyroid. The mechanism that accounts for diminished hormone levels is unknown, and our objective was to study the direct effect of CBZ on iodide uptake and hormone synthesis in thyroid glands of CBZ-treated and pair-fed control rats. Chronic ingestion (per os) of CBZ in male rats reduced the four hour thyroid 131I-iodide uptake by approximately 60%. This inhibition occurred after the animals had received sufficient CBZ to attain plasma CBZ concentrations of 0.8 microgram/ml. Continued treatment with CBZ ranging from 560 to 800 mg/kg/day for 14 days did not result in further inhibition of iodide uptake even though the plasma CBZ concentrations had increased 6-20 fold. No inhibition of iodide uptake was apparent when the animals initially received CBZ ranging from 40 to 152 mg/kg body weight for 22 days when there were no detectable levels of plasma CBZ. Overall growth rates of CBZ-treated rats were slightly (6-10%) less than the pair-fed control animals. Plasma T4 concentrations were reduced by 18% (p less than 0.05) in the CBZ-fed animals, while T3 concentrations were diminished by 53% (p less than 0.01). CBZ appeared to alter thyroidal iodide transport because the thyroid:plasma iodide ratios were decreased by 26% in the drug-treated rats. The distribution of radioiodine in thyroidal iodoamino acids was essentially the same in both groups of rats but the absolute quantities of radioiodine were more than 2.5 times greater in the control rats. CBZ failed to inhibit peroxidase-catalyzed iodide and guaiacol oxidation in vitro

  5. Gas thermodesorption study of barium and strontium cerates

    International Nuclear Information System (INIS)

    Aksenova, T.I.; Khromushin, I.V.; Zhotabaev, Zh.R.; Bukenov, K.D.; Medvedeva, Z.V.; Berdauletov, A.K.

    2002-01-01

    Kinetic of water, oxygen, hydrogen and carbon dioxide molecules release from doped and undoped samples of barium cerates and doped strontium cerates during vacuum heating was studied. The samples were prepared by inductive melting method. The following two kinds of preliminary samples treatments were used: annealing in air (650-750 deg. C) and wet nitrogen atmosphere (625 deg.C). Main results of thermodesorption studies of barium and strontium cerates are represented in the table. The samples of doped LaSrMnO were investigated also. It was found that the initial doped samples (without preliminary annealing) did not show any gas release in temperature range of 20-1100 deg. C. This fact indicates on high stability of compositions and strong bond of 'host' oxygen in their lattice. A significant amount of water and oxygen molecules were released from BaCe 0.9 Nd 0.1 O 3 samples whereas water and hydrogen molecules desorption from SrCe 0.95 Y 0.05 O 3 samples took place. Hydrogen molecules desorption was found for strontium cerates samples; no hydrogen molecules release was observed for doped and pure barium cerate samples.Intensive water molecules release from doped samples confirms the necessity of oxygen vacancies creation in these compounds to get properties of proton conductivity, since it was not found any water molecules release from annealed undoped samples of BaCeO 3 It is necessary to notice that oxygen molecules release from these samples took place at ∼1000 deg. C that is significantly higher then from BaCeNdO samples. Forms of high temperatures part of oxygen and low temperature part of water spectra indicate that phase transformations are responsible for oxygen and water molecules desorption in this cases. These results are in good agreement with literature data. Desorption of water molecules from barium and strontium cerates took place. Oxygen desorption took place only from barium cerates. It can be explained as the following: doped barium cerates have

  6. The method of determination of micro quantities of labelled iodide in Na125 I carrier free solution

    International Nuclear Information System (INIS)

    Kholbaev, A.Kh.; Shilin, E.A.

    1996-01-01

    The analytical method was elaborated with the purpose to increase detection limit and radiation safety of labelled iodide determination. The method includes oxidation of iodide by iodate in diluted sulphur acid solution with molar concentration 0,03-0,04/moles/litre at molar ratio of iodide to iodate I - :IO - 3 1:12,5. The extraction of I 2 produced is done by toluene. (author)

  7. Comment on: 'The strontium isotopic composition of seawater and seawater-oceanic crust interaction' by E.T.C. Spooner

    International Nuclear Information System (INIS)

    Brass, G.W.; Turekian, K.L.

    1977-01-01

    Various processes have been proposed as the source of strontium to the oceans but there is no evidence to support the mechanism of release of relatively unradiogenic strontium from deep dea basalts to sea-water. (B.D.)

  8. Strontium migration in a crystalline medium: effects of the presence of bentonite colloids.

    Science.gov (United States)

    Albarran, Nairoby; Missana, Tiziana; García-Gutiérrez, Miguel; Alonso, Ursula; Mingarro, Manuel

    2011-03-25

    The effects of bentonite colloids on strontium migration in fractured crystalline medium were investigated. We analyzed first the transport behaviour of bentonite colloids alone at different flow rates; then we compared the transport behaviour of strontium as solute and of strontium previously adsorbed onto stable bentonite colloids at a water velocity of approximately 7.1·10(-6)m/s-224m/yr. Experiments with bentonite colloids alone showed that - at the lowest water flow rate used in our experiments (7.1·10(-6)m/s) - approximately 70% of the initially injected colloids were retained in the fracture. Nevertheless, the mobile colloidal fraction, moved through the fracture without retardation, at any flow rate. Bentonite colloids deposited over the fracture surface were identified during post-mortem analyses. The breakthrough curve of strontium as a solute, presented a retardation factor, R(f)~6, in agreement with its sorption onto the granite fracture surface. The breakthrough curve of strontium in the presence of bentonite colloids was much more complex, suggesting additional contributions of colloids to strontium transport. A very small fraction of strontium adsorbed on mobile colloids moved un-retarded (R(f)=1) and this fraction was much lower than the expected, considering the quantity of strontium initially adsorbed onto colloids (90%). This behaviour suggests the hypothesis of strontium sorption reversibility from colloids. On the other hand, bentonite colloids retained within the granite fracture played a major role, contributing to a slower strontium transport in comparison with strontium as a solute. This was shown by a clear peak in the breakthrough curve corresponding to a retardation factor of approximately 20. Copyright © 2010 Elsevier B.V. All rights reserved.

  9. Strontium incorporates at sites critical for bone mineralization in rats with renal failure

    International Nuclear Information System (INIS)

    Oste, Line; Verberckmoes, Steven C.; Behets, Geert J.; Dams, Geert; Bervoets, An R.; De Broe, Marc E.; D'Haese, Patrick C.; Van Hoof, Viviane O.; Bohic, Sylvain; Drakopoulos, Michael

    2007-01-01

    We previously demonstrated the development of a mineralization defect during strontium administration and its reversibility after withdrawal in rats with chronic renal failure. Recently, strontium ranelate has been introduced as a therapeutic agent for osteoporosis. However, caution has to be taken, as this bone disorder mainly develops in elderly people who may present a moderately decreased renal function. In order to assess the ultra-structural localization of strontium in bone and thereby to get a better insight into the element's systemic effects on bone, synchrotron-based x-ray micro-fluorescence was applied, which showed that after 2 weeks of strontium loading (2 g l -1 in drinking water) in rats with renal failure, concomitant with the development of impaired mineralization, the element was localized mainly at the outer edge of the mineralized bone, while after longer loading periods, a more homogeneous distribution was found. After washout, strontium was found at sites deeper within the trabeculae, while newly deposited low-strontium-containing mineral was found at the outer edges. Synchrotron x-ray micro-diffraction analysis showed that strontium is incorporated in the apatite crystal lattice through exchange with calcium. The results show that strontium is initially incorporated in bone at sites of active bone mineralization, close to the osteoid/mineralization front.Most likely, strontium binds to matrix proteins serving as crystal nucleation points and by hetero-ionic substitution with calcium within the hydroxyapatite crystals, thereby impairing further hydroxyapatite formation. After withdrawal, strontium is released from these sites, by which mineralization is restored and the previously formed strontium-containing hydroxyapatite is buried under a new layer of mineralized bone. (authors)

  10. Study on the Electrochemical Behavior of Iodide at Platinum Electrode in Potassium Chlorate Solution

    Energy Technology Data Exchange (ETDEWEB)

    Jung, Sang Hyuk; Yeon, Jei Won; Song, Kyu Seok [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2012-05-15

    Radioactive iodine-131, is one of the most hazardous fission products which could be released from fuels of nuclear reactors during the severe accident of nuclear power plants. Due to its high radioactivity, high fission yield (2.8%) and hazardous biological effects, the behavior of iodine has been taken interests in many research groups. Iodine is known to be released from the fuels as a cesium iodide form, CsI. And, as nuclear fuels are mostly placed in the water pool, it is easily dissolved in the water after released from the fuels. In water, iodide anion could be oxidized into molecular iodine. As the molecular iodine is a volatile species and the oxidizing rate is affected by many environmental facts such as pH, radiolysis products and temperature, the oxidation reaction of the iodide ion has been considered as an important chemical reaction related to the severe accident of nuclear power plants In present work, the electrochemical behavior of iodide anion was observed by using cyclic voltammetric technique in potassium chlorate solutions. We observed two different oxidation waves in the oxidation potential region. From the comparison with the previous reported results, one is regarded as the oxidation of iodide into molecular iodine. The other is evaluated to be the formation of high-valent iodine-containing compounds

  11. Estradiol decreases iodide uptake by rat thyroid follicular FRTL-5 cells

    Directory of Open Access Journals (Sweden)

    Furlanetto T.W.

    2001-01-01

    Full Text Available Estradiol has well-known indirect effects on the thyroid. A direct effect of estradiol on thyroid follicular cells, increasing cell growth and reducing the expression of the sodium-iodide symporter gene, has been recently reported. The aim of the present investigation was to study the effect of estradiol on iodide uptake by thyroid follicular cells, using FRTL-5 cells as a model. Estradiol decreased basal iodide uptake by FRTL-5 cells from control levels of 2.490 ± 0.370 to 2.085 ± 0.364 pmol I-/µg DNA at 1 ng/ml (P<0.02, to 1.970 ± 0.302 pmol I-/µg DNA at 10 ng/ml (P<0.003, and to 2.038 ± 0.389 pmol I-/µg DNA at 100 ng/ml (P<0.02. In addition, 4 ng/ml estradiol decreased iodide uptake induced by 0.02 mIU/ml thyrotropin from 8.678 ± 0.408 to 7.312 ± 0.506 pmol I-/µg DNA (P<0.02. A decrease in iodide uptake by thyroid cells caused by estradiol has not been described previously and may have a role in goiter pathogenesis.

  12. Monitoring of fluoride and iodide levels in drinking water using ion selective electrodes

    International Nuclear Information System (INIS)

    Ahmed, R.; Viqar-Un-Nisa; Hussain, M.; Tanwir, R.; Qureshi, S.A.

    2004-01-01

    Fluoride and iodide, the most important constituents of drinking water are essential as well as toxic depending on their levels. For their analysis in water mostly ion-selective electrodes, spectrophotometry, titrimetry and coulometry etc; have been used and literature has been briefly reviewed. Ion-selective electrodes offer an efficient method for the measurement of the two halides and were mostly used during this work. Fabrication of these electrodes is briefly described. Comparison of results obtained by ion selective electrode and coulometry is given. Recoveries of the added fluoride ions from the samples were good. A large number of water samples from Rawalpindi-Islamabad area were analyzed for fluoride and iodide. Levels of fluoride and iodide from two main water reservoirs of Rawalpindi and Islamabad are reported before and after treatment. Both surface and ground water samples were analyzed and results are compared and discussed. Some samples from northern areas were also analyzed for iodide and fluoride and compared. Intake of fluoride and iodide from water of different areas is also compared. Water samples, which caused bone deformation in certain areas in Punjab due to excess fluoride, were also analyzed for fluoride and results are presented. (author)

  13. Processes of adsorption/desorption of iodides and cadmium cations onto/from Ag(111

    Directory of Open Access Journals (Sweden)

    VLADIMIR D. JOVIĆ

    2011-02-01

    Full Text Available In this work, the adsorption/desorption processes of iodides and cadmium cations in the presence of iodides onto/from Ag(111 were investigated. It was shown that both processes were complex, characterized by several peaks on the cyclic voltammograms (CVs. By PeakFit analysis of the recorded CVs and subsequent fitting of the obtained peaks by the Frumkin adsorption isotherm, the interaction parameter (f and the Gibbs energy of adsorption (DGads for each adsorbed phase were determined. In the case of iodide adsorption, four peaks were characterized by negative values of f, indicating attractive lateral interaction between the adsorbed anions, while two of them possessed value of f < –4, indicating phase transition processes. The adsorption/desorption processes of cadmium cations (underpotential deposition – UPD of cadmium in the presence of iodide anions was characterized by two main peaks, each of them being composed of two or three peaks with negative values of f. By the analysis of charge vs. potential dependences obtained either from the CVs or current transients on potentiostatic pulses, it was concluded that adsorbed iodides did not undergo desorption during the process of Cd UPD, but became replaced by Cd ad-atoms and remained adsorbed on top of a Cd layer and/or in between Cd the ad-atoms.

  14. Alpha-lipoic acid induces sodium iodide symporter expression in TPC-1 thyroid cancer cell line

    International Nuclear Information System (INIS)

    Choi, Hyun-Jeung; Kim, Tae Yong; Ruiz-Llorente, Sergio; Jeon, Min Ji; Han, Ji Min; Kim, Won Gu; Shong, Young Kee; Kim, Won Bae

    2012-01-01

    Introduction: Patients with metastatic thyroid cancers that do not uptake iodine need effective therapeutic option. Differentiation-inducing agents have been tried to restore functional expression of sodium iodide symporter (NIS) without success. Our objective was to assess the effect of alpha-lipoic acid (ALA), known as potential antioxidant, on expression of sodium iodide symporter in thyroid cancer cells. Methods: Human thyroid cancer-derived cell lines, TPC-1, were treated with ALA, and changes in NIS mRNA and protein expression were measured. ALA's effect on NIS gene promoter was evaluated, and functional NIS expression was assessed by iodide uptake assay. Results: Treatment with ALA increased NIS mRNA expression up to ten folds of control dose-dependently after 24 h of exposure. ALA increased NIS promoter activity, and increased iodide uptake by 1.6 fold. ALA induced expression of NIS protein, but had no significant effect on the plasma membrane trafficking. ALA increased phosphorylation of CREB and nuclear translocation of pCREB, and co-treatment of ALA and trichostatin A increased iodide uptake by three folds in TPC-1 cells. Conclusions: ALA is a potential agent to increase NIS transcription in TPC-1. It could be used as an adjunctive agent to increase efficacy of radioiodine therapy if combined with a strategy to increase NIS protein trafficking to cell membrane.

  15. Capture of organic iodides from nuclear waste by metal-organic framework-based molecular traps.

    Science.gov (United States)

    Li, Baiyan; Dong, Xinglong; Wang, Hao; Ma, Dingxuan; Tan, Kui; Jensen, Stephanie; Deibert, Benjamin J; Butler, Joseph; Cure, Jeremy; Shi, Zhan; Thonhauser, Timo; Chabal, Yves J; Han, Yu; Li, Jing

    2017-09-07

    Effective capture of radioactive organic iodides from nuclear waste remains a significant challenge due to the drawbacks of current adsorbents such as low uptake capacity, high cost, and non-recyclability. We report here a general approach to overcome this challenge by creating radioactive organic iodide molecular traps through functionalization of metal-organic framework materials with tertiary amine-binding sites. The molecular trap exhibits a high CH 3 I saturation uptake capacity of 71 wt% at 150 °C, which is more than 340% higher than the industrial adsorbent Ag 0 @MOR under identical conditions. These functionalized metal-organic frameworks also serve as good adsorbents at low temperatures. Furthermore, the resulting adsorbent can be recycled multiple times without loss of capacity, making recyclability a reality. In combination with its chemical and thermal stability, high capture efficiency and low cost, the adsorbent demonstrates promise for industrial radioactive organic iodides capture from nuclear waste. The capture mechanism was investigated by experimental and theoretical methods.Capturing radioactive organic iodides from nuclear waste is important for safe nuclear energy usage, but remains a significant challenge. Here, Li and co-workers fabricate a stable metal-organic framework functionalized with tertiary amine groups that exhibits high capacities for radioactive organic iodides uptake.

  16. An investigation of sodium iodide solubility in sodium-stainless steel systems

    International Nuclear Information System (INIS)

    Sagawa, Norihiko; Tashiro, Suguru

    1996-01-01

    Sodium iodide and major constituents of stainless steel in sodium are determined by using the steel capsules to obtain a better understanding on contribution of the constituents to the apparent iodide solubility in sodium. The capsule loaded with 20 g sodium and 0.1 - 0.3 g powder of sodium iodide is heated at its upper part in a furnace and cooled at its bottom on brass plates to establish a large temperature gradient along the capsule tube. After a given period of equilibration, the iodide and constituents are fixed in solidified sodium by quick quenching of the capsules. Sodium samples are taken from the sectioned capsule tube and submitted to sodium dissolution by vaporized water for determination of the iodine and to vacuum distillation for determination of the metal elements. Iron and nickel concentrations are observed to be lower in the samples at higher iodine concentrations. Chromium and manganese concentrations are seen to be insensitive to the iodine concentrations. The observations can be interpreted by a model that sodium oxide combines with metal iodide in sodium to form a complex compound and with consideration that the compound will fall and deposit onto the bottom of the capsule by thermal diffusion. (author)

  17. Capture of organic iodides from nuclear waste by metal-organic framework-based molecular traps

    KAUST Repository

    Li, Baiyan

    2017-09-01

    Effective capture of radioactive organic iodides from nuclear waste remains a significant challenge due to the drawbacks of current adsorbents such as low uptake capacity, high cost, and non-recyclability. We report here a general approach to overcome this challenge by creating radioactive organic iodide molecular traps through functionalization of metal-organic framework materials with tertiary amine-binding sites. The molecular trap exhibits a high CH3I saturation uptake capacity of 71 wt% at 150 °C, which is more than 340% higher than the industrial adsorbent Ag0@MOR under identical conditions. These functionalized metal-organic frameworks also serve as good adsorbents at low temperatures. Furthermore, the resulting adsorbent can be recycled multiple times without loss of capacity, making recyclability a reality. In combination with its chemical and thermal stability, high capture efficiency and low cost, the adsorbent demonstrates promise for industrial radioactive organic iodides capture from nuclear waste. The capture mechanism was investigated by experimental and theoretical methods.Capturing radioactive organic iodides from nuclear waste is important for safe nuclear energy usage, but remains a significant challenge. Here, Li and co-workers fabricate a stable metal-organic framework functionalized with tertiary amine groups that exhibits high capacities for radioactive organic iodides uptake.

  18. The value of iodide as a parameter in the chemical characterisation of groundwaters

    Science.gov (United States)

    Lloyd, J. W.; Howard, K. W. F.; Pacey, N. R.; Tellam, J. H.

    1982-06-01

    Brackish and saline groundwaters can severely constrain the use of fresh groundwaters. Their chemical characterisation is important in understanding the hydraulic conditions controlling their presence in an aquifer. Major ions are frequently of limited value but minor ions can be used. Iodide in groundwater is particularly significant in many environments due to the presence of soluble iodine in aquifer matrix materials. Iodide is found in groundwaters in parts of the English Chalk aquifer in concentrations higher than are present in modern seawater. Its presence is considered as a indication of groundwater residence and is of use in the characterisation of fresh as well as saline waters. Under certain circumstances modern seawater intrusion into aquifers along English estuaries produces groundwaters which are easily identified due to iodide enrichment from estuarine muds. In other environments iodide concentrations are of value in distinguishing between groundwaters in limestones and shaly gypsiferous rocks as shown by a study in Qatar, while in an alluvial aquifer study in Peru iodide has been used to identify groundwaters entering the aquifer from adjacent granodiorites.

  19. Stable iodide doping induced by photonic curing for carbon nanotube transparent conductive films

    Science.gov (United States)

    Wachi, Atsushi; Nishikawa, Hiroyuki; Zhou, Ying; Azumi, Reiko

    2018-06-01

    Doping has become crucial for achieving stable and high-performance conductive transparent carbon nanotube (CNT) films. In this study, we systematically investigate the doping effects of a few materials including alkali metal iodides, nonmetal iodide, and metals. We demonstrate that photonic curing can enhance the doping effects, and correspondingly improve the conductivity of CNT films, and that such iodides have better doping effects than metals. In particular, doping with a nonmetal compound (NH4I) shows the largest potential to improve the conductivity of CNT films. Typically, doping with metal iodides reduces the sheet resistance (R S) of CNT films with 70–80% optical transmittances at λ = 550 nm from 600–2400 to 250–440 Ω/square, whereas doping with NH4I reduces R S to 57 and 84 Ω/square at 74 and 84% optical transmittances, respectively. Interestingly, such a doped CNT film exhibits only a slight increase in sheet resistance under an extreme environment of high temperature (85 °C) and high relative humidity (85%) for 350 h. The results suggest that photonic-curing-induced iodide doping is a promising approach to producing high-performance conductive transparent CNT films.

  20. Trapping radiodine, in the form of methyl iodide, on nuclear carbon

    Energy Technology Data Exchange (ETDEWEB)

    Nacapricha, D. [Mahidol Univ., Bangkok (Thailand); Taylor, C. [John Moores Univ., Liverpool (United Kingdom)

    1996-12-31

    Studies have been performed on potassium-iodide-impregnated charcoals of the type used in the nuclear industry for trapping radioiodine released during nuclear fission. The effects of various parameters on the trapping efficiency of methyl iodide have been investigated. A variation in particle size within a bulk charcoal caused poor precision in K value measurements because of differences in surface area, pore volume, and bed density, leading to differences in the deposition of the impregnant. Precision is improved by sieving the charcoal to a narrower size because smaller particles have a higher porosity. This finding is supported by surface area and pore measurements. Two methods of impregnation are compared by measuring K values and the deposition of potassium iodide. Charcoal impregnated by rotary evaporation exhibits both higher K values and higher potassium iodide contents than sprayed charcoal. Two designs of spraying drum are compared: a drum with helical vanes allows more efficient deposition and more uniform distribution of impregnant than a drum with axial vanes. A decrease in the K value with increasing humidity correlates with the available surface area. A similar correlation exists between water content and available pore volume. Aging of potassium-iodide-impregnated charcoal, caused by the formation of oxygen complexes on the surface, is associated with significant falls in K value. K values of charcoals also can be restored to at least their original values by heat treatment in the absence of air. 12 refs., 6 figs., 1 tab.

  1. Functional activity of human sodium/iodide symporter in tumor cell lines

    International Nuclear Information System (INIS)

    Petrich, T.; Knapp, W.H.; Poetter, E.

    2003-01-01

    Aim: The sodium/iodide symporter (NIS) actively transports iodide into thyrocytes. Thus, NIS represents a key protein for diagnosis and radioiodine therapy of differentiated thyroid cancer. Additionally, in the future the NIS gene may be used for cancer gene therapy of non-thyroid-derived malignancies. In this study we evaluated the functionality of NIS with respect to iodide uptake in a panel of tumor cell lines and compared this to gene transfer efficiency. Methods: A human NIS-containing expression vector and reporter-gene vectors encoding and beta;-Galactosidase- or EGFP were used for transient transfection of 13 tumor cell lines. Following transfection measurements of NIS-mediated radioiodide uptake using Na 125 I and of transfection efficiency were performed. The latter included β;-Galactosidase activity measurements using a commercial kit and observation by fluorescence microscopy for EGFP expression. Results: In contrast to respective parental cells, most NIS-transfected cell lines displayed high, perchlorate-sensitive radioiodide uptake. Differences in radioiodide uptake between cell lines apparently corresponded to transfection efficiencies, as judged from reporter-gene assays. Conclusion: With respect to iodide uptake we provide evidence that NIS is functional in different cellular context. As iodide uptake capacity appears to be well correlated to gene transfer efficiency, cell type-specific actions on NIS (e. g. post-translational modification such as glycosylation) are not inhibitory to NIS function. Our data support the promising role of NIS in cancer gene therapy strategies. (orig.)

  2. Growth and characterisation of lead iodide single crystals

    International Nuclear Information System (INIS)

    Tonn, Justus

    2012-01-01

    The work in hand deals with the growth and characterisation of lead iodide (PbI 2 ) single crystals. PbI 2 is regarded as a promising candidate for low-noise X- and gamma ray detection at room temperature. Its benefits if compared to conventional materials like HgI 2 , CdTe, Si, or GaAs lie in a band gap energy of 2.32 eV, an excellent ability to absorb radiation, and a high electrical resistivity. For an application of PbI 2 as detector material the growth and characterisation of crystals with high chemical and structural quality is extremely challenging. In light of this, the effectiveness of zone purification of the PbI 2 used for crystal growth was confirmed by spectroscopic analysis. Furthermore, technological aspects during processing of purified PbI 2 were investigated. With the help of thermal analysis, a correlation was found between the degree of exposing the source material to oxygen from the air and the structural quality of the resulting crystals. A hydrogen treatment was applied to PbI 2 as an effective method for the removal of oxidic pollutions, which resulted in a significant reduction of structural defects like polytypic growth and stress-induced cracking. The growth of PbI 2 single crystals was, among others, carried out by the Bridgman-Stockbarger method. In this context, much effort was put on the investigation of influences resulting from the design and preparation of ampoules. For the first time, crystal growth of PbI 2 was also carried out by the Czochralski method. If compared to the Bridgman-Stockbarger method, the Czochralski technique allowed a significantly faster growth of nearly crack-free crystals with a reproducible predetermination of crystallographic orientation. By an optimised sample preparation of PbI 2 , surface orientations perpendicular to the usually cleaved (0001) plane were realised. It is now possible to determine the material properties along directions which were so far not accessible. Thus, for example, the ratio of

  3. Decorporation of mixture of strontium and cesium isotopes with domestic mineral waters

    International Nuclear Information System (INIS)

    Slavov, S.; Filev, G.; Kiradzhiev, G.

    1990-01-01

    The possibilities of Bulgarian mineral waters to decorporate mixtures of strontium and cesium radioisotopes, simultaneous entering the body, were studied. A modified effect in respect to radioactive strontium was found. Modification of the effect of mixing two diferent types of mineral waters was not proven. No effect was found of potassium-containing mineral water on radioactive cesium kinetics. 1 tab., 7 refs

  4. Full-Scale and Bench-Scale Studies on the Removal of Strontium from Water (abstract)

    Science.gov (United States)

    Strontium (Sr) is a natural and commonly occurring alkaline earth metal which has an oxidation state of +2 under normal environmental conditions. Stable strontium is suspended in water and is dissolved after water runs through rocks and soil. It behaves very similar to calcium. G...

  5. Depression Mechanism of Strontium Ions in Bastnaesite Flotation with Salicylhydroxamic Acid as Collector

    Directory of Open Access Journals (Sweden)

    Shiming Cao

    2018-02-01

    Full Text Available Metal ions are widely present in flotation pulp. Metal ions change solution chemistry and mineral surface properties, consequently affecting mineral flotation. In this work, the effect of strontium ions on bastnaesite flotation with salicylhydroxamic acid (SHA was investigated by microflotation tests, contact angle measurements, zeta-potential measurements, and X-ray photoelectron spectroscopy (XPS analysis. Microflotation tests confirmed that the addition of strontium ions decreased bastnaesite floatability, compared with that in the absence of strontium ions. Contact angle measurements suggested that the pretreatment of strontium ions decreased SHA adsorption. Zeta potential measurements confirmed that the bastnaesite was depressed by the adsorption of positively charged strontium species, and the lower adsorption capacity of SHA onto the bastnaesite surfaces was obtained after modifying with strontium ions. XPS analysis demonstrated that strontium ions adsorbed onto the bastnaesite surfaces through the interaction between strontium ions and oxygen atoms of surface ≡ CeOH 0 groups. This occurrence hindered surface Ce sites which chelated with SHA and therefore, decreased bastnaesite floatability.

  6. Marking pike fry otoliths with alizarin complexone and strontium : an evaluation of methods

    DEFF Research Database (Denmark)

    Skov, Christian; Grønkjær, P.; Nielsen, C.

    2001-01-01

    Laboratory experiments demonstrated that both alizarin complexone and strontium are useful in mass marking of pike Esox lucius fry otoliths. Visual detection of alizarin complexone marks was considered more reliable than the quantitative analysis of strontium for differentiating marked and unmarked...

  7. Comparison of modification with strontium and the refining with antimony in A 356 aluminium alloys

    International Nuclear Information System (INIS)

    Fuoco, Ricardo; Correa, Edison Roberto; Correa, Alzira V.O.; Bocalini Junior, Mario

    1992-01-01

    Strontium and Antimony treated A356 aluminium alloy samples were metallographically characterized in the as cast and solution and aged conditions. Antimony treated alloy has shown slower spheroidizing kinetics of the Silicon particles during solution treatment, lower porosity level and higher tensile strength and elongation than Strontium treated one. (author)

  8. DETERMINATION OF STRONTIUM IONS IN WATERS WITH A HIGH CONTENT OF SODIUM IONS

    Directory of Open Access Journals (Sweden)

    Tatiana Mitina

    2015-06-01

    Full Text Available This paper reports on the influence of sodium ions on experimental determination of strontium ions concentration in waters with a high content of sodium ions by using emission flame photometry and atomic absorption spectroscopy. For the method of emission flame photometry it was shown that at a wavelength of 460.7 nm (spectral emission line of strontium the emission is linearly dependent on the concentration of sodium ions. The greatest impact of high concentrations of sodium ions on the result of determination the strontium ions concentration has been registered at low levels of strontium. The influence of nitric acid on the results is also discussed. In the case of using atomic absorption spectroscopy method no influence of sodium ions and nitric acid on the results of determination the strontium ions concentration was revealed. The metrological characteristics of both methods are evaluated.

  9. Application of empore TM strontium rad disks to the analysis of radiostrontium in environmental water samples

    International Nuclear Information System (INIS)

    Smith, L.L.; Seely, D.C.; Shannon, R.T.

    1996-01-01

    A solid phase extraction method for analyzing radioactive strontium in surface, ground, and drinking waters is presented. Strontium is simply isolated by pulling an acidified sample aliquot through an Empore TM strontium rad disk with a vacuum, and the disk is subsequently assayed for beta activity. The method is efficient, safe, reliable, and potentially field deployable. Sample preparation and counting source preparation may be condensed into a single procedure, thereby improving efficiency and eliminating many potential sources of laboratory error. Moreover, many of the hazardous chemicals associated with traditional strontium procedures are eliminated. Samples are easily batched, and a one-liter sample may be prepared with as little as 20 min of effort. For a one-liter aqueous sample, up to 3 mg of strontium can be retained by the disks. Chemical and radiometric interferences are discussed. (orig.)

  10. Study of the separation of strontium from solutions which imitate natural waters of increased mineralization

    International Nuclear Information System (INIS)

    Golub, A.M.; Voitko, I.N.; Glushchenko, L.V.; Mitrofanova, O.G.; Zyryanova, N.P.

    1976-01-01

    It has been shown by experiments on synthetically prepared solutions that it is possible to separate strontium and calcium by carbonate precipitation from the larger part of the magnesium accompanying them in natural high mineral waters. In this way the residual content of strontium is reduced to a value of 40-50 mg/liter and, under conditions of removing CO 2 from the solution, to 5-10 mg/liter. The high ionic strength of the solution prevented a more complete precipitation of strontium. Magnesium may be isolated from the filtrate after precipitation of the calcium-strontium mixture. The possibility has been shown of isolating strontium from the mixture of carbonates by means of pyrolysis at 1100-1200 0 and the selective solution of SrO in hot water

  11. Atomization of magnesium, strontium, barium and lead nitrates on surface of graphite atomizers

    International Nuclear Information System (INIS)

    Nagdaev, V.K.; Pupyshev, A.A.

    1982-01-01

    Modelling of the processes on graphite surface using differential-thermal analysis and graphite core with identification of decomposition products of magnesium, strontium, barium and lead nitrates by X-ray analysis has shown that carbon promotes the formation of strontium, barium and lead carbonates. The obtained temperatures of strontium and barium carbonate decomposition to oxides agree satisfactorily with calculation ones. Magnesium nitrate does not react with carbon. Formation of strontium and barium carbonates results in considerable slowing down of the process of gaseous oxide dissociation. Lead carbonate is unstable and rapidly decomposes to oxide with subsequent reduction to free metal. Formation of magnesium, strontium and barium free atoms is connected with appearance of gaseous oxides in analytical zone. Oxide and free metal lead are present on graphite surface simultaneously

  12. Characteristics of strontium-doped ZnO films on love wave filter applications

    International Nuclear Information System (INIS)

    Water, Walter; Yan, Y.-S.

    2007-01-01

    The effect of dopant concentrations in strontium-doped ZnO films on Love wave filter characteristics was investigated. Strontium-doped ZnO films with a c-axis preferred orientation were grown on ST-cut quartz by radio frequency magnetron sputtering. The crystalline structures and surface morphology of films were studied by X-ray diffraction, scanning electron microscopy and atomic force microscopy. The electromechanical coupling coefficient, dielectric constant, and temperature coefficient of frequency of filters were then determined using a network analyzer. A uniform crystalline structure and smooth surface of the ZnO films were obtained at the 1-2 mol% strontium dopant level. The electromechanical coupling coefficient of the 1 mol% strontium-doped ZnO film reaches a maximum of 0.61%, and the temperature coefficient of frequency declines to + 12.87 ppm/deg. C at a 1.5 mol% strontium dopant level

  13. Formation of barium strontium titanate powder by solid state reaction using different calcination temperatures

    International Nuclear Information System (INIS)

    Teoh Wah Tzu; Ahmad Fauzi Mohd Noor; Zainal Arifin Ahmad

    2002-01-01

    The unique electrical properties of large permittivity in Barium Strontium Titanate have been widely used to make capacitors; it can be produced by solid state reaction. In this study, the mixture of Barium Carbonate, Strontium Carbonate and Titanium Dioxide was calcined at 500 degree C, 1000 degree C, 1100 degree C , 1150 degree C, 1200 degree C, 1250 degree C and 1300 degree C. The results of the phases change in each stage were investigated via X ay Diffraction. The results show that the formation of Barium Strontium Titanate started at 1100 degree C with the presence of other phases. The mixture is fully reacted to form Barium Strontium Titanate at 1150 degree C. Only Barium Strontium Titanate was formed as the calcination temperature was set higher. (Author)

  14. Strontium and calcium accumulation in fish as affected by food composition

    International Nuclear Information System (INIS)

    Ophel, I.L.; Judd, J.M.

    1976-01-01

    Radioactive tracers ( 85 Sr and 47 Ca) were used to investigate the effects of food composition on the accumulation of strontium and calcium by fish and their discrimination between these two elements. The total amount of calcium assimilated by fish was the same for all experimental conditions. Calcium not obtainable from food was absorbed from the water, even when the water concentration was less than 10 mg Ca/l. The major discriminatory process occurred during direct (gill) uptake from water. Gut uptake provided least discrimination against strontium. Strontium content of fish was closely related to the Sr/Ca ratio in their food. Strontium assimilation was found to be a function of: the Sr/Ca ratios of food and water, the amounts of calcium derived from each source and the biological discrimination against strontium relative to calcium

  15. Baseline concentrations of strontium and 90Sr in seawater from the northern Gulf

    International Nuclear Information System (INIS)

    Uddin, S.; Al Ghadban, A.N.; Behbahani, M.

    2013-01-01

    Highlights: • This is the first baseline for strontium and 90 Sr from northern Gulf. • The total strontium concentration is much higher than reported for other oceans. • The Sr/salinity ratio correlates well with global averages. • High Sr might be due to increased salinity/CaCo 3 dissolution in acidifying Gulf waters. -- Abstract: Baseline concentration of strontium and Sr-90 in Gulf is presented. The strontium concentration is much higher than reported for other oceanic waters, while the Sr-90 concentration is low at 0.7–1.0 mBq l −1 , that represents the background level following nuclear tests and can be used as an effective tracer in case of any radioactive release in the region. The strontium concentration is primarily related to the increasing salinity off the Gulf coast

  16. Effect of iodide on glucose oxidation and 32P incorporation into phospholipids stimulated by different agents in dog thyroid slices

    International Nuclear Information System (INIS)

    Tseng, F.Y.; Rani, C.S.; Field, J.B.

    1989-01-01

    Since iodide (I-) inhibits TSH stimulation of cAMP formation, which mediates most of the effects of the hormone, it has been assumed that this accounts for the inhibitory action of iodide on the thyroid. However, TSH stimulation of 32P incorporation into phospholipids and stimulation of thyroid metabolism by other agonists, such as carbachol, phorbol esters, and ionophore A23187, is not cAMP mediated. The present studies examined the effect of iodide on stimulation of glucose oxidation and 32P incorporation into phospholipids by TSH and other agonists to determine if the inhibition of cAMP formation was responsible for the action of iodide. Preincubation of dog thyroid slices for 1 h with iodide (10(-4) M) inhibited TSH-, (Bu)2cAMP-, carbachol-, methylene blue-, 12-O-tetradecanoyl phorbol-13-acetate-, ionophore A23187-, prostaglandin E1-, and cholera toxin-stimulated glucose oxidation. I- also inhibited the stimulation by TSH, 12-O-tetradecanoyl phorbol-13-acetate, carbachol, and ionophore A23187 of 32P incorporation into phospholipids. The inhibition was similar whether iodide was added 2 h before or simultaneously with the agonist. I- itself sometimes stimulated basal glucose oxidation, but had no effect on basal 32P incorporation into phospholipids. The effects of iodide on basal and agonist-stimulated thyroid metabolism were blocked by methimazole (10(-3) M). When dog thyroid slices were preloaded with 32PO4 or [1-14C]glucose, the iodide inhibition of agonist stimulation disappeared, suggesting that the effect of iodide involves the transport process. In conclusion, I- inhibited stimulation of glucose oxidation and 32P incorporation into phospholipids by all agonists, indicating that the effect is independent of the cAMP system and that iodide autoregulation does not only involve this system. Oxidation and organification of iodide are necessary for the inhibition

  17. New Microporous Polymer Electrolyte Based on Polysiloxane Grafted with Imidazolium Iodide Moieties for DSSC

    Directory of Open Access Journals (Sweden)

    Yan Yang

    2011-01-01

    Full Text Available Two types of polysiloxane grafted with different ratio of imidazolium iodide moieties (IL-SiO2 have been synthesized to develop a micro-porous polymer electrolyte for quasi-solid-state dye-sensitized solar cells. The samples were characterized by 1HNMR, FT-IR spectrum, XRD, TEM and SEM, respectively. Moreover, the ionic conductivity of the electrolytes was measured by electrochemical workstation. Nanostructured polysiloxane containing imidazolium iodide showed excellent compatibility with organic solvent and polymer matrix for its ionic liquid characteristics. Increasing the proportion of imidazolium iodide moieties in polysiloxane improved the electrochemical behavior of the gel polymer electrolyte. A dye-sensitized solar cell with gel polymer electrolyte yielded an open-circuit voltage of 0.70 V, short-circuit current of 11.19 mA cm−2, and the conversion efficiency of 3.61% at 1 sun illumination.

  18. The distribution of radioiodine administrated to pregnant mice and the effect of non radioactive iodide

    International Nuclear Information System (INIS)

    Okui, Toyo; Kobayashi, Satoshi

    1987-01-01

    Radioiodine, 131 I, which has a high fission yield in the nuclear reactor, is easily taken into the human body, accumilating in the thyroid gland, when released to the environment. 131 I was administrated orally to pregnant mice, and its transportation to the tissues, particularly the fetus, was examined closely. And further, the non-radioactive iodide, i.e., KI, was administrated to see its radiation protection effect. The transportation of 131 I to the fetus is the second highest, following the thyroid gland in the mother mouse. This transportation to the fetus becomes the higher, the larger the gestation period at which the 131 I administration is made. The administration of the non-radioactive iodide has large radiation protection effect in the thyroid gland of the mother mouse and of the fetus. But, depending on its concentration, the non-radioactive iodide may conversely increase overall exposure of the fetus. (Mori, K.)

  19. Simultaneous detection of iodine and iodide on boron doped diamond electrodes.

    Science.gov (United States)

    Fierro, Stéphane; Comninellis, Christos; Einaga, Yasuaki

    2013-01-15

    Individual and simultaneous electrochemical detection of iodide and iodine has been performed via cyclic voltammetry on boron doped diamond (BDD) electrodes in a 1M NaClO(4) (pH 8) solution, representative of typical environmental water conditions. It is feasible to compute accurate calibration curve for both compounds using cyclic voltammetry measurements by determining the peak current intensities as a function of the concentration. A lower detection limit of about 20 μM was obtained for iodide and 10 μM for iodine. Based on the comparison between the peak current intensities reported during the oxidation of KI, it is probable that iodide (I(-)) is first oxidized in a single step to yield iodine (I(2)). The latter is further oxidized to obtain IO(3)(-). This technique, however, did not allow for a reasonably accurate detection of iodate (IO(3)(-)) on a BDD electrode. Copyright © 2012 Elsevier B.V. All rights reserved.

  20. Dosing of low-activity strontium 90 in human bone ashes - A method based on the quantitative precipitation of strontium nitrate

    International Nuclear Information System (INIS)

    Patti, Francois; Bullier, Denise

    1969-02-01

    The specific separation of strontium nitrate in bone ash samples by red fuming nitric acid requires a succession of precipitation varying in number according to the weight of ashes. The interest of the technique is to define the experimental conditions required for a reproducible quantitative separation of strontium. The operating process tested on over 1.500 samples allowed to obtain chemical yields of about 90 per cent. (authors) [fr

  1. Potentiometric sensing of iodide using polymeric membranes of microwave stabilized β-AgI

    International Nuclear Information System (INIS)

    James, Dhanya; Rao, T. Prasada

    2012-01-01

    Highlights: ► Stable β-phase was obtained by post MW irradiation of AgI precipitate. ► Constructed ISEby dispersing stable β-AgI crystals in polyvinyl chloride. ► Designed iodide ISE exhibited wide linear range and fast response. ► Highly selective with selectivity factors less than 10 −6 . ► Successfully applied to natural waters, table salt and human urine samples. - Abstract: A polymer based heterogeneous ion selective electrode (ISE) membrane was fabricated for the potentiometric sensing of iodide. The sensing element used for the preparation of the ISE membrane was microwave stabilized β-AgI. Because microwave energy was found to be beneficial for causing hysteresis at the phase transition temperature of AgI, an attempt has been made to prepare stable and conductive β-AgI crystals by post microwave irradiation under high pressure. A conventionally precipitated AgI based ISE was also fabricated for comparative studies. The β-AgI based ISE could respond to a wide range of iodide concentrations (1 × 10 −8 to 1 M) within 60 s with a detection limit of 10 nM. The ISE gave stable response to iodide ions in a pH range of 2.0–8.0 and was highly selective in the presence of various interfering ions. The performance of the proposed iodide ISE in the analysis of natural and seawater samples was encouraging, and the determination of iodide in table salt and human urine samples was explained using the developed sensor.

  2. Efficient photoreductive decomposition of N-nitrosodimethylamine by UV/iodide process

    International Nuclear Information System (INIS)

    Sun, Zhuyu; Zhang, Chaojie; Zhao, Xiaoyun; Chen, Jing; Zhou, Qi

    2017-01-01

    Highlights: • N-nitrosodimethylamine (NDMA) was effectively decomposed by UV/iodide process. • NDMA was completely converted to nontoxic end products by UV/iodide process. • The photoreductive process was mainly attributed to the attack of hydrated electrons on the photoexcited NDMA. • The elimination of toxic intermediates was greatly enhanced as pH increased, but its effect on NDMA removal was negligible. - Abstract: N-nitrosodimethylamine (NDMA) has aroused extensive concern as a disinfection byproduct due to its high toxicity and elevated concentration levels in water sources. This study investigates the photoreductive decomposition of NDMA by UV/iodide process. The results showed that this process is an effective strategy for the treatment of NDMA with 99.2% NDMA removed within 10 min. The depletion of NDMA by UV/iodide process obeyed pseudo-first-order kinetics with a rate constant (k_1) of 0.60 ± 0.03 min"−"1. Hydrated electrons (e_a_q"−) generated by the UV irradiation of iodide were proven to play a critical role. Dimethylamine (DMA) and nitrite (NO_2"−) were formed as the main intermediate products, which completely converted to formate (HCOO"−), ammonium (NH_4"+) and nitrogen (N_2). Therefore, not only the high efficiencies in NDMA destruction, but the elimination of toxic intermediates make UV/iodide process advantageous. A photoreduction mechanism was proposed: NDMA initially absorbed photons to a photoexcited state, and underwent a cleavage of N−NO bond under the attack of e_a_q"−. The solution pH had little impact on NDMA removal. However, alkaline conditions were more favorable for the elimination of DMA and NO_2"−, thus effectively reducing the secondary pollution.

  3. Efficient photoreductive decomposition of N-nitrosodimethylamine by UV/iodide process

    Energy Technology Data Exchange (ETDEWEB)

    Sun, Zhuyu; Zhang, Chaojie, E-mail: myrazh@tongji.edu.cn; Zhao, Xiaoyun; Chen, Jing; Zhou, Qi

    2017-05-05

    Highlights: • N-nitrosodimethylamine (NDMA) was effectively decomposed by UV/iodide process. • NDMA was completely converted to nontoxic end products by UV/iodide process. • The photoreductive process was mainly attributed to the attack of hydrated electrons on the photoexcited NDMA. • The elimination of toxic intermediates was greatly enhanced as pH increased, but its effect on NDMA removal was negligible. - Abstract: N-nitrosodimethylamine (NDMA) has aroused extensive concern as a disinfection byproduct due to its high toxicity and elevated concentration levels in water sources. This study investigates the photoreductive decomposition of NDMA by UV/iodide process. The results showed that this process is an effective strategy for the treatment of NDMA with 99.2% NDMA removed within 10 min. The depletion of NDMA by UV/iodide process obeyed pseudo-first-order kinetics with a rate constant (k{sub 1}) of 0.60 ± 0.03 min{sup −1}. Hydrated electrons (e{sub aq}{sup −}) generated by the UV irradiation of iodide were proven to play a critical role. Dimethylamine (DMA) and nitrite (NO{sub 2}{sup −}) were formed as the main intermediate products, which completely converted to formate (HCOO{sup −}), ammonium (NH{sub 4}{sup +}) and nitrogen (N{sub 2}). Therefore, not only the high efficiencies in NDMA destruction, but the elimination of toxic intermediates make UV/iodide process advantageous. A photoreduction mechanism was proposed: NDMA initially absorbed photons to a photoexcited state, and underwent a cleavage of N−NO bond under the attack of e{sub aq}{sup −}. The solution pH had little impact on NDMA removal. However, alkaline conditions were more favorable for the elimination of DMA and NO{sub 2}{sup −}, thus effectively reducing the secondary pollution.

  4. Multicompartmental model for iodide, thyroxine, and triiodothyronine metabolism in normal and spontaneously hyperthyroid cats

    Energy Technology Data Exchange (ETDEWEB)

    Hays, M.T.; Broome, M.R.; Turrel, J.M.

    1988-06-01

    A comprehensive multicompartmental kinetic model was developed to account for the distribution and metabolism of simultaneously injected radioactive iodide (iodide*), T3 (T3*), and T4 (T4*) in six normal and seven spontaneously hyperthyroid cats. Data from plasma samples (analyzed by HPLC), urine, feces, and thyroid accumulation were incorporated into the model. The submodels for iodide*, T3*, and T4* all included both a fast and a slow exchange compartment connecting with the plasma compartment. The best-fit iodide* model also included a delay compartment, presumed to be pooling of gastrosalivary secretions. This delay was 62% longer in the hyperthyroid cats than in the euthyroid cats. Unexpectedly, all of the exchange parameters for both T4 and T3 were significantly slowed in hyperthyroidism, possibly because the hyperthyroid cats were older. None of the plasma equivalent volumes of the exchange compartments of iodide*, T3*, or T4* was significantly different in the hyperthyroid cats, although the plasma equivalent volume of the fast T4 exchange compartments were reduced. Secretion of recycled T4* from the thyroid into the plasma T4* compartment was essential to model fit, but its quantity could not be uniquely identified in the absence of multiple thyroid data points. Thyroid secretion of T3* was not detectable. Comparing the fast and slow compartments, there was a shift of T4* deiodination into the fast exchange compartment in hyperthyroidism. Total body mean residence times (MRTs) of iodide* and T3* were not affected by hyperthyroidism, but mean T4* MRT was decreased 23%. Total fractional T4 to T3 conversion was unchanged in hyperthyroidism, although the amount of T3 produced by this route was increased nearly 5-fold because of higher concentrations of donor stable T4.

  5. Multicompartmental model for iodide, thyroxine, and triiodothyronine metabolism in normal and spontaneously hyperthyroid cats

    International Nuclear Information System (INIS)

    Hays, M.T.; Broome, M.R.; Turrel, J.M.

    1988-01-01

    A comprehensive multicompartmental kinetic model was developed to account for the distribution and metabolism of simultaneously injected radioactive iodide (iodide*), T3 (T3*), and T4 (T4*) in six normal and seven spontaneously hyperthyroid cats. Data from plasma samples (analyzed by HPLC), urine, feces, and thyroid accumulation were incorporated into the model. The submodels for iodide*, T3*, and T4* all included both a fast and a slow exchange compartment connecting with the plasma compartment. The best-fit iodide* model also included a delay compartment, presumed to be pooling of gastrosalivary secretions. This delay was 62% longer in the hyperthyroid cats than in the euthyroid cats. Unexpectedly, all of the exchange parameters for both T4 and T3 were significantly slowed in hyperthyroidism, possibly because the hyperthyroid cats were older. None of the plasma equivalent volumes of the exchange compartments of iodide*, T3*, or T4* was significantly different in the hyperthyroid cats, although the plasma equivalent volume of the fast T4 exchange compartments were reduced. Secretion of recycled T4* from the thyroid into the plasma T4* compartment was essential to model fit, but its quantity could not be uniquely identified in the absence of multiple thyroid data points. Thyroid secretion of T3* was not detectable. Comparing the fast and slow compartments, there was a shift of T4* deiodination into the fast exchange compartment in hyperthyroidism. Total body mean residence times (MRTs) of iodide* and T3* were not affected by hyperthyroidism, but mean T4* MRT was decreased 23%. Total fractional T4 to T3 conversion was unchanged in hyperthyroidism, although the amount of T3 produced by this route was increased nearly 5-fold because of higher concentrations of donor stable T4

  6. Determination of mineral radioactive strontium-{sup 90} in urines; Recherche du strontium mineral radioactif {sup 90}Sr dans les urines

    Energy Technology Data Exchange (ETDEWEB)

    Jeanmaire, L; Jammet, H; Bertrand, S [Commissariat a l' Energie Atomique, Saclay (France).Centre d' Etudes Nucleaires

    1959-07-01

    An analytical procedure for radioactive strontium in urine is described. As a first step, a precipitation of calcium oxalate performed on the urine, allows to detect the presence of various fission products and particularly of strontium which is carried by the precipitate. Strontium can then be selectively separated on ion exchange resins. By studying the growth curve of {beta} activity, it is possible to determine the activities which may be attributed to {sup 89}Sr and {sup 90}Sr respectively. (author) [French] Cet article decrit une technique de dosage du strontium radioactif dans les urines. Dans un premier stade, une precipitation d'oxalate de calcium effectuee sur l'urine permet de deceler la presence de differents produits de fission et en particulier du strontium qui est entraine sur ce precipite. Il est possible ensuite de separer selectivement le strontium au moyen de resines echangeuses d'ions. L'examen de le courbe de croissance de l'activite {beta} permet de determiner les activites dues respectivement a {sup 89}Sr et {sup 90}Sr. (auteur)

  7. Theoretical and experimental investigations on the behaviour of iodine during severe accidents: organic iodide, iodine/silver reaction, iodine/iron reaction. Pt. 4: organic iodide. Final report

    International Nuclear Information System (INIS)

    Hellmann, S.; Greger, G.U.; Funke, F.; Bleier, A.; Zeeh, W.

    1995-11-01

    Analysis of the consequences of severe accidents in nuclear power plants requires knowledge of the behaviour of radionuclides relevant from the radiological viewpoint. The role played by radioiodine is particularly important. In the current modelling of iodine behaviour the heterogeneous formation of organic iodide is not adequately taken into consideration owing to a lack of data or insufficient accuracy of data. This project is intended to eliminate some gaps in critical areas. This final report, part 4, describes the tests carried out in the two relevant areas - heterogeneous formation of organic coatings in the gas phase (containment atmosphere) - heterogeneous formation of organic iodide at organic coatings in aqueous phase (containment sump). Moreover, modelling suggestions how to include the resulting knowledge in the iodine accident behaviour code IMPAIR are given. (orig.) [de

  8. One column method to prepare 11C-labelled methyl iodide

    International Nuclear Information System (INIS)

    Kovacs, Z.; Priboczki, E.

    1999-01-01

    A new method in which the [ 11 C]methyl iodide is prepared on one alumina column is presented. A high specific surface alumina column, previously impregnated with lithium aluminium hydride solution, was used for direct trapping from the target gas and reduction into radiocomplex. The complex was then reacted on this column with HI to form [ 11 C]methyl iodide. The use of one alumina column, instead of a freezing trap, reaction vessel and separate unit for iodination, simplifies the apparatus, shortens the synthesis time and is well suitable for automation. (K.A.)

  9. Uptake of Iodide From Water in Atlantic Halibut Larvae (Hippoglossus Hippoglossus L.)

    DEFF Research Database (Denmark)

    Moren, Mari; Sloth, Jens Jørgen; Hamre, Kristin

    2008-01-01

    The natural diet of marine fish larvae, copepods, contain 60-350 mg I kg(-1), while live feed used in commercial hatcheries have iodine concentrations in the range of 1 mg kg(-1). Seawater is also considered to be an important source of iodine for marine fish. The question asked in this study is ......M. The uptake was partly blocked by perchlorate (ClO3-) which is a known inhibitor of the sodium iodide symporter. This indicates that the Atlantic halibut larvae accumulate iodide through both specific and non-specific uptake pathways....

  10. Optical power limiting and transmitting properties of cadmium iodide single crystals: Temperature dependence

    Energy Technology Data Exchange (ETDEWEB)

    Miah, M. Idrish, E-mail: m.miah@griffith.edu.a [Nanoscale Science and Technology Centre, Griffith University, Nathan, Brisbane, QLD 4111 (Australia)] [Biomolecular and Physical Sciences, Griffith University, Nathan, Brisbane, QLD 4111 (Australia)] [Department of Physics, University of Chittagong, Chittagong 4331 (Bangladesh)

    2009-09-14

    Optical limiting properties of the single crystals of cadmium iodide are investigated using ns laser pulses. It is found that the transmissions in the crystals increase with increasing temperature. However, they limit the transmissions at high input powers. The limiting power is found to be higher at higher temperature. From the measured transmission data, the photon absorption coefficients are estimated. The temperature dependence of the coefficients shows a decrease in magnitude with increasing temperature. This might be due to the temperature-dependent bandgap shift of the material. The results demonstrate that the cadmium iodide single crystals are promising materials for applications in optical power limiting devices.

  11. Optical power limiting and transmitting properties of cadmium iodide single crystals: Temperature dependence

    International Nuclear Information System (INIS)

    Miah, M. Idrish

    2009-01-01

    Optical limiting properties of the single crystals of cadmium iodide are investigated using ns laser pulses. It is found that the transmissions in the crystals increase with increasing temperature. However, they limit the transmissions at high input powers. The limiting power is found to be higher at higher temperature. From the measured transmission data, the photon absorption coefficients are estimated. The temperature dependence of the coefficients shows a decrease in magnitude with increasing temperature. This might be due to the temperature-dependent bandgap shift of the material. The results demonstrate that the cadmium iodide single crystals are promising materials for applications in optical power limiting devices.

  12. Study of adsorption properties of impregnated charcoal for airborne iodine and methyl iodide

    International Nuclear Information System (INIS)

    Qi-dong, L.; Sui-yuang, H.

    1985-01-01

    The adsorption characteristics of airborne radioiodine and methyl iodide on impregnated charcoal were investigated. The activated charcoal tested was made from home-made oil-palm shells, and KI and TEDA were used as impregnants. A new technique was used to plot the dynamic partial adsorption isotherm at challenge concentrations (concentration range of iodine: 1-20 ppm v/v). Some adsorption properties of the impregnated charcoal were estimated with the dynamic partial adsorption isotherm. The dependences of the adsorption capacity and penetration behavior for airborne iodine and methyl iodide on the ambient conditions (temperature, relative humidity, and superficial velocity) were studied

  13. Studying the iodine leaching from the compositions based on epoxide resin and lead iodide

    International Nuclear Information System (INIS)

    Kalinin, N.N.; Elizarova, A.N.

    1988-01-01

    When studying iodine leaching, the possibility to use solid compositions, produced by incorporation of dry powdered lead iodide and its aqueous suspension into epoxide resin for long-term immobilization of iodine-129 under conditions of monitored storage, is evaluated. Analysis of the results obtained has shown that leaching rate in the first 4 days has the maximum value and constitutes (4.2 - 2700.0) x 10 -6 cm/day. Then the process of leaching is determined by diffusion mechanism. For samples, prepared by wet lead iodide incorporation the rate of leaching is higher than that of the corresponding samples prepared by dry compound incorporation

  14. Tris(1,2-dimethoxyethane-κ2O,O′iodidocalcium iodide

    Directory of Open Access Journals (Sweden)

    Siou-Wei Ou

    2012-02-01

    Full Text Available In the title complex, [CaI(C4H10O23]I, the CaII atom is seven-coordinated by six O atoms from three 1,2-dimethoxyethane (DME ligands and one iodide anion in a distorted pentagonal–bipyramidal geometry. The I atom and one of the O atoms from a DME ligand lie in the axial positions while the other O atoms lie in the basal plane. The other iodide anion is outside the complex cation.

  15. 3.2. Antibacterial activity of ethynyl-piperidol polymers and their three-iodides

    International Nuclear Information System (INIS)

    Khalikov, D.Kh.

    2012-01-01

    The antibacterial activity of ethynyl-piperidol polymers and their three-iodides was studied. The antibacterial films based on iodine with copolymer N-vinyl pyrrolidone, methylmethacrylate and butyl acrylate were obtained. It was found that samples containing 9-10% of iodine in copolymer have the antiseptic properties. The antibacterial properties of three-iodides grafted nitrogen containing polymers with cellulose fibrous materials were considered. The membrane-active properties of homo- and copolymers of ethynyl piperidol derivatives were considered as well.

  16. Method for removing radioactive iodine and radioactive organic iodides from effluent gases

    International Nuclear Information System (INIS)

    1975-01-01

    A method and composition for removing radioactive and organic iodides from an 131 I-containing off-gas stream is provided. The composition for removal by adsorption is a ceramic material with a surface area of from about 5 m 2 /g to about 250 m 2 /g impregnated with a metallic salt. The method for removing the iodine or iodide is accomplished by passing the off-gas stream over the ceramic material impregnated with the metallic salt. It finds special application in air filters for nuclear power plants

  17. Sorption of microamount of colloidal silver iodide on hydrated iron(III) oxide

    International Nuclear Information System (INIS)

    Kepak, F.; Nova, J.

    1975-01-01

    Sorption of a microamount of colloidal silver iodide labelled with 131 I on hydrated iron/III/ oxide suspension was studied. The sorption dependence upon pH, sorbent amount, and inert electrolyte concentration has revealed that sorption of silver iodide reaches no more than 63%. The sorption lasted one hour during which the maximum value was reached. Desorption time was one hour, as well. Except for measuring the sorption dependence on pH, the sorption pH was 7.0, temperature 24+-2 0 C. (F.G.)

  18. Barium strontium titanate powders prepared by spray pyrolysis

    International Nuclear Information System (INIS)

    Brankovic, G.; Brankovic, Z.; Goes, M.S.; Paiva-Santos, C.O.; Cilense, M.; Varela, J.A.; Longo, E.

    2005-01-01

    Ultasonic spray pyrolysis (SP) has been investigated for the production of the barium strontium titanate (BST) powders from the polymeric precursors. The processing parameters, such as flux of aerosol and temperature profile inside the furnace, were optimized to obtain single phase BST. The powders were characterized by the methods of X-ray diffraction analysis, SEM, EDS and TEM. The obtained powders were submicronic, consisting of spherical, polycrystalline particles, with internal nanocrystalline structure. Crystallite size of 10 nm, calculated using Rietveld refinement, is in a good agreement with results of HRTEM

  19. Electrical properties and thermal expansion of strontium aluminates

    Energy Technology Data Exchange (ETDEWEB)

    Zakharchuk, K.V. [Department of Materials and Ceramic Engineering, CICECO, University of Aveiro, 3810-193 Aveiro (Portugal); Yaremchenko, A.A., E-mail: ayaremchenko@ua.pt [Department of Materials and Ceramic Engineering, CICECO, University of Aveiro, 3810-193 Aveiro (Portugal); Fagg, D.P. [TEMA-NRD, Mechanical Engineering Department, University of Aveiro, 3810-193 Aveiro (Portugal)

    2014-11-15

    Highlights: • Sr{sub 3}Al{sub 2}O{sub 6}, SrAl{sub 2}O{sub 4} and Sr{sub 4}Al{sub 14}O{sub 25} ceramics are semiconductors. • Electrical conductivity is as low as 10{sup −6}−4×10{sup −5} S/cm at 1273 K in dry air. • SrAl{sub 2}O{sub 4} is a mixed conductor with predominant ionic conductivity. • Sr{sub 3}Al{sub 2}O{sub 6} shows significant contribution of protonic transport in wet atmospheres. • Average TECs vary in the range (8.5–11.1)×10{sup −6} K{sup −1} and are p(O{sub 2})-independent. - Abstract: Strontium aluminate ceramics, including Sr{sub 3}Al{sub 2}O{sub 6}, SrAl{sub 2}O{sub 4} and Sr{sub 4}Al{sub 14}O{sub 25}, synthesized by glycine–nitrate combustion and sintered at 1773 K in air, were characterized by thermal analysis, dilatometry and electrical measurements in controlled atmospheres. All studied strontium aluminates are semiconductors with electrical conductivities as low as 10{sup −6}−4×10{sup −5} S/cm at 1273 K in dry air. Electrical measurements in controlled atmospheres in combination with ion transference number determination demonstrated that SrAl{sub 2}O{sub 4} is a mixed conductor with predominant ionic conductivity and increasing n-type and p-type electronic contributions under highly reducing and oxidizing conditions, respectively. While the behavior of electrical conductivity of Sr{sub 3}Al{sub 2}O{sub 6} in dry atmospheres was qualitatively similar to that of SrAl{sub 2}O{sub 4}, a significant increase of conductivity in wet atmospheres was attributed to a protonic contribution to electrical conduction, in correlation with thermogravimetric data and the tendency of this material to form a hydrogarnet at low temperatures. The average thermal expansion coefficients of strontium aluminates, (8.5–11.1)×10{sup −6} K{sup −1} at 333–1373 K, increase with increasing strontium content in the sequence Sr{sub 4}Al{sub 14}O{sub 25} < SrAl{sub 2}O{sub 4} < Sr{sub 3}Al{sub 2}O{sub 6} and are essentially

  20. Run-off of strontium with melting snow in spring

    International Nuclear Information System (INIS)

    Quenild, C.; Tveten, U.

    1986-09-01

    When assessing the consequences of atmospheric releases caused by a large reactor accident, one usually finds that the major contributions to the dose are via nutrition and from exposure to radiation from radioactive materials deposited on ground. The experiment described is concerned with run-off from agricultural surface which has been contaminated with strontiom while covered with snow. Migration experiments show a significant difference between summer and winter conditions. Roughly 54% of the strontium with which the experimental area was contaminated, ran off with the melt-water. Under winter conditions, portions of the contaminant will flow with the melt-water without coming in contact with the soil

  1. Determination of strontium-90 in the environmental samples at PINSTECH

    International Nuclear Information System (INIS)

    Perveen, N.; Aziz, A.

    1979-01-01

    Strontium-90 a bone seeking radionuclide and a long lived beta emitter is one of the toxic radionuclides detected in the environment arising mainly from the fall out from nuclear detonations. Its concentration in various environmental media such as air, precipitation, surface water, vegetables and other items of diet was measured. This report describes the method of collection, treatment and radiochemical analyses of environmental samples for the determination of Sr-90. The levels of Sr-90 concentration in these media are also recorded. (authors)

  2. Synthesis and thermal properties of strontium and calcium peroxides

    Science.gov (United States)

    Philipp, Warren H.; Kraft, Patricia A.

    1989-01-01

    A practical synthesis and a discussion of some chemical properties of pure strontium peroxide and calcium peroxide are presented. The general synthesis of these peroxides involves precipitation of their octahydrates by addition of H2O2 to aqueous ammoniacal Sr(NO3)2 or CaCl2. The octahydrates are converted to the anhydrous peroxides by various dehydration techniques. A new x-ray diffraction powder pattern for CaO2 x 8H2O is given from which lattice parameters a=6.212830 and c=11.0090 were calculated on the basis of the tetragonal crystal system.

  3. Spectroscopy of strontium Rydberg states using electromagnetically induced transparency

    International Nuclear Information System (INIS)

    Mauger, S; Millen, J; Jones, M P A

    2007-01-01

    We report on the all-optical detection of Rydberg states in an effusive atomic beam of strontium atoms using electromagnetically induced transparency (EIT). Using narrow-linewidth CW lasers we obtain an EIT linewidth of 5 MHz. To illustrate the high spectroscopic resolution offered by this method, we have measured isotope shifts of the 5s18d 1 D 2 and 5s19s 1 S 0 Rydberg states. This technique could be applied to high-resolution, non-destructive measurements of ultra-cold Rydberg gases and plasmas. (fast track communication)

  4. Strontium vanadate nanoribbons: Synthesis, characterization and detection of dopamine

    International Nuclear Information System (INIS)

    Zhou, Qing; Shao, Mingwang; Chen, Tao; Xu, Hongyan

    2010-01-01

    Large-scale, high-purity and uniform strontium vanadate (Sr 2 V 2 O 7 ) nanoribbons were easily synthesized via a hydrothermal process without any surfactants. The as-prepared products were up to hundreds of micrometers in length, 200-600 nm in width, and 20 nm in thickness. These nanomaterials were employed to modify glassy carbon electrode, which displayed excellent electrochemical sensitivity in detecting dopamine in the presence of ascorbic acid. A linear relationship between the concentrations of dopamine and its oxidation peak currents was obtained. The modified electrode exhibited high reproducibility and stability, which might be found potential application in the biosensors.

  5. Magnetite effect in radionuclide retention : cesium, strontium, molybdenum and selenium

    International Nuclear Information System (INIS)

    Rovira, M.; Casas, I.; Gimenez, J.; Clarens, F.; Pablo, J. de

    2004-01-01

    In this work we have investigated the interaction of magnetite with cesium, strontium, molybdenum and selenium, in the frame of radionuclide retention by canister corrosion products. For each radionuclide, the retention on magnetite has been studied as a function of pH and the mass/ volume ratio. The experimental results have been modeled by means of Surface Complexation Models (SCM), that constitute a tool that allows an approach to sorption mechanisms in a wide range of experimental conditions taking into account electrostatic interactions at the mineral-water interface.(Author)

  6. Experimental study of strontium sorption on fissure filling material

    Energy Technology Data Exchange (ETDEWEB)

    Eriksen, T E; Cui, Daqing [Royal Institute of Technology, Stockholm (Sweden). Dept. of Chemistry

    1994-12-01

    We have carried out a comparative study of sorption and desorption of strontium in groundwater on separated magnetic and size fractions of fissure filling material taken from natural fissures in granitic rock. Complete reversibility of the sorption process was demonstrated by identical Freundlich isotherms, isotopic exchangeability and pH dependence of the distribution coefficients Rd. The sorption was found to be strongly pH dependent in the range 3-11. The pH effect can be accommodated in the sorption model by considering the surface areas and surface charges of the minerals in the fissure filling material. 20 refs, 9 figs, 3 tabs.

  7. Experimental study of strontium sorption on fissure filling material

    International Nuclear Information System (INIS)

    Eriksen, T.E.; Cui, Daqing

    1994-12-01

    We have carried out a comparative study of sorption and desorption of strontium in groundwater on separated magnetic and size fractions of fissure filling material taken from natural fissures in granitic rock. Complete reversibility of the sorption process was demonstrated by identical Freundlich isotherms, isotopic exchangeability and pH dependence of the distribution coefficients Rd. The sorption was found to be strongly pH dependent in the range 3-11. The pH effect can be accommodated in the sorption model by considering the surface areas and surface charges of the minerals in the fissure filling material. 20 refs, 9 figs, 3 tabs

  8. Study on the Key Technology of High Purity Strontium Titanate Powder Synthesized from Oxalic Acid Co-sediment Precipitation

    Science.gov (United States)

    Bi, Xiaoguo; Dong, Yingnan; Li, Yingjie; Niu, Wei; Tang, Jian; Ding, Shuang; Li, Meiyang

    2017-09-01

    Oxalate coprecipitation is applied in this paper, high purity titanium tetrachloride, and after the purification of strontium chloride, match with a certain concentration of solution, oxalate and strontium chloride and titanium tetrachloride in 1.005:1.000 make strontium titanium mixture ratio, slowly under 60°C to join in oxalic acid solution, aging around 4 h, get oxygen titanium strontium oxalate (SrTiO(C2O4)2 • 4H2 ) precipitation, after washing, drying and other process made oxygen titanium strontium oxalate powder.

  9. 76 FR 16770 - Petition To Suspend and Cancel All Registrations for the Soil Fumigant Iodomethane (Methyl Iodide...

    Science.gov (United States)

    2011-03-25

    ... ENVIRONMENTAL PROTECTION AGENCY [EPA-HQ-OPP-2010-0541; FRL-8841-7] Petition To Suspend and Cancel... Earthjustice requesting that all uses of iodomethane (methyl iodide) be suspended and cancelled. The Agency is... uses of iodomethane (methyl iodide) be suspended and cancelled. The Agency is posting this petition for...

  10. Studying Equilibrium in the Chemical Reaction between Ferric and Iodide Ions in Solution Using a Simple and Inexpensive Approach

    Science.gov (United States)

    Nikolaychuk, Pavel Anatolyevich; Kuvaeva, Alyona Olegovna

    2016-01-01

    A laboratory experiment on the study of the chemical equilibrium based on the reaction between ferric and iodide ions in solution with the formation of ferrous ions, free iodine, and triiodide ions is developed. The total concentration of iodide and triiodide ions in the reaction mixture during the reaction is determined by the argentometric…

  11. Early effects of external gamma irradiation on iodide metabolism in rat thyroid

    International Nuclear Information System (INIS)

    Niatsetskaya, Z.; Nadolnik, L.

    2006-01-01

    Full text of publication follows: The exposure of the thyroid gland to therapeutic doses of external gamma irradiation is frequently associated with thyroid dysfunction. Although late irradiation effects are well documented, little is still known about the early functional alterations in the thyroid subjected to radiation therapy. The aim of this study was to examine the early effect of single external gamma irradiation on iodide metabolism in the thyroid. The Wistar female rats were irradiated using a 60 Co installation with a constant capacity of 0.64 Gy/min. The doses used were 0.25, 0.5, 1, 2, 5 Gy. The animals were sacrificed after 24 hours following the irradiation. T he thyroid organ culture was cultivated during 24 h and than was irradiated with a single dose of 5 Gy. The thyroid tissue was assayed for thyro-peroxidase activity and concentrations of total, free and protein -binding iodide. It was shown that the 0.25 Gy irradiation depressed thyroid iodide uptake, which was manifested in decreasing total iodide by 25%. The same tendency was observed after the 0.5 Gy irradiation. In the 1, 2, 5 Gy groups, the concentrations of total and free iodide increased by 26 -34% and 50-68%, accordingly. The level of protein-binding iodide in these groups was within the control values. However, protein-binding/total iodide and protein binding/ free iodide ratios decreased by 17 -41%, suggesting inhibition of thyroglobulin iodination. Thyro-peroxidase (T.P.O.) plays a key role in thyroid hormone synthesis by catalyzing both the iodination of thyroglobulin and the coupling some of the iodo-tyrosyl residues. After 24 hours on irradiation, a 31.5-54% dose-dependent inhibition of T.P.O. activity was shown in the 1, 2 and 5 Gy groups. The irradiation of the rat thyroid organ culture with a single dose of 5 Gy also led to significant inhibition of T.P.O. by 56.91% after 2 hours. We compared the enzyme kinetics of thyro-peroxidase from thyroid microsomal fraction control and

  12. Separation and determination of strontium-90 in burnout nuclear fuel

    International Nuclear Information System (INIS)

    Khermann, A.; Katsvinkel', I.

    1975-01-01

    Developed was a simple and selective chromatographic method of the separation of strontium-90, by the content of which it is possible to judge about the degree of nuclear fuel burnup. Among the studied ion exchangers for strontium separation the best results are exhibited by strongly acidic organic cationite, i.e. vofatite (on the base of styrene, 8%-divinylbenzene) in the H + form. Elution was performed by hydrochloric or oxalic acids. The method allows to achieve a high degree of Sr-90 purification from other fission products. Using the method the Sr-90 content was determined in burnup fuel of the fuel elements of EK-10 type. At the fuel storage period less than 2 years it becomes necessary to determine both Sr-90 and Sr-89. Determination of Sr-90 in the presence of Sr-89 was made by daughter product of Sr-90 - Y-90, which is separated in ion-exchange coloumn. Some other methods of Sr-90 determination in the presence of Sr-89 are noted

  13. Sorption of strontium on bentonites from Slovak deposits

    International Nuclear Information System (INIS)

    Kufcakova, J.; Galambos, M.; Rajc, P.

    2005-01-01

    Sorption on bentonite from different Slovak deposits / Jelsovy potok, Kopernica and Lieskove has been investigated under various experimental conditions, such as contact time, pH, sorbate concentrations, presence of complementary cation. The sorption of strontium from aqueous solutions was investigated using a radiometric determination of distribution coefficient, Kd. The individual solutions were labelled with radiotracer. Radiation stability has been investigated, the higher sorption parameters were observed for the irradiated bentonites /tab.l/ , which can be explained by the increase of specific surface and change of solubility of the irradiated samples of bentonite. The presence of complementary cations, Na + , K + , NH 4 + , Ca 2+ , Mg 2+ and Ba 2+ depresses the sorption of Sr on bentonite. In the case of bentonite Kopernica the effectiveness in reducing the sorption of strontium by cations followed the order K + 4 + + 2+ 2+ 2+ . Results indicate that the sorption of Sr + on bentonite will be affected by the presence of high concentrations of various salts in the waste water effluents. (author)

  14. Strontium doped injectable bone cement for potential drug delivery applications.

    Science.gov (United States)

    Taha, Ali; Akram, Muhammad; Jawad, Zaidoon; Alshemary, Ammar Z; Hussain, Rafaqat

    2017-11-01

    Microwave assisted wet precipitation method was used to synthesize calcium deficient strontium doped β-tricalcium phosphate (Sr-βTCP) with a chemical formula of Ca 2.96-x Sr x (PO 4 ) 2 . Sr-βTCP was reacted with monocalcium phosphate monohydrate [Ca(H 2 PO 4 ) 2 .H 2 O, MCPM] in presence of water to furnish corresponding Sr containing brushite cement (Sr-Brc). The samples were characterized by using X-ray diffractometry (XRD), Fourier transform infrared spectroscopy (FTIR) and field emission scanning electron microscopy (FESEM). Strontium content in the prepared samples was determined by using inductively coupled plasma optical emission spectrometry (ICP-OES). The effect of Sr 2+ ions on the structural, mechanical, setting properties and drug release of the cement is reported. Incorporation of Sr 2+ ions improved the injectability, setting time and mechanical properties of the Brc. The release profiles of antibiotics incorporated in Brc and Sr-Brc confirmed that the Sr incorporation into the Brc results in the efficient release of the antibiotics from the cement. Copyright © 2017 Elsevier B.V. All rights reserved.

  15. Physico-chemical studies for strontium sulfate radiation dosimeter

    Directory of Open Access Journals (Sweden)

    M.A.H. Rushdi

    2015-04-01

    Full Text Available Anhydrous strontium sulfate (SrSO4 has shown a promise candidate as a dosimeter for low dose applications producing unique EPR signals with γ-rays which it has a linear response relationship (r2 = 0.999 in the range of 1–100 Gy. The present study extended to evaluate the properties of strontium sulfate dosimeter in intermediate dose range of technology applications. It was observed that the intensity of the EPR signal at g = 2.01081 increases with a 3rd polynomial function in the range of 0.10–15 kGy. In addition, the radical (SO4− provides a stable signal with a good reproducibility (0.107%. Other physics characteristic including the collision of mass stopping power dependence of the system and the effect of atomic number in different energy regions were investigated. The uncertainty budget for high doses has obtained from the measurement with value of 3.57% at 2σ confidence level.

  16. Analysis of leachants from strontium chlorapatite glass ceramics

    International Nuclear Information System (INIS)

    Vijayalakshmi, S.; Ushalakshmi, K.; Annapoorani, S.; Sriram, S.; Uma Maheshwari, R.; Deivanayaki, R.; Sekar, J.K.; Sankaran, K.

    2013-01-01

    Strontium chlorapatite glass ceramics is being tried out as one of the candidate matrices for immobilizing pyrochemical salt waste produced in the nuclear industry. To find-out the suitability of such material for immobilising the waste, leaching of various constituents of the ceramics in water is required. Therefore, in Chemistry Group of IGCAR experiments are being carried out with simulated salt waste (chlorides of Li, Na, K, Cs, Ba, Nd and Ce) of pyrochemical reprocessing method for studying the utilisation of strontium chlorapatite glass ceramics towards the immobilization of radioactive waste. Leaching behaviour study requires the determination of alkali, alkaline earth and rare earth elements in the leachant solutions of the glass ceramic material. Apart from cations, leaching study of anions especially chloride is required as the chloride salts are used in pyrochemical experiments. Considering the good sensitivity of alkali elements in Flame-AES method, all the alkali elements were determined by flame-AES. Ba, Sr and rare earth elements in the leachant solutions were determined using ICP-OES. Chloride was determined using ISE and IC. Standardisation of instrumental techniques and the application of various techniques for the sample analysis will be discussed in the paper. (author)

  17. Structure and thermodynamic properties of molten strontium chloride

    International Nuclear Information System (INIS)

    Pastore, G.; Ballone, P.; Tosi, M.P.; Trieste Univ.

    1985-05-01

    Self-consistent calculations of pair distribution functions and thermodynamic properties are presented for a pair-potentials model of molten strontium chloride. The calculations extend to a strongly asymmetric ionic liquid an earlier assessment of bridge diagrams in a modified hypernetted chain approach to the liquid structure of alkali halides. Good agreement is found with computer simulation data obtained by de Leeuw with the same set of pair potentials, showing that the present approach incorporates genuine general features of liquid structure theory for multicomponent liquids with strong relative ordering of the component species. It is further shown that the strong correlations between the divalent cations, both in the model and in real molten strontium chloride, can be approximately reproduced on the basis of a simple one-component-plasma model, provided that dielectric screening is allowed for in the real liquid. This allows us to tentatively attribute the significant level of disagreement between a pair potentials model of this liquid and the neutron diffraction data of McGreevy and Mitchell to many-body distortions of the electronic shells of the ions. (author)

  18. Seawater strontium isotopes at the Cretaceous-Tertiary boundary

    Science.gov (United States)

    Macdougall, J. D.; Martin, E.

    1988-01-01

    Anomalously high values of Seawater Sr-87/Sr-86 near the Cretaceous-Tertiary (K-T) boundary have been reported. However, few of the data from the literature are from a single continuous section, and perhaps the most complete study of the boundary region, from a shallow marine limestone sequence in Alabama, showed elevated Sr-87/Sr-86 but no pronounced spike. Thus, in order to investigate the cause of the change in strontium isotopic composition, it is important to determine the exact nature and magnitude of the increase by studying in detail continuous sections through the boundary. If there is indeed a Sr isotope spike at the K-T boundary, it requires the addition of a large amount of radiogenic Sr to the oceans over a short time period, a phenomenon that may be linked to other large-scale environmental disturbances which occurred at that time. In order to address this question, a high-resolution strontium isotope study of foraminifera from three Deep Sea Drilling Project (DSDP) cores which recovered the K-T boundary section: Site 356 in the South Atlantic, Site 384 in the North Atlantic and Site 577 from the Shatsky Rise in the Pacific was initiated. The isotope measurements are being made on either single or small numbers of forams carefully picked and identified and in most cases examined by SEM before analysis. Because this work is not yet complete, conclusions drawn here must be viewed as tentative. They are briefly discussed.

  19. Textured strontium titanate layers on platinum by atomic layer deposition

    International Nuclear Information System (INIS)

    Blomberg, T.; Anttila, J.; Haukka, S.; Tuominen, M.; Lukosius, M.; Wenger, Ch.; Saukkonen, T.

    2012-01-01

    Formation of textured strontium titanate (STO) layers with large lateral grain size (0.2–1 μm) and low X-ray reflectivity roughness (∼ 1.36 nm) on Pt electrodes by industry proven atomic layer deposition (ALD) method is demonstrated. Sr(t-Bu 3 Cp) 2 , Ti(OMe) 4 and O 3 precursors at 250 °C were used to deposit Sr rich STO on Pt/Ti/SiO 2 /Si ∅200 mm substrates. After crystallization post deposition annealing at 600 °C in air, most of the STO grains showed a preferential orientation of the {001} plane parallel to the substrate surface, although other orientations were also present. Cross sectional and plan view transmission electron microscopy and electron diffraction analysis revealed more than an order of magnitude larger lateral grain sizes for the STO compared to the underlying multicrystalline {111} oriented platinum electrode. The combination of platinum bottom electrodes with ALD STO(O 3 ) shows a promising path towards the formation of single oriented STO film. - Highlights: ► Amorphous strontium titanate (STO) on platinum formed a textured film after annealing. ► Single crystal domains in 60 nm STO film were 0.2–1 μm wide. ► Most STO grains were {001} oriented.

  20. Study of interaction of the bacterium cupriavidus metallidurans with strontium

    International Nuclear Information System (INIS)

    Boussiga, Rim

    2010-01-01

    Cupriavidus metallidurans strain Ch 34 (previously known as Ralstonia metallidurans, Ralstonia eutropha, and Alcaligenes eutrophus) is an ideal subject to study heavy metal disturbance of cellular processes. Moreover, the capacity of C. metallidurans Ch 34 for in situ bioremediation was assessed and proved to be feasible on pilot scale. In this work, the molecular and physiological response to strontium cations (Sr 2+ ) by C.metallidurans Ch 34 was studied. Results showed that C. metallidurans Ch 34 resisted to high concentrations of Sr (120 m M) and that this resistance is not linked to the presence of its 2 large plasmid pMOL30 or pMOL28. During this study, a tctCBA-dependent tripartite tricarboxylate transport (TTT) system in strain Ch 34 was discovered. Transmission Electron Microscopy (TEM) observation of C.metallidurans challenged with strontium confirms the precipitation of Sr 2+ ) directly onto the surface of cells, inside and in the microenvironment around the cells. These results highlight the potential of C. metalliduras Ch 34 to endure environmental extremes and suggest that in situ bioremediation of Sr-containing waste with Ch 34 might be feasible.

  1. Rapid method for the radioactive strontium determination in natural samples; Brza metoda za odredjivanje radioaktivnog stroncija u prirodnim uzorcima

    Energy Technology Data Exchange (ETDEWEB)

    Grahek, Z; Kosutic, K; Lulic, S [Rudjer Boskovic Institute, Zagreb (Croatia)

    1997-12-31

    Radioactive strontium isotopes belong to the group of isotopes that are very dangerous for human health. Therefore radioactive strontium is regularly determined in natural samples. When determining strontium isotopes in natural samples, it is necessary to isolate strontium from the sample because strontium isotopes are pure {beta}-emitters. As natural samples contain much more calcium and sodium than strontium it is necessary to isolate a small quantity of strontium from large sample with simultaneous separation of calcium and other interfering elements. For this purposes an elegant method based on ion exchange chromatography has been developed. Namely, examinations with model system have shown that strontium may be separated from calcium on the column filled with anion exchanger and the mixture of the methanol and nitric acid as eluent. It was also shown that yttrium does not separate from strontium but elutes almost simultaneously with it. Yttrium may be separated from strontium on the column filled with cation exchanger DOWEX 50X8 and nitric acid as eluent. According to the above examinations, the procedure of isolation of strontium and yttrium from natural sample has been created (on assumption that {sup 90}Sr and {sup 90}Y in secular equilibrium in sample). Strontium and yttrium have been isolated from natural sample (standard IAEA A-7) on the column filled with the exchanger AMBERLITE CG-400 and the mixture of methanol and nitric acid as eluent. Strontium and yttrium have been separated on the column with cation exchanger. {sup 90}Sr has been determined through {sup 90}Y by counting the solid yttrium oxalate immediately upon isolation and separation from strontium. {sup 90}Sr has also been determined by counting {sup 90}Sr-{sup 90}Y in secular equilibrium after 15 days. The obtained results of determination of {sup 90}Sr through {sup 90}Y and through secular equilibrium {sup 90}Sr-{sup 90}Y correspond to the declared values of standard. (author). 2 figs., 1

  2. Hydrologic inferences from strontium isotopes in pore water from the unsaturated zone at Yucca Mountain, Nevada

    International Nuclear Information System (INIS)

    Marshall, B.D.; Futa, K.; Peterman, Z.E.

    1997-01-01

    Calcite is ubiquitous at Yucca Mountain, occurring in the soils and as fracture and cavity coatings within the volcanic tuff section. Strontium is a trace element in calcite, generally at the tens to hundreds of ppm level. Because calcite contains very little rubidium and the half-life of the 87 Rb parent is billions of years, the 87 Sr/ 86 Sr ratios of the calcite record the ratio in the water from which the calcite precipitated. Dissolution and reprecipitation does not alter these compositions so that, in the absence of other sources of strontium, one would expect the strontium ratios along a flow path to preserve variations inherited from strontium in the soil zone. Strontium isotope compositions of calcites from various settings in the Yucca Mountain region have contributed to the understanding of the unsaturated zone (UZ), especially in distinguishing unsaturated zone calcite from saturated zone calcite. Different populations of calcite have been compared, either to group them together or distinguish them from each other in terms of their strontium isotope compositions. Ground water and perched water have also been analyzed; this paper presents strontium isotope data obtained on pore water

  3. Preparation of strontium hexaferrite magnets from celestite and blue dust by mechanochemical route

    Directory of Open Access Journals (Sweden)

    Tiwary R.K.

    2008-01-01

    Full Text Available In the present investigation celestite (natural ore of strontium and blue dust (iron ore fines have been used for the preparation of strontium hexaferrite powder. The mechanical alloying process has been adopted to prepare strontium hexaferrite powder. The celestite after chemical upradation and physically upgraded blue dust alongwith sodium carbonate was taken for the preparation of strontium hexaferrite in this experiment. The high-energy planetary ball mill with tungsten carbide jar and ball was used to prepare strontium hexaferrite powder. A long time of ball milling for different duration has led to displacement solid-state reaction. At the end of each experiment the product was washed thoroughly and dried. The X-ray diffaction study after annealing shows the development of single-phase strontium hexaferrite after 40 hrs. of milling. The resultant powder was compacted under magnetic field and sintered to prepare the magnet after annealing the ferrite powder. The magnetic properties were measured by Pulse magneto meter. The moderate value of coercivity, remanence and energy product were observed in this sintered magnet. The work illustrates the feasibility to prepare strontium hexaferrite magnetic powders directly from natural ores which can reduce the total cost of production as compared to conventional method.

  4. Urinary strontium and the risk of breast cancer: A case-control study in Guangzhou, China

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Li-Juan [The School of Public Health, Sun Yat-sen University, 74 Zhongshan 2nd Rd, Guangzhou 510080 (China); Tang, Lu-Ying [The School of Public Health, Sun Yat-sen University, 74 Zhongshan 2nd Rd, Guangzhou 510080 (China); The Third Affiliated Hospital, Sun Yat-sen University, Guangzhou 510630 (China); He, Jian-Rong [The School of Public Health, Sun Yat-sen University, 74 Zhongshan 2nd Rd, Guangzhou 510080 (China); Guangzhou Women and Children' s Medical Center, Guangzhou 510623 (China); Su, Yi; Cen, Yu-Ling; Yu, Dan-Dan [The School of Public Health, Sun Yat-sen University, 74 Zhongshan 2nd Rd, Guangzhou 510080 (China); Wu, Bang-Hua [The Guangdong Prevention and Treatment Center for Occupational Diseases, Guangzhou 510300 (China); Lin, Ying [The First Affiliated Hospital, Sun Yat-sen University, Guangzhou 510080 (China); Chen, Wei-Qing [The School of Public Health, Sun Yat-sen University, 74 Zhongshan 2nd Rd, Guangzhou 510080 (China); Song, Er-Wei, E-mail: songerwei02@yahoo.com.cn [The Second Affiliated Hospital, Sun Yat-sen University, 107 Yanjiang West, Guangzhou 510120 (China); Ren, Ze-Fang, E-mail: renzef@mail.sysu.edu.cn [The School of Public Health, Sun Yat-sen University, 74 Zhongshan 2nd Rd, Guangzhou 510080 (China)

    2012-01-15

    Strontium has been widely used in industries like electronic and pharmacy. It has a carcinogenic potential, however, and no study has been conducted to evaluate its effects on cancer risk. The aim of this study was to explore the possible association between strontium and breast cancer risk in a case-control study including 240 incident invasive breast cancer patients and 246 age-matched controls. We measured the urinary concentrations of strontium by inductively coupled plasma mass spectrometry, and conducted face-to-face interviews to obtain information on potential breast cancer risk factors. Multivariable analysis was used to estimate the association. Creatinine-adjusted levels [median (25th, 75th) {mu}g/g] of strontium were 155.59 (99.05, 230.70) in the breast cancer patients and 119.62 (81.97, 163.76) in the controls. Women in the highest tertile of strontium showed 124% increased risk of breast cancer, when compared with those in the lowest tertile after adjustment for the potential risk factors [OR (95% CI): 2.24 (1.42-3.81)]. This association was particularly strong for HER2 positive breast cancer [OR (95% CI): 10.92 (3.53-33.77)], and only occurred among premenopausal women. These results suggest a potential role of strontium in the development of breast cancer and urge further studies on the environmental contamination and the physiological and pathological mechanisms of strontium.

  5. Strontium isotope geochemistry of soil and playa a deposits near Yucca Mountain, Nevada

    International Nuclear Information System (INIS)

    Marshall, B.D.; Mahan, S.A.

    1994-01-01

    The isotopic composition of strontium contained in the carbonate fractions of soils provides an excellent tracer which can be used to test models for their origin. This paper reports data on surface coatings and cements, eolian sediments, playas and alluvial fan soils which help to constrain a model for formation of the extensive calcretes and fault infilling in the Yucca Mountain region. The playas contain carbonate with a wide range of strontium compositions; further work will be required to fully understand their possible contributions to the pedogenic carbonate system. Soils from an alluvial fan to the west of Yucca Mountain show that only small amounts of strontium are derived from weathering of silicate detritus. However, calcretes from a fan draining a carbonate terrane have strontium compositions dominated locally by the limestone strontium component. Although much evidence points to an eolian source for at least some of the strontium in the pedogenic carbonates near Yucca Mountain, an additional component or past variation of strontium composition in the eolian source is required to model the pedogenic carbonate system

  6. Organic composite-mediated surface coating of human acellular bone matrix with strontium.

    Science.gov (United States)

    Huang, Yi-Zhou; Wang, Jing-Jing; Huang, Yong-Can; Wu, Cheng-Guang; Zhang, Yi; Zhang, Chao-Liang; Bai, Lin; Xie, Hui-Qi; Li, Zhao-Yang; Deng, Li

    2018-03-01

    Acellular bone matrix (ACBM) provides an osteoconductive scaffold for bone repair, but its osteoinductivity is poor. Strontium (Sr) improves the osteoinductivity of bone implants. In this study, we developed an organic composite-mediated strontium coating strategy for ACBM scaffolds by using the ion chelating ability of carboxymethyl cellulose (CMC) and the surface adhesion ability of dopamine (DOPA). The organic coating composite, termed the CMC-DOPA-Sr composite, was synthesized under a mild condition, and its chemical structure and strontium ion chelating ability were then determined. After surface decoration, the physicochemical properties of the strontium-coated ACBM (ACBM-Sr) scaffolds were characterized, and their biocompatibility and osteoinductivity were determined in vitro and in vivo. The results showed that the CMC-DOPA-Sr composite facilitated strontium coating on the surface of ACBM scaffolds. The ACBM-Sr scaffolds possessed a sustained strontium ion release profile, exhibited good cytocompatibility, and enhanced the osteogenic differentiation of mesenchymal stem cells in vitro. Furthermore, the ACBM-Sr scaffolds showed good histocompatibility after subcutaneous implantation in nude mice. Taken together, this study provided a simple and mild strategy to realize strontium coating for ACBM scaffolds, which resulted in good biocompatibility and improved osteoinductivity. Copyright © 2017 Elsevier B.V. All rights reserved.

  7. Radioiodine source term and its potential impact on the use of potassium iodide

    International Nuclear Information System (INIS)

    Malinauskas, A.P.

    1982-01-01

    Information is presented concerning chemical forms of fission product iodine in the primary circuit; chemical forms of fission product iodine in the containment building; summary of iodine chemistry in light water reactor accidents; and impact of the radiodine source term on the potassium iodide issue

  8. Distribution of bromine in mixed iodide-bromide organolead perovskites and its impact on photovoltaic performance

    NARCIS (Netherlands)

    Zhou, Yang; Wang, Feng; Fang, Hong-Hua; Loi, Maria Antonietta; Xie, Fang-Yan; Zhao, Ni; Wong, Ching-Ping

    2016-01-01

    Mixed iodide-bromide (I-Br) organolead perovskites are of great interest for both single junction and tandem solar cells since the optical bandgap of the materials can be tuned by varying the bromine to iodine ratio. Yet, it remains unclear how bromine incorporation modifies the properties of the

  9. Expedient Method for Samarium(II) Iodide Preparation Utilizing a Flow Approach

    Czech Academy of Sciences Publication Activity Database

    Voltrová, Svatava; Šrogl, Jiří

    2013-01-01

    Roč. 24, č. 3 (2013), s. 394-396 ISSN 0936-5214 R&D Projects: GA MŠk LH12013 Institutional support: RVO:61388963 Keywords : flow * samarium * iodide * reduction Subject RIV: CC - Organic Chemistry Impact factor: 2.463, year: 2013

  10. A portable multi-syringe flow system for spectrofluorimetric determination of iodide in seawater.

    Science.gov (United States)

    Frizzarin, Rejane M; Aguado, Enrique; Portugal, Lindomar A; Moreno, Daniel; Estela, José M; Rocha, Fábio R P; Cerdà, Victor

    2015-11-01

    A miniaturized analyzer encompassing a poly(methyl methacrylate) chip with integrated spectrofluorimetric detection and solutions propelling by a multi-syringe module is proposed. Iodide was determined through its catalytic effect on the reaction between Ce(IV) and As(III). Matrix isopotential synchronous fluorescence was explored to set the excitation and emission wavelengths. A two-level full factorial design allowed to evaluate the significance of variables (Ce(IV), As(III) and H2SO4 concentrations) and their interaction effects in the experimental domain. A Doehlert Matrix was applied to identify the critical values. The optimized procedure showed a linear response from 1 to 100 μg L(-1) (S=53.7+2.61C, in which S is the net fluorescence and C is iodide concentration in μg L(-1)). Detection limit, coefficient of variation (n=6) and sampling rate were estimated at 0.3 μg L(-1), 0.8% and 20 h(-1), respectively. Recoveries within 90-117% were estimated for iodide spiked to seawater samples. The proposed procedure stands out because of the portability, robustness, and simplicity for in-field analysis of iodide in seawater. Copyright © 2015 Elsevier B.V. All rights reserved.

  11. Electron stimulated reactions of methyl iodide coadsorbed with amorphous solid water

    International Nuclear Information System (INIS)

    Perry, C. C.; Faradzhev, N. S.; Madey, T. E.; Fairbrother, D. H.

    2007-01-01

    The electron stimulated reactions of methyl iodide (MeI) adsorbed on and suspended within amorphous solid water (ice) were studied using a combination of postirradiation temperature programmed desorption and reflection absorption infrared spectroscopy. For MeI adsorbed on top of amorphous solid water (ice), electron beam irradiation is responsible for both structural and chemical transformations within the overlayer. Electron stimulated reactions of MeI result principally in the formation of methyl radicals and solvated iodide anions. The cross section for electron stimulated decomposition of MeI is comparable to the gas phase value and is only weakly dependent upon the local environment. For both adsorbed MeI and suspended MeI, reactions of methyl radicals within MeI clusters lead to the formation of ethane, ethyl iodide, and diiodomethane. In contrast, reactions between the products of methyl iodide and water dissociation are responsible for the formation of methanol and carbon dioxide. Methane, formed as a result of reactions between methyl radicals and either parent MeI molecules or hydrogen atoms, is also observed. The product distribution is found to depend on the film's initial chemical composition as well as the electron fluence. Results from this study highlight the similarities in the carbon-containing products formed when monohalomethanes coadsorbed with amorphous solid water are irradiated by either electrons or photons

  12. Continuous monitoring of methyl iodide purity and content in the gas feeding the trapping pilot plant

    International Nuclear Information System (INIS)

    Charrier, G.

    1988-01-01

    An analysis method is developed for inspection of solid traps for gaseous iodine. Methyl iodide injected in the traps is determined by gas chromatography. Contents of 50 ppm in volume are measured. Labelling with iodine 123 allows a better sensitivity, 4 refs, 5 figs, 6 tables [fr

  13. The sodium iodide symporter (NIS) and potential regulators in normal, benign and malignant human breast tissue.

    LENUS (Irish Health Repository)

    Ryan, James

    2011-01-01

    The presence, relevance and regulation of the Sodium Iodide Symporter (NIS) in human mammary tissue remains poorly understood. This study aimed to quantify relative expression of NIS and putative regulators in human breast tissue, with relationships observed further investigated in vitro.

  14. Silver iodide reduction in aqueous solution: application to iodine enhanced separation during spent nuclear fuels reprocessing

    International Nuclear Information System (INIS)

    Badie, Jerome

    2002-01-01

    Silver iodide is a key-compound in nuclear chemistry either in accidental conditions or during the reprocessing of spent nuclear fuel. In that case, the major part of iodine is released in molecular form into the gaseous phase at the time of dissolution in nitric acid. In French reprocessing plants, iodine is trapped in the dissolver off-gas treatment unit by two successive steps: the first consists in absorption by scrubbing with a caustic soda solution and in the second, residual iodine is removed from the gaseous stream before the stack by chemisorption on mineral porous traps made up of beds of amorphous silica or alumina porous balls impregnated with silver nitrate. Reactions of iodine species with the impregnant are assumed to lead to silver iodide and silver iodate. Enhanced separation policy would make necessary to recover iodine from the filters by silver iodide dissolution during a reducing treatment. After a brief silver-iodine chemical bibliographic review, the possible reagents listed in the literature were studied. The choice has been made to use ascorbic acid and hydroxylamine. An experimental work on silver iodide reduction by this two compounds allowed us to determinate reaction products, stoichiometry and kinetics parameters. Finally, the process has been initiated on stable iodine loaded filters samples. (author) [fr

  15. Photoexcitation dynamics in solution-processed formamidinium lead iodide perovskite thin films for solar cell applications

    NARCIS (Netherlands)

    Fang, Hong-Hua; Wang, Feng; Adjokatse, Sampson; Zhao, Ni; Even, Jacky; Loi, Maria Antonietta

    Formamidinium lead iodide (FAPbI(3)) is a newly developed hybrid perovskite that potentially can be used in high-efficiency solution-processed solar cells. Here, the temperature-dependent dynamic optical properties of three types of FAPbI(3) perovskite films (fabricated using three different

  16. Gamma-ray radiolysis of methyl iodide in air, in presence of water vapor

    International Nuclear Information System (INIS)

    Aubert, F.

    2002-03-01

    This work aims at modelling the processes involved in gamma-radiolysis of methyl iodide diluted in air in presence of steam. It is to determine quantitative and qualitative information, to quantify the importance of the organic iodides destruction in case of a nuclear reactor accident. The main data for radiochemistry and iodine compounds (I x O y and INO x ) formation were reviewed and analysed. Literature data about air products radiolysis reactivity towards I 2 and CH 3 I were used to develop a mechanistic model for methyl iodide destruction in the gas phase under gamma irradiation. An ab initio study was realised for a better understanding of atomic nitrogen ( 4 S and 2 D) reactivity towards CH 3 I. The model was tested on the available experimental data and constitute a way to investigate the main processus involved in methyl iodide destruction. For the low CH 3 I concentrations, about 10 -7 - 10 -8 mol.dm -3 , N and e - are mainly responsible for the destruction. I 2 O 4 (highest iodine oxide in the model) and IONO 2 are the main resulting iodinated' compounds. (author)

  17. Iodide-induced thyrotoxicosis in a thyroidectomized patient with metastatic thyroid carcinoma

    Energy Technology Data Exchange (ETDEWEB)

    Yoshinari, M.; Tokuyama, T.; Okamura, K.; Sato, K.; Kusuda, K.; Fujishima, M.

    1988-04-15

    An unusual case of iodide-induced thyrotoxicosis is documented in this article. The patient was a 64-year-old euthyroid man with acromegaly. He also had multiple follicular and papillary thyroid carcinomas with a metastatic lesion in the lumbar vertebrae. After a total thyroidectomy, he became slightly hypothyroid, and the lumbar lesion began to incorporate /sup 131/I by scintigraphy. When an iodine-containing contrast medium happened to be injected, a transient increase of serum thyroid hormone level was observed. After complete thyroid ablation with 83 mCi of /sup 131/I, the oral administration of 100 mg of potassium iodide for 7 days induced a prominent increase of serum thyroid hormone level. These findings indicated that the metastatic thyroid carcinoma could produce excess thyroid hormone insofar as a sufficient amount of iodide was given. Although this is the first report of such a case, iodide-induced thyrotoxicosis may not be rare in patients with thyroid carcinomas because the Wolff-Chaikoff effect is thought to be lost, and the organic iodinating activity and lysosomal protease activity are well-preserved.

  18. The Role of Connectivity on Electronic Properties of Lead Iodide Perovskite-Derived Compounds

    NARCIS (Netherlands)

    Kamminga, Machteld E; De Wijs, Gilles; Havenith, Remco W A; Blake, Graeme R; Palstra, Thomas T M

    2017-01-01

    We use a layered solution crystal growth method to synthesize high-quality single crystals of two different benzylammonium lead iodide perovskite-like organic/inorganic hybrids. The well-known (C6H5CH2NH3)(2)PbI4 phase is obtained in the form of bright orange platelets, with a structure comprised of

  19. Monochloramine determination using NN diethyl-p-phenylene-diamine. Influence of iodide traces

    International Nuclear Information System (INIS)

    Fiquet, J.M.

    1980-09-01

    When determining ''D.P.D.'' free oxidizers, the monochloramine interfers in particular for iodide levels analogous to those likely to be found in sea water. This is not so for iodate. The zero time extrapolation of the change in colour curve is one method that enables the method to be made more selective [fr

  20. Solution enthalpy of potassium iodide in furfural and its mixtures with dimethylsulfoxide

    International Nuclear Information System (INIS)

    Vlasenko, K.K.; Belov, A.A.; Vorob'ev, A.F.

    1986-01-01

    Solution enthalpy of potassium iodide in furfural-dimethylsulfoxide mixtures at 298.15 K and furfural concentration 17.3-100% are determined experimentally. K + and I - ion solvate shell composition, which in the general case doesn't correspond to the mixed solvent composition, is calculated

  1. Iodide Residues in Milk Vary between Iodine-Based Teat Disinfectants

    NARCIS (Netherlands)

    French, Elizabeth A; Mukai, Motoko; Zurakowski, Michael; Rauch, Bradley; Gioia, Gloria; Hillebrandt, Joseph R; Henderson, Mark; Schukken, Ynte H; Hemling, Thomas C

    Majority of iodine found in dairy milk comes from the diet and teat disinfection products used during milking process. The objective of this study was to evaluate the effects of 4 iodine-based teat dips on milk iodide concentrations varying in iodine level (0.25% vs. 0.5%, w/w), normal low viscosity

  2. Kinetic modeling of the purging of activated carbon after short term methyl iodide loading

    International Nuclear Information System (INIS)

    Friedrich, V.; Lux, I.

    1991-01-01

    A bimolecular reaction model containing the physico-chemical parameters of the adsorption and desorption was developed earlier to describe the kinetics of methyl iodide retention by activated carbon adsorber. Both theoretical model and experimental investigations postulated constant upstream methyl iodide concentration till the maximum break-through. The work reported here includes the extension of the theoretical model to the general case when the concentration of the challenging gas may change in time. The effect of short term loading followed by purging with air, and an impulse-like increase in upstream gas concentration has been simulated. The case of short term loading and subsequent purging has been experimentally studied to validate the model. The investigations were carried out on non-impregnated activated carbon. A 4 cm deep carbon bed had been challenged by methyl iodide for 30, 90, 120 and 180 min and then purged with air, downstream methyl iodide concentration had been measured continuously. The main characteristics of the observed downstream concentration curves (time and slope of break-through, time and amplitude of maximum values) showed acceptable agreement with those predicted by the model

  3. Relaxation of the silver/silver iodide electrode in aqueous solution

    NARCIS (Netherlands)

    Peverelli, K.J.

    1979-01-01

    The aim of this study is to detect and characterize relaxation processes on silver/silver iodide electrodes in aqueous electrolyte solution. The information obtained is to be used for an estimation of the consequences of similar processes on colloidal AgI

  4. Regioselective conversion of primary alcohols into iodides in unprotected methyl furanosides and pyranosides

    DEFF Research Database (Denmark)

    Skaanderup, Philip Robert; Poulsen, Carina Storm; Hyldtoft, Lene

    2002-01-01

    Two methods are described for the regioselective displacement of the primary hydroxy group in methyl glycosides with iodide. The first method is a modification of a literature procedure employing triphenylphosphine and iodine, where purification has been carried out on a reverse phase column in o...

  5. Iodide-induced thyrotoxicosis in a thyroidectomized patient with metastatic thyroid carcinoma

    International Nuclear Information System (INIS)

    Yoshinari, M.; Tokuyama, T.; Okamura, K.; Sato, K.; Kusuda, K.; Fujishima, M.

    1988-01-01

    An unusual case of iodide-induced thyrotoxicosis is documented in this article. The patient was a 64-year-old euthyroid man with acromegaly. He also had multiple follicular and papillary thyroid carcinomas with a metastatic lesion in the lumbar vertebrae. After a total thyroidectomy, he became slightly hypothyroid, and the lumbar lesion began to incorporate 131 I by scintigraphy. When an iodine-containing contrast medium happened to be injected, a transient increase of serum thyroid hormone level was observed. After complete thyroid ablation with 83 mCi of 131 I, the oral administration of 100 mg of potassium iodide for 7 days induced a prominent increase of serum thyroid hormone level. These findings indicated that the metastatic thyroid carcinoma could produce excess thyroid hormone insofar as a sufficient amount of iodide was given. Although this is the first report of such a case, iodide-induced thyrotoxicosis may not be rare in patients with thyroid carcinomas because the Wolff-Chaikoff effect is thought to be lost, and the organic iodinating activity and lysosomal protease activity are well-preserved

  6. Sensitive determination of iodide in the presence of large quantities of chloride

    International Nuclear Information System (INIS)

    Hainberger, L.; Lenzi, E.

    1982-01-01

    A determination of iodide with catalytic oxidation of p-phenetidine is described. A dye is formed with a maximum of absorption at 490 nm. The law of Lambert-Beer is obeyed between 0.6 and 2.2 ppm. Some of the interferents are examined. (Author)

  7. Extension of HPM Pulse Duration by Cesium Iodide Cathodes in Crossed Field Devices

    National Research Council Canada - National Science Library

    Benford, James

    1998-01-01

    .... The introduction of cathodes made from Cesium Iodide-coated (CsI) carbon fiber has shown plasma speeds reduced by factors of a few from uncoated carbon fiber, but previous work was at low diode fields of a few 10's of kV/cm...

  8. Iodide and iodate sodalites for the long-term storage of iodine-129

    International Nuclear Information System (INIS)

    Strachan, D.M.; Babad, H.

    1979-01-01

    There exist several proposals for the storage of 129 I. None of these propose the use of a mineral with demonstrated geologic stability. The work described in this paper has identified the minerals iodide and iodate sodalites [Na 8 (AlSiO 4 ) 6 I 2 /(IO 3 ) 2 ] as good candidates for the long-term storage of 129 I. 4 tables

  9. Electrokinetic properties and conductance relaxation of polystyrene and silver iodide plugs

    NARCIS (Netherlands)

    Hoven, van den J.J.

    1984-01-01

    This thesis describes an experimental study on the electrokinetic and electrical properties of concentrated polystyrene and silver iodide dispersions. The purpose of the study is to obtain information on the structure of the electrical double layer at the solid-liquid interface. Special

  10. Experimental study on iodine chemistry (EXSI) - Containment experiments with methyl iodide

    Energy Technology Data Exchange (ETDEWEB)

    Holm, J.; Ekberg, C. (Chalmers Univ. of Technology, Goeteborg (Sweden)); Kaerkelae, T.; Auvinen, A. (VTT, Espoo (Finland)); Glaenneskog, H. (Vattenfall Power Consultant, Goeteborg (Sweden))

    2011-05-15

    An experimental study on radiolytic decomposition of methyl iodide was conducted in co-operation between VTT and Chalmers University of Technology as a part of the NKS-R programs. In year 2008 the NROI project, a Nordic collaboration studying iodine chemistry in the containment, was started. During year 2008 (NROI-1) the radiolytic oxidation of elemental iodine was investigated and during 2009 (NROI-2), the radiolytic oxidation of organic iodine was studied. This project (NROI-3) is a continuation of the investigation of the oxidation of organic iodine. The project has been divided into two parts. 1. The aims of the first part were to investigate the effect of ozone and UV-radiation, in dry and humid conditions, on methyl iodide. 2. The second project was about gamma radiation (approx20 kGy/h) and methyl iodide in dry and humid conditions. 1. Experimental results showed that the methyl iodide concentration in the facility was reduced with increasing temperature and increasing UV-radiation intensity. Similar behaviour occurred when ozone was present in the system. Formed organic gas species during the decomposition of methyl iodide was mainly formaldehyde and methanol. The particle formation was instant and extensive when methyl iodide was exposed to ozone and/or radiation at all temperatures. The size of the formed primary particles was about 10 nm and the size of secondary particles was between 50-200 nm. From the SEM-EDX analyses of the particles, the conclusion was drawn that these were some kind of iodine oxides (I{sub xO{sub y}). However, the correct speciation of the formed particles was difficult to obtain because the particles melted and fused together under the electron beam. 2. The results from this sub-project are more inconsistent and hard to interpret. The particle formation was significant lesser than corresponding experiments when ozone/UV-radiation was used instead of gamma radiation. The transport of gaseous methyl iodide through the facility was

  11. Strontium zirconate as silicon and aluminum scavenger in yttria stabilized zirconia

    DEFF Research Database (Denmark)

    Andersen, Thomas; Hansen, Karin Vels; Chorkendorff, Ib

    2011-01-01

    Here we report on strontium zirconate as a getter for silicon dioxide and aluminum oxide in yttria stabilized zirconia (YSZ) single crystals for cleaning purposes. YSZ single crystals were covered with strontium zirconate powder and heat treated at 1450°C in water vapor. After treatment the YSZ...... by transmission electron microscopy (TEM) the interface region between bump and YSZ single crystal bulk was examined. EDS showed a homogeneous distribution of silicon and aluminum through the cross section of a bump. The results suggest strontium zirconate as a good getter for silicon and aluminum from bulk...

  12. Physicochemical Properties and Cellular Responses of Strontium-Doped Gypsum Biomaterials

    OpenAIRE

    Pouria, Amir; Bandegani, Hadis; Pourbaghi-Masouleh, Milad; Hesaraki, Saeed; Alizadeh, Masoud

    2012-01-01

    This paper describes some physical, structural, and biological properties of gypsum bioceramics doped with various amounts of strontium ions (0.19–2.23 wt%) and compares these properties with those of a pure gypsum as control. Strontium-doped gypsum (gypsum:Sr) was obtained by mixing calcium sulfate hemihydrate powder and solutions of strontium nitrate followed by washing the specimens with distilled water to remove residual salts. Gypsum was the only phase found in the composition of both pu...

  13. Regulation of strontium migration and translocation in chemical reclamation of acid soils

    International Nuclear Information System (INIS)

    Velichko, V.A.; Okonskij, A.I.; Shestakov, E.I.; Panov, N.P.

    1993-01-01

    Results of chemical testing are presented of the local reclamants (ashes of various deposits and ferrochromium plant slags) to study the possibilities of their use for chemical soil reclamation. Attention was paid to the investigation of pollutant (strontium) behaviour in the reclamant-acid soil-plant-ground water system. Tracer method was used, 85 Sr was applied as a label. Prospects of zeolite application to control the strontium behaviour following the reclamant introduction into soil were considered. It was shown that zeolite application permitted to regulate strontium behaviour in the reclamant-soil-plant-ground water system. At that the modified zeolites possessing high Sr selectivity are recommended for application

  14. Bactericidal strontium-releasing injectable bone cements based on bioactive glasses

    OpenAIRE

    Brauer, Delia S.; Karpukhina, Natalia; Kedia, Gopal; Bhat, Aditya; Law, Robert V.; Radecka, Izabela; Hill, Robert G.

    2013-01-01

    Strontium-releasing injectable bone cements may have the potential to prevent implant-related infections through the bactericidal action of strontium, while enhancing bone formation in patients suffering from osteoporosis. A melt-derived bioactive glass (BG) series (SiO2–CaO–CaF2–MgO) with 0–50% of calcium substituted with strontium on a molar base were produced. By mixing glass powder, poly(acrylic acid) and water, cements were obtained which can be delivered by injection and set in situ, gi...

  15. Review and evaluation of extractants for strontium removal using magnetically assisted chemical separation

    International Nuclear Information System (INIS)

    Bauer, C.B.; Rogers, R.D.

    1995-11-01

    A literature review on extractants for strontium removal was initially performed at Northern Illinois University to assess their potential in magnetically assisted chemical separation. A series of potential strontium extractants was systematically evaluated there using radioanalytical methods. Initial experiments were designed to test the uptake of strontium from nitric acid using several samples of magnetic extractant particles that were coated with various crown ether ligands. High partition coefficient (K d ) values for stimulant tank waste were obtained. Further studies demonstrated that the large partitioning was due to uncoated particles

  16. Isotope ratios of strontium and neodymium for characterizing earth mantle materials

    International Nuclear Information System (INIS)

    Brandt, S.B.; Lepin, V.S.; Maslovskaja, M.N.

    1985-01-01

    It is shown that the shares of mantle, crustal and sedimentary materials in rocks and ore deposits can be determined by isotope methods. Using Yakutian kimberlites as an example, mixing processes of mantle and crustal materials are illustrated with the aid of strontium isotopes. Due to the high sensitivity of strontium to hydrothermal effects, the combined use of neodymium and strontium isotopes is considered more appropriate to solve the problem of determining the share of mantle materials. This is demonstrated for rare earth minerals and alkaline rocks of Eastern Siberia and Mongolia. (author)

  17. Thermodynamic study on the adsorption of strontium on polyantimonic acid exchanger

    International Nuclear Information System (INIS)

    Li Mingyu; Chen Jing; Wang Jianchen; Zhao Jing

    2007-01-01

    The adsorption of strontium on the polyantimonic acid adsorbent was studied. The equilibrium data for the adsorption of strontium on polyantimonic acid exchanger from aqueous solutions were obtained and correlated with Langmuir-type and Freundlich-type isotherm equation within the temperature range of 293-323 K and the experimental concentration range. Freundlich adsorption isotherms and the isosteric enthalpy indicate that the adsorption of strontium on polyantimonic acid is an endothermic process from aqueous solutions. The enthalpy, free energy, and entropy of adsorption were calculated. The results indicate that the adsorption process is a complex interaction of physical and chemical processes. The adsorption behaviors were reasonably explained. (authors)

  18. Local structure and speciation of uranium in strontium orthosilicate: TRFS and EXAFS studies

    International Nuclear Information System (INIS)

    Gupta, Santosh K.; Thulasidas, S.K.; Natarajan, V.; Yadav, A.K.; Bhattacharya, D.

    2015-01-01

    TRFS is used to investigate the valence state and coordination behavior of uranium in strontium orthosilicate. From TRFS measurement it was observed that uranium exists as U(VI) in the form of UO 2 2+ in Sr 2 SiO 4 . Based on life time measurement and EXAFS studies it was inferred that uranyl is stabilized on both 9- and 10- coordinated strontium polyhedra. Majority of uranyl ion occupy relatively asymmetric site in strontium silicate most probably 9-coordinated Sr sites. (author)

  19. A distribution ratio model of strontium by crown ether extraction from simulated HLLW

    International Nuclear Information System (INIS)

    Chen Jing; Wang Qiuping; Wang Jianchen; Song Chongli

    1995-01-01

    An experiential distribution ratio model for strontium extraction by dicyclohexano-18-crown-6-n-octanol from simulated high-level waste is established. The experimental points for the model are designed by experimental homogeneous-design method. The regression of distribution ratio model of strontium is carried out by the complex-optimization method. The model is verified with experimental distribution ratio data in different extraction conditions. The results show that the relative deviations are within +-10% and the mean relative divination is 4.4% between the calculated data and the experimental ones. The experiential model together with an iteration program can be used for the strontium extraction process calculation

  20. Effects of mineralogy on sorption of strontium and cesium onto Calico Hills Tuff

    International Nuclear Information System (INIS)

    Meyer, R.E.; Arnold, W.D.; Case, F.I.; O'Kelley, G.D.; Land, J.F.

    1990-04-01

    The sorption properties of tuff formations at the proposed site for the high-level nuclear waste repository at Yucca Mountain, Nevada, have been extensively studied. Sorption and desorption measurements were made of strontium and cesium onto clinoptilolite and Calico Hills Tuff. The object was to see whether there was a correlation between sorption of strontium and cesium onto Calico Hills Tuff and the sorption of strontium and cesium onto clinoptilolite based on the content of clinoptilolite in the Calico Hills Tuff. 13 refs., 10 figs., 6 tabs