WorldWideScience

Sample records for epoxy resins modified

  1. Synthesis and Characterization of Modified Epoxy Resins by Silicic Acid Tetraethyl Ester and Nano-SiO2

    Institute of Scientific and Technical Information of China (English)

    李海燕; 张之圣

    2004-01-01

    A kind of modified epoxy resins was obtained by condensation of epoxy resin with silicic acid tetraethyl ester(TEOS) and nano-SiO2. The reactions were performed with hydrochloric acid as a catalyst at 63 °C.The structure, thermal stability and morphological characteristics of the modified epoxy resins were studied through infrared spectra(FT-IR) analysis, thermogravimetric (TG) analysis and scanning electron microscopy respectively. It has been found from the IR and TG study that modified epoxy resins have greater thermal stability than epoxy resins, and its thermal stability has been improved by the formation of inter-crosslinked network structure. The modified epoxy resins exhibit heterogeneous morphology and heterogeneity increases with more TEOS feeding, which in turn confirms the formation of inter-crosslinked network structure in modified epoxy resins.

  2. Improvement of epoxy resin properties by incorporation of TiO2 nanoparticles surface modified with gallic acid esters

    International Nuclear Information System (INIS)

    Radoman, Tijana S.; Džunuzović, Jasna V.; Jeremić, Katarina B.; Grgur, Branimir N.; Miličević, Dejan S.; Popović, Ivanka G.; Džunuzović, Enis S.

    2014-01-01

    Highlights: • Nanocomposites of epoxy resin and TiO 2 nanoparticles surface modified with gallates. • The T g of epoxy resin was increased by incorporation of surface modified TiO 2 . • WVTR of epoxy resin decreased in the presence of surface modified TiO 2 nanoparticles. • WVTR of nanocomposites was reduced with increasing gallates hydrophobic chain length. • Modified TiO 2 nanoparticles react as oxygen scavengers, inhibiting steel corrosion. - Abstract: Epoxy resin/titanium dioxide (epoxy/TiO 2 ) nanocomposites were obtained by incorporation of TiO 2 nanoparticles surface modified with gallic acid esters in epoxy resin. TiO 2 nanoparticles were obtained by acid catalyzed hydrolysis of titanium isopropoxide and their structural characterization was performed by X-ray diffraction and transmission electron microscopy. Three gallic acid esters, having different hydrophobic part, were used for surface modification of the synthesized TiO 2 nanoparticles: propyl, hexyl and lauryl gallate. The gallate chemisorption onto surface of TiO 2 nanoparticles was confirmed by Fourier transform infrared and ultraviolet–visible spectroscopy, while the amount of surface-bonded gallates was determined using thermogravimetric analysis. The influence of the surface modified TiO 2 nanoparticles, as well as the length of hydrophobic part of the gallate used for surface modification of TiO 2 nanoparticles, on glass transition temperature, barrier, dielectric and anticorrosive properties of epoxy resin was investigated by differential scanning calorimetry, water vapor transmission test, dielectric spectroscopy, electrochemical impedance spectroscopy and polarization measurements. Incorporation of surface modified TiO 2 nanoparticles in epoxy resin caused increase of glass transition temperature and decrease of the water vapor permeability of epoxy resin. The water vapor transmission rate of epoxy/TiO 2 nanocomposites was reduced with increasing hydrophobic part chain length of

  3. Nanosilica Modification of Elastomer-Modified VARTM Epoxy Resins for Improved Resin and Composite Toughness

    National Research Council Canada - National Science Library

    Robinette, Jason; Bujanda, Andres; DeSchepper, Daniel; Dibelka, Jessica; Costanzo, Philip; Jensen, Robert; McKnight, Steven

    2007-01-01

    Recent publications have reported a synergy between rubber and silica in modified epoxy resins that results in significantly improved fracture toughness without reductions in other material properties...

  4. Electrodeposition properties of modified cational epoxy resin-type photoresist

    International Nuclear Information System (INIS)

    Yong He; Yunlong Zhang; Feipeng Wu; Miaozhen Li; Erjian Wang

    1999-01-01

    Multi-component cationic epoxy and acrylic resin system for ED photoresist was used in this work, since they can provide better storage stability for ED emulsion and better physical and chemical properties of deposited film than one-component system. The cationic main resin (AE) was prepared from amine modified epoxy resins and then treated with acetic acid. The amination degree was controlled as required. The synthetic procedure of cationic main resins is described in scheme I. The ED photoresist (AME) is composed of cationic main resin (AE) and nonionic multifunctional acrylic crosslinkers (PETA), in combination with suitable photo-initiator. They can easily be dispersed in deionized water to form a stable ED emulsion. The exposed part of deposited film upon UV irradiation occurs crosslinking to produce an insoluble semi-penetrating network and the unexposed part remains good solubility in the acidic water solution. It is readily utilized for fabrication of fine micropattern. The electrodeposition are carried out on Cu plate at room temperature. To evaluate the electrodeposition properties of ED photoresist (AME), the different influences are examined

  5. The application of epoxy resin coating in grounding grid

    Science.gov (United States)

    Hu, Q.; Chen, Z. R.; Xi, L. J.; Wang, X. Y.; Wang, H. F.

    2018-01-01

    Epoxy resin anticorrosion coating is widely used in grounding grid corrosion protection because of its wide range of materials, good antiseptic effect and convenient processing. Based on the latest research progress, four kinds of epoxy anticorrosive coatings are introduced, which are structural modified epoxy coating, inorganic modified epoxy coating, organic modified epoxy coating and polyaniline / epoxy resin composite coating. In this paper, the current research progress of epoxy base coating is analyzed, and prospected the possible development direction of the anti-corrosion coating in the grounding grid, which provides a reference for coating corrosion prevention of grounding materials.

  6. Aging in CTBN modified epoxy resin stocks

    International Nuclear Information System (INIS)

    Creed, K.E. Jr.

    1979-01-01

    The cause of degradation in the glass transition temperature (T/sub G/) of a partially crystallized polymer was investigated. Sample epoxy resin filled capacitors were cured at 90 0 C for 24 hours, then stored at room atmospheric conditions. These showed typical degradation in T/sub G/ after storage for one month. One set of epoxy resin castings was stored at room atmosphere and another set was stored in a dry box at 0% relative humidity and 27 0 C. The samples at room atmospheric conditions showed typical degradation in T/sub G/, while the T/sub G/ for those stored in the dry box increased. Further tests were then made on epoxy resin castings at various curing temperatures and times at both room atmosphere and 0% humidity. Resulting data indicated that absorption of moisture during storage was the predominant cause of T/sub G/ degradation, with stress relaxation another, though smaller, contributing factor

  7. Modeling and mechanical performance of carbon nanotube/epoxy resin composites

    International Nuclear Information System (INIS)

    Srivastava, Vijay Kumar

    2012-01-01

    Highlights: ► The MWCNT fillers are uniformly dispersed in the epoxy resin, which improved the mechanical properties of epoxy resin. ► Modified Halpin–Tsai model is useful to calculate the Young’s modulus of MWCNT/epoxy resin composite. ► The experimental moduli are within the variation of 27% with the theoretical values. -- Abstract: The effect of multi-walled carbon nanotube (MWCNT) addition on mechanical properties of epoxy resin was investigated to obtain the tensile strength, compressive strength and Young’s modulus from load versus displacement graphs. The result shows that the tensile strength, compressive strength and Young’s modulus of epoxy resin were increased with the addition of MWCNT fillers. The significant improvements in tensile strength, compressive strength and Young’s modulus were obtained due to the excellent dispersion of MWCNT fillers in the epoxy resin. The dispersion of MWCNT fillers in epoxy resin was observed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM) analysis. Also, Halpin–Tsai model was modified by considering the average diameter of internal/external of multi-walled nanotube and orientation factor (α) to calculate the Young’s modulus of multi-walled carbon nanotubes (MWCNTs)/epoxy resin composite. There was a good correlation between the experimentally obtained Young’s modulus and modified Halpin–Tsai model.

  8. Morphology and contact angle studies of poly(styrene-co-acrylonitrile modified epoxy resin blends and their glass fibre reinforced composites

    Directory of Open Access Journals (Sweden)

    2007-06-01

    Full Text Available In this study, the surface characteristics of blends and composites of epoxy resin were investigated. Poly(styrene-co-acylonitrile (SAN was used to modify diglycedyl ether of bisphenol-A (DGEBA type epoxy resin cured with diamino diphenyl sulfone (DDS and the modified epoxy resin was used as the matrix for fibre reinforced composites (FRP’s. E-glass fibre was used as the fibre reinforcement. The scanning electron micrographs of the fractured surfaces of the blends and composites were analyzed. Morphological analysis revealed different morphologies such as dispersed, cocontinuous and phase-inverted structures for the blends. Contact angle studies were carried out using water and methylene iodide at room temperature. The solid surface energy was calculated using harmonic mean equations. Blending of epoxy resin increases its contact angle. The surface free energy, work of adhesion, interfacial free energy, spreading coefficient and Girifalco-Good’s interaction parameter were changed significantly in the case of blends and composites. The incorporation of thermoplastic and glass fibre reduces the wetting and hydrophilicity of epoxy resin.

  9. Imidazolium Ionic Liquid Modified Graphene Oxide: As a Reinforcing Filler and Catalyst in Epoxy Resin

    Directory of Open Access Journals (Sweden)

    Qing Lyu

    2017-09-01

    Full Text Available Surface modification of graphene oxide (GO is one of the most important issues to produce high performance GO/epoxy composites. In this paper, the imidazole ionic liquid (IMD-Si was introduced onto the surface of GO sheets by a cheap and simple method, to prepare a reinforcing filler, as well as a catalyst in epoxy resin. The interlayer spacing of GO sheets was obviously increased by the intercalation of IMD-Si, which strongly facilitated the dispersibility of graphene oxide in organic solvents and epoxy matrix. The addition of 0.4 wt % imidazolium ionic liquid modified graphene oxide (IMD-Si@GO, yielded a 12% increase in flexural strength (141.3 MPa, a 26% increase in flexural modulus (4.69 GPa, and a 52% increase in impact strength (18.7 kJ/m2, compared to the neat epoxy. Additionally the IMD-Si@GO sheets could catalyze the curing reaction of epoxy resin-anhydride system significantly. Moreover, the improved thermal conductivities and thermal stabilities of epoxy composites filled with IMD-Si@GO were also demonstrated.

  10. Organo-modified bentonites as new flame retardant fillers in epoxy resin nanocomposites

    Science.gov (United States)

    Benelli, Tiziana; D'Angelo, Emanuele; Mazzocchetti, Laura; Saraga, Federico; Sambri, Letizia; Franchini, Mauro Comes; Giorgini, Loris

    2016-05-01

    The present work deals with two organophilic bentonites, based on nitrogen-containing compounds: these organoclays were synthesized via an ion exchange process starting from pristine bentonite with 6-(4-butylphenyl)-1,3,5-triazine-2,4-diamine (BFTDA) and 11-amino-N-(pyridine-2yl)undecanamide (APUA) and then used for the production of epoxy-based flame retardant nanocomposites. The amount of organic modifier in the organoclays Bento-BFTDA and Bento-APUA was determined with a TGA analysis and is around 0.4mmol/g for both samples. The effect of the organoclays on a commercial epoxy resin nanocomposite's thermo-mechanical and flammability properties was investigated. Composites containing 3wt% and 5wt% of the nanofillers were prepared by solventless addition of each organoclay to the epoxy resin, followed by further addition of the hardener component. For the sake of comparison a similar nanocomposite with the plain unmodified bentonite was produced in similar condition. The nanocomposites's thermo-mechanical properties of all the produced samples were measured and they resulted slightly improved or practically unaffected. On the contrary, when the flame behaviour was assessed in the cone-calorimeter, an encouraging decrease of 17% in the peak heat released rate (pHRR) was obtained at 3wt% loading level with Bento-APUA. This is a promising result, assessing that the APUA modified organoclay might act as flame retardant.

  11. Green Preparation of Epoxy/Graphene Oxide Nanocomposites Using a Glycidylamine Epoxy Resin as the Surface Modifier and Phase Transfer Agent of Graphene Oxide.

    Science.gov (United States)

    Tang, Xinlei; Zhou, Yang; Peng, Mao

    2016-01-27

    In studies of epoxy/graphene oxide (GO) nanocomposites, organic solvents are commonly used to disperse GO, and vigorous mechanical processes and complicated modification of GO are usually required, increasing the cost and hindering the development and application of epoxy nanocomposites. Here, we report a green, facile, and efficient method of preparing epoxy/GO nanocomposites. When triglycidyl para-aminophenol (TGPAP), a commercially available glycidyl amine epoxy resin with one tertiary amine group per molecule, is used as both the surface modifier and phase transfer agent of GO, GO can be directly and rapidly transferred from water to diglycidyl ether of bisphenol A and other types of epoxy resins by manual stirring under ambient conditions, whereas GO cannot be transferred to these epoxy resins in the absence of TGPAP. The interaction between TGPAP and GO and the effect of the TGPAP content on the dispersion of GO in the epoxy matrix were investigated systematically. Superior dispersion and exfoliation of GO nanosheets and remarkably improved mechanical properties, including tensile and flexural properties, toughness, storage modulus, and microhardness, of the epoxy/GO nanocomposites with a suitable amount of TGPAP were demonstrated. This method is organic-solvent-free and technically feasible for large-scale preparation of high-performance nanocomposites; it opens up new opportunities for exploiting the unique properties of graphene or even other nanofillers for a wide range of applications.

  12. Modification of (DGEBA epoxy resin with maleated depolymerised natural rubber

    Directory of Open Access Journals (Sweden)

    2008-04-01

    Full Text Available In this work, diglycidyl ether of bisphenol A (DEGBA type epoxy resin has been modified with maleated depolymerised natural rubber (MDPR. MDPR was prepared by grafting maleic anhydride onto depolymerised natural rubber. MDPR has been characterized by Fourier transform infrared (FT-IR spectroscopy and nuclear magnetic resonance spectroscopy. MDPR was blended with epoxy resin at three different ratios (97/3, 98/2 and 99/1, by keeping the epoxy resin component as the major phase and maleated depolymerised natural rubber component as the minor phase. The reaction between the two blend components took place between the acid/anhydride group in the MDPR and the epoxide group of the epoxy resin. The proposed reaction schemes were supported by the FT-IR spectrum of the uncured Epoxy/MDPR blends. The neat epoxy resin and Epoxy/MDPR blends were cured by methylene dianiline (DDM at 100°C for three hours. Thermal, morphological and mechanical properties of the neat epoxy and the blends were investigated. Free volume studies of the cured, neat epoxy and Epoxy/MDPR blends were correlated with the morphological and mechanical properties of the same systems using Positron Annihilation Lifetime Studies.

  13. Preparation and Properties of Epoxy Resin-Coated Micro-Sized Ferrosilicon Powder

    OpenAIRE

    Ku,Jiangang; Chen,Huihuang; He,Kui; Yan,Quanxiang

    2016-01-01

    Ferrosilicon powder surface coated with a dense epoxy resin membrane was prepared via coating precipitation methods using silane coupling agents as the modifier and epoxy resin as the coating agent. FTIR, FESEM, MPMS-XL, and TG-DSC were used to analyze the morphology, surface composition, magnetic property and thermostability of ferrosilicon powder before and after the modification and coating. The experimental results indicate that epoxy resin membranes of a certain thickness were successful...

  14. Contact allergy to epoxy resin

    DEFF Research Database (Denmark)

    Bangsgaard, Nannie; Thyssen, Jacob Pontoppidan; Menné, Torkil

    2012-01-01

    Background. Epoxy resin monomers are strong skin sensitizers that are widely used in industrial sectors. In Denmark, the law stipulates that workers must undergo a course on safe handling of epoxy resins prior to occupational exposure, but the effectiveness of this initiative is largely unknown...... in an educational programme. Conclusion. The 1% prevalence of epoxy resin contact allergy is equivalent to reports from other countries. The high occurrence of epoxy resin exposure at work, and the limited use of protective measures, indicate that reinforcement of the law is required....

  15. Surface modification of titanium hydride with epoxy resin via microwave-assisted ball milling

    International Nuclear Information System (INIS)

    Ning, Rong; Chen, Ding; Zhang, Qianxia; Bian, Zhibing; Dai, Haixiong; Zhang, Chi

    2014-01-01

    Highlights: • TiH 2 was modified with epoxy resin by microwave-assisted ball milling. • The epoxy ring was opened under the coupling effect of microwave and ball milling. • Microwave-assisted ball milling improved the compatibility of TiH 2 with epoxy. - Abstract: Surface modification of titanium hydride with epoxy resin was carried out via microwave-assisted ball milling and the products were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), thermo-gravimetry (TG) and Fourier transform infrared spectroscopy (FT-IR). A sedimentation test was performed to investigate the compatibility of the modified nano titanium hydride with the epoxy resin. The results show that the epoxy resin molecules were grafted on the surface of nano titanium hydride particles during the microwave-assisted ball milling process, which led to the improvement of compatibility between the nanoparticles and epoxy resin. According to the FT-IR, the grafting site was likely to be located around the epoxy group due to the fact that the epoxy ring was opened. However, compared with microwave-assisted ball milling, the conventional ball milling could not realize the surface modification, indicating that the coupling effect of mechanical force and microwave played a key role during the process

  16. Biphenyl liquid crystalline epoxy resin as a low-shrinkage resin-based dental restorative nanocomposite.

    Science.gov (United States)

    Hsu, Sheng-Hao; Chen, Rung-Shu; Chang, Yuan-Ling; Chen, Min-Huey; Cheng, Kuo-Chung; Su, Wei-Fang

    2012-11-01

    Low-shrinkage resin-based photocurable liquid crystalline epoxy nanocomposite has been investigated with regard to its application as a dental restoration material. The nanocomposite consists of an organic matrix and an inorganic reinforcing filler. The organic matrix is made of liquid crystalline biphenyl epoxy resin (BP), an epoxy resin consisting of cyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (ECH), the photoinitiator 4-octylphenyl phenyliodonium hexafluoroantimonate and the photosensitizer champhorquinone. The inorganic filler is silica nanoparticles (∼70-100 nm). The nanoparticles were modified by an epoxy silane of γ-glycidoxypropyltrimethoxysilane to be compatible with the organic matrix and to chemically bond with the organic matrix after photo curing. By incorporating the BP liquid crystalline (LC) epoxy resin into conventional ECH epoxy resin, the nanocomposite has improved hardness, flexural modulus, water absorption and coefficient of thermal expansion. Although the incorporation of silica filler may dilute the reinforcing effect of crystalline BP, a high silica filler content (∼42 vol.%) was found to increase the physical and chemical properties of the nanocomposite due to the formation of unique microstructures. The microstructure of nanoparticle embedded layers was observed in the nanocomposite using scanning and transmission electron microscopy. This unique microstructure indicates that the crystalline BP and nanoparticles support each other and result in outstanding mechanical properties. The crystalline BP in the LC epoxy resin-based nanocomposite was partially melted during exothermic photopolymerization, and the resin expanded via an order-to-disorder transition. Thus, the post-gelation shrinkage of the LC epoxy resin-based nanocomposite is greatly reduced, ∼50.6% less than in commercialized methacrylate resin-based composites. This LC epoxy nanocomposite demonstrates good physical and chemical properties and good biocompatibility

  17. Preparation and Performance of Amphiphilic Random Copolymer Noncovalently Modified MWCNTs/Epoxy Composite

    Directory of Open Access Journals (Sweden)

    MA Qiang

    2016-09-01

    Full Text Available An amphiphilic random copolymer of polyglycidyl methacrylate-co-N-vinyl carbazole P(GMA-co-NVC was synthesized by free radical polymerization and was used to noncovalently modify multi-walled carbon nanotubes (MWCNTs. The obtained P(GMA-co-NVC/MWCNTs was mixed with epoxy resin and used to reinforce epoxy resin. Polymer modified carbon nanotubes/epoxy resin composites were prepared by a casting molding method. Tensile test, electrical resistivity test and differential scanning calorimeter(DSC analysis were used to study the effect of polymer modified carbon nanotubes on the mechanical, electrical, and thermal properties of epoxy resin. The results show that the epoxy composite reinforced with P(GMA-co-NVC/MWCNTs shows a remarkable enhancement in both tensile strength and elongation at break compared to either the pure epoxy or the pristine MWCNTs/epoxy composites. In addition, the electrical conductivity of epoxy is significantly improved and the volume resistivity decreases from 1014Ω·m to 106Ω·m with 0.25% mass fraction loading of P(GMA-co-NVC/MWCNTs. Moreover, glass transition temperature of the epoxy composite also increases from 144℃ to 149℃.

  18. Modification of bifunctional epoxy resin using CO2 fixation process and nanoclay

    International Nuclear Information System (INIS)

    Khoshkish, Morteza; Bouhendi, Hosein; Vafayan, Mehdi

    2014-01-01

    A bifunctional epoxy resin was modified by using a CO 2 fixation solution process in the presence of tetra n-butyl ammonium bromide (TBAB) as catalyst and the modified treated resin was treated by cloisite 30B as nano additive. The Unmodified epoxy resin (UME), CO 2 fixated modified epoxy resin (CFME), and CFME/clay nano composite (CFMEN), were cured by diethylenetriamine (DETA). A cycloaliphatic compound as a reactive diluent was used to control the viscosity of high viscose CFME. The exfoliation of organoclay in UME and CFME was investigated by X-ray diffraction and activation energy was computed using the advanced integral isoconversional method. The activation energy dependency demonstrated that the mechanism of UME curing did not change in the presence of nanoclay. In contrast, the CO 2 fixation results showed a significant change in the activation energy dependency. The Thermal stability parameters include the initial degradation temperature (IDT), the temperature at the maximum rate of weight loss (T max ), and the decomposition activation energy (E d ) were determined by thermal gravimetry analysis. Dynamic mechanical thermal analysis measurements showed that the presence of organoclay in CFME increases the T g of nano composite in contrast to UME. The fracture roughness of UME, CFME and CFNE were determined by scanning electron microscope. The exfoliated UME/1%clay nanocomposite was confirmed by TEM image. - Highlights: • A new epoxy resin was synthesized using CO 2 fixation reaction. • The synthesized epoxy resin was modified by an organo nano-clay. • CO 2 fixation noticeably changed the curing mechanism. • CO 2 fixation reaction consumes CO 2 which is a harmful greenhouse gas

  19. Immobilization of spent resin with epoxy resin

    International Nuclear Information System (INIS)

    Gultom, O.; Suryanto; Sayogo; Ramdan

    1997-01-01

    immobilization of spent resin using epoxy resin has been conducted. The spent resin was mixtured with epoxy resin in variation of concentration, i.e., 30, 40, 50, 60, 70 weight percent of spent resin. The mixture were pour into the plastic tube, with a diameter of 40 mm and height of 40 mm. The density, compressive strength and leaching rate were respectively measured by quanta chrome, paul weber apparatus and gamma spectrometer. The results showed that the increasing of waste concentration would be decreased the compressive strength, and increased density by immobilized waste. The leaching rate of 137 Cs from waste product was not detected in experiment (author)

  20. Action of ionizing radiation on epoxy resins

    Energy Technology Data Exchange (ETDEWEB)

    Van de Voorde, M. E.

    1970-12-01

    The resistance of classical and experimental epoxy resins to irradiation was studied. The resistance to irradiation of epoxy resins of diverse compositions as well as the development of resins having a radioresistance that approaches that of certain ceramics are discussed. Sources of irradiation and the techniques of dosimetry used are described. The structures of certain epoxy resins and of hardeners are given. The preparation of these resins and their physical properties is described. The effects of radiation on epoxy resins, as well as conditions of irradiation, and suggested mechanisms for degradation of the irradiated resins are discussed. The relationship between chemical structure of the resins and their physical properties is evaluated. (115 references) (JCB)

  1. Modification of bifunctional epoxy resin using CO{sub 2} fixation process and nanoclay

    Energy Technology Data Exchange (ETDEWEB)

    Khoshkish, Morteza; Bouhendi, Hosein, E-mail: H.boohendi@ippi.ac.ir; Vafayan, Mehdi

    2014-10-15

    A bifunctional epoxy resin was modified by using a CO{sub 2} fixation solution process in the presence of tetra n-butyl ammonium bromide (TBAB) as catalyst and the modified treated resin was treated by cloisite 30B as nano additive. The Unmodified epoxy resin (UME), CO{sub 2} fixated modified epoxy resin (CFME), and CFME/clay nano composite (CFMEN), were cured by diethylenetriamine (DETA). A cycloaliphatic compound as a reactive diluent was used to control the viscosity of high viscose CFME. The exfoliation of organoclay in UME and CFME was investigated by X-ray diffraction and activation energy was computed using the advanced integral isoconversional method. The activation energy dependency demonstrated that the mechanism of UME curing did not change in the presence of nanoclay. In contrast, the CO{sub 2} fixation results showed a significant change in the activation energy dependency. The Thermal stability parameters include the initial degradation temperature (IDT), the temperature at the maximum rate of weight loss (T{sub max}), and the decomposition activation energy (E{sub d}) were determined by thermal gravimetry analysis. Dynamic mechanical thermal analysis measurements showed that the presence of organoclay in CFME increases the T{sub g} of nano composite in contrast to UME. The fracture roughness of UME, CFME and CFNE were determined by scanning electron microscope. The exfoliated UME/1%clay nanocomposite was confirmed by TEM image. - Highlights: • A new epoxy resin was synthesized using CO{sub 2} fixation reaction. • The synthesized epoxy resin was modified by an organo nano-clay. • CO{sub 2} fixation noticeably changed the curing mechanism. • CO{sub 2} fixation reaction consumes CO{sub 2} which is a harmful greenhouse gas.

  2. Preparation and Electrochemical Properties of Graphene/Epoxy Resin Composite Coating

    Science.gov (United States)

    Liao, Zijun; Zhang, Tianchi; Qiao, Sen; Zhang, Luyihang

    2017-11-01

    The multilayer graphene powder as filler, epoxy modified silicone resin as film-forming agent, anticorrosion composite coating has been created using sand dispersion method, the electrochemical performance was compared with different content of graphene composite coating and pure epoxy resin coating. The open circuit potential (OCP), potentiodynamic polarization curves (Tafel Plot) and electrochemical impedance spectroscopy (EIS) were tested. The test results showed that the anti-corrosion performance of multilayer graphene added has improved greatly, and the content of the 5% best corrosion performance of graphene composite coating.

  3. Aspects of the Fracture Toughness of Carbon Nanotube Modified Epoxy Polymer Composites

    Science.gov (United States)

    Mirjalili, Vahid

    Epoxy resins used in fibre reinforced composites exhibit a brittle fracture behaviour, because they show no sign of damage prior to a catastrophic failure. Rubbery materials and micro-particles have been added to epoxy resins to improve their fracture toughness, which reduces strength and elastic properties. In this research, carbon nanotubes (CNTs) are investigated as a potential toughening agent for epoxy resins and carbon fibre reinforced composites, which can also enhance strength and elastic properties. More specifically, the toughening mechanisms of CNTs are investigated theoretically and experimentally. The effect of aligned and randomly oriented carbon nanotubes (CNTs) on the fracture toughness of polymers was modelled using Elastic Plastic Fracture Mechanics. Toughening from CNT pull-out and rupture were considered, depending on the CNTs critical length. The model was used to identify the effect of CNTs geometrical and mechanical properties on the fracture toughness of CNT-modified epoxies. The modelling results showed that a uniform dispersion and alignment of a high volume fraction of CNTs normal to the crack growth plane would lead to the maximum fracture toughness enhancement. To achieve a uniform dispersion, the effect of processing on the dispersion of single walled and multi walled CNTs in epoxy resins was investigated. An instrumented optical microscope with a hot stage was used to quantify the evolution of the CNT dispersion during cure. The results showed that the reduction of the resin viscosity at temperatures greater than 100 °C caused an irreversible re-agglomeration of the CNTs in the matrix. The dispersion quality was then directly correlated to the fracture toughness of the modified resin. It was shown that the fine tuning of the ratio of epoxy resin, curing agent and CNT content was paramount to the improvement of the base resin fracture toughness. For the epoxy resin (MY0510 from Hexcel), an improvement of 38% was achieved with 0.3 wt

  4. Nonlinear DC Conduction Behavior in Graphene Nanoplatelets/Epoxy Resin Composites

    Science.gov (United States)

    Yuan, Yang; Wang, Qingguo; Qu, Zhaoming

    2018-01-01

    Graphene nanoplatelets (GNPs)/Epoxy resin (ER) with a low percolation threshold were fabricated. Then the nonlinear DC conduction behavior of GNPs/ER composites was investigated, which indicates that dispersion, exfoliation level and conductivity of GNPs in specimens are closely related to the conduction of composites. Moreover, it could be seen that the modified graphene nanoplatelets made in this paper could be successfully used for increasing the electric conductivity of the epoxy resin, and the GNPs/ER composites with nonlinear conduction behavior have a good application prospects in the field of intelligent electromagnetic protection.

  5. Preparation and Characterization of Liquid Crystalline Polyurethane/Al2O3/Epoxy Resin Composites for Electronic Packaging

    Directory of Open Access Journals (Sweden)

    Shaorong Lu

    2012-01-01

    Full Text Available Liquid crystalline polyurethane (LCPU/Al2O3/epoxy resin composites were prepared by using LCPU as modifier. The mechanical properties, thermal stability, and electrical properties of the LCPU/Al2O3/epoxy resin composites were investigated systematically. The thermal oxidation analysis indicated that LCPU/Al2O3/epoxy resin composites can sustain higher thermal decomposition temperature. Meanwhile, coefficient of thermal expansion (CTE was also found to decrease with addition of LCPU and nano-Al2O3.

  6. Physico-Chemical Studies Involving Incorporation of Radioactive and Industrial Waste In Cement-Epoxy Resin Matrix

    International Nuclear Information System (INIS)

    Sayed, M.S.; Hafez, N.

    1999-01-01

    Cement and epoxy resin as chemical additives are proposed to incorporate different types of wastes. The study was extended to prepare different mixtures of cement and epoxy resin in presence of some toxic ions. The studied ions were Cd II, Ni II, Cu II, Fe III, Ce IV, 154+152 Eu, phenol and toluene. The physical, mechanical and leaching properties of the mixtures were studied. The thermal analysis and infrared spectra were also investigated. It was observed that all the studied properties of the epoxy modified cement as a disposal matrix was improved

  7. Occupational exposure to epoxy resins

    NARCIS (Netherlands)

    Terwoert, J.; Kersting, K.

    2014-01-01

    Products based on epoxy resins as a binder have become popular in various settings, among which the construction industry and in windmill blade production, as a result of their excellent technical properties. However, due to the same properties epoxy products are a notorious cause of allergic skin

  8. The characteristics of epoxy resin cured by {gamma}-ray and E-beam

    Energy Technology Data Exchange (ETDEWEB)

    Nho, Y.C. E-mail: ycnho@kaeri.re.kr; Kang, Phil Hyun; Park, Jong Seok

    2004-10-01

    Epoxy resins are widely used as high-performance thermosetting resins for many industrial applications. In this study, the effect of an electron beam (E-beam) and {gamma}-ray irradiation on the curing of epoxy resins was investigated. Diglycidyl ether of bisphenol-A(DGEBA), diglycidyl ether of bisphenol-F(DGEBF) as epoxy resins, triarylsulfonium hexafluoroantimonate(TASHFA), and triarylsulfonium hexafluorophosphate(TASHFP) as initiators were used in this study. The chemical and mechanical characteristics of irradiated epoxy resins were compared after curing of E-beam and {gamma}-ray irradiation up to 50 kGy in N{sub 2} and air atmosphere. We ascertained the effect of oxygen on the radiation curing of epoxy resin. The thermal properties of cured epoxy were investigated using DMA and TGA. Mechanical properties such as flexural strength were measured. The chemical structures of cured epoxy were characterized by FT-NIR. The gel fraction and the stress at yield of epoxy resins irradiated by E-beam and {gamma}-ray in N{sub 2} atmosphere were also compared with those of epoxy resins irradiated by E-beam and {gamma}-ray in air.

  9. Surface characterization and stability of an epoxy resin surface modified with polyamines grafted on polydopamine

    Energy Technology Data Exchange (ETDEWEB)

    Schaubroeck, David, E-mail: David.Schaubroeck@elis.ugent.be [Center for Microsystems Technology (CMST), imec and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium); Vercammen, Yannick; Van Vaeck, Luc [Biomolecular and Analytical Mass Spectrometry, University of Antwerp, Universiteitsplein 1, B-2610 Wilrijk (Belgium); Vanderleyden, Els; Dubruel, Peter [Polymer Chemistry and Biomaterials Research Group, Ghent University, Krijgslaan 281 S4 bis, B-9000 Ghent (Belgium); Vanfleteren, Jan [Center for Microsystems Technology (CMST), imec and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium)

    2014-06-01

    This paper reports on polydopamine and polyamine surface modifications of an etched epoxy cresol novolac (ECN) resin using the ‘grafting to’ method. Three different polyamines are used for the grafting reactions: branched polyethyleneimine (B-PEI), linear polyethyleneimine (L-PEI) and diethylenetriamine (DETA). These modifications are compared to control materials prepared via direct deposition of polyamines. The stability of the modifications toward a concentrated hydrochloric acid (HCl) environment is evaluated. The modified surfaces are characterized with scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and time-of-flight static secondary ion mass spectroscopy (TOF-S-SIMS).

  10. Seawater Durability of Nano-Montmorillonite Modified Single-Lap Joining Epoxy Composite Laminates

    OpenAIRE

    ULUS, Hasan; KAYBAL, Halil Burak; DEMİR, Okan; TATAR, Ahmet Caner; SENYURT, Muhammed Ali; AVCI, Ahmet

    2018-01-01

    The objective of this study was to investigate of nano-montmorillonite modified epoxy composite single-lap bonded joints, after being exposed to seawater immersion in order to understand the effect of seawater environment on their performance. To prepare the nano adhesives, nano montmorillonite (2 wt %) was incorporated into epoxy resin. Composite bonded specimens which manufactured with VARIM (Vacuum Assisted Resin Infusion Method) were prepared accordance with ASTM D5868-01 and immersed in ...

  11. Optical emission behavior and radiation resistance of epoxy resins

    International Nuclear Information System (INIS)

    Kawanishi, Shunichi; Udagawa, Akira; Hagiwara, Miyuki

    1987-11-01

    To make clear a mechanism of radiation resistance of epoxy resin systems, a role of energy trapping site induced in bisphenol A type epoxy resins cured with 4 kinds of aromatic amines (Φ N ) was studied in comparison with the case of aliphatic amine curing system through a measurement of optical emission. In the system of the epoxy resin cured with DETA, the optical emission from an excited state of bisphenol A unit of epoxy resin and a charge transfer complex was observed. On the other hand, the optical emission from Φ N was observed in the aromatic amine curing system. Their excitation spectrum consists of peaks of absorption spectrum of BA and those of Φ N , showing that the excited state of Φ N is formed through the excitation of both BA and Φ N . Therefore, the excited energy of BA transfers to the excited state of Φ N . Emission intensity of Φ N band was 20 ∼ 100 times as large as that of BA. These results indicate that the radiation energy is effectively released as an optical emission from excited state of Φ N in the epoxy resin when cured with aromatic amine. It can be concluded from the above results that aromatic amine hardeners contribute to enhancement of the radiation resistance of epoxy resin by acting as an energy transfer agent. (author)

  12. Cure monitoring of epoxy resin by using fiber bragg grating sensor

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Jin Hyuk [KEPCO, Naju (Korea, Republic of); Kim, Dae Hyun [Dept. of Mechanical and Automotive Engineering, Seoul National University of Science and Technology, Seoul (Korea, Republic of)

    2016-06-15

    In several industrial fields, epoxy resin is widely used as an adhesive for co-curing and manufacturing various structures. Controlling the manufacturing process is required for ensuring robust bonding performance and the stability of the structures. A fiber optic sensor is suitable for the cure monitoring of epoxy resin owing to the thready shape of the sensor. In this paper, a fiber Bragg grating (FBG) sensor was applied for the cure monitoring of epoxy resin. Based on the experimental results, it was demonstrated that the FBG sensor can monitor the status of epoxy resin curing by measuring the strain caused by volume shrinkage and considering the compensation of temperature. In addition, two types of epoxy resin were used for the cure-monitoring; moreover, when compared to each other, it was found that the two types of epoxy had different cure-processes in terms of the change of strain during the curing. Therefore, the study proved that the FBG sensor is very profitable for the cure-monitoring of epoxy resin.

  13. Thermoset Blends of an Epoxy Resin and Polydicyclopentadiene

    Energy Technology Data Exchange (ETDEWEB)

    Rohde, Brian J.; Le, Kim Mai; Krishnamoorti, Ramanan; Robertson, Megan L.

    2016-12-13

    The mechanical properties of two chemically distinct and complementary thermoset polymers were manipulated through development of thermoset blends. The thermoset blend system was composed of an anhydride-cured diglycidyl ether of bisphenol A (DGEBA)-based epoxy resin, contributing high tensile strength and modulus, and polydicyclopentadiene (PDCPD), which has a higher toughness and impact strength as compared to other thermoset polymers. Ultra-small-angle and small-angle X-ray scattering analysis explored the morphology of concurrently cured thermoset blends, revealing a macroscopically phase separated system with a surface fractal structure across blended systems of varying composition. The epoxy resin rich and PDCPD rich phases exhibited distinct glass transitions (Tg’s): the Tg observed at higher temperature was associated with the epoxy resin rich phase and was largely unaffected by the presence of PDCPD, whereas the PDCPD rich phase Tg systematically decreased with increasing epoxy resin content due to inhibition of dicyclopentadiene ring-opening metathesis polymerization. The mechanical properties of these phase-separated blends were in reasonable agreement with predictions by the rule of mixtures for the blend tensile strength, modulus, and fracture toughness. Scanning electron microscopy analysis of the tensile and fracture specimen fracture surfaces showed an increase in energy dissipation mechanisms, such as crazing, shear banding, and surface roughness, as the fraction of the more ductile component, PDPCD, increased. These results present a facile method to tune the mechanical properties of a toughened thermoset network, in which the high modulus and tensile strength of the epoxy resin can be largely retained at high epoxy resin content in the blend, while increasing the fracture toughness.

  14. Formulation of eb-curable epoxy resin : some important parameters

    International Nuclear Information System (INIS)

    Dahlan bin Haji Mohd; Hosoi, Fumio; Sasaki, Takashi

    1989-01-01

    The works on the electron-beam curing of surface coatings using epoxy acrylic-based resins were discussed. The works covered among other things the effect of molecular weights of the resins on the physical properties of coatings and their physical and chemical characterizations. The emphasis was given to formulating the resins applicable to surface coatings. Curings were done on a low-energy electron beam accelerator operating at 250 kV. A number of parameters deemed important to formulations, such as the molecular weights of the oligomers and monomers, monomer ratios, and HEA additions were explored. It was found that one could modify the physical properties of the coatings by changing or adjusting those parameters. (author)

  15. A study regarding friction behaviour of lysine and isoleucine modified epoxy matrix

    Science.gov (United States)

    Bălan, I.; Bosoancă, R.; Căpăţină, A.; Graur, I.; Bria, V.; Ungureanu, C.

    2017-02-01

    The aim of this study is to point out the effect of L-lysine and L-isoleucine used as modifying agents for epoxy resins. The amino acids are largely used to turn the usual polymers in bio-compatible materials but they effect also other significant proprieties of formed materials. The general study developed in Polymer Composite Laboratory is focused on analysis of 14 amino acids used as modifying agents but the two above mentioned showed a special behaviour namely they re-crystalized during the polymerization of the matrix. The coefficient of friction was obtained through the calculation of friction torque measured with a loaded cell sensor. As far as we know, there is no report on the friction proprieties of amino acids modified epoxy resins.

  16. A study on the characteristics of modified and novolac type epoxy resin based neutron shielding material

    Energy Technology Data Exchange (ETDEWEB)

    Cho, Soo Haeng; Hong, Sun Seok; Oh, Seung Chul; Do, Jae Bum [Korea Atomic Energy Research Institute, Taejon (Korea)

    1998-10-01

    Because the exposure to radiation in the nuclear facilities can be fatal to human, it is important to reduce the radiation dose level to a tolerable level. The purpose of this study is to develop highly effective neutron shielding materials for the shipping and storage cask of radioactive materials or in the nuclear/radiation facilities. In this study, we developed modified and novolac type epoxy resin based neutron shielding materials and their various material properties, including neutron shielding ability, prolonged time heat resistance, thermal and mechanical properties were evaluated experimently. (author). 31 refs., 27 figs., 16 tabs.

  17. Influence of the reaction stoichiometry on the mechanical and thermal properties of SWCNT-modified epoxy composites

    International Nuclear Information System (INIS)

    Ashrafi, Behnam; Johnston, Andrew; Martinez-Rubi, Yadienka; Kingston, Christopher T; Simard, Benoit; Khoun, Lolei; Yourdkhani, Mostafa; Hubert, Pascal

    2013-01-01

    Previous studies suggest that carbon nanotubes (CNTs) have a considerable influence on the curing behavior and crosslink density of epoxy resins. This invariably has an important effect on different thermal and mechanical properties of the epoxy network. This work focuses on the important role of the epoxy/hardener mixing ratio on the mechanical and thermal properties of a high temperature aerospace-grade epoxy (MY0510 Araldite as an epoxy and 4,4′-diaminodiphenylsulfone as an aromatic hardener) modified with single-walled carbon nanotubes (SWCNTs). The effects of three different stoichiometries (stoichiometric and off-stoichiometric) on various mechanical and thermal properties (fracture toughness, tensile properties, glass transition temperature) of the epoxy resin and its SWCNT-modified composites were obtained. The results were also supported by Raman spectroscopy and scanning electron microscopy (SEM). For the neat resin, it was found that an epoxy/hardener molar ratio of 1:0.8 provides the best overall properties. In contrast, the pattern in property changes with the reaction stoichiometry was considerably different for composites reinforced with unfunctionalized SWCNTs and reduced SWCNTs. A comparison among composites suggests that a 1:1 molar ratio considerably outperforms the other two ratios examined in this work (1:0.8 and 1:1.1). This composition at 0.2 wt% SWCNT loading provides the highest overall mechanical properties by improving fracture toughness, ultimate tensile strength and ultimate tensile strain of the epoxy resin by 40%, 34%, 54%, respectively. (paper)

  18. Effects of Surface Treatments of Montmorillonite Nanoclay on Cure Behavior of Diglycidyl Ether of Bisphenol A Epoxy Resin

    International Nuclear Information System (INIS)

    Tcherbi-Narteh, A.; Hosur, M.V.; Triggs, E.; Jelaani, S.

    2013-01-01

    Diglycidyl ether of Bisphenol A (DGEBA) based SC-15 epoxy resin was modified with three different commercially available montmorillonite (MMT) nanoclay: Nanomer I.28E and Cloisite 10A and 30B. Cure behavior of nanocomposites was studied using a variety of techniques. Primary focus of this study was to investigate influence of different surface modifications of MMT nanoclay on rheological properties and cure behavior of SC-15 epoxy resin. By adding MMT to SC-15 epoxy resin, chemistry of the epoxy is altered leading to changes in rheological properties and ultimately enthalpy and activation energy of reactions. Addition of Nanomer I.28E delayed gelation, while Cloisite 10A and 30B accelerated gelation, regardless of the curing temperature. Activation energy of reaction was lower with the addition of Nanomer I.28E and Cloisite 10A and higher for Cloisite 30B compared to neat SC-15 epoxy composite.

  19. Epoxy-resin adhesive and method for bonding using such an epoxy resin adhesive

    NARCIS (Netherlands)

    Bhowmik, S.; Poulis, J.A.; Benedictus, R.

    2008-01-01

    The invention relates to an epoxy resin adhesive comprising a dotation of nano-substances, wherein the nano- substances are selected from the group comprising carbon-fibre nanotubes, carbon nano-fibres, silicate nano powders, and wherein the nano-substances are dispersed in the adhesive with a

  20. Radiation curing of γ-Al2O3 filled epoxy resin

    International Nuclear Information System (INIS)

    Kang, Phil Hyun; Kim, Dong Jin; Nho, Young Chang

    2003-01-01

    Epoxy resins are widely utilized as high performance thermosetting resins for many industrial applications but characterized by a relatively low toughness. Recently, the incorporation with rigid inorganic was suggested to improve the mechanical properties of epoxy resins. In the present work, an attempt has been taken to disperse nano-sized γ- Al 2 O 3 particles into diglycidyl ether of bisphenol-A (DGEBA) epoxy resins for improvement of the mechanical properties. These hybrid epoxy-alumina composites were prepared using by the γ-ray curing technique that was conducted with 100kGy under nitrogen at room temperature. The composites were characterized by determining gel content, UTM (Instron model 4443), SEM, FT-IR studies

  1. Study on epoxy resin modified by polyether ionic liquid

    Science.gov (United States)

    Jin, X. C.; Guo, L. Y.; Deng, L. L.; Wu, H.

    2017-06-01

    Chloride 1-carboxyl polyether-3-methyl imidazole ionic liquid (PIIL) was synthesized. Then blended with epoxy resin(EP) to prepare the composite materials of PIIL/EP, which cured with aniline curing agent. The structure and curing performance of PIIL/EP were determined by FT-IR and DSC. The effects of the content of PIIL on strength of EP were studied. The results show that the PIIL was the target product. The strength was improved significantly with increase of the PIIL content. The obvious rubber elasticity of PIIL/EP after cured was showed when the content of PIIL accounts for 40% and the impact strength was up to 15.95kJ/m2.

  2. Thermo-mechanical characterization of siliconized E-glass fiber/hematite particles reinforced epoxy resin hybrid composite

    Energy Technology Data Exchange (ETDEWEB)

    Arun Prakash, V.R., E-mail: vinprakash101@gmail.com; Rajadurai, A., E-mail: rajadurai@annauniv.edu.in

    2016-10-30

    Highlights: • Particles dimension have reduced using Ball milling process. • Importance of surface modification was explored. • Surface modification has been done to improve adhesion of fiber/particles with epoxy. • Mechanical properties has been increased by adding modified fiber and particles. • Thermal properties have been increased. - Abstract: In this present work hybrid polymer (epoxy) matrix composite has been strengthened with surface modified E-glass fiber and iron(III) oxide particles with varying size. The particle sizes of 200 nm and <100 nm has been prepared by high energy ball milling and sol-gel methods respectively. To enhance better dispersion of particles and improve adhesion of fibers and fillers with epoxy matrix surface modification process has been done on both fiber and filler by an amino functional silane 3-Aminopropyltrimethoxysilane (APTMS). Crystalline and functional groups of siliconized iron(III) oxide particles were characterized by XRD and FTIR spectroscopy analysis. Fixed quantity of surface treated 15 vol% E-glass fiber was laid along with 0.5 and 1.0 vol% of iron(III) oxide particles into the matrix to fabricate hybrid composites. The composites were cured by an aliphatic hardener Triethylenetetramine (TETA). Effectiveness of surface modified particles and fibers addition into the resin matrix were revealed by mechanical testing like tensile testing, flexural testing, impact testing, inter laminar shear strength and hardness. Thermal behavior of composites was evaluated by TGA, DSC and thermal conductivity (Lee’s disc). The scanning electron microscopy was employed to found shape and size of iron(III) oxide particles adhesion quality of fiber with epoxy matrix. Good dispersion of fillers in matrix was achieved with surface modifier APTMS. Tensile, flexural, impact and inter laminar shear strength of composites was improved by reinforcing surface modified fiber and filler. Thermal stability of epoxy resin was improved

  3. Epoxy-based carbon nanotubes reinforced composites

    CSIR Research Space (South Africa)

    Kesavan Pillai, Sreejarani

    2011-04-01

    Full Text Available of the three major epoxy resin producers worldwide [May, 1987]. Epoxy resin is most commonly used as a matrix for advanced composites due to their superior thermal, mechanical and electrical properties; dimensional stability and chemical resistance. Epoxy... and modifiers to create products with an almost unlimited range and variety of performance properties [The epoxy book, 2000]. Epoxy resins are widely used as high-grade synthetic resins, for example, in the electronics, aeronautics and astronautic industries...

  4. Epoxy resin systems for FGD units

    International Nuclear Information System (INIS)

    Brytus, V.; Puglisi, J.S.

    1984-01-01

    This paper discusses ongoing research work which is directed towards epoxy resins and curing agents which are designed to withstand aggressive environments. This work includes not only a chemical description of the materials involved, but the application testing necessary to verify the usefulness of these systems. It demonstrates that new high performance epoxy systems are superior to those which traditionally come to mind when one thinks epoxy. Finally, it discusses the results of testing designed specifically to screen candidates for use in FGD units

  5. Epoxy resin/phosphonium ionic liquid/carbon nanofiller systems: Chemorheology and properties

    Directory of Open Access Journals (Sweden)

    H. Maka

    2014-10-01

    Full Text Available Epoxy nanocomposites with commercial carbon nanotubes (CNT or graphene (GN have been prepared using phosphonium ionic liquid [trihexyltetradecylphosphonium bis(2,4,4-trimethylpentyl phosphinate, IL-f]. IL-f served simultaneously as nanofiller dispersing medium and epoxy resin catalytic curing agent. An influence of IL-f/epoxy weight ratio (3, 6 and 9/100, phr, carbon nanofiller type and content on viscosity of epoxy compositions during storage at ambient temperature was evaluated. Curing process was controlled for neat and CNT or GN modified epoxy compositions (0.25-1.0 wt.% load using differential scanning calorimetry and rheometry. Epoxy nanocomposites exhibited slightly increased glass transition temperature values (146 to 149°C whereas tan δ and storage modulus decreased (0.30 to 0.27 and 2087 to 1070 MPa, respectively as compared to reference material. Crosslink density regularly decreased for composites with increasing CNT content (11 094 to 7 020 mol/m3. Electrical volume resistivity of the nanocomposites was improved in case of CNT to 4•101 Ω•m and GN to 2•105 Ω•m (nanofiller content 1 wt.%. Flame retardancy was found for modified epoxy materials with as low GN and phosphorus content as 0.25 and 0.7 wt.%, respectively (increase of limiting oxygen index to 26.5%.

  6. UV curing silicon-containing epoxy resin and its glass cloth reinforced composites

    International Nuclear Information System (INIS)

    Yang Guang; Tang Zhuo; Huang Pengcheng

    2007-01-01

    A UV-curable cationic silicon-containing epoxy resin formulation was developed. The gel conversion of the cured resin after 10-min UV irradiation reached 80% in the presence of 5% diaryliodonium salt photoinitiator and 5.5% polyol chain transfer agent by cationic ring-opening polymerization. The glass cloth-reinforced composites were fabricated with the silicon-containing epoxy resin using the wet lay-up technique and UV irradiation. The mechanical properties of the composites were evaluated. Compared with glass cloth reinforced bisphenol A epoxy resin matrix composites, the silicon-containing epoxy resin matrix composites possessed higher tensile strength and interlayer shear strength which was 158.5MPa and 9.9MPa respectively while other mechanical properties such as flexural property and tensile modulus were similar. (authors)

  7. Viscoelastic properties of graphene-based epoxy resins

    Science.gov (United States)

    Nobile, Maria Rossella; Fierro, Annalisa; Rosolia, Salvatore; Raimondo, Marialuigia; Lafdi, Khalid; Guadagno, Liberata

    2015-12-01

    In this paper the viscoelastic properties of an epoxy resin filled with graphene-based nanoparticles have been investigated in the liquid state, before curing, by means of a rotational rheometer equipped with a parallel plate geometry. Exfoliated graphite was prepared using traditional acid intercalation followed by a sudden treatment at high temperature (900°C). The percentage of exfoliated graphite was found to be 56%. The epoxy matrix was prepared by mixing a tetrafunctional precursor with a reactive diluent which produces a significant decrease in the viscosity of the epoxy precursor so that the dispersion step of nanofillers in the matrix can easily occur. The hardener agent, the 4,4-diaminodiphenyl sulfone (DDS), was added at a stoichiometric concentration with respect to all the epoxy rings. The inclusion of the partially exfoliated graphite (pEG) in the formulated epoxy mixture significantly modifies the rheological behaviour of the mixture itself. The epoxy mixture, indeed, shows a Newtonian behaviour while, at 3 wt % pEG content, the complex viscosity of the nanocomposite clearly shows a shear thinning behaviour with η* values much higher at the lower frequencies. The increase in complex viscosity with the increasing of the partially exfoliated graphite content was mostly caused by a dramatic increase in the storage modulus. All the graphene-based epoxy mixtures were cured by a two-stage curing cycles: a first isothermal stage was carried out at the lower temperature of 125°C for 1 hour while the second isothermal stage was performed at the higher temperature of 200°C for 3 hours. The mechanical properties of the cured nanocomposites show high values in the storage modulus and glass transition temperature.

  8. Structure and Performance of Epoxy Resin Cladded Graphite Used as Anode

    Science.gov (United States)

    Zhou, Zhentao; Li, Haijun

    This paper is concerning to prepare modified natural graphite which is low-cost and advanced materials used as lithium ion battery anode using the way of cladding natural graphite with epoxy resin. The results shows that the specific capacity and circular performance of the modified natural graphite, which is prepared in the range of 600°C and 1000°C, have been apparently improved compare with the not-modified natural graphite. The first reversible capacity of the modified natural graphite is 338mAh/g and maintain more than 330mAh/g after 20 charge/discharge circles.

  9. Surface modification of an epoxy resin with polyamines and polydopamine: Adhesion toward electroless deposited copper

    Energy Technology Data Exchange (ETDEWEB)

    Schaubroeck, David, E-mail: David.Schaubroeck@elis.ugent.be [Center for Microsystems Technology (CMST), IMEC and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium); Mader, Lothar [Center for Microsystems Technology (CMST), IMEC and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium); Dubruel, Peter [Polymer Chemistry and Biomaterials Research Group, Ghent University, Krijgslaan 281 S4 bis, B-9000 Ghent (Belgium); Vanfleteren, Jan [Center for Microsystems Technology (CMST), IMEC and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium)

    2015-10-30

    Highlights: • Surface modifications of epoxy resins with polydopamine and grafted polyamines can significantly increase the adhesion toward electroless deposited copper. • A clear characterization of the copper/epoxy interphase is provided by SEM analyses of cross sections. • Tailored conditions such as etching time (roughness) and electroless deposition temperature are needed to increase the adhesion of the modified surfaces. - Abstract: In this paper the influence of the epoxy roughness, surface modifications and ELD (electroless copper deposition) temperatures on the adhesive strength of the copper is studied. Good adhesion at low roughness values is targeted due to their applicability in high density electronic circuits. Roughened epoxy surfaces are modified with adsorbed polyamines, polydopamine and polyamines grafted to polydopamine. Next the, adhesive strength of ELD copper is determined with peel strength measurements and the interphases are examined with SEM (scanning electron microscopy). Polydopamine and polyamines grafted to polydopamine can lead to increased adhesive strength at lower roughness values compared to the non-modified samples at specific plating temperatures.

  10. Synthesis and Thermal Properties of a Novel Nitrogen-containing Epoxy Resin

    Institute of Scientific and Technical Information of China (English)

    Xing Hong ZHANG; Hong Mei WAN; Yu Qin MIN; Zuo FANG; Guo Rong QI

    2005-01-01

    A new nitrogen-containing epoxy resin (XT resin) was synthesized from chain extension of xylenephenolformaldehyde resin (XPF) and triglycidyl isocyanurate (TGIC) in the presence of base catalyst. FT-IR and 1H-NMR analysis confirmed the chemical structure of XT resin. It was cured with dicyandiamide (DICY) and diaminodiphenyl sulfone (DDS). Dynamic mechanical analysis (DMA) results showed that the introduction of triazine ring provides epoxy polymer with good thermal stability. Furthermore, high char yields at 800℃ in thermogravimetric (TGA)analysis indicated that XT resin had potential flame retardance.

  11. Occupational contact dermatitis caused by aniline epoxy resins in the aircraft industry.

    Science.gov (United States)

    Pesonen, Maria; Suuronen, Katri; Jolanki, Riitta; Aalto-Korte, Kristiina; Kuuliala, Outi; Henriks-Eckerman, Maj-Len; Valtanen, Ilona; Alanko, Kristiina

    2015-08-01

    Tetraglycidyl-4,4'-methylenedianiline (TGMDA) is an aniline epoxy resin used in, for example, resin systems of pre-impregnated composite materials (prepregs) of the aircraft industry. Allergic contact dermatitis caused by TGMDA in prepregs has been described previously. To report on 9 patients with occupational allergic contact dermatitis caused by TGMDA in epoxy glues used in helicopter assembly. The patients were examined with patch testing at the Finnish Institute of Occupational Health in 2004-2009. The first patient was diagnosed by testing both components of two epoxy glues from the workplace, and was also tested with glue ingredients, including TGMDA. The following patients were tested with the glues and TGMDA. The resin parts of the glues were analysed for their epoxy compounds, including TGMDA. All of the patients had a patch test reaction to one or both of the resin parts of the TGMDA-containing glues. Eight of them had a strong allergic reaction to TGMDA, and one had a doubtful reaction to TGMDA. Two of the patients also had an allergic reaction to triglycidyl-p-aminophenol (TGPAP), another aniline epoxy resin, which was not present in the TGMDA-containing glues. In aircraft industry workers with suspected occupational dermatitis, aniline epoxy resins should be considered and patch tested as possible contact allergens. © 2015 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

  12. Physical and chemical durability of cement impregnated epoxy resin

    International Nuclear Information System (INIS)

    Suryantoro

    1997-01-01

    Immobilization of simulation radioactive waste contains Cs and Sr with cement impregnated epoxy resin has been done. Low level liquid waste in 30% weight mixed cement homogeneously and then set in its curing time about 28 days. Waste from was impregnated with epoxy resin (Bisphenol-A-diglycidylether) and use Triethylenteramin as catalyst. the sample of cement impregnated epoxy resin 2.5 cm x 2.5 cm in diameter and length was tested by Paul Weber. The compressive strength was obtained of 4.08 kN.cm - 2. The sochxlet apparatus was run on flow rate of 300 ml/hour at 100 o C and during 24 hours. The leaching rate of Cs was round on 5.5 x 10 - 4 g.cm - 2.d - 1 and Sr was 6.1 x 10 - 4 g.cm - 2.d - 1 (author)

  13. Thermal properties and corrosion resistance of organoclay/epoxy resin film

    Science.gov (United States)

    Baiquni, M.; Soegijono, B.

    2018-03-01

    Hybrid materials organoclay/epoxy resin films were prepared by varying organoclay content in epoxy resin as a matrix. The film were investigated by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), and thermal conductivity. TGA and FT-IR results confirmed that the melting temperature shifted to a lower point. The thermal conductivity and corrosion resistant generally increase with increasing organoclay content. The changes on these properties may due to cross link between organoclay and epoxy.

  14. Radiation curing of {gamma}-Al{sub 2}O{sub 3} filled epoxy resin

    Energy Technology Data Exchange (ETDEWEB)

    Kang, Phil Hyun; Kim, Dong Jin; Nho, Young Chang [KAERI, Taejon (Korea, Republic of)

    2003-10-01

    Epoxy resins are widely utilized as high performance thermosetting resins for many industrial applications but characterized by a relatively low toughness. Recently, the incorporation with rigid inorganic was suggested to improve the mechanical properties of epoxy resins. In the present work, an attempt has been taken to disperse nano-sized {gamma}- Al{sub 2}O{sub 3} particles into diglycidyl ether of bisphenol-A (DGEBA) epoxy resins for improvement of the mechanical properties. These hybrid epoxy-alumina composites were prepared using by the {gamma}-ray curing technique that was conducted with 100kGy under nitrogen at room temperature. The composites were characterized by determining gel content, UTM (Instron model 4443), SEM, FT-IR studies.

  15. Characteristics of epoxy resin/SiO2 nanocomposite insulation: effects of plasma surface treatment on the nanoparticles.

    Science.gov (United States)

    Yan, Wei; Phung, B T; Han, Zhao Jun; Ostrikov, Kostya

    2013-05-01

    The present study compares the effects of two different material processing techniques on modifying hydrophilic SiO2 nanoparticles. In one method, the nanoparticles undergo plasma treatment by using a custom-developed atmospheric-pressure non-equilibrium plasma reactor. With the other method, they undergo chemical treatment which grafts silane groups onto their surface and turns them into hydrophobic. The treated nanoparticles are then used to synthesize epoxy resin-based nanocomposites for electrical insulation applications. Their characteristics are investigated and compared with the pure epoxy resin and nanocomposite fabricated with unmodified nanofillers counterparts. The dispersion features of the nanoparticles in the epoxy resin matrix are examined through scanning electron microscopy (SEM) images. All samples show evidence that the agglomerations are smaller than 30 nm in their diameters. This indicates good dispersion uniformity. The Weibull plot of breakdown strength and the recorded partial discharge (PD) events of the epoxy resin/plasma-treated hydrophilic SiO2 nanocomposite (ER/PTI) suggest that the plasma-treated specimen yields higher breakdown strength and lower PD magnitude as compared to the untreated ones. In contrast, surprisingly, lower breakdown strength is found for the nanocomposite made by the chemically treated hydrophobic particles, whereas the PD magnitude and PD numbers remain at a similar level as the plasma-treated ones.

  16. High performance, rapid thermal/UV curing epoxy resin for additive manufacturing of short and continuous carbon fiber epoxy composites

    Science.gov (United States)

    Lewicki, James

    2018-04-17

    An additive manufacturing resin system including an additive manufacturing print head; a continuous carbon fiber or short carbon fibers operatively connected to the additive manufacturing print head; and a tailored resin operatively connected to the print head, wherein the tailored resin has a resin mass and wherein the tailored resin includes an epoxy component, a filler component, a catalyst component, and a chain extender component; wherein the epoxy component is 70-95% of the resin mass, wherein the filler component is 1-20% of the resin mass, wherein the catalyst component is 0.1-10% of the resin mass, and wherein the chain extender component is 0-50% of the resin mass.

  17. Mechanical Properties of Epoxy and Its Carbon Fiber Composites Modified by Nanoparticles

    Directory of Open Access Journals (Sweden)

    Fang Liu

    2017-01-01

    Full Text Available Compressive properties are commonly weak parts in structural application of fiber composites. Matrix modification may provide an effective way to improve compressive performance of the composites. In this work, the compressive property of epoxies (usually as matrices of fiber composites modified by different types of nanoparticles was firstly investigated for the following study on the compressive property of carbon fiber reinforced epoxy composites. Carbon fiber/epoxy composites were fabricated by vacuum assisted resin infusion molding (VARIM technique using stitched unidirectional carbon fabrics, with the matrices modified with nanosilica, halloysite, and liquid rubber. Testing results showed that the effect of different particle contents on the compressive property of fiber/epoxy composites was more obvious than that in epoxies. Both the compressive and flexural results showed that rigid nanoparticles (nanosilica and halloysite have evident strengthening effects on the compression and flexural responses of the carbon fiber composite laminates fabricated from fabrics.

  18. Wear-resistant and electromagnetic absorbing behaviors of oleic acid post-modified ferrite-filled epoxy resin composite coating

    Science.gov (United States)

    Wang, Wenjie; Zang, Chongguang; Jiao, Qingjie

    2015-03-01

    The post-modified Mn-Zn ferrite was prepared by grafting oleic acid on the surface of Mn-Zn ferrite to inhibit magnetic nanoparticle aggregation. Fourier Transform Infrared (FT-IR) spectroscopy was used to characterize the particle surfaces. The friction and electromagnetic absorbing properties of a thin coating fabricated by dispersing ferrite into epoxy resin (EP) were investigated. The roughness of the coating and water contact angle were measured using the VEECO and water contact angle meter. Friction tests were conducted using a stainless-steel bearing ball and a Rockwell diamond tip, respectively. The complex permittivity and complex permeability of the composite coating were studied in the low frequency (10 MHz-1.5 GHz). Surface modified ferrites are found to improve magnetic particles dispersion in EP resulting in significant compatibility between inorganic and organic materials. Results also indicate that modified ferrite/EP coatings have a lower roughness average value and higher water contact angle than original ferrite/EP coatings. The enhanced tribological properties of the modified ferrite/EP coatings can be seen from the increased coefficient value. The composite coatings with modified ferrite are observed to exhibit better reflection loss compared with the coatings with original ferrite.

  19. A biomimetic approach to enhancing interfacial interactions: polydopamine-coated clay as reinforcement for epoxy resin.

    Science.gov (United States)

    Yang, Liping; Phua, Si Lei; Teo, Jun Kai Herman; Toh, Cher Ling; Lau, Soo Khim; Ma, Jan; Lu, Xuehong

    2011-08-01

    A facile biomimetic method was developed to enhance the interfacial interaction in polymer-layered silicate nanocomposites. By mimicking mussel adhesive proteins, a monolayer of polydopamine was constructed on clay surface by a controllable coating method. The modified clay (D-clay) was incorporated into an epoxy resin, it is found that the strong interfacial interactions brought by the polydopamine benefits not only the dispersion of the D-clay in the epoxy but also the effective interfacial stress transfer, leading to greatly improved thermomechanical properties at very low inorganic loadings. Rheological and infrared spectroscopic studies show that the interfacial interactions between the D-clay and epoxy are dominated by the hydrogen bonds between the catechol-enriched polydopamine and the epoxy.

  20. Influence of hematite nanorods on the mechanical properties of epoxy resin

    Directory of Open Access Journals (Sweden)

    Bogdanović Gordana

    2017-01-01

    Full Text Available The mechanical properties of nanocomposites obtained by incorporation of fairly uniform hematite nanorods (α-Fe2O3 NRs into epoxy resin were studied as a function of the content of the inorganic phase. A thorough microstructural characterization of the α-Fe2O3 NRs and the nanocomposites was performed using transmission electron microscopy (TEM and atomic force microscopy (AFM. The TEM measurements revealed rod-like morphology of the nanofiller with a uniform size distribution (8.5 nm×170 nm, diameter×length. High-magnification TEM and AFM measurements indicated agglomeration of α-Fe2O3 NRs embedded in the epoxy resin. Stress at break, strain at break, elastic modulus and tensile toughness of the nanocomposites were compared with the data obtained for pure epoxy resin. Significant influence of nanofiller on the mechanical properties of epoxy resin, as well as on the glass transition temperature, could be noticed for samples with low contents of the inorganic phase (up to 1 wt. %. [Project of the Serbian Ministry of Education, Science and Technological Development, Grant no. 45020

  1. Synthesis and characterization of cement slurries additives with epoxy resins - kinetics, thermodynamic and calorimetric analysis

    International Nuclear Information System (INIS)

    Tavares, A.M.G.; Andrade Junior, M.A.S.; Cestari, A.R.; Vieira, E.F.S.

    2010-01-01

    Cement has been used in the world, presenting a wide versatility. However, due to its chemical nature, it is subject to several types of chemical damages, especially for agents of acidic nature. With the purpose of increase its life-time, new cement slurries have been modified with the addition of specific additives. The objective of this work is to modify cement slurries with epoxy resins, which promote higher resistance of those materials in relation to acid attacks. Three cement slurries were synthesized with epoxy resins and a standard slurries, which was composed by cement and water. After 30 days of hydration, the samples were characterized by XDR, FTIR and thermal analysis (TG and DSC). The hydration processes of the cement slurries were studied by heat-conduction microcalorimetry. A kinetic study of HCl interaction with the new slurries were performed by the batch methodology at 25, 35, 45 e 55 deg C. It was verified that the addition of the polymers delayed the processes of hydration of the slurries, decreasing the flow of heat released as a function of the amount of added resin and, increased the resistance of those slurries to the acid attack. (author)

  2. Positron lifetime study of electron-irradiated epoxy resins

    International Nuclear Information System (INIS)

    Suevegh, K.; Vertes, A.; Wojnarovits, L.; Foeldiak, G.; Liszkai, L.; Kajcsos, Zs.

    1990-01-01

    Two bisphenol-A type epoxy resins were irradiated by electron beam and studied afterwards by positron lifetime spectroscopy. An interesting result is that despite of the considerable amount of free-radicals, no inhibition of positronium formation was observed in the two epoxies. Nevertheless, several serious differences were detected between the studied polymers. The results suggest that the radiation-resistant properties of epoxies depend strongly on the amount of the curing agent. (author) 8 refs.; 2 figs

  3. Paramagnetic epoxy resin

    Directory of Open Access Journals (Sweden)

    E. C. Vazquez Barreiro

    2017-01-01

    Full Text Available This work illustrates that macrocycles can be used as crosslinking agents for curing epoxy resins, provided that they have appropriate organic functionalities. As macrocycles can complex metal ions in their structure, this curing reaction allows for the introduction of that metal ion into the resin network. As a result, some characteristic physical properties of the metallomacrocycle could be transferred to the new material. The bisphenol A diglycidyl ether (BADGE, n = 0 and hemin (a protoporphyrin IX containing the Fe(III ion, and an additional chloride ligand have been chosen. The new material has been characterized by differential scanning calorimetry (DSC, thermogravimetric analysis (TGA, Fourier Transform Infrared (FT-IR, Nuclear Magnetic Resonance (NMR, Transmission Electron Microscopy (TEM, and magnetic susceptibility measurements. Fe(III remains in the high-spin state during the curing process and, consequently, the final material exhibits the magnetic characteristics of hemin. The loss of the chlorine atom ligand during the cure of the resin allows that Fe(III can act as Lewis acid, catalyzing the crosslinking reactions. At high BADGE n = 0/hemin ratios, the formation of ether and ester bonds occurs simultaneously during the process.

  4. Study on Concrete Containing Recycled Aggregates Immersed in Epoxy Resin

    Directory of Open Access Journals (Sweden)

    Adnan Suraya Hani

    2017-01-01

    Full Text Available In recent decades, engineers have sought a more sustainable method to dispose of concrete construction and demolition waste. One solution is to crush this waste concrete into a usable gradation for new concrete mixes. This not only reduces the amount of waste entering landfills but also alleviates the burden on existing sources of quality natural concrete aggregates. There are too many kinds of waste but here constructions waste will be the priority target that should be solved. It could be managed by several ways such as recycling and reusing the concrete components, and the best choice of these components is the aggregate, because of the ease process of recycle it. In addition, recycled aggregates and normal aggregates were immersed in epoxy resin and put in concrete mixtures with 0%, 5%, 10% and 20% which affected the concrete mixtures properties. The strength of the concrete for both normal and recycled aggregates has increased after immersed the aggregates in epoxy resin. The percentage of water absorption and the coefficient of water permeability decreased with the increasing of the normal and the recycled aggregates immersed in epoxy resin. Generally the tests which have been conducted to the concrete mixtures have a significant results after using the epoxy resin with both normal and recycled aggregates.

  5. Improvement of Mechanical and Dielectric Properties of Epoxy Resin Using CNTs/ZnO Nanocomposite.

    Science.gov (United States)

    Vu, Pham Gia; Truc, Trinh Anh; Chinh, Nguyen Thuy; Tham, Do Quang; Trung, Tran Huu; Oanh, Vu Ke; Hang, To Thi Xuan; Olivier, Marjorie; Hoang, Thai

    2018-04-01

    In this study, carbon nanotubes (CNTs)/ZnO composites had been prepared using the sol-gel method and then incorporated into an epoxy resin for reinforcement of mechanical and electrical properties. Fourier Transform Infrared (FTIR), X-ray diffraction (XRD) Field Emission Scanning Electron Microscope (FE-SEM) analyses show that the ZnO nanoparticles deposited on CNTs were crystallized in a hexagonal wurtzite structure. Average particle size of ZnO deposited on the CNT was about 8 nm. The mechanical and dielectric properties of epoxy containing CNTs/ZnO were investigated in comparison to epoxy resin and epoxy resin containing only CNT or ZnO nanoparticles. The results indicated that tensile strength and elongation at break of the nanocomposite were substantially improved with the presence of CNTs/ZnO at the equal volume. The DSC analysis associate with the dielectric results shows that the behavior of epoxy/CNTs/ZnO is identical to epoxy/ZnO composite, and the CNTs is essential to the distributed arrangement of ZnO in the epoxy resin.

  6. Current-Voltage Characteristics of the Composites Based on Epoxy Resin and Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    Iwona Pełech

    2015-01-01

    Full Text Available Polymer composites based on epoxy resin were prepared. Multiwalled carbon nanotubes synthesized on iron-cobalt catalyst were applied as a filler in a polymer matrix. Chlorine or hydroxyl groups were incorporated on the carbon nanotubes surface via chlorination or chlorination followed by hydroxylation. The effect of functionalized carbon nanotubes on the epoxy resin matrix is discussed in terms of the state of CNTs dispersion in composites as well as electrical properties. For the obtained materials current-voltage characteristics were determined. They had a nonlinear character and were well described by an exponential-type equation. For all the obtained materials the percolation threshold occurred at a concentration of about 1 wt%. At a higher filler concentration >2 wt%, better conductivity was demonstrated by polymer composites with raw carbon nanotubes. At a lower filler concentration <2 wt%, higher values of electrical conductivity were obtained for polymer composites with modified carbon nanotubes.

  7. Shape memory polymers from benzoxazine-modified epoxy

    International Nuclear Information System (INIS)

    Rimdusit, Sarawut; Lohwerathama, Montha; Dueramae, Isala; Hemvichian, Kasinee; Kasemsiri, Pornnapa

    2013-01-01

    Novel shape memory polymers (SMPs) were prepared from benzoxazine-modified epoxy resin. Specimens consisting of aromatic epoxy (E), aliphatic epoxy (N), Jeffamine D230 (D) and BA-a benzoxazine monomer (B) were evaluated. The mole ratio of D/B was used as a mixed curing agent for an epoxy system with a fixed E/N. The effects of BA-a content on the thermal, mechanical and shape memory properties of epoxy-based shape memory polymers (SMPs) were investigated by differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA), flexural test and shape recovery test. The results revealed that the obtained SMPs exhibited a higher flexural strength and flexural modulus than those of the unmodified epoxy-based SMP at room temperature and at 20 ° C above glass transition temperature (T g ). The presence of 1 mol BA-a as a curing agent provided the specimen with the highest T g , i.e. about 72 ° C higher than that of epoxy-based SMP cured by Jeffamine D230. All SMP samples needed only a few minutes to fully recover to their original shape. The samples exhibited high shape fixity (98–99%) and shape recovery ratio (90–100%). In addition, the recovery stress values increased with increasing BA-a mole ratio from 20 to 38 kPa, when BA-a up to 1 mol ratio was added. All of the SMP samples exhibited only minimum change in their flexural strength at the end of a 100 recovery cycles test. (paper)

  8. Differences in interfacial bond strengths of graphite fiber-epoxy resin composites

    Science.gov (United States)

    Needles, H. L.

    1985-01-01

    The effect of epoxy-size and degree of cure on the interfacial bonding of an epoxy-amine-graphite fiber composite system is examined. The role of the fiber-resin interface in determining the overall mechanical properties of composites is poorly understood. A good interfacial adhesive bond is required to achieve maximum stress transfer to the fibers in composites, but at the same time some form of energy absorbing interfacial interaction is needed to achieve high fracture toughening. The incompatibility of these two processes makes it important to understand the nature and basic factors involved at the fiber-resin interface as stress is applied. The mechanical properties including interlaminar shear values for graphite fiber-resin composites are low compared to glass and boron-resin composites. These differences have been attributed to poor fiber-matrix adhesion. Graphite fibers are commonly subjected to post-treatments including application of organic sizing in order to improve their compatibility with the resin matrix and to protect the fiber tow from damage during processing and lay-up. In such processes, sized graphite fiber tow is impregnated with epoxy resin and then layed-up i nto the appropriate configuration. Following an extended ambient temperature cure, the graphite-resin composite structure is cured at elevated temperature using a programmed temperature sequence to cure and then cool the product.

  9. Mechanical properties of epoxy composites with plasma-modified rice-husk-derived nanosilica

    Science.gov (United States)

    Hubilla, Fatima Athena D.; Panghulan, Glenson R.; Pechardo, Jason; Vasquez, Magdaleno R., Jr.

    2018-01-01

    In this study, we explored the use of rice-husk-derived nanosilica (nSiO2) as fillers in epoxy resins. The nSiO2 was irradiated with a capacitively coupled 13.56 MHz radio frequency (RF) plasma using an admixture of argon (Ar) and hexamethyldisiloxane (HMDSO) or 1,7-octadiene (OD) monomers. The plasma-polymerized nSiO2 was loaded at various concentrations (1-5%) into the epoxy matrix. Surface hydrophobicity of the plasma-treated nSiO2-filled composites increased, which is attributed to the attachment of functional groups from the monomer gases on the silica surface. Microhardness increased by at least 10% upon the inclusion of plasma-modified nSiO2 compared with pristine nSiO2-epoxy composites. Likewise, hardness increased with increasing loading volume, with the HMDSO-treated silica composite recording the highest increase. Elastic moduli of the composites also showed an increase of at least 14% compared with untreated nSiO2-filled composites. This work demonstrated the use of rice husk, an agricultural waste, as a nSiO2 source for epoxy resin fillers.

  10. Dermatosis profesional por resina epoxi: Presentación de un caso clínico Professional dermatosis for epoxy resin: A clinical case report

    Directory of Open Access Journals (Sweden)

    S Gaviola

    2008-06-01

    Full Text Available Mostramos un caso de dermatosis profesional originado por plásticos (resinas epoxi y la importancia de la detección precoz. Las resinas epoxi son de gran utilización en todo tipo de industrias (artes graficas, construcción, electrónica, componentes de prótesis traumatológicas, prótesis odontológicas, etc. y sus componentes pueden ser causa de dermatitis de contacto irritativa y por sensibilización.We describe a case of professional dermatosis caused by exposition to plastic products (epoxy resin and importance of early detection. The epoxy resins are widely used in all types of industries (graphics arts, construction, electronics, traumathological and odontological prothesis, etc. and their components may be the cause of contact dermatitis and sensitivity. Risk factors at work with epoxy resins are present during the production base resins, hardening agents, plasticizers and dilutants increase the risk of exposition at work. This requires preventive measures and early diagnosis.

  11. Enhanced actuation performance of piezoelectric fiber composites induced by incorporated BaTiO3 nanoparticles in epoxy resin

    International Nuclear Information System (INIS)

    Wu, Mingliang; Yuan, Xi; Luo, Hang; Chen, Haiyan; Chen, Chao; Zhou, Kechao; Zhang, Dou

    2017-01-01

    Piezoelectric fiber composites (PFCs) have attracted much interest owing to their flexibility and toughness compared with conventional monolithic piezoceramic wafers. The free strain values and actuation property of PFCs strongly depend on the active electric field applied in Pb(Zr 1−x Ti x )O 3 (PZT) fibers. Reducing the dielectric constant mismatch between PZT fiber and the assembling epoxy resin would greatly increase the active electric field in PZT fiber. Therefore, BaTiO 3 (BT) nanoparticles were introduced into the epoxy resin to enhance the dielectric constant. Homogeneous dispersion of BT nanoparticles and tight adhesion with the epoxy resin were achieved through a surface modification by dopamine. The maximum dielectric constant of dopamine modified BT/epoxy (BT@Dop/epoxy) nanocomposites was 10.38 with 12 wt% BT@Dop content at 1 kHz. The maximum free strain of PFCs reached 1820 ppm with 6 wt% BT@Dop content, while PFCs assembled by pure epoxy showed 790 ppm at the same processing condition. The tip displacement of cantilever beam actuated by PFCs reached the peak of 19 mm at the resonance frequency with 6 wt% BT@Dop, which was improved by 90% comparing to PFCs with pure epoxy. - Highlights: • The effect of dielectric mismatch on effective electric field in piezoceramic fibers was explained by a model. • The dispersibility and adhesion of BaTiO 3 nanoparticles in epoxy was improved by the dopamine modification. • The actuation performance increased firstly and then decreased with adding BaTiO 3 nanoparticles. • The maximum free strain and displacement of cantilever beam were up to 1820 ppm and 19 mm, respectively.

  12. Effect of epoxy resin sealing on corrosion resistance of arc spraying aluminium coating using cathode electrophoresis method

    Science.gov (United States)

    Pang, Xuming; Wang, Runqiu; Wei, Qian; Zhou, Jianxin

    2018-01-01

    Arc-sprayed Al coating was sealed with epoxy resin using the cathode electrophoresis method. The anti-corrosion performance of the coatings sealed with epoxy resin was studied by means of a 3.5 wt.% NaCl solution test at 40 °C. For comparison, the anti-corrosion performance of Al coating sealed with boiling water was also performed under the same conditions. The results show that epoxy resin with a thickness of about 20 microns can entirely cover open pores and decreases the surface roughness of the as-sprayed Al coating, and the epoxy resin even permeates into the gaps among lamellar splats from open pores. After corrosion, the thickness of the epoxy resin layer is unchanged and can still cover the as-sprayed Al coating entirely. However, the thickness of Al coating sealed with boiling water decreases from 100 to 40 microns, which indicates that the arc-sprayed Al coating has much better corrosion resistance than the Al coating sealed with boiling water. Meanwhile, the content of substituted benzene ring in the epoxy resin increases, but aromatic ring decreases according to the fourier transform infrared spectra, which will cause the rigidity of the epoxy resin to increase, but the toughness slightly decreases after corrosion.

  13. Allergic Reaction to Polyether Ether Ketone Following Cross-Reactivity to Epoxy Resin.

    Science.gov (United States)

    Kofler, Lukas; Wambacher, Markus; Schweinzer, Katrin; Scherl, Maritta; Kofler, Heinz

    Polyether ether ketone (PEEK) is a thermoplastic polymer frequently used in engineering but also in medical devices. Only 1 case of allergic reaction to PEEK used as an implanted medical device has been reported so far; however, the route of sensitization remained unclear. Here we report on a 62-year-old male patient with a preknown, severe type IV allergy to epoxy resin. He reported strong pain in his shoulder after implantation of a PEEK-containing device after a rotator cuff injury. For testing, the device was implanted in a small pouch subcutaneously on the abdomen. The patient reported massive pain starting 8 hours after the implantation, strictly limited to the procedural area and showing perifocal erythema. A possible explanation of the sensitization mode is the source material for PEEK and epoxy resin, as both are mainly based on bisphenols. An allergic reaction to PEEK with preknown epoxy resin sensitization has not been reported so far. As epoxy resins are a frequent cause of occupational contact dermatitis and PEEK is widely used for medical and nonmedical devices, we believe that this is of great clinical relevance.

  14. Experimental Investigation on Fatigue Behavior of Epoxy Resin under Load and Displacement Controls

    Directory of Open Access Journals (Sweden)

    Mahmood Mehrdad Shokrieh

    2014-12-01

    Full Text Available The mechanical properties of epoxy resin including tensile and flexural modulus, tensile and flexural strength for static conditions are currently studied. The frequency effect as significant parameter at room temperature is investigated and fatigue behavior of the epoxy resin in tension-tension loading conditions for different frequencies of 2, 3 and 5 Hz are obtained. The epoxy resin has been taken under flexural bending fatigue loading and fatigue life is investigated. The results of the experiments show the values of 2.5 and 3 GPa of tensile and flexural modules and 59.98 and 110.02 MPa of tensile and flexural strengths for the resin, respectively. To achieve a linear load-deflection relationship in a three-point bending experiment, a maximum allowable deflection of 5 mm is acquired. The relationship between the frequency and fatigue life shows higher frequency results in lower fatigue life. Loading with frequency of 2 Hz has provided 5.8 times more fatigue life compared with 5 Hz loading. For a tension-tension fatigue loading condition, the variation of tensile module of epoxy resin shows no noticeable change during the fatigue loading condition. This module decreases significantly only in the primary and failure cycles close to the fracture point. In further experiments, fatigue behavior of epoxy resin was tested under flexural bending fatigue loadings with controlled deflection at room temperature. Maximum applied normalized stresses versus the number of cycles to failure curve are illustrated and it can be performed in order to predict the number of cycles to failure for the resin in arbitrary applied normal stresses as well.

  15. Electroactive polymer gels based on epoxy resin

    Science.gov (United States)

    Samui, A. B.; Jayakumar, S.; Jayalakshmi, C. G.; Pandey, K.; Sivaraman, P.

    2007-04-01

    Five types of epoxy gels have been synthesized from common epoxy resins and hardeners. Fumed silica and nanoclay, respectively, were used as fillers and butyl methacrylate/acrylamide were used as monomer(s) for making interpenetrating polymer networks (IPNs) in three compositions. Swelling study, tensile property evaluation, dynamic mechanical thermal analysis, thermo-gravimetric analysis, scanning electron microscopy and electroactive property evaluation were done. The gels have sufficient mechanical strength and the time taken for bending to 20° was found to be 22 min for forward bias whereas it was just 12 min for reverse bias.

  16. Experiences with testing PCRV concrete and epoxy resin models

    International Nuclear Information System (INIS)

    Schimmelpfennig, K.; Schnellenbach, G.

    1979-01-01

    A 1:5 scale model of a prestressed concrete pressure vessel was used to investigate its operating behaviour when only partially prestressed so as to allow cracking even under operating conditions. Further experimental work consisted in the building and testing of epoxy resin models to check the results of three-dimensional numerical calculations. Results show that a partially prestressed vessel will operate reliably and that deformations under both short and long-term internal pressure are essentially reversible. The results from the epoxy resin models show that building such models also with complicated geometries and with embedded strain gauges can be successfully carried out and that testing such models is a good tool for checking computer calculations

  17. Surface flashover performance of epoxy resin microcomposites improved by electron beam irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Yin; Min, Daomin [State Key Laboratory of Electrical Insulation and Power Equipment, Xi' an Jiaotong University, Xi' an 710049 (China); Li, Shengtao, E-mail: stli@mail.xjtu.edu.cn [State Key Laboratory of Electrical Insulation and Power Equipment, Xi' an Jiaotong University, Xi' an 710049 (China); Li, Zhen; Xie, Dongri [State Key Laboratory of Electrical Insulation and Power Equipment, Xi' an Jiaotong University, Xi' an 710049 (China); Wang, Xuan [Key Laboratory of Engineering Dielectric and its Application, Ministry of Education, Harbin University of Science and Technology, Harbin 150040 (China); Lin, Shengjun [State Key Laboratory of Electrical Insulation and Power Equipment, Xi' an Jiaotong University, Xi' an 710049 (China); Pinggao Group Company Ltd., State Grid High Voltage Switchgear Insulation Materials Laboratory, Pingdingshan 467001 (China)

    2017-06-01

    Highlights: • Epoxy resin microcomposites were irradiated by electron beam with energies of 10 and 20 keV. • Surface flashover voltage increase with the increase of electron beam energy. • Both the untreated and irradiated samples have two trap centers, which are labeled as shallow and deep traps. • Deposition energy in epoxy resin microcomposites increases with electron beam energy, and surface trap properties are determined by deposition energy. • The influence of surface conductivity and trap distribution on flashover voltage is discussed. - Abstract: The influencing mechanism of electron beam irradiation on surface flashover of epoxy resin/Al{sub 2}O{sub 3} microcomposite was investigated. Epoxy resin/Al{sub 2}O{sub 3} microcomposite samples with a diameter of 50 mm and a thickness of 1 mm were prepared. The samples were irradiated by electron beam with energies of 10 and 20 keV and a beam current of 5 μA for 5 min. Surface potential decay, surface conduction, and surface flashover properties of untreated and irradiated samples were measured. Both the decay rate of surface potential and surface conductivity decrease with an increase in the energy of electron beam. Meanwhile, surface flashover voltage increase. It was found that both the untreated and irradiated samples have two trap centers, which are labeled as shallow and deep traps. The increase in the energy and density of deep surface traps enhance the ability to capture primary emitted electrons. In addition, the decrease in surface conductivity blocks electron emission at the cathode triple junction. Therefore, electron avalanche at the interface between gas and an insulating material would be suppressed, eventually improving surface flashover voltage of epoxy resin microcomposites.

  18. Enhanced actuation performance of piezoelectric fiber composites induced by incorporated BaTiO{sub 3} nanoparticles in epoxy resin

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Mingliang; Yuan, Xi [State Key Laboratory of Powder Metallurgy, Central South University, Changsha, Hunan 410083 (China); Luo, Hang, E-mail: xtluohang@163.com [State Key Laboratory of Powder Metallurgy, Central South University, Changsha, Hunan 410083 (China); College of Chemistry and Chemical Engineering, Central South University, Changsha, Hunan 410083 (China); Chen, Haiyan; Chen, Chao; Zhou, Kechao [State Key Laboratory of Powder Metallurgy, Central South University, Changsha, Hunan 410083 (China); Zhang, Dou, E-mail: dzhang@csu.edu.cn [State Key Laboratory of Powder Metallurgy, Central South University, Changsha, Hunan 410083 (China)

    2017-05-18

    Piezoelectric fiber composites (PFCs) have attracted much interest owing to their flexibility and toughness compared with conventional monolithic piezoceramic wafers. The free strain values and actuation property of PFCs strongly depend on the active electric field applied in Pb(Zr{sub 1−x}Ti{sub x})O{sub 3} (PZT) fibers. Reducing the dielectric constant mismatch between PZT fiber and the assembling epoxy resin would greatly increase the active electric field in PZT fiber. Therefore, BaTiO{sub 3} (BT) nanoparticles were introduced into the epoxy resin to enhance the dielectric constant. Homogeneous dispersion of BT nanoparticles and tight adhesion with the epoxy resin were achieved through a surface modification by dopamine. The maximum dielectric constant of dopamine modified BT/epoxy (BT@Dop/epoxy) nanocomposites was 10.38 with 12 wt% BT@Dop content at 1 kHz. The maximum free strain of PFCs reached 1820 ppm with 6 wt% BT@Dop content, while PFCs assembled by pure epoxy showed 790 ppm at the same processing condition. The tip displacement of cantilever beam actuated by PFCs reached the peak of 19 mm at the resonance frequency with 6 wt% BT@Dop, which was improved by 90% comparing to PFCs with pure epoxy. - Highlights: • The effect of dielectric mismatch on effective electric field in piezoceramic fibers was explained by a model. • The dispersibility and adhesion of BaTiO{sub 3} nanoparticles in epoxy was improved by the dopamine modification. • The actuation performance increased firstly and then decreased with adding BaTiO{sub 3} nanoparticles. • The maximum free strain and displacement of cantilever beam were up to 1820 ppm and 19 mm, respectively.

  19. Structure, thermal and fracture mechanical properties of benzoxazine-modified amine-cured DGEBA epoxy resins

    Directory of Open Access Journals (Sweden)

    2011-03-01

    Full Text Available First, traditional diamine hardeners of epoxy resins (EP were checked as potential accelerators for the benzoxazine (BOX homopolymerization. It was established that the acceleration effect depends on both the type and amount of the diamine compounds. In the follow-up work amine-curable diglycidyl ether bisphenol A (DGEBA type EP was modified with BOX keeping the EP/BOX ratio constant (75/25 wt.%. The amine hardeners, added in the EP in stoichiometric amounts, were of aliphatic and aromatic nature, viz. diethylenetriamine (DETA, 4,4'-diaminodiphenyl methane (DDM, and their 1/1 mixture. The thermal, viscoelastic, flexural and fracture mechanical properties of the EP/BOX hybrids were determined and compared to those of the reference EPs. Based on dynamic-mechanical thermal analysis and atomic force microscopy the formation of co-network between EP and BOX was concluded. Homopolymerized BOX was built in the network in nanoscaled inclusions and it was associated with internal antiplasticization. Incorporation of BOX improved the charring, enhanced the flexural modulus and strength, and reduced the glass transition of the parent EP. The fracture toughness and energy were not improved by hybridization with BOX.

  20. Relationship between ion transport and the failure behavior of epoxy resin coatings

    International Nuclear Information System (INIS)

    Dong, Yuhua; Zhou, Qiong

    2014-01-01

    Highlights: •An epoxy resin-Q345 system with a sandwich structure was prepared. •Cl − ions permeated into epoxy resin coating prior to K + ions. •Free volume size and PAL increased when the coating was immersed into the solution. -- Abstract: An epoxy resin coating with a sandwich structure was prepared to investigate ion transport behavior in the coating. The macro- and micro- appearance of the coating immersed in 5 wt.% KCl solutions was observed by stereomicroscopy, scanning electron microscopy equipped with an energy dispersive spectrometer. The electrochemical property of the coating was characterized by electrochemical impedance spectroscopy, and change of free volume after immersion was characterized by positron annihilation lifetime spectroscopy. The results indicated that Cl − ions permeated into the coating prior to K + ions, the free volume size and positron annihilation lifetime of the coating increased during immersion

  1. Synthesis and characterisation of epoxy resins reinforced with carbon nanotubes and nanofibers.

    Science.gov (United States)

    Prolongo, S G; Gude, M R; Ureña, A

    2009-10-01

    Epoxy nanocomposites were fabricated using two kinds of nanofiller, amino-functionalized multi-walled carbon nanotubes (CNTs) and non-treated long carbon nanofibers (CNFs). The non-cured mixtures were analysed through viscosity measurements. The effect of the nanoreinforcement on the curing process was determined by differential scanning calorimetry. Finally, the characterisation of cured nanocomposites was carried out studying their thermo-mechanical and electrical behaviour. At room temperature, the addition of CNTs causes a viscosity increase of epoxy monomer much more marked than the introduction of CNFs due to their higher specific area. It was probed that in that case exists chemical reaction between amino-functionalized CNTs and the oxirane rings of epoxy monomer. The presence of nanoreinforcement induces a decrease of curing reaction rate and modifies the epoxy conversion reached. The glass transition temperature of the nanocomposites decreases with the contents of CNTs and CNFs added, which could be related to plasticization phenomena of the nanoreinforcements. The storage modulus of epoxy resin significantly increases with the addition of CNTs and CNFs. This augment is higher with amino-functionalized CNTs due, between other reasons, to the stronger interaction with the epoxy matrix. The electrical conductivity is greatly increased with the addition of CNTs and CNFs. In fact, the percolation threshold is lower than 0.25 wt% due to the high aspect ratio of the used nanoreinforcements.

  2. Influence of the silica fillers on the ageing of epoxy resins under irradiations

    International Nuclear Information System (INIS)

    Benard, F.

    2004-01-01

    Various studies were carried out on the ageing of epoxy resins under irradiations. In all cases, pure polymers were studied. The aim of our work managed by the CEA and the CNRS consists on studying the part of fillers and particularly the part of silica on ageing process under electron beam irradiations. Because of their wide use in industrial applications and especially in nuclear environment, the DGEBA-TETA resins (Diglycidylether of Bisphenol A - Triethylenetetramine) were chosen. Those epoxy resins are difficult to analyse because of their insolubility. Some pure and nano-metric silica filled chemical models which chemical structure very close to the one the DGEBA/TETA resin were synthesized and analysed with classical methods in organic chemistry. A major phenomenon of rupture of the C-O and C-N chemical bonds with creation of phenolic extremities, methylketone extremities, of primary and tertiary amines and notably enamine functions were revealed by the analyses. The quantitative 1 H and 13 C NMR analyses revealed the screen effect due to the silica and the reactions between the chemical species created by the irradiations and the silica surface. Thermic and thermodynamic analyses of the different epoxy resins in function of the irradiation dose and of the kind of silica showed the decrease of the glass transition temperature, of the relaxation temperature and of the crosslink density confirming the major phenomenon of bond ruptures during irradiations. With silica, the decrease of the crosslink density is slowed. This phenomenon can be explained with interactions between the nano-metric silica surface and the epoxy resin offsetting the effect of the chain rupture on the resin mechanical properties. The 13 C solid state NMR analyses confirmed the choice of the chemical models and permitted to detect the chemical species created by the irradiations. The analyse of the polarization transfers with 13 C CP-MAS NMR spectroscopy revealed the stiffening of the nano

  3. Design of carbon nanofiber embedded conducting epoxy resin

    International Nuclear Information System (INIS)

    Gantayat, Subhra; Sarkar, Niladri; Rout, Dibyaranjan; Swain, Sarat K.

    2017-01-01

    Acid treated carbon nanofiber (t-CNF) reinforced epoxy nanocomposites were fabricated by hand lay-up method with various wt % of t-CNF loadings. Pristine or unmodified carbon nano fibers (u-CNFs) were made compatible with epoxy matrix by means of mixed acid treatment. Fabricated nanocomposites were characterized with Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) study, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and atomic force microscopy (AFM). Mechanical and thermal properties of the nanocomposites were measured as a function of t-CNF content. Effect of acid treated CNFs on to the mechanical properties of epoxy nanocomposites was justified by comparing the mechanical properties of epoxy/t-CNF and epoxy/u-CNF nanocomposites with same loading level. The electrical conductivity was achieved by epoxy resin with a threshold at 1 wt % of t-CNF. Substantial improvement in thermal, mechanical and electrical properties of the synthesized epoxy/t-CNF nanocomposites may be suitable for fabricating electronic devices. - Highlights: • Epoxy/t-CNF nanocomposites are characterized by XRD, FTIR, SEM, AFM and TEM. • Electrical conductivity was achieved by epoxy with a threshold at 1 wt% of t-CNF. • Tensile strength is enhanced by 40% due to dispersion of t-CNF. • Synthesized nanocomposites are suitable for fabricating electronic devises.

  4. Design of carbon nanofiber embedded conducting epoxy resin

    Energy Technology Data Exchange (ETDEWEB)

    Gantayat, Subhra [Department of Chemistry, Veer Surendra Sai University of Technology, Burla, Sambalpur 768018, Odisha (India); School of Applied Sciences, KIIT University, Bhubaneswar 751024, Odisha (India); Sarkar, Niladri [Department of Chemistry, Veer Surendra Sai University of Technology, Burla, Sambalpur 768018, Odisha (India); Rout, Dibyaranjan [School of Applied Sciences, KIIT University, Bhubaneswar 751024, Odisha (India); Swain, Sarat K., E-mail: swainsk2@yahoo.co.in [Department of Chemistry, Veer Surendra Sai University of Technology, Burla, Sambalpur 768018, Odisha (India)

    2017-01-15

    Acid treated carbon nanofiber (t-CNF) reinforced epoxy nanocomposites were fabricated by hand lay-up method with various wt % of t-CNF loadings. Pristine or unmodified carbon nano fibers (u-CNFs) were made compatible with epoxy matrix by means of mixed acid treatment. Fabricated nanocomposites were characterized with Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) study, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and atomic force microscopy (AFM). Mechanical and thermal properties of the nanocomposites were measured as a function of t-CNF content. Effect of acid treated CNFs on to the mechanical properties of epoxy nanocomposites was justified by comparing the mechanical properties of epoxy/t-CNF and epoxy/u-CNF nanocomposites with same loading level. The electrical conductivity was achieved by epoxy resin with a threshold at 1 wt % of t-CNF. Substantial improvement in thermal, mechanical and electrical properties of the synthesized epoxy/t-CNF nanocomposites may be suitable for fabricating electronic devices. - Highlights: • Epoxy/t-CNF nanocomposites are characterized by XRD, FTIR, SEM, AFM and TEM. • Electrical conductivity was achieved by epoxy with a threshold at 1 wt% of t-CNF. • Tensile strength is enhanced by 40% due to dispersion of t-CNF. • Synthesized nanocomposites are suitable for fabricating electronic devises.

  5. Surface modification of epoxy resin using He/CF{sub 4} atmospheric pressure plasma jet for flashover withstanding characteristics improvement in vacuum

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Sile; Wang, Shuai; Wang, Yibo; Guo, Baohong; Li, Guoqiang; Chang, Zhengshi; Zhang, Guan-Jun, E-mail: gjzhang@xjtu.edu.cn

    2017-08-31

    Highlights: • Epoxy resin (EP) samples are treated by atmospheric pressures plasma jet (APPJ). • Flashover withstanding characteristics of epoxy resin samples are improved a lot after APPJ treatment. • Appropriate treatment conditions are important to modify EP samples by APPJ. • Both physical and chemical effects lead to the enhancement of flashover strength. - Abstract: For enhancing the surface electric withstanding strength of insulating materials, epoxy resin (EP) samples are treated by atmospheric pressure plasma jet (APPJ) with different time interval from 0 to 300s. Helium (He) and tetrafluoromethane (CF{sub 4}) mixtures are used as working gases with the concentration of CF{sub 4} ranging 0%-5%, and when CF{sub 4} is ∼3%, the APPJ exhibits an optimal steady state. The flashover withstanding characteristics of modified EP in vacuum are greatly improved under appropriate APPJ treatment conditions. The surface properties of EP samples are evaluated by surface roughness, scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS) and water contact angle. It is considered that both physical and chemical effects lead to the enhancement of flashover strength. The physical effect is reflected in the increase of surface roughness, while the chemical effect is reflected in the graft of fluorine groups.

  6. Epoxy resin casting of trim coils for superconducting cyclotron

    International Nuclear Information System (INIS)

    Hajra, D.P.; Sarkar, S.C.; Saha, Subimal; Chaudhuri, J.; Bhandari, R.K.

    2006-01-01

    The life of any magnet depends on the soundness of the coil insulation, its aging properties and initial and final endurance limitations. The insulation of water-cooled trim coils for superconducting cyclotron is made of glass fibre tape with heat cured unfilled epoxy resin combination. This type of insulation has been selected to achieve excellent stability against thermal and electromagnetic stresses, tight dimensional control, good dielectric strength, non-hygroscopic and considerably low vapour-pressure as it will be inside rough vacuum. The process development and the difficulties encountered for appropriate selection of epoxy resin combination, potting, vacuum process, curing cycle, control of coil dimension to achieve a sound coil absolutely free from cracks, trapped air and voids has been discussed. (author)

  7. A One-Component, Fast-Cure, and Economical Epoxy Resin System Suitable for Liquid Molding of Automotive Composite Parts

    Directory of Open Access Journals (Sweden)

    Yiru Wang

    2018-04-01

    Full Text Available Imidazole cured epoxy resin systems were evaluated for one-component, fast-curing resins for liquid molding of automotive composite parts according to industry requirements. It was demonstrated that an epoxy resin-1-(cyanoethyl-2-ethyl-4-methylimidazol(EP-1C2E4MIM system would cure in a few minutes at 120 °C, while exhibiting acceptable pot life, viscosity profiles, and low water absorption. Moreover, this system yielded high Tg parts with mechanical properties similar to the amine-epoxy systems, which are the mainstream two-component epoxy resin systems for automobiles.

  8. Preparation of hyperbranched poly (amidoamine)-grafted graphene nanolayers as a composite and curing agent for epoxy resin

    Science.gov (United States)

    Gholipour-Mahmoudalilou, Meysam; Roghani-Mamaqani, Hossein; Azimi, Reza; Abdollahi, Amin

    2018-01-01

    Thermal properties of epoxy resin were improved by preparation of a curing agent of poly (amidoamine) (PAMAM) dendrimer-grafted graphene oxide (GO). Hyperbranched PAMAM-modified GO (GD) was prepared by a divergent dendrimer synthesis methodology. Modification of GO with (3-Aminopropyl)triethoxysilane (APTES), Michael addition of methacrylic acid, and amidation reaction with ethylenediamine results in the curing agent of GD. Then, epoxy resin was cured in the presence of different amounts of GD and the final products were compared with ethylenediamine-cured epoxy resin (E) in their thermal degradation temperature and char contents. Functionalization of GO with APTES and hyperbranched dendrimer formation at the surface of GO were evaluated by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy, X-ray diffraction, and thermogravimetric analysis (TGA) results. TGA results showed that the weight loss associated with chemical moieties in GONH2, GOMA, and GD is estimated to be 10.1, 12.2, and 14.1%, respectively. Covalent attachment of dendrimer at the surface of GO increases its thermal stability. TGA also showed that decomposition temperature and char content are higher for composites compared with E. Scanning and transmission electron microscopies show that flat and smooth graphene nanolayers are wrinkled in GO and re-stacking and flattening of nanolayers is observed in GD.

  9. Preparation and Characterization of Epoxy Resin Cross-Linked with High Wood Pyrolysis Bio-Oil Substitution by Acetone Pretreatment

    Directory of Open Access Journals (Sweden)

    Yi Liu

    2017-03-01

    Full Text Available The use of cost effective solvents may be necessary to store wood pyrolysis bio-oil in order to stabilize and control its viscosity, but this part of the production system has not been explored. Conversely, any rise in viscosity during storage, that would occur without a solvent, will add variance to the production system and render it cost ineffective. The purpose of this study was to modify bio-oil with a common solvent and then react the bio-oil with an epoxy for bonding of wood without any loss in properties. The acetone pretreatment of the bio-oil/epoxy mixture was found to improve the cross-linking potential and substitution rate based on its mechanical, chemical, and thermal properties. Specifically, the bio-oil was blended with epoxy resin at weight ratios ranging from 2:1 to 1:5 and were then cured. A higher bio-oil substitution rate was found to lower the shear bond strength of the bio-oil/epoxy resins. However, when an acetone pretreatment was used, it was possible to replace the bio-oil by as much as 50% while satisfying usage requirements. Extraction of the bio-oil/epoxy mixture with four different solvents demonstrated an improvement in cross-linking after acetone pretreatment. ATR-FTIR analysis confirmed that the polymer achieved a higher cross-linked structure. DSC and TGA curves showed improved thermal stability with the addition of the acetone pretreatment. UV-Vis characterization showed that some functional groups of the bio-oil to epoxy system were unreacted. Finally, when the resin mixture was utilized to bond wood, the acetone pretreatment coupled with precise tuning of the bio-oil:epoxy ratio was an effective method to control cross-linking while ensuring acceptable bond strength.

  10. Polymerization of epoxy resins studied by positron annihilation

    Energy Technology Data Exchange (ETDEWEB)

    Suzuki, T. [Radiation Science Center, High Energy Accelerator Research Organization (KEK), Tsukuba (Japan); Hayashi, T. [Fine Chemical Research Lab., Sumitomo Chemical, Tsukuba (Japan); Ito, Y. [Research Center for Nuclear Science and Technology, Univ. of Tokyo (Japan)

    2001-04-01

    Positron annihilation lifetime spectroscopy (PALS) has been applied to study polymerization of epoxy resins of cresole novolac with a hardener of phenol novolac. PALS uses positrons to probe the microstructure of a nanometer (nm) size. Using PALS polymerization can be followed through three states: powder (monomer), liquid and solid. PALS is a unique method for the detection of intermolecular spaces, hence polymerization was followed from the point of view of free spaces (inter-molecular spaces) between polymer networks. The glass transition temperature (T{sub g}) was determined from the temperature dependence of the positronium (Ps) lifetime. Although Tg determined by PALS is usually lower than that determined by a mechanical analysis (TMA), it was observed that T{sub g} approached the value determined by TMA after long curing. Ps can form bubbles in a liquid, and the surface tension of a mixture of the resin and the hardener was calculated from a simple empirical formula using the Ps lifetime; the resulting value is similar to that of the bisphenol-A epoxy resin. Gelation was observed as an increase in the intensity of Ps and a sharp decrease in the lifetime. (orig.)

  11. Preparation and characterization of polyhedral oligomer silsesquioxane nanocomposites incorporated in epoxy resin

    International Nuclear Information System (INIS)

    Longhi, Marielen; Zini, Lucas Pandolphi; Birriel, Eliena Jonko; Kunst, Sandra Raquel; Zattera, Ademir Jose

    2015-01-01

    The incorporation of nanofiller in thermosetting like epoxy resin as has been studied in order to modify its properties. In this research, nanocomposites were obtained by incorporating 5% by weight of three polyhedral oligomeric silsesquioxane (POSS) with different number of functionalization: Glicidilisobutil-POSS, Triglicidilisobutil- POSS and Glicicil POSS in an epoxy matrix by sonification process. The nanocomposites were characterized by analysis of X-ray diffraction (DRX), transmission electron microscopy (TEM) and thermogravimetric analysis (TGA). The DRX analysis showed the characteristic peak of POSS and TEM images showed that there is a difference in the dispersion of nanocages for the difference in the number of epoxy groups on the POSS. The incorporation of Glicidilisobutil-POSS showed a significant increase in the glass transition temperature (Tg) value, and also that the most effective from the viewpoint of the dispersion, on the other hand, the Glycidyl-POSS had a greater influence on the thermal stability demonstrating that the dispersion medium is an important characteristic to define the most desirable properties. (author)

  12. Biodegradation Study of Nanocomposites of Phenol Novolac Epoxy/Unsaturated Polyester Resin/Egg Shell Nanoparticles Using Natural Polymers

    Directory of Open Access Journals (Sweden)

    S. M. Mousavi

    2015-01-01

    Full Text Available Nanocomposite materials refer to those materials whose reinforcing phase has dimensions on a scale from one to one hundred nanometers. In this study, the nanocomposite biodegradation of the phenol Novolac epoxy and the unsaturated polyester resins was investigated using the egg shell nanoparticle as bioceramic as well as starch and glycerin as natural polymers to modify their properties. The phenol Novolac epoxy resin has a good compatibility with the unsaturated polyester resin. The prepared samples with different composition of materials for specified time were buried under soil and their biodegradation was studied using FTIR and SEM. The FTIR results before and after degradation showed that the presence of the hydroxyl group increased the samples degradation. Also adding the egg shell nanoparticle to samples had a positive effect on its degradation. The SEM results with and without the egg shell nanoparticle also showed that use of the egg shell nanoparticle increases the samples degradation. Additionally, increasing the amount of starch, and glycerol and the presence of egg shell nanoparticles can increase water adsorption.

  13. CHARACTERIZATION OF ALKALINE LIGNINS FOR USE IN PHENOL-FORMALDEHYDE AND EPOXY RESINS

    Directory of Open Access Journals (Sweden)

    Nour Eddine El Mansouri

    2011-05-01

    Full Text Available Besides polyurethanes and polyesters, phenolic and epoxy resins are the most prominent applications for technical lignins in thermosetting materials. To evaluate the potential application of lignin raw materials in phenol formaldehyde and epoxy resins, three types of alkaline lignins were characterized in terms of their structures and thermal properties. The lignin samples analyzed were kraft lignin (LIG-1, soda–rice straw lignin (LIG-2, and soda-wheat straw lignin (LIG-3. FTIR and 1H-NMR methods were used to determine their structure. Gel permeation chromatography (GPC was used to determine the molecular weight distribution (MWD. Differential scanning calorimetry (DSC was used to measure the glass transition temperature (Tg, and thermogravimetric analysis (TGA to determine the thermal stability of lignin samples. Results showed that kraft lignin (LIG-1 has moderate hydroxyl-group content, is rich in G-type units, and has good thermal stability. These properties make it more suitable for direct use in phenol formaldehyde resins, and it is therefore a good raw material for this purpose. The alkaline soda-rice straw lignin (LIG-2 with a high hydroxyl-group content and excellent thermal stability is most suited to preparing lignin-based epoxy resins.

  14. Association between positive patch tests to epoxy resin and fragrance mix I ingredients

    DEFF Research Database (Denmark)

    Andersen, Klaus Ejner; Christensen, Lars Porskjaer; Vølund, Aage

    2009-01-01

    and possibly reproduce this association with the use of TRUE((R)) test data and supplementary tests with fragrance mix ingredients from the Department of Dermatology, Odense University Hospital. MATERIALS AND METHODS: Six thousand one hundred and fifteen consecutive eczema patients tested from 1995 to 2007......BACKGROUND: Both epoxy resin (diglycidyl ether of bisphenol A) and fragrance mix I are included in the European baseline series of contact allergens. A significant association between positive reactions to epoxy resin and fragrance mix has been reported by others. OBJECTIVE: To investigate...... were included, and test results from all patients tested with fragrance mix ingredients were analysed. RESULTS: One hundred and forty-five (2.4%) were positive to epoxy resin and 282 (4.6%) were positive to fragrance mix I. Nineteen were positive to both giving an odds ratio of 3.3, which...

  15. Chronic Dermal Toxicity of Epoxy Resins I. Skin Carcinogenic Potency and General Toxicity

    Energy Technology Data Exchange (ETDEWEB)

    Holland, J.M.

    2001-01-16

    Epoxy resins are a diverse class of chemicals that differ in structure, physical properties, and, presumably, biological activity. The purpose of these experiments was to compare the chronic dermal toxicity and carcinogenicity of selected commercial epoxy resins and to determine the potential for positive synergistic carcinogenic interactions between different resins. This work is an extension and continuation of a Department of Energy sponsored program to evaluate epoxy resins for potential occupational health risks. The materials examined were chosen on the basis of their interest to the U.S. government. They are representative of the manufacturer's production at the time, and therefore the data are completely valid only for the specific production period. Results of the experimental exposures will be reported in two parts. This report describes the test materials, their chemical and physical characteristics and the experimental design. General (systemic) toxicity will be evaluated and the skin carcinogenicity of the materials compared. A subsequent report will provide morphological descriptions of skin and significant internal pathology induced by the various treatments.

  16. Synthesis and characterization of cement slurries additives with epoxy resins - kinetics, thermodynamic and calorimetric analysis; Sintese e caracterizacao de pastas de cimento aditivadas com resinas epoxi - analises cineticas, termodinamicas e calorimetricas

    Energy Technology Data Exchange (ETDEWEB)

    Tavares, A.M.G.; Andrade Junior, M.A.S.; Cestari, A.R.; Vieira, E.F.S., E-mail: macleybiane@gmail.co [Universidade Federal de Sergipe (UFS), Sao Cristovao, SE (Brazil)

    2010-07-01

    Cement has been used in the world, presenting a wide versatility. However, due to its chemical nature, it is subject to several types of chemical damages, especially for agents of acidic nature. With the purpose of increase its life-time, new cement slurries have been modified with the addition of specific additives. The objective of this work is to modify cement slurries with epoxy resins, which promote higher resistance of those materials in relation to acid attacks. Three cement slurries were synthesized with epoxy resins and a standard slurries, which was composed by cement and water. After 30 days of hydration, the samples were characterized by XDR, FTIR and thermal analysis (TG and DSC). The hydration processes of the cement slurries were studied by heat-conduction microcalorimetry. A kinetic study of HCl interaction with the new slurries were performed by the batch methodology at 25, 35, 45 e 55 deg C. It was verified that the addition of the polymers delayed the processes of hydration of the slurries, decreasing the flow of heat released as a function of the amount of added resin and, increased the resistance of those slurries to the acid attack. (author)

  17. Mechanical properties and environmental effects of epoxy resins in the neat state and in composites

    International Nuclear Information System (INIS)

    Yang, C.M.P.

    1984-01-01

    The dynamic mechanical properties of graphite fiber reinforced, epoxy matrix composite laminates subjected to loading perpendicular to the plane of lamination and of neat epoxy resin are reported. The centrosymmetric deformation (CSD) test geometry provides an accurate and convenient test mode for the study of the viscoelastic behavior of very stiff graphite-epoxy laminates. It is found that the in-phase and out-of-phase stiffness superpose to form master curves covering a frequency range of 12 decades. By a suitable scaling procedure of the master curves, it is found that the in-phase stiffness has the same shape and the out-of-phase has the same dispersion for all laminates irrespective of the stacking sequence. The dispersion characteristics of in-situ and neat resin epoxy were nearly identical, but with the neat resin having a lower glass-transition temperature. The graphite/epoxy composites and neat resin epoxy have been shown to be sensitive to hygrothermal environment. For postcured specimens the plasticization and inhomogeneous swelling effects due to the moisture absorbed are found to be reversible, in the sense that the initially dry properties of the laminate are recovered after redrying the wet specimen. On the other hand, for as cured specimens, the plasticization and inhomogeneous swelling effects are found to be irreversible under the same hygrothermal environment

  18. Preparation and Characterization of New Geopolymer-Epoxy Resin Hybrid Mortars

    Directory of Open Access Journals (Sweden)

    Raffaele Cioffi

    2013-07-01

    Full Text Available The preparation and characterization of metakaolin-based geopolymer mortars containing an organic epoxy resin are presented here for the first time. The specimens have been prepared by means of an innovative in situ co-reticulation process, in mild conditions, of commercial epoxy based organic resins and geopolymeric slurry. In this way, geopolymer based hybrid mortars characterized by a different content of normalized sand (up to 66% in weight and by a homogeneous dispersion of the organic resin have been obtained. Once hardened, these new materials show improved compressive strength and toughness in respect to both the neat geopolymer and the hybrid pastes since the organic polymer provides a more cohesive microstructure, with a reduced amount of microcracks. The microstructural characterization allows to point out the presence of an Interfacial Transition Zone similar to that observed in cement based mortars and concretes. A correlation between microstructural features and mechanical properties has been studied too.

  19. Thermosetting polymer for dynamic nuclear polarization: Solidification of an epoxy resin mixture including TEMPO

    Energy Technology Data Exchange (ETDEWEB)

    Noda, Yohei, E-mail: noda.yohei@jaea.go.jp [Quantum Beam Science Centre, Sector of Nuclear Science Research, Japan Atomic Energy Agency, Shirakata-Shirane, Tokai, Ibaraki 319-1195 (Japan); Kumada, Takayuki [Quantum Beam Science Centre, Sector of Nuclear Science Research, Kansai Photon Science Institute, Japan Atomic Energy Agency, Kizugawa, Kyoto 619-0215 (Japan); Yamaguchi, Daisuke; Shamoto, Shin-ichi [Quantum Beam Science Centre, Sector of Nuclear Science Research, Japan Atomic Energy Agency, Shirakata-Shirane, Tokai, Ibaraki 319-1195 (Japan)

    2015-03-11

    We investigated the dynamic nuclear polarization (DNP) of typical thermosetting polymers (two-component type epoxy resins; Araldite{sup ®} Standard or Araldite{sup ®} Rapid) doped with a (2,2,6,6-tetramethylpiperidine-1-yl)oxy (TEMPO) radical. The doping process was developed by carefully considering the decomposition of TEMPO during the solidification of the epoxy resin. The TEMPO electron spin in each two-component paste decayed slowly, which was favorable for our study. Furthermore, despite the dissolved TEMPO, the mixture of the two-component paste successfully solidified. With the resulting TEMPO-doped epoxy-resin samples, DNP experiments at 1.2 K and 3.35 T indicated a magnitude of a proton-spin polarization up to 39%. This polarization is similar to that (35%) obtained for TEMPO-doped polystyrene (PS), which is often used as a standard sample for DNP. To combine this solidification of TEMPO-including mixture with a resin-casting technique enables a creation of polymeric target materials with a precise and complex structure.

  20. Thermosetting epoxy resin/thermoplastic system with combined shape memory and self-healing properties

    International Nuclear Information System (INIS)

    Yao, Yongtao; Wang, Jingjie; Lu, Haibao; Liu, Yanju; Leng, Jinsong; Xu, Ben; Fu, Yongqing

    2016-01-01

    A novel and facile strategy was proposed to construct a thermosetting/thermoplastic system with both shape memory and self-healing properties based on commercial epoxy resin and poly(ϵ-caprolactone)-PCL. Thermoplastic material is capable of re-structuring and changing the stiffness/modulus when the temperature is above melting temperature. PCL microfiber was used as a plasticizer in epoxy resin–based blends, and served as a ‘hard segment’ to fix a temporary shape of the composites during shape memory cycles. In this study, the electrospun PCL membrane with a porous network structure enabled a homogenous PCL fibrous distribution and optimized interaction between fiber and epoxy resin. The self-healing capability is achieved by phase transition during curing of the composites. The mechanism of the shape memory effect of the thermosetting (rubber)/thermoplastic composite is attributed to the structural design of the thermoplastic network inside the thermosetting resin/rubber matrix. (paper)

  1. Creep behavior of an epoxy resin and an epoxy-based FRP in condition of simultaneous supply of radiation and stress at cryogenic temperatures

    International Nuclear Information System (INIS)

    Nishiura, Tetsuya; Nishijima, Shigehiro; Okada, Toichi

    1995-01-01

    Creep tests of an epoxy resin and an epoxy-based FRP in bending under irradiation condition have been carried out, to investigate the synergistic effects of radiation and stress on mechanical properties of FRP. Simultaneous supply of stress and irradiation on the epoxy resin and the FRP enhanced creep rates in comparison with that supply of the stress on a post-irradiated one did. ESR spectra measurement was also carried out to study the change of molecule of the resin irradiated. Increase of molecular weight between crosslinks was found out to be enhanced by the synergistic effect of radiation and stress. The mechanism of increased damage of FRP induced by the effects of simultaneous stress and irradiation is discussed. (author)

  2. Epoxy Resin Modified Quartz Crystal Microbalance Sensor for Chemical Warfare Agent Sulfur Mustard Vapor Detection

    Directory of Open Access Journals (Sweden)

    Rajendra BUNKAR

    2010-02-01

    Full Text Available An epoxy resin polymer coated quartz crystal microbalance (PC-QCM is used for detection of sulfur mustard vapor (SM. When SM vapor is exposed to PC-QCM sensor frequency shift is observed. The response of the sensor in ambient condition is 554 Hz with ±10 % variation upon exposure of 155 ppm of the SM concentration. The observed response loss is nearly 40 % over the period of 15 months. The response of the sensor is higher for SM than compare to structurally similar chloroethyl ether (CEE and other interferences.

  3. The effects of alumina nanofillers on mechanical properties of high-performance epoxy resin.

    Science.gov (United States)

    Zhang, Hui; Zhang, Hui; Tang, Longcheng; Liu, Gang; Zhang, Daijun; Zhou, Lingyun; Zhang, Zhong

    2010-11-01

    In the past decade extensive studies have been focused on mechanical properties of inorganic nanofiller/epoxy matrices. In this work we systematically investigated the mechanical properties of nano-alumina-filled E-54/4, 4-diaminodiphenylsulphone (DDS) epoxy resins, which were prepared via combining high-speed mixing with three-roll milling. Homogeneous dispersion of nano-alumina with small agglomerates was obtained in epoxy resin, which was confirmed using transmission electron microscopy (TEM). The static/dynamic modulus, tensile strength and fracture toughness of the nanocomposites were found to be simultaneously enhanced with addition of nano-alumina fillers. About 50% and 80% increases of K(IC) and G(IC) were achieved in nanocomposite filled with 18.4 wt% alumina nanofillers, as compared to that of the unfilled epoxy resin. Furthermore, the corresponding fracture surfaces of tensile and compact tension samples were examined by scanning electron microscopy (SEM) and atomic force microscopy (AFM) techniques in order to identify the relevant fracture mechanisms involved. Various fracture features including cavities/debonding of nanofiller, local plastic deformation as well as crack pinning/deflection were found to be operative in the presence of nano-alumina fillers.

  4. Characterization of fracture toughness of epoxy resin after hygrothermal aging

    KAUST Repository

    Quispe, Gustavo Q.

    2013-07-01

    Characterization of fracture toughness of epoxy resin after hygrothermal ageing Gustavo Quino Quispe The aim of this work is to characterize the e ects of hygrothermal aging in the plain strain fracture toughness of the epoxy system composed by cycloaliphatic epoxy resin and diglycidyl ether of bisphenol-A (DGEBA). For this, after having been under hygrothermal aging in a climatic chamber, epoxy samples were studied using ASTM D5045 fracture toughness test, and micrography and roughness measurements of the fracture surface. It is reported a rapid decrease of GIc and KIc during the rst 2 days. Moreover, a numerical model [13] was used to simulate and see with more detail the water absorption in the aged samples. From that, it was observed the heterogeneous distribution of water. Accordingly, it was proposed that the results should be correlated with the water content at the vicinity of the crack tip. Consequently, it was possible to obtain, by quasi-static simulations, the ideal load-displacement curves of crack propagation in the heterogeneous samples. Finally, another contribution of this work is the study of the fracture surface, that gives a clue of the relationship among the fracture energy, the appearance of microcracks in the fracture surface, and the roughness (Ra).

  5. Surface treated fly ash filled modified epoxy composites

    Directory of Open Access Journals (Sweden)

    Uma Dharmalingam

    2015-01-01

    Full Text Available Abstract Fly ash, an inorganic alumino silicate has been used as filler in epoxy matrix, but it reduces the mechanical properties due to its poor dispersion and interfacial bonding with the epoxy matrix. To improve its interfacial bonding with epoxy matrix, surface treatment of fly ash was done using surfactant sodium lauryl sulfate and silane coupling agent glycidoxy propyl trimethoxy silane. An attempt is also made to reduce the particle size of fly ash using high pressure pulverizer. To improve fly ash dispersion in epoxy matrix, the epoxy was modified by mixing with amine containing liquid silicone rubber (ACS. The effect of surface treated fly ash with varying filler loadings from 10 to 40% weight on the mechanical, morphological and thermal properties of modified epoxy composites was investigated. The surface treated fly ash was characterized by particle size analyzer and FTIR spectra. Morphological studies of surface treated fly ash filled modified epoxy composites indicate good dispersion of fillers in the modified epoxy matrix and improves its mechanical properties. Impact strength of the surface treated fly ash filled modified epoxy composites show more improvement than unmodified composites.

  6. Curing behaviour of epoxy resin/graphite composites containing ionic liquid

    International Nuclear Information System (INIS)

    Guo Baochun; Wan Jingjing; Lei Yanda; Jia Demin

    2009-01-01

    By adopting the isoconversional method, subtle changes in the curing activation energy (E α ) among epoxy resin/graphite composites by the inclusion of expanded graphite (EG), ionic liquid of 1-butyl-3-methyl-imidazolium hexafluorophosphate ([BMIm]PF 6 ) or their combination are shown in the whole conversion range. At lower concentrations (1 phr) of EG, compared with the E α of the neat epoxy resin, the composite with EG has a lower E α before the gelation, and a higher E α after the gelation. At higher concentrations of EG, however, in the whole conversion range, the composite with EG shows a higher E α compared with the neat epoxy resin. As the curing proceeded, a peculiar increase in E α is found in systems containing [BMIm]PF 6 . Due to the formation of hydrogen bonding between [BMIm]PF 6 and the hardener (Jeffamine), the reactivity of Jeffamine is considerably decreased, leading to a much higher E α in [BMIm]PF 6 -containing systems, especially at higher conversion. In systems containing a combination of [BMIm]PF 6 and EG, due to the interactions between EG and [BMIm]PF 6 , the shielding effect provided by the well-dispersed EG sheets constrains the formation of the hydrogen bonding between [BMIm]PF 6 and Jeffamine, leading to lowered E α compared with that for the system containing [BMIm]PF 6 only.

  7. Synthesis, structure and properties of novel epoxy and rubber-modified epoxy impregnated Y-Ba-Cu-O superconductors

    International Nuclear Information System (INIS)

    Low, I.M.; Lim, F.W.; Chisholm, W.

    1992-01-01

    This paper reports the synthesis, structure and properties of novel YBa 2 Cu 3 O 6+x (123) - polymer composites. The polymers used were epoxy and rubber-modified epoxy resins. Superconducting composites with good strength, toughness, hardness and chemical resistance have been successfully fabricated. The presence of polymer(s) does not appear to affect the superconducting (T c ) of about 90 K. Levitation experiments show that the height (z) of the levitating magnet depends on sample thickness, and mass and pole strength of the magnet. A simple image force model best describes the observed dependence of z on the mass and pole strength. Atomic absorption and pH measurements in the corrosion study show that the polymer coating provides an impermeable barrier to the ingress of solvents and a concomitant resistance to phase decomposition. 12 refs., 2 tabs., 5 figs

  8. Two cases of occupational allergic contact dermatitis from a cycloaliphatic epoxy resin in a neat oil

    DEFF Research Database (Denmark)

    Jensen, Charlotte D; Andersen, Klaus E

    2003-01-01

    to a neat oil used in metal processing. Patch testing revealed that the relevant contact allergen was a cycloaliphatic epoxy resin, 1,2-cyclohexanedicarboxylic acid, bis(oxiranylmethyl) ester, added to the oil as a stabilizer. None of the patients had positive reactions to the bisphenol A-based epoxy resin...... product is essential....

  9. Chemical recycling of carbon fibers reinforced epoxy resin composites in oxygen in supercritical water

    International Nuclear Information System (INIS)

    Bai, Yongping; Wang, Zhi; Feng, Liqun

    2010-01-01

    The carbon fibers in carbon fibers reinforced epoxy resin composites were recovered in oxygen in supercritical water at 30 ± 1 MPa and 440 ± 10 o C. The microstructure of the recovered carbon fibers was observed using scanning electron microscopy (SEM) and atom force microscopy (AFM). The results revealed that the clean carbon fibers were recovered and had higher tensile strength relative to the virgin carbon fibers when the decomposition rate was above 85 wt.%, although the recovered carbon fibers have clean surface, the epoxy resin on the surface of the recovered carbon fibers was readily observed. As the decomposition rate increased to above 96 wt.%, no epoxy resin was observed on the surface of the carbon fibers and the oxidation of the recovered carbon fibers was readily measured by X-ray photoelectron spectroscopy (XPS) analysis. The carbon fibers were ideally recovered and have original strength when the decomposition rates were between 94 and 97 wt.%. This study clearly showed the oxygen in supercritical water is a promising way for recycling the carbon fibers in carbon fibers reinforced resin composites.

  10. Analysis by Fourier Transform Infrared (FTIR) of the gamma radiation effect on epoxy resin, used as solidification agent of radioactive wastes

    International Nuclear Information System (INIS)

    Liu, C.H.; Riella, H.G.; Guedes, S.M.L.

    1995-01-01

    The effects of gamma radiation on Epoxy resin, used as solidification agent of radioactive wastes, were studied by Fourier Transform Infrared (FTIR). The spectra showed no significant modifications on Epoxy resin functional groups (irradiated with dose from 0 to 1 MGy). Up to 1 MGy Epoxy resin did not oxidize, confirming the Epoxy good radiation strength. The presence of aromatic chain and amine group, mainly tertiary amine, give good radiolytic stability to the Epoxy, increasing the interest to use this material in nuclear facilities. (author). 3 refs, 2 figs

  11. The Reverse Thermal Effect in Epoxy Resins and Moisture Absorption in Semi-Interpenetrating Polymer Networks.

    Science.gov (United States)

    El-Sa'Ad, Leila

    1989-12-01

    Available from UMI in association with The British Library. Requires signed TDF. Epoxy resins exhibit many desirable properties which make them ideal subjects for use as matrices of composite materials in many commercial, military and space applications. However, due to their high cross-link density they are often brittle. Epoxy resin networks have been modified by incorporating tough, ductile thermoplastics. Such systems are referred to as Semi-Interpenetrating Polymer Networks (Semi-IPN). Systematic modification to the thermoplastics backbone allowed the morphology of the blend to be controlled from a homogeneous one-phase structure to fully separated structures. The moisture absorption by composites in humid environments has been found to lead to a deterioration in the physical and mechanical properties of the matrix. Therefore, in order to utilize composites to their full potential, their response to hot/wet environments must be known. The aims of this investigation were two-fold. Firstly, to study the effect of varying the temperature of exposure at different stages in the absorption process on the water absorption behaviour of a TGDDM/DDS epoxy resin system. Secondly, to study water absorption characteristics, under isothermal conditions, of Semi-Interpenetrating Polymer Networks possessing different morphologies, and develop a theoretical model to evaluate the diffusion coefficients of the two-phase structures. The mathematical treatment used in this analysis was based on Fick's second law of diffusion. Tests were performed on specimens immersed in water at 10 ^circ, 40^circ and 70^circC, their absorption behaviour and swelling behaviour, as a consequence of water absorption, were investigated. The absorption results of the variable temperature absorption tests indicated a saturation dependence on the absorption behaviour. Specimens saturated at a high temperature will undergo further absorption when transferred to a lower temperature. This behaviour was

  12. Use of 2,5-dimethyl-2,5-hexane diamine as a curing agent for epoxy resins. [Patent application

    Science.gov (United States)

    Rinde, J.A.; Newey, H.A.

    Primary diamines are prepared for use as a curing agent for epoxy resins. These curing agents can be used to form epoxy resin mixtures useful in filament winding and preimpregnated fiber molding and in formulating film adhesives, powder coatings and molding powders. The epoxy mixtures form for such uses a room temperature non-reacting, intermediate stable state which has a latent cross-linking capability.

  13. Literature Review: An Overview of Epoxy Resin Syntactic Foams with Glass Microballoons

    Energy Technology Data Exchange (ETDEWEB)

    Keller, Jennie [Los Alamos National Lab. (LANL), Los Alamos, NM (United States)

    2014-03-12

    Syntactic foams are an important category of composite materials that have abundant applications in a wide variety of fields. The bulk phase of syntactic foams is a three-part epoxy resin formulation that consists of a base resin, a curative (curing agent) and a modifier (diluent and/or accelerator) [12]. These thermoset materials [12] are used frequently for their thermal stability [9], low moisture absorption and high compressive strength [10]. The characteristic feature of a syntactic foam is a network of beads that forms pores within the epoxy matrix [3]. In this review, hollow glass beads (known as glass microballoons) are considered, however, solid beads or microballoons made from materials such as ceramic, polymer or metal can also be used [3M, Peter]. The network of hollow beads forms a closed-cell foam; the term closed-cell comes from the fact that the microspheres used in the resin matrix are completely closed and filled with gas (termed hollow). In contrast, the microspheres used in open-cell foams are either not completely closed or broken so that matrix material can fill the spheres [11]. Although closed foams have been found to possess higher densities than open cell foams, their rigid structures give them superior mechanical properties [12]. Past research has extensively studied the effects that changing the volume fraction of microballoons to epoxy will have on the resulting syntactic foam [3,4,9]. In addition, published literature also explores how the microballoon wall thickness affects the final product [4,9,10]. Findings detail that indeed both the mechanical and some thermal properties of syntactic foams can be tailored to a specific application by varying either the volume fraction or the wall thickness of the microballoons used [10]. The major trends in syntactic foam research show that microballoon volume fraction has an inversely proportionate relationship to dynamic properties, while microballoon wall thickness is proportional to those

  14. Reinforcing styrene butadiene rubber with lignin-novolac epoxy resin networks

    Directory of Open Access Journals (Sweden)

    P. Yu

    2015-01-01

    Full Text Available In this study, lignin-novolac epoxy resin networks were fabricated in the styrene butadiene rubber (SBR matrix by combination of latex compounding and melt mixing. Firstly, SBR/lignin compounds were co-coagulated by SBR latex and lignin aqueous solution. Then the novolac epoxy resin (F51 was added in the SBR/lignin compounds by melt compounding method. F51 was directly cured by lignin via the ring-opening reaction of epoxy groups of F51 and OH groups (or COOH groups of lignin during the curing process of rubber compounds, as was particularly evident from Fourier transform infrared spectroscopy (FTIR studies and maximum torque of the curing analysis. The existence of lignin-F51 networks were also detected by scanning electron microscope (SEM and dynamic mechanical analysis (DMA. The structure of the SBR/lignin/F51 was also characterized by rubber process analyzer (RPA, thermogravimetric analysis (TGA and determination of crosslinking density. Due to rigid lignin-F51 networks achieved in SBR/lignin/F51 composites, it was found that the hardness, modulus, tear strength, crosslinking density, the temperature of 5 and 10% weight-loss were significantly enhanced with the loading of F51.

  15. Hyperbranched polyester: single route synthesis, characterization and evaluation as impact modifier of an epoxy resin; Poliester hiperramificado: sintese por uma rota simples, caracterizacao e avaliacao como modificador de impacto de uma resina epoxi

    Energy Technology Data Exchange (ETDEWEB)

    Miranda, B.H.S.; Sousa, A.R., E-mail: rangel@deii.cefetmg.br [Centro Federal de Educacao Tecnologica de Minas Gerais (DEMAT/CEFET-MG), Belo Horizonte (Brazil). Departamento de Engenharia de Materiais; Alves, A.P.P.; Silva, G.G. [Universidade Federal de Minas Gerais (UFMG), Belo Horizonte (Brazil). Departamento de Quimica. Lab. de Materiais Polimericos Multicomponentes

    2015-07-01

    Two hyperbranched polyesters were obtained using glycerol and adipic acid as monomers, they were characterized through nuclear magnetic resonance ({sup 13}C NMR) to branching degree determination, size exclusion chromatography to molar mass obtention and thermogravimetric analysis (TGA) to evaluate the thermal stability. The polyesters synthesized were added to epoxy resin, at 10% by weight, to evaluate the implication on mechanical properties, impact and stress strain, and thermal (glassy transition temperature - Tg). We observed that rising the synthesis time from 6 to 15,5 hours the degree of branching, molar mass and thermal stability of the polyester increased. The addition of hyperbranched polyesters did not change the mechanical properties of epoxy resin significantly, but the Tg was reduced. (author)

  16. Facile fabrication of superhydrophobic films with fractal structures using epoxy resin microspheres

    Energy Technology Data Exchange (ETDEWEB)

    Quan, Yun-Yun; Zhang, Li-Zhi, E-mail: lzzhang@scut.edu.cn

    2014-02-15

    A simple method has been developed to fabricate superhydrophobic surfaces with fractal structures with epoxy resin microspheres (ERMs). The ERMs is produced by phase separation in an epoxy-amine curing system with a silica sol (SS) dispersant. The transparent epoxy solution becomes cloudy and turns into epoxy suspension (ES) in this process. The fractal structure (two tier structure) generated by synthetic epoxy resin microspheres (ERMs) and deposited nanoincrutations on the surfaces of these ERMs, which have been observed by scanning electron microscope (SEM). The curing time of ES is an important condition to obtain films with good comprehensive performances. Superhydrophobic films can be prepared by adding extra SS into ES with a curing time longer than 5 h. The optimal curing time is 10 h to fabricate a film with good mechanical stability and high superhydrophobicity. In addition, a surface with anti-wetting property of impacting microdroplets can be fabricated by prolonging the curing time of ES to 24 h. The gradually decreased hydrophilic groups resulted from a longer curing time enable the surface to have smaller surface adhesions to water droplets, which is the main reason to keep its superhydrophobicity under impacting conditions. The coated surface is highly hydrophobic and the impacting water droplets are bounced off from the surface.

  17. Facile fabrication of superhydrophobic films with fractal structures using epoxy resin microspheres

    Science.gov (United States)

    Quan, Yun-Yun; Zhang, Li-Zhi

    2014-02-01

    A simple method has been developed to fabricate superhydrophobic surfaces with fractal structures with epoxy resin microspheres (ERMs). The ERMs is produced by phase separation in an epoxy-amine curing system with a silica sol (SS) dispersant. The transparent epoxy solution becomes cloudy and turns into epoxy suspension (ES) in this process. The fractal structure (two tier structure) generated by synthetic epoxy resin microspheres (ERMs) and deposited nanoincrutations on the surfaces of these ERMs, which have been observed by scanning electron microscope (SEM). The curing time of ES is an important condition to obtain films with good comprehensive performances. Superhydrophobic films can be prepared by adding extra SS into ES with a curing time longer than 5 h. The optimal curing time is 10 h to fabricate a film with good mechanical stability and high superhydrophobicity. In addition, a surface with anti-wetting property of impacting microdroplets can be fabricated by prolonging the curing time of ES to 24 h. The gradually decreased hydrophilic groups resulted from a longer curing time enable the surface to have smaller surface adhesions to water droplets, which is the main reason to keep its superhydrophobicity under impacting conditions. The coated surface is highly hydrophobic and the impacting water droplets are bounced off from the surface.

  18. Surface modification of an epoxy resin with polyamines and polydopamine: The effect on the initial electroless copper deposition

    Energy Technology Data Exchange (ETDEWEB)

    Schaubroeck, David, E-mail: David.Schaubroeck@elis.ugent.be [Center for Microsystems Technology (CMST), imec and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium); Mader, Lothar [Center for Microsystems Technology (CMST), imec and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium); De Geyter, Nathalie; Morent, Rino [Research Unit Plasma Technology (RUPT), Department of Applied Physics, Faculty of Engineering, Ghent University, Sint-Pietersnieuwstraat 41, B-9000 Ghent (Belgium); Dubruel, Peter [Polymer Chemistry and Biomaterials Research Group, Ghent University, Krijgslaan 281 S4 bis, B-9000 Ghent (Belgium); Vanfleteren, Jan [Center for Microsystems Technology (CMST), imec and Ghent University, Technologiepark 914A, B-9052 Ghent (Belgium)

    2014-06-01

    This paper describes the influence of polydopamine and polyamine surface modifications of an etched epoxy cresol novolak (ECN) resin on the initial electroless copper deposition. Three different strategies to introduce polyamines on a surface in aqueous environment are applied: via polyethyleneimine adsorption (PEI), via polydopamine and via polyamines grafted to polydopamine. Next, the influence of these surface modifications on the catalytic palladium activation is investigated through X-ray photoelectron spectroscopy (XPS) analysis. Finally, the initial electroless copper deposition on modified epoxy surfaces is evaluated using SEM and Energy Dispersive Spectroscopy (EDS). Grafted polyamines on polydopamine surface modifications result in a large increase of the initial deposited copper.

  19. Thermoplastic impact property improvement in hybrid natural fibre epoxy composite bumper beam

    International Nuclear Information System (INIS)

    Davoodi, M M; Sapuan, S M; Ali, Aidy; Ahmad, D; Khalina, A

    2010-01-01

    Utilization of thermoset resin as a bumper beam composite matrix is currently more dominated in car manufacturer suppliers, because of availability, easy processing, low material cost and production equipment investment. Moreover, low viscosity, shrinkage and excellent flow facilitate better fibre impregnation and proper surface resin wetting. Three-dimensional cross linking curing increase impact, creep and environmental stress cracking resistance properties. Low impact properties of natural fibre epoxy composite, are main issues in its employment for automotive structural components. Impact properties in epoxy composite bumper beam could be increased by modifying the resin, reinforcement and manufacturing process as well as geometry parameters such as cross section, thickness, added ribs and fixing method optimizations could strengthen impact resistance. There are two main methods, flexibilisation and toughening, as modifying the resin in order to improve the impact properties of epoxy composite, which form single phase or two-phase morphology to make modifier as epoxy or from separate phase to keep the thermo-mechanical properties. Liquid rubber, thermoplastic, core shell particle and rigid particle are different methods of toughening improvements. In this research, thermoplastic toughening has used to improve impact properties in hybrid natural fibre epoxy composite for automotive bumper beam and has achieved reasonable impact improvements.

  20. Ultrasonic Characterisation of Epoxy Resin/Polyethylene Terephthalate (PET Char Powder Composites

    Directory of Open Access Journals (Sweden)

    Imran ORAL

    2016-11-01

    Full Text Available This study is carried out in order to determine the elastic properties of the Epoxy Resin (ER / Polyethylene terephthalate (PET Char Powder Composites by ultrasonic wave velocity measurement method. Plastic waste was recycled as raw material for the preparation of epoxy composite materials. The supplied chars were mixed with epoxy resin matrix at weight percentages of 10 %, 20 % and 30 % for preparing ER/PET Char Powder (PCP composites. The effect of PET char powder on the elastic properties of ER/PCP composites were investigated by ultrasonic pulse-echo method. According to the obtained results, the composition ratio of 80:20 is the most appropriate composition ratio, which gave the highest elastic constants values for ER/PCP composites. On the other hand, the best electrical conductivity value was obtained for 70:30 composition ratio. It was observed that ultrasonic shear wave velocity correlated more perfectly than any other parameters with hardness.DOI: http://dx.doi.org/10.5755/j01.ms.22.4.12190

  1. Synthesis of a new hardener agent for self-healing epoxy resins

    Science.gov (United States)

    Raimondo, Marialuigia; Guadagno, Liberata; Naddeo, Carlo; Longo, Pasquale; Mariconda, Annaluisa; Agovino, Anna

    2014-05-01

    Actually, the development of smart composites capable of self-repair in aeronautical structures is still at the planning stage owing to complex issues to overcome. One of the critical points in the development of self-healing epoxy resin is related to the impossibility to employ primary amines as hardeners. In this paper, the synthesis of a new hardener for self-healing resins is shown together with applicability conditions/ranges.

  2. Foam, Foam-resin composite and method of making a foam-resin composite

    Science.gov (United States)

    Cranston, John A. (Inventor); MacArthur, Doug E. (Inventor)

    1995-01-01

    This invention relates to a foam, a foam-resin composite and a method of making foam-resin composites. The foam set forth in this invention comprises a urethane modified polyisocyanurate derived from an aromatic amino polyol and a polyether polyol. In addition to the polyisocyanurate foam, the composite of this invention further contains a resin layer, wherein the resin may be epoxy, bismaleimide, or phenolic resin. Such resins generally require cure or post-cure temperatures of at least 350.degree. F.

  3. Electron-beam curing of epoxy resins: effect of alcohols on cationic ...

    Indian Academy of Sciences (India)

    Unknown

    Electron-beam (e-beam) induced polymerization of epoxy resins proceeds via cationic mechanism in presence of suitable ... generate ionic species, free radicals, and/or molecules in .... bisphenol A) and the effect of presence of different OH.

  4. Block Copolymer Modified Epoxy Amine System for Reactive Rotational Molding: Structures, Properties and Processability

    Science.gov (United States)

    Lecocq, Eva; Nony, Fabien; Tcharkhtchi, Abbas; Gérard, Jean-François

    2011-05-01

    Poly(styrene-butadiene-methylmethacrylate) (SBM) and poly(methylmethacrylate-butyle-acrylate-methylmethacrylate) (MAM) triblock copolymers have been dissolved in liquid DGEBA epoxy resin which is subsequently polymerized by meta-xylene diamine (MXDA) or Jeffamine EDR-148. A chemorheology study of these formulations by plate-plate rheology and by thermal analysis has allowed to conclude that the addition of these copolymer blocks improve the reactive rotational moulding processability without affecting the processing time. Indeed, it prevents the pooling of the formulation at the bottom of the mould and a too rapid build up of resin viscosity of these thermosetting systems. The morphology of the cured blends examined by scanning electron microscopy (SEM) shows an increase of fracture surface area and thereby a potential increase of the toughness with the modification of epoxy system. Dynamic mechanical spectroscopy (DMA) and opalescence of final material show that the block PMMA, initially miscible, is likely to induce phase separation from the epoxy-amine matrix. Thereby, the poor compatibilisation between the toughener and the matrix has a detrimental effect on the tensile mechanical properties. The compatibilisation has to be increased to improve in synergy the processability and the final properties of these block copolymer modified formulations. First attempts could be by adapting the length and ratio of each block.

  5. The Effects of in Situ-Formed Silver Nanoparticles on the Electrical Properties of Epoxy Resin Filled with Silver Nanowires

    Directory of Open Access Journals (Sweden)

    Gwang-Seok Song

    2016-04-01

    Full Text Available A novel method for preparing epoxy/silver nanocomposites was developed via the in situ formation of silver nanoparticles (AgNPs within the epoxy resin matrix while using silver nanowires (AgNWs as a conductive filler. The silver–imidazole complex was synthesized from silver acetate (AgAc and 1-(2-cyanoethyl-2-ethyl-4-methylimidazole (imidazole. AgNPs were generated in situ during the curing of the epoxy resin through the thermal decomposition of the AgAc–imidazole complex, which was capable of reducing Ag+ to Ag by itself. The released imidazole acted as a catalyst to cure the epoxy. Additionally, after the curing process, the in situ-generated AgNPs were stabilized by the formed epoxy network. Therefore, by using the thermal decomposition method, uniformly dispersed AgNPs of approximately 100 nm were formed in situ in the epoxy matrix filled with AgNWs. It was observed that the nanocomposites containing in situ-formed AgNPs exhibited isotropic electrical properties in the epoxy resins in the presence of AgNWs.

  6. Modification of Aliphatic Petroleum Resin by Peracetic Acid

    OpenAIRE

    Bondaletov, Vladimir Grigoryevich; Bondaletova, Lyudmila Ivanovna; Hamlenko, A.; Bondaletov, Oleg Vladimirovich; Starovoit, M.

    2014-01-01

    This work demonstrates the possibility of obtaining modified aliphatic resin (PRC5) by means of petroleum resin oxidation by peracetic acid. We have experimentally determined oxidation conditions that lead to producing resin with maximum epoxy and acid numbers. Ratio of "oxidative system: PRC5" is 0.5:1, process duration is 2 hours. The modified resin structure is determined by IR and NMR spectroscopy.

  7. Optimization of the rheological properties of epoxy resins for glass and carbon reinforced plastics

    Science.gov (United States)

    Phyo Maung, Pyi; Malysheva, G.; Romanova, I.

    2016-10-01

    Vacuum assisted resin transfer moulding (VARTM) offers advantages such as simplicity, low cost of consumables, and the ability to carry out the impregnation process and curing without using expensive equipment and tooling. In the VARTM process, rheological properties of resin have a critical impact on the impregnation and curing process. In this article, the experimental results of viscosity are presented, including the glass transition temperature, and the tensile and bending strength of the epoxy binders with the amine hardener, which depend on the quantity of its active solvent composition. The active solvent used is diethylene glycol. It shows that for an increase in the content of the active solvent, a reduction in the viscosity and a reduction of the glass transition temperature and strength occurs. The optimum composition of the binder is selected by using the Pareto optimization criteria and the Cayley - Smorodinskaya method. By using the epoxy binder, the active solvent should not exceed 10-15% by weight. This approach helps to optimize the amount of active solvent added to the epoxy resins for the criterion of viscosity, strength, and heat resistance.

  8. Influence of the molecular structure on hydrolyzability of epoxy resins

    International Nuclear Information System (INIS)

    Pays, M.F.

    1996-01-01

    EDF has decided to use glass reinforced composites for certain pipework in Pressurized Water Reactors (service water, emergency-supplied service water, fine pipe works, etc...) as a replacement for traditional materials. In practice, steel is prone to rapid corrosion in these circuits; introducing composites could prove economically viable if their long term behaviour can be demonstrated. However, composite materials can undergo deterioration in service through hydrolysis of the resin or the fibre-matrix interface. Different resins can be chosen depending on the programmed use. A first study has covered the hydrolyzability of polyester and vinyl ester resins. The present document undertakes the resistance to hydrolysis of epoxy resins, concentrating on those reputed to withstand high temperatures. This research uses model monomer, linking the molecular structure of the materials to their resistance to hydrolysis. (author)

  9. Recyclable epoxy resins: An example of green approach for advanced composite applications

    Science.gov (United States)

    Cicala, Gianluca; Rosa, Daniela La; Musarra, Marco; Saccullo, Giuseppe; Banatao, Rey; Pastine, Stefan

    2016-05-01

    Automotive composite applications are increasingly growing due to demand for lightweight structures to comply to the requirements for fuel reduction. HP-RTM is gaining relevance as one of the preferred production technologies for high volume applications. The BMW i3 life module being a notable example of HP-RTM application. The key aspects of HP-RTM are the short injection times (i.e. less than 1min) and the fast curing of the thermoset resins (i.e. less than 10min). The choice of using thermosets poses relevant issues for their limited recycling options. The standard recycling solution is the incineration but, this solution poses some concerns in terms of global environmental impact. Novel solutions are presented in this work based on the use of recyclable epoxy systems. In our work the results of experimentation carried out by our group with cleavable ammines by Connora Technologies and bioepoxy resins by Entropy Resins will be discussed. The multiple uses of recycled matrices obtained treating the recyclable epoxy resins are discussed in the framework of a "cradle" to "crave" approach. Finally, Life Cycle Assessment (LCA) is used to evaluate the environmental benefits of the proposed approach.

  10. Experimental study and model development for 'uranium dioxide-epoxy resin' heat treatment

    International Nuclear Information System (INIS)

    Chairat, Aziza

    2015-01-01

    In order to characterize nuclear fuels, samples are currently embedded in an epoxy polymer resin. In storage conditions, the presence of organic products in contact with highly radioactive material generates gas due to a radiolysis phenomenon. Samples management imposes the definition of a fuel and resin separation process. This work aims at developing a tool for the optimal design and control of a suitable heat treatment process. This development is based on experiments and on the modeling of the resin pyrolysis reactions coupled to mass, heat and momentum transfers. One of the difficulties of the study lies to the needed process control on various scales: i) on a global scale to represent the treatment conditions and ii) on a local scale to represent the conditions close to fuel material. This study uses a combined modeling - simulation approach with experiments carried out with the help of a thermo-balance for kinetic data acquisition, on the one hand and in an experimental oven, on the other hand. The process will be performed in two stages, resin pyrolysis and residue (Char) oxidation. Nuclear fuel can be oxidized during both stages. Indeed, the pyrolysis degrades the resin and generated pyrolysis gases, which produce an oxidizing atmosphere. Oxidation of pyrolysis residue can modify the structure of spent fuel and liberate fission gases. The resin pyrolysis produced non-condensable gases, steam, tar and char. The final hydrogen content in the char has to be as low as possible and close to zero to be sure that the radiolysis phenomenon will never occur during of nuclear fuel storage. The process development has been carried out in stages. The first step is to investigate the overall kinetics of epoxy degradation and the determination of the generated gas kinetics. The influence of the presence of nuclear fuel is investigated with epoxy-UO 2 mixture. The results showed no significant effect of the nuclear fuel presence. The second part is the coupling of

  11. Space charge distributions in glass fibre/epoxy resin composites under dc 10 kV mm-1 electric field

    International Nuclear Information System (INIS)

    Tanaka, Hidesato; Ohki, Yoshimichi; Fukunaga, Kaori; Maeno, Takashi; Okamoto, Kenji

    2007-01-01

    In this paper, the authors discuss one- and three-dimensional space charge distributions in glass fibre/epoxy resin composites. By the conventional pulsed electroacoustic (PEA) method, only a one-dimensional distribution of the average charge over a whole area parallel to the two electrodes can be observed. Therefore, the authors have developed a new PEA system capable of measuring a three-dimensional space charge distribution. Using this system, they measured the charge distribution in glass fibre/epoxy resin composites made of lattice-woven glass fibre and epoxy resin. It has become clear that spatial variation in signal intensity observed depends on the internal structure of the composite. There appear repetitious positions where a high charge density is observed on the same lateral cross section along the vertical direction in the composite. Such positions are consistent with the intersections of the glass fibres. Accumulation of mobile charge carriers or appearance of polarization charge due to mismatch of the ratio of the conductivity and permittivity between the glass fibre and the epoxy resin is thought to be responsible for the PEA signals

  12. Epoxy resins used to seal brachytherapy seed

    International Nuclear Information System (INIS)

    Ferreira, Natalia Carolina Camargos; Ferraz, Wilmar Barbosa; Reis, Sergio Carneiro dos; Santos, Ana Maria Matildes dos

    2013-01-01

    Prostate cancer treatment with brachytherapy is recommended for patients with cancer at an early stage. In this treatment, small radioactive seeds are implanted directly in the prostate gland. These seeds are composed at least of one radionuclide carrier and an X-ray marker enclosed within a metallic tube usually sealed by laser process. This process is expensive and, furthermore, it can provoke a partial volatilization of the radionuclide and change the isotropy in dose distribution around the seed. In this paper, we present a new sealing process using epoxy resin. Three kinds of resins were utilized and characterized by scanning electron microscopy (SEM), energy dispersive X ray (EDS) and by differential scanning calorimetry (DSC) after immersion in simulated body fluid (SBF) and in sodium iodine solution (NaI). The sealing process showed excellent potential to replace the sealing laser usually employed. (author)

  13. Nanostructure of tetrafunctional epoxy resins and composites: Correlation to moisture absorption properties

    Science.gov (United States)

    Bolan, Brett Andrew

    The effect that changes in network topology, while maintaining a constant network polarity (i.e. thermodynamic driving force was kept constant), had upon the moisture absorption properties of an aerospace grade tetrafunctional epoxy (TGMDA) cured with multifunctional amines were investigated. Utilizing Positron Annihilation Lifetime Spectroscopy (PALS) to characterize the nanoscale structure of these epoxies, it was found that as the "static" hole volume (a measurement of packing defects at 0K) increased so did the equilibrium uptake. PALS studies of one of these resins cured to varying extents, found that this static amount increased with degree of cure indicating that the network becomes more open as a direct consequence of crosslinking. Polar groups, which are the attractive force for diffusion, are in the vicinity of these crosslinks, therefore it is believed that the increase in static hole volume results in exposing more polar groups for absorption. The diffusion coefficient, which is representative of the kinetic aspect of diffusion, was also investigated. It was discovered that the amount of nanohole volume in the polymer; whether the total, the static, or dynamic (i.e. thermally activated) does not correlate to the diffusion coefficient in anyway. Furthermore, at an isotherm the diffusion coefficients for all these materials were relatively constant. From this it is hypothesized that it is the similar sub-Tsb{g} motions of these resins which is the rate limiting step in diffusion. This was bolstered by the fact that the activation energy for diffusion and for the sub-Tsb{g} motions for these epoxies are of the same order of magnitude. The nanostructure of fiber reinforced epoxy composites (i.e. a boron/epoxy and a graphite/epoxy) were probed with the bulk PALS technique as well. It was observed that for the graphite/epoxy composite and its flash (i.e. no fibers present) cured under identical conditions, that the nanoholes in the composite were larger than

  14. Post-irradiation hardness of resin-modified glass ionomer cements and a polyacid-modified composite resin

    International Nuclear Information System (INIS)

    Yap, A.U.J.

    1997-01-01

    This study examined the post-irradiation hardness of resin-modified glass ionomer cements and a polyacid-modified composite resin using a digital microhardness tester. Change in hardness of these materials over a period of 6 months was compared to that of conventional glass ionomer cements and a composite resin. With the exception of the composite resin, all materials showed a significant increase in hardness over 24 h after their initial set. Dual-cure resin-modified glass ionomer cements showed decreased hardness with increased storage time in saline at 37 o C. Results suggest that the addition of resins to glass ionomer cements does not improve initial hardness and does not negate the acid-base reaction of conventional cements. Resin addition may, however, lead to increased water sorption and decreased hardness. (author)

  15. Flame resistant hybrid epoxy composites

    Czech Academy of Sciences Publication Activity Database

    Śliwa, R.; Oleksy, M.; Heneczkowski, M.; Oliwa, R.; Budzik, G.; Kozik, B.; Markowska, O.; Strachota, Adam

    2015-01-01

    Roč. 60, č. 10 (2015), s. 667-670 ISSN 0032-2725 Institutional support: RVO:61389013 Keywords : epoxy resin * quaternary phosphonium salts * modified bentonite Subject RIV: CD - Macromolecular Chemistry Impact factor: 0.718, year: 2015

  16. Novel epoxy-silicone thermolytic transparent packaging adhesives chemical modified by ZnO nanowires for HB LEDs

    International Nuclear Information System (INIS)

    He Ying; Wang Junan; Pei Changlong; Song Jizhong; Zhu Di; Chen Jie

    2010-01-01

    A novel high transparent thermolytic epoxy-silicone for high-brightness light-emitting diode (HB-LED) is introduced, which was synthesized by polymerization using silicone matrix via diglycidyl ether bisphenol-A epoxy resin (DGEBA) as reinforcing agent, and filling ZnO nanowires to modify thermal conductivity and control refractive index of the hybrid material. The interactions of ZnO nanowires with polymers are mediated by the ligands attached to the nanoparticles. Thus, the ligands markedly influence the properties of ZnO nanowires/epoxy-silicone composites. The refractive indices of the prepared hybrid adhesives can be tuned by the ZnO nanowires from 1.4711 to 1.5605. Light transmittance can be increased by 20% from 80 to 95%. The thermal conductivity of the transparent packaging adhesives is 0.89-0.90 W/mK.

  17. DEVELOPMENT OF A METHOD STATISTICAL ANALYSIS ACCURACY AND PROCESS STABILITY PRODUCTION OF EPOXY RESIN ED-20

    Directory of Open Access Journals (Sweden)

    N. V. Zhelninskaya

    2015-01-01

    Full Text Available Statistical methods play an important role in the objective evaluation of quantitative and qualitative characteristics of the process and are one of the most important elements of the quality assurance system production and total quality management process. To produce a quality product, one must know the real accuracy of existing equipment, to determine compliance with the accuracy of a selected technological process specified accuracy products, assess process stability. Most of the random events in life, particularly in manufacturing and scientific research, are characterized by the presence of a large number of random factors, is described by a normal distribution, which is the main in many practical studies. Modern statistical methods is quite difficult to grasp and wide practical use without in-depth mathematical training of all participants in the process. When we know the distribution of a random variable, you can get all the features of this batch of products, to determine the mean value and the variance. Using statistical control methods and quality control in the analysis of accuracy and stability of the technological process of production of epoxy resin ED20. Estimated numerical characteristics of the law of distribution of controlled parameters and determined the percentage of defects of the investigated object products. For sustainability assessment of manufacturing process of epoxy resin ED-20 selected Shewhart control charts, using quantitative data, maps of individual values of X and sliding scale R. Using Pareto charts identify the causes that affect low dynamic viscosity in the largest extent. For the analysis of low values of dynamic viscosity were the causes of defects using Ishikawa diagrams, which shows the most typical factors of the variability of the results of the process. To resolve the problem, it is recommended to modify the polymer composition of carbon fullerenes and to use the developed method for the production of

  18. Experimental Investigation and Taguchi Optimisation of Drilling Properties on Teak Wood Reinforced Epoxy Resin

    Science.gov (United States)

    Lilly Mercy, J.; Shaqir Tanvir, Mohamed; Swaroopkanth, K.

    2017-05-01

    The drilling properties of teak reinforced epoxy resin composite are explored in this work. The thrust force and temperature during the drilling process was found and optimised. Nine holes were drilled in accordance with L9 orthogonal array on Medium Density Fibre board and Teak wood reinforced epoxy composite board and the thrust force and temperature induced during drilling is measured. Drilling experiments were conducted using CNC Vertical drilling machine and the thrust force was measured using dynamometer and temperature using infra-red thermometer. The experiments were conducted with varying levels of spindle speed and feed rate and optimised using Taguchi optimisation. It was observed that higher thrust and temperature were observed while drilling teak wood composite due to the high mechanical strength of teak wood. The hard and brittle properties of the resin seemed to be more pronounced in the composite. The experimental results were optimised to find the best combination of input parameters for reduced thrust and temperature. When speed increases, thrust force decreases and temperature increases. When feed increases, thrust force increases and temperature decreases. Experimental findings encouragesto use teak wood reinforced epoxy resin as a substitute for the traditionally used Medium Density Fibre Board. The percentage of mixing of teak dust can be increased with various resin combinations to arrive at the best suitable combination for obtaining optimal mechanical properties.

  19. Effect of Thermally Reduced Graphene Oxide on Mechanical Properties of Woven Carbon Fiber/Epoxy Composite

    OpenAIRE

    Nitai Chandra Adak; Suman Chhetri; Naresh Chandra Murmu; Pranab Samanta; Tapas Kuila

    2018-01-01

    Thermally reduced graphene oxide (TRGO) was incorporated as a reinforcing filler in the epoxy resin to investigate the effect on the mechanical properties of carbon fiber (CF)/epoxy composites. At first, the epoxy matrix was modified by adding different wt % of TRGO from 0.05 to 0.4 wt % followed by the preparation of TRGO/CF/epoxy composites througha vacuum-assisted resin transfer molding process. The prepared TRGO was characterized by using Fourier transform infrared spectroscopy, Raman Spe...

  20. Nanocomposites based on epoxy resin and montmorillonite: effect of clay percent and dispersion state on thermomechanical properties

    International Nuclear Information System (INIS)

    Zaioncz, Soraia; Soares, Bluma G.

    2009-01-01

    Nanocomposites of epoxy resin modified with PMMA and montmorillonite organophilic were synthesized with clay content equal to 0.1, 1, 2.5, 5 and 7 (wt %). Dispersion state and the nano structure of materials has been investigated using small angle X-ray scattering (SAXS). The nanocomposites containing 0.1 (wt %) of clay showed an exfoliated morphology, while the nanocomposites with higher clay content (1 to 7 wt %) show that the dispersion state is less uniform and that large aggregates coexist with tactoids stacks of two or three platelets. The nano structure of materials was correlated with its thermomechanical properties obtained by DMTA. The results showed an increase in Tg of the materials to clay content of up to 5 wt % and an increase in the storage modulus for the epoxy matrix. (author)

  1. Influence of Coating with Some Natural Based Materials on the Erosion Wear Behavior of Glass Fiber Reinforced Epoxy Resin

    OpenAIRE

    Aseel Basim Abdul Hussein; Emad Saadi AL-Hassani; Reem Alaa Mohamed

    2015-01-01

    In the present study, composites were prepared by Hand lay-up molding. The composites constituents were epoxy resin as a matrix, 6% volume fractions of glass fibers (G.F) as reinforcement and 3%, 6% volume fractions of preparation natural material (Rice Husk Ash, Carrot Powder, and Sawdust) as filler. Studied the erosion wear behavior and coating by natural wastes (Rice Husk Ash) with epoxy resin after erosion. The results showed the non – reinforced epoxy have lower resistance erosion than n...

  2. Epoxy modified bitumen : Chemical hardening and its interpretation

    NARCIS (Netherlands)

    Apostolidis, P.; Pipintakos, G.; van de Ven, M.F.C.; Liu, X.; Erkens, Sandra; Scarpas, Athanasios

    2018-01-01

    Epoxy modified bitumen (EMB) is a promising technology for long lasting paving materials ensuring higher resistance to rutting, oxygen- and moisture-induced damage. In this paper, an analysis of the chemical reactions that take place during the chemical hardening process (curing) of epoxy modified

  3. The Effect of an Active Diluent on the Properties of Epoxy Resin and Unidirectional Carbon-Fiber-Reinforced Plastics

    Science.gov (United States)

    Solodilov, V. I.; Gorbatkina, Y. A.; Kuperman, A. M.

    2003-11-01

    The influence of an active diluent on the properties of an epoxy matrix and carbon-fiber-reinforced plastics (CFRP) is investigated. The physicomechanical properties of an ED-20 epoxy resin modified with diglycidyl ether of diethylene glycol (DEG-1), the adhesion strength at the epoxy matrix-steel wire interface, and the mechanical properties of unidirectional CFRP are determined. The concentration of DEG-1 was varied from 0 to 50 wt.%. The properties of the matrix, the interface, and the composites are compared. It is stated that the matrix strength affects the strength of unidirectional CFRP in bending and not their strength in tension, compression, and shear. The latter fact seems somewhat unexpected. The interlaminar fracture toughness of the composites investigated correlates with the ultimate elongation of the binder. A comparison between the concentration dependences of adhesion strength and the strength of CFRP shows that the matrices utilized provide such a high interfacial strength that the strength of CFRP no longer depends on the adhesion of its constituents.

  4. Syringaresinol: A Renewable and Safer Alternative to Bisphenol A for Epoxy-Amine Resins.

    Science.gov (United States)

    Janvier, Marine; Hollande, Louis; Jaufurally, Abdus Samad; Pernes, Miguel; Ménard, Raphaël; Grimaldi, Marina; Beaugrand, Johnny; Balaguer, Patrick; Ducrot, Paul-Henri; Allais, Florent

    2017-02-22

    A renewable bisepoxide, SYR-EPO, was prepared from syringaresinol, a naturally occurring bisphenol deriving from sinapic acid, by using a chemo-enzymatic synthetic pathway. Estrogenic activity tests revealed no endocrine disruption for syringaresinol. Its glycidylation afforded SYR-EPO with excellent yield and purity. This biobased, safe epoxy precursor was then cured with conventional and renewable diamines for the preparation of epoxy-amine resins. The resulting thermosets were thermally and mechanically characterized. Thermal analyses of these new resins showed excellent thermal stabilities (T d5 % =279-309 °C) and T g ranging from 73 to 126 °C, almost reaching the properties of those obtained with the diglycidylether of bisphenol A (DGEBA), extensively used in the polymer industry (T d5 % =319 °C and T g =150 °C for DGEBA/isophorone diamine resins). Degradation studies in NaOH and HCl aqueous solutions also highlighted the robustness of the syringaresinol-based resins, similar to bisphenol A (BPA). All these results undoubtedly confirmed the potential of syringaresinol as a greener and safer substitute for BPA. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  5. The study of epoxy polyamide and polyvinyl resins as corrosion ...

    African Journals Online (AJOL)

    The corrosion resistance of two commonly used protective coatings (epoxy polyamide and polyvinyl resins) in the Niger Delta area of Nigeria has been assessed. The coatings on low carbon steel were subjected to varying conditions of pH, temperature and exposure time and the corrosion rates calculated. At a pH of 2, 3, 4, ...

  6. Mechanical properties of multi-walled carbon nanotube/epoxy polysulfide nanocomposite

    International Nuclear Information System (INIS)

    Shirkavand Hadavand, Behzad; Mahdavi Javid, Kimya; Gharagozlou, Mehrnaz

    2013-01-01

    Highlights: ► Preparation of epoxy polysulfide nanocomposite. ► Multi-walled carbon nanotubes have been modified and dispersed in epoxy polysulfide matrix. ► Mechanical properties of MWNT/epoxy polysulfide have been studied. - Abstract: In this research, multi-walled carbon nanotubes (MWCNTs) were modified by acid functionalization (H 2 SO 4 :HNO 3 = 1:3 by volume) and then mechanical properties of reinforced epoxy polysulfide resin by the both pure and treated MWNTs have been evaluated. For achieving this goal, different weight percentages of pure and treated MWCNT (0.1–0.3 wt%) were dispersed in the epoxy polysulfide resin separately and then mixed with curing agent. Experimental results have shown significant difference between acid treated and untreated MWCNTs in mechanical properties of epoxy polysulfide nanocomposites. In nanocomposite with 0.1–0.3% acid treated MWCNTs we observed increase of Young’s modulus from 458 to 723 MPa, tensile strength from 5.29 to 8.83 MPa and fracture strain from 0.16% to 0.25%. For understanding the structure and morphology of nanocomposite, the dispersion states were studied using scanning electron microscopy (SEM) and field emission electron microscopy (FESEM). The results showed better dispersion of modified carbon nanotube than unmodified in polymeric matrix

  7. Influence of Electrolytical Oxidising of Silumine Surfaces on the Quality of Bonding with Epoxy Resin

    Directory of Open Access Journals (Sweden)

    Posmyk A.

    2016-09-01

    Full Text Available The article presents the preparation process of AC-AlSi12 aluminum alloy surface by application of anodic oxidation method. The method enables the formation of a porous oxide layer (Al2O3 which generates the substrate of durable adhesive bond with an epoxy resin. It also presents the influence of the form of silicon precipitates in the modified alloy upon anodizing process, uniform structure and thickness of the oxide layer as well as the topography of its surface which is expected to improve adhesion of the resin and silumin. The paper describes how the position of oxidized surface against the negative electrode influences the coating structure. The studied silumins are intended to form the material for casting of 3 dimensional objects whose parts will change the distribution of electric field strength that may cause non-uniform structure of the coating.

  8. Investigation of nanoscopic free volume and interfacial interaction in an epoxy resin/modified clay nanocomposite using positron annihilation spectroscopy.

    Science.gov (United States)

    Patil, Pushkar N; Sudarshan, Kathi; Sharma, Sandeep K; Maheshwari, Priya; Rath, Sangram K; Patri, Manoranjan; Pujari, Pradeep K

    2012-12-07

    Epoxy/clay nanocomposites are synthesized using clay modified with the organic modifier N,N-dimethyl benzyl hydrogenated tallow quaternary ammonium salt (Cloisite 10A). The purpose is to investigate the influence of the clay concentration on the nanostructure, mainly on the free-volume properties and the interfacial interactions, of the epoxy/clay nanocomposite. Nanocomposites having 1, 3, 5 and 7.5 wt. % clay concentrations are prepared using the solvent-casting method. The dispersion of clay silicate layers and the morphologies of the fractured surfaces in the nanocomposites are studied using X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. The observed XRD patterns reveal an exfoliated clay structure in the nanocomposite with the lowest clay concentration (≤1 wt. %). The ortho-positronium lifetime (τ(3)), a measure of the free-volume size, as well as the fractional free volume (f(v)) are seen to decrease in the nanocomposites as compared to pristine epoxy. The intensity of free positron annihilation (I(2)), an index of the epoxy-clay interaction, decreases with the addition of clay (1 wt. %) but increases linearly at higher clay concentrations. Positron age-momentum correlation measurements are also carried out to elucidate the positron/positronium states in pristine epoxy and in the nanocomposites. The results suggest that in the case of the nanocomposite with the studied lowest clay concentration (1 wt. %), free positrons are primarily localized in the epoxy-clay interfaces, whereas at higher clay concentrations, annihilation takes place from the intercalated clay layers. Copyright © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  9. Leaching of iodine from composites based on epoxy resin and lead iodide

    International Nuclear Information System (INIS)

    Kalinin, N.N.; Elizarova, A.N.

    1988-01-01

    The scope for using solid composites obtained by incorporating dry powdery lead iodide and its aqueous suspension into epoxy resin for prolonged immobilization of iodine-129 under monitorable storage conditions has been assessed by a study of leaching of iodine

  10. Development of highly effective neutron shielding material made of phenol-novolac type epoxy resin

    Energy Technology Data Exchange (ETDEWEB)

    Cho, Soo Haeng; Jeong, Myeong Soo; Hong, Sun Seok; Lee, Won Kyoung; Kim, Ik Soo; Shin, Young Joon; Do, Jae Bum; Ro, Seung Gy; Oh, Seok Jin

    1998-06-01

    Because the exposure to radiation in the nuclear facilities can be fatal to human, it is important to reduce the radiation dose level to a tolerable level. The purpose of this study is to develop highly effective neutron shielding materials for the shipping and storage cask of radioactive materials or in the nuclear/radiation facilities. On this study, we developed epoxy resin based neutron shielding materials and their various material properties, including neutron shielding ability, fire resistance, combustion characteristics, radiation resistance, thermal and mechanical properties were evaluated experimentally. Especially we developed phenol-novolac type epoxy resin based neutron shielding materials and their characteristics were also evaluated. (author). 22 refs., 11 tabs., 21 figs

  11. A novel specimen-preparing method using epoxy resin as binding material for LIBS analysis of powder samples.

    Science.gov (United States)

    Shi, Linli; Lin, Qingyu; Duan, Yixiang

    2015-11-01

    In view of the inevitable preprocessing of powder samples for LIBS detection, epoxy resin glue was investigated for the first time as a binder of powder samples due to its superior property of improved performance in laser induced breakdown spectroscopy (LIBS) technique as a quantitative analytical tool. For comparative studies of the epoxy resin and traditional polyethylene (PE) pellets in soil, sample detection, the signal intensities of Fe (I) at 404.58 nm, Ca (I) at 443.57 nm, and Cr (I) at 453.52 nm, were studied and subsequently, the calibration curves for these elements were constructed using the standard samples with variable concentrations. The signal intensities of epoxy resin samples were, on average, about 2 times greater than those obtained with the traditional PE pellet samples. Meanwhile, the resin samples showed better R square values of 0.981, 0.985 and 0.979 for curves of Fe (I) 404.58 nm, Ca (I) 443.57 nm, and Cr (I) 453.52 nm, compared to the 0.974, 0.950 and 0.934, of the PE pellet samples. Furthermore, the former represented lower limits of detection (LOD) for Fe, Ca and Cr. These experimental results indicated that this proposed novel method based on epoxy resin can attach samples of properties of high homogeneity, cohesiveness, smoothness and hardness, which are conducive to system stability, testing accuracy and signal enhancement. This method can make LIBS more practical in powder sample analysis. Copyright © 2015 Elsevier B.V. All rights reserved.

  12. Epoxy based nanocomposites with fully exfoliated unmodified clay: mechanical and thermal properties.

    Science.gov (United States)

    Li, Binghai; Zhang, Xiaohong; Gao, Jianming; Song, Zhihai; Qi, Guicun; Liu, Yiqun; Qiao, Jinliang

    2010-09-01

    The unmodified clay has been fully exfoliated in epoxy resin with the aid of a novel ultrafine full-vulcanized powdered rubber. Epoxy/rubber/clay nanocomposites with exfoliated morphology have been successfully prepared. The microstructures of the nanocomposites were characterized by means of X-ray diffraction and transmission electron microscopy. It was found that the unmodified clay was fully exfoliated and uniformly dispersed in the resulting nanocomposite. Characterizations of mechanical properties revealed that the impact strength of this special epoxy/rubber/clay nanocomposite increased up 107% over the neat epoxy resin. Thermal analyses showed that thermal stability of the nanocomposite was much better than that of epoxy nanocomposite based on organically modified clay.

  13. Development of microwave absorbing materials prepared from a polymer binder including Japanese lacquer and epoxy resin

    Science.gov (United States)

    Iwamaru, T.; Katsumata, H.; Uekusa, S.; Ooyagi, H.; Ishimura, T.; Miyakoshi, T.

    Microwave absorption composites were synthesized from a poly urushiol epoxy resin (PUE) mixed with one of microwave absorbing materials; Ni-Zn ferrite, Soot, Black lead, and carbon nano tube (CNT) to investigate their microwave absorption properties. PUE binders were specially made from Japanese lacquer and epoxy resin, where Japanese lacquer has been traditionally used for bond and paint because it has excellent beauty. Japanese lacquer solidifies with oxygen contained in air's moisture, which has difficulty in making composite, but we improved Japanese lacquer's solidification properties by use of epoxy resin. We made 10 mm thickness composite samples and cut them into toroidal shape to measure permittivity, permeability, and reflection loss in frequencies ranging from 50 Hz to 20 GHz. Electric magnetic absorber's composites synthesized from a PUE binders mixed either with Soot or CNT showed significantly higher wave absorption over -27 dB than the others at frequencies around 18 GHz, although Japanese lacquer itself doesn't affect absorption. This means Japanese lacquer can be used as binder materials for microwave absorbers.

  14. Epoxy Resin Based Composites, Mechanical and Tribological Properties: A Review

    Directory of Open Access Journals (Sweden)

    S.A. Bello

    2015-12-01

    Full Text Available High fuel consumption by automobile and aerospace vehicles built from legacy alloys has been a great challenge to global design and material engineers. This has called for researches into material development for the production of lighter materials of the same or even superior mechanical properties to the existing materials in this area of applications. This forms a part of efforts to achieve the global vision 2025 i.e to reduce the fuel consumption by automobile and aerospace vehicles by at least 75 %. Many researchers have identified advanced composites as suitable materials in this regard. Among the common matrices used for the development of advanced composites, epoxy resin has attained a dominance among its counterparts because of its excellent properties including chemical, thermal and electrical resistance properties, mechanical properties and dimensional stability. This review is a reflection of the extensive study on the currently ongoing research aimed at development of epoxy resin hybrid nanocomposites for engineering applications. In this paper, brief explanation has been given to different terms related to the research work and also, some previous works (in accordance with materials within authors’ reach in the area of the ongoing research have been reported.

  15. Multi-objective robust optimization method for the modified epoxy resin sheet molding compounds of the impeller

    Directory of Open Access Journals (Sweden)

    Xiaozhang Qu

    2016-07-01

    Full Text Available A kind of modified epoxy resin sheet molding compounds of the impeller has been designed. Through the test, the non-metal impeller has a better environmental aging performance, but must do the waterproof processing design. In order to improve the stability of the impeller vibration design, the influence of uncertainty factors is considered, and a multi-objective robust optimization method is proposed to reduce the weight of the impeller. Firstly, based on the fluid-structure interaction,the analysis model of the impeller vibration is constructed. Secondly, the optimal approximate model of the impeller is constructed by using the Latin hypercube and radial basis function, and the fitting and optimization accuracy of the approximate model is improved by increasing the sample points. Finally, the micro multi-objective genetic algorithm is applied to the robust optimization of approximate model, and the Monte Carlo simulation and Sobol sampling techniques are used for reliability analysis. By comparing the results of the deterministic, different sigma levels and different materials, the multi-objective optimization of the SMC molding impeller can meet the requirements of engineering stability and lightweight. And the effectiveness of the proposed multi-objective robust optimization method is verified by the error analysis. After the SMC molding and the robust optimization of the impeller, the optimized rate reached 42.5%, which greatly improved the economic benefit, and greatly reduce the vibration of the ventilation system.

  16. Evaluation of the use of inorganic pigments and fillers in cure of epoxy resins by microwave irradiation

    International Nuclear Information System (INIS)

    Kersting, Daniel; Wiebeck, Helio

    2013-01-01

    The use of microwave in chemical processes began soon after the WW II. The mechanism of curing via microwave heating is independent of the thermal conductivity of the irradiated material and offers a good solution to operate with materials that do not have a good thermal conductivity, such as polymers. Despite these advantages, the use of multimode microwave ovens, the main source used today, indicates some challenges to overcome. Associated with the use of epoxy resins in various applications, the use of pigments and inorganic fillers has added more variables to be studied. Much of the inorganic fillers used commercially are good absorbers of microwave providing changes in the amount of radiation absorbed, and thus the amount of heat transferred to the epoxy resin curing process. After selecting the key fillers and pigments traditionally used in the production of parts with epoxy resins they were subjected to the same microwave irradiation for evaluation of their behavior alone. In order to observe the effect of mixtures 1, 2, and 5% by weight of filler were added to epoxy resin, and it was verified these effects in the curing process. The preliminary results are promising, because for the same cure cycle for different types of fillers added separately, gains in curing time were obtained, making the process of cure via microwave quick and efficient without substantial losses in thermal properties of the final products obtained. (author)

  17. Rheological and electrical properties of hybrid nanocomposites of epoxy resins filled with graphite nanoplatelets and carbon black.

    Science.gov (United States)

    Truong, Quang-Trung; Lee, Seon-Suk; Lee, Dai-Soo

    2011-02-01

    Graphite nanoplatelets (GNP) were prepared by microwave irradiation of natural graphites intercalated with ferric chloride in nitromethane (GIC). Intercalated structure of GIC was confirmed by X-ray diffraction patterns. SEM images of GIC after microwave irradiation showed the exfoliation of GIC, the formation of GNPs. Hybrid nanocomposites of bisphenol-A type epoxy resins filled with GNP and a conductive carbon black (CB) were prepared and rheological and electrical properties of the nanocomposites were investigated. Viscosity and electrical surface resistivity of the nanocomposites showed minima at certain mixtures of GNP and CB in the epoxy resins.

  18. Nanostructured composites based on carbon nanotubes and epoxy resin for use as radar absorbing materials

    Energy Technology Data Exchange (ETDEWEB)

    Silva, Valdirene Aparecida [Instituto Tecnologico de Aeronautica (ITA), Sao Jose dos Campos, SP (Brazil); Folgueras, Luiza de Castro; Candido, Geraldo Mauricio; Paula, Adriano Luiz de; Rezende, Mirabel Cerqueira, E-mail: mirabelmcr@iae.cta.br [Instituto de Aeronautica e Espaco (IAE), Sao Jose dos Campos, SP (Brazil). Div. de Materiais; Costa, Michelle Leali [Universidade Estadual Paulista Julio de Mesquita Filho (DMT/UNESP), Guaratingueta, SP (Brazil). Dept. de Materiais e Tecnologia

    2013-07-01

    Nanostructured polymer composites have opened up new perspectives for multifunctional materials. In particular, carbon nanotubes (CNTs) present potential applications in order to improve mechanical and electrical performance in composites with aerospace application. The combination of epoxy resin with multi walled carbon nanotubes results in a new functional material with enhanced electromagnetic properties. The objective of this work was the processing of radar absorbing materials based on formulations containing different quantities of carbon nanotubes in an epoxy resin matrix. To reach this objective the adequate concentration of CNTs in the resin matrix was determined. The processed structures were characterized by scanning electron microscopy, rheology, thermal and reflectivity in the frequency range of 8.2 to 12.4 GHz analyses. The microwave attenuation was up to 99.7%, using only 0.5% (w/w) of CNT, showing that these materials present advantages in performance associated with low additive concentrations (author)

  19. 21 CFR 177.2280 - 4,4′-Isopropyl-idenedi-phenol-epichloro-hydrin thermo-setting epoxy resins.

    Science.gov (United States)

    2010-04-01

    ... with mixed dimers and trimers of unsaturated C18 monobasic fatty acids derived from animal and... basic thermosetting epoxy resin is made by reacting 4,4′-isopropylidenediphenol with epi-chloro-hydrin...′-isopropylidenediphenol-epichlorohydrin basic resin and limited to use in contact with alcoholic beverages containing not...

  20. Preparation of carbon nanotubes/epoxy resin composites by using hollow glass beads as the carrier

    International Nuclear Information System (INIS)

    Wu, X.F.; Zhao, Y.K.; Zhang, D.; Chen, T.B.; Ma, L.Y.

    2012-01-01

    Hollow glass beads had been utilized as the carrier to assist dispersion of carbon nanotubes in epoxy resin. Hollow glass beads were firstly aminated with gamma-aminopropyl-triethoxysilane, sencondly reacted with carboxyl-functionalized carbon nanotubes via an amidation reaction and susequently mixed with epoxy resin and hardener. The experimental results showed that carbon nanotubes could be loaded on the surfaces of hollow glass beads and approximately a monolayer of carbon nanotubes was formed when the weight ratio of hollow glass beads to carbon nanotubes was 100:5. Moreover, the dispersity of carbon nanotubes in the matrix was improved as compared to the control samples prepared by using a conventional mixing method. (author)

  1. Tensile Properties of Unsaturated Polyester and Epoxy Resin Reinforced with Recycled Carbon-Fiber-Reinforced Plastic

    Science.gov (United States)

    Okayasu, Mitsuhiro; Kondo, Yuta

    2018-06-01

    To better understand the mechanical properties of recycled carbon-fiber-reinforced plastic (rCFRP), CFRP crushed into small pieces was mixed randomly in different proportions (0-30 wt%) with two different resins: unsaturated polyester and epoxy resin. Two different sizes of crushed CFRP were used: 0.1 mm × 0.007 mm (milled CFRP) and 30 mm × 2 mm (chopped CFRP). The tensile strength of rCFRP was found to depend on both the proportion and the size of the CFRP pieces. It increased with increasing proportion of chopped CFRP, but decreased with increasing proportion of milled CFRP. There was no clear dependence of the tensile strength on the resin that was used. A low fracture strain was found for rCFRP samples made with chopped CFRP, in contrast to those made with milled CFRP. The fracture strain was found to increase with increasing content of milled CFRP up to 20 wt%, at which point, coalescence of existing microvoids occurred. However, there was a reduction in fracture strain for rCFRP with 30 wt% of milled CFRP, owing to the formation of defects (blow holes). Overall, the fracture strain was higher for rCFRPs based on epoxy resin than for those based on unsaturated polyester with the same CFRP content, because of the high ductility of the epoxy resin. The different tensile properties reflected different failure characteristics, with the use of chopped CFRP leading to a complicated rough fracture surface and with milled CFRP causing ductile failure through the presence of tiny dimple-like fractures. However, for a high content of milled CFRP (30 wt%), large blow holes were observed, leading to low ductility.

  2. Optimization of interfacial properties of carbon fiber/epoxy composites via a modified polyacrylate emulsion sizing

    Energy Technology Data Exchange (ETDEWEB)

    Yuan, Xiaomin [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Carbon Fiber Engineering Research Center, School of Materials Science and Engineering, Shandong University, Jinan 250061 (China); Zhu, Bo, E-mail: zhubo@sdu.edu.cn [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Carbon Fiber Engineering Research Center, School of Materials Science and Engineering, Shandong University, Jinan 250061 (China); Cai, Xun, E-mail: caixunzh@sdu.edu.cn [School of Computer Science and Technology, Shandong University, Jinan 250101 (China); Liu, Jianjun [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Carbon Fiber Engineering Research Center, School of Materials Science and Engineering, Shandong University, Jinan 250061 (China); Qiao, Kun [Carbon Fiber Engineering Research Center, School of Materials Science and Engineering, Shandong University, Jinan 250061 (China); Yu, Junwei [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Carbon Fiber Engineering Research Center, School of Materials Science and Engineering, Shandong University, Jinan 250061 (China)

    2017-04-15

    Highlights: • An improved interfacial adhesion in CF/EP composite by FSMPA sizing was put forward. • Sized CFs featured promotions of wettability, chemical activity and mechanical property. • A sizing mechanism containing chemical interaction and physical absorption was proposed. - Abstract: The adhesion behavior of epoxy resin to carbon fibers has always been a challenge, on account of the inertness of carbon fibers and the lack of reactive functional groups. In this work, a modified polyacrylate sizing agent was prepared to modify the interface between the carbon fiber and the epoxy matrix. The surface characteristics of carbon fibers were investigated to determine chemical composition, morphology, wettability, interfacial phase analysis and interfacial adhesion. Sized carbon fibers featured improved wettability and a slightly decreased surface roughness due to the coverage of a smooth sizing layer, compared with the unsized ones. Moreover, the content of surface activated carbon atoms increased from 12.65% to 24.70% and the interlaminar shear strength (ILSS) of carbon fiber/epoxy composites raised by 14.2%, indicating a significant improvement of chemical activity and mechanical property. SEM images of the fractured surface of composites further proved that a gradient interfacial structure with increased thicknesses was formed due to the transition role of the sizing. Based on these results, a sizing mechanism consisting of chemical interaction bonding and physical force absorption was proposed, which provides an efficient and feasible method to solve the poor adhesion between carbon fiber and epoxy matrix.

  3. Optimization of interfacial properties of carbon fiber/epoxy composites via a modified polyacrylate emulsion sizing

    International Nuclear Information System (INIS)

    Yuan, Xiaomin; Zhu, Bo; Cai, Xun; Liu, Jianjun; Qiao, Kun; Yu, Junwei

    2017-01-01

    Highlights: • An improved interfacial adhesion in CF/EP composite by FSMPA sizing was put forward. • Sized CFs featured promotions of wettability, chemical activity and mechanical property. • A sizing mechanism containing chemical interaction and physical absorption was proposed. - Abstract: The adhesion behavior of epoxy resin to carbon fibers has always been a challenge, on account of the inertness of carbon fibers and the lack of reactive functional groups. In this work, a modified polyacrylate sizing agent was prepared to modify the interface between the carbon fiber and the epoxy matrix. The surface characteristics of carbon fibers were investigated to determine chemical composition, morphology, wettability, interfacial phase analysis and interfacial adhesion. Sized carbon fibers featured improved wettability and a slightly decreased surface roughness due to the coverage of a smooth sizing layer, compared with the unsized ones. Moreover, the content of surface activated carbon atoms increased from 12.65% to 24.70% and the interlaminar shear strength (ILSS) of carbon fiber/epoxy composites raised by 14.2%, indicating a significant improvement of chemical activity and mechanical property. SEM images of the fractured surface of composites further proved that a gradient interfacial structure with increased thicknesses was formed due to the transition role of the sizing. Based on these results, a sizing mechanism consisting of chemical interaction bonding and physical force absorption was proposed, which provides an efficient and feasible method to solve the poor adhesion between carbon fiber and epoxy matrix.

  4. Study on polyethylene glycol/epoxy resin composite as a form-stable phase change material

    International Nuclear Information System (INIS)

    Fang Yutang; Kang Huiying; Wang Weilong; Liu Hong; Gao Xuenong

    2010-01-01

    Form-stable polyethylene glycol (PEG)/epoxy resin (EP) composite as a novel phase change material (PCM) was prepared using casting molding method. In this new material, PEG acts as the latent heat storage material and EP polymer serves as the supporting material, which provides structural strength and prevents the leakage of the melted PEG. The structure and morphology of the novel composite were observed using Fourier transformation infrared spectroscope (FTIR) and scanning electronic microscope (SEM). The thermo-mechanical property and transition behavior were characterized by polarizing optical microscope (POM), static thermo-mechanical analysis (TMA) and differential scanning calorimeter (DSC). The experimental results show that, as a result of the physical tangled function of the epoxy resin carrier to the PEG segment, the composite macroscopically presents the solid-solid phase change characteristic.

  5. Effect of cure cycle on curing process and hardness for epoxy resin

    Directory of Open Access Journals (Sweden)

    2009-09-01

    Full Text Available A 3-dimensional finite element model is developed to simulate and analyze the temperature and degree of cure field of epoxy casting part during cure process. The present model based on general finite element software ABAQUS is verified by literature example and experimental data. The numerical results show good agreement with literature example and measured data, and are even more accurate than the simulation of literature. After modeling successfully, the influence of temperature cure cycle ramps have on the temperature and degree of cure gradient is investigated. Moreover, the effect of non-uniform temperature and degree of cure field within epoxy casting part on hardness is demonstrated. The present model provides an accurate and novel method that allows further insight into the process of cure for epoxy resin.

  6. Experimental and numerical investigations of shock and shear wave propagation induced by femtosecond laser irradiation in epoxy resins

    International Nuclear Information System (INIS)

    Ecault, Romain; Touchard, Fabienne; Boustie, Michel; Berthe, Laurent; Lescoute, Emilien; Sollier, Arnaud; Voillaume, Hubert

    2015-01-01

    In this work, original shock experiments are presented. Laser-induced shock and shear wave propagations have been observed in an epoxy resin, in the case of femtosecond laser irradiation. A specific time-resolved shadowgraphy setup has been developed using the photoelasticimetry principle to enhance the shear wave observation. Shear waves have been observed in epoxy resin after laser irradiation. Their propagation has been quantified in comparison with the main shock propagation. A discussion, hinging on numerical results, is finally given to improve understanding of the phenomenon. (paper)

  7. Modified bitumen for embedding of radioactive wastes

    International Nuclear Information System (INIS)

    Bozkurt, C.

    1984-11-01

    This work describes new possibilities of using polymer modified bitumen as matrix material for embedding of low- and medium level radioactive wastes. Epoxy resins, polyurethane resins and styrene-butadiene-copolymers with 20-40 weight per cent are used as modifying agents. Penetration and softening point (ring and ball) of modified samples have been measured. Further the resistance to toluene and leaching rate in n-heptane have been determined. Within these polymer bitumen combinations investigated, the epoxy resins having a high epoxid equivalent weight with dicarbooxylic acid anhydrid hardeners and tertiary amin accelerators give the most dense network, highest thermodimensional stability and lowest leaching rate in organic solvents. 71 refs., 9 figs., 6 tabs

  8. Effect of Thermally Reduced Graphene Oxide on Mechanical Properties of Woven Carbon Fiber/Epoxy Composite

    Directory of Open Access Journals (Sweden)

    Nitai Chandra Adak

    2018-02-01

    Full Text Available Thermally reduced graphene oxide (TRGO was incorporated as a reinforcing filler in the epoxy resin to investigate the effect on the mechanical properties of carbon fiber (CF/epoxy composites. At first, the epoxy matrix was modified by adding different wt % of TRGO from 0.05 to 0.4 wt % followed by the preparation of TRGO/CF/epoxy composites througha vacuum-assisted resin transfer molding process. The prepared TRGO was characterized by using Fourier transform infrared spectroscopy, Raman Spectroscopy and field emission scanning electron microscopy (FE-SEM techniques. It was observed that the wrinkled structure of synthesized TRGO may be helpful to interlock with the epoxy resin and CF.The inter-laminar shear strength, in-plane fracture toughness and impact strength increased by ~67%, 62% and 93% at 0.2 wt % of TRGO loading in the CF/epoxy composites as compared to the CF reinforced epoxy. The mechanical properties of the hybrid composites decreased beyond the 0.2 wt % of TRGO incorporation in the epoxy resin. The fracture surfaces of the hybrid composites were studied by FE-SEM image analysis to investigate the synergistic effect of TRGO in the CF/epoxy composite. This study suggested that TRGO could be used asgood nanofiller to resist the matrix and fiber fracture.

  9. Cellulose whisker/epoxy resin nanocomposites.

    Science.gov (United States)

    Tang, Liming; Weder, Christoph

    2010-04-01

    New nanocomposites composed of cellulose nanofibers or "whiskers" and an epoxy resin were prepared. Cellulose whiskers with aspect ratios of approximately 10 and approximately 84 were isolated from cotton and sea animals called tunicates, respectively. Suspensions of these whiskers in dimethylformamide were combined with an oligomeric difunctional diglycidyl ether of bisphenol A with an epoxide equivalent weight of 185-192 and a diethyl toluenediamine-based curing agent. Thin films were produced by casting these mixtures and subsequent curing. The whisker content was systematically varied between 4 and 24% v/v. Electron microscopy studies suggest that the whiskers are evenly dispersed within the epoxy matrix. Dynamic mechanical thermoanalysis revealed that the glass transition temperature (T(g)) of the materials was not significantly influenced by the incorporation of the cellulose filler. Between room temperature and 150 degrees C, i.e., below T(g), the tensile storage moduli (E') of the nanocomposites increased modestly, for example from 1.6 GPa for the neat polymer to 4.9 and 3.6 GPa for nanocomposites comprising 16% v/v tunicate or cotton whiskers. The relative reinforcement was more significant at 185 degrees C (i.e., above T(g)), where E' was increased from approximately 16 MPa (neat polymer) to approximately 1.6 GPa (tunicate) or approximately 215 MPa (cotton). The mechanical properties of the new materials are well-described by the percolation model and are the result of the formation of a percolating whisker network in which stress transfer is facilitated by strong interactions between the whiskers.

  10. Adhesive Bonding of Aluminium Alloy A5754 by Epoxy Resins

    Directory of Open Access Journals (Sweden)

    Ivan Michalec

    2013-01-01

    Full Text Available Joining thin sheets of aluminium and its alloys is a promising area in the field of joining materials. Nowadays, joining methods that do not melt the material itself are increasingly being utilised. This paper deals with adhesive bonding of aluminium alloy A5754 by two-component epoxy resins. Theresults show that joints bonded by Hysol 9466 have appropriate mechanical properties, but that joints bonded by Hysol 9492 have better thermal stability.

  11. The Influence of Hydroxylated Carbon Nanotubes on Epoxy Resin Composites

    Directory of Open Access Journals (Sweden)

    Jiaoxia Zhang

    2012-01-01

    Full Text Available Hydroxylated multiwall carbon nanotubes (MWNTs/epoxy resin nanocomposites were prepared with ultrasonic dispersion and casting molding. The effect of hydroxylated MWNTs content on reactive activity of composites is discussed. Then the flexural and electrical properties were studied. Transmission electron microscope was employed to characterize the microstructure of nanocomposites. As a result, the reactive activity of nanocomposites obtained increases with the increasing content of MWNTs. When MWNTs content of the composites is 1 wt%, as compared to neat resin, the flexural strength increases from 143 Mpa to 156 MPa, the modulus increases from 3563 Mpa to 3691 MPa, and the volume and surface resistance of nanocomposites decrease by two orders of magnitude, respectively.

  12. The role of the epoxy resin: Curing agent ratio in composite interfacial strength by single fibre microbond test

    DEFF Research Database (Denmark)

    Minty, Ross; Thomason, James L.; Petersen, Helga Nørgaard

    2015-01-01

    This paper focuses on an investigation into the role of the epoxy resin: curing agent ratio in composite interfacial shear strength of glass fibre composites. The procedure involved changing the percentage of curing agent (Triethylenetetramine [TETA]) used in the mixture with several different...... percentages used, ranging from 4% up to 30%, including the stoichiometric ratio. It was found by using the microbond test, that there may exist a relationship between the epoxy resin to curing agent ratio and the level of adhesion between the reinforcing fibre and the polymer matrix of the composite....

  13. SEM examination and analysis of the interface character in surface modified aramid-epoxy composite

    International Nuclear Information System (INIS)

    Hussain, S.; Khan, M.B.; Hussain, R.

    2011-01-01

    The surface of Kevlar fibers is chemically modified by treatment with Phthalic anhydride (PA) and the effect is examined by SEM for the laser cut, three point bending and interlaminar shear delaminated surfaces. The surface modification improved the adhesion to epoxy resin that clearly leads to cohesive fracture as opposed to interfacial failure in the untreated specimen. SEM reveals marginal surface roughening of fibers without compromising their strength. The interface modification technique described in this paper is attractive thermodynamically as it does not compromise surface free energy of the polymer matrix or that of the fiber itself to enhance wet ability. (author)

  14. Production of the Large-area Plastic Scintillator for Beta-ray Detection using Epoxy Resin

    International Nuclear Information System (INIS)

    Nam, Jong Soo; Choi, Yong Seok; Hong, Sang Bum; Seo, Bum Kyung; Moon, Jei Kwon; Choi, Jong Won

    2016-01-01

    In this study, we prepared a plastic scintillator whose manufacturing process is simple and can be freely shaped. A thin plate of the plastic scintillator was manufactured using epoxy resin as a polymer. The plastic scintillator was made by mixing epoxy resin and organic scintillators under various conditions. The optimal mixture ratio to prepare the plastic scintillator was derived from the above results. Using the derived results, we made the large-area plastic scintillator which can quickly measure the contamination site and evaluated characteristics of the large-area plastic scintillator in the laboratory. A thin plate of a plastic scintillator with a simple preparation process can be freely shaped using epoxy resin and organic scintillators such as PPO and POPOP. PPO emits scintillation of light in the ultraviolet range, and POPOP is a wave shifter for moving the wavelength responsible for the PMT. The mixture ratio of PPO and POPOP was determined using their emission spectra. The optimal weight percentage of PPO and POPOP in an organic scintillator was determined to be 0.2 wt%:0.01 wt%. Based on the above results, the large-area plastic scintillator of the window size of a typical pancake-type αβ surface contamination counter was prepared. We want to evaluate the characteristics of the large-area plastic scintillator. However, there were the difficulties in evaluating characteristics of the large-area plastic scintillator. The cross-sectional area of the large-area plastic scintillator is significantly different to PMT

  15. Production of the Large-area Plastic Scintillator for Beta-ray Detection using Epoxy Resin

    Energy Technology Data Exchange (ETDEWEB)

    Nam, Jong Soo; Choi, Yong Seok; Hong, Sang Bum; Seo, Bum Kyung; Moon, Jei Kwon; Choi, Jong Won [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2016-10-15

    In this study, we prepared a plastic scintillator whose manufacturing process is simple and can be freely shaped. A thin plate of the plastic scintillator was manufactured using epoxy resin as a polymer. The plastic scintillator was made by mixing epoxy resin and organic scintillators under various conditions. The optimal mixture ratio to prepare the plastic scintillator was derived from the above results. Using the derived results, we made the large-area plastic scintillator which can quickly measure the contamination site and evaluated characteristics of the large-area plastic scintillator in the laboratory. A thin plate of a plastic scintillator with a simple preparation process can be freely shaped using epoxy resin and organic scintillators such as PPO and POPOP. PPO emits scintillation of light in the ultraviolet range, and POPOP is a wave shifter for moving the wavelength responsible for the PMT. The mixture ratio of PPO and POPOP was determined using their emission spectra. The optimal weight percentage of PPO and POPOP in an organic scintillator was determined to be 0.2 wt%:0.01 wt%. Based on the above results, the large-area plastic scintillator of the window size of a typical pancake-type αβ surface contamination counter was prepared. We want to evaluate the characteristics of the large-area plastic scintillator. However, there were the difficulties in evaluating characteristics of the large-area plastic scintillator. The cross-sectional area of the large-area plastic scintillator is significantly different to PMT.

  16. Gamma ray induced electrical conductivity in bisphenol-A type epoxy resin and polyethylene terephthalate

    International Nuclear Information System (INIS)

    Maeda, Hideaki; Nakakita, Tsuneo

    1978-01-01

    The insulation materials to support magnets for nuclear fusion reactors are exposed to high energy neutron beam and the gamma ray due to the accompanying induced radio activity through blankets or radiation shields. In such materials, radiation-induced conduction (RIC) is a problem, which occurs due to the charged particles generated in the insulation materials during irradiation. As one of such materials, use of epoxy composite material is expected, but its RIC has been scarcely measured. An approach to measure the wave form of transient current (or electric charge) caused by irradiating the radiation pulses of nano-second order to the materials has been developed. This paper reports the results of having measured RIC in bisphenol-A type epoxy resin at the electric field from 1 x 10 4 to 3 x 10 5 V/cm and γ dose rate from 9 x 10 3 to 9 x 10 5 R/h over the temperature range of -170 deg. C to +110 deg. C. The RIC of polyethylene terephthalate (PET) was also measured in the same regions, whose molecular structure is comparatively similar to the bisphenol-A type epoxy resin, and of which the fundamental processes for RIC have been clarified pretty well. The radiation sources of 4.3 kCi 60 Co of NAIG and 45 kCi 60 Co of JAERI were used. The experimental circuits and the cryostat are described, then as for the results, explanation and discussion are given to the characteristics of induced current, dependence on dose rate and dependence on temperature of RIC conductivity. The process of capturing carrier in deep traps seems to be dominant in the bisphenol-A type epoxy resin, similarly to that of PET. (Wakatsuki, Y.)

  17. Mobility restrictions and glass transition behaviour of an epoxy resin under confinement.

    Science.gov (United States)

    Djemour, A; Sanctuary, R; Baller, J

    2015-04-07

    Confinement can have a big influence on the dynamics of glass formers in the vicinity of the glass transition. Already 40 to 50 K above the glass transition temperature, thermal equilibration of glass formers can be strongly influenced by the confining substrate. We investigate the linear thermal expansion and the specific heat capacity cp of an epoxy resin (diglycidyl ether of bisphenol A, DGEBA) in a temperature interval of 120 K around the glass transition temperature. The epoxy resin is filled into controlled pore glasses with pore diameters between 4 and 111 nm. Since DGEBA can form H-bonds with silica surfaces, we also investigate the influence of surface silanization of the porous substrates. In untreated substrates a core/shell structure of the epoxy resin can be identified. The glass transition behaviours of the bulk phase and that of the shell phase are different. In silanized substrates, the shell phase disappears. At a temperature well above the glass transition, a second transition is found for the bulk phase - both in the linear expansion data as well as in the specific heat capacity. The cp data do not allow excluding the glass transition of a third phase as being the cause for this transition, whereas the linear expansion data do so. The additional transition temperature is interpreted as a separation between two regimes: above this temperature, macroscopic flow of the bulk phase inside the porous structure is possible to balance the mismatch of thermal expansion coefficients between DGEBA and the substrate. Below the transition temperature, this degree of freedom is hindered by geometrical constraints of the porous substrates. Moreover, this second transition could also be found in the linear expansion data of the shell phase.

  18. Enhanced lifetime characteristics in flexible polymer light-emitting devices by encapsulation of epoxy/silica-coated gold nanoparticles resin (ESGR)

    International Nuclear Information System (INIS)

    Chiu, Pin-Hsiang; Huang, Chien-Jung; Yang, Cheng-Fu; Meen, Teen-Hang; Wang, Yeong-Her

    2010-01-01

    This paper reports the effects of a new multilayer encapsulation for the lifetime of flexible PLEDs on plastic substrate. The multilayer encapsulation consisted of a novel epoxy/silica-coated gold nanoparticles resin (ESGR) as the pre-encapsulation layer and a SiO 2 layer as the encapsulation cap. The ESGR was prepared by mixing UV-curable epoxy resin and powders of silica-coated gold nanoparticles. The silica-coated gold nanoparticles is a necessity because the epoxy resin is not a good moisture barrier. The flexible PLEDs with multilayer encapsulation exhibited no dark spots after being stored for over 300 h at 25 deg. C and 60% relative humidity. Also, the operational half-luminance decay time of device was 1360 h, seven times longer than that of a device without encapsulation. These results confirmed that the multilayer encapsulation, which restricted the moisture that penetrated into the devices, could be applied to the encapsulation of flexible PLEDs.

  19. Study by dynamic light scattering of an o/w emulsion of an epoxi resin dispersed in water by means of a triblock copolymer of type PEO-PPO-PEO

    International Nuclear Information System (INIS)

    Uscanga, E. H.; Rio, J. M. del; Avendano-Gomez, J. R.

    2009-01-01

    The curing epoxy resins are widely used in various fields of chemical industry, such as adhesives, automotive, coatings, etc. The process operation consisting of flow and mixing of epoxy resins become difficult due to their high viscosity. One solution is to dissolve the epoxy resin in volatile organic solvents (VOS) such as toluene, xylene or benzene. However, the use of VOS is not only expensive but harmful to the environment. (Author)

  20. Development of epoxy resin-type neutron shielding materials (I)

    Energy Technology Data Exchange (ETDEWEB)

    Cho, Soo Haeng; Kim, Ik Soo; Shin, Young Joon; Do, Jae Bum; Ro, Seung Gy

    1997-12-01

    Because the exposure to radiation in the nuclear facilities can be fatal to human, it is important to reduce the radiation dose level to a tolerable level. The purpose of this study is to develop highly effective neutron shielding materials for the shipping and storage cask of radioactive materials or in the nuclear /radiation facilities. On this study, we developed epoxy resin based neutron shielding materials and their various materials properties, including neutron shielding ability, fire resistance, combustion characteristics, radiation resistance, thermal and mechanical properties were evaluated experimentally. (author). 31 refs., 22 tabs., 17 figs.

  1. Near-Infrared Spectroscopic Method for Monitoring Water Content in Epoxy Resins and Fiber-Reinforced Composites

    Directory of Open Access Journals (Sweden)

    Andrey E. Krauklis

    2018-04-01

    Full Text Available Monitoring water content and predicting the water-induced drop in strength of fiber-reinforced composites are of great importance for the oil and gas and marine industries. Fourier transform infrared (FTIR spectroscopic methods are broadly available and often used for process and quality control in industrial applications. A benefit of using such spectroscopic methods over the conventional gravimetric analysis is the possibility to deduce the mass of an absolutely dry material and subsequently the true water content, which is an important indicator of water content-dependent properties. The objective of this study is to develop an efficient and detailed method for estimating the water content in epoxy resins and fiber-reinforced composites. In this study, Fourier transform near-infrared (FT-NIR spectroscopy was applied to measure the water content of amine-epoxy neat resin. The method was developed and successfully extended to glass fiber-reinforced composite materials. Based on extensive measurements of neat resin and composite samples of varying water content and thickness, regression was performed, and the quantitative absorbance dependence on water content in the material was established. The mass of an absolutely dry resin was identified, and the true water content was obtained. The method was related to the Beer–Lambert law and explained in such terms. A detailed spectroscopic method for measuring water content in resins and fiber-reinforced composites was developed and described.

  2. Near-Infrared Spectroscopic Method for Monitoring Water Content in Epoxy Resins and Fiber-Reinforced Composites.

    Science.gov (United States)

    Krauklis, Andrey E; Gagani, Abedin I; Echtermeyer, Andreas T

    2018-04-11

    Monitoring water content and predicting the water-induced drop in strength of fiber-reinforced composites are of great importance for the oil and gas and marine industries. Fourier transform infrared (FTIR) spectroscopic methods are broadly available and often used for process and quality control in industrial applications. A benefit of using such spectroscopic methods over the conventional gravimetric analysis is the possibility to deduce the mass of an absolutely dry material and subsequently the true water content, which is an important indicator of water content-dependent properties. The objective of this study is to develop an efficient and detailed method for estimating the water content in epoxy resins and fiber-reinforced composites. In this study, Fourier transform near-infrared (FT-NIR) spectroscopy was applied to measure the water content of amine-epoxy neat resin. The method was developed and successfully extended to glass fiber-reinforced composite materials. Based on extensive measurements of neat resin and composite samples of varying water content and thickness, regression was performed, and the quantitative absorbance dependence on water content in the material was established. The mass of an absolutely dry resin was identified, and the true water content was obtained. The method was related to the Beer-Lambert law and explained in such terms. A detailed spectroscopic method for measuring water content in resins and fiber-reinforced composites was developed and described.

  3. Comparison of the Amount of Fluoride Release from Nanofilled Resin Modified Glass Ionomer Conventional and Resin Modified Glass Ionomer Cements

    Directory of Open Access Journals (Sweden)

    Sumitha Upadhyay

    2013-01-01

    Full Text Available Objective: To investigate and compare the amount of fluoride release of conventional, resin modified and nanofilled resin modified glass ionomer cements.Materials and Methods: Tablets of glass-ionomer cements were immersed in deionized water and incubated at 37◦C. After 1, 2, 7, 15 and 30 days, fluoride ion was measured under normal atmospheric conditions by fluoride ion selective electrode. Buffer (TISAB II was used to decomplex the fluoride ion and to provide a constant background ionic strength and to maintain the pH of water between 5.0 and 5.5 as the fluoride electrode is sensitive to changes in pH. Statistical evaluation was carried out by one way ANOVA (Analysis of Variance using SPSS 11.0. The significance level was set at p< 0.05.Results: The release of fluoride was highest on day 1 and there was a sudden fall on day 2 in all three groups. Initially fluoride release from conven-tional glass-ionomer cement was highest compared to the other two glass-ionomer cements, but the amount drastically reduced over the period. Although the amount of fluoride release was less than both the resin modified and nanofilled resin modified glass-ionomer cement, the release was sustained consistently for 30 daysConclusion: The cumulative fluoride release of nanofilled resin modified glass ionomer cement was very less compared to the conventional and resin modified glass ionomer cements and Nanofilled resin modified glass ionomer cement released less but steady fluoride as compared to other resin modified glass ionomer cements.

  4. Synthesis, Characterization and Curing Studies of Thermosetting Epoxy Resin with Amines

    International Nuclear Information System (INIS)

    Lakshmi, B.; Mahendra, K. N.; Shivananda, K. N.

    2010-01-01

    A new hybrid thermosetting maleimido epoxy compound 4-(N-maleimidophenyl) glycidylether (N-MPGE) is prepared by reacting N-(4-hydroxyphenyl) maleimide (HPM) with Epichlorohydrin by using benzyltrimethylammonium chloride as a catalyst. The resulting compound possesses both the oxirane ring and maleimide group. The curing reaction of these maleimidophenyl glycidylether epoxy compound (N-MPGE) with amines as curing agents such as ethylendiamine (EDA), diethylentriamine (DETA) and triethylenetetramine (TETA), aminoethylpiperazine (AEP) and isophoronediamine, IPDA), are studied. Incorporation of maleimide groups in the epichlorohydrin provides cyclic imide structure and high cross-linking density to the cured resins. The cured samples exhibited good thermal stability, excellent chemical (acid/alkali/solvent) and water absorption resistance. Morphological studies by the SEM technique further confirmed the phase homogeneity net work of the cured systems

  5. Synthesis, Characterization and Curing Studies of Thermosetting Epoxy Resin with Amines

    Energy Technology Data Exchange (ETDEWEB)

    Lakshmi, B.; Mahendra, K. N. [Bangalore University, Bangalore (India); Shivananda, K. N. [Technion - Israel Institute of Technology, Haifa (Israel)

    2010-08-15

    A new hybrid thermosetting maleimido epoxy compound 4-(N-maleimidophenyl) glycidylether (N-MPGE) is prepared by reacting N-(4-hydroxyphenyl) maleimide (HPM) with Epichlorohydrin by using benzyltrimethylammonium chloride as a catalyst. The resulting compound possesses both the oxirane ring and maleimide group. The curing reaction of these maleimidophenyl glycidylether epoxy compound (N-MPGE) with amines as curing agents such as ethylendiamine (EDA), diethylentriamine (DETA) and triethylenetetramine (TETA), aminoethylpiperazine (AEP) and isophoronediamine, IPDA), are studied. Incorporation of maleimide groups in the epichlorohydrin provides cyclic imide structure and high cross-linking density to the cured resins. The cured samples exhibited good thermal stability, excellent chemical (acid/alkali/solvent) and water absorption resistance. Morphological studies by the SEM technique further confirmed the phase homogeneity net work of the cured systems.

  6. Accelerated thermal aging of rubber modified epoxy encapsulants

    International Nuclear Information System (INIS)

    Sayre, J.A.

    1979-01-01

    A program is outlined to enable prediction of physical properties of rubber modified epoxy encapsulants over the life time of the extended life neutron generators. Preliminary results show that the chief aging phenomenon occurring is increased crosslink density of the epoxy matrix. No changes in the rubber phase have been detected. The effect of increased epoxy crosslink density has been higher volume resistivity at 66 0 C, increased tensile strength, and decreased ultimate elongation

  7. Radiation processing of carbon fiber-acrylated epoxy composites

    International Nuclear Information System (INIS)

    Singh, A.; Saunders, C.B.

    1992-01-01

    Advanced composites, specifically carbon fiber reinforced epoxies, are being used for a variety of demanding structural applications, primarily because of their high strength-to-weight and stiffness-to-weight ratios, corrosion resistance, and damage tolerance characteristics. For these composites the key advantages of using electron beam (EB), rather than thermal curing, are curing at ambient temperature, reduced curing times for individual components, improved resin stability, fewer volatiles, and better control of the profile of energy absorption. Epoxy compounds do, however, have to be modified to make them EB curable. The electron beam penetration limit, a function of beam energy, product density, and the thickness of any container required, must also be examined when considering EB processing. Research is being conducted to develop EB-curable carbon fiber-acrylated epoxy composites. The tensile properties of these laminates are comparable to those of thermally cured epoxy laminates. Research is continuing to develop suitable resin formulations and coupling agents to optimize the mechanical properties of EB-cured carbon fiber laminates. In this chapter the EB curing of epoxies, processing considerations, and typical properties of EB-cured carbon fiber-acrylated epoxy laminates are discussed. (orig.)

  8. Role of Interphase in the Mechanical Behavior of Silica/Epoxy Resin Nanocomposites

    Directory of Open Access Journals (Sweden)

    Yi Hua

    2015-06-01

    Full Text Available A nanoscale representative volume element has been developed to investigate the effect of interphase geometry and property on the mechanical behavior of silica/epoxy resin nanocomposites. The role of interphase–matrix bonding was also examined. Results suggested that interphase modulus and interfacial bonding conditions had significant influence on the effective stiffness of nanocomposites, while its sensitivities with respect to both the thickness and the gradient property of the interphase was minimal. The stiffer interphase demonstrated a higher load-sharing capacity, which also increased the stress distribution uniformity within the resin nanocomposites. Under the condition of imperfect interfacial bonding, the effective stiffness of nanocomposites was much lower, which was in good agreement with the documented experimental observations. This work could shed some light on the design and manufacturing of resin nanocomposites.

  9. Epoxy-based carbon nanotubes reinforced composites

    CSIR Research Space (South Africa)

    Kesavan Pillai, Sreejarani

    2011-04-01

    Full Text Available of the three major epoxy resin producers worldwide [May, 1987]. Epoxy resin is most commonly used as a matrix for advanced composites due to their superior thermal, mechanical and electrical properties; dimensional stability and chemical resistance. Epoxy... are electrical insulators, and the widespread use of the epoxy resins for many high-performance applications is constrained because of their inherent brittleness, delamination and fracture toughness limitations. There were quite a few approaches to enhance...

  10. Distribution and avoidance of debris on epoxy resin during UV ns-laser scanning processes

    Science.gov (United States)

    Veltrup, Markus; Lukasczyk, Thomas; Ihde, Jörg; Mayer, Bernd

    2018-05-01

    In this paper the distribution of debris generated by a nanosecond UV laser (248 nm) on epoxy resin and the prevention of the corresponding re-deposition effects by parameter selection for a ns-laser scanning process were investigated. In order to understand the mechanisms behind the debris generation, in-situ particle measurements were performed during laser treatment. These measurements enabled the determination of the ablation threshold of the epoxy resin as well as the particle density and size distribution in relation to the applied laser parameters. The experiments showed that it is possible to reduce debris on the surface with an adapted selection of pulse overlap with respect to laser fluence. A theoretical model for the parameter selection was developed and tested. Based on this model, the correct choice of laser parameters with reduced laser fluence resulted in a surface without any re-deposited micro-particles.

  11. Effect of titania particles on the microstructure and properties of the epoxy resin coatings on sintered NdFeB permanent magnets

    International Nuclear Information System (INIS)

    Xu, J.L.; Huang, Z.X.; Luo, J.M.; Zhong, Z.C.

    2014-01-01

    The nanometer titania particles enhanced epoxy resin composite coatings were prepared on the sintered NdFeB permanent magnets by cathodic electrophoretic deposition. The effects of titania particle concentrations on the microstructure and properties of the epoxy coatings were investigated by surface and cross-sectional morphologies observation, surface roughness and microhardness measurement, H 2 SO 4 solution immersion test, neutral salt spray test and magnetic properties measurement. The results showed that the thickness of epoxy coatings with and without the titania particles addition was about 40 μm. The titania particles could be uniformly dispersed and embedded in the epoxy matrix if the titania particles concentration was lower than 40 g/l. With increasing titania particle concentrations, the number of the particles embedded in the epoxy matrix increased and the surface roughness and microhardness of the composite coatings increased. At the same time, the weight loss of the coated samples immersed in H 2 SO 4 solution decreased and the neutral salt spray time of the coated samples prolonged. It could be concluded that the titania particles did not change the thickness of the epoxy coatings and did not deteriorate the magnetic properties of NdFeB substrates, but could greatly improve the microhardness and corrosion resistance of the epoxy coatings. - Highlights: • The titania particles enhanced epoxy resin coatings were prepared on sintered NdFeB by cathodic electrophoretic deposition. • The titania particles could be uniformly dispersed and embedded in the epoxy resin matrix. • With increasing titania concentrations, the surface roughness and the microhardness of composite coatings increased. • The addition of titania particles greatly improved the corrosion resistance of the epoxy coatings. • The composition coatings did not deteriorate the magnetic properties of NdFeB substrates

  12. Effect of titania particles on the microstructure and properties of the epoxy resin coatings on sintered NdFeB permanent magnets

    Energy Technology Data Exchange (ETDEWEB)

    Xu, J.L., E-mail: jlxu@nchu.edu.cn; Huang, Z.X.; Luo, J.M.; Zhong, Z.C., E-mail: zzhong.2006@yahoo.com.cn

    2014-04-15

    The nanometer titania particles enhanced epoxy resin composite coatings were prepared on the sintered NdFeB permanent magnets by cathodic electrophoretic deposition. The effects of titania particle concentrations on the microstructure and properties of the epoxy coatings were investigated by surface and cross-sectional morphologies observation, surface roughness and microhardness measurement, H{sub 2}SO{sub 4} solution immersion test, neutral salt spray test and magnetic properties measurement. The results showed that the thickness of epoxy coatings with and without the titania particles addition was about 40 μm. The titania particles could be uniformly dispersed and embedded in the epoxy matrix if the titania particles concentration was lower than 40 g/l. With increasing titania particle concentrations, the number of the particles embedded in the epoxy matrix increased and the surface roughness and microhardness of the composite coatings increased. At the same time, the weight loss of the coated samples immersed in H{sub 2}SO{sub 4} solution decreased and the neutral salt spray time of the coated samples prolonged. It could be concluded that the titania particles did not change the thickness of the epoxy coatings and did not deteriorate the magnetic properties of NdFeB substrates, but could greatly improve the microhardness and corrosion resistance of the epoxy coatings. - Highlights: • The titania particles enhanced epoxy resin coatings were prepared on sintered NdFeB by cathodic electrophoretic deposition. • The titania particles could be uniformly dispersed and embedded in the epoxy resin matrix. • With increasing titania concentrations, the surface roughness and the microhardness of composite coatings increased. • The addition of titania particles greatly improved the corrosion resistance of the epoxy coatings. • The composition coatings did not deteriorate the magnetic properties of NdFeB substrates.

  13. Microwave and thermal curing of an epoxy resin for microelectronic applications

    Energy Technology Data Exchange (ETDEWEB)

    Johnston, K. [Institute of Chemical Sciences, School of Engineering and Physical Sciences, Heriot-Watt University, Edinburgh EH14 4AS (United Kingdom); Pavuluri, S.K.; Leonard, M.T.; Desmulliez, M.P.Y. [MIcroSystems Engineering Centre (MISEC), Institute of Signals, Sensors and Systems, School of Engineering and Physical Sciences, Heriot-Watt University, Edinburgh EH14 4AS (United Kingdom); Arrighi, V., E-mail: v.arrighi@hw.ac.uk [Institute of Chemical Sciences, School of Engineering and Physical Sciences, Heriot-Watt University, Edinburgh EH14 4AS (United Kingdom)

    2015-09-20

    Graphical abstract: - Highlights: • Thermal and microwave curing of a commercial epoxy resin EO1080 are compared. • Microwave curing increases cure rate and does not adversely affect properties. • The curing of EO1080 is generally autocatalytic but deviates at high conversion. • Microwave radiation has a more complex effect on curing kinetics. - Abstract: Microwave curing of thermosetting polymers has a number of advantages to natural or thermal oven curing and is considered a cost-effective alternative. Here we present a detailed study of a commercially available epoxy resin, EO1080. Samples that are thermally cured are compared to curing using a recently developed modular microwave processing system. For commercial purposes it is crucial to demonstrate that microwave curing does not adversely affect the thermal and chemical properties of the material. Therefore, the kinetics of cure and various post cure properties of the resin are investigated. Attenuated Total Reflectance Fourier-Transform Infrared (ATR-FTIR) analysis shows no significant difference between the conventionally and microwave cured samples. Differential scanning calorimetry (DSC) is used to monitor the kinetics of the curing reaction, as well as determine the thermal and ageing properties of the material. As expected, the rate of curing is higher when using microwave energy and we attempt to quantify differences compared to conventional thermal curing. No change in glass transition temperature (T{sub g}) is observed. For the first time, enthalpy relaxation measurements performed on conventional and microwave cured samples are reported and these indicate similar ageing properties at any given temperature under T{sub g}.

  14. Microwave and thermal curing of an epoxy resin for microelectronic applications

    International Nuclear Information System (INIS)

    Johnston, K.; Pavuluri, S.K.; Leonard, M.T.; Desmulliez, M.P.Y.; Arrighi, V.

    2015-01-01

    Graphical abstract: - Highlights: • Thermal and microwave curing of a commercial epoxy resin EO1080 are compared. • Microwave curing increases cure rate and does not adversely affect properties. • The curing of EO1080 is generally autocatalytic but deviates at high conversion. • Microwave radiation has a more complex effect on curing kinetics. - Abstract: Microwave curing of thermosetting polymers has a number of advantages to natural or thermal oven curing and is considered a cost-effective alternative. Here we present a detailed study of a commercially available epoxy resin, EO1080. Samples that are thermally cured are compared to curing using a recently developed modular microwave processing system. For commercial purposes it is crucial to demonstrate that microwave curing does not adversely affect the thermal and chemical properties of the material. Therefore, the kinetics of cure and various post cure properties of the resin are investigated. Attenuated Total Reflectance Fourier-Transform Infrared (ATR-FTIR) analysis shows no significant difference between the conventionally and microwave cured samples. Differential scanning calorimetry (DSC) is used to monitor the kinetics of the curing reaction, as well as determine the thermal and ageing properties of the material. As expected, the rate of curing is higher when using microwave energy and we attempt to quantify differences compared to conventional thermal curing. No change in glass transition temperature (T g ) is observed. For the first time, enthalpy relaxation measurements performed on conventional and microwave cured samples are reported and these indicate similar ageing properties at any given temperature under T g

  15. Transient and steady-state currents in epoxy resin

    International Nuclear Information System (INIS)

    Guillermin, Christophe; Rain, Pascal; Rowe, Stephen W

    2006-01-01

    Charging and discharging currents have been measured in a diglycidyl ether of bisphenol-A epoxy resin with and without silica fillers, below and above its glass transition temperature T g = 65 deg. C. Both transient and steady-state current densities have been analysed. The average applied fields ranged from 3 to 35 kV mm -1 with a sample thickness of 0.5 mm. Above T g , transient currents suggested a phenomenon of charge injection forming trapped space charges even at low fields. Steady-state currents confirmed that the behaviour was not Ohmic and suggested Schottky-type injection. Below T g , the current is not controlled by the metal-dielectric interface but by the conduction in the volume: the current is Ohmic at low fields and both transient and steady-state currents suggest a phenomenon of space-charge limited currents at high fields. The field threshold is similar in the filler-free and the filled resin. Values in the range 12-17 kV mm -1 have been measured

  16. Transient and steady-state currents in epoxy resin

    Energy Technology Data Exchange (ETDEWEB)

    Guillermin, Christophe [Schneider Electric Industries S.A.S., 37 quai Paul-Louis Merlin, 38050 Grenoble Cedex 9 (France); Rain, Pascal [Laboratoire d' Electrostatique et de Materiaux Dielectriques (LEMD), CNRS, 25 avenue des Martyrs, 38042 Grenoble Cedex 9 (France); Rowe, Stephen W [Schneider Electric Industries S.A.S., 37 quai Paul-Louis Merlin, 38050 Grenoble Cedex 9 (France)

    2006-02-07

    Charging and discharging currents have been measured in a diglycidyl ether of bisphenol-A epoxy resin with and without silica fillers, below and above its glass transition temperature T{sub g} = 65 deg. C. Both transient and steady-state current densities have been analysed. The average applied fields ranged from 3 to 35 kV mm{sup -1} with a sample thickness of 0.5 mm. Above T{sub g}, transient currents suggested a phenomenon of charge injection forming trapped space charges even at low fields. Steady-state currents confirmed that the behaviour was not Ohmic and suggested Schottky-type injection. Below T{sub g}, the current is not controlled by the metal-dielectric interface but by the conduction in the volume: the current is Ohmic at low fields and both transient and steady-state currents suggest a phenomenon of space-charge limited currents at high fields. The field threshold is similar in the filler-free and the filled resin. Values in the range 12-17 kV mm{sup -1} have been measured.

  17. Characterization, optical properties and laser ablation behavior of epoxy resin coatings reinforced with high reflectivity ceramic particles

    Science.gov (United States)

    Li, Wenzhi; Kong, Jing; Wu, Taotao; Gao, Lihong; Ma, Zhuang; Liu, Yanbo; Wang, Fuchi; Wei, Chenghua; Wang, Lijun

    2018-04-01

    Thermal damage induced by high power energy, especially high power laser, significantly affects the lifetime and performance of equipment. High-reflectance coating/film has attracted considerable attention due to its good performance in the damage protection. Preparing a high-reflectance coating with high reaction endothermal enthalpy will effectively consume a large amount of incident energy and in turn protect the substrate from thermal damage. In this study, a low temperature process was used to prepare coatings onto substrate with complex shape and avoid thermal effect during molding. An advanced high reflection ceramic powder, La1‑xSrxTiO3+δ , was added in the epoxy adhesive matrix to improve the reflectivity of coating. The optical properties and laser ablation behaviors of coatings with different ceramic additive ratio of La1‑xSrxTiO3+δ and modified epoxy-La1‑xSrxTiO3+δ with ammonium polyphosphate coatings were investigated, respectively. We found that the reflectivity of coatings is extremely high due to mixed high-reflection La1‑xSrxTiO3+δ particles, up to 96% at 1070 nm, which can significantly improve the laser resistance. In addition, the ammonium polyphosphate modifies the residual carbon structure of epoxy resin from discontinuous fine particles structure to continuous and porous structure, which greatly enhances the thermal-insulation property of coating. Furthermore, the laser ablation threshold is improved obviously, which is from 800 W cm‑2 to 1000 W cm‑2.

  18. The epoxy resin variation effect on microstructure and physical properties to improve bonded NdFeB flux magnetic density

    International Nuclear Information System (INIS)

    Rusnaeni, N.; Sarjono, Priyo; Muljadi; Noer, Nasrudin

    2016-01-01

    NdFeB magnets have been fabricated from a mixture of powder NdFeB (MPQ-B+) and epoxy resins (ER) with a variation of 0% wt, 2% wt, 4% wt and 6% wt. The pellets samples were made by pressing 4 tons of the mixture powder at room temperature before curing at 100°C for 1 hour. The SEM-EDX results showed the microstructure with ER were evenly smeared the NdFeB magnetic particles due to higher percent C and lower transition metals value. Sample with 2% wt epoxy resin was able to achieve the highest density of 5.35 g/cm 3 and the highest magnetic flux of 2121 Gauss. The magnetic properties characterization using the permagraph indicates that the sample pellets with 2% wt epoxy resin has a value of remanence (Br) = 4.92 kG, coercivity (Hc) = 7.76 kOe, and energy product (Bhmax) = 4.58 MGOe. Despite low remanence value in the pellet samples, the resistance to demagnetization value was still acceptable. (paper)

  19. The epoxy resin variation effect on microstructure and physical properties to improve bonded NdFeB flux magnetic density

    Science.gov (United States)

    Rusnaeni, N.; Sarjono, Priyo; Muljadi; Noer, Nasrudin

    2016-11-01

    NdFeB magnets have been fabricated from a mixture of powder NdFeB (MPQ-B+) and epoxy resins (ER) with a variation of 0% wt, 2% wt, 4% wt and 6% wt. The pellets samples were made by pressing 4 tons of the mixture powder at room temperature before curing at 100°C for 1 hour. The SEM-EDX results showed the microstructure with ER were evenly smeared the NdFeB magnetic particles due to higher percent C and lower transition metals value. Sample with 2% wt epoxy resin was able to achieve the highest density of 5.35 g/cm3 and the highest magnetic flux of 2121 Gauss. The magnetic properties characterization using the permagraph indicates that the sample pellets with 2% wt epoxy resin has a value of remanence (Br) = 4.92 kG, coercivity (Hc) = 7.76 kOe, and energy product (Bhmax) = 4.58 MGOe. Despite low remanence value in the pellet samples, the resistance to demagnetization value was still acceptable.

  20. Experimental Study on the Characteristics of Polymer Concrete With Epoxy Resin

    Directory of Open Access Journals (Sweden)

    Maria Harja Ioniţă

    2008-01-01

    Full Text Available In the paper are presented the results of some experimental researches concerning polymer mortars and concretes realized of epoxy resin, silica fume and crushed aggregates. The mechanical characteristics of hardened concrete were determined. The silica fume content varied between 6.5% and 30% to polymer mortar and 6.4% and 9.6% to polymer concrete. The obtained results show maximum characteristics for a dosage of 24% resin and maximum dosage of silica fume to the polymer mortar, and for the polymer concrete the mechanical characteristics are influenced by all mixture factors: the compressive strength increases with the increase of silica fume dosage, and the flexure strength and split strength increase with the decreasing of silica fume dosage.

  1. Changes in mass loss and chemistry of AG-80 epoxy resin after 160 keV proton irradiations

    Energy Technology Data Exchange (ETDEWEB)

    Gao Yu [Space Materials and Environment Engineering Lab, Harbin Institute of Technology, Harbin, 150001 (China)]. E-mail: czq04@yahoo.com.cn; Sun Mingren [College of Materials Science and Engineering, Harbin Institute of Technology, Harbin, 150001 (China); Yang Dezhuang [Space Materials and Environment Engineering Lab, Harbin Institute of Technology, Harbin, 150001 (China); He Shiyu [Space Materials and Environment Engineering Lab, Harbin Institute of Technology, Harbin, 150001 (China); Wang Jinhe [Precision Engineering Research Institute, Harbin Institute of Technology, Harbin, 150001 (China); Xiao Jingdong [Space Materials and Environment Engineering Lab, Harbin Institute of Technology, Harbin, 150001 (China); Li Zhijun [39th Institute, China Electronic Science and Technology Groups Inc., Xi-an 710065 (China)

    2005-06-01

    The AG-80 resin is a new type of thermosetting matrix for advanced carbon/epoxy composites. Mass loss effect and the related outgassing are major concerns for its application in space. The changes in mass loss, outgassing and chemical structure under 160 keV proton exposure were investigated for the AG-80 epoxy resin. The variation in chemistry was characterized by X-ray photoelectron spectroscopy. Experimental results show that with increasing the proton fluence, the surface colour of specimens is getting darker. Mass loss ratios ascend remarkably until the fluence of approximately 5.5 x 10{sup 15} cm{sup -2}, and then tend to leveling off. The surface roughness of specimens exhibits an increasing trend followed by decreasing as a function of proton fluence. Under the exposure, the C-C, C-H, C-N and C-O bonds are broken, a variety of molecule ions with smaller molecule weight are formed, and carbon is enriched in the surface layer of specimens. The changes in mass loss and surface roughness of the AG-80 epoxy resin could be attributed to the formation of the molecule ions and the enrichment of carbon content in the surface layer due to proton radiation.

  2. Multi-wall carbon nanotubes/epoxy resin composites characterization of the starting materials and evaluation of thermal and electrical conductivity

    International Nuclear Information System (INIS)

    Silva, Wellington Marcos da

    2009-01-01

    In this study we investigate the electrical and thermal properties of I) composite materials fabricated with O, I, 0,5 and I wt% of concentric multi-wall carbon nanotubes/epoxy resin (MWNT) dispersed randomly in the resin; 2) MWNT buckypaper/resin composite materials; 3) and neat MWNT buckypaper. Initially, we use the techniques of thermogravimetry, infrared spectroscopy, nuclear magnetic resonance, energy dispersive spectroscopy, x-ray fluorescence, scanning and transmission electron microscopy for a broadening characterization of the starting materials, to evaluate its morphology, purity, chemical composition and structure, in order to optimize the properties of crosslinked resin and, consequently, of the composite systems. Important parameters such as the average molecular mass and the equivalent weight of epoxy resin (DGEBA) were determined by 1 H-NMR analysis and, after that, resin/curing agent relations with Phr 10, 15, 20 and 53,2 were elaborated and investigated by thermogravimetry, the resin/curing agent relation with Phr 10 showed to be the most thermally stable. This stoichiometric relation was used to elaborate the composites. We have evaluated that the effect of adding 10 wt% of the solvent acetone to the epoxy resin preparation does not alter its properties so we have adopted two routes to fabricate the composites. In the first route we used 10 wt% of acetone and, in the second the MWNT were dispersed in the matrix without using the solvent. However, no significant difference was observed for the dispersion of the bundle tubes in both systems. The electrical conductivity of the composites and buckypapers was evaluated by impedance spectroscopy and the thermal conductivity by the flash laser flash method. Only the buckypapers presented high values for electrical conductivity (10 3 S.m -1 ). The composite systems presented values of 10 -3 S.m -1 , only a bit different from the value of the crosslinked resin. For thermal conductivity, the values for the

  3. Epoxy-silicate nanocomposites: Cure monitoring and characterization

    International Nuclear Information System (INIS)

    Hussain, Farzana; Chen, Jihua; Hojjati, Mehdi

    2007-01-01

    Epoxy-clay nanocomposites were prepared with organically modified layered clay with varying clay contents (1-8 wt.%). Neat resin and nanocomposite were characterized using different techniques. At first, the effect of nanoclay concentration on the cure behaviour was investigated using an on-line dielectric cure monitoring technique. Differential scanning calorimetry (DSC) was used to verify the dielectric measurement results. Furthermore, mechanical and thermal properties were studied using tensile test and Dynamic Mechanical Analysis (DMA), respectively. Experimental results showed that properties of the epoxy were changed evidently because of the nanoclay loading. The tensile modulus of the nanocomposites increased by 47%, however, no improvement in tensile strength and glass transition temperature (T g ) was observed. Fracture surface of the tensile samples were analyzed by Scanning Electron Microscope (SEM). The nanocomposites structures were characterized with Wide Angle X-Ray Diffraction (WAXD) and Transmission Electron Microscopy (TEM), which revealed the intercalated morphology of clay layers in the epoxy resin systems

  4. Properties of halloysite nanotube-epoxy resin hybrids and the interfacial reactions in the systems

    Energy Technology Data Exchange (ETDEWEB)

    Liu Mingxian; Guo Baochun; Du Mingliang; Cai Xiaojia; Jia Demin [Department of Polymer Materials and Engineering, South China University of Technology, Guangzhou 510640 (China)

    2007-11-14

    A naturally occurred microtubullar silicate, halloysite nanotubes (HNTs), was co-cured with epoxy/cyanate ester resin to form organic-inorganic hybrids. The coefficient of thermal expansion (CTE) of the hybrids with low HNT concentration was found to be substantially lower than that of the plain cured resin. The moduli of the hybrids in the glassy state and rubbery state were significantly higher than those for the plain cured resin. The dispersion of HNTs in the resin matrix was very uniform as revealed by the transmission electron microscopy (TEM) results. The interfacial reactions between the HNTs and cyanate ester (CE) were revealed by the results of Fourier transform infrared spectroscopy (FTIR) and x-ray photoelectron spectroscopy (XPS). The substantially increased properties of the hybrids were attributed to the covalent bonding between the nanotubes and the matrix.

  5. Properties of halloysite nanotube-epoxy resin hybrids and the interfacial reactions in the systems

    International Nuclear Information System (INIS)

    Liu Mingxian; Guo Baochun; Du Mingliang; Cai Xiaojia; Jia Demin

    2007-01-01

    A naturally occurred microtubullar silicate, halloysite nanotubes (HNTs), was co-cured with epoxy/cyanate ester resin to form organic-inorganic hybrids. The coefficient of thermal expansion (CTE) of the hybrids with low HNT concentration was found to be substantially lower than that of the plain cured resin. The moduli of the hybrids in the glassy state and rubbery state were significantly higher than those for the plain cured resin. The dispersion of HNTs in the resin matrix was very uniform as revealed by the transmission electron microscopy (TEM) results. The interfacial reactions between the HNTs and cyanate ester (CE) were revealed by the results of Fourier transform infrared spectroscopy (FTIR) and x-ray photoelectron spectroscopy (XPS). The substantially increased properties of the hybrids were attributed to the covalent bonding between the nanotubes and the matrix

  6. Cure Kinetics of Benzoxazine/Cycloaliphatic Epoxy Resin by Differential Scanning Calorimetry

    Science.gov (United States)

    Gouni, Sreeja Reddy

    Understanding the curing kinetics of a thermoset resin has a significant importance in developing and optimizing curing cycles in various industrial manufacturing processes. This can assist in improving the quality of final product and minimizing the manufacturing-associated costs. One approach towards developing such an understanding is to formulate kinetic models that can be used to optimize curing time and temperature to reach a full cure state or to determine time to apply pressure in an autoclave process. Various phenomenological reaction models have been used in the literature to successfully predict the kinetic behavior of a thermoset system. The current research work was designed to investigate the cure kinetics of Bisphenol-A based Benzoxazine (BZ-a) and Cycloaliphatic epoxy resin (CER) system under isothermal and nonisothermal conditions by Differential Scanning Calorimetry (DSC). The cure characteristics of BZ-a/CER copolymer systems with 75/25 wt% and 50/50 wt% have been studied and compared to that of pure benzoxazine under nonisothermal conditions. The DSC thermograms exhibited by these BZ-a/CER copolymer systems showed a single exothermic peak, indicating that the reactions between benzoxazine-benzoxazine monomers and benzoxazine-cycloaliphatic epoxy resin were interactive and occurred simultaneously. The Kissinger method and isoconversional methods including Ozawa-Flynn-Wall and Freidman were employed to obtain the activation energy values and determine the nature of the reaction. The cure behavior and the kinetic parameters were determined by adopting a single step autocatalytic model based on Kamal and Sourour phenomenological reaction model. The model was found to suitably describe the cure kinetics of copolymer system prior to the diffusion-control reaction. Analyzing and understanding the thermoset resin system under isothermal conditions is also important since it is the most common practice in the industry. The BZ-a/CER copolymer system with

  7. Carboxyl-terminated butadiene-acrylonitrile-toughened epoxy/carboxyl-modified carbon nanotube nanocomposites: Thermal and mechanical properties

    Directory of Open Access Journals (Sweden)

    H. F. Xie

    2012-09-01

    Full Text Available Carboxyl-modified multi-walled carbon nanotubes (MWCNT–COOHs as nanofillers were incorporated into diglycidyl ether of bisphenol A (DGEBA toughened with carboxyl-terminated butadiene-acrylonitrile (CTBN. The carboxyl functional carbon nanotubes were characterized by Fourier-transform infrared spectroscopy and thermogravimetric analysis. Furthermore, cure kinetics, glass transition temperature (Tg, mechanical properties, thermal stability and morphology of DGEBA/CTBN/MWCNT–COOHs nanocomposites were investigated by differential scanning calorimetry (DSC, dynamic mechanical analysis (DMA, universal test machine, thermogravimetric analysis and scanning electron microscopy (SEM. DSC kinetic studies showed that the addition of MWCNT–COOHs accelerated the curing reaction of the rubber-toughened epoxy resin. DMA results revealed that Tg of rubber-toughened epoxy nanocomposites lowered with MWCNT–COOH contents. The tensile strength, elongation at break, flexural strength and flexural modulus of DGEBA/CTBN/MWCNT-COOHs nanocomposites were increased at lower MWCNT-COOH concentration. A homogenous dispersion of nanocomposites at lower MWCNT–COOH concentration was observed by SEM.

  8. Studies on the structural changes during curing of epoxy and its blend with CTBN

    Science.gov (United States)

    Srivastava, Kavita; Rathore, Ashwani Kumar; Srivastava, Deepak

    2018-01-01

    Cashew nut shell liquid (CNSL), an agricultural renewable resource material, produces natural phenolic distillates such as cardanol. Cardanol condenses with formaldehyde at the ortho- and para-position of the phenolic ring under acidic or alkaline condition to yield a series of polymers of novolac- or resol-type phenolic resins. These phenolic resins may further be modified by epoxidation with epichlorohydrin to duplicate the performance of such phenolic-type novolacs (CFN). The structural changes during curing of blend samples of epoxy and carboxyl terminated poly (butadiene-co-acrylonitrile) (CTBN) were studies by Fourier-transform infrared (FTIR) spectrophotometer. The epoxy samples were synthesized by biomass material, cardanol. Blend sample was prepared by physical mixing of CTBN ranging between 0 and 20 weight percent CTBN liquid rubber into cardanol-based epoxidized novolac (CEN) resin. The FTIR spectrum of uncured blend sample clearly indicated that there appeared a band in the region of 3200-3500 cm- 1 which might be due to the presence of phenolic hydroxyl group and sbnd OH group of the opened epoxide. Pure epoxy resin showed peaks near 856 cm- 1 which might be due to oxirane functionality of the epoxidized novolac resin. Both epoxy and its blend sample was cured with polyamine. The cure temperature of CEN resin was found to be decreased by the incorporation of CTBN. The decomposition behavior was also studied by thermogravimetric analyzer (TGA). Two-step decomposition behavior was observed in both epoxy and its blend samples.

  9. Morphological and mechanical analyses of laminates manufactured from randomly positioned carbon fibre/epoxy resin prepreg scraps

    Science.gov (United States)

    Souza, Christiane S. R.; Cândido, Geraldo M.; Alves, Wellington; Marlet, José Maria F.; Rezende, Mirabel C.

    2017-10-01

    This study aims to contribute to sustainability by proposing the reuse of composite prepreg scrap as an added value from discards. The research evaluates the microstructure and mechanical properties of laminates processed by the reuse of uncured carbon fibre/F155-epoxy resin prepreg scraps, waste from the ply cutting area of an aeronautical industry. The composite scraps were used as collected and were randomly positioned to produce laminates to be cured at an autoclave. The mechanical characterization shows a decrease of 39% for the compression property due to the discontinuous fibres in the laminate and an increase of 34% for the interlaminar shear strength, when compared to continuous fibre laminates. This increase is attributed to the higher crosslink density of the epoxy resin, as a result of the cure temperature used in autoclave (60 °C higher than suggested by supplier) and also to the randomly positioned scraps. Microscopic analyses confirm the consolidation of laminates, although show resin rich areas with different sizes and shapes attributed to the overlapping of the scraps with different sizes and shapes. These resin rich areas may contribute to decrease the mechanical properties of laminates. The correlation between mechanical and morphological results shows potential to be used on non-critical structural application, as composite jigs, contributing to sustainability.

  10. Curing agent for polyepoxides and epoxy resins and composites cured therewith. [preventing carbon fiber release

    Science.gov (United States)

    Serafini, T. T.; Delvigs, P.; Vannucci, R. D. (Inventor)

    1981-01-01

    A curing for a polyepoxide is described which contains a divalent aryl radical such as phenylene a tetravalent aryl radical such as a tetravalent benzene radical. An epoxide is cured by admixture with the curing agent. The cured epoxy product retains the usual properties of cured epoxides and, in addition, has a higher char residue after burning, on the order of 45% by weight. The higher char residue is of value in preventing release to the atmosphere of carbon fibers from carbon fiber-epoxy resin composites in the event of burning of the composite.

  11. Biodeterioration of epoxy resin: a microbial survey through culture-independent and culture-dependent approaches.

    Science.gov (United States)

    Pangallo, Domenico; Bučková, Maria; Kraková, Lucia; Puškárová, Andrea; Šaková, Nikoleta; Grivalský, Tomaš; Chovanová, Katarina; Zemánková, Milina

    2015-02-01

    During the 20th century, synthetic polymers were greatly used in the field of art. In particular, the epoxy resins were used for both conservation and for creating sculptures. The biodeterioration of these polymers has not been adequately studied. The aim of this investigation was to examine the microflora responsible for the deterioration of an epoxy statue exposed to outdoor conditions. Fungal and bacterial microflora were isolated from the art object, clustered by fluorescence-ITS (internal transcribed spacer), identified by ITS and 16S rRNA sequencing and tested for their lipolytic abilities by three agar assays. Different algal, bacterial, cyanobacterial and fungal clone libraries were constructed. The surrounding airborne microflora was analyzed using culture-dependent and culture-independent approaches. The results indicated the presence, on the statue surface, of an interesting and differentiate microbial community composed of rock-inhabiting members, algal photobionts (Trebouxia spp., Chloroidium ellipsoideum and Chlorella angustoellipsoidea), Cyanobacteria (Leptolyngbya sp., Phormidium sp., Cylindrospermum stagnale, Hassallia byssoidea and Geitlerinema sp.), black yeasts related to the species Friedmanniomyces endolithicus, Pseudotaeniolina globosa, Phaeococcomyces catenatus and Catenulostroma germanicum and several plant-associated fungi. This investigation provides new information on the potential microfloral inhabitants of epoxy resin discovering a new ecological niche, occupied mainly by several members of rock-colonizing microbial species. © 2014 Society for Applied Microbiology and John Wiley & Sons Ltd.

  12. Effect of epoxy resin on bending momentum in L type corner joins

    Directory of Open Access Journals (Sweden)

    Mehmet Nuri Yıldırım

    2017-11-01

    Full Text Available In the furniture industry, the joining points of frame and box construction furniture according to the loads to be affected by the use place is important for the security of the user and service life of the furniture element. In this direction, it is aimed to determine the diagonal compression and diagonal tensile moment values of "L" type corner joints of box framed construction furniture prepared from solid wood materials. The Pinus Nigra, Fagus Orientalis L and Populus Nigra were used as solid wood materials. Wood-based biscuit joining elements were used in corner joints of the test construction and epoxy resin was used as glue for materials. The static loads were applied to construction according to ASTM-D1037. The results show that, the highest tensile and compression values were obtained from Fagus Orientalis L and the lowest values were obtained from Populus Nigra specimens. In the statistical study, the difference between the tensile and compressive bending moment values of the biscuit connection element was found to be statistically significant. This study indicates that, it is suggested to use of L type joints prepared from Fagus Orientalis L by using epoxy resin and wood based biscuit joining element in frame constructions.

  13. Physical properties of a high molecular weight hydroxyl-terminated polydimethylsiloxane modified castor oil based polyurethane/epoxy interpenetrating polymer network composites

    Science.gov (United States)

    Chen, Shoubing; Wang, Qihua; Wang, Tingmei

    2011-06-01

    A series of polyurethane (PU)/epoxy resin (EP) graft interpenetrating polymer network (IPN) composites modified by a high molecular weight hydroxyl-terminated polydimethylsiloxane (HTPDMS) were prepared. The effects of HTPDMS content on the phase structure, damping properties and the glass transition temperature ( Tg) of the HTPDMS-modified PU/EP IPN composites were studied by scanning electron microscopy (SEM) and dynamic mechanical analysis (DMA). Thermogravimetric analysis (TGA) showed that the thermal decomposition temperature of the composites increased with the increase of HTPDMS content. The tensile strength and impact strength of the IPN composites were also significantly improved, especially when the HTPDMS content was 10%. The modified IPN composites were expected to be used as structural damping materials in the future.

  14. Study of Dielectric Properties and Morphology of Epoxy Resin with Silicon Dioxide Microparticles and Nanoparticles

    Czech Academy of Sciences Publication Activity Database

    Hudec, Jiří; Neděla, Vilém

    2016-01-01

    Roč. 22, S3 (2016), s. 1896-1897 ISSN 1431-9276 R&D Projects: GA MŠk ED0017/01/01 Institutional support: RVO:68081731 Keywords : epoxy resin ESEM * Nanoparticles * silicon dioxide * ESEM Subject RIV: JA - Electronics ; Optoelectronics, Electrical Engineering Impact factor: 1.891, year: 2016

  15. The effect of bulk-resin CNT-enrichment on damage and plasticity in shear-loaded laminated composites

    KAUST Repository

    Ventura, Isaac Aguilar

    2013-07-01

    One way to improve multi functionality of epoxy-based laminated composites is to dope the resin with carbon nanotubes. Many investigators have focused on the elastic and fracture behavior of such nano-modified polymers under tensile loading. Yet, in real structural applications, laminated composites can exhibit plasticity and progressive damage initiated mainly by shear loading. We investigated the damage and plasticity induced by the addition of carbon nanotubes to the matrix of a glass fiber/epoxy composite system. We characterized both the modified epoxy resin and the associated modified laminates using classical mesoscale analysis. We used dynamic mechanical analysis, scanning electron microscopy, atomic force microscopy and classical mechanical testing to characterize samples with different concentrations of nanofillers. Since the samples were prepared using the solvent evaporation technique, we also studied the influence of this process. We found that in addition to the global increase in elastic regime properties, the addition of carbon nanotubes also accelerates the damage process in both the bulk resin and its associated glass-fiber composite. © 2013 Elsevier Ltd.

  16. Comparative study of resin sealant and resin modified glass ionomer as pit and fissure sealant

    Directory of Open Access Journals (Sweden)

    Shirin Malek

    2017-02-01

    Full Text Available The purpose of the present study was to compare the marginal integrity of resin modified glass ionomer cement with that of resin sealant, in vitro. Forty artificial pit and fissure cavities were prepared in occlusal surface of extracted premolar teeth by using ¼ round carbide bur. Cavities were condensed with artificial organic debris followed by cleaning with prophylaxis pumice brush and paste and then separated into two treatment groups. In Group A, 15 fissure cavities were sealed by resin sealant and in Group B, 15 fissure cavities were sealed by resin modified glass ionomer sealant. These specimens were subjected to thermo-cycling followed by dye penetration test. The remaining 5 cavities from each group were analyzed for debris score by the SEM. The results of the microleakage test showed that the efficacy of preventing microleakage of samples sealed by resin modified glass ionomer sealant was higher than the samples sealed by resin sealant. However, no significant differences were found. It can be concluded that use of resin modified glass ionomer sealant is a good alternative for sealing pits and fissures.

  17. Fracture frequency and longevity of fractured resin composite, polyacid-modified resin composite, and resin-modified glass ionomer cement class IV restorations: an up to 14 years of follow-up

    DEFF Research Database (Denmark)

    van Dijken, Jan W V; Pallesen, Ulla

    2010-01-01

    The aim of this study was to evaluate the fracture frequency and longevity of fractured class IV resin composite (RC), polyacid-modified resin composite (compomer; PMRC), and resin-modified glass ionomer cement (RMGIC) restorations in a longitudinal long-term follow-up. Eighty-five class IV RC (43...

  18. Evaluación de la adherencia de uniones adhesivas metálicas con adhesivos epoxídicos modificados Evaluation of the adherence of bonded metallic joints with modified epoxy adhesives

    Directory of Open Access Journals (Sweden)

    Filiberto González Garcia

    2008-03-01

    Full Text Available En este trabajo fueron evaluadas las propiedades adhesivas de la resina epoxídica del tipo éter diglicidílico del bisfenol A. La resina fue modificada con dos modificadores poliméricos, uno de ellos un copolímero derivado del butadieno, y el otro un copolímero acrílico con el propósito de aumentar la tenacidad de la resina. Tres aminas alifáticas primarias fueron utilizadas como agentes de curado, trietilentetramina, N-(2-aminoetilpiperazina e isoforondiamina. Las propiedades adhesivas fueron investigadas usando la resina pura, así como la resina modificada. Las propiedades adhesivas de la resina modificada y pura fueron estudiadas usando como adherente una aleación de acero (ASTM A36. La adherencia fue evaluada por ensayos de adhesión usando tres geometrías de uniones adhesivas de acero-acero. El comportamiento reológico de los adhesivos fue investigado en condiciones isotérmicas. Los parámetros reológicos relacionados con la reacción de polimerización tales como velocidad de reacción, tiempo de manipulación, y tiempo de gelación de los adhesivos puros fueron relacionados con la estructura química del agente de curado. El tiempo de separación de fases, y de gelación de los adhesivos modificados fue relacionado con la morfología generada, y con la velocidad de la reacción, respectivamente. La morfología fue caracterizada por microscopia electrónica de barrido. La adherencia de las uniones adhesivas sometidas a las diferentes solicitaciones mecánicas fue relacionada a la morfología generada por la fase dispersa de cada modificador, y con las estructuras de redes de los adhesivos.In this work the adhesive properties of epoxy resins based on diglycidyl ether of bisphenol A have been evaluated. The epoxy resin was modified with butadiene and acrylic copolymers to obtain toughened adhesives. The aliphatic primary amines triethylenetetramine, N-(2-aminoethylpiperazine and isophorone diamine were investigated as curing

  19. Effects of Core-Shell Rubber (CSR) Nanoparticles on the Fracture Toughness of an Epoxy Resin at Cryogenic Temperatures

    Science.gov (United States)

    Wang, J.; Cannon, S. A.; Schneider, J. A.

    2008-01-01

    This study investigates the effects of core-shell rubber (CSR) nanoparticles on the fracture toughness of an epoxy resin at liquid nitrogen (LN2) temperatures. Varying amounts of Kane Ace (Registered TradeMark) MX130 toughening agent were added to a commercially available EPON 862/W epoxy resin. Resulting fracture toughness was evaluated by the use of Charpy impact tests conducted on an instrumented drop tower. The size and distribution of the CSR nanoparticles were characterized using Transmission Electric Microscopy (TEM) and Small Angle X-ray Scattering (SAXS). Up to nominal 4.6% addition of the CSR nanoparticles, resulted in a nearly 5 times increase in the measured breaking energy. However, further increases in the amount of CSR nanoparticles had no appreciable affect on the breaking energy.

  20. Epoxy cracking in the epoxy-impregnated superconducting winding: nonuniform dissipation of stress energy in a wire-epoxy matrix model

    International Nuclear Information System (INIS)

    Tsukamoto, O.; Iwasa, Y.

    1985-01-01

    The authors present the epoxy-crack-induced temperature data of copper wires imbedded in wire-epoxy resin composite model at 4.2 K. The experimental results show that the epoxy-crackinduced temperature rise is higher in the copper wires than in the epoxy matrix, indicating that in stress-induced wire-epoxy failure, stress energy stored in the wire-epoxy matrix is preferrentially dissipated in the wire. A plausible mechanism of the nonuniform dissipation is presented

  1. Comparison of Mechanical Properties of Resin Composites with Resin Modified Glass Ionomers

    Directory of Open Access Journals (Sweden)

    Taha NA

    2015-06-01

    Full Text Available Statement of Problem: There are controversial reports regarding physical and mechanical properties of resin composites and glass ionomer cements. Some revealed higher strength and hardness for resin composites while others showed a comparable value for glass ionomer cements. Evaluation of mechanical properties of different types of resin composites in comparison with resin modified glass ionomers is not widely studied. Objectives: To measure and compare the flexural strength and Vickers hardness of three resin composites and two resins modified glass ionomer cements before and after ageing. Materials and Methods: Three resin composites, i.e. Filtek Supreme XTE (3M ESPE, Ice (SDI, Gradia (GC, and two resins modified glass ionomers, i.e. Fuji II LC (GC and Riva Light Cure (SDI, were selected. Ten barshaped specimens were prepared for each material and cured using LED curing light. After 24 hours storage in distilled water at 37oC, the specimens were randomly divided into two equal groups (n=5. The first group was tested as a baseline and the second group was restored at 37oC for another 29 days. Flexural strength was performed by four-point bending test using universal testing machine at crosshead speed of 0.5mm/min, and the maximum load at failure was recorded. The specimen’s halves were used for evaluating Vickers hardness, using a Digital Hardness Tester (300 g/15 sec and the Vickers hardness number (VHN was recorded. Data were analyzed using one-way analysis of variance (ANOVA, Tukey’s and student’s t-test. Results: After 24 hours of immersion, the highest hardness number was found for Filtek Supreme and Ice and the highest flexural strength was obtained for Gradia. After 30 days of storage, hardness of Fuji II LC and Gradia showed a significant decrease; flexural strength of Ice and Fuji II LC revealed a significant increase while Gradia and Filtek Supreme showed a significant decrease. Conclusions: Resin modified glass ionomers showed

  2. Leaching test of bituminized waste and waste solidified by epoxy resin

    International Nuclear Information System (INIS)

    Yoshinaka, Kazuyuki; Sugaya, Atsushi; Onizawa, Toshikazu; Takano, Yugo; Kimura, Yukihiko

    2008-10-01

    About 30,000 bituminized waste drums and about 1800 drums of waste solidified by epoxy resin, generated from Tokai Reprocessing Plant, were stored in storage facilities. And study for disposal of these waste is performed. It was considered that radioactive nuclides and chemical components were released from these waste by contact of underground water, when disposed there waste. This paper is reported that result of leaching tests for these waste, done from 2003 to 2006. We've get precious knowledge and data, as follows. (1) In leaching tests for bituminized waste, it has detected iodine-129 peak, considered difficult too low energy gamma to detect. We've get data and knowledge of iodine-129 behavior first. Leached radioactivity for 50 days calculated by peak area was equal for about 40% and 100% of including radioactivity in bituminized waste sample. And we've get data of behavior of nitric acid ion and so on, important to study for disposal, in various condition of sample shape or leaching liquid temperature. (2) In leaching test for waste solidified by epoxy resin, we've get data of behavior of TBP, radionuclides and so on, important to study for disposal. Leached TBP was equal about 1% of including of sample. And we've get data of iodine-129 behavior, too. It was confirmed that leached iodine-129 was equal for about 60% and 100% of including sample, for 90 days. (author)

  3. Incorporation of the Fe3O4 and SiO2 nanoparticles in epoxy-modified silicone resin as the coating for soft magnetic composites with enhanced performance

    Science.gov (United States)

    Luo, Dahao; Wu, Chen; Yan, Mi

    2018-04-01

    Three inorganic-organic hybrids have been designed by incorporating epoxy-modified silicone resin (ESR) with SiO2, Fe3O4 and their mixture in the application as the coating of Fe soft magnetic composites (SMCs). The introduced SiO2 nanoparticles are well dispersed in the ESR, while the Fe3O4 tends to agglomerate or even separate from the ESR. Simultaneous addition of the SiO2 and Fe3O4 gives rise to satisfactory distribution of both nanoparticles and optimized magnetic performance of the SMCs with high permeability (124.6) and low loss (807.8 mW/cm3). On one hand, introduction of the ferromagnetic Fe3O4 reduces the magnetic dilution effect, which is beneficial for improved magnetization and permeability. On the other hand, SiO2 incorporation prevents the agglomeration of the Fe3O4 nanoparticles and gives rise to increased electrical resistivity for reduced core loss as well as enhanced mechanical strength of the SMCs.

  4. A Study of Clay-Epoxy Nanocomposites Consisting of Unmodified Clay and Organo Clay

    Directory of Open Access Journals (Sweden)

    Graham Edward

    2006-04-01

    Full Text Available Clay-epoxy nanocomposites were synthesized from DGEBA resin and montmorillonite clay with an in-situ polymerization. One type of untreated clay and two types of organo clay were used to produce the nanocompsoites. The aims of this study were to examine the nanocomposite structure using different tools and to compare the results between the unmodified clay and modified clays as nanofillers. Although diffractogram in reflection mode did not show any apparent peak of both types of materials, the transmitted XRD (X-Ray Difraction graphs, DSC (Differential Scanning Calorimeter analysis and TEM (Transmission Electron Microscope images revealed that the modified clay-epoxy and unmodified clay-epoxy provides different results. Interestingly, the micrographs showed that some of the modified clay layers possessed non-exfoliated layers in the modified clay-epoxy nanocomposites. Clay aggregates and a hackle pattern were found from E-SEM images for both types of nanocomposite materials. It is shown that different tools should be used to determine the nanocomposite structure.

  5. Characterization of Epoxy Functionalized Graphite Nanoparticles and the Physical Properties of Epoxy Matrix Nanocomposites

    Science.gov (United States)

    Miller, Sandi G.; Bauer, Jonathan L.; Maryanski, Michael J.; Heimann, Paula J.; Barlow, Jeremy P.; Gosau, Jan-Michael; Allred, Ronald E.

    2010-01-01

    This work presents a novel approach to the functionalization of graphite nanoparticles. The technique provides a mechanism for covalent bonding between the filler and matrix, with minimal disruption to the sp2 hybridization of the pristine graphene sheet. Functionalization proceeded by covalently bonding an epoxy monomer to the surface of expanded graphite, via a coupling agent, such that the epoxy concentration was measured as approximately 4 wt.%. The impact of dispersing this material into an epoxy resin was evaluated with respect to the mechanical properties and electrical conductivity of the graphite-epoxy nanocomposite. At a loading as low as 0.5 wt.%, the electrical conductivity was increased by five orders of magnitude relative to the base resin. The material yield strength was increased by 30% and Young s modulus by 50%. These results were realized without compromise to the resin toughness.

  6. Thermally activated, single component epoxy systems

    KAUST Repository

    Unruh, David A.; Pastine, Stefan J.; Moreton, Jessica C.; Frechet, Jean

    2011-01-01

    A single component epoxy system in which the resin and hardener components found in many two-component epoxies are combined onto the same molecule is described. The single molecule precursor to the epoxy resin contains both multiple epoxide moieties and a diamine held latent by thermally degradable carbamate linkages. These bis-carbamate "single molecule epoxies" have an essentially infinite shelf life and access a significant range in curing temperatures related to the structure of the carbamate linkages used. © 2011 American Chemical Society.

  7. Thermally activated, single component epoxy systems

    KAUST Repository

    Unruh, David A.

    2011-08-23

    A single component epoxy system in which the resin and hardener components found in many two-component epoxies are combined onto the same molecule is described. The single molecule precursor to the epoxy resin contains both multiple epoxide moieties and a diamine held latent by thermally degradable carbamate linkages. These bis-carbamate "single molecule epoxies" have an essentially infinite shelf life and access a significant range in curing temperatures related to the structure of the carbamate linkages used. © 2011 American Chemical Society.

  8. Manufacturing of REBCO coils strongly bonded to cooling members with epoxy resin aimed at its application to Maglev

    International Nuclear Information System (INIS)

    Mizuno, Katsutoshi; Ogata, Masafumi; Hasegawa, Hitoshi

    2014-01-01

    Highlights: • Paraffin has a risk of losing thermal coupling during cooling down. • We propose an epoxy impregnated REBCO coil co-wound with PTFE tape. • The coil is tightly bonded to cooling members by epoxy resin without the degradation. • We made a REBCO racetrack coil with the same outer dimension as the Maglev magnet. - Abstract: The REBCO coated conductor has been attracted attention because of its high current density in the presence of high magnetic field. If the coated conductor is applied to Maglev, the operational temperature of the on-board magnets will be over 40 K and energy consumption of cryocoolers will be reduced. That high operational temperature also means the absence of liquid helium. Therefore, reliable thermal coupling is desirable for cooling the coils. We propose an epoxy impregnated REBCO coil co-wound with PTFE tape. While the PTFE tape prevents the performance degradation of the coil, the epoxy resin bonds the coil to cooling members. We carried out three experiments to confirm that the coil structure which we propose has robust thermal coupling without the degradation. First, thermal resistances of paraffin and epoxy were measured varying the temperature from room temperature to 10 K. The measurement result indicates that paraffin has a risk of losing thermal coupling during cooling down. In another experiment, PTFE (polytetrafluoroethylene) tape insulator prevented performance degradation of a small epoxy impregnated REBCO coil, while another REBCO coil with polyimide tape showed clear performance degradation. Finally, we produced a racetrack REBCO coil with the same outer dimension as a Maglev on-board magnet coil. Although the racetrack coil was installed in a GFRP coil case and tightly bonded to the case by epoxy impregnation, any performance degradation was not observed

  9. Manufacturing of REBCO coils strongly bonded to cooling members with epoxy resin aimed at its application to Maglev

    Energy Technology Data Exchange (ETDEWEB)

    Mizuno, Katsutoshi, E-mail: mizuno.katsutoshi.14@rtri.or.jp; Ogata, Masafumi; Hasegawa, Hitoshi

    2014-11-15

    Highlights: • Paraffin has a risk of losing thermal coupling during cooling down. • We propose an epoxy impregnated REBCO coil co-wound with PTFE tape. • The coil is tightly bonded to cooling members by epoxy resin without the degradation. • We made a REBCO racetrack coil with the same outer dimension as the Maglev magnet. - Abstract: The REBCO coated conductor has been attracted attention because of its high current density in the presence of high magnetic field. If the coated conductor is applied to Maglev, the operational temperature of the on-board magnets will be over 40 K and energy consumption of cryocoolers will be reduced. That high operational temperature also means the absence of liquid helium. Therefore, reliable thermal coupling is desirable for cooling the coils. We propose an epoxy impregnated REBCO coil co-wound with PTFE tape. While the PTFE tape prevents the performance degradation of the coil, the epoxy resin bonds the coil to cooling members. We carried out three experiments to confirm that the coil structure which we propose has robust thermal coupling without the degradation. First, thermal resistances of paraffin and epoxy were measured varying the temperature from room temperature to 10 K. The measurement result indicates that paraffin has a risk of losing thermal coupling during cooling down. In another experiment, PTFE (polytetrafluoroethylene) tape insulator prevented performance degradation of a small epoxy impregnated REBCO coil, while another REBCO coil with polyimide tape showed clear performance degradation. Finally, we produced a racetrack REBCO coil with the same outer dimension as a Maglev on-board magnet coil. Although the racetrack coil was installed in a GFRP coil case and tightly bonded to the case by epoxy impregnation, any performance degradation was not observed.

  10. Electrochemical Performance of a New Modified Graphite-Epoxy Electrode for Covalent Immobilization of DNA

    OpenAIRE

    Balbin-Tamayo, Abel I; Riso, Laura S; Esteva-Guas, Ana Margarita; Mardini-Farias, Pércio Augusto; Pérez-Gramatges, Aurora

    2017-01-01

    A new epoxy conducting composite material prepared from epoxy resin, graphite and benzoic acid was developed and used for the manufacture of electrodes, which were characterized by cyclic voltammetry, Raman spectroscopy and field-emission scanning electron microscopy (FESEM). The dependence of peak-to-peak potential, peak anodic current, and the anodic peak/cathodic peak current ratio with scan rate were evaluated by cyclic voltammetry taking into account the Fe(CN)6(3-/4-) standard redox sys...

  11. Surface Modifier-Free Organic-Inorganic Hybridization To Produce Optically Transparent and Highly Refractive Bulk Materials Composed of Epoxy Resins and ZrO2 Nanoparticles.

    Science.gov (United States)

    Enomoto, Kazushi; Kikuchi, Moriya; Narumi, Atsushi; Kawaguchi, Seigou

    2018-04-25

    Surface modifier-free hybridization of ZrO 2 nanoparticles (NPs) with epoxy-based polymers is demonstrated for the first time to afford highly transparent and refractive bulk materials. This is achieved by a unique and versatile hybridization via the one-pot direct phase transfer of ZrO 2 NPs from water to epoxy monomers without any aggregation followed by curing with anhydride. Three types of representative epoxy monomers, bisphenol A diglycidyl ether (BADGE), 3,4-epoxycyclohexylmethyl-3',4'-epoxycyclohexane carboxylate (CEL), and 1,3,5-tris(3-(oxiran-2-yl)propyl)-1,3,5-triazinane-2,4,6-trione (TEPIC), are used to produce transparent viscous dispersions. The resulting ZrO 2 NPs are thoroughly characterized using dynamic light scattering (DLS), transmission electron microscopy (TEM), Fourier transform infrared (FT-IR), and solid-state 13 C CP/MAS NMR measurements. The results from DLS and TEM analyses indicate nanodispersion of ZrO 2 into epoxy monomers as a continuous medium. A surface modification mechanism and the binding fashion during phase transfer are proposed based on the FT-IR and solid-state 13 C CP/MAS NMR measurements. Epoxy-based hybrid materials with high transparency and refractive index are successfully fabricated by heat curing or polymerizing a mixture of monomers containing epoxy-functionalized ZrO 2 NPs and methylhexahydrophthalic anhydride in the presence of a phosphoric catalyst. The TEM and small-angle X-ray scattering measurements of the hybrids show a nanodispersion of ZrO 2 in the epoxy networks. The refractive index at 594 nm ( n 594 ) increases up to 1.765 for BADGE-based hybrids, 1.667 for CEL-based hybrids, and 1.693 for TEPIC-based hybrids. Their refractive indices and Abbe's numbers are quantitatively described by the Lorentz-Lorenz effective medium expansion theory. Their transmissivity is also reasonably explained using Fresnel refraction, Rayleigh scattering, and the Lambert-Beer theories. This surface modifier-free hybridization

  12. Structural investigation of e-beam cured epoxy resins through solid state NMR

    International Nuclear Information System (INIS)

    Alessi, Sabina; Spinella, Alberto; Caponetti, Eugenio; Dispenza, Clelia; Spadaro, Giuseppe

    2012-01-01

    In this paper the network structure of e-beam cured DGEBF based epoxy resins is investigated. Two epoxy systems, having different reactivity and cured in different process conditions, were analyzed through solid state NMR spectroscopy. The analysis shows that the more reactive system has higher cross-linking density and higher uniformity of network distribution. Similar information were obtained, in a previous work, on the same systems through dynamic mechanical thermal analysis. It is worth noting that unlike DMTA tests, which interfere with the molecular structure of the analyzed material, due to the heating during the analysis itself, more reliable information, without any artefact, are obtained by solid state NMR, carried out at constant room temperature. - Highlights: ► The structure of two e-beam cured epoxy systems is investigated through solid state NMR. ► The aim is to have direct information about the structure without inducing modifications. ► The different molecular structures are able to emphasize the response of solid state NMR. ► T 1 H, T 1ρ H and T CH measurements indicate different cross-linking degrees. ► The NMR results are in agreement with DMTA analysis performed in a previous paper.

  13. Effect of epoxy resin and hardener containing microcapsules on healing efficiency of epoxy adhesive based metal joints

    International Nuclear Information System (INIS)

    Khan, Nazrul Islam; Halder, Sudipta; Goyat, M.S.

    2016-01-01

    Dual component microcapsules of epoxy resin and polyamine hardener with polymethyl methacrylate (PMMA) shell were synthesized using a water-oil-water emulsion solvent evaporation method. The high concentration of sodium dodecyl sulfate (SDS) was used to reduce the thickness of shell wall of dual component microcapsules. The dual microcapsules of 1:1 weight ratio were introduced in the epoxy adhesive to study the healing effect. The morphology, chemical structure and thermal characteristics of the microcapsules were characterized by scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA), respectively. The insertion of dual component microcapsules in epoxy matrix reduced the lap shear strength of adhesive joints, which may be attributed to the generation of stress concentration cites because of micron sized capsules. However, the extension and absorbed failure energy of adhesive joints under uniaxial loading increased with the increase of concentration of dual microcapsules. The viscoelastic nature of the dual microcapsules may be responsible for this enhancement. Significant enhancement in the healing efficiency (90.93%) of the joints was achieved for 10 wt% of dual microcapsules. The crack pinning and crack blunting mechanisms at the vicinity of the crack path adjacent to the microcapsules were found responsible for significant enhancement in the healing efficiency of the adhesive joints. - Highlights: • High SDS concentration was used to control the dual component microcapsules shell wall thickness. • Self-healing performance of dual component microcapsules reinforced epoxy adhesive based single lap joints was studied. • 90.93% of the damage healing was achieved for self-healing adhesive based single lap joints. • Increase in concentration of microcapsules reduces the lap shear properties of the self-healing joints.

  14. Effect of epoxy resin and hardener containing microcapsules on healing efficiency of epoxy adhesive based metal joints

    Energy Technology Data Exchange (ETDEWEB)

    Khan, Nazrul Islam [Department of Mechanical Engineering, National Institute of Technology Silchar, Silchar 788010, Assam (India); Halder, Sudipta, E-mail: shalder@nits.ac.in [Department of Mechanical Engineering, National Institute of Technology Silchar, Silchar 788010, Assam (India); Goyat, M.S. [Department of Physics, University of Petroleum & Energy Studies, Dehradun, Uttarakhand 248007 (India)

    2016-03-01

    Dual component microcapsules of epoxy resin and polyamine hardener with polymethyl methacrylate (PMMA) shell were synthesized using a water-oil-water emulsion solvent evaporation method. The high concentration of sodium dodecyl sulfate (SDS) was used to reduce the thickness of shell wall of dual component microcapsules. The dual microcapsules of 1:1 weight ratio were introduced in the epoxy adhesive to study the healing effect. The morphology, chemical structure and thermal characteristics of the microcapsules were characterized by scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA), respectively. The insertion of dual component microcapsules in epoxy matrix reduced the lap shear strength of adhesive joints, which may be attributed to the generation of stress concentration cites because of micron sized capsules. However, the extension and absorbed failure energy of adhesive joints under uniaxial loading increased with the increase of concentration of dual microcapsules. The viscoelastic nature of the dual microcapsules may be responsible for this enhancement. Significant enhancement in the healing efficiency (90.93%) of the joints was achieved for 10 wt% of dual microcapsules. The crack pinning and crack blunting mechanisms at the vicinity of the crack path adjacent to the microcapsules were found responsible for significant enhancement in the healing efficiency of the adhesive joints. - Highlights: • High SDS concentration was used to control the dual component microcapsules shell wall thickness. • Self-healing performance of dual component microcapsules reinforced epoxy adhesive based single lap joints was studied. • 90.93% of the damage healing was achieved for self-healing adhesive based single lap joints. • Increase in concentration of microcapsules reduces the lap shear properties of the self-healing joints.

  15. Synthesis and electrical characterization of low-temperature thermal-cured epoxy resin/functionalized silica hybrid-thin films for application as gate dielectrics

    Energy Technology Data Exchange (ETDEWEB)

    Na, Moonkyong, E-mail: nmk@keri.re.kr [HVDC Research Division, Korea Electrotechnology Research Institute, Changwon, 642-120 (Korea, Republic of); System on Chip Chemical Process Research Center, Department of Chemical Engineering, Pohang University of Science and Technology (POSTECH), Pohang, 790-784 (Korea, Republic of); Kang, Young Taec [Creative and Fundamental Research Division, Korea Electrotechnology Research Institute, Changwon, 642-120 (Korea, Republic of); Department of Polymer Science and Engineering, Pusan National University, Busan, 609-735 (Korea, Republic of); Kim, Sang Cheol [HVDC Research Division, Korea Electrotechnology Research Institute, Changwon, 642-120 (Korea, Republic of); Kim, Eun Dong [Creative and Fundamental Research Division, Korea Electrotechnology Research Institute, Changwon, 642-120 (Korea, Republic of)

    2013-07-31

    Thermal-cured hybrid materials were synthesized from homogenous hybrid sols of epoxy resins and organoalkoxysilane-functionalized silica. The chemical structures of raw materials and obtained hybrid materials were characterized using Fourier transform infrared spectroscopy. The thermal resistance of the hybrids was enhanced by hybridization. The interaction between epoxy matrix and the silica particles, which caused hydrogen bonding and van der Waals force was strengthened by organoalkoxysilane. The degradation temperature of the hybrids was improved by approximately 30 °C over that of the parent epoxy material. The hybrid materials were formed into uniformly coated thin films of about 50 nm-thick using a spin coater. An optimum mixing ratio was used to form smooth-surfaced hybrid films. The electrical property of the hybrid film was characterized, and the leakage current was found to be well below 10{sup −6} A cm{sup −2}. - Highlights: • Preparation of thermal-curable hybrid materials using epoxy resin and silica. • The thermal stability was enhanced through hybridization. • The insulation property of hybrid film was investigated as gate dielectrics.

  16. Aging of Organic Matrices, Epoxy Resins; Causas de envejecimiento de matrices organicas. Resinas epoxidicas

    Energy Technology Data Exchange (ETDEWEB)

    Pazos, M.; Prendes, P.; Varela, M.; Paz, S. [Departamento de I mas D de Gairesa, La Coruna (Spain)

    1997-09-01

    Epoxy resins are very important polymers widely used in advance materials. Approximately 200.000 Tns/year are used in different fields such as coating, floor and paving, adhesives, composites, etc. Due to the importance of these polymers, aging studies are necessary. In this work most important aging-factors are described. We have observed that the water plays a very important role in the degradation-process. (Author)

  17. Fabrication and characterization of TiO2-epoxy nanocomposite

    International Nuclear Information System (INIS)

    Chatterjee, Amit; Islam, Muhammad S.

    2008-01-01

    A systematic study has been conducted to investigate the matrix properties by introducing nanosize TiO 2 (5-40 nm, 0.5-2% by weight) fillers into an epoxy resin. Ultrasonic mixing process, via sonic cavitations, was employed to disperse the particles into the resin system. The thermal, mechanical, morphology and the viscoelastic properties of the nanocomposite and the neat resin were measured with TGA, DMA, TEM and Instron. The nano-particles are dispersed evenly throughout the entire volume of the resin. The nanofiller infusion improves the thermal, mechanical and viscoelastic properties of the epoxy resin. The nanocomposite shows increase in storage modulus, glass transition temperature, tensile modulus, flexural modulus and short beam shear strength from neat epoxy resin. The mechanical performance and thermal stability of the epoxy nanocomposites are depending on with the dispersion state of the TiO 2 in the epoxy matrix and are correlated with loading (0.0015-0.006% by volume). In addition, the nanocomposite shows enhanced flexural strength. Several reasons to explain these effects in terms of reinforcing mechanisms were discussed

  18. Effect of Graphene Oxide Mixed Epoxy on Mechanical Properties of Carbon Fiber/Acrylonitrile-Butadiene-Styrene Composites.

    Science.gov (United States)

    Wang, Cuicui; Ge, Heyi; Ma, Xiaolong; Liu, Zhifang; Wang, Ting; Zhang, Jingyi

    2018-04-01

    In this study, the watersoluble epoxy resin was prepared via the ring-opening reaction between diethanolamine and epoxy resin. The modified resin mixed with graphene oxide (GO) as a sizing agent was coated onto carbon fiber (CF) and then the GO-CF reinforced acrylonitrile-butadienestyrene (ABS) composites were prepared. The influences of the different contents of GO on CF and CF/ABS composite were explored. The combination among epoxy, GO sheets and maleic anhydride grafted ABS (ABSMA) showed a synergistic effect on improving the properties of GO-CF and GO-CF/ABS composite. The GO-CF had higher single tensile strength than the commercial CF. The maximum ILSS of GO-CF/ABS composite obtained 19.2% improvement as compared with that of the commercial CF/ABS composite. Such multiscale enhancement method and the synergistic reinforced GO-CF/ABS composite show good prospective applications in many industry areas.

  19. Influence of epoxy resin as encapsulation material of silicon photovoltaic cells on maximum current

    Directory of Open Access Journals (Sweden)

    Acevedo-Gómez David

    2017-01-01

    Full Text Available This work presents an analysis about how the performance of silicon photovoltaic cells is influenced by the use of epoxy resin as encapsulation material with flat roughness. The effect of encapsulation on current at maximum power of mono-crystalline cell was tested indoor in a solar simulator bench at 1000 w/m² and AM1.5G. The results show that implementation of flat roughness layer onto cell surface reduces the maximum current inducing on average 2.7% less power with respect to a cell before any encapsulation. The losses of power and, in consequence, the less production of energy are explained by resin light absorption, reflection and partially neutralization of non-reflective coating.

  20. Thermo-curable epoxy systems for nanoimprint lithography

    International Nuclear Information System (INIS)

    Wu, Chun-Chang; Hsu, Steve Lien-Chung

    2010-01-01

    In this work, we have used solvent-free thermo-curable epoxy systems for low-pressure and moderate-temperature nanoimprint lithography (NIL). The curing kinetic parameters and conversion of diglycidyl ether of bisphenol A (DGEBA) resin with different ambient-cure 930 and 954 hardeners were studied by the isothermal DSC technique. They are useful for the study of epoxy resins in the imprinting application. The DGEBA/930 and DGEBA/954 epoxy resists can be imprinted to obtain high-density nano- and micro-scale patterns on a flexible indium tin oxide/poly(ethylene terephthalate) (ITO/PET) substrate. The DGEBA/930 epoxy resin is not only suitable for resist material, but also for plastic mold material. Highly dense nanometer patterns can be successfully imprinted using a UV-curable resist from the DGEBA/930 epoxy mold. Using the replicated DGEBA/930 epoxy mold instead of the expensive master can prevent brittle failure of the silicon molds in the NIL

  1. Crosslinking of epoxy-oligoesteric mixtures in the presence of dioxydiphenylpropane diglycidyl ether modified with adipic acid

    Czech Academy of Sciences Publication Activity Database

    Bratychak, M.; Zubal, O.; Bashta, Bogdana; Ivashkiv, O.; Shyshchak, O.; Haponiuk, J.

    2017-01-01

    Roč. 11, č. 2 (2017), s. 180-187 ISSN 1996-4196 Institutional support: RVO:61389013 Keywords : crosslinking * polymer films * epoxy resin Subject RIV: CD - Macromolecular Chemistry OBOR OECD: Polymer science

  2. The ionic conductivity, mechanical performance and morphology of two-phase structural electrolytes based on polyethylene glycol, epoxy resin and nano-silica

    Energy Technology Data Exchange (ETDEWEB)

    Feng, Qihang; Yang, Jiping, E-mail: jyang08@163.com; Yu, Yalin; Tian, Fangyu; Zhang, Boming; Feng, Mengjie; Wang, Shubin

    2017-05-15

    Highlights: • Structural electrolytes based on PEG-epoxy resins were prepared. • Factors of influencing ionic conductivity and mechanical properties were studied. • Co-continuous morphology was benefit for improved structural electrolyte property. • Efficiently optimized multifunctional electrolyte performance was achieved. - Abstract: As one of significant parts of structural power composites, structural electrolytes have desirable mechanical properties like structural resins while integrating enough ionic conductivity to work as electrolytes. Here, a series of polyethylene glycol (PEG)-epoxy-based electrolytes filled with nano-silica were prepared. The ionic conductivity and mechanical performance were studied as functions of PEG content, lithium salt concentration, nano-silica content and different curing agents. It was found that, PEG-600 and PEG-2000 content in the epoxy electrolyte system had a significant effect on their ionic conductivity. Furthermore, increasing the nano-silica content in the system induced increased ionic conductivity, decreased glass transition temperature and mechanical properties, and more interconnected irregular network in the cured systems. The introduction of rigid m-xylylenediamine resulted in enhanced mechanical properties and reasonably decreased ionic conductivity. As a result, these two-phase epoxy structural electrolytes have great potential to be used in the multifunctional energy storage devices.

  3. Effect of γ irradiation on the properties of basalt fiber reinforced epoxy resin matrix composite

    International Nuclear Information System (INIS)

    Li, Ran; Gu, Yizhuo; Yang, Zhongjia; Li, Min; Wang, Shaokai; Zhang, Zuoguang

    2015-01-01

    Gamma-ray (γ-ray) irradiation is a crucial reason for the aging in materials used for nuclear industry. Due to high specific strength and stiffness, light weight and good corrosion resistance, fiber reinforced composites are regarded as an alternative of traditional materials used on nuclear facilities. In this study, basalt fiber (BF)/AG80 epoxy composite laminates were fabricated by autoclave process and treated with "6"0Co gamma irradiation dose up to 2.0 MGy. Irradiation induced polymer chain scission and oxidation of AG80 resin were detected from physical and chemical analysis. The experimental results show that the tensile and flexural performances of irradiated BF/AG80 composite maintain stable and have a low amplitude attenuation respectively, and the interlaminar shear strength has increased from irradiation dose of 0–1.5 MGy. Furthermore, the comparison between the studied BF composite and reported polymer and composite materials was done for evaluating the γ resistance property of BF composite. - Highlights: • The properties of basalt fiber reinforced epoxy resin matrix composite under "6"0Co γ irradiation up to 2.0 MGy were studied. • Basalt fiber can weaken the aging effects of γ irradiation on the resin matrix. • Tensile property of basalt fiber composite remains stable and flexural property has a low degree of attenuation. • Basalt fiber composite is an ideal candidate of structural material for nuclear industry.

  4. Effect of thermally reduced graphene oxide on dynamic mechanical properties of carbon fiber/epoxy composite

    Science.gov (United States)

    Adak, Nitai Chandra; Chhetri, Suman; Murmu, Naresh Chandra; Samanta, Pranab; Kuila, Tapas

    2018-03-01

    The Carbon fiber (CF)/epoxy composites are being used in the automotive and aerospace industries owing to their high specific mechanical strength to weight ratio compared to the other conventional metal and alloys. However, the low interfacial adhesion between fiber and polymer matrix results the inter-laminar fracture of the composites. Effects of different carbonaceous nanomaterials i.e., carbon nanotubes (CNT), graphene nanosheets (GNPs), graphene oxide (GO) etc. on the static mechanical properties of the composites were investigated in detail. Only a few works focused on the improvement of the dynamic mechanical of the CF/epoxy composites. Herein, the effect of thermally reduced grapheme oxide (TRGO) on the dynamic mechanical properties of the CF/epoxy composites was investigated. At first, GO was synthesized using modified Hummers method and then reduced the synthesized GO inside a vacuum oven at 800 °C for 5 min. The prepared TRGO was dispersed in the epoxy resin to modify the epoxy matrix. Then, a number of TRGO/CF/epoxy laminates were manufactured incorporating different wt% of TRGO by vacuum assisted resin transfer molding (VARTM) technique. The developed laminates were cured at room temperature for 24 h and then post cured at 120 °C for 2 h. The dynamic mechanical analyzer (DMA 8000 Perkin Elmer) was used to examine the dynamic mechanical properties of the TRGO/CF/epoxy composites according to ASTM D7028. The dimension of the specimen was 44×10×2.4 mm3 for the DMA test. This test was carried out under flexural loading mode (duel cantilever) at a frequency of 1 Hz and amplitude of 50 μm. The temperature was ramped from 30 to 200 °C with a heating rate of 5 °C min-1. The dynamic mechanical analysis of the 0.2 wt% TRGO incorporated CF/epoxy composites showed ~ 96% enhancement in storage modulus and ~ 12 °C increments in glass transition temperature (Tg) compared to the base CF/epoxy composites. The fiber-matrix interaction was studied by Cole

  5. Improvement of the epoxy coating properties by incorporation of polyaniline surface treated TiO2 nanoparticles previously modified with vitamin B6

    OpenAIRE

    Radoman, Tijana S.; Džunuzović, Jasna V.; Grgur, Branimir; Gvozdenović, Milica M.; Jugović, Branimir; Miličević, Dejan S.; Džunuzović, Enis S.

    2016-01-01

    Novel TiO2-PANI core-shell nanocomposite, prepared by in situ oxidative polymerization of aniline in the presence of TiO2 nanoparticles surface modified with vitamin B6, was used to reinforce epoxy resin. The size of prepared TiO2 nanoparticles and TiO2-PANI nanocomposite were determined by a transmission electron microscopy (TEM). The surface modification of TiO2 nanoparticles was confirmed by FTIR and UV–vis spectroscopy, while the morphology of PANI and TiO2-PANI nanocomposite was investig...

  6. Long-Term Durability of Basalt Fiber-Reinforced Polymer (BFRP Sheets and the Epoxy Resin Matrix under a Wet–Dry Cyclic Condition in a Chloride-Containing Environment

    Directory of Open Access Journals (Sweden)

    Zhongyu Lu

    2017-11-01

    Full Text Available Basalt fiber-reinforced polymer (BFRP composites are receiving increasing attention as they represent a low-cost green source of raw materials. FRP composites have to face harsh environments, such as chloride ions in coastal marine environments or cold regions with salt deicing. The resistance of FRPs subjected to the above environments is critical for the safe design and application of BFRP composites. In the present paper, the long-term durability of BFRP sheets and the epoxy resin matrix in a wet–dry cyclic environment containing chloride ions was studied. The specimens of the BFRP sheet and epoxy resin matrix were exposed to alternative conditions of 8-h immersion in 3.5% NaCl solution at 40 °C and 16-h drying at 25 °C and 60% relative humidity (RH. The specimens were removed from the exposure chamber at the end of the 180th, 270th and 360th cycles of exposure and were analyzed for degradation with tensile tests, scanning electron microscopy (SEM and void volume fractions. It was found that the tensile modulus of the BFRP sheet increased by 3.4%, and the tensile strength and ultimate strain decreased by 45% and 65%, respectively, after the 360th cycle of exposure. For the epoxy resin matrix, the tensile strength, tensile modulus and ultimate strain decreased by 27.8%, 3.2% and 64.8% after the 360th cycle of exposure, respectively. The results indicated that the degradation of the BFRP sheet was dominated by the damage of the interface between the basalt fiber and epoxy resin matrix. In addition, salt precipitate accelerated the fiber–matrix interfacial debonding, and hydrolysis of the epoxy resin matrix resulted in many voids, which accelerated the degradation of the BFRP sheet.

  7. Exploring the tensile strain energy absorption of hybrid modified epoxies containing soft particles

    International Nuclear Information System (INIS)

    Abadyan, M.; Bagheri, R.; Kouchakzadeh, M.A.; Hosseini Kordkheili, S.A.

    2011-01-01

    Research highlights: → Two epoxy systems have been modified by combination of fine and coarse modifiers. → While both hybrid systems reveal synergistic K IC , no synergism is observed in tensile test. → It is found that coarse particles induce stress concentration in hybrid samples. → Stress concentration leads to fracture of samples at lower energy absorption levels. -- Abstract: In this paper, tensile strain energy absorption of two different hybrid modified epoxies has been systematically investigated. In one system, epoxy has been modified by amine-terminated butadiene acrylonitrile (ATBN) and hollow glass spheres as fine and coarse modifiers, respectively. The other hybrid epoxy has been modified by the combination of ATBN and recycled Tire particles. The results of fracture toughness measurement of blends revealed synergistic toughening for both hybrid systems in some formulations. However, no evidence of synergism is observed in tensile test of hybrid samples. Scanning electron microscope (SEM), transmission optical microscope (TOM) and finite element (FEM) simulation were utilized to study deformation mechanisms of hybrid systems in tensile test. It is found that coarse particles induce stress concentration in hybrid samples. This produces non-uniform strain localized regions which lead to fracture of hybrid samples at lower tensile loading and energy absorption levels.

  8. Improving Fracture Toughness of Epoxy Nanocomposites by Silica Nanoparticles

    Directory of Open Access Journals (Sweden)

    Seyed Reza Akherati Sany

    2017-04-01

    Full Text Available An epoxy resin was modified by silica nanoparticles and cured with an anhydride. The particles with different batches of 12, 20, and 40 nm sizes were each distributed into the epoxy resin ultrasonically. Electron microscopy images showed that the silica particles were well dispersed throughout the resin. Tensile test results showed that Young’s modulus and tensile strength increased with the volume fraction and surface area of the silica particles. The simultaneous use of two average sizes of 20 and 40 nm diameter silica particles still increased these mechanical properties but other combinations of silica particles were unsuccessful. A three-point bending test on each pre-cracked specimen was performed to measure the mode I fracture toughness energy. The fracture energy increased from 283 J/m2 for the unmodified epoxy to about 740 J/m2 for the epoxy with 4.5 wt% of 12 nm diameter silica nanoparticles. The fracture energy of smaller particles was greater because of their higher surface to volume ratio. The fracture energy results showed also that the combined nanoparticles has a synergic effect on the fracture toughness of nanocomposites. Simultaneous use of 10 and 20 nm particles increased the fracture energy to about 770 J/m2. Finally, crack-opening displacement was calculated and found to be in the range of several micrometers which was much larger than the sizes of particles studied. Thus, the toughening mechanisms of crack pinning and crack deflection have a negligible effect on improvement of toughness, nevertheless, the plastic deformation and plastic void growth are dominant mechanisms in epoxy toughening by nanoparticles.

  9. Friction and wear behavior of nanosilica-filled epoxy resin composite coatings

    International Nuclear Information System (INIS)

    Kang Yingke; Chen Xinhua; Song Shiyong; Yu Laigui; Zhang Pingyu

    2012-01-01

    Hydrophilic silica nanoparticles (abridged as nano-SiO 2 ) surface-capped with epoxide were dispersed in the solution of epoxy resin (abridged as EP) in tetrahydrofuran under magnetic stirring. Resultant suspension of nano-SiO 2 in EP was then coated onto the surface of glass slides and dried at 80 °C in a vacuum oven for 2 h, generating epoxy resin-nanosilica composite coatings (coded as EP/nano-SiO 2 ). EP coating without nano-SiO 2 was also prepared as a reference in the same manner. A water contact angle meter and a surface profiler were separately performed to measure the water contact angles and surface roughness of as-prepared EP/nano-SiO 2 composite coatings. The friction and wear behavior of as-prepared EP/nano-SiO 2 composite coatings sliding against steel in a ball-on-plate contact configuration under unlubricated condition was evaluated. Particularly, the effect of coating composition on the friction and wear behavior of the composite coatings was highlighted in relation to their microstructure and worn surface morphology examined by means of scanning electron microscopy. Results indicate that EP/nano-SiO 2 composite coatings have a higher surface roughness and water contact angle than EP coating. The EP-SiO 2 coatings doped with a proper amount of hydrophilic SiO 2 nanoparticles show lower friction coefficient than EP coating. However, the introduction of surface-capped nanosilica as the filler results in inconsistent change in the friction coefficient and wear rate of the filled EP-matrix composites; and it needs further study to achieve well balanced friction-reducing and antiwear abilities of the composite coatings for tribological applications.

  10. A study of thermal diffusivity of carbon-epoxy and glass-epoxy composites using the modified pulse method

    Directory of Open Access Journals (Sweden)

    Terpiłowski Janusz

    2014-09-01

    Full Text Available Transient heat transfer is studied and compared in two planeparallel composite walls and one EPIDIAN 53 epoxy resin wall acting as a matrix for both composites. The first of the two walls is made of carbonepoxy composite; the other wall is made of glass-epoxy composite, both with comparable thickness of about 1 mm and the same number of carbon and glass fabric layers (four layers. The study was conducted for temperatures in the range of 20-120 °C. The results of the study of thermal diffusivity which characterizes the material as a heat conductor under transient conditions have a preliminary character. Three series of tests were conducted for each wall. Each series took about 24 h. The results from the three series were approximated using linear functions and were found between (0.7-1.35×10−7m2/s. In the whole range of temperature variation, the thermal diffusivity values for carbon-epoxy composite are from 1.2 to 1.5 times higher than those for the other two materials with nearly the same thermal diffusivity characteristics.

  11. Preparation of epoxy/zirconia hybrid materials via in situ polymerization using zirconium alkoxide coordinated with acid anhydride

    International Nuclear Information System (INIS)

    Ochi, Mitsukazu; Nii, Daisuke; Harada, Miyuki

    2011-01-01

    Highlights: → Novel epoxy/zirconia hybrid materials were synthesized via in situ polymerization using zirconium alkoxide coordinated with acid anhydride. → The half-ester compound of acid anhydride desorbed from zirconium played as curing agent of epoxy resin. → The zirconia was uniformly dispersed in the epoxy matrix on the nanometer or sub-nanometer scale by synchronizing the epoxy curing and sol-gel reactions. → The refractive indices of the hybrid materials significantly improved with an increase in the zirconia content. - Abstract: Novel epoxy/zirconia hybrid materials were synthesized using a bisphenol A epoxy resin (diglycidyl ether of bisphenol A; DGEBA), zirconium(IV)-n-propoxide (ZTNP), and hexahydrophthalic anhydride (HHPA) via in situ polymerization. HHPA played two roles in this system: it acted as a modifier to control the hydrolysis and condensation reactions of zirconium alkoxide and also as a curing agent - the half-ester compound of HHPA desorbed from zirconium reacted with the epoxy resin to form the epoxy network. As a result, both the sol-gel reaction and epoxy curing occurred simultaneously in a homogeneous solution, and organic-inorganic hybrid materials were readily obtained. Further, the zirconia produced by the in situ polymerization was uniformly dispersed in the epoxy matrix on the nanometer or sub-nanometer scale; thus, hybrid materials that exhibited excellent optical transparency were obtained. Furthermore, the heat resistance of the hybrid materials could be improved by hybridization with zirconia. And, the refractive indices of the hybrid materials significantly improved with an increase in the zirconia content.

  12. Novel halogen-free flame retardant thermoset from a hybrid hexakis (methoxymethyl melamine/phosphorus-containing epoxy resin cured with phenol formaldehyde novolac

    Directory of Open Access Journals (Sweden)

    2009-12-01

    Full Text Available This paper describes the curing behaviours, thermal properties and flame-resistance of a novel halogen-free epoxy hybrid thermoset, prepared by the curing reaction of hexakis (methoxymethyl melamine (HMMM, a phosphorouscontaining epoxy resin (EPN-D with 9, 10-dihydro-9-oxa-10-phosphaphenanthrene 10-oxide (DOPO group and phenol formaldehyde novolac (n-PF. The resultant thermosets showed high glass-transition temperatures (Tg, 123–147°C as determined by thermal mechanical analysis (TMA, excellent thermal stability with high 5 wt% decomposition temperatures (Td,5% ≥308°C and high char yields (Yc ≥39.4 wt% from the thermogravimetric analysis (TGA. All the cured EPND/ HMMM/n-PF hybrid resins achieved the UL 94 V-0 grade with high limited oxygen indices (LOI > 45.7. It is found that phosphorous and nitrogen elements in the cured EPN-D/HMMM/n-PF hybrid resins had a positive synergistic effect on the improvement of the flame retardancy.

  13. Experimental design applied optimization of a state in epoxy clay dispersion; Planejamento de experimentos aplicado a otimizacao do estado de dispersao de argilas em epoxi

    Energy Technology Data Exchange (ETDEWEB)

    Paz, Juliana D' Avila; Bertholdi, Jonas; Folgueras, Marilena Valadares; Pezin, Sergio Henrique; Coelho, Luiz Antonio Ferreira, E-mail: julianadpaz@yahoo.com.b [Universidade do Estado de Santa Catarina (UDESC), Joinville, SC (Brazil). Centro de Ciencias Tecnologicas

    2010-07-01

    This paper presents some analysis showed that the exfoliation / intercalation of a montmorillonite clay in epoxy resin such as viscosity, X-ray diffraction (XRD), scanning electron microscopy (SEM) and thermogravimetry (TG). Increasing the viscosity of epoxy resin diglycidyl ether bisphenol A with the addition of clay associated with the sonification system at the time of dispersion is a good indication of exfoliation. The X-ray diffraction already cured composite shows a decrease of crystallinity of clay and EDS microanalysis of SEM, non-uniform dispersion of clay in epoxy resin. Thermal analysis TG composite clay / epoxy shows an increase in thermal stability relative to pure epoxy. (author)

  14. ORGANIC/INORGANIC HYBRID EPOXY NANOCOMPOSITES BASED ON OCTA(AMINOPHENYL)SILSESQUIOXANE

    Institute of Scientific and Technical Information of China (English)

    Hai-bo Fan; Rong-jie Yang; Xiang-mei Li

    2013-01-01

    Octa(aminophenyl)silsesquioxane (OAPS) was used as the curing agent of diglycidyl ether of bisphenol-A (DGEBA) epoxy resin.A study on comparison of DGEBA/OAPS with DGEBA/4,4'-diaminodiphenyl sulfone (DDS) epoxy resins was achieved.Differential scanning calorimetry was used to investigate the curing reaction and its kinetics,and the glass transition of DGEBA/OAPS.Thermogravimetric analysis was used to investigate thermal decomposition of the two kinds of epoxy resins.The reactions between amino groups and epoxy groups were investigated using Fourier transform infrared spectroscopy.Scanning electron microscopy was used to observe morphology of the two epoxy resins.The results indicated that OAPS had very good compatibility with DGEBA in molecular level,and could form a transparent DGEBA/OAPS resin.The curing reaction of the DGEBA/OAPS prepolymer could occur under low temperatures compared with DGEBA/DDS.The DGEBA/OAPS resin didn't exhibit glass transition,but the DGEBA/DDS did,which meant that the large cage structure of OAPS limited the motion of chains between the cross-linking points.Measurements of the contact angle indicated that the DGEBA/OAPS showed larger angles with water than the DGEBA/DDS resin.Thermogravimetric analysis indicated that the incorporation of OAPS into epoxy system resulted in low mass loss rate and high char yield,but its initial decomposition temperature seemed to be lowered.

  15. Degradation of modified carbon black/epoxy nanocomposite coatings under ultraviolet exposure

    International Nuclear Information System (INIS)

    Ghasemi-Kahrizsangi, Ahmad; Shariatpanahi, Homeira; Neshati, Jaber; Akbarinezhad, Esmaeil

    2015-01-01

    Graphical abstract: - Highlights: • Degradation behavior of modified Carbon Black (CB) epoxy coating was studied under UV irradiation using based on EIS technique. • By using SDS as a surfactant, nano particles of CB were uniformly dispersed in an epoxy matrix. • ATR-FTIR analysis showed that the CB coatings were degraded less than epoxy coating. • EIS results showed the coating with 2.5 wt% CB nanoparticles had higher corrosion resistance than neat epoxy. - Abstract: Degradation of epoxy coatings with and without Carbon Black (CB) nanoparticles under ultraviolet (UV) radiation were investigated using electrochemical impedance spectroscopy (EIS). Sodium dodecyl sulfate (SDS) was used to obtain a good dispersion of CB nanoparticles in a polymer matrix. TEM analysis proved a uniform dispersion of modified CB nanoparticles in epoxy coating. The coatings were subjected to UV radiation to study the degradation behavior and then immersed in 3.5 wt% NaCl. The results showed that the electrochemical behavior of neat epoxy coating was related to the formation and development of microcracks on the surface. The occurrence of microcracks on the surface of the coatings and consequently the penetration of ionic species reduced by adding CB nanoparticles into the formulation of the coatings. CB nanoparticles decreased degradation of CB coatings by absorbing UV irradiation. The ATR-FTIR results showed that decrease in the intensity of methyl group as main peak in presence of 2.5 wt% CB was lower than neat epoxy. In addition, the reduction in impedance of neat epoxy coating under corrosive environment was larger than CB coatings. The CB coating with 2.5 wt% nanoparticles had the highest impedance to corrosive media after 2000 h UV irradiation and 24 h immersion in 3.5 wt% NaCl.

  16. Degradation of modified carbon black/epoxy nanocomposite coatings under ultraviolet exposure

    Energy Technology Data Exchange (ETDEWEB)

    Ghasemi-Kahrizsangi, Ahmad, E-mail: ahmad_usk@yahoo.com [Corrosion Department, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745-4163, Tehran (Iran, Islamic Republic of); Shariatpanahi, Homeira, E-mail: shariatpanahih@ripi.ir [Coating Research Center, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745-4163, Tehran (Iran, Islamic Republic of); Neshati, Jaber [Corrosion Department, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745-4163, Tehran (Iran, Islamic Republic of); Akbarinezhad, Esmaeil [Coating Research Center, Research Institute of Petroleum Industry (RIPI), P.O. Box 18745-4163, Tehran (Iran, Islamic Republic of)

    2015-10-30

    Graphical abstract: - Highlights: • Degradation behavior of modified Carbon Black (CB) epoxy coating was studied under UV irradiation using based on EIS technique. • By using SDS as a surfactant, nano particles of CB were uniformly dispersed in an epoxy matrix. • ATR-FTIR analysis showed that the CB coatings were degraded less than epoxy coating. • EIS results showed the coating with 2.5 wt% CB nanoparticles had higher corrosion resistance than neat epoxy. - Abstract: Degradation of epoxy coatings with and without Carbon Black (CB) nanoparticles under ultraviolet (UV) radiation were investigated using electrochemical impedance spectroscopy (EIS). Sodium dodecyl sulfate (SDS) was used to obtain a good dispersion of CB nanoparticles in a polymer matrix. TEM analysis proved a uniform dispersion of modified CB nanoparticles in epoxy coating. The coatings were subjected to UV radiation to study the degradation behavior and then immersed in 3.5 wt% NaCl. The results showed that the electrochemical behavior of neat epoxy coating was related to the formation and development of microcracks on the surface. The occurrence of microcracks on the surface of the coatings and consequently the penetration of ionic species reduced by adding CB nanoparticles into the formulation of the coatings. CB nanoparticles decreased degradation of CB coatings by absorbing UV irradiation. The ATR-FTIR results showed that decrease in the intensity of methyl group as main peak in presence of 2.5 wt% CB was lower than neat epoxy. In addition, the reduction in impedance of neat epoxy coating under corrosive environment was larger than CB coatings. The CB coating with 2.5 wt% nanoparticles had the highest impedance to corrosive media after 2000 h UV irradiation and 24 h immersion in 3.5 wt% NaCl.

  17. Preparation and characterization of polyhedral oligomer silsesquioxane nanocomposites incorporated in epoxy resin; Elaboracao e caracterizacao de nanocompositos de oligomero poliedrico de silsesquioxano incorporados na resina epoxidica

    Energy Technology Data Exchange (ETDEWEB)

    Longhi, Marielen; Zini, Lucas Pandolphi; Birriel, Eliena Jonko; Kunst, Sandra Raquel; Zattera, Ademir Jose, E-mail: marielen_longhi@hotmail.com [Universidade de Caxias do Sul (LPOL/UCS), RS (Brazil). Laboratorio de Polimeros; Pistor, Vinicius [Universidade Federal do Rio Grande do Sul (UFRGS), Porto Alegre, RS (Brazil)

    2015-07-01

    The incorporation of nanofiller in thermosetting like epoxy resin as has been studied in order to modify its properties. In this research, nanocomposites were obtained by incorporating 5% by weight of three polyhedral oligomeric silsesquioxane (POSS) with different number of functionalization: Glicidilisobutil-POSS, Triglicidilisobutil- POSS and Glicicil POSS in an epoxy matrix by sonification process. The nanocomposites were characterized by analysis of X-ray diffraction (DRX), transmission electron microscopy (TEM) and thermogravimetric analysis (TGA). The DRX analysis showed the characteristic peak of POSS and TEM images showed that there is a difference in the dispersion of nanocages for the difference in the number of epoxy groups on the POSS. The incorporation of Glicidilisobutil-POSS showed a significant increase in the glass transition temperature (Tg) value, and also that the most effective from the viewpoint of the dispersion, on the other hand, the Glycidyl-POSS had a greater influence on the thermal stability demonstrating that the dispersion medium is an important characteristic to define the most desirable properties. (author)

  18. Relationship between the dielectric and mechanical properties and the ratio of epoxy resin to hardener of the hybrid thermosetting polymers

    International Nuclear Information System (INIS)

    Dias Filho, Newton Luiz; Aquino, Hermes Adolfo de; Pires, Geovanna; Caetano, Laercio

    2006-01-01

    The relationship between the dielectric properties (dielectric constant, ε'', and loss factor, ε''; activation energy, E a ) and the ratio of epoxy resin (OG) to hardener of the epoxy resin thermosetting polymers was investigated. The amplitude of the ε'' peak decreases with increasing OG content until about 73 wt.% and slightly increases at higher OG content. The temperature of the position of the ε'' peak increases with the increasing of OG content, reaching maximum values for compositions in the range of 67 and 73 wt.%, and then it decreases sharply at higher OG content. The activation energy obtained from dielectric relaxation increased with increasing wt.% OG up to around 70 wt.%. Further increase in concentration of OG up to 83 wt.% reduced E a . The curves of tensile modulus and fracture (author)

  19. The nanoscale phase distinguishing of PCL-PB-PCL blended in epoxy resin by tapping mode atomic force microscopy

    Science.gov (United States)

    Li, Huiqin; Sun, Limin; Shen, Guangxia; Liang, Qi

    2012-02-01

    In this work, we investigated the bulk phase distinguishing of the poly(ɛ-caprolactone)-polybutadiene-poly(ɛ-caprolactone) (PCL-PB-PCL) triblock copolymer blended in epoxy resin by tapping mode atomic force microscopy (TM-AFM). We found that at a set-point amplitude ratio ( r sp) less than or equal to 0.85, a clear phase contrast could be obtained using a probe with a force constant of 40 N/m. When r sp was decreased to 0.1 or less, the measured size of the PB-rich domain relatively shrank; however, the height images of the PB-rich domain would take reverse (translating from the original light to dark) at r sp = 0.85. Force-probe measurements were carried out on the phase-separated regions by TM-AFM. According to the phase shift angle vs. r sp curve, it could be concluded that the different force exerting on the epoxy matrix or on the PB-rich domain might result in the height and phase image reversion. Furthermore, the indentation depth vs. r sp plot showed that with large tapping force (lower r sp), the indentation depth for the PB-rich domain was nearly identical for the epoxy resin matrix.

  20. In Situ Exfoliation of Graphene in Epoxy Resins: A Facile Strategy to Efficient and Large Scale Graphene Nanocomposites.

    Science.gov (United States)

    Li, Yan; Zhang, Han; Crespo, Maria; Porwal, Harshit; Picot, Olivier; Santagiuliana, Giovanni; Huang, Zhaohui; Barbieri, Ettore; Pugno, Nicola M; Peijs, Ton; Bilotti, Emiliano

    2016-09-14

    Any industrial application aiming at exploiting the exceptional properties of graphene in composites or coatings is currently limited by finding viable production methods for large volumes of good quality and high aspect ratio graphene, few layer graphene (FLG) or graphite nanoplatelets (GNP). Final properties of the resulting composites are inherently related to those of the initial graphitic nanoparticles, which typically depend on time-consuming, resource-demanding and/or low yield liquid exfoliation processes. In addition, efficient dispersion of these nanofillers in polymer matrices, and their interaction, is of paramount importance. Here we show that it is possible to produce graphene/epoxy nanocomposites in situ and with high conversion of graphite to FLG/GNP through the process of three-roll milling (TRM), without the need of any additives, solvents, compatibilisers or chemical treatments. This readily scalable production method allows for more than 5 wt % of natural graphite (NG) to be directly exfoliated into FLG/GNP and dispersed in an epoxy resin. The in situ exfoliated graphitic nanoplatelets, with average aspect ratios of 300-1000 and thicknesses of 5-17 nm, were demonstrated to conferee exceptional enhancements in mechanical and electrical properties to the epoxy resin. The above conclusions are discussed and interpreted in terms of simple analytical models.

  1. 5-year clinical performance of resin composite versus resin modified glass ionomer restorative system in non-carious cervical lesions

    DEFF Research Database (Denmark)

    Franco, Eduardo Batista; Benetti, Ana Raquel; Ishikiriama, Sérgio Kiyoshi

    2006-01-01

    To comparatively assess the 5-year clinical performance of a 1-bottle adhesive and resin composite system with a resin-modified glass ionomer restorative in non-carious cervical lesions.......To comparatively assess the 5-year clinical performance of a 1-bottle adhesive and resin composite system with a resin-modified glass ionomer restorative in non-carious cervical lesions....

  2. Development of sealed radioactive sources immobilized in epoxy resin for verification of detectors used in nuclear medicine

    Energy Technology Data Exchange (ETDEWEB)

    Tiezzi, Rodrigo; Rostelato, Maria Elisa C.M.; Nagatomi, Helio R.; Zeituni, Calos A.; Benega, Marcos A.G.; Souza, Daiane B. de; Costa, Osvaldo L. da; Souza, Carla D.; Rodrigues, Bruna T.; Souza, Anderson S. de; Peleias Junior, Fernando S.; Santos, Rafael Melo dos; Melo, Emerson Ronaldo de, E-mail: rktiezzi@gmail.com [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil); Karan Junior, Dib [Universidade de Sao Paulo (USP), Sao Paulo, SP (Brazil)

    2015-07-01

    The radioactive sealed sources are used in verification ionization chamber detectors, which measure the activity of radioisotopes used in several areas, such as in nuclear medicine. The measurement of the activity of radioisotopes must be made with accuracy, because it is administered to a patient. To ensure the proper functioning of the ionization chamber detectors, standardized tests are set by the International Atomic Energy Agency (IAEA) and the National Nuclear Energy Commission using sealed radioactive sources of Barium-133, Cesium-137 and Cobalt-57. The tests assess the accuracy, precision, reproducibility and linearity of response of the equipment. The focus of this work was the study and the development of these radioactive sources with standard Barium-133, Cesium-137 and Cobalt-57,using a polymer, in case commercial epoxy resin of diglycidyl ether of bisphenol A (DGEBA) and a curing agent based on modified polyamine diethylenetriamine (DETA), to immobilize the radioactive material. The polymeric matrix has the main function of fix and immobilize the radioactive contents not allowing them to leak within the technical limits required by the standards of radiological protection in the category of characteristics of a sealed source and additionally have the ability to retain the emanation of any gases that may be formed during the manufacture process and the useful life of this artifact. The manufacturing process of a sealed source standard consists of the potting ,into bottle standardized geometry, in fixed volume of a quantity of a polymeric matrix within which is added and dispersed homogeneously to need and exact amount in activity of the radioactive materials standards. Accordingly, a study was conducted for the choice of epoxy resin, analyzing its characteristics and properties. Studies and tests were performed, examining the maximum solubility of the resin in water (acidic solution, simulating the conditions of radioactive solution), loss of mechanical

  3. Curing behavior and thermal properties of trifunctional epoxy resin cured by 4, 4’-diaminodiphenyl sulfone

    Directory of Open Access Journals (Sweden)

    2009-08-01

    Full Text Available A novel trifunctional epoxy resin 4-(3, 3-dihydro-7-hydroxy-2, 4, 4-trimethyl-2H-1-benzopyran-2-yl-1, 3-benzenediol glycidyl (shorted as TMBPBTH-EPOXY was synthesized in our lab to improve thermal performance. Its curing behavior and performance were studied by using 4, 4′-diaminodiphenyl sulfone (DDS as hardener with the mass ratio of 100:41 of TMBPBTH-EPOXY and DDS. The curing activation energy was investigated by differential scanning calorimetry (DSC to be 64.0 kJ/mol estimated by Kissinger’s method and 68.7 kJ/mol estimated by Flynn-Wall-Ozawa method respectively. Thermogravimetric analyzer (TGA was used to investigate the thermal decomposition of cured compounds. It was found that when curing temperature was lower than 180°C, the thermal decomposition temperature increased with the rise of curing temperature and curing time. On the other hand, when the curing temperature was higher than 180°C, the thermal decomposition temperature went down instead with the increase of curing time that might be the over-crosslinking of TMBPBTH-EPOXY and DDS hardener. The glass transition temperature (Tg of cured TMBPBTH-EPOXY/DDS compound determined by dynamic mechanical thermal analysis (DMTA is 290.1°C.

  4. Hydrothermal oxidation of an epoxy resin through the study of two model molecules: N-methyl-acetamide and N,N-di[1(phenoxy)2-hydroxy propyl-3] propyl-amine

    International Nuclear Information System (INIS)

    Moutonnet-Fromonteil, C.

    2000-01-01

    The study consists in choosing and developing a technology to realize damage experiments of an epoxy resin which is used as coating of embedded nuclear samples. Hydrothermal oxidation is the chosen method. We first identified the chemical composition of the epoxy resin. Then we studied hydrolysis and oxidation of a molecule which contains a function of the epoxy network: N-methyl-acetamide. The comparison between our results and those already existing allowed to validate this degradation method. In a second part, we studied a model molecule of the polymer network: N, N-di[1(phenoxy)2-hydroxy propyl-3] propyl-amine. The hydrolysis temperatures are relatively high: the compound is totally destroyed at 300 deg C. Its oxidation leads to the formation of acetic acid from 220 deg C. In the third study, we determined the best experimental conditions to destroy the epoxy resin. Experiments were performed at different temperatures between 200 deg C and 410 deg C. The degradation rates are classically defined by amounts of constituents in liquid and gaseous phases. (author)

  5. Physical and Mechanical Characterization of Artificial Stone with Marble Calcite Waste and Epoxy Resin

    OpenAIRE

    Silva, Fernanda Souza; Ribeiro, Carlos Eduardo Gomes; Rodriguez, Rubén Jesus Sánchez

    2017-01-01

    The incorporation of calcite marble waste in epoxy resin for the production of artificial stone can represent a technical-economical method and environmentally viable, reducing the amount of discarded residue in the environment, and adding economic value to marble waste and enabling the generation of jobs. The production of natural stone in Brazil recorded an exorbitant amount of waste generated in marble processing. Only 75% of marble taken from the deposits it becomes the finished product t...

  6. Thermomechanical Behavior of High Performance Epoxy/Organoclay Nanocomposites

    Directory of Open Access Journals (Sweden)

    Artur Soares Cavalcanti Leal

    2014-01-01

    Full Text Available Nanocomposites of epoxy resin containing bentonite clay were fabricated to evaluate the thermomechanical behavior during heating. The epoxy resin system studied was prepared using bifunctional diglycidyl ether of bisphenol A (DGEBA, crosslinking agent diaminodiphenylsulfone (DDS, and diethylenetriamine (DETA. The purified bentonite organoclay (APOC was used in all experiments. The formation of nanocomposite was confirmed by X-ray diffraction analysis. Specimens of the fabricated nanocomposites were characterized by dynamic mechanical analysis (DMA. According to the DMA results a significant increase in glass transition temperature and storage modulus was evidenced when 1 phr of clay is added to epoxy resin.

  7. Structural and electrical properties of functionalized multiwalled carbon nanotube/epoxy composite

    International Nuclear Information System (INIS)

    Gantayat, S.; Rout, D.; Swain, S. K.

    2016-01-01

    The effect of the functionalization of multiwalled carbon nanotube on the structure and electrical properties of composites was investigated. Samples based on epoxy resin with different weight percentage of MWCNTs were prepared and characterized. The interaction between MWCNT & epoxy resin was noticed by Fourier transform infrared spectroscopy (FTIR). The structure of functionalized multiwalled carbon nanotube (f-MWCNT) reinforced epoxy composite was studied by field emission scanning electron microscope (FESEM). The dispersion of f-MWCNT in epoxy resin was evidenced by high resolution transmission electron microscope (HRTEM). Electrical properties of epoxy/f-MWCNT nanocomposites were measured & the result indicated that the conductivity increased with increasing concentration of f-MWCNTs.

  8. Experimental design applied optimization of a state in epoxy clay dispersion

    International Nuclear Information System (INIS)

    Paz, Juliana D'Avila; Bertholdi, Jonas; Folgueras, Marilena Valadares; Pezin, Sergio Henrique; Coelho, Luiz Antonio Ferreira

    2010-01-01

    This paper presents some analysis showed that the exfoliation / intercalation of a montmorillonite clay in epoxy resin such as viscosity, X-ray diffraction (XRD), scanning electron microscopy (SEM) and thermogravimetry (TG). Increasing the viscosity of epoxy resin diglycidyl ether bisphenol A with the addition of clay associated with the sonification system at the time of dispersion is a good indication of exfoliation. The X-ray diffraction already cured composite shows a decrease of crystallinity of clay and EDS microanalysis of SEM, non-uniform dispersion of clay in epoxy resin. Thermal analysis TG composite clay / epoxy shows an increase in thermal stability relative to pure epoxy. (author)

  9. Robust synthesis of epoxy resin-filled microcapsules for application to self-healing materials.

    Science.gov (United States)

    Bolimowski, Patryk A; Bond, Ian P; Wass, Duncan F

    2016-02-28

    Mechanically and thermally robust microcapsules containing diglycidyl ether bisphenol A-based epoxy resin and a high-boiling-point organic solvent were synthesized in high yield using in situ polymerization of urea and formaldehyde in an oil-in-water emulsion. Microcapsules were characterized in terms of their size and size distribution, shell surface morphology and thermal resistance to the curing cycles of commercially used epoxy polymers. The size distribution of the capsules and characteristics such as shell thickness can be controlled by the specific parameters of microencapsulation, including concentrations of reagents, stirrer speed and sonication. Selected microcapsules, and separated core and shell materials, were analysed using thermogravimetric analysis and differential scanning calorimetry. It is demonstrated that capsules lose minimal 2.5 wt% at temperatures no higher than 120°C. These microcapsules can be applied to self-healing carbon fibre composite structural materials, with preliminary results showing promising performance. © 2016 The Author(s).

  10. Measurement of glass transition temperature, residual heat of reaction and mixing ratio of epoxy resins using near infrared spectroscopy: a preliminary study

    DEFF Research Database (Denmark)

    Houmøller, Lars Plejdrup; Laursen, Peter Clemen

    2003-01-01

    As a measure of the degree of curing of epoxy resins, the glass transition temperature, Tg, and the residual heat of reaction, DeltaHr, are often used. In this study, near infrared spectroscopy and multivariate calibration (partial least squares regression (PLSR)) have been used to monitor the two...... variables, using differential scanning calorimetry (DSC) as the reference method. The epoxy under study was a commercial system consisting of the resin, trimethylolpropanetriglycidylether, and the hardener, 3-aminomethyl-3,5,5,-trimethylcyclohexylamine. Using samples cured under different conditions......, calibrations resulted in root mean square errors of cross-validation (RMSECV) of 18 J/g for DeltaHr (range for Hr: 6.1-231.3 J/g) and 7.2ºC for Tg (range for Tg: 41.5-98.8ºC). Also, a PLSR model for mixing ratio of hardener and resin was obtained, resulting in a RMSECV of 0.0040 (range for mixing ratio: 0.180-0.380)...

  11. Relationship between the dielectric and mechanical properties and the ratio of epoxy resin to hardener of the hybrid thermosetting polymers

    Energy Technology Data Exchange (ETDEWEB)

    Dias Filho, Newton Luiz; Aquino, Hermes Adolfo de; Pires, Geovanna; Caetano, Laercio [UNESP, Ilha Solteira, SP (Brazil). Faculdade de Engenharia. Dept. de Fisica e Quimica]. E-mail: nldias@dfq.feis.unesp.br

    2006-05-15

    The relationship between the dielectric properties (dielectric constant, {epsilon}'', and loss factor, {epsilon}''; activation energy, E{sub a}) and the ratio of epoxy resin (OG) to hardener of the epoxy resin thermosetting polymers was investigated. The amplitude of the {epsilon}'' peak decreases with increasing OG content until about 73 wt.% and slightly increases at higher OG content. The temperature of the position of the {epsilon}'' peak increases with the increasing of OG content, reaching maximum values for compositions in the range of 67 and 73 wt.%, and then it decreases sharply at higher OG content. The activation energy obtained from dielectric relaxation increased with increasing wt.% OG up to around 70 wt.%. Further increase in concentration of OG up to 83 wt.% reduced E{sub a}. The curves of tensile modulus and fracture (author)

  12. Comparison of tensile strength of different carbon fabric reinforced epoxy composites

    Directory of Open Access Journals (Sweden)

    Jane Maria Faulstich de Paiva

    2006-03-01

    Full Text Available Carbon fabric/epoxy composites are materials used in aeronautical industry to manufacture several components as flaps, aileron, landing-gear doors and others. To evaluate these materials become important to know their mechanical properties, for example, the tensile strength. Tensile tests are usually performed in aeronautical industry to determinate tensile property data for material specifications, quality assurance and structural analysis. For this work, it was manufactured four different laminate families (F155/PW, F155/HS, F584/PW and F584/HS using pre-impregnated materials (prepregs based on F155TM and F584TM epoxy resins reinforced with carbon fiber fabric styles Plain Weave (PW and Eight Harness Satin (8HS. The matrix F155TM code is an epoxy resin type DGEBA (diglycidil ether of bisphenol A that contains a curing agent and the F584TM code is a modified epoxy resin type. The laminates were obtained by handing lay-up process following an appropriate curing cycle in autoclave. The samples were evaluated by tensile tests according to the ASTM D3039. The F584/PW laminates presented the highest values of tensile strength. However, the highest modulus results were determined for the 8HS composite laminates. The correlation of these results emphasizes the importance of the adequate combination of the polymeric matrix and the reinforcement arrangement in the structural composite manufacture. The microscopic analyses of the tested specimens show valid failure modes for composites used in aeronautical industry.

  13. Environmental Factors Affecting the Strength Characteristics of Modified Resin Mortars

    Science.gov (United States)

    Debska, Bernardeta; Licholai, Lech

    2017-12-01

    Resin concretes are composites in which a cement binder has been completely replaced by a synthetic resin. These materials are a good choice for the construction industry, especially in solutions requiring high strength, fast curing and durability. Polymer mortars are mainly used for the manufacture of industrial floors and prefabricated products such as tanks for aggressive chemicals, sewage pipes, or road and bridge drainage systems, as well as for the repair of damaged concrete structures. In all these applications, the strength and high chemical resistance of the applied material solutions are of key importance. It is particularly crucial to obtain information on how resin composites behave when exposed to aggressive agents over extended periods of time. It is also very important to use waste materials in order to obtain resin composites, as these activities are very well inscribed in the idea of environmental protection and meet the criteria of sustainable construction. The mortars described in this article meet the above principles. The article presents how the compressive strength of glycolyzate-modified epoxy mortars, obtained with the use of poly(ethylene terephthalate), changes after they are immersed in 10% sodium chloride solution. Sodium chloride solution was chosen due to the prospective applicability of the tested composites as repair materials used for e.g. bridges or overpasses that are exposed to this salt solution in wintertime. Changes in the properties of the composite samples were monitored over the period of one year. Statistical analysis of the test results was carried out with the use of Statistica programme. The module available in the mentioned program called Nonparametric Statistics - Comparing multiple independent samples made it possible to check the monitoring times during which the compressive strength values differed significantly. The obtained results allowed for determining the equation of the function approximating the course of

  14. Neutron shielding material based on colemanite and epoxy resin

    International Nuclear Information System (INIS)

    Okuno, K.

    2005-01-01

    In recent years, there has been a need for compact shielding design such as self-shielding of a PET cyclotron or up-gradation of radiation machinery in existing facilities. In these cases, high performance shielding materials are needed. Concrete or polyethylene have been used for a neutron shield. However, for compact shielding, they fall short in terms of performance or durability. Therefore, a new type of neutron shielding material based on epoxy resin and colemanite has been developed. Slab attenuation experiments up to 40 cm for the new shielding material were carried out using a 252 Cf neutron source. Measurement was carried out using a REM-counter, and compared with calculation. The results show that the shielding performance is better than concrete and polyethylene mixed with 10 wt% boron oxide. From the result, we confirmed that the performance of the new material is suitable for practical use. (authors)

  15. Preparation and characterization of hybrid materials of epoxy resin type bisphenol a with silicon and titanium oxides by sol-gel process

    International Nuclear Information System (INIS)

    Carrillo C, A.; Osuna A, J. G.

    2011-01-01

    Hybrid materials were synthesized from epoxy resins as a result bisphenol type A-silicon oxide and epoxy resin bisphenol type A-titanium oxide were obtained. The synthesis was done by sol-gel process using tetraethyl orthosilicate (Teos) and titanium isopropoxide (I Ti) as inorganic precursors. The molar ratio of bisphenol A to the inorganic precursors was the studied variable. The materials were characterized by thermal analysis, infrared spectroscopy, scanning electron microscopy and energy dispersive X-ray spectroscopy. The hybrid nature of the materials was demonstrated through thermal analysis and infrared spectroscopy. In both systems, as the amount of alkoxide increased, the bands described above were more defined. This behavior indicates the interactions between the resin and the alkoxides. Hybrids with Teos showed a smoother and homogeneous surface in its entirety, without irregularities. Hybrids with titanium isopropoxide had low roughness. Both Teos and I Ti hybrids showed a decrease on the atomic weight percentage of carbon due to a slight reduction of the organic part on the surface. (Author)

  16. Preparation and characterization of hybrid materials of epoxy resin type bisphenol a with silicon and titanium oxides by sol-gel process

    Energy Technology Data Exchange (ETDEWEB)

    Carrillo C, A.; Osuna A, J. G., E-mail: acc.carrillo@gmail.com [Universidad Autonoma de Coahuila, Facultad de Ciencias Quimicas, Blvd. Venustiano Carranza y Jose Cardenas Valdes, 25000 Saltillo, Coahuila (Mexico)

    2011-07-01

    Hybrid materials were synthesized from epoxy resins as a result bisphenol type A-silicon oxide and epoxy resin bisphenol type A-titanium oxide were obtained. The synthesis was done by sol-gel process using tetraethyl orthosilicate (Teos) and titanium isopropoxide (I Ti) as inorganic precursors. The molar ratio of bisphenol A to the inorganic precursors was the studied variable. The materials were characterized by thermal analysis, infrared spectroscopy, scanning electron microscopy and energy dispersive X-ray spectroscopy. The hybrid nature of the materials was demonstrated through thermal analysis and infrared spectroscopy. In both systems, as the amount of alkoxide increased, the bands described above were more defined. This behavior indicates the interactions between the resin and the alkoxides. Hybrids with Teos showed a smoother and homogeneous surface in its entirety, without irregularities. Hybrids with titanium isopropoxide had low roughness. Both Teos and I Ti hybrids showed a decrease on the atomic weight percentage of carbon due to a slight reduction of the organic part on the surface. (Author)

  17. Behavior study of spend ion exchange resins immobilized in pyrolyzed polymer matrix

    International Nuclear Information System (INIS)

    Ramos, P.B; Fuentes, N.O; Luca, V.

    2012-01-01

    The pyrolysis of spent ion exchange resins contained in epoxy resins represents an attractive alternative to cementation as a confining method. In this sense, a significant reduction of volume can be achieved, as well as avoiding the dispersion of the exhausted ion exchange resin by the means of an epoxy resin used as a matrix, while potentially limiting the release of highly radioactive long life isotopes such us Cs-137, Sr-90 and Co-60 among others. Three types of monoliths were made: (i) epoxy resin, (ii) epoxy resin with carbon and (iii) a binder of epoxy resin and clay. In every case, the monolith contained the ion exchange resin. They were prepared by the mixing of resin pearl loaded with epoxy cations and a subsequent pyrolysis process with a temperature increase ratio of 2 o C /min reaching maximum values in the range between 200 o C - 800 o C, remaining in it for 1 hour. Monoliths obtained for each final temperature had been characterized to obtain data corresponding to the mass loss, volume reduction and lixiviation, as well as mechanical and microstructural properties (author)

  18. Processing of intractable polymers using reactive solvents: 1. Poly(2,6-dimethyl-1,4-phenylene ether)/epoxy resin

    NARCIS (Netherlands)

    Venderbosch, R.W.; Meijer, H.E.H.; Lemstra, P.J.

    1994-01-01

    A new processing route for poly(2,6-dimethyl-1,4-phenylene ether) (PPE), an intractable polymer on account of its thermal and oxidative sensitivity, was explored. PPE can be dissolved at elevated temperatures in epoxy resin and these solutions can then be processed at temperatures as low as 175°C.

  19. Voltage-Induced Nonlinear Conduction Properties of Epoxy Resin/Micron-Silver Particles Composites

    Science.gov (United States)

    Qu, Zhaoming; Lu, Pin; Yuan, Yang; Wang, Qingguo

    2018-01-01

    The nonlinear conduction properties of epoxy resin (ER)/micron-silver particles (MP) composites were investigated. Under sufficient high intensity applied constant voltage, the obvious nonlinear conduction properties of the samples with volume fraction 25% were found. With increments in the voltage, the conductive switching effect was observed. The nonlinear conduction mechanism of the ER/MP composites under high applied voltages could be attributed to the electrical current conducted via discrete paths of conductive particles induced by the electric field. The test results show that the ER/MP composites with nonlinear conduction properties are of great potential application in electromagnetic protection of electron devices and systems.

  20. Colorless triphenylamine-based aliphatic thermoset epoxy for multicolored and near-infrared electrochromic applications.

    Science.gov (United States)

    Chuang, Ya-Wen; Yen, Hung-Ju; Wu, Jia-Hao; Liou, Guey-Sheng

    2014-03-12

    In this study, two novel colorless thermoset epoxy resins with anodically electrochromism were prepared from the thermal curing of two triphenylamine-based diamine monomers, 4,4'-diamino-4″-methoxytriphenylamine (1) and N,N'-bis(4-aminophenyl)-N,N'-di(4-methoxylphenyl)-1,4-phenylenediamine (2) with aliphatic epoxy triglycidyl isocyanurate, respectively. The resulting thermoset epoxy resins showed excellent softening temperature (Ts, 270 and 280 °C) due to the rigid structure and highly crosslinking density. In addition, novel colorless epoxy resin films revealed good reversible electrochemical oxidation and interesting multi-electrochromic behavior with high contrast ratio both in visible and near-infrared regions. The aliphatic thermoset epoxy resins also exhibited high transparency in visible region as colorless and great potential for practical electrochromic applications.

  1. Relationship Between the Process Parameters and Resin Content of a Glass/Epoxy Prepreg Produced by Dipping Method

    Directory of Open Access Journals (Sweden)

    Hamid Reza Khalafi

    2015-02-01

    Full Text Available The properties of prepregs are characterized in terms of their volatile content, resin content, the degree of pre-cure, void content, tack and flow ability. Resin content is one of the most important properties of prepregs so that its changing will result in altered properties such as, tack and resin flow. In order to monitor the resin content, a quantitative relation to the processing parameters such as line speed, viscosity and distance between the resin up taking rollers have to be determined. In this study, a tri-axial E-glass fabric with the areal weight of 1025 g/m2 and an epoxy resin (Epon 828 were used to produce the prepreg by the dipping method. In the theoretical part of this work, the free coating is studied and as a result the thickness layer of the coating resin through the resin bath is calculated by Landau-Levich model. In continuation, the achieved thickness was considered as a feed for the calendering process. Using the momentum equation for the passing impregnated fibres through the extra resin uptake rollers, the relation between the internal resin layer thickness and final coating resin layer thickness was achieved in an integral equation form. In order to solve this integral equation, MAPLE software was applied. The theoretical results were in good agreement with the experimental data and showed that the resin content increased linearly with increasing the distance between rollers, the radius and roller angular velocity. In contrast, the resin content decreased with increasing the line speed. According to our calculations, the effect of the resin viscosity variation on the resin content was negligibly small.

  2. Contact allergy to epoxy (meth)acrylates.

    Science.gov (United States)

    Aalto-Korte, Kristiina; Jungewelter, Soile; Henriks-Eckerman, Maj-Len; Kuuliala, Outi; Jolanki, Riitta

    2009-07-01

    Contact allergy to epoxy (meth)acrylates, 2,2-bis[4-(2-hydroxy-3-methacryloxypropoxy) phenyl]propane (bis-GMA), 2,2-bis[4-(2-hydroxy-3-acryloxypropoxy)phenyl]-propane (bis-GA), 2,2-bis[4-(methacryl-oxyethoxy)phenyl] propane (bis-EMA), 2,2-bis[4-(methacryloxy)phenyl]-propane (bis-MA), and glycidyl methacrylate (GMA) is often manifested together with contact allergy to diglycidyl ether of bisphenol A (DGEBA) epoxy resin. To analyse patterns of concomitant allergic reactions to the five epoxy (meth)acrylates in relation to exposure. We reviewed the 1994-2008 patch test files at the Finnish Institute of Occupational Health (FIOH) for reactions to the five epoxy (meth)acrylates, and examined the patients' medical records for exposure. Twenty-four patients had an allergic reaction to at least one of the studied epoxy (meth)acrylates, but specific exposure was found only in five patients: two bis-GMA allergies from dental products, two bis-GA allergies from UV-curable printing inks, and one bis-GA allergy from an anaerobic glue. Only 25% of the patients were negative to DGEBA epoxy resin. The great majority of allergic patch test reactions to bis-GMA, bis-GA, GMA and bis-EMA were not associated with specific exposure, and cross-allergy to DGEBA epoxy resin remained a probable explanation. However, independent reactions to bis-GA indicated specific exposure. Anaerobic sealants may induce sensitization not only to aliphatic (meth)acrylates but also to aromatic bis-GA.

  3. Study on the pyrolysis of phenol-formaldehyde (PF) resin and modified PF resin

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Jigang, E-mail: wangjigang@seu.edu.cn [Jiangsu Key Laboratory of Advanced Metallic Materials, School of Materials Science and Engineering, Southeast University, Nanjing 211189 (China); Jiang, Haiyun [Jiangsu Key Laboratory of Advanced Metallic Materials, School of Materials Science and Engineering, Southeast University, Nanjing 211189 (China); School of Materials Science and Engineering, Southeast University, Nanjing Institute of Technology, Nanjing 210013 (China); Jiang, Nan [Institute of Theoretical and Computational Chemistry, Nanjing University, Nanjing 210093 (China)

    2009-12-10

    The pyrolysis of pure phenol-formaldehyde (PF) resin and boron carbide (B{sub 4}C) modified PF resin was investigated by using thermogravimetry (TG) and pyrolysis gas-chromatography-mass-spectrometry (PY-GC/MS). Scanning electron microscope (SEM) and Fourier transform infrared (FT-IR) spectroscopy were also employed to investigate the micro-structural evolution. It was shown from the TG analysis that the char residues of pure PF resin were 62.9 and 60.5% after being pyrolyzed at 700 and 1000 {sup o}C, respectively. The degradation and failure of the resin matrix were mainly resulted from the release of volatiles. The phenol and its methyl derivates took a large proportion in the amount of volatiles. In comparison with the pure PF resin, the char residues of B{sub 4}C modified PF resin were obviously higher, with the values of 71.9 and 68.4% at 700 and 1000 {sup o}C, respectively. Due to the oxidation-reduction reactions between B{sub 4}C additive and oxygen-containing volatiles including CO and H{sub 2}O, partial carbon and oxygen elements in the volatiles remained in the resin matrix in the forms of amorphous carbon and B{sub 2}O{sub 3}, respectively. The results of SEM and FT-IR characterization demonstrated the occurrence of the modification, and the amorphous carbon existed in the form of reticular substance. In addition, the amount of the released phenol and its methyl derivates was also decreased drastically due to the formation of borate.

  4. Synthesis of polyoxometalate-loaded epoxy composites

    Science.gov (United States)

    Anderson, Benjamin J

    2014-10-07

    The synthesis of a polyoxometalate-loaded epoxy uses a one-step cure by applying an external stimulus to release the acid from the polyoxometalate and thereby catalyze the cure reaction of the epoxy resin. Such polyoxometalate-loaded epoxy composites afford the cured epoxy unique properties imparted by the intrinsic properties of the polyoxometalate. For example, polyoxometalate-loaded epoxy composites can be used as corrosion resistant epoxy coatings, for encapsulation of electronics with improved dielectric properties, and for structural applications with improved mechanical properties.

  5. Microstructure aspects of radiation-cured networks: Cationically polymerized aromatic epoxy resins

    Science.gov (United States)

    Kowandy, Christelle; Ranoux, Guillaume; Walo, Marta; Vissouvanadin, Bertrand; Teyssedre, Gilbert; Laurent, Christian; Berquand, Alexandre; Molinari, Michaël; Coqueret, Xavier

    2018-02-01

    The thermo-mechanical properties and nanostructural features of epoxy aromatic resins cationically cured by UV-visible or electron beam radiation have been studied by FT-NIR spectroscopy, dynamic mechanical analysis (DMA), dielectric spectroscopy (DS), and atomic force microscopy (AFM). The influence of formulation (nature and content of onium salt) and of curing parameters (doses, thermal treatment) on the thermophysical have been investigated. The presence of several relaxation domains observed by DMA and DS analysis confirms the presence of heterogeneities in the cured materials. Network formation is described by the percolation of glassy nanoclusters which are evidenced by AFM analyses. AFM probing by quantitative nanomechanical measurements confirms the gradual build-up of the local Young's modulus in good agreement with the macroscopic value.

  6. Nuclear characteristics of epoxy resin as a space environment neutron shielding

    Energy Technology Data Exchange (ETDEWEB)

    Adeli, Ruhollah [Nuclear Science and Technology Research Institute, Yazd (Iran, Islamic Republic of). Central Iran Research Complex; Shirmardi, Seyed Pezhman [Nuclear Science and Technology Research Institute, Tehran (Iran, Islamic Republic of). Radiation Application Research School; Mazinani, Saideh [Amirkabir Nanotechnology Research Institute, Tehran (Iran, Islamic Republic of); Ahmadi, Seyed Javad [Nuclear Science and Technology Research Institute, Tehran (Iran, Islamic Republic of). Nuclear Fuel Cycle Research School

    2017-03-15

    In recent years many investigations have been done for choosing applicable light neutron shielding in space environmental applications. In this study, we have considered the neutron radiation-protective characteristics of neat epoxy resin, a thermoplastic polymer material and have compared it with various candidate materials in neutron radiation protection such as Al 6061 alloy and Polyethylene. The aim of this investigation is the effect of type of moderator for fast neutron, notwithstanding neutron absorbers fillers. The nuclear interactions and the effective dose at shields have been studied with the Monte Carlo N-Particle transport code (MCNP), using variance reductions to reduce the relative error. Among the candidates, polymer matrix showed a better performance in attenuating fast neutrons and caused a lower neutron and secondary photon effective dose.

  7. Mechanical Property Analysis on Sandwich Structured Hybrid Composite Made from Natural Fibre, Glass Fibre and Ceramic Fibre Wool Reinforced with Epoxy Resin

    Science.gov (United States)

    Bharat, K. R.; Abhishek, S.; Palanikumar, K.

    2017-06-01

    Natural fibre composites find wide range of applications and usage in the automobile and manufacturing industries. They find lack in desired properties, which are required for present applications. In current scenario, many developments in composite materials involve the synthesis of Hybrid composite materials to overcome some of the lacking properties. In this present investigation, two sandwich structured hybrid composite materials have been made by reinforcing Aloe Vera-Ceramic Fibre Wool-Glass fibre with Epoxy resin matrix and Sisal fibre-Ceramic Fibre Wool-Glass fibre with Epoxy resin matrix and its mechanical properties such as Tensile, Flexural and Impact are tested and analyzed. The test results from the two samples are compared and the results show that sisal fibre reinforced hybrid composite has better mechanical properties than aloe vera reinforced hybrid composite.

  8. Thermal conductivity and Kapitza resistance of epoxy resin fiberglass tape at superfluid helium temperature

    Science.gov (United States)

    Baudouy, B.; Polinski, J.

    2009-03-01

    The system of materials composed of fiberglass epoxy resin impregnated tape constitutes in many cases the electrical insulation for "dry"-type superconducting accelerator magnet such as Nb 3Sn magnets. Nb 3Sn magnet technology is still under development in a few programs to reach higher magnetic fields than what NbTi magnets can produce. The European program, Next European Dipole (NED), is one of such programs and it aims to develop and construct a 15 T class Nb 3Sn magnet mainly for upgrading the Large Hardron Collider. Superfluid helium is considered as one possible coolant and since the magnet has been designed with a "dry" insulation, the thermal conductivity and the Kapitza resistance of the electrical insulation are the key properties that must be know for the thermal design of such a magnet. Accordingly, property measurements of the epoxy resin fiberglass tape insulation system developed for the NED project was carried out in superfluid helium. Four sheets with thicknesses varying from 40 to 300 μm have been tested in a steady-state condition. The determined thermal conductivity, k, is [(25.8 ± 2.8) · T - (12.2 ± 4.9)] × 10 -3 W m -1 K -1 and the Kapitza resistance is given by R K = (1462 ± 345) · T(-1.86 ± 0.41) × 10 -6 Km 2 W -1 in the temperature range of 1.55-2.05 K.

  9. Non-isothermal cure and exfoliation of tri-functional epoxy-clay nanocomposites

    Directory of Open Access Journals (Sweden)

    F. Shiravand

    2015-08-01

    Full Text Available The non-isothermal cure kinetics of polymer silicate layered nanocomposites based on a tri-functional epoxy resin has been investigated by differential scanning calorimetry. From an analysis of the kinetics as a function of the clay content, it can be concluded that the non-isothermal cure reaction can be considered to consist of four different processes: the reaction of epoxy groups with the diamine curing agent; an intra-gallery homopolymerisation reaction which occurs concurrently with the epoxy-amine reaction; and two extra-gallery homopolymerisation reactions, catalysed by the onium ion of the organically modified clay and by the tertiary amines resulting from the epoxy-amine reaction. The final nanostructure displays a similar quality of exfoliation as that observed for the isothermal cure of the same nanocomposite system. This implies that the intra-gallery reaction, which is responsible for the exfoliation, is not significantly inhibited by the extra-gallery epoxy-amine cross-linking reaction.

  10. Effect of silica concentration on electrical conductivity of epoxy resin-carbon black-silica nanocomposites

    International Nuclear Information System (INIS)

    Zhang Wei; Blackburn, Richard S.; Dehghani-Sanij, Abbas A.

    2007-01-01

    Electrical properties of nanocomposites are determined by the conductive paths of carbon black and influenced by a 'network' of silica. With increasing content of silica, carbon black (CB) particles are optimally dispersed, contributing to the generation of a conductive network between CB particles via direct particle contact and a tunneling effect; maximum conductivity for the epoxy resin-CB-silica nanocomposite described herein occurs at a ratio of 0.6:1.0 (SiO 2 :CB). As a non-conductive component, excessive silica will prevent electron flow, giving rise to low conductivity

  11. New experimental and analytical results for diffusion and swelling of resins used in graphite/epoxy composite materials

    Science.gov (United States)

    Hiel, C. C.; Adamson, M. J.

    1986-01-01

    The epoxy resins currently in use can slowly absorb moisture from the atmosphere over a long period. This reduces those mechanical properties of composites which depend strongly on the matrix, such as compressive strength and buckling instabilities. The effect becomes greater at elevated temperatures. The paper will discuss new phenomena which occur under simultaneous temperature and moisture variations. An analytical model will also be discussed and documented.

  12. Studies on preparation and properties of the multi-walled carbon nanotubes (MWNTs)/epoxy nanocomposites

    International Nuclear Information System (INIS)

    Deng Huayang; Cao Qi; Wang Xianyou; Chen Quanqi; Kuang Hao; Wang Xiaofeng

    2011-01-01

    Highlights: → We use the modified MWNTs as fillers fabricated epoxy nanocomposites. → The mechanical, thermal and dielectric properties of nanocomposites are measured. → The nanocomposites exhibited better mechanical and dielectric properties. - Abstract: The MWNTs were coated with polyaniline (PANI) by in situ chemical oxidation polymerization method. FTIR spectroscopy, scanning electron microscope (SEM) and X-ray diffraction (XRD) indicated that the MWNTs were coated with PANI. The MWNTs/epoxy nanocomposites were fabricated by using the solution blending method. Differential scanning calorimetry (DSC), tensile testing, HP 4294A impedance analyzer and SEM were used to investigate the properties of the nanocomposites. The results showed that the modified carbon nanotubes were well dispersed in the polymer matrix. The nanocomposites have enhancements in mechanical, thermal and dielectric properties compare with the neat epoxy resin. The nanocomposites were proven to be a good polymer dielectric material.

  13. Evolution of the macroscopic properties of two epoxy resins during ageing under irradiation

    International Nuclear Information System (INIS)

    Vignoud, L.

    2001-11-01

    In this study, the thermomechanical properties of two epoxy resins (DGEBA/TETA and DGEBA/DDM systems) are analysed as a function of the irradiation dose. The maximum conversion and reticulation is obtained by post-curing treatment. Irradiation by electrons results in a decrease of the glass transition temperature and of the elastic modulus in the rubbery region. These results can be interpreted invoking a destruction of the crosslinks and chains breaks within the resin. The Arrhenius diagrams obtained for the various doses shows that the cooperative mobility associated with the α relaxation becomes faster after the irradiation. On the contrary, more local mobility corresponding to the γ relaxation is also modified, but in a lesser extent. The stress-strain curves are also discussed. In uniaxial compression test, the plastic flow stress σ p decreases when the irradiation dose increases and this effect can largely be accounted for by a variation of T g . Post-irradiative effects are studied in inert atmosphere. Reticulation increases when the material is heated to a higher temperature than its T g . This effect suggest the presence of radical formed during irradiation. For DGEBA/TETA system, glass transition temperature T g shifts towards lowest temperatures. This shift increases the molecular mobility and enhances the physical ageing process at the ambient temperature. The results are well described by the quasi point defects theory. Direct effect of irradiation and physical ageing evolve with the scale parameter t 0 . This parameter characterizes the gap (in time and/or temperature) between the principal relaxation and simplest ones. By connecting t 0 to the amount of irradiation, it is possible to predict the modifications of the behaviour and to predict these evolutions for various amounts. (author)

  14. Study of the reaction between polyethylene glycol and epoxy resins using N,N-dimethylbenzylamine as catalyst

    International Nuclear Information System (INIS)

    Zacharuk, Mario; Coelho, Luiz A.F.; Pezzin, Sergio H.; Becker, Daniela

    2009-01-01

    In this work the use of N,N-dimethylbenzylamine as a catalyst of the reaction of polyethylene glycol (PEG) and epoxy resin (DGEBA) was studied. The reaction products were evaluated by infra-red spectroscopy (FTIR), nuclear magnetic resonance spectroscopy (NMR) and viscosity measurements. Samples cured with a polyamine-based hardener were also submitted to tensile tests and differential scanning calorimetry (DSC). The results of the viscosity analyses, FTIR and RMN ( 1 H) had confirmed the occurrence of the reaction between DGEBA epoxy groups and PEG hydroxyl groups in the presence of N, N-dimethylbenzylamine as catalyst, at 100 deg C. DSC analyses and tensile tests of cured systems showed that the reaction of DGEBA with PEG leads to a reduction of the Tg, generating a more flexible material. (author)

  15. Isothermal and non-isothermal cure of a tri-functional epoxy resin (TGAP): a stochastic TMDSC study

    OpenAIRE

    Hutchinson, John M.; Shiravand, Fatemeh; Calventus Solé, Yolanda; Fraga Rivas, Iria

    2012-01-01

    The isothermal cure of a highly reactive tri-functional epoxy resin, tri-glycidyl para-amino phenol (TGAP), with diamino diphenyl sulphone (DDS), at two different cure temperatures Tc has been studied by both conventional differential scanning calorimetry (DSC) and by a stochastic temperature modulated DSC technique, TOPEM. From a series of isothermal cure experiments for increasing cure times, the glass transition temperature Tg as a function of isothermal cure time is determined by co...

  16. Flame retardancy and thermal properties of epoxy acrylate resin/alpha-zirconium phosphate nanocomposites used for UV-curing flame retardant films

    International Nuclear Information System (INIS)

    Xing Weiyi; Jie Ganxin; Song Lei; Wang Xin; Lv Xiaoqi; Hu Yuan

    2011-01-01

    This paper reported the UV-curing flame retardant film, which consisted of epoxy acrylate resin (EA) used as an oligomer, tri(acryloyloxyethyl) phosphate (TAEP) and triglycidyl isocyanurate acrylate (TGICA) used as flame retardant (FR). The flame retardancy and thermal properties of films were reinforced by using alpha-zirconium phosphate (α-Zr (HPO 4 ) 2 H 2 O, α-ZrP). The morphology of nanocomposite film was characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results showed that the organophilic α-ZrP (OZrP) layers were dispersed well in epoxy acrylate resin. Microscale Combustion Calorimeter (MCC), thermogravimetric analysis (TGA) and thermogravimetric analysis/infrared spectrometry (TGA-IR) were used to characterize the flame retardant property and thermal stability. It was found that the incorporation of TAEP and TGICA can reduce the flammability of EA. Moreover, further reductions were observed due to the addition of OZrP. The char residue for systems with or without OZrP was also explored by scanning electron microscopy (SEM).

  17. Synthesis of Polyurethane/Silica Modified Epoxy Polymer Based on 1,3-Propanediol for Coating Application

    Directory of Open Access Journals (Sweden)

    Lutviasari Nuraini

    2017-11-01

    Full Text Available Studies on the synthesis of polyurethane/silica modified epoxy polymer using 1,3-propanediol has been conducted. Synthesis of polymers made by reaction of tolonate and 1,3-propanediol (ratio NCO/OH=2.5 as the building blocks of polyurethane with diglycidyl ether bisphenol A (DGEBA epoxy and catalyst dibutyltin dilaurate (DBTL.The total weight of the polyurethane used was 20% (w/w of the total epoxy. Based on Fourier Transform Infrared (FTIR and 1H-Nuclear Magnetic Resonance (1H-NMR spectra indicated the existence of a new bond that is formed from the reaction of isocyanate group and hydroxyl group, where the hydroxyl groups derived from epoxy and 1,3-propanediol. The addition of silica (5, 10, and 15% w/w to epoxy into the epoxy-modified polyurethane has been carried out through sol-gel reaction of tetraethyl orthosilicate (TEOS. The isocyanate conversion rate for the addition of silica 5, 10, and 15% are 95.69; 100, and 100%, respectively. The morphology and element identification by Scanning Electron Microscopy/Energy Dispersive X-Ray Analysis (SEM/EDX, showed that Si element has been successfully added in the polymer. From the tensile strength and elongation analysis, also thermal stability analysis using Thermal Gravimetric Analyzer (TGA, the increase of silica amount into the polyurethane modified epoxy did not significantly affect to thermal properties, but decrease the tensile strength of the polymer.

  18. Corrosion study of the graphene oxide and reduced graphene oxide-based epoxy coatings

    Science.gov (United States)

    Ghauri, Faizan Ali; Raza, Mohsin Ali; Saad Baig, Muhammad; Ibrahim, Shoaib

    2017-12-01

    This work aims to determine the effect of graphene oxide (GO) and reduced graphene oxide (rGO) incorporation as filler on the corrosion protection ability of epoxy coatings in saline media. GO was derived from graphite powder following modified Hummers’ method, whereas rGO was obtained after reduction of GO with hydrazine solution. About 1 wt.% of GO or rGO were incorporated in epoxy resin by solution mixing process followed by ball milling. GO and rGO-based epoxy composite coatings were coated on mild steel substrates using film coater. The coated samples were characterized by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization tests after 1 and 24 h immersion in 3.5% NaCl. The results suggested that GO-based epoxy composite coatings showed high impedance and low corrosion rate.

  19. High Tg and fast curing epoxy-based anisotropic conductive paste for electronic packaging

    Science.gov (United States)

    Keeratitham, Waralee; Somwangthanaroj, Anongnat

    2016-03-01

    Herein, our main objective is to prepare the fast curing epoxy system with high glass transition temperature (Tg) by incorporating the multifunctional epoxy resin into the mixture of diglycidyl ether of bisphenol A (DGEBA) as a major epoxy component and aromatic diamine as a hardener. Furthermore, the curing behavior as well as thermal and thermomechanical properties were investigated by differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA) and thermomechanical analysis (TMA). It was found that Tg obtained from tan δ of DGEBA/aromatic diamine system increased from 100 °C to 205 °C with the presence of 30 percentage by weight of multifunctional epoxy resin. Additionally, the isothermal DSC results showed that the multifunctional epoxy resin can accelerate the curing reaction of DGEBA/aromatic diamine system. Namely, a high degree of curing (˜90%) was achieved after a few minutes of curing at low temperature of 130 °C, owing to a large number of epoxy ring of multifunctional epoxy resin towards the active hydrogen atoms of aromatic diamine.

  20. Effect of Montmorillonite Nanogel Composite Fillers on the Protection Performance of Epoxy Coatings on Steel Pipelines.

    Science.gov (United States)

    Atta, Ayman M; El-Saeed, Ashraf M; Al-Lohedan, Hamad A; Wahby, Mohamed

    2017-06-02

    Montmorillonite (MMT) clay mineral is widely used as filler for several organic coatings. Its activity is increased by exfoliation via chemical modification to produce nanomaterials. In the present work, the modification of MMT to form nanogel composites is proposed to increase the dispersion of MMT into epoxy matrices used to fill cracks and holes produced by the curing exotherms of epoxy resins. The dispersion of MMT in epoxy improved both the mechanical and anti-corrosion performance of epoxy coatings in aggressive marine environments. In this respect, the MMT surfaces were chemically modified with different types of 2-acrylamido-2-methyl propane sulfonic acid (AMPS) nanogels using a surfactant-free dispersion polymerization technique. The effect of the chemical structure, nanogel content and the interaction with MMT surfaces on the surface morphology, surface charges and dispersion in the epoxy matrix were investigated for use as nano-filler for epoxy coatings. The modified MMT nanogel epoxy composites showed excellent resistance to mechanical damage and salt spray resistance up to 1000 h. The interaction of MMT nanogel composites with the epoxy matrix and good response of AMPS nanogel to sea water improve their ability to act as self-healing materials for epoxy coatings for steel.

  1. Studies on the absorption of epoxy resin 14C-epidian 5 through the skin of guinea pigs

    International Nuclear Information System (INIS)

    Woyton, A.; Wozniak, M.; Dobryszycka, W.

    1976-01-01

    The absorption and spread of epoxy resin labelled with 14 C-epidian 5, was evaluated by measurements of radioactivity of the skin and individual organs in guinea pigs and of the ovum in pregnant guinea pigs. It has been demonstrated that the radioactive resin is slowly absorbed through the skin and reaches, by blood vessels, inner organs and the skin distant from the smeared site. The liver participates actively in the metabolism of epidian 5. The radioactivity of the nervous tissue and urine of the guinea pig bladder increased successively with the length of time, which indicates this way of excretion of the resin. In fetal membranes the level of radioactivity was considerably higher than in the placental tissue and fetal fluids. Worthy of note is also that livers of guinea pig fetuses showed an isotope mark and that radioactivity increased in the fetal pulmonary tissue. (author)

  2. The effect of bulk-resin CNT-enrichment on damage and plasticity in shear-loaded laminated composites

    KAUST Repository

    Ventura, Isaac Aguilar; Lubineau, Gilles

    2013-01-01

    One way to improve multi functionality of epoxy-based laminated composites is to dope the resin with carbon nanotubes. Many investigators have focused on the elastic and fracture behavior of such nano-modified polymers under tensile loading. Yet

  3. Comparative study of the use of non-ionizing and ionizing radiation in the cure of epoxy resin: microwave versus electron electron

    Energy Technology Data Exchange (ETDEWEB)

    Kersting, Daniel, E-mail: daniel.kersting@usp.br [Centro Tecnologico da Marinha em Sao Paulo (CTMSP/USP), Sao Paulo, SP (Brazil); Wiebeck, Helio, E-mail: hwiebeck@usp.br [Universidade de Sao Paulo (USP), Sao Paulo, SP (Brazil). Escola Politecnica. Dept. de Engenharia Metalurgica; Marinucci, Gerson; Silva, Leonardo G.A. e, E-mail: marinuci@ipen.br, E-mail: gasilva@ipen.br [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

    2013-07-01

    Several processes for curing epoxy resins were developed over the years. Two methods are discussed in this paper, in order to present the main advantages and disadvantages of using microwave radiation (non-ionizing radiation) and electron beam radiation (ionizing radiation). The microwave radiation is a non-ionizing radiation, with great power of penetration and transfer of heat in microwave absorbing materials, or materials with microwave absorbing fillers. The frequency usually used in research and development is 2.45 GHz, the same available in commercial equipment. The microwave effect provides increase on the collision velocity between the reactant which, combined with energy absorbed by the reaction system, accelerates the curing reaction. None modifications in the epoxy system are required to use microwave heating for the curing process.On the other hand, the electron beam is a form of ionizing radiation in which the high energy electrons have the ability to interact with the irradiated material and produce ions, free radicals, and molecules in excited state, which can be used to initiate and propagate a polymerization. Specific initiators are necessary for an effective cure of the resin. In this study, a DGEBA epoxy resin with initiators based on anhydride and amine was used under the same conditions indicated by the manufacturer. The curing of the catalyzed system was performed in a domestic microwave oven adapted for laboratory use. The degradation and glass transition temperatures were evaluated by thermal analysis techniques. For comparative purposes, it was used data available in the literature for electron beam irradiation. (author)

  4. Comparative study of the use of non-ionizing and ionizing radiation in the cure of epoxy resin: microwave versus electron electron

    International Nuclear Information System (INIS)

    Kersting, Daniel; Wiebeck, Helio

    2013-01-01

    Several processes for curing epoxy resins were developed over the years. Two methods are discussed in this paper, in order to present the main advantages and disadvantages of using microwave radiation (non-ionizing radiation) and electron beam radiation (ionizing radiation). The microwave radiation is a non-ionizing radiation, with great power of penetration and transfer of heat in microwave absorbing materials, or materials with microwave absorbing fillers. The frequency usually used in research and development is 2.45 GHz, the same available in commercial equipment. The microwave effect provides increase on the collision velocity between the reactant which, combined with energy absorbed by the reaction system, accelerates the curing reaction. None modifications in the epoxy system are required to use microwave heating for the curing process.On the other hand, the electron beam is a form of ionizing radiation in which the high energy electrons have the ability to interact with the irradiated material and produce ions, free radicals, and molecules in excited state, which can be used to initiate and propagate a polymerization. Specific initiators are necessary for an effective cure of the resin. In this study, a DGEBA epoxy resin with initiators based on anhydride and amine was used under the same conditions indicated by the manufacturer. The curing of the catalyzed system was performed in a domestic microwave oven adapted for laboratory use. The degradation and glass transition temperatures were evaluated by thermal analysis techniques. For comparative purposes, it was used data available in the literature for electron beam irradiation. (author)

  5. MWCNTs/P(St-co-GMA) composite nanofibers of engineered interface chemistry for epoxy matrix nanocomposites.

    Science.gov (United States)

    Özden-Yenigün, Elif; Menceloğlu, Yusuf Z; Papila, Melih

    2012-02-01

    Strengthened nanofiber-reinforced epoxy matrix composites are demonstrated by engineering composite electrospun fibers of multi-walled carbon nanotubes (MWCNTs) and reactive P(St-co-GMA). MWCNTs are incorporated into surface-modified, reactive P(St-co-GMA) nanofibers by electrospinning; functionalization of these MWCNT/P(St-co-GMA) composite nanofibers with epoxide moieties facilitates bonding at the interface of the cross-linked fibers and the epoxy matrix, effectively reinforcing and toughening the epoxy resin. Rheological properties are determined and thermodynamic stabilization is demonstrated for MWCNTs in the P(St-co-GMA)-DMF polymer solution. Homogeneity and uniformity of the fiber formation within the electrospun mats are achieved at polymer concentration of 30 wt %. Results show that the MWCNT fraction decreases the polymer solution viscosity, yielding a narrower fiber diameter. The fiber diameter drops from an average of 630 nm to 460 nm, as the MWCNTs wt fraction (1, 1.5, and 2%) is increased. The electrospun nanofibers of the MWCNTs/P(St-co-GMA) composite are also embedded into an epoxy resin to investigate their reinforcing abilities. A significant increase in the mechanical response is observed, up to >20% in flexural modulus, when compared to neat epoxy, despite a very low composite fiber weight fraction (at about 0.2% by a single-layer fibrous mat). The increase is attributed to the combined effect of the two factors the inherent strength of the well-dispersed MWCNTs and the surface chemistry of the electrospun fibers that have been modified with epoxide to enable cross-linking between the polymer matrix and the nanofibers.

  6. Low Temperature Mechanical Testing of Carbon-Fiber/Epoxy-Resin Composite Materials

    Science.gov (United States)

    Nettles, Alan T.; Biss, Emily J.

    1996-01-01

    The use of cryogenic fuels (liquid oxygen and liquid hydrogen) in current space transportation vehicles, in combination with the proposed use of composite materials in such applications, requires an understanding of how such materials behave at cryogenic temperatures. In this investigation, tensile intralaminar shear tests were performed at room, dry ice, and liquid nitrogen temperatures to evaluate the effect of temperature on the mechanical response of the IM7/8551-7 carbon-fiber/epoxy-resin system. Quasi-isotropic lay-ups were also tested to represent a more realistic lay-up. It was found that the matrix became both increasingly resistant to microcracking and stiffer with decreasing temperature. A marginal increase in matrix shear strength with decreasing temperature was also observed. Temperature did not appear to affect the integrity of the fiber-matrix bond.

  7. Novel thermal curing of cycloaliphatic resins by thiol-epoxy click process with several multifunctional thiols

    OpenAIRE

    Guzman, Dailyn; Mateu, Blai; Fernández Francos, Xavier; Ramis Juan, Xavier; Serra Albet, Àngels

    2017-01-01

    Novel thermosets were prepared by the base-catalysed reaction between a cycloaliphatic resin (ECC) and various thiol crosslinkers. 4-(N,N-Dimethylaminopyridine) (DMAP) was used as base catalyst for the thiol–epoxy reaction. A commercial tetrathiol (PETMP) and three different thiols synthesized by us, 6SH-SQ, 3SH-EU and 3SH-ISO, were tested. 6SH-SQ and 3SH-EU were prepared from vinyl or allyl compounds from renewable resources such as squalene and eugenol, respectively. Thiol 3SH-ISO was prepa...

  8. Manufacturing of microcapsules with liquid core and their healing performance in epoxy for resin transfer molding

    OpenAIRE

    Yılmaz, Çağatay; Yilmaz, Cagatay

    2013-01-01

    Microcapsules with different active core materials have been receiving a great deal of attention for developing polymer based materials with selfhealing abilities. The self-healing ability is crucial in particular for matrix materials having brittle nature such as epoxy resin. In order for abstaining from an abrupt failure of structural brittle manner polymeric materials, microcapsules can be used excellently as a viable repair agent. In this work, we present a study on the catalyst-free micr...

  9. Nanoindentation study of interphases in epoxy/amine thermosetting systems modified with thermoplastics.

    Science.gov (United States)

    Ramos, Jose Angel; Blanco, Miren; Zalakain, Iñaki; Mondragon, Iñaki

    2009-08-15

    The characterization of a mixture of epoxy/amine with different stoichiometric ratios was carried out by means of nanoindentation. The epoxy system was composed by diglycidyl ether of bisphenol-A and 4,4'-methylene bis-(3-chloro 2,6-diethylaniline). Diffusion through interface formed by epoxy/amine system in stoichiometric ratio and several thermoplastic polymers was also analyzed by means of stiffness analysis, as studied by atomic force microscopy (AFM) and coupled nanoindentation tests. Used thermoplastics were an amorphous, atactic polystyrene, and two semicrystalline, syndiotactic polystyrene and poly(phenylene sulfide). Larger range diffusion was obtained in epoxy/amine systems modified with atactic polystyrene while the study of the influence of stoichiometric ratio suggests that the excess of epoxy generated stiffer material. In addition, larger indentation loads resulted in higher apparent stiffness because of the more number of polymer chains that had to re-accommodate owing to the increase in contact area.

  10. Synthesis of improved phenolic and polyester resins

    Science.gov (United States)

    Delano, C. B.

    1980-01-01

    Thirty-seven cured phenolic resin compositions were prepared and tested for their ability to provide improved char residues and moisture resistance over state of the art epoxy resin composite matrices. Cyanate, epoxy novolac and vinyl ester resins were investigated. Char promoter additives were found to increase the anaerobic char yield at 800 C of epoxy novolacs and vinyl esters. Moisture resistant cyanate and vinyl ester compositions were investigated as composite matrices with Thornel 300 graphite fiber. A cyanate composite matrix provided state of the art composite mechanical properties before and after humidity exposure and an anaerobic char yield of 46 percent at 800 C. The outstanding moisture resistance of the matrix was not completely realized in the composite. Vinyl ester resins showed promise as candidates for improved composite matrix systems.

  11. Behaviour of Epoxy Silica Nanocomposites Under Static and Creep Loading

    Science.gov (United States)

    Constantinescu, Dan Mihai; Picu, Radu Catalin; Sandu, Marin; Apostol, Dragos Alexandru; Sandu, Adriana; Baciu, Florin

    2017-12-01

    Specific manufacturing technologies were applied for the fabrication of epoxy-based nanocomposites with silica nanoparticles. For dispersing the fillers in the epoxy resin special equipment such as a shear mixer and a high energy sonicator with temperature control were used. Both functionalized and unfunctionalized silica nanoparticles were added in three epoxy resins. The considered filling fraction was in most cases 0.1, 0.3 and 0.5 wt%.. The obtained nanocomposites were subjected to monotonic uniaxial and creep loading at room temperature. The static mechanical properties were not significantly improved regardless the filler percentage and type of epoxy resin. Under creep loading, by increasing the stress level, the nanocomposite with 0.1 wt% silica creeps less than all other materials. Also the creep rate is reduced by adding silica nanofillers.

  12. Study on direct-chain diacid modified phenolic resin for Al-alloy casting

    Directory of Open Access Journals (Sweden)

    Yundong JI

    2005-02-01

    Full Text Available Resin coated sand (RCS with phenolic resin matrix can hardly be collapsed when it is used in Al-alloy casting. Adding collapsing agent and reducing the concentration of resin are solutions adopted by workers, but these methods tend to reduce the initial strength of RCS. Synthesis of modified phenolic resin with direct-chain diacid DAn (/JS=6, where n means carbon amount was studied here. The effects of the addition of modifying agent on molecular weight, gel time and softening point were investigated. Optimal addition of DAn (10% phenol was obtained by testing the initial and retained flexural strengths of the modified resin. FT-IR spectra showed that carbonyl shifts to higher wave number. With the use of TG, SEM and strength loss curves, the relation between initial and retained strengths was analysed. Tests on the heated deformation curve, before and after resin modification, show that PF-DA10 has the characteristic of higher initial and retained strengths together.

  13. Sensibilización a bisfenol A y bisfenol F en trabajadores expuestos a resinas epoxi

    Directory of Open Access Journals (Sweden)

    L. Jiménez Bajo

    2008-06-01

    Full Text Available Las aplicaciones de las diferentes resinas epoxi basadas en bisfenol A y F son extensas. Las resinas epoxi basadas en bisfenol F son más nuevas y resistentes que las de bisfenol A, y ambas son causa conocida de dermatitis de contacto alérgica. Se estudian 39 casos de sensibilización a resinas epoxi en los últimos 5 años. Los resultados obtenidos son: prevalencia de sensibilización a resinas epoxi entre los pacientes estudiados del 2%, 27 varones y 8 mujeres, con una edad media de 42.77, un período de medio sensibilización de 23,8 meses. La sensibilización a bisfenol F desde que se incluye para las pruebas del parche en la batería de resinas epoxi es del 100% para los casos sensibilizados a la resina. La localización mayoritaria se dio en las manos, con una relevancia actual del 84%. Se recomendó un cambio de puesto en el trabajo al 46% de estos pacientes. El aumento de la sensibilización encontrada a bisfenol F puede explicarse por una sensibilización concomitante con bisfenol A, una declaración incorrecta de la composición de la resina o una reactividad cruzada de ambos.The applications of epoxy resins based on bisphenol A and F are extensive. Epoxy resins based on bisphenol F are new and more resistant than epoxy resins based on bisphenol A. Both of them cause allergic contact dermatitis. In the last 5 years, we have studied 39 cases of sensitization to epoxy resin. The results of our study were these: the global prevalence of epoxy resin sensitization was 2%, 27 men and 8 women. The mean age was 42.77 years and the sensitization period was 23.8 months. The most frequent localization of the lesions were hands (84% of the patients. Since bisphenol F was included in epoxy resin battery for patch testing, a 100% of positives responses in patients sensitized to epoxy resin have been found. Sensitization to epoxy resins was a cause of change in workplace in 46% of cases in our series. There has been an increase in sensitization of

  14. Void-free epoxy castings for cryogenic insulators and seals

    International Nuclear Information System (INIS)

    Quirk, J.F.

    1983-01-01

    The design of the Westinghouse Magnet for the Oak Ridge National Laboratory's Large Coil Program (LCP) incorporates a main lead bushing which transmits heat-leak loads by conduction to the supercritical helium stream. The bushing, which consists of epoxy resin cast about a copper conductor, must be electrically insulated, vacuum tight and be capable of withstanding the stresses encountered in cryognic service. The seal design of the bushing is especially important; leakage from either the helium system or the external environment into the vacuum will cause the magnet to quench. Additionally, the epoxy-resin casting must resist mechanical loads caused by the weight of leads attached to the bushing and thermal stresses transmitted to the epoxy via the conductor. The epoxy resin is cast about the conductor in such a way as to provide the required vacuum tight seal. The technique by which this is accomplished is reviewed. Equally important is the elimination of voids in the epoxy which will act as stress-concentrating discontinuities during cooling to or warming from 4K. The types of voids that could be expected and their causes are described. The paper reviews techniques employed to eliminate voids within the cast-resin portion of the bushing

  15. Response behavior of an epoxy resin/amine curing agent/carbon black composite film to various solvents

    Energy Technology Data Exchange (ETDEWEB)

    Luo Yanling [School of Chemistry and Materials Science, Shaanxi Normal University, Xi' an 710062 (China)]. E-mail: luoyl0401@yahoo.com.cn; Li Zhanqing [School of Chemistry and Materials Science, Shaanxi Normal University, Xi' an 710062 (China); Lan Wenxiang [School of Chemistry and Materials Science, Shaanxi Normal University, Xi' an 710062 (China)

    2007-04-25

    A novel polymer based sensitive film was prepared from thermosetting epoxy resins (EP) filled with carbon blacks. The curing reaction of amine curing agents with epoxy resins and the response of the curing resultants to solvent vapors were dealt with. The influence of the types and content of carbon blacks and curing agents, and curing temperatures and time on curing reactions and response selectivity of the conductive films were investigated. The structural characterization was conducted on a Fourier transform infrared spectrophotometer (FTIR). The results indicated that the conductive films showed high response selectivity to polar solvent vapors, especially to chloroform vapor, while no response was observed in non-polar solvent vapors. The responsivity of the film increased with the decreased carbon black contents. The film filled with acetylene carbon black gave an optimal response, with responsivity of about 700 times. The response performances were improved with the amount of curing agents increased, and an optimal response appeared at the amount of the curing agent of 8%. The film's responsivity was remarkably enhanced, the reversibility property, however, rapidly declined in the order of diethyleneltriamine < triethylenetetramine < ethylenediamine. The curing reaction tended to complete with the curing temperature elevated and the curing time prolonged. But the response performance dropped because of over cross-linking as the temperature was too high or the time was too long.

  16. Response behavior of an epoxy resin/amine curing agent/carbon black composite film to various solvents

    International Nuclear Information System (INIS)

    Luo Yanling; Li Zhanqing; Lan Wenxiang

    2007-01-01

    A novel polymer based sensitive film was prepared from thermosetting epoxy resins (EP) filled with carbon blacks. The curing reaction of amine curing agents with epoxy resins and the response of the curing resultants to solvent vapors were dealt with. The influence of the types and content of carbon blacks and curing agents, and curing temperatures and time on curing reactions and response selectivity of the conductive films were investigated. The structural characterization was conducted on a Fourier transform infrared spectrophotometer (FTIR). The results indicated that the conductive films showed high response selectivity to polar solvent vapors, especially to chloroform vapor, while no response was observed in non-polar solvent vapors. The responsivity of the film increased with the decreased carbon black contents. The film filled with acetylene carbon black gave an optimal response, with responsivity of about 700 times. The response performances were improved with the amount of curing agents increased, and an optimal response appeared at the amount of the curing agent of 8%. The film's responsivity was remarkably enhanced, the reversibility property, however, rapidly declined in the order of diethyleneltriamine < triethylenetetramine < ethylenediamine. The curing reaction tended to complete with the curing temperature elevated and the curing time prolonged. But the response performance dropped because of over cross-linking as the temperature was too high or the time was too long

  17. Surface modification of epoxy resin using He/CF4 atmospheric pressure plasma jet for flashover withstanding characteristics improvement in vacuum

    Science.gov (United States)

    Chen, Sile; Wang, Shuai; Wang, Yibo; Guo, Baohong; Li, Guoqiang; Chang, Zhengshi; Zhang, Guan-Jun

    2017-08-01

    For enhancing the surface electric withstanding strength of insulating materials, epoxy resin (EP) samples are treated by atmospheric pressure plasma jet (APPJ) with different time interval from 0 to 300s. Helium (He) and tetrafluoromethane (CF4) mixtures are used as working gases with the concentration of CF4 ranging 0%-5%, and when CF4 is ∼3%, the APPJ exhibits an optimal steady state. The flashover withstanding characteristics of modified EP in vacuum are greatly improved under appropriate APPJ treatment conditions. The surface properties of EP samples are evaluated by surface roughness, scanning electron microscope (SEM), X-ray photoelectron spectroscopy (XPS) and water contact angle. It is considered that both physical and chemical effects lead to the enhancement of flashover strength. The physical effect is reflected in the increase of surface roughness, while the chemical effect is reflected in the graft of fluorine groups.

  18. A new technology for separation and recovery of materials from waste printed circuit boards by dissolving bromine epoxy resins using ionic liquid

    International Nuclear Information System (INIS)

    Zhu, P.; Chen, Y.; Wang, L.Y.; Qian, G.Y.; Zhou, M.; Zhou, J.

    2012-01-01

    Highlights: ► WPCBs were heated in [EMIM + ][BF 4 − ] for recovering solider at 240 °C. ► The bromine epoxy resins in WPCBs were all dissolved in [EMIM + ][BF 4 − ] at 260 °C. ► Used [EMIM + ][BF 4 − ] is treated by water to obtain regeneration. - Abstract: Recovery of valuable materials from waste printed circuit boards (WPCBs) is quite difficult because WPCBs is a heterogeneous mixture of polymer materials, glass fibers, and metals. In this study, WPCBs was treated using ionic liquid (1-ethyl-3-methylimizadolium tetrafluoroborate [EMIM + ][BF 4 − ]). Experimental results showed that the separation of the solders went to completion, and electronic components (ECs) were removed in WPCBs when [EMIM + ][BF 4 − ] solution containing WPCBs was heated to 240 °C. Meanwhile, metallographic observations verified that the WPCBs had an initial delamination. When the temperature increased to 260 °C, the separation of the WPCBs went to completion, and coppers and glass fibers were obtained. The used [EMIM + ][BF 4 − ] was treated by water to generate a solid–liquid suspension, which was separated completely to obtain solid residues by filtration. Thermal analyses combined with infrared ray spectra (IR) observed that the solid residues were bromine epoxy resins. NMR (nuclear magnetic resonance) showed that hydrogen bond played an important role for [EMIM + ][BF 4 − ] dissolving bromine epoxy resins. This clean and non-polluting technology offers a new way to recycle valuable materials from WPCBs and prevent environmental pollution from WPCBs effectively.

  19. Manufacturing of REBCO coils strongly bonded to cooling members with epoxy resin aimed at its application to Maglev

    Science.gov (United States)

    Mizuno, Katsutoshi; Ogata, Masafumi; Hasegawa, Hitoshi

    2014-11-01

    The REBCO coated conductor has been attracted attention because of its high current density in the presence of high magnetic field. If the coated conductor is applied to Maglev, the operational temperature of the on-board magnets will be over 40 K and energy consumption of cryocoolers will be reduced. That high operational temperature also means the absence of liquid helium. Therefore, reliable thermal coupling is desirable for cooling the coils. We propose an epoxy impregnated REBCO coil co-wound with PTFE tape. While the PTFE tape prevents the performance degradation of the coil, the epoxy resin bonds the coil to cooling members. We carried out three experiments to confirm that the coil structure which we propose has robust thermal coupling without the degradation. First, thermal resistances of paraffin and epoxy were measured varying the temperature from room temperature to 10 K. The measurement result indicates that paraffin has a risk of losing thermal coupling during cooling down. In another experiment, PTFE (polytetrafluoroethylene) tape insulator prevented performance degradation of a small epoxy impregnated REBCO coil, while another REBCO coil with polyimide tape showed clear performance degradation. Finally, we produced a racetrack REBCO coil with the same outer dimension as a Maglev on-board magnet coil. Although the racetrack coil was installed in a GFRP coil case and tightly bonded to the case by epoxy impregnation, any performance degradation was not observed.

  20. Effects of Core-Shell Rubber (CSR) Nanoparticles on the Cryogenic Fracture Toughness of CSR Modified Epoxy

    Science.gov (United States)

    Wang, Jun; Magee, Daniel; Schneider, Judy; Cannon, Seth

    2009-01-01

    This study investigated the effects of core-shell rubber (CSR) nanoparticles on the mechanical properties and fracture toughness of an epoxy resin at ambient and liquid nitrogen (LN2) temperatures. Varying amounts of Kane Ace(Registered TradeMark) MX130 and Kane Ace(Registered TradeMark) MX960 toughening agent were added to a commercially available EPON 862/Epikure W epoxy resin. Elastic modulus was calculated using quasi-static tensile data. Fracture toughness was evaluated by the resulting breaking energy measured in Charpy impact tests conducted on an instrumented drop tower. The size and distribution of the CSR nanoparticles were characterized using Transmission Electron Microscopy (TEM) and Small Angle X-ray Scattering (SAXS). Scanning Electron Microscopy (SEM) was used to study the fracture surface morphology. The addition of the CSR nanoparticles increased the breaking energy with negligible change in elastic modulus and ultimate tensile stress (UTS). At ambient temperature the breaking energy increased with increasing additions of the CSR nanoparticles up to 13.8wt%, while at LN2 temperatures, it reached a plateau at much lower CSR concentration.

  1. Studies on the absorption of epoxy resin /sup 14/C-epidian 5 through the skin of guinea pigs

    Energy Technology Data Exchange (ETDEWEB)

    Woyton, A; Wozniak, M; Dobryszycka, W [Akademia Medyczna, Wroclaw (Poland)

    1976-01-01

    The absorption and spread of epoxy resin labelled with /sup 14/C-epidian 5 was evaluated by measurements of radioactivity of the skin and individual organs in guinea pigs and of the ovum in pregnant guinea pigs. It has been demonstrated that the radioactive resin is slowly absorbed through the skin and reaches, by blood vessels, inner organs and the skin distant from the smeared site. The liver participates actively in the metabolism of epidian 5. The radioactivity of the nervous tissue and urine of the guinea pig bladder increased successively with the length of time, which indicates this way of excretion of the resin. In fetal membranes the level of radioactivity was considerably higher than in the placental tissue and fetal fluids. Worthy of note is also that livers of guinea pig fetuses showed an isotope mark and that radioactivity increased in the fetal pulmonary tissue.

  2. Mechanical and thermal properties of biocomposites from nonwoven industrial Fique fiber mats with Epoxy Resin and Linear Low Density Polyethylene

    Directory of Open Access Journals (Sweden)

    Miguel A. Hidalgo-Salazar

    2018-03-01

    Full Text Available In this work Linear Low Density Polyethylene-nonwoven industrial Fique fiber mat (LLDPE-Fique and Epoxy Resin-nonwoven industrial Fique fiber mat (EP-Fique biocomposites were prepared using thermocompression and resin film infusion processes. Neat polymeric matrices and its biocomposites were tested following ASTM standards in order to evaluate tensile and flexural mechanical properties. Also, thermal behavior of these materials has been studied by differential scanning calorimetry (DSC and thermogravimetric analysis (TGA. Tensile and flexural test revealed that nonwoven Fique reinforced composites exhibited higher modulus and strength but lower deformation capability as compared with LLDPE and EP neat matrices. TG thermograms showed that nonwoven Fique fibers incorporation has an effect on the thermal stability of the composites. On the other hand, Fique fibers did not change the crystallization and melting processes of the LLDPE matrix but restricts the motion of EP macromolecules chains thus increases the Tg of the EP-Fique composite. Finally, this work opens the possibility of considering non-woven Fique fibers as a reinforcement material with a high potential for the manufacture of biocomposites for automotive applications. In addition to the processing test specimens, it was also possible to manufacture a part of LLDPE-Fique, and one part of EP-Fique. Keywords: Biocomposites, Natural materials, Nonwoven Fique fiber mat, LLDPE, Epoxy Resin

  3. High T{sub g} and fast curing epoxy-based anisotropic conductive paste for electronic packaging

    Energy Technology Data Exchange (ETDEWEB)

    Keeratitham, Waralee, E-mail: waralee.ke@student.chula.ac.th; Somwangthanaroj, Anongnat, E-mail: anongnat.s@chula.ac.th [Department of Chemical Engineering, Faculty of Engineering, Chulalongkorn University, Bangkok, 10330 (Thailand)

    2016-03-09

    Herein, our main objective is to prepare the fast curing epoxy system with high glass transition temperature (T{sub g}) by incorporating the multifunctional epoxy resin into the mixture of diglycidyl ether of bisphenol A (DGEBA) as a major epoxy component and aromatic diamine as a hardener. Furthermore, the curing behavior as well as thermal and thermomechanical properties were investigated by differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA) and thermomechanical analysis (TMA). It was found that T{sub g} obtained from tan δ of DGEBA/aromatic diamine system increased from 100 °C to 205 °C with the presence of 30 percentage by weight of multifunctional epoxy resin. Additionally, the isothermal DSC results showed that the multifunctional epoxy resin can accelerate the curing reaction of DGEBA/aromatic diamine system. Namely, a high degree of curing (∼90%) was achieved after a few minutes of curing at low temperature of 130 °C, owing to a large number of epoxy ring of multifunctional epoxy resin towards the active hydrogen atoms of aromatic diamine.

  4. Thermal and mechanical interfacial properties of epoxy composites based on functionalized carbon nanotubes

    International Nuclear Information System (INIS)

    Jin Fanlong; Ma Changjie; Park, Soo-Jin

    2011-01-01

    Highlights: → CNTs were functionalized by acid and amine treatments. → Epoxy resin/CNT composites were prepared. → T g of the composites increased by about 10 deg. C compared to neat epoxy resins. → Toughness of the composites was significantly improved by the addition of functionalized CNTs. - Abstract: Carbon nanotubes (CNTs) were treated by a mixture of acid and functionalized subsequently by amine treatment to improve interfacial interactions and dispersion of CNTs in epoxy matrix. The thermal stabilities and mechanical interfacial properties of epoxy/CNT composites were investigated using several techniques. The dispersion state of CNTs in the epoxy matrix was observed by scanning electron microscope (SEM) and transmission electron microscopy (TEM). As a result, the glass transition temperature of epoxy/CNT composites increased by about 11 deg. C compared to neat epoxy resins. The mechanical interfacial property of the composites was significantly increased by the addition of amine treated CNTs. The SEM and TEM results showed that the separation and uniform dispersion of CNTs in the epoxy matrix.

  5. Resin-modified and conventional glass ionomer restorations in primary teeth: 8-year results

    DEFF Research Database (Denmark)

    Qvist, V.; Manscher, E.; Teglers, P.T.

    2004-01-01

    clinical trial, cariostatic effects, dental restorations, glass ionomer cement, long-term behaviour, pedodontics, resin-modified glass ionomer......clinical trial, cariostatic effects, dental restorations, glass ionomer cement, long-term behaviour, pedodontics, resin-modified glass ionomer...

  6. Novel Formulations of Phase Change Materials—Epoxy Composites for Thermal Energy Storage

    OpenAIRE

    Maria Elena Arce; Miguel Angel Alvarez Feijoo; Andres Suarez Garcia; Claudia C. Luhrs

    2018-01-01

    This research aimed to evaluate the thermal properties of new formulations of phase change materials (PCMs)-epoxy composites, containing a thickening agent and a thermally conductive phase. The composite specimens produced consisted of composites fabricated using (a) inorganic PCMs (hydrated salts), epoxy resins and aluminum particulates or (b) organic PCM (paraffin), epoxy resins, and copper particles. Differential Scanning Calorimetry (DSC) was used to analyze the thermal behavior of the sa...

  7. Rheological properties of epoxy/MWCNT suspensions associated with the surface modification of MWCNT by physisorption of aromatic ionic salts

    Energy Technology Data Exchange (ETDEWEB)

    Chang, Yu-Hsun [Institute of Polymer Science and Engineering, National Taiwan University, Taipei 106, Taiwan (China); Lin, King-Fu, E-mail: kflin@ntu.edu.tw [Institute of Polymer Science and Engineering, National Taiwan University, Taipei 106, Taiwan (China); Department of Materials Science and Engineering, National Taiwan University, Taipei 106, Taiwan (China)

    2016-04-15

    The multi-walled carbon nanotubes (MWCNTs) physisorbed by aromatic ionic salts such as 10-methyl-acridinium iodide (MAcI) were found to well disperse in diglycidyl ether of bisphenol-A epoxy resin. As they were subjected to the rheological study at 30 °C, the gelation of epoxy/MWCNT-MAcI suspension occurred at 0.75 wt% MWCNT-MAcI, which was less than that using pristine MWCNT. As to the viscosity measurements, the dilation effect that the viscosity of epoxy/MWCNT suspension increases with shear rate was found and more pronounced by incorporating MWCNT-MAcI. According to the Thomas-modified Einstein viscosity equation, the dilation effect was attributed to the excess amount of epoxy resin trapping in the aggregated domain of MWCNT. By increasing the shear rate to a certain point, the shear thinning effect that the viscosity decreases with shear rate was also observed. Interestingly, the transition point that the dilation effect changes to shear thinning effect shifted to lower shear rate as the content of MWCNT increased and/or MWCNT-MAcI was incorporated. Notably, better dispersion and less aggregated domains for the suspensions with MWCNT-MAcI compared to pristine MWCNT were further supported by small angle x-ray scattering and transmission electron microscopy. - Highlights: • Dilation effect that viscosity of epoxy/MWCNT suspension increases with shear rate was discovered. • Dilation effect was attributed to the excess epoxy resin trapping in the aggregated domain of MWCNT. • The transition point that the dilation effect changes to shear thinning effect was observed.

  8. Development of sealed radioactive sources immobilized in epoxy resin for verification of detectors used in nuclear medicine

    International Nuclear Information System (INIS)

    Tiezzi, Rodrigo

    2016-01-01

    The radioactive sealed sources are used in verification ionization chamber detectors, which measure the activity of radioisotopes used in several areas, such as in nuclear medicine. The measurement of the activity of radioisotopes must be made with accuracy, because it is administered to a patient. To ensure the proper functioning of the ionization chamber detectors, standardized tests are set by the International Atomic Energy Agency (IAEA) and the National Nuclear Energy Commission using sealed radioactive sources of Barium-133, Cesium-137 and Cobalt-57. The tests assess the accuracy, precision, reproducibility and linearity of response of the equipment. The focus of this work was the study and the development of these radioactive sources with standard Barium-133 and Cesium-137,using a polymer, in case commercial epoxy resin of diglycidyl ether of bisphenol A (DGEBA) and a curing agent based on modified polyamine diethylenetriamine (DETA), to immobilize the radioactive material. The polymeric matrix has the main function of fix and immobilize the radioactive contents not allowing them to leak within the technical limits required by the standards of radiological protection in the category of characteristics of a sealed source and additionally have the ability to retain the emanation of any gases that may be formed during the manufacture process and the useful life of this artifact. The manufacturing process of a sealed source standard consists of the potting ,into bottle standardized geometry, in fixed volume of a quantity of a polymeric matrix within which is added and dispersed homogeneously to need and exact amount in activity of the radioactive materials standards. Accordingly, a study was conducted for the choice of epoxy resin, analyzing its characteristics and properties. Studies and tests were performed, examining the maximum miscibility of the resin with the water (acidic solution, simulating the conditions of radioactive solution), loss of mechanical and

  9. Tunable Thermosetting Epoxies Based on Fractionated and Well-Characterized Lignins.

    Science.gov (United States)

    Gioia, Claudio; Lo Re, Giada; Lawoko, Martin; Berglund, Lars

    2018-03-21

    Here we report the synthesis of thermosetting resins from low molar mass Kraft lignin fractions of high functionality, refined by solvent extraction. Such fractions were fully characterized by 31 P NMR, 2D-HSQC NMR, SEC, and DSC in order to obtain a detailed description of the structures. Reactive oxirane moieties were introduced on the lignin backbone under mild reaction conditions and quantified by simple 1 H NMR analysis. The modified fractions were chemically cross-linked with a flexible polyether diamine ( M n ≈ 2000), in order to obtain epoxy thermosets. Epoxies from different lignin fractions, studied by DSC, DMA, tensile tests, and SEM, demonstrated substantial differences in terms of thermo-mechanical properties. For the first time, strong relationships between lignin structures and epoxy properties could be demonstrated. The suggested approach provides unprecedented possibilities to tune network structure and properties of thermosets based on real lignin fractions, rather than model compounds.

  10. Rational interface design of epoxy-organoclay nanocomposites: role of structure-property relationship for silane modifiers.

    Science.gov (United States)

    Bruce, Alex N; Lieber, Danielle; Hua, Inez; Howarter, John A

    2014-04-01

    Montmorillonite was modified by three silane surfactants with different functionalities to investigate the role of surfactant structure on the properties of a final epoxy-organoclay nanocomposite. N-aminopropyldimethylethoxysilane (APDMES), an aminated monofunctional silane, was chosen as a promising surfactant for several reasons: (1) it will bond to silica in montmorillonite, (2) it will bond to epoxide groups, and (3) to overcome difficulties found with trifunctional aminosilane bonding clay layers together and preventing exfoliation. A trifunctional and non-aminated version of APDMES, 3-aminopropyltriethoxysilane (APTES) and n-propyldimethylmethoxysilane (PDMMS), respectively, was also studied to provide comparison to this rationally chosen surfactant. APDMES and APTES were grafted onto montmorillonite in the same amount, while PDMMS was barely grafted (nanocomposite gallery spacing was not dependent on the surfactant used. Different concentrations of APDMES modified montmorillonite yielded different properties, as concentration decreased glass transition temperature increased, thermal stability increased, and the storage modulus decreased. Storage modulus, glass transition temperature, and thermal stability were more similar for epoxy-organoclay composites modified with the same concentration of silane surfactant, neat epoxy, and epoxy-montmorillonite nanocomposite. Copyright © 2013 Elsevier Inc. All rights reserved.

  11. Nanocomposite of photocurable epoxy-acrylate resin and carbon nanotubes: dynamic-mechanical, thermal and tribological properties

    Directory of Open Access Journals (Sweden)

    Marcos Nunes dos Santos

    2013-04-01

    Full Text Available In this study, the thermal, dynamic-mechanical and tribological behavior of nanocomposites of a photocurable epoxy-acrylate resin and multiwalled carbon nanotubes (MWCNT are investigated. A route consisting of a combination of sonication, mechanical and magnetic stirring is used to disperse 0.25-0.75 wt. (% MWCNT into the resin. Two photocuring cycles using 12 hours and 24 hours of UV-A radiation are studied. The storage modulus, the loss modulus and the tan delta are obtained by dynamic mechanical analysis. Thermal stability is investigated by thermogravimetry, morphology by transmission electronic microscopy (TEM and tribological performance using a pin-on-disk apparatus. The results indicate an increase in stiffness and higher ability to dissipate energy, as well as a shift in the glass transition temperature for the nanocomposites. The addition of nanofillers also decreased friction coefficient and wear rate of the nanocomposites but did not change the observed wear mechanisms.

  12. Nanocomposite of photocurable epoxy-acrylate resin and carbon nanotubes: dynamic-mechanical, thermal and tribological properties

    Directory of Open Access Journals (Sweden)

    Marcos Nunes dos Santos

    2012-01-01

    Full Text Available In this study, the thermal, dynamic-mechanical and tribological behavior of nanocomposites of a photocurable epoxy-acrylate resin and multiwalled carbon nanotubes (MWCNT are investigated. A route consisting of a combination of sonication, mechanical and magnetic stirring is used to disperse 0.25-0.75 wt. (% MWCNT into the resin. Two photocuring cycles using 12 hours and 24 hours of UV-A radiation are studied. The storage modulus, the loss modulus and the tan delta are obtained by dynamic mechanical analysis. Thermal stability is investigated by thermogravimetry, morphology by transmission electronic microscopy (TEM and tribological performance using a pin-on-disk apparatus. The results indicate an increase in stiffness and higher ability to dissipate energy, as well as a shift in the glass transition temperature for the nanocomposites. The addition of nanofillers also decreased friction coefficient and wear rate of the nanocomposites but did not change the observed wear mechanisms.

  13. Impact damage, hardness and tribology characterization of epoxy resin based composites reinforced with basalt fibers in combination with TiO_2, BaSO_4 and SiC

    International Nuclear Information System (INIS)

    Babu, T. Narendiranath; Mangalaraja, R.V.; Saravanan, S.; Prabha, D. Rama

    2016-01-01

    Impact damage, hardness characterization, frictional and wear behavior of epoxy resin based composites reinforced with basalt fibers in combination with TiO_2, BaSO_4 and SiC were investigated using an impact testing machine, a hardness testing machine and a pin on disc machine. The basalt contained different fillers and short fibers whose presence varied in steps of weight percentage from 23 % to 50 %. It was fabricated using the conventional hand-layup technique followed by the light compression moulding technique. The frictional behavior of the composite specimen was determined by testing on a pin on disc test machine under different operating conditions. The present investigation focused on the determination of the friction coefficient of epoxy resin based composites reinforced with basalt fibers in combination with the fillers. The effects of basalt short fibers content and load were examined under dry conditions. The results showed that the friction coefficient decreased with the filler contents increase. The hardness and the impact damage of epoxy resin reinforced with basalt fiber was examined and it was found that its reinforcement with basalt fiber along with fillers such as titanium oxide, silicon carbide, barium sulphate and graphite made it more advantageous than other specimens. Keywords: basalt fiber, impact behavior, hardness, wear resistance.

  14. Primary study on synthesis and characterization of the new type EB curable resins. Pt.1: Acrylic resins modified by light-oil

    International Nuclear Information System (INIS)

    Wei Jinshan; Yi Min; Wang Ruiyu; Li Jun; Ha Hongfei

    1995-01-01

    An acrylic resin modified by vegetable oil with high degree of unsaturation level has been synthesized. The characterization of coating film EB cured by the modified acrylic resin was studied primarily. The new type of EB curable acrylic resin is possessed of many merits such as cheap raw materials, simple synthesis technique and pretty characteristics of coating film. It is especially fit for timber surface coatings cured by EB radiation

  15. PENGARUH PENAMBAHAN SILIKON TERHADAP SUDUT KONTAK HIDROPOBIK DAN KARAKTERISTIK ARUS BOCOR PERMUKAAN BAHAN RESIN EPOKSI

    Directory of Open Access Journals (Sweden)

    Abdul Syakur

    2012-02-01

    Full Text Available Currently, polymer materials such as epoxy resin have been used as an insulator in the distribution andtransmission line. Some advantages of using this epoxy resin material having the dielectric properties are betterthan porcelain and glass insulators. On the other side, epoxy resins are also disadvantage the surface ishygroscopic. For the repair was done by adding the surface properties of silicone rubber materialThis paper describes the effect of adding silicone rubber against contact angle of hidrophobicity and surfaceleakage current characteristics of epoxy resin materials ( Di-Glycidyl Ether of Bisphenol A (DGEBA andMethaphenilene Diamine (MPDA. The study was conducted in the laboratory using the electrode method IEC587:1984 with NH4Cl contaminants. The voltage applied to the epoxy resin sample at 3.5 kV and 50 HzfrequencyThe experimental results showed that the addition of silicon rubber in epoxy resin makes the surface materialcontact angle increases. The higher percentage of silicone rubber, the greater the contact angle and the longertime required for the occurrence of surface discharge.

  16. Interaction of water with epoxy.

    Energy Technology Data Exchange (ETDEWEB)

    Powers, Dana Auburn

    2009-07-01

    The chemistries of reactants, plasticizers, solvents and additives in an epoxy paint are discussed. Polyamide additives may play an important role in the absorption of molecular iodine by epoxy paints. It is recommended that the unsaturation of the polyamide additive in the epoxy cure be determined. Experimental studies of water absorption by epoxy resins are discussed. These studies show that absorption can disrupt hydrogen bonds among segments of the polymers and cause swelling of the polymer. The water absorption increases the diffusion coefficient of water within the polymer. Permanent damage to the polymer can result if water causes hydrolysis of ether linkages. Water desorption studies are recommended to ascertain how water absorption affects epoxy paint.

  17. Modified silyl-terminated polyether polymer blends with bisphenol A diglycidyl ether epoxy for adhesive applications

    International Nuclear Information System (INIS)

    Bitenieks, J; Meri, R Merijs; Zicans, J; Berzins, R; Umbraško, J; Rekners, U

    2016-01-01

    Modified silyl-terminated polyether polymer (MS Polymer) was blended with bisphenol A diglycidyl ether (DGEBPA) epoxy at MS Polymer/epoxy ratio from 30/70 to 70/30. MS Polymer/epoxy systems were examined for two-component adhesive formulation with additional fillers. Applicability of the MS Polymer/epoxy system at the ratio of the components 60/40 is demonstrated for the development of adhesive formulation. Rheological analysis of the components A and B shows suitable viscosity values for development of two- component adhesives formulation. Curing dynamics as well as tensile stress-strain properties and Shore A hardness of the chosen adhesive formulation are reasonable for the development of MS Polymer/epoxy type adhesive. (paper)

  18. Annealing effects of carbon fiber-reinforced epoxy resin composites irradiated by electron beams

    International Nuclear Information System (INIS)

    Udagawa, Akira; Sasuga, Tuneo; Ito, Hiroshi; Hagiwara, Miyuki

    1987-01-01

    Carbon cloth-reinforced epoxy resin composites were irradiated with 2 MeV electrons at room temperature and then annealed in air for 2 h at temperatures up to 180 deg C. A considerable decrease in the three-point bending strength occurred when the irradiated composites were annealed in the temperature range of 115 - 135 deg C which is below the glass transition temperature T g of the matrix resin, while the bending strength remained unchanged up to 180 deg C for the unirradiated composites. In the dynamic viscoelastic spectra of the irradiated matrix, a new relaxation appeared at the temperature extending from 50 deg C to just below the matrix T g and disappeared on annealing for 2 h at 135 deg C. Annealing also decreased the concentration of free radicals existing stably in the irradiated matrix at room temperature. After annealing, a large amount of clacks and voids were observed in the fractography of the composites by scanning electron microscopy. These results indicate: (1) Annealing brings about rearrangement of the radiation-induced molecular chain scission in the matrix; (2) The bending strength of the irradiated composites decreased owing to the increased brittleness of the matrix by annealing. (author)

  19. Effect of the surface roughness on interfacial properties of carbon fibers reinforced epoxy resin composites

    International Nuclear Information System (INIS)

    Song Wei; Gu Aijuan; Liang Guozheng; Yuan Li

    2011-01-01

    The effect of the surface roughness on interfacial properties of carbon fibers (CFs) reinforced epoxy (EP) resin composite is studied. Aqueous ammonia was applied to modify the surfaces of CFs. The morphologies and chemical compositions of original CFs and treated CFs (a-CFs) were characterized by Atomic Force Microscopy (AFM), and X-ray Photoelectron Spectroscopy (XPS). Compared with the smooth surface of original CF, the surface of a-CF has bigger roughness; moreover, the roughness increases with the increase of the treating time. On the other hand, no obvious change in chemical composition takes place, indicating that the treating mechanism of CFs by aqueous ammonia is to physically change the morphologies rather than chemical compositions. In order to investigate the effect of surface roughness on the interfacial properties of CF/EP composites, the wettability and Interfacial Shear Strength (IFSS) were measured. Results show that with the increase of the roughness, the wettabilities of CFs against both water and ethylene glycol improves; in addition, the IFSS value of composites also increases. These attractive phenomena prove that the surface roughness of CFs can effectively overcome the poor interfacial adhesions between CFs and organic matrix, and thus make it possible to fabricate advanced composites based on CFs.

  20. Degradation of modified carbon black/epoxy nanocomposite coatings under ultraviolet exposure

    Science.gov (United States)

    Ghasemi-Kahrizsangi, Ahmad; Shariatpanahi, Homeira; Neshati, Jaber; Akbarinezhad, Esmaeil

    2015-10-01

    Degradation of epoxy coatings with and without Carbon Black (CB) nanoparticles under ultraviolet (UV) radiation were investigated using electrochemical impedance spectroscopy (EIS). Sodium dodecyl sulfate (SDS) was used to obtain a good dispersion of CB nanoparticles in a polymer matrix. TEM analysis proved a uniform dispersion of modified CB nanoparticles in epoxy coating. The coatings were subjected to UV radiation to study the degradation behavior and then immersed in 3.5 wt% NaCl. The results showed that the electrochemical behavior of neat epoxy coating was related to the formation and development of microcracks on the surface. The occurrence of microcracks on the surface of the coatings and consequently the penetration of ionic species reduced by adding CB nanoparticles into the formulation of the coatings. CB nanoparticles decreased degradation of CB coatings by absorbing UV irradiation. The ATR-FTIR results showed that decrease in the intensity of methyl group as main peak in presence of 2.5 wt% CB was lower than neat epoxy. In addition, the reduction in impedance of neat epoxy coating under corrosive environment was larger than CB coatings. The CB coating with 2.5 wt% nanoparticles had the highest impedance to corrosive media after 2000 h UV irradiation and 24 h immersion in 3.5 wt% NaCl.

  1. Radio-iodide uptake by modified poly (glycidyl methacrylate) as anion exchange resin

    Energy Technology Data Exchange (ETDEWEB)

    Othman, Sameh H. [Atomic Energy Authority, Cairo (Egypt). Nuclear Research Center; Atomic Energy Authority, Cairo (Egypt). Second Research Reactor; Elbarbary, Ahmed M. [Atomic Energy Authority, Cairo (Egypt). Radiation Research of Polymer Chemistry Dept.; Rashad, Ghada; Fasih, T.W. [Atomic Energy Authority, Cairo (Egypt). Hot Laboratories Center

    2017-03-01

    Poly(glycidyl methacrylate) (PGMA) microspheres were prepared by radiation induced polymerization of glycidyl methacrylate (GMA) monomer. The factors affecting the degree of polymerization and yield (%) of PGMA such as type of solvent, monomer concentration, and irradiation dose were investigated. It was found that the PGMA yield (%) increases with increasing monomer concentration up to 50% and absorbed dose of 5 kGy. The resulting PGMA containing the epoxy group was chemically modified by hydroxyl amine to act as anion-exchange resin for uptake of {sup 131}I{sup -} ions. The modified PGMA (MPGMA) was characterized by Fourier transform infrared (FT-IR) spectrophotometer, thermal gravimetric analysis (TGA) and scanning electron microscopy (SEM). I-131 is produced from the fission of U-235 with low-enrichment uranium (LEU) targets in the Egyptian Second Research Reactor (ETRR-2). Separation of iodide from the radioactive solution by batchwise and column techniques was employed to determine the adsorption capacity of the MPGMA. Quality control of {sup 131}I product solution and radiochemical purity was examined by using the ascending paper chromatography method. The uptake behavior of MPGMA towards {sup 131}I{sup -} ions were studied at different experimental conditions and achieved by X-ray fluorescence (XRF). The synthesized MPGMA showed good results as anion-exchange and an effective adsorbent for uptaking {sup 131}I{sup -} ions.

  2. Curing kinetics, mechanism and chemorheological behavior of methanol etherified amino/novolac epoxy systems

    Directory of Open Access Journals (Sweden)

    S. F. Zhao

    2014-02-01

    Full Text Available The curing kinetics and mechanism of epoxy novolac resin (DEN and modified epoxy novolac resin (MDEN with methanol etherified amino resin were studied by means of differential scanning calorimetry (DSC, Fourier transforminfrared (FT-IR spectroscopy and chemorheological analysis. Their kinetics parameters and models of the curing were examined utilizing isoconversional methods, Flynn-Wall-Ozawa and Friedman methods. For the DEN mixture, its average activation energy (Ea was 71.05 kJ/mol and the autocatalytic model was established to describe the curing reaction. The MDEN mixture exhibited three dominant curing processes, termed as reaction 1, reaction 2 and reaction 3; and their Ea were 70.05, 106.55 and 101.91 kJ/mol, respectively. Besides, Ea of reaction 1 was similar to that of DEN mixture, while Ea of reactions 2 and 3 corresponded to that of the etherification reaction between hydroxyl and epoxide group. Moreover, these three dominant reactions were nth order in nature. Furthermore, their curing mechanisms were proposed from the results of DSC and FTIR. The chemorheological behavior was also investigated to obtain better plastics products via optimizing the processing schedules.

  3. Modification of epoxy resin, silicon and glass surfaces with alkyl- or fluoroalkylsilanes for hydrophobic properties

    International Nuclear Information System (INIS)

    Marczak, Jacek; Kargol, Marta; Psarski, Maciej; Celichowski, Grzegorz

    2016-01-01

    Graphical abstract: - Highlights: • Chemical structure of alkylsilanes and fluoroalkylsilanes can affect the hydrophobic and surface performance of the modified samples. • Wet chemical hydrophobization is relatively simple and inexpensive method to obtain hydrophobic/superhydrophobic coatings. • The samples degradation is not observed and hydrophobic coatings seem to be stable in UV light. - Abstract: Preparation of superhydrophobic materials inspired by nature has attracted a great scientific interest in recent decades. Some of these materials have hierarchical lotus-like structures, i.e. micro- and nano-objects coated by hydrophobic compounds. A major challenge of applying the superhydrophobic surfaces for the self-cleaning coatings preparation is their improved efficiency in varying atmospheric conditions, e.g. UV light. The objective of this research work was to investigate the effect of the different chemical structure and the surface free energy on the hydrophobic and tribological properties of the alkylsilanes and fluoroalkylsilanes deposited on silicon wafers, glass slides and epoxy resin. Tribological and hydrophobic properties of the modified surfaces were correlated with their chemical structures. Chemical structures of the deposited materials were examined by using Fourier transform infrared (FT-IR) spectroscopy and hydrophobic properties were investigated by water contact angle (WCA) and surface free energy (SFE) measurements. The modified surfaces exhibited water contact angles of above 100° for the selected modifiers. It was noticed that the replacement of hydrogen atoms by fluorine atoms in alkyl chain caused an increase in the water contact angle values and a decrease in friction coefficients. The obtained results showed that the carbon chain length of a modifier and its chemical structure can strongly affect the hydrophobic and tribological properties of the modified surfaces. The highest values of WCA, lowest values of SFE and coefficient

  4. Mechanical properties of graphene oxide (GO/epoxy composites

    Directory of Open Access Journals (Sweden)

    Shivan Ismael Abdullah

    2015-08-01

    Full Text Available In this study, the effects of graphene oxide (GO on composites based on epoxy resin were analyzed. Different contents of GO (1.5–6 vol.% were added to epoxy resin. The GO/epoxy composite was prepared using the casting method and was prepared under room temperature. Mechanical tests’ results such as tensile test, impact test and hardness test show enhancements of the mechanical properties of the GO/epoxy composite. The experimental results clearly show an improvement in the Young’s modulus, tensile strength and hardness. The impact strength was seen to decrease, pointing to brittleness increase of the GO/epoxy composite. A microstructure analysis using Scanning Electron Microscopy (SEM and X-ray diffraction (XRD analysis was also performed, which showed how GO impeded the propagation of cracks in the composite. From the SEM images we observed the interface between the GO and the epoxy composite. As can be seen from this research, the GO/epoxy composites can be used for a large number of applications. The results of this research are a strong evidence for GO/epoxy composites being a potential candidate for use in a variety of industrial applications, especially for automobile parts, aircraft components, and electronic parts such as supercapacitors, transistors, etc.

  5. Influence of structure of a crosslinked epoxy resin on its properties studied by positron annihilation and other methods

    International Nuclear Information System (INIS)

    Debowska, M.; Baranowski, A.; Jerie, K.; Rudzinska-Girulska, J.; Kurzeja, L.; Hennek, K.

    1996-01-01

    Positron annihilation has been applied to study samples of two crosslinked epoxy resins: diglycidyl ether of bisphenol A (Epikote 828) and polyglycidyl-ether of phenol-formaldehyde novolac (Epikote 155) cured with 4,4'-diamino-diphenylo-methane (MDA), phenol-formaldehyde novolac resin (Novolac Z) and bisphenol A (formaldehyde resin). Results of measurements of positron lifetime spectra were compared with the ones coming from DMTA, flexural strength testing and density measurements. The most important features of samples (glass transition temperature, storage modulus, flexural strength, crosslinking density and tan δ) proved to be correlated with the product Ι 3 x v-bar, proportional to the fractional free volume in samples. Values of v-bar have been estimated from the values of τ 3 , the longest lifetime in positron lifetime spectra. Ι 3 corresponds to the intensity of the longest-lived component in them. Distributions of free volume radii reconstructed in the basis of PAL measurements are given for all samples. The influences of structure of both cured resin and the curing agent on the properties of the crosslinked products is clearly seen from the presented results. (author)

  6. Surface and buried interfacial structures of epoxy resins used as underfills studied by sum frequency generation vibrational spectroscopy.

    Science.gov (United States)

    Vázquez, Anne V; Holden, Brad; Kristalyn, Cornelius; Fuller, Mike; Wilkerson, Brett; Chen, Zhan

    2011-05-01

    Flip chip technology has greatly improved the performance of semiconductor devices, but relies heavily on the performance of epoxy underfill adhesives. Because epoxy underfills are cured in situ in flip chip semiconductor devices, understanding their surface and interfacial structures is critical for understanding their adhesion to various substrates. Here, sum frequency generation (SFG) vibrational spectroscopy was used to study surface and buried interfacial structures of two model epoxy resins used as underfills in flip chip devices, bisphenol A digylcidyl ether (BADGE) and 1,4-butanediol diglycidyl ether (BDDGE). The surface structures of these epoxies were compared before and after cure, and the orientations of their surface functional groups were deduced to understand how surface structural changes during cure may affect adhesion properties. Further, the effect of moisture exposure, a known cause of adhesion failure, on surface structures was studied. It was found that the BADGE surface significantly restructured upon moisture exposure while the BDDGE surface did not, showing that BADGE adhesives may be more prone to moisture-induced delamination. Lastly, although surface structure can give some insight into adhesion, buried interfacial structures more directly correspond to adhesion properties of polymers. SFG was used to study buried interfaces between deuterated polystyrene (d-PS) and the epoxies before and after moisture exposure. It was shown that moisture exposure acted to disorder the buried interfaces, most likely due to swelling. These results correlated with lap shear adhesion testing showing a decrease in adhesion strength after moisture exposure. The presented work showed that surface and interfacial structures can be correlated to adhesive strength and may be helpful in understanding and designing optimized epoxy underfill adhesives.

  7. Analysis and Testing of Bisphenol A—Free Bio-Based Tannin Epoxy-Acrylic Adhesives

    Directory of Open Access Journals (Sweden)

    Shayesteh Jahanshahi

    2016-04-01

    Full Text Available A tannin-based epoxy acrylate resin was prepared from glycidyl ether tannin (GET and acrylic acid. The influence of the reaction condition for producing tannin epoxy acrylate was studied by FT-MIR, 13C-NMR, MALDI-TOF spectroscopy and shear strength. The best reaction conditions for producing tannin epoxy acrylate resin without bisphenol A was by reaction between GET and acrylic acid in the presence of a catalyst and hydroquinone at 95 °C for 12 h. FT-MIR, 13C-NMR and MALDI-TOF analysis have confirmed that the resin has been prepared under these conditions. The joints bonded with this resin were tested for block shear strength. The results obtained indicated that the best strength performance was obtained by the bioepoxy-acrylate adhesive resin prepared at 95 °C for a 12-h reaction.

  8. Design and Analysis of Drive Shaft using Kevlar/Epoxy and Glass/Epoxy as a Composite Material

    Science.gov (United States)

    Karthikeyan, P.; Gobinath, R.; Kumar, L. Ajith; Jenish, D. Xavier

    2017-05-01

    In automobile industry drive shaft is one of the most important components to transmit power form the engine to rear wheel through the differential gear. Generally steel drive shaft is used in automobile industry, nowadays they are more interested to replace steel drive shaft with that of composite drive shaft. The overall objective of this paper is to analyze the composite drive shaft using to find out the best replacement for conventional steel drive shaft. The uses of advanced composite materials such as Kevlar, Graphite, Carbon and Glass with proper resins ware resulted in remarkable achievements in automobile industry because of its greater specific strength and specific modulus, improved fatigue and corrosion resistances and reduction in energy requirements due to reduction in weight as compared to steel shaft. This paper is to presents, the modeling and analysis of drive shaft using Kevlar/Epoxy and Glass/Epoxy as a composite material and to find best replacement for conventional steel drive shafts with an Kevlar/epoxy or Glass/Epoxy resin composite drive shaft. Modeling is done using CATIA software and Analysis is carried out by using ANSYS 10.0 software for easy understanding. The composite drive shaft reduces the weight by 81.67 % for Kevlar/Epoxy and 72.66% for Glass/Epoxy when compared with conventional steel drive shaft.

  9. Chemical tools: epoxic resins; Herramientas quimicas: resinas epoxidicas

    Energy Technology Data Exchange (ETDEWEB)

    Paz, S.; Pazos, M.; Prendes, P.

    1998-10-01

    Epoxy resins are very useful products for different applications in different fields. Due to the fact that they are a highly versatile products they can be considered as chemical tools. However the epoxy resins must be correctly formulated in order to obtain the final properties. In this article an easy and reliable method to optimise the energy formulation is presented. (Author)

  10. Temperature dependence of Young's modulus and internal friction of G-10CR and G-11CR epoxy resins

    International Nuclear Information System (INIS)

    Ledbetter, H.M.; Maerz, G.

    1980-01-01

    The Young's moduli of the epoxy-resin matrix material used in NEMA-designation G-10CR and G-11CR fiberglass-cloth-reinforced composites were measured dynamically and semicontinuously between ambient and liquid-nitrogen temperatures. Both materials exhibit regular temperature behavior, showing large Young's-modulus changes, about 125 and 50%, respectively. Internal friction decreased about 80% during cooling to liquid-nitrogen temperature (76 0 K). The different thermoelastic coefficients of the two materials indicate a different internal structure

  11. Synthesis on the durability of composite fiberglass/epoxy resin structures

    International Nuclear Information System (INIS)

    Thevenin, P.

    1997-01-01

    The purpose of this paper is to collect together in a systematic way information and results relating to the durability of composite fiberglass/ epoxy resin structures. First it is a matter of assessing the average level of understanding the long term behaviour of these structures which change under the combined effects of varied mechanical loading and stresses of a physico-chemical type linked to the environment. Looking at phenomena encountered and facts from current analyses, it will then be advisable to specify a methodology which can be applied to industrial piping used in PWR cooling systems for transporting raw water under pressure. In fact assessment of their service life is at present based on long and costly testing (ASTM D 2992 B standard), the appearance of which is inherited from metal piping testing.. Therefore it appears essential to study substitution test procedures, more composite specific and at the same time which can be conducted in reasonable time. For this purpose, by coherently accelerating and combining them in order not to underestimate their effects, ageing tests shall reproduce mechanisms representative of operating conditions. (author)

  12. Tailored SWCNT functionalization optimized for compatibility with epoxy matrices

    International Nuclear Information System (INIS)

    Martinez-Rubi, Y; Kingston, C T; Daroszewska, M; Barnes, M; Simard, B; Gonzalez-Dominguez, J M; Ansón-Casaos, A; Martinez, M T; Hubert, P; Cattin, C

    2012-01-01

    We have modified single walled carbon nanotubes (SWCNTs) with well defined matrix-based architectures to improve interface interaction in SWCNT/epoxy composites. The hardener and two pre-synthesized oligomers containing epoxy and hardener moieties were covalently attached to the SWCNT walls by in situ diazonium or carboxylic coupling reactions. In this way, SWCNTs bearing amine or epoxide-terminated fragments of different molecular weights, which resemble the chemical structure of the cured resin, were synthesized. A combination of characterization techniques such as Raman and infrared absorption (FTIR) spectroscopy, elemental analysis and coupled thermogravimetry-FTIR spectroscopy were used to identify both the functional groups and degree of functionalization of SWCNTs synthesized by the laser ablation and arc-discharge methods. Depending on the type of reaction employed for the chemical functionalization and the molecular weight of the attached fragment, it was possible to control the degree of functionalization and the electronic properties of the functionalized SWCNTs. Improved dispersion of SWCNTs in the epoxy matrix was achieved by direct integration without using solvents, as observed from optical microscopy and rheology measurements of the SWCNT/epoxy mixtures. Composite materials using these fillers are expected to exhibit improved properties while preserving the thermosetting architecture. (paper)

  13. Photocured epoxy/graphene nanocomposites with enhanced water vapor barrier properties

    Science.gov (United States)

    Periolatto, M.; Sangermano, M.; Spena, P. Russo

    2016-05-01

    A transparent, water vapor barrier film made of an epoxy resin and graphene oxide (GO) was synthesized by photopolymerization process. The epoxy/GO film with just 0.05 wt% GO gives a 93% WVTR reduction with respect to the pristine polymer, reaching barrier properties better than other polymer composites containing higher amounts of graphene. The excellent water vapor barrier is attributed to the good dispersion of GO in the polymer matrix. Moreover, GO significantly enhances the toughness and the damping capacity of the epoxy resins. The hybrid film can have potential applications in anticorrosive coatings, electronic devices, pharmaceuticals and food packaging.

  14. Photocured epoxy/graphene nanocomposites with enhanced water vapor barrier properties

    Energy Technology Data Exchange (ETDEWEB)

    Periolatto, M.; Spena, P. Russo [Faculty of Science and Technology, Free University of Bozen-Bolzano, Piazza Università 5, Bolzano (Italy); Sangermano, M. [Dipartimento di Scienza Applicata e Tecnologia, Politecnico di Torino, C.so Duca degli Abruzzi 24, Torino (Italy)

    2016-05-18

    A transparent, water vapor barrier film made of an epoxy resin and graphene oxide (GO) was synthesized by photopolymerization process. The epoxy/GO film with just 0.05 wt% GO gives a 93% WVTR reduction with respect to the pristine polymer, reaching barrier properties better than other polymer composites containing higher amounts of graphene. The excellent water vapor barrier is attributed to the good dispersion of GO in the polymer matrix. Moreover, GO significantly enhances the toughness and the damping capacity of the epoxy resins. The hybrid film can have potential applications in anticorrosive coatings, electronic devices, pharmaceuticals and food packaging.

  15. Photocured epoxy/graphene nanocomposites with enhanced water vapor barrier properties

    International Nuclear Information System (INIS)

    Periolatto, M.; Spena, P. Russo; Sangermano, M.

    2016-01-01

    A transparent, water vapor barrier film made of an epoxy resin and graphene oxide (GO) was synthesized by photopolymerization process. The epoxy/GO film with just 0.05 wt% GO gives a 93% WVTR reduction with respect to the pristine polymer, reaching barrier properties better than other polymer composites containing higher amounts of graphene. The excellent water vapor barrier is attributed to the good dispersion of GO in the polymer matrix. Moreover, GO significantly enhances the toughness and the damping capacity of the epoxy resins. The hybrid film can have potential applications in anticorrosive coatings, electronic devices, pharmaceuticals and food packaging.

  16. Latent Hardeners for the Assembly of Epoxy Composites

    Science.gov (United States)

    Palmieri, Frank; Wohl, Christopher J.; Connell, John W.; Mercado, Zoar; Galloway, Jordan

    2016-01-01

    Large-scale composite structures are commonly joined by secondary bonding of molded-and-cured thermoset components. This approach may result in unpredictable joint strengths. In contrast, assemblies made by co-curing, although limited in size by the mold, result in stable structures, and are certifiable for commercial aviation because of structural continuity through the joints. Multifunctional epoxy resins were prepared that should produce fully-cured subcomponents with uncured joining surfaces, enabling them to be assembled by co-curing in a subsequent out-of-autoclave process. Aromatic diamines were protected by condensation with a ketone or aldehyde to form imines. Properties of the amine-cured epoxy were compared with those of commercially available thermosetting epoxy resins and rheology and thermal analysis were used to demonstrate the efficacy of imine protection. Optimum conditions to reverse the protecting chemistry in the solid state using moisture and acid catalysis were determined. Alternative chemistries were also investigated. For example, chain reaction depolymerization and photoinitiated catalysts would be expected to minimize liberation of volatile organic content upon deprotection and avoid residual reactive species that could damage the resin. Results from the analysis of protected and deprotected resins will be presented.

  17. Epoxy – the hub for the most versatile polymer with exceptional combination of superlative features

    OpenAIRE

    Inam, Fawad

    2014-01-01

    Epoxy resins and epoxy based materials have experienced significant advancement since their beginning in 1936, when Dr. Castan of Switzerland and Dr. Greenlee of USA succeeded in synthesizing the very first bisphenol-A-based epoxy resins. Whether it is the new carbon fiber composite of Boeing’s Dreamliner or the thin set terrazzo flooring, epoxy has always been the ideal choice because of its superlative properties and unique chemical composition. Belonging to thermoset family, it is certainl...

  18. AFM and XRD characterization of silver nanoparticles films deposited on the surface of DGEBA epoxy resin by ion sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Andrade, Jose Elisandro de; Machado, Rogerio; Macedo, Marcelo Andrade; Cunha, Frederico Guilherme Carvalho [Clinica de Medicina Nuclear e Radiologia de Maceio (MedRadiUS), Radiology and Imaging Diagnosis at Universidade Federal de Alagoas (UFAL), Maceio, AL (Brazil)

    2012-07-01

    In this work, silver atoms were deposited by ion sputtering on the surface of diglycidyl ether of bisphenol A (DGEBA) epoxy resin cured at 150 deg C for 6 hours in air. The films of DGEBA and its precursors were characterized by Raman spectroscopy to identify the main functional groups and their relationship with the deposited silver atoms. Silver thin films of 5, 10, 15 and 20 nm were deposited on the epoxy resin at room temperature. Both the initial film of DGEBA and the subsequent silver thin film were analyzed by Atomic Force Microscopy (AFM) in the non-contact mode. Silver thin films were also analyzed using X-ray diffraction (XRD) at room temperature. The AFM results showed the formation of silver crystallites on the surface of DGEBA at very low coverage whereas XRD indicated that most of them had their main axis aligned to the normal of the surface. An increase in the coverage led to an increase in the grain size as indicated by AFM. However, XRD results indicated that the crystallite size remained almost constant while the appearance of peaks corresponding to other crystalline orientations suggests the coalescence of the original crystallites and an increase in size of the more dense planes, namely [111]. (author)

  19. AFM and XRD characterization of silver nanoparticles films deposited on the surface of DGEBA epoxy resin by ion sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Andrade, Jose Elisandro de; Machado, Rogerio; Macedo, Marcelo Andrade [Universidade Federal de Sergipe (UFSE), Aracaju, SE (Brazil). Programa de Pos-graduacao em Fisica; Cunha, Frederico Guilherme Carvalho [Universidade Federal de Sergipe (UFSE), Aracaju, SE (Brazil). Programa de Pos-graduacao em Ciencia e Engenharia de Materiais

    2012-07-01

    In this work, silver atoms were deposited by ion sputtering on the surface of diglycidyl ether of bisphenol A (DGEBA) epoxy resin cured at 150 Degree-Sign C for 6 hours in air. The films of DGEBA and its precursors were characterized by Raman spectroscopy to identify the main functional groups and their relationship with the deposited silver atoms. Silver thin films of 5, 10, 15 and 20 nm were deposited on the epoxy resin at room temperature. Both the initial film of DGEBA and the subsequent silver thin film were analyzed by Atomic Force Microscopy (AFM) in the non-contact mode. Silver thin films were also analyzed using X-ray diffraction (XRD) at room temperature. The AFM results showed the formation of silver crystallites on the surface of DGEBA at very low coverage whereas XRD indicated that most of them had their main axis aligned to the normal of the surface. An increase in the coverage led to an increase in the grain size as indicated by AFM. However, XRD results indicated that the crystallite size remained almost constant while the appearance of peaks corresponding to other crystalline orientations suggests the coalescence of the original crystallites and an increase in size of the more dense planes, namely [111]. (author)

  20. AFM and XRD characterization of silver nanoparticles films deposited on the surface of DGEBA epoxy resin by ion sputtering

    Directory of Open Access Journals (Sweden)

    José Elisandro de Andrade

    2013-01-01

    Full Text Available In this work, silver atoms were deposited by ion sputtering on the surface of diglycidyl ether of bisphenol A (DGEBA epoxy resin cured at 150 °C for 6 hours in air. The films of DGEBA and its precursors were characterized by Raman spectroscopy to identify the main functional groups and their relationship with the deposited silver atoms. Silver thin films of 5, 10, 15 and 20 nm were deposited on the epoxy resin at room temperature. Both the initial film of DGEBA and the subsequent silver thin film were analyzed by Atomic Force Microscopy (AFM in the non-contact mode. Silver thin films were also analyzed using X-ray diffraction (XRD at room temperature. The AFM results showed the formation of silver crystallites on the surface of DGEBA at very low coverage whereas XRD indicated that most of them had their main axis aligned to the normal of the surface. An increase in the coverage led to an increase in the grain size as indicated by AFM. However, XRD results indicated that the crystallite size remained almost constant while the appearance of peaks corresponding to other crystalline orientations suggests the coalescence of the original crystallites and an increase in size of the more dense planes, namely [111].

  1. Epoxy coatings for anticorrosion challenges: a link between chemistry and performance?

    Energy Technology Data Exchange (ETDEWEB)

    Sauvant-Moynot, Valerie; Schweitzer, Sylvie; Grenier, Jacky; Duval, Sebastien [Institut Francais du Petrole, 1 et 4 avenue Bois Preau, 92450 Rueil-Malmaison (France)

    2004-07-01

    Epoxy coatings have been used extensively for pipeline protection in the oil and gas industries over the past decades. Thank to their outstanding adhesive properties, epoxy resins are classically used for external coating of offshore pipelines although cathodic protection is applied. They provide corrosion protection while being used as neat coating or as primer layer in a three-layer coating. Protection of internal pipelines devoted to gas transport is another application of epoxy coatings. Whatever the case, the choice of the right epoxy formulation should be adapted to the service conditions, namely exposition medium and temperature, in order to provide efficient and sustainable corrosion protection. Epoxy resins constitute a wide family and classical formulations may not fulfill the requirements of today's challenges: as pipelines are require d to operate in more and more difficult conditions, coatings are expected to function in higher temperature conditions; additionally, practical conditions such as temporary injection of methanol make the environmental exposure of the epoxy coating harsher. Therefore, there is a need of a better knowledge of technical performance and limitations of high temperature epoxy resins. This paper examined the influence of the epoxy network architecture on their protection properties and durability while exposed to distilled / sea water at 110 deg. C and to methanol at room temperature. The objective was to investigate the link between resin chemistry and final performance with respect to anticorrosion applications. Five epoxy resin formulations mixed in stoichiometric proportions were cured and post-cured to infinite extent in order to achieve densely cross-linked networks exhibiting controlled and reproducible architectures. Gravimetric and pressurised differential scanning calorimetry (DSC) measurements were performed to evaluate the plasticization effect of both water and methanol on formulations under study. The related

  2. Reinforced carbon fiber laminates with oriented carbon nanotube epoxy nanocomposites: Magnetic field assisted alignment and cryogenic temperature mechanical properties.

    Science.gov (United States)

    He, Yuxin; Yang, Song; Liu, Hu; Shao, Qian; Chen, Qiuyu; Lu, Chang; Jiang, Yuanli; Liu, Chuntai; Guo, Zhanhu

    2018-05-01

    The epoxy nanocomposites with ordered multi-walled carbon nanotubes (MWCNTs) were used to influence the micro-cracks resistance of carbon fiber reinforced epoxy (CF/EP) laminate at 77 K, Oxidized MWCNTs functionalized with Fe 3 O 4 (Fe 3 O 4 /O-MWCNTs) with good magnetic properties were prepared by co-precipitation method and used to modify epoxy (EP) for cryogenic applications. Fe 3 O 4 /O-MWCNTs reinforced carbon fiber epoxy composites were also prepared through vacuum-assisted resin transfer molding (VARTM). The ordered Fe 3 O 4 /O-MWCNTs were observed to have effectively improved the mechanical properties of epoxy (EP) matrix at 77 K and reduce the coefficient of thermal expansion (CTE) of EP matrix. The ordered Fe 3 O 4 /O-MWCNTs also obviously improved the micro-cracks resistance of CF/EP composites at 77 K. Compared to neat EP, the CTE of ordered Fe 3 O 4 /O-MWCNTs modified CF/EP composites was decreased 37.6%. Compared to CF/EP composites, the micro-cracks density of ordered Fe 3 O 4 /O-MWCNTs modified CF/EP composites at 77 K was decreased 37.2%. Copyright © 2018 Elsevier Inc. All rights reserved.

  3. Epoxy/α-alumina nanocomposite with high electrical insulation performance

    Directory of Open Access Journals (Sweden)

    Yun Chen

    2017-10-01

    Full Text Available An experimental study was conducted to improve the electrical insulation of epoxy resin. The effects of boehmite, γ-alumina and α-alumina nanoparticles on the volume resistivity, dielectric strength and glass transition temperature of epoxy nanocomposites were investigated. The results showed that α-alumina nanoparticles displayed obvious advantages in enhancing electrical insulation performance of epoxy nanocomposites, compared to boehmite and γ-alumina nanoparticles. The direct current volume resistivity and breakdown strength of epoxy nanocomposite with 2.0 wt% α-alumina nanoparticles was improved to 2.2 × 1018 Ω cm and 76.1 kV mm−1 respectively. And these improved values of electrical insulation properties are much higher than these of epoxy nanocomposites reported in previous studies. The main reason of these improvements may be that the epoxy/α-alumina interaction zone was enhanced by crosslink. Keywords: Nanocomposite, Epoxy resin, Insulation, α-alumina

  4. Catalyzed Synthesis and Characterization of a Novel Lignin-Based Curing Agent for the Curing of High-Performance Epoxy Resin

    Directory of Open Access Journals (Sweden)

    Saeid Nikafshar

    2017-07-01

    Full Text Available In this study, lignin, an aromatic compound from the forestry industry, was used as a renewable material to synthesize a new aromatic amine curing agent for epoxy resin. Firstly, lignin was separated from black liquor and hydroxyl groups were converted to tosyl groups as leaving groups. Then, primary amination was conducted using an ammonia solution at high pressure and temperature, in the presence of a nano-alumina-based catalyst. The structure of the nanocatalyst was confirmed by FT-IR, ICP, SEM, and XPS analyses. According to the FT-IR spectra, a demethylation reaction, the substitution of hydroxyl groups with tosyl groups, and then an amination reaction were successfully performed on lignin, which was further confirmed by the 13C NMR and CHNS analyses. The active hydrogen equivalent of aminated lignin was determined and three samples with 9.9 wt %, 12.9 wt %, and 15.9 wt % of aminated lignin, as curing agents, were prepared for curing the diglycidyl ether of bisphenol A (DGEBA. The thermal characteristics of the curing process of these epoxy samples were determined by DSC and TGA analyses. Moreover, the mechanical performance of the cured epoxy systems, e.g., the tensile strength and Izod impact strength, were measured, showing that in the presence of 12.9 wt % aminated lignin, the mechanical properties of the aminated lignin-epoxy system exhibited the best performance, which was competitive, compared to the epoxy systems cured by commercial aromatic curing agents.

  5. Stronger Fire-Resistant Epoxies

    Science.gov (United States)

    Fohlen, George M.; Parker, John A.; Kumar, Devendra

    1988-01-01

    New curing agent improves mechanical properties and works at lower temperature. Use of aminophenoxycyclotriphosphazene curing agents yields stronger, more heat- and fire-resistant epoxy resins. Used with solvent if necessary for coating fabrics or casting films.

  6. Allergic contact dermatitis from resin hardeners during the manufacture of thermosetting coating paints.

    Science.gov (United States)

    Foulds, I S; Koh, D

    1992-02-01

    5 production operators from 2 factories manufacturing thermosetting coating paint developed work-related skin disorders within 12 months of the introduction of a new powdered paint product. All 5 workers were found to have allergic contact dermatitis from 2 epoxy resin hardeners, both of which were commercial preparations of triglycidyl isocyanurate (TGIC). 2 of the workers had concomitant sensitization to epoxy resin in the standard series and several of the epoxy resin preparations at the workplace. TGIC has been reported as a contact sensitizer both in persons producing the chemical and among end-users of TGIC-containing products. These 5 reported cases document allergic contact dermatitis from commercial TGIC among exposed workers during an intermediate process of powdered paint manufacture. The possibility of substituting this epoxy resin hardener with less sensitizing alternatives should be explored.

  7. Effects of Nanofillers on the Thermo-Mechanical Properties and Chemical Resistivity of Epoxy Nanocomposites.

    Science.gov (United States)

    Atchudan, Raji; Pandurangan, Arumugam; Joo, Jin

    2015-06-01

    MWCNTs was synthesized using Ni-Cr/MgO by CVD method and were purified. The purified MWCNT was used as a filler material for the fabrication of epoxy nanocomposites. The epoxy nanocomposites with different amount (wt% = 0.5, 1.0, 2.0, 3.0, 4.0 and 5.0) of nanofillers (CB, SiO2 and MWCNTs) were prepared by casting method. The effects of nanofillers on the properties of neat epoxy matrix were well studied. The thermal properties of nanocomposites were studied using DSC, TGA and flame retardant, and also the mechanical properties such as tensile strength, flexural strength, compressive strength, impact strength, determination of hardness and chemical resistance were studied extensively. Based on the experiment's results, 2 wt% MWCNTs loading in epoxy resin showed the highest improvement in tensile strength, as compared to neat epoxy and to other epoxy systems (CB/epoxy, SiO2/epoxy). Improvements in tensile strength, glass transition temperature and decomposition temperature were observed by the addition of MWCNTs. The mechanical properties of the epoxy nanocomposites were improved due to the interfacial bonding between the MWCNTs and epoxy resin. Strain hardening behavior was higher for MWCNT/epoxy nanocomposites compared with CB/epoxy and SiO2/epoxy nanocomposites. The investigation of thermal and mechanical properties reveals that the incorporation of MWCNTs into the epoxy nanocomposites increases its thermal stability to a great extent. Discrete increase of glass transition temperature of nanocomposites is linearly dependent on MWCNTs content. Due to strong interfacial bonding between MWCNTs and epoxy resin, the chemical resistivity of MWCNT/epoxy nanocomposites is superior to neat epoxy and other epoxy systems.

  8. The use of Electronic Speckle Pattern Interferometry (ESPI) in the crack propagation analysis of epoxy resins

    Science.gov (United States)

    Herbert, D. P.; Al-Hassani, A. H. M.; Richardson, M. O. W.

    The ESPI (electronic speckle pattern interferometry) technique at high magnification levels is demonstrated to be of considerable value in interpreting the fracture behaviour of epoxy resins. The fracture toughness of powder coating system at different thicknesses has been measured using a TDCB (tapered double cantilever beam) technique and the deformation zone at the tip of the moving crack monitored. Initial indications are that a mechanistic changeover occurs at a critical bond (coating) thickness and that this is synonymous with the occurence of a fracture toughness maximum, which in turn is associated with a deformation zone of specific diameter.

  9. Enhancement of mechanical and electrical properties of continuous-fiber-reinforced epoxy composites with stacked graphene.

    Science.gov (United States)

    Naveh, Naum; Shepelev, Olga; Kenig, Samuel

    2017-01-01

    Impregnation of expandable graphite (EG) after thermal treatment with an epoxy resin containing surface-active agents (SAAs) enhanced the intercalation of epoxy monomer between EG layers and led to further exfoliation of the graphite, resulting in stacks of few graphene layers, so-called "stacked" graphene (SG). This process enabled electrical conductivity of cured epoxy/SG composites at lower percolation thresholds, and improved thermo-mechanical properties were measured with either Kevlar, carbon or glass-fiber-reinforced composites. Several compositions with SAA-modified SG led to higher dynamic moduli especially at high temperatures, reflecting the better wetting ability of the modified nanoparticles. The hydrophilic/hydrophobic nature of the SAA dictates the surface energy balance. More hydrophilic SAAs promoted localization of the SG at the Kevlar/epoxy interface, and morphology seems to be driven by thermodynamics, rather than the kinetic effect of viscosity. This effect was less obvious with carbon or glass fibers, due to the lower surface energy of the carbon fibers or some incompatibility with the glass-fiber sizing. Proper choice of the surfactant and fine-tuning of the crosslink density at the interphase may provide further enhancements in thermo-mechanical behavior.

  10. Enhancement of mechanical and electrical properties of continuous-fiber-reinforced epoxy composites with stacked graphene

    Directory of Open Access Journals (Sweden)

    Naum Naveh

    2017-09-01

    Full Text Available Impregnation of expandable graphite (EG after thermal treatment with an epoxy resin containing surface-active agents (SAAs enhanced the intercalation of epoxy monomer between EG layers and led to further exfoliation of the graphite, resulting in stacks of few graphene layers, so-called “stacked” graphene (SG. This process enabled electrical conductivity of cured epoxy/SG composites at lower percolation thresholds, and improved thermo-mechanical properties were measured with either Kevlar, carbon or glass-fiber-reinforced composites. Several compositions with SAA-modified SG led to higher dynamic moduli especially at high temperatures, reflecting the better wetting ability of the modified nanoparticles. The hydrophilic/hydrophobic nature of the SAA dictates the surface energy balance. More hydrophilic SAAs promoted localization of the SG at the Kevlar/epoxy interface, and morphology seems to be driven by thermodynamics, rather than the kinetic effect of viscosity. This effect was less obvious with carbon or glass fibers, due to the lower surface energy of the carbon fibers or some incompatibility with the glass-fiber sizing. Proper choice of the surfactant and fine-tuning of the crosslink density at the interphase may provide further enhancements in thermo-mechanical behavior.

  11. The immobilization of anion exchange resins in polymer modified cements

    International Nuclear Information System (INIS)

    Dyer, A.; Morgan, P.D.

    1991-09-01

    Organic anion exchange resins, loaded with 99-Tc as the pertechnate ion, were incorporated into polymer modified cements (Flexocrete Ltd, Preston). BFS/OPC (9:1 mix) also was modified by three polymers from the same source (styrene acrylic (2) styrene butadiene) and loaded with anion exchanger containing the pertechnate. Composites were tested for initial compressive strengths, under water and radiation stability and leach rate. IAEA standard leach testing was with simulated sea and ground waters. Ground water leaching also was carried out on composites subjected to 1.10 9 rads (γ). Leach testing correlated well with compressive strength. Modified composites performed better than the BFS/OPC mix under all conditions studied and were able to encapsulate higher resin loadings. (author)

  12. Industrial-Graded Epoxy Nanocomposites with Mechanically Dispersed Multi-Walled Carbon Nanotubes: Static and Damping Properties

    Directory of Open Access Journals (Sweden)

    Andrea Giovannelli

    2017-10-01

    Full Text Available The majority of currently published dispersion protocols of carbon nanotubes rely on techniques that are not scalable to an industrial level. This work shows how to obtain polymer nanocomposites with good mechanical characteristics using multi-walled carbon nanotubes epoxy resins obtained by mechanical mixing only. The mechanical dispersion method illustrated in this work is easily scalable to industrial level. The high shearing force due to the complex field of motion produces a good and reproducible carbon nanotube dispersion. We have tested an industrial epoxy matrix with good baseline mechanical characteristics at different carbon nanotube weight loads. ASTM-derived tensile and compressive tests show an increment in both Young’s modulus and compressive strength compared with the pristine resin from a starting low wt %. Comparative vibration tests show improvement in the damping capacity. The new carbon nanotube enhanced epoxy resin has superior mechanical proprieties compared to the market average competitor, and is among the top products in the bi-components epoxy resins market. The new dispersion method shows significant potential for the industrial use of CNTs in epoxy matrices.

  13. Industrial-Graded Epoxy Nanocomposites with Mechanically Dispersed Multi-Walled Carbon Nanotubes: Static and Damping Properties.

    Science.gov (United States)

    Giovannelli, Andrea; Di Maio, Dario; Scarpa, Fabrizio

    2017-10-24

    The majority of currently published dispersion protocols of carbon nanotubes rely on techniques that are not scalable to an industrial level. This work shows how to obtain polymer nanocomposites with good mechanical characteristics using multi-walled carbon nanotubes epoxy resins obtained by mechanical mixing only. The mechanical dispersion method illustrated in this work is easily scalable to industrial level. The high shearing force due to the complex field of motion produces a good and reproducible carbon nanotube dispersion. We have tested an industrial epoxy matrix with good baseline mechanical characteristics at different carbon nanotube weight loads. ASTM-derived tensile and compressive tests show an increment in both Young's modulus and compressive strength compared with the pristine resin from a starting low wt %. Comparative vibration tests show improvement in the damping capacity. The new carbon nanotube enhanced epoxy resin has superior mechanical proprieties compared to the market average competitor, and is among the top products in the bi-components epoxy resins market. The new dispersion method shows significant potential for the industrial use of CNTs in epoxy matrices.

  14. Nanocellulose composites with enhanced interfacial compatibility and mechanical properties using a hybrid-toughened epoxy matrix.

    Science.gov (United States)

    Kuo, Pei-Yu; Barros, Luizmar de Assis; Yan, Ning; Sain, Mohini; Qing, Yan; Wu, Yiqiang

    2017-12-01

    Although there is a growing interest in utilizing nanocellulose fibres (NCFs) based composites for achieving a higher sustainability, mechanical performance of these composites is limited due to the poor compatibility between fibre reinforcement and polymer matrices. Here we developed a bio-nanocomposite with an enhanced fibre/resin interface using a hybrid-toughened epoxy. A strong reinforcing effect of NCFs was achieved, demonstrating an increase up to 88% in tensile strength and 298% in tensile modulus as compared to neat petro-based P-epoxy. The toughness of neat P-epoxy was improved by 84% with the addition of 10wt% bio-based E-epoxy monomers, which also mitigated the amount of usage of bisphenol A (BPA). The morphological analyses showed that the hybrid epoxy improved the resin penetration and fibre distribution significantly in the resulting composites. Thus, our findings demonstrated the promise of developing sustainable and high performance epoxy composites combing NCFs with a hybrid petro-based and bio-based epoxy resin system. Copyright © 2017 Elsevier Ltd. All rights reserved.

  15. Analysis and Testing of Bisphenol A-Free Bio-Based Tannin Epoxy-Acrylic Adhesives

    OpenAIRE

    Jahanshahi , Shayesteh; Pizzi , Antonio; Abdulkhani , Ali; Shakeri , Alireza

    2016-01-01

    International audience; A tannin-based epoxy acrylate resin was prepared from glycidyl ether tannin (GET) and acrylic acid. The influence of the reaction condition for producing tannin epoxy acrylate was studied by FT-MIR, C-13-NMR, MALDI-TOF spectroscopy and shear strength. The best reaction conditions for producing tannin epoxy acrylate resin without bisphenol A was by reaction between GET and acrylic acid in the presence of a catalyst and hydroquinone at 95 degrees C for 12 h. FT-MIR, C-13...

  16. Isothermal relaxation current and microstructure changes of thermally aged polyester films impregnated by epoxy resin

    Science.gov (United States)

    Jiang, Xiongwei; Sun, Potao; Peng, Qingjun; Sima, Wenxia

    2018-01-01

    In this study, to understand the effect of thermal aging on polymer films degradation, specimens of polyester films impregnated by epoxy resin with different thermal aging temperatures (80 and 130 °C) and aging times (500, 1600, 2400 and 3000 h) are prepared, then charge de-trapping properties of specimens are investigated via the isothermal relaxation current (IRC) measurement, the distributions of trap level and its corresponding density are obtained based on the modified IRC model. It is found that the deep trap density increases remarkably at the beginning of thermal aging (before 1600 h), but it decreases obviously as the aging degree increases. At elevated aging temperature and, in particular considering the presence of air gap between two-layer insulation, the peak densities of deep traps decrease more significant in the late period of aging. It can be concluded that it is the released energy from de-trapping process leads to the fast degradation of insulation. Moreover, after thermal aging, the microstructure changes of crystallinity and molecular structures are analyzed via the x-ray diffraction experiment and Fourier transform infrared spectrometer. The results indicate that the variation of the deep trap density is closely linked with the changes of microstructure, a larger interface of crystalline/amorphous phase, more defects and broken chains caused by thermal aging form higher deep trap density stored in the samples.

  17. The effects of cross-link length on the thermal properties of epoxy-resins from 1.5 to 80 K

    International Nuclear Information System (INIS)

    Nicholls, C.I.; Rosenberg, H.M.

    1981-01-01

    The thermal conductivity and diffusivity of epoxy-resins with cross-links of varying lengths have been measured from 1.5 to 80 K. The longer the cross-links, the higher is the conductivity in the liquid helium range, but this behaviour is inverted at 80 K. The specific heat is not dependent on the length of the cross-links. The results are discussed in the light of current ideas on the thermal properties of glasses. (orig.)

  18. Tensile Mechanical Properties and Failure Modes of a Basalt Fiber/Epoxy Resin Composite Material

    Directory of Open Access Journals (Sweden)

    Jingjing He

    2018-01-01

    Full Text Available Uniaxial tensile tests of basalt fiber/epoxy (BF/EP composite material with four different fiber orientations were conducted under four different fiber volume fractions, and the variations of BF/EP composite material failure modes and tensile mechanical properties were analyzed. The results show that when the fiber volume fraction is constant, the tensile strength, elastic modulus, and limiting strain of BF/EP composite material all decrease with increasing fiber orientation angle. When the fiber orientation angle is constant, the tensile strength, elastic modulus, and limiting strain of BF/EP composite material all increase with increasing fiber volume fraction. A certain degree of fiber clustering appears in the epoxy resin when the basalt fiber volume fraction is >1.2%. The fiber equidistribution coefficient and clustering fiber content were used to characterize the basalt fiber clustering effect. With the increase of fiber volume fraction, the clustering fiber content gradually increased, but the fiber equidistribution coefficient decreased. Meanwhile, based on Tsai theory, a geometric model and a tensile mechanical model of the clustering fiber are established. By considering the fiber clustering effect, the BF/EP composite material tensile strength is calculated, and the calculated values are close to the experimental results.

  19. Effect of calcium hydroxide and double and triple antibiotic pastes on the bond strength of epoxy resin-based sealer to root canal dentin.

    Science.gov (United States)

    Akcay, Merve; Arslan, Hakan; Topcuoglu, Hüseyin Sinan; Tuncay, Oznur

    2014-10-01

    The aim of this study was to evaluate the effects of calcium hydroxide (CH) and triple (TAP) and double (DAP) antibiotic pastes on the bond strength of an epoxy resin-based sealer (AH Plus Jet; Dentsply DeTrey, Konstanz, Germany) to the root canal dentin. Sixty-four single-rooted human mandibular premolars were decoronated and prepared using the rotary system to size 40. The specimens were randomly divided into a control group (without intracanal dressing) and 3 experimental groups that received an intracanal dressing with either CH, DAP, or TAP (n = 16). The intracanal dressing was removed by rinsing with 10 mL 17% EDTA followed by 10 mL 2.5% sodium hypochlorite. The root canals were then obturated with gutta-percha and AH Plus Jet sealer. A push-out test was used to measure the bond strength between the root canal dentin and the sealer. The data were analyzed using 2-way analysis of variance and Tukey post hoc tests to detect the effect of the independent variables (intracanal medicaments and root canal thirds) and their interactions on the push-out bond strength of the root canal filling material to the root dentin (P = .05). The push-out bond strength values were significantly affected by the intracanal medicaments (P .05). In the middle and apical third, the bond strength of the TAP group was higher than those of the CH and DAP groups (P < .05). The DAP and CH did not affect the bond strength of the epoxy resin-based sealer. Additionally, the TAP improved the bond strength of the epoxy resin-based sealer in the middle and apical thirds. Copyright © 2014 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

  20. Rheological characterization of geopolymer binder modified by organic resins

    Science.gov (United States)

    Cekalová, M.; Kovárík, T.; Rieger, D.

    2017-01-01

    The purpose of this study is going to investigate properties of alkali-activated powder (calcined kaoilinitic clay and granulated blast furnace slag) prepared as a geopolymer paste and modified by various amount of organic resin. Hybrid organic-inorganic binders were prepared as a mix of organic resin and geopolymer inorganic paste under vacuum conditions. The process of solidification was investigated by measurements of storage (G’) and loss modulus ( G’) in torsion. The measurement was conducted in oscillatory mode by constant strain of 0.01 %. This strain is set in linear visco-elastic region for minimization influence of paste structure. The effect of organic resin is presented and determined by changes of viscosity (‘n*), modules in torsion and tangent of loss angle (tan 8). Results indicate that addition of organic resin significantly affects the initial viscosity and hardening kinetics.

  1. Microwave absorption properties of polypyrrole-SrFe12O19-TiO2-epoxy resin nanocomposites: Optimization using response surface methodology

    Science.gov (United States)

    Seyed Dorraji, M. S.; Rasoulifard, M. H.; Amani-Ghadim, A. R.; Khodabandeloo, M. H.; Felekari, M.; Khoshrou, M. R.; hajimiri, I.

    2016-10-01

    At a few works are discussed about formation of heterogeneous composites with different distribution of particle shape and size that are used for electromagnetic absorption purposes. In this study a novel heterogeneous nanocpmposites is investigated. The nanocomposite has been successfully prepared based on epoxy resin including various nano-metal oxides (TiO2, SrFe12O19) and polypyrrole (PPy) by sol-gel and the solution chemistry method, respectively. The performance of prepared nanocomposite in absorption of microwave in X-band range was investigated and transmission line method by X-band waveguide straight was used to measure EM parameters of nanocomposites. The Response surface methodology (RSM) with central composite design (CCD) was utilized to study the effects of the wt.% TiO2 in SrFe12O19, wt.% Tio2-SrFe12O19 in PPy and wt.% TiO2-SrFe12O19-PPy in epoxy resin, on the microwave absorption properties with the absorber thickness of only 2 mm. The proposed quadratic model was in accordance with the experimental results with correlation coefficient of 96.5%. The optimum condition for maximum microwave absorption efficiency were wt.% TiO2 in SrFe12O19 of 70, wt.% TiO2-SrFe12O19 in PPy of 10 and wt.% TiO2-SrFe12O19-PPy in epoxy of 25. The sample prepared in optimal conditions indicated reflection loss of -15 dB corresponding to 97% absorption, at the range of 9.2-10.8 GHz.

  2. Effects of benzoxazine resin on property enhancement of shape memory epoxy: A dual function of benzoxazine resin as a curing agent and a stable network segment

    Directory of Open Access Journals (Sweden)

    T. Tanpitaksit

    2015-09-01

    Full Text Available An ability of bisphenol-A/aniline based benzoxazine resin (BA-a to simultaneously acts as a curing agent and a stable or rigid network segment for shape memory epoxy, i.e. a two component system, is demonstrated. This significantly simplifies a formulation of present shape memory epoxy systems, i.e. a three or four component system. A suitable content of BA-a in the aliphatic epoxy (NGDE/polybenzoxazine (PBA-a samples for good shape memory performance is in a range of 30 to 50 mol%. The storage modulus of the obtained NGDE/PBA-a shape memory polymers (SMPs was increased from 3.57 GPa for 30 mol% BA-a content to 4.50 GPa for 50 mol% BA-a content. Glass transition temperature of the sample was also substantially increased with increasing BA-a fraction, i.e. from 51°C to 140°C. Flexural modulus and strength at room temperature of the samples at 50 mol% BA-a were found to be as high as 3.97 GPa and 132 MPa compared to the maximum values of 2.54 GPa and 100 MPa of SMP based on cyanate ester-epoxy. All samples exhibited a high value of shape fixity close to 100%. A presence of the BA-a in the samples also imparted a greater recovery stress ranging from 0.25 to 1.59 MPa. Consequently, the obtained NGDE/PBA-a copolymers are highly attractive for shape memory materials to be used in a broader range of applications particularly at elevated temperature and a higher recovery stress value.

  3. Synthesis of adhesive radiohardenable resins of the modified polyepoxide type

    International Nuclear Information System (INIS)

    Acquacalda, J.-M.

    1972-01-01

    Eight adhesive radiohardenable resins of the modified epoxide type have been synthesized. Four were obtained from commercial resins: EPON 812, 827, 871 and ARALDITE 106. The synthesis of the four others required the development of analytical techniques to characterize of the reagents beforehand and then to identify the resins themselves. From a study of behavior under irradiation it seems that all the compounds obey a law of acrylic double bond disappearance with the logarithm of irradiation dose for which it is hard to find a detailed theoretical interpretation. The fracture of irradiated adhesive assemblies and their comparison has shown that for acceptable irradiation doses the synthesized resins, especially the product of Bisphenol A condensation on glycidyl acrylate, behave quite as well as polyepoxide resins without possessing the disadvantages inherent to the incorporation of standard chemical hardeners [fr

  4. Isothermal and non-isothermal cure of a tri-functional epoxy resin (TGAP): A stochastic TMDSC study

    International Nuclear Information System (INIS)

    Hutchinson, John M.; Shiravand, Fatemeh; Calventus, Yolanda; Fraga, Iria

    2012-01-01

    Highlights: ► First evaluation of T g of tri-functional epoxy resin TGAP by DSC. ► Clearly shows advantages of TOPEM for isothermal and non-isothermal cure analysis. ► Evidence of highly non-linear enthalpy relaxation in partially cured TGAP system. - Abstract: The isothermal cure of a highly reactive tri-functional epoxy resin, tri-glycidyl para-amino phenol (TGAP), with diamino diphenyl sulphone (DDS), at two different cure temperatures T c has been studied by both conventional differential scanning calorimetry (DSC) and by a stochastic temperature modulated DSC technique, TOPEM. From a series of isothermal cure experiments for increasing cure times, the glass transition temperature T g as a function of isothermal cure time is determined by conventional DSC from a second (non-isothermal) scan, and the vitrification time t v is obtained as the time at which T g = T c . In parallel, TOPEM experiments at the same T c lead directly to the determination of t v from the sigmoidal change in the quasi-static heat capacity. It is not possible to identify the glass transition temperature of the fully cured system, T g∞ , in a third scan by conventional DSC. In contrast, with TOPEM a second (non-isothermal) scan at 2 K/min after the isothermal cure gives rise to three separate transitions: devitrification of the partially cured and vitrified material; almost immediate vitrification as the T g of the system again rises; finally another devitrification, at a temperature approximating closely to T g∞ . Thus with TOPEM it is possible to obtain a calorimetric measure of the glass transition temperature of this fully cured system.

  5. Chemically Modified Starch; Allyl- and Epoxy-Starch Derivatives: Their Synthesis and Characterization

    NARCIS (Netherlands)

    Franssen, M.C.R.; Boeriu, C.

    2014-01-01

    Both native and modified starches, such as starch that is pregelatinized, extruded, acid-converted, cross-linked, and substituted, are widely used in industry. This chapter describes a mild two-step process for the synthesis of novel, highly reactive granular epoxy-starch derivatives. Via this

  6. Partial discharges within two spherical voids in an epoxy resin

    International Nuclear Information System (INIS)

    Illias, H A; Mokhlis, H; Tunio, M A; Chen, G; Bakar, A H A

    2013-01-01

    A void in a dielectric insulation material may exist due to imperfection in the insulation manufacturing or long term stressing. Voids have been identified as one of the common sources of partial discharge (PD) activity within an insulation system, such as in cable insulation and power transformers. Therefore, it is important to study PD phenomenon within void cavities in insulation. In this work, a model of PD activity within two spherical voids in a homogeneous dielectric material has been developed using finite element analysis software to study the parameters affecting PD behaviour. The parameters that have been taken into account are the void surface conductivity, electron generation rate and the inception and extinction fields. Measurements of PD activity within two spherical voids in an epoxy resin under ac sinusoidal applied voltage have also been performed. The simulation results have been compared with the measurement data to validate the model and to identify the parameters affecting PD behaviour. Comparison between measurements of PD activity within single and two voids in a dielectric material have also been made to observe the difference of the results under both conditions. (paper)

  7. DEGRADATION OF MAGNET EPOXY AT NSLS X-RAY RING.

    Energy Technology Data Exchange (ETDEWEB)

    HU,J.P.; ZHONG,Z.; HAAS,E.; HULBERT,S.; HUBBARD,R.

    2004-05-24

    Epoxy resin degradation was analyzed for NSLS X-ring magnets after two decades of 2.58-2.8 GeV continuous electron-beam operation, based on results obtained from thermoluminescent dosimeters irradiated along the NSLS ring and epoxy samples irradiated at the beamline target location. A Monte Carlo-based particle transport code, MCNP, was utilized to verify the dose from synchrotron radiation distributed along the axial- and transverse-direction in a ring model, which simulates the geometry of a ring quadrupole magnet and its central vacuum chamber downstream of the bending-magnet photon ports. The actual life expectancy of thoroughly vacuum baked-and-cured epoxy resin was estimated from radiation tests on similar polymeric materials using a radiation source developed for electrical insulation and mechanical structure studies.

  8. Evaluation of epoxy resin for cryogenic use by positron annihilation method. Change of characteristics of epoxy resin with cross-linking density and positron lifetime

    International Nuclear Information System (INIS)

    Nishijima, Shigehiro; Honda, Yoshihide; Okada, Toichi; Kobayashi, Yoshinori; Namba, Shingo.

    1994-01-01

    The positron annihilation method has been applied to evaluate unoccupied space in epoxy aiming at the design of the molecular structure for cryogenic use. To confirm the model in which molecular free space is needed in the epoxy for cryogenic use, the molecular weight between cross-linkings in epoxy was changed. The increase of molecular weight between cross-linkings brought an increase of fracture toughness even at liquid helium temperature and the model was found to be confirmed. The increase of molecular weight between cross-linkings was also found to decrease the 3rd lifetime of positrons. It suggested that the epoxy main chains were folded and this was confirmed by the molecular mechanical calculation. (author)

  9. Thermoset nanocomposites from waterborne bio-based epoxy resin and cellulose nanowhiskers.

    Science.gov (United States)

    Wu, Guo-min; Liu, Di; Liu, Gui-feng; Chen, Jian; Huo, Shu-ping; Kong, Zhen-wu

    2015-01-01

    Thermoset nanocomposites were prepared from a waterborne terpene-maleic ester type epoxy resin (WTME) and cellulose nanowhiskers (CNWs). The curing behaviors of WTME/CNWs nanocomposites were measured with rotational rheometer. The results show that the storage modulus (G') of WTME/CNWs nanocomposites increased with the increase of CNWs content. Observations by scanning electron microscopy (SEM) demonstrate that the incorporation of CNWs in WTME matrix caused microphase separation and destroyed the compactness of the matrix. This effect leads to the glass transition temperatures (Tg) of WTME/CNWs nanocomposites slightly decrease with the increase of CNWs content, which were confirmed by both DSC and DMA tests. The mechanical properties of WTME/CNWs nanocomposites were investigated by tensile testing. The Yong's modulus (E) and tensile strength (σb) of the nanocomposites were significantly reinforced by the addition of CNWs. These results indicate that CNWs exhibit excellent reinforcement effect on WTME matrix, due to the formation and increase of interfacial interaction by hydrogen bonds between CNWs nano-filler and the WTME matrix. Copyright © 2015 Elsevier Ltd. All rights reserved.

  10. Treatment by gliding arc of epoxy resin: preliminary analysis of surface modifications

    Science.gov (United States)

    Faubert, F.; Wartel, M.; Pellerin, N.; Pellerin, S.; Cochet, V.; Regnier, E.; Hnatiuc, B.

    2016-12-01

    Treatments with atmospheric pressure non-thermal plasma are easy to implement and inexpensive. Among them gliding arc (GlidArc) remains rarely used in surface treatment of polymers. However, it offers economic and flexible way to treat quickly large areas. In addition the choice of carrier gas makes it possible to bring the active species and other radicals allowing different types of grafting and functionalization of the treated surfaces, for example in order to apply for anti-biofouling prevention. This preliminary work includes analysis of the surface of epoxy resins by infrared spectroscopy: the different affected chemical bonds were studied depending on the duration of treatment. The degree of oxidation (the C/O ratio) is obtained by X-ray microanalysis and contact angle analysis have been performed to determinate the wettability properties of the treated surface. A spectroscopic study of the plasma allows to determine the possible active species in the different zones of the discharge.

  11. Barium ferrite/epoxy resin nanocomposite system: Fabrication, dielectric, magnetic and hydration studies

    Directory of Open Access Journals (Sweden)

    A. Kanapitsas

    2016-03-01

    Full Text Available Composite systems of epoxy resin and barium ferrite nanoparticles have been prepared, and studied varying the content of the inclusions. Morphology of prepared samples has been examined via scanning electron microscopy and X-ray diffraction spectra, while electrical and magnetic properties were investigated by means of broadband dielectric spectroscopy, and magnetization tests respectively. Finally, water vapor sorption measurements were conducted in order to study the water sorption dynamics of the system. Electron microscopy images revealed the successful fabrication of nanocomposites. Dielectric permittivity increases with filler content, while three relaxation processes were detected in the relative spectra. These processes are attributed to interfacial polarization, glass to rubber transition of the matrix, and re-orientation of polar side groups of the polymer’s chain. Magnetization and magnetic saturation increase with magnetic nano-powder content. Nanocomposites absorb a small amount of water, not exceeding 1.7 wt%, regardless filler content, indicating their hydrophobic character.

  12. Halloysite reinforced epoxy composites with improved mechanical properties

    Directory of Open Access Journals (Sweden)

    Saif Muhammad Jawwad

    2016-03-01

    Full Text Available Halloysite nanotubes (HNTs reinforced epoxy composites with improved mechanical properties were prepared. The prepared HNTs reinforced epoxy composites demonstrated improved mechanical properties especially the fracture toughness and flexural strength. The flexural modulus of nanocomposite with 6% mHNTs loading was 11.8% higher than that of neat epoxy resin. In addition, the nanocomposites showed improved dimensional stability. The prepared halloysite reinforced epoxy composites were characterized by thermal gravimetric analysis (TGA. The improved properties are attributed to the unique characteristics of HNTs, uniform dispersion of reinforcement and interfacial coupling.

  13. A critical evaluation of the enhancement of mechanical properties of epoxy modified using CNTs

    Science.gov (United States)

    Bedsole, Robert W.; Park, Cheol; Bogert, Philip B.; Tippur, Hareesh V.

    2015-09-01

    Carbon nanotubes (CNTs) have been widely shown in the literature to improve mechanical properties of epoxy, such as tensile strength, elastic modulus, strain to failure, and fracture toughness. These improvements in nanocomposite properties have been attributed to the extraordinary properties of the nanotubes, as well as the quality of their dispersion within and adhesion to the epoxy matrix. However, many authors have also struggled to show significant mechanical improvements using similar methodologies and despite, in some cases, showing qualitative improvements in dispersion with optical microscopy. These authors have frequently resorted to other methods for improving the mechanical properties of CNT/epoxy, such as electrically aligning CNTs, using different types of CNTs, or modifying the stoichiometry. The current work examines many different dispersion techniques, types of CNTs, types of epoxies, curing cycles, and other variables in an attempt to improve the mechanical properties of neat epoxy with CNTs. Despite seeing significant changes in the microscopy, no significant improvements in tensile or fracture properties have been attributed to CNTs in this work.

  14. Hydrothermal oxidation of an epoxy resin through the study of two model molecules: N-methyl-acetamide and N,N-di[1(phenoxy)2-hydroxy propyl-3] propyl-amine; Oxydation hydrothermale d'une resine epoxyde au travers de l'etude de deux molecules modeles: le N-methylacetamide et la N,N-di[1-(phenoxy) 2-hydroxy propyl-3] propylamine

    Energy Technology Data Exchange (ETDEWEB)

    Moutonnet-Fromonteil, C. [CEA/Cadarache, Dept. d' Etudes des Combustibles (DEC), 13 - Saint-Paul-lez-Durance (France)]|[Bordeaux-1 Univ., 33 (France)

    2000-07-01

    The study consists in choosing and developing a technology to realize damage experiments of an epoxy resin which is used as coating of embedded nuclear samples. Hydrothermal oxidation is the chosen method. We first identified the chemical composition of the epoxy resin. Then we studied hydrolysis and oxidation of a molecule which contains a function of the epoxy network: N-methyl-acetamide. The comparison between our results and those already existing allowed to validate this degradation method. In a second part, we studied a model molecule of the polymer network: N, N-di[1(phenoxy)2-hydroxy propyl-3] propyl-amine. The hydrolysis temperatures are relatively high: the compound is totally destroyed at 300 deg C. Its oxidation leads to the formation of acetic acid from 220 deg C. In the third study, we determined the best experimental conditions to destroy the epoxy resin. Experiments were performed at different temperatures between 200 deg C and 410 deg C. The degradation rates are classically defined by amounts of constituents in liquid and gaseous phases. (author)

  15. Comparative efficacy of nanofilled and microfilled resin-modified glass ionomer as pits and fissure sealant in permanent molar teeth

    Directory of Open Access Journals (Sweden)

    Manzuma Akhter Zakaria

    2017-05-01

    Full Text Available The purpose of the present study was to compare the efficacy of nanofilled and microfilled resin- modified glass ionomer as pits and fissure sealants in permanent molar teeth. Ninety six teeth having fissure at the occlusal surface were randomly divided into two groups: Group I: Treated by nanofilled resin-modified glass ionomer sealant and Group II: Treated by microfilled resin- modified glass ionomer sealants. Clinical assessment was performed by modified Ryge´s criteria by means of retention, color match, marginal adaptation at 3, 6, and 12 months follow-up visit. Chi-square test was used for testing differences between the two groups; a value of p<0.05 was considered as statistically significant. The results revealed that at 12 months observation period, nanofilled resin-modified glass ionomer sealant showed better retention, color stability and marginal adaptation than that of microfilled resin-modified glass ionomer sealants. Furthermore, the differences between two groups in respect to marginal adaptation and color match were statistically significant (p<0.05. It can be concluded that nanofilled resin-modified glass ionomer sealant could be a better alternative to microfilled resin- modified glass ionomer sealant.

  16. Radiation curable epoxy resin

    International Nuclear Information System (INIS)

    Najvar, D.J.

    1978-01-01

    A carboxyl containing polymer is either prepared in the presence of a polyepoxide or reacted with a polyepoxide. The polymer has sufficient acid groups to react with only about 1 to 10 percent of the epoxide (oxirane) groups. The remaining epoxide groups are reacted with an unsaturated monocarboxylic acid such as acrylic or methacrylic acid to form a radiation curable resin

  17. Modification of a Phenolic Resin with Epoxy- and Methacrylate-Functionalized Silica Sols to Improve the Ablation Resistance of Their Glass Fiber-Reinforced Composites

    Directory of Open Access Journals (Sweden)

    Yu Hu

    2014-01-01

    Full Text Available Functionalized silica sols were obtained by the hydrolytic condensation of (γ-methacryloxypropyltrimethoxysilane (MPMS, (γ-glycidyloxypropyltrimethoxysilane (GPMS and tetraethoxysilane (TEOS. Three different sols were obtained: MPS (derived from MPMS and TEOS, GPS-MPS (derived from GPMS, MPMS and TEOS, and GPSD (derived from GPMS, TEOS and diglycidyl ether of bisphenol A, DGEBA. These silica sols were mixed with a phenolic resin (PR. Ethylenediamine was used as a hardener for epoxy-functionalized sols and benzoyl peroxide was used as an initiator of the free-radical polymerization of methacrylate-functionalized silica sols. Glass fiber-reinforced composites were obtained from the neat PR and MPS-PR, GPS-MPS-PR and GPSD-PR. The resulting composites were evaluated as ablation resistant materials in an acetylene-oxygen flame. A large increase in the ablation resistance was observed when the PR was modified by the functionalized silica sols. The ablation resistance of the composites decreased as follows: GPSD-PR > MPS-PR > GPS-MPS-PR > PR.

  18. Toughening Mechanisms in Silica-Filled Epoxy Nanocomposites

    Science.gov (United States)

    Patel, Binay S.

    Epoxies are widely used as underfill resins throughout the microelectronics industry to mechanically couple and protect various components of flip-chip assemblies. Generally rigid materials largely surround underfill resins. Improving the mechanical and thermal properties of epoxy resins to better match those of their rigid counterparts can help extend the service lifetime of flip-chip assemblies. Recently, researchers have demonstrated that silica nanoparticles are effective toughening agents for lightly-crosslinked epoxies. Improvements in the fracture toughness of silica-filled epoxy nanocomposites have primarily been attributed to two toughening mechanisms: particle debonding with subsequent void growth and matrix shear banding. Various attempts have been made to model the contribution of these toughening mechanisms to the overall fracture energy observed in silica-filled epoxy nanocomposites. However, disparities still exist between experimental and modeled fracture energy results. In this dissertation, the thermal, rheological and mechanical behavior of eight different types of silica-filled epoxy nanocomposites was investigated. Each nanocomposite consisted of up to 10 vol% of silica nanoparticles with particle sizes ranging from 20 nm to 200 nm, with a variety of surface treatments and particle structures. Fractographical analysis was conducted with new experimental approaches in order to accurately identify morphological evidence for each proposed toughening mechanism. Overall, three major insights into the fracture behavior of real world silica-filled epoxy nanocomposites were established. First, microcracking was observed as an essential toughening mechanism in silica-filled epoxy nanocomposites. Microcracking was observed on the surface and subsurface of fractured samples in each type of silica-filled epoxy nanocomposite. The additional toughening contribution of microcracking to overall fracture energy yielded excellent agreement between experimental

  19. Graphene-epoxy flexible transparent capacitor obtained by graphene-polymer transfer and UV-induced bonding.

    Science.gov (United States)

    Sangermano, Marco; Chiolerio, Alessandro; Veronese, Giulio Paolo; Ortolani, Luca; Rizzoli, Rita; Mancarella, Fulvio; Morandi, Vittorio

    2014-02-01

    A new approach is reported for the preparation of a graphene-epoxy flexible transparent capacitor obtained by graphene-polymer transfer and UV-induced bonding. SU8 resin is employed for realizing a well-adherent, transparent, and flexible supporting layer. The achieved transparent graphene/SU8 membrane presents two distinct surfaces: one homogeneous conductive surface containing a graphene layer and one dielectric surface typical of the epoxy polymer. Two graphene/SU8 layers are bonded together by using an epoxy photocurable formulation based on epoxy resin. The obtained material showed a stable and clear capacitive behavior. © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  20. Diastereoisomeric diversity dictates reactivity of epoxy groups in limonene dioxide polymerization

    Directory of Open Access Journals (Sweden)

    M. Soto

    2018-06-01

    Full Text Available Limonene dioxide (LDO has the potential to find a wide application as a bio-based epoxy resin. Its polymerizations by catalyzed ring-opening, and by polyaddition with diamines were compared with the polymerizations of the commercial epoxy resins bisphenol-A diglycidyl ether (BADGE, and 3,4-epoxycyclohexylmethyl-3′,4′-epoxycyclohexane carboxylate (ECC. Differential scanning calorimetry (DSC studies showed that LDO polymerizations suffer in all cases studied from incomplete conversions. Nuclear magnetic resonance (NMR studies revealed that in cis-isomers of LDO the internal epoxide rings were not reacting. The low reactivity of this epoxide group was explained by mechanistic considerations making use of the Fürst-Plattner rule, or trans-diaxial effect. Due to diastereomeric diversity approximately one-fourth of epoxide groups present in LDO could not react. Therefore, a diastereoselective epoxidation of limonene could provide a fully reactive bio-based epoxy resin.

  1. Relationships between nanostructure and dynamic-mechanical properties of epoxy network containing PMMA-modified silsesquioxane

    Directory of Open Access Journals (Sweden)

    2009-06-01

    Full Text Available A new class of organic-inorganic hybrid nanocomposites was obtained by blending PMMA-modified silsesquioxane hybrid materials with epoxy matrix followed by curing with methyl tetrahydrophthalic anhydride. The hybrid materials were obtained by sol-gel method through the hydrolysis and polycondensation of the silicon species of the hybrid precursor, 3-methacryloxypropyltrimethoxysilane (MPTS, simultaneously to the polymerization of the methacrylate (MMA groups covalently bonded to the silicon atoms. The nanostructure of these materials was investigated by small angle X-ray scattering (SAXS and correlated to their dynamic mechanical properties. The SAXS results revealed a hierarchical nanostructure consisting on two structural levels. The first level is related to the siloxane nanoparticles spatially correlated in the epoxy matrix, forming larger hybrid secondary aggregates. The dispersion of siloxane nanoparticles in epoxy matrix was favored by increasing the MMA content in the hybrid material. The presence of small amount of hybrid material affected significantly the dynamic mechanical properties of the epoxy networks.

  2. Dry sliding wear behaviour of organo-modified montmorillonite filled epoxy nanocomposites using Taguchi's techniques

    International Nuclear Information System (INIS)

    Rashmi; Renukappa, N.M.; Suresha, B.; Devarajaiah, R.M.; Shivakumar, K.N.

    2011-01-01

    Highlights: → Successful fabrication of OMMT filled epoxy nanocomposites by high-shear mixing mehod. → Systematic tribological behaviour of the nanocomposites was made using Taguchi method. → Worn surface morphologies of the samples were discussed for different wear mechanisms. → Generation of wear data for sliding/bearing parts for different industries. -- Abstract: The aim of the research article is to study the dry sliding wear behaviour of epoxy with different wt.% of organo-modified montmorillonite (OMMT) filled nanocomposites. An orthogonal array (L 9 ) was used to investigate the influence of tribological parameters. The results indicate that the sliding distance emerges as the most significant factor affecting wear rate of epoxy nanocomposites. Experimental results showed that the inclusion of 5 wt.% OMMT nanofiller increased the wear resistance of the epoxy nanocomposite significantly. Furthermore, the worn surfaces of the samples were analyzed by scanning electron microscopy (SEM) to study the wear mechanisms and to correlate them with the wear test results.

  3. Performance of epoxy-nanocomposite under corrosive environment

    Directory of Open Access Journals (Sweden)

    2007-06-01

    Full Text Available Nanocomposite materials consisting of polymeric matrix materials and natural or synthetic layered minerals like clay are currently an expanding field of study because these new materials often exhibit a wide range of improved properties over their unmodified starting polymers. Epoxy/organoclay nanocomposites have been prepared by intercalating epoxy into the organoclay via direct mixing process. The clay exfoliation was monitored by X-ray diffraction (XRD and transmission electron microscopy (TEM. Water diffusion and sulfuric acid corrosion resistance of epoxy-based nanocomposites were evaluated. Diffusion was studied through epoxy samples containing up to 6 phr (parts per hundred resin of an organically treated montmorillonite. The diffusion of the environmental solution was measured by noting the increase in weight of the samples as a function of immersion time in these solutions at 80°C. The effect of the degree of exfoliation of the organoclay on water barrier and corrosion resistance was specifically studied. The data have been compared to those obtained from the neat epoxy resin to evaluate the diffusion properties of the nanocomposites. The flexural strength of the epoxy/organoclay nanocomposites samples made was examined to compare their mechanical performance under corrosive conditions as a function of immersion time and temperature. It was found, that the organoclay was mainly intercalated with some exfoliation and that addition of the organoclay yields better flexural strength retention under immersion into sulfuric acid.

  4. Novel Formulations of Phase Change Materials—Epoxy Composites for Thermal Energy Storage

    Science.gov (United States)

    Alvarez Feijoo, Miguel Angel

    2018-01-01

    This research aimed to evaluate the thermal properties of new formulations of phase change materials (PCMs)-epoxy composites, containing a thickening agent and a thermally conductive phase. The composite specimens produced consisted of composites fabricated using (a) inorganic PCMs (hydrated salts), epoxy resins and aluminum particulates or (b) organic PCM (paraffin), epoxy resins, and copper particles. Differential Scanning Calorimetry (DSC) was used to analyze the thermal behavior of the samples, while hardness measurements were used to determine changes in mechanical properties at diverse PCM and conductive phase loading values. The results indicate that the epoxy matrix can act as a container for the PCM phase without hindering the heat-absorbing behavior of the PCMs employed. Organic PCMs presented reversible phase transformations over multiple cycles, an advantage that was lacking in their inorganic counterparts. The enthalpy of the organic PCM-epoxy specimens increased linearly with the PCM content in the matrix. The use of thickening agents prevented phase segregation issues and allowed the fabrication of specimens containing up to 40% PCM, a loading significantly higher than others reported. The conductive phase seemed to improve the heat transfer and the mechanical properties of the composites when present in low percentages (phase combination (PCM + epoxy resin + hardener + thickening agent) presents great potential as a heat-absorbing material at the temperatures employed. PMID:29373538

  5. Effects of alumina nanoparticles on dynamic impact responses of carbon fiber reinforced epoxy matrix nanocomposites

    OpenAIRE

    Halil B. Kaybal; Hasan Ulus; Okan Demir; Ömer S. Şahin; Ahmet Avcı

    2018-01-01

    The influence of alumina (Al2O3) nanoparticles addition upon low-velocity impact behaviors of carbon fiber (CF) reinforced laminated epoxy nanocomposites have been investigated. For this purpose, different amounts of Al2O3 nanoparticles ranging from 1 to 5 wt% were added to the epoxy resin in order to observe the effect of nanoparticle loadings. CF reinforced epoxy based laminated nanocomposites were produced using Vacuum Assisted Resin Infusion Method (VARIM). The low velocity impact (LVI) t...

  6. Fiber-Reinforced Epoxy Composites and Methods of Making Same Without the Use of Oven or Autoclave

    Science.gov (United States)

    Barnell, Thomas J. (Inventor); Rauscher, Michael D. (Inventor); Stienecker, Rick D. (Inventor); Nickerson, David M. (Inventor); Tong, Tat H. (Inventor)

    2016-01-01

    Method embodiments for producing a fiber-reinforced epoxy composite comprise providing a mold defining a shape for a composite, applying a fiber reinforcement over the mold, covering the mold and fiber reinforcement thereon in a vacuum enclosure, performing a vacuum on the vacuum enclosure to produce a pressure gradient, insulating at least a portion of the vacuum enclosure with thermal insulation, infusing the fiber reinforcement with a reactive mixture of uncured epoxy resin and curing agent under vacuum conditions, wherein the reactive mixture of uncured epoxy resin and curing agent generates exothermic heat, and producing the fiber-reinforced epoxy composite having a glass transition temperature of at least about 100.degree. C. by curing the fiber reinforcement infused with the reactive mixture of uncured epoxy resin and curing agent by utilizing the exothermically generated heat, wherein the curing is conducted inside the thermally insulated vacuum enclosure without utilization of an external heat source or an external radiation source.

  7. Selective Clay Placement within a Silicate Clay-Epoxy Blend Nanocomposite and the Effect on Physical Properties

    Science.gov (United States)

    Miller, Sandi G.; Scheiman, Daniel A; Kohlmman, Lee W.

    2009-01-01

    Many epoxy systems under consideration for composite pressure vessels are composed of toughened epoxy resins. In this work, epoxy blends containing both rigid aromatic and flexible aliphatic components were prepared, to model toughened systems, and determine the optimum route of silicate addition. Compositions were chosen such that both glassy and rubbery resins were obtained at room temperature. The physical properties of the nanocomposites varied with T(g) and silicate placement, however, nanocomposite T(g)s were observed which exceeded that of the base resin by greater than 10 C. The tensile strength of the glassy resin remained constant or decreased on the dispersion of clay while that of the rubbery material doubled. Selectively placing the clay in the aliphatic component of the rubbery blend resulted in a greater than 100% increase in material toughness.

  8. Interpretation of Mechanical and Thermal Properties of Heavy Duty Epoxy Based Floor Coating Doped by Nanosilica

    Science.gov (United States)

    Nikje, M. M. Alavi; Khanmohammadi, M.; Garmarudi, A. Bagheri

    Epoxy-nano silica composites were prepared using Bisphenol-A epoxy resin (Araldite® GY 6010) resin obtained from in situ polymerization or blending method. SiO2 nanoparticles were pretreated by a silan based coupling agent. Surface treated nano silica was dispersed excellently by mechanical and ultrasonic homogenizers. A dramatic increase in the interfacial area between fillers and polymer can significantly improve the properties of the epoxy coating product such as tensile, elongation, abrasion resistance, etc.

  9. Bond strength of orthodontic light-cured resin-modified glass ionomer cement.

    Science.gov (United States)

    Cheng, Hsiang Yu; Chen, Chien Hsiu; Li, Chuan Li; Tsai, Hung Huey; Chou, Ta Hsiung; Wang, Wei Nan

    2011-04-01

    The purpose of this study was to compare the bond strengths and debonded interfaces achieved with light-cured resin-modified glass ionomer cement (RMGIC) and conventional light-cured composite resin. In addition, the effects of acid etching and water contamination were examined. One hundred human premolars were randomly divided into five equal groups. The mini Dyna-lock upper premolar bracket was selected for testing. The first four groups were treated with light-cured RMGIC with or without 15 per cent phosphoric acid-etching treatment and with or without water contamination preceding bracket bonding. The control samples were treated with the conventional light-cured Transbond composite resin under acid etching and without water contamination. Subsequently, the brackets were debonded by tensile force using an Instron machine. The modified adhesive remnant index (ARI) scores were assigned to the bracket base of the debonded interfaces using a scanning electron microscope. The bond strength and modified ARI scores were determined and analysed statistically by one-way analysis of variance and chi-square test. Under all four conditions, the bond strength of the light-cure RMGIC was equal to or higher than that of the conventional composite resin. The highest bond strength was achieved when using RMGIC with acid etching but without water contamination. The modified ARI scores were 2 for Fuji Ortho LC and 3 for Transbond. No enamel detachment was found in any group. Fifteen per cent phosphoric acid etching without moistening the enamel of Fuji Ortho LC provided the more favourable bond strength. Enamel surfaces, with or without water contamination and with or without acid etching, had the same or a greater bond strength than Transbond.

  10. Mixed resin and carbon fibres surface treatment for preparation of carbon fibres composites with good interfacial bonding strength

    International Nuclear Information System (INIS)

    He, Hongwei; Wang, Jianlong; Li, Kaixi; Wang, Jian; Gu, Jianyu

    2010-01-01

    The objective of this work is to improve the interlaminar shear strength of composites by mixing epoxy resin and modifying carbon fibres. The effect of mixed resin matrix's structure on carbon fibres composites was studied. Anodic oxidation treatment was used to modify the surface of carbon fibres. The tensile strength of multifilament and interlaminar shear strength of composites were investigated respectively. The morphologies of untreated and treated carbon fibres were characterized by scanning electron microscope and X-ray photoelectron spectroscopy. Surface analysis indicates that the amount of carbon fibres chemisorbed oxygen-containing groups, active carbon atom, the surface roughness, and wetting ability increases after treatment. The tensile strength of carbon fibres decreased little after treatment by anodic oxidation. The results show that the treated carbon fibres composites could possess excellent interfacial properties with mixed resins, and interlaminar shear strength of the composites is up to 85.41 MPa. The mechanism of mixed resins and treated carbon fibres to improve the interfacial property of composites is obtained.

  11. Influence of aromatic amine hardeners in the cure kinetics of an epoxy resin used in advanced composites

    Directory of Open Access Journals (Sweden)

    Michelle Leali Costa

    2005-03-01

    Full Text Available Composite structures for aerospace applications are mainly made by the well-known prepreg technology. In order to achieve adequate prepreg processing schedules, and consequently maximum fiber strength utilization, one has to know in deep the cure kinetics of matrix, which held the fibers together. This work describes a procedure to study the cure kinetic and has as example how aromatic amine hardeners influence the cure kinetics of an epoxy resin used in advanced composites. The investigation was carried out by using the DSC technique and it was found that depending on the system used the cure kinetics of the formulation obeys order n or autocatalytic order.

  12. A contribution from dielectric analysis to the study of the formation of multi-wall carbon nanotubes percolated networks in epoxy resin under an electric field

    International Nuclear Information System (INIS)

    Risi, Celso L.S.; Hattenhauer, Irineu; Ramos, Airton; Coelho, Luiz A.F.; Pezzin, Sérgio H.

    2015-01-01

    The formation of percolation networks in epoxy matrix nanocomposites reinforced with multi-wall carbon nanotubes (MWNT) during the curing process, at different MWNT contents, was studied by using a parallel plate cell subjected to a 300 V/cm AC electric field at 1 kHz. The percolation was verified by the electrical current output measured during and after the resin curing. The behavior of electric dipoles was characterized by impedance spectroscopy and followed the Debye first order dispersion model, by which an average relaxation time of 6.0 × 10 −4 s and a cut-off frequency of 1.7 kHz were experimentally found. By applying the theory of percolation, a critical probability, p c , equal to 0.038 vol% and an exponent of conductivity of 2.0 were found. Both aligned and random samples showed dipole relaxation times typical of interfacial and/or charge-hopping polarization, while the permittivity exhibited an exponential decrease with frequency. This behavior can be related to the increased ability to trap electrical charges due to the formation of the carbon nanotubes network. Optical and electron microscopies confirm the theoretical prediction that the application of an electric field during cure helps the process of MWNT debundling in epoxy resin. - Highlights: • We report the formation of percolating networks of MWNTs under AC electric field. • MWNT/epoxy dielectric properties were measured by impedance spectroscopy. • Lower percolation thresholds were obtained for composites with aligned CNTs. • Application of AC electric field helps the debundling of CNTs. • CNT/Epoxy with percolated networks presents interfacial and hopping polarizations

  13. Specific heat of nano-ferrites modified composites

    Directory of Open Access Journals (Sweden)

    Muntenita Cristian

    2017-01-01

    Full Text Available The specific heat of nano-ferrites modified composites was studied using differential scanning calorimeter (DSC method in the temperature range of 30 to 150°C. Initially, nano-ferrites were introduced in epoxy systems in order to improve the electromagnetic properties of formed materials. Together with the changes in electromagnetic properties some modifications occur regarding thermal and mechanical properties. The materials were formed by placing 5g or 10g of ferrite into 250g polymer matrix leading to a very low weight ratio of modifying agent. At so low ratios the effect of ferrite presence should be insignificant according to mixing rule. Anyway there is possible to appear some chelation reaction with effects on thermal properties of materials. Three types of epoxy resins had been used as matrix and barium ferrite and strontium ferrite as modifying agents. The thermal analysis was developed on two heatingcooling cycles and the specific heat was evaluated for each segment of the cycle analysis.

  14. Los morteros epoxi en la construcción

    Directory of Open Access Journals (Sweden)

    Fernández Cánovas, Manuel

    1968-02-01

    Full Text Available Epoxi resins are being increasingly applied in construction in recent years. This is due to their excellent properties and an improving technology, which enables these resins to be applied to more delicate and difficult uses. This article describes the work done by the author as part of an extensive program of experimental work at the Instituto Eduardo Torroja laboratory. This program of work refers particularly to mortars with a low content of epoxi resins. By this is meant a mixture of none fine aggregate with the least quantity of resin necessary to obtain a suitable bond. The investigation involved a study of the proportioning of sand and resin, the relation between proportioning, the age and the mechanical strength and also the physical properties of the resulting mortars.Desde hace unos años las resinas epoxi están encontrando una mayor aplicación en el campo de la construcción. Esto es debido a sus excelentes propiedades y a una tecnología cada vez más perfeccionada, las cuales permiten realizar, con éxito, muchas de sus aplicaciones a problemas cada día más difíciles y delicados. El autor da cuenta, en este artículo, de los trabajos que ha realizado sobre morteros epoxi como parte de un amplio plan de ensayos experimentales que el Instituto Eduardo Torroja lleva a cabo en sus laboratorios. Este estudio se refiere a los morteros epoxídicos pobres, entendiéndose por tales, la mezcla de árido exento de finos con la mínima cantidad de resina precisa para su confección. En el mismo se estudian las influencias de: la granulometría de la arena en la cantidad de resina a emplear; de la dosificación y de la edad en la resistencia mecánica, así como de las propiedades físicas de los morteros así formados.

  15. Biocompatible epoxy modified bio-based polyurethane nanocomposites: mechanical property, cytotoxicity and biodegradation.

    Science.gov (United States)

    Dutta, Suvangshu; Karak, Niranjan; Saikia, Jyoti Prasad; Konwar, Bolin Kumar

    2009-12-01

    Epoxy modified Mesua ferrea L. seed oil (MFLSO) based polyurethane nanocomposites with different weight % of clay loadings (1%, 2.5% and 5%) have been evaluated as biocompatible materials. The nanocomposites were prepared by ex situ solution technique under high mechanical shearing and ultrasonication at room temperature. The partially exfoliated nanocomposites were characterized by Fourier transform infra-red (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) techniques. The mechanical properties such as tensile strength and scratch hardness were improved 2 and 5 times, respectively by nanocomposites formation. Even the impact resistance improved a little. The thermostability of the nanocomposites was enhanced by about 40 degrees C. Biodegradation study confirmed 5-10 fold increase in biodegradation rate for the nanocomposites compared to the pristine polymers. All the nanocomposites showed non-cytotoxicity as evident from RBC hemolysis inhibition observed in anti-hemolytic assay carried over the sterilized films. The study reveals that the epoxy modified MFLSO based polyurethane nanocomposites deserve the potential to be applicable as biomaterials.

  16. Reducing composite restoration polymerization shrinkage stress through resin modified glass-ionomer based adhesives.

    Science.gov (United States)

    Naoum, S J; Mutzelburg, P R; Shumack, T G; Thode, Djg; Martin, F E; Ellakwa, A E

    2015-12-01

    The aim of this study was to determine whether employing resin modified glass-ionomer based adhesives can reduce polymerization contraction stress generated at the interface of restorative composite adhesive systems. Five resin based adhesives (G Bond, Optibond-All-in-One, Optibond-Solo, Optibond-XTR and Scotchbond-Universal) and two resin modified glass-ionomer based adhesives (Riva Bond-LC, Fuji Bond-LC) were analysed. Each adhesive was applied to bond restorative composite Filtek-Z250 to opposing acrylic rods secured within a universal testing machine. Stress developed at the interface of each adhesive-restorative composite system (n = 5) was calculated at 5-minute intervals over 6 hours. The resin based adhesive-restorative composite systems (RBA-RCS) demonstrated similar interface stress profiles over 6 hours; initial rapid contraction stress development (0-300 seconds) followed by continued contraction stress development ≤0.02MPa/s (300 seconds - 6 hours). The interface stress profile of the resin modified glass-ionomer based adhesive-restorative composite systems (RMGIBA-RCS) differed substantially to the RBA-RCS in several ways. Firstly, during 0-300 seconds the rate of contraction stress development at the interface of the RMGIBA-RCS was significantly (p adhesives can significantly reduce the magnitude and rate of polymerization contraction stress developed at the interface of adhesive-restorative composite systems. © 2015 Australian Dental Association.

  17. Effects of ultraviolet and electron radiations on graphite-reinforced polysulfone and epoxy resins

    International Nuclear Information System (INIS)

    Giori, C.; Yamauchi, T.

    1984-01-01

    Degradation mechanisms have been investigated for graphite/polysulfone and graphite/epoxy laminates exposed to ultraviolet and high-energy electron radiations in vacuum up to 960 equivalent sun hours and 10 9 rads, respectively. Based on GC and combined GC/MS analysis of volatile by-products evolved during irradiation, several free radical mechanisms of composite degradation have been identified. All the composite materials evaluated have shown high electron radiation stability and relatively low ultraviolet stability as indicated by low G values and high quantum yields for gas formation. Mechanical property measurements of irradiated samples did not reveal significant changes, with the possible exception of UV exposed polysulfone laminates. Hydrogen and methane have been identified as the main byproducts of irradiation, along with unexpectedly high levels of CO and CO 2 . Initial G values for methane relative to hydrogen formation are higher in the presence of isopropylidene linkages, which occur in bisphenol-A resins

  18. Study of matrix micro-cracking in nano clay and acrylic tri-block-copolymer modified epoxy/basalt fiber-reinforced pressure-retaining structures

    Directory of Open Access Journals (Sweden)

    2011-10-01

    Full Text Available In fiber-reinforced polymer pressure-retaining structures, such as pipes and vessels, micro-level failure commonly causes fluid permeation due to matrix cracking. This study explores the effect of nano-reinforcements on matrix cracking in filament-wound basalt fiber/epoxy composite structures. The microstructure and mechanical properties of bulk epoxy nanocomposites and hybrid fiber-reinforced composite pipes modified with acrylic tri-block-copolymer and organophilic layered silicate clay were investigated. In cured epoxy, the tri-block-copolymer phase separated into disordered spherical micelle inclusions; an exfoliated and intercalated structure was observed for the nano-clay. Block-copolymer addition significantly enhanced epoxy fracture toughness by a mechanism of particle cavitation and matrix shear yielding, whereas toughness remained unchanged in nano-clay filled nanocomposites due to the occurrence of lower energy resistance phenomena such as crack deflection and branching.Tensile stiffness increased with nano-clay content, while it decreased slightly for block-copolymer modified epoxy. Composite pipes modified with either the organic and inorganic nanoparticles exhibited moderate improvements in leakage failure strain (i.e. matrix cracking strain; however, reductions in functional and structural failure strength were observed.

  19. Effect of electron beam irradiation on thermal and mechanical properties of aluminum based epoxy composites

    Science.gov (United States)

    Visakh, P. M.; Nazarenko, O. B.; Sarath Chandran, C.; Melnikova, T. V.; Nazarenko, S. Yu.; Kim, J.-C.

    2017-07-01

    The epoxy resins are widely used in nuclear and aerospace industries. The certain properties of epoxy resins as well as the resistance to radiation can be improved by the incorporation of different fillers. This study examines the effect of electron beam irradiation on the thermal and mechanical properties of the epoxy composites filled with aluminum nanoparticles at percentage of 0.35 wt%. The epoxy composites were exposed to the irradiation doses of 30, 100 and 300 kGy using electron beam generated by the linear electron accelerator ELU-4. The effects of the doses on thermal and mechanical properties of the aluminum based epoxy composites were investigated by the methods of thermal gravimetric analysis, tensile test, and dynamic mechanical analysis. The results revealed that the studied epoxy composites showed good radiation resistance. The thermal and mechanical properties of the aluminum based epoxy composites increased with increasing the irradiation dose up to 100 kGy and decreased with further increasing the dose.

  20. Novel Formulations of Phase Change Materials—Epoxy Composites for Thermal Energy Storage

    Directory of Open Access Journals (Sweden)

    Maria Elena Arce

    2018-01-01

    Full Text Available This research aimed to evaluate the thermal properties of new formulations of phase change materials (PCMs-epoxy composites, containing a thickening agent and a thermally conductive phase. The composite specimens produced consisted of composites fabricated using (a inorganic PCMs (hydrated salts, epoxy resins and aluminum particulates or (b organic PCM (paraffin, epoxy resins, and copper particles. Differential Scanning Calorimetry (DSC was used to analyze the thermal behavior of the samples, while hardness measurements were used to determine changes in mechanical properties at diverse PCM and conductive phase loading values. The results indicate that the epoxy matrix can act as a container for the PCM phase without hindering the heat-absorbing behavior of the PCMs employed. Organic PCMs presented reversible phase transformations over multiple cycles, an advantage that was lacking in their inorganic counterparts. The enthalpy of the organic PCM-epoxy specimens increased linearly with the PCM content in the matrix. The use of thickening agents prevented phase segregation issues and allowed the fabrication of specimens containing up to 40% PCM, a loading significantly higher than others reported. The conductive phase seemed to improve the heat transfer and the mechanical properties of the composites when present in low percentages (<10 wt %; however, given its mass, the enthalpy detected in the composites was reduced as their loading further increased. The conductive phase combination (PCM + epoxy resin + hardener + thickening agent presents great potential as a heat-absorbing material at the temperatures employed.

  1. Fracture Resistance of Endodontically Treated Teeth Restored with Biodentine, Resin Modified GIC and Hybrid Composite Resin as a Core Material.

    Science.gov (United States)

    Subash, Dayalan; Shoba, Krishnamma; Aman, Shibu; Bharkavi, Srinivasan Kumar Indu; Nimmi, Vijayan; Abhilash, Radhakrishnan

    2017-09-01

    The restoration of a severely damaged tooth usually needs a post and core as a part of treatment procedure to provide a corono - radicular stabilization. Biodentine is a class of dental material which possess high mechanical properties with excellent biocompatibility and bioactive behaviour. The sealing ability coupled with optimum physical properties could make Biodentine an excellent option as a core material. The aim of the study was to determine the fracture resistance of Biodentine as a core material in comparison with resin modified glass ionomer and composite resin. Freshly extracted 30 human permanent maxillary central incisors were selected. After endodontic treatment followed by post space preparation and luting of Glass fibre post (Reforpost, Angelus), the samples were divided in to three groups based on the type of core material. The core build-up used in Group I was Biodentine (Septodont, France), Group II was Resin-Modified Glass Ionomer Cement (GC, Japan) and Group III was Hybrid Composite Resin (TeEconom plus, Ivoclar vivadent). The specimens were subjected to fracture toughness using Universal testing machine (1474, Zwick/Roell, Germany) and results were compared using One-way analysis of variance with Tukey's Post hoc test. The results showed that there was significant difference between groups in terms of fracture load. Also, composite resin exhibited highest mean fracture load (1039.9 N), whereas teeth restored with Biodentine demonstrated the lowest mean fracture load (176.66 N). Resin modified glass ionomer exhibited intermediate fracture load (612.07 N). The primary mode of failure in Group I and Group II was favourable (100%) while unfavourable fracture was seen in Group III (30%). Biodentine, does not satisfy the requirements to be used as an ideal core material. The uses of RMGIC's as a core build-up material should be limited to non-stress bearing areas. Composite resin is still the best core build-up material owing to its high fracture

  2. High-Performance Epoxy-Resin-Bonded Magnets Produced from the Sm2Fe17Nx Powders Coated by Copper and Zinc Metals

    Science.gov (United States)

    Noguchi, Kenji; Machida, Ken-ichi; Adachi, Gin-ya

    2001-04-01

    Fine powders of Sm2Fe17Nx coated with copper metal reduced from CuCl2 and/or zinc metal subsequently derived by photo-decomposition of diethylzinc [Zn(C2H5)2] were prepared, and their magnetic properties were characterized in addition to those of epoxy-resin-bonded magnets produced from the coated powders (Cu/Sm2Fe17Nx, Zn/Sm2Fe17Nx and Zn/Cu/Sm2Fe17Nx). The remanence (Br) and maximum energy product [(\\mathit{BH})max] of double metal-coated Zn/Cu/Sm2Fe17Nx powders were maintained at higher levels than those of single Zn metal-coated Sm2Fe17Nx ones (Zn/Sm2Fe17Nx) even after heat treatment at 673 K since the oxidation resistance and thermal stability were effectively improved by formation of the thick and uniform protection layer on the surface of Sm2Fe17Nx particles. Moreover, the epoxy-resin-bonded magnets produced from the Zn/Cu/Sm2Fe17Nx powders possessed good corrosion resistance in air at 393 K which it resulted in the smaller thermal irreversible flux loss than that of uncoated and single Zn metal-coated Sm2Fe17Nx powders in the temperature range of above 393 K.

  3. Fabrication of High Gas Barrier Epoxy Nanocomposites: An Approach Based on Layered Silicate Functionalized by a Compatible and Reactive Modifier of Epoxy-Diamine Adduct

    Directory of Open Access Journals (Sweden)

    Ran Wei

    2018-05-01

    Full Text Available To solve the drawbacks of poor dispersion and weak interface in gas barrier nanocomposites, a novel epoxy-diamine adduct (DDA was synthesized by reacting epoxy monomer DGEBA with curing agent D400 to functionalize montmorillonite (MMT, which could provide complete compatibility and reactivity with a DGEBA/D400 epoxy matrix. Thereafter, sodium type montmorillonite (Na-MMT and organic-MMTs functionalized by DDA and polyether amines were incorporated with epoxy to manufacture nanocomposites. The effects of MMT functionalization on the morphology and gas barrier property of nanocomposites were evaluated. The results showed that DDA was successfully synthesized, terminating with epoxy and amine groups. By simulating the small-angle neutron scattering data with a sandwich structure model, the optimal dispersion/exfoliation of MMT was observed in a DDA-MMT/DGEBA nanocomposite with a mean radius of 751 Å, a layer thickness of 30.8 Å, and only two layers in each tactoid. Moreover, the DDA-MMT/DGEBA nanocomposite exhibited the best N2 barrier properties, which were about five times those of neat epoxy. Based on a modified Nielsen model, it was clarified that this excellent gas barrier property was due to the homogeneously dispersed lamellas with almost exfoliated structures. The improved morphology and barrier property confirmed the superiority of the adduct, which provides a general method for developing gas barrier nanocomposites.

  4. Enhanced microwave shielding and mechanical properties of high loading MWCNT–epoxy composites

    International Nuclear Information System (INIS)

    Singh, B. P.; Prasanta; Choudhary, Veena; Saini, Parveen; Pande, Shailaja; Singh, V. N.; Mathur, R. B.

    2013-01-01

    Dispersion of high loading of carbon nanotubes (CNTs) in epoxy resin is a challenging task for the development of efficient and thin electromagnetic interference (EMI) shielding materials. Up to 20 wt% of multiwalled carbon nanotubes (MWCNTs) loading in the composite was achieved by forming CNT prepreg in the epoxy resin as a first step. These prepreg laminates were then compression molded to form composites which resulted in EMI shielding effectiveness of −19 dB for 0.35 mm thick film and −60 dB at for 1.75 mm thick composites in the X-band (8.2–12.4 GHz). One of the reasons for such high shielding is attributed to the high electrical conductivity of the order of 9 S cm −1 achieved in these composites which is at least an order of magnitude higher than previously reported results at this loading. In addition, an improvement of 40 % in the tensile strength over the neat resin value is observed. Thermal conductivity of the MWCNTs–epoxy composite reached 2.18 W/mK as compared to only 0.14 W/mK for cured epoxy.

  5. Enhanced microwave shielding and mechanical properties of high loading MWCNT-epoxy composites

    Science.gov (United States)

    Singh, B. P.; Prasanta; Choudhary, Veena; Saini, Parveen; Pande, Shailaja; Singh, V. N.; Mathur, R. B.

    2013-04-01

    Dispersion of high loading of carbon nanotubes (CNTs) in epoxy resin is a challenging task for the development of efficient and thin electromagnetic interference (EMI) shielding materials. Up to 20 wt% of multiwalled carbon nanotubes (MWCNTs) loading in the composite was achieved by forming CNT prepreg in the epoxy resin as a first step. These prepreg laminates were then compression molded to form composites which resulted in EMI shielding effectiveness of -19 dB for 0.35 mm thick film and -60 dB at for 1.75 mm thick composites in the X-band (8.2-12.4 GHz). One of the reasons for such high shielding is attributed to the high electrical conductivity of the order of 9 S cm-1 achieved in these composites which is at least an order of magnitude higher than previously reported results at this loading. In addition, an improvement of 40 % in the tensile strength over the neat resin value is observed. Thermal conductivity of the MWCNTs-epoxy composite reached 2.18 W/mK as compared to only 0.14 W/mK for cured epoxy.

  6. The effect of particle addition and fibrous reinforcement on epoxy-matrix composites for severe sliding conditions

    DEFF Research Database (Denmark)

    Larsen, Thomas Ricco Ølholm; Løgstrup Andersen, Tom; Thorning, Bent

    2008-01-01

    This paper reports production and tribological testing of epoxy-matrix composites for dry-sliding conditions. The examined composites are produced using the following components: epoxy resin (EP), glass fiber weave (G), carbon/aramid hybrid weave (CA), PTFE particles and nano-scale CuO particles...... are seen when the fibers are parallel and anti-parallel (P-AP) to the sliding direction compared to normal and parallel (N-P). Experiments with incorporating micro-scale PTFE particles and nano-scale CuO particles, respectively, into the epoxy resin along with the carbon/aramid weave shows no difference...... in friction but minor improvements in wear. When micro-scale PTFE particles are incorporated into the neat epoxy resin, i.e. without fibers, an increase in and a decrease in A are measured. When the same is done with nano-CuO a deterioration of both friction and wear properties are seen. At the three roughest...

  7. Thiol-yne/thiol-epoxy hybrid crosslinked materials based on propargyl modified hyperbranched poly(ethyleneimine) and diglycidylether of bisphenol A resins

    OpenAIRE

    Acebo Gorostiza, Cristina; Fernández Francos, Xavier; Ramis Juan, Xavier; Serra Albet, Àngels

    2016-01-01

    A novel curing methodology based on the combination of thiol-yne and thiol-epoxy click reactions has been developed. The curing process consists of a first photoinitiated thiol-yne reaction, followed by a thermal thiol-epoxy process. As alkyne substrate a new propargyl terminated hyperbranched poly(ethyleneimine) (PEIyne) has been synthesized from the reaction of commercial poly(ethylenimine) (PEI) and glycidyl propargyl ether. The evolution of the curing of different mixtures of PEIyne and d...

  8. High Temperature Epoxy Foam: Optimization of Process Parameters

    Directory of Open Access Journals (Sweden)

    Samira El Gazzani

    2016-06-01

    Full Text Available For many years, reduction of fuel consumption has been a major aim in terms of both costs and environmental concerns. One option is to reduce the weight of fuel consumers. For this purpose, the use of a lightweight material based on rigid foams is a relevant choice. This paper deals with a new high temperature epoxy expanded material as substitution of phenolic resin, classified as potentially mutagenic by European directive Reach. The optimization of thermoset foam depends on two major parameters, the reticulation process and the expansion of the foaming agent. Controlling these two phenomena can lead to a fully expanded and cured material. The rheological behavior of epoxy resin is studied and gel time is determined at various temperatures. The expansion of foaming agent is investigated by thermomechanical analysis. Results are correlated and compared with samples foamed in the same temperature conditions. The ideal foaming/gelation temperature is then determined. The second part of this research concerns the optimization of curing cycle of a high temperature trifunctional epoxy resin. A two-step curing cycle was defined by considering the influence of different curing schedules on the glass transition temperature of the material. The final foamed material has a glass transition temperature of 270 °C.

  9. Enhancing Mechanical and Thermal Properties of Epoxy Nanocomposites via Alignment of Magnetized SiC Whiskers.

    Science.gov (United States)

    Townsend, James; Burtovyy, Ruslan; Aprelev, Pavel; Kornev, Konstantin G; Luzinov, Igor

    2017-07-12

    This research is focused on the fabrication and properties of epoxy nanocomposites containing magnetized SiC whiskers (MSiCWs). To this end, we report an original strategy for fabrication of magnetically active SiCWs by decorating the whiskers with magnetic (iron oxide) nanoparticles via polymer-polymer (poly(acrylic acid)/poly(2-vinyl pyridine)) complexation. The obtained whiskers demonstrated a substantial magnetic response in the polymerizing epoxy resin, with application of only a 20 mT (200 G) magnetic field. We also found that the whiskers chemically reacted with the epoxy resin, causing formation of an extended interphase near the boundary of the whiskers. The SiC whiskers oriented with the magnetic field demonstrated positive effects on the behavior of epoxy-based nanocomposites. Namely, the aligned MSiCWs enhanced the thermomechanical properties of the materials significantly above that of the neat epoxy and epoxy nanocomposite, with randomly oriented whiskers.

  10. Mechanism of adhesion of epoxy resin to steel surface; Tekko hyomen to epoxy jushino secchaku mechanism

    Energy Technology Data Exchange (ETDEWEB)

    Nakazawa, M. [Nippon Steel Corp., Tokyo (Japan)

    1994-08-01

    In the present research, an adhesion-breaking test and a molecular-scale model experiment were conducted to elucidate the adhesion mechanism of epoxy resin (R) to the cold rolled steel sheet (CR) and galvanized steel sheet (GI). As for the adhesive joint strength in the humid environment, the GI is inferior in residual strength to the CR. The GI joint fracture is an interfacial fracture between the plating and adhesive agent, while the CR joint fracture is a combination of cohesive fracture and interfacial fracture. It is attributable to the difference in adhesion mechanism of R and degradation due to humidity between the surface solely of zinc and iron-containing surface. The adhesion state of R to the zinc oxide and iron oxide was observed by temperature-programed desorption in an ultrahigh vacuum. On each of both oxides, the R chemically adsorbs through bond scission between the phenoxy oxide and carbon. If the water dissociatively adsorbs onto the surface, the bond is destroyed between the zinc oxide and R. The formation of interfacial chemical bond contributes to the adhesion of R to the CR and GI. In case of GI, this band is destroyed by the interfacial infiltration of water, while it is not done in case of CR. The CR excels the GI in adhesive durability. 20 refs., 8 figs., 3 tabs.

  11. Determinants of epoxy allergy in the construction industry : a case-control study

    NARCIS (Netherlands)

    Spee, Ton; Timmerman, Johan G; Rühl, Reinhold; Kersting, Klaus; Heederik, Dick J J; Smit, Lidwien A M

    2016-01-01

    BACKGROUND: Workers exposed to epoxy products are at risk of developing allergic contact dermatitis. OBJECTIVES: To compare workers throughout the German construction industry with and without skin allergy to epoxy resins, hardeners, and/or reactive diluents, and to investigate which determinants

  12. Mechanical Reinforcement of Epoxy Composites with Carbon Fibers and HDPE

    Science.gov (United States)

    He, R.; Chang, Q.; Huang, X.; Li, J.

    2018-01-01

    Silanized carbon fibers (CFs) and a high-density polyethylene with amino terminal groups (HDPE) were introduced into epoxy resins to fabricate high-performance composites. A. mechanical characterization of the composites was performed to investigate the effect of CFs in cured epoxy/HDPE systems. The composites revealed a noticeable improvement in the tensile strength, elongation at break, flexural strength, and impact strength in comparison with those of neat epoxy and cured epoxy/HDPE systems. SEM micrographs showed that the toughening effect could be explained by yield deformations, phase separation, and microcracking.

  13. Hydrophobic Modification of Layered Clays and Compatibility for Epoxy Nanocomposites

    Directory of Open Access Journals (Sweden)

    Jiang-Jen Lin

    2010-04-01

    Full Text Available Recent studies on the intercalation and exfoliation of layered clays with polymeric intercalating agents involving poly(oxypropylene-amines and the particular uses for epoxy nanocomposites are reviewed. For intercalation, counter-ionic exchange reactions of clays including cationic layered silicates and anionic Al-Mg layered double hydroxide (LDH with polymeric organic ions afforded organoclays led to spatial interlayer expansion from 12 to 92 Å (X-ray diffraction as well as hydrophobic property. The inorganic clays of layered structure could be modified by the poly(oxypropyleneamine-salts as the intercalating agents with molecular weights ranging from 230 to 5,000 g/mol. Furthermore, natural montmorillonite (MMT clay could be exfoliated into thin layer silicate platelets (ca. 1 nm thickness in one step by using polymeric types of exfoliating agents. Different lateral dimensions of MMT, synthetic fluorinated Mica and LDH clays had been cured into epoxy nanocomposites. The hydrophobic amine-salt modification resulting in high spacing of layered or exfoliation of individual clay platelets is the most important factor for gaining significant improvements of properties. In particular, these modified clays were reported to gain significant improvements such as reduced coefficient of thermal expansion (CTE, enhanced thermal stability, and hardness. The utilization of these layered clays for initiating the epoxy self-polymerization was also reported to have a unique compatibility between clay and organic resin matrix. However, the matrix domain lacks of covalently bonded crosslink and leads to the isolation of powder material. It is generally concluded that the hydrophobic expansion of the clay inter-gallery spacing is the crucial step for enhancing the compatibility and the ultimate preparation of the advanced epoxy materials.

  14. Hydrophobic Modification of Layered Clays and Compatibility for Epoxy Nanocomposites

    Science.gov (United States)

    Lin, Jiang-Jen; Chan, Ying-Nan; Lan, Yi-Fen

    2010-01-01

    Recent studies on the intercalation and exfoliation of layered clays with polymeric intercalating agents involving poly(oxypropylene)-amines and the particular uses for epoxy nanocomposites are reviewed. For intercalation, counter-ionic exchange reactions of clays including cationic layered silicates and anionic Al-Mg layered double hydroxide (LDH) with polymeric organic ions afforded organoclays led to spatial interlayer expansion from 12 to 92 Å (X-ray diffraction) as well as hydrophobic property. The inorganic clays of layered structure could be modified by the poly(oxypropylene)amine-salts as the intercalating agents with molecular weights ranging from 230 to 5,000 g/mol. Furthermore, natural montmorillonite (MMT) clay could be exfoliated into thin layer silicate platelets (ca. 1 nm thickness) in one step by using polymeric types of exfoliating agents. Different lateral dimensions of MMT, synthetic fluorinated Mica and LDH clays had been cured into epoxy nanocomposites. The hydrophobic amine-salt modification resulting in high spacing of layered or exfoliation of individual clay platelets is the most important factor for gaining significant improvements of properties. In particular, these modified clays were reported to gain significant improvements such as reduced coefficient of thermal expansion (CTE), enhanced thermal stability, and hardness. The utilization of these layered clays for initiating the epoxy self-polymerization was also reported to have a unique compatibility between clay and organic resin matrix. However, the matrix domain lacks of covalently bonded crosslink and leads to the isolation of powder material. It is generally concluded that the hydrophobic expansion of the clay inter-gallery spacing is the crucial step for enhancing the compatibility and the ultimate preparation of the advanced epoxy materials.

  15. Revestimentos de alta camada obtidos com a modificação de resinas epóxi novolaca pela reação com organo-siloxano e catálise ácida

    Directory of Open Access Journals (Sweden)

    Roberta Jachura Rocha

    Full Text Available Epoxy resins are an important class of thermostable polymers, widely used in structural applications or as adhesives. However, the low fracture resistance is their main weakness in many applications. Due to this fact, this study aims to modify a polymer matrix based on a novolac epoxy resin with an organo siloxane (AMS. The final properties of cured epoxys resins are affected by the curing process and the coatings modified in this study with AMS and cured with acid catalyst presented greater resistance to thermal decomposition compared to that cured with Aradur, demonstrating a higher content of crosslinking in the siloxane polyether and the novolak epoxy resin chains. This epoxy matrix modified was used to prepare coatings whose films applied to 1020 steel surfaces presented a resistance of 1010 Ohm-cm-2. This resistance value is one order of magnitude greater than that of epoxy resins films modified by siloxanes in published studies, which demonstrates a potential economy in terms of maintenance costs of metal structures and machines used in power plants (UTE. To obtain the developed inks in pilot plant scale, it was used an aromatic polyamine as curing agent, characterizing the product obtained as an epoxy bi-component paint for commercial use.

  16. Characterization of epoxy hybrid composites filled with cellulose fibers and nano-SiC

    KAUST Repository

    Alamri, H.; Low, I. M.

    2012-01-01

    Three different approaches have been applied and investigated to enhance the thermal and mechanical properties of epoxy resin. Epoxy system reinforced with either recycled cellulose fibers (RCF) or nanosilicon carbide (n-SiC) particles as well

  17. A novel calorimetry technique for monitoring electron beam curing of polymer resins

    International Nuclear Information System (INIS)

    Chen, J.H.; Johnston, A.; Petrescue, L.; Hojjati, M.

    2006-01-01

    This paper describes the development of a calorimetry-based technique for monitoring of the curing of electron beam (EB) curable resins, including design of the calorimeter hardware and the development of an analytical model for calculating resin cure rates and radiation dose. Factors affecting the performance of the calorimeter were investigated. Experimental trials monitoring the curing of epoxy resin were conducted under single pass and multiple passes of EB irradiation. Results show that the developed calorimeter is a simple, inexpensive and reasonably accurate technique for monitoring the EB curing of cationic epoxies

  18. Adhesives from modified soy protein

    Science.gov (United States)

    Sun, Susan [Manhattan, KS; Wang, Donghai [Manhattan, KS; Zhong, Zhikai [Manhattan, KS; Yang, Guang [Shanghai, CN

    2008-08-26

    The present invention provides useful adhesive compositions having similar adhesive properties to conventional UF and PPF resins. The compositions generally include a protein portion and modifying ingredient portion selected from the group consisting of carboxyl-containing compounds, aldehyde-containing compounds, epoxy group-containing compounds, and mixtures thereof. The composition is preferably prepared at a pH level at or near the isoelectric point of the protein. In other preferred forms, the adhesive composition includes a protein portion and a carboxyl-containing group portion.

  19. Development of sealed radioactive sources immobilized in epoxy resin for verification of detectors used in nuclear medicine; Desenvolvimento de fontes radioativas seladas imobilizadas em resina epoxi para verificacao de detectores utilizados em medicina nuclear

    Energy Technology Data Exchange (ETDEWEB)

    Tiezzi, Rodrigo

    2016-07-01

    The radioactive sealed sources are used in verification ionization chamber detectors, which measure the activity of radioisotopes used in several areas, such as in nuclear medicine. The measurement of the activity of radioisotopes must be made with accuracy, because it is administered to a patient. To ensure the proper functioning of the ionization chamber detectors, standardized tests are set by the International Atomic Energy Agency (IAEA) and the National Nuclear Energy Commission using sealed radioactive sources of Barium-133, Cesium-137 and Cobalt-57. The tests assess the accuracy, precision, reproducibility and linearity of response of the equipment. The focus of this work was the study and the development of these radioactive sources with standard Barium-133 and Cesium-137,using a polymer, in case commercial epoxy resin of diglycidyl ether of bisphenol A (DGEBA) and a curing agent based on modified polyamine diethylenetriamine (DETA), to immobilize the radioactive material. The polymeric matrix has the main function of fix and immobilize the radioactive contents not allowing them to leak within the technical limits required by the standards of radiological protection in the category of characteristics of a sealed source and additionally have the ability to retain the emanation of any gases that may be formed during the manufacture process and the useful life of this artifact. The manufacturing process of a sealed source standard consists of the potting ,into bottle standardized geometry, in fixed volume of a quantity of a polymeric matrix within which is added and dispersed homogeneously to need and exact amount in activity of the radioactive materials standards. Accordingly, a study was conducted for the choice of epoxy resin, analyzing its characteristics and properties. Studies and tests were performed, examining the maximum miscibility of the resin with the water (acidic solution, simulating the conditions of radioactive solution), loss of mechanical and

  20. UV irradiation improves the bond strength of resin cement to fiber posts.

    Science.gov (United States)

    Zhong, Bo; Zhang, Yong; Zhou, Jianfeng; Chen, Li; Li, Deli; Tan, Jianguo

    2011-01-01

    The purpose is to evaluate the effect of UV irradiation on the bond strength between epoxy-based glass fiber posts and resin cement. Twelve epoxy-based glass fiber posts were randomly divided into three groups. Group 1 (Cont.): No surface treatment. Group 2 (Low-UV): UV irradiation was conducted from a distance of 10 cm for 10 min. Group 3 (High-UV): UV irradiation was conducted from a distance of 1 cm for 3 min. A resin cement (CLEARFIL SA LUTING) was used for the post cementation to form resin slabs which contained fiber posts in the center. Microtensile bond strengths were tested and the mean bond strengths (MPa) were 18.81 for Cont. group, 23.65 for Low-UV group, 34.75 for High-UV group. UV irradiation had a significant effect on the bond strength (pUV irradiation demonstrates its capability to improve the bond strength between epoxy-based glass fiber posts and resin cement.

  1. A Twofold Comparison between Dual Cure Resin Modified Cement and Glass Ionomer Cement for Orthodontic Band Cementation.

    Science.gov (United States)

    Attar, Hanaa El; Elhiny, Omnia; Salem, Ghada; Abdelrahman, Ahmed; Attia, Mazen

    2016-12-15

    To test the solubility of dual cure resin modified resin cement in a food simulating solution and the shear bond strength compared to conventional Glass ionomer cement. The materials tested were self-adhesive dual cure resin modified cement and Glass Ionomer (GIC). Twenty Teflon moulds were divided into two groups of tens. The first group was injected and packed with the modified resin cement, the second group was packed with GIC. To test the solubility, each mould was weighed before and after being placed in an analytical reagent for 30 days. The solubility was measured as the difference between the initial and final drying mass. To measure the Shear bond strength, 20 freshly extracted wisdom teeth were equally divided into two groups and embedded in self-cure acrylic resin. Four mm sections of stainless steel bands were cemented to the exposed buccal surfaces of teeth under a constant load of 500 g. Shear bond strength was measured using a computer controlled materials testing machine and the load required to deband the samples was recorded in Newtons. GIC showed significantly higher mean weight loss and an insignificant lower Shear bond strength, compared to dual cure resin Cement. It was found that dual cure resin modified cement was less soluble than glass ionomer cement and of comparable bond strength rendering it more useful clinically for orthodontic band cementation.

  2. Effect of silane coupling agent on interfacial adhesion of copper/glass fabric/epoxy composites

    International Nuclear Information System (INIS)

    Langroudi, A. E.; Yousefi, A. A.; Kabiri, Kourosh

    2003-01-01

    The effect of silane coupling agent on the peel strength of copper/prep reg/copper composites was investigated. The composite consisted of one or two sheets of prepress covered by two copper plates. The prep reg was prepared by hand dry-lay-up technique using an epoxy resin and an electrical resistant glass fabric (e-glass style 2165). 4,4'-methylene dianiline. An aromatic amine, was used as curing agent. curing times for prep reg and composite at 120 d ig C and 170 d ig C were 15 min and 1 h, respectively. γ-aminopropyl trimethoxy silane was used as coupling agent. The effect of aminopropyl trimethoxy silane on the adhesion of epoxy/glass and epoxy/copper interfaces was investigated by two methods. In the first method, the surface of the glass fabric and/or the copper plates were treated by aminopropyl trimethoxy silane. In the second method, aminopropyl trimethoxy silane was directly added to epoxy resin. In addition, the effect of additional resin on the adhesion strength was also studied by the latter method

  3. Exploring biomass based carbon black as filler in epoxy composites: Flexural and thermal properties

    International Nuclear Information System (INIS)

    Abdul Khalil, H.P.S.; Firoozian, P.; Bakare, I.O.; Akil, Hazizan Md.; Noor, Ahmad Md.

    2010-01-01

    Carbon blacks (CB), derived from bamboo stem (BS-CB), coconut shells (CNS-CB) and oil palm empty fiber bunch (EFB-CB), were obtained by pyrolysis of fibers at 700 o C, characterized and used as filler in epoxy composites. The results obtained showed that the prepared carbon black possessed well-developed porosities and are predominantly made up of micropores. The BS-CB, CNS-CB and EFB-CB filled composites were prepared and characterized using scanning electron microscope (SEM) and thermogravimetric analyzer (TGA). The SEM showed that the fractured surface of the composite indicates its high resistance to fracture. The CBs-epoxy composites exhibited better flexural properties than the neat epoxy, which was attributed to better adhesion between the CBs and the epoxy resin. TGA showed that there was improvement in thermal stability of the carbon black filled composites compared to the neat epoxy resin.

  4. Static and Dynamic Mechanical Properties of Graphene Oxide-Incorporated Woven Carbon Fiber/Epoxy Composite

    Science.gov (United States)

    Adak, Nitai Chandra; Chhetri, Suman; Kim, Nam Hoon; Murmu, Naresh Chandra; Samanta, Pranab; Kuila, Tapas

    2018-03-01

    This study investigates the synergistic effects of graphene oxide (GO) on the woven carbon fiber (CF)-reinforced epoxy composites. The GO nanofiller was incorporated into the epoxy resin with variations in the content, and the CF/epoxy composites were manufactured using a vacuum-assisted resin transfer molding process and then cured at 70 and 120 °C. An analysis of the mechanical properties of the GO (0.2 wt.%)/CF/epoxy composites showed an improvement in the tensile strength, Young's modulus, toughness, flexural strength and flexural modulus by 34, 20, 83, 55 and 31%, respectively, when compared to the CF/epoxy composite. The dynamic mechanical analysis of the composites exhibited an enhancement of 56, 114 and 22% in the storage modulus, loss modulus and damping capacity (tan δ), respectively, at its glass transition temperature. The fiber-matrix interaction was studied using a Cole-Cole plot analysis.

  5. Corrosion behavior of duplex polyaniline/epoxy coating on mild steel in 3% NaCl

    Directory of Open Access Journals (Sweden)

    Gvozdenović Milica M.

    2005-01-01

    Full Text Available The corrosion behavior and thermal stability of epoxy coatings electrodeposited on mild steel and on mild steel with electrochemically deposited polyaniline (PANI film were investigated by electrochemical impedance spectroscopy (EIS and thermo gravimetric analysis (TGA. The aim of the paper was to present new findings on the corrosion protection of mild steel by a duplex PANI/-epoxy coating in 3% NaCI solution and to determine the effect of thin PANI film on the protective properties of the coating. PANI film was deposited electrochemically on mild steel from an aqueous solution of 0.5 mol dm"3 sodium benzoate and 0.1 mol dm"3 aniline at a constant current density of 1.5 mA cm"2. Non-pigmented epoxy coatings on mild steel and on mild steel with PANI film were obtained by cathodic electrode position at constant voltage and stirring conditions. The resin concentration in the electrode position bath was 10 wt.% solid dispersion in water at pH 5.7. The applied voltage was 250 V, the temperature 26°C and the deposition time 3 min. It was shown that thin PANI film could be used to modify the surface of mild steel prior to epoxy coating deposition, due to the increased corrosion protection of a duplex PANI/epoxy coating comparing to an epoxy coating on mild steel in 3% NaCl solution.

  6. Electrical Tracking Formation on Silane Epoxy Resin under Various Contaminants

    Directory of Open Access Journals (Sweden)

    NFN Rochmadi

    2013-03-01

    Full Text Available Contamination at the surface of the insulator becomes a serious problem in power system operation, especially for the tropical area. Humidity and rainfall play an important role in wetness by the water at the surface of the insulator, which result in the presence of contaminant and leakage current flowing at the surface of the insulator. This leakage current will generate heat which occurs at the surface of an insulator, so that dry band area will be formed. This ultimately leads to flashover. This paper presents the influence of contaminants to leakage current and formation of electrical tracking at the surface of epoxy resin compound wit silicon rubber. The test was based on Inclined-Planed Tracking method with NH4Cl as contaminants. The industrial and coastal contaminants are used to explain the effect of contaminant at surface tracking process. The flow rate of contaminant was 0.3 ml/min. The 3.5 kV AC high voltage 50 Hz was applied to the top electrodes. It is found that industrial contamination resulting in the smallest surface leakage current is 327.6 mA. Also it is found that coastal contaminant (1420 mS/cm showed the severest damage at surface of test sample. Therefore, special treatment of the sample are needed under these conditions so that the material performance can be improved, especially against the electrical tracking.

  7. Advanced resin systems and 3D textile preforms for low cost composite structures

    Science.gov (United States)

    Shukla, J. G.; Bayha, T. D.

    1993-01-01

    Advanced resin systems and 3D textile preforms are being evaluated at Lockheed Aeronautical Systems Company (LASC) under NASA's Advanced Composites Technology (ACT) Program. This work is aimed towards the development of low-cost, damage-tolerant composite fuselage structures. Resin systems for resin transfer molding and powder epoxy towpreg materials are being evaluated for processability, performance and cost. Three developmental epoxy resin systems for resin transfer molding (RTM) and three resin systems for powder towpregging are being investigated. Various 3D textile preform architectures using advanced weaving and braiding processes are also being evaluated. Trials are being conducted with powdered towpreg, in 2D weaving and 3D braiding processes for their textile processability and their potential for fabrication in 'net shape' fuselage structures. The progress in advanced resin screening and textile preform development is reviewed here.

  8. Mechanical performance optimization of neutron shielding material based on short carbon fiber reinforced B4C/epoxy resin

    International Nuclear Information System (INIS)

    Wang Peng; Tang Xiaobin; Chen Feida; Chen Da

    2013-01-01

    To satisfy engineering requirements for mechanics performance of neutron shielding material, short carbon fiber was used to reinforce the traditional containing B 4 C neutron shielding material and effects of fiber content, length and surface treatment to mechanics performance of material was discussed. Based on Americium-Beryllium neutron source, material's neutron shielding performance was tested. The result of experiment prove that tensile strength of material which the quality ratio of resin and fiber is 5:1 is comparatively excellent for 10wt% B 4 C of carbon fiber reinforced epoxy resin. The tensile properties of material change little with the fiber length ranged from 3-10 mm The treatment of fiber surface with silane coupling agent KH-550 can increase the tensile properties of materials by 20% compared with the untreated of that. A result of shielding experiment that the novel neutron shielding material can satisfy the neutron shielding requirements can be obtained by comparing with B 4 C/polypropylene materials. The material has good mechanical properties and wide application prospect. (authors)

  9. Bond Strength of Silorane- and Methacrylate-Based Composites to Resin-Modified Glass Ionomers

    Science.gov (United States)

    2012-01-13

    genre was given the name of resin-modified glass ionomers (RMGI) (Antonucci et al., 1988). The addition of resin improved many of the drawbacks of...entire surface for 15 seconds then gentle air was used to create an even film over the sample. This layer was cured for 10 seconds using the Bluephase

  10. The impact of nano-coating on surface charge accumulation of epoxy resin insulator: characteristic and mechanism

    Science.gov (United States)

    Qi, Bo; Gao, Chunjia; Lv, Yuzhen; Li, Chengrong; Tu, Youping; Xiong, Jun

    2018-06-01

    The flashover phenomenon of the insulator is the main cause for insulating failure of GIS/GIL, and one of the most critical impacting factors is the accumulation of surface charge. The common methods to restrain the surface charge accumulation are reviewed in this paper. Through the reasonable comparison and analysis of these methods, nano-coatings for the insulator were selected as a way to restrain the surface charge accumulation. Based on this, six nano-coated epoxy resin samples with different concentrations of P25-TiO2 nanoparticles were produced. A high precision 3D surface charge measurement system was developed in this paper with a spatial resolution of 4.0 mm2 and a charge resolution of 0.01 µC (m2 · mV)‑1. The experimental results for the epoxy resin sample showed that with the concentration of nanoparticles of the coating material increasing, the surface charge density tended to first decrease and then increase. In the sample coated with 0.5% concentration of nanoparticles, the suppression effect is the optimum, leading to a 63.8% reduction of charge density under DC voltage. The application test for actual nano-coated GIS/GIL basin insulator indicated that the maximum suppression degree for the charge density under DC voltage could reach 48.3%, while it could reach 22.2% for switching impulse voltage and 12.5% for AC context. The control mechanism of nano-coatings on charge accumulation was proposed based on the analysis for surface morphology features and traps characteristics; the shallow traps dominate in the migration of charges while the deep traps operate on the charge accumulation. With the concentration of nanoparticles in nano-coating material mounting up, the density of shallow traps continuously increases, while for deep traps, it first decreases and then increases. For the sample with 0.5% concentration of nanoparticles coated, the competition between shallow traps and deep traps comes to the most balanced state, producing the most

  11. Characterization of Polyimide Matrix Resins and Prepregs

    Science.gov (United States)

    Maximovich, M. G.; Galeos, R. M.

    1985-01-01

    Graphite/polyimide composite materials are attractive candidates for a wide range of aerospace applications. They have many of the virtues of graphite/epoxies, i.e., high specific strengths and stiffness, and also outstanding thermal/oxidative stability. Yet they are not widely used in the aerospace industry due to problems of procesability. By their nature, modern addition polyimide (PI) resins and prepregs are more complex than epoxies; the key to processing lies in characterizing and understanding the materials. Chemical and rheological characterizations are carried out on several addition polyimide resins and graphite reinforced prepregs, including those based on PMR-15, LARC 160 (AP 22), LARC 160 (Curithane 103) and V378A. The use of a high range torque transducer with a Rheometrics mechanical spectrometer allows rheological data to be generated on prepreg materials as well as neat resins. The use of prepreg samples instead of neat resins eliminates the need for preimidization of the samples and the data correlates well with processing behavior found in the shop. Rheological characterization of the resins and prepregs finds significant differences not readily detected by conventional chemical characterization techniques.

  12. Fabrication and mechanical properties of multi-walled carbon nanotubes/epoxy nanocomposites

    International Nuclear Information System (INIS)

    Yeh, M.-K.; Hsieh, T.-H.; Tai, N.-H.

    2008-01-01

    Carbon nanotubes have better physical and mechanical behavior than the traditional materials. In this study, the multi-walled carbon nanotubes (MWNTs) were added to the epoxy resin as a reinforcement to fabricate MWNTs/epoxy nanocomposites. The pressure and temperature were applied to cure the MWNTs/epoxy compound by hot press method. Mechanical properties such as tensile strength, Young's modulus, and Poisson's ratio were measured. The effect of weight percentages of the MWNTs was investigated. Morphologies of the fracture surface of MWNTs/epoxy nanocomposites were observed by scanning electron microscope

  13. Generalized morphea/eosinophilic fasciitis overlap after epoxy exposure

    Directory of Open Access Journals (Sweden)

    Warren H. Chan, MS

    2018-03-01

    Full Text Available Generalized morphea is associated with epoxy resin vapors and is characterized by the development of lesions shortly after exposure. Morphea presenting along with eosinophilic fasciitis (EF, or morphea/EF overlap, is rare and an indicator of poor prognosis and resistance to treatment. Here we present a case of generalized morphea/EF overlap linked to epoxy exposure. Our patient received multiple therapies—ultraviolet A1 phototherapy, prednisone, methotrexate, azathioprine, mycophenolate mofetil, cyclophosphamide, cyclosporine, and rituximab—none of which led to a significant response. The refractory nature of this disease warrants vigilance in its association with epoxy exposure.

  14. Leakage Current Waveforms and Arcing Characteristics of Epoxy Resin for Outdoor Insulators under Clean and Salt Fogs

    Directory of Open Access Journals (Sweden)

    Suwarno

    2008-05-01

    Full Text Available Ceramic outdoor insulators have been used in high voltage transmission lines since long time ago. Due to superiority in their resistance to pollution, recently, polymeric outdoor insulators are widely used. Epoxy resin is one polymer which shows good properties for outdoor insulation. During service, outdoor insulators may severe a certain degree of pollution which may reduce their surface resistance. Leakage current (LC usually increase and degradation may take place. This paper reports experimental results on the leakage current waveforms and arcing characteristics of epoxy resin under clean and salt fog. The samples used are blocks of epoxy resin with dimension of 250 x 50 x 20 mm3. The samples were put in a test chamber with dimension of 900x900x1200 mm3 with controllable humidity and pollution conditions. Clean and salt fog were generated according to IEC 60-1 and 507. The arcing experiment was done with incline plane test in accordance with IEC 587. AC voltage in the range from 5 kV to 50 kV with frequency of 50 Hz was applied. The LC waveforms up to flash over were measured. The magnitudes as well as harmonic content of the LC were analyzed. The correlation between LC waveforms and dry band arching phenomenon was elaborated. Visual observation of the arc on the sample surfaces was observed using a video camera. Experimental results indicated that LC magnitude on clean samples was slightly affected by humidity (RH. However, under salt fog, RH greatly affected the LC magnitude. The flashover voltage of clean samples under salt fog reduced significantly for fog conductivity of more than 1.2 mS/cm. Kaolin-polluted samples under salt fog showed an Ohmic behaviour. The LC magnitude was high and a large discrepancy of LC magnitude was observed for high applied voltage of larger than 25 kV. The largest LC magnitude was observed on salt-kaolin polluted samples under clean fog at high RH. LC waveforms analysis indicated that in general LC waveforms

  15. Wear Behavior of Woven Roving Aramid / Epoxy Composite under Different Conditions

    Directory of Open Access Journals (Sweden)

    Asad A. Khalid

    2012-09-01

    Full Text Available Wear behavior studies of aramid woven roving /epoxy composite has been conducted. Sliding the material against smooth steel counter face under dry and  lubricated with oil conditions has been investigated. Powder of Silicon carbide has been mixed with the epoxy resin and tested also. The powder was mixed in a volumetric fraction of 10% with the epoxy resin. Four Laminates of six layers were fabricated by hand lay up  method. A pin on disc apparatus has been fabricated to conduct the sliding wear tests on specimens of (4 mm   4 mm   12 mm in size have been cut from the four laminates. The effect of sliding condition including dry, lubricated, dry with additives and lubricated with additives have been studied. Wear rate tests have been conducted at different sliding speeds and loads. Results show that the wear characteristics are influenced by the operating conditions and the construction of the composite material used. It was also found that the wear of aramid /epoxy composite onto the steel counter face were significantly reduced by using lubricant and additives but still took place.Keywords: Wear, Composite materials, Woven roving aramid, Epoxy, Additives, Lubricant.

  16. Adhesion between coating layers based on epoxy and silicone

    DEFF Research Database (Denmark)

    Svendsen, Jacob R.; Kontogeorgis, Georgios; Kiil, Søren

    2007-01-01

    The adhesion between a silicon tie-coat and epoxy primers, used in marine coating systems, has been studied in this work. Six epoxy coatings (with varying chain lengths of the epoxy resins), some of which have shown problems with adhesion to the tie-coat during service life, have been considered....... The experimental investigation includes measurements of the surface tension of the tie-coat and the critical surface tensions of the epoxies, topographic investigation of the surfaces of cured epoxy coatings via atomic force microscopy (AFM), and pull-off tests for investigating the strength of adhesion...... to the silicon/epoxy systems. Calculations for determining the roughness factor of the six epoxy coatings (based on the AFM topographies) and the theoretical work of adhesion have been carried out. The coating surfaces are also characterized based on the van Oss-Good theory. Previous studies on the modulus...

  17. Characterization of cure kinetics and physical properties of a high performance, glass fiber-reinforced epoxy prepreg and a novel fluorine-modified, amine-cured commercial epoxy

    Science.gov (United States)

    Bilyeu, Bryan

    Kinetic equation parameters for the curing reaction of a commercial glass fiber reinforced high performance epoxy prepreg composed of the tetrafunctional epoxy tetraglycidyl 4,4-diaminodiphenyl methane (TGDDM), the tetrafunctional amine curing agent 4,4'-diaminodiphenylsulfone (DDS) and an ionic initiator/accelerator, are determined by various thermal analysis techniques and the results compared. The reaction is monitored by heat generated determined by differential scanning calorimetry (DSC) and by high speed DSC when the reaction rate is high. The changes in physical properties indicating increasing conversion are followed by shifts in glass transition temperature determined by DSC, temperature-modulated DSC (TMDSC), step scan DSC and high speed DSC, thermomechanical (TMA) and dynamic mechanical (DMA) analysis and thermally stimulated depolarization (TSD). Changes in viscosity, also indicative of degree of conversion, are monitored by DMA. Thermal stability as a function of degree of cure is monitored by thermogravimetric analysis (TGA). The parameters of the general kinetic equations, including activation energy and rate constant, are explained and used to compare results of various techniques. The utilities of the kinetic descriptions are demonstrated in the construction of a useful time-temperature-transformation (TTT) diagram and a continuous heating transformation (CHT) diagram for rapid determination of processing parameters in the processing of prepregs. Shrinkage due to both resin consolidation and fiber rearrangement is measured as the linear expansion of the piston on a quartz dilatometry cell using TMA. The shrinkage of prepregs was determined to depend on the curing temperature, pressure applied and the fiber orientation. Chemical modification of an epoxy was done by mixing a fluorinated aromatic amine (aniline) with a standard aliphatic amine as a curing agent for a commercial Diglycidylether of Bisphenol-A (DGEBA) epoxy. The resulting cured network

  18. Development of high radiation-resistant glass fiber reinforced plastics with cyanate-based resin for superconducting magnet systems

    Energy Technology Data Exchange (ETDEWEB)

    Idesaki, Akira, E-mail: idesaki.akira@qst.go.jp [Quantum Beam Science Directorate, Japan Atomic Energy Agency, Watanuki 1233, Takasaki, Gunma 370-1292 (Japan); Nakamoto, Tatsushi [Cryogenic Science Center, High Energy Accelerator Research Organization (KEK), 1-1 Oho, Tsukuba, Ibaraki 305-0801 (Japan); Yoshida, Makoto [Institute of Particle and Nuclear Studies, High Energy Accelerator Research Organization (KEK), 1-1 Oho, Tsukuba, Ibaraki 305-0801 (Japan); Shimada, Akihiko [Quantum Beam Science Directorate, Japan Atomic Energy Agency, Watanuki 1233, Takasaki, Gunma 370-1292 (Japan); Iio, Masami; Sasaki, Kenichi; Sugano, Michinaka [Cryogenic Science Center, High Energy Accelerator Research Organization (KEK), 1-1 Oho, Tsukuba, Ibaraki 305-0801 (Japan); Makida, Yasuhiro [Institute of Particle and Nuclear Studies, High Energy Accelerator Research Organization (KEK), 1-1 Oho, Tsukuba, Ibaraki 305-0801 (Japan); Ogitsu, Toru [Cryogenic Science Center, High Energy Accelerator Research Organization (KEK), 1-1 Oho, Tsukuba, Ibaraki 305-0801 (Japan)

    2016-11-15

    Highlights: • GFRPs for superconducting magnet systems were developed. • Cyanate-based resins were used for GFRPs as matrices. • Radiation resistance was evaluated based on gas evolution and mechanical properties. • GFRP with bismaleimide-triazine resin exhibited excellent radiation resistance. - Abstract: Glass fiber reinforced plastics (GFRPs) with cyanate ester resin/epoxy resin, bismaleimide resin/epoxy resin, and bismaleimide-triazine resin as matrices were developed for the superconducting magnet systems used in high intensity accelerators. The radiation resistance of these GFRPs was evaluated based on their gas evolution and changes in their mechanical properties after gamma-ray irradiation with dose of 100 MGy in vacuum at ambient temperature. After irradiation, a small amount of gas was evolved from all of the GFRPs, and a slight decrease in mechanical properties was observed compared with the conventional epoxy resin-GFRP, G10. Among the GFRPs, the smallest amount of gas (6 × 10{sup −5} mol/g) was evolved from the GFRP with the bismaleimide-triazine resin, which also retained more than 88% of its flexural strength after 100 MGy irradiation; this GFRP is thus considered the most promising material for superconducting magnet systems.

  19. Novel epoxy-benzoxazine water-based emulsions with reactive benzoxazine surfactants for coatings

    Directory of Open Access Journals (Sweden)

    M. Krajnc

    2014-08-01

    Full Text Available Novel epoxy-benzoxazine emulsions designed for water-based coatings were prepared and investigated. Bisphenol A-based epoxy resins with molar weights of 340, 377 and 1750 g/mol along with epoxidized soybean oil were emulsified using mono- and bi-functional benzoxazine surfactants, which are able to react with epoxy resins at their cure temperature. The structure of synthesized surfactants carrying one or two polyether chains was confirmed using Fourier transform infrared spectroscopy, 1H nuclear magnetic resonance and differential scanning calorimetry. Stability of emulsions was verified by particle diameters measurements. Coatings, made directly from emulsions, were dried and cured at elevated temperature using 3,3'-dimetoxybenzidine as curing agent to ensure a highly cross-linked structure of thermosetting films. Curing process, thermal properties and hardness of cured films were investigated. It was found that benzoxazine molecules were well incorporated into the epoxy network upon curing, which ensures no void structure of cured copolymer and enhanced coating properties.

  20. Degradation of basalt fibre and glass fibre/epoxy resin composites in seawater

    International Nuclear Information System (INIS)

    Wei Bin; Cao Hailin; Song Shenhua

    2011-01-01

    Research highlights: → BFRP degradation process in seawater environment was first investigated. → The mass gain change includes two effects: absorption and extraction. → The interfacial adhesion of BFRP is bigger than GFRP. → After treated, the bending strength of BFRP is lower than GFRP. → Reducing the Fe 2+ in the basalt fibre could lead to a higher stability of BFRP. - Abstract: Epoxy resins reinforced, respectively, by basalt fibres and glass fibres were treated with a seawater solution for different periods of time. Both the mass gain ratio and the strength maintenance ratio of the composites were examined after the treatment. The fracture surfaces were characterized using scanning electron microscopy. The tensile and bending strengths of the seawater treated samples showed a decreasing trend with treating time. In general, the anti-seawater corrosion property of the basalt fibre reinforced composites was almost the same as that of the glass fibre reinforced ones. Based on the experimental results, possible corrosion mechanisms were explored, indicating that an effective lowering of the Fe 2+ content in the basalt fibre could lead to a higher stability for the basalt fibre reinforced composites in a seawater environment.

  1. Carbon nanotube epoxy nanocomposites: the effects of interfacial modifications on the dynamic mechanical properties of the nanocomposites.

    Science.gov (United States)

    Yoonessi, Mitra; Lebrón-Colón, Marisabel; Scheiman, Daniel; Meador, Michael A

    2014-10-08

    Surface functionalization of pretreated carbon nanotubes (CNT) using aromatic, aliphatic, and aliphatic ether diamines was performed. The pretreatment of the CNT consisted of either acid- or photo-oxidation. The acid treated CNT had a higher initial oxygen content compared to the photo-oxidized CNT and this resulted in a higher density of functionalization. X-ray photoelectron spectroscopy (XPS) and thermal gravimetric analysis (TGA) were used to verify the presence of the oxygenated and amine moieties on the CNT surfaces. Epoxy/0.1 wt % CNT nanocomposites were prepared using the functionalized CNT and the bulk properties of the nanocomposites were examined. Macroscale correlations between the interfacial modification and bulk dynamic mechanical and thermal properties were observed. The amine modified epoxy/CNT nanocomposites exhibited up to a 1.9-fold improvement in storage modulus (G') below the glass transition (Tg) and up to an almost 4-fold increase above the Tg. They also exhibited a 3-10 °C increase in the glass transition temperature. The aromatic diamine surface modified epoxy/CNT nanocomposites resulted in the largest increase in shear moduli below and above the Tg and the largest increase in the Tg. Surface examination of the nanocomposites with scanning electron microscopy (SEM) revealed indications of a greater adhesion of the epoxy resin matrix to the CNT, most likely due to the covalent bonding.

  2. SETH 200: new mobile unit for spent ion-exchange resins embedding in polymers

    International Nuclear Information System (INIS)

    de Buzonniere, A.; Raibaud, J.; Augustin, X.

    1985-01-01

    The CEA embedding process for low- and medium-activity waste in thermosetting resins (polyester or epoxy) has been used industrially. Recent developments (elimination of chemical pretreatment thanks to a new epoxy formulation and technological breakthroughs in the operating techniques) have greatly increased the potential of the process and have allowed with Technicatome's industrial experience, the elaboration of a new mobile unit easily operated and very competitive, particularly in spent resin processing

  3. Bending characteristics of resin concretes

    Directory of Open Access Journals (Sweden)

    Ribeiro Maria Cristina Santos

    2003-01-01

    Full Text Available In this research work the influence of composition and curing conditions in bending strength of polyester and epoxy concrete is analyzed. Various mixtures of resin and aggregates were considered in view of an optimal combination. The Taguchi methodology was applied in order to reduce the number of tests, and in order to evaluate the influence of various parameters in concrete properties. This methodology is very useful for the planning of experiments. Test results, analyzed by this methodology, shown that the most significant factors affecting bending strength properties of resin concretes are the type of resin, resin content and charge content. An optimal formulation leading to a maximum bending strength was achieved in terms of material parameters.

  4. Surface Modified Characteristics of the Tetracalcium Phosphate as Light-Cured Composite Resin Fillers

    Directory of Open Access Journals (Sweden)

    Wen-Cheng Chen

    2014-01-01

    Full Text Available The objectives of this study are to characterize the properties of light-cured composite resins that are reinforced with whisker surface-modified particles of tetracalcium phosphate (TTCP and to investigate the influence of thermal cycling on the reinforced composites properties. The characteristics of ultimate diametral tensile strength (DTS, moduli, pH values, and fracture surfaces of the samples with different amounts of surface-modified TTCP (30%–60% were determined before and after thermal cycling between 5°C and 55°C in deionized water for 600 cycles. The trends of all groups were ductile prior to thermal cycling and the moduli of all groups increased after thermal cycling. The ductile property of the control group without filler was not significantly affected. Larger amounts of fillers caused the particles to aggregate, subsequently decreasing the resin’s ability to disperse external forces and leading to brittleness after thermal cycling. Therefore, the trend of composite resins with larger amounts of filler would become more brittle and exhibited higher moduli after thermal cycling. This developed composite resin with surface modified-TTCP fillers has the potential to be successful dental restorative materials.

  5. Carbon nanotube (CNT)–epoxy nanocomposites: a systematic investigation of CNT dispersion

    International Nuclear Information System (INIS)

    Chakraborty, Amit K.; Plyhm, Tiia; Barbezat, Michel; Necola, Adly; Terrasi, Giovanni P.

    2011-01-01

    A systematic investigation of the dispersion of carbon nanotubes (CNTs), 1–6 nm in diameter and a few microns in length, in a bisphenol F-based epoxy resin has been presented. Several dispersing techniques including high-speed dissolver, ultrasonic bath/horn, 3-roll mill, etc. have been employed. Optical microscopy has been extensively used to systematically characterise the state of CNT dispersion in the epoxy resin during the entire processing cycle from mixing CNT with resin to adding and curing with hardener. Complimentary viscosity measurements were also performed at various stages of nanocomposite processing. A method to produce a good CNT dispersion in resin was established, but the state of CNT dispersion was found to be extremely sensitive to its physical and chemical environments. The cured nanocomposites were further tested for their thermo-mechanical properties by dynamic mechanical thermal analysis (DMTA), and for flexural and compressive mechanical properties. The measured properties of various nanocomposite plates were then discussed in view of the corresponding CNT dispersion.

  6. Preparation of novel polyamine-type chelating resin with hyperbranched structures and its adsorption performance

    Science.gov (United States)

    Zhao, Wei; Wang, Huan; Li, Yuhong; Li, Chenxi

    2018-01-01

    This paper explored the method of combining atom transfer radical polymerization (ATRP) technology and hyperbranched polymer principle to prepare the high capacity chelating resin. First, surface-initiated atom transfer radical polymerization (SI-ATRP) method was used to graft glycidyl methacrylate (GMA) on chloromethylated cross-linked styrene-divinylbenzene resin, and then the novel polyamine chelating resin with a kind of hyperbranched structure was prepared through the amination reaction between amino group of (2-aminoethyl) triamine and epoxy group in GMA. This resin had a selective effect on As(V) and Cr(VI) at a relatively low pH and can be used for the disposal of waste water containing As(V) and Cr(VI). It had a relatively strong adsorption effect on Cu(II), Pb(II), Cd(II) and Cr(III) and can be used for the disposal of heavy metal ion waste water. The finding was that, the adsorption capacity of resin on the studied heavy metal ions was higher than that of the chelating resin synthesized by traditional technology and also higher than that of the resin modified by ATRP technology and bifunctional chelator, indicating that the combination of ATRP and hyperbranched polymer concept is an effective method to prepare chelating resin with high capacity. PMID:29515875

  7. Preparation of novel polyamine-type chelating resin with hyperbranched structures and its adsorption performance

    Science.gov (United States)

    Chen, Youning; Zhao, Wei; Wang, Huan; Li, Yuhong; Li, Chenxi

    2018-02-01

    This paper explored the method of combining atom transfer radical polymerization (ATRP) technology and hyperbranched polymer principle to prepare the high capacity chelating resin. First, surface-initiated atom transfer radical polymerization (SI-ATRP) method was used to graft glycidyl methacrylate (GMA) on chloromethylated cross-linked styrene-divinylbenzene resin, and then the novel polyamine chelating resin with a kind of hyperbranched structure was prepared through the amination reaction between amino group of (2-aminoethyl) triamine and epoxy group in GMA. This resin had a selective effect on As(V) and Cr(VI) at a relatively low pH and can be used for the disposal of waste water containing As(V) and Cr(VI). It had a relatively strong adsorption effect on Cu(II), Pb(II), Cd(II) and Cr(III) and can be used for the disposal of heavy metal ion waste water. The finding was that, the adsorption capacity of resin on the studied heavy metal ions was higher than that of the chelating resin synthesized by traditional technology and also higher than that of the resin modified by ATRP technology and bifunctional chelator, indicating that the combination of ATRP and hyperbranched polymer concept is an effective method to prepare chelating resin with high capacity.

  8. Preparation and optical properties of indium tin oxide/epoxy nanocomposites with polyglycidyl methacrylate grafted nanoparticles.

    Science.gov (United States)

    Tao, Peng; Viswanath, Anand; Schadler, Linda S; Benicewicz, Brian C; Siegel, Richard W

    2011-09-01

    Visibly highly transparent indium tin oxide (ITO)/epoxy nanocomposites were prepared by dispersing polyglycidyl methacrylate (PGMA) grafted ITO nanoparticles into a commercial epoxy resin. The oleic acid stabilized, highly crystalline, and near monodisperse ITO nanoparticles were synthesized via a nonaqueous synthetic route with multigram batch quantities. An azido-phosphate ligand was synthesized and used to exchange with oleic acid on the ITO surface. The azide terminal group allows for the grafting of epoxy resin compatible PGMA polymer chains via Cu(I) catalyzed alkyne-azide "click" chemistry. Transmission electron microscopy (TEM) observation shows that PGMA grafted ITO particles were homogeneously dispersed within the epoxy matrix. Optical properties of ITO/epoxy nanocomposites with different ITO concentrations were studied with an ultraviolet-visible-near-infrared (UV-vis-NIR) spectrometer. All the ITO/epoxy nanocomposites show more than 90% optical transparency in the visible light range and absorption of UV light from 300 to 400 nm. In the near-infrared region, ITO/epoxy nanocomposites demonstrate low transmittance and the infrared (IR) transmission cutoff wavelength of the composites shifts toward the lower wavelength with increased ITO concentration. The ITO/epoxy nanocomposites were applied onto both glass and plastic substrates as visibly transparent and UV/IR opaque optical coatings.

  9. The effects of reactive diluents on the mechanical behaviour of an anhydride-cured epoxy resin system

    International Nuclear Information System (INIS)

    Stevens, G.T.; Lupton, A.W.

    1976-10-01

    A study was made of the tensile behaviour at room temperature, 75 0 C and 100 0 C, of diglycidyl ether of bisphenol A resin systems modified by the introduction of (i) a linear mono-epoxide aliphatic glycidyl ether, (ii) a highly branched mono-epoxide glycidyl ester of a saturated tertiary mono-carboxylic acid, (iii) a mixture of the linear mono-glycidyl and diglycidyl ethers of butanediol and (iv) a low viscosity diepoxide and also an elastomer (Hycar CTBN). Resin systems showing relatively high elongation to failure without severe degradation of strength or stiffness at elevated temperatures were obtained. (author)

  10. Local lymph node assay (LLNA): comparison of different protocols by testing skin-sensitizing epoxy resin system components.

    Science.gov (United States)

    Gamer, Armin O; Nies, Eberhard; Vohr, Hans-Werner

    2008-12-01

    Thirteen epoxy resin system components were tested in the LLNA with regard to their sensitizing potency. Lymph node stimulation was quantified not only by measuring the incorporation of [3H]-thymidine into the ear lymph nodes but also the counts of cells recovered from these organs. Equivalent figures were obtained with both endpoints used for the evaluation of lymph node cell proliferation if the reference stimulation indices were adjusted. When dissolved in acetone, all test substances showed skin-sensitizing potential, mainly on the boundary between "strong" and "moderate" according to common potency evaluation schemes. Replacing acetone with acetone/olive oil (4:1) as a vehicle for four selected test items, resulted in considerably lower estimated concentrations for sensitization induction. The challenges in comparing the results obtained by different LLNA variations are discussed.

  11. Preparation and Various Characteristics of Epoxy/Alumina Nanocomposites

    Science.gov (United States)

    Kozako, Masahiro; Ohki, Yoshimichi; Kohtoh, Masanori; Okabe, Shigemitsu; Tanaka, Toshikatsu

    Epoxy/ alumina nanocomposites were newly prepared by dispersing 3, 5, 7, and 10 weight (wt) % boehmite alumina nanofillers in a bisphenol-A epoxy resin using a special two-stage direct mixing method. It was confirmed by scanning electron microscopy imaging that the nanofillers were homogeneously dispersed in the epoxy matrix. Dielectric, mechanical, and thermal properties were investigated. It was elucidated that nanofillers affects various characteristics of epoxy resins, when they are nanostructrued. Such nano-effects we obtained are summarized as follows. Partial discharge resistance increases as the filler content increases; e.g. 7 wt% nanofiller content creates a 60 % decrease in depth of PD-caused erosion. Weibull analysis shows that short-time electrical treeing breakdown time is prolonged to 265 % by 5 wt% addition of nanofillers. But there was more data scatter in nanocomposites than in pure epoxy. Permittivity tends to increase from 3.7 to 4.0 by 5 wt% nanofiller addition as opposed to what was newly found in the recent past. Glass transition temperature remains unchanged as 109 °C. Mechanical properties such as flexural strength and flexural modulus increase; e.g. flexural strength and flexural modulus are improved by 5 % and 8 % with 5 wt% content, respectively. Excess addition causes a reverse effect. It is concluded from permittivity and glass transition temperature characteristics that interfacial bonding seems to be more or less weak in the nanocomposite specimens prepared this time, even though mechanical strengths increase. There is a possibility that the nanocomposites specimens will be improved in interfacial quality.

  12. Impact behavior of f-silica and amine terminated polybutadiene co-acrylonitrile rubber modified novolac epoxy/Kevlar nanocomposites

    Science.gov (United States)

    Kavita, Pal, Vijayeta; Tiwari, R. K.

    2018-05-01

    In the present work, nano-fumed silica treated with 3-Glycidoxypropyl trimethoxy silane (f-silica) was used as a nanoreinforcement in the fabrication of amine terminated polybutadiene co-acrylonitrile rubber (ATBN) modified Kevlar/epoxy based nanocomposites. Nanocomposites with different f-silica loading (0, 0.5, 1.0 and 2.0 wt. %) and having same ATBN (10 wt. %) were made and characterized by Izod impact test for evaluating impact strength values. All the nanocomposites showed better impact strength than neat Kevlar/novolac epoxy based composite.

  13. Organic materials for semiconductor. Epoxy molding compound for IC encapsulation; Handotai kanren no yuki zairyo. Handotai fushiyo epoxy seikei zairyo ni tsuite

    Energy Technology Data Exchange (ETDEWEB)

    Kusuhara, A. [Sumitomo Bakelite Co. Ltd., Tokyo (Japan)

    1998-11-05

    This paper describes organic materials for semiconductor. Based on the composition and raw material, typical materials are epoxy resins, curing agents including phenol-novolak resins, fillers including silica and alumina, flame retardants including brominated epoxy resin and antimony oxide, hardening accelerators including amine compounds and phosphorus compounds, coupling agents including silane compounds and titanate compounds, and the others including colorants and mold lubricants. Raw materials are heated and kneaded after mixing, and produced as tablets after cooling and crushing. Recently, the packages have changed from insertion type to surface mounting type for the small thin IC package and for improving the efficiency of soldering during the incorporation of IC package on the print circuit substrate. High temperature of 260degC has been employed from the conventional limit of 100degC. Reduction of water absorption, improvement of adhesion, reduction of thermal expansion coefficient, and reduction of elastic modulus during heating are promoted for avoiding the peeling and cracking due to the sudden evaporation of adsorbed moisture. This paper also describes the organic materials for BGA. 10 figs., 4 tabs.

  14. Characterization of the flexural behavior of a reactive graphitic nanofibers reinforced epoxy using a non-linear damage model

    Energy Technology Data Exchange (ETDEWEB)

    Jana, Soumen [Department of Mechanical Engineering and Applied Mechanics, North Dakota State University, Fargo, ND 58105 (United States); Zhong Weihong [Department of Mechanical Engineering and Applied Mechanics, North Dakota State University, Fargo, ND 58105 (United States)]. E-mail: Katie.zhong@ndsu.edu; Gan, Yong X. [Department of Mechanical Engineering, Albert Nerken School of Engineering, Cooper Union for the Advancement of Science and Art, 51 Astor Place, New York City, NY 10003 (United States)

    2007-02-15

    In our previous work, a nano-epoxy was developed based on the preparation of reactive graphitic nanofibers (r-GNFs). The objective of this work is to study the effect of the r-GNFs in an epoxy resin on the mechanical properties of the resulting nano-epoxy composites. Three-point bending tests were carried out for the pure epoxy and nano-epoxy materials with 0.15, 0.2, 0.3, 0.5 wt% r-GNFs to obtain the flexural behaviors. The nano-epoxy composite containing 0.3 wt% of r-GNFs showed the best flexural properties including highest flexural strength, modules and ductility values among all the tested materials. Non-linear fracture mechanics (NLFM) was applied to analyze the phenomena occurred during the bending tests. A non-linear damage model was used to interpret the flexural stress-strain relationships of the tested materials, which showed agreement with the testing results. The fracture surfaces of the nano-epoxy composites were examined with scanning electron microscopy (SEM), and the morphological features on the SEM images also reveals that the nano-epoxy composites are tougher than the pure epoxy resin.

  15. Effect of γ irradiation on the properties of basalt fiber reinforced epoxy resin matrix composite

    Science.gov (United States)

    Li, Ran; Gu, Yizhuo; Yang, Zhongjia; Li, Min; Wang, Shaokai; Zhang, Zuoguang

    2015-11-01

    Gamma-ray (γ-ray) irradiation is a crucial reason for the aging in materials used for nuclear industry. Due to high specific strength and stiffness, light weight and good corrosion resistance, fiber reinforced composites are regarded as an alternative of traditional materials used on nuclear facilities. In this study, basalt fiber (BF)/AG80 epoxy composite laminates were fabricated by autoclave process and treated with 60Co gamma irradiation dose up to 2.0 MGy. Irradiation induced polymer chain scission and oxidation of AG80 resin were detected from physical and chemical analysis. The experimental results show that the tensile and flexural performances of irradiated BF/AG80 composite maintain stable and have a low amplitude attenuation respectively, and the interlaminar shear strength has increased from irradiation dose of 0-1.5 MGy. Furthermore, the comparison between the studied BF composite and reported polymer and composite materials was done for evaluating the γ resistance property of BF composite.

  16. Silver-embedded modified hyperbranched epoxy/clay nanocomposites as antibacterial materials.

    Science.gov (United States)

    Roy, Buddhadeb; Bharali, Pranjal; Konwar, B K; Karak, Niranjan

    2013-01-01

    Silver-embedded modified hyperbranched epoxy/clay nanocomposites were prepared at different wt.% of octadecyl amine-modified montmorillonite at a constant silver concentration (1 wt.%). UV-visible, XRD and TEM studies confirmed the formation of silver nanoparticles. Compared to the system without silver and clay, the gloss from 70° to 94°, scratch hardness from 4 to 5.8 kg, impact strength from 60 to 90 cm, tensile strength from 8.5 to 15.5 MPa, adhesive strength from 5 to 7.1 × 10(9)N/m, flexibility from >6 to nanocomposites showed antibacterial activity in well diffusion assays against Staphylococcus aureus (ATCC11632), Bacillus subtilis (ATCC11774), Escherichia coli (MTCC40), Pseudomonas aeruginosa (MTCC7814) and Klebsiella pneumoniae (ATCC10031). The results showed that these nanocomposites have potential to be used as antimicrobial materials. Copyright © 2012 Elsevier Ltd. All rights reserved.

  17. Radiation damage on high polymer epoxies

    Energy Technology Data Exchange (ETDEWEB)

    Pak, H M [Royal Military Coll. of Canada, Kingston, ON (Canada)

    1994-12-31

    The effect of irradiation in a SLOWPOKE-2 reactor on the adhesive strength of epoxy resins was studied using the ASTM D897 standard testing procedure. Although the results were variable, indicating the doses were not well defined, nevertheless, there was evidence of strengthening associated with radiation-induced crosslinking. 2 figs., 1 tab.

  18. In-situ Elevated Temperature Mechanical Performance of MWCNT/epoxy Nanocomposite

    Directory of Open Access Journals (Sweden)

    Bhanu Pratap Singh

    2017-03-01

    Full Text Available The present investigation has been focused on the effects of multi-walled carbon nanotube (MWCNT addition on the mechanical performance of epoxy under different in-service elevated temperature environments. Room temperature flexural test results revealed that addition of 0.1 wt. % MWCNT into epoxy resin resulted in modulus and strength enhancement of 21 % and 9 % respectively. With increase in service temperature, significant decrement in both modulus and strength was noticed for both materials (neat epoxy and MWCNT/epoxy nanocomposite, but the rate of degradation was found to be quite drastic for the nanocomposite. At 90 °C temperature, the CNT/epoxy nanocomposite exhibited inferior modulus and strength, which are 41 % and 59 % lower than neat epoxy respectively. The variation trend in elastic modulus with temperature obtained from both flexural testing and DMA for both these materials was also analyzed. It was found that addition of 0.1 % CNT in the epoxy reduced the glass transition temperature by about 16°C.

  19. Microleakage of conventional, resin-modified, and nano-ionomer glass ionomer cement as primary teeth filling material

    Directory of Open Access Journals (Sweden)

    Dita Madyarani

    2014-12-01

    Full Text Available Background: Glass ionomer cements are one of many dental materials that widely used in pediatric dentistry due to their advantage of fluoride release and chemical bond to tooth structure. Adherence of the filling material to the cavity walls is one of the most important characteristic that need to be examined its effect on microleakage. Purpose: This study was conducted to examine the microleakage of nano-ionomer glass ionomer cement compared with the conventional and resin-modified glass ionomer cements. Methods: Standard class V cavities sized 3 mm x 2 mm x 2 mm were made on a total of 21 extracted maxillary primary canine teeth and restored with the conventional, resin-modified, dan nano-ionomer glass ionomer cements. All the teeth were immersed in a 2% methylene blue dye for 4 hours. The depth of dye penetration was assessed using digital microscope after sectioning the teeth labio-palatally. The results were statistically analyzed using Kruskal-Wallis test. Results: All type of glass ionomer material showed microleakage. Conventional glass ionomer cement demonstrated the least microleakage with mean score 1.29. the resin-modified glass ionomer cements (mean score 1.57 and nano-ionomer glass ionomer cement (mean score 2.57. Conclusion: The conventional glassionomer, resin modified glassionomer, and nano-ionomer glassionomer showed micro leakage as filling material in primary teeth cavity. The micro leakage among three types was not significant difference. All three material were comparable in performance and can be used for filling material but still needs a coating material to fill the microleakage.Latar belakang: Semen ionomer kaca adalah salah satu dari banyak bahan gigi yang banyak digunakan dalam praktek kedokteran gigi anak karena bahan tersebut merilis fluoride dan berikatan kimia dengan struktur gigi. Perlekatan bahan tumpatan pada dinding kavitas adalah salah satu karakteristik paling penting yang perlu diteliti efeknya terhadap

  20. Self-Healable and Reprocessable Polysulfide Sealants Prepared from Liquid Polysulfide Oligomer and Epoxy Resin.

    Science.gov (United States)

    Gao, Wentong; Bie, Mengyao; Liu, Fu; Chang, Pengshan; Quan, Yiwu

    2017-05-10

    Polysulfide sealants have been commercially applied in many industrial fields. In this article, we study the self-healing property of the epoxy resin-cured polysulfide sealants for the first time. The obtained sealants showed a flexible range of ultimate elongation of 157-478% and a tensile strength of 1.02-0.75 MPa corresponding to different polysulfide oligomers. By taking advantage of the dynamic reversible exchange of disulfide bonds, polysulfide sealants exhibited good self-healing ability under a moderate thermal stimulus. A higher molecular weight and a lower degree of cross-linking of polysulfide oligomer were helpful in improving the ultimate elongation and healing efficiency of the polysulfide sealants. After subjecting to a temperature of 75 °C for 60 min, both the tensile strength and ultimate elongation of a fully cut sample, LP55-F, were restored to 91% of the original values, without affecting the sealing property. Furthermore, the sample exhibited excellent reshaping and reprocessing abilities. These outcomes offer a paradigm toward sustainable industrial applications of the polysulfide-based sealants.

  1. Modificação de fibra de carbono com PBLH e sua utilização em compósitos com resina epoxídica Hydroxyl-terminated polybutadiene-grafted carbon fiber in epoxy resin-based composites

    Directory of Open Access Journals (Sweden)

    Fábio L. Barcia

    1999-06-01

    Full Text Available Fibras de carbono contendo 1,4 e 2,1mmol/g de grupos carboxila e hidroxila fenólica, respectivamente, foram modificadas através de reação com TDI, resultando em fibras contendo 3,1 mmol/g de grupos isocianato. A introdução de grupos isocianato na superfície da fibra tornou possível a sua modificação com polibutadieno líquido hidroxilado. Fibras de carbono modificadas e não modificadas foram empregadas na preparação de compósitos com resina epoxídica, sendo observado um aumento considerável de resistência ao impacto em compósitos constituídos de fibras de carbono enxertadas com PBLH, devido, provavelmente, à natureza elastomérica da interface e à melhor adesão interfacial.Carbon fibers containing 1,4 e 2,1 mmol/g of carboxyl and phenolic hydroxyl groups, respectively, were modified through the reaction with TDI. The presence of isocyanate groups at the fiber surface made possible the fiber modification with hydroxyl terminated polybutadiene (HTPB. These modified and unmodified carbon fibers were employed in the preparation of epoxy resin-based composites. A substantial improvement in the impact properties was observed in the composites with HTPB-grafted carbon fibers when compared to unmodified carbon fibers. These results may be attributed to a higher interfacial adhesion promoted by reactions between the functional groups present at the modified carbon fiber surface and the epoxy matrix.

  2. High-performance fiber/epoxy composite pressure vessels

    Science.gov (United States)

    Chiao, T. T.; Hamstad, M. A.; Jessop, E. S.; Toland, R. H.

    1978-01-01

    Activities described include: (1) determining the applicability of an ultrahigh-strength graphite fiber to composite pressure vessels; (2) defining the fatigue performance of thin-titanium-lined, high-strength graphite/epoxy pressure vessel; (3) selecting epoxy resin systems suitable for filament winding; (4) studying the fatigue life potential of Kevlar 49/epoxy pressure vessels; and (5) developing polymer liners for composite pressure vessels. Kevlar 49/epoxy and graphite fiber/epoxy pressure vessels, 10.2 cm in diameter, some with aluminum liners and some with alternation layers of rubber and polymer were fabricated. To determine liner performance, vessels were subjected to gas permeation tests, fatigue cycling, and burst tests, measuring composite performance, fatigue life, and leak rates. Both the metal and the rubber/polymer liner performed well. Proportionately larger pressure vessels (20.3 and 38 cm in diameter) were made and subjected to the same tests. In these larger vessels, line leakage problems with both liners developed the causes of the leaks were identified and some solutions to such liner problems are recommended.

  3. Experimental and Numerical Simulation Analysis of Typical Carbon Woven Fabric/Epoxy Laminates Subjected to Lightning Strike

    Science.gov (United States)

    Yin, J. J.; Chang, F.; Li, S. L.; Yao, X. L.; Sun, J. R.; Xiao, Y.

    2017-12-01

    To clarify the evolution of damage for typical carbon woven fabric/epoxy laminates exposed to lightning strike, artificial lightning testing on carbon woven fabric/epoxy laminates were conducted, damage was assessed using visual inspection and damage peeling approaches. Relationships between damage size and action integral were also elucidated. Results showed that damage appearance of carbon woven fabric/epoxy laminate presents circular distribution, and center of the circle located at the lightning attachment point approximately, there exist no damage projected area dislocations for different layers, visual damage territory represents maximum damage scope; visible damage can be categorized into five modes: resin ablation, fiber fracture and sublimation, delamination, ablation scallops and block-shaped ply-lift; delamination damage due to resin pyrolysis and internal pressure exist obvious distinguish; project area of total damage is linear with action integral for the same type specimens, that of resin ablation damage is linear with action integral, but no correlation with specimen type, for all specimens, damage depth is linear with logarithm of action integral. The coupled thermal-electrical model constructed is capable to simulate the ablation damage for carbon woven fabric/epoxy laminates exposed to simulated lightning current through experimental verification.

  4. Curing reaction of bisphenol-A based benzoxazine with cyanate ester resin and the properties of the cured thermosetting resin

    Directory of Open Access Journals (Sweden)

    H. Kimura

    2011-12-01

    Full Text Available Curing reaction of bisphenol-A based benzoxazine with cyanate ester resin and the properties of the cured thermosetting resin were investigated. The cure behavior of benzoxazine with cyanate ester resin was monitored by model reaction using nuclear magnetic resonance (NMR. As a result of the model reaction, the ring opening reaction of benzoxazine ring and thermal self-cyclotrimerization of cyanate ester group occurred, and then the phenolic hydoroxyl group generated by the ring opening reaction of benzoxazine ring co-reacted with cyanate ester group. The properties of the cured thermosetting resin were estimated by mechanical properties, electrical resistivity, water resistance and heat resistance. The cured thermosetting resin from benzoxazine and cyanate ester resin showed good heat resistance, high electrical resistivity and high water resistance, compared with the cured thermosetting resin from benzoxazine and epoxy resin.

  5. Epoxy Nanocomposites - Curing Rheokinetics, Wetting and Adhesion to Fibers

    International Nuclear Information System (INIS)

    Ilyin, S. O.; Kotomin, S. V.; Kulichikhin, V. G.

    2010-01-01

    Epoxy nanocomposites considered as challenging polymeric matrix for advanced reinforced plastics. Nanofillers change rheokinetics of epoxy resin curing, affect wetting and adhesion to aramid and carbon fibers. In all cases extreme dependence of adhesive strength vs filler content in the binder was observed. New experimental techniques were developed to study wettability and fiber-matrix adhesion interaction, using yarn penetration path length, aramid fiber knot pull-up test and electrical admittance of the fracture surface of CFRP.

  6. Fish DNA-modified clays: Towards highly flame retardant polymer nanocomposite with improved interfacial and mechanical performance

    Science.gov (United States)

    Zabihi, Omid; Ahmadi, Mojtaba; Khayyam, Hamid; Naebe, Minoo

    2016-12-01

    Deoxyribonucleic Acid (DNA) has been recently found to be an efficient renewable and environmentally-friendly flame retardant. In this work, for the first time, we have used waste DNA from fishing industry to modify clay structure in order to increase the clay interactions with epoxy resin and take benefit of its additional thermal property effect on thermo-physical properties of epoxy-clay nanocomposites. Intercalation of DNA within the clay layers was accomplished in a one-step approach confirmed by FT-IR, XPS, TGA, and XRD analyses, indicating that d-space of clay layers was expanded from ~1.2 nm for pristine clay to ~1.9 nm for clay modified with DNA (d-clay). Compared to epoxy nanocomposite containing 2.5%wt of Nanomer I.28E organoclay (m-clay), it was found that at 2.5%wt d-clay loading, significant enhancements of ~14%, ~6% and ~26% in tensile strength, tensile modulus, and fracture toughness of epoxy nanocomposite can be achieved, respectively. Effect of DNA as clay modifier on thermal performance of epoxy nanocomposite containing 2.5%wt d-clay was evaluated using TGA and cone calorimetry analysis, revealing significant decreases of ~4000 kJ/m2 and ~78 kW/m2 in total heat release and peak of heat release rate, respectively, in comparison to that containing 2.5%wt of m-clay.

  7. Novel Formulations of Phase Change Materials-Epoxy Composites for Thermal Energy Storage.

    Science.gov (United States)

    Arce, Maria Elena; Alvarez Feijoo, Miguel Angel; Suarez Garcia, Andres; Luhrs, Claudia C

    2018-01-26

    This research aimed to evaluate the thermal properties of new formulations of phase change materials (PCMs)-epoxy composites, containing a thickening agent and a thermally conductive phase. The composite specimens produced consisted of composites fabricated using (a) inorganic PCMs (hydrated salts), epoxy resins and aluminum particulates or (b) organic PCM (paraffin), epoxy resins, and copper particles. Differential Scanning Calorimetry (DSC) was used to analyze the thermal behavior of the samples, while hardness measurements were used to determine changes in mechanical properties at diverse PCM and conductive phase loading values. The results indicate that the epoxy matrix can act as a container for the PCM phase without hindering the heat-absorbing behavior of the PCMs employed. Organic PCMs presented reversible phase transformations over multiple cycles, an advantage that was lacking in their inorganic counterparts. The enthalpy of the organic PCM-epoxy specimens increased linearly with the PCM content in the matrix. The use of thickening agents prevented phase segregation issues and allowed the fabrication of specimens containing up to 40% PCM, a loading significantly higher than others reported. The conductive phase seemed to improve the heat transfer and the mechanical properties of the composites when present in low percentages (material at the temperatures employed.

  8. Enhancement of mechanical properties of epoxy/graphene nanocomposite

    Science.gov (United States)

    Berhanuddin, N. I. C.; Zaman, I.; Rozlan, S. A. M.; Karim, M. A. A.; Manshoor, B.; Khalid, A.; Chan, S. W.; Meng, Q.

    2017-10-01

    Graphene is a novel class of nanofillers possessing outstanding characteristics including most compatible with most polymers, high absolute strength, high aspect ratio and cost effectiveness. In this study, graphene was used to reinforce epoxy as a matrix, to enhance its mechanical properties. Two types of epoxy composite were developed which are epoxy/graphene nanocomposite and epoxy/modified graphene nanocomposite. The fabrication of graphene was going through thermal expansion and sonication process. Chemical modification was only done for modified graphene where 4,4’-Methylene diphenyl diisocyanate (MDI) is used. The mechanical properties of both nanocomposite, such as Young’s modulus and maximum stress were investigated. Three weight percentage were used for this study which are 0.5 wt%, 1.0 wt% and 1.5 wt%. At 0.5 wt%, modified and unmodified shows the highest value compared to neat epoxy, where the value were 8 GPa, 6 GPa and 0.675 GPa, respectively. For maximum stress, neat epoxy showed the best result compared to both nanocomposite due to the changes of material properties when adding the filler into the matrix. Therefore, both nanocomposite increase the mechanical properties of the epoxy, however modification surface of graphene gives better improvement.

  9. Development of melamine modified urea formaldehyde resins based o nstrong acidic pH catalyzed urea formaldehyde polymer

    Science.gov (United States)

    Chung-Yun Hse

    2009-01-01

    To upgrade the performance of urea-formaldehyde (UF) resin bonded particleboards, melamine modified urea-formaldehyde (MUF) resins based on strong acidic pH catalyzed UF polymers were investigated. The study was conducted in a series of two experiments: 1) formulation of MUF resins based on a UF polymer catalyzed with strong acidic pH and 2) determination of the...

  10. Improved Dielectric Properties and Energy Storage Density of Poly(vinylidene fluoride-co-hexafluoropropylene) Nanocomposite with Hydantoin Epoxy Resin Coated BaTiO3.

    Science.gov (United States)

    Luo, Hang; Zhang, Dou; Jiang, Chao; Yuan, Xi; Chen, Chao; Zhou, Kechao

    2015-04-22

    Energy storage materials are urgently demanded in modern electric power supply and renewable energy systems. The introduction of inorganic fillers to polymer matrix represents a promising avenue for the development of high energy density storage materials, which combines the high dielectric constant of inorganic fillers with supernal dielectric strength of polymer matrix. However, agglomeration and phase separation of inorganic fillers in the polymer matrix remain the key barriers to promoting the practical applications of the composites for energy storage. Here, we developed a low-cost and environmentally friendly route to modifying BaTiO3 (BT) nanoparticles by a kind of water-soluble hydantoin epoxy resin. The modified BT nanoparticles exhibited homogeneous dispersion in the ferroelectric polymer poly(vinylidene fluoride-co-hexafluoropropylene) (P(VDF-HFP)) matrix and strong interfacial adhesion with the polymer matrix. The dielectric constants of the nanocomposites increased significantly with the increase of the coated BT loading, while the dielectric loss of the nanocomposites was still as low as that of the pure P(VDF-HFP). The energy storage density of the nanocomposites was largely enhanced with the coated BT loading at the same electric field. The nanocomposite with 20 vol % BT exhibited an estimated maximum energy density of 8.13 J cm(-3), which was much higher than that of pure P(VDF-HFP) and other dielectric polymers. The findings of this research could provide a feasible approach to produce high energy density materials for practical application in energy storage.

  11. Thermal contraction effects in epoxy resin composites at low temperatures

    International Nuclear Information System (INIS)

    Evans, D.; Morgan, J.T.

    1979-10-01

    Because of their electrical and thermal insulation characteristics, high strength fibreglass/epoxy composites are widely used in the construction of bubble chamber and other cryogenic equipment. Thermal contraction effects on cooling to operating temperature present problems which need to be taken into account at the design stage. This paper gives results of thermal contraction tests carried out on fibreglass/epoxy composites including the somewhat anomalous results obtained with rings and tubes. Also considered are some of the problems associated with the use of these materials at temperatures in the region of 20K. (author)

  12. Flexural Properties of Activated Carbon Filled Epoxy Nano composites

    International Nuclear Information System (INIS)

    Khalil, H.P.S.A.; Khalil, H.P.S.A.; Alothman, O.Y.; Paridah, M.T.; Zainudin, E.S.

    2014-01-01

    Activated carbon (AC) filled epoxy nano composites obtained by mixing the desired amount of nano AC viz., bamboo stem, oil palm empty fruit bunch, and coconut shell from agricultural biomass with the epoxy resin. Flexural properties of activated carbons filled epoxy nano composites with 1 %, and 5 % filler loading were measured. In terms of flexural strength and modulus, a significant increment was observed with addition of 1 % vol and 5 % vol nano-activated carbon as compared to neat epoxy. The effect of activated carbon treated by two chemical agents (potassium hydroxide and phosphoric acid) on the flexural properties of epoxy nano composites were also investigated. Flexural strength of activated carbon-bamboo stem, activated carbon-oil palm, and activated carbon-coconut shell reinforced epoxy nano composites showed almost same value in case of 5 % potassium hydroxide activated carbon. Flexural strength of potassium hydroxide activated carbon-based epoxy nano composites was higher than phosphoric acid activated carbon. The flexural toughness of both the potassium hydroxide and phosphoric acid activated carbon reinforced composites range between 0.79 - 0.92 J. It attributed that developed activated carbon filled epoxy nano composites can be used in different applications. (author)

  13. Epoxy-coal hydraulic insulation for structures of the Nurek Hydroelectric Powerplant

    Energy Technology Data Exchange (ETDEWEB)

    Sakharov, V I; Segal, M S; Solov' ev, I N; Yazev, R E

    1978-03-01

    The design of the Nurek Powerplant exposed the base of the core of the dam to a head of 270 m. To avoid seepage, it was decided to construct an antiseepage screen. Given the total hydraulic insulation area required, 26,540 m/sup 2/, the use of a metal screen would be quite expensive. It was therefore decided to use an epoxy-coal material consisting of a primer, varnish and enamel based on epoxy resins modified by the addition of coal tar, a waste product from the dry distillation of coal. A typical hydraulic insulation layer consists of a coat of primer, three or four coats of varnish and a coat of enamel. Glass-reinforced fabric is used with the first through third coats of varnish to increase crack resistance. The coating thus produced is found to be resistant to overbearing soil pressure of up to 600 t/m/sup 2/, hydrostatic head of up to 300 m and constant shear forces of up to 100 t/m/sup 2/. The method also saves labor and expensive metal.

  14. Fabrication of tough epoxy with shape memory effects by UV-assisted direct-ink write printing.

    Science.gov (United States)

    Chen, Kaijuan; Kuang, Xiao; Li, Vincent; Kang, Guozheng; Qi, H Jerry

    2018-03-07

    3D printing of epoxy-based shape memory polymers with high mechanical strength, excellent thermal stability and chemical resistance is highly desirable for practical applications. However, thermally cured epoxy in general is difficult to print directly. There have been limited numbers of successes in printing epoxy but they suffer from relatively poor mechanical properties. Here, we present an ultraviolet (UV)-assisted 3D printing of thermally cured epoxy composites with high tensile toughness via a two-stage curing approach. The ink containing UV curable resin and epoxy oligomer is used for UV-assisted direct-ink write (DIW)-based 3D printing followed by thermal curing of the part containing the epoxy oligomer. The UV curable resin forms a network by photo polymerization after the 1st stage of UV curing, which can maintain the printed architecture at an elevated temperature. The 2nd stage thermal curing of the epoxy oligomer yields an interpenetrating polymer network (IPN) composite with highly enhanced mechanical properties. It is found that the printed IPN epoxy composites enabled by the two-stage curing show isotropic mechanical properties and high tensile toughness. We demonstrated that the 3D-printed high-toughness epoxy composites show good shape memory properties. This UV-assisted DIW 3D printing via a two-stage curing method can broaden the application of 3D printing to fabricate thermoset materials with enhanced tensile toughness and tunable properties for high-performance and functional applications.

  15. Three-Phase Carbon Fiber Amine Functionalized Carbon Nanotubes Epoxy Composite: Processing, Characterisation, and Multiscale Modeling

    Directory of Open Access Journals (Sweden)

    Kamal Sharma

    2014-01-01

    Full Text Available The present paper discusses the key issues of carbon nanotube (CNT dispersion and effect of functionalisation on the mechanical properties of multiscale carbon epoxy composites. In this study, CNTs were added in epoxy matrix and further reinforced with carbon fibres. Predetermined amounts of optimally amine functionalised CNTs were dispersed in epoxy matrix, and unidirectional carbon fiber laminates were produced. The effect of the presence of CNTs (1.0 wt% in the resin was reflected by pronounced increase in Young’s modulus, inter-laminar shear strength, and flexural modulus by 51.46%, 39.62%, and 38.04%, respectively. However, 1.5 wt% CNT loading in epoxy resin decreased the overall properties of the three-phase composites. A combination of Halpin-Tsai equations and micromechanics modeling approach was also used to evaluate the mechanical properties of multiscale composites and the differences between the predicted and experimental values are reported. These multiscale composites are likely to be used for potential missile and aerospace structural applications.

  16. Interlaminar fracture in woven carbon/epoxy laminates

    Directory of Open Access Journals (Sweden)

    Paulo N.B. Reis

    2014-10-01

    Full Text Available This paper describes an experimental study developed to characterize the mode I and mode II fracture toughness of carbon/epoxy woven composites, using DCB and ENF tests, respectively. The laminates were manufactured using an epoxy resin and twelve woven balanced bi-directional layers of carbon fibres, all of them with the same orientation (0/90º. Significant instantaneous delaminations were observed particularly for the DCB specimen, which were responsible for an oscillatory behaviour of GI versus crack length. The maximum values obtained for GIC and GIIC were 281 and 1800 J/m2, respectively.

  17. Adhesion of pineapple-leaf fiber to epoxy matrix: The role of surface treatments

    Directory of Open Access Journals (Sweden)

    Yusran Payae

    2009-07-01

    Full Text Available Natural fibers are considered to have potential use as reinforcing agents in polymer composite materials because of their principle benefits: moderate strength and stiffness, low cost, and be an environmental friendly, degradable, and renewablematerial. Due to their inherently hydrophilic nature, they are prone to absorb moisture, which can plasticise or weaken theadhesion of fibers to the surrounding matrix and by this affect the performance of composites used in atmospheric humidity,particularly at elevated temperatures. The surface treatments are often applied to the fiber to improve the bond strengthbetween the fibers and matrix. This work discussed the effect of sodium hydroxide (NaOH treatment and epoxy resin as acompatibilizing agent on interface properties of pineapple leaf fiber (PALF-epoxy composites. A single-fiber fragmentationtest coupled with data reduction technique was employed to assess interface quality in terms of apparent interfacial shearstrength (IFSS or a of untreated, NaOH, and epoxy resin treated PALFs-epoxy composites. Tensile properties of untreatedand treated PALFs were also examined. It was found that both treatments substantially increase a, corresponding to animproved level of adhesion. The improvement in the level of adhesion for the alkali and epoxy treated fiber composites wasdue to an increase in the physical bonding between the alkali treated fibers and the matrix, and due to a promoted compatibilitybetween the epoxy treated fibers and matrix, respectively.

  18. Preparation and characterization of rubbery epoxy/multiwall carbon nanotubes composites using amino acid salt assisted dispersion technique

    Directory of Open Access Journals (Sweden)

    S. B. Jagtap

    2013-04-01

    Full Text Available Epoxy/multiwall carbon nanotubes (MWCNT composites were prepared using sodium salt of 6-aminohexanoic acid (SAHA modified MWCNT and its effect properties of related composites were investigated. The composite prepared using a polar solvent, tetrahydrofuran exhibits better mechanical properties compared to those prepared using less polar solvent and without using solvent. The tensile properties and dynamic storage modulus was found to be increased as a result of modification of MWCNT with SAHA. This improvement in the tensile properties and dynamic mechanical properties of epoxy/MWCNT composite is a combined effect of cation-π interaction and chemical bonding. Fourier transform infrared spectroscopy (FTIR and Raman spectroscopy were used to explain cation-π interaction between SAHA with MWCNT and chemical bonding of SAHA with epoxy resin. The effect of modification of MWCNT on morphology of a nanocomposite was confirmed by using scanning electron microscopy (SEM and transmission electron microscopy (TEM. The present approach does not disturb the ! electron clouds of MWCNT as opposed to chemical functionalization strategy.

  19. Analysis of effective thermal conductivity for mineral cast material structures with varying epoxy content using TPS method

    Directory of Open Access Journals (Sweden)

    A. Selvakumar

    2012-01-01

    Full Text Available Conventionally, cast iron is the material used for high speed machine tool structures. As an alternate material to improve the structural properties, composite materials are being used, which are known to exhibit excellent thermal and mechanical properties. While selecting an alternate material, thermal conductivity is an important thermo physical property of the material that should be studied. A resin composite material has a lesser thermal conductivity and its thermal properties vary with the composition of the mixture. A material with lower thermal conductivity will have higher heat concentration within the structure, which may result in structural deformation. In this analysis, epoxy granite, a material which is tested to exhibit excellent mechanical properties has been selected to study its thermal properties. Tests are carried out using Transient Plane Source (TPS method, on eight samples with varying volume fraction of epoxy content in the range 10-24%. It is observed that, the effective thermal conductivity decreases with an increase in epoxy resin content in the mixture because the resin content increases interfacial resistance between particles. Hence, lower epoxy content in the mixture that maximizes the effective thermal conductivity while maintaining good mechanical properties is to be selected.

  20. Analysis of effective thermal conductivity for mineral cast material structures with varying epoxy content using TPS method

    Directory of Open Access Journals (Sweden)

    A. Selvakumar

    2013-04-01

    Full Text Available Conventionally, cast iron is the material used for high speed machine tool structures. As an alternate material to improve the structural properties, composite materials are being used, which are known to exhibit excellent thermal and mechanical properties. While selecting an alternate material, thermal conductivity is an important thermo physical property of the material that should be studied. A resin composite material has a lesser thermal conductivity and its thermal properties vary with the composition of the mixture. A material with lower thermal conductivity will have higher heat concentration within the structure, which may result in structural deformation. In this analysis, epoxy granite, a material which is tested to exhibit excellent mechanical properties has been selected to study its thermal properties. Tests are carried out using Transient Plane Source (TPS method, on eight samples with varying volume fraction of epoxy content in the range 10-24%. It is observed that, the effective thermal conductivity decreases with an increase in epoxy resin content in the mixture because the resin content increases interfacial resistance between particles. Hence, lower epoxy content in the mixture that maximizes the effective thermal conductivity while maintaining good mechanical properties is to be selected.