High-quality nonpolar a-plane GaN epitaxial films grown on r-plane sapphire substrates by the combination of pulsed laser deposition and metal–organic chemical vapor deposition

Science.gov (United States)

Yang, Weijia; Zhang, Zichen; Wang, Wenliang; Zheng, Yulin; Wang, Haiyan; Li, Guoqiang

2018-05-01

High-quality a-plane GaN epitaxial films have been grown on r-plane sapphire substrates by the combination of pulsed laser deposition (PLD) and metal–organic chemical vapor deposition (MOCVD). PLD is employed to epitaxial growth of a-plane GaN templates on r-plane sapphire substrates, and then MOCVD is used. The nonpolar a-plane GaN epitaxial films with relatively small thickness (2.9 µm) show high quality, with the full-width at half-maximum values of GaN(11\\bar{2}0) along [1\\bar{1}00] direction and GaN(10\\bar{1}1) of 0.11 and 0.30°, and a root-mean-square surface roughness of 1.7 nm. This result is equivalent to the quality of the films grown by MOCVD with a thickness of 10 µm. This work provides a new and effective approach for achieving high-quality nonpolar a-plane GaN epitaxial films on r-plane sapphire substrates.

Successful Fabrication of GaN Epitaxial Layer on Non-Catalytically grown Graphene

Energy Technology Data Exchange (ETDEWEB)

Hwang, Sung Won [Konkuk University, Chungju (Korea, Republic of); Choi, Suk-Ho [Kyung Hee University, Yongin (Korea, Republic of)

2016-07-15

Sapphire is widely used as a substrate for the growth of GaN epitaxial layer (EPI), but has several drawbacks such as high cost, large lattice mismatch, non-flexibility, and so on. Here, we first employ graphene directly grown on Si or sapphire substrate as a platform for the growth and lift-off of GaN-light-emitting diode (LED) EPI, useful for not only recycling the substrate but also transferring the GaN-LED EPI to other flexible substrates. Sequential standard processes of nucleation/recrystallization of GaN seeds and deposition of undoped (u-) GaN/AlN buffer layer were done on graphene/substrate before the growth of GaN-LED EPI, accompanied by taping and lift-off of u-GaN/AlN or GaN-LED EPI. This approach can overcome the limitations by the catalytic growth and transfer of graphene, and make the oxygen-plasma treatment of graphene for the growth of GaN EPI unnecessary.

A new approach to epitaxially grow high-quality GaN films on Si substrates: the combination of MBE and PLD.

Science.gov (United States)

Wang, Wenliang; Wang, Haiyan; Yang, Weijia; Zhu, Yunnong; Li, Guoqiang

2016-04-22

High-quality GaN epitaxial films have been grown on Si substrates with Al buffer layer by the combination of molecular beam epitaxy (MBE) and pulsed laser deposition (PLD) technologies. MBE is used to grow Al buffer layer at first, and then PLD is deployed to grow GaN epitaxial films on the Al buffer layer. The surface morphology, crystalline quality, and interfacial property of as-grown GaN epitaxial films on Si substrates are studied systematically. The as-grown ~300 nm-thick GaN epitaxial films grown at 850 °C with ~30 nm-thick Al buffer layer on Si substrates show high crystalline quality with the full-width at half-maximum (FWHM) for GaN(0002) and GaN(102) X-ray rocking curves of 0.45° and 0.61°, respectively; very flat GaN surface with the root-mean-square surface roughness of 2.5 nm; as well as the sharp and abrupt GaN/AlGaN/Al/Si hetero-interfaces. Furthermore, the corresponding growth mechanism of GaN epitaxial films grown on Si substrates with Al buffer layer by the combination of MBE and PLD is hence studied in depth. This work provides a novel and simple approach for the epitaxial growth of high-quality GaN epitaxial films on Si substrates.

Improvement of GaN epilayer by gradient layer method with molecular-beam epitaxy

International Nuclear Information System (INIS)

Chen, Yen-Liang; Lo, Ikai; Gau, Ming-Hong; Hsieh, Chia-Ho; Sham, Meng-Wei; Pang, Wen-Yuan; Hsu, Yu-Chi; Tsai, Jenn-Kai; Schuber, Ralf; Schaadt, Daniel

2012-01-01

We demonstrated a molecular beam epitaxy method to resolve the dilemma between structural and morphological quality in growth of the GaN epilayer. A gradient buffer layer was grown in such a way that the N/Ga ratio was gradually changed from nitrogen-rich to gallium-rich. The GaN epitaxial layer was then grown on the gradient buffer layer. In the X-ray diffraction analysis of GaN(002) rocking curves, we found that the full width at half-maximum was improved from 531.69″ to 59.43″ for the sample with a gradient buffer layer as compared to a purely gallium-rich grown sample. Atomic force microscopy analysis showed that the root-mean-square roughness of the surface was improved from 18.28 nm to 1.62 nm over an area of 5 × 5 μm 2 with respect to a purely nitrogen-rich grown sample. Raman scattering showed the presence of a slightly tilted plane in the gradient layer. Furthermore we showed that the gradient layer can also slash the strain force caused by either Ga-rich GaN epitaxial layer or AlN buffer layer. - Highlights: ► The samples were grown by plasma-assisted molecular beam epitaxy. ► The GaN epilayer was grown on sapphire substrate. ► The samples were characterized by X-ray diffraction and atomic force microscopy. ► The sample quality was improved by gradient buffer layer.

Interaction of GaN epitaxial layers with atomic hydrogen

Energy Technology Data Exchange (ETDEWEB)

Losurdo, M.; Giangregorio, M.M.; Capezzuto, P.; Bruno, G.; Namkoong, G.; Doolittle, W.A.; Brown, A.S

2004-08-15

GaN surface passivation processes are still under development and among others hydrogen treatments are investigated. In this study, we use non-destructive optical and electrical probes such as spectroscopic ellipsometry (SE) and surface potential Kelvin probe microscopy (SP-KPM) in conjunction with non-contact atomic force microscopy (AFM) for the study of the different reactivity of Ga-polar and N-polar GaN epitaxial layers with atomic hydrogen. The GaN epitaxial layers are grown by molecular beam epitaxy on sapphire (0 0 0 1) substrates, and GaN and AlN buffer layers are used to grow N-polar and Ga-polar films, respectively. The atomic hydrogen is produced by a remote rf (13.56 MHz) H{sub 2} plasma in order to rule out any ion bombardment of the GaN surface and make the interaction chemical. It is found that the interaction of GaN surfaces with atomic hydrogen depends on polarity, with N-polar GaN exhibiting greater reactivity. Furthermore, it is found that atomic hydrogen is effective in the passivation of grain boundaries and surface defects states.

Interaction of GaN epitaxial layers with atomic hydrogen

International Nuclear Information System (INIS)

Losurdo, M.; Giangregorio, M.M.; Capezzuto, P.; Bruno, G.; Namkoong, G.; Doolittle, W.A.; Brown, A.S.

2004-01-01

GaN surface passivation processes are still under development and among others hydrogen treatments are investigated. In this study, we use non-destructive optical and electrical probes such as spectroscopic ellipsometry (SE) and surface potential Kelvin probe microscopy (SP-KPM) in conjunction with non-contact atomic force microscopy (AFM) for the study of the different reactivity of Ga-polar and N-polar GaN epitaxial layers with atomic hydrogen. The GaN epitaxial layers are grown by molecular beam epitaxy on sapphire (0 0 0 1) substrates, and GaN and AlN buffer layers are used to grow N-polar and Ga-polar films, respectively. The atomic hydrogen is produced by a remote rf (13.56 MHz) H 2 plasma in order to rule out any ion bombardment of the GaN surface and make the interaction chemical. It is found that the interaction of GaN surfaces with atomic hydrogen depends on polarity, with N-polar GaN exhibiting greater reactivity. Furthermore, it is found that atomic hydrogen is effective in the passivation of grain boundaries and surface defects states

Fabrication of GaN epitaxial thin film on InGaZnO4 single-crystalline buffer layer

International Nuclear Information System (INIS)

Shinozaki, Tomomasa; Nomura, Kenji; Katase, Takayoshi; Kamiya, Toshio; Hirano, Masahiro; Hosono, Hideo

2010-01-01

Epitaxial (0001) films of GaN were grown on (111) YSZ substrates using single-crystalline InGaZnO 4 (sc-IGZO) lattice-matched buffer layers by molecular beam epitaxy with a NH 3 source. The epitaxial relationships are (0001) GaN //(0001) IGZO //(111) YSZ in out-of-plane and [112-bar 0] GaN //[112-bar 0] IGZO //[11-bar 0] YSZ in in-plane. This is different from those reported for GaN on many oxide crystals; the in-plane orientation of GaN crystal lattice is rotated by 30 o with respect to those of oxide substrates except for ZnO. Although these GaN films showed relatively large tilting and twisting angles, which would be due to the reaction between GaN and IGZO, the GaN films grown on the sc-IGZO buffer layers exhibited stronger band-edge photoluminescence than GaN grown on a low-temperature GaN buffer layer.

Improvement of electrical property of Si-doped GaN grown on r-plane sapphire by metalorganic vapor-phase epitaxy

International Nuclear Information System (INIS)

Kusakabe, K.; Furuzuki, T.; Ohkawa, K.

2006-01-01

Electrical property of Si-doped GaN layers grown on r-plane sapphire substrates by atmospheric metalorganic vapor-phase epitaxy was investigated. The electron mobility was drastically improved when GaN was grown by means of optimized combinations of growth temperature and low-temperature GaN buffer thickness. The highest room-temperature mobility of 220cm 2 /Vs was recorded at the carrier density of 1.1x10 18 cm -3 . Temperature dependence of electrical property revealed that the peak mobility of 234cm 2 /Vs was obtained at 249K. From the slope of carrier density as a function of inverse temperature, the activation energy of Si-donors was evaluated to be 11meV

Infrared Reflectance Analysis of Epitaxial n-Type Doped GaN Layers Grown on Sapphire.

Science.gov (United States)

Tsykaniuk, Bogdan I; Nikolenko, Andrii S; Strelchuk, Viktor V; Naseka, Viktor M; Mazur, Yuriy I; Ware, Morgan E; DeCuir, Eric A; Sadovyi, Bogdan; Weyher, Jan L; Jakiela, Rafal; Salamo, Gregory J; Belyaev, Alexander E

2017-12-01

Infrared (IR) reflectance spectroscopy is applied to study Si-doped multilayer n + /n 0 /n + -GaN structure grown on GaN buffer with GaN-template/sapphire substrate. Analysis of the investigated structure by photo-etching, SEM, and SIMS methods showed the existence of the additional layer with the drastic difference in Si and O doping levels and located between the epitaxial GaN buffer and template. Simulation of the experimental reflectivity spectra was performed in a wide frequency range. It is shown that the modeling of IR reflectance spectrum using 2 × 2 transfer matrix method and including into analysis the additional layer make it possible to obtain the best fitting of the experimental spectrum, which follows in the evaluation of GaN layer thicknesses which are in good agreement with the SEM and SIMS data. Spectral dependence of plasmon-LO-phonon coupled modes for each GaN layer is obtained from the spectral dependence of dielectric of Si doping impurity, which is attributed to compensation effects by the acceptor states.

Improvement of GaN epilayer by gradient layer method with molecular-beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Chen, Yen-Liang [Department of Physics, Institute of Material Science and Engineering, Center for Nanoscience and Nanotechnology, National Sun Yat-Sen University, Kaohsiung 80424, Taiwan, ROC (China); Lo, Ikai, E-mail: ikailo@mail.phys.nsysu.edu.tw [Department of Physics, Institute of Material Science and Engineering, Center for Nanoscience and Nanotechnology, National Sun Yat-Sen University, Kaohsiung 80424, Taiwan, ROC (China); Gau, Ming-Hong; Hsieh, Chia-Ho; Sham, Meng-Wei; Pang, Wen-Yuan; Hsu, Yu-Chi [Department of Physics, Institute of Material Science and Engineering, Center for Nanoscience and Nanotechnology, National Sun Yat-Sen University, Kaohsiung 80424, Taiwan, ROC (China); Tsai, Jenn-Kai [Department of Electronics Engineering, National Formosa University, Hu-Wei, Yun-Lin County 63208, Taiwan, ROC (China); Schuber, Ralf; Schaadt, Daniel [Institute of Applied Physics/DFG-Center for Functional Nanostructures (CFN), Karlsruhe Institute of Technology (KIT), Karlsruhe (Germany)

2012-07-31

We demonstrated a molecular beam epitaxy method to resolve the dilemma between structural and morphological quality in growth of the GaN epilayer. A gradient buffer layer was grown in such a way that the N/Ga ratio was gradually changed from nitrogen-rich to gallium-rich. The GaN epitaxial layer was then grown on the gradient buffer layer. In the X-ray diffraction analysis of GaN(002) rocking curves, we found that the full width at half-maximum was improved from 531.69 Double-Prime to 59.43 Double-Prime for the sample with a gradient buffer layer as compared to a purely gallium-rich grown sample. Atomic force microscopy analysis showed that the root-mean-square roughness of the surface was improved from 18.28 nm to 1.62 nm over an area of 5 Multiplication-Sign 5 {mu}m{sup 2} with respect to a purely nitrogen-rich grown sample. Raman scattering showed the presence of a slightly tilted plane in the gradient layer. Furthermore we showed that the gradient layer can also slash the strain force caused by either Ga-rich GaN epitaxial layer or AlN buffer layer. - Highlights: Black-Right-Pointing-Pointer The samples were grown by plasma-assisted molecular beam epitaxy. Black-Right-Pointing-Pointer The GaN epilayer was grown on sapphire substrate. Black-Right-Pointing-Pointer The samples were characterized by X-ray diffraction and atomic force microscopy. Black-Right-Pointing-Pointer The sample quality was improved by gradient buffer layer.

Axial p-n junction and space charge limited current in single GaN nanowire

Science.gov (United States)

Fang, Zhihua; Donatini, Fabrice; Daudin, Bruno; Pernot, Julien

2018-01-01

The electrical characterizations of individual basic GaN nanostructures, such as axial nanowire (NW) p-n junctions, are becoming indispensable and crucial for the fully controlled realization of GaN NW based devices. In this study, electron beam induced current (EBIC) measurements were performed on two single axial GaN p-n junction NWs grown by plasma-assisted molecular beam epitaxy. I-V characteristics revealed that both ohmic and space charge limited current (SCLC) regimes occur in GaN p-n junction NW. Thanks to an improved contact process, both the electric field induced by the p-n junction and the SCLC in the p-part of GaN NW were disclosed and delineated by EBIC signals under different biases. Analyzing the EBIC profiles in the vicinity of the p-n junction under 0 V and reverse bias, we deduced a depletion width in the range of 116-125 nm. Following our previous work, the acceptor N a doping level was estimated to be 2-3 × 1017 at cm-3 assuming a donor level N d of 2-3 × 1018 at cm-3. The hole diffusion length in n-GaN was determined to be 75 nm for NW #1 and 43 nm for NW #2, demonstrating a low surface recombination velocity at the m-plane facet of n-GaN NW. Under forward bias, EBIC imaging visualized the electric field induced by the SCLC close to p-side contact, in agreement with unusual SCLC previously reported in GaN NWs.

Axial p-n junction and space charge limited current in single GaN nanowire.

Science.gov (United States)

Fang, Zhihua; Donatini, Fabrice; Daudin, Bruno; Pernot, Julien

2018-01-05

The electrical characterizations of individual basic GaN nanostructures, such as axial nanowire (NW) p-n junctions, are becoming indispensable and crucial for the fully controlled realization of GaN NW based devices. In this study, electron beam induced current (EBIC) measurements were performed on two single axial GaN p-n junction NWs grown by plasma-assisted molecular beam epitaxy. I-V characteristics revealed that both ohmic and space charge limited current (SCLC) regimes occur in GaN p-n junction NW. Thanks to an improved contact process, both the electric field induced by the p-n junction and the SCLC in the p-part of GaN NW were disclosed and delineated by EBIC signals under different biases. Analyzing the EBIC profiles in the vicinity of the p-n junction under 0 V and reverse bias, we deduced a depletion width in the range of 116-125 nm. Following our previous work, the acceptor N a doping level was estimated to be 2-3 × 10 17 at cm -3 assuming a donor level N d of 2-3 × 10 18 at cm -3 . The hole diffusion length in n-GaN was determined to be 75 nm for NW #1 and 43 nm for NW #2, demonstrating a low surface recombination velocity at the m-plane facet of n-GaN NW. Under forward bias, EBIC imaging visualized the electric field induced by the SCLC close to p-side contact, in agreement with unusual SCLC previously reported in GaN NWs.

Reduced-droop green III-nitride light-emitting diodes utilizing GaN tunnel junction

Science.gov (United States)

Alhassan, Abdullah I.; Young, Erin C.; Alyamani, Ahmed Y.; Albadri, Abdulrahman; Nakamura, Shuji; DenBaars, Steven P.; Speck, James S.

2018-04-01

We report the fabrication of low-droop high-efficiency green c-plane light-emitting diodes (LEDs) utilizing GaN tunnel junction (TJ) contacts. The LED epitaxial layers with a top p-GaN layer were grown by metal organic chemical vapor deposition and an n++-GaN layer was deposited by molecular beam epitaxy to form a TJ. The TJ LEDs were then compared with equivalent LEDs having a tin-doped indium oxide (ITO) contact. The TJ LEDs exhibited a higher performance and a lower efficiency droop than did the ITO LEDs. At 35 A/cm2, the external quantum efficiencies for the TJ and ITO LEDs were 31.2 and 27%, respectively.

Atomic layer epitaxy of ZnO for applications in molecular beam epitaxy growth of GaN and InGaN

International Nuclear Information System (INIS)

Godlewski, M.; Szczerbakow, A.; Ivanov, V. Yu.; Barski, A.; Goldys, E.M.

2000-01-01

We report the successful atomic layer epitaxy growth of thin ZnO films and their use for GaN and InGaN epitaxy. The properties of ZnO epilayers, obtained by four different procedures, are analysed, as well as of GaN and InGaN films grown on ZnO-coated Si and GaAs by MBE. (author)

Characterization of GaN quantum discs embedded in AlxGa1-xN nanocolumns grown by molecular beam epitaxy

International Nuclear Information System (INIS)

Ristic, J.; Calleja, E.; Sanchez-Garcia, M.A.; Ulloa, J.M.; Sanchez-Paramo, J.; Calleja, J.M.; Jahn, U.; Trampert, A.; Ploog, K.H.

2003-01-01

GaN quantum discs embedded in AlGaN nanocolumns with outstanding crystal quality and very high luminescence efficiency were grown on Si(111) substrates by plasma-assisted molecular beam epitaxy under highly N-rich conditions. Nanocolumns with diameters in the range of 30-150 nm, with no traces of any extended defects, as confirmed by transmission electron microscopy, were obtained. GaN quantum discs, 2 and 4 nm thick, were grown embedded in AlGaN nanocolumns by switching on and off the Al flux during variable time spans. Strong optical emissions from GaN quantum discs, observed by photoluminescence and cathodoluminescence measurements, reveal quantum confinement effects. While Raman data indicate that the nanocolumns are fully relaxed, the quantum discs appear to be fully strained. These nanostructures have a high potential for application in efficient vertical cavity emitters

P-N junction solar cell grown by molecular beam epitaxy

International Nuclear Information System (INIS)

Hazrati Fard, M.

2001-01-01

Growth of GaAs epilayers by Molecular Beam Epitaxy was accomplished for the first time in Iran. The layers were grown on GaAs (001) substrates (p+ wafer) with Si impurity for p n junction solar cell fabrication at a rate of nearly one micron per hour and 0.25 micron per quarter. Crystalline quality of grown layers had been monitored during growth by Reflection High Energy Electron Diffraction system. Doping profile and layer thickness was assessed by electrochemical C-V profiling method. Then Hall measurements were conducted on small samples both in room temperature and liquid nitrogen temperature so giving average carrier concentration and compensation ratio. The results as like: V oc , I sc , F F, η were comparable with other laboratory reports. information for obtaining good and repeatable growths was collected. Therefore, the conditions of repeatable quality growth p n junction solar cells onto GaAs (001) substrates were determined

Vertical current-flow enhancement via fabrication of GaN nanorod p–n junction diode on graphene

Energy Technology Data Exchange (ETDEWEB)

Ryu, Sung Ryong [Quantum-functional Semiconductor Research Center, Dongguk University-Seoul, 100-715 (Korea, Republic of); Department of physics, Dongguk University, Seoul, 100-715 (Korea, Republic of); Ram, S.D. Gopal; Lee, Seung Joo; Cho, Hak-dong; Lee, Sejoon [Quantum-functional Semiconductor Research Center, Dongguk University-Seoul, 100-715 (Korea, Republic of); Kang, Tae Won, E-mail: twkang@dongguk.edu [Quantum-functional Semiconductor Research Center, Dongguk University-Seoul, 100-715 (Korea, Republic of); Clean Energy and Nano Convergence Centre, Hindustan University, Chennai 600 016 (India); Kwon, Sangwoo; Yang, Woochul [Department of physics, Dongguk University, Seoul, 100-715 (Korea, Republic of); Shin, Sunhye [Soft-Epi Inc., 240 Opo-ro, Opo-eup, Gwangju-si, Gyeonggi-do (Korea, Republic of); Woo, Yongdeuk [Department of Mechanical and Automotive Engineering, Woosuk University, Chonbuk 565-701 (Korea, Republic of)

2015-08-30

Highlights: • Uniaxial p–n junction diode in GaN nanorod is made by Hydride vapor phase epitaxy method. • The p–n junction diode property is clearly observed from the fabricated uniaxial p–n junction nanorod GaN nanorod. • Graphene is used as a current spreading layer to reduce the lateral resistance up to 700 times when compared with the commercial sapphire substrate, which is clearly explained with the aid of an equivalent circuit. • Kelvin Force Probe microscopy method is employed to visualize the p- and n- regions in a single GaN nanorod. - Abstract: Mg doped GaN nanorods were grown on undoped n-type GaN nanorods uniaxial on monolayer graphene by hydride vapor phase epitaxy (HVPE) method. The monolayer graphene used as the bottom electrode and a substrate as well provides good electrical contact, acts as a current spreading layer, well suitable for the growth of hexagonal GaN nanorod. In addition it has a work function suitable to that of n-GaN. The formed p–n nanorods show a Schottky behavior with a turn on voltage of 3 V. Using graphene as the substrate, the resistance of the nanorod is reduced by 700 times when compared with the case without using graphene as the current spreading layer. The low resistance of graphene acts in parallel with the resistance of the GaN buffer layer, and reduces the resistance drastically. The formed p–n junction in a single GaN nanorod is visualized by Kelvin Force Probe Microscopy (KPFM) to have distinctively contrast p and n regions. The measured contact potential difference of p-and n-region has a difference of 103 mV which well confirms the formed regions are electronically different. Low temperature photoluminescence (PL) spectra give evidence of dopant related acceptor bound emission at 3.2 eV different from 3.4 eV of undoped GaN. The crystalline structure, compositional purity is confirmed by X-ray diffraction (XRD), Transmission and Scanning electron microcopies (SEM), (TEM), Energy dispersive analysis

Vertical current-flow enhancement via fabrication of GaN nanorod p–n junction diode on graphene

International Nuclear Information System (INIS)

Ryu, Sung Ryong; Ram, S.D. Gopal; Lee, Seung Joo; Cho, Hak-dong; Lee, Sejoon; Kang, Tae Won; Kwon, Sangwoo; Yang, Woochul; Shin, Sunhye; Woo, Yongdeuk

2015-01-01

Highlights: • Uniaxial p–n junction diode in GaN nanorod is made by Hydride vapor phase epitaxy method. • The p–n junction diode property is clearly observed from the fabricated uniaxial p–n junction nanorod GaN nanorod. • Graphene is used as a current spreading layer to reduce the lateral resistance up to 700 times when compared with the commercial sapphire substrate, which is clearly explained with the aid of an equivalent circuit. • Kelvin Force Probe microscopy method is employed to visualize the p- and n- regions in a single GaN nanorod. - Abstract: Mg doped GaN nanorods were grown on undoped n-type GaN nanorods uniaxial on monolayer graphene by hydride vapor phase epitaxy (HVPE) method. The monolayer graphene used as the bottom electrode and a substrate as well provides good electrical contact, acts as a current spreading layer, well suitable for the growth of hexagonal GaN nanorod. In addition it has a work function suitable to that of n-GaN. The formed p–n nanorods show a Schottky behavior with a turn on voltage of 3 V. Using graphene as the substrate, the resistance of the nanorod is reduced by 700 times when compared with the case without using graphene as the current spreading layer. The low resistance of graphene acts in parallel with the resistance of the GaN buffer layer, and reduces the resistance drastically. The formed p–n junction in a single GaN nanorod is visualized by Kelvin Force Probe Microscopy (KPFM) to have distinctively contrast p and n regions. The measured contact potential difference of p-and n-region has a difference of 103 mV which well confirms the formed regions are electronically different. Low temperature photoluminescence (PL) spectra give evidence of dopant related acceptor bound emission at 3.2 eV different from 3.4 eV of undoped GaN. The crystalline structure, compositional purity is confirmed by X-ray diffraction (XRD), Transmission and Scanning electron microcopies (SEM), (TEM), Energy dispersive analysis

Optical properties of C-doped bulk GaN wafers grown by halide vapor phase epitaxy

International Nuclear Information System (INIS)

Khromov, S.; Hemmingsson, C.; Monemar, B.; Hultman, L.; Pozina, G.

2014-01-01

Freestanding bulk C-doped GaN wafers grown by halide vapor phase epitaxy are studied by optical spectroscopy and electron microscopy. Significant changes of the near band gap (NBG) emission as well as an enhancement of yellow luminescence have been found with increasing C doping from 5 × 10 16 cm −3 to 6 × 10 17 cm −3 . Cathodoluminescence mapping reveals hexagonal domain structures (pits) with high oxygen concentrations formed during the growth. NBG emission within the pits even at high C concentration is dominated by a rather broad line at ∼3.47 eV typical for n-type GaN. In the area without pits, quenching of the donor bound exciton (DBE) spectrum at moderate C doping levels of 1–2 × 10 17 cm −3 is observed along with the appearance of two acceptor bound exciton lines typical for Mg-doped GaN. The DBE ionization due to local electric fields in compensated GaN may explain the transformation of the NBG emission

Atomic force microscopy studies of homoepitaxial GaN layers grown on GaN template by laser MBE

Energy Technology Data Exchange (ETDEWEB)

Choudhary, B. S. [CSIR-National Physical Laboratory, Dr K.S. Krishnan Road, New Delhi 110012 (India); Rajasthan Technical University, Rawatbhata Road, Kota 324010 (India); Singh, A.; Tyagi, P. K. [Department of Applied Physics, Delhi Technological University, Delhi 110042 (India); Tanwar, S. [Rajasthan Technical University, Rawatbhata Road, Kota 324010 (India); Kumar, M. Senthil; Kushvaha, S. S., E-mail: kushvahas@nplindia.org [CSIR-National Physical Laboratory, Dr K.S. Krishnan Road, New Delhi 110012 (India)

2016-04-13

We have grown homoepitaxial GaN films on metal organic chemical vapor deposition (MOCVD) grown 3.5 µm thick GaN on sapphire (0001) substrate (GaN template) using an ultra-high vacuum (UHV) laser assisted molecular beam epitaxy (LMBE) system. The GaN films were grown by laser ablating a polycrystalline solid GaN target in the presence of active r.f. nitrogen plasma. The influence of laser repetition rates (10-30 Hz) on the surface morphology of homoepitaxial GaN layers have been studied using atomic force microscopy. It was found that GaN layer grown at 10 Hz shows a smooth surface with uniform grain size compared to the rough surface with irregular shape grains obtained at 30 Hz. The variation of surface roughness of the homoepitaxial GaN layer with and without wet chemical etching has been also studied and it was observed that the roughness of the film decreased after wet etching due to the curved structure/rough surface.

Nanoselective area growth of GaN by metalorganic vapor phase epitaxy on 4H-SiC using epitaxial graphene as a mask

International Nuclear Information System (INIS)

Puybaret, Renaud; Jordan, Matthew B.; Voss, Paul L.; Ougazzaden, Abdallah; Patriarche, Gilles; Sundaram, Suresh; El Gmili, Youssef; Salvestrini, Jean-Paul; Heer, Walt A. de; Berger, Claire

2016-01-01

We report the growth of high-quality triangular GaN nanomesas, 30-nm thick, on the C-face of 4H-SiC using nanoselective area growth (NSAG) with patterned epitaxial graphene grown on SiC as an embedded mask. NSAG alleviates the problems of defects in heteroepitaxy, and the high mobility graphene film could readily provide the back low-dissipative electrode in GaN-based optoelectronic devices. A 5–8 graphene-layer film is first grown on the C-face of 4H-SiC by confinement-controlled sublimation of silicon carbide. Graphene is then patterned and arrays of 75-nm-wide openings are etched in graphene revealing the SiC substrate. A 30-nm-thick GaN is subsequently grown by metal organic vapor phase epitaxy. GaN nanomesas grow epitaxially with perfect selectivity on SiC, in the openings patterned through graphene. The up-or-down orientation of the mesas on SiC, their triangular faceting, and cross-sectional scanning transmission electron microscopy show that they are biphasic. The core is a zinc blende monocrystal surrounded with single-crystal wurtzite. The GaN crystalline nanomesas have no threading dislocations or V-pits. This NSAG process potentially leads to integration of high-quality III-nitrides on the wafer scalable epitaxial graphene/silicon carbide platform.

Nanoselective area growth of GaN by metalorganic vapor phase epitaxy on 4H-SiC using epitaxial graphene as a mask

Energy Technology Data Exchange (ETDEWEB)

Puybaret, Renaud; Jordan, Matthew B.; Voss, Paul L.; Ougazzaden, Abdallah, E-mail: aougazza@georgiatech-metz.fr [School of Electrical and Computer Engineering, Georgia Institute of Technology, Atlanta, Georgia 30332 (United States); CNRS UMI 2958, Georgia Institute of Technology, 2 Rue Marconi, 57070 Metz (France); Patriarche, Gilles [CNRS, Laboratoire de Photonique et de Nanostructures, Route de Nozay, 91460 Marcoussis (France); Sundaram, Suresh; El Gmili, Youssef [CNRS UMI 2958, Georgia Institute of Technology, 2 Rue Marconi, 57070 Metz (France); Salvestrini, Jean-Paul [Université de Lorraine, CentraleSupélec, LMOPS, EA4423, 57070 Metz (France); Heer, Walt A. de [School of Physics, Georgia Institute of Technology, Atlanta, Georgia 30332 (United States); Berger, Claire [School of Physics, Georgia Institute of Technology, Atlanta, Georgia 30332 (United States); CNRS, Institut Néel, BP166, 38042 Grenoble Cedex 9 (France)

2016-03-07

We report the growth of high-quality triangular GaN nanomesas, 30-nm thick, on the C-face of 4H-SiC using nanoselective area growth (NSAG) with patterned epitaxial graphene grown on SiC as an embedded mask. NSAG alleviates the problems of defects in heteroepitaxy, and the high mobility graphene film could readily provide the back low-dissipative electrode in GaN-based optoelectronic devices. A 5–8 graphene-layer film is first grown on the C-face of 4H-SiC by confinement-controlled sublimation of silicon carbide. Graphene is then patterned and arrays of 75-nm-wide openings are etched in graphene revealing the SiC substrate. A 30-nm-thick GaN is subsequently grown by metal organic vapor phase epitaxy. GaN nanomesas grow epitaxially with perfect selectivity on SiC, in the openings patterned through graphene. The up-or-down orientation of the mesas on SiC, their triangular faceting, and cross-sectional scanning transmission electron microscopy show that they are biphasic. The core is a zinc blende monocrystal surrounded with single-crystal wurtzite. The GaN crystalline nanomesas have no threading dislocations or V-pits. This NSAG process potentially leads to integration of high-quality III-nitrides on the wafer scalable epitaxial graphene/silicon carbide platform.

Epitaxial growth of M-plane GaN on ZnO micro-rods by plasma-assisted molecular beam epitaxy

Directory of Open Access Journals (Sweden)

Shuo-Ting You

2015-12-01

Full Text Available We have studied the GaN grown on ZnO micro-rods by plasma-assisted molecular beam epitaxy. From the analyses of GaN microstructure grown on non-polar M-plane ZnO surface ( 10 1 ̄ 0 by scanning transmission electron microscope, we found that the ZnGa2O4 compound was formed at the M-plane hetero-interface, which was confirmed by polarization-dependent photoluminescence. We demonstrated that the M-plane ZnO micro-rod surface can be used as an alternative substrate to grow high quality M-plane GaN epi-layers.

GaN Schottky diodes with single-crystal aluminum barriers grown by plasma-assisted molecular beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Tseng, H. Y.; Yang, W. C.; Lee, P. Y.; Lin, C. W.; Cheng, Kai-Yuan; Hsieh, K. C.; Cheng, K. Y., E-mail: kycheng@ee.nthu.edu.tw [Department of Electrical Engineering, National Tsing Hua University, Hsinchu 30013, Taiwan (China); Hsu, C.-H. [Division of Scientific Research, National Synchrotron Radiation Research Center, Hsinchu 30076, Taiwan (China)

2016-08-22

GaN-based Schottky barrier diodes (SBDs) with single-crystal Al barriers grown by plasma-assisted molecular beam epitaxy are fabricated. Examined using in-situ reflection high-energy electron diffractions, ex-situ high-resolution x-ray diffractions, and high-resolution transmission electron microscopy, it is determined that epitaxial Al grows with its [111] axis coincident with the [0001] axis of the GaN substrate without rotation. In fabricated SBDs, a 0.2 V barrier height enhancement and 2 orders of magnitude reduction in leakage current are observed in single crystal Al/GaN SBDs compared to conventional thermal deposited Al/GaN SBDs. The strain induced piezoelectric field is determined to be the major source of the observed device performance enhancements.

Polarized infrared reflectance study of free standing cubic GaN grown by molecular beam epitaxy

International Nuclear Information System (INIS)

Lee, S.C.; Ng, S.S.; Hassan, H. Abu; Hassan, Z.; Zainal, N.; Novikov, S.V.; Foxon, C.T.; Kent, A.J.

2014-01-01

Optical properties of free standing cubic gallium nitride grown by molecular beam epitaxy system are investigated by a polarized infrared (IR) reflectance technique. A strong reststrahlen band, which reveals the bulk-like optical phonon frequencies, is observed. Meanwhile, continuous oscillation fringes, which indicate the sample consists of two homogeneous layers with different dielectric constants, are observed in the non-reststrahlen region. By obtaining the first derivative of polarized IR reflectance spectra measured at higher angles of incidence, extra phonon resonances are identified at the edges of the reststrahlen band. The observations are verified with the theoretical results simulated based on a multi-oscillator model. - Highlights: • First time experimental studies of IR optical phonons in bulk like, cubic GaN layer. • Detection of extra phonon modes of cubic GaN by polarized IR reflectance technique. • Revelation of IR multiphonon modes of cubic GaN by first derivative numerical method. • Observation of multiphonon modes requires very high angle of incidence. • Resonance splitting effect induced by third phonon mode is a qualitative indicator

Cyan laser diode grown by plasma-assisted molecular beam epitaxy

International Nuclear Information System (INIS)

Turski, H.; Muziol, G.; Wolny, P.; Cywiński, G.; Grzanka, S.; Sawicka, M.; Perlin, P.; Skierbiszewski, C.

2014-01-01

We demonstrate AlGaN-cladding-free laser diodes (LDs), operating in continuous wave (CW) mode at 482 nm grown by plasma-assisted molecular beam epitaxy (PAMBE). The maximum CW output power was 230 mW. LDs were grown on c-plane GaN substrates obtained by hydride vapor phase epitaxy. The PAMBE process was carried out in metal-rich conditions, supplying high nitrogen flux (Φ N ) during quantum wells (QWs) growth. We found that high Φ N improves quality of high In content InGaN QWs. The role of nitrogen in the growth of InGaN on (0001) GaN surface as well as the influence of LDs design on threshold current density are discussed

Structural characteristics of single crystalline GaN films grown on (111) diamond with AlN buffer

DEFF Research Database (Denmark)

Pécz, Béla; Tóth, Lajos; Barna, Árpád

2013-01-01

Hexagonal GaN films with the [0001] direction parallel to the surface normal were grown on (111) oriented single crystalline diamond substrates by plasma-assisted molecular beam epitaxy. Pre-treatments of the diamond surface with the nitrogen plasma beam, prior the nucleation of a thin AlN layer......, eliminated the inversion domains and reduced the density of threading dislocations in the GaN epilayers. The films have an in-plane epitaxial relationship [1010]GaN//[110]diamond. Thus GaN (0001) thin films of single epitaxial relationship and of single polarity were realised on diamond with AlN buffer....

Epitaxial condition and polarity in GaN grown on a HfN-buffered Si(111) wafer

Science.gov (United States)

Xu, X.; Armitage, R.; Shinkai, Satoko; Sasaki, Katsutaka; Kisielowski, C.; Weber, E. R.

2005-05-01

Single-crystal GaN thin films have been deposited epitaxially on a HfN-buffered Si(111) substrates by molecular-beam epitaxy. The microstructural and compositional characteristics of the films were studied in detail by transmission electron microscopy (TEMs). Cross-sectional TEM investigations have revealed the crystallographic orientation relationship in different GaN /HfN/Si layers. GaN film polarity is studied by conventional TEM and convergent beam electron diffraction simulations, and the results show that the GaN film has a Ga polarity with relatively high density of inversion domains. Based on our observations, growth mechanisms related to the structural properties are discussed.

TEM characterization of catalyst- and mask-free grown GaN nanorods

International Nuclear Information System (INIS)

Schowalter, M; Aschenbrenner, T; Kruse, C; Hommel, D; Rosenauer, A

2010-01-01

Catalyst- and mask-free grown GaN nanorods have been investigated using transmission electron microscopy (TEM), scanning transmission electron microscopy (STEM) and energy filtered transmission electron microscopy (EFTEM). The nanorods were grown on nitridated r-plane sapphire substrates in a molecular beam epitaxy reactor. We investigated samples directly after the nitridation and after the overgrowth of the structure with GaN. High resolution transmission electron microscopy (HRTEM) and EFTEM revealed that AlN islands have formed due to nitridation. After overgrowth, the AlN islands could not be observed any more, neither by EFTEM nor by Z-contrast imaging. Instead, a smooth layer consisting of AlGaN was found. The investigation of the overgrown sample revealed that an a-plane GaN layer and GaN nanorods on top of the a-plane GaN have formed. The nanorods reduced from top of the a-plane GaN towards the a-plane GaN/sapphire interface suggesting that the nanorods originate at the AlN islands found after nitridation. However, this could not be shown unambiguously. The number of threading dislocations in the nanorods was very low. The analysis of the epitaxial relationship to the a-plane GaN showed that the nanorods grew along the [000-1] direction, and the [1-100] direction of the rods was parallel to the [0001] direction of the a-plane GaN.

Characterization of GaN/AlGaN epitaxial layers grown by ...

Indian Academy of Sciences (India)

GaN and AlGaN epitaxial layers are grown by a metalorganic chemical ... reported by introducing annealing of the GaN layer in nitrogen [5], Fe doping [6], .... [2] Y F Wu, S M Wood, R P Smith, S Sheppard, S T Allen, P Parikh and J Milligan,.

Effect of annealing on metastable shallow acceptors in Mg-doped GaN layers grown on GaN substrates

OpenAIRE

Pozina, Galia; Hemmingsson, Carl; Paskov, Plamen P.; Bergman, Peder; Monemar, Bo; Kawashima, T.; Amano, H.; Akasaki, I.; Usui, A.

2008-01-01

Mg-doped GaN layers grown by metal-organic vapor phase epitaxy on GaN substrates produced by the halide vapor phase technique demonstrate metastability of the near-band-gap photoluminescence (PL). The acceptor bound exciton (ABE) line possibly related to the C acceptor vanishes in as-grown samples within a few minutes under UV laser illumination. Annealing activates the more stable Mg acceptors and passivates C acceptors. Consequently, only the ABE line related to Mg is dominant in PL spectra...

Band offsets and growth mode of molecular beam epitaxy grown MgO (111) on GaN (0002) by x-ray photoelectron spectroscopy

Science.gov (United States)

Craft, H. S.; Collazo, R.; Losego, M. D.; Mita, S.; Sitar, Z.; Maria, J.-P.

2007-10-01

MgO is a proposed dielectric for use as a tunneling barrier in devices integrating GaN and ferroelectric oxides. In this study, we present data regarding the growth mode and band offsets of MgO grown epitaxially on GaN (0002) surfaces using molecular beam epitaxy. Using in situ x-ray photoelectron spectroscopy (XPS) and molecular beam epitaxy, we determine, from sequential growth experiments, that the growth of MgO proceeds via the Volmer-Weber (three-dimensional) mode, and full coalescence of the film does not occur until approximately 12nm of MgO has been deposited. The observation of a three-dimensional growth mode is in agreement with previously published data. For the valence band offset, we find a value of 1.2±0.2eV, which corresponds to a 3.2eV conduction band offset. XPS measurements suggest a chemically abrupt interface and no effect on band lineup due to the slow coalescence behavior.

Band offsets and growth mode of molecular beam epitaxy grown MgO (111) on GaN (0002) by x-ray photoelectron spectroscopy

International Nuclear Information System (INIS)

Craft, H. S.; Collazo, R.; Losego, M. D.; Mita, S.; Sitar, Z.; Maria, J.-P.

2007-01-01

MgO is a proposed dielectric for use as a tunneling barrier in devices integrating GaN and ferroelectric oxides. In this study, we present data regarding the growth mode and band offsets of MgO grown epitaxially on GaN (0002) surfaces using molecular beam epitaxy. Using in situ x-ray photoelectron spectroscopy (XPS) and molecular beam epitaxy, we determine, from sequential growth experiments, that the growth of MgO proceeds via the Volmer-Weber (three-dimensional) mode, and full coalescence of the film does not occur until approximately 12 nm of MgO has been deposited. The observation of a three-dimensional growth mode is in agreement with previously published data. For the valence band offset, we find a value of 1.2±0.2 eV, which corresponds to a 3.2 eV conduction band offset. XPS measurements suggest a chemically abrupt interface and no effect on band lineup due to the slow coalescence behavior

Influence of Si-doping on heteroepitaxially grown a-plane GaN

Energy Technology Data Exchange (ETDEWEB)

Wieneke, Matthias; Bastek, Barbara; Noltemeyer, Martin; Hempel, Thomas; Rohrbeck, Antje; Witte, Hartmut; Veit, Peter; Blaesing, Juergen; Dadgar, Armin; Christen, Juergen; Krost, Alois [Otto-von-Guericke-Universitaet Magdeburg, FNW/IEP, Universitaetsplatz 2, 39106 Magdeburg (Germany)

2011-07-01

Si-doped a-plane GaN samples with nominal doping levels up to 10{sup 20} cm{sup -3} were grown on r-plane sapphire by metal organic vapor phase epitaxy. Silane flow rates higher than 59 nmol/min lead to three dimensional grown crystallites as revealed by scanning electron microscopy. High resolution X-ray diffraction, photoluminescence and cathodoluminescence suggest considerably reduced defect densities in the large micrometer-sized GaN crystallites. Especially, transmission electron microscopy images verify a very low density of basal plane stacking faults less than 10{sup 4} cm{sup -1} in these crystallites consisting of heteroepitaxially grown a-plane GaN. In our presentation the influence of the Si doping on the basal plane stacking faults will be discussed.

Real time ellipsometry for monitoring plasma-assisted epitaxial growth of GaN

Energy Technology Data Exchange (ETDEWEB)

Bruno, Giovanni [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM UdR Bari, via Orabona, 4, 70126 Bari (Italy); Losurdo, Maria [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM UdR Bari, via Orabona, 4, 70126 Bari (Italy)]. E-mail: maria.losurdo@ba.imip.cnr.it; Giangregorio, Maria M. [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM UdR Bari, via Orabona, 4, 70126 Bari (Italy); Capezzuto, Pio [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM UdR Bari, via Orabona, 4, 70126 Bari (Italy); Brown, April S. [Department of Electrical and Computer Engineering, Duke University, 128 Hudson Hall, Durham, NC (United States); Kim, Tong-Ho [Department of Electrical and Computer Engineering, Duke University, 128 Hudson Hall, Durham, NC (United States); Choi, Soojeong [Department of Electrical and Computer Engineering, Duke University, 128 Hudson Hall, Durham, NC (United States)

2006-10-31

GaN is grown on Si-face 4H-SiC(0 0 0 1) substrates using remote plasma-assisted methods including metalorganic chemical vapour deposition (RP-MOCVD) and molecular beam epitaxy (MBE). Real time spectroscopic ellipsometry is used for monitoring all the steps of substrate pre-treatments and the heteroepitaxial growth of GaN on SiC. Our characterization emphasis is on understanding the nucleation mechanism and the GaN growth mode, which depend on the SiC surface preparation.

Elimination of macrostep-induced current flow nonuniformity in vertical GaN PN diode using carbon-free drift layer grown by hydride vapor phase epitaxy

Science.gov (United States)

Fujikura, Hajime; Hayashi, Kentaro; Horikiri, Fumimasa; Narita, Yoshinobu; Konno, Taichiro; Yoshida, Takehiro; Ohta, Hiroshi; Mishima, Tomoyoshi

2018-04-01

In vertical GaN PN diodes (PNDs) grown entirely by metal–organic chemical vapor deposition (MOCVD), large current nonuniformity was observed. This nonuniformity was induced by macrosteps on the GaN surface through modulation of carbon incorporation into the n-GaN crystal. It was eliminated in a hybrid PND consisting of a carbon-free n-GaN layer grown by hydride vapor phase epitaxy (HVPE) and an MOCVD-regrown p-GaN layer. The hybrid PND showed a fairly low on-resistance (2 mΩ cm2) and high breakdown voltage (2 kV) even without a field plate electrode. These results clearly indicated the strong advantages of the HVPE-grown drift layer for improving power device performance, uniformity, and yield.

Preparation of freestanding GaN wafer by hydride vapor phase epitaxy on porous silicon

Science.gov (United States)

Wu, Xian; Li, Peng; Liang, Renrong; Xiao, Lei; Xu, Jun; Wang, Jing

2018-05-01

A freestanding GaN wafer was prepared on porous Si (111) substrate using hydride vapor phase epitaxy (HVPE). To avoid undesirable effects of the porous surface on the crystallinity of the GaN, a GaN seed layer was first grown on the Si (111) bare wafer. A pattern with many apertures was fabricated in the GaN seed layer using lithography and etching processes. A porous layer was formed in the Si substrate immediately adjacent to the GaN seed layer by an anodic etching process. A 500-μm-thick GaN film was then grown on the patterned GaN seed layer using HVPE. The GaN film was separated from the Si substrate through the formation of cracks in the porous layer caused by thermal mismatch stress during the cooling stage of the HVPE. Finally, the GaN film was polished to obtain a freestanding GaN wafer.

Microstructures of GaN1-xPx layers grown on (0001) GaN substrates by gas source molecular beam epitaxy

Science.gov (United States)

Seong, Tae-Yeon; Bae, In-Tae; Choi, Chel-Jong; Noh, D. Y.; Zhao, Y.; Tu, C. W.

1999-03-01

Transmission electron microscope (TEM), transmission electron diffraction (TED), and synchrotron x-ray diffraction (XRD) studies have been performed to investigate microstructural behavior of gas source molecular beam epitaxial GaN1-xPx layers grown on (0001) GaN/sapphire at temperatures (Tg) in the range 500-760 °C. TEM, TED, and XRD results indicate that the samples grown at Tg⩽600 °C undergo phase separation resulting in a mixture of GaN-rich and GaP-rich GaNP with zinc-blende structure. However, the samples grown at Tg⩾730 °C are found to be binary zinc-blende GaN(P) single crystalline materials. As for the 500 °C layer, the two phases are randomly oriented and distributed, whereas the 600 °C layer consists of phases that are elongated and inclined by 60°-70° clockwise from the [0001]α-GaN direction. The samples grown at Tg⩾730 °C are found to consist of two types of microdomains, namely, GaN(P)I and GaN(P)II; the former having twin relation to the latter.

Lateral epitaxial overgrowth of GaN on a patterned GaN-on-silicon substrate by molecular beam epitaxy

International Nuclear Information System (INIS)

Wang, Yongjin; Hu, Fangren; Hane, Kazuhiro

2011-01-01

We report here the lateral epitaxial overgrowth (LEO) of GaN on a patterned GaN-on-silicon substrate by molecular beam epitaxy (MBE) growth with radio frequency nitrogen plasma as a gas source. Two kinds of GaN nanostructures are defined by electron beam lithography and realized on a GaN substrate by fast atom beam etching. The epitaxial growth of GaN by MBE is performed on the prepared GaN template, and the selective growth of GaN takes place with the assistance of GaN nanostructures. The LEO of GaN produces novel GaN epitaxial structures which are dependent on the shape and the size of the processed GaN nanostructures. Periodic GaN hexagonal pyramids are generated inside the air holes, and GaN epitaxial strips with triangular section are formed in the grating region. This work provides a promising way for producing novel GaN-based devices by the LEO of GaN using the MBE technique

Large-area, laterally-grown epitaxial semiconductor layers

Science.gov (United States)

Han, Jung; Song, Jie; Chen, Danti

2017-07-18

Structures and methods for confined lateral-guided growth of a large-area semiconductor layer on an insulating layer are described. The semiconductor layer may be formed by heteroepitaxial growth from a selective growth area in a vertically-confined, lateral-growth guiding structure. Lateral-growth guiding structures may be formed in arrays over a region of a substrate, so as to cover a majority of the substrate region with laterally-grown epitaxial semiconductor tiles. Quality regions of low-defect, stress-free GaN may be grown on silicon.

Photoconduction efficiencies and dynamics in GaN nanowires grown by chemical vapor deposition and molecular beam epitaxy: A comparison study

International Nuclear Information System (INIS)

Chen, R. S.; Tsai, H. Y.; Huang, Y. S.; Chen, Y. T.; Chen, L. C.; Chen, K. H.

2012-01-01

The normalized gains, which determines the intrinsic photoconduction (PC) efficiencies, have been defined and compared for the gallium nitride (GaN) nanowires (NWs) grown by chemical vapor deposition (CVD) and molecular beam epitaxy (MBE). By excluding the contributions of experimental parameters and under the same light intensity, the CVD-grown GaN NWs exhibit the normalized gain which is near two orders of magnitude higher than that of the MBE-ones. The temperature-dependent time-resolved photocurrent measurement further indicates that the higher photoconduction efficiency in the CVD-GaN NWs is originated from the longer carrier lifetime induced by the higher barrier height (φ B = 160 ± 30 mV) of surface band bending. In addition, the experimentally estimated barrier height at 20 ± 2 mV for the MBE-GaN NWs, which is much lower than the theoretical value, is inferred to be resulted from the lower density of charged surface states on the non-polar side walls.

Strain-free GaN thick films grown on single crystalline ZnO buffer layer with in situ lift-off technique

International Nuclear Information System (INIS)

Lee, S. W.; Minegishi, T.; Lee, W. H.; Goto, H.; Lee, H. J.; Lee, S. H.; Lee, Hyo-Jong; Ha, J. S.; Goto, T.; Hanada, T.; Cho, M. W.; Yao, T.

2007-01-01

Strain-free freestanding GaN layers were prepared by in situ lift-off process using a ZnO buffer as a sacrificing layer. Thin Zn-polar ZnO layers were deposited on c-plane sapphire substrates, which was followed by the growth of Ga-polar GaN layers both by molecular beam epitaxy (MBE). The MBE-grown GaN layer acted as a protecting layer against decomposition of the ZnO layer and as a seeding layer for GaN growth. The ZnO layer was completely in situ etched off during growth of thick GaN layers at low temperature by hydride vapor phase epitaxy. Hence freestanding GaN layers were obtained for the consecutive growth of high-temperature GaN thick layers. The lattice constants of freestanding GaN agree with those of strain-free GaN bulk. Extensive microphotoluminescence study indicates that strain-free states extend throughout the high-temperature grown GaN layers

Real time spectroscopic ellipsometry investigation of homoepitaxial GaN grown by plasma assisted molecular beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Kim, Tong-Ho; Choi, Soojeong; Wu, Pae; Brown, April [Department of Electrical and Computer Engineering, Duke University, 128 Hudson Hall, Durham, NC (United States); Losurdo, Maria; Giangregorio, Maria M.; Bruno, Giovanni [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR and INSTM UdR Bari, via Orabona, 4, 70126 Bari (Italy); Moto, Akihiro [Innovation Core SEI, Inc., 3235 Kifer Road, Santa Clara, CA 95051 (United States)

2006-06-15

The growth of GaN by plasma assisted molecular beam epitaxy on GaN template substrates (GaN on sapphire) is investigated with in-situ multi-channel spectroscopic ellipsometry. Growth is performed under various Ga/N flux ratios at growth temperatures in the range 710-780 C. The thermal roughening of the GaN template caused by decomposition of the surface is investigated through the temporal variation of the GaN pseudodielectric function over the temperature range of 650 C to 850 C. The structural, morphological, and optical properties are also discussed. (copyright 2006 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Buffer optimization for crack-free GaN epitaxial layers grown on Si(1 1 1) substrate by MOCVD

International Nuclear Information System (INIS)

Arslan, Engin; Ozbay, Ekmel; Ozturk, Mustafa K; Ozcelik, Suleyman; Teke, Ali

2008-01-01

We report the growth of GaN films on the Si(1 1 1) substrate by metalorganic chemical vapour phase deposition (MOCVD). Different buffer layers were used to investigate their effects on the structural and optical properties of GaN layers. A series of GaN layers were grown on Si(1 1 1) with different buffer layers and buffer thicknesses and were characterized by Nomarski microscopy, atomic force microscopy, high-resolution x-ray diffraction (XRD) and photoluminescence (PL) measurements. We first discuss the optimization of the LT-AlN/HT-AlN/Si(1 1 1) templates and then the optimization of the graded AlGaN intermediate layers. In order to prevent stress relaxation, step-graded AlGaN layers were introduced along with a crack-free GaN layer of thickness exceeding 2.6 μm. The XRD and PL measurements results confirmed that a wurtzite GaN was successfully grown. The resulting GaN film surfaces were flat, mirror-like and crack-free. The mosaic structure in the GaN layers was investigated. With a combination of Williamson-Hall measurements and the fitting of twist angles, it was found that the buffer thickness determines the lateral coherence length, vertical coherence length, as well as the tilt and twist of the mosaic blocks in GaN films. The PL spectra at 8 K show that a strong band edge photoluminescence of GaN on Si (1 1 1) emits light at an energy of 3.449 eV with a full width at half maximum (FWHM) of approximately 16 meV. At room temperature, the peak position and FWHM of this emission become 3.390 eV and 58 meV, respectively. The origin of this peak was attributed to the neutral donor bound exciton. It was found that the optimized total thickness of the AlN and graded AlGaN layers played a very important role in the improvement of quality and in turn reduced the cracks during the growth of GaN/Si(1 1 1) epitaxial layers

Horizontal Assembly of Single Nanowire Diode Fabricated by p-n Junction GaN NW Grown by MOCVD

Directory of Open Access Journals (Sweden)

Ji-Hyeon Park

2014-01-01

Full Text Available Uniaxially p-n junction gallium nitride nanowires have been synthesized via metal-organic chemical vapor deposition method. Nanowires prepared on Si(111 substrates were found to grow perpendicular to the substrate, and the transmission electron microscopy studies demonstrated that the nanowires had singlecrystalline structures with a growth axis. The parallel assembly of the p-n junction nanowire was prepared on a Si substrate with a thermally grown SiO2 layer. The transport studies of horizontal gallium nitride nanowire structures assembled from p- and n-type materials show that these junctions correspond to well-defined p-n junction diodes. The p-n junction devices based on GaN nanowires suspended over the electrodes were fabricated and their electrical properties were investigated. The horizontally assembled gallium nitride nanowire diodes suspended over the electrodes exhibited a substantial increase in conductance under UV light exposure. Apart from the selectivity to different light wavelengths, high responsivity and extremely short response time have also been obtained.

m-plane GaN layers grown by rf-plasma assisted molecular beam epitaxy with varying Ga/N flux ratios on m-plane 4H-SiC substrates

International Nuclear Information System (INIS)

Armitage, R.; Horita, M.; Suda, J.; Kimoto, T.

2007-01-01

A series of m-plane GaN layers with the Ga beam-equivalent pressure (BEP) as the only varied parameter was grown by rf-plasma assisted molecular beam epitaxy on m-plane 4H-SiC substrates using AlN buffer layers. The smoothest growth surfaces and most complete film coalescence were found for the highest Ga BEP corresponding to the Ga droplet accumulation regime. However, better structural quality as assessed by x-ray rocking curves was observed for growth at a lower Ga BEP value below the droplet limit. The variation of rocking curve widths for planes inclined with respect to the epilayer c axis followed a different trend with Ga BEP than those of reflections parallel to the c axis. The GaN layers were found to exhibit a large residual compressive strain along the a axis

High electron mobility through the edge states in random networks of c-axis oriented wedge-shaped GaN nanowalls grown by molecular beam epitaxy

International Nuclear Information System (INIS)

Bhasker, H. P.; Dhar, S.; Sain, A.; Kesaria, Manoj; Shivaprasad, S. M.

2012-01-01

Transport and optical properties of random networks of c-axis oriented wedge-shaped GaN nanowalls grown spontaneously on c-plane sapphire substrates through molecular beam epitaxy are investigated. Our study suggests a one dimensional confinement of carriers at the top edges of these connected nanowalls, which results in a blue shift of the band edge luminescence, a reduction of the exciton-phonon coupling, and an enhancement of the exciton binding energy. Not only that, the yellow luminescence in these samples is found to be completely suppressed even at room temperature. All these changes are highly desirable for the enhancement of the luminescence efficiency of the material. More interestingly, the electron mobility through the network is found to be significantly higher than that is typically observed for GaN epitaxial films. This dramatic improvement is attributed to the transport of electrons through the edge states formed at the top edges of the nanowalls.

Mg doping of GaN grown by plasma-assisted molecular beam epitaxy under nitrogen-rich conditions

International Nuclear Information System (INIS)

Zhang Meng; Bhattacharya, Pallab; Guo Wei; Banerjee, Animesh

2010-01-01

Acceptor doping of GaN with Mg during plasma-assisted molecular beam epitaxy, under N-rich conditions and a relatively high growth temperature of 740 deg. C, was investigated. The p-doping level steadily increases with increasing Mg flux. The highest doping level achieved, determined from Hall measurements, is 2.1x10 18 cm -3 . The corresponding doping efficiency and hole mobility are ∼4.9% and 3.7 cm 2 /V s at room temperature. Cross-sectional transmission electron microscopy and photoluminescence measurements confirm good crystalline and optical quality of the Mg-doped layers. An InGaN/GaN quantum dot light emitting diode (λ peak =529 nm) with p-GaN contact layers grown under N-rich condition exhibits a low series resistance of 9.8 Ω.

The trap states in lightly Mg-doped GaN grown by MOVPE on a freestanding GaN substrate

Science.gov (United States)

Narita, Tetsuo; Tokuda, Yutaka; Kogiso, Tatsuya; Tomita, Kazuyoshi; Kachi, Tetsu

2018-04-01

We investigated traps in lightly Mg-doped (2 × 1017 cm-3) p-GaN fabricated by metalorganic vapor phase epitaxy (MOVPE) on a freestanding GaN substrate and the subsequent post-growth annealing, using deep level transient spectroscopy. We identified four hole traps with energy levels of EV + 0.46, 0.88, 1.0, and 1.3 eV and one electron trap at EC - 0.57 eV in a p-type GaN layer uniformly doped with magnesium (Mg). The Arrhenius plot of hole traps with the highest concentration (˜3 × 1016 cm-3) located at EV + 0.88 eV corresponded to those of hole traps ascribed to carbon on nitrogen sites in n-type GaN samples grown by MOVPE. In fact, the range of the hole trap concentrations at EV + 0.88 eV was close to the carbon concentration detected by secondary ion mass spectroscopy. Moreover, the electron trap at EC - 0.57 eV was also identical to the dominant electron traps commonly observed in n-type GaN. Together, these results suggest that the trap states in the lightly Mg-doped GaN grown by MOVPE show a strong similarity to those in n-type GaN, which can be explained by the Fermi level close to the conduction band minimum in pristine MOVPE grown samples due to existing residual donors and Mg-hydrogen complexes.

Fabrication of magnetic tunnel junctions with epitaxial and textured ferromagnetic layers

Science.gov (United States)

Chang, Y. Austin; Yang, Jianhua Joshua

2008-11-11

This invention relates to magnetic tunnel junctions and methods for making the magnetic tunnel junctions. The magnetic tunnel junctions include a tunnel barrier oxide layer sandwiched between two ferromagnetic layers both of which are epitaxial or textured with respect to the underlying substrate upon which the magnetic tunnel junctions are grown. The magnetic tunnel junctions provide improved magnetic properties, sharper interfaces and few defects.

Epitaxial growth and characterization of approximately 300-nm-thick AlInN films nearly lattice-matched to c-plane GaN grown on sapphire

Science.gov (United States)

Miyoshi, Makoto; Yamanaka, Mizuki; Egawa, Takashi; Takeuchi, Tetsuya

2018-05-01

AlInN epitaxial films with film thicknesses up to approximately 300 nm were grown nearly lattice-matched to a c-plane GaN-on-sapphire template by metalorganic chemical vapor deposition. The AlInN films showed relative good crystal qualities and flat surfaces, despite the existence of surface pits connected to dislocations in the underlying GaN film. The refractive index derived in this study agreed well with a previously reported result obtained over the whole visible wavelength region. The extinction coefficient spectrum exhibited a clear absorption edge, and the bandgap energy for AlInN nearly lattice-matched to GaN was determined to be approximately 4.0 eV.

Epitaxial Ge Solar Cells Directly Grown on Si (001) by MOCVD Using Isobutylgermane

Science.gov (United States)

Kim, Youngjo; Kim, Kangho; Lee, Jaejin; Kim, Chang Zoo; Kang, Ho Kwan; Park, Won-Kyu

2018-03-01

Epitaxial Ge layers have been grown on Si (001) substrates by metalorganic chemical vapor deposition (MOCVD) using an isobutylgermane (IBuGe) metalorganic source. Low and high temperature two-step growth and post annealing techniques are employed to overcome the lattice mismatch problem between Ge and Si. It is demonstrated that high quality Ge epitaxial layers can be grown on Si (001) by using IBuGe with surface RMS roughness of 2 nm and an estimated threading dislocation density of 4.9 × 107 cm -2. Furthermore, single-junction Ge solar cells have been directly grown on Si substrates with an in situ MOCVD growth. The epitaxial Ge p- n junction structures are investigated with transmission electron microscopy and electrochemical C- V measurements. As a result, a power conversion efficiency of 1.69% was achieved for the Ge solar cell directly grown on Si substrate under AM1.5G condition.

Characterization of as-grown and heavily irradiated GaN epitaxial structures by photoconductivity and photoluminescence

International Nuclear Information System (INIS)

Gaubas, E.; Jurs e-dot nas, S.; Tomasiunas, R.; Vaitkus, J.; Zukauskas, A.; Blue, A.; Rahman, M.; Smith, K.M.

2005-01-01

The influence of radiation defects on photoconductivity transients and photoluminescence (PL) spectra have been examined in semi-insulating GaN epitaxial layers grown on bulk n-GaN/sapphire substrates. Defects induced by 10-keV X-ray irradiation with a dose of 600Mrad and 100-keV neutrons with fluences of 5x10 14 and 10 16 cm -2 have been revealed through contact photoconductivity and microwave absorption transients. The amplitude of the initial photoconductivity decay is significantly reduced by the radiation defect density. A simultaneous decrease with radiation-induced defect density is also observed in the steady-state PL intensity of yellow, blue and ultraviolet bands peaked at 2.18, 2.85, and 3.42eV, respectively. The decrease of the PL intensity is accompanied by an increase of asymptotic decay lifetime, which is due to excess carrier multi-trapping. The decay can be described by the stretched exponential approximation exp[-(t/τ) α ] with different values of α in as-grown material (α∼0.7) and irradiated samples (α∼0.3). The value of the fracton dimension d s of the disordered structure, evaluated as d s =2α/(1-α), changes from 4.7 to 0.86 for as-grown and irradiated material, respectively, implying percolative carrier motion on an infinite cluster of dislocations net in the as-grown material and cluster fragmentation into finite fractons after irradiation

Electrical, luminescent, and deep trap properties of Si doped n-GaN grown by pendeo epitaxy

Energy Technology Data Exchange (ETDEWEB)

Polyakov, A. Y. [National University of Science and Technology MISiS, Leninskiy pr. 4, Moscow 119049 (Russian Federation); Smirnov, N. B. [National University of Science and Technology MISiS, Leninskiy pr. 4, Moscow 119049 (Russian Federation); Institute of Rare Metals, B. Tolmachevsky, 5, Moscow 119017 (Russian Federation); Yakimov, E. B. [National University of Science and Technology MISiS, Leninskiy pr. 4, Moscow 119049 (Russian Federation); Institute of Microelectronics Technology and High Purity Materials, Russian Academy of Science, 6, Academician Ossipyan str., Chernogolovka, Moscow Region 142432 (Russian Federation); Lee, In-Hwan, E-mail: ihlee@jbnu.ac.kr [School of Advanced Materials Engineering and Research Center of Advanced Materials Development, Chonbuk National University, Jeonju 561-756 (Korea, Republic of); Pearton, S. J. [University of Florida, Gainesville, Florida 32611 (United States)

2016-01-07

Electrical and luminescent properties and deep trap spectra of Si doped GaN films grown by maskless epitaxial lateral overgrowth (MELO) are reported. The dislocation density in the wing region of the structure was 10{sup 6 }cm{sup −2}, while in the seed region it was 10{sup 8 }cm{sup −2}. The major electron traps present had activation energy of 0.56 eV and concentrations in the high 10{sup 15 }cm{sup −3} range. A comparison of diffusion length values and 0.56 eV trap concentration in MELO GaN and epitaxial lateral overgrowth (ELOG) GaN showed a good correlation, suggesting these traps could be effective in carrier recombination. The doped MELO films were more uniform in their electrical properties than either ELOG films or undoped MELO films. We also discuss the differences in deep trap spectra and luminescence spectra of low-dislocation-density MELO, ELOG, and bulk n-GaN samples grown by hydride vapor phase epitaxy. It is suggested that the observed differences could be caused by the differences in oxygen and carbon contamination levels.

Structural and optical inhomogeneities of Fe doped GaN grown by hydride vapor phase epitaxy

Science.gov (United States)

Malguth, E.; Hoffmann, A.; Phillips, M. R.

2008-12-01

We present the results of cathodoluminescence experiments on a set of Fe doped GaN samples with Fe concentrations of 5×1017, 1×1018, 1×1019, and 2×1020 cm-3. These specimens were grown by hydride vapor phase epitaxy with different concentrations of Fe. The introduction of Fe is found to promote the formation of structurally inhomogeneous regions of increased donor concentration. We detect a tendency of these regions to form hexagonal pits at the surface. The locally increased carrier concentration leads to enhanced emission from the band edge and the internal T41(G)-A61(S) transition of Fe3+. In these areas, the luminescence forms a finely structured highly symmetric pattern, which is attributed to defect migration along strain-field lines. Fe doping is found to quench the yellow defect luminescence band and to enhance the blue luminescence band due to the lowering of the Fermi level and the formation of point defects, respectively.

Electronic Transport Mechanism for Schottky Diodes Formed by Au/HVPE a-Plane GaN Templates Grown via In Situ GaN Nanodot Formation

Directory of Open Access Journals (Sweden)

Moonsang Lee

2018-06-01

Full Text Available We investigate the electrical characteristics of Schottky contacts for an Au/hydride vapor phase epitaxy (HVPE a-plane GaN template grown via in situ GaN nanodot formation. Although the Schottky diodes present excellent rectifying characteristics, their Schottky barrier height and ideality factor are highly dependent upon temperature variation. The relationship between the barrier height, ideality factor, and conventional Richardson plot reveals that the Schottky diodes exhibit an inhomogeneous barrier height, attributed to the interface states between the metal and a-plane GaN film and to point defects within the a-plane GaN layers grown via in situ nanodot formation. Also, we confirm that the current transport mechanism of HVPE a-plane GaN Schottky diodes grown via in situ nanodot formation prefers a thermionic field emission model rather than a thermionic emission (TE one, implying that Poole–Frenkel emission dominates the conduction mechanism over the entire range of measured temperatures. The deep-level transient spectroscopy (DLTS results prove the presence of noninteracting point-defect-assisted tunneling, which plays an important role in the transport mechanism. These electrical characteristics indicate that this method possesses a great throughput advantage for various applications, compared with Schottky contact to a-plane GaN grown using other methods. We expect that HVPE a-plane GaN Schottky diodes supported by in situ nanodot formation will open further opportunities for the development of nonpolar GaN-based high-performance devices.

Nucleation of single GaN nanorods with diameters smaller than 35 nm by molecular beam epitaxy

International Nuclear Information System (INIS)

Chen, Yen-Ting; Araki, Tsutomu; Palisaitis, Justinas; Persson, Per O. Å.; Olof Holtz, Per; Birch, Jens; Chen, Li-Chyong; Chen, Kuei-Hsien; Nanishi, Yasushi

2013-01-01

Nucleation mechanism of catalyst-free GaN nanorod grown on Si(111) is investigated by the fabrication of uniform and narrow (<35 nm) nanorods without a pre-defined mask by molecular beam epitaxy. Direct evidences show that the nucleation of GaN nanorods stems from the sidewall of the underlying islands down to the Si(111) substrate, different from commonly reported ones on top of the island directly. Accordingly, the growth and density control of the nanorods is exploited by a “narrow-pass” approach that only narrow nanorod can be grown. The optimal size of surrounding non-nucleation area around single nanorod is estimated as 88 nm

Nucleation of single GaN nanorods with diameters smaller than 35 nm by molecular beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Chen, Yen-Ting [Institute of Atomic and Molecular Sciences, Academia Sinica, 10617 Taipei, Taiwan (China); Department of Physics, Chemistry and Biology (IFM), Linköping University, S-58183 Linköping (Sweden); Araki, Tsutomu [Department of Electrical and Electronic Engineering, Ritsumeikan University, 525-8577 Shiga (Japan); Palisaitis, Justinas; Persson, Per O. Å.; Olof Holtz, Per; Birch, Jens [Department of Physics, Chemistry and Biology (IFM), Linköping University, S-58183 Linköping (Sweden); Chen, Li-Chyong [Center for Condensed Matter Sciences, National Taiwan University, 10617 Taipei, Taiwan (China); Chen, Kuei-Hsien [Institute of Atomic and Molecular Sciences, Academia Sinica, 10617 Taipei, Taiwan (China); Center for Condensed Matter Sciences, National Taiwan University, 10617 Taipei, Taiwan (China); Nanishi, Yasushi [Global Innovation Research Organization, Ritsumeikan University, 525-8577 Shiga (Japan)

2013-11-11

Nucleation mechanism of catalyst-free GaN nanorod grown on Si(111) is investigated by the fabrication of uniform and narrow (<35 nm) nanorods without a pre-defined mask by molecular beam epitaxy. Direct evidences show that the nucleation of GaN nanorods stems from the sidewall of the underlying islands down to the Si(111) substrate, different from commonly reported ones on top of the island directly. Accordingly, the growth and density control of the nanorods is exploited by a “narrow-pass” approach that only narrow nanorod can be grown. The optimal size of surrounding non-nucleation area around single nanorod is estimated as 88 nm.

Hall-effect measurements of metalorganic vapor-phase epitaxy-grown p-type homoepitaxial GaN layers with various Mg concentrations

Science.gov (United States)

Horita, Masahiro; Takashima, Shinya; Tanaka, Ryo; Matsuyama, Hideaki; Ueno, Katsunori; Edo, Masaharu; Takahashi, Tokio; Shimizu, Mitsuaki; Suda, Jun

2017-03-01

Mg-doped p-type gallium nitride (GaN) layers with doping concentrations in the range from 6.5 × 1016 cm-3 (lightly doped) to 3.8 × 1019 cm-3 (heavily doped) were investigated by Hall-effect measurement for the analysis of hole concentration and mobility. p-GaN was homoepitaxially grown on a GaN free-standing substrate by metalorganic vapor-phase epitaxy. The threading dislocation density of p-GaN was 4 × 106 cm-2 measured by cathodoluminescence mapping. Hall-effect measurements of p-GaN were carried out at a temperature in the range from 130 to 450 K. For the lightly doped p-GaN, the acceptor concentration of 7.0 × 1016 cm-3 and the donor concentration of 3.2 × 1016 cm-3 were obtained, where the compensation ratio was 46%. We also obtained the depth of the Mg acceptor level to be 220 meV. The hole mobilities of 86, 31, 14 cm2 V-1 s-1 at 200, 300, 400 K, respectively, were observed in the lightly doped p-GaN.

Growth of cubic GaN on a nitrided AlGaAs (001) substrate by using hydried vapor phase epitaxy

International Nuclear Information System (INIS)

Lee, H. J.; Yang, M.; Ahn, H. S.; Kim, K. H.; Yi, J. Y.; Jang, K. S.; Chang, J. H.; Kim, H. S.; Cho, C. R.; Kim, S. W.

2006-01-01

GaN layers were grown on AlGaAs (001) substrates by using hydride vapor phase epitaxy (HVPE). Growth parameters such as the nitridation temperature of the AlGaAs substrate and the growth rate of the GaN layer were found to be critical determinants for the growth of cubic GaN layer. Nitridation of the AlGaAs surface was performed in a NH 3 atmosphere at a temperature range of 550 - 700 .deg. C. GaN layers were grown at different growth rates on the nitrided AlGaAs substrates. The surface morphologies and the chemical constituents of the nitrided AlGaAs layers were characterized with scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). For the optical and the crystalline characterization of the GaN films, cathodoluminescence (CL) and X-ray diffraction (XRD) were carried out.

Effect of III/V ratio on the polarity of AlN and GaN layers grown in the metal rich growth regime on Si(111) by plasma assisted molecular beam epitaxy

International Nuclear Information System (INIS)

Agrawal, Manvi; Dharmarasu, Nethaji; Radhakrishnan, K.; Pramana, Stevin Snellius

2015-01-01

Wet chemical etching, reflection high energy electron diffraction, scanning electron microscope and convergent beam electron diffraction have been employed to study the polarities of AlN and the subsequently grown GaN as a function of metal flux in the metal rich growth regime. Both AlN and GaN exhibited metal polarity in the intermediate growth conditions. However, in the droplet growth regime, the polarity of AlN and GaN were N polar and Ga polar, respectively. It was observed that Ga polar GaN could be obtained on both Al and N polar AlN. AlGaN/GaN high electron mobility transistor (HEMT) heterostructure exhibiting hall mobility of 900 cm 2 V -1 s -1 and sheet carrier density of 1.2 × 10 13 cm -2 was demonstrated using N polar AlN which confirmed Ga polarity of GaN. Al metal flux was likely to play an important role in controlling the polarity of AlN and determining the polarity of the subsequent GaN grown on Si(111) by plasma assisted molecular beam epitaxy (PA-MBE). (author)

Metal modulation epitaxy growth for extremely high hole concentrations above 1019 cm-3 in GaN

Science.gov (United States)

Namkoong, Gon; Trybus, Elaissa; Lee, Kyung Keun; Moseley, Michael; Doolittle, W. Alan; Look, David C.

2008-10-01

The free hole carriers in GaN have been limited to concentrations in the low 1018cm-3 range due to the deep activation energy, lower solubility, and compensation from defects, therefore, limiting doping efficiency to about 1%. Herein, we report an enhanced doping efficiency up to ˜10% in GaN by a periodic doping, metal modulation epitaxy growth technique. The hole concentrations grown by periodically modulating Ga atoms and Mg dopants were over ˜1.5×1019cm-3.

Blue-violet InGaN laser diodes grown on bulk GaN substrates by plasma-assisted molecular-beam epitaxy

International Nuclear Information System (INIS)

Skierbiszewski, C.; Wasilewski, Z.R.; Siekacz, M.; Feduniewicz, A.; Perlin, P.; Wisniewski, P.; Borysiuk, J.; Grzegory, I.; Leszczynski, M.; Suski, T.; Porowski, S.

2005-01-01

We report on the InGaN multiquantum laser diodes (LDs) made by rf plasma-assisted molecular beam epitaxy (PAMBE). The laser operation at 408 nm is demonstrated at room temperature with pulsed current injections using 50 ns pulses at 0.25% duty cycle. The threshold current density and voltage for the LDs with cleaved uncoated mirrors are 12 kA/cm 2 (900 mA) and 9 V, respectively. High output power of 0.83 W is obtained during pulse operation at 3.6 A and 9.6 V bias with the slope efficiency of 0.35 W/A. The laser structures are deposited on the high-pressure-grown low dislocation bulk GaN substrates taking full advantage of the adlayer enhanced lateral diffusion channel for adatoms below the dynamic metallic cover. Our devices compare very favorably to the early laser diodes fabricated using the metalorganic vapor phase epitaxy technique, providing evidence that the relatively low growth temperatures used in this process pose no intrinsic limitations on the quality of the blue optoelectronic components that can be fabricated using PAMBE

The influence of Fe doping on the surface topography of GaN epitaxial material

International Nuclear Information System (INIS)

Cui Lei; Yin Haibo; Jiang Lijuan; Wang Quan; Feng Chun; Xiao Hongling; Wang Cuimei; Wang Xiaoliang; Gong Jiamin; Zhang Bo; Li Baiquan; Wang Zhanguo

2015-01-01

Fe doping is an effective method to obtain high resistivity GaN epitaxial material. But in some cases, Fe doping could result in serious deterioration of the GaN material surface topography, which will affect the electrical properties of two dimensional electron gas (2DEG) in HEMT device. In this paper, the influence of Fe doping on the surface topography of GaN epitaxial material is studied. The results of experiments indicate that the surface topography of Fe-doped GaN epitaxial material can be effectively improved and the resistivity could be increased after increasing the growth rate of GaN materials. The GaN material with good surface topography can be manufactured when the Fe doping concentration is 9 × 10 19 cm −3 . High resistivity GaN epitaxial material which is 1 × 10 9 Ω·cm is achieved. (paper)

Addition of Sb as a surfactant for the growth of nonpolar a-plane GaN by using mixed-source hydride vapor phase epitaxy

International Nuclear Information System (INIS)

Ok, Jin Eun; Jo, Dong Wan; Yun, Wy Il; Han, Young Hun; Jeon, Hun Soo; Lee, Gang Suok; Jung, Se Gyo; Bae, Seon Min; Ahn, Hyung Soo; Yang, Min

2011-01-01

The influence of Sb as a surfactant on the morphology and on the structural and the optical characteristics of a-plane GaN grown on r-plane sapphire by using mixed-source hydride vapor phase epitaxy was investigated. The a-plane GaN:Sb layers were grown at various temperatures ranging from 1000 .deg. C to 1100 .deg. C, and the reactor pressure was maintained at 1 atm. The atomic force microscope (AFM), scanning electron microscope (SEM), X-ray diffraction (XRD) and photoluminescence(PL) results indicated that the surface morphologies and the structural and the optical characteristics of a-plane GaN were markedly improved, compared to the a-plane GaN layers grown without Sb, by using Sb as a surfactant. The addition of Sb was found to alter epitaxial lateral overgrowth (ELO) facet formation. The Sb was not detected from the a-plane-GaN epilayers within the detection limit of the energy dispersive spectroscopy (EDS) and x-ray photoelectron spectroscopy (XPS) measurements, suggesting that Sb act as a surfactant during the growth of a-plane GaN by using mixed-source HVPE method.

Metal modulation epitaxy growth for extremely high hole concentrations above 1019 cm-3 in GaN

International Nuclear Information System (INIS)

Namkoong, Gon; Trybus, Elaissa; Lee, Kyung Keun; Moseley, Michael; Doolittle, W. Alan; Look, David C.

2008-01-01

The free hole carriers in GaN have been limited to concentrations in the low 10 18 cm -3 range due to the deep activation energy, lower solubility, and compensation from defects, therefore, limiting doping efficiency to about 1%. Herein, we report an enhanced doping efficiency up to ∼10% in GaN by a periodic doping, metal modulation epitaxy growth technique. The hole concentrations grown by periodically modulating Ga atoms and Mg dopants were over ∼1.5x10 19 cm -3

Hybrid tunnel junction contacts to III–nitride light-emitting diodes

KAUST Repository

Young, Erin C.; Yonkee, Benjamin P.; Wu, Feng; Oh, Sang Ho; DenBaars, Steven P.; Nakamura, Shuji; Speck, James S.

2016-01-01

In this work, we demonstrate highly doped GaN p–n tunnel junction (TJ) contacts on III–nitride heterostructures where the active region of the device and the top p-GaN layers were grown by metal organic chemical vapor deposition and highly doped n-GaN was grown by NH3 molecular beam epitaxy to form the TJ. The regrowth interface in these hybrid devices was found to have a high concentration of oxygen, which likely enhanced tunneling through the diode. For optimized regrowth, the best tunnel junction device had a total differential resistivity of 1.5 × 10−4 Ω cm2, including contact resistance. As a demonstration, a blue-light-emitting diode on a ($20\\bar{2}\\bar{1}$) GaN substrate with a hybrid tunnel junction and an n-GaN current spreading layer was fabricated and compared with a reference sample with a transparent conducting oxide (TCO) layer. The tunnel junction LED showed a lower forward operating voltage and a higher efficiency at a low current density than the TCO LED.

Hybrid tunnel junction contacts to III–nitride light-emitting diodes

KAUST Repository

Young, Erin C.

2016-01-26

In this work, we demonstrate highly doped GaN p–n tunnel junction (TJ) contacts on III–nitride heterostructures where the active region of the device and the top p-GaN layers were grown by metal organic chemical vapor deposition and highly doped n-GaN was grown by NH3 molecular beam epitaxy to form the TJ. The regrowth interface in these hybrid devices was found to have a high concentration of oxygen, which likely enhanced tunneling through the diode. For optimized regrowth, the best tunnel junction device had a total differential resistivity of 1.5 × 10−4 Ω cm2, including contact resistance. As a demonstration, a blue-light-emitting diode on a ($20\\\\bar{2}\\\\bar{1}$) GaN substrate with a hybrid tunnel junction and an n-GaN current spreading layer was fabricated and compared with a reference sample with a transparent conducting oxide (TCO) layer. The tunnel junction LED showed a lower forward operating voltage and a higher efficiency at a low current density than the TCO LED.

Integration and electrical properties of epitaxial LiNbO{sub 3} ferroelectric film on n-type GaN semiconductor

Energy Technology Data Exchange (ETDEWEB)

Hao Lanzhong, E-mail: hao_lanzhong@live.cn [State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054 (China); Faculty of Science, China University of Petroleum, Tsingtao, Shandong 266555 (China); Zhu Jun, E-mail: junzhu@uestc.edu.cn [State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054 (China); Liu Yunjie [Faculty of Science, China University of Petroleum, Tsingtao, Shandong 266555 (China); Wang Shuili; Zeng Huizhong; Liao Xiuwei; Liu Yingying; Lei Huawei; Zhang Ying; Zhang Wanli; Li Yanrong [State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054 (China)

2012-01-31

LiNbO{sub 3} (LNO) films were epitaxially grown on n-type GaN templates using pulsed laser deposition technique. The microstructures and electrical properties of the LNO/GaN heterostructure were characterized by x-ray diffraction, transmission electron microscope, and capacitance-voltage (C-V) measurements. The LNO films had two variants of grains rotated 60 Degree-Sign in-plane to each other. The epitaxial relationship of the respective variants could be built as [10-10]LNO//[1-210]GaN and [1-100]LNO//[11-20]GaN via 30 Degree-Sign in-plane rotation of the LNO film relative to the GaN layer. Interface analysis of the heterostructure demonstrated that two different epitaxial growth mechanisms vertical heteroepitaxy and lateral homoepitaxy, should happen at the interface of LNO/GaN. Counterclockwise C-V windows induced by the ferroelectric polarizations of LNO film could be observed clearly. The size of the window increased with increasing the sweep bias and a large window of 5.8 V was achieved at {+-} 15 V. By solving Poisson and drift-diffusion equations, the physical mechanisms of the C-V characteristics were demonstrated.

Ellipsometric study of GaN/AIN/Si(111) heterostructures grown by molecular beam epitaxy

International Nuclear Information System (INIS)

Nabi, M. A. U.; Ashfaq, A.; Arshad, M. I.; Ali, A.; Mahmood, K.; Hasan, M. A.; Asghar, M.

2013-01-01

GaN and related structures attracted a great interest in the recent years for electronic and optoelectronic applications due to their promising properties. GaN is grown popularly on foreign substrates like sapphire and SiC. However, silicon due to its favourable properties attended the great attention of material scientists and researchers to utilize as substrate for heteroepitaxy of GaN based structures and devices. Silicon substrates are low cost, available in large diameters and have well characterized thermal and electrical properties. In this study, GaN/AlN/Si(111) heterostructures were grown by molecular beam epitaxy. We performed x-ray diffraction spectroscopy and spectroscopic ellipsometry on these samples to study their structural and optical properties. XRD measurements performed on these samples revealed the presence of high quality GaN films as well as the presence of AlN buffer layer with the following miller indices: GaN (002), GaN (004), GaN (006) and GaN (110) along with Si peak of phase (111). The ellipsometric data obtained were used to characterize the GaN/Si samples as a function of film thickness. Refractive index, extinction coefficient and dielectric constant were calculated by the measured data. (author)

Spectroscopic and magnetic properties of Mn doped GaN epitaxial films grown by plasma assisted molecular beam epitaxy

International Nuclear Information System (INIS)

Vidyasagar, R.; Lin, Y.-T.; Tu, L.-W.

2012-01-01

Graphical abstract: We report here that micro-Raman scattering spectrum for Mn doped GaN thin film has displayed a new peak manifested at 578 cm −1 , by which it is attributed to interior LVM originated by the incorporation of Mn ions in place of Ga sites. Mn doped GaN thin film also showed the typical negative magnetoresistance up to ∼50 K, revealing that the film showed magnetic ordering of spins below 50 K. Display Omitted Highlights: ► GaN and Mn doped GaN single phase wurtzite structures grown by PAMBE. ► The phase purity of the epilayers investigated by HRXRD, HRSEM and EDX. ► The red shift in near band edge emission has been observed using micro-PL. ► A new peak related LVM at 578 cm −1 in micro-Raman scattering measurements confirmed Mn doped into GaN. ► Negative-magnetoresistance investigations have showed that the film has T c −1 , which is attributed to the vacancy-related local vibrational mode of Mn occupying the Ga site. Temperature dependent negative magnetoresistance measurements provide a direct evidence of magnetic ordering below 50 K for the Mn doped GaN thin film.

White emission from non-planar InGaN/GaN MQW LEDs grown on GaN template with truncated hexagonal pyramids.

Science.gov (United States)

Lee, Ming-Lun; Yeh, Yu-Hsiang; Tu, Shang-Ju; Chen, P C; Lai, Wei-Chih; Sheu, Jinn-Kong

2015-04-06

Non-planar InGaN/GaN multiple quantum well (MQW) structures are grown on a GaN template with truncated hexagonal pyramids (THPs) featuring c-plane and r-plane surfaces. The THP array is formed by the regrowth of the GaN layer on a selective-area Si-implanted GaN template. Transmission electron microscopy shows that the InGaN/GaN epitaxial layers regrown on the THPs exhibit different growth rates and indium compositions of the InGaN layer between the c-plane and r-plane surfaces. Consequently, InGaN/GaN MQW light-emitting diodes grown on the GaN THP array emit multiple wavelengths approaching near white light.

Carrier confinement effects of InxGa1-xN/GaN multi quantum disks with GaN surface barriers grown in GaN nanorods

Science.gov (United States)

Park, Youngsin; Chan, Christopher C. S.; Taylor, Robert A.; Kim, Nammee; Jo, Yongcheol; Lee, Seung W.; Yang, Woochul; Im, Hyunsik

2018-04-01

Structural and optical properties of InxGa1-xN/GaN multi quantum disks (QDisks) grown on GaN nanorods by molecular beam epitaxy have been investigated by transmission electron microscopy and micro-photoluminescence (PL) spectroscopy. Two types of InGaN QDisks were grown: a pseudo-3D confined InGaN pillar-type QDisks embedded in GaN nanorods; and QDisks in flanged cone type GaN nanorods. The PL emission peak and excitation dependent PL behavior of the pillar-type Qdisks differ greatly from those of the flanged cone type QDisks. Time resolved PL was carried out to probe the differences in charge carrier dynamics. The results suggest that by constraining the formation of InGaN QDisks within the centre of the nanorod, carriers are restricted from migrating to the surface, decreasing the surface recombination at high carrier densities.

Multilayer porous structures of HVPE and MOCVD grown GaN for photonic applications

Science.gov (United States)

Braniste, T.; Ciers, Joachim; Monaico, Ed.; Martin, D.; Carlin, J.-F.; Ursaki, V. V.; Sergentu, V. V.; Tiginyanu, I. M.; Grandjean, N.

2017-02-01

In this paper we report on a comparative study of electrochemical processes for the preparation of multilayer porous structures in hydride vapor phase epitaxy (HVPE) and metal organic chemical vapor phase deposition (MOCVD) grown GaN. It was found that in HVPE-grown GaN, multilayer porous structures are obtained due to self-organization processes leading to a fine modulation of doping during the crystal growth. However, these processes are not totally under control. Multilayer porous structures with a controlled design have been produced by optimizing the technological process of electrochemical etching in MOCVD-grown samples, consisting of five pairs of thin layers with alternating-doping profiles. The samples have been characterized by SEM imaging, photoluminescence spectroscopy, and micro-reflectivity measurements, accompanied by transfer matrix analysis and simulations by a method developed for the calculation of optical reflection spectra. We demonstrate the applicability of the produced structures for the design of Bragg reflectors.

Stress engineering in GaN structures grown on Si(111) substrates by SiN masking layer application

Energy Technology Data Exchange (ETDEWEB)

Szymański, Tomasz, E-mail: tomasz.szymanski@pwr.edu.pl; Wośko, Mateusz; Paszkiewicz, Bogdan; Paszkiewicz, Regina [The Faculty of Microsystem Electronics and Photonics, Wrocaw University of Technology, Janiszewskiego 11/17, 50-372 Wroclaw (Poland); Drzik, Milan [International Laser Center, Ilkovicova 3, 841-04 Bratislava 4 (Slovakia)

2015-07-15

GaN layers without and with an in-situ SiN mask were grown by using metal organic vapor phase epitaxy for three different approaches used in GaN on silicon(111) growth, and the physical and optical properties of the GaN layers were studied. For each approach applied, GaN layers of 1.4 μm total thickness were grown, using silan SiH{sub 4} as Si source in order to grow Si{sub x}N{sub x} masking layer. The optical micrographs, scanning electron microscope images, and atomic force microscope images of the grown samples revealed cracks for samples without SiN mask, and micropits, which were characteristic for the samples grown with SiN mask. In situ reflectance signal traces were studied showing a decrease of layer coalescence time and higher degree of 3D growth mode for samples with SiN masking layer. Stress measurements were conducted by two methods—by recording micro-Raman spectra and ex-situ curvature radius measurement—additionally PLs spectra were obtained revealing blueshift of PL peak positions with increasing stress. The authors have shown that a SiN mask significantly improves physical and optical properties of GaN multilayer systems reducing stress in comparison to samples grown applying the same approaches but without SiN masking layer.

Demonstration of forward inter-band tunneling in GaN by polarization engineering

International Nuclear Information System (INIS)

Krishnamoorthy, Sriram; Park, Pil Sung; Rajan, Siddharth

2011-01-01

We report on the design, fabrication, and characterization of GaN interband tunnel junction showing forward tunneling characteristics. We have achieved very high forward tunneling currents (153 mA/cm 2 at 10 mV, and 17.7 A/cm 2 peak current) in polarization-engineered GaN/InGaN/GaN heterojunction diodes grown by plasma assisted molecular beam epitaxy. We also report the observation of repeatable negative differential resistance in interband III-Nitride tunnel junctions, with peak-valley current ratio of 4 at room temperature. The forward current density achieved in this work meets the typical current drive requirements of a multi-junction solar cell.

High quality self-separated GaN crystal grown on a novel nanoporous template by HVPE.

Science.gov (United States)

Huo, Qin; Shao, Yongliang; Wu, Yongzhong; Zhang, Baoguo; Hu, Haixiao; Hao, Xiaopeng

2018-02-16

In this study, a novel nanoporous template was obtained by a two-step etching process from MOCVD-GaN/Al 2 O 3 (MGA) with electrochemical etching sequentially followed by chemical wet etching. The twice-etched MOCVD-GaN/Al 2 O 3 (TEMGA) templates were utilized to grow GaN crystals by hydride vapor phase epitaxy (HVPE) method. The GaN crystals were separated spontaneously from the TEMGA template with the assistance of voids formed by the etched nanopores. Several techniques were utilized to characterize the quality of the free-standing GaN crystals obtained from the TEMGA template. Results showed that the quality of the as-obtained GaN crystals was improved obviously compared with those grown on the MGA. This convenient technique can be applied to grow high-quality free-standing GaN crystals.

GaN and LED structures grown on pre-patterned silicon pillar arrays

Energy Technology Data Exchange (ETDEWEB)

Li, Shunfeng; Fuendling, Soenke; Soekmen, Uensal; Merzsch, Stephan; Neumann, Richard; Peiner, Erwin; Wehmann, Hergo-Heinrich; Waag, Andreas [Institut fuer Halbleitertechnik, TU Braunschweig, Hans-Sommer-Strasse 66, 38106 Braunschweig (Germany); Hinze, Peter; Weimann, Thomas [Physikalisch-Technische Bundesanstalt (PTB), Bundesallee 100, 38116 Braunschweig (Germany); Jahn, Uwe; Trampert, Achim; Riechert, Henning [Paul-Drude-Institut fuer Festkoerperelektronik, Hausvoigteiplatz 5-7, 10117 Berlin (Germany)

2010-01-15

GaN nanorods (or nanowires) have attracted great interest in a variety of applications, e.g. high-efficiency light emitting diodes, monolithic white light emission and optical interconnection due to their superior properties. In contrast to the mostly investigated self-assembled growth of GaN nanorods, we performed GaN nanorod growth by pre-patterning of the Si substrates. The pattern was transferred to Si substrates by photolithography and cryo-temperature inductively-coupled plasma etching. These Si templates then were used for further GaN nanorod growth by metal-organic vapour phase epitaxy (MOVPE). The low temperature AlN nucleation layer had to be optimized since it differs from its 2D layer counterpart on the surface area and orientations. We found a strong influence of diffusion processes, i.e. the GaN grown on top of the Si nanopillars can deplete the GaN around the Si pillars. Transmission electron microscopy measurements demonstrated clearly that the threading dislocations bend to the side facets of the pyramidal GaN nanostructures and terminate. Cathodoluminescence measurements reveal a difference of In composition and/or thickness of InGaN quantum wells on the different facets of the pyramidal GaN nanostructures. (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Reproducible increased Mg incorporation and large hole concentration in GaN using metal modulated epitaxy

International Nuclear Information System (INIS)

Burnham, Shawn D.; Doolittle, W. Alan; Namkoong, Gon; Look, David C.; Clafin, Bruce

2008-01-01

The metal modulated epitaxy (MME) growth technique is reported as a reliable approach to obtain reproducible large hole concentrations in Mg-doped GaN grown by plasma-assisted molecular-beam epitaxy on c-plane sapphire substrates. An extremely Ga-rich flux was used, and modulated with the Mg source according to the MME growth technique. The shutter modulation approach of the MME technique allows optimal Mg surface coverage to build between MME cycles and Mg to incorporate at efficient levels in GaN films. The maximum sustained concentration of Mg obtained in GaN films using the MME technique was above 7x10 20 cm -3 , leading to a hole concentration as high as 4.5x10 18 cm -3 at room temperature, with a mobility of 1.1 cm 2 V -1 s -1 and a resistivity of 1.3 Ω cm. At 580 K, the corresponding values were 2.6x10 19 cm -3 , 1.2 cm 2 V -1 s -1 , and 0.21 Ω cm, respectively. Even under strong white light, the sample remained p-type with little change in the electrical parameters

Reproducible increased Mg incorporation and large hole concentration in GaN using metal modulated epitaxy

Science.gov (United States)

Burnham, Shawn D.; Namkoong, Gon; Look, David C.; Clafin, Bruce; Doolittle, W. Alan

2008-07-01

The metal modulated epitaxy (MME) growth technique is reported as a reliable approach to obtain reproducible large hole concentrations in Mg-doped GaN grown by plasma-assisted molecular-beam epitaxy on c-plane sapphire substrates. An extremely Ga-rich flux was used, and modulated with the Mg source according to the MME growth technique. The shutter modulation approach of the MME technique allows optimal Mg surface coverage to build between MME cycles and Mg to incorporate at efficient levels in GaN films. The maximum sustained concentration of Mg obtained in GaN films using the MME technique was above 7×1020cm-3, leading to a hole concentration as high as 4.5×1018cm-3 at room temperature, with a mobility of 1.1cm2V-1s-1 and a resistivity of 1.3Ωcm. At 580K, the corresponding values were 2.6×1019cm-3, 1.2cm2V-1s-1, and 0.21Ωcm, respectively. Even under strong white light, the sample remained p-type with little change in the electrical parameters.

The investigation of stress in freestanding GaN crystals grown from Si substrates by HVPE.

Science.gov (United States)

Lee, Moonsang; Mikulik, Dmitry; Yang, Mino; Park, Sungsoo

2017-08-17

We investigate the stress evolution of 400 µm-thick freestanding GaN crystals grown from Si substrates by hydride vapour phase epitaxy (HVPE) and the in situ removal of Si substrates. The stress generated in growing GaN can be tuned by varying the thickness of the MOCVD AlGaN/AlN buffer layers. Micro Raman analysis shows the presence of slight tensile stress in the freestanding GaN crystals and no stress accumulation in HVPE GaN layers during the growth. Additionally, it is demonstrated that the residual tensile stress in HVPE GaN is caused only by elastic stress arising from the crystal quality difference between Ga- and N-face GaN. TEM analysis revealed that the dislocations in freestanding GaN crystals have high inclination angles that are attributed to the stress relaxation of the crystals. We believe that the understanding and characterization on the structural properties of the freestanding GaN crystals will help us to use these crystals for high-performance opto-electronic devices.

Influence of substrate quality on structural properties of AlGaN/GaN superlattices grown by molecular beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Schubert, F. [NaMLab gGmbH, Nöthnitzer Straße 64, 01187 Dresden (Germany); Merkel, U.; Schmult, S. [TU Dresden, Institute of Semiconductors and Microsystems, Nöthnitzer Straße 64, 01187 Dresden (Germany); Mikolajick, T. [NaMLab gGmbH, Nöthnitzer Straße 64, 01187 Dresden (Germany); TU Dresden, Institute of Semiconductors and Microsystems, Nöthnitzer Straße 64, 01187 Dresden (Germany)

2014-02-28

Short-period AlGaN/GaN superlattices were established as versatile test structures to investigate the structural properties of molecular beam epitaxy (MBE)-grown GaN and AlGaN layers and their dependence on the GaN substrate quality. X-ray diffractometry data of the investigated superlattices allow access to relevant structural parameters such as aluminum mole fraction and layer thicknesses. The occurrence of theoretically predicted intense high-order satellite peaks and pronounced interface fringes in the diffraction pattern reflects abrupt interfaces and perfect 2-dimensional growth resulting in smooth surfaces. The data unambiguously demonstrate that the structural quality of the MBE grown layers is limited by the structural properties of the GaN substrate.

Microstructures and growth mechanisms of GaN films epitaxially grown on AlN/Si hetero-structures by pulsed laser deposition at different temperatures.

Science.gov (United States)

Wang, Wenliang; Yang, Weijia; Lin, Yunhao; Zhou, Shizhong; Li, Guoqiang

2015-11-13

2 inch-diameter GaN films with homogeneous thickness distribution have been grown on AlN/Si(111) hetero-structures by pulsed laser deposition (PLD) with laser rastering technique. The surface morphology, crystalline quality, and interfacial property of as-grown GaN films are characterized in detail. By optimizing the laser rastering program, the ~300 nm-thick GaN films grown at 750 °C show a root-mean-square (RMS) thickness inhomogeneity of 3.0%, very smooth surface with a RMS surface roughness of 3.0 nm, full-width at half-maximums (FWHMs) for GaN(0002) and GaN(102) X-ray rocking curves of 0.7° and 0.8°, respectively, and sharp and abrupt AlN/GaN hetero-interfaces. With the increase in the growth temperature from 550 to 850 °C, the surface morphology, crystalline quality, and interfacial property of as-grown ~300 nm-thick GaN films are gradually improved at first and then decreased. Based on the characterizations, the corresponding growth mechanisms of GaN films grown on AlN/Si hetero-structures by PLD with various growth temperatures are hence proposed. This work would be beneficial to understanding the further insight of the GaN films grown on Si(111) substrates by PLD for the application of GaN-based devices.

Reduction of buffer layer conduction near plasma-assisted molecular-beam epitaxy grown GaN/AlN interfaces by beryllium doping

International Nuclear Information System (INIS)

Storm, D.F.; Katzer, D.S.; Binari, S.C.; Glaser, E.R.; Shanabrook, B.V.; Roussos, J.A.

2002-01-01

Beryllium doping of epitaxial GaN layers is used to reduce leakage currents through interfacial or buffer conducting layers grown by plasma-assisted molecular-beam epitaxy on SiC. Capacitance-voltage measurements of Schottky barrier test structures and dc pinch-off characteristics of unintentionally doped GaN high-electron-mobility transistors indicate that these leakage currents are localized near the GaN/AlN interface of our AlGaN/GaN/AlN device structures. Insertion of a 2000 Aa Be:GaN layer at the interface reduces these currents by three orders of magnitude

Molecular-Beam Epitaxially Grown MgB2 Thin Films and Superconducting Tunnel Junctions

Directory of Open Access Journals (Sweden)

Jean-Baptiste Laloë

2011-01-01

Full Text Available Since the discovery of its superconducting properties in 2001, magnesium diboride has generated terrific scientific and engineering research interest around the world. With a of 39 K and two superconducting gaps, MgB2 has great promise from the fundamental point of view, as well as immediate applications. Several techniques for thin film deposition and heterojunction formation have been established, each with its own advantages and drawbacks. Here, we will present a brief overview of research based on MgB2 thin films grown by molecular beam epitaxy coevaporation of Mg and B. The films are smooth and highly crystalline, and the technique allows for virtually any heterostructure to be formed, including all-MgB2 tunnel junctions. Such devices have been characterized, with both quasiparticle and Josephson tunneling reported. MgB2 remains a material of great potential for a multitude of further characterization and exploration research projects and applications.

Epitaxial growth of SrTiO3 (001) films on multilayer buffered GaN (0002) by pulsed laser deposition

International Nuclear Information System (INIS)

Luo, W B; Jing, J; Shuai, Y; Zhu, J; Zhang, W L; Zhou, S; Gemming, S; Du, N; Schmidt, H

2013-01-01

SrTiO 3 films were grown on CeO 2 /YSZ/TiO 2 multilayer buffered GaN/Al 2 O 3 (0001) substrates with and without the YBa 2 Cu 3 O 7-x (YBCO) bridge layer by pulsed laser deposition (PLD). The deposition process of the buffer layers was in situ monitored by reflection high-energy electron diffraction. The crystallographical orientation of the heterostructure was studied by x-ray diffraction (XRD). With the introduction of the YBCO (001) layer, the STO (001) film was epitaxially grown on the GaN substrate. There were three sets of inplane domains separated from each other by 30° in both STO and YBCO buffer layers. The epitaxial relationship was STO (002)[110]∥YBCO(001)[110]∥CeO 2 (002)[010]∥YSZ (002)[010]∥GaN(0001)[1 1 -2 0] according to XRD results. By comparing the orientation of STO grown on GaN with and without the YBCO top buffer layer, the surface chemical bonding was found to be a very important factor in determining the orientation relationship of STO.

Effect of growth temperature on the epitaxial growth of ZnO on GaN by ALD

Science.gov (United States)

Särkijärvi, Suvi; Sintonen, Sakari; Tuomisto, Filip; Bosund, Markus; Suihkonen, Sami; Lipsanen, Harri

2014-07-01

We report on the epitaxial growth of ZnO on GaN template by atomic layer deposition (ALD). Diethylzinc (DEZn) and water vapour (H2O) were used as precursors. The structure and the quality of the grown ZnO layers were studied with scanning electron microscope (SEM), X-ray diffraction (XRD), photoluminescence (PL) measurements and positron annihilation spectroscopy. The ZnO films were confirmed epitaxial, and the film quality was found to improve with increasing deposition temperature in the vicinity of the threshold temperature of two dimensional growth. We conclude that high quality ZnO thin films can be grown by ALD. Interestingly only separate Zn-vacancies were observed in the films, although ZnO thin films typically contain fairly high density of surface pits and vacancy clusters.

Mg doping of GaN by molecular beam epitaxy

International Nuclear Information System (INIS)

Lieten, R R; Buchowicz, G; Dubon, O; Motsnyi, V; Zhang, L; Cheng, K; Leys, M; Degroote, S; Borghs, G

2011-01-01

We present a systematic study on the influence of growth conditions on the incorporation and activation of Mg in GaN layers grown by plasma-assisted molecular beam epitaxy. We show that high quality p-type GaN layers can be obtained on GaN-on-silicon templates. The Mg incorporation and the electrical properties have been investigated as a function of growth temperature, Ga : N flux ratio and Mg : Ga flux ratio. It was found that the incorporation of Mg and the electrical properties are highly sensitive to the Ga : N flux ratio. The highest hole mobility and lowest resistivity were achieved for slightly Ga-rich conditions. In addition to an optimal Ga : N ratio, an optimum Mg : Ga flux ratio was also observed at around 1%. We observed a clear Mg flux window for p-type doping of GaN : 0.31% 17 cm -3 and a mobility of 15 cm 2 V -1 s -1 . Temperature-dependent Hall effect measurements indicate an acceptor depth in these samples of 100 meV for a hole concentration of 5.5 x 10 17 cm -3 . The corresponding Mg concentration is 5 x 10 19 cm -3 , indicating approximately 1% activation at room temperature. In addition to continuous growth of Mg-doped GaN layers we also investigated different modulated growth procedures. We show that a modulated growth procedure has only limited influence on Mg doping at a growth temperature of 800 deg. or higher. This result is thus in contrast to previously reported GaN : Mg doping at much lower growth temperatures of 500 deg. C.

Void Shapes Controlled by Using Interruption-Free Epitaxial Lateral Overgrowth of GaN Films on Patterned SiO2 AlN/Sapphire Template

Directory of Open Access Journals (Sweden)

Yu-An Chen

2014-01-01

Full Text Available GaN epitaxial layers with embedded air voids grown on patterned SiO2 AlN/sapphire templates were proposed. Using interruption-free epitaxial lateral overgrowth technology, we realized uninterrupted growth and controlled the shape of embedded air voids. These layers showed improved crystal quality using X-ray diffraction and measurement of etching pits density. Compared with conventional undoped-GaN film, the full width at half-maximum of the GaN (0 0 2 and (1 0 2 peaks decreased from 485 arcsec to 376 arcsec and from 600 arcsec to 322 arcsec, respectively. Transmission electron microscopy results showed that the coalesced GaN growth led to bending threading dislocation. We also proposed a growth model based on results of scanning electron microscopy.

Growth and coalescence control of inclined c-axis polar and semipolar GaN multilayer structures grown on Si(111), Si(112), and Si(115) by metalorganic vapor phase epitaxy

Energy Technology Data Exchange (ETDEWEB)

Szymański, Tomasz, E-mail: tomasz.szymanski@pwr.edu.pl; Wośko, Mateusz; Paszkiewicz, Bartłomiej; Paszkiewicz, Bogdan; Paszkiewicz, Regina [The Faculty of Microsystem Electronics and Photonics, Wroclaw University of Technology, Janiszewskiego 11/17, 50-372 Wroclaw (Poland); Sankowska, Iwona [The Institute of Electron Technology, Al. Lotnikow 32/46, 02-668 Warszawa (Poland)

2016-09-15

Herein, silicon substrates in alternative orientations from the commonly used Si(111) were used to enable the growth of polar and semipolar GaN-based structures by the metalorganic vapor phase epitaxy method. Specifically, Si(112) and Si(115) substrates were used for the epitaxial growth of nitride multilayer structures, while the same layer schemes were also deposited on Si(111) for comparison purposes. Multiple approaches were studied to examine the influence of the seed layers and the growth process conditions upon the final properties of the GaN/Si(11x) templates. Scanning electron microscope images were acquired to examine the topography of the deposited samples. It was observed that the substrate orientation and the process conditions allow control to produce an isolated GaN block growth or a coalesced layer growth, resulting in inclined c-axis GaN structures under various forms. The angles of the GaN c-axis inclination were determined by x-ray diffraction measurements and compared with the results obtained from the analysis of the atomic force microscope (AFM) images. The AFM image analysis method to determine the structure tilt was found to be a viable method to estimate the c-axis inclination angles of the isolated blocks and the not-fully coalesced layers. The quality of the grown samples was characterized by the photoluminescence method conducted at a wide range of temperatures from 77 to 297 K, and was correlated with the sample degree of coalescence. Using the free-excitation peak positions plotted as a function of temperature, analytical Bose-Einstein model parameters were fitted to obtain further information about the grown structures.

Ultralow threading dislocation density in GaN epilayer on near-strain-free GaN compliant buffer layer and its applications in hetero-epitaxial LEDs.

Science.gov (United States)

Shih, Huan-Yu; Shiojiri, Makoto; Chen, Ching-Hsiang; Yu, Sheng-Fu; Ko, Chung-Ting; Yang, Jer-Ren; Lin, Ray-Ming; Chen, Miin-Jang

2015-09-02

High threading dislocation (TD) density in GaN-based devices is a long unresolved problem because of the large lattice mismatch between GaN and the substrate, which causes a major obstacle for the further improvement of next-generation high-efficiency solid-state lighting and high-power electronics. Here, we report InGaN/GaN LEDs with ultralow TD density and improved efficiency on a sapphire substrate, on which a near strain-free GaN compliant buffer layer was grown by remote plasma atomic layer deposition. This "compliant" buffer layer is capable of relaxing strain due to the absorption of misfit dislocations in a region within ~10 nm from the interface, leading to a high-quality overlying GaN epilayer with an unusual TD density as low as 2.2 × 10(5) cm(-2). In addition, this GaN compliant buffer layer exhibits excellent uniformity up to a 6" wafer, revealing a promising means to realize large-area GaN hetero-epitaxy for efficient LEDs and high-power transistors.

Understanding the Growth Mechanism of GaN Epitaxial Layers on Mechanically Exfoliated Graphite.

Science.gov (United States)

Li, Tianbao; Liu, Chenyang; Zhang, Zhe; Yu, Bin; Dong, Hailiang; Jia, Wei; Jia, Zhigang; Yu, Chunyan; Gan, Lin; Xu, Bingshe; Jiang, Haiwei

2018-04-27

The growth mechanism of GaN epitaxial layers on mechanically exfoliated graphite is explained in detail based on classic nucleation theory. The number of defects on the graphite surface can be increased via O-plasma treatment, leading to increased nucleation density on the graphite surface. The addition of elemental Al can effectively improve the nucleation rate, which can promote the formation of dense nucleation layers and the lateral growth of GaN epitaxial layers. The surface morphologies of the nucleation layers, annealed layers and epitaxial layers were characterized by field-emission scanning electron microscopy, where the evolution of the surface morphology coincided with a 3D-to-2D growth mechanism. High-resolution transmission electron microscopy was used to characterize the microstructure of GaN. Fast Fourier transform diffraction patterns showed that cubic phase (zinc-blend structure) GaN grains were obtained using conventional GaN nucleation layers, while the hexagonal phase (wurtzite structure) GaN films were formed using AlGaN nucleation layers. Our work opens new avenues for using highly oriented pyrolytic graphite as a substrate to fabricate transferable optoelectronic devices.

Low-temperature ballistic transport in nanoscale epitaxial graphene cross junctions

OpenAIRE

Weingart, S.; Bock, C.; Kunze, U.; Speck, F.; Seyller, Th.; Ley, L.

2009-01-01

We report on the observation of inertial-ballistic transport in nanoscale cross junctions fabricated from epitaxial graphene grown on SiC(0001). Ballistic transport is indicated by a negative bend resistance of R12,43 ~ 170 ohm which is measured in a non-local, four-terminal configuration at 4.2 K and which vanishes as the temperature is increased above 80 K.

Broadband nanophotonic waveguides and resonators based on epitaxial GaN thin films

Energy Technology Data Exchange (ETDEWEB)

Bruch, Alexander W.; Xiong, Chi; Leung, Benjamin; Poot, Menno; Han, Jung; Tang, Hong X., E-mail: hong.tang@yale.edu [Department of Electrical Engineering, Yale University, New Haven, Connecticut 06511 (United States)

2015-10-05

We demonstrate broadband, low loss optical waveguiding in single crystalline GaN grown epitaxially on c-plane sapphire wafers through a buffered metal-organic chemical vapor phase deposition process. High Q optical microring resonators are realized in near infrared, infrared, and near visible regimes with intrinsic quality factors exceeding 50 000 at all the wavelengths we studied. TEM analysis of etched waveguide reveals growth and etch-induced defects. Reduction of these defects through improved material and device processing could lead to even lower optical losses and enable a wideband photonic platform based on GaN-on-sapphire material system.

Electronic structure analysis of GaN films grown on r- and a-plane sapphire

Energy Technology Data Exchange (ETDEWEB)

Mishra, Monu; Krishna TC, Shibin; Aggarwal, Neha [Physics of Energy Harvesting Division, CSIR-National Physical Laboratory (CSIR-NPL), Dr. K.S. Krishnan Marg, New Delhi 110012 (India); Academy of Scientific and Innovative Research (AcSIR), CSIR-NPL Campus, Dr. K.S. Krishnan Marg, New Delhi 110012 (India); Vihari, Saket [Physics of Energy Harvesting Division, CSIR-National Physical Laboratory (CSIR-NPL), Dr. K.S. Krishnan Marg, New Delhi 110012 (India); Gupta, Govind, E-mail: govind@nplindia.org [Physics of Energy Harvesting Division, CSIR-National Physical Laboratory (CSIR-NPL), Dr. K.S. Krishnan Marg, New Delhi 110012 (India); Academy of Scientific and Innovative Research (AcSIR), CSIR-NPL Campus, Dr. K.S. Krishnan Marg, New Delhi 110012 (India)

2015-10-05

Graphical abstract: Substrate orientation induced changes in surface chemistry, band bending, hybridization states, electronic properties and surface morphology of epitaxially grown GaN were investigated via photoemission spectroscopic and Atomic Force Microscopic measurements. - Highlights: • Electronic structure and surface properties of GaN film grown on r/a-plane sapphire. • Downward band bending (0.5 eV) and high surface oxide is observed for GaN/a-sapphire. • Electron affinity and ionization energy is found to be higher for GaN/a-sapphire. - Abstract: The electronic structure and surface properties of epitaxial GaN films grown on r- and a-plane sapphire substrates were probed via spectroscopic and microscopic measurements. X-ray photoemission spectroscopic (XPS) measurements were performed to analyse the surface chemistry, band bending and valence band hybridization states. It was observed that GaN/a-sapphire display a downward band bending of 0.5 eV and possess higher amount of surface oxide compared to GaN/r-sapphire. The valence band (VB) investigation revealed that the hybridization corresponds to the interactions of Ga 4s and Ga 4p orbitals with N 2p orbital, and result in N2p–Ga4p, N2p–Ga4s{sup ∗}, mixed and N2p–Ga4s states. The energy band structure and electronic properties were measured via ultraviolet photoemission spectroscopic (UPS) experiments. The band structure analysis and electronic properties calculations divulged that the electron affinity and ionization energy of GaN/a-sapphire were 0.3 eV higher than GaN/r-sapphire film. Atomic Force Microscopic (AFM) measurements revealed faceted morphology of GaN/r-sapphire while a smooth pitted surface was observed for GaN/a-sapphire film, which is closely related to surface oxide coverage.

Impact of substrate temperature on the incorporation of carbon-related defects and mechanism for semi-insulating behavior in GaN grown by molecular beam epitaxy

International Nuclear Information System (INIS)

Armstrong, A.; Poblenz, C.; Green, D.S.; Mishra, U.K.; Speck, J.S.; Ringel, S.A.

2006-01-01

The electrical conductivity and deep level spectrum of GaN grown by molecular beam epitaxy and codoped with carbon and silicon were investigated for substrate temperatures T s of 650 and 720 deg. C as a function relative carbon and silicon doping levels. With sufficiently high carbon doping, semi-insulating behavior was observed for films grown at both temperatures, and growth at T s =720 deg. C enhanced the carbon compensation ratio. Similar carbon-related band gap states were observed via deep level optical spectroscopy for films grown at both substrate temperatures. Due to the semi-insulating nature of the films, a lighted capacitance-voltage technique was required to determine individual deep level concentrations. Carbon-related band gap states underwent substantial redistribution between deep level and shallow acceptor configurations with change in T s . In light of a T s dependence for the preferential site of carbon incorporation, a model of semi-insulating behavior in terms of carbon impurity state incorporation mediated by substrate temperature is proposed

Influence of V/III growth flux ratio on trap states in m-plane GaN grown by ammonia-based molecular beam epitaxy

International Nuclear Information System (INIS)

Zhang, Z.; Arehart, A. R.; Hurni, C. A.; Speck, J. S.; Ringel, S. A.

2012-01-01

Deep level transient spectroscopy (DLTS) and deep level optical spectroscopy (DLOS) were utilized to investigate the behavior of deep states in m-plane, n-type GaN grown by ammonia-based molecular beam epitaxy (NH 3 -MBE) as a function of systematically varied V/III growth flux ratios. Levels were detected at E C - 0.14 eV, E C - 0.21 eV, E C - 0.26 eV, E C - 0.62 eV, E C - 0.67 eV, E C - 2.65 eV, and E C - 3.31 eV, with the concentrations of several traps exhibiting systematic dependencies on V/III ratio. The DLTS spectra are dominated by traps at E C - 0.14 eV and E C - 0.67 eV, whose concentrations decreased monotonically with increasing V/III ratio and decreasing oxygen impurity concentration, and by a trap at E C - 0.21 eV that revealed no dependence of its concentration on growth conditions, suggestive of different physical origins. Higher concentrations of deeper trap states detected by DLOS with activation energies of E C - 2.65 eV and E C - 3.31 eV in each sample did not display measureable sensitivity to the intentionally varied V/III ratio, necessitating further study on reducing these deep traps through growth optimization for maximizing material quality of NH 3 -MBE grown m-plane GaN.

Comparison of stress states in GaN films grown on different substrates: Langasite, sapphire and silicon

Science.gov (United States)

Park, Byung-Guon; Saravana Kumar, R.; Moon, Mee-Lim; Kim, Moon-Deock; Kang, Tae-Won; Yang, Woo-Chul; Kim, Song-Gang

2015-09-01

We demonstrate the evolution of GaN films on novel langasite (LGS) substrate by plasma-assisted molecular beam epitaxy, and assessed the quality of grown GaN film by comparing the experimental results obtained using LGS, sapphire and silicon (Si) substrates. To study the substrate effect, X-ray diffraction (XRD), scanning electron microscopy (SEM), Raman spectroscopy and photoluminescence (PL) spectra were used to characterize the microstructure and stress states in GaN films. Wet etching of GaN films in KOH solution revealed that the films deposited on GaN/LGS, AlN/sapphire and AlN/Si substrates possess Ga-polarity, while the film deposited on GaN/sapphire possess N-polarity. XRD, Raman and PL analysis demonstrated that a compressive stress exist in the films grown on GaN/LGS, AlN/sapphire, and GaN/sapphire substrates, while a tensile stress appears on AlN/Si substrate. Comparative analysis showed the growth of nearly stress-free GaN films on LGS substrate due to the very small lattice mismatch ( 3.2%) and thermal expansion coefficient difference ( 7.5%). The results presented here will hopefully provide a new framework for the further development of high performance III-nitride-related devices using GaN/LGS heteroepitaxy.

Strain and crystalline defects in epitaxial GaN layers studied by high-resolution X-ray diffraction

Energy Technology Data Exchange (ETDEWEB)

Chierchia, Rosa

2007-07-01

This thesis treats strain and dislocations in MOVPE GaN layers. The mosaic structure of metalorganic vapour phase epitaxy (MOVPE)-grown GaN layers was studied in dependence on the grain diameter utilizing high-resolution XRD. Different models for the defect structure were analyzed, the edge type TD densities were calculated under the assumption that the dislocations are not randomly distributed but localized at the grain boundaries. Moreover, in situ measurements have shown that the layers are under tension in the c-plane when a nucleation layer is used. The second part of this thesis treats a particular approach to reduce dislocations in MOVPE GaN layers, i.e. maskless pendeo epitaxial growth of MOVPE GAN layers. FE simulations assuming the strain to be completely induced during cooling of the structures after growth agree only partly with experimental data. The strain state of single layers and stripes of GaN grown on SiC was studied to exploit the evolution of the strain in the different phases of the PE growth. The biaxial compressive stress, due to the lattice mismatch between the GaN layer and the AlN nucleation layer is plastically relieved before overgrowth. Temperature dependent measurements show a linear reduction of the wing tilt with increasing temperature varying from sample to sample. Bent TDs have been observed in TEM images of maskless PE samples. Stress induced from the mismatch between the AlN buffer layer and the GaN also contributes to the remaining part of the wing tilt not relieved thermally. It has to be noted that the rest tilt value varies from sample to sample at the growth temperature. In fact some of the data indicate that the wing tilt decreases with increasing V/III ratio. In the last Chapter the application of X-ray techniques for the analysis of strain and composition in layers of inhomogeneous composition is explored. In the first part of the Chapter the strain state and the Al content of AlGaN buffer layers grown directly on (0001

Stress evolution of GaN/AlN heterostructure grown on 6H-SiC substrate by plasma assisted molecular beam epitaxy

Science.gov (United States)

Agrawal, M.; Ravikiran, L.; Dharmarasu, N.; Radhakrishnan, K.; Karthikeyan, G. S.; Zheng, Y.

2017-01-01

The stress evolution of GaN/AlN heterostructure grown on 6H-SiC substrate by plasma assisted molecular beam epitaxy (PA-MBE) has been studied. AlN nucleation layer and GaN layer were grown as a function of III/V ratio. GaN/AlN structure is found to form buried cracks when AlN is grown in the intermediate growth regime(III/V˜1)and GaN is grown under N-rich growth regime (III/VHEMT) heterostructure was demonstrated on 2-inch SiC that showed good two dimensional electron gas (2DEG) properties with a sheet resistance of 480 Ω/sq, mobility of 1280 cm2/V.s and sheet carrier density of 1×1013 cm-2.

GaN nanorods and LED structures grown on patterned Si and AlN/Si substrates by selective area growth

Energy Technology Data Exchange (ETDEWEB)

Li, Shunfeng; Fuendling, Soenke; Soekmen, Uensal; Neumann, Richard; Merzsch, Stephan; Peiner, Erwin; Wehmann, Hergo-Heinrich; Waag, Andreas [Institut fuer Halbleitertechnik, TU Braunschweig (Germany); Hinze, Peter; Weimann, Thomas [Physikalisch-Technische Bundesanstalt (PTB), Braunschweig (Germany); Jahn, Uwe; Trampert, Achim; Riechert, Henning [Paul-Drude-Institut fuer Festkoerperelektronik, Berlin (Germany)

2010-07-15

GaN nanorods (NRs) show promising applications in high-efficiency light emitting diodes, monolithic white light emission and optical interconnection due to their superior properties. In this work, we performed GaN nanostructures growth by pre-patterning the Si and AlN/Si substrates. The pattern was transferred to Si and AlN/Si substrates by photolithography and inductively-coupled plasma etching. GaN NRs were grown on these templates by metal-organic vapour phase epitaxy (MOVPE). GaN grown on Si pillar templates show a truncated pyramidal structure. Transmission electron microscopy measurements demonstrated clearly that the threading dislocations bend to the side facets of the GaN nanostructures and terminate. GaN growth can also be observed on the sidewalls and bottom surface between the Si pillars. A simple phenomenological model is proposed to explain the GaN nanostructure growth on Si pillar templates. Based on this model, we developed another growth method, by which we grow GaN rod structures on pre-patterned AlN/Si templates. By in-situ nitridation and decreasing of the V/III ratio, we found that GaN rods only grew on the patterned AlN/Si dots with an aspect ratio of about 1.5 - 2. (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

High-Temperature Growth of GaN and Al x Ga1- x N via Ammonia-Based Metalorganic Molecular-Beam Epitaxy

Science.gov (United States)

Billingsley, Daniel; Henderson, Walter; Doolittle, W. Alan

2010-05-01

The effect of high-temperature growth on the crystalline quality and surface morphology of GaN and Al x Ga1- x N grown by ammonia-based metalorganic molecular-beam epitaxy (NH3-MOMBE) has been investigated as a means of producing atomically smooth films suitable for device structures. The effects of V/III ratio on the growth rate and surface morphology are described herein. The crystalline quality of both GaN and AlGaN was found to mimic that of the GaN templates, with (002) x-ray diffraction (XRD) full-widths at half- maximum (FWHMs) of ~350 arcsec. Nitrogen-rich growth conditions have been found to provide optimal surface morphologies with a root-mean-square (RMS) roughness of ~0.8 nm, yet excessive N-rich environments have been found to reduce the growth rate and result in the formation of faceted surface pitting. AlGaN exhibits a decreased growth rate, as compared with GaN, due to increased N recombination as a result of the increased pyrolysis of NH3 in the presence of Al. AlGaN films grown directly on GaN templates exhibited Pendellösung x-ray fringes, indicating an abrupt interface and a planar AlGaN film. AlGaN films grown for this study resulted in an optimal RMS roughness of ~0.85 nm with visible atomic steps.

GaN Bulk Growth and Epitaxy from Ca-Ga-N Solutions, Phase I

Data.gov (United States)

National Aeronautics and Space Administration — This SBIR proposal addresses the liquid phase epitaxy (LPE) of gallium nitride (GaN) films using nitrogen-enriched metal solutions. Growth of GaN from solutions...

Dependence of the Mg-related acceptor ionization energy with the acceptor concentration in p-type GaN layers grown by molecular beam epitaxy

International Nuclear Information System (INIS)

Brochen, Stéphane; Brault, Julien; Chenot, Sébastien; Dussaigne, Amélie; Leroux, Mathieu; Damilano, Benjamin

2013-01-01

Hall effect and capacitance-voltage C(V) measurements were performed on p-type GaN:Mg layers grown on GaN templates by molecular beam epitaxy with a high range of Mg-doping concentrations. The free hole density and the effective dopant concentration N A −N D as a function of magnesium incorporation measured by secondary ion mass spectroscopy clearly reveal both a magnesium doping efficiency up to 90% and a strong dependence of the acceptor ionization energy Ea with the acceptor concentration N A . These experimental observations highlight an isolated acceptor binding energy of 245±25 meV compatible, at high acceptor concentration, with the achievement of p-type GaN:Mg layers with a hole concentration at room temperature close to 10 19 cm −3

Investigation of AlN films grown by molecular beam epitaxy on vicinal Si(111) as templates for GaN quantum dots

International Nuclear Information System (INIS)

Benaissa, M.; Vennegues, P.; Tottereau, O.; Nguyen, L.; Semond, F.

2006-01-01

The use of AlN epitaxial films deposited on vicinal Si(111) as templates for the growth of GaN quantum dots is investigated by transmission electron microscopy and atomic force microscopy. It is found that the substrate vicinality induces both a slight tilt of the AlN (0001) direction with respect to the [111] direction and a step bunching mechanism. As a consequence, a dislocation dragging behavior is observed giving rise to dislocation-free areas well suited for the nucleation of GaN quantum dots

Lattice-Symmetry-Driven Epitaxy of Hierarchical GaN Nanotripods

KAUST Repository

Wang, Ping; Wang, Xinqiang; Wang, Tao; Tan, Chih Shan; Sheng, Bowen; Sun, Xiaoxiao; Li, Mo; Rong, Xin; Zheng, Xiantong; Chen, Zhaoying; Yang, Xuelin; Xu, Fujun; Qin, Zhixin; Zhang, Jian; Zhang, Xixiang; Shen, Bo

2017-01-01

-resolution transmission electron microscopy confirms that two kinds of lattice-symmetry, wurtzite (wz) and zinc-blende (zb), coexist in the GaN nanotripods. Periodical transformation between wz and zb drives the epitaxy of the hierarchical nanotripods with N

Polarization-enhanced InGaN/GaN-based hybrid tunnel junction contacts to GaN p-n diodes and InGaN LEDs

Science.gov (United States)

Mughal, Asad J.; Young, Erin C.; Alhassan, Abdullah I.; Back, Joonho; Nakamura, Shuji; Speck, James S.; DenBaars, Steven P.

2017-12-01

Improved turn-on voltages and reduced series resistances were realized by depositing highly Si-doped n-type GaN using molecular beam epitaxy on polarization-enhanced p-type InGaN contact layers grown using metal-organic chemical vapor deposition. We compared the effects of different Si doping concentrations and the addition of p-type InGaN on the forward voltages of p-n diodes and light-emitting diodes, and found that increasing the Si concentrations from 1.9 × 1020 to 4.6 × 1020 cm-3 and including a highly doped p-type InGaN at the junction both contributed to reductions in the depletion width, the series resistance of 4.2 × 10-3-3.4 × 10-3 Ω·cm2, and the turn-on voltages of the diodes.

Polarization-enhanced InGaN/GaN-based hybrid tunnel junction contacts to GaN p–n diodes and InGaN LEDs

KAUST Repository

Mughal, Asad J.

2017-11-27

Improved turn-on voltages and reduced series resistances were realized by depositing highly Si-doped n-type GaN using molecular beam epitaxy on polarization-enhanced p-type InGaN contact layers grown using metal–organic chemical vapor deposition. We compared the effects of different Si doping concentrations and the addition of p-type InGaN on the forward voltages of p–n diodes and light-emitting diodes, and found that increasing the Si concentrations from 1.9 × 1020 to 4.6 × 1020 cm−3 and including a highly doped p-type InGaN at the junction both contributed to reductions in the depletion width, the series resistance of 4.2 × 10−3–3.4 × 10−3 Ωcenterdotcm2, and the turn-on voltages of the diodes.

Polarization-enhanced InGaN/GaN-based hybrid tunnel junction contacts to GaN p–n diodes and InGaN LEDs

KAUST Repository

Mughal, Asad J.; Young, Erin C.; Alhassan, Abdullah I.; Back, Joonho; Nakamura, Shuji; Speck, James S.; DenBaars, Steven P.

2017-01-01

Improved turn-on voltages and reduced series resistances were realized by depositing highly Si-doped n-type GaN using molecular beam epitaxy on polarization-enhanced p-type InGaN contact layers grown using metal–organic chemical vapor deposition. We compared the effects of different Si doping concentrations and the addition of p-type InGaN on the forward voltages of p–n diodes and light-emitting diodes, and found that increasing the Si concentrations from 1.9 × 1020 to 4.6 × 1020 cm−3 and including a highly doped p-type InGaN at the junction both contributed to reductions in the depletion width, the series resistance of 4.2 × 10−3–3.4 × 10−3 Ωcenterdotcm2, and the turn-on voltages of the diodes.

Luminescence and Morphological Properties of GaN Layers Grown on SiC/Si(111) Substrates

Energy Technology Data Exchange (ETDEWEB)

Sanchez-Garcia, M.A.; Ristic, J.; Calleja, E. [ISOM and Dpto. Ing. Electronica, ETSI Telecomunicacion, Univ. Politecnica de Madrid, Ciudad Universitaria s/n, 28040 Madrid (Spain); Perez-Rodriguez, A.; Serre, C.; Romano-Rodriguez, A.; Morante, J.R. [EME - Electronic Materials and Engineering, Department of Electronics, Universidad de Barcelona, Marti i Franques 1, 08028 Barcelona (Spain); Koegler, R.; Skorupa, W. [Institute of Ion Beam Physics and Materials Research, Forschungszentrum Rossendorf e.V., 01314 Dresden (Germany); Trampert, A.; Ploog, K.H. [Paul-Drude-Institut fuer Festkoerperelektronik, Hausvogteiplatz 5-7, 10117 Berlin (Germany)

2002-08-16

This article describes the fabrication of SiC thin films on top of Si(111) substrates by means of a multiple C-ion implantation and the subsequent growth by plasma-assisted molecular beam epitaxy of GaN layers. The stoichiometry of the top SiC layer is controlled by reactive ion etching. Photoluminescence spectra reveal that all GaN layers are under biaxial tensile strain of thermal origin. The photoluminescence efficiency clearly depends on the stoichiometry of the initial SiC layer and on whether AlN buffer layers are used or not. GaN layers grown directly on bare non-stoichiometric SiC layers exhibit the best photoluminescence efficiency but also a high degree of mosaicity, as measured by X-ray diffraction techniques. The nucleation process involved in the initial stages of the growth leads to the formation of large dislocation-free grains with a high PL efficiency and with a higher tensile strain character. Despite the lack of a perfect monocrystalline SiC substrate lattice, high quality GaN microcrystals are obtained. (Abstract Copyright[2002], Wiley Periodicals, Inc.)

Effects of Mg/Ga and V/III source ratios on hole concentration of N-polar (000\\bar{1}) p-type GaN grown by metalorganic vapor phase epitaxy

Science.gov (United States)

Nonoda, Ryohei; Shojiki, Kanako; Tanikawa, Tomoyuki; Kuboya, Shigeyuki; Katayama, Ryuji; Matsuoka, Takashi

2016-05-01

The effects of growth conditions such as Mg/Ga and V/III ratios on the properties of N-polar (000\\bar{1}) p-type GaN grown by metalorganic vapor phase epitaxy were studied. Photoluminescence spectra from Mg-doped GaN depended on Mg/Ga and V/III ratios. For the lightly doped samples, the band-to-acceptor emission was observed at 3.3 eV and its relative intensity decreased with increasing V/III ratio. For the heavily doped samples, the donor-acceptor pair emission was observed at 2.8 eV and its peak intensity monotonically decreased with V/III ratio. The hole concentration was maximum for the Mg/Ga ratio. This is the same tendency as in group-III polar (0001) growth. The V/III ratio also reduced the hole concentration. The higher V/III ratio reduced the concentration of residual donors such as oxygen by substituting nitrogen atoms. The surface became rougher with increasing V/III ratio and the hillock density increased.

Polarity analysis of GaN nanorods by photo-assisted Kelvin probe force microscopy

Energy Technology Data Exchange (ETDEWEB)

Wei, Jiandong; Neumann, Richard; Wang, Xue; Li, Shunfeng; Fuendling, Soenke; Merzsch, Stephan; Al-Suleiman, Mohamed A.M.; Soekmen, Uensal; Wehmann, Hergo-H.; Waag, Andreas [Institut fuer Halbleitertechnik, TU Braunschweig (Germany)

2011-07-15

Polarity dependence (N-polar (000-1) and Ga-polar (0001)) of surface photovoltage of epitaxially grown, vertically aligned GaN nanorods has been investigated by photo-assisted Kelvin probe force microscopy (KPFM). Commercial GaN substrates with known polarities are taken as reference samples. The polarity of GaN substrates can be well distinguished by the change in surface photovoltage upon UV illumination in air ambient. These different behaviors of Ga- and N-polar surfaces are attributed to the polarity-related surface-bound charges and photochemical reactivity. GaN nanorods were grown on patterned SiO{sub 2}/sapphire templates by metal-organic vapor phase epitaxy (MOVPE). In order to analyze the bottom surface of the grown GaN nanorods, a technique known from high power electronics and joining techniques is applied to remove the substrate. The top and bottom surfaces of the GaN nanorods are identified to be N-polar and Ga-polar according to the KPFM results, respectively. Our experiments demonstrate that KPFM is a simple and suitable method capable to identify the polarity of GaN nanorods. (copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Epitaxial GaN films by hyperthermal ion-beam nitridation of Ga droplets

Energy Technology Data Exchange (ETDEWEB)

Gerlach, J. W.; Ivanov, T.; Neumann, L.; Hoeche, Th.; Hirsch, D.; Rauschenbach, B. [Leibniz-Institut fuer Oberflaechenmodifizierung (IOM), D-04318 Leipzig (Germany)

2012-06-01

Epitaxial GaN film formation on bare 6H-SiC(0001) substrates via the process of transformation of Ga droplets into a thin GaN film by applying hyperthermal nitrogen ions is investigated. Pre-deposited Ga atoms in well defined amounts form large droplets on the substrate surface which are subsequently nitridated at a substrate temperature of 630 Degree-Sign C by a low-energy nitrogen ion beam from a constricted glow-discharge ion source. The Ga deposition and ion-beam nitridation process steps are monitored in situ by reflection high-energy electron diffraction. Ex situ characterization by x-ray diffraction and reflectivity techniques, Rutherford backscattering spectrometry, and electron microscopy shows that the thickness of the resulting GaN films depends on the various amounts of pre-deposited gallium. The films are epitaxial to the substrate, exhibit a mosaic like, smooth surface topography and consist of coalesced large domains of low defect density. Possible transport mechanisms of reactive nitrogen species during hyperthermal nitridation are discussed and the formation of GaN films by an ion-beam assisted process is explained.

Photoluminescence studies of cubic phase GaN grown by molecular beam epitaxy on (001) silicon covered with SiC layer

International Nuclear Information System (INIS)

Godlewski, M.; Ivanov, V.Yu.; Bergman, J.P.; Monemar, B.; Barski, A.; Langer, R.

1997-01-01

In this work we evaluate optical properties of cubic phase GaN epilayers grown on top of (001) silicon substrate prepared by new process. Prior to the growth Si substrate was annealed at 1300-1400 o C in propane. The so-prepared substrate is covered within a thin (∼ 4 nm) SiC wafer, which allowed a successful growth of good morphological quality cubic phase GaN epilayers. The present results confirm recent suggestion on smaller ionization energies of acceptors in cubic phase GaN epilayers. (author)

Epitaxial NbN/AlN/NbN tunnel junctions on Si substrates with TiN buffer layers

Directory of Open Access Journals (Sweden)

Rui Sun

2016-06-01

Full Text Available We have developed epitaxial NbN/AlN/NbN tunnel junctions on Si (100 substrates with a TiN buffer layer. A 50-nm-thick (200-oriented TiN thin film was introduced as the buffer layer for epitaxial growth of NbN/AlN/NbN trilayers on Si substrates. The fabricated NbN/AlN/NbN junctions demonstrated excellent tunneling properties with a high gap voltage of 5.5 mV, a large IcRN product of 3.8 mV, a sharp quasiparticle current rise with a ΔVg of 0.4 mV, and a small subgap leakage current. The junction quality factor Rsg/RN was about 23 for the junction with a Jc of 47 A/cm2 and was about 6 for the junction with a Jc of 3.0 kA/cm2. X-ray diffraction and transmission electron microscopy observations showed that the NbN/AlN/NbN trilayers were grown epitaxially on the (200-orientated TiN buffer layer and had a highly crystalline structure with the (200 orientation.

Epitaxial NbN/AlN/NbN tunnel junctions on Si substrates with TiN buffer layers

Energy Technology Data Exchange (ETDEWEB)

Sun, Rui [State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Microsystem and Information Technology (SIMIT), Chinese Academy of Sciences (CAS), Shanghai 200050 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Makise, Kazumasa; Terai, Hirotaka [Advanced ICT Research Institute, National Institute of Information and Communications Technology (Japan); Zhang, Lu [State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Microsystem and Information Technology (SIMIT), Chinese Academy of Sciences (CAS), Shanghai 200050 (China); Wang, Zhen, E-mail: zwang@mail.sim.ac.cn [State Key Laboratory of Functional Materials for Informatics, Shanghai Institute of Microsystem and Information Technology (SIMIT), Chinese Academy of Sciences (CAS), Shanghai 200050 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Shanghai Tech University, Shanghai 201210 (China)

2016-06-15

We have developed epitaxial NbN/AlN/NbN tunnel junctions on Si (100) substrates with a TiN buffer layer. A 50-nm-thick (200)-oriented TiN thin film was introduced as the buffer layer for epitaxial growth of NbN/AlN/NbN trilayers on Si substrates. The fabricated NbN/AlN/NbN junctions demonstrated excellent tunneling properties with a high gap voltage of 5.5 mV, a large I{sub c}R{sub N} product of 3.8 mV, a sharp quasiparticle current rise with a ΔV{sub g} of 0.4 mV, and a small subgap leakage current. The junction quality factor R{sub sg}/R{sub N} was about 23 for the junction with a J{sub c} of 47 A/cm{sup 2} and was about 6 for the junction with a J{sub c} of 3.0 kA/cm{sup 2}. X-ray diffraction and transmission electron microscopy observations showed that the NbN/AlN/NbN trilayers were grown epitaxially on the (200)-orientated TiN buffer layer and had a highly crystalline structure with the (200) orientation.

Epitaxial Single-Layer MoS2 on GaN with Enhanced Valley Helicity

KAUST Repository

Wan, Yi

2017-12-19

Engineering the substrate of 2D transition metal dichalcogenides can couple the quasiparticle interaction between the 2D material and substrate, providing an additional route to realize conceptual quantum phenomena and novel device functionalities, such as realization of a 12-time increased valley spitting in single-layer WSe2 through the interfacial magnetic exchange field from a ferromagnetic EuS substrate, and band-to-band tunnel field-effect transistors with a subthreshold swing below 60 mV dec−1 at room temperature based on bilayer n-MoS2 and heavily doped p-germanium, etc. Here, it is demonstrated that epitaxially grown single-layer MoS2 on a lattice-matched GaN substrate, possessing a type-I band alignment, exhibits strong substrate-induced interactions. The phonons in GaN quickly dissipate the energy of photogenerated carriers through electron–phonon interaction, resulting in a short exciton lifetime in the MoS2/GaN heterostructure. This interaction enables an enhanced valley helicity at room temperature (0.33 ± 0.05) observed in both steady-state and time-resolved circularly polarized photoluminescence measurements. The findings highlight the importance of substrate engineering for modulating the intrinsic valley carriers in ultrathin 2D materials and potentially open new paths for valleytronics and valley-optoelectronic device applications.

Epitaxial Single-Layer MoS2 on GaN with Enhanced Valley Helicity

KAUST Repository

Wan, Yi; Xiao, Jun; Li, Jingzhen; Fang, Xin; Zhang, Kun; Fu, Lei; Li, Pan; Song, Zhigang; Zhang, Hui; Wang, Yilun; Zhao, Mervin; Lu, Jing; Tang, Ning; Ran, Guangzhao; Zhang, Xiang; Ye, Yu; Dai, Lun

2017-01-01

Engineering the substrate of 2D transition metal dichalcogenides can couple the quasiparticle interaction between the 2D material and substrate, providing an additional route to realize conceptual quantum phenomena and novel device functionalities, such as realization of a 12-time increased valley spitting in single-layer WSe2 through the interfacial magnetic exchange field from a ferromagnetic EuS substrate, and band-to-band tunnel field-effect transistors with a subthreshold swing below 60 mV dec−1 at room temperature based on bilayer n-MoS2 and heavily doped p-germanium, etc. Here, it is demonstrated that epitaxially grown single-layer MoS2 on a lattice-matched GaN substrate, possessing a type-I band alignment, exhibits strong substrate-induced interactions. The phonons in GaN quickly dissipate the energy of photogenerated carriers through electron–phonon interaction, resulting in a short exciton lifetime in the MoS2/GaN heterostructure. This interaction enables an enhanced valley helicity at room temperature (0.33 ± 0.05) observed in both steady-state and time-resolved circularly polarized photoluminescence measurements. The findings highlight the importance of substrate engineering for modulating the intrinsic valley carriers in ultrathin 2D materials and potentially open new paths for valleytronics and valley-optoelectronic device applications.

Fabrication of GaN with buried tungsten (W) structures using epitaxial lateral overgrowth (ELO) via LP-MOVPE

International Nuclear Information System (INIS)

Miyake, Hideto; Yamaguchi, Motoo; Haino, Masahiro

2000-01-01

A buried tungsten (W) mask structure with GaN is successfully obtained by epitaxial lateral overgrowth (ELO) technique via low-pressure metalorganic vapor phase epitaxy (LP-MOVPE). The selectivity of GaN growth on the window region vs. the mask region is good. An underlying GaN with a striped W metal mask is easily decomposed above 500 C by the W catalytic effect, by which radical hydrogen is reacted with GaN. It is difficult to bury the W mask because severe damage occurs in the GaN epilayer under the mask. It is found that an underlying AlGaN/GaN layer with a narrow W stripe mask width (mask/window - 2/2 microm) leads the ELO GaN layer to be free from damage, resulting in an excellent W-buried structure

Influence of in-situ deposited SiNx interlayer on crystal quality of GaN epitaxial films

Science.gov (United States)

Fan, Teng; Jia, Wei; Tong, Guangyun; Zhai, Guangmei; Li, Tianbao; Dong, Hailiang; Xu, Bingshe

2018-05-01

GaN epitaxial films with SiNx interlayers were prepared by metal organic chemical vapor deposition (MOCVD) on c-plane sapphire substrates. The influences of deposition times and locations of SiNx interlayers on crystal quality of GaN epitaxial films were studied. Under the optimal growth time of 120 s for the SiNx interlayer, the dislocation density of GaN film is reduced to 4.05 × 108 cm-2 proved by high resolution X-ray diffraction results. It is found that when the SiNx interlayer deposits on the GaN nucleation islands, the subsequent GaN film has the lowest dislocation density of only 2.89 × 108 cm-2. Moreover, a model is proposed to illustrate the morphological evolution and associated propagation processes of TDs in GaN epi-layers with SiNx interlayers for different deposition times and locations.

Epitaxial Gd2O3 on GaN and AlGaN: a potential candidate for metal oxide semiconductor based transistors on Si for high power application

Science.gov (United States)

Ghosh, Kankat; Das, S.; Khiangte, K. R.; Choudhury, N.; Laha, Apurba

2017-11-01

We report structural and electrical properties of hexagonal Gd2O3 grown epitaxially on GaN/Si (1 1 1) and AlGaN/GaN/Si(1 1 1) virtual substrates. GaN and AlGaN/GaN heterostructures were grown on Si(1 1 1) substrates by plasma assisted molecular beam epitaxy (PA-MBE), whereas the Gd2O3 layer was grown by the pulsed laser ablation (PLA) technique. Initial structural characterizations show that Gd2O3 grown on III-nitride layers by PLA, exhibit a hexagonal structure with an epitaxial relationship as {{≤ft[ 0 0 0 1 \\right]}G{{d2}{{O}3}}}||{{≤ft[ 0 0 0 1 \\right]}GaN} and {{≤ft[ 1 \\bar{1} 0 0 \\right]}G{{d2}{{O}3}}}||{{≤ft[ 1 \\bar{1} 0 0 \\right]}GaN} . X-ray photoelectron measurements of the valence bands revealed that Gd2O3 exhibits band offsets of 0.97 eV and 0.4 eV, for GaN and Al0.3Ga0.7N, respectively. Electrical measurements such as capacitance-voltage and leakage current characteristics further confirm that epi-Gd2O3 on III-nitrides could be a potential candidate for future metal-oxide-semiconductor (MOS)-based transistors also for high power applications in radio frequency range.

Growth and structural investigations of epitaxial hexagonal YMnO3 thin films deposited on wurtzite GaN(001) substrates

International Nuclear Information System (INIS)

Balasubramanian, K.R.; Chang, Kai-Chieh; Mohammad, Feroz A.; Porter, Lisa M.; Salvador, Paul A.; DiMaio, Jeffrey; Davis, Robert F.

2006-01-01

Epitaxial hexagonal YMnO 3 (h-YMnO 3 ) films having sharp (00l) X-ray diffraction peaks were grown above 700 deg. C in 5 mTorr O 2 via pulsed laser deposition both on as-received wurtzite GaN/AlN/6H-SiC(001) (w-GaN) substrates as well as on w-GaN surfaces that were etched in 50% HF solution. High-resolution transmission electron microscopy revealed an interfacial layer between film and the unetched substrate; this layer was absent in those samples wherein an etched substrate was used. However, the substrate treatment did not affect the epitaxial arrangement between the h-YMnO 3 film and w-GaN substrate. The epitaxial relationships of the h-YMnO 3 films with the w-GaN(001) substrate was determined via X-ray diffraction to be (001) YMnO 3 -parallel (001) GaN : [11-bar0] YMnO 3 -parallel [110] GaN ; in other words, the basal planes of the film and the substrate are aligned parallel to one another, as are the most densely packed directions in planes of the film and the substrate. Interestingly, this arrangement has a larger lattice mismatch than if the principal axes of the unit cells were aligned

Development of Epitaxial GaN Films for RF Communications, Phase I

Data.gov (United States)

National Aeronautics and Space Administration — The primary objective of this SBIR is to develop epitaxial GaN films with threading dislocation density less than 10^6 cm^-2. We propose an innovative approach...

N-polar GaN epitaxy and high electron mobility transistors

International Nuclear Information System (INIS)

Wong, Man Hoi; Keller, Stacia; Dasgupta, Nidhi Sansaptak; Denninghoff, Daniel J; Kolluri, Seshadri; Brown, David F; Lu, Jing; Fichtenbaum, Nicholas A; Ahmadi, Elaheh; DenBaars, Steven P; Speck, James S; Mishra, Umesh K; Singisetti, Uttam; Chini, Alessandro; Rajan, Siddharth

2013-01-01

This paper reviews the progress of N-polar (0001-bar) GaN high frequency electronics that aims at addressing the device scaling challenges faced by GaN high electron mobility transistors (HEMTs) for radio-frequency and mixed-signal applications. Device quality (Al, In, Ga)N materials for N-polar heterostructures are developed using molecular beam epitaxy and metalorganic chemical vapor deposition. The principles of polarization engineering for designing N-polar HEMT structures will be outlined. The performance, scaling behavior and challenges of microwave power devices as well as highly-scaled depletion- and enhancement-mode devices employing advanced technologies including self-aligned processes, n+ (In,Ga)N ohmic contact regrowth and high aspect ratio T-gates will be discussed. Recent research results on integrating N-polar GaN with Si for prospective novel applications will also be summarized. (invited review)

Surface morphology of homoepitaxial GaN grown on non- and semipolar GaN substrates

Energy Technology Data Exchange (ETDEWEB)

Wernicke, Tim; Ploch, Simon [Institute of Solid State Physics, Technische Universitaet Berlin, Hardenbergstr. 36, 10623 Berlin (Germany); Hoffmann, Veit; Knauer, Arne; Weyers, Markus [Ferdinand-Braun-Institut, Leibniz Institut fuer Hoechstfrequenztechnik, Gustav-Kirchhoff-Str. 4, 12489 Berlin (Germany); Kneissl, Michael [Institute of Solid State Physics, Technische Universitaet Berlin, Hardenbergstr. 36, 10623 Berlin (Germany); Ferdinand-Braun-Institut, Leibniz Institut fuer Hoechstfrequenztechnik, Gustav-Kirchhoff-Str. 4, 12489 Berlin (Germany)

2011-03-15

GaN layers on bulk m-plane, (11 anti 22), (10 anti 12) and (10 anti 11) GaN substrates were grown by metal organic vapor phase epitaxy. XRD rocking curves have a FWHM of less than 150'', indicating excellent crystalline quality. However in many cases surface morphology exhibits hillocks with a height of 1-2 {mu}m and a lateral extension of 50-200 {mu}m whereas a smooth surface would be desirable for optoelectronic devices. The influence of growth parameters on the surface morphology was studied. The goal was, to constrain the material redistribution, that is necessary to form large hillocks. This was achieved by lowering the adatom diffusion length by a reduction of temperature and an increased reactor pressure. In the case of the (10 anti 11) and (10 anti 12) semipolar planes a reduction of the adatom diffusion length leads to a reduction of hillock density, hillock size and a smoother surface between hillocks. However, the m-plane surface does not react to a reduction of adatom mobility. Even at 890 C and 400 mbar rectangular pyramids cover the surface. In contrast to the other planes, the (11 anti 22) becomes instable, when the adatom diffusion length is reduced. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Probing defect states in polycrystalline GaN grown on Si(111) by sub-bandgap laser-excited scanning tunneling spectroscopy

Science.gov (United States)

Hsiao, F.-M.; Schnedler, M.; Portz, V.; Huang, Y.-C.; Huang, B.-C.; Shih, M.-C.; Chang, C.-W.; Tu, L.-W.; Eisele, H.; Dunin-Borkowski, R. E.; Ebert, Ph.; Chiu, Y.-P.

2017-01-01

We demonstrate the potential of sub-bandgap laser-excited cross-sectional scanning tunneling microscopy and spectroscopy to investigate the presence of defect states in semiconductors. The characterization method is illustrated on GaN layers grown on Si(111) substrates without intentional buffer layers. According to high-resolution transmission electron microscopy and cathodoluminescence spectroscopy, the GaN layers consist of nanoscale wurtzite and zincblende crystallites with varying crystal orientations and hence contain high defect state densities. In order to discriminate between band-to-band excitation and defect state excitations, we use sub-bandgap laser excitation. We probe a clear increase in the tunnel current at positive sample voltages during sub-bandgap laser illumination for the GaN layer with high defect density, but no effect is found for high quality GaN epitaxial layers. This demonstrates the excitation of free charge carriers at defect states. Thus, sub-bandgap laser-excited scanning tunneling spectroscopy is a powerful complimentary characterization tool for defect states.

Optical and magnetic resonance studies of Mg-doped GaN homoepitaxial layers grown by molecular beam epitaxy

International Nuclear Information System (INIS)

Glaser, E.R.; Murthy, M.; Freitas, J.A.; Storm, D.F.; Zhou, L.; Smith, D.J.

2007-01-01

Low-temperature photoluminescence (PL) and optically detected magnetic resonance (ODMR) at 24 GHz have been performed on a series of MBE-grown Mg-doped (10 17 -10 20 cm -3 ) GaN homoepitaxial layers. High-resolution PL at 5 K revealed intense bandedge emission with narrow linewidths (0.2-0.4 meV) attributed to annihilation of excitons bound to shallow Mg acceptors. In contrast to many previous reports for GaN heteroepitaxial layers doped with [Mg]>3x10 18 cm -3 , the only visible PL observed was strong shallow donor-shallow acceptor recombination with zero phonon line at 3.27 eV. Most notably, ODMR on this emission from a sample doped with [Mg] of 1x10 17 cm -3 revealed the first evidence for the highly anisotropic g-tensor (g parallel ∼2.19, g perpendicular ∼0) expected for Mg shallow acceptors in wurtzite GaN. This result is attributed to the much reduced dislocation densities (≤5x10 6 cm -3 ) and Mg impurity concentrations compared to those characteristic of the more conventional investigated Mg-doped GaN heteroepitaxial layers

Post-annealing effects on pulsed laser deposition-grown GaN thin films

International Nuclear Information System (INIS)

Cheng, Yu-Wen; Wu, Hao-Yu; Lin, Yu-Zhong; Lee, Cheng-Che; Lin, Ching-Fuh

2015-01-01

In this work, the post-annealing effects on gallium nitride (GaN) thin films grown from pulsed laser deposition (PLD) are investigated. The as-deposited GaN thin films grown from PLD are annealed at different temperatures in nitrogen ambient. Significant changes of the GaN crystal properties are observed. Raman spectroscopy is used to observe the crystallinity, the change of residual stress, and the thermal decomposition of the annealed GaN thin films. X-ray diffraction is also applied to identify the crystal phase of GaN thin films, and the surface morphology of GaN thin films annealed at different temperatures is observed by scanning electron microscopy. Through the above analyses, the GaN thin films grown by PLD undergo three stages: phase transition, stress alteration, and thermal decomposition. At a low annealing temperature, the rock salt GaN in GaN films is transformed into wurtzite. The rock salt GaN diminishes with increasing annealing temperature. At a medium annealing temperature, the residual stress of the film changes significantly from compressive strain to tensile strain. As the annealing temperature further increases, the GaN undergoes thermal decomposition and the surface becomes granular. By investigating the annealing temperature effects and controlling the optimized annealing temperature of the GaN thin films, we are able to obtain highly crystalline and strain-free GaN thin films by PLD. - Highlights: • The GaN thin film is grown on sapphire by pulsed laser deposition. • The GaN film undergoes three stages with increasing annealing temperature. • In the first stage, the film transfers from rock salt to wurtzite phase. • In the second stage, the stress in film changes from compressive to tensile. • In the final stage, the film thermally decomposes and becomes granular

Epitaxial lateral overgrowth - a tool for dislocation blockade in multilayer system

International Nuclear Information System (INIS)

Zytkiewicz, Z.R.

1998-01-01

Results on epitaxial lateral overgrowth of GaAs layers are reported. The methods of controlling the growth anisotropy, the effect of substrate defects filtration in epitaxial lateral overgrowth procedure and influence of the mask on properties of epitaxial lateral overgrowth layers will be discussed. The case od GaAs epitaxial lateral overgrowth layers grown by liquid phase epitaxy on heavily dislocated GaAs substrates was chosen as an example to illustrate the processes discussed. The similarities between our results and those reported recently for GaN layers grown laterally by metalorganic vapour phase epitaxy will be underlined. (author)

Microstructure of nitrides grown on inclined c-plane sapphire and SiC substrate

International Nuclear Information System (INIS)

Imura, M.; Honshio, A.; Miyake, Y.; Nakano, K.; Tsuchiya, N.; Tsuda, M.; Okadome, Y.; Balakrishnan, K.; Iwaya, M.; Kamiyama, S.; Amano, H.; Akasaki, I.

2006-01-01

High-quality (112-bar 0) GaN layers with atomically flat surface have been grown on a precisely offset-angle-controlled (11-bar 02) sapphire substrate by metal-organic vapor phase epitaxy (MOVPE). Insertion of AlGaN layer between underlying AlN layer and GaN was found to improve crystalline quality of upper GaN layer. In addition, a combination of high growth condition followed and epitaxial lateral overgrowth has been employed for the growth of GaN and this helped in reducing the dislocation density in the resultant layers. GaN and AlN were grown on (303-bar 8) SiC substrates by MOVPE and sublimation methods, respectively. The crystal orientation of GaN and AlN could be just aligned to that of the substrate. Microstructure analysis of the layers was also carried out by transmission electron microscopy

Characterization of vertical GaN p-n diodes and junction field-effect transistors on bulk GaN down to cryogenic temperatures

Science.gov (United States)

Kizilyalli, I. C.; Aktas, O.

2015-12-01

There is great interest in wide-bandgap semiconductor devices and most recently in vertical GaN structures for power electronic applications such as power supplies, solar inverters and motor drives. In this paper the temperature-dependent electrical behavior of vertical GaN p-n diodes and vertical junction field-effect transistors fabricated on bulk GaN substrates of low defect density (104 to 106 cm-2) is described. Homoepitaxial MOCVD growth of GaN on its native substrate and the ability to control the doping in the drift layers in GaN have allowed the realization of vertical device architectures with drift layer thicknesses of 6 to 40 μm and net carrier electron concentrations as low as 1 × 1015 cm-3. This parameter range is suitable for applications requiring breakdown voltages of 1.2 kV to 5 kV. Mg, which is used as a p-type dopant in GaN, is a relatively deep acceptor (E A ≈ 0.18 eV) and susceptible to freeze-out at temperatures below 200 K. The loss of holes in p-GaN has a deleterious effect on p-n junction behavior, p-GaN contacts and channel control in junction field-effect transistors at temperatures below 200 K. Impact ionization-based avalanche breakdown (BV > 1200 V) in GaN p-n junctions is characterized between 77 K and 423 K for the first time. At higher temperatures the p-n junction breakdown voltage improves due to increased phonon scattering. A positive temperature coefficient in the breakdown voltage is demonstrated down to 77 K; however, the device breakdown characteristics are not as abrupt at temperatures below 200 K. On the other hand, contact resistance to p-GaN is reduced dramatically above room temperature, improving the overall device performance in GaN p-n diodes in all cases except where the n-type drift region resistance dominates the total forward resistance. In this case, the electron mobility can be deconvolved and is found to decrease with T -3/2, consistent with a phonon scattering model. Also, normally-on vertical junction

Step-flow anisotropy of the m-plane GaN (1100) grown under nitrogen-rich conditions by plasma-assisted molecular beam epitaxy

International Nuclear Information System (INIS)

Sawicka, Marta; Siekacz, Marcin; Skierbiszewski, Czeslaw; Turski, Henryk; Krysko, Marcin; DziePcielewski, Igor; Grzegory, Izabella; Smalc-Koziorowska, Julita

2011-01-01

The homoepitaxial growth of m-plane (1100) GaN was investigated by plasma-assisted molecular beam epitaxy under nitrogen-rich conditions. The surface morphologies as a function of sample miscut were studied, providing evidence for a strong growth anisotropy that is a consequence of the anisotropy of Ga adatom diffusion barriers on the m-plane surface recently calculated ab initio[Lymperakis and Neugebauer, Phys. Rev. B 79, 241308(R) (2009)]. We found that substrate miscut toward [0001] implies a step flow toward while substrate miscut toward [0001] causes formation of atomic steps either perpendicular or parallel to the [0001] direction, under N-rich conditions at 730 deg C. We describe the growth conditions for achieving atomically flat m-plane GaN layers with parallel atomic steps.

Stress evolution of GaN/AlN heterostructure grown on 6H-SiC substrate by plasma assisted molecular beam epitaxy

Directory of Open Access Journals (Sweden)

M. Agrawal

2017-01-01

Full Text Available The stress evolution of GaN/AlN heterostructure grown on 6H-SiC substrate by plasma assisted molecular beam epitaxy (PA-MBE has been studied. AlN nucleation layer and GaN layer were grown as a function of III/V ratio. GaN/AlN structure is found to form buried cracks when AlN is grown in the intermediate growth regime(III/V∼1and GaN is grown under N-rich growth regime (III/V<1. The III/V ratio determines the growth mode of the layers that influences the lattice mismatch at the GaN/AlN interface. The lattice mismatch induced interfacial stress at the GaN/AlN interface relaxes by the formation of buried cracks in the structure. Additionally, the stress also relaxes by misorienting the AlN resulting in two misorientations with different tilts. Crack-free layers were obtained when AlN and GaN were grown in the N-rich growth regime (III/V<1 and metal rich growth regime (III/V≥1, respectively. AlGaN/GaN high electron mobility transistor (HEMT heterostructure was demonstrated on 2-inch SiC that showed good two dimensional electron gas (2DEG properties with a sheet resistance of 480 Ω/sq, mobility of 1280 cm2/V.s and sheet carrier density of 1×1013 cm−2.

Transient atomic behavior and surface kinetics of GaN

International Nuclear Information System (INIS)

Moseley, Michael; Billingsley, Daniel; Henderson, Walter; Trybus, Elaissa; Doolittle, W. Alan

2009-01-01

An in-depth model for the transient behavior of metal atoms adsorbed on the surface of GaN is developed. This model is developed by qualitatively analyzing transient reflection high energy electron diffraction (RHEED) signals, which were recorded for a variety of growth conditions of GaN grown by molecular-beam epitaxy (MBE) using metal-modulated epitaxy (MME). Details such as the initial desorption of a nitrogen adlayer and the formation of the Ga monolayer, bilayer, and droplets are monitored using RHEED and related to Ga flux and shutter cycles. The suggested model increases the understanding of the surface kinetics of GaN, provides an indirect method of monitoring the kinetic evolution of these surfaces, and introduces a novel method of in situ growth rate determination.

Transient atomic behavior and surface kinetics of GaN

Science.gov (United States)

Moseley, Michael; Billingsley, Daniel; Henderson, Walter; Trybus, Elaissa; Doolittle, W. Alan

2009-07-01

An in-depth model for the transient behavior of metal atoms adsorbed on the surface of GaN is developed. This model is developed by qualitatively analyzing transient reflection high energy electron diffraction (RHEED) signals, which were recorded for a variety of growth conditions of GaN grown by molecular-beam epitaxy (MBE) using metal-modulated epitaxy (MME). Details such as the initial desorption of a nitrogen adlayer and the formation of the Ga monolayer, bilayer, and droplets are monitored using RHEED and related to Ga flux and shutter cycles. The suggested model increases the understanding of the surface kinetics of GaN, provides an indirect method of monitoring the kinetic evolution of these surfaces, and introduces a novel method of in situ growth rate determination.

Carrier concentration dependence of donor activation energy in n-type GaN epilayers grown on Si (1 1 1) by plasma-assisted MBE

International Nuclear Information System (INIS)

Kumar, Mahesh; Bhat, Thirumaleshwara N.; Roul, Basanta; Rajpalke, Mohana K.; Kalghatgi, A.T.; Krupanidhi, S.B.

2012-01-01

Highlights: ► The n-type GaN layers were grown by plasma-assisted molecular beam epitaxy. ► The optical characteristics of a donor level in Si-doped GaN were studied. ► Activation energy of a Si-related donor was estimated from temperature dependent PL measurements. ► PL peak positions, FWHM of PL and activation energies are found to be proportional to the cube root of carrier density. ► The involvement of donor levels is supported by the temperature-dependent electron concentration measurements. -- Abstract: The n-type GaN layers were grown by plasma-assisted MBE and either intentionally doped with Si or unintentionally doped. The optical characteristics of a donor level in Si-doped, GaN were studied in terms of photoluminescence (PL) spectroscopy as a function of electron concentration. Temperature dependent PL measurements allowed us to estimate the activation energy of a Si-related donor from temperature-induced decay of PL intensity. PL peak positions, full width at half maximum of PL and activation energies are found to be proportional to the cube root of carrier density. The involvement of donor levels is supported by the temperature-dependent electron concentration measurements.

The Study of Al0.29Ga0.71N-BASED Schottky Photodiodes Grown on Silicon by Plasma-Assisted Molecular Beam Epitaxy

Science.gov (United States)

Mohd Yusoff, M. Z.; Hassan, Z.; Chin, C. W.; Hassan, H. Abu; Abdullah, M. J.; Mohammad, N. N.; Ahmad, M. A.; Yusof, Y.

2013-05-01

In this paper, the growth and characterization of epitaxial Al0.29Ga0.71N grown on Si(111) by RF-plasma assisted molecular beam epitaxy (MBE) are described. The Al mole fraction was derived from the HR-XRD symmetric rocking curve (RC) ω/2θ scans of (0002) plane as x = 0.29. PL spectrum of sample has shown sharp and intense band edge emission of GaN without the existence of yellow emission band, showing that it is comparable in crystal quality of the sample when compared with previous reports. From the Raman measurement of as-grown Al0.29Ga0.71N layer on GaN/AlN/Si sample. We found that the dominant E2 (high) phonon mode of GaN appears at 572.7 cm-1. The E2 (high) mode of AlN appears at 656.7 cm-1 and deviates from the standard value of 655 cm-1 for unstrained AlN. Finally, AlGaN Schottky photodiode have been fabricated and analyzed by mean of electrical characterization, using current-voltage (I-V) measurement to evaluate the performance of this device.

Characterization of vertical GaN p–n diodes and junction field-effect transistors on bulk GaN down to cryogenic temperatures

International Nuclear Information System (INIS)

Kizilyalli, I C; Aktas, O

2015-01-01

There is great interest in wide-bandgap semiconductor devices and most recently in vertical GaN structures for power electronic applications such as power supplies, solar inverters and motor drives. In this paper the temperature-dependent electrical behavior of vertical GaN p–n diodes and vertical junction field-effect transistors fabricated on bulk GaN substrates of low defect density (10 4 to 10 6 cm −2 ) is described. Homoepitaxial MOCVD growth of GaN on its native substrate and the ability to control the doping in the drift layers in GaN have allowed the realization of vertical device architectures with drift layer thicknesses of 6 to 40 μm and net carrier electron concentrations as low as 1 × 10 15 cm −3 . This parameter range is suitable for applications requiring breakdown voltages of 1.2 kV to 5 kV. Mg, which is used as a p-type dopant in GaN, is a relatively deep acceptor (E A  ≈ 0.18 eV) and susceptible to freeze-out at temperatures below 200 K. The loss of holes in p-GaN has a deleterious effect on p–n junction behavior, p-GaN contacts and channel control in junction field-effect transistors at temperatures below 200 K. Impact ionization-based avalanche breakdown (BV > 1200 V) in GaN p–n junctions is characterized between 77 K and 423 K for the first time. At higher temperatures the p–n junction breakdown voltage improves due to increased phonon scattering. A positive temperature coefficient in the breakdown voltage is demonstrated down to 77 K; however, the device breakdown characteristics are not as abrupt at temperatures below 200 K. On the other hand, contact resistance to p-GaN is reduced dramatically above room temperature, improving the overall device performance in GaN p–n diodes in all cases except where the n-type drift region resistance dominates the total forward resistance. In this case, the electron mobility can be deconvolved and is found to decrease with T −3/2 , consistent with a phonon scattering model. Also

Chemical lift-off of (11-22) semipolar GaN using periodic triangular cavities

Science.gov (United States)

Jeon, Dae-Woo; Lee, Seung-Jae; Jeong, Tak; Baek, Jong Hyeob; Park, Jae-Woo; Jang, Lee-Woon; Kim, Myoung; Lee, In-Hwan; Ju, Jin-Woo

2012-01-01

Chemical lift-off of (11-22) semipolar GaN using triangular cavities was investigated. The (11-22) semipolar GaN was grown using epitaxial lateral overgrowth by metal-organic chemical vapor deposition on m-plane sapphire, in such a way as to keep N terminated surface of c-plane GaN exposed in the cavities. After regrowing 300 μm thick (11-22) semipolar GaN by hydride vapor phase epitaxy for a free-standing (11-22) semipolar GaN substrate, the triangular cavities of the templates were chemically etched in molten KOH. The (000-2) plane in the triangular cavities can be etched in the [0002] direction with the high lateral etching rate of 196 μm/min. The resulting free-standing (11-22) semipolar GaN substrate was confirmed to be strain-free by the Raman analysis.

GaN growth via HVPE on SiC/Si substrates: growth mechanisms

Science.gov (United States)

Sharofidinov, Sh Sh; Redkov, A. V.; Osipov, A. V.; Kukushkin, S. A.

2017-11-01

The article focuses on the study of GaN thin film growth via chloride epitaxy on SiC/Si hybrid substrate. SiC buffer layer was grown by a method of substitution of atoms, which allows one to reduce impact of mechanical stress therein on subsequent growth of III-nitride films. It is shown, that change in GaN growth conditions leads to change in its growth mechanism. Three mechanisms: epitaxial, spiral and stepwise growth are considered and mechanical stresses are estimated via Raman spectroscopy.

Thermal Annealing induced relaxation of compressive strain in porous GaN structures

KAUST Repository

Ben Slimane, Ahmed

2012-01-01

The effect of annealing on strain relaxation in porous GaN fabricated using electroless chemical etching is presented. The Raman shift of 1 cm-1 in phonon frequency of annealed porous GaN with respect to as-grown GaN corresponds to a relaxation of compressive strain by 0.41 ± 0.04 GPa. The strain relief promises a marked reduction in threading dislocation for subsequent epitaxial growth.

Defect attributed variations of the photoconductivity and photoluminescence in the HVPE and MOCVD as-grown and irradiated GaN structures

International Nuclear Information System (INIS)

Gaubas, E.; Pobedinskas, P.; Vaitkus, J.; Uleckas, A.; Zukauskas, A.; Blue, A.; Rahman, M.; Smith, K.M.; Aujol, E.; Beaumont, B.; Faurie, J.-P.; Gibart, P.

2005-01-01

The effect of native and radiation induced defects on the photoconductivity transients and photoluminescence spectra have been examined in GaN epitaxial layers of 2.5 and 12μm thickness grown on bulk n-GaN/sapphire substrates by metal-organic chemical vapor deposition (MOCVD). For comparison, free-standing GaN as-grown samples of 500μm thickness, fabricated by hydride vapor phase epitaxy (HVPE), were investigated. Manifestation of defects induced by 10-keV X-ray irradiation with the dose of 600Mrad and 100-keV neutrons with the fluences of 5x10 14 and 10 16 cm -2 as well as of 24GeV/c protons with fluence 10 16 cm -2 have been revealed through contact photoconductivity and microwave absorption transients. The amplitude of the initial photoconductivity decay is significantly reduced by the native and radiation defects density. Synchronous decrease of the steady-state PL intensity of yellow, blue and ultraviolet bands peaked at 2.18, 2.85, and 3.42eV, respectively, with density of radiation-induced defects is observed. The decrease of the PL intensity is accompanied by an increase of asymptotic decay lifetime in the photoconductivity transients, which is due to excess-carrier multi-trapping. The decay fits the stretched exponent approximation exp[-(t/τ) α ] with the different factors α in as-grown material (α∼0.7) and irradiated samples (α∼0.3). The fracton dimension d s of disordered structure changes from 4.7 to 0.86 for as-grown and irradiated material, respectively, and it implies the percolative carrier motion on an infinite cluster of dislocations net in the as-grown material and cluster fragmentation into finite fractons after irradiations

Ga induced superstructures as templates for lattice matched hetroepitaxial growth of GaN on Si(111) substrate

International Nuclear Information System (INIS)

Kumar, Praveen; Kuyyalil, Jithesh; Shivaprasad, S. M.

2010-01-01

High quality GaN is grown by plasma assisted molecular beam epitaxy on Ga induced superstructural phases of Si(111)7x7. Three stable surface phases induced by Ga adsorption, viz., (1x1), (6.3x6.3), and (√3x√3)R30 deg., are employed as templates to grow epitaxial (0001) GaN thin films. GaN grown on Si(√3x√3)R30 deg. -Ga is found to be highly crystalline with intense (0002) x-ray diffraction and photoluminescence peaks with low full width at half maximum, low surface roughness, and stoichiometric surface composition. The high quality of these GaN films formed at a low temperature of 400 deg. C is explained by the integral (x2) lattice matching between the unit cell of GaN and the (√3x√3) phase. The experiments demonstrate a plausible approach of adsorbate induced surface modifications as templates for III-V hetroepitaxy on Si surfaces.

Characterization and growth mechanism of nonpolar and semipolar GaN layers grown on patterned sapphire substrates

International Nuclear Information System (INIS)

Okada, Narihito; Tadatomo, Kazuyuki

2012-01-01

Nonpolar and semipolar GaN layers with markedly improved crystalline quality can be obtained by selective-area growth from the sapphire sidewalls of patterned sapphire substrates (PSSs). In this paper, we review the crystalline qualities of GaN layers grown on PSSs and their growth mechanism. We grew semipolar {1 1 −2 2} and {1 0 −1 1} GaN layers on r- and n-PSSs. The crystalline qualities of the GaN layers grown on the PSSs were higher than those of GaN layers grown directly on heteroepitaxial substrates. To reveal the growth mechanism of GaN layers grown on PSSs, we also grew various nonpolar and semipolar GaN layers such as m-GaN on a-PSS, {1 1 −2 2} GaN on r-PSS, {1 0 − 1  1} GaN on n-PSS, m-GaN on c-PSS and a-GaN on m-PSS. It was found that the nucleation of GaN on the c-plane-like sapphire sidewall results in selective growth from the sapphire sidewall, and nonpolar or semipolar GaN can be obtained. Finally, we demonstrated a light-emitting diode fabricated on a {1 1 −2 2} GaN layer grown on an r-PSS. (paper)

Improved InGaN/GaN quantum wells on treated GaN template with a Ga-rich GaN interlayer

International Nuclear Information System (INIS)

Fang, Zhilai; Shen, Xiyang; Wu, Zhengyuan; Zhang, Tong-Yi

2015-01-01

Treated GaN template was achieved by in situ droplet epitaxy of a Ga-rich GaN interlayer on the conventional GaN template. InGaN/GaN quantum wells (QWs) were grown on the conventional and treated GaN templates under the same growth conditions and then comprehensively characterized. The indium homogeneity in the InGaN layers and the interface sharpness between InGaN and GaN layers of the InGaN/GaN QWs on the treated GaN template were significantly improved. The emission intensity from the InGaN/GaN QWs on the treated GaN template was enhanced by 20% than that on the conventional GaN template, which was attributed to the strain reduction and the improvement in crystalline quality. (copyright 2015 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Ion Beam Assisted Deposition of Thin Epitaxial GaN Films.

Science.gov (United States)

Rauschenbach, Bernd; Lotnyk, Andriy; Neumann, Lena; Poppitz, David; Gerlach, Jürgen W

2017-06-23

The assistance of thin film deposition with low-energy ion bombardment influences their final properties significantly. Especially, the application of so-called hyperthermal ions (energy GaN thin films on (0001)-oriented 6H-SiC substrates at 700 °C. The films are studied in situ by reflection high energy electron diffraction, ex situ by X-ray diffraction, scanning tunnelling microscopy, and high-resolution transmission electron microscopy. It is demonstrated that the film growth mode can be controlled by varying the ion to atom ratio, where 2D films are characterized by a smooth topography, a high crystalline quality, low biaxial stress, and low defect density. Typical structural defects in the GaN thin films were identified as basal plane stacking faults, low-angle grain boundaries forming between w-GaN and z-GaN and twin boundaries. The misfit strain between the GaN thin films and substrates is relieved by the generation of edge dislocations in the first and second monolayers of GaN thin films and of misfit interfacial dislocations. It can be demonstrated that the low-energy nitrogen ion assisted molecular beam epitaxy is a technique to produce thin GaN films of high crystalline quality.

Structural, electrical and luminescent characteristics of ultraviolet light emitting structures grown by hydride vapor phase epitaxy

Directory of Open Access Journals (Sweden)

A.Y. Polyakov

2017-03-01

Full Text Available Electrical and luminescent properties of near-UV light emitting diode structures (LEDs prepared by hydride vapor phase epitaxy (HVPE were studied. Variations in photoluminescence and electroluminescence efficiency observed for LEDs grown under nominally similar conditions could be attributed to the difference in the structural quality (dislocation density, density of dislocations agglomerates of the GaN active layers, to the difference in strain relaxation achieved by growth of AlGaN/AlGaN superlattice and to the presence of current leakage channels in current confining AlGaN layers of the double heterostructure.

Growth kinetics and structural perfection of (InN)_1/(GaN)_1_–_2_0 short-period superlattices on +c-GaN template in dynamic atomic layer epitaxy

International Nuclear Information System (INIS)

Kusakabe, Kazuhide; Hashimoto, Naoki; Wang, Ke; Imai, Daichi; Itoi, Takaomi; Yoshikawa, Akihiko

2016-01-01

The growth kinetics and structural perfection of (InN)_1/(GaN)_1_–_2_0 short-period superlattices (SPSs) were investigated with their application to ordered alloys in mind. The SPSs were grown on +c-GaN template at 650 °C by dynamic atomic layer epitaxy in conventional plasma-assisted molecular beam epitaxy. It was found that coherent structured InN/GaN SPSs could be fabricated when the thickness of the GaN barrier was 4 ML or above. Below 3 ML, the formation of SPSs was quite difficult owing to the increased strain in the SPS structure caused by the use of GaN as a template. The effective or average In composition of the (InN)_1/(GaN)_4 SPSs was around 10%, and the corresponding InN coverage in the ∼1 ML-thick InN wells was 50%. It was found that the effective InN coverage in ∼1 ML-thick InN wells could be varied with the growth conditions. In fact, the effective In composition could be increased up to 13.5%, i.e., the corresponding effective InN coverage was about 68%, by improving the capping/freezing speed by increasing the growth rate of the GaN barrier layer.

High-quality GaN nanowires grown on Si and porous silicon by thermal evaporation

Energy Technology Data Exchange (ETDEWEB)

Shekari, L., E-mail: lsg09_phy089@student.usm.my [Nano-Optoelectronics Research and Technology Laboratory, School of Physics, Universiti Sains Malaysia, 11800 USM, Penang (Malaysia); Ramizy, A.; Omar, K.; Hassan, H. Abu; Hassan, Z. [Nano-Optoelectronics Research and Technology Laboratory, School of Physics, Universiti Sains Malaysia, 11800 USM, Penang (Malaysia)

2012-12-15

Highlights: Black-Right-Pointing-Pointer A new kind of substrate (porous silicon) was used. Black-Right-Pointing-Pointer Also this research introduces an easy and safe method to grow high quality GaN NWs. Black-Right-Pointing-Pointer This is a new growth process to decrease the cost, complexity of growth of GaN NWs. Black-Right-Pointing-Pointer It is a controllable method to synthesize GaN NWs by thermal evaporation. - Abstract: Nanowires (NWs) of GaN thin films were prepared on as-grown Si (1 1 1) and porous silicon (PS) substrates using thermal evaporation method. The film growth produced high-quality wurtzite GaN NWs. The size, morphology, and nanostructures of the crystals were investigated through scanning electron microscopy, high-resolution X-ray diffraction and photoluminescence spectroscopy. The NWs grown on porous silicon were thinner, longer and denser compared with those on as-grown Si. The energy band gap of the NWs grown on PS was larger than that of NWs on as-grown Si. This is due to the greater quantum confinement effects of the crystalline structure of the NWs grown on PS.

Electrothermal evaluation of thick GaN epitaxial layers and AlGaN/GaN high-electron-mobility transistors on large-area engineered substrates

Science.gov (United States)

Anderson, Travis J.; Koehler, Andrew D.; Tadjer, Marko J.; Hite, Jennifer K.; Nath, Anindya; Mahadik, Nadeemullah A.; Aktas, Ozgur; Odnoblyudov, Vladimir; Basceri, Cem; Hobart, Karl D.; Kub, Francis J.

2017-12-01

AlGaN/GaN high-electron-mobility transistor (HEMT) device layers were grown by metal organic chemical vapor deposition (MOCVD) on commercial engineered QST™ substrates to demonstrate a path to scalable, cost-effective foundry processing while supporting the thick epitaxial layers required for power HEMT structures. HEMT structures on 150 mm Si substrates were also evaluated. The HEMTs on engineered substrates exhibited material quality, DC performance, and forward blocking performance superior to those of the HEMT on Si. GaN device layers up to 15 µm were demonstrated with a wafer bow of 1 µm, representing the thickest films grown on 150-mm-diameter substrates with low bow to date.

High optical and structural quality of GaN epilayers grown on ( 2¯01) β-Ga2O3

KAUST Repository

Mumthaz Muhammed, Mufasila; Peres, M.; Yamashita, Y.; Morishima, Y.; Sato, S.; Franco, N.; Lorenz, K.; Kuramata, A.; Roqan, Iman S.

2014-01-01

Producing highly efficient GaN-based optoelectronic devices has been a challenge for a long time due to the large lattice mismatch between III-nitride materials and the most common substrates, which causes a high density of threading dislocations. Therefore, it is essential to obtain alternative substrates with small lattice mismatches, appropriate structural, thermal and electrical properties, and a competitive price. Our results show that (2̄01) oriented β-Ga2O3 has the potential to be used as a transparent and conductive substrate for GaN-growth. Photoluminescence spectra of thick GaN layers grown on (2̄01) oriented β-Ga 2O3 are found to be dominated by intense bandedge emission. Atomic force microscopy studies show a modest threading dislocation density of ∼108cm-2. X-ray diffraction studies show the high quality of the single-phase wurtzite GaN thin film on (2̄01) β-Ga2O3 with in-plane epitaxial orientation relationships between the β-Ga2O3 and the GaN thin film defined by (010) β-Ga2O3 || (112̄0) GaN and (2̄01) β-Ga2O3 || (0001) GaN leading to a lattice mismatch of ∼4.7%. Complementary Raman spectroscopy indicates that the quality of the GaN epilayer is high. © 2014 AIP Publishing LLC.

High optical and structural quality of GaN epilayers grown on ( 2¯01) β-Ga2O3

KAUST Repository

Mumthaz Muhammed, Mufasila

2014-07-28

Producing highly efficient GaN-based optoelectronic devices has been a challenge for a long time due to the large lattice mismatch between III-nitride materials and the most common substrates, which causes a high density of threading dislocations. Therefore, it is essential to obtain alternative substrates with small lattice mismatches, appropriate structural, thermal and electrical properties, and a competitive price. Our results show that (2̄01) oriented β-Ga2O3 has the potential to be used as a transparent and conductive substrate for GaN-growth. Photoluminescence spectra of thick GaN layers grown on (2̄01) oriented β-Ga 2O3 are found to be dominated by intense bandedge emission. Atomic force microscopy studies show a modest threading dislocation density of ∼108cm-2. X-ray diffraction studies show the high quality of the single-phase wurtzite GaN thin film on (2̄01) β-Ga2O3 with in-plane epitaxial orientation relationships between the β-Ga2O3 and the GaN thin film defined by (010) β-Ga2O3 || (112̄0) GaN and (2̄01) β-Ga2O3 || (0001) GaN leading to a lattice mismatch of ∼4.7%. Complementary Raman spectroscopy indicates that the quality of the GaN epilayer is high. © 2014 AIP Publishing LLC.

GaN epilayers on nanopatterned GaN/Si(1 1 1) templates: Structural and optical characterization

International Nuclear Information System (INIS)

Wang, L.S.; Tripathy, S.; Wang, B.Z.; Chua, S.J.

2006-01-01

Template-based nanoscale epitaxy has been explored to realize high-quality GaN on Si(1 1 1) substrates. We have employed polystyrene-based nanosphere lithography to form the nano-hole array patterns on GaN/Si(1 1 1) template and then, subsequent regrowth of GaN is carried out by metalorganic chemical vapor deposition (MOCVD). During the initial growth stage of GaN on such nanopatterned substrates, we have observed formation of nanoislands with hexagonal pyramid shape due to selective area epitaxy. With further epitaxial regrowth, these nanoislands coalesce and form continuous GaN film. The overgrown GaN on patterned and non-patterned regions is characterized by high-resolution X-ray diffraction (HRXRD) and high-spatial resolution optical spectroscopic methods. Micro-photoluminescence (PL), micro-Raman scattering and scanning electron microscopy (SEM) have been used to assess the microstructural and optical properties of GaN. Combined PL and Raman data analyses show improved optical quality when compared to GaN simultaneously grown on non-patterned bulk Si(1 1 1). Such thicker GaN templates would be useful to achieve III-nitride-based opto- and electronic devices integrated on Si substrates

Effect of SiC buffer layer on GaN growth on Si via PA-MBE

Science.gov (United States)

Kukushkin, S. A.; Mizerov, A. M.; Osipov, A. V.; Redkov, A. V.; Telyatnik, R. S.; Timoshnev, S. N.

2017-11-01

The study is devoted to comparison of GaN thin films grown on SiC/Si substrates made by the method of atoms substitution with the films grown directly on Si substrates. The growth was performed in a single process via plasma assisted molecular beam epitaxy. The samples were studied via optical microscopy, Raman spectroscopy, ellipsometry, and a comparison of their characteristics was made. Using chemical etching in KOH, the polarity of GaN films grown on SiC/Si and Si substrates was determined.

Lattice site location of optical centers in GaN:Eu light emitting diode material grown by organometallic vapor phase epitaxy

KAUST Repository

Lorenz, K.; Alves, E.; Roqan, Iman S.; O’ Donnell, K. P.; Nishikawa, A.; Fujiwara, Y.; Boćkowski, M.

2010-01-01

Eu-doped GaN was grown by organometallic vapor phase epitaxy at temperatures from 900 to 1100 °C. Eu incorporation is influenced by temperature with the highest concentration found for growth at 1000 °C. In all samples, Eu is incorporated entirely on substitutional Ga sites with a slight displacement which is highest (∼0.2 Å) in the sample grown at 900 °C and mainly directed along the c-axis. The major optical Eu3+ centers are identical for in situdoped and ion-implanted samples after high temperature and pressure annealing. The dominant Eu3+luminescence lines are attributed to isolated, substitutional Eu.

Lattice site location of optical centers in GaN:Eu light emitting diode material grown by organometallic vapor phase epitaxy

KAUST Repository

Lorenz, K.

2010-09-16

Eu-doped GaN was grown by organometallic vapor phase epitaxy at temperatures from 900 to 1100 °C. Eu incorporation is influenced by temperature with the highest concentration found for growth at 1000 °C. In all samples, Eu is incorporated entirely on substitutional Ga sites with a slight displacement which is highest (∼0.2 Å) in the sample grown at 900 °C and mainly directed along the c-axis. The major optical Eu3+ centers are identical for in situdoped and ion-implanted samples after high temperature and pressure annealing. The dominant Eu3+luminescence lines are attributed to isolated, substitutional Eu.

Impact of substrate off-angle on the m-plane GaN Schottky diodes

Science.gov (United States)

Yamada, Hisashi; Chonan, Hiroshi; Takahashi, Tokio; Shimizu, Mitsuaki

2018-04-01

We investigated the effects of the substrate off-angle on the m-plane GaN Schottky diodes. GaN epitaxial layers were grown by metal-organic chemical vapor deposition on m-plane GaN substrates having an off-angle of 0.1, 1.1, 1.7, or 5.1° toward [000\\bar{1}]. The surface of the GaN epitaxial layers on the 0.1°-off substrate consisted of pyramidal hillocks and contained oxygen (>1017 cm-3) and carbon (>1016 cm-3) impurities. The residual carbon and oxygen impurities decreased to current of the 0.1°-off m-plane GaN Schottky diodes originated from the +c facet of the pyramidal hillocks. The leakage current was efficiently suppressed through the use of an off-angle that was observed to be greater than 1.1°. The off-angle of the m-plane GaN substrate is critical in obtaining high-performance Schottky diodes.

Molecular beam epitaxy of InN layers on Sapphire, GaN and indium tin oxide

Energy Technology Data Exchange (ETDEWEB)

Denker, Christian; Landgraf, Boris; Schuhmann, Henning; Malindretos, Joerg; Seibt, Michael; Rizzi, Angela [IV. Physikalisches Institut, Georg-August-Universitaet Goettingen (Germany); Segura-Ruiz, Jaime; Gomez-Gomez, Maribel; Cantarero, Andres [Materials Science Institute, University of Valencia, Paterna (Spain)

2009-07-01

Among the group-III nitrides semiconductors, InN is the one with the narrowest gap (0.67 eV), lowest effective electron mass and highest peak drift velocity. It is therefore a very interesting material for several applications, in particular semiconductor solar cells. Furthermore, the high electron affinity makes it suitable also as electrode material for organic solar cells. InN layers were grown by molecular beam epitaxy on MOCVD GaN templates, on bare c-plane sapphire and on polycrystalline indium tin oxide. On all substrates the III-V ratio as well as the substrate temperature was varied. A RHEED analysis of InN growth on GaN showed a relatively sharp transition from N-rich and columnar growth to In-rich growth with droplet formation by increasing the In flux impinging on the surface. The InN layers on single crystalline substrates were characterized by SEM, AFM, XRD, PL and Raman. The InN layers on ITO were mainly analyzed with respect to the surface morphology with SEM. HRTEM in cross section gives insight into the structure of the interface to the ITO substrate.

Photoluminescence of Mg-doped m-plane GaN grown by MOCVD on bulk GaN substrates

Energy Technology Data Exchange (ETDEWEB)

Monemar, Bo [Department of Physics, Chemistry and Biology, Linkoeping University, 581 83 Linkoeping (Sweden); Solid State Physics-The Nanometer Structure Consortium, Lund University, Box 118, 221 00 Lund (Sweden); Paskov, Plamen; Pozina, Galia; Hemmingsson, Carl; Bergman, Peder [Department of Physics, Chemistry and Biology, Linkoeping University, 581 83 Linkoeping (Sweden); Lindgren, David; Samuelson, Lars [Solid State Physics-The Nanometer Structure Consortium, Lund University, Box 118, 221 00 Lund (Sweden); Ni, Xianfeng; Morkoc, Hadis [Department of Electrical and Computer Engineering, Virginia Commonwealth University, Richmond, Virginia 23284-3072 (United States); Paskova, Tanya [Kyma Technologies Inc., Raleigh, North Carolina 27617 (United States); Bi, Zhaoxia; Ohlsson, Jonas [Glo AB, Ideon Science Park, Scheelevaegen 17, 223 70 Lund (Sweden)

2011-07-15

Photoluminescence (PL) properties are reported for a set of m-plane GaN films with Mg doping varied from mid 10{sup 18} cm{sup -3} to above 10{sup 20} cm{sup -3}. The samples were grown with MOCVD at reduced pressure on low defect density bulk GaN templates. The sharp line near bandgap bound exciton (BE) spectra observed below 50 K, as well as the broader donor-acceptor pair (DAP) PL bands at 2.9-3.3 eV give evidence of several Mg related acceptors, similar to the case of c-plane GaN. The dependence of the BE spectra on excitation intensity as well as the transient decay behaviour demonstrate acoustic phonon assisted transfer between the acceptor BE states. The lower energy donor-acceptor pair spectra suggest the presence of deep acceptors, in addition to the two main shallower ones at about 0.23 eV. Similar spectra from Mg-doped GaN nanowires (NWs) grown by MOCVD are also briefly discussed. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

High-resolution hydrogen profiling in AlGaN/GaN heterostructures grown by different epitaxial methods

Energy Technology Data Exchange (ETDEWEB)

Gonzalez-Posada Flores, F; Redondo-Cubero, A; Bengoechea, A; Brana, A F; Munoz, E [Instituto de Sistemas Optoelectronicos y Microtecnologia (ISOM) and Dpto. IngenierIa Electronica (DIE), ETSI de Telecomunicacion, Universidad Politecnica de Madrid, E-28040 Madrid (Spain); Gago, R [Centro de Micro-Analisis de Materiales, Universidad Autonoma de Madrid, E-28049 Madrid (Spain); Jimenez, A [Dpto. Electronica, Escuela Politecnica Superior, Universidad de Alcala, E-28805 Alcala de Henares, Madrid (Spain); Grambole, D, E-mail: fposada@die.upm.e [Institute of Ion Beam Physics and Materials Research, Forschungszentrum Dresden-Rossendorf, PF 51019, D-01314 Dresden (Germany)

2009-03-07

Hydrogen (H) incorporation into AlGaN/GaN heterostructures used in high electron mobility transistors, grown by different methods, is studied by high-resolution depth profiling. Samples grown on sapphire and Si(1 1 1) substrates by molecular-beam epitaxy and metal-organic vapour phase epitaxy; involving H-free and H-containing precursors, were analysed to evaluate the eventual incorporation of H into the wafer. The amount of H was measured by means of nuclear reaction analysis (NRA) using the {sup 1}H({sup 15}N,{alpha}{gamma}){sup 12}C reaction up to a depth of {approx}110 nm into the heterostructures. Interestingly, the H profiles are similar in all the samples analysed, with an increasing H content towards the surface and a negligible H incorporation into the GaN layer (0.24 {+-} 0.08 at%) or at the AlGaN/GaN interface. Therefore, NRA shows that H uptake is not related to the growth process or technique employed and that H contamination may be due to external sources after growth. The eventual correlation between topographical defects on the AlGaN surface and the H concentration are also discussed.

Heteroepitaxial growth of basal plane stacking fault free a-plane GaN

Energy Technology Data Exchange (ETDEWEB)

Wieneke, Matthias; Hempel, Thomas; Noltemeyer, Martin; Witte, Hartmut; Dadgar, Armin; Blaesing, Juergen; Christen, Juergen; Krost, Alois [Otto-von-Guericke Universitaet Magdeburg, FNW/IEP, Magdeburg (Germany)

2010-07-01

Growth of light emitting quantum-wells based on a-plane GaN is a possibility to reduce or even to avoid polarization correlated luminescence red shift and reduction of radiative recombination efficiency. But until now heteroepitaxially grown a-plane GaN films are characterized by a poor crystalline quality expressed by a high density of basal plane stacking faults (BSF) and partial dislocations. We present Si doped a-plane GaN films grown on r-plane sapphire substrates by metal organic vapor phase epitaxy using high temperature AlGaN nucleation layers. FE-SEM images revealed three dimensionally grown GaN crystallites sized up to tenth micrometer in the basal plane and a few tenth micrometers along the c-axes. Though, the full width at half maxima of the X-ray diffraction {omega}-scans of the in-plane GaN(1 anti 100) and GaN(0002) Bragg reflections exhibited a very high crystal quality. Furthermore, luminescence spectra were dominated by near band gap emission, while there was no separated peak of the basal plane stacking fault. In summary we present heteroepitaxially grown a-plane GaN without an evidence of basal plane stacking faults in X-ray diffraction measurements and luminescence spectra.

Molecular beam epitaxy of InP single junction and InP/In0.53Ga0.47As monolithically integrated tandem solar cells using solid phosphorous source material

International Nuclear Information System (INIS)

Delaney, A.; Chin, K.; Street, S.; Newman, F.; Aguilar, L.; Ignatiev, A.; Monier, C.; Velela, M.; Freundlich, A.

1998-01-01

This work reports the first InP solar cells, InP/In 0.53 Ga 0.47 As tandem solar cells and InP tunnel junctions to be grown using a solid phosphorous source cracker cell in a molecular beam epitaxy system. High p-type doping achieved with this system allowed for the development of InP tunnel junctions. These junctions which allow for improved current matching in subsequent monolithically integrated tandem devices also do not absorb photons which can be utilized in the InGaAs structure. Photocurrent spectral responses compared favorably to devices previously grown in a chemical beam epitaxy system. High resolution x-ray scans demonstrated good lattice matching between constituent parts of the tandem cell. AM0 efficiencies of both InP and InP/InGaAs tandem cells are reported

Electrical, optical, and structural properties of GaN films prepared by hydride vapor phase epitaxy

International Nuclear Information System (INIS)

Polyakov, A.Y.; Smirnov, N.B.; Yakimov, E.B.; Usikov, A.S.; Helava, H.; Shcherbachev, K.D.; Govorkov, A.V.; Makarov, Yu N.; Lee, In-Hwan

2014-01-01

Highlights: • GaN films are prepared by hydride vapor phase epitaxy (HVPE). • Residual donors and deep traps show a minimum density versus growth temperature. • This minimum is located close to the HVPE growth temperature of 950 °C. • Good crystalline GaN with residual donor density < 10 16 cm −3 can be grown at 950 °C. - Abstract: Two sets of undoped GaN films with the thickness of 10–20 μm were prepared by hydride vapor phase epitaxy (HVPE) and characterized by capacitance–voltage (C–V) profiling, microcathodoluminescence (MCL) spectra measurements, MCL imaging, electron beam induced current (EBIC) imaging, EBIC dependence on accelerating voltage, deep levels transient spectroscopy, high resolution X-ray diffraction measurements. The difference in growth conditions was mainly related to the lower (850 °C, group 1) or higher (950 °C, group 2) growth temperature. Both groups of samples showed similar crystalline quality with the dislocation density close to 10 8 cm −2 , but very different electrical and optical properties. In group 1 samples the residual donors concentration was ∼10 17 cm −3 or higher, the MCL spectra were dominated by the band-edge luminescence, and the diffusion length of charge carriers was close to 0.1 μm. Group 2 samples had a 2–4.5 μm thick highly resistive layer on top, for which MCL spectra were determined by green, yellow and red defect bands, and the diffusion length was 1.5 times higher than in group 1. We also present brief results of growth at the “standard” HVPE growth temperature of 1050 °C that show the presence of a minimum in the net donor concentration and deep traps density as a function of the growth temperature. Possible reasons for the observed results are discussed in terms of the electrical compensation of residual donors by deep traps

Impact of barrier thickness on transistor performance in AlN/GaN high electron mobility transistors grown on free-standing GaN substrates

International Nuclear Information System (INIS)

Deen, David A.; Storm, David F.; Meyer, David J.; Bass, Robert; Binari, Steven C.; Gougousi, Theodosia; Evans, Keith R.

2014-01-01

A series of six ultrathin AlN/GaN heterostructures with varied AlN thicknesses from 1.5–6 nm have been grown by molecular beam epitaxy on free-standing hydride vapor phase epitaxy GaN substrates. High electron mobility transistors (HEMTs) were fabricated from the set in order to assess the impact of barrier thickness and homo-epitaxial growth on transistor performance. Room temperature Hall characteristics revealed mobility of 1700 cm 2 /V s and sheet resistance of 130 Ω/□ for a 3 nm thick barrier, ranking amongst the lowest room-temperature sheet resistance values reported for a polarization-doped single heterostructure in the III-Nitride family. DC and small signal HEMT electrical characteristics from submicron gate length HEMTs further elucidated the effect of the AlN barrier thickness on device performance.

Impact of barrier thickness on transistor performance in AlN/GaN high electron mobility transistors grown on free-standing GaN substrates

Energy Technology Data Exchange (ETDEWEB)

Deen, David A., E-mail: david.deen@alumni.nd.edu; Storm, David F.; Meyer, David J.; Bass, Robert; Binari, Steven C. [Electronics Science and Technology Division, Naval Research Laboratory, Washington, DC 20375-5347 (United States); Gougousi, Theodosia [Physics Department, University of Maryland Baltimore County, Baltimore, Maryland 21250 (United States); Evans, Keith R. [Kyma Technologies, Raleigh, North Carolina 27617 (United States)

2014-09-01

A series of six ultrathin AlN/GaN heterostructures with varied AlN thicknesses from 1.5–6 nm have been grown by molecular beam epitaxy on free-standing hydride vapor phase epitaxy GaN substrates. High electron mobility transistors (HEMTs) were fabricated from the set in order to assess the impact of barrier thickness and homo-epitaxial growth on transistor performance. Room temperature Hall characteristics revealed mobility of 1700 cm{sup 2}/V s and sheet resistance of 130 Ω/□ for a 3 nm thick barrier, ranking amongst the lowest room-temperature sheet resistance values reported for a polarization-doped single heterostructure in the III-Nitride family. DC and small signal HEMT electrical characteristics from submicron gate length HEMTs further elucidated the effect of the AlN barrier thickness on device performance.

Sidewall GaAs tunnel junctions fabricated using molecular layer epitaxy

Directory of Open Access Journals (Sweden)

Takeo Ohno and Yutaka Oyama

2012-01-01

Full Text Available In this article we review the fundamental properties and applications of sidewall GaAs tunnel junctions. Heavily impurity-doped GaAs epitaxial layers were prepared using molecular layer epitaxy (MLE, in which intermittent injections of precursors in ultrahigh vacuum were applied, and sidewall tunnel junctions were fabricated using a combination of device mesa wet etching of the GaAs MLE layer and low-temperature area-selective regrowth. The fabricated tunnel junctions on the GaAs sidewall with normal mesa orientation showed a record peak current density of 35 000 A cm-2. They can potentially be used as terahertz devices such as a tunnel injection transit time effect diode or an ideal static induction transistor.

''Cube-on-hexagon'' orientation relationship for Fe on GaN(0001): The missing link in bcc/hcp epitaxy

International Nuclear Information System (INIS)

Gao Cunxu; Brandt, Oliver; Laehnemann, Jonas; Jahn, Uwe; Jenichen, Bernd; Schoenherr, Hans-Peter; Erwin, Steven C.

2010-01-01

We investigate, experimentally and theoretically, the epitaxy of body-centered-cubic Fe on hexagonal GaN. For growth on the Ga-polar GaN(0001) surface we find the well-known Pitsch-Schrader orientation relationship between Fe and GaN. On the N-polar GaN(0001) surface we observe coexistence between the familiar Burgers orientation and a new orientation in which the Fe(001) plane is parallel to GaN(0001). This 'cube-on-hexagon' orientation constitutes the high-symmetry link required for constructing a symmetry diagram for bcc/hcp systems in which all orientation relationships are connected by simple rotations.

Defect structure in m-plane GaN grown on LiAlO{sub 2} using metalorganic and hydride vapour phase epitaxy

Energy Technology Data Exchange (ETDEWEB)

Wernicke, Tim; Netzel, Carsten; Richter, Eberhard; Knauer, Arne; Brunner, Frank; Weyers, Markus [FBH Berlin (Germany); Mogliatenko, Anna; Neumann, Wolfgang [AG Kristallographie, Institut fuer Physik, HU Berlin (Germany); Kneissl, Michael [FBH Berlin (Germany); Institute of Solid State Physics, TU Berlin (Germany)

2008-07-01

The FWHM of symmetric (10 anti 10) XRD rocking curves of m-plane GaN grown on LiAlO{sub 2} is anisotropic. By investigating the microstructure with transmission electron microscopy (TEM) we identified basal plane stacking faults (BSF) and stacking mismatch boundaries (SMB) in the GaN layers. BSFs are aligned in-plane along the a-direction and therefore cause an anisotropic broadening of the FWHM{sub (10 anti 10)} with incidence along [0001]. SMBs have no preferential direction and hence result in an isotropic broadening of the FWHM{sub (10 anti 10)}. We observed that this anisotropy can be reduced by lowering the MOVPE growth temperature. We propose that the lowering of the growth temperature leads to a reduction of BSFs which is accompanied by an increase in SMBs. The MOVPE grown layers were used as templates for the growth of 200 {mu}m thick m-plane GaN layers by HVPE. During HVPE growth the LiAlO{sub 2} substrate thermally decomposed and peeled off after cool-down. On the surface a network of cracks not being aligned to crystallographic directions was found. The layers were not transparent probably due to metallic Ga inclusions and exhibited an asymmetric bow according to the lattice anisotropy of the (100) LiAlO{sub 2} surface.

Si Complies with GaN to Overcome Thermal Mismatches for the Heteroepitaxy of Thick GaN on Si.

Science.gov (United States)

Tanaka, Atsunori; Choi, Woojin; Chen, Renjie; Dayeh, Shadi A

2017-10-01

Heteroepitaxial growth of lattice mismatched materials has advanced through the epitaxy of thin coherently strained layers, the strain sharing in virtual and nanoscale substrates, and the growth of thick films with intermediate strain-relaxed buffer layers. However, the thermal mismatch is not completely resolved in highly mismatched systems such as in GaN-on-Si. Here, geometrical effects and surface faceting to dilate thermal stresses at the surface of selectively grown epitaxial GaN layers on Si are exploited. The growth of thick (19 µm), crack-free, and pure GaN layers on Si with the lowest threading dislocation density of 1.1 × 10 7 cm -2 achieved to date in GaN-on-Si is demonstrated. With these advances, the first vertical GaN metal-insulator-semiconductor field-effect transistors on Si substrates with low leakage currents and high on/off ratios paving the way for a cost-effective high power device paradigm on an Si CMOS platform are demonstrated. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Epitaxy of GaN on silicon-impact of symmetry and surface reconstruction

International Nuclear Information System (INIS)

Dadgar, A; Schulze, F; Wienecke, M; Gadanecz, A; Blaesing, J; Veit, P; Hempel, T; Diez, A; Christen, J; Krost, A

2007-01-01

GaN-on-silicon is a low-cost alternative to growth on sapphire or SiC. Today epitaxial growth is usually performed on Si(111), which has a threefold symmetry. The growth of single crystalline GaN on Si(001), the material of the complementary metal oxide semiconductor (CMOS) industry, is more difficult due to the fourfold symmetry of this Si surface leading to two differently aligned domains. We show that breaking the symmetry to achieve single crystalline growth can be performed, e.g. by off-oriented substrates to achieve single crystalline device quality GaN layers. Furthermore, an exotic Si orientation for GaN growth is Si(110), which we show is even better suited as compared to Si(111) for the growth of high quality GaN-on-silicon with a nearly threefold reduction in the full width at half maximum (FWHM) of the (1 1-bar 0 0)ω-scan. It is found that a twofold surface symmetry is in principal suitable for the growth of single crystalline GaN on Si

Junction Transport in Epitaxial Film Silicon Heterojunction Solar Cells: Preprint

Energy Technology Data Exchange (ETDEWEB)

Young, D. L.; Li, J. V.; Teplin, C. W.; Stradins, P.; Branz, H. M.

2011-07-01

We report our progress toward low-temperature HWCVD epitaxial film silicon solar cells on inexpensive seed layers, with a focus on the junction transport physics exhibited by our devices. Heterojunctions of i/p hydrogenated amorphous Si (a-Si) on our n-type epitaxial crystal Si on n++ Si wafers show space-charge-region recombination, tunneling or diffusive transport depending on both epitaxial Si quality and the applied forward voltage.

Photoluminescence of Mg-doped m-plane GaN grown by MOCVD on bulk GaN substrates

OpenAIRE

Monemar, Bo; Paskov, Plamen; Pozina, Galia; Hemmingsson, Carl; Bergman, Peder; Lindgren, David; Samuelson, Lars; Ni, Xianfeng; Morkoç, Hadis; Paskova, Tanya; Bi, Zhaoxia; Ohlsson, Jonas

2011-01-01

Photoluminescence (PL) properties are reported for a set of m-plane GaN films with Mg doping varied from mid 1018cm-3 to well above 1019 cm-3. The samples were grown with MOCVD at reduced pressure on low defect density m-plane bulk GaN templates. The sharp line near bandgap bound exciton (BE) spectra observed below 50 K, as well as the broader donor-acceptor pair (DAP) PL bands at 2.9 eV to 3.3 eV give evidence of several Mg related acceptors, similar to the case of c-plane GaN. The dependenc...

GaN Nanowire Arrays for High-Output Nanogenerators

KAUST Repository

Huang, Chi-Te

2010-04-07

Three-fold symmetrically distributed GaN nanowire (NW) arrays have been epitaxially grown on GaN/sapphire substrates. The GaN NW possesses a triangular cross section enclosed by (0001), (2112), and (2112) planes, and the angle between the GaN NW and the substrate surface is ∼62°. The GaN NW arrays produce negative output voltage pulses when scanned by a conductive atomic force microscope in contact mode. The average of piezoelectric output voltage was about -20 mV, while 5-10% of the NWs had piezoelectric output voltages exceeding -(0.15-0.35) V. The GaN NW arrays are highly stable and highly tolerate to moisture in the atmosphere. The GaN NW arrays demonstrate an outstanding potential to be utilized for piezoelectric energy generation with a performance probably better than that of ZnO NWs. © 2010 American Chemical Society.

Induced defects in neutron irradiated GaN single crystals

International Nuclear Information System (INIS)

Park, I. W.; Koh, E. K.; Kim, Y. M.; Choh, S. H.; Park, S. S.; Kim, B. G.; Sohn, J. M.

2005-01-01

The local structure of defects in undoped, Si-doped, and neutron irradiated free standing GaN bulk crystals, grown by hydride vapor phase epitaxy, has been investigated by employing Raman scattering and cathodoluminescence. The GaN samples were irradiated to a dose of 2 x 10 17 neutrons in an atomic reactor at Korea Atomic Energy Research Institute. There was no appreciable change in the Raman spectra for undoped GaN samples before and after neutron irradiation. However, a forbidden transition, A 1 (TO) mode, appeared for a neutron irradiated Si-doped GaN crystal. Cathodoluminescence spectrum for the neutron irradiated Si-doped GaN crystal became much more broadened than that for the unirradiated one. The experimental results reveal the generation of defects with locally deformed structure in the wurtzite Si-doped GaN single crystal

GaN and ZnO nanostructures

Energy Technology Data Exchange (ETDEWEB)

Fuendling, Soenke; Soekmen, Uensal; Behrends, Arne; Al-Suleiman, Mohamed Aid Mansur; Merzsch, Stephan; Li, Shunfeng; Bakin, Andrey; Wehmann, Hergo-Heinrich; Waag, Andreas [Institut fuer Halbleitertechnik, Technische Universitaet Braunschweig, Braunschweig (Germany); Laehnemann, Jonas; Jahn, Uwe; Trampert, Achim; Riechert, Henning [Paul-Drude-Institut fuer Festkoerperelektronik, Berlin (Germany)

2010-10-15

GaN and ZnO are both wide band gap semiconductors with interesting properties concerning optoelectronic and sensor device applications. Due to the lack or the high costs of native substrates, alternatives like sapphire, silicon, or silicon carbide are taken, but the resulting lattice and thermal mismatches lead to increased defect densities which reduce the material quality. In contrast, nanostructures with high aspect ratio have lower defect densities as compared to layers. In this work, we give an overview on our results achieved on both ZnO as well as GaN based nanorods. ZnO nanostructures were grown by a wet chemical approach as well as by VPT on different substrates - even on flexible polymers. To compare the growth results we analyzed the structures by XRD and PL and show possible device applications. The GaN nano- and microstructures were grown by metal organic vapor phase epitaxy either in a self-organized process or by selective area growth for a better control of shape and material composition. Finally we take a look onto possible device applications, presenting our attempts, e.g., to build LEDs based on GaN nanostructures. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

Transport and optical properties of c-axis oriented wedge shaped GaN nanowall network grown by molecular beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Bhasker, H. P.; Dhar, S. [Department of Physics, Indian Institute of Technology Bombay, Powai, Mumbai, Maharashtra-400076 (India); Thakur, Varun; Kesaria, Manoj; Shivaprasad, S. M. [Jawaharlal Nehru Centre for Advanced Scientific Research (JNCASR) Bangalore- 560064 (India)

2014-02-21

The transport and optical properties of wedge-shaped nanowall network of GaN grown spontaneously on cplane sapphire substrate by Plasma-Assisted Molecular Beam Epitaxy (PAMBE) show interesting behavior. The electron mobility at room temperature in these samples is found to be orders of magnitude higher than that of a continuous film. Our study reveals a strong correlation between the mobility and the band gap in these nanowall network samples. However, it is seen that when the thickness of the tips of the walls increases to an extent such that more than 70% of the film area is covered, it behaves close to a flat sample. In the sample with lower surface coverage (≈40% and ≈60%), it was observed that the conductivity, mobility as well as the band gap increase with the decrease in the average tip width of the walls. Photoluminescence (PL) experiments show a strong and broad band edge emission with a large (as high as ≈ 90 meV) blue shift, compared to that of a continuous film, suggesting a confinement of carriers on the top edges of the nanowalls. The PL peak width remains wide at all temperatures suggesting the existence of a high density of tail states at the band edge, which is further supported by the photoconductivity result. The high conductivity and mobility observed in these samples is believed to be due to a “dissipation less” transport of carriers, which are localized at the top edges (edge states) of the nanowalls.

Transport and optical properties of c-axis oriented wedge shaped GaN nanowall network grown by molecular beam epitaxy

International Nuclear Information System (INIS)

Bhasker, H. P.; Dhar, S.; Thakur, Varun; Kesaria, Manoj; Shivaprasad, S. M.

2014-01-01

The transport and optical properties of wedge-shaped nanowall network of GaN grown spontaneously on cplane sapphire substrate by Plasma-Assisted Molecular Beam Epitaxy (PAMBE) show interesting behavior. The electron mobility at room temperature in these samples is found to be orders of magnitude higher than that of a continuous film. Our study reveals a strong correlation between the mobility and the band gap in these nanowall network samples. However, it is seen that when the thickness of the tips of the walls increases to an extent such that more than 70% of the film area is covered, it behaves close to a flat sample. In the sample with lower surface coverage (≈40% and ≈60%), it was observed that the conductivity, mobility as well as the band gap increase with the decrease in the average tip width of the walls. Photoluminescence (PL) experiments show a strong and broad band edge emission with a large (as high as ≈ 90 meV) blue shift, compared to that of a continuous film, suggesting a confinement of carriers on the top edges of the nanowalls. The PL peak width remains wide at all temperatures suggesting the existence of a high density of tail states at the band edge, which is further supported by the photoconductivity result. The high conductivity and mobility observed in these samples is believed to be due to a “dissipation less” transport of carriers, which are localized at the top edges (edge states) of the nanowalls

Polarization Raman spectroscopy of GaN nanorod bundles

International Nuclear Information System (INIS)

Tite, T.; Lee, C. J.; Chang, Y.-M.

2010-01-01

We performed polarization Raman spectroscopy on single wurtzite GaN nanorod bundles grown by plasma-assisted molecular beam epitaxy. The obtained Raman spectra were compared with those of GaN epilayer. The spectral difference between the GaN nanorod bundles and epilayer reveals the relaxation of Raman selection rules in these GaN nanorod bundles. The deviation of polarization-dependent Raman spectroscopy from the prediction of Raman selection rules is attributed to both the orientation of the crystal axis with respect to the polarization vectors of incident and scattered light and the structural defects in the merging boundary of GaN nanorods. The presence of high defect density induced by local strain at the merging boundary was further confirmed by transmission electron microscopy. The averaged defect interspacing was estimated to be around 3 nm based on the spatial correlation model.

Transmission electron microscopy of GaN based, doped semiconductor heterostructures

Energy Technology Data Exchange (ETDEWEB)

Pretorius, A.

2006-07-01

This thesis addresses the analysis of GaN based heterostructures with transmission electron microscopy (TEM). Basic properties of the material of interest are introduced in chapter 2. These include the structural and optical properties as well as an introduction to the growth methods used for the samples analysed in this work. In chapter 3 a brief theoretical treatment of TEM is given. As one main topic of this work is the determination of the In concentration in InGaN islands using strain state analysis, a detailed description of the method is given. Chapter 4 describes the results obtained for pyramidal defects present in metalorganic vapour phase epitaxy grown GaN:Mg with high dopant concentration. Based on the experimental results and the well established knowledge that GaN of inverted polarity is present inside the pyramidal defects, a variety of basal plane inversion domain boundary models was set up. From these models, HRTEM images were simulated using the multislice approach, followed by a quantitative comparison to experimentally obtained HRTEM images. Another focus of this work is the analysis of In{sub x}Ga{sub 1-x}N islands grown on GaN presented in chapter 5. Following a literature survey which describes different methods used to obtain In{sub x}Ga{sub 1-x}N islands, the first topic is the distinction of In{sub x}Ga{sub 1-x}N islands and metal droplets, which can form during growth. This is followed by the experimental results of molecular beam epitaxy and metalorganic vapour phase epitaxy grown In{sub x}Ga{sub 1-x}N island and quantum dot samples. (orig.)

Understanding the Room Temperature Ferromagnetism in GaN Nanowires with Pd Doping

International Nuclear Information System (INIS)

Manna, S; De, S K

2011-01-01

We report the first synthesis and characterization of 4d transition metal palladium-doped GaN nanowires (NWs). Room temperature ferromagnetism has been observed in high quality Vapor Liquid Solid (VLS) epitaxy grown undoped n-type GaN nanowires. It was proposed that this type of magnetism is due to defects which are not observed in Bulk GaN because of large formation energy of defects in bulk GaN. Here we have successfully doped 4d transition metal Pd in GaN NWs. We find fairly strong and long-range ferromagnetic coupling between Pd substituted for Ga in GaN . The results suggest that 4d metals such as Pd may also be considered as candidates for ferromagnetic dopants in semiconductors.

Semi-polar GaN heteroepitaxy an high index Si-surfaces

Energy Technology Data Exchange (ETDEWEB)

Ravash, Roghaiyeh; Blaesing, Juergen; Hempel, Thomas; Dadgar, Armin; Christen, Juergen; Krost, Alois [Otto-von-Guericke-University Magdeburg, FNW/IEP/AHE, Magdeburg (Germany)

2011-07-01

Due to the lack of GaN homosubstrates, the growth of GaN-based devices is usually performed on heterosubstrates as sapphire or SiC. These substrates are either insulating or expensive, and both unavailable in large diameters. Meanwhile, silicon can meet the requirements for a low price and thermally well conducting substrate and also enabling the integration of optoelectronic devices with Si-based electronics. Up to now, the good matching of hexagonal GaN with the three-fold symmetry of Si(111) greatly promotes the c-axis orientated growth of GaN on this surface plane. A large spontaneous and piezoelectric polarization oriented along the c-axis exists in such hexagonal structure leading to low efficiencies for thick quantum wells. The attention to the growth of non-polar or semi-polar GaN based epitaxial structures has been increased recently because of reducing the effect of the polarization fields in these growth directions. Therefore we studied semi-polar GaN epilayers grown by metalorganic vapor phase epitaxy on silicon substrates with different orientations from Si(211) to Si(711). We observed that AlN seeding layer growth time play a significant role in obtaining the different GaN texture.

Optical properties of metastable shallow acceptors in Mg-doped GaN layers grown by metal-organic vapor phase epitaxy

OpenAIRE

Pozina, Galia; Hemmingsson, Carl; Bergman, Peder; Kawashima, T.; Amano, H.; Akasaki, I.; Usui, A.; Monemar, Bo

2010-01-01

GaN layers doped by Mg show a metastable behavior of the near-band-gap luminescence caused by electron irradiation or UV excitation. At low temperatures < 30 K the changes in luminescence are permanent. Heating to room temperature recovers the initial low temperature spectrum shape completely. Two acceptors are involved in the recombination process as confirmed by transient PL. In as-grown samples a possible candidate for the metastable acceptor is C-N, while after annealing a second m...

InGaN pn-junctions grown by PA-MBE: Material characterization and fabrication of nanocolumn electroluminescent devices

Science.gov (United States)

Gherasoiu, I.; Yu, K. M.; Reichertz, L.; Walukiewicz, W.

2015-09-01

PN junctions are basic building blocks of many electronic devices and their performance depends on the structural properties of the component layers and on the type and the amount of the doping impurities incorporated. Magnesium is the common p-type dopant for nitride semiconductors while silicon and more recently germanium are the n-dopants of choice. In this paper, therefore we analyze the quantitative limits for Mg and Ge incorporation on GaN and InGaN with high In content. We also discuss the challenges posed by the growth and characterization of InGaN pn-junctions and we discuss the properties of large area, long wavelength nanocolumn LEDs grown on silicon (1 1 1) by PA-MBE.

Effects of material growth technique and Mg doping on Er3+ photoluminescence in Er-implanted GaN

International Nuclear Information System (INIS)

Kim, S.; Henry, R. L.; Wickenden, A. E.; Koleske, D. D.; Rhee, S. J.; White, J. O.; Myoung, J. M.; Kim, K.; Li, X.; Coleman, J. J.

2001-01-01

Photoluminescence (PL) and photoluminescence excitation (PLE) spectroscopies have been carried out at 6 K on the ∼1540 nm 4 I 13/2 - 4 I 15/2 emissions of Er 3+ in Er-implanted and annealed GaN. These studies revealed the existence of multiple Er 3+ centers and associated PL spectra in Er-implanted GaN films grown by metalorganic chemical vapor deposition, hydride vapor phase epitaxy, and molecular beam epitaxy. The results demonstrate that the multiple Er 3+ PL centers and below-gap defect-related absorption bands by which they are selectively excited are universal features of Er-implanted GaN grown by different techniques. It is suggested that implantation-induced defects common to all the GaN samples are responsible for the Er site distortions that give rise to the distinctive, selectively excited Er 3+ PL spectra. The investigations of selectively excited Er 3+ PL and PLE spectra have also been extended to Er-implanted samples of Mg-doped GaN grown by various techniques. In each of these samples, the so-called violet-pumped Er 3+ PL band and its associated broad violet PLE band are significantly enhanced relative to the PL and PLE of the other selectively excited Er 3+ PL centers. More importantly, the violet-pumped Er 3+ PL spectrum dominates the above-gap excited Er 3+ PL spectrum of Er-implanted Mg-doped GaN, whereas it was unobservable under above-gap excitation in Er-implanted undoped GaN. These results confirm the hypothesis that appropriate codopants can increase the efficiency of trap-mediated above-gap excitation of Er 3+ emission in Er-implanted GaN. [copyright] 2001 American Institute of Physics

Thermodynamic analysis of trimethylgallium decomposition during GaN metal organic vapor phase epitaxy

Science.gov (United States)

Sekiguchi, Kazuki; Shirakawa, Hiroki; Chokawa, Kenta; Araidai, Masaaki; Kangawa, Yoshihiro; Kakimoto, Koichi; Shiraishi, Kenji

2018-04-01

We analyzed the decomposition of Ga(CH3)3 (TMG) during the metal organic vapor phase epitaxy (MOVPE) of GaN on the basis of first-principles calculations and thermodynamic analysis. We performed activation energy calculations of TMG decomposition and determined the main reaction processes of TMG during GaN MOVPE. We found that TMG reacts with the H2 carrier gas and that (CH3)2GaH is generated after the desorption of the methyl group. Next, (CH3)2GaH decomposes into (CH3)GaH2 and this decomposes into GaH3. Finally, GaH3 becomes GaH. In the MOVPE growth of GaN, TMG decomposes into GaH by the successive desorption of its methyl groups. The results presented here concur with recent high-resolution mass spectroscopy results.

Ethanol surface chemistry on MBE-grown GaN(0001), GaOx/GaN(0001), and Ga2O3(2¯01).

Science.gov (United States)

Kollmannsberger, Sebastian L; Walenta, Constantin A; Winnerl, Andrea; Knoller, Fabian; Pereira, Rui N; Tschurl, Martin; Stutzmann, Martin; Heiz, Ueli

2017-09-28

In this work, ethanol is used as a chemical probe to study the passivation of molecular beam epitaxy-grown GaN(0001) by surface oxidation. With a high degree of oxidation, no reaction from ethanol to acetaldehyde in temperature-programmed desorption experiments is observed. The acetaldehyde formation is attributed to a mechanism based on α-H abstraction from the dissociatively bound alcohol molecule. The reactivity is related to negatively charged surface states, which are removed upon oxidation of the GaN(0001) surface. This is compared with the Ga 2 O 3 (2¯01) single crystal surface, which is found to be inert for the acetaldehyde production. These results offer a toolbox to explore the surface chemistry of nitrides and oxynitrides on an atomic scale and relate their intrinsic activity to systems under ambient atmosphere.

Selective-area growth of GaN nanowires on SiO{sub 2}-masked Si (111) substrates by molecular beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Kruse, J. E.; Doundoulakis, G. [Department of Physics, University of Crete, P. O. Box 2208, 71003 Heraklion (Greece); Institute of Electronic Structure and Laser, Foundation for Research and Technology–Hellas, N. Plastira 100, 70013 Heraklion (Greece); Lymperakis, L. [Max-Planck-Institut für Eisenforschung, Max-Planck-Straße 1, 40237 Düsseldorf (Germany); Eftychis, S.; Georgakilas, A., E-mail: alexandr@physics.uoc.gr [Department of Physics, University of Crete, P. O. Box 2208, 71003 Heraklion (Greece); Adikimenakis, A.; Tsagaraki, K.; Androulidaki, M.; Konstantinidis, G. [Institute of Electronic Structure and Laser, Foundation for Research and Technology–Hellas, N. Plastira 100, 70013 Heraklion (Greece); Olziersky, A.; Dimitrakis, P.; Ioannou-Sougleridis, V.; Normand, P. [Institute of Nanoscience and Nanotechnology, NCSR Demokritos, Patriarchou Grigoriou and Neapoleos 27, 15310 Aghia Paraskevi, Athens (Greece); Koukoula, T.; Kehagias, Th.; Komninou, Ph. [Department of Physics, Aristotle University of Thessaloniki, 54124 Thessaloniki (Greece)

2016-06-14

We analyze a method to selectively grow straight, vertical gallium nitride nanowires by plasma-assisted molecular beam epitaxy (MBE) at sites specified by a silicon oxide mask, which is thermally grown on silicon (111) substrates and patterned by electron-beam lithography and reactive-ion etching. The investigated method requires only one single molecular beam epitaxy MBE growth process, i.e., the SiO{sub 2} mask is formed on silicon instead of on a previously grown GaN or AlN buffer layer. We present a systematic and analytical study involving various mask patterns, characterization by scanning electron microscopy, transmission electron microscopy, and photoluminescence spectroscopy, as well as numerical simulations, to evaluate how the dimensions (window diameter and spacing) of the mask affect the distribution of the nanowires, their morphology, and alignment, as well as their photonic properties. Capabilities and limitations for this method of selective-area growth of nanowires have been identified. A window diameter less than 50 nm and a window spacing larger than 500 nm can provide single nanowire nucleation in nearly all mask windows. The results are consistent with a Ga diffusion length on the silicon dioxide surface in the order of approximately 1 μm.

Laboratory Instrumentation Design Research for Scalable Next Generation Epitaxy: Non-Equilibrium Wide Application Epitaxial Patterning by Intelligent Control (NEW-EPIC). Volume 1. 3D Composition/Doping Control via Micromiror Patterned Deep UV Photodesorption: Revolutionary in situ Characterization/Control

Science.gov (United States)

2009-02-19

34 (to be submitted to APL) " Positron Annihilation Spectroscopy of Annealed and As-grown Be-doped GaN" (to be submitted to APL - delayed by the...WIDE APPLICATION EPITAXIAL PATTERNING BY INTELLIGENT CONTROL (NEW-EPIC) 6. AUTHOR(S) DRS DOOLITTILE, FRAZIER, BURNHAM, PRITCHETT, BILLINGSLEY...NEXT GENERATION EPITAXY: NON-EQUILIBRIUM WIDE APPLICATION EPITAXIAL PATTERNING BY INTELLIGENT CONTROL (NEW-EPIC) VOLUME I 3D COMPOSITION/DOPING

Valence band offset of β-Ga2O3/wurtzite GaN heterostructure measured by X-ray photoelectron spectroscopy.

Science.gov (United States)

Wei, Wei; Qin, Zhixin; Fan, Shunfei; Li, Zhiwei; Shi, Kai; Zhu, Qinsheng; Zhang, Guoyi

2012-10-10

A sample of the β-Ga2O3/wurtzite GaN heterostructure has been grown by dry thermal oxidation of GaN on a sapphire substrate. X-ray diffraction measurements show that the β-Ga2O3 layer was formed epitaxially on GaN. The valence band offset of the β-Ga2O3/wurtzite GaN heterostructure is measured by X-ray photoelectron spectroscopy. It is demonstrated that the valence band of the β-Ga2O3/GaN structure is 1.40 ± 0.08 eV.

Synthesis of p-type GaN nanowires.

Science.gov (United States)

Kim, Sung Wook; Park, Youn Ho; Kim, Ilsoo; Park, Tae-Eon; Kwon, Byoung Wook; Choi, Won Kook; Choi, Heon-Jin

2013-09-21

GaN has been utilized in optoelectronics for two decades. However, p-type doping still remains crucial for realization of high performance GaN optoelectronics. Though Mg has been used as a p-dopant, its efficiency is low due to the formation of Mg-H complexes and/or structural defects in the course of doping. As a potential alternative p-type dopant, Cu has been recognized as an acceptor impurity for GaN. Herein, we report the fabrication of Cu-doped GaN nanowires (Cu:GaN NWs) and their p-type characteristics. The NWs were grown vertically via a vapor-liquid-solid (VLS) mechanism using a Au/Ni catalyst. Electrical characterization using a nanowire-field effect transistor (NW-FET) showed that the NWs exhibited n-type characteristics. However, with further annealing, the NWs showed p-type characteristics. A homo-junction structure (consisting of annealed Cu:GaN NW/n-type GaN thin film) exhibited p-n junction characteristics. A hybrid organic light emitting diode (OLED) employing the annealed Cu:GaN NWs as a hole injection layer (HIL) also demonstrated current injected luminescence. These results suggest that Cu can be used as a p-type dopant for GaN NWs.

MOVPE of InN films on GaN templates grown on sapphire and silicon(111) substrates

International Nuclear Information System (INIS)

Jamil, Muhammad; Arif, Ronald A.; Ee, Yik-Khoon; Tong, Hua; Tansu, Nelson; Higgins, John B.

2008-01-01

This paper reports the study of MOVPE of InN on GaN templates grown on sapphire and silicon(111) substrates. Thermodynamic analysis of MOVPE of InN performed using NH 3 as nitrogen source and the experimental findings support the droplet-free epitaxial growth of InN under high V/III ratios of input precursors. At a growth pressure of 500 Torr, the optimum growth temperature and V/III ratio of the InN film are 575-650 C and >3 x 10 5 , respectively. The surface RMS roughness of InN film grown GaN/sapphire template is ∝0.3 nm on 2 μm x 2 μm area, while the RMS roughness of the InN film grown on GaN/Si(111) templates is found as ∝0.7 nm. The X-ray diffraction (XRD) measurement reveals the (0002) texture of the InN film on GaN/sapphire template with a FWHM of 281 arcsec of the InN(0002) ω rocking curve. For the film grown on GaN/Si template under identical growth conditions, the XRD measurements show the presence of metallic In, in addition to the (0002) orientation of InN layer. (copyright 2008 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Epitaxial-graphene/graphene-oxide junction: an essential step towards epitaxial graphene electronics.

Science.gov (United States)

Wu, Xiaosong; Sprinkle, Mike; Li, Xuebin; Ming, Fan; Berger, Claire; de Heer, Walt A

2008-07-11

Graphene-oxide (GO) flakes have been deposited to bridge the gap between two epitaxial-graphene electrodes to produce all-graphene devices. Electrical measurements indicate the presence of Schottky barriers at the graphene/graphene-oxide junctions, as a consequence of the band gap in GO. The barrier height is found to be about 0.7 eV, and is reduced after annealing at 180 degrees C, implying that the gap can be tuned by changing the degree of oxidation. A lower limit of the GO mobility was found to be 850 cm2/V s, rivaling silicon. In situ local oxidation of patterned epitaxial graphene has been achieved.

Tolerance of GaAs as an original substrate for HVPE growth of free standing GaN

Science.gov (United States)

Suzuki, Mio; Sato, T.; Suemasu, T.; Hasegawa, F.

2004-09-01

In order to investigate possibility of thick GaN growth on a GaAs substrate by halide vapar phase epitaxy (HVPE), GaN was grown on GaAs(111)/Ti wafer with Ti deposited by E-gun. It was found that surface treatment of the GaAs substrate by HF solution deteriorated greatly the tolerence of GaAs and that Ti can protected GaAs from erosion by NH3. By depositing Ti on GaAs(111)A surface, a millor-like GaN layer could be grown at 1000 °C for 1 hour without serious deterioration of the original GaAs substrate. By increasing the growth rate, a thick free standing GaN will be obtained with GaAs as an original substrate in near future.

Effect of the Ti-Nanolayer Thickness on the Self-Lift-off of Thick GaN Epitaxial Layers

International Nuclear Information System (INIS)

Yugov, A. A.; Malahov, S. S.; Donskov, A. A.; Duhnovskii, M. P.; Knyazev, S. N.; Kozlova, Yu. P.; Yugova, T. G.; Belogorokhov, I. A.

2016-01-01

The effect of the type of substrate, sapphire substrate (c- and r-orientation) or GaN/Al_2O_3 template (c- and r-orientations), on the nitridation of an amorphous titanium nanolayer is shown. The effect of the titanium-nanolayer thickness on thick GaN epitaxial layer self-separation from the substrate is revealed. The titanium-nanolayer thickness at which thick GaN layer is reproducibly self-separated is within 20–40 nm.

Ethanol surface chemistry on MBE-grown GaN(0001), GaOx/GaN(0001), and Ga2O3(2 \\xAF 01 )

Science.gov (United States)

Kollmannsberger, Sebastian L.; Walenta, Constantin A.; Winnerl, Andrea; Knoller, Fabian; Pereira, Rui N.; Tschurl, Martin; Stutzmann, Martin; Heiz, Ueli

2017-09-01

In this work, ethanol is used as a chemical probe to study the passivation of molecular beam epitaxy-grown GaN(0001) by surface oxidation. With a high degree of oxidation, no reaction from ethanol to acetaldehyde in temperature-programmed desorption experiments is observed. The acetaldehyde formation is attributed to a mechanism based on α -H abstraction from the dissociatively bound alcohol molecule. The reactivity is related to negatively charged surface states, which are removed upon oxidation of the GaN(0001) surface. This is compared with the Ga2O3(2 ¯ 01 ) single crystal surface, which is found to be inert for the acetaldehyde production. These results offer a toolbox to explore the surface chemistry of nitrides and oxynitrides on an atomic scale and relate their intrinsic activity to systems under ambient atmosphere.

Effect of the nand p-type Si(100) substrates with a SiC buffer layer on the growth mechanism and structure of epitaxial layers of semipolar AlN and GaN

Science.gov (United States)

Bessolov, V. N.; Grashchenko, A. S.; Konenkova, E. V.; Myasoedov, A. V.; Osipov, A. V.; Red'kov, A. V.; Rodin, S. N.; Rubets, V. P.; Kukushkin, S. A.

2015-10-01

A new effect of the n-and p-type doping of the Si(100) substrate with a SiC film on the growth mechanism and structure of AlN and GaN epitaxial layers has been revealed. It has been experimentally shown that the mechanism of AlN and GaN layer growth on the surface of a SiC layer synthesized by substituting atoms on n- and p-Si substrates is fundamentally different. It has been found that semipolar AlN and GaN layers on the SiC/Si(100) surface grow in the epitaxial and polycrystalline structures on p-Si and n-Si substrates, respectively. A new method for synthesizing epitaxial semipolar AlN and GaN layers by chloride-hydride epitaxy on silicon substrates has been proposed.

Above room-temperature ferromagnetism of Mn delta-doped GaN nanorods

International Nuclear Information System (INIS)

Lin, Y. T.; Wadekar, P. V.; Kao, H. S.; Chen, T. H.; Chen, Q. Y.; Tu, L. W.; Huang, H. C.; Ho, N. J.

2014-01-01

One-dimensional nitride based diluted magnetic semiconductors were grown by plasma-assisted molecular beam epitaxy. Delta-doping technique was adopted to dope GaN nanorods with Mn. The structural and magnetic properties were investigated. The GaMnN nanorods with a single crystalline structure and with Ga sites substituted by Mn atoms were verified by high-resolution x-ray diffraction and Raman scattering, respectively. Secondary phases were not observed by high-resolution x-ray diffraction and high-resolution transmission electron microscopy. In addition, the magnetic hysteresis curves show that the Mn delta-doped GaN nanorods are ferromagnetic above room temperature. The magnetization with magnetic field perpendicular to GaN c-axis saturates easier than the one with field parallel to GaN c-axis

The Growth of GaN on Si by the Beam Flux Modulation

International Nuclear Information System (INIS)

Roh, C. H.; Ha, M. W.; Song, H. J.; Choi, H. G.; Lee, J. H.; Ra, Y. W.; Hahn, C. K.

2011-01-01

AlGaN/GaN HEMT structure was grown on Si (111) substrate by plasma-assisted molecular beam epitaxy (PA-MBE) using a beam flux modulation methods. In this result, it was verified that the propagation of treading dislocation (TD) due to N-rich GaN layer was effectively suppressed.

Polarity-inverted lateral overgrowth and selective wet-etching and regrowth (PILOSWER) of GaN.

Science.gov (United States)

Jang, Dongsoo; Jue, Miyeon; Kim, Donghoi; Kim, Hwa Seob; Lee, Hyunkyu; Kim, Chinkyo

2018-03-07

On an SiO 2 -patterned c-plane sapphire substrate, GaN domains were grown with their polarity controlled in accordance with the pattern. While N-polar GaN was grown on hexagonally arranged circular openings, Ga-polar GaN was laterally overgrown on mask regions due to polarity inversion occurring at the boundary of the circular openings. After etching of N-polar GaN on the circular openings by H 3 PO 4 , this template was coated with 40-nm Si by sputtering and was slightly etched by KOH. After slight etching, a thin layer of Si left on the circular openings of sapphire,but not on GaN, was oxidized during thermal annealing and served as a dielectric mask during subsequent regrowth. Thus, the subsequent growth of GaN was made only on the existing Ga-polar GaN domains, not on the circular openings of the sapphire substrate. Transmission electron microscopy analysis revealed no sign of threading dislocations in this film. This approach may help fabricating an unholed and merged GaN film physically attached to but epitaxially separated from the SiO 2 -patterned sapphire.

Tunnel currents produced by defects in p-n junctions of GaAs grown on vapor phase

International Nuclear Information System (INIS)

Barrales Guadarrama, V R; Rodríguez Rodriguez, E M; Barrales Guadarrama, R; Reyes Ayala, N

2017-01-01

With the purpose of assessing if the epitaxy on vapor phase technique “Close Space Vapor Deposition (CSVT)” is capable of produce thin films with adequate properties in order to manufacture p-n junctions, a study of invert and direct current was developed, in a temperature range of 94K to 293K, to junctions p-n of GaAs grown through the technique CSVT. It is shown that the dominant current, within the range 10 -7 to 10 -2 A, is consistent with a currents model of the type of internal emission form field, which shows these currents are due to the presence of localized states in the band gap. (paper)

Backward diodes using heavily Mg-doped GaN growth by ammonia molecular-beam epitaxy

Science.gov (United States)

Okumura, Hironori; Martin, Denis; Malinverni, Marco; Grandjean, Nicolas

2016-02-01

We grew heavily Mg-doped GaN using ammonia molecular-beam epitaxy. The use of low growth temperature (740 °C) allows decreasing the incorporation of donor-like defects (p-type doping compensation. As a result, a net acceptor concentration of 7 × 1019 cm-3 was achieved, and the hole concentration measured by Hall effect was as high as 2 × 1019 cm-3 at room temperature. Using such a high Mg doping level, we fabricated GaN backward diodes without polarization-assisted tunneling. The backward diodes exhibited a tunneling-current density of 225 A/cm2 at a reverse bias of -1 V at room temperature.

Characteristics of AlN/GaN nanowire Bragg mirror grown on (001) silicon by molecular beam epitaxy

KAUST Repository

Heo, Junseok

2013-10-01

GaN nanowires containing AlN/GaN distributed Bragg reflector (DBR) heterostructures have been grown on (001) silicon substrate by molecular beam epitaxy. A peak reflectance of 70% with normal incidence at 560 nm is derived from angle resolved reflectance measurements on the as-grown nanowire DBR array. The measured peak reflectance wavelength is significantly blue-shifted from the ideal calculated value. The discrepancy is explained by investigating the reflectance of the nanoscale DBRs with a finite difference time domain technique. Ensemble nanowire microcavities with In0.3Ga 0.7N nanowires clad by AlN/GaN DBRs have also been characterized. Room temperature emission from the microcavity exhibits considerable linewidth narrowing compared to that measured for unclad In0.3Ga0.7N nanowires. The resonant emission is characterized by a peak wavelength and linewidth of 575 nm and 39 nm, respectively. © 2013 AIP Publishing LLC.

Step-flow growth mode instability of N-polar GaN under N-excess

International Nuclear Information System (INIS)

Chèze, C.; Sawicka, M.; Siekacz, M.; Łucznik, B.; Boćkowski, M.; Skierbiszewski, C.; Turski, H.; Cywiński, G.; Smalc-Koziorowska, J.; Weyher, J. L.; Kryśko, M.

2013-01-01

GaN layers were grown on N-polar GaN substrates by plasma-assisted molecular beam epitaxy under different III/V ratios. Ga-rich conditions assure step-flow growth with atomically flat surface covered by doubly-bunched steps, as for Ga-polar GaN. Growth under N-excess however leads to an unstable step-flow morphology. Particularly, for substrates slightly miscut towards , interlacing fingers are covered by atomic steps pinned on both sides by small hexagonal pits. In contrast, a three-dimensional island morphology is observed on the Ga-polar equivalent sample. We attribute this result to lower diffusion barriers on N-polar compared to Ga-polar GaN under N-rich conditions

The impact of SiC substrate treatment on the heteroepitaxial growth of GaN by plasma assisted MBE

Energy Technology Data Exchange (ETDEWEB)

Brown, A.S.; Kim, T.H.; Choi, S.; Morse, M.; Wu, P. [Department of Electrical and Computer Engineering, Duke University, Durham, NC 27709 (United States); Losurdo, M.; Giangregorio, M.M.; Capezzuto, P.; Bruno, G. [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR, and INSTM via Orabona 4 -70126, Bari (Italy)

2005-11-01

We report on the impact of the preparation of the Si-face 4H-SiC(0001){sub Si} substrate using a Ga flash-off process on the epitaxial growth of GaN by plasma-assisted molecular beam epitaxy. The nucleation, as well as the resultant structural and morphological properties of GaN grown directly on 4H-SiC(0001){sub Si} are strongly influenced by the chemical and morphological modifications of the SiC surface induced by the Ga flash-off process. Herein we describe the impact of the specific concentration of Ga incident on the surface (quantified in terms of monolayer (ML) coverage): of 0.5 ML, 1ML and 2ML. The residual oxygen at the SiC surface, unintentional SiC nitridation and the formation of cubic GaN grains during the initial nucleation stage, are all reduced when a 2 ML Ga flash is used. All of the above factors result in structural improvement of the GaN epitaxial layers. The correlation between the SiC surface modification, the initial nucleation stage, and the GaN epitaxial layer structural quality has been articulated using x-ray photoelectron spectroscopy, X-ray diffraction, atomic force microscopy and spectroscopic ellipsometry data. (copyright 2005 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Hydride vapor phase epitaxy growth of GaN, InGaN, ScN, and ScAIN

NARCIS (Netherlands)

Bohnen, T.

2010-01-01

Chemical vapor deposition (CVD); hydride vapor phase epitaxy (HVPE); gallium nitride (GaN); indium gallium nitride (InGaN); scandium nitride (ScN); scandium aluminum nitride (ScAlN); semiconductors; thin films; nanowires; III nitrides; crystal growth - We studied the HVPE growth of different III

As-grown deep-level defects in n-GaN grown by metal-organic chemical vapor deposition on freestanding GaN

International Nuclear Information System (INIS)

Chen Shang; Ishikawa, Kenji; Hori, Masaru; Honda, Unhi; Shibata, Tatsunari; Matsumura, Toshiya; Tokuda, Yutaka; Ueda, Hiroyuki; Uesugi, Tsutomu; Kachi, Tetsu

2012-01-01

Traps of energy levels E c -0.26 and E c -0.61 eV have been identified as as-grown traps in n-GaN grown by metal-organic chemical vapor deposition by using deep level transient spectroscopy of the Schottky contacts fabricated by resistive evaporation. The additional traps of E c -0.13 and E c -0.65 eV have been observed in samples whose contacts are deposited by electron-beam evaporation. An increase in concentration of the E c -0.13 and E c -0.65 eV traps when approaching the interface between the contact and the GaN film supports our argument that these traps are induced by electron-beam irradiation. Conversely, the depth profiles of as-grown traps show different profiles between several samples with increased or uniform distribution in the near surface below 50 nm. Similar profiles are observed in GaN grown on a sapphire substrate. We conclude that the growth process causes these large concentrations of as-grown traps in the near-surface region. It is speculated that the finishing step in the growth process should be an essential issue in the investigation of the surface state of GaN.

Undoped p-type GaN1-xSbx alloys: Effects of annealing

Science.gov (United States)

Segercrantz, N.; Baumgartner, Y.; Ting, M.; Yu, K. M.; Mao, S. S.; Sarney, W. L.; Svensson, S. P.; Walukiewicz, W.

2016-12-01

We report p-type behavior for undoped GaN1-xSbx alloys with x ≥ 0.06 grown by molecular beam epitaxy at low temperatures (≤400 °C). Rapid thermal annealing of the GaN1-xSbx films at temperatures >400 °C is shown to generate hole concentrations greater than 1019 cm-3, an order of magnitude higher than typical p-type GaN achieved by Mg doping. The p-type conductivity is attributed to a large upward shift of the valence band edge resulting from the band anticrossing interaction between localized Sb levels and extended states of the host matrix.

Growth kinetics and mass transport mechanisms of GaN columns by selective area metal organic vapor phase epitaxy

Science.gov (United States)

Wang, Xue; Hartmann, Jana; Mandl, Martin; Sadat Mohajerani, Matin; Wehmann, Hergo-H.; Strassburg, Martin; Waag, Andreas

2014-04-01

Three-dimensional GaN columns recently have attracted a lot of attention as the potential basis for core-shell light emitting diodes for future solid state lighting. In this study, the fundamental insights into growth kinetics and mass transport mechanisms of N-polar GaN columns during selective area metal organic vapor phase epitaxy on patterned SiOx/sapphire templates are systematically investigated using various pitch of apertures, growth time, and silane flow. Species impingement fluxes on the top surface of columns Jtop and on their sidewall Jsw, as well as, the diffusion flux from the substrate Jsub contribute to the growth of the GaN columns. The vertical and lateral growth rates devoted by Jtop, Jsw and Jsub are estimated quantitatively. The diffusion length of species on the SiOx mask surface λsub as well as on the sidewall surfaces of the 3D columns λsw are determined. The influences of silane on the growth kinetics are discussed. A growth model is developed for this selective area metal organic vapor phase epitaxy processing.

Tolerance of GaAs as an original substrate for HVPE growth of free standing GaN

Energy Technology Data Exchange (ETDEWEB)

Suzuki, Mio; Sato, T.; Suemasu, T.; Hasegawa, F. [University of Tsukuba, Institute of Applied Physics, Tsukuba, Ibaraki 305-8573 (Japan)

2004-09-01

In order to investigate possibility of thick GaN growth on a GaAs substrate by halide vapar phase epitaxy (HVPE), GaN was grown on GaAs(111)/Ti wafer with Ti deposited by E-gun. It was found that surface treatment of the GaAs substrate by HF solution deteriorated greatly the tolerance of GaAs and that Ti can protected GaAs from erosion by NH{sub 3}. By depositing Ti on GaAs(111)A surface, a mirror-like GaN layer could be grown at 1000 C for 1 hour without serious deterioration of the original GaAs substrate. By increasing the growth rate, a thick free standing GaN will be obtained with GaAs as an original substrate in near future. (copyright 2004 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Surfactant effects of indium on cracking in AlN/GaN distributed Bragg reflectors grown via metal organic vapor phase epitaxy

Science.gov (United States)

Rodak, L. E.; Miller, C. M.; Korakakis, D.

2011-01-01

Aluminum Nitride (AlN) and Gallium Nitride (GaN) superlattice structures are often characterized by a network of cracks resulting from the large lattice mismatch and difference in thermal expansion coefficients, especially as the thickness of the layers increases. This work investigates the influence of indium as a surfactant on strain and cracking in AlN/GaN DBRs grown via Metal Organic Vapor Phase Epitaxy (MOVPE). DBRs with peak reflectivities ranging from 465 nm to 540 nm were grown and indium was introduced during the growth of the AlN layer. Image processing techniques were used to quantify the crack length per square millimeter and it was observed that indium has a significant effect on the crack formation and reduced the total crack length in these structures by a factor of two.

Viability and proliferation of endothelial cells upon exposure to GaN nanoparticles.

Science.gov (United States)

Braniste, Tudor; Tiginyanu, Ion; Horvath, Tibor; Raevschi, Simion; Cebotari, Serghei; Lux, Marco; Haverich, Axel; Hilfiker, Andres

2016-01-01

Nanotechnology is a rapidly growing and promising field of interest in medicine; however, nanoparticle-cell interactions are not yet fully understood. The goal of this work was to examine the interaction between endothelial cells and gallium nitride (GaN) semiconductor nanoparticles. Cellular viability, adhesion, proliferation, and uptake of nanoparticles by endothelial cells were investigated. The effect of free GaN nanoparticles versus the effect of growing endothelial cells on GaN functionalized surfaces was examined. To functionalize surfaces with GaN, GaN nanoparticles were synthesized on a sacrificial layer of zinc oxide (ZnO) nanoparticles using hydride vapor phase epitaxy. The uptake of GaN nanoparticles by porcine endothelial cells was strongly dependent upon whether they were fixed to the substrate surface or free floating in the medium. The endothelial cells grown on surfaces functionalized with GaN nanoparticles demonstrated excellent adhesion and proliferation, suggesting good biocompatibility of the nanostructured GaN.

Study of Charge Carrier Transport in GaN Sensors

Science.gov (United States)

Gaubas, Eugenijus; Ceponis, Tomas; Kuokstis, Edmundas; Meskauskaite, Dovile; Pavlov, Jevgenij; Reklaitis, Ignas

2016-01-01

Capacitor and Schottky diode sensors were fabricated on GaN material grown by hydride vapor phase epitaxy and metal-organic chemical vapor deposition techniques using plasma etching and metal deposition. The operational characteristics of these devices have been investigated by profiling current transients and by comparing the experimental regimes of the perpendicular and parallel injection of excess carrier domains. Profiling of the carrier injection location allows for the separation of the bipolar and the monopolar charge drift components. Carrier mobility values attributed to the hydride vapor phase epitaxy (HVPE) GaN material have been estimated as μe = 1000 ± 200 cm2/Vs for electrons, and μh = 400 ± 80 cm2/Vs for holes, respectively. Current transients under injection of the localized and bulk packets of excess carriers have been examined in order to determine the surface charge formation and polarization effects. PMID:28773418

Investigation of aluminium ohmic contacts to n-type GaN grown by molecular beam epitaxy

Science.gov (United States)

Kribes, Y.; Harrison, I.; Tuck, B.; Kim, K. S.; Cheng, T. S.; Foxon, C. T.

1997-11-01

Using epi-layers of different doping concentrations, we have investigated aluminium contacts on n-type gallium nitride grown by plasma source molecular beam epitaxy. To achieve repeatable and reliable results it was found that the semiconductor needed to be etched in aqua-regia before the deposition of the contact metallization. Scanning electron micrographs of the semiconductor surface show a deterioration of the semiconductor surface on etching. The specific contact resistivity of the etched samples were, however, superior. Annealing the contacts at 0268-1242/12/11/030/img9 produced contacts with the lowest specific contact resistance of 0268-1242/12/11/030/img10. The long-term aging of these contacts was also investigated. The contacts and the sheet resistance were both found to deteriorate over a three-month period.

Increased p-type conductivity through use of an indium surfactant in the growth of Mg-doped GaN

Science.gov (United States)

Kyle, Erin C. H.; Kaun, Stephen W.; Young, Erin C.; Speck, James S.

2015-06-01

We have examined the effect of an indium surfactant on the growth of p-type GaN by ammonia-based molecular beam epitaxy. p-type GaN was grown at temperatures ranging from 700 to 780 °C with and without an indium surfactant. The Mg concentration in all films in this study was 4.5-6 × 1019 cm-3 as measured by secondary ion mass spectroscopy. All p-type GaN films grown with an indium surfactant had higher p-type conductivities and higher hole concentrations than similar films grown without an indium surfactant. The lowest p-type GaN room temperature resistivity was 0.59 Ω-cm, and the highest room temperature carrier concentration was 1.6 × 1018 cm-3. Fits of the temperature-dependent carrier concentration data showed a one to two order of magnitude lower unintentional compensating defect concentration in samples grown with the indium surfactant. Samples grown at higher temperature had a lower active acceptor concentration. Improvements in band-edge luminescence were seen by cathodoluminescence for samples grown with the indium surfactant, confirming the trends seen in the Hall data.

Uniform GaN thin films grown on (100) silicon by remote plasma atomic layer deposition

International Nuclear Information System (INIS)

Shih, Huan-Yu; Chen, Miin-Jang; Lin, Ming-Chih; Chen, Liang-Yih

2015-01-01

The growth of uniform gallium nitride (GaN) thin films was reported on (100) Si substrate by remote plasma atomic layer deposition (RP-ALD) using triethylgallium (TEG) and NH 3 as the precursors. The self-limiting growth of GaN was manifested by the saturation of the deposition rate with the doses of TEG and NH 3 . The increase in the growth temperature leads to the rise of nitrogen content and improved crystallinity of GaN thin films, from amorphous at a low deposition temperature of 200 °C to polycrystalline hexagonal structures at a high growth temperature of 500 °C. No melting-back etching was observed at the GaN/Si interface. The excellent uniformity and almost atomic flat surface of the GaN thin films also infer the surface control mode of the GaN thin films grown by the RP-ALD technique. The GaN thin films grown by RP-ALD will be further applied in the light-emitting diodes and high electron mobility transistors on (100) Si substrate. (paper)

Control of ion content and nitrogen species using a mixed chemistry plasma for GaN grown at extremely high growth rates >9 μm/h by plasma-assisted molecular beam epitaxy

Science.gov (United States)

Gunning, Brendan P.; Clinton, Evan A.; Merola, Joseph J.; Doolittle, W. Alan; Bresnahan, Rich C.

2015-10-01

Utilizing a modified nitrogen plasma source, plasma assisted molecular beam epitaxy (PAMBE) has been used to achieve higher growth rates in GaN. A higher conductance aperture plate, combined with higher nitrogen flow and added pumping capacity, resulted in dramatically increased growth rates up to 8.4 μm/h using 34 sccm of N2 while still maintaining acceptably low operating pressure. It was further discovered that argon could be added to the plasma gas to enhance growth rates up to 9.8 μm/h, which was achieved using 20 sccm of N2 and 7.7 sccm Ar flows at 600 W radio frequency power, for which the standard deviation of thickness was just 2% over a full 2 in. diameter wafer. A remote Langmuir style probe employing the flux gauge was used to indirectly measure the relative ion content in the plasma. The use of argon dilution at low plasma pressures resulted in a dramatic reduction of the plasma ion current by more than half, while high plasma pressures suppressed ion content regardless of plasma gas chemistry. Moreover, different trends are apparent for the molecular and atomic nitrogen species generated by varying pressure and nitrogen composition in the plasma. Argon dilution resulted in nearly an order of magnitude achievable growth rate range from 1 μm/h to nearly 10 μm/h. Even for films grown at more than 6 μm/h, the surface morphology remained smooth showing clear atomic steps with root mean square roughness less than 1 nm. Due to the low vapor pressure of Si, Ge was explored as an alternative n-type dopant for high growth rate applications. Electron concentrations from 2.2 × 1016 to 3.8 × 1019 cm-3 were achieved in GaN using Ge doping, and unintentionally doped GaN films exhibited low background electron concentrations of just 1-2 × 1015 cm-3. The highest growth rates resulted in macroscopic surface features due to Ga cell spitting, which is an engineering challenge still to be addressed. Nonetheless, the dramatically enhanced growth rates demonstrate

Doping of GaN by ion implantation: Does It Work?

International Nuclear Information System (INIS)

Suvkhanov, A.; Wu, W.; Price, K.; Parikh, N.; Irene, E.; Hunn, J.; Thomson, D.; Davis, R.F.; Krasnobaev, L.

1998-04-01

Epitaxially grown GaN by metal organic chemical vapor deposition (MOCVD) on SiC were implanted with 100 keV Si + (for n-type) and 80 keV Mg + (for p-type) with various fluences from 1 x 10 12 to 7 x 10 15 ions/cm 2 at liquid nitrogen temperature (LT), room temperature (RT), and 700 C (HT). High temperature (1,200 C and 1,500 C) annealing was carried out after capping the GaN with epitaxial AlN by MOCVD to study damage recovery. Samples were capped by a layer of AlN in order to protect the GaN surface during annealing. Effects of implant temperature, damage and dopant activation are critically studied to evaluate a role of ion implantation in doping of GaN. The damage was studied by Rutherford Backscattering/Channeling, spectroscopic ellipsometry and photoluminescence. Results show dependence of radiation damage level on temperature of the substrate during implantation: implantations at elevated temperatures up to 550 C decrease the lattice disorder; hot implants above 550 C can not be useful in doping of GaN due to nitrogen loss from the surface. SE measurements have indicated very high sensitivity to the implantation damage. PL measurements at LT of 80 keV Mg + (5 x 10 14 cm 2 ) implanted and annealed GaN showed two peaks: one ∼ 100 meV and another ∼ 140 meV away from the band edge

Suppression of concentration quenching of Er-related luminescence in Er-doped GaN

International Nuclear Information System (INIS)

Chen Shaoqiang; Tomita, Shigeo; Kudo, Hiroshi; Akimoto, Katsuhiro; Dierre, Benjamin; Lee, Woong; Sekiguchi, Takashi

2010-01-01

Erbium-doped GaN with different doping concentrations were grown by ammonia-source molecular beam epitaxy. The intra-4f-shell transitions related green luminescence were observed by both photoluminescence (PL) and cathodoluminescence (CL) measurements. It was found that concentration quenching of Er-related luminescence was observed in PL measurements while not in CL measurements. The different excitation and relaxation processes are suggested as the cause of the concentration quenching characteristics between PL and CL. The strong Er-related CL intensity in highly doped GaN demonstrates that high energy excitation is a promising approach to suppress the concentration quenching in Er-doped GaN.

Low dislocation density InAlN/AlN/GaN heterostructures grown on GaN substrates and the effects on gate leakage characteristics

Energy Technology Data Exchange (ETDEWEB)

Kotani, Junji, E-mail: kotani.junji-01@jp.fujitsu.com; Yamada, Atsushi; Ishiguro, Tetsuro; Tomabechi, Shuichi; Nakamura, Norikazu [Fujitsu Laboratories Ltd., 10-1 Morinosato-Wakamiya, Atsugi, Kanagawa 243-0197 (Japan)

2016-04-11

This paper reports on the electrical characterization of Ni/Au Schottky diodes fabricated on InAlN high-electron-mobility transistor (HEMT) structures grown on low dislocation density free-standing GaN substrates. InAlN HEMT structures were grown on sapphire and GaN substrates by metal-organic vapor phase epitaxy, and the effects of threading dislocation density on the leakage characteristics of Ni/Au Schottky diodes were investigated. Threading dislocation densities were determined to be 1.8 × 10{sup 4 }cm{sup −2} and 1.2 × 10{sup 9 }cm{sup −2} by the cathodoluminescence measurement for the HEMT structures grown on GaN and sapphire substrates, respectively. Leakage characteristics of Ni/Au Schottky diodes were compared between the two samples, and a reduction of the leakage current of about three to four orders of magnitude was observed in the forward bias region. For the high reverse bias region, however, no significant improvement was confirmed. We believe that the leakage current in the low bias region is governed by a dislocation-related Frenkel–Poole emission, and the leakage current in the high reverse bias region originates from field emission due to the large internal electric field in the InAlN barrier layer. Our results demonstrated that the reduction of dislocation density is effective in reducing leakage current in the low bias region. At the same time, it was also revealed that another approach will be needed, for instance, band modulation by impurity doping and insertion of insulating layers beneath the gate electrodes for a substantial reduction of the gate leakage current.

Growth on nonpolar and semipolar GaN: The substrate dilemma

Energy Technology Data Exchange (ETDEWEB)

Wernicke, T.; Weyers, M. [Ferdinand-Braun-Institute, Berlin (Germany); Kneissl, M. [Ferdinand-Braun-Institute, Berlin (Germany); Institute of Solid State Physics, TU Berlin (Germany)

2009-07-01

Growth of nonpolar and semipolar GaN is very promising for achieving green laser diodes (LDs). However, the choice of the substrate is a difficult one: Heteroepitaxial growth on sapphire, SiC, LiAlO{sub 2} yields GaN films with a poor surface quality and high defect densities. On the other hand non- and semipolar bulk GaN substrates provide excellent crystal quality, but are so far only available in very small sizes. In this paper hetero- and homoepitaxial growth is compared. For all heteroepitaxially grown semi- and nonpolar GaN layers threading dislocations (TD) and basal plane stacking faults (BSF) can be found. There are four possible mechanisms for the generation of BSF: Growth of the N-polar basal plane, formation during nucleation at substrate steps, formation at the coalescence front of differently stacked nucleation islands, and generation at planar defects occurring in m-plane GaN on LiAlO{sub 2}. BSF induce surface roughening and are associated with partial dislocations causing nonradiative recombination. Thus they affect the performance of devices. We show that BSFs and TDs can be reduced by epitaxial lateral overgrowth resulting in several micrometer wide defect free areas. However, for LEDs larger defect-free areas are required. GaN layers grown on bulk GaN substrates exhibit a high crystal quality, but show in many cases long-range surface structures with a height of {approx}1{mu}m.

Highly repeatable room temperature negative differential resistance in AlN/GaN resonant tunneling diodes grown by molecular beam epitaxy

International Nuclear Information System (INIS)

Growden, Tyler A.; Fakhimi, Parastou; Berger, Paul R.; Storm, David F.; Meyer, David J.; Zhang, Weidong; Brown, Elliott R.

2016-01-01

AlN/GaN resonant tunneling diodes grown on low dislocation density semi-insulating bulk GaN substrates via plasma-assisted molecular-beam epitaxy are reported. The devices were fabricated using a six mask level, fully isolated process. Stable room temperature negative differential resistance (NDR) was observed across the entire sample. The NDR exhibited no hysteresis, background light sensitivity, or degradation of any kind after more than 1000 continuous up-and-down voltage sweeps. The sample exhibited a ∼90% yield of operational devices which routinely displayed an average peak current density of 2.7 kA/cm 2 and a peak-to-valley current ratio of ≈1.15 across different sizes.

Highly repeatable room temperature negative differential resistance in AlN/GaN resonant tunneling diodes grown by molecular beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Growden, Tyler A.; Fakhimi, Parastou; Berger, Paul R., E-mail: pberger@ieee.org [Department of Electrical and Computer Engineering, The Ohio State University, Columbus, Ohio 43210 (United States); Storm, David F.; Meyer, David J. [U.S. Naval Research Laboratory, Washington, DC 20375 (United States); Zhang, Weidong; Brown, Elliott R. [Departments of Physics and Electrical Engineering, Wright State University, Dayton, Ohio 45435 (United States)

2016-08-22

AlN/GaN resonant tunneling diodes grown on low dislocation density semi-insulating bulk GaN substrates via plasma-assisted molecular-beam epitaxy are reported. The devices were fabricated using a six mask level, fully isolated process. Stable room temperature negative differential resistance (NDR) was observed across the entire sample. The NDR exhibited no hysteresis, background light sensitivity, or degradation of any kind after more than 1000 continuous up-and-down voltage sweeps. The sample exhibited a ∼90% yield of operational devices which routinely displayed an average peak current density of 2.7 kA/cm{sup 2} and a peak-to-valley current ratio of ≈1.15 across different sizes.

Coherence in a transmon qubit with epitaxial tunnel junctions

Energy Technology Data Exchange (ETDEWEB)

Weides, Martin [National Institute of Standards and Technology, Boulder, Colorado 80305 (United States); Karlsruhe Institute of Technology (Germany); Kline, Jeffrey; Vissers, Michael; Sandberg, Martin; Pappas, David [National Institute of Standards and Technology, Boulder, Colorado 80305 (United States); Wisbey, David [National Institute of Standards and Technology, Boulder, Colorado 80305 (United States); Saint Louis University, St. Louis, Missouri 63103 (United States); Johnson, Blake; Ohki, Thomas [Raytheon BBN Technologies, Cambridge, Massachusetts 02138 (United States)

2012-07-01

Transmon qubits based on epitaxial tunnel junctions and interdigitated capacitors were developed. This multileveled qubit, patterned by use of all-optical lithography, is a step towards scalable qubits with a high integration density. The relaxation time T{sub 1} is.72-.86 {mu} sec and the ensemble dephasing time T{sub 2}{sup *} is slightly larger than T{sub 1}. The dephasing time T{sub 2} (1.36 {mu} sec) is nearly energy-relaxation-limited. Qubit spectroscopy yields weaker level splitting than observed in qubits with amorphous barriers in equivalent-size junctions. The qubit's inferred microwave loss closely matches the weighted losses of the individual elements (junction, wiring dielectric, and interdigitated capacitor), determined by independent resonator measurements.

Leakage current reduction of vertical GaN junction barrier Schottky diodes using dual-anode process

Science.gov (United States)

Hayashida, Tetsuro; Nanjo, Takuma; Furukawa, Akihiko; Watahiki, Tatsuro; Yamamuka, Mikio

2018-04-01

The origin of the leakage current of a trench-type vertical GaN diode was discussed. We found that the edge of p-GaN is the main leakage spot. To reduce the reverse leakage current at the edge of p-GaN, a dual-anode process was proposed. As a result, the reverse blocking voltage defined at the leakage current density of 1 mA/cm2 of a vertical GaN junction barrier Schottky (JBS) diode was improved from 780 to 1,190 V, which is the highest value ever reported for vertical GaN Schottky barrier diodes (SBDs).

X-ray absorption near-edge structure of GaN with high Mn concentration grown on SiC

Science.gov (United States)

Sancho-Juan, O.; Cantarero, A.; Garro, N.; Cros, A.; Martínez-Criado, G.; Salomé, M.; Susini, J.; Olguín, D.; Dhar, S.

2009-07-01

By means of x-ray absorption near-edge structure (XANES) several Ga1-xMnxN (0.03GaN samples consisted of different epilayers grown by molecular beam epitaxy on [0001] SiC substrates. The low mismatch between GaN and SiC allows for a good quality and homogeneity of the material. The measurements were performed in fluorescence mode around both the Ga and Mn K edges. All samples studied present a similar Mn ionization state, very close to 2+, and tetrahedral coordination. In order to interpret the near-edge structure, we have performed ab initio calculations using the full potential linear augmented plane wave method as implemented in the Wien2k code. The calculations show the appearance of a Mn bonding \\mathrm {t_{2}}\\uparrow band localized in the gap region, and the corresponding anti-bonding state \\mathrm {t_{2}}\\downarrow , which seem to be responsible for the double structure which appears at the pre-edge absorption region. The shoulders and main absorption peak of the XANES spectra are attributed to transitions from the Mn(1s) band to the conduction bands, which are partially dipole allowed because of the Mn(4p) contribution to these bands.

Resistivity analysis of epitaxially grown, doped semiconductors using energy dependent secondary ion mass spectroscopy

International Nuclear Information System (INIS)

Burnham, Shawn D.; Thomas, Edward W.; Doolittle, W. Alan

2006-01-01

A characterization technique is discussed that allows quantitative optimization of doping in epitaxially grown semiconductors. This technique uses relative changes in the host atom secondary ion (HASI) energy distribution from secondary ion mass spectroscopy (SIMS) to indicate relative changes in conductivity of the material. Since SIMS is a destructive process due to sputtering through a film, a depth profile of the energy distribution of sputtered HASIs in a matrix will contain information on the conductivity of the layers of the film as a function of depth. This process is demonstrated with Mg-doped GaN, with the Mg flux slowly increased through the film. Three distinct regions of conductivity were observed: one with Mg concentration high enough to cause compensation and thus high resistivity, a second with moderate Mg concentration and low resistivity, and a third with little to no Mg doping, causing high resistivity due to the lack of free carriers. During SIMS analysis of the first region, the energy distributions of sputtered Ga HASIs were fairly uniform and unchanging for a Mg flux above the saturation, or compensation, limit. For the second region, the Ga HASI energy distributions shifted and went through a region of inconsistent energy distributions for Mg flux slightly below the critical flux for saturation, or compensation. Finally, for the third region, the Ga HASI energy distributions then settled back into another fairly unchanging, uniform pattern. These three distinct regions were analyzed further through growth of Mg-doped step profiles and bulk growth of material at representative Mg fluxes. The materials grown at the two unchanging, uniform regions of the energy distributions yielded highly resistive material due to too high of Mg concentration and low to no Mg concentration, respectively. However, material grown in the transient energy distribution region with Mg concentration between that of the two highly resistive regions yielded low

Resistivity analysis of epitaxially grown, doped semiconductors using energy dependent secondary ion mass spectroscopy

Science.gov (United States)

Burnham, Shawn D.; Thomas, Edward W.; Doolittle, W. Alan

2006-12-01

A characterization technique is discussed that allows quantitative optimization of doping in epitaxially grown semiconductors. This technique uses relative changes in the host atom secondary ion (HASI) energy distribution from secondary ion mass spectroscopy (SIMS) to indicate relative changes in conductivity of the material. Since SIMS is a destructive process due to sputtering through a film, a depth profile of the energy distribution of sputtered HASIs in a matrix will contain information on the conductivity of the layers of the film as a function of depth. This process is demonstrated with Mg-doped GaN, with the Mg flux slowly increased through the film. Three distinct regions of conductivity were observed: one with Mg concentration high enough to cause compensation and thus high resistivity, a second with moderate Mg concentration and low resistivity, and a third with little to no Mg doping, causing high resistivity due to the lack of free carriers. During SIMS analysis of the first region, the energy distributions of sputtered Ga HASIs were fairly uniform and unchanging for a Mg flux above the saturation, or compensation, limit. For the second region, the Ga HASI energy distributions shifted and went through a region of inconsistent energy distributions for Mg flux slightly below the critical flux for saturation, or compensation. Finally, for the third region, the Ga HASI energy distributions then settled back into another fairly unchanging, uniform pattern. These three distinct regions were analyzed further through growth of Mg-doped step profiles and bulk growth of material at representative Mg fluxes. The materials grown at the two unchanging, uniform regions of the energy distributions yielded highly resistive material due to too high of Mg concentration and low to no Mg concentration, respectively. However, material grown in the transient energy distribution region with Mg concentration between that of the two highly resistive regions yielded low

Optical excitation and external photoluminescence quantum efficiency of Eu3+ in GaN

NARCIS (Netherlands)

de Boer, W.D.A.M.; McGonigle, C.; Gregorkiewicz, T.; Fujiwara, Y.; Stallinga, P.

2014-01-01

We investigate photoluminescence of Eu-related emission in a GaN host consisting of thin layers grown by organometallic vapor-phase epitaxy. By comparing it with a reference sample of Eu-doped Y2O3, we find that the fraction of Eu3+ ions that can emit light upon optical excitation is of the order of

Increased p-type conductivity through use of an indium surfactant in the growth of Mg-doped GaN

Energy Technology Data Exchange (ETDEWEB)

Kyle, Erin C. H., E-mail: erinkyle@engineering.ucsb.edu; Kaun, Stephen W.; Young, Erin C.; Speck, James S. [Materials Department, University of California, Santa Barbara, California 93106 (United States)

2015-06-01

We have examined the effect of an indium surfactant on the growth of p-type GaN by ammonia-based molecular beam epitaxy. p-type GaN was grown at temperatures ranging from 700 to 780 °C with and without an indium surfactant. The Mg concentration in all films in this study was 4.5–6 × 10{sup 19} cm{sup −3} as measured by secondary ion mass spectroscopy. All p-type GaN films grown with an indium surfactant had higher p-type conductivities and higher hole concentrations than similar films grown without an indium surfactant. The lowest p-type GaN room temperature resistivity was 0.59 Ω-cm, and the highest room temperature carrier concentration was 1.6 × 10{sup 18} cm{sup −3}. Fits of the temperature-dependent carrier concentration data showed a one to two order of magnitude lower unintentional compensating defect concentration in samples grown with the indium surfactant. Samples grown at higher temperature had a lower active acceptor concentration. Improvements in band-edge luminescence were seen by cathodoluminescence for samples grown with the indium surfactant, confirming the trends seen in the Hall data.

High Al-content AlxGa1-xN epilayers grown on Si substrate by plasma-assisted molecular beam epitaxy

International Nuclear Information System (INIS)

Hussein, A.SH.; Thahab, S.M.; Hassan, Z.; Chin, C.W.; Abu Hassan, H.; Ng, S.S.

2009-01-01

The microstructure and optical properties of Al x Ga 1-x N/GaN/AlN films on Si (1 1 1) substrate grown by plasma-assisted molecular beam epitaxy (MBE) have been studied and investigated. Reflection high energy electron diffraction (RHEED), scanning electron microscopy (SEM), high-resolution X-ray diffraction (HR-XRD), energy dispersive X-ray spectroscopy (EDS) line analysis and photoluminescence (PL) were used to investigate a reconstruction pattern, cross-section, mole fraction and crystalline quality of the heterostructure. By applying the Vegard's law, a high Al-mole fraction of Al x Ga 1-x N sample with value of 0.43 has been obtained and compared with EDS line analysis measurement value. PL spectrum has exhibited a sharp and intense band edge emission of GaN with the absence of yellow emission band, indicating good crystal quality of the Al x Ga 1-x N has been successfully grown on Si substrate.

High quality junctions by interpenetration of vapor liquid solid grown nanostructures for microchip integration

Energy Technology Data Exchange (ETDEWEB)

Jebril, Seid; Kuhlmann, Hanna; Adelung, Rainer [Funktionale Nanomaterialien, CAU Kiel (Germany); Mueller, Sven [Nanowires and Thin Films, II. Physikalisches Institut, Goettingen (Germany); Ronning, Carsten [Institute for Solid State Physics, Universitaet Jena (Germany); Kienle, Lorenz [Synthese und Realstruktur, CAU Kiel (Germany); Duppel, Viola [MPI fuer Festkoerperforschung, Stuttgart (Germany)

2009-07-01

The usability of nanostructures in electrical devices like gas sensors depends critically on the ability to form high quality contacts and junctions. For the fabrication of various nanostructures, vapor-liquid-solid (VLS) growth is a wide spread and very efficient technique. However, forming contacts with the VLS grown structures to utilize them in a device is still tedious, because either the substrate has to be epitaxial to the VLS material or a manual alignment is necessary. Here we demonstrate the contact formation by simply using the ability of individual crystals to interpenetrate each other during the straight forward VLS growth. This allows growing VLS structures directly on two neighboring gold circuit paths of a microchip; bridges over predefined gaps will be formed. Moreover, TEM investigations confirm the high quality of the crystalline junctions that allow demonstrations as UV and hydrogen-sensor. The VLS devices are compared with conventional produced.

P-type conduction in Mg-doped GaN treated with low-energy electron beam irradiation (LEEBI)

International Nuclear Information System (INIS)

Amano, Hiroshi; Kito, Masahiro; Hiramatsu, Kazumasa

1989-01-01

Distinct p-type conduction is realized with Mg-doped GaN by the low-energy electron-beam irradiation (LEEBI) treatment, and the properties of the GaN p-n junction LED are reported for the first time. It was found that the LEEBI treatment drastically lowers the resistivity and remarkably enhances the PL efficiency of MOVPE-grown Mg-doped GaN. The Hall effect measurement of this Mg-doped GaN treated with LEEBI at room temperature showed that the hole concentration is ∼2·10 16 cm -3 , the hole mobility is ∼8 cm 2 /V·s and the resistivity is ∼35Ω· cm. The p-n junction LED using Mg-doped GaN treated with LEEBI as the p-type material showed strong near-band-edge emission due to the hole injection from the p-layer to the n-layer at room temperature. (author)

Oxygen adsorption and incorporation at irradiated GaN(0001) and GaN(0001¯) surfaces: First-principles density-functional calculations

Science.gov (United States)

Sun, Qiang; Selloni, Annabella; Myers, T. H.; Doolittle, W. Alan

2006-11-01

Density functional theory calculations of oxygen adsorption and incorporation at the polar GaN(0001) and GaN(0001¯) surfaces have been carried out to explain the experimentally observed reduced oxygen concentration in GaN samples grown by molecular beam epitaxy in the presence of high energy (˜10keV) electron beam irradiation [Myers , J. Vac. Sci. Technol. B 18, 2295 (2000)]. Using a model in which the effect of the irradiation is to excite electrons from the valence to the conduction band, we find that both the energy cost of incorporating oxygen impurities in deeper layers and the oxygen adatom diffusion barriers are significantly reduced in the presence of the excitation. The latter effect leads to a higher probability for two O adatoms to recombine and desorb, and thus to a reduced oxygen concentration in the irradiated samples, consistent with experimental observations.

P-type doping of semipolar GaN(11 anti 22) by plasma-assisted molecular-beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Das, A.; Lahourcade, L. [Equipe Mixte CEA-CNRS, Nanophysique et Semiconducteurs, CEA-Grenoble, INAC/SP2M, Grenoble (France); Pernot, J. [Institut Neel, CNRS et Universite Joseph Fourier, Grenoble (France); Valdueza-Felip, S. [Equipe Mixte CEA-CNRS, Nanophysique et Semiconducteurs, CEA-Grenoble, INAC/SP2M, Grenoble (France); Dept. Electronica, Escuela Politecnica, Universidad de Alcala, Alcala de Henares, Madrid (Spain); Ruterana, P. [CIMAP, UMR6252, CNRS-ENSICAEN-CEA-UCBN, Caen (France); Laufer, A.; Eickhoff, M. [I. Physikalisches Institut, Justus-Liebig-Universitaet Giessen (Germany); Monroy, E.

2010-07-15

We report the effect of Mg doping on the growth kinetics of semipolar GaN(11-22) synthesized by plasma-assisted molecular-beam epitaxy. Mg tends to segregate on the surface, inhibiting the formation of the self-regulated Ga film which is used as a surfactant for the growth of undoped and Si-doped GaN(11-22). As a result, the growth widow is reduced for Mg doped layers, and we observe a certain deterioration of the surface morphology. In spite of this difficulties, homogenous Mg incorporation is achieved and layers display p -type conductivity for Mg atomic concentration higher than 7 x 10{sup 18} cm{sup -3}. Microscopy studies show no evidence of the pyramidal defects or polarity inversion domains found in Mg-doped GaN(0001). (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Initial stages of the ion-beam assisted epitaxial GaN film growth on 6H-SiC(0001)

International Nuclear Information System (INIS)

Neumann, L.; Gerlach, J.W.; Rauschenbach, B.

2012-01-01

Ultra-thin gallium nitride (GaN) films were deposited using the ion-beam assisted molecular-beam epitaxy technique. The influence of the nitrogen ion to gallium atom flux ratio (I/A ratio) during the early stages of GaN nucleation and thin film growth directly, without a buffer layer on super-polished 6H-SiC(0001) substrates was studied. The deposition process was performed at a constant substrate temperature of 700 °C by evaporation of Ga and irradiation with hyperthermal nitrogen ions from a constricted glow-discharge ion source. The hyperthermal nitrogen ion flux was kept constant and the kinetic energy of the ions did not exceed 25 eV. The selection of different I/A ratios in the range from 0.8 to 3.2 was done by varying the Ga deposition rate between 5 × 10 13 and 2 × 10 14 at. cm −2 s −1 . The crystalline surface structure during the GaN growth was monitored in situ by reflection high-energy electron diffraction. The surface topography of the films as well as the morphology of separated GaN islands on the substrate surface was examined after film growth using a scanning tunneling microscope without interruption of ultra-high vacuum. The results show, that the I/A ratio has a major impact on the properties of the resulting ultra-thin GaN films. The growth mode, the surface roughness, the degree of GaN coverage of the substrate and the polytype mixture depend notably on the I/A ratio. - Highlights: ► Ultra-thin epitaxial GaN films prepared by hyperthermal ion-beam assisted deposition. ► Surface structure and topography studied during and after initial growth stages. ► Growth mode dependent on nitrogen ion to gallium atom flux ratio. ► Change from three-dimensional to two-dimensional growth for Ga-rich growth conditions.

Study of optical properties of bulk GaN crystals grown by HVPE

Energy Technology Data Exchange (ETDEWEB)

Gu, Hong; Ren, Guoqiang; Zhou, Taofei; Tian, Feifei; Xu, Yu; Zhang, Yumin; Wang, Mingyue; Zhang, Zhiqiang [Suzhou Institute of Nano-tech and Nano-bionics, Chinese Academy of Sciences, Suzhou 215123 (China); Cai, Demin [Suzhou Nanowin Science and Technology Co., Ltd., Suzhou 215123 (China); Wang, Jianfeng [Suzhou Institute of Nano-tech and Nano-bionics, Chinese Academy of Sciences, Suzhou 215123 (China); Suzhou Nanowin Science and Technology Co., Ltd., Suzhou 215123 (China); Xu, Ke, E-mail: kxu2006@sinano.ac.cn [Suzhou Institute of Nano-tech and Nano-bionics, Chinese Academy of Sciences, Suzhou 215123 (China); Suzhou Nanowin Science and Technology Co., Ltd., Suzhou 215123 (China)

2016-07-25

We investigated the optical properties of a series of GaN samples sliced from the same bulk crystal grown using hydride vapor phase epitaxy. The high crystalline quality of the samples was evaluated using cathodoluminescence measurements, and the dislocation density ranged from 2.4 × 10{sup 6} to 2.3 × 10{sup 5} cm{sup −2}. The impurity concentration was determined using secondary-ion mass spectroscopy, and photoluminescence (PL) measurements were conducted in the range of 3–300 K. We did not find a correlation between the O or C impurities and the weak yellow luminescence (YL) band. As the dislocation density decreased, the intensity of the band edge emission increased and that of the YL band decreased. A competition between the two-electron satellite lines correlated to Si and the YL band was also observed in the low-temperature PL spectra, which demonstrated that the Si impurity also plays an important role in the weak YL band of these GaN samples. These results indicate that the Si donors around the dislocations, as reasonable sources of shallow donors, will recombine with possible deep acceptors and finally respond with the YL. - Highlights: • The investigated samples were sliced from the same bulk crystal. • No correlation between the O or C impurities and the weak YL band is observed. • A well-regulated relationship between the YL band and the dislocations is found. • A competition between the TES-Si lines and the YL band is discussed. • The dislocations trapping Si impurity is suggested to be responsible for YL band.

Infrared reflectance of GaN films grown on Si(001) substrates

International Nuclear Information System (INIS)

Zhang, Xiong; Hou, Yong-Tian; Feng, Zhe-Chuan; Chen, Jin-Li

2001-01-01

GaN thin films on Si(001) substrates are studied by infrared reflectance (IRR) spectroscopy at room temperature (RT). Variations in the IRR spectral line shape with the microstructure of GaN/Si(011) film are quantitatively explained in terms of a three-component effective medium model. In this model, the nominally undoped GaN film is considered to consist of three elementary components, i.e., single crystalline GaN grains, pores (voids), and inter-granulated materials (amorphous GaN clusters). Such a polycrystalline nature of the GaN/Si(001) films was confirmed by scanning electron microscopy measurements. It was demonstrated that based on the proposed three-component effective medium model, excellent overall simulation of the RT-IRR spectra can be achieved, and the fine structures of the GaN reststrahlen band in the measured RT-IRR spectra can also be interpreted very well. Furthermore, the volume fraction for each component in the GaN/Si(001) film was accurately determined by fitting the experimental RT-IRR spectra with the theoretical simulation. These results indicate that IRR spectroscopy can offer a sensitive and convenient tool to probe the microstructure of GaN films grown on silicon. [copyright] 2001 American Institute of Physics

Macrodefect-free, large, and thick GaN bulk crystals for high-quality 2–6 in. GaN substrates by hydride vapor phase epitaxy with hardness control

Science.gov (United States)

Fujikura, Hajime; Konno, Taichiro; Suzuki, Takayuki; Kitamura, Toshio; Fujimoto, Tetsuji; Yoshida, Takehiro

2018-06-01

On the basis of a novel crystal hardness control, we successfully realized macrodefect-free, large (2–6 in.) and thick +c-oriented GaN bulk crystals by hydride vapor phase epitaxy. Without the hardness control, the introduction of macrodefects including inversion domains and/or basal-plane dislocations seemed to be indispensable to avoid crystal fracture in GaN growth with millimeter thickness. However, the presence of these macrodefects tended to limit the applicability of the GaN substrate to practical devices. The present technology markedly increased the GaN crystal hardness from below 20 to 22 GPa, thus increasing the available growth thickness from below 1 mm to over 6 mm even without macrodefect introduction. The 2 and 4 in. GaN wafers fabricated from these crystals had extremely low dislocation densities in the low- to mid-105 cm‑2 range and low off-angle variations (2 in.: <0.1° 4 in.: ∼0.2°). The realization of such high-quality 6 in. wafers is also expected.

Surface chemistry and electronic structure of nonpolar and polar GaN films

Energy Technology Data Exchange (ETDEWEB)

Mishra, Monu; Krishna, T.C. Shibin; Aggarwal, Neha; Gupta, Govind, E-mail: govind@nplindia.org

2015-08-01

Highlights: • Surface chemistry and electronic structure of polar and nonpolar GaN is reported. • Influence of polarization on electron affinity of p & np GaN films is investigated. • Correlation between surface morphology and polarity has been deduced. - Abstract: Photoemission and microscopic analysis of nonpolar (a-GaN/r-Sapphire) and polar (c-GaN/c-Sapphire) epitaxial gallium nitride (GaN) films grown via RF-Molecular Beam Epitaxy is reported. The effect of polarization on surface properties like surface states, electronic structure, chemical bonding and morphology has been investigated and correlated. It was observed that polarization lead to shifts in core level (CL) as well as valence band (VB) spectra. Angle dependent X-ray Photoelectron Spectroscopic analysis revealed higher surface oxide in polar GaN film compared to nonpolar GaN film. On varying the take off angle (TOA) from 0° to 60°, the Ga−O/Ga−N ratio varied from 0.11–0.23 for nonpolar and 0.17–0.36 for polar GaN film. The nonpolar film exhibited N-face polarity while Ga-face polarity was perceived in polar GaN film due to the inherent polarization effect. Polarization charge compensated surface states were observed on the polar GaN film and resulted in downward band bending. Ultraviolet photoelectron spectroscopic measurements revealed electron affinity and ionization energy of 3.4 ± 0.1 eV and 6.8 ± 0.1 eV for nonpolar GaN film and 3.8 ± 0.1 eV and 7.2 ± 0.1 eV for polar GaN film respectively. Field Emission Scanning Electron Microscopy measurements divulged smooth morphology with pits on polar GaN film. The nonpolar film on the other hand showed pyramidal structures having facets all over the surface.

Stress relaxed nanoepitaxy GaN for growth of phosphor-free indium-rich nanostructures incorporated in apple-white LEDs

Energy Technology Data Exchange (ETDEWEB)

Soh, C.B.; Liu, W.; Ang, N.S.S.; Yong, A.M.; Lai, S.C.; Teng, J.H. [Institute of Materials Research and Engineering, Agency for Science, Technology and Research, 3 Research Link, Singapore 117602 (Singapore); Chua, S.J. [Institute of Materials Research and Engineering, Agency for Science, Technology and Research, 3 Research Link, Singapore 117602 (Singapore); Singapore-MIT Alliance, 4 Engineering Drive 3, Singapore 117576 (Singapore)

2010-06-15

Phosphor-free apple-white light emitting diodes (LEDs) have been fabricated using dual stacked InGaN/GaN multiple quantum wells (MQWs) comprising a lower set of long wavelength emitting indium rich nanostructures incorporated in MQWs with an upper set of cyan-green emitting MQWs. The LEDs were grown on nano-epitaxial lateral overgrown (ELO) GaN template formed by regrowth of GaN over SiO{sub 2} film patterned using an anodic alumina oxide mask with holes of {proportional_to}125 nm diameter and a period of 250 nm. The MQWs grown on the nano-ELO GaN templates show stronger photoluminescence intensity and a higher activation energy for their peak emission. A minimal shift in the electroluminescence (EL) spectra with higher injection current applied for LEDs grown on ELO-GaN compared to conventional GaN template, suggests a reduction in strain of the quantum well layers on the nano-ELO GaN template. An enhancement in the light extraction efficiency is also achieved with multiple scattering via the embedded SiO{sub 2} mask. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

Growth modes of InN (000-1) on GaN buffer layers on sapphire

International Nuclear Information System (INIS)

Liu Bing; Kitajima, Takeshi; Chen Dongxue; Leone, Stephen R.

2005-01-01

In this work, using atomic force microscopy and scanning tunneling microscopy, we study the surface morphologies of epitaxial InN films grown by plasma-assisted molecular beam epitaxy with intervening GaN buffer layers on sapphire substrates. On smooth GaN buffer layers, nucleation and evolution of three-dimensional InN islands at various coverages and growth temperatures are investigated. The shapes of the InN islands are observed to be predominantly mesalike with large flat (000-1) tops, which suggests a possible role of indium as a surfactant. Rough GaN buffer layers composed of dense small GaN islands are found to significantly improve uniform InN wetting of the substrates, on which atomically smooth InN films are obtained that show the characteristics of step-flow growth. Scanning tunneling microscopy imaging reveals the defect-mediated surface morphology of smooth InN films, including surface terminations of screw dislocations and a high density of shallow surface pits with depths less than 0.3 nm. The mechanisms of the three-dimensional island size and shape evolution and formation of defects on smooth surfaces are considered

Structure Shift of GaN Among Nanowall Network, Nanocolumn, and Compact Film Grown on Si (111) by MBE.

Science.gov (United States)

Zhong, Aihua; Fan, Ping; Zhong, Yuanting; Zhang, Dongping; Li, Fu; Luo, Jingting; Xie, Yizhu; Hane, Kazuhiro

2018-02-13

Structure shift of GaN nanowall network, nanocolumn, and compact film were successfully obtained on Si (111) by plasma-assisted molecular beam epitaxy (MBE). As is expected, growth of the GaN nanocolumns was observed in N-rich condition on bare Si, and the growth shifted to compact film when the Ga flux was improved. Interestingly, if an aluminum (Al) pre-deposition for 40 s was carried out prior to the GaN growth, GaN grows in the form of the nanowall network. Results show that the pre-deposited Al exits in the form of droplets with typical diameter and height of ~ 80 and ~ 6.7 nm, respectively. A growth model for the nanowall network is proposed and the growth mechanism is discussed. GaN grows in the area without Al droplets while the growth above Al droplets is hindered, resulting in the formation of continuous GaN nanowall network that removes the obstacles of nano-device fabrication.

Role of dislocations and carrier concentration in limiting the electron mobility of InN films grown by plasma assisted molecular beam epitaxy

Science.gov (United States)

Tangi, Malleswararao; De, Arpan; Shivaprasad, S. M.

2018-01-01

We report the molecular beam epitaxy growth of device quality InN films on GaN epilayer and nano-wall network (NWN) templates deposited on c-sapphire by varying the film thickness up to 1 μm. The careful experiments are directed towards obtaining high mobility InN layers having a low band gap with improved crystal quality. The dislocation density is quantified by using high resolution X-ray diffraction rocking curve broadening values of symmetric and asymmetric reflections, respectively. We observe that the dislocation density of the InN films grown on GaN NWN is less than that of the films grown on the GaN epilayer. This is attributed to the nanoepitaxial lateral overlayer growth (ELOG) process, where the presence of voids at the interface of InN/GaN NWN prevents the propagation of dislocation lines into the InN epilayers, thereby causing less defects in the overgrown InN films. Thus, this new adaptation of the nano-ELOG growth process enables us to prepare InN layers with high electron mobility. The obtained electron mobility of 2121 cm2/Vs for 1 μm thick InN/GaN NWN is comparable with the literature values of similar thickness InN films. Furthermore, in order to understand the reasons that limit electron mobility, the charge neutrality condition is employed to study the variation of electron mobility as a function of dislocation density and carrier concentration. Overall, this study provides a route to attaining improved crystal quality and electronic properties of InN films.

Significantly improved surface morphology of N-polar GaN film grown on SiC substrate by the optimization of V/III ratio

Science.gov (United States)

Deng, Gaoqiang; Zhang, Yuantao; Yu, Ye; Yan, Long; Li, Pengchong; Han, Xu; Chen, Liang; Zhao, Degang; Du, Guotong

2018-04-01

In this paper, N-polar GaN films with different V/III ratios were grown on vicinal C-face SiC substrates by metalorganic chemical vapor deposition. During the growth of N-polar GaN film, the V/III ratio was controlled by adjusting the molar flow rate of ammonia while keeping the trimethylgallium flow rate unchanged. The influence of the V/III ratio on the surface morphology of N-polar GaN film has been studied. We find that the surface root mean square roughness of N-polar GaN film over an area of 20 × 20 μm2 can be reduced from 8.13 to 2.78 nm by optimization of the V/III ratio. Then, using the same growth conditions, N-polar InGaN/GaN multiple quantum wells (MQWs) light-emitting diodes (LEDs) were grown on the rough and the smooth N-polar GaN templates, respectively. Compared with the LED grown on the rough N-polar GaN template, dramatically improved interface sharpness and luminescence uniformity of the InGaN/GaN MQWs are achieved for the LED grown on the smooth N-polar GaN template.

Growth of c-plane ZnO on γ-LiAlO2 (1 0 0) substrate with a GaN buffer layer by plasma assisted molecular beam epitaxy

International Nuclear Information System (INIS)

Yan, T.; Lu, C.-Y.J.; Schuber, R.; Chang, L.; Schaadt, D.M.; Chou, M.M.C.; Ploog, K.H.; Chiang, C.-M.

2015-01-01

Highlights: • ZnO epilayers were grown on LiAlO 2 (1 0 0) substrate with a GaN buffer layer by MBE. • A high Zn/O flux ratio is beneficial for reducing the density of screw dislocations. • Reciprocal space maps demonstrate that the misfit strain in ZnO has been relaxed. • No interfacial layer is formed at ZnO/GaN interface using a Zn pre-exposure strategy. - Abstract: C-plane ZnO epilayers were grown on LiAlO 2 (1 0 0) substrate with a GaN buffer layer by plasma assisted molecular beam epitaxy. Both the X-ray rocking curves and the transmission electron microscopy analyses indicate that the ZnO epilayers exhibit a lower threading dislocation density (∼1 × 10 10 cm −2 ) as compared to those grown on LiAlO 2 substrate without the buffer layer. A high Zn/O flux ratio is beneficial for reducing the density of screw-type dislocations. Reciprocal space maps demonstrate that the misfit strain has been relaxed. No interfacial layer is formed at the ZnO/GaN interface by using a Zn pre-exposure strategy. The ZnO epilayers exhibit a strong near band edge emission at 3.28 eV at room temperature with a negligible green band emission

High growth rate GaN on 200 mm silicon by metal-organic vapor phase epitaxy for high electron mobility transistors

Science.gov (United States)

Charles, M.; Baines, Y.; Bavard, A.; Bouveyron, R.

2018-02-01

It is increasingly important to reduce the cycle time of epitaxial growth, in order to reduce the costs of device fabrication, especially for GaN based structures which typically have growth cycles of several hours. We have performed a comprehensive study using metal-organic vapor phase epitaxy (MOVPE) investigating the effects of changing GaN growth rates from 0.9 to 14.5 μm/h. Although there is no significant effect on the strain incorporated in the layers, we have seen changes in the surface morphology which can be related to the change in dislocation behaviour and surface diffusion effects. At the small scale, as seen by AFM, increased dislocation density for higher growth rates leads to increased pinning of growth terraces, resulting in more closely spaced terraces. At a larger scale of hundreds of μm observed by optical profiling, we have related the formation of grains to the rate of surface diffusion of adatoms using a random walk model, implying diffusion distances from 30 μm for the highest growth rates up to 100 μm for the lowest. The increased growth rate also increases the intrinsic carbon incorporation which can increase the breakdown voltage of GaN films. Despite an increased threading dislocation density, these very high growth rates of 14.5 μm/hr by MOVPE have been shown to be appealing for reducing epitaxial growth cycle times and therefore costs in High Electron Mobility Transistor (HEMT) structures.

Inductively Coupled Plasma-Induced Etch Damage of GaN p-n Junctions

International Nuclear Information System (INIS)

SHUL, RANDY J.; ZHANG, LEI; BACA, ALBERT G.; WILLISON, CHRISTI LEE; HAN, JUNG; PEARTON, S.J.; REN, F.

1999-01-01

Plasma-induced etch damage can degrade the electrical and optical performance of III-V nitride electronic and photonic devices. We have investigated the etch-induced damage of an Inductively Coupled Plasma (ICP) etch system on the electrical performance of mesa-isolated GaN pn-junction diodes. GaN p-i-n mesa diodes were formed by Cl 2 /BCl 3 /Ar ICP etching under different plasma conditions. The reverse leakage current in the mesa diodes showed a strong relationship to chamber pressure, ion energy, and plasma flux. Plasma induced damage was minimized at moderate flux conditions (≤ 500 W), pressures ≥2 mTorr, and at ion energies below approximately -275 V

Performace of Dilute Nitride Triple Junction Space Solar Cell Grown by MBE

Directory of Open Access Journals (Sweden)

Aho Arto

2017-01-01

Full Text Available Dilute nitride arsenide antimonide compounds offer widely tailorable band-gaps, ranging from 0.8 eV to 1.4 eV, for the development of lattice-matched multijunction solar cells with three or more junctions. Here we report on the performance of GaInP/GaAs/GaInNAsSb solar cell grown by molecular beam epitaxy. An efficiency of 27% under AM0 conditions is demonstrated. In addition, the cell was measured at different temperatures. The short circuit current density exhibited a temperature coefficient of 0.006 mA/cm2/°C while the corresponding slope for the open circuit voltage was −6.8 mV/°C. Further efficiency improvement, up to 32%, is projected by better current balancing and structural optimization.

Comparative study of polar and semipolar (112¯2) InGaN layers grown by metalorganic vapour phase epitaxy

International Nuclear Information System (INIS)

Dinh, Duc V.; Zubialevich, V. Z.; Oehler, F.; Kappers, M. J.; Humphreys, C. J.; Alam, S. N.; Parbrook, P. J.; Caliebe, M.; Scholtz, F.

2014-01-01

InGaN layers were grown simultaneously on (112 ¯ 2) GaN and (0001) GaN templates by metalorganic vapour phase epitaxy. At higher growth temperature (≥750 °C), the indium content ( ¯ 2) and (0001) InGaN layers was similar. However, for temperatures less than 750 °C, the indium content of the (112 ¯ 2) InGaN layers (15%–26%) were generally lower than those with (0001) orientation (15%–32%). The compositional deviation was attributed to the different strain relaxations between the (112 ¯ 2) and (0001) InGaN layers. Room temperature photoluminescence measurements of the (112 ¯ 2) InGaN layers showed an emission wavelength that shifts gradually from 380 nm to 580 nm with decreasing growth temperature (or increasing indium composition). The peak emission wavelength of the (112 ¯ 2) InGaN layers with an indium content of more than 10% blue-shifted a constant value of ≈(50–60) nm when using higher excitation power densities. This blue-shift was attributed to band filling effects in the layers.

GaN-based vertical-cavity surface-emitting lasers with tunnel junction contacts grown by metal-organic chemical vapor deposition

Science.gov (United States)

Lee, SeungGeun; Forman, Charles A.; Lee, Changmin; Kearns, Jared; Young, Erin C.; Leonard, John T.; Cohen, Daniel A.; Speck, James S.; Nakamura, Shuji; DenBaars, Steven P.

2018-06-01

We report the first demonstration of III–nitride vertical-cavity surface-emitting lasers (VCSELs) with tunnel junction (TJ) intracavity contacts grown completely by metal–organic chemical vapor deposition (MOCVD). For the TJs, n++-GaN was grown on in-situ activated p++-GaN after buffered HF surface treatment. The electrical properties and epitaxial morphologies of the TJs were first investigated on TJ LED test samples. A VCSEL with a TJ intracavity contact showed a lasing wavelength of 408 nm, a threshold current of ∼15 mA (10 kA/cm2), a threshold voltage of 7.8 V, a maximum output power of 319 µW, and a differential efficiency of 0.28%.

Elimination of trench defects and V-pits from InGaN/GaN structures

International Nuclear Information System (INIS)

Smalc-Koziorowska, Julita; Grzanka, Ewa; Czernecki, Robert; Schiavon, Dario; Leszczyński, Mike

2015-01-01

The microstructural evolution of InGaN/GaN multiple quantum wells grown by metalorganic chemical vapor phase epitaxy was studied as a function of the growth temperature of the GaN quantum barriers (QBs). We observed the formation of basal stacking faults (BSFs) in GaN QBs grown at low temperature. The presence of BSFs terminated by stacking mismatch boundaries (SMBs) leads to the opening of the structure at the surface into a V-shaped trench loop. This trench may form above an SMB, thereby terminating the BSF, or above a junction between the SMB and a subsequent BSF. Fewer BSFs and thus fewer trench defects were observed in GaN QBs grown at temperatures higher than 830 °C. Further increase in the growth temperature of the GaN QBs led to the suppression of the threading dislocation opening into V-pits

Effect of diffusion from a lateral surface on the rate of GaN nanowire growth

International Nuclear Information System (INIS)

Sibirev, N. V.; Tchernycheva, M.; Cirlin, G. E.; Patriarche, G.; Harmand, J. C.; Dubrovskii, V. G.

2012-01-01

The kinetics of the growth of GaN crystalline nanowires on a Si (111) surface with no catalyst is studied experimentally and theoretically. Noncatalytic GaN nanowires were grown by molecular-beam epitaxy with AlN inserts, which makes it possible to determine the rate of the vertical growth of nanowires. A model for the formation of GaN nanowires is developed, and an expression for their rate of growth is derived. It is shown that, in the general case, the dependence of the rate of growth on the nanowire diameter has a minimum. The diameter corresponding to the experimentally observed minimum of the rate of growth steadily increases with increasing diffusion flux from the lateral surface.

AlGaN nanocolumns and AlGaN/GaN/AlGaN nanostructures grown by molecular beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Ristic, J.; Sanchez-Garcia, M.A.; Ulloa, J.M.; Calleja, E. [Departamento de Ingenieria Electronica, ETSI Telecomunicacion, Universidad Politecnica de Madrid, Ciudad Universitaria, 28040 Madrid (Spain); Sanchez-Paramo, J.; Calleja, J.M. [Departamento de Fisica de Materiales, Universidad Autonoma de Madrid, Cantoblanco, 28049 Madrid (Spain); Jahn, U.; Trampert, A.; Ploog, K.H. [Paul-Drude-Institut fuer Festkoerperelektronik, Hausvogteiplatz 5-7, 10117 Berlin (Germany)

2002-12-01

This work reports on the characterization of hexagonal, single crystal AlGaN nanocolumns with diameters in the range of 30 to 100 nm grown by molecular beam epitaxy on Si(111) substrates. The change of the flux ratio between the Al and the total III-element controls the alloy composition. The Al composition trend versus the Al flux is consistent both with the E{sub 2} phonon energy values measured by inelastic light scattering and the luminescence emission peaks position. High quality low dimensional AlGaN/GaN/AlGaN heterostructures with five GaN quantum discs, 2 and 4 nm thick, embedded into the AlGaN columns, were designed in order to study the quantum confinement effects. (Abstract Copyright [2002], Wiley Periodicals, Inc.)

Self-organization of dislocation-free, high-density, vertically aligned GaN nanocolumns involving InGaN quantum wells on graphene/SiO2 covered with a thin AlN buffer layer

International Nuclear Information System (INIS)

Hayashi, Hiroaki; Konno, Yuta; Kishino, Katsumi

2016-01-01

We demonstrated the self-organization of high-density GaN nanocolumns on multilayer graphene (MLG)/SiO 2 covered with a thin AlN buffer layer by RF-plasma-assisted molecular beam epitaxy. MLG/SiO 2 substrates were prepared by the transfer of CVD graphene onto thermally oxidized SiO 2 /Si [100] substrates. Employing the MLG with an AlN buffer layer enabled the self-organization of high-density and vertically aligned nanocolumns. Transmission electron microscopy observation revealed that no threading dislocations, stacking faults, or twinning defects were included in the self-organized nanocolumns. The photoluminescence (PL) peak intensities of the self-organized GaN nanocolumns were 2.0–2.6 times higher than those of a GaN substrate grown by hydride vapor phase epitaxy. Moreover, no yellow luminescence or ZB-phase GaN emission was observed from the nanocolumns. An InGaN/GaN MQW and p-type GaN were integrated into GaN nanocolumns grown on MLG, displaying a single-peak PL emission at a wavelength of 533 nm. Thus, high-density nitride p–i–n nanocolumns were fabricated on SiO 2 /Si using the transferred MLG interlayer, indicating the possibility of developing visible nanocolumn LEDs on graphene/SiO 2 . (paper)

X-ray absorption near-edge structure of GaN with high Mn concentration grown on SiC

Energy Technology Data Exchange (ETDEWEB)

Sancho-Juan, O; Cantarero, A; Garro, N; Cros, A [Materials Science Institute, University of Valencia, PO Box 22085, E46071 Valencia (Spain); Martinez-Criado, G; Salome, M; Susini, J [European Synchrotron Radiation Facility, 6 rue Jules Horowitz, 38043 Grenoble (France); Olguin, D [Dept. de Fisica, CINVESTAV-IPN, 07300 Mexico D F (Mexico); Dhar, S [Experimentalphysik, Universitaet Duisburg-Essen, Lotharstrasse 1, 47057 Duisburg (Germany)

2009-07-22

By means of x-ray absorption near-edge structure (XANES) several Ga{sub 1-x}Mn{sub x}N (0.03GaN samples consisted of different epilayers grown by molecular beam epitaxy on [0001] SiC substrates. The low mismatch between GaN and SiC allows for a good quality and homogeneity of the material. The measurements were performed in fluorescence mode around both the Ga and Mn K edges. All samples studied present a similar Mn ionization state, very close to 2+, and tetrahedral coordination. In order to interpret the near-edge structure, we have performed ab initio calculations using the full potential linear augmented plane wave method as implemented in the Wien2k code. The calculations show the appearance of a Mn bonding t{sub 2}arrow up band localized in the gap region, and the corresponding anti-bonding state t{sub 2}arrow down, which seem to be responsible for the double structure which appears at the pre-edge absorption region. The shoulders and main absorption peak of the XANES spectra are attributed to transitions from the Mn(1s) band to the conduction bands, which are partially dipole allowed because of the Mn(4p) contribution to these bands.

Bi-epitaxial tilted out-of-plane YBCO junctions on NdGaO{sub 3} substrates with YSZ seeding layer

Energy Technology Data Exchange (ETDEWEB)

Mozhaev, P.B. (Institute of Physics and Technology RAS, Moscow (Russian Federation)); Mozhaev, J.E.; Bindslev Hansen, J.; Jacobsen, C.S. (Technical Univ. of Denmark, Dept. of Physics, Kgs. Lyngby (Denmark)); Kotelyanskil, I.M.; Luzanov, V.A. (Institute of Radio Engineering and Electronics RAS, Moscow (Russian Federation)); Benacka, S.; Strbik, V. (Institute of Electrical Engineering SAS, Bratislava (SK))

2008-10-15

Bi-epitaxial junctions with out-of plane tilt of the c axis were fabricated of YBCO superconducting thin films on NdGaO{sub 3} substrates with different miscut angles. Bi-epitaxial growth was provided by implementation of an Y:ZrO{sub 2} seeding layer on a certain part of the substrate. Junctions with different orientation of the bi-epitaxial boundaries were fabricated, their DC electrical properties were studied as a function of the boundary orientation angle. The junctions showed extremely high critical current densities for all tested miscut angles and bi-epitaxial boundary orientations (about 105 A/cm2 at 77 K and up to 106 A/cm2 at 4.2 K). The dependence of critical current density on the bi-epitaxial boundary orientation angle may be explained as an effect of a d-wave pairing mechanism in the HTSC with the simple Sigrist-Rice model. The studied boundaries may be considered as model structures for the grain boundaries in the coated conductors. (au)

Determination of carrier diffusion length in GaN

Science.gov (United States)

Hafiz, Shopan; Zhang, Fan; Monavarian, Morteza; Avrutin, Vitaliy; Morkoç, Hadis; Özgür, Ümit; Metzner, Sebastian; Bertram, Frank; Christen, Jürgen; Gil, Bernard

2015-01-01

Diffusion lengths of photo-excited carriers along the c-direction were determined from photoluminescence (PL) and cross-sectional cathodoluminescence (CL) measurements in p- and n-type GaN epitaxial layers grown on c-plane sapphire by metal-organic chemical vapor deposition. The investigated samples incorporate a 6 nm thick In0.15Ga0.85N active layer capped with either 500 nm p-GaN or 1500 nm n-GaN. The top GaN layers were etched in steps and PL from the InGaN active region and the underlying layers was monitored as a function of the top GaN thickness upon photo-generation near the surface region by above bandgap excitation. Taking into consideration the absorption in the top GaN layer as well as active and underlying layers, the diffusion lengths at 295 K and at 15 K were measured to be 93 ± 7 nm and 70 ± 7 nm for Mg-doped p-type GaN and 432 ± 30 nm and 316 ± 30 nm for unintentionally doped n-type GaN, respectively, at photogenerated carrier densities of 4.2 × 1018 cm-3 using PL spectroscopy. CL measurements of the unintentionally doped n-type GaN layer at much lower carrier densities of 1017 cm-3 revealed a longer diffusion length of 525 ± 11 nm at 6 K.

Phonon deformation potentials of hexagonal GaN studied by biaxial stress modulation

Directory of Open Access Journals (Sweden)

Jun-Yong Lu

2011-09-01

Full Text Available In this work, a biaxial stress modulation method, combining the microfabrication technique, finite element analysis and a weighted averaging process, was developed to study piezospectroscopic behavior of hexagonal GaN films, epitaxially grown by metalorganic chemical vapor deposition on c-sapphire and Si (111 substrates. Adjusting the size of patterned islands, various biaxial stress states could be obtained at the island centers, leading to abundant stress-Raman shift data. With the proposed stress modulation method, the Raman biaxial stress coefficients of E2H and A1 (LO phonons of GaN were determined to be 3.43 cm-1/GPa and 2.34 cm-1/GPa, respectively.

Control of ion content and nitrogen species using a mixed chemistry plasma for GaN grown at extremely high growth rates >9 μm/h by plasma-assisted molecular beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Gunning, Brendan P.; Clinton, Evan A.; Merola, Joseph J.; Doolittle, W. Alan, E-mail: alan.doolittle@ece.gatech.edu [Georgia Institute of Technology, Atlanta, Georgia 30332 (United States); Bresnahan, Rich C. [Veeco Instruments, St. Paul, Minnesota 55127 (United States)

2015-10-21

Utilizing a modified nitrogen plasma source, plasma assisted molecular beam epitaxy (PAMBE) has been used to achieve higher growth rates in GaN. A higher conductance aperture plate, combined with higher nitrogen flow and added pumping capacity, resulted in dramatically increased growth rates up to 8.4 μm/h using 34 sccm of N{sub 2} while still maintaining acceptably low operating pressure. It was further discovered that argon could be added to the plasma gas to enhance growth rates up to 9.8 μm/h, which was achieved using 20 sccm of N{sub 2} and 7.7 sccm Ar flows at 600 W radio frequency power, for which the standard deviation of thickness was just 2% over a full 2 in. diameter wafer. A remote Langmuir style probe employing the flux gauge was used to indirectly measure the relative ion content in the plasma. The use of argon dilution at low plasma pressures resulted in a dramatic reduction of the plasma ion current by more than half, while high plasma pressures suppressed ion content regardless of plasma gas chemistry. Moreover, different trends are apparent for the molecular and atomic nitrogen species generated by varying pressure and nitrogen composition in the plasma. Argon dilution resulted in nearly an order of magnitude achievable growth rate range from 1 μm/h to nearly 10 μm/h. Even for films grown at more than 6 μm/h, the surface morphology remained smooth showing clear atomic steps with root mean square roughness less than 1 nm. Due to the low vapor pressure of Si, Ge was explored as an alternative n-type dopant for high growth rate applications. Electron concentrations from 2.2 × 10{sup 16} to 3.8 × 10{sup 19} cm{sup −3} were achieved in GaN using Ge doping, and unintentionally doped GaN films exhibited low background electron concentrations of just 1–2 × 10{sup 15} cm{sup −3}. The highest growth rates resulted in macroscopic surface features due to Ga cell spitting, which is an engineering challenge still to be

Control of ion content and nitrogen species using a mixed chemistry plasma for GaN grown at extremely high growth rates >9 μm/h by plasma-assisted molecular beam epitaxy

International Nuclear Information System (INIS)

Gunning, Brendan P.; Clinton, Evan A.; Merola, Joseph J.; Doolittle, W. Alan; Bresnahan, Rich C.

2015-01-01

Utilizing a modified nitrogen plasma source, plasma assisted molecular beam epitaxy (PAMBE) has been used to achieve higher growth rates in GaN. A higher conductance aperture plate, combined with higher nitrogen flow and added pumping capacity, resulted in dramatically increased growth rates up to 8.4 μm/h using 34 sccm of N 2 while still maintaining acceptably low operating pressure. It was further discovered that argon could be added to the plasma gas to enhance growth rates up to 9.8 μm/h, which was achieved using 20 sccm of N 2 and 7.7 sccm Ar flows at 600 W radio frequency power, for which the standard deviation of thickness was just 2% over a full 2 in. diameter wafer. A remote Langmuir style probe employing the flux gauge was used to indirectly measure the relative ion content in the plasma. The use of argon dilution at low plasma pressures resulted in a dramatic reduction of the plasma ion current by more than half, while high plasma pressures suppressed ion content regardless of plasma gas chemistry. Moreover, different trends are apparent for the molecular and atomic nitrogen species generated by varying pressure and nitrogen composition in the plasma. Argon dilution resulted in nearly an order of magnitude achievable growth rate range from 1 μm/h to nearly 10 μm/h. Even for films grown at more than 6 μm/h, the surface morphology remained smooth showing clear atomic steps with root mean square roughness less than 1 nm. Due to the low vapor pressure of Si, Ge was explored as an alternative n-type dopant for high growth rate applications. Electron concentrations from 2.2 × 10 16 to 3.8 × 10 19 cm −3 were achieved in GaN using Ge doping, and unintentionally doped GaN films exhibited low background electron concentrations of just 1–2 × 10 15 cm −3 . The highest growth rates resulted in macroscopic surface features due to Ga cell spitting, which is an engineering challenge still to be addressed. Nonetheless, the

High-quality AlGaN/GaN grown on sapphire by gas-source molecular beam epitaxy using a thin low-temperature AlN layer

Energy Technology Data Exchange (ETDEWEB)

Jurkovic, M.J.; Li, L.K.; Turk, B.; Wang, W.I.; Syed, S.; Simonian, D.; Stormer, H.L.

2000-07-01

Growth of high-quality AlGaN/GaN heterostructures on sapphire by ammonia gas-source molecular beam epitaxy is reported. Incorporation of a thin AlN layer grown at low temperature within the GaN buffer is shown to result in enhanced electrical and structural characteristics for subsequently grown heterostructures. AlGaN/GaN structures exhibiting reduced background doping and enhanced Hall mobilities (2100, 10310 and 12200 cm{sup 2}/Vs with carrier sheet densities of 6.1 x 10{sup 12} cm{sup {minus}2}, and 5.8 x 10{sup 12} cm{sup {minus}2} at 300 K, 77 K, and 0.3 K, respectively) correlate with dislocation filtering in the thin AlN layer. Magnetotransport measurements at 0.3 K reveal well-resolved Shubnikov-de Haas oscillations starting at 3 T.

GaN membrane MSM ultraviolet photodetectors

Science.gov (United States)

Muller, A.; Konstantinidis, G.; Kostopoulos, A.; Dragoman, M.; Neculoiu, D.; Androulidaki, M.; Kayambaki, M.; Vasilache, D.; Buiculescu, C.; Petrini, I.

2006-12-01

GaN exhibits unique physical properties, which make this material very attractive for wide range of applications and among them ultraviolet detection. For the first time a MSM type UV photodetector structure was manufactured on a 2.2 μm. thick GaN membrane obtained using micromachining techniques. The low unintentionally doped GaN layer structure was grown by MOCVD on high resistivity (ρ>10kΩcm) oriented silicon wafers, 500μm thick. The epitaxially grown layers include a thin AlN layer in order to reduce the stress in the GaN layer and avoid cracking. Conventional contact lithography, e-gun Ni/Au (10nm /200nm) evaporation and lift-off techniques were used to define the interdigitated Schottky metalization on the top of the wafer. Ten digits with a width of 1μm and a length of 100μm were defined for each electrode. The distance between the digits was also 1μm. After the backside lapping of the wafer to a thickness of approximately 150μm, a 400nm thick Al layer was patterned and deposited on the backside, to be used as mask for the selective reactive ion etching of silicon. The backside mask, for the membrane formation, was patterned using double side alignment techniques and silicon was etched down to the 2.2μm thin GaN layer using SF 6 plasma. A very low dark current (30ρA at 3V) was obtained. Optical responsivity measurements were performed at 1.5V. A maximum responsivity of 18mA/W was obtained at a wavelength of 370nm. This value is very good and can be further improved using transparent contacts for the interdigitated structure.

The dependence of Raman scattering on Mg concentration in Mg-doped GaN grown by MBE

International Nuclear Information System (INIS)

Flynn, Chris; Lee, William

2014-01-01

Magnesium-doped GaN (GaN:Mg) films having Mg concentrations in the range 5 × 10 18 –5 × 10 20 cm −3 were fabricated by molecular beam epitaxy. Raman spectroscopy was employed to study the effects of Mg incorporation on the positions of the E 2 and A 1 (LO) lines identifiable in the Raman spectra. For Mg concentrations in excess of 2 × 10 19 cm −3 , increases in the Mg concentration shift both lines to higher wave numbers. The shifts of the Raman lines reveal a trend towards compressive stress induced by incorporation of Mg into the GaN films. The observed correlation between the Mg concentration and the Raman line positions establish Raman spectroscopy as a useful tool for optimizing growth of Mg-doped GaN. (papers)

Characteristics of Mg-doped and In-Mg co-doped p-type GaN epitaxial layers grown by metal organic chemical vapour deposition

International Nuclear Information System (INIS)

Chung, S J; Lee, Y S; Suh, E-K; Senthil Kumar, M; An, M H

2010-01-01

Mg-doped and In-Mg co-doped p-type GaN epilayers were grown using the metal organic chemical vapour deposition technique. The effect of In co-doping on the physical properties of p-GaN layer was examined by high resolution x-ray diffraction (HRXRD), transmission electron microscopy (TEM), Hall effect, photoluminescence (PL) and persistent photoconductivity (PPC) at room temperature. An improved crystalline quality and a reduction in threading dislocation density are evidenced upon In doping in p-GaN from HRXRD and TEM images. Hole conductivity, mobility and carrier density also significantly improved by In co-doping. PL studies of the In-Mg co-doped sample revealed that the peak position is blue shifted to 3.2 eV from 2.95 eV of conventional p-GaN and the PL intensity is increased by about 25%. In addition, In co-doping significantly reduced the PPC effect in p-type GaN layers. The improved electrical and optical properties are believed to be associated with the active participation of isolated Mg impurities.

Determination of carrier diffusion length in p- and n-type GaN

Science.gov (United States)

Hafiz, Shopan; Metzner, Sebastian; Zhang, Fan; Monavarian, Morteza; Avrutin, Vitaliy; Morkoç, Hadis; Karbaum, Christopher; Bertram, Frank; Christen, Jürgen; Gil, Bernard; Özgür, Ümit

2014-03-01

Diffusion lengths of photo-excited carriers along the c-direction were determined from photoluminescence (PL) measurements in p- and n-type GaN epitaxial layers grown on c-plane sapphire by metal-organic chemical vapor deposition. The investigated samples incorporate a 6 nm thick In0.15Ga0.85N active layer capped with either 500 nm p- GaN or 1300 nm n-GaN. The top GaN layers were etched in steps and PL from the InGaN active region and the underlying layers was monitored as a function of the top GaN thickness upon photogeneration near the surface region by above bandgap excitation. Taking into consideration the absorption in the active and underlying layers, the diffusion lengths at 295 K and at 15 K were measured to be about 92 ± 7 nm and 68 ± 7 nm for Mg-doped p-type GaN and 432 ± 30 nm and 316 ± 30 nm for unintentionally doped n-type GaN, respectively. Cross-sectional cathodoluminescence line-scan measurement was performed on a separate sample and the diffusion length in n-type GaN was measured to be 280 nm.

Three-dimensionally structured silicon as a substrate for the MOVPE growth of GaN nanoLEDs

Energy Technology Data Exchange (ETDEWEB)

Fuendling, Soenke; Li, Shunfeng; Soekmen, Uensal; Merzsch, Stephan; Peiner, Erwin; Wehmann, Hergo-Heinrich; Waag, Andreas [Institut fuer Halbleitertechnik, TU Braunschweig, Braunschweig (Germany); Hinze, Peter; Weimann, Thomas [Physikalisch-Technische Bundesanstalt (PTB), Braunschweig (Germany); Jahn, Uwe; Trampert, Achim; Riechert, Henning [Paul-Drude-Institut fuer Festkoerperelektronik, Berlin (Germany)

2009-06-15

Three-dimensionally patterned Si(111) substrates are used to grow GaN based heterostructures by metalorganic vapour phase epitaxy, with the goal of fabricating well controlled, defect reduced GaN-based nanoLEDs. In contrast to other approaches to achieve GaN nanorods, we employed silicon substrates with deep etched nanopillars to control the GaN nanorods growth by varying the size and distance of the Si pillars. The small footprint of GaN nanorods grown on Si pillars minimise the influence of the lattice mismatched substrate and improve the material quality. For the Si pillars an inductively coupled plasma dry-etching process at cryogenic temperature has been developed. An InGaN/GaN multi quantum well (MQW) structure has been incorporated into the GaN nanorods. We found GaN nanostructures grown on top of the silicon pillars with a pyramidal shape. This shape results from a competitive growth on different facets as well as from surface diffusion of the growth species. Spatially resolved optical properties of the structures are analysed by cathodoluminescence. Strongly spatial-dependent MQW emission spectra indicate the growth rate differences on top of the rods. (copyright 2009 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

High temperature refractive indices of GaN

Energy Technology Data Exchange (ETDEWEB)

Liu, C.; Stepanov, S.; Gott, A.; Shields, P.A.; Zhirnov, E.; Wang, W.N. [Department of Physics, University of Bath, Bath, BA2 7AY (United Kingdom); Steimetz, E.; Zettler, J.T. [LayTec, Helmholtzstr. 13-14, 10587 Berlin (Germany)

2006-06-15

Undoped GaN (u-GaN) films were grown by low pressure metalorganic vapour phase epitaxy (LP-MOVPE) on sapphire substrates. In situ optical monitoring was applied to the growth process either using a LayTec EpiR-DA TT spectroscopic reflectometer or Filmetrics F30. Refractive indices of u-GaN films at 1060 C were obtained in a spectral range from 370-900 nm. A peak at 412{+-}5 nm in refractive index spectra was observed, which most likely corresponds to the band-gap of hexagonal GaN at a temperature of 1060 C. Refractive indices below this band-gap are fitted well to the first-order Sellmeier formula. As an example of the applications of the refractive indices, the effective film thicknesses of GaN during the resumption from 3 dimensional (3D) to 2 dimensional (2D) growth have been calculated from the spectra recorded by a LayTec system using the optical constants obtained. (copyright 2006 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

Surface morphology of homoepitaxial GaN grown on non- and semipolar GaN substrates

Energy Technology Data Exchange (ETDEWEB)

Wernicke, Tim; Hoffmann, Veit; Netzel, Carsten; Knauer, Arne; Weyers, Markus [FBH, Berlin (Germany); Ploch, Simon; Rass, Jens [Institute of Solid State Physics, TU Berlin (Germany); Schade, Lukas; Schwarz, Ulrich [IAF, Freiburg (Germany); Kneissl, Michael [FBH, Berlin (Germany); Institute of Solid State Physics, TU Berlin (Germany)

2010-07-01

Recently a number of groups have reported laser diodes in the green spectral range on semi- and nonpolar GaN. Nevertheless the growth process on semipolar surfaces is not well understood. In this study 3.5 {mu} m thick MOVPE grown GaN layers on bulk m-plane, (11 anti 22), (10 anti 12), and (10 anti 11) GaN substrates were investigated. XRD rocking curves exhibit a FWHM of less than 150{sup ''}, indicating excellent crystalline quality. But the surface morphology exhibits hillocks with a height of 1 {mu}m and lateral extension of 150 {mu}m in many cases. Depending on the substrate orientation and the growth temperature different hillock shapes were observed. Morphology and luminescence data point to threading dislocations as formation sources. In QWs the hillock structure is reproduced in the emission intensity and wavelength distribution on (10 anti 11) but not on the m-plane surfaces. The hillocks could be eliminated for the semipolar planes (not for the m-plane) by increasing the reactor pressure and lowering the growth temperature. Hillock free separate confinement laser structures emitting at 405 nm feature a very homogeneous luminescence in micro-PL and show amplified spontaneous emission under high power stripe excitation. Furthermore the In incorporation was found to be highest in QWs on (10 anti 11).

Photoreflectance study of strained GaAsN/GaAs T-junction quantum wires grown by metal-organic vapor phase epitaxy.

Science.gov (United States)

Klangtakai, Pawinee; Sanorpim, Sakuntam; Onabe, Kentaro

2011-12-01

Strained GaAsN T-junction quantum wires (T-QWRs) with different N contents grown on GaAs by two steps metal-organic vapor phase epitaxy in [001] and [110] directions, namely QW1 and QW2 respectively, have been investigated by photoreflectance (PR) spectroscopy. Two GaAsN T-QWRs with different N contents were formed by T-intersection of (i) a 6.4-nm-thick GaAs0.89N0.011 QW1 and a 5.2-nm-thick GaAs0.968N0.032 QW2 and (ii) a 5.0-nm-thick GaAs0.985N0.015 QW1 and a 5.2-nm-thick GaAs0.968N0.032 QW2. An evidence of a one-dimensional structure at T-intersection of the two QWs on the (001) and (110) surfaces was established by PR resonances associated with extended states in all the QW and T-QWR samples. It is found that larger lateral confinement energy than 100 meV in both of [001] and [110] directions were achieved for GaAsN T-QWRs. With increasing temperature, the transition energy of GaAsN T-QWRs decreases with a faster shrinking rate compared to that of bulk GaAs. Optical quality of GaAsN T-QWRs is found to be affected by the N-induced band edge fluctuation, which is the unique characteristic of dilute III-V-nitrides.

Heteroepitaxial growth of In-face InN on GaN (0001) by plasma-assisted molecular-beam epitaxy

International Nuclear Information System (INIS)

Dimakis, E.; Iliopoulos, E.; Tsagaraki, K.; Kehagias, Th.; Komninou, Ph.; Georgakilas, A.

2005-01-01

The thermodynamic aspects of indium-face InN growth by radio frequency plasma-assisted molecular-beam epitaxy (rf-MBE) and the nucleation of InN on gallium-face GaN (0001) surface were investigated. The rates of InN decomposition and indium desorption from the surface were measured in situ using reflected high-energy electron diffraction and the rf-MBE 'growth window' of In-face InN (0001) was identified. It is shown that sustainable growth can be achieved only when the arrival rate of active nitrogen species on the surface is higher than the arrival rate of indium atoms. The maximum substrate temperature permitting InN growth as a function of the active nitrogen flux was determined. The growth mode of InN on Ga-face GaN (0001) surface was investigated by reflected high-energy electron diffraction and atomic force microscopy. It was found to be of the Volmer-Weber-type for substrate temperatures less than 350 deg. C and of the Stranski-Krastanov for substrate temperatures between 350 and 520 deg. C. The number of monolayers of initial two-dimensional growth, in the case of Stranski-Krastanov mode, varies monotonically with substrate temperature, from 2 ML at 400 deg. C to about 12 ML at 500 deg. C. The evolution and coalescence of nucleated islands were also investigated as a function of substrate temperature. It was found that at higher temperature their coalescence is inhibited leading to porous-columnar InN thin films, which exhibit growth rates higher than the nominal value. Therefore, in order to achieve continuous InN layers on GaN (0001) a two-step growth approach is introduced. In that approach, InN is nucleated at low temperatures on GaN and the growth continues until full coalescence of the nucleated islands. Subsequently, this nucleation layer is overgrown at higher substrate temperature in order to achieve high-quality continuous films. The InN films grown by the two-step method were investigated by x-ray diffraction, Hall-effect measurements, and

Integration of epitaxial Pb(Zr{sub 0.52}Ti{sub 0.48})O{sub 3} films on GaN/AlGaN/GaN/Si(111) substrates using rutile TiO{sub 2} buffer layers

Energy Technology Data Exchange (ETDEWEB)

Elibol, K. [MESA + Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500AE Enschede (Netherlands); Nguyen, M.D. [MESA + Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500AE Enschede (Netherlands); SolMateS B.V., Drienerlolaan 5, Building 6, 7522NB Enschede (Netherlands); International Training Institute for Materials Science, Hanoi University of Science and Technology, No.1 Dai Co Viet road, Hanoi 10000 (Viet Nam); Hueting, R.J.E. [MESA + Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500AE Enschede (Netherlands); Gravesteijn, D.J. [MESA + Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500AE Enschede (Netherlands); NXP Semiconductors Research, High Tech Campus 46, 5656AE Eindhoven (Netherlands); Koster, G., E-mail: g.koster@utwente.nl [MESA + Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500AE Enschede (Netherlands); Rijnders, G. [MESA + Institute for Nanotechnology, University of Twente, P.O. Box 217, 7500AE Enschede (Netherlands)

2015-09-30

The integration of ferroelectric layers on gallium nitride (GaN) offers a great potential for various applications. Lead zirconate titanate (PZT), in particular Pb(Zr{sub 0.52}Ti{sub 0.48})O{sub 3}, is an interesting candidate. For that a suitable buffer layer should be grown on GaN in order to prevent the reaction between PZT and GaN, and to obtain PZT with a preferred orientation and phase. Here, we study pulsed laser deposited (100) rutile titanium oxide (R-TiO{sub 2}) as a potential buffer layer candidate for ferroelectric PZT. For this purpose, the growth, morphology and the surface chemical composition of R-TiO{sub 2} films were analyzed by reflection high-energy electron diffraction, atomic force microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy. We find optimally (100) oriented R-TiO{sub 2} growth on GaN (0002) using a 675 °C growth temperature and 2 Pa O{sub 2} deposition pressure as process conditions. More importantly, the R-TiO{sub 2} buffer layer grown on GaN/Si substrates prevents the unwanted formation of the PZT pyrochlore phase. Finally, the remnant polarization and coercive voltage of the PZT film on TiO{sub 2}/GaN/Si with an interdigitated-electrode structure were found to be 25.6 μC/cm{sup 2} and 8.1 V, respectively. - Highlights: • Epitaxial rutile TiO{sub 2} films were grown on GaN layer buffered Si substrate using pulsed laser deposition. • The rutile-TiO{sub 2} layer suppresses the formation of the pyrochlore phase in the epitaxial PZT film grown on GaN/Si. • An epitaxial PZT film on GaN/Si substrate with rutile TiO{sub 2} buffer layer exhibits good ferroelectric properties.

Study of epitaxial lateral overgrowth of semipolar (1 1 − 2 2) GaN by using different SiO2 pattern sizes

International Nuclear Information System (INIS)

Song, Ki-Ryong; Lee, Jae-Hwan; Han, Sang-Hyun; Yi, Hye-Rin; Lee, Sung-Nam

2013-01-01

Graphical abstract: - Highlights: • We examine comparative studies of semipolar ELO-GaN film. • Semipolar ELO-GaN film was grown by three step growth method. • The achievement of smooth surface morphology of semipolar ELO-GaN. • The crystal and optical properties was significantly improved by ELO process. - Abstract: We investigated the growth mode and the crystal properties of lateral epitaxial overgrowth (LEO) semipolar (1 1 − 2 2) GaN by using the various SiO 2 pattern sizes of 6, 8, 10 and 12 μm with the window width of 4.0 μm. By using three-step growth technique, we successfully obtained the fully-coalescenced semipolar (1 1 − 2 2) LEO-GaN films regardless of the SiO 2 pattern sizes. However, the coalescence thickness of LEO-GaN film was decreased with decreasing SiO 2 pattern size, indicating that the coalescence of semipolar (1 1 − 2 2) GaN was easily formed by decreasing the pattern size of SiO 2 mask. The full width at half maximums (FWHMs) of X-ray rocking curves (XRCs) of LEO-GaN films decreased with increasing SiO 2 pattern size. In the pattern size of 4 × 10 μm, we achieved the minimum XRCs FWHM of 537 and 368 arc s with two different X-ray incident beam directions of [1 1 − 2 − 3] and [1 − 1 0 0], respectively. Moreover, the photoluminescence bandedge emission of semipolar (1 1 − 2 2) GaN was 45 times increased by LEO process. Based on these results, we concluded that the LEO pattern size of 4 × 10 μm would effectively decrease crystal defects of semipolar (1 1 − 2 2) GaN epilayer, resulting in an improvement of the optical properties

Formation of helical dislocations in ammonothermal GaN substrate by heat treatment

International Nuclear Information System (INIS)

Horibuchi, Kayo; Yamaguchi, Satoshi; Kimoto, Yasuji; Nishikawa, Koichi; Kachi, Tetsu

2016-01-01

GaN substrate produced by the basic ammonothermal method and an epitaxial layer on the substrate was evaluated using synchrotron radiation x-ray topography and transmission electron microscopy. We revealed that the threading dislocations present in the GaN substrate are deformed into helical dislocations and the generation of the voids by heat treatment in the substrate for the first observation in the GaN crystal. These phenomena are formed by the interactions between the dislocations and vacancies. The helical dislocation was formed in the substrate region, and not in the epitaxial layer region. Furthermore, the evaluation of the influence of the dislocations on the leakage current of Schottky barrier diodes fabricated on the epitaxial layer is discussed. The dislocations did not affect the leakage current characteristics of the epitaxial layer. Our results suggest that the deformation of dislocations in the GaN substrate does not adversely affect the epitaxial layer. (paper)

Anatase thin film with diverse epitaxial relationship grown on yttrium stabilized zirconia substrate by chemical vapor deposition

International Nuclear Information System (INIS)

Miyagi, Takahira; Ogawa, Tomoyuki; Kamei, Masayuki; Wada, Yoshiki; Mitsuhashi, Takefumi; Yamazaki, Atsushi

2003-01-01

An anatase epitaxial thin film with diverse epitaxial relationship, YSZ (001) // anatase (001), YSZ (010) // anatase (110), was grown on a single crystalline yttrium stabilized zirconia (YSZ) (001) substrate by metal organic chemical vapor deposition (MOCVD). The full width at half maximum (FWHM) of the (004) reflection of this anatase epitaxial film was 0.4deg, and the photoluminescence of this anatase epitaxial film showed visible emission with broad spectral width and large Stokes shift at room temperature. These results indicate that this anatase epitaxial film possessed almost equal crystalline quality compared with that grown under identical growth conditions on single crystalline SrTiO 3 substrate. (author)

High temperature dielectric function of silicon, germanium and GaN

Energy Technology Data Exchange (ETDEWEB)

Leyer, Martin; Pristovsek, Markus; Kneissl, Michael [Technische Universitaet Berlin (Germany). Institut fuer Festkoerperphysik

2010-07-01

In the last few years accurate values for the optical properties of silicon, germanium and GaN at high temperatures have become important as a reference for in-situ analysis, e.g. reflectometry. Precise temperature dependent dielectric measurements are necessary for the growth of GaInP/GaInAs/Ge triple-junction solar cells and the hetero epitaxy of GaN on silicon and sapphire. We performed spectroscopic ellipsometry (SE) measurements of the dielectric function of silicon, germanium and GaN between 1.5 eV and 6.5 eV in the temperature range from 300 K to 1300 K. The Samples were deoxidized chemically or by heating. High resolution SE spectra were taken every 50 K while cooling down to room temperature. The temperature dependence of the critical energies is compared to literature. Measurements for germanium showed a shift of the E{sub 2} critical point of {proportional_to}0.1 eV toward lower energies. The reason for this behavior is a non-negligible oxide layer on the samples in the literature.

Site-selective spectroscopy of Er in GaN

International Nuclear Information System (INIS)

Dierolf, V.; Sandmann, C.; Zavada, J.; Chow, P.; Hertog, B.

2004-01-01

We investigated different Er 3+ defect sites found in Er-doped GaN layers by site-selective combined excitation-emission spectroscopy and studied the role of these sites in different direct and multistep excitation schemes. The layers were grown by molecular beam epitaxy and were 200 nm thick. Two majority sites were found along with several minority sites. The sites strongly differ in excitation and energy transfer efficiencies as well as branching ratios during relaxation. For this reason, relative emission intensities from these sites depend strongly on emission and excitation. The sites were identified for several transitions and a comprehensive list of energy levels has been compiled. One of the minority sites appears strongly under ultraviolet excitation above the GaN band gap suggesting that this site is an excellent trap for excitation energy of electron-hole pairs

Epitaxial growth of GaN by radical-enhanced metalorganic chemical vapor deposition (REMOCVD) in the downflow of a very high frequency (VHF) N2/H2 excited plasma - effect of TMG flow rate and VHF power

Science.gov (United States)

Lu, Yi; Kondo, Hiroki; Ishikawa, Kenji; Oda, Osamu; Takeda, Keigo; Sekine, Makoto; Amano, Hiroshi; Hori, Masaru

2014-04-01

Gallium nitride (GaN) films have been grown by using our newly developed Radical-Enhanced Metalorganic Chemical Vapor Deposition (REMOCVD) system. This system has three features: (1) application of very high frequency (60 MHz) power in order to increase the plasma density, (2) introduction of H2 gas together with N2 gas in the plasma discharge region to generate not only nitrogen radicals but also active NHx molecules, and (3) radical supply under remote plasma arrangement with suppression of charged ions and photons by employing a Faraday cage. Using this new system, we have studied the effect of the trimethylgallium (TMG) source flow rate and of the plasma generation power on the GaN crystal quality by using scanning electron microscopy (SEM) and double crystal X-ray diffraction (XRD). We found that this REMOCVD allowed the growth of epitaxial GaN films of the wurtzite structure of (0001) orientation on sapphire substrates with a high growth rate of 0.42 μm/h at a low temperature of 800 °C. The present REMOCVD is a promising method for GaN growth at relatively low temperature and without using costly ammonia gas.

Liquid phase epitaxy of abrupt junctions in InAs and studies of injection radiative tunneling processes

International Nuclear Information System (INIS)

Bull, D.J.

1977-01-01

The p-n junction in a InAs crystal, by liquid phase epitaxy is obtained. The processes of injection and tunneling radiative recombination by emitted radiation from active region of p-n junction for low injection current are studied. (M.C.K.) [pt

Deep levels in as-grown and electron-irradiated n-type GaN studied by deep level transient spectroscopy and minority carrier transient spectroscopy

Energy Technology Data Exchange (ETDEWEB)

Duc, Tran Thien [Department of Physics, Chemistry and Biology (IFM), Linköping University, S-581 83 Linköping (Sweden); School of Engineering Physics, Hanoi University of Science and Technology, 1 Dai Co Viet Road, Hanoi (Viet Nam); Pozina, Galia; Son, Nguyen Tien; Kordina, Olof; Janzén, Erik; Hemmingsson, Carl [Department of Physics, Chemistry and Biology (IFM), Linköping University, S-581 83 Linköping (Sweden); Ohshima, Takeshi [Japan Atomic Energy Agency (JAEA), Takasaki, Gunma 370-1292 (Japan)

2016-03-07

Development of high performance GaN-based devices is strongly dependent on the possibility to control and understand defects in material. Important information about deep level defects is obtained by deep level transient spectroscopy and minority carrier transient spectroscopy on as-grown and electron irradiated n-type bulk GaN with low threading dislocation density produced by halide vapor phase epitaxy. One hole trap labelled H1 (E{sub V} + 0.34 eV) has been detected on as-grown GaN sample. After 2 MeV electron irradiation, the concentration of H1 increases and at fluences higher than 5 × 10{sup 14 }cm{sup −2}, a second hole trap labelled H2 is observed. Simultaneously, the concentration of two electron traps, labelled T1 (E{sub C} – 0.12 eV) and T2 (E{sub C} – 0.23 eV), increases. By studying the increase of the defect concentration versus electron irradiation fluence, the introduction rate of T1 and T2 using 2 MeV- electrons was determined to be 7 × 10{sup −3 }cm{sup −1} and 0.9 cm{sup −1}, respectively. Due to the low introduction rate of T1, it is suggested that the defect is associated with a complex. The high introduction rate of trap H1 and T2 suggests that the defects are associated with primary intrinsic defects or complexes. Some deep levels previously observed in irradiated GaN layers with higher threading dislocation densities are not detected in present investigation. It is therefore suggested that the absent traps may be related to primary defects segregated around dislocations.

Photoelectrochemical liftoff of LEDs grown on freestanding c-plane GaN substrates

KAUST Repository

Hwang, David

2016-09-23

We demonstrate a thin-film flip-chip (TFFC) process for LEDs grown on freestanding c-plane GaN substrates. LEDs are transferred from a bulk GaN substrate to a sapphire submount via a photoelectrochemical (PEC) undercut etch. This PEC liftoff method allows for substrate reuse and exposes the N-face of the LEDs for additional roughening. The LEDs emitted at a wavelength of 432 nm with a turn on voltage of ~3 V. Etching the LEDs in heated KOH after transferring them to a sapphire submount increased the peak external quantum efficiency (EQE) by 42.5% from 9.9% (unintentionally roughened) to 14.1% (intentionally roughened).

Influence of structural properties on ballistic transport in nanoscale epitaxial graphene cross junctions

International Nuclear Information System (INIS)

Bock, Claudia; Weingart, Sonja; Karaissaridis, Epaminondas; Kunze, Ulrich; Speck, Florian; Seyller, Thomas

2012-01-01

In this paper we investigate the influence of material and device properties on the ballistic transport in epitaxial monolayer graphene and epitaxial quasi-free-standing monolayer graphene. Our studies comprise (a) magneto-transport in two-dimensional (2D) Hall bars, (b) temperature- and magnetic-field-dependent bend resistance of unaligned and step-edge-aligned orthogonal cross junctions, and (c) the influence of the lead width of the cross junctions on ballistic transport. We found that ballistic transport is highly sensitive to scattering at the step edges of the silicon carbide substrate. A suppression of the ballistic transport is observed if the lead width of the cross junction is reduced from 50 nm to 30 nm. In a 50 nm wide device prepared on quasi-free-standing graphene we observe a gradual transition from the ballistic into the diffusive transport regime if the temperature is increased from 4.2 to about 50 K, although 2D Hall bars show a temperature-independent mobility. Thus, in 1D devices additional temperature-dependent scattering mechanisms play a pivotal role. (paper)

Large lattice relaxation deep levels in neutron-irradiated GaN

International Nuclear Information System (INIS)

Li, S.; Zhang, J.D.; Beling, C.D.; Wang, K.; Wang, R.X.; Gong, M.; Sarkar, C.K.

2005-01-01

Deep level transient spectroscopy (DLTS) and deep level optical spectroscopy (DLOS) measurements have been carried out in neutron-irradiated n-type hydride-vapor-phase-epitaxy-grown GaN. A defect center characterized by a DLTS line, labeled as N1, is observed at E C -E T =0.17 eV. Another line, labeled as N2, at E C -E T =0.23 eV, seems to be induced at the same rate as N1 under irradiation and may be identified with E1. Other defects native to wurtzite GaN such as the C and E2 lines appear to enhance under neutron irradiation. The DLOS results show that the defects N1 and N2 have large Frank-Condon shifts of 0.64 and 0.67 eV, respectively, and hence large lattice relaxations. The as-grown and neutron-irradiated samples all exhibit the persistent photoconductivity effect commonly seen in GaN that may be attributed to DX centers. The concentration of the DX centers increases significantly with neutron dosage and is helpful in sustaining sample conductivity at low temperatures, thus making possible DLTS measurements on N1 an N2 in the radiation-induced deep-donor defect compensated material which otherwise are prevented by carrier freeze-out

Van der Waals epitaxial growth and optoelectronics of large-scale WSe2/SnS2 vertical bilayer p-n junctions.

Science.gov (United States)

Yang, Tiefeng; Zheng, Biyuan; Wang, Zhen; Xu, Tao; Pan, Chen; Zou, Juan; Zhang, Xuehong; Qi, Zhaoyang; Liu, Hongjun; Feng, Yexin; Hu, Weida; Miao, Feng; Sun, Litao; Duan, Xiangfeng; Pan, Anlian

2017-12-04

High-quality two-dimensional atomic layered p-n heterostructures are essential for high-performance integrated optoelectronics. The studies to date have been largely limited to exfoliated and restacked flakes, and the controlled growth of such heterostructures remains a significant challenge. Here we report the direct van der Waals epitaxial growth of large-scale WSe 2 /SnS 2 vertical bilayer p-n junctions on SiO 2 /Si substrates, with the lateral sizes reaching up to millimeter scale. Multi-electrode field-effect transistors have been integrated on a single heterostructure bilayer. Electrical transport measurements indicate that the field-effect transistors of the junction show an ultra-low off-state leakage current of 10 -14 A and a highest on-off ratio of up to 10 7 . Optoelectronic characterizations show prominent photoresponse, with a fast response time of 500 μs, faster than all the directly grown vertical 2D heterostructures. The direct growth of high-quality van der Waals junctions marks an important step toward high-performance integrated optoelectronic devices and systems.

GaN microrod sidewall epitaxial lateral overgrowth on a close-packed microrod template

Science.gov (United States)

Duan, Xiaoling; Zhang, Jincheng; Xiao, Ming; Zhang, Jinfeng; Hao, Yue

2018-05-01

We demonstrate a GaN growth method using microrod sidewall epitaxial lateral overgrowth (MSELO) on a close-packed microrod template by a nonlithographic technique. The density and distribution of threading dislocations were determined by the density and distribution of microrods and the nucleation model. MSELO exhibited two different nucleation models determined by the direction and degree of substrate misorientation and the sidewall curvature: one-sidewall and three-sidewall nucleation, predicting the dislocation density values. As a result, the threading dislocation density was markedly decreased from 2 × 109 to 5 × 107 cm‑2 with a small coalescence thickness of ∼2 µm for the close-packed 3000 nm microrod sample.

Cu-doped AlN: A possible spinaligner at room-temperature grown by molecular beam epitaxy?

Science.gov (United States)

Ganz, P. R.; Schaadt, D. M.

2011-12-01

Cu-doped AlN was prepared by plasma assisted molecular beam epitaxy on C-plane sapphire substrates. The growth conditions were investigated for different Cu to Al flux ratios from 1.0% to 4.0%. The formation of Cu-Al alloys on the surface was observed for all doping level. In contrast to Cu-doped GaN, all samples showed diamagnetic behavior determined by SQUID measurements.

In-situ grazing incidence X-ray diffraction measurements of relaxation in Fe/MgO/Fe epitaxial magnetic tunnel junctions during annealing

Energy Technology Data Exchange (ETDEWEB)

Eastwood, D.S. [Department of Physics, Durham University, South Road, Durham DH1 3LE (United Kingdom); Ali, M.; Hickey, B.J. [Department of Physics and Astronomy, University of Leeds, Leeds LS2 1JT (United Kingdom); Tanner, B.K., E-mail: b.k.tanner@dur.ac.uk [Department of Physics, Durham University, South Road, Durham DH1 3LE (United Kingdom)

2013-12-15

The relaxation of Fe/MgO/Fe tunnel junctions grown epitaxially on (001) MgO substrates has been measured by in-situ grazing incidence in-plane X-ray diffraction during the thermal annealing cycle. We find that the Fe layers are fully relaxed and that there are no irreversible changes during annealing. The MgO tunnel barrier is initially strained towards the Fe but on annealing, relaxes and expands towards the bulk MgO value. The strain dispersion is reduced in the MgO by about 40% above 480 K post-annealing. There is no significant change in the “twist” mosaic. Our results indicate that the final annealing stage of device fabrication, crucial to attainment of high TMR, induces substantial strain relaxation at the MgO barrier/lower Fe electrode interface. - Highlights: • Lattice relaxation of Fe/MgO/Fe epitaxial magnetic tunnel junctions measured. • In-plane lattice parameter of Fe equal to bulk value; totally relaxed. • MgO barrier initially strained towards the Fe but relaxes on annealing. • Reduction in strain dispersion in the MgO barrier by 40% above about 470 K. • No change in the in-plane “twist” mosaic throughout the annealing cycle.

TEM EDS analysis of epitaxially-grown self-assembled indium islands

Directory of Open Access Journals (Sweden)

Jasmine Sears

2017-05-01

Full Text Available Epitaxially-grown self-assembled indium nanostructures, or islands, show promise as nanoantennas. The elemental composition and internal structure of indium islands grown on gallium arsenide are explored using Transmission Electron Microscopy (TEM Energy Dispersive Spectroscopy (EDS. Several sizes of islands are examined, with larger islands exhibiting high (>94% average indium purity and smaller islands containing inhomogeneous gallium and arsenic contamination. These results enable more accurate predictions of indium nanoantenna behavior as a function of growth parameters.

Transparent Semiconductor-Superconductor Interface and Induced Gap in an Epitaxial Heterostructure Josephson Junction

NARCIS (Netherlands)

Kjaergaard, M.; Suominen, H. J.; Nowak, M.P.; Akhmerov, A.R.; Shabani, J.; Palmstrøm, C. J.; Nichele, F.; Marcus, C.M.

2017-01-01

Measurement of multiple Andreev Reflection (MAR) in a Josephson junction made from an InAs quantum well heterostructure with epitaxial aluminum is used to quantify a highly transparent effective semiconductor-superconductor interface with near-unity transmission. The observed temperature

The structural and optical properties of metal ion-implanted GaN

Energy Technology Data Exchange (ETDEWEB)

Macková, A.; Malinský, P. [Nuclear Physics Institute of the Academy of Sciences of the Czech Republic, v.v.i., 250 68 Řež (Czech Republic); Department of Physics, Faculty of Science, J.E. Purkinje University, České Mládeže 8, 400 96 Ústí nad Labem (Czech Republic); Sofer, Z.; Šimek, P.; Sedmidubský, D. [Department of Inorganic Chemistry, Institute of Chemical Technology, 166 28 Prague (Czech Republic); Veselý, M. [Dept. of Organic Technology, University of Chemistry and Technology Prague, Technická 5, 166 28 Prague 6 (Czech Republic); Böttger, R. [Institute of Ion Beam Physics and Materials Research, Helmholtz-Zentrum Dresden – Rossendorf, 01328 Dresden (Germany)

2016-03-15

The practical development of novel optoelectronic materials with appropriate optical properties is strongly connected to the structural properties of the prepared doped structures. We present GaN layers oriented along the (0 0 0 1) crystallographic direction that have been grown by low-pressure metal–organic vapour-phase epitaxy (MOVPE) on sapphire substrates implanted with 200 keV Co{sup +}, Fe{sup +} and Ni{sup +} ions. The structural properties of the ion-implanted layers have been characterised by RBS-channelling and Raman spectroscopy to obtain a comprehensive insight into the structural modification of implanted GaN layers and to study the subsequent influence of annealing on crystalline-matrix recovery. Photoluminescence was measured to control the desired optical properties. The post-implantation annealing induced the structural recovery of the modified GaN layer depending on the introduced disorder level, e.g. depending on the ion implantation fluence, which was followed by structural characterisation and by the study of the surface morphology by AFM.

Investigation of the GaN-on-GaAs interface for vertical power device applications

International Nuclear Information System (INIS)

Möreke, Janina; Uren, Michael J.; Kuball, Martin; Novikov, Sergei V.; Foxon, C. Thomas; Hosseini Vajargah, Shahrzad; Wallis, David J.; Humphreys, Colin J.; Haigh, Sarah J.; Al-Khalidi, Abdullah; Wasige, Edward; Thayne, Iain

2014-01-01

GaN layers were grown onto (111) GaAs by molecular beam epitaxy. Minimal band offset between the conduction bands for GaN and GaAs materials has been suggested in the literature raising the possibility of using GaN-on-GaAs for vertical power device applications. I-V and C-V measurements of the GaN/GaAs heterostructures however yielded a rectifying junction, even when both sides of the junction were heavily doped with an n-type dopant. Transmission electron microscopy analysis further confirmed the challenge in creating a GaN/GaAs Ohmic interface by showing a large density of dislocations in the GaN layer and suggesting roughening of the GaN/GaAs interface due to etching of the GaAs by the nitrogen plasma, diffusion of nitrogen or melting of Ga into the GaAs substrate.

Investigation of the GaN-on-GaAs interface for vertical power device applications

Energy Technology Data Exchange (ETDEWEB)

Möreke, Janina, E-mail: janina.moereke@bristol.ac.uk; Uren, Michael J.; Kuball, Martin [H.H. Wills Physics Laboratory, Tyndall Avenue, Bristol BS8 1TL (United Kingdom); Novikov, Sergei V.; Foxon, C. Thomas [Department of Physics and Astronomy, University of Nottingham, Nottingham NG7 2RD (United Kingdom); Hosseini Vajargah, Shahrzad; Wallis, David J.; Humphreys, Colin J. [Department of Materials Science and Metallurgy, University of Cambridge, 27 Charles Babbage Road, Cambridge CB3 0FS (United Kingdom); Haigh, Sarah J. [Super STEM Laboratory, STFC Daresbury Campus, Keckwick Lane, Daresbury WA4 4AD (United Kingdom); School of Materials, University of Manchester, Manchester M13 9PL (United Kingdom); Al-Khalidi, Abdullah; Wasige, Edward; Thayne, Iain [School of Engineering, University of Glasgow, Rankine Bldg, Oakfield Avenue, Glasgow G12 8LT (United Kingdom)

2014-07-07

GaN layers were grown onto (111) GaAs by molecular beam epitaxy. Minimal band offset between the conduction bands for GaN and GaAs materials has been suggested in the literature raising the possibility of using GaN-on-GaAs for vertical power device applications. I-V and C-V measurements of the GaN/GaAs heterostructures however yielded a rectifying junction, even when both sides of the junction were heavily doped with an n-type dopant. Transmission electron microscopy analysis further confirmed the challenge in creating a GaN/GaAs Ohmic interface by showing a large density of dislocations in the GaN layer and suggesting roughening of the GaN/GaAs interface due to etching of the GaAs by the nitrogen plasma, diffusion of nitrogen or melting of Ga into the GaAs substrate.

Characterization of low-frequency noise in molecular beam epitaxy-grown GaN epilayers deposited on double buffer layers

International Nuclear Information System (INIS)

Fong, W.K.; Ng, S.W.; Leung, B.H.; Surya, Charles

2003-01-01

We report the growth of high-mobility Si-doped GaN epilayers utilizing unique double buffer layer (DBL) structures, which consist of a thin buffer layer and a thick GaN intermediate-temperature buffer layer (ITBL). In this study, three types of DBL were investigated: (i) thin GaN low-temperature buffer layer/GaN ITBL (type I); (ii) nitridated Ga metal film/GaN ITBL (type II); and (iii) thin AlN high-temperature buffer layer/GaN ITBL (type III). Systematic measurements were conducted on the electron mobilities and the low-frequency noise over a wide range of temperatures. It is found that the electron mobilities of the GaN films are substantially improved with the use of DBLs, with the sample using type III DBL which exhibits the highest low-temperature mobility. Furthermore, the same sample also demonstrates the elimination of deep levels at 91 and 255 meV below the conduction band. This is believed to result from the relaxation of tensile stress during growth with the use of type III DBLs

A submillimetre-wave SIS mixer using NbN/MgO/NbN trilayers grown epitaxially on an MgO substrate

CERN Document Server

Uzawa, Y; Saito, A; Takeda, M; Wang, Z

2002-01-01

We have designed, fabricated and tested a quasi-optical superconductor-insulator-superconductor (SIS) mixer employing distributed NbN/MgO/NbN tunnel junctions and NbN/MgO/NbN microstriplines at submillimetre-wave frequencies. These trilayers were fabricated by dc- and rf-magnetron sputtering on an MgO substrate at ambient temperature so that the NbN and MgO films were grown epitaxially. Our SIS mixer consists of an MgO hyperhemispherical lens with an antireflection cap and a self-complementary log-periodic antenna made of a single-crystal NbN film, on which the distributed SIS junctions and the two-section impedance transformers were mirror-symmetrically placed at the feed point of the antenna. As designed, the junctions are 0.6 mu m wide and 15.5 mu m long, which is sufficient to absorb the incoming signal along this lossy transmission line, assuming a current density of 10 kA cm sup - sup 2. The mixer showed good I-V characteristics, with subgap-to-normal resistance ratios of about 13, although weak-link br...

Photoluminescence and photoluminescence excitation studies in 80 MeV Ni ion irradiated MOCVD grown GaN

Energy Technology Data Exchange (ETDEWEB)

Devaraju, G. [School of Physics, University of Hyderabad, Central University P.O., Hyderabad 500 046 (India); Pathak, A.P., E-mail: appsp@uohyd.ernet.in [School of Physics, University of Hyderabad, Central University P.O., Hyderabad 500 046 (India); Srinivasa Rao, N.; Saikiran, V. [School of Physics, University of Hyderabad, Central University P.O., Hyderabad 500 046 (India); Enrichi, Francesco [Coordinamento Interuniversitario Veneto per le Nanotecnologie (CIVEN), via delle Industrie 5, Marghera, I-30175Venice (Italy); Trave, Enrico [Dipartimento di Chimica Fisica, Universita Ca' Foscari Venezia, Dorsoduro 2137, I-30123 Venice (Italy)

2011-09-01

Highlights: {yields} MOCVD grown GaN samples are irradiated with 80 MeV Ni ions at room temperature. {yields} PL and PLE studies have been carried out for band to band, BL and YL emissions. {yields} Ni ions irradiated GaN shows BL band at 450 nm besides YL band. {yields} Radiation annealed Ga vacancies have quenching effect on YL intensity. {yields} We speculated that BL and YL are associated with N and Ga vacancies, respectively. - Abstract: We report damage creation and annihilation under energetic ion bombardment at a fixed fluence. MOCVD grown GaN thin films were irradiated with 80 MeV Ni ions at a fluence of 1 x 10{sup 13} ions/cm{sup 2}. Irradiated GaN thin films were subjected to rapid thermal annealing for 60 s in nitrogen atmosphere to anneal out the defects. The effects of defects on luminescence were explored with photoluminescence measurements. Room temperature photoluminescence spectra from pristine sample revealed presence of band to band transition besides unwanted yellow luminescence. Irradiated GaN does not show any band to band transition but there is a strong peak at 450 nm which is attributed to ion induced defect blue luminescence. However, irradiated and subsequently annealed samples show improved band to band transitions and a significant decrease in yellow luminescence intensity due to annihilation of defects which were created during irradiation. Irradiation induced effects on yellow and blue emissions are discussed.

Investigation of GaN LED with Be-implanted Mg-doped GaN layer

International Nuclear Information System (INIS)

Huang, H.-W.; Kao, C.C.; Chu, J.T.; Kuo, H.C.; Wang, S.C.; Yu, C.C.; Lin, C.F.

2004-01-01

We report the electrical and optical characteristics of GaN light emitting diode (LED) with beryllium (Be) implanted Mg-doped GaN layer. The p-type layer of Be-implanted GaN LED showed a higher hole carrier concentration of 2.3 x 10 18 cm -3 and low specific contact resistance value of 2.0 x 10 -4 Ωcm 2 than as-grown p-GaN LED samples without Be-implantation. The Be-implanted GaN LEDs with InGaN/GaN MQW show slightly lower light output (about 10%) than the as-grown GaN LEDs, caused by the high RTA temperature annealing process

Photoemission electronic states of epitaxially grown magnetite films

International Nuclear Information System (INIS)

Zalecki, R.; Kolodziejczyk, A.; Korecki, J.; Spiridis, N.; Zajac, M.; Kozlowski, A.; Kakol, Z.; Antolak, D.

2007-01-01

The valence band photoemission spectra of epitaxially grown 300 A single crystalline magnetite films were measured by the angle-resolved ultraviolet photoemission spectroscopy (ARUPS) at 300 K. The samples were grown either on MgO(0 0 1) (B termination) or on (0 0 1) Fe (iron-rich A termination), thus intentionally presenting different surface stoichiometry, i.e. also different surface electronic states. Four main features of the electron photoemission at about -1.0, -3.0, -5.5 and -10.0 eV below a chemical potential show systematic differences for two terminations; this difference depends on the electron outgoing angle. Our studies confirm sensitivity of angle resolved PES technique on subtleties of surface states

Metalorganic chemical vapor deposition growth of high-mobility AlGaN/AlN/GaN heterostructures on GaN templates and native GaN substrates

Energy Technology Data Exchange (ETDEWEB)

Chen, Jr-Tai, E-mail: jrche@ifm.liu.se; Hsu, Chih-Wei; Forsberg, Urban; Janzén, Erik [Department of Physics, Chemistry, and Biology (IFM), Linköping University, SE 581 83 Linköping (Sweden)

2015-02-28

Severe surface decomposition of semi-insulating (SI) GaN templates occurred in high-temperature H{sub 2} atmosphere prior to epitaxial growth in a metalorganic chemical vapor deposition system. A two-step heating process with a surface stabilization technique was developed to preserve the GaN template surface. Utilizing the optimized heating process, a high two-dimensional electron gas mobility ∼2000 cm{sup 2}/V·s was obtained in a thin AlGaN/AlN/GaN heterostructure with an only 100-nm-thick GaN spacer layer homoepitaxially grown on the GaN template. This technique was also demonstrated viable for native GaN substrates to stabilize the surface facilitating two-dimensional growth of GaN layers. Very high residual silicon and oxygen concentrations were found up to ∼1 × 10{sup 20 }cm{sup −3} at the interface between the GaN epilayer and the native GaN substrate. Capacitance-voltage measurements confirmed that the residual carbon doping controlled by growth conditions of the GaN epilayer can be used to successfully compensate the donor-like impurities. State-of-the-art structural properties of a high-mobility AlGaN/AlN/GaN heterostructure was then realized on a 1 × 1 cm{sup 2} SI native GaN substrate; the full width at half maximum of the X-ray rocking curves of the GaN (002) and (102) peaks are only 21 and 14 arc sec, respectively. The surface morphology of the heterostructure shows uniform parallel bilayer steps, and no morphological defects were noticeable over the entire epi-wafer.

Mechanism of nucleation and growth of catalyst-free self-organized GaN columns by MOVPE

Science.gov (United States)

Wang, Xue; Li, Shunfeng; Fündling, Sönke; Wehmann, Hergo-H.; Strassburg, Martin; Lugauer, Hans-Jürgen; Steegmüller, Ulrich; Waag, Andreas

2013-05-01

The growth mechanism of catalyst-free self-organized GaN nuclei and three-dimensional columns on sapphire by metal organic vapour phase epitaxy (MOVPE) is investigated. Temperature- and time-dependent growth is performed. The growth behaviour can be characterized by two different kinetic regimes: mass-transport-limited growth and thermodynamically limited growth. The sum of activation energies for thermodynamic barrier of nucleation and for surface diffusion/mass-transport limitation, i.e. Whet +Ed, is 0.57 eV in the ‘low’-temperature region and 2.43 eV in the ‘high’-temperature region. GaN columns grown under the same conditions have very comparable height, which is not dependent on their diameter or the distance to other columns. Therefore, the growth rate is presumably limited by the incorporation rate on the top surface of columns. The height and diameter at the top of the GaN columns increase linearly with time and no height limit is observed. The GaN columns can reach more than 40 µm in height. Moreover, the investigated GaN columns are Ga-polar.

Low-leakage superconducting tunnel junctions with a single-crystal Al{sub 2}O{sub 3} barrier

Energy Technology Data Exchange (ETDEWEB)

Oh, S [National Institute of Standards and Technology, Boulder, CO 80305 (United States); Department of Physics, University of Illinois, Urbana, IL 61801 (United States); Cicak, K; Osborn, K D; Simmonds, R W; Pappas, D P [National Institute of Standards and Technology, Boulder, CO 80305 (United States); McDermott, R; Cooper, K B; Steffen, M; Martinis, J M [University of California, Santa Barbara, CA 93106 (United States)

2005-10-01

We have developed a two-step growth scheme for single-crystal Al{sub 2}O{sub 3} tunnel barriers. The barriers are epitaxially grown on single-crystal rhenium (Re) base electrodes that are grown epitaxially on a sapphire substrate, while polycrystalline Al is used as the top electrode. We show that by first growing an amorphous aluminium (Al) oxide layer at room temperature and crystallizing it at a high temperature in oxygen environment, a morphologically intact single-crystal Al{sub 2}O{sub 3} layer is obtained. Tunnel junctions fabricated from these trilayers show very low subgap leakage current. This single-crystal Al{sub 2}O{sub 3} junction may open a new venue for coherent quantum devices.

GaN/NbN epitaxial semiconductor/superconductor heterostructures

Science.gov (United States)

Yan, Rusen; Khalsa, Guru; Vishwanath, Suresh; Han, Yimo; Wright, John; Rouvimov, Sergei; Katzer, D. Scott; Nepal, Neeraj; Downey, Brian P.; Muller, David A.; Xing, Huili G.; Meyer, David J.; Jena, Debdeep

2018-03-01

Epitaxy is a process by which a thin layer of one crystal is deposited in an ordered fashion onto a substrate crystal. The direct epitaxial growth of semiconductor heterostructures on top of crystalline superconductors has proved challenging. Here, however, we report the successful use of molecular beam epitaxy to grow and integrate niobium nitride (NbN)-based superconductors with the wide-bandgap family of semiconductors—silicon carbide, gallium nitride (GaN) and aluminium gallium nitride (AlGaN). We apply molecular beam epitaxy to grow an AlGaN/GaN quantum-well heterostructure directly on top of an ultrathin crystalline NbN superconductor. The resulting high-mobility, two-dimensional electron gas in the semiconductor exhibits quantum oscillations, and thus enables a semiconductor transistor—an electronic gain element—to be grown and fabricated directly on a crystalline superconductor. Using the epitaxial superconductor as the source load of the transistor, we observe in the transistor output characteristics a negative differential resistance—a feature often used in amplifiers and oscillators. Our demonstration of the direct epitaxial growth of high-quality semiconductor heterostructures and devices on crystalline nitride superconductors opens up the possibility of combining the macroscopic quantum effects of superconductors with the electronic, photonic and piezoelectric properties of the group III/nitride semiconductor family.

High-Quality GaN Epilayers Achieved by Facet-Controlled Epitaxial Lateral Overgrowth on Sputtered AlN/PSS Templates.

Science.gov (United States)

He, Chenguang; Zhao, Wei; Zhang, Kang; He, Longfei; Wu, Hualong; Liu, Ningyang; Zhang, Shan; Liu, Xiaoyan; Chen, Zhitao

2017-12-13

It is widely believed that the lack of high-quality GaN wafers severely hinders the progress in GaN-based devices, especially for defect-sensitive devices. Here, low-cost AlN buffer layers were sputtered on cone-shaped patterned sapphire substrates (PSSs) to obtain high-quality GaN epilayers. Without any mask or regrowth, facet-controlled epitaxial lateral overgrowth was realized by metal-organic chemical vapor deposition. The uniform coating of the sputtered AlN buffer layer and the optimized multiple modulation guaranteed high growth selectivity and uniformity of the GaN epilayer. As a result, an extremely smooth surface was achieved with an average roughness of 0.17 nm over 3 × 3 μm 2 . It was found that the sputtered AlN buffer layer could significantly suppress dislocations on the cones. Moreover, the optimized three-dimensional growth process could effectively promote dislocation bending. Therefore, the threading dislocation density (TDD) of the GaN epilayer was reduced to 4.6 × 10 7 cm -2 , which is about an order of magnitude lower than the case of two-step GaN on the PSS. In addition, contamination and crack in the light-emitting diode fabricated on the obtained GaN were also effectively suppressed by using the sputtered AlN buffer layer. All of these advantages led to a high output power of 116 mW at 500 mA with an emission wavelength of 375 nm. This simple, yet effective growth technique is believed to have great application prospects in high-performance TDD-sensitive optoelectronic and electronic devices.

Polarization of stacking fault related luminescence in GaN nanorods

Directory of Open Access Journals (Sweden)

G. Pozina

2017-01-01

Full Text Available Linear polarization properties of light emission are presented for GaN nanorods (NRs grown along [0001] direction on Si(111 substrates by direct-current magnetron sputter epitaxy. The near band gap photoluminescence (PL measured at low temperature for a single NR demonstrated an excitonic line at ∼3.48 eV and the stacking faults (SFs related transition at ∼3.43 eV. The SF related emission is linear polarized in direction perpendicular to the NR growth axis in contrast to a non-polarized excitonic PL. The results are explained in the frame of the model describing basal plane SFs as polymorphic heterostructure of type II, where anisotropy of chemical bonds at the interfaces between zinc blende and wurtzite GaN subjected to in-built electric field is responsible for linear polarization parallel to the interface planes.

Characterisation of Cs ion implanted GaN by DLTS

Science.gov (United States)

Ngoepe, P. N. M.; Meyer, W. E.; Auret, F. D.; Omotoso, E.; Hlatshwayo, T. T.; Diale, M.

2018-04-01

Deep level transient spectroscopy (DLTS) was used to characterise Cs implanted GaN grown by hydride vapour phase epitaxy (HVPE). This implantation was done at room temperature using energy of 360 keV to a fluence of 10-11 cm-2. A defect with activation energy of 0.19 eV below the conduction band and an apparent capture cross section of 1.1 × 10-15 cm2 was induced. This defect has previously been observed after rare earth element (Eu, Er and Pr) implantation. It has also been reported after electron, proton and He ion implantation.

Optical excitation of Er centers in GaN epilayers grown by MOCVD

Science.gov (United States)

George, D. K.; Hawkins, M. D.; Jiang, H. X.; Lin, J. Y.; Zavada, J. M.; Vinh, N. Q.

2016-02-01

In this paper we present results of photoluminescence (PL), photoluminescence excitation (PLE), and time resolved PL spectroscopy of the 4I13/2 → 4I15/2 transition in Er optical centers in GaN epilayers grown by metal-organic chemical vapor deposition. Under resonance excitation via the higher-lying inner 4f shell transitions and band-to-band excitation of the semiconductor host, the PL and PLE spectra reveal an existence of two types of Er optical centers from isolated and the defect-related Er centers in GaN epilayers. These centers have different PL spectra, local defect environments, decay dynamics, and excitation cross-sections. The isolated Er optical center, which can be excited by either excitation mechanism, has the same decay dynamics, but possesses a much higher cross-section under band-to-band excitation. In contrast, the defect-related Er center can only be observed through band-to-band excitation but has the largest crosssection. Our results indicate pathways for efficient optical excitation of Er-doped GaN semiconductors.

Growing GaN LEDs on amorphous SiC buffer with variable C/Si compositions

Science.gov (United States)

Cheng, Chih-Hsien; Tzou, An-Jye; Chang, Jung-Hung; Chi, Yu-Chieh; Lin, Yung-Hsiang; Shih, Min-Hsiung; Lee, Chao-Kuei; Wu, Chih-I; Kuo, Hao-Chung; Chang, Chun-Yen; Lin, Gong-Ru

2016-01-01

The epitaxy of high-power gallium nitride (GaN) light-emitting diode (LED) on amorphous silicon carbide (a-SixC1−x) buffer is demonstrated. The a-SixC1−x buffers with different nonstoichiometric C/Si composition ratios are synthesized on SiO2/Si substrate by using a low-temperature plasma enhanced chemical vapor deposition. The GaN LEDs on different SixC1−x buffers exhibit different EL and C-V characteristics because of the extended strain induced interfacial defects. The EL power decays when increasing the Si content of SixC1−x buffer. The C-rich SixC1−x favors the GaN epitaxy and enables the strain relaxation to suppress the probability of Auger recombination. When the SixC1−x buffer changes from Si-rich to C-rich condition, the EL peak wavelengh shifts from 446 nm to 450 nm. Moreover, the uniform distribution contour of EL intensity spreads between the anode and the cathode because the traping density of the interfacial defect gradually reduces. In comparison with the GaN LED grown on Si-rich SixC1−x buffer, the device deposited on C-rich SixC1−x buffer shows a lower turn-on voltage, a higher output power, an external quantum efficiency, and an efficiency droop of 2.48 V, 106 mW, 42.3%, and 7%, respectively. PMID:26794268

Ultraviolet light-absorbing and emitting diodes consisting of a p-type transparent-semiconducting NiO film deposited on an n-type GaN homoepitaxial layer

Science.gov (United States)

Nakai, Hiroshi; Sugiyama, Mutsumi; Chichibu, Shigefusa F.

2017-05-01

Gallium nitride (GaN) and related (Al,Ga,In)N alloys provide practical benefits in the production of light-emitting diodes (LEDs) and laser diodes operating in ultraviolet (UV) to green wavelength regions. However, obtaining low resistivity p-type AlN or AlGaN of large bandgap energies (Eg) is a critical issue in fabricating UV and deep UV-LEDs. NiO is a promising candidate for useful p-type transparent-semiconducting films because its Eg is 4.0 eV and it can be doped into p-type conductivity of sufficiently low resistivity. By using these technologies, heterogeneous junction diodes consisting of a p-type transparent-semiconducting polycrystalline NiO film on an n-type single crystalline GaN epilayer on a low threading-dislocation density, free-standing GaN substrate were fabricated. The NiO film was deposited by using the conventional RF-sputtering method, and the GaN homoepitaxial layer was grown by metalorganic vapor phase epitaxy. They exhibited a significant photovoltaic effect under UV light and also exhibited an electroluminescence peak at 3.26 eV under forward-biased conditions. From the conduction and valence band (EV) discontinuities, the NiO/GaN heterointerface is assigned to form a staggered-type (TYPE-II) band alignment with the EV of NiO higher by 2.0 eV than that of GaN. A rectifying property that is consistent with the proposed band diagram was observed in the current-voltage characteristics. These results indicate that polycrystalline NiO functions as a hole-extracting and injecting layer of UV optoelectronic devices.

Growth temperature and dopant species effects on deep levels in Si grown by low temperature molecular beam epitaxy

International Nuclear Information System (INIS)

Chung, Sung-Yong; Jin, Niu; Rice, Anthony T.; Berger, Paul R.; Yu, Ronghua; Fang, Z-Q.; Thompson, Phillip E.

2003-01-01

Deep-level transient spectroscopy measurements were performed in order to investigate the effects of substrate growth temperature and dopant species on deep levels in Si layers during low-temperature molecular beam epitaxial growth. The structures studied were n + -p junctions using B doping for the p layer and p + -n junctions using P doping for the n layer. While the density of hole traps H1 (0.38-0.41 eV) in the B-doped p layers showed a clear increase with decreasing growth temperature from 600 to 370 degree sign C, the electron trap density was relatively constant. Interestingly, the minority carrier electron traps E1 (0.42-0.45 eV) and E2 (0.257 eV), found in the B-doped p layers, are similar to the majority carrier electron traps E11 (0.48 eV) and E22 (0.269 eV) observed in P-doped n layers grown at 600 degree sign C. It is hypothesized that these dominating electron traps are associated with pure divacancy defects and are independent of the dopant species

Morphological and microstructural stability of N-polar InAlN thin films grown on free-standing GaN substrates by molecular beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Hardy, Matthew T., E-mail: matthew.hardy.ctr@nrl.navy.mil; Storm, David F.; Downey, Brian P.; Katzer, D. Scott; Meyer, David J. [Electronics Science and Technology Division, Naval Research Laboratory, 4555 Overlook Avenue SW, Washington DC 20375 (United States); McConkie, Thomas O.; Smith, David J. [Department of Physics, Arizona State University, Tempe, Arizona 85287-1504 (United States); Nepal, Neeraj [Sotera Defense Solutions, 2200 Defense Hwy Suite 405, Crofton, Maryland 21114 (United States)

2016-03-15

The sensitivity of the surface morphology and microstructure of N-polar-oriented InAlN to variations in composition, temperature, and layer thickness for thin films grown by plasma-assisted molecular beam epitaxy (PAMBE) has been investigated. Lateral compositional inhomogeneity is present in N-rich InAlN films grown at low temperature, and phase segregation is exacerbated with increasing InN fraction. A smooth, step-flow surface morphology and elimination of compositional inhomogeneity can be achieved at a growth temperature 50 °C above the onset of In evaporation (650 °C). A GaN/AlN/GaN/200-nm InAlN heterostructure had a sheet charge density of 1.7 × 10{sup 13 }cm{sup −2} and no degradation in mobility (1760 cm{sup 2}/V s) relative to 15-nm-thick InAlN layers. Demonstration of thick-barrier high-electron-mobility transistors with good direct-current characteristics shows that device quality, thick InAlN layers can be successfully grown by PAMBE.

Morphological and microstructural stability of N-polar InAlN thin films grown on free-standing GaN substrates by molecular beam epitaxy

International Nuclear Information System (INIS)

Hardy, Matthew T.; Storm, David F.; Downey, Brian P.; Katzer, D. Scott; Meyer, David J.; McConkie, Thomas O.; Smith, David J.; Nepal, Neeraj

2016-01-01

The sensitivity of the surface morphology and microstructure of N-polar-oriented InAlN to variations in composition, temperature, and layer thickness for thin films grown by plasma-assisted molecular beam epitaxy (PAMBE) has been investigated. Lateral compositional inhomogeneity is present in N-rich InAlN films grown at low temperature, and phase segregation is exacerbated with increasing InN fraction. A smooth, step-flow surface morphology and elimination of compositional inhomogeneity can be achieved at a growth temperature 50 °C above the onset of In evaporation (650 °C). A GaN/AlN/GaN/200-nm InAlN heterostructure had a sheet charge density of 1.7 × 10 13  cm −2 and no degradation in mobility (1760 cm 2 /V s) relative to 15-nm-thick InAlN layers. Demonstration of thick-barrier high-electron-mobility transistors with good direct-current characteristics shows that device quality, thick InAlN layers can be successfully grown by PAMBE

Structural properties of In0.53Ga0.47As epitaxial films grown on Si (111) substrates by molecular beam epitaxy

International Nuclear Information System (INIS)

Gao, Fangliang; Wen, Lei; Zhang, Xiaona; Guan, Yunfang; Li, Jingling; Zhang, Shuguang; Li, Guoqiang

2015-01-01

In 0.53 Ga 0.47 As epitaxial films are grown on 2-inch diameter Si (111) substrates by growing a low-temperature In 0.4 Ga 0.6 As buffer layer using molecular beam epitaxy. The effect of the buffer layer thickness on the as-grown In 0.53 Ga 0.47 As films is characterized by X-ray diffraction, scanning electron microscopy, atomic force microscopy and transmission electron microscopy (TEM). It is revealed that the crystalline quality and surface morphology of as-grown In 0.53 Ga 0.47 As epilayer are strongly affected by the thickness of the In 0.4 Ga 0.6 As buffer layer. From TEM investigation, we understand that the type and the distribution of dislocations of the buffer layer and the as-grown In 0.53 Ga 0.47 As film are different. We have demonstrated that the In 0.4 Ga 0.6 As buffer layer with a thickness of 12 nm can advantageously release the lattice mismatch stress between the In 0.53 Ga 0.47 As and Si substrate, ultimately leading to a high-quality In 0.53 Ga 0.47 As epitaxial film with low surface roughness. - Highlights: • We provide a simple approach to achieve high-quality In 0.53 Ga 0.47 As films on Si. • An appropriate thickness of In 0.4 Ga 0.6 As buffer layer can release mismatch strain. • High-quality In 0.53 Ga 0.47 As film is grown on Si using 12-nm-thick buffer layer. • Smooth surface In 0.53 Ga 0.47 As film is grown on Si using 12-nm-thick buffer layer

Structural and optical properties of GaN thin films grown on Al2O3 substrates by MOCVD at different reactor pressures

International Nuclear Information System (INIS)

Guillén-Cervantes, A.; Rivera-Álvarez, Z.; López-López, M.; Ponce-Pedraza, A.; Guarneros, C.; Sánchez-Reséndiz, V.M.

2011-01-01

GaN thin films grown by MOCVD on (0 0 0 1) Al 2 O 3 substrates at different growth pressures were characterized by field-emission scanning electron microscopy, atomic force microscopy, micro-Raman, and photoluminescence at room temperature. It was found that there is an optimum pressure of 76 Torr at which the structural and optical properties of the GaN samples are superior. On the other hand samples grown at higher pressure exhibited hexagonal surface pits and surface spirals. The results showed that the growth pressure strongly influences the morphology, and significantly affects the structural and optical properties of the GaN epilayers.

InP tunnel junctions for InP/InGaAs tandem solar cells

Science.gov (United States)

Vilela, Mauro F.; Freundlich, Alex; Renaud, P.; Medelci, N.; Bensaoula, A.

1996-01-01

We report, for the first time, an epitaxially grown InP p(+)/n(++) tunnel junction. A diode with peak current densities up to 1600 A/cm and maximum specific resistivities (Vp/Ip - peak voltage to peak current ratio) in the range of 10(exp -4)Omega cm(exp 2) is obtained. This peak current density is comparable to the highest results previously reported for lattice matched In(0.53)Ga(0.47)As tunnel junctions. Both results were obtained using chemical beam epitaxy (CBE). In this paper we discuss the electrical characteristics of these tunnel diodes and how the growth conditions influence them.

Influence of the interface on growth rates in AlN/GaN short period superlattices via metal organic vapor phase epitaxy

Science.gov (United States)

Rodak, L. E.; Korakakis, D.

2011-11-01

AlN/GaN short period superlattices are well suited for a number of applications including, but not limited to, digital alloys, intersubband devices, and emitters. In this work, AlN/GaN superlattices with periodicities ranging from 10 to 20 Å have been grown via metal organic vapor phase epitaxy in order to investigate the influence of the interface on the binary alloy growth rates. The GaN growth rate at the interface was observed to decrease with increasing GaN thickness while the AlN growth rate remained constant. This has been attributed to a decrease in the decomposition rate of GaN at the hetero-interface as seen in other III-V hetero-structures.

Effects of film polarities on InN growth by molecular-beam epitaxy

International Nuclear Information System (INIS)

Xu, K.; Yoshikawa, A.

2003-01-01

Effects of the film polarity on InN growth were investigated in molecular-beam epitaxy (MBE). It was found that N-polarity InN could be grown at higher temperatures than In-polarity one. For the In-polarity films, which were grown on Ga-polar GaN template, the highest growth temperature was limited below 500 deg. C, and the surface morphology and crystal quality tended to be poor mainly because of the tolerated low growth temperature. While for the N-polarity InN films, which were grown on MBE-grown N-polar GaN, the growth temperature could be as high as 600 deg. C. The step-flow-like growth morphology was achieved for the InN films grown with N polarity at 580 deg. C. The resulting full widths of half maximum of x-ray rocking curve around InN (002) and (102) reflections were about 200-250 and 950-1100 arc sec, respectively. The photoluminescence of the InN films peaked at 0.697 eV. The recording Hall mobility of InN film grown in N polarity is 1400 cm 2 /V s with a background carrier concentration of 1.56x10 18 cm -3 at room temperature. For both-polarity films, we found N-rich condition was necessary for the stable InN growth

Epitaxially Grown Ultra-Flat Self-Assembling Monolayers with Dendrimers

Directory of Open Access Journals (Sweden)

Takane Imaoka

2018-02-01

Full Text Available Mono-molecular films formed by physical adsorption and dendrimer self-assembly were prepared on various substrate surfaces. It was demonstrated that a uniform dendrimer-based monolayer on the subnanometer scale can be easily constructed via simple dip coating. Furthermore, it was shown that an epitaxially grown monolayer film reflecting the crystal structure of the substrate (highly ordered pyrolytic graphite (HOPG can also be formed by aligning specific conditions.

Nonpolar a-plane GaN grown on r-plane sapphire using multilayer AlN buffer by metalorganic chemical vapor deposition

International Nuclear Information System (INIS)

Chiang, C.H.; Chen, K.M.; Wu, Y.H.; Yeh, Y.S.; Lee, W.I.; Chen, J.F.; Lin, K.L.; Hsiao, Y.L.; Huang, W.C.; Chang, E.Y.

2011-01-01

Mirror-like and pit-free non-polar a-plane (1 1 -2 0) GaN films are grown on r-plane (1 -1 0 2) sapphire substrates using metalorganic chemical vapor deposition (MOCVD) with multilayer high-low-high temperature AlN buffer layers. The buffer layer structure and film quality are essential to the growth of a flat, crack-free and pit-free a-plane GaN film. The multilayer AlN buffer structure includes a thin low-temperature-deposited AlN (LT-AlN) layer inserted into the high-temperature-deposited AlN (HT-AlN) layer. The results demonstrate that the multilayer AlN buffer structure can improve the surface morphology of the upper a-plane GaN film. The grown multilayer AlN buffer structure reduced the tensile stress on the AlN buffer layers and increased the compressive stress on the a-plane GaN film. The multilayer AlN buffer structure markedly improves the surface morphology of the a-plane GaN film, as revealed by scanning electron microscopy. The effects of various growth V/III ratios was investigated to obtain a-plane GaN films with better surface morphology. The mean roughness of the surface was 1.02 nm, as revealed by atomic force microscopy. Accordingly, the multilayer AlN buffer structure improves the surface morphology and facilitates the complete coalescence of the a-plane GaN layer.

Suppression of metastable-phase inclusion in N-polar (0001¯) InGaN/GaN multiple quantum wells grown by metalorganic vapor phase epitaxy

International Nuclear Information System (INIS)

Shojiki, Kanako; Iwabuchi, Takuya; Kuboya, Shigeyuki; Choi, Jung-Hun; Tanikawa, Tomoyuki; Hanada, Takashi; Katayama, Ryuji; Matsuoka, Takashi; Usami, Noritaka

2015-01-01

The metastable zincblende (ZB) phase in N-polar (0001 ¯ ) (−c-plane) InGaN/GaN multiple quantum wells (MQWs) grown by metalorganic vapor phase epitaxy is elucidated by the electron backscatter diffraction measurements. From the comparison between the −c-plane and Ga-polar (0001) (+c-plane), the −c-plane MQWs were found to be suffered from the severe ZB-phase inclusion, while ZB-inclusion is negligible in the +c-plane MQWs grown under the same growth conditions. The ZB-phase inclusion is a hurdle for fabricating the −c-plane light-emitting diodes because the islands with a triangular shape appeared on a surface in the ZB-phase domains. To improve the purity of stable wurtzite (WZ)-phase, the optimum conditions were investigated. The ZB-phase is dramatically eliminated with decreasing the V/III ratio and increasing the growth temperature. To obtain much-higher-quality MQWs, the thinner InGaN wells and the hydrogen introduction during GaN barriers growth were tried. Consequently, MQWs with almost pure WZ phase and with atomically smooth surface have been demonstrated

Thermal degradation of ohmic contacts on semipolar (11-22) GaN films grown on m-plane (1-100) sapphire substrates

International Nuclear Information System (INIS)

Kim, Doo Soo; Kim, Deuk Young; Seo, Yong Gon; Kim, Ji Hoon; Hwang, Sung Min; Baik, Kwang Hyeon

2012-01-01

Semipolar (11-22) GaN films were grown on m-plane (1-100) sapphire substrates by using metalorganic chemical vapor deposition. The line widths of the omega rocking curves of the semipolar GaN films were 498 arcsec along the [11-23] GaN direction and 908 arcsec along the [10-10] GaN direction. The properties of the Ti/Al/Ni/Au metal contact were investigated using transmission-line-method patterns oriented in both the [11-23] GaN and the [10-10] GaN directions of semipolar (11-22) GaN. The minimum specific contact resistance of ∼3.6 x 10 -4 Ω·cm -2 was obtained on as-deposited metal contacts. The Ohmic contact properties of semipolar (11-22) GaN became degraded with increasing annealing temperature above 400 .deg. C. The thermal degradation of the metal contacts may be attributed to the surface property of N-polarity on the semipolar (11-22) GaN films. Also, the semipolar (11-22) GaN films did not show clear anisotropic behavior of the electrical properties for different azimuthal angles.

Incorporation of Mg in Free-Standing HVPE GaN Substrates

Science.gov (United States)

Zvanut, M. E.; Dashdorj, J.; Freitas, J. A.; Glaser, E. R.; Willoughby, W. R.; Leach, J. H.; Udwary, K.

2016-06-01

Mg, the only effective p-type dopant for nitrides, is well studied in thin films due to the important role of the impurity in light-emitting diodes and high-power electronics. However, there are few reports of Mg in thick free-standing GaN substrates. Here, we demonstrate successful incorporation of Mg into GaN grown by hydride vapor-phase epitaxy (HVPE) using metallic Mg as the doping source. The concentration of Mg obtained from four separate growth runs ranged between 1016 cm-3 and 1019 cm-3. Raman spectroscopy and x-ray diffraction revealed that Mg did not induce stress or perturb the crystalline quality of the HVPE GaN substrates. Photoluminescence (PL) and electron paramagnetic resonance (EPR) spectroscopies were performed to investigate the types of point defects in the crystals. The near-band-edge excitonic and shallow donor-shallow acceptor radiative recombination processes involving shallow Mg acceptors were prominent in the PL spectrum of a sample doped to 3 × 1018 cm-3, while the EPR signal was also thought to represent a shallow Mg acceptor. Detection of this signal reflects minimization of nonuniform strain obtained in the thick free-standing HVPE GaN compared with heteroepitaxial thin films.

Coherent Charge Transport in Ballistic InSb Nanowire Josephson Junctions

Science.gov (United States)

Li, S.; Kang, N.; Fan, D. X.; Wang, L. B.; Huang, Y. Q.; Caroff, P.; Xu, H. Q.

2016-01-01

Hybrid InSb nanowire-superconductor devices are promising for investigating Majorana modes and topological quantum computation in solid-state devices. An experimental realisation of ballistic, phase-coherent superconductor-nanowire hybrid devices is a necessary step towards engineering topological superconducting electronics. Here, we report on a low-temperature transport study of Josephson junction devices fabricated from InSb nanowires grown by molecular-beam epitaxy and provide a clear evidence for phase-coherent, ballistic charge transport through the nanowires in the junctions. We demonstrate that our devices show gate-tunable proximity-induced supercurrent and clear signatures of multiple Andreev reflections in the differential conductance, indicating phase-coherent transport within the junctions. We also observe periodic modulations of the critical current that can be associated with the Fabry-Pérot interference in the nanowires in the ballistic transport regime. Our work shows that the InSb nanowires grown by molecular-beam epitaxy are of excellent material quality and hybrid superconducting devices made from these nanowires are highly desirable for investigation of the novel physics in topological states of matter and for applications in topological quantum electronics. PMID:27102689

Low p-type contact resistance by field-emission tunneling in highly Mg-doped GaN

Science.gov (United States)

Okumura, Hironori; Martin, Denis; Grandjean, Nicolas

2016-12-01

Mg-doped GaN with a net acceptor concentration (NA-ND) in the high 1019 cm-3 range was grown using ammonia molecular-beam epitaxy. Electrical properties of NiO contact on this heavily doped p-type GaN were investigated. A potential-barrier height of 0.24 eV was extracted from the relationship between NA-ND and the specific contact resistivity (ρc). We found that there is an optimum NA-ND value of 5 × 1019 cm-3 for which ρc is as low as 2 × 10-5 Ω cm2. This low ρc is ascribed to hole tunneling through the potential barrier at the NiO/p+-GaN interface, which is well accounted for by the field-emission model.

Dry etching of MgCaO gate dielectric and passivation layers on GaN

International Nuclear Information System (INIS)

Hlad, M.; Voss, L.; Gila, B.P.; Abernathy, C.R.; Pearton, S.J.; Ren, F.

2006-01-01

MgCaO films grown by rf plasma-assisted molecular beam epitaxy and capped with Sc 2 O 3 are promising candidates as surface passivation layers and gate dielectrics on GaN-based high electron mobility transistors (HEMTs) and metal-oxide semiconductor HEMTs (MOS-HEMTs), respectively. Two different plasma chemistries were examined for etching these thin films on GaN. Inductively coupled plasmas of CH 4 /H 2 /Ar produced etch rates only in the range 20-70 A/min, comparable to the Ar sputter rates under the same conditions. Similarly slow MgCaO etch rates (∼100 A/min) were obtained with Cl 2 /Ar discharges under the same conditions, but GaN showed rates almost an order of magnitude higher. The MgCaO removal rates are limited by the low volatilities of the respective etch products. The CH 4 /H 2 /Ar plasma chemistry produced a selectivity of around 2 for etching the MgCaO with respect to GaN

Study on ECR dry etching and selective MBE growth of AlGaN/GaN for fabrication of quantum nanostructures on GaN (0001) substrates

International Nuclear Information System (INIS)

Oikawa, Takeshi; Ishikawa, Fumitaro; Sato, Taketomo; Hashizume, Tamotsu; Hasegawa, Hideki

2005-01-01

This paper attempts to form AlGaN/GaN quantum wire (QWR) network structures on patterned GaN (0001) substrates by selective molecular beam epitaxy (MBE) growth. Substrate patterns were prepared along - and -directions by electron cyclotron resonance assisted reactive-ion beam etching (ECR-RIBE) process. Selective growth was possible for both directions in the case of GaN growth, but only in the -direction in the case of AlGaN growth. A hexagonal QWR network was successfully grown on a hexagonal mesa pattern by combining the -direction and two other equivalent directions. AFM observation confirmed excellent surface morphology of the grown network. A clear cathodoluminescence (CL) peak coming from the embedded AlGaN/GaN QWR structure was clearly identified

Proposal of leak path passivation for InGaN solar cells to reduce the leakage current

Energy Technology Data Exchange (ETDEWEB)

Wang, Ke, E-mail: ke.wang@chiba-u.jp; Imai, Daichi; Kusakabe, Kazuhide [Center for SMART Green Innovation Research, Chiba University, 1-33, Yayoi-cho, Inage-ku, Chiba 263-8522 (Japan); Yoshikawa, Akihiko, E-mail: yoshi@faculty.chiba-u.jp [Center for SMART Green Innovation Research, Chiba University, 1-33, Yayoi-cho, Inage-ku, Chiba 263-8522 (Japan); Department of Information and Communication Engineering, Graduate School of Engineering, Kogakuin University, Nakano-cho, Hachioji, Tokyo 2665-1 (Japan)

2016-01-25

We propose some general ways to passivate the leak paths in InGaN solar cells and report some experimental evidences of its effectiveness. By adopting an AlOx passivation process, the photovoltaic performances of GaN pn-junctions and InGaN solar cells, grown by molecular beam epitaxy, have been significantly improved. The open circuit voltage under 1 sun illumination increases from 1.46 to 2.26 V for a GaN pn junction, and from 0.95 to 1.27 V for an InGaN solar cell, demonstrating evidence of leak path passivation (LPP) by AlOx. The proposed LPP is expected to be a realistic way to exploit the potential of thick and relaxed but defective InGaN for solar cell applications.

Molecular beam epitaxial growth of Bi2Te3 and Sb2Te3 topological insulators on GaAs (111 substrates: a potential route to fabricate topological insulator p-n junction

Directory of Open Access Journals (Sweden)

Zhaoquan Zeng

2013-07-01

Full Text Available High quality Bi2Te3 and Sb2Te3 topological insulators films were epitaxially grown on GaAs (111 substrate using solid source molecular beam epitaxy. Their growth and behavior on both vicinal and non-vicinal GaAs (111 substrates were investigated by reflection high-energy electron diffraction, atomic force microscopy, X-ray diffraction, and high resolution transmission electron microscopy. It is found that non-vicinal GaAs (111 substrate is better than a vicinal substrate to provide high quality Bi2Te3 and Sb2Te3 films. Hall and magnetoresistance measurements indicate that p type Sb2Te3 and n type Bi2Te3 topological insulator films can be directly grown on a GaAs (111 substrate, which may pave a way to fabricate topological insulator p-n junction on the same substrate, compatible with the fabrication process of present semiconductor optoelectronic devices.

Hollow-anode plasma source for molecular beam epitaxy of gallium nitride

International Nuclear Information System (INIS)

Anders, A.; Newman, N.; Rubin, M.; Dickinson, M.; Jones, E.; Phatak, P.; Gassmann, A.

1996-01-01

GaN films have been grown by molecular beam epitaxy (MBE) using a hollow-anode nitrogen plasma source. The source was developed to minimize defect formation as a result of contamination and ion damage. The hollow-anode discharge is a special form of glow discharge with very small anode area. A positive anode voltage drop of 30 endash 40 V and an increased anode sheath thickness leads to ignition of a relatively dense plasma in front of the anode hole. Driven by the pressure gradient, the open-quote open-quote anode close-quote close-quote plasma forms a bright plasma jet streaming with supersonic velocity towards the substrate. Films of GaN have been grown on (0001) SiC and (0001) Al 2 O 3 at 600 endash 800 degree C. The films were investigated by photoluminescence, cathodoluminescence, x-ray diffraction, Rutherford backscattering, and particle-induced x-ray emission. The film with the highest structural quality had a rocking curve width of 5 arcmin, the lowest reported value for MBE growth to date. copyright 1996 American Institute of Physics

Self-assembled GaN nano-column grown on Si(111) substrate using Au+Ga alloy seeding method by metalorganic chemical vapor deposition

International Nuclear Information System (INIS)

Shim, Byung-Young; Ko, Eun-A; Song, Jae-Chul; Kang, Dong-Hun; Kim, Dong-Wook; Lee, In-Hwan; Kannappan, Santhakumar; Lee, Cheul-Ro

2007-01-01

Single-crystal GaN nano-column arrays were grown on Au-coated silicon (111) substrate by Au-Ga alloy seeding method using metalorganic chemical vapor deposition (MOCVD). The nano-column arrays were studied as a function of growth parameters and Au thin film thickness. The diameter and length of the as-grown nano-column vary from 100 to 500 nm and 4 to 6 μm, respectively. The surface morphology and optical properties of the nano-columns were investigated using scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), cathodoluminescence (CL) and photoluminescence (PL). The Au+Ga alloy droplets were found to be uniformly distributed on silicon surface. Further, SEM image reveals a vertical growth and cylindrical in shape GaN nano-column. The chemical composition of the nano-column, which composed of gallium and nitrogen ions, was estimated by EDX. CL reveals a strong band edge emission from the GaN nano-column. PL spectra show a peak at 365.7 nm with a full-width half maximum (FWHM) of 65 meV which indicates good optical quality GaN nano-column with low dislocation density. Our results suggest that single crystal GaN nano-column can be grown on Au+Ga alloy on silicon substrate with a low dislocation density for better device performances. (author)

Tunneling anisotropic magnetoresistance in Co/AIOx/Al tunnel junctions with fcc Co (111) electrodes

NARCIS (Netherlands)

Wang, Kai; Tran, T. Lan Ahn; Brinks, Peter; Brinks, P.; Sanderink, Johannes G.M.; Bolhuis, Thijs; van der Wiel, Wilfred Gerard; de Jong, Machiel Pieter

2013-01-01

Tunneling anisotropic magnetoresistance (TAMR) has been characterized in junctions comprised of face-centered cubic (fcc) Co (111) ferromagnetic electrodes grown epitaxially on sapphire substrates, amorphous AlOx tunnel barriers, and nonmagnetic Al counterelectrodes. Large TAMR ratios have been

Epitaxial Growth of MgxCa1-xO on GaN by Atomic Layer Deposition.

Science.gov (United States)

Lou, Xiabing; Zhou, Hong; Kim, Sang Bok; Alghamdi, Sami; Gong, Xian; Feng, Jun; Wang, Xinwei; Ye, Peide D; Gordon, Roy G

2016-12-14

We demonstrate for the first time that a single-crystalline epitaxial Mg x Ca 1-x O film can be deposited on gallium nitride (GaN) by atomic layer deposition (ALD). By adjusting the ratio between the amounts of Mg and Ca in the film, a lattice matched Mg x Ca 1-x O/GaN(0001) interface can be achieved with low interfacial defect density. High-resolution X-ray diffraction (XRD) shows that the lattice parameter of this ternary oxide nearly obeys Vegard's law. An atomically sharp interface from cross-sectional transmission electron microscopy (TEM) confirmed the high quality of the epitaxy. High-temperature capacitance-voltage characterization showed that the film with composition Mg 0.25 Ca 0.75 O has the lowest interfacial defect density. With this optimal oxide composition, a Mg 0.25 Ca 0.75 O/AlGaN/GaN metal-oxide-semiconductor high-electron-mobility (MOS-HEMT) device was fabricated. An ultrahigh on/off ratio of 10 12 and a near ideal SS of 62 mV/dec were achieved with this device.

Control of residual carbon concentration in GaN high electron mobility transistor and realization of high-resistance GaN grown by metal-organic chemical vapor deposition

Energy Technology Data Exchange (ETDEWEB)

He, X.G. [State Key Laboratory on Integrated Optoelectronics, Institute of Semiconductors, Chinese Academy of Sciences, P.O. Box 912, Beijing 100083 (China); Zhao, D.G., E-mail: dgzhao@red.semi.ac.cn [State Key Laboratory on Integrated Optoelectronics, Institute of Semiconductors, Chinese Academy of Sciences, P.O. Box 912, Beijing 100083 (China); Jiang, D.S.; Liu, Z.S.; Chen, P.; Le, L.C.; Yang, J.; Li, X.J. [State Key Laboratory on Integrated Optoelectronics, Institute of Semiconductors, Chinese Academy of Sciences, P.O. Box 912, Beijing 100083 (China); Zhang, S.M.; Zhu, J.J.; Wang, H.; Yang, H. [Suzhou Institute of Nano-tech and Nano-bionics, Chinese Academy of Sciences, Suzhou 215125 (China)

2014-08-01

GaN films were grown by metal-organic chemical vapor deposition (MOCVD) under various growth conditions. The influences of MOCVD growth parameters, i.e., growth pressure, ammonia (NH{sub 3}) flux, growth temperature, trimethyl-gallium flux and H{sub 2} flux, on residual carbon concentration ([C]) were systematically investigated. Secondary ion mass spectroscopy measurements show that [C] can be effectively modulated by growth conditions. Especially, it can increase by reducing growth pressure up to two orders of magnitude. High-resistance (HR) GaN epilayer with a resistivity over 1.0 × 10{sup 9} Ω·cm is achieved by reducing growth pressure. The mechanism of the formation of HR GaN epilayer is discussed. An Al{sub x}Ga{sub 1−x}N/GaN high electron mobility transistor structure with a HR GaN buffer layer and an additional low-carbon GaN channel layer is presented, exhibiting a high two dimensional electron gas mobility of 1815 cm{sup 2}/Vs. - Highlights: • Influence of MOCVD parameters on residual carbon concentration in GaN is studied. • GaN layer with a resistivity over 1 × 10{sup 9} Ω·cm is achieved by reducing growth pressure. • High electron mobility transistor (HEMT) structures were prepared. • Control of residual carbon content results in HEMT with high 2-D electron gas mobility.

Strain in epitaxial high-index Bi{sub 2}Se{sub 3}(221) films grown by molecular-beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Li, Bin [Physics Department, The University of Hong Kong, Pokfulam Road (Hong Kong); Chen, Weiguang [College of Physics and Electronic Engineering, Henan Normal University, Xinxiang, Henan 453007 (China); School of Physics and Electronic Engineering, Zhengzhou Normal University, Zhengzhou, Henan 450044 (China); Guo, Xin; Ho, Wingkin [Physics Department, The University of Hong Kong, Pokfulam Road (Hong Kong); Dai, Xianqi [College of Physics and Electronic Engineering, Henan Normal University, Xinxiang, Henan 453007 (China); School of Physics and Electronic Engineering, Zhengzhou Normal University, Zhengzhou, Henan 450044 (China); Jia, Jinfeng [Key Laboratory of Artificial Structures and Quantum Control (Ministry of Education), Collaborative Innovation Center of Advanced Microstructures, Department of Physics and Astronomy, Shanghai Jiaotong University, 800 Dongchuan Road, Shanghai 200240 (China); Xie, Maohai, E-mail: mhxie@hku.hk [Physics Department, The University of Hong Kong, Pokfulam Road (Hong Kong)

2017-02-28

Highlights: • High-index, off c-axis, Bi{sub 2}Se{sub 3} has been grown by molecular beam epitaxy on In{sub 2}Se{sub 3}. • A retarded strain relaxation process in such high-index Bi{sub 2}Se{sub 3} is observed, enabling experimentally probe strain effect on topological insulators. • It has been shown by calculation that the Dirac electrons participate in chemical bonding at the heterointerface. - Abstract: High-index Bi{sub 2}Se{sub 3}(221) film has been grown on In{sub 2}Se{sub 3}-buffered GaAs(001), in which a much retarded strain relaxation dynamics is recorded. The slow strain-relaxation process of in epitaxial Bi{sub 2}Se{sub 3}(221) can be attributed to the layered structure of Bi{sub 2}Se{sub 3} crystal, where the epifilm grown along [221] is like a pile of weakly-coupled quintuple layer slabs stacked side-by-side on substrate. Finally, we reveal strong chemical bonding at the interface of Bi{sub 2}Se{sub 3} and In{sub 2}Se{sub 3} by plotting differential charge contour calculated by first-principle method. This study points to the feasibility of achieving strained TIs for manipulating the properties of topological systems.

Improvement of optical quality of semipolar (11 2 ¯ 2 ) GaN on m-plane sapphire by in-situ epitaxial lateral overgrowth

Science.gov (United States)

Monavarian, Morteza; Izyumskaya, Natalia; Müller, Marcus; Metzner, Sebastian; Veit, Peter; Can, Nuri; Das, Saikat; Özgür, Ümit; Bertram, Frank; Christen, Jürgen; Morkoç, Hadis; Avrutin, Vitaliy

2016-04-01

Among the major obstacles for development of non-polar and semipolar GaN structures on foreign substrates are stacking faults which deteriorate the structural and optical quality of the material. In this work, an in-situ SiNx nano-network has been employed to achieve high quality heteroepitaxial semipolar (11 2 ¯ 2 ) GaN on m-plane sapphire with reduced stacking fault density. This approach involves in-situ deposition of a porous SiNx interlayer on GaN that serves as a nano-mask for the subsequent growth, which starts in the nanometer-sized pores (window regions) and then progresses laterally as well, as in the case of conventional epitaxial lateral overgrowth (ELO). The inserted SiNx nano-mask effectively prevents the propagation of defects, such as dislocations and stacking faults, in the growth direction and thus reduces their density in the overgrown layers. The resulting semipolar (11 2 ¯ 2 ) GaN layers exhibit relatively smooth surface morphology and improved optical properties (PL intensity enhanced by a factor of 5 and carrier lifetimes by 35% to 85% compared to the reference semipolar (11 2 ¯ 2 ) GaN layer) which approach to those of the c-plane in-situ nano-ELO GaN reference and, therefore, holds promise for light emitting and detecting devices.

Self-catalyst growth of novel GaN nanowire flowers on Si (111) using thermal evaporation technique

Energy Technology Data Exchange (ETDEWEB)

Saron, K.M.A., E-mail: kamalmohammedabdalla@yahoo.com [Nano-Optoelectronics Research and Technology Laboratory (NOR), School of Physics, Universiti Sains Malaysia, Penang 11800 (Malaysia); Hashim, M.R., E-mail: roslan@usm.my [Nano-Optoelectronics Research and Technology Laboratory (NOR), School of Physics, Universiti Sains Malaysia, Penang 11800 (Malaysia)

2013-05-15

We investigated the effect of substrate temperature on nanowire (NW) flower GaN epitaxial layers grown on catalyst-free Si (111) through physical vapor deposition via the thermal evaporation of GaN powder at 1150 °C in the absence of NH{sub 3} gas. The NW flowers were grown at various substrate temperatures from 1000 °C to 1100 °C for 60 min in N{sub 2} ambient. The surface morphology as well as the structural and optical properties of GaN NW flowers were examined by scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy, X-ray diffraction, and photoluminescence (PL). The results showed that the increase in substrate temperature resulted in a variation in crystal quality and surface morphology. SEM showed that the substrate temperature has a stronger effect on NW density and growth rate with respect to time. The average length of GaN flowers is estimated to be longer than 300 μm after 1 h at 1100 °C, which corresponds to a fast growth rate of more than 200 μm h{sup −1} at all substrate temperatures. The PL measurements showed strong near-band-edge (NBE) emission with a weak deep level emission. The green-yellow emission (GYE) can be attributed to N vacancies or to the V{sub Ga}–O{sub N}-complexes. The NBE peak exhibited a redshift with increasing substrate temperature, which results from the increase in strain level. The growth mechanism of the polycrystalline GaN NWs was also discussed. - Highlights: ► GaN nanowired flowers were grown on free-catalysts Si (111) using PVD. ► A higher temperature, higher uniformity, larger lengths and diameters of the NW flowers. ► As substrate temperature increases the diameters and growth rate of NWs increases. ► A lower temperature resulted in a high density and good crystal quality of GaN NWs. ► The increase in substrate temperature increased the redshift in UV band emission.

Self-catalyst growth of novel GaN nanowire flowers on Si (111) using thermal evaporation technique

International Nuclear Information System (INIS)

Saron, K.M.A.; Hashim, M.R.

2013-01-01

We investigated the effect of substrate temperature on nanowire (NW) flower GaN epitaxial layers grown on catalyst-free Si (111) through physical vapor deposition via the thermal evaporation of GaN powder at 1150 °C in the absence of NH 3 gas. The NW flowers were grown at various substrate temperatures from 1000 °C to 1100 °C for 60 min in N 2 ambient. The surface morphology as well as the structural and optical properties of GaN NW flowers were examined by scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy, X-ray diffraction, and photoluminescence (PL). The results showed that the increase in substrate temperature resulted in a variation in crystal quality and surface morphology. SEM showed that the substrate temperature has a stronger effect on NW density and growth rate with respect to time. The average length of GaN flowers is estimated to be longer than 300 μm after 1 h at 1100 °C, which corresponds to a fast growth rate of more than 200 μm h −1 at all substrate temperatures. The PL measurements showed strong near-band-edge (NBE) emission with a weak deep level emission. The green-yellow emission (GYE) can be attributed to N vacancies or to the V Ga –O N -complexes. The NBE peak exhibited a redshift with increasing substrate temperature, which results from the increase in strain level. The growth mechanism of the polycrystalline GaN NWs was also discussed. - Highlights: ► GaN nanowired flowers were grown on free-catalysts Si (111) using PVD. ► A higher temperature, higher uniformity, larger lengths and diameters of the NW flowers. ► As substrate temperature increases the diameters and growth rate of NWs increases. ► A lower temperature resulted in a high density and good crystal quality of GaN NWs. ► The increase in substrate temperature increased the redshift in UV band emission

Field plated 0.15 μm GaN HEMTs for millimeter-wave application

International Nuclear Information System (INIS)

Ren Chunjiang; Li Zhonghui; Yu Xuming; Wang Quanhui; Wang Wen; Chen Tangsheng; Zhang Bin

2013-01-01

SiN dielectrically-defined 0.15 μm field plated GaN HEMTs for millimeter-wave application have been presented. The AlGaN/GaN hetero-structure epitaxial material for HEMTs fabrication was grown on a 3-inch SiC substrate with an Fe doped GaN buffer layer by metal-organic chemical deposition. Electron beam lithography was used to define both the gate footprint and the cap of the gate with an integrated field plate. Gate recessing was performed to control the threshold voltage of the devices. The fabricated GaN HEMTs exhibited a unit current gain cut-off frequency of 39 GHz and a maximum frequency of oscillation of 63 GHz. Load-pull measurements carried out at 35 GHz showed a power density of 4 W/mm with associated power gain and power added efficiency of 5.3 dB and 35%, respectively, for a 0.15 mm gate width device operated at a 24 V drain bias. The developed 0.15 μm gate length GaN HEMT technology is suitable for Ka band applications and is ready for millimeter-wave power MMICs development. (semiconductor devices)

MOVPE growth of violet GaN LEDs on β-Ga2O3 substrates

Science.gov (United States)

Li, Ding; Hoffmann, Veit; Richter, Eberhard; Tessaro, Thomas; Galazka, Zbigniew; Weyers, Markus; Tränkle, Günther

2017-11-01

We report that a H2-free atmosphere is essential for the initial stage of metalorganic vapour phase epitaxy (MOVPE) growth of GaN on β-Ga2O3 to prevent the surface from damage. A simple growth method is proposed that can easily transfer established GaN growth recipes from sapphire to β-Ga2O3 with both (-2 0 1) and (1 0 0) orientations. This method features a thin AlN nucleation layer grown below 900 °C in N2 atmosphere to protect the surface of β-Ga2O3 from deterioration during further growth under the H2 atmosphere. Based on this, we demonstrate working violet vertical light emitting diodes (VLEDs) on n-conductive β-Ga2O3 substrates.

Single phase semipolar (11 anti 22) GaN on (10 anti 10) sapphire

Energy Technology Data Exchange (ETDEWEB)

Ploch, S.; Stellmach, J.; Schwaner, T.; Frentrup, M.; Wernicke, T.; Pristovsek, M.; Kneissl, M. [Institute of Solid States Physics, (Germany); Park, J.B.; Niermann, T.; Lehmann, M. [Institute of Optics and Atomic Physics, TU Berlin, Hardenbergstr. 36, 10623 Berlin (Germany)

2011-07-01

InGaN quantum well based light emitters grown on (0001) GaN suffer from poor quantum efficiencies with increasing indium mole fraction due to strong polarization fields along the polar crystal orientation. This effect can be greatly reduced by growing on semi- and non-polar GaN orientations. Semipolar (11 anti 22) GaN layers were deposited by metalorganic vapour phase epitaxy on (10 anti 10) sapphire. After sapphire substrate nitridation at 1000 C, a GaN nucleation layer was deposited at high temperature, followed by the deposition of 1.5 nm thick GaN buffer layers. The samples show predominantly (11 anti 22) orientation with a small fraction of (10 anti 13) oriented domains. With increasing nitridation layer thickness the (10 anti 13) phase is suppressed leading to a very smooth surface morphology (rms roughness < 4nm). PL measurements show dominant basel plane stacking fault (BSF) I{sub 1} luminescence without any other defects. Transmission electron microscopy measurements reveal a high BSF density. The FWHM of the X-ray diffraction rocking curve measurements of the (1122) reflection decreases to 1193 arcsec and 739 arcsec along [1 anti 100] and [11 anti 23] respectively with increasing nucleation temperature. Using high temperature nucleation smooth and homogeneous (11 anti 22) phase GaN layers have been obtained.

Effect of Al/N ratio during nucleation layer growth on Hall mobility and buffer leakage of molecular-beam epitaxy grown AlGaN/GaN heterostructures

International Nuclear Information System (INIS)

Storm, D.F.; Katzer, D.S.; Binari, S.C.; Shanabrook, B.V.; Zhou Lin; Smith, David J.

2004-01-01

AlGaN/GaN high electron mobility transistor structures have been grown by plasma-assisted molecular beam epitaxy on semi-insulating 4H-SiC utilizing an AlN nucleation layer. The electron Hall mobility of these structures increases from 1050 cm 2 /V s to greater than 1450 cm 2 /V s when the Al/N flux ratio during the growth of the nucleation layer is increased from 0.90 to 1.07. Buffer leakage currents increase abruptly by nearly three orders of magnitude when the Al/N ratio increases from below to above unity. Transmission electron microscopy indicates that high buffer leakage is correlated with the presence of stacking faults in the nucleation layer and cubic phase GaN in the buffer, while low mobilities are correlated with high dislocation densities

Conduction band offset at the InN/GaN heterojunction

International Nuclear Information System (INIS)

Wang Kejia; Lian Chuanxin; Su Ning; Jena, Debdeep; Timler, John

2007-01-01

The conduction-band offset between GaN and InN is experimentally determined. InN/n-type GaN isotype heterojunctions grown by molecular beam epitaxy are observed to exhibit Schottky-junction like behavior based on rectifying vertical current flow. From capacitance-voltage measurements on the heterojunction, the Schottky barrier height is found to be ∼0.94 eV. The photocurrent spectroscopy measurement by backside illumination reveals an energy barrier height of 0.95 eV across the heterojunction, consistent with the capacitance measurement. By combining electrical transport, capacitance-voltage, and photocurrent spectroscopy measurement results, the conduction band offset between InN and GaN is estimated to be ΔE C =1.68±0.1 eV

Thick Bi2Sr2CaCu2O8+δ films grown by liquid-phase epitaxy for Josephson THz applications

Science.gov (United States)

Simsek, Y.; Vlasko-Vlasov, V.; Koshelev, A. E.; Benseman, T.; Hao, Y.; Kesgin, I.; Claus, H.; Pearson, J.; Kwok, W.-K.; Welp, U.

2018-01-01

Theoretical and experimental studies of intrinsic Josephson junctions (IJJs) that naturally occur in high-T c superconducting Bi2Sr2CaCu2O8+δ (Bi-2212) have demonstrated their potential for novel types of compact devices for the generation and sensing of electromagnetic radiation in the THz range. Here, we show that the THz-on-a-chip concept may be realized in liquid-phase epitaxial-grown (LPE) thick Bi-2212 films. We have grown μm thick Bi-2212 LPE films on MgO substrates. These films display excellent c-axis alignment and single crystal grains of about 650 × 150 μm2 in size. A branched current-voltage characteristic was clearly observed in c-axis transport, which is a clear signature of underdamped IJJs, and a prerequisite for THz-generation. We discuss LPE growth conditions allowing improvement of the structural quality and superconducting properties of Bi-2212 films for THz applications.

Direct assessment of p-n junctions in single GaN nanowires by Kelvin probe force microscopy

Science.gov (United States)

Minj, Albert; Cros, Ana; Auzelle, Thomas; Pernot, Julien; Daudin, Bruno

2016-09-01

Making use of Kelvin probe force microscopy, in dark and under ultraviolet illumination, we study the characteristics of p-n junctions formed along the axis of self-organized GaN nanowires (NWs). We map the contact potential difference of the single NW p-n junctions to locate the space charge region and directly measure the depletion width and the junction voltage. Simulations indicate a shrinkage of the built-in potential for NWs with small diameter due to surface band bending, in qualitative agreement with the measurements. The photovoltage of the NW/substrate contact is studied by analyzing the response of NW segments with p- and n-type doping under illumination. Our results show that the shifts of the Fermi levels, and not the changes in surface band bending, are the most important effects under above band-gap illumination. The quantitative electrical information obtained here is important for the use of NW p-n junctions as photovoltaic or rectifying devices at the nanoscale, and is especially relevant since the technique does not require the formation of ohmic contacts to the NW junction.

Resonant Raman and FTIR spectra of carbon doped GaN

Science.gov (United States)

Ito, S.; Kobayashi, H.; Araki, K.; Suzuki, K.; Sawaki, N.; Yamashita, K.; Honda, Y.; Amano, H.

2015-03-01

Intentionally carbon (C) doped (0 0 0 1)GaN was grown using C2H2 on a sapphire substrate by metalorganic vapor phase epitaxy. Optical spectra of the heavily doped samples were investigated at room temperature. In Raman spectra excited by the 325 nm line of a He-Cd laser, multiple LO phonon scattering signals up to 7th order were observed, and the A1(LO) phonon energy was determined to be 737.5 cm-1 (91.45 meV). In infrared reflectance spectra, on the other hand, a local vibration mode was found at 777.5 cm-1, which is attributed to a Ga-C bond in the GaN matrix suggesting that the C sits on an N site (CN). In spite of the strong suggestion of CN, the samples did not show p-type conduction. Possible origin of the carrier compensation is discussed in relation to the enhancement of defect related yellow luminescence in the photoluminescence spectra.

Electron beam and optical depth profiling of quasibulk GaN

International Nuclear Information System (INIS)

Chernyak, L.; Osinsky, A.; Nootz, G.; Schulte, A.; Jasinski, J.; Benamara, M.; Liliental-Weber, Z.; Look, D. C.; Molnar, R. J.

2000-01-01

Electron beam and optical depth profiling of thick (5.5--64 μm) quasibulk n-type GaN samples, grown by hydride vapor-phase epitaxy, were carried out using electron beam induced current (EBIC), microphotoluminescence (PL), and transmission electron microscopy (TEM). The minority carrier diffusion length, L, was found to increase linearly from 0.25 μm, at a distance of about 5 μm from the GaN/sapphire interface, to 0.63 μm at the GaN surface, for a 36-μm-thick sample. The increase in L was accompanied by a corresponding increase in PL band-to-band radiative transition intensity as a function of distance from the GaN/sapphire interface. We attribute the latter changes in PL intensity and minority carrier diffusion length to a reduced carrier mobility and lifetime at the interface, due to scattering at threading dislocations. The results of EBIC and PL measurements are in good agreement with the values for dislocation density obtained using TEM

The role of inversion domain boundaries in fabricating crack-free GaN films on sapphire substrates by hydride vapor phase epitaxy

International Nuclear Information System (INIS)

Ahn, Yong Nam; Lee, Sung Hoon; Lim, Sung Keun; Woo, Kwang Je; Kim, Hyunbin

2015-01-01

Highlights: • Atomistic simulations of inversion domain boundary (IDB) in GaN were performed. • The existence of IDBs in GaN films leads to the reduction of the film stiffness. • A sudden reduction of IDB density induces a strong tensile stress within the films. • The density of IDB in GaN film can be controlled by adjusting GaCl/NH 3 flow ratio. • A microstructure of GaN buffer layer for minimization of stress was proposed. - Abstract: Inversion domain boundaries (IDBs) are frequently found in GaN films grown on sapphire substrates. However, the lack of atomic-level understandings about the effects of the IDBs on the properties of GaN films has hindered to utilize the IDBs for the stress release that minimizes the crack-formation in GaN films. This study performed atomistic computational analyses to fundamentally understand the roles of the IDBs in the development of the stresses in the GaN films. A sudden reduction of the IDB density induces a strong intrinsic stress in the GaN films, possibly leading to the mud-cracking of the films. A gradual decrease in the IDB density was achieved by slowly reducing the GaCl flux during the growth process of GaN buffer layer on sapphire substrates, and allowed us to experimentally demonstrate the successful fabrication of 4-in. crack-free GaN films. This approach may contribute to the fabrication of larger crack-free GaN films

The role of inversion domain boundaries in fabricating crack-free GaN films on sapphire substrates by hydride vapor phase epitaxy

Energy Technology Data Exchange (ETDEWEB)

Ahn, Yong Nam, E-mail: ynahn81@gmail.com; Lee, Sung Hoon, E-mail: sunghoon.lee@corning.com; Lim, Sung Keun, E-mail: sk96.lim@samsung.com; Woo, Kwang Je, E-mail: kwangje.woo@corning.com; Kim, Hyunbin, E-mail: hyunbin.kim@corning.com

2015-03-15

Highlights: • Atomistic simulations of inversion domain boundary (IDB) in GaN were performed. • The existence of IDBs in GaN films leads to the reduction of the film stiffness. • A sudden reduction of IDB density induces a strong tensile stress within the films. • The density of IDB in GaN film can be controlled by adjusting GaCl/NH{sub 3} flow ratio. • A microstructure of GaN buffer layer for minimization of stress was proposed. - Abstract: Inversion domain boundaries (IDBs) are frequently found in GaN films grown on sapphire substrates. However, the lack of atomic-level understandings about the effects of the IDBs on the properties of GaN films has hindered to utilize the IDBs for the stress release that minimizes the crack-formation in GaN films. This study performed atomistic computational analyses to fundamentally understand the roles of the IDBs in the development of the stresses in the GaN films. A sudden reduction of the IDB density induces a strong intrinsic stress in the GaN films, possibly leading to the mud-cracking of the films. A gradual decrease in the IDB density was achieved by slowly reducing the GaCl flux during the growth process of GaN buffer layer on sapphire substrates, and allowed us to experimentally demonstrate the successful fabrication of 4-in. crack-free GaN films. This approach may contribute to the fabrication of larger crack-free GaN films.

Proton irradiation effects on deep level states in Mg-doped p-type GaN grown by ammonia-based molecular beam epitaxy

Science.gov (United States)

Zhang, Z.; Arehart, A. R.; Kyle, E. C. H.; Chen, J.; Zhang, E. X.; Fleetwood, D. M.; Schrimpf, R. D.; Speck, J. S.; Ringel, S. A.

2015-01-01

The impact of proton irradiation on the deep level states throughout the Mg-doped p-type GaN bandgap is investigated using deep level transient and optical spectroscopies. Exposure to 1.8 MeV protons of 1 × 1013 cm-2 and 3 × 1013 cm-2 fluences not only introduces a trap with an EV + 1.02 eV activation energy but also brings monotonic increases in concentration for as-grown deep states at EV + 0.48 eV, EV + 2.42 eV, EV + 3.00 eV, and EV + 3.28 eV. The non-uniform sensitivities for individual states suggest different physical sources and/or defect generation mechanisms. Comparing with prior theoretical calculations reveals that several traps are consistent with associations to nitrogen vacancy, nitrogen interstitial, and gallium vacancy origins, and thus are likely generated through displacing nitrogen and gallium atoms from the crystal lattice in proton irradiation environment.

High-Brightness Blue Light-Emitting Diodes Enabled by a Directly Grown Graphene Buffer Layer.

Science.gov (United States)

Chen, Zhaolong; Zhang, Xiang; Dou, Zhipeng; Wei, Tongbo; Liu, Zhiqiang; Qi, Yue; Ci, Haina; Wang, Yunyu; Li, Yang; Chang, Hongliang; Yan, Jianchang; Yang, Shenyuan; Zhang, Yanfeng; Wang, Junxi; Gao, Peng; Li, Jinmin; Liu, Zhongfan

2018-06-08

Single-crystalline GaN-based light-emitting diodes (LEDs) with high efficiency and long lifetime are the most promising solid-state lighting source compared with conventional incandescent and fluorescent lamps. However, the lattice and thermal mismatch between GaN and sapphire substrate always induces high stress and high density of dislocations and thus degrades the performance of LEDs. Here, the growth of high-quality GaN with low stress and a low density of dislocations on graphene (Gr) buffered sapphire substrate is reported for high-brightness blue LEDs. Gr films are directly grown on sapphire substrate to avoid the tedious transfer process and GaN is grown by metal-organic chemical vapor deposition (MOCVD). The introduced Gr buffer layer greatly releases biaxial stress and reduces the density of dislocations in GaN film and In x Ga 1- x N/GaN multiple quantum well structures. The as-fabricated LED devices therefore deliver much higher light output power compared to that on a bare sapphire substrate, which even outperforms the mature process derived counterpart. The GaN growth on Gr buffered sapphire only requires one-step growth, which largely shortens the MOCVD growth time. This facile strategy may pave a new way for applications of Gr films and bring several disruptive technologies for epitaxial growth of GaN film and its applications in high-brightness LEDs. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Structural and luminescence properties of GaN nanowires grown using cobalt phthalocyanine as catalyst

Science.gov (United States)

Yadav, Shivesh; Rodríguez-Fernández, Carlos; de Lima, Mauricio M.; Cantarero, Andres; Dhar, Subhabrata

2015-12-01

Catalyst free methods have usually been employed to avoid any catalyst induced contamination for the synthesis of GaN nanowires with better transport and optical properties. Here, we have used a catalytic route to grow GaN nanowires, which show good optical quality. Structural and luminescence properties of GaN nanowires grown by vapor-liquid-solid technique using cobalt phthalocyanine as catalyst are systematically investigated as a function of various growth parameters such as the growth temperature and III/V ratio. The study reveals that most of the nanowires, which are several tens of microns long, grow along [ 10 1 ¯ 0 ] direction. Interestingly, the average wire diameter has been found to decrease with the increase in III/V ratio. It has also been observed that in these samples, defect related broad luminescence features, which are often present in GaN, are completely suppressed. At all temperatures, photoluminescence spectrum is found to be dominated only by a band edge feature, which comprises of free and bound excitonic transitions. Our study furthermore reveals that the bound excitonic feature is associated with excitons trapped in certain deep level defects, which result from the deficiency of nitrogen during growth. This transition has a strong coupling with the localized vibrational modes of the defects.

A study of the red-shift of a neutral donor bound exciton in GaN nanorods by hydrogenation.

Science.gov (United States)

Park, Byung-Guon; Lee, Sang-Tae; Reddeppa, Maddaka; Kim, Moon-Deock; Oh, Jae-Eung; Lee, Sang-Kwon

2017-09-08

In this paper we account for the physics behind the exciton peak shift in GaN nanorods (NRs) due to hydrogenation. GaN NRs were selectively grown on a patterned Ti/Si(111) substrate using plasma-assisted molecular beam epitaxy, and the effect of hydrogenation on their optical properties was investigated in detail using low-temperature photoluminescence measurements. Due to hydrogenation, the emissions corresponding to the donor-acceptor pair and yellow luminescence in GaN NRs were strongly suppressed, while the emission corresponding to the neutral to donor bound exciton (D 0 X) exhibited red-shift. Thermal annealing of hydrogenated GaN NRs demonstrated the recovery of the D 0 X and deep level emission. To determine the nature of the D 0 X peak shift due to hydrogenation, comparative studies were carried out on various diameters of GaN NRs, which can be controlled by different growth conditions and wet-etching times. Our experimental results reveal that the D 0 X shift depends on the diameter of the GaN NRs after hydrogenation. The results clearly demonstrate that the hydrogenation leads to band bending of GaN NRs as compensated by hydrogen ions, which causes a red-shift in the D 0 X emission.

A study of the red-shift of a neutral donor bound exciton in GaN nanorods by hydrogenation

Science.gov (United States)

Park, Byung-Guon; Lee, Sang-Tae; Reddeppa, Maddaka; Kim, Moon-Deock; Oh, Jae-Eung; Lee, Sang-Kwon

2017-09-01

In this paper we account for the physics behind the exciton peak shift in GaN nanorods (NRs) due to hydrogenation. GaN NRs were selectively grown on a patterned Ti/Si(111) substrate using plasma-assisted molecular beam epitaxy, and the effect of hydrogenation on their optical properties was investigated in detail using low-temperature photoluminescence measurements. Due to hydrogenation, the emissions corresponding to the donor-acceptor pair and yellow luminescence in GaN NRs were strongly suppressed, while the emission corresponding to the neutral to donor bound exciton (D0X) exhibited red-shift. Thermal annealing of hydrogenated GaN NRs demonstrated the recovery of the D0X and deep level emission. To determine the nature of the D0X peak shift due to hydrogenation, comparative studies were carried out on various diameters of GaN NRs, which can be controlled by different growth conditions and wet-etching times. Our experimental results reveal that the D0X shift depends on the diameter of the GaN NRs after hydrogenation. The results clearly demonstrate that the hydrogenation leads to band bending of GaN NRs as compensated by hydrogen ions, which causes a red-shift in the D0X emission.

Physical origin of the incubation time of self-induced GaN nanowires

International Nuclear Information System (INIS)

Consonni, V.; Trampert, A.; Geelhaar, L.; Riechert, H.

2011-01-01

The nucleation process of self-induced GaN nanowires grown by molecular beam epitaxy has been investigated by reflection high-energy electron diffraction measurements. It is found that stable nuclei in the form of spherical cap-shaped islands develop only after an incubation time that is strongly dependent upon the growth conditions. Its evolution with the growth temperature and gallium rate has been described within standard island nucleation theory, revealing a nucleation energy of 4.9 ± 0.1 eV and a very small nucleus critical size. The consideration of the incubation time is critical for the control of the nanowire morphology.

Luminescence of highly excited nonpolar a-plane GaN and AlGaN/GaN multiple quantum wells

International Nuclear Information System (INIS)

Jursenas, S.; Kuokstis, E.; Miasojedovas, S.; Kurilcik, G.; Zukauskas, A.; Chen, C.Q.; Yang, J.W.; Adivarahan, V.; Asif Khan, M.

2004-01-01

Carrier recombination dynamics in polar and nonpolar GaN epilayers and GaN/AlGaN multiple quantum wells grown over sapphire substrates with a various crystallographic orientation were studied under high photoexcitation by 20 ps laser pulses. The transient luminescence featured a significant enhancement on nonradiative recombination of free carriers for nonpolar a-plane GaN epilayers compared to conventional c-plane samples. The epitaxial layer overgrowth technique was demonstrated to significantly improve the quality of nonpolar a-plane films. This was proved by more than 40-fold increase in luminescence decay time (430 ps compared to ≤ 10 ps in the ordinary a-plane epilayer). Under high-excitation regime, a complete screening of built-in electric field by free carriers in multiple quantum wells grown on c-plane and r-plane sapphire substrates was achieved. Under such high excitation, luminescence efficiency and carrier lifetime of multiple quantum wells were shown to be determined by the substrate quality. (author)

Radiation sensors based on GaN microwires

Science.gov (United States)

Verheij, D.; Peres, M.; Cardoso, S.; Alves, L. C.; Alves, E.; Durand, C.; Eymery, J.; Lorenz, K.

2018-05-01

GaN microwires were shown to possess promising characteristics as building blocks for radiation resistant particle detectors. They were grown by metal organic vapour phase epitaxy with diameters between 1 and 2 μm and lengths around 20 μm. Devices were fabricated by depositing gold contacts at the extremities of the wires using photolithography. The response of these single wire radiation sensors was then studied under irradiation with 2 MeV protons. Severe degradation of the majority of devices only sets in for fluences above protons cm‑2 revealing good radiation resistance. During proton irradiation, a clear albeit small current gain was observed with a corresponding decay time below 1 s. Photoconductivity measurements upon irradiation with UV light were carried out before and after the proton irradiation. Despite a relatively low gain, attributed to significant dark currents caused by a high dopant concentration, fast response times of a few seconds were achieved comparable to state-of-the-art GaN nanowire photodetectors. Irradiation and subsequent annealing resulted in an overall improvement of the devices regarding their response to UV radiation. The photocurrent gain increased compared to the values that were obtained prior to the irradiation, without compromising the decay times. The results indicate the possibility of using GaN microwires not only as UV detectors, but also as particle detectors.

Emission dynamics of hybrid plasmonic gold/organic GaN nanorods

Science.gov (United States)

Mohammadi, F.; Schmitzer, H.; Kunert, G.; Hommel, D.; Ge, J.; Duscher, G.; Langbein, W.; Wagner, H. P.

2017-12-01

We studied the emission of bare and aluminum quinoline (Alq3)/gold coated wurtzite GaN nanorods by temperature- and intensity-dependent time-integrated and time-resolved photoluminescence (PL). The GaN nanorods of ˜1.5 μm length and ˜250 nm diameter were grown by plasma-assisted molecular beam epitaxy. Gold/Alq3 coated GaN nanorods were synthesized by organic molecular beam deposition. The near band-edge and donor-acceptor pair luminescence was investigated in bare GaN nanorods and compared with multilevel model calculations providing the dynamical parameters for electron-hole pairs, excitons, impurity bound excitons, donors and acceptors. Subsequently, the influence of a 10 nm gold coating without and with an Alq3 spacer layer was studied and the experimental results were analyzed with the multilevel model. Without a spacer layer, a significant PL quenching and lifetime reduction of the near band-edge emission is found. The behavior is attributed to surface band-bending and Förster energy transfer from excitons to surface plasmons in the gold layer. Inserting a 5 nm Alq3 spacer layer reduces the PL quenching and lifetime reduction which is consistent with a reduced band-bending and Förster energy transfer. Increasing the spacer layer to 30 nm results in lifetimes which are similar to uncoated structures, showing a significantly decreased influence of the gold coating on the excitonic dynamics.

Cathodoluminescence of GaN diped with Zn in the process of epitaxial growth and by the method of ionic implantation

International Nuclear Information System (INIS)

Khasanov, I.Sh.; Gippius, A.A.; Kuznetsov, A.V.; Petrov, M.N.; Sletov, M.M.

1984-01-01

The cathodoluminescence (CL) method was used to investigate the epitaxial GaN layers doped with Zn both in the process of growth and by the method of ionic implantation for the purpose of clarifying the effect of doping technique on impurity luminescence. It was shown that (2-3)x10 18 cm -3 concentration is optimal with respect to intensity of impurity ''blue'' luminescence for gallium nitride doped with Zn. The intensity of GaN ''blue'' luminescence during Zn ionic implantation is several times lower as compared with doping in the process of growth. This is related to incomplete optical activation of impurity atoms in the process of postimplantation thermal annealing. Increase of zinc concentration above optimal during ionic implantation intensifies crystal lattice disordering, which is supported by intensification of 1.7 eV cathodoluminescence band in spectra conditioned by defects

Plasmas for the low-temperature growth of high-quality GaN films by molecular beam epitaxy and remote plasma MOCVD

Energy Technology Data Exchange (ETDEWEB)

Losurdo, M.; Capezzuto, P.; Bruno, G. [Plasmachemistry Research Center, CNR, Bari (Italy); Namkoong, G.; Doolittle, W.A.; Brown, A.S. [Georgia Inst. of Tech., Atlanta (United States). School of Electrical and Computer Engineering, Microelectronic Research Center

2002-03-16

GaN heteroepitaxial growth on sapphire (0001) substrates was carried out by both radio-frequency (rf) remote plasma metalorganic chemical vapor deposition (RP-MOCVD) and molecular beam epitaxy (MBE). A multistep growth process including substrate plasma cleaning and nitridation, buffer growth, its subsequent annealing and epilayer growth was used. In order to achieve a better understanding of the GaN growth, in-situ real time investigation of the surface chemistry is performed for all the steps using the conventional reflection high-energy electron spectroscopy (RHEED) during the MBE process, while laser reflectance interferometry (LRI) and spectroscopic ellipsometry (SE), which do not require UHV conditions, are used for the monitoring of the RP-MOCVD process. The chemistry of the rf N{sub 2} plasma sapphire nitridation and its effect on the epilayer growth and quality are discussed in both MBE and RP-MOCVD. (orig.)

Epitaxially grown polycrystalline silicon thin-film solar cells on solid-phase crystallised seed layers

Energy Technology Data Exchange (ETDEWEB)

Li, Wei, E-mail: weili.unsw@gmail.com; Varlamov, Sergey; Xue, Chaowei

2014-09-30

Highlights: • Crystallisation kinetic is used to analyse seed layer surface cleanliness. • Simplified RCA cleaning for the seed layer can shorten the epitaxy annealing duration. • RTA for the seed layer can improve the quality for both seed layer and epi-layer. • Epitaxial poly-Si solar cell performance is improved by RTA treated seed layer. - Abstract: This paper presents the fabrication of poly-Si thin film solar cells on glass substrates using seed layer approach. The solid-phase crystallised P-doped seed layer is not only used as the crystalline template for the epitaxial growth but also as the emitter for the solar cell structure. This paper investigates two important factors, surface cleaning and intragrain defects elimination for the seed layer, which can greatly influence the epitaxial grown solar cell performance. Shorter incubation and crystallisation time is observed using a simplified RCA cleaning than the other two wet chemical cleaning methods, indicating a cleaner seed layer surface is achieved. Cross sectional transmission microscope images confirm a crystallographic transferal of information from the simplified RCA cleaned seed layer into the epi-layer. RTA for the SPC seed layer can effectively eliminate the intragrain defects in the seed layer and improve structural quality of both of the seed layer and the epi-layer. Consequently, epitaxial grown poly-Si solar cell on the RTA treated seed layer shows better solar cell efficiency, V{sub oc} and J{sub sc} than the one on the seed layer without RTA treatment.

Multilayer epitaxial graphene grown on the (SiC 000 1-bar ) surface; structure and electronic properties

International Nuclear Information System (INIS)

Sprinkle, M; Hicks, J; Tinkey, H; Clark, M C; Hass, J; Conrad, E H; Tejeda, A; Taleb-Ibrahimi, A; Le Fevre, P; Bertran, F; Soukiassian, P; Martinotti, D

2010-01-01

We review the progress towards developing epitaxial graphene as a material for carbon electronics. In particular, we discuss improvements in epitaxial graphene growth, interface control and the understanding of multilayer epitaxial graphene's (MEG's) electronic properties. Although graphene grown on both polar faces of SiC will be discussed, our discussions will focus on graphene grown on the (0 0 0 1-bar ) C-face of SiC. The unique properties of C-face MEG have become apparent. These films behave electronically like a stack of nearly independent graphene sheets rather than a thin Bernal stacked graphite sample. The origins of multilayer graphene's electronic behaviour are its unique highly ordered stacking of non-Bernal rotated graphene planes. While these rotations do not significantly affect the inter-layer interactions, they do break the stacking symmetry of graphite. It is this broken symmetry that leads to each sheet behaving like isolated graphene planes.

Effect of Mg Doping on the Photoluminescence of GaN:Mg Films by Radio-Frequency Plasma-Assisted Molecular Beam Epitaxy

International Nuclear Information System (INIS)

Sui Yan-Ping; Yu Guang-Hui

2011-01-01

We investigate undoped GaN and Mg-doped GaN grown by rf plasma-assisted molecular beam epitaxy (MBE) with different Mg concentrations by photoluminescence (PL) at low temperature, Hall-effect and XRD measurements. In the PL spectra of lightly Mg-doped GaN films, a low intensity near band edge (NBE) emission and strong donor-acceptor pair (DAP) emission with its phonon replicas are observed. As the Mg concentration is increased, the DAP and NBE bands become weaker and a red shift of these bands is observed in the PL spectra. Yellow luminescence (YL) is observed in heavily Mg-doped GaN. The x-ray diffraction is employed to study the structure of the films. Hall measurement shows that there is a maximum value (3.9 × 10 18 cm −3 ) of hole concentration with increasing Mg source temperature for compensation effect. PL spectra of undoped GaN are also studied under N-rich and Ga-rich growth conditions. Yellow luminescences of undoped Ga-rich GaN and heavily Mg-doped GaN are compared, indicating the different origins of the YL bands. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

Van der Waals epitaxy of GaN-based light-emitting diodes on wet-transferred multilayer graphene film

Science.gov (United States)

Li, Yang; Zhao, Yun; Wei, Tongbo; Liu, Zhiqiang; Duan, Ruifei; Wang, Yunyu; Zhang, Xiang; Wu, QingQing; Yan, Jianchang; Yi, Xiaoyao; Yuan, Guodong; Wang, Junxi; Li, Jimin

2017-08-01

We experimentally investigated the possibility of using multilayer graphene to solve large mismatch problems between sapphire and nitride and further studied the effects of a multilayer graphene interlayer on the optical and electrical properties of LEDs. For the subsequent growth of 3-µm-thick GaN on AlN, multilayer graphene helps release stress and effectively removes cracks. In addition, multilayer graphene increases the diffraction of the substrate surface as determined from the increase in optical transmittance spectra in the wavelength range of 400-900 nm. Although the crystalline quality of GaN with multilayer graphene is slightly decreased, LEDs grown on multilayer graphene still show a higher output power than those grown on conventional sapphire. The present findings showed that the multilayer graphene layer is attractive as a potential substrate for the epitaxial growth of III-nitride to reduce stress and it could improve back light extraction as a rough layer to increase external quantum efficiency.

Mosaic Structure Characterization of the AlInN Layer Grown on Sapphire Substrate

Directory of Open Access Journals (Sweden)

Engin Arslan

2014-01-01

Full Text Available The 150 nm thick, (0001 orientated wurtzite-phase Al1−xInxN epitaxial layers were grown by metal organic chemical vapor deposition on GaN (2.3 µm template/(0001 sapphire substrate. The indium (x concentration of the Al1−xInxN epitaxial layers was changed as 0.04, 0.18, 0.20, 0.47, and 0.48. The Indium content (x, lattice parameters, and strain values in the AlInN layers were calculated from the reciprocal lattice mapping around symmetric (0002 and asymmetric (10–15 reflection of the AlInN and GaN layers. The mosaic structure characteristics of the AlInN layers, such as lateral and vertical coherence lengths, tilt and twist angle, heterogeneous strain, and dislocation densities (edge and screw type dislocations of the AlInN epilayers, were investigated by using high-resolution X-ray diffraction measurements and with a combination of Williamson-Hall plot and the fitting of twist angles.

Stopping Power and Energy Straggling of Channeled He-Ions in GaN

International Nuclear Information System (INIS)

Turos, A.; Ratajczak, R.; Pagowska, K.; Nowicki, L.; Stonert, A.; Caban, P.

2011-01-01

GaN epitaxial layers are usually grown on sapphire substrates. To avoid disastrous effect of the large lattice mismatch a thin polycrystalline nucleation layer is grown at 500 o C followed by the deposition of thick GaN template at much higher temperature. Remnants of the nucleation layer were visualized by transmission electron microscopy as defect agglomeration at the GaN/sapphire interface and provide a very useful depth marker for the measurement of channeled ions stopping power. Random and aligned spectra of He ions incident at energies ranging from 1.7 to 3.7 MeV have been measured and evaluated using the Monte Carlo simulation code McChasy. Impact parameter dependent stopping power has been calculated for channeling direction and its parameters have been adjusted according to experimental data. For virgin, i.e. as grown, samples, the ratio of channeled to random stopping power is constant and amounts to 0.7 in the energy range studied. Defects produced by ion implantation largely influence the stopping power. For channeled ions the variety of possible trajectories leads to different energy loss at a given depth, thus resulting in much larger energy straggling than that for the random path. Beam energy distributions at different depths have been calculated using the McChasy code. They are significantly broader than those predicted by the Bohr formula for random direction. (author)

Reduced defect densities in the ZnO epilayer grown on Si substrates by laser-assisted molecular-beam epitaxy using a ZnS epitaxial buffer layer

International Nuclear Information System (INIS)

Onuma, T.; Chichibu, S.F.; Uedono, A.; Yoo, Y.-Z.; Chikyow, T.; Sota, T.; Kawasaki, M.; Koinuma, H.

2004-01-01

Nonradiative photoluminescence (PL) lifetime (τ nr ) and point defect density in the (0001) ZnO epilayer grown on (111) Si substrates by laser-assisted molecular-beam epitaxy (L-MBE) using a (0001) ZnS epitaxial buffer layer were compared with those in the ZnO films on (111) and (001) Si substrates prepared by direct transformation of ZnS epilayers on Si by thermal oxidation [Yoo et al., Appl. Phys. Lett. 78, 616 (2001)]. Both the ZnO films exhibited excitonic reflectance anomalies and corresponding PL peaks at low temperature, and the density or size of vacancy-type point defects (Zn vacancies), which were measured by the monoenergetic positron annihilation measurement, in the L-MBE epilayer was lower than that in the films prepared by the oxidation transformation. The ZnO epilayer grown on a (0001) ZnS epitaxial buffer on (111) Si exhibited longer τ nr of 105 ps at room temperature

X-ray diffraction study of rare earth epitaxial structures grown by MBE onto (111) GaAs

International Nuclear Information System (INIS)

Bennett, W.R.; Farrow, R.F.C.; Parkin, S.S.P.; Marinero, E.E.; Segmuller, A.P.

1989-01-01

The authors report on the new epitaxial system LaF 3 /Er/Dy/Er/LaF 3 /GaAs(111) grown by molecular beam epitaxy. X-ray diffraction studies have been used to determine the epitaxial relationships between the rare earths, the LaF 3 and the substrate. Further studies of symmetric and asymmetric reflections yielded the in-plane and perpendicular strain components of the rare earth layers. Such systems may be used to probe the effects of magnetoelastic interactions and dimensionality on magnetic ordering in rare earth metal films

Molecular beam epitaxial growth of Bi{sub 2}Te{sub 3} and Sb{sub 2}Te{sub 3} topological insulators on GaAs (111) substrates: a potential route to fabricate topological insulator p-n junction

Energy Technology Data Exchange (ETDEWEB)

Zeng, Zhaoquan; Morgan, Timothy A.; Li, Chen; Hirono, Yusuke; Hu, Xian; Hawkridge, Michael E.; Benamara, Mourad; Salamo, Gregory J. [Arkansas Institute for Nanoscale Material Sciences and Engineering, University of Arkansas, Fayetteville, AR 72701 (United States); Fan, Dongsheng; Yu, Shuiqing [Arkansas Institute for Nanoscale Material Sciences and Engineering, University of Arkansas, Fayetteville, AR 72701 (United States); Department of Electrical Engineering, University of Arkansas, Fayetteville, AR 72701 (United States); Zhao, Yanfei [International Center for Quantum Materials, School of Physics, Peking University, Beijing, 100871 (China); Lee, Joon Sue [The Center for Nanoscale Science and Department of Physics, The Pennsylvania State University, University Park, PA 16802 (United States); Wang, Jian [International Center for Quantum Materials, School of Physics, Peking University, Beijing, 100871 (China); The Center for Nanoscale Science and Department of Physics, The Pennsylvania State University, University Park, PA 16802 (United States); Wang, Zhiming M. [Arkansas Institute for Nanoscale Material Sciences and Engineering, University of Arkansas, Fayetteville, AR 72701 (United States); State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054 (China); Engineering Research Center for Semiconductor Integrated Technology, Institute of Semiconductors, Chinese Academy of Science, Beijing 100083 (China)

2013-07-15

High quality Bi{sub 2}Te{sub 3} and Sb{sub 2}Te{sub 3} topological insulators films were epitaxially grown on GaAs (111) substrate using solid source molecular beam epitaxy. Their growth and behavior on both vicinal and non-vicinal GaAs (111) substrates were investigated by reflection high-energy electron diffraction, atomic force microscopy, X-ray diffraction, and high resolution transmission electron microscopy. It is found that non-vicinal GaAs (111) substrate is better than a vicinal substrate to provide high quality Bi{sub 2}Te{sub 3} and Sb{sub 2}Te{sub 3} films. Hall and magnetoresistance measurements indicate that p type Sb{sub 2}Te{sub 3} and n type Bi{sub 2}Te{sub 3} topological insulator films can be directly grown on a GaAs (111) substrate, which may pave a way to fabricate topological insulator p-n junction on the same substrate, compatible with the fabrication process of present semiconductor optoelectronic devices.

Optical properties of aluminum nitride thin films grown by direct-current magnetron sputtering close to epitaxy

Energy Technology Data Exchange (ETDEWEB)

Stolz, A. [Institut d' Electronique de Microélectronique et de Nanotechnologie (IEMN), UMR CNRS 8520, PRES Lille, Université Nord de France, Avenue Poincaré, 59652 Villeneuve d' Ascq Cedex (France); Soltani, A., E-mail: ali.soltani@iemn.univ-lille1.fr [Institut d' Electronique de Microélectronique et de Nanotechnologie (IEMN), UMR CNRS 8520, PRES Lille, Université Nord de France, Avenue Poincaré, 59652 Villeneuve d' Ascq Cedex (France); Abdallah, B. [Department of Materials Physics, Atomic Energy Commission of Syria, Damascus, P.O. Box 6091 (Syrian Arab Republic); Charrier, J. [Fonctions Optiques pour les Technologies de l' informatiON (FOTON), UMR CNRS 6082, 6, rue de Kerampont CS 80518, 22305 Lannion Cedex (France); Deresmes, D. [Institut d' Electronique de Microélectronique et de Nanotechnologie (IEMN), UMR CNRS 8520, PRES Lille, Université Nord de France, Avenue Poincaré, 59652 Villeneuve d' Ascq Cedex (France); Jouan, P.-Y.; Djouadi, M.A. [Institut des Matériaux Jean Rouxel – IMN, UMR CNRS 6502, 2, rue de la Houssinère BP 32229, 44322 Nantes (France); Dogheche, E.; De Jaeger, J.-C. [Institut d' Electronique de Microélectronique et de Nanotechnologie (IEMN), UMR CNRS 8520, PRES Lille, Université Nord de France, Avenue Poincaré, 59652 Villeneuve d' Ascq Cedex (France)

2013-05-01

Low-temperature Aluminum Nitride (AlN) thin films with a thickness of 3 μm were deposited by Direct-Current magnetron sputtering on sapphire substrate. They present optical properties similar to those of epitaxially grown films. Different characterization methods such as X-Ray Diffraction, Transmission Electron Microscopy and Atomic Force Microscopy were used to determine the structural properties of the films such as its roughness and crystallinity. Newton interferometer was used for stress measurement of the films. Non-destructive prism-coupling technique was used to determine refractive index and thickness homogeneity by a mapping on the whole sample area. Results show that AlN films grown on AlGaN layer have a high crystallinity close to epitaxial films, associated to a low intrinsic stress for low thickness. These results highlight that it is possible to grow thick sample with microstructure and optical properties close to epitaxy, even on a large surface. - Highlights: ► Aluminum Nitride sputtering technique with a low temperature growth process ► Epitaxial quality of two microns sputtered Aluminum Nitride film ► Optics as a non-destructive accurate tool for acoustic wave investigation.

Evidence for graphite-like hexagonal AlN nanosheets epitaxially grown on single crystal Ag(111)

Energy Technology Data Exchange (ETDEWEB)

Tsipas, P.; Kassavetis, S.; Tsoutsou, D.; Xenogiannopoulou, E.; Golias, E.; Giamini, S. A.; Dimoulas, A. [National Center for Scientific Research “Demokritos,” 15310 Athens (Greece); Grazianetti, C.; Fanciulli, M. [Laboratorio MDM, IMM-CNR, I-20864, Agrate Brianza (MB) (Italy); Dipartimento di Scienza dei Materiali, Università degli Studi di Milano Bicocca, I-20126, Milano (Italy); Chiappe, D.; Molle, A. [Laboratorio MDM, IMM-CNR, I-20864, Agrate Brianza (MB) (Italy)

2013-12-16

Ultrathin (sub-monolayer to 12 monolayers) AlN nanosheets are grown epitaxially by plasma assisted molecular beam epitaxy on Ag(111) single crystals. Electron diffraction and scanning tunneling microscopy provide evidence that AlN on Ag adopts a graphite-like hexagonal structure with a larger lattice constant compared to bulk-like wurtzite AlN. This claim is further supported by ultraviolet photoelectron spectroscopy indicating a reduced energy bandgap as expected for hexagonal AlN.

Influence of different aspect ratios on the structural and electrical properties of GaN thin films grown on nanoscale-patterned sapphire substrates

Energy Technology Data Exchange (ETDEWEB)

Lee, Fang-Wei [Department of Electrophysics, National Chiao-Tung University, Hsinchu 300, Taiwan (China); Ke, Wen-Cheng, E-mail: wcke@mail.ntust.edu.tw [Department of Materials Science and Engineering, National Taiwan University of Science and Technology, Taipei 106, Taiwan (China); Cheng, Chun-Hong; Liao, Bo-Wei; Chen, Wei-Kuo [Department of Electrophysics, National Chiao-Tung University, Hsinchu 300, Taiwan (China)

2016-07-01

Highlights: • Nanoscale patterned sapphire substrate was prepared by anodic-aluminum-oxide etching mask. • Influence of aspect ratio of NPSS on structural and electrical properties of GaN films was studied. • Low dislocation density and high carrier mobility of GaN films were grown on high aspect ratio NPSS. - Abstract: This study presents GaN thin films grown on nanoscale-patterned sapphire substrates (NPSSs) with different aspect ratios (ARs) using a homemade metal-organic chemical vapor deposition system. The anodic aluminum oxide (AAO) technique is used to prepare the dry etching mask. The cross-sectional view of the scanning electron microscope image shows that voids exist between the interface of the GaN thin film and the high-AR (i.e. ∼2) NPSS. In contrast, patterns on the low-AR (∼0.7) NPSS are filled full of GaN. The formation of voids on the high-AR NPSS is believed to be due to the enhancement of the lateral growth in the initial growth stage, and the quick-merging GaN thin film blocks the precursors from continuing to supply the bottom of the pattern. The atomic force microscopy images of GaN on bare sapphire show a layer-by-layer surface morphology, which becomes a step-flow surface morphology for GaN on a high-AR NPSS. The edge-type threading dislocation density can be reduced from 7.1 × 10{sup 8} cm{sup −2} for GaN on bare sapphire to 4.9 × 10{sup 8} cm{sup −2} for GaN on a high-AR NPSS. In addition, the carrier mobility increases from 85 cm{sup 2}/Vs for GaN on bare sapphire to 199 cm{sup 2}/Vs for GaN on a high-AR NPSS. However, the increased screw-type threading dislocation density for GaN on a low-AR NPSS is due to the competition of lateral growth on the flat-top patterns and vertical growth on the bottom of the patterns that causes the material quality of the GaN thin film to degenerate. Thus, the experimental results indicate that the AR of the particular patterning of a NPSS plays a crucial role in achieving GaN thin film with

Morphology of self-catalyzed GaN nanowires and chronology of their formation by molecular beam epitaxy

International Nuclear Information System (INIS)

Galopin, E; Largeau, L; Patriarche, G; Travers, L; Glas, F; Harmand, J C

2011-01-01

GaN nanowires are synthesized by plasma-assisted molecular beam epitaxy on Si(111) substrates. The strong impact of the cell orientation relative to the substrate on the nanowire morphology is shown. To study the kinetics of growth, thin AlN markers are introduced periodically during NW growth. These markers are observed in single nanowires by transmission electron microscopy, giving access to the chronology of the nanowire formation and to the time evolution of the nanowire morphology. A long delay precedes the beginning of nanowire formation. Then, their elongation proceeds at a constant rate. Later, shells develop on the side-wall facets by ascending growth of layer bunches which first agglomerate at the nanowire foot.

Origin of Spontaneous Core-Shell AIGaAs Nanowires Grown by Molecular Beam Epitaxy

DEFF Research Database (Denmark)

Dubrovskii, V. G.; Shtrom, I. V.; Reznik, R. R.

2016-01-01

Based on the high-angle annular dark-field scanning transmission electron microscopy and energy dispersive X-ray spectroscopy studies, we unravel the origin of spontaneous core shell AlGaAs nanowires grown by gold-assisted molecular beam epitaxy. Our AlGaAs nanowires have a cylindrical core...

Impact of oxygen precursor flow on the forward bias behavior of MOCVD-Al2O3 dielectrics grown on GaN

Science.gov (United States)

Chan, Silvia H.; Bisi, Davide; Liu, Xiang; Yeluri, Ramya; Tahhan, Maher; Keller, Stacia; DenBaars, Steven P.; Meneghini, Matteo; Mishra, Umesh K.

2017-11-01

This paper investigates the effects of the oxygen precursor flow supplied during metalorganic chemical vapor deposition (MOCVD) of Al2O3 films on the forward bias behavior of Al2O3/GaN metal-oxide-semiconductor capacitors. The low oxygen flow (100 sccm) delivered during the in situ growth of Al2O3 on GaN resulted in films that exhibited a stable capacitance under forward stress, a lower density of stress-generated negative fixed charges, and a higher dielectric breakdown strength compared to Al2O3 films grown under high oxygen flow (480 sccm). The low oxygen grown Al2O3 dielectrics exhibited lower gate current transients in stress/recovery measurements, providing evidence of a reduced density of trap states near the GaN conduction band and an enhanced robustness under accumulated gate stress. This work reveals oxygen flow variance in MOCVD to be a strategy for controlling the dielectric properties and performance.

Transmission electron microscopy study of vertical quantum dots molecules grown by droplet epitaxy

Energy Technology Data Exchange (ETDEWEB)

Hernandez-Maldonado, D., E-mail: david.hernandez@uca.es [Departamento de Ciencia de los Materiales e I.M. y Q.I., Facultad de Ciencias, Universidad de Cadiz, Campus Rio San Pedro, s/n, 11510 Puerto Real, Cadiz (Spain); Herrera, M.; Sales, D.L. [Departamento de Ciencia de los Materiales e I.M. y Q.I., Facultad de Ciencias, Universidad de Cadiz, Campus Rio San Pedro, s/n, 11510 Puerto Real, Cadiz (Spain); Alonso-Gonzalez, P.; Gonzalez, Y.; Gonzalez, L. [Instituto de Microelectronica de Madrid (CNM-CSIC), Isaac Newton 8 (PTM), 28760 Tres Cantos, Madrid (Spain); Pizarro, J.; Galindo, P.L. [Departamento de Lenguajes y Sistemas Informaticos, CASEM, Universidad de Cadiz, Campus Rio San Pedro, s/n, 11510 Puerto Real, Cadiz (Spain); Molina, S.I. [Departamento de Ciencia de los Materiales e I.M. y Q.I., Facultad de Ciencias, Universidad de Cadiz, Campus Rio San Pedro, s/n, 11510 Puerto Real, Cadiz (Spain)

2010-07-01

The compositional distribution of InAs quantum dots grown by molecular beam epitaxy on GaAs capped InAs quantum dots has been studied in this work. Upper quantum dots are nucleated preferentially on top of the quantum dots underneath, which have been nucleated by droplet epitaxy. The growth process of these nanostructures, which are usually called as quantum dots molecules, has been explained. In order to understand this growth process, the analysis of the strain has been carried out from a 3D model of the nanostructure built from transmission electron microscopy images sensitive to the composition.

Transmission electron microscopy study of vertical quantum dots molecules grown by droplet epitaxy

International Nuclear Information System (INIS)

Hernandez-Maldonado, D.; Herrera, M.; Sales, D.L.; Alonso-Gonzalez, P.; Gonzalez, Y.; Gonzalez, L.; Pizarro, J.; Galindo, P.L.; Molina, S.I.

2010-01-01

The compositional distribution of InAs quantum dots grown by molecular beam epitaxy on GaAs capped InAs quantum dots has been studied in this work. Upper quantum dots are nucleated preferentially on top of the quantum dots underneath, which have been nucleated by droplet epitaxy. The growth process of these nanostructures, which are usually called as quantum dots molecules, has been explained. In order to understand this growth process, the analysis of the strain has been carried out from a 3D model of the nanostructure built from transmission electron microscopy images sensitive to the composition.

Magnetoresistance of galfenol-based magnetic tunnel junction

International Nuclear Information System (INIS)

Gobaut, B.; Vinai, G.; Castán-Guerrero, C.; Krizmancic, D.; Panaccione, G.; Torelli, P.; Rafaqat, H.; Roddaro, S.; Rossi, G.; Eddrief, M.; Marangolo, M.

2015-01-01

The manipulation of ferromagnetic layer magnetization via electrical pulse is driving an intense research due to the important applications that this result will have on memory devices and sensors. In this study we realized a magnetotunnel junction in which one layer is made of Galfenol (Fe 1-x Ga x ) which possesses one of the highest magnetostrictive coefficient known. The multilayer stack has been grown by molecular beam epitaxy and e-beam evaporation. Optical lithography and physical etching have been combined to obtain 20x20 micron sized pillars. The obtained structures show tunneling conductivity across the junction and a tunnel magnetoresistance (TMR) effect of up to 11.5% in amplitude

Raman investigation of GaP–Si interfaces grown by molecular beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Bondi, A.; Cornet, C.; Boyer, S.; Nguyen Thanh, T.; Létoublon, A.; Pedesseau, L.; Durand, O. [Université Européenne de Bretagne, INSA, FOTON, UMR CNRS 6082, 20 Avenue des Buttes de Coësmes, F-35708 Rennes (France); Moreac, A. [Institut de Physique de Rennes, UMR-CNRS n°6251, Université Rennes1, Campus de Beaulieu — 35042 Rennes cedex (France); Ponchet, A. [CEMES, UPR CNRS 8011, F-31055 Toulouse (France); Le Corre, A. [Université Européenne de Bretagne, INSA, FOTON, UMR CNRS 6082, 20 Avenue des Buttes de Coësmes, F-35708 Rennes (France); Even, J., E-mail: jacky.even@insa.rennes.fr [Université Européenne de Bretagne, INSA, FOTON, UMR CNRS 6082, 20 Avenue des Buttes de Coësmes, F-35708 Rennes (France)

2013-08-31

Raman spectroscopy was used to investigate the residual strain in thin GaP layers deposited on Si substrates by molecular beam epitaxy. Different growth conditions were used to obtain a clean GaP–Si interface, including migration enhanced epitaxy. The strain induced Raman shifts of the longitudinal and the transverse optical GaP lattice modes were analyzed. The effects of crystalline defects are discussed, supported by high resolution transmission electron microscopy and X-ray scattering studies. Finally, Raman Spectroscopy reveals the presence of disorder (or surface)-activated optical phonons. This result is discussed in the light of surface morphology analyses. - Highlights: ► GaP thin layers grown by molecular beam epitaxy on Si substrates. ► Strain-induced Raman shifts of the optical GaP modes are analyzed. ► Simulation of optical GaP modes by density functional perturbation theory. ► Comparison with X-ray diffraction and electron and scanning probe microscopy data.

Study of electrical properties of single GaN nanowires grown by MOCVD with a Ti mask

International Nuclear Information System (INIS)

Vasiliev, A A; Mozharov, A M; Mukhin, I S; Rozhavskaya, M M; Lundin, V V

2016-01-01

We researched electrical characteristics of GaN nanowires (NWs) grown by MOCVD through solid titanium film. The technology of creating the ohmic contacts and MESFET structure on single NWs has been developed. The optimal annealing temperature of contacts has been found and conductivity structure, the free carrier concentration and mobility has been evaluated. (paper)

Characterization of 380nm UV-LEDs grown on free-standing GaN by atmospheric-pressure metal-organic chemical vapor deposition

Science.gov (United States)

Shieh, C. Y.; Li, Z. Y.; Kuo, H. C.; Chang, J. Y.; Chi, G. C.

2014-03-01

We reported the defects and optical characterizations of the ultraviolet light-emitting diodes grown on free-standing GaN substrate (FS-GaN) and sapphire. Cross-sectional transmission electron microscopy (TEM) images showed that the total defect densities of grown UV LEDs on FS-GaN and sapphire including edge, screw and mixed type were 3.6×106 cm-2 and 5.5×108 cm-2. When substrate of UV LEDs was changed from sapphire to FS-GaN, it can be clearly found that the crystallography of GaN epilayers was drastically different from that GaN epilayers on sapphire. Besides, the microstructures or indium clustering can be not observed at UV LEDs on FS-GaN from TEM measurement. The internal quantum efficiency of UVLEDs on FS-GaN and sapphire were 34.8 % and 39.4 % respectively, which attributed to indium clustering in multi-layers quantum wells (MQWs) of UV LEDs on sapphire. The relationship between indiumclustering and efficiency droop were investigated by temperature-dependent electroluminescence (TDEL) measurements.

Solution-grown organic single-crystalline p-n junctions with ambipolar charge transport.

Science.gov (United States)

Fan, Congcheng; Zoombelt, Arjan P; Jiang, Hao; Fu, Weifei; Wu, Jiake; Yuan, Wentao; Wang, Yong; Li, Hanying; Chen, Hongzheng; Bao, Zhenan

2013-10-25

Organic single-crystalline p-n junctions are grown from mixed solutions. First, C60 crystals (n-type) form and, subsequently, C8-BTBT crystals (p-type) nucleate heterogeneously on the C60 crystals. Both crystals continue to grow simultaneously into single-crystalline p-n junctions that exhibit ambipolar charge transport characteristics. This work provides a platform to study organic single-crystalline p-n junctions. © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

High-mobility BaSnO{sub 3} grown by oxide molecular beam epitaxy

Energy Technology Data Exchange (ETDEWEB)

Raghavan, Santosh; Schumann, Timo; Kim, Honggyu; Zhang, Jack Y.; Cain, Tyler A.; Stemmer, Susanne, E-mail: stemmer@mrl.ucsb.edu [Materials Department, University of California, Santa Barbara, California 93106-5050 (United States)

2016-01-01

High-mobility perovskite BaSnO{sub 3} films are of significant interest as new wide bandgap semiconductors for power electronics, transparent conductors, and as high mobility channels for epitaxial integration with functional perovskites. Despite promising results for single crystals, high-mobility BaSnO{sub 3} films have been challenging to grow. Here, we demonstrate a modified oxide molecular beam epitaxy (MBE) approach, which supplies pre-oxidized SnO{sub x}. This technique addresses issues in the MBE of ternary stannates related to volatile SnO formation and enables growth of epitaxial, stoichiometric BaSnO{sub 3}. We demonstrate room temperature electron mobilities of 150 cm{sup 2} V{sup −1} s{sup −1} in films grown on PrScO{sub 3}. The results open up a wide range of opportunities for future electronic devices.

Absence of strain-mediated magnetoelectric coupling at fully epitaxial Fe/BaTiO3 interface (invited)

International Nuclear Information System (INIS)

Radaelli, G.; Petti, D.; Cantoni, M.; Rinaldi, C.; Bertacco, R.

2014-01-01

Interfacial MagnetoElectric coupling (MEC) at ferroelectric/ferromagnetic interfaces has recently emerged as a promising route to achieve electrical writing of magnetic information in spintronic devices. For the prototypical Fe/BaTiO 3 (BTO) system, various MEC mechanisms have been theoretically predicted. Experimentally, it is well established that using BTO single crystal substrates MEC is dominated by strain-mediated mechanisms. In case of ferromagnetic layers epitaxially grown onto BTO films, instead, no direct evidence for MEC has been provided, apart from the results obtained on tunneling junction sandwiching a BTO tunneling barrier. In this paper, MEC at fully epitaxial Fe/BTO interface is investigated by Magneto-Optical Kerr Effect and magnetoresistance measurements on magnetic tunnel junctions fabricated on BTO. We find no evidence for strain-mediated MEC mechanisms in epitaxial systems, likely due to clamping of BTO to the substrate. Our results indicate that pure electronic MEC is the route of choice to be explored for achieving the electrical writing of information in epitaxial ferromagnet-ferroelectric heterostructures

Disorder in silicon films grown epitaxially at low temperature

International Nuclear Information System (INIS)

Schwarzkopf, J.; Selle, B.; Bohne, W.; Roehrich, J.; Sieber, I.; Fuhs, W.

2003-01-01

Homoepitaxial Si films were prepared by electron cyclotron resonance plasma enhanced chemical vapor deposition on Si(100) substrates at temperatures of 325-500 deg. C using H 2 , Ar, and SiH 4 as process gases. The gas composition, substrate temperature, and substrate bias voltage were systematically varied to study the breakdown of epitaxial growth. Information from ion beam techniques, like Rutherford backscattering and heavy-ion elastic recoil detection analysis, was combined with transmission and scanning electron micrographs to examine the transition from ordered to amorphous growth. The results suggest that the breakdown proceeds in two stages: (i) highly defective but still ordered growth with a defect density increasing with increasing film thickness and (ii) formation of conically shaped amorphous precipitates. The hydrogen content is found to be directly related to the degree of disorder which acts as sink for excessive hydrogen. Only in almost perfect epitaxially grown films is the hydrogen level low, and an exponential tail of the H concentration into the crystalline substrate is observed as a result of the diffusive transport of hydrogen

Zero lattice mismatch and twin-free single crystalline ScN buffer layers for GaN growth on silicon

Energy Technology Data Exchange (ETDEWEB)

Lupina, L.; Zoellner, M. H.; Dietrich, B.; Capellini, G. [IHP, Im Technologiepark 25, 15236 Frankfurt, Oder (Germany); Niermann, T.; Lehmann, M. [Technische Universität Berlin, Institut für Optik und Atomare Physik, Straße des 17. Juni 135, 10623 Berlin (Germany); Thapa, S. B.; Haeberlen, M.; Storck, P. [SILTRONIC AG, Hanns-Seidel-Platz 4, 81737 München (Germany); Schroeder, T. [IHP, Im Technologiepark 25, 15236 Frankfurt, Oder (Germany); BTU Cottbus, Konrad-Zuse-Str. 1, 03046 Cottbus (Germany)

2015-11-16

We report the growth of thin ScN layers deposited by plasma-assisted molecular beam epitaxy on Sc{sub 2}O{sub 3}/Y{sub 2}O{sub 3}/Si(111) substrates. Using x-ray diffraction, Raman spectroscopy, and transmission electron microscopy, we find that ScN films grown at 600 °C are single crystalline, twin-free with rock-salt crystal structure, and exhibit a direct optical band gap of 2.2 eV. A high degree of crystalline perfection and a very good lattice matching between ScN and GaN (misfit < 0.1%) makes the ScN/Sc{sub 2}O{sub 3}/Y{sub 2}O{sub 3} buffer system a very promising template for the growth of high quality GaN layers on silicon.

InGaN/GaN multilayer quantum dots yellow-green light-emitting diode with optimized GaN barriers.

Science.gov (United States)

Lv, Wenbin; Wang, Lai; Wang, Jiaxing; Hao, Zhibiao; Luo, Yi

2012-11-07

InGaN/GaN multilayer quantum dot (QD) structure is a potential type of active regions for yellow-green light-emitting diodes (LEDs). The surface morphologies and crystalline quality of GaN barriers are critical to the uniformity of InGaN QD layers. While GaN barriers were grown in multi-QD layers, we used improved growth parameters by increasing the growth temperature and switching the carrier gas from N2 to H2 in the metal organic vapor phase epitaxy. As a result, a 10-layer InGaN/GaN QD LED is demonstrated successfully. The transmission electron microscopy image shows the uniform multilayer InGaN QDs clearly. As the injection current increases from 5 to 50 mA, the electroluminescence peak wavelength shifts from 574 to 537 nm.

Microstructural dependency of optical properties of m-plane InGaN multiple quantum wells grown on 2° misoriented bulk GaN substrates

Energy Technology Data Exchange (ETDEWEB)

Tang, Fengzai; Barnard, Jonathan S.; Zhu, Tongtong; Oehler, Fabrice; Kappers, Menno J.; Oliver, Rachel A., E-mail: rao28@cam.ac.uk [Department of Materials Science and Metallurgy, University of Cambridge, 27 Charles Babbage Road, Cambridge CB3 0FS (United Kingdom)

2015-08-24

A non-polar m-plane structure consisting of five InGaN/GaN quantum wells (QWs) was grown on ammonothermal bulk GaN by metal-organic vapor phase epitaxy. Surface step bunches propagating through the QW stack were found to accommodate the 2° substrate miscut towards the -c direction. Both large steps with heights of a few tens of nanometres and small steps between one and a few atomic layers in height are observed, the former of which exhibit cathodoluminescence at longer wavelengths than the adjacent m-plane terraces. This is attributed to the formation of semi-polar facets at the steps on which the QWs are shown to be thicker and have higher Indium contents than those in the adjacent m-plane regions. Discrete basal-plane stacking faults (BSFs) were occasionally initiated from the QWs on the main m-plane terraces, but groups of BSFs were frequently observed to initiate from those on the large steps, probably related to the increased strain associated with the locally higher indium content and thickness.

Microstructural dependency of optical properties of m-plane InGaN multiple quantum wells grown on 2° misoriented bulk GaN substrates

International Nuclear Information System (INIS)

Tang, Fengzai; Barnard, Jonathan S.; Zhu, Tongtong; Oehler, Fabrice; Kappers, Menno J.; Oliver, Rachel A.

2015-01-01

A non-polar m-plane structure consisting of five InGaN/GaN quantum wells (QWs) was grown on ammonothermal bulk GaN by metal-organic vapor phase epitaxy. Surface step bunches propagating through the QW stack were found to accommodate the 2° substrate miscut towards the -c direction. Both large steps with heights of a few tens of nanometres and small steps between one and a few atomic layers in height are observed, the former of which exhibit cathodoluminescence at longer wavelengths than the adjacent m-plane terraces. This is attributed to the formation of semi-polar facets at the steps on which the QWs are shown to be thicker and have higher Indium contents than those in the adjacent m-plane regions. Discrete basal-plane stacking faults (BSFs) were occasionally initiated from the QWs on the main m-plane terraces, but groups of BSFs were frequently observed to initiate from those on the large steps, probably related to the increased strain associated with the locally higher indium content and thickness

Microstructure of epitaxial YBa2Cu3O7-x thin films grown on LaAlO3 (001)

International Nuclear Information System (INIS)

Hsieh, Y.; Siegal, M.P.; Hull, R.; Phillips, J.M.

1990-01-01

We report a microstructural investigation of the epitaxial growth of YBa 2 Cu 3 O 7-x (YBCO) thin films on LaAlO 3 (001) substrates using transmission electron microscopy (TEM). Epitaxial films grow with two distinct modes: c epitaxy (YBCO) single crystal with the c (axis normal to the surface and a epitaxy (YBCO) single crystal with the c axis in the interfacial plane), where c epitaxy is the dominant mode grown in all samples 35--200 nm thick. In 35 nm YBCO films annealed at 850 degree C, 97±1% of the surface area is covered by c epitaxy with embedded anisotropic a-epitaxial grains. Quantitative analysis reveals the effect of film thickness and annealing temperature on the density, grain sizes, areal coverages, and anisotropic growth of a epitaxy

Optoelectronic Properties and Structural Characterization of GaN Thick Films on Different Substrates through Pulsed Laser Deposition

Directory of Open Access Journals (Sweden)

Wei-Kai Wang

2017-01-01

Full Text Available Approximately 4-μm-thick GaN epitaxial films were directly grown onto a GaN/sapphire template, sapphire, Si(111, and Si(100 substrates by high-temperature pulsed laser deposition (PLD. The influence of the substrate type on the crystalline quality, surface morphology, microstructure, and stress states was investigated by X-ray diffraction (XRD, photoluminescence (PL, atomic force microscopy (AFM, transmission electron microscopy (TEM, and Raman spectroscopy. Raman scattering spectral analysis showed a compressive film stress of −0.468 GPa for the GaN/sapphire template, whereas the GaN films on sapphire, Si(111, and Si(100 exhibited a tensile stress of 0.21, 0.177, and 0.081 GPa, respectively. Comparative analysis indicated the growth of very close to stress-free GaN on the Si(100 substrate due to the highly directional energetic precursor migration on the substrate’s surface and the release of stress in the nucleation of GaN films during growth by the high-temperature (1000 °C operation of PLD. Moreover, TEM images revealed that no significant GaN meltback (Ga–Si etching process was found in the GaN/Si sample surface. These results indicate that PLD has great potential for developing stress-free GaN templates on different substrates and using them for further application in optoelectronic devices.

Epitaxial properties of ZnO thin films on SrTiO3 substrates grown by laser molecular beam epitaxy

International Nuclear Information System (INIS)

Wei, X. H.; Li, Y. R.; Zhu, J.; Huang, W.; Zhang, Y.; Luo, W. B.; Ji, H.

2007-01-01

Epitaxial ZnO thin films with different orientations have been grown by laser molecular beam epitaxy on (001)- (011)-, and (111)-orientated SrTiO 3 single-crystal substrates. The growth behavior was in situ monitored by reflection high-energy electron diffraction, and the epitaxial orientation relations were reconfirmed by ex situ x-ray diffraction measurements. In the case of ZnO on SrTiO 3 (001), four orthogonal domains coexisted in the ZnO epilayer, i.e., ZnO(110) parallel SrTiO 3 (001) and ZnO[-111] parallel SrTiO 3 . For (011)- and (111)-orientated substrates, single-domain epitaxy with c axial orientation was observed, in which the in-plane relationship was ZnO[110] parallel SrTiO 3 [110] irrespective of the substrate orientations. Additionally, the crystalline quality of ZnO on SrTiO 3 (111) was better than that of ZnO on SrTiO 3 (011) because of the same symmetry between the (111) substrates and (001) films. The obtained results can be attributed to the difference of the in-plane crystallographic symmetry. Furthermore, those alignments can be explained by the interface stress between the substrates and the films

In situ synthesis and characterization of GaN nanorods through thermal decomposition of pre-grown GaN films

International Nuclear Information System (INIS)

Yan, P; Qin, D; An, Y K; Li, G Z; Xing, J; Liu, J J

2008-01-01

Herein we describe a thermal treatment route to synthesize gallium nitride (GaN) nanorods. In this method, GaN nanorods were synthesized by thermal treatment of GaN films at a temperature of 800 deg. C. The morphology and structure of GaN nanorods were characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results show that GaN nanorods have a hexagonal wurtzite structure with diameters ranging from 30 to 50 nm. Additionally, GaN nanoplates are also founded in the products. The growth process of GaN nanostructures was investigated and a thermal decomposition mechanism was proposed. Our method provides a cost-effective route to fabricate GaN nanorods, which will benefit the fabrication of one-dimensional nanomaterials and device applications

Recent Advances on p-Type III-Nitride Nanowires by Molecular Beam Epitaxy