Critical current in nonhomogeneous YBCO coated conductors

International Nuclear Information System (INIS)

Rostila, L; Mikkonen, R; Lehtonen, J

2008-01-01

The critical current of an YBCO tape is determined by the magnetic field inside the YBCO layer and the quality of YBCO material. In thick YBCO layers the average critical current density is reduced by the self-field and decreased material quality. In this paper the combined influence of the material nonhomogeneities and self-field on the critical current of YBCO tapes is scrutinised. First, the zero field critical current density was assumed to decrease along the YBCO thickness. Secondly, the possible defects created in the cutting of YBCO tapes were modelled as a function of lowered critical current density near the tape edges. In both cases the critical current was computed numerically with integral element method. The results suggest that the variation of zero field critical current density, J c0 , along the tape thickness does not effect on the critical current if the mean value of J c0 is kept constant. However, if J c0 is varied along the tape width the critical current can change due to the variated self-field. The computations can be used to determine when it is possible to evaluate the average zero field critical current density from a voltage-current measurement with an appropriate accuracy

Prospects for enhancement of critical current of HTSC: thin films with artificial pinning centres

Energy Technology Data Exchange (ETDEWEB)

Mozhaev, P.B. (Institute of Physics and Technology RAS, Moscow (Russian Federation)); Mozhaev, J.E.; Khoryushin, A.V.; Bindslev Hansen, J.; Jacobsen, C.S. (Technical Univ. of Denmark, Dept. of Physics, Kgs. Lyngby (Denmark)); Kotelyanskil, I.M.; Luzanov, V.A. (Institute of Radio Engineering and Electronics RAS, Moscow (Russian Federation)); Puriy, A.V. (Moscow Institute of Physics and Technology, Moscow (Russian Federation)); Yurchenko, V.; Johansen, T. (Univ. of Oslo, Dept. of Physics, Oslo (Norway))

2008-10-15

Improvement of the critical current of YBCO thin films and heterostructures remains one of the main tasks for fabrication of modern superconducting wires and connectors. Possible ways of achieving the goal are choice of superconductor composition, engineering of artificial pinning centres, and combination of the superconducting layer with other materials. The team of the Department of Physics at Technical University of Denmark is working in all these fields and this paper is a short review of our achievements in an attempt to improve the critical current density of YBCO thin films. (au)

Critical current enhancement driven by suppression of superconducting fluctuation in ion-gated ultrathin FeSe

Science.gov (United States)

Harada, T.; Shiogai, J.; Miyakawa, T.; Nojima, T.; Tsukazaki, A.

2018-05-01

The framework of phase transition, such as superconducting transition, occasionally depends on the dimensionality of materials. Superconductivity is often weakened in the experimental conditions of two-dimensional thin films due to the fragile superconducting state against defects and interfacial effects. In contrast to this general trend, superconductivity in the thin limit of FeSe exhibits an opposite trend, such as an increase in critical temperature (T c) and the superconducting gap exceeding the bulk values; however, the dominant mechanism is still under debate. Here, we measured thickness-dependent electrical transport properties of the ion-gated FeSe thin films to evaluate the superconducting critical current (I c) in the ultrathin FeSe. Upon systematically decreasing the FeSe thickness by the electrochemical etching technique in the Hall bar-shaped electric double-layer transistors, we observed a dramatic enhancement of I c reaching about 10 mA and corresponding to about 107 A cm‑2 in the thinnest condition. By analyzing the transition behavior, we clarify that the suppressed superconducting fluctuation is one of the origins of the large I c in the ion-gated ultrathin FeSe films. These results indicate the existence of a robust superconducting state possibly with dense Cooper pairs at the thin limit of FeSe.

Current-ripple effect on superconductive dc critical current measurements

International Nuclear Information System (INIS)

Goodrich, L.F.; Bray, S.L.; Clark, A.F.

1988-01-01

The effect of sample-current power-supply ripple on dc critical current measurement in multifilamentary NbTi superconductors was evaluated. In general the ripple in a current supply became more significant above 500 A because effective filtering was hard to achieve. Ripple also caused noise at the input of the voltmeter used for the measurements. The quantitative effect of current ripple was studied using a battery current supply modified to allow the creation of ripple current with variable frequency and amplitude. Problems common to all large-conductor critical current measurements are discussed

Enhanced vortex pinning and critical current density in proton-irradiated YBa2Cu3O7-δ thin films

International Nuclear Information System (INIS)

Venturini, E.L.; Siegal, M.P.; White, A.E.; Hou, S.Y.; Phillips, J.M.

1993-01-01

The appropriate fluence of 2.0 MeV H + ions has been shown previously to enhance the critical current density J c by a factor of two at a magnetic field of 0.9 tesla in 1,000 angstrom thick epitaxial films of YBa 2 Cu 3 O 7-δ grown by the ex situ BaF 2 process. The as-grown films exhibit single crystal-like behavior in both atomic ordering and J c versus temperature and magnetic field. TRIM simulations suggest that H + irradiation generates mainly point defects throughout the crystal structure. The authors show here that such defects result in an even greater enhancement of J c for fields above 1 tesla plus a significant increase in the apparent vortex pinning potential deduced from magnetization relaxation data

Enhanced vortex pinning and critical current density in proton-irradiated YBa2Cu3O(7-delta) thin films

Science.gov (United States)

Venturini, E. L.; Siegal, M. P.; White, A. E.; Hou, S. Y.; Phillips, J. M.

1992-11-01

The appropriate fluence of 2.0 MeV H(sup +) ions has been shown previously to enhance the critical current density J(sub c) by a factor of two at a magnetic field of 0.9 tesla in 1000 (Angstrom) thick epitaxial films of YBa(2)Cu(3)O(7-delta) grown by the ex situ BaF2 process. The as-grown films exhibit single crystal-like behavior in both atomic ordering and J(sub c) versus temperature and magnetic field. TRIM simulations suggest that H(sup +) irradiation generates mainly point defects throughout the crystal structure. We show here that such defects produce both a large enhancement of J(sub c) for fields above 1 tesla and a significant increase in the apparent vortex pinning potential deduced from magnetization relaxation data.

Improvement of critical currents in Bi-2223 bulk superconductors

International Nuclear Information System (INIS)

Eujen, R.; Brauer, D.J.; Huedepohl, J.

1991-01-01

Potential applications of the high-Tc superconductors for energy transport or high-field magnets require high critical current densities. A limiting factor in polycrystalline oxidic materials is the quality of the grain boundaries. Weak links have been made responsible for the steep decrease in the critical current density j c upon application of even weak magnetic fields of YBa CuO whereas flux creep seems to dominate the obtainable j c values for the Bi-Sr-Ca-Cu-O system (BSCCO) at 77 K. In the lead containing material (BPSCCO) the formation of a porous microstructure is enhanced by the platelike shape of the crystals. Special techniques such as powder-in-tube, hot isostatic pressing, zone melting or application of fluxes have been used in order to improve the grain contacts. A positive influence of fluxes on j c , e.g. by addition of Ca 2 CuO 3 or Ag 2 O, has been reported. In this study we have investigated the influence of various compositions and conditions on the formation of the BSCCO-2223 phase (T c ca. 107 K), the critical current density j c , and the magnet field dependence of the a.c. susceptibility. (orig.)

Toward superconducting critical current by design

OpenAIRE

Sadovskyy, I. A.; Jia, Y.; Leroux, M.; Kwon, J.; Hu, H.; Fang, L.; Chaparro, C.; Zhu, S.; Welp, U.; Zuo, J. -M.; Zhang, Y.; Nakasaki, R.; Selvamanickam, V.; Crabtree, G. W.; Koshelev, A. E.

2015-01-01

We present the new paradigm of critical current by design. Analogous to materials by design, it aims at predicting the optimal defect landscape in a superconductor for targeted applications by elucidating the vortex dynamics responsible for the bulk critical current. To highlight this approach, we demonstrate the synergistic combination of critical current measurements on commercial high-temperature superconductors containing self-assembled and irradiation tailored correlated defects by using...

Toward Superconducting Critical Current by Design.

Science.gov (United States)

Sadovskyy, Ivan A; Jia, Ying; Leroux, Maxime; Kwon, Jihwan; Hu, Hefei; Fang, Lei; Chaparro, Carlos; Zhu, Shaofei; Welp, Ulrich; Zuo, Jian-Min; Zhang, Yifei; Nakasaki, Ryusuke; Selvamanickam, Venkat; Crabtree, George W; Koshelev, Alexei E; Glatz, Andreas; Kwok, Wai-Kwong

2016-06-01

A new critical-current-by-design paradigm is presented. It aims at predicting the optimal defect landscape in superconductors for targeted applications by elucidating the vortex dynamics responsible for the bulk critical current. To this end, critical current measurements on commercial high-temperature superconductors are combined with large-scale time-dependent Ginzburg-Landau simulations of vortex dynamics. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Investigation on the enhancement of the critical current densities in bronze-process Nb3Sn

International Nuclear Information System (INIS)

Hong, M.; Wu, I.W.; Morris, J.W. Jr.; Gilbert, W.; Hassenzahl, W.V.; Taylor, C.

1981-10-01

The work reported here addressed the problem of improving the critical current characteristic of a comercial multifilamentary Nb 3 Sn strand by varying its heat treatment. The work was done from the perspective that the critical current characteristic is controlled by the metallurgical state of the reacted layer, which is, in turn, fixed by the processing the wire has undergone. The research was carried out in parallel with metallographic studies which analyzed the microstructure and composition profile within the reacted Nb 3 Sn layer as a function of heat treatment. The combined results of metallographic and processing research suggest that it is possible to engineer the microstructure of the reacted layer to improve J/sub c/(H). The specific product of the work is a tailored double-aging treatment which introduces a favorable combination of microstructure and composition in the reacted layer and causes a substantial improvement in the critical current characteristic of the strand

Microstructural and crystallographic imperfections of MgB2 superconducting wire and their correlation with the critical current density

Science.gov (United States)

Shahabuddin, Mohammed; Alzayed, Nasser S.; Oh, Sangjun; Choi, Seyong; Maeda, Minoru; Hata, Satoshi; Shimada, Yusuke; Hossain, Md Shahriar Al; Kim, Jung Ho

2014-01-01

A comprehensive study of the effects of structural imperfections in MgB2 superconducting wire has been conducted. As the sintering temperature becomes lower, the structural imperfections of the MgB2 material are increased, as reflected by detailed X-ray refinement and the normal state resistivity. The crystalline imperfections, caused by lattice disorder, directly affect the impurity scattering between the π and σ bands of MgB2, resulting in a larger upper critical field. In addition, low sintering temperature keeps the grain size small, which leads to a strong enhancement of pinning, and thereby, enhanced critical current density. Owing to both the impurity scattering and the grain boundary pinning, the critical current density, irreversibility field, and upper critical field are enhanced. Residual voids or porosities obviously remain in the MgB2, however, even at low sintering temperature, and thus block current transport paths.

Dependence of critical current on sample length analyzed by the variation of local critical current bent of BSCCO superconducting composite tape

International Nuclear Information System (INIS)

Matsubayashi, H.; Mukai, Y.; Shin, J.K.; Ochiai, S.; Okuda, H.; Osamura, K.; Otto, A.; Malozemoff, A.

2008-01-01

Using the high critical current type BSCCO composite tape fabricated at American Superconductor Corporation, the relation of overall critical current to the distribution of local critical current and the dependence of overall critical current on sample length of the bent samples were studied experimentally and analytically. The measured overall critical current was described well from the distribution of local critical current and n-value of the constituting short elements, by regarding the overall sample to be composed of local series circuits and applying the voltage summation model. Also the dependence of overall critical current on sample length could be reproduced in computer satisfactorily by the proposed simulation method

Critical current properties in superconducting melt processed Y-Ba-Cu-O

International Nuclear Information System (INIS)

Matsushita, Teruo

1993-01-01

The critical current density in bulk superconducting Y-Ba-Cu-O has been remarkably improved by employing the so-called melt process. However, its value is still far below those reported in single-crystalline thin films. Important key factors that determine the critical current density are the flux pinning mechanism and defective structures such as cracks or weak links. In this article, these factors in melt-processed Y-Ba-Cu-O are argued from various measurements of the critical current density on the microstructure dependence, the magnetic field dependence, the temperature dependence, the history effect, the longitudinal field effect and the imaginary ac susceptibility. As for the pinning mechanism, it is concluded that the dominant pinning centers in the high temperature region around 77 K are normal 211 (Y 2 BaCuO 5 ) particles, while small defects such as lattice defects or oxygen deficiencies seem to be dominant in the lower temperature region. It is suggested that much finer normal particles should be introduced in order to improve the critical current density especially at higher temperatures. From the rapid decrease of the critical current density with elevating temperature below 30 K, some kind of weak links are considered to still remain in these materials. However, the observed critical current density did not depend on the history of application of the magnetic field and a large enhancement of the critical current density was observed in the longitudinal field geometry at 4.2 K. These results suggest that the weak links in these materials are of much different kind from those at large angle grain boundaries in sintered polycrystalline materials. From the X-ray diffraction measurements, a domain structure of a mean domain size of about 100 μm was found. These domain boundaries may cause weak links in melt-processed Y-Ba-Cu-O. It is also shown that the typical size of channels of flowing current can be obtained by the imaginary ac susceptibility

Microstructural and crystallographic imperfections of MgB{sub 2} superconducting wire and their correlation with the critical current density

Energy Technology Data Exchange (ETDEWEB)

Shahabuddin, Mohammed; Alzayed, Nasser S. [Department of Physics and Astronomy, College of Science, P. O. Box 2455, King Saud University, Riyadh 11451 (Saudi Arabia); Oh, Sangjun [Materials Research Team, National Fusion Research Institute, Yueeong, Daejeon 305-333 (Korea, Republic of); Choi, Seyong [Busan Center, Korea Basic Science Institute, Geumjeong, Busan 609-735 (Korea, Republic of); Maeda, Minoru [Department of Physics, College of Science and Technology, Nihon University, 1-8 Kanda-Surugadai, Chiyoda-ku, Tokyo 101-8308 (Japan); Hata, Satoshi; Shimada, Yusuke [Interdisciplinary Graduate School of Engineering Sciences, Kyushu University, 6-1 Kasugakoen, Kasuga, Fukuoka 816-8580 (Japan); Hossain, Md Shahriar Al [Institute for Superconducting and Electronic Materials, University of Wollongong, North Wollongong, New South Wales 2500 (Australia); Kim, Jung Ho, E-mail: jhk@uow.edu.au [Department of Physics and Astronomy, College of Science, P. O. Box 2455, King Saud University, Riyadh 11451 (Saudi Arabia); Institute for Superconducting and Electronic Materials, University of Wollongong, North Wollongong, New South Wales 2500 (Australia)

2014-01-15

A comprehensive study of the effects of structural imperfections in MgB{sub 2} superconducting wire has been conducted. As the sintering temperature becomes lower, the structural imperfections of the MgB{sub 2} material are increased, as reflected by detailed X-ray refinement and the normal state resistivity. The crystalline imperfections, caused by lattice disorder, directly affect the impurity scattering between the π and σ bands of MgB{sub 2}, resulting in a larger upper critical field. In addition, low sintering temperature keeps the grain size small, which leads to a strong enhancement of pinning, and thereby, enhanced critical current density. Owing to both the impurity scattering and the grain boundary pinning, the critical current density, irreversibility field, and upper critical field are enhanced. Residual voids or porosities obviously remain in the MgB{sub 2}, however, even at low sintering temperature, and thus block current transport paths.

Critical currents in columnar vanadium films

International Nuclear Information System (INIS)

Cherkasova, V.G.; Kolin'ko, A.E.; Slatin, A.E.; Fogel, N.Y.

1982-01-01

The angular dependence of the critical current I/sub c/ is studied in columnar vanadium films. In measurements in constant magnetic fields an anomalous maximum I/sub c/ is found on the I/sub c/(theta) curves at arbitrary values of the external magnetic field and temperature, when the magnetic field is perpendicular to the plane of the specimen. The angular dependence of I/sub c/ measured in constant reduced magnetic fields h = H/H/sub c/2(T,theta) shows no singularities in the vicinity of the angle at which the I/sub c/ peak is found in the case H = const, i.e., the critical current is isotropic. This implies that a change in the relative orientation of the vortices and column boundaries produces no change in critical current. The experimental data obtained permit the conclusion that the anisotropy of I/sub c/ observed in a constant magnetic field H is merely a consequence of the anisotropy of the critical magnetic field H/sub c/: the critical current ''tracking'' the magnitude and angular dependence of H/sub c/

Method for critical current testing

International Nuclear Information System (INIS)

Siddall, M.B.; Smathers, D.B.

1989-01-01

Superconducting critical current testing software was developed with four important features not feasible with analog test equipment. First, quasi-steady-state sample current conditions are achieved by incrementing sample current, followed by holding some milliseconds until the transient voltage decays before voltage sampling. Then the self-field correction from a helically wound sample is computed and subtracted from each sampled field reading. A copper wire inductively wound shunt which is used for quench protection has a constant measured resistance from which the shunt leakage current is computed and subtracted from the sample current by measuring the shunt voltage after each sample current reading. Finally, the critical current is recomputed from a least squares curve fit to the power law: E=A*In when the correlation coefficient for the fit is high enough to ensure a better result than the raw datum. Comparison with NBS Standard Reference Material (NbTi) and current round robin Nb/sub 3/Sn testing is examined

Analysis of strain distribution and critical current of superconductors based on a strain-critical current measurement system

International Nuclear Information System (INIS)

Liu Fang; Wu Yu; Long Feng

2010-01-01

Based on Pacman device which is widely used to investigate the axial strain dependence of the critical current in superconductors, the finite element analysis method is employed to carry out the force analysis of the spring and the superconducting strand, thereby the axial and lateral strain distributions of the superconducting strand are obtained. According to the two extreme assumptions(low inter-filament resistance and high inter-filament resistance), the effects of the strain homogeneity at the cross section of the superconductor on the critical current is analyzed combined with the Nb 3 Sn deviatoric strain-critical current scaling law. (authors)

Development of MgB2 superconductor wire with high critical current

International Nuclear Information System (INIS)

Kim, Chan Joong; Jun, Byung Hyuk; Park, Soon Dong; Kim, Nam Kyu; Kim, Yi Jeong; Yi, Ji Hye; Lee, Ji Hyun; Tan, Kai Sin

2009-07-01

The MgB 2 superconductor with smaller grain size could improve its critical properties by providing flux pinning centers with high grain boundary density. The effects of C doping such as charcoal, paper ash and glycerin on the superconducting properties was investigated for in situ processed MgB 2 samples using low purity semi-crystalline B powder. The results show a decrease in Tc and an enhancement of Jc at high fields for the C-doped samples as compared to the un-doped samples. A combined process of a mechanical ball milling and liquid glycerin (C 3 H 8 O 3 ) treatment of B powder has been conducted to enhance the superconducting properties of MgB 2 . The mechanical ball milling was effective for grain refinement, and a lattice disorder was easily achieved by glycerin addition. With the combined process, the critical properties was further increased due to a higher grain boundary density and a greater C substitution. To get fine grain structure of MgB 2 with high critical current properties, mechanical milling for as-received B powder and low temperature solid-state reaction of 550 or 600 .deg. C were attempted to in situ powder-in-tube processed MgB 2 /Fe wires. The critical current properties of the MgB 2 wires using the milled B powder were enhanced due to a smaller grain size and an increased volume of the superconducting phase. The solid-state reaction of a low temperature process for the samples using the milled B powder resulted in a poorer crystallinity with a smaller grain size, which improved superconducting properties. We established the system to measure the transport current properties of the MgB 2 wires. The field dependence of the transport Jc was evaluated for the MgB 2 wires heat-treated at different heat treatment conditions using ball-milled and glycerin-treated B powder. The MgB 2 magnet was developed and the AC loss of MgB 2 wire was also investigated. A conduction cooling device to cool the MgB 2 coil down to 4 K has been fabricated and the

Statistical analysis of the distribution of critical current and the correlation of n value to the critical current of bent Bi2223 composite tape

International Nuclear Information System (INIS)

Ochiai, S; Matsubayashi, H; Okuda, H; Osamura, K; Otto, A; Malozemoff, A

2009-01-01

Distributions of local and overall critical currents and correlation of n value to the critical current of bent Bi2223 composite tape were studied from the statistical viewpoint. The data of the local and overall transport critical currents and n values of the Bi2223 composite tape specimens were collected experimentally for a wide range of bending strain (0-1.1%) by using the specimens, designed so as to characterize the local and overall critical currents and n values. The measured local and overall critical currents were analyzed with various types of Weibull distribution function. Which of the Weibull distribution functions is suitable for the description of the distribution of local and overall critical currents at each bending strain, and also how much the Weibull parameter values characterizing the distribution vary with bending strain, were revealed. Then we attempted to reproduce the overall critical current distribution and correlation of the overall n value to the overall critical current from the distribution of local critical currents and the correlation of the local n value to the local critical current by a Monte Carlo simulation. The measured average values of critical current and n value at each bending strain and the correlation of n value to critical current were reproduced well by the present simulation, while the distribution of critical current values was reproduced fairly well but not fully. The reason for this is discussed.

Method for measuring the resistive transition and critical current in superconductors using pulsed current

International Nuclear Information System (INIS)

McGinnis, W.C.; Jones, T.E.

1993-01-01

A method is described for measuring the intragranular critical current of a granular superconductive material, comprising the steps of: conducting a substantially rectangular electronic pulse through said material so as to conduct a current through said material such that when said intragranular critical current of said material is exceeded, any grains present in said material are in a superconducting state when said current is less than said intragranular critical current, said material having a critical temperature; measuring said current through said material while conducting said pulse; measuring a voltage difference across said material while conducting said pulse; and determining said intragranular critical current through said material by varying said current to discern a current level at which an electrical resistance of said material increases to that of a non-superconducting state as the grains of said material transition from said superconducting to said non-superconducting state

Enhancement of critical current density of in situ processed MgB sub 2 tapes by WB addition

CERN Document Server

Fujii, H; Kumakura, H

2003-01-01

The effect of tungsten boride (WB) addition on the microstructure and superconducting properties of Fe-sheathed MgB sub 2 tapes has been investigated. The microstructure was not influenced appreciably by the addition, whereas the superconducting properties changed. Even by a 5 mol% addition, the critical temperature (T sub c) decreased by about 0.5 K. However, the field dependence of the inductive critical current density (J sub c sub i) became smaller with the increase in the amount of addition, suggesting that pinning centres effective in a high-field region were possibly introduced. The transport critical current density (J sub c sub t) at 4.2 K increased about twice by the 5 mol% addition and reached 15 and 5 kA cm sup - sup 2 at 8 and 10 T, respectively.

Critical temperature gradient and critical current density in thin films of a type I superconductor

Energy Technology Data Exchange (ETDEWEB)

Heubener, R P

1968-12-16

Measurements of the critical temperature gradient and the critical current density in superconducting lead films in a transverse magnetic field indicate that the critical current flows predominantly along the surface of the films and that the critical surface currents contribute only very little to the Lorentz force on a fluxoid.

Analytical model of the critical current of a bent Nb3Sn strand

International Nuclear Information System (INIS)

Koizumi, Norikiyo; Murakami, Haruyuki; Hemmi, Tsutomu; Nakajima, Hideo

2011-01-01

The critical current performance of a large Nb 3 Sn cable-in-conduit conductor (CICC) was degraded by periodic bending of strands due to a large transverse electromagnetic force. The degradation of each strand due to this bending should be evaluated in calculations of the critical current of a CICC, but a suitable model has not been developed yet. Therefore, the authors have developed a new analytical model which takes into account plastic deformation of copper and bronze and filament breakage. The calculated results were compared with test results for uniformly bent Nb 3 Sn bronze-route strands. The calculated results assuming a high transverse resistance model (HTRM) show good agreement with the test results, a finding which confirms the validity of the model. Because of a much shorter calculation time than for numerical simulation, the developed model seems much more practical for use in calculating the critical current performance of a Nb 3 Sn CICC. In addition, simulation results show that since the neutral axis of a bent strand shifts to the compressive side due to plastic deformation of the copper and bronze, and/or filament breakage, the strand is elongated by bending. This elongation may enhance the strand's critical current performance. Moreover, the calculated results indicate that the dependence of the critical current on the bending strain is affected by the bending history if the strand is excessively bent, especially when filaments are broken. In a real magnet, since a strand in a CICC is normally subject to the maximum electromagnetic force prior to an evaluation of its performance at a lower electromagnetic force, the effect of over-bending should be taken into account in calculations of its critical current performance, especially when filament breakage occurs.

Critical currents in multilayered superconducting films

International Nuclear Information System (INIS)

Raffy, Helene

1977-01-01

The superconducting critical currents Isub(c) were measured as a function of magnetic field H and temperature T, on multilayered films. These films consist of alternating layers of two different superconductors S 1 and S 2 being a weaker superconductor acting as a flux pinning barrier region. A strong anisotropy was observed between the two situations where the magnetic field H is applied parallel or perpendicular to the layers. In the case discussed, there is a peak effect in the curves Isub(c)H well defined at the highest temperatures, and disappearing at low temperatures. The anisotropy of the critical current at constant field presents a maximum at a temperature T* close to the critical temperature Tsub(c 2 ) of S 2 [fr

High Critical Current Coated Conductors

Energy Technology Data Exchange (ETDEWEB)

Paranthaman, M. P.; Selvamanickam, V. (SuperPower, Inc.)

2011-12-27

One of the important critical needs that came out of the DOE’s coated conductor workshop was to develop a high throughput and economic deposition process for YBCO. Metal-organic chemical vapor deposition (MOCVD) technique, the most critical steps in high technical micro fabrications, has been widely employed in semiconductor industry for various thin film growth. SuperPower has demonstrated that (Y,Gd)BCO films can be deposited rapid with world record performance. In addition to high critical current density with increased film thickness, flux pinning properties of REBCO films needs to be improved to meet the DOE requirements for various electric-power equipments. We have shown that doping with Zr can result in BZO nanocolumns, but at substantially reduced deposition rate. The primary purpose of this subtask is to develop high current density MOCVD-REBCO coated conductors based on the ion-beam assisted (IBAD)-MgO deposition process. Another purpose of this subtask is to investigate HTS conductor design optimization (maximize Je) with emphasis on stability and protection issues, and ac loss for REBCO coated conductors.

Critical transport current in granular high temperature superconductors

International Nuclear Information System (INIS)

Bogolyubov, N.A.

1999-01-01

The temperature and size dependence of the critical current in a zero magnetic field of three bismuth-based ceramic samples with round cross section and one sample with rectangular triangle cross section have been studied by a contactless technique. It is shown that the critical current can be presented as a product of the temperature and size dependent factors. The temperature-dependent multiplier reflects the individual peculiarities of the Josephson net of each sample, while the size factor is a homogeneous function of the cross-section sizes. The index of this function is independent of the cross-section form, the temperature and individual properties of HTSC samples. The radial distribution of critical current density in round samples and dependence of the critical current density on the magnetic conduction in granular HTSC have been found from the analysis of experimental data

Enhancing Critical Thinking in a PBL Environment

DEFF Research Database (Denmark)

Guerra, Aida; Holgaard, Jette Egelund

2016-01-01

Engineering education accreditation bodies emphasize the need for competencies beyond technical expertise. Critical thinking is one of these competencies, which is also considered as a precursor for the development of other competencies such as multidisciplinary collaboration, problem......-solving skills and lifelong learning. There is an urgent need to enhance engineering students’ critical thinking and one way to do this is to make use of active, student-centred learning approaches such as Problem Based Learning (PBL). This study aims to provide a model for understanding and enhancing critical...... thinking in a PBL environment. The development of the model takes its point of departure from a conceptual model for critical thinking that is concretized in a PBL context by including theoretical as well as empirical perspectives. The empirical study was conducted at the Faculty of Engineering and Science...

Critical-state model for the determination of critical currents in disk-shaped superconductors

International Nuclear Information System (INIS)

Frankel, D.J.

1979-01-01

A series of experiments has been carried out on the flux trapping and shielding capabilities of a flat strip of Nb-Ti/Cu composite material. A circular piece of material from the strip was tested in a uniform field directed perpendicularly to the surface of the sample. Profiles of the normal component of the field along the sample diameter were measured. The critical-state model was adapted for this geometry and proved capable of reproducing the measured field profiles. Model curves agreed well with experimental field profiles generated when the full sample was in the critical state, when only a portion of the sample was in the critical state, and when profiles were obtained after the direction of the rate change of the magnetic field was reversed. The adaption of the critical-state model to disk geometry provides a possible method either to derive values of the critical current from measurements of field profiles above thin flat samples, or to predict the trapping and shielding behavior of such samples if the critical current is already known. This method of determining critical currents does not require that samples be formed into narrow strips or wires, as is required for direct measurements of J/sub c/, or into tubes or cylinders, as is usually required for magnetization-type measurements. Only a relatively small approximately circular piece of material is needed. The method relies on induced currents, so there is no need to pass large currents into the sample. The field-profile measurements are easily performed with expensive Hall probes and do not require detection of the resistive transition of the superconductor

Improved critical current of YBaCuO thick-films and ceramics by the addition of Ag

International Nuclear Information System (INIS)

Dwir, B.; Kellett, B.; Mieville, L.; Pavuna, D.

1991-01-01

In a series of papers we have discussed the importance of Ag for contacts and analyzed the resistivity, magnetization, critical current density and percolation properties of YBCO-Ag ceramics. This work has been followed by investigation of electrical and structural properties of thick-films containing Ag in their composition. Here we summarize the most important of our results: In YBCO-Ag ceramic compounds, silver fills the intergranular space (voids), improving the YBaCuO compactness and enhancing the critical current density. These properties are mostly enhanced at 10-20% wt% Ag. The reduction in normal-state resistivity can be described well by 3D percolation theory with a critical concentration of ≅20%. In thick films, prepared by spinning YBaCuO powders on a substrate, adding silver (in the form of Ag 2 O) to the powder mixture improves both T c and J c (by up to 50%), as well as resistivity and resistivity slope. The structural properties, like amount of secondary phases and micro-crack density, are also improved by the addition of Ag. (orig.)

Model for the resistive critical current transition in composite superconductors

International Nuclear Information System (INIS)

Warnes, W.H.

1988-01-01

Much of the research investigating technological type-II superconducting composites relies on the measurement of the resistive critical current transition. We have developed a model for the resistive transition which improves on older models by allowing for the very different nature of monofilamentary and multifilamentary composite structures. The monofilamentary model allows for axial current flow around critical current weak links in the superconducting filament. The multifilamentary model incorporates an additional radial current transfer between neighboring filaments. The development of both models is presented. It is shown that the models are useful for extracting more information from the experimental data than was formerly possible. Specific information obtainable from the experimental voltage-current characteristic includes the distribution of critical currents in the composite, the average critical current of the distribution, the range of critical currents in the composite, the field and temperature dependence of the distribution, and the fraction of the composite dissipating energy in flux flow at any current. This additional information about the distribution of critical currents may be helpful in leading toward a better understanding of flux pinning in technological superconductors. Comparison of the models with several experiments is given and shown to be in reasonable agreement. Implications of the models for the measurement of critical currents in technological composites is presented and discussed with reference to basic flux pinning studies in such composites

The critical current of superconductors: an historical review

International Nuclear Information System (INIS)

Dew-Hughes, D.

2001-01-01

The most important practical characteristic of a superconductor is its critical current density. This article traces the history, both of the experimental discoveries and of the development of the theoretical ideas that have lead to the understanding of those factors that control critical current densities. These include Silsbee's hypothesis, the Meissner effect, London, Ginsburg-Landau and Abrikosov theories, flux pinning and the critical state, and the control of texture in high temperature superconductors

Enhancing Critical Thinking Skills among Authoritarian Students

Science.gov (United States)

Henderson Hurley, Martha; Hurley, David

2013-01-01

This article focuses on assignments designed to enhance critical thinking skills for authoritarian personality types. This paper seeks to add to the literature by exploring instructional methods to overcome authoritarian traits that could inhibit the development of critical thinking skills. The article presents a strategy which can be employed…

Enhancing Critical Thinking Via a Clinical Scholar Approach.

Science.gov (United States)

Simpson, Vicki; McComb, Sara A; Kirkpatrick, Jane M

2017-11-01

Safety, quality improvement, and a systems perspective are vital for nurses to provide quality evidence-based care. Responding to the call to prepare nurses with these perspectives, one school of nursing used a clinical scholar approach, enhanced by systems engineering to more intentionally develop the ability to clinically reason and apply evidence-based practice. A two-group, repeated-measures control trial was used to determine the effects of systems engineering content and support on nursing students' clinical judgment and critical thinking skills. Findings indicated this approach had a positive effects on student's clinical judgment and clinical reasoning skills. This approach helped students view health care issues from a broader perspective and use evidence to guide solution development, enhancing the focus on evidence-based practice, and quality improvement. Intentional integration of an evidence-based, systems perspective by nursing faculty supports development of nurses who can function safely and effectively in the current health care system. [J Nurs Educ. 2017;56(11):679-682.]. Copyright 2017, SLACK Incorporated.

Correlation of superconductor strand, cable, and dipole critical currents in CBA magnets

International Nuclear Information System (INIS)

Tannenbaum, M.J.; Garber, M.; Sampson, W.B.

1982-01-01

A calibration between vendor critical current data for 0.0268'' diameter superconductor strand supplied to Fermilab, and the BNL 10 -12 Ωcm critical current specification is presented. Vendor critical current data for over 400 Fermilab type billets are shown, both as supplied by the vendor and converted to BNL units. Predictions of cable critical current are made using the sum of the critical currents of the 23 strands, where all strands from the same half billet are assigned the same critical current. The measured critical current shows excellent correlation to the predicted value and is approximately 14 +- 2 percent below it. Colliding Beam Accelerator (CBA) full length dipoles reach the conductor critical current limit, essentially without training. Magnet performance is predictable from the measured critical current of a short sample of cable to within 2%

Variation of local critical current and its influence on overall current of bent multifilamentary Bi2223/Ag tape

International Nuclear Information System (INIS)

Ochiai, S.; Doko, D.; Rokkaku, H.; Fujimoto, M.; Okuda, H.; Hojo, M.; Tanaka, M.; Sugano, M.; Osamura, K.; Mimura, M.

2006-01-01

The correlation between the local and overall currents in a multifilamentary Bi2223/Ag/Ag alloy composite tape under bending strain was studied. The correlation of the measured distributed local critical current and n-value to overall critical current was described comprehensively with a voltage summation model that regards the overall sample to be composed of a series circuit. The analysis of the measured critical current and n-value revealed that the distribution of local critical current could be described with the Weibull distribution function and the n-value could be expressed as a function of critical current as a first approximation. By combining the Weibull distribution function of the local critical current, the empirical formula of the n-value as a function of critical current, voltage summation model and Monte Carlo method, the overall current and n-value could be predicted fairly well from those of local elements

Critical current studies of a HTS rectangular coil

Energy Technology Data Exchange (ETDEWEB)

Zhong, Z. [Department of Engineering, University of Cambridge (United Kingdom); Chudy, M., E-mail: Michal.chudy@stuba.sk [Graduate School of Technology Management, University of Pretoria (South Africa); Institute of Power and Applied Electrical Engineering, Slovak University of Technology in Bratislava (Slovakia); Ruiz, H.S. [Department of Engineering, University of Leicester, Leicester LE1 7RH (United Kingdom); Zhang, X.; Coombs, T. [Department of Engineering, University of Cambridge (United Kingdom)

2017-05-15

Highlights: • Unique square pancake coil was manufactured. • Measurements in relatively high magnetic field were performed. • Different sections of the coil were characterized. • Parts of the coil which are limiting critical current were identified. - Abstract: Nowadays, superconducting high field magnets are used in numerous applications due to their superior properties. High temperature superconductors (HTS) are usually used for production of circular pancake or racetrack coils. However different geometries of HTS coils might be required for some specific applications. In this study, the HTS coil wound on a rectangular frame was fully characterized in homogeneous DC background field. The study contains measurements of critical current angular dependencies. The critical current of the entire coil and two selected strands under different magnitudes and orientations of external magnetic fields are measured. The critical regions of the coil in different angular regimes are determined. This study brings better understanding of the in- field performance of HTS coils wound on frames with right-angles.

Microstructures and critical currents in high-Tc superconductors

International Nuclear Information System (INIS)

Suenaga, Masaki

1998-01-01

Microstructural defects are the primary determining factors for the values of critical-current densities in a high T c superconductor after the electronic anisotropy along the a-b plane and the c-direction. A review is made to assess firstly what would be the maximum achievable critical-current density in YBa 2 Cu 3 O 7 if nearly ideal pinning sites were introduced and secondly what types of pinning defects are currently introduced or exist in YBa 2 Cu 3 O 7 and how effective are these in pinning vortices

Critical current density and upper critical field of the PbMo6S8 Chevrel phase

International Nuclear Information System (INIS)

Seeber, B.; Decroux, M.; Fischer, O.

1988-01-01

A detailed discussion of critical current density and upper critical field for PbMo 6 S 8 (PMS) is given. It is shown that PMS bulk as well as wire samples can be prepared with sufficient quality to observe the scaling law for the volume pinning force. Using the scaling law an estimation for the critical current density as a function of field and temperature was made. The study also indicates that a substantial improvement of the critical current density can be expected by optimizing the upper critical field without changing the microstructure. It is shown that the availability of high quality samples of EuMo 6 S 8 , to which PMS is similar, makes it possible to study separately the different physical parameters which determine the upper critical field in PMS

In silico optimization of critical currents in superconductors

Energy Technology Data Exchange (ETDEWEB)

Kimmel, Gregory; Sadovskyy, Ivan A.; Glatz, Andreas

2017-07-01

For many technological applications of superconductors the performance of a material is determined by the highest current it can carry losslessly-the critical current. In turn, the critical current can be controlled by adding nonsuperconducting defects in the superconductor matrix. Here we report on systematic comparison of different local and global optimization strategies to predict optimal structures of pinning centers leading to the highest possible critical currents. We demonstrate performance of these methods for a superconductor with randomly placed spherical, elliptical, and columnar defects.

Simulation of the d.c. critical current in superconducting sintered ceramics

International Nuclear Information System (INIS)

Riedinger, R.; Habig, P.; Hlil, E.K.; Arnaud, M.; Boulesteix, C.

1990-01-01

The new superconducting high-T c sintered ceramics can be described in some case as a lattice of interconnected rods, in other cases as a more or less random packing of parallelepiped crystallites; their size is about a few microns. The d.c. critical current at zero voltage of such a material is not related to the critical current of the bulk material, but to its granular structure. Indeed, the critical current between two adjacent cells is governed by the critical current of the weak link between them; this link behaves within some limits as a Josephson junction, the critical current of which is known. For our present problem, the system can be modeled as a lattice of Josephson junctions. We present here results for the d.c. critical current at zero voltage of lattices of identical Josephson junctions in two dimensions. The influence of the finiteness of size of the sample is examined. The relationship with normal conductivity simulations and percolation is discussed

Field modulation of the critical current in magnetic Josephson junctions

International Nuclear Information System (INIS)

Blamire, M G; Smiet, C B; Banerjee, N; Robinson, J W A

2013-01-01

The dependence of the critical current of a simple Josephson junction on the applied magnetic field is well known and, for a rectangular junction, gives rise to the classic ‘Fraunhofer’ modulation with periodic zeros at the fields that introduce a flux quantum into the junction region. Much recent work has been performed on Josephson junctions that contain magnetic layers. The magnetization of such layers introduces additional flux into the junction and, for large junction areas or strong magnetic materials, can significantly distort the modulation of the critical current and strongly suppress the maximum critical current. The growing interest in junctions that induce odd-frequency triplet pairing in a ferromagnet, and the need to make quantitative comparisons with theory, mean that a full understanding of the role of magnetic barriers in controlling the critical current is necessary. This paper analyses the effect of magnetism and various magnetic configurations on Josephson critical currents; the overall treatment applies to junctions of general shape, but the specific cases of square and rectangular junctions are considered. (paper)

Critical power for lower hybrid current drive

International Nuclear Information System (INIS)

Assis, A.S. de; Sakanaka, P.H.; Azevedo, C.A. de; Busnardo-Neto, J.

1995-11-01

We have solved numerically the quasilinear Fokker-Planck equation which models the critical power for lower hybrid wave current drive. An exact value for the critical power necessary for current saturation, for tokamak current drive experiments, has been obtained. The nonlinear treatment presented here leads to a final profile for the parallel distribution function which is a plateau only in a part of the resonance region. This form of the distribution function is intermediate between two well known results: a plateau throughout the resonance region for the linear strong-source regime, D wave >> D coll and no plateau at all in the resonance region the linear weak-source regimen, D wave coll . The strength of the external power source and the value of the dc electric field are treated as given parameters in the integration scheme. (author). 24 refs, 6 figs

Improvements of fabrication processes and enhancement of critical current densities in (Ba,K)Fe2As2 HIP wires and tapes

Science.gov (United States)

Pyon, Sunseng; Suwa, Takahiro; Tamegai, Tsuyoshi; Takano, Katsutoshi; Kajitani, Hideki; Koizumi, Norikiyo; Awaji, Satoshi; Zhou, Nan; Shi, Zhixiang

2018-05-01

We fabricated (Ba,K)Fe2As2 superconducting wires and tapes using the powder-in-tube method and hot isostatic pressing (HIP). HIP wires and tapes showed a high value of transport critical current density (J c) exceeding 100 kAcm‑2 at T = 4.2 K and the self-field. Transport J c in the HIP wire reached 38 kAcm‑2 in a high magnetic field of 100 kOe. This value is almost twice larger than the previous highest value of J c among round wires using iron-based superconductors. Enhancement of J c in the wires and tapes was caused by improvement of the drawing process, which caused degradation of the core, formation of microcracks, weak links between grains, and random orientation of grains. Details of the effect of the improved fabrication processes on the J c are discussed.

Enhancement of the critical current density in FeO-coated MgB2 thin films at high magnetic fields

Directory of Open Access Journals (Sweden)

Andrei E. Surdu

2011-12-01

Full Text Available The effect of depositing FeO nanoparticles with a diameter of 10 nm onto the surface of MgB2 thin films on the critical current density was studied in comparison with the case of uncoated MgB2 thin films. We calculated the superconducting critical current densities (Jc from the magnetization hysteresis (M–H curves for both sets of samples and found that the Jc value of FeO-coated films is higher at all fields and temperatures than the Jc value for uncoated films, and that it decreases to ~105 A/cm2 at B = 1 T and T = 20 K and remains approximately constant at higher fields up to 7 T.

Large critical current density improvement in Bi-2212 wires through the groove-rolling process

International Nuclear Information System (INIS)

Malagoli, A; Bernini, C; Braccini, V; Romano, G; Putti, M; Chaud, X; Debray, F

2013-01-01

Recently there has been a growing interest in Bi-2212 superconductor round wire for high magnetic field use despite the fact that an increase of the critical current is still needed to boost its successful use in such applications. Recent studies have demonstrated that the main obstacle to current flow, especially in long wires, is the residual porosity inside these powder-in-tube processed conductors that develops from bubble agglomeration when the Bi-2212 melts. In this work we tried to overcome this issue affecting the wire densification by changing the deformation process. Here we show the effects of groove rolling versus the drawing process on the critical current density J C and on the microstructure. In particular, groove-rolled multifilamentary wires show a J C increased by a factor of about 3 with respect to drawn wires prepared with the same Bi-2212 powder and architecture. We think that this approach in the deformation process is able to produce the required improvements both because the superconducting properties are enhanced and because it makes the fabrication process faster and cheaper. (paper)

A statistical study of current-sheet formation above solar active regions based on selforganized criticality

Science.gov (United States)

Dimitropoulou, M.; Isliker, H.; Vlahos, L.; Georgoulis, M.; Anastasiadis, A.; Toutountzi, A.

2013-09-01

We treat flaring solar active regions as physical systems having reached the self-organized critical state. Their evolving magnetic configurations in the low corona may satisfy an instability criterion, related to the excession of a specific threshold in the curl of the magnetic field. This imposed instability criterion implies an almost zero resistivity everywhere in the solar corona, except in regions where magnetic-field discontinuities and. hence, local currents, reach the critical value. In these areas, current-driven instabilities enhance the resistivity by many orders of magnitude forming structures which efficiently accelerate charged particles. Simulating the formation of such structures (thought of as current sheets) via a refined SOC cellular-automaton model provides interesting information regarding their statistical properties. It is shown that the current density in such unstable regions follows power-law scaling. Furthermore, the size distribution of the produced current sheets is best fitted by power laws, whereas their formation probability is investigated against the photospheric magnetic configuration (e.g. Polarity Inversion Lines, Plage). The average fractal dimension of the produced current sheets is deduced depending on the selected critical threshold. The above-mentioned statistical description of intermittent electric field structures can be used by collisional relativistic test particle simulations, aiming to interpret particle acceleration in flaring active regions and in strongly turbulent media in astrophysical plasmas. The above work is supported by the Hellenic National Space Weather Research Network (HNSWRN) via the THALIS Programme.

Influence of self-field on the critical current of Bi-2223/Ag tapes

International Nuclear Information System (INIS)

Lehtonen, Jorma; Korpela, Aki; Nah, Wansoo; Kang, Joonsun; Kovac, Pavol; Melisek, Tibor

2004-01-01

The knowledge of critical current density in a superconducting wire is essential in order to compute AC losses. In HTS tapes the critical current density is difficult to estimate from the measured critical current because self-field tends to reduce the current carrying capacity. In this paper the critical current is measured with a single sample and with two similar samples connected in antiparallel in order to compensate the self-field. Both types of measurement are simulated with finite element method. The simulations help to understand the relation between the measured critical current and material properties. The results suggest that in a high quality tape the self-field effect reduced the measured critical current ∼25% if compared to the real critical current at the zero external field

Measurement of local critical currents in TFA-MOD processed coated conductors by use of scanning Hall-probe microscopy

International Nuclear Information System (INIS)

Shiohara, K.; Higashikawa, K.; Kawaguchi, T.; Inoue, M.; Kiss, T.; Yoshizumi, M.; Izumi, T.

2011-01-01

We have investigated 2-dimensional distribution of critical current density. We have measured TFA-MOD processed YBCO coated conductor. We used scanning Hall-probe microscopy. These provided information is useful for fabrication process of coated conductor. We have carried out 2-dimensional (2D) measurement of local critical current in a Trifluoroacetates-Metal Organic Deposition (TFA-MOD) processed YBCO coated conductor using scanning Hall-probe microscopy. Recently, remarkable R and D accomplishments on the fabrication processes of coated conductors have been conducted extensively and reported. The TFA-MOD process has been expected as an attractive process to produce coated conductors with high performance at a low production cost due to a simple process using non-vacuum equipments. On the other hand, enhancement of critical currents and homogenization of the critical current distribution in the coated conductors are definitely very important for practical applications. According to our measurements, we can detect positions and spatial distribution of defects in the conductor. This kind of information will be very helpful for the improvement of the TFA-MOD process and for the design of the conductor intended for practical electric power device applications.

The influence of tensile strain to critical current of Bi2223 composite tape

International Nuclear Information System (INIS)

Mukai, Y.; Shin, J.K.; Ochiai, S.; Okuda, H.; Sugano, M.; Osamura, K.

2008-01-01

As the stress-induced damage evolution is different from position to position in the sample, the local critical current is scattered in a sample, affecting on the overall current. The present work aimed to describe the distribution of local critical current and its relation to overall critical current under tensile stress for Bi2223/Ag superconducting composite tape. In the experiment, seven voltage probes were attached in a step of 10 mm. The local critical current and n-value at 77 K under various applied stress levels were measured for a voltage probe distance 10 mm and the overall ones for a probe distance 60 mm. Main results are summarized as follows. The overall critical current and n-value were described well by using the voltage summation model in which the sample was regarded as a one dimensional series circuit. For the low applied stress, the distribution of local critical current was described with the three parameter Weibull distribution function. Using the measured distribution of the local critical current, an experimental relation of critical current to n-value and the voltage summation model, and applying the Monte Carlo method, the overall critical current was predicted, which was in good agreement with the experimental results. Based on these results, the sample length dependence of critical current of the sample damaged by tensile stress was discussed

Enhancement of spin Hall effect induced torques for current-driven magnetic domain wall motion: Inner interface effect

KAUST Repository

Bang, Do; Yu, Jiawei; Qiu, Xuepeng; Wang, Yi; Awano, Hiroyuki; Manchon, Aurelien; Yang, Hyunsoo

2016-01-01

We investigate the current-induced domain wall motion in perpendicular magnetized Tb/Co wires with structure inversion asymmetry and different layered structures. We find that the critical current density to drive domain wall motion strongly depends on the layered structure. The lowest critical current density ∼15MA/cm2 and the highest slope of domain wall velocity curve are obtained for the wire having thin Co sublayers and more inner Tb/Co interfaces, while the largest critical current density ∼26MA/cm2 required to drive domain walls is observed in the Tb-Co alloy magnetic wire. It is found that the Co/Tb interface contributes negligibly to Dzyaloshinskii-Moriya interaction, while the effective spin-orbit torque strongly depends on the number of Tb/Co inner interfaces (n). An enhancement of the antidamping torques by extrinsic spin Hall effect due to Tb rare-earth impurity-induced skew scattering is suggested to explain the high efficiency of current-induced domain wall motion.

Enhancement of spin Hall effect induced torques for current-driven magnetic domain wall motion: Inner interface effect

KAUST Repository

Bang, Do

2016-05-23

We investigate the current-induced domain wall motion in perpendicular magnetized Tb/Co wires with structure inversion asymmetry and different layered structures. We find that the critical current density to drive domain wall motion strongly depends on the layered structure. The lowest critical current density ∼15MA/cm2 and the highest slope of domain wall velocity curve are obtained for the wire having thin Co sublayers and more inner Tb/Co interfaces, while the largest critical current density ∼26MA/cm2 required to drive domain walls is observed in the Tb-Co alloy magnetic wire. It is found that the Co/Tb interface contributes negligibly to Dzyaloshinskii-Moriya interaction, while the effective spin-orbit torque strongly depends on the number of Tb/Co inner interfaces (n). An enhancement of the antidamping torques by extrinsic spin Hall effect due to Tb rare-earth impurity-induced skew scattering is suggested to explain the high efficiency of current-induced domain wall motion.

Further investigations of the upper critical field and the high field critical current density in Nb-Ti and its alloys

International Nuclear Information System (INIS)

Hawksworth, D.G.; Larbalestier, D.C.

1980-09-01

This paper reports further measurements of Hc 2 in the Nb-Ti-Ta and Nb-Ti-Hf systems. Whilst we find only small enhancements of approx. 0.3 Tesla in μ 0 Hc 2 (4.2 0 K) compared to binary Nb-Ti, at 2 0 K there is a wide composition range in the Nb-Ti-Ta system where μ 0 Hc 2 (2 0 K) exceeds 15 Tesla, reaching a maximum of 15.5 Tesla. This represents an enhancement of 1.3 Tesla over unalloyed Nb-Ti. By comparison alloys in the Nb-Ti-Hf system show a maximum enhancement in μ 0 Hc 2 (2 0 K) of only 0.3 Tesla. The reasons both for the enhancements in Hc 2 and for the differences in behavior shown by alloys containing Ta and Hf are briefly discussed. This paper also discusses common features in the behavior of the high field critical current density, J/sub c/, of four commercial Nb-Ti composites and upon the basis of this behavior predict the enhancements in high field J/sub c/ to be expected from using Nb-Ti-Ta and its alloys

Critical current of high Tc superconducting Bi223/Ag tapes

NARCIS (Netherlands)

Huang, Y.; ten Haken, Bernard; ten Kate, Herman H.J.

1998-01-01

The magnetic field dependence of the critical current of various high Tc superconducting Bi2223/Ag tapes indicates that the transport current is carried through two paths: one is through weakly-linked grain boundaries (Josephson junctions); another is through well-connected grains. The critical

The critical current of granular superconductor

International Nuclear Information System (INIS)

Ignat'ev, V.K.

1998-01-01

A mechanism of hyper vortex pinning in granular superconductors is proposed to describe the field dependence of the critical current density and pinning potential. The results are in a good agreement with the experiment. The model represents the peak effect and the percolation mechanism of conductivity in ceramic superconductors

Enhancing Critical Thinking: Accounting Students' Perceptions

Science.gov (United States)

Wilkin, Carla L.

2017-01-01

Purpose: The purpose of this paper is to demonstrate how assessment design was used to enhance students' critical thinking in a subject concerned with business enterprise systems. The study shows positive results and favorable perceptions of the merit of the approach. Design/Methodology/Approach: A case study approach was used to examine how the…

Effect of strain on the critical-current density of Cu-Nb composites

International Nuclear Information System (INIS)

Klein, J.D.; Rose, R.M.

1987-01-01

Microfilamentary superconducting composites of Nb fibers in Cu matrices prepared by the stack and draw method were tested for tensile critical-current performance at 4.2 K. The superconducting critical-current densities increased exponentially under the influence of an applied mechanical strain until the onset of Nb fiber plastic deformation. In the elastic range, the critical-current densities conformed to log 10 J/sub c/ = m (strain)+b. In several tests the critical current was increased by more than an order of magnitude by the applied strain. This behavior is consistent with an increase in the upper critical field of the Nb fibers by the applied stress

Enhanced Critical Thinking Skills through Problem-Solving Games in Secondary Schools

OpenAIRE

Scott D McDonald

2017-01-01

Aim/Purpose: Students face many challenges improving their soft skills such as critical thinking. This paper offers one possible solution to this problem. Background: This paper considers one method of enhancing critical thinking through a problem-solving game called the Coffee Shop. Problem-solving is a key component to critical thinking, and game-playing is one method of enhancing this through an interactive teaching method. Methodology: Three classes of Vietnamese high school stude...

Differences between two definitions of the critical current of HTS coils

International Nuclear Information System (INIS)

Pitel, Jozef

2013-01-01

Definition of the critical current of a coil made of anisotropic high temperature superconducting conductor is rather complicated and ambiguous, since the magnetic field generated across the winding can differ considerably in relation to both its magnitude and orientation. Two definitions of the critical current of such coils are discussed. The first definition, very often used in calculations to analyze the current carrying capacity, electric field and power dissipation of individual turns, represents an operating current at which an electric field of 1 μV cm −1 appears on one turn. The second definition represents an integral approach, and is used in experiments. This definition introduces the critical current of the coil as an operating current at which an average electric field E s , usually 0.1 μV cm −1 , appears on coil terminals. As an example, the distribution of the critical current and electric field of individual turns in the winding of a BSCCO model coil was analyzed. Critical currents of the coil as a function of an external magnetic field parallel with the coil axis were calculated according to both definitions. The results show that the first definition, which characterizes the winding at the local level, is suitable for HTS coils either operating in self-field or in a low external field, because the differences between the critical currents and n-indices of individual turns are considerable. The second criterion is suitable for the HTS coils operating in high fields, i.e. like high field insert coils. The self-field of a high field insert coil is negligible if the external field is high. As a result, the critical currents of all turns are almost identical, and the anisotropy in I c (B) characteristic plays practically no role. Rather unexpected behavior of the voltage–current characteristic of the model coil is predicted if an external field is applied. (paper)

Critical current of pure SNS junctions

International Nuclear Information System (INIS)

Golub, A.A.; Bezzub, O.P.

1982-01-01

Boundary conditions at the superconductor-normal metal interface are determined, taking into account the differences in the effective masses and the density of states of the metals constituting the transition and assumed to be pure. The potential barrier of the interface is chosen to be zero. The critical current of the junction is calculated [ru

Topology-induced critical current enhancement in Josephson networks

International Nuclear Information System (INIS)

Silvestrini, P.; Russo, R.; Corato, V.; Ruggiero, B.; Granata, C.; Rombetto, S.; Russo, M.; Cirillo, M.; Trombettoni, A.; Sodano, P.

2007-01-01

We investigate the properties of Josephson junction networks with inhomogeneous architecture. The networks are shaped as 'square comb' planar lattices on which Josephson junctions link superconducting islands arranged in the plane to generate the pertinent topology. Compared to the behavior of reference linear arrays, the temperature dependencies of the Josephson currents of the branches of the network exhibit relevant differences. The observed phenomena evidence new and surprising behavior of superconducting Josephson arrays

Topology-induced critical current enhancement in Josephson networks

Energy Technology Data Exchange (ETDEWEB)

Silvestrini, P. [Dipartimento d' Ingegneria dell' Informazione, Seconda Universita di Napoli, Aversa (Italy); Istituto di Cibernetica ' E. Caianiello' del CNR, Pozzuoli (Italy)], E-mail: p.silvestrini@cib.na.cnr.it; Russo, R. [Istituto di Cibernetica ' E. Caianiello' del CNR, Pozzuoli (Italy); Corato, V. [Dipartimento d' Ingegneria dell' Informazione, Seconda Universita di Napoli, Aversa (Italy); Ruggiero, B.; Granata, C.; Rombetto, S.; Russo, M. [Istituto di Cibernetica ' E. Caianiello' del CNR, Pozzuoli (Italy); Cirillo, M. [Dipartimento di Fisica and INFM, Universita di Roma ' Tor Vergata' , 00173 Roma (Italy); Trombettoni, A. [International School for Advanced Studies and Sezione INFN, Via Beirut 2/4, 34104 Trieste (Italy); Sodano, P. [International School for Advanced Studies and Sezione INFN, Via Beirut 2/4, 34104 Trieste (Italy); Dipartimento di Fisica, Universita di Perugia, 06123 Perugia, and Sezione INFN, Perugia (Italy); Progetto Lagrange, Fondazione C.R.T. e Fondazione I.S.I., Dipartimento di Fisica, Politecnico di Torino, Corso Duca degli Abruzzi 24, 10124 Torino (Italy)

2007-10-29

We investigate the properties of Josephson junction networks with inhomogeneous architecture. The networks are shaped as 'square comb' planar lattices on which Josephson junctions link superconducting islands arranged in the plane to generate the pertinent topology. Compared to the behavior of reference linear arrays, the temperature dependencies of the Josephson currents of the branches of the network exhibit relevant differences. The observed phenomena evidence new and surprising behavior of superconducting Josephson arrays.

Temperature and pinning strength dependence of the critical current of a superconductor with a square periodic array of pinning sites

International Nuclear Information System (INIS)

Benkraouda, M.; Obaidat, I.M.; Al Khawaja, U.

2006-01-01

We have conducted extensive series of molecular dynamic simulations on driven vortex lattices interacting with periodic square arrays of pinning sites. In solving the over damped equation of vortex motion we took into account the vortex-vortex repulsion interaction, the attractive vortex-pinning interaction, and the driving Lorentz force at several values of temperature. We have studied the effect of varying the driving Lorentz force and varying the pinning strength on the critical current for several pinning densities, and temperature values. We have found that the pinning strength play an important role in enhancing the critical current over the whole temperature range. At low temperatures, the critical current was found to increase linearly with increasing the pinning strengths for all pinning densities. As the temperature increases, the effect of small pinning strengths diminishes and becomes insignificant at high temperatures

Strain reduced critical current in Bi-2223/Ag superconductors under axial tension and compression

International Nuclear Information System (INIS)

Haken, B. ten; Godeke, A.; Kate, H.H.J. ten

1997-01-01

The critical current of Ag sheathed Bi(Pb)SrCaCuO-2223 tape conductors is investigated as a function of various strain components. A reduction of the critical current occurs due to both tensile or a compressive strain. The critical current reduction is qualitatively similar with the results as observed in Bi-2212 conductors. An axial compression leads to an immediate critical current reduction. The critical current in an axially elongated sample remains nearly constant up to a certain limit typically close to 0.3% strain. For a larger elongation the critical current reduces rapidly. A transverse pressure acting on the tape surface leads also to an irreversible critical current reduction. This behavior is compared with the influence of an axial compression with an effective Young's modulus. The deformation induced critical current reductions in Bi-2223 conductors can be described by a model that is already proposed for Bi-2212 conductors. This model is based on the irreversible nature of the critical current reduction due to a certain deformation

Nursing care plans versus concept maps in the enhancement of critical thinking skills in nursing students enrolled in a baccalaureate nursing program.

Science.gov (United States)

Sinatra-Wilhelm, Tina

2012-01-01

Appropriate and effective critical thinking and problem solving is necessary for all nurses in order to make complex decisions that improve patient outcomes, safety, and quality of nursing care. With the current emphasis on quality improvement, critical thinking ability is a noteworthy concern within the nursing profession. An in-depth review of literature related to critical thinking was performed. The use of nursing care plans and concept mapping to improve critical thinking skills was among the recommendations identified. This study compares the use of nursing care plans and concept mapping as a teaching strategy for the enhancement of critical thinking skills in baccalaureate level nursing students. The California Critical Thinking Skills Test was used as a method of comparison and evaluation. Results indicate that concept mapping enhances critical thinking skills in baccalaureate nursing students.

Strain dependence of the critical current and critical field in multifilamentary Nb3Sn composites

International Nuclear Information System (INIS)

Ekin, J.W.

1979-01-01

High-J/sub c/ multifilamentary Nb 3 Sn superconductors with widely varying amounts of prestrain and critical field values can be characterized fairly accurately by a single normalized critical field-strain relationship. Such a relationship permits first order prediction of critical-current degradation at arbitrary magnetic field magnitudes with knowledge of only two parameters for any conductor, the prestrain and the maximum critical field. Some of the conductor-fabrication factors affecting the parameters are considered

Stress induced degradation of critical currents in filamentary Nb3Sn

International Nuclear Information System (INIS)

McDougall, I.L.

1976-01-01

An investigation of the critical stress and strain values of bronze, Nb 3 Sn composites at 4.2 K has been made with simultaneous determination of critical currents in a field of 2.5 Tesla. Evidence of grain boundary microcrack formation has been found associated with reversible degradation of critical current. At a critical strain characteristic of the composite geometry these cracks propagate to give a GB fracture network. A compound with a small grain size formed at low temperatures has the best mechanical properties with a critical strain to the onset of reversible degradation of about 0.5%. (author)

Microstructural factors influencing critical-current densities of high-temperature superconductors

International Nuclear Information System (INIS)

Suenaga, M.

1992-01-01

Microstructural defects are the primary determining factors for the values of critical current densities in superconductors. A review is made to assess, (1) what would be the maximum achievable critical-current density in the oxide superconductors if nearly ideal pinning sites were introduced? and (2) what types of pinning defects are currently introduced in these superconductors and how effective are these in pinning the vortices? Only the case where the applied field is parallel to the c-axis is considered here

Critical unpairing currents in narrow niobium films

International Nuclear Information System (INIS)

Gershenzon, M.E.; Gubankov, V.N.

1979-01-01

Investigated are the dependences of critical currents of narrow ( with the width of W=0.5-15 μm) superconducting niobium films on temperature and a magnetic field. The proposed method of film production with the width of the 1μm order and with small edge inhomogeneities ((<=500 A) permitted to realize the Ginsburg-Landau unpairing currents in the wide range of temperatures. The correct comparison with the theory showed that the unpairing currents are observed if W(< or approximately) 2delta, where delta is the effective depth of the penetration of the perpendicular magnetic field

Online discussion: Enhancing students' critical thinking skills

Science.gov (United States)

Rathakrishnan, Mohan; Ahmad, Rahayu; Suan, Choo Ling

2017-10-01

Online discussion has become one of the important strategies for the teacher to teach the students to think critically when conveying their ideas and become more proactive and creative. In this paper, padlet online discussion communication was conducted to examine its effectiveness in enhancing critical thinking. In this study, there are two types of critical thinking: macro and micro critical thinking. A total of 70 Universiti Utara Malaysia Management Foundation Programme students involved in this experimental research design. The students in treatment class are divided to few groups. Every group uses padlet online discussion to discuss the topic given. All the group members discuss and write their ideas in padlet. Ideas that are posted in padlet will be displayed in front of the class so that the entire group in the treatment class could see the given ideas. Paul's (1993) model was used to analyze student's macro and micro critical thinking in padlet online discussion and communication. The finding shows that students who used padlet online discussion backchannel communication have greater macro and micro critical thinking level than students who do not use online discussion.

Critical Current Properties in Longitudinal Magnetic Field of YBCO Superconductor with APC

Science.gov (United States)

Kido, R.; Kiuchi, M.; Otabe, E. S.; Matsushita, T.; Jha, A. K.; Matsumoto, K.

The critical current density (Jc) properties of the Artificial Pinning Center (APC) introduced YBa2Cu3O7 (YBCO) films in the longitudinal magnetic field were measured. Y2O3 or Y2BaCuO5 (Y211) was introduced as APCs to YBCO, and YBCO films with APC were fabricated on SrTiO3 single crystal substrate. The sizes of Y2O3 and Y211 were 5-10 nm and 10-20 nm, respectively. As a result, Jc enhancement in the longitudinal magnetic field was observed in Y2O3 introduced YBCO films. However, it was not observed in Y211 introduced YBCO films. Therefore, it was considered that Jc properties in the longitudinal magnetic field were affected by introducing of small size APC, and it was necessary that APC does not disturb the current pathway in the superconductor.

Use of a Web Site to Enhance Criticality Safety Training

International Nuclear Information System (INIS)

Huang, S T; Morman, J

2003-01-01

Currently, a website dedicated to enhancing communication and dissemination of criticality safety information is sponsored by the U.S. Department of Energy (DOE) Nuclear Criticality Safety Program (NCSP). This website was developed as part of the DOE response to the Defense Nuclear Facilities Safety Board (DNFSB) Recommendation 97-2, which reflected the need to make criticality safety information available to a wide audience. The website is the focal point for DOE nuclear criticality safety (NCS) activities, resources and references, including hyperlinks to other sites actively involved in the collection and dissemination of criticality safety information. The website is maintained by the Lawrence Livermore National Laboratory (LLNL) under auspices of the NCSP management. One area of the website contains a series of Nuclear Criticality Safety Engineer Training (NCSET) modules. During the past few years, many users worldwide have accessed the NCSET section of the NCSP website and have downloaded the training modules as an aid for their training programs. This trend was remarkable in that it points out a continuing need of the criticality safety community across the globe. It has long been recognized that training of criticality safety professionals is a continuing process involving both knowledge-based training and experience-based operations floor training. As more of the experienced criticality safety professionals reach retirement age, the opportunities for mentoring programs are reduced. It is essential that some method be provided to assist the training of young criticality safety professionals to replenish this limited human expert resource to support on-going and future nuclear operations. The main objective of this paper is to present the features of the NCSP website, including its mission, contents, and most importantly its use for the dissemination of training modules to the criticality safety community. We will discuss lessons learned and several ideas

Magnetic properties and critical current density of bulk MgB2 polycrystalline with Bi-2212 addition

International Nuclear Information System (INIS)

Shen, T M; Li, G; Zhu, X T; Cheng, C H; Zhao, Y

2005-01-01

Bulk samples of MgB 2 were prepared with 0, 3, 5, and 10 wt% Bi 2 Sr 2 CaCu 2 O 8 (Bi-2212) particles, added using a simple solid-state reaction route in order to investigate the effect of inclusions of a material with higher T c than the superconducting matrix. The density, diamagnetic signal, and critical current density, J c , of the samples change significantly with the doping level. It is found that J c is significantly enhanced by the Bi-2212 addition. Microstructural analysis indicates that a small amount of Bi-2212 is decomposed into Cu 2 O and other impurity phases while a significant amount of unreacted Bi-2212 particles remains in MgB 2 matrix, and these act as effective pinning centres for vortices. The enhanced pinning force is mainly attributable to these highly dispersed inclusions inserted in the MgB 2 grains. Despite the effectiveness of the high-T c inclusions in increasing superconducting critical currents in our experiment, our results seem to demonstrate the superiority of attractive centres over repulsive ones. A pinning mechanism is proposed to account for the contribution of this type of pinning centre in MgB 2 superconductors. (rapid communication)

Critical currents and fields of disordered nanocrystalline superconductors

International Nuclear Information System (INIS)

Yavary, H.; Shahzamanian, M.A.; Rabbani, H.

2007-01-01

Full text: There is an enormous effort directed at increasing the upper critical field of the superconducting materials because this upper critical field provides a fundamental limit to the maximum field a magnet system can produce. High-energy particle accelerators and medical resonance imaging body scanners are limited by the for NbTi (10 T). Gigahertz class nuclear-magnetic-resonance and high field laboratory magnets are limited by for Nb 3 Sn (23 T) [1]. However, the values of critical current density are too low for industrial use, possibly because of degraded or nonsuperconducting phases, such as MoS 2 or Mo 2 S 3 , at the grain boundaries or because the pinning site density is not high enough. It has long been known that decreasing the grain size of low-temperature superconducting (LTS) materials, such as Nb 3 Sn, increases the density of flux pinning sites and hence. Nanocrystalline materials are characterized by ultrafine grains and a high density of grain boundaries [2]. Hence nanocrystalline materials can exhibit unusual physical, chemical, and mechanical properties with respect to conventional polycrystalline materials. The purpose of this paper is to investigate the structure of currents and fields in disordered nanocrystalline superconducting materials by the use of quasiclassical many body techniques. The Keldish Greens functions are used to calculate the current density of the system. Since the disorder and microstructure of these nanocrystalline materials are on a sufficiently short length scale as to increase both the density of pinning site and the upper critical field. (authors)

Critical potentials, leptons, and weak currents

International Nuclear Information System (INIS)

Smith, P.F.; Lewin, J.D.

1977-12-01

A theoretical study is made of the interaction of very strong localised electromagnetic potentials with charged leptons, and with the vacuum state. The principal objective is to investigate the phenomena which occur when the potential reaches or exceeds the critical value at which bound levels are drawn into the lower continuum. The behaviour of bound and continuum solutions of the Dirac equation for the specific model of a short range potential well in an arbitrarily large bounded volume is examined in detail. Vacuum polarisation effects are computed by summation over the infinite set of single particle levels, and special attention is given to the behaviour of the overall charge distribution as the potential strength increases through the critical value. The most significant features of the results are (a) the formation of highly localised electron or muon bound states, (b) similar critical potential strengths for electrons and muons, and (c) redefinition of the vacuum by one charge unit at the critical potential. These features are analogous to some properties of leptonic and hadronic weak currents, and the hypothesis is proposed that strong short range potentials may provide a possible mediating mechanism for the weak interaction and also a lepton confinement mechanism within the structure of hadrons. (author)

The enhancement of critical current density on the bulk of BPSCCO-system superconductor with silver additions

International Nuclear Information System (INIS)

Engkir Sukirman; Wisnu Ari Adi; Puji Sulisworo dan W Prasuad

1999-01-01

The influence of silver additions on the critical current density (Jc) of BPSCCO-bulk superconductor was investigated, with the aim of getting an increase of its Jc and trying to find out a correlation of Jc and structures of BPSCCO-silver composites. The BPSCCO-system superconductors with nominal composition Bi 1.84 Pb 0.34 Sr 2.00 Ca 2.03 Cu 3.06 O x (2223-phase) were synthesized by using solid state reaction method. The silver added was in the powder-AgO form varied from 0 to 30 wt % AgO. The critical current density, crystal structure, and micro-structure of BPSCCO-silver composites were characterized by means of four-point probe, x-ray diffractometer, and scanning electron microscope that is equipped with a link system energy dispersive spectrometer. It was found that silver additions to BPSCCO cause a reasonable improvement in Jc from 120 to 215 A/cm 2 , and a slight increase in Tc from 92 to 108 K, and lattice parameters of the 2223-phase from a 3.811(3) to 3.820(2) A, and from c = 37.08(3) to 37.15(2) A, with the optimum value occurs at 20 wt % AgO. The AgO powders added to the BPSCCO specimens were converted to Ag 2 O and metallic Ag during the annealing process at 827degC for 96 h in air. The addition of AgO to BPSCCO system does not necessarily lead to decomposition of the 2223-phase. The AgO reacts with and suppresses the 2201-phase. (author)

On the critical current of ionisation waves in gas discharges

International Nuclear Information System (INIS)

Sato, M.

1982-01-01

Measurement methods for determining the critical current of ionisation waves in gas discharge tubes are examined in detail. The conventional visual method which finds the current at which the waves disappear is erroneous since the criterion, 'observable', depends on the observing conditions. In the rigorous method it is defined as a current at which the linear growth rate of waves is zero. For the measured upper critical (Pupp) current of argon gas, close agreement is found between the results of other workers and those of the present author over a wide range of pressure-radius product 0.3 approximately equal to 60 Torr cm. (author)

Microstructure and critical current density in high-Tc metal oxide superconductors

International Nuclear Information System (INIS)

Johnson, S.M.; Gusman, M.I.

1992-03-01

Superconductor powders in the U-Ba-Cu-O (YBCO) and Bi-Pb-Sr-Ca-Cu-O (BSCCO) systems were synthesized by freeze-drying. Powders were characterized, and processed into samples for evaluation of superconducting behavior. Freeze-drying is attractive because the powders have high purity, are homogeneous, have a small size and are active. YBCO powders can be sintered to high density at 890 degrees C. Many compositions, processing approaches and heat treatments were explored in an effort to understand relations between microstructure and critical density, and to improve the critical current density. Powders were also formed into sputtering targets for coating preparation at Stanford University. The highest critical current density achieved with the YBCO powders was ∼15,000 A/cm 2 at 4.2K and 0.5T using powders treated to prevent carbon contamination. The BSCCO materials with the highest critical current density, ∼30,000 A/cm 2 at the same conditions were formed by heat treating melted and quenched samples. All critical current density measurements were made by Stanford University, a subcontractor to this effort. Stanford University also prepared coatings by off-axis magnetron sputtering

Enhancement of critical temperature in fractal metamaterial superconductors

Energy Technology Data Exchange (ETDEWEB)

Smolyaninov, Igor I., E-mail: smoly@umd.edu [Department of Electrical and Computer Engineering, University of Maryland, College Park, MD 20742 (United States); Smolyaninova, Vera N. [Department of Physics Astronomy and Geosciences, Towson University, 8000 York Road, Towson, MD 21252 (United States)

2017-04-15

Fractal metamaterial superconductor geometry has been suggested and analyzed based on the recently developed theoretical description of critical temperature increase in epsilon near zero (ENZ) metamaterial superconductors. Considerable enhancement of critical temperature has been predicted in such materials due to appearance of large number of additional poles in the inverse dielectric response function of the fractal. Our results agree with the recent observation (Fratini et al. Nature 466, 841 (2010)) that fractal defect structure promotes superconductivity.

Technique of Critical Current Density Measurement of Bulk Superconductor with Linear Extrapolation Method

International Nuclear Information System (INIS)

Adi, Wisnu Ari; Sukirman, Engkir; Winatapura, Didin S.

2000-01-01

Technique of critical current density measurement (Jc) of HTc bulk ceramic superconductor has been performed by using linear extrapolation with four-point probes method. The measurement of critical current density HTc bulk ceramic superconductor usually causes damage in contact resistance. In order to decrease this damage factor, we introduce extrapolation method. The extrapolating data show that the critical current density Jc for YBCO (123) and BSCCO (2212) at 77 K are 10,85(6) Amp.cm - 2 and 14,46(6) Amp.cm - 2, respectively. This technique is easier, simpler, and the use of the current flow is low, so it will not damage the contact resistance of the sample. We expect that the method can give a better solution for bulk superconductor application. Key words. : superconductor, critical temperature, and critical current density

A Critical Test of Self-Enhancement, Exposure, and Self-Categorization Explanations for First- and Third-Person Perceptions

Science.gov (United States)

Reid, Scott A.; Byrne, Sahara; Brundidge, Jennifer S.; Shoham, Mirit D.; Marlow, Mikaela L.

2007-01-01

The third-person perception is the tendency for people to believe that others are more influenced by media content than themselves (W. P. Davison, 1983). The current study provides a critical test of self-enhancement, exposure, and self-categorization explanations for first- (i.e., self more influenced than others) and third-person perceptions.…

Non Pharmacological Cognitive Enhancers - Current Perspectives.

Science.gov (United States)

Sachdeva, Ankur; Kumar, Kuldip; Anand, Kuljeet Singh

2015-07-01

Cognition refers to the mental processes involved in thinking, knowing, remembering, judging, and problem solving. Cognitive dysfunctions are an integral part of neuropsychiatric disorders as well as in healthy ageing. Cognitive Enhancers are molecules that help improve aspects of cognition like memory, intelligence, motivation, attention and concentration. Recently, Non Pharmacological Cognitive Enhancers have gained popularity as effective and safe alternative to various established drugs. Many of these Non Pharmacological Cognitive Enhancers seem to be more efficacious compared to currently available Pharmacological Cognitive Enhancers. This review describes and summarizes evidence on various Non Pharmacological Cognitive Enhancers such as physical exercise, sleep, meditation and yoga, spirituality, nutrients, computer training, brain stimulation, and music. We also discuss their role in ageing and different neuro-psychiatric disorders, and current status of Cochrane database recommendations. We searched the Pubmed database for the articles and reviews having the terms 'non pharmacological and cognitive' in the title, published from 2000 till 2014. A total of 11 results displayed, out of which 10 were relevant to the review. These were selected and reviewed. Appropriate cross-references within the articles along with Cochrane reviews were also considered and studied.

Critical currents of variable thickness bridges

International Nuclear Information System (INIS)

Lapir, G.M.; Likharev, K.K.; Maslova, L.A.; Semenov, V.K.

1975-01-01

A variable thickness bridge (VTB) is a short strip of thin normal or superconducting electrodes - 'banks'. This type of weak link has the peculiarity of having the changes of the modulus of the orderparameter localized in the film of the bridge. Only changes of the phase of the orderparameter take place in the banks, and so the electrodynamics of the banks is linear. The problem of the distribution of the linear density of current Jsub(s)(psi) and of the phase difference of the banks psi along the VTB width is considered and the critical current Isub(c) for the important case of a VTB deposited over a superconducting ground plate - 'screen' is calculated. (Auth.)

Oscillation of Critical Current by Gate Voltage in Cooper Pair Transistor

International Nuclear Information System (INIS)

Kim, N.; Cheong, Y.; Song, W.

2010-01-01

We measured the critical current of a Cooper pair transistor consisting of two Josephson junctions and a gate electrode. The Cooper pair transistors were fabricated by using electron-beam lithography and double-angle evaporation technique. The Gate voltage dependence of critical current was measured by observing voltage jumps at various gate voltages while sweeping bias current. The observed oscillation was 2e-periodic, which shows the Cooper pair transistor had low level of quasiparticle poisoning.

Distribution of local critical current along sample length and its relation to overall current in a long Bi2223/Ag superconducting composite tape

International Nuclear Information System (INIS)

Ochiai, S; Doko, D; Okuda, H; Oh, S S; Ha, D W

2006-01-01

The distribution of the local critical current and the n-value along the sample length and its relation to the overall critical current were studied experimentally and analytically for the bent multifilamentary Bi2223/Ag/Ag-Mg alloy superconducting composite tape. Then, based on the results, it was attempted to simulate on a computer the dependence of the critical current on the sample length. The main results are summarized as follows. The experimentally observed relation of the distributed local critical current and n-value to the overall critical current was described comprehensively with a simple voltage summation model, in which the sample was regarded as a one-dimensional series circuit. The sample length dependence of the critical current was reproduced on the computer by a Monte Carlo simulation incorporating the voltage summation model and the regression analysis results for the local critical current distribution and the relation of the n-value to the critical current

Critical current characteristics and history dependence in superconducting SmFeAsOF bulk

International Nuclear Information System (INIS)

Ni, B; Ge, J; Kiuchi, M; Otabe, E S; Gao, Z; Wang, L; Qi, Y; Zhang, X; Ma, Y

2010-01-01

The superconducting SmFeAsO 1-x F x (x=0.2) polycrystalline bulks were prepared by the powder-in-tube (PIT) method. The magnetic field and temperature dependences of critical current densities in the samples were investigated by resistive and ac inductive (Campbell's) methods. It was found that a fairly large shielding current density over 10 9 A/m 2 , which is considered to correspond to the local critical current density, flows locally with the perimeter size similar to the average grain size of the bulk samples, while an extremely low transport current density of about 10 5 A/m 2 corresponding to the global critical current density flows through the whole sample. Furthermore, a unique history dependence of global critical current density was observed, i.e., it shows a smaller value in the increasing-field process than that in the decreasing-field process. The history dependence of global critical current characteristic in our case can be ascribed to the existence of the weak-link property between the grains in SmFeAsO 1-x F x bulk.

Mesoscopic fluctuations in the critical current in InAs-coupled Josephson junctions

International Nuclear Information System (INIS)

Takayanagi, Hideaki; Hansen, J.B.; Nitta, Junsaku

1994-01-01

Mesoscopic fluctuations were confirmed for the critical current in a p-type InAs-coupled Josephson junction. The critical current was measured as a function of the gate voltage corresponding to the change in the Fermi energy. The critical current showed a mesoscopic fluctuation and its behavior was the same as that of the conductance measured at the same time in both the weak and strong localization regimes. The magnitude and the typical period of the fluctuation are discussed and compared to theoretical predictions. ((orig.))

Processing and critical currents of high-Tc superconductor wires

International Nuclear Information System (INIS)

Krauth, H.; Heine, K.; Tenbrink, J.

1991-01-01

High-Tc superconductors are expected to have a major impact on magnet and energy technology. For technical applications they have to fulfill the requirement of carrying sufficient current at a critical current density of the order of 10 5 A/cm 2 at operating temperature and magnetic field. At 77 K these values have not been achieved yet in bulk material or wires due to weak link problems and flux creep effects. Progress made so far and remaining problems will be discussed in detail concentrating on problems concerning development of technical wires. In Bi-based materials technically interesting critical current densities could be achieved at 4.2 K in fields above 20 T (1,2), rendering possible the use of such material for very high field application. (orig.)

Enhanced Critical Thinking Skills through Problem-Solving Games in Secondary Schools

Science.gov (United States)

McDonald, Scott Douglas

2017-01-01

Aim/Purpose: Students face many challenges improving their soft skills such as critical thinking. This paper offers one possible solution to this problem. Background: This paper considers one method of enhancing critical thinking through a problem-solving game called the Coffee Shop. Problem-solving is a key component to critical thinking, and…

Non-monotonic field dependence of critical current in composite superconductors

International Nuclear Information System (INIS)

Andrianov, V.V.; Baev, V.P.; Ivanov, S.S.

1982-01-01

The nonmonotonic field dependence of critical current Im(B/sub a/ in composite superconductors is investigated experimentally for current and field varying simultaneously with final rates I and B/sub a/

Electromigration kinetics and critical current of Pb-free interconnects

Energy Technology Data Exchange (ETDEWEB)

Lu, Minhua; Rosenberg, Robert [IBM T. J. Watson Research Center, Yorktown Heights, New York 10598 (United States)

2014-04-07

Electromigration kinetics of Pb-free solder bump interconnects have been studied using a single bump parameter sweep technique. By removing bump to bump variations in structure, texture, and composition, the single bump sweep technique has provided both activation energy and power exponents that reflect atomic migration and interface reactions with fewer samples, shorter stress time, and better statistics than standard failure testing procedures. Contact metallurgies based on Cu and Ni have been studied. Critical current, which corresponds to the Blech limit, was found to exist in the Ni metallurgy, but not in the Cu metallurgy. A temperature dependence of critical current was also observed.

Critical current and electric transport properties of superconducting epitaxial Nb(Ti)N submicron structures

Science.gov (United States)

Klimov, A.; Słysz, W.; Guziewicz, M.; Kolkovsky, V.; Wegrzecki, M.; Bar, J.; Marchewka, M.; Seredyński, B.

2016-12-01

Critical current and current-voltage characteristics of epitaxial Nb(Ti)N submicron ultrathin structures were measured as function of temperature. For 700-nm-wide bridge we found current-driven vortex de-pinning at low temperatures and thermally activated flux flow closer to the transition temperature, as the limiting factors for the critical current density. For 100-nm-wide meander we observed combination of phase-slip activation and vortex-anti-vortex pair (VAP) thermal excitation. Our Nb(Ti)N meander structure demonstrates high de-pairing critical current densities 107 A/cm2 at low temperatures, but the critical currents are much smaller due to presence of the local constrictions.

Phthalocyanine doping to improve critical current densities in MgB2 tapes

International Nuclear Information System (INIS)

Zhang Xianping; Ma Yanwei; Wang Dongliang; Gao Zhaoshun; Wang Lei; Qi Yanpeng; Awaji, Satoshi; Watanabe, Kazuo; Mossang, Eric

2009-01-01

Phthalocyanine-doped MgB 2 tapes were prepared by the in situ powder-in-tube method. The relationships between the critical current properties, crystallinity and microstructure were studied as a function of the phthalocyanine doping level. It is found that both H irr and H c2 were improved when MgB 2 samples were doped with phthalocyanine, which are mainly attributed to the effective carbon substitution and enhanced flux pinning strength caused by very fine grain sizes. Furthermore, compared to pure samples, the MgO content remained almost unchanged in all doped tapes, which is very beneficial to having better grain connectivity in MgB 2 . Significantly improved J c was obtained in the phthalocyanine-doped MgB 2 tapes, especially under high magnetic fields.

Critical current studies on fine filamentary NbTi accelerator wires

International Nuclear Information System (INIS)

Garber, M.; Sabatini, R.L.; Sampson, W.B.; Suenaga, M.

1986-01-01

The magnets for the Superconducting Super Collider, a high energy proton colliding beam accelerator, require a superconductor with very high current density (> 2400 A/mm 2 at 5 T) and very small filaments ( about 2μ m in diameter). Previous work has shown that by controling the formation of Cu 4 Ti compound particles on the filament surfaces it is possible to make fine filamentary NbTi wire with high critical current density. The performance of multi-filamentary wire is characterized by the current density and the quantity ''n'' which describes the superconducting-normal transition. Micrographs of wires having high J /SUB c/ and high n show smooth, uniform filaments. Recently wires of very high critical current and high n have been produced in experimental quantities by commercial manufacturers

Critical current studies on fine filamentary NbTi accelerator wires

International Nuclear Information System (INIS)

Garber, M.; Suenaga, M.; Sampson, W.B.; Sabatini, R.L.

1985-01-01

The magnets for the Superconductig Super Collider, a high energy proton colliding beam accelerator, require a superconductor with very high current density (>2400 A/mm 2 at 5 T) and very small filaments (approx. 2μm in diameter). Previous work has shown that by controlling the formation of Cu 4 Ti compound particles on the filament surfaces it is possible to make fine filamentary NbTi wire with high critical current density. The performance of multi-filamentary wire is characterized by the current density and the quantity ''n'' which describes the superconducting-normal transition. Micrographs of wires having high J/sub c/ and high n show smooth, uniform filaments. Recently wires of very high critical current and high n have been produced in experimental quantities by commercial manufactures

Modification of critical current in HTSC tape conductors by a ferromagnetic layer

International Nuclear Information System (INIS)

Goemoery, F; Souc, J; Seiler, E; Vojenciak, M; Granados, X

2008-01-01

In some applications of tape conductors from high temperature superconductors (HTSC) the magnetic field is created by the transported current itself. This is e.g. the case of power transmission cables or current leads. Quite complex distribution of local magnetic field determines then the ability of the superconducting element to carry electrical current. We have investigated how much the critical current of a tape conductor can be changed by putting a ferromagnetic layer in the vicinity of the HTSC material. Numerical procedure has been developed to resolve the current and field distribution in such superconductor-ferromagnet composite tape. Theoretical predictions have been confirmed by experiments on sample made from Bi-2223/Ag composite tape. The critical current of such tape can be improved by placing a soft ferromagnetic material at the tape's edges. On the other hand, the calculations show that the ferromagnetic substrate of YBCO coated tape reduces its self-field critical current

Electric field effect on the critical current of SNS-contact

International Nuclear Information System (INIS)

Rakhmanov, A.L.; Rozhkov, A.V.

1995-01-01

Electric field effect on the SNS-contact critical current is investigated in the Ginzburg-Landau theory approximation. It is shown that the electric field may cause a notable increase of the contact critical current especially if the sample temperature is close to the temperature of a superconducting transition of T sc normal layer. Electric field effect is increased with the reduction of film thickness, but it can strong enough for thick films as well at temperature close to T sc . 11 refs.; 4 figs

New developments enhancing MCNP for criticality safety

International Nuclear Information System (INIS)

Hendricks, J.S.; McKinney, G.W.; Forster, R.A.

1993-01-01

Since the early 80's MCNP has had three estimates of k eff : collision, absorption, and track length. MCNP has also had collision and absorption estimators of removal lifetime. These are calculated for every cycle and are averaged over the cycles as simple averages and covariance weighted averages. Correlation coefficients between estimators are also calculated. These criticality estimators are all in addition to the extensive summary information and tally edits used in shielding and other problems. A number of significant new developments have been made to enhance the MCNP Monte Carlo radiation transport code for criticality safety applications. These are available in the newly released MCNP4A version of the code

Critical current density for spin transfer torque switching with composite free layer structure

OpenAIRE

You, Chun-Yeol

2009-01-01

Critical current density of composite free layer (CFL) in magnetic tunneling junction is investigated. CFL consists of two exchange coupled ferromagnetic layers, where the coupling is parallel or anti-parallel. Instability condition of the CFL under the spin transfer torque, which is related with critical current density, is obtained by analytic spin wave excitation model and confirmed by macro-spin Landau-Lifshitz-Gilbert equation. The critical current densities for the coupled two identical...

Crack problem in superconducting cylinder with exponential distribution of critical-current density

Science.gov (United States)

Zhao, Yufeng; Xu, Chi; Shi, Liang

2018-04-01

The general problem of a center crack in a long cylindrical superconductor with inhomogeneous critical-current distribution is studied based on the extended Bean model for zero-field cooling (ZFC) and field cooling (FC) magnetization processes, in which the inhomogeneous parameter η is introduced for characterizing the critical-current density distribution in inhomogeneous superconductor. The effect of the inhomogeneous parameter η on both the magnetic field distribution and the variations of the normalized stress intensity factors is also obtained based on the plane strain approach and J-integral theory. The numerical results indicate that the exponential distribution of critical-current density will lead a larger trapped field inside the inhomogeneous superconductor and cause the center of the cylinder to fracture more easily. In addition, it is worth pointing out that the nonlinear field distribution is unique to the Bean model by comparing the curve shapes of the magnetization loop with homogeneous and inhomogeneous critical-current distribution.

Numerical prediction of a dip effect in the critical current density

International Nuclear Information System (INIS)

Al Khawaja, U.; Benkraouda, M.; Obaidat, I.M.

2007-01-01

We have conducted extensive series of molecular dynamic simulations on the properties of the critical current density in systems with periodic square arrays of pinning sites. The density of the pinning sites was kept fixed while the density of vortices, pinning strength, and temperature were varied several times. At zero temperature, we have observed a substantial dip in the critical current density that occurs only at a fixed value of the vortex density and for specific values of pinning strength. We have found that the occurrence of the dip depends mainly on the initial positions of the vortices with respect to the positions of the pinning sites. At the dip, we have found that the interstitial vortices form moving channels leading to the observed drop in the critical current density

Induced critical current density limit of Ag sheathed Bi-2223 tape conductor

International Nuclear Information System (INIS)

Ogiwara, H.; Satou, M.; Yamada, Y.; Kitamura, T.; Hasegawa, T.

1994-01-01

The authors have already reported the best critical current density of 66,000 A/cm 2 with an Ag sheathed Bi-2223 tape conductor. The Brick-wall model is for explaining the current transport mechanism of this conductor. The model has its roots in the fact that the Bi-2223 tape core is a complicated stack of crystals which have a mica-flake structure. The orientation of the crystals which have a mica-flake structure. The orientation of the crystals seriously affects the current transport capability. Moreover, the contacts between the stacking crystals are very important. The transport current flows dividing into many branch paths. Under high magnetic field, the different paths experienced different electromagnetic forces. Differences between the electromagnetic forces on the different crystals can affect the contacts so as to increase resistivity and decrease overall critical current density of the tape. This effect can foretell the limit of the critical current density obtainable with these kinds of conductors

Critical current measurement in superconducting rings using an automatic inductive technique

International Nuclear Information System (INIS)

Gonzalez-Jorge, H.; Linares, B.; Quelle, I.; Carballo, E.; Romani, L.; Domarco, G.

2007-01-01

A measurement technique was developed to identify the critical current of superconducting rings. It is based on the detection of the voltage on a secondary coil when the current induced in the superconductor by a primary one go beyond to the critical value. The technique uses a DC power supply to control the AC current circulating by the primary circuit. Such circuit mainly consists on an AC power supply which gives a constant AC voltage, a primary inducting coil and a control coil with iron core. The AC current circulating by this circuit is modified with the change in the impedance of the control coil due to the fact of the DC current supplied by the power supply in parallel with it

Effect of 520 MeV Kr{sup 20+} ion irradiation on the critical current density of Bi-2212 single crystals

Energy Technology Data Exchange (ETDEWEB)

Terai, Takayuki; Ito, Yasuyuki [Tokyo Univ. (Japan). Faculty of Engineering; Kishio, Kouji

1996-10-01

Change in magnetic properties of Bi{sub 2}Sr{sub 2}CaCu{sub 2}O{sub 8+y} (Bi-2212) single crystals due to Kr{sup 20+} ion irradiation is reported, focused on critical current density and irreversibility magnetic field. The Bi-2212 single crystal specimens (3x3x0.3 mm{sup 3}) were prepared by the floating zone method. Each specimen was irradiated with 520 MeV Kr{sup 20+} ions of 10{sup 10}-10{sup 11} cm{sup -2} in the fluence. Magnetic hysteresis was measured at 4.2K-60K with a vibrating sample magnetometer before and after irradiation. Very large enhancement was observed in critical current density and irreversibility magnetic field above 20K. (author)

Transport measurements in superconductors: critical current of granular high TC ceramic superconductor samples

International Nuclear Information System (INIS)

Passos, W.A.C.

2016-01-01

This work presents a method to obtain critical current of granular superconductors. We have carried out transport measurements (ρxT curves and VxI curves) in a YBa_2Cu_3O_7_-_δ sample to determine critical current density of it. Some specimens reveal a 'semiconductor-like' behavior (electrical resistivity decreases with increasing temperatures above critical temperature T_c of material) competing with superconductor behavior. Due to high granular fraction of the sample, these competition is clearly noted in ρxT curves. Measurements carried out from 0 to 8500 Oe of applied field show the same behavior, and the critical current density of the samples is shown. (author)

Critical current of Josephson contacts with accidental position of vortexes

International Nuclear Information System (INIS)

Fistul', M.V.

1989-01-01

Josephson contact critical current dependence on magnetic field under different concentrations of Abrikosov vortices (AV) in superconducting shores is found. Pinned vortex concentration as well as correlation in the vortex position can be determined by Josephson current dependence on magnetic field

Critical current in the Integral Quantum Hall Effect

International Nuclear Information System (INIS)

Kostadinov, I.Z.

1985-11-01

A multiparticle theory of the Integral Quantum Hall Effect (IQHE) was constructed operating with pairs wave function as an order parameter. The IQHE is described with bosonic macroscopic states while the fractional QHE with fermionic ones. The calculation of the critical current and Hall conductivity temperature dependence is presented. (author)

Enhancement of Students' Independent Learning through Their Critical Thinking Skills Development

Science.gov (United States)

Kopzhassarova, Umit; Akbayeva, Gulden; Eskazinova, Zhanar; Belgibayeva, Gulbarshyn; Tazhikeyeva, Akerke

2016-01-01

The article focuses on the problem of developing students' critical thinking skills, which help them become independent learners. Analysis of research works of educators and scholars enable the authors to reveal qualities, necessary for students to enhance their critical thinking skills and become independent learners. Different points of view on…

Magnetic Field Dependence of the Critical Current in S-N Bilayer Thin Films

Science.gov (United States)

Sadleir, John E.; Lee, Sang-Jun; Smith, Stephen James; Bandler, Simon; Chervenak, James; Kilbourne, Caroline A.; Finkbeiner, Fred M.; Porter, Frederick S.; Kelley, Richard L.; Adams, Joseph S.;

Critical currents and superconductivity ferromagnetism coexistence in high-Tc oxides

CERN Document Server

Khene, Samir

2016-01-01

The book comprises six chapters which deal with the critical currents and the ferromagnetism-superconductivity coexistence in high-Tc oxides. It begins by gathering key data for superconducting state and the fundamental properties of the conventional superconductors, followed by a recap of the basic theories of superconductivity. It then discusses the differences introduced by the structural anisotropy on the Ginzburg-Landau approach and the Lawrence-Doniach model before addressing the dynamics of vortices and the ferromagnetism-superconductivity coexistence in high-Tc oxides, and provides an outline of the pinning phenomena of vortices in these materials, in particular the pinning of vortices by the spins. It elucidates the methods to improve the properties of superconducting materials for industrial applications. This optimization aims at obtaining critical temperatures and densities of critical currents at the maximum level possible. Whereas the primary objective is the basic mechanisms pushing the superco...

Strand critical current degradation in $Nb_{3}$ Sn Rutherford cables

CERN Document Server

Barzi, E; Higley, H C; Scanlan, R M; Yamada, R; Zlobin, A V

2001-01-01

Fermilab is developing 11 Tesla superconducting accelerator magnets based on Nb/sub 3/Sn superconductor. Multifilamentary Nb/sub 3/Sn strands produced using the modified jelly roll, internal tin, and powder-in-tube technologies were used for the development and test of the prototype cable. To optimize the cable geometry with respect to the critical current, short samples of Rutherford cable with packing factors in the 85 to 95% range were fabricated and studied. In this paper, the results of measurements of critical current, n-value and RRR made on the round virgin strands and on the strands extracted from the cable samples are presented. (5 refs).

Ponderomotive enhancement of charged particle beam limiting current

International Nuclear Information System (INIS)

Grebogi, C.; Uhm, H.S.

1987-01-01

The space charge limiting current problem is investigated for a magnetized particle beam propagating in a cylindrical drift tube and in presence of a waveguide mode. It is shown that with a proper choice of a waveguide mode, the limiting current can be greatly enhanced due to ponderomotive effects. Physically, this is accomplished by using the ponderomotive energy to reduce the potential depression due to the beam's self space charge field. Formulas for the limiting current as a function of beam energy and waveguide r.f. field for solid and hollow beams are derived. It is found from these formulas that, in appropriate parameter regimes, the space charge limiting current, say, of a 250kV bem can be enhanced by 70%

Critical current characteristics in high T/sub c/ oxide superconductors

International Nuclear Information System (INIS)

Matsushita, T.; Ni, B.

1989-01-01

Critical current densities are theoretically estimated for single-crystalline thin films, polycrystalline bulk materials with oriented and random textures of superconducting oxides. The percolation theory is used and the effect of depression of the transport current through grain boundaries is taken into account. A comparison is made with existing experimental results

A Monte Carlo simulation on critical current distribution of bent-damaged multifilamentary Bi2223 composite tape

International Nuclear Information System (INIS)

Ochiai, S.; Okuda, H.; Fujimoto, M.; Shin, J.K.; Oh, S.S.; Ha, D.W.

2011-01-01

We simulate critical current distribution of bent-damaged Bi2223 composite tape. We use a Monte Carlo method and a damage evolution model for simulation. With the present simulation approach, experimental results are described well. Critical current distribution stems mainly from difference in damage evolution. It was attempted to reproduce the measured critical current (I c ) distributions of the Bi2223 composite tape bent by 0-0.833% by simulation. Simulation was carried out with a Monte Carlo method in combination with a model that correlates the critical current to damage evolution. Two variables that differ from specimen to specimen were input in the simulation. One was the damage strain parameter, with which the difference in extent of damage among specimens was expressed. Another was the original critical current (I c0 ) values at zero bending strain. With the present simulation approach, the measured distributions of critical current at various bending strains, and the measured variations of average and coefficient of variation of critical current values with increasing bending strain were reproduced well.

Hierarchical modular structure enhances the robustness of self-organized criticality in neural networks

International Nuclear Information System (INIS)

Wang Shengjun; Zhou Changsong

2012-01-01

One of the most prominent architecture properties of neural networks in the brain is the hierarchical modular structure. How does the structure property constrain or improve brain function? It is thought that operating near criticality can be beneficial for brain function. Here, we find that networks with modular structure can extend the parameter region of coupling strength over which critical states are reached compared to non-modular networks. Moreover, we find that one aspect of network function—dynamical range—is highest for the same parameter region. Thus, hierarchical modularity enhances robustness of criticality as well as function. However, too much modularity constrains function by preventing the neural networks from reaching critical states, because the modular structure limits the spreading of avalanches. Our results suggest that the brain may take advantage of the hierarchical modular structure to attain criticality and enhanced function. (paper)

Magnetic field dependence of the critical superconducting current induced by the proximity effect in silicon

International Nuclear Information System (INIS)

Nishino, T.; Kawabe, U.; Yamada, E.

1986-01-01

The magnetic field dependence of the critical superconducting current induced by the proximity effect in heavily-boron-doped Si is studied experimentally. It is found that the critical current flowing through the p-type-Si-coupled junction decreases with increasing applied magnetic field. The critical current can be expressed as the product of three factors: the current induced by de Gennes's proximity effect, the exponential decrease due to pair breaking by the magnetic field, and the usual diffraction-pattern-like dependence on the magnetic field due to the Josephson effect. The second factor depends on the carrier concentration in the semiconductor. The local critical current shows a rapid decrease at the edge of the electrodes

Angular and magnetic field dependences of critical current in irradiated YBaCuO single crystals

International Nuclear Information System (INIS)

Petrusenko, Yu.

2010-01-01

The investigation of mechanisms responsible for the current-carrying capability of irradiated high-temperature superconductors (HTSC) was realized. For the purpose, experiments were made to investigate the effect of point defects generated by high-energy electron irradiation on the critical temperature and the critical current in high-Tc superconducting single crystals YBa 2 Cu 3 O 7-x . The transport current density measured in HTSC single crystals YBa 2 Cu 3 O 7-x by the dc-method was found to exceed 80000 A/cm 2 . The experiments have demonstrated a more than 30-fold increase in the critical current density in single crystals irradiated with 2.5 MeV electrons to a dose of 3·10 18 el/cm 2 . Detailed studies were made into the anisotropy of critical current and the dependence of critical current on the external magnetic field strength in irradiated single crystals. A high efficiency of point defects as centers of magnetic vortex pinning in HTSC single crystals was first demonstrated.

Implementation and evaluation of critical thinking strategies to enhance critical thinking skills in Middle Eastern nurses.

Science.gov (United States)

Simpson, Elaine; Courtney, Mary

2008-12-01

The purpose of this study was to develop, implement and evaluate critical thinking strategies to enhance critical thinking skills in Middle Eastern nurses. Critical thinking strategies such as questioning, debate, role play and small group activity were developed and used in a professional development programme, which was trialled on a sample of Middle Eastern nurses (n = 20), to promote critical thinking skills, encourage problem solving, development of clinical judgment making and care prioritization in order to improve patient care and outcomes. Classroom learning was transformed from memorization to interaction and active participation. The intervention programme was successful in developing critical thinking skills in both the nurse educators and student nurses in this programme. This programme successfully integrated critical thinking strategies into a Middle Eastern nursing curriculum. Recommendations are as follows: (1) utilize evidence-based practice and stem questions to encourage the formulation of critical thinking questions; (2) support the needs of nurse educators for them to effectively implement teaching strategies to foster critical thinking skills; and (3) adopt creative approaches to (i) transform students into interactive participants and (ii) open students' minds and stimulate higher-level thinking and problem-solving abilities.

The Use of Argument Mapping to Enhance Critical Thinking Skills in Business Education

Science.gov (United States)

Kunsch, David W.; Schnarr, Karin; van Tyle, Russell

2014-01-01

Complex business problems require enhanced critical thinking skills. In a dedicated, in-person critical thinking class, argument mapping techniques were used in conjunction with business and nonbusiness case studies to build the critical thinking skills of a group of master of business administration students. Results demonstrated that the…

Influence of anisotropy and pinning centers on critical current properties in Bi-2212 superconductors

International Nuclear Information System (INIS)

Haraguchi, T.; Takayama, S.; Kiuchi, M.; Otabe, E.S.; Matsushita, T.; Yasuda, T.; Okayasu, S.; Uchida, S.; Shimoyama, J.; Kishio, K.

2006-01-01

The critical current density in Bi-2212 superconductors with various anisotropies irradiated by heavy ions was investigated in the medium temperature region to understand the effects of defect size and the anisotropy of the superconductor. It was found that the critical current density and the irreversibility field were larger for the specimen with larger defect and/or with smaller anisotropy. Introduction of stronger pinning centers and the optimization of the doping condition to improve the dimensionality are desired for further improvement of the critical current properties

Interlaboratory comparison on high-temperature superconductor critical-current measurements

International Nuclear Information System (INIS)

Wiejaczka, J.A.; Goodrich, L.F.

1997-01-01

An extensive interlaboratory comparison was conducted on high temperature superconductor (HTS) critical-current measurements. This study was part of an international cooperative effort through the Versailles Project on Advanced Materials and Standards (VAMAS). The study involved six US laboratories that are recognized leaders in the field of HTS. This paper includes the complete results from this comparison of critical-current measurements on Ag-sheathed Bi 2 Sr 2 Ca 2 Cu 3 O 10-x (2223) tapes. The effects of sample characteristics, specimen mounting, measurement technique, and specimen damage were studied. The future development of a standard HTS measurement method is also discussed. Most of the evolution of this emerging technology has occurred in improvement of the performance of the conductors. The successful completion of this interlaboratory comparison is an important milestone in the evolution of HTS technology and marks a level of maturity that the technology has reached

Critical current measurements of high Tc superconductors in a scanning low temperature cryostat

International Nuclear Information System (INIS)

Telschow, K.L.; O'Brien, T.K.

1991-01-01

Maintaining uniformity of properties over long distances is one of the fabrication problems encountered with the new high T c superconductors. Uniform properties are crucial in long tapes or wires with high critical current since local nonuniformities can limit the current carrying capacity of the whole piece. Transport critical currents in high T c superconductors are conventionally measured with the contact 4-point probe DC current-voltage technique. This technique requires contact with the sample and and spatially averages over the region between the two voltage contacts. Two techniques have been used to infer the critical state model. The first uses the net magnetization of a suitably shaped sample in an external magnetic field. The second combines a DC magnetic field with AC induced currents to infer spatial flux profiles. The AC magnetization technique offers an advantage in that it is noncontacting; however, it also averages the measurement over a large area and requires that the sample be shaped and positioned such that it exhibits zero demagnetizing factor. This paper describes a measurement technique and a scanning cryostat assembly that are capable of determining local critical current in a tape or wire with high resolution and without any direct sample electrical contact. A small compensated coil was used to induce AC currents in slab-shaped samples. The coil was situated near the surface on one side of the slab. With this method, the AC probe can be used as a noncontacting dissipation probe, replacing the voltage probe in the 4-point contact method, when an externally driven transport current is used, or by itself as a local critical state generator and dissipation detector. The results are shown to be meaningful even when the internal magnetic field is not uniform due to shape demagnetizing effects. 10 refs., 5 figs

Rationing critical care medicine: recent studies and current trends.

Science.gov (United States)

Ward, Nicholas S

2005-12-01

This paper reviews the literature on the rationing of critical care resources. Although much has been written about the concept of rationing, there have been few scientific studies as to its prevalence. A recent meta-analysis reviewed all previously published studies on rationing access to intensive care units but little is known about practices within the intensive care unit. Much literature in the past few years has focused on the growing use of critical care resources and projections for the future. Several authors suggest there may be a crisis in financial or personnel resources if some rationing does not take place. Other papers have argued that the methods of rationing critical care previously proposed, such as limiting the care of dying patients or using cost-effectiveness analysis to determine care, may not be effective or viewed as ethical by some. Finally, several recent papers review how critical care is practiced and allocated in India and Asian countries that already practice open rationing in their health care systems. There is currently no published evidence that overt rationing is taking place in critical care medicine. There is growing evidence that in the future, the need for critical care may outstrip financial resources unless some form of rationing takes place. It is also clear from the literature that choosing how to ration critical care will be a difficult task.

Magnetic field oscillations of the critical current in long ballistic graphene Josephson junctions

Science.gov (United States)

Rakyta, Péter; Kormányos, Andor; Cserti, József

2016-06-01

We study the Josephson current in long ballistic superconductor-monolayer graphene-superconductor junctions. As a first step, we have developed an efficient computational approach to calculate the Josephson current in tight-binding systems. This approach can be particularly useful in the long-junction limit, which has hitherto attracted less theoretical interest but has recently become experimentally relevant. We use this computational approach to study the dependence of the critical current on the junction geometry, doping level, and an applied perpendicular magnetic field B . In zero magnetic field we find a good qualitative agreement with the recent experiment of M. Ben Shalom et al. [Nat. Phys. 12, 318 (2016), 10.1038/nphys3592] for the length dependence of the critical current. For highly doped samples our numerical calculations show a broad agreement with the results of the quasiclassical formalism. In this case the critical current exhibits Fraunhofer-like oscillations as a function of B . However, for lower doping levels, where the cyclotron orbit becomes comparable to the characteristic geometrical length scales of the system, deviations from the results of the quasiclassical formalism appear. We argue that due to the exceptional tunability and long mean free path of graphene systems a new regime can be explored where geometrical and dynamical effects are equally important to understand the magnetic field dependence of the critical current.

Plasma-enhanced chemical vapor deposition for YBCO film fabrication of superconducting fault-current limiter

Energy Technology Data Exchange (ETDEWEB)

Jun, Byung Hyuk; Kim, Chan Joong

2006-05-15

Since the high-temperature superconductor of oxide type was founded, many researches and efforts have been performed for finding its application field. The YBCO superconducting film fabricated on economic metal substrate with uniform critical current density is considered as superconducting fault-current limiter (SFCL). There are physical and chemical processes to fabricate superconductor film, and it is understood that the chemical methods are more economic to deposit large area. Among them, chemical vapor deposition (CVD) is a promising deposition method in obtaining film uniformity. To solve the problems due to the high deposition temperature of thermal CVD, plasma-enhanced chemical vapor deposition (PECVD) is suggested. This report describes the principle and fabrication trend of SFCL, example of YBCO film deposition by PECVD method, and principle of plasma deposition.

Upper critical fields and critical current densities of Fe-based superconductors as compared to those of other technical superconductors

Energy Technology Data Exchange (ETDEWEB)

Pallecchi, I., E-mail: ilaria.pallecchi@spin.cnr.it [CNR-SPIN, Corso Perrone 24, 16152 Genova (Italy); Tropeano, M. [Columbus Superconductors S.p.A, Via delle Terre Rosse 30, 16133 Genova (Italy); Lamura, G. [CNR-SPIN, Corso Perrone 24, 16152 Genova (Italy); Pani, M. [Dipartimento di Chimica e Chimica Industriale, Universita di Genova, Via Dodecaneso 31, 16146 Genova (Italy); Palombo, M. [Columbus Superconductors S.p.A, Via delle Terre Rosse 30, 16133 Genova (Italy); Dipartimento di Chimica e Chimica Industriale, Universita di Genova, Via Dodecaneso 31, 16146 Genova (Italy); Dipartimento di Fisica, Universita di Genova, Via Dodecaneso 33, 16146 Genova (Italy); Palenzona, A. [Dipartimento di Chimica e Chimica Industriale, Universita di Genova, Via Dodecaneso 31, 16146 Genova (Italy); Putti, M. [CNR-SPIN, Corso Perrone 24, 16152 Genova (Italy); Dipartimento di Fisica, Universita di Genova, Via Dodecaneso 33, 16146 Genova (Italy)

2012-11-20

Three years since the discovery by the Hosono's group of Fe-based superconductors, an enormous number of compounds, belonging to several different families have been discovered and fundamental properties have been deeply investigated in order to clarify the interplay between magnetisms and superconductivity in these compounds. Indeed, the actual potential of these compounds for practical applications remains still unclear. Fe-based superconductors are midway between high temperature superconductors (HTSCs) and MgB{sub 2}. In Fe-based superconductors the critical current is rather independent of the field, similarly to HTSCs, as a consequence of the exceptionally high upper critical field and strong pinning associated with nm-scale local modulations of the order parameter. They exhibit low anisotropy of the critical current with respect to the crystalline directions, as in the case of MgB{sub 2}, which allows current flow along the c-axis. However, Fe-based superconductor polycrystalline materials currently available still exhibit electromagnetic granularity, like the HTSCs, which suppresses superconducting current flow over long length. Whether the nature of such granularity is extrinsic, as due to spurious phases or cracks between grains or intrinsic, as related to misalignment of adjacent grains, is under debate. These aspects will be reviewed in the light of the recent literature.

Study of the inhomogeneity of critical current under in-situ tensile stress for YBCO tape

Science.gov (United States)

Zhu, Y. P.; Chen, W.; Zhang, H. Y.; Liu, L. Y.; Pan, X. F.; Yang, X. S.; Zhao, Y.

2018-07-01

A Hall sensor system was used to measure the local critical current of YBCO tape with high spatial resolution under in-situ tensile stress. The hot spot generation and minimum quench energy of YBCO tape, which depended on the local critical current, was calculated through the thermoelectric coupling model. With the increase in tensile stress, the cracks which have different dimensions and critical current degradation arose more frequently and lowered the thermal stability of the YBCO tape.

Effect of stress on the critical current of NbTi multifilamentary composite wire

International Nuclear Information System (INIS)

Ekin, J.W.; Fickett, F.R.; Clark, A.F.

1977-01-01

Superconducting composites within large-scale magnets can be subjected to high stresses. These stresses arise from several sources, chief among them being the winding tension and prestressing during construction of the magnet, the thermomechanical forces incurred during thermal cycling to cryogenic temperatures, and especially in large-scale systems, the magnetomechanical forces generated when the magnet is energized. Typically, data on the critical-current characteristics of superconducting composites are obtained on wires that are in an unstressed state. Very little is known, however, about how the critical current behaves in wires experiencing stresses of the type described above. To measure these effects, short sample critical current tests were made under conditions simultaneously simulating the mechanical and magnetic environments of high-field superconducting magnets. The program was initiated both to form a basis for the fundamental understanding of stress effects on superconductor stability and to provide engineering data for optimizing design and construction of high-field magnets. The preliminary results indicate that NbTi multifilamentary superconducting composite wires are not characterized by a single critical current vs. field curve, but rather by a family of curves, each corresponding to a different operating stress level

Critical current density in railgrun accelerators with composite electrodes

International Nuclear Information System (INIS)

Stankevich, S.V.; Shvetsov, G.A.

1995-01-01

The present paper is intended to study the possibilities of increasing the critical current density in railgun accelerators using composite electrodes of various structure. Before proceeding to the analysis this way, it should be noted that the requirements for materials selected for the rails go beyond the values of the current density. In real practice account should be taken of the technological problems concerned with the production of the electrodes, as well as of those concerned with the railgun performance, including the multishot life

Magnetic microscopy for characterization of local critical current in iron-sheathed MgB2 wires

International Nuclear Information System (INIS)

Higashikawa, K.; Yamamoto, A.; Kiss, T.; Ye, S.; Matsumoto, A.; Kumakura, H.

2014-01-01

Highlights: • We developed a characterization method of local critical current in MgB 2 wires. • Local homogeneity was visualized by the scanning Hall-probe microscopy (SHPM). • Local critical current value was quantified with the aid of the finite element method (FEM). • MgB 2 wire still has inhomogeneous distribution in local critical current. • Higher potential than that estimated by the four-probe transport method was suggested. - Abstract: We have developed a characterization method of local critical current in iron-sheathed MgB 2 wires. Local homogeneity was visualized by the scanning Hall-probe microscopy (SHPM). The value of local critical current was quantified with the aid of the finite element method (FEM) considering the ferromagnetic properties of the iron sheath. The results suggested that MgB 2 wires fabricated by internal Mg diffusion processes still have large longitudinal inhomogeneity and much higher potential than that estimated by the four-probe transport method. This will be very important information for making a correct strategy for further development of MgB 2 wires

Preparation and characterization of high-Tc superconducting thin films with high critical current densities

International Nuclear Information System (INIS)

Vase, P.

1991-08-01

The project was carried out in relation to possible cable and electronics applications of high-T c materials. Laser ablation was used as the deposition technique because of its stoichiometry conservation. Films were made in the YBa 2 Cu 3 O 7 compound due to its relatively simple stoichiometry compared to other High-T c compounds. Much attention was paid to the critical current density. A very high critical current density was reached. By using texture analysis by X-ray diffraction, it was found that films with high critical current densities were epitaxial, while films with low critical current densities contained several crystalline orientations. Four techniques for patterning the films were used - photo lithography and wet etch, laser ablation lithography, laser writing and electron beam lithography and ion milling. Sub-micron patterning has been demonstrated without degradation of the superconducting properties. The achieved patterning resolution is sufficient for preparation of many superconducting components. (AB)

Magnetic field dependence of the critical current density in YBa2Cu3Ox ceramics

International Nuclear Information System (INIS)

Zhukov, A.A.; Moshchalkov, V.V.; Komarkov, D.A.; Shabatin, V.P.; Gordeev, S.N.; Shelomov, D.V.

1989-01-01

Three magnetic field ranges corresponding to different critical current density j c behavior have been found out. They correlate with grain magnetization changes. The inverse critical current density is shown to depend linearly on the sample cross-section due to the magnetic field induced by the flowing current

Sample-length dependence of the critical current of slightly and significantly bent-damaged Bi2223 superconducting composite tape

International Nuclear Information System (INIS)

Ochiai, S; Fujimoto, M; Okuda, H; Oh, S S; Ha, D W

2007-01-01

The local critical current along a sample length is different from position to position in a long sample, especially when the sample is damaged by externally applied strain. In the present work, we attempted to reveal the relation of the distribution of the local critical current to overall critical current and the sample-length dependence of critical current for slightly and significantly damaged Bi2223 composite tape samples. In the experiment, 48 cm long Bi2223 composite tape samples, composed of 48 local elements with a length of 1 cm and 8 parts with a length 6 cm, were bent by 0.37 and 1.0% to cause slight and significant damage, respectively. The V-I curve, critical current (1 μV cm -1 criterion) and n value were measured for the overall sample as well as for the local elements and parts. It was found that the critical current distributions of the 1 cm elements at 0.37 and 1.0% bending strains are described by the three-parameter- and bimodal Weibull distribution functions, respectively. The critical current of a long sample at both bending strains could be described well by substituting the distributed critical current and n value of the short elements into the series circuit model for voltage generation. Also the measured relation of average critical current to sample length could be reproduced well in the computer by a Monte Carlo simulation method. It was shown that the critical current and n value decrease with increasing sample length at both bending strains. The extent of the decrease in critical current with sample length is dependent on the criterion of the critical current; the critical current decreases only slightly under the 1 μV cm -1 criterion which is not damage-sensitive, while it decreases greatly with increasing sample length under damage-sensitive criteria such as the 1 μV one

Magnetization and critical currents of NbTi wires with fine filaments

International Nuclear Information System (INIS)

Ghosh, A.K.; Sampson, W.B.

1985-01-01

In high energy accelerators such as the SSC, the magnetization of the superconductor is an important component in determining the harmonic fields at injection (approx.0.3T). In an effort to reduce these residual fields, interest has focused on NbTi conductors with fine filaments which are expected to have a reduced magnetization as dictated by the critical state model. With this in view, the magnetization and critical currents were measured at 4.3K for a set of NbTi wires with filament diameters, d, ranging from 1.0 to 5.0 microns. The data show that, although the magnetization scales linearly with d, it does not do so with the product J/sub c/d for d less than 3 μm. However, at these d values, the critical transport current density, J/sub c/ of NbTi was observed to decrease rapidly as a function of d. The origin of this J/sub c/ degradation and its effect on the scaling of magnetization within the framework of the critical state model is explored. We also examine the question of the observed asymmetry of the hysteretic magnetization

Relationship between critical current properties and microstructure in cylindrical RE123 melt-solidified bulks

International Nuclear Information System (INIS)

Nakashima, T.; Shimoyama, J.; Honzumi, M.; Tazaki, Y.; Horii, S.; Kishio, K.

2005-01-01

We report the synthesis of cylindrical melt-solidified bulks in REBa 2 Cu 3 O y (RE = Sm, Gd, Dy, Ho, Y and Er), and their critical current properties and microstructures of the a- and the c-growth regions. It was found from the microstructure analysis that the volume fractions of RE211 particles in the c-growth region were always lower than those in the a-growth region. Moreover, those in the c-growth region were increased with distance from the seed crystal. Interestingly, the second peak effects in J c -B curves were prominently enhanced for the c-growth region. J c values at zero field for the c-growth region through the appropriate oxygen post-annealing reached approximately 95 kA cm -2 for RE = Ho, Dy and Y

Critical thinking instruction and technology enhanced learning from the student perspective: A mixed methods research study.

Science.gov (United States)

Swart, Ruth

2017-03-01

Critical thinking is acclaimed as a valuable asset for graduates from higher education programs. Technology has advanced in quantity and quality; recognized as a requirement of 21st century learners. A mixed methods research study was undertaken, examining undergraduate nursing student engagement with critical thinking instruction, platformed on two technology-enhanced learning environments: a classroom response system face-to-face in-class and an online discussion forum out-of-class. The Community of Inquiry framed the study capturing constructivist collaborative inquiry to support learning, and facilitate critical thinking capability. Inclusion of quantitative and qualitative data sources aimed to gather a comprehensive understanding of students' development of critical thinking and engagement with technology-enhanced learning. The findings from the students' perspectives were positive toward the inclusion of technology-enhanced learning, and use in supporting their development of critical thinking. Students considered the use of two forms of technology beneficial in meeting different needs and preferences, offering varied means to actively participate in learning. They valued critical thinking instruction being intentionally aligned with subject-specific content facilitating understanding, application, and relevance of course material. While the findings are limited to student participants, the instructional strategies and technology-enhanced learning identified as beneficial can inform course design for the development of critical thinking. Copyright © 2017 Elsevier Ltd. All rights reserved.

Space-charge-limited currents for cathodes with electric field enhanced geometry

Energy Technology Data Exchange (ETDEWEB)

Lai, Dingguo, E-mail: laidingguo@nint.ac.cn; Qiu, Mengtong; Xu, Qifu [State Key Laboratory of Intense Pulsed Radiation Simulation and Effect, Northwest Institute of Nuclear Technology, Xi' an 701124 (China); Huang, Zhongliang [Department of Engineering Physics, Tsinghua University, Beijing 100084 (China)

2016-08-15

This paper presents the approximate analytic solutions of current density for annulus and circle cathodes. The current densities of annulus and circle cathodes are derived approximately from first principles, which are in agreement with simulation results. The large scaling laws can predict current densities of high current vacuum diodes including annulus and circle cathodes in practical applications. In order to discuss the relationship between current density and electric field on cathode surface, the existing analytical solutions of currents for concentric cylinder and sphere diodes are fitted from existing solutions relating with electric field enhancement factors. It is found that the space-charge-limited current density for the cathode with electric-field enhanced geometry can be written in a general form of J = g(β{sub E}){sup 2}J{sub 0}, where J{sub 0} is the classical (1D) Child-Langmuir current density, β{sub E} is the electric field enhancement factor, and g is the geometrical correction factor depending on the cathode geometry.

Altering critical depinning current via domain wall pile-up in magnetic nanowires

International Nuclear Information System (INIS)

Geng, Liwei D.; Jin, Yongmei M.

2015-01-01

An important role of domain wall pile-up in current-driven domain wall depinning in magnetic nanowires is revealed using micromagnetic simulations. It is found that the critical current for domain wall depinning can be substantially reduced and conveniently tuned by controlling domain wall number in the pile-up at pinning site, in analogy to dislocation pile-up responsible for Hall–Petch effect in mechanical strength. Domain wall pinning and depinning at an s-shape bend is considered, and the effects of curvature and current crowding in magnetic circuit on domain wall behaviors are discussed. - Highlights: • Advance fundamental knowledge of current-driven domain wall phenomena. • Provide a novel approach to drastically reduce the critical depinning current. • Solve an outstanding problem of effective control of domain wall pinning/depinning. • Report appealing new findings of magnetic domain wall pile-up mechanism. • Overcome the limitations of materials properties for domain wall-based devices

Micromagnetic modeling of critical current oscillations in magnetic Josephson junctions

NARCIS (Netherlands)

golovchanskiy, I.A.; Bol'ginov, V.V.; Stolyarov, V.S.; Abramov, N.N.; Ben Hamida, A.; Emelyanova, O.V.; Stolyarov, B.S.; Kupriyanov, M..Y.; Golubov, Alexandre Avraamovitch; Ryazanov, V.V.

2016-01-01

In this work we propose and explore an effective numerical approach for investigation of critical current dependence on applied magnetic field for magnetic Josephson junctions with in-plane magnetization orientation. This approach is based on micromagnetic simulation of the magnetization reversal

Criticality safety enhancements for SCALE 6.2 and beyond

International Nuclear Information System (INIS)

Rearden, Bradley T.; Bekar, Kursat B.; Celik, Cihangir; Clarno, Kevin T.; Dunn, Michael E.; Hart, Shane W.; Ibrahim, Ahmad M.; Johnson, Seth R.; Langley, Brandon R.; Lefebvre, Jordan P.; Lefebvre, Robert A.; Marshall, William J.; Mertyurek, Ugur; Mueller, Don; Peplow, Douglas E.; Perfetti, Christopher M.; Petrie Jr, Lester M.; Thompson, Adam B.; Wiarda, Dorothea; Wieselquist, William A.; Williams, Mark L.

2015-01-01

SCALE is a widely used suite of tools for nuclear systems modeling and simulation that provides comprehensive, verified and validated, user-friendly capabilities for criticality safety, reactor physics, radiation shielding, and sensitivity and uncertainty analysis. Since 1980, regulators, industry, and research institutions around the world have relied on SCALE for nuclear safety analysis and design. SCALE 6.2 provides several new capabilities and significant improvements in many existing features for criticality safety analysis. Enhancements are realized for nuclear data; multigroup resonance self-shielding; continuous-energy Monte Carlo analysis for sensitivity/uncertainty analysis, radiation shielding, and depletion; and graphical user interfaces. An overview of these capabilities is provided in this paper, and additional details are provided in several companion papers.

Pulsed transport critical currents of Bi2212 tapes in pulsed magnetic fields

Energy Technology Data Exchange (ETDEWEB)

Rogacki, K [Institute of Low Temperature and Structure Research, Polish Academy of Sciences, Wroclaw (Poland); Gilewski, A; Klamut, J [International Laboratory of High Magnetic Fields and Low Temperatures, Polish Academy of Sciences, Wroclaw (Poland); Newson, M; Jones, H [Clarendon Laboratory, University of Oxford, Oxford (United Kingdom); Glowacki, B A [IRC in Superconductivity and Department of Materials Science, University of Cambridge, Cambridge (United Kingdom)

2002-07-01

If high-T{sub C} superconductors are ever to be used in high-field applications, it is vital that the critical surfaces can be mapped under high-field conditions. However, the latest superconductors have high currents even at fields over 20 T, making accurate measurements very difficult due to the thermal and mechanical problems. In this paper, we compare measurements on BSCCO-2212 tape using a number of different methods, particularly an innovative pulsed transport current and pulsed field mode. We show how the analysis of the voltage signal from BSCCO-2212 tape in pulsed conditions may be used to extract the critical current in quasi-stationary conditions. The effect of a metallic substrate on the results is also briefly discussed. (author)

Critical current density and wire fabrication of high-TC superconductors

International Nuclear Information System (INIS)

Schlabach, T.D.; Jin, S.; Sherwood, R.C.; Tiefel, T.H.

1989-01-01

In this paper, some of the recent investigations of wire fabrication techniques and critical current behavior in high T c superconductors will be reviewed. In spite of the tremendous interest and research effort, the progress toward major applications of the bulk high-temperature superconductors has been impeded by, among other thins, the low critical currents and their severe deterioration in weak magnetic fields. Significant advances, however, have been made in understanding the causes of the problem as well as in improving the current-carrying capacity through proper microstructural control such as the melt-textured-growth in Y-Ba-Cu-O. The low density of effective flux-pinning sites in bulk Y-Ba-Cu-O limits J c at 77K in high magnetic fields to about 10 4 A/cm 2 even in the absence of weak links. Magnetization measurements on Bi-Sr-Ca-Cu-O and Tl-Ba-Ca-Cu-O at 77K by various researchers indicate even weaker flux pinning capabilities in these materials than in Y-Ba-Cu-O. The challenge in the future is to obtain suitable flux-pinning defects by choosing the right processing and chemistry changes

The relationship between critical current and microstructure of internal tin wire

International Nuclear Information System (INIS)

Dietderich, D.R.; Hassenzahl, W.V.; Morris, J.W. Jr.

1986-01-01

Prior work on internal tin wire has shown that an increase in critical current results when the Nb 3 Sn reaction temperatures (650-730 0 C) are preceded by low temperature diffusion heat treatments that distribute the tin. These heat treatments produce a more uniform tin distribution through the niobium filament array before substantial Nb 3 Sn formation has occurred. Heat treatments as long as 19 days have been proposed as the optimal heat treatment for the conductor. However, it is possible to substantially reduce the low temperature heat treatment time while retaining the same high critical current. The success of shortened heat treatments may be interpreted on the basis of the Cu-Sn reaction, diffusion kinetics and the Nb 3 Sn growth kinetics

'Leak Current' correction for critical current measurement of no-insulation HTS coil

Energy Technology Data Exchange (ETDEWEB)

Song, Jung Bin [Laboratoire National des Champs Magnétiques Intenses, CNRS, Grenoble (France); Hahn, Seung Yong [Dept. of Electrical and Computer Engineering, Seoul National University, Seoul (Korea, Republic of)

2017-06-15

Discrepancy between a power supply current and an actual “spiral” coil current makes the conventional 4-probe measurement of a critical current (I{sub c}) of a no-insulation (NI) high temperature superconductor (HTS) coil inaccurate and time-consuming. This paper presents a fast and accurate approach for I{sub c} measurement of NI HTS coils. With an NI HTS coil energized at a constant ramping rate, a complete analytic expression for the spiral coil current was obtained from a first-order partial differential equation that derived from an equivalent circuit model of the NI coil. From the analytic solution, both spiral coil current and radial leak current can be obtained simultaneously, which enables fast and accurate measurement of the NI coil I{sub c}. To verify the proposed approach, an NI double-pancake (DP) coil, wound with GdBCO tapes of 6 mm × 0.1 mm, was constructed and its Ic was repeatedly measured with various ramping rates in a bath of liquid nitrogen at 77 K. The measured results agreed well with the calculated ones, which validates the proposed approach to measure I{sub c} of an NI HTS coil.

Enhancement in transport critical current density of ex situ PIT Ag/(Ba, K)Fe2As2 tapes achieved by applying a combined process of flat rolling and uniaxial pressing

Science.gov (United States)

Togano, Kazumasa; Gao, Zhaoshun; Matsumoto, Akiyoshi; Kumakura, Hiroaki

2013-11-01

We report that the transport critical current density Jc of ex situ powder-in-tube (PIT) processed (Ba, K)Fe2As2 (Ba-122) tapes can be significantly enhanced by applying uniaxial cold pressing at the final stage of deformation. The tapes were prepared by packing high quality precursor powder into a Ag tube, cycles of rolling and intermediate annealing, and pressing followed by the final heat treatment for sintering. The Jc values in applied magnetic fields were increased by almost one order of magnitude compared to the tapes processed without pressing, exceeding 104 A cm-2 at 4.2 K. We achieved the highest Jc (at 4.2 K and 10 T) of 2.1×104 A cm-2 among PIT-processed Fe-based wires and tapes reported so far. The Jc-H curves measured at higher temperatures maintain small field dependence up to around 20 K, suggesting that these tapes are promising for applications at higher temperatures as well as at liquid helium temperature. The microstructure investigations reveal that there are two possible causes of the large Jc enhancement by pressing: one is densification and the other is the change of crack structure. Optimization of processing parameters such as the reduction ratio of rolling and pressing is expected to yield further Jc enhancement.

Characterization of the critical current and physical properties of superconducting epitaxial NbTiN sub-micron structures

Energy Technology Data Exchange (ETDEWEB)

Klimov, A., E-mail: aklimov@ite.waw.pl [Institute of Electron Technology, Al. Lotników 32/46, 02-668 Warsaw (Poland); Słysz, W.; Guziewicz, M. [Institute of Electron Technology, Al. Lotników 32/46, 02-668 Warsaw (Poland); Kolkovsky, V.; Zaytseva, I.; Malinowski, A. [Institute of Physics Polish Academy of Science, Al. Lotników 32/46, 02-668 Warsaw (Poland)

2017-05-15

Highlights: • This manuscript presents investigation of the critical current dependence of Nb(Ti)N nanostructured superconducting single photon detectors (SNSPD) in function of temperature and applied magnetic field. • Presented results are complimentary and compared with the same data received for submicron-wide single bridge Nb(Ti)N structures. • Our data demonstrate significant influence of local constrictions on physical properties of our SNSPD detectors. - Abstract: Measurements of critical current in NbTiN as a function of applied magnetic field and temperature are reported for two samples: 700-nm-wide bridge and 100-nm-wide meander. In 700-nm-wide NbTiN bridge we pinpointed the limiting factors for the critical current density to be current-driven vortex de-pinning at low temperatures and thermally activated flux flow closer to the transition temperature. In 100-nm-wide NbTiN meander we found phase slips activation, accompanied by hotspots formation at all measured temperatures. These two types of structures demonstrate different dependence of the critical current on the applied magnetic field. Although our NbTiN meander structures has high de-pairing critical current densities ∼10{sup 7} A/cm{sup 2} at low temperatures, the real critical currents are smaller due to the presence of the local constrictions.

Critical dimension and pattern size enhancement using pre-strained lithography

Energy Technology Data Exchange (ETDEWEB)

Hong, Jian-Wei [Department of Power Mechanical Engineering, National Tsing Hua University, 101, Section 2, Kuang Fu Road, Hsin Chu 30013, Taiwan (China); Yang, Chung-Yuan [Institute of NanoEngineering and MicroSystems, National Tsing Hua University, 101, Section 2, Kuang Fu Road, Hsin Chu 30013, Taiwan (China); Lo, Cheng-Yao, E-mail: chengyao@mx.nthu.edu.tw [Department of Power Mechanical Engineering, National Tsing Hua University, 101, Section 2, Kuang Fu Road, Hsin Chu 30013, Taiwan (China); Institute of NanoEngineering and MicroSystems, National Tsing Hua University, 101, Section 2, Kuang Fu Road, Hsin Chu 30013, Taiwan (China)

2014-10-13

This paper proposes a non-wavelength-shortening-related critical dimension and pattern size reduction solution for the integrated circuit industry that entails generating strain on the substrate prior to lithography. Pattern size reduction of up to 49% was achieved regardless of shape, location, and size on the xy plane, and complete theoretical calculations and process steps are described in this paper. This technique can be applied to enhance pattern resolution by employing materials and process parameters already in use and, thus, to enhance the capability of outdated lithography facilities, enabling them to particularly support the manufacturing of flexible electronic devices with polymer substrates.

Stock markets and criticality in the current economic crisis

Science.gov (United States)

da Silva, Roberto; Zembrzuski, Marcelo; Correa, Fabio C.; Lamb, Luis C.

2010-12-01

We show that the current economic crisis has led the market to exhibit a non-critical behavior. We do so by analyzing the quantitative parameters of time series from the main assets of the Brazilian Stock Market BOVESPA. By monitoring global persistence we show a deviation of power law behavior during the crisis in a strong analogy with spin systems (from where this concept was originally conceived). Such behavior is corroborated by an emergent heavy tail of absolute return distribution and also by the magnitude autocorrelation exponent. Comparisons with universal exponents obtained in the international stock markets are also performed. This suggests how a thorough analysis of suitable exponents can bring a possible way of forecasting market crises characterized by non-criticality.

Effect of sheath material on critical current characteristics of MgB2 at high temperatures

International Nuclear Information System (INIS)

Kiuchi, M.; Yamauchi, K.; Kurokawa, T.; Otabe, E.S.; Matsushita, T.; Okada, M.; Tanaka, K.; Kumakura, H.; Kitaguchi, H.

2004-01-01

Critical current density and irreversibility field were measured at various temperatures and magnetic fields for MgB 2 PIT tape specimens with different sheaths materials. The experimental results were compared with theoretical estimations using the flux creep-flow model. It is found that the hardness of sheath material indirectly affects the pinning property only through the packing density of MgB 2 . It is considered that the critical current density is mainly determined by a low value of distributed local critical current density determined by grain connectivity. On the other hand, the irreversibility field which is approximately the same among the three tapes is mainly determined by the average pinning strength

Critical current densities in thick yttrium-barium cuprate (1-2-3) films

International Nuclear Information System (INIS)

Ryvkina, G.G.; Gorlanov, S.F.; Vedernikov, G.E.; Telegin, A.B.; Ryabin, V.A.; Khodos, M.Ya.

1993-01-01

The study of critical current densities j c of oxide superconductors and their thick films is a very important practical task because the value of j c is one of the main criteria for their utilization in modern cryoelectronics. For most devices based on the Josephson effect, the value of j c ∼ 10 2 - 10 3 A/cm 2 is acceptable, which is easily attainable for polycrystalline thick films obtained by stenciling. The study of the current-transport phenomenon involves a number of difficulties, especially for direct current, because both the sample itself and the lead-in contacts are resistance-heated during the measurements, which, in turn, results in lower values of the j c . Measurements with pulsed currents allow one to lower the power that is applied to the sample; the heat that is released in the sample is reduced, in comparison to measurements with direct current, by a factor of the pulsed-current duty cycle. In addition, measurements with direct current detects only the appearance of resistance; it provides no information on the rest of the transition from the normal to the superconductive state, i.e., on the so-called 'tail' of the transition. In this work, the authors studied critical current densities of thick HTSC yttrium-barium cuprate films of the 1-2-3 composition using pulsed current

Analysis of critical current-bend strain relationships in composite Nb3Sn superconducting wires

International Nuclear Information System (INIS)

Luhman, T.; Welch, D.O.

1979-01-01

In order to be used successfully in fusion magnets, Nb 3 Sn conductors must meet several mechanical strain criteria, including tolerance to bending strains encountered during magnet construction. Since Nb 3 Sn is extremely brittle much information has been generated regarding the sensitivity of these conductros to tensile strain. A recent comparison of critical current-bend and tensile test data indicates that the strain required to initiate compound cracking during bending is significantly less than the strain required to do so by tensile of critical current on bending strains in monofilamentary Nb 3 Sn wires is calculated and compared with experimental data. The calculation takes into account a shift in the composite's neutral axis which occurs during bending. The analysis correctly predicts the observed depdndence of the critical current on bending strains

Magnetic response and critical current properties of mesoscopic-size YBCO superconducting samples

International Nuclear Information System (INIS)

Lisboa-Filho, P N; Deimling, C V; Ortiz, W A

2010-01-01

In this contribution superconducting specimens of YBa 2 Cu 3 O 7-δ were synthesized by a modified polymeric precursor method, yielding a ceramic powder with particles of mesoscopic-size. Samples of this powder were then pressed into pellets and sintered under different conditions. The critical current density was analyzed by isothermal AC-susceptibility measurements as a function of the excitation field, as well as with isothermal DC-magnetization runs at different values of the applied field. Relevant features of the magnetic response could be associated to the microstructure of the specimens and, in particular, to the superconducting intra- and intergranular critical current properties.

Magnetic response and critical current properties of mesoscopic-size YBCO superconducting samples

Energy Technology Data Exchange (ETDEWEB)

Lisboa-Filho, P N [UNESP - Universidade Estadual Paulista, Grupo de Materiais Avancados, Departamento de Fisica, Bauru (Brazil); Deimling, C V; Ortiz, W A, E-mail: plisboa@fc.unesp.b [Grupo de Supercondutividade e Magnetismo, Departamento de Fisica, Universidade Federal de Sao Carlos, Sao Carlos (Brazil)

2010-01-15

In this contribution superconducting specimens of YBa{sub 2}Cu{sub 3}O{sub 7-{delta}} were synthesized by a modified polymeric precursor method, yielding a ceramic powder with particles of mesoscopic-size. Samples of this powder were then pressed into pellets and sintered under different conditions. The critical current density was analyzed by isothermal AC-susceptibility measurements as a function of the excitation field, as well as with isothermal DC-magnetization runs at different values of the applied field. Relevant features of the magnetic response could be associated to the microstructure of the specimens and, in particular, to the superconducting intra- and intergranular critical current properties.

Enhancement of superconducting critical current by injection of quasiparticles in superconductor semiconductor devices

DEFF Research Database (Denmark)

Kutchinsky, Jonatan; Taboryski, Rafael Jozef; Sørensen, C. B.

2000-01-01

We report new measurements on 3-terminal superconductor semiconductor injection devices, demonstrating enhancement of the supercurrent by injection from a superconducting injector electrode. Two other electrodes were used as detectors. Applying a small voltage to the injector, reduced the maximum...

Structural and critical current properties in Al-doped MgB2

International Nuclear Information System (INIS)

Zheng, D.N.; Xiang, J.Y.; Lang, P.L.; Li, J.Q.; Che, G.C.; Zhao, Z.W.; Wen, H.H.; Tian, H.Y.; Ni, Y.M.; Zhao, Z.X.

2004-01-01

A series of Al-doped Mg 1-x Al x B 2 samples have been fabricated and systematic study on structure and superconducting properties have been carried out for the samples. In addition to a structural transition observed by XRD, TEM micrographs showed the existence of a superstructure of double c-axis lattice constant along the direction perpendicular to the boron honeycomb sheet. In order to investigate the effect of Al doping on flux pinning and critical current properties in MgB 2 , measurements on the superconducting transition temperature T c , irreversible field B irr and critical current density J c were performed too, for the samples with the doping levels lower than 0.15 in particular. These experimental observations were discussed in terms of Al doping induced changes in carrier concentration

Structural and critical current properties in Al-doped MgB 2

Science.gov (United States)

Zheng, D. N.; Xiang, J. Y.; Lang, P. L.; Li, J. Q.; Che, G. C.; Zhao, Z. W.; Wen, H. H.; Tian, H. Y.; Ni, Y. M.; Zhao, Z. X.

2004-08-01

A series of Al-doped Mg 1- xAl xB 2 samples have been fabricated and systematic study on structure and superconducting properties have been carried out for the samples. In addition to a structural transition observed by XRD, TEM micrographs showed the existence of a superstructure of double c-axis lattice constant along the direction perpendicular to the boron honeycomb sheet. In order to investigate the effect of Al doping on flux pinning and critical current properties in MgB 2, measurements on the superconducting transition temperature Tc, irreversible field Birr and critical current density Jc were performed too, for the samples with the doping levels lower than 0.15 in particular. These experimental observations were discussed in terms of Al doping induced changes in carrier concentration.

Current algebra of WZNW models at and away from criticality

International Nuclear Information System (INIS)

Abdalla, E.; Forger, M.

1992-01-01

In this paper, the authors derive the current algebra of principal chiral models with a Wess-Zumino term. At the critical coupling where the model becomes conformally invariant (Wess-Zumino-Novikov-Witten theory), this algebra reduces to two commuting Kac-Moody algebras, while in the limit where the coupling constant is taken to zero (ordinary chiral model), we recover the current algebra of that model. In this way, the latter is explicitly realized as a deformation of the former, with the coupling constant as the deformation parameter

Low field critical currents and ac losses of thin film niobium--tin superconductors

International Nuclear Information System (INIS)

Howard, R.E.

1977-01-01

The results of a study of the low field critical current and ac loss properties of niobium-tin thin films and layered composites fabricated by electron-beam coevaporation are presented. Particular emphasis is placed upon determining the suitability of this material for use as a conductor in a superconducting power transmission line. Chapter I contains a summary of this work and its major results together with an introduction to the scientific and engineering concepts associated with a superconducting power transmission line. Chapter II is a discussion of the physics of current transport and the associated loss mechanisms in a type-II superconductor. Chapter III gives the details of the electron-beam coevaporation technique developed to fabricate the samples for this study. Also discussed in this chapter are the effects of the evaporation conditions on the growth morphology of the niobium-tin films. Chapter IV presents the details of the experimental techniques developed to measure the ac loss and critical current in these samples as a function of temperature. Chapter V shows the dependence of the critical current of these films and composites on temperature, magnetic field, and on the number of artificially introduced pinning centers in the layered composites. Experimental results are also presented concerning the stability of these conductors against flux jumps. Chapter VI is a discussion of the ac losses in these samples. Detailed comparisons are made between the measured loss and the predictions of the critical state model

Using Quantitative Literacy to Enhance Critical Thinking Skills in Undergraduate Nursing Students.

Science.gov (United States)

Asknes, Edna

2017-04-01

Critical thinking and quantitative literacy (QL) are similarly grounded: both focus on analyzing and evaluating evidence, identifying implications and consequences, drawing inferences, and communicating information. This teaching strategy was based on those commonalities and was designed so that undergraduate nursing students would enhance their critical thinking skills as they used their QL skills. QL skills are most effective when taught, learned, and used to solve significant, pertinent problems. Using the principles of learner-centered, team-based learning, QL was integrated into the curriculum of the Maternal-Newborn Nursing course at an urban community college with a diverse student population. Students were engaged and demonstrated enhanced and ongoing development of their critical thinking and problem-solving skills. They also reported a better understanding of data interpretation and use. The positive outcome of this project revealed further opportunities for incorporating QL into nursing curricula and highlighted the need for research on the use of QL in nursing education. [J Nurs Educ. 2017;56(4):240-242.]. Copyright 2017, SLACK Incorporated.

Using the 5E Learning Cycle with Metacognitive Technique to Enhance Students’ Mathematical Critical Thinking Skills

Directory of Open Access Journals (Sweden)

Runisah Runisah

2017-02-01

Full Text Available This study aims to describe enhancement and achievement of mathematical critical thinking skills of students who received the 5E Learning Cycle with Metacognitive technique, the 5E Learning Cycle, and conventional learning. This study use experimental method with pretest-posttest control group design. Population are junior high school students in Indramayu city, Indonesia. Sample are three classes of eighth grade students from high level school and three classes from medium level school. The study reveal that in terms of overall, mathematical critical thinking skills enhancement and achievement of students who received the 5E Learning Cycle with Metacognitive technique is better than students who received the 5E Learning Cycle and conventional learning. Mathematical critical thinking skills of students who received the 5E Learning Cycle is better than students who received conventional learning. There is no interaction effect between learning model and school level toward enhancement and achievement of students’ mathematical critical thinking skills.

The influence of strain introduced by differential thermal contraction on the critical current of Nb3Sn supercontractors

International Nuclear Information System (INIS)

Pasztor, G.; Jakob, B.

1992-01-01

The NET Team initiated in 1988 a development program for a high current cable-in-conduit superconductor planned for fusion magnets. The basic strand chosen for the cable was a Nb 3 Sn wire of TWCA made by the MJR method. The electrical testing of the stand and sub-cables was carried out at several European Laboratories including PSI (Paul Scherrer Institute). The inter-laboratory comparison of the results revealed large differences in the measured critical currents of the strands. Obviously, each laboratory performed the measurement of critical current in its own way, and as a result some discrepancies in the measured values were inevitable. No standard technique of measuring critical current has been developed for Nb 3 Sn wires. The main source of difficulty arises from the strain sensitivity of Nb 3 Sn. It has been shown that the sample holder material and geometry as well as the bonding method of the specimen to its holder have important effects on the critical current measurements. It was found recently that the reaction mandrel material significantly influences the current-carrying capacity of Nb 3 Sn wires. The aim of this paper is to improve current understanding of the effect of sample configuration on critical current in Nb 3 Sn multifilamentary wires. The present study confirms the important role of reaction mandrel material on critical current. Based on comparative critical current measurements of straight and coil samples, an attempt is made to find the sample configuration which eliminates the strain induced in the specimen

Cathodic current enhancement via manganese and oxygen related reactions in marine biofilms

Science.gov (United States)

Strom, Matthew James

Corrosion is a threat that has economic, and environmental impacts worldwide. Many types of corrosive attack are the subject of ongoing research. One of these areas of research is microbiologically influenced corrosion, which is the enhancement and/or initiation of corrosion events caused by microorganisms. It is well known that colonies of microorganisms can enhance cathodic currents through biofilm formation. The aim of the present work was to elucidate the role of manganese in enhancing cathodic currents in the presence of biofilms. Repeated polarizations conducted in Delaware Bay waters, on biofilm coated Cr identified potentially sustainable reduction reactions. The reduction of MnO2 and the enhancement of the oxygen reduction reaction (ORR) were proven to be factors that influence cathodic current enhancement. The removal of ambient oxygen during polarizations resulted in a shutdown of cathodic current enhancement. These field data led to an exploration of the synergistic relationship between MnO2 and the ORR. Laboratory studies of the catalysis of peroxide disproportionation by MnO2 were monitored using a hanging mercury drop electrode. Experiments were run at an ambient sweater pH of 8 and pH 9, which simulated the near-surface conditions typical of cathodes immersed in seawater. Rapid reoxidation at the more basic pH was shown to allow manganese to behave as a persistent catalyst under the typical electrochemical surface conditions of a cathode. As a result a mechanism for ORR enhancement by manganese was proposed as a unique mechanism for cathodic current enhancement in biofilms. A separate field study of Delaware biofilms on stainless steel coupled to a sacrificial Al anode was carried out to identify the ORR enhancement mechanism and sustainable redox reactions at the cathode. Chemical treatments of glutaraldehyde and formaldoxime were applied to cathodes with biofilms to distinguish between enzymatic and MnO2 related ORR enhancement. The results ruled

Use of a web site to enhance criticality safety training

International Nuclear Information System (INIS)

Huang, Song T.; Morman, James A.

2003-01-01

Establishment of the NCSP (Nuclear Criticality Safety Program) website represents one attempt by the NCS (Nuclear Criticality Safety) community to meet the need to enhance communication and disseminate NCS information to a wider audience. With the aging work force in this important technical field, there is a common recognition of the need to capture the corporate knowledge of these people and provide an easily accessible, web-based training opportunity to those people just entering the field of criticality safety. A multimedia-based site can provide a wide range of possibilities for criticality safety training. Training modules could range from simple text-based material, similar to the NCSET (Nuclear Criticality Safety Engineer Training) modules, to interactive web-based training classes, to video lecture series. For example, the Los Alamos National Laboratory video series of interviews with pioneers of criticality safety could easily be incorporated into training modules. Obviously, the development of such a program depends largely upon the need and participation of experts who share the same vision and enthusiasm of training the next generation of criticality safety engineers. The NCSP website is just one example of the potential benefits that web-based training can offer. You are encouraged to browse the NCSP website at http://ncsp.llnl.gov. We solicit your ideas in the training of future NCS engineers and welcome your participation with us in developing future multimedia training modules. (author)

Scanning Hall-probe microscopy system for two-dimensional imaging of critical current density in RE-123 coated conductors

International Nuclear Information System (INIS)

Higashikawa, K.; Inoue, M.; Kawaguchi, T.; Shiohara, K.; Imamura, K.; Kiss, T.; Iijima, Y.; Kakimoto, K.; Saitoh, T.; Izumi, T.

2011-01-01

Nondestructive characterization method of in-plane distribution of critical current density for coated conductors. Current distribution in a coated conductor compared with that from theoretical analysis. Relationship between local critical current density and local magnetic field. We have developed a characterization method for two-dimensional imaging of critical current density in coated conductors (CCs) based on scanning Hall-probe microscopy (SHPM). The distributions of the magnetic field around a sample were measured for several different conditions of external magnetic fields, and then were converted to those of the sheet current density which flowed to shield the external magnetic field or to trap the penetrated magnetic field. As a result, it was found that the amplitude of the sheet current density corresponded to that of critical current density almost in all the area of the sample except for the region where current direction changed. This indicates that we could obtain an in-plane distribution of the critical current density with a spatial resolution of around 100 μm in non-destructive manner by this method. We believe that this measurement will be a multifunctional and comprehensive characterization method for coated conductors.

Kiloampere, Variable-Temperature, Critical-Current Measurements of High-Field Superconductors.

Science.gov (United States)

Goodrich, L F; Cheggour, N; Stauffer, T C; Filla, B J; Lu, X F

2013-01-01

We review variable-temperature, transport critical-current (I c) measurements made on commercial superconductors over a range of critical currents from less than 0.1 A to about 1 kA. We have developed and used a number of systems to make these measurements over the last 15 years. Two exemplary variable-temperature systems with coil sample geometries will be described: a probe that is only variable-temperature and a probe that is variable-temperature and variable-strain. The most significant challenge for these measurements is temperature stability, since large amounts of heat can be generated by the flow of high current through the resistive sample fixture. Therefore, a significant portion of this review is focused on the reduction of temperature errors to less than ±0.05 K in such measurements. A key feature of our system is a pre-regulator that converts a flow of liquid helium to gas and heats the gas to a temperature close to the target sample temperature. The pre-regulator is not in close proximity to the sample and it is controlled independently of the sample temperature. This allows us to independently control the total cooling power, and thereby fine tune the sample cooling power at any sample temperature. The same general temperature-control philosophy is used in all of our variable-temperature systems, but the addition of another variable, such as strain, forces compromises in design and results in some differences in operation and protocol. These aspects are analyzed to assess the extent to which the protocols for our systems might be generalized to other systems at other laboratories. Our approach to variable-temperature measurements is also placed in the general context of measurement-system design, and the perceived advantages and disadvantages of design choices are presented. To verify the accuracy of the variable-temperature measurements, we compared critical-current values obtained on a specimen immersed in liquid helium ("liquid" or I c liq) at 5

Enhanced performance of high current discharges in JET produced by ICRF heating during the current rise

International Nuclear Information System (INIS)

Bures, M.; Bhatnagar, V.; Christiansen, J.P.

1989-01-01

The performance of high current discharges can be improved by applying central ICRF heating before or shortly after the onset of sawtooth activity in the plasma current rise phase. Long sawtooth-free periods have been obtained which result in a transiently-enhanced discharge performance. High T c (0) = 9-10.5 keV with peaked profile T e (0)/ e > = 3-4 were obtained giving values of N e (0)T e (0) up to 6 x 10 20 (keV m -3 ). Improvements in T i (0) and neutron production are observed. A best value of n Dd (0)T i (0)τ E = 1.65 x 10 20 (m -3 keV s) was achieved. Local transport simulation shows that the electron and ion thermal diffusivities do not differ substantially in the two cases of current-rise (CR) and flat-top (FT) heating, the performance of the central plasma region being enhanced, in the case of current-rise, entirely by the elimination of the sawtooth instability. The maximum D-D reaction rate is enhanced by a factor of 2 compared to the flat-top value. An appreciable part of the reaction rate is attributed to 2nd harmonic deuterium (2ω CD ) heating. In all current-rise discharges radiation amounts to 25-50% of total power and Ζ eff remains roughly constant. (author)

Critical current fluctuation in a microwave-driven Josephson junction

International Nuclear Information System (INIS)

Dong Ning; Sun Guozhu; Wang Yiwen; Cao Junyu; Yu Yang; Chen Jian; Kang Lin; Xu Weiwei; Han Siyuan; Wu Peiheng

2007-01-01

Josephson junction devices are good candidates for quantum computation. A large energy splitting was observed in the spectroscopy of a superconducting Josephson junction. The presence of the critical current fluctuation near the energy splitting indicated coupling between the junction and a two-level system. Furthermore, we find that this fluctuation is microwave dependent. It only appears at certain microwave frequency. This relation suggested that the decoherence of qubits is influenced by the necessary computing operations

Calculation of the Critical Current Reduction in a Brittle Round Multifilamentary Wire due to External Forces

NARCIS (Netherlands)

ten Haken, Bernard; Godeke, A.; ten Kate, Herman H.J.

1994-01-01

A simple model is presented that can describe the electro-mechanical state of a multifilamentary wire. An elastic cylinder model is used to derive the strain state analytically. Axial and transverse forces came a position dependent critical current density in the wire. The integral critical current

Thermodynamic parameters of single- or multi-band superconductors derived from self-field critical currents

Energy Technology Data Exchange (ETDEWEB)

Talantsev, Evgueni [Robinson Research Institute, Victoria University of Wellington, Lower Hutt (New Zealand); Crump, Wayne P.; Tallon, Jeffery L. [Robinson Research Institute, Victoria University of Wellington, Lower Hutt (New Zealand); MacDiarmid Institute for Advanced Materials and Nanotechnology, Lower Hutt (New Zealand)

2017-12-15

Key questions for any superconductor include: what is its maximum dissipation-free electrical current (its 'critical current') and can this be used to extract fundamental thermodynamic parameters? Present models focus on depinning of magnetic vortices and implicate materials engineering to maximise pinning performance. But recently we showed that the self-field critical current for thin films is a universal property, independent of microstructure, controlled only by the penetration depth. Here, using an extended BCS-like model, we calculate the penetration depth from the temperature dependence of the superconducting energy gap thus allowing us to fit self-field critical current data. In this way we extract from the T-dependent gap a set of key thermodynamic parameters, the ground-state penetration depth, energy gap and jump in electronic specific heat. Our fits to 79 available data sets, from zinc nanowires to compressed sulphur hydride with critical temperatures of 0.65 to 203 K, respectively, are excellent and the extracted parameters agree well with reported bulk values. Samples include thin films, wires or nanowires of single- or multi-band s-wave and d-wave superconductors of either type I or type II. For multiband or multiphase samples we accurately recover individual band contributions and phase fractions. (copyright 2017 by WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Critical current degradation in superconducting niobium-titanium alloys in external magnetic fields under loading

International Nuclear Information System (INIS)

Bojko, V.S.; Lazareva, M.B.; Starodubov, Ya.D.; Chernyj, O.V.; Gorbatenko, V.M.

1992-01-01

The effect of external magnetic fields on the stress at which the critical current starts to degrade (the degradation threshold σ 0 e ) under mechanical loads in superconducting Nb-Ti alloys is studied and a possible mechanism of realization of the effect observed is proposed.It is assumed that additional stresses on the transformation dislocation from the external magnetic fields are beneficial for the growth of martensite inclusions whose superconducting parameters (critical current density j k and critical temperature T k ) are lower then those in the initial material.The degradation threshold is studied experimentally in external magnetic fields H up to 7 T.The linear dependence σ 0 e (H) is observed.It is shown that external magnetic fields play an important role in the critical current degradation at the starting stages of deformation.This fact supports the assumption that the degradation of superconducting parameters under loading are due to the phenomenon of superelasticity,i.e. a reversible load-induced change in the martensite inclusions sizes rather than the reversible mechanical twinning.The results obtained are thought to be important to estimating superconducting solenoid stability in a wide range of magnetic fields

Study of critical current density from ac susceptibility measurements in (La1-xYx)2Ba2CaCu5O2 superconductors

International Nuclear Information System (INIS)

Nayak, P.K.; Ravi, S. . sravi@iitg.ernet.in

2008-01-01

We have prepared a series of compounds (La 1-x Y x ) 2 Ba 2 CaCu 5 O 2 for x = 0 to 0.5 by adding a CaCuO 2 layer to the parent compound La 2 Ba 2 Cu 4 O 2 and by doping Y in place of La. These materials are also prepared by adding 5 wt% of Ag to enhance the intergranular coupling and critical current density. X-ray diffraction measurements show that all the samples are essentially in single phase form and the patterns could be refined using P4/mmm space group in tetragonal cell. The typical lattice parameters are found to be a = b 3.856 A, c = 11.576 A for x = 0.5 sample. Temperature variations of dc electrical resistivity measured on the above samples show that they exhibit superconductivity with T c ranging from 60 to 75 K. Temperature and ac field amplitude variation of ac susceptibility have been measured on the above samples. The field variation of ac susceptibility data has been analyzed by using Bean critical state model. Using both temperature and field variations of ac susceptibility data, the material dependent parameters, such as critical current density as a function of temperature and effective volume fraction grains have been estimated. The Ag doped samples show relatively large critical current density compared to pure samples due to improved intergranular coupling. (author)

Stress effect on the critical current of Ti-Nb-Zr-Ta multifilamentary superconductors

International Nuclear Information System (INIS)

Monju, Yoshiyuki; Tatara, Isamu

1978-01-01

The tensile behaviour at R.T., 77K, 4.2K and the degradation of the critical current with stress have been measured on multifilamentary Ti-Nb-Zr-Ta alloy superconductors. The assembly of the stress effect apparatus is as follows; At the center of the 60KOe superconducting solenoid coil, sample wire is hold around an FRP spool and the wire ends are gripped to the load train. Current is supplied through helium vapourcooled flexible leads up to 2000 A. It was clear that a definite degradation of the critical current with stress was not observed up to the stress equal to one third of the fracture stress at 4.2K. This stress value should be defined the maximum allowable stress of alloy superconductors examined from stress effects. (author)

Microstructure and critical current of superconducting YBa/sub 2/Cu/sub 3/Osub(7-x)

Energy Technology Data Exchange (ETDEWEB)

Camps, R A; Evetts, J E; Glowacki, B A; Newcomb, S B; Somekh, R E; Stobbs, W M

1987-09-17

The authors present the main results of a detailed electron microscopical study of sintered YBa/sub 2/Cu/sub 3/0sub(7-x), and discuss their relevance to observed critical current and its modification by increased silicon impurity levels. In the light of these results, the prospects are assessed for controlling microstructure development so as to optimize the critical current for technological application.

Evidence from EXAFS for Different Ta/Ti Site Occupancy in High Critical Current Density Nb3Sn Superconductor Wires.

Science.gov (United States)

Heald, Steve M; Tarantini, Chiara; Lee, Peter J; Brown, Michael D; Sung, ZuHawn; Ghosh, Arup K; Larbalestier, David C

2018-03-19

To meet critical current density, J c , targets for the Future Circular Collider (FCC), the planned replacement for the Large Hadron Collider (LHC), the high field performance of Nb 3 Sn must be improved, but champion J c values have remained static for the last 10 years. Making the A15 phase stoichiometric and enhancing the upper critical field H c2 by Ti or Ta dopants are the standard strategies for enhancing high field performance but detailed recent studies show that even the best modern wires have broad composition ranges. To assess whether further improvement might be possible, we employed Extended X-ray Absorption Fine Structure (EXAFS) to determine the lattice site location of dopants in modern high-performance Nb 3 Sn strands with J c values amongst the best so far achieved. Although Ti and Ta primarily occupy the Nb sites in the A15 structure, we also find significant Ta occupancy on the Sn site. These findings indicate that the best performing Ti-doped stand is strongly sub-stoichiometric in Sn and that antisite disorder likely explains its high average H c2 behavior. These new results suggest an important role for dopant and antisite disorder in minimizing superconducting property distributions and maximizing high field J c properties.

Grain size dependence of the critical current density in YBa2Cu3Ox superconductors

International Nuclear Information System (INIS)

Kuwabara, M.; Shimooka, H.

1989-01-01

The grain size dependence of the critical current density in bulk single-phase YBa 2 Cu 3 O x ceramics was investigated. The grain size of the materials was changed to range approximately from 1.0 to 25 μm by changing the conditions of power processing and sintering, associated with an increase in the sintered density of the materials with increasing grain size. The critical current density has been found to exhibit a significant grain size dependence, changing from 880 A/cm 2 to a value of 100 A/cm 2 with a small increase in the average grain size from 1.2 to 2.0 μm. This seems to provide information about the nature of the weak link between superconducting grains which might govern the critical current density of the materials

The nature of transport critical current hysteresis in HTSC: magnetic fields and high pressures. [Y-Ba-Cu-O

Energy Technology Data Exchange (ETDEWEB)

Svistunov, V M; Yachenko, A.I. d' ; Tarenkov, V Yu [Donetsk Physico-Technical Inst., Ukrainian SSR (USSR)

1991-12-01

It was found that pressure has a strong influence on the critical current hysteresis loop of ceramics at H {proportional to} 10 kOe. The phenomenon is attributed to the critical current hysteresis of separate Josephson contacts and is due to the Abrikosov vortex density gradient within granules. The gradient defines both the sign and the value of the pinning current, whereas the sign of Meissner reversible surfaces current component is determined by the external field H direction. As a result the critical current of Josephson contacts defined by the total surface value depends on the magnetic prehistory of a sample. (orig.).

Nb/sub 3/Sn critical-current measurements using tubular fiberglass-epoxy mandrels

International Nuclear Information System (INIS)

Goodrich, L.F.; Bray, S.L.; Stauffer, T.C.

1989-01-01

A systematic study of the effect of sample mounting techniques on the superconducting critical-current measurement was made in conjunction with the VAMAS (Versailles Agreement on Advanced Materials and Standards) interlaboratory comparison (round robin) measurements. A seemingly small change in mandrel geometry can result in a 40% change in the measured critical current of a Nb/sub 3/Sn sample at 12 T. This is a result of a change in the conductor pre-strain at 4 K caused by variation in thermal contraction between thick- and thin-walled fiberglass-epoxy composite (G-10) tubes. An approximate measure of the variations in thermal contraction (from room to liquid nitrogen temperature) indicate a 0.2% greater contraction for the thick-walled tube. This difference, combined with strain sensitivity measurements, is consistent with the observed decrease in critical current. Previous publications on thermal contraction of G-10 have addressed the plate geometry, but not the tube geometry. The contraction of a G-10 plate is highly anisotropic. The radial contraction of a tube is different than the contraction of a plate, however, because the circumferential fiberglass is put into hoop compression by the epoxy, and the resulting contraction is a competition between the two structural components. This appears to be the source of the variation in thermal contraction with tube wall thickness

Optimizing critical heat flux enhancement through nano-particle-based surface modifications

International Nuclear Information System (INIS)

Truong, B.; Hu, L. W.; Buongiorno, J.

2008-01-01

Colloidal dispersions of nano-particles, also known as nano-fluids, have shown to yield significant Critical Heat Flux (CHF) enhancement. The CHF enhancement mechanism in nano-fluids is due to the buildup of a porous layer of nano-particles upon boiling. Unlike microporous coatings that had been studied extensively, nano-particles have the advantages of forming a thin layer on the substrate with surface roughness ranges from the sub-micron to several microns. By tuning the chemical properties it is possible to coat the nano-particles in colloidal dispersions onto the desired surface, as has been demonstrated in engineering thin film industry. Building on recent work conducted at MIT, this paper illustrates the maximum CHF enhancement that can be achieved based on existing correlations. Optimization of the CHF enhancement by incorporation of key factors, such as the surface wettability and roughness, will also be discussed. (authors)

Reduction of Gas Bubbles and Improved Critical Current Density in Bi-2212 Round Wire by Swaging

CERN Document Server

Jiang, J; Huang, Y; Hong, S; Parrell, J; Scheuerlein, C; Di Michiel, M; Ghosh, A; Trociewitz, U; Hellstrom, E; Larbalestier, D

2013-01-01

Bi-2212 round wire is made by the powder-in-tube technique. An unavoidable property of powder-in-tube conductors is that there is about 30% void space in the as-drawn wire. We have recently shown that the gas present in the as-drawn Bi-2212 wire agglomerates into large bubbles and that they are presently the most deleterious current limiting mechanism. By densifying short 2212 wires before reaction through cold isostatic pressing (CIPping), the void space was almost removed and the gas bubble density was reduced significantly, resulting in a doubled engineering critical current density (JE) of 810 A/mm2 at 5 T, 4.2 K. Here we report on densifying Bi-2212 wire by swaging, which increased JE (4.2 K, 5 T) from 486 A/mm2 for as-drawn wire to 808 A/mm2 for swaged wire. This result further confirms that enhancing the filament packing density is of great importance for making major JE improvement in this round-wire magnet conductor.

Enhanced performance on high current discharges in JET produced by ICRF heating during the current rise

International Nuclear Information System (INIS)

Bures, M.; Bhatnagar, V.; Cotrell, G.; Corti, S.; Christiansen, J.P.; Hellsten, T.; Jacquinot, J.; Lallia, P.; Lomas, P.; O'Rourke, J.; Taroni, A.; Tibone, F.; Start, D.F.H.

1989-01-01

The performance of high current discharges can be increased by applying central ICRF heating before or shortly after the onset of sawtooth activity in the plasma current rise phase. Sawtooth-free periods have been obtained resulting in the enhanced discharge performance. High T e (0) 9 - 10.5 keV with peaked profiles T e (0)/ e > = 3 - 4 were obtained giving values of n e (0)T e (0) up to 6x10 20 (keV m -3 ). Improvements in T i (0) and neutron production are observed. A 60 % enhancement in D-D reaction rate from 2nd harmonic deuterium (2ω CD ) heating appears to be present. In all current rise (CR) discharges radiation amounts to 25-50 % of total power. (author) 4 refs., 6 figs

Enhanced upper critical fields in binary Nb-Ti alloys

International Nuclear Information System (INIS)

Hariharan, Y.; Sastry, V.S.; Janawadkar, M.P.; Radhakrishnan, T.S.

1986-01-01

The authors report the enhancement of H/sub c2/ in quenched and suitably heat treated binary Nb-65 at % Ti alloys. The inherent metastability of the bcc β phase and its instability towards athermal ω are used to realise high values of normal state resistivity ε/sub n/. The consequences of this on the upper critical field have been experimentally determined by the measurement of dH/sub c2//dT at T/sub c/ and of T/sub c/. These together with our similar measurements on Nb-83 at % Ti alloy to which at 1 at % N was added (to retain it in the β phase) are analysed in terms of the existing theories for upper critical fields. It is shown that a peak in H/sub c2/(o) occurs at 17 - 18 T when ε/sub n/ has a value of approximately 100 μΩcm

Using a kinesthetic learning strategy to engage nursing student thinking, enhance retention, and improve critical thinking.

Science.gov (United States)

Wagner, Elissa A

2014-06-01

This article reports the outcomes of a kinesthetic learning strategy used during a cardiac lecture to engage students and to improve the use of classroom-acquired knowledge in today's challenging clinical settings. Nurse educators are constantly faced with finding new ways to engage students, stimulate critical thinking, and improve clinical application in a rapidly changing and complex health care system. Educators who deviate from the traditional pedagogy of didactic, content-driven teaching to a concept-based, student-centered approach using active and kinesthetic learning activities can enhance engagement and improve clinical problem solving, communication skills, and critical thinking to provide graduates with the tools necessary to be successful. The goals of this learning activity were to decrease the well-known classroom-clinical gap by enhancing engagement, providing deeper understanding of cardiac function and disorders, enhancing critical thinking, and improving clinical application. Copyright 2014, SLACK Incorporated.

Current anti-doping policy: a critical appraisal.

Science.gov (United States)

Kayser, Bengt; Mauron, Alexandre; Miah, Andy

2007-03-29

Current anti-doping in competitive sports is advocated for reasons of fair-play and concern for the athlete's health. With the inception of the World Anti Doping Agency (WADA), anti-doping effort has been considerably intensified. Resources invested in anti-doping are rising steeply and increasingly involve public funding. Most of the effort concerns elite athletes with much less impact on amateur sports and the general public. We review this recent development of increasingly severe anti-doping control measures and find them based on questionable ethical grounds. The ethical foundation of the war on doping consists of largely unsubstantiated assumptions about fairness in sports and the concept of a "level playing field". Moreover, it relies on dubious claims about the protection of an athlete's health and the value of the essentialist view that sports achievements reflect natural capacities. In addition, costly antidoping efforts in elite competitive sports concern only a small fraction of the population. From a public health perspective this is problematic since the high prevalence of uncontrolled, medically unsupervised doping practiced in amateur sports and doping-like behaviour in the general population (substance use for performance enhancement outside sport) exposes greater numbers of people to potential harm. In addition, anti-doping has pushed doping and doping-like behaviour underground, thus fostering dangerous practices such as sharing needles for injection. Finally, we argue that the involvement of the medical profession in doping and anti-doping challenges the principles of non-maleficience and of privacy protection. As such, current anti-doping measures potentially introduce problems of greater impact than are solved, and place physicians working with athletes or in anti-doping settings in an ethically difficult position. In response, we argue on behalf of enhancement practices in sports within a framework of medical supervision. Current anti

Criticality safety evaluation for the Advanced Test Reactor enhanced low enriched uranium fuel elements

Energy Technology Data Exchange (ETDEWEB)

Montierth, Leland M. [Idaho National Lab. (INL), Idaho Falls, ID (United States)

2016-07-19

The Global Threat Reduction Initiative (GTRI) convert program is developing a high uranium density fuel based on a low enriched uranium (LEU) uranium-molybdenum alloy. Testing of prototypic GTRI fuel elements is necessary to demonstrate integrated fuel performance behavior and scale-up of fabrication techniques. GTRI Enhanced LEU Fuel (ELF) elements based on the ATR-Standard Size elements (all plates fueled) are to be fabricated for testing in the Advanced Test Reactor (ATR). While a specific ELF element design will eventually be provided for detailed analyses and in-core testing, this criticality safety evaluation (CSE) is intended to evaluate a hypothetical ELF element design for criticality safety purposes. Existing criticality analyses have analyzed Standard (HEU) ATR elements from which controls have been derived. This CSE documents analysis that determines the reactivity of the hypothetical ELF fuel elements relative to HEU ATR elements and whether the existing HEU ATR element controls bound the ELF element. The initial calculations presented in this CSE analyzed the original ELF design, now referred to as Mod 0.1. In addition, as part of a fuel meat thickness optimization effort for reactor performance, other designs have been evaluated. As of early 2014 the most current conceptual designs are Mk1A and Mk1B, that were previously referred to as conceptual designs Mod 0.10 and Mod 0.11, respectively. Revision 1 evaluates the reactivity of the ATR HEU Mark IV elements for a comparison with the Mark VII elements.

Criticality safety evaluation for the Advanced Test Reactor enhanced low enriched uranium fuel elements

International Nuclear Information System (INIS)

Montierth, Leland M.

2016-01-01

The Global Threat Reduction Initiative (GTRI) convert program is developing a high uranium density fuel based on a low enriched uranium (LEU) uranium-molybdenum alloy. Testing of prototypic GTRI fuel elements is necessary to demonstrate integrated fuel performance behavior and scale-up of fabrication techniques. GTRI Enhanced LEU Fuel (ELF) elements based on the ATR-Standard Size elements (all plates fueled) are to be fabricated for testing in the Advanced Test Reactor (ATR). While a specific ELF element design will eventually be provided for detailed analyses and in-core testing, this criticality safety evaluation (CSE) is intended to evaluate a hypothetical ELF element design for criticality safety purposes. Existing criticality analyses have analyzed Standard (HEU) ATR elements from which controls have been derived. This CSE documents analysis that determines the reactivity of the hypothetical ELF fuel elements relative to HEU ATR elements and whether the existing HEU ATR element controls bound the ELF element. The initial calculations presented in this CSE analyzed the original ELF design, now referred to as Mod 0.1. In addition, as part of a fuel meat thickness optimization effort for reactor performance, other designs have been evaluated. As of early 2014 the most current conceptual designs are Mk1A and Mk1B, that were previously referred to as conceptual designs Mod 0.10 and Mod 0.11, respectively. Revision 1 evaluates the reactivity of the ATR HEU Mark IV elements for a comparison with the Mark VII elements.

Optimization of superconductor--normal-metal--superconductor Josephson junctions for high critical-current density

International Nuclear Information System (INIS)

Golub, A.; Horovitz, B.

1994-01-01

The application of superconducting Bi 2 Sr 2 CaCu 2 O 8 and YBa 2 Cu 3 O 7 wires or tapes to electronic devices requires the optimization of the transport properties in Ohmic contacts between the superconductor and the normal metal in the circuit. This paper presents results of tunneling theory in superconductor--normal-metal--superconductor (SNS) junctions, in both pure and dirty limits. We derive expressions for the critical-current density as a function of the normal-metal resistivity in the dirty limit or of the ratio of Fermi velocities and effective masses in the clean limit. In the latter case the critical current increases when the ratio γ of the Fermi velocity in the superconductor to that of the weak link becomes much less than 1 and it also has a local maximum if γ is close to 1. This local maximum is more pronounced if the ratio of effective masses is large. For temperatures well below the critical temperature of the superconductors the model with abrupt pair potential on the SN interfaces is considered and its applicability near the critical temperature is examined

Effects of sintering conditions on critical current properties and microstructures of MgB2 bulks

International Nuclear Information System (INIS)

Yamamoto, Akiyasu; Shimoyama, Jun-ichi; Ueda, Shinya; Katsura, Yukari; Iwayama, Isao; Horii, Shigeru; Kishio, Kohji

2005-01-01

The effects of heating conditions on critical current properties and microstructures of undoped MgB 2 bulks were systematically studied. Strong correlation was observed between J c and microstructures. The network structure with an excellent inter-grain connectivity of MgB 2 grains contributed to high-J c under low magnetic fields, and small grain size of MgB 2 enhanced the grain boundary flux pinning. Long time heating at low temperatures below the melting point of magnesium was discovered to be most effective for synthesis of MgB 2 bulks having strongly connected MgB 2 network structure with small grains. The sample heated at 550 deg. C for 1200 h recorded a high-J c of 4.02 x 10 5 A cm -2 at 20 K in self-field, while high-temperature and long time heating brought a significant grain growth which resulted in low J c

Tensile Strain Dependence of Critical Current for RHQ-Nb3Al Wires

OpenAIRE

Jin, Xinzhe; Oguro, Hidetoshi; Nakamoto, Tatsushi; Awaji, Satoshi; Ogitsu, Toru; Tsuchiya, Kiyosumi; Yamamoto, Akira; Kikuchi, Akihiro; Takeuchi, Takao

2011-01-01

KEK and NIMS have been jointly developing Nb3Al superconducting wire with a rapid heating and quenching (RHQ) method towards high field accelerator magnets in the Large Hadron Collider (LHC) luminosity upgrade. A15-type superconductors such as Nb3Al and Nb3Sn exhibit strain dependence with respect to their critical currents. Therefore, a thorough understanding of strain behavior is necessary for high field accelerator magnet development, which will be critical for the luminosity upgrade of th...

Transport critical current density in flux creep model

International Nuclear Information System (INIS)

Wang, J.; Taylor, K.N.R.; Russell, G.J.; Yue, Y.

1992-01-01

The magnetic flux creep model has been used to derive the temperature dependence of the critical current density in high temperature superconductors. The generally positive curvature of the J c -T diagram is predicted in terms of two interdependent dimensionless fitting parameters. In this paper, the results are compared with both SIS and SNS junction models of these granular materials, neither of which provides a satisfactory prediction of the experimental data. A hybrid model combining the flux creep and SNS mechanisms is shown to be able to account for the linear regions of the J c -T behavior which are observed in some materials

Contactless estimation of critical current density and its temperature dependence using magnetic measurements

Czech Academy of Sciences Publication Activity Database

Youssef, A.; Baničová, L.; Švindrych, Zdeněk; Janů, Zdeněk

2010-01-01

Roč. 118, č. 5 (2010), s. 1036-1037 ISSN 0587-4246. [Czech and Slovak Conference on Magnetism /14./. Košice, 06.07.2010-09.07.2010] R&D Projects: GA MŠk(CZ) ME10069 Institutional research plan: CEZ:AV0Z10100520 Keywords : superconductivity * critical state * Bean model * critical current density Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.467, year: 2010

Depairing critical current achieved in superconducting thin films with through-thickness arrays of artificial pinning centers

International Nuclear Information System (INIS)

Dinner, Rafael B; Wimbush, Stuart C; MacManus-Driscoll, Judith L; Blamire, Mark G; Robinson, Adam P

2011-01-01

Large area arrays of through-thickness nanoscale pores have been milled into superconducting Nb thin films via a process utilizing anodized aluminum oxide thin film templates. These pores act as artificial flux pinning centers, increasing the superconducting critical current, J c , of the Nb films. By optimizing the process conditions including anodization time, pore size and milling time, J c values approaching and in some cases matching the Ginzburg-Landau depairing current of 30 MA cm -2 at 5 K have been achieved-a J c enhancement over as-deposited films of more than 50 times. In the field dependence of J c , a matching field corresponding to the areal pore density has also been clearly observed. The effect of backfilling the pores with magnetic material has then been investigated. While backfilling with Co has been successfully achieved, the effect of the magnetic material on J c has been found to be largely detrimental compared to voids, although a distinct influence of the magnetic material in producing a hysteretic J c versus applied field behavior has been observed. This behavior has been tested for compatibility with currently proposed models of magnetic pinning and found to be most closely explained by a model describing the magnetic attraction between the flux vortices and the magnetic inclusions.

Contradiction between the results of observations of resistance and critical current quantum oscillations in asymmetric superconducting rings

International Nuclear Information System (INIS)

Gurtovoi, V. L.; Dubonos, S. V.; Karpii, S. V.; Nikulov, A. V.; Tulin, V. A.

2007-01-01

Magnetic field dependences of critical current, resistance, and rectified voltage of asymmetric (half circles of different widths) and symmetrical (half circles of equal widths) aluminum rings close to the super-conducting transition were measured. All these dependences are periodic magnetic field functions with periods corresponding to the flux quantum in the ring. The periodic dependences of critical current measured in opposite directions were found to be close to each other for symmetrical rings and shifted with respect to each other by half the flux quantum in asymmetric rings with ratios between half circle widths of from 1.25 to 2. This shift of the dependences by a quarter of the flux quantum as the ring becomes asymmetric makes critical current anisotropic, which explains the effect of alternating current rectification observed for asymmetric rings. Shifts of the extrema of the periodic dependences of critical current by a quarter of the flux quantum directly contradict the results obtained by measuring asymmetric ring resistance oscillations, whose extrema are, as for symmetrical rings, observed at magnetic fluxes equal to an integer and a half of flux quanta

Reversible oxidation and critical current of YBa2Cu3Ox coated conductors

International Nuclear Information System (INIS)

Claus, H.; Uprety, K.K.; Ma, B.; Paulikas, A.P.; Vlasko-Vlasov, V.K.; Welp, U.; Veal, B.W.; Gray, K.E.

2004-01-01

We were able to vary the oxygen concentration of a YBCO coated-conductor sample from the under-doped to the over-doped regime. This was achieved by secondary oxygenation treatments at temperatures between 250 deg. C and 500 deg. C employing a novel oxygenation scheme. The YBCO-coated conductor was fabricated by the inclined substrate deposition method. Superconducting transition temperature and critical current as function of temperature and magnetic field were determined by a contact-free magnetization technique on a ring sample. It is observed that for temperatures at and below 77 K, the maximum critical current is obtained in the most over-doped state where the transition temperature is significantly depressed

Correlations between critical current density, jc, critical temperature, Tc, and structural quality of Y1B2Cu3O7-x thin superconducting films

International Nuclear Information System (INIS)

Chrzanowski, J.; Xing, W.B.; Atlan, D.

1994-01-01

Correlations between critical current density (j c ) critical temperature (T c ) and the density of edge dislocations and nonuniform strain have been observed in YBCO thin films deposited by pulsed laser ablation on (001) LaAlO 3 single crystals. Distinct maxima in j c as a function of the linewidths of the (00 ell) Bragg reflections and as a function of the mosaic spread have been found in the epitaxial films. These maxima in j c indicate that the magnetic flux lines, in films of structural quality approaching that of single crystals, are insufficiently pinned which results in a decreased critical current density. T c increased monotonically with improving crystalline quality and approached a value characteristic of a pure single crystal. A strong correlation between j c and the density of edge dislocations N D was found. At the maximum of the critical current density the density of edge dislocations was estimated to be N D ∼1-2 x 10 9 /cm 2

Analysis of critical thinking ability in direct current electrical problems solving

Science.gov (United States)

Hartono; Sunarno, Widha; Sarwanto; Arya Nugraha, Dewanta

2017-11-01

This study concern on analyzing the ability of students in critical thinking skills on the subject matter of direct current electricity. Samples were taken using purposive random sampling consisted of 32 students of grade XI, Multimedia 1, SMK Negeri 3 Surakarta in academic year 2016/2017. This study used descriptive quantitative method. The data were collected using tests and interviews regarding the subject matter of direct current electricity. Based on the results, students are getting some difficulties in solving problem in indicator 4. The average of students’ correct answer is 62.8%.

Flux pinning and critical current in layered type-II superconductors in parallel magnetic fields

International Nuclear Information System (INIS)

Prokic, V.; Davidovic, D.; Dobrosavljevic-Grujic, L.

1995-01-01

We have shown, within the Ginzburg-Landau theory, that the interaction between vortices and normal-metal layers in high-T c superconductor--normal-metal superlattices can cause high critical-current densities j c . The interaction is primarily magnetic, except at very low temperatures T, where the core interaction is dominant. For a lattice of vortices commensurate with an array of normal-metal layers in a parallel magnetic field H, strong magnetic pinning is obtained, with a nonmonotonic critical-current dependence on H, and with j c of the order of 10 7 --10 8 A/cm 2

Critical current densities and vortex dynamics in FeTexSe1-x single crystals

International Nuclear Information System (INIS)

Taen, T.; Tsuchiya, Y.; Nakajima, Y.; Tamegai, T.

2010-01-01

The critical current density and the normalized relaxation rate are reported in FeTe 0.59 Se 0.41 single crystal. Critical current density is of order of 10 5 A/cm 2 , which is comparable to that in Co-doped BaFe 2 As 2 . In low temperature and low field region, the vortex dynamics of this system is well defined by the collective creep theory, which is quite similar to Co-doped BaFe 2 As 2 reported before. We also discuss the origin of the anomaly in the field dependence of the relaxation rate.

Enhanced Spin-Orbit Torque via Modulation of Spin Current Absorption

KAUST Repository

Qiu, Xuepeng

2016-11-18

The magnitude of spin-orbit torque (SOT), exerted to a ferromagnet (FM) from an adjacent heavy metal (HM), strongly depends on the amount of spin current absorbed in the FM. We exploit the large spin absorption at the Ru interface to manipulate the SOTs in HM/FM/Ru multilayers. While the FM thickness is smaller than its spin dephasing length of 1.2 nm, the top Ru layer largely boosts the absorption of spin currents into the FM layer and substantially enhances the strength of SOT acting on the FM. Spin-pumping experiments induced by ferromagnetic resonance support our conclusions that the observed increase in the SOT efficiency can be attributed to an enhancement of the spin-current absorption. A theoretical model that considers both reflected and transmitted mixing conductances at the two interfaces of FM is developed to explain the results.

Calibration of Hall sensor array for critical current measurement of YBCO tape with ferromagnetic substrate

International Nuclear Information System (INIS)

Zhu, Yunpeng; Wang, Gang; Liu, Liyuan; Yang, Xinsheng; Zhao, Yong

2015-01-01

Abstract : HAS (Hall sensor array) is a powerful tool to detect the uniformity of HTS (high temperature superconductor) tape through mapping the distribution of remanent or shielding field along the surface of the tape. However, measurement of HTS tape with ferromagnetic parts by HSA is still an issue because the ferromagnetic substrate has influence on the magnetic field around the HTS layer. In this work, a continuous HSA system has been designed to measure the critical current of the YBCO tape with ferromagnetic substrate. The relationship between the remanent field and critical current was calibrated by the finite element method. The result showed that the HSA is an effective method for evaluating the critical current of the HTS tape with ferromagnetic substrate. - Highlight: • A continuous Hall sensor array system has been designed. • The inhomogeneity of YBCO tape with ferromagnetic substrate can be detected by HAS. • Finite element method is an effective method for calibrating the remanent field.

Numerical versus analytical Ic(H) patterns in Josephson junctions with periodically alternating critical current density

International Nuclear Information System (INIS)

Lazarides, N

2004-01-01

An analytical expression for the magnetic-field-dependent critical current I c (H) of Josephson junctions with periodically alternating critical current density J c (x) is derived within the uniform field approximation. Comparison with numerically calculated I c (H) patterns for junctions with identical, thick, periodically arranged defects with the corresponding analytical expression reveals fair agreement for a wide range of parameters, due to increased characteristic length. Based on qualitative arguments, we give the dependence of the new characteristic length on the geometrical parameters of the junction, which is in agreement with self-consistent calculations with the static sine-Gordon equation. The analytical expression captures the observed qualitative features of the I c (H) patterns, while it is practically exact for short junctions or high fields. It also produces the shift of the major peak from the zero-field position of the standard Fraunhofer pattern to another position related to the periodicity of the critical current density in φ-junctions

Calibration of Hall sensor array for critical current measurement of YBCO tape with ferromagnetic substrate

Energy Technology Data Exchange (ETDEWEB)

Zhu, Yunpeng; Wang, Gang; Liu, Liyuan [Key laboratory of Magnetic levitation Technologies and Maglev Trains (Ministry of Education), Superconductor and New Energy R& D Center, Mail Stop 165#, Southwest Jiaotong University, Chengdu, 610031 (China); Yang, Xinsheng, E-mail: xsyang@swjtu.edu.cn [Key laboratory of Magnetic levitation Technologies and Maglev Trains (Ministry of Education), Superconductor and New Energy R& D Center, Mail Stop 165#, Southwest Jiaotong University, Chengdu, 610031 (China); Zhao, Yong [Key laboratory of Magnetic levitation Technologies and Maglev Trains (Ministry of Education), Superconductor and New Energy R& D Center, Mail Stop 165#, Southwest Jiaotong University, Chengdu, 610031 (China); Superconductivity Research Group, School of Materials Science and Engineering, University of New South Wale, Sydney 2052, NSW (Australia)

2015-12-15

Abstract : HAS (Hall sensor array) is a powerful tool to detect the uniformity of HTS (high temperature superconductor) tape through mapping the distribution of remanent or shielding field along the surface of the tape. However, measurement of HTS tape with ferromagnetic parts by HSA is still an issue because the ferromagnetic substrate has influence on the magnetic field around the HTS layer. In this work, a continuous HSA system has been designed to measure the critical current of the YBCO tape with ferromagnetic substrate. The relationship between the remanent field and critical current was calibrated by the finite element method. The result showed that the HSA is an effective method for evaluating the critical current of the HTS tape with ferromagnetic substrate. - Highlight: • A continuous Hall sensor array system has been designed. • The inhomogeneity of YBCO tape with ferromagnetic substrate can be detected by HAS. • Finite element method is an effective method for calibrating the remanent field.

Simulation of transport critical current of Bi2223/Ag tape with ferromagnetic shielding

International Nuclear Information System (INIS)

Gu, C.; Alamgir, A.K.M.; Qu, T.M.; Han, Z.

2008-01-01

Ferromagnetic shielding (FS) was coated onto the surface of the Bi2223/Ag multi-filamentary tape. Transport critical current of the Bi2223/Ag multi-filamentary tape with a FS was systematically studied by numerical simulation. In the help of a finite element analysis (FEA) tool, we are able to understand how the FS alters the flux inside the superconductor region and thus increases and decreases the critical current density locally. The results show the open FS function both positively and negatively to the performance of the tape. An optimization process was proposed, aiming to reach a tradeoff between I c increasing and less usage of the ferromagnetic material. Three important shielding parameters, shielding width, shielding thickness, and shielding material were taken into account

Simulation of transport critical current of Bi2223/Ag tape with ferromagnetic shielding

Energy Technology Data Exchange (ETDEWEB)

Gu, C. [Applied Superconductivity Research Center, Department of Physics, Tsinghua University, Beijing 100084 (China)], E-mail: guchen@tsinghua.edu.cn; Alamgir, A.K.M. [Faculty of Engineering, Yokohama National University, 75-9 Tokiwadai, Hodogaya, ku, Yokohama (Japan); Qu, T.M. [Applied Superconductivity Research Center, Department of Physics, Tsinghua University, Beijing 100084 (China); Key Laboratory for Advanced Materials Processing Technology, Ministry of Education (China); Han, Z. [Applied Superconductivity Research Center, Department of Physics, Tsinghua University, Beijing 100084 (China)

2008-09-15

Ferromagnetic shielding (FS) was coated onto the surface of the Bi2223/Ag multi-filamentary tape. Transport critical current of the Bi2223/Ag multi-filamentary tape with a FS was systematically studied by numerical simulation. In the help of a finite element analysis (FEA) tool, we are able to understand how the FS alters the flux inside the superconductor region and thus increases and decreases the critical current density locally. The results show the open FS function both positively and negatively to the performance of the tape. An optimization process was proposed, aiming to reach a tradeoff between I{sub c} increasing and less usage of the ferromagnetic material. Three important shielding parameters, shielding width, shielding thickness, and shielding material were taken into account.

Critical tunnel currents and dissipation of Quantum-Hall bilayers in the excitonic condensate state

International Nuclear Information System (INIS)

Yoon, Y; Huang, X; Yarar, E; Dietsche, W; Tiemann, L; Schmult, S; Klitzing, K v

2011-01-01

Transport and tunneling is studied in the regime of the excitonic condensate at total filling factor one using the counterflow geometry. At small currents the coupling between the layers is large making the two layers virtually electrically inseparable. Above a critical current the tunneling becomes negligible. An onset of dissipation in the longitudinal transport is observed in the same current range.

Critical currents and flux-pinning properties in PbMo6S8 superconductors

International Nuclear Information System (INIS)

Noto, K.; Hamasaki, K.; Komata, T.; Saito, T.; Watanabe, K.; Yamashita, T.

1986-01-01

We report on recent investigations of the fabrication of PbMo 6 S 8 tapes prepared using an electro-plating and diffusion technique. Measurement of critical currents was carried out in either 16.5 T superconducting magnet, or 20.5 T (HM-3) and 23 T (HM-2) hybrid magnets in High Field Laboratory for Superconducting Materials RIISOM, Tohoku University in Japan. After optimal reaction the critical temperature measured by a resistive method reaches about 14.5 K, and a transition width was less than 0.5 K. Critical current densities are relatively high in a low magnetic field, and reached 1X10 4 A/cm 2 in a 15 T magnetic field at 4.2 K. However, J /SUB c/ 's in a strong magnetic field above 15 T are still insufficient for practical applications. In some of these samples pinning force densities were found to obey a simple scaling law, and in most cases the scaling is not obey. Poor J /SUB c/ -B characteristics in a strong magnetic field may be due to inhomogeneities of this compound

The potential of large critical currents in the high Tc oxides

International Nuclear Information System (INIS)

Deutcher, G.

1993-01-01

The potential for high critical current densities is examined. on a thermodynamical basis, the energy scale for vortex pinning can be derived for instance from a measurement of the width of the critical region. This energy scale is of the order of 0.2 eV in YBCO, which is sufficient for practical applications. Another important parameter is the short coherence length. The inner plane length, of the order of a few lattice spacing, is favorable for pinning by point defects. But the very short outer plane length gives rise to anomalous magnetic behavior, unfavorable for high-field applications at high temperature; this is true in particular in most anisotropic oxides, such as the Bi compounds (author)

Fabrication of Ba-K-Bi-O thick film artefacts with improved critical currents

International Nuclear Information System (INIS)

Moore, J.C.; Salter, C.J.; Jenkins, R.J.; Grovenor, C.R.M.; Jones, H.

1993-01-01

The Ba-K-Bi-O system has a maximum T c of around 30K for a composition of Ba 0.6 K 0.4 BiO 3 . Fabrication of good quality single phase samples is extremely difficult and requires careful control of the fabrication conditions. Successful synthesis procedures for Ba-K-Bi-O powder and melt cast material which allow some control of the potassium content of the product were established by Hinks et al. The process is based on a melt and sinter step in an inert atmosphere which creates oxygen vacancies and allows potassium to enter the lattice. The oxygen vacancies are then filled by a subsequent oxygen anneal to obtain superconductivity. Ba-K-Bi-O is, therefore, metastable and consequently difficult to synthesise. There have been few reports of transport measurements and even fewer reports of transport critical currents for bulk material. It is often accepted that Ba-K-Bi-O has an intrinsically low critical current, and extremely poor critical current densities of 0.05 Acm -2 have been quoted for melt cast material. It has been suggested that the presence of weak links is the cause. However, there has been little research into the relationship between process conditions and superconducting properties for melt processed Ba-K-Bi-O to confirm this. (orig.)

Influence of electron spectrum dielectrizations on critical current of the Josephson medium BaPb1-xBixO3

International Nuclear Information System (INIS)

Vojtenko, A.I.; Gabovich, A.M.; Moiseev, D.P.; Postnikov, V.M.; Shpigel', A.S.

1990-01-01

Temperature dependences of the critical current I c across the symmetrical tunnel Josephson junctions between superconductors with partially-gapped electron spectrum were calculated. Densities J c of the critical current for the bulk Josephson-type samples and current-voltage characteristics of the tunnel-type were measured

Transport critical current density and microstructure in extruded YBa2Cu3O7-x wires processed by zone melting

International Nuclear Information System (INIS)

Shi, D.; Krishnan, H.; Hong, J.M.; Miller, D.; McGinn, P.J.; Chen, W.H.; Xu, M.; Chen, J.G.; Fang, M.M.; Welp, U.; Lanagan, M.T.; Goretta, K.C.; Dusek, J.T.; Picciolo, J.J.; Balachandran, U.

1990-01-01

YBa 2 Cu 3 O 7-x compounds were extruded into long wires with the diameter of 1 mm after sintering. The sintered wires were subsequently zone melted to develop a highly textured microstructure. Magnetization experiments at 77 K indicated a J c value of 1x10 5 A/cm 2 at 1 T. Transport measurements at 77 K showed a greatly enhanced field dependence of the critical current density. Transmission electron microscopy revealed an important grain-boundary feature which eliminated the weak-link behavior. Large amounts of dislocations have also been found in the zone-melted sample which may contribute to flux pinning in the system

Higher spin currents in the critical O(N) vector model at 1/N2

International Nuclear Information System (INIS)

Manashov, A.N.; Strohmaier, M.

2017-06-01

We calculate the anomalous dimensions of higher spin singlet currents in the critical O(N) vector model at order 1/N 2 . The results are shown to be in agreement with the four-loop perturbative computation in φ 4 theory in 4-2ε dimensions. It is known that the order 1/N anomalous dimensions of higher-spin currents happen to be the same in the Gross-Neveu and the critical vector model. On the contrary, the order 1/N 2 corrections are different. The results can also be interpreted as a prediction for the two-loop computation in the dual higher-spin gravity.

Critical report of current fisheries management measures implemented for the North Sea mixed demersal fisheries

DEFF Research Database (Denmark)

Nielsen, J. Rasmus; Ulrich, Clara; Hegland, Troels J.

The present report is an EU-FP7-SOCIOEC Report giving an overview and critical evaluation of the current management measures implemented for the North Sea mixed demersal fisheries and the fish stocks involved in this. Also, this involves review and critical evaluation of the scientific advice...

Influence of the current-phase relation on the critical-current-applied-magnetic-flux dependence in parallel-connected Josephson junctions

International Nuclear Information System (INIS)

Tsang, W.; Van Duzer, T.

1976-01-01

The form of the current-phase relations for the Josephson junctions is shown to have a significant influence on the relation I/sub c/(theta/sub a/) between critical current and applied flux for two junctions connected in parallel in a superconducting circuit. The observed one-flux-quantum periodicity and inversion symmetry of the I/sub c/(theta/sub a/) relation are shown to result from the fact that the current-phase, i-phi, relations of the junctions satisfy i (phi+2mπ) =i (phi) and i (-phi) =-i (phi), respectively. It is also shown that if the current-phase relations for the two junctions are different, an asymmetry appears in the I/sub c/(theta/sub a/)

Improved critical current densities and compressive strength in porous superconducting structures containing calcium

International Nuclear Information System (INIS)

Walsh, D; Hall, S R; Wimbush, S C

2008-01-01

Templated control of crystallization by biopolymers is a new technique in the synthesis of high temperature superconducting phases. By controlling the way YBa 2 Cu 3 O 7-δ (Y123) materials crystallize and are organized in three dimensions, the critical current density can be improved. In this work, we present the results of doping superconducting sponges with calcium ions, which result in higher critical current densities (J c ) and improved compressive strength compared to that of commercially available Y123, in spite of minor reductions in T c . Y123 synthesis using the biopolymer dextran achieves not only an extremely effective oxygenation of the superconductor but also an in situ template-directing of the crystal morphology producing high J c , homogeneous superconducting structures with nano-scale crystallinity

Critical current of the nonuniform Josephson transition at intergranular boundary with random dislocation distribution

International Nuclear Information System (INIS)

Mejlikhov, E.Z.; Farzetdinova, R.M.

1997-01-01

Critical current of inhomogeneous intergranular Josephson transition is calculated in the assumption concerning superconductivity suppression by local strains of boundary dislocations with random distribution

Design verification enhancement of field programmable gate array-based safety-critical I&C system of nuclear power plant

Energy Technology Data Exchange (ETDEWEB)

Ahmed, Ibrahim [Department of Nuclear Engineering, Kyung Hee University, 1732 Deogyeong-daero, Giheung-gu, Yongin-si, Gyeonggi-do 17104 (Korea, Republic of); Jung, Jaecheon, E-mail: jcjung@kings.ac.kr [Department of Nuclear Power Plant Engineering, KEPCO International Nuclear Graduate School, 658-91 Haemaji-ro, Seosang-myeon, Ulju-gun, Ulsan 45014 (Korea, Republic of); Heo, Gyunyoung [Department of Nuclear Engineering, Kyung Hee University, 1732 Deogyeong-daero, Giheung-gu, Yongin-si, Gyeonggi-do 17104 (Korea, Republic of)

2017-06-15

Highlights: • An enhanced, systematic and integrated design verification approach is proposed for V&V of FPGA-based I&C system of NPP. • RPS bistable fixed setpoint trip algorithm is designed, analyzed, verified and discussed using the proposed approaches. • The application of integrated verification approach simultaneously verified the entire design modules. • The applicability of the proposed V&V facilitated the design verification processes. - Abstract: Safety-critical instrumentation and control (I&C) system in nuclear power plant (NPP) implemented on programmable logic controllers (PLCs) plays a vital role in safe operation of the plant. The challenges such as fast obsolescence, the vulnerability to cyber-attack, and other related issues of software systems have currently led to the consideration of field programmable gate arrays (FPGAs) as an alternative to PLCs because of their advantages and hardware related benefits. However, safety analysis for FPGA-based I&C systems, and verification and validation (V&V) assessments still remain important issues to be resolved, which are now become a global research point of interests. In this work, we proposed a systematic design and verification strategies from start to ready-to-use in form of model-based approaches for FPGA-based reactor protection system (RPS) that can lead to the enhancement of the design verification and validation processes. The proposed methodology stages are requirement analysis, enhanced functional flow block diagram (EFFBD) models, finite state machine with data path (FSMD) models, hardware description language (HDL) code development, and design verifications. The design verification stage includes unit test – Very high speed integrated circuit Hardware Description Language (VHDL) test and modified condition decision coverage (MC/DC) test, module test – MATLAB/Simulink Co-simulation test, and integration test – FPGA hardware test beds. To prove the adequacy of the proposed

Design verification enhancement of field programmable gate array-based safety-critical I&C system of nuclear power plant

International Nuclear Information System (INIS)

Ahmed, Ibrahim; Jung, Jaecheon; Heo, Gyunyoung

2017-01-01

Highlights: • An enhanced, systematic and integrated design verification approach is proposed for V&V of FPGA-based I&C system of NPP. • RPS bistable fixed setpoint trip algorithm is designed, analyzed, verified and discussed using the proposed approaches. • The application of integrated verification approach simultaneously verified the entire design modules. • The applicability of the proposed V&V facilitated the design verification processes. - Abstract: Safety-critical instrumentation and control (I&C) system in nuclear power plant (NPP) implemented on programmable logic controllers (PLCs) plays a vital role in safe operation of the plant. The challenges such as fast obsolescence, the vulnerability to cyber-attack, and other related issues of software systems have currently led to the consideration of field programmable gate arrays (FPGAs) as an alternative to PLCs because of their advantages and hardware related benefits. However, safety analysis for FPGA-based I&C systems, and verification and validation (V&V) assessments still remain important issues to be resolved, which are now become a global research point of interests. In this work, we proposed a systematic design and verification strategies from start to ready-to-use in form of model-based approaches for FPGA-based reactor protection system (RPS) that can lead to the enhancement of the design verification and validation processes. The proposed methodology stages are requirement analysis, enhanced functional flow block diagram (EFFBD) models, finite state machine with data path (FSMD) models, hardware description language (HDL) code development, and design verifications. The design verification stage includes unit test – Very high speed integrated circuit Hardware Description Language (VHDL) test and modified condition decision coverage (MC/DC) test, module test – MATLAB/Simulink Co-simulation test, and integration test – FPGA hardware test beds. To prove the adequacy of the proposed

What happens in Josephson junctions at high critical current densities

Science.gov (United States)

Massarotti, D.; Stornaiuolo, D.; Lucignano, P.; Caruso, R.; Galletti, L.; Montemurro, D.; Jouault, B.; Campagnano, G.; Arani, H. F.; Longobardi, L.; Parlato, L.; Pepe, G. P.; Rotoli, G.; Tagliacozzo, A.; Lombardi, F.; Tafuri, F.

2017-07-01

The impressive advances in material science and nanotechnology are more and more promoting the use of exotic barriers and/or superconductors, thus paving the way to new families of Josephson junctions. Semiconducting, ferromagnetic, topological insulator and graphene barriers are leading to unconventional and anomalous aspects of the Josephson coupling, which might be useful to respond to some issues on key problems of solid state physics. However, the complexity of the layout and of the competing physical processes occurring in the junctions is posing novel questions on the interpretation of their phenomenology. We classify some significant behaviors of hybrid and unconventional junctions in terms of their first imprinting, i.e., current-voltage curves, and propose a phenomenological approach to describe some features of junctions characterized by relatively high critical current densities Jc. Accurate arguments on the distribution of switching currents will provide quantitative criteria to understand physical processes occurring in high-Jc junctions. These notions are universal and apply to all kinds of junctions.

Field mapping measurements to determine spatial and field dependence of critical current density in YBCO tapes

International Nuclear Information System (INIS)

Leclerc, J.; Berger, K.; Douine, B.; Lévêque, J.

2013-01-01

Highlights: • A method for characterizing superconducting tapes from field mapping is presented. • A new and efficient field mapping apparatus has been setup. • This method allows the spatial characterization of superconducting tapes. • The critical current density is obtained as a function of the flux density. • This method has been experimentally tested on an YBCO tape. -- Abstract: In this paper a measurement method that allows the determination of the critical current density of superconducting tape from field mapping measurements is presented. This contact-free method allows obtaining characteristics of the superconductor as a function of the position and of the applied flux density. With some modifications, this technique can be used for reel-to-reel measurements. The determination of the critical current density is based on an inverse calculation. This involves calculating the current distribution in the tape from magnetic measurements. An YBaCuO tape has been characterized at 77 K. A defect in this superconductor has been identified. Various tests were carried out to check the efficiency of the method. The inverse calculation was tested theoretically and experimentally. Comparison with a transport current measurement was also performed

Experimental and numerical study of influence of ferromagnetic cover on critical current of BiSCCO-2223/Ag tape superconductor

International Nuclear Information System (INIS)

Vojenciak, M; Souc, J; Goemoery, F

2009-01-01

Samples of commercially available BiSCCO-2223/Ag tape have been partially covered by the ferromagnetic material. Improvement of the self-field critical current up to 15 % has been achieved by this procedure. A critical current of such tape strongly depends on geometric and magnetic properties of both, the superconducting tape as well as the ferromagnetic cover. Numerical simulations, based on the critical state model using commercial finite element method (FEM) code, have been performed. Properties of superconductor are characterized by anisotropic dependence of the critical current density on magnetic field as well as detail geometry of filaments. The ferromagnetic material is characterized by nonlinear magnetization curve. Nonlinear dependences of the critical current on selected parameters are shown in this work. Optimization of the cover parameters using these curves has been made. Samples with various parameters have been manufactured for the confirmation of numerical simulations results. Experimental results are in good qualitative agreement with results obtained by numerical simulations.

Influence of two-stage annealing treatment on critical current of bronze-processed multifilamentary Nb/sub 3/Sn superconducting materials

International Nuclear Information System (INIS)

Ochiai, S.; Osamura, K.; Ryoji, M.

1987-01-01

The influence of changes of volume fraction of Nb/sub 3/Sn, grain size and upper critical magnetic field due to two-stage annealing treatment (low temperature annealing to form fine grains + high temperature annealing to raise upper critical magnetic field) on overall critical current and critical current density were studied at magnetic field of 3-15 T. When annealing temperature was low (773-923 K) and the volume fraction of Nb/sub 3/Sn was low in first stage annealing, second stage annealing could raise the overall critical current over the range of the applied magnetic field due to increase in upper critical magnetic field H/sub c2/ and volume fraction of Nb/sub 3/Sn accompanying with reduction in Sn concentration in the bronze matrix, which played a role to reduce residual strain in Nb/sub 3/Sn, leading to high H/sub c2/ although the loss in pinning force arose from the coarsening of the grains. When the annealing temperature was high (973 K) and the Nb/sub 3/Sn was formed until the Sn was consumed in the first stage, second stage annealing could not raise the critical current due to increase in grain size and no effective increase in H/sub c2/. The critical current density at low magnetic fields below several Teslas was reduced by the second stage annealing due to increase in grain size but that at high fields was raised due to increase in high H/sub c2/. The reverse two-stage annealing treatment (high temperature annealing in the first stage+low temperature annealing in the second stage) reduced the H/sub c2/ slightly with increasing second stage annealing temperature and time. The critical current density at low magnetic fields was determined mainly by the grain size and that at high fields was determined by the combination of the upper critical field and grain size

Higher critical current density achieved in Bi-2223 High-Tc superconductors

Directory of Open Access Journals (Sweden)

M.S. Shalaby

2016-07-01

Full Text Available Bi2Sr2Ca2Cu3Ox (Bi-2223 were prepared using a solid state reaction method at different sintering times and temperatures. Structural phase identifications have been done using X-Ray analysis and refinement by Reitveld method which proves the coexistence of Bi-2223 and Bi-2212 phases. The critical transition temperature Tc and critical current density Jc values were measured using superconducting quantum interference device magnetometer (SQUID and by the magneto-optics technique. A remarkable rapid decrease to the diamagnetic signal in the magnetization versus temperature M(T at 110 K and Jc around 1.2 × 107 A/m2 at 5 K are confirmed for the Bi-2223 compound.

ON current enhancement of nanowire Schottky barrier tunnel field effect transistors

Science.gov (United States)

Takei, Kohei; Hashimoto, Shuichiro; Sun, Jing; Zhang, Xu; Asada, Shuhei; Xu, Taiyu; Matsukawa, Takashi; Masahara, Meishoku; Watanabe, Takanobu

2016-04-01

Silicon nanowire Schottky barrier tunnel field effect transistors (NW-SBTFETs) are promising structures for high performance devices. In this study, we fabricated NW-SBTFETs to investigate the effect of nanowire structure on the device characteristics. The NW-SBTFETs were operated with a backgate bias, and the experimental results demonstrate that the ON current density is enhanced by narrowing the width of the nanowire. We confirmed using the Fowler-Nordheim plot that the drain current in the ON state mainly comprises the quantum tunneling component through the Schottky barrier. Comparison with a technology computer aided design (TCAD) simulation revealed that the enhancement is attributed to the electric field concentration at the corners of cross-section of the NW. The study findings suggest an effective approach to securing the ON current by Schottky barrier width modulation.

ac loss and dc critical current densities of Nb3Sn tapes by the solid state diffusion process

International Nuclear Information System (INIS)

Suenaga, M.; Klamut, C.; Bussiere, J.F.

1976-01-01

The effects of metallurgical processing on 60 Hz ac losses and dc critical currents in Nb 3 Sn tapes fabricated by the solid state diffusion technique were investigated. An addition of Al to the Cu--Sn alloy for the matrix resulted in large reduction in the ac losses of Nb 3 Sn tapes, but the highest linear critical current densities were observed in Nb 3 Sn tapes produced with a Nb-1 wt percent Zr core in a Cu-13 wt percent Sn matrix. Values of the losses and the critical currents in these tapes can meet the present requirements for the ac superconducting power cables

Drive Current Enhancement in TFET by Dual Source Region

Directory of Open Access Journals (Sweden)

Zhi Jiang

2015-01-01

Full Text Available This paper presents tunneling field-effect transistor (TFET with dual source regions. It explores the physics of drive current enhancement. The novel approach of dual source provides an effective technique for enhancing the drive current. It is found that this structure can offer four tunneling junctions by increasing a source region. Meanwhile, the dual source structure does not influence the excellent features of threshold slope (SS of TFET. The number of the electrons and holes would be doubled by going through the tunneling junctions on the original basis. The overlap length of gate-source is also studied. The dependence of gate-drain capacitance Cgd and gate-source capacitance Cgs on gate-to-source voltage Vgs and drain-to-source voltage Vds was further investigated. There are simulation setups and methodology used for the dual source TFET (DS-TFET assessment, including delay time, total energy per operation, and energy-delay product. It is confirmed that the proposed TFET has strong potentials for VLSI.

Exponential temperature dependence of the critical transport current in Y-Ba-Cu-O thin films

International Nuclear Information System (INIS)

Yom, S.S.; Hahn, T.S.; Kim, Y.H.; Chu, H.; Choi, S.S.

1989-01-01

We have measured the critical currents in rf-sputtered YBa 2 Cu 3 O/sub 7-x/ thin films deposited on polycrystalline yttria-stabilized zirconia substrates as a function of temperature down to 10 K. The dependence of the granular films at low temperature indicated exponential behavior which is similar to the superconductor-normal metal-superconductor (S-N-S) type tunneling junctions. For the films with a grain size of approximately 1 μm, we observed two exponential decay constants, which suggest that Josephson junctions limiting the transport critical current are possible both at the grain boundaries and at twin boundaries

Critical Thinking and Collaboration: A Strategy to Enhance Student Learning

Directory of Open Access Journals (Sweden)

Ronald A. Styron, Jr.

2014-12-01

Full Text Available In numerous studies relative to collaboration and critical thinking, an instructional strategy called Team- Based Learning has proven to be an effective approach to teaching and learning. Team-Based Learning utilizes a specific sequence of individual work, group work and immediate feedback to create a motivational framework in which students increasingly hold each other accountable for coming to class prepared and contributing to discussion. Using an action research conceptual model diffusion of innovation theory, the process of P-20 quality enhancement using Team-Based Learning is examined.

Critical current density of four-CuO2-layer T1Ba2Ca3Cu4O11-δ

International Nuclear Information System (INIS)

Zhang, L.; Liu, J.Z.; Shelton, R.N.

1998-01-01

Full text: A key requirement for technological application is to have superconductors with high critical current density at practical operating temperatures and magnetic fields. The critical current density is strongly related to underlying properties of high T c superconductors, such as layering, anisotropy and other intrinsic material structures. The thallium-based superconductors attracted much attention at early stage mainly due to their high superconducting transitions. Recent studies show that these materials appear to be a better choice for achieving higher critical current density because of a stronger interlayer coupling between superconducting layers. Single crystals of TlBa 2 Ca 3 Cu 4 O 11-δ were grown by a self-flux method. This material is a strong-layered superconductor with four-CuO 2 -planes in a unit cell and a superconducting transition temperature of 128K. Our experimental results show that TlBa 2 Ca 3 Cu 4 O 11-δ crystals have high irreversibility line, large critical current density and high upper critical field. The impact of layering and the number of Cu-O layers on flux pinning, critical current density and other magnetic properties will also be discussed

Study of critical beta non-circular tokamak equilibria sustained in steady state by beam driven currents

International Nuclear Information System (INIS)

Okano, K.; Ogawa, Y.; Naitou, H.

1988-07-01

A new MHD-equilibrium/current-drive analysis code was developed to analyse the high beta tokamak equilibria consistent with the beam driven current profiles. In this new code, the critical beta equilibrium, which is stable against the ballooning mode, the kink mode and the Mercier mode, is determined first using MHD equilibrium and stability analysis codes (EQLAUS/ERATO). Then, the current drive parameters and the plasma parameters, required to sustain this critical beta equilibrium, are determined by iterative calculations. The beam driven current profiles are evaluated by the Fokker-Planck calculations on individual flux surfaces, where the toroidal effects on the beam ion and plasma electron trajectories are considered. The pressure calculation takes into account the beam ion and fast alpha components. A peculiarity of our new method is that the obtained solution is not only consistent with the MHD equilibrium but also consistent with the critical beta limit conditions, in the current profile and the pressure profile. Using this new method, β ∼ 21 % bean and β ∼ 6 % D-type critical beta equilibria were scanned for various parameters; the major radius, magnetic field, temperature, injection energy, etc. It was found that the achievable Q value for the bean type was always about 30 % larger than for the D-type cases, where Q = fusion power/beam power. With strong beanness, Q ∼ 6 for DEMO type tokamaks (∼500 MWth) and Q ∼ 20 for power reactor size (4.5 GWth) are achievable. On the other hand, the Q value would not exceed sixteen for the D-type machines. (author)

Counter terrorism functions to enhance critical infrastructure resilience against CBRNe terrorism

NARCIS (Netherlands)

Bonsen, I.M.; Gaasbeek, R.C.

2009-01-01

Current approaches in critical infrastructure protection use long lists of items that fail to give its user a structured answer to the state of protection of its object. The functionality approach uses different terrorist functions to structure the threat (which are to have intent, to scout, to

Critical condition for current-driven instability excited in turbulent heating of TRIAM-1 tokamak plasma

Energy Technology Data Exchange (ETDEWEB)

Nakamura, Y; Watanabe, T; Nagao, A; Nakamura, K; Kikuchi, M; Aoki, T; Hiraki, N; Itoh, S [Kyushu Univ., Fukuoka (Japan). Research Inst. for Applied Mechanics; Mitarai, O

1982-02-01

Critical condition for current-driven instability excited in turbulently heated TRIAM-1 tokamak plasma is investigated experimentally. Resistive hump in loop voltage, plasma density fluctuation and rapid increase of electron temperature in a skin layer are simultaneously observed at the time when the electron drift velocity amounts to the critical drift velocity for low-frequency ion acoustic instability.

Critical carbon input to maintain current soil organic carbon stocks in global wheat systems.

Science.gov (United States)

Wang, Guocheng; Luo, Zhongkui; Han, Pengfei; Chen, Huansheng; Xu, Jingjing

2016-01-13

Soil organic carbon (SOC) dynamics in croplands is a crucial component of global carbon (C) cycle. Depending on local environmental conditions and management practices, typical C input is generally required to reduce or reverse C loss in agricultural soils. No studies have quantified the critical C input for maintaining SOC at global scale with high resolution. Such information will provide a baseline map for assessing soil C dynamics under potential changes in management practices and climate, and thus enable development of management strategies to reduce C footprint from farm to regional scales. We used the soil C model RothC to simulate the critical C input rates needed to maintain existing soil C level at 0.1° × 0.1° resolution in global wheat systems. On average, the critical C input was estimated to be 2.0 Mg C ha(-1) yr(-1), with large spatial variability depending on local soil and climatic conditions. Higher C inputs are required in wheat system of central United States and western Europe, mainly due to the higher current soil C stocks present in these regions. The critical C input could be effectively estimated using a summary model driven by current SOC level, mean annual temperature, precipitation, and soil clay content.

Advanced electrical current measurements of microdischarges: evidence of sub-critical pulses and ion currents in barrier discharge in air

Science.gov (United States)

Synek, Petr; Zemánek, Miroslav; Kudrle, Vít; Hoder, Tomáš

2018-04-01

Electrical current measurements in corona or barrier microdischarges are a challenge as they require both high temporal resolution and a large dynamic range of the current probe used. In this article, we apply a simple self-assembled current probe and compare it to commercial ones. An analysis in the time and frequency domain is carried out. Moreover, an improved methodology is presented, enabling both temporal resolution in sub-nanosecond times and current sensitivity in the order of tens of micro-amperes. Combining this methodology with a high-tech oscilloscope and self-developed software, a unique statistical analysis of currents in volume barrier discharge driven in atmospheric-pressure air is made for over 80 consecutive periods of a 15 kHz applied voltage. We reveal the presence of repetitive sub-critical current pulses and conclude that these can be identified with the discharging of surface charge microdomains. Moreover, extremely low, long-lasting microsecond currents were detected which are caused by ion flow, and are analysed in detail. The statistical behaviour presented gives deeper insight into the discharge physics of these usually undetectable current signals.

Current enhancement in crystalline silicon photovoltaic by low-cost nickel silicide back contact

KAUST Repository

Bahabry, R. R.; Gumus, A.; Kutbee, A. T.; Wehbe, N.; Ahmed, S. M.; Ghoneim, M. T.; Lee, K. -T.; Rogers, J. A.; Hussain, M. M.

2016-01-01

We report short circuit current (Jsc) enhancement in crystalline silicon (C-Si) photovoltaic (PV) using low-cost Ohmic contact engineering by integration of Nickel mono-silicide (NiSi) for back contact metallization as an alternative to the status quo of using expensive screen printed silver (Ag). We show 2.6 mA/cm2 enhancement in the short circuit current (Jsc) and 1.2 % increment in the efficiency by improving the current collection due to the low specific contact resistance of the NiSi on the heavily Boron (B) doped Silicon (Si) interface.

Current enhancement in crystalline silicon photovoltaic by low-cost nickel silicide back contact

KAUST Repository

Bahabry, R. R.

2016-11-30

We report short circuit current (Jsc) enhancement in crystalline silicon (C-Si) photovoltaic (PV) using low-cost Ohmic contact engineering by integration of Nickel mono-silicide (NiSi) for back contact metallization as an alternative to the status quo of using expensive screen printed silver (Ag). We show 2.6 mA/cm2 enhancement in the short circuit current (Jsc) and 1.2 % increment in the efficiency by improving the current collection due to the low specific contact resistance of the NiSi on the heavily Boron (B) doped Silicon (Si) interface.

CRITICAL RADAR: TOOL AND METHODOLOGY FOR EVALUATING CURRENT PROJECTS USING MULTIPLE VARIABLES

Directory of Open Access Journals (Sweden)

André M. Ferrari

2017-06-01

Full Text Available Many resources are invested in measurement processes of projects indicators without, however, give a clear view of which projects deserves the right attention at the right time. This paper proposes the use of statistics, through the analysis of multiple variables and their interrelationships, to give better basis to a critical assessment methodology of current projects used in a multinational mining company. The contribution of the research is to report the methodology called Critical Radar which is based on a graphical tool with simple operationalization that can support the decision making in complex environments, and has great flexibility across the different market scenarios and possible changes in companies guidelines. The tool has great potential to help evaluate current projects due to their characteristics of flexible use in different business areas; high degree of freedom for improvement; use of known market tool in its development; ease of viewing the results through charts and notes and user freedom to use any existing indicators in the company if complied with some statistical data quality characteristics.

Influence of the 3D-2D crossover on the critical current of Nb/Cu multilayers

DEFF Research Database (Denmark)

Krasnov, V. M.; Pedersen, Niels Falsig; Oboznov, V. A.

1994-01-01

We report the experimental observation of the Josephson critical current across layers, I(c) perpendicular-to, for Nb/Cu multilayers. Unique samples with a small cross section (20 mum in diameter) consisting of ten Nb/Cu junctions were fabricated for such measurements. A strong influence of the d......We report the experimental observation of the Josephson critical current across layers, I(c) perpendicular-to, for Nb/Cu multilayers. Unique samples with a small cross section (20 mum in diameter) consisting of ten Nb/Cu junctions were fabricated for such measurements. A strong influence...... of the dimensional 3D-2D cross-over on the I(c)perpendicular-to was observed. Thus, as the temperature becomes smaller than T2D, hysteresis in the current-voltage characteristic appears and the behavior of the temperature dependence of the I(c)perpendicular-to changes. For T > T2D the diminishing of the hysteresis...... is caused by a sharp decrease of the junction capacitance in the 3D regime when the sample becomes uniform across layers. Calculation of the critical-current temperature dependence I(c)perpendicular-to (T) for our multilayers was made. An agreement between experimental and theoretical dependencies I...

Investigation of inter-grain critical current density in Bi2Sr2CaCu2O8+δ superconducting wires and its relationship with the heat treatment protocol

Science.gov (United States)

Pallecchi, I.; Leveratto, A.; Braccini, V.; Zunino, V.; Malagoli, A.

2017-09-01

In this work we investigate the effect of each different heat treatment stage in the fabrication of Bi2Sr2CaCu2O8+δ superconducting wires on intra-grain and inter-grain superconducting properties. We measure magnetic critical temperature T c values and transport critical current density J c at temperatures from 4 K to 40 K and in fields up to 7 T. From an analysis of the temperature dependence of the self-field critical current density J c(T) that takes into account weak link behavior and the proximity effect, we study grain boundary (GB) transparency to supercurrents; we also establish a relationship between GB oxygenation in the different steps of the fabrication process and GB transparency to supercurrents. We find that GB oxygenation starts in the first crystallization stage, but it becomes complete in the plateau at 836 °C and in slow cooling stages and is further enhanced in the prolonged post-annealing step. Such oxygenation makes GBs more conductive, thus improving the inter-grain J c value and temperature dependence. On the other hand, from inspection of the T c values in the framework of the phase diagram dome, we find that grains are already oxygenated in the crystallization step up to the optimal doping, while successive slow cooling and post-annealing treatments further enhance the degree of overdoping, especially if carried out in oxygen atmosphere rather than in air.

Higher spin currents in the critical O(N) vector model at 1/N{sup 2}

Energy Technology Data Exchange (ETDEWEB)

Manashov, A.N. [Hamburg Univ. (Germany). 2. Inst. fuer Theoretische Physik; Regensburg Univ. (Germany). Inst. fuer Theoretische Physik; Skvortsov, E.D. [Munich Univ. (Germany). Arnold Sommerfeld Center for Theoretical Physics; Lebedev Institute of Physics, Moscow (Russian Federation); Strohmaier, M. [Regensburg Univ. (Germany). Inst. fuer Theoretische Physik

2017-06-15

We calculate the anomalous dimensions of higher spin singlet currents in the critical O(N) vector model at order 1/N{sup 2}. The results are shown to be in agreement with the four-loop perturbative computation in φ{sup 4} theory in 4-2ε dimensions. It is known that the order 1/N anomalous dimensions of higher-spin currents happen to be the same in the Gross-Neveu and the critical vector model. On the contrary, the order 1/N{sup 2} corrections are different. The results can also be interpreted as a prediction for the two-loop computation in the dual higher-spin gravity.

Temperature dependence of critical current and transport current losses of 4 mm YBCO coated conductors manufactured using nonmagnetic substrate

Science.gov (United States)

Kvitkovic, J.; Hatwar, R.; Pamidi, S. V.; Fleshler, S.; Thieme, C.

2015-12-01

The temperature dependence of the critical current and AC losses were measured on American Superconductor Corporation's (AMSC) second generation high temperature superconducting (2G HTS) wire produced by Rolling Assisted Biaxially Textured Substrate (RABiTS) and Metal Organic Deposition (MOD) process. Wires manufactured with two types of substrates were characterized. The magnetic substrate with composition Ni5a%W exhibits a magnetic signature and has non-negligible AC losses in AC power applications. A new nonmagnetic substrate with an alloy composition Ni9a%W has been developed by AMSC to address the AC losses in 2G HTS. The data presented show that the performance of the new conductor is identical to the conductor with magnetic substrate in terms of critical current density. The data on AC losses demonstrate the absence of ferromagnetic loss component in the new conductor and significantly reduced AC losses at low to moderate values of I/Ic. The reduced losses will translate into reduced capital costs and lower operating costs of superconducting electrical devices for AC applications.

Effects of small magnetic fields on the critical current of thin films

International Nuclear Information System (INIS)

Passos, Wagner de Assis Cangussu; Lisboa-Filho, Paulo Noronha; Ortiz, Wilson Aires; Kang, W.N.; Choi, Eun-Mi; Hyeong-Jin, Kim; Lee, Sung-Ik Lee

2002-01-01

Full text: Magnetic fields applied perpendicularly to superconducting thin films may produce dendritic patterns, where penetrated and Meissner regions coexist, as observed in Nb, YBaCuO and MgB 2 [1]. A temperature-dependent limiting-field, Hd(T), separates the dendritic mode from a critical-state-like penetration regime. Due to large demagnetizing factors in the perpendicular geometry, small fields may be enough to drive portions of the sample into the mixed state. Lack of symmetry and local defects might then permeate the dendritic mode. Hd(T) is related[2] to the bulk lower critical field, Hc1, which depends on the in-plane current density, J. Not surprisingly, Hd is depressed by J[3]. The dendritic mode can be detected by the AC-susceptibility: penetrated fingers act as intergranular material, and the imaginary component peaks at Tc-inter(J). Films of 0.2-0.4 microns, with millimeter lateral sizes, develop dendrites when submitted to Earth's field[2], what limits the critical current, J c . This contribution studies how J c is affected by field-induced granularity in thin films. 1. C. A. Duran et al., PRB 52 (1995) 75; P. Leiderer et al., PRL. 71 (1993) 2646; T.H. Johansen et al., Supercond. Sci. Technol. 14 (2001) 1. 2. W. A. Ortiz et al., Physica C 361 (2001) 267. 3. A. V. Bobyl et al., cond-mat/0201260, submitted to APL

Theory of flux cutting and flux transport at the critical current of a type-II superconducting cylindrical wire

International Nuclear Information System (INIS)

Clem, John R.

2011-01-01

I introduce a critical-state theory incorporating both flux cutting and flux transport to calculate the magnetic-field and current-density distributions inside a type-II superconducting cylinder at its critical current in a longitudinal applied magnetic field. The theory is an extension of the elliptic critical-state model introduced by Romero-Salazar and Perez-Rodriguez. The vortex dynamics depend in detail on two nonlinear effective resistivities for flux cutting (ρ(parallel)) and flux flow (ρ(perpendicular)), and their ratio r = ρ(parallel)/ρ(perpendicular). When r c (φ) that makes the vortex arc unstable.

Field-dependent transport critical current in single crystals of Ba(Fe1-xTMx)2As2 (TM = Co, Ni) superconductors

International Nuclear Information System (INIS)

Tanatar, M A; Ni, N; Bud'ko, S L; Canfield, P C; Prozorov, R

2010-01-01

Critical current density was studied by direct electrical transport measurements in single crystals of Ba(Fe 1-x TM x ) 2 As 2 under magnetic fields up to 9 T. To understand the relation of the critical current to the structural transformations in the material, the electron doping level was controlled by the amount of TM = Co (underdoped x = 0.054 versus optimally doped x = 0.074) and by the nature of the dopant (optimally doped TM = Co versus TM = Ni). It is found that the suppression of the critical current density by the magnetic field is much slower for Ni and underdoped Co compositions than for an optimally doped Co composition. We relate this difference to the proximity to the orthorhombic/antiferromagnetic phase boundary in the T(x) phase diagram. Structural domains formed in this area of the phase diagram create favorable conditions for pinning and not only increase critical current densities, but also hamper the degradation of the critical current under magnetic field.

Critical Thinking Skills and Academic Maturity: Emerging Results from a Five-Year Quality Enhancement Plan (QEP) Study

Science.gov (United States)

Toppin, Ian N.; Chitsonga, Shadreck

2016-01-01

The QEP that was implemented in this study focused on enhancing students' critical thinking skills. A pretest/posttest approach was used to assess students' critical thinking progress in freshman level core English and Math courses. An intervention was performed involving intensive instruction and assignments relating to a set of reasoning…

Hysteresis of critical currents of superconducting bridges in low perpendicular magnetic fields

International Nuclear Information System (INIS)

Aomine, T.; Tanaka, E.; Yamasaki, S.; Tani, K.; Yonekura, A.

1989-01-01

Hysteresis of critical currents I c of superconducting bridges with In, Nb, and NbN has been studied in low perpendicular magnetic fields. Influences of bridge geometry, small field sweep, trapped flux, and bombardment of argon ions on the hysteresis were made clear. The experimental results suggest that the edge pinning and trapped flux in the bank of bridges are associated with the hysteresis. The peak value of I c of NbN bridges, as well as granular Al and In bridges reported before, in decreasing fields agrees with the calculated pair-breaking current. The origin of the hysteresis is discussed

Dependence of critical current density on crystalline direction in thin YBCO films

DEFF Research Database (Denmark)

Paturi, P.; Peurla, M.; Raittila, J.

2005-01-01

The dependence of critical current density (J(c)) on the angle between the current direction and the (100) direction in the ab-plane of thin YBCO films deposited on (001)-SrTiO3 from natiocrystalline and microcrystalline targets is studied using magneto-optical microscopy. In the films made from...... the nanocrystalline target it is found that J(c) does not depend on the angle whereas J(c) decreases with increasing angle in the films made from the microcrystalline target. The films were characterized by detailed X-ray diffraction measurements. The findings are explained in terms of a network of planar defects...

Recalled peer relationship experiences and current levels of self-criticism and self-reassurance.

Science.gov (United States)

Kopala-Sibley, Daniel C; Zuroff, David C; Leybman, Michelle J; Hope, Nora

2013-03-01

Numerous studies have shown that personality factors may increase or decrease individuals' vulnerability to depression, but little research has examined the role of peer relationships in the development of these factors. Accordingly, this study examined the role of recalled parenting and peer experiences in the development of self-criticism and self-reassurance. It was hypothesized that, controlling for recalled parenting behaviours, specific recalled experiences of peer relationships would be related to current levels of specific forms of self-criticism and self-reassurance. Hypotheses were tested using a retrospective design in which participants were asked to recall experiences of parenting and peer relationships during early adolescence. This age was chosen as early adolescence has been shown to be a critical time for the development of vulnerability to depression. A total of 103 female and 97 male young adults completed measures of recalled parenting, overt and relational victimization and prosocial behaviour by peers, and current levels of self-criticism and self-reassurance. Hierarchical regression analyses showed that parents and peers independently contributed to the development of self-criticism and self-reassurance. Specifically, controlling for parental care and control, overt victimization predicted self-hating self-criticism, relational victimization predicted inadequacy self-criticism, and prosocial behaviour predicted self-reassurance. As well, prosocial behaviour buffered the effect of overt victimization on self-reassurance. Findings highlight the importance of peers in the development of personality risk and resiliency factors for depression, and suggest avenues for interventions to prevent the development of depressive vulnerabilities in youth. The nature of a patient's personality vulnerability to depression may be better understood through a consideration of the patient's relationships with their peers as well as with parents during

Uranium systems to enhance benchmarks for use in the verification of criticality safety computer models. Final report, February 16, 1990--December 31, 1994

International Nuclear Information System (INIS)

Busch, R.D.

1995-01-01

Dr. Robert Busch of the Department of Chemical and Nuclear Engineering was the principal investigator on this project with technical direction provided by the staff in the Nuclear Criticality Safety Group at Los Alamos. During the period of the contract, he had a number of graduate and undergraduate students working on subtasks. The objective of this work was to develop information on uranium systems to enhance benchmarks for use in the verification of criticality safety computer models. During the first year of this project, most of the work was focused on setting up the SUN SPARC-1 Workstation and acquiring the literature which described the critical experiments. By august 1990, the Workstation was operational with the current version of TWODANT loaded on the system. MCNP, version 4 tape was made available from Los Alamos late in 1990. Various documents were acquired which provide the initial descriptions of the critical experiments under consideration as benchmarks. The next four years were spent working on various benchmark projects. A number of publications and presentations were made on this material. These are briefly discussed in this report

Cooperative doping effects of Ti and nano-SiC on transport critical current density and grain connectivity of in situ MgB{sub 2} tapes

Energy Technology Data Exchange (ETDEWEB)

Pan, X.F., E-mail: PAN.Xifeng@nims.go.jp [National Institute for Materials Science, Superconducting Materials Research Center, 1-2-1, Sengen, Tsukuba, Ibaraki 305-0047 (Japan)] [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Chengdu 610031 (China); Matsumoto, A.; Kumakura, H. [National Institute for Materials Science, Superconducting Materials Research Center, 1-2-1, Sengen, Tsukuba, Ibaraki 305-0047 (Japan); Cheng, C.H.; Zhao, Y. [Key Laboratory of Magnetic Levitation and Maglev Trains (Ministry of Education of China), Superconductivity R and D Center (SRDC), Southwest Jiaotong University, Chengdu 610031 (China)] [School of Materials Science and Engineering, University of New South Wales, Sydney 2052, NSW (Australia)

2011-11-15

We studied the cooperative doping effects of Ti and nano-SiC on transport J{sub c} and grain connectivity of MgB{sub 2} tape. Ti doping significantly weakens the current dependence of T{sub c} of MgB{sub 2} tapes at self-field, and does not change T{sub c} or slightly increases T{sub c}. Further Ti adding can enhance in-field J{sub c} performance of SiC doped MgB{sub 2} tapes by a factor of 50-100% at 4.2 K and 10 T. Ti addition improves the J{sub c} performance of undoped and SiC doped MgB{sub 2} by modifying their grains connection. By now, nano-SiC powder (20-30 nm) is still the most effective additive for improving upper critical field and critical current density of MgB{sub 2}-based superconducting materials. However, some decomposed carbon aggregates at grain boundaries and results in serious weak-links of MgB{sub 2} grains, and these weak-links limit the further improvement of critical current density, J{sub c} of MgB{sub 2}, especially at lower fields. Ti doping is reported to increase the compactness of MgB{sub 2}, and modify its intergranular coupling by forming ultrathin TiB{sub 2} layer at grain boundaries. In this work, we studied the cooperative doping effects of Ti and nano-SiC on transport J{sub c} and grain connectivity of MgB{sub 2} and the possibility to improve transport J{sub c} of SiC doped MgB{sub 2} by introducing Ti additive. The results suggest the Ti addition can obviously improve J{sub c} of MgB{sub 2} at lower fields and also enhance the J{sub c} of SiC doped MgB{sub 2} by improving their grain connectivity which shows serious intergranular weak-links.

The reduction of optimal heat treatment temperature and critical current density enhancement of ex situ processed MgB2 tapes using ball milled filling powder

Science.gov (United States)

Fujii, Hiroki; Iwanade, Akio; Kawada, Satoshi; Kitaguchi, Hitoshi

2018-01-01

The optimal heat treatment temperature (Topt) at which best performance in the critical current density (Jc) property at 4.2 K is obtained is influenced by the quality or reactivity of the filling powder in ex situ processed MgB2 tapes. Using a controlled fabrication process, the Topt decreases to 705-735 °C, which is lower than previously reported by more than 50 °C. The Topt decrease is effective to suppress both the decomposition of MgB2 and hence the formation of impurities such as MgB4, and the growth of crystallite size which decreases upper critical filed (Hc2). These bring about the Jc improvement and the Jc value at 4.2 K and 10 T reaches 250 A/mm2. The milling process also decreases the critical temperature (Tc) below 30 K. The milled powder is easily contaminated in air and thus, the Jc property of the contaminated tapes degrades severely. The contamination can raise the Topt by more than 50 °C, which is probably due to the increased sintering temperature required against contaminated surface layer around the grains acting as a barrier.

Fatigue-damage evolution and damage-induced reduction of critical current of a Nb3Al superconducting composite

International Nuclear Information System (INIS)

Ochiai, S; Sekino, F; Sawada, T; Ohno, H; Hojo, M; Tanaka, M; Okuda, H; Koganeya, M; Hayashi, K; Yamada, Y; Ayai, N; Watanabe, K

2003-01-01

We have studied the fatigue-damage mechanism of a Nb 3 Al superconducting composite at room temperature, and the influences of the fatigue damages introduced at room temperature on the critical current at 4.2 K and the residual strength at room temperature. The main (largest) fatigue crack arose first in the clad copper and then extended into the inner core with an increasing number of stress cycles. The cracking of the Nb 3 Al filaments in the core region occurred at a late stage (around 60-90% of the fatigue life). Once the fracture of the core occurred, it extended very quickly, resulting in a quick reduction in critical current and the residual strength with increasing stress cycles. Such a behaviour was accounted for by the crack growth calculated from the S-N curves (the relation of the maximum stress to the number of stress cycles at failure) combined with the Paris law. The size and distribution of the subcracks along the specimen length, and therefore the reduction in critical current of the region apart from the main crack, were dependent on the maximum stress level. The large subcracks causing fracture of the Nb 3 Al filaments were formed when the maximum stress was around 300-460 MPa, resulting in large reduction in critical current, but not when the maximum stress was outside such a stress range

A high critical current density MOCVD coated conductor with strong vortex pinning centers suitable for very high field use

International Nuclear Information System (INIS)

Chen, Z; Kametani, F; Larbalestier, D C; Chen, Y; Xie, Y; Selvamanickam, V

2009-01-01

We have made extensive low temperature and high field evaluations of a recent 2.1 μm thick coated conductor (CC) grown by metal-organic chemical vapor deposition (MOCVD) with a view to its use for high field magnet applications, for which its very strong Hastelloy substrate makes it very suitable. This conductor contains dense three-dimensional (Y,Sm) 2 O 3 nanoprecipitates, which are self-aligned in planes tilted ∼7 deg. from the tape plane. Very strong vortex pinning is evidenced by high critical current density J c values of ∼3.1 MA cm -2 at 77 K and ∼43 MA cm -2 at 4.2 K, and by a strongly enhanced irreversibility field H irr , which reaches that of Nb 3 Sn (∼28 T at 1.5 K) at 60 K, even in the inferior direction of H parallel c axis. At 4.2 K, J c values are ∼15% of the depairing current density J d , much the highest of any superconductor suitable for magnet construction.

A high critical current density MOCVD coated conductor with strong vortex pinning centers suitable for very high field use

Energy Technology Data Exchange (ETDEWEB)

Chen, Z; Kametani, F; Larbalestier, D C [National High Magnetic Field Laboratory, Florida State University, Tallahassee, FL 32310 (United States); Chen, Y; Xie, Y; Selvamanickam, V [SuperPower Incorporated, Schenectady, NY 12304 (United States)], E-mail: zhijun@asc.magnet.fsu.edu

2009-05-15

We have made extensive low temperature and high field evaluations of a recent 2.1 {mu}m thick coated conductor (CC) grown by metal-organic chemical vapor deposition (MOCVD) with a view to its use for high field magnet applications, for which its very strong Hastelloy substrate makes it very suitable. This conductor contains dense three-dimensional (Y,Sm){sub 2}O{sub 3} nanoprecipitates, which are self-aligned in planes tilted {approx}7 deg. from the tape plane. Very strong vortex pinning is evidenced by high critical current density J{sub c} values of {approx}3.1 MA cm{sup -2} at 77 K and {approx}43 MA cm{sup -2} at 4.2 K, and by a strongly enhanced irreversibility field H{sub irr}, which reaches that of Nb{sub 3}Sn ({approx}28 T at 1.5 K) at 60 K, even in the inferior direction of H parallel c axis. At 4.2 K, J{sub c} values are {approx}15% of the depairing current density J{sub d}, much the highest of any superconductor suitable for magnet construction.

The influence of vortex pinning and grain boundary structure on critical currents across grain boundaries in YBa2Cu3Ox

International Nuclear Information System (INIS)

Miller, D. J.

1998-01-01

We have used studies of single grain boundaries in YBCO thin films and bulk bicrystals to study the influence of vortex pinning along a grain boundary on dissipation. The critical current density for transport across grain boundaries in thin films is typically more than an order of magnitude larger than that measured for transport across grain boundaries in bulk samples. For low disorientation angles, the difference in critical current density within the grains that form the boundary can contribute to the substantial differences in current density measured across the boundary. However, substantial differences exist in the critical current density across boundaries in thin film compared to bulk bicrystals even in the higher angle regime in which grain boundary dissipation dominates. The differences in critical current density in this regime can be understood on the basis of vortex pinning along the boundary

Anisotropy of the critical current in MgB₂ tapes made of high energy milled precursor powder

DEFF Research Database (Denmark)

Hässler, W.; Kovac, P.; Eisterer, M.

2010-01-01

For applications of MgB2 wires or tapes, high critical currents in high magnetic fields are essential. By using tapes in superconducting coils the anisotropic behaviour of the critical current, i.e. the dependence on the direction of the external field in relation to the tape surface, has to be t...

Toward Principles for Enhancing the Resilience of Ecosystem Services

NARCIS (Netherlands)

Biggs, R.; Schlüter, M.; Biggs, D.; Bohensky, E.L.; BurnSilver, S.; Cundill, G.; Dakos, V.; Daw, T.M.; Evans, L.S.; Kotschy, K.; Leitch, A.M.; Meek, C.; Quinlan, A.; Raudsepp-Hearne, C.; Robards, M.D.; Schoon, M.L.; Schultz, L.; West, P.C.

2012-01-01

Enhancing the resilience of ecosystem services (ES) that underpin human well-being is critical for meeting current and future societal needs, and requires specific governance and management policies. Using the literature, we identify seven generic policy-relevant principles for enhancing the

Critical current density and flux pinning in superconducting wires and coils of silver-clad Bi-Pb-Sr-Ca-Cu-O

International Nuclear Information System (INIS)

Dou, S.X.; Liu, H.K.; Apperley, M.H.; Song, K.H.; Sorrell, C.C.; Guo, S.J.; Loberg, B.; Easterling, K.E.

1991-01-01

The critical current density (J c ) of Ag-clad of Bi-Pb-Sr-Ca-Cu-O has been measured to be about 12,000 A/cm 2 at 77 K in zero field. This wire was rolled into a tape of thickness 0.1 mm and width of 2 to 3 mm, and a coil of 35 mm diameter was formed. The J c of this coil was measured to be about 2,000 A/cm 2 at 77 K over the full length (1.00 meter) of the coil. In this paper compositions, heat treatment parameters, and cold-deformation for enhancement of J c are presented. The microstructure is characterized and pinning interactions as well as possible weak links are emphasised. (orig.)

Passivity enhancement by series LC filtered active damper with zero current reference

DEFF Research Database (Denmark)

Bai, Haofeng; Wang, Xiongfei; Blaabjerg, Frede

2016-01-01

can be improved by enhancing the passivity of the total admittance seen by the grid, which allows for a zero current reference and a much simpler current controller for the active damper. To show the performance of the active damper with zero reference, this paper first carries out the impedance based...... stability analysis of grid converters in the weak grid. Based on the impedance model of the series LC filtered active damper, the real part of its output admittance is investigated and shown to be able to enhance the passivity of the admittance of the converters seen by the grid. Finally, simulation...

Superconductivity, critical current density, and flux pinning in MgB2-x(SiC)x/2 superconductor after SiC nanoparticle doping

Science.gov (United States)

Dou, S. X.; Pan, A. V.; Zhou, S.; Ionescu, M.; Wang, X. L.; Horvat, J.; Liu, H. K.; Munroe, P. R.

2003-08-01

We investigated the effect of SiC nanoparticle doping on the crystal lattice structure, critical temperature Tc, critical current density Jc, and flux pinning in MgB2 superconductor. A series of MgB2-x(SiC)x/2 samples with x=0-1.0 were fabricated using an in situ reaction process. The contraction of the lattice and depression of Tc with increasing SiC doping level remained rather small most likely due to the counterbalancing effect of Si and C co-doping. The high level Si and C co-doping allowed the creation of intragrain defects and highly dispersed nanoinclusions within the grains which can act as effective pinning centers for vortices, improving Jc behavior as a function of the applied magnetic field. The enhanced pinning is mainly attributable to the substitution-induced defects and local structure fluctuations within grains. A pinning mechanism is proposed to account for different contributions of different defects in MgB2-x(SiC)x/2 superconductors.

Experiment to measure the effects of biaxial strain on the critical current of NbTi superconductor

International Nuclear Information System (INIS)

Froelich, K.J.

1975-01-01

Twisted multifilament, copper-clad NbTi superconductors have been axially and biaxially strained at 4.2K with a 7.5T background field. A simply-constructed cryogenic loading frame was built and used to strain the conductor. Results on 1.27 mm x 3.13 mm conductor have shown that degradation of less than .3 percent of critical current occurred when the wire was biaxially strained to +3260 μepsilon in the axial direction and -1875 μepsilon in the transverse direction. Degradation approaches 3 percent of critical current at approximately 6000 μepsilon in the axial direction only

Majorana splitting from critical currents in Josephson junctions

Science.gov (United States)

Cayao, Jorge; San-Jose, Pablo; Black-Schaffer, Annica M.; Aguado, Ramón; Prada, Elsa

2017-11-01

A semiconducting nanowire with strong Rashba spin-orbit coupling and coupled to a superconductor can be tuned by an external Zeeman field into a topological phase with Majorana zero modes. Here we theoretically investigate how this exotic topological superconductor phase manifests in Josephson junctions based on such proximitized nanowires. In particular, we focus on critical currents in the short junction limit (LN≪ξ , where LN is the junction length and ξ is the superconducting coherence length) and show that they contain important information about nontrivial topology and Majoranas. This includes signatures of the gap inversion at the topological transition and a unique oscillatory pattern that originates from Majorana interference. Interestingly, this pattern can be modified by tuning the transmission across the junction, thus providing complementary evidence of Majoranas and their energy splittings beyond standard tunnel spectroscopy experiments, while offering further tunability by virtue of the Josephson effect.

Development of Bi-based high critical current density superconducting tapes

International Nuclear Information System (INIS)

Swaminathan, G.

1995-01-01

In order to achieve the aim of developing suitable superconducting materials the main emphasis has to be made in the following areas viz., synthesizing powders, detailed study of sintering and phase conversion process in relation to the critical current density (J c ) on pellets and optimising of tape processing parameters. The bismuth system has been found to be more favourable for making wires and tapes because of its high transition temperature, good stability, does not require oxygen on cooling and is non-toxic. These have been the most convenient properties which made the BiSCO material the most popular one

Transport currents along c-axis and (a,b) planes in YBCO single domain materials. Critical current densities and normal-superconducting transitions

International Nuclear Information System (INIS)

Porcar, L.; Bourgault, D.; Chaud, X.; Noudem, J.G.; Tournier, R.; Tixador, P.

1998-01-01

High transport currents along the (a,b) planes and along the c-axis have been measured in pulsed current of different pseudo-frequencies. Self field losses and transport current of 8000 A (20000 A cm -2 ) have been measured in Y 1 Ba 2 Cu 3 O 7-δ bars textured by the melting zone technique. Critical currents as high as 500 A (90000 A cm -2 ) along the (a,b) planes or 3000 A (7500 A cm -2 ) along the c-axis have been measured. For both orientations, the transition from the normal state to the superconducting state has been observed. Electric field of 1000 V m -1 and study of the superconducting state recovery are reported. (orig.)

Simulations of enhanced reversed shear TFTR discharges with lower hybrid current drive

International Nuclear Information System (INIS)

Kesner, J.; Bateman, G.

1996-01-01

The BALDUR based BBK code permits predictive simulations of time-dependent tokamak discharges and has the capability to include neutral beam heating, pellet injection, bootstrap currents and lower hybrid current drive. BALDUR contains a theory based multi-regime transport model and previous work has shown excellent agreement with both L-mode and supershot TFTR discharges. These simulations reveal that core transport is dominated by η i and trapped electron modes and the outer region by resistive ballooning. We simulate enhanced reverse shear discharges by beginning with a supershot simulation with a reversed shear profile. Similarly to the TFTR experiments the reversed shear profile is obtained through the programming of the current during startup and the freezing in of these profiles by subsequent heating. At the time of transition into the enhanced confinement regime we turn off the η i and trapped-electron mode transport. We examine the further modification of the plasma current profile that can be obtained with the application of lower hybrid current drive. The results of these simulations will be discussed

Current Trends in Developing Medical Students' Critical Thinking Abilities

Directory of Open Access Journals (Sweden)

Peter H. Harasym

2008-07-01

Full Text Available Health care is fallible and prone to diagnostic and management errors. The major categories of diagnostic errors include: (1 no-fault errors—the disease is present but not detected; (2 system errors—a diagnosis is delayed or missed because of the imperfection in the health care system; and (3 cognitive errors—a misdiagnosis from faulty data collection or interpretation, flawed reasoning, or incomplete knowledge. Approximately one third of patient problems are mismanaged because of diagnostic errors. Part of the solution lies in improving the diagnostic skills and critical thinking abilities of physicians as they progress through medical school and residency training. However, this task is challenging since both medical problem-solving and the learning environments are complex and not easily understood. There are many interacting variables including the motivation of the medical student (e.g. deep versus surface learning, the acquisition and evolution of declarative and conditional knowledge (e.g. reduced, dispersed, elaborated, scheme, and scripted, problem-solving strategies (e.g. procedural knowledge—guessing, hypothetical deductive, scheme inductive, and pattern recognition, curricular models (e.g. apprenticeship, discipline-based, body system-based, case-based, clinical presentation-based, teaching strategies (e.g. teaching general to specific or specific to general, the presented learning opportunities (PBL versus scheme inductive PBL, and the nature of the learning environment (e.g. modeling critical thinking and expert problem-solving. This paper elaborates on how novices differ from experts and how novices can be educated in a manner that enhances their level of expertise and diagnostic abilities as they progress through several years of medical training.

Forces of vortice trapping and critical current in type II superconductors

International Nuclear Information System (INIS)

Bormio, C.

1985-12-01

The vortice-centers interactions of trapping in type II superconductor materials were studied by two theories: thermodynamic (Hampshire-Taylor) and microscopic (Larkin - Ovchinnikov). The study was applied to NbTi with composition of 50% weight of Ti. They are commercial cables containing 361 filaments with final diameter of 0.35 mm for the wire and 9.2 μm foi filaments. The material presents high deformation rate in area and high density of dislocations. These defects actuate as centers of trapping. Variations in themomechanical treatments of superconductor cables modify the interaction mechanisms. The specific mechanism for each treatment type was identified. Measurements of critical current density in function of magnetic field in the range from 1 to 7 Tesla were done, which the usual superconductor parameters as upper critical field and Ginzburg - Landau (Kappa-k) parameter are estimated from literature data. (M.C.K.) [pt

Self-field AC losses and critical currents in multi-tube Ag-Bi-2223 conductors

Energy Technology Data Exchange (ETDEWEB)

Ciszek, M; Ashworth, S P; Campbell, A M [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); James, M P; Glowacki, B A [IRC in Superconductivity, University of Cambridge, Madingley Road, Cambridge CB3 0HE (United Kingdom); Department of Materials Science and Metallurgy, University of Cambridge, Pembroke Street, Cambridge CB2 3QZ (United Kingdom); Garre, R; Conti, S [Centro Ricerche Europa Metalli, Fornaci di Barga, LU (Italy)

1996-05-01

The purpose of this work was to investigate the influence of different technological treatments of silver sheathed Bi-2223 tapes on the critical current density and the AC transport losses. The tapes were produced using the 'tube-in-tube' technique, by including a silver rod in the centre of the superconducting powder during packing of the silver tube. The aim of the process is to increase the silver to superconductor surface area and thus also the alignment at the centre of the conductor ceramic core. AC transport losses were measured by means of an electrical method using sinusoidally varying currents in the frequency range 30-180 Hz. In this range the power losses are hysteretic. The measured variation in losses from those predicted by a critical state model is attributed to the complex geometry of superconducting regions existing in these tapes. (author)

Uniaxial Strain Induced Critical Current Degradation of Ag-Sheathed Bi-2212 Round Wire

NARCIS (Netherlands)

Dai, Chao; Qin, Jinggang; Liu, Bo; Liu, Peihang; Wu, Yu; Nijhuis, Arend; Zhou, Chao; Li, Chenshan; Hao, Qingbin; Liu, Sheng

2018-01-01

The critical current degradation of Bi-2212 Ag-sheathed round wire subjected to uniaxial strain was studied at 4.2 K in 14 T background field. The strains applied on the sample are both tension and compression. The additional tensile strain caused by the difference in thermal expansion between the

Application of a combined superconducting fault current limiter and STATCOM to enhancement of power system transient stability

Energy Technology Data Exchange (ETDEWEB)

Mahdad, Belkacem, E-mail: bemahdad@mselab.org; Srairi, K.

2013-12-15

Highlights: •A simple interactive model SFCL–STATCOM Controller is proposed to enhance the transient stability. •The STATCOM controller is integrated in coordination with the SFCL to support the excessive reactive power during fault. •Voltage stability index based continuation power flow is used to locate the STATCOM and the SFCL. •The clearing time improved compared to other cases (with only SFCL, with only STATCOM). •The choice of the STATCOM parameters is very important to exploit efficiently the integration of STATCOM Controller. -- Abstract: Stable and reliable operation of the power system network is dependent on the dynamic equilibrium between energy production and power demand under large disturbance such as short circuit or important line tripping. This paper investigates the use of combined model based superconducting fault current limiter (SFCL) and shunt FACTS Controller (STATCOM) for assessing the transient stability of a power system considering the automatic voltage regulator. The combined model located at a specified branch based on voltage stability index using continuation power flow. The main role of the proposed combined model is to achieve simultaneously a flexible control of reactive power using STATCOM Controller and to reduce fault current using superconducting technology based SFCL. The proposed combined model has been successfully adapted within the transient stability program and applied to enhance the transient power system stability of the WSCC9-Bus system. Critical clearing time (CCT) has been used as an index to evaluate and validate the contribution of the proposed coordinated Controller. Simulation results confirm the effectiveness and perspective of this combined Controller to enhance the dynamic power system performances.

The critical current of point symmetric Josephson tunnel junctions

International Nuclear Information System (INIS)

Monaco, Roberto

2016-01-01

Highlights: • We disclose some geometrical properties of the critical current field dependence that apply to a large class of Josephson junctions characterized by a point symmetric shape. • The developed theory is valid for any orientation of the applied magnetic field, therefore it allows the determine the consequences of field misalignment in the experimental setups. • We also address that the threshold curves of Josephson tunnel junctions with complex shapes can be expressed as a linear combination of the threshold curves of junctions with simpler point symmetric shapes. - Abstract: The physics of Josephson tunnel junctions drastically depends on their geometrical configurations. The shape of the junction determines the specific form of the magnetic-field dependence of its Josephson current. Here we address the magnetic diffraction patterns of specially shaped planar Josephson tunnel junctions in the presence of an in-plane magnetic field of arbitrary orientations. We focus on a wide ensemble of junctions whose shape is invariant under point reflection. We analyze the implications of this type of isometry and derive the threshold curves of junctions whose shape is the union or the relative complement of two point symmetric plane figures.

Critical Current Properties of HTS Twisted Stacked-Tape Cable in Subcooled- and Pressurized-Liquid Nitrogen

International Nuclear Information System (INIS)

Tomita, M; Suzuki, K; Fukumoto, Y; Ishihara, A; Akasaka, T; Kobayashi, Y; Maeda, A; Takayasu, M

2015-01-01

A 2 m length Twisted Stacked-Tape Cable (TSTC) conductor which was fabricated by 32-YBCO-tapes (4 mm width) with a 200 mm twist pitch was investigated at various temperatures near 77 K in subcooled- and pressurized-liquid nitrogen. The critical current of the TSTC cable which was 1.45 kA at 77 K measured from 64 K to 85 K by controlling the equilibrium vapor pressure of nitrogen bath and were varied from 3.65 kA at 64 K to 0.42 kA at 85 K. The temperature dependence of cables’ critical current agrees with that of the 4 mm width YBCO tape. These results are encouraging for applications of a compact Twisted Stacked-Tape Cable application in railway systems. (paper)

Critical current and flux dynamics in Ag-doped FeSe superconductor

Science.gov (United States)

Galluzzi, A.; Polichetti, M.; Buchkov, K.; Nazarova, E.; Mancusi, D.; Pace, S.

2017-02-01

The measurements of DC magnetization as a function of the temperature M(T), magnetic field M(H), and time M(t) have been performed in order to compare the superconducting and pinning properties of an undoped FeSe0.94 sample and a silver doped FeSe0.94 + 6 wt% Ag sample. The M(T) curves indicate an improvement of the superconducting critical temperature and a reduction of the non-superconducting phase Fe7Se8 due to the silver doping. This is confirmed by the field and temperature dependent critical current density Jc(H,T) extracted from the superconducting hysteresis loops at different temperatures within the Bean critical state model. Moreover, the combined analysis of the Jc(T) and of the pinning force Fp(H/Hirr) indicate that the pinning mechanisms in both samples can be described in the framework of the collective pinning theory. The U*(T, J) curves show a pinning crossover from an elastic creep regime of intermediate size flux bundles, for low temperatures, to a plastic creep regime at higher temperatures for both the samples. Finally, the vortex hopping attempt time has been evaluated for both samples and the results are comparable with the values reported in the literature for high Tc materials.

SCALE Graphical Developments for Improved Criticality Safety Analyses

International Nuclear Information System (INIS)

Barnett, D.L.; Bowman, S.M.; Horwedel, J.E.; Petrie, L.M.

1999-01-01

New computer graphic developments at Oak Ridge National Ridge National Laboratory (ORNL) are being used to provide visualization of criticality safety models and calculational results as well as tools for criticality safety analysis input preparation. The purpose of this paper is to present the status of current development efforts to continue to enhance the SCALE (Standardized Computer Analyses for Licensing Evaluations) computer software system. Applications for criticality safety analysis in the areas of 3-D model visualization, input preparation and execution via a graphical user interface (GUI), and two-dimensional (2-D) plotting of results are discussed

Enhancing students’ critical thinking skills through critical thinking assessment in calculus course

Science.gov (United States)

Zulfaneti; Edriati, S.; Mukhni

2018-01-01

This study aims to determine the development of students’ critical thinking skills through the implementation of critical thinking instruments in Calculus lectures. The instruments consist of observation sheets, critical thinking test, self-assessment, peer assessment and portfolio. The research was a qualitative research; with the participants were 53 first-year students who take Integral Calculus in Mathematics Education Department STKIP PGRI Sumatera Barat representing high-ability students, medium and low. The data in this study were collected by tests, interviews, observations and field notes. Data were analyzed descriptively; data reduction, data presentation, and conclusions. For testing the validity of data, it was used credibility test data by increasing persistence and triangulation. The results showed that in high-level students there is a change of ability from Critical enough to be Very Critical, in the students with moderate and low ability there is a change of ability from Uncritical to Critical. So it can be concluded that the assessment instruments have a good contribution and can improve the ability of critical thinking.

Controlled enhancement of spin-current emission by three-magnon splitting.

Science.gov (United States)

Kurebayashi, Hidekazu; Dzyapko, Oleksandr; Demidov, Vladislav E; Fang, Dong; Ferguson, A J; Demokritov, Sergej O

2011-07-03

Spin currents--the flow of angular momentum without the simultaneous transfer of electrical charge--play an enabling role in the field of spintronics. Unlike the charge current, the spin current is not a conservative quantity within the conduction carrier system. This is due to the presence of the spin-orbit interaction that couples the spin of the carriers to angular momentum in the lattice. This spin-lattice coupling acts also as the source of damping in magnetic materials, where the precessing magnetic moment experiences a torque towards its equilibrium orientation; the excess angular momentum in the magnetic subsystem flows into the lattice. Here we show that this flow can be reversed by the three-magnon splitting process and experimentally achieve the enhancement of the spin current emitted by the interacting spin waves. This mechanism triggers angular momentum transfer from the lattice to the magnetic subsystem and modifies the spin-current emission. The finding illustrates the importance of magnon-magnon interactions for developing spin-current based electronics.

Relation of n-value to critical current for local sections and overall sample in a SmBCO coated conductor pulled in tension

International Nuclear Information System (INIS)

Ochiai, Shojiro; Okuda, Hiroshi; Nagano, Shinji; Sugano, Michinaka; Oh, Sang-Song; Ha, Hong-Soo; Osamura, Kozo

2014-01-01

Under application of tensile stress to a SmBCO (SmBa 2 Cu 3 O 7-δ ) coated conductor sample consisting of series electric circuit of local sections, the relation of voltage-current curve, critical current and n-value of the sections to those of overall sample was studied. The change in critical current and n-value with increasing applied stress was different from section to section due to the difference in damage behavior of the SmBCO layer among the sections. When the difference in extent of damage among the sections was small, the voltages developed in all sections contributed to the voltage of overall sample. In this case, the critical current and n-value of overall sample were within the range of the highest and lowest values among the sections. On the other hand, when the damage in one section was far severer than that of other sections, the voltage developed in the most severely damaged section largely contributed to the overall voltage, and hence the voltage-current curves of the most severely damaged section were almost the same as those of overall sample. In this case, critical current of the overall sample was slightly higher and n-value of the overall sample was lower than the critical current and n-value of the most severely damaged section. Accordingly, the decrease in n-value with decreasing critical current in overall sample was sharper than that in sections. This phenomenon was accounted for by the increase in shunting current at cracked part at higher voltage in the most severely damaged section. (author)

Metal-enhanced luminescence: Current trend and future perspectives- A review

International Nuclear Information System (INIS)

Ranjan, Rajeev; Esimbekova, Elena N.; Kirillova, Maria A.; Kratasyuk, Valentina A.

2017-01-01

Optically enhanced biosensing strategies are prerequisites for developing miniature and highly sensitive multiplexed analytical platforms. Such smart biosensing systems are highly promising for use in the fields of biomedicine and environmental monitoring. Optical signal enhancement during bioassays is attributed to the complex opto-electronic interactions of incoming photonic signals at the nanomaterial interface. Research on the use of metals other than gold and silver for such purposes tends to extend the spectral window to observe luminescence enhancement effects. Such manifold increase in luminescence may be explained by the principles of plasmon coupling, directional emission led high collection efficiency, Rayleigh scattering and related opto-electronic events. The present review begins with a mechanistic description of important phenomena associated with metal-induced luminescence enhancement, particularly focusing on the origin of metal-enhanced luminescence. This review further analyses the hybrid nanostructure capabilities responsible for maintaining unique opto-electronic properties during bio-functionalisation. Current research trends in this area, future scope of this field for designing useful bioassays and concluding remarks are then discussed. - Highlights: • Nanomaterials significantly differ from their bulk counterparts. • Strong and pronounced photophysical effects at the metal surface provide opportunities for designing novel biosensors. • Metal-enhanced luminescence increases the quantum yield of luminescent reactions. • Under optimal conditions, plasmon coupling enhances the optical effects at the nanometal surface.

Metal-enhanced luminescence: Current trend and future perspectives- A review

Energy Technology Data Exchange (ETDEWEB)

Ranjan, Rajeev [Laboratory of Bioluminescent Biotechnologies, Department of Biophysics, Institute of Fundamental Biology and Biotechnology, Siberian Federal University, 79 Svobodny Prospect, Krasnoyarsk 660041 (Russian Federation); Esimbekova, Elena N., E-mail: esimbekova@yandex.ru [Laboratory of Bioluminescent Biotechnologies, Department of Biophysics, Institute of Fundamental Biology and Biotechnology, Siberian Federal University, 79 Svobodny Prospect, Krasnoyarsk 660041 (Russian Federation); Institute of Biophysics SB RAS, Federal Research Center “Krasnoyarsk Science Center SB RAS”, Akademgorodok 50/50, Krasnoyarsk 660036 (Russian Federation); Kirillova, Maria A. [Laboratory of Bioluminescent Biotechnologies, Department of Biophysics, Institute of Fundamental Biology and Biotechnology, Siberian Federal University, 79 Svobodny Prospect, Krasnoyarsk 660041 (Russian Federation); Kratasyuk, Valentina A. [Laboratory of Bioluminescent Biotechnologies, Department of Biophysics, Institute of Fundamental Biology and Biotechnology, Siberian Federal University, 79 Svobodny Prospect, Krasnoyarsk 660041 (Russian Federation); Institute of Biophysics SB RAS, Federal Research Center “Krasnoyarsk Science Center SB RAS”, Akademgorodok 50/50, Krasnoyarsk 660036 (Russian Federation)

2017-06-08

Optically enhanced biosensing strategies are prerequisites for developing miniature and highly sensitive multiplexed analytical platforms. Such smart biosensing systems are highly promising for use in the fields of biomedicine and environmental monitoring. Optical signal enhancement during bioassays is attributed to the complex opto-electronic interactions of incoming photonic signals at the nanomaterial interface. Research on the use of metals other than gold and silver for such purposes tends to extend the spectral window to observe luminescence enhancement effects. Such manifold increase in luminescence may be explained by the principles of plasmon coupling, directional emission led high collection efficiency, Rayleigh scattering and related opto-electronic events. The present review begins with a mechanistic description of important phenomena associated with metal-induced luminescence enhancement, particularly focusing on the origin of metal-enhanced luminescence. This review further analyses the hybrid nanostructure capabilities responsible for maintaining unique opto-electronic properties during bio-functionalisation. Current research trends in this area, future scope of this field for designing useful bioassays and concluding remarks are then discussed. - Highlights: • Nanomaterials significantly differ from their bulk counterparts. • Strong and pronounced photophysical effects at the metal surface provide opportunities for designing novel biosensors. • Metal-enhanced luminescence increases the quantum yield of luminescent reactions. • Under optimal conditions, plasmon coupling enhances the optical effects at the nanometal surface.

Critical currents and energy dissipation in Y1Ba2Cu3O7-δ films

International Nuclear Information System (INIS)

Windte, C.V.

1993-09-01

The critical current density j c of patterned YBaCuO thin film samples and the electric field E seen by the superconductor were calculated from data of magnetization loops, external magnetic field sweeps and relaxation, respectively. Data were taken at 77 K up to external magnetic fields of 150 mT with a sensitive Hall probe detecting the magnetic fields of the screening currents of the sample. The E(j) characteristic could be determined over six decades of magnitude of E (10 -7 μV/cm -1 μV/cm). These characteristics permit the comparison with theoretical pictures: They are incompatible with Kim-Andersons flux-creep and a power law behaviour. The characteristics are compatible with the vortex-glass or the collective pinning ansatz. There exists a limiting critical current beyond no known theoretical picture describes the E(j) characteristic. (orig.) [de

Critical current, pinning and resistive state of superconducting single-crystal niobium with different types of defect structure

International Nuclear Information System (INIS)

Sokolenko, V.I.; Starodubov, Ya.D.

2005-01-01

Critical current pinning and resistive state of single crystal niobium of texture orientation are studied for different structural states obtained by rolling at 20 K by 42% and polishing the surface layers. It is found that the heterogeneous structures typical of the strained sample even after its thinning down to approx 10% display a lower current-carrying capability due to an increase of the thermomagnetic instability within the fragmented structure sections in the near-surface layers. For a homogeneous defect structure of the sample core with the density of equilibrium distributed dislocations of 1.3 centre dot 10 11 cm -2 , a correlation between the normal current density and the critical current density in the resistive state is found, in agreement with the concepts of flux creep due to the scatter of local values of J c

Improvements in the critical current densities of Nb3Sn by solid solution additions of Sn in Nb

International Nuclear Information System (INIS)

Luhman, T.; Suenaga, M.

1975-01-01

The effectiveness of solid solution additions of Sn to Nb in improving the superconducting properties of diffusion processed Nb 3 Sn conductors was examined. It was found that an increase in the superconducting critical current density, Jc, as function of layer thickness (d) may be obtained for thick Nb 3 Sn layers by solid solution additions of Sn in Nb. A large increase in J/sub c/ (d) is also achieved by increasing the Sn content in the bronze matrix material. In addition to uses of this material in magnet fabrications a potential application of these improved J/sub c/(d) values may lie in the use of Nb 3 Sn in power transmission lines. Here, a high superconducting critical current density is necessary throughout the material to carry the increased current during fault conditions. The magnetic field dependence of J/sub c/ is a function of alloy content but the alloying changes studied here do not increase the high field critical current capability of Nb 3 Sn. (auth)

Enhanced magnetocaloric properties and critical behavior of (Fe0.72Cr0.28)3Al alloys for near room temperature cooling

Science.gov (United States)

Sharma, V.; Maheshwar Repaka, D. V.; Chaudhary, V.; Ramanujan, R. V.

2017-04-01

Magnetic cooling is an environmentally friendly, energy efficient, thermal management technology relying on high performance magnetocaloric materials (MCM). Current research has focused on low cost, corrosion resistant, rare earth (RE) free MCMs. We report the structural and magnetocaloric properties of novel, low cost, RE free, iron based (Fe0.72Cr0.28)3Al alloys. The arc melted buttons and melt spun ribbons possessed the L21 crystal structure and B2 crystal structure, respectively. A notable enhancement of 33% in isothermal entropy change (-ΔS m) and 25% increase in relative cooling power (RCP) for the ribbons compared to the buttons can be attributed to higher structural disorder in the Fe-Cr and Fe-Al sub-lattices of the B2 structure. The critical behavior was investigated using modified Arrott plots, the Kouvel-Fisher plot and the critical isotherm technique; the critical exponents were found to correspond to the short-range order 3D Heisenberg model. The field and temperature dependent magnetization curves of (Fe0.72Cr0.28)3Al alloys revealed their soft magnetic nature with negligible hysteresis. Thus, these alloys possess promising performance attributes for near room temperature magnetic cooling applications.

Individual and collective processes in the construction of the self: self-enhancement in the United States and self-criticism in Japan.

Science.gov (United States)

Kitayama, S; Markus, H R; Matsumoto, H; Norasakkunkit, V

1997-06-01

A collective constructionist theory of the self proposes that many psychological processes, including enhancement of the self (pervasive in the United States) and criticism and subsequent improvement of the self (widespread in Japan), result from and support the very ways in which social acts and situations are collectively defined and subjectively experienced in the respective cultural contexts. In support of the theory, 2 studies showed, first, that American situations are relatively conducive to self-enhancement and American people are relatively likely to engage in self-enhancement and, second, that Japanese situations are relatively conducive to self-criticism and Japanese people are relatively likely to engage in self-criticism. Implications are discussed for the collective construction of psychological processes implicated in the self and, more generally, for the mutual constitution of culture and the self.

Dislocation structure, aging processes and critical currents of vanadium-gallium alloys

International Nuclear Information System (INIS)

Pan, V.M.; Beletskii, Yu.I.; Flis, V.S.; Firstov, S.A.; Sarzhan, G.F.

1976-04-01

An electron microscopical investigation of the structural and phase changes in vanadium-gallium alloys was carried out in the range of concentrations corresponding to a supersaturated mixed crystal with bcc lattice during plastic deformation and annealing. The determined data were compared with the measured results of the electrophysical and superconducting properties. It was shown that the deformed and aged vanadium-gallium samples at 4.2 K could conduct a dissipation-free transport current with a density of 8 x 10 3 A/cm 2 in the transversal magnetic field of 60 kOe. Based on the experimental results of the dislocation structure, the mechanism and kinetics of the separation process, conclusions were drawn as to the character of the exceeding of the critical current density in the presence of a magnetic field in these compounds. (orig.) [de

Uranium doping and neutron irradiation of Bi-2223 superconduction tapes for improved critical current density

International Nuclear Information System (INIS)

Moss, S.D.; Wang, W.G.; Dou, S.X.; Weinstein, R.

1998-01-01

It is demonstrated that a combination of neutron irradiation with uranium doping introduce fission tracks through a Bi-2223 tape which act as effective pinning centres, leading to a substantial increase in critical current. Preliminary data suggests that the combination of uranium doping and neutron irradiation produces improved flux pinning in Bi-2223 tapes over neutron irradiation alone. Before irradiation, SEM, DTA and XRD analyses were performed on the tapes. Both before and after irradiation the trapped maximum magnetic flux was measured at 77K. Before neutron irradiation, uranium doping has no effect on critical current. Preliminary SEM data suggested that the uranium is homogeneously distributed throughout the oxide core of the tape. The presence of 2212 and other secondary phases in the doped tapes suggest further refinement of the sintering procedure is necessary. (authors)

A Teacher Action Research Study: Enhancing Student Critical Thinking Knowledge, Skills, Dispositions, Application and Transfer in a Higher Education Technology Course

Science.gov (United States)

Phelan, Jack Gordon

2012-01-01

This study examined the effects of a critical thinking instructional intervention in a higher education technology course with the purpose of determining the extent to which the intervention enhanced student critical thinking knowledge, skills, dispositions, application and transfer abilities. Historically, critical thinking has been considered…

Critical current densities amd pinning mechanisms of high-Tc films on single crystalline and technologically relevant substrates. Final report

International Nuclear Information System (INIS)

Adrian, H.

1995-12-01

The report deals with six project tasks: (1) Effects of impurity additions at atomic level on the pinning behaviour and the critical current densities, examined in epitactic YBA 2 (Cu 1-x Ni x ) 3 O 7 films. It could be proven that the Ni atoms increase the activation energy for flux movement and the critical current density in a concentration range of 0 2 Sr 2 Ca n-1 Cu n O 2n+4+δ films (n = 2 and 3) with good crystalline properties, high critical currents, and high current densities were prepared. Thin YBa 2 Cu 3 O 7 films of high quality could be grown on saphire substrates, both by the MO-CVD process and by MBE. The aim of depositing biaxially textured YBa 2 Cu 3 O 7 films with high critical current densities on polycrystalline, metallic substrates was achieved by the IBAD process combined with MBE. The buffer layer was YSZ. Heterostructures of the layer sequence YBa 2 Cu 3 O 7 /CeO 2 /Y 0.3 Pr 0.7 Ba 2 Cu 3 O 7 /YBa 2 Cu 3 O 7 and YBa 2 Cu 3 O 7 /CeO 2 /Au were prepared by laser ablation and sputtering processes, in order to examine Josephson ramp contacts and superconducting field-effect transistors. (orig./MM) [de

Plasma position and current control system enhancements for the JET ITER-like wall

Energy Technology Data Exchange (ETDEWEB)

De Tommasi, G. [Associazione EURATOM-ENEA-CREATE, Univ. di Napoli Federico II, Via Claudio 21, 80125 Napoli (Italy); Maviglia, F. [Associazione EURATOM-ENEA-CREATE, Via Claudio 21, 80125 Napoli (Italy); Neto, A.C. [Ass. EURATOM-IST, Instituto de Plasmas e Fusão Nuclear, IST, 1049-001 Lisboa (Portugal); Lomas, P.J.; McCullen, P.; Rimini, F.G. [Euratom-CCFE, Culham Science Centre, OX14 3DB Abingdon (United Kingdom)

2014-03-15

Highlights: • JET plasma position and current control system enhanced for the JET ITER like wall. • Vertical stabilization system enhanced to speed up its response and to withstand larger perturbations. • Improved termination management system. • Implementation of the current limit avoidance system. • Implementation of PFX-on-early-task. - Abstract: The upgrade of Joint European Torus (JET) to a new all-metal wall, the so-called ITER-like wall (ILW), has posed a set of new challenges regarding both machine operation and protection. The plasma position and current control (PPCC) system plays a crucial role in minimizing the possibility that the plasma could permanently damage the ILW. The installation of the ILW has driven a number of upgrades of the two PPCC components, namely the Vertical Stabilization (VS) system and the Shape Controller (SC). The VS system has been enhanced in order to speed up its response and to withstand larger perturbations. The SC upgrade includes three new features: an improved termination management system, the current limit avoidance system, and the PFX-on-early-task. This paper describes the PPCC upgrades listed above, focusing on the implementation issues and on the experimental results achieved during the 2011–12 JET experimental campaigns.

An exponential scaling law for the strain dependence of the Nb3Sn critical current density

International Nuclear Information System (INIS)

Bordini, B; Alknes, P; Bottura, L; Rossi, L; Valentinis, D

2013-01-01

The critical current density of the Nb 3 Sn superconductor is strongly dependent on the strain applied to the material. In order to investigate this dependence, it is a common practice to measure the critical current of Nb 3 Sn strands for different values of applied axial strain. In the literature, several models have been proposed to describe these experimental data in the reversible strain region. All these models are capable of fitting the measurement results in the strain region where data are collected, but tend to predict unphysical trends outside the range of data, and especially for large strain values. In this paper we present a model of a new strain function, together with the results obtained by applying the new scaling law on relevant datasets. The data analyzed consisted of the critical current measurements at 4.2 K that were carried out under applied axial strain at Durham University and the University of Geneva on different strand types. With respect to the previous models proposed, the new scaling function does not present problems at large strain values, has a lower number of fitting parameters (only two instead of three or four), and is very stable, so that, starting from few experimental points, it can estimate quite accurately the strand behavior in a strain region where there are no data. A relationship is shown between the proposed strain function and the elastic strain energy, and an analogy is drawn with the exponential form of the McMillan equation for the critical temperature. (paper)

Does mindfulness enhance critical thinking? Evidence for the mediating effects of executive functioning in the relationship between mindfulness and critical thinking

Directory of Open Access Journals (Sweden)

Chris eNoone

2016-01-01

Full Text Available Mindfulness originated in the Buddhist tradition as a way of cultivating clarity of thought. Despite the fact that this behaviour is best captured using critical thinking assessments, no studies have examined the effects of mindfulness on critical thinking or the mechanisms underlying any such possible relationship. Even so, mindfulness has been suggested as being beneficial for critical thinking in higher education. Critical thinking is recognised as an important higher-order cognitive process which involves the ability to analyse and evaluate evidence and arguments. Such non-automatic, reflective responses generally require the engagement of executive functioning which includes updating, inhibition and shifting of representations in working memory. Based on research showing that mindfulness enhances aspects of executive functioning and certain higher-order cognitive processes, we hypothesised that individuals higher in facets of dispositional mindfulness would demonstrate greater critical thinking performance, and that this relationship would be mediated by executive functioning. Cross-sectional assessment of these constructs in a sample of 178 university students was achieved using the observing and non-reactivity sub-scales of the Five Factor Mindfulness Questionnaire, a battery of executive functioning tasks and the Halpern Critical Thinking Assessment. Our hypotheses were tested by constructing a multiple meditation model which was analysed using Structural Equation Modelling. Evidence was found for inhibition mediating the relationships between both observing and non-reactivity and critical thinking in different ways. Indirect-only (or full mediation was demonstrated for the relationship between observing, inhibition and critical thinking. Competitive mediation was demonstrated for the relationship between non-reactivity, inhibition and critical thinking. This suggests additional mediators of the relationship between non-reactivity and

Critical current density of MgB2 thin films and the effect of interface pinning

International Nuclear Information System (INIS)

Choi, Eun-Mi; Gupta, S K; Sen, Shashwati; Lee, Hyun-Sook; Kim, Hyun-Jung; Lee, Sung-Ik

2004-01-01

Preferentially oriented MgB 2 thin films with c-axis normal to the surface have been prepared and characterized for microstructure and transport properties. The magnetic field dependence of superconducting critical current density J c has been determined from the magnetization hysteresis (M-H) loops at various temperatures using the Bean's critical state model. High J c of these films show their potential for applications. We have also measured the angular dependences of J c . The angular dependence is seen to be in agreement with the anisotropic Ginzburg-Landau model except that at angles close to the ab plane, increased pinning due to film-substrate interaction is observed. The angular range where interface pinning is effective has been determined by measurement of asymmetry in dissipation on reversal of current for fields applied at angles close to the ab plane

Analysis of the ac SQUID with low inductance and low critical current

DEFF Research Database (Denmark)

Sørensen, O. H.

1976-01-01

The properties of the ac SQUID magnetometer has been analyzed. The results are valid in the low-inductance low-critical-current regime, where the Lri0 producted is belowthe value at which the relation between the enclosed and externally applied magnetic dc flux becomes reentrant. The effects...... of the screening current circulating in the SQUID ring as well as of the SQUID-ring time constant, tau-Lr/R9 are taken into account. Here LR IS THE SQUID-ring inductance, and R is the shunt resistance in the shunted junction model assumed to describe the weak link. It is shown that for finite values of omegatau...... constriuctively with the result that the optimal response occurs at a definite and finite value of omegatau. If omegatau is increased beyond this optimal value the weak link behavior is dominated by the Ohmic current channel implying that only if the shunt conductance contains a term depending...

Enhanced optical spin current injection in the hexagonal lattice with intrinsic and Rashba spin–orbit interactions

Energy Technology Data Exchange (ETDEWEB)

Zou, Jianfei, E-mail: zoujianfei@hhu.edu.cn; Tang, Chunmei; Zhang, Aimei

2017-04-04

We study the photo-induced spin current injection in a hexagonal lattice with both intrinsic and Rashba spin–orbit interactions which is irradiated by a polarized light beam. It is found that the spin current injection rate could be enhanced as the graphene lattice is in the topological insulator state. Furthermore, the spin current injection rate could be remarkably modulated by the degree of polarization of light and its frequency. - Highlights: • The optical spin current could be enhanced by the intrinsic spin–orbit interaction. • The optical spin current could be modulated by the degree of polarization of light. • The maximum of the spin current injection rate is obtained.

[Team approaches to critical bleeding (massive bleeding and transfusion) - chairmen's introductory remarks. Questionnaire survey on current status of hospital clinical laboratories evaluating critical hemorrhage].

Science.gov (United States)

Kino, Shuichi; Suwabe, Akira

2014-12-01

In 2007, "the Guidelines for Actions against Intraoperative Critical Hemorrhage" were established by the Japanese Society of Anaesthesiologists and the Japanese Society of Blood transfusion and Cell Therapy. The documentation of in-hospital procedures for critical hemorrhage, especially about how to select RBC units, has widely standardized hospital practice. Patients with intraoperative critical hemorrhage sometimes suffer from massive blood loss. In this situation, some patients develop coagulopathy. To treat them, we need to evaluate their coagulation status based on laboratory test results. So, we performed a nationwide questionnaire survey on the current status of hospital clinical laboratories evaluating critical hemorrhage. From the results of this survey, it was recommended that central hospital laboratories should try to reduce the turn-around time required to test for coagulation parameters as much as possible for appropriate substitution therapy. (Review).

Significantly enhanced critical current density in nano-MgB2 grains rapidly formed at low temperature with homogeneous carbon doping

Science.gov (United States)

Liu, Yongchang; Lan, Feng; Ma, Zongqing; Chen, Ning; Li, Huijun; Barua, Shaon; Patel, Dipak; Shahriar, M.; Hossain, Al; Acar, S.; Kim, Jung Ho; Xue Dou, Shi

2015-05-01

High performance MgB2 bulks using carbon-coated amorphous boron as a boron precursor were fabricated by Cu-activated sintering at low temperature (600 °C, below the Mg melting point). Dense nano-MgB2 grains with a high level of homogeneous carbon doping were formed in these MgB2 samples. This type of microstructure can provide a stronger flux pinning force, together with depressed volatility and oxidation of Mg owing to the low-temperature Cu-activated sintering, leading to a significant improvement of critical current density (Jc) in the as-prepared samples. In particular, the value of Jc for the carbon-coated (Mg1.1B2)Cu0.05 sample prepared here is even above 1 × 105 A cm-2 at 20 K, 2 T. The results herein suggest that the combination of low-temperature Cu-activated sintering and employment of carbon-coated amorphous boron as a precursor could be a promising technique for the industrial production of practical MgB2 bulks or wires with excellent Jc, as the carbon-coated amorphous boron powder can be produced commercially at low cost, while the addition of Cu is very convenient and inexpensive.

Low noise signal-to-noise ratio enhancing readout circuit for current-mediated active pixel sensors

International Nuclear Information System (INIS)

Ottaviani, Tony; Karim, Karim S.; Nathan, Arokia; Rowlands, John A.

2006-01-01

Diagnostic digital fluoroscopic applications continuously expose patients to low doses of x-ray radiation, posing a challenge to both the digital imaging pixel and readout electronics when amplifying small signal x-ray inputs. Traditional switch-based amorphous silicon imaging solutions, for instance, have produced poor signal-to-noise ratios (SNRs) at low exposure levels owing to noise sources from the pixel readout circuitry. Current-mediated amorphous silicon pixels are an improvement over conventional pixel amplifiers with an enhanced SNR across the same low-exposure range, but whose output also becomes nonlinear with increasing dosage. A low-noise SNR enhancing readout circuit has been developed that enhances the charge gain of the current-mediated active pixel sensor (C-APS). The solution takes advantage of the current-mediated approach, primarily integrating the signal input at the desired frequency necessary for large-area imaging, while adding minimal noise to the signal readout. Experimental data indicates that the readout circuit can detect pixel outputs over a large bandwidth suitable for real-time digital diagnostic x-ray fluoroscopy. Results from hardware testing indicate that the minimum achievable C-APS output current that can be discerned at the digital fluoroscopic output from the enhanced SNR readout circuit is 0.341 nA. The results serve to highlight the applicability of amorphous silicon current-mediated pixel amplifiers for large-area flat panel x-ray imagers

Effects of oxygen content on the pinning energy and critical current in the granular (Hg, Re)-1223 superconductors

International Nuclear Information System (INIS)

Passos, C.A.C.; Orlando, M.T.D.; Fernandes, A.A.R.; Oliveira, F.D.C.; Simonetti, D.S.L.; Fardin, J.F.; Belich, H.; Ferreira, M.M.

2005-01-01

Hg 0.82 Re 0.18 Ba 2 Ca 2 Cu 3 O 8+d polycrystalline samples, with different oxygen content, were investigated by ac resistance measurements under different applied magnetic field (up to 3 A/m) and critical current measurements. The intergrain and intragrain regions have shown an improvement in the pinning energy and critical current density, as considering the precursor preparation with 10% of O 2 and 90% of Ar (optimal doped). In addition, the samples presented S-I-S junctions type as considering Ambegaokar-Baratoff theory

Critical current degradation of short YBa2Cu3O7-δ coated conductor due to an unprotected quench

International Nuclear Information System (INIS)

Wang, X; Trociewitz, U P; Schwartz, J

2011-01-01

The critical current of a short YBa 2 Cu 3 O 7-δ (YBCO) coated conductor sample degrades in an unprotected quench performed in a nearly adiabatic environment at 30 K. The conductor has Cu stabilizers on both surfaces. The quench is initiated by a heater attached to the sample surface. The amplitude of the transport current is fixed as 91% of the sample's initial critical current. The duration of the current is increased to simulate an unprotected quench and to reach increasing and controlled voltage and temperature levels. A peak temperature of 490 ± 50 K and a heating rate of 1800 K s -1 are measured when the critical current degrades by ∼ 5%. The applied thermal strain on the YBCO layer from 30 to 490 K is estimated to be 0.31% and is applied at a strain rate of ∼ 1% s -1 . The rate of temperature change and the time to reach a certain peak temperature, determined by the current density in the Cu stabilizer, are estimated assuming adiabatic conditions based on the short sample case. For a Cu stabilizer current density ranging from 1000 to 2000 A mm -2 , achieved in commercial conductors currently available, the quench detection and protection requires a response time -2 may challenge the existing detection and protection techniques for the same 200 K limit. Integrating the substrate as part of the stabilizer may help reduce the stabilizer current density to gain more time for quench detection and protection while maintaining the engineering current density.

Maximum Bandwidth Enhancement of Current Mirror using Series-Resistor and Dynamic Body Bias Technique

Directory of Open Access Journals (Sweden)

V. Niranjan

2014-09-01

Full Text Available This paper introduces a new approach for enhancing the bandwidth of a low voltage CMOS current mirror. The proposed approach is based on utilizing body effect in a MOS transistor by connecting its gate and bulk terminals together for signal input. This results in boosting the effective transconductance of MOS transistor along with reduction of the threshold voltage. The proposed approach does not affect the DC gain of the current mirror. We demonstrate that the proposed approach features compatibility with widely used series-resistor technique for enhancing the current mirror bandwidth and both techniques have been employed simultaneously for maximum bandwidth enhancement. An important consequence of using both techniques simultaneously is the reduction of the series-resistor value for achieving the same bandwidth. This reduction in value is very attractive because a smaller resistor results in smaller chip area and less noise. PSpice simulation results using 180 nm CMOS technology from TSMC are included to prove the unique results. The proposed current mirror operates at 1Volt consuming only 102 µW and maximum bandwidth extension ratio of 1.85 has been obtained using the proposed approach. Simulation results are in good agreement with analytical predictions.

Limits to the critical transport current in superconducting (Bi,Pb)2Sr2Ca2Cu3O10 silver-sheathed tapes: The railway-switch model

International Nuclear Information System (INIS)

Hensel, B.; Grasso, G.; Fluekiger, R.

1995-01-01

We have proposed the ''railway-switch'' model to describe the superconducting transport current in (Bi,Pb) 2 Sr 2 Ca 2 Cu 3 O 10 silver-sheathed tapes. The model assumes that in the textured polycrystalline filament the frequent small-angle c-axis tilt grain boundaries (''railway switches'') constitute strong links for the supercurrent. With the objective to identify the mechanisms that limit the critical-current density in the tapes we present measurements of the transport critical current normal to the tape plane and of the current-transfer length along the tape axis. From I-V curves we obtain the longitudinal critical-current distribution and compare it to the thickness variation of the filament. The experiments have been performed on monofilamentary powder-in-tube samples prepared in long lengths by rolling as the only tape-forming process. For all investigated samples the critical-current density at T=77 K in self-field was in the range j c =20--30 kA/cm 2 . We conclude that the dominant limitation for the transport critical current in the tapes is imposed by the low intragrain critical-current density j c c along the c axis (as compared to the in-plane critical-current density j c ab ) and by the even lower critical-current density j c t across twist boundaries or intergrowths. Possibilities for an improvement of the performance of the (Bi,Pb) 2 Sr 2 Ca 2 Cu 3 O 10 silver-sheathed tapes are discussed

Current clinical nutrition practices in critically ill patients in Latin America: a multinational observational study.

Science.gov (United States)

Vallejo, Karin Papapietro; Martínez, Carolina Méndez; Matos Adames, Alfredo A; Fuchs-Tarlovsky, Vanessa; Nogales, Guillermo Carlos Contreras; Paz, Roger Enrique Riofrio; Perman, Mario Ignacio; Correia, Maria Isabel Toulson Davisson; Waitzberg, Dan Linetzky

2017-08-25

Malnutrition in critically ill adults in the intensive care unit (ICU) is associated with a significantly elevated risk of mortality. Adequate nutrition therapy is crucial to optimise outcomes. Currently, there is a paucity of such data in Latin America. Our aims were to characterise current clinical nutrition practices in the ICU setting in Latin America and evaluate whether current practices meet caloric and protein requirements in critically ill patients receiving nutrition therapy. We conducted a cross-sectional, retrospective, observational study in eight Latin American countries (Argentina, Brazil, Chile, Colombia, Ecuador, Mexico, Panama, and Peru). Eligible patients were critically ill adults hospitalised in the ICU and receiving enteral nutrition (EN) and/or parenteral nutrition (PN) on the Screening Day and the previous day (day -1). Caloric and protein balance on day -1, nutritional status, and prescribed nutrition therapy were recorded. Multivariable logistic regression analysis was performed to identify independent predictors of reaching daily caloric and protein targets. The analysis included 1053 patients from 116 hospitals. Evaluation of nutritional status showed that 74.1% of patients had suspected/moderate or severe malnutrition according to the Subjective Global Assessment. Prescribed nutrition therapy included EN alone (79.9%), PN alone (9.4%), and EN + PN (10.7%). Caloric intake met >90% of the daily target in 59.7% of patients on day -1; a caloric deficit was present in 40.3%, with a mean (±SD) daily caloric deficit of -688.8 ± 455.2 kcal. Multivariable logistic regression analysis showed that combined administration of EN + PN was associated with a statistically significant increase in the probability of meeting >90% of daily caloric and protein targets compared with EN alone (odds ratio, 1.56; 95% confidence interval, 1.02-2.39; p = 0.038). In the ICU setting in Latin America, malnutrition was highly prevalent and caloric

Current-enhanced SASE using an optical laser and its application to the LCLS

International Nuclear Information System (INIS)

Zholents, Alexander A.; Fawley, William M.; Emma, Paul; Huang, Zhirong; Reiche, Sven; Stupakov, Gennady

2004-01-01

We propose a significant enhancement of the electron peak current entering a SASE undulator by inducing an energy modulation in an upstream wiggler magnet via resonant interaction with an optical laser, followed by microbunching of the energy-modulated electrons at the accelerator exit. This current enhancement allows a reduction of the FEL gain length. The x-ray output consists of a series of uniformly spaced spikes, each spike being temporally coherent. The duration of this series is controlled by the laser pulse and in principle can be narrowed down to just a single, 200-attosecond spike. Given potentially absolute temporal synchronization of the x-ray spikes to the energy-modulating laser pulse, this scheme naturally makes pump-probe experiments available to SASE FEL's. We also study various detrimental effects related to the high electron peak current

Critical current oscillations in superconductor-ferromagnet-superconductor structure taking into account s-d scattering

International Nuclear Information System (INIS)

Vedyaev, A.V.; Ryzhanova, N.V.; Pugach, N.G.

2007-01-01

One calculated the critical current in the Josephson contact with the transition metal slightly ferromagnetic alloy interlayer. One solved the Gorkov equations taking into account s-d-scattering in a ferromagnet. The account of the mentioned scattering breaking down the Cooper pairs is shown to enable to ensure the conformity with the experiment [ru

Development of high temperature superconductors having high critical current density

International Nuclear Information System (INIS)

Hong, Gye Wong; Kim, C. J.; Lee, H.G.; Kwon, S. C.; Lee, H. J.; Kim, K. B.; Park, J. Y.; Jung, C. H.

2000-08-01

Fabrication of high T c superconductors and its applications for electric power device were carried out for developing superconductor application technologies. High quality YBCO superconductors was fabricated by melt texture growth, top-seeded melt growth process and multi-seeded melt growth process and the properties was compared. The critical current density of the melt processed YBCO superconductors was about few 10,000 A/cm 2 and the levitation force was 50 N. The processing time needed for the growth of the 123 single grain was greatly reduced by applying multi-seeding without no significant degradation of the levitation force. The multi-seeded melt growth process was confirmed as a time-saving and cost-effective method for the fabrication of bulk superconductors with controlled crystallographic orientation

Development of high temperature superconductors having high critical current density

Energy Technology Data Exchange (ETDEWEB)

Hong, Gye Wong; Kim, C. J.; Lee, H.G.; Kwon, S. C.; Lee, H. J.; Kim, K. B.; Park, J. Y.; Jung, C. H

2000-08-01

Fabrication of high T{sub c} superconductors and its applications for electric power device were carried out for developing superconductor application technologies. High quality YBCO superconductors was fabricated by melt texture growth, top-seeded melt growth process and multi-seeded melt growth process and the properties was compared. The critical current density of the melt processed YBCO superconductors was about few 10,000 A/cm{sup 2} and the levitation force was 50 N. The processing time needed for the growth of the 123 single grain was greatly reduced by applying multi-seeding without no significant degradation of the levitation force. The multi-seeded melt growth process was confirmed as a time-saving and cost-effective method for the fabrication of bulk superconductors with controlled crystallographic orientation.

Enhancing Seasonal Water Outlooks: Needs and Opportunities in the Critical Runoff Season

Science.gov (United States)

Ray, A. J.; Barsugli, J. J.; Yocum, H.; Stokes, M.; Miskus, D.

2017-12-01

The runoff season is a critical period for the management of water supply in the western U.S., where in many places over 70% of the annual runoff occurs in the snowmelt period. Managing not only the volume, but the intra-seasonal timing of the runoff is important for optimizing storage, as well as achieving other goals such as mitigating flood risk, and providing peak flows for riparian habitat management, for example, for endangered species. Western river forecast centers produce volume forecasts for western reservoirs that are key input into many water supply decisions, and also short term river forecasts out to 10 days. The early volume forecasts each year typically begin in December, and are updated throughout the winter and into the runoff season (April-July for many areas, but varies). This presentation will discuss opportunities for enhancing this existing suite of RFC water outlooks, including the needs for and potential use for "intraseasonal" products beyond those provided by the Ensemble Streamflow Prediction system and the volume forecasts. While precipitation outlooks have little skill for many areas and seasons, and may not contribute significantly to the outlook, late winter and spring temperature forecasts have meaningful skill in certain areas and sub-seasonal to seasonal time scales. This current skill in CPC temperature outlooks is an opportunity to translate these products into information about the snowpack and potential runoff timing, even where the skill in precipitation is low. Temperature is important for whether precipitation falls as snow or rain, which is critical for streamflow forecasts, especially in the melt season in snowpack-dependent watersheds. There is a need for better outlooks of the evolution of snowpack, conditions influencing the April-July runoff, and the timing of spring peak or shape of the spring hydrograph. The presentation will also discuss a our work with stakeholders of the River Forecast Centers and the NIDIS

INQUIRY –BASED LEARNING FOR ENHANCING CRITICAL THINKING SKILLS: INDONESIAN STUDENTS‘ PERSPECTIVES

Directory of Open Access Journals (Sweden)

Hersulastuti Hersulastuti

2017-12-01

Full Text Available This paper was mainly intended to shed light on students‘ response towards the implementation of Inquiry-Based Learning (IBL in Reading and Writing subject, and explore its benefits for enhancing critical thinking skills from students‘perspectives in ELT context. This research was conducted through a qualitative case study approach. Three students of graduate program were purposively selected to be the participants. Data were gathered primarily from observation notes and interviews, and then further analyzed using interractive model analysis as proposed by Miles & Huberman (1994. The findings demonstrate that students have good responses towards the implementation of IBL. Moreover, IBL is beneficial to make students become more self-directed, selfdisciplined, self-monitored thinkers. Through IBL, students develop their critical thinking abilities: 1 raise vital questions and problems; 2 gather and assess relevant information; 3 drawing well-reasoned conclusions; and 4 communicate effectively with others to seek solution to complex problems.

Enhanced Phase-Shifted Current Control for Harmonic Cancellation in Three-Phase Multiple Adjustable Speed Drive Systems

DEFF Research Database (Denmark)

Yang, Yongheng; Davari, Pooya; Zare, Firuz

2017-01-01

A phase-shifted current control can be employed to mitigate certain harmonics induced by the Diode Rectifiers (DR) and Silicon-Controlled Rectifiers (SCR) as the front-ends of multiple parallel Adjustable Speed Drive (ASD) systems. However, the effectiveness of the phase-shifted control relies...... on the loading condition of each drive unit as well as the number of drives in parallel. In order to enhance the harmonic cancellation by means of the phase-shifted current control, the currents drawn by the rectifiers should be maintained almost at the same level. Thus, this paper firstly analyzes the impact...... of unequal loading among the parallel drives, and a scheme to enhance the performance is introduced to improve the quality of the total grid current, where partial loading operation should be enabled. Simulation and experimental case studies on multidrive systems have demonstrated that the enhanced phase...

Effect of copper additions in tin molten pool on stability temperature and critical current of Nb3Sn

International Nuclear Information System (INIS)

Kruzliak, J.; Hutka, P.; Tomasich, M.

1979-01-01

Tested is the effect of 55 at% copper addition into the tin bath on the stability temperature and crytical current of Nb 3 Sn, prepared by the diffusion method. It is shown that copper presence in the tin bath transfers the stability temperature of NbSn 2 and Nb 6 Sn 5 phases below the annealing temperature of 700 deg C. It results in Nb 3 Sn appearance at the annealing temperatures above 600 deg C. The critical current increase is explained as follows: lower Nb 3 Sn appearance temperatures provide fine-grained structure of superconducting Nb 3 Sn layer with greater density of binning centers and with higher critical current in accordance with NbSn prepared by the diffusion of pure tin into niobium

Enhanced magnetocaloric properties and critical behavior of (Fe0.72Cr0.28)3Al alloys for near room temperature cooling

International Nuclear Information System (INIS)

Sharma, V; Maheshwar Repaka, D V; Chaudhary, V; Ramanujan, R V

2017-01-01

Magnetic cooling is an environmentally friendly, energy efficient, thermal management technology relying on high performance magnetocaloric materials (MCM). Current research has focused on low cost, corrosion resistant, rare earth (RE) free MCMs. We report the structural and magnetocaloric properties of novel, low cost, RE free, iron based (Fe 0.72 Cr 0.28 ) 3 Al alloys. The arc melted buttons and melt spun ribbons possessed the L2 1 crystal structure and B2 crystal structure, respectively. A notable enhancement of 33% in isothermal entropy change (−Δ S m ) and 25% increase in relative cooling power (RCP) for the ribbons compared to the buttons can be attributed to higher structural disorder in the Fe–Cr and Fe–Al sub-lattices of the B2 structure. The critical behavior was investigated using modified Arrott plots, the Kouvel–Fisher plot and the critical isotherm technique; the critical exponents were found to correspond to the short-range order 3D Heisenberg model. The field and temperature dependent magnetization curves of (Fe 0.72 Cr 0.28 ) 3 Al alloys revealed their soft magnetic nature with negligible hysteresis. Thus, these alloys possess promising performance attributes for near room temperature magnetic cooling applications. (paper)

Brain tumor radiosurgery. Current status and strategies to enhance the effect of radiosurgery

International Nuclear Information System (INIS)

Niranjan, A.; Lunsford, L.D.; Gobbel, G.T.; Kondziolka, D.; Maitz, A.; Flickinger, J.C.

2000-01-01

First, the current status of brain tumor radiosurgery is reviewed, and radiosurgery for brain tumors, including benign tumors, malignant tumors, primary glial tumors, and metastatic tumors, is described. Rapid developments in neuroimaging, stereotactic techniques, and robotic technology in the last decade have contributed to improved results and wider applications of radiosurgery. Radiosurgery has become the preferred management modality for many intracranial tumors, including schwannomas, meningiomas, and metastatic tumors. Although radiosurgery provides survival benefits in patients with diffuse malignant brain tumors, cure is still not possible. Microscopic tumor infiltration into surrounding normal tissue is the main cause of recurrence. Additional strategies are needed to specifically target tumor cells. Next, strategies to enhance the effect of radiosurgery are reviewed. Whereas the long-term clinical results of radiosurgery have established its role in the treatment of benign tumors, additional strategies are needed to improve cell killing in malignant brain tumors and to protect normal surrounding brain. The first strategy included the use of various agents to protect normal brain while delivering a high dose to the tumor cells, but finding an effective radioprotective agent has been problematic. Pentobarbital and 21-aminosteroid (21-AS) are presented as examples. The second strategy for radiation protection aimed at the repair of radiation-induced damage to the normal brain. The cause of radiation-induced breakdown of normal tissue is unclear. The white matter and the cerebral vasculature appear to be particularly susceptible to radiation. Oligodendrocytes and endothelial cells may be critical targets of radiation. The authors hypothesize that radiation-induced damage to these cell types can be repaired by neural stem cells. They also describe the use of tumor necrosis factor alpha (TNF-alpha) and neural stem cells as a means of enhancing the effect of

Importance of critical micellar concentration for the prediction of solubility enhancement in biorelevant media.

Science.gov (United States)

Ottaviani, G; Wendelspiess, S; Alvarez-Sánchez, R

2015-04-06

This study evaluated if the intrinsic surface properties of compounds are related to the solubility enhancement (SE) typically observed in biorelevant media like fasted state simulated intestinal fluids (FaSSIF). The solubility of 51 chemically diverse compounds was measured in FaSSIF and in phosphate buffer and the surface activity parameters were determined. This study showed that the compound critical micellar concentration parameter (CMC) correlates strongly with the solubility enhancement (SE) observed in FaSSIF compared to phosphate buffer. Thus, the intrinsic capacity of molecules to form micelles is also a determinant for each compound's affinity to the micelles of biorelevant surfactants. CMC correlated better with SE than lipophilicity (logD), especially over the logD range typically covered by drugs (2 < logD < 4). CMC can become useful to guide drug discovery scientists to better diagnose, improve, and predict solubility in biorelevant media, thereby enhancing oral bioavailability of drug candidates.

The critical particle size for enhancing thermal conductivity in metal nanoparticle-polymer composites

Science.gov (United States)

Lu, Zexi; Wang, Yan; Ruan, Xiulin

2018-02-01

Polymers used as thermal interface materials are often filled with high-thermal conductivity particles to enhance the thermal performance. Here, we have combined molecular dynamics and the two-temperature model in 1D to investigate the impact of the metal filler size on the overall thermal conductivity. A critical particle size has been identified above which thermal conductivity enhancement can be achieved, caused by the interplay between high particle thermal conductivity and the added electron-phonon and phonon-phonon thermal boundary resistance brought by the particle fillers. Calculations on the SAM/Au/SAM (self-assembly-monolayer) system show a critical thickness Lc of around 10.8 nm. Based on the results, we define an effective thermal conductivity and propose a new thermal circuit analysis approach for the sandwiched metal layer that can intuitively explain simulation and experimental data. The results show that when the metal layer thickness decreases to be much smaller than the electron-phonon cooling length (or as the "thin limit"), the effective thermal conductivity is just the phonon portion, and electrons do not participate in thermal transport. As the thickness increases to the "thick limit," the effective thermal conductivity recovers the metal bulk value. Several factors that could affect Lc are discussed, and it is discovered that the thermal conductivity, thermal boundary resistance, and the electron-phonon coupling factor are all important in controlling Lc.

Compression enhancement by current stepping in a multicascade liner gas-puff Z-pinch plasma

Energy Technology Data Exchange (ETDEWEB)

Khattak, N A D [Department of Physics, Gomal Unversity, D I Khan (Pakistan); Ahmad, Zahoor; Murtaza, G [National Tokamak Fusion Program, PAEC, Islamabad (Pakistan); Zakaullah, M [Department of Physics, Quaid-i-Azam University, Islamabad 45320 (Pakistan)], E-mail: ktk_nad@yahoo.com

2008-04-15

Plasma dynamics of a liner consisting of two or three annular cascade gas-puffs with entrained axial magnetic field is studied using the modified snow-plow model. The current stepping technique (Les 1984 J. Phys. D: Appl. Phys. 17 733) is employed to enhance compression of the imploding plasma. A small-diameter low-voltage-driven system of imploding plasma is considered in order to work out the possibility of the highest gain, in terms of plasma parameters and radiation yield with a relatively simple and compact system. Our numerical results demonstrate that current stepping enhances the plasma compression, yielding high values of the plasma parameters and compressed magnetic field B{sub z} (in magnitudes), if the switching time for the additional current is properly synchronized.

Compression enhancement by current stepping in a multicascade liner gas-puff Z-pinch plasma

International Nuclear Information System (INIS)

Khattak, N A D; Ahmad, Zahoor; Murtaza, G; Zakaullah, M

2008-01-01

Plasma dynamics of a liner consisting of two or three annular cascade gas-puffs with entrained axial magnetic field is studied using the modified snow-plow model. The current stepping technique (Les 1984 J. Phys. D: Appl. Phys. 17 733) is employed to enhance compression of the imploding plasma. A small-diameter low-voltage-driven system of imploding plasma is considered in order to work out the possibility of the highest gain, in terms of plasma parameters and radiation yield with a relatively simple and compact system. Our numerical results demonstrate that current stepping enhances the plasma compression, yielding high values of the plasma parameters and compressed magnetic field B z (in magnitudes), if the switching time for the additional current is properly synchronized

Grid-Current-Feedback Control for LCL-Filtered Grid Converters With Enhanced Stability

DEFF Research Database (Denmark)

Xin, Zhen; Wang, Xiongfei; Loh, Poh Chiang

2017-01-01

This paper proposes a Second-Order-Generalized- Integrator (SOGI)-based time delay compensation method for extending the stable region of dual-loop Grid-Current-Feedback (GCF) control system. According to the analysis, stable region of the dual-loop system should be designed below a certain...... critical frequency, before time delay compensation method can be applied. To always meet the requirement, relationship between single-loop converter-current-feedback and dual-loop GCF control is clarified, before a robust inner-loop gain for the dualloop GCF scheme is determined. Enforcing this gain allows...

Effect of axial strain on the critical current of Ag-sheathed Bi-based superconductors in magnetic fields up to 25 T

International Nuclear Information System (INIS)

Ekin, J.W.; Finnemore, D.K.; Li, Q.; Tenbrink, J.; Carter, W.

1992-01-01

The irreversible strain limit ε irrev for the onset of permanent axial strain damage to Ag-sheathed Bi 2 Sr 2 Ca 1 Cu 2 O 8+x and Bi 2 Sr 2 Ca 2 Cu 3 O 10+x superconductors has been measured to be in the range of 0.2%--0.35%. This strain damage onset is about an order of magnitude higher than for bulk sintered Y-, Bi-, or Tl-based superconductors and is approaching practical values for magnet design. The measurements show that the value of ε irrev is not dependent on magnetic field, nor does the critical current depend on strain below ε irrev at least up to 25 T at 4.2 K. Both of these factors indicate that the observed strain effect in Ag-sheathed Bi-based superconductors is not intrinsic to the superconductor material. Rather, the effect is extrinsic and arises from superconductor fracture. Thus, the damage onset is amenable to further enhancement. Indeed, the data suggest that subdividing the superconductor into fine filaments or adding Ag to the superconductor powder prior to processing significantly enhances the damage threshold ε irrev to above 0.6%

Superconductivity, intergrain, and intragrain critical current densities of materials

International Nuclear Information System (INIS)

Thompson, J.R.; Brynestad, J.; Kroeger, D.M.; Kim, Y.C.; Sekula, S.T.; Christen, D.K.; Specht, E.D.

1989-01-01

Bulk sintered and powdered samples of the high-temperature superconductive compounds Tl 2 Ca 2 Ba 2 Cu 3 O/sub 1+//sub δ/ (Tl-2:2:2:3) and Tl 2 Ca 2 Ba 2 Cu 2 O/sub 8+//sub δ/ (Tl-2:1:2:2) have been synthesized with phase purity of approximately 90%. The materials were characterized by x-ray-diffraction, metallographic, and electron microprobe analyses. The electronic and superconductive properties were investigated through measurement of the electrical resistivity and the critical current density J/sub c/ using transport methods and by extensive magnetization measurements. Primary results and conclusions are that (1) the intragrain J/sub c/ values were large, much larger than the transport values; (2) both sintered and powdered materials exhibited large flux creep; (3) and the J/sub c/ decreased exponentially with temperature. These features are qualitatively very similar to those found in the corresponding YBa 2 Cu 3 O/sub z/ (with z≅7) series of compounds

Significantly enhanced critical current density in nano-MgB2 grains rapidly formed at low temperature with homogeneous carbon doping

International Nuclear Information System (INIS)

Liu, Yongchang; Lan, Feng; Ma, Zongqing; Chen, Ning; Li, Huijun; Barua, Shaon; Patel, Dipak; Shahriar, M; Hossain, Al; Kim, Jung Ho; Dou, Shi Xue; Acar, S

2015-01-01

High performance MgB 2 bulks using carbon-coated amorphous boron as a boron precursor were fabricated by Cu-activated sintering at low temperature (600 °C, below the Mg melting point). Dense nano-MgB 2 grains with a high level of homogeneous carbon doping were formed in these MgB 2 samples. This type of microstructure can provide a stronger flux pinning force, together with depressed volatility and oxidation of Mg owing to the low-temperature Cu-activated sintering, leading to a significant improvement of critical current density (J c ) in the as-prepared samples. In particular, the value of J c for the carbon-coated (Mg 1.1 B 2 )Cu 0.05 sample prepared here is even above 1 × 10 5 A cm −2 at 20 K, 2 T. The results herein suggest that the combination of low-temperature Cu-activated sintering and employment of carbon-coated amorphous boron as a precursor could be a promising technique for the industrial production of practical MgB 2 bulks or wires with excellent J c , as the carbon-coated amorphous boron powder can be produced commercially at low cost, while the addition of Cu is very convenient and inexpensive. (paper)

High critical current density YBCO films and fabrication of dc-SQUIDs

CERN Document Server

Kuriki, S; Kawaguchi, Y; Matsuda, M; Otowa, T

2002-01-01

In order to improve the sensitivity of SQUID magnetometers made of high-T sub c films, we have studied the conditions of pulsed-laser deposition of YBCO films. Among the different deposition parameters examined, extensive degassing of the vacuum chamber before and precise control of the substrate temperature during the film deposition were found effective for obtaining high critical temperature T sub c and high critical current density J sub c. It was also found that the residual-resistance ratio has a clear correlation with J sub c , indicating that it can be a good, and easy to measure, index of the film quality. Films having T sub c approx 89-90 K and J sub c >= 5x10 sup 6 A cm sup - sup 2 at 77 K were used to fabricate SQUIDs without a pickup loop. Grain-boundary junctions formed on bicrystal substrates with a 30 deg. misorientation angle exhibited I sub c R sub n values of more than 100 mu V at 77 K. The well-known scaling behaviour of the relation I sub c R sub n propor to (J sup G sup B sub c) sup 1 su...

Characterisation of an optimised high current MgO/Bi{sub 2}Sr{sub 2}CaCu{sub 2}O{sub 8.21} composite conductor using pulsed transport currents with pulsed magnetic fields

Energy Technology Data Exchange (ETDEWEB)

Glowacki, B A; Gilewski, A; Rogacki, K; Kursumovic, A; Evetts, J E; Jones, H; Henson, R; Tsukamoto, O

2003-01-15

High temperature superconducting conductors are already used in hybrid magnets to produce fields that enhance the performance of conventional magnets made from A-15 type low temperature superconducting wires. For such applications it is vital that the interdependence of the critical parameters such as critical current versus magnetic field can be mapped under high field and high current conditions. However these superconductors have high critical currents even at fields over 20 T, making accurate measurements difficult due to the thermal and mechanical problems. In this paper, we compare measurements on the fully optimised Bi{sub 2}Sr{sub 2}CaCu{sub 2}O{sub 8.21} flat rigid conductors using an innovative pulsed high transport current and pulsed high field technique. We show how analysis of the voltage signal from Bi{sub 2}Sr{sub 2}CaCu{sub 2}O{sub 8.21} tape in pulsed conditions may be used to extract the critical current under quasi-stationary conditions.

Global trends in critical values practices and their harmonization.

Science.gov (United States)

Kost, Gerald J; Hale, Kristin N

2011-02-01

The objectives of this article were 1) to identify current trends in critical values practices in North America, Europe, and other regions; 2) to describe progress toward harmonization of critical limits; and 3) to synthesize strategies that will encourage global consensus. Critical limits are described in national surveys. Critical value practices are guided by federal statutes, The Joint Commission regulations, and accreditation requirements in the US; by provincial healthcare agencies in Canada; by thought leaders and ISO EN 15189:2007 in Europe; and in SE Asia, mostly by ad hoc policies lacking statutory grip. Review of databases, literature, websites, federal statutes, litigation, official policies, current affairs, and accreditation agency requirements. Practical strategies will accelerate harmonization of critical values practices, as follows: a) continue national and international survey comparisons; b) clarify age, ethnic, and subject dependencies; c) standardize qualitative and quantitative decision levels for urgent clinician notification; d) monitor compliance and timeliness for safety; and e) alert high frequencies of critical values related to adverse events. New expectations and communication technologies present opportunities for enhanced performance using wireless closed-loop reporting with recipient acknowledgment to reduce phone calls and improve efficiency. Hospitals worldwide can benefit from developing consensus for critical values practices.

Current Enhancement with Contact-Area-Limited Doping for Bottom-Gate, Bottom-Contact Organic Thin-Film Transistors

Science.gov (United States)

Noda, Kei; Wakatsuki, Yusuke; Yamagishi, Yuji; Wada, Yasuo; Toyabe, Toru; Matsushige, Kazumi

2013-02-01

The current enhancement mechanism in contact-area-limited doping for bottom-gate, bottom-contact (BGBC) p-channel organic thin-film transistors (OTFTs) was investigated both by simulation and experiment. Simulation results suggest that carrier shortage and large potential drop occur in the source-electrode/channel interface region in a conventional BGBC OTFT during operation, which results in a decrease in the effective field-effect mobility. These phenomena are attributed to the low carrier concentration of active semiconductor layers in OTFTs and can be alleviated by contact-area-limited doping, where highly doped layers are prepared over source-drain electrodes. According to two-dimensional current distribution obtained from the device simulation, a current flow from the source electrode to the channel region via highly doped layers is generated in addition to the direct carrier injection from the source electrode to the channel, leading to the enhancement of the drain current and effective field-effect mobility. The expected current enhancement mechanism in contact-area-limited doping was experimentally confirmed in typical α-sexithiophene (α-6T) BGBC thin-film transistors.

Enhanced vortex damping by eddy currents in superconductor-semiconductor hybrids

Science.gov (United States)

Danckwerts; Goni; Thomsen; Eberl; Rojo

2000-04-17

An enhancement of vortex-motion damping in thin Pb/In superconducting films is obtained through coupling to an adjacent two-dimensional electron gas formed in a modulation-doped GaAs/AlGaAs heterostructure. This effect is observed by monitoring the power dissipation in the superconductor in the vortex state while increasing the density of the electron gas using a gate voltage. Quantitative agreement is found with calculations based on a viscous damping model which considers generation of eddy currents in the electron gas by moving flux lines. In the regime of filamentary vortex flow, eddy-current damping leads to a striking dissipation breakdown due to the stopping of entire vortex channels.

Influence of B4C-doping and high-energy ball milling on phase formation and critical current density of (Bi,Pb)-2223 HTS

Science.gov (United States)

Margiani, N. G.; Mumladze, G. A.; Adamia, Z. A.; Kuzanyan, A. S.; Zhghamadze, V. V.

2018-05-01

In this paper, the combined effects of B4C-doping and planetary ball milling on the phase evolution, microstructure and transport properties of Bi1.7Pb0.3Sr2Ca2Cu3Oy(B4C)x HTS with x = 0 ÷ 0.125 were studied through X-ray diffraction (XRD), scanning electron microscopy (SEM), resistivity and critical current density measurements. Obtained results have shown that B4C additive leads to the strong acceleration of high-Tc phase formation and substantial enhancement in Jc. High-energy ball milling seems to produce a more homogeneous distribution of refined doped particles in the (Bi,Pb)-2223 HTS which results in an improved intergranular flux pinning and better self-field Jc performance.

Comparison of AC losses, magnetic field/current distributions and critical currents of superconducting circular pancake coils and infinitely long stacks using coated conductors

Energy Technology Data Exchange (ETDEWEB)

Yuan Weijia; Campbell, A M; Hong, Z; Ainslie, M D; Coombs, T A, E-mail: wy215@cam.ac.u [Electronic, Power and Energy Conversion Group, Electrical Engineering Division, Engineering Department, University of Cambridge, Cambridge CB3 0FA (United Kingdom)

2010-08-15

A model is presented for calculating the AC losses, magnetic field/current density distribution and critical currents of a circular superconducting pancake coil. The assumption is that the magnetic flux lines will lie parallel to the wide faces of tapes in the unpenetrated area of the coil. Instead of using an infinitely long stack to approximate the circular coil, this paper gives an exact circular coil model using elliptic integrals. A new efficient numerical method is introduced to yield more accurate and fast computation. The computation results are in good agreement with the assumptions. For a small value of the coil radius, there is an asymmetry along the coil radius direction. As the coil radius increases, this asymmetry will gradually decrease, and the AC losses and penetration depth will increase, but the critical current will decrease. We find that if the internal radius is equal to the winding thickness, the infinitely long stack approximation overestimates the loss by 10% and even if the internal radius is reduced to zero, the error is still only 60%. The infinitely long stack approximation is therefore adequate for most practical purposes. In addition, the comparison result shows that the infinitely long stack approximation saves computation time significantly.

Critical current scaling and the pivot-point in Nb3Sn strands

International Nuclear Information System (INIS)

Tsui, Y; Hampshire, D P

2012-01-01

Detailed measurements are provided of the engineering critical current density (J c ) and the index of transition (n-value) of two different types of advanced ITER Nb 3 Sn superconducting strand for fusion applications. The samples consist of one internal-tin strand (OST) and two bronze-route strands (BEAS I and BEAS II—reacted using different heat treatments). Tests on different sections of these wires show that prior to applying strain, J c is homogeneous to better than 2% along the length of each strand. J c data have been characterized as a function of magnetic field (B ≤ 14.5 T), temperature (4.2 K ≤ T ≤ 12 K) and applied axial strain ( − 1% ≤ ε A ≤ 0.8%). Strain-cycling tests demonstrate that the variable strain J c data are reversible to better than 2% when the applied axial strain is in the range of − 1% ≤ ε A ≤ 0.5%. The wires are damaged when the intrinsic strain (ε I ) is ε I ≥ 0.55% and ε I ≥ 0.23% for the OST and BEAS strands, respectively. The strain dependences of the normalized J c for each type of strand are similar to those of prototype strands of similar design measured in 2005 and 2008 to about 2% which makes them candidate strands for a round-robin interlaboratory comparison. The J c data are described by Durham, ITER and Josephson-junction parameterizations to an accuracy of about 4%. For all of these scaling laws, the percentage difference between the data and the parameterization is larger when J c is small, caused by high B, T or |ε I |. The n-values can be described by a modified power law of the form n=1+rI c s , where r and s are approximately constant and I c is the critical current. It has long been known that pivot-points (or cross-overs) in J c occur at high magnetic field and temperature. Changing the magnetic field or temperature from one side of the pivot-point to the other changes the highest J c sample to the lowest J c sample and vice versa. The pivot-point follows the B–T phase boundary

Anisotropy of critical current density in the superconducting Nb/sub 3/Sn tape wires

Energy Technology Data Exchange (ETDEWEB)

Glowacki, B A [Technical Univ., Wroclaw (Poland). Inst. of Fundamental Electrotechnics and Electrotechnology

1985-04-01

In this letter the results are presented of an investigation of Isub(c parallel) and Isub(c perpendicular) in Nb/sub 3/Sn layers obtained in the process diffusion of tin atoms from liquid bronze solution Cu-80% Sn to the Nb-1.5% Zr substrate. Measurements of critical current density in Nb/sub 3/Sn layers were carried out in a perpendicular magnetic field of the induction value 4.25 T for different sample surface orientations in relation to the magnetic field strength vector defined by the value of angle. The critical current density was measured at a temperature of 4.2 K. Phase identification and investigation of the microstructure of superconducting Nb-Sn layers were performed on the Moessbauer spectrometer and scanning electron microscope, respectively. Classification measurements of grains in Nb-Sn layers were carried out with TV automatic image analyser. The texture and lattice parameter in Nb/sub 3/Sn layers were investigated by means of an X-ray diffractometer. The surface zone of Nb/sub 3/Sn layer was removed with the use of an argon ion gun. Results are presented and discussed.

Magnetic penetration depth δ o and critical current density in Y-BA-Cu-O crystals

International Nuclear Information System (INIS)

Zavaritsky, N.V.; Zavaritsky, V.N.

1989-01-01

Magnetic penetration depthδ o ∼1.03 10 - 5 cm and critical current density (j c = 0.5 divided-by 1 x 10 5 A/cm 2 at T/T ∼0.98) are determined from low-field do magnetization measurements on Y 1 Ba 2 Cu 3 O 7 - crystals

Angular dependence of critical current density and magnetoresistance of sputtered high-T{sub c}-films

Energy Technology Data Exchange (ETDEWEB)

Geerkens, A.; Frenck, H.J.; Ewert, S. [Technical Univ. of Cottbus (Germany)] [and others

1994-12-31

The angular dependence of the critical current density and the magnetoresistance of high-T{sub c}-films in high and low magnetic fields and for different temperatures were measured to investigate the flux pinning and the superconducting properties. A comparison of the results for the different superconductors shows their increasing dependence on the angle {Theta} between the magnetic field and the c-axis of the film due to the anisotropy of the chosen superconductor. Furthermore the influence of the current direction to the {Theta}-rotation plane is discussed.

Energization of the Ring Current through Convection of Substorm Enhancements of the Plasma Sheet Source.

Science.gov (United States)

Menz, A.; Kistler, L. M.; Mouikis, C.; Spence, H. E.; Henderson, M. G.; Matsui, H.

2017-12-01

It has been shown that electric field strength and night-side plasma sheet density are the two best predictors of the adiabatic energy gain of the ring current during geomagnetic storms (Liemohn and Khazanov, 2005). While H+ dominates the ring current during quiet times, O+ can contribute substantially during geomagnetic storms. Substorm activity provides a mechanism to enhance the energy density of O+ in the plasma sheet during geomagnetic storms, which is then convected adiabatically into the inner-magnetosphere. Using the Van Allen Probes data in the the plasma sheet source region (defined as L>5.5 during storms) and the inner magnetosphere, along with LANL-GEO data to identify substorm injection times, we show that adiabatic convection of O+ enhancements in the source region can explain the observed enhancements in the inner magnetosphere. We use the UNH-IMEF electric field model to calculate drift times from the source region to the inner magnetosphere to test whether enhancements in the inner-magnetosphere can be explained by dipolarization driven enhancements in the plasma sheet source hours before.

Effect of the critical current density and the junction size on the leakage current of Nb/Al-AlOx/Nb superconducting tunnel junctions for radiation detection

International Nuclear Information System (INIS)

Joosse, K.; Nakagawa, Hiroshi; Akoh, Hiroshi; Takada, Susumu; Maehata, Keisuke; Ishibashi, Kenji.

1996-01-01

Nb/Al-AlO x /Nb superconducting tunnel junctions (STJ's) designed for X-ray detection have been fabricated. The behavior of the low-temperature subgap leakage current, which severely limits the energy resolution obtained in such devices, is investigated. From trends in the dependence of the leakage currents on the critical current density and the size of the STJ, as well as from the low-temperature current-voltage characteristics, and an analysis of the base electrode surface morphology, it is concluded that physical defects in the barrier region are the most probable cause of the leakage currents. Suggestions are given for optimization of the device processing. (author)

Constructing vulnerabilty and protective measures indices for the enhanced critical infrastructure protection program.

Energy Technology Data Exchange (ETDEWEB)

Fisher, R. E.; Buehring, W. A.; Whitfield, R. G.; Bassett, G. W.; Dickinson, D. C.; Haffenden, R. A.; Klett, M. S.; Lawlor, M. A.; Decision and Information Sciences; LANL

2009-10-14

The US Department of Homeland Security (DHS) has directed its Protective Security Advisors (PSAs) to form partnerships with the owners and operators of assets most essential to the Nation's well being - a subclass of critical infrastructure and key resources (CIKR) - and to conduct site visits for these and other high-risk assets as part of the Enhanced Critical Infrastructure Protection (ECIP) Program. During each such visit, the PSA documents information about the facility's current CIKR protection posture and overall security awareness. The primary goals for ECIP site visits (DHS 2009) are to: (1) inform facility owners and operators of the importance of their facilities as an identified high-priority CIKR and the need to be vigilant in light of the ever-present threat of terrorism; (2) identify protective measures currently in place at these facilities, provide comparisons of CIKR protection postures across like assets, and track the implementation of new protective measures; and (3) enhance existing relationships among facility owners and operators; DHS; and various Federal, State, local tribal, and territorial partners. PSAs conduct ECIP visits to assess overall site security; educate facility owners and operators about security; help owners and operators identify gaps and potential improvements; and promote communication and information sharing among facility owners and operators, DHS, State governments, and other security partners. Information collected during ECIP visits is used to develop metrics; conduct sector-by-sector and cross-sector vulnerability comparisons; identify security gaps and trends across CIKR sectors and subsectors; establish sector baseline security survey results; and track progress toward improving CIKR security through activities, programs, outreach, and training (Snyder 2009). The data being collected are used in a framework consistent with the National Infrastructure Protection Plan (NIPP) risk criteria (DHS 2009). The

Superconducting critical-current densities of commercial multifilamentary Nb3Sn(Ti) wires made by the bronze process

International Nuclear Information System (INIS)

Suenaga, M.; Tsuchiya, K.; Higuchi, N.; Tachikawa, K.

1985-01-01

Superconducting critical-current densities Jsub(c) in fields up to 24 T and at 4.2 and 1.8 K were measured for a number of commercial Nb 3 Sn wires which were alloyed with Ti. The best values of Jsub(c) at 20 T and at 4.2 and 1.8 K were 78 and 156 A mm -2 , respectively. In order to achieve these high current densities at H>20 T, it was shown that nonuniformity of the filaments had to be minimized. It was also shown that the grain size of Nb 3 Sn is not very important in determining Jsub(c) at these high magnetic fields, and that achieving high values of critical magnetic field Hsub(c2) is more important than small grain size. (author)

Measurement of weak electric currents in copper wire phantoms using MRI: influence of susceptibility enhancement.

Science.gov (United States)

Huang, Ruiwang; Posnansky, Oleg; Celik, Abdullah; Oros-Peusquens, Ana-Maria; Ermer, Veronika; Irkens, Marco; Wegener, H-Peter; Shah, N Jon

2006-08-01

The use of magnetic resonance imaging (MRI)-based methods for the direct detection of neuronal currents is a topic of intense investigation. Much experimental work has been carried out with the express aim of establishing detection thresholds and sensitivity to flowing currents. However, in most of these experiments, magnetic susceptibility enhancement was ignored. In this work, we present results that show the influence of a susceptibility artefact on the detection threshold and sensitivity. For this purpose, a novel phantom, consisting of a water-filled cylinder with two wires of different materials connected in series, was constructed. Magnitude MR images were acquired from a single slice using a gradient-echo echo planar imaging (EPI) sequence. The data show that the time course of the detected MR signal magnitude correlates very well with the waveform of the input current. The effect of the susceptibility artefacts arising from the two different wires was examined by comparing the magnitudes of the MR signals at different voxel locations. Our results indicate the following: (1) MR signal enhancement arising from the magnetic susceptibility effect influences the detection sensitivity of weak current; (2) the detection threshold and sensitivity are phantom-wire dependent; (3) sub-mu A electric current detection in a phantom is possible on a 1.5-T MR scanner in the presence of susceptibility enhancement.

Advances in superconductivity: new materials, critical currents and devices

International Nuclear Information System (INIS)

Pinto, R.; Malik, S.K.; Grover, A.K.; Ayyub, P.

1997-01-01

The discovery of superconductivity in the cuprates produced an explosive growth in research, driven by the quest for higher and higher superconducting transition temperatures. In the initial stages, the excitement was tremendous both in the physical sciences and in engineering. However, the complexity of the new materials on the one hand, and the absence of a viable theory on the other, have made further developments much more difficult. It is to be expected therefore, that the early excitement and the subsequent rapid advances have paved the way for more systematic and detailed studies of all aspects of superconductivity. The International Symposium was intended to provide a forum to review the progress in selected areas in superconductivity. The emphasis was on experimental and theoretical studies of the new superconductors, advances in the theoretical understanding, progress in studies of flux pinning and vortex dynamics which affect critical currents, and developments of novel material synthesis methods. Recent developments in the twin areas of thin films and devices were extensively discussed during the symposium. Papers relevant to INIS are indexed separately

Access of energetic particles to storm time ring current through enhanced radial diffusion

International Nuclear Information System (INIS)

Lyons, L.R.; Schulz, M.

1989-01-01

Magnetic storms are distinguishable from other periods of geomagnetic activity by the injection of trapped electrons and ions to the 2 approx-lt L approx-lt 4 region. It has been proposed previously that this injection results from an inward displacement of the preexisting trapped-particle population by enhanced storm time electric fields. However, high-energy (approx-gt 40 keV) ring-current particles have drift periods that are typically shorter than the time of the main-phase development, and so the direct radial transport of these particles is restricted. The authors propose here that the transport of approx-gt 40 keV particles into the storm time ring current can result from enhanced stochastic radial transport driven by fluctuating electric fields during a storm's main phase. They estimate the effects of such electric fields by applying radial-diffusion theory, assuming a preexisting trapped-particle population as the initial conditions, and they demonstrate the feasibility of explaining observed flux increases of approx-gt 40-keV particles at L approx-lt 4 by enhanced radial diffusion. It is necessary that new particles be injected near the outer boundary of the trapping region so as to maintain the fluxes there as an outer boundary condition, and they estimate that the approx-gt 40-keV portion of the storm time ring current at L ∼ 3 consists of about 50% preexisting and about 50% new particles. They thus find that formation of the storm time ring current may be explainable via a combination of direct radial transport at energies approx-lt 40 keV and diffusive radial transport at higher energies

Critical current densities and flux creep rate in Co-doped BaFe2As2 with columnar defects introduced by heavy-Ion irradiation

International Nuclear Information System (INIS)

Nakajima, Y.; Tsuchiya, Y.; Taen, T.; Yagyuda, H.; Tamegai, T.; Okayasu, S.; Sasase, M.; Kitamura, H.; Murakami, T.

2010-01-01

We report the formation of columnar defects in Co-doped BaFe 2 As 2 single crystals with different heavy-ion irradiations. The formation of columnar defects by 200 MeV Au ion irradiation is confirmed by transmission electron microscopy and their density is about 40% of the irradiation dose. Magneto-optical imaging and bulk magnetization measurements reveal that the critical current density J c is enhanced in the 200 MeV Au and 800 MeV Xe ion irradiated samples while J c is unchanged in the 200 MeV Ni ion irradiated sample. We also find that vortex creep rates are strongly suppressed by the columnar defects. We compare the effect of heavy-ion irradiation into Co-doped BaFe 2 As 2 and cuprate superconductors.

Rated-voltage enhancement by fast-breaking of the fault current for a resistive superconducting fault current limiter component

International Nuclear Information System (INIS)

Park, C.-R.; Kim, M.-J.; Yu, S.-D.; Yim, S.-W.; Kim, H.-R.; Hyun, O.-B.

2010-01-01

Performance of a resistive superconducting fault current limiter (SFCL) component is usually limited by temperature rise associated with energy input by fault current application during a fault. Therefore, it is expected that short application of the fault current may enhance the power ratings of the component. This can be accomplished by a combination of a HTS component and a mechanical switch. The fast switch (FS) developed recently enables the fault duration to be as short as 1/2 cycle after a fault. Various second-generation (2G) high temperature superconductors (HTS) and YBCO thin films have been tested. The relation between the rated voltage V and the fault duration time t was found to be V 2 ∼ t -1 . Based upon the relation, we predict that when the FS break the fault current within 1/2 cycle after a fault, the amount of HTS components required to build an SFCL can be reduced by as much as about 60%, of that when breaking the fault current at three cycles.

Perineuronal nets increase inhibitory GABAergic currents during the critical period in rats

Directory of Open Access Journals (Sweden)

Zheng-Qin Yin

2013-04-01

Full Text Available AIM: To investigate inhibitory γ-aminobutyric acid (GABA ergic postsynaptic currents (IPSCs and postsynaptic currents (PSCs in layer IV of the rat visual cortex during the critical period and when plasticity was extended through dissolution of the perineuronal nets (PNNs.METHODS:We employed 24 normal Long-Evans rats to study GABAA-PSC characteristics of neurons within layer IV of the visual cortex during development. The animals were divided into six groups of four rats according to ages at recording:PW3 (P21-23d, PW4 (P28-30d, PW5 (P35-37d, PW6 (P42-44d, PW7 (P49-51d, and PW8 (56-58d. An additional 24 chondroitin sulfate proteoglycan (CSPG degradation rats (also Long-Evans were generated by making a pattern of injections of chondroitinase ABC (chABC into the visual cortex 1 week prior to recording at PW3, PW4, PW5, PW6, PW7, and PW8. Immunohistochemistry was used to identify the effect of chABC injection on CSPGs. PSCswere detected with whole-cell patch recordings, and GABAA receptor-mediated IPSCs were pharmacologically isolated.RESULTS:IPSC peak current showed a strong rise in the age-matched control group, peaked at PW5 and were maintained at a roughly constant value thereafter. Although there was a small increase in peak current for the chABC group with age, the peak currents continued to decrease with the delayed highest value at PW6, resulting in significantly different week-by-week comparison with normal development. IPSC decay time continued to increase until PW7 in the control group, while those in the chABC group were maintained at a stable level after an initial increase at PW4. Compared with normal rats, the decay times recorded in the chABC rats were always shorter, which differed significantly at each age. We did not observe any differences in IPSC properties between the age-matched control and penicillinase (P-ase group.However, the change in IPSCs after chABC treatment was not reflected in the total PSCs or in basic membrane

Correlations between critical current density, j{sub c}, critical temperature, T{sub c}, and structural quality of Y{sub 1}B{sub 2}Cu{sub 3}O{sub 7-x} thin superconducting films

Energy Technology Data Exchange (ETDEWEB)

Chrzanowski, J.; Xing, W.B.; Atlan, D. [Simon Fraser Univ., British Columbia (Canada)] [and others

1994-12-31

Correlations between critical current density (j{sub c}) critical temperature (T{sub c}) and the density of edge dislocations and nonuniform strain have been observed in YBCO thin films deposited by pulsed laser ablation on (001) LaAlO{sub 3} single crystals. Distinct maxima in j{sub c} as a function of the linewidths of the (00{ell}) Bragg reflections and as a function of the mosaic spread have been found in the epitaxial films. These maxima in j{sub c} indicate that the magnetic flux lines, in films of structural quality approaching that of single crystals, are insufficiently pinned which results in a decreased critical current density. T{sub c} increased monotonically with improving crystalline quality and approached a value characteristic of a pure single crystal. A strong correlation between j{sub c} and the density of edge dislocations N{sub D} was found. At the maximum of the critical current density the density of edge dislocations was estimated to be N{sub D}{approximately}1-2 x 10{sup 9}/cm{sup 2}.

Enhancement of critical current density of YBa2Cu3O7-δ thin films by nanoscale CeO2 pretreatment of substrate surfaces

International Nuclear Information System (INIS)

Cui, X.M.; Liu, G.Q.; Wang, J.; Huang, Z.C.; Zhao, Y.T.; Tao, B.W.; Li, Y.R.

2007-01-01

YBa 2 Cu 3 O 7-δ (YBCO) films were prepared on single-crystal SrTiO 3 substrates with metal-organic deposition using trifluoroacetates (TFA-MOD). Positive results have been acquired in controlled study to investigate the effects of substrate surface modification on the growth-induced flux-pinning nanostructures in YBCO films. Nanoscale CeO 2 particles were applied to single-crystal SrTiO 3 substrate surfaces using pulsed laser deposition before YBCO precursors coating. Superconducting properties of the YBCO films grown on the controlled CeO 2 -modified substrates have shown substantial improvement in the critical current densities (J c ) at 77 K over those grown on untreated substrates in almost all the field (78% increment at 1 T, 77 K). We think the reason is that the CeO 2 nanoparticles act as pinning centers

Effects of stress on critical current in V3Ga tape

International Nuclear Information System (INIS)

Okada, Touichi; Terada, R.

1979-01-01

For the generation of magnetic field less than 8T NbTi conductors have been used with considerable reliability. For the higher field (which is strongly expected for advanced SCM in near future) compound type superconductors such as Nb 3 Sn or V 3 Ga are to be used. These compound superconducting materials are, however, intrinsically brittle, so that it has been said that considerable degradation cannot be avoided, if they are subjected to certain amount of strain say, --0.1%. This is the main reason that compound superconducting materials have been hesitated to the application to the LARGE magnets. To give a clearer insight to the problem we have studied stress/strain degradation effects on commercially available superconducting V 3 Ga tape using specially designed apparatus by making ''in situ'' experiment, i.e. 1) in liquid He, 2) with external magnetic field, 3) with current in the conductor and 4) with stresses. An interesting and very important results were obtained that the critical current density increases with stress (or strain) at the first stage and degraded drastically after the sample is strained higher than about ''one percent''. (author)

Magnetization, critical current, and injection field harmonics in superconducting accelerator magnets

International Nuclear Information System (INIS)

Ghosh, A.K.; Sampson, W.B.; Wanderer, P.

1985-01-01

The very large energy ratio of machines such as the SSC dictates rather low injection field (for 6T, 20 TeV it is approximately 0.3T). Since the harmonic content at such low fields is largely determined by magnetization currents in the superconductor, the random errors depend on the uniformity of the superconducting wire. In principle the magnitude of the residual fields can be reduced indefinitely by using finer filaments, but in practice there is a lower limit of a few microns. We have compared the injection field harmonics for a number of accelerator dipoles with magnetization measurements made on samples of the conductor used to wind the coils. In addition both the magnetization and harmonics have been compared with short sample critical current measurements made at 5T. The results indicated that an accurate estimate of the variation in injection field harmonics can only be obtained from direct measurements of the magnetization of the cable. It appears feasible to use such measurements to ''shuffle'' magnets for a large accelerator by predicting the low field properties of a magnet before actually winding the coils. 10 refs., 4 figs., 2 tabs

Strong enhancement of streaming current power by application of two phase flow

NARCIS (Netherlands)

Xie, Yanbo; Sherwood, John D.; Shui, Lingling; van den Berg, Albert; Eijkel, Jan C.T.

2011-01-01

We show that the performance of a streaming-potential based microfluidic energy conversion system can be strongly en-hanced by the use of two phase flow. In single-phase systems, the internal conduction current induced by the streaming poten-tial limits the output power, while in a two-phase system

The European cooperative approach to securing critical information infrastructure.

Science.gov (United States)

Purser, Steve

2011-10-01

This paper provides an overview of the EU approach to securing critical information infrastructure, as defined in the Action Plan contained in the Commission Communication of March 2009, entitled 'Protecting Europe from large-scale cyber-attacks and disruptions: enhancing preparedness, security and resilience' and further elaborated by the Communication of May 2011 on critical Information infrastructure protection 'Achievements and next steps: towards global cyber-security'. After explaining the need for pan-European cooperation in this area, the CIIP Action Plan is explained in detail. Finally, the current state of progress is summarised together with the proposed next steps.

Distribution Analysis of the Local Critical Temperature and Current Density in YBCO Coated Conductors using Low-temperature Scanning Laser and Hall Probe Microscopy

International Nuclear Information System (INIS)

Park, S. K.; Cho, B. R.; Park, H. Y.; Ri, H. C.

2011-01-01

Distribution of the local critical temperature and current density in YBCO coated conductors were analyzed using Low-temperature Scanning Laser and Hall Probe Microscopy (LTSLHPM). We prepared YBCO coated conductors of various bridge types to study the spatial distribution of the critical temperature and the current density in single and multi bridges. LTSLHPM system was modified for detailed linescan or two-dimensional scan both scanning laser and scanning Hall probe method simultaneously. We analyzed the local critical temperature of single and multi bridges from series of several linescans of scanning laser microscopy. We also investigated local current density and hysteresis curve of single bridge from experimental results of scanning Hall probe microscopy.

Critical currents of Y sub 1 Ba sub 2 Cu sub 3 O sub 7-. delta. ceramics

Energy Technology Data Exchange (ETDEWEB)

Vasiliev, B V; Obukhov, Yu V [Joint Inst. for Nuclear Research, Low Temperature Physics Dept., Moscow (USSR)

1991-12-01

The magnetization measurements on a ceramic YBaCuO sample were carried out. The M(H,T) dependence has demonstrated some peculiarities which we suppose to be connected with H{sub j1}, H{sub j2}, H{sub C1} fields. By analizing the magnetization in the field region between H{sub j1} and H{sub j2} within the frame of the critical state model one can found the dependence of the intergranular critical current density on field and temperature. (orig.).

Vortex lines in layered superconductors. II. Pinning and critical currents in high temperature superconductors

Science.gov (United States)

Manuel, P.

1994-02-01

In this article, a qualitative survey is given on the various phenomena which influence the critical current of high temperature superconductors. Critical current is defined as a property related to a non-zero electric field criterion, the level of which is fixed by experimental considerations, or efficiency requirements of applications. The presentation is restricted to extrinsic intragranular critical current, which depends in a complex way on the interplay between the characteristics of pinning centres and the properties of the vortex lattice. The discussion is focussed on the configuration {B} / / {c}, which contains the main elements of this problem. Differences of behaviour between Y(123) and BSCCO (Bi(2212) or Bi(2223)) are analysed in the context of their respective anisotropy factors. Possible regimes for pinning and creep are discussed in various temperature domains. From critical current results, a strong pinning regime is found to occur in BSCCO, whereas the pinning strength in Y(123) is still an open question. The thermal decrease of critical current allows a collective creep regime to appear in both materials, but at different temperature ranges. The disappearance of correlation effects near the irreversibility line results in a fall of the effective pinning energy. We show that in BSCCO, the effective pinning energy deduced from experimental results is not in agreement with pinning by randomly dispersed oxygen vacancies. Finally, we shortly describe the microstructures which could allow a more efficient pinning in future materials. On effectue une présentation qualitative des divers phénomènes qui contrôlent la valeur du courant critique dans les supraconducteurs à haute température. La notion de courant critique qui est utilisée est reliée à un critère de champ électrique non nul, fixé par des considérations expérimentales ou des exigences de rendement pour les applications. On se restreint au problème des courants critiques

Anomalous enhancement of the lower critical field deep in the superconducting state of LaRu4As12

Science.gov (United States)

Juraszek, J.; Bochenek, Ł.; Wawryk, R.; Henkie, Z.; Konczykowski, M.; Cichorek, T.

2018-05-01

LaRu4As12 with the critical temperature Tc = 10.4 K displays several features which point at a non-singlet superconducting order parameter, although the bcc crystal structure of the filled skutterudites does not favour the emergence of multiple energy gaps. LaRu4As12 displays an unexpected enhancement of the lower critical field deep in superconducting state which can be attributed to the existence of two superconducting gaps. At T = 0.4 K, the local magnetization measurements were performed utilizing miniaturized Hall sensors.

Constructing a resilience index for the Enhanced Critical Infrastructure Protection Program

Energy Technology Data Exchange (ETDEWEB)

Fisher, R. E.; Bassett, G. W.; Buehring, W. A.; Collins, M. J.; Dickinson, D. C.; Eaton, L. K.; Haffenden, R. A.; Hussar, N. E.; Klett, M. S.; Lawlor, M. A.; Millier, D. J.; Petit, F. D.; Peyton, S. M.; Wallace, K. E.; Whitfield, R. G.; Peerenboom, J P

2010-10-14

Following recommendations made in Homeland Security Presidential Directive 7, which established a national policy for the identification and increased protection of critical infrastructure and key resources (CIKR) by Federal departments and agencies, the U.S. Department of Homeland Security (DHS) in 2006 developed the Enhanced Critical Infrastructure Protection (ECIP) program. The ECIP program aimed to provide a closer partnership with state, regional, territorial, local, and tribal authorities in fulfilling the national objective to improve CIKR protection. The program was specifically designed to identify protective measures currently in place in CIKR and to inform facility owners/operators of the benefits of new protective measures. The ECIP program also sought to enhance existing relationships between DHS and owners/operators of CIKR and to build relationships where none existed (DHS 2008; DHS 2009). In 2009, DHS and its protective security advisors (PSAs) began assessing CIKR assets using the ECIP program and ultimately produced individual protective measure and vulnerability values through the protective measure and vulnerability indices (PMI/VI). The PMI/VI assess the protective measures posture of individual facilities at their 'weakest link,' allowing for a detailed analysis of the most vulnerable aspects of the facilities (Schneier 2003), while maintaining the ability to produce an overall protective measures picture. The PMI has six main components (physical security, security management, security force, information sharing, protective measures assessments, and dependencies) and focuses on actions taken by a facility to prevent or deter the occurrence of an incident (Argonne National Laboratory 2009). As CIKR continue to be assessed using the PMI/VI and owners/operators better understand how they can prevent or deter incidents, academic research, practitioner emphasis, and public policy formation have increasingly focused on resilience as a

Finite element transport methods for criticality calculations - current status and potential applications

International Nuclear Information System (INIS)

Oliveira, C.R.E. de; Goddard, A.

1991-01-01

In this paper we review the current status of the finite element method applied to the solution of the neutron transport equation and we discuss its potential role in the field of criticality safety. We show that the method's ability in handling complex, irregular geometry in two- and three-dimensions coupled with its accurate solutions potentially renders it an attractive alternative to the longer-established Monte Carlo method. Details of the most favoured form of the method - that which combines finite elements in space and spherical harmonics in angle - are presented. This form of the method, which has been extensively investigated over the last decade by research groups at the University of London, has been numerically implemented in the finite element code EVENT. The code has among its main features the capability of solving fixed source eigenvalue and time-dependent complex geometry problems in two- and three-dimensions. Other features of the code include anisotropic up- and down-scatter, direct and/or adjoint solutions and access to standard data libraries. Numerical examples, ranging from simple criticality benchmark studies to the analysis of idealised three-dimensional reactor cores, are presented to demonstrate the potential of the method. (author)

The influence of atomic disordering on the critical currents in A15 superconductors near Hsub(c1)

International Nuclear Information System (INIS)

Faehnle, M.; Kronmueller, H.

1976-01-01

By a model calculation based on the Labbe-Friedel-van-Reuth model of A15 superconductors it is shown that atomic disordering in Nb 3 Sn reduces significantly the critical current densities, jsub(c), in materials with large pinning effects. (author)

Critical current anisotropy in Ag/(Pb,Bi){sub 2}Sr{sub 2}Ca{sub 2}Cu{sub 3}O{sub 10+x} multifilamentary tapes: influence of self-magnetic field

Energy Technology Data Exchange (ETDEWEB)

Majoros, M [IRC in Superconductivity, University of Cambridge, Cambridge (United Kingdom); Institute of Electrical Engineering, Slovak Academy of Sciences, Bratislava (Slovakia); Glowacki, B A [IRC in Superconductivity, University of Cambridge, Cambridge (United Kingdom); Department of Materials Science and Metallurgy, University of Cambridge, Cambridge (United Kingdom); Campbell, A M [IRC in Superconductivity, University of Cambridge, Cambridge (United Kingdom)

2001-06-01

Two factors affect critical current anisotropy in multifilamentary Ag/(Pb,Bi){sub 2}Sr{sub 2}Ca{sub 2}Cu{sub 3}O{sub 10+x} tapes - the intrinsic material anisotropy and the geometry. Experimental results on the magnetic field dependence and anisotropy of the critical current in a multifilamentary Ag/(Pb,Bi){sub 2}Sr{sub 2}Ca{sub 2}Cu{sub 3}O{sub 10+x} tape after correction for self-magnetic field effects were found to fit the anisotropic Kim relation. Based on this relation a finite-element-method numerical code for solving the nonlinear Poisson equation for vector magnetic potential was adopted. It allowed the experimental data to be reproduced by back calculation and made possible the study of the interplay of self and external magnetic fields in different cases with well defined physical parameters of the material. The model was used to analyse the distribution of the critical current in individual filaments as well as to evaluate the influence of their geometrical arrangements on the critical current of the tape. The self-field critical current of an individual filament 'extracted' from the tape was compared with the critical current of the overall tape. The effect of the self-magnetic field on critical current distribution obtained by the cutting method was determined. The critical currents of the tapes with different cross sections were calculated and compared with experiments and the influence of the self-field was analysed. The anisotropic properties of a low anisotropy architecture of a multifilamentary Ag/(Pb,Bi){sub 2}Sr{sub 2}Ca{sub 2}Cu{sub 3}O{sub 10+x} conductor were studied. The dependence of critical currents (normalized to self-field critical currents) on external magnetic field corrected for the self-field was found to follow nearly the same curves as those for tapes with different critical current densities (in the range 20-70 kA cm{sup -2} in a self-field), which makes the numerical model applicable to different tapes. (author)

Correlation between in-field critical currents in Zr-added (Gd, Y)Ba2Cu3Ox superconducting tapes at 30 and 77 K

Energy Technology Data Exchange (ETDEWEB)

Selvamanickam, V; Xu, A; Liu, Y; Khatri, ND; Lei, C; Chen, Y; Galstyan, E; Majkic, G

2014-03-11

Critical current (I-c) values of 1384 Lambda/12 mm, corresponding to a critical current density of 12.47 MA cm(-2) and a pinning force of 374 GN m(-3), have been achieved at 30 K, 3 T in the orientation of field parallel to the c axis (B parallel to c) in (Gd, Y)BaCuO tapes with 15 mol% Zr addition made by metal organic chemical vapor deposition (MOCVD). These tapes show pinning force levels as high as 453 GN m(-3) at 30 K. An analysis of the properties of 24-28 (Gd, Y)BaCuO tapes with 15 mol% Zr addition showed a lack of correlation between their critical currents at 30 K, 3 T (B parallel to c) and I-c values both at 77 K, zero field and at 77 K, 1 T (B parallel to c). However, a strong correlation was found between the critical currents at 30 K, 3 T and at 77 K, 3 T (B parallel to c). It has also been discovered that the minimum critical current (I-c, (min)) value at 77 K, 3 T has no influence on the I-c,I- (min) value at 30 K, 3 T, and it in turn depends on the ratio of the I-c values in the orientations of field parallel and perpendicular to the c axis at 77 K, 3 T.

Enhanced D-T supershot performance at high current using extensive lithium conditioning in TFTR

International Nuclear Information System (INIS)

Mansfield, D.K.; Strachan, J.D.; Bell, M.G.; Scott, S.D.; Budny, R.; Bell, R.E.; Bitter, M.; Darrow, D.S.; Fredrickson, E.; Grek, B.

1995-05-01

A substantial improvement in supershot fusion plasma performance has been realized by combining the enhanced confinement due to tritium fueling with the enhanced confinement due to extensive Li conditioning of the TFTR limiter. This combination has resulted in not only significantly higher global energy confinement times than had previously been obtained in high current supershots, but also the highest ratio of central fusion output power to input power observed to date

Influence of copper volume fraction on tensile strain/stress tolerances of critical current in a copper-plated DyBCO-coated conductor

International Nuclear Information System (INIS)

Ochiai, Shojiro; Okuda, Hiroshi; Arai, Takahiro; Sugano, Michinaka; Osamura, Kozo; Prusseit, Werner

2013-01-01

The influence of the volume fraction (V f ) of copper, plated at room temperature over a DyBa 2 Cu 3 O 7-δ -coated conductor, on the tensile strain tolerance and stress tolerance of critical current at 77 K was studied over a wide range of copper V f values. The copper plating exerts a tensile stress during cooling because copper has a higher coefficient of thermal expansion than the substrate conductor. Before application of tensile strain, the copper plated at room temperature yielded at 77 K when the copper V f was lower than a critical value, and was in an elastic state at 77 K when the copper V f was higher than the critical value. The strain tolerance of critical current increased with increasing copper V f due to an increase in thermally induced compressive strain in the substrate tape. The stress tolerance of critical current decreased with increasing copper V f because copper is softer than the substrate tape. These results, together with the trade-off between strain tolerance and stress tolerance (i.e., stress tolerance decreases with increasing strain tolerance), were analyzed by modeling. The results show that the restriction imposed by the trade-off, which limits the ability to simultaneously obtain a high strain tolerance and a high stress tolerance, can be relaxed by strengthening the copper. (author)

Critical review: medical students' motivation after failure.

Science.gov (United States)

Holland, Chris

2016-08-01

About 10 % of students in each years' entrants to medical school will encounter academic failure at some stage in their programme. The usual approach to supporting these students is to offer them short term remedial study programmes that often enhance approaches to study that are orientated towards avoiding failure. In this critical review I will summarise the current theories about student motivation that are most relevant to this group of students and describe how they are enhanced or not by various contextual factors that medical students experience during their programme. I will conclude by suggesting ways in which support programmes for students who have encountered academic failure might be better designed and researched in the future.

Effect of pelletization pressure on structural properties and critical current hysteresis of ceramic superconducting Bi sub 1 sub . sub 7 Pb sub 0 sub . sub 3 Sr sub 2 Ca sub 2 Cu sub 3 O sub y

CERN Document Server

Tepe, M; Abukay, D

2003-01-01

The effect of pelletization pressures on structural properties and critical current hysteresis of Bi sub 1 sub . sub 7 Pb sub 0 sub . sub 3 Sr sub 2 Ca sub 2 Cu sub 3 O sub y samples was investigated. The samples used in this study were prepared by classical solid-state reaction at the pressures from 100 up to 500 MPa. The obtained samples were characterized by resistance vs. temperature, (R-T), critical current density vs. applied magnetic field, (J sub c -H), material density vs. pressure, (rho-P), XRD, SEM, and EDAX. The results of this study showed that the quality of electrical and structural properties of Bi-2223 bulk superconductors strongly depends on the pelletization pressure. Pressing of bulk samples at 400 MPa produces textured grain alignment and associates microstructural modifications in order to enhance flux pinning and thus increases current carrying capacities. (Abstract Copyright [2003], Wiley Periodicals, Inc.)

Effect of Y2O3 Nanoparticles on Critical Current Density of YBa2Cu3O7-x Thin Films

International Nuclear Information System (INIS)

Tran, H. D.; Reddy, Sreekantha; Wie, C. H.; Kang, B.; Oh, Sang Jun; Lee, Sung Ik

2009-01-01

Introduction of proper impurity into YBa 2 Cu 3 O 7-x (YBCO) thin films is an effective way to enhance its flux-pinning properties. We investigate effect of Y 2 O 3 nanoparticles on the critical current density J c of the YBCO thin films. The Y 2 O 3 nanoparticles were created perpendicular to the film surface (parallel with the c-axis) either between YBCO and substrate or on top of YBCO, YBCO/Y 2 O 3 /LAO or Y 2 O 3 /YBCO/STO, by pulsed laser deposition. The deposition temperature of the YBCO films were varied (780 degree C and 800 degree C) to modify surface morphology of the YBCO films. Surface morphology characterization revealed that the lower deposition temperature of 780 degree C created nano-sized holes on the YBCO film surface which may behave as intrinsic pinning centers, while the higher deposition temperature produced much denser and smoother surface. J-c values of the YBCO films with Y 2 O 3 particles were either remained nearly the same or decreased for the samples in which YBCO is grown at 780 degree C. On the other hand, J-c values were enhanced for the samples in which YBCO is grown at higher temperature of 800 degree C. The difference in the effect of Y 2 O 3 can be explained by the fact that the higher deposition temperature of 800 degree C reduces intrinsic pinning centers and J c is enhanced by introduction of artificial pinning centers in the form of Y 2 O 3 nanoparticles.

Heat treatment effect on the strain dependence of the critical current for an internal-tin processed Nb3Sn strand

International Nuclear Information System (INIS)

Oh, Sangjun; Park, Soo-Hyeon; Lee, Chulhee; Choi, Heekyung; Kim, Keeman

2010-01-01

A comparative study on the effects of heat treatment, especially, the duration of the A15 reaction temperature plateau on the strain dependence of the critical current for an internal-tin processed Nb 3 Sn strand has been carried out. The strain dependence of the critical current is measured by a variable temperature Walter spiral probe that we have developed. It was shown that prolonged heat treatment can be a very effective way to improve the strain dependency. For a quantitative analysis, the measured data were analyzed with various proposed scaling laws: the scaling law based on strong-coupling theory, the modified deviatoric strain scaling law, and the interpolative scaling law. We found that there is a slight increase in the critical temperature and a substantial improvement in the maximum pinning force. The origin of improved strain dependency is further discussed.

Enhancing Critical Thinking Skills in First Year Environmental Management Students: A Tale of Curriculum Design, Application and Reflection

Science.gov (United States)

Whiley, Dona; Witt, Bradd; Colvin, R. M.; Sapiains Arrue, Rodolfo; Kotir, Julius

2017-01-01

This paper chronicles the experience of academic staff in developing a course to enhance the critical thinking skills of environmental management undergraduates. We outline our considerations and process for course development, discuss insights from course evaluations, and reflect on the challenges encountered. We believe these perspectives will…

Spatial variations in composition in high-critical-current-density Bi-2223 tapes

International Nuclear Information System (INIS)

Holesinger, T. G.; Bingert, J. F.; Teplitsky, M.; Li, Q.; Parrella, R.; Rupich, M. P.; Riley, G. N. Jr.

2000-01-01

A detailed compositional analysis of high-critical-current-density (J c ) (55 and 65 kA/cm2 at 77 K) (Bi, Pb) 2 Sr 2 Ca 2 Cu 3 O y (Bi-2223) tapes was undertaken by energy dispersive spectroscopy in the transmission electron microscope. Structural features were coupled with characteristic compositions of the Bi-2223 phase. The average of all compositional measurements of the Bi-2223 phase was determined to be Bi 1.88 Pb 0.23 Sr 1.96 Ca 1.95 Cu 2.98 O y . However, spatial variations in the Bi-2223 composition and differing phase equilibria were found throughout the filament structure. In particular, a considerable range of Bi-2223 compositions can be found within a single tape, and the lead content of the Bi-2223 phase is significantly depressed in the vicinity of lead-rich phases. The depletion of lead in the Bi-2223 phase around the 3221 phases may be a current-limiting microstructure in these tapes. (c) 2000 Materials Research Society

Pulsed critical current measurements of NbTi in perpendicular and parallel pulsed magnetic fields using the new Cryo-BI-Pulse System

International Nuclear Information System (INIS)

Stehr, V; Tan, K S; Hopkins, S C; Glowacki, B A; Keyser, A De; Bockstal, L Van; Deschagt, J

2006-01-01

Rapid transport current versus high magnetic field characterisation of high-irreversibility type II superconductors is important to maximise their critical parameters. HTS conductors are already used to produce insert coils that increase the fields of conventional magnets made from NbTi (Nb, Ta) 3 Sn and Nb 3 Al wires. There is fundamental interest in the study of HTS tapes and wires in magnetic fields higher than 21T, the current limit of superconducting magnets producing a DC field. Such fields can be obtained by using pulse techniques. High critical currents cannot be routinely measured with a continuous current applied at liquid helium, hydrogen or neon temperatures because of thermal and mechanical effects. A newly developed pulsed magnetic field and pulsed current system which allows rapid J c (B, T) measurements of the whole range of superconducting materials was tested with a multifilamentary NbTi wire in perpendicular and parallel orientations

Critical current simulation in granular superconductors above the percolation threshold

Science.gov (United States)

Riedinger, Roland

1992-02-01

In the phase-coherent regime without applied external magnetic field, the critical superconducting current is limited by intragranular junctions which behave like Josephson junctions. We study the percolation aspects specific to lattices of such junctions and/or the mixing of superconductor with normal grains by averaging over configurations. We illustrate on 2 and 3 dimensional examples. The power laws valid near the percolation threshold are valid well above it, in two and three dimensions. We discuss the other models limiting the superconducting current, the vortex creep and superconducting order parameter fluctuations. Dans la limite de champ magnétique nul et de cohérence de phase du paramètre d'ordre supraconducteur, le courant supraconducteur maximal dans un réseau est limité par les jonctions intergranulaires qui se comportent comme des jonctions Josephson. Nous analysons les problèmes de percolation spécifiques aux réseaux de jonctions et du mélange de grains normaux et supraconducteurs. Nous donnons des exemples bidimensionnels et tridimensionnels ; après moyenne sur les configurations et analyse en taille finie, nous montrons que les lois de puissance valables au voisinage du seuil de percolation s'étendent sur un grand domaine au-delà du seuil de percolation, à deux et trois dimensions. Nous discutons les autres modèles limitant le courant supraconducteur, ancrage de vortex et fluctuations du paramètre d'ordre.

Effect of external magnetic field on critical current for the onset of virtual cathode oscillations in relativistic electron beams

International Nuclear Information System (INIS)

Hramov, Alexander; Koronovskii, Alexey; Morozov, Mikhail; Mushtakov, Alexander

2008-01-01

In this Letter we research the space charge limiting current value at which the oscillating virtual cathode is formed in the relativistic electron beam as a function of the external magnetic field guiding the beam electrons. It is shown that the space charge limiting (critical) current decreases with growth of the external magnetic field, and that there is an optimal induction value of the magnetic field at which the critical current for the onset of virtual cathode oscillations in the electron beam is minimum. For the strong external magnetic field the space charge limiting current corresponds to the analytical relation derived under the assumption that the motion of the electron beam is one-dimensional [D.J. Sullivan, J.E. Walsh, E. Coutsias, in: V.L. Granatstein, I. Alexeff (Eds.), Virtual Cathode Oscillator (Vircator) Theory, in: High Power Microwave Sources, vol. 13, Artech House Microwave Library, 1987, Chapter 13]. Such behavior is explained by the characteristic features of the dynamics of electron space charge in the longitudinal and radial directions in the drift space at the different external magnetic fields

Thinking Critically about Critical Thinking: Integrating Online Tools to Promote Critical Thinking

Directory of Open Access Journals (Sweden)

B. Jean Mandernach

2006-01-01

Full Text Available The value and importance of critical thinking is clearly established; the challenge for instructors lies in successfully promoting students’ critical thinking skills within the confines of a traditional classroom experience. Since instructors are faced with limited student contact time to meet their instructional objectives and facilitate learning, they are often forced to make instructional decisions between content coverage, depth of understanding, and critical analysis of course material. To address this dilemma, it is essential to integrate instructional strategies and techniques that can efficiently and effectively maximize student learning and critical thinking. Modern advances in educational technology have produced a range of online tools to assist instructors in meeting this instructional goal. This review will examine the theoretical foundations of critical thinking in higher education, discuss empirically-based strategies for integrating online instructional supplements to enhance critical thinking, offer techniques for expanding instructional opportunities outside the limitations of traditional class time, and provide practical suggestions for the innovative use of critical thinking strategies via online resources.

Electron mean free path dependence of the critical currents and the pair-breaking limit in superconducting films

International Nuclear Information System (INIS)

Fedorov, N.; Rinderer, L.

1977-01-01

We have studied the current-induced breakdown of superconductivity in wide (100--980 μm) and thin (0.25--0.98 μm) films of tin. It is shown that the current at which the resistance of the sample begins to rise rapidly in the process of the destruction of superconductivity by a current can be fairly well associated with the theoretical value of the pair-breaking current in the Ginzburg-Landau phenomenological approach (I/sub c//sup G L/). This effect is observed over a rather wide temperature region (up to ΔTapprox.0.7 K), depending on the electron mean free path in the films. The values of the critical currents outside the above-mentioned region correlate qualitatively with those determined by inhomogeneities of the films as proposed by Larkin and Ovchinnikov

Improved critical current densities of bulk MgB.sub.2./sub. using carbon-coated amorphous boron

Czech Academy of Sciences Publication Activity Database

Muralidhar, M.; Higuchi, M.; Jirsa, Miloš; Diko, P.; Kokal, I.; Murakami, M.

2017-01-01

Roč. 27, č. 4 (2017), s. 1-4, č. článku 6201104. ISSN 1051-8223 Institutional support: RVO:68378271 Keywords : carbon-encapsulated boron * critical current density * flux pinning * micro-structure Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 1.092, year: 2015

Current-induced nonuniform enhancement of sheet resistance in A r+ -irradiated SrTi O3

Science.gov (United States)

Roy, Debangsu; Frenkel, Yiftach; Davidovitch, Sagi; Persky, Eylon; Haham, Noam; Gabay, Marc; Kalisky, Beena; Klein, Lior

2017-06-01

The sheet resistance Rs of A r+ irradiated SrTi O3 in patterns with a length scale of several microns increases significantly below ˜40 K in connection with driving currents exceeding a certain threshold. The initial lower Rs is recovered upon warming with accelerated recovery around 70 and 160 K. Scanning superconducting quantum interference device microscopy shows local irreversible changes in the spatial distribution of the current with a length scale of several microns. We attribute the observed nonuniform enhancement of Rs to the attraction of the charged single-oxygen and dioxygen vacancies by the crystallographic domain boundaries in SrTi O3 . The boundaries, which are nearly ferroelectric below 40 K, are polarized by the local electrical field associated with the driven current and the clustered vacancies which suppress conductivity in their vicinity and yield a noticeable enhancement in the device resistance when the current path width is on the order of the boundary extension. The temperatures of accelerated conductivity recovery are associated with the energy barriers for the diffusion of the two types of vacancies.

Critical current density, irreversibility line, and flux creep activation energy in silver-sheathed Bi2Sr2Ca2Cu3Ox superconducting tapes

International Nuclear Information System (INIS)

Shi, D.; Wang, Z.; Sengupta, S.; Smith, M.; Goodrich, L.F.; Dou, S.X.; Liu, H.K.; Guo, Y.C.

1992-08-01

Transport data, magnetic hysteresis and flux creep activation energy experimental results are presented for silver-sheathed high-T c Bi 2 Sr 2 Ca 2 Cu 3 O x superconducting tapes. The 110 K superconducting phase was formed by lead doping in a Bi-Sr-Ca-Cu-0 system. The transport critical current density was measured at 4.0 K to be 0.7 x 10 5 A/cm 2 (the corresponding critical current is 74 A) at zero field and 1.6 x 10 4 A/cm 2 at 12 T for H parallel ab. Excellent grain alignment in the a-b plane was achieved by a short-melting method, which considerably improved the critical current density and irreversibility line. Flux creep activation energy as a function of current is obtained based on the magnetic relaxation measurements

Critical current measurements of high-temperature superconducting short samples at a wide range of temperatures and magnetic fields

Science.gov (United States)

Ma, Hongjun; Liu, Huajun; Liu, Fang; Zhang, Huahui; Ci, Lu; Shi, Yi; Lei, Lei

2018-01-01

High-Temperature Superconductors (HTS) are potential materials for high-field magnets, low-loss transmission cables, and Superconducting Magnetic Energy Storage (SMES) due to their high upper critical magnetic field (Hc2) and critical temperature (Tc). The critical current (Ic) of HTS, which is one of the most important parameters for superconductor application, depends strongly on the magnetic fields and temperatures. A new Ic measurement system that can carry out accurate Ic measurement for HTS short samples with various temperatures (4.2-80 K), magnetic fields (0-14 T), and angles of the magnetic field (0°-90°) has been developed. The Ic measurement system mainly consists of a measurement holder, temperature-control system, background magnet, test cryostat, data acquisition system, and DC power supply. The accuracy of temperature control is better than ±0.1 K over the 20-80 K range and ±0.05 K when measured below 20 K. The maximum current is over 1000 A with a measurement uncertainty of 1%. The system had been successfully used for YBa2Cu3O7-x(YBCO) tapes Ic determination with different temperatures and magnetic fields.

Critical current measurements of high-temperature superconducting short samples at a wide range of temperatures and magnetic fields.

Science.gov (United States)

Ma, Hongjun; Liu, Huajun; Liu, Fang; Zhang, Huahui; Ci, Lu; Shi, Yi; Lei, Lei

2018-01-01

High-Temperature Superconductors (HTS) are potential materials for high-field magnets, low-loss transmission cables, and Superconducting Magnetic Energy Storage (SMES) due to their high upper critical magnetic field (H c2 ) and critical temperature (T c ). The critical current (I c ) of HTS, which is one of the most important parameters for superconductor application, depends strongly on the magnetic fields and temperatures. A new I c measurement system that can carry out accurate I c measurement for HTS short samples with various temperatures (4.2-80 K), magnetic fields (0-14 T), and angles of the magnetic field (0°-90°) has been developed. The I c measurement system mainly consists of a measurement holder, temperature-control system, background magnet, test cryostat, data acquisition system, and DC power supply. The accuracy of temperature control is better than ±0.1 K over the 20-80 K range and ±0.05 K when measured below 20 K. The maximum current is over 1000 A with a measurement uncertainty of 1%. The system had been successfully used for YBa 2 Cu 3 O 7-x (YBCO) tapes I c determination with different temperatures and magnetic fields.

Current practices in the identification of critical habitat for threatened species.

Science.gov (United States)

Camaclang, Abbey E; Maron, Martine; Martin, Tara G; Possingham, Hugh P

2015-04-01

The term critical habitat is used to describe the subset of habitat that is essential to the survival and recovery of species. Some countries legally require that critical habitat of listed threatened and endangered species be identified and protected. However, there is little evidence to suggest that the identification of critical habitat has had much impact on species recovery. We hypothesized that this may be due at least partly to a mismatch between the intent of critical habitat identification, which is to protect sufficient habitat for species persistence and recovery, and its practice. We used content analysis to systematically review critical habitat documents from the United States, Canada, and Australia. In particular, we identified the major trends in type of information used to identify critical habitat and in occupancy of habitat identified as critical. Information about population viability was used to identify critical habitat for only 1% of the species reviewed, and for most species, designated critical habitat did not include unoccupied habitat. Without reference to population viability, it is difficult to determine how much of a species' occupied and unoccupied habitat will be required for persistence. We therefore conclude that the identification of critical habitat remains inconsistent with the goal of protecting sufficient habitat to support persistence and recovery of the species. Ensuring that critical habitat identification aligns more closely with its intent will improve the accuracy of the designations and may therefore help improve the benefits to species recovery when combined with adequate implementation and enforcement of legal protections. © 2014 Society for Conservation Biology.

Critical current density measurement of thin films by AC susceptibility based on the penetration parameter h

DEFF Research Database (Denmark)

Li, Xiao-Fen; Grivel, Jean-Claude; Abrahamsen, Asger B.

2012-01-01

We have numerically proved that the dependence of AC susceptibility χ of a E(J) power law superconducting thin disc on many parameters can be reduced to one penetration parameter h, with E the electric field and J the current density. Based on this result, we propose a way of measuring the critical...... current density Jc of superconducting thin films by AC susceptibility. Compared with the normally used method based on the peak of the imaginary part, our method uses a much larger range of the AC susceptibility curve, thus allowing determination of the temperature (T) dependence of Jc from a normally...

Identifying Critical Thinking Styles to Enhance Volunteer Development

Science.gov (United States)

Gay, Keegan D.; Terry, Bryan; Lamm, Alexa J.

2015-01-01

Diversity in learning options can increase efficacy of volunteer development systems. The University of Florida Critical Thinking Inventory (UFCTI) is designed to explicate an individual's critical thinking style based upon a continuum from Seeking Information to Engagement. Static and interpretive materials are best used with individuals of a…

Determination of the inter- and intra-granular critical currents in superconducting YBa2Cu3O7 welds

International Nuclear Information System (INIS)

Bozzo, B; Iliescu, S; Bartolome, E; Palau, A; Granados, X; Puig, T; Obradors, X; Amoros, J; Carrera, M

2005-01-01

A method for determining simultaneously the inter- and intra-grain critical currents has been developed in welded YBa 2 Cu 3 O 7 (YBCO) ceramics by solving the Inverse Problem for local maps of the magnetic field in the remanent state. From that current distribution, the current density flowing through the superconducting weld as well as the current density circulating inside the grains can be deduced. The method is discussed and it is applied to several examples of YBCO/Ag/YBCO welds. The results obtained show that it is possible to obtain superconducting joints with a quality at the same level as that of the starting material

Critical Education, Critical Pedagogies, Marxist Education in the United States

Science.gov (United States)

Foley, Jean Ann; Morris, Doug; Gounari, Panayota; Agostinone-Wilson, Faith

2015-01-01

As critical pedagogy becomes more mainstream on the educational landscape in the United States, it is important to revisit the original tenets of critical pedagogy and explore their current manifestations. Since the beginning of "criticalism" from the theoretical/foundational work of the Frankfurt School of Critical Social Theory,…

Transcranial direct current stimulation (tDCS) to improve naming ability in post-stroke aphasia: A critical review.

Science.gov (United States)

ALHarbi, Mohammed F; Armijo-Olivo, Susan; Kim, Esther S

2017-08-14

Transcranial Direct Current Stimulation (tDCS) is a non-invasive neuromodulation tool that can be used to influence cortical brain activity to induce measurable behavioral changes. Although there is growing evidence that tDCS combined with behavioural language therapy could boost language recovery in patients with post-stroke aphasia, there is great variability in patient characteristics, treatment protocols, and outcome measures in these studies that poses challenges for analyzing the evidence. The purpose of this study is to critically analyze the methodological rigor of the evidence regarding the use of tDCS for post-stroke anomia. This critical review was conducted by searching four databases (MEDLINE, EMBase, PsycINFO, and CINAHL). Nineteen studies fully met the inclusion criteria. Three critical appraisal tools and Robey and Schultz's (1998) five- phase model for conducting clinical outcome research were adopted to evaluate and analyze the current level of evidence. Methodological issues of the studies were also identified. The current level of evidence for using tDCS for anomia is at the pre-efficacy level with emerging evidence at the efficacy level. Lack of proper evaluation of carry-over effects in cross-over studies, lack of or unclear randomization, allocation concealment, and incomplete data handling were the main methodological issues that could threaten the validity of the tDCS for anomia studies. Several methodological issues have been identified in pre-efficacy studies that pose challenges in determining whether tDCS is a beneficial adjunct to behavioral aphasia therapy. Future studies need to improve the quality of the methods used to investigate the effect of tDCS for anomia. Copyright © 2017 Elsevier B.V. All rights reserved.

Fostering critical thinking skills: a strategy for enhancing evidence based wellness care

Directory of Open Access Journals (Sweden)

Jamison Jennifer R

2005-09-01

Full Text Available Abstract Chiropractic has traditionally regarded itself a wellness profession. As wellness care is postulated to play a central role in the future growth of chiropractic, the development of a wellness ethos acceptable within conventional health care is desirable. This paper describes a unit which prepares chiropractic students for the role of "wellness coaches". Emphasis is placed on providing students with exercises in critical thinking in an effort to prepare them for the challenge of interfacing with an increasingly evidence based health care system. Methods This case study describes how health may be promoted and disease prevented through development of personalized wellness programs. As critical thinking is essential to the provision of evidence based wellness care, diverse learning opportunities for developing and refining critical thinking skills have been created. Three of the learning opportunities are an intrinsic component of the subject and, taken together, contributed over 50% of the final grade of the unit. They include a literature review, developing a client wellness contract and peer evaluation. In addition to these 3 compulsory exercises, students were also given an opportunity to develop their critical appraisal skills by undertaking voluntary self- and unit evaluation. Several opportunities for informal self-appraisal were offered in a structured self-study guide, while unit appraisal was undertaken by means of a questionnaire and group discussion at which the Head of School was present. Results Formal assessment showed all students capable of preparing a wellness program consistent with current thinking in contemporary health care. The small group of students who appraised the unit seemed to value the diversity of learning experiences provided. Opportunities for voluntary unit and self-appraisal were used to varying degrees. Unit evaluation provided useful feedback that led to substantial changes in unit structure

High-transport current density up to 30 T in bulk YBa2Cu3O7 and the critical angle effect

International Nuclear Information System (INIS)

Ekin, J.W.; Salama, K.; Selvamanickam, V.

1991-01-01

Measurements of the dc transport critical current of oriented-grained YBa 2 Cu 3 O 7 have been made using high quality Ag contacts and a high-current sample mount. The critical- current density J c at 77 K for mutually perpendicular current and magnetic field B in the a,b plane is 8 kA/cm 2 at 8 T, decreasing gradually to 3.7 kA/cm 2 at 20 T, and remaining over 1 kA/cm 2 out to 30 T. High magnetic field measurements of J c as a function of the angle θ of B with respect to the c axis are also reported. In contrast to earlier results at lower fields ( c vs θ curve with a head-and-shoulders shape, consisting of a sharp peak (''head'') 2 planes, and a wide (30 degree at 9 T, for example) shoulder region on either side of B perpendicular c, where the transport J c remains high and constant. Beyond the shoulder region, however, the transport J c decreases sharply, giving rise to the concept of a critical field angle for application design, defined by the minima in d 2 J c /dθ 2 at the edge of the shoulders

Critical role of NKT cells in posttransplant alloantibody production.

Science.gov (United States)

Zimmerer, J M; Swamy, P; Sanghavi, P B; Wright, C L; Abdel-Rasoul, M; Elzein, S M; Brutkiewicz, R R; Bumgardner, G L

2014-11-01

We previously reported that posttransplant alloantibody production in CD8-deficient hosts is IL-4+ CD4+ T cell-dependent and IgG1 isotype-dominant. The current studies investigated the hypothesis that IL-4-producing natural killer T cells (NKT cells) contribute to maximal alloantibody production. To investigate this, alloantibody levels were examined in CD8-deficient WT, CD1d KO and Jα18 KO transplant recipients. We found that the magnitude of IgG1 alloantibody production was critically dependent on the presence of type I NKT cells, which are activated by day 1 posttransplant. Unexpectedly, type I NKT cell contribution to enhanced IgG1 alloantibody levels was interferon-γ-dependent and IL-4-independent. Cognate interactions between type I NKT and B cells alone do not stimulate alloantibody production. Instead, NKT cells appear to enhance maturation of IL-4+ CD4+ T cells. To our knowledge, this is the first report to substantiate a critical role for type I NKT cells in enhancing in vivo antibody production in response to endogenous antigenic stimuli. © Copyright 2014 The American Society of Transplantation and the American Society of Transplant Surgeons.

c-Axis correlated extended defects and critical current in YBa2Cu3Ox films grown on Au and Ag-nano dot decorated substrates

International Nuclear Information System (INIS)

Mikheenko, P.; Sarkar, A.; Dang, V.-S.; Tanner, J.L.; Abell, J.S.; Crisan, A.

2009-01-01

We report measurements of critical current in YBa 2 Cu 3 O x films deposited on SrTiO 3 substrates decorated with silver and gold nanodots. An increase in critical current in these films, in comparison with the films deposited on non-decorated substrates, has been achieved. We argue that this increase comes from the c-axis correlated extended defects formed in the films and originated from the nanodots. Additionally to creating extended defects, the nanodots pin them and prevent their exit from the sample during the film growth, thus keeping a high density of defects and providing a lower rate of decrease of the critical current with the thickness of the films. The best pinning is achieved in the samples with silver nanodots by optimising their deposition temperature. The nanodots grown at a temperature of a few hundred deg. C have a small diameter of a few nanometres and a high surface density of 10 11 -10 12 particles/cm 2 . We give evidence of c-axis correlated extended defects in YBa 2 Cu 3 O x films by planar and cross-sectional atomic force microscopy, transmission electron microscopy and angle-dependent transport measurements of critical current.

Neurostimulation for Memory Enhancement in Epilepsy.

Science.gov (United States)

Meisenhelter, Stephen; Jobst, Barbara C

2018-04-19

Memory is one of the top concerns of epilepsy patients, but there are no known treatments to directly alleviate the memory deficits associated with epilepsy. Neurostimulation may provide new therapeutic tools to enhance memory in epilepsy patients. Here, we critically review recent investigations of memory enhancement using transcranial electrical stimulation (tES), transcranial magnetic stimulation (TMS), vagus nerve stimulation (VNS), chronic intracranial stimulation, and acute intracranial stimulation. Existing literature suggests that transcranial direct current stimulation (tDCS) produces a small enhancement in memory in neuropsychological patients, but transcranial alternating current stimulation (tACS) and transcranial random noise stimulation (tRNS) have not been found to have an effect on memory. Most studies of transcranial magnetic stimulation (TMS) have found that TMS has no positive effect on memory. Vagus nerve stimulation can acutely enhance memory, while chronic therapy does not appear to alter memory performance. We found that there is the most evidence for significant memory enhancement using intracranial stimulation techniques, especially chronic stimulation of the fornix and task-responsive stimulation of the lateral temporal lobe. Presently, there are no existing therapeutic options for directly treating epilepy-related memory deficits. While neurostimulation technologies for memory enhancement are largely still in the experimental phase, neurostimulation appears promising as a future technique for treating epilepsy-related memory deficits.

A hybrid superconducting fault current limiter for enhancing transient stability in Korean power systems

Science.gov (United States)

Seo, Sangsoo; Kim, Seog-Joo; Moon, Young-Hwan; Lee, Byongjun

2013-11-01

Additional power generation sites have been limited in Korea, despite the fact load demands are gradually increasing. In order to meet these increasing demands, Korea’s power system company has begun constructing new generators at existing sites. Thus, multi-unit plants can create problems in terms of transient stability when a large disturbance occurs. This paper proposes a hybrid superconducting fault current limiter (SFCL) application to enhance the transient stability of multi-unit power plants. SFCLs reduce fault currents, and limitation currents decrease the imbalance of the mechanical and electrical torque of the generators, resulting in an improvement in transient stability.

Strain induced irreversible critical current degradation in highly dense Bi-2212 round wire

CERN Document Server

Bjoerstad, R; Rikel, M.O.; Ballarino, A; Bottura, L; Jiang, J; Matras, M; Sugano, M; Hudspeth, J; Di Michiel, M

2015-01-01

The strain induced critical current degradation of overpressure processed straight Bi 2212/Ag wires has been studied at 77 K in self-field. For the first time superconducting properties, lattice distortions, composite wire stress and strain have been measured simultaneously in a high energy synchrotron beamline. A permanent Ic degradation of 5% occurs when the wire strain exceeds 0.60%. At a wire strain of about 0.65% a drastic n value and Ic reduction occur, and the composite stress and the Bi-2212 lattice parameter reach a plateau, indicating Bi-2212 filament fracturing. The XRD measurements show that Bi-2212 exhibits linear elastic behaviour up to the irreversible strain limit.

The Impacts of 'Problem-Based Learning’ Approach in Enhancing Critical Thinking Skills to Teaching Literature

Directory of Open Access Journals (Sweden)

Mairas Abd Rahman

2016-11-01

Full Text Available Teaching can be challenging task especially when the students are categorized as reluctant readers, low self-motivated and lack of critical thinking skills. Therefore, this study focuses on a successful problem-based learning approach on university course called ‘Literature for Language Purposes' taken by Bachelor of English with Communication students at a local Malaysian university. The aim of this study is to investigate the impacts of carrying out problem-based learning in teaching literature. The project involved 55 undergraduates and part of their major course assignments was to organize and participate in an annual English language drama competition. The data was collected through students’ reflective journals, researchers’ reflective journals, response from end of semester questionnaire given and, lecturers’ evaluation on FILA tables. The findings show that problem-based learning is suitable and beneficial in teaching and enhancing critical thinking skills.

Magnetic Criticality Enhanced Hybrid Nanodiamond Thermometer under Ambient Conditions

Science.gov (United States)

Wang, Ning; Liu, Gang-Qin; Leong, Weng-Hang; Zeng, Hualing; Feng, Xi; Li, Si-Hong; Dolde, Florian; Fedder, Helmut; Wrachtrup, Jörg; Cui, Xiao-Dong; Yang, Sen; Li, Quan; Liu, Ren-Bao

2018-01-01

Nitrogen-vacancy (NV) centers in diamond are attractive as quantum sensors owing to their superb coherence under ambient conditions. However, the NV center spin resonances are relatively insensitive to some important parameters such as temperature and pressure. Here we design and experimentally demonstrate a hybrid nanothermometer composed of NV centers and a magnetic nanoparticle (MNP), in which the temperature sensitivity is enhanced by the critical magnetization of the MNP near the ferromagnetic-paramagnetic transition temperature. The temperature susceptibility of the NV center spin resonance reaches 14 MHz /K , nearly 200 times larger than that of bare NV centers. The sensitivity of a hybrid nanothermometer composed of a Cu1 -xNix MNP and a nanodiamond is measured to be 11 mK /√{Hz } under ambient conditions. The working range of the hybrid thermometer can be designed from cryogenic temperature to about 600 K by tuning the chemical composition of the Cu1 -xNix MNP. We demonstrate in situ detection of the magnetic phase transition of a single magnetic nanoparticle using the hybrid nanothermometer. This hybrid nanothermometer provides a novel approach to studying a broad range of thermal processes at nanoscales such as nanoplasmonics, heat-stimulated subcellular processes, and thermodynamics of nanosystems.

Magnetic Criticality Enhanced Hybrid Nanodiamond Thermometer under Ambient Conditions

Directory of Open Access Journals (Sweden)

Ning Wang

2018-03-01

Full Text Available Nitrogen-vacancy (NV centers in diamond are attractive as quantum sensors owing to their superb coherence under ambient conditions. However, the NV center spin resonances are relatively insensitive to some important parameters such as temperature and pressure. Here we design and experimentally demonstrate a hybrid nanothermometer composed of NV centers and a magnetic nanoparticle (MNP, in which the temperature sensitivity is enhanced by the critical magnetization of the MNP near the ferromagnetic-paramagnetic transition temperature. The temperature susceptibility of the NV center spin resonance reaches 14  MHz/K, nearly 200 times larger than that of bare NV centers. The sensitivity of a hybrid nanothermometer composed of a Cu_{1-x}Ni_{x} MNP and a nanodiamond is measured to be 11  mK/sqrt[Hz] under ambient conditions. The working range of the hybrid thermometer can be designed from cryogenic temperature to about 600 K by tuning the chemical composition of the Cu_{1-x}Ni_{x} MNP. We demonstrate in situ detection of the magnetic phase transition of a single magnetic nanoparticle using the hybrid nanothermometer. This hybrid nanothermometer provides a novel approach to studying a broad range of thermal processes at nanoscales such as nanoplasmonics, heat-stimulated subcellular processes, and thermodynamics of nanosystems.

AC losses in a type II superconductor strip with inhomogeneous critical current distribution

International Nuclear Information System (INIS)

Tsukamoto, Osami

2005-01-01

Analytical formulae derived by Brandt and Indenbom (1993 Phys. Rev. B 48 12893-906) and Norris (1970 J. Phys. D: Appl. Phys. 3 489-507) are often used to calculate the magnetization and AC transport current losses in HTS strip conductors, respectively. In these formulae, homogeneous distribution of critical sheet current density σ c in the strip is assumed. However, it is considered that σ c distributions are inhomogeneous in actual HTS strips and that the inhomogeneous σ c distributions cause deviations of the measured AC loss data of actual HTS strips from those formulae. A semi-analytical method to calculate AC transport current and magnetization losses is derived for a type II superconductor strip with inhomogeneous distribution of σ c in the direction of the strip width. The method is derived modifying the analysis of Brandt et al. The validity of the semi-analytical method is shown by comparing the results calculated by this method with those calculated by the Norris and Brandt formulae and by a different method of our previous work and also with experimental data. Moreover, it is shown that the deviation of the measured data from the Norris and Brandt models can be estimated by assuming proper σ c distributions

Can critical inquiry differ from criticism? A dialogue with current occupational science and occupational therapy schools of inquiry

Directory of Open Access Journals (Sweden)

Jessie Wilson

2016-07-01

Full Text Available Introduction: Critical inquiry has been adopted by various academic disciplines. However, there is a lack of consistency and transparency in the way this complex theoretical and methodological position is applied in research. For novice researchers that ambiguity can lead to blurring the conceptual distinction between critical research and the act of criticizing. Objective: The purpose of this essay is to reflect on what it means to keep a critical perspective for novice researchers. Method: The concepts are explored through a personal narrative that allows authors to examine the details of their trajectory to embrace a critical perspective, which has the power to lead to change, both personal and social. Results: We explore the methodological foundations of the critical research and observe how the emotion is taken over or suppressed in the investigation process. Conclusion: We contextualize key concepts of critical investigation, examining its recent application both in occupational science and in occupational therapy.

Transport measurements in superconductors: critical current of granular high TC ceramic superconductor samples; Medidas de transporte em supercondutores: corrente critica de supercondutores granulares de alta temperatura critica

Energy Technology Data Exchange (ETDEWEB)

Passos, W.A.C., E-mail: wagner.passos@univasf.edu.br [Universidade Federal do Vale do Sao Francisco (IPCM/UNIVASF), Juazeiro do Norte, BA (Brazil). Instituto de Pesquisas em Ciencia dos Materiais; Silva, E.B. [Companhia Energetica do Sao Francisco (CHESF), Recife, PE (Brazil)

2016-07-01

This work presents a method to obtain critical current of granular superconductors. We have carried out transport measurements (ρxT curves and VxI curves) in a YBa{sub 2}Cu{sub 3}O{sub 7-δ} sample to determine critical current density of it. Some specimens reveal a 'semiconductor-like' behavior (electrical resistivity decreases with increasing temperatures above critical temperature T{sub c} of material) competing with superconductor behavior. Due to high granular fraction of the sample, these competition is clearly noted in ρxT curves. Measurements carried out from 0 to 8500 Oe of applied field show the same behavior, and the critical current density of the samples is shown. (author)

Choice of sample size for high transport critical current density in a granular superconductor: percolation versus self-field effects

International Nuclear Information System (INIS)

Mulet, R.; Diaz, O.; Altshuler, E.

1997-01-01

The percolative character of the current paths and the self-field effects were considered to estimate optimal sample dimensions for the transport current of a granular superconductor by means of a Monte Carlo algorithm and critical-state model calculations. We showed that, under certain conditions, self-field effects are negligible and the J c dependence on sample dimensions is determined by the percolative character of the current. Optimal dimensions are demonstrated to be a function of the fraction of superconducting phase in the sample. (author)

Enhanced transport currents in Cu-sheathed MgB{sub 2} wires

Energy Technology Data Exchange (ETDEWEB)

Eisterer, M; Weber, H W [Atomic Institute of the Austrian Universities, Vienna (Austria); Glowacki, B A [Department of Materials Science and Metallurgy, University of Cambridge, Cambridge (United Kingdom); Pacific Northwest National Laboratory, Richland, WA (United States); Greenwood, L R [Pacific Northwest National Laboratory, Richland, WA (United States); Majoros, M [Interdisciplinary Research Centre in Superconductivity, University of Cambridge, Cambridge (United Kingdom)

2002-07-01

Copper-sheathed MgB{sub 2} wires, prepared by an in-situ process, were exposed to neutron radiation in order to introduce defects into the superconductor. The high level of disorder (4.6x10{sup -2} dpa) leads to a decrease of the transition temperature by more than 4 K, but to an increase of the slope of the irreversibility line, thus resulting in higher irreversibility fields at low temperatures. The transport currents are significantly enhanced at 4.2 K for fields above 2 T. (author)

The low-temperature, high-magnetic-field critical current characteristics of Zr-added (Gd, Y)Ba2Cu3Ox superconducting tapes

Energy Technology Data Exchange (ETDEWEB)

Selvamanickam, V; Yao, Y; Chen, Y; Shi, T; Liu, Y; Khatri, ND; Liu, J; Lei, C; Galstyan, E; Majkic, G

2012-10-26

Critical current performances of state-of-the-art Zr-added (Gd, Y)BaCuO tapes have been investigated over a temperature range of 20-77 K, in magnetic fields up to 9 T and over a wide angular range of magnetic field orientations. The peak in critical current that is commonly observed in the field orientation perpendicular to the tape in BaZrO3 (BZO) containing superconducting tapes is found to vanish at 30 K in magnetic fields at 1-9 T. While the critical current of 15% Zr-added tapes was about 40% lower than that of 7.5% Zr-added tapes at 77 K, the pinning force values of the former were found to be 18-23% higher than those of the latter in the temperature range of 20-40 K and in magnetic fields of 3-5 T. The results from this study emphasize the importance of optimization of coated conductor fabrication processes for optimum performance not just in low magnetic fields at 77 K but also at the operating conditions of low temperatures and high magnetic fields that are of interest, especially for rotating superconducting machinery applications.

The low-temperature, high-magnetic-field critical current characteristics of Zr-added (Gd,Y)Ba2Cu3Ox superconducting tapes

International Nuclear Information System (INIS)

Selvamanickam, V; Yao, Y; Shi, T; Liu, Y; Khatri, N D; Liu, J; Galstyan, E; Majkic, G; Chen, Y; Lei, C

2012-01-01

Critical current performances of state-of-the-art Zr-added (Gd, Y)BaCuO tapes have been investigated over a temperature range of 20–77 K, in magnetic fields up to 9 T and over a wide angular range of magnetic field orientations. The peak in critical current that is commonly observed in the field orientation perpendicular to the tape in BaZrO 3 (BZO) containing superconducting tapes is found to vanish at 30 K in magnetic fields at 1–9 T. While the critical current of 15% Zr-added tapes was about 40% lower than that of 7.5% Zr-added tapes at 77 K, the pinning force values of the former were found to be 18–23% higher than those of the latter in the temperature range of 20–40 K and in magnetic fields of 3–5 T. The results from this study emphasize the importance of optimization of coated conductor fabrication processes for optimum performance not just in low magnetic fields at 77 K but also at the operating conditions of low temperatures and high magnetic fields that are of interest, especially for rotating superconducting machinery applications. (paper)