  1. Morphological changes produced by acid dissolution in Er:YAG laser irradiated dental enamel.

    Science.gov (United States)

    Manuela Díaz-Monroy, Jennifer; Contreras-Bulnes, Rosalía; Fernando Olea-Mejía, Oscar; Emma Rodríguez-Vilchis, Laura; Sanchez-Flores, Ignacio

    2014-06-01

    Several scientific reports have shown the effects of Er:YAG laser irradiation on enamel morphology. However, there is lack of information regarding the morphological alterations produced by the acid attack on the irradiated surfaces. The aim of this study was to evaluate the morphological changes produced by acid dissolution in Er:YAG laser irradiated dental enamel. Forty-eight enamel samples were divided into four groups (n = 12). GI (control); Groups II, III, and IV were irradiated with Er:YAG at 100 mJ (12.7 J/cm(2) ), 200 mJ (25.5 J/cm(2) ), and 300 mJ (38.2 J/cm(2) ), respectively, at 10 Hz without water irrigation. Enamel morphology was evaluated before-irradiation, after-irradiation, and after-acid dissolution, by scanning electron microscopy (SEM). Sample coating was avoided and SEM analysis was performed in a low-vacuum mode. To facilitate the location of the assessment area, a reference point was marked. Morphological changes produced by acid dissolution of irradiated enamel were observed, specifically on laser-induced undesired effects. These morphological changes were from mild to severe, depending on the presence of after-irradiation undesired effects. © 2014 Wiley Periodicals, Inc.

  2. Effects of blue light irradiation on dental enamel remineralization in vitro

    International Nuclear Information System (INIS)

    Kato, Ilka Tiemy

    2009-01-01

    This study aimed to investigate the effects of blue radiation on dental enamel remineralization. In addition, a methodology of analysis was developed to evaluate alterations of enamel mineral content by optical coherence tomography. Artificial lesions were formed in bovine dental enamel slabs by immersing the samples in under saturated acetate buffer (2 mL/mm 2 e 6.25 mL/mm 2 ). The lesions were irradiated with blue LED (l=455±20nm), with radiant power of 110 mW, irradiance of 1.4 W/cm 2 , radiant exposure of 13.8 J/ c m2 and exposure time of 10 s. Remineralization was induced by pH-cycling model during 8 days. Cross-sectional hardness and optical coherence tomography (OCT) were used to assess mineral changes after remineralization. Hardness data showed that non-irradiated enamel lesions presented higher mineral content than irradiated ones and this difference was more evident in lesions formed in higher solution volume. The analysis of OCT signal also demonstrated that the mineral content of non-irradiated group was higher than in irradiated one; however, no significant difference was observed. Furthermore, significant differences in OCT sign were detected between sound and demineralized enamel. Based on the results obtained in the present study it can be concluded that blue radiation caused an inhibition of enamel remineralization. The methodology adopted for OCT analysis allowed the quantification of enamel mineral loss; however, the remineralization process could not be evaluated by this technique. (author)

  3. Human dental enamel and dentin structural effects after Er:YAG laser irradiation.

    Science.gov (United States)

    Lima, Darlon Martíns; Tonetto, Mateus Rodrigues; de Mendonça, Adriano Augusto Melo; Elossais, André Afif; Saad, José Roberto Cury; de Andrade, Marcelo Ferrarezi; Pinto, Shelon Cristina Souza; Bandéca, Matheus Coelho

    2014-05-01

    Ideally projected to be applied on soft tissues, infrared lasers were improved by restorative dentistry to be used in hard dental tissues cavity preparations--namely enamel and dentin. This paper evidentiates the relevant aspects of infrared Erbium laser's action mechanism and its effects, and characterizes the different effects deriving from the laser's beams emission. The criteria for use and selection of optimal parameters for the correct application of laser systems and influence of supporting factors on the process, such as water amount and its presence in the ablation process, protection exerted by the plasma shielding and structural factors, which are indispensable in dental tissues cavity preparation related to restorative technique, are subordinated to optical modifications caused by the interaction of the energy dissipated by these laser light emission systems in the targeted tissue substrate. Differences in the action of infrared Erbium laser system in regard to the nature of the ablation process and variations on the morphological aspects observed in the superficial structure of the target tissue irradiated, may be correlated to the structural optical modifications of the substrate produced by an interaction of the energy propagated by laser systems.

  4. Sub ablative Er: YAG laser irradiation on surface roughness of eroded dental enamel.

    Science.gov (United States)

    Curylofo-Zotti, Fabiana Almeida; Lepri, Taísa Penazzo; Colucci, Vivian; Turssi, Cecília Pedroso; Corona, Silmara Aparecida Milori

    2015-11-01

    This study evaluated the effects of Er:YAG laser irradiation applied at varying pulse repetition rate on the surface roughness of eroded enamel. Bovine enamel slabs (n = 10) were embedded in polyester resin, ground, and polished. To erosive challenges, specimens were immersed two times per day in 20mL of concentrated orange juice (pH = 3.84) under agitation, during a two-day period. Specimens were randomly assigned to irradiation with the Er:YAG laser (focused mode, pulse energy of 60 mJ and energy density of 3.79 J/cm(2) ) operating at 1, 2, 3, or 4 Hz. The control group was left nonirradiated. Surface roughness measurements were recorded post erosion-like formation and further erosive episodes by a profilometer and observed through atomic force microscopy (AFM). Analysis of variance revealed that the control group showed the lowest surface roughness, while laser-irradiated substrates did not differ from each other following post erosion-like lesion formation. According to analysis of covariance, at further erosive episodes, the control group demonstrated lower surface roughness (P > 0.05), than any of the irradiated groups (P enamel eroded. The AFM images showed that the specimens irradiated by the Er:YAG laser at 1 Hz presented a less rough surface than those irradiated at 2, 3, and 4 Hz. © 2015 Wiley Periodicals, Inc.

  5. Radiation exposure during in-vivo analysis of human dental enamel by proton irradiation

    International Nuclear Information System (INIS)

    Baijot-Stroobants, J.; Bodart, F.; Deconninck, G.; Vreven, J.

    Fluorine can be analysed by proton activation, with detection of prompt γ-rays. Using external beams, it is possible to make in-vivo determinations and to follow the concentration in fluoridated enamel. Radiation damage and radiation hazards are investigated. It is found that the dose rate is very small and that the technique can be used without radiation problems. Local destruction on the enamel surface is investigated using a scanning microscope, no modification is observed in the cristallite structure after irradiation. (author)

  6. Weaker dental enamel explains dental decay.

    Science.gov (United States)

    Vieira, Alexandre R; Gibson, Carolyn W; Deeley, Kathleen; Xue, Hui; Li, Yong

    2015-01-01

    Dental caries continues to be the most prevalent bacteria-mediated non-contagious disease of humankind. Dental professionals assert the disease can be explained by poor oral hygiene and a diet rich in sugars but this does not account for caries free individuals exposed to the same risk factors. In order to test the hypothesis that amount of amelogenin during enamel development can influence caries susceptibility, we generated multiple strains of mice with varying levels of available amelogenin during dental development. Mechanical tests showed that dental enamel developed with less amelogenin is "weaker" while the dental enamel of animals over-expressing amelogenin appears to be more resistant to acid dissolution.

  7. Nanostructured synthetic hydroxyapatite and dental enamel heated and irradiated by ER,CR:YSGG: characterized by FTIR and XRD

    International Nuclear Information System (INIS)

    Rabelo Neto, Jose da Silva

    2009-01-01

    The study evaluate the physical changes and/or chemical that occurs in synthetic hydroxyapatite (HAP) and in enamel under action of thermal heating in oven or laser irradiation of Er,Cr:YSGG that may cause changes in its structure to make them more resistant to demineralization aiming the formation of dental caries. The synthetic HAP was produced by reaction of solutions of Ca(NO 3 ) and (NH 4 ) 2 HPO 4 with controlled temperature and pH. The enamel powder was collected from the bovine teeth. Samples of powder enamel and synthetic HAP were subjected to thermal heating in oven at temperatures of 200 deg C, 400 deg C, 600 deg C, 800 deg C and 1000 deg C. For the laser irradiation of materials, were made with 5,79 J/cm 2 of irradiation, 7,65 J/cm 2 , 10,55 J/cm 2 and 13,84 J/cm 2 for synthetic HAP and 7,53 J/cm 2 , 10,95 J/cm 2 , and 13,74 J/cm 2 for the enamel. The samples were evaluated by X-ray diffraction (XRD) for analysis of crystallographic phases and analysis by the Rietveld method, to determine their respective proportions in the material, as well as results of changes of the lattice unit cell parameters (axis-a, axis-c and volume), crystallites sizes and the occupation rate of sites of Ca and P atoms. The samples were analyzed by Fourier transform infrared spectroscopy (FTIR), which should compositional changes due to treatment related to carbonate, phosphate, adsorbed water and hydroxyl radicals content. The infrared was used to measure the surface temperature generated by the laser beam in the solid samples of enamel. Besides the major hydroxyapatite crystallographic phases, there was formations of octa calcium phosphate (OCP) and phase β of tricalcium phosphate (β-TCP ) in enamel heated at 800 deg C. There was reduction of the axis-a, volume and size of crystallites to the temperatures between 400 degree C and 600 deg C and also on laser irradiated samples. Above the temperature of 600 degree C it is observed the effect in the lattice parameters. The Ca

  8. In vitro study of morphological and chemical modification threshold of bovine dental enamel irradiated by the holmium laser

    International Nuclear Information System (INIS)

    Eduardo, Patricia Lerro de Paula

    2001-01-01

    The aim of this study is to investigate the Ho:YLF laser effects on the dental enamel surface with regards to its morphology, thermal variations during its irradiation in the pulp chamber and its increased resistance to demineralization through quantitative analysis of calcium and phosphorous atoms reactive concentrations in samples. Twenty samples of bovine enamel were used and divided in four groups: control - acidulated phosphate fluoride (APF) application followed by demineralization treatment with lactic acid; irradiation with Ho:YLF laser (100 J/cm 2 ) followed by APF topic application and demineralization treatment with lactic acid; irradiation with Ho:YLF laser (350 J/cm 2 ) followed by APF topic application and demineralization treatment with lactic acid: and irradiation with Ho:YLF laser ( 450 J/cm 2 ) followed by APF topic application and demineralization treatment with lactic acid. Ali samples were quantified according to their calcium and phosphorous atoms relative concentrations before and after the treatments above. X-Ray fluorescence spectrochemical analysis and scanning electron microscopy were carried out. It was observed an increase on the calcium and phosphorous atoms concentration ratio and therefore the enamel demineralization reduction as a result of the lactic acid treatment in the samples irradiated with the holmium laser followed by the APF application. In order to evaluate the feasibility of this study for clinical purposes, morphological changes caused by the holmium laser irradiation were analyzed. Such modifications were characterized by melted and re-solidified regions of the enamel with consequent changes on its permeability and solubility. Temperature changes of ten human pre-molars teeth irradiated with 350 J/cm 2 and 450 J/cm 2 were also monitored in the pulp chamber in real time. Temperature increases over 4,20 C did not occur. The results obtained from this study along with the results from previous researches developed at

  9. Study in vitro of dental enamel irradiated with a high power diode laser operating at 960 nm: morphological analysis of post-irradiation dental surface and thermal effect analysis in pulp chamber due to laser application

    International Nuclear Information System (INIS)

    Quinto Junior, Jose

    2001-01-01

    Objectives: This study examines the structural and thermal modifications induced in dental enamel under dye assisted diode laser irradiation. The aim of this study is to verify if this laser-assisted treatment is capable to modify the enamel surface by causing fusion of the enamel surface layer. At the same time, the pulpal temperature rise must be kept low enough in order not to cause pulpar necrosis. To achieve this target, it is necessary to determine suitable laser parameters. As is known, fusion of the enamel surface followed by re-solidification produce a more acid resistant layer. This surface treatment is being researched as a new method for caries prevention. Method and Materials: A series of fourteen identically prepared enamel samples of human teeth were irradiated with a high power diode laser operating at 960 nm and using fiber delivery. Prior to irradiation, a fine layer of cromophorous ink was applied to the enamel surface. In the first part of the experiment the best parameter for pulse duration was determined. In the second part of the experimental phase the same energy density was used but with different repetition rates. During irradiation we monitored the temperature rise in the pulpal cavity. The morphology of the treated samples was analysed under SEM. Results: The morphology of the treated samples showed a homogeneously re-solidified enamel layer. The results of the temperature analysis showed a decrease of the pulpal temperature rise with decreasing repetition rate. Conclusion: With the diode laser it is possible to cause morphological alterations of the enamel surface, which is known to increase the enamel resistance against acid attack, and still maintain the temperature rise in the pulpar chamber below damage threshold. (author)

  10. Synergistic effect of fluoride and laser irradiation for the inhibition of the demineralization of dental enamel

    Science.gov (United States)

    Lee, Raymond; Chan, Kenneth H.; Jew, Jamison; Simon, Jacob C.; Fried, Daniel

    2017-02-01

    Both laser irradiation and fluoride treatment alone are known to provide increased resistance to acid dissolution. CO2 lasers tuned to a wavelength of 9.3 μm can be used to efficiently convert the carbonated hydroxyapatite of enamel to a much more acid resistant purer phase hydroxyapatite (HAP). Further studies have shown that fluoride application to HAP yields fluoroapatite (FAP) which is even more resistant against acid dissolution. Previous studies show that CO2 lasers and fluoride treatments interact synergistically to provide significantly higher protection than either method alone, but the mechanism of interaction has not been elucidated. We recently observed the formation of microcracks or a "crazed" zone in the irradiated region that is resistant to demineralization using high-resolution microscopy. The microcracks are formed due to the slight contraction of enamel due to transformation of carbonated hydroxyapatite to the more acid resistant pure phase hydroxyapatite (HAP) that has a smaller lattice. In this study, we test the hypothesis that these small cracks will provide greater adhesion for topical fluoride for greater protection against acid demineralization.

  11. Effects of blue light irradiation on dental enamel remineralization in vitro; Avaliacao dos efeitos promovidos pela radiacao azul na remineralizacao do esmalte dentario in vitro

    Energy Technology Data Exchange (ETDEWEB)

    Kato, Ilka Tiemy

    2009-07-01

    This study aimed to investigate the effects of blue radiation on dental enamel remineralization. In addition, a methodology of analysis was developed to evaluate alterations of enamel mineral content by optical coherence tomography. Artificial lesions were formed in bovine dental enamel slabs by immersing the samples in under saturated acetate buffer (2 mL/mm{sup 2} e 6.25 mL/mm{sup 2}). The lesions were irradiated with blue LED (l=455{+-}20nm), with radiant power of 110 mW, irradiance of 1.4 W/cm{sup 2}, radiant exposure of 13.8 J/{sup c}m2 and exposure time of 10 s. Remineralization was induced by pH-cycling model during 8 days. Cross-sectional hardness and optical coherence tomography (OCT) were used to assess mineral changes after remineralization. Hardness data showed that non-irradiated enamel lesions presented higher mineral content than irradiated ones and this difference was more evident in lesions formed in higher solution volume. The analysis of OCT signal also demonstrated that the mineral content of non-irradiated group was higher than in irradiated one; however, no significant difference was observed. Furthermore, significant differences in OCT sign were detected between sound and demineralized enamel. Based on the results obtained in the present study it can be concluded that blue radiation caused an inhibition of enamel remineralization. The methodology adopted for OCT analysis allowed the quantification of enamel mineral loss; however, the remineralization process could not be evaluated by this technique. (author)

  12. Dental Enamel Defects and Celiac Disease

    Science.gov (United States)

    ... Digestive System & How it Works Zollinger-Ellison Syndrome Dental Enamel Defects and Celiac Disease Celiac disease manifestations ... affecting any organ or body system. One manifestation—dental enamel defects—can help dentists and other health ...

  13. In vitro study of demineralization resistance and fluoride retention in dental enamel irradiated with Er,Cr: YSGG laser

    International Nuclear Information System (INIS)

    Ana, Patricia Aparecida da.

    2007-01-01

    This study aimed to establish irradiation conditions of Er,Cr:YSGG laser (λ of 2.79 μm) which could propitiate changes on human dental enamel and increase its resistance to demineralization, when associated or not with topical application of acidulated phosphate fluoride (APF). Fluences of 2,8 J/cm 2 , 5,6 J/cm 2 e 8,5 J/cm 2 were selected; they were associated or not with previous application of a photo absorber (coal paste) and then APF was applied or not after laser irradiation. In a first step, the morphological findings, the surface temperatures, and the pupal temperatures were evaluated during laser irradiation. After that, the treated samples were submitted to a a ten-day pH-cycling model. After producing the incipient white-spots lesions, the following aspects were evaluated: the mineral loss, the loosely bound fluoride and the firmly bound fluoride. All the demineralizing and remineralizing pH-cycling solutions were evaluated with respect to their calcium (Ca), inorganic phosphorous (Pi) and fluoride (F - ) concentrations. The data had their normality and homogeneity distribution statistically evaluated, and it was chosen an appropriated statistical test for each performed analysis according to the obtained results, considering 5% significant level. The fluences selected for this study created ablated surfaces; the fluences of 5.6 J/cm 2 and 8.5 J/cm 2 promoted increments in surface temperature above 110 deg C. The intrapupal temperature changes revealed that laser irradiation did not increase the pulpal temperatures above the critical threshold for induction of pulpitis. The coal paste did not promote any changes on surface morphology or in the intrapulpal temperature changes; however, this paste increased the surface temperatures during laser irradiation. Only laser irradiation at 8.5 J/cm 2 was able to decrease the mineral loss when compared to the no-treatment group; although the association of coal paste + laser at 2.8 J/cm 2 + APF application

  14. An in vitro investigation of human enamel wear by restorative dental materials

    International Nuclear Information System (INIS)

    Adachi, L.K.; Saiki, M.; De Campos, T.N.

    2001-01-01

    A radiometric method was applied to asses enamel wear by another enamel and by restorative materials. The radioactive enamel was submitted to wear in a machine which allows sliding motion of an antagonistic surface in contact with the radioactive enamel. The enamel wear was evaluated by measuring the beta-activity of 32 P transferred to water from this irradiated tooth. Results obtained indicated that dental porcelains cause pronounced enamel wear when compared with that provoked by another natural enamel or by resin materials. Resin materials caused less enamel wear than another natural enamel. Vickers microhardness data obtained for antagonistic materials showed a correlation with the wear caused to the enamel. (author)

  15. In Situ analysis of CO2 laser irradiation on controlling progression of erosive lesions on dental enamel.

    Science.gov (United States)

    Lepri, Taísa Penazzo; Scatolin, Renata Siqueira; Colucci, Vivian; De Alexandria, Adílis Kalina; Maia, Lucianne Cople; Turssi, Cecília Pedroso; Corona, Silmara Aparecida Milori

    2014-08-01

    The present study aimed to evaluate in situ the effect of CO2 laser irradiation to control the progression of enamel erosive lesions. Fifty-six slabs of bovine incisors enamel (5 × 3 × 2.5 mm(3) ) were divided in four distinct areas: (1) sound (reference area), (2) initial erosion, (3) treatment (irradiated or nonirradiated with CO2 laser), (4) final erosion (after in situ phase). The initial erosive challenge was performed with 1% citric acid (pH = 2.3), for 5 min, 2×/day, for 2 days. The slabs were divided in two groups according to surface treatment: irradiated with CO2 laser (λ = 10.6 µm; 0.5 W) and nonirradiate. After a 2-day lead-in period, 14 volunteers wore an intraoral palatal appliance containing two slabs (irradiated and nonirradiated), in two intraoral phases of 5 days each. Following a cross-over design during the first intraoral phase, half of the volunteers immersed the appliance in 100 mL of citric acid for 5 min, 3×/day, while other half of the volunteers used deionized water (control). The volunteers were crossed over in the second phase. Enamel wear was determined by an optical 3D profilometer. Three-way ANOVA for repeated measures revealed that there was no significant interaction between erosive challenge and CO2 laser irradiation (P = 0.419). Erosive challenge significantly increased enamel wear (P = 0.001), regardless whether or not CO2 laser irradiation was performed. There was no difference in enamel wear between specimens CO2 -laser irradiated and non-irradiated (P = 0.513). Under intraoral conditions, CO2 laser irradiation did not control the progression of erosive lesions in enamel caused by citric acid. © 2014 Wiley Periodicals, Inc.

  16. Evaluation of radiation effects on dental enamel hardness and dental restorative materials

    International Nuclear Information System (INIS)

    Adachi, Lena Katekawa; Saiki, Mitiko; Campos, Tomie Nakakuki

    2000-01-01

    This research presents the results of the microhardness of human dental enamel and of the following dental restorative materials: three dental porcelains - Ceramco II, Finesse and Noritake, and two resin restorative materials - Artglass and Targis, for materials submitted to different times of irradiation at the IEA-R1m nuclear reactor under a thermal neutron flux of 10 12 n cm -2 .s -1 . The results obtained indicated that there is a decrease of the surface microhardness when the enamel is irradiated for 1 h and when dental materials are irradiated for 3 h. However, enamels irradiated for 30 min. did not show significant change of their surface hardness. Therefore, the selection of irradiation time is an important factor to be considered when irradiated teeth or dental materials are used in the investigations of their properties. (author)

  17. Effects of 960 nm diode laser irradiation on dental enamel in vitro: temperature and morphological analysis and evaluation of enamel demineralization

    International Nuclear Information System (INIS)

    Kato, Ilka Tiemy

    2004-01-01

    The aim of this study is to determine the effects of diode laser irradiation on enamel demineralization. To achieve this goal appropriate photon absorbing substances for the laser radiation, safe laser parameters and adequate temperature measuring apparatus had to be determined. Next, the effects of diode laser and acidulated phosphate fluoride on enamel demineralization by calcium content analysis were evaluated with inductively coupled plasma atomic emission spectrometry (ICP-AES). In the first part of the study, five dyes consisting of vegetable coal diluted in five different liquids were analyzed and vegetable coal diluted in physiological solution was chosen for use as absorber. Methodologies to measure pulp chamber temperature were evaluated and modeling clay was chosen as fixture for the enamel samples held at body temperature. In the second part of the study, different energy density parameters (1.8 J/cm 2 , 3.7 J/cm 2 , 5.6 J/cm 2 , 7.4 J/cm 2 and 9.3 J/cm 2 ) exposure times (10, 15, 20, 25 e 30 seconds) and time intervals between dye application and laser irradiation (5, 30, 60, 90 e 120 seconds) were evaluated with respect to temperature changes in the pulp chamber. The enamel morphology was analyzed by scanning electron microscopy. Acid resistance was measured using seventy five enamel specimens, divided in five groups (control, fluoride, laser, laser + fluoride and fluoride + laser). The amount of calcium lost during demineralization in lactic acid was measured by ICP-AES. The results obtained in this experiment permit the conclusion that diode laser irradiation did not increase acid resistance. When associated with fluoride, the acid resistance did not differ from the results obtained with fluoride alone. (author)

  18. Radiation damage in bioapatites: the ESR spectrum of irradiated dental enamel revisited

    International Nuclear Information System (INIS)

    Rossi, A.M.; Poupeau, G.

    1990-01-01

    We have studied the ESR spectrum of enamel from fossil vertebrate teeth perpendicular = 2.0026 and g longitudinal = 1.9975; and species B, having an orthorhombic symmetry with g 1 = 2.0032, g 2 = 2.0018 and g 3 = 1.9975. Center A is probably located at an OH - site of the hydroxyapatite lattice. Centre B could be a distorted centre A. (author)

  19. Evaluation of temperature variation in pulp chamber after high power diode laser irradiation (λ=830 nm) on dental enamel: 'in vitro' study

    International Nuclear Information System (INIS)

    Macri, Rodrigo Teixeira

    2001-01-01

    The aim of this study was to observe the variation of temperature in the pulp chamber caused by irradiation of a commercial diode laser operating in continuous wave with wavelength 830 nm over the dental enamel. In the first part of this study, two types of tooth models were tested: 3,5 mm slice and whole tooth. In the second part, we irradiated the buccal si de of the enamel in 2 primary lower incisors from cattle with Opus 10 diode laser for 10 s with power levels of 1 W and 2 W, always using an absorber. Two thermocouples were used. The first one was inserted in the dentin wall closest to the irradiation site, while the second was inserted in the middle of the pulp chamber. It was observed that the thermocouples registered different temperatures. Always, the dentin thermocouple registered higher temperatures. Considering the dentin records, the irradiation of 1 W for 10 s can be safe for the pulp. Further studies must be developed related to the correct positioning of the thermocouples inside the pulp chamber. This was a first step of using diode laser in enamel, and in this study, we concluded that the Opus 10 diode laser shown to be safe for this use, with 1 W power for 10 S. (author)

  20. The fracture behaviour of dental enamel

    OpenAIRE

    Bechtle, Sabine; Habelitz, Stefan; Klocke, Arndt; Fett, Theo; Schneider, Gerold A.

    2009-01-01

    Abstract Enamel is the hardest tissue in the human body covering the crowns of teeth. Whereas the underlying dental material dentin is very well characterised in terms of mechanical and fracture properties, available data for enamel are quite limited and are apart from the most recent investigation mainly based on indentation studies. Within the current study, stable crack-growth experiments in bovine enamel have been performed, to measure fracture resistance curves for enamel. Single edge...

  1. Near-UV laser treatment of extrinsic dental enamel stains.

    Science.gov (United States)

    Schoenly, J E; Seka, W; Featherstone, J D B; Rechmann, P

    2012-04-01

    The selective ablation of extrinsic dental enamel stains using a 400-nm laser is evaluated at several fluences for completely removing stains with minimal damage to the underlying enamel. A frequency-doubled Ti:sapphire laser (400-nm wavelength, 60-nanosecond pulse duration, 10-Hz repetition rate) was used to treat 10 extracted human teeth with extrinsic enamel staining. Each tooth was irradiated perpendicular to the surface in a back-and-forth motion over a 1-mm length using an ∼300-µm-diam 10th-order super-Gaussian beam with fluences ranging from 0.8 to 6.4 J/cm(2) . Laser triangulation determined stain depth and volume removed by measuring 3D surface images before and after irradiation. Scanning electron microscopy evaluated the surface roughness of enamel following stain removal. Fluorescence spectroscopy measured spectra of unbleached and photobleached stains in the spectral range of 600-800 nm. Extrinsic enamel stains are removed with laser fluences between 0.8 and 6.4 J/cm(2) . Stains removed on sound enamel leave behind a smooth enamel surface. Stain removal in areas with signs of earlier cariogenic acid attacks resulted in isolated and randomly located laser-induced, 50-µm-diam enamel pits. These pits contain 0.5-µm diam, smooth craters indicative of heat transfer from the stain to the enamel and subsequent melting and water droplet ejection. Ablation stalling of enamel stains is typically observed at low fluences (Laser ablation of extrinsic enamel stains at 400 nm is observed to be most efficient above 3 J/cm(2) with minimal damage to the underlying enamel. Unsound underlying enamel is also observed to be selectively removed after irradiation. Copyright © 2012 Wiley Periodicals, Inc.

  2. Surface morphological changes on the human dental enamel and cement after the Er:YAG laser irradiation at different incidence angles

    International Nuclear Information System (INIS)

    Tannous, Jose Trancoso

    2001-01-01

    This is a morphological analysis study through SEM of the differences of the laser tissue interaction as a function of the laser beam irradiation angle, under different parameters of energy. Fourteen freshly extracted molars stored in a 0,9% sodium chloride solution were divided in seven pairs and were irradiated with 100, 200, 300, 400, 500, 600 and 700 mJ per pulse, respectively. Each sample received three enamel irradiations and three cement irradiations, either in the punctual or in the contact mode, one near to the other, with respectively 30, 45 and 90 inclinations degrees of dental surface-laser-beam incidence. Four Er:YAG pulses (2,94 μm, 7-20 Hz, 0,1-1 J energy/pulse - Opus 20 - Opus Dent) with water cooling system (0,4 ml/s) were applied. After the laser irradiation the specimens were analysed through scanning electron microscope (SEM). The results were analysed by SEM micrographs showing a great difference on the laser tissue interaction characteristics as a function of the irradiation angle of the laser beam. All the observations led to conclude that, considering the laser parameters used, the incidence angle variation is a very important parameter regarding the desired morphological effects. This represents an extremely relevant detail on the technical description of the Er:YAG laser irradiation protocols on dental tissues. (author)

  3. Dental enamel, fluorosis and amoxicillin

    Directory of Open Access Journals (Sweden)

    I. Ciarrocchi

    2012-06-01

    Full Text Available Introduction: Amoxicillin is one of the most used antibiotics among pediatric patients for the treatment of upper respiratory tract infections and specially for acute otitis media (AOM, a common diseases of infants and childhood. It has been speculated that the use of amoxicillin during early childhood could be associated with dental enamel fluorosis, also described in literature with the term Molar Incisor Hypomineralization (MIH, because they are generally situated in one or more 1st permanent molars and less frequently in the incisors. The effect of Amoxicillin seems to be independent of other risk factors such as fluoride intake, prematurity, hypoxia, hypocalcaemia, exposure to dioxins, chikenpox, otitis media, high fever and could have a significant impact on oral health for the wide use of this drug in that period of life. Objective: The aim of this work was to review the current literature about the association between amoxicillin and fluorosis. Methods and Results: A literature survey was done by applying the Medline database (Entrez PubMed; the Cochrane Library database of the Cochrane Collaboration (CENTRAL. The databases were searched using the following strategy and keywords: amoxicillin* AND (dental fluorosis* OR dental enamel* AND MIH*. After selecting the studies, only three relevant articles published between 1966 and 2011 were included in the review. Conclusion: The presence of several methodological issues does not allow to draw any evidence-based conclusions. No evidence of association was detected, therefore, there is a need of further well-designed studies to assess the scientific evidence of the relationship between amoxicillin and fluorosis and to restrict the prescription of this drug for recurrent upper respiratory tract infections especially acute otitis media (AOM during the first two years of life. When it is possible can be opportune to use an alternative antibiotic treatment.

  4. Potential of sub-ablative pulsed CO2 laser irradiation on inhibition of artificial caries-like lesion progress in bovine dental enamel

    International Nuclear Information System (INIS)

    Oliveira, Marcella Esteves

    2005-01-01

    The aim of this study was to investigate whether sub-ablative pulsed C0 2 laser (1 0,6 μm) irradiation is capable of reducing the susceptibility of the dental enamel to demineralization, and thus achieving a potential caries-protective effect. The crowns of 51 bovine front teeth, embedded in acrylic resin and polished until exposure of flat enamel surface, were used. The samples were cut in cubes of 10x10 mm, and totally coated with acid-resistant nail varnish, except for an enamel exposed window of 16 mm square. Three groups (n=17) were obtained: control group (CG) not irradiated; group laser A (LA) and group laser B (LB) where the samples were irradiated. The conditions were 60 mJ, 100 Hz, 0,3 J/cm 2 for LA and 135 mJ, 10 Hz, 0,7 J/cm 2 for LB. Two samples of each group were submitted to SEM analysis and fifteen to demineralization in 3 ml acetate buffer solution (0,1 mol/L) with pH 4,5 for 24h at 37 deg C, with regular agitation. After the specimens were removed from the solution, the calcium and phosphorous content were measured with an inductively coupled plasma optical emission spectrometer and 2 more samples of each were submitted to SEM analysis. The obtained Ca and P means in μg/ml and the calculated Ca/P molar ratio were: CG (367,88 ± 33,47; 168,91 ± 14,55; 1,70 ± 0,07) ; LA (372,70 ± 41,70; 161,46 ± 15,26; 1,79 ± 0,07) and LB (328,87 ± 24,91; 145,02 ± 11,04; 1,77 ± 0,05). The ANOVA statistical test revealed statistically significant difference for [Ca], [P] e Ca/P content between the groups (p 2 pulsed CO 2 laser irradiation of bovine enamel was capable of reducing the enamel acid solubility without causing damage to the surface and therefore is a potential method of caries prevention. (author)

  5. Dental enamel cells express functional SOCE channels.

    Science.gov (United States)

    Nurbaeva, Meerim K; Eckstein, Miriam; Concepcion, Axel R; Smith, Charles E; Srikanth, Sonal; Paine, Michael L; Gwack, Yousang; Hubbard, Michael J; Feske, Stefan; Lacruz, Rodrigo S

    2015-10-30

    Dental enamel formation requires large quantities of Ca(2+) yet the mechanisms mediating Ca(2+) dynamics in enamel cells are unclear. Store-operated Ca(2+) entry (SOCE) channels are important Ca(2+) influx mechanisms in many cells. SOCE involves release of Ca(2+) from intracellular pools followed by Ca(2+) entry. The best-characterized SOCE channels are the Ca(2+) release-activated Ca(2+) (CRAC) channels. As patients with mutations in the CRAC channel genes STIM1 and ORAI1 show abnormal enamel mineralization, we hypothesized that CRAC channels might be an important Ca(2+) uptake mechanism in enamel cells. Investigating primary murine enamel cells, we found that key components of CRAC channels (ORAI1, ORAI2, ORAI3, STIM1, STIM2) were expressed and most abundant during the maturation stage of enamel development. Furthermore, inositol 1,4,5-trisphosphate receptor (IP3R) but not ryanodine receptor (RyR) expression was high in enamel cells suggesting that IP3Rs are the main ER Ca(2+) release mechanism. Passive depletion of ER Ca(2+) stores with thapsigargin resulted in a significant raise in [Ca(2+)]i consistent with SOCE. In cells pre-treated with the CRAC channel blocker Synta-66 Ca(2+) entry was significantly inhibited. These data demonstrate that enamel cells have SOCE mediated by CRAC channels and implicate them as a mechanism for Ca(2+) uptake in enamel formation.

  6. Study in vitro of dental enamel irradiated with a high power diode laser operating at 960 nm: morphological analysis of post-irradiation dental surface and thermal effect analysis in pulp chamber due to laser application; Estudo in vitro do esmalte dental irradiado com laser de diodo de alta potencia em 960 nm: analise morfologica da superficie dental pos-irradiada e analise do comportamento termico na camara pulpar devido a aplicacao laser

    Energy Technology Data Exchange (ETDEWEB)

    Quinto Junior, Jose

    2001-07-01

    Objectives: This study examines the structural and thermal modifications induced in dental enamel under dye assisted diode laser irradiation. The aim of this study is to verify if this laser-assisted treatment is capable to modify the enamel surface by causing fusion of the enamel surface layer. At the same time, the pulpal temperature rise must be kept low enough in order not to cause pulpar necrosis. To achieve this target, it is necessary to determine suitable laser parameters. As is known, fusion of the enamel surface followed by re-solidification produce a more acid resistant layer. This surface treatment is being researched as a new method for caries prevention. Method and Materials: A series of fourteen identically prepared enamel samples of human teeth were irradiated with a high power diode laser operating at 960 nm and using fiber delivery. Prior to irradiation, a fine layer of cromophorous ink was applied to the enamel surface. In the first part of the experiment the best parameter for pulse duration was determined. In the second part of the experimental phase the same energy density was used but with different repetition rates. During irradiation we monitored the temperature rise in the pulpal cavity. The morphology of the treated samples was analysed under SEM. Results: The morphology of the treated samples showed a homogeneously re-solidified enamel layer. The results of the temperature analysis showed a decrease of the pulpal temperature rise with decreasing repetition rate. Conclusion: With the diode laser it is possible to cause morphological alterations of the enamel surface, which is known to increase the enamel resistance against acid attack, and still maintain the temperature rise in the pulpar chamber below damage threshold. (author)

  7. An in vitro study of dental enamel wear by restorative materials using radiometric method

    International Nuclear Information System (INIS)

    Adachi, Lena Katekawa

    2000-01-01

    There is an increasing demand and interest to study the dental materials wear as well as about the abrasion effect on antagonistic teeth. Due to the fact that the existent restorative materials have no specifications about their abrasiveness, it is necessary the establishment of degrees of comparison among them to support clinical application. In this work, the radiometric method was applied to study the enamel wear caused by another enamel and by restorative materials (Ceramco II, Noritake and Finesse porcelains, Artglass and Targis). The dental enamel made radioactive by irradiation at the IEA-R1m nuclear research reactor under a thermal neutron flux was submitted to wear in a machine which allows sliding motion of an antagonistic surface in contact with this radioactive enamel. The enamel wear was evaluated by measuring beta activity of 32 P transferred to water from this irradiated tooth. Results obtained indicated that dental porcelains cause pronounced enamel wear when compared with that provoked by another enamel or by resin materials. Resin materials caused less enamel wear than another enamel. Vickers microhardness data obtained for antagonistic materials showed a correlation with the wear caused to the enamel. This study allowed to conclude that the radiometric method proposed can be used satisfactorily in the evaluation of enamel wear by restorative materials. This method presents advantages due to quick responses and ease of analyses There is (author)

  8. Evaluation of radiation effects on dental enamel hardness and dental restorative materials; Avaliacao do efeito da irradiacao na dureza do esmalte dental e de materiais odontologicos

    Energy Technology Data Exchange (ETDEWEB)

    Adachi, Lena Katekawa; Saiki, Mitiko [Instituto de Pesquisas Energeticas e Nucleares (IPEN), Sao Paulo, SP (Brazil). Supervisao de Radioquimica; Campos, Tomie Nakakuki [Sao Paulo Univ., SP (Brazil). Faculdade de Odontologia. Dept. de Protese

    2000-07-01

    This research presents the results of the microhardness of human dental enamel and of the following dental restorative materials: three dental porcelains - Ceramco II, Finesse and Noritake, and two resin restorative materials - Artglass and Targis, for materials submitted to different times of irradiation at the IEA-R1m nuclear reactor under a thermal neutron flux of 10{sup 12}n cm{sup -2}.s{sup -1} . The results obtained indicated that there is a decrease of the surface microhardness when the enamel is irradiated for 1 h and when dental materials are irradiated for 3 h. However, enamels irradiated for 30 min. did not show significant change of their surface hardness. Therefore, the selection of irradiation time is an important factor to be considered when irradiated teeth or dental materials are used in the investigations of their properties. (author)

  9. In vitro study of morphological and chemical modification threshold of bovine dental enamel irradiated by the holmium laser; Estudo in vitro das alteracoes morfologicas e quimicas do esmalte dental bovino irradiado pelo laser de holmio

    Energy Technology Data Exchange (ETDEWEB)

    Eduardo, Patricia Lerro de Paula

    2001-07-01

    The aim of this study is to investigate the Ho:YLF laser effects on the dental enamel surface with regards to its morphology, thermal variations during its irradiation in the pulp chamber and its increased resistance to demineralization through quantitative analysis of calcium and phosphorous atoms reactive concentrations in samples. Twenty samples of bovine enamel were used and divided in four groups: control - acidulated phosphate fluoride (APF) application followed by demineralization treatment with lactic acid; irradiation with Ho:YLF laser (100 J/cm{sup 2}) followed by APF topic application and demineralization treatment with lactic acid; irradiation with Ho:YLF laser (350 J/cm{sup 2}) followed by APF topic application and demineralization treatment with lactic acid: and irradiation with Ho:YLF laser ( 450 J/cm{sup 2}) followed by APF topic application and demineralization treatment with lactic acid. Ali samples were quantified according to their calcium and phosphorous atoms relative concentrations before and after the treatments above. X-Ray fluorescence spectrochemical analysis and scanning electron microscopy were carried out. It was observed an increase on the calcium and phosphorous atoms concentration ratio and therefore the enamel demineralization reduction as a result of the lactic acid treatment in the samples irradiated with the holmium laser followed by the APF application. In order to evaluate the feasibility of this study for clinical purposes, morphological changes caused by the holmium laser irradiation were analyzed. Such modifications were characterized by melted and re-solidified regions of the enamel with consequent changes on its permeability and solubility. Temperature changes of ten human pre-molars teeth irradiated with 350 J/cm{sup 2} and 450 J/cm{sup 2} were also monitored in the pulp chamber in real time. Temperature increases over 4,20 C did not occur. The results obtained from this study along with the results from previous

  10. Utilization of radiometric method in evaluation of wear on human dental enamel in vitro by dental porcelain glazed and polished

    International Nuclear Information System (INIS)

    Adachi, Lena Katekawa; Campos, Tomie Nakakuki de; Adachi, Eduardo Makoto

    2005-01-01

    The dental porcelain is a material commonly used in prosthesis. Disadvantages of dental porcelain use include possibility to cause tooth or dental materials wear. Before its use in the mouth, surfaces are treated with polishing and/or glazing. This research used the radiometric method to verify the influence of these surface treatments on the porcelains of commercial brands: Ceramco II, Noritake and Finesse. This method was originally developed for dentifrice abrasiveness evaluation. Five specimens of dental enamel and 10 specimens of each porcelain (5 glazed, 5 polished) were used. The dental enamel was flattened and irradiated with neutrons from the IEA-R1 (IPEN/CNEN) nuclear reactor. Then it was weared by each porcelain in sliding motion, with water. After 2,500 cycles for each porcelain specimen, the released enamel residue was measured. The enamel wear was evaluated by measuring beta activity of 32 P transferred to water from the irradiated tooth. Results varied from 2.57 to 5.81 μg of enamel /mm 2 weared surface. There was no statistical difference (α=0.05) between dental enamel wear caused by the same porcelains glazed or polished. The results suggest that adequate surface finishing depend on the type of dental porcelain. (author)

  11. The fracture behaviour of dental enamel.

    Science.gov (United States)

    Bechtle, Sabine; Habelitz, Stefan; Klocke, Arndt; Fett, Theo; Schneider, Gerold A

    2010-01-01

    Enamel is the hardest tissue in the human body covering the crowns of teeth. Whereas the underlying dental material dentin is very well characterized in terms of mechanical and fracture properties, available data for enamel are quite limited and are apart from the most recent investigation mainly based on indentation studies. Within the current study, stable crack-growth experiments in bovine enamel have been performed, to measure fracture resistance curves for enamel. Single edge notched bending specimens (SENB) prepared out of bovine incisors were tested in 3-point bending and subsequently analysed using optical and environmental scanning electron microscopy. Cracks propagated primarily within the protein-rich rod sheaths and crack propagation occurred under an inclined angle to initial notch direction not only due to enamel rod and hydroxyapatite crystallite orientation but potentially also due to protein shearing. Determined mode I fracture resistance curves ranged from 0.8-1.5 MPa*m(1/2) at the beginning of crack propagation up to 4.4 MPa*m(1/2) at 500 microm crack extension; corresponding mode II values ranged from 0.3 to 1.5 MPa*m(1/2).

  12. CO2 laser irradiation enhances CaF2 formation and inhibits lesion progression on demineralized dental enamel-in vitro study.

    Science.gov (United States)

    Zancopé, Bruna R; Rodrigues, Lívia P; Parisotto, Thais M; Steiner-Oliveira, Carolina; Rodrigues, Lidiany K A; Nobre-dos-Santos, Marinês

    2016-04-01

    This study evaluated if Carbon dioxide (CO2) (λ 10.6 μm) laser irradiation combined with acidulated phosphate fluoride gel application (APF gel) enhances "CaF2" uptake by demineralized enamel specimens (DES) and inhibits enamel lesion progression. Thus, two studies were conducted and DES were subjected to APF gel combined or not with CO2 laser irradiation (11.3 or 20.0 J/cm(2), 0.4 or 0.7 W) performed before, during, or after APF gel application. In study 1, 165 DES were allocated to 11 groups. Fluoride as "CaF2 like material" formed on enamel was determined in 100 DES (n = 10/group), and the surface morphologies of 50 specimens were evaluated by scanning electron microscopy (SEM) before and after "CaF2" extraction. In study 2, 165 DES (11 groups, n = 15), subjected to the same treatments as in study 1, were further subjected to a pH-cycling model to simulate a high cariogenic challenge. The progression of demineralization in DES was evaluated by cross-sectional microhardness and polarized light microscopy analyses. Laser at 11.3 J/cm(2) applied during APF gel application increased "CaF2" uptake on enamel surface. Laser irradiation and APF gel alone arrested the lesion progression compared with the control (p enamel surface and a synergistic effect was found. However, regarding the inhibition of caries lesion progression, no synergistic effect could be demonstrated. In conclusion, the results have shown that irradiation with specific laser parameters significantly enhanced CaF2 uptake by demineralized enamel and inhibited lesion progression.

  13. THE EFFECT OF IRRADIATION ON ENAMEL MICRO-STRUCTURE CHANGES

    Directory of Open Access Journals (Sweden)

    Harun Gunawan

    2015-06-01

    Full Text Available Radiotherapy plays an important role in the management of head and neck carcinoma therapy. The radiation dose ranges from 40 – 70 Gy, depends on the severity and location of the malignancy. Many patients experience an increased dental caries or sensitivity occurrence following radiotherapy. The objective of this study is to analyze the enamel micro-structure changes after irradiation. Nine polished enamel slabs were prepared from impacted 3rd molars. The slabs were flushed in non-ionic distilled water and dried by using air spray and divided into 3 groups, the control, 20 Gy and 40 Gy irradiation group. Irradiations were performed from Co60 using Gammacell-220E, with duration variables to produce the irradiation doses of 20 and 40 Gy. Philips pW370-XRD was used to examine specimen microstructure changes after irradiation. 1-way ANOVA was used for statistics analysis. It was revealed that grain size after 40 Gy irradiation was 66.29±2.7 nm, and after 20 Gy was 51.64±15.8 whilst 43.95±11.1 nm for the control group. The micro-stain deviation of the 40 Gy group was 0.594±0.15 N/m, and 0.45±2.6 N/m for the 20 Gy group, and 0.378±0.27 N/m for control group. Statistic analysis showed significant grain size differences between 40 Gy compared to both 20 Gy and control groups, but not between 20 Gy compared to the control group. Similarly, there were micro-stain differences between 40 Gy compared to 20 Gy and control groups, but not between 20 Gy compared to control group. It was concluded that irradiation with 40 Gy caused elevation of the enamel microstrain and apaite grainsize. Elevation of the enamel microstrain could lead to enamel crack and gave hypersensitive sensation.

  14. Dental enamel defects in children with coeliac disease

    NARCIS (Netherlands)

    Werink, Claar D.; van Diermen, Denise E.; Aartman, Irene H. A.; Heymans, Hugo S. A.

    2007-01-01

    OBJECTIVE: The aim of this study was to investigate whether Dutch children with proven coeliac disease show specific dental enamel defects, and to asses whether children with the same gastrointestinal complaints, but proved no-coeliac disease, lack these specific dental enamel defects. MATERIALS AND

  15. In vitro study of the diode laser effect on artificial demineralized surface of human dental enamel

    International Nuclear Information System (INIS)

    Ebel, Patricia

    2003-01-01

    In scientific literature there are many reports about fusion and resolidification of dental enamel after laser irradiation and their capability to generate surfaces with increased resistance to demineralization compared to non-irradiated areas. The use of high power diode laser on demineralized surfaces of human dental enamel is presented as a good alternative in caries prevention. The purpose of this study is to investigate the morphological changes produced by the use of one high power diode laser on human dental enamel surface after demineralization treatment with lactic acid, under chosen parameters. Fifteen samples of human dental molars were used and divided in four groups: control - demineralization treatment with lactic acid and no irradiation, and demineralization treatment with lactic acid followed of irradiation with 212,20 mJ/cm 2 , 282,84 mJ/cm 2 and 325,38 mJ/cm 2 , respectively. The samples were irradiated with high power diode laser (808 nm) with a 300 μm diameter fiber optics. Black ink was used on enamel surface to enhance the superficial absorption. The samples were studied by optical microscopy and scanning electron microscopy. Modifications on the enamel surfaces were observed. Such modifications were characterized by melted and re-solidified region of the enamel. According with our results the best parameter was 2.0 W, presenting the most uniform surface. The use of high power diode laser as demonstrated in this study is able to promote melting and re-solidification on human dental enamel. (author)

  16. An in vitro study of dental enamel wear by restorative materials using radiometric method; Estudo in vitro do desgaste do esmalte dental pelos materiais restauradores utilizando metodo radiometrico

    Energy Technology Data Exchange (ETDEWEB)

    Adachi, Lena Katekawa

    2000-07-01

    There is an increasing demand and interest to study the dental materials wear as well as about the abrasion effect on antagonistic teeth. Due to the fact that the existent restorative materials have no specifications about their abrasiveness, it is necessary the establishment of degrees of comparison among them to support clinical application. In this work, the radiometric method was applied to study the enamel wear caused by another enamel and by restorative materials (Ceramco II, Noritake and Finesse porcelains, Artglass and Targis). The dental enamel made radioactive by irradiation at the IEA-R1m nuclear research reactor under a thermal neutron flux was submitted to wear in a machine which allows sliding motion of an antagonistic surface in contact with this radioactive enamel. The enamel wear was evaluated by measuring beta activity of {sup 32}P transferred to water from this irradiated tooth. Results obtained indicated that dental porcelains cause pronounced enamel wear when compared with that provoked by another enamel or by resin materials. Resin materials caused less enamel wear than another enamel. Vickers microhardness data obtained for antagonistic materials showed a correlation with the wear caused to the enamel. This study allowed to conclude that the radiometric method proposed can be used satisfactorily in the evaluation of enamel wear by restorative materials. This method presents advantages due to quick responses and ease of analyses There is (author)

  17. Targeted p120-catenin ablation disrupts dental enamel development

    DEFF Research Database (Denmark)

    Bartlett, John D; Dobeck, Justine M; Tye, Coralee E

    2010-01-01

    Dental enamel development occurs in stages. The ameloblast cell layer is adjacent to, and is responsible for, enamel formation. When rodent pre-ameloblasts become tall columnar secretory-stage ameloblasts, they secrete enamel matrix proteins, and the ameloblasts start moving in rows that slide...... by one another. This movement is necessary to form the characteristic decussating enamel prism pattern. Thus, a dynamic system of intercellular interactions is required for proper enamel development. Cadherins are components of the adherens junction (AJ), and they span the cell membrane to mediate...... attachment to adjacent cells. p120 stabilizes cadherins by preventing their internalization and degradation. So, we asked if p120-mediated cadherin stability is important for dental enamel formation. Targeted p120 ablation in the mouse enamel organ had a striking effect. Secretory stage ameloblasts detached...

  18. Size dependent elastic modulus and mechanical resilience of dental enamel.

    Science.gov (United States)

    O'Brien, Simona; Shaw, Jeremy; Zhao, Xiaoli; Abbott, Paul V; Munroe, Paul; Xu, Jiang; Habibi, Daryoush; Xie, Zonghan

    2014-03-21

    Human tooth enamel exhibits a unique microstructure able to sustain repeated mechanical loading during dental function. Although notable advances have been made towards understanding the mechanical characteristics of enamel, challenges remain in the testing and interpretation of its mechanical properties. For example, enamel was often tested under dry conditions, significantly different from its native environment. In addition, constant load, rather than indentation depth, has been used when mapping the mechanical properties of enamel. In this work, tooth specimens are prepared under hydrated conditions and their stiffnesses are measured by depth control across the thickness of enamel. Crystal arrangement is postulated, among other factors, to be responsible for the size dependent indentation modulus of enamel. Supported by a simple structure model, effective crystal orientation angle is calculated and found to facilitate shear sliding in enamel under mechanical contact. In doing so, the stress build-up is eased and structural integrity is maintained. Copyright © 2014 Elsevier Ltd. All rights reserved.

  19. Dental Enamel Development: Proteinases and Their Enamel Matrix Substrates

    Science.gov (United States)

    Bartlett, John D.

    2013-01-01

    This review focuses on recent discoveries and delves in detail about what is known about each of the proteins (amelogenin, ameloblastin, and enamelin) and proteinases (matrix metalloproteinase-20 and kallikrein-related peptidase-4) that are secreted into the enamel matrix. After an overview of enamel development, this review focuses on these enamel proteins by describing their nomenclature, tissue expression, functions, proteinase activation, and proteinase substrate specificity. These proteins and their respective null mice and human mutations are also evaluated to shed light on the mechanisms that cause nonsyndromic enamel malformations termed amelogenesis imperfecta. Pertinent controversies are addressed. For example, do any of these proteins have a critical function in addition to their role in enamel development? Does amelogenin initiate crystallite growth, does it inhibit crystallite growth in width and thickness, or does it do neither? Detailed examination of the null mouse literature provides unmistakable clues and/or answers to these questions, and this data is thoroughly analyzed. Striking conclusions from this analysis reveal that widely held paradigms of enamel formation are inadequate. The final section of this review weaves the recent data into a plausible new mechanism by which these enamel matrix proteins support and promote enamel development. PMID:24159389

  20. Optically stimulated luminescence (OSL) of dental enamel for retrospective assessment of radiation exposure

    International Nuclear Information System (INIS)

    Yukihara, E.G.; Mittani, J.; McKeever, S.W.S.; Simon, S.L.

    2007-01-01

    This paper briefly reviews the optically stimulated luminescence (OSL) properties of dental enamel and discusses the potential and challenges of OSL for filling the technology gap in biodosimetry required for medical triage following a radiological/nuclear accident or terrorist event. The OSL technique uses light to stimulate a radiation-induced luminescence signal from materials previously exposed to ionizing radiation. This luminescence originates from radiation-induced defects in insulating crystals and is proportional to the absorbed dose of ionizing radiation. In our research conducted to date, we focused on fundamental investigations of the OSL properties of dental enamel using extracted teeth and tabletop OSL readers. The objective was to obtain information to support the development of the necessary instrumentation for retrospective dosimetry using dental enamel in laboratory, or for in situ and non-invasive accident dosimetry using dental enamel in emergency triage. An OSL signal from human dental enamel was detected using blue, green, or IR stimulation. Blue/green stimulation associated with UV emission detection seems to be the most appropriate combination in the sense that there is no signal from un-irradiated samples and the shape of the OSL decay is clear. Improvements in the minimum detection level were achieved by incorporating an ellipsoidal mirror in the OSL system to maximize light collection. Other possibilities to improve the sensitivity and research steps necessary to establish the feasibility of the technique for retrospective assessment of radiation exposure are also discussed

  1. Bond strength of etch-and-rinse and self-etch adhesive systems to enamel and dentin irradiated with a novel CO2 9.3 μm short-pulsed laser for dental restorative procedures.

    Science.gov (United States)

    Rechmann, Peter; Bartolome, N; Kinsel, R; Vaderhobli, R; Rechmann, B M T

    2017-12-01

    The objective of this study was to evaluate the influence of CO 2 9.3 μm short-pulsed laser irradiation on the shear bond strength of composite resin to enamel and dentin. Two hundred enamel and 210 dentin samples were irradiated with a 9.3 µm carbon dioxide laser (Solea, Convergent Dental, Inc., Natick, MA) with energies which either enhanced caries resistance or were effective for ablation. OptiBond Solo Plus [OptiBondTE] (Kerr Corporation, Orange, CA) and Peak Universal Bond light-cured adhesive [PeakTE] (Ultradent Products, South Jordan, UT) were used. In addition, Scotchbond Universal [ScotchbondSE] (3M ESPE, St. Paul, MN) and Peak SE self-etching primer with Peak Universal Bond light-cured adhesive [PeakSE] (Ultradent Products) were tested. Clearfil APX (Kuraray, New York, NY) was bonded to the samples. After 24 h, a single plane shear bond test was performed. Using the caries preventive setting on enamel resulted in increased shear bond strength for all bonding agents except for self-etch PeakSE. The highest overall bond strength was seen with PeakTE (41.29 ± 6.04 MPa). Etch-and-rinse systems achieved higher bond strength values to ablated enamel than the self-etch systems did. PeakTE showed the highest shear bond strength with 35.22 ± 4.40 MPa. OptiBondTE reached 93.8% of its control value. The self-etch system PeakSE presented significantly lower bond strength. The shear bond strength to dentin ranged between 19.15 ± 3.49 MPa for OptiBondTE and 43.94 ± 6.47 MPa for PeakSE. Etch-and-rinse systems had consistently higher bond strength to CO 2 9.3 µm laser-ablated enamel. Using the maximum recommended energy for dentin ablation, the self-etch system PeakSE reached the highest bond strength (43.9 ± 6.5 MPa).

  2. Targeted p120-catenin ablation disrupts dental enamel development.

    Science.gov (United States)

    Bartlett, John D; Dobeck, Justine M; Tye, Coralee E; Perez-Moreno, Mirna; Stokes, Nicole; Reynolds, Albert B; Fuchs, Elaine; Skobe, Ziedonis

    2010-09-16

    Dental enamel development occurs in stages. The ameloblast cell layer is adjacent to, and is responsible for, enamel formation. When rodent pre-ameloblasts become tall columnar secretory-stage ameloblasts, they secrete enamel matrix proteins, and the ameloblasts start moving in rows that slide by one another. This movement is necessary to form the characteristic decussating enamel prism pattern. Thus, a dynamic system of intercellular interactions is required for proper enamel development. Cadherins are components of the adherens junction (AJ), and they span the cell membrane to mediate attachment to adjacent cells. p120 stabilizes cadherins by preventing their internalization and degradation. So, we asked if p120-mediated cadherin stability is important for dental enamel formation. Targeted p120 ablation in the mouse enamel organ had a striking effect. Secretory stage ameloblasts detached from surrounding tissues, lost polarity, flattened, and ameloblast E- and N-cadherin expression became undetectable by immunostaining. The enamel itself was poorly mineralized and appeared to be composed of a thin layer of merged spheres that abraded from the tooth. Significantly, p120 mosaic mouse teeth were capable of forming normal enamel demonstrating that the enamel defects were not a secondary effect of p120 ablation. Surprisingly, blood-filled sinusoids developed in random locations around the developing teeth. This has not been observed in other p120-ablated tissues and may be due to altered p120-mediated cell signaling. These data reveal a critical role for p120 in tooth and dental enamel development and are consistent with p120 directing the attachment and detachment of the secretory stage ameloblasts as they move in rows.

  3. Development of fluorapatite cement for dental enamel defects repair.

    Science.gov (United States)

    Wei, Jie; Wang, Jiecheng; Shan, Wenpeng; Liu, Xiaochen; Ma, Jian; Liu, Changsheng; Fang, Jing; Wei, Shicheng

    2011-06-01

    In order to restore the badly carious lesion of human dental enamel, a crystalline paste of fluoride substituted apatite cement was synthesized by using the mixture of tetracalcium phosphate (TTCP), dicalcium phosphate anhydrous (DCPA) and ammonium fluoride. The apatite cement paste could be directly filled into the enamel defects (cavities) to repair damaged dental enamel. The results indicated that the hardened cement was fluorapatite [Ca(10)(PO(4))(6)F(2), FA] with calcium to phosphorus atom molar ratio (Ca/P) of 1.67 and Ca/F ratio of 5. The solubility of FA cement in Tris-HCl solution (pH = 5) was slightly lower than the natural enamel, indicating the FA cement was much insensitive to the weakly acidic solutions. The FA cement was tightly combined with the enamel surface, and there was no obvious difference of the hardness between the FA cement and natural enamel. The extracts of FA cement caused no cytotoxicity on L929 cells, which satisfied the relevant criterion on dental biomaterials, revealing good cytocompatibility. In addition, the results showed that the FA cement had good mechanical strength, hydrophilicity, and anti-bacterial adhesion properties. The study suggested that using FA cement was simple and promising approach to effectively and conveniently restore enamel defects.

  4. Evaluation of temperature variation in pulp chamber after high power diode laser irradiation ({lambda}=830 nm) on dental enamel: 'in vitro' study; Avaliacao da variacao da temperatura na camara pulpar apos a irradiacao de diodo laser de alta potencia de 830 nanometros em esmalte dental: estudo 'in vitro'

    Energy Technology Data Exchange (ETDEWEB)

    Macri, Rodrigo Teixeira

    2001-07-01

    The aim of this study was to observe the variation of temperature in the pulp chamber caused by irradiation of a commercial diode laser operating in continuous wave with wavelength 830 nm over the dental enamel. In the first part of this study, two types of tooth models were tested: 3,5 mm slice and whole tooth. In the second part, we irradiated the buccal si de of the enamel in 2 primary lower incisors from cattle with Opus 10 diode laser for 10 s with power levels of 1 W and 2 W, always using an absorber. Two thermocouples were used. The first one was inserted in the dentin wall closest to the irradiation site, while the second was inserted in the middle of the pulp chamber. It was observed that the thermocouples registered different temperatures. Always, the dentin thermocouple registered higher temperatures. Considering the dentin records, the irradiation of 1 W for 10 s can be safe for the pulp. Further studies must be developed related to the correct positioning of the thermocouples inside the pulp chamber. This was a first step of using diode laser in enamel, and in this study, we concluded that the Opus 10 diode laser shown to be safe for this use, with 1 W power for 10 S. (author)

  5. SEM analysis of enamel surface treated by Er:YAG laser: influence of irradiation distance.

    Science.gov (United States)

    Souza-Gabriel, A E; Chinelatti, M A; Borsatto, M C; Pécora, J D; Palma-Dibb, R G; Corona, S A M

    2008-07-01

    Depending on the distance of laser tip to dental surface a specific morphological pattern should be expected. However, there have been limited reports that correlate the Er:YAG irradiation distance with dental morphology. To assess the influence of Er:YAG laser irradiation distance on enamel morphology, by means of scanning electron microscopy (SEM). Sixty human third molars were employed to obtain discs (approximately =1 mm thick) that were randomly assigned to six groups (n=10). Five groups received Er:YAG laser irradiation (80 mJ/2 Hz) for 20 s, according to the irradiation distance: 11, 12, 14, 16, or 17 mm and the control group was treated with 37% phosphoric acid for 15 s. The laser-irradiated discs were bisected. One hemi-disc was separated for superficial analysis without subsequent acid etching, and the other one, received the phosphoric acid for 15 s. Samples were prepared for SEM. Laser irradiation at 11 and 12 mm provided an evident ablation of enamel, with evident fissures and some fused areas. At 14, 16 and 17 mm the superficial topography was flatter than in the other distances. The subsequent acid etching on the lased-surface partially removed the disorganized tissue. Er:YAG laser in defocused mode promoted slight morphological alterations and seems more suitable for enamel conditioning than focused irradiation. The application of phosphoric acid on lased-enamel surface, regardless of the irradiation distance, decreased the superficial irregularities.

  6. 'In vitro' assessment to instrumented indentation hardness tests in enamel of bovine teeth, before and after dental bleaching by laser

    International Nuclear Information System (INIS)

    Britto Junior, Francisco Meira

    2004-01-01

    The laser enamel bleaching is a common used procedure due to its satisfactory esthetic results. The possible changes on the dental structures caused by the bleaching technique are of great importance. The enamel superficial microhardness changes through instrumented indentation hardness on bovine teeth were analyzed in this present study. The samples were divided in two halves, one being the control and the other irradiated with a diode laser (808 nm) or with a Nd:YAG laser (1064 nm) to activate the Whiteness HP bleaching gel (hydrogen peroxide at 35%). It was possible to conclude that there was a statistical significant increase on the enamel superficial microhardness (Group I, sample 1 and Group II, sample 1) despite this increase did not seem to indicate a concern regarding the enamel surface resistance change. There was not a significant statistical change on the enamel microhardness on the other samples. The final conclusion is that there was no superficial enamel morphological change after these treatments. (author)

  7. Targeted overexpression of amelotin disrupts the microstructure of dental enamel.

    Science.gov (United States)

    Lacruz, Rodrigo S; Nakayama, Yohei; Holcroft, James; Nguyen, Van; Somogyi-Ganss, Eszter; Snead, Malcolm L; White, Shane N; Paine, Michael L; Ganss, Bernhard

    2012-01-01

    We have previously identified amelotin (AMTN) as a novel protein expressed predominantly during the late stages of dental enamel formation, but its role during amelogenesis remains to be determined. In this study we generated transgenic mice that produce AMTN under the amelogenin (Amel) gene promoter to study the effect of AMTN overexpression on enamel formation in vivo. The specific overexpression of AMTN in secretory stage ameloblasts was confirmed by Western blot and immunohistochemistry. The gross histological appearance of ameloblasts or supporting cellular structures as well as the expression of the enamel proteins amelogenin (AMEL) and ameloblastin (AMBN) was not altered by AMTN overexpression, suggesting that protein production, processing and secretion occurred normally in transgenic mice. The expression of Odontogenic, Ameloblast-Associated (ODAM) was slightly increased in secretory stage ameloblasts of transgenic animals. The enamel in AMTN-overexpressing mice was much thinner and displayed a highly irregular surface structure compared to wild type littermates. Teeth of transgenic animals underwent rapid attrition due to the brittleness of the enamel layer. The microstructure of enamel, normally a highly ordered arrangement of hydroxyapatite crystals, was completely disorganized. Tomes' process, the hallmark of secretory stage ameloblasts, did not form in transgenic mice. Collectively our data demonstrate that the overexpression of amelotin has a profound effect on enamel structure by disrupting the formation of Tomes' process and the orderly growth of enamel prisms.

  8. Targeted overexpression of amelotin disrupts the microstructure of dental enamel.

    Directory of Open Access Journals (Sweden)

    Rodrigo S Lacruz

    Full Text Available We have previously identified amelotin (AMTN as a novel protein expressed predominantly during the late stages of dental enamel formation, but its role during amelogenesis remains to be determined. In this study we generated transgenic mice that produce AMTN under the amelogenin (Amel gene promoter to study the effect of AMTN overexpression on enamel formation in vivo. The specific overexpression of AMTN in secretory stage ameloblasts was confirmed by Western blot and immunohistochemistry. The gross histological appearance of ameloblasts or supporting cellular structures as well as the expression of the enamel proteins amelogenin (AMEL and ameloblastin (AMBN was not altered by AMTN overexpression, suggesting that protein production, processing and secretion occurred normally in transgenic mice. The expression of Odontogenic, Ameloblast-Associated (ODAM was slightly increased in secretory stage ameloblasts of transgenic animals. The enamel in AMTN-overexpressing mice was much thinner and displayed a highly irregular surface structure compared to wild type littermates. Teeth of transgenic animals underwent rapid attrition due to the brittleness of the enamel layer. The microstructure of enamel, normally a highly ordered arrangement of hydroxyapatite crystals, was completely disorganized. Tomes' process, the hallmark of secretory stage ameloblasts, did not form in transgenic mice. Collectively our data demonstrate that the overexpression of amelotin has a profound effect on enamel structure by disrupting the formation of Tomes' process and the orderly growth of enamel prisms.

  9. Measurement of fluorine total concentration in dental enamel using fast neutron activation

    International Nuclear Information System (INIS)

    Mouadili, A.; Vernais, J.; Isabelle, D.B.

    1988-01-01

    Fluorine which is present in dental enamel, at the level of a few tens to a few hundred ppm, plays an important role in the behaviour of this tissue. Therefore quantitative determination is of interest for particular studies of the dental system. We present a nuclear nondestructive method to determine the total fluorine content in dental enamel by cyclotron-produced fast-neutron activation. The 19 F(n,2n) reaction leads to 18 F which is a β + emitter with a 109.8 min half-life. The irradiated sample activity is measured by detecting in coincidence the annihilation photons. A fluorine standard is used for calibration. The detection limit is of the order of 1 ppm, while the reproducibility is better than 95% [pt

  10. Surface morphological changes on the human dental enamel and cement after the Er:YAG laser irradiation at different incidence angles; Avaliacao morfologica das superficies do esmalte e do cimento dental apos a irradiacao do laser de Er:YAG em diferentes angulacoes

    Energy Technology Data Exchange (ETDEWEB)

    Tannous, Jose Trancoso

    2001-07-01

    This is a morphological analysis study through SEM of the differences of the laser tissue interaction as a function of the laser beam irradiation angle, under different parameters of energy. Fourteen freshly extracted molars stored in a 0,9% sodium chloride solution were divided in seven pairs and were irradiated with 100, 200, 300, 400, 500, 600 and 700 mJ per pulse, respectively. Each sample received three enamel irradiations and three cement irradiations, either in the punctual or in the contact mode, one near to the other, with respectively 30, 45 and 90 inclinations degrees of dental surface-laser-beam incidence. Four Er:YAG pulses (2,94 {mu}m, 7-20 Hz, 0,1-1 J energy/pulse - Opus 20 - Opus Dent) with water cooling system (0,4 ml/s) were applied. After the laser irradiation the specimens were analysed through scanning electron microscope (SEM). The results were analysed by SEM micrographs showing a great difference on the laser tissue interaction characteristics as a function of the irradiation angle of the laser beam. All the observations led to conclude that, considering the laser parameters used, the incidence angle variation is a very important parameter regarding the desired morphological effects. This represents an extremely relevant detail on the technical description of the Er:YAG laser irradiation protocols on dental tissues. (author)

  11. Regulation of Dental Enamel Shape and Hardness

    Science.gov (United States)

    Simmer, J.P.; Papagerakis, P.; Smith, C.E.; Fisher, D.C.; Rountrey, A.N.; Zheng, L.; Hu, J.C.-C.

    2010-01-01

    Epithelial-mesenchymal interactions guide tooth development through its early stages and establish the morphology of the dentin surface upon which enamel will be deposited. Starting with the onset of amelogenesis beneath the future cusp tips, the shape of the enamel layer covering the crown is determined by five growth parameters: the (1) appositional growth rate, (2) duration of appositional growth (at the cusp tip), (3) ameloblast extension rate, (4) duration of ameloblast extension, and (5) spreading rate of appositional termination. Appositional growth occurs at a mineralization front along the ameloblast distal membrane in which amorphous calcium phosphate (ACP) ribbons form and lengthen. The ACP ribbons convert into hydroxyapatite crystallites as the ribbons elongate. Appositional growth involves a secretory cycle that is reflected in a series of incremental lines. A potentially important function of enamel proteins is to ensure alignment of successive mineral increments on the tips of enamel ribbons deposited in the previous cycle, causing the crystallites to lengthen with each cycle. Enamel hardens in a maturation process that involves mineral deposition onto the sides of existing crystallites until they interlock with adjacent crystallites. Neutralization of acidity generated by hydroxyapatite formation is a key part of the mechanism. Here we review the growth parameters that determine the shape of the enamel crown as well as the mechanisms of enamel appositional growth and maturation. PMID:20675598

  12. Proteomic Mapping of Dental Enamel Matrix from Inbred Mouse Strains: Unraveling Potential New Players in Enamel.

    Science.gov (United States)

    Lima Leite, Aline; Silva Fernandes, Mileni; Charone, Senda; Whitford, Gary Milton; Everett, Eric T; Buzalaf, Marília Afonso Rabelo

    2018-01-01

    Enamel formation is a complex 2-step process by which proteins are secreted to form an extracellular matrix, followed by massive protein degradation and subsequent mineralization. Excessive systemic exposure to fluoride can disrupt this process and lead to a condition known as dental fluorosis. The genetic background influences the responses of mineralized tissues to fluoride, such as dental fluorosis, observed in A/J and 129P3/J mice. The aim of the present study was to map the protein profile of enamel matrix from A/J and 129P3/J strains. Enamel matrix samples were obtained from A/J and 129P3/J mice and analyzed by 2-dimensional electrophoresis and liquid chromatography coupled with mass spectrometry. A total of 120 proteins were identified, and 7 of them were classified as putative uncharacterized proteins and analyzed in silico for structural and functional characterization. An interesting finding was the possibility of the uncharacterized sequence Q8BIS2 being an enzyme involved in the degradation of matrix proteins. Thus, the results provide a comprehensive view of the structure and function for putative uncharacterized proteins found in the enamel matrix that could help to elucidate the mechanisms involved in enamel biomineralization and genetic susceptibility to dental fluorosis. © 2018 S. Karger AG, Basel.

  13. Nanostructured synthetic hydroxyapatite and dental enamel heated and irradiated by ER,CR:YSGG: characterized by FTIR and XRD; Hidroxiapatita sintetica nanoestruturada e esmalte dental aquecidos e irradiados por laser de Er,Cr:YSGG: caracterizacao por FTIR e por DRX

    Energy Technology Data Exchange (ETDEWEB)

    Rabelo Neto, Jose da Silva

    2009-07-01

    The study evaluate the physical changes and/or chemical that occurs in synthetic hydroxyapatite (HAP) and in enamel under action of thermal heating in oven or laser irradiation of Er,Cr:YSGG that may cause changes in its structure to make them more resistant to demineralization aiming the formation of dental caries. The synthetic HAP was produced by reaction of solutions of Ca(NO{sub 3}) and (NH{sub 4}){sub 2}HPO{sub 4} with controlled temperature and pH. The enamel powder was collected from the bovine teeth. Samples of powder enamel and synthetic HAP were subjected to thermal heating in oven at temperatures of 200 deg C, 400 deg C, 600 deg C, 800 deg C and 1000 deg C. For the laser irradiation of materials, were made with 5,79 J/cm{sup 2} of irradiation, 7,65 J/cm{sup 2}, 10,55 J/cm{sup 2} and 13,84 J/cm{sup 2} for synthetic HAP and 7,53 J/cm{sup 2}, 10,95 J/cm{sup 2}, and 13,74 J/cm{sup 2} for the enamel. The samples were evaluated by X-ray diffraction (XRD) for analysis of crystallographic phases and analysis by the Rietveld method, to determine their respective proportions in the material, as well as results of changes of the lattice unit cell parameters (axis-a, axis-c and volume), crystallites sizes and the occupation rate of sites of Ca and P atoms. The samples were analyzed by Fourier transform infrared spectroscopy (FTIR), which should compositional changes due to treatment related to carbonate, phosphate, adsorbed water and hydroxyl radicals content. The infrared was used to measure the surface temperature generated by the laser beam in the solid samples of enamel. Besides the major hydroxyapatite crystallographic phases, there was formations of octa calcium phosphate (OCP) and phase {beta} of tricalcium phosphate ({beta}-TCP ) in enamel heated at 800 deg C. There was reduction of the axis-a, volume and size of crystallites to the temperatures between 400 degree C and 600 deg C and also on laser irradiated samples. Above the temperature of 600 degree C it

  14. Enamel tissue engineering using subcultured enamel organ epithelial cells in combination with dental pulp cells.

    Science.gov (United States)

    Honda, Masaki J; Shinmura, Yuka; Shinohara, Yoshinori

    2009-01-01

    We describe a strategy for the in vitro engineering of enamel tissue using a novel technique for culturing enamel organ epithelial (EOE) cells isolated from the enamel organ using 3T3-J2 cells as a feeder layer. These subcultured EOE cells retain the capacity to produce enamel structures over a period of extended culture. In brief, enamel organs from 6-month-old porcine third molars were dissociated into single cells and subcultured on 3T3-J2 feeder cell layers. These subcultured EOE cells were then seeded onto a collagen sponge in combination with primary dental pulp cells isolated at an early stage of crown formation, and these constructs were transplanted into athymic rats. After 4 weeks, complex enamel-dentin structures were detected in the implants. These results show that our culture technique maintained ameloblast lineage cells that were able to produce enamel in vivo. This novel subculture technique provides an important tool for tooth tissue engineering. Copyright 2008 S. Karger AG, Basel.

  15. Amelogenesis Imperfect, Enamel Hypoplasia and Fluorosis Dental - Literature Review

    Directory of Open Access Journals (Sweden)

    Flávia Magnani Bevilacqua

    2015-12-01

    Full Text Available The developmental disorders of enamel are abnormalities of structure which can affect both dentitions. These abnormalities include amelogenesis imperfecta, enamel hypoplasia and dental fluorosis. The amelogenesis imperfecta is a hereditary change and enamel hypoplasia is a quantitative defect of enamel that occurs as a result of systemic problems, local and also inherited factors, or even the combination of them. Dental fluorosis is a hypoplasia caused by the chronic ingestion of fluoride during odontogenesis. All these anomalies have similar clinical characteristics, and it is necessary to be careful in their assessment. It is extremely important to know these abnormalities to establish a differential diagnosis and, consequently, a treatment plan, which can be set for each situation. Therefore, the purpose of this study was to review the literature regarding these three anomalies: amelogenesis imperfecta, enamel hypoplasia and dental fluorosis. It was concluded that to establish the differential diagnosis of these abnormalities as well as a proper treatment plan, it is indispensable the professional knowledge associated with the clinical examination. The examination has to consist of medical history and physical examination, and in some cases, x-ray examination.

  16. Femtosecond laser etching of dental enamel for bracket bonding.

    Science.gov (United States)

    Kabas, Ayse Sena; Ersoy, Tansu; Gülsoy, Murat; Akturk, Selcuk

    2013-09-01

    The aim is to investigate femtosecond laser ablation as an alternative method for enamel etching used before bonding orthodontic brackets. A focused laser beam is scanned over enamel within the area of bonding in a saw tooth pattern with a varying number of lines. After patterning, ceramic brackets are bonded and bonding quality of the proposed technique is measured by a universal testing machine. The results are compared to the conventional acid etching method. Results show that bonding strength is a function of laser average power and the density of the ablated lines. Intrapulpal temperature changes are also recorded and observed minimal effects are observed. Enamel surface of the samples is investigated microscopically and no signs of damage or cracking are observed. In conclusion, femtosecond laser exposure on enamel surface yields controllable patterns that provide efficient bonding strength with less removal of dental tissue than conventional acid-etching technique.

  17. DENTAL ENAMEL FORMATION AND IMPLICATIONS FOR ORAL HEALTH AND DISEASE.

    Science.gov (United States)

    Lacruz, Rodrigo S; Habelitz, Stefan; Wright, J Timothy; Paine, Michael L

    2017-07-01

    Dental enamel is the hardest and most mineralized tissue in extinct and extant vertebrate species and provides maximum durability that allows teeth to function as weapons and/or tools as well as for food processing. Enamel development and mineralization is an intricate process tightly regulated by cells of the enamel organ called ameloblasts. These heavily polarized cells form a monolayer around the developing enamel tissue and move as a single forming front in specified directions as they lay down a proteinaceous matrix that serves as a template for crystal growth. Ameloblasts maintain intercellular connections creating a semi-permeable barrier that at one end (basal/proximal) receives nutrients and ions from blood vessels, and at the opposite end (secretory/apical/distal) forms extracellular crystals within specified pH conditions. In this unique environment, ameloblasts orchestrate crystal growth via multiple cellular activities including modulating the transport of minerals and ions, pH regulation, proteolysis, and endocytosis. In many vertebrates, the bulk of the enamel tissue volume is first formed and subsequently mineralized by these same cells as they retransform their morphology and function. Cell death by apoptosis and regression are the fates of many ameloblasts following enamel maturation, and what cells remain of the enamel organ are shed during tooth eruption, or are incorporated into the tooth's epithelial attachment to the oral gingiva. In this review, we examine key aspects of dental enamel formation, from its developmental genesis to the ever-increasing wealth of data on the mechanisms mediating ionic transport, as well as the clinical outcomes resulting from abnormal ameloblast function. Copyright © 2017 the American Physiological Society.

  18. Polymer coated liposomes for dental drug delivery--interactions with parotid saliva and dental enamel.

    Science.gov (United States)

    Nguyen, S; Hiorth, M; Rykke, M; Smistad, G

    2013-09-27

    The interactions between pectin coated liposomes and parotid saliva and dental enamel were studied to investigate their potential to mimic the protective biofilm formed naturally on tooth surfaces. Different pectin coated liposomes with respect to pectin type (LM-, HM- and AM-pectin) and concentration (0.05% and 0.2%) were prepared. Interactions between the pectin coated liposomes and parotid saliva were studied by turbidimetry and imaging by atomic force microscopy. The liposomes were adsorbed to hydroxyapatite (HA) and human dental enamel using phosphate buffer and parotid saliva as adsorption media. A continuous flow was imposed on the enamel surfaces for various time intervals to examine their retention on the dental enamel. The results were compared to uncoated, charged liposomes. No aggregation tendencies for the pectin coated liposomes and parotid saliva were revealed. This makes them promising as drug delivery systems to be used in the oral cavity. In phosphate buffer the adsorption to HA of pectin coated liposomes was significantly lower than the negative liposomes. The difference diminished in parotid saliva. Positive liposomes adsorbed better to the dental enamel than the pectin coated liposomes. However, when subjected to flow for 1h, no significant differences in the retention levels on the enamel were found between the formulations. For all formulations, more than 40% of the liposomes still remained on the enamel surfaces. At time point 20 min the retention of HM-pectin coated and positive liposomes were significantly higher. It was concluded that pectin coated liposomes can adsorb to HA as well as to the dental enamel. Their ability to retain on the enamel surfaces promotes the concept of using them as protective structures for the teeth. Copyright © 2013 Elsevier B.V. All rights reserved.

  19. High Radiation Doses from Radiotherapy Measured by Electron Spin Resonance in Dental Enamel

    International Nuclear Information System (INIS)

    Pass, B.; Wood, R.E.; Liu, F.; McLean, M.; Aldrich, J.E.

    1998-01-01

    For radiotherapy, an error in the complicated treatment planning or treatment procedure is a possibility, however remote. Thus, in the present study electron spin resonance (ESR) in dental enamel was investigated for the first time as a means of retrospective dosimetry for validating applied radiotherapy doses to the head and neck regions. Total absorbed radiation doses measured by ESR in dental enamel were compared to the doses determined by treatment planning for 19 patients who received radiotherapy for intra-oral, pharyngeal or laryngeal malignancies, or total-body irradiation prior to bone marrow transplants (BMT). For the 15 tumour irradiations there was, within the framework of the tooth positions as presented, general agreement between the treatment planned and ESR dose determinations. There were, however, both significant and minor discrepancies. For the BMT patients there were major discrepancies for two of the four patients investigated. This study indicates that ESR in dental enamel may be useful as the only means of retrospective dosimetry for validating applied radiotherapy doses after treatment. However, further research must be carried out before this technique can be accepted as accurate and reliable. (author)

  20. Effects of 960 nm diode laser irradiation on dental enamel in vitro: temperature and morphological analysis and evaluation of enamel demineralization; Estudo in vitro dos efeitos promovidos pelo laser de diodo em 960 nm no esmalte dental humano: analise de temperatura, analise morfologica e avaliacao da resistencia a desmineralizacao

    Energy Technology Data Exchange (ETDEWEB)

    Kato, Ilka Tiemy

    2004-07-01

    The aim of this study is to determine the effects of diode laser irradiation on enamel demineralization. To achieve this goal appropriate photon absorbing substances for the laser radiation, safe laser parameters and adequate temperature measuring apparatus had to be determined. Next, the effects of diode laser and acidulated phosphate fluoride on enamel demineralization by calcium content analysis were evaluated with inductively coupled plasma atomic emission spectrometry (ICP-AES). In the first part of the study, five dyes consisting of vegetable coal diluted in five different liquids were analyzed and vegetable coal diluted in physiological solution was chosen for use as absorber. Methodologies to measure pulp chamber temperature were evaluated and modeling clay was chosen as fixture for the enamel samples held at body temperature. In the second part of the study, different energy density parameters (1.8 J/cm{sup 2}, 3.7 J/cm{sup 2}, 5.6 J/cm{sup 2}, 7.4 J/cm{sup 2} and 9.3 J/cm{sup 2}) exposure times (10, 15, 20, 25 e 30 seconds) and time intervals between dye application and laser irradiation (5, 30, 60, 90 e 120 seconds) were evaluated with respect to temperature changes in the pulp chamber. The enamel morphology was analyzed by scanning electron microscopy. Acid resistance was measured using seventy five enamel specimens, divided in five groups (control, fluoride, laser, laser + fluoride and fluoride + laser). The amount of calcium lost during demineralization in lactic acid was measured by ICP-AES. The results obtained in this experiment permit the conclusion that diode laser irradiation did not increase acid resistance. When associated with fluoride, the acid resistance did not differ from the results obtained with fluoride alone. (author)

  1. Application of the ultrashort pulses in bovine dental enamel

    International Nuclear Information System (INIS)

    Todescan, Carla de Rago

    2003-01-01

    The interaction of lasers with the hard structures of the teeth, has found the excess of heat as a problem for its utilization. This study analyzes, in vitro, the interaction of the ultrashort pulse laser of Ti:safire (830 nm) with the bovine dental enamel. The system consisted in one main oscillator integrated with an amplifier (CPA). The pulses extracted before the temporal compression inside the amplifier had 30 ps, 1000 Hz and ∼1 mJ. The pulses extracted after the compression had 60 fs, 1000 Hz and ∼0,7 mJ. The M 2 was 1,3, the focal lens 2,5 cm, the focal distance 29,7 and a computerized translation stage x,y,z. We evaluated the amount of tissue removed per pulse,the resulting cavities and the surrounding tissues not irradiated, under OM and SEM. The fluency was the major factor for differentiating the two regimens studied, therefore, the intensity was not so important as we expected in this process. We found: one ablation region in 'cat tongue', one ablation length, one fluency ∼0,7 J/cm 2 for 30 ps and ∼0,5 J/cm 2 for 60 fs (50% of high speed burr), smooth edge for 30 ps and high precision of the sharp edge cut of submicrometric order for 60 fs. (author)

  2. Towards enamel biomimetics: Structure, mechanical properties and biomineralization of dental enamel

    Science.gov (United States)

    Fong, Hanson Kwok

    Dental enamel is the most mineralized tissue in the human body. This bioceramic, composed largely of hydroxyapatite (HAp), is also one of the most durable tissues despite a lifetime of masticatory loading and bacterial attack. The biosynthesis of enamel, which occurs in physiological conditions is a complex orchestration of protein assembly and mineral formation. The resulting product is the hardest tissue in the vertebrate body with the longest and most organized arrangement of hydroxyapatite crystals known to biomineralizing systems. Detail understanding of the structure of enamel in relationship to its mechanical function and the biomineralization process will provide a framework for enamel regeneration as well as potential lessons in the design of engineering materials. The objective of this study, therefore, is twofold: (1) establish the structure-function relationship of enamel as well as the dentine-enamel junction (DEJ) and (2) determine the effect of proteins on the enamel biomineralization process. A hierarchy in the enamel structure was established by means of various microscopy techniques (e.g. SEM, TEM, AFM). Mechanical properties (hardness and elastic modulus) associated with the microstructural features were also determined by nanoindentation. Furthermore, the DEJ was found to have a width in the range of micrometers to 10s of micrometers with continuous change in structure and mechanical properties. Indentation tests and contact fatigue tests using a spherical indenter have revealed that the structural features in the enamel and the DEJ played important roles in containing crack propagation emanating from the enamel tissue. To further understand the effect of this protein on the biominerailzation process, we have studied genetically engineered animals that express altered amelogenin which lack the known self-assembly properties. This in vivo study has revealed that, without the proper self-assembly of the amelogenin protein as demonstrated by the

  3. Recovery of crystallographic texture in remineralized dental enamel.

    Science.gov (United States)

    Siddiqui, Samera; Anderson, Paul; Al-Jawad, Maisoon

    2014-01-01

    Dental caries is the most prevalent disease encountered by people of all ages around the world. Chemical changes occurring in the oral environment during the caries process alter the crystallography and microstructure of dental enamel resulting in loss of mechanical function. Little is known about the crystallographic effects of demineralization and remineralization. The motivation for this study was to develop understanding of the caries process at the crystallographic level in order to contribute towards a long term solution. In this study synchrotron X-ray diffraction combined with scanning electron microscopy and scanning microradiography have been used to correlate enamel crystallography, microstructure and mineral concentration respectively in enamel affected by natural caries and following artificial demineralization and remineralization regimes. In particular, the extent of destruction and re-formation of this complex structure has been measured. 2D diffraction patterns collected at the European Synchrotron Radiation Facility were used to quantify changes in the preferred orientation (crystallographic texture) and position of the (002) Bragg reflection within selected regions of interest in each tooth slice, and then correlated with the microstructure and local mineral mass. The results revealed that caries and artificial demineralization cause a large reduction in crystallographic texture which is coupled with the loss of mineral mass. Remineralization restores the texture to the original level seen in healthy enamel and restores mineral density. The results also showed that remineralization promotes ordered formation of new crystallites and growth of pre-existing crystallites which match the preferred orientation of healthy enamel. Combining microstructural and crystallographic characterization aids the understanding of caries and erosion processes and assists in the progress towards developing therapeutic treatments to allow affected enamel to regain

  4. Recovery of crystallographic texture in remineralized dental enamel.

    Directory of Open Access Journals (Sweden)

    Samera Siddiqui

    Full Text Available Dental caries is the most prevalent disease encountered by people of all ages around the world. Chemical changes occurring in the oral environment during the caries process alter the crystallography and microstructure of dental enamel resulting in loss of mechanical function. Little is known about the crystallographic effects of demineralization and remineralization. The motivation for this study was to develop understanding of the caries process at the crystallographic level in order to contribute towards a long term solution. In this study synchrotron X-ray diffraction combined with scanning electron microscopy and scanning microradiography have been used to correlate enamel crystallography, microstructure and mineral concentration respectively in enamel affected by natural caries and following artificial demineralization and remineralization regimes. In particular, the extent of destruction and re-formation of this complex structure has been measured. 2D diffraction patterns collected at the European Synchrotron Radiation Facility were used to quantify changes in the preferred orientation (crystallographic texture and position of the (002 Bragg reflection within selected regions of interest in each tooth slice, and then correlated with the microstructure and local mineral mass. The results revealed that caries and artificial demineralization cause a large reduction in crystallographic texture which is coupled with the loss of mineral mass. Remineralization restores the texture to the original level seen in healthy enamel and restores mineral density. The results also showed that remineralization promotes ordered formation of new crystallites and growth of pre-existing crystallites which match the preferred orientation of healthy enamel. Combining microstructural and crystallographic characterization aids the understanding of caries and erosion processes and assists in the progress towards developing therapeutic treatments to allow affected

  5. Composition of enamel pellicle from dental erosion patients.

    Science.gov (United States)

    Carpenter, G; Cotroneo, E; Moazzez, R; Rojas-Serrano, M; Donaldson, N; Austin, R; Zaidel, L; Bartlett, D; Proctor, G

    2014-01-01

    Oral health is dependent upon a thin mobile film of saliva on soft and hard tissues. Salivary proteins adhere to teeth to form the acquired enamel pellicle which is believed to protect teeth from acid erosion. This study investigated whether patients suffering diet-induced dental erosion had altered enamel pellicles. Thirty patients suffering erosion were compared to healthy age-matched controls. Subjects wore a maxillary splint holding hydroxyapatite and human enamel blocks for 1 h. The acquired enamel pellicle was removed from the blocks and compared to the natural incisor pellicle. Basic Erosive Wear Examination scores confirmed that dental erosion was present in erosion patients and absent from healthy age-matched controls. Erosion patients had half the amount of proteins (BCA assay) within the acquired pellicle forming on splint blocks compared to normal controls (p erosion patients (p erosion patients and healthy controls. In summary, the formation of new acquired pellicles on surfaces was reduced in erosion patients, which may explain their greater susceptibility to acid erosion of teeth. © 2014 S. Karger AG, Basel.

  6. Error in assessing the absorbed dose from the EPR signal from dental enamel

    International Nuclear Information System (INIS)

    Kleshchenko, E.D.; Kushnereva, K.K.

    1997-01-01

    Dose measurements from EPR signals from dental enamel were analyzed in a random sampling of 100 teeth extracted in liquidators of the Chernobyl accident aftermath and the EPR spectra of dental enamel of 80 intact teeth from children studied. The mean square deviation of enamel sensitivity to ionizing radiation in some teeth is approximately 0.3 of the mean sensitivity value. The variability of the nature EPR spectrum of dental enamel limits in principle the lower threshold of EPR-measured 60 mGy doses. When assessing the individual absorbed doses from the EPR signal from dental enamel without additional exposure it is necessary to bear in mind the extra error of approximately 6-% at a confidence probability P=0.95 caused by the variability of enamel sensitivity to radiation in some teeth. This additional error may be ruled out by graduated additional exposure of the examined enamel samples

  7. Potential of sub-ablative pulsed CO{sub 2} laser irradiation on inhibition of artificial caries-like lesion progress in bovine dental enamel; Potencial de inibicao da progressao da carie artificial por irradiacao sub-ablativa com laser de CO{sub 2} pulsado em esmalte dental bovino

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, Marcella Esteves

    2005-07-01

    The aim of this study was to investigate whether sub-ablative pulsed C0{sub 2} laser (1 0,6 {mu}m) irradiation is capable of reducing the susceptibility of the dental enamel to demineralization, and thus achieving a potential caries-protective effect. The crowns of 51 bovine front teeth, embedded in acrylic resin and polished until exposure of flat enamel surface, were used. The samples were cut in cubes of 10x10 mm, and totally coated with acid-resistant nail varnish, except for an enamel exposed window of 16 mm square. Three groups (n=17) were obtained: control group (CG) not irradiated; group laser A (LA) and group laser B (LB) where the samples were irradiated. The conditions were 60 mJ, 100 Hz, 0,3 J/cm{sup 2} for LA and 135 mJ, 10 Hz, 0,7 J/cm{sup 2} for LB. Two samples of each group were submitted to SEM analysis and fifteen to demineralization in 3 ml acetate buffer solution (0,1 mol/L) with pH 4,5 for 24h at 37 deg C, with regular agitation. After the specimens were removed from the solution, the calcium and phosphorous content were measured with an inductively coupled plasma optical emission spectrometer and 2 more samples of each were submitted to SEM analysis. The obtained Ca and P means in {mu}g/ml and the calculated Ca/P molar ratio were: CG (367,88 {+-} 33,47; 168,91 {+-} 14,55; 1,70 {+-} 0,07) ; LA (372,70 {+-} 41,70; 161,46 {+-} 15,26; 1,79 {+-} 0,07) and LB (328,87 {+-} 24,91; 145,02 {+-} 11,04; 1,77 {+-} 0,05). The ANOVA statistical test revealed statistically significant difference for [Ca], [P] e Ca/P content between the groups (p<0,05). The Tukey test results showed that LB had significantly lower means of Ca and P content in demineralization solution than the other groups (p<0,01), and between LA and control there was not statistically significant difference. For the Ca/P molar ratio LA and LB means were significantly higher than the control (p<0,01) and there was not statistical difference between the two irradiated groups. SEM observations

  8. The Chernobyl accident: EPR dosimetry on dental enamel of children

    International Nuclear Information System (INIS)

    Gualtieri, G.; Colacicchi, S.; Sgattoni, R.; Giannoni, M.

    2001-01-01

    The radiation dose on tooth enamel of children living close to Chernobyl has been evaluated by EPR. The sample preparation was reduced to a minimum of mechanical steps to remove a piece of enamel. A standard X-ray tube at low energy was used for additive irradiation. The filtration effect of facial soft tissue was taken into account. The radiation dose for a group of teeth slightly exceeds the annual dose, whereas for another group the dose very much exceeds the annual dose. Since the higher dose is found in teeth whose enamel have much lower EPR sensitivity to the radiation, it can be suggested that for these teeth the native signal could alter the evaluation of the smaller radiation signal

  9. Dental enamel defect diagnosis through different technology-based devices.

    Science.gov (United States)

    Kobayashi, Tatiana Yuriko; Vitor, Luciana Lourenço Ribeiro; Carrara, Cleide Felício Carvalho; Silva, Thiago Cruvinel; Rios, Daniela; Machado, Maria Aparecida Andrade Moreira; Oliveira, Thais Marchini

    2018-06-01

    Dental enamel defects (DEDs) are faulty or deficient enamel formations of primary and permanent teeth. Changes during tooth development result in hypoplasia (a quantitative defect) and/or hypomineralisation (a qualitative defect). To compare technology-based diagnostic methods for detecting DEDs. Two-hundred and nine dental surfaces of anterior permanent teeth were selected in patients, 6-11 years of age, with cleft lip with/without cleft palate. First, a conventional clinical examination was conducted according to the modified Developmental Defects of Enamel Index (DDE Index). Dental surfaces were evaluated using an operating microscope and a fluorescence-based device. Interexaminer reproducibility was determined using the kappa test. To compare groups, McNemar's test was used. Cramer's V test was used for comparing the distribution of index codes obtained after classification of all dental surfaces. Cramer's V test revealed statistically significant differences (P < .0001) in the distribution of index codes obtained using the different methods; the coefficients were 0.365 for conventional clinical examination versus fluorescence, 0.961 for conventional clinical examination versus operating microscope and 0.358 for operating microscope versus fluorescence. The sensitivity of the operating microscope and fluorescence method was statistically significant (P = .008 and P < .0001, respectively). Otherwise, the results did not show statistically significant differences in accuracy and specificity for either the operating microscope or the fluorescence methods. This study suggests that the operating microscope performed better than the fluorescence-based device and could be an auxiliary method for the detection of DEDs. © 2017 FDI World Dental Federation.

  10. Quantitative assessment of the enamel machinability in tooth preparation with dental diamond burs.

    Science.gov (United States)

    Song, Xiao-Fei; Jin, Chen-Xin; Yin, Ling

    2015-01-01

    Enamel cutting using dental handpieces is a critical process in tooth preparation for dental restorations and treatment but the machinability of enamel is poorly understood. This paper reports on the first quantitative assessment of the enamel machinability using computer-assisted numerical control, high-speed data acquisition, and force sensing systems. The enamel machinability in terms of cutting forces, force ratio, cutting torque, cutting speed and specific cutting energy were characterized in relation to enamel surface orientation, specific material removal rate and diamond bur grit size. The results show that enamel surface orientation, specific material removal rate and diamond bur grit size critically affected the enamel cutting capability. Cutting buccal/lingual surfaces resulted in significantly higher tangential and normal forces, torques and specific energy (pmachinability for clinical dental practice. Copyright © 2014 Elsevier Ltd. All rights reserved.

  11. Dental radiography: tooth enamel EPR dose assessment from Rando phantom measurements

    International Nuclear Information System (INIS)

    Aragno, D.; Fattibene, P.; Onori, S.

    2000-01-01

    Electron paramagnetic resonance dosimetry of tooth enamel is now established as a suitable method for individual dose reconstruction following radiation accidents. The accuracy of the method is limited by some confounding factors, among which is the dose received due to medical x-ray irradiation. In the present paper the EPR response of tooth enamel to endoral examination was experimentally evaluated using an anthropomorphic phantom. The dose to enamel for a single exposure of a typical dental examination performed with a new x-ray generation unit working at 65 kVp gave rise to a CO 2 -signal of intensity similar to that induced by a dose of about 2 mGy of 60 Co. EPR measurements were performed on the entire tooth with no attempt to separate buccal and lingual components. Also the dose to enamel for an orthopantomography exam was estimated. It was derived from TLD measurements as equivalent to 0.2 mGy of 60 Co. In view of application to risk assessment analysis, in the present work the value for the ratio of the reference dose at the phantom surface measured with TLD to the dose at the tooth measured with EPR was determined. (author)

  12. Signal processing for radiation dosimetry using EPR in dental enamel: comparison of three methods

    International Nuclear Information System (INIS)

    Pass, B. Barry.; Shames, A.I. Alexander I.

    2000-01-01

    We are reporting an alternative method of extracting useful dose information from complex EPR spectra of dental enamel. Digital differentiation of the initial first derivative spectrum followed by filtering is used to clearly distinguish the radiation-induced signal from the native background signal. The peak-to-peak height of the resulting second derivative of the signal is then measured as an indication of absorbed dose. This method does not require preliminary elimination of the native background signal, and is not effected by any uncertainty in the determination of the background signal or by errors resulting from the subtraction of two signals of comparable magnitude. Ten enamel samples were irradiated with known doses in the range of 250-10 5 mGy. There was agreement for all the samples, within the typical experimental error of ±10% for EPR dosimetry in dental enamel, between the doses determined by two common techniques using native signal subtraction and the doses determined by the new second derivative method proposed here

  13. Functions of KLK4 and MMP-20 in dental enamel formation

    Science.gov (United States)

    Lu, Yuhe; Papagerakis, Petros; Yamakoshi, Yasuo; Hu, Jan C-C.; Bartlett, John D.; Simmer, James P.

    2009-01-01

    Two proteases are secreted into the enamel matrix of developing teeth. The early protease is enamelysin (MMP-20). The late protease is kallikrein 4 (KLK4). Mutations in MMP20 and KLK4 both cause autosomal recessive amelogenesis imperfecta, a condition featuring soft, porous enamel containing residual protein. MMP-20 is secreted along with enamel proteins by secretory stage ameloblasts. Enamel protein cleavage products accumulate in the space between the crystal ribbons, helping to support them. MMP-20 steadily cleaves accumulated enamel proteins, so their concentration decreases with depth. Kallikrein 4 is secreted by transition and maturation stage ameloblasts. KLK4 aggressively degrades the retained organic matrix following the termination of enamel protein secretion. The principle functions of MMP-20 and KLK4 in dental enamel formation are to facilitate the orderly replacement of organic matrix with mineral, generating an enamel layer that is harder, less porous, and unstained by retained enamel proteins. PMID:18627287

  14. In vitro study of demineralization resistance and fluoride retention in dental enamel irradiated with Er,Cr: YSGG laser; Estudo in vitro da resistencia a desmineralizacao e da retencao de fluor em esmalte dental irradiado com laser de Er, Cr: YSGG

    Energy Technology Data Exchange (ETDEWEB)

    Ana, Patricia Aparecida da. E-mail: patriciadaana@yahoo.com.br

    2007-07-01

    This study aimed to establish irradiation conditions of Er,Cr:YSGG laser ({lambda} of 2.79 {mu}m) which could propitiate changes on human dental enamel and increase its resistance to demineralization, when associated or not with topical application of acidulated phosphate fluoride (APF). Fluences of 2,8 J/cm{sup 2}, 5,6 J/cm{sup 2} e 8,5 J/cm{sup 2} were selected; they were associated or not with previous application of a photo absorber (coal paste) and then APF was applied or not after laser irradiation. In a first step, the morphological findings, the surface temperatures, and the pupal temperatures were evaluated during laser irradiation. After that, the treated samples were submitted to a a ten-day pH-cycling model. After producing the incipient white-spots lesions, the following aspects were evaluated: the mineral loss, the loosely bound fluoride and the firmly bound fluoride. All the demineralizing and remineralizing pH-cycling solutions were evaluated with respect to their calcium (Ca), inorganic phosphorous (Pi) and fluoride (F{sup -}) concentrations. The data had their normality and homogeneity distribution statistically evaluated, and it was chosen an appropriated statistical test for each performed analysis according to the obtained results, considering 5% significant level. The fluences selected for this study created ablated surfaces; the fluences of 5.6 J/cm{sup 2} and 8.5 J/cm{sup 2} promoted increments in surface temperature above 110 deg C. The intrapupal temperature changes revealed that laser irradiation did not increase the pulpal temperatures above the critical threshold for induction of pulpitis. The coal paste did not promote any changes on surface morphology or in the intrapulpal temperature changes; however, this paste increased the surface temperatures during laser irradiation. Only laser irradiation at 8.5 J/cm{sup 2} was able to decrease the mineral loss when compared to the no-treatment group; although the association of coal paste

  15. Enamel microabrasion for aesthetic management of dental fluorosis.

    Science.gov (United States)

    Pandey, Pallavi; Ansari, Afroz Alam; Moda, Preeti; Yadav, Madhulika

    2013-10-11

    Fluorosis has increased in recent times due to fluoridation of drinking water and addition of fluoride to various edible items, which leads to unaesthetic appearance of teeth visible at close quarters. The enamel microabrasion technique is a conservative method that improves the appearance of the teeth by restoring bright and superficial smoothness, without causing significant structural loss. The aim of this article is to describe an easy technique for managing mild to moderate dental fluorosis using Opalustre (Ultradent Products) microabrasion slurry. This conservative approach may be considered an interesting alternative to more invasive prosthetic techniques like composite resin restorations, ceramic veneers or crown fabrications.

  16. A comparative study on component volumes from outer to inner dental enamel in relation to enamel tufts.

    Science.gov (United States)

    Setally Azevedo Macena, Marcus; de Alencar e Silva Leite, Maria Luísa; de Lima Gouveia, Cíntia; de Lima, Tamires Alcoforado Sena; Athayde, Priscilla Alves Aguiar; de Sousa, Frederico Barbosa

    2014-06-01

    Dental enamel presents marked mechanical properties gradients from outer to inner enamel, a region lacking component volumes profiles. Tufts, structures of inner enamel, have been shown to play a role in enamel resilience. We aimed at comparing component volumes from inner to outer enamel in relation to enamel tufts. Transversal ground sections from the cervical half of unerupted human third molars (n=10) were prepared and histological points were selected along transversal lines (extending from innermost to outer enamel) traced across tufts and adjacent control areas without tufts. Component volumes were measured at each histological point. Component volumes ranges were: 70.6-98.5% (mineral), 0.02-20.78% (organic), 3.8-9.8% (total water), 3-9% (firmly bound water), and 0.02-3.3% (loosely bound water). Inner enamel presented the lowest mineral volumes and the highest non-mineral volumes. Mineral, water and organic contents differed as a function of the distance from innermost enamel but not between the tuft and control lines. Tufts presented opaqueness in polarizing microscopy (feature of fracture lines). Organic volume gradient correlated with a relatively flat profile of loosely bound water. Inner, but not outer enamel, rehydrated after air-dried enamel was heated to 50°C and re-exposed to room conditions, as predicted by the organic/water gradient profiles. Component volumes vary markedly from outer to inner enamel, but not between areas with or without tufts (that behave like fracture lines under polarizing microscopy). Copyright © 2014 Elsevier Ltd. All rights reserved.

  17. Retrospective dosimetry by electronic paramagnetic resonance (EPR) in dental enamel

    International Nuclear Information System (INIS)

    Dubner, D.; Gisone, P.; Perez, M.R.; Davila, F.A.; Boveris, A.; Puntarulo, S.

    1998-01-01

    Biophysical dosimetry based on EPR in biological solid samples (like bone and teeth) or in organic materials (like textile fibres, sugar, etc.) is a complementary technique that could contribute, along with the biological dosimetry, to the retrospective evaluation of the absorbed dose in accidental situations. Dental enamel could be considered as the only tissue with structure and composition essentially constant over time: this characteristic feature allows its use as an index of radiation exposure since tooth retains indefinitely its radiation history. Samples of human molars were exposed to gamma-Rays (Co 60) with doses between 0,5 Gy to 10 Gy. After a chemical treatment of samples, enamel was removed by grinding with a dental drill and reduced to a fine powder. A characteristic EPR signal was detected at g=2.002. The dose effect curves were done using 20 mw of microwave power. Measurements were done both, with flat cells and disposable Pasteur pipettes allowing the use of lower amounts of sample. The intensity of the signal was proportional to the dose and linearity was verified in both cases. We discuss the applicability of this technique in evaluating radiation dose in accidental overexposures. (author) [es

  18. In vitro study of the diode laser effect on artificial demineralized surface of human dental enamel; Estudo in vitro do efeito do laser diodo sobre a superficie de esmalte dental humano desmineralizado artificialmente

    Energy Technology Data Exchange (ETDEWEB)

    Ebel, Patricia

    2003-07-01

    In scientific literature there are many reports about fusion and resolidification of dental enamel after laser irradiation and their capability to generate surfaces with increased resistance to demineralization compared to non-irradiated areas. The use of high power diode laser on demineralized surfaces of human dental enamel is presented as a good alternative in caries prevention. The purpose of this study is to investigate the morphological changes produced by the use of one high power diode laser on human dental enamel surface after demineralization treatment with lactic acid, under chosen parameters. Fifteen samples of human dental molars were used and divided in four groups: control - demineralization treatment with lactic acid and no irradiation, and demineralization treatment with lactic acid followed of irradiation with 212,20 mJ/cm{sup 2}, 282,84 mJ/cm{sup 2} and 325,38 mJ/cm{sup 2}, respectively. The samples were irradiated with high power diode laser (808 nm) with a 300 {mu}m diameter fiber optics. Black ink was used on enamel surface to enhance the superficial absorption. The samples were studied by optical microscopy and scanning electron microscopy. Modifications on the enamel surfaces were observed. Such modifications were characterized by melted and re-solidified region of the enamel. According with our results the best parameter was 2.0 W, presenting the most uniform surface. The use of high power diode laser as demonstrated in this study is able to promote melting and re-solidification on human dental enamel. (author)

  19. Mesoscopic modeling of the response of human dental enamel to mid-infrared radiation

    Science.gov (United States)

    Vila Verde, Ana; Ramos, Marta; Stoneham, A. M.

    2006-03-01

    Ablation of human dental enamel, a composite biomaterial with water pores, is of significant importance in minimally invasive laser dentistry but progress in the area is hampered by the lack of optimal laser parameters. We use mesoscopic finite element models of this material to study its response to mid-infrared radiation. Our results indicate that the cost-effective, off-the-shelf CO2 laser at λ = 10.6 μm may in fact ablate enamel precisely, reproducibly and with limited unwanted side effects such as cracking or heating, provided that a pulse duration of 10 μs is used. Furthermore, our results also indicate that the Er:YAG laser (λ = 2.94 μm), currently popular for laser dentistry, may in fact cause unwanted deep cracking in the enamel when regions with unusually high water content are irradiated, and also provide an explanation for the large range of ablation threshold values observed for this material. The model may be easily adapted to study the response of any composite material to infrared radiation and thus may be useful for the scientific community.

  20. Utilization of radiometric method in evaluation of wear on human dental enamel in vitro by dental porcelain glazed and polished; Utilizacao do metodo radiometrico na avaliacao in vitro do desgaste provocado ao esmalte dental humano por porcelanas dentais glazeadas e polidas

    Energy Technology Data Exchange (ETDEWEB)

    Adachi, Lena Katekawa; Campos, Tomie Nakakuki de; Adachi, Eduardo Makoto [Sao Paulo Univ., SP (Brazil). Faculdade de Odontologia. Dept. de Protese]. E-mail: katekawa@usp.br; Saiki, Mitiko [Instituto de Pesquisas Energeticas e Nucleares (IPEN), Sao Paulo, SP (Brazil)]. E-mail: mitiko@curiango.ipen.br

    2005-07-01

    The dental porcelain is a material commonly used in prosthesis. Disadvantages of dental porcelain use include possibility to cause tooth or dental materials wear. Before its use in the mouth, surfaces are treated with polishing and/or glazing. This research used the radiometric method to verify the influence of these surface treatments on the porcelains of commercial brands: Ceramco II, Noritake and Finesse. This method was originally developed for dentifrice abrasiveness evaluation. Five specimens of dental enamel and 10 specimens of each porcelain (5 glazed, 5 polished) were used. The dental enamel was flattened and irradiated with neutrons from the IEA-R1 (IPEN/CNEN) nuclear reactor. Then it was weared by each porcelain in sliding motion, with water. After 2,500 cycles for each porcelain specimen, the released enamel residue was measured. The enamel wear was evaluated by measuring beta activity of {sup 32}P transferred to water from the irradiated tooth. Results varied from 2.57 to 5.81 {mu}g of enamel /mm{sup 2} weared surface. There was no statistical difference ({alpha}=0.05) between dental enamel wear caused by the same porcelains glazed or polished. The results suggest that adequate surface finishing depend on the type of dental porcelain. (author)

  1. Sea otter dental enamel is highly resistant to chipping due to its microstructure.

    Science.gov (United States)

    Ziscovici, Charles; Lucas, Peter W; Constantino, Paul J; Bromage, Timothy G; van Casteren, Adam

    2014-10-01

    Dental enamel is prone to damage by chipping with large hard objects at forces that depend on chip size and enamel toughness. Experiments on modern human teeth have suggested that some ante-mortem chips on fossil hominin enamel were produced by bite forces near physiological maxima. Here, we show that equivalent chips in sea otter enamel require even higher forces than human enamel. Increased fracture resistance correlates with more intense enamel prism decussation, often seen also in some fossil hominins. It is possible therefore that enamel chips in such hominins may have formed at even greater forces than currently envisaged. © 2014 The Author(s) Published by the Royal Society. All rights reserved.

  2. FT-Raman spectroscopic characterization of enamel surfaces irradiated with Nd:YAG and Er:YAG lasers

    Directory of Open Access Journals (Sweden)

    Sima Shahabi

    2016-12-01

    Full Text Available Background. Despite recent advances in dental caries prevention, caries is common and remains a serious health problem. Laser irradiation is one of the most common methods in preventive measures in recent years. Raman spectroscopy technique is utilized to study the microcrystalline structure of dental enamel. In this study, FT-Raman spectroscopy was used to evaluate chemical changes in enamel structure irradiated with Nd:YAG and Er:YAG lasers. Methods. We used 15 freshly-extracted, non-carious, human molars that were treated as follows: No treatment was carried out in group A (control group; Group B was irradiated with Er:YAG laser for 10 seconds under air and water spray; and Group C was irradiated with Nd:YAG laser for 10 seconds under air and water spray. After treatment, the samples were analyzed by FT-Raman spectroscopy. Results. The carbonate content evaluation with regard to the integrated area under the curve (1065/960 cm–1 exhibited a significant reduction in its ratio in groups B and C. The organic content (2935/960 cm-1 area exhibited a significant decrease after laser irradiation in group B and C. Conclusion. The results showed that the mineral and organic matrices of enamel structure were affected by laser irradiation; therefore, it might be a suitable method for caries prevention.

  3. Exogenous mineralization of hard tissues using photo-absorptive minerals and femto-second lasers; the case of dental enamel.

    Science.gov (United States)

    Anastasiou, A D; Strafford, S; Thomson, C L; Gardy, J; Edwards, T J; Malinowski, M; Hussain, S A; Metzger, N K; Hassanpour, A; Brown, C T A; Brown, A P; Duggal, M S; Jha, A

    2018-04-15

    A radical new methodology for the exogenous mineralization of hard tissues is demonstrated in the context of laser-biomaterials interaction. The proposed approach is based on the use of femtosecond pulsed lasers (fs) and Fe 3+ -doped calcium phosphate minerals (specifically in this work fluorapatite powder containing Fe 2 O 3 nanoparticles (NP)). A layer of the synthetic powder is applied to the surface of eroded bovine enamel and is irradiated with a fs laser (1040 nm wavelength, 1 GHz repetition rate, 150 fs pulse duration and 0.4 W average power). The Fe 2 O 3 NPs absorb the light and may act as thermal antennae, dissipating energy to the vicinal mineral phase. Such a photothermal process triggers the sintering and densification of the surrounding calcium phosphate crystals thereby forming a new, dense layer of typically ∼20 μm in thickness, which is bonded to the underlying surface of the natural enamel. The dispersed iron oxide NPs, ensure the localization of temperature excursion, minimizing collateral thermal damage to the surrounding natural tissue during laser irradiation. Simulated brushing trials (pH cycle and mechanical force) on the synthetic layer show that the sintered material is more acid resistant than the natural mineral of enamel. Furthermore, nano-indentation confirms that the hardness and Young's modulus of the new layers are significantly more closely matched to enamel than current restorative materials used in clinical dentistry. Although the results presented herein are exemplified in the context of bovine enamel restoration, the methodology may be more widely applicable to human enamel and other hard-tissue regenerative engineering. In this work we provide a new methodology for the mineralisation of dental hard tissues using femtosecond lasers and iron doped biomaterials. In particular, we demonstrate selective laser sintering of an iron doped fluorapatite on the surface of eroded enamel under low average power and mid

  4. Real-time near-IR imaging of laser-ablation crater evolution in dental enamel

    Science.gov (United States)

    Darling, Cynthia L.; Fried, Daniel

    2007-02-01

    We have shown that the enamel of the tooth is almost completely transparent near 1310-nm in the near-infrared and that near-IR (NIR) imaging has considerable potential for the optical discrimination of sound and demineralized tissue and for observing defects in the interior of the tooth. Lasers are now routinely used for many applications in dentistry including the ablation of dental caries. The objective of this study was to test the hypothesis that real-time NIR imaging can be used to monitor laser-ablation under varying conditions to assess peripheral thermal and transient-stress induced damage and to measure the rate and efficiency of ablation. Moreover, NIR imaging may have considerable potential for monitoring the removal of demineralized areas of the tooth during cavity preparations. Sound human tooth sections of approximately 3-mm thickness were irradiated by a CO II laser under varying conditions with and without a water spray. The incision area in the interior of each sample was imaged using a tungsten-halogen lamp with band-pass filter centered at 131--nm combined with an InGaAs focal plane array with a NIR zoom microscope in transillumination. Due to the high transparency of enamel at 1310-nm, laser-incisions were clearly visible to the dentin-enamel junction and crack formation, dehydration and irreversible thermal changes were observed during ablation. This study showed that there is great potential for near-IR imaging to monitor laser-ablation events in real-time to: assess safe laser operating parameters by imaging thermal and stress-induced damage, elaborate the mechanisms involved in ablation such as dehydration, and monitor the removal of demineralized enamel.

  5. Penetration of Streptococcus sobrinus and Streptococcus sanguinis into dental enamel.

    Science.gov (United States)

    Kneist, Susanne; Nietzsche, Sandor; Küpper, Harald; Raser, Gerhard; Willershausen, Brita; Callaway, Angelika

    2015-10-01

    The aim of this pilot study was to assess the difference in virulence of acidogenic and aciduric oral streptococci in an in vitro caries model using their penetration depths into dental enamel. 30 caries-free extracted molars from 11- to 16-year-olds were cleaned ultrasonically for 1 min with de-ionized water and, after air-drying, embedded in epoxy resin. After 8-h of setting at room temperature, the specimens were ground on the buccal side with SiC-paper 1200 (particle size 13-16 μm). Enamel was removed in circular areas sized 3 mm in diameter; the mean depth of removed enamel was 230 ± 60 μm. 15 specimens each were incubated anaerobically under standardized conditions with 24 h-cultures of Streptococcus sanguinis 9S or Streptococcus sobrinus OMZ 176 in Balmelli broth at 37 ± 2 °C; the pH-values of the broths were measured at the beginning and end of each incubation cycle. After 2, 4, 6, 8, and 10 weeks 3 teeth each were fixed in 2.5% glutaraldehyde in cacodylate buffer for 24 h, washed 3× and dehydrated 30-60min by sequential washes through a series of 30-100% graded ethanol. The teeth were cut in half longitudinally; afterward, two slits were made to obtain fracture surfaces in the infected area. After critical-point-drying the fragments were gold-sputtered and viewed in a scanning electron microscope at magnifications of ×20-20,000. After 10 weeks of incubation, penetration of S. sanguinis of 11.13 ± 24.04 μm below the break edges into the enamel was observed. The invasion of S. sobrinus reached depths of 87.53 ± 76.34 μm. The difference was statistically significant (paired t test: p = 0.033). The experimental penetration depths emphasize the importance of S. sanguinis versus S. sobrinus in the context of the extended ecological plaque hypothesis. Copyright © 2015 Elsevier Ltd. All rights reserved.

  6. Isotopic study of the comparative uptake and release of ions by deciduous and permanent dental enamel

    International Nuclear Information System (INIS)

    Tetteh, G.K.

    1975-01-01

    A comparative study of the uptake and release of calcium, orthophosphate, strontium and sodium from decidus and permanent dental enamel has been made using radioactive techniques. The rates of uptake and release of orthophosphate, strontium and sodium were observed to be greater in deciduous than in permanent enamel. However, for calcium, the rate of uptake was observed to be greater in the deciduous than in the permanent enamel but the rate of release was observed to be smaller in the deciduous enamel. These results in conjunction with the findings of Tetteh (1974) suggest that most of the calcification in the early stages of development of dental enamel is by a hetero-ionic exchange. (author) [fr

  7. Isotopic study of the comparative uptake and release of ions by deciduous and permanent dental enamel

    Energy Technology Data Exchange (ETDEWEB)

    Tetteh, G K [Department of Physics, University of Ghana,Legon

    1975-04-01

    A comparative study of the uptake and release of calcium, orthophosphate, strontium and sodium from decidus and permanent dental enamel has been made using radioactive techniques. The rates of uptake and release of orthophosphate, strontium and sodium were observed to be greater in deciduous than in permanent enamel. However, for calcium, the rate of uptake was observed to be greater in the deciduous than in the permanent enamel but the rate of release was observed to be smaller in the deciduous enamel. These results in conjunction with the findings of Tetteh (1974) suggest that most of the calcification in the early stages of development of dental enamel is by a hetero-ionic exchange.

  8. The vanadium content of human dental enamel and its relationship to caries

    International Nuclear Information System (INIS)

    Byrne, A.R.; Vrbic, V.

    1979-01-01

    A method for the determination of vanadium in dental enamel based on neutron activation analysis is described. After rapid dissolution of the irradiated sample in perchloric acid, 52 V is quickly separated by solvent extraction from mixed perchloric-hydrochloric medium with N-benzoyl-N-phenyl hydroxylamine (BPHA) reagent in toluene in 95% yield. The technique was applied to samples from a low caries area of Dalmatia, Zemunik (DMFT 5), in the same region. No significant differences in vanadium content were found between the two areas, nor between deciduous and permanent teeth. The levels in other areas of Yugoslavia were found to be similar, with a mean concentration of 3.7 +- 1.5 ngxg -1 for 37 samples, with a nearly normal distribution; a few impacted teeth gave lower values. The method can also be adapted to the analysis of bone and biological materials generally. (author)

  9. Vanadium content of human dental enamel and its relationship to caries

    Energy Technology Data Exchange (ETDEWEB)

    Byrne, A R [Institut Jozef Stefan, Ljubljana (Yugoslavia); Vrbic, V [Ljubljana Univ. (Yugoslavia)

    1979-01-01

    A method for the determination of vanadium in dental enamel based on neutron activation analysis is described. After rapid dissolution of the irradiated sample in perchloric acid, /sup 52/V is quickly separated by solvent extraction from mixed perchloric-hydrochloric medium with N-benzoyl-N-phenyl hydroxylamine (BPHA) reagent in toluene in 95% yield. The technique was applied to samples from a low caries area of Dalmatia, Zemunik (DMFT < 2), and a normal area, Novigrad (DMFT > 5), in the same region. No significant differences in vanadium content were found between the two areas, nor between deciduous and permanent teeth. The levels in other areas of Yugoslavia were found to be similar, with a mean concentration of 3.7 +- 1.5 ngxg/sup -1/ for 37 samples, with a nearly normal distribution; a few impacted teeth gave lower values. The method can also be adapted to the analysis of bone and biological materials generally.

  10. Anisotropic local physical properties of human dental enamel in comparison to properties of some common dental filling materials.

    Science.gov (United States)

    Raue, Lars; Hartmann, Christiane D; Rödiger, Matthias; Bürgers, Ralf; Gersdorff, Nikolaus

    2014-11-01

    A major aspect in evaluating the quality of dental materials is their physical properties. Their properties should be a best fit of the ones of dental hard tissues. Manufacturers give data sheets for each material. The properties listed are characterized by a specific value. This assumes (but does not prove) that there is no direction dependence of the properties. However, dental enamel has direction-dependent properties which additionally vary with location in the tooth. The aim of this paper is to show the local direction dependence of physical properties like the elastic modulus or the thermal expansion in dental hard tissues. With this knowledge the 'perfect filling/dental material' could be characterized. Enamel sections of ∼400-500 μm thickness have been cut with a diamond saw from labial/buccal to palatal/lingual (canine, premolar and molar) and parallel to labial (incisor). Crystallite arrangements have been measured in over 400 data points on all types of teeth with x-ray scattering techniques, known from materials science. X-ray scattering measurements show impressively that dental enamel has a strong direction dependence of its physical properties which also varies with location within the tooth. Dental materials possess only little or no property direction dependence. Therefore, a mismatch was found between enamel and dental materials properties. Since dental materials should possess equal (direction depending) properties, worthwhile properties could be characterized by transferring the directional properties of enamel into a property 'wish list' which future dental materials should fulfil. Hereby the 'perfect dental material' can be characterized.

  11. Prevalence of enamel defects and association with dental caries in preschool children.

    Science.gov (United States)

    Massignan, C; Ximenes, M; da Silva Pereira, C; Dias, L; Bolan, M; Cardoso, M

    2016-12-01

    This was to evaluate the prevalence of the developmental defects of enamel (DDE) in primary teeth and its association with dental caries. A cross-sectional study with a randomised representative sample was carried out with 1101 children aged 2-5 years enrolled in public preschools (50% prevalence of DDE in primary teeth, a standard error of 3%, and a confidence level of 95%). Three calibrated dentists (K > 0.62) performed clinical examination. Data collected were: sex, age, DDE (Modified DDE Index) and dental caries (WHO). Descriptive analysis, Chi-square test and multinomial logistic regression were applied for data analysis. Among children, 565 (51.3%) were boys; mean age was 3.7 (±0.9 years). The prevalence of enamel defect was 39.1%; the prevalence of diffuse opacities, demarcated opacities and enamel hypoplasia was 25.3, 19.1 and 6.1%, respectively. The prevalence of dental caries was 31.0%, with mean def-t 1.14 (±2.44). Primary teeth with enamel hypoplasia had three times the odds of having dental caries than those with absence of enamel defects (OR = 3.10; 95% CI: 1.91, 5.01). The presence of enamel defects was moderate and associated with dental caries.

  12. Association between developmental defects of enamel and dental caries: A systematic review and meta-analysis.

    Science.gov (United States)

    Vargas-Ferreira, F; Salas, M M S; Nascimento, G G; Tarquinio, S B C; Faggion, C M; Peres, M A; Thomson, W M; Demarco, F F

    2015-06-01

    Dental caries is the main problem oral health and it is not well established in the literature if the enamel defects are a risk factor for its development. Studies have reported a potential association between developmental defects enamel (DDE) and dental caries occurrence. We investigated the association between DDE and caries in permanent dentition of children and teenagers. A systematic review was carried out using four databases (Pubmed, Web of Science, Embase, and Science Direct), which were searched from their earliest records until December 31, 2014. Population-based studies assessing differences in dental caries experience according to the presence of enamel defects (and their types) were included. PRISMA guidelines for reporting systematic reviews were followed. Meta-analysis was performed to assess the pooled effect, and meta-regression was carried out to identify heterogeneity sources. From the 2558 initially identified papers, nine studies fulfilled all inclusion criteria after checking the titles, abstracts, references, and complete reading. Seven of them were included in the meta-analysis with random model. A positive association between enamel defects and dental caries was identified; meta-analysis showed that individuals with DDE had higher pooled odds of having dental caries experience [OR 2.21 (95% CI 1.3; 3.54)]. Meta-regression analysis demonstrated that adjustment for sociodemographic factors, countries' socioeconomic status, and bias (quality of studies) explained the high heterogeneity observed. A higher chance of dental caries should be expected among individuals with enamel defects. Copyright © 2015 Elsevier Ltd. All rights reserved.

  13. Association of dental enamel lead levels with risk factors for environmental exposure.

    Science.gov (United States)

    Olympio, Kelly Polido Kaneshiro; Naozuka, Juliana; Oliveira, Pedro Vitoriano; Cardoso, Maria Regina Alves; Bechara, Etelvino José Henriques; Günther, Wanda Maria Risso

    2010-10-01

    To analyze household risk factors associated with high lead levels in surface dental enamel. A cross-sectional study was conducted with 160 Brazilian adolescents aged 1418 years living in poor neighborhoods in the city of Bauru, southeastern Brazil, from August to December 2008. Body lead concentrations were assessed in surface dental enamel acid-etch microbiopsies. Dental enamel lead levels were measured by graphite furnace atomic absorption spectrometry and phosphorus levels were measured by inductively coupled plasma optical emission spectrometry. The parents answered a questionnaire about their children's potential early (05 years old) exposure to well-known lead sources. Logistic regression was used to identify associations between dental enamel lead levels and each environmental risk factor studied. Social and familial covariables were included in the models. The results suggest that the adolescents studied were exposed to lead sources during their first years of life. Risk factors associated with high dental enamel lead levels were living in or close to a contaminated area (OR = 4.49; 95% CI: 1.69;11.97); and member of the household worked in the manufacturing of paints, paint pigments, ceramics or batteries (OR = 3.43; 95% CI: 1.31;9.00). Home-based use of lead-glazed ceramics, low-quality pirated toys, anticorrosive paint on gates and/or sale of used car batteries (OR = 1.31; 95% CI: 0.56;3.03) and smoking (OR = 1.66; 95% CI: 0.52;5.28) were not found to be associated with high dental enamel lead levels. Surface dental enamel can be used as a marker of past environmental exposure to lead and lead concentrations detected are associated to well-known sources of lead contamination.

  14. Association of dental enamel lead levels with risk factors for environmental exposure

    Directory of Open Access Journals (Sweden)

    Kelly Polido Kaneshiro Olympio

    2010-10-01

    Full Text Available OBJECTIVE: To analyze household risk factors associated with high lead levels in surface dental enamel. METHODS: A cross-sectional study was conducted with 160 Brazilian adolescents aged 14-18 years living in poor neighborhoods in the city of Bauru, southeastern Brazil, from August to December 2008. Body lead concentrations were assessed in surface dental enamel acid-etch microbiopsies. Dental enamel lead levels were measured by graphite furnace atomic absorption spectrometry and phosphorus levels were measured by inductively coupled plasma optical emission spectrometry. The parents answered a questionnaire about their children's potential early (05 years old exposure to well-known lead sources. Logistic regression was used to identify associations between dental enamel lead levels and each environmental risk factor studied. Social and familial covariables were included in the models. RESULTS: The results suggest that the adolescents studied were exposed to lead sources during their first years of life. Risk factors associated with high dental enamel lead levels were living in or close to a contaminated area (OR = 4.49; 95% CI: 1.69;11.97; and member of the household worked in the manufacturing of paints, paint pigments, ceramics or batteries (OR = 3.43; 95% CI: 1.31;9.00. Home-based use of lead-glazed ceramics, low-quality pirated toys, anticorrosive paint on gates and/or sale of used car batteries (OR = 1.31; 95% CI: 0.56;3.03 and smoking (OR = 1.66; 95% CI: 0.52;5.28 were not found to be associated with high dental enamel lead levels. CONCLUSIONS: Surface dental enamel can be used as a marker of past environmental exposure to lead and lead concentrations detected are associated to well-known sources of lead contamination.

  15. Dental enamel defects in Italian children with cystic fibrosis: an observational study.

    Science.gov (United States)

    Ferrazzano, G F; Sangianantoni, G; Cantile, T; Amato, I; Orlando, S; Ingenito, A

    2012-03-01

    The relationship between cystic fibrosis (CF) and caries experience has already been explored, but relatively little information is available on dental enamel defects prevalence among children affected by cystic fibrosis. The aim of this study was to investigate this issue in deciduous and permanent teeth of children with CF resident in southern Italy. This cross sectional observational study was undertaken between October 2009 and March 2010. 88 CF patients and 101 healthy age-matched participated in this study. The prevalence of dental enamel defects was calculated using a modified Developmental Defects of Enamel (DDE) index. The comparison of dental enamel defects prevalence among groups was carried out using regression binary logistic analysis. In the CF subjects there was a higher prevalence (56%) of enamel defects in comparison to the healthy group (22%). The most prevalent enamel defect was hypoplasia with loss of enamel (23% of CF patients vs 1 1/2% of control group) in permanent teeth. This study confirms that children with cystic fibrosis are at increased risk of developing hypoplastic defects on their permanent teeth.

  16. Influence of bleaching agents on surface roughness of sound or eroded dental enamel specimens.

    Science.gov (United States)

    Azrak, Birgül; Callaway, Angelika; Kurth, Petra; Willershausen, Brita

    2010-12-01

    The aim of the present in vitro study was to assess the effect of bleaching agents on eroded and sound enamel specimens. Enamel specimens prepared from human permanent anterior teeth were incubated with different bleaching agents containing active ingredients as 7.5 or 13.5% hydrogen peroxide or 35% carbamide peroxide, ranging in pH from 4.9 to 10.8. The effect of the tooth whitening agents on surface roughness was tested for sound enamel surfaces as well as for eroded enamel specimens. To provoke erosive damage, the enamel specimens were incubated for 10 hours with apple juice (pH = 3.4). Afterwards, pretreated and untreated dental slices were incubated with one of the bleaching agents for 10 hours. The surface roughness (R(a)) of all enamel specimens (N = 80) was measured using an optical profilometric device. A descriptive statistical analysis of the R(a) values was performed. The study demonstrated that exposure to an acidic bleaching agent (pH = 4.9) resulted in a higher surface roughness (p = 0.043) than treatment with a high peroxide concentration (pH = 6.15). If the enamel surface was previously exposed to erosive beverages, subsequent bleaching may enhance damage to the dental hard tissue. Bleaching agents with a high concentration of peroxide or an acidic pH can influence the surface roughness of sound or eroded enamel. © 2010, COPYRIGHT THE AUTHORS. JOURNAL COMPILATION © 2010, WILEY PERIODICALS, INC.

  17. Ceramic-like wear behaviour of human dental enamel.

    Science.gov (United States)

    Arsecularatne, J A; Hoffman, M

    2012-04-01

    This paper reports a transmission electron microscopy (TEM) analysis of subsurfaces of enamel specimens following in vitro reciprocating wear tests with an enamel cusp sliding on a flat enamel specimen under hydrated conditions. The obtained results show that crack formation occurred in the wear scar subsurface. The path followed by these cracks seems to be dictated either by the histological structure of enamel or by the contact stress field. Moreover, the analysis of a set of enamel wear results obtained from the literature and application of fracture-based models, originally developed for ceramics, correlate well, confirming the similar wear processes taking place in these materials. This analysis also reveals a marked influence of coefficient of friction on the enamel wear rate: for a higher coefficient of friction value, enamel wear can be severe even under forces generated during normal operation of teeth. Copyright © 2011 Elsevier Ltd. All rights reserved.

  18. Retrospective radiation dosimetry using electron paramagnetic resonance in canine dental enamel

    International Nuclear Information System (INIS)

    Khan, Rao F.H.; Pekar, J.; Rink, W.J.; Boreham, D.R.

    2005-01-01

    Electron paramagnetic resonance (EPR) biodosimetry of human tooth enamel has been widely used for measuring radiation doses in various scenarios. We have now developed EPR dosimetry in tooth enamel extracted from canines. Molars and incisors from canines were cleaned by processing in supersaturated aqueous potassium hydroxide solution. The dosimetric signal in canine tooth enamel was found to increase linearly as a function of laboratory added dose from 0.44±0.02 to 4.42±0.22 Gy. The gamma radiation sensitivity of the canine molar enamel was found to be comparable to that of human tooth enamel. The dosimetric signal in canine enamel has been found to be stable up to at least 6 weeks after in vitro irradiation. A dosimetric signal variation of 10-25% was observed for canines ranging from in age 3 years to 16 year old

  19. Enamel protein regulation and dental and periodontal physiopathology in MSX2 mutant mice.

    Science.gov (United States)

    Molla, Muriel; Descroix, Vianney; Aïoub, Muhanad; Simon, Stéphane; Castañeda, Beatriz; Hotton, Dominique; Bolaños, Alba; Simon, Yohann; Lezot, Frédéric; Goubin, Gérard; Berdal, Ariane

    2010-11-01

    Signaling pathways that underlie postnatal dental and periodontal physiopathology are less studied than those of early tooth development. Members of the muscle segment homeobox gene (Msx) family encode homeoproteins that show functional redundancy during development and are known to be involved in epithelial-mesenchymal interactions that lead to crown morphogenesis and ameloblast cell differentiation. This study analyzed the MSX2 protein during mouse postnatal growth as well as in the adult. The analysis focused on enamel and periodontal defects and enamel proteins in Msx2-null mutant mice. In the epithelial lifecycle, the levels of MSX2 expression and enamel protein secretion were inversely related. Msx2+/- mice showed increased amelogenin expression, enamel thickness, and rod size. Msx2-/- mice displayed compound phenotypic characteristics of enamel defects, related to both enamel-specific gene mutations (amelogenin and enamelin) in isolated amelogenesis imperfecta, and cell-cell junction elements (laminin 5 and cytokeratin 5) in other syndromes. These effects were also related to ameloblast disappearance, which differed between incisors and molars. In Msx2-/- roots, Malassez cells formed giant islands that overexpressed amelogenin and ameloblastin that grew over months. Aberrant expression of enamel proteins is proposed to underlie the regional osteopetrosis and hyperproduction of cellular cementum. These enamel and periodontal phenotypes of Msx2 mutants constitute the first case report of structural and signaling defects associated with enamel protein overexpression in a postnatal context.

  20. Fluoride reactions with dental enamel following different forms of fluoride supply

    International Nuclear Information System (INIS)

    Hellstroem, I.; Ericsson, Y.

    1976-01-01

    The reactions with dental enamel of NaF as tablets dissolved in different beverages or supplied with NaCl, simulating domestic salt fluoridation, were studied in tests with enamel surfaces and enamel powder. It was confirmed that powdered enamel can react quite differently from enamel surfaces under certain conditions. Enamel surfaces took up much more fluoride (F) from orange juice than from water or milk, and neither the low pH nor the citrate content of the juice increased the formation of unstable CaF 2 in the enamel, as judged from a KOH leaching test. The F uptake by enamel surfaces from 0.25 mM NaF in 175 mM NaCl, corresponding to a dish prepared with salt containing 500 parts/10 6 F, was about 80 percent greater than from the same NaF concentration in water. This NaCl concentration did not increase the formation of CaF 2 in the enamel, as judged from the KOH test, while 350 mM NaCl caused a moderate increase. The investigations support the administration of NaF tablets with orange juice and the plans for domestic salt fluoridation. (author)

  1. Fluoride uptake from restorative dental materials by human enamel

    International Nuclear Information System (INIS)

    Forsten, L.; Rytoemaa, I.; Anttila, A.; Keinonen, J.

    1976-01-01

    The purpose of the study was to determine the uptake in vitro of fluoride from restorative materials by tooth enamel and whether prior etching of the enamel causes a change of uptake. The outermost layer of the labial surface of extracted canines was removed by grinding and the enamel was covered with five different fluoride-containing materials ; a silicate, a composite resin, an amalgam, a silicophosphate, and a polycarboxylate luting cement. The material was either removed immediately or after storing the tooth in distilled water. The fluoride content was determined using a sensitive physical method based on the 19 F (p, αγ) 16 O reaction. In addition, the fluoride content of enamel after etching for different periods of time and of etched enamel which had been in contact with silicate cement was determined. The mean fluoride content of uncovered interior enamel was 226 parts 10 6 . All materials, except the composite, increased clearly the fluoride content of the underlying enamel. Etching of interior enamel also increased the fluoride values. No difference could be shown in fluoride uptake from silicate and composite resin between etched and unetched enamel. (author)

  2. Laser investigation of the non-uniformity of fluorescent species in dental enamel

    Science.gov (United States)

    Tran, Stephanie U.; Ridge, Jeremy S.; Nelson, Leonard Y.; Seibel, Eric J.

    In the present study, artificial type I and type II erosions were created on dental specimen using acetic acid and EDTA respectively. Specimens were prepared by etching extracted teeth samples in acid to varying degrees, after which the absolute fluorescence intensity ratio of the etched enamel relative to sound enamel was recorded for each specimen using 405 and 532 nm laser excitation. Results showed differences in the fluorescence ratio of etched to sound enamel for type I and II erosions. These findings suggest a non-uniform distribution of fluorescent species in the interprismatic region as compared to the prismatic region.

  3. Distribution patterns of elements in dental enamel of G. blacki: a preliminary dietary investigation using SRXRF

    Energy Technology Data Exchange (ETDEWEB)

    Qu, Yating; Hu, Yaowu; Shang, Xue; Wang, Changsui [Chinese Academy of Sciences, Lab of Human Evolution, Institute of Vertebrate Paleontology and Paleoanthropology, Beijing (China); University of Chinese Academy of Sciences, Department of Scientific History and Archaeometry, School of Humanities, Beijing (China); Jin, Changzhu; Zhang, Yingqi [Chinese Academy of Sciences, Key Laboratory of Evolutionary Systematics of Vertebrates, Institute of Vertebrate Paleontology and Paleoanthropology, Beijing (China)

    2013-04-15

    We measured the elemental mappings in dental enamel of Gigantopithecus blacki (n=3) using synchrotron radiation X-ray fluorescence (SRXRF) to understand the dietary variation during the time of tooth eruption. In order to account for the effects of diagenesis on the variation of elements in these fossil teeth, we compared the Fe and Mn elemental distribution and levels in dental enamel of G. blacki with that of a single modern pig tooth and found no differences. The observation of the variations of Sr, Ca and RE (rare earth elements) distribution in the incremental lines reveals that the plant foods utilized by G. blacki from the early Pleistocene or the middle Pleistocene had varied during the formation of dental enamel, possibly caused by the change of living environment or food resources. The variations of elemental distribution in different incremental lines are very promising to understand the nutritional and physical stress of G. blacki during the tooth eruption and environmental adaptations. (orig.)

  4. Distribution patterns of elements in dental enamel of G. blacki: a preliminary dietary investigation using SRXRF

    Science.gov (United States)

    Qu, Yating; Jin, Changzhu; Zhang, Yingqi; Hu, Yaowu; Shang, Xue; Wang, Changsui

    2013-04-01

    We measured the elemental mappings in dental enamel of Gigantopithecus blacki ( n=3) using synchrotron radiation X-ray fluorescence (SRXRF) to understand the dietary variation during the time of tooth eruption. In order to account for the effects of diagenesis on the variation of elements in these fossil teeth, we compared the Fe and Mn elemental distribution and levels in dental enamel of G. blacki with that of a single modern pig tooth and found no differences. The observation of the variations of Sr, Ca and RE (rare earth elements) distribution in the incremental lines reveals that the plant foods utilized by G. blacki from the early Pleistocene or the middle Pleistocene had varied during the formation of dental enamel, possibly caused by the change of living environment or food resources. The variations of elemental distribution in different incremental lines are very promising to understand the nutritional and physical stress of G. blacki during the tooth eruption and environmental adaptations.

  5. Distribution patterns of elements in dental enamel of G. blacki: a preliminary dietary investigation using SRXRF

    International Nuclear Information System (INIS)

    Qu, Yating; Hu, Yaowu; Shang, Xue; Wang, Changsui; Jin, Changzhu; Zhang, Yingqi

    2013-01-01

    We measured the elemental mappings in dental enamel of Gigantopithecus blacki (n=3) using synchrotron radiation X-ray fluorescence (SRXRF) to understand the dietary variation during the time of tooth eruption. In order to account for the effects of diagenesis on the variation of elements in these fossil teeth, we compared the Fe and Mn elemental distribution and levels in dental enamel of G. blacki with that of a single modern pig tooth and found no differences. The observation of the variations of Sr, Ca and RE (rare earth elements) distribution in the incremental lines reveals that the plant foods utilized by G. blacki from the early Pleistocene or the middle Pleistocene had varied during the formation of dental enamel, possibly caused by the change of living environment or food resources. The variations of elemental distribution in different incremental lines are very promising to understand the nutritional and physical stress of G. blacki during the tooth eruption and environmental adaptations. (orig.)

  6. Titanium dioxide in dental enamel as a trace element and its variation with bleaching.

    Science.gov (United States)

    Vargas-Koudriavtsev, Tatiana; Durán-Sedó, Randall; Herrera-Sancho, Óscar-Andrey

    2018-06-01

    Titanium is a less studied trace element in dental enamel. Literature relates an increased Titanium concentration with a decreased enamel crystal domain size, which in turn is related to a higher color value. The aim of our study was to analyze the effect of tooth bleaching agents on its concentration in dental enamel by means of confocal Raman spectroscopy. Human teeth were randomly distributed in six experimental groups (n=10) and submitted to different bleaching protocols according to the manufacturer´s instructions. Confocal Raman spectroscopy was carried out in order to identify and quantify the presence of titanium dioxide molecules in enamel prior to and during whitening. Statistical analysis included repeated measures analysis of variance ( p ≤0.05) and Bonferroni pairwise comparisons. Titanium dioxide concentration was negatively affected by the longer bleaching protocols (at-home bleaching gels). All in-office whitening products increased significantly the studied molecule ( p ≤0,05). All dental specimens depicted the presence of titanium dioxide as a trace element in dental enamel. Bleaching gels that have to be applied at higher concentrations but for shorter periods of time increase the concentration of titanium dioxide, whilst at-home whitening gels used for longer periods of time despite the lower concentration caused a loss in titanium. Key words: Bleaching, whitening, hydrogen peroxide, carbamide peroxide, Raman spectroscopy, titanium dioxide.

  7. Oral aspects in celiac disease children: clinical and dental enamel chemical evaluation.

    Science.gov (United States)

    de Carvalho, Fabrício Kitazono; de Queiroz, Alexandra Mussolino; Bezerra da Silva, Raquel Assed; Sawamura, Regina; Bachmann, Luciano; Bezerra da Silva, Léa Assed; Nelson-Filho, Paulo

    2015-06-01

    The aim of this study was to evaluate the oral manifestations of celiac disease (CD), the chemical composition of dental enamel, and the occurrence of CD in children with dental enamel defects (DEDs). In the study, 52 children with CD and 52 controls were examined for DEDs, recurrent aphthous stomatitis (RAS), dental caries experience, and salivary parameters. In addition, 10 exfoliated primary enamel molars from each group were analyzed by energy dispersive x-ray spectroscopy and Fourier transform infrared spectroscopy. Fifty children with DEDs were submitted to CD diagnosis. Among the children with CD, a higher prevalence of DEDs (P = .00001) and RAS (P = .0052), lower caries experience (P = .0024), and reduction of salivary flow (P = .0060) were observed. Dental enamel from the children with CD demonstrated a lower calcium-to-phosphorus ratio (P = .0136), but no difference in the carbonate-to-phosphate ratio (P = .5862) was observed. In the multivariate analysis, CD was a protective factor for caries (OR = 0.74) and a risk factor for RAS (OR3.23). The children with CD presented with more RAS, DEDs, reduction of salivary flow, and chemical alterations in the enamel. Copyright © 2015 Elsevier Inc. All rights reserved.

  8. Impact of combined CO2 laser irradiation and fluoride on enamel and dentin biofilm-induced mineral loss.

    Science.gov (United States)

    Esteves-Oliveira, Marcella; El-Sayed, Karim Fawzy; Dörfer, Christof; Schwendicke, Falk

    2017-05-01

    The caries-protective effects of CO 2 laser irradiation on dental enamel have been demonstrated using chemical demineralization models. We compared the effect of CO 2 laser irradiation, sodium fluoride, or both on biofilm-induced mineral loss (∆Z) and Streptococcus mutans adhesion to enamel and dentin in vitro. Ground, polished bovine enamel, and dentin samples were allocated to four groups (n = 12/group): no treatment (C); single 22,600-ppm fluoride (F) varnish (5 % NaF) application; single CO 2 laser treatment (L) with short pulses (5 μs/λ = 10.6 μm); and laser and subsequent fluoride treatment (LF). Samples were sterilized and submitted to an automated mono-species S. mutans biofilm model. Brain heart infusion plus 5 % sucrose medium was provided eight times daily, followed by rinses with artificial saliva. After 10 days, bacterial numbers in biofilms were enumerated as colony-forming units/ml (CFU/ml) (n = 7/group). ∆Z was assessed using transversal microradiography (n = 12/group). Univariate ANOVA with post hoc Tukey honestly-significant-difference test was used for statistical analysis. Bacterial numbers were significantly higher on dentin than enamel (p  0.05). In dentin, only LF (163/227) significantly reduced ∆Z (p fluoride application was required to protect dentin.

  9. Physical and adhesive properties of dental enamel after radiotherapy and bonding of metal and ceramic brackets.

    Science.gov (United States)

    Santin, Gabriela Cristina; Palma-Dibb, Regina Guenka; Romano, Fábio Lourenço; de Oliveira, Harley Francisco; Nelson Filho, Paulo; de Queiroz, Alexandra Mussolino

    2015-08-01

    The increasing success rates for cancer patients treated with radiotherapy and the frequent occurrence of tooth loss during treatment have led to an increased demand for orthodontic treatment after radiotherapy. The aim of this study was to evaluate tooth enamel of irradiated teeth after the bonding and debonding of metal and ceramic brackets. Ten permanent molars were cut into enamel fragments measuring 1 mm(2) and divided into an irradiated group (total dose of 60 Gy) and a nonirradiated group. The fragments were subjected to microshear testing to evaluate whether radiotherapy altered the strength of the enamel. Furthermore, 90 prepared premolars were divided into 6 groups and subgroups (n = 15): group 1, nonirradiated and nonaged; group 2, nonirradiated and aged (thermal cycled); group 3, irradiated and aged; each group was divided into 2 subgroups: metallic and ceramic brackets. After thermal cycling and radiotherapy, the brackets were bonded onto the specimens with Transbond XT (3M Unitek, Monrovia, Calif). After 24 hours, the specimens were subjected to the shear tests. Images of the enamel surfaces were classified using the adhesive remnant index. The composite resin-enamel interface was also evaluated. Enamel fragments subjected to radiation had lower strength than did the nonirradiated samples (P enamel interface, resin tags were more extensive on irradiated tooth enamel. Radiation decreased tooth enamel strength, and the specimens treated with radiotherapy had higher frequencies of adhesive failure between the bracket and the composite resin as well as more extensive tags. Copyright © 2015 American Association of Orthodontists. Published by Elsevier Inc. All rights reserved.

  10. Acids with an equivalent taste lead to different erosion of human dental enamel.

    Science.gov (United States)

    Beyer, Markus; Reichert, Jörg; Bossert, Jörg; Sigusch, Bernd W; Watts, David C; Jandt, Klaus D

    2011-10-01

    The consumption of acidic soft drinks may lead to demineralization and softening of human dental enamel, known as dental erosion. The aims of this in vitro study were to determine: (i) if different acids with a similar sensorial acidic taste lead to different hardness loss of enamel and (ii) if the fruit acids tartaric, malic, lactic or ascorbic acid lead to less hardness loss of enamel than citric or phosphoric acid when their concentration in solution is based on an equivalent sensorial acidic taste. Enamel samples of non-erupted human third molars were treated with acidic solutions of tartaric (TA), malic (MA), lactic (LA), ascorbic (AA), phosphoric (PA) and citric (CA) acids with a concentration that gave an equivalent sensorial acidic taste. The acidic solutions were characterized by pH value and titratable acidity. Atomic force microscopy (AFM) based nanoindentation was used to study the nano mechanical properties and scanning electron microscopy (SEM) was used to study the morphology of the treated enamel samples and the untreated control areas, respectively. The investigated acids fell into two groups. The nano hardnesses of MA, TA and CA treated enamel samples (group I) were statistically significantly greater (penamel samples (group II). Within each group the nano hardness was not statistically significantly different (p>0.05). The SEM micrographs showed different etch prism morphologies depending on the acid used. In vitro, the acids investigated led to different erosion effects on human dental enamel, despite their equivalent sensorial acidic taste. This has not been reported previously. Copyright © 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

  11. Morphology and structure of polymer layers protecting dental enamel against erosion.

    Science.gov (United States)

    Beyer, Markus; Reichert, Jörg; Sigusch, Bernd W; Watts, David C; Jandt, Klaus D

    2012-10-01

    Human dental erosion caused by acids is a major factor for tooth decay. Adding polymers to acidic soft drinks is one important approach to reduce human dental erosion caused by acids. The aim of this study was to investigate the thickness and the structure of polymer layers adsorbed in vitro on human dental enamel from polymer modified citric acid solutions. The polymers propylene glycol alginate (PGA), highly esterified pectin (HP) and gum arabic (GA) were used to prepare polymer modified citric acids solutions (PMCAS, pH 3.3). With these PMCAS, enamel samples were treated for 30, 60 and 120s respectively to deposit polymer layers on the enamel surface. Profilometer scratches on the enamel surface were used to estimate the thickness of the polymer layers via atomic force microscopy (AFM). The composition of the deposited polymer layers was investigated with X-ray photoelectron spectroscopy (XPS). In addition the polymer-enamel interaction was investigated with zeta-potential measurements and scanning electron microscopy (SEM). It has been shown that the profilometer scratch depth on the enamel with deposited polymers was in the range of 10nm (30s treatment time) up to 25nm (120s treatment time). Compared to this, the unmodified CAS-treated surface showed a greater scratch depth: from nearly 30nm (30s treatment time) up to 60nm (120s treatment time). Based on XPS measurements, scanning electron microscopy (SEM) and zeta-potential measurements, a model was hypothesized which describes the layer deposited on the enamel surface as consisting of two opposing gradients of polymer molecules and hydroxyapatite (HA) particles. In this study, the structure and composition of polymer layers deposited on in vitro dental enamel during treatment with polymer modified citric acid solutions were investigated. Observations are consistent with a layer consisting of two opposing gradients of hydroxyapatite particles and polymer molecules. This leads to reduced erosive effects of

  12. Chromatographic separation of alkaline phosphatase from dental enamel

    DEFF Research Database (Denmark)

    Moe, D; Kirkeby, S; Salling, E

    1989-01-01

    Alkaline phosphatase (AP) was prepared from partly mineralized bovine enamel by extraction in phosphate buffer, centrifugation and various chromatographic techniques. Chromatofocusing showed that the enamel enzyme possessed five isoelectric points at the acid pH level ranging from pH 5.7 to pH 4.......4. Three enzyme peaks were eluted using low pressure chromatography with a Bio-gel column. With a HPLC gel filtration column the separation of the enamel extract resulted in only one peak with AP activity. The fractions of this peak were used to produce an antibody against bovine AP....

  13. Effects of enamel abrasion, salivary pellicle, and measurement angle on the optical assessment of dental erosion

    Science.gov (United States)

    Lussi, Adrian; Bossen, Anke; Höschele, Christoph; Beyeler, Barbara; Megert, Brigitte; Meier, Christoph; Rakhmatullina, Ekaterina

    2012-09-01

    The present study assessed the effects of abrasion, salivary proteins, and measurement angle on the quantification of early dental erosion by the analysis of reflection intensities from enamel. Enamel from 184 caries-free human molars was used for in vitro erosion in citric acid (pH 3.6). Abrasion of the eroded enamel resulted in a 6% to 14% increase in the specular reflection intensity compared to only eroded enamel, and the reflection increase depended on the erosion degree. Nevertheless, monitoring of early erosion by reflection analysis was possible even in the abraded eroded teeth. The presence of the salivary pellicle induced up to 22% higher reflection intensities due to the smoothing of the eroded enamel by the adhered proteins. However, this measurement artifact could be significantly minimized (pmeasurement angles from 45 to 60 deg did not improve the sensitivity of the analysis at late erosion stages. The applicability of the method for monitoring the remineralization of eroded enamel remained unclear in a demineralization/remineralization cycling model of early dental erosion in vitro.

  14. Correlation between enamel morphological and dental pulp physiological outcomes as a function of lasing parameters

    Science.gov (United States)

    Arcoria, Charles J.; Wagner, Martin J.; Vitasek, Bunny A.

    1992-06-01

    Previous oral medicine research has insufficiently quantified and correlated laser effects on calcified/soft-tissue combinations. The purpose of this study was to explain lasing effects on outcome variables (pulp response and enamel condition). Vital animal molars were irradiated using several mediums, with predetermined energy densities serving as independent variables. Predetermined safe-tissue thresholds, including pulp/enamel conditions, can be demonstrated to display linear relationships using several laser systems.

  15. Dental enamel defects in adult coeliac disease: prevalence and correlation with symptoms and age at diagnosis.

    Science.gov (United States)

    Trotta, Lucia; Biagi, Federico; Bianchi, Paola I; Marchese, Alessandra; Vattiato, Claudia; Balduzzi, Davide; Collesano, Vittorio; Corazza, Gino R

    2013-12-01

    Coeliac disease is a condition characterized by a wide spectrum of clinical manifestations. Any organ can be affected and, among others, dental enamel defects have been described. Our aims were to study the prevalence of dental enamel defects in adults with coeliac disease and to investigate a correlation between the grade of teeth lesion and clinical parameters present at the time of diagnosis of coeliac disease. A dental examination was performed in 54 coeliac disease patients (41 F, mean age 37 ± 13 years, mean age at diagnosis 31 ± 14 years). Symptoms leading to diagnosis were diarrhoea/weight loss (32 pts.), anaemia (19 pts.), familiarity (3 pts.); none of the patients was diagnosed because of enamel defects. At the time of evaluation, they were all on a gluten-free diet. Enamel defects were classified from grade 0 to 4 according to its severity. Enamel defects were observed in 46/54 patients (85.2%): grade 1 defects were seen in 18 patients (33.3%) grade 2 in 16 (29.6%), grade 3 in 8 (14.8%), and grade 4 in 4 (7.4%). We also observed that grades 3 and 4 were more frequent in patients diagnosed with classical rather than non-classical coeliac disease (10/32 vs. 2/20). However, this was not statistically significant. This study confirms that enamel defects are common in adult coeliac disease. Observation of enamel defects is an opportunity to diagnose coeliac disease. Copyright © 2013 European Federation of Internal Medicine. Published by Elsevier B.V. All rights reserved.

  16. Function and repair of dental enamel - Potential role of epithelial transport processes of ameloblasts.

    Science.gov (United States)

    Varga, Gábor; Kerémi, Beáta; Bori, Erzsébet; Földes, Anna

    2015-07-01

    The hardest mammalian tissue, dental enamel is produced by ameloblasts, which are electrolyte-transporting epithelial cells. Although the end product is very different, they show many similarities to transporting epithelia of the pancreas, salivary glands and kidney. Enamel is produced in a multi-step epithelial secretory process that features biomineralization which is an interplay of secreted ameloblast specific proteins and the time-specific transport of minerals, protons and bicarbonate. First, "secretory" ameloblasts form the entire thickness of the enamel layer, but with low mineral content. Then they differentiate into "maturation" ameloblasts, which remove organic matrix from the enamel and in turn further build up hydroxyapatite crystals. The protons generated by hydroxyapatite formation need to be buffered, otherwise enamel will not attain full mineralization. Buffering requires a tight pH regulation and secretion of bicarbonate by ameloblasts. The whole process has been the focus of many immunohistochemical and gene knock-out studies, but, perhaps surprisingly, no functional data existed for mineral ion transport by ameloblasts. However, recent studies including ours provided a better insight for molecular mechanism of mineral formation. The secretory regulation is not completely known as yet, but its significance is crucial. Impairing regulation retards or prevents completion of enamel mineralization and results in the development of hypomineralized enamel that easily erodes after dental eruption. Factors that impair this function are fluoride and disruption of pH regulators. Revealing these factors may eventually lead to the treatment of enamel hypomineralization related to genetic or environmentally induced malformation. Copyright © 2015 IAP and EPC. Published by Elsevier B.V. All rights reserved.

  17. Dental stigmata and enamel thickness in a probable case of congenital syphilis from XVI century Croatia.

    Science.gov (United States)

    Lauc, Tomislav; Fornai, Cinzia; Premužić, Zrinka; Vodanović, Marin; Weber, Gerhard W; Mašić, Boris; Rajić Šikanjić, Petra

    2015-10-01

    To analyse the dental remains of an individual with signs of congenital syphilis by using macroscopic observation, CBCT and micro-CT images, and the analysis of the enamel thickness. Anthropological analysis of human skeletal remains from the 16th century archaeological site Park Grič in Zagreb, Croatia discovered a female, 17-20 years old at the time of death, with dental signs supportive of congenital syphilis: mulberry molars and canine defects, as well as non-specific hypoplastic changes on incisors. The focus of the analysis was on three aspects: gross morphology, hypoplastic defects of the molars, canines and incisors, as well as enamel thickness of the upper first and second molars. The observed morphology of the first molars corresponds to the typical aspect of mulberry molars, while that of the canines is characterised by hypomineralisation. Hypoplastic grooves were observed on the incisal edges of all incisors. The enamel of the first molars is underdeveloped while in the second molars a thick-enamelled condition is observed. Our observations for the dental and skeletal evidence are supportive to a diagnosis of congenital syphilis for this specimen from XVI century Croatia. The use of CT imaging helped documenting the diagnostic features and quantifying the effect of the dental stigmata on first molars. Copyright © 2015 Elsevier Ltd. All rights reserved.

  18. Application of the ultrashort pulses in bovine dental enamel; Aplicacao de pulsos ultracurtos em esmalte dental bovino

    Energy Technology Data Exchange (ETDEWEB)

    Todescan, Carla de Rago

    2003-07-01

    The interaction of lasers with the hard structures of the teeth, has found the excess of heat as a problem for its utilization. This study analyzes, in vitro, the interaction of the ultrashort pulse laser of Ti:safire (830 nm) with the bovine dental enamel. The system consisted in one main oscillator integrated with an amplifier (CPA). The pulses extracted before the temporal compression inside the amplifier had 30 ps, 1000 Hz and {approx}1 mJ. The pulses extracted after the compression had 60 fs, 1000 Hz and {approx}0,7 mJ. The M{sup 2} was 1,3, the focal lens 2,5 cm, the focal distance 29,7 and a computerized translation stage x,y,z. We evaluated the amount of tissue removed per pulse,the resulting cavities and the surrounding tissues not irradiated, under OM and SEM. The fluency was the major factor for differentiating the two regimens studied, therefore, the intensity was not so important as we expected in this process. We found: one ablation region in 'cat tongue', one ablation length, one fluency {approx}0,7 J/cm{sup 2} for 30 ps and {approx}0,5 J/cm{sup 2} for 60 fs (50% of high speed burr), smooth edge for 30 ps and high precision of the sharp edge cut of submicrometric order for 60 fs. (author)

  19. Application of the ultrashort pulses in bovine dental enamel; Aplicacao de pulsos ultracurtos em esmalte dental bovino

    Energy Technology Data Exchange (ETDEWEB)

    Todescan, Carla de Rago

    2003-07-01

    The interaction of lasers with the hard structures of the teeth, has found the excess of heat as a problem for its utilization. This study analyzes, in vitro, the interaction of the ultrashort pulse laser of Ti:safire (830 nm) with the bovine dental enamel. The system consisted in one main oscillator integrated with an amplifier (CPA). The pulses extracted before the temporal compression inside the amplifier had 30 ps, 1000 Hz and {approx}1 mJ. The pulses extracted after the compression had 60 fs, 1000 Hz and {approx}0,7 mJ. The M{sup 2} was 1,3, the focal lens 2,5 cm, the focal distance 29,7 and a computerized translation stage x,y,z. We evaluated the amount of tissue removed per pulse,the resulting cavities and the surrounding tissues not irradiated, under OM and SEM. The fluency was the major factor for differentiating the two regimens studied, therefore, the intensity was not so important as we expected in this process. We found: one ablation region in 'cat tongue', one ablation length, one fluency {approx}0,7 J/cm{sup 2} for 30 ps and {approx}0,5 J/cm{sup 2} for 60 fs (50% of high speed burr), smooth edge for 30 ps and high precision of the sharp edge cut of submicrometric order for 60 fs. (author)

  20. Effect of Enamel and Dentin Irradiation by Gamma Rays on the Bond Strength of Two Adhesive Restorations

    International Nuclear Information System (INIS)

    Zein, N.S.A.

    2014-01-01

    There have been many reports related to the high incidence of the head and neck cancers including those of the oral cavity. Ablative surgery, radiotherapy, chemotherapy and reconstructive surgery are components of the curative or palliative treatment of head and neck cancers which are intended to improve survival time and quality of life. In addition to the desirable anticancer effects, ionizing radiation causes damage to normal tissues located within the irradiation fields (1). The early responses of teeth to irradiation include dental hypersensitivity and spontaneous pain (2). Several types of desensitizers may be applied to the tooth after cavity preparation in an attempt to manage dental hypersensitivity. The most common form of management is the placement of a topically applied agent either by a dental professional or by the patient at home. These agents stimulate mineral deposition or occlude dental tubules to reduce hypersensitivity (3,4). Radiation caries is another irradiation-related damage to dental structures. It remains the most threatening complication of radiotherapy for the dentition. It is a highly destructive form of dental caries with a rapid onset and progression. Radiation caries may become evident as early as three months following the initiation of head and neck radiotherapy. In severe cases, a previously healthy dentition can be completely lost within a year (5). Radiation caries involves both enamel and dentin; it tends to first affect the cervical and incisal edges of the teeth. Beside the irradiation-induced xerostomia, the effect of irradiation on dental hard tissues may be an important factor in radiation caries. Studies have reported the physical and chemical changes in enamel after radiotherapy, which are a direct consequence of the irradiation treatment. For dentin, a significant reduction in microhardness is observed after irradiation accompanied by reduced stability of the dentino-enamel junction (DEJ) The oral environment of head

  1. Effect of different dental ceramic systems on the wear of human enamel: An in vitro study.

    Science.gov (United States)

    Zandparsa, Roya; El Huni, Rabie M; Hirayama, Hiroshi; Johnson, Marc I

    2016-02-01

    The wear of tooth structure opposing different advanced dental ceramic systems requires investigation. The purpose of this in vitro study was to compare the wear of advanced ceramic systems against human enamel antagonists. Four ceramic systems (IPS e.max Press, IPS e.max CAD, Noritake Super Porcelain EX-3, and LAVA Plus Zirconia) and 1 control group containing human enamel specimens were used in this study (n = 12). All specimens were fabricated as disks 11 mm in diameter and 3 mm thick. The mesiopalatal cusps of the maxillary third molars were prepared to serve as the enamel styluses. All specimens were embedded individually in 25 mm(3) autopolymerizing acrylic resin blocks. Wear was measured with a cyclic loading machine and a newly designed wear simulator. All enamel styluses (cusps) were scanned using the Activity 880 digital scanner (SmartOptics). Data from the base line and follow-up scans were collected and compared with Qualify 2012 3-dimensional (3D) and 2D digital inspection software (Geomagic), which aligned the models and detected the geometric changes and the wear caused by the antagonist specimen. One-way ANOVA was used to analyze the collected data. After 125,000 bidirectional loading cycles, the mean loss of opposing enamel volume for the enamel disks in the control group was 37.08 μm(3), the lowest mean value for IPS e.max Press system was 39.75 μm(3); 40.58 μm(3) for IPS e.max CAD; 45.08 μm(3) for Noritake Super Porcelain EX-3 system; and 48.66 μm(3) for the Lava Plus Zirconia system. No statically significant differences were found among the groups in opposing enamel volume loss (P=.225) or opposing enamel height loss (P=.149). In terms of opposing enamel height loss, Lava Plus Zirconia system showed the lowest mean value of 27.5 μm. The mean value for the IPS e.max CAD system was 27.91 μm; 29.08 μm for the control enamel; 33.25 μm for the IPS e.max Press system; and 34.75 μm for the Noritake Super Porcelain EX-3 system. Within the

  2. Matrix metalloproteinase-20 mediates dental enamel biomineralization by preventing protein occlusion inside apatite crystals.

    Science.gov (United States)

    Prajapati, Saumya; Tao, Jinhui; Ruan, Qichao; De Yoreo, James J; Moradian-Oldak, Janet

    2016-01-01

    Reconstruction of enamel-like materials is a central topic of research in dentistry and material sciences. The importance of precise proteolytic mechanisms in amelogenesis to form a hard tissue with more than 95% mineral content has already been reported. A mutation in the Matrix Metalloproteinase-20 (MMP-20) gene results in hypomineralized enamel that is thin, disorganized and breaks from the underlying dentin. We hypothesized that the absence of MMP-20 during amelogenesis results in the occlusion of amelogenin in the enamel hydroxyapatite crystals. We used spectroscopy and electron microscopy techniques to qualitatively and quantitatively analyze occluded proteins within the isolated enamel crystals from MMP-20 null and Wild type (WT) mice. Our results showed that the isolated enamel crystals of MMP-20 null mice had more organic macromolecules occluded inside them than enamel crystals from the WT. The crystal lattice arrangements of MMP-20 null enamel crystals analyzed by High Resolution Transmission Electron Microscopy (HRTEM) were found to be significantly different from those of the WT. Raman studies indicated that the crystallinity of the MMP-20 null enamel crystals was lower than that of the WT. In conclusion, we present a novel functional mechanism of MMP-20, specifically prevention of unwanted organic material entrapped in the forming enamel crystals, which occurs as the result of precise amelogenin cleavage. MMP-20 action guides the growth morphology of the forming hydroxyapatite crystals and enhances their crystallinity. Elucidating such molecular mechanisms can be applied in the design of novel biomaterials for future clinical applications in dental restoration or repair. Copyright © 2015 Elsevier Ltd. All rights reserved.

  3. Measurement of the efficacy of calcium silicate for the protection and repair of dental enamel.

    Science.gov (United States)

    Parker, Alexander S; Patel, Anisha N; Al Botros, Rehab; Snowden, Michael E; McKelvey, Kim; Unwin, Patrick R; Ashcroft, Alexander T; Carvell, Mel; Joiner, Andrew; Peruffo, Massimo

    2014-06-01

    To investigate the formation of hydroxyapatite (HAP) from calcium silicate and the deposition of calcium silicate onto sound and acid eroded enamel surfaces in order to investigate its repair and protective properties. Calcium silicate was mixed with phosphate buffer for seven days and the resulting solids analysed for crystalline phases by Raman spectroscopy. Deposition studies were conducted on bovine enamel surfaces. Acid etched regions were produced on the enamel surfaces using scanning electrochemical cell microscopy (SECCM) with acid filled pipettes and varying contact times. Following treatment with calcium silicate, the deposition was visualised with FE-SEM and etch pit volumes were measured by AFM. A second set of bovine enamel specimens were pre-treated with calcium silicate and fluoride, before acid exposure with the SECCM. The volumes of the resultant acid etched pits were measured using AFM and the intrinsic rate constant for calcium loss was calculated. Raman spectroscopy confirmed that HAP was formed from calcium silicate. Deposition studies demonstrated greater delivery of calcium silicate to acid eroded than sound enamel and that the volume of acid etched enamel pits was significantly reduced following one treatment (penamel was 0.092 ± 0.008 cm/s. This was significantly reduced, 0.056 ± 0.005 cm/s, for the calcium silicate treatments (penamel surfaces. Calcium silicate can provide significant protection of sound enamel from acid challenges. Calcium silicate is a material that has potential for a new approach to the repair of demineralised enamel and the protection of enamel from acid attacks, leading to significant dental hard tissue benefits. © 2014 Elsevier Ltd. All rights reserved.

  4. Year of birth determination using radiocarbon dating of dental enamel.

    Science.gov (United States)

    Buchholz, B A; Spalding, K L

    2010-05-01

    Radiocarbon dating is typically an archaeological tool rather than a forensic one. Recently however, we have shown that the amount of radiocarbon present in tooth enamel, as a result of nuclear bomb testing during the cold war, is a remarkably accurate indicator of when a person is born. Enamel isolated from human teeth is processed to form graphite and carbon-14 ((14)C) levels are measured using accelerator mass spectrometry. Since there is no turnover of enamel after it is formed, (14)C levels in the enamel represent (14)C levels in the atmosphere at the time of its formation. In this paper we describe the strategy used to determine the date of birth of an individual based on radiocarbon levels in tooth enamel, focusing on the methodology of this strategy. Year of birth information can significantly assist police investigators when the identity of a deceased individual is unknown. In such cases police will try to match particulars of the unidentified individual (which is often only gender and/or an estimate of age), with particulars from missing persons lists.

  5. Year of Birth Determination Using Radiocarbon Dating of Dental Enamel

    Energy Technology Data Exchange (ETDEWEB)

    Buchholz, B A; Spalding, K L

    2009-03-10

    Radiocarbon dating is typically an archaeological tool rather than a forensic one. Recently however, we have shown that the amount of radiocarbon present in tooth enamel, as a result of nuclear bomb testing during the cold war, is a remarkably accurate indicator of when a person is born. Enamel isolated from human teeth is processed to form graphite and carbon-14 ({sup 14}C) levels are measured using accelerator mass spectrometry. Since there is no turnover of enamel after it is formed, {sup 14}C levels in the enamel represent {sup 14}C levels in the atmosphere at the time of its formation. In this paper we describe the strategy used to determine the date of birth of an individual based on radiocarbon levels in tooth enamel, focusing on the methodology of this strategy. Year of birth information can significantly assist police investigators when the identity of a deceased individual is unknown. In such cases police will try to match particulars of the unidentified individual (which is often only gender and/or an estimate of age), with particulars from missing persons lists.

  6. 'In vitro' assessment to instrumented indentation hardness tests in enamel of bovine teeth, before and after dental bleaching by laser; Avaliacao in vitro' de ensaios instrumentados de dureza em esmalte de dente bovino, antes e apos clareamento dental a laser

    Energy Technology Data Exchange (ETDEWEB)

    Britto Junior, Francisco Meira

    2004-07-01

    The laser enamel bleaching is a common used procedure due to its satisfactory esthetic results. The possible changes on the dental structures caused by the bleaching technique are of great importance. The enamel superficial microhardness changes through instrumented indentation hardness on bovine teeth were analyzed in this present study. The samples were divided in two halves, one being the control and the other irradiated with a diode laser (808 nm) or with a Nd:YAG laser (1064 nm) to activate the Whiteness HP bleaching gel (hydrogen peroxide at 35%). It was possible to conclude that there was a statistical significant increase on the enamel superficial microhardness (Group I, sample 1 and Group II, sample 1) despite this increase did not seem to indicate a concern regarding the enamel surface resistance change. There was not a significant statistical change on the enamel microhardness on the other samples. The final conclusion is that there was no superficial enamel morphological change after these treatments. (author)

  7. Comparative study of dental enamel loss after debonding braces by analytical scanning electron microscopy (SEM).

    Science.gov (United States)

    Rodríguez-Chávez, Jacqueline Adelina; Arenas-Alatorre, Jesús; Belio-Reyes, Irma Araceli

    2017-07-01

    Clinical procedures when shear forces are applied to brackets suggest adhesion forces between 2.8 and 10.0 MPa as appropriate. In this study dental enamel was evaluated by scanning electron microscopy (SEM) before and after removing the brackets. Thirty bicuspids (previous prophylaxis) with metallic brackets (Roth Inovation 0.022 GAC), Transbond Plus SEP 3M Unitek adhesive and Transbond XT 3M resin were used. The samples were preserved to 37°C during 24 hr and submited to tangential forces with the Instron Universal machine 1.0 mm/min speed load strength resistance debonding. Also the Adhesive Remanent Index (ARI) test was made, evaluating the bracket base and the bicuspid surface. All the bracket SEM images were processed with AutoCAD to determine the enamel detached area. The average value was 6.86 MPa (SD ± 3.2 MPa). ARI value 1= 63.3%, value 2= 20%, value 3= 13.3% and 33% presented value 0. All those samples with dental enamel loss, presented different situations as fractures, ledges, horizontal, and vertical loss in some cases, and some scratch lines. There is no association between the debonding resistance and enamel presence. Less than half of the remanent adhesive on the dental enamel was present in most of the samples when the ARI test was applied. When the resin area increases, the debonding resistance also increases, and when the enamel loss increases, the resin free metallic area of the bracket base decreases in the debonding. © 2017 Wiley Periodicals, Inc.

  8. Susceptibility of bovine dental enamel with initial erosion lesion to new erosive challenges.

    Science.gov (United States)

    Oliveira, Gabriela Cristina de; Tereza, Guida Paola Genovez; Boteon, Ana Paula; Ferrairo, Brunna Mota; Gonçalves, Priscilla Santana Pinto; Silva, Thiago Cruvinel da; Honório, Heitor Marques; Rios, Daniela

    2017-01-01

    This in vitro study evaluated the impact of initial erosion on the susceptibility of enamel to further erosive challenge. Thirty bovine enamel blocks were selected by surface hardness and randomized into two groups (n = 15): GC- group composed by enamel blocks without erosion lesion and GT- group composed by enamel blocks with initial erosion lesion. The baseline profile of each block was determined using the profilometer. The initial erosion was produced by immersing the blocks into HCl 0.01 M, pH 2.3 for 30 seconds, under stirring. The erosive cycling consisted of blocks immersion in hydrochloric acid (0.01 M, pH 2.3) for 2 minutes, followed by immersion in artificial saliva for 120 minutes. This procedure was repeated 4 times a day for 5 days, and the blocks were kept in artificial saliva overnight. After erosive cycling, final profile measurement was performed. Profilometry measured the enamel loss by the superposition of initial and final profiles. Data were analyzed by t-test (perosion on bovine dental enamel does not enhance its susceptibility to new erosive challenges.

  9. Susceptibility of bovine dental enamel with initial erosion lesion to new erosive challenges.

    Directory of Open Access Journals (Sweden)

    Gabriela Cristina de Oliveira

    Full Text Available This in vitro study evaluated the impact of initial erosion on the susceptibility of enamel to further erosive challenge. Thirty bovine enamel blocks were selected by surface hardness and randomized into two groups (n = 15: GC- group composed by enamel blocks without erosion lesion and GT- group composed by enamel blocks with initial erosion lesion. The baseline profile of each block was determined using the profilometer. The initial erosion was produced by immersing the blocks into HCl 0.01 M, pH 2.3 for 30 seconds, under stirring. The erosive cycling consisted of blocks immersion in hydrochloric acid (0.01 M, pH 2.3 for 2 minutes, followed by immersion in artificial saliva for 120 minutes. This procedure was repeated 4 times a day for 5 days, and the blocks were kept in artificial saliva overnight. After erosive cycling, final profile measurement was performed. Profilometry measured the enamel loss by the superposition of initial and final profiles. Data were analyzed by t-test (p<0.05. The result showed no statistically significant difference between groups (GS = 14.60±2.86 and GE = .14.69±2.21 μm. The presence of initial erosion on bovine dental enamel does not enhance its susceptibility to new erosive challenges.

  10. HeNe-laser light scattering by human dental enamel

    NARCIS (Netherlands)

    Zijp, [No Value; tenBosch, JJ; Groenhuis, RAJ

    1995-01-01

    Knowledge of the optical properties of tooth enamel and an understanding of the origin of these properties are necessary for the development of new optical methods for caries diagnosis and the measurement of tooth color. We measured the scattering intensity functions for HeNe-laser light of 80- to

  11. Quantitative study of fluoride transport during subsurface dissolution of dental enamel

    International Nuclear Information System (INIS)

    Chu, J.S.; Fox, J.L.; Higuchi, W.I.

    1989-01-01

    Previous studies using bovine dental enamel as a model have shown that surface and subsurface dissolution of enamel may be governed by micro-environmental solution conditions. We have now investigated the demineralization phenomenon more rigorously with the primary objective of developing a method for deducing solution species concentration profiles as a function of time from appropriate experimental data. More specifically, in this report, a model-independent method is described for determination of the pore solution fluoride gradients in bovine enamel during subsurface demineralization. Microradiography was used to determine the mineral density profiles, and an electron microprobe technique to determine total fluoride (F) profiles associated with the enamel. In each case, matched sections of bovine enamel were exposed to partially saturated acetate buffers at pH = 4.5 containing 0.5 ppm F for various periods of time (from six to 24 hours). The treated enamel was found to have an intact surface layer and subsurface demineralization. The extent of the demineralization and the depths of the lesions increased with time in all cases. The data were first used to calculate (a) the total F gradients in the enamel at various times, and (b) the local uptake rate of F as a function of time and position. Then, by manipulation of the equations describing the uptake and transport of F, we calculated the pore diffusion rate of F and the micro-environmental solution F concentration in the aqueous pores as a function of time and of distance from the enamel surface. It was also possible to calculate an intrinsic F diffusion coefficient in the pores, which was about 1.0 X 10(-5) cm2/sec, in good agreement with reported values

  12. Evaluation of crystalline changes and resistance to demineralization of the surface of human dental enamel treated with Er:YAG laser and fluoride using x-ray diffraction analysis and Vickers microhardness

    Science.gov (United States)

    Behroozibakhsh, Marjan; Shahabi, Sima; Ghavami-Lahiji, Mehrsima; Sadeghian, Safura; Sadat Faal Nazari, Neda

    2018-06-01

    This study aimed to investigate the changes in crystalline structure and resistance to demineralization of human dental surface enamel treated with erbium-doped yttrium aluminium garnet laser (Er:YAG) laser and fluoride. The enamel surfaces were divided into four groups according to the treatment process including, (L): irradiated with Er:YAG; (F): treated with acidulated phosphate fluoride gel (LF): Pre-irradiated surfaces with Er:YAG subjected to acidulated phosphate fluoride gel and (FL): laser irradiation was performed on the fluoridated enamel surface. Before and after the treatment procedure, the samples were evaluated using X-ray diffraction, scanning electron microscope (SEM) and the Vickers microhardness test. The surface microhardness values also were measured after a pH-cycling regime and acid challenge. The a-axis of all lased groups was contracted after treatment procedure. Measurement of the area under the peaks showed the highest crysallinity in the FL group. The hardness values of all laser treated samples significantly reduced after treatment procedure compared to the F group (p  ⩽  0.001). The morphological observations showed remarkable changes on the lased enamel surfaces including cracks, craters and exposed prisms. These findings suggest, irradiation of the Er:YAG laser accompanying with fluoride application can induce some beneficial crystalline changes regarding the acid-resistance properties of enamel, however, the craters and cracks produced by laser irradiation can promote enamel demineralization and consequently the positive effects of the Er:YAG laser will be eliminated.

  13. Evaluation of primary tooth enamel surface morphology and microhardness after Nd:YAG laser irradiation and APF gel treatment--an in vitro study.

    Science.gov (United States)

    Banda, Naveen Reddy; Vanaja Reddy, G; Shashikiran, N D

    2011-01-01

    Laser irradiation and fluoride has been used as a preventive tool to combat dental caries in permanent teeth, but little has been done for primary teeth which are more prone to caries. The purpose of this study was to evaluate microhardness alterations in the primary tooth enamel after Nd-YAG laser irradiation alone and combined with topical fluoride treatment either before or after Nd-YAG laser irradiation. Ten primary molars were sectioned and assigned randomly to: control group, Nd-YAG laser irradiation, Nd-YAG lasing before APF and APF followed by Nd-YAG lasing. The groups were evaluated for microhardness. Surface morphological changes were observed using SEM. Statistical comparisons were performed. The control group's SEM showed a relatively smooth enamel surface and lasing group had fine cracks and porosities. In the lasing + fluoride group a homogenous confluent surface was seen. In the fluoride + lasing group an irregular contour with marked crack propagation was noted. There was a significant increase in the microhardness of the treatment groups. Nd-YAG laser irradiation and combined APF treatment of the primary tooth enamel gave morphologically hardened enamel surface which can be a protective barrier against a cariogenic attack.

  14. Effect of pretreatment with an Er:YAG laser and fluoride on the prevention of dental enamel erosion.

    Science.gov (United States)

    dos Reis Derceli, Juliana; Faraoni-Romano, Juliana Jendiroba; Azevedo, Danielle Torres; Wang, Linda; Bataglion, César; Palma-Dibb, Regina Guenka

    2015-02-01

    The aim of this study was to evaluate the effect of the Er:YAG laser and its association with fluoride (1.23% acidulate phosphate fluoride gel) on the prevention of enamel erosion. Sixty specimens were obtained from bovine enamel (4 × 4 mm), which were ground flat, polished, and randomly divided into five groups according to the preventive treatments: control-fluoride application; L--Er:YAG laser; L+F--laser + fluoride; F+L--fluoride + laser; L/F--laser/fluoride simultaneously. Half of the enamel surface was covered with nail varnish (control area), and the other half was pretreated with one of the preventive strategies to subsequently be submitted to erosive challenge. When the laser was applied, it was irradiated for 10 s with a focal length of 4 mm and 60 mJ/2 Hz. Fluoride gel was applied for 4 min. Each specimen was individually exposed to regular Coca-Cola® for 1 min, four times/day, for 5 days. Wear analysis was performed with a profilometer, and demineralization was assessed with an optical microscope. Data were analyzed using the Kruskal-Wallis test (wear)/Dunn test and ANOVA/Fisher's exact tests. The group L/F was similar to control group. The other groups showed higher wear, which did not present differences among them. In the demineralization assessment, the groups F+L and L/F showed lower demineralization in relation to the other groups. It can be concluded that none preventive method was able to inhibit dental wear. The treatments L/F and F+L showed lower enamel demineralization.

  15. Determination of thermal diffusivity of dental enamel and dentin as a function of temperature, using infrared thermography

    International Nuclear Information System (INIS)

    Pereira, Thiago Martini

    2009-01-01

    In this work it was developed a software that calculates automatically, the thermal diffusivity value as a function of temperature in materials. The infrared thermography technique was used for data acquisition of temperature distribution as a function of time. These data were used to adjust a temperature function obtained from the homogeneous heat equation with specific boundary conditions. For that, an infrared camera (detecting from 8 μm to 9 μm) was calibrated to detect temperature ranging from 185 degree C up to 1300 degree C at an acquisition rate of 300 Hz. It was used, 10 samples of dental enamel and 10 samples of dentin, with 4 mm x 4 mm x 2 mm, which were obtained from bovine lower incisor teeth. These samples were irradiated with an Er:Cr:YSGG pulsed laser (λ = 2,78 μm). The resulting temperature was recorded 2 s prior, 10 s during irradiation and continuing for 2 more seconds after it. After each irradiation, all obtained thermal images were processed in the software, creating a file with the data of thermal diffusivity as a function of temperature. Another file with the thermal diffusivity values was also calculated after each laser pulse. The mean result of thermal diffusivity obtained for dental enamel was 0,0084 ± 0,001 cm2/s for the temperature interval of 220-550 degree C. The mean value for thermal diffusivity obtained for dentin was 0,0015 0,0004 cm2/s in temperatures up to 360 degree C; however, this value increases for higher temperatures. According to these results, it was possible to conclude that the use of infrared thermography, associated with the software developed in this work, is an efficient method to determine the thermal diffusivity values as a function of temperature in different materials. (author)

  16. Influence of tooth bleaching on dental enamel microhardness: a systematic review and meta-analysis.

    Science.gov (United States)

    Zanolla, J; Marques, Abc; da Costa, D C; de Souza, A S; Coutinho, M

    2017-09-01

    Several studies have investigated the effect of bleaching on dental tissues. The evaluation of the effect of home bleaching with 10% carbamide peroxide is important for assessing alterations in enamel microhardness that may affect dental health in terms of resistance to masticatory forces. This meta-analysis was performed in order to determine scientific evidence regarding the effects of home vital bleaching with 10% carbamide peroxide gel on the microhardness of human dental enamel. A systematic electronic literature search was conducted in the PubMed and Web of Science databases using search terms. Two independent researchers evaluated the information and methodological quality of the studies. Inclusion and exclusion criteria were established for article selection; further, only studies published in English were selected. Thirteen studies that met all of the inclusion and exclusion criteria were selected and underwent statistical analysis. The results of this meta-analysis showed no significant changes in enamel microhardness when using the 10% carbamide peroxide bleaching gel over periods of 7, 14 and 21 days. © 2016 Australian Dental Association.

  17. Prenatal effects by exposing to amoxicillin on dental enamel in Wistar rats.

    Science.gov (United States)

    Gottberg, Beatriz; Berné, Jeanily; Quiñónez, Belkis; Solórzano, Eduvigis

    2014-01-01

    Amoxicillin is an antibiotic widely prescribed; its most frequent side effects are gastrointestinal disorders and hypersensitivity reactions. Over the last 10 years studies have been published which suggest that amoxicillin may cause dental alterations similar to dental fluorosis. Never the less, the results are not conclusive, this is why it was planned the need to make controlled studies on test animals. The purpose of this study was to determine the effect produced by amoxicillin prenatal administration on dental enamel in Wistar rats. 12 pregnant adult rats were used distributed into five different groups: witness control (n=2) didn't get any treatment; negative control (n=2) they were prescribed with saline solution; positive control (n=3) they were prescribed with tetracycline 130 mg/kg, and two groups (n=3 and n=2) treated with amoxicillin doses of 50 and 100 mg/kg respectively. The treatments were daily administered by mouth, from the 6th gestation day to the end of gestation. Twenty five days after they were born, the offspring were sacrificed with a sodium pentobarbital overdose, the mandible was dissected and the first lower molars were gotten. The samples were fixed in 10% formaldehyde solution and clinically and histologically observed to determine any enamel disorders. hypomineralization was observed in every single sample of the tetracyclic and amoxicillin treated group 100 mg/kg, meanwhile only 50% from the group administered with 50 mg/kg amoxicillin showed this histological disorder. the side effect caused by amoxicillin on dental enamel was doses dependent.

  18. Effect of moisture on dental enamel in the interaction of two orthodontic bonding systems.

    Science.gov (United States)

    Bertoz, André Pinheiro de Magalhães; de Oliveira, Derly Tescaro Narcizo; Gimenez, Carla Maria Melleiro; Briso, André Luiz Fraga; Bertoz, Francisco Antonio; Santos, Eduardo César Almada

    2013-01-01

    The purpose of this study was to assess by means of scanning electron microscopy (SEM) the remaining adhesive interface after debonding orthodontic attachments bonded to bovine teeth with the use of hydrophilic and hydrophobic primers under different dental substrate moisture conditions. Twenty mandibular incisors were divided into four groups (n = 5). In Group I, bracket bonding was performed with Transbond MIP hydrophilic primer and Transbond XT adhesive paste applied to moist substrate, and in Group II a bonding system comprising Transbond XT hydrophobic primer and adhesive paste was applied to moist substrate. Brackets were bonded to the specimens in Groups III and IV using the same adhesive systems, but on dry dental enamel. The images were qualitatively assessed by SEM. The absence of moisture in etched enamel enabled better interaction between bonding materials and the adamantine structure. The hydrophobic primer achieved the worst micromechanical interlocking results when applied to a moist dental structure, whereas the hydrophilic system proved versatile, yielding acceptable results in moist conditions and excellent interaction in the absence of contamination. The authors assert that the best condition for the application of primers to dental enamel occurs in the absence of moisture.

  19. Trace elementary concentration in enamel after dental bleaching using HI-ERDA

    Energy Technology Data Exchange (ETDEWEB)

    Added, N [GFAA, Depto de Fisica Nuclear, IFUSP, University of Sao Paulo, Travessa R da rua do Matao 187, Cidade Universitaria, Caixa Postal 66318, CEP 05508-970 Sao Paulo, SP (Brazil); Rizzutto, M A [GFAA, Depto de Fisica Nuclear, IFUSP, University of Sao Paulo, Travessa R da rua do Matao 187, Cidade Universitaria, Caixa Postal 66318, CEP 05508-970 Sao Paulo, SP (Brazil); Curado, J F [GFAA, Depto de Fisica Nuclear, IFUSP, University of Sao Paulo, Travessa R da rua do Matao 187, Cidade Universitaria, Caixa Postal 66318, CEP 05508-970 Sao Paulo, SP (Brazil); Francci, C [School of Dentistry, University of Sao Paulo (Brazil); Markarian, R [School of Dentistry, University of Sao Paulo (Brazil); Mori, M [School of Dentistry, University of Sao Paulo (Brazil)

    2006-08-15

    Changes of elementary concentrations in dental enamel after a bleaching treatment with different products, is presented, with special focus on the oxygen contribution. Concentrations for Ca, P, O and C and some other trace elements were obtained for enamel of bovine incisor teeth by HI-ERDA measurements using a {sup 35}Cl incident beam and an ionization chamber. Five groups of teeth with five samples each were treated with a different bleaching agents. Each tooth had its crown sectioned in two halves, one for bleaching test and one the other used as a control. Average values of C/Ca, O/Ca, F/Ca enrichment factors were found. The comparison between bleached and non-bleached halves indicates that bleaching treatment did not affect the mineral structure when low-concentration whitening systems were used. The almost constant oxygen concentration in enamel, suggests little changes due to whitening therapy.

  20. Trace elementary concentration in enamel after dental bleaching using HI-ERDA

    International Nuclear Information System (INIS)

    Added, N.; Rizzutto, M.A.; Curado, J.F.; Francci, C.; Markarian, R.; Mori, M.

    2006-01-01

    Changes of elementary concentrations in dental enamel after a bleaching treatment with different products, is presented, with special focus on the oxygen contribution. Concentrations for Ca, P, O and C and some other trace elements were obtained for enamel of bovine incisor teeth by HI-ERDA measurements using a 35 Cl incident beam and an ionization chamber. Five groups of teeth with five samples each were treated with a different bleaching agents. Each tooth had its crown sectioned in two halves, one for bleaching test and one the other used as a control. Average values of C/Ca, O/Ca, F/Ca enrichment factors were found. The comparison between bleached and non-bleached halves indicates that bleaching treatment did not affect the mineral structure when low-concentration whitening systems were used. The almost constant oxygen concentration in enamel, suggests little changes due to whitening therapy

  1. Trace elementary concentration in enamel after dental bleaching using HI-ERDA

    Science.gov (United States)

    Added, N.; Rizzutto, M. A.; Curado, J. F.; Francci, C.; Markarian, R.; Mori, M.

    2006-08-01

    Changes of elementary concentrations in dental enamel after a bleaching treatment with different products, is presented, with special focus on the oxygen contribution. Concentrations for Ca, P, O and C and some other trace elements were obtained for enamel of bovine incisor teeth by HI-ERDA measurements using a 35Cl incident beam and an ionization chamber. Five groups of teeth with five samples each were treated with a different bleaching agents. Each tooth had its crown sectioned in two halves, one for bleaching test and one the other used as a control. Average values of C/Ca, O/Ca, F/Ca enrichment factors were found. The comparison between bleached and non-bleached halves indicates that bleaching treatment did not affect the mineral structure when low-concentration whitening systems were used. The almost constant oxygen concentration in enamel, suggests little changes due to whitening therapy.

  2. Enamel apatite crystallinity significantly contributes to mammalian dental adaptations

    Czech Academy of Sciences Publication Activity Database

    Kallistová, Anna; Skála, Roman; Šlouf, Miroslav; Čejchan, Petr; Matulková, I.; Horáček, I.

    2018-01-01

    Roč. 8, APR 3 2018 (2018), č. článku 5544. ISSN 2045-2322 R&D Projects: GA MŠk(CZ) LO1507 Institutional support: RVO:67985831 ; RVO:61389013 Keywords : tooth enamel * mechanical -properties * electron-microscopy * diffraction * teeth * size * morphology * behavior * minipig * pattern Subject RIV: EA - Cell Biology; CD - Macromolecular Chemistry (UMCH-V) OBOR OECD: Other biological topics; Polymer science (UMCH-V) Impact factor: 4.259, year: 2016

  3. AFM analysis of bleaching effects on dental enamel microtopography

    International Nuclear Information System (INIS)

    Pedreira de Freitas, Ana Carolina; Cardoso Espejo, Luciana; Brossi Botta, Sergio; Sa Teixeira, Fernanda de; Cerqueira, Luz Maria Aparecida A.; Garone-Netto, Narciso; Bona Matos, Adriana; Barbosa da Silveira Salvadori, Maria Cecilia

    2010-01-01

    The purpose of this in vitro study was to test a new methodology to evaluate the effects of 35% hydrogen peroxide agent on the microtopography of sound enamel using an atomic force microscope (AFM). The buccal sound surfaces of three extracted human lower incisors were used, without polishing the surfaces to maintain them with natural morphology. These unpolished surfaces were subjected to bleaching procedure with 35% hydrogen peroxide that consisted of 4 applications of the bleaching agent on enamel surfaces for 10 min each application. Surface images were obtained in a 15 μm x 15 μm area using an AFM. The roughness (Ra and RMS) and the power spectral density (PSD) were obtained before and after the bleaching treatment. As results we could inquire that the PSD analyses were very suitable to identifying the morphological changes on the surfaces, while the Ra and RMS parameters were insufficient to represent the morphological alterations promoted by bleaching procedure on enamel. The morphological wavelength in the range of visible light spectrum (380-750 nm) was analyzed, showing a considerable increase of the PSD with the bleaching treatment.

  4. AFM analysis of bleaching effects on dental enamel microtopography

    Energy Technology Data Exchange (ETDEWEB)

    Pedreira de Freitas, Ana Carolina, E-mail: anacarolfreitas@usp.br [Departamento de Dentistica, Faculdade de Odontologia da Universidade de Sao Paulo, Av. Prof. Lineu Prestes, 2227 - Cidade Universitaria, CEP 05508-000, Sao Paulo (Brazil); Cardoso Espejo, Luciana, E-mail: luespejo@hotmail.com [Departamento de Dentistica, Faculdade de Odontologia da Universidade de Sao Paulo, Av. Prof. Lineu Prestes, 2227 - Cidade Universitaria, CEP 05508-000, Sao Paulo (Brazil); Brossi Botta, Sergio, E-mail: sbbotta@usp.br [Departamento de Dentistica, Faculdade de Odontologia da Universidade de Sao Paulo, Av. Prof. Lineu Prestes, 2227 - Cidade Universitaria, CEP 05508-000, Sao Paulo (Brazil); Sa Teixeira, Fernanda de, E-mail: nandast@if.usp.br [Laboratorio de Filmes Finos, Instituto de Fisica da Universidade de Sao Paulo, Rua do Matao, Travessa R, 187 - Cidade Universitaria, CEP 05314-970, Sao Paulo (Brazil); Cerqueira, Luz Maria Aparecida A., E-mail: maacluz@usp.br [Departamento de Dentistica, Faculdade de Odontologia da Universidade de Sao Paulo, Av. Prof. Lineu Prestes, 2227 - Cidade Universitaria, CEP 05508-000, Sao Paulo (Brazil); Garone-Netto, Narciso, E-mail: ngarone@usp.br [Departamento de Dentistica, Faculdade de Odontologia da Universidade de Sao Paulo, Av. Prof. Lineu Prestes, 2227 - Cidade Universitaria, CEP 05508-000, Sao Paulo (Brazil); Bona Matos, Adriana, E-mail: bona@usp.br [Departamento de Dentistica, Faculdade de Odontologia da Universidade de Sao Paulo, Av. Prof. Lineu Prestes, 2227 - Cidade Universitaria, CEP 05508-000, Sao Paulo (Brazil); Barbosa da Silveira Salvadori, Maria Cecilia, E-mail: mcsalva@if.usp.br [Laboratorio de Filmes Finos, Instituto de Fisica da Universidade de Sao Paulo, Rua do Matao, Travessa R, 187 - Cidade Universitaria, CEP 05314-970, Sao Paulo (Brazil)

    2010-02-15

    The purpose of this in vitro study was to test a new methodology to evaluate the effects of 35% hydrogen peroxide agent on the microtopography of sound enamel using an atomic force microscope (AFM). The buccal sound surfaces of three extracted human lower incisors were used, without polishing the surfaces to maintain them with natural morphology. These unpolished surfaces were subjected to bleaching procedure with 35% hydrogen peroxide that consisted of 4 applications of the bleaching agent on enamel surfaces for 10 min each application. Surface images were obtained in a 15 {mu}m x 15 {mu}m area using an AFM. The roughness (Ra and RMS) and the power spectral density (PSD) were obtained before and after the bleaching treatment. As results we could inquire that the PSD analyses were very suitable to identifying the morphological changes on the surfaces, while the Ra and RMS parameters were insufficient to represent the morphological alterations promoted by bleaching procedure on enamel. The morphological wavelength in the range of visible light spectrum (380-750 nm) was analyzed, showing a considerable increase of the PSD with the bleaching treatment.

  5. A New Sugarcane Cystatin Strongly Binds to Dental Enamel and Reduces Erosion.

    Science.gov (United States)

    Santiago, A C; Khan, Z N; Miguel, M C; Gironda, C C; Soares-Costa, A; Pelá, V T; Leite, A L; Edwardson, J M; Buzalaf, M A R; Henrique-Silva, F

    2017-08-01

    Cystatin B was recently identified as an acid-resistant protein in acquired enamel pellicle; it could therefore be included in oral products to protect against caries and erosion. However, human recombinant cystatin is very expensive, and alternatives to its use are necessary. Phytocystatins are reversible inhibitors of cysteine peptidases that are found naturally in plants. In plants, they have several biological and physiological functions, such as the regulation of endogenous processes, defense against pathogens, and response to abiotic stress. Previous studies performed by our research group have reported high inhibitory activity and potential agricultural and medical applications of several sugarcane cystatins, including CaneCPI-1, CaneCPI-2, CaneCPI-3, and CaneCPI-4. In the present study, we report the characterization of a novel sugarcane cystatin, named CaneCPI-5. This cystatin was efficiently expressed in Escherichia coli, and inhibitory assays demonstrated that it was a potent inhibitor of human cathepsins B, K, and L ( K i = 6.87, 0.49, and 0.34 nM, respectively). The ability of CaneCPI-5 to bind to dental enamel was evaluated using atomic force microscopy. Its capacity to protect against initial enamel erosion was also tested in vitro via changes in surface hardness. CaneCPI-5 showed a very large force of interaction with enamel (e.g., compared with mucin and casein) and significantly reduced initial enamel erosion. These results suggest that the inclusion of CaneCPIs in dental products might confer protection against enamel erosion.

  6. Interactions between dodecyl phosphates and hydroxyapatite or tooth enamel: relevance to inhibition of dental erosion.

    Science.gov (United States)

    Jones, Siân B; Barbour, Michele E; Shellis, R Peter; Rees, Gareth D

    2014-05-01

    Tooth surface modification is a potential method of preventing dental erosion, a form of excessive tooth wear facilitated by softening of tooth surfaces through the direct action of acids, mainly of dietary origin. We have previously shown that dodecyl phosphates (DPs) effectively inhibit dissolution of native surfaces of hydroxyapatite (the type mineral for dental enamel) and show good substantivity. However, adsorbed saliva also inhibits dissolution and DPs did not augment this effect, which suggests that DPs and saliva interact at the hydroxyapatite surface. In the present study the adsorption and desorption of potassium and sodium dodecyl phosphates or sodium dodecyl sulphate (SDS) to hydroxyapatite and human tooth enamel powder, both native and pre-treated with saliva, were studied by high performance liquid chromatography-mass Spectrometry. Thermo gravimetric analysis was used to analyse residual saliva and surfactant on the substrates. Both DPs showed a higher affinity than SDS for both hydroxyapatite and enamel, and little DP was desorbed by washing with water. SDS was readily desorbed from hydroxyapatite, suggesting that the phosphate head group is essential for strong binding to this substrate. However, SDS was not desorbed from enamel, so that this substrate has surface properties different from those of hydroxyapatite. The presence of a salivary coating had little or no effect on adsorption of the DPs, but treatment with DPs partly desorbed saliva; this could account for the failure of DPs to increase the dissolution inhibition due to adsorbed saliva. Copyright © 2014 Elsevier B.V. All rights reserved.

  7. Bonding performance of universal adhesives to er,cr:YSGG laser-irradiated enamel.

    Science.gov (United States)

    Ayar, Muhammet Kerim; Erdemir, Fatih

    2017-04-01

    Universal adhesives have been recently introduced for use as self-etch or etch-and-rinse adhesives depending on the dental substrate and clinical condition. However, their bonding effectiveness to laser-irradiated enamel is still not well-known. Thus, the aim of this study was to compare the shear bond strength (SBS) of universal adhesives (Single Bond Universal; Nova Compo-B Plus) applied to Er,Cr:YSGG laser-irradiated enamel with SBS of the same adhesives applied in self-etch and acid-etching modes, respectively. Crown segments of sixty bovine incisors were embedded into standardized acrylic blocks. Flattened enamel surfaces were prepared. Specimens were divided into six groups according to universal adhesives and application modes randomly (n = 10), as follows: Single Bond Universal/acid-etching mode; Nova Compo-B Plus/acid-etching mode; Single Bond Universal/self-etching mode; Nova Compo-B Plus/self-etching mode; and Single Bond Universal/Er,Cr:YSGG Laser-etching mode; Nova Compo-B Plus/Er,Cr:YSGG Laser-etching mode. After surface treatments, universal adhesives were applied onto surfaces. SBS was determined after storage in water for 24 h using a universal testing machine with a crosshead speed of 0.5 mm min -1 . Failure modes were evaluated using a stereomicroscope. Data was analyzed using two-way of analyses of variances (ANOVA) (p = 0.05). Two-way ANOVA revealed that adhesive had no effect on SBS (p = 0.88), but application mode significantly influenced SBS (p = 0.00). Acid-etching significantly increased SBS, whereas there are no significant differences between self-etch mode and laser-etching for both adhesives. The bond strength of universal adhesives may depend on application mode. Acid etching may significantly increase bond strength, while laser etching may provide similar bond strength when compared to self-etch mode. © 2016 Wiley Periodicals, Inc.

  8. Effect of tooth-bleaching on the carbonate concentration in dental enamel by Raman spectroscopy

    OpenAIRE

    Vargas-Koudriavtsev, Tatiana; Herrera-Sancho, ?scar-Andrey

    2017-01-01

    Background There are not many studies evaluating the effects of surface treatments at the molecular level. The aim of this in vitro study was to analyze the concentration of carbonate molecules in dental enamel by Raman spectroscopy after the application of in-office and home whitening agents. Material and Methods Sixty human teeth were randomly divided into six groups and exposed to three different home bleaching gels (Day White) and three in-office whitening agents (Zoom! Whitespeed and Pol...

  9. Effects of a Novel Whitening Formulation on Dental Enamel.

    Science.gov (United States)

    Takesh, Thair; Sargsyan, Anik; Anbarani, Afarin; Ho, Jessica; Wilder-Smith, Petra

    2017-04-01

    The goal of this study was to evaluate the enamel whitening effects of 2 new test formulations, one of which was a rinse, and the other a whitening strip. Forty enamel chips were prepared from 20 healthy extracted teeth (2 from each tooth). After pre-staining and colorimetry to measure L* and b* values, 20 matched samples were immersed in either test or control rinses, and then colorimetry was performed again after 1 hr, 2 hr, 3 hr, 6 hr, 12 hr, 24 hr and 48 hrs (Each hour equates to one month of clinical use at the recommended dosage of 1 minute exposure 2 times a day). The remaining 20 matched samples were exposed to the test or control whitening strips and colorimetry was performed every 30 minutes for a total of 10 treatments. Overall, the whitening performance of test and control strips was similar. The test and control rinses had a similar lightening effect over the first 3 hours (equivalent to 3 months of clinical use). Subsequently, the control rinse continued to lighten samples, whereas the test rinse had little further effect. Test and control-whitening strips showed similar effects; over time whitening strips showed a greater lightening effect than whitening rinses.

  10. Dental enamel defects, caries experience and oral health-related quality of life: a cohort study.

    Science.gov (United States)

    Arrow, P

    2017-06-01

    The impact of enamel defects of the first permanent molars on caries experience and child oral health-related quality of life was evaluated in a cohort study. Children who participated in a study of enamel defects of the first permanent molars 8 years earlier were invited for a follow-up assessment. Consenting children completed the Child Perception Questionnaire and the faces Modified Child Dental Anxiety Scale, and were examined by two calibrated examiners. ANOVA, Kruskal-Wallis, negative binomial and logistic regression were used for data analyses. One hundred and eleven children returned a completed questionnaire and 91 were clinically examined. Negative binomial regression found that oral health impacts were associated with gender (boys, risk ratio (RR) = 0.73, P = 0.03) and decayed, missing or filled permanent teeth (DMFT) (RR = 1.1, P = 0.04). The mean DMFT of children were sound (0.9, standard deviation (SD) = 1.4), diffuse defects (0.8, SD = 1.7), demarcated defects (1.5, SD = 1.4) and pit defects (1.3, SD = 2.3) (Kruskal-Wallis, P = 0.05). Logistic regression of first permanent molar caries found higher odds of caries experience with baseline primary tooth caries experience (odds ratio (OR) = 1.5, P = 0.01), the number of teeth affected by enamel defects (OR = 1.9, P = 0.05) and lower odds with the presence of diffuse enamel defects (OR = 0.1, P = 0.04). The presence of diffuse enamel defects was associated with lower odds of caries experience. © 2016 Australian Dental Association.

  11. Morphological and mineral analysis of dental enamel after erosive challenge in gastric juice and orange juice.

    Science.gov (United States)

    Braga, Sheila Regina Maia; De Faria, Dalva Lúcia Araújo; De Oliveira, Elisabeth; Sobral, Maria Angela Pita

    2011-12-01

    This study evaluated and compared in vitro the morphology and mineral composition of dental enamel after erosive challenge in gastric juice and orange juice. Human enamel specimens were submitted to erosive challenge using gastric juice (from endoscopy exam) (n = 10), and orange juice (commercially-available) (n = 10), as follows: 5 min in 3 mL of demineralization solution, rinse with distilled water, and store in artificial saliva for 3 h. This cycle was repeated four times a day for 14 days. Calcium (Ca) loss after acid exposure was determined by atomic emission spectroscopy. The presence of carbonate (CO) and phosphate (PO) in the specimens was evaluated before and after the erosive challenge by FT-Raman spectroscopy. Data were tested using t-tests (P enamel was observed in scanning electron microscopy (SEM). The mean loss of Ca was: 12.74 ± 3.33 mg/L Ca (gastric juice) and 7.07 ± 1.44 mg/L Ca (orange juice). The analysis by atomic emission spectroscopy showed statistically significant difference between erosive potential of juices (P = 0.0003). FT-Raman spectroscopy found no statistically significant difference in the ratio CO/PO after the erosive challenge. The CO/PO ratios values before and after the challenge were: 0.16/0.17 (gastric juice) (P = 0.37) and 0.18/0.14 (orange juice) (P = 0.16). Qualitative analysis by SEM showed intense alterations of enamel surface. The gastric juice caused more changes in morphology and mineral composition of dental enamel than orange juice. The atomic emission spectroscopy showed to be more suitable to analyze small mineral loss after erosive challenge than FT-Raman. Copyright © 2011 Wiley Periodicals, Inc.

  12. Efficacy and cytotoxicity of a bleaching gel after short application times on dental enamel.

    Science.gov (United States)

    Soares, Diana Gabriela; Ribeiro, Ana Paula Dias; da Silveira Vargas, Fernanda; Hebling, Josimeri; de Souza Costa, Carlos Alberto

    2013-11-01

    This study aimed to evaluate and correlate the efficacy and cytotoxicity of a 35 % hydrogen peroxide (HP) bleaching gel after different application times on dental enamel. Enamel/dentin disks in artificial pulp chambers were placed in wells containing culture medium. The following groups were formed: G1, control (no bleaching); G2 and G3, three or one 15-min bleaching applications, respectively; and G4 and G5, three or one 5-min bleaching applications, respectively. Extracts (culture medium with bleaching gel components) were applied for 60 min on cultured odontoblast-like MDPC-23 cells. Cell metabolism (methyl tetrazolium assay) (Kruskal-Wallis/Mann-Whitney; α = 5 %) and cell morphology (scanning electron microscopy) were analyzed immediately after the bleaching procedures and the trans-enamel and trans-dentinal HP diffusion quantified (one-way analysis of variance/Tukey's test; α = 5 %). The alkaline phosphatase (ALP) activity was evaluated 24 h after the contact time of the extracts with the cells (Kruskal-Wallis/Mann-Whitney; α = 5 %). Tooth color was analyzed before and 24 h after bleaching using a spectrophotometer according to the Commission Internationale de l'Eclairage L*a*b* system (Kruskal-Wallis/Mann-Whitney; α = 0.05). Significant difference (p 0.05). The lowest amount of HP diffusion was observed in G5 (p 0.05). HP diffusion through dental tissues and its cytotoxic effects were proportional to the contact time of the bleaching gel with enamel. However, shorter bleaching times reduced bleaching efficacy. Shortening the in-office tooth bleaching time could be an alternative to minimize the cytotoxic effects of this clinical procedure to pulp tissue. However, the reduced time of bleaching agent application on enamel may not provide adequate esthetic outcome.

  13. Wear properties of dental ceramics and porcelains compared with human enamel.

    Science.gov (United States)

    D'Arcangelo, Camillo; Vanini, Lorenzo; Rondoni, Giuseppe D; De Angelis, Francesco

    2016-03-01

    Contemporary pressable and computer-aided design/manufacturing (CAD/CAM) ceramics exhibit good mechanical and esthetic properties. Their wear resistance compared with human enamel and traditional gold based alloys needs to be better investigated. The purpose of this in vitro study was to compare the 2-body wear resistance of human enamel, gold alloy, and 5 different dental ceramics, including a recently introduced zirconia-reinforced lithium silicate ceramic (Celtra Duo). Cylindrical specimens were fabricated from a Type III gold alloy (Aurocast8), 2 hot pressed ceramics (Imagine PressX, IPS e.max Press), 2 CAD/CAM ceramics (IPS e.max CAD, Celtra Duo), and a CAD/CAM feldspathic porcelain (Vitablocs Mark II) (n=10). Celtra Duo was tested both soon after grinding and after a subsequent glaze firing cycle. Ten flat human enamel specimens were used as the control group. All specimens were subjected to a 2-body wear test in a dual axis mastication simulator for 120000 loading cycles against yttria stabilized tetragonal zirconia polycrystal cusps. The wear resistance was analyzed by measuring the vertical substance loss (mm) and the volume loss (mm(3)). Antagonist wear (mm) was also recorded. Data were statistically analyzed with 1-way ANOVA tests (α=.05). The wear depth (0.223 mm) of gold alloy was the closest to that of human enamel (0.217 mm), with no significant difference (P>.05). The greatest wear was recorded on the milled Celtra Duo (wear depth=0.320 mm), which appeared significantly less wear resistant than gold alloy or human enamel (Pceramics did not statistically differ in comparison with the human enamel. Copyright © 2016 Editorial Council for the Journal of Prosthetic Dentistry. Published by Elsevier Inc. All rights reserved.

  14. The influence of the Nd:YAG laser bleaching on physical and mechanical properties of the dental enamel.

    Science.gov (United States)

    Marcondes, Maurem; Paranhos, Maria Paula Gandolfi; Spohr, Ana Maria; Mota, Eduardo Gonçalves; da Silva, Isaac Newton Lima; Souto, André Arigony; Burnett, Luiz Henrique

    2009-07-01

    The Nd:YAG laser can be used in Dentistry to remove soft tissue, disinfect canals in endodontic procedures and prevent caries. However, there is no protocol for Nd:YAG laser application in dental bleaching. The aims of this in vitro study were: (a) to observe the tooth shade alteration when hydrogen peroxide whitening procedures are associated with dyes with different wavelengths and irradiated with Nd:YAG laser or halogen light; (b) to measure the Vickers (VHN) enamel microhardness before and after the whitening procedure; (c) to evaluate the tensile bond strength of two types of adhesive systems applied on bleached enamel; (d) to observe the failure pattern after bond strength testing; (e) to evaluate the pulpal temperature during the bleaching procedures with halogen light or laser; (f) to measure the kinetic reaction of hydrogen peroxide. Extracted sound human molar crowns were sectioned in the mesiodistal direction to obtain 150 fragments that were divided into five groups for each adhesive system: WL (H(2)O(2) + thickener and Nd:YAG), WH (H(2)O(2) + thickener and halogen light), QL (H(2)O(2) + carbopol + Q-switch and Nd:YAG), QH (H(2)O(2) + carbopol + Q-switch and halogen light), and C (Control, without whitening agent). Shade assessment was made with a shade guide and the microhardness tests were performed before and after the bleaching procedures. Immediately afterwards, the groups were restored with the adhesive systems Adper Single Bond 2 or Solobond M plus composite resin, and the tensile bond strength test was performed. The temperature was measured by thermocouples placed on the enamel surface and intrapulpal chamber. The kinetics of hydrogen peroxide was observed by ultraviolet analysis. The shade changed seven levels for Nd:YAG laser groups and eight levels for halogen light. According to the student's t-test, there was no statistical difference between the VHN before and after the whitening protocols (p > 0.05). The tensile bond strength showed no

  15. Alteration of dentin-enamel mechanical properties due to dental whitening treatments.

    Science.gov (United States)

    Zimmerman, B; Datko, L; Cupelli, M; Alapati, S; Dean, D; Kennedy, M

    2010-05-01

    The mechanical properties of dentin and enamel affect the reliability and wear properties of a tooth. This study investigated the influence of clinical dental treatments and procedures, such as whitening treatments or etching prior to restorative procedures. Both autoclaved and non-autoclaved teeth were studied in order to allow for both comparison with published values and improved clinical relevance. Nanoindentation analysis with the Oliver-Pharr model provided elastic modulus and hardness across the dentin-enamel junction (DEJ). Large increases were observed in the elastic modulus of enamel in teeth that had been autoclaved (52.0 GPa versus 113.4 GPa), while smaller increases were observed in the dentin (17.9 GPa versus 27.9 GPa). Likewise, there was an increase in the hardness of enamel (2.0 GPa versus 4.3 GPa) and dentin (0.5 GPa versus 0.7 GPa) with autoclaving. These changes suggested that the range of elastic modulus and hardness values previously reported in the literature may be partially due to the sterilization procedures. Treatment of the exterior of non-autoclaved teeth with Crest Whitestrips, Opalescence or UltraEtch caused changes in the mechanical properties of both the enamel and dentin. Those treated with Crest Whitestrips showed a reduction in the elastic modulus of enamel (55.3 GPa to 32.7 GPa) and increase in the elastic modulus of dentin (17.2 GPa to 24.3 GPa). Opalescence treatments did not significantly affect the enamel properties, but did result in a decrease in the modulus of dentin (18.5 GPa to 15.1 GPa). Additionally, as expected, UltraEtch treatment decreased the modulus and hardness of enamel (48.7 GPa to 38.0 GPa and 1.9 GPa to 1.5 GPa, respectively) and dentin (21.4 GPa to 15.0 GPa and 1.9 GPa to 1.5 GPa, respectively). Changes in the mechanical properties were linked to altered protein concentration within the tooth, as evidenced by fluorescence microscopy and Fourier transform infrared spectroscopy. Published by Elsevier Ltd.

  16. COMPARATIVE STUDY OF THE SHEAR BOND STRENGTH OF COMPOSITE RESIN TO DENTAL ENAMEL CONDITIONED WITH PHOSPHORIC ACID OR Nd: YAG LASER

    Directory of Open Access Journals (Sweden)

    EDUARDO Carlos de Paula

    1997-01-01

    Full Text Available This study has been focused on a comparison between the shear bond strength of a composite resin attached to dental enamel surface, after a 35% phosphoric acid etching and after a Nd:YAG laser irradiation with 165.8 J/cm2 of energy density per pulse. After etching and attaching resin to these surfaces, the specimens were thermocycled and then underwent the shearing bond strength tests at a speed of 5 mm/min. The results achieved, after statistical analysis with Student's t-test, showed that the adhesion was significantly greater in the 35% phosphoric acid treated group than in the group treated with the Nd:YAG laser, thus demonstrating the need for developing new studies to reach the ideal parameters for an effective enamel surface conditioning as well as specific adhesives and composite resins when Nd:YAG laser is used

  17. Threshold value of enamel mineral solubility and dental erosion after consuming acidic soft drinks

    Directory of Open Access Journals (Sweden)

    Muhammad Ilyas

    2011-09-01

    Full Text Available Background: Dental erosion is irreversible and can caused by acidic soft drink consumption. Dental erosion prevention had already been done, but it still has not been satisfying since the consumption of acidic soft drink is still high. There is still no explanation about the threshold value of enamel mineral solubility and the occurance of dental erosion after consuming acidic soft drink. Purpose: This research is aimed to find the threshold value of enamel mineral solubility and dental erosion before and after consuming acidic soft drinks. Methods: Subjects of the research are saliva and enamel of 12 rabbits, which have some criteria such as age > 70 days, body weight > 600 grams, and teeth considered to be healthy. The sample devided equally into 4 groups. Each of those marmooths was given a drink as much as 2.5 cc/consumption (there are 1, 2 and 3× per day by using syringe without injection needle. Salivary minerals then were examined by using atomic absorption spectrophotometric (ASS, while dental erosion was examined using scanning electron microscop (SEM. The data were analyzed by using Paired t-test. Results: It is known that the threshold value of enamel mineral solubility (K, Na, Fe, Mg, Cl, P, Ca, F, C has significant difference (p < 0.05 after being exposed to folic acid. Meanwhile, Fe did not have significant difference (p = 0.090 after being exposed to citric acid. Similarly, C did not have significant difference (p = 0.063 after being exposed to bicarbonate acid. Furthermore, it is also known that the threshold time value of dental erosion are on the 105th day for folic acid, on the 111th day for citric acid, and on the 117th day for bicarbonate acid. Conclusion: Threshold value of enamel mineral solubility before and after consuming soft drinks containing acid is different. Based on the threshold value of dental erosion, it is known that folic acid is the most erosive acid.Latar belakang: Erosi gigi bersifat irreversible

  18. Ph-activated nano-amorphous calcium phosphate-based cement to reduce dental enamel demineralization.

    Science.gov (United States)

    Melo, Mary A S; Weir, Michael D; Passos, Vanara F; Powers, Michael; Xu, Hockin H K

    2017-12-01

    Enamel demineralization is destructive, esthetically compromised, and costly complications for orthodontic patients. Nano-sized amorphous calcium phosphate (NACP) has been explored to address this challenge. The 20% NACP-loaded ortho-cement notably exhibited favorable behavior on reducing demineralization of enamel around brackets in a caries model designed to simulate the carious attack. The 20% NACP-loaded ortho-cement markedly promotes higher calcium and phosphate release at a low pH, and the mineral loss was almost two fold lower and carious lesion depth decreased the by 1/3. This novel approach is promising co-adjuvant route for prevention of dental caries dissemination in millions of patients under orthodontic treatment.

  19. Evaluation of microshear bond strength of resin composites to enamel of dental adhesive systems associated with Er,Cr:YSGG laser

    Science.gov (United States)

    Cassimiro-Silva, Patricia F.; Zezell, Denise M.; Monteiro, Gabriela Q. d. M.; Benetti, Carolina; de Paula Eduardo, Carlos; Gomes, Anderson S. L.

    2016-02-01

    The aim of this in vitro study was to evaluate the microshear bond strength (μSBS) of resin composite to enamel etching by Er,Cr:YSGG laser with the use of two differents adhesives systems. Fifty freshly extracted human molars halves were embedded in acrylic resin before preparation for the study, making a total of up to 100 available samples. The specimens were randomly assigned into six groups (η=10) according to substrate pre-treatment and adhesive system on the enamel. A two-step self-etching primer system (Clearfil SE Bond) and a universal adhesive used as an etch-andrinse adhesive (Adper Single Bond Universal) were applied to the nonirradiated enamel surface according to manufacturer's instructions, as control groups (Control CF and Control SB, respectively). For the other groups, enamel surfaces were previously irradiated with the Er,Cr:YSGG laser with 0.5 W, 75 mJ and 66 J/cm2 (CF 5 Hz and SB 5 Hz) and 1.25 W, 50 mJ and 44 J/cm2 (CF 15 Hz and SB 15 Hz). Irradiation was performed under air (50%) and water (50%) cooling. An independent t-test was performed to compare the adhesive systems. Mean μSBS ± sd (MPa) for each group was 16.857 +/- 2.61, 17.87 +/- 5.83, 12.23 +/- 2.02, 9.88 +/- 2.26, 15.94 +/- 1.98, 17.62 +/- 2.10, respectively. The control groups and the 50 mJ laser groups showed no statistically significant differences, regardless of the adhesive system used. The results obtained lead us to affirm that the bonding interaction of adhesives to enamel depends not only on the morphological aspects of the dental surface, but also on the characteristics of the adhesive employed and the parameters of the laser.

  20. Effect of beverages on bovine dental enamel subjected to erosive challenge with hydrochloric acid.

    Science.gov (United States)

    Amoras, Dinah Ribeiro; Corona, Silmara Aparecida Milori; Rodrigues, Antonio Luiz; Serra, Mônica Campos

    2012-01-01

    This study evaluated by an in vitro model the effect of beverages on dental enamel previously subjected to erosive challenge with hydrochloric acid. The factor under study was the type of beverage, in five levels: Sprite® Zero Low-calorie Soda Lime (positive control), Parmalat® ultra high temperature (UHT) milk, Ades® Original soymilk, Leão® Ice Tea Zero ready-to-drink low-calorie peach-flavored black teaand Prata® natural mineral water (negative control). Seventy-five bovine enamel specimens were distributed among the five types of beverages (n=15), according to a randomized complete block design. For the formation of erosive wear lesions, the specimens were immersed in 10 mL aqueous solution of hydrochloric acid 0.01 M for 2 min. Subsequently, the specimens were immersed in 20 mL of the beverages for 1 min, twice daily for 2 days at room temperature. In between, the specimens were kept in 20 mL of artificial saliva at 37ºC. The response variable was the quantitative enamel microhardness. ANOVA and Tukey's test showed highly significant differences (penamel exposed to hydrochloric acid and beverages. The soft drink caused a significantly higher decrease in microhardness compared with the other beverages. The black tea caused a significantly higher reduction in microhardness than the mineral water, UHT milk and soymilk, but lower than the soft drink. Among the analyzed beverages, the soft drink and the black tea caused the most deleterious effects on dental enamel microhardness.

  1. Histological observation on dental hard tissue irradiated by ultrashort-pulsed laser

    Science.gov (United States)

    Uchizono, Takeyuki; Awazu, Kunio; Igarashi, Akihiro; Kato, Junji; Hirai, Yoshito

    2006-04-01

    In the field of dentistry, effectiveness of USPL irradiation is researched because USPL has less thermal side effect to dental hard tissue. In this paper, we observed morphological change and optical change of dental hard tissue irradiated by USPL for discussing the safety and effectiveness of USPL irradiation to dental hard tissues. Irradiated samples were crown enamel and root dentin of bovine teeth. Lasers were Ti:sapphire laser, which had pulse duration (P d)of 130 fsec and pulse repetition rate (f) of 1kHz and wavelength (l) of 800nm, free electron laser (FEL), which had P d of 15 μsec and f of 10Hz and wavelength of 9.6μm, and Er:YAG laser, which had P d of 250 μsec and f of 10Hz and wavelength of 2.94μm. After laser irradiation, the sample surfaces and cross sections were examined with SEM and EDX. The optical change of samples was observed using FTIR. In SEM, the samples irradiated by USPL had sharp and accurate ablation with no crack and no carbonization. But, in FEL and Er:YAG laser, the samples has rough ablation with crack and carbonization. It was cleared that the P/Ca ratio of samples irradiated by USPL had same value as non-irradiated samples. There was no change in the IR absorption spectrum between samples irradiated by USPL and non-irradiated sample. But, they of samples irradiated by FEL and Er:YAG laser, however, had difference value as non-irradiated samples. These results showed that USPL might be effective to ablate dental hard tissue without thermal damage.

  2. ON THE EROSIVE EFFECT OF SOME BEVERAGES FOR SPORTSMEN UPON DENTAL ENAMEL

    Directory of Open Access Journals (Sweden)

    Cosmin ARNAUTEANU

    2015-06-01

    Full Text Available The aim of the study was to compare the surface morphology of enamel and the variation of the mineral ions concentration after the manifestation of the erosive effect determined by various commercial beverages for athletes. 14 premolars extracted from orthodontic reasons have been cut in two halves. On each section, an enamel surface of 3x3 mm was preserved for investigations. The samples have been divided into 4 groups. In the control group, the 7 sections were kept in artificial saliva while, in the other 3 groups, the sections were introduced in 3 beverages for athletes: Gatorade Citron (Pepsi Cola Co., 5-hour Energy (Living Essentials, Powerade Cherry (Coca Cola Co.. The samples were analyzed on an electronic microscope with Vega II LSH scanning device, coupled with EDX Quantax QX2 detector. SEM analysis evidenced erosion zones at the level of enamel, which appears pinched in the samples subjected to the action of acid beverages. A decreasing tendency of the average values of calcium ion concentrations was observed in the batches in which the enamel samples had been subjected to the action of beverages for athletes. The highest relative variations of calcium and phosphorous ions (10%, respectively 8% were recorded for Gatorade, followed, in decreasing order, by Powerade, for which variations of 9%, respectively 6%, were noticed, and by the 5-hour Energy beverage, in which the relative losses were of 5%, respectively 3%. All beverages for athletes tested in the present study showed erosion potential upon the dental enamel. Gatorade appeared as the most aggressive beverage for athletes followed by Powerade and 5-hour Energy.

  3. Dental prostheses mimic the natural enamel behavior under functional loading: A review article

    Directory of Open Access Journals (Sweden)

    Ahmed A. Madfa

    2016-02-01

    Full Text Available Alumina- and zirconia-based ceramic dental restorations are designed to repair functionality as well as esthetics of the failed teeth. However, these materials exhibited several performance deficiencies such as fracture, poor esthetic properties of ceramic cores (particularly zirconia cores, and difficulty in accomplishing a strong ceramic–resin-based cement bond. Therefore, improving the mechanical properties of these ceramic materials is of great interest in a wide range of disciplines. Consequently, spatial gradients in surface composition and structure can improve the mechanical integrity of ceramic dental restorations. Thus, this article reviews the current status of the functionally graded dental prostheses inspired by the dentino-enamel junction (DEJ structures and the linear gradation in Young's modulus of the DEJ, as a new material design approach, to improve the performance compared to traditional dental prostheses. This is a remarkable example of nature's ability to engineer functionally graded dental prostheses. The current article opens a new avenue for recent researches aimed at the further development of new ceramic dental restorations for improving their clinical durability.

  4. Do pediatric medicines induce topographic changes in dental enamel?

    Science.gov (United States)

    Alexandria, Adílis Kalina; Meckelburg, Nicolli de Araujo; Puetter, Ursula Tavares; Salles, Jordan Trugilho; Souza, Ivete Pomarico Ribeiro; Maia, Lucianne Cople

    2016-01-01

    The purpose of the present study was to evaluate the effect of common pediatric liquid medicines on surface roughness and tooth structure loss and to evaluate the pH values of these medicines at room and cold temperatures in vitro. Eighty-four bovine enamel blocks were divided into seven groups (n = 12): G1-Alivium®, G2-Novalgina®, G3-Betamox®, G4-Clavulin®, G5-Claritin®, G6-Polaramine® and G7-Milli-Q water (negative control). The pH was determined and the samples were immersed in each treatment 3x/day for 5 min. 3D non-contact profilometry was used to determine surface roughness (linear Ra, volumetric Sa) and the Gap formed between treated and control areas in each block. Scanning electron microscopy (SEM) and energy dispersive spectrometry (EDS) were also performed. The majority of liquid medicines had pH ≤ 5.50. G1, G4, and G5 showed alterations in Ra when compared with G7 (p < 0.05). According to Sa and Gap results, only G5 was different from G7 (p < 0.05). Alteration in surface was more evident in G5 SEM images. EDS revealed high concentrations of carbon, oxygen, phosphorus, and calcium in all tested groups. Despite the low pH values of all evaluated medicines, only Alivium®, Clavulin®, and Claritin® increased linear surface roughness, and only Claritin® demonstrated the in vitro capacity to produce significant tooth structure loss.

  5. Effect of Toothpaste Application Prior to Dental Bleaching on Whitening Effectiveness and Enamel Properties.

    Science.gov (United States)

    Vieira-Junior, W F; Lima, D A N L; Tabchoury, C P M; Ambrosano, G M B; Aguiar, F H B; Lovadino, J R

    2016-01-01

    The purpose of this study was to investigate the effects on the enamel properties and effectiveness of bleaching using 35% hydrogen peroxide (HP) when applying toothpastes with different active agents prior to dental bleaching. Seventy enamel blocks (4 × 4 × 2 mm) were submitted to in vitro treatment protocols in a tooth-brushing machine (n=10): with distilled water and exposure to placebo gel (negative control [NC]) or HP bleaching (positive control [PC]); and brushing with differing toothpastes prior to HP bleaching, including potassium nitrate toothpaste (PN) containing NaF, conventional sodium monofluorophosphate toothpaste (FT), arginine-based toothpastes (PA and SAN), or a toothpaste containing bioactive glass (NM). Color changes were determined using the CIE L*a*b* system (ΔE, ΔL, Δa, and Δb), and a roughness (Ra) analysis was performed before and after treatments. Surface microhardness (SMH) and cross-sectional microhardness (CSMH) were analyzed after treatment. Data were analyzed with repeated measures ANOVA for Ra, one-way ANOVA (SMH, ΔE, ΔL, Δa, and Δb), split-plot ANOVA (CSMH), and Tukey post hoc test (α PA = SAN > all other groups) or decreased HP effects (CSMH). Ra increased in all bleached groups, with the exception of NM, which did not differ from the NC. The variation in the color variables (ΔL, Δa, and Δb) explained 21% of the variation in the physical surface variables (Ra and SMH). The application of toothpaste prior to dental bleaching did not interfere with the effectiveness of treatment. The bioactive glass based toothpaste protected the enamel against the deleterious effects of dental bleaching.

  6. The staining effect of different mouthwashes containing nanoparticles on dental enamel.

    OpenAIRE

    Eslami, Neda; Ahrari, Farzaneh; Rajabi, Omid; Zamani, Roya

    2015-01-01

    Background This study aimed to evaluate the effects of several mouthwashes containing nanoparticles on discoloration of dental enamel, and compare the results with that of 0.2% chlorhexidine (CHX). Material and Methods Sixty intact premolars were randomly assigned to six groups. A spectrophotometer was used to measure the color of the teeth (T1) according to the CIELAB system. The specimens in groups 1 to 4 were then immersed in colloidal solutions containing nanoTiO2 (Group 1), nanoZnO (Grou...

  7. Dental management of the irradiated patient

    International Nuclear Information System (INIS)

    Beumer III, J.; Brady, F.A.

    1978-01-01

    There is an increasing number of patients receiving radiation therapy for oral malignancies. In many malignant tumors, radiation is often the treatment of choice, while in others it may be used in conjunction with surgery or chemotherapy. There are inherent dental and oral problems associated with radiation therapy. It is the purpose of this paper to deal briefly with the physical principles and the biological basis of radiation theraphy. In addition, the specific radiation effects on oral mucous membranes, taste buds, salivary glands, bone, the periodontium and teeth will be discussed. Radiation complications in edentulous patients, and in particular the problems of wearing dentures in such patients will be evaluated. An approach to the problem of dental extractions and other dental treatments in the pre- and post-irradiated patient is suggested. (author)

  8. Selective ablation of dental enamel and dentin using femtosecond laser pulses

    International Nuclear Information System (INIS)

    Lizarelli, R F Z; Costa, M M; Carvalho-Filho, E; Bagnato, V S; Nunes, F D

    2008-01-01

    The study of the interaction of intense laser light with matter, as well as transient response of atoms and molecules is very appropriated because of the laser energy concentration in a femtosecond optical pulses. The fundamental problem to be solved is to find tools and techniques which allow us to observe and manipulate on a femtosecond time scale the photonics events on and into the matter. Six third human extracted molars were exposed to a femtosecond Ti:Sapphire Q-switched and mode locked laser (Libra-S, Coherent, Palo Alto, CA, USA), emitting pulses with 70 fs width, radiation wavelength of 801 nm, at a constant pulse repetition rate of 1 KHz. The laser was operated at different power levels (70 to 400 mW) with constant exposition time of 10 seconds, at focused and defocused mode. Enamel and dentin surfaces were evaluated concerned ablation rate and morphological aspects under scanning electron microscopic. The results in this present experiment suggest that at the focused mode and under higher average power, enamel tissues present microcavities with higher depth and very precise edges, but, while dentin shows a larger melt-flushing, lower depth and melting and solidification aspect. In conclusion, it is possible to choose hard or soft ablation, under lower and higher average power, respectively, revealing different aspects of dental enamel and dentin, depending on the average power, fluence and distance from the focal point of the ultra-short pulse laser on the tooth surface

  9. Effect of tooth-bleaching on the carbonate concentration in dental enamel by Raman spectroscopy.

    Science.gov (United States)

    Vargas-Koudriavtsev, Tatiana; Herrera-Sancho, Óscar-Andrey

    2017-01-01

    There are not many studies evaluating the effects of surface treatments at the molecular level. The aim of this in vitro study was to analyze the concentration of carbonate molecules in dental enamel by Raman spectroscopy after the application of in-office and home whitening agents. Sixty human teeth were randomly divided into six groups and exposed to three different home bleaching gels (Day White) and three in-office whitening agents (Zoom! Whitespeed and PolaOffice) according to the manufacturer´s instructions. The concentration of carbonate molecules in enamel was measured prior to and during the treatment by means of Raman spectroscopy. Statistical analysis included repeated measures analysis of variance ( p ≤0.05) and Bonferroni pairwise comparisons. At home bleaching agents depicted a decrease in the carbonate molecule. This decrease was statistically significant for the bleaching gel with the highest hydrogen peroxide concentration ( p ≤0,05). In-office whitening agents caused an increase in carbonate, which was significant for all three groups ( p ≤0,05). In-office bleaching gels seem to cause a gain in carbonate of the enamel structure, whilst at-home whitening gels caused a loss in carbonate. Key words: Bleaching, whitening, hydrogen peroxide, carbamide peroxide, Raman spectroscopy, carbonate.

  10. Genes expressed in dental enamel development are associated with molar-incisor hypomineralization.

    Science.gov (United States)

    Jeremias, Fabiano; Koruyucu, Mine; Küchler, Erika C; Bayram, Merve; Tuna, Elif B; Deeley, Kathleen; Pierri, Ricardo A; Souza, Juliana F; Fragelli, Camila M B; Paschoal, Marco A B; Gencay, Koray; Seymen, Figen; Caminaga, Raquel M S; dos Santos-Pinto, Lourdes; Vieira, Alexandre R

    2013-10-01

    Genetic disturbances during dental development influence variation of number and shape of the dentition. In this study, we tested if genetic variation in enamel formation genes is associated with molar-incisor hypomineralization (MIH), also taking into consideration caries experience. DNA samples from 163 cases with MIH and 82 unaffected controls from Turkey, and 71 cases with MIH and 89 unaffected controls from Brazil were studied. Eleven markers in five genes [ameloblastin (AMBN), amelogenin (AMELX), enamelin (ENAM), tuftelin (TUFT1), and tuftelin-interacting protein 11 (TFIP11)] were genotyped by the TaqMan method. Chi-square was used to compare allele and genotype frequencies between cases with MIH and controls. In the Brazilian data, distinct caries experience within the MIH group was also tested for association with genetic variation in enamel formation genes. The ENAM rs3796704 marker was associated with MIH in both populations (Brazil: p=0.03; OR=0.28; 95% C.I.=0.06-1.0; Turkey: p=1.22e-012; OR=17.36; 95% C.I.=5.98-56.78). Associations between TFIP11 (p=0.02), ENAM (p=0.00001), and AMELX (p=0.01) could be seen with caries independent of having MIH or genomic DNA copies of Streptococcus mutans detected by real time PCR in the Brazilian sample. Several genes involved in enamel formation appear to contribute to MIH. Copyright © 2013 Elsevier Ltd. All rights reserved.

  11. Analysis of the Early Stages and Evolution of Dental Enamel Erosion.

    Science.gov (United States)

    Derceli, Juliana Dos Reis; Faraoni, Juliana Jendiroba; Pereira-da-Silva, Marcelo Assumpção; Palma-Dibb, Regina Guenka

    2016-01-01

    The aim of this study was to evaluate by atomic force microscopy (AFM) the early phases and evolution of dental enamel erosion caused by hydrochloric acid exposure, simulating gastroesophageal reflux episodes. Polished bovine enamel slabs (4x4x2 mm) were selected and exposed to 0.1 mL of 0.01 M hydrochloric acid (pH=2) at 37 ?#61472;?#61616;C using five different exposure intervals (n=1): no acid exposure (control), 10 s, 20 s, 30 s and 40 s. The exposed area was analyzed by AFM in 3 regions to measure the roughness, surface area and morphological surface. The data were analyzed qualitatively. Roughness started as low as that of the control sample, Rrms=3.5 nm, and gradually increased at a rate of 0.3 nm/s, until reaching Rrms=12.5 nm at 30 s. After 40 s, the roughness presented increment of 0.40 nm only. Surface area (SA) increased until 20 s, and for longer exposures, the surface area was constant (at 30 s, SA=4.40 μm2 and at 40 s, SA=4.43 μm2). As regards surface morphology, the control sample presented smaller hydroxyapatite crystals (22 nm) and after 40 s the crystal size was approximately 60 nm. Short periods of exposure were sufficient to produce enamel demineralization in different patterns and the morphological structure was less affected by exposure to hydrochloric acid over 30 s.

  12. Developmental defects of enamel and dental caries in the primary dentition: A systematic review and meta-analysis.

    Science.gov (United States)

    Costa, Francine S; Silveira, Ethieli R; Pinto, Gabriela S; Nascimento, Gustavo G; Thomson, William Murray; Demarco, Flávio F

    2017-05-01

    This systematic review and meta-analysis evaluated the association between developmental defects of enamel and dental caries in the primary dentition. Electronic searches were performed in PubMed, Web of Knowledge, Scopus and Scielo for the identification of relevant studies. Observational studies that examined the association between developmental defects of enamel and dental caries in the deciduous dentition were included. Additionally, meta-analysis, funnel plots and sensitivity analysis were employed to synthesize the available evidence. Multivariable meta-regression analysis was performed to explore heterogeneity among studies. A total of 318 articles were identified in the electronic searches. Of those, 16 studies were included in the meta-analysis. Pooled estimates revealed that children with developmental defects of enamel had higher odds of having dental caries (OR 3.32; 95%CI 2.41-4.57), with high heterogeneity between studies (I 2 80%). Methodological characteristic of the studies, such as where it was conducted, the examined teeth and the quality of the study explained about 30% of the variability. Concerning type of defect, children with hypoplasia and diffuse opacities had higher odds of having dental caries (OR 4.28; 95%CI 2.24-8.15; OR1.42; 95%CI 1.15-1.76, respectively). This systematic review and meta-analysis demonstrates a clear association between developmental defects of enamel and dental caries in the primary dentition. Copyright © 2017 Elsevier Ltd. All rights reserved.

  13. In vitro studies of morphological changes in enamel surface after Er:YAG and Nd:YAG laser irradiation, by SEM; Estudo in vitro do efeito do laser Nd:YAG e Er:YAG sobre o esmalte dental humano atraves de microscopia eletronica de varredura

    Energy Technology Data Exchange (ETDEWEB)

    Verlangieri, Eleonora Jaeger

    2001-07-01

    The caries prevention by using laser irradiation has been investigated by many authors using various lasers with different irradiations conditions. The purpose of this study was to investigated the morphological changes in enamel surface after Er:YAG and Nd:YAG laser irradiation, in vitro, by SEM. Fifteen freshly extracted, intact, caries-free, human third molars, were used in this study. The coronary portions were sectioned, from buccal to lingual direction, in two half-parts. Each one was irradiated by a different laser. The first one was irradiated with water-air spray, by a Nd:YAG laser, at 1.084 nm wave length, at 10 W, 10 Hz, 100 mJ for 60 sec., with an optical fiber in contact mode (0,32 mm of diameter); and the other half, with water-air spray by an Er:YAG laser at 2,94 micrometers wave length at the parameters of 4 Hz, 80 mJ, 24.95 J/cm{sup 2} for 60 sec. The results of this study suggested that both lasers promoted morphological changes in the enamel surface enhancing resistance and can be an alternative clinical method for caries preventions. (author)

  14. In vitro study of 960 nm high power diode laser applications in dental enamel, aided by the presence of a photoinitiator dye: scanning electron microscopy analysis

    International Nuclear Information System (INIS)

    Oliveira, Marcelo Vinicius de

    2002-06-01

    The objective of this study is to verify if a high power diode laser can effectively modify the morphology of an enamel surface, and if this can be done in a controlled fashion by changing the lasers parameters. Previous studies using SEM demonstrated that through irradiation with Nd:YAG laser (1064 nm) it is possible to modify the morphology of the dental surface in such way as to increase its resistance against caries decays. The desired procedures that should achieve a decrease of the index of caries decays and of its sequels are on a primary level, which means that action is necessary before the disease installs itself. In this study it was used for the first time a prototype of a high power diode laser operating at 960 nm, produced by the Laboratory of Development of Lasers of the Center for Lasers and Applications of the IPEN. This equipment can present several advantages as reliability, reduced size and low cost. The aim was establish parameters of laser irradiation that produce the desired effects wanted in the enamel and protocols that guarantee its safety during application in dental hard tissues, protecting it of heating effects such as fissures and carbonization. (author)

  15. Shear bond strength and SEM morphology evaluation of different dental adhesives to enamel prepared with ER:YAG laser.

    Science.gov (United States)

    Pires, Patrícia T; Ferreira, João C; Oliveira, Sofia A; Azevedo, Alvaro F; Dias, Walter R; Melo, Paulo R

    2013-01-01

    Early observations of enamel surfaces prepared by erbium lasers motivated clinicians to use laser as an alternative to chemical etching. Evaluate shear bond strength (SBS) values of different dental adhesives on Erbium:Yttrium Aluminum Garnet (Er:YAG) laser prepared enamel and to evaluate possible etching patterns correlations between dental adhesives and SBS values. One hundred bovine incisors were randomly assigned to SBS tests on enamel (n = 15) and to enamel morphology analysis (n = 5) after Er:YAG laser preparation as follows: Group I - 37% phosphoric acid (PA)+ ExciTE(®); Group II - ExciTE(®); Group III - AdheSE(®) self-etching; Group IV - FuturaBond(®) no-rinse. NR; Group V - Xeno(®) V. Teeth were treated with the adhesive systems and subjected to thermal cycling. SBS were performed in a universal testing machine at 5 mm/min. One-way ANOVA and post-hoc tests (P adhesive systems yielded significantly different SBSs. Acid etching significantly increased the adhesion in laser treated enamel. No differences in SBS values were obtained between AdheSE(®) and ExciTE(®) without condition with PA. FuturaBond(®) NR and Xeno(®) V showed similar SBS, which was lower in comparison to the others adhesives. No correlation between enamel surface morphology and SBS values was observed, except when PA was used.

  16. Novel Dental Cement to Combat Biofilms and Reduce Acids for Orthodontic Applications to Avoid Enamel Demineralization

    Directory of Open Access Journals (Sweden)

    Ning Zhang

    2016-05-01

    Full Text Available Orthodontic treatments often lead to biofilm buildup and white spot lesions due to enamel demineralization. The objectives of this study were to develop a novel bioactive orthodontic cement to prevent white spot lesions, and to determine the effects of cement compositions on biofilm growth and acid production. 2-methacryloyloxyethyl phosphorylcholine (MPC, nanoparticles of silver (NAg, and dimethylaminohexadecyl methacrylate (DMAHDM were incorporated into a resin-modified glass ionomer cement (RMGI. Enamel shear bond strength (SBS was determined. Protein adsorption was determined using a micro bicinchoninic acid method. A dental plaque microcosm biofilm model with human saliva as inoculum was used to investigate metabolic activity, colony-forming units (CFU and lactic acid production. Incorporating 3% of MPC, 1.5% of DMAHDM, and 0.1% of NAg into RMGI, and immersing in distilled water at 37 °C for 30 days, did not decrease the SBS, compared to control (p > 0.1. RMGI with 3% MPC + 1.5% DMAHDM + 0.1% NAg had protein amount that was 1/10 that of control. RMGI with triple agents (MPC + DMAHDM + NAg had much stronger antibacterial property than using a single agent or double agents (p < 0.05. Biofilm CFU on RMGI with triple agents was reduced by more than 3 orders of magnitude, compared to commercial control. Biofilm metabolic activity and acid production were also greatly reduced. In conclusion, adding MPC + DMAHDM + NAg in RMGI substantially inhibited biofilm viability and acid production, without compromising the orthodontic bracket bond strength to enamel. The novel bioactive cement is promising for orthodontic applications to hinder biofilms and plaque buildup and enamel demineralization.

  17. Acid demineralization susceptibility of dental enamel submitted to different bleaching techniques and fluoridation regimens.

    Science.gov (United States)

    Salomão, Dlf; Santos, Dm; Nogueira, Rd; Palma-Dibb, Rg; Geraldo-Martins, Vr

    2014-01-01

    The aim of the current study was to assess the acid demineralization susceptibility of bleached dental enamel submitted to different fluoride regimens. One hundred bovine enamel blocks (6×6×3 mm) were randomly divided into 10 groups (n=10). Groups 1 and 2 received no bleaching. Groups 3 to 6 were submitted to an at-home bleaching technique using 6% hydrogen peroxide (HP; G3 and G4) or 10% carbamide peroxide (CP; G5 and G6). Groups 7 to 10 were submitted to an in-office bleaching technique using 35% HP (G7 and G8) or 35% CP (G9 and G10). During bleaching, a daily fluoridation regimen of 0.05% sodium fluoride (NaF) solution was performed on groups 3, 5, 7, and 9, while weekly fluoridation with a 2% NaF gel was performed on groups 4, 6, 8, and 10. The samples in groups 2 to 10 were pH cycled for 14 consecutive days. The samples from all groups were then assessed by cross-sectional Knoop microhardness at different depths from the outer enamel surface. The average Knoop hardness numbers (KHNs) were compared using one-way analysis of variance and Tukey tests (α=0.05). The comparison between groups 1 and 2 showed that the demineralization method was effective. The comparison among groups 2 to 6 showed the same susceptibility to acid demineralization, regardless of the fluoridation method used. However, the samples from groups 8 and 10 showed more susceptibility to acid demineralization when compared with group 2 (penamel to acid demineralization. However, the use of 35% HP and 35% CP must be associated with a daily fluoridation regimen, otherwise the in-office bleaching makes the bleached enamel more susceptible to acid demineralization.

  18. Disturbances in dental development after total body irradiation in bone marrow transplant recipients

    International Nuclear Information System (INIS)

    Dahlloef, G.B.; Barr, M.; Bolme, P.; Modeer, T.; Loennqvist, B.R.; Ringden, O.; Heimdahl, A.

    1988-01-01

    The dental status of 16 children who had been treated with bone marrow transplantation (BMT) for serious bone marrow diseases was followed for up to 6 years. Several types of disturbances in dental development were observed in children who had been conditioned with total body irradiation (TBI) at 10 Gy before BMT. Thus, impaired root development that caused short V-shaped roots was found in all patients, a complete failure of root development and premature apical closure were found in five patients, enamel hypoplasia was observed in four patients, and microdontia was observed in three patients conditioned with TBI. Patients younger than 6 years of age at BMT exhibited the most severe and extensive dental aberrations. The TBI at 10 Gy appeared to be the major cause of the disturbances found

  19. Micro energy-dispersive X-ray fluoresence mapping of enamel and dental materials after chemical erosion.

    Science.gov (United States)

    Soares, Luís Eduardo Silva; de Oliveira, Rodrigo; Nahórny, Sídnei; Santo, Ana Maria do Espírito; Martin, Airton Abrahão

    2012-10-01

    Energy-dispersive X-ray fluorescence was employed to test the hypothesis that beverage consumption or mouthwash utilization will change the chemical properties of dental materials and enamel mineral content. Bovine enamel samples (n = 45) each received two cavity preparations (n = 90), each pair filled with one of three dental materials (R: nanofilled composite resin; GIC: glass-ionomer cement; RMGIC: resin-modified GIC). Furthermore, they were treated with three different solutions (S: saliva; E: erosion/Pepsi Twist®; or EM: erosion+mouthwash/Colgate Plax®). It was found that mineral loss in enamel was greater in GICE samples than in RE > RMGICE > RMGICEM > REM > GICEM. An increased percentage of Zr was found in REM indicating organic matrix degradation. Dental materials tested (R, GIC, and RMGIC) were not able to protect adjacent enamel from acid erosion by the soft drink tested. The use of mouthwash promoted protection of enamel after erosion by the soft drink. To avoid chemical dissolution by mouthwashes, protection by resin composites with surface sealants is recommended.

  20. The role of mesoscopic modelling in understanding the response of dental enamel to mid-infrared radiation

    Energy Technology Data Exchange (ETDEWEB)

    Verde, A Vila [Department of Chemical Engineering, Fenske Laboratory, Pennsylvania State University, University Park, PA 16802 (United States); Ramos, M M D [Department of Physics, University of Minho, 4710-057 Braga (Portugal); Stoneham, A M [London Centre for Nanotechnology and Department of Physics and Astronomy, University College London, Gower Street, London WC1E 6BT (United Kingdom)

    2007-05-21

    Human dental enamel has a porous mesostructure at the nanometre to micrometre scales that affects its thermal and mechanical properties relevant to laser treatment. We exploit finite-element models to investigate the response of this mesostructured enamel to mid-infrared lasers (CO{sub 2} at 10.6 {mu}m and Er:YAG at 2.94 {mu}m). Our models might easily be adapted to investigate ablation of other brittle composite materials. The studies clarify the role of pore water in ablation, and lead to an understanding of the different responses of enamel to CO{sub 2} and Er:YAG lasers, even though enamel has very similar average properties at the two wavelengths. We are able to suggest effective operating parameters for dental laser ablation, which should aid the introduction of minimally-invasive laser dentistry. In particular, our results indicate that, if pulses of {approx}10 {mu}s are used, the CO{sub 2} laser can ablate dental enamel without melting, and with minimal damage to the pulp of the tooth. Our results also suggest that pulses with 0.1-1 {mu}s duration can induce high stress transients which may cause unwanted cracking.

  1. The role of mesoscopic modelling in understanding the response of dental enamel to mid-infrared radiation

    Science.gov (United States)

    Vila Verde, A.; Ramos, M. M. D.; Stoneham, A. M.

    2007-05-01

    Human dental enamel has a porous mesostructure at the nanometre to micrometre scales that affects its thermal and mechanical properties relevant to laser treatment. We exploit finite-element models to investigate the response of this mesostructured enamel to mid-infrared lasers (CO2 at 10.6 µm and Er:YAG at 2.94 µm). Our models might easily be adapted to investigate ablation of other brittle composite materials. The studies clarify the role of pore water in ablation, and lead to an understanding of the different responses of enamel to CO2 and Er:YAG lasers, even though enamel has very similar average properties at the two wavelengths. We are able to suggest effective operating parameters for dental laser ablation, which should aid the introduction of minimally-invasive laser dentistry. In particular, our results indicate that, if pulses of ap10 µs are used, the CO2 laser can ablate dental enamel without melting, and with minimal damage to the pulp of the tooth. Our results also suggest that pulses with 0.1-1 µs duration can induce high stress transients which may cause unwanted cracking.

  2. The role of mesoscopic modelling in understanding the response of dental enamel to mid-infrared radiation

    International Nuclear Information System (INIS)

    Verde, A Vila; Ramos, M M D; Stoneham, A M

    2007-01-01

    Human dental enamel has a porous mesostructure at the nanometre to micrometre scales that affects its thermal and mechanical properties relevant to laser treatment. We exploit finite-element models to investigate the response of this mesostructured enamel to mid-infrared lasers (CO 2 at 10.6 μm and Er:YAG at 2.94 μm). Our models might easily be adapted to investigate ablation of other brittle composite materials. The studies clarify the role of pore water in ablation, and lead to an understanding of the different responses of enamel to CO 2 and Er:YAG lasers, even though enamel has very similar average properties at the two wavelengths. We are able to suggest effective operating parameters for dental laser ablation, which should aid the introduction of minimally-invasive laser dentistry. In particular, our results indicate that, if pulses of ∼10 μs are used, the CO 2 laser can ablate dental enamel without melting, and with minimal damage to the pulp of the tooth. Our results also suggest that pulses with 0.1-1 μs duration can induce high stress transients which may cause unwanted cracking

  3. Adherence inhibition of Streptococcus mutans on dental enamel surface using silver nanoparticles

    International Nuclear Information System (INIS)

    Espinosa-Cristóbal, L.F.; Martínez-Castañón, G.A.; Téllez-Déctor, E.J.

    2013-01-01

    The aim of this ex vivo study was to evaluate the adherence capacity of Streptococcus mutans after being exposed to three different sizes of silver nanoparticles on healthy human dental enamel. Three different sizes of silver nanoparticles (9.3, 21.3 and 98 nm) were prepared, characterized and an adherence testing was performed to evaluate their anti-adherence activity on a reference strain of S. mutans on healthy dental enamel surfaces. Colony-Forming Unit count was made for adherence test and light microscopy, atomic force microscopy and scanning electron microscopy were used to compare qualitative characteristics of S. mutans. 9.3 nm and 21.3 nm groups did not show differences between them but statistical differences were found when 9.3 nm and 21.3 nm groups were compared with 98 nm and negative control groups (p < 0.05). Microscopy analysis shows a better inhibition of S. mutans adherence in 9.3 nm and 21.3 nm groups than the 98 nm group when compared with control group. Silver nanoparticles showed an adherence inhibition on S. mutans and the anti-adherence capacity was better when silver nanoparticles were smaller. Highlights: ► We examined how SNP can affect cellular adhesion from S. mutans. ► Several techniques were applied to analyzed S. mutans biofilm on enamel. ► All SNP sizes had an adhesion inhibition of S. mutans. ► Smaller SNP showed a better adhesion inhibition than larger SNP. ► Inhibition effect of SNP could be related with adhesion inhibition from S. mutans

  4. Adherence inhibition of Streptococcus mutans on dental enamel surface using silver nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Espinosa-Cristóbal, L.F. [Doctorado Institucional en Ingeniería y Ciencia de Materiales, Universidad Autónoma de San Luis Potosí, Av. Salvador Nava S/N, Zona Universitaria, C.P. 78290 San Luis Potosí, S.L.P. (Mexico); Maestría en Ciencias Odontológicas en el Área de Odontología Integral Avanzada, Universidad Autónoma de San Luis Potosí, Av. Salvador Nava S/N, Zona Universitaria, C.P. 78290 San Luis Potosí, S.L.P. (Mexico); Martínez-Castañón, G.A., E-mail: mtzcastanon@fciencias.uaslp.mx [Doctorado Institucional en Ingeniería y Ciencia de Materiales, Universidad Autónoma de San Luis Potosí, Av. Salvador Nava S/N, Zona Universitaria, C.P. 78290 San Luis Potosí, S.L.P. (Mexico); Maestría en Ciencias Odontológicas en el Área de Odontología Integral Avanzada, Universidad Autónoma de San Luis Potosí, Av. Salvador Nava S/N, Zona Universitaria, C.P. 78290 San Luis Potosí, S.L.P. (Mexico); Téllez-Déctor, E.J. [Facultad de Odontología de la Universidad Veracruzana campus Río Blanco, Mariano Abasolo S/N. Col. Centro. Río Blanco, Veracruz (Mexico); and others

    2013-05-01

    The aim of this ex vivo study was to evaluate the adherence capacity of Streptococcus mutans after being exposed to three different sizes of silver nanoparticles on healthy human dental enamel. Three different sizes of silver nanoparticles (9.3, 21.3 and 98 nm) were prepared, characterized and an adherence testing was performed to evaluate their anti-adherence activity on a reference strain of S. mutans on healthy dental enamel surfaces. Colony-Forming Unit count was made for adherence test and light microscopy, atomic force microscopy and scanning electron microscopy were used to compare qualitative characteristics of S. mutans. 9.3 nm and 21.3 nm groups did not show differences between them but statistical differences were found when 9.3 nm and 21.3 nm groups were compared with 98 nm and negative control groups (p < 0.05). Microscopy analysis shows a better inhibition of S. mutans adherence in 9.3 nm and 21.3 nm groups than the 98 nm group when compared with control group. Silver nanoparticles showed an adherence inhibition on S. mutans and the anti-adherence capacity was better when silver nanoparticles were smaller. Highlights: ► We examined how SNP can affect cellular adhesion from S. mutans. ► Several techniques were applied to analyzed S. mutans biofilm on enamel. ► All SNP sizes had an adhesion inhibition of S. mutans. ► Smaller SNP showed a better adhesion inhibition than larger SNP. ► Inhibition effect of SNP could be related with adhesion inhibition from S. mutans.

  5. [The effects of topical fluoridation of enamel on the growth of cariogenic bacteria contained in the dental plaque].

    Science.gov (United States)

    Płuciennik-Stronias, Małgorzata; Zarzycka, Beata; Bołtacz-Rzepkowska, Elzbieta

    2013-01-01

    Dental caries is a bacterial disease. The most important element used in caries prevention is fluoride, which is derived from the air, diet or fluoride-containing preparations and materials, e.g. glass-ionomer restorations. Fluoride can inhibit metabolism and bacterial growth in the dental plaque. The aim of the study was to evaluate the effect of topical fluoridation of the enamel on the growth of Lactobacillus spp. in the dental plaque. The study was carried out in 15 patients with good oral hygiene, in whom three-day dental plaque from the enamel was examined. Next, fluoride was rubbed on the same surface and the examination of three-day dental plaque was repeated. No statistically significant differences (p = 0.475) in the amounts of Lactobacillus spp. in the plaque collected prior to and after the topical fluoridation were revealed. Fluoride rubbed in the enamel, did not affect the amount of Lactobacillus spp. in the dental plaque growing on this material.

  6. Efficacy of microtensile versus microshear bond testing for evaluation of bond strength of dental adhesive systems to enamel

    NARCIS (Netherlands)

    El Zohairy, A.A.; Saber, M.H.; Abdalla, A.I.; Feilzer, A.J.

    2010-01-01

    Objective The aim of the study was to evaluate the efficacy of the microtensile bond test (μTBS) and the microshear bond test (μSBS) in ranking four dental adhesives according to bond strength to enamel and identify the modes of failure involved. Materials and methods Forty-four caries-free human

  7. Detection sensitivity of fluorine in dental enamel through the 19F(p,psup(')γ)19F reaction

    International Nuclear Information System (INIS)

    Papper, C.S.; Chittleborough, G.; Kennett, S.R.; Chaudhri, M.A.

    1978-01-01

    The total cross sections for production of 109 and 197 keV gamma rays in the reaction 19 F(p,psup(')γ) 19 F have been measured, over a range of energies up to 4.3 MeV. From these cross sections, the thick detection sensitivities for a uniform distribution of fluorine in dental enamel have been calculated

  8. Prevalence of dental anomalies and enamel hypoplasia in primary dentition among preschool children of West Godavari District, Andhra Pradesh -A cross - sectional study

    Directory of Open Access Journals (Sweden)

    Suzan Sahana

    2013-01-01

    Full Text Available Background: It is axiomatic that Pediatric dental anomalies and enamel hypoplasia (E.H are routinely encountered in primary dentition and early detection and prudent management of the condition facilitates normal occlusal development. Objectives: To determine the prevalence of various dental anomalies and enamel hypoplasia in preschool children between two to six years of age. Materials & Method: A total of 1898 children, between two to six years were randomly selected and screened for dental anomalies and enamel hypoplasia The chi square test was used to analyze the data statistically. Results: The overall prevalence rate of dental anomalies and enamel hypoplasia in this study was 0.63% and 8.95% respectively. Double teeth were the most frequently reported dental anomaly while supernumerary teeth were least reported. None of them reported with hypodontia.

  9. Qualitative and quantitative evaluation of human dental enamel after bracket debonding: a noncontact three-dimensional optical profilometry analysis.

    Science.gov (United States)

    Ferreira, Fabiano G; Nouer, Darcy F; Silva, Nelson P; Garbui, Ivana U; Correr-Sobrinho, Lourenço; Nouer, Paulo R A

    2014-09-01

    The aim of this study was to undertake a qualitative and quantitative evaluation of changes on enamel surfaces after debonding of brackets followed by finishing procedures, using a high-resolution three-dimensional optical profiler and to investigate the accuracy of the technique. The labial surfaces of 36 extracted upper central incisors were examined. Before bonding, the enamel surfaces were subjected to profilometry, recording four amplitude parameters. Brackets were then bonded using two types of light-cured orthodontic adhesive: composite resin and resin-modified glass ionomer cement. Finishing was performed by three different methods: pumice on a rubber cup, fine and ultrafine aluminum oxide discs, and microfine diamond cups followed by silicon carbide brushes. The samples were subsequently re-analyzed by profilometry. Wilcoxon signed-rank test, Kruskal-Wallis test (p enamel roughness when diamond cups followed by silicon carbide brushes were used to finish surfaces that had remnants of resin-modified glass ionomer adhesive and when pumice was used to finish surfaces that had traces of composite resin. Enamel loss was minimal. The 3D optical profilometry technique was able to provide accurate qualitative and quantitative assessment of changes on the enamel surface after debonding. Morphological changes in the topography of dental surfaces, especially if related to enamel loss and roughness, are of considerable clinical importance. The quantitative evaluation method used herein enables a more comprehensive understanding of the effects of orthodontic bonding on teeth.

  10. Oriented and Ordered Biomimetic Remineralization of the Surface of Demineralized Dental Enamel Using HAP@ACP Nanoparticles Guided by Glycine

    Science.gov (United States)

    Wang, Haorong; Xiao, Zuohui; Yang, Jie; Lu, Danyang; Kishen, Anil; Li, Yanqiu; Chen, Zhen; Que, Kehua; Zhang, Qian; Deng, Xuliang; Yang, Xiaoping; Cai, Qing; Chen, Ning; Cong, Changhong; Guan, Binbin; Li, Ting; Zhang, Xu

    2017-01-01

    Achieving oriented and ordered remineralization on the surface of demineralized dental enamel, thereby restoring the satisfactory mechanical properties approaching those of sound enamel, is still a challenge for dentists. To mimic the natural biomineralization approach for enamel remineralization, the biological process of enamel development proteins, such as amelogenin, was simulated in this study. In this work, carboxymethyl chitosan (CMC) conjugated with alendronate (ALN) was applied to stabilize amorphous calcium phosphate (ACP) to form CMC/ACP nanoparticles. Sodium hypochlorite (NaClO) functioned as the protease which decompose amelogenin in vivo to degrade the CMC-ALN matrix and generate HAP@ACP core-shell nanoparticles. Finally, when guided by 10 mM glycine (Gly), HAP@ACP nanoparticles can arrange orderly and subsequently transform from an amorphous phase to well-ordered rod-like apatite crystals to achieve oriented and ordered biomimetic remineralization on acid-etched enamel surfaces. This biomimetic remineralization process is achieved through the oriented attachment (OA) of nanoparticles based on non-classical crystallization theory. These results indicate that finding and developing analogues of natural proteins such as amelogenin involved in the biomineralization by natural macromolecular polymers and imitating the process of biomineralization would be an effective strategy for enamel remineralization. Furthermore, this method represents a promising method for the management of early caries in minimal invasive dentistry (MID).

  11. Evaluation of enamel by scanning electron microscopy green LED associated to hydrogen peroxide 35% for dental bleaching

    Science.gov (United States)

    Monteiro, Juliana S. C.; de Oliveira, Susana C. P. S.; Zanin, Fátima A. A.; Santos, Gustavo M. P.; Sampaio, Fernando J. P.; Gomes Júnior, Rafael Araújo; Gesteira, Maria F. M.; Vannier-Santos, Marcos A.; Pinheiro, Antônio Luiz B.

    2014-02-01

    Dental bleaching is a frequently requested procedure in clinical dental practice. The literature is contradictory regarding the effects of bleaching agents on both morphology and demineralization of enamel after bleaching. The aim of this study was to analyze by SEM the effect of 35% neutral hydrogen peroxide cured by green LED. Buccal surfaces of 15 pre-molars were sectioned and marked with a central groove to allow experimental and control groups on the same specimen. For SEM, 75 electron micrographs were evaluated by tree observers at 43X, 220X and 1000X. Quantitative analysis for the determination of the surface elemental composition of the samples through X-ray microanalysis by SEM was also performed. The protocol tested neither showed significant changes in mineral composition of the samples nor to dental enamel structure when compared to controls. SEM analysis allowed inferring that there were marked morphological differences between the enamel samples highlighting the need for the use of the same tooth in comparative morphological studies. The tested protocol did not cause morphological damage the enamel surface when compared to their respective controls.

  12. Evaluation of dental enamel caries assessment using Quantitative Light Induced Fluorescence and Optical Coherence Tomography.

    Science.gov (United States)

    Maia, Ana Marly Araújo; de Freitas, Anderson Zanardi; de L Campello, Sergio; Gomes, Anderson Stevens Leônidas; Karlsson, Lena

    2016-06-01

    An in vitro study of morphological alterations between sound dental structure and artificially induced white spot lesions in human teeth, was performed through the loss of fluorescence by Quantitative Light-Induced Fluorescence (QLF) and the alterations of the light attenuation coefficient by Optical Coherence Tomography (OCT). To analyze the OCT images using a commercially available system, a special algorithm was applied, whereas the QLF images were analyzed using the software available in the commercial system employed. When analyzing the sound region against white spot lesions region by QLF, a reduction in the fluorescence intensity was observed, whilst an increase of light attenuation by the OCT system occurred. Comparison of the percentage of alteration between optical properties of sound and artificial enamel caries regions showed that OCT processed images through the attenuation of light enhanced the tooth optical alterations more than fluorescence detected by QLF System. QLF versus OCT imaging of enamel caries: a photonics assessment. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  13. Randomized clinical study of alterations in the color and surface roughness of dental enamel brushed with whitening toothpaste.

    Science.gov (United States)

    de Moraes Rego Roselino, Lourenço; Tirapelli, Camila; de Carvalho Panzeri Pires-de-Souza, Fernanda

    2018-03-30

    This clinical study evaluated the influence of whitening toothpaste on color and surface roughness of dental enamel. Initially, the abrasiveness of the toothpastes used (Sorriso Dentes Brancos [SDB]; Colgate Luminous White and Close up White Now) was tested on 30 (n = 10) plexiglass acrylic plates that were submitted to mechanical tooth brushing totalizing 29,200 cycles. Subsequently, 30 participants were selected, and received a toothbrush and nonwhitening toothpaste (SDB). The participants used these products for 7 days and initial color readouts (Spectrophotometer) and surface roughness of one maxillary central incisors was performed after this period of time. For surface roughness readouts, one replica of the maxillary central incisor was obtained by a polyvinyl siloxane impression material (Express) and polyurethane resin. After baseline measurements, participants were separated into three groups (n = 10), according to the toothpaste used. The participants returned after 7, 30, and 90 days when new color readouts and surface roughness were recorded. The measured values were statistically analyzed (2-way-ANOVA, repeated measures, Tukey, P Whitening toothpastes did not promote significant (P > .05) color alteration and nor increased the surface roughness of the dental enamel in brushing time of the study. The abrasiveness of whitening toothpaste and the brushing trial period did not affect the surface roughness of dental enamel. However, color changes observed on enamel were above the perceptibility and acceptability thresholds reported in the literature. The over-the-counter toothpastes tested had an effect on dental enamel color above the perceptibility and acceptability thresholds but did not change the surface roughness of the teeth. © 2018 Wiley Periodicals, Inc.

  14. Structure and composition of enamel and dentin after thermal treatment or infrared laser irradiation

    International Nuclear Information System (INIS)

    Bachmann, Luciano

    2004-01-01

    The main purpose of this work is to identify the crystallographic structure, optical properties, chemical composition and electron paramagnetic signals that laser irradiation or oven heating produces on the tissue. The thermal treatment was conducted in oven with temperature range below 1000 deg C and the laser irradiation with holmium (Ho:YLF - 2,065 μm) and erbium (Er:YAG - 2,94 μm) laser. The tissue characterization was carried out with X-ray diffraction, scanning electron microscopy, ultraviolet and visible transmission spectroscopy, light microscopy, infrared transmission/reflection spectroscopy and electron paramagnetic resonance. The holmium irradiated enamel (600-800 J/cm 2 ) shows the presence of tetracalcium phosphate that coexists with the natural phase (hydroxyapatite). The irradiated dentin shows only the sharper diffraction peaks of the natural phase. The narrows peaks, observed after irradiation, could be assigned to the dentin crystal growth and impurities elimination. Tissue discoloration is observed after thermal treatment with temperatures above 100 deg C. Heated enamel become white-opaque and the origin is assigned to the water elimination, which promotes higher light scattering by the prismatic structure. On the other hand, heated dentin, with similar temperatures becomes brown. The dentin browning changes with the temperature and shown two peaks, at 375 deg C and 700 deg C. The peak at 375 deg C is assigned to the collagen structure degradation and at 700 deg C to the cyanate formation. The dentin discoloration produced with temperatures below 200 deg C is reversible after the tissue hydration. Both enamel and dentin discoloration are also observed in erbium irradiated tissues. Thermal treatments, heating in oven or laser irradiation, change mainly the organic matrix composition and water present in the tissues. The inorganic matrix is more stable and its radicals are changed, with more predominance, only at temperatures higher than 500 deg

  15. Research on optical properties of dental enamel for early caries diagnostics using a He-Ne laser

    Science.gov (United States)

    Tang, Jing; Liu, Li; Li, Song-zhan

    2008-12-01

    A new and non-invasive method adapted for optical diagnosis of early caries is proposed by researching on the interaction mechanism of laser with dental tissue and relations of remitted light with optical properties of the tissue. This method is based on simultaneous analyses of the following parameters: probing radiation, backscattering and auto-fluorescence. Investigation was performed on 104 dental samples in vitro by using He-Ne laser (λ=632.8nm, 2.0+/-0.1mW) as the probing. Spectrums of all samples were obtained. Characteristic spectrums of dental caries in various stages (intact, initial, moderate and deep) were given. Using the back-reflected light to normalize the intensity of back-scattering and fluorescence, a quantitative diagnosis standard for different stages of caries is proposed. In order to verify the test, comparison research was conducted among artificial caries, morphological damaged enamel, dental calculus and intact tooth. Results show that variations in backscattering characteristic changes in bio-tissue morphological and the quantity of auto-fluorescence is correlated with concentration of anaerobic microflora in hearth of caries lesion. This method poses a high potential of diagnosing various stages of dental caries, and is more reliability to detect early caries, surface damage of health enamel and dental calculus.

  16. The effect of fractional CO2 laser irradiation on remineralization of enamel white spot lesions.

    Science.gov (United States)

    Poosti, Maryam; Ahrari, Farzaneh; Moosavi, Horieh; Najjaran, Hoda

    2014-07-01

    This study investigated the combined effect of fractional CO(2) laser irradiation and fluoride on treatment of enamel caries. Sixty intact premolars were randomly assigned into four groups and then stored in a demineralizing solution to induce white spot lesions. Tooth color was determined at baseline (T1) and after demineralization (T2). Afterwards, the teeth in group 1 remained untreated (control), while group 2 was exposed to an acidulated phosphate fluoride (APF) gel for 4 min. In groups 3 and 4, a fractional CO(2) laser was applied (10 mJ, 200 Hz, 10 s) either before (group 3) or through (group 4) the APF gel. The teeth were then immersed in artificial saliva for 90 days while subjected to daily fluoride mouthrinse and weekly brushing. Color examinations were repeated after topical fluoride application (T3) and 90 days later (T4). Finally, the teeth were sectioned, and microhardness was measured at the enamel surface and at 30 and 60 μ from the surface. In both lased groups, the color change between T1 and T4 stages (∆E(T1-T4)) was significantly lower than those of the other groups (p Laser irradiation followed by fluoride application (group 3) caused a significant increase in surface microhardness compared to APF alone and control groups (p laser before fluoride therapy is suggested for recovering the color and rehardening of demineralized enamel.

  17. [Differential diagnosis of dental enamel focal demineralization and fluorosis by means of spectrophotometry].

    Science.gov (United States)

    Makarova, N E; Vinnichenko, Yu A

    2018-01-01

    The article presents the results of spectrophotometric tooth enamel scanning for differential diagnosis of focal enamel demineralization and fluorosis. Research was conducted in vivo on teeth affected by these diseases. VITA EasyShade spectrophotometer measurements were made on the affected area and on the visually healthy part of enamel. The lightness appeared as the only one differential significant optical characteristics of tooth enamel. Lightness metrics were higher in the case of initial caries than on the healthy part of enamel when these metrics were lower in the case of fluorosis than on the healthy part of enamel.

  18. The impact of stannous, fluoride ions and its combination on enamel pellicle proteome and dental erosion prevention.

    Directory of Open Access Journals (Sweden)

    A A Algarni

    Full Text Available To compare the effects of stannous (Sn and fluoride (F ions and their combination on acquired enamel pellicle (AEP protein composition (proteome experiment, and protection against dental erosion (functional experiment.In the proteome experiment, bovine enamel specimens were incubated in whole saliva supernatant for 24h for AEP formation. They were randomly assigned to 4 groups (n=10, according to the rinse treatment: Sn (800ppm/6.7mM, SnCl2, F (225ppm/13mM, NaF, Sn and F combination (Sn+F and deionized water (DIW, negative control. The specimens were immersed 3× in the test rinses for 2min, 2h apart. Pellicles were collected, digested, and analyzed for protein content using liquid chromatography electrospray ionization tandem mass spectrometry. In the functional experiment, bovine enamel specimens (n=10 were similarly treated for pellicle formation. Then, they were subjected to a five-day erosion cycling model, consisting of 5min erosive challenges (15.6 mM citric acid, pH 2.6, 6×/d and 2min treatment with the rinses containing Sn, F or Sn+F (3×/d. Between the treatments, all specimens were incubated in whole saliva supernatant. Surface loss was determined by profilometry.Our proteome approach on bovine enamel identified 72 proteins that were common to all groups. AEP of enamel treated with Sn+F demonstrated higher abundance for most of the identified proteins than the other groups. The functional experiment showed reduction of enamel surface loss for Sn+F (89%, Sn (67% and F (42% compared to DIW (all significantly different, p<0.05.This study highlighted that anti-erosion rinses (e.g. Sn+F can modify quantitatively and qualitatively the AEP formed on bovine enamel. Moreover, our study demonstrated a combinatory effect that amplified the anti-erosive protection on tooth surface.

  19. Identification of novel candidate genes involved in mineralization of dental enamel by genome-wide transcript profiling.

    Science.gov (United States)

    Lacruz, Rodrigo S; Smith, Charles E; Bringas, Pablo; Chen, Yi-Bu; Smith, Susan M; Snead, Malcolm L; Kurtz, Ira; Hacia, Joseph G; Hubbard, Michael J; Paine, Michael L

    2012-05-01

    The gene repertoire regulating vertebrate biomineralization is poorly understood. Dental enamel, the most highly mineralized tissue in mammals, differs from other calcifying systems in that the formative cells (ameloblasts) lack remodeling activity and largely degrade and resorb the initial extracellular matrix. Enamel mineralization requires that ameloblasts undergo a profound functional switch from matrix-secreting to maturational (calcium transport, protein resorption) roles as mineralization progresses. During the maturation stage, extracellular pH decreases markedly, placing high demands on ameloblasts to regulate acidic environments present around the growing hydroxyapatite crystals. To identify the genetic events driving enamel mineralization, we conducted genome-wide transcript profiling of the developing enamel organ from rat incisors and highlight over 300 genes differentially expressed during maturation. Using multiple bioinformatics analyses, we identified groups of maturation-associated genes whose functions are linked to key mineralization processes including pH regulation, calcium handling, and matrix turnover. Subsequent qPCR and Western blot analyses revealed that a number of solute carrier (SLC) gene family members were up-regulated during maturation, including the novel protein Slc24a4 involved in calcium handling as well as other proteins of similar function (Stim1). By providing the first global overview of the cellular machinery required for enamel maturation, this study provide a strong foundation for improving basic understanding of biomineralization and its practical applications in healthcare. Copyright © 2011 Wiley Periodicals, Inc.

  20. Systematic dental management in head and neck irradiation

    International Nuclear Information System (INIS)

    Horiot, J.C.; Bone, M.C.; Ibrahim, E.

    1981-01-01

    Preservation of teeth has been possible in 528 head and neck patients treated with irradiation at Centre Georges Leclerc, University of Dijon, by careful adherence to precise dental care. Careful initial dental evaluation with appropriate x rays, restoration of oral hygiene, atraumatic extraction technique where indicated, and institution of a program of topical fluoridation has resulted in an overall incidence of less than 3% post-irradiation dental decay and 2% osteoradionecrosis. In a small group of 22 patient who required extraction post-irradiation, precise, strict technique resulted in successful extraction in all but one patient who subsequently developed osteonecrosis. Soft-based dental prostheses were well tolerated in nearly 90% of patients. Adherence to the described principles of dental care will virtually eliminate post-irradiation decay and osteoradionecrosis

  1. [Dental enamel prisms of Mesopithecus pentelicus Wagner, 1839, compared with recent cercopithecids (Primates: Cercopithecidae)].

    Science.gov (United States)

    Dostal, A; Zapfe, H

    1986-01-01

    The dental enamel prisms of Cercopithecidae were examined by scanning electron microscopy. The main task of this study was to show the prism morphology representatives of different genera as well as their comparison with the fossil Mesopithecus pentelicus Wagner, 1839. The method used to show the enamel prisms was to etch the tooth surface with hydrochloric acid. In this way the outlines of the prisms were better contrasted for the descriptive morphology of the prisms than in etching with phosphoric acid. Two types were determined, in accord with the systematic division into subfamilies. In the subfamily Cercopithecinae elongated slender prisms were dominating, some with pointed, others with truncated tops. Most characteristic of this type were Macaca and Cercopithecus. An exception was Papio hamadryas which had broader, rounded prisms. In this way it differed largely from P. anubis whose prisms were short and mostly triangular. A very interesting fact was that very different patterns were found in P. anubis and P. hamadryas, although these two species are regarded as only one species by many authors. The second subfamily, the Colobinae, was characterized by broader prisms with a rounded shape, nearly as long as wide. Exceptions of the 'Colobine type' were at first Colobus with prisms little longer than wide and secondly Nasalis, with mostly parallel sides and truncated tops of the prisms. The prism outlines of Mesopithecus showed the greatest similarity to those of Presbytis which represents the characteristic 'Colobine type'. This fact confirmed the actual systematic position of the fossil Mesopithecus within the subfamily Colobinae. In addition to previously known primitive features of Mesopithecus within the subfamily of Colobinae, we present here a further concrete, common feature with asiatic Colobines.

  2. In Vitro Comparative Study of Two Different Bleaching Agents on Micro-hardness Dental Enamel.

    Science.gov (United States)

    Fatima, Nazish; Ali Abidi, Syed Yawar; Meo, Ashraf Ali

    2016-02-01

    To evaluate the effect of home-use bleaching agent containing 16% Carbamide Peroxide (CP) and in-office bleaching agent containing 38% Hydrogen Peroxide (HP) on enamel micro-hardness. An in vitroexperimental study. Department of Operative Dentistry and Science of Dental Materials at Dr. Ishrat-ul-Ebad Khan Institute of Oral Health Sciences, Dow University of Health Sciences and Material Engineering Department of NED University of Engineering and Technology, Karachi, from July to December 2014. Atotal of 90 enamel slabs from 45 sound human 3rd molar were randomly divided into 3 groups. Each group contained 30 specimens (n=30). Group 1 was kept in artificial saliva at 37°C in incubator during the whole experiment. However, Groups 2 and 3 were treated with power whitening gel and tooth whitening pen respectively. After bleaching session, specimens were thoroughly rinsed with deionized water again for 10 seconds and then stored in artificial saliva at 37°C in incubator. Artificial saliva was changed after every 2 days. The Vickers hardness tester (Wolpert 402 MVD, Germany) was adjusted to a load of 0.1 kg (100 gm) and dwell time of 5 seconds. Three Vickers were performed on each specimen using a hardness tester according to the ISO 6507-3:1998 specification. Micro-hardness measurements were performed before and after bleaching at day 1, 7 and 14. In the control group, the baseline micro-hardness was 181.1 ±9.3 which was reduced after the storage on day 1, 7 and 14 (p = 0.104). In Group 2, baseline micro-hardness was 180.4 ±10.1 which was reduced to 179.79 ±10.0 units after day 1. Whereas, on day 7 and 14, the values of micro-hardness were 179.8 ±10 and 179.7 ±10.29, respectively (p=0.091). Furthermore, the baseline micro-hardness in Group 3 was 174.0 ±22.9 units which was reduced to 173 ±23 on day 1, 170 ±30 on day 7 and 173 ±23 on day 14 (p = 0.256). The statistically insignificant difference was found among micro-hardness values of different bleaching

  3. In Vitro Comparative Study of Two Different Bleaching Agents on Micro-hardness Dental Enamel

    International Nuclear Information System (INIS)

    Fatima, N.; Abidi, S. Y. A.; Meo, A. A.

    2016-01-01

    Objective: To evaluate the effect of home-use bleaching agent containing 16 percentage Carbamide Peroxide (CP) and in-office bleaching agent containing 38 percentage Hydrogen Peroxide (HP) on enamel micro-hardness. Study Design: An in vitro experimental study. Place and Duration of Study: Department of Operative Dentistry and Science of Dental Materials at Dr. Ishrat-ul-Ebad Khan Institute of Oral Health Sciences, Dow University of Health Sciences and Material Engineering Department of NED University of Engineering and Technology, Karachi, from July to December 2014. Methodology: A total of 90 enamel slabs from 45 sound human 3rd molar were randomly divided into 3 groups. Each group contained 30 specimens (n=30). Group 1 was kept in artificial saliva at 37 Degree C in incubator during the whole experiment. However, Groups 2 and 3 were treated with power whitening gel and tooth whitening pen respectively. After bleaching session, specimens were thoroughly rinsed with deionized water again for 10 seconds and then stored in artificial saliva at 37 Degree C in incubator. Artificial saliva was changed after every 2 days. The Vickers hardness tester (Wolpert 402 MVD, Germany) was adjusted to a load of 0.1 kg (100 gm) and dwell time of 5 seconds. Three Vickers were performed on each specimen using a hardness tester according to the ISO 6507-3:1998 specification. Micro-hardness measurements were performed before and after bleaching at day 1, 7 and 14. Results: In the control group, the baseline micro-hardness was 181.1 ± 9.3 which was reduced after the storage on day 1, 7 and 14 (p = 0.104). In Group 2, baseline micro-hardness was 180.4 ±10.1 which was reduced to 179.79 ± 10.0 units after day 1. Whereas, on day 7 and 14, the values of micro-hardness were 179.8 ±10 and 179.7 ±10.29, respectively (p=0.091). Furthermore, the baseline micro-hardness in Group 3 was 174.0 ±22.9 units which was reduced to 173 ± 23 on day 1, 170 ±30 on day 7 and 173 ± 23 on day 14 (p = 0

  4. Dental care for the irradiated patient

    International Nuclear Information System (INIS)

    Breytenbach, H.S.

    1979-01-01

    Many treatment sequelae are encountered when treating head and neck cancer patients by means of ionizing radiation therapy. In many cases, these sequelae are compounded by various nutritional and other medical disorders. Many sequelae can eventually result in severe complications of the jaws and teeth. The radiotherapist needs to utilize the help of the dentist (as well as the surgeon) to prevent many of these complications from occurring, to maintain and manage those that do occur, and to contribute to the overall care of head and neck cancer patients. It was thought for many years that problems of the jaws and teeth, such as osteoradionecrosis and post-irradiation caries of the teeth, were an end product of aggressive radiotherapy. Many of these complications can now be prevented. It should be borne in mind that changes that do occur start approximately 2 months after initiation of irradiation, although it sometimes takes a long time to observe the changes. The priorities along which the objectives of dental treatment should be directed, are discussed in this article

  5. Dental care for the irradiated patient

    Energy Technology Data Exchange (ETDEWEB)

    Breytenbach, H S [University of the Western Cape, Bellville (South Africa). Stomatology Unit

    1979-07-01

    Many treatment sequelae are encountered when treating head and neck cancer patients by means of ionizing radiation therapy. In many cases, these sequelae are compounded by various nutritional and other medical disorders. Many sequelae can eventually result in severe complications of the jaws and teeth. The radiotherapist needs to utilize the help of the dentist (as well as the surgeon) to prevent many of these complications from occurring, to maintain and manage those that do occur, and to contribute to the overall care of head and neck cancer patients. It was thought for many years that problems of the jaws and teeth, such as osteoradionecrosis and post-irradiation caries of the teeth, were an end product of aggressive radiotherapy. Many of these complications can now be prevented. It should be borne in mind that changes that do occur start approximately 2 months after initiation of irradiation, although it sometimes takes a long time to observe the changes. The priorities along which the objectives of dental treatment should be directed, are discussed in this article.

  6. Matching the optical properties of direct esthetic dental restorative materials to those of human enamel and dentin

    Science.gov (United States)

    Ragain, James Carlton, Jr.

    One of the goals of the restorative dentist is to restore the appearance of the natural dentition. Clinical matching of teeth and restorative materials are seldom accurate and shade selection techniques are subjective. The first specific aim of this research was to characterize the optical absorption and scattering that occurs within enamel, dentin, and composite resin and compomer restorative materials and to relate those phenomena to translucency and color. The second aim was to evaluate small color differences among composite restorative materials which would be detectable by humans. The last aim was to lay the foundation for developing an improved model of specifying layers of dental restorative materials in order to match the translucency and color to those of human enamel. The Kubelka-Munk theory was validated for enamel, dentin, and the restorative materials. These tissues and materials were then characterized in terms of their color parameters. Tooth cores were also characterized in terms of color space parameters. Human subjects were evaluated for their abilities to discriminate small color differences in the dental composite resin materials. The following conclusions were derived from this study: (1) Kubelka-Munk theory accurately predicts the diffuse reflectance spectra of enamel, dentin, and the direct esthetic dental restorative materials studied. (2) Scattering and absorption coefficients of the dental tissues and esthetic restorative materials can be directly calculated from diffuse reflectance measurements of a uniformly thick slab of tissue/material using black and white backings and the appropriate refractive index. (3) For tooth cores, there is a positive correlation between L* and b* and a negative correlation between L* and a*. (4) The range of translucency parameters for the restorative materials studied does not match those of enamel and dentin. (5) None of the shades of the dental composite resin restorative materials studied fit into the

  7. Influence of multi-wavelength laser irradiation of enamel and dentin surfaces at 0.355, 2.94, and 9.4 μm on surface morphology, permeability, and acid resistance.

    Science.gov (United States)

    Chang, Nai-Yuan N; Jew, Jamison M; Simon, Jacob C; Chen, Kenneth H; Lee, Robert C; Fried, William A; Cho, Jinny; Darling, Cynthia L; Fried, Daniel

    2017-12-01

    Ultraviolet (UV) and infrared (IR) lasers can be used to specifically target protein, water, and mineral, respectively, in dental hard tissues to produce varying changes in surface morphology, permeability, reflectivity, and acid resistance. The purpose of this study was to explore the influence of laser irradiation and topical fluoride application on the surface morphology, permeability, reflectivity, and acid resistance of enamel and dentin to shed light on the mechanism of interaction and develop more effective treatments. Twelve bovine enamel surfaces and twelve bovine dentin surfaces were irradiated with various combinations of lasers operating at 0.355 (Freq.-tripled Nd:YAG (UV) laser), 2.94 (Er:YAG laser), and 9.4 μm (CO 2 laser), and surfaces were exposed to an acidulated phosphate fluoride gel and an acid challenge. Changes in the surface morphology, acid resistance, and permeability were measured using digital microscopy, polarized light microscopy, near-IR reflectance, fluorescence, polarization sensitive-optical coherence tomography (PS-OCT), and surface dehydration rate measurements. Different laser treatments dramatically influenced the surface morphology and permeability of both enamel and dentin. CO 2 laser irradiation melted tooth surfaces. Er:YAG and UV lasers, while not melting tooth surfaces, showed markedly different surface roughness. Er:YAG irradiation led to significantly rougher enamel and dentin surfaces and led to higher permeability. There were significant differences in acid resistance among the various treatment groups. Surface dehydration measurements showed significant changes in permeability after laser treatments, application of fluoride and after exposure to demineralization. CO 2 laser irradiation was most effective in inhibiting demineralization on enamel while topical fluoride was most effective for dentin surfaces. Lasers Surg. Med. 49:913-927, 2017. © 2017 Wiley Periodicals, Inc. © 2017 Wiley Periodicals, Inc.

  8. Raman spectroscopy analysis of dental enamel treated with whitening product - Influence of saliva in the remineralization

    Science.gov (United States)

    Silveira, J.; Coutinho, S.; Marques, D.; Castro, J.; Mata, A.; Carvalho, M. L.; Pessanha, S.

    2018-06-01

    In this work we present the analysis of dental enamel treated with an over-the-counter whitening product, bought in e-commerce at a very low cost, used without medical supervision in an abusive manner, in order to evaluate its demineralization action. Moreover, we studied the influence of renewal or non-renewal of saliva solution in which the specimens were stored throughout the study. The Degree of Demineralization was determined through the evaluation of the PO43- symmetric stretching band ( 959 cm-1) in Raman spectra of the specimens in different days during the course of the study. Results showed that a maximum of demineralization occurred between days 27 and 34 of application. Titration of the whitening product revealed a content of hydrogen peroxide 170-fold higher than what is allowed in Europe, according with legislation. Despite this extreme concentration of hydrogen peroxide, the demineralization was not as great as could be expected suggesting an important role of the pH of the solution in this demineralization mechanism.

  9. Changes in surface morphology of enamel after Er:YAG laser irradiation

    Science.gov (United States)

    Rechmann, Peter; Goldin, Dan S.; Hennig, Thomas

    1998-04-01

    Aim of the study was to investigate the surface and subsurface structure of enamel after irradiation with an Er:YAG laser (wavelength 2.94 micrometer, pulse duration 250 - 500 microseconds, free running, beam profile close to tophead, focus diameter 600 micrometer, focus distance 13 mm, different power settings, air-water spray 2 ml/min; KAVO Key Laser 1242, Kavo Biberach, Germany). The surface of more than 40 freshly extracted wisdom teeth were irradiated using a standardized application protocol (pulse repetition rate 4 and 6 Hz, moving speed of the irradiation table 2 mm/sec and 3 mm/sec, respectively). On each surface between 3 and 5 tracks were irradiated at different laser energies (60 - 500 mJ/pulse) while each track was irradiated between one and ten times respectively. For the scanning electron microscope investigation teeth were dried in alcohol and sputtered with gold. For light microscopic examinations following laser impact, samples were fixed in formaldehyde, dried in alcohol and embedded in acrylic resin. Investigations revealed that at subsurface level cracks can not be observed even at application of highest energies. Borders of the irradiated tracks seem to be sharp while melted areas of different sizes are observed on the bottom of the tracks depending on applied energy. Small microcracks can be seen on the surface of these melted areas.

  10. Influence of a pulsed CO2 laser operating at 9.4 μm on the surface morphology, reflectivity, and acid resistance of dental enamel below the threshold for melting

    Science.gov (United States)

    Kim, Jin Wan; Lee, Raymond; Chan, Kenneth H.; Jew, Jamison M.; Fried, Daniel

    2017-02-01

    Below the threshold for laser ablation, the mineral phase of enamel is converted into a purer phase hydroxyapatite with increased acid resistance. Studies suggest the possibility of achieving the conversion without visible surface alteration. In this study, changes in the surface morphology, reflectivity, and acid resistance were monitored with varying irradiation intensity. Bovine enamel specimens were irradiated using a CO2 laser operating at 9.4 μm with a Gaussian spatial beam profile-1.6 to 3.1 mm in diameter. After laser treatment, samples were subjected to demineralization to simulate the acidic intraoral conditions of dental decay. The resulting demineralization and erosion were assessed using polarization-sensitive optical coherence tomography, three-dimensional digital microscopy, and polarized light microscopy. Distinct changes in the surface morphology and the degree of inhibition were found within the laser-treated area in accordance with the laser intensity profile. Subtle visual changes were noted below the melting point for enamel that appear to correspond to thresholds for denaturation of the organic phase and thermal decomposition of the mineral phase. There was significant protection from laser irradiation in areas in which the reflectivity was not increased significantly, suggesting that aesthetically sensitive areas of the tooth can be treated for caries prevention.

  11. Application of quantitative light-induced fluorescence to determine the depth of demineralization of dental fluorosis in enamel microabrasion: a case report

    Directory of Open Access Journals (Sweden)

    Tae-Young Park

    2016-08-01

    Full Text Available Enamel microabrasion has become accepted as a conservative, nonrestorative method of removing intrinsic and superficial dysmineralization defects from dental fluorosis, restoring esthetics with minimal loss of enamel. However, it can be difficult to determine if restoration is necessary in dental fluorosis, because the lesion depth is often not easily recognized. This case report presents a method for analysis of enamel hypoplasia that uses quantitative light-induced fluorescence (QLF followed by a combination of enamel microabrasion with carbamide peroxide home bleaching. We describe the utility of QLF when selecting a conservative treatment plan and confirming treatment efficacy. In this case, the treatment plan was based on QLF analysis, and the selected combination treatment of microabrasion and bleaching had good results.

  12. Irradiation hazards and safety standards for patients in dental radiography

    Energy Technology Data Exchange (ETDEWEB)

    Williamson, B D.P.

    1975-07-01

    The historical developments which have led to a reduction in the hazards or potential hazards to patients in dental radiography are reviewed. Based on a simple risk estimate, the safety of present-day techniques employed in routine dental radiography is assessed. Also included in the review is a description of techniques used and results obtained from the National Radiation Laboratory's (NRL) surveillance programme of patients' exposure to irradiation in dental radiography. The possibilities of and need for achieving further reductions of irradiation are discussed.

  13. Primary experimental studies on mid-infrared FEL irradiation on dental substances at BFEL

    CERN Document Server

    Biao, Z J; Gao Xue Ju; He Wei; Huang Yu Ying; Li Yong Gui; LiuNianQing; Wang Min Kai; Wu Gan; Yan Xue Pin; Zhang Guo Qing

    2001-01-01

    A free electron laser (FEL) with its characteristics of wide wavelength tunability, ultrashort pulse time structure, and high peak power density is predominantly superior to all other conventional lasers in applications. Several experimental studies on mid-infrared FEL irradiation on dental enamel and dentine were performed at the Beijing FEL. Experimental aims were to investigate changes in the hardness, ratios of P to Ca and Cs before and after irradiation on samples with a characteristic absorption wavelength of 9.66 mu m, in the colors of these sample surfaces after irradiation with different wavelengths around the peak wavelength. The time dependence of temperature of the dentine sample was measured with its ps pulse effects compared to that with a continuous CO sub 2 laser. FTIR absorption spectra in the range of 2.5-15.4 mu m for samples of these hard dental substances and pure hydroxyapatite were first examined to decide their chemical components and absorption maximums. Primary experimental results w...

  14. Shear bond strength and SEM morphology evaluation of different dental adhesives to enamel prepared with ER:YAG laser

    Directory of Open Access Journals (Sweden)

    Patrícia T Pires

    2013-01-01

    Full Text Available Context: Early observations of enamel surfaces prepared by erbium lasers motivated clinicians to use laser as an alternative to chemical etching. Aims: Evaluate shear bond strength (SBS values of different dental adhesives on Erbium:Yttrium Aluminum Garnet (Er:YAG laser prepared enamel and to evaluate possible etching patterns correlations between dental adhesives and SBS values. Subjects and Methods: One hundred bovine incisors were randomly assigned to SBS tests on enamel (n = 15 and to enamel morphology analysis ( n = 5 after Er:YAG laser preparation as follows: Group I - 37% phosphoric acid (PA+ ExciTE® ; Group II - ExciTE® ; Group III - AdheSE® self-etching; Group IV - FuturaBond® no-rinse. NR; Group V - Xeno® V. Teeth were treated with the adhesive systems and subjected to thermal cycling. SBS were performed in a universal testing machine at 5 mm/min. Statistical Analysis Used: One-way ANOVA and post-hoc tests (p < 0.05. For the morphology evaluation, specimens were immersed in Ethylenediamine tetraacetic acid (EDTA and the etching pattern analyzed under Scanning Electron Microscope (SEM. Results: Mean bond strengths were Group I - 47.17 ± 1.61 MPa (type I etching pattern; Group II - 32.56 ± 1.64 MPa, Group III - 29.10 ± 1.34 MPa, Group IV - 23.32 ± 1.53 MPa (type III etching pattern; Group V - 24.43 MPa ± 1.55 (type II etching pattern. Conclusions: Different adhesive systems yielded significantly different SBSs. Acid etching significantly increased the adhesion in laser treated enamel. No differences in SBS values were obtained between AdheSE® and ExciTE® without condition with PA. FuturaBond® NR and Xeno® V showed similar SBS, which was lower in comparison to the others adhesives. No correlation between enamel surface morphology and SBS values was observed, except when PA was used.

  15. Effect of tooth bleaching agents on protein content and mechanical properties of dental enamel.

    Science.gov (United States)

    Elfallah, Hunida M; Bertassoni, Luiz E; Charadram, Nattida; Rathsam, Catherine; Swain, Michael V

    2015-07-01

    This study investigated the effect of two bleaching agents, 16% carbamide peroxide (CP) and 35% hydrogen peroxide (HP), on the mechanical properties and protein content of human enamel from freshly extracted teeth. The protein components of control and treated enamel were extracted and examined on sodium dodecyl sulfate polyacrylamide gel electrophoresis (SDS-PAGE). Marked reduction of the protein matrix and random fragmentation of the enamel proteins after bleaching treatments was found. The mechanical properties were analyzed with Vickers indentations to characterize fracture toughness, and nanoindentation to establish enamel hardness, elastic modulus and creep deformation. Results indicate that the hardness and elastic modulus of enamel were significantly reduced after treatment with CP and HP. After bleaching, the creep deformation at maximum load increased and the recovery upon unloading reduced. Crack lengths of CP and HP treated enamel were increased, while fracture toughness decreased. Additionally, the microstructures of fractured and indented samples were examined with field emission gun scanning electron microscopy (FEG-SEM) showing distinct differences in the fracture surface morphology between pre- and post-bleached enamel. In conclusion, tooth bleaching agents can produce detrimental effects on the mechanical properties of enamel, possibly as a consequence of damaging or denaturing of its protein components. Copyright © 2015 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  16. Micro-structural integrity of dental enamel subjected to two tooth whitening regimes.

    Science.gov (United States)

    Tanaka, Reina; Shibata, Yo; Manabe, Atsufumi; Miyazaki, Takashi

    2010-04-01

    Colour modification of tooth enamel has proven successful, but it is unclear how various bleaching applications affect micro-structural integrity of the whitened enamel. To investigate the internal structural integrity of human intact tooth enamel with the application of two commonly used whitening regimes (in-office power bleaching with 35% hydrogen peroxide and home bleaching with 10% carbamide peroxide), evaluations were performed on teeth of identical colour classification. After the bleaching applications, the enamel mineral density was quantified and visualised with micro-computed tomography. The micro-structural differences between the whitened tooth enamel samples were distinctive, though the colour parameter changes within the samples were equivalent. Home bleaching achieved colour modification by demineralisation, whereas in-office bleaching depended on redistribution of the minerals after treatment and subsequent enhanced mineralisation.

  17. Developmental enamel and anatomical tooth defects in dogs – Experience from veterinary dental referral practice and review of the literature

    Directory of Open Access Journals (Sweden)

    Sonja Catharina Boy

    2016-02-01

    Full Text Available Developmental tooth abnormalities in dogs are uncommon in general veterinary practice but understanding thereof is important for optimal management in order to maintain gnathic function through conservation of the dentition. The purpose of this review is to discuss abnormalities of enamel structure and macroscopic tooth anatomy in dogs encountered in veterinary dental referral practice in South Africa and the United Kingdom. The basis of the pathogenesis, resultant clinical appearance and the management principles of each anomaly will be considered. Future research should aim to provide a detailed individual tooth mineralization schedule for dogs.

  18. Effects of enamel fluorosis and dental caries on quality of life.

    Science.gov (United States)

    Onoriobe, U; Rozier, R G; Cantrell, J; King, R S

    2014-10-01

    The objectives of this study were to determine the impact of enamel fluorosis and dental caries on oral health-related quality of life (OHRQoL) in North Carolina schoolchildren and their families. Students (n = 7,686) enrolled in 398 classrooms in grades K-12 were recruited for a onetime survey. Parents of students in grades K-3 and 4-12 completed the Early Childhood Oral Health Impact Scale (ECOHIS) and Family Impact Scale (FIS), respectively. Students in grades 4-12 completed the Child Perceptions Questionnaire (CPQ8-10 in grades 4-5; CPQ11-14 in grades 6-12). All students were examined for fluorosis (Dean's index) and caries experience (d2-3fs or D2-3MFS indices). OHRQoL scores (sum response codes) were analyzed for their association with fluorosis categories and sum of d2-3fs and D2-3MFS according to ordinary least squares regression with SAS procedures for multiple imputation and analysis of complex survey data. Differences in OHRQoL scores were evaluated against statistical and minimal important difference (MID) thresholds. Of 5,484 examined students, 71.8% had no fluorosis; 24.4%, questionable to very mild fluorosis; and 3.7%, mild, moderate, or severe fluorosis. Caries categories were as follows: none (43.1%), low (28.6%), and moderate to high (28.2%). No associations between fluorosis and any OHRQoL scales met statistical or MID thresholds. The difference (5.8 points) in unadjusted mean ECOHIS scores for the no-caries and moderate-to-high caries groups exceeded the MID estimate (2.7 points) for that scale. The difference in mean FIS scores (1.5 points) for the no-caries and moderate-to-high groups exceeded the MID value (1.2 points). The sum of d2-3fs and D2-3MFS scores was positively associated with CPQ11-14 (B = 0.240, p caries experience negatively affects OHRQoL, while fluorosis has little impact. © International & American Associations for Dental Research.

  19. [In vivo retention of KOH soluble and firmly bound fluoride in demineralized dental enamel].

    Science.gov (United States)

    Hellwig, E; Klimek, J; Albert, G

    1989-03-01

    Cylindrical enamel blocks with initial carious lesions were treated for one hour with Duraphat or Fluor-Protector. After removal of the fluoride varnishes the enamel blocks were kept in the mouths of 3 probands for 5 days. Plaque was allowed to accumulate on half of the enamel cylinders, while the other half was kept clean. Part of the enamel cylinders were retained as fluoridated controls. Compared with Duraphat the application of Fluor-Protector resulted in a significantly higher uptake of KOH soluble and firmly bound fluoride. During the 5 days of the experiment the amount of KOH soluble fluorides decreased in both groups. In the presence of plaque the fluoride loss was higher. The amount of firmly bound fluoride increased both in the plaque covered and in the clean enamel. The durable cariostatic effect of fluoridated varnishes seems to be due to the slow dissolution of Ca F2-like precipitates on the enamel surface and the concomitant fluoride uptake in the underlying demineralized enamel.

  20. [Evaluation of shear bond strengths of self-etching and total-etching dental adhesives to enamel and dentin].

    Science.gov (United States)

    Yu, Ling; Liu, Jing-Ming; Wang, Xiao-Yan; Gao, Xue-Jun

    2009-03-01

    To evaluate the shear bond strengths of four dental adhesives in vitro. The facial surfaces of 20 human maxillary incisors were prepared to expose fresh enamel and randomly divided into four groups, in each group 5 teeth were bonded with one adhesives: group A (Clearfil Protect Bond, self-etching two steps), group B (Adper( Prompt, self-etching one step), group C (SwissTEC SL Bond, total-etching two steps), group D (Single Bond, total-etching two steps). Shear bond strengths were determined using an universal testing machine after being stored in distilled water for 24 h at 37 degrees C. The bond strengths to enamel and dentin were (25.33 +/- 2.84) and (26.07 +/- 5.56) MPa in group A, (17.08 +/- 5.13) and (17.93 +/- 4.70) MPa in group B, (33.14 +/- 6.05) and (41.92 +/- 6.25) MPa in group C, (22.51 +/- 6.25) and (21.45 +/- 7.34) MPa in group D. Group C showed the highest and group B the lowest shear bond strength to enamel and dentin among the four groups. The two-step self-etching adhesive showed comparable shear bond strength to some of the total-etching adhesives and higher shear bond strength than one-step self-etching adhesive.

  1. ESR dosimetry below 1 Gy, in X-ray irradiated tooth enamel

    International Nuclear Information System (INIS)

    Fainstein, Carlos; Winkler, Elin

    2000-01-01

    Tooth enamel, extracted from molars, was irradiated with 66 keV X-rays, with doses up to 1 Gy. The preparation of the powder samples is described, as well as the protocol for the acquisition and processing of the spectra. The radiation induced paramagnetism is measured, at room temperature, by ESR Spectroscopy. The ESR spectra is well described considering two paramagnetic species, with magnetic moments (in units of Bohr magneton) g=2,0041, and g 1 =2,0018, g 2 =1,9972. The ESR data (peak-to-peak amplitude per mg, hpp/mg, vs dose D), for doses 0 Gy 2 =0,996) with the linear expression: [hpp/mg] = -0,2(0,4)+14,9(0,5). D [Gy]. The result supports the growing confidence in the use of this material, and method, in Retrospective Dosimetry. (author)

  2. ESR Dosimetry Below 1 Gy, in X-Ray Irradiated Tooth Enamel

    International Nuclear Information System (INIS)

    Fainstein, Carlos; Winkler, E; Dubner, D; Gisone, P; Perez, M.R; Saravi, M; Alvarez, P; Davila, F

    2000-01-01

    Tooth enamel, extracted from molars, was irradiated with 66keV X-rays, with doses up to 1Gy.The preparation of the powder samples is described, as well as the protocol for the acquisition and processing of the spectra.The radiation induced paramagnetism is measured, at room temperature, by ESR Spectroscopy.The ESR spectra is well described considering two paramagnetic species, with magnetic moments (in units of Bohr magnetons) g=2,0041, and g1=2,0018, g2=1,9972.The ESR data (peak-to-peak amplitude per mg, hpp/mg, vs dose D), for doses 0Gy 2 =0,996) with the linear expression: [hpp/mg] = -0,2( 0,4)+14,9(0,5). D [Gy].The result supports the growing confidence in the use of this material, and method, in Retrospective Dosimetry

  3. Sub-10-micrometer toughening and crack tip toughness of dental enamel

    OpenAIRE

    Ang, Siang Fung; Schulz, Anja; Pacher Fernandes, Rodrigo; Schneider, Gerold A.

    2011-01-01

    In previous studies, enamel showed indications to occlude small cracks in-vivo and exhibited R-curve behaviors for bigger cracks ex-vivo. This study quantifies the crack tip toughness (KI0, KIII0), the crack closure stress and the cohesive zone size at the crack tip of enamel and investigates the toughening mechanisms near the crack tip down to the length scale of a single enamel crystallite. The crack-opening-displacement (COD) profile of cracks induced by Vickers indents on mature bovine en...

  4. FT-Raman spectroscopic analysis of Nd:YAG and Er,Cr:YSGG laser irradiated enamel for preventive purposes

    Science.gov (United States)

    Ana, P. A.; Kauffmann, C. M. F.; Bachmann, L.; Soares, L. E. S.; Martin, A. A.; Gomes, A. S. L.; Zezell, D. M.

    2014-03-01

    This study evaluated the effect of combining laser irradiation with fluoride on an enamel microstructure and demineralization by FT-Raman spectroscopy (FTRS). Eighty human enamel slabs were divided into eight groups: (G1) untreated; (G2) acidulated phosphate fluoride application (APF—1.23% F- for 4 min) (G3) Nd:YAG irradiation (84.9 J cm-2, 60 mJ/pulse) (G4) Nd:YAG + APF; (G5) APF + Nd:YAG; (G6) Er,Cr:YSGG irradiation (2.8 J cm-2, 12.5 mJ/pulse) (G7) Er,Cr:YSGG + APF; and (G8) APF + Er,Cr:YSGG. After treatment, the samples were submitted to a ten-day pH-cycling model. Chemical changes were determined on the slabs before and after treatment, and also after pH-cycling, by FTRS in the range 400-4000 cm-1. The inorganic bands at 440, 590, 870, 960, 1100 cm-1, and the organic bands at 1270, 1450, 1670, 2945 cm-1 were considered. Demineralization promoted reduction in organic contents; Nd:YAG laser irradiation promoted loss of carbonate and organic content, while Er,Cr:YSGG did not produce significant changes in the relative band intensities of organic and inorganic contents of the enamel. In lased samples, no effects caused by pH-cycling on enamel were observed. In conclusion, laser treatment and its association with fluoride can somehow interfere with the demineralization dynamics, reducing its effects over the enamel.

  5. FT-Raman spectroscopic analysis of Nd:YAG and Er,Cr:YSGG laser irradiated enamel for preventive purposes

    International Nuclear Information System (INIS)

    Ana, P A; Kauffmann, C M F; Gomes, A S L; Bachmann, L; Soares, L E S; Martin, A A; Zezell, D M

    2014-01-01

    This study evaluated the effect of combining laser irradiation with fluoride on an enamel microstructure and demineralization by FT-Raman spectroscopy (FTRS). Eighty human enamel slabs were divided into eight groups: (G1) untreated; (G2) acidulated phosphate fluoride application (APF—1.23% F − for 4 min); (G3) Nd:YAG irradiation (84.9 J cm −2 , 60 mJ/pulse); (G4) Nd:YAG + APF; (G5) APF + Nd:YAG; (G6) Er,Cr:YSGG irradiation (2.8 J cm −2 , 12.5 mJ/pulse); (G7) Er,Cr:YSGG + APF; and (G8) APF + Er,Cr:YSGG. After treatment, the samples were submitted to a ten-day pH-cycling model. Chemical changes were determined on the slabs before and after treatment, and also after pH-cycling, by FTRS in the range 400−4000 cm −1 . The inorganic bands at 440, 590, 870, 960, 1100 cm −1 , and the organic bands at 1270, 1450, 1670, 2945 cm −1 were considered. Demineralization promoted reduction in organic contents; Nd:YAG laser irradiation promoted loss of carbonate and organic content, while Er,Cr:YSGG did not produce significant changes in the relative band intensities of organic and inorganic contents of the enamel. In lased samples, no effects caused by pH-cycling on enamel were observed. In conclusion, laser treatment and its association with fluoride can somehow interfere with the demineralization dynamics, reducing its effects over the enamel. (paper)

  6. Amelogenin and Enamel Biomimetics

    Science.gov (United States)

    Ruan, Qichao; Moradian-Oldak, Janet

    2015-01-01

    Mature tooth enamel is acellular and does not regenerate itself. Developing technologies that rebuild tooth enamel and preserve tooth structure is therefore of great interest. Considering the importance of amelogenin protein in dental enamel formation, its ability to control apatite mineralization in vitro, and its potential to be applied in fabrication of future bio-inspired dental material this review focuses on two major subjects: amelogenin and enamel biomimetics. We review the most recent findings on amelogenin secondary and tertiary structural properties with a focus on its interactions with different targets including other enamel proteins, apatite mineral, and phospholipids. Following a brief overview of enamel hierarchical structure and its mechanical properties we will present the state-of-the-art strategies in the biomimetic reconstruction of human enamel. PMID:26251723

  7. Study of the arrangement of crystallites in γ-irradiated human enamel by electron paramagnetic resonance

    International Nuclear Information System (INIS)

    Cevc, P.; Schara, M.; Ravnik, C.; Skaleric, U.

    1976-01-01

    The arrangement of tooth enamel microcrystals has been studied on CO 3 3- bound electrons by paramagnetic resonance. It was found that noncarious human maxillary central incisors have a greater degree of alignment of tooth enamel microcrystals than the carious ones. The outermost surface layer of enamel showed a greater crystallite degree of alignment than other parts

  8. Effects of fluoride and epigallocatechin gallate on soft-drink-induced dental erosion of enamel and root dentin.

    Science.gov (United States)

    Wang, Yin-Lin; Chang, Hao-Hueng; Chiang, Yu-Chih; Lu, Yu-Chen; Lin, Chun-Pin

    2018-04-01

    Fluoride and epigallocatechin gallate (EGCG) have been proven to prevent dental caries. The purpose of this study was to evaluate the effects of fluoride and EGCG on soft-drink-induced dental erosion in vitro. Forty enamel and dentin specimens were prepared from extracted human teeth. The specimens were divided into 4 groups and treated separately with distilled water (as control), 0.5 M sodium fluoride (NF), 400 μM EGCG (EG), and a solution containing 0.5 M NaF and 400 μM EGCG (FG). Cyclic erosive treatment was performed according to the experimental procedures. The specimens were analyzed using laser scanning confocal microscopy, scanning electron microscopy, and a microhardness tester. The data were analyzed using ANOVA and Bonferroni's post hoc test. The significance level was set at 5%. The amount of substance loss was lower in the NF and EG groups than in the control group (p erosion-caused substance loss was more pronounced in the dentin than in the enamel specimens. Surface microhardness loss was lower in the NF and EG groups than in the control group (p erosion compared with the control group. Fluoride and EGCG may interfere with each other. The mechanisms of the anti-erosive effect need to be explored in the future. Copyright © 2018. Published by Elsevier B.V.

  9. Dental enamel defects predict adolescent health indicators: A cohort study among the Tsimane' of Bolivia.

    Science.gov (United States)

    Masterson, Erin E; Fitzpatrick, Annette L; Enquobahrie, Daniel A; Mancl, Lloyd A; Eisenberg, Dan T A; Conde, Esther; Hujoel, Philippe P

    2018-05-01

    Bioarchaeological findings have linked defective enamel formation in preadulthood with adult mortality. We investigated how defective enamel formation in infancy and childhood is associated with risk factors for adult morbidity and mortality in adolescents. This cohort study of 349 Amerindian adolescents (10-17 years of age) related extent of enamel defects on the central maxillary incisors (none, less than 1/3, 1/3 to 2/3, more than 2/3) to adolescent anthropometrics (height, weight) and biomarkers (hemoglobin, glycated hemoglobin, white blood cell count, and blood pressure). Risk differences and 95% confidence intervals were estimated using multiple linear regression. Enamel defects and stunted growth were compared in their ability to predict adolescent health indicators using log-binomial regression and receiver operating characteristics (ROCs). Greater extent of defective enamel formation on the tooth surface was associated with shorter height (-1.35 cm, 95% CI: -2.17, -0.53), lower weight (-0.98 kg, 95% CI: -1.70, -0.26), lower hemoglobin (-0.36 g/dL, 95% CI: -0.59, -0.13), lower glycated hemoglobin (-0.04 %A 1c , 95% CI: -0.08, -0.00008), and higher white blood cell count (0.74 10 9 /L, 95% CI: 0.35, 1.14) in adolescence. Extent of enamel defects and stunted growth independently performed similarly as risk factors for adverse adolescent outcomes, including anemia, prediabetes/type II diabetes, elevated WBC count, prehypertension/hypertension, and metabolic health. Defective enamel formation in infancy and childhood predicted adolescent health outcomes and may be primarily associated with infection. Extent of enamel defects and stunted growth may be equally predictive of adverse adolescent health outcomes. © 2018 Wiley Periodicals, Inc.

  10. Type 1 diabetes mellitus effects on dental enamel formation revealed by microscopy and microanalysis.

    Science.gov (United States)

    Silva, Bruna Larissa Lago; Medeiros, Danila Lima; Soares, Ana Prates; Line, Sérgio Roberto Peres; Pinto, Maria das Graças Farias; Soares, Telma de Jesus; do Espírito Santo, Alexandre Ribeiro

    2018-03-01

    Type 1 diabetes mellitus (T1DM) largely affects children, occurring therefore at the same period of deciduous and permanent teeth development. The aim of this work was to investigate birefringence and morphology of the secretory stage enamel organic extracellular matrix (EOECM), and structural and mechanical features of mature enamel from T1DM rats. Adult Wistar rats were maintained alive for a period of 56 days after the induction of experimental T1DM with a single dose of streptozotocin (60 mg/kg). After proper euthanasia of the animals, fixed upper incisors were accurately processed, and secretory stage EOECM and mature enamel were analyzed by transmitted polarizing and bright field light microscopies (TPLM and BFLM), energy-dispersive x-ray (EDX) analysis, scanning electron microscopy (SEM), and microhardness testing. Bright field light microscopies and transmitted polarizing light microscopies showed slight morphological changes in the secretory stage EOECM from diabetic rats, which also did not exhibit statistically significant alterations in birefringence brightness when compared to control animals (P > .05). EDX analysis showed that T1DM induced statistically significant little increases in the amount of calcium and phosphorus in outer mature enamel (P  .05). T1DM also caused important ultrastructural alterations in mature enamel as revealed by SEM and induced a statistically significant reduction of about 13.67% in its microhardness at 80 μm from dentin-enamel junction (P enamel development, leading to alterations in mature enamel ultrastructure and in its mechanical features. © 2017 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

  11. Comparison of hydroxyapatite and dental enamel for testing shear bond strengths.

    Science.gov (United States)

    Imthiaz, Nishat; Georgiou, George; Moles, David R; Jones, Steven P

    2008-05-01

    To investigate the feasibility of using artificial hydroxyapatite as a future biomimetic laboratory substitute for human enamel in orthodontic bond strength testing by comparing the shear bond strengths and nature of failure of brackets bonded to samples of hydroxyapatite and enamel. One hundred and fifty hydroxyapatite discs were prepared by compression at 20 tons and fired in a furnace at 1300 degrees C. One hundred and five enamel samples were prepared from the buccal and palatal/lingual surfaces of healthy premolars extracted for orthodontic purposes. Orthodontic brackets were bonded to each sample and these were subjected to shear bond strength testing using a custom-made jig mounted in an Instron Universal Testing Machine. The force value at bond failure was obtained, together with the nature of failure which was assessed using the Adhesive Remnant Index. The mean shear bond strength for the enamel samples was 16.62 MPa (95 per cent CI: 15.26, 17.98) and for the hydroxyapatite samples 20.83 MPa (95 per cent CI: 19.68, 21.98). The difference between the two samples was statistically significant (p enamel samples scored 2 or 3, while 49 per cent of the hydroxyapatite samples scored 0 or 1. Hydroxyapatite was an effective biomimetic substrate for bond strength testing with a mean shear bond strength value (20.83 MPa) at the upper end of the normal range attributed to enamel (15-20 MPa). Although the difference between the shear bond strengths for hydroxyapatite and enamel was statistically significant, hydroxyapatite could be used as an alternative to enamel for comparative laboratory studies until a closer alternative is found. This would eliminate the need for extracted teeth to be collected. However, it should be used with caution for quantitative studies where true bond strengths are to be investigated.

  12. Influence of the incidence angle on the morphology of enamel and dentin under Er:YAG laser irradiation

    International Nuclear Information System (INIS)

    Junqueira Junior, Duilio Naves

    2002-01-01

    The purpose of this study is to make an in vitro evaluation, using scanning electron microscopy, of the influence of the laser beam irradiation angle on the enamel and dentin morphology. These tissues were both irradiated by Er:YAG Laser, with the same energy parameter. Twenty-four incisive bovine teeth were used, separated in eight groups, four of enamel, and four of dentin, with three specimens in each group. Each specimen was submitted to three laser applications, varying the incidence angle, between the laser and the tooth surface, at 90, 50 and 20 degrees. The applied frequency was 2 Hz, with 20 pulses in each application. The KaVo Key Laser 3 was employed, wavelength at 2940 nm, adjustable energy from 40 to 600 mJ and repetition rate from 1 to 25 Hz. The groups were distributed according to the energy parameter as follows - enamel: 250 mJ; 300 mJ; 350 mJ and 400 mJ; dentin: 200 mJ; 250 mJ; 300 mJ and 350 mJ. The results evidenced the Laser incidence angle importance; it is an essential parameter in the protocol of utilization and it should not be disregarded. The observations of this study allow to conclude that the Laser incidence angle has direct influence on the morphological aspect of the alterations produced in enamel and dentin. (author)

  13. The Effects of Remineralization via Fluoride Versus Low-Level Laser IR810 and Fluoride Agents on the Mineralization and Microhardness of Bovine Dental Enamel

    Directory of Open Access Journals (Sweden)

    Edith Lara-Carrillo

    2018-01-01

    Full Text Available The objective of this study was to assess the mineralization and microhardness of bovine dental enamel surfaces treated with fluoride, tri-calcium phosphate, and infrared (IR 810 laser irradiation. The study used 210 bovine incisors, which were divided into six groups (n = 35 in each: Group A: Untreated (control, Group B: Fluoride (Durapath-Colgate, Group C: Fluoride+Tri-calcium phosphate (Clin-Pro White-3 M, Group D: Laser IR 810 (Quantum, Group E: Fluoride+laser, and Group F: Fluoride+tri-calcium phosphate+laser. Mineralization was measured via UV-Vis spectroscopy for phosphorus and via atomic absorption spectroscopy for calcium upon demineralization and remineralization with proven agents. Microhardness (SMH was measured after enamel remineralization. Mineral loss data showed differences between the groups before and after the mineralizing agents were placed (p < 0.05. Fluoride presented the highest remineralization tendency for both calcium and phosphate, with a Vickers microhardness of 329.8 HV0.1/11 (p < 0.05. It was observed that, if remineralization solution contained fewer minerals, the microhardness surface values were higher (r = −0.268 and −0.208; p < 0.05. This study shows that fluoride has a remineralizing effect compared with calcium triphosphate and laser IR810. This in vitro study imitated the application of different remineralizing agents and showed which one was the most efficient for treating non-cavitated injuries. This can prevent the progression of lesions in patients with white spot lesions.

  14. In Vitro Inhibition of Enamel Demineralisation by Fluoride-releasing Restorative Materials and Dental Adhesives.

    Science.gov (United States)

    Dionysopoulos, Dimitrios; Koliniotou-Koumpia, Eugenia; Helvatzoglou-Antoniades, Maria; Kotsanos, Nikolaos

    2016-01-01

    To determine the ability of 5 contemporary fluoride-releasing restoratives and 3 fluoride-releasing adhesives to inhibit enamel demineralisation surrounding restorations, and the associations between inhibition and the levels of fluoride released from these materials. Five fluoride-releasing restoratives (Fuji IX GP, Ketac N100, Dyract Extra, Beautifil II and Wave) and 3 fluoride-releasing adhesives (Stae, Prime & Bond NT and Fluoro Bond II) were investigated. Eight disks of each material were prepared. Fluoride release was measured daily using a fluoride-ion-selective electrode for 15 days. Twenty-four cavities for each group were restored with a restorative and an adhesive. Specimens were subjected to thermal stress and stored for 30 days in saline solution. After a 15-day pH-cycling regimen, two 150-μm-thick sections were derived from each specimen. Enamel lesion depth was measured at 0, 100, and 200 μm from each restoration's margin via polarised light microscopy. Of the restoratives investigated, Fuji IX GP released the most fluoride. The fluoride-releasing restoratives tested exhibited shallower enamel lesions than did the control group at all distances tested (p < 0.05). Fuji IX GP yielded significantly lower enamel lesion depth than did the other experimental materials. The depths of enamel lesions did not differ significantly when comparing restoratives applied with a fluoride-releasing adhesive with those applied with a non-fluoride-releasing adhesive. The fluoride-releasing materials tested reduced enamel demineralisation but to different extents, depending on their levels of fluoride release. Fluoride-releasing adhesives did not influence enamel lesion formation.

  15. Effects of fluoride and epigallocatechin gallate on soft-drink-induced dental erosion of enamel and root dentin

    Directory of Open Access Journals (Sweden)

    Yin-Lin Wang

    2018-04-01

    Full Text Available Background/Purpose: Fluoride and epigallocatechin gallate (EGCG have been proven to prevent dental caries. The purpose of this study was to evaluate the effects of fluoride and EGCG on soft-drink-induced dental erosion in vitro. Methods: Forty enamel and dentin specimens were prepared from extracted human teeth. The specimens were divided into 4 groups and treated separately with distilled water (as control, 0.5 M sodium fluoride (NF, 400 μM EGCG (EG, and a solution containing 0.5 M NaF and 400 μM EGCG (FG. Cyclic erosive treatment was performed according to the experimental procedures. The specimens were analyzed using laser scanning confocal microscopy, scanning electron microscopy, and a microhardness tester. The data were analyzed using ANOVA and Bonferroni's post hoc test. The significance level was set at 5%. Results: The amount of substance loss was lower in the NF and EG groups than in the control group (p < 0.05. The erosion-caused substance loss was more pronounced in the dentin than in the enamel specimens. Surface microhardness loss was lower in the NF and EG groups than in the control group (p < 0.05. The diameter of the dentinal tubule was wider in the control group than in the NF and EG groups (p < 0.05. No combined effects were observed in the FG group. Conclusion: Both fluoride and EGCG are effective in preventing soft-drink-induced erosion compared with the control group. Fluoride and EGCG may interfere with each other. The mechanisms of the anti-erosive effect need to be explored in the future. Keywords: Dental erosion, Fluoride, Epigallocatechin gallate, Soft drinks, Laser scanning confocal microscopy

  16. Assessment of the survival of dental implants in irradiated jaws ...

    African Journals Online (AJOL)

    Background: In patients undergoing head and neck surgery for various pathologic conditions, implants are one of the best restorative options and are increasing widely used. Therefore, we evaluated the success of dental implants in the irradiated jaws of patients following treatment of oral cancer oral cancer treated patients ...

  17. Assessment of the Survival of Dental Implants in Irradiated Jaws ...

    African Journals Online (AJOL)

    frequency of dental implant placement in irradiated jaws from. 2002 to 2008 in India. Table 2 ..... Linsen SS, Martini M, Stark H. Long-term results of endosteal implants following radical oral ... Oral Health 2015:5;1-6. 21. Visch LL, van Waas MA ...

  18. Mathematical model governing laser-produced dental cavity

    Science.gov (United States)

    Yilbas, Bekir S.; Karatoy, M.; Yilbas, Z.; Karakas, Eyup S.; Bilge, A.; Ustunbas, Hasan B.; Ceyhan, O.

    1990-06-01

    Formation of dental cavity may be improved by using a laser beam. This provides nonmechanical contact, precise location of cavity, rapid processing and increased hygienity. Further examination of interaction mechanism is needed to improve the application of lasers in density. Present study examines the tenperature rise and thermal stress development in the enamel during Nd YAG laser irradiation. It is found that the stresses developed in the enamel is not sufficiently high enough to cause crack developed in the enamel.

  19. Effects of tooth whitening and orange juice on surface properties of dental enamel.

    Science.gov (United States)

    Ren, Yan-Fang; Amin, Azadeh; Malmstrom, Hans

    2009-06-01

    To study the effects of 6% H2O2 activated with LED light on surface enamel as compared to orange juice challenges in vitro. A total of 40 human enamel discs were incubated in saliva overnight to allow pellicle formation and then divided into three groups: 15 for whitening treatments, 15 for orange juice immersions and 10 for normal saline controls. Baseline microhardness was measured with a microhardness Knoop indenter (50g, 10s) and surface topography was evaluated with a focus-variation 3D scanning microscopy. Enamel discs were treated with H2O2 or orange juice for 20 min each cycle for five cycles to simulate daily treatment with the products for 5 days. The discs were stored in saliva between treatment cycles. Microhardness and surface topography were evaluated again after treatments. Changes in microhardness and in surface area roughness (Sa), mean maximum peak-to-valley distance (Sz) and the developed surface area ratio (Sdr) were compared before and after treatments (t-test) and among groups (ANOVA). Enamel surface hardness decreased by 84% after orange juice immersion but no statistically significant changes were observed in the whitening and control groups. Surface topography changed significantly only in the orange juice group as shown by increased Sa (1.2 microm vs. 2.0 microm), Sz (7.7 microm vs. 10.2 microm) and Sdr (2.8% vs. 6.0%). No such changes were observed in the whitening and control groups. In comparison to orange juice challenges, the effects of 6% H2O2 on surface enamel are insignificant. Orange juice erosion markedly decreased hardness and increased roughness of enamel.

  20. Effect of acidity upon attrition-corrosion of human dental enamel.

    Science.gov (United States)

    Wu, Yun-Qi; Arsecularatne, Joseph A; Hoffman, Mark

    2015-04-01

    Attrition-corrosion is a synthesized human enamel wear process combined mechanical effects (attrition) with corrosion. With the rising consumption of acidic food and beverages, attrition-corrosion is becoming increasingly common. Yet, research is limited and the underlying mechanism remains unclear. In this study, in vitro wear loss of human enamel was investigated and the attrition-corrosion process and wear mechanism were elucidated by the analysis of the wear scar and its subsurface using focused ion beam (FIB) sectioning and scanning electron microscopy (SEM). Human enamel flat-surface samples were prepared with enamel cusps as the wear antagonists. Reciprocating wear testing was undertaken under load of 5N at the speed of 66 cycle/min for 2250 cycles with lubricants including citric acid (at pH 3.2 and 5.5), acetic acid (at pH 3.2 and 5.5) and distilled water. All lubricants were used at 37°C. Similar human enamel flat-surface samples were also exposed to the same solutions as a control group. The substance loss of enamel during wear can be linked to the corrosion potential of a lubricant used. Using a lubricant with very low corrosion potential (such as distilled water), the wear mechanism was dominated by delamination with high wear loss. Conversely, the wear mechanism changed to shaving of the softened layer with less material loss in an environment with medium corrosion potential such as citric acid at pH 3.2 and 5.5 and acetic acid at pH 5.5. However, a highly corrosive environment (e.g., acetic acid at pH 3.2) caused the greatest loss of substance during wear. Copyright © 2015 Elsevier Ltd. All rights reserved.

  1. Sub-10-micrometer toughening and crack tip toughness of dental enamel.

    Science.gov (United States)

    Ang, Siang Fung; Schulz, Anja; Pacher Fernandes, Rodrigo; Schneider, Gerold A

    2011-04-01

    In previous studies, enamel showed indications to occlude small cracks in-vivo and exhibited R-curve behaviors for bigger cracks ex-vivo. This study quantifies the crack tip's toughness (K(I0),K(III0)), the crack's closure stress and the cohesive zone size at the crack tip of enamel and investigates the toughening mechanisms near the crack tip down to the length scale of a single enamel crystallite. The crack-opening-displacement (COD) profile of cracks induced by Vickers indents on mature bovine enamel was studied using atomic force microscopy (AFM). The mode I crack tip toughness K(I0) of cracks along enamel rod boundaries and across enamel rods exhibit a similar range of values: K(I0,Ir)=0.5-1.6MPa m(0.5) (based on Irwin's 'near-field' solution) and K(I0,cz)=0.8-1.5MPa m(0.5) (based on the cohesive zone solution of the Dugdale-Muskhelishvili (DM) crack model). The mode III crack tip toughness K(III0,Ir) was computed as 0.02-0.15MPa m(0.5). The crack-closure stress at the crack tip was computed as 163-770 MPa with a cohesive zone length and width 1.6-10.1μm and 24-44 nm utilizing the cohesive zone solution. Toughening elements were observed under AFM and SEM: crack bridging due to protein ligament and hydroxyapatite fibres (micro- and nanometer scale) as well as microcracks were identified. Crown Copyright © 2010. Published by Elsevier Ltd. All rights reserved.

  2. Effect of high energy X-ray irradiation on the nano-mechanical properties of human enamel and dentine

    Energy Technology Data Exchange (ETDEWEB)

    Liang, Xue; Zhang, Jing Yang; Cheng, Iek Ka [State Key Laboratory of Oral Diseases, Sichuan University, Chengdu (China); Li, Ji Yao, E-mail: jiyao_li@aliyun.com [West China School of Stomatology, Sichuan University, Chengdu (China)

    2016-05-01

    Radiotherapy for malignancies in the head and neck can cause common complications that can result in tooth damage that are also known as radiation caries. The aim of this study was to examine damage to the surface topography and calculate changes in friction behavior and the nano-mechanical properties (elastic modulus, nano hardness and friction coefficient) of enamel and dentine from extracted human third molars caused by exposure to radiation. Enamel and dentine samples from 50 human third molars were randomly assigned to four test groups or a control group. The test groups were exposed to high energy X-rays at 2 Gy/day, 5 days/week for 5 days (10 Gy group), 15 days (30 Gy group), 25 days (50 Gy group), 35 days (70 Gy group); the control group was not exposed. The nano hardness, elastic modulus, and friction coefficient were analyzed using a Hysitron Triboindenter. The nano-mechanical properties of both enamel and dentine showed significant dose-response relationships. The nano hardness and elastic modulus were most variable between 30-50 Gy, while the friction coefficient was most variable between 0-10 Gy for dentine and 30-50 Gy for enamel. After exposure to X-rays, the fracture resistance of the teeth clearly decreased (rapidly increasing friction coefficient with increasing doses under the same load), and they were more fragile. These nano-mechanical changes in dental hard tissue may increase the susceptibility to caries. Radiotherapy caused nano-mechanical changes in dentine and enamel that were dose related. The key doses were 30-50 Gy and the key time points occurred during the 15{sup th}-25{sup th} days of treatment, which is when application of measures to prevent radiation caries should be considered. (author)

  3. Effect of high energy X-ray irradiation on the nano-mechanical properties of human enamel and dentine

    Directory of Open Access Journals (Sweden)

    Xue LIANG

    2016-01-01

    Full Text Available Abstract Radiotherapy for malignancies in the head and neck can cause common complications that can result in tooth damage that are also known as radiation caries. The aim of this study was to examine damage to the surface topography and calculate changes in friction behavior and the nano-mechanical properties (elastic modulus, nanohardness and friction coefficient of enamel and dentine from extracted human third molars caused by exposure to radiation. Enamel and dentine samples from 50 human third molars were randomly assigned to four test groups or a control group. The test groups were exposed to high energy X-rays at 2 Gy/day, 5 days/week for 5 days (10 Gy group, 15 days (30 Gy group, 25 days (50 Gy group, 35 days (70 Gy group; the control group was not exposed. The nanohardness, elastic modulus, and friction coefficient were analyzed using a Hysitron Triboindenter. The nano-mechanical properties of both enamel and dentine showed significant dose-response relationships. The nanohardness and elastic modulus were most variable between 30-50 Gy, while the friction coefficient was most variable between 0-10 Gy for dentine and 30-50 Gy for enamel. After exposure to X-rays, the fracture resistance of the teeth clearly decreased (rapidly increasing friction coefficient with increasing doses under the same load, and they were more fragile. These nano-mechanical changes in dental hard tissue may increase the susceptibility to caries. Radiotherapy caused nano-mechanical changes in dentine and enamel that were dose related. The key doses were 30-50 Gy and the key time points occurred during the 15th-25th days of treatment, which is when application of measures to prevent radiation caries should be considered.

  4. Effect of high energy X-ray irradiation on the nano-mechanical properties of human enamel and dentine

    International Nuclear Information System (INIS)

    Liang, Xue; Zhang, Jing Yang; Cheng, Iek Ka; Li, Ji Yao

    2016-01-01

    Radiotherapy for malignancies in the head and neck can cause common complications that can result in tooth damage that are also known as radiation caries. The aim of this study was to examine damage to the surface topography and calculate changes in friction behavior and the nano-mechanical properties (elastic modulus, nano hardness and friction coefficient) of enamel and dentine from extracted human third molars caused by exposure to radiation. Enamel and dentine samples from 50 human third molars were randomly assigned to four test groups or a control group. The test groups were exposed to high energy X-rays at 2 Gy/day, 5 days/week for 5 days (10 Gy group), 15 days (30 Gy group), 25 days (50 Gy group), 35 days (70 Gy group); the control group was not exposed. The nano hardness, elastic modulus, and friction coefficient were analyzed using a Hysitron Triboindenter. The nano-mechanical properties of both enamel and dentine showed significant dose-response relationships. The nano hardness and elastic modulus were most variable between 30-50 Gy, while the friction coefficient was most variable between 0-10 Gy for dentine and 30-50 Gy for enamel. After exposure to X-rays, the fracture resistance of the teeth clearly decreased (rapidly increasing friction coefficient with increasing doses under the same load), and they were more fragile. These nano-mechanical changes in dental hard tissue may increase the susceptibility to caries. Radiotherapy caused nano-mechanical changes in dentine and enamel that were dose related. The key doses were 30-50 Gy and the key time points occurred during the 15 th -25 th days of treatment, which is when application of measures to prevent radiation caries should be considered. (author)

  5. Surface variations affecting human dental enamel studied using nanomechanical and chemical analysis

    Science.gov (United States)

    Dickinson, Michelle Emma

    The enamel surface is the interface between the tooth and its ever changing oral environment. Cavity (caries) formation and extrinsic tooth staining are due, respectively, to degradation of the enamel structure under low pH conditions and interactions between salivary pellicle and dietary elements. Both of these occur at the enamel surface and are caused by the local environment changing the chemistry of the surface. The results can be detrimental to the enamel's mechanical integrity and aesthetics. Incipient carious lesions are the precursor to caries and form due to demineralisation of enamel. These carious lesions are a reversible structure where ions (e.g. Ca2+, F -) can diffuse in (remineralisation) to preserve the tooth's structural integrity. This investigation used controlled in vitro demineralisation and remineralisation to study artificial carious lesion formation and repair. The carious lesions were cross-sectioned and characterised using nanoindentation, electron probe micro-analysis and time of flight secondary ion mass spectrometry. Mechanical and chemical maps showed the carious lesion had a significantly reduced hardness and elastic modulus, and the calcium and phosphate content was lower than in sound enamel. Fluoride based remineralisation treatments gave a new phase (possibly fluorohydroxyapatite) within the lesion with mechanical properties higher than sound enamel. The acquired salivary pellicle is a protein-rich film formed by the physisorption of organic molecules in saliva onto the enamel surface. Its functions include lubrication during mastication and chemical protection. However, pellicle proteins react with dietary elements such as polyphenols (tannins in tea) causing a brown stain. This study has used in vitro dynamic nanoindentation and atomic force microscopy to examine normal and stained pellicles formed in vivo. The effects of polyphenols on the pellicle's mechanical properties and morphology have been studied. It was found that the

  6. In vivo PIXE-PIGE study of enhanced retention of fluorine in tooth enamel after laser irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Demortier, Guy [Department of Physics, University of Namur, 61, rue de Bruxelles, B5000 Namur (Belgium)], E-mail: guy.demortier@tvcablenet.be; Nammour, Samir [Faculty of Medicine, University of Liege, 8, rue Paul Spaak, B-1000 Bruxelles (Belgium)

    2008-05-15

    The presence of fluoride in tooth enamel reduces the solubility of hydroxylapatite by acid attack. Fluoride presence (even at low concentration) in the oral cavity is efficient against caries process. We propose a new approach of the explanation of the increase of fluoride retention in the tooth enamel when low power laser irradiation is applied after the treatment with fluoride gel (fluoridation). External beam PIGE measurements of fluorine on extracted teeth have been made in order to determine the best sequence of the operations. The laser irradiation after fluoride application is more efficient than the reverse procedure. This observation is in agreement with previous observations that the fluorine penetration in the enamel takes place first in the soft organic material present between the polycrystalline (prismatic) structure before being integrated in the crystalline composition of hydroxylapatite in order to produce fluoro-apatite. As those in vitro measurements do not reflect the whole process in the saliva, in vivo PIGE measurements have been also performed. We have demonstrated, by repeating the PIGE measurements (at least five times at various time intervals) that a significant increase of the fluoride retention took place even 18 months after the unique laser treatment. The complete experimental procedure is described: fluoride application, laser irradiation, PIGE measurements with 2.7 MeV protons (repeated measurements at the same place on the same tooth in order to follow the evolution) and safety tests before in vivo analyses.

  7. The Role of Na:K:2Cl Cotransporter 1 (NKCC1/SLC12A2) in Dental Epithelium during Enamel Formation in Mice

    Science.gov (United States)

    Jalali, Rozita; Lodder, Johannes C.; Zandieh-Doulabi, Behrouz; Micha, Dimitra; Melvin, James E.; Catalan, Marcelo A.; Mansvelder, Huibert D.; DenBesten, Pamela; Bronckers, Antonius

    2017-01-01

    Na+:K+:2Cl− cotransporters (NKCCs) belong to the SLC12A family of cation-coupled Cl− transporters. We investigated whether enamel-producing mouse ameloblasts express NKCCs. Transcripts for Nkcc1 were identified in the mouse dental epithelium by RT-qPCR and NKCC1 protein was immunolocalized in outer enamel epithelium and in the papillary layer but not the ameloblast layer. In incisors of Nkcc1-null mice late maturation ameloblasts were disorganized, shorter and the mineral density of the enamel was reduced by 10% compared to wild-type controls. Protein levels of gap junction protein connexin 43, Na+-dependent bicarbonate cotransporter e1 (NBCe1), and the Cl−-dependent bicarbonate exchangers SLC26A3 and SLC26A6 were upregulated in Nkcc1-null enamel organs while the level of NCKX4/SLC24A4, the major K+, Na+ dependent Ca2+ transporter in maturation ameloblasts, was slightly downregulated. Whole-cell voltage clamp studies on rat ameloblast-like HAT-7 cells indicated that bumetanide increased ion-channel activity conducting outward currents. Bumetanide also reduced cell volume of HAT-7 cells. We concluded that non-ameloblast dental epithelium expresses NKCC1 to regulate cell volume in enamel organ and provide ameloblasts with Na+, K+ and Cl− ions required for the transport of mineral- and bicarbonate-ions into enamel. Absence of functional Nkcc1 likely is compensated by other types of ion channels and ion transporters. The increased amount of Cx43 in enamel organ cells in Nkcc1-null mice suggests that these cells display a higher number of gap junctions to increase intercellular communication. PMID:29209227

  8. Effect of carbonated beverages, coffee, sports and high energy drinks, and bottled water on the in vitro erosion characteristics of dental enamel.

    Science.gov (United States)

    Kitchens, Michael; Owens, Barry M

    2007-01-01

    This study evaluated the effect of carbonated and non-carbonated beverages, bottled and tap water, on the erosive potential of dental enamel with and without fluoride varnish protection. Beverages used in this study included: Coca Cola Classic, Diet Coke, Gatorade sports drink, Red Bull high-energy drink, Starbucks Frappuccino coffee drink, Dasani water (bottled), and tap water (control). Enamel surfaces were coated with Cavity Shield 5% sodium fluoride treatment varnish. Twenty-eight previously extracted human posterior teeth free of hypocalcification and caries were used in this study. The coronal portion of each tooth was removed and then sectioned transverse from the buccal to lingual surface using a diamond coated saw blade. The crown sections were embedded in acrylic resin blocks leaving the enamel surfaces exposed. The enamel surfaces were polished using 600 to 2000 grit abrasive paper and diamond paste. Test specimens were randomly distributed to seven beverage groups and comprised 4 specimens per group. Two specimens per beverage group were treated with a fluoride varnish while 2 specimens did not receive fluoride coating. Surface roughness (profilometer) readings were performed at baseline (prior to fluoride treatment and immersion in the beverage) and again, following immersion for 14 days (24 hours/day). The test beverages were changed daily and the enamel specimens were immersed at 37 degrees C. Surface roughness data was evaluated using multiple factor ANOVA at a significance level of pStarBucks coffee, Dasani water, and tap water. Fluoride varnish was not a significant impact factor; however, beverage (type) and exposure time were significant impact variables. Both carbonated and non-carbonated beverages displayed a significant erosive effect on dental enamel; however, fluoride varnish treatments did not demonstrate a significant protective influence on enamel surfaces.

  9. The effect of acidulated phosphate fluoride application on dental enamel surfaces hardness

    Directory of Open Access Journals (Sweden)

    Edhie Arief P

    2007-09-01

    Full Text Available Enamel demineralization by acid is the first step of caries process. It has recently been shown that acidulated phosphate fluoride (APF can maintain the hardness of enamel surface. The aim of this study was examine the effect of APF application in the hardest of enamel surface. Fifty extracted teeth were cut at their crown, 40 teeth were taken randomly then divided into 4 groups, group 1 as the control, group 2 was treated with APF for 1 minute, group 3 for 4 minutes and group 4 for 7 minutes, then all the samples were washed with demineralized water. To see the effect of APF, all of the samples were soaked in lactic acid demineralization solution with pH 4,5 for 72 hours., the hardness of the surfaces of those samples before and after the treatment was measured by Micro Vickers Hardness Tester. The data were analyzed using One-Way ANOVA and LSD tests. In conclusion, 1.23% APF gel can reduce higher enamel demineralization.

  10. [Effects of tooth whitening agents and acidic drinks on the surface properties of dental enamel].

    Science.gov (United States)

    Chen, Xiaoling; Chen, Zhiqun; Lin, Yao; Shao, Jinquan; Yin, Lu

    2013-10-01

    Using tooth whitening agents (bleaching clip) in vitro and acidic drinks, we conducted a comparative study of the changes in enamel surface morphology, Ca/P content, and hardness. Tooth whitening glue pieces, cola, and orange juice were used to soak teeth in artificial saliva in vitro. Physiological saline was used as a control treatment. The morphology of the four groups was observed under a scanning electron microscope (SEM) immediately after the teeth were soaked for 7 and 14 d. The changes in Ca/P content and microhardness were analyzed. The enamel surfaces of the teeth in the three test groups were demineralized. The Ca/P ratio and the average microhardness were significantly lower than those of the control group immediately after the teeth were soaked (P 0.05). Bleaching agents caused transient demineralization of human enamel, but these agents could induce re-mineralization and repair of enamel over time. Demineralization caused by bleaching covered a relatively normal range compared with acidic drinks and daily drinking.

  11. Histomorphometric and microchemical characterization of maturing dental enamel in rats fed a boron-deficient diet

    Science.gov (United States)

    Few reports are available in the literature on enamel formation under nutritional deficiencies. Continuously erupting rodent incisors have considerable potential to serve as a model system for amelogenesis. Thus, we performed a study to determine the effects of boron (B) deficiency on the maturing d...

  12. Distribution and structure of dental enamel in incisors of Tabby mice

    Czech Academy of Sciences Publication Activity Database

    Risnes, S.; Peterková, Renata; Lesot, H.

    2005-01-01

    Roč. 50, - (2005), s. 181-184 ISSN 0003-9969 R&D Projects: GA MŠk(CZ) OC B23.002; GA ČR GA304/02/0448 Institutional research plan: CEZ:AV0Z5039906 Keywords : enamel * incisor * mouse Subject RIV: EB - Genetics ; Molecular Biology Impact factor: 1.288, year: 2005

  13. Teeth and irradiation: dental care and treatment of osteoradionecrosis after irradiation in head and neck cancer

    International Nuclear Information System (INIS)

    Thariat, J.; Ortholan, C.; Thariat, J.; Darcourt, V.; Poissonnet, G.; Dassonville, O.; Marcy, P.Y.; Bozec, A.; Ortholan, C.; Santini, J.; Thariat, J.; Mones, E. de; Darcourt, V.; Poissonnet, G.; Dassonville, O.; Bozec, A.; Santini, J.; Marcy, P.Y.; Guevara, N.; Bensadoun, R.J.

    2010-01-01

    Pre-irradiation dental care depends on teeth health, fields and dose of irradiation, compliance to fluorides, cessation of tobacco and psycho-social cofactors. Dental care aims at preventing complications and preserving the quality of life (eating, speech, and aesthetics). The role of hyperbaric oxygen therapy for the prevention of osteoradionecrosis after teeth removal on the mandible in areas receiving 50 Gy or more is still controversial. Medical treatments may be sufficient for early stages of osteoradionecrosis (antibiotics, pain killers, non-steroidal anti-inflammatory drugs as well as clodronate, vitamin E, pentoxifylline). However, reconstructive surgery should not be delayed in advanced stages of osteoradionecrosis. New irradiation techniques are changing dose distributions and therefore require close collaboration between odonto-stomatologists and radiation oncologists to define the best dental care. (authors)

  14. Determination of thermal diffusivity of dental enamel and dentin as a function of temperature, using infrared thermography; Determinacao da difusividade termica do esmalte e dentina em funcao de temperatura, utilizando termografia no infravermelho

    Energy Technology Data Exchange (ETDEWEB)

    Pereira, Thiago Martini

    2009-07-01

    In this work it was developed a software that calculates automatically, the thermal diffusivity value as a function of temperature in materials. The infrared thermography technique was used for data acquisition of temperature distribution as a function of time. These data were used to adjust a temperature function obtained from the homogeneous heat equation with specific boundary conditions. For that, an infrared camera (detecting from 8 {mu}m to 9 {mu}m) was calibrated to detect temperature ranging from 185 degree C up to 1300 degree C at an acquisition rate of 300 Hz. It was used, 10 samples of dental enamel and 10 samples of dentin, with 4 mm x 4 mm x 2 mm, which were obtained from bovine lower incisor teeth. These samples were irradiated with an Er:Cr:YSGG pulsed laser ({lambda} = 2,78 {mu}m). The resulting temperature was recorded 2 s prior, 10 s during irradiation and continuing for 2 more seconds after it. After each irradiation, all obtained thermal images were processed in the software, creating a file with the data of thermal diffusivity as a function of temperature. Another file with the thermal diffusivity values was also calculated after each laser pulse. The mean result of thermal diffusivity obtained for dental enamel was 0,0084 {+-} 0,001 cm2/s for the temperature interval of 220-550 degree C. The mean value for thermal diffusivity obtained for dentin was 0,0015 0,0004 cm2/s in temperatures up to 360 degree C; however, this value increases for higher temperatures. According to these results, it was possible to conclude that the use of infrared thermography, associated with the software developed in this work, is an efficient method to determine the thermal diffusivity values as a function of temperature in different materials. (author)

  15. A quantitative light microscopic study of the odontoblast and subodontoblastic reactions to active and arrested enamel caries without cavitation

    DEFF Research Database (Denmark)

    Bjørndal, L.; Darvann, T.A.; Thylstrup, Anders

    1998-01-01

    Carious lesions, Computerized histomorphology, Dental pulp, Dentine, Enamel, Microradiography, Odontoblast......Carious lesions, Computerized histomorphology, Dental pulp, Dentine, Enamel, Microradiography, Odontoblast...

  16. Determination of biomechanical characteristics of dentine and dental enamel in vitro

    OpenAIRE

    UTYUZH ANATOLIJ SERGEEVICH; YUMASHEV ALEKSEJ VALERIEVICH; ZAGORSKY VLADISLAV VALERIEVICH; ZAKHAROV ALEKSEJ NIKOLAEVICH; NEFEDOVA IRINA VALERIEVNA

    2016-01-01

    Hardness characteristics of the hard tissues of a tooth are widely used in dentistry practice, both in diagnostics and in therapy, they are also very important for individual selection of restoration and other specialized materials. During examination of enamel and dentine hardness, it is very important to handle information that beside its theoretical value also has high practical value. For this purpose, we suggest to calculate hardness of tooth tissue on the basis of quantitative indicator...

  17. Morphological Alterations of the Surfaces of Enamel and Dentin of Deciduous Teeth Irradiated with Nd:YAG, C0(2)and Diode Lasers

    OpenAIRE

    Souza, Mónica Rodrigues de; Watanabe, Ii-Sei; Azevedo, Luciane H; Tanji, Edgar Y

    2009-01-01

    In this work, we studied the effects of C0(2), Nd:YAG and diode lasers on the enamel and dentin of deciduous human teeth. After the irradiations, the samples were duly prepared and set up on metallic bases, covered with gold and examined in the scanning electron microscope. The results showed that the irradiation with the C0(2) mode locked laser with 1.0 W power caused melting and irregularities with small cavities on the surface of the enamel. The irradiated area on the dentin surface appear...

  18. Ameloblasts require active RhoA to generate normal dental enamel.

    Science.gov (United States)

    Xue, Hui; Li, Yong; Everett, Eric T; Ryan, Kathleen; Peng, Li; Porecha, Rakhee; Yan, Yan; Lucchese, Anna M; Kuehl, Melissa A; Pugach, Megan K; Bouchard, Jessica; Gibson, Carolyn W

    2013-08-01

    RhoA plays a fundamental role in regulation of the actin cytoskeleton, intercellular attachment, and cell proliferation. During amelogenesis, ameloblasts (which produce the enamel proteins) undergo dramatic cytoskeletal changes and the RhoA protein level is up-regulated. Transgenic mice were generated that express a dominant-negative RhoA transgene in ameloblasts using amelogenin gene-regulatory sequences. Transgenic and wild-type (WT) molar tooth germs were incubated with sodium fluoride (NaF) or sodium chloride (NaCl) in organ culture. Filamentous actin (F-actin) stained with phalloidin was elevated significantly in WT ameloblasts treated with NaF compared with WT ameloblasts treated with NaCl or with transgenic ameloblasts treated with NaF, thereby confirming a block in the RhoA/Rho-associated protein kinase (ROCK) pathway in the transgenic mice. Little difference in quantitative fluorescence (an estimation of fluorosis) was observed between WT and transgenic incisors from mice provided with drinking water containing NaF. We subsequently found reduced transgene expression in incisors compared with molars. Transgenic molar teeth had reduced amelogenin, E-cadherin, and Ki67 compared with WT molar teeth. Hypoplastic enamel in transgenic mice correlates with reduced expression of the enamel protein, amelogenin, and E-cadherin and cell proliferation are regulated by RhoA in other tissues. Together these findings reveal deficits in molar ameloblast function when RhoA activity is inhibited. © 2013 Eur J Oral Sci.

  19. Prevalence and extent of dental caries, dental fluorosis, and developmental enamel defects in Lithuanian teenage populations with different fluoride exposures

    DEFF Research Database (Denmark)

    Machiulskiene, Vita; Bælum, Vibeke; Fejerskov, Ole

    2009-01-01

    The aim of this study was to describe the pattern of dental caries, dental fluorosis, and developmental defects of non-fluoride origin in Lithuanian children born and raised in regions with 1.1 ppm (1.1 mg/l F) and 0.3 ppm (0.3 mg/l F) water fluoride levels, respectively. All permanent surfaces/t...... difference, 3.43). The results lend support to the hypothesis that the presence of fluoride in the oral environment promotes lesion arrest rather than inhibiting the initiation of new lesions......./teeth of 300 teenagers were examined for dental caries, dental fluorosis, and non-fluoride developmental defects. The caries prevalence of the study population was 100%. The mean number of decayed surfaces (DS) differed only slightly and statistically insignificantly between the '1.1 ppm fluoride' and '0.3 ppm...

  20. The effects of acid erosion and remineralization on enamel and three different dental materials: FT-Raman spectroscopy and scanning electron microscopy analysis.

    Science.gov (United States)

    Soares, Luís Eduardo Silva; Soares, Ana Lúcia Silva; De Oliveira, Rodrigo; Nahórny, Sidnei

    2016-07-01

    FT-Raman spectroscopy and scanning electron microscopy (SEM) were employed to test the hypothesis that the beverage consumption or mouthwash utilization would change the chemistry of dental materials and enamel inorganic content. Bovine enamel samples (n = 36) each received two cavity preparations (n = 72), each pair filled with one of three dental materials (R: nanofilled composite resin, GIC: glass-ionomer cement, RMGIC: resin-modified GIC). Furthermore, they were treated with three different solutions (S: artificial saliva, E: erosion/Pepsi Twist or EM: erosion + mouthwash/Colgate Plax). Reduction of carbonate content of enamel was greater in RE than RS (P erosion. Material degradation was greater after E and EM than S. GIC and RMGIC materials had a positive effect against acid erosion in the adjacent enamel after remineralization with mouthwash. The beverage and mouthwash utilization would change R and GIC chemical properties. A professional should periodically monitor the glass-ionomer and resin restorations, as they degrade over time under erosive challenges and mouthwash utilization. Microsc. Res. Tech., 2016. © 2016 Wiley Periodicals, Inc. Microsc. Res. Tech. 79:646-656, 2016. © 2016 Wiley Periodicals, Inc. © 2016 Wiley Periodicals, Inc.

  1. Structural changes in fluorosed dental enamel of red deer (Cervus elaphus L.) from a region with severe environmental pollution by fluorides

    International Nuclear Information System (INIS)

    Kierdorf, U.; Kierdorf, H.; Sedlacek, F.; Fejerskov, O.

    1996-01-01

    A macroscopic, microradiographic and scanning electron microscope study was performed on the structure of fluorosed dental enamel in red deer from a fluoride polluted region (North Bohemia, Czech Republic). As was revealed by analysis of mandibular bone fluoride content, the rate of skeletal fluoride accumulation in the fluorotic deer was about 6 times that in controls taken from a region not exposed to excessive fluoride deposition. In all fluorosed mandibles, the 1st molar was consistently less fluorotic than the other permanent teeth. This was related to the fact that crown formation in the M1 takes place prenatally and during the lactation period. Fluorosed teeth exhibited opaque and posteruptively stained enamel, reduction or loss of enamel ridges, moderately to grossly increased wear and, in more severe cases, also enamel surface lesions of partly posteruptive, partly developmental origin. Microradiographically, fluorosed enamel was characterised by subsurface hypomineralisation, interpreted as a result of fluoride interference with the process of enamel maturation. In addition, an accentuation of the incremental pattern due to the occurrence of alternating bands with highly varying mineral content was observed in severely fluorosed teeth, denoting fluoride disturbance during the secretory stage of amelogenesis. A corresponding enhancement of the incremental pattern was also seen in the dentine. The enamel along the more pronounced hypoplasias consisted of stacked, thin layers of crystals arranged in parallel, indicating that the ameloblasts in these locations had lost the distal (prism-forming) portions of their Tomes processes. The findings of the present study indicate that red deer are highly sensitive bioindicators of environmental pollution by fluorides

  2. Effect of thickener agents on dental enamel microhardness submitted to at-home bleaching Efeito de agentes espessantes na microdureza do esmalte submetido ao clareamento dental caseiro

    Directory of Open Access Journals (Sweden)

    José Augusto Rodrigues

    2007-06-01

    Full Text Available Dental bleaching occurs due to an oxidation reaction between the bleaching agents and the macromolecules of pigments in the teeth. This reaction is unspecific and the peroxides can also affect the dental matrix causing mineral loss. On the other hand, recent studies have suggested that the thickener agent carbopol can also cause mineral loss. Thus, the objective of this study was to evaluate in vitro the effect of at-home dental bleaching on dental enamel microhardness after the use of bleaching agents with and without carbopol as a thickener agent. Bovine dental slabs with 3 x 3 x 3 mm were obtained, sequentially polished, and randomly divided into 4 groups according to the experimental treatment: G1: 2% carbopol; G2: 10% carbamide peroxide with carbopol; G3: carbowax; G4: 10% carbamide peroxide with poloxamer. Bleaching was performed daily for 4 weeks, immersed in artificial saliva. Enamel microhardness values were obtained before the treatment (T0 and 7 (T1, 14 (T2, 21 (T3, 28 (T4, and 42 (T5 days after the beginning of the treatment. ANOVA and Tukey's test revealed statistically significant differences only for the factor Time (F = 5.48; p O clareamento dental ocorre devido a uma reação de oxidação entre o agente clareador e as macromoléculas de pigmentos presentes nos dentes. Esta reação é inespecífica e o peróxido pode agir na matriz dental causando perdas de mineral. Por outro lado, estudos recentes sugerem que o agente espessante carbopol também pode causar perda mineral. Assim, o objetivo deste trabalho foi avaliar in vitro o efeito do clareamento caseiro sobre a microdureza do esmalte após o uso de agentes clareadores com e sem carbopol como espessante. Fragmentos de esmalte bovino de 3 x 3 x 3 mm foram obtidos, polidos seqüencialmente e aleatoriamente divididos em 4 grupos de acordo com o tratamento experimental: G1: carbopol a 2%; G2: peróxido de carbamida a 10% com carbopol; G3: carbowax; G4: peróxido de carbamida a

  3. Enamel formation and amelogenesis imperfecta.

    Science.gov (United States)

    Hu, Jan C-C; Chun, Yong-Hee P; Al Hazzazzi, Turki; Simmer, James P

    2007-01-01

    Dental enamel is the epithelial-derived hard tissue covering the crowns of teeth. It is the most highly mineralized and hardest tissue in the body. Dental enamel is acellular and has no physiological means of repair outside of the protective and remineralization potential provided by saliva. Enamel is comprised of highly organized hydroxyapatite crystals that form in a defined extracellular space, the contents of which are supplied and regulated by ameloblasts. The entire process is under genetic instruction. The genetic control of amelogenesis is poorly understood, but requires the activities of multiple components that are uniquely important for dental enamel formation. Amelogenesis imperfecta (AI) is a collective designation for the variety of inherited conditions displaying isolated enamel malformations, but the designation is also used to indicate the presence of an enamel phenotype in syndromes. Recently, genetic studies have demonstrated the importance of genes encoding enamel matrix proteins in the etiology of isolated AI. Here we review the essential elements of dental enamel formation and the results of genetic analyses that have identified disease-causing mutations in genes encoding enamel matrix proteins. In addition, we provide a fresh perspective on the roles matrix proteins play in catalyzing the biomineralization of dental enamel. Copyright 2007 S. Karger AG, Basel.

  4. EPR dosimetry in tooth enamel by x radiation; Dosimetria EPR en esmalte dental irradiado con rayos X

    Energy Technology Data Exchange (ETDEWEB)

    Dubner, Diana; Perez, Maria del Rosario; Gisone, P. [Autoridad Regulatoria Nuclear, Buenos Aires (Argentina)] E-mail: ddubner@cae.arn.gov.ar; Fainstein, C.; Winkler, E. [Comision Nacional de Energia Atomica (CNEA), San Carlos de Bariloche (Argentina). Centro Atomico Bariloche]|[Universidad Nacional de Cuyo, Mendoza (Argentina). Inst. Balseiro; Saravi, Margarita [Comision Nacional de Energia Atomica (CNEA) (Argentina). Centro Atomico Ezeiza; Davila, Francisco [Ateneo Argentino de Odontologia, Buenos Aires (Argentina)

    2001-07-01

    Tooth enamel, extracted from molars, was irradiated with 66 keV X-rays, with doses up to 1 Gy. The preparation of the powder samples is described, as well as the protocol for the acquisition and processing of the spectra. The radiation induced paramagnetism is measured, at room temperature, by ESR spectroscopy. The ESR spectra is well described considering two paramagnetic species, with magnetic moments (in units of Bohr magnetrons) g=2,0041, and g1=2,0018, g2=1,9972. The ESR data (peak-to-peak amplitude per mg, hpp/mg, vs dose D), for doses 0 Gy

  5. Fluorine uptake into human enamel around a fluoride-containing dental material during cariogenic pH cycling

    International Nuclear Information System (INIS)

    Komatsu, H.; Yamamoto, H.; Nomachi, M.; Yasuda, K.; Matsuda, Y.; Murata, Y.; Kijimura, T.; Sano, H.; Sakai, T.; Kamiya, T.

    2007-01-01

    the enamel adjacent to the material remained a caries inhibition zone due to low rate of demineralization. With caries progression, fluorine accumulated in the subsurface of the caries lesion, while the outermost surface of the caries lesion gradually dissolved under increasing pH cycling. The data obtained using PIGE (TIARA, JAPAN) technique were useful to understand the fluorine benefit for preventing dental caries by means of fluoride-containing dental materials

  6. Fluorine uptake into human enamel around a fluoride-containing dental material during cariogenic pH cycling

    Energy Technology Data Exchange (ETDEWEB)

    Komatsu, H. [Graduate School of Dental Medicine, Hokkaido University, Kita-13, Nishi-7, Kita-ku, Sapporo 060-8586 (Japan)]. E-mail: kom@den.hokudai.ac.jp; Yamamoto, H. [Graduate School of Dentistry, Osaka University, 1-8 Yamada-Oka, Suita 565-0871 (Japan); Nomachi, M. [Graduate School of Science, Osaka University, 1-1 Machikaneyama, Toyonaka 560-0043 (Japan); Yasuda, K. [Wakasa wan Energy Research Center, 64-52-1 Hase, Tsuruga 914-0192 (Japan); Matsuda, Y. [Graduate School of Dental Medicine, Hokkaido University, Kita-13, Nishi-7, Kita-ku, Sapporo 060-8586 (Japan); Murata, Y. [Graduate School of Dental Medicine, Hokkaido University, Kita-13, Nishi-7, Kita-ku, Sapporo 060-8586 (Japan); Kijimura, T. [Graduate School of Dental Medicine, Hokkaido University, Kita-13, Nishi-7, Kita-ku, Sapporo 060-8586 (Japan); Sano, H. [Graduate School of Dental Medicine, Hokkaido University, Kita-13, Nishi-7, Kita-ku, Sapporo 060-8586 (Japan); Sakai, T. [Takasaki Advanced Radiation Research Institute, JAEA, 1233 Watanuki-machi, Takasaki 370-1292 (Japan); Kamiya, T. [Takasaki Advanced Radiation Research Institute, JAEA, 1233 Watanuki-machi, Takasaki 370-1292 (Japan)

    2007-07-15

    duration of pH cycling, although the enamel adjacent to the material remained a caries inhibition zone due to low rate of demineralization. With caries progression, fluorine accumulated in the subsurface of the caries lesion, while the outermost surface of the caries lesion gradually dissolved under increasing pH cycling. The data obtained using PIGE (TIARA, JAPAN) technique were useful to understand the fluorine benefit for preventing dental caries by means of fluoride-containing dental materials.

  7. A study in vitro on radiation effects by Er:YAG laser combined with the fluorine therapy in the acid resistance of the dental enamel submitted to orthodontical brackets

    International Nuclear Information System (INIS)

    Yoshiyasu, Roseli Y.A.

    2001-01-01

    Several researches have been demonstrating an increase in the resistance acid of the enamel surface when irradiated by some lasers types as Nd:YAG, C0 2 , Er:YAG, and others, mainly when combined with the fluoride therapy after the irradiation of the laser. This study in vitro used the laser of Er:YAG which density of energy of 8.1 J/cm 2 on the enamel about of orthodontical brackets of teeth extracted pre-molars. These teeth were then submitted to a rich way in S. mutans for twenty one days. The cases were analyzed: (1) enamel surface without any treatment, (2) enamel surface without any irradiation laser, but with therapy with acidulated phosphate fluoride, (3) enamel surface irradiated with laser of Er:YAG and (4) enamel surface irradiated by laser of Er:YAG and with application of acidulated phosphate fluoride. The results were analyzed through optical microscopy and scanning electron microscopy. The morphologic changes observed to the scanning electron microscopy suggest increase in the acid resistance of the enamel surface. However, to the optical microscopy, it was still possible to visualize undesirable white stains in the surface of the enamel. (author)

  8. Analysis of fluorine by nuclear reactions and applications to human dental enamel

    International Nuclear Information System (INIS)

    Stroobants, J.; Bodart, F.; Deconninck, G.; Demortier, G.; Nicolas, G.

    Nuclear reactions induced on Fluorine by low energy protons are investigated, thick target excitation yield curves and tables for 19 F(p,p'γ) 19 F and 19 F(p,αγ) 16 O reactions are given between 0.3 and 2.5 MeV. Interferences from other nuclear reactions, detection limits and sensitivity for Fluorine detection are investigated. After a wide investigation of the repartition of Fluorine in tooth enamel it is concluded that there is an equilibrium of the concentrations between tooth and saliva which is rapidly restored after the perturbation introduced by the external treatments. (author)

  9. Results of the topical in vitro and in vivo fluorination of dental enamel

    International Nuclear Information System (INIS)

    Baijot-Stroobants, J.; Deconninck, G.; Vreven, J.

    1978-01-01

    Fluorine in human enamel has been analysed by proton bombardment and detection of prompt γ-rays. Proton beam is used at atmospheric pressure; two different sets of experiments are reported: the first one consists in studying fluoridation effects on extracted teeth and the second one in making in vivo Fluorine determinations before and after topical applications. Several commercial gels and solutions have been tested with regard to their efficiency for Fluorine fixation: in vitro and in vivo results are in good agreement. (author)

  10. 3D scanning electron microscopy applied to surface characterization of fluorosed dental enamel.

    Science.gov (United States)

    Limandri, Silvina; Galván Josa, Víctor; Valentinuzzi, María Cecilia; Chena, María Emilia; Castellano, Gustavo

    2016-05-01

    The enamel surfaces of fluorotic teeth were studied by scanning electron stereomicroscopy. Different whitening treatments were applied to 25 pieces to remove stains caused by fluorosis and their surfaces were characterized by stereomicroscopy in order to obtain functional and amplitude parameters. The topographic features resulting for each treatment were determined through these parameters. The results obtained show that the 3D reconstruction achieved from the SEM stereo pairs is a valuable potential alternative for the surface characterization of this kind of samples. Copyright © 2016 Elsevier Ltd. All rights reserved.

  11. Dental management of patients irradiated for oral cancer

    International Nuclear Information System (INIS)

    Regezi, J.A.; Courtney, R.M.; Kerr, D.A.

    1976-01-01

    Management of patients irradiated for oral cancer should include consideration of their oral health prior to, and after, radiation therapy. Data from 130 patients, followed for a period of 1 to 10 years, are presented and evaluated. The philosophy of retention and maintenance of as many teeth as possible is supported by this data. Extraction of teeth with severe periodontal disease after irradiation also proves to be a relatively safe operation. Osteoradionecrosis tends to be limited in extent and is generally well tolerated by the patient when treated conservatively. A treatment regimen is presented that significantly reduces the morbidity from therapeutic irradiation of the jaws. A comprehensive dental evaluation and follow-up plan coupled with patient cooperation are instrumental to the success of this program

  12. Controlling dental enamel-cavity ablation depth with optimized stepping parameters along the focal plane normal using a three axis, numerically controlled picosecond laser.

    Science.gov (United States)

    Yuan, Fusong; Lv, Peijun; Wang, Dangxiao; Wang, Lei; Sun, Yuchun; Wang, Yong

    2015-02-01

    The purpose of this study was to establish a depth-control method in enamel-cavity ablation by optimizing the timing of the focal-plane-normal stepping and the single-step size of a three axis, numerically controlled picosecond laser. Although it has been proposed that picosecond lasers may be used to ablate dental hard tissue, the viability of such a depth-control method in enamel-cavity ablation remains uncertain. Forty-two enamel slices with approximately level surfaces were prepared and subjected to two-dimensional ablation by a picosecond laser. The additive-pulse layer, n, was set to 5, 10, 15, 20, 25, 30, 35, 40, 45, 50, 55, 60, 65, 70. A three-dimensional microscope was then used to measure the ablation depth, d, to obtain a quantitative function relating n and d. Six enamel slices were then subjected to three dimensional ablation to produce 10 cavities, respectively, with additive-pulse layer and single-step size set to corresponding values. The difference between the theoretical and measured values was calculated for both the cavity depth and the ablation depth of a single step. These were used to determine minimum-difference values for both the additive-pulse layer (n) and single-step size (d). When the additive-pulse layer and the single-step size were set 5 and 45, respectively, the depth error had a minimum of 2.25 μm, and 450 μm deep enamel cavities were produced. When performing three-dimensional ablating of enamel with a picosecond laser, adjusting the timing of the focal-plane-normal stepping and the single-step size allows for the control of ablation-depth error to the order of micrometers.

  13. In vitro evaluation of casein phosphopeptide-amorphous calcium phosphate effect on the shear bond strength of dental adhesives to enamel.

    Science.gov (United States)

    Shadman, Niloofar; Ebrahimi, Shahram Farzin; Shoul, Maryam Azizi; Sattari, Hasti

    2015-01-01

    Casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) is applied for remineralization of early caries lesions or tooth sensitivity conditions and may affect subsequent resin bonding. This in vitro study investigated the effect of CPP-ACP on the shear bond strength of dental adhesives to enamel. Sixty extracted human molar teeth were selected and randomly divided into three groups and six subgroups. Buccal or lingual surfaces of teeth were prepared to create a flat enamel surface. Adhesives used were Tetric N-Bond, AdheSE and AdheSE One F. In three subgroups, before applying adhesives, enamel surfaces were treated with Tooth Mousse CPP-ACP for one hour, rinsed and stored in 37°C temperature with 100% humidity. This procedure was repeated for 5 days and then adhesives were applied and Tetric N-Ceram composite was adhered to the enamel. This procedure was also fulfilled for the other three subgroups without CPP-ACP treatment. After 24 hour water storage, samples were tested for shear bond strength test in a universal testing machine. Failure modes were determined by stereomicroscope. Data were analyzed by t-test and one-way analysis of variance with P enamel only in Tetric N-Bond (P > 0.05). In non-applied CPP-ACP subgroups, there were statistically significant differences among all subgroups. Tetric N-Bond had the highest and AdheSE One F had the lowest shear bond strength. CPP-ACP application reduces the shear bond strength of AdheSE and AdheSE One F to enamel but not Tetric N-Bond.

  14. Effect of CPP-ACP paste with and without CO2 laser irradiation on demineralized enamel microhardness and bracket shear bond strength

    Directory of Open Access Journals (Sweden)

    Nasrin Farhadian

    Full Text Available ABSTRACT Introduction: Many patients seeking orthodontic treatment already have incipient enamel lesions and should be placed under preventive treatments. The aim of this in vitro study was to evaluate the effect of CPP-ACP paste and CO2 laser irradiation on demineralized enamel microhardness and shear bond strength of orthodontic brackets. Methods: Eighty caries-free human premolars were subjected to a demineralization challenge using Streptococcus mutans. After demineralization, the samples were randomly divided into five equal experimental groups: Group 1 (control, the brackets were bonded without any surface treatment; Group 2, the enamel surfaces were treated with CPP-ACP paste for 4 minutes before bonding; Group 3, the teeth were irradiated with CO2 laser beams at a wavelength of 10.6 µm for 20 seconds. The samples in Groups 4 and 5 were treated with CO2 laser either before or through CPP-ACP application. SEM photomicrographs of a tooth from each group were taken to observe the enamel surface. The brackets were bonded to the buccal enamel using a conventional method. Shear bond strength of brackets and ARI scores were measured. Vickers microhardness was measured on the non-bonded enamel surface. Data were analyzed with ANOVA and Tukey test at the p< 0.05 level. Results: The mean shear bond strength and microhardness of the laser group were higher than those in the control group and this difference was statistically significant (p< 0.05. All groups showed a higher percentage of ARI score 4. Conclusion: CO2 laser at a wavelength of 10.6 µm significantly increased demineralized enamel microhardness and enhanced bonding to demineralized enamel.

  15. Evaluation of external and internal irradiation on uranium mining enterprise staff by tooth enamel EPR spectroscopy

    Science.gov (United States)

    Zhumadilov, Kassym; Ivannikov, Alexander; Khailov, Artem; Orlenko, Sergei; Skvortsov, Valeriy; Stepanenko, Valeriy; Kuterbekov, Kairat; Toyoda, Shin; Kazymbet, Polat; Hoshi, Masaharu

    2017-11-01

    In order to estimate radiation effects on uranium enterprise staff and population teeth samples were collected for EPR tooth enamel dosimetry from population of Stepnogorsk city and staff of uranium mining enterprise in Shantobe settlment (Akmola region, North of Kazakhstan). By measurements of tooth enamel EPR spectra, the total absorbed dose in the enamel samples and added doses after subtraction of the contribution of natural background radiation are determined. For the population of Stepnogorsk city average added dose value of 4 +/- 11 mGy with variation of 51 mGy was obtained. For the staff of uranium mining enterprise in Shantobe settlment average value of added dose 95 +/- 20 mGy, with 85 mGy variation was obtained. Higher doses and the average value and a large variation for the staff, probably is due to the contribution of occupational exposure.

  16. Investigations on the uptake of 14C-labelled chlorhexidine diglutonate through dental enamel

    International Nuclear Information System (INIS)

    Stary, W.

    1981-01-01

    In this dissertation it was shown using radioactively labelled 14 C tracer molecules that chlorhexidine is adsorbed on the dental surface of extracted teeth. Evidence for this was provided by the three following methods: a) back diffusion and release in rinses; b) thin layer chromatography of the adsorbed substance, and c) autoradiography. (orig./MG) [de

  17. Crystallite size and lattice distortion of human dental enamel estimated from the integral width of x-ray diffraction peak profile

    International Nuclear Information System (INIS)

    Maruyama, Fumiaki; Sakae, Toshiro

    2000-01-01

    Crystallite size and lattice distortion of human dental enamel were estimated by peak profile analysis using x-ray diffraction pattern. Firstly, noises were removed from x-ray diffraction pattern, and deconvolution of overlapping peaks and determination of baseline level were carried out. Then, the instrumental peak broadening and effect of overlapping Kα1 and Kα2 were eliminated to obtain pure peak profile using the Stokes's Fourier method. The integral width method was applied for estimation of crystallite size and 'upper-limit of distortion', assuming the peak profile as Cauchy function. The estimated crystallite size and distortion were ca. 210 A and ca. 0.4% in the a-axis direction and ca. 550 A and ca. 0.7% in the c-axis direction, respectively. The crystallite size value along the a-axis was almost the same to the previously reported values, but the value for along the c-axis was nearly half of the reported values. The crystallite size in this study means the size of coherent domain in contrast to the size of particle which may contain several domains in the case of enamel crystals. The results suggest that human enamel crystals grow in their size along the c-axis by multiplication, fusion of crystallites. It was notable that the distortion value was larger in the c-axis direction. The phenomenon may partly be due to the high carbonate ion content of enamel crystals and partly due to crystal growth mechanism. (author)

  18. Influence of the number of cycles on shear fatigue strength of resin composite bonded to enamel and dentin using dental adhesives in self-etching mode.

    Science.gov (United States)

    Tsujimoto, Akimasa; Barkmeier, Wayne W; Erickson, Robert L; Takamizawa, Toshiki; Latta, Mark A; Miyazaki, Masashi

    2018-01-30

    The influence of the number of cycles on shear fatigue strength to enamel and dentin using dental adhesives in self-etch mode was investigated. A two-step self-etch adhesive and two universal adhesives were used to bond to enamel and dentin in self-etch mode. Initial shear bond strength and shear fatigue strength to enamel and dentin using the adhesive in self-etch mode were determined. Fatigue testing was used with 20 Hz frequency and cycling periods of 50,000, 100,000 and 1,000,000 cycles, or until failure occurred. For each of the cycling periods, there was no significant difference in shear fatigue strength across the cycling periods for the individual adhesives. Differences in shear fatigue strength were found between the adhesives within the cycling periods. Regardless of the adhesive used in self-etch mode for bonding to enamel or dentin, shear fatigue strength was not influenced by the number of cycles used for shear fatigue strength testing.

  19. A simple, sensitive and non-destructive technique for characterizing bovine dental enamel erosion: attenuated total reflection Fourier transform infrared spectroscopy.

    Science.gov (United States)

    Kim, In-Hye; Son, Jun Sik; Min, Bong Ki; Kim, Young Kyoung; Kim, Kyo-Han; Kwon, Tae-Yub

    2016-03-30

    Although many techniques are available to assess enamel erosion in vitro, a simple, non-destructive method with sufficient sensitivity for quantifying dental erosion is required. This study characterized the bovine dental enamel erosion induced by various acidic beverages in vitro using attenuated total reflection Fourier transform infrared (ATR-FTIR) spectroscopy. Deionized water (control) and 10 acidic beverages were selected to study erosion, and the pH and neutralizable acidity were measured. Bovine anterior teeth (110) were polished with up to 1 200-grit silicon carbide paper to produce flat enamel surfaces, which were then immersed in 20 mL of the beverages for 30 min at 37 °C. The degree of erosion was evaluated using ATR-FTIR spectroscopy and Vickers' microhardness measurements. The spectra obtained were interpreted in two ways that focused on the ν1, ν3 phosphate contour: the ratio of the height amplitude of ν3 PO4 to that of ν1 PO4 (Method 1) and the shift of the ν3 PO4 peak to a higher wavenumber (Method 2). The percentage changes in microhardness after the erosion treatments were primarily affected by the pH of the immersion media. Regression analyses revealed highly significant correlations between the surface hardness change and the degree of erosion, as detected by ATR-FTIR spectroscopy (Perosion.

  20. Residual heat deposition in dental enamel during IR laser ablation at 2.79, 2.94, 9.6, and 10.6 microm.

    Science.gov (United States)

    Fried, D; Ragadio, J; Champion, A

    2001-01-01

    The principal factor limiting the rate of laser ablation of dental hard tissue is the risk of excessive heat accumulation in the tooth. Excessive heat deposition or accumulation may result in unacceptable damage to the pulp. The objective of this study was to measure the residual heat deposition during the laser ablation of dental enamel at those IR laser wavelengths well suited for the removal of dental caries. Optimal laser ablation systems minimize the residual heat deposition in the tooth by efficiently transferring the deposited laser energy to kinetic and internal energy of ejected tissue components. The residual heat deposition in dental enamel was measured at laser wavelengths of 2.79, 2.94, 9.6, and 10.6 microm and pulse widths of 150 nsec -150 microsec using bovine block "calorimeters." Water droplets were applied to the surface before ablation with 150 microsec Er:YAG laser pulses to determine the influence of an optically thick water layer on reducing heat deposition. The residual heat was at a minimum for fluences well above the ablation threshold where measured values ranged from 25-70% depending on pulse duration and wavelength for the systems investigated. The lowest values of the residual heat were measured for short (heat deposition during ablation with 150 microsec Er:YAG laser pulses. Residual heat deposition can be markedly reduced by using CO(2) laser pulses of less than 20 microsec duration and shorter Q-switched Er:YAG and Er:YSGG laser pulses for enamel ablation. Copyright 2001 Wiley-Liss, Inc.

  1. In vivo Evaluation of Enamel Dental Restoration Interface by Optical Coherence Tomography

    International Nuclear Information System (INIS)

    Mota, Claudia C. B. O.; Gomes, Anderson S. L.; Kashyap, Hannah U. K. S.; Kyotoku, Bernardo B. C.

    2009-01-01

    In this work, we report in vivo application of Optical Coherence Tomography (OCT) to assess dental restorations in humans. After approval by the Ethical Committee in Humans Research of the Federal University of Pernambuco, thirty patients with resin composite restorations performed in anterior teeth were selected. The patients were clinically evaluated, and OCT was performed. Images were obtained using OCT operating in the spectral domain, with a 840 nm super luminescent diode light source (spectral width of 50 nm, fiber output power 25mW and a measured spatial resolution of 10 μm). The image acquisition time was less than one second. The results were analyzed with respect to the integrity and marginal adaptation of the restoration. Using appropriate software, the lesion region can be exactly located and a new restoration procedure can be carried out. We have shown that OCT is more than adequate in clinical practice to assess dental restorations. (Author)

  2. Effect of light irradiation on tooth whitening: enamel microhardness and color change.

    Science.gov (United States)

    Gomes, Mauricio Neves; Francci, Carlos; Medeiros, Igor Studart; De Godoy Froes Salgado, Nívea Regina; Riehl, Heraldo; Marasca, José Milton; Muench, Antônio

    2009-01-01

    The aim of this study was to evaluate the influence of light exposure associated with 35% hydrogen peroxide (Pola Office, SDI, Melbourne, Vic., Australia) or 15% hydrogen peroxide (BriteSmile, Discus, Culver City, CA, USA) on the microhardness and color changes of bovine enamel. Experimental groups were Britesmile + Light (BL) (15% hydrogen peroxide + plasm arc; 4 x 20 minutes), Britesmile + No Light (BN) (BL, no light), Pola office + Light (PL) (35% hydrogen peroxide + LED; 4 x 8 minutes), and Pola office + No light (PN) (PL, no light). Color changes (DeltaE) and the CIELAB (Commission Internationale de l' Eclairage, L* a* b* color system) parameters (L*, a*, and b*) were assessed with a spectrophotometer before (B), immediately (A), 1 day and 7 days after bleaching. The microhardness was measured before (B) and after (A), the obtained data were submitted to a two-way analysis of variance, and DeltaE were submitted to t-test for each period. Only Pola Office, in which the peroxide is associated with the light, improved DeltaE when evaluated immediately after bleaching (p enamel microhardness was not altered after bleaching for BriteSmile. However, enamel microhardness was reduced after bleaching for Pola Office, 283 MPa (+/-21) and 265 MPa (+/-27), respectively. It was concluded that these two bleaching systems were efficient regardless of the light systems used. However, the 35% hydrogen peroxide altered the enamel microhardness. CLINICAL SIGNIFICANCE Enamel microhardness was affected by a 35% hydrogen peroxide in-office bleaching therapy. Moreover, the in-office bleaching outcome was not improved by using the light associated with systems tested in this study. (J Esthet Restor Dent 21:387-396, 2009).

  3. Bonding efficacy of new self-etching, self-adhesive dual-curing resin cements to dental enamel.

    Science.gov (United States)

    Benetti, Paula; Fernandes, Virgílio Vilas; Torres, Carlos Rocha; Pagani, Clovis

    2011-06-01

    This study evaluated the efficacy of the union between two new self-etching self-adhesive resin cements and enamel using the microtensile bond strength test. Buccal enamel of 80 bovine teeth was submitted to finishing and polishing with metallographic paper to a refinement of #600, in order to obtain a 5-mm2 flat area. Blocks (2 x 4 x 4 mm) of laboratory composite resin were cemented to enamel according to different protocols: (1) untreated enamel + RelyX Unicem cement (RX group); (2) untreated enamel + Bifix SE cement (BF group); (3) enamel acid etching and application of resin adhesive Single Bond + RelyX Unicem (RXA group); (4) enamel acid etching and application of resin adhesive Solobond M + Bifix SE (BFA group). After 7 days of storage in distillated water at 37°C, the blocks were sectioned for obtaining microbar specimens with an adhesive area of 1 mm2 (n = 120). Specimens were submitted to the microtensile bond strength test at a crosshead speed of 0.5 mm/min. The results (in MPa) were analyzed statistically by ANOVA and Tukey's test. Enamel pre-treatment with phosphoric acid and resin adhesive (27.9 and 30.3 for RXA and BFA groups) significantly improved (p ≤ 0.05) the adhesion of both cements to enamel compared to the union achieved with as-polished enamel (9.9 and 6.0 for RX and BF). Enamel pre-treatment with acid etching and the application of resin adhesive significantly improved the bond efficacy of both luting agents compared to the union achieved with as-polished enamel.

  4. Systematic preservation of teeth and prophylaxis of dental decay on irradiated patients

    International Nuclear Information System (INIS)

    Horiot, J.C.; Schraub, S.

    1975-01-01

    200 patients were irradiated on the oral cavity and on salivary glands with doses of 3,000Rads and up. Teeth were preserved. A prophylactic treatment of dental decay was made using 5 minutes daily a fluoride gel into a carrier. The results showed an incidence of 5% for dental decay and 1% for osteo-radionecroses. Details are given about the selection of patients, the dental work-up and dental care before, during and after radiation therapy [fr

  5. Systematic preservation of teeth and prophylaxis of dental decay on irradiated patients. Preliminary results

    Energy Technology Data Exchange (ETDEWEB)

    Horiot, J C [Centre de Lutte contre le Cancer Georges-Francois-Leclerc, 21 - Dijon (France); Schraub, S [Centre Hospitalier Universitaire, 25 - Besancon (France)

    1975-11-01

    200 patients were irradiated on the oral cavity and on salivary glands with doses of 3,000 Rads and up. Teeth were preserved. A prophylactic treatment of dental decay was made using 5 minutes daily a fluoride gel into a carrier. The results showed an incidence of 5% for dental decay and 1% for osteo-radionecroses. Details are given about the selection of patients, the dental work-up and dental care before, during and after radiation therapy.

  6. Study on Dental Treatment with YAG Laser (1st Report): Temperature of Dental Tissue Irradiated with Laser Beam

    OpenAIRE

    上田, 隆司; 山田, 啓司; 古本, 達明

    2000-01-01

    The flash temperature of a dental hard tissue irradiated with pulsed Nd:YAG laser is measured using a two-color pyrometer with an optical fiber. This pyrometer consists of a chalcogenide optical fiber and a laminated infrared detector. The influence of the laser power on the temperature of the dental tissue is investigated, and the relationship between the laser power and the removal volume of the dental tissue is obtained. In order to examine the thermal damage on the dental tissue, hardness...

  7. In vitro evaluation of casein phosphopeptide-amorphous calcium phosphate effect on the shear bond strength of dental adhesives to enamel

    Directory of Open Access Journals (Sweden)

    Niloofar Shadman

    2015-01-01

    Full Text Available Background: Casein phosphopeptide-amorphous calcium phosphate (CPP-ACP is applied for remineralization of early caries lesions or tooth sensitivity conditions and may affect subsequent resin bonding. This in vitro study investigated the effect of CPP-ACP on the shear bond strength of dental adhesives to enamel. Materials and Methods: Sixty extracted human molar teeth were selected and randomly divided into three groups and six subgroups. Buccal or lingual surfaces of teeth were prepared to create a flat enamel surface. Adhesives used were Tetric N-Bond, AdheSE and AdheSE One F. In three subgroups, before applying adhesives, enamel surfaces were treated with Tooth Mousse CPP-ACP for one hour, rinsed and stored in 37°C temperature with 100% humidity. This procedure was repeated for 5 days and then adhesives were applied and Tetric N-Ceram composite was adhered to the enamel. This procedure was also fulfilled for the other three subgroups without CPP-ACP treatment. After 24 hour water storage, samples were tested for shear bond strength test in a universal testing machine. Failure modes were determined by stereomicroscope. Data were analyzed by t-test and one-way analysis of variance with P 0.05. In non-applied CPP-ACP subgroups, there were statistically significant differences among all subgroups. Tetric N-Bond had the highest and AdheSE One F had the lowest shear bond strength. Conclusion: CPP-ACP application reduces the shear bond strength of AdheSE and AdheSE One F to enamel but not Tetric N-Bond.

  8. Spectrophotometric evaluation of dental bleaching under orthodontic bracket in enamel and dentin

    Science.gov (United States)

    Correr, Americo-Bortolazzo; Rastelli, Alessandra-Nara-Souza; Lima, Débora-Alves-Nunes-Leite; Consani, Rafael-Leonardo-Xediek

    2014-01-01

    Aware of the diffusion capacity of bleaching in the dental tissues, many orthodontists are subjecting their patients to dental bleaching during orthodontic treatment for esthetic purposes or to anticipate the exchange of esthetic restorations after the orthodontic treatment. For this purpose specific products have been developed in pre-loaded whitening trays designed to fit over and around brackets and wires, with clinical efficacy proven. Objective: The objective of this study was to evaluate, through spectrophotometric reflectance, the effectiveness of dental bleaching under orthodontic bracket. Material and Methods: Thirty-two bovine incisors crown blocks of 8 mm x 8 mm height lengths were used. Staining of tooth blocks with black tea was performed for six days. They were distributed randomly into 4 groups (1-home bleaching with bracket, 2- home bleaching without bracket, 3- office bleaching with bracket, 4 office bleaching without bracket). The color evaluation was performed (CIE L * a * b *) using color reflectance spectrophotometer. Metal brackets were bonded in groups 1 and 3. The groups 1 and 2 samples were subjected to the carbamide peroxide at 15%, 4 hours daily for 21 days. Groups 3 and 4 were subjected to 3 in-office bleaching treatment sessions, hydrogen peroxide 38%. After removal of the brackets, the second color evaluation was performed in tooth block, difference between the area under the bracket and around it, and after 7 days to verified color stability. Data analysis was performed using the paired t-test and two-way variance analysis and Tukey’s. Results: The home bleaching technique proved to be more effective compared to the office bleaching. There was a significant difference between the margin and center color values of the specimens that were subjected to bracket bonding. Conclusions: The bracket bond presence affected the effectiveness of both the home and office bleaching treatments. Key words:Tooth bleaching, spectrophotometry

  9. In vitro study of dose-response relationship of fluoride with dental enamel

    Directory of Open Access Journals (Sweden)

    Arthur, Rodrigo Alex et al.

    2007-01-01

    Full Text Available Modelos in vitro para avaliação da reatividade do fluoreto (F devem apresentar resposta dose-efeito. Dessa forma, o objetivo desse estudo foi avaliar a relação dose-resposta do fluoreto presente em solução aquosa com o esmalte dental bovino. Cento e vinte blocos de esmalte bovino (5 × 5 × 2 mm, 60 hígidos e 60 com lesão artificial de cárie, foram submetidos durante 10 minutos à água destilada e deionizada (controle negativo e soluções aquosas contendo 50, 100, 200 ou 400 µg F/mL. Cada grupo experimental recebeu 12 blocos hígidos e 12 blocos com lesão artificial de cárie. Duas camadas consecutivas de esmalte dental foram removidas de todos os blocos dentais por meio de ataque ácido e o fluoreto extraído foi determinado com eletrodo específico. Os resultados de fluoreto incorporado foram expressos em µg por g de esmalte removido, considerando a quantidade total das duas camadas. A incorporação de fluoreto pelo esmalte hígido mostrou uma relação dose-resposta linear (p = 0,0001, enquanto que os blocos com lesão de cárie mostraram relação polinomial quadrática (p < 0,0001. Os resultados sugerem que o modelo in vitro de reatividade empregado no presente estudo é apropriado para avaliar a relação doseresposta entre o fluoreto em solução aquosa e aquele incorporado pelo esmalte dental bovino hígido ou com lesão artificial de cárie.

  10. Effect of irradiation on the dental pulp tissues in streptozotocin-induced diabetic rats

    International Nuclear Information System (INIS)

    Kang, Ho Duk; Hwang, Eui Hwan; Lee, Sang Rae

    2005-01-01

    To observe the histological changes in the pulp tissues of mandibular molars in streptozotocin-induced diabetic rats after irradiation. The male Sprague-Dawley rats weighing approximately 250 gm were divided into four groups : control, diabetes, irradiation, and diabetes-irradiation groups. Diabetes mellitus was induced in the rats by injecting streptozotocin. Rats in control and irradiation groups were injected with citrate buffer only. After 5 days, the head and neck region of the rats in irradiation and diabetes-irradiation groups were irradiated with a single absorbed dose of 10 Gy. All the rats were sacrificed at 3, 7, 14, 21, and 28 days after irradiation. The specimen including the mandibular molars were sectioned and observed using a histopathological method. In the diabetes group, capillary dilatation was observed. However, there was no obvious morphologic alteration of the odontoblasts. In the irradiation group, generalized necrosis of the dental pulp tissues was observed. Vacuolation of the odontoblasts and dilatation of the capillaries were noted in the early experimental phases. In the diabetes-irradiation group, generalized degeneration of the dental pulp tissues was observed. Vacuolation of the dental pulp cells and the odontoblasts was noted in the late experimental phases. This experiment suggest that dilatation of the capillaries in the dental pulp tissue is induced by diabetic state, and generalized degeneration of the dental pulp tissues is induced by irradiation of the diabetic group.

  11. Dental enamel Hypoplasia. Investigations on the Bones Exhumed from the Medieval Necropole of Lozova (Republic of Moldova, XIVth–XVth Centuries

    Directory of Open Access Journals (Sweden)

    Robert Daniel Simalcsik

    2014-10-01

    Full Text Available Dental hypoplasia is a developmental anomaly based on perturbations of amelogenesis. Hypoplasia defects are part of the unspecific quantitative indicators for the state of health and / or nutritional state during the formation of the dental buds. It is a response of the human organism to physiological stress. The incidence of this dysplasia in a past population can indicate its biological frailty in its attempt to adapt to the environmental changes. The osteological material was excavated in the interval 2010 – 2011 by archaeologists from the Archaeology Centre in Chisinau, from the Medieval cemetery of Lozova (Straseni County, Republic of Moldova, dated for the XIVth and XVth centuries. Fifty one skeletons from 50 inhumation graves have been excavated and analyzed so far. Only 40 individuals had most of their teeth present. The enamel hypoplasia is of linear transversal type, located on the labial surface of the dental crowns, in the median third. The canine is the most affected tooth, followed by the incisors. The incidence of dental enamel hypoplasia at population level (based on the data collected and on the number of graves excavates so far, which does not illustrate the entire population of the cemetery is 7.5%. The incidence of dental caries is 23.53%, of cribra orbitalia – 11.75%, and of cribra cranii externa – 1.96%. The results obtained for a relatively small rural community illustrate a good adaptation to the stressing environmental factors. The possible malnutrition and illness episodes suffered during early childhood were recovered along the growth and development processes.

  12. Estimation of accumulated dose of radiation by the method of ESR-spectrometry of dental enamel of mammals

    International Nuclear Information System (INIS)

    Serezhenkov, V.A.; Moroz, I.A.; Vanin, A.F.; Klevezal, G.A.

    1997-01-01

    ESR-spectrometry was used to investigate radiation-induced paramagnetic centers in enamel of mammals: carnivores (polar bear and fox), ungulates (reindeer, European bison, moose), and man. Values at half the microwave power saturation of the radiation signal, P 1/2 , evaluated at room temperature, was found to range from 16 to 26 mW for animals and man. A new approach to discrimination of the radiation induced signal from the total ESR spectrum of reindeer enamel is proposed. ''Dose-response'' dependencies of enamel of different species mammals were measured within the dose range from 0.48 up to 10.08 Gy. Estimations of ''radiosensitivity'' enamel of carnivores and ungulates showed good agreement with radiosensitivity enamel of man by ESR method. (Author)

  13. Influence of a Brazilian wild green propolis on the enamel mineral loss and Streptococcus mutans' count in dental biofilm.

    Science.gov (United States)

    Cardoso, Julia Gabiroboertz; Iorio, Natalia Lopes Pontes; Rodrigues, Luís Fernando; Couri, Maria Luiza Barra; Farah, Adriana; Maia, Lucianne Cople; Antonio, Andréa Gonçalves

    2016-05-01

    This study investigated the anti-demineralizing and antibacterial effects of a propolis ethanolic extract (EEP) against Streptococcus mutans dental biofilm. Blocks of sound bovine enamel (n=24) were fixed on polystyrene plates. S. mutans inoculum (ATCC 25175) and culture media were added (48 h-37 °C) to form biofilm. Blocks with biofilm received daily treatment (30 μL/1 min), for 5 days, as following: G1 (EEP 33.3%); G2 (chlorhexidine digluconate 0.12%); G3 (ethanol 80%); and G4 (Milli-Q water). G5 and G6 were blocks without biofilm that received only EEP and Milli-Q water, respectively. Final surface hardness was evaluated and the percentage of hardness loss (%HL) was calculated. The EEP extract pH and total solids were determined. S. mutans count was expressed by log10 scale of Colony-Forming Units (CFU/mL). One way ANOVA was used to compare results which differed at a 95% significance level. G2 presented the lowest average %HL value (68.44% ± 12.98) (p=0.010), while G4 presented the highest (90.49% ± 5.38%HL) (p=0.007). G1 showed %HL (84.41% ± 2.77) similar to G3 (87.80% ± 6.89) (p=0.477). Groups G5 and G6 presented %HL=16.11% ± 7.92 and 20.55% ± 10.65; respectively (p=0.952). G1 and G4 differed as regards to S. mutans count: 7.26 ± 0.08 and 8.29 ± 0.17 CFU/mL, respectively (p=0.001). The lowest bacterial count was observed in chlorhexidine group (G2=6.79 ± 0.10 CFU/mL) (p=0.043). There was no difference between S. mutans count of G3 and G4 (p=0.435). The EEP showed pH 4.8 and total soluble solids content=25.9 Brix. The EEP seems to be a potent antibacterial substance against S. mutans dental biofilm, but presented no inhibitory action on the de-remineralization of caries process. Copyright © 2016 Elsevier Ltd. All rights reserved.

  14. Resolution of the hydroxyapatite crystal lattice in bone and dental enamel by electron microscopy

    International Nuclear Information System (INIS)

    Selvig, K.A.

    1975-01-01

    The molecular and atomic structure of hydroxyapatite was studied by transmission electron microscopy. The form, size and packing of hydroxyapatite crystals in sections of bone and dental hard tissues could be determined. Lattice fringe patterns with repeat distances in the range 2.7-8.2 A occurred in images of individual crystals. On the basis of these fringes the true orientation of the crystals relative to the plane of sectioning was calculated. The observed crystal lattice spacings and interplanar angles were in close agreement with data derived from X-ray diffraction analysis. This study shows that the possibility exists of relating crystallographic analysis to the morphology and fine structure of calcified tissue in health and disease

  15. The effects of three different food acids on the attrition-corrosion wear of human dental enamel

    Science.gov (United States)

    Zhang, Yichi; Arsecularatne, Joseph A.; Hoffman, Mark

    2015-07-01

    With increased consumption of acidic drinks and foods, the wear of human teeth due to attrition in acidic environments is an increasingly important issue. Accordingly, the present paper investigates in vitro the wear of human enamel in three different acidic environments. Reciprocating wear tests in which an enamel cusp slides on an enamel flat surface were carried out using acetic, citric and lactic acid lubricants (at pH 3-3.5). Distilled water was also included as a lubricant for comparison. Focused ion beam milling and scanning electron microscopy imaging were then used to investigate the enamel subsurfaces following wear tests. Nanoindentation was used to ascertain the changes in enamel mechanical properties. The study reveals crack generation along the rod boundaries due to the exposure of enamel to the acidic environments. The wear mechanism changes from brittle fracture in distilled water to ploughing or shaving of the softened layer in acidic environments, generating a smooth surface with the progression of wear. Moreover, nanoindentation results of enamel samples which were exposed to the above acids up to a duration of the wear tests show decreasing hardness and Young’s modulus with exposure time.

  16. Application of the specular and diffuse reflection analysis for in vitro diagnostics of dental erosion: correlation with enamel softening, roughness, and calcium release

    Science.gov (United States)

    Rakhmatullina, Ekaterina; Bossen, Anke; Höschele, Christoph; Wang, Xiaojie; Beyeler, Barbara; Meier, Christoph; Lussi, Adrian

    2011-01-01

    We present assembly and application of an optical reflectometer for the analysis of dental erosion. The erosive procedure involved acid-induced softening and initial substance loss phases, which are considered to be difficult for visual diagnosis in a clinic. Change of the specular reflection signal showed the highest sensitivity for the detection of the early softening phase of erosion among tested methods. The exponential decrease of the specular reflection intensity with erosive duration was compared to the increase of enamel roughness. Surface roughness was measured by optical analysis, and the observed tendency was correlated with scanning electron microscopy images of eroded enamel. A high correlation between specular reflection intensity and measurement of enamel softening (r2 ≥ −0.86) as well as calcium release (r2 ≥ −0.86) was found during erosion progression. Measurement of diffuse reflection revealed higher tooth-to-tooth deviation in contrast to the analysis of specular reflection intensity and lower correlation with other applied methods (r2 = 0.42–0.48). The proposed optical method allows simple and fast surface analysis and could be used for further optimization and construction of the first noncontact and cost-effective diagnostic tool for early erosion assessment in vivo. PMID:22029364

  17. Application of the specular and diffuse reflection analysis for in vitro diagnostics of dental erosion: correlation with enamel softening, roughness, and calcium release

    Science.gov (United States)

    Rakhmatullina, Ekaterina; Bossen, Anke; Höschele, Christoph; Wang, Xiaojie; Beyeler, Barbara; Meier, Christoph; Lussi, Adrian

    2011-10-01

    We present assembly and application of an optical reflectometer for the analysis of dental erosion. The erosive procedure involved acid-induced softening and initial substance loss phases, which are considered to be difficult for visual diagnosis in a clinic. Change of the specular reflection signal showed the highest sensitivity for the detection of the early softening phase of erosion among tested methods. The exponential decrease of the specular reflection intensity with erosive duration was compared to the increase of enamel roughness. Surface roughness was measured by optical analysis, and the observed tendency was correlated with scanning electron microscopy images of eroded enamel. A high correlation between specular reflection intensity and measurement of enamel softening (r2 >= -0.86) as well as calcium release (r2 >= -0.86) was found during erosion progression. Measurement of diffuse reflection revealed higher tooth-to-tooth deviation in contrast to the analysis of specular reflection intensity and lower correlation with other applied methods (r2 = 0.42-0.48). The proposed optical method allows simple and fast surface analysis and could be used for further optimization and construction of the first noncontact and cost-effective diagnostic tool for early erosion assessment in vivo.

  18. β-pyrophosphate: A potential biomaterial for dental applications

    Energy Technology Data Exchange (ETDEWEB)

    Anastasiou, A.D., E-mail: a.anastasiou@leeds.ac.uk [School of Chemical and Process Engineering, University of Leeds, Leeds LS2 9JT (United Kingdom); Strafford, S. [Leeds Dental School, Worsley Building, University of Leeds, Leeds LS2 9JT (United Kingdom); Posada-Estefan, O. [Leeds Institute of Cardiovascular and Metabolic Medicine, Faculty of Medicine and Health, University of Leeds, LS2 9JT (United Kingdom); Thomson, C.L. [SUPA, School of Physics and Astronomy, University of St Andrews, North Haugh, St Andrews, Fife KY16 9SS (United Kingdom); Hussain, S.A. [SUPA, School of Physics and Astronomy, University of St Andrews, North Haugh, St Andrews, Fife KY16 9SS (United Kingdom); Cambridge Graphene Centre, Engineering Department, University of Cambridge, 9, JJ Thomson Avenue, Cambridge CB3 0FA (United Kingdom); Edwards, T.J. [SUPA, School of Physics and Astronomy, University of St Andrews, North Haugh, St Andrews, Fife KY16 9SS (United Kingdom); Malinowski, M. [Leeds Dental School, Worsley Building, University of Leeds, Leeds LS2 9JT (United Kingdom); Hondow, N. [School of Chemical and Process Engineering, University of Leeds, Leeds LS2 9JT (United Kingdom); Metzger, N.K.; Brown, C.T.A. [SUPA, School of Physics and Astronomy, University of St Andrews, North Haugh, St Andrews, Fife KY16 9SS (United Kingdom); Routledge, M.N. [Leeds Institute of Cardiovascular and Metabolic Medicine, Faculty of Medicine and Health, University of Leeds, LS2 9JT (United Kingdom); Brown, A.P. [School of Chemical and Process Engineering, University of Leeds, Leeds LS2 9JT (United Kingdom); Duggal, M.S. [Leeds Dental School, Worsley Building, University of Leeds, Leeds LS2 9JT (United Kingdom); Jha, A. [School of Chemical and Process Engineering, University of Leeds, Leeds LS2 9JT (United Kingdom)

    2017-06-01

    Tooth hypersensitivity is a growing problem affecting both the young and ageing population worldwide. Since an effective and permanent solution is not yet available, we propose a new methodology for the restoration of dental enamel using femtosecond lasers and novel calcium phosphate biomaterials. During this procedure the irradiated mineral transforms into a densified layer of acid resistant iron doped β-pyrophosphate, bonded with the surface of eroded enamel. Our aim therefore is to evaluate this densified mineral as a potential replacement material for dental hard tissue. To this end, we have tested the hardness of β-pyrophosphate pellets (sintered at 1000 °C) and its mineral precursor (brushite), the wear rate during simulated tooth-brushing trials and the cytocompatibility of these minerals in powder form. It was found that the hardness of the β-pyrophosphate pellets is comparable with that of dental enamel and significantly higher than dentine while, the brushing trials prove that the wear rate of β-pyrophosphate is much slower than that of natural enamel. Finally, cytotoxicity and genotoxicity tests suggest that iron doped β-pyrophosphate is cytocompatible and therefore could be used in dental applications. Taken together and with the previously reported results on laser irradiation of these materials we conclude that iron doped β-pyrophosphate may be a promising material for restoring acid eroded and worn enamel. - Highlights: • A novel procedure for the restoration of dental enamel is introduced. • Fe-doped ß-pyrophosphate is evaluated as potential biomaterial for enamel restoration. • Fe-doped ß-pyrophosphate found to have the same hardness as natural enamel and dramatically lower wear rate. • Cytotoxicity and genotoxicity tests suggest that Fe-doped ß-pyrophosphate is safe for dental applications.

  19. β-pyrophosphate: A potential biomaterial for dental applications

    International Nuclear Information System (INIS)

    Anastasiou, A.D.; Strafford, S.; Posada-Estefan, O.; Thomson, C.L.; Hussain, S.A.; Edwards, T.J.; Malinowski, M.; Hondow, N.; Metzger, N.K.; Brown, C.T.A.; Routledge, M.N.; Brown, A.P.; Duggal, M.S.; Jha, A.

    2017-01-01

    Tooth hypersensitivity is a growing problem affecting both the young and ageing population worldwide. Since an effective and permanent solution is not yet available, we propose a new methodology for the restoration of dental enamel using femtosecond lasers and novel calcium phosphate biomaterials. During this procedure the irradiated mineral transforms into a densified layer of acid resistant iron doped β-pyrophosphate, bonded with the surface of eroded enamel. Our aim therefore is to evaluate this densified mineral as a potential replacement material for dental hard tissue. To this end, we have tested the hardness of β-pyrophosphate pellets (sintered at 1000 °C) and its mineral precursor (brushite), the wear rate during simulated tooth-brushing trials and the cytocompatibility of these minerals in powder form. It was found that the hardness of the β-pyrophosphate pellets is comparable with that of dental enamel and significantly higher than dentine while, the brushing trials prove that the wear rate of β-pyrophosphate is much slower than that of natural enamel. Finally, cytotoxicity and genotoxicity tests suggest that iron doped β-pyrophosphate is cytocompatible and therefore could be used in dental applications. Taken together and with the previously reported results on laser irradiation of these materials we conclude that iron doped β-pyrophosphate may be a promising material for restoring acid eroded and worn enamel. - Highlights: • A novel procedure for the restoration of dental enamel is introduced. • Fe-doped ß-pyrophosphate is evaluated as potential biomaterial for enamel restoration. • Fe-doped ß-pyrophosphate found to have the same hardness as natural enamel and dramatically lower wear rate. • Cytotoxicity and genotoxicity tests suggest that Fe-doped ß-pyrophosphate is safe for dental applications.

  20. β-pyrophosphate: A potential biomaterial for dental applications

    OpenAIRE

    Anastasiou, AD; Strafford, S; Posada-Estefan, O; Thomson, CL; Hussaein, SA; Edwards, TJ; Malinowski, M; Hondow, N; Metzger, NK; Brown, CTA; Routledge, MN; Brown, AP; Duggal, MS; Jha, A

    2017-01-01

    Tooth hypersensitivity is a growing problem affecting both the young and ageing population worldwide. Since an effective and permanent solution is not yet available, we propose a new methodology for the restoration of dental enamel using femtosecond lasers and novel calcium phosphate biomaterials. During this procedure the irradiated mineral transforms into a densified layer of acid resistant iron doped β-pyrophosphate, bonded with the surface of eroded enamel. Our aim therefore is to evaluat...

  1. In vitro study of 960 nm high power diode laser applications in dental enamel, aided by the presence of a photoinitiator dye: scanning electron microscopy analysis; Estudo in vitro das aplicacoes do laser de diodo de alta potencia 960 nm em esmalte dentario, assistido por um fotoiniciador: analise de microscopia eletronica de varredura

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, Marcelo Vinicius de

    2002-06-15

    The objective of this study is to verify if a high power diode laser can effectively modify the morphology of an enamel surface, and if this can be done in a controlled fashion by changing the lasers parameters. Previous studies using SEM demonstrated that through irradiation with Nd:YAG laser (1064 nm) it is possible to modify the morphology of the dental surface in such way as to increase its resistance against caries decays. The desired procedures that should achieve a decrease of the index of caries decays and of its sequels are on a primary level, which means that action is necessary before the disease installs itself. In this study it was used for the first time a prototype of a high power diode laser operating at 960 nm, produced by the Laboratory of Development of Lasers of the Center for Lasers and Applications of the IPEN. This equipment can present several advantages as reliability, reduced size and low cost. The aim was establish parameters of laser irradiation that produce the desired effects wanted in the enamel and protocols that guarantee its safety during application in dental hard tissues, protecting it of heating effects such as fissures and carbonization. (author)

  2. Antibacterial activity against Streptococcus mutans and inhibition of bacterial induced enamel demineralization of propolis, miswak, and chitosan nanoparticles based dental varnishes.

    Science.gov (United States)

    Wassel, Mariem O; Khattab, Mona A

    2017-07-01

    Using natural products can be a cost-effective approach for caries prevention especially in low income countries where dental caries is highly prevalent and the resources are limited. Specially prepared dental varnishes containing propolis, miswak, and chitosan nanoparticles (CS-NPs) with or without sodium fluoride (NaF) were assessed for antibacterial effect against Streptococcus mutans ( S. mutans ) using disk diffusion test. In addition, the protective effect of a single pretreatment of primary teeth enamel specimens against in vitro bacterial induced enamel demineralization was assessed for 3 days. All natural products containing varnishes inhibited bacterial growth significantly better than 5% NaF varnish, with NaF loaded CS-NPs (CSF-NPs) showing the highest antibacterial effect, though it didn't significantly differ than those of other varnishes except miswak ethanolic extract (M) varnish. Greater inhibitory effect was noted with varnish containing freeze dried aqueous miswak extract compared to that containing ethanolic miswak extract, possibly due to concentration of antimicrobial substances by freeze drying. Adding natural products to NaF in a dental varnish showed an additive effect especially compared to fluoride containing varnish. 5% NaF varnish showed the best inhibition of demineralization effect. Fluoride containing miswak varnish (MF) and CSF-NPs varnish inhibited demineralization significantly better than all experimental varnishes, especially during the first 2 days, though CSF-NPs varnish had a low fluoride concentration, probably due to better availability of fluoride ions and the smaller size of nanoparticles. Incorporating natural products with fluoride into dental varnishes can be an effective approach for caries prevention, especially miswak and propolis when financial resources are limited.

  3. Effects of moisture conditions of dental enamel surface on bond strength of brackets bonded with moisture-insensitive primer adhesive system.

    Science.gov (United States)

    Endo, Toshiya; Ozoe, Rieko; Sanpei, Sugako; Shinkai, Koichi; Katoh, Yoshiroh; Shimooka, Shohachi

    2008-07-01

    The purposes of this study were to evaluate the effects of different degrees of water contamination on the shear bond strength of orthodontic brackets bonded to dental enamel with a moisture-insensitive primer (MIP) adhesive system and to compare the modes of bracket/adhesive failure. A total of 68 human premolars were divided into four groups by primers and enamel surface conditions (desiccated, blot dry, and overwet). In group I, the hydrophobic Transbond XT primer adhesive system was used under desiccated conditions for bonding the brackets; in group II, the hydrophilic Transbond MIP adhesive system was used under desiccated conditions; in group III, the hydrophilic Transbond MIP adhesive system was used under blot dry conditions; and in group IV, the hydrophilic Transbond MIP adhesive system was used under overwet conditions. Shear bond strength was measured with a universal testing machine, and the mode of bracket/adhesive failure was determined according to the adhesive remnant index. The mean shear bond strengths were not significantly different among groups I, II, and III, and were higher than the clinically required range of 6 to 8 MPa. The mean shear bond strength achieved in group IV was significantly lower than that achieved in groups I, II, and III, and also lower than the clinically required values. Bond failure occurred at the enamel-adhesive interface more frequently in group IV than in groups I and III. To achieve clinically sufficient bond strengths with the hydrophilic MIP adhesive system, excess water should be blotted from the water-contaminated enamel surface.

  4. Implications of gluten exposure period, CD clinical forms, and HLA typing in the association between celiac disease and dental enamel defects in children. A case-control study.

    Science.gov (United States)

    Majorana, Alessandra; Bardellini, Elena; Ravelli, Alberto; Plebani, Alessandro; Polimeni, Antonella; Campus, Guglielmo

    2010-03-01

    The association between coeliac disease (CD) and dental enamel defects (DED) is well known. The aim of this study was to investigate the prevalence of DED in children with CD and to specifically find the association of DED and gluten exposure period, CD clinical forms, HLA class II haplotype. This study was designed as a matched case-control study: 250 children were enrolled (125 coeliac children - 79 female and 46 male, 7.2 +/- 2.8 years and 125 healthy children). Data about age at CD diagnosis, CD clinical form, and HLA haplotype were recorded. Dental enamel defects were detected in 58 coeliac subjects (46.4%) against seven (5.6%) controls (P < 0.005). We found an association between DED and gluten exposure period, as among CD subjects the mean age at CD diagnosis was significantly (P = 0.0004) higher in the group with DED (3.41 +/- 1.27) than without DED (1.26 +/- 0.7). DED resulted more frequent (100%) in atypical and silent CD forms than in the typical one (30.93%). The presence of HLA DR 52-53 and DQ7antigens significantly increased the risk of DED (P = 0.0017) in coeliac children. Our results confirmed a possible correlation between HLA antigens and DED.

  5. The EPR investigation of tooth enamel for measurements of tooth enamel for measurements of absorbed gamma doses of people irradiated in Chernobyl accident

    International Nuclear Information System (INIS)

    Baran, N.P.; Barchuk, V.I.; Bar'yakhtar, V.G.; Bugaj, A.A.; Koval', G.N.; Maksimenko, V.M.; Berezhnoj, A.B.; Zakharash, M.P.; AN Ukrainskoj SSR, Kiev

    1993-01-01

    The EPR spectra of the tooth enamel of Chernobyl 'liquidators' were investigated. A lot of people were engaged in work at the Chernobyl area after the accident in 1986. A part of them is under regular medical control at the Ukrainian security service hospital. When patients lose the teeth for some reasons the EPR spectra of radiation centers in tooth enamel caused by emergency gamma radiation were investigated. The measurement of the intensities of the EPR spectra give the real individual absorbed doses of gamma radiation which are much higher than the official values registered in the medical cards of liquidators

  6. Effects of 45S5 bioglass on surface properties of dental enamel subjected to 35% hydrogen peroxide

    OpenAIRE

    Deng, Meng; Wen, Hai-Lin; Dong, Xiao-Li; Li, Feng; Xu, Xin; Li, Hong; Li, Ji-Yao; Zhou, Xue-Dong

    2013-01-01

    Tooth bleaching agents may weaken the tooth structure. Therefore, it is important to minimize any risks of tooth hard tissue damage caused by bleaching agents. The aim of this study was to evaluate the effects of applying 45S5 bioglass (BG) before, after, and during 35% hydrogen peroxide (HP) bleaching on whitening efficacy, physicochemical properties and microstructures of bovine enamel. Seventy-two bovine enamel blocks were prepared and randomly divided into six groups: distilled deionized ...

  7. An Analysis of Dental Enamel after Bleaching using 35% Hydrogen Peroxide with Energy-dispersive X-ray Spectroscopy

    OpenAIRE

    Asmawati, Dr. drg. Asmawati, M.Kes

    2017-01-01

    Hydrogen peroxide (H2O2) is an effective bleaching agent of tooth whitening, but its use causes changes in the chemical composition of the elements that configure tooth enamel. The purpose of this study is to determine whether there are changes in the composition of the elements that configure the tooth enamel after bleaching using 35% hydrogen peroxide. Background: Hydrogen peroxide (H2O2) is an effective bleaching agent of tooth whitening, but its use causes changes in the chemical compo...

  8. Ultrastructure of the surface of dental enamel with molar incisor hypomineralization (MIH) with and without acid etching.

    Science.gov (United States)

    Bozal, Carola B; Kaplan, Andrea; Ortolani, Andrea; Cortese, Silvina G; Biondi, Ana M

    2015-01-01

    The aim of the present work was to analyze the ultrastructure and mineral composition of the surface of the enamel on a molar with MIH, with and without acid etching. A permanent tooth without clinical MIH lesions (control) and a tooth with clinical diagnosis of mild and moderate MIH, with indication for extraction, were processed with and without acid etching (H3PO4 37%, 20") for observation with scanning electron microscope (SEM) ZEISS (Supra 40) and mineral composition analysis with an EDS detector (Oxford Instruments). The control enamel showed normal prismatic surface and etching pattern. The clinically healthy enamel on the tooth with MIH revealed partial loss of prismatic pattern. The mild lesion was porous with occasional cracks. The moderate lesion was more porous, with larger cracks and many scales. The mineral composition of the affected surfaces had lower Ca and P content and higher O and C. On the tooth with MIH, even on normal looking enamel, the demineralization does not correspond to an etching pattern, and exhibits exposure of crystals with rods with rounded ends and less demineralization in the inter-prismatic spaces. Acid etching increased the presence of cracks and deep pores in the adamantine structure of the enamel with lesion. In moderate lesions, the mineral composition had higher content of Ca, P and Cl. Enamel with MIH, even on clinically intact adamantine surfaces, shows severe alterations in the ultrastructure and changes in ionic composition, which affect the acid etching pattern and may interfere with adhesion.

  9. EPR dosimetry of irradiated human teeth

    International Nuclear Information System (INIS)

    Rodas Duran, J.E.; Panzeri, H.; Mascarenhas, S.

    1985-01-01

    The determination of the absorbed radiation dose in man may be made by Electron Paramagnetic Resonance (EPR) spectroscopy of dental enamel. We analysed the EPR signals for dental enamel submitted to gamma radiation in doses between 1 Gy and 25 Gy. We conclude that independent of the type of tooth analysed there exists a linear relation between the EPR signals and the absorbed doses. These studies were extended to enamel irradiated with gamma rays and with X rays in doses between 0.1 Gy and 0.6 Gy. The graph of the intensity of the EPR signals as a function of the dose has a slope of 0.22. This calibration may be used to calculate the absorbed dose for humans from a measurement of the EPR signal from small samples of enamel taken from any permanent tooth. Finally we comment on some EPR studies of effects of radiation of milk teeth. (author)

  10. Dental bleaching on teeth submitted to enamel microabrasion 30 years ago-a case report of patients' compliance during bleaching treatment.

    Science.gov (United States)

    Sundfeld, Daniel; Pavani, Caio Cesar; Schott, Timm Cornelius; Machado, Lucas Silveira; Pini, Núbia Inocêncya Pavesi; Bertoz, André Pinheiro de Magalhães; Sundfeld, Renato Herman

    2018-04-20

    The present dental bleaching case report describes a new method that precisely quantifies the daily wearing-times of the bleaching product by inserting a microsensor in the acetate custom tray. The bleaching efficacy was also discussed since the patient was previously submitted to enamel microabrasion. The patient was submitted to enamel microabrasion in 1987, and bleaching treatment was performed in 2005. In 2017, re-bleaching was executed using 10% peroxide carbamide. The electronic microsensor, TheraMon (TheraMon® microelectronic system; Sales Agency Gschladt, Hargelsberg, Austria), was embedded in the labial region of the upper and lower acetate trays to evaluate the wearing-times of the acetate trays/bleaching product. The patient was instructed to wear the tray for 6 to 8 h/day while sleeping. After 24 days of bleaching treatment, the data obtained from the TheraMon electronic devices was collected and interpreted. The patient did not entirely follow the bleaching treatment as recommended, as there was no evidence of use of the upper and lower trays for some days; additionally, the bleaching product was used for shorter and longer periods than was instructed. The TheraMon microeletronic device precisely measured the wearing-times of the acetate tray/bleaching product during the bleaching treatment. Teeth submitted to enamel microabrasion presented with a healthy clinical appearance after 30 years. Measuring the length and frequency of use of an acetate tray/bleaching product can be important to clinicians and patients for obtaining a controlled and adequate bleaching treatment.

  11. Caries like lesion initiation in sound enamel following CW CO2 laser irradiation: an in vitro study

    International Nuclear Information System (INIS)

    Nafie, A.; Issam, A.; Ali, M. S. R.

    2005-01-01

    This Study aimed to asses the caries - preventive potential of various CW CO 2 laser parameters, and to explore the effect of the laser power density, and the exposure time on the varies inhibition activity. Materials and Methods: Extracted human premolar teeth were irradiated with three different power densities (7.95, 15.9 and 31.8) W/Cm 2 for three different exposure times (0.2, 0.4 and 0.8) sec of 10.6 μm CW CO 2 laser. All teeth were subjected to caries like lesion formation by 3.5 pH lactic acid for 21 days. The teeth after that were sectioned into ground cross section and the lesion depths were measured using a graticule polarizing microscope. CW CO 2 laser preventive treatments inhibit caries like lesion progression up to 44%. This effect was improved with: (1) Increased power density for each of the three exposure times. (2) Decreased exposure time for each of the three power densities within the limits of the previously listed laser parameters. Conclusion: (1) short exposure time of CW CO 2 laser results in a significant inhibition of the enamel caries like lesion formation. (2) The inhibitory effect depends upon the power density and the exposure time of the laser beam. (3) The optimal CW CO 2 laser parameters used for caries inhibition purpose is achieved with approximately 30 W/Cm 2 power density and 0.2 sec exposure time. (author)

  12. In vitro studies of morphological changes in enamel surface after Er:YAG and Nd:YAG laser irradiation, by SEM

    International Nuclear Information System (INIS)

    Verlangieri, Eleonora Jaeger

    2001-01-01

    The caries prevention by using laser irradiation has been investigated by many authors using various lasers with different irradiations conditions. The purpose of this study was to investigated the morphological changes in enamel surface after Er:YAG and Nd:YAG laser irradiation, in vitro, by SEM. Fifteen freshly extracted, intact, caries-free, human third molars, were used in this study. The coronary portions were sectioned, from buccal to lingual direction, in two half-parts. Each one was irradiated by a different laser. The first one was irradiated with water-air spray, by a Nd:YAG laser, at 1.084 nm wave length, at 10 W, 10 Hz, 100 mJ for 60 sec., with an optical fiber in contact mode (0,32 mm of diameter); and the other half, with water-air spray by an Er:YAG laser at 2,94 micrometers wave length at the parameters of 4 Hz, 80 mJ, 24.95 J/cm 2 for 60 sec. The results of this study suggested that both lasers promoted morphological changes in the enamel surface enhancing resistance and can be an alternative clinical method for caries preventions. (author)

  13. Using dental enamel wrinkling to define sauropod tooth morphotypes from the Cañadón Asfalto Formation, Patagonia, Argentina.

    Directory of Open Access Journals (Sweden)

    Femke M Holwerda

    Full Text Available The early Middle Jurassic is regarded as the period when sauropods diversified and became major components of the terrestrial ecosystems. Not many sites yield sauropod material of this time; however, both cranial and postcranial material of eusauropods have been found in the Cañadón Asfalto Formation (latest Early Jurassic-early Middle Jurassic in Central Patagonia (Argentina, which may help to shed light on the early evolution of eusauropods. These eusauropod remains include teeth associated with cranial and mandibular material as well as isolated teeth found at different localities. In this study, an assemblage of sauropod teeth from the Cañadón Asfalto Formation found in four different localities in the area of Cerro Condor (Chubut, Argentina is used as a mean of assessing sauropod species diversity at these sites. By using dental enamel wrinkling, primarily based on the shape and orientation of grooves and crests of this wrinkling, we define and describe three different morphotypes. With the exception of one taxon, for which no cranial material is currently known, these morphotypes match the local eusauropod diversity as assessed based on postcranial material. Morphotype I is tentatively assigned to Patagosaurus, whereas morphotypes II and III correspond to new taxa, which are also distinguished by associated postcranial material. This study thus shows that enamel wrinkling can be used as a tool in assessing sauropod diversity.

  14. Using dental enamel wrinkling to define sauropod tooth morphotypes from the Cañadón Asfalto Formation, Patagonia, Argentina.

    Science.gov (United States)

    Holwerda, Femke M; Pol, Diego; Rauhut, Oliver W M

    2015-01-01

    The early Middle Jurassic is regarded as the period when sauropods diversified and became major components of the terrestrial ecosystems. Not many sites yield sauropod material of this time; however, both cranial and postcranial material of eusauropods have been found in the Cañadón Asfalto Formation (latest Early Jurassic-early Middle Jurassic) in Central Patagonia (Argentina), which may help to shed light on the early evolution of eusauropods. These eusauropod remains include teeth associated with cranial and mandibular material as well as isolated teeth found at different localities. In this study, an assemblage of sauropod teeth from the Cañadón Asfalto Formation found in four different localities in the area of Cerro Condor (Chubut, Argentina) is used as a mean of assessing sauropod species diversity at these sites. By using dental enamel wrinkling, primarily based on the shape and orientation of grooves and crests of this wrinkling, we define and describe three different morphotypes. With the exception of one taxon, for which no cranial material is currently known, these morphotypes match the local eusauropod diversity as assessed based on postcranial material. Morphotype I is tentatively assigned to Patagosaurus, whereas morphotypes II and III correspond to new taxa, which are also distinguished by associated postcranial material. This study thus shows that enamel wrinkling can be used as a tool in assessing sauropod diversity.

  15. The developmental clock of dental enamel: a test for the periodicity of prism cross-striations in modern humans and an evaluation of the most likely sources of error in histological studies of this kind

    Science.gov (United States)

    Antoine, Daniel; Hillson, Simon; Dean, M Christopher

    2009-01-01

    Dental tissues contain regular microscopic structures believed to result from periodic variations in the secretion of matrix by enamel- and dentine-forming cells. Counts of these structures are an important tool for reconstructing the chronology of dental development in both modern and fossil hominids. Most studies rely on the periodicity of the regular cross-banding that occurs along the long axis of enamel prisms. These prism cross-striations are widely thought to reflect a circadian rhythm of enamel matrix secretion and are generally regarded as representing daily increments of tissue. Previously, some researchers have argued against the circadian periodicity of these structures and questioned their use in reconstructing dental development. Here we tested the periodicity of enamel cross-striations – and the accuracy to which they can be used – in the developing permanent dentition of five children, excavated from a 19th century crypt in London, whose age-at-death was independently known. The interruption of crown formation by death was used to calibrate cross-striation counts. All five individuals produced counts that were strongly consistent with those expected from the independently known ages, taking into account the position of the neonatal line and factors of preservation. These results confirm that cross-striations do indeed reflect a circadian rhythm in enamel matrix secretion. They further validate their use in reconstructing dental development and in determining the age-at-death of the remains of children whose dentitions are still forming at the time of death. Significantly they identify the most likely source of error and the common difficulties encountered in histological studies of this kind. PMID:19166472

  16. Effects of 45S5 bioglass on surface properties of dental enamel subjected to 35% hydrogen peroxide.

    Science.gov (United States)

    Deng, Meng; Wen, Hai-Lin; Dong, Xiao-Li; Li, Feng; Xu, Xin; Li, Hong; Li, Ji-Yao; Zhou, Xue-Dong

    2013-06-01

    Tooth bleaching agents may weaken the tooth structure. Therefore, it is important to minimize any risks of tooth hard tissue damage caused by bleaching agents. The aim of this study was to evaluate the effects of applying 45S5 bioglass (BG) before, after, and during 35% hydrogen peroxide (HP) bleaching on whitening efficacy, physicochemical properties and microstructures of bovine enamel. Seventy-two bovine enamel blocks were prepared and randomly divided into six groups: distilled deionized water (DDW), BG, HP, BG before HP, BG after HP and BG during HP. Colorimetric and microhardness tests were performed before and after the treatment procedure. Representative specimens from each group were selected for morphology investigation after the final tests. A significant color change was observed in group HP, BG before HP, BG after HP and BG during HP. The microhardness loss was in the following order: group HP>BG before HP, BG after HP>BG during HP>DDW, BG. The most obvious morphological alteration of was observed on enamel surfaces in group HP, and a slight morphological alteration was also detected in group BG before HP and BG after HP. Our findings suggest that the combination use of BG and HP could not impede the tooth whitening efficacy. Using BG during HP brought better protective effect than pre/post-bleaching use of BG, as it could more effectively reduce the mineral loss as well as retain the surface integrity of enamel. BG may serve as a promising biomimetic adjunct for bleaching therapy to prevent/restore the enamel damage induced by bleaching agents.

  17. Enamel proteins mitigate mechanical and structural degradations in mature human enamel during acid attack

    Science.gov (United States)

    Lubarsky, Gennady V.; Lemoine, Patrick; Meenan, Brian J.; Deb, Sanjukta; Mutreja, Isha; Carolan, Patrick; Petkov, Nikolay

    2014-04-01

    A hydrazine deproteination process was used to investigate the role of enamel proteins in the acid erosion of mature human dental enamel. Bright field high resolution transmission electron micrographs and x-ray diffraction analysis show no crystallographic changes after the hydrazine treatment with similar nanoscale hydroxyapatite crystallite size and orientation for sound and de-proteinated enamel. However, the presence of enamel proteins reduces the erosion depth, the loss of hardness and the loss of structural order in enamel, following exposure to citric acid. Nanoindentation creep is larger for sound enamel than for deproteinated enamel but it reduces in sound enamel after acid attack. These novel results are consistent with calcium ion-mediated visco-elasticty in enamel matrix proteins as described previously for nacre, bone and dental proteins. They are also in good agreement with a previous double layer force spectroscopy study by the authors which found that the proteins electrochemically buffer enamel against acid attack. Finally, this suggests that acid attack, and more specifically dental erosion, is influenced by ionic permeation through the enamel layer and that it is mitigated by the enamel protein matrix.

  18. Enamel proteins mitigate mechanical and structural degradations in mature human enamel during acid attack

    International Nuclear Information System (INIS)

    Lubarsky, Gennady V; Lemoine, Patrick; Meenan, Brian J; Deb, Sanjukta; Mutreja, Isha; Carolan, Patrick; Petkov, Nikolay

    2014-01-01

    A hydrazine deproteination process was used to investigate the role of enamel proteins in the acid erosion of mature human dental enamel. Bright field high resolution transmission electron micrographs and x-ray diffraction analysis show no crystallographic changes after the hydrazine treatment with similar nanoscale hydroxyapatite crystallite size and orientation for sound and de-proteinated enamel. However, the presence of enamel proteins reduces the erosion depth, the loss of hardness and the loss of structural order in enamel, following exposure to citric acid. Nanoindentation creep is larger for sound enamel than for deproteinated enamel but it reduces in sound enamel after acid attack. These novel results are consistent with calcium ion-mediated visco-elasticty in enamel matrix proteins as described previously for nacre, bone and dental proteins. They are also in good agreement with a previous double layer force spectroscopy study by the authors which found that the proteins electrochemically buffer enamel against acid attack. Finally, this suggests that acid attack, and more specifically dental erosion, is influenced by ionic permeation through the enamel layer and that it is mitigated by the enamel protein matrix. (papers)

  19. Efficacy of Microwave Disinfection on Moist and Dry Dental Stone Casts with Different Irradiation Times

    Directory of Open Access Journals (Sweden)

    Mahmood Robati Anaraki

    2015-07-01

    Full Text Available Objectives: Dental practice contains the use of instruments and multiuse items that should be sterilized or disinfected properly. The aim of the current study was to investigate the effect of microwave irradiation on dental stone cast disinfection in moist and dry condition. Materials and Methods: In this in vitro study, 76 stone casts were prepared by a sterile method. The casts were contaminated by Pseudomonas aeruginosa (ATCC 9027, Staphylococcus aureus (ATCC 6538, Enterococcus faecalis (ATCC 29212 as well as Candida albicans (ATCC 10231. Half the samples were dried for two hours and the other half was studied while still moist. The samples were irradiated by a household microwave at 600 W for 3, 5 and 7 minutes. The microorganisms on the samples were extracted by immersion in tryptic soy broth and .001 ml of that was cultured in nutrient agar media, incubated overnight and counted and recorded as colony forming unit per milliliter (CFU/mL. Results: The findings showed that microorganisms reduced to 4.87 logarithm of CFU/mL value on dental cast within seven minutes in comparison with positive control. Although microbial count reduction was observed as a result of exposure time increase, comparison between moist and dried samples showed no significant difference. Conclusions: Seven-minute microwave irradiation at 600 W can effectively reduce the microbial load of dental stone casts. Wetting the casts does not seem to alter the efficacy of irradiation.   Keywords: Microwave Disinfection; Dental Stone Casts; Irradiation Times

  20. Theobromine Effects on Enamel Surface Microhardness: In Vitro

    OpenAIRE

    Grace Syafira; Rina Permatasari; Nina Wardani

    2013-01-01

    Dental caries is still a dental health problem in Indonesia. Fluoride, one of the dental caries prevention material, but its safety and the danger of fluorosis is still debated. Theobromine is an alkaloid compound contained in cocoa beans. Theobromine is believed to increase enamel microhardness with mineral changes in the enamel superficial layer. Objectives: To determine the influence of theobromine on the enamel surface microhardness. Methods: This study used 40 premolar tooth crown pieces...

  1. Evaluation of the effect of different methods of microabrasion and polishing on surface roughness of dental enamel.

    Science.gov (United States)

    Bertoldo, Carlos; Lima, Debora; Fragoso, Larissa; Ambrosano, Glaucia; Aguiar, Flavio; Lovadino, Jose

    2014-01-01

    The microabrasion technique of enamel consists of selectively abrading the discolored areas or causing superficial structural changes in a selective way. In microabrasion technique, abrasive products associated with acids are used, and the evaluation of enamel roughness after this treatment, as well as surface polishing, is necessary. This in-vitro study evaluated the enamel roughness after microabrasion, followed by different polishing techniques. Roughness analyses were performed before microabrasion (L1), after microabrasion (L2), and after polishing (L3).Thus, 60 bovine incisive teeth divided into two groups were selected (n=30): G1- 37% phosphoric acid (37%) (Dentsply) and pumice; G2- hydrochloric acid (6.6%) associated with silicon carbide (Opalustre - Ultradent). Thereafter, the groups were divided into three sub-groups (n=10), according to the system of polishing: A - Fine and superfine granulation aluminum oxide discs (SofLex 3M); B - Diamond Paste (FGM) associated with felt discs (FGM); C - Silicone tips (Enhance - Dentsply). A PROC MIXED procedure was applied after data exploratory analysis, as well as the Tukey-Kramer test (5%). No statistical differences were found between G1 and G2 groups. L2 differed statistically from L1 and showed superior amounts of roughness. Differences in the amounts of post-polishing roughness for specific groups (1A, 2B, and 1C) arose, which demonstrated less roughness in L3 and differed statistically from L2 in the polishing system. All products increased enamel roughness, and the effectiveness of the polishing systems was dependent upon the abrasive used.

  2. An investigation using atomic force microscopy nanoindentation of dental enamel demineralization as a function of undissociated acid concentration and differential buffer capacity

    International Nuclear Information System (INIS)

    Barbour, Michele E; Shellis, R Peter

    2007-01-01

    Acidic drinks and foodstuffs can demineralize dental hard tissues, leading to a pathological condition known as dental erosion, which is of increasing clinical concern. The first step in enamel dissolution is a demineralization of the outer few micrometres of tissue, which results in a softening of the structure. The primary determinant of dissolution rate is pH, but the concentration of undissociated acid, which is related to buffer capacity, also appears to be important. In this study, atomic force microscopy nanoindentation was used to measure the first initial demineralization (softening) induced within 1 min by exposure to solutions with a range of undissociated acid concentration and natural pH of 3.3 or with an undissociated acid concentration of 10 mmol l -1 and pH adjusted to 3.3. The results indicate that differential buffering capacity is a better determinant of softening than undissociated acid concentration. Under the conditions of these experiments, a buffer capacity of >3 mmol l -1 pH -1 does not have any further effect on dissolution rate. These results imply that differential buffering capacity should be used for preference over undissociated acid concentration or titratable acidity, which are more commonly employed in the literature

  3. An investigation using atomic force microscopy nanoindentation of dental enamel demineralization as a function of undissociated acid concentration and differential buffer capacity

    Science.gov (United States)

    Barbour, Michele E.; Shellis, R. Peter

    2007-02-01

    Acidic drinks and foodstuffs can demineralize dental hard tissues, leading to a pathological condition known as dental erosion, which is of increasing clinical concern. The first step in enamel dissolution is a demineralization of the outer few micrometres of tissue, which results in a softening of the structure. The primary determinant of dissolution rate is pH, but the concentration of undissociated acid, which is related to buffer capacity, also appears to be important. In this study, atomic force microscopy nanoindentation was used to measure the first initial demineralization (softening) induced within 1 min by exposure to solutions with a range of undissociated acid concentration and natural pH of 3.3 or with an undissociated acid concentration of 10 mmol l-1 and pH adjusted to 3.3. The results indicate that differential buffering capacity is a better determinant of softening than undissociated acid concentration. Under the conditions of these experiments, a buffer capacity of >3 mmol l-1 pH-1 does not have any further effect on dissolution rate. These results imply that differential buffering capacity should be used for preference over undissociated acid concentration or titratable acidity, which are more commonly employed in the literature.

  4. Thermal stress in dentin and enamel under CO2 laser irradiation

    Science.gov (United States)

    Meyer, Dirk H.; Foth, Hans-Jochen

    1996-01-01

    Ablation of dentin and tartar was studied under carbon dioxide-laser irradiation in cw and pulse mode with pulse length down to 150 microseconds. The specimens had been cut by a diamant blade to slices of thicknesses between 0.8 and 2.8 mm. The laser induced temperature rise was measured by an infrared camera monitoring the backside of the samples. The specimens shape and structure at the laser spot was analyzed by electron microscopy. Of special interest was the testing of the SwiftLaseTM to reducing the heat. The experimental results show the necessity of a water cooling in all application modes. The origin of the cracks which had been observed in many of the samples, is currently under investigation.

  5. Viability of dental implants in head and neck irradiated patients: A systematic review.

    Science.gov (United States)

    Zen Filho, Edson Virgílio; Tolentino, Elen de Souza; Santos, Paulo Sérgio Silva

    2016-04-01

    The purpose of this systematic review was to evaluate the safety of dental implants placed in irradiated bone and to discuss their viability when placed post-radiotherapy (RT). A systematic review was performed to answer the questions: "Are dental implants in irradiated bone viable?" and "What are the main factors that influence the loss of implants in irradiated patients?" The search strategy resulted in 8 publications. A total of 331 patients received 1237 implants, with an overall failure rate of 9.53%. The osseointegration success rates ranged between 62.5% and 100%. The optimal time interval between irradiation and dental implantation varied from 6 to 15 months. The interval time between RT and implant placement and the radiation doses are not associated with significant implant failure rates. The placement of implants in irradiated bone is viable, and head and neck RT should not be considered as a contraindication for dental rehabilitation with implants. © 2015 Wiley Periodicals, Inc. Head Neck 38: E2229-E2240, 2016. © 2015 Wiley Periodicals, Inc.

  6. A study in vitro on radiation effects by Er:YAG laser combined with the fluorine therapy in the acid resistance of the dental enamel submitted to orthodontical brackets; Um estudo in vitro sobre os efeitos da irradiacao pelo laser de Er:YAG combinado com a terapia com fluor na resistencia acida do esmalte de dentes submetidos a aparelho ortodontico fixo

    Energy Technology Data Exchange (ETDEWEB)

    Yoshiyasu, Roseli Y A

    2001-07-01

    Several researches have been demonstrating an increase in the resistance acid of the enamel surface when irradiated by some lasers types as Nd:YAG, C0{sub 2}, Er:YAG, and others, mainly when combined with the fluoride therapy after the irradiation of the laser. This study in vitro used the laser of Er:YAG which density of energy of 8.1 J/cm{sup 2} on the enamel about of orthodontical brackets of teeth extracted pre-molars. These teeth were then submitted to a rich way in S. mutans for twenty one days. The cases were analyzed: (1) enamel surface without any treatment, (2) enamel surface without any irradiation laser, but with therapy with acidulated phosphate fluoride, (3) enamel surface irradiated with laser of Er:YAG and (4) enamel surface irradiated by laser of Er:YAG and with application of acidulated phosphate fluoride. The results were analyzed through optical microscopy and scanning electron microscopy. The morphologic changes observed to the scanning electron microscopy suggest increase in the acid resistance of the enamel surface. However, to the optical microscopy, it was still possible to visualize undesirable white stains in the surface of the enamel. (author)

  7. Retrospective biodosimetry with small tooth enamel samples using K-Band and X-Band

    International Nuclear Information System (INIS)

    Gomez, Jorge A.; Kinoshita, Angela; Leonor, Sergio J.; Belmonte, Gustavo C.; Baffa, Oswaldo

    2011-01-01

    In an attempt to make the in vitro electron spin resonance (ESR) retrospective dosimetry of the tooth enamel a lesser invasive method, experiments using X-Band and K-Band were performed, aiming to determine conditions that could be used in cases of accidental exposures. First, a small prism from the enamel was removed and ground with an agate mortar and pestle until particles reach a diameter of approximately less than 0.5 mm. This enamel extraction process resulted in lower signal artifact compared with the direct enamel extraction performed with a diamond burr abrasion. The manual grinding of the enamel does not lead to any induced ESR signal artifact, whereas the use of a diamond burr at low speed produces a signal artifact equivalent to the dosimetric signal induced by a dose of 500 mGy of gamma irradiation. A mass of 25 mg of enamel was removed from a sound molar tooth previously irradiated in vitro with a dose of 100 mGy. This amount of enamel was enough to detect the dosimetric signal in a standard X-Band spectrometer. However using a K-Band spectrometer, samples mass between 5 and 10 mg were sufficient to obtain the same sensitivity. An overall evaluation of the uncertainties involved in the process in this and other dosimetric assessments performed at our laboratory indicates that it is possible at K-Band to estimate a 100 mGy dose with 25% accuracy. In addition, the use of K-Band also presented higher sensitivity and allowed the use of smaller sample mass in comparison with X-Band. Finally, the restoration process performed on a tooth after extraction of the 25 mg of enamel is described. This was conducted by dental treatment using photopolymerizable resin which enabled complete recovery of the tooth from the functional and aesthetic viewpoint showing that this procedure can be minimally invasive.

  8. Retrospective biodosimetry with small tooth enamel samples using K-Band and X-Band

    Energy Technology Data Exchange (ETDEWEB)

    Gomez, Jorge A. [Departamento de Fisica, FFCLRP, Universidade de Sao Paulo, 14040-901 Ribeirao Preto, Sao Paulo (Brazil); Kinoshita, Angela [Departamento de Fisica, FFCLRP, Universidade de Sao Paulo, 14040-901 Ribeirao Preto, Sao Paulo (Brazil); Universidade Sagrado Coracao - USC, 17011-160 Bauru, Sao Paulo (Brazil); Leonor, Sergio J. [Departamento de Fisica, FFCLRP, Universidade de Sao Paulo, 14040-901 Ribeirao Preto, Sao Paulo (Brazil); Belmonte, Gustavo C. [Universidade Sagrado Coracao - USC, 17011-160 Bauru, Sao Paulo (Brazil); Baffa, Oswaldo, E-mail: baffa@usp.br [Departamento de Fisica, FFCLRP, Universidade de Sao Paulo, 14040-901 Ribeirao Preto, Sao Paulo (Brazil)

    2011-09-15

    In an attempt to make the in vitro electron spin resonance (ESR) retrospective dosimetry of the tooth enamel a lesser invasive method, experiments using X-Band and K-Band were performed, aiming to determine conditions that could be used in cases of accidental exposures. First, a small prism from the enamel was removed and ground with an agate mortar and pestle until particles reach a diameter of approximately less than 0.5 mm. This enamel extraction process resulted in lower signal artifact compared with the direct enamel extraction performed with a diamond burr abrasion. The manual grinding of the enamel does not lead to any induced ESR signal artifact, whereas the use of a diamond burr at low speed produces a signal artifact equivalent to the dosimetric signal induced by a dose of 500 mGy of gamma irradiation. A mass of 25 mg of enamel was removed from a sound molar tooth previously irradiated in vitro with a dose of 100 mGy. This amount of enamel was enough to detect the dosimetric signal in a standard X-Band spectrometer. However using a K-Band spectrometer, samples mass between 5 and 10 mg were sufficient to obtain the same sensitivity. An overall evaluation of the uncertainties involved in the process in this and other dosimetric assessments performed at our laboratory indicates that it is possible at K-Band to estimate a 100 mGy dose with 25% accuracy. In addition, the use of K-Band also presented higher sensitivity and allowed the use of smaller sample mass in comparison with X-Band. Finally, the restoration process performed on a tooth after extraction of the 25 mg of enamel is described. This was conducted by dental treatment using photopolymerizable resin which enabled complete recovery of the tooth from the functional and aesthetic viewpoint showing that this procedure can be minimally invasive.

  9. Influence of an oxygen-inhibited layer on enamel bonding of dental adhesive systems: surface free-energy perspectives.

    Science.gov (United States)

    Ueta, Hirofumi; Tsujimoto, Akimasa; Barkmeier, Wayne W; Oouchi, Hajime; Sai, Keiichi; Takamizawa, Toshiki; Latta, Mark A; Miyazaki, Masashi

    2016-02-01

    The influence of an oxygen-inhibited layer (OIL) on the shear bond strength (SBS) to enamel and surface free-energy (SFE) of adhesive systems was investigated. The adhesive systems tested were Scotchbond Multipurpose (SM), Clearfil SE Bond (CS), and Scotchbond Universal (SU). Resin composite was bonded to bovine enamel surfaces to determine the SBS, with and without an OIL, of adhesives. The SFE of cured adhesives with and without an OIL were determined by measuring the contact angles of three test liquids. There were no significant differences in the mean SBS of SM and CS specimens with or without an OIL; however, the mean SBS of SU specimens with an OIL was significantly higher than that of SU specimens without an OIL. For all three systems, the mean total SFE (γS), polarity force (γSp), and hydrogen bonding force (γSh) values of cured adhesives with an OIL were significantly higher than those of cured adhesives without an OIL. The results of this study indicate that the presence of an OIL promotes higher SBS of a single-step self-etch adhesive system, but not of a three-step or a two-step self-etch primer system. The SFE values of cured adhesives with an OIL were significantly higher than those without an OIL. The SFE characteristics of the OIL of adhesives differed depending on the type of adhesive. © 2015 Eur J Oral Sci.

  10. Protection of enamel surfaces in the oral cavity

    DEFF Research Database (Denmark)

    Lazovic, Maja Bruvo

    The two main diseases that can affect the tooth enamel are dental caries and dental erosion, which both are caused by exposure of the enamel surfaces to acids. In the case of dental caries, acids from bacterial metabolism cause chemical dissolution of the tooth surface, whereas acids from drinks...... and foodstuffs or gastric juice can cause dental erosion. During a lifetime the enamel surface is also exposed to fluids that can have protective effects against dental caries and erosion such as saliva, various foodstuffs, drinking water and many types of drinks. However, little is still known about simple...... inorganic interactions between different fluids and dental caries and little is also known about which saliva proteins are able to protect the enamel surface against dental erosion. Therefore, the overall aim of this thesis was to examine simple inorganic and protein related protective effects with dental...

  11. Effect of Er,Cr:YSGG laser irradiation on bovine enamel surface during in-office tooth bleaching ex vivo.

    Science.gov (United States)

    Dionysopoulos, Dimitrios; Strakas, Dimitrios; Koliniotou-Koumpia, Eugenia; Koumpia, Effimia

    2017-07-01

    The aim of this in vitro study was to evaluate the effect of using Er,Cr:YSGG laser during in-office tooth bleaching on bovine enamel surface to evaluate the safety of this therapy on tooth tissues. Thirty-six enamel specimens were prepared from bovine incisors and divided into three groups: Group 1 specimens (control) received no bleaching treatment; Group 2 received a conventional in-office bleaching treatment (40 % H 2 O 2 ); Group 3 received laser-assisted bleaching procedure (40 % H 2 O 2 ) utilizing an Er,Cr:YSGG laser. The specimens were stored for 10 days after the bleaching treatment in artificial saliva. Vickers hardness was determined using a microhardness tester, and measurements for surface roughness were done using a VSI microscope. Three specimens for each experimental group were examined under SEM and mineral composition of the specimens was evaluated using EDS. Data were statistically analyzed using one-way ANOVA, Tukey's post hoc, Wilcoxon signed rank and Kruskal-Wallis tests (a = 0.05). The Vickers hardness of the enamel was reduced after in-office bleaching procedures (p  0.05), and no changes in mineral composition of the enamel were detected after in-office bleaching procedures (p > 0.05). The laser-assisted bleaching treatment with Er,Cr:YSGG laser did not influence the enamel surface compared to the conventional bleaching technique. The safety of the use of Er,Cr:YSGG laser during in-office tooth bleaching regarding the surface properties of the enamel was confirmed under in vitro conditions.

  12. Fluorine uptake into human enamel around fluoride-containing dental materials during cariogenic pH cycling

    International Nuclear Information System (INIS)

    Komatsu, H.; Yamamoto, H.; Nomachi, M.; Yasuda, K.; Matsuda, Y.; Kinugawa, M.; Kijimura, T.; Sano, H.; Satou, T.; Oikawa, S.; Kamiya, T.

    2009-01-01

    Using PIGE (Proton Induced Gamma Emission) technique at TARRI (Takasaki Advanced Radiation Research Institute), Japan, we measured fluorine (F) uptake into the tooth enamel around two fluoride-containing materials during caries progression using pH cycling. Class V cavities in extracted human teeth were drilled and filled with fluoride-containing materials (i.e. 'Fuji IX' (FN) and 'UniFil flow with MEGA bond' (UF)) and a non-fluoride-containing material (i.e. 'SOLARE with MEGA bond' (SO)). Three 120 μm longitudinal sections including the filling material were obtained from each tooth. In order to simulate daily acid attack occurring in the oral cavity, the pH cycling (pH 6.8-4.5) was carried out for 1, 3 and 5 weeks, separately. After pH cycling, the caries progression in all specimens was observed using transverse microradiography (TMR). The F and calcium distributions of the specimens were evaluated using PIGE and PIXE techniques. The F distribution of the specimens clearly showed the F uptake from FN into enamel adjacent to the filling material, while the F uptakes from UF and SO were not detected. For UF, the MEGA bond (non-fluoride-containing) between the tooth and UniFil flow interfered with the F absorption into the tooth. For FN, the amount of F uptake into the subsurface enamel increased during pH cycling. The amount of F uptake in 5-week pH cycling had significantly higher value compared to those in 1- and 3-week pH cycling. For UF and SO, there were no significant differences between the different durations of pH cycling. Among fluoride-containing materials, there were some differences in the F uptake with increased pH cycling, which could possibly lead to obtaining difference in clinical performance. The data obtained using PIGE and PIXE techniques were useful in understanding the benefit of fluorine by means of fluoride-containing material for preventing caries.

  13. Fluorine uptake into human enamel around fluoride-containing dental materials during cariogenic pH cycling

    Energy Technology Data Exchange (ETDEWEB)

    Komatsu, H. [Graduate School of Dental Medicine, Hokkaido University, Kita-13, Nishi-7, Kita-ku, Sapporo 060-8586 (Japan)], E-mail: kom@den.hokudai.ac.jp; Yamamoto, H. [Graduate School of Dentistry, Osaka University, 1-8 Yamada-Oka, Suita 565-0871 (Japan); Nomachi, M. [Graduate School of Science, Osaka University, 1-1 Machikaneyama, Toyonaka 560-0043 (Japan); Yasuda, K. [The Wakasa wan Energy Research Center, 64-52-1 Hase, Tsuruga 914-0192 (Japan); Matsuda, Y.; Kinugawa, M.; Kijimura, T.; Sano, H. [Graduate School of Dental Medicine, Hokkaido University, Kita-13, Nishi-7, Kita-ku, Sapporo 060-8586 (Japan); Satou, T.; Oikawa, S.; Kamiya, T. [Advanced Radiation Technology, TARRI, JAEA, 1233 Watanuki-machi, Takasaki 370-1292 (Japan)

    2009-06-15

    Using PIGE (Proton Induced Gamma Emission) technique at TARRI (Takasaki Advanced Radiation Research Institute), Japan, we measured fluorine (F) uptake into the tooth enamel around two fluoride-containing materials during caries progression using pH cycling. Class V cavities in extracted human teeth were drilled and filled with fluoride-containing materials (i.e. 'Fuji IX' (FN) and 'UniFil flow with MEGA bond' (UF)) and a non-fluoride-containing material (i.e. 'SOLARE with MEGA bond' (SO)). Three 120 {mu}m longitudinal sections including the filling material were obtained from each tooth. In order to simulate daily acid attack occurring in the oral cavity, the pH cycling (pH 6.8-4.5) was carried out for 1, 3 and 5 weeks, separately. After pH cycling, the caries progression in all specimens was observed using transverse microradiography (TMR). The F and calcium distributions of the specimens were evaluated using PIGE and PIXE techniques. The F distribution of the specimens clearly showed the F uptake from FN into enamel adjacent to the filling material, while the F uptakes from UF and SO were not detected. For UF, the MEGA bond (non-fluoride-containing) between the tooth and UniFil flow interfered with the F absorption into the tooth. For FN, the amount of F uptake into the subsurface enamel increased during pH cycling. The amount of F uptake in 5-week pH cycling had significantly higher value compared to those in 1- and 3-week pH cycling. For UF and SO, there were no significant differences between the different durations of pH cycling. Among fluoride-containing materials, there were some differences in the F uptake with increased pH cycling, which could possibly lead to obtaining difference in clinical performance. The data obtained using PIGE and PIXE techniques were useful in understanding the benefit of fluorine by means of fluoride-containing material for preventing caries.

  14. A laser-abrasive method for the cutting of enamel and dentin.

    Science.gov (United States)

    Altshuler, G B; Belikov, A V; Sinelnik, Y A

    2001-01-01

    This paper introduced a new method for the removal of hard dental tissue based upon the use of particles accelerated by laser irradiation, which the authors have called the laser-abrasive method. The particles used were sapphire as powder or an aqueous suspension. The effect of the products of enamel ablation was also investigated. The particles were accelerated using submillisecond pulses of Er:YAG and Nd:YAG lasers. A strobing CCD camera was used to measure the speed of the ejected particles. The additional contribution of these particles to the efficiency of laser ablation of enamel and dentin was also investigated. The results showed that the enamel particles produced by the beam-tissue interaction were also accelerated by this process of ablation and were effective in the removal of enamel and dentin. The use of an aqueous suspension of sapphire particles increased the efficiency of enamel removal threefold when compared with the use of an Er:YAG laser with water spray. The laser-abrasive method allowed for the removal of enamel and dentin at speeds approaching those of the high-speed turbine. Copyright 2001 Wiley-Liss, Inc.

  15. Mechanism of Action of TiF4 on Dental Enamel Surface: SEM/EDX, KOH-Soluble F, and X-Ray Diffraction Analysis.

    Science.gov (United States)

    Comar, Lívia P; Souza, Beatriz M; Al-Ahj, Luana P; Martins, Jessica; Grizzo, Larissa T; Piasentim, Isabelle S; Rios, Daniela; Buzalaf, Marília Afonso Rabelo; Magalhães, Ana Carolina

    2017-10-12

    This in vitro study aimed to evaluate the action of TiF4 on sound and carious bovine and human enamel. Sound (S) and pre-demineralised (DE) bovine and human (primary and permanent) enamel samples were treated with TiF4 (pH 1.0) or NaF varnishes (pH 5.0), containing 0.95, 1.95, or 2.45% F for 12 h. The enamel surfaces were analysed using SEM-EDX (scanning electron microscopy/energy-dispersive X-ray spectroscopy) (n = 10, 5 S and 5 DE) and KOH-soluble fluoride was quantified (n = 20, 10 S and 10 DE). Hydroxyapatite powder produced by precipitation method was treated with the corresponding fluoride solutions for 1 min (n = 2). The formed compounds were detected using X-ray diffraction (XRD). All TiF4 varnishes produced a coating layer rich in Ti and F on all types of enamel surface, with micro-cracks in its extension. TiF4 (1.95 and 2.45% F) provided higher fluoride deposition than NaF, especially for bovine enamel (p enamel. The Ti content was higher for bovine and human primary enamel than human permanent enamel, with some differences between S and DE. The XRD analysis showed that TiF4 induced the formation of new compounds such as CaF2, TiO2, and Ti(HPO4)2·H2O. In conclusion, TiF4 (>0.95% F) interacts better, when compared to NaF, with bovine and human primary enamel than with human permanent enamel. TiF4 provoked higher F deposition compared to NaF. Carious enamel showed higher F uptake than sound enamel by TiF4 application, while Ti uptake was dependent on the enamel condition and origin. © 2017 S. Karger AG, Basel.

  16. Evaluation of skin exposure of patients and the irradiation field dimensions in dental radiography

    International Nuclear Information System (INIS)

    Khoury, H.J.; Hazin, C.A.; Andrade Lima, F.R.; Lopes Filho, F.J.

    1991-01-01

    This work aimed to estimate the skin exposure to patients in dental radiography, as well as, evaluate the magnitude of the skin area irradiated during a typical radiographic procedure. The study was based in a preliminary survey of dental X-ray equipments installed in the metropolitan region of Recife. The results showed that in 90% of the equipments surveyed the estimated patient skin exposure was above the recommended value of 500 mR. For X-ray beam diameters, the results showed values ranging from 4.5 to 11.5 cm, which do not agree with those set up by either national or international radiation protection organizations. (author)

  17. Single session of Nd:YAG laser intracanal irradiation neutralizes endotoxin in dental root dentin.

    Science.gov (United States)

    Archilla, José R F; Moreira, Maria S N A; Miyagi, Sueli P H; Bombana, Antônio C; Gutknecht, Norbert; Marques, Márcia M

    2012-11-01

    Endotoxins released in the dental root by Gram-negative microorganisms can be neutralized by calcium hydroxide, when this medication is applied inside the root canal for at least seven days. However, several clinical situations demand faster root canal decontamination. Thus, for faster endotoxin neutralization, endodontists are seeking additional treatments. The in vitro study tested whether or not intracanal Nd:YAG laser irradiation would be able to neutralize endotoxin within the human dental root canal in a single session. Twenty-four human teeth with one root were mounted between two chambers. After conventional endodontic treatment, root canals were contaminated with Escherichia coli endotoxin. Then they were irradiated or not (controls) in contact mode with an Nd:YAG laser (1.5 W, 15 Hz, 100 mJ and pulse fluency of 124  J/cm2). The endotoxin activity was measured using the limulus lysate technique and data were statistically compared (p≤0.05). The concentration of active endotoxin measured in the negative control group was significantly lower than that of the positive control group (p=0.04). The concentrations of endotoxin in both irradiated groups were significantly lower than that of the positive control group (p=0.027) and similar to that of negative control group (p=0.20). A single session of intracanal Nd:YAG laser irradiation is able to neutralize endotoxin in the dental root tissues.

  18. Single session of Nd:YAG laser intracanal irradiation neutralizes endotoxin in dental root dentin

    Science.gov (United States)

    Archilla, José R. F.; Moreira, Maria S. N. A.; Miyagi, Sueli P. H.; Bombana, Antônio C.; Gutknecht, Norbert; Marques, Márcia M.

    2012-11-01

    Endotoxins released in the dental root by Gram-negative microorganisms can be neutralized by calcium hydroxide, when this medication is applied inside the root canal for at least seven days. However, several clinical situations demand faster root canal decontamination. Thus, for faster endotoxin neutralization, endodontists are seeking additional treatments. The in vitro study tested whether or not intracanal Nd:YAG laser irradiation would be able to neutralize endotoxin within the human dental root canal in a single session. Twenty-four human teeth with one root were mounted between two chambers. After conventional endodontic treatment, root canals were contaminated with Escherichia coli endotoxin. Then they were irradiated or not (controls) in contact mode with an Nd:YAG laser (1.5 W, 15 Hz, 100 mJ and pulse fluency of 124 J/cm2). The endotoxin activity was measured using the limulus lysate technique and data were statistically compared (p≤0.05). The concentration of active endotoxin measured in the negative control group was significantly lower than that of the positive control group (p=0.04). The concentrations of endotoxin in both irradiated groups were significantly lower than that of the positive control group (p=0.027) and similar to that of negative control group (p=0.20). A single session of intracanal Nd:YAG laser irradiation is able to neutralize endotoxin in the dental root tissues.

  19. An experimental study on the effect of irradiation on deciduous dental pulp and periodontal membrane

    International Nuclear Information System (INIS)

    Nagayama, Takehiko

    1986-01-01

    Left mandibular third deciduous molars of young dogs were irradiated for 3,000 R with 200 kVp X-ray and the effect on the dental pulp and periodontal membrane was investigated histopathologically. 1. From 3rd to 7th days after irradiation, localized inflammatory cell infiltration was observed in part in the dental pulp tissue. No abnormal findings were observed in the periodontal membrane. 2. On 14th day after irradiation in the coronal dental pulp, cells decreased; karyopycnosis occurred; cells were connected only by cellular processes, and large and small reticular networks were formed. In the periodontal membrane, fibers ran irregularly although in part and findings of atrophy were seen. Fibroblasts showed a decreasing tendency. 3. In the cases from 1 to 2 months after irradiation, the pulp tissue showed marked atrophy of odontoblasts and the dental pulp showed hyalinization-like changes. In the periodontal membrane, Sharpey's fibers ran irregularly or became indistinct, and fibroblasts decreased extensively. The periodontal membrane in general showed hyalinization. 4. In the cases of 4 months after irradiation, the pulp tissue on the whole showed marked atrophy and disappearance of odontoblast layers. In the periodontal membrane, inflammatory cell infiltration was seen in part and membrane fibers, as those in 2nd month, showed marked atrophy, became enlarged, and presented findings of hyalinization. 5. At 8th month, the necleoli nearly disappeared in the pulp tissue from the crown to the root and the cells were connected like filaments by cellular processes. Nearly all the blood vessels and fibers disappeared. In the periodontal membrane, most of Sharpey's fibers disappeared. Fibroblasts showed marked atrophy and disappearance, and few normal fibloblasts could be found. (J.P.N.)

  20. Assessing the irradiance delivered from light-curing units in private dental offices in Jordan.

    Science.gov (United States)

    Maghaireh, Ghada A; Alzraikat, Hanan; Taha, Nessrin A

    2013-08-01

    The authors conducted a study to examine the irradiance from light-curing units (LCUs) used in dental offices in Jordan. Two of the authors visited 295 private dental offices (15 percent) in Jordan and collected the following information about the LCUs: age, type (quartz-tungsten-halogen or light-emitting diode), date of last maintenance, type of maintenance, last date of use, number of times used during the day, availability of a radiometer, exposure time for each resin-based composite increment, size of light-curing tips and presence of resin-based composite on the tips. The authors used a radiometer to measure the irradiance from the LCUs. They used linear regression with stepwise correlation for the statistical analysis. The authors set the minimum acceptable irradiance at 300 milliwatts/square centimeter. The mean irradiance of the 295 LCUs examined was 361 mW/cm(2), and 136 LCUs (46.1 percent) delivered an irradiance of less than 300 mW/cm(2). The unit's age, type and presence of resin-based composite on the light-curing tips had a significant effect on the irradiance (P ≤ .001). Only 37 of the 141 quartz-tungsten-halogen units (26.2 percent) and 122 of the 154 light-emitting diode units (79.2 percent) delivered at least 300 mW/cm(2). Resin contamination on the light-curing tips had a significant effect on the irradiance delivered. The irradiance from the LCUs decreased with use. Practical Implications. The irradiance from many of the units in this study was less than 300 mW/cm(2), which may affect the quality of resin-based composite restorations. Dentists should monitor the performance of the LCUs in their offices weekly.

  1. Chosen single nucleotide polymorphisms (SNPs) of enamel formation genes and dental caries in a population of Polish children.

    Science.gov (United States)

    Gerreth, Karolina; Zaorska, Katarzyna; Zabel, Maciej; Borysewicz-Lewicka, Maria; Nowicki, Michał

    2017-09-01

    It is increasingly emphasized that the influence of a host's factors in the etiology of dental caries are of most interest, particularly those concerned with genetic aspect. The aim of the study was to analyze the genotype and allele frequencies of single nucleotide polymorphisms (SNPs) in AMELX, AMBN, TUFT1, TFIP11, MMP20 and KLK4 genes and to prove their association with dental caries occurrence in a population of Polish children. The study was performed in 96 children (48 individuals with caries - "cases" and 48 free of this disease - "controls"), aged 20-42 months, chosen out of 262 individuals who had dental examination performed and attended 4 day nurseries located in Poznań (Poland). From both groups oral swab was collected for molecular evaluation. Eleven selected SNPs markers were genotyped by Sanger sequencing. Genotype and allele frequencies were calculated and a standard χ2 analysis was used to test for deviation from Hardy-Weinberg equilibrium. The association of genetic variations with caries susceptibility or resistance was assessed by the Fisher's exact test and p ≤ 0.05 was considered statistically significant. Five markers were significantly associated with caries incidence in children in the study: rs17878486 in AMELX (p caries occurrence in Polish children.

  2. Microradiographical aspects of maxillo-dental lesions in the irradiated cat

    International Nuclear Information System (INIS)

    Dambrain, R.; Dhem, A.; Winant, M.; Wambersie, A.

    1986-01-01

    This paper describes the reactions of bone tissue and teeth, in cats, after continuous low rate irradiation, in conditions similar to those encountered in interstitial therapy. Irradiations were performed using 3 hairpin shape iridium-192 wires. The doses were assessed following the Paris System. As far as the teeth are concerned, the development proceeds normally after 60 Gy irradiation delivered over 6 days. At 80 Gy, irradiation has an indirect effect on the teeth by altering the salivary environment; the dental crowns are coated with a thick layer of tarter and show cavities reaching the pulp. As far as the bony tissue is concerned, its normal development is not altered after 60 Gy. At 80 Gy, a destructive process appears, similar to those oberved in patients with mandibular osteoradionecrosis. The foci of destruction are very irregular in shape; the cavities do not contain osteoclasts but small mononucleated cells

  3. Molecular analysis of tooth enamel by Raman spectroscopy after treatment with bleaching agents at different concentrations; Analisis molecular del esmalte dental por medio de espectroscopia Raman despues del tratamiento con agentes blanqueadores a diferentes concentraciones

    Energy Technology Data Exchange (ETDEWEB)

    Duran Sedo, Randall; Obando Rosabal, Sofia; Saenz Bonilla, Paola; Soto Aguilar, Calendy; Vasquez Rodriguez, Amaya

    2014-07-01

    The changes in the concentration of the v1 phosphate molecule of the surface of dentin enamel are treated and researched with bleaching agents of chemical activation to basis of hydrogen peroxide than 9,5% and 14% and carbamide peroxide than 38%, for a period of 28 days. Raman spectroscopy was used and 30 dental pieces extracted, of which, were to be free of blemishes and pigmentations, without possessing fractures of the enamel, decay nor any other type of defect. The Raman spectrum was obtained of each dental piece prior to the application of bleaching agents. The specimens were separated into three experimental groups according to the concentration of whitening. The concentration of the v1 phosphate molecule was measured in the tooth enamel to the second and fourth week of treatment. In addition, ANOVA was performed for respective measurements (p≤0.05). A reduction of the v1 phosphate molecule were observed during and after the bleaching process in the experimental groups that have used of hydrogen peroxide to 14% and carbamide peroxide 38%. In the group of hydrogen peroxide to 9,5% has remained unproven a significant reduction. Within the limitations of this study is concluded that the bleaching agent causes a loss of v1 phosphate. This loss has been greater in the whitening of higher concentration. In spite, that the possible effect remineralizing of the saliva on a teeth whitening process has been unevaluated, it is recommended using during and after the treatment, toothpastes, mouthwashes, chewing gums, dental floss, among others, that contain ACP to help to cushion the potential loss of phosphate from tooth enamel. (author) [Spanish] Los cambios en la concentracion de la molecula de fosfato v1 de la superficie del esmalte dental son tratados e investigados con agentes blanqueadores de activacion quimica a base de peroxido de hidrogeno al 9,5% y 14% y peroxido de carbamida al 38%, por un periodo de 28 dias. Espectroscopia Raman fue utilizada y 30 piezas

  4. Effect of light intensity and irradiation time on the polymerization process of a dental composite resin

    Directory of Open Access Journals (Sweden)

    Discacciati José Augusto César

    2004-01-01

    Full Text Available Polymerization shrinkage is a critical factor affecting the longevity and acceptability of dental composite resins. The aim of this work was to evaluate the effect of light intensity and irradiation time on the polymerization process of a photo cured dental composite resin by measuring the Vickers hardness number (VHN and the volumetric polymerization shrinkage. Samples were prepared using a dental manual light-curing unit. The samples were submitted to irradiation times of 5, 10, 20 and 40 s, using 200 and 400 mW.cm-2 light intensities. Vickers hardness number was obtained at four different moments after photoactivation (immediate, 1 h, 24 h and 168 h. After this, volumetric polymerization shrinkage values were obtained through a specific density method. The values were analyzed by ANOVA and Duncan's (p = 0.05. Results showed increase in hardness values from the immediate reading to 1 h and 24 h readings. After 24 h no changes were observed regardless the light intensities or activation times. The hardness values were always smaller for the 200 mW.cm-2 light intensity, except for the 40 s irradiation time. No significant differences were detected in volumetric polymerization shrinkage considering the light intensity (p = 0.539 and the activation time (p = 0.637 factors. In conclusion the polymerization of the material does not terminate immediately after photoactivation and the increase of irradiation time can compensate a lower light intensity. Different combinations between light intensity and irradiation time, i.e., different amounts of energy given to the system, have not affected the polymerization shrinkage.

  5. Near-ultraviolet removal rates for subgingival dental calculus at different irradiation angles

    Science.gov (United States)

    Schoenly, Joshua E.; Seka, Wolf D.; Rechmann, Peter

    2011-07-01

    The laser ablation rate of subgingival dental calculus irradiated at a 400-nm-wavelength, 7.4-mJ pulse energy, and 85- and 20-deg irradiation angles is measured using laser triangulation. Three-dimensional images taken before and after irradiation create a removal map with 6-μm axial resolution. Fifteen human teeth with subgingival calculus are irradiated in vitro under a cooling water spray with an ~300-μm-diam, tenth-order super-Gaussian beam. The average subgingival calculus removal rates for irradiation at 85 and 20 deg are 11.1+/-3.6 and 11.5+/-5.9 μm/pulse, respectively, for depth removal and 4.5+/-1.7×105 and 4.8+/-2.3×105 μm3/pulse, respectively, for volume removal. The ablation rate is constant at each irradiation site but varies between sites because of the large differences in the physical and optical properties of calculus. Comparison of the average depth- and volume-removal rates does not reveal any dependence on the irradiation angle and is likely due to the surface topology of subgingival calculus samples that overshadows any expected angular dependence.

  6. Development of rampant dental caries, and composition of plaque fluid and saliva in irradiated primates

    Energy Technology Data Exchange (ETDEWEB)

    Edgar, W M; Bowen, W H; Cole, M F [National Caries Program, National Institute of Dental Research, Maryland USA

    1981-01-01

    Co-60 gamma irradiation of the salivary glands of Macaca mulata monkeys fed a cariogenic diet led to the rapid onset of dental caries resembling that in irradiated human patients. Plaque fluid and saliva were sampled from irradiated monkeys, nonirradiated controls and a group of animals fed a noncariogenic diet in order to look for changes which might occur in inorganic composition related to the caries development and to dietary differences. Salivary calcium and phosphate levels were not markedly changed after irradiation: iodide levels were raised, while thiocyanate levels fell. In plaque fluid, calcium concentrations were not affected by irradiation, but were higher in animals fed a noncariogenic diet. Phosphate levels were higher with a cariogenic diet and further increased in irradiated animals. Magnesium levels were occasionally higher than those of calcium. Other differences in plaque fluid composition may be related to secondary effects of the concomitant gingival disease. The results do not point clearly a specific change in the quality of the saliva produced by the residual gland tissue after irradiation which precipitates the rampant caries. It is more likely that the grat reduction in the quantity of saliva with its protective constituents is responsible.

  7. Development of rampant dental caries, and composition of plaque fluid and saliva in irradiated primates

    International Nuclear Information System (INIS)

    Edgar, W.M.; Bowen, W.H.; Cole, M.F.

    1981-01-01

    Co-60 gamma irradiation of the salivary glands of Macaca mulata monkeys fed a cariogenic diet led to the rapid onset of dental caries resembling that in irradiated human patients. Plaque fluid and saliva were sampled from irradiated monkeys, nonirradiated controls and a group of animals fed a noncariogenic diet in order to look for changes which might occur in inorganic composition related to the caries development and to dietary differences. Salivary calcium and phosphate levels were not markedly changed after irradiation: iodide levels were raised, while thiocyanate levels fell. In plaque fluid, calcium concentrations were not affected by irradiation, but were higher in animals fed a noncariogenic diet. Phosphate levels were higher with a cariogenic diet and further increased in irradiated animals. Magnesium levels were occasionally higher than those of calcium. Other differences in plaque fluid composition may be related to secondary effects of the concomitant gingival disease. The results do not point clearly a specific change in the quality of the saliva produced by the residual gland tissue after irradiation which precipitates the rampant caries. It is more likely that the grat reduction in the quantity of saliva with its protective constituents is responsible. (author)

  8. Er,Cr:YSGG Laser Energy Delivery: Pulse and Power Effects on Enamel Surface and Erosive Resistance.

    Science.gov (United States)

    de Oliveira, Renan Mota; de Souza, Vinicius Matsuzaki; Esteves, Camila Machado; de Oliveira Lima-Arsati, Ynara Bosco; Cassoni, Alessandra; Rodrigues, José Augusto; Brugnera Junior, Aldo

    2017-11-01

    High power lasers have been suggested as a useful tool for dental caries and erosion prevention due to the increase of enamel acid resistance. to evaluate the effect of Er,Cr:YSGG (erbium,chromium:yttrium, scandium, gallium, garnet) laser irradiation pulse frequency and power on enamel surface and acid erosion resistance. By combining pulse frequency (5-75 Hz) and power settings (0.10-1.00 W), 20 irradiated groups and one nonirradiated control group were tested. A total of 63 bovine enamel blocks (n = 3/group) were prepared for surface hardness and roughness evaluation, performed in three phases: baseline, after irradiation, and after erosive challenge. Enamel blocks were irradiated with Er,Cr:YSGG laser with MZ8 tip (iPlus; Waterlase, Biolase, CA) for 30 sec according to experimental group and submitted. Erosive challenge consisted of four cycles alternating immersion in 0.01 M HCl (5 mL/mm 2 ; 2 min; at 37°C) and immersion in artificial saliva for 3 h. Analysis of variance (three-way ANOVA), Tukey's test, and Pearson correlation were performed for the statistical analysis (p hardness. After erosive challenge, 5 and 75 W groups showed increase in surface hardness; 0.25, 0.5, 0.75, and 1 W groups showed minor alterations in surface roughness. the irradiation of Er,Cr:YSGG laser with different parameters of power and pulse frequency settings may alter enamel surface and erosive resistance differently. Pulse frequency of 30 Hz and power of 0.50 W was considered the best parameter to prevent enamel acid erosion.

  9. Bond strength of dental adhesive systems irradiated with ionizing radiation.

    Science.gov (United States)

    Dibo da Cruz, Adriana; Goncalves, Luciano de Souza; Rastelli, Alessandra Nara de Souza; Correr-Sobrinho, Lorenco; Bagnato, Vanderlei Salvador; Boscolo, Frab Norberto

    2010-04-01

    The aim of the present paper was to determine the effect of different types of ionizing radiation on the bond strength of three different dentin adhesive systems. One hundred twenty specimens of 60 human teeth (protocol number: 032/2007) sectioned mesiodistally were divided into 3 groups according to the adhesives systems used: SB (Adper Single Bond Plus), CB (Clearfil SE Bond) and AP (Adper Prompt Self-Etch). The adhesives were applied on dentin and photo-activated using LED (Lec 1000, MMoptics, 1000 mW/cm2). Customized elastomer molds (0.5 mm thickness) with three orifices of 1.2 mm diameter were placed onto the bonding areas and filled with composite resin (Filtek Z-250), which was photo-activated for 20 s. Each group was subdivided into 4 subgroups for application of the different types of ionizing radiation: ultraviolet radiation (UV), diagnostic x-ray radiation (DX), therapeutic x-ray radiation (TX) and without irradiation (control group, CG). Microshear tests were carried out (Instron, model 4411), and afterwards the modes of failure were evaluated by optical and scanning electron microscope and classified using 5 scores: adhesive failure, mixed failures with 3 significance levels, and cohesive failure. The results of the shear bond strength test were submitted to ANOVA with Tukey's test and Dunnett's test, and the data from the failure pattern evaluation were analyzed with the Mann Whitney test (p = 0.05). No change in bond strength of CB and AP was observed after application of the different radiation types, only SB showed increase in bond strength after UV (p = 0.0267) irradiation. The UV also changed the failure patterns of SB (p = 0.0001). The radio-induced changes did not cause degradation of the restorations, which means that they can be exposed to these types of ionizing radiation without weakening the bond strength.

  10. Interaction of ArF laser with dental hard tissue (AEM Study

    Directory of Open Access Journals (Sweden)

    Abbas Majdabadi

    2016-07-01

    Full Text Available Background and Aims: Nowadays lasers are used as alternatives to the tooth preparation because of reducing pain and bloodshed. The aim of this study was to observe the effect of ArF laser on the dental hard tissues. Materials and Methods: For this research human molar teeth with no caries or dental restoration and enamel cracks were used. Irradiation laser energies were taken 95, 70 and 50 mJ for enamel and 80, 70 and 50 mJ for dentine. Then, for each of energy values pulse numbers (repetition rate were adjusted at 200, 400, 600, 800, 1000 and 1500. Ablation was carried out without water spray on both enamel and dentine. Finally, the dimensions of ablated areas were measured by using a camera connected to the computer and results were applied in graphs. Results: For each energy value, the ablation dimension increased by increasing pulse numbers. Ablation depth in dentine was more than that of for enamel. Trends of graphs for dentine and enamel were the same. SEM images of ablations by 95 mJ energy on enamel and 80 mJ energy on dentine showed sharp edges. Conclusion: Ablation depths increased by increasing pulse numbers, for each energy level. However, this increase was not that as expected, because the lack of water spray while irradiating.

  11. Antibiotic protocol for the prevention of osteoradionecrosis following dental extractions in irradiated head and neck cancer patients: A 10 years prospective study

    Directory of Open Access Journals (Sweden)

    Saleh A Al-Bazie

    2016-01-01

    Conclusion: Based on the results of this study, perioperative oral antibiotics in combination with antibacterial mouthwashes are effective in preventing ORN following dental extractions in irradiated patients.

  12. An in vitro study to evaluate the effect of two ethanol-based and two acetone-based dental bonding agents on the bond strength of composite to enamel treated with 10% carbamide peroxide

    Directory of Open Access Journals (Sweden)

    Deepa Basavaraj Benni

    2014-01-01

    Full Text Available Background and Objective: Carbamide peroxide bleaching has been implicated in adversely affecting the bond strength of composite to enamel. The objective of this in vitro study was to evaluate the effect of ethanol-based (Clearfil S 3 bond, Kuraray, Adper Single bond 2, 3M ESPE dental products and acetone-based (Prime and Bond NT, Dentsply, One Step, Bisco bonding agents on the shear bond strength of composite to enamel treated with 10% carbamide peroxide bleaching agent. Materials and Methods: A total of 120 extracted human noncarious permanent incisors were randomly divided into two groups (control and experimental. Experimental group specimens were subjected to a bleaching regimen with a 10% carbamide peroxide bleaching system (Opalescence; Ultradent Products Inc, South Jordan, USA. Composite resin cylinders were bonded to the specimens using four bonding agents and shear bond strength was determined with universal testing machine. Results: There was no statistically significant difference in the shear bond strength between control and experimental groups with both ethanol-based (Clearfil S 3 Bond and Adper Single Bond 2 and acetone-based bonding agent (Prime and Bond NT and One Step. Interpretation and Conclusion: The adverse effect of bleaching on bonding composite to enamel can be reduced or eliminated by using either ethanol- or acetone-based bonding agent. Clinical Significances: Immediate bonding following bleaching procedure can be done using ethanol- or acetone-based bonding agent without compromising bond strength.

  13. Dental microwear variability on buccal tooth enamel surfaces of extant Catarrhini and the Miocene fossil Dryopithecus laietanus (Hominoidea).

    Science.gov (United States)

    Galbany, J; Moyà-Solà, S; Pérez-Pérez, A

    2005-01-01

    Analyses of buccal tooth microwear have been used to trace dietary habits of modern hunter-gatherer populations. In these populations, the average density and length of striations on the buccal surfaces of teeth are significantly cor-related with the abrasive potential of food items consumed. In non-human pri-mates, tooth microwear patterns on both occlusal and buccal wear facets have been thoroughly studied and the results applied to the characterization of dietary habits of fossil species. In this paper, we present inter- and intra-specific buccal microwear variability analyses in extant Cercopithecoidea (Cercopithecus mitis, C. neglectus, Chlorocebus aethiops, Colobus spp., Papio anubis) and Hominoidea (Gorilla gorilla, Pan troglodytes, Pongo pygmaeus). The results are tentatively compared to buccal microwear patterns of the Miocene fossils Dryopithecus and Oreopithecus. Significant differences in striation density and length are found among the fossil taxa studied and the extant primates, suggesting that buccal microwear can be used to identify dietary differences among taxa. The Dryopithecus buccal microwear pattern most closely resembles that of abrasive, tough plant foods consumers, such as the gorilla, in contrast to stud-ies of dental morphology that suggest a softer, frugivorous diet. Results for Oreopithecus were equivocal, but suggest a more abrasive diet than that previously thought. (c) 2005 S. Karger AG, Basel.

  14. Analysis of Dental Enamel Surface Submitted to Fruit Juice Plus Soymilk by Micro X-Ray Fluorescence: In Vitro Study

    Directory of Open Access Journals (Sweden)

    Janaína Salmos Brito

    2016-01-01

    Full Text Available Objective. This paper aimed to analyze the in vitro industrialized fruit juices effect plus soy to establish the erosive potential of these solutions. Materials and Methods. Seventy bovine incisors were selected after being evaluated under stereomicroscope. Their crowns were prepared and randomly divided into 7 groups, using microhardness with allocation criteria. The crowns were submitted to the fruit juice plus soy during 15 days, twice a day. The pH values, acid titration, and Knoop microhardness were recorded and the specimens were evaluated using X-ray microfluorescence (µXRF. Results. The pH average for all juices and after 3 days was significantly below the critical value for dental erosion. In average, the pH value decreases 14% comparing initial time and pH after 3 days. Comparing before and after, there was a 49% microhardness decrease measured in groups (p<0.05. Groups G1, G2, G5, and G6 are above this average. The analysis by μXRF showed a decrease of approximately 7% Ca and 4% P on bovine crowns surface. Florida (FL statistical analysis showed a statistically significant 1 difference between groups. Thus, a tooth chance to suffer demineralization due to industrialized fruit juices plus soy is real.

  15. Influence of the incidence angle on the morphology of enamel and dentin under Er:YAG laser irradiation; Estudo da influencia da angulacao do feixe laser na morfologia de esmalte e dentina irradiados com laser de Er:YAG

    Energy Technology Data Exchange (ETDEWEB)

    Junqueira Junior, Duilio Naves

    2002-07-01

    The purpose of this study is to make an in vitro evaluation, using scanning electron microscopy, of the influence of the laser beam irradiation angle on the enamel and dentin morphology. These tissues were both irradiated by Er:YAG Laser, with the same energy parameter. Twenty-four incisive bovine teeth were used, separated in eight groups, four of enamel, and four of dentin, with three specimens in each group. Each specimen was submitted to three laser applications, varying the incidence angle, between the laser and the tooth surface, at 90, 50 and 20 degrees. The applied frequency was 2 Hz, with 20 pulses in each application. The KaVo Key Laser 3 was employed, wavelength at 2940 nm, adjustable energy from 40 to 600 mJ and repetition rate from 1 to 25 Hz. The groups were distributed according to the energy parameter as follows - enamel: 250 mJ; 300 mJ; 350 mJ and 400 mJ; dentin: 200 mJ; 250 mJ; 300 mJ and 350 mJ. The results evidenced the Laser incidence angle importance; it is an essential parameter in the protocol of utilization and it should not be disregarded. The observations of this study allow to conclude that the Laser incidence angle has direct influence on the morphological aspect of the alterations produced in enamel and dentin. (author)

  16. Temperature evaluation of dental implant surface irradiated with high-power diode laser.

    Science.gov (United States)

    Rios, F G; Viana, E R; Ribeiro, G M; González, J C; Abelenda, A; Peruzzo, D C

    2016-09-01

    The prevalence of peri-implantitis and the absence of a standard approach for decontamination of the dental implant surface have led to searches for effective therapies. Since the source of diode lasers is portable, has reduced cost, and does not cause damage to the titanium surface of the implant, high-power diode lasers have been used for this purpose. The effect of laser irradiation on the implants is the elevation of the temperature surface. If this elevation exceeds 47 °C, the bone tissue is irreversibly damaged, so for a safety therapy, the laser parameters should be controlled. In this study, a diode laser of GaAsAl was used to irradiate titanium dental implants, for powers 1.32 to 2.64 W (real) or 2.00 to 4.00 W (nominal), in continuous/pulsed mode DC/AC, with exposure time of 5/10 s, with/without air flow for cooling. The elevation of the temperature was monitored in real time in two positions: cervical and apical. The best results for decontamination using a 968-nm diode laser were obtained for a power of 1.65 and 1.98 W (real) for 10 s, in DC or AC mode, with an air flow of 2.5 l/min. In our perspective in this article, we determine a suggested approach for decontamination of the dental implant surface using a 968-nm diode laser.

  17. Biomodulatory effects of laser irradiation on dental pulp cells in vitro

    Science.gov (United States)

    Milward, Michael R.; Hadis, Mohammed A.; Cooper, Paul R.; Gorecki, Patricia; Carroll, James D.; Palin, William M.

    2015-03-01

    Low level laser/light therapy (LLLT) or photobiomodulation is a biophysical approach that can be used to reduce pain, inflammation and modulate tissue healing and repair. However, its application has yet to be fully realized for dental disease treatment. The aim of this study was to assess the modulation of dental pulp cell (DPC) responses using two LLLT lasers with wavelengths of 660nm and 810nm. Human DPCs were isolated and cultured in phenol-red-free α- MEM/10%-FCS at 37°C in 5% CO2. Central wells of transparent-based black walled 96-microplates were seeded with DPCs (passages 2-4; 150μL; 25,000 cell/ml). At 24h post-seeding, cultures were irradiated using a Thor Photomedicine LLLT device (THOR Photomedicine, UK) at 660nm (3, 6 or 13s to give 2, 5 and 10J/cm2) or 810nm (for 1, 2 or 5s to deliver 5, 10 and 20J/cm2). Metabolic activity was assessed via a modified MTT assay 24h post-irradiation. Statistical differences were identified using analysis of variance and post-hoc Tukey tests (P=0.05) and compared with nonirradiated controls. Significantly higher MTT activity was obtained for both lasers (P0.05). Consequently, enhanced irradiation parameters was apparent for both lasers. These parameters should be further optimised to identify the most effective for therapeutic application.

  18. The irradiation action on human dental tissue by X-rays and electrons. A nanoindenter study

    Energy Technology Data Exchange (ETDEWEB)

    Fraenzel, Wolfgang [Halle-Wittenberg Univ., Halle (Germany). Dept. of Physics; Gerlach, Reinhard [Halle-Wittenberg Univ., Halle (Germany). Clinic of Radiation Therapy

    2009-07-01

    It is known that ionizing radiation is used in medicine for Roentgen diagnostics and for radiation therapy. The radiation interacts with matter, in particular with biological one, essentially by scattering, photoelectric effect, Compton effect and pair production. To what extent the biological material is changed thereby, depends on the type and the amount of radiation energy, on the dose and on the tissue constitution. In modern radiation therapy two different kinds of radiation are used: high energy X-rays and electron radiation. In the case of head-neck tumors the general practice is an irradiation with high energy X-rays with absorbed dose to water up to 70 Gy. Teeth destruction has been identified as a side effect during irradiation. In addition, damage to the salivary glands is often observed which leads to a decrease or even the complete loss of the salivary secretion (xerostomia). This study shows how the different energy and radiation types damage the tooth tissue. The effects of both, high X-ray energy and high energy electrons, on the mechanical properties hardness and elasticity of the human dental tissue are measured by the nanoindentation technique. We compare these results with the effect of the irradiation of low X-ray energy on the dental tissue. (orig.)

  19. The irradiation action on human dental tissue by X-rays and electrons. A nanoindenter study

    International Nuclear Information System (INIS)

    Fraenzel, Wolfgang; Gerlach, Reinhard

    2009-01-01

    It is known that ionizing radiation is used in medicine for Roentgen diagnostics and for radiation therapy. The radiation interacts with matter, in particular with biological one, essentially by scattering, photoelectric effect, Compton effect and pair production. To what extent the biological material is changed thereby, depends on the type and the amount of radiation energy, on the dose and on the tissue constitution. In modern radiation therapy two different kinds of radiation are used: high energy X-rays and electron radiation. In the case of head-neck tumors the general practice is an irradiation with high energy X-rays with absorbed dose to water up to 70 Gy. Teeth destruction has been identified as a side effect during irradiation. In addition, damage to the salivary glands is often observed which leads to a decrease or even the complete loss of the salivary secretion (xerostomia). This study shows how the different energy and radiation types damage the tooth tissue. The effects of both, high X-ray energy and high energy electrons, on the mechanical properties hardness and elasticity of the human dental tissue are measured by the nanoindentation technique. We compare these results with the effect of the irradiation of low X-ray energy on the dental tissue. (orig.)

  20. Enamel micromorphology of the tribosphenic molar

    OpenAIRE

    Hanousková, Pavla

    2014-01-01

    The tribosphenic molar is an ancestral type of mammalian teeth and a phy- lotypic stage of the mammalian dental evolution. Yet, in contrast to derived teeth types, its enamel microarchitecture attracted only little attention and the information on that subject is often restricted to statements suggesting a simple homogenous arrangement of a primitive radial prismatic enamel. The present paper tests this prediction with aid of comparative study of eight model species representing the orders Ch...

  1. β-pyrophosphate : a potential biomaterial for dental applications

    OpenAIRE

    Anastasiou, A. D.; Strafford, S.; Posada-Estefan, O.; Thomson, C. L.; Hussaein, S. A.; Edwards, T. J.; Malinowski, M.; Hondow, N.; Metzger, N. K.; Brown, C. T. A.; Routledge, M. N.; Brown, A. P.; Duggal, M. S.; Jha, A.

    2017-01-01

    The authors acknowledge support from the sponsors of this work; the EPSRC LUMIN (EP/K020234/1) and EU-Marie-Curie-IAPP LUSTRE (324538) projects. Tooth hypersensitivity is a growing problem affecting both the young and ageing population worldwide. Since an effective and permanent solution is not yet available, we propose a new methodology for the restoration of dental enamel using femtosecond lasers and novel calcium phosphate biomaterials. During this procedure the irradiated mineral trans...

  2. Dental Calculus Arrest of Dental Caries.

    Science.gov (United States)

    Keyes, Paul H; Rams, Thomas E

    An inverse relationship between dental calculus mineralization and dental caries demineralization on teeth has been noted in some studies. Dental calculus may even form superficial layers over existing dental caries and arrest their progression, but this phenomenon has been only rarely documented and infrequently considered in the field of Cariology. To further assess the occurrence of dental calculus arrest of dental caries, this study evaluated a large number of extracted human teeth for the presence and location of dental caries, dental calculus, and dental plaque biofilms. A total of 1,200 teeth were preserved in 10% buffered formal saline, and viewed while moist by a single experienced examiner using a research stereomicroscope at 15-25× magnification. Representative teeth were sectioned and photographed, and their dental plaque biofilms subjected to gram-stain examination with light microscopy at 100× magnification. Dental calculus was observed on 1,140 (95%) of the extracted human teeth, and no dental carious lesions were found underlying dental calculus-covered surfaces on 1,139 of these teeth. However, dental calculus arrest of dental caries was found on one (0.54%) of 187 evaluated teeth that presented with unrestored proximal enamel caries. On the distal surface of a maxillary premolar tooth, dental calculus mineralization filled the outer surface cavitation of an incipient dental caries lesion. The dental calculus-covered carious lesion extended only slightly into enamel, and exhibited a brown pigmentation characteristic of inactive or arrested dental caries. In contrast, the tooth's mesial surface, without a superficial layer of dental calculus, had a large carious lesion going through enamel and deep into dentin. These observations further document the potential protective effects of dental calculus mineralization against dental caries.

  3. Dental Calculus Arrest of Dental Caries

    Science.gov (United States)

    Keyes, Paul H.; Rams, Thomas E.

    2016-01-01

    Background An inverse relationship between dental calculus mineralization and dental caries demineralization on teeth has been noted in some studies. Dental calculus may even form superficial layers over existing dental caries and arrest their progression, but this phenomenon has been only rarely documented and infrequently considered in the field of Cariology. To further assess the occurrence of dental calculus arrest of dental caries, this study evaluated a large number of extracted human teeth for the presence and location of dental caries, dental calculus, and dental plaque biofilms. Materials and methods A total of 1,200 teeth were preserved in 10% buffered formal saline, and viewed while moist by a single experienced examiner using a research stereomicroscope at 15-25× magnification. Representative teeth were sectioned and photographed, and their dental plaque biofilms subjected to gram-stain examination with light microscopy at 100× magnification. Results Dental calculus was observed on 1,140 (95%) of the extracted human teeth, and no dental carious lesions were found underlying dental calculus-covered surfaces on 1,139 of these teeth. However, dental calculus arrest of dental caries was found on one (0.54%) of 187 evaluated teeth that presented with unrestored proximal enamel caries. On the distal surface of a maxillary premolar tooth, dental calculus mineralization filled the outer surface cavitation of an incipient dental caries lesion. The dental calculus-covered carious lesion extended only slightly into enamel, and exhibited a brown pigmentation characteristic of inactive or arrested dental caries. In contrast, the tooth's mesial surface, without a superficial layer of dental calculus, had a large carious lesion going through enamel and deep into dentin. Conclusions These observations further document the potential protective effects of dental calculus mineralization against dental caries. PMID:27446993

  4. On the use of dental ceramics as a possible second-line approach to accident irradiation dosimetry

    International Nuclear Information System (INIS)

    Davies, J.E.

    1979-01-01

    Recent development in dental ceramic production has resulted in natural or depleted uranium, used for over half a century to mimic the fluorescence of natural teeth, being substituted in such ceramics by non-radioactive fluorescent materials. This creates the possibility of using dental ceramics incorporating the latter as second-line dosimeters in cases of accidental irradiation. This pilot study shows the feasbility of such an approach using both thermally stimulated exoelectron and thermoluminescent techniques. In conclusion, it is considered that it would be of interest to continue this investigation of dental ceramic materials as second-line accident dosimeters

  5. Concentração de chumbo, defeitos de esmalte e cárie em dentes decíduos Lead level, enamel defects and dental caries in deciduous teeth

    Directory of Open Access Journals (Sweden)

    Viviane Elisângela Gomes

    2004-10-01

    Full Text Available OBJETIVO: Verificar a relação da concentração de chumbo no esmalte de dentes decíduos com a presença de defeitos de esmalte e sua relação com cárie dental em pré-escolares. MÉTODOS: A amostra foi de 329 crianças de pré-escolas municipais de uma área próxima de indústrias (N=132 e outra não industrial (N=197 da cidade de Piracicaba, Estado de São Paulo. Essa amostra pertencente a um estudo inicial realizado entre 2000 e 2001 no qual o chumbo foi analisado por meio de biópsia de esmalte. Foram realizados exames clínicos bucais para verificação da prevalência de defeitos de esmalte (Developmental Defects of Enamel Index - DDE, da Federação Dentária Internacional - FDI e cárie (Índice ceos, Organização Mundial da Saúde, em ambas regiões. Foram utilizados teste de qui-quadrado e cálculo do risco relativo ao nível de significância de 5%, considerando cada região separadamente. RESULTADOS: Houve maior proporção de crianças com cárie entre aquelas com maiores concentrações de chumbo nos decíduos na região não industrial (p=0,02, o que não se observou na região industrial (p=0,89. Houve risco relativo (RR aumentado de cárie nas crianças da região não industrial o que não foi verificado nas crianças da região industrial. Não se observou relação entre a presença de chumbo e os defeitos de esmalte. CONCLUSÕES: Não foram encontados dados que evidenciassem a relação entre concentração de chumbo e defeitos no esmalte em nenhuma das regiões pesquisadas. Não foi encontrada relação entre chumbo e cárie na região industrial, ressaltando a necessidade de mais estudos dessas relações.OBJECTIVE: To verify the relationship between lead concentration in the enamel of deciduous teeth and the presence of enamel defects and, consequently, with dental caries among preschool children. METHODS: The sample consisted of 329 preschool children in Piracicaba, State of São Paulo: 132 attending municipal

  6. The effects of low level laser irradiation on proliferation of human dental pulp: a narrative review.

    Science.gov (United States)

    Staffoli, S; Romeo, U; Amorim, R N S; Migliau, G; Palaia, G; Resende, L; Polimeni, A

    2017-01-01

    Mesenchymal stem cells (MSCs) have the capability for self-renewal, proliferation, and differentiation in various types of specialized cells, so they are very important in cellular therapies. MSC from dental pulp are simply obtainable and have high proliferative capability. Among the therapies that can stimulate the proliferation of certain cell types, low-level laser therapy (LLLT) stands out. The target of this study is to perform a literature review to investigate these effects of low-level laser irradiation on proliferation of human dental pulp.The electronic search of scientific papers was conducted in the Lilacs, Scielo, Medline and PubMed databases through scientific articles published in national and international journals in the past 20 years.The results of this review suggest that LLLT may be a useful and important tool for future advances in cell therapy and tissue engineering associated to stem cells. Studies on cell therapy for regenerating dental tissues has already been done, and shows promising results.

  7. Morphology of the cemento-enamel junction in premolar teeth.

    Science.gov (United States)

    Arambawatta, Kapila; Peiris, Roshan; Nanayakkara, Deepthi

    2009-12-01

    The present study attempted to describe the distribution of the mineralized tissues that compose the cemento-enamel junction, with respect to both the different types of permanent premolars of males and females and the various surfaces of individual teeth. The cervical region of ground sections of 67 premolars that had been extracted for orthodontic reasons were analyzed using transmitted light microscopy to identify which of the following tissue interrelationships was present at the cemento-enamel junction: cementum overlapping enamel; enamel overlapping cementum; edge-to-edge relationship between cementum and enamel; or the presence of gaps between the enamel and cementum with exposed dentin. An edge-to-edge interrelation between root cementum and enamel was predominant (55.1%). In approximately one-third of the sample, gaps between cementum and enamel with exposed dentin were observed. Cementum overlapping enamel was less prevalent than previously reported, and enamel overlapping cementum was seen in a very small proportion of the sample. In any one tooth, the distribution of mineralized tissues at the cemento-enamel junction was irregular and unpredictable. The frequency of gaps between enamel and cementum with exposure of dentin was higher than previously reported, which suggests that this region is fragile and strongly predisposed to pathological changes. Hence, this region should be protected and carefully managed during routine clinical procedures such as dental bleaching, orthodontic treatment, and placement of restorative materials.

  8. Surface modification of Ti dental implants by Nd:YVO4 laser irradiation

    International Nuclear Information System (INIS)

    Braga, Francisco J.C.; Marques, Rodrigo F.C.; Filho, Edson de A.; Guastaldi, Antonio C.

    2007-01-01

    Surface modifications have been applied in endosteal bone devices in order to improve the osseointegration through direct contact between neoformed bone and the implant without an intervening soft tissue layer. Surface characteristics of titanium implants have been modified by addictive methods, such as metallic titanium, titanium oxide and hydroxyapatite powder plasma spray, as well as by subtractive methods, such as acid etching, acid etching associated with sandblasting by either AlO 2 or TiO 2 , and recently by laser ablation. Surface modification for dental and medical implants can be obtained by using laser irradiation technique where its parameters like repetition rate, pulse energy, scanning speed and fluency must be taken into accounting to the appropriate surface topography. Surfaces of commercially pure Ti (cpTi) were modified by laser Nd:YVO 4 in nine different parameters configurations, all under normal atmosphere. The samples were characterized by SEM and XRD refined by Rietveld method. The crystalline phases αTi, βTi, Ti 6 O, Ti 3 O and TiO were formed by the melting and fast cooling processes during irradiation. The resulting phases on the irradiated surface were correlated with the laser beam parameters. The aim of the present work was to control titanium oxides formations in order to improve implants osseointegration by using a laser irradiation technique which is of great importance to biomaterial devices due to being a clean and reproducible process

  9. Characterization of the porosity of human dental enamel and shear bond strength in vitro after variable etch times: initial findings using the BET method.

    Science.gov (United States)

    Nguyen, Trang T; Miller, Arthur; Orellana, Maria F

    2011-07-01

    (1) To quantitatively characterize human enamel porosity and surface area in vitro before and after etching for variable etching times; and (2) to evaluate shear bond strength after variable etching times. Specifically, our goal was to identify the presence of any correlation between enamel porosity and shear bond strength. Pore surface area, pore volume, and pore size of enamel from extracted human teeth were analyzed by Brunauer-Emmett-Teller (BET) gas adsorption before and after etching for 15, 30, and 60 seconds with 37% phosphoric acid. Orthodontic brackets were bonded with Transbond to the samples with variable etch times and were subsequently applied to a single-plane lap shear testing system. Pore volume and surface area increased after etching for 15 and 30 seconds. At 60 seconds, this increase was less pronounced. On the contrary, pore size appears to decrease after etching. No correlation was found between variable etching times and shear strength. Samples etched for 15, 30, and 60 seconds all demonstrated clinically viable shear strength values. The BET adsorption method could be a valuable tool in enhancing our understanding of enamel characteristics. Our findings indicate that distinct quantitative changes in enamel pore architecture are evident after etching. Further testing with a larger sample size would have to be carried out for more definitive conclusions to be made.

  10. Enamel Regeneration - Current Progress and Challenges

    Science.gov (United States)

    Baswaraj; H.K, Navin; K.B, Prasanna

    2014-01-01

    Dental Enamel is the outermost covering of teeth. It is hardest mineralized tissue present in the human body. Enamel faces the challenge of maintaining its integrity in a constant demineralization and remineralization within the oral environment and it is vulnerable to wear, damage, and decay. It cannot regenerate itself, because it is formed by a layer of cells that are lost after the tooth eruption. Conventional treatment relies on synthetic materials to restore lost enamel that cannot mimic natural enamel. With advances in material science and understanding of basic principles of organic matrix mediated mineralization paves a way for formation of synthetic enamel. The knowledge of enamel formation and understanding of protein interactions and their gene products function along with the isolation of postnatal stem cells from various sources in the oral cavity, and the development of smart materials for cell and growth factor delivery, makes possibility for biological based enamel regeneration. This article will review the recent endeavor on biomimetic synthesis and cell based strategies for enamel regeneration. PMID:25386548

  11. The CuHBr laser in hard dental tissues

    International Nuclear Information System (INIS)

    Miyakawa, Walter

    2004-01-01

    In this work, it was verified the viability of characterization of laser-irradiated dental tissues in two extreme conditions: high and low absorption by the dental tissue. Comparison with light microscopy and scanning electronic microscopy revealed that these techniques are complementary each other: quantitative topographic information is directly extracted from the atomic force microscopy, while morphological aspects can be imaged by light microscopy or scanning electronic microscopy. A cavity generated by Cu-HyBrID laser in human dental enamel was also evaluated by atomic force microscopy. Structural and morphological differences between the fused and resolidified enamel from the cavity walls and the enamel from the natural tis sue were analyzed. A model, based on the Monte Carlo method described the propagation of CuHBr laser radiation and the absorbed energy distribution in dental tissues. Experimental measures with a CCD camera were used to semiquantitatively characterize the scattered light distribution in the tooth and they corroborated the model. It was observed that Rayleigh scattering and diffuse scattered radiation is predominant. The absorbed energy distribution map and the temperature variation along the beam propagation axis presented strong dependence with the absorption coefficient of the dental enamel and they cannot be deduced from the light distribution profile. The exposure time threshold for dental enamel melting and evaporation, irradiated by a specific condition of the green line of the Cu-HyBrID laser, was determined and a phenomenological model was discussed for the laser-matter interaction, based on pulse accumulation effect. Theoretical temperature calculations associated with experimental evidences strongly suggest that optical and thermal parameters should vary with temperature. The obtained exposure time threshold should correspond to the time necessary to the sample reach the critical temperature, at which the increase of absorption

  12. MMP20 Promotes a Smooth Enamel Surface, a Strong DEJ, and a Decussating Enamel Rod Pattern

    Science.gov (United States)

    Bartlett, John D.; Skobe, Ziedonis; Nanci, Antonio; Smith, Charles E.

    2012-01-01

    Mutations of the Matrix metalloproteinase-20 (MMP20, enamelysin) gene cause autosomal recessive amelogenesis imperfecta and Mmp20 ablated mice also have malformed dental enamel. Here we show that Mmp20 null mouse secretory stage ameloblasts maintained a columnar shape and were present as a single layer of cells. However, the null maturation stage ameloblasts covered extraneous nodules of ectopic calcified material formed at the enamel surface. Remarkably, nodule formation occurs in null mouse enamel when MMP20 is normally no longer expressed. The malformed enamel in Mmp20 null teeth was loosely attached to the dentin and the entire enamel layer tended to separate from the dentin indicative of a faulty DEJ. The enamel rod pattern was also altered in Mmp20 null mice. Each enamel rod is formed by a single ameloblast and is a mineralized record of the migration path of the ameloblast that formed it. The Mmp20 null mouse enamel rods were grossly malformed or were absent indicating that the ameloblasts do not migrate properly when backing away from the DEJ. Thus, MMP20 is required for ameloblast cell movement necessary to form the decussating enamel rod patterns, for the prevention of ectopic mineral formation, and to maintain a functional DEJ. PMID:22243247

  13. EPR dosimetry of cortical bone and tooth enamel irradiated with X and gamma rays: Study of energy dependence

    International Nuclear Information System (INIS)

    Schauer, D.A.; Links, J.M.; Desrosiers, M.F.; Le, F.G.; Seltzer, S.M.

    1994-01-01

    Previous investigators have reported that the radiation-induced EPR signal intensity in compact or cortical bone increases up to a factor of two with decreasing photon energy for a given absorbed dose. If the EPR signal intensity was dependent on energy, it could limit the application of EPR spectrometry and the additive reirradiation method to obtain dose estimates. We have recently shown that errors in the assumptions governing conversion of measured exposure to absorbed dose can lead to similar open-quotes apparentclose quotes energy-dependence results. We hypothesized that these previous results were due to errors in the estimated dose in bone, rather than the effects of energy dependence per se. To test this hypothesis we studied human adult cortical bone from male and female donors ranging in age from 23 to 95 years, and bovine tooth enamel, using 34 and 138 keV average energy X-ray beams and 137 Cs (662 keV) and 60 Co (1250 keV) γ rays. In a femur from a 47-year-old male (subject 1), there was a difference of borderline significance at the α = 0.05 level in the mean radiation-induced hydroxyapatite signal intensities as a function of photon energy. No other statistically significant differences in EPR signal intensity as a function of photon energy were observed in this subject, or in the tibia from a 23-year-old male (subject 2) and the femur from a 75-year-old female (subject 3). However, there was a trend toward a decrease (12-15%) in signal intensity at the lowest energy compared with the highest energy in subjects 1 and 3. Further analysis of the data from subject 1 revealed that this trend, which is in the opposite direction of previous reports but is consistent with theory, is statistically significant. There were no efforts of energy dependence in the tooth samples. 16 refs., 7 figs., 5 tabs

  14. Er:YAG and CTH:YAG laser radiation: contact versus non-contact enamel ablation and sonic-activated bulk composite placement

    International Nuclear Information System (INIS)

    Buckova, M; Kasparova, M; Dostalova, T; Jelinkova, H; Sulc, J; Nemec, M; Fibrich, M; Bradna, P; Miyagi, M

    2013-01-01

    Laser radiation can be used for effective caries removal and cavity preparation without significant thermal effects, collateral damage of tooth structure, or patient discomfort. The aim of this study was to compare the quality of tissue after contact or non-contact Er:YAG and CTH:YAG laser radiation ablation. The second goal was to increase the sealing ability of hard dental tissues using sonic-activated bulk filling material with change in viscosity during processing. The artificial caries was prepared in intact teeth to simulate a demineralized surface and then the Er:YAG or CTH:YAG laser radiation was applied. The enamel artificial caries was gently removed by the laser radiation and sonic-activated composite fillings were inserted. A stereomicroscope and then a scanning electron microscope were used to evaluate the enamel surface. Er:YAG contact mode ablation in enamel was quick and precise; the cavity was smooth with a keyhole shaped prism and rod relief arrangement without a smear layer. The sonic-activated filling material was consistently regularly distributed; no cracks or microleakage in the enamel were observed. CTH:YAG irradiation was able to clean but not ablate the enamel surface; in contact and also in non-contact mode there was evidence of melting and fusing of the enamel. (paper)

  15. Er:YAG and CTH:YAG laser radiation: contact versus non-contact enamel ablation and sonic-activated bulk composite placement

    Science.gov (United States)

    Buckova, M.; Kasparova, M.; Dostalova, T.; Jelinkova, H.; Sulc, J.; Nemec, M.; Fibrich, M.; Bradna, P.; Miyagi, M.

    2013-05-01

    Laser radiation can be used for effective caries removal and cavity preparation without significant thermal effects, collateral damage of tooth structure, or patient discomfort. The aim of this study was to compare the quality of tissue after contact or non-contact Er:YAG and CTH:YAG laser radiation ablation. The second goal was to increase the sealing ability of hard dental tissues using sonic-activated bulk filling material with change in viscosity during processing. The artificial caries was prepared in intact teeth to simulate a demineralized surface and then the Er:YAG or CTH:YAG laser radiation was applied. The enamel artificial caries was gently removed by the laser radiation and sonic-activated composite fillings were inserted. A stereomicroscope and then a scanning electron microscope were used to evaluate the enamel surface. Er:YAG contact mode ablation in enamel was quick and precise; the cavity was smooth with a keyhole shaped prism and rod relief arrangement without a smear layer. The sonic-activated filling material was consistently regularly distributed; no cracks or microleakage in the enamel were observed. CTH:YAG irradiation was able to clean but not ablate the enamel surface; in contact and also in non-contact mode there was evidence of melting and fusing of the enamel.

  16. Indirect veneer treatment of anterior maxillary teeth with enamel hypoplasia

    OpenAIRE

    Juniarti, Devi Eka

    2010-01-01

    Background: Nowadays, aesthetic rehabilitation becomes a necessity. It is affected by patient’s background, especially career, social and economic status. The aesthetic abnormality of anterior teeth i.e discoloration, malposition and malformation can affect patient’s appearance, especially during smile. These dental abnormalities, as a result, can decrease patient’s performance. Dental malformation, for instance, can be caused by developmental tooth defect, such as enamel hypoplasia. Enamel h...

  17. Frequency of Application of AmF/NaF/SnCl2 Solution and Its Potential in Inhibiting the Progression of Erosion in Human Dental Enamel - An In Vitro Study.

    Science.gov (United States)

    da Silva, Camilla Vieira; Nazello, Jessica Laporta; de Freitas, Patricia Moreira

    To evaluate whether increasing the frequency of its use can enhance the protective effect of AmF/NaF/SnCl2 solution against dental erosion. Sixty human enamel samples were obtained from sound human third molars, and after the formation of incipient erosive lesions (1% citric acid, pH 4.0, for 3 min), they were divided into five treatment groups (n = 12): G1 - deionised water (negative control); G2 - NaF solution (positive control) once a day; G3 - NaF solution (positive control) twice a day; G4 - AmF/NaF/SnCl2 solution once a day; G5 - AmF/NaF/SnCl2 solution twice a day. The samples were then subjected to 5 days of erosive cycling through 6 daily immersions (2 min each) in citric acid solution (0.05 M, pH 2.6). At the end of erosive cycling, surface wear was determined by means of optical profilometry. One-way ANOVA showed that the surface wear was affected by surface treatments (p enamel surface loss and its use twice a day potentiated its anti-erosive effect.

  18. Study of two new methods of geochronometry: dating method of carbonaceous formations by U-series disequilibrium gamma spectrometry; ESR dating method of rich U-content fossil dental enamel

    International Nuclear Information System (INIS)

    Ma, Jean-Luc

    1984-01-01

    First, the U-series disequilibrium dating method was re-examined using non-destructive γ-spectrometry. A new low-background (≤ 10 ppb U- equivalent) Ge-HP γ-spectrometer has been used to date travertine with small U-content (∼ 0.1 ppm) and low (≤ 5%) Th/U , content, by comparison with old-limestone γ-spectra. Second, a new ESR dating method has been developed using fossil dental enamel which is rich in U-content (10 - 100 ppm). Both methods were applied to Arago Cave (Tautavel, France): - with an ionium-age of 120 ka (10%), the upper travertine seems to have been set up during the Riss-deglaciation period. - the high (∼ 50%) Th/U-content samples of the intermediate travertine are un-datable. - the ESR-age of EQUUS mosbachensis enamel is 400 ka (10%) for the G-soil of Arago. XXI H. erectus, and 600 ka (10%) for the Q-soil above (- 1 m) of the lower travertine of which Io-age is older than 350 ka. (author)

  19. Evaluation of the cavity margins after Er:YAG laser ablation of the enamel and dentin

    Science.gov (United States)

    Dostalova, Tatjana; Krejsa, Otakar; Jelinkova, Helena; Hamal, Karel

    1994-12-01

    This study investigates the checks of cavity margin after enamel and dentin ablation. The Er:YAG laser enamel and dentin ablation can be directly connected with the danger of cracks originating in the enamel near the cavity. This study evaluates the quality of the enamel edges after Er:YAG laser preparation. The enamel and dentin of buccal surfaces were ablated by the Er:YAG laser radiation. An Erbium:YAG laser system with the energy of 200 mJ was used to generate 200 microsecond(s) long pulses of mid-infrared 2.94 micrometers light in multimode configuration. The laser was operating in a free running mode, the repetition rate being 0.5 Hz with average laser power of 100 mW. Laser radiation was focused on the tooth tissue. Water cooling was used during the procedure in order to prevent tooth tissue destruction. The time of laser preparation was 5 minutes. A cavity of class V was prepared. The teeth were immersed into 0.5% basic fuchsin and then centrifuged at 6000 rev/min for 20 minutes. The microphotographs of the margins stained with 0.5% basic fuchsin were made and then the longitudinal section of the teeth were evaluated. The micrographs of the longitudinal section were checked and measured afterwards. The effect of the investigated laser irradiation on the origin of cracks was analyzed in the scanning electron microscope. Micrographs of each tooth before and after the laser ablation were compared. Micrographs of the intact teeth after extraction present the cracks of the enamel. They depend on the pressure exerted during extraction. The influence of the laser ablation proper is it bears no signs of new cracks. The conclusions of this study demonstrate the non-invasive nature of the Er:YAG laser ablation of the hard dental tissues.

  20. To Analyse the Erosive Potential of Commercially Available Drinks on Dental Enamel and Various Tooth Coloured Restorative Materials - An In-vitro Study.

    Science.gov (United States)

    Karda, Babita; Jindal, Ritu; Mahajan, Sandeep; Sandhu, Sanam; Sharma, Sunila; Kaur, Rajwinder

    2016-05-01

    With the enormous change in life style pattern of a common man through the past few decades, there has been proportional variation in the amount and frequency of consumption of drinks. An increased consumption of these drinks will concurrently increase enamel surface roughness by demineralization, resulting in hypersensitivity and elevated caries risk. The present study was designed to evaluate the erosive potential of commercially available drinks on tooth enamel and various tooth coloured restorative materials. Extracted human teeth were taken and divided into four groups i.e. tooth enamel, glass ionomer cement, composite and compomer. Four commercially available drinks were chosen these were Coca -Cola, Nimbooz, Frooti and Yakult. The pH of each drink was measured. Each group was immersed in various experimental drinks for a period of 14 days. The erosive potential of each drink was measured by calculating the change in average surface roughness of these groups after the immersion protocol in various drinks. The data analysis was done by One Way Anova, Post-Hoc Bonferroni, and paired t -test. Group II-GIC showed highest values for mean of change in average surface roughness and the values were statistically significant (pCoca-cola showed the highest erosive potential and Yakult showed the lowest, there was no statistical significant difference between the results shown by Yakult and Frooti. Characteristics which may promote erosion of enamel and tooth coloured restorative materials were surface texture of the material and pH of the drinks.

  1. Modeling of thermal and optical effects in dental pulp during the irradiation with neodymium and diode lasers

    International Nuclear Information System (INIS)

    Farhat, Patricia Bahls de Almeida

    2003-01-01

    During the development of applications of high intensity lasers in the enamel and dentine, adverse thermal effects into the entire dental structure, including the pulp, must be verified. The measurement of the temperature in the intact pulp, however, is not a solved problem. For this purpose, models have been used frequently, using extracted teeth, with pulpal cavities filled with materials that simulate only thermal properties of the pulp. Current models, however, do not simulate optical properties of the pulp, not taking the remaining radiation in the pulp chamber into account. The aim of this study was to verify if the remaining radiation from neodymium and diode lasers that reach the pulp chamber, at the models using extracted bovine teeth, can cause local thermal effects. For this purpose, two models were developed, using extracted bovine teeth with their pulp chambers filled with water (simulating pulp thermal characteristics) without (model 1) and with (model 2) an optical absorbent. Models were radiated with 1 W. The obtained results show that, for both lasers, the temperature rise in model 2 pulp chamber is: up to 11 % higher than in the model 1 when the enamel is radiated; and up to 37% higher than in the model 1 when dentine is radiated (1 mm from the pulp), indicating that the level of the remaining radiation is relevant for the construction of models excited by the neodymium and diode lasers. (author)

  2. The molecular basis of hereditary enamel defects in humans.

    Science.gov (United States)

    Wright, J T; Carrion, I A; Morris, C

    2015-01-01

    The formation of human enamel is highly regulated at the molecular level and involves thousands of genes. Requisites for development of this highly mineralized tissue include cell differentiation; production of a unique extracellular matrix; processing of the extracellular matrix; altering of cell function during different stages of enamel formation; cell movement and attachment; regulation of ion and protein movement; and regulation of hydration, pH, and other conditions of the microenvironment, to name just a few. Not surprising, there is a plethora of hereditary conditions with an enamel phenotype. The objective of this review was to identify the hereditary conditions listed on Online Mendelian Inheritance in Man (OMIM) that have an associated enamel phenotype and whether a causative gene has been identified. The OMIM database was searched with the terms amelogenesis, enamel, dental, and tooth, and all results were screened by 2 individuals to determine if an enamel phenotype was identified. Gene and gene product function was reviewed on OMIM and from publications identified in PubMed. The search strategy revealed 91 conditions listed in OMIM as having an enamel phenotype, and of those, 71 have a known molecular etiology or linked genetic loci. The purported protein function of those conditions with a known genetic basis included enzymes, regulatory proteins, extracellular matrix proteins, transcription factors, and transmembrane proteins. The most common enamel phenotype was a deficient amount of enamel, or enamel hypoplasia, with hypomineralization defects being reported less frequently. Knowing these molecular defects allows an initial cataloging of molecular pathways that lead to hereditary enamel defects in humans. This knowledge provides insight into the diverse molecular pathways involved in enamel formation and can be useful when searching for the genetic etiology of hereditary conditions that involve enamel. © International & American Associations for

  3. Analysis of human enamel and dentine by neutron activation analysis

    International Nuclear Information System (INIS)

    Soares, Marco A.B.

    2005-01-01

    Determination of trace elements in dental tissues has been of great interest to study the correlation between element composition and caries as well as food habits of individuals. In the present study dentine and enamel samples from healthy individuals were analysed by neutron activation analysis. The teeth were provided form dental clinics, and they were previously washed using purified water and acetone. Then they were dried at 40 deg C and ground in a agate mortar. The samples and element standards were irradiated with thermal neutrons at the IEA-R1 nuclear reactor. Long irradiations of 8 h under thermal neutron flux of 5x10 12 n cm -2 s -1 were used for Ca, Na, Sr and Zn determinations. In short irradiations of 15 s and under neutron flux of 10 12 n cm -2 s -1 the elements Mg, Mn, Na e Sr were determined. The induced gamma activities of the samples and standards were measured using a hyperpure Ge detector coupled to a gamma ray spectrometer. Elemental concentrations were calculated by comparative method. Results obtained showed that Ca, Mg and Na are present in both tissues at the level of percentages and the elements Mn, Sr and Zn at the μg g -1 levels. For quality control of the results the certified reference materials NIST 1400 Bone Ash and NIST 1486 Bone Meal were analysed. (author)

  4. Teeth and irradiation: dental care and treatment of osteoradionecrosis after irradiation in head and neck cancer; Dent et irradiation: prevention et traitement des complications dentaires de la radiotherapie y compris l'osteoradionecrose

    Energy Technology Data Exchange (ETDEWEB)

    Thariat, J.; Ortholan, C. [Centre Antoine-Lacassagne, Service de radiotherapie, 06 - Nice (France); Thariat, J.; Darcourt, V.; Poissonnet, G.; Dassonville, O.; Marcy, P.Y.; Bozec, A.; Ortholan, C.; Santini, J. [Universite de Nice Sophia-Antipolis, 06 - Nice (France); Thariat, J. [IBDC CNRS UMR 6543, 06 - Nice (France); Mones, E. de [CHU de Bordeaux, Service ORL, 33 - Bordeaux (France); Darcourt, V. [Centre Antoine-Lacassagne, Service de radiotherapie-dentisterie, 06 - Nice (France); Poissonnet, G.; Dassonville, O.; Bozec, A.; Santini, J. [Centre Antoine-Lacassagne, Service ORL, 06 - Nice (France); Marcy, P.Y. [Centre Antoine-Lacassagne, Service de radiologie, 06 - Nice (France); Guevara, N. [CHU, Service ORL et de chirurgie maxillofaciale, 06 - Nice (France); Bensadoun, R.J. [CHU, Service de radiotherapie, 86 - Poitiers (France)

    2010-04-15

    Pre-irradiation dental care depends on teeth health, fields and dose of irradiation, compliance to fluorides, cessation of tobacco and psycho-social cofactors. Dental care aims at preventing complications and preserving the quality of life (eating, speech, and aesthetics). The role of hyperbaric oxygen therapy for the prevention of osteoradionecrosis after teeth removal on the mandible in areas receiving 50 Gy or more is still controversial. Medical treatments may be sufficient for early stages of osteoradionecrosis (antibiotics, pain killers, non-steroidal anti-inflammatory drugs as well as clodronate, vitamin E, pentoxifylline). However, reconstructive surgery should not be delayed in advanced stages of osteoradionecrosis. New irradiation techniques are changing dose distributions and therefore require close collaboration between odonto-stomatologists and radiation oncologists to define the best dental care. (authors)

  5. The combined action of UV irradiation and chemical treatment on the titanium surface of dental implants

    Energy Technology Data Exchange (ETDEWEB)

    Spriano, Silvia [Politecnico di Torino, Department of Applied Science and Technology, Corso Duca degli Abruzzi, 24-10129 Torino (Italy); Ferraris, Sara, E-mail: sara.ferraris@polito.it [Politecnico di Torino, Department of Applied Science and Technology, Corso Duca degli Abruzzi, 24-10129 Torino (Italy); Bollati, Daniele; Morra, Marco; Cassinelli, Clara [Nobil Bio Ricerche, Portacomaro (Italy); Lorenzon, Giorgio [Centro Chirurgico, Via Mallonetto, 47, 10032, Brandizzo Torino (Italy)

    2015-09-15

    Highlights: • A combined UV irradiation and H{sub 2}O{sub 2} treatment was applied to titanium surfaces. • A thin, homogeneous, not porous, crack-free and bioactive oxide layer was obtained. • The process significantly improves the biological response of titanium surfaces. • A clinical case demonstrates the effectiveness of the proposed treatment. - Abstract: The purpose of this paper is to describe an innovative treatment for titanium dental implants, aimed at faster and more effective osteointegration. The treatment has been performed with the use of hydrogen peroxide, whose action was enhanced by concomitant exposure to a source of ultraviolet light. The developed surface oxide layer was characterized from the physical and chemical points of view. Moreover osteoblast-like SaOS2 cells were cultured on treated and control titanium surfaces and cell behavior investigated by scanning electron microscope observation and gene expression measurements. The described process produces, in only 6 min, a thin, homogeneous, not porous, free of cracks and bioactive (in vitro apatite precipitation) oxide layer. High cell density, peculiar morphology and overexpression of several genes involved with osteogenesis have been observed on modified surfaces. The proposed process significantly improves the biological response of titanium surfaces, and is an interesting solution for the improvement of bone integration of dental implants. A clinical application of the described surfaces, with a 5 years follow-up, is reported in the paper, as an example of the effectiveness of the proposed treatment.

  6. Treatment of tooth fracture by medium-energy CO2 laser and DP-bioactive glass paste: the interaction of enamel and DP-bioactive glass paste during irradiation by CO2 laser.

    Science.gov (United States)

    Lin, C P; Tseng, Y C; Lin, F H; Liao, J D; Lan, W H

    2001-03-01

    Acute trauma or trauma associated with occlusal disturbance can produce tooth crack or fracture. Although several methods are proposed to treat the defect, however, the prognosis is generally poor. If the fusion of a tooth fracture by laser is possible, it will offer an alternative to extraction or at least serve as an adjunctive treatment in the reconstruction. We have tried to use a continuous-wave CO2 laser and a newly developed DP-bioactive glass paste (DPGP) to fuse or bridge tooth crack or fracture lines. Both the DP-bioactive glass paste and tooth enamel have strong absorption bands at the wavelength of 10.6 microm. Therefore, under CO2 laser, DPGP and enamel should have an effective absorption and melt together. The interface between DPGP and enamel could be regarded as a mixture of DPGP and enamel (DPG-E). The study focused on the phase transformation, microstructure, functional group and thermal behavior of DPG-E with or without CO2 laser irradiation, by the analytical techniques of XRD, FTIR, DTA/TGA, and SEM. The results of XRD showed that the main crystal phase in the DPG-E was dicalcium phosphate dihydrate (CaHPO4.2H2O). It changed into CaHPO4, gamma-Ca2P2O7, beta-Ca2P2O7 and finally alpha-Ca2P2O7 with increasing temperature. In the FTIR analysis, the 720 cm(-1) absorption band ascribed to the P-O-P linkage in pyrophosphate rose up and the intensities of the OH- bands reduced after laser irradiation. In regard to the results of DTA/TGA after irradiation, the weight loss decreased due to the removal of part of absorption water and crystallization water by the CO2 laser. SEM micrographs revealed that the melted masses and the plate-like crystals formed a tight chemical bond between the enamel and DPGP. We expect that DPGP with the help of CO2 laser can be an alternative to the treatment of tooth crack or fracture.

  7. Potential of CO2 lasers (10.6 µm associated with fluorides in inhibiting human enamel erosion

    Directory of Open Access Journals (Sweden)

    Thayanne Monteiro RAMOS-OLIVEIRA

    2014-01-01

    Full Text Available This in vitro study aimed to investigate the potential of CO2 lasers associated with different fluoride agents in inhibiting enamel erosion. Human enamel samples were randomly divided into 9 groups (n = 12: G1-eroded enamel; G2-APF gel; G3-AmF/NaF gel; G4-AmF/SnF2 solution; G5-CO2 laser (λ = 10.6 µm+APF gel; G6-CO2 laser+AmF/NaF gel; G7-CO2laser+AmF/SnF2solution; G8-CO2 laser; and G9-sound enamel. The CO2 laser parameters were: 0.45 J/cm2; 6 μs; and 128 Hz. After surface treatment, the samples (except from G9 were immersed in 1% citric acid (pH 4.0, 3 min. Surface microhardness was measured at baseline and after surface softening. The data were statistically analyzed by one-way ANOVA and Tukey’s tests (p < 0.05. G2 (407.6 ± 37.3 presented the highest mean SMH after softening, followed by G3 (407.5 ± 29.8 and G5 (399.7 ± 32.9. Within the fluoride-treated groups, G4 (309.0 ± 24.4 had a significantly lower mean SMH than G3 and G2, which were statistically similar to each other. AmF/NaF and APF application showed potential to protect and control erosion progression in dental enamel, and CO2 laser irradiation at 0.45J/cm2 did not influence its efficacy. CO2 laser irradiation alone under the same conditions could also significantly decrease enamel erosive mineral loss, although at lower levels.

  8. Evaluation of the bleached human enamel by Scanning Electron Microscopy Avaliação do esmalte dental humano submetido ao tratamento clareador por meio de Microscopia Eletrônica de Varredura

    Directory of Open Access Journals (Sweden)

    Carolina Baptista Miranda

    2005-06-01

    Full Text Available Since bleaching has become a popular procedure, the effect of peroxides on dental hard tissues is of great interest in research. Purpose: The aim of this in vitro study was to perform a qualitative analysis of the human enamel after the application of in-office bleaching agents, using Scanning Electron Microscopy (SEM. Materials and Methods: Twenty intact human third molars extracted for orthodontic reasons were randomly divided into four groups (n=5 treated as follows: G1- storage in artificial saliva (control group; G2- four 30-minute applications of 35% carbamide peroxide (total exposure: 2h; G3- four 2-hour exposures to 35% carbamide peroxide (total exposure: 8h; G4- two applications of 35% hydrogen peroxide, which was light-activated with halogen lamp at 700mW/cm² during 7min and remained in contact with enamel for 20min (total exposure: 40min. All bleaching treatments adopted in this study followed the application protocols advised by manufacturers. Evaluation of groups submitted to 35% carbamide peroxide was carried out after two time intervals (30 minutes and 2 hours per session, following the extreme situations recommended by the manufacturer. Specimens were prepared for SEM analysis performing gold sputter coating under vacuum and were examined using 15kV at 500x and 2000x magnification. Results: Morphological alterations on the enamel surface were similarly detected after bleaching with either 35% carbamide peroxide or 35% hydrogen peroxide. Surface porosities were characteristic of an erosive process that took place on human enamel. Depression areas, including the formation of craters, and exposure of enamel rods could also be detected. Conclusion: Bleaching effects on enamel morphology were randomly distributed throughout enamel surface and various degrees of enamel damage could be noticed. Clinical significance: In-office bleaching materials may adversely affect enamel morphology and therefore should be used with caution.Desde o

  9. Measurement of in-vivo dosage increase due to dental alloys during therapeutic irradiation of the mouth cavity

    International Nuclear Information System (INIS)

    Thilmann, C.; Mose, S.; Saran, F.; Schopohl, B.; Boettcher, H.D.

    1995-01-01

    The degree of dosage increase in the immediate surrounding of metallic dental materials was measured in an in-vivo study during therapeutic irradiation with 60 Co gamma rays in the area of mouth cavity of 11 patients. Measurements were carried out by thermoluminescent dosimetry at permamently fixed golden teeth and alloy specimens containing gold and palladium and amalgam. The following relative dodage values according to a simultanelusly measured reference value were measured at the surface of the different dental materials: 161% near fixed golden caps, 168% near the specimen containing gold in a high percentage, 133% near the specimen of palladium and 161% near the specimen of amalgam. The in vivo measured dosage increases due to metallic dental prosthesis are less than values obtained using back scatter arramgements for irradiating phantoms. Despite this, they could be of clinical relevance. Thus the usage of a mucous membrane protection during irradiation with 60 Co, as a means of preventing local lesions of the oral mucosa, due to dental alloys within the treatment volume remains inevitable. (orig.) [de

  10. Effects of gamma radiation on hard dental tissues of albino rats using scanning electron microscope - Part 1

    Science.gov (United States)

    El-Faramawy, Nabil; Ameen, Reham; El-Haddad, Khaled; Maghraby, Ahmed; El-Zainy, Medhat

    2011-12-01

    In the present study, 40 adult male albino rats were used to study the effect of gamma radiation on the hard dental tissues (enamel surface, dentinal tubules and the cementum surface). The rats were irradiated at 0.2, 0.5, 1.0, 2.0, 4.0 and 6.0 Gy gamma doses. The effects of irradiated hard dental tissues samples were investigated using a scanning electron microscope. For doses up to 0.5 Gy, there was no evidence of the existence of cracks on the enamel surface. With 1 Gy irradiation dose, cracks were clearly observed with localized erosive areas. At 2 Gy irradiation dose, the enamel showed morphological alterations as disturbed prismatic and interprismatic areas. An increase in dentinal tubules diameter and a contemporary inter-tubular dentine volume decrease were observed with higher irradiation dose. Concerning cementum, low doses,<0.5 Gy, showed surface irregularities and with increase in the irradiation dose to≥1 Gy, noticeable surface irregularities and erosive areas with decrease in Sharpey's fiber sites were observed. These observations could shed light on the hazardous effects of irradiation fields to the functioning of the human teeth.

  11. Natural enamel caries in polarized light microscopy: differences in histopathological features derived from a qualitative versus a quantitative approach to interpret enamel birefringence.

    Science.gov (United States)

    De Medeiros, R C G; Soares, J D; De Sousa, F B

    2012-05-01

    Lesion area measurement of enamel caries using polarized light microscopy (PLM) is currently performed in a large number of studies, but measurements are based mainly on a mislead qualitative interpretation of enamel birefringence in a single immersion medium. Here, five natural enamel caries lesions are analysed by microradiography and in PLM, and the differences in their histopathological features derived from a qualitative versus a quantitative interpretation of enamel birefringence are described. Enamel birefringence in different immersion media (air, water and quinoline) is interpreted by both qualitative and quantitative approaches, the former leading to an underestimation of the depth of enamel caries mainly when the criterion of validating sound enamel as a negatively birefringent area in immersion in water is used (a current common practice in dental research). Procedures to avoid the shortcomings of a qualitative interpretation of enamel birefringence are presented and discussed. © 2012 The Authors Journal of Microscopy © 2012 Royal Microscopical Society.

  12. 'In vitro' study of the efficacy of diode laser and LED irradiation during dental bleaching

    International Nuclear Information System (INIS)

    Barroso, Marcia Cristina da Silva

    2003-01-01

    This in vitro study evaluated the efficacy of LED and laser diode irradiation during the dental bleaching procedure, using two bleaching agents (Opalescence X-tra and HP Whiteness). The diode laser and the LED were operated in the continuous mode, with wavelength of 808 nm and 470 nm, respectively. The results of the irradiations were characterized with the CIELAB system calculating the L * a * b * values for the darkened and the bleached teeth (60 bovine incisors). This is to our knowledge the first time that light sources laser and LED are compared with respect to their whitening capability when applied to different agents. Significant differences in the chroma value are obtained for the two whitening agents and for the different light sources, too. Also, in terms of luminance, the combination of laser/ Whiteness HP showed significantly better results than when the same agent was used alone or in combination with LED. Best overall results are obtained with the combination of Whiteness HP and laser. (author)

  13. Dental OCT

    Science.gov (United States)

    Wilder-Smith, Petra; Otis, Linda; Zhang, Jun; Chen, Zhongping

    This chapter describes the applications of OCT for imaging in vivo dental and oral tissue. The oral cavity is a diverse environment that includes oral mucosa, gingival tissues, teeth and their supporting structures. Because OCT can image both hard and soft tissues of the oral cavity at high resolution, it offers the unique capacity to identity dental disease before destructive changes have progressed. OCT images depict clinically important anatomical features such as the location of soft tissue attachments, morphological changes in gingival tissue, tooth decay, enamel thickness and decay, as well as the structural integrity of dental restorations. OCT imaging allows for earlier intervention than is possible with current diagnostic modalities.

  14. The investigation of usage of fluorapatite mineral (Ca{sub 5}F(PO{sub 4}){sub 3}) in tooth enamel under the different pre-irradiation thermal treatments

    Energy Technology Data Exchange (ETDEWEB)

    Toktamiş, Hüseyin, E-mail: toktamis@gantep.edu.tr [University of Gaziantep, Department of Engineering Physics, 27310 Gaziantep (Turkey); Toktamiş, Dilek; Yilmaz, S. Merve; Yazici, A. Necmeddin [University of Gaziantep, Department of Engineering Physics, 27310 Gaziantep (Turkey); Yildirim, Cihan [University of Gaziantep, Faculty of Dentistry, 27310 Gaziantep (Turkey); Özbiçki, Özlem [Dentalazer Hospital, 27310 Gaziantep (Turkey)

    2015-01-20

    Highlights: • The fluorapatite mineral extracted from tooth enamel shows TL properties. • The pre-irradiation annealing process affects the TL glow curve shape. • A huge increase was observed in maximum TL for sample annealed at 1100 °C. • Annealing about 120 min causes a huge enhancement in maximum TL peak intensity • The best reproducibility is obtained at 1000 °C of annealing temperature. - Abstract: Fluorapatite Ca{sub 5}F(PO{sub 4}){sub 3} is a kind of important thermoluminescence dosimeter (TLD) material, because the effective atomic number of fluorapatite is close to that of human bones and teeth. In the present study, thermoluminescence (TL) properties of fluorapatite mineral in tooth enamel under the different annealing temperatures with various annealing times were investigated. This study reveals that the fluorapatite in tooth enamel exhibits TL properties. Annealing of the sample affects extremely the TL glow curve and causes a huge enhancement in the sensitization of TL peak. The sample annealed at 1000 °C about 120 min gives best TL peak intensity (150 factors than un-annealed sample) and has a distinct peak around 230 °C. Also, the best reproducibility was observed for 1000 °C annealed sample temperature while un-annealed sample shows the worst reproducibility. Moreover, a good linearity in dose response is observed in the samples annealed at 400 °C and 700 °C.

  15. Enamel subsurface damage due to tooth preparation with diamonds.

    Science.gov (United States)

    Xu, H H; Kelly, J R; Jahanmir, S; Thompson, V P; Rekow, E D

    1997-10-01

    In clinical tooth preparation with diamond burs, sharp diamond particles indent and scratch the enamel, causing material removal. Such operations may produce subsurface damage in enamel. However, little information is available on the mechanisms and the extent of subsurface damage in enamel produced during clinical tooth preparation. The aim of this study, therefore, was to investigate the mechanisms of subsurface damage produced in enamel during tooth preparation by means of diamond burs, and to examine the dependence of such damage on enamel rod orientation, diamond particle size, and removal rate. Subsurface damage was evaluated by a bonded-interface technique. Tooth preparation was carried out on two enamel rod orientations, with four clinical diamond burs (coarse, medium, fine, and superfine) used in a dental handpiece. The results of this study showed that subsurface damage in enamel took the form of median-type cracks and distributed microcracks, extending preferentially along the boundaries between the enamel rods. Microcracks within individual enamel rods were also observed. The median-type cracks were significantly longer in the direction parallel to the enamel rods than perpendicular to the rods. Preparation with the coarse diamond bur produced cracks as deep as 84 +/- 30 microns in enamel. Finishing with fine diamond burs was effective in crack removal. The crack lengths in enamel were not significantly different when the removal rate was varied. Based on these results, it is concluded that subsurface damage in enamel induced by tooth preparation takes the form of median-type cracks as well as inter- and intra-rod microcracks, and that the lengths of these cracks are sensitive to diamond particle size and enamel rod orientation, but insensitive to removal rate.

  16. Relationship between free radical content in human tooth enamel and radiation dose

    International Nuclear Information System (INIS)

    Zhou Yongzeng; Wang Jiadong; Jia Xiaomei; Wu Ke; Cong Jianbo; Sun Cunpu

    2000-01-01

    Application of ESR technique of tooth enamel have become more and more wide-spread in accidental and retrospective dosimetry. The purpose of this paper is to study relationship between free radical content in tooth enamel and radiation dose. Method Samples of 25 Chinese adult teeth, 25 child permanent teeth and 35 milk teeth were used in the study. All teeth were obtained from patients in the course of dental practice. Tooth enamel was separated from dentine using dental drill and then crushed manually into grains of about 0.5-1.5 mm in diameter. The mass of each sample is 100 mg. Signal intensity of enamel samples was measured by ESR technique (Bruker-ESP300). Parameters used were modulation frequency 50 KHz, modulation amplitude 0.2 mT, time constant 41 ms, scan width 15 mT, microwave power 5 mw, room temperature. Samples of 25 adult teeth, 25 child permanent teeth and 35 milk teeth were divided into 5 dose groups, respectively, and irradiated with 60 Co γ-ray at dose rate of 0.48 Gy/min. Radiation doses of the 5 groups were 0.30, 0.50, 1.00, 3.00 and 5.00 Gy, respectively. After irradiation, each sample was subjected to ESR measurements. There is no significant difference in background signal intensity between male and female samples for both child permanent teeth and milk teeth. And also no significant difference in background signal intensity between child permanent teeth and milk teeth was observed. Results of study on adult teeth indicated that radiation sensitivity of different teeth is fairly uniform. Free radical content in enamel of child permanent teeth and milk teeth increases linearly with increasing of radiation dose, and similar results were obtained for adult teeth. Slope of the dose-response curve for adult teeth is somewhat steeper than that for milk teeth. There exists a linear relation between ESR signals intensity and radiation doses for adult teeth, child permanent and milk teeth. In the case of radiation accident, the dose-response curves

  17. Interaction of slow highly charged ions with hard dental tissue: studies of fluoride uptake and reminalization efficacy

    International Nuclear Information System (INIS)

    Daskalova, A; Kasperski, G; Rousseau, P; Domaracka, A; Lawicki, A

    2014-01-01

    TOF-SIMS mass spectroscopy data are presented on ion irradiation of hard dental tissue using a beam of 129 Xe 20+ (15 kV) ions delivered in the ARIBE facility by an ECR source. The investigation was focused on the mass distribution of the fragment ions. A comparison is made between the mass spectra from hard dental tissue treated by olaflur-(C 27 H 60 F 2 N 2 O 3 ) and untreated hard dental tissue obtained under irradiation by low-energy highly-charged ions (HCIs). We found significant differences between the mass spectra of enamel after introducing amine fluoride (olaflur) and the mass spectra of pure untreated enamel. Further, we separated out the effects caused by radiation induced in the tooth enamel from those induced in dentin, which has not been performed before. In order to conduct a further detailed analysis, it is necessary to extend the research scope to include the influence of fluorine compounds on enamel and dentin.

  18. Survival of dental implants in native and grafted bone in irradiated head and neck cancer patients: a retrospective analysis.

    Science.gov (United States)

    Buddula, Aravind; Assad, Daniel A; Salinas, Thomas J; Garces, Yolanda I

    2011-01-01

    To study the long-term survival of dental implants placed in native or grafted bone in irradiated bone in subjects who had received radiation for head and neck cancer. A retrospective chart review was conducted for all patients who received dental implants following radiation treatment for head and neck cancer between May 1, 1987 and July 1, 2008. Only patients irradiated with a radiation dose of 50 Gy or greater and those who received dental implants in the irradiated field after head and neck radiation were included in the study. The associations between implant survival and patient/implant characteristics were estimated by fitting univariate marginal Cox proportional hazards models. A total of 48 patients who had prior head and neck radiation had 271 dental implants placed during May 1987-July 2008. There was no statistically significant difference between implant failure in native and grafted bone (P=0.76). Survival of implants in grafted bone was 82.3% and 98.1% in maxilla and mandible, respectively, after 3 years. Survival of implants in native bone in maxilla and mandible was 79.8% and 100%, respectively, after 3 years. For implants placed in the native bone, there was a higher likelihood of failure in the maxilla compared to the mandible and there was also a tendency for implants placed in the posterior region to fail compared to those placed in the anterior region. There was no significant difference in survival when implants were placed in native or grafted bone in irradiated head and neck cancer patients. For implants placed in native bone, survival was significantly influenced by the location of the implant (maxilla or mandible, anterior or posterior).

  19. Survival of dental implants in native and grafted bone in irradiated head and neck cancer patients: A retrospective analysis

    Directory of Open Access Journals (Sweden)

    Aravind Buddula

    2011-01-01

    Full Text Available Aim: To study the long-term survival of dental implants placed in native or grafted bone in irradiated bone in subjects who had received radiation for head and neck cancer. Materials and Methods: A retrospective chart review was conducted for all patients who received dental implants following radiation treatment for head and neck cancer between May 1, 1987 and July 1, 2008. Only patients irradiated with a radiation dose of 50 Gy or greater and those who received dental implants in the irradiated field after head and neck radiation were included in the study. The associations between implant survival and patient/implant characteristics were estimated by fitting univariate marginal Cox proportional hazards models. Results: A total of 48 patients who had prior head and neck radiation had 271 dental implants placed during May 1987-July 2008. There was no statistically significant difference between implant failure in native and grafted bone (P=0.76. Survival of implants in grafted bone was 82.3% and 98.1% in maxilla and mandible, respectively, after 3 years. Survival of implants in native bone in maxilla and mandible was 79.8% and 100%, respectively, after 3 years. For implants placed in the native bone, there was a higher likelihood of failure in the maxilla compared to the mandible and there was also a tendency for implants placed in the posterior region to fail compared to those placed in the anterior region. Conclusion: There was no significant difference in survival when implants were placed in native or grafted bone in irradiated head and neck cancer patients. For implants placed in native bone, survival was significantly influenced by the location of the implant (maxilla or mandible, anterior or posterior.

  20. Automated classification and visualization of healthy and pathological dental tissues based on near-infrared hyper-spectral imaging

    Science.gov (United States)

    Usenik, Peter; Bürmen, Miran; Vrtovec, Tomaž; Fidler, Aleš; Pernuš, Franjo; Likar, Boštjan

    2011-03-01

    Despite major improvements in dental healthcare and technology, dental caries remains one of the most prevalent chronic diseases of modern society. The initial stages of dental caries are characterized by demineralization of enamel crystals, commonly known as white spots which are difficult to diagnose. If detected early enough, such demineralization can be arrested and reversed by non-surgical means through well established dental treatments (fluoride therapy, anti-bacterial therapy, low intensity laser irradiation). Near-infrared (NIR) hyper-spectral imaging is a new promising technique for early detection of demineralization based on distinct spectral features of healthy and pathological dental tissues. In this study, we apply NIR hyper-spectral imaging to classify and visualize healthy and pathological dental tissues including enamel, dentin, calculus, dentin caries, enamel caries and demineralized areas. For this purpose, a standardized teeth database was constructed consisting of 12 extracted human teeth with different degrees of natural dental lesions imaged by NIR hyper-spectral system, X-ray and digital color camera. The color and X-ray images of teeth were presented to a clinical expert for localization and classification of the dental tissues, thereby obtaining the gold standard. Principal component analysis was used for multivariate local modeling of healthy and pathological dental tissues. Finally, the dental tissues were classified by employing multiple discriminant analysis. High agreement was observed between the resulting classification and the gold standard with the classification sensitivity and specificity exceeding 85 % and 97 %, respectively. This study demonstrates that NIR hyper-spectral imaging has considerable diagnostic potential for imaging hard dental tissues.

  1. Effects of the low-intensity red laser radiation on the fluoride uptake in enamel. A clinical trial

    International Nuclear Information System (INIS)

    Nakasone, Regina Keiko

    2004-01-01

    Fluoride has been the most important preventive method on development of the caries. This in vivo study evaluated the effects of low-intensity red laser radiation on the fluoride uptake in enamel. Ten healthy participants were recruited for this study. The two maxillary central incisors of each volunteer to be biopsied were used and divided into 4 groups: group G C (control, which was untreated; group G F (fluoride), which received topical acidulated phosphate fluoride (APF) 1,23% treatment for 4 minutes; group G LF (laser + fluoride), which was irradiated with a low-intensity diode laser (λ= 660 nm and dose= 6 J/cm 2 ) with APF application after irradiation and group G FL (fluoride + laser), which received APF before irradiation using the same parameters as G LF . The determination of fluoride was performed using a fluoride ion electrode after an acid-etch enamel biopsy. The results show a significant increase of the fluoride uptake in enamel for groups G F , G LF and G FL when compared to control group. Although a percentage increase of 57% was observed for G LF with respect to G F , there were no statistical differences among treated groups. These findings suggest that low-intensity laser radiation used before APF could be employed in the clinical practice to prevent dental caries. (author)

  2. The Molecular Basis of Hereditary Enamel Defects in Humans

    Science.gov (United States)

    Carrion, I.A.; Morris, C.

    2015-01-01

    The formation of human enamel is highly regulated at the molecular level and involves thousands of genes. Requisites for development of this highly mineralized tissue include cell differentiation; production of a unique extracellular matrix; processing of the extracellular matrix; altering of cell function during different stages of enamel formation; cell movement and attachment; regulation of ion and protein movement; and regulation of hydration, pH, and other conditions of the microenvironment, to name just a few. Not surprising, there is a plethora of hereditary conditions with an enamel phenotype. The objective of this review was to identify the hereditary conditions listed on Online Mendelian Inheritance in Man (OMIM) that have an associated enamel phenotype and whether a causative gene has been identified. The OMIM database was searched with the terms amelogenesis, enamel, dental, and tooth, and all results were screened by 2 individuals to determine if an enamel phenotype was identified. Gene and gene product function was reviewed on OMIM and from publications identified in PubMed. The search strategy revealed 91 conditions listed in OMIM as having an enamel phenotype, and of those, 71 have a known molecular etiology or linked genetic loci. The purported protein function of those conditions with a known genetic basis included enzymes, regulatory proteins, extracellular matrix proteins, transcription factors, and transmembrane proteins. The most common enamel phenotype was a deficient amount of enamel, or enamel hypoplasia, with hypomineralization defects being reported less frequently. Knowing these molecular defects allows an initial cataloging of molecular pathways that lead to hereditary enamel defects in humans. This knowledge provides insight into the diverse molecular pathways involved in enamel formation and can be useful when searching for the genetic etiology of hereditary conditions that involve enamel. PMID:25389004

  3. Effects of ultrasonic instrumentation on enamel surfaces with various defects.

    Science.gov (United States)

    Kim, S-Y; Kang, M-K; Kang, S-M; Kim, H-E

    2018-05-01

    The aim of this study was to analyse the enamel damage caused by ultrasonic scaling of teeth with various enamel conditions that are difficult to identify by visual inspection, such as enamel cracks, early caries and resin restorations. In total, 120 tooth surfaces were divided into 4 experimental groups using a quantitative light-induced fluorescence-digital system: sound enamel group, enamel cracks group, early caries group and resin restoration group. A skilled dental hygienist performed ultrasonic scaling under a standardized set of conditions: a ≤ 15° angle between the scaler tip and tooth surface and 40-80 g of lateral pressure at the rate of 12 times/10 s. Following scaling, the depth of enamel damage was measured using a surface profilometer and observed using scanning electron microscopy (SEM). The damage depth was the greatest in the enamel cracks group (37.63 ± 34.42 μm), followed by the early caries group (26.81 ± 8.67 μm), resin restoration group (19.63 ± 6.73 μm) and the sound enamel group (17.00 ± 5.66 μm). The damage depth was significantly deeper in the enamel cracks and early caries groups than in the sound enamel group (P enamel loss in the enamel cracks, early caries and resin restoration groups. The results of this study suggest that ultrasonic scaling can cause further damage to teeth with enamel cracks, early caries and resin restorations. Therefore, accurate identification of tooth conditions and calculus before the initiation of ultrasonic scaling is necessary to minimize damage. © 2018 John Wiley & Sons A/S. Published by John Wiley & Sons Ltd.

  4. Measurement of opalescence of tooth enamel.

    Science.gov (United States)

    Lee, Yong-Keun; Yu, Bin

    2007-08-01

    Opalescent dental esthetic restoratives look natural and esthetic in any light, react to light in the same manner as the natural tooth and show improved masking effect. The objective of this study was to determine the opalescence of tooth enamel with reflection spectrophotometers. Color of intact bovine and human enamel was measured in the reflectance and transmittance modes. Two kinds of spectrophotometers were used for bovine and one kind was used for human enamel. The opalescence parameter (OP) was calculated as the difference in yellow-blue color coordinate (CIE Deltab(*)) and red-green color coordinate (CIE Deltaa(*)) between the reflected and transmitted colors. Mean OP value of bovine enamel was 10.6 (+/-1.4) to 19.0 (+/-2.1), and varied by the configuration of spectrophotometers. Mean OP value of human enamel was 22.9 (+/-1.9). Opalescence varied by the configuration of measuring spectrophotometer and the species of enamel. These values could be used in the development of esthetic restorative materials.

  5. Tooth enamel hypoplasia in PHACE syndrome.

    Science.gov (United States)

    Chiu, Yvonne E; Siegel, Dawn H; Drolet, Beth A; Hodgson, Brian D

    2014-01-01

    Individuals with PHACE syndrome (posterior fossa malformations, hemangiomas, arterial anomalies, cardiac defects, eye abnormalities, sternal cleft, and supraumbilical raphe syndrome) have reported dental abnormalities to their healthcare providers and in online forums, but dental involvement has not been comprehensively studied. A study was conducted at the third PHACE Family Conference, held in Milwaukee, Wisconsin, in July 2012. A pediatric dentist examined subjects at enrollment. Eighteen subjects were enrolled. The median age was 4.2 years (range 9 mos-9 yrs; 14 girls, 4 boys). Eleven of 18 patients had intraoral hemangiomas and five of these (50%) had hypomature enamel hypoplasia. None of the seven patients without intraoral hemangiomas had enamel hypoplasia. No other dental abnormalities were seen. Enamel hypoplasia may be a feature of PHACE syndrome when an intraoral hemangioma is present. Enamel hypoplasia increases the risk of caries, and clinicians should refer children with PHACE syndrome to a pediatric dentist by 1 year of age. © 2014 Wiley Periodicals, Inc.

  6. Theobromine Effects on Enamel Surface Microhardness: In Vitro

    Directory of Open Access Journals (Sweden)

    Grace Syafira

    2013-07-01

    Full Text Available Dental caries is still a dental health problem in Indonesia. Fluoride, one of the dental caries prevention material, but its safety and the danger of fluorosis is still debated. Theobromine is an alkaloid compound contained in cocoa beans. Theobromine is believed to increase enamel microhardness with mineral changes in the enamel superficial layer. Objectives: To determine the influence of theobromine on the enamel surface microhardness. Methods: This study used 40 premolar tooth crown pieces that were embedded in epoxy resin. Furthermore specimens were randomly divided into 4 groups, which were control (distilled water, theobromine 100 mg/L (T100, theobromine 500 mg/L (T500 and theobromine 1000 mg/L (T1000. Specimens were immersed for 15 minutes and microhardness test was performed using Knoop microhardness tester. Results: Increasing enamel microhardness was observed after treatment with four different theobromine concentrations. The highest icreased of enamel microhardness was shown in T1000 group and difference compared to other groups were statistically significant (p<0.05. Conclusion: theobromine is a potential dental caries prevention material due to its effect in improving the microhardness of tooth enamel.

  7. Comparison of chemical composition of materials used in dental restorations 08 years after the irradiation

    International Nuclear Information System (INIS)

    Maio, Mireia Florencio; Santos, Adimir dos; Fernandes, Marco A.R.

    2009-01-01

    The purpose of this work consisted of quantitative studies of the effects caused by ionizing radiation on the materials commonly used in dental restorations (amalgam, composite resin and Compomer), to mitigate the deleterious effects of radiotherapy when patients with tumors in head and neck, observed when the teeth are restored within the field of radiation. Samples were submitted to the beam of radiation from a source of cobalt-therapy, and analyzed by a X-ray fluorescence technique, by comparing the chemical composition of samples before and after irradiation. Gamma spectrometry was performed with detector of NaI and HPGe in the same samples. Then, the samples were kept in an appropriate place and after 08 years is repeated the same analysis. With these tests, it was possible to verify small changes in the composition of bodies of evidence due to the interaction 08 years after exposure to gamma radiation beams, simulating a patient who develops deleterious effects of radiation after the end radiotherapy treatment. (author)

  8. Comparison of chemical composition of materials used in dental restorations 08 years after the irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Maio, Mireia Florencio; Santos, Adimir dos, E-mail: mfmaio@ipen.b, E-mail: asantos@ipen.b [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP) Sao Paulo, SP (Brazil); Fernandes, Marco A.R., E-mail: marcosrf@salesiano-ata.b [UNESP, Botucatu, SP (Brazil). Faculdade de Medicina

    2009-07-01

    The purpose of this work consisted of quantitative studies of the effects caused by ionizing radiation on the materials commonly used in dental restorations (amalgam, composite resin and Compomer), to mitigate the deleterious effects of radiotherapy when patients with tumors in head and neck, observed when the teeth are restored within the field of radiation. Samples were submitted to the beam of radiation from a source of cobalt-therapy, and analyzed by a X-ray fluorescence technique, by comparing the chemical composition of samples before and after irradiation. Gamma spectrometry was performed with detector of NaI and HPGe in the same samples. Then, the samples were kept in an appropriate place and after 08 years is repeated the same analysis. With these tests, it was possible to verify small changes in the composition of bodies of evidence due to the interaction 08 years after exposure to gamma radiation beams, simulating a patient who develops deleterious effects of radiation after the end radiotherapy treatment. (author)

  9. Revisiting the dose-effect correlations in irradiated head and neck cancer using automatic segmentation tools of the dental structures, mandible and maxilla

    International Nuclear Information System (INIS)

    Thariat, J.; Ramus, L.; Odin, G.; Vincent, S.; Orlanducci, M.H.; Dassonville, O.; Darcourt, V.; Lacout, A.; Marcy, P.Y.; Cagnol, G.; Malandain, G.

    2011-01-01

    Purpose. - Manual delineation of dental structures is too time-consuming to be feasible in routine practice. Information on dose risk levels is crucial for dentists following irradiation of the head and neck to avoid post-extraction osteoradionecrosis based on empirical dose-effects data established on bidimensional radiation therapy plans. Material and methods. - We present an automatic atlas-based segmentation framework of the dental structures, called Dentalmaps, constructed from a patient image-segmentation database. Results. - This framework is accurate (within 2 Gy accuracy) and relevant for the routine use. It has the potential to guide dental care in the context of new irradiation techniques. Conclusion. - This tool provides a user-friendly interface for dentists and radiation oncologists in the context of irradiated head and neck cancer patients. It will likely improve the knowledge of dose-effect correlations for dental complications and osteoradionecrosis. (authors)

  10. Bleaching and enamel surface interactions resulting from the use of highly-concentrated bleaching gels.

    Science.gov (United States)

    Grazioli, Guillermo; Valente, Lisia Lorea; Isolan, Cristina Pereira; Pinheiro, Helena Alves; Duarte, Camila Gonçalves; Münchow, Eliseu Aldrighi

    2018-03-01

    Tooth bleaching is considered a non-invasive treatment, although the use of highly-concentrated products may provoke increased surface roughness and enamel demineralization, as well as postoperative sensitivity. Thus, the aim of this study was to investigate whether hydrogen peroxide (H 2 O 2 ) concentration would affect tooth bleaching effectiveness and the enamel surface properties. Enamel/dentin bovine specimens (6 × 4 mm) were immersed in coffee solution for 7 days and evaluated with a spectrophotometer (Easyshade; baseline), using the CIEL * a * b * color parameters. Hardness was measured using a hardness tester. The specimens were randomly assigned into four groups: one negative control, in which the specimens were not bleached, but they were irradiated with a laser-light source (Whitening Lase II, DMC Equipments); and three groups using distinct H 2 O 2 concentration, namely LP15% (15% Lase Peroxide Lite), LP25% (25% Lase Peroxide Sensy), and LP35% (35% Lase Peroxide Sensy), all products from DMC. The bleached specimens were also irradiated with the laser-light source. After bleaching, all specimens were evaluated using scanning electron microscopy (SEM). pH kinetics and rate was monitored during bleaching. The data were analyzed using ANOVA and Tukey's test (p bleaching gels produced similar color change (p > 0.05). Concerning hardness, only the LP25% and LP35% significantly reduced hardness after bleaching; also, there was a progressive tendency for a greater percentage reduction in hardness with increased H 2 O 2 concentration of the gel (R 2  = 0.9973, p bleaching effectiveness, and may increase the possibility for alteration of enamel hardness, surface morphology, and acidity of the medium. When using H 2 O 2 -based bleaching agents, dental practitioners should choose for less concentrated gels, e.g., around the 15% level. Copyright © 2017 Elsevier Ltd. All rights reserved.

  11. Evaluation of thermal damage in dental implants after irradiation with 980nm diode laser. An in vitro study

    Directory of Open Access Journals (Sweden)

    Carlo Cafiero

    2016-12-01

    Full Text Available Purpose: The aim of this study was to analyze the thermal damage in dental implants after irradiations with a 980nm diode laser, normally used for the decontamination. Material and Methods: Five Titanium Plasma Sprayed dental implants were irradiated with a 980nm diode laser at different parameters. Temperature increase on implant surface was evaluated by a Mid-Wavelength Infrared thermal-camera (Merlin®, FLIR, USA. Temperature increase (ΔT was compared to environmental temperature (27°C and recorded in three points: “A” (laser spot, “B” (3mm apically to the laser spot and “C” (2mm horizontally to the laser spot. Finally, a morphological evaluation at optical stereomicroscopy was performed. Results: When 0.6W power was applied, a moderate increase of temperature in point A (5.5°C-15.0°C, a slight increase in point B (0.1°C-6.2°C and point C (0.1°C-5.7°C, were registered after 30” of irradiation. In the samples treated at 6W, in “point A” an impressive ΔT increase was immediately recorded (over 70°C. In “point B” was recorded a slight ΔT after 2 sec. irradiation (range 2.3°C-6.0°C, a moderate ΔT after 4 sec. irradiation (16.4°C and a consistent ΔT after 8-10 sec. irradiation (range 36.6°C-46.2°C. In “point C” ΔT values were very similar to those collected in “point B”. Optical stereomicroscopy examination at a magnification of 32x did not show any surface alteration or damage after whichever laser irradiation independently from irradiation time and power output . Conclusions: 980nm diode laser, used at controlled parameters, can be used in the decontamination of dental implants, without causing any thermal damage or increase.

  12. Dental Pulp Defence and Repair Mechanisms in Dental Caries

    OpenAIRE

    Farges, Jean-Christophe; Alliot-Licht, Brigitte; Renard, Emmanuelle; Ducret, Maxime; Gaudin, Alexis; Smith, Anthony J.; Cooper, Paul R.

    2015-01-01

    Dental caries is a chronic infectious disease resulting from the penetration of oral bacteria into the enamel and dentin. Microorganisms subsequently trigger inflammatory responses in the dental pulp. These events can lead to pulp healing if the infection is not too severe following the removal of diseased enamel and dentin tissues and clinical restoration of the tooth. However, chronic inflammation often persists in the pulp despite treatment, inducing permanent loss of normal tissue and red...

  13. Probing atomic scale transformation of fossil dental enamel using Fourier transform infrared and nuclear magnetic resonance spectroscopy: a case study from the Tugen Hills (Rift Gregory, Kenya).

    Science.gov (United States)

    Yi, Haohao; Balan, Etienne; Gervais, Christel; Ségalen, Loïc; Roche, Damien; Person, Alain; Fayon, Franck; Morin, Guillaume; Babonneau, Florence

    2014-09-01

    A series of fossil tooth enamel samples was investigated by Fourier transform infrared (FTIR) spectroscopy, (13)C and (19)F magic-angle spinning nuclear magnetic resonance (MAS NMR) and scanning electron microscopy (SEM). Tooth remains were collected in Mio-Pliocene deposits of the Tugen Hills in Kenya. Significant transformations were observed in fossil enamel as a function of increasing fluorine content (up to 2.8wt.%). FTIR spectroscopy revealed a shift of the ν1 PO4 stretching band to higher frequency. The ν2 CO3 vibrational band showed a decrease in the intensity of the primary B-type carbonate signal, which was replaced by a specific band at 864cm(-1). This last band was ascribed to a specific carbonate environment in which the carbonate group is closely associated to a fluoride ion. The occurrence of this carbonate defect was consistently attested by the observation of two different fluoride signals in the (19)F NMR spectra. One main signal, at ∼-100ppm, is related to structural F ions in the apatite channel and the other, at -88ppm, corresponds to the composite defect. These spectroscopic observations can be understood as resulting from the mixture of two phases: biogenic hydroxylapatite (bioapatite) and secondary fluorapatite. SEM observations of the most altered sample confirmed the extensive replacement of the bioapatite by fluorapatite, resulting from the dissolution of the primary bioapatite followed by the precipitation of carbonate-fluorapatite. The ν2 CO3 IR bands can be efficiently used to monitor the extent of this type of bioapatite transformation during fossilization. Copyright © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  14. EPR dosimetry with tooth enamel: A review

    International Nuclear Information System (INIS)

    Fattibene, Paola; Callens, Freddy

    2010-01-01

    When tooth enamel is exposed to ionizing radiation, radicals are formed, which can be detected using electron paramagnetic resonance (EPR) techniques. EPR dosimetry using tooth enamel is based on the (presumed) correlation between the intensity or amplitude of some of the radiation-induced signals with the dose absorbed in the enamel. In the present paper a critical review is given of this widely applied dosimetric method. The first part of the paper is fairly fundamental and deals with the main properties of tooth enamel and some of its model systems (e.g., synthetic apatites). Considerable attention is also paid to the numerous radiation-induced and native EPR signals and the radicals responsible for them. The relevant methods for EPR detection, identification and spectrum analyzing are reviewed from a general point of view. Finally, the needs for solid-state modelling and studies of the linearity of the dose response are investigated. The second part is devoted to the practical implementation of EPR dosimetry using enamel. It concerns specific problems of preparation of samples, their irradiation and spectrum acquisition. It also describes how the dosimetric signal intensity and dose can be retrieved from the EPR spectra. Special attention is paid to the energy dependence of the EPR response and to sources of uncertainties. Results of and problems encountered in international intercomparisons and epidemiological studies are also dealt with. In the final section the future of EPR dosimetry with tooth enamel is analyzed.

  15. Modelling of micromachining of human tooth enamel by erbium laser radiation

    Energy Technology Data Exchange (ETDEWEB)

    Belikov, A V; Skrypnik, A V; Shatilova, K V [St. Petersburg National Research University of Information Technologies, Mechanics and Optics, St. Petersburg (Russian Federation)

    2014-08-31

    We consider a 3D cellular model of human tooth enamel and a photomechanical cellular model of enamel ablation by erbium laser radiation, taking into account the structural peculiarities of enamel, energy distribution in the laser beam cross section and attenuation of laser energy in biological tissue. The surface area of the texture in enamel is calculated after its micromachining by erbium laser radiation. The influence of the surface area on the bond strength of enamel with dental filling materials is discussed. A good correlation between the computer simulation of the total work of adhesion and experimentally measured bond strength between the dental filling material and the tooth enamel after its micromachining by means of YAG : Er laser radiation is attained. (laser biophotonics)

  16. Modelling of micromachining of human tooth enamel by erbium laser radiation

    International Nuclear Information System (INIS)

    Belikov, A V; Skrypnik, A V; Shatilova, K V

    2014-01-01

    We consider a 3D cellular model of human tooth enamel and a photomechanical cellular model of enamel ablation by erbium laser radiation, taking into account the structural peculiarities of enamel, energy distribution in the laser beam cross section and attenuation of laser energy in biological tissue. The surface area of the texture in enamel is calculated after its micromachining by erbium laser radiation. The influence of the surface area on the bond strength of enamel with dental filling materials is discussed. A good correlation between the computer simulation of the total work of adhesion and experimentally measured bond strength between the dental filling material and the tooth enamel after its micromachining by means of YAG : Er laser radiation is attained. (laser biophotonics)

  17. Dental problems and irradiation of the O.R.L. sphere: a new attitude. Preliminary results on 488 cases

    International Nuclear Information System (INIS)

    Paget, C.R.

    1975-01-01

    High-energy radiotherapy has greatly improved the percentage of cures in cancers of the ORL sphere, but it is debatable whether the same progress has been made in the prevention of its sequels and complications. Post-radiotherapeutic dental decay, the result of asialia, is almost inevitable when the saliva glands are irradiated at doses above 3000 rads. These post-radiotherapeutic caries with their train of local infections, pains, and in some very serious but fortunately rare cases evolution towards osteonecrosis of the lower jaw, more often affected than the upper, can cancel out all the benefits derived from a cervico-facial radiotherapy from which a local sterilisation has been obtained. Post-radiotherapeutic tooth decay and its evolution towards osteoradionecrosis are described. A combined effort has been made by a team of ORL specialists, radiotherapists and dentists in an attempt to work out a dental policy aimed at reducing these complications to a minimum [fr

  18. Trace Elements in Human Tooth Enamel

    Energy Technology Data Exchange (ETDEWEB)

    Nixon, G. S. [Turner Dental School, University Of Manchester, Manchester (United Kingdom); Smith, H.; Livingston, H. D. [Department of Forensic Medicine, University Of Glasgow, Glasgow (United Kingdom)

    1967-10-15

    The trace elements are considered to play a role in the resistance of teeth to dental caries. The exact mechanism by which they act has not yet been fully established. Estimations of trace elements have been undertaken in sound human teeth. By means of activation analysis it has been possible to determine trace element concentrations in different layers of enamel in the same tooth. The concentrations of the following elements have been determined: arsenic, antimony, copper, zinc, manganese, mercury, molybdenum and vanadium. The distribution of trace elements in enamel varies from those with a narrow range, such as manganese, to those with a broad range, such as antimony. The elements present in the broad range are considered to be non-essential and their presence is thought to result from a chance incorporation into the enamel. Those in the narrow range appear to be essential trace elements and are present in amounts which do not vary unduly from other body tissues. Only manganese and zinc were found in higher concentrations in the surface layer of enamel compared with the inner layers. The importance of the concentration of trace elements on this surface layer of enamel is emphasized as this layer is the site of the first attack by the carious process. (author)

  19. Deformation behavior of human enamel and dentin-enamel junction under compression.

    Science.gov (United States)

    Zaytsev, Dmitry; Panfilov, Peter

    2014-01-01

    Deformation behavior under uniaxial compression of human enamel and dentin-enamel junction (DEJ) is considered in comparison with human dentin. This deformation scheme allows estimating the total response from all levels of the hierarchical composite material in contrast with the indentation, which are limited by the mesoscopic and microscopic scales. It was shown for the first time that dental enamel is the strength (up to 1850MPa) hard tissue, which is able to consider some elastic (up to 8%) and plastic (up to 5%) deformation under compression. In so doing, it is almost undeformable substance under the creep condition. Mechanical properties of human enamel depend on the geometry of sample. Human dentin exhibits the similar deformation behavior under compression, but the values of its elasticity (up to 40%) and plasticity (up to 18%) are much more, while its strength (up to 800MPa) is less in two times. Despite the difference in mechanical properties, human enamel is able to suppress the cracking alike dentin. Deformation behavior under the compression of the samples contained DEJ as the same to dentin. This feature allows a tooth to be elastic-plastic (as dentin) and wear resistible (as enamel), simultaneously. © 2013 Elsevier B.V. All rights reserved.

  20. Effect of tumor therapeutic irradiation on the mechanical properties of teeth tissue

    International Nuclear Information System (INIS)

    Fraenzel, W.; Gerlach, R.; Hein, H.J.; Schaller, H.G.

    2006-01-01

    Tumor irradiation of the head-neck area is accompanied by the development of a so-called radiation caries in the treated patients. In spite of conservative therapeutic measures, the process results in tooth destruction. The present study investigated the effects of irradiation on the demineralization and remineralization of the dental tissue. For this purpose, retained third molars were prepared and assigned either to a test group, which was exposed to fractional irradiation up to 60 Gy, or to a non-irradiated control group. Irradiated and non-irradiated teeth were then demineralized using acidic hydroxyl-cellulose gel; afterwards the teeth were remineralized using either Bifluorid12 registered or elmex gelee registered . The nanoindentation technique was used to measure the mechanical properties, hardness and elasticity, of the teeth in each of the conditions. The values were compared to the non-irradiated control group. Irradiation decreased dramatically the mechanical parameters of enamel and dentine. In non-irradiated teeth, demineralization had nearly the same effects of irradiation on the mechanical properties. In irradiated teeth, the effects of demineralization were negligible in comparison to non-irradiated teeth. Remineralization with Bifluorid12 registered or elmex gelee registered led to a partial improvement of the mechanical properties of the teeth. The enamel was more positively affected, by remineralization than the dentine. (orig.)

  1. Effect of tumor therapeutic irradiation on the mechanical properties of teeth tissue

    Energy Technology Data Exchange (ETDEWEB)

    Fraenzel, W. [Dept. of Physics, Martin Luther Univ. Halle (Germany); Gerlach, R. [Univ. Clinic and Policlinic for Radiation Therapy, Martin Luther Univ. Halle (Germany); Hein, H.J. [Univ. Clinic and Policlinic for Orthopaedics and Physical Medicine, Martin Luther Univ. Halle (Germany); Schaller, H.G. [Dept. of Operative Dentistry and Periodontology, Martin Luther Univ. Halle (Germany)

    2006-07-01

    Tumor irradiation of the head-neck area is accompanied by the development of a so-called radiation caries in the treated patients. In spite of conservative therapeutic measures, the process results in tooth destruction. The present study investigated the effects of irradiation on the demineralization and remineralization of the dental tissue. For this purpose, retained third molars were prepared and assigned either to a test group, which was exposed to fractional irradiation up to 60 Gy, or to a non-irradiated control group. Irradiated and non-irradiated teeth were then demineralized using acidic hydroxyl-cellulose gel; afterwards the teeth were remineralized using either Bifluorid12 {sup registered} or elmex gelee {sup registered}. The nanoindentation technique was used to measure the mechanical properties, hardness and elasticity, of the teeth in each of the conditions. The values were compared to the non-irradiated control group. Irradiation decreased dramatically the mechanical parameters of enamel and dentine. In non-irradiated teeth, demineralization had nearly the same effects of irradiation on the mechanical properties. In irradiated teeth, the effects of demineralization were negligible in comparison to non-irradiated teeth. Remineralization with Bifluorid12 {sup registered} or elmex gelee {sup registered} led to a partial improvement of the mechanical properties of the teeth. The enamel was more positively affected, by remineralization than the dentine. (orig.)

  2. Effect of a New Surface Treatment Solution on the Bond Strength of Composite to Enamel

    Science.gov (United States)

    2016-06-01

    Bond Strength of Composite to Enamel " is appropriately acknowledged and, beyond brief excerpts, is with the permission of the copyright owner...Solution on the Bond Strength of Composite to Enamel ABSTRACT Clean & Boost (Apex Dental Materials) is a novel surface treatment solution...designed to be used in place of phosphoric acid to increase the bond strength of self-etch adhesives to enamel and more effectively remove contaminants

  3. Heat generation caused by ablation of dental hard tissues with an ultrashort pulse laser (USPL) system.

    Science.gov (United States)

    Braun, Andreas; Krillke, Raphael Franz; Frentzen, Matthias; Bourauel, Christoph; Stark, Helmut; Schelle, Florian

    2015-02-01

    Heat generation during the removal of dental hard tissues may lead to a temperature increase and cause painful sensations or damage dental tissues. The aim of this study was to assess heat generation in dental hard tissues following laser ablation using an ultrashort pulse laser (USPL) system. A total of 85 specimens of dental hard tissues were used, comprising 45 specimens of human dentine evaluating a thickness of 1, 2, and 3 mm (15 samples each) and 40 specimens of human enamel with a thickness of 1 and 2 mm (20 samples each). Ablation was performed with an Nd:YVO4 laser at 1,064 nm, a pulse duration of 9 ps, and a repetition rate of 500 kHz with an average output power of 6 W. Specimens were irradiated for 0.8 s. Employing a scanner system, rectangular cavities of 1-mm edge length were generated. A temperature sensor was placed at the back of the specimens, recording the temperature during the ablation process. All measurements were made employing a heat-conductive paste without any additional cooling or spray. Heat generation during laser ablation depended on the dental hard tissue (enamel or dentine) and the thickness of the respective tissue (p dental hard tissues, heat generation has to be considered. Especially during laser ablation next to pulpal tissues, painful sensations and potential thermal injury of pulp tissue might occur.

  4. Thermal induced EPR signals in tooth enamel

    International Nuclear Information System (INIS)

    Fattibene, P.; Aragno, D.; Onori, S.; Pressello, M.C.

    2000-01-01

    Electron paramagnetic resonance (EPR) spectroscopy was used to detect the effects of temperature on powdered human tooth enamel, not irradiated in the laboratory. Samples were heated at temperature between 350 and 450, at 600 and at 1000 deg. C, for different heating times, between 6 min and 39 h. Changes in the EPR spectra were detected, with the formation of new signals. Possible correlation between the changes in EPR spectra and modifications in the enamel and in the mineral phase of bone detected with other techniques is discussed. The implications for dosimetric applications of signals induced by overheating due to mechanical friction during sample preparation are underlined

  5. Endocytosis and Enamel Formation

    Directory of Open Access Journals (Sweden)

    Cong-Dat Pham

    2017-07-01

    Full Text Available Enamel formation requires consecutive stages of development to achieve its characteristic extreme mineral hardness. Mineralization depends on the initial presence then removal of degraded enamel proteins from the matrix via endocytosis. The ameloblast membrane resides at the interface between matrix and cell. Enamel formation is controlled by ameloblasts that produce enamel in stages to build the enamel layer (secretory stage and to reach final mineralization (maturation stage. Each stage has specific functional requirements for the ameloblasts. Ameloblasts adopt different cell morphologies during each stage. Protein trafficking including the secretion and endocytosis of enamel proteins is a fundamental task in ameloblasts. The sites of internalization of enamel proteins on the ameloblast membrane are specific for every stage. In this review, an overview of endocytosis and trafficking of vesicles in ameloblasts is presented. The pathways for internalization and routing of vesicles are described. Endocytosis is proposed as a mechanism to remove debris of degraded enamel protein and to obtain feedback from the matrix on the status of the maturing enamel.

  6. Residual energy deposition in dental enamel during IR laser ablation at 2.79, 2.94, 9.6, and 10.6 μm

    Science.gov (United States)

    Ragadio, Jerome N.; Lee, Christian K.; Fried, Daniel

    2000-03-01

    The objective of this study was to measure the residual heat deposition during laser ablation at those IR laser wavelengths best suited for the removal of dental caries. The principal factor limiting the rate of laser ablation of dental hard tissue is the risk of excessive heat accumulation in the tooth, which has the potential for causing damage to the pulp. Optimal laser ablation systems minimize the residual energy deposition in the tooth by transferring deposited laser energy to kinetic and internal energy of ejected tissue components. The residual heat deposition in the tooth was measured at laser wavelengths of 2.79, 2.94, 9.6 and 10.6 micrometer and pulse widths of 150 ns - 150 microsecond(s) . The residual energy was at a minimum for fluences well above the ablation threshold where it saturates at values from 25 - 70% depending on pulse duration and wavelength for the systems investigated. The lowest values of the residual energy were measured for short (less than 20 microseconds) CO2 laser pulses at 9.6 micrometer and for Q-switched erbium laser pulses. This work was supported by NIH/NIDCR R29DE12091 and the Center for Laser Applications in Medicine, DOE DEFG0398ER62576.

  7. In vitro study of hydroxy apatite and enamel powder fused in human enamel by Nd:YAG laser

    International Nuclear Information System (INIS)

    Ferrreira, Marcus Vinicius Lucas

    2000-01-01

    The aim of this study was to evaluate the effects of pulsed Nd:YAG (1064 nm) laser irradiation on hydroxyapatite and enamel powder fusion. This laser beam is not well absorbed by this two compounds for this reason they were mixed with vegetal coal to increase the absorption of the laser beam. Fifteen enamel flat surfaces and six occlusal enamel surfaces were prepared with three different substances: hydroxyapatite mixed with vegetal coal (3:1 in weigh); enamel powder mixed with vegetal coal (3:1 in weigh); vegetal coal. The occlusal surfaces were utilized to determine if the compounds could seal pits and fissures. Flat surfaces were utilized to determine fusion of hydroxyapatite and enamel powder. All samples were irradiated with Nd:YAG laser with the parameters: 80 mJ, 15 Hz, 1,2 W, 100 μs pulse-width, 131,1 J/cm 2 . Laser beam was delivered to the samples with a 300 μm diameter fiber optic. Morphology of the irradiated surfaces were examined by scanning electron microscopy (SEM). The compounds with hydroxyapatite and enamel powder were fused to enamel surfaces. Only partial pits and fissures sealing could be observed. (author)

  8. Precise femtosecond laser ablation of dental hard tissue: preliminary investigation on adequate laser parameters

    International Nuclear Information System (INIS)

    Hikov, Todor; Pecheva, Emilia; Petrov, Todor; Montgomery, Paul; Antoni, Frederic; Leong-Hoi, Audrey

    2017-01-01

    This work aims at evaluating the possibility of introducing state-of-the-art commercial femtosecond laser system in restorative dentistry by maintaining well-known benefits of lasers for caries removal, but also in overcoming disadvantages such as thermal damage of irradiated substrate. Femtosecond ablation of dental hard tissue is investigated by changing the irradiation parameters (pulsed laser energy, scanning speed and pulse repetition rate), assessed for enamel and dentin. The femtosecond laser system used in this work may be suitable for cavity preparation in dentin and enamel, due to the expected effective ablation and low temperature increase when using ultra short laser pulses. If adequate laser parameters are selected, this system seems to be promising for promoting a laser-assisted, minimally invasive approach in restorative dentistry. (paper)

  9. A study on the effect of 60Co gamma ray irradiation on the abrasion of dental polymethylmethacrylate, (3)

    International Nuclear Information System (INIS)

    Kimura, Hiroshi

    1981-01-01

    This report intends to clarify the relationship between the total exposure dose and scratch resistance to the specimens SF, SH, MF and MH, giving coating treatments to P.M.M.A. (dental polymethylmethacrylate) and exposing to the irradiation of 60 Co gamma ray at each dose rate. And based on the results, it is intended to develop coated P.M.M.A. with excellent scratch resistance give by irradiation of radioactive ray. From this study, the following results have been obtained. Irradiation of 60 Co gamma ray would give the best results at the exposure at 1 x 10 6 R. The SF and SH specimens in wet condition exposed to 60 Co gamma ray irradiation at 1 x 10 6 R showed a quantity of abrasion of only 17% that of untreated P.M.M.A. and the barrel test revealed outstanding abrasion and scratch resistance. Abrasion and scratch resistance of coated specimens are better utilized in wet conditions performing three times better than those in dry conditions. (author)

  10. Assessment of the Survival of Dental Implants in Irradiated Jaws Following Treatment of Oral Cancer: A Retrospective Study

    Science.gov (United States)

    Rana, Meenakshi Chauhan; Solanki, Swati; Pujari, Sudarshan C; Shaw, Eisha; Sharma, Swati; Anand, Abhishek; Singh, Harkanwal Preet

    2016-01-01

    Background: In patients undergoing head and neck surgery for various pathologic conditions, implants are one of the best restorative options and are increasing widely used. Therefore, we evaluated the success of dental implants in the irradiated jaws of patients following treatment of oral cancer oral cancer treated patients. Materials and Methods: Data of oral cancer treated patients was collected retrospectively from 2002 to 2008. We took 46 oral cancer treated patients in which implants were placed in irradiated jaws for rehabilitation. Results: It was found that out of 162 dental implants placed, 52 failed. Furthermore, there was no variation in the implant survival rate in between both the jaws. Radiation dose of <50 Gy units also showed significantly increased amount of implant survival rate. Conclusions: Implant survival is multifactorial and depends upon a number of factors like level of radiation exposure in that area, time gap between last radiation doses etc., Further research is required in this field to improve the esthetics and quality of life of cancer treated patients. PMID:27843270

  11. Assessment of the survival of dental implants in irradiated jaws following treatment of oral cancer: A retrospective study

    Directory of Open Access Journals (Sweden)

    Meenakshi Chauhan Rana

    2016-01-01

    Full Text Available Background: In patients undergoing head and neck surgery for various pathologic conditions, implants are one of the best restorative options and are increasing widely used. Therefore, we evaluated the success of dental implants in the irradiated jaws of patients following treatment of oral cancer oral cancer treated patients. Materials and Methods: Data of oral cancer treated patients was collected retrospectively from 2002 to 2008. We took 46 oral cancer treated patients in which implants were placed in irradiated jaws for rehabilitation. Results: It was found that out of 162 dental implants placed, 52 failed. Furthermore, there was no variation in the implant survival rate in between both the jaws. Radiation dose of <50 Gy units also showed significantly increased amount of implant survival rate. Conclusions: Implant survival is multifactorial and depends upon a number of factors like level of radiation exposure in that area, time gap between last radiation doses etc., Further research is required in this field to improve the esthetics and quality of life of cancer treated patients.

  12. Assessment of Dental Fluorosis in Mmp20+/− Mice

    OpenAIRE

    Sharma, R.; Tye, C.E.; Arun, A.; MacDonald, D.; Chatterjee, A.; Abrazinski, T.; Everett, E.T.; Whitford, G.M.; Bartlett, J.D.

    2011-01-01

    The molecular mechanisms that underlie dental fluorosis are poorly understood. The retention of enamel proteins hallmarking fluorotic enamel may result from impaired hydrolysis and/or removal of enamel proteins. Previous studies have suggested that partial inhibition of Mmp20 expression is involved in the etiology of dental fluorosis. Here we ask if mice expressing only one functional Mmp20 allele are more susceptible to fluorosis. We demonstrate that Mmp20+/− mice express approximately half ...

  13. Spectroscopic and thermal characterization of bovine enamel and dentine using the photoacoustic effect

    International Nuclear Information System (INIS)

    Stolf, Sandro Fernando

    2003-01-01

    The optical and thermal properties of dental tissues determine the nature and extent of the tissue response through the processes of absorption, transmission, reflection and scattering of the laser light and the heat produced by the absorption of that light. The spectroscopic characterization of bovine dentine and enamel, and the determination of the thermal diffusivity were the aim of this study. The photoacoustic spectra from these tissues were obtained in the Near-Infrared range 900 - 2500 nm, which is the clinical range for odontological application of most lasers. Photoacoustic spectra were taken from block, slices and powder of enamel and dentine. Also photoacoustic spectra were registered before and after 2, 5 and 10 h of topical fluoride (2.26%) application. Using the same technique spectra were taken from dentine and enamel after irradiation with Nd:YAG, Er:YAG, Ho:YLF and CO 2 . It is evident from the results that the presence of O-H in the composition of hydroxyapatite and the water present in the teeth tissue make the obtention of spectrum from components other than O-H bond a very difficult task. In this way, only bands assigned to overtones and combinations of O-H stretch were observed. The thermal diffusivity of the bovine dentine was also measured using the photoacoustic technique. The thermal diffusivity is the physical quantity which measures the rate of heat diffusion throughout the sample. For higher values of the thermal diffusivity the heat diffusion and temperature rise will be faster. As there is many studies devoted to the processes of heat transfer throughout dental tissues using bovine teeth, it is important the determination of its thermal diffusivity. The measured value was found to be a = 2.0 (±0.1).1O -3 cm 2 /s for the both direction, perpendicular and parallel to the dentinal tubules. These a lues indicate that there is no difference between the thermal diffusivities for the both directions. (author)

  14. Refining enamel thickness measurements from B-mode ultrasound images.

    Science.gov (United States)

    Hua, Jeremy; Chen, Ssu-Kuang; Kim, Yongmin

    2009-01-01

    Dental erosion has been growing increasingly prevalent with the rise in consumption of heavy starches, sugars, coffee, and acidic beverages. In addition, various disorders, such as Gastroenterological Reflux Disease (GERD), have symptoms of rapid rates of tooth erosion. The measurement of enamel thickness would be important for dentists to assess the progression of enamel loss from all forms of erosion, attrition, and abrasion. Characterizing enamel loss is currently done with various subjective indexes that can be interpreted in different ways by different dentists. Ultrasound has been utilized since the 1960s to determine internal tooth structure, but with mixed results. Via image processing and enhancement, we were able to refine B-mode dental ultrasound images for more accurate enamel thickness measurements. The mean difference between the measured thickness of the occlusal enamel from ultrasound images and corresponding gold standard CT images improved from 0.55 mm to 0.32 mm with image processing (p = 0.033). The difference also improved from 0.62 to 0.53 mm at the buccal/lingual enamel surfaces, but not significantly (p = 0.38).

  15. Enamel lesions in development, classification in Costa Rican families

    International Nuclear Information System (INIS)

    Murillo Knudsen, Gina; Berrocal Salazar, Cristina

    2013-01-01

    Enamel lesions in development were identified and classified in patients of Llano Grande de Cartago, examined at the Facultad de Odontologia of the Universidad de Costa Rica. A guide is provided over the topic. 15 children and 2 Costa Rican adults were selected. Clinical examinations, radiographs and clinical photographs were used as data collection method. Dental defects of the enamel were classified according to the possible genetic causes and without genetic causes. Imperfect Amelogenesis (IA) was diagnosed in 10 of patients. Hypoplastic IA was determined in 3 siblings with autosomal recessive inheritance, for 16% of the total sample. Hypomineralized IA was identified in an adult and two of his sons, with autosomal dominant inheritance. The remaining 4 cases of IA have been sporadic. Lesions of dental fluorosis were determined in the Horowitz index in 4 individuals, from 2 unrelated families. Other defects unspecified of the enamel or hypoplasias were found in 3 individuals. Enamel lesions in development should be classified with precision, for the purpose to inform to patients affected about their condition, origin, prognosis and appropriate treatment. The basis are established to implement reliability in the construction of family genealogy, identification and classification of enamel lesions, as well as the probabilities of future generations to express the lesions in the enamel of temporary or permanent dentition [es

  16. On the critical parameters that regulate the deformation behaviour of tooth enamel.

    Science.gov (United States)

    Xie, Zonghan; Swain, Michael; Munroe, Paul; Hoffman, Mark

    2008-06-01

    Tooth enamel is the hardest tissue in the human body with a complex hierarchical structure. Enamel hypomineralisation--a developmental defect--has been reported to cause a marked reduction in the mechanical properties of enamel and loss of dental function. We discover a distinctive difference in the inelastic deformation mechanism between sound and hypomineralised enamels that is apparently controlled by microstructural variation. For sound enamel, when subjected to mechanical forces the controlling deformation mechanism was distributed shearing within nanometre thick protein layer between its constituent mineral crystals; whereas for hypomineralised enamel microcracking and subsequent crack growth were more evident in its less densely packed microstructure. We develop a mechanical model that not only identifies the critical parameters, i.e., the thickness and shear properties of enamels, that regulate the mechanical behaviour of enamel, but also explains the degradation of hypomineralised enamel as manifested by its lower resistance to deformation and propensity for catastrophic failure. With support of experimental data, we conclude that for sound enamel an optimal microstructure has been developed that endows enamel with remarkable structural integrity for durable mechanical function.

  17. Enamel alteration following tooth bleaching and remineralization.

    Science.gov (United States)

    Coceska, Emilija; Gjorgievska, Elizabeta; Coleman, Nichola J; Gabric, Dragana; Slipper, Ian J; Stevanovic, Marija; Nicholson, John W

    2016-06-01

    The purpose of this study was to compare the effects of professional tooth whitening agents containing highly concentrated hydrogen peroxide (with and without laser activation), on the enamel surface; and the potential of four different toothpastes to remineralize any alterations. The study was performed on 50 human molars, divided in two groups: treated with Opalescence(®) Boost and Mirawhite(®) Laser Bleaching. Furthermore, each group was divided into five subgroups, a control one and 4 subgroups remineralized with: Mirasensitive(®) hap+, Mirawhite(®) Gelleѐ, GC Tooth Mousse™ and Mirafluor(®) C. The samples were analysed by SEM/3D-SEM-micrographs, SEM/EDX-qualitative analysis and SEM/EDX-semiquantitative analysis. The microphotographs show that both types of bleaching cause alterations: emphasized perikymata, erosions, loss of interprizmatic substance; the laser treatment is more aggressive and loss of integrity of the enamel is determined by shearing off the enamel rods. In all samples undergoing remineralization deposits were observed, those of toothpastes based on calcium phosphate technologies seem to merge with each other and cover almost the entire surface of the enamel. Loss of integrity and minerals were detected only in the line-scans of the sample remineralized with GC Tooth Mousse™. The semiquantitative EDX analysis of individual elements in the surface layer of the enamel indicates that during tooth-bleaching with HP statistically significant loss of Na and Mg occurs, whereas the bleaching in combination with a laser leads to statistically significant loss of Ca and P. The results undoubtedly confirm that teeth whitening procedures lead to enamel alterations. In this context, it must be noted that laser bleaching is more aggressive for dental substances. However, these changes are reversible and can be repaired by application of remineralization toothpastes. © 2015 The Authors Journal of Microscopy © 2015 Royal Microscopical Society.

  18. Keratins as components of the enamel organic matrix

    Science.gov (United States)

    Duverger, Olivier; Beniash, Elia; Morasso, Maria I.

    2016-01-01

    Dental enamel is a hardest tissue in the human body, and although it starts as a tissue rich in proteins, by the time of eruption of the tooth in the oral cavity only a small fraction of the protein remains. While this organic matrix of enamel represents less than 1% by weight it plays essential roles in improving both toughness and resilience to chemical attacks. Despite the fact that the first studies of the enamel matrix began in the 19th century its exact composition and mechanisms of its function remain poorly understood. It was proposed that keratin or a keratin-like primitive epithelial component exists in mature enamel, however due to the extreme insolubility of its organic matrix the presence of keratins there was never clearly established. We have recently identified expression of a number of hair keratins in ameloblasts, the enamel secreting cells, and demonstrated their incorporation into mature enamel. Mutation in epithelial hair keratin KRT75 leads to a skin condition called pseudofollicularis barbae. Carriers of this mutation have an altered enamel structure and mechanical properties. Importantly, these individuals have a much higher prevalence of caries. To the best of our knowledge, this is the first study showing a direct link between a mutation in a protein-coding region of a gene and increased caries rates. In this paper we present an overview of the evidence of keratin-like material in enamel that has accumulated over the last 150 years. Furthermore, we propose potential mechanisms of action of KTR75 in enamel and highlight the clinical implications of the link between mutations in KRT75 and caries. Finally, we discuss the potential use of keratins for enamel repair. PMID:26709044

  19. Enamel formation and growth in non-mammalian cynodonts

    Science.gov (United States)

    Dirks, Wendy; Martinelli, Agustín G.

    2018-01-01

    The early evolution of mammals is associated with the linked evolutionary origin of diphyodont tooth replacement, rapid juvenile growth and determinate adult growth. However, specific relationships among these characters during non-mammalian cynodont evolution require further exploration. Here, polarized light microscopy revealed incremental lines, resembling daily laminations of extant mammals, in histological sections of enamel in eight non-mammalian cynodont species. In the more basal non-probainognathian group, enamel extends extremely rapidly from cusp to cervix. By contrast, the enamel of mammaliamorphs is gradually accreted, with slow rates of crown extension, more typical of the majority of non-hypsodont crown mammals. These results are consistent with the reduction in dental replacement rate across the non-mammalian cynodont lineage, with greater rates of crown extension required in most non-probainognathians, and slower crown extension rates permitted in mammaliamorphs, which have reduced patterns of dental replacement in comparison with many non-probainognathians. The evolution of mammal-like growth patterns, with faster juvenile growth and more abruptly terminating adult growth, is linked with this reduction in dental replacement rates and may provide an additional explanation for the observed pattern in enamel growth rates. It is possible that the reduction in enamel extension rates in mammaliamorphs reflects an underlying reduction in skeletal growth rates at the time of postcanine formation, due to a more abruptly terminating pattern of adult growth in these more mammal-like, crownward species. PMID:29892415

  20. Photoacoustic imaging of teeth for dentine imaging and enamel characterization

    Science.gov (United States)

    Periyasamy, Vijitha; Rangaraj, Mani; Pramanik, Manojit

    2018-02-01

    Early detection of dental caries, cracks and lesions is needed to prevent complicated root canal treatment and tooth extraction procedures. Resolution of clinically used x-ray imaging is low, hence optical imaging techniques such as optical coherence tomography, fluorescence imaging, and Raman imaging are widely experimented for imaging dental structures. Photoacoustic effect is used in photon induced photoacoustic streaming technique to debride the root canal. In this study, the extracted teeth were imaged using photoacoustic tomography system at 1064 nm. The degradation of enamel and dentine is an indicator of onset of dental caries. Photoacoustic microscopy (PAM) was used to study the tooth enamel. Images were acquired using acoustic resolution PAM system. This was done to identify microscopic cracks and dental lesion at different anatomical sites (crown and cementum). The PAM tooth profile is an indicator of calcium distribution which is essential for demineralization studies.

  1. Resistência ao cisalhamento de um selante associado a componentes de um sistema adesivo dental Shear bond strength of an enamel sealant using components of a dental adhesive system

    Directory of Open Access Journals (Sweden)

    Zilda Maria MUSSOLINO

    1998-10-01

    Full Text Available Cilindros de selante, padronizados, foram unidos ao esmalte das superfícies vestibulares de incisivos bovinos, após serem planificadas e condicionadas, com ácido fosfórico a 37%, durante 30 segundos. Foram utilizados 40 dentes, aleatoriamente divididos em 4 grupos, cujas coroas foram secionadas, de modo a obter-se duas porções, cervical e incisal. No Grupo I, após o condicionamento, aplicou-se o selante Fluroshield; no Grupo II, antes da aplicação do selante, uma camada do "primer" do Probond foi aplicada; no Grupo III, após o "primer", aplicou-se o adesivo do Probond; e no Grupo IV, somente o adesivo foi aplicado antes do selante. Os espécimes foram armazenados em água a 37°C, durante 36 horas, e então submetidos aos ensaios de cisalhamento. A análise estatística revelou significante diminuição na resistência ao cisalhamento, quando o "primer" foi aplicado previamente ao selante, enquanto a resistência ao cisalhamento do selante foi semelhante quando o adesivo do Probond foi aplicado, com ou sem o "primer". A resistência ao cisalhamento do selante ao esmalte é maior no terço incisal que no terço cervical da coroa.Standardized cylinders of sealants were bonded to the flattened labial enamel of bovine incisor teeth that had previously been subjected to 37% phosphoric acid gel for 30 seconds. A total of 40 teeth were tested, randomly divided in four groups of 10 teeth each. In Group I, the sealant Fluroshield was applied after etching; in Group II after etching, the "primer" of Probond was used before the sealant; in Group III after etching, the bond of Probond was used after the "primer"; and in Group IV only the bond was applied before the sealant. Specimens were stored in water at 37°C during 36 hours, before shear testing using a Universal Testing Machine. There was significant reduction in shear bond strength of the sealant when only the "primer" was used previously to the application of the sealant. There were no

  2. Enamel microabrasion: An overview of clinical and scientific considerations

    Science.gov (United States)

    Pini, Núbia Inocencya Pavesi; Sundfeld-Neto, Daniel; Aguiar, Flavio Henrique Baggio; Sundfeld, Renato Herman; Martins, Luis Roberto Marcondes; Lovadino, José Roberto; Lima, Débora Alves Nunes Leite

    2015-01-01

    Superficial stains and irregularities of the enamel are generally what prompt patients to seek dental intervention to improve their smile. These stains or defects may be due to hypoplasia, amelogenesis imperfecta, mineralized white spots, or fluorosis, for which enamel microabrasion is primarily indicated. Enamel microabrasion involves the use of acidic and abrasive agents, such as with 37% phosphoric acid and pumice or 6% hydrochloric acid and silica, applied to the altered enamel surface with mechanical pressure from a rubber cup coupled to a rotatory mandrel of a low-rotation micromotor. If necessary, this treatment can be safely combined with bleaching for better esthetic results. Recent studies show that microabrasion is a conservative treatment when the enamel wear is minimal and clinically imperceptible. The most important factor contributing to the success of enamel microabrasion is the depth of the defect, as deeper, opaque stains, such as those resulting from hypoplasia, cannot be resolved with microabrasion, and require a restorative approach. Surface enamel alterations that result from microabrasion, such as roughness and microhardness, are easily restored by saliva. Clinical studies support the efficacy and longevity of this safe and minimally invasive treatment. The present article presents the clinical and scientific aspects concerning the microabrasion technique, and discusses the indications for and effects of the treatment, including recent works describing microscopic and clinical evaluations. PMID:25610848

  3. Effects of simvastain and enamel matrix derivative on Portland cement with bismuth oxide-induced growth and odontoblastic differentiation in human dental pulp cells.

    Science.gov (United States)

    Lee, So-Youn; Min, Kyung-San; Choi, Gi-Woon; Park, Jae-Hong; Park, Sang-Hyuk; Lee, Sang-Im; Kim, Eun-Cheol

    2012-03-01

    We previously reported that bismuth oxide containing Portland cement (BPC) showed similar biocompatibility to Portland cement (PC) in periodontal ligament cells. However, the bioactivity of simvastatin and Emdogain (Biora AB, Malmö, Sweden) on BPC was not reported. The aim of this study was to evaluate the effects of simvastatin and Emdogain on BPC compared with mineral trioxide aggregate (MTA) in human dental pulp cells (HDPCs). Cell growth was determined by 3-(4,5-Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium-bromide (MTT) assay. Differentiation was evaluated by alkaline phosphatase (ALP) activity, alizarin red staining, and reverse-transcriptase polymerase chain reaction. The cell growth of HDPCs exposed to Emdogain and simvastatin plus BPC was superior to those administered BPC alone and similar to those that received MTA for 14 days. The simvastatin and Emdogain groups increased the odontogenic potential of the BPC group with respect to ALP activity, mineralization nodules, messenger RNA expression of ALP, osteopontin, osteocalcin, Runx2, and osterix. These results suggest that simvastatin and Emdogain improved cell growth and the differentiation of the BPC group in HDPCs and may be useful ingredients in BPC as pulp-capping material. Copyright © 2012 American Association of Endodontists. Published by Elsevier Inc. All rights reserved.

  4. Os defeitos do esmalte e a erupção dentária em crianças prematuras Evaluation of the dental eruption pattern and of enamel defects in the premature child

    Directory of Open Access Journals (Sweden)

    Fabíola Ferreira Caixeta

    2005-08-01

    Full Text Available OBJETIVO: A proposta do trabalho foi verificar a relação entre defeitos do esmalte e atraso da erupção dentária com prematuridade. MÉTODOS: A amostra consistiu de 100 crianças prematuras, entre seis meses a seis anos de idade em acompanhamento no Instituto da Criança da Faculdade de Medicina da USP. Foi feita uma anamnese da cavidade bucal por apenas um observador, avaliando o tempo da erupção dentária e a ocorrência de defeitos no esmalte. Realizou-se também uma avaliação médica, com dados referentes a possíveis problemas durante o período pré-natal, neonatal e pós-natal. A avaliação estatística utilizou análise descritiva, freqüência média e intervalo de confiança de 95%. RESULTADOS: Defeitos apareceram em 35% das crianças prematuras; 51,43% das que tinham defeitos haviam nascido com peso baixo (2500g . Não houve relação entre ocorrência de defeitos com baixo Boletim de Apgar em 1 minuto, 2 minutos e 5 minutos (p=0,628; p=0,308; p=0,193. Os defeitos mais comuns foram as opacidades brancas, tanto na dentição decídua (19% quanto na permanente (100%. Os terços incisais e cervicais das superfícies vestibulares foram os mais afetados com valores de 88,04% na dentição decídua e 100% na permanente. Cerca de 42% das crianças tiveram dentes irrompidos entre 6 e 10 meses. CONCLUSÃO: Crianças prematuras podem apresentar defeitos do esmalte causados por diferentes fatores durante a gravidez com uma possível associação entre baixo peso e defeito. Os dentes irromperam em tempo normal, no entanto, o número total de dentes até os 36 meses foi menor do que os encontrados em crianças nascidas a termo.BACKGROUD: The purpose of this study was to analyze the relation between enamel defects and delay of dental eruption with prematurity. METHODS: the sample consisted of 100 premature children ranging from six months to six years of age, observed in the Children Institute of the Medical School of the USP. An anamnesis

  5. Enamel hypoplasia and its role in identification of individuals: A review of literature

    Science.gov (United States)

    Kanchan, Tanuj; Machado, Meghna; Rao, Ashwin; Krishan, Kewal; Garg, Arun K.

    2015-01-01

    Identification of individuals is the mainstay of any forensic investigation especially in cases of mass disasters when mutilated remains are brought for examination. Dental examination helps in establishing the identity of an individual and thus, has played a vital role in forensic investigation process since long. In this regard, description on the role of enamel hypoplasia is limited in the literature. The present article reviews the literature on the enamel hypoplasia and discusses its utility in forensic identification. Enamel hypoplasia is a surface defect of the tooth crown caused by disturbance of enamel matrix secretion. Enamel defects can be congenital or acquired. In cases of mass disasters, or when the body is completely charred, putrefied and mutilated beyond recognition, the unique dental features can help in identification of the victims. PMID:26097340

  6. Fine structure and development of the collar enamel in gars, Lepisosteus oculatus, Actinopterygii

    Science.gov (United States)

    Sasagawa, Ichiro; Ishiyama, Mikio; Yokosuka, Hiroyuki; Mikami, Masato

    2008-06-01

    The fine structure of collar enamel and the cells constituting the enamel organ during amelogenesis in Lepisosteus oculatus was observed by light, scanning electron and transmission electron microscopy. In the enamel, slender crystals were arranged perpendicular to the surface and the stripes that were parallel to the surface were observed, suggesting that the enamel in Lepisosteus shares common morphol