WorldWideScience

Sample records for dc reactive magnetron

  1. CrN thin films prepared by reactive DC magnetron sputtering for symmetric supercapacitors

    KAUST Repository

    Wei, Binbin; Liang, Hanfeng; Zhang, Dongfang; Wu, Zhengtao; Qi, Zhengbing; Wang, Zhoucheng

    2016-01-01

    stability are promising candidates as supercapacitor electrode materials. In this work, we report the fabrication of CrN thin films using reactive DC magnetron sputtering and further their applications for symmetric supercapacitors for the first time. The Cr

  2. Dielectric properties of DC reactive magnetron sputtered Al2O3 thin films

    International Nuclear Information System (INIS)

    Prasanna, S.; Mohan Rao, G.; Jayakumar, S.; Kannan, M.D.; Ganesan, V.

    2012-01-01

    Alumina (Al 2 O 3 ) thin films were sputter deposited over well-cleaned glass and Si substrates by DC reactive magnetron sputtering under various oxygen gas pressures and sputtering powers. The composition of the films was analyzed by X-ray photoelectron spectroscopy and an optimal O/Al atomic ratio of 1.59 was obtained at a reactive gas pressure of 0.03 Pa and sputtering power of 70 W. X-ray diffraction results revealed that the films were amorphous until 550 °C. The surface morphology of the films was studied using scanning electron microscopy and the as-deposited films were found to be smooth. The topography of the as-deposited and annealed films was analyzed by atomic force microscopy and a progressive increase in the rms roughness of the films from 3.2 nm to 4.53 nm was also observed with increase in the annealing temperature. Al-Al 2 O 3 -Al thin film capacitors were then fabricated on glass substrates to study the effect of temperature and frequency on the dielectric property of the films. Temperature coefficient of capacitance, AC conductivity and activation energy were determined and the results are discussed. - Highlights: ► Al 2 O 3 thin films were deposited by DC reactive magnetron sputtering. ► The films were found to be amorphous up to annealing temperature of 550 C. ► An increase in rms roughness of the films was observed with annealing. ► Al-Al 2 O 3 -Al thin film capacitors were fabricated and dielectric constant was 7.5. ► The activation energy decreased with increase in frequency.

  3. Bioactivity response of Ta_1_-_xO_x coatings deposited by reactive DC magnetron sputtering

    International Nuclear Information System (INIS)

    Almeida Alves, C.F.; Cavaleiro, A.; Carvalho, S.

    2016-01-01

    The use of dental implants is sometimes accompanied by failure due to periimplantitis disease and subsequently poor esthetics when soft–hard tissue margin recedes. As a consequence, further research is needed for developing new bioactive surfaces able to enhance the osseous growth. Tantalum (Ta) is a promising material for dental implants since, comparing with titanium (Ti), it is bioactive and has an interesting chemistry which promotes the osseointegration. Another promising approach for implantology is the development of implants with oxidized surfaces since bone progenitor cells interact with the oxide layer forming a diffusion zone due to its ability to bind with calcium which promotes a stronger bond. In the present report Ta-based coatings were deposited by reactive DC magnetron sputtering onto Ti CP substrates in an Ar + O_2 atmosphere. In order to assess the osteoconductive response of the studied materials, contact angle and in vitro tests of the samples immersed in Simulated Body Fluid (SBF) were performed. Structural results showed that oxide phases where achieved with larger amounts of oxygen (70 at.% O). More compact and smooth coatings were deposited by increasing the oxygen content. The as-deposited Ta coating presented the most hydrophobic character (100°); with increasing oxygen amount contact angles progressively diminished, down to the lowest measured value, 63°. The higher wettability is also accompanied by an increase on the surface energy. Bioactivity tests demonstrated that highest O-content coating, in good agreement with wettability and surface energy values, showed an increased affinity for apatite adhesion, with higher Ca/P ratio formation, when compared to the bare Ti substrates. - Highlights: • Ta_1_-_xO_x coatings were deposited by reactive DC magnetron sputtering. • Amorphous oxide phases were achieved with higher oxygen amounts. • Contact angles progressively diminished, with increasing oxygen content. • Ta oxide surface

  4. Aluminum oxide films deposited in low pressure conditions by reactive pulsed dc magnetron sputtering

    CERN Document Server

    Seino, T

    2002-01-01

    The reactive pulsed dc sputtering technique is widely used for the deposition of oxide films. The operating pressure for sputtering is commonly above 0.13 Pa. In this study, however, aluminum oxide (alumina) films were deposited at operating pressures from 0.06 to 0.4 Pa using a sputtering system equipped with a scanning magnetron cathode and a pulsed dc power supply. The pulsed dc power was found to be useful not only to reduce arcing, but also to sustain the discharge at low pressure. The electrical breakdown field, intrinsic stress, O/Al ratio, refractive index, and surface roughness were investigated. Both a low intrinsic stress and an O/Al ratio around the stoichiometry were required to get the film having a high breakdown field. A low operating pressure of 0.1 Pa was found to provide the necessary stress and O/Al ratio targets. A 50-nm-thick alumina film having a maximum breakdown field of 7.4 MV/cm was obtained.

  5. CrN thin films prepared by reactive DC magnetron sputtering for symmetric supercapacitors

    KAUST Repository

    Wei, Binbin

    2016-12-29

    Supercapacitors have been becoming indispensable energy storage devices in micro-electromechanical systems and have been widely studied over the past few decades. Transition metal nitrides with excellent electrical conductivity and superior cycling stability are promising candidates as supercapacitor electrode materials. In this work, we report the fabrication of CrN thin films using reactive DC magnetron sputtering and further their applications for symmetric supercapacitors for the first time. The CrN thin film electrodes fabricated under the deposition pressure of 3.5 Pa show an areal specific capacitance of 12.8 mF cm at 1.0 mA cm and high cycling stability with 92.1% capacitance retention after 20 000 cycles in a 0.5 M HSO electrolyte. Furthermore, our developed CrN//CrN symmetric supercapacitor can deliver a high energy density of 8.2 mW h cm at the power density of 0.7 W cm along with outstanding cycling stability. Thus, the CrN thin films have great potential for application in supercapacitors and other energy storage systems.

  6. Electrical and optical properties of reactive DC magnetron sputtered silver oxide thin films: role of oxygen

    Energy Technology Data Exchange (ETDEWEB)

    Kumar Barik, Ullash; Srinivasan, S; Nagendra, C L; Subrahmanyam, A

    2003-04-01

    Silver oxide thin films have been prepared on soda lime glass substrates at room temperature (300 K) by reactive DC Magnetron sputtering technique using pure silver metal target; the oxygen flow rates have been varied in the range 0.00-2.01 sccm. The X-ray diffraction data on these films show a systematic change from metallic silver to silver (sub) oxides. The electrical resistivity increases with increasing oxygen flow. The films show a p-type behavior (by both Hall and Seebeck measurements) for the oxygen flow rates of 0.54, 1.09 and 1.43 sccm. The refractive index of the films (at 632.8 nm) decreases with increasing oxygen content and is in the range 1.167-1.145, whereas the p-type films show a higher refractive index (1.186-1.204). The work function of these silver oxide films has been measured by Kelvin Probe technique. The results, in specific, the p-type conductivity in the silver oxide films, have been explained on the basis of the theory of partial ionic charge proposed by Sanderson.

  7. Electrical and optical properties of reactive DC magnetron sputtered silver oxide thin films: role of oxygen

    International Nuclear Information System (INIS)

    Kumar Barik, Ullash; Srinivasan, S.; Nagendra, C.L.; Subrahmanyam, A.

    2003-01-01

    Silver oxide thin films have been prepared on soda lime glass substrates at room temperature (300 K) by reactive DC Magnetron sputtering technique using pure silver metal target; the oxygen flow rates have been varied in the range 0.00-2.01 sccm. The X-ray diffraction data on these films show a systematic change from metallic silver to silver (sub) oxides. The electrical resistivity increases with increasing oxygen flow. The films show a p-type behavior (by both Hall and Seebeck measurements) for the oxygen flow rates of 0.54, 1.09 and 1.43 sccm. The refractive index of the films (at 632.8 nm) decreases with increasing oxygen content and is in the range 1.167-1.145, whereas the p-type films show a higher refractive index (1.186-1.204). The work function of these silver oxide films has been measured by Kelvin Probe technique. The results, in specific, the p-type conductivity in the silver oxide films, have been explained on the basis of the theory of partial ionic charge proposed by Sanderson

  8. Structural and optical properties of DC reactive magnetron sputtered zinc aluminum oxide thin films

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, B. Rajesh, E-mail: rajphyind@gmail.com [Department of Physics, GITAM Institute of Technology, GITAM University, Visakhapatnam - 530 045, A.P. (India); Rao, T. Subba, E-mail: thotasubbarao6@gmail.com [Department of Physics, Sri Krishnadevaraya University, Anantapuramu - 515 003, A.P. (India)

    2014-10-15

    Highly transparent conductive Zinc Aluminum Oxide (ZAO) thin films have been deposited on glass substrates using DC reactive magnetron sputtering method. The thin films were deposited at 200 °C and post-deposition annealing from 15 to 90 min. XRD patterns of ZAO films exhibit only (0 0 2) diffraction peak, indicating that they have c-axis preferred orientation perpendicular to the substrate. Scanning electron microscopy (SEM) is used to study the surface morphology of the films. The grain size obtained from SEM images of ZAO thin films are found to be in the range of 20 - 26 nm. The minimum resistivity of 1.74 × 10{sup −4} Ω cm and an average transmittance of 92% are obtained for the thin film post annealed for 30 min. The optical band gap of ZAO thin films increased from 3.49 to 3.60 eV with the increase of annealing time due to Burstein-Moss effect. The optical constants refractive index (n) and extinction coefficient (k) were also determined from the optical transmission spectra.

  9. Quantitative characterization of silicon- and aluminium oxynitride films produced by reactive dc-magnetron sputtering

    International Nuclear Information System (INIS)

    Dreer, S.

    2000-05-01

    The deposition of aluminum and silicon oxynitride films by reactive dc-magnetron sputtering was systematically planned by design of experiments, carried out and evaluated with the application of specialized statistics software. The influence of the deposition parameters on the resulting films was evaluated by multiple regression analysis. With the obtained data a model of the deposition process for the quantitative prediction of the deposition parameters necessary to obtain films with desired composition was built. This is also of technological importance, since the physical properties of the films strongly depend on their composition. Furthermore, the long term repeatability of the deposition process was implemented into the model. A precise and economic way for quantitative bulk analysis of silicon/aluminum, oxygen and nitrogen based on EPMA was presented and the use of data gained by the latter method is discussed for the calculation of relative sensitivity factors for SIMS and hf-SNMS. Advantages and disadvantages of SIMS, hf-SNMS, hf-GD-OES, and sputter AES were compared. The combination FT-IR/EPMA/SIMS at present offers the best possibility for a quantitative bulk and in depth distribution analysis of such films in the range of 20 to 1000 nm thickness. The films were also characterized by XRD and PAA. The refractive index and the growth rate of the films were determined by spectroscopic ellipsometry. With indentation by a nano hardness tester the hardness and the Young's modulus of the films were obtained. The results of these measurements were evaluated by statistical software. The dependencies of the physical properties on the deposition parameters and on the film thickness were evaluated and quantified. Furthermore, the dependencies of the physical properties on the film composition represented by the oxygen content were evaluated. (author)

  10. Substantial difference in target surface chemistry between reactive dc and high power impulse magnetron sputtering

    Science.gov (United States)

    Greczynski, G.; Mráz, S.; Schneider, J. M.; Hultman, L.

    2018-02-01

    The nitride layer formed in the target race track during the deposition of stoichiometric TiN thin films is a factor 2.5 thicker for high power impulse magnetron sputtering (HIPIMS), compared to conventional dc processing (DCMS). The phenomenon is explained using x-ray photoelectron spectroscopy analysis of the as-operated Ti target surface chemistry supported by sputter depth profiles, dynamic Monte Carlo simulations employing the TRIDYN code, and plasma chemical investigations by ion mass spectrometry. The target chemistry and the thickness of the nitride layer are found to be determined by the implantation of nitrogen ions, predominantly N+ and N2+ for HIPIMS and DCMS, respectively. Knowledge of this method-inherent difference enables robust processing of high quality functional coatings.

  11. Superhydrophobic photocatalytic PTFE – Titania coatings deposited by reactive pDC magnetron sputtering from a blended powder target

    Energy Technology Data Exchange (ETDEWEB)

    Ratova, Marina, E-mail: marina_ratova@hotmail.com; Kelly, Peter J.; West, Glen T.

    2017-04-01

    The production of photocatalytic coatings with superhydrophobic properties, as opposed to the conventional hydrophilic properties, is desirable for the prevention of adhesion of contaminants to photocatalytic surfaces with subsequent deterioration of photocatalytic properties. In this work polytetrafluoroethylene (PTFE) – TiO{sub 2} composite thin films were deposited using a novel method of reactive pulsed direct current (pDC) magnetron sputtering of a blended PTFE – titanium oxide powder target. The surface characteristics and photocatalytic properties of the deposited composite coatings were studied. The as-deposited coatings were annealed at 523 K in air and analysed with Raman spectroscopy, optical profilometry and scanning electron microscopy. Hydrophobicity was assessed though measurements of water contact angles, and photocatalytic properties were studied via methylene blue dye degradation under UV irradiation. It was found that variations of gas flow and, hence, process pressures allowed deposition of samples combining superhydrophobicity with stable photocatalytic efficiency under UV light irradiation. Reversible wettability behaviour was observed with the alternation of light-dark cycles. - Highlights: • PTFE-TiO{sub 2} coatings were deposited by pDC reactive magnetron sputtering. • Blended powder target was used for coatings deposition. • Deposited coatings combined superhydrophobic and photocatalytic properties. • Under UV irradiation coatings exhibited reversible wettability.

  12. Pulsed dc self-sustained magnetron sputtering

    International Nuclear Information System (INIS)

    Wiatrowski, A.; Posadowski, W. M.; Radzimski, Z. J.

    2008-01-01

    The magnetron sputtering has become one of the commonly used techniques for industrial deposition of thin films and coatings due to its simplicity and reliability. At standard magnetron sputtering conditions (argon pressure of ∼0.5 Pa) inert gas particles (necessary to sustain discharge) are often entrapped in the deposited films. Inert gas contamination can be eliminated during the self-sustained magnetron sputtering (SSS) process, where the presence of the inert gas is not a necessary requirement. Moreover the SSS process that is possible due to the high degree of ionization of the sputtered material also gives a unique condition during the transport of sputtered particles to the substrate. So far it has been shown that the self-sustained mode of magnetron operation can be obtained using dc powering (dc-SSS) only. The main disadvantage of the dc-SSS process is its instability related to random arc formation. In such case the discharge has to be temporarily extinguished to prevent damaging both the magnetron source and power supply. The authors postulate that pulsed powering could protect the SSS process against arcs, similarly to reactive pulsed magnetron deposition processes of insulating thin films. To put this concept into practice, (i) the high enough plasma density has to be achieved and (ii) the type of pulsed powering has to be chosen taking plasma dynamics into account. In this article results of pulsed dc self-sustained magnetron sputtering (pulsed dc-SSS) are presented. The planar magnetron equipped with a 50 mm diameter and 6 mm thick copper target was used during the experiments. The maximum target power was about 11 kW, which corresponded to the target power density of ∼560 W/cm 2 . The magnetron operation was investigated as a function of pulse frequency (20-100 kHz) and pulse duty factor (50%-90%). The discharge (argon) extinction pressure level was determined for these conditions. The plasma emission spectra (400-410 nm range) and deposition

  13. Dielectric properties of DC reactive magnetron sputtered Al{sub 2}O{sub 3} thin films

    Energy Technology Data Exchange (ETDEWEB)

    Prasanna, S. [Thin Film Center, Department of Physics, PSG College of Technology, Coimbatore, 641 004 (India); Mohan Rao, G. [Department of Instrumentation, Indian Institute of Science (IISc), Bangalore, 560 012 (India); Jayakumar, S., E-mail: s_jayakumar_99@yahoo.com [Thin Film Center, Department of Physics, PSG College of Technology, Coimbatore, 641 004 (India); Kannan, M.D. [Thin Film Center, Department of Physics, PSG College of Technology, Coimbatore, 641 004 (India); Ganesan, V. [Low Temperature Lab, UGC-DAE Consortium for Scientific Research (CSR), Indore, 452 017 (India)

    2012-01-31

    Alumina (Al{sub 2}O{sub 3}) thin films were sputter deposited over well-cleaned glass and Si < 100 > substrates by DC reactive magnetron sputtering under various oxygen gas pressures and sputtering powers. The composition of the films was analyzed by X-ray photoelectron spectroscopy and an optimal O/Al atomic ratio of 1.59 was obtained at a reactive gas pressure of 0.03 Pa and sputtering power of 70 W. X-ray diffraction results revealed that the films were amorphous until 550 Degree-Sign C. The surface morphology of the films was studied using scanning electron microscopy and the as-deposited films were found to be smooth. The topography of the as-deposited and annealed films was analyzed by atomic force microscopy and a progressive increase in the rms roughness of the films from 3.2 nm to 4.53 nm was also observed with increase in the annealing temperature. Al-Al{sub 2}O{sub 3}-Al thin film capacitors were then fabricated on glass substrates to study the effect of temperature and frequency on the dielectric property of the films. Temperature coefficient of capacitance, AC conductivity and activation energy were determined and the results are discussed. - Highlights: Black-Right-Pointing-Pointer Al{sub 2}O{sub 3} thin films were deposited by DC reactive magnetron sputtering. Black-Right-Pointing-Pointer The films were found to be amorphous up to annealing temperature of 550 C. Black-Right-Pointing-Pointer An increase in rms roughness of the films was observed with annealing. Black-Right-Pointing-Pointer Al-Al{sub 2}O{sub 3}-Al thin film capacitors were fabricated and dielectric constant was 7.5. Black-Right-Pointing-Pointer The activation energy decreased with increase in frequency.

  14. Decorative black TiCxOy film fabricated by DC magnetron sputtering without importing oxygen reactive gas

    Science.gov (United States)

    Ono, Katsushi; Wakabayashi, Masao; Tsukakoshi, Yukio; Abe, Yoshiyuki

    2016-02-01

    Decorative black TiCxOy films were fabricated by dc (direct current) magnetron sputtering without importing the oxygen reactive gas into the sputtering chamber. Using a ceramic target of titanium oxycarbide (TiC1.59O0.31), the oxygen content in the films could be easily controlled by adjustment of total sputtering gas pressure without remarkable change of the carbon content. The films deposited at 2.0 and 4.0 Pa, those are higher pressure when compared with that in conventional magnetron sputtering, showed an attractive black color. In particular, the film at 4.0 Pa had the composition of TiC1.03O1.10, exhibited the L* of 41.5, a* of 0.2 and b* of 0.6 in CIELAB color space. These values were smaller than those in the TiC0.29O1.38 films (L* of 45.8, a* of 1.2 and b* of 1.2) fabricated by conventional reactive sputtering method from the same target under the conditions of gas pressure of 0.3 Pa and optimized oxygen reactive gas concentration of 2.5 vol.% in sputtering gas. Analysis of XRD and XPS revealed that the black film deposited at 4.0 Pa was the amorphous film composed of TiC, TiO and C. The adhesion property and the heat resisting property were enough for decorative uses. This sputtering process has an industrial advantage that the decorative black coating with color uniformity in large area can be easily obtained by plain operation because of unnecessary of the oxygen reactive gas importing which is difficult to be controlled uniformly in the sputtering chamber.

  15. Bonding structure and morphology of chromium oxide films grown by pulsed-DC reactive magnetron sputter deposition

    Energy Technology Data Exchange (ETDEWEB)

    Gago, R., E-mail: rgago@icmm.csic.es [Instituto de Ciencia de Materiales de Madrid, Consejo Superior de Investigaciones Científicas, E-28049 Madrid (Spain); Vinnichenko, M. [Fraunhofer-Institut für Keramische Technologien und Systeme IKTS, D-01277 Dresden (Germany); Hübner, R. [Helmholtz-Zentrum Dresden – Rossendorf, Institute of Ion Beam Physics and Materials Research, Bautzner Landstraße 400, 01328 Dresden (Germany); Redondo-Cubero, A. [Departamento de Física Aplicada and Centro de Microanálisis de Materiales, Universidad Autónoma de Madrid, E-28049 Madrid (Spain)

    2016-07-05

    Chromium oxide (CrO{sub x}) thin films were grown by pulsed-DC reactive magnetron sputter deposition in an Ar/O{sub 2} discharge as a function of the O{sub 2} fraction in the gas mixture (ƒ) and for substrate temperatures, T{sub s}, up to 450 °C. The samples were analysed by Rutherford backscattering spectrometry (RBS), spectroscopic ellipsometry (SE), atomic force microscopy (AFM), scanning (SEM) and transmission (TEM) electron microscopy, X-ray diffraction (XRD), and X-ray absorption near-edge structure (XANES). On unheated substrates, by increasing ƒ the growth rate is higher and the O/Cr ratio (x) rises from ∼2 up to ∼2.5. Inversely, by increasing T{sub s} the atomic incorporation rate drops and x falls to ∼1.8. XRD shows that samples grown on unheated substrates are amorphous and that nanocrystalline Cr{sub 2}O{sub 3} (x = 1.5) is formed by increasing T{sub s}. In amorphous CrO{sub x}, XANES reveals the presence of multiple Cr environments that indicate the growth of mixed-valence oxides, with progressive promotion of hexavalent states with ƒ. XANES data also confirms the formation of single-phase nanocrystalline Cr{sub 2}O{sub 3} at elevated T{sub s}. These structural changes also reflect on the optical and morphological properties of the films. - Highlights: • XANES of CrO{sub x} thin films grown by pulsed-DC reactive magnetron sputtering. • Identification of mixed-valence amorphous CrO{sub x} oxides on unheated substrates. • Promotion of amorphous chromic acid (Cr{sup VI}) by increasing O{sub 2} partial pressure. • Production of single-phase Cr{sub 2}O{sub 3} films by increasing substrate temperature. • Correlation of bonding structure with morphological and optical properties.

  16. Bioactivity response of Ta{sub 1-x}O{sub x} coatings deposited by reactive DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Almeida Alves, C.F., E-mail: cristiana.alves@fisica.uminho.pt [GRF-CFUM, Physics Departament, University of Minho, Campus of Azurem, Guimaraes 4800-058 (Portugal); Cavaleiro, A. [SEG-CEMUC, Mechanical Engineering Department, University of Coimbra, Coimbra 3030-788 (Portugal); Carvalho, S. [GRF-CFUM, Physics Departament, University of Minho, Campus of Azurem, Guimaraes 4800-058 (Portugal); SEG-CEMUC, Mechanical Engineering Department, University of Coimbra, Coimbra 3030-788 (Portugal)

    2016-01-01

    The use of dental implants is sometimes accompanied by failure due to periimplantitis disease and subsequently poor esthetics when soft–hard tissue margin recedes. As a consequence, further research is needed for developing new bioactive surfaces able to enhance the osseous growth. Tantalum (Ta) is a promising material for dental implants since, comparing with titanium (Ti), it is bioactive and has an interesting chemistry which promotes the osseointegration. Another promising approach for implantology is the development of implants with oxidized surfaces since bone progenitor cells interact with the oxide layer forming a diffusion zone due to its ability to bind with calcium which promotes a stronger bond. In the present report Ta-based coatings were deposited by reactive DC magnetron sputtering onto Ti CP substrates in an Ar + O{sub 2} atmosphere. In order to assess the osteoconductive response of the studied materials, contact angle and in vitro tests of the samples immersed in Simulated Body Fluid (SBF) were performed. Structural results showed that oxide phases where achieved with larger amounts of oxygen (70 at.% O). More compact and smooth coatings were deposited by increasing the oxygen content. The as-deposited Ta coating presented the most hydrophobic character (100°); with increasing oxygen amount contact angles progressively diminished, down to the lowest measured value, 63°. The higher wettability is also accompanied by an increase on the surface energy. Bioactivity tests demonstrated that highest O-content coating, in good agreement with wettability and surface energy values, showed an increased affinity for apatite adhesion, with higher Ca/P ratio formation, when compared to the bare Ti substrates. - Highlights: • Ta{sub 1-x}O{sub x} coatings were deposited by reactive DC magnetron sputtering. • Amorphous oxide phases were achieved with higher oxygen amounts. • Contact angles progressively diminished, with increasing oxygen content. • Ta

  17. Electrical and optical properties of reactive dc magnetron sputtered silver-doped indium oxide thin films: role of oxygen

    International Nuclear Information System (INIS)

    Subrahmanyam, A.; Barik, U.K.

    2006-01-01

    Silver-doped indium oxide thin films have been prepared on glass and quartz substrates at room temperature (300 K) by a reactive dc magnetron sputtering technique using an alloy target of pure indium and silver (80:20 at. %). During sputtering, the oxygen flow rates are varied in the range 0.00-2.86 sccm keeping the magnetron power constant at 40 W. The resistivity of these films is in the range 10 0 -10 -3 Ωcm and they show a negative temperature coefficient of resistivity. The films exhibit p-type conductivity at an oxygen flow rate of 1.71 sccm. The work function of these silver-indium oxide films has been measured by a Kelvin probe technique. The refractive index of the films (at 632.8 nm) varies in the range 1.13-1.20. Silver doping in indium oxide narrows the band gap of indium oxide (3.75 eV). (orig.)

  18. Electrical and optical properties of reactive dc magnetron sputtered silver-doped indium oxide thin films: role of oxygen

    Energy Technology Data Exchange (ETDEWEB)

    Subrahmanyam, A; Barik, U K [Indian Institute of Technology Madras, Semiconductor Physics Laboratory, Department of Physics, Chennai (India)

    2006-07-15

    Silver-doped indium oxide thin films have been prepared on glass and quartz substrates at room temperature (300 K) by a reactive dc magnetron sputtering technique using an alloy target of pure indium and silver (80:20 at. %). During sputtering, the oxygen flow rates are varied in the range 0.00-2.86 sccm keeping the magnetron power constant at 40 W. The resistivity of these films is in the range 10{sup 0}-10{sup -3} {omega}cm and they show a negative temperature coefficient of resistivity. The films exhibit p-type conductivity at an oxygen flow rate of 1.71 sccm. The work function of these silver-indium oxide films has been measured by a Kelvin probe technique. The refractive index of the films (at 632.8 nm) varies in the range 1.13-1.20. Silver doping in indium oxide narrows the band gap of indium oxide (3.75 eV). (orig.)

  19. Incorporation of N in TiO{sub 2} films grown by DC-reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Serio, S. [CEFITEC, Departamento de Fisica, Faculdade de Ciencias e Tecnologia da Universidade Nova de Lisboa, 2829-516 Caparica (Portugal); Melo Jorge, M.E. [CCMM, Departamento de Quimica e Bioquimica, Faculdade de Ciencias da Universidade de Lisboa, Campo Grande C8, 1749-016 Lisboa (Portugal); Nunes, Y. [CEFITEC, Departamento de Fisica, Faculdade de Ciencias e Tecnologia da Universidade Nova de Lisboa, 2829-516 Caparica (Portugal); Barradas, N.P. [Instituto Tecnologico e Nuclear and CFNUL, E.N. 10, Sacavem 2686-953 (Portugal); Alves, E., E-mail: ealves@itn.pt [Instituto Tecnologico e Nuclear and CFNUL, E.N. 10, Sacavem 2686-953 (Portugal); Munnik, F. [Helmholtz-Zentrum Dresden-Rossendorf (Germany)

    2012-02-15

    Photocatalytic properties of TiO{sub 2} are expected to play an important role on emerging technologies based on OH radicals to destroy harmful nonbiodegradable organic and inorganic contaminants in water. The drawback is the wide band gap of TiO{sub 2} (3.2 eV) limiting its use to the UV part of electromagnetic spectrum under sunlight. Therefore, modifications of TiO{sub 2} are needed to tune the gap in order to allow an efficient use of the entire solar spectrum. One possibility is N-doping of TiO{sub 2} to make the photocatalytic activity possible under visible light and more suitable for water treatment. In our study nitrogen-doped TiO{sub 2} (TiO{sub 2-x}N{sub x}) films were deposited by DC-reactive magnetron sputtering using a dual-magnetron co-deposition apparatus on unheated glass and silicon substrates using a pure titanium target. The depth profile of nitrogen was measured with heavy ion elastic recoil detection analysis combined with Rutherford backscattering spectrometry (RBS) and correlated with the optical and structural properties obtained by UV-VIS spectroscopy and X-ray diffraction (XRD).

  20. The microstructure and wettability of the TiO{sub x} films synthesized by reactive DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Lin Zeng [School of Mechanical Engineering and Automation, Northeastern University, Shenyang 110004 (China); State Key Laboratory of Plastic Forming Simulation and Die and Mould Technology Wuhan, Hubei 430074 (China)], E-mail: linzengsy@gmail.com; Liu Kun; Zhang Yichen; Yue Xiangji; Song Guiqiu [School of Mechanical Engineering and Automation, Northeastern University, Shenyang 110004 (China); Ba Dechun [School of Mechanical Engineering and Automation, Northeastern University, Shenyang 110004 (China)], E-mail: dechunba@yahoo.com

    2009-01-25

    Different chemical state of titanium oxide films were deposited on commercially pure Ti (CP Ti) by reactive DC magnetron sputtering under different oxygen flow rates to examine a possibility of their applications to endovascular stents. The chemical composition and crystal structure of the obtained films were analyzed by XPS and XRD, respectively. In dependence on the deposition parameters employed, the obtained films demonstrated different mixture of anatase TiO{sub 2}, Ti{sub 2}O{sub 3}, TiO and Ti. The wettability of the films was measured by the water contact angle variation. By formation of titanium oxide film on CP Ti, contact angle was decreased. In order to modify and control the surface wettability, the resultant TiO{sub x} films were etched subsequently by different plasma. The wettability was influenced by etched process according to the decreased contact angle values of etched TiO{sub x} film. Furthermore, TiO{sub x} films became highly hydrophilic by ultraviolet (UV) irradiation, and returned to the initial relatively hydrophobic state by visible-light (VIS) irradiation. The wettability of the TiO{sub x} film was enabled to convert between hydrophilic and hydrophobic reversibly by alternative UV and VIS irradiation. By adjusting deposition parameter and further modification process, the wettability of the TiO{sub x} films can be changed freely in the range of 0-90 deg.

  1. Preparation of p-type transparent conducting tin-antimony oxide thin films by DC reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Ji, Zhenguo [College of Electronic Information, Hangzhou Dianzi University, Hangzhou (China); State Key Laboratory for Silicon Materials, Zhejiang University, Hangzhou (China); Xi, Junhua; Huo, Lijuan; Zhao, Yi [State Key Laboratory for Silicon Materials, Zhejiang University, Hangzhou (China)

    2008-07-01

    P-type transparent conducting tin-antimony oxide (TAO) films were successfully prepared by DC reactive magnetron sputtering followed by post annealing in the air. Structural, optical and electrical properties of the TAO films were investigated. X-ray diffraction studies showed that the films are polycrystalline with orthorhombic structure of Sb{sub 2}O{sub 4}. UV-Visible absorption and transmittance spectra showed that the optical band-gap of the TAO films is about 3.90 eV, and the overall transmittance is higher than 85% in the visible region. Hall effect measurement indicated that the Sn/Sb ratio is a critical parameter to get p-type conducting TAO films. It was found that 0.19

  2. Optical emission and mass spectroscopy of plasma processes in reactive DC pulsed magnetron sputtering of aluminium oxide

    Czech Academy of Sciences Publication Activity Database

    Novotný, Michal; Bulíř, Jiří; Pokorný, Petr; Bočan, Jiří; Fitl, Přemysl; Lančok, Ján; Musil, Jindřich

    2010-01-01

    Roč. 12, č. 3 (2010), 697-700 ISSN 1454-4164 R&D Projects: GA AV ČR IAA100100718; GA AV ČR KAN400100653; GA ČR GP202/09/P324 Institutional research plan: CEZ:AV0Z10100522 Keywords : reactive magnetron sputtering * alumina * plasma spectroscopy * mass spectroscopy * optical emission spectroscopy Subject RIV: BH - Optics, Masers, Lasers Impact factor: 0.412, year: 2010

  3. Hetero-epitaxial growth of TiC films on MgO(001) at 100 °C by DC reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Braic, M.; Zoita, N.C.; Danila, M.; Grigorescu, C.E.A.; Logofatu, C.

    2015-01-01

    Hetero-epitaxial TiC thin films were deposited at 100 °C on MgO(001) by DC reactive magnetron sputtering in a mixture of Ar and CH 4 . The 62 nm thick films were analyzed for elemental composition and chemical bonding by Auger electron spectroscopy, X-ray photoelectron spectroscopy and micro-Raman spectroscopy. The crystallographic structure investigation by high resolution X-ray diffraction revealed that the films consist of two layers: an interface partially strained epilayer with high crystalline quality, and a relaxed layer, formed by columnar grains, maintaining the epitaxial relationship with the substrate. The films presented smooth surfaces (RMS roughness ~ 0.55 nm), with circular equi-sized grains/crystallites, as observed by atomic force microscopy. The Hall measurements in Van der Pauw geometry revealed relatively high resistivity value ~ 620 μΩ cm, ascribed to electron scattering on interfaces, on grain boundaries and on different defects/dislocations. - Highlights: • Hetero-epitaxial TiC 0.84 thin films were grown on MgO(001) at 100 °C by magnetron sputtering. • 62 nm thick films were synthesized by magnetron sputtering, using Ti, Ar and CH 4 . • The film comprises a partially strained interface epilayer and a relaxed top layer. • Both layers preserve the epitaxial relationship with the substrate. • Low RMS surface roughness ~ 0.55 nm and grains with mean lateral size of ~ 38.5 nm were observed

  4. Hetero-epitaxial growth of TiC films on MgO(001) at 100 °C by DC reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Braic, M. [National Institute for Optoelectronics, 409 Atomistilor St., 077125 Magurele (Romania); Zoita, N.C., E-mail: cnzoita@inoe.ro [National Institute for Optoelectronics, 409 Atomistilor St., 077125 Magurele (Romania); Danila, M. [National Institute for Research and Development in Microtechnology, 126A Erou Iancu Nicolae Blvd., 077190 Bucharest (Romania); Grigorescu, C.E.A. [National Institute for Optoelectronics, 409 Atomistilor St., 077125 Magurele (Romania); Logofatu, C. [National Institute of Materials Physics, 105 bis Atomistilor St., 077125 Magurele (Romania)

    2015-08-31

    Hetero-epitaxial TiC thin films were deposited at 100 °C on MgO(001) by DC reactive magnetron sputtering in a mixture of Ar and CH{sub 4}. The 62 nm thick films were analyzed for elemental composition and chemical bonding by Auger electron spectroscopy, X-ray photoelectron spectroscopy and micro-Raman spectroscopy. The crystallographic structure investigation by high resolution X-ray diffraction revealed that the films consist of two layers: an interface partially strained epilayer with high crystalline quality, and a relaxed layer, formed by columnar grains, maintaining the epitaxial relationship with the substrate. The films presented smooth surfaces (RMS roughness ~ 0.55 nm), with circular equi-sized grains/crystallites, as observed by atomic force microscopy. The Hall measurements in Van der Pauw geometry revealed relatively high resistivity value ~ 620 μΩ cm, ascribed to electron scattering on interfaces, on grain boundaries and on different defects/dislocations. - Highlights: • Hetero-epitaxial TiC{sub 0.84} thin films were grown on MgO(001) at 100 °C by magnetron sputtering. • 62 nm thick films were synthesized by magnetron sputtering, using Ti, Ar and CH{sub 4}. • The film comprises a partially strained interface epilayer and a relaxed top layer. • Both layers preserve the epitaxial relationship with the substrate. • Low RMS surface roughness ~ 0.55 nm and grains with mean lateral size of ~ 38.5 nm were observed.

  5. Enhancement in dye-sensitized solar cells based on MgO-coated TiO2 electrodes by reactive DC magnetron sputtering

    International Nuclear Information System (INIS)

    Wu Sujuan; Han Hongwei; Tai Qidong; Zhang Jing; Xu Sheng; Zhou Conghua; Yang Ying; Hu Hao; Chen Bolei; Sebo, Bobby; Zhao Xingzhong

    2008-01-01

    A surface modification method was carried out by reactive DC magnetron sputtering to fabricate TiO 2 electrodes coated with insulating MgO for dye-sensitized solar cells. The MgO-coated TiO 2 electrode had been characterized by x-ray photoelectron spectroscopy (XPS), energy-dispersive x-ray spectroscopy (EDX), scanning electron microscopy (SEM), UV-vis spectrophotometer, cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The study results revealed that the TiO 2 modification increases dye adsorption, decreases trap states and suppresses interfacial recombination. The effects of sputtering MgO for different times on the performance of DSSCs were investigated. It indicated that sputtering MgO for 3 min on TiO 2 increases all cell parameters, resulting in increasing efficiency from 6.45% to 7.57%

  6. Effect of N Concentration on Microstructure Evolution of the Nanostructured (Al, Ti, SiN Coatings Prepared by d.c. Reactive Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    L. Jakab-Farkas

    2009-12-01

    Full Text Available Nanostructured (Al, Ti, SiN thin film coatings were synthesized by d.c. reactive magnetron sputtering, performed in an Ar/N2 gas mixture from a planar rectangular Al:Ti:Si=50:25:25 alloyed target. The mass flow of N2 reactive gas was strictly controlled in sputtering process. Conventional transmission electron microscopy (TEM technique was used for microstructure investigation of the as deposited films. Cross-sectional cuts performed through the deposited films revealed distinct microstructure evolution for different samples. It was found that the variation of the reactive gas amount induced changes in film microstructure. The metallic AlTiSi film exhibited strong columnar growth with a crystalline structure. The addition of a small amount of nitrogen to the process gas leads to a crystallite refinement. Further increase of N concentration resulted in evolution of fine lamellae growth morphology consisting of hainlike pearls in a dendrite, clusters of very fine grains in close crystallographic orientation.

  7. Studies on the electrical properties of reactive DC magnetron-sputtered indium-doped silver oxide thin films: The role of oxygen

    Energy Technology Data Exchange (ETDEWEB)

    Subrahmanyam, A [Semiconductor Physics Laboratory, Department of Physics, Indian Institute of Technology Madras, Chennai 600036 (India); Barik, Ullash Kumar [Semiconductor Physics Laboratory, Department of Physics, Indian Institute of Technology Madras, Chennai 600036 (India)

    2007-03-15

    Indium ({approx}10 at.%)-doped silver oxide (AIO) thin films have been prepared on glass substrates at room temperature (300 K) by reactive DC magnetron sputtering technique using an alloy target made of pure (99.99%) silver and indium (90:10 at.%) metals. The oxygen flow rates have been varied in the range 0.00-3.44 sccm during sputtering. The X-ray diffraction data on these indium-doped silver oxide films show polycrystalline nature. With increasing oxygen flow rate, the carrier concentration, the Hall mobility and the electron mean free path decrease. These films show a very low positive temperature coefficient of resistivity {approx}3.40x10{sup -8} ohm-cm/K. The work function values for these films (measured by Kelvin probe technique) are in the range 4.81-5.07 eV. The high electrical resistivity indicate that the films are in the island state (size effects). Calculations of the partial ionic charge (by Sanderson's theory) show that indium doping in silver oxide thin films enhance the ionicity.

  8. Studies on the electrical properties of reactive DC magnetron-sputtered indium-doped silver oxide thin films: The role of oxygen

    International Nuclear Information System (INIS)

    Subrahmanyam, A.; Barik, Ullash Kumar

    2007-01-01

    Indium (∼10 at.%)-doped silver oxide (AIO) thin films have been prepared on glass substrates at room temperature (300 K) by reactive DC magnetron sputtering technique using an alloy target made of pure (99.99%) silver and indium (90:10 at.%) metals. The oxygen flow rates have been varied in the range 0.00-3.44 sccm during sputtering. The X-ray diffraction data on these indium-doped silver oxide films show polycrystalline nature. With increasing oxygen flow rate, the carrier concentration, the Hall mobility and the electron mean free path decrease. These films show a very low positive temperature coefficient of resistivity ∼3.40x10 -8 ohm-cm/K. The work function values for these films (measured by Kelvin probe technique) are in the range 4.81-5.07 eV. The high electrical resistivity indicate that the films are in the island state (size effects). Calculations of the partial ionic charge (by Sanderson's theory) show that indium doping in silver oxide thin films enhance the ionicity

  9. Optical properties and thermal stability of TiAlN/AlON tandem absorber prepared by reactive DC/RF magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Barshilia, Harish C.; Selvakumar, N.; Rajam, K.S. [Surface Engineering Division, National Aerospace Laboratories, Bangalore 560 017 (India); Biswas, A. [Spectroscopy Division, Bhabha Atomic Research Center, Mumbai 400 085 (India)

    2008-11-15

    Spectrally selective TiAlN/AlON tandem absorbers were deposited on copper and stainless steel substrates using a reactive DC/RF magnetron sputtering system. The compositions and thicknesses of the individual component layers were optimized to achieve high absorptance ({alpha}=0.931-0.942) and low emittance ({epsilon}=0.05-0.06) on copper substrate. The experimental spectroscopic ellipsometric data have been fitted with the theoretical models to derive the dispersion of the optical constants (n and k). In order to study the thermal stability of the tandem absorbers, they were subjected to heat treatment (in air and vacuum) for different durations and temperatures. The tandem absorber deposited on Cu substrates exhibited high solar selectivity ({alpha}/{epsilon}) of 0.946/0.07 even after heat treatment in air up to 600 C for 2 h. At 625 C, the solar selectivity decreased significantly on Cu substrates (e.g., {alpha}/{epsilon}=0.924/0.30). The tandem absorber on Cu substrates was also stable in air up to 100 h at 400 C with a solar selectivity of 0.919/0.06. Studies on the accelerated aging tests indicated that the activation energy for the degradation of the tandem absorber is of the order of 100 kJ/mol. (author)

  10. Reactive dual magnetron sputtering for large area application

    International Nuclear Information System (INIS)

    Struempfel, J.

    2002-01-01

    Production lines for large area coating demand high productivity of reactive magnetron sputtering processes. Increased dynamic deposition rates for oxides and nitrides were already obtained by using of highly powered magnetrons in combination with advanced sputter techniques. However, besides high deposition rates the uniformity of such coatings has to be carefully considered. First the basics of reactive sputtering processes and dual magnetron sputtering are summarized. Different methods for process stabilization and control are commonly used for reactive sputtering. The Plasma Emission Monitor (PE M) offers the prerequisite for fast acting process control derived from the in-situ intensity measurements of a spectral line of the sputtered target material. Combined by multiple Plasma Emission Monitor control loops segmented gas manifolds are able to provide excellent thin film uniformity at high deposition rates. The Dual Magnetron allows a broad range of processing by different power supply modes. Medium frequency, DC and pulsed DC power supplies can be used for high quality layers. Whereas the large area coating of highly isolating layers like TiO 2 or SiO 2 is dominated by MF sputtering best results for coating with transparent conductive oxides are obtained by dual DC powering of the dual magnetron arrangement. (Author)

  11. Raman studies of reactive DC-magnetron sputtered thin films of YBaCuO on MgO

    International Nuclear Information System (INIS)

    Sheng, K.C.; Lee, S.J.; Shen, Y.H.; Wang, X.K.; Rippert, E.D.; Van Duyne, R.P.; Ketterson, J.B.; Chang, R.P.H.

    1989-01-01

    Raman spectroscopy was employed to study Y-Ba-Cu-O films prepared by multilayer, reactive sputtering from separate Y, Cu, and Ba 0.5 Cu 0.5 targets. A set of films having the composition Y x Ba 2 Cu y O z with 0.7 c (R=0), ranging from 25 to 90 K was studied with the Raman technique. The correlation between Raman data and critical temperature, T c , was investigated. This technique provides important information concerning the film crystallinity, homogeneity, and impurity content (including other phases) which is useful in judging the quality of high T c superconducting films. We also found that the rapid thermal annealing process is a very efficient way to reduce chemical reactions between the film and the substrate

  12. Controlled formation of anatase and rutile TiO2 thin films by reactive magnetron sputtering

    NARCIS (Netherlands)

    Rafieian Boroujeni, Damon; Ogieglo, Wojciech; Savenije, Tom; Lammertink, Rob G.H.

    2015-01-01

    We discuss the formation of TiO2 thin films via DC reactive magnetron sputtering. The oxygen concentration during sputtering proved to be a crucial parameter with respect to the final film structure and properties. The initial deposition provided amorphous films that crystallise upon annealing to

  13. Controlled formation of anatase and rutile TiO2 thin films by reactive magnetron sputtering

    OpenAIRE

    Rafieian Boroujeni, Damon; Ogieglo, Wojciech; Savenije, Tom; Lammertink, Rob G.H.

    2015-01-01

    We discuss the formation of TiO2 thin films via DC reactive magnetron sputtering. The oxygen concentration during sputtering proved to be a crucial parameter with respect to the final film structure and properties. The initial deposition provided amorphous films that crystallise upon annealing to anatase or rutile, depending on the initial sputtering conditions. Substoichiometric films (TiOx

  14. Heteroepitaxial Ge-on-Si by DC magnetron sputtering

    Directory of Open Access Journals (Sweden)

    Martin Steglich

    2013-07-01

    Full Text Available The growth of Ge on Si(100 by DC Magnetron Sputtering at various temperatures is studied by Spectroscopic Ellipsometry and Transmission Electron Microscopy. Smooth heteroepitaxial Ge films are prepared at relatively low temperatures of 380°C. Typical Stransky-Krastanov growth is observed at 410°C. At lower temperatures (320°C, films are essentially amorphous with isolated nanocrystallites at the Si-Ge interface. A minor oxygen contamination at the interface, developing after ex-situ oxide removal, is not seen to hinder epitaxy. Compensation of dislocation-induced acceptors in Ge by sputtering from n-doped targets is proposed.

  15. Discharge Characteristic of VHF-DC Superimposed Magnetron Sputtering System

    Science.gov (United States)

    Toyoda, Hirotaka; Fukuoka, Yushi; Fukui, Takashi; Takada, Noriharu; Sasai, Kensuke

    2014-10-01

    Magnetron plasmas are one of the most important tools for sputter deposition of thin films. However, energetic particles from the sputtered target such as backscattered rare gas atoms or oxygen negative ions from oxide targets sometimes induce physical and chemical damages as well as surface roughening to the deposited film surface during the sputtering processes. To suppress kinetic energy of such particles, superposition of RF or VHF power to the DC power has been investigated. In this study, influence of the VHF power superposition on the DC target voltage, which is important factor to determine kinetic energy of high energy particles, is investigated. In the study, 40 MHz VHF power was superimposed to an ITO target and decrease in the target DC voltage was measured as well as deposited film deposition properties such as deposition rate or electrical conductivity. From systematic measurement of the target voltage, it was revealed that the target voltage can be determined by a very simple parameter, i.e., a ratio of VHF power to the total input power (DC and VHF powers) in spite of the DC discharge current. Part of this work was supported by ASTEP, JST.

  16. Dependence of plasma characteristics on dc magnetron sputter parameters

    International Nuclear Information System (INIS)

    Wu, S.Z.

    2005-01-01

    Plasma discharge characteristics of a dc magnetron system were measured by a single Langmuir probe at the center axis of the dual-side process chamber. Plasma potential, floating potential, electron and ion densities, and electron temperature were extracted with varying dc power and gas pressure during sputter deposition of a metal target; strong correlations were shown between these plasma parameters and the sputter parameters. The electron density was controlled mostly by secondary electron generation in constant power mode, while plasma potential reflects the confinement space variation due to change of discharge voltage. When discharge pressure was varied, plasma density increases with the increased amount of free stock molecules, while electron temperature inversely decreased, due to energy-loss collision events. In low-pressure discharges, the electron energy distribution function measurements show more distinctive bi-Maxwellian distribution, with the fast electron temperature gradually decreases with increased gas pressure

  17. Microstructural variation in titanium oxide thin films deposited by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Pandian, Ramanathaswamy; Natarajan, Gomathi; Kamruddin, M.; Tyagi, A.K.

    2013-01-01

    We report on the microstructural evolution of titanium oxide thin films deposited by reactive DC magnetron sputtering using titanium metal target. By varying the ratio of sputter-gas mixture containing argon, oxygen and nitrogen various phases of titanium oxide, almost pure rutile, rutile-rich and anatase-rich nano-crystalline, were deposited on Si substrates at room temperature. Using high-resolution scanning electron microscopy, X-ray diffraction and micro-Raman techniques the microstructure of the films were revealed. The relationship between the microstructure of the films and the oxygen partial pressure during sputtering is discussed

  18. ELECTRICAL PROPERTIES OF DC REACTIVE MAGNETRON ...

    African Journals Online (AJOL)

    Mgina

    value of the AC resistivity was given by the ZnO:Al film with the highest value of ... Compared to other thin film ... critical parameters in determining the ... approach in studying the electronic transport ..... J 2009 Electrical and optical studies of.

  19. Effect of electroless nickel interlayer on the electrochemical behavior of single layer CrN, TiN, TiAlN coatings and nanolayered TiAlN/CrN multilayer coatings prepared by reactive dc magnetron sputtering

    International Nuclear Information System (INIS)

    Grips, V.K. William; Ezhil Selvi, V.; Barshilia, Harish C.; Rajam, K.S.

    2006-01-01

    The electrochemical behavior of single layer TiN, CrN, TiAlN and multilayer TiAlN/CrN coatings, deposited on steel substrates using a multi-target reactive direct current (dc) magnetron sputtering process, was studied in 3.5% NaCl solution. The total thickness of the coatings was about 1.5 μm. About 0.5 μm thick chromium interlayer was used to improve adhesion of the coatings. With an aim to improve the corrosion resistance, an additional interlayer of approximately 5 μm thick electroless nickel (EN) was deposited on the substrate. Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) were used to study the corrosion behavior of the coatings. Scanning electron microscopy and energy dispersive X-ray analysis were used to characterize the corroded samples. The potentiodynamic polarization tests showed lower corrosion current density and higher polarization resistance (R p ) for the coatings with EN interlayer. For example, the corrosion current density of TiN coated steel was decreased by a factor of 10 by incorporating 5 μm thick EN interlayer. Similarly, multilayer coatings of TiAlN/CrN with EN interlayer showed about 30 times improved corrosion resistance as compared to the multilayers without EN interlayer. The porosity values were calculated from the potentiodynamic polarization data. The Nyquist and the Bode plots obtained from the EIS data were fitted by appropriate equivalent circuits. The pore resistance (R pore ), the charge transfer resistance (R ct ), the coating capacitance (Q coat ) and the double layer capacitance (Q dl ) of the coatings were obtained from the equivalent circuit. Multilayer coatings showed higher R pore and R ct values as compared to the single layer coatings. Similarly, the Q coat and Q dl values decreased from uncoated substrate to the multilayer coatings, indicating a decrease in the defect density by the addition of EN interlayer. These studies were confirmed by examining the corroded samples under

  20. Rutile TiO2 thin films grown by reactive high power impulse magnetron sputtering

    International Nuclear Information System (INIS)

    Agnarsson, B.; Magnus, F.; Tryggvason, T.K.; Ingason, A.S.; Leosson, K.; Olafsson, S.; Gudmundsson, J.T.

    2013-01-01

    Thin TiO 2 films were grown on Si(001) substrates by reactive dc magnetron sputtering (dcMS) and high power impulse magnetron sputtering (HiPIMS) at temperatures ranging from 300 to 700 °C. Optical and structural properties of films were compared both before and after post-annealing using scanning electron microscopy, low angle X-ray reflection (XRR), grazing incidence X-ray diffractometry and spectroscopic ellipsometry. Both dcMS- and HiPIMS-grown films reveal polycrystalline rutile TiO 2 , even prior to post-annealing. The HiPIMS-grown films exhibit significantly larger grains compared to that of dcMC-grown films, approaching 100% of the film thickness for films grown at 700 °C. In addition, the XRR surface roughness of HiPIMS-grown films was significantly lower than that of dcMS-grown films over the whole temperature range 300–700 °C. Dispersion curves could only be obtained for the HiPIMS-grown films, which were shown to have a refractive index in the range of 2.7–2.85 at 500 nm. The results show that thin, rutile TiO 2 films, with high refractive index, can be obtained by HiPIMS at relatively low growth temperatures, without post-annealing. Furthermore, these films are smoother and show better optical characteristics than their dcMS-grown counterparts. - Highlights: • We demonstrate growth of rutile TiO 2 on Si (111) by high power impulse magnetron sputtering. • The films exhibit significantly larger grains than dc magnetron sputtered films • TiO 2 films with high refractive index are obtained without post-growth annealing

  1. Crystalline silicon films grown by pulsed dc magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Reinig, Peter; Fenske, Frank; Fuhs, Walther; Selle, Burkhardt [Hahn-Meitner-Institut Berlin, Abt. Silizium-Photovoltaik, Kekulestr. 5, D-12489 Berlin (Germany)

    2002-04-01

    Pulsed dc magnetron sputtering is used as a novel method for the deposition of crystalline silicon films on glass substrates. Hydrogen-free polycrystalline Si-films are deposited with high deposition rates at temperatures of 400-450 C and pulse frequencies f in the range 0-250 kHz. Strong preferential (100) orientation of the crystallites is observed with increasing f. High frequency and similarly high negative substrate bias cause an increase of the Ar content and an enhancement of structural disorder. Measurements of the transient floating potential suggest that the observed structural effects are related to bombardment of the growing film by Ar{sup +} ions of high energy.

  2. RF Reactive Magnetron Sputter Deposition of Silicon Sub-Oxides

    NARCIS (Netherlands)

    Hattum, E.D. van

    2007-01-01

    RF reactive magnetron plasma sputter deposition of silicon sub oxide E.D. van Hattum Department of Physics and Astronomy, Faculty of Sciences, Utrecht University The work described in the thesis has been inspired and stimulated by the use of SiOx layers in the direct inductive printing technology,

  3. DC Magnetron Sputtered IZTO Thin Films for Organic Photovoltaic Application.

    Science.gov (United States)

    Lee, Hye Ji; Noviyana, Imas; Putri, Maryane; Koo, Chang Young; Lee, Jung-A; Kim, Jeong-Joo; Jeong, Youngjun; Lee, Youngu; Lee, Hee Young

    2018-02-01

    IZTO20 (In0.6Zn0.2Sn0.2O1.5) ceramic target was prepared from oxide mixture of In2O3, ZnO, and SnO2 powders. IZTO20 thin films were then deposited onto glass substrate at 400 °C by DC magnetron sputtering. The average optical transmittance determined by ultraviolet-visible spectroscopy was higher than 85% for all films. The minimum resistivity of the annealed IZTO20 thin film was approximately 6.1×10-4 Ω·cm, which tended to increase with decreasing indium content. Substrate heating and annealing were found to be important parameters affecting the electrical and optical properties. An organic photovoltaic (OPV) cell was fabricated using the IZTO20 film deposited under the optimized condition as an anode electrode and the efficiency of up to 80% compared to that of a similar OPV cell using ITO film was observed. Reduction of surface roughness and electrical resistivity through annealing treatment was found to contribute to the improved efficiency of the OPV cell.

  4. Growth and characterization of a-axis oriented Cr-doped AlN films by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Panda, Padmalochan; Ramaseshan, R., E-mail: seshan@igcar.gov.in; Dash, S. [Materials Science Group, IGCAR, Kalpakkam, 603102 (India); Krishna, Nanda Gopala [Corrosion Science and Technology Group, IGCAR, Kalpakkam, 603102 (India)

    2016-05-23

    Wurtzite type Cr-doped AlN thin films were grown on Si (100) substrates using DC reactive magnetron sputtering with a function of N{sub 2} concentration (15 to 25%). Evolution of crystal structure of these films was studied by GIXRD where a-axis preferred orientation was observed. The electronic binding energy and concentration of Cr in these films were estimated by X-ray photoemission spectroscopy (XPS). We have observed indentation hardness (H{sub IT}) of around 28.2 GPa for a nitrogen concentration of 25%.

  5. Controlled formation of anatase and rutile TiO2 thin films by reactive magnetron sputtering

    OpenAIRE

    Rafieian, Damon; Ogieglo, Wojciech; Savenije, T.J.; Lammertink, Rob G H

    2015-01-01

    We discuss the formation of TiO2 thin films via DC reactive magnetron sputtering. The oxygen concentration during sputtering proved to be a crucial parameter with respect to the final film structure and properties. The initial deposition provided amorphous films that crystallise upon annealing to anatase or rutile, depending on the initial sputtering conditions. Substoichiometric films (TiOx), obtained by sputtering at relatively low oxygen concentration, formed rutile upon annealing in air, ...

  6. Structural and thermal properties of nanocrystalline CuO synthesized by reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Verma, M. [Department of Chemistry, IIT Roorkee, Roorkee-247667, India and Nano Science Laboratory, Institute Instrumentation Centre, IIT Roorkee, Roorkee-247667 (India); Gupta, V. K. [Department of Chemistry, IIT Roorkee, Roorkee-247667 (India); Gautam, Y. K.; Dave, V.; Chandra, R. [Nano Science Laboratory, Institute Instrumentation Centre, IIT Roorkee, Roorkee-247667 (India)

    2014-01-28

    Recent research has shown immense application of metal oxides like CuO, MgO, CaO, Al{sub 2}O{sub 3}, etc. in different areas which includes chemical warfare agents, medical drugs, magnetic storage media and solar energy transformation. Among the metal oxides, CuO nanoparticles are of special interest because of their excellent gas sensing and catalytic properties. In this paper we report structural and thermal properties of CuO synthesized by reactive magnetron DC sputtering. The synthesized nanoparticles were characterized by X-ray diffractometer. The XRD result reveals that as DC power increased from 30W to 80W, size of the CuO nanoparticles increased. The same results have been verified through TEM analysis. Thermal properties of these particles were studied using thermogravimetry.

  7. Giant Negative Piezoresistive Effect in Diamond-like Carbon and Diamond-like Carbon-Based Nickel Nanocomposite Films Deposited by Reactive Magnetron Sputtering of Ni Target

    DEFF Research Database (Denmark)

    Meškinis, Šaru Nas; Gudaitis, Rimantas; Šlapikas, Kęstutis

    2018-01-01

    deposited by either reactive HIPIMS or dc magnetron sputtering of Ni target was explained by possible clustering of the sp2-bonded carbon and/or formation of areas with the decreased hydrogen content. It was suggested that the tensile stress-induced rearrangements of these conglomerations have resulted......Piezoresistive properties of hydrogenated diamond-like carbon (DLC) and DLC-based nickel nanocomposite (DLC:Ni) films were studied in the range of low concentration of nickel nanoparticles. The films were deposited by reactive high power pulsed magnetron sputtering (HIPIMS) of Ni target, and some...... samples were deposited by direct current (dc) reactive magnetron sputtering for comparison purposes. Raman scattering spectroscopy, energy-dispersive X-ray spectrometry (EDS), and X-ray photoelectron spectroscopy (XPS) were used to study the structure and chemical composition of the films. A four...

  8. Reactive magnetron sputtering model at making Ti-TiOx coatings

    International Nuclear Information System (INIS)

    Luchkin, A G; Kashapov, N F

    2014-01-01

    Mathematical model of reactive magnetron sputtering for plant VU 700-D is described. Approximating curves for experimental current-voltage characteristic for two gas input schemas are shown. Choice of gas input schema influences on model parameters (mainly on pumping speed). Reactive magnetron sputtering model allows develop technology of Ti - TiO x coatings deposition without changing atmosphere and pressure in vacuum chamber

  9. A novel DC Magnetron sputtering facility for space research and synchrotron radiation optics

    DEFF Research Database (Denmark)

    Hussain, A.M.; Christensen, Finn Erland; Pareschi, G.

    1998-01-01

    A new DC magnetron sputtering facility has been build up at the Danish Space Research Institute (DSRI), specially designed to enable uniform coatings of large area curved optics, such as Wolter-I mirror optics used in space telescopes and curved optics used in synchrotron radiation facilities...

  10. Corrosion resistance of CrN thin films produced by dc magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Ruden, A. [Laboratorio de Física del Plasma, Universidad Nacional de Colombia Sede Manizales, Km. 9 vía al Magdalena, Manizales (Colombia); Laboratorio de Recubrimientos Duros y Aplicaciones Industriales–RDAI, Universidad del Valle, Calle 13 N° 100-00 Ciudadela Meléndez, Cali (Colombia); Departamento de matemáticas, Universidad Tecnológica de Pereira, Pereira (Colombia); Restrepo-Parra, E., E-mail: erestrepopa@unal.edu.co [Laboratorio de Física del Plasma, Universidad Nacional de Colombia Sede Manizales, Km. 9 vía al Magdalena, Manizales (Colombia); Paladines, A.U.; Sequeda, F. [Laboratorio de Recubrimientos Duros y Aplicaciones Industriales–RDAI, Universidad del Valle, Calle 13 N° 100-00 Ciudadela Meléndez, Cali (Colombia)

    2013-04-01

    In this study, the electrochemical behavior of chromium nitride (CrN) coatings deposited on two steel substrates, AISI 304 and AISI 1440, was investigated. The CrN coatings were prepared using a reactive d.c. magnetron sputtering deposition technique at two different pressures (P1 = 0.4 Pa and P2 = 4 Pa) with a mixture of N{sub 2}–Ar (1.5-10). The microstructure and crystallinity of the CrN coatings were investigated using X-ray diffraction. The aqueous corrosion behavior of the coatings was evaluated using two methods. The polarization resistance (Tafel curves) and electrochemical impedance spectra (EIS) in a saline (3.5% NaCl solution) environment were measured in terms of the open-circuit potentials and polarization resistance (R{sub p}). The results indicated that the CrN coatings present better corrosion resistance and R{sub p} values than do the uncoated steel substrates, especially for the coatings produced on the AISI 304 substrates, which exhibited a strong enhancement in the corrosion resistance. Furthermore, better behavior was observed for the coatings produced at lower pressures (0.4 Pa) than those grown at 4 Pa.

  11. Controlled formation of anatase and rutile TiO2 thin films by reactive magnetron sputtering

    Directory of Open Access Journals (Sweden)

    Damon Rafieian

    2015-09-01

    Full Text Available We discuss the formation of TiO2 thin films via DC reactive magnetron sputtering. The oxygen concentration during sputtering proved to be a crucial parameter with respect to the final film structure and properties. The initial deposition provided amorphous films that crystallise upon annealing to anatase or rutile, depending on the initial sputtering conditions. Substoichiometric films (TiOx<2, obtained by sputtering at relatively low oxygen concentration, formed rutile upon annealing in air, whereas stoichiometric films formed anatase. This route therefore presents a formation route for rutile films via lower (<500 °C temperature pathways. The dynamics of the annealing process were followed by in situ ellipsometry, showing the optical properties transformation. The final crystal structures were identified by XRD. The anatase film obtained by this deposition method displayed high carriers mobility as measured by time-resolved microwave conductance. This also confirms the high photocatalytic activity of the anatase films.

  12. Studies on the reactive deposition of TiN{sub x} and TiO{sub x} in a DC magnetron plasma; Untersuchungen zur reaktiven Abscheidung von TiN{sub x} und TiO{sub x} in einem DC-Magnetronplasma

    Energy Technology Data Exchange (ETDEWEB)

    Wrehde, Stefan

    2009-10-30

    In the present thesis experiments in a magnetron coating plasma on the (reactive) deposition of Ti, Ti{sub x}, and TiO{sub x} layers were performed. The aim was to meet by correlation of measurements of the ion and energy current on the substrate during the coating procedure with studies of the properties of the deposed layers statements about the connections of deposition conditions and layer properties. The layers deposed in the argon plasma without reactive gas contained beside titanium as main component also small concentrations of oxygen in the range of 8..15%, no completely pure respectively metallic titanium layers could be deposed. In the layers deposed in the argon-nitrogen plasma the increasing nitrogen admixture to the plasma leads mto an increasing nitridation of the layers. The measurements of the crystal structure show higher macroscopical stresses in the layers deposed in the unbalanced mode. From the combination of the higher thicknesses and densities of the layers deposed in the unbalanced mode in this operation mode of the magnetron higher deposition rates result. In the argon-oxygen plasma at increasing oxygen part it comes to a distinct increasement of the oxygen concentration at simultaneous decreasement of the relative titanium concentration in the deposed layers. The deposition in the unbalanced mode leads against the that in the balanced mode to a slightly lower oxygen concentration in the layers. The measurements of the crystal structure show also a lower oxygen insertion and tendentially lower macroscopical stresses in the layers deposed in the unbalanced mode. The measured densities of the layers deposed in the unbalanced mode are distinctly lower than to be expected, and above all smaller than those of the layers deposed in the balanced mode.

  13. Investigation of photocatalytic activity of titanium dioxide deposited on metallic substrates by DC magnetron sputtering

    DEFF Research Database (Denmark)

    Daviðsdóttir, Svava; Canulescu, Stela; Dirscherl, Kai

    2013-01-01

    The photocatalytic properties of titanium dioxide (TiO2) coating in the anatase crystalline structure deposited on aluminium AA1050 alloy and stainless steel S316L substrates were investigated. The coating was prepared by DC magnetron sputtering. The microstructure and surface morphology of the c......The photocatalytic properties of titanium dioxide (TiO2) coating in the anatase crystalline structure deposited on aluminium AA1050 alloy and stainless steel S316L substrates were investigated. The coating was prepared by DC magnetron sputtering. The microstructure and surface morphology...... sweep voltammetry, impedance measurements. The microstructure and surface morphology of the coating were similar irrespective of the nature of the substrate, while the photocatalytic behaviour was found to vary depending on the substrate type. In general the TiO2 coating on stainless steel was shown...

  14. Fine control of the amount of preferential <001> orientation in DC magnetron sputtered nanocrystalline TiO2 films

    International Nuclear Information System (INIS)

    Stefanov, B; Granqvist, C G; Österlund, L

    2014-01-01

    Different crystal facets of anatase TiO 2 are known to have different chemical reactivity; in particular the {001} facets which truncates the bi-tetrahedral anatase morphology are reported to be more reactive than the usually dominant {101} facets. Anatase TiO 2 thin films were deposited by reactive DC magnetron sputtering in Ar/O 2 atmosphere and were characterized using Rietveld refined grazing incidence X-ray diffraction, atomic force microscopy and UV/Vis spectroscopy. By varying the partial O2 pressure in the deposition chamber, the degree of orientation of the grains in the film could be systematically varied with preferred <001> orientation changing from random upto 39% as determined by March-Dollase method. The orientation of the films is shown to correlate with their reactivity, as measured by photo-degradation of methylene blue in water solutions. The results have implications for fabrication of purposefully chemically reactive thin TiO 2 films prepared by sputtering methods

  15. Effect of target power on the physical properties of Ti thin films prepared by DC magnetron sputtering with supported discharge

    Directory of Open Access Journals (Sweden)

    Kavitha A.

    2017-02-01

    Full Text Available The present paper describes the effect of target power on the properties of Ti thin films prepared by DC magnetron sputtering with (triode mode and without (diode mode supported discharge. The traditional diode magnetron sputtering with an addition of a hot filament has been used to sustain the discharge at a lower pressure. The effect of target power (60, 80, 100 and 120 W on the physical properties of Ti thin films has been studied in diode and triode modes. XRD studies showed that the Ti thin films prepared at a target power up to 100 W in diode mode were amorphous in nature. The Ti thin films exhibited crystalline structure at much lower target power of 80 W with a preferred orientation along (0 0 2 plane. The grain size of Ti thin films prepared in triode mode increased from 64 nm to 80 nm, whereas in diode mode, the grain size increased from 2 nm to 5 nm. EDAX analysis confirmed that the incorporation of reactive gases was lower in triode mode compared to diode mode. The electrical resistivity of Ti thin films deposited in diode mode was found to be 85 µΩ⋅cm (target power 120 W. The electrical resistivity of Ti thin films in triode mode was found to be deceased to 15.2 µΩ⋅cm (target power 120 W.

  16. Initial growth and texture formation during reactive magnetron sputtering of TiN on Si(111)

    CERN Document Server

    Li, T Q; Tsuji, Y; Ohsawa, T; Komiyama, H

    2002-01-01

    The initial growth and texture formation mechanism of titanium nitride (TiN) films were investigated by depositing TiN films on (111) silicon substrates by using reactive magnetron sputtering of a Ti metallic target under a N sub 2 /Ar atmosphere, and then analyzing the films in detail by using transmission electron microscopy (TEM) and x-ray diffraction (XRD). Two power sources for the sputtering, dc and rf, were compared. At the initial growth stage, a continuous amorphous film containing randomly oriented nuclei was observed when the film thickness was about 3 nm. The nuclei grew and formed a polycrystalline layer when the film thickness was about 6 nm. As the film grew further, its orientation changed depending on the deposition conditions. For dc sputtering, the appearance of (111) or (200)-preferred orientations depended on the N sub 2 partial pressure, and the intensity of the preferred orientation increased with increasing film thickness. For rf sputtering, however, when the film thickness was small (...

  17. Reactive magnetron sputtering deposition of bismuth tungstate onto titania nanoparticles for enhancing visible light photocatalytic activity

    Energy Technology Data Exchange (ETDEWEB)

    Ratova, Marina, E-mail: marina_ratova@hotmail.com [Surface Engineering Group, School of Engineering, Manchester Metropolitan University, Manchester, M1 5GD (United Kingdom); Kelly, Peter J.; West, Glen T. [Surface Engineering Group, School of Engineering, Manchester Metropolitan University, Manchester, M1 5GD (United Kingdom); Tosheva, Lubomira; Edge, Michele [School of Science and the Environment, Manchester Metropolitan University, Manchester M1 5GD (United Kingdom)

    2017-01-15

    Highlights: • Bismuth tungstate coatings were deposited by reactive magnetron sputtering. • Oscillating bowl was introduced to the system to enable coating of nanopartulates. • Deposition of Bi{sub 2}WO{sub 6} enhanced visible light activity of titania nanoparticles. • The best results were obtained for coating with Bi:W ratio of approximately 2:1. • Deposition of Bi{sub 2}WO{sub 6} onto TiO{sub 2} resulted in more efficient electron-hole separation. - Abstract: Titanium dioxide − bismuth tungstate composite materials were prepared by pulsed DC reactive magnetron sputtering of bismuth and tungsten metallic targets in argon/oxygen atmosphere onto anatase and rutile titania nanoparticles. The use of an oscillating bowl placed beneath the two magnetrons arranged in a co-planar closed field configuration enabled the deposition of bismuth tungstate onto loose powders, rather than a solid substrate. The atomic ratio of the bismuth/tungsten coatings was controlled by varying the power applied to each target. The effect of the bismuth tungstate coatings on the phase, optical and photocatalytic properties of titania was investigated by X-ray diffraction, energy-dispersive X-ray spectroscopy (EDX), Brunauer–Emmett–Teller (BET) surface area measurements, transmission electron microscopy (TEM), UV–vis diffuse reflectance spectroscopy and an acetone degradation test. The latter involved measurements of the rate of CO{sub 2} evolution under visible light irradiation of the photocatalysts, which indicated that the deposition of bismuth tungstate resulted in a significant enhancement of visible light activity, for both anatase and rutile titania particles. The best results were achieved for coatings with a bismuth to tungsten atomic ratio of 2:1. In addition, the mechanism by which the photocatalytic activity of the TiO{sub 2} nanoparticles was enhanced by compounding it with bismuth tungstate was studied by microwave cavity perturbation. The results of these

  18. DC Magnetron sputtering of Y-Ba-Cu-O thin films

    International Nuclear Information System (INIS)

    Larsson, Gunnar.

    1990-01-01

    I have been studying dc magnetron sputtering of thin film YBa 2 Cu 3 O 6+x , one of the recently discovered high- temperatures superconductors. In the introduction a brief review of the subjects sputtering and superconductivity is given. Since partial pressure measurements, especially for oxygen, have been important in the work I include a short description of the operating principles of mass spectroscopy. Experimental results in addition to what is given in the papers concerning plasma are presented in an appendix at the end of the introduction. (au)

  19. A study of the plasma electronegativity in an argon-oxygen pulsed-dc sputter magnetron

    International Nuclear Information System (INIS)

    You, S D; Dodd, R; Edwards, A; Bradley, J W

    2010-01-01

    Using Langmuir probe-assisted laser photodetachment, the temporal evolution of the O - density was determined in the bulk plasma of a unipolar pulsed-dc magnetron. The source was operated in reactive mode, at a fixed nominal on-time power of 100 W, sputtering Ti in argon-oxygen atmospheres at 1.3 Pa pressure, but over a variation of duty cycles from 5% to 50% and oxygen partial pressures of 10% and 50% of the total pressure. In the plasma on-time, for all duty cycles the negative ion density (n - ) rises marginally reaching values typically less than 2 x 10 15 m -3 with negative ion-to-electron density ratios, α - falls by about 20-30% as fast O - species created at the cathode exit the system. This is followed by a rapid rise in n - to values at least 2 or 3 times that in the on-time. The rate of rise of n - and its maximum value both increase with decreasing duty cycle. In the off-time, the electron density falls rapidly (initial decay rates of several tens of μs), and therefore the afterglow plasma becomes highly electronegative, with α reaching 4.6 and 14.4 for 10% and 50% oxygen partial pressure, respectively. The rapid rise in n - in the afterglow (in which the electron temperature falls from about 5 to 0.5 eV) is attributed to the dissociative attachment of highly excited oxygen metastables, which themselves are created in the pulse on-time. At the lowest duty of 5%, the long-term O - decay times are several hundred μs. Langmuir probe characteristics show the clear signature that negative ions dominate over the electrons in the off-time. From the ion and electron saturation current ratios, α has been estimated in some chosen cases and found to agree within a factor between 2 and 10 with those obtained more directly from the photodetachment method.

  20. Reactive magnetron sputtering of N-doped carbon thin films on quartz glass for transmission photocathode applications

    Science.gov (United States)

    Balalykin, N. I.; Huran, J.; Nozdrin, M. A.; Feshchenko, A. A.; Kobzev, A. P.; Sasinková, V.; Boháček, P.; Arbet, J.

    2018-03-01

    N-doped carbon thin films were deposited on a silicon substrate and quartz glass by RF reactive magnetron sputtering using a carbon target and an Ar+N2 gas mixture. During the magnetron sputtering, the substrate holder temperatures was kept at 800 °C. The carbon film thickness on the silicon substrate was about 70 nm, while on the quartz glass it was in the range 15 nm – 60 nm. The elemental concentration in the films was determined by RBS and ERD. Raman spectroscopy was used to evaluate the intensity ratios I D/I G of the D and G peaks of the carbon films. The transmission photocathodes prepared were placed in the hollow-cathode assembly of a Pierce-structure DC gun to produce photoelectrons. The quantum efficiency (QE) was calculated from the laser energy and cathode charge measured. The properties of the transmission photocathodes based on semitransparent N-doped carbon thin films on quartz glass and their potential for application in DC gun technology are discussed.

  1. Rotating dust ring in an RF discharge coupled with a dc-magnetron sputter source. Experiment and simulation

    International Nuclear Information System (INIS)

    Matyash, K; Froehlich, M; Kersten, H; Thieme, G; Schneider, R; Hannemann, M; Hippler, R

    2004-01-01

    During an experiment involving coating of dust grains trapped in an RF discharge using a sputtering dc-magnetron source, a rotating dust ring was observed and investigated. After the magnetron was switched on, the dust cloud levitating above the RF electrode formed a ring rotating as a rigid body. Langmuir probe diagnostics were used for the measurement of plasma density and potential. It was discovered that the coupling of the dc-magnetron source to the RF discharge causes steep radial gradients in electron density and plasma potential. The rotation of the dust ring is attributed to the azimuthal component of the ion drag force, which appears due to the azimuthal drift of the ions caused by crossed radial electric and axial magnetic fields. In order to get more insight into the mechanism of dust ring rotation, a Particle-in-Cell simulation of a rotating dust cloud was performed. The results of the experiment and simulation are presented and discussed

  2. Rotating dust ring in an RF discharge coupled with a dc-magnetron sputter source. Experiment and simulation

    Energy Technology Data Exchange (ETDEWEB)

    Matyash, K [Institut fuer Niedertemperaturplasmaphysik Greifswald, Fr.-L.-Jahn-Strasse 19, 17489 Greifswald (Germany); Froehlich, M [Institut fuer Physik, Ernst-Moritz-Arndt-Universitaet Greifswald, Domstrasse 10a, 17487 Greifswald (Germany); Kersten, H [Institut fuer Niedertemperaturplasmaphysik Greifswald, Fr.-L.-Jahn-Strasse 19, 17489 Greifswald (Germany); Thieme, G [Institut fuer Physik, Ernst-Moritz-Arndt-Universitaet Greifswald, Domstrasse 10a, 17487 Greifswald (Germany); Schneider, R [Max-Planck-Institut fuer Plasmaphysik, Teilinstitut Greifswald, Wendelsteinstrasse 1, 17489 Greifswald (Germany); Hannemann, M [Institut fuer Niedertemperaturplasmaphysik Greifswald, Fr.-L.-Jahn-Strasse 19, 17489 Greifswald (Germany); Hippler, R [Institut fuer Physik, Ernst-Moritz-Arndt-Universitaet Greifswald, Domstrasse 10a, 17487 Greifswald (Germany)

    2004-10-07

    During an experiment involving coating of dust grains trapped in an RF discharge using a sputtering dc-magnetron source, a rotating dust ring was observed and investigated. After the magnetron was switched on, the dust cloud levitating above the RF electrode formed a ring rotating as a rigid body. Langmuir probe diagnostics were used for the measurement of plasma density and potential. It was discovered that the coupling of the dc-magnetron source to the RF discharge causes steep radial gradients in electron density and plasma potential. The rotation of the dust ring is attributed to the azimuthal component of the ion drag force, which appears due to the azimuthal drift of the ions caused by crossed radial electric and axial magnetic fields. In order to get more insight into the mechanism of dust ring rotation, a Particle-in-Cell simulation of a rotating dust cloud was performed. The results of the experiment and simulation are presented and discussed.

  3. Deposition of Al/Cu Multilayer By Double Targets Cylindrical DC Magnetron Sputtering System

    Directory of Open Access Journals (Sweden)

    P. Balashabadi

    2013-12-01

    Full Text Available A cylindrical direct current magnetron sputtering coater with two targets for deposition of multilayer thin films and cermet solar selective surfaces has been constructed. The substrate holder was able to rotate around the target for obtaining the uniform layer and separated multilayer phases. The Al/ Cu multilayer film was deposited on the glass substrate at the following conditions: Working gas = Pure argon, Working pressure = 1 Pa, Cathode current = 8 A and cathode voltage = -600 V .Microstructure of the film was investigated by X-Ray Diffraction and the scanning electron microscopy analyses. The elements profile was determined by glow discharge–optical emission spectroscopy analysis. During deposition, both targets with magnetron configuration were sputtered simultaneously by argon ions. A Plasma column on the targets surface was generated by a 290 G permanent magnet unit. Two DC power supply units with three phases input and maximum output of 12 A/1000V were used to deposit the multilayer thin films. A control phase system was used to adjust output voltage.

  4. Effects of Annealing on TiN Thin Film Growth by DC Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Azadeh Jafari

    2014-07-01

    Full Text Available We have reviewed the deposition of titanium nitride (TiN thin films on stainless steel substrates by a DC magnetron sputtering method and annealing at different annealing temperatures of 500, 600, and 700°C for 120 min in nitrogen/argon atmospheres. Effects of annealing temperatures on the structural and the optical properties of TiN films were investigated using X-ray diffraction (XRD, atomic force microscope (AFM, field emission scanning electron microscopy (FESEM, and UV-VIS spectrophotometer. Our experimental studies reveal that the annealing temperature appreciably affected the structures, crystallite sizes, and reflection of the films. By increasing the annealing temperature to 700°C crystallinity and reflection of the film increase. These results suggest that annealed TiN films can be good candidate for tokamak first wall due to their structural and optical properties.

  5. Synthesis and characterization of DC magnetron sputtered nano structured molybdenum thin films

    Energy Technology Data Exchange (ETDEWEB)

    Rondiya, S. R.; Rokade, A. V.; Jadhavar, A. A.; Pandharkar, S. M.; Kulkarni, R. R.; Karpe, S. D.; Diwate, K. D. [School of Energy Studies, Savitribai Phule Pune University, Pune 411007 (India); Jadkar, S. R., E-mail: sandesh@physics.unipune.ac.in [Department of Physics, Savitribai Phule Pune University, Pune 411007 (India)

    2016-04-13

    Molybdenum (Mo) thin films were deposited on corning glass (#7059) substrates using DC magnetron sputtering system. The effect of substrate temperature on the structural, morphology and topological properties have been investigated. Films were characterized by variety of techniques such as low angle x-ray diffraction (low angle XRD), field emission scanning electron microscopy (FE-SEM), atomic force microscopy (AFM). The low angle XRD analysis revealed that the synthesized Mo films are nanocrystalline having cubic crystal structure with (110) preferential orientation. The microstructure of the deposited Mo thin films observed with FE-SEM images indicated that films are homogeneous and uniform with randomly oriented leaf shape morphology. The AFM analysis shows that with increase in substrate temperature the rms roughness of Mo films increases. The obtained results suggest that the synthesized nanostructured Mo thin films have potential application as a back contact material for high efficiency solar cells like CdTe, CIGS, CZTS etc.

  6. Effect of interelectrode distance on dc magnetron current-pressure characteristics

    Science.gov (United States)

    Mankelevich, Yu A.; Pal, A. F.; Ryabinkin, A. N.; Serov, A. O.

    2018-01-01

    The current-pressure (I-P) non-monotonic characteristic in the magnetron discharge dc in argon at different interelectrode distances was investigated. The ion spatial distribution was obtained with optical emission spectroscopy and the characteristic dimensions of the discharge structure in near cathode region were determined. It is shown that decreasing the distance between electrodes does not affect the shape and position of the nonmonotonic part of I-P characteristic until this distance become comparable with the dimensions of the ionization region near cathode. The existence of non-monotonic part of I-P characteristic is determined by the processes in the near cathode region and is probably unrelated with the cold electron transfer in the rest of the plasma.

  7. AlN/Al dual protective coatings on NdFeB by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Li Jinlong; Mao Shoudong; Sun Kefei [Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China); Li Xiaomin [Shanghai Institute of Ceramics Chinese Academy of Sciences, Shanghai 200050 (China); Song Zhenlun [Zhejiang Province Key Laboratory of Magnetic Materials and Application Technology, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201 (China)], E-mail: songzhenlun@nimte.ac.cn

    2009-11-15

    AlN/Al dual protective coatings were prepared on NdFeB by DC magnetron sputtering in a home-made industrial apparatus. Comparing with Al coating, AlN/Al coatings have a denser structure of an outmost AlN amorphous layer following an inner Al columnar crystal layer. The coatings and NdFeB substrate combine well, and moreover, there is occurrence of metallurgy bonding in the interface layer. Both Al and AlN/Al coatings have a good protective ability to NdFeB. Especially, the corrosion resistance of AlN/Al coated NdFeB is improved largely. AlN/Al and Al protective coatings not only do not deteriorate the magnetic properties of NdFeB, but contribute to their slight increase.

  8. AlN/Al dual protective coatings on NdFeB by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Li Jinlong; Mao Shoudong; Sun Kefei; Li Xiaomin; Song Zhenlun

    2009-01-01

    AlN/Al dual protective coatings were prepared on NdFeB by DC magnetron sputtering in a home-made industrial apparatus. Comparing with Al coating, AlN/Al coatings have a denser structure of an outmost AlN amorphous layer following an inner Al columnar crystal layer. The coatings and NdFeB substrate combine well, and moreover, there is occurrence of metallurgy bonding in the interface layer. Both Al and AlN/Al coatings have a good protective ability to NdFeB. Especially, the corrosion resistance of AlN/Al coated NdFeB is improved largely. AlN/Al and Al protective coatings not only do not deteriorate the magnetic properties of NdFeB, but contribute to their slight increase.

  9. Operational limit of a planar DC magnetron cluster source due to target erosion

    International Nuclear Information System (INIS)

    Rai, A.; Mutzke, A.; Bandelow, G.; Schneider, R.; Ganeva, M.; Pipa, A.V.; Hippler, R.

    2013-01-01

    The binary collision-based two dimensional SDTrimSP-2D model has been used to simulate the erosion process of a Cu target and its influence on the operational limit of a planar DC magnetron nanocluster source. The density of free metal atoms in the aggregation region influences the cluster formation and cluster intensity during the target lifetime. The density of the free metal atoms in the aggregation region can only be predicted by taking into account (i) the angular distribution of the sputtered flux from the primary target source and (ii) relative downwards shift of the primary source of sputtered atoms during the erosion process. It is shown that the flux of the sputtered atoms smoothly decreases with the target erosion

  10. DC magnetron sputtering prepared Ag-C thin film anode for thin film lithium ion microbatteries

    International Nuclear Information System (INIS)

    Li, Y.; Tu, J.P.; Shi, D.Q.; Huang, X.H.; Wu, H.M.; Yuan, Y.F.; Zhao, X.B.

    2007-01-01

    An Ag-C thin film was prepared by DC magnetron co-sputtering, using pure silver and graphite as the targets. The microstructure and morphology of the deposited thin film were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). Electrochemical performances of the Ag-C thin film anode were investigated by means of discharge/charge and cyclic voltammogram (CV) tests in model cells. The electrochemical impedance spectrum (EIS) characteristics and the chemical diffusion coefficient, D Li of the Ag-C thin film electrode at different discharging states were discussed. It was believed that the excellent cycling performance of the Ag-C electrode was ascribed to the good conductivity of silver and the volume stability of the thin film

  11. Synthesis and characterization of DC magnetron sputtered ZnO thin films under high working pressures

    International Nuclear Information System (INIS)

    Hezam, M.; Tabet, N.; Mekki, A.

    2010-01-01

    ZnO thin films were deposited on glass substrates using direct current (dc) magnetron sputtering under high working pressures. A pure zinc target was used, and sputtering was carried out in an oxygen atmosphere. The working pressure was varied between 50 and 800 mTorr. XRD characterization showed that for a window of working pressures between 300 and 500 mTorr, the deposited films were polycrystalline, with strong preferential orientation of grains along the c-axis. The film deposited at 400 mTorr had the highest (002) peak with the largest estimated grain size. Outside this window, the crystallinity and c-orientation of grains are lost. The microstructure of the films was investigated by Atomic Force microscopy (AFM). Optical transparency of the films was about 85%. The films produced were highly resistive, which might provide new alternatives for the synthesis of ZnO thin films aimed for SAW devices.

  12. Effect of sputtering power on structure and properties of Bi film deposited by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Liao Guo; He Zhibing; Xu Hua; Li Jun; Chen Taihua; Chen Jiajun

    2012-01-01

    Bi film was fabricated at different sputtering powers by DC magnetron sputtering. The deposition rate of Bi film as the function of sputtering power was studied. The surface topography of Bi film was observed by SEM, and the growth mode of Bi film was investigated. The crystal structure was analyzed by XRD. The grain size and stress of Bi film were calculated. The SEM images show that all the films are columnar growth. The average grain size firstly increases as the sputtering power increases, then decreases at 60 W. The film becomes loose with the increase of sputtering power, while, the film gets compact when the sputtering power becomes from 45 to 60 W. The XRD results show that films are polycrystalline of hexagonal. And the stress transforms from the tensile stress to compressive stress as the sputtering power increases. (authors)

  13. Structural and optical properties of zirconia thin films deposited by reactive high-power impulse magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Xiaoli; Jin, Jie [Tianjin University, School of Electronic Information Engineering, Tianjin (China); Cheng, Jui-Ching, E-mail: juiching@ntut.edu.tw [Chang-Gung University, Department of Electronics, Taoyuan, Taiwan (China); Lee, Jyh-Wei [Ming Chi University of Technology, College of Materials Engineering, New Taipei City, Taiwan (China); Wu, Kuo-Hong [Chang-Gung University, Department of Electronics, Taoyuan, Taiwan (China); Lin, Kuo-Cheng; Tsai, Jung-Ruey [Asia University, Department of Photonics and Communication Engineering, Taichung, Taiwan (China); Liu, Kou-Chen, E-mail: jacobliu@mail.cgu.edu.tw [Chang-Gung University, Department of Electronics, Taoyuan, Taiwan (China)

    2014-11-03

    Zirconia films are deposited by reactive high power impulse magnetron sputtering (HiPIMS) technology on glass and indium-tin-oxide (ITO)/glass substrates. Preparation, microstructure and optical characteristics of the films have been studied. During deposition, the influence of the target power and duty cycle on the peak current–voltage and power density has been observed in oxide mode. Transparent thin films under different oxygen proportions are obtained on the two substrates. Atomic force microscopy measurements showed that the surface roughness of the films was lower by reactive HiPIMS than DC sputtering for all oxygen contents. The transmission and reflectance properties of differently grown zirconia films were also investigated using an ultraviolet–visible spectrophotometer. The optical transmittance of films grown on glass substrates by HiPIMS reached maximum values above 90%, which exceeded that by DC sputtering. The band edge near 5.86 eV shifted to a lower wavelength for zirconia films prepared with oxygen flow rates lower than 4.5 sccm. For the films prepared on ITO/glass substrates, the transmittance and the band gap of zirconia films were limited by ITO films; a maximum average transmittance of 84% was obtained at 4.5 sccm O{sub 2} and the energy band gap was in the range of 3.7–3.8 eV for oxygen flow rates ranging from 3.5 to 5.0 sccm. Finally, the electrical properties of zirconia films have also been discussed. - Highlights: • Zirconia films are deposited by reactive high power impulse magnetron sputtering. • Low roughness films are obtained. • Films show a high transmittance (> 90%). • Films prepared on glass have a band gap of 5.9 eV.

  14. Low-cost ZnO:Al transparent contact by reactive rotatable magnetron sputtering for Cu(In,Ga)Se2 solar modules

    International Nuclear Information System (INIS)

    Menner, R.; Hariskos, D.; Linss, V.; Powalla, M.

    2011-01-01

    Sputtering ZnO as transparent front contact (TCO) is standard in today's industrial scale Cu(In,Ga)Se 2 (CIGS) module manufacturing. Although innovative concepts like rotatable magnetron sputtering from ceramic targets have been realised, costs are still high due to expensive ceramic targets. Significant cost reductions are expected by using reactive sputtering of metallic targets. Therefore, ZSW and industrial partners investigated the reactive sputtering of Al-doped zinc oxide (ZAO) as TCO on CIGS absorbers of high quality and industrial relevance. The reactive DC sputtering from rotatable magnetron targets is controlled in the transition mode by adjusting oxygen flow and discharge voltage. Optimisation leads to ZAO films with a TCO quality nearly comparable to standard films deposited by DC ceramic sputtering. Scanning electron microscopy, X-ray diffraction, and Hall analyses of the ZAO films are performed. Medium-size CIGS modules are coated with reactively sputtered ZAO, resulting in 12.8% module efficiency and surpassing the efficiency of the ceramic witness device. Cd-free buffered devices are also successfully coated with reactive TCO. Damp heat stability according to IEC61646 is met by all reactively sputtered devices.

  15. Zn{sub x}Zr{sub y}O{sub z} thin films grown by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Sanchez, O. [Instituto de Ciencia de Materiales de Madrid (CSIC), Madrid (Spain); Hernandez-Velez, M. [Departamento de Fisica Aplicada, Universidad Autonoma de Madrid (Spain)

    2017-10-15

    The structural and optical properties of thin films deposited by DC reactive magnetron co-sputtering using Zn and Zr targets in argon and oxygen gas mixtures at room temperature are reported. The power applied to the Zr cathode was kept constant, while that applied to the Zn cathode was varied between 0 and 150 W to produce very different Zn{sub x}Zr{sub y}O{sub z} ternary compounds with Zn/Zr atomic ratios in the range of 0.1-10. The composition, crystalline structure, and optical properties of the samples were determined by EDX, XRD, FTIR, and UV-visible spectroscopies. The grown films are polycrystalline, and the preferred crystallographic orientation depends on the Zn atomic concentration in the film. The optical transmission in the UV-visible range is approximately 80% in all cases, and as the Zn atomic content increases, the absorption edge shifts to longer wavelengths. The optical band gap, E{sub g}, shifted from 5.5 to 3.5 eV when the Zn/Zr atomic ratio was increased. The results indicate the potential use of these materials in optoelectronic applications. (copyright 2017 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  16. Texture of the nano-crystalline AlN thin films and the growth conditions in DC magnetron sputtering

    Directory of Open Access Journals (Sweden)

    Shakil Khan

    2015-08-01

    Full Text Available DC reactive magnetron sputtering technique has been used for the preparation of AlN thin films. The deposition temperature and the flow ratio of N2/Ar were varied and subsequent dependency of the films crystallites orientation/texture has been addressed. In general, deposited films were found hexagonal polycrystalline with a (002 preferred orientation. The X-ray diffraction (XRD data revealed that the film crystallinity improves, with the increase of substrate temperature from 300 °C to 500 °C. The dropped in full width half maximum (FWHM of the XRD rocking curve value further confirmed it. However, increasing substrate temperature above 500 °C or reducing the nitrogen condition (from 60 to 30% in the environment induced the growth of crystallites with (102 and (103 orientations. The rise of rocking curve FWHM for the corresponding conditions depicted that the films texture quality deteriorated. A further confirmation of the variation in film texture/orentation with the growth conditions has been obtained from the variation in FWHM values of a dominant E1 (TO mode in the Fourier transform infrared (FTIR spectra and the E2 (high mode in Raman spectra. We have correlated the columnar structure in AFM surface analyses with the (002 or c-axis orientation as well. Spectroscopic ellipsometry of the samples have shown a higher refractive index at 500 °C growth temperature.

  17. Characterization of DC magnetron plasma in Ar/Kr/N2 mixture during deposition of (Cr,Al)N coating

    International Nuclear Information System (INIS)

    Bobzin, K; Bagcivan, N; Theiß, S; Brugnara, R; Bibinov, N; Awakowicz, P

    2017-01-01

    Reactive sputter deposition of (Cr,Al)N coatings in DC magnetron plasmas containing Ar/Kr/N 2 mixtures is characterized by applying a combination of voltage–current measurement, optical emission spectroscopy (OES) and numerical simulation. Theoretical and experimental methods supplement each other and their combination permits us to obtain the most reliable information about the processes by physical vapor deposition. Gas temperature ( T g ) and plasma parameters, namely electron density n e and electron temperature T e are determined by spatial resolved measurements of molecular nitrogen photoemission. Steady-state densities of Cr and Al atoms are measured using OES. The sputtering of Cr and Al atoms is simulated using the TRIDYN code, measured electric current and applied voltage. Transport of sputtered atoms through the plasma volume is simulated by adopting a Monte-Carlo code. In order to quantify the ‘poisoning’ of the target surface with nitrogen, simulated steady state densities of Al and Cr atoms at different states of poisoning and at different distances from the target are compared with the measured densities. In addition, simulated fluxes of Cr and Al atoms to the substrate are compared with the measured deposition rates of the (Cr,Al)N coating. (paper)

  18. Experimental investigation of plasma dynamics in dc and short-pulse magnetron discharges

    International Nuclear Information System (INIS)

    Seo, Sang-Hun; In, Jung-Hwan; Chang, Hong-Young

    2006-01-01

    The spatiotemporal evolution of the electron energy distribution function (EEDF) and of plasma parameters such as the electron density, the electron temperature and the plasma and floating potentials has been investigated using spatially and temporally resolved single Langmuir probe measurements in dc and mid-frequency, short-pulse magnetron discharges with a repetition frequency of 10 kHz and a duty cycle of 10%. In the pulsed discharge of the short duty cycle, a peak electron temperature higher than 10 eV was observed near the cathode fall region during the early phase of the pulse-on, which is about three times higher than the steady-state value of the electron temperature in the dc discharge. The temporal evolution of the measured EEDFs showed the initial efficient electron heating during the early phase of the pulse-on and the subsequent relaxation of electron energy by the inelastic collisions and the diffusive loss. The high-energy electrons generated during the pulse-on phase diffused the downstream region toward the grounded substrate, resulting in a bi-Maxwellian EEDF consisting of the background low-energy electrons and the high-energy electrons. The results of the spatially and temporally resolved probe measurements will be presented and the enhanced efficiency of the electron heating in the short-pulse discharge will be explained on the basis of the global model of a pulsed discharge

  19. Surface treatment effect on Si (111) substrate for carbon deposition using DC unbalanced magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Aji, A. S., E-mail: aji.ravazes70@gmail.com; Sahdan, M. F.; Hendra, I. B.; Dinari, P.; Darma, Y. [Quantum Semiconductor and Devices Lab., Physics of Material Electronics Research Division, Department of Physics, Institut Teknologi Bandung (Indonesia)

    2015-04-16

    In this work, we studied the effect of HF treatment in silicon (111) substrate surface for depositing thin layer carbon. We performed the deposition of carbon by using DC Unbalanced Magnetron Sputtering with carbon pallet (5% Fe) as target. From SEM characterization results it can be concluded that the carbon layer on HF treated substrate is more uniform than on substrate without treated. Carbon deposition rate is higher as confirmed by AFM results if the silicon substrate is treated by HF solution. EDAX characterization results tell that silicon (111) substrate with HF treatment have more carbon fraction than substrate without treatment. These results confirmed that HF treatment on silicon Si (111) substrates could enhance the carbon deposition by using DC sputtering. Afterward, the carbon atomic arrangement on silicon (111) surface is studied by performing thermal annealing process to 900 °C. From Raman spectroscopy results, thin film carbon is not changing until 600 °C thermal budged. But, when temperature increase to 900 °C, thin film carbon is starting to diffuse to silicon (111) substrates.

  20. Influence of Continuous and Discontinuous Depositions on Properties of Ito Films Prepared by DC Magnetron Sputtering

    Science.gov (United States)

    Aiempanakit, K.; Rakkwamsuk, P.; Dumrongrattana, S.

    Indium tin oxide (ITO) films were deposited on glass substrate without external heating by DC magnetron sputtering with continuous deposition of 800 s (S1) and discontinuous depositions of 400 s × 2 times (S2), 200 s × 4 times (S3) and 100 s × 8 times (S4). The structural, surface morphology, optical transmittance and electrical resistivity of ITO films were measured by X-ray diffraction, atomic force microscope, spectrophotometer and four-point probe, respectively. The deposition process of the S1 condition shows the highest target voltage due to more target poisoning occurrence. The substrate temperature of the S1 condition increases with the saturation curve of the RC charging circuit while other conditions increase and decrease due to deposition steps as DC power turns on and off. Target voltage and substrate temperature of ITO films decrease when changing the deposition conditions from S1 to S2, S3 and S4, respectively. The preferential orientation of ITO films were changed from dominate (222) plane to (400) plane with the increasing number of deposition steps. The ITO film for the S4 condition shows the lowest electrical resistivity of 1.44 × 10-3 Ω·cm with the highest energy gap of 4.09 eV and the highest surface roughness of 3.43 nm. These results were discussed from the point of different oxygen occurring on the surface ITO target between the sputtering processes which affected the properties of ITO films.

  1. A study of the transient plasma potential in a pulsed bi-polar dc magnetron discharge

    International Nuclear Information System (INIS)

    Bradley, J W; Karkari, S K; Vetushka, A

    2004-01-01

    The temporal evolution of the plasma potential, V p , in a pulsed dc magnetron plasma has been determined using the emissive probe technique. The discharge was operated in the 'asymmetric bi-polar' mode, in which the discharge voltage changes polarity during part of the pulse cycle. The probe measurements, with a time-resolution of 20 ns or better, were made along a line above the racetrack, normal to the plane of the cathode target, for a fixed frequency (100 kHz), duty cycle (50%), argon pressure (0.74 Pa) and discharge power (583 W). At all the measured positions, V p was found to respond to the large and rapid changes in the cathode voltage, V d , during the different phases of the pulse cycle, with V p always more positive than V d . At a typical substrate position (>80 mm from the target), V p remains a few volts above the most positive surface in the discharge at all times. In the 'on' phase of the pulse, the measurements show a significant axial electric field is generated in the plasma, with the plasma potential dropping by a total of about 30 V over a distance of 70 mm, from the bulk plasma to a position close to the beginning of the cathode fall. This is consistent with measurements made in the dc magnetron. During the stable 'reverse' phase of the discharge, for distances greater than 18 mm from the target, the axial electric field is found to collapse, with V p elevated uniformly to about 3 V above V d . Between the target and this field-free region an ion sheath forms, and the current flowing to the target is still an ion current in this 'reverse' period. During the initial 200 ns of the voltage 'overshoot' phase (between 'on' and 'reverse' phases), V d reached a potential of +290 V; however, close to the target, V p was found to attain a much higher value, namely +378 V. Along the line of measurement, the axial electric field reverses in direction in this phase, and an electron current of up to 9 A flows to the target. The spatial and temporal

  2. Effect of N{sub 2} flow rate on the properties of N doped TiO{sub 2} films deposited by DC coupled RF magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Peng, Shou [State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, Wuhan 430000 (China); State Key Laboratory of Advanced Technology for Float Glass, Bengbu Design & Research Institute for Glass Industry, Bengbu 233000 (China); Yang, Yong, E-mail: 88087113@163.com [State Key Laboratory of Advanced Technology for Float Glass, Bengbu Design & Research Institute for Glass Industry, Bengbu 233000 (China); Li, Gang; Jiang, Jiwen; Jin, Kewu; Yao, TingTing; Zhang, Kuanxiang [State Key Laboratory of Advanced Technology for Float Glass, Bengbu Design & Research Institute for Glass Industry, Bengbu 233000 (China); Cao, Xin [State Key Laboratory of Advanced Technology for Float Glass, Bengbu Design & Research Institute for Glass Industry, Bengbu 233000 (China); School of Materials Science and Engineering, Dalian Jiaotong University, Dalian 116000 (China); Wang, Yun; Xu, Genbao [State Key Laboratory of Advanced Technology for Float Glass, Bengbu Design & Research Institute for Glass Industry, Bengbu 233000 (China)

    2016-09-05

    N doped TiO{sub 2} films were deposited on glass substrates at room temperature using DC coupled RF magnetron sputtering with a TiO{sub 2} ceramic target. The influences of N{sub 2} flow rate on the deposition rate, crystal structure, chemical composition and band gap of the deposited films were investigated by Optical profiler, X-ray diffraction, X-ray photoelectron spectroscope and ultraviolet-visible spectrophotometer. The film growth rate gradually decreased with increasing N{sub 2} flow rate. As N{sub 2} flow rate increased, the crystallization of the films deteriorated, and the films tended to form amorphous structure. XPS analysis revealed that N dopant atoms were added at the substitutional sites into TiO{sub 2} lattice structure. FE-SEM results showed that the grain size of the film decreased and the crystallinity degraded as N{sub 2} flow rate increases. In addition, N doping caused an obvious red shift in the optical absorption edge. - Highlights: • N doped TiO{sub 2} films were deposited by DC coupled RF magnetron reactive sputtering. • As N{sub 2} flow rate increases, the crystallization of the deposited films degrades. • The higher N{sub 2} flow rate is beneficial to form more substituted N in the film. • N doping causes an obvious red shift in the absorption wavelength.

  3. Effect of N_2 flow rate on the properties of N doped TiO_2 films deposited by DC coupled RF magnetron sputtering

    International Nuclear Information System (INIS)

    Peng, Shou; Yang, Yong; Li, Gang; Jiang, Jiwen; Jin, Kewu; Yao, TingTing; Zhang, Kuanxiang; Cao, Xin; Wang, Yun; Xu, Genbao

    2016-01-01

    N doped TiO_2 films were deposited on glass substrates at room temperature using DC coupled RF magnetron sputtering with a TiO_2 ceramic target. The influences of N_2 flow rate on the deposition rate, crystal structure, chemical composition and band gap of the deposited films were investigated by Optical profiler, X-ray diffraction, X-ray photoelectron spectroscope and ultraviolet-visible spectrophotometer. The film growth rate gradually decreased with increasing N_2 flow rate. As N_2 flow rate increased, the crystallization of the films deteriorated, and the films tended to form amorphous structure. XPS analysis revealed that N dopant atoms were added at the substitutional sites into TiO_2 lattice structure. FE-SEM results showed that the grain size of the film decreased and the crystallinity degraded as N_2 flow rate increases. In addition, N doping caused an obvious red shift in the optical absorption edge. - Highlights: • N doped TiO_2 films were deposited by DC coupled RF magnetron reactive sputtering. • As N_2 flow rate increases, the crystallization of the deposited films degrades. • The higher N_2 flow rate is beneficial to form more substituted N in the film. • N doping causes an obvious red shift in the absorption wavelength.

  4. Electrical resistivity of CuAlMo thin films grown at room temperature by dc magnetron sputtering

    OpenAIRE

    Birkett, Martin; Penlington, Roger

    2016-01-01

    We report on the thickness dependence of electrical resistivity of CuAlMo films grown by dc magnetron sputtering on glass substrates at room temperature. The electrical resistance of the films was monitored in situ during their growth in the thickness range 10–1000 nm. By theoretically modelling the evolution of resistivity during growth we were able to gain an insight into the dominant electrical conduction mechanisms with increasing film thickness. For thicknesses in the range 10–25 nm the ...

  5. Properties of Ce-doped ITO films deposited on polymer substrate by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Kang, Y.M.; Kwon, S.H.; Choi, J.H.; Cho, Y.J.; Song, P.K.

    2010-01-01

    Ce-doped indium tin oxide (ITO:Ce) films were deposited on flexible polyimide substrates by DC magnetron sputtering using ITO targets containing various CeO 2 contents (CeO 2 : 0, 0.5, 3.0, 4.0, 6.0 wt.%) at room temperature and post-annealed at 200 o C. The crystallinity of the ITO films decreased with increasing Ce content, and it led to a decrease in surface roughness. In addition, a relatively small change in resistance in dynamic stress mode was obtained for ITO:Ce films even after the annealing at high temperature (200 o C). The minimum resistivity of the amorphous ITO:Ce films was 3.96 x 10 -4 Ωcm, which was deposited using a 3.0 wt.% CeO 2 doped ITO target. The amorphous ITO:Ce films not only have comparable electrical properties to the polycrystalline films but also have a crystallization temperature > 200 o C. In addition, the amorphous ITO:Ce film showed stable mechanical properties in the bended state.

  6. Structure evolution of zinc oxide thin films deposited by unbalance DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Aryanto, Didik, E-mail: didi027@lipi.go.id [Research Center for Physics, Indonesian Institute of Sciences, Serpong 15314, Tangerang Selatan (Indonesia); Materials Research Group, Physics Department, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia); Marwoto, Putut; Sugianto [Physics Department, Faculty of Mathematics and Science, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia); Materials Research Group, Physics Department, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia); Sudiro, Toto [Research Center for Physics, Indonesian Institute of Sciences, Serpong 15314, Tangerang Selatan (Indonesia); Birowosuto, Muhammad D. [Research Center for Physics, Indonesian Institute of Sciences, Serpong 15314, Tangerang Selatan (Indonesia); CINTRA UMI CNRS/NTU/THALES 3288 Research Techno Plaza, 50 Nanyang Drive, Border X Block, level 6, 637553 (Singapore); Sulhadi [Physics Department, Faculty of Mathematics and Science, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia)

    2016-04-19

    Zinc oxide (ZnO) thin films are deposited on corning glass substrates using unbalanced DC magnetron sputtering. The effect of growth temperature on surface morphology and crystallographic orientation of ZnO thin film is studied using atomic force microscopy (AFM) and X-ray diffraction (XRD) techniques. The surface morphology and crystallographic orientation of ZnO thin film are transformed against the increasing of growth temperature. The mean grain size of film and the surface roughness are inversely and directly proportional towards the growth temperature from room temperature to 300 °C, respectively. The smaller grain size and finer roughness of ZnO thin film are obtained at growth temperature of 400 °C. The result of AFM analysis is in good agreement with the result of XRD analysis. ZnO thin films deposited in a series of growth temperatures have hexagonal wurtzite polycrystalline structures and they exhibit transformations in the crystallographic orientation. The results in this study reveal that the growth temperature strongly influences the surface morphology and crystallographic orientation of ZnO thin film.

  7. Study on helium-charged titanium films deposited by DC-magnetron sputtering

    International Nuclear Information System (INIS)

    Shi Liqun; Jin Qinhua; Liu Chaozhuo; Xu Shilin; Zhou Zhuying

    2005-01-01

    Helium trapping in the Ti films deposited by DC magnetron sputtering with a He/Ar mixture was studied. He atoms with a surprisingly high concentration (He/Ti atomic ratio is as high as 56%) incorporate evenly in deposited film. The trapped amount of He can be controlled by the helium partial amount. The introduction of the helium with no extra damage (or very low damage) can be realized by choosing suitable deposition conditions. It was also found that because of the formation of nanophase Ti film a relative high He flux for bubble formation is needed and the amount of the retaining He in sputtering Ti films is much higher than that in the coarse-grain Ti films. The nanophase Ti film can accommodate larger concentration of trapped sites to He, which results in a high density and small size of the He bubbles. With increasing He irradiation flux, the grain size of Ti film decreases and the lattice spacing and width of the X-ray diffraction peak increase due to the He introduction, and the film tends to amorphous phase. (authors)

  8. Room temperature growth of nanocrystalline anatase TiO2 thin films by dc magnetron sputtering

    International Nuclear Information System (INIS)

    Singh, Preetam; Kaur, Davinder

    2010-01-01

    We report, the structural and optical properties of nanocrystalline anatase TiO 2 thin films grown on glass substrate by dc magnetron sputtering at room temperature. The influence of sputtering power and pressure over crystallinity and surface morphology of the films were investigated. It was observed that increase in sputtering power activates the TiO 2 film growth from relative lower surface free energy to higher surface free energy. XRD pattern revealed the change in preferred orientation from (1 0 1) to (0 0 4) with increase in sputtering power, which is accounted for different surface energy associated with different planes. Microstructure of the films also changes from cauliflower type to columnar type structures with increase in sputtering power. FESEM images of films grown at low pressure and low sputtering power showed typical cauliflower like structure. The optical measurement revealed the systematic variation of the optical constants with deposition parameters. The films are highly transparent with transmission higher than 90% with sharp ultraviolet cut off. The transmittance of these films was found to be influenced by the surface roughness and film thickness. The optical band gap was found to decrease with increase in the sputtering power and pressure. The refractive index of the films was found to vary in the range of 2.50-2.24 with increase in sputtering pressure or sputtering power, resulting in the possibility of producing TiO 2 films for device applications with different refractive index, by changing the deposition parameters.

  9. Low friction coefficient coatings Ni-Cr by magnetron sputtering, DC

    Energy Technology Data Exchange (ETDEWEB)

    Morales-Hernandez, J.; Mandujano-Ruiz, A.; Torres-Gonzalez, J.; Espinosa-Beltran, F. J.; Herrera-Hernandez, H.

    2015-07-01

    Magnetron Sputter Deposition technique with DC was used for the deposition of Ni-Cr coatings on AISI 316 SS like substrate. The cathode with a nominal composition Ni-22 at% Cr was prepared by Mechanical Alloying (MA) technique, with a maximum milling time of 16 hours and, with a high energy SPEX 8000 mill. The coatings were made under Argon atmosphere at room temperature with a power of 100 W at different times of growth. Chemical composition, microstructure, topography, nano hardness and wear of the coatings were evaluated using the techniques of microanalysis by energy dispersive X-ray analyzer (EDAX), X-Ray Diffraction (XRD), Atomic Force Microscopy (AFM), Nano-indentation and pin-on-Disk, respectively. After milling, was not detected contamination in the mixtures. XRD analysis revealed that the microstructure of the Ni-Cr alloy was maintained in the coatings with respect to MA powders, with some degree of recrystallization. Nano hardness values were in the order of 8.8 GPa with a Youngs modulus of 195 GPa. The adhesion of the films was evaluated according to their resistance to fracture when these were indented at different loads using Vickers microhardness. The wear test results showed a decrease in the friction coefficient with respect to the increase of thickness films, getting a minimum value of 0.08 with a thickness of 1 μm and which correspond with the maximum growing time. (Author)

  10. Transparent conducting Al-doped ZnO thin films prepared by magnetron sputtering with dc and rf powers applied in combination

    International Nuclear Information System (INIS)

    Minami, Tadatsugu; Ohtani, Yuusuke; Miyata, Toshihiro; Kuboi, Takeshi

    2007-01-01

    A newly developed Al-doped ZnO (AZO) thin-film magnetron-sputtering deposition technique that decreases resistivity, improves resistivity distribution, and produces high-rate depositions has been demonstrated by dc magnetron-sputtering depositions that incorporate rf power (dc+rf-MS), either with or without the introduction of H 2 gas into the deposition chamber. The dc+rf-MS preparations were carried out in a pure Ar or an Ar+H 2 (0%-2%) gas atmosphere at a pressure of 0.4 Pa by adding a rf component (13.56 MHz) to a constant dc power of 80 W. The deposition rate in a dc+rf-MS deposition incorporating a rf power of 150 W was approximately 62 nm/min, an increase from the approximately 35 nm/min observed in dc magnetron sputtering with a dc power of 80 W. A resistivity as low as 3x10 -4 Ω cm and an improved resistivity distribution could be obtained in AZO thin films deposited on substrates at a low temperature of 150 deg. C by dc+rf-MS with the introduction of hydrogen gas with a content of 1.5%. This article describes the effects of adding a rf power component (i.e., dc+rf-MS deposition) as well as introducing H 2 gas into dc magnetron-sputtering preparations of transparent conducting AZO thin films

  11. Low friction coefficient coatings Ni-Cr by magnetron sputtering, DC

    Directory of Open Access Journals (Sweden)

    Morales-Hernández, Jorge

    2015-09-01

    Full Text Available Magnetron Sputter Deposition technique with DC was used for the deposition of Ni-Cr coatings on AISI 316 SS like substrate. The cathode with a nominal composition Ni-22 at% Cr was prepared by Mechanical Alloying (MA technique, with a maximum milling time of 16 hours and, with a high energy SPEX 8000 mill. The coatings were made under Argon atmosphere at room temperature with a power of 100 W at different times of growth. Chemical composition, microstructure, topography, nanohardness and wear of the coatings were evaluated using the techniques of microanalysis by energy dispersive X-ray analyzer (EDAX, X-Ray Diffraction (XRD, Atomic Force Microscopy (AFM, Nano-indentation and pin-on-Disk, respectively. After milling, was not detected contamination in the mixtures. XRD analysis revealed that the microstructure of the Ni-Cr alloy was maintained in the coatings with respect to MA powders, with some degree of recrystallization. Nanohardness values were in the order of 8.8 GPa with a Young’s modulus of 195 GPa. The adhesion of the films was evaluated according to their resistance to fracture when these were indented at different loads using Vickers microhardness. The wear test results showed a decrease in the friction coefficient with respect to the increase of thickness’ films, getting a minimum value of 0.08 with a thickness of 1 μm and which correspond with the maximum growing time.La técnica de Deposición por Chisporroteo Magnético (Magnetron Sputtering con el proceso DC, fue usado para la deposición de los recubrimientos de Ni-Cr sobre acero inoxidable AISI 316 como sustrato. El cátodo con una composición nominal Ni-22 at% Cr fue preparado por la técnica de Aleado Mecánico (AM, con un tiempo máximo de molienda de 16 horas y con un molino de alta energía tipo SPEX 8000. Las películas se realizaron bajo una atmósfera de argón a temperatura ambiente con una potencia de 100 W a diferentes tiempos de crecimiento. La composición qu

  12. Oxidation resistance of CrN/(Cr,V)N hard coatings deposited by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Panjan, P., E-mail: peter.panjan@ijs.si [Jožef Stefan Institute, Jamova 39, 1000 Ljubljana (Slovenia); Drnovšek, A.; Kovač, J.; Gselman, P. [Jožef Stefan Institute, Jamova 39, 1000 Ljubljana (Slovenia); Bončina, T. [University of Maribor, Faculty of Mechanical Engineering, Smetanova 17, 2000 Maribor (Slovenia); Paskvale, S.; Čekada, M.; Kek Merl, D.; Panjan, M. [Jožef Stefan Institute, Jamova 39, 1000 Ljubljana (Slovenia)

    2015-09-30

    In recent years vanadium-doped hard coatings have become available as possible candidates for self-lubrication at high temperatures. Their low coefficient of friction has mainly been attributed to the formation of the V{sub 2}O{sub 5} phase. However, the formation of vanadium oxides must be controlled by the out-diffusion of vanadium in order to achieve the combination of a low coefficient of friction and good mechanical properties for the protective coatings. In this work the application of a nanolayer of CrN/(Cr,V)N hard coating was proposed as a way to better control the out-diffusion of vanadium, while the topmost chromium oxide layer acts as barrier for the vanadium diffusion. However, the aim of this investigation was not only to focus on the formation of the oxide layer. Special attention was given to the oxidation process that takes place at the growth defects, where we observed a strong diffusion of vanadium taking place. The CrN/(Cr,V)N nanolayer coatings were deposited by DC unbalanced magnetron sputtering in an CC800/9 (CemeCon) industrial unit. The vanadium concentration in the (Cr,V)N layers was varied in the range 1.0–11.5 at.%. - Highlights: • Oxidation processes of CrN/(Cr,V)N nanolayers with vanadium content were investigated. • The CrN/(Cr,V)N hard layers were oxidized at high temperature in O2 atm. • The top chromium oxide layer acts as a diffusion barrier for vanadium ions during oxidation. • Important role of growth defects during the oxidation process is demonstrated.

  13. Oxidation resistance of CrN/(Cr,V)N hard coatings deposited by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Panjan, P.; Drnovšek, A.; Kovač, J.; Gselman, P.; Bončina, T.; Paskvale, S.; Čekada, M.; Kek Merl, D.; Panjan, M.

    2015-01-01

    In recent years vanadium-doped hard coatings have become available as possible candidates for self-lubrication at high temperatures. Their low coefficient of friction has mainly been attributed to the formation of the V_2O_5 phase. However, the formation of vanadium oxides must be controlled by the out-diffusion of vanadium in order to achieve the combination of a low coefficient of friction and good mechanical properties for the protective coatings. In this work the application of a nanolayer of CrN/(Cr,V)N hard coating was proposed as a way to better control the out-diffusion of vanadium, while the topmost chromium oxide layer acts as barrier for the vanadium diffusion. However, the aim of this investigation was not only to focus on the formation of the oxide layer. Special attention was given to the oxidation process that takes place at the growth defects, where we observed a strong diffusion of vanadium taking place. The CrN/(Cr,V)N nanolayer coatings were deposited by DC unbalanced magnetron sputtering in an CC800/9 (CemeCon) industrial unit. The vanadium concentration in the (Cr,V)N layers was varied in the range 1.0–11.5 at.%. - Highlights: • Oxidation processes of CrN/(Cr,V)N nanolayers with vanadium content were investigated. • The CrN/(Cr,V)N hard layers were oxidized at high temperature in O2 atm. • The top chromium oxide layer acts as a diffusion barrier for vanadium ions during oxidation. • Important role of growth defects during the oxidation process is demonstrated.

  14. Post-deposition annealing effects in RF reactive magnetron sputtered indium tin oxide thin films

    Energy Technology Data Exchange (ETDEWEB)

    Martinez, M A; Herrero, J; Gutierrez, M T [Inst. de Energias Renovables (CIEMAT), Madrid (Spain)

    1992-05-01

    Indium tin oxide films have been grown by RF reactive magnetron sputtering. The influence of the deposition parameters on the properties of the films has been investigated and optimized, obtaining a value for the figure of merit of 6700 ({Omega} cm){sup -1}. As-grown indium tin oxide films were annealed in vacuum and O{sub 2} atmosphere. After these heat treatments the electro-optical properties were improved, with values for the resistivity of 1.9x10{sup -4} {Omega} cm and the figure of merit of 26700 ({Omega} cm){sup -1}. (orig.).

  15. Effect of deposition parameters on properties of ITO films prepared by reactive middle frequency pulsed dual magnetron sputtering

    International Nuclear Information System (INIS)

    Rogozin, A.I.; Vinnichenko, M.V.; Kolitsch, A.; Moeller, W.

    2004-01-01

    ITO layers with low resistivity and high visible transmittance were produced by means of middle frequency reactive dual magnetron sputtering. The influence of base pressure, Ar/O 2 ratio and magnetron pulse duration on the film composition, structure, electrical, and optical properties has been investigated. The deposition rate is proportional to the magnetron operation power at changing pulse duration and constant Ar and O 2 flows. At enhanced O 2 flows an onset of the magnetron target oxidation is discussed as a reason for the decrease of the deposition rate. The presence of water vapor in the residual gas is determined to be a reason for deterioration of resistivity and optical transmittance observed for ITO films produced at a base pressures higher than 5·10 -4 Pa. It is demonstrated that spectroscopic ellipsometry can be used as a noncontact tool to monitor the resistivity of ITO films

  16. Urea impedimetric biosensor based on reactive RF magnetron sputtered zinc oxide nanoporous transducer

    International Nuclear Information System (INIS)

    Mozaffari, Sayed Ahmad; Rahmanian, Reza; Abedi, Mohammad; Amoli, Hossein Salar

    2014-01-01

    Graphical abstract: - Highlights: • Application and optimization of reactive RF magnetron sputtering for homogeneous nanoporous ZnO thin film formation. • Exploiting nanoporous ZnO thin film as a good porous framework with large surface area/volume for having stable immobilized enzyme with minimum loss of activity. • Application of impedimetric assessment for urea biosensing due to its rapidity, sensitivity, and repeatability. - Abstract: Uniform sputtered nanoporous zinc oxide (Nano-ZnO) thin film on the conductive fluorinated-tin oxide (FTO) layer was applied to immobilize urease enzyme (Urs) for urea detection. Highly uniform nanoporous ZnO thin film were obtained by reactive radio frequency (RF) magnetron sputtering system at the optimized instrumental deposition conditions. Characterization of the surface morphology and roughness of ZnO thin film by field emission-scanning electron microscopy (FE-SEM) exhibits cavities of nanoporous film as an effective biosensing area for enzyme immobilization. Step by step monitoring of FTO/Nano-ZnO/Urs biosensor fabrication were performed using electrochemical methods such as cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) techniques. Fabricated FTO/Nano-ZnO/Urs biosensor was used for urea determination using EIS experiments. The impedimetric results show high sensitivity for urea detection within 0.83–23.24 mM and limit of detection as 0.40 mM

  17. Control of the optical properties of silicon and chromium mixed oxides deposited by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Vergara, L.; Galindo, R. Escobar; Martinez, R.; Sanchez, O.; Palacio, C.; Albella, J.M.

    2011-01-01

    The development of mixed-oxide thin films allows obtaining materials with better properties than those of the different binary oxides, which makes them suitable for a great number of applications in different fields, such as tribology, optics or microelectronics. In this paper we investigate the deposition of mixed chromium and silicon oxides deposited by reactive magnetron sputtering with a view to use them as optical coatings with an adjustable refractive index. These films have been characterized by means of Rutherford backscattering spectrometry, Auger electron spectroscopy, X-ray diffraction, scanning electron microscopy, Fourier-transform infrared spectroscopy and spectroscopic ellipsometry so as to determine how the deposition conditions influence the characteristics of the material. We have found that the deposition parameter whose influence determines the properties of the films to a greater extent is the amount of oxygen in the reactive sputtering gas.

  18. Fabrication of thin ZnO films with wide-range tuned optical properties by reactive magnetron sputtering

    Science.gov (United States)

    Davydova, A.; Tselikov, G.; Dilone, D.; Rao, K. V.; Kabashin, A. V.; Belova, L.

    2018-02-01

    We report the manufacturing of thin zinc oxide films by reactive magnetron sputtering at room temperature, and examine their structural and optical properties. We show that the partial oxygen pressure in DC mode can have dramatic effect on absorption and refractive index (RI) of the films in a broad spectral range. In particular, the change of the oxygen pressure from 7% to 5% can lead to either conventional crystalline ZnO films having low absorption and characteristic descending dependence of RI from 2.4-2.7 RIU in the visible to 1.8-2 RIU in the near-infrared (1600 nm) range, or to untypical films, composed of ZnO nano-crystals embedded into amorphous matrix, exhibiting unexpectedly high absorption in the visible-infrared region and ascending dependence of RI with values varying from 1.5 RIU in the visible to 4 RIU in the IR (1600 nm), respectively. Untypical optical characteristics in the second case are explained by defects in ZnO structure arising due to under-oxidation of ZnO crystals. We also show that the observed defect-related film structure remains stable even after annealing of films under relatively high temperatures (30 min under 450 °C). We assume that both types of films can be of importance for photovoltaic (as contact or active layers, respectively), as well as for chemical or biological sensing, optoelectronics etc.

  19. Effects of oxygen contents on the electrochromic properties of tungsten oxide films prepared by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Lu, H.-H.

    2008-01-01

    The electrochromism have been extensively investigated due to their potential applications such as smart window of architecture and automobile glazing to save energy and modulate the transmittance of light and solar radiation. The objective of this study is to investigate the effects of sputtering conditions on the microstructure and electrochromic properties of tungsten oxide films prepared by dc reactive magnetron sputtering. Experimental results showed that the deposition rate of WO 3-y films decreased with increasing oxygen flow rate. XRD and Raman spectra analysis suggests that the WO 3-y films deposited at various oxygen flow rates are poor crystallinity or amorphous. The transmission change between colored and bleached states at a wavelength of 550 nm was 61.4% as the oxygen content was 60%. The coloration efficiency slightly increases with increasing oxygen flow rate in the low oxygen content region and reaching a maximum value of 38.94 cm 2 /C at 60% oxygen content. In addition, the films deposited at 60% oxygen content showed a good reversibility. The effects of lithium ions intercalated on the transmission of WO 3-y films were also discussed

  20. Study of sterilization-treatment in pure and N- doped carbon thin films synthesized by inductively coupled plasma assisted pulsed-DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Javid, Amjed [Center for Advanced Plasma Surface Technology (CAPST), NU-SKKU Joint Institute for Plasma Nano-Materials (IPNM), Advanced Materials Science and Engineering, Sungkyunkwan University, Suwon 440-746 (Korea, Republic of); Department of Textile Processing, National Textile University, Faisalabad 37610 (Pakistan); Kumar, Manish, E-mail: manishk@skku.edu [Center for Advanced Plasma Surface Technology (CAPST), NU-SKKU Joint Institute for Plasma Nano-Materials (IPNM), Advanced Materials Science and Engineering, Sungkyunkwan University, Suwon 440-746 (Korea, Republic of); Han, Jeon Geon, E-mail: hanjg@skku.edu [Center for Advanced Plasma Surface Technology (CAPST), NU-SKKU Joint Institute for Plasma Nano-Materials (IPNM), Advanced Materials Science and Engineering, Sungkyunkwan University, Suwon 440-746 (Korea, Republic of)

    2017-01-15

    Highlights: • Pure and N-doped nanocrystallie carbon films are synthesized by ICP assisted pulsed DC plasma process. • ICP power induces the increase in average graphitic crystallite size from 4.86 nm to 6.42 nm. • Beneficial role of ICP source assistance to achieve high sputtering throughput (deposition rate ∼55 nm/min). • Post-sterilization electron-transport study shows N-doped carbon films having promising stability. - Abstract: Electrically-conductive nanocrystalline carbon films, having non-toxic and non-immunogenic characteristics, are promising candidates for reusable medical devices. Here, the pure and N- doped nanocrystalline carbon films are deposited by the assistance of inductively coupled plasma (ICP) in an unbalanced facing target pulsed-DC magnetron sputtering process. Through the optical emission spectroscopy study, the role of ICP assistance and N-doping on the reactive components/radicals during the synthesis is presented. The N-doping enhances the three fold bonding configurations by increasing the ionization and energies of the plasma species. Whereas, the ICP addition increases the plasma density to control the deposition rate and film structure. As a result, sputtering-throughput (deposition rate: 31–55 nm/min), electrical resistivity (4–72 Ωcm) and water contact angle (45.12°–54°) are significantly tailored. Electric transport study across the surface microchannel confirms the superiority of N-doped carbon films for sterilization stability over the undoped carbon films.

  1. Deposition and characterization of ZrMoN thin films by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Fontes Junir, A.S.; Felix, L.C.; Oliveira, G.B. de; Fernandez, D.R.; Carvalho, R.G.; Tentardini, E.K.; Silva Junior, A.H. da

    2016-01-01

    Thin films of ZrMoN were deposited by magnetron reactive sputtering technique in order to study the molybdenum influence on the mechanical properties and oxidation resistance of these coatings. Three thin films with molybdenum concentrations from 25 to 40 at.% were selected. The displacement of characteristic peaks of ZrN where identified by GIXRD results of films with larger Mo content. This result is indicative of the Mo accommodation in the lattice structure. Hardness tests revealed favorable results with values up to 33 GPa. Oxidation tests showed that ZrN oxidized at 500 °C with a monoclinic ZrO 2 and tetragonal formation; whereas the thin films with Mo addition impeded the formation of the monoclinic ZrO 2 phase at partial oxidation. (author)

  2. Distribution of Fe atom density in a dc magnetron sputtering plasma source measured by laser-induced fluorescence imaging spectroscopy

    Science.gov (United States)

    Shibagaki, K.; Nafarizal, N.; Sasaki, K.; Toyoda, H.; Iwata, S.; Kato, T.; Tsunashima, S.; Sugai, H.

    2003-10-01

    Magnetron sputtering discharge is widely used as an efficient method for thin film fabrication. In order to achieve the optimized fabrication, understanding of the kinetics in plasmas is essential. In the present work, we measured the density distribution of sputtered Fe atoms using laser-induced fluorescence imaging spectroscopy. A dc magnetron plasma source with a Fe target was used. An area of 20 × 2 mm in front of the target was irradiated by a tunable laser beam having a planar shape. The picture of laser-induced fluorescence on the laser beam was taken using an ICCD camera. In this way, we obtained the two-dimensional image of the Fe atom density. As a result, it has been found that the Fe atom density observed at a distance of several centimeters from the target is higher than that adjacent to the target, when the Ar gas pressure was relatively high. It is suggested from this result that some gas-phase production processes of Fe atoms are available in the plasma. This work has been performed under the 21st Century COE Program by the Ministry of Education, Culture, Sports, Science and Technology in Japan.

  3. Composition and optical properties tunability of hydrogenated silicon carbonitride thin films deposited by reactive magnetron sputtering

    Science.gov (United States)

    Bachar, A.; Bousquet, A.; Mehdi, H.; Monier, G.; Robert-Goumet, C.; Thomas, L.; Belmahi, M.; Goullet, A.; Sauvage, T.; Tomasella, E.

    2018-06-01

    Radiofrequency reactive magnetron sputtering was used to deposit hydrogenated amorphous silicon carbonitride (a-SiCxNy:H) at 400 °C by sputtering a silicon target under CH4 and N2 reactive gas mixture. Rutherford backscattering spectrometry revealed that the change of reactive gases flow rate (the ratio R = FN2/(FN2+FCH4)) induced a smooth chemical composition tunability from a silicon carbide-like film for R = 0 to a silicon nitride-like one at R = 1 with a large area of silicon carbonitrides between the two regions. The deconvolution of Fourier Transform InfraRed and X-ray photoelectron spectroscopy spectrum highlighted a shift of the chemical environment of the deposited films corresponding to the changes seen by RBS. The consequence of these observations is that a control of refractive index in the range of [1.9-2.5] at λ = 633 nm and optical bandgap in the range [2 eV-3.8 eV] have been obtained which induces that these coatings can be used as antireflective coatings in silicon photovoltaic cells.

  4. Electron beam induced coloration and luminescence in layered structure of WO3 thin films grown by pulsed dc magnetron sputtering

    International Nuclear Information System (INIS)

    Karuppasamy, A.; Subrahmanyam, A.

    2007-01-01

    Tungsten oxide thin films have been deposited by pulsed dc magnetron sputtering of tungsten in argon and oxygen atmosphere. The as-deposited WO 3 film is amorphous, highly transparent, and shows a layered structure along the edges. In addition, the optical properties of the as-deposited film show a steplike behavior of extinction coefficient. However, the electron beam irradiation (3.0 keV) of the as-deposited films results in crystallization, coloration (deep blue), and luminescence (intense red emission). The above changes in physical properties are attributed to the extraction of oxygen atoms from the sample and the structural modifications induced by electron bombardment. The present method of coloration and luminescence has a potential for fabricating high-density optical data storage device

  5. Structural and electrical characteristics of highly textured oxidation-free Ru thin films by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Tian, H.-Y.; Wang Yu; Chan, H.-L-W.; Choy, C.-L.; No, K.-S.

    2005-01-01

    Textured Ru thin films (∼120 nm) were deposited on Si and rolling-assisted biaxially textured Ni substrates by a DC magnetron sputtering technique with a two-step process. The biaxially textured pure Ni substrates with a thickness of 80 μm were fabricated by rolling followed by recrystallization. The alignments and the crystallinity of Ru films were analyzed by pole figures, as well as X-ray diffraction (θ - 2θ) analysis. The highly (0 0 2) oriented Ru films were fabricated on Si substrates, and four-fold symmetric Ru films on Ni(2 0 0) substrates. The resistivities of pure metallic Ru films were 20-80 μΩ cm for Ru on Si and 16-40 μΩ cm on Ni, respectively, which is sufficiently low to be used as a buffer layer in superconductor tapes or electrode materials in capacitor dielectrics

  6. The Effect of Thickness on the Physical Properties of Fe2O3 Thin Films Prepared by DC Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Baha'a A. Al-Hilli

    2017-11-01

    Full Text Available The objective of this study is to assess the influence of nano-particle Fe2O3 thin film thickness on some physical properties which were prepared by magnetron DC- sputtering on glass substrate at room temperature. The structure was tested with X-Ray diffraction and it was to be amorphous and to become single crystal with recognized peak in (003 after annealing at temperature 500oC. The physical properties as a function of deposition parameters and then film thickness were studied. The optical properties such as absorbance, energy gap and some optical constants are measured and found that of about (3eV energy gap.

  7. Thin Film growth and characterization of Ti doped ZnO by RF/DC magnetron sputtering

    KAUST Repository

    Baseer Haider, M.

    2015-01-01

    Thin film Ti doped ZnO (Ti-ZnO) film were grown on sapphire (0001) substrate by RF and DC magnetron sputtering. Films were grown at a substrate temperature of 250 °C with different Ti/Zn concentration. Surface chemical study of the samples was performed by X-ray photoelectron spectroscopy to determine the stoichiometry and Ti/Zn ratio for all samples. Surface morphology of the samples were studied by atomic force microscopy. X-ray diffraction was carried out to determine the crystallinity of the film. No secondary phases of TixOy was observed. We observed a slight increase in the lattice constant with the increase in Ti concentration in ZnO. No ferromagnetic signal was observed for any of the samples. However, some samples showed super-paramagnetic phase. © 2015 Materials Research Society.

  8. Combined optical emission and resonant absorption diagnostics of an Ar-O{sub 2}-Ce-reactive magnetron sputtering discharge

    Energy Technology Data Exchange (ETDEWEB)

    El Mel, A.A. [Chimie des Interactions Plasma-Surface (ChIPS), Research Institute for Materials Science and Engineering, Université de Mons, Place du Parc 23, Mons B-7000 (Belgium); Institut des Matériaux Jean Rouxel, Université de Nantes, CNRS, 2 rue de la Houssinière B.P. 32229, Nantes Cedex 3 44322 (France); Ershov, S. [Chimie des Interactions Plasma-Surface (ChIPS), Research Institute for Materials Science and Engineering, Université de Mons, Place du Parc 23, Mons B-7000 (Belgium); Britun, N., E-mail: nikolay.britun@umons.ac.be [Chimie des Interactions Plasma-Surface (ChIPS), Research Institute for Materials Science and Engineering, Université de Mons, Place du Parc 23, Mons B-7000 (Belgium); Ricard, A. [Université de Toulouse, UPS, INPT, LAPLACE (Laboratoire Plasma et Conversion d' Energie), 118 route de Narbonne, Toulouse Cedex 9 F-31062 (France); Konstantinidis, S. [Chimie des Interactions Plasma-Surface (ChIPS), Research Institute for Materials Science and Engineering, Université de Mons, Place du Parc 23, Mons B-7000 (Belgium); Snyders, R. [Chimie des Interactions Plasma-Surface (ChIPS), Research Institute for Materials Science and Engineering, Université de Mons, Place du Parc 23, Mons B-7000 (Belgium); Materia Nova Research Center, Parc Initialis, Avenue Copernic 1, Mons B-7000 (Belgium)

    2015-01-01

    We report the results on combined optical characterization of Ar-O{sub 2}-Ce magnetron sputtering discharges by optical emission and resonant absorption spectroscopy. In this study, a DC magnetron sputtering system equipped with a movable planar magnetron source with a Ce target is used. The intensities of Ar, O, and Ce emission lines, as well as the absolute densities of Ar metastable and Ce ground state atoms are analyzed as a function of the distance from the magnetron target, applied DC power, O{sub 2} content, etc. The absolute number density of the Ar{sup m} is found to decrease exponentially as a function of the target-to-substrate distance. The rate of this decrease is dependent on the sputtering regime, which should be due to the different collisional quenching rates of Ar{sup m} by O{sub 2} molecules at different oxygen contents. Quantitatively, the absolute number density of Ar{sup m} is found to be equal to ≈ 3 × 10{sup 8} cm{sup −3} in the metallic, and ≈ 5 × 10{sup 7} cm{sup −3} in the oxidized regime of sputtering, whereas Ce ground state densities at the similar conditions are found to be few times lower. The absolute densities of species are consistent with the corresponding deposition rates, which decrease sharply during the transition from metallic to poisoned sputtering regime. - Highlights: • Optical emission and resonant absorption spectroscopy are employed to study Ar-O{sub 2}-Ce magnetron sputtering discharges. • The density of argon metastables is found to decrease exponentially when increasing the target-to-substrate distance. • The collision-quenching rates of Ar{sup m} by O{sub 2} molecules at different oxygen contents is demonstrated. • The deposition rates of cerium and cerium oxide thin films decrease sharply during the transition from the metallic to the poisoned sputtering regime.

  9. Corrosion resistance of ZrNxOy thin films obtained by rf reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Ariza, E.; Rocha, L.A.; Vaz, F.; Cunha, L.; Ferreira, S.C.; Carvalho, P.; Rebouta, L.; Alves, E.; Goudeau, Ph.; Riviere, J.P.

    2004-01-01

    The main aim of this work is the investigation of the corrosion resistance of single layered zirconium oxynitride, ZrN x O y , thin films in artificial sweat solution at ambient temperature. The films were produced by rf reactive magnetron sputtering, using a pure Zr target at a constant temperature of 300 deg. C. Two different sets of samples were produced. In the first set of films, the substrate bias voltage was the main variable, whereas in the second set, the flow rate of reactive gases (oxygen/nitrogen ratio) was varied. The control of the amount of oxygen allowed the film properties to be tailored from those of covalent zirconium nitride to those of the correspondent ionic oxide. The corrosion behaviour was evaluated by potentiodynamic polarization and Electrochemical Impedance Spectroscopy (EIS) tests. The analysis of EIS data provided detailed information of the corrosion processes occurring at the surface of the system throughout the immersion time. The modifications of the coating microstructure and/or chemical composition induced by the variation of the deposition parameters were also evaluated and correlated with the corrosion mechanisms occurring in each system

  10. Thermoelectric properties of epitaxial ScN films deposited by reactive magnetron sputtering onto MgO(001) substrates

    Science.gov (United States)

    Burmistrova, Polina V.; Maassen, Jesse; Favaloro, Tela; Saha, Bivas; Salamat, Shuaib; Rui Koh, Yee; Lundstrom, Mark S.; Shakouri, Ali; Sands, Timothy D.

    2013-04-01

    Epitaxial ScN(001) thin films were grown on MgO(001) substrates by dc reactive magnetron sputtering. The deposition was performed in an Ar/N2 atmosphere at 2 × 10-3 Torr at a substrate temperature of 850 °C in a high vacuum chamber with a base pressure of 10-8 Torr. In spite of oxygen contamination of 1.6 ± 1 at. %, the electrical resistivity, electron mobility, and carrier concentration obtained from a typical film grown under these conditions by room temperature Hall measurements are 0.22 mΩ cm, 106 cm2 V-1 s-1, and 2.5 × 1020 cm-3, respectively. These films exhibit remarkable thermoelectric power factors of 3.3-3.5 × 10-3 W/mK2 in the temperature range of 600 K to 840 K. The cross-plane thermal conductivity is 8.3 W/mK at 800 K yielding an estimated ZT of 0.3. Theoretical modeling of the thermoelectric properties of ScN calculated using a mean-free-path of 23 nm at 300 K is in very good agreement with the experiment. These results also demonstrate that further optimization of the power factor of ScN is possible. First-principles density functional theory combined with the site occupancy disorder technique was used to investigate the effect of oxygen contamination on the electronic structure and thermoelectric properties of ScN. The computational results suggest that oxygen atoms in ScN mix uniformly on the N site forming a homogeneous solid solution alloy. Behaving as an n-type donor, oxygen causes a shift of the Fermi level in ScN into the conduction band without altering the band structure and the density of states.

  11. Tribological Testing, Analysis and Characterization of D.C. Magnetron Sputtered Ti-Nb-N Thin Film Coatings on Stainless Steel

    Science.gov (United States)

    Joshi, Prathmesh

    To enhance the surface properties of stainless steel, the substrate was coated with a 1μm thick coating of Ti-Nb-N by reactive DC magnetron sputtering at different N2 flow rates, substrate biasing and Nb-Ti ratio. The characterization of the coated samples was performed by the following techniques: hardness by Knoop micro-hardness tester, phase analysis by X-ray Diffraction (XRD), compositional analysis by Energy Dispersive X-ray Spectroscopy (EDS) and adhesion by scratch test. The tribology testing was performed on linearly reciprocating ball-on-plate wear testing machine and wear depth and wear volume were evaluated by white light interferometer. The micro-hardness test yielded appreciable enhancement in the surface hardness with the highest value being 1450 HK. Presence of three prominent phases namely NbN, Nb2N3 and TiN resulted from the XRD analysis. EDS analysis revealed the presence of Ti, Nb and Nitrogen. Adhesion was evaluated on the basis of critical loads for cohesive (Lc1) and adhesive (Lc2) failures with values varying between 7-12 N and 16-25 N respectively, during scratch test for coatings on SS substrates.

  12. Residual stress and texture in Aluminum doped Zinc Oxide layers deposited by reactive radio frequency magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Azanza Ricardo, C.L., E-mail: Cristy.Azanza@ing.unitn.it [Department of Civil, Environmental and Mechanical Engineering, University of Trento, 38123 via Mesiano 77, Trento (Italy); Pastorelli, M.; D' Incau, M. [Department of Civil, Environmental and Mechanical Engineering, University of Trento, 38123 via Mesiano 77, Trento (Italy); Aswath, P. [College of Engineering, University of Texas at Arlington, TX (United States); Scardi, P. [Department of Civil, Environmental and Mechanical Engineering, University of Trento, 38123 via Mesiano 77, Trento (Italy)

    2016-04-30

    Aluminum doped Zinc Oxide thin films were deposited on standard soda-lime substrates by reactive radio frequency magnetron sputtering. Residual stress and texture were studied by X-ray diffraction, while X-ray Absorption Near Edge Spectroscopy provided information on the Al environment in the best performing thin films. The influence of deposition parameters on structural and microstructural properties is discussed. A correlation between microstructure and residual stress state with electrical and optical properties is proposed. - Highlights: • Al doped ZnO thin films were obtained by reactive radio frequency magnetron sputtering. • Correlation of stresses and texture with electrical and optical properties is shown. • Homogeneous and stress-free thin-films are the best performing ones. • XANES confirmed the doping mechanism and excluded some spurious phases.

  13. Structure adhesion and corrosion resistance study of tungsten bisulfide doped with titanium deposited by DC magnetron co-sputtering

    Energy Technology Data Exchange (ETDEWEB)

    De La Roche, J. [Laboratorio de Física del Plasma, Universidad Nacional de Colombia Sede Manizales, Km. 9 vía al aeropuerto, Campus La Nubia, Manizales (Colombia); González, J.M. [Laboratorio de Recubrimientos Duros y Aplicaciones Industriales – RDAI, Universidad del Valle, Calle 13 N° 100-00 Ciudadela Meléndez, Cali (Colombia); Restrepo-Parra, E., E-mail: erestrepop@unal.edu.co [Laboratorio de Física del Plasma, Universidad Nacional de Colombia Sede Manizales, Km. 9 vía al aeropuerto, Campus La Nubia, Manizales (Colombia); Sequeda, F. [Laboratorio de Recubrimientos Duros y Aplicaciones Industriales – RDAI, Universidad del Valle, Calle 13 N° 100-00 Ciudadela Meléndez, Cali (Colombia); Alleh, V.; Scharf, T.W. [The University of North Texas, Department of Materials Science and Engineering, Denton, TX 76203 (United States)

    2014-11-30

    Highlights: • Ti-doped WS{sub 2} films were grown via the magnetron co-sputtering technique. • At a high Ti percentage, the crystalline structure of WS{sub 2} coatings tends to be amorphous. • As the Ti percentage increases in WS{sub 2} coatings, nanocomposites tend to form. • Ti-doped WS{sub 2} films have elastic behavior compared with the plastic response of pure WS{sub 2} films. • A high Ti percentage increases the corrosion resistance of WS{sub 2} films. - Abstract: Titanium-doped tungsten bisulfide thin films (WS{sub 2}-Ti) were grown using a DC magnetron co-sputtering technique on AISI 304 stainless steel and silicon substrates. The films were produced by varying the Ti cathode power from 0 to 25 W. Using energy dispersive spectroscopy (EDS), the concentration of Ti in the WS{sub 2} was determined, and a maximum of 10% was obtained for the sample grown at 25 W. Moreover, the S/W ratio was calculated and determined to increase as a function of the Ti cathode power. According to transmission electron microscopy (TEM) results, at high titanium concentrations (greater than 6%), nanocomposite formation was observed, with nanocrystals of Ti embedded in an amorphous matrix of WS{sub 2}. Using the scratch test, the coatings’ adhesion was analyzed, and it was observed that as the Ti percentage was increased, the critical load (Lc) also increased. Furthermore, the failure type changed from plastic to elastic. Finally, the corrosion resistance was evaluated using the electrochemical impedance spectroscopy (EIS) technique, and it was observed that at high Ti concentrations, the corrosion resistance was improved, as Ti facilitates coating densification and generates a protective layer.

  14. Effects of nitrogen ion implantation time on tungsten films deposited by DC magnetron sputtering on AISI 410 martensitic stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Malau, Viktor, E-mail: malau@ugm.ac.id; Ilman, Mochammad Noer, E-mail: noer-ilman@yahoo.com; Iswanto, Priyo Tri, E-mail: priyatri@yahoo.com; Jatisukamto, Gaguk, E-mail: gagukjtsk@yahoo.co.id [Mechanical and Industrial Engineering Department, Gadjah Mada University Jl. Grafika 2, Yogyakarta, 55281 (Indonesia)

    2016-03-29

    Nitrogen ion implantation time on tungsten thin film deposited on surface of AISI 410 steel has been performed. Tungsten thin film produced by dc magnetron sputtering method was deposited on AISI 410 martensitic stainless steel substrates, and then the nitrogen ions were implanted on tungsten thin film. The objective of this research is to investigate the effects of implantation deposition time on surface roughness, microhardness, specific wear and corrosion rate of nitrogen implanted on tungsten film. Magnetron sputtering process was performed by using plasma gas of argon (Ar) to bombardier tungsten target (W) in a vacuum chamber with a pressure of 7.6 x 10{sup −2} torr, a voltage of 300 V, a sputter current of 80 mA for sputtered time of 10 minutes. Nitrogen implantation on tungsten film was done with an initial pressure of 3x10{sup −6} mbar, a fluence of 2 x 10{sup 17} ions/cm{sup 2}, an energy of 100 keV and implantation deposition times of 0, 20, 30 and 40 minutes. The surface roughness, microhardness, specific wear and corrosion rate of the films were evaluated by surfcorder test, Vickers microhardness test, wear test and potentiostat (galvanostat) test respectively. The results show that the nitrogen ions implanted deposition time on tungsten film can modify the surface roughness, microhardness, specific wear and corrosion rate. The minimum surface roughness, specific wear and corrosion rate can be obtained for implantation time of 20 minutes and the maximum microhardness of the film is 329 VHN (Vickers Hardness Number) for implantation time of 30 minutes. The specific wear and corrosion rate of the film depend directly on the surface roughness.

  15. Chemical environment of iron atoms in iron oxynitride films synthesized by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Grafoute, M.; Petitjean, C.; Rousselot, C.; Pierson, J.F.; Greneche, J.M.

    2007-01-01

    An iron oxynitride film was deposited on silicon and glass substrates by magnetron sputtering in an Ar-N 2 -O 2 reactive mixture. Rutherford back-scattering spectrometry was used to determine the film composition (Fe 1.06 O 0.35 N 0.65 ). X-ray diffraction revealed the formation of a face-centred cubic (fcc) structure with a lattice parameter close to that of γ'''-FeN. X-ray photoelectron spectroscopy showed the occurrence of Fe-N and Fe-O bonds in the film. The local environment of iron atoms studied by 57 Fe Moessbauer spectrometry at both 300 and 77 K gives clear evidence that the Fe 1.06 O 0.35 N 0.65 is not a mixture of iron oxide and iron nitride phases. Despite a small amount of an iron nitride phase, the main sample consists of an iron oxynitride phase with an NaCl-type structure where oxygen atoms partially substitute for nitrogen atoms, thus indicating the formation of a iron oxynitride with an fcc structure

  16. Thermal stability of tungsten sub-nitride thin film prepared by reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, X.X. [School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050 (China); State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730050 (China); Wu, Y.Z., E-mail: youzhiwu@163.com [School of Materials Science and Engineering, Lanzhou University of Technology, Lanzhou, 730050 (China); Mu, B. [College of Petrochemical Technology, Lanzhou University of Technology, Lanzhou, 730050 (China); Qiao, L. [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730050 (China); Li, W.X.; Li, J.J. [Beijing National Laboratory for Condensed Matter Physics, Institute of Physics, Chinese Academy of Sciences, Beijing 100190 (China); Wang, P., E-mail: pengwang@licp.cas.cn [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730050 (China)

    2017-03-15

    Tungsten sub-nitride thin films deposited on silicon samples by reactive magnetron sputtering were used as a model system to study the phase stability and microstructural evolution during thermal treatments. XRD, SEM&FIB, XPS, RBS and TDS were applied to investigate the stability of tungsten nitride films after heating up to 1473 K in vacuum. At the given experimental parameters a 920 nm thick crystalline film with a tungsten and nitrogen stoichiometry of 2:1 were achieved. The results showed that no phase and microstructure change occurred due to W{sub 2}N film annealing in vacuum up to 973 K. Heating up to 1073 K led to a partial decomposition of the W{sub 2}N phase and the formation of a W enrichment layer at the surface. Increasing the annealing time at the same temperature, the further decomposition of the W{sub 2}N phase was negligible. The complete decomposition of W{sub 2}N film happened as the temperature reached up to 1473 K.

  17. Deposition and characterization of NbAIN thin films by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Carvalho, R.G.; Felix, L.C.; Fernandez, D.A.R.; Fontes Junior, A.S.; Oliveira, G.B.; Tentardini, E.K.

    2016-01-01

    The objective of this work was to study NbAlN thin films and the influence of variation in the concentration of aluminum in the crystal structure and oxidation resistance of these coatings. The thin films were deposited by reactive magnetron sputtering and characterized by Grazing Incidence X-ray Diffraction (GIXRD), Energy Dispersive Spectroscopy (EDS) and oxidation tests at high temperatures. NbAlN thin films were deposited and present at concentration of 10, 20 and 42 at% Al. The NbAlN crystalline phase obtained was the δ-NbN, however it was observed a shift of the peaks in the patterns obtained GIXRD of regions for larger angles for these samples, indicating the formation of a solid solution. The higher oxidation resistance temperature was 700° C for the sample with 42 in at% Al. From the SEM analysis it was possible to observe the surface of the film after oxidation, all films showed defects, however the amount of such defects was lower in samples with higher aluminum concentrations. (author)

  18. Deposition and characterization of IrOx nanofoils on carbon nanotube templates by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Chen, Yi-Min; Cai, Jhen-Hong; Huang, Ying-Sheng; Lee, Kuei-Yi; Tsai, Dah-Shyang; Tiong, Kwong-Kau

    2012-01-01

    Large surface area IrO x nanofoils (IrO x NF) were deposited on multi-wall carbon nanotube (MWCNT) templates, forming IrO x /MWCNT nanocomposites, by reactive radio frequency magnetron sputtering using Ir metal target. The structural and spectroscopic properties of IrO x NF were characterized. The micrographs of field emission scanning electron microscopy showed the formation of foil-like structure for the as-deposited samples. Transmission electron microscopy analysis revealed the contiguous presence of glassy iridium oxide, iridium metal, and iridium dioxide nanocrystals in the foil. X-ray photoelectron spectroscopy analysis provided the information of the oxidation states and the stoichiometry of IrO x NF. Raman spectra revealed the amorphous-like phase of the as-deposited IrO x NF. The nanofoil structure provided ultra-high surface area for electrical charge storage which made the IrO x /MWCNT nanocomposites as an attractive candidate for the supercapacitor applications.

  19. Adhesion analysis for chromium nitride thin films deposited by reactive magnetron sputtering

    Science.gov (United States)

    Rusu, F. M.; Merie, V. V.; Pintea, I. M.; Molea, A.

    2016-08-01

    The thin film industry is continuously growing due to the wide range of applications that require the fabrication of advanced components such as sensors, biological implants, micro-electromechanical devices, optical coatings and so on. The selection regarding the deposition materials, as well as the deposition technology influences the properties of the material and determines the suitability of devices for certain real-world applications. This paper is focused on the adhesion force for several chromium nitride thin films obtained by reactive magnetron sputtering. All chromium nitride thin films were deposited on a silicon substrate, the discharge current and the argon flow being kept constant. The main purpose of the paper is to determine the influence of deposition parameters on the adhesion force. Therefore some of the deposition parameters were varied in order to study their effect on the adhesion force. Experimentally, the values of the adhesion force were determined in multiple points for each sample using the spectroscopy in point mode of the atomic force microscope. The obtained values were used to estimate the surface energy of the CrN thin films based on two existing mathematical models for the adhesion force when considering the contact between two bodies.

  20. Growth of high quality AlN films on CVD diamond by RF reactive magnetron sputtering

    Science.gov (United States)

    Chen, Liang-xian; Liu, Hao; Liu, Sheng; Li, Cheng-ming; Wang, Yi-chao; An, Kang; Hua, Chen-yi; Liu, Jin-long; Wei, Jun-jun; Hei, Li-fu; Lv, Fan-xiu

    2018-02-01

    A highly oriented AlN layer has been successfully grown along the c-axis on a polycrystalline chemical vapor deposited (CVD) diamond by RF reactive magnetron sputtering. Structural, morphological and mechanical properties of the heterostructure were investigated by Scanning Electron Microscopy (SEM), Atomic Force Microscopy (AFM), Transmission Electron Microscopy (TEM), X-ray diffraction (XRD), Nano-indentation and Four-probe meter. A compact AlN film was demonstrated on the diamond layer, showing columnar grains and a low surface roughness of 1.4 nm. TEM results revealed a sharp AlN/diamond interface, which was characterized by the presence of a distinct 10 nm thick buffer layer resulting from the initial AlN growth stage. The FWHM of AlN (002) diffraction peak and its rocking curve are as low as 0.41° and 3.35° respectively, indicating a highly preferred orientation along the c-axis. AlN sputtered films deposited on glass substrates show a higher bulk resistivity (up to 3 × 1012 Ω cm), compared to AlN films deposited on diamond (∼1010 Ω cm). Finally, the film hardness and Young's modulus of AlN films on diamond are 25.8 GPa and 489.5 GPa, respectively.

  1. Structural and mechanical properties of ZrSiN thin films prepared by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Freitas, F.G.R.; Conceicao, A.G.S.; Vitoria, E.R.; Carvalho, R.G.; Tentardini, E.K.; Hübler, R.; Soares, G.

    2014-01-01

    Zirconium silicon nitride (ZrSiN) thin films were deposited by reactive magnetron sputtering in order to verify the silicon influence on coating morphology and mechanical properties. The Si/(Zr+Si) ratio was adjusted between 0 to 14.5% just modifying the power applied on the silicon target. Only peaks associated to ZrN crystalline structure were observed in XRD analysis, since Si_3N_4 phase was amorphous. All samples have (111) preferred orientation, but there is a peak intensity reduction and a broadening increase for the sample with the highest Si/(Zr+Si) ratio (14.5%), demonstrating a considerable loss of crystallinity or grain size reduction (about 8 nm calculated by Scherrer). It was also observed that the texture coefficient for (200) increases with silicon addition. Chemical composition and thickness of the coatings were determined by RBS analysis. No significant changes in nano hardness with increasing Si content were found. The thin film morphology observed by SEM presents columnar and non columnar characteristics. The set of results suggests that Si addition is restricting the columnar growth of ZrN thin films. This conclusion is justified by the fact that Si contributes to increase the ZrN grains nucleation during the sputtering process. (author)

  2. Biocompatibility and Surface Properties of TiO2 Thin Films Deposited by DC Magnetron Sputtering

    Science.gov (United States)

    López-Huerta, Francisco; Cervantes, Blanca; González, Octavio; Hernández-Torres, Julián; García-González, Leandro; Vega, Rosario; Herrera-May, Agustín L.; Soto, Enrique

    2014-01-01

    We present the study of the biocompatibility and surface properties of titanium dioxide (TiO2) thin films deposited by direct current magnetron sputtering. These films are deposited on a quartz substrate at room temperature and annealed with different temperatures (100, 300, 500, 800 and 1100 °C). The biocompatibility of the TiO2 thin films is analyzed using primary cultures of dorsal root ganglion (DRG) of Wistar rats, whose neurons are incubated on the TiO2 thin films and on a control substrate during 18 to 24 h. These neurons are activated by electrical stimuli and its ionic currents and action potential activity recorded. Through X-ray diffraction (XRD), the surface of TiO2 thin films showed a good quality, homogeneity and roughness. The XRD results showed the anatase to rutile phase transition in TiO2 thin films at temperatures between 500 and 1100 °C. This phase had a grain size from 15 to 38 nm, which allowed a suitable structural and crystal phase stability of the TiO2 thin films for low and high temperature. The biocompatibility experiments of these films indicated that they were appropriated for culture of living neurons which displayed normal electrical behavior. PMID:28788667

  3. Nanoscale compositional analysis of NiTi shape memory alloy films deposited by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, S. K.; Mohan, S. [Centre for Nano Science and Engineering, Indian Institute of Science, Bangalore-560012 (India); Bysakh, S. [Central Glass and Ceramics Research Institute, Kolkata-700032 (India); Kumar, A.; Kamat, S. V. [Defence Metallurgical Research Laboratory, Hyderabad-500058 (India)

    2013-11-15

    The formation of surface oxide layer as well as compositional changes along the thickness for NiTi shape memory alloy thin films deposited by direct current magnetron sputtering at substrate temperature of 300 °C in the as-deposited condition as well as in the postannealed (at 600 °C) condition have been thoroughly studied by using secondary ion mass spectroscopy, x-ray photoelectron spectroscopy, and scanning transmission electron microscopy-energy dispersive x-ray spectroscopy techniques. Formation of titanium oxide (predominantly titanium dioxide) layer was observed in both as-deposited and postannealed NiTi films, although the oxide layer was much thinner (8 nm) in as-deposited condition. The depletion of Ti and enrichment of Ni below the oxide layer in postannealed films also resulted in the formation of a graded microstructure consisting of titanium oxide, Ni{sub 3}Ti, and B2 NiTi. A uniform composition of B2 NiTi was obtained in the postannealed film only below a depth of 200–250 nm from the surface. Postannealed film also exhibited formation of a ternary silicide (Ni{sub x}Ti{sub y}Si) at the film–substrate interface, whereas no silicide was seen in the as-deposited film. The formation of silicide also caused a depletion of Ni in the film in a region ∼250–300 nm just above the film substrate interface.

  4. Room temperature H2S gas sensing property of indium oxide thin films obtained by pulsed D.C. magnetron sputtering

    International Nuclear Information System (INIS)

    Nisha, R.; Madhusoodanan, K.N.; Karthikeyan, Sreejith; Hill, Arthur E.; Pilkington, Richard D.

    2013-01-01

    Indium oxide thin films were prepared by pulsed dc magnetron sputtering technique with no substrate heating. X-ray diffraction was used to investigate the structural properties and AFM was used to study the surface morphology gas sensing performance were conducted using a static gas sensing system. Room temperature gas sensing performance was conducted in range of 17 to 286 ppm. The sensitivity, response and recovery time of the sensor was also determined. (author)

  5. Structure, adhesive strength and electrochemical performance of nitrogen doped diamond-like carbon thin films deposited via DC magnetron sputtering.

    Science.gov (United States)

    Khun, N W; Liu, E; Krishna, M D

    2010-07-01

    Nitrogen doped diamond-like carbon (DLC:N) thin films were deposited on p-Si (100) substrates by DC magnetron sputtering with different nitrogen flow rates at a substrate temperature of about 100 degrees C. The chemical bonding structure of the films was characterized by X-ray photoelectron spectroscopy (XPS) and micro-Raman spectroscopy. The adhesive strength and surface morphology of the films were studied using micro-scratch tester and scanning electron microscope (SEM), respectively. The electrochemical performance of the films was evaluated by potentiodynamic polarization testing and linear sweep voltammetry. The electrolytes used for the electrochemical tests were deaerated and unstirred 0.47 M KCl aqueous solution for potentiodynamic polarization testing and 0.2 M KOH and 0.1 M KCl solutions for voltammetric analysis. It was found that the DLC:N films could well passivate the underlying substrates though the corrosion resistance of the films decreased with increased nitrogen content in the films. The DLC:N films showed wide potential windows in the KOH solution, in which the detection ability of the DLC:N films to trace lead of about 1 x 10(-3) M Pb(2+) was also tested.

  6. The influence of target oxygen on the YBa2Cu3O6+δ DC Magnetron sputtering process

    International Nuclear Information System (INIS)

    Larsson, G.; Selinder, T.I.; Helmersson, U

    1990-01-01

    The oxygen partial pressure and the target potential have been monitored under a range of process conditions during single target dc magnetron sputtering of Y-Ba-Cu-O. The introduced sputtering gas consisted in all but one instance of pure argon and hence the oxygen present in the plasma originated mainly from the target. During the first hours of sputtering the oxygen partial pressure was of the same magnitude as the argon pressure (3.0 Pa). As the oxygen was released from the target and subsequently removed by pumping, the target potential increased and the film composition became more stoichiometric. After 30-40 hours of sputtering the target potential and the oxygen pressure stabilized and the film composition was equal to that of the stoichiometric target. If an oxygen flow exceeding a critical level was mixed into the sputtering gas the target potential and the deposition rate decreased swiftly. This was due to target oxidation, further manifested in changing plasma and target colours. In some instances the stabilization after 'presputtering' was incomplete and oscillations in target voltage and oxygen partial pressure were observed. The fluctuations made it virtually impossible to obtain stoichiometric films. The oscillative behaviour of the sputtering process is tentatively explained by a target temperature dependent oxygen diffusion. (au)

  7. Synthesis and characterization of MoB2−x thin films grown by nonreactive DC magnetron sputtering

    International Nuclear Information System (INIS)

    Malinovskis, Paulius; Lewin, Erik; Jansson, Ulf; Palisaitis, Justinas; Persson, Per O. Å.

    2016-01-01

    DC magnetron sputtering was used to deposit molybdenum boride thin films for potential low-friction applications. The films exhibit a nanocomposite structure with ∼10 nm large MoB 2−x (x > 0.4) grains surrounded by a boron-rich tissue phase. The preferred formation of the metastable and substoichiometric hP3-MoB 2 structure (AlB 2 -type) is explained with kinetic constraints to form the thermodynamically stable hR18-MoB 2 phase with a very complex crystal structure. Nanoindentation revealed a relatively high hardness of (29 ± 2) GPa, which is higher than bulk samples. The high hardness can be explained by a hardening effect associated with the nanocomposite microstructure where the surrounding tissue phase restricts dislocation movement. A tribological study confirmed a significant formation of a tribofilm consisting of molybdenum oxide and boron oxide, however, without any lubricating effects at room temperature.

  8. Impedimetric Thiourea Sensing in Copper Electrorefining Bath based on DC Magnetron Sputtered Nanosilver as Highly Uniform Transducer

    International Nuclear Information System (INIS)

    Mozaffari, S.A.; Amoli, H. Salar; Simorgh, S.; Rahmanian, R.

    2015-01-01

    Highlights: • Fabrication of a novel disposable impedimetric thiourea sensor based on nanostructured Ag film transducer. • Exploiting sputtering as a high-tech method for preparation of highly uniform nanostructured Ag film. • A wonderful combination of nanostructured Ag film and carbon paper substrate as remarkably stable and reproducible sensor for thiourea detection in copper electrorefining bath. • Application of impedimetric assessment for thiourea monitoring due to its rapidity, sensitivity, and repeatability. - Abstract: Highly uniform sputtered nanostructured silver (Nano-Ag) film on the conductive carbon paper (CP) substrate (Nano-Ag/CP) was applied as a novel approach for thiourea (TU) measurement in copper electrorefining bath. Nano-Ag film was achieved by direct current (DC) magnetron sputtering system at the optimized instrumental deposition conditions. Characterization of the surface structure of Nano-Ag film by field emission-scanning electron microscopy (FE-SEM), exhibits uniform Nano-Ag film as an effective transducer for TU sensing. Step by step monitoring of Nano-Ag/CP electrode fabrication were performed using electrochemical methods such as cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) techniques. Fabricated Nano-Ag/CP electrode was used for TU determination using EIS assessment. The impedimetric results show high sensitivity for TU sensing within 2.0–250 ppm.

  9. The Optimum Fabrication Condition of p-Type Antimony Tin Oxide Thin Films Prepared by DC Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Huu Phuc Dang

    2016-01-01

    Full Text Available Transparent Sb-doped tin oxide (ATO thin films were fabricated on quartz glass substrates via a mixed (SnO2 + Sb2O3 ceramic target using direct current (DC magnetron sputtering in ambient Ar gas at a working pressure of 2 × 10−3 torr. X-ray diffraction (XRD, X-ray photoelectron spectroscopy (XPS, Hall-effect, and UV-vis spectra measurements were performed to characterize the deposited films. The substrate temperature of the films was investigated in two ways: (1 films were annealed in Ar ambient gas after being deposited at room temperature or (2 they were deposited directly at different temperatures. The first process for fabricating the ATO films was found to be easier than the second process. The deposited films showed p-type electrical properties, a polycrystalline tetragonal rutile structure, and their average transmittance was greater than 80% in the visible light range at the optimum annealing temperature of 500°C. The best electrical properties of the film were obtained on a 10 wt% Sb2O3-doped SnO2 target with a resistivity, hole concentration, and Hall mobility of 0.55 Ω·cm, 1.2 × 1019 cm−3, and 0.54 cm2V−1s−1, respectively.

  10. Synthesis and characterization of MoB{sub 2−x} thin films grown by nonreactive DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Malinovskis, Paulius, E-mail: paulius.malinovskis@kemi.uu.se; Lewin, Erik; Jansson, Ulf [Department of Chemistry–Ångström Laboratory, Uppsala University, SE-751 21 Uppsala (Sweden); Palisaitis, Justinas; Persson, Per O. Å. [Department of Physics, Chemistry, and Biology (IFM), Thin Film Physics Division, Linköping University, SE-581 83 Linköping (Sweden)

    2016-05-15

    DC magnetron sputtering was used to deposit molybdenum boride thin films for potential low-friction applications. The films exhibit a nanocomposite structure with ∼10 nm large MoB{sub 2−x} (x > 0.4) grains surrounded by a boron-rich tissue phase. The preferred formation of the metastable and substoichiometric hP3-MoB{sub 2} structure (AlB{sub 2}-type) is explained with kinetic constraints to form the thermodynamically stable hR18-MoB{sub 2} phase with a very complex crystal structure. Nanoindentation revealed a relatively high hardness of (29 ± 2) GPa, which is higher than bulk samples. The high hardness can be explained by a hardening effect associated with the nanocomposite microstructure where the surrounding tissue phase restricts dislocation movement. A tribological study confirmed a significant formation of a tribofilm consisting of molybdenum oxide and boron oxide, however, without any lubricating effects at room temperature.

  11. Room temperature growth of nanocrystalline anatase TiO{sub 2} thin films by dc magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Preetam, E-mail: preetamphy@gmail.co [Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology, Indian Institute of Technology Roorkee, Roorkee 247667 (India); Kaur, Davinder [Functional Nanomaterials Research Lab, Department of Physics and Centre of Nanotechnology, Indian Institute of Technology Roorkee, Roorkee 247667 (India)

    2010-03-01

    We report, the structural and optical properties of nanocrystalline anatase TiO{sub 2} thin films grown on glass substrate by dc magnetron sputtering at room temperature. The influence of sputtering power and pressure over crystallinity and surface morphology of the films were investigated. It was observed that increase in sputtering power activates the TiO{sub 2} film growth from relative lower surface free energy to higher surface free energy. XRD pattern revealed the change in preferred orientation from (1 0 1) to (0 0 4) with increase in sputtering power, which is accounted for different surface energy associated with different planes. Microstructure of the films also changes from cauliflower type to columnar type structures with increase in sputtering power. FESEM images of films grown at low pressure and low sputtering power showed typical cauliflower like structure. The optical measurement revealed the systematic variation of the optical constants with deposition parameters. The films are highly transparent with transmission higher than 90% with sharp ultraviolet cut off. The transmittance of these films was found to be influenced by the surface roughness and film thickness. The optical band gap was found to decrease with increase in the sputtering power and pressure. The refractive index of the films was found to vary in the range of 2.50-2.24 with increase in sputtering pressure or sputtering power, resulting in the possibility of producing TiO{sub 2} films for device applications with different refractive index, by changing the deposition parameters.

  12. Effect of arc suppression on the physical properties of low temperature dc magnetron sputtered tantalum thin films

    International Nuclear Information System (INIS)

    Subrahmanyam, A.; Valleti, Krishna; Joshi, Srikant V.; Sundararajan, G.

    2007-01-01

    Arcing is a common phenomenon in the sputtering process. Arcs and glow discharges emit electrons which may influence the physical properties of films. This article reports the properties of tantalum (Ta) thin films prepared by continuous dc magnetron sputtering in normal and arc-suppression modes. The substrate temperature was varied in the range of 300-673 K. The tantalum films were ∼1.8 μm thick and have good adherence to 316 stainless steel and single-crystal silicon substrates. The phase of the Ta thin film determines the electrical and tribological properties. The films deposited at 300 K using both methods were crystallized in a tetragonal structure (β phase) with a smooth surface (grain size of ∼10 nm) and exhibited an electrical resistivity of ∼194 μΩ cm and a hardness of ∼20 GPa. When the substrate temperature was 473 K and higher, the arc-suppression mode appears to influence the films to crystallize in the α phase with a grain size of ∼40 nm, whereas the normal power mode gave mixed phases β and α beyond 473 K, the arc-suppression mode yields larger grain sizes in the Ta thin films and the hardness decreases. These changes in the physical properties in arc-suppression mode are attributed to either the change in plasma characteristics or the energetic particle bombardment onto the substrate, or both

  13. Electrical and optical properties of indium tin oxide thin films deposited on unheated substrates by d.c. reactive sputtering

    International Nuclear Information System (INIS)

    Karasawa, T.; Miyata, Y.

    1993-01-01

    Transparent conducting thin films of indium tin oxide (ITO) have been deposited by d.c. reactive planar magnetron sputtering by using metal In-Sn alloy target in an Ar-O 2 gas mixture. The study demonstrates that the deposition on unheated substrates achieved sheet resistance of as low as about 50-60 Ω/□ (or a resistivity of about 7 x 10 -4 Ω cm), and visible transmission of about 90% for a wavelength of 420 nm. The effects of heat treatment at 450 C in air depends on the deposition conditions of the as-deposited ITO films. Although annealing improves the properties of as-deposited ITO films which were deposited with non-optimum conditions, the optimized condition for the formation of the film in the as-deposited state is essential to obtain a high quality transparent conducting coating. (orig.)

  14. Silicon oxynitride films deposited by reactive high power impulse magnetron sputtering using nitrous oxide as a single-source precursor

    Energy Technology Data Exchange (ETDEWEB)

    Hänninen, Tuomas, E-mail: tuoha@ifm.liu.se; Schmidt, Susann; Jensen, Jens; Hultman, Lars; Högberg, Hans [Thin Film Physics Division, Department of Physics, Chemistry, and Biology (IFM), Linköping University, Linköping SE-581 83 (Sweden)

    2015-09-15

    Silicon oxynitride thin films were synthesized by reactive high power impulse magnetron sputtering of silicon in argon/nitrous oxide plasmas. Nitrous oxide was employed as a single-source precursor supplying oxygen and nitrogen for the film growth. The films were characterized by elastic recoil detection analysis, x-ray photoelectron spectroscopy, x-ray diffraction, x-ray reflectivity, scanning electron microscopy, and spectroscopic ellipsometry. Results show that the films are silicon rich, amorphous, and exhibit a random chemical bonding structure. The optical properties with the refractive index and the extinction coefficient correlate with the film elemental composition, showing decreasing values with increasing film oxygen and nitrogen content. The total percentage of oxygen and nitrogen in the films is controlled by adjusting the gas flow ratio in the deposition processes. Furthermore, it is shown that the film oxygen-to-nitrogen ratio can be tailored by the high power impulse magnetron sputtering-specific parameters pulse frequency and energy per pulse.

  15. High-speed deposition of protective films of aluminium oxide by the method of reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Bugaev, S.P.; Zakhrov, A.N.; Ladyzhenskii, O.P.; Sochugov, M.S.

    2001-01-01

    The high optical characteristics of aluminium films made them attractive for different functional and decorative applications. It is well-known that the corrosion resistance of alloying is determined by the presence of the oxide film on its surface, but on the aluminium films, deposited by vacuum methods, the resistance is extremely low resulting in the relatively rapid failure of the coating. At present, there is a large number of methods of depositing the films of aluminium oxide. In most cases, it is recommended to use reactive magnetron sputtering of an aluminium target in a magnetron spraying system (MSS) using direct current, on dispersion of the target of aluminium oxide in a high-frequency MSS

  16. Microstructure and tribological properties of NbN-Ag composite films by reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Ju, Hongbo; Xu, Junhua, E-mail: jhxu@just.edu.cn

    2015-11-15

    Highlights: • NbN-Ag films were deposited by reactive magnetron sputtering. • The fcc-NbN, hcp-NbN and fcc-Ag coexisted in NbN-Ag films. • The incorporation of Ag into NbN matrix led to the decrease of hardness. • The films (9.2–13.5 at.% Ag) were found to be optimized for wear resistance tools. - Abstract: Recently, the chameleon thin films were developed with the purpose of adjusting their chemistry at self-mating interfaces in response to environmental changes at a wide temperature range. However, very few studies have focused on what state the lubricious noble metal exists in the films and the tribological properties at room temperature (RT). Composite NbN-Ag films with various Ag content (Ag/(Nb + Ag)) were deposited using reactive magnetron sputtering to investigate the crystal structure, mechanical and tribological properties. A combination of X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS) and high resolution transmission electron microscopy (HRTEM) analyses showed that face-centered cubic (fcc) NbN, hexagonal close-packed (hcp) NbN and fcc silver coexisted in NbN-Ag films. The incorporation of soft Ag into NbN matrix led to the hardness decrease from 29.6 GPa at 0 at.% Ag to 11.3 GPa at 19.9 at.% Ag. Tribological properties of NbN-Ag films performed using dry pin-on-disc wear tests against Al{sub 2}O{sub 3} depended on Ag content to a large extent. The average friction coefficient and wear rate of NbN-Ag films decreased as Ag content increased from 4.0 to 9.2 at.%. With a further increase of Ag content, the average friction coefficient further decreased, while the wear rate increased gradually. The optimal Ag content was found to be 9.2–13.5 at.%, which showed low average friction coefficient values of 0.46–0.40 and wear rate values of 1.1 × 10{sup −8} to 1.7 × 10{sup −8} mm{sup 3}/(mm N). 3D Profiler and Raman spectroscopy measurements revealed that the lubricant tribo-film AgNbO{sub 3} detected on the surface of the

  17. Gas barrier properties of titanium oxynitride films deposited on polyethylene terephthalate substrates by reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Lin, M.-C. [Department of Materials Science and Engineering, National ChungHsin University, 250, Kuo-Kung Road, 40227 Taichung, Taiwan (China); Chang, L.-S. [Department of Materials Science and Engineering, National ChungHsin University, 250, Kuo-Kung Road, 40227 Taichung, Taiwan (China)], E-mail: lschang@dragon.nchu.edu.tw; Lin, H.C. [Department of Materials Science and Engineering, National Taiwan University, 1, Roosevelt Road, Sec. 4, 106 Taipei, Taiwan (China)

    2008-03-30

    Titanium oxynitride (TiN{sub x}O{sub y}) films were deposited on polyethylene terephthalate (PET) substrates by means of a reactive radio frequency (RF) magnetron sputtering system in which the power density and substrate bias were the varied parameters. Experimental results show that the deposited TiN{sub x}O{sub y} films exhibited an amorphous or a columnar structure with fine crystalline dependent on power density. The deposition rate increases significantly in conjunction as the power density increases from 2 W/cm{sup 2} to 7 W/cm{sup 2}. The maximum deposition rate occurs, as the substrate bias is -40 V at a certain power densities chosen in this study. The film's roughness slightly decreases with increasing substrate bias. The TiN{sub x}O{sub y} films deposited at power densities above 4 W/cm{sup 2} show a steady Ti:N:O ratio of about 1:1:0.8. The water vapor and oxygen transmission rates of the TiN{sub x}O{sub y} films reach values as low as 0.98 g/m{sup 2}-day-atm and 0.60 cm{sup 3}/m{sup 2}-day-atm which are about 6 and 47 times lower than those of the uncoated PET substrate, respectively. These transmission rates are comparable to those of DLC, carbon-based and Al{sub 2}O{sub 3} barrier films. Therefore, TiN{sub x}O{sub y} films are potential candidates to be used as a gas permeation barrier for PET substrate.

  18. Resonance hairpin and Langmuir probe-assisted laser photodetachment measurements of the negative ion density in a pulsed dc magnetron discharge

    Energy Technology Data Exchange (ETDEWEB)

    Bradley, James W.; Dodd, Robert; You, S.-D.; Sirse, Nishant; Karkari, Shantanu Kumar [Department of Electrical Engineering and Electronics, University of Liverpool, Liverpool (United Kingdom); National Centre for Plasma Science and Technology, Dublin City University, Dublin 9, Republic of Ireland (Ireland); National Centre for Plasma Science and Technology, Dublin City University, Dublin 9, Republic of Ireland and Institute for Plasma Research, Bhat Gandhinagar, Gujarat (India)

    2011-05-15

    The time-resolved negative oxygen ion density n{sub -} close to the center line in a reactive pulsed dc magnetron discharge (10 kHz and 50% duty cycle) has been determined for the first time using a combination of laser photodetachment and resonance hairpin probing. The discharge was operated at a power of 50 W in 70% argon and 30% oxygen gas mixtures at 1.3 Pa pressure. The results show that the O{sup -} density remains pretty constant during the driven phase of the discharge at values typically below 5x10{sup 14} m{sup -3}; however, in the off-time, the O{sup -} density grows reaching values several times those in the on-time. This leads to the negative ion fraction (or degree of electronegativity) {alpha}=n{sub -}/n{sub e} being higher in the off phase (maximum value {alpha}{approx}1) than in the on phase ({alpha}=0.05-0.3). The authors also see higher values of {alpha} at positions close to the magnetic null than in the more magnetized region of the plasma. This fractional increase in negative ion density during the off-phase is attributed to the enhanced dissociative electron attachment of highly excited oxygen molecules in the cooling plasma. The results show that close to the magnetic null the photodetached electron density decays quickly after the laser pulse, followed by a slow decay over a few microseconds governed by the negative ion temperature. However, in the magnetized regions of the plasma, this decay is more gradual. This is attributed to the different cross-field transport rates for electrons in these two regions. The resonance hairpin probe measurements of the photoelectron densities are compared directly to photoelectron currents obtained using a conventional Langmuir probe. There is good agreement in the general trends, particularly in the off-time.

  19. Structural and optical properties of DC magnetron sputtered ZnO films on glass substrate and their modification by Ag ions implantation

    Science.gov (United States)

    Ahmad, R.; Afzal, Naveed; Amjad, U.; Jabbar, S.; Hussain, T.; Hussnain, A.

    2017-07-01

    This work is focused on investigating the effects of deposition time and Ag ions implantation on structural and optical properties of ZnO film. The ZnO film was prepared on glass substrate by pulsed DC magnetron sputtering of pure Zn target in reactive oxygen environment for 2 h, 3 h, 4 h and 5 h respectively. X-ray diffraction results revealed polycrystalline ZnO film whose crystallinity was improved with increase of the deposition time. The morphological features indicated agglomeration of smaller grains into larger ones by increasing the deposition time. The UV-vis spectroscopy analysis depicted a small decrease in the band gap of ZnO from 3.36 eV to 3.27 eV with increase of deposition time. The Ag ions implantation in ZnO films deposited for 5 h on glass was carried out by using Pelletron Accelerator at different ions fluences ranging from 1  ×  1011 ions cm-2 to 2  ×  1012 ions cm-2. XRD patterns of Ag ions implanted ZnO did not show significant change in crystallite size by increasing ions fluence from 1  ×  1011 ions cm-2 to 5  ×  1011 ions cm-2. However, with further increase of the ions fluence, the crystallite size was decreased. The band gap of Ag ions implanted ZnO indicated anomalous variations with increase of the ions fluence.

  20. Effect of Nitrogen Content on Physical and Chemical Properties of TiN Thin Films Prepared by DC Magnetron Sputtering with Supported Discharge

    Science.gov (United States)

    Kavitha, A.; Kannan, R.; Gunasekhar, K. R.; Rajashabala, S.

    2017-10-01

    Amorphous titanium nitride (TiN) thin films have been prepared on silicon (Si) and glass substrates by direct-current (DC) reactive magnetron sputtering with a supported discharge (triode). Nitrogen gas (N2) at partial pressure of 0.3 Pa, 0.4 Pa, 0.5 Pa, and 0.6 Pa was used to prepare the TiN thin films, maintaining total pressure of argon and N2 of about 0.7 Pa. The chemical, microstructural, optical, and electrical properties of the TiN thin films were systematically studied. Presence of different phases of Ti with nitrogen (N), oxygen (O2), and carbon (C) elements was revealed by x-ray photoelectron spectroscopy characterization. Increase in the nitrogen pressure from 0.3 Pa to 0.6 Pa reduced the optical bandgap of the TiN thin film from 2.9 eV to 2.7 eV. Photoluminescence study showed that TiN thin film deposited at N2 partial pressure of 0.3 Pa exhibited three shoulder peaks at 330 nm, 335 nm, and 340 nm, which disappeared when the sample was deposited with N2 partial pressure of 0.6 Pa. Increase in the nitrogen content decreased the electrical resistivity of the TiN thin film from 3200 μΩ cm to 1800 μΩ cm. Atomic force microscopy studies of the TiN thin films deposited with N2 partial pressure of 0.6 Pa showed a uniform surface pattern associated with accumulation of fine grains. The results and advantages of this method of preparing TiN thin films are also reported.

  1. Preliminary study of CdTe and CdTe:Cu thin films nanostructures deposited by using DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Marwoto, Putut; Made, D. P. Ngurah; Sugianto [Departement of Physics, Faculty of Mathematics and Natural Sciences, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia); Wibowo, Edy; Astuti, Santi Yuli; Aryani, Nila Prasetya [Materials Research Group, Laboratory of Thin Film, Department of Physics, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia); Othaman, Zulkafli [Departement of Physics, Universiti Teknologi Malaysia (UTM), Skudai, Johor Bahru (Malaysia)

    2013-09-03

    Growth and properties of CdTe and CdTe:Cu thin films nanostrucures deposited by using dc magnetron sputtering are reported. Scanning electron microscope (SEM) was used to observe the surface morphologies of the thin films. At growth conditions of 250 °C and 14 W, CdTe films did not yet evenly deposited. However, at growth temperature and plasma power of 325 °C and 43 W, both CdTe and CdTe:Cu(2%) have deposited on the substrates. In this condition, the morphology of the films indicate that the films have a grain-like nanostructures. Grain size diameter of about 200 nm begin to appear on top of the films. Energy Dispersive X-rays spectroscopy (EDX) was used to investigate chemical elements of the Cu doped CdTe film deposited. It was found that the film deposited consist of Cd, Te and Cu elements. XRD was used to investigate the full width at half maximum (FWHM) values of the thin films deposited. The results show that CdTe:Cu(2%) thin film has better crystallographic properties than CdTe thin film. The UV-Vis spectrometer was used to investigate the optical properties of thin films deposited. The transmittance spectra showed that transmittance of CdTe:Cu(2%) film is lower than CdTe film. It was found that the bandgap energy of CdTe and CdTe:Cu(2%) thin films of about 1.48 eV.

  2. Electrical resistivity of CuAlMo thin films grown at room temperature by dc magnetron sputtering

    Science.gov (United States)

    Birkett, Martin; Penlington, Roger

    2016-07-01

    We report on the thickness dependence of electrical resistivity of CuAlMo films grown by dc magnetron sputtering on glass substrates at room temperature. The electrical resistance of the films was monitored in situ during their growth in the thickness range 10-1000 nm. By theoretically modelling the evolution of resistivity during growth we were able to gain an insight into the dominant electrical conduction mechanisms with increasing film thickness. For thicknesses in the range 10-25 nm the electrical resistivity is found to be a function of the film surface roughness and is well described by Namba’s model. For thicknesses of 25-40 nm the experimental data was most accurately fitted using the Mayadas and Shatkes model which accounts for grain boundary scattering of the conduction electrons. Beyond 40 nm, the thickness of the film was found to be the controlling factor and the Fuchs-Sonheimer (FS) model was used to fit the experimental data, with diffuse scattering of the conduction electrons at the two film surfaces. By combining the Fuchs and Namba (FN) models a suitable correlation between theoretical and experimental resistivity can be achieved across the full CuAlMo film thickness range of 10-1000 nm. The irreversibility of resistance for films of thickness >200 nm, which demonstrated bulk conductivity, was measured to be less than 0.03% following subjection to temperature cycles of -55 and +125 °C and the temperature co-efficient of resistance was less than ±15 ppm °C-1.

  3. Highly stable hydrogenated gallium-doped zinc oxide thin films grown by DC magnetron sputtering using H2/Ar gas

    International Nuclear Information System (INIS)

    Takeda, Satoshi; Fukawa, Makoto

    2004-01-01

    The effects of water partial pressure (P H 2 O ) on electrical and optical properties of Ga-doped ZnO films grown by DC magnetron sputtering were investigated. With increasing P H 2 O , the resistivity (ρ) of the films grown in pure Ar gas (Ar-films) significantly increased due to the decrease in both free carrier density and Hall mobility. The transmittance in the wavelength region of 300-400 nm for the films also increased with increasing P H 2 O . However, no significant P H 2 O dependence of the electrical and optical properties was observed for the films grown in H 2 /Ar gas mixture (H 2 /Ar-films). Secondary ion mass spectrometry (SIMS) and X-ray diffraction (XRD) analysis revealed that hydrogen concentration in the Ar-films increased with increasing P H 2 O and grain size of the films decreases with increasing the hydrogen concentration. These results indicate that the origin of the incorporated hydrogen is attributed to the residual water vapor in the coating chamber, and that the variation of ρ and transmittance along with P H 2 O of the films resulted from the change in the grain size. On the contrary, the hydrogen concentration in H 2 /Ar-films was almost constant irrespective of P H 2 O and the degree of change in the grain size of the films versus P H 2 O was much smaller than that of Ar-films. These facts indicate that the hydrogen primarily comes from H 2 gas and the adsorption species due to H 2 gas preferentially adsorb to the growing film surface over residual water vapor. Consequently, the effects of P H 2 O on the crystal growth are reduced

  4. The role of target-to-substrate distance on the DC magnetron sputtered zirconia thin films' bioactivity

    Energy Technology Data Exchange (ETDEWEB)

    Thaveedeetrakul, Arisara [Department of Chemical Engineering, King Mongkut' s University of Technology Thonburi, Bangkok (Thailand); Witit-anun, Nirun [Department of Physics, Burapha University, Chon Buri (Thailand); Thailand Center of Excellence in Physics, CHE, Ministry of Education, Bangkok (Thailand); Boonamnuayvitaya, Virote, E-mail: virote.boo@kmutt.ac.th [Department of Chemical Engineering, King Mongkut' s University of Technology Thonburi, Bangkok (Thailand)

    2012-01-15

    Zirconium dioxide thin films were deposited on 316L-stainless steel type substrates using DC unbalanced magnetron sputtering. The process parameter of this work was the target-to-substrate distance (d{sub t-s}), which was varied from 60 to 120 mm. The crystal structure and surface topography of zirconium dioxide thin films were characterized by X-ray diffraction (XRD) and atomic force microscopy (AFM). The results demonstrate that all of the ZrO{sub 2} thin films are composed monoclinic phase. The film sputtered at short d{sub t-s} (60 mm) shows a rather heterogeneous, uneven surface. The grain size, roughness, and thickness of thin films were decreased by increasing d{sub t-s}. The bioactivity was assessed by investigating the formation of hydroxyapatite (Ca{sub 10}(PO{sub 4}){sub 6}(OH){sub 2}) on the thin film surface soaked in simulated body fluids (SBF) for 7 days. XRD and scanning electron microscopy (SEM) were used to verify the formation of apatite layers on the samples. Bone-like apatites were formed on the surface of the ZrO{sub 2} thin film in SBF immersion experiments. A nanocrystalline hydroxyapatite (HA) with a particle size of 2-4 {mu}m was deposited. Higher crystallinity of HA on the surface was observed when the distance d{sub t-s} increased to more than 80 mm. Therefore, it seems that a d{sub t-s} greater than 80 mm is an important sputtering condition for inducing HA on the zirconia film.

  5. Thermal conductivity of nitride films of Ti, Cr, and W deposited by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Jagannadham, Kasichainula

    2015-01-01

    Nitride films of Ti, Cr, and W were deposited using reactive magnetron sputtering from metal targets in argon and nitrogen plasma. TiN films with (200) orientation were achieved on silicon (100) at the substrate temperature of 500 and 600 °C. The films were polycrystalline at lower temperature. An amorphous interface layer was observed between the TiN film and Si wafer deposited at 600 °C. TiN film deposited at 600 °C showed the nitrogen to Ti ratio to be near unity, but films deposited at lower temperature were nitrogen deficient. CrN film with (200) orientation and good stoichiometry was achieved at 600 °C on Si(111) wafer but the film deposited at 500 °C showed cubic CrN and hexagonal Cr 2 N phases with smaller grain size and amorphous back ground in the x-ray diffraction pattern. An amorphous interface layer was not observed in the cubic CrN film on Si(111) deposited at 600 °C. Nitride film of tungsten deposited at 600 °C on Si(100) wafer was nitrogen deficient, contained both cubic W 2 N and hexagonal WN phases with smaller grain size. Nitride films of tungsten deposited at 500 °C were nonstoichiometric and contained cubic W 2 N and unreacted W phases. There was no amorphous phase formed along the interface for the tungsten nitride film deposited at 600 °C on the Si wafer. Thermal conductivity and interface thermal conductance of all the nitride films of Ti, Cr, and W were determined by transient thermoreflectance technique. The thermal conductivity of the films as function of deposition temperature, microstructure, nitrogen stoichiometry and amorphous interaction layer at the interface was determined. Tungsten nitride film containing both cubic and hexagonal phases was found to exhibit much higher thermal conductivity and interface thermal conductance. The amorphous interface layer was found to reduce effective thermal conductivity of TiN and CrN films

  6. The properties of TiN ultra-thin films grown on SiO{sub 2} substrate by reactive high power impulse magnetron sputtering under various growth angles

    Energy Technology Data Exchange (ETDEWEB)

    Shayestehaminzadeh, S., E-mail: ses30@hi.is [Science Institute, University of Iceland, Dunhaga 3, IS-107 Reykjavik (Iceland); Tryggvason, T.K. [Science Institute, University of Iceland, Dunhaga 3, IS-107 Reykjavik (Iceland); Karlsson, L. [School of Engineering and Science, Jacobs University Bremen, Campus Ring 1, 28759 Bremen (Germany); Olafsson, S. [Science Institute, University of Iceland, Dunhaga 3, IS-107 Reykjavik (Iceland); Gudmundsson, J.T. [Science Institute, University of Iceland, Dunhaga 3, IS-107 Reykjavik (Iceland); University of Michigan-Shanghai Jiao Tong University, University Joint Institute, Shanghai Jiao Tong University, 800 Dong Chuan Road, Shanghai 200240 (China)

    2013-12-02

    Thin TiN films were grown on SiO{sub 2} by reactive high power impulse magnetron sputtering (HiPIMS) and conventional dc magnetron sputtering (dcMS) while varying the angle between the target and the substrate surface from 0° (on-axis growth) to 90° (off-axis growth). Surface morphology and structural characterization were carried out using X-ray diffraction and reflection methods and the film properties were compared. The dcMS process shows higher growth rate than the HiPIMS process for on-axis grown films but the dcMS growth rate drops drastically for off-axis growth while the HiPIMS growth rate decreases slowly with increased angle between target and substrate for off-axis growth and becomes comparable to the dcMS growth rate. The dcMS grown films exhibit angle dependence in the density and surface roughness while the HiPIMS process creates denser and smoother films that are less angle dependent in all aspects. It was observed that the HiPIMS grown films remain poly-crystalline for all angles of rotation while the dcMS grown films are somewhat amorphous after 60°. The [111] and [200] grain sizes are comparable to the total film thickness in the HiPIMS grown films for all angles of rotation. In the case of dcMS, the [111], [200] and [220] grain sizes are roughly of the same size and much smaller than the total thickness for all growth angles except at 60° and higher. - Highlights: • TiN films were grown on SiO{sub 2} by HiPIMS and dcMS under various growth angles. • Influence of growth angle α = 0–90° on deposition rate and film quality was studied. • The HiPIMS process produces denser and smoother films for all growth angles. • At α = 0°, the growth rate of HiPIMS is 25% of dcMS while it is 50% at 90°. • The HiPIMS grown films remain poly-crystalline for all growth angles.

  7. Effects of oxygen addition in reactive cluster beam deposition of tungsten by magnetron sputtering with gas aggregation

    International Nuclear Information System (INIS)

    Polášek, J.; Mašek, K.; Marek, A.; Vyskočil, J.

    2015-01-01

    In this work, we investigated the possibilities of tungsten and tungsten oxide nanoclusters generation by means of non-reactive and reactive magnetron sputtering with gas aggregation. It was found that in pure argon atmosphere, cluster aggregation proceeded in two regimes depending on argon pressure in the aggregation chamber. At the lower pressure, cluster generation was dominated by two-body collisions yielding larger clusters (about 5.5 nm in diameter) at lower rate. At higher pressures, cluster generation was dominated by three-body collisions yielding smaller clusters (3–4 nm in diameter) at higher rate. The small amount of oxygen admixture in the aggregation chamber had considerable influence on cluster aggregation process. At certain critical pressure, the presence of oxygen led to the raise of deposition rate and cluster size. Resulting clusters were composed mostly of tungsten trioxide. The oxygen pressure higher than critical led to the target poisoning and the decrease in the sputtering rate. Critical oxygen pressure decreased with increasing argon pressure, suggesting that cluster aggregation process was influenced by atomic oxygen species (namely, O"− ion) generated by oxygen–argon collisions in the magnetron plasma. - Highlights: • Formation of tungsten and tungsten oxide clusters was observed. • Two modes of cluster aggregation in pure argon atmosphere were found. • Dependence of cluster deposition speed and size on oxygen admixture was observed. • Changes of dependence on oxygen with changing argon pressure were described.

  8. Effects of oxygen addition in reactive cluster beam deposition of tungsten by magnetron sputtering with gas aggregation

    Energy Technology Data Exchange (ETDEWEB)

    Polášek, J., E-mail: xpolasekj@seznam.cz [Department of Surface and Plasma Science, Faculty of Mathematics and Physic, Charles University, V Holešovičkách 2, Prague 8, CZ-18000 (Czech Republic); Mašek, K. [Department of Surface and Plasma Science, Faculty of Mathematics and Physic, Charles University, V Holešovičkách 2, Prague 8, CZ-18000 (Czech Republic); Marek, A.; Vyskočil, J. [HVM Plasma Ltd., Na Hutmance 2, Prague 5, CZ-158 00 (Czech Republic)

    2015-09-30

    In this work, we investigated the possibilities of tungsten and tungsten oxide nanoclusters generation by means of non-reactive and reactive magnetron sputtering with gas aggregation. It was found that in pure argon atmosphere, cluster aggregation proceeded in two regimes depending on argon pressure in the aggregation chamber. At the lower pressure, cluster generation was dominated by two-body collisions yielding larger clusters (about 5.5 nm in diameter) at lower rate. At higher pressures, cluster generation was dominated by three-body collisions yielding smaller clusters (3–4 nm in diameter) at higher rate. The small amount of oxygen admixture in the aggregation chamber had considerable influence on cluster aggregation process. At certain critical pressure, the presence of oxygen led to the raise of deposition rate and cluster size. Resulting clusters were composed mostly of tungsten trioxide. The oxygen pressure higher than critical led to the target poisoning and the decrease in the sputtering rate. Critical oxygen pressure decreased with increasing argon pressure, suggesting that cluster aggregation process was influenced by atomic oxygen species (namely, O{sup −} ion) generated by oxygen–argon collisions in the magnetron plasma. - Highlights: • Formation of tungsten and tungsten oxide clusters was observed. • Two modes of cluster aggregation in pure argon atmosphere were found. • Dependence of cluster deposition speed and size on oxygen admixture was observed. • Changes of dependence on oxygen with changing argon pressure were described.

  9. Observation of a periodic runaway in the reactive Ar/O2 high power impulse magnetron sputtering discharge

    Directory of Open Access Journals (Sweden)

    Seyedmohammad Shayestehaminzadeh

    2015-11-01

    Full Text Available This paper reports the observation of a periodic runaway of plasma to a higher density for the reactive discharge of the target material (Ti with moderate sputter yield. Variable emission of secondary electrons, for the alternating transition of the target from metal mode to oxide mode, is understood to be the main reason for the runaway occurring periodically. Increasing the pulsing frequency can bring the target back to a metal (or suboxide mode, and eliminate the periodic transition of the target. Therefore, a pulsing frequency interval is defined for the reactive Ar/O2 discharge in order to sustain the plasma in a runaway-free mode without exceeding the maximum power that the magnetron can tolerate.

  10. Reduction of DC-link Capacitor in Case of Cascade Multilevel Converters by means of Reactive Power Control

    DEFF Research Database (Denmark)

    Gohil, Ghanshyamsinh Vijaysinh; Wang, Huai; Liserre, Marco

    2014-01-01

    A method to selectively control the amount of dc link voltage ripple by processing desired reactive power by a DC/DC converter in isolated AC/DC or AC/DC/AC system is proposed. The concept can reduce the dc link capacitors used for balancing the input and output power and thereby limiting...... the voltage ripple. It allows the use of smaller dc link capacitor and hence a longer lifetime and at the same time high power density and low cost can be achieved. The isolated DC/DC converter is controlled to process the desired reactive power in addition to the active power. The control system to achieve...

  11. Effect of Oxygen Partial Pressure on the Electrical and Optical Properties of DC Magnetron Sputtered Amorphous TiO2 Films

    OpenAIRE

    Chandra Sekhar, M.; Kondaiah, P.; Radha Krishna, B.; Uthanna, S.

    2013-01-01

    Titanium dioxide (TiO2) thin films were deposited on p-Si (100) and Corning glass substrates held at room temperature by DC magnetron sputtering at different oxygen partial pressures in the range 9 × 10−3–9 × 10−2 Pa. The influence of oxygen partial pressure on the structural, electrical, and optical properties of the deposited films was systematically studied. XPS studies confirmed that the film formed at an oxygen partial pressure of 6×10−2 Pa was nearly stoichiometric. TiO2 films formed at...

  12. Preparation and characterization of photocatalytic performance of hierarchical heterogeneous nanostructured ZnO/TiO2 films made by DC magnetron sputtering

    International Nuclear Information System (INIS)

    Le Phuc Quy; Vu Thi Hanh Thu

    2013-01-01

    With the aim to enhance photocatalytic properties and anti-Ecoli bacteria abilities of TiO 2 thin films; hierarchical heterogeneous nanostructured ZnO/TiO 2 (HN s ) films were deposited by DC magnetron sputtering. The obtained results showed that both the photocatalytic performance and anti-Ecoli bacteria ability of HN s films exhibited enhancement in comparison with standard TiO 2 films. This enhancement was explained due to the reduction of the electron - hole recombination and the red shift of absorption edge of the HNs films. (author)

  13. Ion beam analysis, corrosion resistance and nanomechanical properties of TiAlCN/CN{sub x} multilayer grown by reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Alemón, B.; Flores, M. [Departamento de Ingeniería de Proyectos, CUCEI, Universidad de Guadalajara, J. Guadalupe Zuno 48, Los Belenes, Zapopan, Jal. 45101 (Mexico); Canto, C. [Instituto de Física, UNAM, Avenida de la Investigación S/N, Coyoacán, Mexico, DF 04510 (Mexico); Andrade, E., E-mail: andrade@fisica.unam.mx [Instituto de Física, UNAM, Avenida de la Investigación S/N, Coyoacán, Mexico, DF 04510 (Mexico); Lucio, O.G. de [Instituto de Física, UNAM, Avenida de la Investigación S/N, Coyoacán, Mexico, DF 04510 (Mexico); Rocha, M.F. [ESIME-Z, Instituto Politécnico Nacional, ALM Zacatenco, Mexico, DF 07738 (Mexico); Broitman, E. [Thin Films Physics Division, IFM, Linköping University, SE-58183 Linköping (Sweden)

    2014-07-15

    A novel TiAlCN/CN{sub x} multilayer coating, consisting of nine TiAlCN/CN{sub x} periods with a top layer 0.5 μm of CN{sub x}, was designed to enhance the corrosion resistance of CoCrMo biomedical alloy. The multilayers were deposited by dc and RF reactive magnetron sputtering from Ti{sub 0.5}Al{sub 0.5} and C targets respectively in a N{sub 2}/Ar plasma. The corrosion resistance and mechanical properties of the multilayer coatings were analyzed and compared to CoCrMo bulk alloy. Ion beam analysis (IBA) and X-ray diffraction tests were used to measure the element composition profiles and crystalline structure of the films. Corrosion resistance was evaluated by means of potentiodynamic polarization measurements using simulated body fluid (SBF) at typical body temperature and the nanomechanical properties of the multilayer evaluated by nanoindentation tests were analyzed and compared to CoCrMo bulk alloy. It was found that the multilayer hardness and the elastic recovery are higher than the substrate of CoCrMo. Furthermore the coated substrate shows a better general corrosion resistance than that of the CoCrMo alloy alone with no observation of pitting corrosion.

  14. Corrosion resistance of zirconium oxynitride coatings deposited via DC unbalanced magnetron sputtering and spray pyrolysis-nitriding

    Energy Technology Data Exchange (ETDEWEB)

    Cubillos, G.I., E-mail: gcubillos@unal.edu.co [Department of Chemistry, Group of Materials and Chemical Processes, Universidad Nacional de Colombia, Av. Cra. 30 No 45-03, Bogotá (Colombia); Bethencourt, M., E-mail: manuel.bethencourt@uca.es [Department of Materials Science, Metallurgy Engineering and Inorganic Chemistry, International Campus of Excellence of the Sea - CEI-MAR, University of Cadiz, Avda. República Saharaui s/n, 11510 Puerto Real, Cádiz (Spain); Olaya, J.J., E-mail: jjolayaf@unal.edu.co [Faculty of Engineering, Group of Materials and Chemical Processes, Universidad Nacional de Colombia, Av. Cra. 30 No 45-03, Bogotá (Colombia)

    2015-02-01

    Highlights: • New ZrO{sub x}N{sub y} films were deposited on stainless steel 316L using PSY-N and UBMS. • ZrO{sub x}N{sub y} rhombohedral polycrystalline film grew with PSY-N. • Zr{sub 2}ON{sub 2} crystalline structures, mostly oriented along the (2 2 2) plane, grew with UBMS. • Layers improved corrosion behavior in NaCl media, especially those deposited by UBMS. - Abstract: ZrO{sub x}N{sub y}/ZrO{sub 2} thin films were deposited on stainless steel using two different methods: ultrasonic spray pyrolysis-nitriding (SPY-N) and the DC unbalanced magnetron sputtering technique (UBMS). Using the first method, ZrO{sub 2} was initially deposited and subsequently nitrided in an anhydrous ammonia atmosphere at 1023 K at atmospheric pressure. For UBMS, the film was deposited in an atmosphere of air/argon with a Φair/ΦAr flow ratio of 3.0. Structural analysis was carried out through X-ray diffraction (XRD), and morphological analysis was done through scanning electron microscopy (SEM) and atomic force microscopy (AFM). Chemical analysis was carried out using X-ray photoelectron spectroscopy (XPS). ZrO{sub x}N{sub y} rhombohedral polycrystalline film was produced with spray pyrolysis-nitriding, whereas using the UBMS technique, the oxynitride films grew with cubic Zr{sub 2}ON{sub 2} crystalline structures preferentially oriented along the (2 2 2) plane. Upon chemical analysis of the surface, the coatings exhibited spectral lines of Zr3d, O1s, and N1s, characteristic of zirconium oxynitride/zirconia. SEM analysis showed the homogeneity of the films, and AFM showed morphological differences according to the deposition technique of the coatings. Zirconium oxynitride films enhanced the stainless steel's resistance to corrosion using both techniques. The protective efficacy was evaluated using electrochemical techniques based on linear polarization (LP). The results indicated that the layers provide good resistance to corrosion when exposed to chloride

  15. Ultrahigh vacuum dc magnetron sputter-deposition of epitaxial Pd(111)/Al2O3(0001) thin films.

    Science.gov (United States)

    Aleman, Angel; Li, Chao; Zaid, Hicham; Kindlund, Hanna; Fankhauser, Joshua; Prikhodko, Sergey V; Goorsky, Mark S; Kodambaka, Suneel

    2018-05-01

    Pd(111) thin films, ∼245 nm thick, are deposited on Al 2 O 3 (0001) substrates at ≈0.5 T m , where T m is the Pd melting point, by ultrahigh vacuum dc magnetron sputtering of Pd target in pure Ar discharges. Auger electron spectra and low-energy electron diffraction patterns acquired in situ from the as-deposited samples reveal that the surfaces are compositionally pure 111-oriented Pd. Double-axis x-ray diffraction (XRD) ω-2θ scans show only the set of Pd 111 peaks from the film. In triple-axis high-resolution XRD, the full width at half maximum intensity Γ ω of the Pd 111 ω-rocking curve is 630 arc sec. XRD 111 pole figure obtained from the sample revealed six peaks 60°-apart at a tilt angles corresponding to Pd 111 reflections. XRD ϕ scans show six 60°-rotated 111 peaks of Pd at the same ϕ angles for 11[Formula: see text]3 of Al 2 O 3 based on which the epitaxial crystallographic relationships between the film and the substrate are determined as [Formula: see text]ǁ[Formula: see text] with two in-plane orientations of [Formula: see text]ǁ[Formula: see text] and [Formula: see text]ǁ[Formula: see text]. Using triple axis symmetric and asymmetric reciprocal space maps, interplanar spacings of out-of-plane (111) and in-plane (11[Formula: see text]) are found to be 0.2242 ± 0.0003 and 0.1591 ± 0.0003 nm, respectively. These values are 0.18% lower than 0.2246 nm for (111) and the same, within the measurement uncertainties, as 0.1588 nm for (11[Formula: see text]) calculated from the bulk Pd lattice parameter, suggesting a small out-of-plane compressive strain and an in-plane tensile strain related to the thermal strain upon cooling the sample from the deposition temperature to room temperature. High-resolution cross-sectional transmission electron microscopy coupled with energy dispersive x-ray spectra obtained from the Pd(111)/Al 2 O 3 (0001) samples indicate that the Pd-Al 2 O 3 interfaces are essentially atomically abrupt and

  16. Generation of positive and negative oxygen ions in magnetron discharge during reactive sputtering of alumina

    Czech Academy of Sciences Publication Activity Database

    Pokorný, Petr; Bulíř, Jiří; Lančok, Ján; Musil, Jindřich; Novotný, Michal

    2010-01-01

    Roč. 7, č. 11 (2010), s. 910-914 ISSN 1612-8850 R&D Projects: GA AV ČR IAA100100718; GA AV ČR KAN400100653; GA ČR GP202/09/P324 Institutional research plan: CEZ:AV0Z10100522 Keywords : aluminium oxide * ion-energy distribution function * magnetron * mass spectrometry * pulsed discharges Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.643, year: 2010

  17. Reactive magnetron sputtering of Si-C-N films with controlled mechanical and optical properties

    Czech Academy of Sciences Publication Activity Database

    Vlček, J.; Kormunda, M.; Čížek, J.; Soukup, Z.; Peřina, Vratislav; Zemek, Josef

    2003-01-01

    Roč. 12, č. 8 (2003), s. 1287-1294 ISSN 0925-9635 R&D Projects: GA MŠk ME 203; GA MŠk OC 527.90 Institutional research plan: CEZ:MSM 235200002 Keywords : silicon-carbon-nitride films * magnetron co-sputtering Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders Impact factor: 1.867, year: 2003

  18. Molybdenum thin film deposited by in-line DC magnetron sputtering as a back contact for Cu(In,Ga)Se{sub 2} solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Li Zhaohui; Cho, Eou-Sik [Department of Electronics Engineering, Kyungwon University, San 65, Bokjung-dong, Soojung-gu, Seongnam city, Kyunggi-do, 461-701 (Korea, Republic of); Kwon, Sang Jik, E-mail: sjkwon@kyungwon.ac.kr [Department of Electronics Engineering, Kyungwon University, San 65, Bokjung-dong, Soojung-gu, Seongnam city, Kyunggi-do, 461-701 (Korea, Republic of)

    2011-09-01

    In this paper, we reported the effect of the power and the working pressure on the molybdenum (Mo) films deposited using an in-line direct current (DC) magnetron sputtering system. The electrical and the structural properties of Mo film were improved by increasing DC power from 1 to 3 kW. On the other side, the resistivity of the Mo films became higher with the increasing working pressure. However, the adhesion property was improved when the working pressure was higher. In this work, in order to obtain an optimal Mo film as a back metal contact of Cu(In,Ga)Se{sub 2} (CIGS) solar cells, a bilayer Mo film was formed through the different film structures depending on the working pressure. The first layer was formed at a high pressure of 12 mTorr for a better adhesion and the second layer was formed at a low pressure of 3 mTorr for a lower resistivity.

  19. Ga-doped ZnO films deposited with varying sputtering powers and substrate temperatures by pulsed DC magnetron sputtering and their property improvement potentials

    International Nuclear Information System (INIS)

    Lee, Sanghun; Cheon, Dongkeun; Kim, Won-Jeong; Ham, Moon-Ho; Lee, Woong

    2012-01-01

    Ga-doped ZnO (GZO) transparent conductive oxide (TCO) films were deposited on glass substrates by pulsed DC magnetron sputtering with varying sputtering power and substrate temperature while fixing the Ga concentration in the sputtering target. The application of higher sputtering power by pulsed DC magnetrons sputtering at a moderate temperature of 423 K results in increased carrier concentration and mobility which accompanied improved doping efficiency and crystalline quality. Substrate temperature was found to be the more dominant parameter in controlling the electrical properties and crystallinity, while the sputtering power played synergistic auxiliary roles. Electrical and optical properties of the GZO TCO films fulfilled requirements for transparent electrodes, despite relatively low substrate temperature (423 K) and small thickness (100 nm). In an attempt to improve the electrical properties of the GZO films by hydrogen-treatment, it was observed that the substitutional Ga plays the complex role of carrier generator as donor and carrier suppressor deactivating the oxygen vacancy simultaneously, which would complicate the property improvement by increasing doping efficiency.

  20. Electrical Properties of DC Reactive Magnetron Sputtered ZnO:Al ...

    African Journals Online (AJOL)

    Films optical spectra were fitted with the Drude model to determine their charge carrier concentration, mobility and the alternating current (AC) resistivity. The highest values of mobility and charge carrier concentration were 8.31cm2/Vs and 2.14 x 1021cm-3 respectively. The lowest value of the AC resistivity was given by the ...

  1. Electrochromism in surface modified crystalline WO3 thin films grown by reactive DC magnetron sputtering

    Science.gov (United States)

    Karuppasamy, A.

    2013-10-01

    In the present work, tungsten oxide thin films were deposited at various oxygen chamber pressures (1.0-5.0 × 10-3 mbar) by maintaining the sputtering power density and argon pressure constant at 3.0 W/cm2 and 1.2 × 10-2 mbar, respectively. The role of surface morphology and porosity on the electrochromic properties of crystalline tungsten oxide thin films has been investigated. XRD and Raman studies reveal that all the samples post annealed at 450 ̊C in air for 3.0 h settle in monoclinic crystal system of tungsten oxide (W18O49). Though the phase of material is indifferent to oxygen pressure variations (PO2), morphology and film density shows a striking dependence on PO2. A systematic study on plasma (OES), morphology, optical and electrochromic properties of crystalline tungsten oxide reveal that the films deposited at PO2 of 2.0 × 10-3 mbar exhibit better coloration efficiency (58 cm2/C), electron/ion capacity (Qc: -25 mC/cm2), and reversibility (92%). This is attributed to the enhanced surface properties like high density of pores and fine particulates (100 nm) and to lesser bulk density of the film (ρ/ρo = 0.84) which facilitates the process of intercalation/de-intercalation of protons and electrons. These results show good promise toward stable and efficient crystalline tungsten oxide based electrochromic device applications.

  2. Deposition of TiN/CrN hard superlattices by reactive d.c. magnetron ...

    Indian Academy of Sciences (India)

    Unknown

    cal properties, as compared to single-layered structures, have been reported both for .... The top panel of figure 2 shows a ... supported by XRD data, which showed the loss of super- ... Though the cross-sectional transmission electron micro-.

  3. Process stabilization by peak current regulation in reactive high-power impulse magnetron sputtering of hafnium nitride

    International Nuclear Information System (INIS)

    Shimizu, T; Villamayor, M; Helmersson, U; Lundin, D

    2016-01-01

    A simple and cost effective approach to stabilize the sputtering process in the transition zone during reactive high-power impulse magnetron sputtering (HiPIMS) is proposed. The method is based on real-time monitoring and control of the discharge current waveforms. To stabilize the process conditions at a given set point, a feedback control system was implemented that automatically regulates the pulse frequency, and thereby the average sputtering power, to maintain a constant maximum discharge current. In the present study, the variation of the pulse current waveforms over a wide range of reactive gas flows and pulse frequencies during a reactive HiPIMS process of Hf-N in an Ar–N 2 atmosphere illustrates that the discharge current waveform is a an excellent indicator of the process conditions. Activating the reactive HiPIMS peak current regulation, stable process conditions were maintained when varying the N 2 flow from 2.1 to 3.5 sccm by an automatic adjustment of the pulse frequency from 600 Hz to 1150 Hz and consequently an increase of the average power from 110 to 270 W. Hf–N films deposited using peak current regulation exhibited a stable stoichiometry, a nearly constant power-normalized deposition rate, and a polycrystalline cubic phase Hf-N with (1 1 1)-preferred orientation over the entire reactive gas flow range investigated. The physical reasons for the change in the current pulse waveform for different process conditions are discussed in some detail. (paper)

  4. Photoelectron-spectroscopic and reactivity investigation of thin Pd-Sn films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Skala, T.; Veltruska, K.; Sedlacek, L.; Masek, K.; Matolinova, I.; Matolin, V.

    2007-01-01

    We have studied Pd-Sn layers with different composition prepared by magnetron sputtering. Layers were sputtered onto Al 2 O 3 and SiO 2 substrates and studied by X-ray photoelectron spectroscopy (XPS). Spectra confirmed that after vacuum annealing residual oxygen and carbon have been removed and bimetallic bonds have been created. The shift of Pd 3d 5/2 core level to higher binding energy followed by the peak narrowing in dependence on the composition was observed, accompanied by the shift of the Pd 4d in the valence band region, induced by hybridization of Pd-d and Sn-s,p states. Experiments carried out on a gas-flow reactor indicate increasing temperature of the CO oxidation with tin ratio in the alloy

  5. Deposition and characterization of TaAIN thin films by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Oliveira, G.B.; Fernandez, D.R.; Fontes Junior, A.S.; Felix, L.C.; Tentardini, E.K.; Silva Junior, A.H. da

    2016-01-01

    Phase stability, oxidation resistance and great mechanical properties are the main objectives when synthesizing protective coatings. The tantalum nitride (TaN) has aroused interest because of its high temperature stability, chemical inertness and thermal conductivity. However, it has a low hardness value when compared to other coatings. Researches has shown that one way to improvements in the properties of a thin film is by adding other elements in the deposition process. Therefore, the objective of this study was to deposit thin films of TaAlN by magnetron sputtering, changing the aluminum concentration of 2, 5, 7, to 14%. Then the coatings were characterized by EDS, RBS, GIXRD and nanohardness. In this study was found that the aluminum deposited did not change the oxidation resistance of the coating, and the highest value of hardness was 28 GPa for the sample with 14 at.%. (author)

  6. Properties of reactively radio frequency-magnetron sputtered (Zr,Sn)TiO4 dielectric films

    International Nuclear Information System (INIS)

    Huang, C.-L.; Hsu, C.-H.

    2004-01-01

    Zirconium tin titanium oxide doped 1 wt % ZnO thin films on n-type Si substrate were deposited by rf magnetron sputtering at a fixed rf power of 350 W with various argon-oxygen (Ar/O 2 ) mixture and different substrate temperatures. Electrical properties and microstructures of ZnO-doped (Zr 0.8 Sn 0.2 )TiO 4 thin films prepared by rf magnetron sputtering on n-type Si(100) substrates at different Ar/O 2 ratios and substrate temperatures have been investigated. The surface structural and morphological characteristics analyzed by x-ray diffraction, scanning electron microscopy, and atomic force microscope were sensitive to the deposition conditions, such as Ar/O 2 ratio (100/0-80/20) and substrate temperature (350 deg. C-450 deg. C). The selected-area diffraction pattern showed that the deposited films exhibited a polycrystalline microstructure. All films exhibited ZST (111) orientation perpendicular to the substrate surface and the grain size as well as the deposition rate of the films increased with the increase of both the Ar partial pressure and the substrate temperature. At a Ar/O 2 ratio of 100/0, rf power level of 350 W and substrate temperature of 450 deg. C, the Zr 0.8 Sn 0.2 TiO 4 films with 6.44 μm thickness possess a dielectric constant of 42 (at 10 MHz), a dissipation factor of 0.065 (at 10 MHz), and a leakage current density of 2x10 -7 A/cm 2 at an electrical field of 1 kV/cm

  7. ZnO film deposition by DC magnetron sputtering: Effect of target configuration on the film properties

    Energy Technology Data Exchange (ETDEWEB)

    Arakelova, E.; Khachatryan, A.; Kteyan, A.; Avjyan, K.; Grigoryan, S.

    2016-08-01

    Ballistic transport model for target-to-substrate atom transfer during magnetron sputter deposition was used to develop zinc target (cathode) configuration that enabled growth of uniform zinc oxide films on extensive surfaces and provided reproducibility of films characteristics irrespective of the cathode wear-out. The advantage of the developed target configuration for high-quality ZnO film deposition was observed in the sputtering pressure range of 5− 50 mTorr, and in the range of cathode-to-substrate distances 7–20 cm. Characteristics of the deposited films were demonstrated by using X-ray diffraction analysis, as well as optical and electrical measurements. - Highlights: • Change of target configuration for optimization of magnetron sputtering deposition is proposed. • Improvement of ZnO film properties due to use of this target is demonstrated. • This configuration provided reproducibility of the deposited films properties.

  8. Pulsed-DC selfsputtering of copper

    International Nuclear Information System (INIS)

    Wiatrowski, A; Posadowski, W M; Radzimski, Z J

    2008-01-01

    At standard magnetron sputtering conditions (argon pressure ∼0.5 Pa) inert gas particles are often entrapped in the formed films. Inert gas contamination can be eliminated by using the self-sustained magnetron sputtering process because it is done in the absence of the inert gas atmosphere. The self-sustained sputtering (SSS) gives also a unique condition during the transport of sputtered particles to the substrate. It is especially useful for filling high aspect ratio submicron scale structures for microelectronics. So far it has been shown that the self-sputtering process can be sustained in the DC operation mode (DC-SSS) only. The main disadvantage of DC-SSS process is instability related to possible arc formation. Usage of pulsed sputtering, similarly to reactive pulsed magnetron sputtering, could eliminate this problem. In this paper results of pulsed-DC self-sustained magnetron sputtering (pulsed DC-SSS) of copper are presented for the first time. The planar magnetron equipped with a 50 mm in diameter and 6 mm thick copper target was powered by DC-power supply modulated by power switch. The maximum target power was about 11 kW (∼550W/cm 2 ). The magnetron operation was investigated as a function of pulsing frequency (20-100 kHz) and duty factor (50-90%). The discharge extinction pressure was determined for these conditions. The plasma emission spectra (400-410nm range) and deposition rates were observed for both DC and pulsed DC sustained self-sputtering processes. The presented results illustrate that stable pulsed DC-SSS process can be obtained at pulsing frequency in the range of 60-100 kHz and duty factor of 70-90%

  9. Pulsed-DC selfsputtering of copper

    Science.gov (United States)

    Wiatrowski, A.; Posadowski, W. M.; Radzimski, Z. J.

    2008-03-01

    At standard magnetron sputtering conditions (argon pressure ~0.5 Pa) inert gas particles are often entrapped in the formed films. Inert gas contamination can be eliminated by using the self-sustained magnetron sputtering process because it is done in the absence of the inert gas atmosphere. The self-sustained sputtering (SSS) gives also a unique condition during the transport of sputtered particles to the substrate. It is especially useful for filling high aspect ratio submicron scale structures for microelectronics. So far it has been shown that the self-sputtering process can be sustained in the DC operation mode (DC-SSS) only. The main disadvantage of DC-SSS process is instability related to possible arc formation. Usage of pulsed sputtering, similarly to reactive pulsed magnetron sputtering, could eliminate this problem. In this paper results of pulsed-DC self-sustained magnetron sputtering (pulsed DC-SSS) of copper are presented for the first time. The planar magnetron equipped with a 50 mm in diameter and 6 mm thick copper target was powered by DC-power supply modulated by power switch. The maximum target power was about 11 kW (~550W/cm2). The magnetron operation was investigated as a function of pulsing frequency (20-100 kHz) and duty factor (50-90%). The discharge extinction pressure was determined for these conditions. The plasma emission spectra (400-410nm range) and deposition rates were observed for both DC and pulsed DC sustained self-sputtering processes. The presented results illustrate that stable pulsed DC-SSS process can be obtained at pulsing frequency in the range of 60-100 kHz and duty factor of 70-90%.

  10. Properties of TiO{sub 2} thin films deposited by rf reactive magnetron sputtering on biased substrates

    Energy Technology Data Exchange (ETDEWEB)

    Nezar, Sawsen, E-mail: snezar@cdta.dz [Equipe Plasma & Applications, Division des Milieux Ionisés et Lasers, Centre de Développement des Technologies Avancées, Cité du 20 Aout 1956, Baba Hassen, Alger (Algeria); Laboratoire des phénomènes de transfert, génie chimique, Faculté de Génie des procèdes, USTHB, BP 32 El-alia, Bab Ezzouar, Alger (Algeria); Saoula, Nadia [Equipe Plasma & Applications, Division des Milieux Ionisés et Lasers, Centre de Développement des Technologies Avancées, Cité du 20 Aout 1956, Baba Hassen, Alger (Algeria); Sali, Samira [Centre de Recherche en Technologie des Semi-conducteurs pour l’Energétique (CRTSE Algiers) (Algeria); Faiz, Mohammed; Mekki, Mogtaba [Physics Department, King Fahd University of Petroleum and Minerals, Dhahran (Saudi Arabia); Laoufi, Nadia Aïcha [Laboratoire des phénomènes de transfert, génie chimique, Faculté de Génie des procèdes, USTHB, BP 32 El-alia, Bab Ezzouar, Alger (Algeria); Tabet, Nouar [Qatar Environment and Energy Research Institute, Hamad Bin Khalifa University (HBKU), Doha (Qatar)

    2017-02-15

    Highlights: • TiO{sub 2} thin films were deposited on negatively biased substrates by rf magnetron sputtering technique. • The bias favors the formation of TiO{sub 2} crystalline phase. • The roughness of the films increases and the grain size decreases as the bias voltage is varied between (0 and −100 V). • XPS reveals the presence of adsorbed humidity of the surface and Ti{sup 4+} oxidation state in the as prepared samples. - Abstract: TiO{sub 2} thin films are of paramount importance due to their pervasive applications. In contrast to previous published works where the substrate was heated at high temperatures to obtain TiO{sub 2} crystalline phase, we show in this study that it is possible to deposit crystalline TiO{sub 2} thin films on biased and unbiased substrate at room temperature using reactive rf magnetron sputtering. The bias voltage was varied from 0 V to −100 V. The deposited films were characterized using X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), UV–vis spectroscopy, Raman spectroscopy, X-ray Photoelectron Spectroscopy (XPS) and atomic force microscopy (AFM). The average crystallite size was estimated using x-ray diffraction. The results showed that the application of negative bias affects the surface roughness of the films and favors the formation of the rutile phase. The root mean square roughness (R{sub rms}), the average grain size and the optical band gap of the films decreased as the substrate bias voltage was varied from 0 to −100 V. The UV–visible transmittance spectra showed that the films were transparent in the visible range and absorb strongly in the UV range. This study shows that biasing the substrate could be a promising and effective alternative to deposit TiO{sub 2} crystallized thin films of engineered properties at room temperature.

  11. A global plasma model for reactive deposition of compound films by modulated pulsed power magnetron sputtering discharges

    Science.gov (United States)

    Zheng, B. C.; Wu, Z. L.; Wu, B.; Li, Y. G.; Lei, M. K.

    2017-05-01

    A spatially averaged, time-dependent global plasma model has been developed to describe the reactive deposition of a TiAlSiN thin film by modulated pulsed power magnetron sputtering (MPPMS) discharges in Ar/N2 mixture gas, based on the particle balance and the energy balance in the ionization region, and considering the formation and erosion of the compound at the target surface. The modeling results show that, with increasing the N2 partial pressure from 0% to 40% at a constant working pressure of 0.3 Pa, the electron temperature during the strongly ionized period increases from 4 to 7 eV and the effective power transfer coefficient, which represents the power fraction that effectively heats the electrons and maintains the discharge, increases from about 4% to 7%; with increasing the working pressure from 0.1 to 0.7 Pa at a constant N2 partial pressure of 25%, the electron temperature decreases from 10 to 4 eV and the effective power transfer coefficient decreases from 8% to 5%. Using the modeled plasma parameters to evaluate the kinetic energy of arriving ions, the ion-to-neutral flux ratio of deposited species, and the substrate heating, the variations of process parameters that increase these values lead to an enhanced adatom mobility at the target surface and an increased input energy to the substrate, corresponding to the experimental observation of surface roughness reduction, the microstructure transition from the columnar structure to the dense featureless structure, and the enhancement of phase separation. At higher N2 partial pressure or lower working pressure, the modeling results demonstrate an increase in electron temperature, which shifts the discharge balance of Ti species from Ti+ to Ti2+ and results in a higher return fraction of Ti species, corresponding to the higher Al/Ti ratio of deposited films at these conditions. The modeling results are well correlated with the experimental observation of the composition variation and the microstructure

  12. Electrical properties of AlN{sub x}O{sub y} thin films prepared by reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Borges, J., E-mail: joelborges@fisica.uminho.pt [Centro de Fisica, Universidade do Minho, 4710-057 Braga (Portugal); Martin, N. [Institut FEMTO-ST, Departement MN2S, UMR 6174 (CNRS, UFC, ENSMM, UTBM) 32, Avenue de l' Observatoire 25044 BESANCON Cedex (France); Barradas, N.P.; Alves, E. [Instituto Superior Tecnico, Instituto Tecnologico Nuclear, E.N. 10, 2686-953 Sacavem (Portugal); Eyidi, D.; Beaufort, M.F.; Riviere, J.P. [Institut PPRIME, UPR 3346 CNRS-Universite de Poitiers-ENSMA, Departement de Physique et Mecanique des Materiaux, BP 30179 86962 Chasseneuil-Futuroscope Cedex (France); Vaz, F.; Marques, L. [Centro de Fisica, Universidade do Minho, 4710-057 Braga (Portugal)

    2012-08-31

    Direct current magnetron sputtering was used to produce AlN{sub x}O{sub y} thin films, using an aluminum target, argon and a mixture of N{sub 2} + O{sub 2} (17:3) as reactive gases. The partial pressure of the reactive gas mixture was increased, maintaining the discharge current constant. Within the two identified regimes of the target (metallic and compound), four different tendencies for the deposition rate were found and a morphological evolution from columnar towards cauliflower-type, ending up as dense and featureless-type films. The structure was found to be Al-type (face centered cubic) and the structural characterization carried out by X-ray diffraction and transmission electron microscopy suggested the formation of an aluminum-based polycrystalline phase dispersed in an amorphous aluminum oxide/nitride (or oxynitride) matrix. This type of structure, composition, morphology and grain size, were found to be strongly correlated with the electrical response of the films, which showed a gradual transition between metallic-like responses towards semiconducting and even insulating-type behaviors. A group of films with high aluminum content revealed a sharp decrease of the temperature coefficient of resistance (TCR) as the concentration ratio of non-metallic/aluminum atomic ratio increased. Another group of samples, where the non-metallic content became more important, revealed a smooth transition between positive and negative values of TCR. In order to test whether the oxynitride films have a unique behavior or simply a transition between the typical responses of aluminum and of those of the correspondent nitride and oxide, the electrical properties of the ternary oxynitride system were compared with AlN{sub x} and AlO{sub y} systems, prepared in similar conditions. - Highlights: Black-Right-Pointing-Pointer AlN{sub x}O{sub y} thin films were produced using magnetron sputtering. Black-Right-Pointing-Pointer AlN{sub x}O{sub y} film morphology, composition and

  13. In Situ and Ex Situ Studies of Molybdenum Thin Films Deposited by rf and dc Magnetron Sputtering as a Back Contact for CIGS Solar Cells

    Directory of Open Access Journals (Sweden)

    K. Aryal

    2012-01-01

    Full Text Available Molybdenum thin films were deposited by rf and dc magnetron sputtering and their properties analyzed with regards to their potential application as a back contact for CIGS solar cells. It is shown that both types of films tend to transition from tensile to compressive strain when the deposition pressure increases, while the conductivity and the grain size decreas. The nucleation of the films characterized by in situ and real time spectroscopic ellipsometry shows that both films follow a Volmer-Weber growth, with a higher surface roughness and lower deposition rate for the rf deposited films. The electronic relaxation time was then extracted as a function of bulk layer thickness for rf and dc films by fitting each dielectric function to a Drude free-electron model combined with a broad Lorentz oscillator. The values were fitted to a conical growth mode and demonstrated that the rf-deposited films have already smaller grains than the dc films when the bulk layer thickness is 30 nm.

  14. Effect of working pressure on corrosion behavior of nitrogen doped diamond-like carbon thin films deposited by DC magnetron sputtering.

    Science.gov (United States)

    Khun, N W; Liu, E

    2011-06-01

    Nitrogen doped diamond-like carbon thin films were deposited on highly conductive p-silicon(100) substrates using a DC magnetron sputtering deposition system by varying working pressure in the deposition chamber. The bonding structure, adhesion strength, surface roughness and corrosion behavior of the films were investigated by using X-ray photoelectron spectroscopy, micro-Raman spectroscopy, micro-scratch test, atomic force microscopy and potentiodynamic polarization test. A 0.6 M NaCl electrolytic solution was used for the corrosion tests. The optimum corrosion resistance of the films was found at a working pressure of 7 mTorr at which a good balance between the kinetics of the sputtered ions and the surface mobility of the adatoms promoted a microstructure of the films with fewer porosities.

  15. Investigation of physical properties and surface morphology of Cu nanolayer deposited on glass and (Al, Fe) thin films by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Eslami, P.A. [Islamic Azad Univ., North Tehran (Iran, Islamic Republic of). Dept. of Chemistry; Islamic Azad Univ., Tabriz (Iran, Islamic Republic of). Dept. of Science-Applied Chemistry; Laheghi, S.N.; Ghoranneviss, M. [Islamic Azad Univ., Tehran (Iran, Islamic Republic of). Plasma Research Center; Moradi, S. [Islamic Azad Univ., Tehran (Iran, Islamic Republic of). Dept. of Chemistry; Aberumand, P. [Islamic Azad Univ., Tehran (Iran, Islamic Republic of). Science and Research Laboratory Complex

    2008-07-01

    The applications for copper (Cu) thin films with micro or nanostructural dimensions range from catalysis to microelectronic devices. This paper reported on a study in which DC magnetron sputtering was used to coat iron (Fe), copper (Cu) and aluminum (Al) on glass substrate under a particular voltage, time and optimized deposition pressure. The samples were then coated with Cu using the same technique in preparation of different multilayers. Physical properties such as transmission and reflection per cent, magnetic and electrical properties, size and surface morphology were analyzed using data from AFM, XRD, SEM, Four point probe, and magneto resistive spectrophotometers. The study showed that the size, surface morphology and some physical properties of Cu nanolayer depend on substrate materials, surface morphology and physical properties below the nanolayer. Future work will focus on chemical properties such as catalytic and electrochemical properties. Copper nanoparticles will also be synthesized on other materials such as ZnO. 14 refs., 1 tab., 3 figs.

  16. Measurement of deposition rate and ion energy distribution in a pulsed dc magnetron sputtering system using a retarding field analyzer with embedded quartz crystal microbalance.

    Science.gov (United States)

    Sharma, Shailesh; Gahan, David; Scullin, Paul; Doyle, James; Lennon, Jj; Vijayaraghavan, Rajani K; Daniels, Stephen; Hopkins, M B

    2016-04-01

    A compact retarding field analyzer with embedded quartz crystal microbalance has been developed to measure deposition rate, ionized flux fraction, and ion energy distribution arriving at the substrate location. The sensor can be placed on grounded, electrically floating, or radio frequency (rf) biased electrodes. A calibration method is presented to compensate for temperature effects in the quartz crystal. The metal deposition rate, metal ionization fraction, and energy distribution of the ions arriving at the substrate location are investigated in an asymmetric bipolar pulsed dc magnetron sputtering reactor under grounded, floating, and rf biased conditions. The diagnostic presented in this research work does not suffer from complications caused by water cooling arrangements to maintain constant temperature and is an attractive technique for characterizing a thin film deposition system.

  17. Preparation of Ga-doped ZnO films by pulsed dc magnetron sputtering with cylindrical rotating target for thin film solar cell applications

    International Nuclear Information System (INIS)

    Shin, Beom-Ki; Lee, Tae-Il; Park, Ji-Hyeon; Park, Kang-Il; Ahn, Kyung-Jun; Park, Sung-Kee; Lee, Woong; Myoung, Jae-Min

    2011-01-01

    Applicability of Ga-doped ZnO (GZO) films for thin film solar cells (TFSCs) was investigated by preparing GZO films via pulsed dc magnetron sputtering (PDMS) with rotating target. The GZO films showed improved crystallinity and increasing degree of Ga doping with increasing thickness to a limit of 1000 nm. The films also fulfilled requirements for the transparent electrodes of TFSCs in terms of electrical and optical properties. Moreover, the films exhibited good texturing potential based on etching studies with diluted HCl, which yielded an improved light trapping capability without significant degradation in electrical propreties. It is therefore suggested that the surface-textured GZO films prepared via PDMS and etching are promising candidates for indium-free transparent electrodes for TFSCs.

  18. Preparation of Ga-doped ZnO films by pulsed dc magnetron sputtering with cylindrical rotating target for thin film solar cell applications

    Science.gov (United States)

    Shin, Beom-Ki; Lee, Tae-Il; Park, Ji-Hyeon; Park, Kang-Il; Ahn, Kyung-Jun; Park, Sung-Kee; Lee, Woong; Myoung, Jae-Min

    2011-11-01

    Applicability of Ga-doped ZnO (GZO) films for thin film solar cells (TFSCs) was investigated by preparing GZO films via pulsed dc magnetron sputtering (PDMS) with rotating target. The GZO films showed improved crystallinity and increasing degree of Ga doping with increasing thickness to a limit of 1000 nm. The films also fulfilled requirements for the transparent electrodes of TFSCs in terms of electrical and optical properties. Moreover, the films exhibited good texturing potential based on etching studies with diluted HCl, which yielded an improved light trapping capability without significant degradation in electrical propreties. It is therefore suggested that the surface-textured GZO films prepared via PDMS and etching are promising candidates for indium-free transparent electrodes for TFSCs.

  19. Low resistivity of Ni–Al co-doped ZnO thin films deposited by DC magnetron sputtering at low sputtering power

    Energy Technology Data Exchange (ETDEWEB)

    Lee, JongWoo [Department of Materials Science and Engineering, Pusan National University, San 30 Jangjeon-dong, Geumjeong-gu, Busan 609-735 (Korea, Republic of); Hui, K.N. [Department of Mechanical Engineering, Hanyang University, 17 Haengdang-dong, Seongdong-gu, Seoul 133-791 (Korea, Republic of); Hui, K.S., E-mail: kshui@hanyang.ac.kr [Department of Mechanical Engineering, Hanyang University, 17 Haengdang-dong, Seongdong-gu, Seoul 133-791 (Korea, Republic of); Cho, Y.R., E-mail: yescho@pusan.ac.kr [Department of Materials Science and Engineering, Pusan National University, San 30 Jangjeon-dong, Geumjeong-gu, Busan 609-735 (Korea, Republic of); Chun, Ho-Hwan [Global Core Research Center for Ships and Offshore Plants (GCRC-SOP), Pusan National University, San 30 Jangjeon-dong, Geumjeong-gu, Busan 609-735 (Korea, Republic of)

    2014-02-28

    Ni–Al co-doped ZnO (NiAl:ZnO) thin films were deposited on glass substrates by DC magnetron sputtering in Ar using a single ceramic, spark-plasma-sintered target with 2 wt% Al and 5 wt% Ni. The effects of the sputtering power and gas pressure on the NiAl:ZnO films were studied. The structural, electrical, and optical properties of the films were characterized by X-ray diffraction, field emission scanning electron microscopy, Hall effect measurements and UV–vis transmission spectroscopy. As the sputtering power and gas pressure increased, the crystallinity, electrical properties and optical band gap of the films were improved. The NiAl:ZnO film deposited at 40 W at 6.0 mTorr had the strongest (0 0 2) XRD peak and the lowest resistivity of approximately 2.19 × 10{sup −3} Ω cm with an optical transmittance of 90%.

  20. Measurement of deposition rate and ion energy distribution in a pulsed dc magnetron sputtering system using a retarding field analyzer with embedded quartz crystal microbalance

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, Shailesh, E-mail: shailesh.sharma6@mail.dcu.ie [Dublin City University, Glasnevin, Dublin 9 (Ireland); Impedans Limited, Chase House, City Junction Business Park, Northern Cross, D17 AK63, Dublin 17 (Ireland); Gahan, David, E-mail: david.gahan@impedans.com; Scullin, Paul; Doyle, James; Lennon, Jj; Hopkins, M. B. [Impedans Limited, Chase House, City Junction Business Park, Northern Cross, D17 AK63, Dublin 17 (Ireland); Vijayaraghavan, Rajani K.; Daniels, Stephen [Dublin City University, Glasnevin, Dublin 9 (Ireland)

    2016-04-15

    A compact retarding field analyzer with embedded quartz crystal microbalance has been developed to measure deposition rate, ionized flux fraction, and ion energy distribution arriving at the substrate location. The sensor can be placed on grounded, electrically floating, or radio frequency (rf) biased electrodes. A calibration method is presented to compensate for temperature effects in the quartz crystal. The metal deposition rate, metal ionization fraction, and energy distribution of the ions arriving at the substrate location are investigated in an asymmetric bipolar pulsed dc magnetron sputtering reactor under grounded, floating, and rf biased conditions. The diagnostic presented in this research work does not suffer from complications caused by water cooling arrangements to maintain constant temperature and is an attractive technique for characterizing a thin film deposition system.

  1. Effects of substrate heating and vacuum annealing on optical and electrical properties of alumina-doped ZnO films deposited by DC magnetron sputtering

    Science.gov (United States)

    Tang, Chien-Jen; Wang, Chun-Yuan; Jaing, Cheng-Chung

    2011-10-01

    Alumina-doped zinc oxide (AZO) films have wide range of applications in optical and optoelectronic devices. AZO films have advantage in high transparency, high stability to hydrogen plasma and low cost to alternative ITO film. AZO film was prepared by direct-current (DC) magnetron sputtering from ceramic ZnO:Al2O3 target. The AZO films were compared in two different conditions. The first is substrate heating process, in which AZO film was deposited by different substrate temperature, room temperature, 150 °C and 250 °C. The second is vacuum annealing process, in which AZO film with deposited at room temperature have been annealed at 250 °C and 450 °C in vacuum. The optical properties, electrical properties, grain size and surface structure properties of the films were studied by UV-VIS-NIR spectrophotometer, Hall effect measurement equipment, x-ray diffraction, and scanning electron microscopy. The resistivity, carrier mobility, carrier concentration, and grain size of AZO films were 1.92×10-3 Ω-cm, 6.38 cm2/Vs, 5.08×1020 #/cm3, and 31.48 nm respectively, in vacuum annealing of 450 °C. The resistivity, carrier mobility, carrier concentration, and grain size of AZO films were 8.72×10-4 Ω-cm, 6.32 cm2/Vs, 1.13×1021 #/cm3, and 31.56 nm, respectively, when substrate temperature was at 250 °C. Substrate heating process is better than vacuum annealed process for AZO film deposited by DC Magnetron Sputtering.

  2. Study of working pressure on the optoelectrical properties of Al–Y codoped ZnO thin-film deposited using DC magnetron sputtering for solar cell applications

    International Nuclear Information System (INIS)

    Hsu, Feng-Hao; Wang, Na-Fu; Tsai, Yu-Zen; Chuang, Ming-Chieh; Cheng, Yu-Song; Houng, Mau-Phon

    2013-01-01

    Low cost transparent conductive Al–Y codoped ZnO (AZOY) thin-films were prepared on a glass substrate using a DC magnetron sputtering technique with various working pressures in the range of 5–13 mTorr. The relationship among the structural, electrical, and optical properties of sputtered AZOY films was studied as a function of working pressure. The XRD measurements show that the crystallinity of the films degraded as the working gas pressure increased. The AZOY thin-film deposited at a working pressure of 5 mTorr exhibited the lowest electrical resistivity of 4.3 × 10 −4 Ω cm, carrier mobility of 30 cm 2 /V s, highest carrier concentration of 4.9 × 10 20 cm −3 , and high transmittance in the visible region (400–800 nm) of approximately 90%. Compared with Al doped ZnO (AZO) thin-films deposited using DC or RF magnetron sputtering methods, a high carrier mobility was observed in our AZOY thin-films. This result can be used to effectively decrease the absorption of near infrared-rays in solar cell applications. The mechanisms are attributed to the larger transition energy between Ar atoms and sputtering particles and the size compensation of the dopants. Finally, the optimal quality AZOY thin-film was used as an emitter layer (or window layer) to form AZOY/n-Si heterojunction solar cells, which exhibited a stable conversion efficiency (η) of 9.4% under an AM1.5 illumination condition.

  3. Study of working pressure on the optoelectrical properties of Al–Y codoped ZnO thin-film deposited using DC magnetron sputtering for solar cell applications

    Energy Technology Data Exchange (ETDEWEB)

    Hsu, Feng-Hao [Institute of Microelectronics, Department of Electrical Engineering, National Cheng Kung University, No. 1, Dasyue Road, East District, Tainan City 701, Taiwan (China); Wang, Na-Fu; Tsai, Yu-Zen; Chuang, Ming-Chieh; Cheng, Yu-Song [Department of Electronic Engineering, Cheng Shiu University, 840 Chengcing Road, Niaosong District, Kaohsiung City 833, Taiwan (China); Houng, Mau-Phon, E-mail: mphoung@eembox.ncku.edu.tw [Institute of Microelectronics, Department of Electrical Engineering, National Cheng Kung University, No. 1, Dasyue Road, East District, Tainan City 701, Taiwan (China)

    2013-09-01

    Low cost transparent conductive Al–Y codoped ZnO (AZOY) thin-films were prepared on a glass substrate using a DC magnetron sputtering technique with various working pressures in the range of 5–13 mTorr. The relationship among the structural, electrical, and optical properties of sputtered AZOY films was studied as a function of working pressure. The XRD measurements show that the crystallinity of the films degraded as the working gas pressure increased. The AZOY thin-film deposited at a working pressure of 5 mTorr exhibited the lowest electrical resistivity of 4.3 × 10{sup −4} Ω cm, carrier mobility of 30 cm{sup 2}/V s, highest carrier concentration of 4.9 × 10{sup 20} cm{sup −3}, and high transmittance in the visible region (400–800 nm) of approximately 90%. Compared with Al doped ZnO (AZO) thin-films deposited using DC or RF magnetron sputtering methods, a high carrier mobility was observed in our AZOY thin-films. This result can be used to effectively decrease the absorption of near infrared-rays in solar cell applications. The mechanisms are attributed to the larger transition energy between Ar atoms and sputtering particles and the size compensation of the dopants. Finally, the optimal quality AZOY thin-film was used as an emitter layer (or window layer) to form AZOY/n-Si heterojunction solar cells, which exhibited a stable conversion efficiency (η) of 9.4% under an AM1.5 illumination condition.

  4. Deposition of the low resistive ITO-films by means of reactive magnetron sputtering of the In/Sn target on the cold substrate

    Science.gov (United States)

    Zhidik, Y. S.; Troyan, P. E.; Baturina, E. V.; Korzhenko, D. V.; Yurjev, Y. N.

    2016-06-01

    Detailed information on the deposition technology of the low-resistive ITO-films in oxygen-containing media by magnetron reactive sputtering from the In(90%)/Sn(10%) target on the cold substrate is given. Developed technology allows deposition ITO-films with sheet resistance 2-3 Ω/□, transparency higher than 90%. Developed technology is notable for high reproducibility of results and is compatible with production technology of semiconductor devices of optoelectronics.

  5. Deposition of the low resistive ITO-films by means of reactive magnetron sputtering of the In/Sn target on the cold substrate

    OpenAIRE

    Zhidik, Y. S.; Troyan, P. E.; Baturina, E. V.; Korzhenko, Dmitry Vladimirovich; Yuriev, Yuri Nikolaevich

    2016-01-01

    Detailed information on the deposition technology of the low-resistive ITO-films in oxygen-containing media by magnetron reactive sputtering from the In(90%)/Sn(10%) target on the cold substrate is given. Developed technology allows deposition ITO-films with sheet resistance transparency higher than 90%. Developed technology is notable for high reproducibility of results and is compatible with production technology of semiconductor devices of optoelectronics.

  6. Studies on the cross-magnetron effect in the reactive indium tin oxide deposition. Effects of an inhomogeneous plasma distribution on the coating properties in dynamic and static coating by means of a pulsed dual magnetron

    International Nuclear Information System (INIS)

    Kleinhempel, Ronny

    2008-01-01

    In the present thesis the reactive ITO deposition process under application of metallic In:Sn targets is intensively studied. The coating deposition pursues at a symmetric bipolarly pulsed dual magnetron both on resting and moving substrates. The thesis comprehends two partial fields. On the one hand the dynamic deposition process was comprehensively characterized at an near-industry test facility and successfully transformed by means of its physical parameters to an industrial coating facility. On the other hand static depositions were performed. These allow the analysis of the lateral distribution of the functional coating properties. By this a correlation to the lateral distributions of the measured plasma parameters could be elaborated [de

  7. Magnetron reactively sputtered Ti-DLC coatings on HNBR rubber : The influence of substrate bias

    NARCIS (Netherlands)

    Bui, X.L.; Pei, Y.T.; Hosson, J.Th.M. De

    2008-01-01

    In this study, Ti-containing diamond-like carbon (Ti-DLC) coatings have been deposited on HNBR (hydrogenated nitrile butadiene) rubber and also on Si wafer as reference via unbalanced magnetroli reactive sputtering from a Ti target in C2H2/Ar plasma. The deposition rates of coatings on rubber and Si

  8. Composition and morphology of metal-containing diamond-like carbon films obtained by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Corbella, C.; Pascual, E.; Oncins, G.; Canal, C.; Andujar, J.L.; Bertran, E.

    2005-01-01

    The addition of metal atoms within the matrix of diamond-like carbon films leads to the improvement of their mechanical properties. The present paper discusses the relationship between the composition and morphology of metal-containing (W, Nb, Mo, Ti) diamond-like carbon thin films deposited at room temperature by reactive magnetron sputtering from a metal target in an argon and methane atmosphere. Composition was measured either by electron microprobe technique or by X-ray photoelectron spectroscopy and shows a smooth variation with relative methane flow. High relative methane flows lead to a bulk saturation of carbon atoms, which leads to a lack of homogeneity in the films as confirmed by secondary ion mass spectrometry. Cross-section micrographs were observed by transmission electron microscopy and revealed a structure strongly influenced by the metal inserted and its abundance. The surface pattern obtained by scanning electrochemical potential microscopy provided the metallicity distribution. These measurements were completed with atomic force microscopy of the surface. Selected area electron diffraction and X-ray diffraction measurements provided data of the crystalline structure along with nano-crystallite size. High-resolution transmission electron microscopy provided images of these crystallites

  9. Influence of reactive oxygen species during deposition of iron oxide films by high power impulse magnetron sputtering

    Science.gov (United States)

    Stranak, V.; Hubicka, Z.; Cada, M.; Bogdanowicz, R.; Wulff, H.; Helm, C. A.; Hippler, R.

    2018-03-01

    Iron oxide films were deposited using high power impulse magnetron sputtering (HiPIMS) of an iron cathode in an argon/oxygen gas mixture at different gas pressures (0.5 Pa, 1.5 Pa, and 5.0 Pa). The HiPIMS system was operated at a repetition frequency f  =  100 Hz with a duty cycle of 1%. A main goal is a comparison of film growth during conventional and electron cyclotron wave resonance-assisted HiPIMS. The deposition plasma was investigated by means of optical emission spectroscopy and energy-resolved mass spectrometry. Active oxygen species were detected and their kinetic energy was found to depend on the gas pressure. Deposited films were characterized by means of spectroscopic ellipsometry and grazing incidence x-ray diffraction. Optical properties and crystallinity of as-deposited films were found to depend on the deposition conditions. Deposition of hematite iron oxide films with the HiPIMS-ECWR discharge is attributed to the enhanced production of reactive oxygen species.

  10. Microstructure, chemical states, and mechanical properties of V–C–Co coatings prepared by non-reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Zhang, Xiaojuan; Wang, Bo; Zhan, Zhaolin; Huang, Feng

    2013-01-01

    V–C–Co coatings have been prepared by non-reactive magnetron co-sputtering from VC and Co targets. The microstructure, chemical states, and mechanical properties are examined as a function of Co content in the coatings. The coatings are dense, with columnar growth structures. High resolution transmission electron microscopy (HRTEM) studies identify a nanocomposite microstructure for the 12.4 at.% Co coating, in which ligament-like Co-rich regions partially separate the nanocrystalline VC grains. X-ray photoelectron spectroscopy studies reveal a noticeable charge transfer from Co 2p states to C 1s states. This charge transfer, in addition to the ligament-like Co-rich regions as revealed by HRTEM, points to the formation of a strong Co/VC interface. The nanoindentation hardness of the coatings drops steadily with the Co content, from 29 GPa for pure VC to ∼ 21 GPa for the 12.4 at.% Co coating. Meanwhile, the plasticity characteristic increased from 0.42 to 0.53. - Highlights: • Nanocomposite V–C–Co coatings with strong Co/VC interfaces were formed. • Found nanocrystalline VC grains separated by ∼ 1 nm thin Co-rich ligaments. • A noticeable amount of C-Co bonds between VC and Co is identified. • V–C–Co coatings exhibited a higher plasticity characteristic than VC

  11. Microstructure, chemical states, and mechanical properties of V–C–Co coatings prepared by non-reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Xiaojuan [Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201 (China); School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming, Yunnan 650000 (China); Wang, Bo [Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201 (China); Zhan, Zhaolin [School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming, Yunnan 650000 (China); Huang, Feng, E-mail: huangfeng@nimte.ac.cn [Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, Zhejiang 315201 (China)

    2013-07-01

    V–C–Co coatings have been prepared by non-reactive magnetron co-sputtering from VC and Co targets. The microstructure, chemical states, and mechanical properties are examined as a function of Co content in the coatings. The coatings are dense, with columnar growth structures. High resolution transmission electron microscopy (HRTEM) studies identify a nanocomposite microstructure for the 12.4 at.% Co coating, in which ligament-like Co-rich regions partially separate the nanocrystalline VC grains. X-ray photoelectron spectroscopy studies reveal a noticeable charge transfer from Co 2p states to C 1s states. This charge transfer, in addition to the ligament-like Co-rich regions as revealed by HRTEM, points to the formation of a strong Co/VC interface. The nanoindentation hardness of the coatings drops steadily with the Co content, from 29 GPa for pure VC to ∼ 21 GPa for the 12.4 at.% Co coating. Meanwhile, the plasticity characteristic increased from 0.42 to 0.53. - Highlights: • Nanocomposite V–C–Co coatings with strong Co/VC interfaces were formed. • Found nanocrystalline VC grains separated by ∼ 1 nm thin Co-rich ligaments. • A noticeable amount of C-Co bonds between VC and Co is identified. • V–C–Co coatings exhibited a higher plasticity characteristic than VC.

  12. Structural, Mechanical and Tribological Properties of NbCN-Ag Nanocomposite Films Deposited by Reactive Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Fanjing Wu

    2018-01-01

    Full Text Available In this study, reactive magnetron sputtering was applied for preparing NbCN-Ag films with different Ag additions. Ag contents in the as-deposited NbCN-Ag films were achieved by adjusting Ag target power. The composition, microstructure, mechanical properties, and tribological properties were characterized using energy-dispersive X-ray spectroscopy (EDS, X-ray diffraction (XRD, field emission scanning electron microscope (FE-SEM, high resolution transmission electron microscopy (HRTEM, Raman spectrometry, nano-indentation, and high-temperature sliding wear tests. Results indicated that face-centered cubic (fcc NbN, hexagonal close-packed (hcp NbN and fcc Ag, amorphous C and amorphous CNx phase co-existed in the as-deposited NbCN-Ag films. After doping with 2.0 at.% Ag, the hardness and elastic modulus reached a maximum value of 33 GPa and 340 GPa, respectively. Tribological properties were enhanced by adding Ag in NbCN-Ag films at room temperature. When the test temperature rose from 300 to 500 °C, the addition of Ag was found beneficial for the friction properties, showing a lowest friction coefficient of ~0.35 for NbCN-12.9 at.% Ag films at 500 °C. This was mainly attributed to the existence of AgOx, NbOx, and AgNbOx lubrication phases that acted as solid lubricants to modify the wear mechanism.

  13. Characterization and temperature controlling property of TiAlN coatings deposited by reactive magnetron co-sputtering

    International Nuclear Information System (INIS)

    Chen, J.T.; Wang, J.; Zhang, F.; Zhang, G.A.; Fan, X.Y.; Wu, Z.G.; Yan, P.X.

    2009-01-01

    Titanium aluminum nitride (TiAlN) ternary coating is a potential material which is expected to be applied on satellite for thermal controlling. In order to investigate thermal controlling property, TiAlN coatings were deposited on Si wafers with different N 2 and Ar flux ratio by reactive magnetron co-sputtering. The structure, morphology, chemical composition and optical reflectance are investigated by X-ray diffraction (XRD), field emission scanning electron microscope (FE-SEM), atom force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and spectrophotometer, respectively. The orientation of the coatings depends on the N 2 /Ar flux ratio. The coatings deposited with N 2 /Ar ratio of 10, 30 and 60% show the cubic-TiN [2 2 0] preferred orientation and the coating deposited with N 2 /Ar ratio of 100% exhibits the phase of hexagonal-AlN and cubic-TiN. The surface of the coatings becomes more compact and smoother with the N 2 /Ar ratios increase. XPS spectrum indicates that the oxides (TiO 2 and Al 2 O 3 ), oxynitride (TiN x O y ) and nitrides (TiN and AlN x ) appear at the surface of the coatings. Ignoring internal power, the optimum equilibrium temperature of TiAlN coatings is 18 deg. C and the equilibrium temperature after heat-treated has slight change, which provides the prospective application on thermal controlling

  14. Synthesis and characterization of porous crystalline SiC thin films prepared by radio frequency reactive magnetron sputtering technique

    Energy Technology Data Exchange (ETDEWEB)

    Qamar, Afzaal, E-mail: afzaalqamar@gmail.com [Department of Physics and Applied Mathematics, PIEAS, Nilore, Islamabad, Punjab 42600 (Pakistan); Mahmood, Arshad [National Institute of Laser and Optronics, Nilore, Islamabad (Pakistan); Sarwar, Tuba; Ahmed, Nadeem [Department of Physics and Applied Mathematics, PIEAS, Nilore, Islamabad, Punjab 42600 (Pakistan)

    2011-05-15

    Hexagonal SiC thin films have been deposited using radio frequency reactive magnetron sputtering technique by varying the substrate temperature and other deposition conditions. Prior to deposition surface modification of the substrate Si(1 0 0) played an important role in deposition of the hexagonal SiC structure. The effect of substrate temperature during deposition on structure, composition and surface morphology of the SiC films has been analyzed using atomic force microscopy, Fourier transform infrared spectroscopy and spectroscopic ellipsometry. X-ray diffraction in conventional {theta}-2{theta} mode and omega scan mode revealed that the deposited films were crystalline having 8H-SiC structure and crystallinity improved with increase of deposition temperature. The bonding order and Si-C composition within the films showed improvement with the increase of deposition temperature. The surface of thin films grew in the shape of globes and columns depending upon deposition temperature. The optical properties also showed improvement with increase of deposition temperature and the results obtained by ellipsometry reinforced the results of other techniques.

  15. Role of copper/vanadium on the optoelectronic properties of reactive RF magnetron sputtered NiO thin films

    Science.gov (United States)

    Panneerselvam, Vengatesh; Chinnakutti, Karthik Kumar; Thankaraj Salammal, Shyju; Soman, Ajith Kumar; Parasuraman, Kuppusami; Vishwakarma, Vinita; Kanagasabai, Viswanathan

    2018-04-01

    In this study, pristine nickel oxide (NiO), copper-doped NiO (Cu-NiO) and vanadium-doped NiO (V-NiO) thin films were deposited using reactive RF magnetron co-sputtering as a function of dopant sputtering power. Cu (0-8 at%) and V (0-1 at%) were doped into the NiO lattice by varying the sputtering power of Cu and V in the range of 5-15 W. The effect of dopant concentration on optoelectronic behavior is investigated by UV-Vis-NIR spectrophotometer and Hall measurements. XRD analysis showed that the preferred orientation of the cubic phase for undoped NiO changes from (200) to (111) plane when the sputtering parameters are varied. The observed changes in the lattice parameters and bonding states of the doped NiO indicate the substitution of Ni ions by monovalent Cu and trivalent V ions. The optical bandgap of pristine NiO, Cu-NiO, and V-NiO was found to be 3.6, 3.45, and 3.05 eV, respectively, with decreased transmittance and resistivity. Further analysis using SEM and AFM described the morphological behavior of doped NiO thin films and Raman spectroscopy indicated the structural changes on doping. These findings would be helpful in fabricating solid-state solar cells using doped NiO as efficient hole transporting material.

  16. Structural and corrosive properties of ZrO2 thin films on zircaloy-4 by RF reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Kim, Soo Ho; Lee, Kwang Hoon; Ko, Jae Hwan; Yoon, Young Soo; Baek, Jong Hyuk; Lee, Sang Jin

    2006-01-01

    Zirconium-oxide (ZrO 2 ) thin films as protective layers were grown on a Zircaloy-4 (Z-4) cladding material as a substrate by RF reactive magnetron sputtering at room temperature. To investigate the effect of plasma immersion on the structural and the corrosive properties of the as-grown ZrO 2 thin film, we immersed Z-4 in plasma during the deposition process. X-ray diffraction (XRD) measurements showed that the as-grown ZrO 2 thin films immersed in plasma had cubic, well as monoclinic and tetragonal, phases whereas those immersed in the plasma had monoclinic and tetragonal phases only. Atomic force microscopy (AFM) measurements of the surface morphology showed that the surface roughness of the as-grown ZrO 2 thin films immersed in plasma was larger than that of the films not immersed in plasma. In addition, the corrosive property of the as-grown ZrO 2 thin films immersed in the plasma was characterized using the weight gains of Z-4 after the corrosion test. Compared with the non-immersed films, the weight gains of the immersed films were larger. These results indicate that the ZrO 2 films immersed in plasma cannot protect Z-4 from corrosive phenomena.

  17. Composition, structure and properties of SiN x films fabricated by pulsed reactive closed-field unbalanced magnetron sputtering

    International Nuclear Information System (INIS)

    Yao, Zh.Q.; Yang, P.; Huang, N.; Sun, H.; Wan, G.J.; Leng, Y.X.; Chen, J.Y.

    2005-01-01

    Silicon nitride (SiN x ) thin films are of special interest in both scientific research and industrial applications due to their remarkable properties such as high thermal stability, chemical inertness, high hardness and good dielectric properties. In this work, SiN x films were fabricated by pulsed reactive closed-field unbalanced magnetron sputtering of high purity single crystal silicon targets in an Ar-N 2 mixture. The effect of N 2 partial pressure on the film composition, chemical bonding configurations, surface morphology, surface free energy, optical and mechanical properties were investigated. We showed that with increased N 2 partial pressure, the N to Si ratio (N/Si) in the film increased and N atoms are preferentially incorporated in the NSi 3 stoichiometric configuration. It leads the Si-N network a tendency to chemical order. Films deposited at a high N 2 fraction were consistently N-rich. The film surface transformed from a loose granular structure with microporosity to a homogeneous, continuous, smooth and dense structure. A progressive densification of the film microstructure occurs as the N 2 fraction is increased. The reduced surface roughness and the increased N incorporation in the film give rise to the increased contact angle with double-distilled water from 24 o to 49.6 o . To some extent, the SiN x films deposited by pulsed magnetron sputtering are hydrophilic in nature. The as-deposited SiN x films exhibit good optical transparency in the visible region and the optical band gap E opt can be varied from 1.68 eV for a-Si to 3.62 eV for SiN x films, depending on the synthesis parameters. With the increase of the N/Si atomic ratio, wear resistance of the SiN x films was improved, a consequence of increased hardness and elastic modulus. The SiN x films have lower friction coefficient and better wear resistance than 316L stainless steel under dry sliding friction, where the SiN x films experienced only fatigue wear

  18. Improvement of corrosion protection property of Mg-alloy by DLC and Si-DLC coatings with PBII technique and multi-target DC-RF magnetron sputtering

    International Nuclear Information System (INIS)

    Masami, Ikeyama; Setsuo, Nakao; Tsutomu, Sonoda; Junho, Choi

    2009-01-01

    Magnesium alloys have been considered as one of the most promising light weight materials with potential applications for automobile and aircraft components. Their poor corrosion resistance, however, has to date prevented wider usage. Diamond-like carbon (DLC) and silicon-incorporated DLC (Si-DLC) coatings are known to provide a high degree of corrosion protection, and hold accordingly promise for enhancing the corrosion resistance of the magnesium alloys. In this work we have studied the effect of coating conditions of DLC coatings as well as Si incorporation into coating on corrosion resistance, deposited onto AZ91 magnesium alloy substrates by plasma based ion implantation (PBII). The influences of a Ti interlayer beneath the DLC, Si-DLC and Ti incorporated DLC (Ti-DLC) coatings fabricated by multi-target direct-current radio-frequency (DC-RF) magnetron sputtering were also examined on both the adhesion strength and corrosion resistance of the materials. We have also examined the effect of the Si content in the Si-DLC coatings made by magnetron sputtering on the alloys' corrosion resistance. The results of potentiodynamic polarization measurements demonstrate that Si-DLC coating deposited by PBII exhibits the highest corrosion resistance in an aqueous 0.05 M NaCl solution. Although Ti layer is helpful in increasing adhesion between DLC coating and AZ91 substrate, it also influences adversely corrosion protection. The ozone treatment of the magnesium alloy's surface before the formation of coatings has been found to improve both adhesion strength and corrosion resistance.

  19. Improvement of corrosion protection property of Mg-alloy by DLC and Si-DLC coatings with PBII technique and multi-target DC-RF magnetron sputtering

    Science.gov (United States)

    Masami, Ikeyama; Setsuo, Nakao; Tsutomu, Sonoda; Junho, Choi

    2009-05-01

    Magnesium alloys have been considered as one of the most promising light weight materials with potential applications for automobile and aircraft components. Their poor corrosion resistance, however, has to date prevented wider usage. Diamond-like carbon (DLC) and silicon-incorporated DLC (Si-DLC) coatings are known to provide a high degree of corrosion protection, and hold accordingly promise for enhancing the corrosion resistance of the magnesium alloys. In this work we have studied the effect of coating conditions of DLC coatings as well as Si incorporation into coating on corrosion resistance, deposited onto AZ91 magnesium alloy substrates by plasma based ion implantation (PBII). The influences of a Ti interlayer beneath the DLC, Si-DLC and Ti incorporated DLC (Ti-DLC) coatings fabricated by multi-target direct-current radio-frequency (DC-RF) magnetron sputtering were also examined on both the adhesion strength and corrosion resistance of the materials. We have also examined the effect of the Si content in the Si-DLC coatings made by magnetron sputtering on the alloys' corrosion resistance. The results of potentiodynamic polarization measurements demonstrate that Si-DLC coating deposited by PBII exhibits the highest corrosion resistance in an aqueous 0.05 M NaCl solution. Although Ti layer is helpful in increasing adhesion between DLC coating and AZ91 substrate, it also influences adversely corrosion protection. The ozone treatment of the magnesium alloy's surface before the formation of coatings has been found to improve both adhesion strength and corrosion resistance.

  20. High-rate reactive magnetron sputtering of zirconia films for laser optics applications

    International Nuclear Information System (INIS)

    Juskevicius, K.; Subacius, A.; Drazdys, R.; Juskenas, R.; Audronis, M.; Matthews, A.; Leyland, A.

    2014-01-01

    ZrO 2 exhibits low optical absorption in the near-UV range and is one of the highest laser-induced damage threshold (LIDT) materials; it is, therefore, very attractive for laser optics applications. This paper reports explorations of reactive sputtering technology for deposition of ZrO 2 films with low extinction coefficient k values in the UV spectrum region at low substrate temperature. A high deposition rate (64 % of the pure metal rate) process is obtained by employing active feedback reactive gas control which creates a stable and repeatable deposition processes in the transition region. Substrate heating at 200 C was found to have no significant effect on the optical ZrO 2 film properties. The addition of nitrogen to a closed-loop controlled process was found to have mostly negative effects in terms of deposition rate and optical properties. Open-loop O 2 gas-regulated ZrO 2 film deposition is slow and requires elevated (200 C) substrate temperature or post-deposition annealing to reduce absorption losses. Refractive indices of the films were distributed in the range n = 2.05-2.20 at 1,000 nm and extinction coefficients were in the range k = 0.6 x 10 -4 and 4.8 x 10 -3 at 350 nm. X-ray diffraction analysis showed crystalline ZrO 2 films consisted of monoclinic + tetragonal phases when produced in Ar/O 2 atmosphere and monoclinic + rhombohedral or a single rhombohedral phase when produced in Ar/O 2 + N 2 . Optical and physical properties of the ZrO 2 layers produced in this study are suitable for high-power laser applications in the near-UV range. (orig.)

  1. Deposition and characterization of TaAIN thin films by reactive magnetron sputtering; Deposicao e caracterizacao de filmes finos de TaAIN depositados por magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Oliveira, G.B.; Fernandez, D.R.; Fontes Junior, A.S.; Felix, L.C.; Tentardini, E.K. [Universidade Federal de Sergipe (UFS), Sao Cristovao, SE (Brazil). Departamento de Ciencia e Engenharia de Materiais; Hubler, R. [Pontificia Universidade Catolica do Rio Grande do Sul (PUC-RS), RS (Brazil); Silva Junior, A.H. da, E-mail: brito-g@hotmail.com [Universidade Federal do Rio Grande do Sul (UFRGS), RS (Brazil)

    2016-07-01

    Phase stability, oxidation resistance and great mechanical properties are the main objectives when synthesizing protective coatings. The tantalum nitride (TaN) has aroused interest because of its high temperature stability, chemical inertness and thermal conductivity. However, it has a low hardness value when compared to other coatings. Researches has shown that one way to improvements in the properties of a thin film is by adding other elements in the deposition process. Therefore, the objective of this study was to deposit thin films of TaAlN by magnetron sputtering, changing the aluminum concentration of 2, 5, 7, to 14%. Then the coatings were characterized by EDS, RBS, GIXRD and nanohardness. In this study was found that the aluminum deposited did not change the oxidation resistance of the coating, and the highest value of hardness was 28 GPa for the sample with 14 at.%. (author)

  2. Researches on the Improvement of the Bioactivity of TiO2 Deposits, Obtained by Magnetron Sputtering - DC

    Science.gov (United States)

    Toma, B. F.; Baciu, R. E.; Bejinariu, C.; Cimpoieşu, N.; Ciuntu, B. M.; Toma, S. L.; Burduhos-Nergis, D. P.; Timofte, D.

    2018-06-01

    In this paper, layers of TiO2 were deposited, by magnetron sputtering, on a glass support. The parameters of the deposition process were kept constant except for the O2/(Ar + O2) ratio that varied on three levels. The physical and mechanical properties of the layers obtained were investigated by SEM optical microscopy, electronics, AFM and X-ray diffraction. The bioactivity of TiO2 surfaces was investigated by growing M3C3-E1 osteoblast cells produced by RIKEN Cell Bank (Japan) for a period of 5 days. The modification of the working environment in the enclosure determines both the phasic modification in the TiO2 film, respectively the amount of the anatase or rutile phase and the decrease of the average roughness of the film from 112.3nm to 56.7nm. The research has demonstrated that the finer layers with a high content of anatase promote the growth of M3C3-E1 cells.

  3. Self-assembled Au nanoparticles on heated Corning glass by dc magnetron sputtering: size-dependent surface plasmon resonance tuning

    Energy Technology Data Exchange (ETDEWEB)

    Grammatikopoulos, S.; Pappas, S. D. [University of Patras, Laboratory of High-Tech Materials, School of Engineering (Greece); Dracopoulos, V. [Hellas-Institute of Chemical Engineering and High Temperature Chemical Processes, (FORTH/ICE-HT), Foundation for Research and Technology (Greece); Poulopoulos, P., E-mail: poulop@upatras.gr [University of Patras, Laboratory of High-Tech Materials, School of Engineering (Greece); Fumagalli, P. [Freie Universitaet Berlin, Institut fuer Experimentalphysik (Germany); Velgakis, M. J.; Politis, C. [University of Patras, Laboratory of High-Tech Materials, School of Engineering (Greece)

    2013-02-15

    We report on the growth of Au nanoparticles on Corning glass by direct current magnetron sputtering and on the optical absorption of the films. The substrate temperature was kept to relatively high temperatures of 100 or 450 Degree-Sign C. This lead to the growth of Au nanoparticles instead of smooth Au films as the surface energy of Au is much larger than the one of glass. The size of the particles depended on the substrate temperature and deposition time and was shown to follow a logarithmic normal distribution function. Both, the surface plasmon resonance position and bandwidth, were found to depend upon the average particle size. The surface plasmon resonance position showed a 75 nm continuous blue shift from 14 nm down to 2.5 nm average particle size. Thus, we have shown how to tune the nanoparticle size and surface plasmon resonance of Au by varying the substrate temperature and deposition time. The experimental results are reproduced reasonably using a method which is based on the size- and wavelength-dependent complex dielectric function of Au within the framework of the Mie theory for the optical properties of metallic nanospheres.

  4. The influence of annealing on yttrium oxide thin film deposited by reactive magnetron sputtering: Process and microstructure

    Directory of Open Access Journals (Sweden)

    Y. Mao

    2017-01-01

    Full Text Available Yttrium oxide thin films were prepared by reactive magnetron sputtering in different deposition condition with various oxygen flow rates. The annealing influence on the yttrium oxide film microstructure is investigated. The oxygen flow shows a hysteresis behavior on the deposition rate. With a low oxygen flow rate, the so called metallic mode process with a high deposition rate (up to 1.4µm/h was achieved, while with a high oxygen flow rate, the process was considered to be in the poisoned mode with an extremely low deposition rate (around 20nm/h. X-ray diffraction (XRD results show that the yttrium oxide films that were produced in the metallic mode represent a mixture of different crystal structures including the metastable monoclinic phase and the stable cubic phase, while the poisoned mode products show a dominating monoclinic phase. The thin films prepared in metallic mode have relatively dense structures with less porosity. Annealing at 600 °C for 15h, as a structure stabilizing process, caused a phase transformation that changes the metastable monoclinic phase to stable cubic phase for both poisoned mode and metallic mode. The composition of yttrium oxide thin films changed from nonstoichiometric to stoichiometric together with a lattice parameter variation during annealing process. For the metallic mode deposition however, cracks were formed due to the thermal expansion coefficient difference between thin film and the substrate material which was not seen in poisoned mode deposition. The yttrium oxide thin films that deposited in different modes give various application options as a nuclear material.

  5. Characterization and temperature controlling property of TiAlN coatings deposited by reactive magnetron co-sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Chen, J.T. [School of Physical Science and Technology, Lanzhou University, Lanzhou 730000 (China); Wang, J. [School of Physical Science and Technology, Lanzhou University, Lanzhou 730000 (China); National Key Laboratory of Surface Engineering, Lanzhou Institute of Physics, Lanzhou 730000 (China); Zhang, F.; Zhang, G.A.; Fan, X.Y.; Wu, Z.G. [School of Physical Science and Technology, Lanzhou University, Lanzhou 730000 (China); Yan, P.X. [School of Physical Science and Technology, Lanzhou University, Lanzhou 730000 (China); State Key Laboratory of Solid Lubrication, Lanzhou Institute Chemical and Physics, Chinese Academy of Sciences, Lanzhou 730000 (China)], E-mail: pxyan@lzu.edu.cn

    2009-03-20

    Titanium aluminum nitride (TiAlN) ternary coating is a potential material which is expected to be applied on satellite for thermal controlling. In order to investigate thermal controlling property, TiAlN coatings were deposited on Si wafers with different N{sub 2} and Ar flux ratio by reactive magnetron co-sputtering. The structure, morphology, chemical composition and optical reflectance are investigated by X-ray diffraction (XRD), field emission scanning electron microscope (FE-SEM), atom force microscopy (AFM), X-ray photoelectron spectroscopy (XPS) and spectrophotometer, respectively. The orientation of the coatings depends on the N{sub 2}/Ar flux ratio. The coatings deposited with N{sub 2}/Ar ratio of 10, 30 and 60% show the cubic-TiN [2 2 0] preferred orientation and the coating deposited with N{sub 2}/Ar ratio of 100% exhibits the phase of hexagonal-AlN and cubic-TiN. The surface of the coatings becomes more compact and smoother with the N{sub 2}/Ar ratios increase. XPS spectrum indicates that the oxides (TiO{sub 2} and Al{sub 2}O{sub 3}), oxynitride (TiN{sub x}O{sub y}) and nitrides (TiN and AlN{sub x}) appear at the surface of the coatings. Ignoring internal power, the optimum equilibrium temperature of TiAlN coatings is 18 deg. C and the equilibrium temperature after heat-treated has slight change, which provides the prospective application on thermal controlling.

  6. Structural and optical properties of titanium dioxide films deposited by reactive magnetron sputtering in pure oxygen plasma

    International Nuclear Information System (INIS)

    Asanuma, T.; Matsutani, T.; Liu, C.; Mihara, T.; Kiuchi, M.

    2004-01-01

    Titanium dioxide (TiO 2 ) thin films were deposited on unheated quartz (SiO 2 ) substrates in 'pure oxygen' plasma by reactive radio-frequency (rf) magnetron sputtering. The structural and optical properties of deposited films were systematically studied by changing the deposition parameters, and it was very recently found that crystalline TiO 2 films grew effectively in pure O 2 atmosphere. For TiO 2 films deposited at a rf power P rf of 200 W, x-ray diffraction patterns show the following features: (a) no diffraction peak was observed at a total sputtering pressure p tot of 1.3 Pa; (b) rutile (110) diffraction was observed at 4.0 Pa, (c) the dominant diffraction was from anatase (101) planes, with additional diffraction from (200), under p tot between 6.7 and 13 Pa. For the deposition at 140 W, however, crystalline films with mixed phases were observed only between 4.0 and 6.7 Pa. The peaks of both the deposition rate and the anatase weight ratio for the films produced at 140 W were found at p tot of approximately 6.7 Pa. This suggests that the nucleation and growth of TiO 2 films were affected by the composition, density, and kinetic energy of the particles impinging on the substrate surface. The optical absorption edge analysis showed that the optical band gap E g and the constant B could sensitively detect the film growth behavior, and determine the film structure and optical absorption. The change in the shape of the fundamental absorption edge is considered to reflect the variation of density and the short-range structural modifications

  7. High rate reactive sputtering in an opposed cathode closed-field unbalanced magnetron sputtering system

    Science.gov (United States)

    Sproul, William D.; Rudnik, Paul J.; Graham, Michael E.; Rohde, Suzanne L.

    1990-01-01

    Attention is given to an opposed cathode sputtering system constructed with the ability to coat parts with a size up to 15 cm in diameter and 30 cm in length. Initial trials with this system revealed very low substrate bias currents. When the AlNiCo magnets in the two opposed cathodes were arranged in a mirrored configuration, the plasma density at the substrate was low, and the substrate bias current density was less than 1 mA/sq cm. If the magnets were arranged in a closed-field configuration where the field lines from one set of magnets were coupled with the other set, the substrate bias current density was as high as 5.7 mA/sq cm when NdFeB magnets were used. In the closed-field configuration, the substrate bias current density was related to the magnetic field strength between the two cathodes and to the sputtering pressure. Hard well-adhered TiN coatings were reactively sputtered in the opposed cathode system in the closed-field configuration, but the mirrored configuration produced films with poor adhesion because of etching problems and low plasma density at the substrate.

  8. Nitrogen doping on NiO by reactive magnetron sputtering: A new pathway to dynamically tune the optical and electrical properties

    Energy Technology Data Exchange (ETDEWEB)

    Keraudy, Julien, E-mail: julien.keraudy@liu.se [Institut de Recherche Technologique (IRT), Chemin du Chaffault, 44340, Bouguenais (France); Institut des Matériaux Jean Rouxel (IMN), Université de Nantes, CNRS, 2 rue de la Houssinière, BP32229, 44322, Nantes Cedex 3 (France); Plasma & Coatings Physics Division, IFM Materials Physics, Linköping University, Linköping, SE 581-83 (Sweden); Ferrec, Axel; Richard-Plouet, Mireille; Hamon, Jonathan; Goullet, Antoine; Jouan, Pierre-Yves [Institut des Matériaux Jean Rouxel (IMN), Université de Nantes, CNRS, 2 rue de la Houssinière, BP32229, 44322, Nantes Cedex 3 (France)

    2017-07-01

    Highlights: • Nitrogen doping into NiO lattice (4 at.%) is achieved by only monitoring the N{sub 2}/O{sub 2} gas ratio in the plasma. • The replacement of O by N leads to a narrowing of the optical band-gap energy from 3.6 to 2.3 eV. • The origin of the narrowing is explained by the presence of an intermediate band and the introduction of occupied N 2p states. • Electrical conductivity of NiO:N samples depends on the amount of nickel vacancies and the nitrogen doping. - Abstract: N-doped nickel oxide (NiO:N) thin films were deposited on glass and silicon substrates by reactive DC magnetron sputtering in Ar/O{sub 2}/N{sub 2} gas atmosphere with a series of N{sub 2}/O{sub 2} gas ratio ranging from 0 to 80%. X-ray diffraction measurements have revealed that the films are constituted of Ni{sub 1-x}O grains and showed enhanced polycrystalline features with increasing N-doping concentration. For the first time, we report here that N-doping in the Ni-deficient NiO (Ni{sub 1-x}O) film leads to a band-gap narrowing from 3.6 to 2.3 eV. X-ray photoelectron spectroscopy (XPS) measurements proved that up to 4 atomic percent (at.%) nitrogen can be incorporated at least at the surface of the NiO:N samples. In addition, XPS valence band spectra and UV–vis transmission measurements have demonstrated that the band-gap narrowing may originates from the contribution of an intermediate band (IB) ∼2.4 eV just above the valence band maximum and the up-shifting of the valence band edge (∼0.3 eV) due to the introduction of occupied N 2p states. Local I–V measurements, carried out by conductive AFM (C-AFM), have revealed that the extrinsic doping of N atoms within the oxide can be a good way to precisely control the electrical conductivity of such p-type materials.

  9. High performance W-AIN cermet solar coatings designed by modelling calculations and deposited by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Qi-Chu Zhang [The University of Sydney (Australia). School of Physics; Shen, Y.G. [City University of Hong Kong (Hong Kong). Department of Manufacturing Engineering and Engineering Management

    2004-01-25

    High solar performance W-AIN cermet solar coatings were designed using a numerical computer model and deposited experimentally. In the numerical calculations aluminium oxynitride (AlON) was used as ceramic component. The dielectric functions and then complex refractive index of W-AlON cermet materials were calculated using the Sheng's approximation. The layer thickness and W metal volume fraction were optimised to achieve maximum photo-thermal conversion efficiency for W-AlON cermet solar coatings on an Al reflector with a surface AlON ceramic anti-reflection layer. Optimisation calculations show that the W-AlON cermet solar coatings with two and three cermet layers have nearly identical solar absorptance, emittance and photo-thermal conversion efficiency that are much better than those for films with one cermet layer. The optimised calculated AlON/W-AlON/Al solar coating film with two cermet layers has a high solar absorptance of 0.953 and a low hemispherical emittance of 0.051 at 80{sup o}C for a concentration factor of 2. The AlN/W-AlN/Al solar selective coatings with two cermet layers were deposited using two metal target direct current magnetron sputtering technology. During the deposition of W-AlN cermet layer, both Al and W targets were run simultaneously in a gas mixture of argon and nitrogen. By substrate rotation a multi-sub-layer system consisting of alternating AlN ceramic and W metallic sub-layers was deposited that can be considered as a macro-homogeneous W-AlN cermet layer. A solar absorptance of 0.955 and nearly normal emittance of 0.056 at 80{sup o}C have been achieved for deposited W-AlN cermet solar coatings. (author)

  10. High performance W-AlN cermet solar coatings designed by modelling calculations and deposited by DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Qi-Chu [School of Physics, The University of Sydney, Sydney, NSW 2006 (Australia); Shen, Y.G. [Department of Manufacturing Engineering and Engineering Management, City University of Hong Kong (Hong Kong)

    2004-01-25

    High solar performance W-AlN cermet solar coatings were designed using a numerical computer model and deposited experimentally. In the numerical calculations aluminium oxynitride (AlON) was used as ceramic component. The dielectric function and then complex refractive index of W-AlON cermet materials were calculated using the Sheng's approximation. The layer thickness and W metal volume fraction were optimised to achieve maximum photo-thermal conversion efficiency for W-AlON cermet solar coatings on an Al reflector with a surface AlON ceramic anti-reflection layer. Optimisation calculations show that the W-AlON cermet solar coatings with two and three cermet layers have nearly identical solar absorptance, emittance and photo-thermal conversion efficiency that are much better than those for films with one cermet layer. The optimised calculated AlON/W-AlON/Al solar coating film with two cermet layers has a high solar absorptance of 0.953 and a low hemispherical emittance of 0.051 at 80C for a concentration factor of 2. The AlN/W-AlN/Al solar selective coatings with two cermet layers were deposited using two metal target direct current magnetron sputtering technology. During the deposition of W-AlN cermet layer, both Al and W targets were run simultaneously in a gas mixture of argon and nitrogen. By substrate rotation a multi-sub-layer system consisting of alternating AlN ceramic and W metallic sub-layers was deposited that can be considered as a macro-homogeneous W-AlN cermet layer. A solar absorptance of 0.955 and nearly normal emittance of 0.056 at 80C have been achieved for deposited W-AlN cermet solar coatings.

  11. Control and enhancement of the oxygen storage capacity of ceria films by variation of the deposition gas atmosphere during pulsed DC magnetron sputtering

    Science.gov (United States)

    Eltayeb, Asmaa; Vijayaraghavan, Rajani K.; McCoy, Anthony; Venkatanarayanan, Anita; Yaremchenko, Aleksey A.; Surendran, Rajesh; McGlynn, Enda; Daniels, Stephen

    2015-04-01

    In this study, nanostructured ceria (CeO2) films are deposited on Si(100) and ITO coated glass substrates by pulsed DC magnetron sputtering using a CeO2 target. The influence on the films of using various gas ambients, such as a high purity Ar and a gas mixture of high purity Ar and O2, in the sputtering chamber during deposition are studied. The film compositions are studied using XPS and SIMS. These spectra show a phase transition from cubic CeO2 to hexagonal Ce2O3 due to the sputtering process. This is related to the transformation of Ce4+ to Ce3+ and indicates a chemically reduced state of CeO2 due to the formation of oxygen vacancies. TGA and electrochemical cyclic voltammetry (CV) studies show that films deposited in an Ar atmosphere have a higher oxygen storage capacity (OSC) compared to films deposited in the presence of O2. CV results specifically show a linear variation with scan rate of the anodic peak currents for both films and the double layer capacitance values for films deposited in Ar/O2 mixed and Ar atmosphere are (1.6 ± 0.2) × 10-4 F and (4.3 ± 0.5) × 10-4 F, respectively. Also, TGA data shows that Ar sputtered samples have a tendency to greater oxygen losses upon reduction compared to the films sputtered in an Ar/O2 mixed atmosphere.

  12. Influences of the RF power ratio on the optical and electrical properties of GZO thin films by DC coupled RF magnetron sputtering at room temperature

    Energy Technology Data Exchange (ETDEWEB)

    Peng, Shou [State Key Laboratory of Advanced Technology for Float Glass, Bengbu 233018 (China); Bengbu Design & Research Institute for Glass Industry, Bengbu 233018 (China); Yao, Tingting, E-mail: yaott0815@163.com [State Key Laboratory of Advanced Technology for Float Glass, Bengbu 233018 (China); Bengbu Design & Research Institute for Glass Industry, Bengbu 233018 (China); Yang, Yong; Zhang, Kuanxiang; Jiang, Jiwen; Jin, Kewu; Li, Gang; Cao, Xin; Xu, Genbao; Wang, Yun [State Key Laboratory of Advanced Technology for Float Glass, Bengbu 233018 (China); Bengbu Design & Research Institute for Glass Industry, Bengbu 233018 (China)

    2016-12-15

    Ga-doped zinc oxide (GZO) thin films were deposited by closed field unbalanced DC coupled RF magnetron sputtering system at room temperature. The RF sputtering power ratio was adjusted from 0% to 100%. The crystal structure, surface morphology, transmittance and electrical resistivity of GZO films mainly influenced by RF sputtering power ratio were investigated by X-ray diffractometer, scanning electronic microscope, ultraviolet-visible spectrophotometer and Hall effect measurement. The research results indicate that the increasing RF power ratio can effectively reduce the discharge voltage of system and increase the ionizing rate of particles. Meanwhile, the higher RF power ratio can increase the carrier mobility in GZO thin film and improve the optical and electrical properties of GZO thin film significantly. Within the optimal discharge voltage window, the film deposits at 80% RF power ratio exhibits the lowest resistivity of 2.6×10{sup −4} Ω cm. We obtain the GZO film with the best average optical transmittance is approximately 84% in the visible wavelength. With the increasing RF power ratio, the densification of GZO film is enhanced. The densification of GZO film is decrease when the RF power ratio is 100%.

  13. THE EFFECT OF PRESSURE, BIAS VOLTAGE AND ANNEALING TEMPERATURE ON N₂ AND N₂+SiH₄ DOPED WC/C DC MAGNETRON SPUTTERED LAYERS

    Directory of Open Access Journals (Sweden)

    Peter Hornak

    2017-12-01

    Full Text Available Tungsten carbide (WC/C layers are often researched due to their outstanding mechanical and tribological properties. Here, optimized indented hardness (HIT, indentation modulus (EIT and coefficient of friction (COF values were measured to study the effect of pressure and bias voltage on WC/C layers, deposited on Si by DC magnetron spluttering. Maximal values of HIT=37.2±4.8 GPa, EIT=447±28 GPa and COF=0.64±0.09 were obtained. Additionally, the effect of temperature on optimized layers deposited with and without N₂ and N₂+SiH₄ annealed at 200 °C, 500 °C and 800 °C, were also investigated. The values of HIT, EIT and COF and, observed morphology and structural composition of these contaminated and non-contaminated WC/C layers were evaluated. It was found that layer degradation occurred at different rates depending on the temperature and gas mixture used during the annealing and deposition process, respectively.

  14. Temperature-dependent interface characteristic of silicon wafer bonding based on an amorphous germanium layer deposited by DC-magnetron sputtering

    Science.gov (United States)

    Ke, Shaoying; Lin, Shaoming; Ye, Yujie; Mao, Danfeng; Huang, Wei; Xu, Jianfang; Li, Cheng; Chen, Songyan

    2018-03-01

    We report a near-bubble-free low-temperature silicon (Si) wafer bonding with a thin amorphous Ge (a-Ge) intermediate layer. The DC-magnetron-sputtered a-Ge film on Si is demonstrated to be extremely flat (RMS = 0.28 nm) and hydrophilic (contact angle = 3°). The effect of the post-annealing temperature on the surface morphology and crystallinity of a-Ge film at the bonded interface is systematically identified. The relationship among the bubble density, annealing temperature, and crystallinity of a-Ge film is also clearly clarified. The crystallization of a-Ge film firstly appears at the bubble region. More interesting feature is that the crystallization starts from the center of the bubbles and sprawls to the bubble edge gradually. The H2 by-product is finally absorbed by intermediate Ge layer with crystalline phase after post annealing. Moreover, the whole a-Ge film out of the bubble totally crystallizes when the annealing time increases. This Ge integration at the bubble region leads to the decrease of the bubble density, which in turn increases the bonding strength.

  15. Synthesis of Ag-Cu-Pd alloy thin films by DC-magnetron sputtering: Case study on microstructures and optical properties

    Science.gov (United States)

    Rezaee, Sahar; Ghobadi, Nader

    2018-06-01

    The present study aims to investigate optical properties of Ag-Cu-Pd alloy thin films synthesized by DC-magnetron sputtering method. The thin films are deposited on the glass and silicon substrates using Argon gas and Ag-Cu-Pd target. XRD analysis confirms the successful growth of Ag, Cu, and Pd NPs with FCC crystalline structure. Moreover, UV-visible absorption spectroscopy is applied to determine optical properties of the prepared samples which are affected by changes in surface morphology. The existence of single surface plasmon resonance (SPR) peak near 350 nm proves the formation of silver nanoparticles with a slight red shift through increasing deposition time. Ineffective thickness method (ITM) and Derivation of ineffective thickness method (DITM) are applied to extract optical band gap and transition type via absorption spectrum. SEM and AFM analyses show the distribution of near-spherical nanoparticles covering the surface of thin films. Furthermore, thickness variation affects the grain size. In addition, TEM image reveals the uniform size distribution of nanoparticles with an average particle size of about 15 nm. The findings show that increasing grain size and crystallite order along with the decrease of structural defect and disorders decrease optical band gap from 3.86 eV to 2.58 eV.

  16. Evaluation of the optoelectronic properties and corrosion behavior of Al2O3-doped ZnO films prepared by dc pulsed magnetron sputtering

    International Nuclear Information System (INIS)

    Zubizarreta, C; Berasategui, E G; Bayón, R; Barriga, J; Escobar Galindo, R; Barros, R; Gaspar, D; Nunes, D; Calmeiro, T; Martins, R; Fortunato, E

    2014-01-01

    The main requirements for transparent conducting oxide (TCO) films acting as electrodes are a high transmission rate in the visible spectral region and low resistivity. However, in many cases, tolerance to temperature and humidity exposure is also an important requirement to be fulfilled by the TCOs to assure proper operation and durability. Besides improving current encapsulation methods, the corrosion resistance of the developed TCOs must also be enhanced to warrant the performance of optoelectronic devices. In this paper the performance of aluminum-doped zinc oxide (AZO) films deposited by pulsed dc magnetron sputtering has been studied. Structure, optical transmittance/reflectance, electrical properties (resistivity, carrier concentration and mobility) and corrosion resistance of the developed coatings have been analyzed as a function of the doping of the target and the coating thickness. Films grown from a 2.0 wt% Al 2 O 3 target with a thickness of approximately 1 µm showed a very low resistivity of 6.54  ×  10 –4  Ωcm and a high optical transmittance in the visible range of 84%. Corrosion studies of the developed samples have shown very low corrosion currents (nanoamperes), very high corrosion resistances (in the order of 10 7  Ω) and very high electrochemical stability, indicating no tendency for electrochemical corrosion degradation. (paper)

  17. Evaluation of the optoelectronic properties and corrosion behavior of Al2O3-doped ZnO films prepared by dc pulsed magnetron sputtering

    Science.gov (United States)

    Zubizarreta, C.; Berasategui, E. G.; Bayón, R.; Escobar Galindo, R.; Barros, R.; Gaspar, D.; Nunes, D.; Calmeiro, T.; Martins, R.; Fortunato, E.; Barriga, J.

    2014-12-01

    The main requirements for transparent conducting oxide (TCO) films acting as electrodes are a high transmission rate in the visible spectral region and low resistivity. However, in many cases, tolerance to temperature and humidity exposure is also an important requirement to be fulfilled by the TCOs to assure proper operation and durability. Besides improving current encapsulation methods, the corrosion resistance of the developed TCOs must also be enhanced to warrant the performance of optoelectronic devices. In this paper the performance of aluminum-doped zinc oxide (AZO) films deposited by pulsed dc magnetron sputtering has been studied. Structure, optical transmittance/reflectance, electrical properties (resistivity, carrier concentration and mobility) and corrosion resistance of the developed coatings have been analyzed as a function of the doping of the target and the coating thickness. Films grown from a 2.0 wt% Al2O3 target with a thickness of approximately 1 µm showed a very low resistivity of 6.54  ×  10-4 Ωcm and a high optical transmittance in the visible range of 84%. Corrosion studies of the developed samples have shown very low corrosion currents (nanoamperes), very high corrosion resistances (in the order of 107 Ω) and very high electrochemical stability, indicating no tendency for electrochemical corrosion degradation.

  18. Deposition and characterization of zirconium nitride (ZrN) thin films by reactive magnetron sputtering with linear gas ion source and bias voltage

    Energy Technology Data Exchange (ETDEWEB)

    Kavitha, A.; Kannan, R. [Department of Physics, University College of Engineering, Anna University, Dindugal-624622 (India); Subramanian, N. Sankara [Department of Physics, Thiagarajar College of Engineering, Madurai -625015, Tamilnadu (India); Loganathan, S. [Ion Plating, Titan Industries Ltd., Hosur - 635126, Tamilnadu (India)

    2014-04-24

    Zirconium nitride thin films have been prepared on stainless steel substrate (304L grade) by reactive cylindrical magnetron sputtering method with Gas Ion Source (GIS) and bias voltage using optimized coating parameters. The structure and surface morphologies of the ZrN films were characterized using X-ray diffraction, atomic microscopy and scanning electron microscopy. The adhesion property of ZrN thin film has been increased due to the GIS. The coating exhibits better adhesion strength up to 10 N whereas the ZrN thin film with bias voltage exhibits adhesion up to 500 mN.

  19. Cathode and ion-luminescence of Eu:ZnO thin films prepared by reactive magnetron sputtering and plasma decomposition of non-volatile precursors

    Energy Technology Data Exchange (ETDEWEB)

    Gil-Rostra, Jorge [Instituto de Ciencia de Materiales de Sevilla, CSIC, Univ. Sevilla, C/Américo Vespucio 49, E-41092 Sevilla (Spain); Ferrer, Francisco J. [Centro Nacional de Aceleradores, CSIC, Univ. Sevilla, Av. Thomas A. Edison 7, E-41092 Sevilla (Spain); Martín, Inocencio R. [Departamento de Física Fundamental y Experimental, Electrónica y Sistemas, U. La Laguna, C/Astrofísico Francisco Sánchez s/n, E-38206 La Laguna, Santa Cruz de Tenerife (Spain); González-Elipe, Agustín R.; Yubero, Francisco [Instituto de Ciencia de Materiales de Sevilla, CSIC, Univ. Sevilla, C/Américo Vespucio 49, E-41092 Sevilla (Spain)

    2016-10-15

    This paper reports the luminescent behavior of Eu:ZnO thin films prepared by an one-step procedure that combines reactive magnetron sputtering deposition of ZnO with the plasma activated decomposition of a non-volatile acetylacetonate precursor of Eu sublimated in an effusion cell. Chemical composition and microstructure of the Eu:ZnO thin films have been characterized by several methods and their photo-, cathode- and ion-luminescent properties studied as a function of Eu concentration. The high transparency and well controlled optical properties of the films have demonstrated to be ideal for the development of cathode- and ion- luminescence sensors.

  20. Corrosion of thin, magnetron sputtered Nb_2O_5 films

    International Nuclear Information System (INIS)

    Pillis, Marina Fuser; Geribola, Guilherme Altomari; Scheidt, Guilherme; Gonçalves de Araújo, Edval; Lopes de Oliveira, Mara Cristina; Antunes, Renato Altobelli

    2016-01-01

    Highlights: • Niobium oxide based films were obtained by DC magnetron sputtering. • Different deposition times were tested. • The best corrosion resistance was obtained for the Nb_2O_5 film produced at 15′. • Film porosity determines the corrosion resistance. - Abstract: Niobium oxide based thin films were deposited on AISI 316 stainless steel substrates using reactive DC magnetron sputtering. Structure, composition and corrosion resistance of the niobium oxide films were studied. The corrosion behavior of the specimens was evaluated by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. The concentration of niobium and oxygen in the films was obtained by Rutherford backscattering spectroscopy (RBS). The film structure was analyzed by X-ray diffractometry. The corrosion resistance of the substrate was improved by the Nb_2O_5 layers. The best protective performance was achieved for the deposition time of 15 min.

  1. 3C-SiC epitaxial films deposited by reactive magnetron sputtering: Growth, characterization and device development

    Energy Technology Data Exchange (ETDEWEB)

    Wahab, Qamar ul.

    1994-01-01

    Epitaxial 3C-SiC films were grown on silicon substrates by reactive magnetron sputtering of pure Si target in a mixed Ar-CH[sub 4] discharges. Films were grown on Si(001), and 4 degrees off-oriented (001) substrates. Epitaxial 3C-SiC films with sharp interface to Si substrates have been grown at substrate temperatures [<=] 900 degrees C. Above 900 degrees C interfacial reaction starts resulting in a rough SiC/Si interface. The carbon content as well as the crystalline structure was also found to be strongly dependent on CH[sub 4] partial pressure (PCH[sub 4]) and stoichiometric composition can only be obtained in a narrow PCH[sub 4] range. Films grown on Si(001) substrates contained anti domain boundaries as evident by cross-sectional transmission electron microscopy (XTEM). Films grown on (111)-oriented substrates were epitaxial at 850 degrees C but contained double positioning domains as determined by X-ray diffraction analysis and XTEM. High quality films were obtained on 4 degrees off-oriented Si(001) substrates at T[sub s]=850 degrees C and PCH[sub 4]=0.6 mTorr. Films grown on off-oriented substrates showed atomically sharp interface to Si and also a smooth top surface. SiO[sub 2] layer grown on such films showed atomically sharp oxide/film interface. Also the growth of epitaxial Si films on top of SiC films was realized. Au-Schottky diodes fabricated on (001)-oriented 3C-SiC films showed good rectification with a leakage current density = 4 [mu]A cm[sup -2], a breakdown voltage of -15 V, an ideality factor of 1.27 and a barrier height of 1.04 eV. Metal oxide semiconductor structures were fabricated by thermally grown SiO[sub 2] on (111)-oriented SiC films. The capacitance-voltage measurements showed the accumulation, depletion and deep depletion region in the C-V curve. The interface trap densities were 3-7 x 10[sup 11] cm[sup -2] eV[sup -1]. Finally 3C-SiC/Si heterojunction diodes processed showed good rectification and the diode had a breakdown at -110 V.

  2. 3C-SiC epitaxial films deposited by reactive magnetron sputtering: Growth, characterization and device development

    International Nuclear Information System (INIS)

    Wahab, Qamar ul.

    1994-01-01

    Epitaxial 3C-SiC films were grown on silicon substrates by reactive magnetron sputtering of pure Si target in a mixed Ar-CH 4 discharges. Films were grown on Si(001), and 4 degrees off-oriented (001) substrates. Epitaxial 3C-SiC films with sharp interface to Si substrates have been grown at substrate temperatures ≤ 900 degrees C. Above 900 degrees C interfacial reaction starts resulting in a rough SiC/Si interface. The carbon content as well as the crystalline structure was also found to be strongly dependent on CH 4 partial pressure (PCH 4 ) and stoichiometric composition can only be obtained in a narrow PCH 4 range. Films grown on Si(001) substrates contained anti domain boundaries as evident by cross-sectional transmission electron microscopy (XTEM). Films grown on (111)-oriented substrates were epitaxial at 850 degrees C but contained double positioning domains as determined by X-ray diffraction analysis and XTEM. High quality films were obtained on 4 degrees off-oriented Si(001) substrates at T s =850 degrees C and PCH 4 =0.6 mTorr. Films grown on off-oriented substrates showed atomically sharp interface to Si and also a smooth top surface. SiO 2 layer grown on such films showed atomically sharp oxide/film interface. Also the growth of epitaxial Si films on top of SiC films was realized. Au-Schottky diodes fabricated on (001)-oriented 3C-SiC films showed good rectification with a leakage current density = 4 μA cm -2 , a breakdown voltage of -15 V, an ideality factor of 1.27 and a barrier height of 1.04 eV. Metal oxide semiconductor (MOS) structures were fabricated by thermally grown SiO 2 on (111)-oriented SiC films. The capacitance-voltage measurements showed the accumulation, depletion and deep depletion region in the C-V curve. The interface trap densities were 3-7 x 10 11 cm -2 eV -1 . Finally 3C-SiC/Si heterojunction diodes processed showed good rectification and the diode had a breakdown at -110 V. 59 refs, figs, tabs

  3. Growth and characterization of textured YBaCo2O5+δ thin films grown on (001)-SrTiO3 via DC magnetron sputtering

    International Nuclear Information System (INIS)

    Galeano, V.; Arnache, O.; Supelano, I.; Vargas, C.A. Parra; Morán, O.

    2016-01-01

    Thin films of the layered cobaltite YBaCo 2 O 5+δ were successfully grown on (001)-oriented SrTiO 3 single-crystal substrates by means of DC magnetron sputtering. The 112 phase of the compound was stabilized by choosing an adequate Co reactant and through careful thermal treatment of the target. The results demonstrate the strong influence of these variables on the final phase of the compound. A substrate temperature of 1053 K and an oxygen pressure of 300 Pa seemed to be appropriate growing conditions for depositing (00ℓ)-textured YBaCo 2 O 5+δ thin films onto the chosen substrate. In like fashion to the polycrystalline YBaCo 2 O 5+δ , the films showed a clear sequence of antiferromagnetic–ferromagnetic–paramagnetic transitions within a narrow temperature range. Well-defined hysteresis loops were observed at temperatures as high as 270 K, which supports the existence of a FM order in the films. In turn, the dependence of the resistivity on the temperature shows a semiconductor-like behavior, without any distinguishable structure, within the temperature range measured (50–350 K). The analysis of the experimental data showed that the transport mechanism in the films is well described by using the Mott variable range hopping (VRH) conduction model. - Highlights: • YBaCo 2 O 5+δ thin films are grown on SrTiO 3 substrates. • Strong (00ℓ) reflections are observed in the X-ray diffraction pattern. • A clear sequence of magnetic transitions is observed. • Semiconducting-like behavior is verified.

  4. Effect of deposition angle on the structure and properties of pulsed-DC magnetron sputtered TiAlN thin films

    International Nuclear Information System (INIS)

    Shetty, A.R.; Karimi, A.; Cantoni, M.

    2011-01-01

    This article reports the comparison of structure and properties of titanium aluminum nitride (TiAlN) films deposited onto Si(100) substrates under normal and oblique angle depositions using pulsed-DC magnetron sputtering. The substrate temperature was set at room temperature, 400 o C and 650 o C, and the bias was kept at 0, - 25, - 50, and - 80 V for both deposition angles. The surface and cross-section of the films were observed by scanning electron microscopy. It was found that as the deposition temperature increases, films deposited under normal incidence exhibit distinct faceted crystallites, whereas oblique angle deposited (OAD) films develop a kind of 'tiles of a roof' or 'stepwise structure', with no facetted crystallites. The OAD films showed an inclined columnar structure, with columns tilting in the direction of the incident flux. As the substrate temperature was increased, the tilting of columns nearly approached the substrate normal. Both hardness and Young's modulus decreases when the flux angle was changed from α = 0 o to 45 o as measured by nanoindentation. This was attributed to the voids formed due to the shadowing effect. The crystallographic properties of these coatings were studied by θ-2θ scan and pole figure X-ray diffraction. Films deposited at α = 0 o showed a mixed (111) and (200) out-of-plane orientation with random in-plane alignment. On the other hand, films deposited at α = 45 o revealed an inclined texture with (111) orientation moving towards the incident flux direction and the (200) orientation approaching the substrate normal, showing substantial in-plane alignment.

  5. High-rate deposition of Ta-doped SnO2 films by reactive magnetron sputtering using a Sn–Ta metal-sintered target

    International Nuclear Information System (INIS)

    Muto, Y.; Nakatomi, S.; Oka, N.; Iwabuchi, Y.; Kotsubo, H.; Shigesato, Y.

    2012-01-01

    Ta-doped SnO 2 films were deposited on glass substrate (either unheated or heated at 200 °C) by reactive magnetron sputtering with a Sn–Ta metal-sintered target using a plasma control unit (PCU) and mid-frequency (mf, 50 kHz) unipolar pulsing. The PCU feedback system precisely controlled the flow of the reactive and sputtering gases (O 2 and Ar, respectively) by monitoring either discharge impedance or the plasma emission of the atomic O* line at 777 nm. The planar target was connected to the switching unit, which was operated in unipolar pulse mode. Power density on the target was maintained at 4.4 W cm −2 during deposition. The lowest obtained resistivity for the films deposited on heated substrate was 6.4 × 10 −3 Ωcm, where the deposition rate was 250 nm min −1 .

  6. Influence of reactive oxygen species during deposition of iron oxide films by high power impulse magnetron sputtering

    Czech Academy of Sciences Publication Activity Database

    Straňák, V.; Hubička, Zdeněk; Čada, Martin; Bogdanowicz, R.; Wulff, H.; Helm, C.A.; Hippler, R.

    2018-01-01

    Roč. 51, č. 9 (2018), s. 1-12, č. článku 095205. ISSN 0022-3727 R&D Projects: GA ČR GA17-08389S Institutional support: RVO:68378271 Keywords : high power impulse magnetron sputtering (HiPIMS) * iron oxide thin films * wüstite * magnetite * maghemite * hematite Subject RIV: BL - Plasma and Gas Discharge Physics OBOR OECD: Fluids and plasma physics (including surface physics ) Impact factor: 2.588, year: 2016

  7. Geometric considerations in magnetron sputtering

    International Nuclear Information System (INIS)

    Thornton, J.A.

    1982-01-01

    The recent development of high performance magnetron type discharge sources has greatly enhaced the range of coating applications where sputtering is a viable deposition process. Magnetron sources can provide high current densities and sputtering rates, even at low pressures. They have much reduced substrate heating rates and can be scaled to large sizes. Magnetron sputter coating apparatuses can have a variety of geometric and plasma configurations. The target geometry affects the emission directions of both the sputtered atoms and the energetic ions which are neutralized and reflected at the cathode. This fact, coupled with the long mean free particle paths which are prevalent at low pressures, can make the coating properties very dependent on the apparatus geometry. This paper reviews the physics of magnetron operation and discusses the influences of apparatus geometry on the use of magnetrons for rf sputtering and reactive sputtering, as well as on the microstructure and internal stresses in sputtered metallic coatings. (author) [pt

  8. Niobium-based catalysts prepared by reactive radio-frequency magnetron sputtering and arc plasma methods as non-noble metal cathode catalysts for polymer electrolyte fuel cells

    International Nuclear Information System (INIS)

    Ohnishi, Ryohji; Katayama, Masao; Takanabe, Kazuhiro; Kubota, Jun; Domen, Kazunari

    2010-01-01

    Two vacuum methods, reactive radio-frequency (RF) magnetron sputtering and arc plasma deposition, were used to prepare niobium-based catalysts for an oxygen reduction reaction (ORR) as non-noble metal cathodes for polymer electrode fuel cells (PEFCs). Thin films with various N and O contents, denoted as NbO x and Nb-O-N, were prepared on glassy carbon plates by RF magnetron sputtering with controlled partial pressures of oxygen and nitrogen. Electrochemical measurements indicated that the introduction of the nitrogen species into the thin film resulted in improved ORR activity compared to the oxide-only film. Using an arc plasma method, niobium was deposited on highly oriented pyrolytic graphite (HOPG) substrates, and the sub-nanoscale surface morphology of the deposited particles was investigated using scanning tunneling microscopy (STM). To prepare practical cathode catalysts, niobium was deposited on carbon black (CB) powders by arc plasma method. STM and transmission electron microscopy observations of samples on HOPG and CB indicated that the prepared catalysts were highly dispersed at the atomic level. The onset potential of oxygen reduction on Nb-O-N/CB was 0.86 V vs. a reversible hydrogen electrode, and the apparent current density was drastically improved by the introduction of nitrogen.

  9. Investigation of CaTiO3:Pr3+ thin films deposited by radiofrequency reactive magnetron sputtering for electroluminescence application

    International Nuclear Information System (INIS)

    Sarakha, L; Bousquet, A; Tomasella, E; Boutinaud, P; Mahiou, R

    2010-01-01

    In this report we successfully deposited thin films of CaTiO 3 :Pr 3+ by radiofrequency magnetron sputtering. The films were studied and we tried to understand the evolution of their optical and electrical properties. We noticed that the annealing temperature and the deposition pressures have an important influence on these properties. Thin films with good optical and electrical properties have been obtained. These films are transparent and are characterized by an intense red photoluminescence and a low fixed charge density. They are well dedicated for electroluminescence purposes.

  10. Cu2SixSn1-xS3 Thin Films Prepared by Reactive Magnetron Sputtering For Low-Cost Thin Film Solar Cells

    Science.gov (United States)

    Yan, Chang; Liu, Fang-Yang; Lai, Yan-Qing; Li, Jie; Liu, Ye-Xiang

    2011-10-01

    We report the preparation of Cu2SixSn1-xS3 thin films for thin film solar cell absorbers using the reactive magnetron co-sputtering technique. Energy dispersive spectrometer and x-ray diffraction analyses indicate that Cu2Si1-xSnxS3 thin films can be synthesized successfully by partly substituting Si atoms for Sn atoms in the Cu2SnS3 lattice, leading to a shrinkage of the lattice, and, accordingly, by 2θ shifting to larger values. The blue shift of the Raman peak further confirms the formation of Cu2SixSn1-xS3. Environmental scanning electron microscope analyses reveal a polycrystalline and homogeneous morphology with a grain size of about 200-300 nm. Optical measurements indicate an optical absorption coefficient of higher than 104 cm-1 and an optical bandgap of 1.17±0.01 eV.

  11. Room Temperature Optical Constants and Band Gap Evolution of Phase Pure M1-VO2 Thin Films Deposited at Different Oxygen Partial Pressures by Reactive Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Meng Jiang

    2014-01-01

    Full Text Available Spectroscopic ellipsometry study was employed for phase pure VO2(M1 thin films grown at different oxygen partial pressures by reactive magnetron sputtering. The optical constants of the VO2(M1 thin films have been determined in a photon energy range between 0.73 and 5.05 eV. The near-infrared extinction coefficient and optical conductivity of VO2(M1 thin films rapidly increase with decreasing O2-Ar ratios. Moreover, two electronic transitions can be uniquely assigned. The energy gaps correlated with absorption edge (E1 at varied O2-Ar ratios are almost the same (~2.0 eV; consequently, the absorption edge is not significantly changed. However, the optical band gap corresponding to semiconductor-to-metal phase transition (E2 decreases from 0.53 to 0.18 eV with decreasing O2-Ar ratios.

  12. Studies of the composition, tribology and wetting behavior of silicon nitride films formed by pulsed reactive closed-field unbalanced magnetron sputtering

    International Nuclear Information System (INIS)

    Yao, Zh.Q.; Yang, P.; Huang, N.; Wang, J.; Wen, F.; Leng, Y.X.

    2006-01-01

    Silicon nitride films were formed by pulsed reactive closed-field unbalanced magnetron sputtering of high purity Si targets in an Ar-N 2 mixture. The effects of N 2 fraction on the chemical composition, and tribological and wetting behaviors were investigated. The films deposited at a high N 2 fraction were consistently N-rich. The surface microstructure changed from continuous granular surrounded by tiny void regions to a homogeneous and dense microstructure, and densitied as the N 2 fraction is increased. The as-deposited films have a relatively low friction coefficient and better wear resistance than 316L stainless steel under dry sliding friction and experienced only abrasive wear. The decreased surface roughness and increased nitrogen incorporation in the film give rise to increased contact angle with double-stilled water from 24 deg. to 49.6 deg. To some extent, the silicon nitride films deposited are hydrophilic in nature

  13. Effect of deposition temperature on the properties of nitrogen-doped AZO thin films grown on glass by rf reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Cho, Shinho, E-mail: scho@silla.ac.kr [Center for Green Fusion Technology and Department of Electronic Materials Engineering, Silla University, Busan 617-736 (Korea, Republic of); Kim, Heetae [Backlight Technology, LCD Division, Samsung Electronics Co., Ltd., Asan 336-841 (Korea, Republic of)

    2010-09-15

    Nitrogen-doped aluminum zinc oxide (NAZO) thin films were deposited on glass substrates at various deposition temperatures by rf reactive magnetron sputtering. The NAZO film deposited at 400 deg. C shows a strongly c-axis preferred orientation and n-type conduction with a resistivity of 2.1 x 10{sup -2} {Omega} cm, Hall mobility of 7.7 cm{sup 2} V{sup -1} s{sup -1}, and electron concentration of 3.8 x 10{sup 19} cm{sup -3}. The optimum crystallographic structure occurs at a deposition temperature of 400 deg. C, where a considerable crystallinity enhancement of the films is observed. The band gap energies of the NAZO films, obtained by using Tauc model and parabolic bands, are found to significantly depend on the deposition temperature, along with the band gap narrowing at higher deposition temperature due to renormalization effects.

  14. STRUCTURAL, PHOTO-FUNCTIONAL AND SEMICONDUCTOR PROPERTIES OF COPPER OXIDE THIN FILMS PREPARED BY DC REACTIVE METHOD UNDER VARIOUS THICKNESSES Anmar H. Shukur

    Directory of Open Access Journals (Sweden)

    Anmar H. Shukur

    2018-01-01

    Full Text Available Cuprous oxide (Cu2O has been formed on glass substrates by dc reactive magnetron sputtering method, whereas pure target of the solid copper was sputtered with a mixture of plasma for argon gas and oxygen gas was used to form these films. Under vacuum chamber pressure of 1.2×10-5 Pa, thin film thickness was changed from 100 nm to 300 nm while other deposition parameters were fixed. The influence of changing the thickness of thin films on the electrical and the optical properties was investigated in this study. X-ray photoelectron spectroscopy (XPS, X-ray Diffractions system XRD, Atomic Force Microscopy (AFM, hall effect measurement system, UV–VIS spectrophotometer were employed to determine the characteristic of the deposited thin films. Thin film of 200 nm has observed low resistivity of 60.63 Ω cm and direct band gap of 2.5eV. This study has demonstrated that the thickness has direct influence on electrical and optical properties.

  15. Structural, electrical and magnetic characterization of in-situ crystallized ZnO:Co thin films synthesized by reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Lardjane, Soumia, E-mail: lardjanesoumia@yahoo.fr [IRTES-LERMPS, UTBM, Site de Montbéliard, 90010 Belfort Cedex (France); Division Etude et Prédiction des Matériaux, Unité de Recherche Matériaux et Energies Renouvelables, Université Abou Bekr Belkaid, Tlemcen (Algeria); Pour Yazdi, Mohammad Arab [IRTES-LERMPS, UTBM, Site de Montbéliard, 90010 Belfort Cedex (France); Martin, Nicolas [FEMTO-ST, Département MN2S, UMR 6174 CNRS, Université de Franche-Comté, ENSMM, UTBM, 32, Avenue de l’Observatoire, 25044 Besancon Cedex (France); Bellouard, Christine [Laboratoire de Physique des Matériaux, Nancy University, CNRS, 54506 Vandoeuvre-lès-Nancy Cedex (France); Fenineche, Nour-eddine [IRTES-LERMPS, UTBM, Site de Montbéliard, 90010 Belfort Cedex (France); Schuler, Andreas [Solar Energy and Buildings Physics Laboratory, EPFL ENAC IIC LESO-PB, Station 18, Bâtiment LE, 1015 Lausanne (Switzerland); Merad, Ghouti [Division Etude et Prédiction des Matériaux, Unité de Recherche Matériaux et Energies Renouvelables, Université Abou Bekr Belkaid, Tlemcen (Algeria); Billard, Alain [IRTES-LERMPS, UTBM, Site de Montbéliard, 90010 Belfort Cedex (France)

    2015-07-01

    Zn{sub 1−x}Co{sub x}O (0 < x < 0.146) conductive thin films have been deposited by reactive magnetron sputtering of metallic Zn and Co targets at high pressure and temperature. The structural properties have been investigated by using X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). It has been observed that all as-deposited films are crystallized in pure hcp ZnO structure and neither traces of metallic nor oxide Co-rich clusters were detected. The average grain size estimated from full width at half maximum of XRD results varied between 65 and 83 nm. XPS analyses exhibit that Co ions are successfully entered into ZnO lattice as Co{sup +2}. The electrical properties including conductivity, carrier density and carrier mobility were determined by Hall effect measurements in a temperature range from 300 K to 475 K. The conductivity of the films decreases from σ{sub 300K} = 2.2 × 10{sup 4} to 2.3 × 10{sup −1} Sm{sup −1} as the Co content changes from 0 to 0.146. Magnetic measurements reveal the absence of ferromagnetism even at 3 K and a paramagnetic Curie–Weiss behavior associated to magnetic clusters. - Highlights: • Zn{sub 1−x}Co{sub x}O conductive thin films were synthesized by reactive magnetron sputtering. • Structural characterization exhibited the absence of Co clusters or secondary phases. • The film conductivity decreased with increasing of Co concentration. • No ferromagnetism was observed in all Co doped ZnO samples. • Magnetic properties are described by a Curie–Weiss behavior associated to clusters.

  16. Tube Inner Coating of Non-Conductive Films by Pulsed Reactive Coaxial Magnetron Plasma with Outer Anode

    Directory of Open Access Journals (Sweden)

    Musab Timan Idriss Gasab

    2018-03-01

    Full Text Available The double-ended coaxial magnetron pulsed plasma (DCMPP method with auxiliary outer anode was introduced in order to achieve the uniform coating of non-conductive thin films on the inner walls of insulator tubes. In this study, titanium (Ti was employed as a cathode (sputtering target, and a glass tube was used as a substrate. In an argon (Ar and oxygen (O2 gas mixture, magnetron plasma was generated. Oxygen gas was introduced to deposit a titanium oxide (TiO2 film. A comparison between films coated with and without an auxiliary outer anode was made. As a result, it was clearly shown that the DCMPP method using an auxiliary outer anode enhanced the uniformity of the deposited non-conductive film compared to the conventional DCMPP method. Moreover, the optimum conditions under which the thin TiO2 film was deposited on the inner wall of the glass tube were revealed. From the results, it was supposed that the auxiliary outer anode contributed to the uniformity of the distributions of deposited negative charge on the non-conductive film and consequently the electric field and the plasma density uniform.

  17. Optical and Chemical Properties of Mixed-valent Rhenium Oxide Films Synthesized by Reactive DC Magnetron Sputtering

    Science.gov (United States)

    2015-04-03

    films were deposited within a stainless steel high vacuum chamber evacuated to a pressure of 5.3 105 Pa (4 107 Torr). A 3 mm thick, 50 mm diameter...G.E. Jellison, Thin Solid Films 234 (1993) 416 –422. [34] J.I. Pankove, Absorption, in: Optical Processes in Semiconductors, Dover Publications, New

  18. Investigation of DC magnetron-sputtered TiO2 coatings: Effect of coating thickness, structure, and morphology on photocatalytic activity

    DEFF Research Database (Denmark)

    Daviðsdóttir, Svava; Shabadi, Rajashekhara; Galca, Aurelian Catalin

    2014-01-01

    The photocatalytic performance of magnetron-sputtered titanium dioxide (TiO2) coatings of different thickness in anatase crystalline structure deposited on aluminium 1050 alloy substrates was investigated using a combination of photo-electrochemistry, methylene blue decomposition, and microscopic...

  19. Amorphous indium-tin-zinc oxide films deposited by magnetron sputtering with various reactive gases: Spatial distribution of thin film transistor performance

    International Nuclear Information System (INIS)

    Jia, Junjun; Torigoshi, Yoshifumi; Shigesato, Yuzo; Kawashima, Emi; Utsuno, Futoshi; Yano, Koki

    2015-01-01

    This work presents the spatial distribution of electrical characteristics of amorphous indium-tin-zinc oxide film (a-ITZO), and how they depend on the magnetron sputtering conditions using O 2 , H 2 O, and N 2 O as the reactive gases. Experimental results show that the electrical properties of the N 2 O incorporated a-ITZO film has a weak dependence on the deposition location, which cannot be explained by the bombardment effect of high energy particles, and may be attributed to the difference in the spatial distribution of both the amount and the activity of the reactive gas reaching the substrate surface. The measurement for the performance of a-ITZO thin film transistor (TFT) also suggests that the electrical performance and device uniformity of a-ITZO TFTs can be improved significantly by the N 2 O introduction into the deposition process, where the field mobility reach to 30.8 cm 2 V –1 s –1 , which is approximately two times higher than that of the amorphous indium-gallium-zinc oxide TFT

  20. Er2O3 coating by reactive magnetron sputtering: Effect of oxygen supply and erbium pre-layer deposition

    Directory of Open Access Journals (Sweden)

    P.A. Rayjada

    2016-12-01

    The film grows in mixed phase of cubic and monoclinic structures when erbium metal pre-layer is deposited on the P91 steel substrate and in pure monoclinic phase in absence of the pre-layer. Post annealing seems to partially convert monoclinic into cubic phase in the mixed phase coating. Better crystallization and slightly more surface roughness is observed in the sample processed with higher oxygen to argon ratio. DC resistivity is found in 1015Ω*cm range and it is marginally more in the sample processed with more oxygen. The spectroscopic ellipsometry on these films to obtain optical dielectric properties gives encouraging results in terms of close match of the thickness and roughness values with those obtained from SEM and AFM respectively. Systematic study of optical dielectric property suggests a trend consistent with DC resistivity.

  1. Polyester fabric coated with Ag/ZnO composite film by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Yuan, Xiaohong, E-mail: yxhong1981_2004@126.com [Key Laboratory of Eco-Textiles, Ministry of Education, Jiangnan University, Wuxi 214122, Jiangsu (China); Faculty of Clothing and Design, Minjiang University, Fuzhou 350121, Fujian (China); Xu, Wenzheng, E-mail: xwz8199@126.com [Key Laboratory of Eco-Textiles, Ministry of Education, Jiangnan University, Wuxi 214122, Jiangsu (China); Huang, Fenglin, E-mail: windhuang325@163.com [Key Laboratory of Eco-Textiles, Ministry of Education, Jiangnan University, Wuxi 214122, Jiangsu (China); Chen, Dongsheng, E-mail: mjuchen@126.com [Faculty of Clothing and Design, Minjiang University, Fuzhou 350121, Fujian (China); Wei, Qufu, E-mail: qfwei@jiangnan.edu.cn [Key Laboratory of Eco-Textiles, Ministry of Education, Jiangnan University, Wuxi 214122, Jiangsu (China)

    2016-12-30

    Highlights: • Ag/ZnO composite film was successfully deposited on polyester fabric by magnetron sputtering technique. • Ag film was easily oxidized into Ag{sub 2}O film in high vacuum oxygen environment. • The zinc film coated on the surface of Ag film before RF reactive sputtering could protect the silver film from oxidation. • Polyester fabric coated with Ag/ZnO composite film can obtained structural color. • The anti-ultraviolet and antistatic properties of polyester fabric coated with Ag/ZnO composite film all were good. - Abstract: Ag/ZnO composite film was successfully deposited on polyester fabric by using direct current (DC) magnetron sputtering and radio frequency (RF) magnetron reaction sputtering techniques with pure silver (Ag) and zinc (Zn) targets. X-ray photoelectron spectroscopy (XPS) and X-ray diffraction (XRD) were used to examine the deposited film on the fabric. It was found that the zinc film coated on Ag film before RF reactive sputtering could protect the silver film from oxidation. Anti-ultraviolet property and antistatic property of the coated samples using different magnetron sputtering methods were also investigated. The experimental results showed that Ag film was oxidized into in Ag{sub 2}O film in high vacuum oxygen environment. The deposition of Zn film on the surface of the fabric coated with Ag film before RF reactive sputtering, could successfully obtained Ag/ZnO composite film, and also generated structural color on the polyester fabric.

  2. Effect of various nitrogen flow ratios on the optical properties of (Hf:N-DLC films prepared by reactive magnetron sputtering

    Directory of Open Access Journals (Sweden)

    Meng Qi

    2017-08-01

    Full Text Available Hf and N co-doped diamond-like carbon [(Hf:N-DLC] films were deposited on 316L stainless steel and glass substrates through reactive magnetron sputtering of hafnium and carbon targets at various nitrogen flow ratios (R=N2/[N2+CH4+Ar]. The effects of chemical composition and crystal structure on the optical properties of the (Hf:N-DLC films were studied. The obtained films consist of uniform HfN nanocrystallines embedded into the DLC matrix. The size of the graphite clusters with sp2 bonds (La and the ID/IG ratio increase to 2.47 nm and 3.37, respectively, with increasing R. The optical band gap of the films decreases from 2.01 eV to 1.84 eV with increasing R. This finding is consistent with the trends of structural transformations and could be related to the increase in the density of π-bonds due to nitrogen incorporation. This paper reports the influence of nitrogen flow ratio on the correlation among the chemical composition, crystal structure, and optical properties of (Hf:N-DLC films.

  3. Structure and phase composition of the titanium dioxide thin films deposited on the surface of the metallized track membranes from polyethyleneterephthalate by reactive magnetron sputtering

    International Nuclear Information System (INIS)

    Artoshina, O.V.; Semina, V.K.; Kochnev, Yu.K.; Nechaev, A.N.; Apel', P.Yu.; Milovich, F.O.; Iskhakova, L.D.; Ermakov, R.P.; Rossouw, A.; Gorberg, B.L.

    2016-01-01

    Thin films of TiO 2 , Ag, Ag-TiO 2 , Cu-TiO 2 deposited on the surface of polyethyleneterephthalate track membranes (TM) were investigated. Metals and oxide deposition was carried out by the method of vacuum reactive sputtering with application of a planar magnetron. The microstructure of samples was studied by the scanning and transmission electron microscopy (TEM) techniques. The elemental composition of coatings was investigated using energy-dispersive spectroscopy. For the identification of phase structure, X-ray diffraction phase analysis was used at various temperatures, and the XRD crystal structure patterns of the samples were obtained by the selected area electron diffraction (SAED) in TEM analysis. It was found that titanium dioxide on the TM surface can be present in three forms: nanocrystals of tetragonal anatase with impurity of rhombic brookite and the so-called X-ray amorphous TiO 2 . Cubical Cu 2 O was identified in TM metallized by copper. Optical properties of composite membranes and films were investigated by the method of absorption spectroscopy. Calculation of energies of the direct and indirect allowed optical transitions was carried out based on the analysis of absorption spectra of the studied composite membranes. [ru

  4. Transmission photocathodes based on stainless steel mesh and quartz glass coated with N-doped DLC thin films prepared by reactive magnetron sputtering

    Science.gov (United States)

    Balalykin, N. I.; Huran, J.; Nozdrin, M. A.; Feshchenko, A. A.; Kobzev, A. P.; Arbet, J.

    2016-03-01

    The influence was investigated of N-doped diamond-like carbon (DLC) films properties on the quantum efficiency of a prepared transmission photocathode. N-doped DLC thin films were deposited on a silicon substrate, a stainless steel mesh and quartz glass (coated with 5 nm thick Cr adhesion film) by reactive magnetron sputtering using a carbon target and gas mixture Ar, 90%N2+10%H2. The elements' concentration in the films was determined by RBS and ERD. The quantum efficiency was calculated from the measured laser energy and the measured cathode charge. For the study of the vectorial photoelectric effect, the quartz type photocathode was irradiated by intensive laser pulses to form pin-holes in the DLC film. The quantum efficiency (QE), calculated at a laser energy of 0.4 mJ, rose as the nitrogen concentration in the DLC films was increased and rose dramatically after the micron-size perforation in the quartz type photocathodes.

  5. Photomodulated reflectance study on optical property of InN thin films grown by reactive gas-timing rf magnetron sputtering

    International Nuclear Information System (INIS)

    Porntheeraphat, S.; Nukeaw, J.

    2008-01-01

    The photoreflectance (PR) spectroscopy has been applied to investigate the band-gap energy (E g ) of indium nitride (InN) thin films grown by rf magnetron sputtering. A novel reactive gas-timing technique applied for the sputtering process has been successfully employed to grow InN thin films without neither substrate heating nor post annealing. The X-ray diffraction (XRD) patterns exhibit strong peaks in the orientation along (0 0 2) and (1 0 1) planes, corresponding to the polycrystalline hexagonal-InN structure. The band-gap transition energy of InN was determined by fitting the PR spectra to a theoretical line shape. The PR results show the band-gap energy at 1.18 eV for hexagonal-InN thin films deposited at the rf powers of 100 and 200 W. The high rf sputtering powers in combination with the gas-timing technique should lead to a high concentration of highly excited nitrogen ions in the plasma, which enables the formation of InN without substrate heating. Auger electron spectroscopy (AES) measurements further reveal traces of oxygen in these InN films. This should explain the elevated band-gap energy, in reference to the band-gap value of 0.7 eV for pristine InN films

  6. Comparative study of total power density at a substrate in pulsed DC magnetron and hollow-cathode plasma jet sputtering systems

    Czech Academy of Sciences Publication Activity Database

    Čada, Martin; Virostko, Petr; Kment, Štěpán; Hubička, Zdeněk

    2009-01-01

    Roč. 6, S1 (2009), S247-S252 ISSN 1612-8850. [International Conference on Plasma Surface Engineering /11./. Garmisch Partenkirchen, 15.09.2008-19.09.2008] R&D Projects: GA AV ČR KAN301370701; GA AV ČR KJB100100707; GA AV ČR KJB100100805; GA MŠk(CZ) 1M06002 Institutional research plan: CEZ:AV0Z10100522 Keywords : calorimeter probe * floating substrate * magnetron * plasma jet * pulsed discharge Subject RIV: BH - Optics, Masers, Lasers Impact factor: 4.037, year: 2009

  7. Structure and electronic properties of AlCrO{sub x}N{sub 1−x} thin films deposited by reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Najafi, H.; Karimi, A. [Institute of Condensed Matter Physics (ICMP), Swiss Federal Institute of Technology Lausanne (EPFL), CH-1015 Lausanne (Switzerland); Oveisi, E. [Electron Spectrometry and Microscopy Laboratory (LSME-ICMP), Swiss Federal Institute of Technology in Lausanne (EPFL), CH-1015 Lausanne (Switzerland); Morstein, M. [PLATIT AG, Advanced Coating Systems, CH-2545 Selzach (Switzerland)

    2014-12-01

    In this study, the main attempt is devoted to investigating the microstructure and electronic properties of AlCrO{sub x}N{sub 1−x} films in a wide range of oxygen concentrations from 0 to 1. These oxynitride films were deposited by pulsed DC magnetron sputtering from Al{sub 55}Cr{sub 45} targets. Our results showed that films with x = O/(O + N) < 0.6, exhibit a cubic (B1) lattice with a well-developed columnar structure. The incorporation of oxygen into the films without any oxide segregation results in the formation of a substitutional AlCrO{sub x}N{sub 1−x} solid solution and material system behaves like nitrides electronically. In the range of oxygen contents from 0.6 ≤ O/(O + N) < 0.97, coatings with fine columns, diffuse boundaries and high values of metal vacancies were formed. However, the B1 lattice survived despite the large proportion of oxygen. According to the structural and electronic properties of the corresponding layers, we assign this region to the formation of an amorphous phase and metastable monoxides with a B1 structure. Coatings with O/(O + N) ≥ 0.97 are electronically assigned to a solid solution of α-(Al,Cr){sub 2}(O{sub 0.97},N{sub 0.03}){sub 3} with corundum lattice and finer columnar structure. - Highlights: • AlCr(O{sub x}N{sub 1−x}) layers with variable oxygen content 0 < x < 1 were grown. • The layers with the lowest oxygen content, x < 0.6, electronically behave like nitrides. • Coatings with 0.6 ≤ x < 0.97 are assigned to metastable monoxides. • The oxide region consisted of a solid solution of α-phase with a corundum structure.

  8. Morphology and structure evolution of Cu(In,Ga)S{sub 2} films deposited by reactive magnetron co-sputtering with electron cyclotron resonance plasma assistance

    Energy Technology Data Exchange (ETDEWEB)

    Nie, Man, E-mail: man.nie@helmholtz-berlin.de; Ellmer, Klaus [Department of Solar Fuels and Energy Storage Materials, Helmholtz-Zentrum Berlin für Materialien und Energie GmbH, Hahn-Meitner-Platz 1, D14109 Berlin (Germany)

    2014-02-28

    Cu(In,Ga)S{sub 2} (CIGS) films were deposited on Mo coated soda lime glass substrates using an electron cyclotron resonance plasma enhanced one-step reactive magnetron co-sputtering process (ECR-RMS). The crystalline quality and the morphology of the Cu(In,Ga)S{sub 2} films were investigated by X-ray diffraction, atomic force microscopy, scanning electron microscopy, and X-ray fluorescence. We also compared these CIGS films with films previously prepared without ECR assistance and find that the crystallinity of the CIGS films is correlated with the roughness evolution during deposition. Atomic force microscopy was used to measure the surface topography and to derive one-dimensional power spectral densities (1DPSD). All 1DPSD spectra of CIGS films exhibit no characteristic peak which is typical for the scaling of a self-affine surface. The growth exponent β, characterizing the roughness R{sub q} evolution during the film growth as R{sub q} ∼ d{sup β}, changes with film thickness. The root-mean-square roughness at low temperatures increases only slightly with a growth exponent β = 0.013 in the initial growth stage, while R{sub q} increases with a much higher exponent β = 0.584 when the film thickness is larger than about 270 nm. Additionally, we found that the H{sub 2}S content of the sputtering atmosphere and the Cu- to-(In + Ga) ratio has a strong influence of the morphology of the CIGS films in this one-step ECR-RMS process.

  9. Low-loss interference filter arrays made by plasma-assisted reactive magnetron sputtering (PARMS) for high-performance multispectral imaging

    Science.gov (United States)

    Broßmann, Jan; Best, Thorsten; Bauer, Thomas; Jakobs, Stefan; Eisenhammer, Thomas

    2016-10-01

    Optical remote sensing of the earth from air and space typically utilizes several channels in the visible and near infrared spectrum. Thin-film optical interference filters, mostly of narrow bandpass type, are applied to select these channels. The filters are arranged in filter wheels, arrays of discrete stripe filters mounted in frames, or patterned arrays on a monolithic substrate. Such multi-channel filter assemblies can be mounted close to the detector, which allows a compact and lightweight camera design. Recent progress in image resolution and sensor sensitivity requires improvements of the optical filter performance. Higher demands placed on blocking in the UV and NIR and in between the spectral channels, in-band transmission and filter edge steepness as well as scattering lead to more complex filter coatings with thicknesses in the range of 10 - 25μm. Technological limits of the conventionally used ion-assisted evaporation process (IAD) can be overcome only by more precise and higher-energetic coating technologies like plasma-assisted reactive magnetron sputtering (PARMS) in combination with optical broadband monitoring. Optics Balzers has developed a photolithographic patterning process for coating thicknesses up to 15μm that is fully compatible with the advanced PARMS coating technology. This provides the possibility of depositing multiple complex high-performance filters on a monolithic substrate. We present an overview of the performance of recently developed filters with improved spectral performance designed for both monolithic filter-arrays and stripe filters mounted in frames. The pros and cons as well as the resulting limits of the filter designs for both configurations are discussed.

  10. Characterization of single crystal uranium-oxide thin films grown via reactive-gas magnetron sputtering on yttria-stabilized zirconia and sapphire

    Energy Technology Data Exchange (ETDEWEB)

    Strehle, Melissa M.; Heuser, Brent J., E-mail: bheuser@illinois.edu; Elbakhshwan, Mohamed S.; Han Xiaochun; Gennardo, David J.; Pappas, Harrison K.; Ju, Hyunsu

    2012-06-30

    The microstructure and valence states of three single crystal thin film systems, UO{sub 2} on (11{sup Macron }02) r-plane sapphire, UO{sub 2} on (001) yttria-stabilized zirconia, and U{sub 3}O{sub 8} on (11{sup Macron }02) r-plane sapphire, grown via reactive-gas magnetron sputtering are analyzed primarily with X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and ultraviolet photoelectron spectroscopy (UPS). XRD analysis indicates the growth of single crystal domains with varying degrees of mosaicity. XPS and UPS analyses yield U-4f, U-5f, O-1s, and O-2p electron binding energies consistent with reported bulk values. A change from p-type to n-type semiconductor behavior induced by preferential sputtering of oxygen during depth profile analysis was observed with both XPS and UPS. Trivalent cation impurities (Nd and Al) in UO{sub 2} lower the Fermi level, shifting the XPS spectral weight. This observation is consistent with hole-doping of a Mott-Hubbard insulator. The uranium oxide-(11{sup Macron }02) sapphire system is unstable with respect to Al interdiffusion across the film-substrate interface at elevated temperature. - Highlights: Black-Right-Pointing-Pointer Single crystal uranium-oxides grown on sapphire and yttria-stabilized zirconia. Black-Right-Pointing-Pointer Anion and cation valence states studied by photoelectron emission spectroscopy. Black-Right-Pointing-Pointer Trivalent Nd and Al impurities lower the Fermi level. Black-Right-Pointing-Pointer Uranium-oxide films on sapphire found to be unstable with respect to Al interdiffusion.

  11. Compositionally modulated multilayer diamond-like carbon coatings with AlTiSi multi-doping by reactive high power impulse magnetron sputtering

    Science.gov (United States)

    Dai, Wei; Gao, Xiang; Liu, Jingmao; Kwon, Se-Hun; Wang, Qimin

    2017-12-01

    Diamond-like carbon (DLC) coatings with AlTiSi multi-doping were prepared by a reactive high power impulse magnetron sputtering with using a gas mixture of Ar and C2H2 as precursor. The composition, microstructure, compressive stress, and mechanical property of the as-deposited DLC coatings were studied systemically by using SEM, XPS, TEM, Raman spectrum, stress-tester, and nanoindentation as a function of the Ar fraction. The results show that the doping concentrations of the Al, Ti and Si atoms increased as the Ar fraction increased. The doped Ti and Si preferred to bond with C while the doped Al mainly existed in oxidation state without bonding with C. As the doping concentrations increased, TiC carbide nanocrystals were formed in the DLC matrix. The microstructure of coatings changed from an amorphous feature dominant AlTiSi-DLC to a carbide nanocomposite AlTiSi-DLC with TiC nanoparticles embedding. In addition, the coatings exhibited the compositionally modulated multilayer consisting of alternate Al-rich layer and Al-poor layer due to the rotation of the substrate holder and the diffusion behavior of the doped Al which tended to separate from C and diffuse towards the DLC matrix surface owing to its weak interactions with C. The periodic Al-rich layer can effectively release the compressive stress of the coatings. On the other hand, the hard TiC nanoparticles were conducive to the hardness of the coatings. Consequently, the DLC coatings with relatively low residual stress and high hardness could be acquired successfully through AlTiSi multi-doping. It is believed that the AlCrSi multi-doping may be a good way for improving the comprehensive properties of the DLC coatings. In addition, we believe that the DLC coatings with Al-rich multilayered structure have a high oxidation resistance, which allows the DLC coatings application in high temperature environment.

  12. Intrinsic Photocatalytic Assessment of Reactively Sputtered TiO2 Films

    NARCIS (Netherlands)

    Rafieian Boroujeni, Damon; Driessen, Rick Theodorus; Driessen, Rick T.; Ogieglo, Wojciech; Lammertink, Rob G.H.

    2015-01-01

    Thin TiO2 films were prepared by DC magnetron reactive sputtering at different oxygen partial pressures. Depending on the oxygen partial pressure during sputtering, a transition from metallic Ti to TiO2 was identified by spectroscopic ellipsometry. The crystalline nature of the film developed during

  13. High power pulsed magnetron sputtering of transparent conducting oxides

    International Nuclear Information System (INIS)

    Sittinger, V.; Ruske, F.; Werner, W.; Jacobs, C.; Szyszka, B.; Christie, D.J.

    2008-01-01

    High power pulsed magnetron sputtering (HPPMS) has been used in order to study the deposition of transparent conducting oxides. We summarize the studies carried out on different materials (indium tin oxide-ITO and aluminium-doped zinc oxide-AZO) using rather different technological approaches, namely sputtering of ceramic targets and reactive sputtering. For the deposition of AZO reactive HPPMS for metallic targets has been used. A feedback control loop has been implemented in order to stabilize the discharge at any given setpoint on the hysteresis curve. The hysteresis was also found to have a rather untypical form. Reactive HPPMS was found to be a promising tool for obtaining high quality films of low total thickness. In the case of ITO deposition a ceramic target has been used. The process has been characterized in terms of its plasma emission and increasing indium ionization was found for higher peak power densities. The properties of the deposited films were compared to DC sputtered films. While for DC sputtering the choice of oxygen addition and shieldings is crucial for determining surface morphology and resistivity, in HPPMS sputtering peak power density has been found to be a good parameter for influencing the crystal structure. The morphologies obtained differ strongly from those seen in DC sputtering. At high power densities films with low surface roughness and excellent resistivity could be deposited without the use of shieldings

  14. Influence of reactive gas admixture on transition metal cluster nucleation in a gas aggregation cluster source

    Science.gov (United States)

    Peter, Tilo; Polonskyi, Oleksandr; Gojdka, Björn; Mohammad Ahadi, Amir; Strunskus, Thomas; Zaporojtchenko, Vladimir; Biederman, Hynek; Faupel, Franz

    2012-12-01

    We quantitatively assessed the influence of reactive gases on the formation processes of transition metal clusters in a gas aggregation cluster source. A cluster source based on a 2 in. magnetron is used to study the production rate of titanium and cobalt clusters. Argon served as working gas for the DC magnetron discharge, and a small amount of reactive gas (oxygen and nitrogen) is added to promote reactive cluster formation. We found that the cluster production rate depends strongly on the reactive gas concentration for very small amounts of reactive gas (less than 0.1% of total working gas), and no cluster formation takes place in the absence of reactive species. The influence of discharge power, reactive gas concentration, and working gas pressure are investigated using a quartz micro balance in a time resolved manner. The strong influence of reactive gas is explained by a more efficient formation of nucleation seeds for metal-oxide or nitride than for pure metal.

  15. Transparent Conductive In and Ga Doped ZnO/Cu Bi-Layered Films Deposited by DC and RF Magnetron Sputtering

    International Nuclear Information System (INIS)

    Moon, Hyun-Joo; Song, Young-Hwan; Oh, Jung-Hyun; Heo, Sung-Bo; Kim, Daeil

    2016-01-01

    In- and Ga-doped ZnO (IGZO) films were deposited on 5 nm thick Cu film buffered poly-carbonate substrates with RF magnetron sputtering and the effects of the Cu buffer layer on the optical and electrical properties of the films were investigated. The IGZO single layer films exhibited an electrical resistivity of 1.2×10"-1 Ω cm while the IGZO/Cu bi-layered films exhibited a lower resistivity of 1.6×10"-3 Ω cm. With respect to optical properties, the optical band gap of the IGZO films appeared to decrease as a result of an increasing carrier concentration due to the Cu buffer layer. In addition, the RMS roughness (8.2 nm) of the IGZO films also decreased to 6.8 nm by a Cu buffer layer in AFM observation. Although the optical transmittance in the range of visible wavelengths was deteriorated by the Cu buffer layer, the IGZO films with a 5 nm thick Cu buffer layer exhibited a higher figure of merit of 2.6×10"-4 Ω"-1 compared with the IGZO single layer films due to enhanced optoelectrical performance.

  16. Transparent Conductive In and Ga Doped ZnO/Cu Bi-Layered Films Deposited by DC and RF Magnetron Sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Moon, Hyun-Joo; Song, Young-Hwan; Oh, Jung-Hyun; Heo, Sung-Bo; Kim, Daeil [University of Ulsan, Ulsan (Korea, Republic of)

    2016-06-15

    In- and Ga-doped ZnO (IGZO) films were deposited on 5 nm thick Cu film buffered poly-carbonate substrates with RF magnetron sputtering and the effects of the Cu buffer layer on the optical and electrical properties of the films were investigated. The IGZO single layer films exhibited an electrical resistivity of 1.2×10{sup -}1 Ω cm while the IGZO/Cu bi-layered films exhibited a lower resistivity of 1.6×10{sup -}3 Ω cm. With respect to optical properties, the optical band gap of the IGZO films appeared to decrease as a result of an increasing carrier concentration due to the Cu buffer layer. In addition, the RMS roughness (8.2 nm) of the IGZO films also decreased to 6.8 nm by a Cu buffer layer in AFM observation. Although the optical transmittance in the range of visible wavelengths was deteriorated by the Cu buffer layer, the IGZO films with a 5 nm thick Cu buffer layer exhibited a higher figure of merit of 2.6×10{sup -}4 Ω{sup -}1 compared with the IGZO single layer films due to enhanced optoelectrical performance.

  17. Influence of Microwave Power on the Properties of Hydrogenated Diamond-Like Carbon Films Prepared by ECR Plasma Enhanced DC Magnetron Sputtering

    International Nuclear Information System (INIS)

    Ru Lili; Huang Jianjun; Gao Liang; Qi Bing

    2010-01-01

    Electron cyclotron resonance (ECR) plasma was applied to enhance the direct current magnetron sputtering to prepare hydrogenated diamond-like carbon (H-DLC) films. For different microwave powers, both argon and hydrogen gas are introduced separately as the ECR working gas to investigate the influence of microwave power on the microstructure and electrical property of the H-DLC films deposited on P-type silicon substrates. A series of characterization methods including the Raman spectrum and atomic force microscopy are used. Results show that, within a certain range, the increase in microwave power affects the properties of the thin films, namely the sp 3 ratio, the hardness, the nanoparticle size and the resistivity all increase while the roughness decreases with the increase in microwave power. The maximum of resistivity amounts to 1.1 x 10 9 Ω · cm. At the same time it is found that the influence of microwave power on the properties of H-DLC films is more pronounced when argon gas is applied as the ECR working gas, compared to hydrogen gas.

  18. Microporous TiO2-WO3/TiO2 films with visible-light photocatalytic activity synthesized by micro arc oxidation and DC magnetron sputtering

    International Nuclear Information System (INIS)

    Wu, Kee-Rong; Hung, Chung-Hsuang; Yeh, Chung-Wei; Wu, Jiing-Kae

    2012-01-01

    Highlights: ► A simple MAO is used to prepare porous WO 3 /TiO 2 layer on Ti sheet as a visible-light enabled catalyst. ► The photocatalytic activity of the WO 3 /TiO 2 is enhanced by sputtering over an N,C-TiO 2 layer. ► This is ascribed to the synergetic effect of hybrid sample prepared by two-step method. - Abstract: This study reports the preparation of microporous TiO 2 -WO 3 /TiO 2 films with a high surface area using a two-step approach. A porous WO 3 /TiO 2 template was synthesized by oxidizing a titanium sheet using a micro arc oxidation (MAO) process. This sheet was subsequently overlaid with a visible light (Vis)-enabled TiO 2 (N,C-TiO 2 ) film, which was deposited by codoping nitrogen (N) and carbon (C) ions into a TiO 2 lattice using direct current magnetron sputtering. The resulting microporous TiO 2 -WO 3 /TiO 2 film with a 0.38-μm-thick N,C-TiO 2 top-layer exhibited high photocatalytic activity in methylene blue (MB) degradation among samples under ultraviolet (UV) and Vis irradiation. This is attributable to the synergetic effect of two-step preparation method, which provides a highly porous microstructure and the well-crystallized N,C-TiO 2 top-layer. This is because a higher surface area with high crystallinity favors the adsorption of more MB molecules and more photocatalytic active areas. Thus, the microporous TiO 2 -WO 3 /TiO 2 film has promising applications in the photocatalytic degradation of dye solution under UV and Vis irradiation. These results imply that the microporous WO 3 /TiO 2 can be used as a template of hybrid electrode because it enables rapid fabrication.

  19. Effect of organic-buffer-layer on electrical property and environmental reliability of Ga-doped ZnO films prepared by RF plasma assisted DC magnetron sputtering on plastic substrate

    International Nuclear Information System (INIS)

    Hinoki, Toshio; Kyuhara, Chika; Agura, Hideaki; Yazawa, Kenji; Kinoshita, Kentaro; Ohmi, Koutoku; Kishida, Satoru

    2010-01-01

    Ga-doped ZnO (GZO) transparent conductive films have been prepared by RF plasma assisted DC magnetron sputtering under a reductive atmosphere on organic-buffer-layer (OBL) coated polyethylene telephthalate (PET) substrates without intentionally heating substrates. Electrical and optical properties, crystallinity, and environmental reliability of the GZO films have been investigated. The distributional characteristic of resistivity is observed in the GZO film deposited on the OBL-coated PET substrates. The high resistivity at facing the erosion area in the source target is reduced by providing the RF plasma and H 2 gas near the substrate, resulting in a uniform distribution of the sheet resistance. It has been also found that the increase of resistivity by an accelerated aging test performed under a storage condition at 60 o C and at a relative humidity of 95% is suppressed by employing the OBL. The OBL suppresses the formation of cracks, which are induced by the aging test. These facts are thought to contribute to a high environmental reliability of GZO films on PET substrates. Values of resistivity, Hall mobility and carrier concentration are obtained: 5.0-20 x 10 -3 Ω cm, 4.0 cm 2 /Vs, and 3.8 x 10 20 cm -3 , respectively. An average transmittance of the GZO film including OBL and PET substrate is 78% in a visible region. The OBL enables to realize the practical use of GZO films on PET sheets.

  20. Pure and Nb2O5-doped TiO2 amorphous thin films grown by dc magnetron sputtering at room temperature: Surface and photo-induced hydrophilic conversion studies

    International Nuclear Information System (INIS)

    Suchea, M.; Christoulakis, S.; Tudose, I.V.; Vernardou, D.; Lygeraki, M.I.; Anastasiadis, S.H.; Kitsopoulos, T.; Kiriakidis, G.

    2007-01-01

    Photo-induced hydrophilicity of titanium dioxide makes this material one of the most suitable for various coating applications in antifogging mirrors and self-cleaning glasses. The field of functional titanium dioxide coatings is expanding rapidly not only in applications for glass but also in applications for polymer, metal and ceramic materials. The high hydrophilic surface of TiO 2 is interesting for understanding also the basic photon-related surface science of titanium dioxide. In doing so, it is inevitably necessary to understand the relationship between the photoreaction and the surface properties. In this work, photo-induced hydrophilic conversion was evaluated on amorphous pure and niobium oxide-doped titanium dioxide thin films on Corning 1737F glass grown by dc magnetron sputtering technique at room temperature. This study is focused on the influence of the Ar:O ratio during sputtering plasma deposition on thin film surface morphology and subsequent photo-induced hydrophilic conversion results. Structural characterization carried out by X-ray diffraction and atomic force microscopy (AFM) has shown that our films are amorphous and extremely smooth with a surface roughness bellow 1 nm. Contact angle measurements were performed on as-deposited and during/after 10 min UV exposure. We present evidence that the photo-induced hydrophilic conversion of film surface is directly correlated with surface morphology and can be controlled by growth conditions

  1. Effect of deposition temperature on the properties of Al-doped ZnO films prepared by pulsed DC magnetron sputtering for transparent electrodes in thin-film solar cells

    Science.gov (United States)

    Kim, Doo-Soo; Park, Ji-Hyeon; Shin, Beom-Ki; Moon, Kyeong-Ju; Son, Myoungwoo; Ham, Moon-Ho; Lee, Woong; Myoung, Jae-Min

    2012-10-01

    A simple but scalable approach to the production of surface-textured Al-doped ZnO(AZO) films for low-cost transparent electrode applications in thin-film solar cells is introduced in this study by combining pulsed dc magnetron sputtering (PDMS) with wet etching in sequence. First, structural, electrical, and optical properties of the AZO films prepared by a PDMS were investigated as functions of deposition temperature to obtain transparent electrode films that can be used as indium-free alternative to ITO electrodes. Increase in the deposition temperature to 230 °C accompanied the improvement in crystalline quality and doping efficiency, which enabled the lowest electrical resistivity of 4.16 × 10-4 Ω cm with the carrier concentration of 1.65 × 1021 cm-3 and Hall mobility of 11.3 cm2/V s. The wet etching of the films in a diluted HCl solution resulted in surface roughening via the formation of crater-like structures without significant degradation in the electrical properties, which is responsible for the enhanced light scattering capability required for anti-reflective electrodes in thin film solar cells.

  2. Effect of a Ga-doped ZnO thin film with a ZTO buffer layer fabricated by using pulsed DC magnetron sputter for dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Song, Sang-Woo; Lee, Kyung-Ju; Roh, Ji-Hyung; Park, On-Jeon; Kim, Hwan-Sun; Moon, Byung-Moo [Korea University, Seoul (Korea, Republic of); Ji, Min-Woo [Yonsei University, Seoul (Korea, Republic of)

    2014-08-15

    The electrical property of a Ga-doped ZnO(GZO) thin film is well known to be similar that of commercialized fluorine-doped tin oxide(FTO). However GZO is limited for use at high process temperatures for solar cells because of its unstable resistivity at temperatures above 300 .deg. C. A GZO thin film compared to zinc tin oxide(ZTO)-GZO multilayer can be used at high process temperatures. A GZO thin film was deposited on glass by using pulsed DC magnetron sputter. Then, a ZTO buffer layer was deposited on the GZO surface. During the deposition, the working pressure was 5 mTorr (Z-1 glass) and 1 mTorr (Z-2 glass). Dye-sensitized solar cells (DSSCs) were fabricated using Z-1, Z-2 and commercialized FTO glasses. Z-2 showed a conversion efficiency of 4.265%, which was enhanced by 0.399% compared to that of the DSSCs using FTO(3.784%). The conversion efficiency for Z-1 (3.889%) was a little higher than that of FTO. Thus, the ZTO-GZO electrode showed better characteristics than those obtained using the FTO electrode, which can be attributed to the reduced charge recombination and series resistance.

  3. Influence of vanadium incorporation on the microstructure, mechanical and tribological properties of Nb–V–Si–N films deposited by reactive magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Ju, Hongbo; Xu, Junhua, E-mail: jhxu@just.edu.cn

    2015-09-15

    Composite Nb–V–Si–N films with various V contents (3.7–13.2 at.%) were deposited by reactive magnetron sputtering and the effects of V content on the microstructure, mechanical and tribological properties of Nb–V–Si–N films were investigated. The results revealed that a three-phase structure, consisting of face-centered cubic (fcc) Nb–V–Si–N, hexagonal close-packed (hcp) Nb–V–Si–N and amorphous Si{sub 3}N{sub 4}, co-exists in the Nb–V–Si–N films and the cubic phase is dominant. The hardness and critical load (L{sub c}) of Nb–V–Si–N films initially increased gradually and reached a summit, then decreased with the increasing V content in the films and the maximum values were 35 GPa and 9.8 N, respectively, at 6.4 at.% V. The combination of V into Nb–Si–N film led to the fracture toughness linearly increasing from 1.11 MPa·m{sup 1/2} at 3.7 at.% V to 1.67 MPa·m{sup 1/2} at 13.2 at.% V. At room temperature (RT), the average friction coefficient decreased from 0.80 at 3.7 at.% V to 0.55 at 13.2 at.% V for the Nb–V–Si–N films. The wear rate of Nb–V–Si–N films initially decreased and then increased after reaching a minimum value of about 6.35 × 10{sup −} {sup 7} mm{sup 3}/N·mm at 6.4 at.% V. As the rise of testing temperature from 200 °C to 600 °C, the average friction coefficient of Nb–V–Si–N films decreased with the increase of the testing temperature regardless of V content. However, the wear rate gradually increased for all films. The average friction coefficient and wear rate at RT and elevated temperatures were mainly influenced by the vanadium oxides with weakly bonded lattice planes. - Highlight: • Fcc-Nb–V–Si–N, hcp-Nb–V–Si–N and amorphous Si{sub 3}N{sub 4} co-existed in the films. • The amount of Si{sub 3}N{sub 4} decreased with increasing V content in the films. • Hardness of Nb–V–Si–N film (6.4 at.%) reached a maximum value of 35 GPa. • Addition of V led to the

  4. DC-magnetron sputtering of ZnO:Al films on (00.1)Al2O3 substrates from slip-casting sintered ceramic targets

    International Nuclear Information System (INIS)

    Miccoli, I.; Spampinato, R.; Marzo, F.; Prete, P.; Lovergine, N.

    2014-01-01

    Highlights: • ZnO:Al was DC-sputtered on sapphire >350 °C by slip-casting sintered AZO target. • Films are highly (00.1)-oriented, smooth and transparent in the NIR–visible range. • Films growth rate decreases with temperature, while their grain size increases. • A high temperature reduction for sticking coefficients of impinging species is proved. • We prove that Thornton model does not apply to high-temperature DC-sputtered ZnO. - Abstract: High (>350 °C) temperature DC-sputtering deposition of ZnO:Al thin films onto single-crystal (00.1) oriented Al 2 O 3 (sapphire) substrates is reported, using a ultrahigh-density, low-resistivity and low-cost composite ceramic target produced by slip-casting (pressureless) sintering of ZnO–Al 2 O 3 (AZO) powders. The original combination of high-angle θ–2θ (Bragg–Brentano geometry) X-ray diffraction with low angle θ–2θ X-ray reflectivity (XRR) techniques allows us to define the AZO target composition and investigate the structural properties and surface/interface roughness of as-sputtered ZnO:Al films; besides, the growth dynamics of ZnO:Al is unambiguously determined. The target turned out composed of the sole wurtzite ZnO and spinel ZnAl 2 O 4 phases. X-ray diffraction analyses revealed highly (00.1)-oriented (epitaxial) ZnO:Al films, the material mean crystallite size being in the 13–20 nm range and increasing with temperature between 350 °C and 450 °C, while the film growth rate (determined via XRR measurements) decreases appreciably. XRR spectra also allowed to determine rms surface roughness <1 nm for present films and showed ZnO:Al density changes by only a few percent between 350 °C and 450 °C. The latter result disproves the often-adopted Thornton model for the description of the sputter-grown ZnO films and instead points out toward a reduction of the sticking coefficients of impinging species, as the main origin of film growth rate and grain size dependence with temperature. Zn

  5. High-rate deposition of high-quality Sn-doped In2O3 films by reactive magnetron sputtering using alloy targets

    International Nuclear Information System (INIS)

    Oka, Nobuto; Kawase, Yukari; Shigesato, Yuzo

    2012-01-01

    Sn-doped In 2 O 3 (ITO) films were deposited on heated (200 °C) fused silica glass substrates by reactive DC sputtering with mid-frequency pulsing (50 kHz) and a plasma control unit combined with a feedback system of the optical emission intensity for the atomic O* line at 777 nm. A planar In–Sn alloy target was connected to the switching unit, which was operated in the unipolar pulse mode. The power density on the target was maintained at 4.4 W cm −2 during deposition. The feedback system precisely controlled the oxidation of the target surface in “the transition region.” The ITO film with lowest resistivity (3.1 × 10 −4 Ω cm) was obtained with a deposition rate of 310 nm min −1 and transmittance in the visible region of approximately 80%. The deposition rate was about 6 times higher than that of ITO films deposited by conventional sputtering using an oxide target.

  6. Growth and characterization of textured YBaCo{sub 2}O{sub 5+δ} thin films grown on (001)-SrTiO{sub 3} via DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Galeano, V. [Universidad Nacional de Colombia, Campus Medellín, Facultad de Ciencias, Departamento de Física, Laboratorio de Cerámicos y Vítreos, A.A. 568, Medellín (Colombia); Arnache, O. [Grupo de Estado Sólido, Departamento de Física, Universidad de Antioquia, A.A. 1226, Medellín (Colombia); Supelano, I.; Vargas, C.A. Parra [Universidad Pedagógica y Tecnológica de Colombia, Departamento de Física, Avenida Central del Norte 39-115, Tunja (Colombia); Morán, O., E-mail: omoranc@unal.edu.co [Universidad Nacional de Colombia, Campus Medellín, Facultad de Ciencias, Departamento de Física, Laboratorio de Cerámicos y Vítreos, A.A. 568, Medellín (Colombia)

    2016-06-30

    Thin films of the layered cobaltite YBaCo{sub 2}O{sub 5+δ} were successfully grown on (001)-oriented SrTiO{sub 3} single-crystal substrates by means of DC magnetron sputtering. The 112 phase of the compound was stabilized by choosing an adequate Co reactant and through careful thermal treatment of the target. The results demonstrate the strong influence of these variables on the final phase of the compound. A substrate temperature of 1053 K and an oxygen pressure of 300 Pa seemed to be appropriate growing conditions for depositing (00ℓ)-textured YBaCo{sub 2}O{sub 5+δ} thin films onto the chosen substrate. In like fashion to the polycrystalline YBaCo{sub 2}O{sub 5+δ}, the films showed a clear sequence of antiferromagnetic–ferromagnetic–paramagnetic transitions within a narrow temperature range. Well-defined hysteresis loops were observed at temperatures as high as 270 K, which supports the existence of a FM order in the films. In turn, the dependence of the resistivity on the temperature shows a semiconductor-like behavior, without any distinguishable structure, within the temperature range measured (50–350 K). The analysis of the experimental data showed that the transport mechanism in the films is well described by using the Mott variable range hopping (VRH) conduction model. - Highlights: • YBaCo{sub 2}O{sub 5+δ} thin films are grown on SrTiO{sub 3} substrates. • Strong (00ℓ) reflections are observed in the X-ray diffraction pattern. • A clear sequence of magnetic transitions is observed. • Semiconducting-like behavior is verified.

  7. Effect of Ta buffer and NiFe seed layers on pulsed-DC magnetron sputtered Ir{sub 20}Mn{sub 80}/Co{sub 90}Fe{sub 10} exchange bias

    Energy Technology Data Exchange (ETDEWEB)

    Oksuezoglu, Ramis Mustafa, E-mail: rmoksuzoglu@anadolu.edu.t [University of Anadolu, Faculty of Engineering and Architecture, Department of Materials Sciences and Engineering, Iki Eyluel Campus, 26555 Eskisehir (Turkey); Yildirim, Mustafa; Cinar, Hakan [University of Anadolu, Faculty of Engineering and Architecture, Department of Materials Sciences and Engineering, Iki Eyluel Campus, 26555 Eskisehir (Turkey); Hildebrandt, Erwin; Alff, Lambert [Department of Materials Sciences, Darmstadt University of Technology, Petersenstrasse 23, D-64287 Darmstadt (Germany)

    2011-07-15

    A systematic investigation has been done on the correlation between texture, grain size evolution and magnetic properties in Ta/Ni{sub 81}Fe{sub 19}/Ir{sub 20}Mn{sub 80}/Co{sub 90}Fe{sub 10}/Ta exchange bias in dependence of Ta buffer and NiFe seed layer thickness in the range of 2-10 nm, deposited by pulsed DC magnetron sputtering technique. A strong dependence of <1 1 1> texture on the Ta/NiFe thicknesses was found, where the reducing and increasing texture was correlated with exchange bias field and unidirectional anisotropy energy constant at both NiFe/IrMn and IrMn/CoFe interfaces. However, a direct correlation between average grain size in IrMn and H{sub ex} and H{sub c} was not observed. L1{sub 2} phase IrMn{sub 3} could be formed by thickness optimization of Ta/NiFe layers by deposition at room temperature, for which the maximum exchange coupling parameters were achieved. We conclude finally that the coercivity is mainly influenced by texture induced interfacial effects at NiFe/IrMn/CoFe interfaces developing with Ta/NiFe thicknesses. - Research highlights: We discussed the influence of Ta/NiFe thicknesses on structure and grain size in AF layer and texture. A direct correlation between the <1 1 1> texture and exchange coupling was found. A direct relation between average grain size and H{sub ex} and H{sub c} was not observed. L1{sub 2} phase IrMn{sub 3} was formed by deposition at room temperature for Ta (5-6 nm)/NiFe (6-8 nm). We conclude that the coercivity is influenced by order/disorder at NiFe/IrMn/CoFe interfaces.

  8. Effect of deposition temperature on the properties of Al-doped ZnO films prepared by pulsed DC magnetron sputtering for transparent electrodes in thin-film solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Doo-Soo; Park, Ji-Hyeon; Shin, Beom-Ki; Moon, Kyeong-Ju [Information and Electronic Materials Research Laboratory, Department of Materials Science and Engineering, Yonsei University, 134 Shinchon-dong, Seodaemun-gu, Seoul 120-749 (Korea, Republic of); Son, Myoungwoo [Department of Nanobio Materials and Electronics, Gwangju Institute of Science and Technology, Gwangju 500-712 (Korea, Republic of); Ham, Moon-Ho [Department of Nanobio Materials and Electronics, Gwangju Institute of Science and Technology, Gwangju 500-712 (Korea, Republic of); School of Materials Science and Engineering, Gwangju Institute of Science and Technology, Gwangju 500-712 (Korea, Republic of); Lee, Woong [School of Nano and Advanced Materials Engineering, Changwon National University, 9 Sarim-Dong, Changwon, Gyeongnam 641-773 (Korea, Republic of); Myoung, Jae-Min, E-mail: jmmyoung@yonsei.ac.kr [Information and Electronic Materials Research Laboratory, Department of Materials Science and Engineering, Yonsei University, 134 Shinchon-dong, Seodaemun-gu, Seoul 120-749 (Korea, Republic of)

    2012-10-15

    Highlights: Black-Right-Pointing-Pointer Surface-textured AZO films were achieved by combining PDMS method with wet etching. Black-Right-Pointing-Pointer The AZO film deposited at 230 Degree-Sign C by PDMS exhibited the best performance. Black-Right-Pointing-Pointer It is due to the higher plasma density supplied from PDMS system. Black-Right-Pointing-Pointer Wet etching of the films produces a crater-like rough surface morphology. - Abstract: A simple but scalable approach to the production of surface-textured Al-doped ZnO(AZO) films for low-cost transparent electrode applications in thin-film solar cells is introduced in this study by combining pulsed dc magnetron sputtering (PDMS) with wet etching in sequence. First, structural, electrical, and optical properties of the AZO films prepared by a PDMS were investigated as functions of deposition temperature to obtain transparent electrode films that can be used as indium-free alternative to ITO electrodes. Increase in the deposition temperature to 230 Degree-Sign C accompanied the improvement in crystalline quality and doping efficiency, which enabled the lowest electrical resistivity of 4.16 Multiplication-Sign 10{sup -4} {Omega} cm with the carrier concentration of 1.65 Multiplication-Sign 10{sup 21} cm{sup -3} and Hall mobility of 11.3 cm{sup 2}/V s. The wet etching of the films in a diluted HCl solution resulted in surface roughening via the formation of crater-like structures without significant degradation in the electrical properties, which is responsible for the enhanced light scattering capability required for anti-reflective electrodes in thin film solar cells.

  9. Effect of deposition temperature on the properties of Al-doped ZnO films prepared by pulsed DC magnetron sputtering for transparent electrodes in thin-film solar cells

    International Nuclear Information System (INIS)

    Kim, Doo-Soo; Park, Ji-Hyeon; Shin, Beom-Ki; Moon, Kyeong-Ju; Son, Myoungwoo; Ham, Moon-Ho; Lee, Woong; Myoung, Jae-Min

    2012-01-01

    Highlights: ► Surface-textured AZO films were achieved by combining PDMS method with wet etching. ► The AZO film deposited at 230 °C by PDMS exhibited the best performance. ► It is due to the higher plasma density supplied from PDMS system. ► Wet etching of the films produces a crater-like rough surface morphology. - Abstract: A simple but scalable approach to the production of surface-textured Al-doped ZnO(AZO) films for low-cost transparent electrode applications in thin-film solar cells is introduced in this study by combining pulsed dc magnetron sputtering (PDMS) with wet etching in sequence. First, structural, electrical, and optical properties of the AZO films prepared by a PDMS were investigated as functions of deposition temperature to obtain transparent electrode films that can be used as indium-free alternative to ITO electrodes. Increase in the deposition temperature to 230 °C accompanied the improvement in crystalline quality and doping efficiency, which enabled the lowest electrical resistivity of 4.16 × 10 −4 Ω cm with the carrier concentration of 1.65 × 10 21 cm −3 and Hall mobility of 11.3 cm 2 /V s. The wet etching of the films in a diluted HCl solution resulted in surface roughening via the formation of crater-like structures without significant degradation in the electrical properties, which is responsible for the enhanced light scattering capability required for anti-reflective electrodes in thin film solar cells.

  10. Mechanical properties, chemical analysis and evaluation of antimicrobial response of Si-DLC coatings fabricated on AISI 316 LVM substrate by a multi-target DC-RF magnetron sputtering method for potential biomedical applications

    Science.gov (United States)

    Bociaga, Dorota; Sobczyk-Guzenda, Anna; Szymanski, Witold; Jedrzejczak, Anna; Jastrzebska, Aleksandra; Olejnik, Anna; Jastrzebski, Krzysztof

    2017-09-01

    In this study silicon doped diamond-like carbon (Si-DLC) coatings were synthesized on two substrates: silicon and AISI 316LVM stainless steel using a multi-target DC-RF magnetron sputtering method. The Si content in the films ranged between 4 and 16 at.%, and was controlled by the electrical power applied in RF regime to Si cathode target. The character of the chemical bonds was revealed by FTIR analysis. With the addition of silicon the hydroxyl absorption (band in the range of 3200-3600 cm-1) increased what suggests more hydrophilic character of the coating. There were also observed significant changes in bonding of Si atoms. For low content of dopant, Si-O-Si bond system is predominant, while for the highest content of silicon there is an evidence of the shift to Si-C bonds in close proximity to methyl groups. The Raman spectroscopy revealed that the G peak position is shifted to a lower wavenumber and the ID/IG ratio decreased with increasing Si content, which indicates an increase in the C-sp3 content. Regardless of the coatings' composition, the improvement of hardness in comparison to pure substrate material (AISI 316 LVM) was observed. Although the reduction of the level of hardness from the level of 10.8 GPa for pure DLC to about 9.4 GPa for the silicon doped coatings was observed, the concomitant improvement of films adhesion with higher amount of Si was revealed. Although incorporation of the dopant to DLC coatings increases the number of E. coli cells which adhered to the examined surfaces, the microbial colonisation remains on the level of substrate material. The presented results prove the potential of Si-DLC coatings in biomedical applications from the point of view of their mechanical properties.

  11. Study of the oxidation resistance of ZrxNand ZrxSi1-xN thin films deposited by reactive magnetron sputtering; Estudo da resistencia a oxidacao de filmes finos de ZrxN e ZrxSi1-xN depositados por magnetron sputtering reativo

    Energy Technology Data Exchange (ETDEWEB)

    Fernandez, D.R.; Freitas, F.G.R.; Felix, L.C.; Carvalho, R.G.; Fontes Junior, A.S.; Tentardini, E.K., E-mail: daniel.angel0275@gmail.com [Universidade Federal de Sergipe (UFS), Sao Cristovao, SE (Brazil). Departamento de Ciencia e Engenharia de Materiais; Silva Junior, H. da [Universidade Federal do Rio Grande do Sul (UFRGS), Porto Alegre, RS (Brazil)

    2016-07-01

    The objective of this work is to evaluate the oxidation resistance on pure zirconium nitride thin films and with silicon addition (ZrN and ZrSiN respectively). The thin films deposition were performed using reactive magnetron sputtering. The coatings were characterized by Rutherford Backscattering Spectroscopy (RBS), grazing angle X ray diffraction (GAXRD), scanning electronic microscopy (SEM-FEG) and oxidation tests starting from 500°C to 700°C. This study evaluated thin films with silicon content up to 14,9 at.%. GAXRD results showed only ZrN characteristics peaks, which allow the inference that Si3N4 has an amorphous structure. Oxidation tests demonstrate that the film with highest silicon content shows an increase of 200°C in oxidation temperature when compared with ZrN pure thin film. (author)

  12. Deposition of PZT thin film onto copper-coated polymer films by mean of pulsed-DC and RF-reactive sputtering

    Czech Academy of Sciences Publication Activity Database

    Suchaneck, G.; Labitzke, R.; Adolphi, B.; Jastrabík, Lubomír; Adámek, Petr; Drahokoupil, Jan; Hubička, Zdeněk; Kiselev, D.A.; Kholkin, A. L.; Gerlach, G.; Dejneka, Alexandr

    2011-01-01

    Roč. 205, č. 2 (2011), S241-S244 ISSN 0257-8972 R&D Projects: GA ČR GC202/09/J017; GA AV ČR KAN301370701; GA MŠk(CZ) 1M06002 Institutional research plan: CEZ:AV0Z10100522 Keywords : pulsed DC reactive sputtering * RF reactive sputtering * complex oxide film deposition * polymer substrate Subject RIV: BH - Optics, Masers, Lasers Impact factor: 1.867, year: 2011

  13. Microstructural Analysis of TiAl x N y O z Coatings Fabricated by DC Reactive Sputtering

    Science.gov (United States)

    García-González, L.; Hernández-Torres, J.; Flores-Ramírez, N.; Martínez-Castillo, J.; García-Ramírez, P. J.; Muñoz-Saldaña, J.; Espinoza-Beltrán, F. J.

    2009-02-01

    TiAl x N y O z coatings were prepared by DC reactive sputtering on AISI D2 tool steel substrates, using a target of Ti-Al-O fabricated from a mixture of powders of Ti (22.60 wt.%), Al (24.77 wt.%), and O (52.63 wt.%). The coatings were deposited on substrates at room temperature in a reactive atmosphere of nitrogen and argon under a pressure of 8.5 × 10-3 mbar. X-ray diffraction, electron dispersive spectroscopy, Raman scattering, and nanoindentation techniques were employed to investigate the coatings. The results show that the increment in the nitrogen flow affects the structure and the mechanical properties of the coatings. The sample with the lowest nitrogen flow presented the highest hardness (10.5 GPa) and the Young’s modulus (179.5 GPa). The hardness of the coatings TiAl x N y O z as a function of crystalline grain size shows a behavior consistent with the Hall-Petch relation.

  14. Effect of nitrogen doping on TiO.sub.x./sub.N.sub.y./sub. thin film formation at reactive high-power pulsed magnetron sputtering

    Czech Academy of Sciences Publication Activity Database

    Straňák, Vítězslav; Quaas, M.; Bogdanowicz, R.; Steffen, H.; Wulff, H.; Hubička, Zdeněk; Tichý, M.; Hippler, R.

    2010-01-01

    Roč. 43, č. 28 (2010), s. 1-7 ISSN 0022-3727 R&D Projects: GA AV ČR KAN301370701; GA MŠk(CZ) 1M06002 Grant - others:AVČR(CZ) M100100915 Institutional research plan: CEZ:AV0Z10100522 Keywords : magnetron sputtering * TiO 2 * pulse discharge * XRD * band gap Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 2.105, year: 2010 http://iopscience.iop.org/0022-3727/43/28/285203/

  15. Deposition of SiOx thin films on Y-TZP by reactive magnetron sputtering: influence of plasma parameters on the adhesion properties between Y-TZP and resin cement for application in dental prosthesis

    Directory of Open Access Journals (Sweden)

    José Renato Calvacanti de Queiroz

    2011-01-01

    Full Text Available In this paper SiOx thin films were deposited on Y-TZP ceramics by reactive magnetron sputtering technique in order to improve the adhesion properties between Y-TZP and resin cement for applications in dental prosthesis. For fixed cathode voltage, target current, working pressure and target-to-substrate distance, SiOx thin films were deposited at different oxygen concentrations in the Ar+O2 plasma forming gas. After deposition processes, SiOx thin films were characterized by profilometry, energy dispersive spectroscopy (EDS, optical microscopy and scanning electron microscopy (SEM. Adhesion properties between Y-TZP and resin cement were evaluated by shear testing. Results indicate that films deposited at 20%O2 increased the bond strength to (32.8 ± 5.4 MPa. This value has not been achieved by traditional methods.

  16. Influence of the electrical power applied to the target on the optical and structural properties of ZrON films produced via RF magnetron sputtering in a reactive atmosphere

    International Nuclear Information System (INIS)

    Pinzón, M.J.; Alfonso, J.E.; Olaya, J.J.; Cubillos, G.I.; Romero, E.

    2014-01-01

    The influence of the variation of electrical power applied to the target on the morphology and optical properties of zirconium oxynitride - zirconium oxide (ZrON) films deposited via RF magnetron sputtering on common glass substrates in a reactive atmosphere of N 2 /O 2 , with a flow ratio ΦN 2 /ΦO 2 of 1.25 was investigated. The crystallographic structure of the films was established through X-ray diffraction (XRD), the morphology was evaluated through scanning electron microscopy (SEM) and atomic force microscopy (AFM), and the optical behavior was evaluated through transmittance measurements. The XRD analysis showed that the films grew with mixed crystalline structures: monoclinic (ZrO 2 ) and body-centered cubic (Zr 2 ON 2 ). SEM analysis showed that the films grew with a homogeneous morphology, and AFM results established that as the electrical power applied to the target increased, there were changes in the grain size and the roughness of the films. The thickness, refractive index, and absorption coefficient of the films were calculated using the values of the transmittance through the Swanepoel method. Additionally, the energy band gap was determined via analysis of the free interference region. - Highlights: • We growth zirconium oxynitride films by RF magnetron sputtering in reactive atmosphere. • We determine the influence of the electrical power applied at the target in optical and structural properties. • We determine the crystallite size, grain size and roughness of the zirconium oxynitride films. • We determine the optical parameters such refractive index of the zirconium oxynitride films through Swanepoel method. • We calculated the absorption coefficient and optical band gap of the zirconium oxynitride films

  17. Influence of the electrical power applied to the target on the optical and structural properties of ZrON films produced via RF magnetron sputtering in a reactive atmosphere

    Energy Technology Data Exchange (ETDEWEB)

    Pinzón, M.J. [Grupo de Ciencia de Materiales y Superficies, Departamento de Física, Universidad Nacional de Colombia, AA 14490 Bogotá (Colombia); Alfonso, J.E., E-mail: jealfonsoo@unal.edu.co [Grupo de Ciencia de Materiales y Superficies, Departamento de Física, Universidad Nacional de Colombia, AA 14490 Bogotá (Colombia); Olaya, J.J. [Grupo de Ciencia de Materiales y Superficies, Departamento de Física, Universidad Nacional de Colombia, AA 14490 Bogotá (Colombia); Cubillos, G.I.; Romero, E. [Grupo de Materiales y Procesos Químicos, Universidad Nacional de Colombia, AA 14490 Bogotá (Colombia)

    2014-12-01

    The influence of the variation of electrical power applied to the target on the morphology and optical properties of zirconium oxynitride - zirconium oxide (ZrON) films deposited via RF magnetron sputtering on common glass substrates in a reactive atmosphere of N{sub 2}/O{sub 2}, with a flow ratio ΦN{sub 2}/ΦO{sub 2} of 1.25 was investigated. The crystallographic structure of the films was established through X-ray diffraction (XRD), the morphology was evaluated through scanning electron microscopy (SEM) and atomic force microscopy (AFM), and the optical behavior was evaluated through transmittance measurements. The XRD analysis showed that the films grew with mixed crystalline structures: monoclinic (ZrO{sub 2}) and body-centered cubic (Zr{sub 2}ON{sub 2}). SEM analysis showed that the films grew with a homogeneous morphology, and AFM results established that as the electrical power applied to the target increased, there were changes in the grain size and the roughness of the films. The thickness, refractive index, and absorption coefficient of the films were calculated using the values of the transmittance through the Swanepoel method. Additionally, the energy band gap was determined via analysis of the free interference region. - Highlights: • We growth zirconium oxynitride films by RF magnetron sputtering in reactive atmosphere. • We determine the influence of the electrical power applied at the target in optical and structural properties. • We determine the crystallite size, grain size and roughness of the zirconium oxynitride films. • We determine the optical parameters such refractive index of the zirconium oxynitride films through Swanepoel method. • We calculated the absorption coefficient and optical band gap of the zirconium oxynitride films.

  18. Studies on the reactive pulsed-magnetron sputtering of ITO from metallic targets; Untersuchungen zum reaktiven Pulsmagnetronsputtern von ITO von metallischen Targets

    Energy Technology Data Exchange (ETDEWEB)

    Gnehr, W.M.

    2006-06-15

    The thesis deals with a reactive sputter process for the deposition of ITO- films. In contrast to the usual technique, the sputter targets consists of indium-tin-alloy instead of ceramic ITO. All experiments were conducted on an inline coater with 600 mm target-width. The process is stabilized by a control loop based on optical emission detection. The experiments prove, that this control loop guarantees a long term stability of the outcomes of the coating process.Process parameters, that are crucial for the optical and electrical properties of the deposited thin films are identified and studied. Among them are the flow of oxygen and the substrate temperature but also less obvious parameters such as the distance between target and substrate.Througout the work the focus is on the film deposition with pulsed plasmas. Novel bipolar DC pulse- and pulse package generators are employed for the deposition.In order to shed some light onto the influence of certain pulse parameters on the outcome of a particular coating process, a Monte-Carlo-Simulation of the particle flow in pulsed plasmas is developed. This simulation yields the distribution of particles and their respective energies on deliberately placed planes in the process chamber. Particles under investigation are both sputtered species and neutral sputter gas atoms reflected at the target. The results of this simulation provide an explanation for the influence of certain pulse parameters on the outcome of the coating process. The further investigations deal with the influence of the construction of the process chamber on the coating process. For this purpose, locally resolved optical spectra are recorded. In order to analyse these spectra, a novel connected fit algorithm is developed.This algorithm yields the distribution of certain fitparameters on the substrate. Provided the most complex of the discussed parametrizations of the dielectric function are used, these can be crucial properties such as the carrier

  19. Structural, chemical and nanomechanical investigations of SiC/polymeric a-C:H films deposited by reactive RF unbalanced magnetron sputtering

    Science.gov (United States)

    Tomastik, C.; Lackner, J. M.; Pauschitz, A.; Roy, M.

    2016-03-01

    Amorphous carbon (or diamond-like carbon, DLC) films have shown a number of important properties usable for a wide range of applications for very thin coatings with low friction and good wear resistance. DLC films alloyed with (semi-)metals show some improved properties and can be deposited by various methods. Among those, the widely used magnetron sputtering of carbon targets is known to increase the number of defects in the films. Therefore, in this paper an alternative approach of depositing silicon-carbide-containing polymeric hydrogenated DLC films using unbalanced magnetron sputtering was investigated. The influence of the C2H2 precursor concentration in the deposition chamber on the chemical and structural properties of the deposited films was investigated by Raman spectroscopy, X-ray photoelectron spectroscopy and elastic recoil detection analysis. Roughness, mechanical properties and scratch response of the films were evaluated with the help of atomic force microscopy and nanoindentation. The Raman spectra revealed a strong correlation of the film structure with the C2H2 concentration during deposition. A higher C2H2 flow rate results in an increase in SiC content and decrease in hydrogen content in the film. This in turn increases hardness and elastic modulus and decreases the ratio H/E and H3/E2. The highest scratch resistance is exhibited by the film with the highest hardness, and the film having the highest overall sp3 bond content shows the highest elastic recovery during scratching.

  20. A comparison of reactive plasma pre-treatments on PET substrates by Cu and Ti pulsed-DC and HIPIMS discharges

    Energy Technology Data Exchange (ETDEWEB)

    Audronis, M., E-mail: m.audronis@yahoo.co.uk [Gencoa Ltd, Physics Road, Speke, Liverpool, L24 9HP (United Kingdom); Hinder, S.J. [The Surface Analysis Laboratory, Faculty of Engineering and Physical Sciences, University of Surrey, Guildford, GU2 7XH (United Kingdom); Mack, P. [ThermoFisher Scientific Ltd, Imberhorne Lane, East Grinstead, Sussex, RH19 1UB (United Kingdom); Bellido-Gonzalez, V. [Gencoa Ltd, Physics Road, Speke, Liverpool, L24 9HP (United Kingdom); Bussey, D.; Matthews, A. [Department of Engineering Materials, University of Sheffield, Sheffield S1 3JD (United Kingdom); Baker, M.A. [The Surface Analysis Laboratory, Faculty of Engineering and Physical Sciences, University of Surrey, Guildford, GU2 7XH (United Kingdom)

    2011-12-30

    PET web samples have been treated by magnetically enhanced glow discharges powered using either medium frequency pulse direct current (p-DC) or low frequency high power pulse (HIPIMS) sources. The plasma pre-treatment processes were carried out in an Ar-O{sub 2} atmosphere using either Cu or Ti sputter targets. XPS, AFM and sessile drop water contact angle measurements have been employed to examine changes in surface chemistry and morphology for different pre-treatment process parameters. Deposition of metal oxide onto the PET surface is observed as a result of the sputter magnetron-based glow discharge web treatment. Using the Cu target, both the p-DC and HIPIMS processes result in the formation of a thin CuO layer (with a thickness between 1 and 11 nm) being deposited onto the PET surface. Employing the Ti target, both p-DC and HIPIMS processes give rise to a much lower concentration of Ti (< 5 at.%), in the form of TiO{sub 2} on the PET treated surface. The TiO{sub 2} is probably distributed as an island-like distribution covering the PET surface. Presence of Cu and Ti oxide constituents on the treated PET is beneficial in aiding the adhesion but alone (i.e. without oxygen plasma activation) is not enough to provide very high levels of hydrophilicity as is clear from sessile drop water contact angle measurements on aged samples. Exposure to the plasma treatments leads to a small amount of roughening of the substrate surface, but the average surface roughness in all cases is below 2.5 nm. The PET structure at the interface with a coating is mostly or wholly preserved. The oxygen plasma treatment, metal oxide deposition and surface roughening resulting from the HIPIMS and p-DC treatments will promote adhesion to any subsequent thin film that is deposited immediately following the plasma treatment.

  1. Polarity inversion of AlN film grown on nitrided a-plane sapphire substrate with pulsed DC reactive sputtering

    Directory of Open Access Journals (Sweden)

    Marsetio Noorprajuda

    2018-04-01

    Full Text Available The effect of oxygen partial pressure (PO2 on polarity and crystalline quality of AlN films grown on nitrided a-plane sapphire substrates by pulsed direct current (DC reactive sputtering was investigated as a fundamental study. The polarity inversion of AlN from nitrogen (−c-polarity to aluminum (+c-polarity occurred during growth at a high PO2 of 9.4×103 Pa owing to Al-O octahedral formation at the interface of nitrided layer and AlN sputtered film which reset the polarity of AlN. The top part of the 1300 nm-thick AlN film sputtered at the high PO2 was polycrystallized. The crystalline quality was improved owing to the high kinetic energy of Al sputtered atom in the sputtering phenomena. Thinner AlN films were also fabricated at the high PO2 to eliminate the polycrystallization. For the 200 nm-thick AlN film sputtered at the high PO2, the full width at half-maximum values of the AlN (0002 and (10−12 X-ray diffraction rocking curves were 47 and 637 arcsec, respectively.

  2. On the control of deposition process for enhanced mechanical properties of nc-TiC/a-C: H coatings with DC magnetron sputtering at low or high ion flux

    Czech Academy of Sciences Publication Activity Database

    Souček, P.; Schmidtová, T.; Zábranský, L.; Buršíková, V.; Vašina, P.; Caha, O.; Buršík, Jiří; Peřina, Vratislav; Mikšová, Romana; Pei, Y.; de Hosson, J. T. M.

    Roč. 255, 25 September (2014), s. 8-14 ISSN 0257-8972 Institutional support: RVO:68081723 ; RVO:61389005 Keywords : enhanced mechanical properties * ion flux on the substrate * magnetron sputtering Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 1.998, year: 2014

  3. Surface treatment of diamond-like carbon films by reactive Ar/CF{sub 4} high-power pulsed magnetron sputtering plasmas

    Energy Technology Data Exchange (ETDEWEB)

    Kimura, Takashi, E-mail: t-kimura@nitech.ac.jp [Graduate School of Engineering, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, Nagoya 466-8555 (Japan); Nishimura, Ryotaro [Graduate School of Engineering, Nagoya Institute of Technology, Gokiso-cho, Showa-ku, Nagoya 466-8555 (Japan); Azuma, Kingo [Department of Electrical Engineering and Computer Sciences, University of Hyogo, 2167 Shosha, Himeji, Hyogo 671-2280 (Japan); Nakao, Setsuo; Sonoda, Tsutomu; Kusumori, Takeshi; Ozaki, Kimihiro [National Institute of Advanced Industrial Science and Technology (AIST) - Chubu, 2266-98 Anagahora, Moriyama, Nagoya 463-8560 (Japan)

    2015-12-15

    Surface modification of diamond-like carbon films deposited by a high-power pulsed magnetron sputtering (HPPMS) of Ar was carried out by a HPPMS of Ar/CF{sub 4} mixture, changing a CF{sub 4} fraction from 2.5% to 20%. The hardness of the modified films markedly decreased from about 13 to about 3.5 GPa with increasing CF{sub 4} fraction, whereas the water contact angle of the modified films increased from 68° to 109° owing to the increase in the CF{sub x} content on the film surface. C 1s spectra in X-ray photoelectron spectroscopy indicated that a graphitic structure of modified films was formed at CF{sub 4} fractions less than 5%, above which the modified films possessed a polymer-like structure. Influence of treatment time on the properties of the modified films was also investigated in the range of treatment time from 5 to 30 min. The properties of the modified films did not depend on the treatment time in the range of treatment time longer than 10 min, whereas the water contact angle was not sensitive to the treatment time at any treatment time.

  4. Crystallization of Sr0.5Ba0.5Nb2O6 Thin Films on LaNiO3 Electrodes by RF Magnetron Reactive Sputtering

    Science.gov (United States)

    Jong, Chao-An; Gan, Jon-Yiew

    2000-02-01

    Strontium barium niobium (Sr0.5Ba0.5Nb2O6) (SBN) thin films are prepared on conductive-oxide LNO (LaNiO3) electrodes by the rf magnetron sputtering system. Instead of conventional furnace annealing, SBN thin films are crystallized by rapid thermal annealing (RTA) above 700°C for 5 min. The textured SBN films are crystallized with two orientations: one is the (001) or (310) direction, and the other is the (002) or (620) direction. Films compositions measured by the electron spectroscopy of chemical analysis (ESCA) quantitative analysis method show nearly the same stoichiometric ratio as the target. The depth profiles of SBN films and the target are examined by secondary ion mass spectrometer (SIMS). The concentrations of the films are quite uniform. After being heat treated at 800°C for 5 min by RTA, La and Ni diffuse into the SBN film. The diffusion coefficient of La in SBN films is also calculated.

  5. Determination of the oxidation mechanism to Cd Te obtained by rf reactive magnetron sputtering in a plasma of Ar-N{sub 2}O; Determinacion del mecanismo de oxigenacion del CdTe obtenido por rf sputtering reactivo con magnetron en un plasma de Ar-N{sub 2}O

    Energy Technology Data Exchange (ETDEWEB)

    Caballero B, F.; Zapata N, A.; Bartolo P, P.; Castro R, R.; Zapata T, M.; Cauich, W.; Pena, J.L. [Departamento de Fisica Aplicada, Centro deInvestigacion y de Estudios Avanzados, Instituto Politecnico Nacional, Unidad Merida, Apartado postal 73, Cordemex, 97310 Merida, Yucatan (Mexico)

    1998-12-31

    In this work we did studies to determinate the oxidation site and incorporation mechanism of oxygen to Cd Te, when preparing Cd Te:O thin films by r f reactive magnetron sputtering, using a Cd Te target and a controlled plasma of Ar-N{sub 2}O. We study the influence in the oxygen content in films due to the variation of N{sub 2}O partial pressure, plasma power and substrate position. We monitored the process in situ by mass spectrometry to determinate the variation of present compounds when varying the N{sub 2}O partial pressure and plasma power. Thin films composition was determined by Auger electron spectroscopy and their structure by X-ray diffraction. We demonstrate that oxygen incorporation has place mainly in the substrate, forming an amorphous Cd Te:O film. We found that exists Cd Te oxidation without using nitrous oxide, may be due to residual atmosphere. We demonstrate that Cd Te oxidation depends on nitrous oxide partial pressure and plasma power. We found that deposition rate of Cd Te:O thin films depend on nitrous oxide interaction with Cd Te in the target and on the chamber walls. We propose a reaction mechanism to explain the oxygen incorporation to Cd Te. (Author)

  6. Preparation and comparison of a-C:H coatings using reactive sputter techniques

    Energy Technology Data Exchange (ETDEWEB)

    Keunecke, M., E-mail: martin.keunecke@ist.fraunhofer.d [Fraunhofer Institute for Surface Engineering and Thin Films (IST), Braunschweig (Germany); Weigel, K.; Bewilogua, K. [Fraunhofer Institute for Surface Engineering and Thin Films (IST), Braunschweig (Germany); Cremer, R.; Fuss, H.-G. [CemeCon AG, Wuerselen (Germany)

    2009-12-31

    Amorphous hydrogenated carbon (a-C:H) coatings are widely used in several industrial applications. These coatings commonly will be prepared by plasma activated chemical vapor deposition (PACVD). The main method used to prepare a-C:H coating in industrial scale is based on a glow discharge in a hydrocarbon gas like acetylene or methane using a substrate electrode powered with medium frequency (m.f. - some 10 to 300 kHz). Some aims of further development are adhesion improvement, increase of hardness and high coating quality on complex geometries. A relatively new and promising technique to fulfil these requirements is the deposition of a-C:H coatings by a reactive d.c. magnetron sputter deposition from a graphite target with acetylene as reactive gas. An advancement of this technique is the deposition in a pulsed magnetron sputter process. Using these three mentioned techniques a-C:H coatings were prepared in the same deposition machine. For adhesion improvement different interlayer systems were applied. The effect of different substrate bias voltages (d.c. and d.c. pulse) was investigated. By applying the magnetron sputter technique in the d.c. pulse mode, plastic hardness values up to 40 GPa could be reached. Besides hardness other mechanical properties like resistance against abrasive wear were measured and compared. Cross sectional SEM images showed the growth structure of the coatings.

  7. Reactive sputter deposition of boron nitride

    International Nuclear Information System (INIS)

    Jankowski, A.F.; Hayes, J.P.; McKernan, M.A.; Makowiecki, D.M.

    1995-10-01

    The preparation of fully dense, boron targets for use in planar magnetron sources has lead to the synthesis of Boron Nitride (BN) films by reactive rf sputtering. The deposition parameters of gas pressure, flow and composition are varied along with substrate temperature and applied bias. The films are characterized for composition using Auger electron spectroscopy, for chemical bonding using Raman spectroscopy and for crystalline structure using transmission electron microscopy. The deposition conditions are established which lead to the growth of crystalline BN phases. In particular, the growth of an adherent cubic BN coating requires 400--500 C substrate heating and an applied -300 V dc bias

  8. High-rate reactive deposition of transparent SiO.sub.2./sub. films containing low amount of Zr from molten magnetron target

    Czech Academy of Sciences Publication Activity Database

    Musil, Jindřich; Satava, V.; Baroch, P.

    2010-01-01

    Roč. 519, č. 2 (2010), s. 775-777 ISSN 0040-6090 Institutional research plan: CEZ:AV0Z10100520 Keywords : sputtering * evaporation * reactive deposition * target power density Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.909, year: 2010

  9. Measurement and modeling of plasma parameters in reactive high-power impulse magnetron sputtering of Ti in Ar/O.sub.2./sub. mixtures

    Czech Academy of Sciences Publication Activity Database

    Čada, Martin; Lundin, D.; Hubička, Zdeněk

    2017-01-01

    Roč. 121, č. 17 (2017), s. 1-7, č. článku 171913. ISSN 0021-8979 R&D Projects: GA ČR(CZ) GA15-00863S EU Projects: European Commission(XE) 608800 - HIPPOCAMP Institutional support: RVO:68378271 Keywords : reactive sputtering * HiPIMS * Langmuir probe * R-IRM model * plasma density * electron temperature Subject RIV: BL - Plasma and Gas Discharge Physics OBOR OECD: Fluids and plasma physics (including surface physics) Impact factor: 2.068, year: 2016

  10. Magnetron plasma and nanotechnology

    International Nuclear Information System (INIS)

    Kashtanov, Pavel V; Smirnov, Boris M; Hippler, Rainer

    2007-01-01

    Magnetron plasma processes involving metal atoms and clusters are reviewed. The formation of metal atoms near the cathode and their nucleation in a buffer gas flow are discussed. The flow of a buffer gas with metal clusters through a magnetron chamber disturbs the equilibrium between the buffer gas flow and clusters near the exit orifice and is accompanied by cluster attachment to the chamber walls. Cluster charging far off the cathode, the disturbance of equilibrium between the buffer gas flow and cluster drift, and the attachment of charged clusters to the chamber walls - the factors determining the output parameters of the cluster beam escaping the magnetron chamber - are analyzed. Cluster deposition on a solid surface and on dusty plasma particles is considered. (reviews of topical problems)

  11. Influence of deposition parameters on the optical and structural properties of TiO/sub 2/ films produced by reactive dc plasmatron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Schiller, S; Beister, G; Sieber, W; Schirmer, G; Hacker, E

    1981-09-11

    We investigated the variations in the structure and optical properties of TiO/sub 2/ films produced by reactive d.c. plasmatron sputtering with the most important deposition parameters. Over a wide range, the phase composition (ratio of rutile to anatase) and the grain size of the TiO/sub 2/ films can be influenced in a controlled manner by variations in the substrate temperature and the oxygen partial pressure. Because of their high refractive index and low light-scattering losses, plasmatron-sputtered TiO/sub 2/ films are of great interest in the field of optical interference coatings, e.g. for dielectric multilayer stacks.

  12. Reactive sputter deposition

    CERN Document Server

    Mahieu, Stijn

    2008-01-01

    In this valuable work, all aspects of the reactive magnetron sputtering process, from the discharge up to the resulting thin film growth, are described in detail, allowing the reader to understand the complete process. Hence, this book gives necessary information for those who want to start with reactive magnetron sputtering, understand and investigate the technique, control their sputtering process and tune their existing process, obtaining the desired thin films.

  13. Ionic conductivity and thermal stability of magnetron-sputtered nanocrystalline yttria-stabilized zirconia

    DEFF Research Database (Denmark)

    Sillassen, M.; Eklund, P.; Sridharan, M.

    2009-01-01

    Thermally stable, stoichiometric, cubic yttria-stabilized zirconia (YSZ) thin-film electrolytes have been synthesized by reactive pulsed dc magnetron sputtering from a Zr–Y (80/20 at. %) alloy target. Films deposited at floating potential had a texture. Single-line profile analysis of the 111 x.......5% at bias voltages of −175 and −200 V with additional incorporation of argon. The films were thermally stable; very limited grain coarsening was observed up to an annealing temperature of 800 °C. Temperature-dependent impedance spectroscopy analysis of the YSZ films with Ag electrodes showed that the in......-plane ionic conductivity was within one order of magnitude higher in films deposited with substrate bias corresponding to a decrease in grain size compared to films deposited at floating potential. This suggests that there is a significant contribution to the ionic conductivity from grain boundaries...

  14. Electrochemical behavior of single layer CrN, TiN, TiAlN coatings and nanolayered TiAlN/CrN multilayer coatings prepared by reactive direct current magnetron sputtering

    International Nuclear Information System (INIS)

    William Grips, V.K.; Barshilia, Harish C.; Selvi, V. Ezhil; Kalavati; Rajam, K.S.

    2006-01-01

    The corrosion behaviors of single layer TiN, CrN, TiAlN and multilayer TiAlN/CrN coatings, deposited on steel substrate using a multi-target reactive direct current magnetron sputtering process, were studied in 3.5% NaCl solution by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The total thickness of the coatings was about 1.5 μm. About 0.5 μm thick chromium interlayer was used for improved adhesion of the coatings. The potentiodynamic polarization measurements showed that for all the coatings the corrosion potential shifted to higher values as compared to the uncoated substrate. Similarly, the corrosion current density decreased for coated samples, indicating better corrosion resistance of the coated samples. The multilayer coatings of TiAlN/CrN exhibited superior corrosion behavior as compared to the single layer coatings. The Nyquist and the Bode plots obtained from the EIS measurements were fitted by appropriate equivalent circuits to calculate the pore resistance, the charge transfer resistance and the capacitance. These studies revealed that the pore resistance was lowest for TiN coatings, which increased for TiAlN coatings. TiAlN/CrN multilayer coatings exhibited highest pore resistance. No significant change in the capacitive behavior of the coatings was observed, suggesting minimal morphological changes as a result of immersion in the electrolyte. This could be attributed to shorter immersion durations. These studies were confirmed by examining the corroded samples under scanning electron microscope. Preliminary experiments conducted with additional interlayer of electroless nickel (5.0 μm thick) have shown significant improvement in the corrosion resistance of the coatings

  15. Magnetron injection gun scaling

    International Nuclear Information System (INIS)

    Lawson, W.

    1988-01-01

    Existing analytic design equations for magnetron injection guns (MIG's) are approximated to obtain a set of scaling laws. The constraints are chosen to examine the maximum peak power capabilities of MIG's. The scaling laws are compared with exact solutions of the design equations and are supported by MIG simulations

  16. Ring magnetron ionizer

    International Nuclear Information System (INIS)

    Alessi, J.G.

    1986-01-01

    A ring magnetron D - charge exchange ionizer has been built and tested. An H - current of 500 μA was extracted with an estimated H 0 density in the ionizer of 10 12 cm -3 . This exceeds the performance of ionizers presently in use on polarized H - sources. The ionizer will soon be tested with a polarized atomic beam

  17. High frequency pulse anodising of magnetron sputtered Al–Zr and Al–Ti Coatings

    DEFF Research Database (Denmark)

    Gudla, Visweswara Chakravarthy; Bordo, Kirill; Engberg, Sara

    2016-01-01

    High frequency pulse anodising of Al–Zr and Al–Ti coatings is studied as a surface finishing technique and compared to conventional decorative DC anodising. The Al–Zr and Al–Ti coatings were deposited using DC magnetron sputtering and were heat treated after deposition to generate a multiphase mi...

  18. Substrate heating and cooling during magnetron sputtering of copper target

    Energy Technology Data Exchange (ETDEWEB)

    Shapovalov, Viktor I.; Komlev, Andrey E.; Bondarenko, Anastasia S., E-mail: stopnastia@gmail.com; Baykov, Pavel B.; Karzin, Vitaliy V.

    2016-02-22

    Heating and cooling processes of the substrate during the DC magnetron sputtering of the copper target were investigated. The sensitive element of a thermocouple was used as a substrate. It was found, that the heat outflow rate from the substrate is lower when the magnetron is turned off rather than when it is turned on. Furthermore, the heating rate, the ultimate temperature, and the heat outflow rate related to the deposition of copper atoms are directly proportional to the discharge current density. - Highlights: • New effect of heat outflow from substrate when magnetron is on was discovered. • This new effect is linear in terms of heat outflow rate to target current ratio. • Kinetic equation for heating process additively considers this effect.

  19. Structure dependent resistivity and dielectric characteristics of tantalum oxynitride thin films produced by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Cristea, D., E-mail: daniel.cristea@unitbv.ro [Department of Materials Science, Transilvania University, 500036 Brasov (Romania); Crisan, A. [Department of Materials Science, Transilvania University, 500036 Brasov (Romania); Cretu, N. [Electrical Engineering and Applied Physics Department, Transilvania University, 500036 Brasov (Romania); Borges, J. [Centro de Física, Universidade do Minho, Campus de Gualtar, 4710 - 057 Braga (Portugal); Instituto Pedro Nunes, Laboratório de Ensaios, Desgaste e Materiais, Rua Pedro Nunes, 3030-199 Coimbra (Portugal); SEG-CEMUC, Mechanical Engineering Department, University of Coimbra, 3030-788 Coimbra (Portugal); Lopes, C.; Cunha, L. [Centro de Física, Universidade do Minho, Campus de Gualtar, 4710 - 057 Braga (Portugal); Ion, V.; Dinescu, M. [National Institute for Lasers, Plasma and Radiation Physics, Lasers Department, “Photonic Processing of Advanced Materials” Group, PO Box MG-16, RO 77125 Magurele-Bucharest (Romania); Barradas, N.P. [Centro de Ciências e Tecnologias Nucleares, Instituto Superior Técnico, Universidade de Lisboa, E.N. 10 ao km 139,7, 2695-066 Bobadela LRS (Portugal); Alves, E. [Instituto de Plasmas e Fusão Nuclear, Instituto Superior Técnico, Universidade de Lisboa, E.N. 10 ao km 139,7, 2695-066 Bobadela LRS (Portugal); Apreutesei, M. [MATEIS Laboratory-INSA de Lyon, 21 Avenue Jean Capelle, 69621 Villeurbanne cedex (France); Université de Lyon, Institut des Nanotechnologies de Lyon INL-UMR5270, CNRS, Ecole Centrale de Lyon, Ecully F-69134 (France); Munteanu, D. [Department of Materials Science, Transilvania University, 500036 Brasov (Romania)

    2015-11-01

    Highlights: • Tantalum oxynitride thin films have been deposited by magnetron sputtering, in various configurations. • The rising of the reactive gases mixture flow has the consequence of a gradual increase in the non-metallic content in the films, which results in a 10 orders of magnitude resistivity domain. • The higher resistivity films exhibit dielectric constants up to 41 and quality factors up to 70. - Abstract: The main purpose of this work is to present and to interpret the change of electrical properties of Ta{sub x}N{sub y}O{sub z} thin films, produced by DC reactive magnetron sputtering. Some parameters were varied during deposition: the flow of the reactive gases mixture (N{sub 2} and O{sub 2}, with a constant concentration ratio of 17:3); the substrate voltage bias (grounded, −50 V or −100 V) and the substrate (glass, (1 0 0) Si or high speed steel). The obtained films exhibit significant differences. The variation of the deposition parameters induces variations of the composition, microstructure and morphology. These differences cause variation of the electrical resistivity essentially correlated with the composition and structural changes. The gradual decrease of the Ta concentration in the films induces amorphization and causes a raise of the resistivity. The dielectric characteristics of some of the high resistance Ta{sub x}N{sub y}O{sub z} films were obtained in the samples with a capacitor-like design (deposited onto high speed steel, with gold pads deposited on the dielectric Ta{sub x}N{sub y}O{sub z} films). Some of these films exhibited dielectric constant values higher than those reported for other tantalum based dielectric films.

  20. Recent progress in thin film processing by magnetron sputtering with plasma diagnostics

    International Nuclear Information System (INIS)

    Han, Jeon G

    2009-01-01

    The precise control of the structure and related properties becomes crucial for sophisticated applications of thin films deposited by magnetron sputtering in emerging industries including the flat panel display, digital electronics and nano- and bio-industries. The film structure is closely related to the total energy delivered to the substrate surface for nucleation and growth during all kinds of thin film processes, including magnetron sputtering. Therefore, the energy delivered to the surface for nucleation and growth during magnetron sputtering should be measured and analysed by integrated diagnostics of the plasma parameters which are closely associated with the process parameters and other external process conditions. This paper reviews the background of thin film nucleation and growth, the status of magnetron sputtering technology and the progress of plasma diagnostics for plasma processing. The evolution of the microstructure during magnetron sputtering is then discussed with respect to the change in the process variables in terms of the plasma parameters along with empirical data of the integrated plasma diagnostics for various magnetron sputtering conditions with conventional dc, pulsed dc and high power pulsed dc sputtering modes. Among the major energy terms to be discussed are the temperature change in the top surface region and the energies of ions and neutral species. (topical review)

  1. Effect of plasma immersion on crystallinity of V2O5 film grown by dc reactive sputtering at room temperature

    International Nuclear Information System (INIS)

    Choi, Sun Hee; Kim, Joosun; Yoon, Young Soo

    2005-01-01

    Vanadium oxide thin films were grown at room temperature by direct current reactive sputtering. To investigate the effect of plasma immersion on the crystallinity of as-grown film, we immersed samples in plasma during the deposition process. X-ray diffraction (XRD) measurements show that as-deposited thin films immersed in plasma are crystalline, whereas those not immersed in the plasma are amorphous. Images taken with scanning electron microscopy show that the surface of films exposed to plasma have a different morphology to the surface of films not exposed to plasma. The Li-intercalation feature of as-deposited films immersed in plasma shows the typical behavior of crystalline vanadium oxide; such behavior is unsuitable for the cathode of thin film batteries (TFBs). These results indicate that direct current plasma promotes the growth of crystalline vanadium oxide films

  2. Effect of substrate type on the electrical and structural properties of TiO2 thin films deposited by reactive DC sputtering

    Science.gov (United States)

    Cheng, Xuemei; Gotoh, Kazuhiro; Nakagawa, Yoshihiko; Usami, Noritaka

    2018-06-01

    Electrical and structural properties of TiO2 thin films deposited at room temperature by reactive DC sputtering have been investigated on three different substrates: high resistivity (>1000 Ω cm) float zone Si(1 1 1), float zone Si(1 0 0) and alkali free glass. As-deposited TiO2 films on glass substrate showed extremely high resistivity of (∼5.5 × 103 Ω cm). In contrast, lower resistivities of ∼2 Ω cm and ∼5 Ω cm were obtained for films on Si(1 1 1) and Si(1 0 0), respectively. The as-deposited films were found to be oxygen-rich amorphous TiO2 for all the substrates as evidenced by X-ray photoemission spectroscopy and X-ray diffraction. Subsequent annealing led to appearance of anatase TiO2 on Si but not on glass. The surface of as-deposited TiO2 on Si was found to be rougher than that on glass. These results suggest that the big difference of electrical resistivity of TiO2 would be related with existence of more anatase nuclei forming on crystalline substrates, which is consistent with the theory of charged clusters that smaller clusters tend to adopt the substrate structure.

  3. Research and Development for an Alternative RF Source Using Magnetrons in CEBAF

    Science.gov (United States)

    Jacobs, Andrew

    2016-09-01

    At Jefferson Lab, klystrons are currently used as a radiofrequency (RF) power source for the 1497 MHz Continuous Electron Beam Accelerator Facility (CEBAF) Continuous Wave (CW) system. A drop-in replacement for the klystrons in the form of a system of magnetrons is being developed. The klystron DC-RF efficiency at CEBAF is 35-51% while the estimated magnetron efficiency is 80-90%. Thus, the introduction of magnetrons to CEBAF will have enormous benefits in terms of electrical power saving. The primary focus of this project was to characterize a magnetron's frequency pushing and pulling curves at 2.45 GHz with stub tuner and anode current adjustments so that a Low Level RF controller for a new 1.497 GHz magnetron can be built. A Virtual Instrument was created in LabVIEW, and data was taken. The resulting data allowed for the creation of many constant lines of frequency and output power. Additionally, the results provided a characterization of magnetron oven temperature drift over the operation time and the relationship between anode current and frequency. Using these results, the control model of different variables and their feedback or feedforward that affect the frequency pushing and pulling of the magnetron is better developed. Department of Energy, Science Undergraduate Laboratory Internships, and Jefferson Lab.

  4. Influence of stress on the structural and dielectric properties of rf magnetron sputtered zinc oxide thin film

    Science.gov (United States)

    Menon, Rashmi; Sreenivas, K.; Gupta, Vinay

    2008-05-01

    Highly c axis oriented zinc oxide (ZnO) thin films have been prepared on 1737 Corning glass substrate by planar rf magnetron sputtering under varying pressure (10-50mTorr) and different oxygen percentage (40%-100%) in reactive gas mixtures. The as-grown ZnO thin films were found to have stress over a wide range from -6×1010to-9×107dynes/cm2. The presence of stress depends strongly on processing conditions, and films become almost stress free under a unique combination of sputtering pressure and reactive gas composition. The studies show a correlation of stress with structural and electrical properties of the ZnO thin film. The stressed films possess high electrical conductivity and exhibits strong dielectric dispersion over a wide frequency (1kHz-1MHz). The dielectric constant ɛ'(ω) of stress free ZnO film was almost frequency independent and was close to the bulk value. The measured value of dc conductivity, σdc(ω) and ac conductivity σac(ω) of stress free ZnO film was 1.3×10-9 and 6.8×10-5Ω-1cm-1, respectively. The observed variation in the structural and electrical properties of ZnO thin film with stress has been analyzed in the light of growth kinetics.

  5. Advanced DC/DC converters

    CERN Document Server

    Luo, Fang Lin

    2003-01-01

    DC/DC conversion techniques have undergone rapid development in recent decades. With the pioneering work of these authors, DC/DC converters have now moved into their sixth generation. This book offers a concise, practical presentation of DC/DC converters, summarizing the spectrum of conversion tecnologies and presentingmany new ideas and more than 100 new topologies. Nowhere else in the literature are DC/DC converters so logically sorted and systematically introduced, and nowhere else can readers find detailed information on prototype topologies that represent a major contribution to modern power engineering. More than 320 figures, 60 tables, and 500 formulae facilitate understand and provide precise data.

  6. Study of static properties of magnetron-type space charges

    International Nuclear Information System (INIS)

    Delcroix, Jean-Loup

    1953-01-01

    This research thesis reports an in-depth analysis of physical properties of static regimes to address the issue of space charges. This theoretical study of the Hull magnetron is followed by the description of experiments on the Hull magnetron which highlight transitions between the different regimes. Then, another theoretical approach aims at generalising the magnetron theory, based on other types of magnetron theory (general equations of magnetron-type space charges, inverted Hull magnetron theory, circular field magnetron theory)

  7. dc Arc Fault Effect on Hybrid ac/dc Microgrid

    Science.gov (United States)

    Fatima, Zahra

    The advent of distributed energy resources (DER) and reliability and stability problems of the conventional grid system has given rise to the wide spread deployment of microgrids. Microgrids provide many advantages by incorporating renewable energy sources and increasing the reliability of the grid by isolating from the main grid in case of an outage. AC microgrids have been installed all over the world, but dc microgrids have been gaining interest due to the advantages they provide over ac microgrids. However the entire power network backbone is still ac and dc microgrids require expensive converters to connect to the ac power network. As a result hybrid ac/dc microgrids are gaining more attention as it combines the advantages of both ac and dc microgrids such as direct integration of ac and dc systems with minimum number of conversions which increases the efficiency by reducing energy losses. Although dc electric systems offer many advantages such as no synchronization and no reactive power, successful implementation of dc systems requires appropriate protection strategies. One unique protection challenge brought by the dc systems is dc arc faults. A dc arc fault is generated when there is a gap in the conductor due to insulation degradation and current is used to bridge the gap, resulting in an arc with very high temperature. Such a fault if it goes undetected and is not extinguished can cause damage to the entire system and cause fires. The purpose of the research is to study the effect of the dc arc fault at different locations in the hybrid ac/dc microgrid and provide insight on the reliability of the grid components when it is impacted by arc faults at various locations in the grid. The impact of dc arc fault at different locations on the performance of the PV array, wind generation, and constant power loads (CPL) interfaced with dc/dc converters is studied. MATLAB/Simulink is used to model the hybrid ac/dc microgrid and arc fault.

  8. Experimental study on an S-band near-field microwave magnetron power transmission system on hundred-watt level

    Science.gov (United States)

    Zhang, Biao; Jiang, Wan; Yang, Yang; Yu, Chengyang; Huang, Kama; Liu, Changjun

    2015-11-01

    A multi-magnetron microwave source, a metamaterial transmitting antenna, and a large power rectenna array are presented to build a near-field 2.45 GHz microwave power transmission system. The square 1 m2 rectenna array consists of sixteen rectennas with 2048 Schottky diodes for large power microwave rectifying. It receives microwave power and converts them into DC power. The design, structure, and measured performance of a unit rectenna as well as the entail rectenna array are presented in detail. The multi-magnetron microwave power source switches between half and full output power levels, i.e. the half-wave and full-wave modes. The transmission antenna is formed by a double-layer metallic hole array, which is applied to combine the output power of each magnetron. The rectenna array DC output power reaches 67.3 W on a 1.2 Ω DC load at a distance of 5.5 m from the transmission antenna. DC output power is affected by the distance, DC load, and the mode of microwave power source. It shows that conventional low power Schottky diodes can be applied to a microwave power transmission system with simple magnetrons to realise large power microwave rectifying.

  9. TOPICAL REVIEW: Physics and phenomena in pulsed magnetrons: an overview

    Science.gov (United States)

    Bradley, J. W.; Welzel, T.

    2009-05-01

    This paper reviews the contribution made to the observation and understanding of the basic physical processes occurring in an important type of magnetized low-pressure plasma discharge, the pulsed magnetron. In industry, these plasma sources are operated typically in reactive mode where a cathode is sputtered in the presence of both chemically reactive and noble gases typically with the power modulated in the mid-frequency (5-350 kHz) range. In this review, we concentrate mostly, however, on physics-based studies carried out on magnetron systems operated in argon. This simplifies the physical-chemical processes occurring and makes interpretation of the observations somewhat easier. Since their first recorded use in 1993 there have been more than 300 peer-reviewed paper publications concerned with pulsed magnetrons, dealing wholly or in part with fundamental observations and basic studies. The fundamentals of these plasmas and the relationship between the plasma parameters and thin film quality regularly have whole sessions at international conferences devoted to them; however, since many different types of magnetron geometries have been used worldwide with different operating parameters the important results are often difficult to tease out. For example, we find the detailed observations of the plasma parameter (particle density and temperature) evolution from experiment to experiment are at best difficult to compare and at worst contradictory. We review in turn five major areas of studies which are addressed in the literature and try to draw out the major results. These areas are: fast electron generation, bulk plasma heating, short and long-term plasma parameter rise and decay rates, plasma potential modulation and transient phenomena. The influence of these phenomena on the ion energy and ion energy flux at the substrate is discussed. This review, although not exhaustive, will serve as a useful guide for more in-depth investigations using the referenced

  10. Physics and phenomena in pulsed magnetrons: an overview

    International Nuclear Information System (INIS)

    Bradley, J W; Welzel, T

    2009-01-01

    This paper reviews the contribution made to the observation and understanding of the basic physical processes occurring in an important type of magnetized low-pressure plasma discharge, the pulsed magnetron. In industry, these plasma sources are operated typically in reactive mode where a cathode is sputtered in the presence of both chemically reactive and noble gases typically with the power modulated in the mid-frequency (5-350 kHz) range. In this review, we concentrate mostly, however, on physics-based studies carried out on magnetron systems operated in argon. This simplifies the physical-chemical processes occurring and makes interpretation of the observations somewhat easier. Since their first recorded use in 1993 there have been more than 300 peer-reviewed paper publications concerned with pulsed magnetrons, dealing wholly or in part with fundamental observations and basic studies. The fundamentals of these plasmas and the relationship between the plasma parameters and thin film quality regularly have whole sessions at international conferences devoted to them; however, since many different types of magnetron geometries have been used worldwide with different operating parameters the important results are often difficult to tease out. For example, we find the detailed observations of the plasma parameter (particle density and temperature) evolution from experiment to experiment are at best difficult to compare and at worst contradictory. We review in turn five major areas of studies which are addressed in the literature and try to draw out the major results. These areas are: fast electron generation, bulk plasma heating, short and long-term plasma parameter rise and decay rates, plasma potential modulation and transient phenomena. The influence of these phenomena on the ion energy and ion energy flux at the substrate is discussed. This review, although not exhaustive, will serve as a useful guide for more in-depth investigations using the referenced

  11. Comparative study of nanocomposites prepared by pulsed and dc sputtering combined with plasma polymerization suitable for photovoltaic device applications

    Energy Technology Data Exchange (ETDEWEB)

    Hussain, Amreen A. [Physical Sciences Division, Institute of Advanced Study in Science and Technology, Guwahati, Assam (India); Pal, Arup R., E-mail: arpal@iasst.gov.in [Physical Sciences Division, Institute of Advanced Study in Science and Technology, Guwahati, Assam (India); Kar, Rajib [Laser and Plasma Technology Division, Bhabha Atomic Research Center, Trombay, Mumbai (India); Bailung, Heremba; Chutia, Joyanti [Physical Sciences Division, Institute of Advanced Study in Science and Technology, Guwahati, Assam (India); Patil, Dinkar S. [Laser and Plasma Technology Division, Bhabha Atomic Research Center, Trombay, Mumbai (India)

    2014-12-15

    Plasma processing, a single step method for production of large area composite films, is employed to deposit plasma polymerized aniline-Titanium dioxide (PPani-TiO{sub 2}) nanocomposite thin films. The deposition of PPani-TiO{sub 2} nanocomposite films are made using reactive magnetron sputtering and plasma polymerization combined process. This study focuses on the direct comparison between continuous and pulsed dc magnetron sputtering techniques of titanium in combination with rf plasma polymerization of aniline. The deposited PPani-TiO{sub 2} nanocomposite films are characterized and discussed in terms of structural, morphological and optical properties. A self powered hybrid photodetector has been developed by plasma based process. The proposed method provides a new route where the self-assembly of molecules, that is, the spontaneous association of atomic or molecular building blocks under plasma environment, emerge as a successful strategy to form well-defined structural and morphological units of nanometer dimensions. - Highlights: • PPani-TiO{sub 2} nanocomposite by pulsed and dc sputtering with rf plasma polymerization. • In-situ and Ex-situ H{sub 2}SO{sub 4} doping in PPani-TiO{sub 2} nanocomposite. • PPani-TiO{sub 2} nanocomposite based self-powered-hybrid photodetector.

  12. Comparative study of nanocomposites prepared by pulsed and dc sputtering combined with plasma polymerization suitable for photovoltaic device applications

    International Nuclear Information System (INIS)

    Hussain, Amreen A.; Pal, Arup R.; Kar, Rajib; Bailung, Heremba; Chutia, Joyanti; Patil, Dinkar S.

    2014-01-01

    Plasma processing, a single step method for production of large area composite films, is employed to deposit plasma polymerized aniline-Titanium dioxide (PPani-TiO 2 ) nanocomposite thin films. The deposition of PPani-TiO 2 nanocomposite films are made using reactive magnetron sputtering and plasma polymerization combined process. This study focuses on the direct comparison between continuous and pulsed dc magnetron sputtering techniques of titanium in combination with rf plasma polymerization of aniline. The deposited PPani-TiO 2 nanocomposite films are characterized and discussed in terms of structural, morphological and optical properties. A self powered hybrid photodetector has been developed by plasma based process. The proposed method provides a new route where the self-assembly of molecules, that is, the spontaneous association of atomic or molecular building blocks under plasma environment, emerge as a successful strategy to form well-defined structural and morphological units of nanometer dimensions. - Highlights: • PPani-TiO 2 nanocomposite by pulsed and dc sputtering with rf plasma polymerization. • In-situ and Ex-situ H 2 SO 4 doping in PPani-TiO 2 nanocomposite. • PPani-TiO 2 nanocomposite based self-powered-hybrid photodetector

  13. Amorphous ITO thin films prepared by DC sputtering for electrochromic applications

    International Nuclear Information System (INIS)

    Teixeira, V.; Cui, H.N.; Meng, L.J.; Fortunato, E.; Martins, R.

    2002-01-01

    Indium-Tin-Oxide (ITO) thin films were deposited on glass substrates using DC magnetron reactive sputtering at different bias voltages and substrate temperatures. Some improvements were obtained on film properties, microstructure and other physical characteristics for different conditions. Amorphous and polycrystalline films can be obtained for various deposition conditions. The transmission, absorption, spectral and diffuse reflection of ITO films were measured in some ranges of UV-Vis-NIR. The refractive index (n), Energy band gap E g and the surface roughness of the film were derived from the measured spectra data. The carrier density (n c ) and the carrier mobility (μ) of the film micro conductive properties were discussed. The films exhibited suitable optical transmittance and conductivity for electrochromic applications

  14. Peripheral Blood CD4 T-Cell and Plasmacytoid Dendritic Cell (pDC) Reactivity to Herpes Simplex Virus 2 and pDC Number Do Not Correlate with the Clinical or Virologic Severity of Recurrent Genital Herpes

    Science.gov (United States)

    Moss, Nicholas J.; Magaret, Amalia; Laing, Kerry J.; Kask, Angela Shaulov; Wang, Minna; Mark, Karen E.; Schiffer, Joshua T.; Wald, Anna

    2012-01-01

    Leukocytes participate in the immune control of herpes simplex virus (HSV). Data from HIV coinfections, germ line mutations, and case reports suggest involvement of CD4 T cells and plasmacytoid dendritic cells (pDC). We investigated the relationships between these cells and recurrent genital herpes disease severity in the general population. Circulating CD4 T-cell responses to HSV-2 were measured in specimens from 67 immunocompetent individuals with measured genital lesion and HSV shedding rates. Similarly, pDC number and functional responses to HSV-2 were analyzed in 40 persons. CD4 responses and pDC concentrations and responses ranged as much as 100-fold between persons while displaying moderate within-person consistency over time. No correlations were observed between these immune response parameters and genital HSV-2 severity. Cytomegalovirus (CMV) coinfection was not correlated with differences in HSV-2-specific CD4 T-cell responses. The CD4 T-cell response to HSV-2 was much more polyfunctional than was the response to CMV. These data suggest that other immune cell subsets with alternate phenotypes or anatomical locations may be responsible for genital herpes control in chronically infected individuals. PMID:22761381

  15. See Also:physica status solidi (b)physica status solidi (c)Copyright © 2004 WILEY-VCH Verlag GmbH & Co. KGaA, WeinheimGet Sample CopyFree Online Trial -->Recommend to Your LibrarianSave Title to My ProfileSet E-Mail Alert var homepagelinks = new Array(new Array("Journal Home","/cgi-bin/jhome/40000761",""),new Array("Issues","/cgi-bin/jtoc/40000761/",""),new Array("Early View","/cgi-bin/jeview/40000761/",""),new Array("News","/cgi-bin/jabout/40000761/news/index.html",""),new Array("Reviews","/cgi-bin/jabout/40000761/reviews.html",""),new Array("Read Cover Story","/cgi-bin/jabout/40000761/cover/2231/current.html","e"),new Array("","","s"),new Array("Product Information","/cgi-bin/jabout/40000761/2231_info.html",""),new Array("Editorial Board","/cgi-bin/jabout/40000761/edbd.html",""),new Array("For Authors","/cgi-bin/jabout/40000761/authors.html",""),new Array("For Referees","/cgi-bin/jabout/40000761/refserv.html",""),new Array("Subscribe","http://jws-edcv.wiley.com/jcatalog/JournalsCatalogOrder/JournalOrder?PRINT_ISSN=0031-8965",""),new Array("Contact","/cgi-bin/jabout/40000761/contact.html",""),new Array("Online Submission","http://www.manuscriptxpress.org/osm/",""),new Array("","","x"));writeJournalLinks("", "40000761");issue nav --> Previous Issue | Next Issue >issue nav -->Volume 201, Issue14 (November 2004)Articles in the Current Issue:Rapid Research NoteHighly (001)-textured WS2-x films prepared by reactive radio frequency magnetron sputtering

    Science.gov (United States)

    Ellmer, K.; Mientus, R.; Seeger, S.; Weiß, V.

    2004-11-01

    Highly (001)-oriented WS2-x films were grown onto oxidized silicon substrates by reactive magnetron sputtering from a metallic tungsten target in argon-hydrogen sulfide mixtures. The best films with respect to the van-der-Waals orientation, i.e. with the (001) planes parallel to the substrate surface, were grown by excitation of the plasma with radio frequency of 27.12 MHz. These films exhibit the largest grains and the lowest film strain. It is shown that this effect is not due to the lower deposition rate at this high excitation frequency. Instead it was found that the lower DC voltage at the sputtering target is advantageous for the film growth since the bombardment of the growing film by highly energetic particles is avoided by this type of plasma excitation.

  16. Magnetron sputtered gadolinia-doped ceria diffusion barriers for metal-supported solid oxide fuel cells

    DEFF Research Database (Denmark)

    Sønderby, Steffen; Klemensø, Trine; Christensen, Bjarke H.

    2014-01-01

    Gadolinia-doped ceria (GDC) thin films are deposited by reactive magnetron sputtering in an industrial-scale setup and implemented as barrier layers between the cathode and electrolyte in metal-based solid oxide fuel cells consisting of a metal support, an electrolyte of ZrO2 co-doped with Sc2O3...

  17. Milliwatt dc/dc Inverter

    Science.gov (United States)

    Mclyman, C. W.

    1983-01-01

    Compact dc/dc inverter uses single integrated-circuit package containing six inverter gates that generate and amplify 100-kHz square-wave switching signal. Square-wave switching inverts 10-volt local power to isolated voltage at another desired level. Relatively high operating frequency reduces size of filter capacitors required, resulting in small package unit.

  18. Domino Platform: PVD Coaters for Arc Evaporation and High Current Pulsed Magnetron Sputtering

    International Nuclear Information System (INIS)

    Vetter, J; Müller, J; Erkens, G

    2012-01-01

    AlTiN and CrN coatings were deposited in hybrid DOMINO platforms by magnetron sputtering (DC-MS, DC-MS+HCP-MS, HCP-MS) and vacuum arc evaporation. The ion cleaning was done by the AEGD process. The coating rates and the energy efficiency of both deposition processes were compared. The roughness effects of the different coating types were discussed. Preliminary results of the change of pulse characteristics during simultaneously running of HCP-MS plus vacuum arc evaporation are shown.

  19. Setup for in situ X-ray diffraction studies of thin film growth by magnetron sputtering

    CERN Document Server

    Ellmer, K; Weiss, V; Rossner, H

    2001-01-01

    A novel method is described for the in situ-investigation of nucleation and growth of thin films during magnetron sputtering. Energy dispersive X-ray diffraction with synchrotron light is used for the structural analysis during film growth. An in situ-magnetron sputtering chamber was constructed and installed at a synchrotron radiation beam line with a bending magnet. The white synchrotron light (1-70 keV) passes the sputtering chamber through Kapton windows and hits one of the substrates on a four-fold sample holder. The diffracted beam, observed under a fixed diffraction angle between 3 deg. and 10 deg., is energy analyzed by a high purity Ge-detector. The in situ-EDXRD setup is demonstrated for the growth of tin-doped indium oxide (ITO) films prepared by reactive magnetron sputtering from a metallic target.

  20. The Pulsed Cylindrical Magnetron for Deposition

    Science.gov (United States)

    Korenev, Sergey

    2012-10-01

    The magnetron sputtering deposition of films and coatings broadly uses in microelectronics, material science, environmental applications and etc. The rate of target evaporation and time for deposition of films and coatings depends on magnetic field. These parameters link with efficiency of gas molecules ionization by electrons. The cylindrical magnetrons use for deposition of films and coatings on inside of pipes for different protective films and coatings in oil, chemical, environmental applications. The classical forming of magnetic field by permanent magnets or coils for big and long cylindrical magnetrons is complicated. The new concept of pulsed cylindrical magnetron for high rate deposition of films and coating for big and long pipes is presented in this paper. The proposed cylindrical magnetron has azimuthally pulsed high magnetic field, which allows forming the high ionized plasma and receiving high rate of evaporation material of target (central electrode). The structure of proposed pulsed cylindrical magnetron sputtering system is given. The main requirements to deposition system are presented. The preliminary data for forming of plasma and deposition of Ta films and coatings on the metal pipers are discussed. The comparison of classical and proposed cylindrical magnetrons is given. The analysis of potential applications is considered.

  1. Negative Ion Sources: Magnetron and Penning

    International Nuclear Information System (INIS)

    Faircloth, D C

    2013-01-01

    The history of the magnetron and Penning electrode geometry is briefly outlined. Plasma generation by electrical discharge-driven electron impact ionization is described and the basic physics of plasma and electrodes relevant to magnetron and Penning discharges are explained. Negative ions and their applications are introduced, along with their production mechanisms. Caesium and surface production of negative ions are detailed. Technical details of how to build magnetron and Penning surface plasma sources are given, along with examples of specific sources from around the world. Failure modes are listed and lifetimes compared. (author)

  2. Negative Ion Sources: Magnetron and Penning

    CERN Document Server

    Faircloth, D.C.

    2013-12-16

    The history of the magnetron and Penning electrode geometry is briefly outlined. Plasma generation by electrical discharge-driven electron impact ionization is described and the basic physics of plasma and electrodes relevant to magnetron and Penning discharges are explained. Negative ions and their applications are introduced, along with their production mechanisms. Caesium and surface production of negative ions are detailed. Technical details of how to build magnetron and Penning surface plasma sources are given, along with examples of specific sources from around the world. Failure modes are listed and lifetimes compared.

  3. Effect of negative bias on the composition and structure of the tungsten oxide thin films deposited by magnetron sputtering

    Science.gov (United States)

    Wang, Meihan; Lei, Hao; Wen, Jiaxing; Long, Haibo; Sawada, Yutaka; Hoshi, Yoichi; Uchida, Takayuki; Hou, Zhaoxia

    2015-12-01

    Tungsten oxide thin films were deposited at room temperature under different negative bias voltages (Vb, 0 to -500 V) by DC reactive magnetron sputtering, and then the as-deposited films were annealed at 500 °C in air atmosphere. The crystal structure, surface morphology, chemical composition and transmittance of the tungsten oxide thin films were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), X-ray photoelectron spectroscopy (XPS) and UV-vis spectrophotometer. The XRD analysis reveals that the tungsten oxide films deposited at different negative bias voltages present a partly crystallized amorphous structure. All the films transfer from amorphous to crystalline (monoclinic + hexagonal) after annealing 3 h at 500 °C. Furthermore, the crystallized tungsten oxide films show different preferred orientation. The morphology of the tungsten oxide films deposited at different negative bias voltages is consisted of fine nanoscale grains. The grains grow up and conjunct with each other after annealing. The tungsten oxide films deposited at higher negative bias voltages after annealing show non-uniform special morphology. Substoichiometric tungsten oxide films were formed as evidenced by XPS spectra of W4f and O1s. As a result, semi-transparent films were obtained in the visible range for all films deposited at different negative bias voltages.

  4. Characterisation of magnetron sputtered SmCo5 thin films

    International Nuclear Information System (INIS)

    Wang, Y.; Sood, D.K.; Kothari

    1999-01-01

    SmCo 5 thin films were deposited using DC magnetron sputtering on single crystal silicon substrate with chromium and SiO 2 top layers. Deposition was carried out at three different substrate temperatures: room temperature, 400 deg C and 600 deg C. Films were characterised by using Rutherford Backscattering Spectroscopy (RBS), X-ray Diffraction (XRD), Secondary Ion Mass Spectrometry (SIMS) and SQUID magnetometer. RBS analysis indicated that the films have excellent stoichiometry with the Sm to Co ratio of 1:5. This analysis also showed that the films deposited or annealed at high temperatures (≥600 deg C) indicated significant inter-diffusion at the interface between the barrier layer and the film. Oxygen was found to be the major impurity in the films. XRD data indicated that the films formed 1:5 and 2:17 phases under different deposition conditions. The preliminary studies of these films using magnetic force microscopy revealed the presence of magnetic domains

  5. A Plasma Lens for Magnetron Sputtering

    International Nuclear Information System (INIS)

    Anders, Andre; Brown, Jeff

    2010-01-01

    A plasma lens, consisting of a solenoid and potential-defining ring electrodes, has been placed between a magnetron and substrates to be coated. Photography reveals qualitative information on excitation, ionization, and the transport of plasma to the substrate.

  6. High rate deposition of thin film cadmium sulphide by pulsed direct current magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Lisco, F., E-mail: F.Lisco@lboro.ac.uk [Centre for Renewable Energy Systems Technology (CREST), School of Electronic, Electrical and Systems Engineering, Loughborough University, Leicestershire LE11 3TU (United Kingdom); Kaminski, P.M.; Abbas, A.; Bowers, J.W.; Claudio, G. [Centre for Renewable Energy Systems Technology (CREST), School of Electronic, Electrical and Systems Engineering, Loughborough University, Leicestershire LE11 3TU (United Kingdom); Losurdo, M. [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR, via Orabona 4, 70126 Bari (Italy); Walls, J.M. [Centre for Renewable Energy Systems Technology (CREST), School of Electronic, Electrical and Systems Engineering, Loughborough University, Leicestershire LE11 3TU (United Kingdom)

    2015-01-01

    Cadmium Sulphide (CdS) is an important n-type semiconductor widely used as a window layer in thin film photovoltaics Copper Indium Selenide, Copper Indium Gallium (di)Selenide, Copper Zinc Tin Sulphide and Cadmium Telluride (CdTe). Cadmium Sulphide has been deposited using a number of techniques but these techniques can be slow (chemical bath deposition and Radio Frequency sputtering) or the uniformity and the control of thickness can be relatively difficult (close space sublimation). In this paper we report on the development of a process using pulsed Direct Current magnetron sputtering which allows nanometre control of thin film thickness using time only. The CdS thin films deposited in this process are highly uniform and smooth. They exhibit the preferred hexagonal structure at room temperature deposition and they have excellent optical properties. Importantly, the process is highly stable despite the use of a semi-insulating magnetron target. Moreover, the process is very fast. The deposition rate using 1.5 kW of power to a 6-inch circular magnetron was measured to be greater than 8 nm/s. This makes the process suitable for industrial deployment. - Highlights: • Pulsed DC magnetron sputtering of CdS • High deposition rate deposition • Uniform, pinhole free films.

  7. High rate deposition of thin film cadmium sulphide by pulsed direct current magnetron sputtering

    International Nuclear Information System (INIS)

    Lisco, F.; Kaminski, P.M.; Abbas, A.; Bowers, J.W.; Claudio, G.; Losurdo, M.; Walls, J.M.

    2015-01-01

    Cadmium Sulphide (CdS) is an important n-type semiconductor widely used as a window layer in thin film photovoltaics Copper Indium Selenide, Copper Indium Gallium (di)Selenide, Copper Zinc Tin Sulphide and Cadmium Telluride (CdTe). Cadmium Sulphide has been deposited using a number of techniques but these techniques can be slow (chemical bath deposition and Radio Frequency sputtering) or the uniformity and the control of thickness can be relatively difficult (close space sublimation). In this paper we report on the development of a process using pulsed Direct Current magnetron sputtering which allows nanometre control of thin film thickness using time only. The CdS thin films deposited in this process are highly uniform and smooth. They exhibit the preferred hexagonal structure at room temperature deposition and they have excellent optical properties. Importantly, the process is highly stable despite the use of a semi-insulating magnetron target. Moreover, the process is very fast. The deposition rate using 1.5 kW of power to a 6-inch circular magnetron was measured to be greater than 8 nm/s. This makes the process suitable for industrial deployment. - Highlights: • Pulsed DC magnetron sputtering of CdS • High deposition rate deposition • Uniform, pinhole free films

  8. Deposition and characterization of titania-silica optical multilayers by asymmetric bipolar pulsed dc sputtering of oxide targets

    Energy Technology Data Exchange (ETDEWEB)

    Sagdeo, P R; Shinde, D D; Misal, J S [Optics and Thin Film Laboratory, Autonagar, BARC-Vizag, Visakhapatnam -530012 (India); Kamble, N M; Tokas, R B; Biswas, A; Poswal, A K; Thakur, S; Bhattacharyya, D; Sahoo, N K; Sabharwal, S C, E-mail: nksahoo@barc.gov.i, E-mail: sahoonk@gmail.co [Spectroscopy Division, Bhabha Atomic Research Centre, Trombay, Mumbai 400 085 (India)

    2010-02-03

    Titania-silica (TiO{sub 2}/SiO{sub 2}) optical multilayer structures have been conventionally deposited by reactive sputtering of metallic targets. In order to overcome the problems of arcing, target poisoning and low deposition rates encountered there, the application of oxide targets was investigated in this work with asymmetric bipolar pulsed dc magnetron sputtering. In order to evaluate the usefulness of this deposition methodology, an electric field optimized Fabry Perot mirror for He-Cd laser ({lambda} = 441.6 nm) spectroscopy was deposited and characterized. For comparison, this mirror was also deposited by the reactive electron beam (EB) evaporation technique. The mirrors developed by the two complementary techniques were investigated for their microstructural and optical reflection properties invoking atomic force microscopy, ellipsometry, grazing incidence reflectometry and spectrophotometry. From these measurements the layer geometry, optical constants, mass density, topography, surface and interface roughness and disorder parameters were evaluated. The microstructural properties and spectral functional characteristics of the pulsed dc sputtered multilayer mirror were found to be distinctively superior to the EB deposited mirror. The knowledge gathered during this study has been utilized to develop a 21-layer high-pass edge filter for radio photoluminescence dosimetry.

  9. Deposition and characterization of titania-silica optical multilayers by asymmetric bipolar pulsed dc sputtering of oxide targets

    International Nuclear Information System (INIS)

    Sagdeo, P R; Shinde, D D; Misal, J S; Kamble, N M; Tokas, R B; Biswas, A; Poswal, A K; Thakur, S; Bhattacharyya, D; Sahoo, N K; Sabharwal, S C

    2010-01-01

    Titania-silica (TiO 2 /SiO 2 ) optical multilayer structures have been conventionally deposited by reactive sputtering of metallic targets. In order to overcome the problems of arcing, target poisoning and low deposition rates encountered there, the application of oxide targets was investigated in this work with asymmetric bipolar pulsed dc magnetron sputtering. In order to evaluate the usefulness of this deposition methodology, an electric field optimized Fabry Perot mirror for He-Cd laser (λ = 441.6 nm) spectroscopy was deposited and characterized. For comparison, this mirror was also deposited by the reactive electron beam (EB) evaporation technique. The mirrors developed by the two complementary techniques were investigated for their microstructural and optical reflection properties invoking atomic force microscopy, ellipsometry, grazing incidence reflectometry and spectrophotometry. From these measurements the layer geometry, optical constants, mass density, topography, surface and interface roughness and disorder parameters were evaluated. The microstructural properties and spectral functional characteristics of the pulsed dc sputtered multilayer mirror were found to be distinctively superior to the EB deposited mirror. The knowledge gathered during this study has been utilized to develop a 21-layer high-pass edge filter for radio photoluminescence dosimetry.

  10. Study of static properties of magnetron-type space charges; Etude des proprietes statiques des charges d'espace du type magnetron

    Energy Technology Data Exchange (ETDEWEB)

    Delcroix, Jean-Loup

    1953-05-30

    This research thesis reports an in-depth analysis of physical properties of static regimes to address the issue of space charges. This theoretical study of the Hull magnetron is followed by the description of experiments on the Hull magnetron which highlight transitions between the different regimes. Then, another theoretical approach aims at generalising the magnetron theory, based on other types of magnetron theory (general equations of magnetron-type space charges, inverted Hull magnetron theory, circular field magnetron theory)

  11. Magnetron sputtering system with an annual discharge zone and two cathode modules

    International Nuclear Information System (INIS)

    Savich, V. A.; Yasyunas, A. A.; Kovrigo, V. M.; Kotov, D. A.; Shiripov, V. Ya.

    2013-01-01

    In this article, general discharge characteristics of a cylindrical magnetron sputtering system with an annual sputtering zone and a high target usage coefficient designed for transparent conducting coatings are shown. Two coupled DC-cathodes are used to improve coating uniformity. Radial sputtered material fluxes are being created. The engineered magnetic system is extremely balanced (G-factor is much higher than 2) and thus provides maximal effective operating power higher than 6 kW. The effectiveness of a magnetic trap results in a fast work cycle (less than 1.5 min) and a high target material usage coefficient (higher than 40%). A multipole magnetic field with null magnetic flux density zones lower target’s surface is being created. There is an influence between cathode modules despite mutual magnetic isolation, so magnetic conductors-shunts are used to weaken it. The magnetron can be used to sputter both metals and conducting ceramics (including ITO). (authors)

  12. Microstructural evaluation of NiTi-based films deposited by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Crăciunescu, Corneliu M., E-mail: corneliu.craciunescu@upt.ro; Mitelea, Ion, E-mail: corneliu.craciunescu@upt.ro; Budău, Victor, E-mail: corneliu.craciunescu@upt.ro [Department of Materials and Manufacturing Engineering, Politehnica University of Timisoara (Romania); Ercuţa, Aurel [Department of Materials and Manufacturing Engineering, Politehnica University of Timisoara and Department of Physics, West University Timisoara (Romania)

    2014-11-24

    Shape memory alloy films belonging to the NiTi-based systems were deposited on heated and unheated substrates, by magnetron sputtering in a custom made system, and their structure and composition was analyzed using electron microscopy. Several substrates were used for the depositions: glass, Cu-Zn-Al, Cu-Al-Ni and Ti-NiCu shape memory alloy ribbons and kapton. The composition of the Ti-Ni-Cu films showed limited differences, compared to the one of the target and the microstructure for the DC magnetron sputtering revealed crystallized structure with features determined on peel off samples from a Si wafer. Both inter and transcrystalline fractures were observed and related to the interfacial stress developed on cooling from deposition temperature.

  13. The microstructure and properties of titanium dioxide films synthesized by unbalanced magnetron sputtering

    International Nuclear Information System (INIS)

    Leng, Y.X.; Chen, J.Y.; Yang, P.; Sun, H.; Huang, N.

    2007-01-01

    In this work, titanium oxide films were deposited on Ti6Al4V and Si (1 0 0) by DC unbalanced magnetron sputtering method at different oxygen pressure. X-ray diffraction (XRD), microhardness tests, pin-on-disk wear experiments, surface contact angle tests and platelet adhesion investigation were conducted to evaluate the properties of the films. The corrosion behavior of titanium dioxide films was characterized by potentiodynamic polarization. The results showed that titanium oxide films deposited by unbalance magnetron sputtering were compact and could obviously enhance microhardness, wear resistance of titanium alloy substrate. Potentiodynamic polarization curves showed that Ti-6Al-4V deposited with titanium dioxide films had lower dissolution currents than that of the uncoated one. The results of in vitro hemocompatibility analyses indicated that the blood compatibility of the titanium dioxide films with bandgap 3.2 eV have better blood compatibility

  14. A Unidirectional DC-DC Autotransformer for DC Grid Application

    Directory of Open Access Journals (Sweden)

    Meng Zhou

    2018-03-01

    Full Text Available Conventional unidirectional DC-DC converters for DC grid application employ DC-AC-DC two-stage conversion technology and suffer from high converter cost and power loss. To solve these issues, a unidirectional step-up DC-DC autotransformer (UUDAT and a unidirectional step-down DC-DC autotransformer (DUDAT are studied. The UUDAT and DUDAT are composed of a series connection of diode bridges and voltage source converters. Topologies of UUDAT and DUDAT are detailed. The harmonic and un-controllability issues are discussed. Control and possible application scenarios for UUDAT and DUDAT are depicted. DC fault isolation mechanism and the methods of dimensioning the voltage and power ratings of the components in UUDAT and DUDAT are studied. Extensive simulations on power system level and experiments on a UUDAT and DUDAT prototype verified their technical feasibility.

  15. Characteristics of W Doped Nanocrystalline Carbon Films Prepared by Unbalanced Magnetron Sputtering.

    Science.gov (United States)

    Park, Yong Seob; Park, Chul Min; Kim, Nam-Hoon; Kim, Jae-Moon

    2016-05-01

    Nanocrystalline tungsten doped carbon (WC) films were prepared by unbalanced magnetron sputtering. Tungsten was used as the doping material in carbon thin films with the aim of application as a contact strip in an electric railway. The structural, physical, and electrical properties of the fabricated WC films with various DC bias voltages were investigated. The films had a uniform and smooth surface. Hardness and frication characteristics of the films were improved, and the resistivity and sheet resistance decreased with increasing negative DC bias voltage. These results are associated with the nanocrystalline WC phase and sp(2) clusters in carbon networks increased by ion bombardment enhanced with increasing DC bias voltage. Consequently, the increase of sp(2) clusters containing WC nanocrystalline in the carbon films is attributed to the improvement in the physical and electrical properties.

  16. Stability of Brillouin flow in planar, conventional, and inverted magnetrons

    International Nuclear Information System (INIS)

    Simon, D. H.; Lau, Y. Y.; Greening, G.; Wong, P.; Gilgenbach, R. M.; Hoff, B. W.

    2015-01-01

    The Brillouin flow is the prevalent flow in crossed-field devices. We systematically study its stability in the conventional, planar, and inverted magnetron geometry. To investigate the intrinsic negative mass effect in Brillouin flow, we consider electrostatic modes in a nonrelativistic, smooth bore magnetron. We found that the Brillouin flow in the inverted magnetron is more unstable than that in a planar magnetron, which in turn is more unstable than that in the conventional magnetron. Thus, oscillations in the inverted magnetron may startup faster than the conventional magnetron. This result is consistent with simulations, and with the negative mass property in the inverted magnetron configuration. Inclusion of relativistic effects and electromagnetic effects does not qualitatively change these conclusions

  17. Arc-discharge and magnetron sputtering combined equipment for nanocomposite coating deposition

    International Nuclear Information System (INIS)

    Koval, N.N.; Borisov, D.P.; Savostikov, V.M.

    2005-01-01

    It is known that characteristics of nanocomposite coatings produced by reactive magnetron sputtering undergo an essential influence on the following parameters such as original component composition of targets being sputtered, as well as abundance ratio of such components in the coatings deposited, relative content of inert and reactionary gases in a gas mixture used and a value of operating pressure in a chamber, substrate temperature, and a value of substrate bias potential, determining energy of ionized atoms, ionized atoms flow density, i.e. ion current density on a substrate. The multifactor character of production process of nanocomposite coatings with certain physical and mechanical properties demands a purposeful and complex control on all above-mentioned parameters. To solve such a problem, an arc-discharge and magnetron sputtering combined equipment including a vacuum chamber of approximately ∼ 0.5 m 3 with a built-in low-pressure plasma generator made on the basis of non-self-sustained discharge with a thermal cathode and a planar magnetron combined with two sputtered targets has been created. Construction of such a complex set-up provides both an autonomous mode of operation and simultaneous operation of an arc plasma generator and magnetron sputtering system. Magnetron sputtering of either one or two targets simultaneously is provided as well. An arc plasma generator enables ions current density control on a substrate in a wide range due to discharge current varying from 1 to 100 A. Energy of ions is also being controlled in a wide range by a negative bias potential from 0 to 1000 V applied to a substrate. The wide control range of gas plasma density of a arc discharge of approximately 10 9 -10 11 cm -3 and high uniformity of its distribution over the total volume of an operating chamber (about 15% error with regard to the mean value) provides a purposeful and simultaneous control either of magnetron discharge characteristics (operating pressure of

  18. CEERI-CAT joint venture for development of accelerator magnetrons

    International Nuclear Information System (INIS)

    Prasad, Sharda; Kaushik, S.C.; Mahesh Kumar; Chaudhary, P.; Shrivastava, Purushottam; Wanmode, Y.; Hannurkar, P.R.

    2003-01-01

    LINAC and Microtron systems for electron acceleration up to few tens of MeV, requires pulsed RF sources such as magnetron and klystron in S-Band frequency range with peak power in the range of few MW. The major emphasis under this program was to develop critical technologies involved in the development of 2 MW magnetron. This paper discusses the development of 2 MW magnetron along with critical technologies involved and test facilities developed by CAT for testing of this magnetron

  19. Analysis of peer-to-peer locking of magnetrons

    International Nuclear Information System (INIS)

    Pengvanich, P.; Lau, Y. Y.; Cruz, E.; Gilgenbach, R. M.; Hoff, B.; Luginsland, J. W.

    2008-01-01

    The condition for mutual, or peer-to-peer, locking of two magnetrons is derived. This condition reduces to Adler's classical phase-locking condition in the limit where one magnetron becomes the ''master'' and the other becomes the ''slave.'' The formulation is extended to the peer-to-peer locking of N magnetrons, under the assumption that the electromagnetic coupling among the N magnetrons is modeled by an N-port network.

  20. Step-Up DC-DC converters

    DEFF Research Database (Denmark)

    Forouzesh, Mojtaba; Siwakoti, Yam P.; Gorji, Saman A.

    2017-01-01

    on the general law and framework of the development of next-generation step-up dc-dc converters, this paper aims to comprehensively review and classify various step-up dc-dc converters based on their characteristics and voltage-boosting techniques. In addition, the advantages and disadvantages of these voltage...

  1. Microstructural control of TiC/a-C nanocomposite coatings with pulsed magnetron sputtering

    International Nuclear Information System (INIS)

    Pei, Y.T.; Chen, C.Q.; Shaha, K.P.; De Hosson, J.Th.M.; Bradley, J.W.; Voronin, S.A.; Cada, M.

    2008-01-01

    In this paper, we report some striking results on the microstructural control of TiC/a-C nanocomposite coatings with pulsed direct current (DC) magnetron sputtering. The interface morphology and microstructure evolution as a function of pulse frequency and duty cycle were scrutinized using atomic force microscopy, scanning electron microscopy and high-resolution transmission electron microscopy techniques. It is shown that, with increasing pulse frequency, the nanocomposite coatings exhibit evolutions in morphology of the growing interface from rough to smooth and in the microstructure from strongly columnar to fully columnar-free. In addition, the smoothly growing interface favors the formation of a tailor-made multilayered nanocomposite structure. The fundamental mechanisms are analyzed with the assistance of plasma diagnostic experiments. Ion mass/energy spectrometry measurements reveal that, depending on the frequency and duty cycle of DC pulses, pulsing of the magnetrons can control the flux and energy distribution of Ar + ions over a very broad range for concurrent impingement on the growing interface of deposited coatings, in comparison with DC sputtering. The significantly enhanced energy flux density is thought to be responsible for the 'adatom transfer' in interface smoothening and thus the restraint of columnar growth

  2. The structural properties of CdS deposited by chemical bath deposition and pulsed direct current magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Lisco, F., E-mail: F.Lisco@lboro.ac.uk [Centre for Renewable Energy Systems Technology (CREST), School of Electronic, Electrical and Systems Engineering, Loughborough University, Leicestershire, LE11 3TU (United Kingdom); Kaminski, P.M.; Abbas, A.; Bass, K.; Bowers, J.W.; Claudio, G. [Centre for Renewable Energy Systems Technology (CREST), School of Electronic, Electrical and Systems Engineering, Loughborough University, Leicestershire, LE11 3TU (United Kingdom); Losurdo, M. [Institute of Inorganic Methodologies and of Plasmas, IMIP-CNR, via Orabona 4, 70126 Bari (Italy); Walls, J.M. [Centre for Renewable Energy Systems Technology (CREST), School of Electronic, Electrical and Systems Engineering, Loughborough University, Leicestershire, LE11 3TU (United Kingdom)

    2015-05-01

    Cadmium sulphide (CdS) thin films were deposited by two different processes, chemical bath deposition (CBD), and pulsed DC magnetron sputtering (PDCMS) on fluorine doped-tin oxide coated glass to assess the potential advantages of the pulsed DC magnetron sputtering process. The structural, optical and morphological properties of films obtained by CBD and PDCMS were investigated using X-ray photoelectron spectroscopy, X-ray diffraction, scanning and transmission electron microscopy, spectroscopic ellipsometry and UV-Vis spectrophotometry. The as-grown films were studied and comparisons were drawn between their morphology, uniformity, crystallinity, and the deposition rate of the process. The highest crystallinity is observed for sputtered CdS thin films. The absorption in the visible wavelength increased for PDCMS CdS thin films, due to the higher density of the films. The band gap measured for the as-grown CBD-CdS is 2.38 eV compared to 2.34 eV for PDCMS-CdS, confirming the higher density of the sputtered thin film. The higher deposition rate for PDCMS is a significant advantage of this technique which has potential use for high rate and low cost manufacturing. - Highlights: • Pulsed DC magnetron sputtering (PDCMS) of CdS films • Chemical bath deposition of CdS films • Comparison between CdS thin films deposited by chemical bath and PDCMS techniques • High deposition rate deposition for PDCMS deposition • Uniform, pinhole free CdS thin films.

  3. The structural properties of CdS deposited by chemical bath deposition and pulsed direct current magnetron sputtering

    International Nuclear Information System (INIS)

    Lisco, F.; Kaminski, P.M.; Abbas, A.; Bass, K.; Bowers, J.W.; Claudio, G.; Losurdo, M.; Walls, J.M.

    2015-01-01

    Cadmium sulphide (CdS) thin films were deposited by two different processes, chemical bath deposition (CBD), and pulsed DC magnetron sputtering (PDCMS) on fluorine doped-tin oxide coated glass to assess the potential advantages of the pulsed DC magnetron sputtering process. The structural, optical and morphological properties of films obtained by CBD and PDCMS were investigated using X-ray photoelectron spectroscopy, X-ray diffraction, scanning and transmission electron microscopy, spectroscopic ellipsometry and UV-Vis spectrophotometry. The as-grown films were studied and comparisons were drawn between their morphology, uniformity, crystallinity, and the deposition rate of the process. The highest crystallinity is observed for sputtered CdS thin films. The absorption in the visible wavelength increased for PDCMS CdS thin films, due to the higher density of the films. The band gap measured for the as-grown CBD-CdS is 2.38 eV compared to 2.34 eV for PDCMS-CdS, confirming the higher density of the sputtered thin film. The higher deposition rate for PDCMS is a significant advantage of this technique which has potential use for high rate and low cost manufacturing. - Highlights: • Pulsed DC magnetron sputtering (PDCMS) of CdS films • Chemical bath deposition of CdS films • Comparison between CdS thin films deposited by chemical bath and PDCMS techniques • High deposition rate deposition for PDCMS deposition • Uniform, pinhole free CdS thin films

  4. Highly -oriented growth of polycrystalline silicon films on glass by pulsed magnetron sputtering

    International Nuclear Information System (INIS)

    Reinig, P.; Selle, B.; Fenske, F.; Fuhs, W.; Alex, V.; Birkholz, M.

    2002-01-01

    Nominally undoped polycrystalline silicon (poly-Si) thin films were deposited on glass at 450 deg. C at high deposition rate (>100 nm/min) by pulsed dc magnetron sputtering. The pulse frequency was found to have a significant influence on the preferred grain orientation. The x-ray diffraction pattern exhibits a strong enhancement of the (400) reflex with increasing pulse frequency. The quantitative evaluation reveals that over 90% of the grains are oriented. The observed change in preferred grain orientation in poly-Si films at low temperatures is associated with concurrent ion bombardment of the growing film

  5. Intrinsic photocatalytic assessment of reactively sputtered TiO₂ films.

    Science.gov (United States)

    Rafieian, Damon; Driessen, Rick T; Ogieglo, Wojciech; Lammertink, Rob G H

    2015-04-29

    Thin TiO2 films were prepared by DC magnetron reactive sputtering at different oxygen partial pressures. Depending on the oxygen partial pressure during sputtering, a transition from metallic Ti to TiO2 was identified by spectroscopic ellipsometry. The crystalline nature of the film developed during a subsequent annealing step, resulting in thin anatase TiO2 layers, displaying photocatalytic activity. The intrinsic photocatalytic activity of the catalysts was evaluated for the degradation of methylene blue (MB) using a microfluidic reactor. A numerical model was employed to extract the intrinsic reaction rate constants. High conversion rates (90% degradation within 20 s residence time) were observed within these microreactors because of the efficient mass transport and light distribution. To evaluate the intrinsic reaction kinetics, we argue that mass transport has to be accounted for. The obtained surface reaction rate constants demonstrate very high reactivity for the sputtered TiO2 films. Only for the thinnest film, 9 nm, slightly lower kinetics were observed.

  6. The Development and Application of the Magnetron,

    Science.gov (United States)

    1982-03-31

    of *medicine. The power of the magnetron used is from several tens of watts to several hundred watts. Microwave physiotherapy has been used in...clinical practice for the fast cure of arthritis , rheumatism and the subsidence of swelling. Therapeutic results have been excellent. In recent years

  7. Simulation of the electric potential and plasma generation coupling in magnetron sputtering discharges

    Science.gov (United States)

    Trieschmann, Jan; Krueger, Dennis; Schmidt, Frederik; Brinkmann, Ralf Peter; Mussenbrock, Thomas

    2016-09-01

    Magnetron sputtering typically operated at low pressures below 1 Pa is a widely applied deposition technique. For both, high power impulse magnetron sputtering (HiPIMS) as well as direct current magnetron sputtering (dcMS) the phenomenon of rotating ionization zones (also referred to as spokes) has been observed. A distinct spatial profile of the electric potential has been associated with the latter, giving rise to low, mid, and high energy groups of ions observed at the substrate. The adherent question of which mechanism drives this process is still not fully understood. This query is approached using Monte Carlo simulations of the heavy particle (i.e., ions and neutrals) transport consistently coupled to a pre-specified electron density profile via the intrinsic electric field. The coupling between the plasma generation and the electric potential, which establishes correspondingly, is investigated. While the system is observed to strive towards quasi-neutrality, distinct mechanisms governing the shape of the electric potential profile are identified. This work is supported by the German Research Foundation (DFG) in the frame of the transregional collaborative research centre TRR 87.

  8. The influence of annealing treatments on the properties of Ag:TiO{sub 2} nanocomposite films prepared by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Adochite, R.C. [Centro de Fisica, Universidade do Minho, Campus de Azurem, 4800-058 Guimaraes (Portugal); Department of Materials Science and Engineering, ' Transilvania' University, 29 Eroilor Blvd., 500036 Brasov (Romania); Munteanu, D., E-mail: muntean.d@unitbv.ro [Department of Materials Science and Engineering, ' Transilvania' University, 29 Eroilor Blvd., 500036 Brasov (Romania); Torrell, M.; Cunha, L. [Centro de Fisica, Universidade do Minho, Campus de Azurem, 4800-058 Guimaraes (Portugal); Alves, E.; Barradas, N.P. [Instituto Tecnologico e Nuclear, Dept. Fisica, Apartado 21, E.N. 10, 2686-953 Sacavem (Portugal); Cavaleiro, A. [SEC-CEMUC - Universidade de Coimbra, Dept. Eng. Mecanica, Polo II, 3030-788 Coimbra (Portugal); Riviere, J.P.; Le Bourhis, E.; Eyidi, D. [Institut Pprime, UPR 3346-CNRS-Universite de Poitiers-ENSMA, SP2MI, teleport2, Bd M. et Pierre Curie, BP 30179, 86962 Futuroscope-Chasseneuil (France); Vaz, F. [Centro de Fisica, Universidade do Minho, Campus de Azurem, 4800-058 Guimaraes (Portugal)

    2012-02-01

    The present paper reports on the preparation and characterization of DC reactive magnetron sputtered Ag:TiO{sub 2} nanocomposite coatings, with a silver content of about 8 at.% (average estimation). The as-deposited samples were subjected to annealing, in a protective atmosphere, at temperatures ranging from 200 to 800 Degree-Sign C. Morphology, structure, hardness and friction behaviour were characterised after each heat treatment. The cross-sections of the films were studied by transmission electron microscopy (TEM). X-ray diffraction (XRD) was used to determine the thin-film structure and crystallinity as a function of annealing temperature. XRD analysis confirmed the presence of silver in all the samples and the crystallization of the TiO{sub 2} matrix for the samples annealed at temperatures above 300 Degree-Sign C. These structural changes were also followed by significant morphological variations, which resulted in the change of the mechanical properties of the films (hardness and Young's modulus) as well as of their tribological behaviour.

  9. DC Home Appliances for DC Distribution System

    Directory of Open Access Journals (Sweden)

    MUHAMMAD KAMRAN

    2017-10-01

    Full Text Available This paper strengthens the idea of DC distribution system for DC microgrid consisting of a building of 50 apartments. Since the war of currents AC system has been dominant because of the paucity of research in the protection of the DC system. Now with the advance research in power electronics material and components, generation of electricity is inherently DC as by solar PV, fuel cell and thermoelectric generator that eliminates the rectification process. Transformers are replaced by the power electronics buck-boost converters. DC circuit breakers have solved the protection problems for both DC transmission and distribution system. In this paper 308V DC microgrid is proposed and home appliances (DC internal are modified to operate on 48V DC from DC distribution line. Instead of using universal and induction motors in rotary appliances, BLDC (Brushless DC motors are proposed that are highly efficient with minimum electro-mechanical and no commutation losses. Proposed DC system reduces the power conversion stages, hence diminishes the associated power losses and standby losses that boost the overall system efficiency. So in view of all this a conventional AC system can be replaced by a DC system that has many advantages by cost as well as by performance

  10. Step-Up DC-DC converters

    DEFF Research Database (Denmark)

    Forouzesh, Mojtaba; Siwakoti, Yam P.; Gorji, Saman A.

    2017-01-01

    on the general law and framework of the development of next-generation step-up dc-dc converters, this paper aims to comprehensively review and classify various step-up dc-dc converters based on their characteristics and voltage-boosting techniques. In addition, the advantages and disadvantages of these voltage......DC-DC converters with voltage boost capability are widely used in a large number of power conversion applications, from fraction-of-volt to tens of thousands of volts at power levels from milliwatts to megawatts. The literature has reported on various voltage-boosting techniques, in which......-boosting techniques and associated converters are discussed in detail. Finally, broad applications of dc-dc converters are presented and summarized with comparative study of different voltage-boosting techniques....

  11. DC electric springs with DC/DC converters

    DEFF Research Database (Denmark)

    Wang, Qingsong; Cheng, Ming; Jiang, Yunlei

    2016-01-01

    The concept of DC electric spring (DCES) was recently proposed to solve the stability issue caused by integrating intermittent renewable energy sources (RESs) to DC microgrids. In this paper, a new topology of DCES is proposed based on DC/DC converters. The proposed DCES consists of a bi-directio......The concept of DC electric spring (DCES) was recently proposed to solve the stability issue caused by integrating intermittent renewable energy sources (RESs) to DC microgrids. In this paper, a new topology of DCES is proposed based on DC/DC converters. The proposed DCES consists of a bi...... and/or constant discharging for batteries is adopted and four operating modes are analyzed as charging-positive, charging-negative, discharging-positive and discharging-negative modes. An additional mechanism for fast charging or fast discharging is also designed to secure normal operation...... of batteries. With the proposed DCES, the power fluctuations due to intermittent RESs can be passed to non-critical loads (NCLs) and batteries while power on critical loads (CLs) is kept stable. This is possibly the first attempt to design a DCES with only DC/DC converters. The performances of the proposed...

  12. Functional nanostructured titanium nitride films obtained by sputtering magnetron

    International Nuclear Information System (INIS)

    Sanchez, O.; Hernandez-Velez, M.; Navas, D.; Auger, M.A.; Baldonedo, J.L.; Sanz, R.; Pirota, K.R.; Vazquez, M.

    2006-01-01

    Development of new methods in the formation of hollow structures, in particular, nanotubes and nanocages are currently generating a great interest as a consequence of the growing relevance of these nanostructures on many technological fields, ranging from optoelectronics to biotechnology. In this work, we report the formation of titanium nitride (TiN) nanotubes and nanohills via reactive sputtering magnetron processes. Anodic Alumina Membranes (AAM) were used as template substrates to grow the TiN nanostructures. The AAM were obtained through electrochemical anodization processes by using oxalic acid solutions as electrolytes. The nanotubes were produced at temperatures below 100 deg. C, and using a pure titanium (99.995%) sputtering target and nitrogen as reactive gas. The obtained TiN thin films showed surface morphologies adjusted to pore diameter and interpore distance of the substrates, as well as ordered arrays of nanotubes or nanohills depending on the sputtering and template conditions. High Resolution Scanning Electron Microscopy (HRSEM) was used to elucidate both the surface order and morphology of the different grown nanostructures. The crystalline structure of the samples was examined using X-ray Diffraction (XRD) patterns and their qualitative chemical composition by using X-ray Energy Dispersive Spectroscopy (XEDS) in a scanning electron microscopy

  13. Electron relaxation properties of Ar magnetron plasmas

    Science.gov (United States)

    Xinjing, CAI; Xinxin, WANG; Xiaobing, ZOU

    2018-03-01

    An understanding of electron relaxation properties in plasmas is of importance in the application of magnetrons. An improved multi-term approximation of the Boltzmann equation is employed to study electron transport and relaxation properties in plasmas. Elastic, inelastic and nonconservative collisions between electrons and neutral particles are considered. The expressions for the transport coefficients are obtained using the expansion coefficients and the collision operator term. Numerical solutions of the matrix equations for the expansion coefficients are also investigated. Benchmark calculations of the Reid model are presented to demonstrate the accuracy of the improved multi-term approximation. It is shown that the two-term approximation is generally not accurate enough and the magnetic fields can reduce the anisotropy of the velocity distribution function. The electron relaxation properties of Ar plasmas in magnetrons for various magnetic fields are studied. It is demonstrated that the energy parameters change more slowly than the momentum parameters.

  14. Fuzzy tungsten in a magnetron sputtering device

    Energy Technology Data Exchange (ETDEWEB)

    Petty, T.J., E-mail: tjpetty@liv.ac.uk [Department of Electrical Engineering and Electronics, University of Liverpool, Brownlow Hill, Liverpool, L69 3GJ (United Kingdom); Khan, A. [Pariser Building-G11, School of Mechanical, Aerospace and Civil Engineering, The University of Manchester, Manchester, M13 9PL (United Kingdom); Heil, T. [NiCaL, Block C Waterhouse Building, 1-3 Brownlow Street, Liverpool, L69 3GL (United Kingdom); Bradley, J.W., E-mail: j.w.bradley@liverpool.ac.uk [Department of Electrical Engineering and Electronics, University of Liverpool, Brownlow Hill, Liverpool, L69 3GJ (United Kingdom)

    2016-11-15

    Helium ion induced tungsten nanostructure (tungsten fuzz) has been studied in a magnetron sputtering device. Three parameters were varied, the fluence from 3.4 × 10{sup 23}–3.0 × 10{sup 24} m{sup −2}, the He ion energy from 25 to 70 eV, and the surface temperature from 900 to 1200 K. For each sample, SEM images were captured, and measurements of the fuzz layer thickness, surface roughness, reflectivity, and average structure widths are provided. A cross-over point from pre-fuzz to fully formed fuzz is found at 2.4 ± 0.4 × 10{sup 24} m{sup −2}, and a temperature of 1080 ± 60 K. No significant change was observed in the energy sweep. The fuzz is compared to low fluence fuzz created in the PISCES-A linear plasma device. Magnetron fuzz is less uniform than fuzz created by PISCES-A and with generally larger structure widths. The thicknesses of the magnetron samples follow the original Φ{sup 1/2} relation as opposed to the incubation fluence fit. - Highlights: • Fuzz has been created in a magnetron sputtering device. • Three parameters for fuzz formation have been swept. • A cross-over from pre-fuzz to fully formed fuzz is seen. • Evidence for annealing out at lower temperatures than has been seen before. • Evidence to suggest that fuzz grown in discrete exposures is not consistent with fuzz grown in one long exposure.

  15. Fuzzy tungsten in a magnetron sputtering device

    International Nuclear Information System (INIS)

    Petty, T.J.; Khan, A.; Heil, T.; Bradley, J.W.

    2016-01-01

    Helium ion induced tungsten nanostructure (tungsten fuzz) has been studied in a magnetron sputtering device. Three parameters were varied, the fluence from 3.4 × 10 23 –3.0 × 10 24  m −2 , the He ion energy from 25 to 70 eV, and the surface temperature from 900 to 1200 K. For each sample, SEM images were captured, and measurements of the fuzz layer thickness, surface roughness, reflectivity, and average structure widths are provided. A cross-over point from pre-fuzz to fully formed fuzz is found at 2.4 ± 0.4 × 10 24  m −2 , and a temperature of 1080 ± 60 K. No significant change was observed in the energy sweep. The fuzz is compared to low fluence fuzz created in the PISCES-A linear plasma device. Magnetron fuzz is less uniform than fuzz created by PISCES-A and with generally larger structure widths. The thicknesses of the magnetron samples follow the original Φ 1/2 relation as opposed to the incubation fluence fit. - Highlights: • Fuzz has been created in a magnetron sputtering device. • Three parameters for fuzz formation have been swept. • A cross-over from pre-fuzz to fully formed fuzz is seen. • Evidence for annealing out at lower temperatures than has been seen before. • Evidence to suggest that fuzz grown in discrete exposures is not consistent with fuzz grown in one long exposure.

  16. Magnetic properties of in-plane oriented barium hexaferrite thin films prepared by direct current magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Xiaozhi; Yue, Zhenxing, E-mail: yuezhx@mail.tsinghua.edu.cn; Meng, Siqin; Yuan, Lixin [State Key Laboratory of New Ceramics and Fine Processing, School of Materials Science and Engineering, Tsinghua University, Beijing 100084 (China)

    2014-12-28

    In-plane c-axis oriented Ba-hexaferrite (BaM) thin films were prepared on a-plane (112{sup ¯}0) sapphire (Al{sub 2}O{sub 3}) substrates by DC magnetron sputtering followed by ex-situ annealing. The DC magnetron sputtering was demonstrated to have obvious advantages over the traditionally used RF magnetron sputtering in sputtering rate and operation simplicity. The sputtering power had a remarkable influence on the Ba/Fe ratio, the hematite secondary phase, and the grain morphology of the as-prepared BaM films. Under 80 W of sputtering power, in-plane c-axis highly oriented BaM films were obtained. These films had strong magnetic anisotropy with high hysteresis loop squareness (M{sub r}/M{sub s} of 0.96) along the in-plane easy axis and low M{sub r}/M{sub s} of 0.03 along the in-plane hard axis. X-ray diffraction patterns and pole figures revealed that the oriented BaM films grew via an epitaxy-like growth process with the crystallographic relationship BaM (101{sup ¯}0)//α-Fe{sub 2}O{sub 3}(112{sup ¯}0)//Al{sub 2}O{sub 3}(112{sup ¯}0)

  17. A resonant dc-dc power converter assembly

    DEFF Research Database (Denmark)

    2015-01-01

    The present invention relates to a resonant DC-DC power converter assembly comprising a first resonant DC-DC power converter and a second resonant DC-DC power converter having identical circuit topologies. A first inductor of the first resonant DC-DC power converter and a second inductor of the s......The present invention relates to a resonant DC-DC power converter assembly comprising a first resonant DC-DC power converter and a second resonant DC-DC power converter having identical circuit topologies. A first inductor of the first resonant DC-DC power converter and a second inductor...... of the second resonant DC-DC power converter are configured for magnetically coupling the first and second resonant DC-DC power converters to each other to forcing substantially 180 degrees phase shift, or forcing substantially 0 degree phase shift, between corresponding resonant voltage waveforms of the first...

  18. Relationship Between Crystalline Structure and Hardness of Ti-Si-N-O Coatings Fabricated by dc Sputtering

    Science.gov (United States)

    García-González, Leandro; Hernández-Torres, Julián; Mendoza-Barrera, Claudia; Meléndez-Lira, Miguel; García-Ramírez, Pedro J.; Martínez-Castillo, Jaime; Sauceda, Ángel; Herrera-May, Agustin L.; Muñoz Saldaña, Juan; Espinoza-Beltrán, Francisco J.

    2008-08-01

    Ti-Si-N-O coatings were deposited on AISI D2 tool steel and silicon substrates by dc reactive magnetron co-sputtering using a target of Ti-Si with a constant area ratio of 0.2. The substrate temperature was 400 °C and reactive atmosphere of nitrogen and argon. For all samples, argon flow was maintained constant at 25 sccm, while the flow of the nitrogen was varied to analyze the structural changes related to chemical composition and resistivity. According to results obtained by x-ray diffraction and stoichiometry calculations by x-ray energy dispersive spectroscopy the Ti-Si-N-O coatings contain two solid solutions. The higher crystalline part corresponds to titanium oxynitrure. Hardness tests on the coatings were carried out using the indentation work model and the hardness value was determined. Finally, the values of hardness were corroborated by nanoindentation test, and values of Young’s modulus and elastic recovery were discussed. We concluded that F2TSN sample ( F Ar = 25 sccm, F N = 5 sccm, P = 200 W, and P W = 8.9 × 10-3 mbar) presented the greatest hardness and the lowest resistivity values, due to its preferential crystalline orientation.

  19. A PLL based automated magnetron tuning mechanism for electron accelerators

    International Nuclear Information System (INIS)

    Khan, A M; Mahfooz, Mohammed; Sanjeev, Ganesh

    2008-01-01

    In this paper we report on a control system developed to tune the magnetron frequency to get the maximum beam pulse in a Microtron (an electron accelerator facility at Mangalore University). The control system so designed consists of a Microcontroller Unit (MCU), a Phase Locked Loop (PLL) and a Digital to Analog Converter (DAC) to track and tune the magnetron frequency. A PLL is used to track the deviation of the magnetron output frequency, and by monitoring the reflected wave voltage level, the microcontroller unit tunes the magnetron with the help of a tuner mechanism connected through a stepper motor.

  20. A PLL based automated magnetron tuning mechanism for electron accelerators

    Energy Technology Data Exchange (ETDEWEB)

    Khan, A M; Mahfooz, Mohammed [Dept. of Electronics, Mangalore University, Mangalagangotri, Karnataka State, India - 574 199 (India); Sanjeev, Ganesh [Microtron Centre, Mangalore University, Mangalagangotri, Karnataka State, India - 574 199 (India)], E-mail: mahfooz_81@yahoo.com

    2008-09-15

    In this paper we report on a control system developed to tune the magnetron frequency to get the maximum beam pulse in a Microtron (an electron accelerator facility at Mangalore University). The control system so designed consists of a Microcontroller Unit (MCU), a Phase Locked Loop (PLL) and a Digital to Analog Converter (DAC) to track and tune the magnetron frequency. A PLL is used to track the deviation of the magnetron output frequency, and by monitoring the reflected wave voltage level, the microcontroller unit tunes the magnetron with the help of a tuner mechanism connected through a stepper motor.

  1. Physical–chemical and biological behavior of an amorphous calcium phosphate thin film produced by RF-magnetron sputtering

    International Nuclear Information System (INIS)

    Santos, Euler A. dos; Moldovan, Simona; Mateescu, Mihaela; Faerber, Jacques; Acosta, Manuel; Pelletier, Hervé; Anselme, Karine; Werckmann, Jacques

    2012-01-01

    This work evaluates the thermal reactivity and the biological reactivity of an amorphous calcium phosphate thin film produced by radio frequency (RF) magnetron sputtering onto titanium substrates. The analyses showed that the sputtering conditions used in this work led to the deposition of an amorphous calcium phosphate. The thermal treatment of this amorphous coating in the presence of H 2 O and CO 2 promoted the formation of a carbonated HA crystalline coating with the entrance of CO 3 2− ions into the hydroxyl HA lattice. When immersed in culture medium, the amorphous and carbonated coatings exhibited a remarkable instability. The presence of proteins increased the dissolution process, which was confirmed by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) analyses. Moreover, the carbonated HA coating induced precipitation independently of the presence of proteins under dynamic conditions. Despite this surface instability, this reactive calcium phosphate significantly improved the cellular behavior. The cell proliferation was higher on the Ticp than on the calcium phosphate coatings, but the two coatings increased cellular spreading and stress fiber formation. In this sense, the presence of reactive calcium phosphate coatings can stimulate cellular behavior. - Highlights: ► Functionalization of Ti with reactive CaP thin film by RF-magnetron sputtering. ► De-hydroxylation facilitating the insertion of CO 3 2− into the HA lattice. ► High surface reactivity in the presence of culture medium. ► Cell behavior improved by the presence of reactive films.

  2. Fabrication and characterization of anatase/rutile–TiO2 thin films by magnetron sputtering: a review

    Directory of Open Access Journals (Sweden)

    Sakae Tanemura, Lei Miao, Wilfried Wunderlich, Masaki Tanemura, Yukimasa Mori, Shoichi Toh and Kenji Kaneko

    2005-01-01

    Full Text Available This review article summarizes briefly some important achievements of our recent reserach on anatase and/or rutile TiO2 thin films, fabricated by helicon RF magnetron sputtering, with good crystal quality and high density, and gives the-state-of-the-art of the knowledge on systematic interrelationship for fabrication conditions, crystal structure, composition, optical properties, and bactericidal abilities, and on the effective surface treatment to improve the optical reactivity of the obtained films.

  3. IGBT Based DC/DC Converter

    Directory of Open Access Journals (Sweden)

    M. Akherraz

    1997-12-01

    Full Text Available This paper presents an in-depth analytical and experimental investigation of an indirect DC-DC converter. The DC-AC conversion is a full bridge based on IGBT power modules, and the AC-DC conversion is done via a high  frequency AC link and a first diode bridge. The AC link, which consists of snubbing capacitors and a variable air-gap transformer, is analytically designed to fulfill Zero Voltage commutation requirement. The proposed converter is simulated using PSPICE and a prototype is designed built and tested in the laboratory. PSPICE simulation and experimental results are presented and compared.

  4. DEVICE FOR INVESTIGATION OF MAGNETRON AND PULSED-LASER PLASMA

    Directory of Open Access Journals (Sweden)

    A. P. Burmakov

    2012-01-01

    Full Text Available Various modifications of complex pulsed laser and magnetron deposition thin-film structures unit are presented. They include joint and separate variants of layer deposition. Unit realizes the plasma parameters control and enhances the possibility of laser-plasma and magnetron methods of coatings deposition.

  5. Indium oxide-based transparent conductive films deposited by reactive sputtering using alloy targets

    Science.gov (United States)

    Miyazaki, Yusuke; Maruyama, Eri; Jia, Junjun; Machinaga, Hironobu; Shigesato, Yuzo

    2017-04-01

    High-quality transparent conductive oxide (TCO) films, Sn-doped In2O3 (ITO) and In2O3-ZnO (IZO), were successfully deposited on either synthetic silica or polyethylene terephthalate (PET) substrates in the “transition region” by reactive dc magnetron sputtering using In-Zn and In-Sn alloy targets, respectively, with a specially designed plasma emission feedback system. The composition, crystallinity, surface morphology, and electrical and optical properties of the films were analyzed. All of the IZO films were amorphous, whereas the ITO films were polycrystalline over a wide range of deposition conditions. The minimum resistivities of the IZO and ITO films deposited on the heated PET substrates at 150 °C were 3.3 × 10-4 and 5.4 × 10-4 Ω·cm, respectively. By applying rf bias to unheated PET substrates, ITO films with a resistivity of 4.4 × 10-4 Ω·cm were deposited at a dc self-bias voltage of -60 V.

  6. A resonant dc-dc power converter assembly

    OpenAIRE

    Madsen, Mickey Pierre

    2015-01-01

    The present invention relates to a resonant DC-DC power converter assembly comprising a first resonant DC-DC power converter and a second resonant DC-DC power converter having identical circuit topologies. A first inductor of the first resonant DC-DC power converter and a second inductor of the second resonant DC-DC power converter are configured for magnetically coupling the first and second resonant DC-DC power converters to each other to forcing substantially 180 degrees phase shift, or fo...

  7. Fabrication and characterization of He-charged ODS-FeCrNi films deposited by a radio-frequency plasma magnetron sputtering technique

    Science.gov (United States)

    Song, Liang; Wang, Xianping; Wang, Le; Zhang, Ying; Liu, Wang; Jiang, Weibing; Zhang, Tao; Fang, Qianfeng; Liu, Changsong

    2017-04-01

    He-charged oxide dispersion strengthened (ODS) FeCrNi films were prepared by a radio-frequency (RF) plasma magnetron sputtering method in a He and Ar mixed atmosphere at 150 °C. As a comparison, He-charged FeCrNi films were also fabricated at the same conditions through direct current (DC) plasma magnetron sputtering. The doping of He atoms and Y2O3 in the FeCrNi films was realized by the high backscattered rate of He ions and Y2O3/FeCrNi composite target sputtering method, respectively. Inductive coupled plasma (ICP) and x-ray photoelectron spectroscopy (XPS) analysis confirmed the existence of Y2O3 in FeCrNi films, and Y2O3 content hardly changed with sputtering He/Ar ratio. Cross-sectional scanning electron microscopy (SEM) shows that the FeCrNi films were composed of dense columnar nanocrystallines and the thickness of the films was obviously dependent on He/Ar ratio. Nanoindentation measurements revealed that the FeCrNi films fabricated through DC/RF plasma magnetron sputtering methods exhibited similar hardness values at each He/Ar ratio, while the dispersion of Y2O3 apparently increased the hardness of the films. Elastic recoil detection (ERD) showed that DC/RF magnetron sputtered FeCrNi films contained similar He amounts (˜17 at.%). Compared with the minimal change of He level with depth in DC-sputtered films, the He amount decreases gradually in depth in the RF-sputtered films. The Y2O3-doped FeCrNi films were shown to exhibit much smaller amounts of He owing to the lower backscattering possibility of Y2O3 and the inhibition effect of nano-sized Y2O3 particles on the He element.

  8. A microcontroller based tuning mechanism for the magnetron

    International Nuclear Information System (INIS)

    Khan, A.M.; Mahfooz, M.; Hanumaiah, B.; Ganesh; Siddappa, K.

    2006-01-01

    In this paper we report on a control system developed to tune the magnetron frequency to get the maximum beam pulse in the microtron (electron accelerator facility at Mangalore University). The control system so designed consists of a microcontroller, a phase locked loop (PLL) and a digital to analog converter (DAC) to control the magnetron frequency. The voltage value given by the microcontroller through the DAC decides the reference frequency. The PLL gives the error voltage whenever there is difference between the reference and the magnetron frequencies. The microcontroller unit tracks the error voltage and tunes the magnetron with the help of a tuner mechanism connected through a stepper motor. The microcontroller also monitors the beam current level and accordingly adjusts the reference frequency to successfully tune the magnetron. (author)

  9. Active superconducting DC fault current limiter based on flux compensation

    International Nuclear Information System (INIS)

    Shi Jing; Tang Yuejin; Wang, Chen; Zhou Yusheng; Li Jingdong; Ren Li; Chen Shijie

    2006-01-01

    With the extensive application of DC power systems, suppression of DC fault current is an important subject that guarantees system security. This paper presents an active superconducting DC fault current limiter (DC-SFCL) based on flux compensation. The DC-SFCL is composed of two superconducting windings wound on a single iron core, the primary winding is in series with DC power system, and the second winding is connected with AC power system through a PWM converter. In normal operating state, the flux in the iron core is compensated to zero, and the SFCL has no influence on DC power system. In the case of DC system accident, through regulating the active power exchange between the SFCL's second winding and the AC power system, the current on the DC side can be limited to different level complying with the system demand. Moreover, the PWM converter that interface the DC system and AC system can be controlled as a reactive power source to supply voltage support for the AC side, which has little influence on the performance of SFCL. Using MATLAB SIMULINK, the mathematic model of the DC-SFCL is created, simulation results validate the dynamics of system, and the performance of DC-SFCL is confirmed

  10. The improvement of all-solid-state electrochromic devices fabricated with the reactive sputter and cathodic arc technology

    Directory of Open Access Journals (Sweden)

    Min-Chuan Wang

    2016-11-01

    Full Text Available The all-solid-state electrochromic device (ECD with the one substrate structure fabricated by the reactive dc magnetron sputtering (DCMS and cathodic vacuum arc plasma (CVAP technology has been developed for smart electrochromic (EC glass application. The EC layer and ion conductor layer were deposited by reactive DCMS and CVAP technology, respectively. The ion conductor layer Ta2O5 deposited by the CVAP technology has provided the better porous material structure for ion transportation and showed 1.76 times ion conductivity than devices with all sputtering process. At the same time, the EC layer WO3 and NiO deposited by the reactive DCMS have also provided the high quality and uniform characteristic to overcome the surface roughness effect of the CVAP ion conductor layer in multilayer device structure. The all-solid-state ECD with the CVAP ion conductor layer has demonstrated a maximum transmittance variation (ΔT of 55% at 550nm and a faster-switching speed. Furthermore, the lower equipment cost and higher deposition rate could be achieved by the application of CVAP technology.

  11. Deposition Rates of High Power Impulse Magnetron Sputtering: Physics and Economics

    Energy Technology Data Exchange (ETDEWEB)

    Anders, Andre

    2009-11-22

    Deposition by high power impulse magnetron sputtering (HIPIMS) is considered by some as the new paradigm of advanced sputtering technology, yet this is met with skepticism by others for the reported lower deposition rates, if compared to rates of more conventional sputtering of equal average power. In this contribution, the underlying physical reasons for the rate changes are discussed, including (i) ion return to the target and self-sputtering, (ii) the less-than-linear increase of the sputtering yield with increasing ion energy, (iii) yield changes due to the shift of species responsible for sputtering, (iv) changes to due to greater film density, limited sticking, and self-sputtering on the substrate, (v) noticeable power losses in the switch module, (vi) changes of the magnetic balance and particle confinement of the magnetron due to self-fields at high current, and (vii) superposition of sputtering and sublimation/evaporation for selected materials. The situation is even more complicated for reactive systems where the target surface chemistry is a function of the reactive gas partial pressure and discharge conditions. While most of these factors imply a reduction of the normalized deposition rate, increased rates have been reported for certain conditions using hot targets and less poisoned targets. Finally, some points of economics and HIPIMS benefits considered.

  12. Deposition rates of high power impulse magnetron sputtering: Physics and economics

    International Nuclear Information System (INIS)

    Anders, Andre

    2010-01-01

    Deposition by high power impulse magnetron sputtering (HIPIMS) is considered by some as the new paradigm of advanced sputtering technology, yet this is met with skepticism by others for the reported lower deposition rates, if compared to rates of more conventional sputtering of equal average power. In this contribution, the underlying physical reasons for the rate changes are discussed, including (i) ion return to the target and self-sputtering, (ii) the less-than-linear increase in the sputtering yield with increasing ion energy, (iii) yield changes due to the shift of species responsible for sputtering, (iv) changes due to greater film density, limited sticking, and self-sputtering on the substrate, (v) noticeable power losses in the switch module, (vi) changes in the magnetic balance and particle confinement of the magnetron due to self-fields at high current, and (vii) superposition of sputtering and sublimation/evaporation for selected materials. The situation is even more complicated for reactive systems where the target surface chemistry is a function of the reactive gas partial pressure and discharge conditions. While most of these factors imply a reduction in the normalized deposition rate, increased rates have been reported for certain conditions using hot targets and less poisoned targets. Finally, some points of economics and HIPIMS benefits are considered.

  13. Surface functionalization of nanostructured LaB{sub 6}-coated Poly Trilobal fabric by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Yan, E-mail: wuyanchn@hotmail.com [Mechanical and Electrical Engineering Branch, Jiaxing Nanyang Polytechnic Institute, Jiaxing 314003 (China); Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Zhang, Lin, E-mail: zhanglin2007@sdu.edu.cn [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Min, Guanghui, E-mail: ghmin@sdu.edu.cn [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China); Yu, Huashun; Gao, Binghuan; Liu, Huihui; Xing, Shilong; Pang, Tao [Key Laboratory for Liquid-Solid Structural Evolution and Processing of Materials (Ministry of Education), Shandong University, Jinan 250061 (China)

    2016-10-30

    Highlights: • Nanostructured LaB{sub 6} films were deposited on flexible textile substrates by dc magnetron sputtering. • The pronounced influence of the working pressure on the morphologies and optical properties of LaB{sub 6} films has been revealed. • The concept of Ultraviolet Protection Factor (UPF) was employed and LaB{sub 6}-coated PET textiles with ultraviolet protection ability were obtained. - Abstract: Nanostructured LaB{sub 6} films were deposited on flexible Poly Trilobal substrates (PET textiles) through direct current magnetron sputtering in order to broaden its applications and realize surface functionalization of polyester fabrics. Characterizations and performances were investigated by employing a scanning electron microscope (SEM), Fourier transformation infrared spectroscopy (FT-IR) and ultraviolet-visible (UV–vis) spectrophotometer. Ultraviolet Protection Factor (UPF) conducted by the integral conversion was employed to measure the ultraviolet protection ability. As expected, the growth of LaB{sub 6} film depending on the pressure variation enhanced UV-blocking ability (UPF rating at 30.17) and absorption intensity of the textiles.

  14. Structure and morphology of magnetron sputter deposited ultrathin ZnO films on confined polymeric template

    Science.gov (United States)

    Singh, Ajaib; Schipmann, Susanne; Mathur, Aakash; Pal, Dipayan; Sengupta, Amartya; Klemradt, Uwe; Chattopadhyay, Sudeshna

    2017-08-01

    The structure and morphology of ultra-thin zinc oxide (ZnO) films with different film thicknesses on confined polymer template were studied through X-ray reflectivity (XRR) and grazing incidence small angle X-ray scattering (GISAXS). Using magnetron sputter deposition technique ZnO thin films with different film thicknesses (weight of polystyrene). The detailed internal structure, along the surface/interfaces and the growth direction of the system were explored in this study, which provides insight into the growth procedure of ZnO on confined polymer and reveals that a thin layer of ZnO, with very low surface and interface roughness, can be grown by DC magnetron sputtering technique, with approximately full coverage (with bulk like electron density) even in nm order of thickness, in 2-7 nm range on confined polymer template, without disturbing the structure of the underneath template. The resulting ZnO-polystyrene hybrid systems show strong ZnO near band edge (NBE) and deep-level (DLE) emissions in their room temperature photoluminescence spectra, where the contribution of DLE gets relatively stronger with decreasing ZnO film thickness, indicating a significant enhancement of surface defects because of the greater surface to volume ratio in thinner films.

  15. Electrical and Optical Properties of Fluorine Doped Tin Oxide Thin Films Prepared by Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Ziad Y. Banyamin

    2014-10-01

    Full Text Available Fluorine doped tin oxide (FTO coatings have been prepared using the mid-frequency pulsed DC closed field unbalanced magnetron sputtering technique in an Ar/O2 atmosphere using blends of tin oxide and tin fluoride powder formed into targets. FTO coatings were deposited with a thickness of 400 nm on glass substrates. No post-deposition annealing treatments were carried out. The effects of the chemical composition on the structural (phase, grain size, optical (transmission, optical band-gap and electrical (resistivity, charge carrier, mobility properties of the thin films were investigated. Depositing FTO by magnetron sputtering is an environmentally friendly technique and the use of loosely packed blended powder targets gives an efficient means of screening candidate compositions, which also provides a low cost operation. The best film characteristics were achieved using a mass ratio of 12% SnF2 to 88% SnO2 in the target. The thin film produced was polycrystalline with a tetragonal crystal structure. The optimized conditions resulted in a thin film with average visible transmittance of 83% and optical band-gap of 3.80 eV, resistivity of 6.71 × 10−3 Ω·cm, a carrier concentration (Nd of 1.46 × 1020 cm−3 and a mobility of 15 cm2/Vs.

  16. Phase and Frequency Locked Magnetrons for SRF Sources

    International Nuclear Information System (INIS)

    Neubauer, M.; Johnson, R.P.; Popovic, M.; Moretti, A.

    2009-01-01

    Magnetrons are low-cost highly-efficient microwave sources, but they have several limitations, primarily centered about the phase and frequency stability of their output. When the stability requirements are low, such as for medical accelerators or kitchen ovens, magnetrons are the very efficient power source of choice. But for high energy accelerators, because of the need for frequency and phase stability - proton accelerators need 1-2 degrees source phase stability, and electron accelerators need .1-.2 degrees of phase stability - they have rarely been used. We describe a novel variable frequency cavity technique which will be utilized to phase and frequency lock magnetrons.

  17. Full range ZVS DC-DC converter

    International Nuclear Information System (INIS)

    Upadhyay, Rinki; Badapanda, M.K.; Hannurkar, P.R.

    2011-01-01

    A 500 V, 24 Amp DC-DC converter with digital signal processor (DSP) based control and protection has been designed, fabricated and tested. Its power circuit consists of IGBT based single phase inverter bridge, ferrite transformer and diode rectifier. All IGBTs in the inverter bridge are operated in zero voltage switching (ZVS) mode to minimize switching losses thereby increasing the efficiency of the converter significantly. The efficiency of this converter is measured to be greater than 97% at full load. In a conventional full bridge inverter, typically ZVS is achieved under full load condition while at light load ZVS is lost. An auxiliary LC circuit has been intentionally incorporated in this converter to achieve ZVS even at light loaded conditions. Detailed simulation of the converter circuit is carried out and crucial waveforms have been presented in this paper. Microchip make dsPIC30F2020 DSP is employed to provide phase shifted PWMs to IGBTs in the inverter bridge. All the crucial parameters are also monitored by this DSP and in case of any unfavorable conditions, the converter is tripped off. Suitable experiments were carried out in this DC-DC converter under different loaded conditions and a close match between the simulated and experimental results were obtained. Such DC-DC converters can be connected in series or parallel for the development of solid state modular power supplies for various applications. (author)

  18. Direct current magnetron sputter-deposited ZnO thin films

    International Nuclear Information System (INIS)

    Hoon, Jian-Wei; Chan, Kah-Yoong; Krishnasamy, Jegenathan; Tou, Teck-Yong; Knipp, Dietmar

    2011-01-01

    Zinc oxide (ZnO) is a very promising electronic material for emerging transparent large-area electronic applications including thin-film sensors, transistors and solar cells. We fabricated ZnO thin films by employing direct current (DC) magnetron sputtering deposition technique. ZnO films with different thicknesses ranging from 150 nm to 750 nm were deposited on glass substrates. The deposition pressure and the substrate temperature were varied from 12 mTorr to 25 mTorr, and from room temperature to 450 deg. C, respectively. The influence of the film thickness, deposition pressure and the substrate temperature on structural and optical properties of the ZnO films was investigated using atomic force microscopy (AFM) and ultraviolet-visible (UV-Vis) spectrometer. The experimental results reveal that the film thickness, deposition pressure and the substrate temperature play significant role in the structural formation and the optical properties of the deposited ZnO thin films.

  19. Unbalanced Cylindrical Magnetron for Accelerating Cavities Coating

    CERN Document Server

    Rosaz, Guillaume; Calatroni, Sergio; Sublet, Alban; Tobarelli, Mauro

    2016-01-01

    We report in this paper the design and qualification of a cylindrical unbalanced magnetron source. The dedicated magnetic assemblies were simulated using a finite element model. A hall-effect magnetic probe was then used to characterize those assemblies and compared to the theoretical magnet profiles. These show a good agreement between the expected and actual values. the qualification of the different magnetic assemblies was then performed by measuring the ion flux density reaching the surface of the sample to be coated using a commercial retarding field energy analyzer. The strongest unbalanced configuration shows an increase from 0.016A.cm^-2 to 0.074A.cm^-2 of the ion flux density reaching the sample surface compared to the standard balanced configuration for a pressure 5.10^-3 mbar and a plasma source power of 300W.

  20. RF and dc desensitized electroexplosive device

    Science.gov (United States)

    Krainiak, John W.; Speaks, Paul D.; Cornett, Michael S.

    1989-07-01

    This patent application relates to electroexplosive devices (EEDs) such as detonators, blasting caps and squibs, in particular to a method and device for desensitizing EEDs to electromagnetic radiation and electrostatic charges with the added ability to desensitize the device to essentially dc currents. An insensitive electroexplosive device to electrically ignite explosive is disclosed. This device is inherently immune to radio frequency (RF) radiation, and also provides protection against dc or very low frequency RF induced by arcing. A central feature is use of zeners and capacitors to form a reactively balanced bridge circuit. When constructed in semiconductor form, as described in this application, the device is capable of incorporation in small caliber ordnance.

  1. Characterization and Optimization of the Magnetron Directional Amplifier

    National Research Council Canada - National Science Library

    Hatfield, Michael

    1999-01-01

    .... A conventional microwave oven magnetron may be converted into a two-port amplifier capable of delivering over 30 dB of gain, while remaining phase-locked to the input signal over a wide frequency range...

  2. Two-dimensional spatial survey of the plasma potential and electric field in a pulsed bipolar magnetron discharge

    International Nuclear Information System (INIS)

    Vetushka, A.; Karkari, S.K.; Bradley, J.W.

    2004-01-01

    Emissive and Langmuir probe techniques have been used to obtain two-dimensional (2D) spatial maps of the plasma potential V p , electric field E, and ion trajectories in a pulsed bipolar magnetron discharge. The magnetron was pulsed at a frequency of 100 kHz, with a 50% duty cycle and operated at an argon pressure of 0.74 Pa. The pulse wave form was characterized by three distinct phases: the 'overshoot', 'reverse', and 'on' phases. In the 'on' phase of the pulse, when the cathode voltage is driven to -670 V, the 2D spatial distribution of V p has a similar form to that in dc magnetron, with significant axial and radial electric fields in the bulk plasma, accelerating ions to the sheath edge above the cathode racetrack region. During the 'overshoot' phase (duration 200 ns), V p is raised to values greater than +330 V, more than 100 V above the cathode potential, with E pointing away from the target. In the 'reverse' phase V p has a value of +45 V at all measured positions, 2 V more positive than the target potential. In this phase there is no electric field present in the plasma. In the bulk of the plasma, the results from Langmuir probe and the emissive probe are in good agreement, however, in one particular region of the plasma outside the radius of the cathode, the emissive probe measurements are consistently more positive (up to 45 V in the 'on' time). This discrepancy is discussed in terms of the different frequency response of the probes and their perturbation of the plasma. A simple circuit model of the plasma-probe system has been proposed to explain our results. A brief discussion of the effect of the changing plasma potential distribution on the operation of the magnetron is given

  3. Life test on indigenous s-band pulsed magnetron

    International Nuclear Information System (INIS)

    Wanmode, Y.D.; Shrivastava, P.; Hannurkar, P.R.

    1999-01-01

    A 2 MW S-band pulsed magnetron has been developed under joint collaboration between CAT and CEERI. In this development effort several lab prototypes were evaluated on 2 MW microwave test facility developed at CAT. One magnetron is subjected to life test. The present paper describes the setup and procedures used for life test. Various observations and corrections made during the life tests are also described. Results of the tests are discussed. (author)

  4. High voltage dc cables

    Energy Technology Data Exchange (ETDEWEB)

    Bjustrom, B

    1965-12-01

    How stress distribution in dc cables varies with temperature and stress level, influence of polarity reversals and space charges, and different types of overvoltage to which dc cable may be subjected are discussed. Design problems, especially as related to corrosion protection and to mechanical stress caused by wire armoring during manufacturing and laying, accessories and work done on test methods, and the possibility of designing 400 to 600 kV dc cables for transmitting 2000 to 4000 MW are described.

  5. Inverted relativistic magnetron with a single axial output

    International Nuclear Information System (INIS)

    Ballard, W.P.; Earley, L.M.; Wharton, C.B.

    1986-01-01

    A twelve vane, 1 MV, S-band magnetron has been designed and tested. An inverted design was selected to minimize the parasitic axial electron losses. The stainless steel anode is approximately one wavelength long. One end is partially short-circuited to rf, while the other end has a mode transformer to couple the 3.16 GHz π-mode out into a TM 01 circular waveguide. The magnetron has a loaded output Q of about 100. Operation at 1 MV, 0.31 T, 5 kA routinely produces approx.150 MW peak rms and 100 MW average rms with pulse lengths adjustable from 5 to 70 ns. The microwave power pulse has a rise time of approx.2 ns. The output power is diagnosed using four methods: calorimetry, two circular-waveguide directional couplers installed on the magnetron, two transmitting-receiving systems, and gaseous breakdown. Operation at other voltages and magnetic fields shows that the oscillation frequency is somewhat dependent on the magnetron current. Frequency changes of approx.20 MHz/kA occur as the operating conditions are varied. A series of experiments varying the anode conductivity, the electron emission profile, and the output coupling transformer design showed that none of these significantly increased the output power. Therefore, we have concluded that this magnetron operates in saturation. Because of the anode lifetime and repeatability, this magnetron has the potential to be repetitively pulsed. 36 refs., 16 figs

  6. Family of multiport bidirectional DC-DC converters

    NARCIS (Netherlands)

    Tao, H.; Kotsopoulos, A.; Duarte, J.L.; Hendrix, M.A.M.

    2006-01-01

    Multiport DC-DC converters are of potential interest in applications such as generation systems utilising multiple sustainable energy sources. A family of multiport bidirectional DC-DC converters derived from a general topology is presented. The topology shows a combination of DC-link and magnetic

  7. Programmable dc motor controller

    Science.gov (United States)

    Hopwood, J. E.

    1982-11-01

    A portable programmable dc motor controller, with features not available on commercial instruments was developed for controlling fixtures during welding processes. The controller can be used to drive any dc motor having tachometer feedback and motor requirements not exceeding 30 volts, 3 amperes. Among the controller's features are delayed start time, upslope time, speed, and downslope time.

  8. Multilevel DC link inverter

    Science.gov (United States)

    Su, Gui-Jia

    2003-06-10

    A multilevel DC link inverter and method for improving torque response and current regulation in permanent magnet motors and switched reluctance motors having a low inductance includes a plurality of voltage controlled cells connected in series for applying a resulting dc voltage comprised of one or more incremental dc voltages. The cells are provided with switches for increasing the resulting applied dc voltage as speed and back EMF increase, while limiting the voltage that is applied to the commutation switches to perform PWM or dc voltage stepping functions, so as to limit current ripple in the stator windings below an acceptable level, typically 5%. Several embodiments are disclosed including inverters using IGBT's, inverters using thyristors. All of the inverters are operable in both motoring and regenerating modes.

  9. Development of new cylindrical magnetrons for industrial use

    International Nuclear Information System (INIS)

    Clayton, B.

    2000-09-01

    A number of alternative techniques were considered and tested with a view to the construction of a cylindrical sputtering device. This device was required to be capable of depositing tribological coatings inside approximately cylindrical substrates of diameters less than 100mm, in an industrial situation. A cylindrical magnetron device was designed, and constructed as a prototype, using a magnetic assembly inside a cylindrical target with outside diameter (o.d.) 40mm. Two alternative magnetic assemblies were tested, and found to have complimentary advantages. The magnetron characteristics of the device were tested, as were key properties (such as adhesion level and hardness) of the coatings deposited. In all cases good results were obtained. A 22mm o.d. device based on the same design was shown to operate, but with less satisfactory characteristics. In an attempt to improve the miniaturised design, the feasibility of gas cooling (rather than water cooling) the cylindrical magnetron was demonstrated. A system incorporating four 40mm o.d. cylindrical magnetrons was designed, constructed and briefly tested. This was intended to prove the feasibility of using a multi-magnetron system to reduce the cost to coat. Its dimensions and design were tailored to an industrially specified engine block. In use the plasma rings formed on the 40mm magnetron target surfaces during operation were found to be of unequal intensities, especially on the shorter magnetron design used in the four-fold system. In an attempt to tackle this problem, a finite element model of the magnetic field generated by the magnetic assembly was built, run and verified. Changes were made to this model, and a new .magnet assembly was built and tested based on the results obtained. This did not lead to a final solution of the problem, but has set bounds within which the solution must lie. (author)

  10. Evolution of film temperature during magnetron sputtering

    International Nuclear Information System (INIS)

    Shaginyan, L.R.; Han, J.G.; Shaginyan, V.R.; Musil, J.

    2006-01-01

    We report on the results of measurements of the temperature T F surf which developed on the surface of films deposited by magnetron sputtering of chromium and copper targets on cooling and non-cooling silicon substrates. The T F surf and substrate temperature (T s ) were simultaneously measured using high-resolution IR camera and thermocouple, respectively. We revealed that the T F surf steeply grows, keeps constant when it achieves saturation level, and rapidly drops to the value of the T s after stopping the deposition. At the same time, the T s either does not change for the case of cooling substrate or increases to a certain level for noncooling substrate. However, in both cases the T s remains several times lower than the T F surf . The T F surf is proportional to the flux of energy delivered to the growth surface by sputtered atoms and other fast particles, weakly depends on the depositing metal and can achieve several hundreds of deg. C. This phenomenon is explained by a model assuming formation of a hot thin surface layer (HTSL) on the top of the growing film, which exists only during film deposition and exhibits extremely low thermal conductivity. Due to this unique property the temperature T F surf of HTSL is several times higher than the T s . Variations in the T F surf fairly correlate with structure changes of Cr films along thickness investigated in detail previously

  11. Magnetron sputtered Hf-B-Si-C-N films with controlled electrical conductivity and optical transparency, and with ultrahigh oxidation resistance

    Czech Academy of Sciences Publication Activity Database

    Šímová, V.; Vlček, J.; Zuzjaková, Š.; Houška, J.; Shen, Y.; Jiang, J. C.; Meletis, E. I.; Peřina, Vratislav

    2018-01-01

    Roč. 653, č. 5 (2018), s. 333-340 ISSN 0040-6090 R&D Projects: GA MŠk LM2015056 Institutional support: RVO:61389005 Keywords : Hf-B-Si-C-N films * pulsed reactive magnetron sputtering * electrical conductivitiy * optical transparency * high-temperature oxidation resistance Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders OBOR OECD: Nuclear physics Impact factor: 1.879, year: 2016

  12. Characteristics of a-IGZO/ITO hybrid layer deposited by magnetron sputtering.

    Science.gov (United States)

    Bang, Joon-Ho; Park, Hee-Woo; Cho, Sang-Hyun; Song, Pung-Keun

    2012-04-01

    Transparent a-IGZO (In-Ga-Zn-O) films have been actively studied for use in the fabrication of high-quality TFTs. In this study, a-IGZO films and a-IGZO/ITO double layers were deposited by DC magnetron sputtering under various oxygen flow rates. The a-IGZO films showed an amorphous structure up to 500 degrees C. The deposition rate of these films decreased with an increase in the amount of oxygen gas. The amount of indium atoms in the film was confirmed to be 11.4% higher than the target. The resistivity of double layer follows the rules for parallel DC circuits The maximum Hall mobility of the a-IGZO/ITO double layers was found to be 37.42 cm2/V x N s. The electrical properties of the double layers were strongly dependent on their thickness ratio. The IGZO/ITO double layer was subjected to compressive stress, while the ITO/IGZO double layer was subjected to tensile stress. The bending tolerance was found to depend on the a-IGZO thickness.

  13. Characterization and device applications of ZnO films deposited by high power impulse magnetron sputtering (HiPIMS)

    Science.gov (United States)

    Partridge, J. G.; Mayes, E. L. H.; McDougall, N. L.; Bilek, M. M. M.; McCulloch, D. G.

    2013-04-01

    ZnO films have been reactively deposited on sapphire substrates at 300 °C using a high impulse power magnetron sputtering deposition system and characterized structurally, optically and electronically. The unintentionally doped n-type ZnO films exhibit high transparency, moderate carrier concentration (˜5 × 1018 cm-3) and a Hall mobility of 8.0 cm2 V-1 s-1, making them suitable for electronic device applications. Pt/ZnO Schottky diodes formed on the HiPIMS deposited ZnO exhibited rectification ratios up to 104 at ±2 V and sensitivity to UV light.

  14. Bidirectional dc-to-dc Power Converter

    Science.gov (United States)

    Griesbach, C. R.

    1986-01-01

    Solid-state, series-resonant converter uses high-voltage thyristors. Converter used either to convert high-voltage, low-current dc power to lowvoltage, high current power or reverse. Taking advantage of newly-available high-voltage thyristors to provide better reliability and efficiency than traditional converters that use vacuum tubes as power switches. New converter essentially maintenance free and provides greatly increased mean time between failures. Attractive in industrial applications whether or not bidirectional capability is required.

  15. Tribological characterization of TiN coatings prepared by magnetron sputtering

    Science.gov (United States)

    Makwana, Nishant S.; Chauhan, Kamlesh V.; Sonera, Akshay L.; Chauhan, Dharmesh B.; Dave, Divyeshkumar P.; Rawal, Sushant K.

    2018-05-01

    Titanium nitride (TiN) coating deposited on aluminium and brass pin substrates using RF reactive magnetron sputtering. The structural properties and surface morphology were characterized by X-ray diffraction (XRD), atomic force microscope (AFM) and field emission scanning electron microscope (FE-SEM). There was formation of (101) Ti2N, (110) TiN2 and (102) TiN0.30 peaks at 3.5Pa, 2Pa and 1.25Pa sputtering pressure respectively. The tribological properties of coating were inspected using pin on disc tribometer equipment. It was observed that TiN coated aluminium and brass pins demonstrated improved wear resistance than uncoated aluminium and brass pins.

  16. Synthesis of ReN3 Thin Films by Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    G. Soto

    2014-01-01

    Full Text Available In this work ReNx films were prepared by reactive magnetron sputtering at room temperature and deposited on a silicon wafer. It was found that the diffractograms of the nitrogen-rich rhenium film are consistent with those produced by high-pressure high-temperature methods, under the assumption that the film is oriented on the substrate. Using density functional calculations it was found that the composition of this compound could be ReN3, instead of ReN2, as stated on previous works. The ReN3 compound fits in the Ama2 (40 orthorhombic space group, and due to the existence of N3 anions between Re layers it should be categorized as an azide. The material is exceptionally brittle and inherently unstable under indentation testing.

  17. Optical properties of ITO films obtained by high-frequency magnetron sputtering with accompanying ion treatment

    Energy Technology Data Exchange (ETDEWEB)

    Krylov, P. N., E-mail: ftt@uni.udm.ru; Zakirova, R. M.; Fedotova, I. V. [Udmurt State University (Russian Federation)

    2013-10-15

    A variation in the properties of indium-tin-oxide (ITO) films obtained by the method of reactive magnetron sputtering with simultaneous ion treatment is reported. The ITO films feature the following parameters in the optical range of 450-1100 nm: a transmission coefficient of 80%, band gap of 3.50-3.60 eV, and a refractive index of 1.97-2.06. All characteristics of the films depend on the ion-treatment current. The latter, during the course of deposition, reduces the resistivity of the ITO films with the smallest value of the resistivity being equal to 2 Multiplication-Sign 10{sup -3} {Omega} cm. The degradation of films with a high resistivity when kept in air is observed.

  18. Direct current magnetron sputtering deposition of InN thin films

    International Nuclear Information System (INIS)

    Cai Xingmin; Hao Yanqing; Zhang Dongping; Fan Ping

    2009-01-01

    In this paper, InN thin films were deposited on Si (1 0 0) and K9 glass by reactive direct current magnetron sputtering. The target was In metal with the purity of 99.999% and the gases were Ar (99.999%) and N 2 (99.999%). The properties of InN thin films were studied. Scanning electron microscopy (SEM) shows that the film surface is very rough and energy dispersive X-ray spectroscopy (EDX) shows that the film contains In, N and very little O. X-ray diffraction (XRD) and Raman scattering reveal that the film mainly contains hexagonal InN. The four-probe measurement shows that InN film is conductive. The transmission measurement demonstrates that the transmission of InN deposited on K9 glass is as low as 0.5% from 400 nm to 800 nm.

  19. A DC Transformer

    Data.gov (United States)

    National Aeronautics and Space Administration — The goal of the project was to demonstrate a true direct current (DC) transformer, a new electro-mechanical component with potentially high power applications; in...

  20. Influence of Magnetron Effect on Barium Hexaferrite Thin Layers

    International Nuclear Information System (INIS)

    Hassane, H.; Chatelon, J.P.; Rousseau, J.J; Siblini, A.; Kriga, A.

    2011-01-01

    In this paper, we study the effects of a magnet, located in the cathode, on barium hexaferrite thin films deposited by RF magnetron sputtering technique. During the process, these effects can modify thickness, roughness and stress of coatings. The characteristics of the deposited layers depend on the substrate position that is located opposite of magnetron cathode. In the m agnetron area , one can observe that the high stress can produce cracks or detachment of layers and the increasing of both depositing rate and surface roughness. After sputtering elaboration, barium hexaferrite films are in a compressive stress mode. But, after the post-deposition heat treatment these films are in a tensile stress mode. To improve the quality of BaM films, the subsrtate has to be set outside the magnetron area. (author)

  1. Very low pressure high power impulse triggered magnetron sputtering

    Science.gov (United States)

    Anders, Andre; Andersson, Joakim

    2013-10-29

    A method and apparatus are described for very low pressure high powered magnetron sputtering of a coating onto a substrate. By the method of this invention, both substrate and coating target material are placed into an evacuable chamber, and the chamber pumped to vacuum. Thereafter a series of high impulse voltage pulses are applied to the target. Nearly simultaneously with each pulse, in one embodiment, a small cathodic arc source of the same material as the target is pulsed, triggering a plasma plume proximate to the surface of the target to thereby initiate the magnetron sputtering process. In another embodiment the plasma plume is generated using a pulsed laser aimed to strike an ablation target material positioned near the magnetron target surface.

  2. RF Magnetron Sputtering Deposited W/Ti Thin Film For Smart Window Applications

    Science.gov (United States)

    Oksuz, Lutfi; Kiristi, Melek; Bozduman, Ferhat; Uygun Oksuz, Aysegul

    2014-10-01

    Electrochromic (EC) devices can change reversible and persistent their optical properties in the visible region (400-800 nm) upon charge insertion/extraction according to the applied voltage. A complementary type EC is a device containing two electrochromic layers, one of which is anodically colored such as vanadium oxide (V2 O5) while the other cathodically colored such as tungsten oxide (WO3) which is separated by an ionic conduction layer (electrolyte). The use of a solid electrolyte such as Nafion eliminates the need for containment of the liquid electrolyte, which simplifies the cell design, as well as improves safety and durability. In this work, the EC device was fabricated on a ITO/glass slide. The WO3-TiO2 thin film was deposited by reactive RF magnetron sputtering using a 2-in W/Ti (9:1%wt) target with purity of 99.9% in a mixture gas of argon and oxygen. As a counter electrode layer, V2O5 film was deposited on an ITO/glass substrate using V2O3 target with the same conditions of reactive RF magnetron sputtering. Modified Nafion was used as an electrolyte to complete EC device. The transmittance spectra of the complementary EC device was measured by optical spectrophotometry when a voltage of +/-3 V was applied to the EC device by computer controlled system. The surface morphology of the films was characterized by scanning electron microscopy (SEM) and atomic force microscopy (AFM) (Fig. 2). The cyclic voltammetry (CV) for EC device was performed by sweeping the potential between +/-3 V at a scan rate of 50 mV/s.

  3. REACTIVE POWER DEVICES IN SYSTEMS OF ELECTRIC TRACTION

    Directory of Open Access Journals (Sweden)

    M. O. Kostin

    2010-04-01

    Full Text Available A comparative characteristic of different concepts and expressions for determination of reactive power in the circuits with non-sinusoidal electric values has been given. For the first Ukrainian electric locomotives of DE1 type with the system of DC electric traction, the values of reactive power after Budeany, Fryze, and also the differential, integral and generalized reactive powers have been determined. Some measures on reducing its consumption by the DC electric rolling stock have been suggested.

  4. Three new DC-to-DC Single-Switch Converters

    Directory of Open Access Journals (Sweden)

    Barry W. Williams

    2017-06-01

    Full Text Available This paper presents a new family of three previously unidentified dc-to-dc converters, buck, boost, and buck-boost voltage-transfer-function topologies, which offer advantageous transformer coupling features and low capacitor dc voltage stressing. The three single-switch, single-diode, converters offer the same features as basic dc-to-dc converters, such as the buck function with continuous output current and the boost function with continuous input current. Converter time-domain simulations and experimental results (including transformer coupling support and extol the dc-to-dc converter concepts and analysis presented.

  5. High-current magnetron discharge with magnetic insulation of anode

    International Nuclear Information System (INIS)

    Bizyukov, A.A.; Sereda, K.N.; Sleptsov, V.V.

    2008-01-01

    In magnetron discharge at currents higher then critical which magnitude is in the range of 15...30 A the transition from glow discharge in transverse magnetic field to arc discharge occurs. In the present time the problem of arc blowout is solved at the expense of pulse and HF power supply applying. In this paper the alternative method of limiting current of magnetron discharge increasing at the expense of increasing of discharge gap resistance by means of additional anode layer transverse magnetic field and arc current interruption by sectioning of current collector of anode surface is carrying out

  6. Nanoporous zinc oxide films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Ghimpu, L.; Lupan, O.; Popescu, L.; Tiginyanu, I.M.

    2011-01-01

    In this paper we demonstrate an inexpensive approach for the fabrication of nanoporous zinc oxide films by using magnetron sputtering. Study of the structural properties proves the crystallographic perfection of porous nanostructures and the possibility of its controlling by adjusting the technological parameters in the growth process. The XRD pattern of nanoporous ZnO films exhibits high intensity of the peaks relative to the background signal which is indicative of the ZnO hexagonal phase and a good crystallinity of the samples grown by magnetron sputtering.

  7. Plasma diagnostics during magnetron sputtering of aluminum doped zinc oxide

    DEFF Research Database (Denmark)

    Stamate, Eugen; Crovetto, Andrea; Sanna, Simone

    2016-01-01

    Plasma parameters during magnetron sputtering of aluminum-doped zinc oxide are investigated with optical emission spectroscopy, electrostatic probes and mass spectrometry with the aim of understanding the role of negative ions of oxygen during the film growth and improving the uniformity of the f......Plasma parameters during magnetron sputtering of aluminum-doped zinc oxide are investigated with optical emission spectroscopy, electrostatic probes and mass spectrometry with the aim of understanding the role of negative ions of oxygen during the film growth and improving the uniformity...

  8. Structure and morphology of magnetron sputter deposited ultrathin ZnO films on confined polymeric template

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Ajaib [Discipline of Metallurgy Engineering and Materials Science, Indian Institute of Technology Indore, Indore 453552 (India); Schipmann, Susanne [II. Insatitute of Physics and JARA-FIT, RWTH Aachen University, 52056 Aachen (Germany); Mathur, Aakash; Pal, Dipayan [Discipline of Metallurgy Engineering and Materials Science, Indian Institute of Technology Indore, Indore 453552 (India); Sengupta, Amartya [Department of Physics, Indian Institute of Technology Delhi, Delhi 110016 (India); Klemradt, Uwe [II. Insatitute of Physics and JARA-FIT, RWTH Aachen University, 52056 Aachen (Germany); Chattopadhyay, Sudeshna, E-mail: sudeshna@iiti.ac.in [Discipline of Metallurgy Engineering and Materials Science, Indian Institute of Technology Indore, Indore 453552 (India); Discipline of Physics, Indian Institute of Technology Indore, Indore 453552 (India); Centre for Biosciences and Biomedical Engineering, Indian Institute of Technology Indore, Indore 453552 (India)

    2017-08-31

    Highlights: • Ultra-thin ZnO films grown on confined polymeric (polystyrene, PS) template. • XRR and GISAXS explore the surface/interfaces structure and morphology of ZnO/PS. • Insights into the growth mechanism of magnetron sputtered ZnO thin film on PS template. • Nucleated disk-like cylindrical particles are the basis of the formation of ZnO layers. • Effect of ZnO film thickness on room temperature PL spectra in ZnO/PS systems. - Abstract: The structure and morphology of ultra-thin zinc oxide (ZnO) films with different film thicknesses on confined polymer template were studied through X-ray reflectivity (XRR) and grazing incidence small angle X-ray scattering (GISAXS). Using magnetron sputter deposition technique ZnO thin films with different film thicknesses (<10 nm) were grown on confined polystyrene with ∼2R{sub g} film thickness, where R{sub g} ∼ 20 nm (R{sub g} is the unperturbed radius of gyration of polystyrene, defined by R{sub g} = 0.272 √M{sub 0}, and M{sub 0} is the molecular weight of polystyrene). The detailed internal structure, along the surface/interfaces and the growth direction of the system were explored in this study, which provides insight into the growth procedure of ZnO on confined polymer and reveals that a thin layer of ZnO, with very low surface and interface roughness, can be grown by DC magnetron sputtering technique, with approximately full coverage (with bulk like electron density) even in nm order of thickness, in 2–7 nm range on confined polymer template, without disturbing the structure of the underneath template. The resulting ZnO-polystyrene hybrid systems show strong ZnO near band edge (NBE) and deep-level (DLE) emissions in their room temperature photoluminescence spectra, where the contribution of DLE gets relatively stronger with decreasing ZnO film thickness, indicating a significant enhancement of surface defects because of the greater surface to volume ratio in thinner films.

  9. DC Collection Network Simulation for Offshore Wind Farms

    DEFF Research Database (Denmark)

    Vogel, Stephan; Rasmussen, Tonny Wederberg; El-Khatib, Walid Ziad

    2015-01-01

    The possibility to connect offshore wind turbines with a collection network based on Direct Current (DC), instead of Alternating Current (AC), gained attention in the scientific and industrial environment. There are many promising properties of DC components that could be beneficial such as......: smaller dimensions, less weight, fewer conductors, no reactive power considerations, and less overall losses due to the absence of proximity and skin effects. This work describes a study about the simulation of a Medium Voltage DC (MVDC) grid in an offshore wind farm. Suitable converter concepts...

  10. A Secondary Voltage Control Method for an AC/DC Coupled Transmission System Based on Model Predictive Control

    DEFF Research Database (Denmark)

    Xu, Fengda; Guo, Qinglai; Sun, Hongbin

    2015-01-01

    For an AC/DC coupled transmission system, the change of transmission power on the DC lines will significantly influence the AC systems’ voltage. This paper describes a method to coordinated control the reactive power of power plants and shunt capacitors at DC converter stations nearby, in order t...

  11. Origin of stress in radio frequency magnetron sputtered zinc oxide thin films

    International Nuclear Information System (INIS)

    Menon, Rashmi; Gupta, Vinay; Sreenivas, K.; Tan, H. H.; Jagadish, C.

    2011-01-01

    Highly c-axis oriented ZnO thin films have been deposited on silicon substrates by planar rf magnetron sputtering under varying pressure (10-50 mTorr) and oxygen percentage (50-100%) in the reactive gas (Ar + O 2 ) mixture. The as-grown films were found to be stressed over a wide range from -1 x 10 11 to -2 x 10 8 dyne/cm 2 that in turn depends strongly on the processing conditions, and the film becomes stress free at a unique combination of sputtering pressure and reactive gas composition. Raman spectroscopy and photoluminescence (PL) analyses identified the origin of stress as lattice distortion due to defects introduced in the ZnO thin film. FTIR study reveals that Zn-O bond becomes stronger with the increase in oxygen fraction in the reactive gas mixture. The lattice distortion or stress depends on the type of defects introduced during deposition. PL spectra show the formation of a shoulder in band emission with an increase in the processing pressure and are related to the presence of stress. The ratio of band emission to defect emission decreases with the increase in oxygen percentage from 50 to 100%. The studies show a correlation of stress with the structural, vibrational, and photoluminescence properties of the ZnO thin film. The systematic study of the stress will help in the fabrication of efficient devices based on ZnO film.

  12. Plasma kinetics of Ar/O2 magnetron discharge by two-dimensional multifluid modeling

    International Nuclear Information System (INIS)

    Costin, C.; Minea, T. M.; Popa, G.; Gousset, G.

    2010-01-01

    Multifluid two-dimensional model was developed to describe the plasma kinetics of the direct current Ar/O 2 magnetron, coupling two modules: charged particles and neutrals. The first module deals with three positive ions - Ar + , O 2 + , and O + - and two negative species - e - and O - - treated by the moments of Boltzmann's equation. The second one follows seven neutral species (Ar, O 2 , O, O 3 , and related metastables) by the multicomponent diffusion technique. The two modules are self-consistently coupled by the mass conservation and kinetic coefficients taking into account more than 100 volume reactions. The steady state is obtained when the overall convergence is achieved. Calculations for 10%O 2 in Ar/O 2 mixture at 2.67 and 4 Pa show that the oxygen excited species are mainly created by electron collisions in the negative glow of the discharge. Decreasing the pressure down to 0.67 Pa, the model reveals the nonlocal behavior of the reactive species. The density gradient of O 2 ground state is reversed with respect to all gradients of the other reactive species, since the latter ones originate from the molecular ground state of oxygen. It is also found that the wall reactions drastically modify the space gradient of neutral reactive species, at least as much as the pressure, even if the discharge operates in compound mode.

  13. Plasma kinetics of Ar/O{sub 2} magnetron discharge by two-dimensional multifluid modeling

    Energy Technology Data Exchange (ETDEWEB)

    Costin, C.; Minea, T. M.; Popa, G.; Gousset, G. [LPGP, UMR 8578, CNRS-Paris-Sud XI University, Bat. 210, Orsay Cedex 91405, France and Faculty of Physics, Al. I. Cuza University, 11 Carol I Blvd., Iasi 700506 (Romania); LPGP, UMR 8578, CNRS-Paris-Sud XI University, Bat. 210, Orsay Cedex 91405 (France); Faculty of Physics, Al. I. Cuza University, 11 Carol I Blvd., Iasi 700506 (Romania); LPGP, UMR 8578, CNRS-Paris-Sud XI University, Bat. 210, Orsay Cedex 91405 (France)

    2010-03-15

    Multifluid two-dimensional model was developed to describe the plasma kinetics of the direct current Ar/O{sub 2} magnetron, coupling two modules: charged particles and neutrals. The first module deals with three positive ions - Ar{sup +}, O{sub 2}{sup +}, and O{sup +} - and two negative species - e{sup -} and O{sup -} - treated by the moments of Boltzmann's equation. The second one follows seven neutral species (Ar, O{sub 2}, O, O{sub 3}, and related metastables) by the multicomponent diffusion technique. The two modules are self-consistently coupled by the mass conservation and kinetic coefficients taking into account more than 100 volume reactions. The steady state is obtained when the overall convergence is achieved. Calculations for 10%O{sub 2} in Ar/O{sub 2} mixture at 2.67 and 4 Pa show that the oxygen excited species are mainly created by electron collisions in the negative glow of the discharge. Decreasing the pressure down to 0.67 Pa, the model reveals the nonlocal behavior of the reactive species. The density gradient of O{sub 2} ground state is reversed with respect to all gradients of the other reactive species, since the latter ones originate from the molecular ground state of oxygen. It is also found that the wall reactions drastically modify the space gradient of neutral reactive species, at least as much as the pressure, even if the discharge operates in compound mode.

  14. Origin of stress in radio frequency magnetron sputtered zinc oxide thin films

    Science.gov (United States)

    Menon, Rashmi; Gupta, Vinay; Tan, H. H.; Sreenivas, K.; Jagadish, C.

    2011-03-01

    Highly c-axis oriented ZnO thin films have been deposited on silicon substrates by planar rf magnetron sputtering under varying pressure (10-50 mTorr) and oxygen percentage (50-100%) in the reactive gas (Ar + O2) mixture. The as-grown films were found to be stressed over a wide range from -1 × 1011 to -2 × 108 dyne/cm2 that in turn depends strongly on the processing conditions, and the film becomes stress free at a unique combination of sputtering pressure and reactive gas composition. Raman spectroscopy and photoluminescence (PL) analyses identified the origin of stress as lattice distortion due to defects introduced in the ZnO thin film. FTIR study reveals that Zn-O bond becomes stronger with the increase in oxygen fraction in the reactive gas mixture. The lattice distortion or stress depends on the type of defects introduced during deposition. PL spectra show the formation of a shoulder in band emission with an increase in the processing pressure and are related to the presence of stress. The ratio of band emission to defect emission decreases with the increase in oxygen percentage from 50 to 100%. The studies show a correlation of stress with the structural, vibrational, and photoluminescence properties of the ZnO thin film. The systematic study of the stress will help in the fabrication of efficient devices based on ZnO film.

  15. Three-port DC-DC converter with new integrated transformer for DC Distribution Systems

    DEFF Research Database (Denmark)

    Ouyang, Ziwei; Andersen, Michael A. E.

    2014-01-01

    A new integrated transformer for three-port dc-dc converter is proposed to overcome the power coupling effect existed in some known multiple inputs dc-dc converters. Orthogonal primary windings arrangement and in series connection of diagonal secondary Windings enables a fully power decoupling...

  16. 75 FR 23571 - Airworthiness Directives; McDonnell Douglas Corporation Model DC-10-10, DC-10-10F, DC-10-15, DC...

    Science.gov (United States)

    2010-05-04

    ... Airworthiness Directives; McDonnell Douglas Corporation Model DC- 10-10, DC-10-10F, DC-10-15, DC-10-30, DC-10... amends Sec. 39.13 by adding the following new AD: 2010-09-12 McDonnell Douglas Corporation: Amendment 39... to McDonnell Douglas Corporation Model DC- 10-10, DC-10-10F, DC-10-15, DC-10-30, DC-10-30F (KC-10A...

  17. Performance Test of the Microwave Ion Source with the Multi-layer DC Break

    International Nuclear Information System (INIS)

    Kim, Dae Il; Kwon, Hyeok Jung; Kim, Han Sung; Seol, Kyung Tae; Cho, Yong Sub

    2012-01-01

    A microwave proton source has been developed as a proton injector for the 100-MeV proton linac of the PEFP (Proton Engineering Frontier Project). On microwave ion source, the high voltage for the beam extraction is applied to the plasma chamber, also to the microwave components such as a 2.45GHz magnetron, a 3-stub tuner, waveguides. If microwave components can be installed on ground side, the microwave ion source can be operated and maintained easily. For the purpose, the multi-layer DC break has been developed. A multi-layer insulation has the arrangement of conductors and insulators as shown in the Fig. 1. For the purpose of stable operation as the multi-layer DC break, we checked the radiation of the insulator depending on materials and high voltage test of a fabricated multi-layer insulation. In this report, the details of performance test of the multi-layer DC break will be presented

  18. Variable Power, Short Microwave Pulses Generation using a CW Magnetron

    Directory of Open Access Journals (Sweden)

    CIUPA, R.

    2011-05-01

    Full Text Available Fine control of microwave power radiation in medical and scientific applications is a challenging task. Since a commercial Continuous Wave (CW magnetron is the most inexpensive microwave device available today on the market, it becomes the best candidate for a microwave power generator used in medical diathermy and hyperthermia treatments or high efficiency chemical reactions using microwave reactors as well. This article presents a new method for driving a CW magnetron with short pulses, using a modified commercial Zero Voltage Switching (ZVS inverter, software driven by a custom embedded system. The microwave power generator designed with this method can be programmed for output microwave pulses down to 1% of the magnetron's power and allows microwave low frequency pulse modulation in the range of human brain electrical activity, intended for medical applications. Microwave output power continuous control is also possible with the magnetron running in the oscillating area, using a dual frequency Pulse Width Modulation (PWM, where the low frequency PWM pulse is modulating a higher resonant frequency required by the ZVS inverter's transformer. The method presented allows a continuous control of both power and energy (duty-cycle at the inverter's output.

  19. Geometrical Aspects of a Hollow-cathode Magnetron (HCM)

    International Nuclear Information System (INIS)

    Cohen, Samuel A.; Wang, Zhehui

    1998-01-01

    A hollow-cathode magnetron (HCM), built by surrounding a planar sputtering-magnetron cathode with a hollow-cathode structure (HCS), is operable at substantially lower pressures than its planar-magnetron counterpart. We have studied the dependence of magnetron operational parameters on the inner diameter D and length L of a cylindrical HCS. Only when L is greater than L sub zero, a critical length, is the HCM operable in the new low-pressure regime. The critical length varies with HCS inner diameter D. Explanations of the lower operational pressure regime, critical length, and plasma shape are proposed and compared with a one-dimension diffusion model for energetic or primary electron transport. At pressures above 1 mTorr, an electron-impact ionization model with Bohm diffusion at a temperature equivalent to one-half the primary electron energy and with an ambipolar constraint can explain the ion-electron pair creation required to sustain the discharge. The critical length L sub zero is determined by the magnetization length of the primary electrons

  20. Operational experience with the BNL magnetron H- source

    International Nuclear Information System (INIS)

    Witkover, R.L.

    1983-01-01

    A magnetron H - source with a grooved cathode has been in operation at the BNL Linac for over 18 months. The source has run at 5 pps with a 600 μsec pulse width for periods as long as 5 months. Its development and performance will be discussed

  1. Spatiotemporal synchronization of drift waves in a magnetron sputtering plasma

    Czech Academy of Sciences Publication Activity Database

    Martines, E.; Zuin, M.; Cavazzana, R.; Adámek, Jiří; Antoni, V.; Serianni, G.; Spolaore, M.; Vianello, N.

    2014-01-01

    Roč. 21, č. 10 (2014), s. 102309-102309 ISSN 1070-664X Institutional support: RVO:61389021 Keywords : Drift waves * Magnetron sputtering plasma * Spatiotemporal synchronization Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 2.142, year: 2014 http://dx.doi.org/10.1063/1.4898693

  2. Design and Testing of Boost Type DC/DC Converter for DC Motor Control Applications

    OpenAIRE

    Samman, Faizal Arya; Akil, Yusri Syam; Noor, Nirwan A.

    2017-01-01

    in The Proceeding of The 2nd International Symposium on Smart Material and Mechatronics 2015 This paper presents the design and testing of a boost type DC/DC converter circuit, which can be used for DC motor control applications. The Boost converter is designed using DC chopper and DC chopper cascade configurations. The experimental setup was made by connecting the boost converter circuit with four types of DC motor, i.e. self-excited DC motor shunt, series, compound and separately exci...

  3. Control of improved full-bridge three-level DC/DC converter for wind turbines in a DC grid

    DEFF Research Database (Denmark)

    Deng, Fujin; Chen, Zhe

    2013-01-01

    transformer in the IFBTL dc/dc converter. A modulation strategy, including two operation modes, is proposed for the IFBTL dc/dc converter. Then, a voltage balancing control strategy is proposed for the IFBTL dc/dc converter. Furthermore, the control of the wind turbine based on the IFBTL dc/dc converter......This paper presents an improved full-bridge three-level (IFBTL) dc/dc converter for a wind turbine in a dc grid by inserting a passive filter into the dc/dc converter to improve the performance of the converter. The passive filter can effectively reduce the voltage stress of the medium frequency...

  4. Overview of Multi-DC-Bus Solutions for DC Microgrids

    DEFF Research Database (Denmark)

    Ricchiuto, D.; Mastromauro, R.A.; Liserre, Marco

    2013-01-01

    DC Microgrids have recently received a lot of attention in the last years due to high penetration of renewable energy sources as well as distributed energy storage systems. In the future DC microgrids could be preferable respect to AC microgrids in terms of redundancy since multi-DC-Bus solutions...... could provide a continuative power supply to the loads. An overview of Multi-DC-Bus solutions is presented in this paper. The performances are compared on the basis of possible DC microgrid configurations, redundancy, different DC voltage levels....

  5. Adhesion Improvement and Characterization of Magnetron Sputter Deposited Bilayer Molybdenum Thin Films for Rear Contact Application in CIGS Solar Cells

    Directory of Open Access Journals (Sweden)

    Weimin Li

    2016-01-01

    Full Text Available Molybdenum (Mo thin films are widely used as rear electrodes in copper indium gallium diselenide (CIGS solar cells. The challenge in Mo deposition by magnetron sputtering lies in simultaneously achieving good adhesion to the substrates while retaining the electrical and optical properties. Bilayer Mo films, comprising five different thickness ratios of a high pressure (HP deposited bottom layer and a low pressure (LP deposited top layer, were deposited on 40 cm × 30 cm soda-lime glass substrates by DC magnetron sputtering. We focus on understanding the effects of the individual layer properties on the resulting bilayer Mo films, such as microstructure, surface morphology, and surface oxidation. We show that the thickness of the bottom HP Mo layer plays a major role in determining the micromechanical and physical properties of the bilayer Mo stack. Our studies reveal that a thicker HP Mo bottom layer not only improves the adhesion of the bilayer Mo, but also helps to improve the film crystallinity along the preferred [110] direction. However, the surface roughness and the porosity of the bilayer Mo films are found to increase with increasing bottom layer thickness, which leads to lower optical reflectance and a higher probability for oxidation at the Mo surface.

  6. Modeling and experimental studies of a side band power re-injection locked magnetron

    Science.gov (United States)

    Ye, Wen-Jun; Zhang, Yi; Yuan, Ping; Zhu, Hua-Cheng; Huang, Ka-Ma; Yang, Yang

    2016-12-01

    A side band power re-injection locked (SBPRIL) magnetron is presented in this paper. A tuning stub is placed between the external injection locked (EIL) magnetron and the circulator. Side band power of the EIL magnetron is reflected back to the magnetron. The reflected side band power is reused and pulled back to the central frequency. A phase-locking model is developed from circuit theory to explain the process of reuse of side band power in SBPRIL magnetron. Theoretical analysis proves that the side band power is pulled back to the central frequency of the SBPRIL magnetron, then the amplitude of the RF voltage increases and the phase noise performance is improved. Particle-in-cell (PIC) simulation of a 10-vane continuous wave (CW) magnetron model is presented. Computer simulation predicts that the frequency spectrum’s peak of the SBPRIL magnetron has an increase of 3.25 dB compared with the free running magnetron. The phase noise performance at the side band offset reduces 12.05 dB for the SBPRIL magnetron. Besides, the SBPRIL magnetron experiment is presented. Experimental results show that the spectrum peak rises by 14.29% for SBPRIL magnetron compared with the free running magnetron. The phase noise reduces more than 25 dB at 45-kHz offset compared with the free running magnetron. Project supported by the National Basic Research Program of China (Grant No. 2013CB328902) and the National Natural Science Foundation of China (Grant No. 61501311).

  7. Internal stress and opto-electronic properties of ZnO thin films deposited by reactive sputtering in various oxygen partial pressures

    Science.gov (United States)

    Tuyaerts, Romain; Poncelet, Olivier; Raskin, Jean-Pierre; Proost, Joris

    2017-10-01

    In this article, we propose ZnO thin films as a suitable material for piezoresistors in transparent and flexible electronics. ZnO thin films have been deposited by DC reactive magnetron sputtering at room temperature at various oxygen partial pressures. All the films have a wurtzite structure with a strong (0002) texture measured by XRD and are almost stoichiometric as measured by inductively coupled plasma optical emission spectroscopy. The effect of oxygen concentration on grain growth has been studied by in-situ multi-beam optical stress sensor, showing internal stress going from 350 MPa to -1.1 GPa. The transition between tensile and compressive stress corresponds to the transition between metallic and oxidized mode of reactive sputtering. This transition also induces a large variation in optical properties—from absorbent to transparent, and in the resistivity—from 4 × 10 - 2 Ω .cm to insulating. Finally, the piezoresistance of the thin film has been studied and showed a gauge factor (ΔR/R)/ɛ comprised between -5.8 and -8.5.

  8. Deposition of lead-silicate glassy thin coatings by RF magnetron sputtering: Correlation between deposition parameters and electrical and structural properties

    International Nuclear Information System (INIS)

    Rigato, V.; Maggioni, G.; Boscarino, D.; Della Mea, G.; Univ. di Trento, Mesiano

    1996-01-01

    Lead-silicate glassy thin films produced by means of Reactive Radio Frequency Magnetron Sputtering have found recent application in the development of MicroStrip Gas Chambers radiation detectors. Here, thin films (100--400 nm) of lead silicate glass have been deposited by RF magnetron sputtering in Ar plasma at different discharge conditions. The interaction of the sputtered species with the gas atoms during the transport process through the discharge region and the kinetics of growth of the films have been investigated as a function of the target composition and of the substrate temperature. This study demonstrates the possibility of controlling the surface electrical resistance of the films in a wide range of values ranging from 10 12 to 10 17 Ω/□ during the film growth

  9. Structural study and fabrication of nano-pattern on ultra thin film of Ag grown by magnetron sputtering

    International Nuclear Information System (INIS)

    Banerjee, S.; Mukherjee, S.; Kundu, S.

    2001-01-01

    We present the structural study of ultra thin Ag films using grazing incidence x-ray reflectivity and the modification of these films with the tip of an atomic force microscope. Ag thin films are deposited using dc magnetron sputtering on a Si(001) substrate. Initially, the growth of the film is carpet like and above a certain thickness (∼42 A) the film structure changes to form mounds. This ultra thin film of Ag having carpet-like growth can be modified by the tip of an atomic force microscope, which occurs due to the porous nature of the film. A periodic pattern of nanometer dimensions has been fabricated on this film using the atomic force microscope tip. (author)

  10. Effect of High Temperature Annealing on Conduction-Type ZnO Films Prepared by Direct-Current Magnetron Sputtering

    International Nuclear Information System (INIS)

    Sun Li-Jie; He Dong-Kai; Xu Xiao-Qiu; Zhong Ze; Wu Xiao-Peng; Lin Bi-Xia; Fu Zhu-Xi

    2010-01-01

    We experimentally find that the ZnO thin films deposited by dc-magnetron sputtering have different conduction types after annealing at high temperature in different ambient. Hall measurements show that ZnO films annealed at 1100°C in N 2 and in O 2 ambient become n-type and p-type, respectively. This is due to the generation of different intrinsic defects by annealing in different ambient. X-ray photoelectron spectroscopy and photolumi-nescence measurements indicate that zinc interstitial becomes a main defects after annealing at 1100°C in N 2 ambient, and these defects play an important role for n-type conductivity of ZnO. While the ZnO films annealed at 1100°C in O 2 ambient, the oxygen antisite contributes ZnO films to p-type. (condensed matter: structure, mechanical and thermal properties)

  11. Electrical and optical study of transparent V-based oxide semiconductors prepared by magnetron sputtering under different conditions

    Directory of Open Access Journals (Sweden)

    E. Prociow

    2011-04-01

    Full Text Available This work is focused on structural, optical and electrical behaviors of vanadium-based oxide thin films prepared by magnetron sputtering under different conditions. Thin films have been deposited on glass substrates from metallic vanadium target at low sputtering pressure. Different working gases: argon/oxygen mixture, and especially pure oxygen gas, have been applied. Results of X-ray diffraction together with optical transmission and temperature- dependent electrical resistivity measurements have been presented. Transmission coefficient, cut-off wavelength and the width of the optical band gap have been calculated from optical measurements. The d.c. resistivity values at room temperature and thermal activation energy have been obtained from electrical investigations. The influence of sputtering process conditions on optical and electrical properties has been discussed.

  12. Effect of cesium assistance on the electrical and structural properties of indium tin oxide films grown by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Song, Jaewon; Hwang, Cheol Seong; Park, Sung Jin; Yoon, Neung Ku [Department of Materials Science and Engineering and Inter-university Semiconductor Research Center, Seoul National University, Seoul 151-742 (Korea, Republic of); Sorona Inc., Pyeongtaek, Gyeonggi 451-841 (Korea, Republic of)

    2009-07-15

    Indium tin oxide (ITO) thin films were deposited by cesium (Cs)-assisted dc magnetron sputtering in an attempt to achieve a high performance at low temperatures. The films were deposited on SiO{sub 2}/Si wafer and glass (Eagle 2000) substrates at a substrate temperature of 100 degree sign C with a Cs vapor flow during the deposition process. The ITO thin films deposited in the presence of Cs vapor showed better crystallinity than the control films grown under normal Ar/O{sub 2} plasma conditions. The resistivity of the films with the Cs assistance was lower than that of the control films. The lowest resistivity of 6.2x10{sup -4} {Omega} cm, which is {approx}20% lower than that of the control sample, was obtained without any postdeposition thermal annealing. The surface roughness increased slightly when Cs vapor was added. The optical transmittance was >80% at wavelengths ranging from 380 to 700 nm.

  13. Comparative study of zinc oxide and aluminum doped zinc oxide transparent thin films grown by direct current magnetron sputtering

    International Nuclear Information System (INIS)

    Suchea, M.; Christoulakis, S.; Katsarakis, N.; Kitsopoulos, T.; Kiriakidis, G.

    2007-01-01

    Pure and aluminum (Al) doped zinc oxide (ZnO and ZAO) thin films have been grown using direct current (dc) magnetron sputtering from pure metallic Zn and ceramic ZnO targets, as well as from Al-doped metallic ZnAl2at.% and ceramic ZnAl2at.%O targets at room temperature (RT). The effects of target composition on the film's surface topology, crystallinity, and optical transmission have been investigated for various oxygen partial pressures in the sputtering atmosphere. It has been shown that Al-doped ZnO films sputtered from either metallic or ceramic targets exhibit different surface morphology than the undoped ZnO films, while their preferential crystalline growth orientation revealed by X-ray diffraction remains always the (002). More significantly, Al-doping leads to a larger increase of the optical transmission and energy gap (E g ) of the metallic than of the ceramic target prepared films

  14. Multi Bus DC-DC Converter in Electric Hybrid Vehicles

    Science.gov (United States)

    Krithika, V.; Subramaniam, C.; Sridharan, R.; Geetha, A.

    2018-04-01

    This paper is cotncerned with the design, simulation and fabrication of the prototype of a Multi bus DC- DC converter operating from 42V DC and delivering 14V DC and 260V DC. As a result, three DC buses are interconnected through a single power electronic circuitry. Such a requirement is energized in the development of a hybrid electric automobile which uses the technology of fuel cell. This is implemented by using a Bidirectional DC-DC converter configuration which is ideally suitable for multiple outputs with mutual electrical isolation. For the sake of reduced size and cost of step-up transformer, selection of a high frequency switching cycle at 10 KHz was done.

  15. Temporal evolution of electron energy distribution function and plasma parameters in the afterglow of drifting magnetron plasma

    International Nuclear Information System (INIS)

    Seo, Sang-Hun; In, Jung-Hwan; Chang, Hong-Young

    2005-01-01

    The temporal behaviour of the electron energy distribution function (EEDF) and the plasma parameters such as electron density, electron temperature and plasma and floating potentials in a mid-frequency pulsed dc magnetron plasma are investigated using time-resolved probe measurements. A negative-voltage dc pulse with an average power of 160 W during the pulse-on period, a repetition frequency of 20 kHz and a duty cycle of 50% is applied to the cathode of a planar unbalanced magnetron discharge with a grounded substrate. The measured electron energy distribution is found to exhibit a bi-Maxwellian distribution, which can be resolved with the low-energy electron group and the high-energy tail part during the pulse-on period, and a Maxwellian distribution only with low-energy electrons as a consequence of initially rapid decay of the high-energy tail part during the pulse-off period. This characteristic evolution of the EEDF is reflected in the decay characteristics of the electron density and temperature in the afterglow. These parameters exhibit twofold decay represented by two characteristic decay times of an initial fast decay time τ 1 , and a subsequent slower decay time τ 2 in the afterglow when approximated with a bi-exponential function. While the initial fast decay times are of the order of 1 μs (τ T1 ∼ 0.99 μs and τ N1 ∼ 1.5 μs), the slower decay times are of the order of a few tens of microseconds (τ T2 ∼ 7 μs and τ N2 ∼ 40 μs). The temporal evolution of the plasma parameters are qualitatively explained by considering the formation mechanism of the bi-Maxwellian electron distribution function and the electron transports of these electron groups in bulk plasma

  16. Investigation of the possible technological use of magnetron-synthetic coverings on the basis of niobium nitridium to manufacture high conductivity windings during the generation of power magnetic fields

    International Nuclear Information System (INIS)

    Kadyrzhanov, K.; Zhetbaev, A.; Tuleushev, A.; Penkov, F.; Lisitsin, V.; Kim, S.; Tuleushev, Yu.; Turkebaev, T.; Borisenko, A.; Gorlachev, I.; Platov, A.; Lisuchin, S.; Skoz, E.; Zhukov, V.; Guliykin, Yu.; Chavalinsky, Yu.

    1996-01-01

    The main objective. The objective of this project is to investigate the possibilities for technological use of niobium nitride-based magnetron synthesized coatings for the purpose of manufacture of superconducting tape windings when generating strong magnetic fields for NMR-tomographs and commercial magnets. Background. Niobium nitride can be produced by sputtering as a continuous coating directly on the surface of a substrate made of a normal conductor, e.g. a copper or aluminium thin tape, by well-known techniques of plasma-chemical synthesis, using magnetron procedure (d.c. magnetron), allowing al synthesis, using magnetron procedure (d.c. magnetron), allowing to solve some difficult problems of superconductor manufacture by means of plastic deformation. For example, risk of break of a superconducting thread will no longer arises and the procedure of control for heat removal and relation between the thickness of superconducting and normal components will be made much easier, and, in turn, this enables to enhance stability of superconductivity and to prevent flux quench. Methodology. The group of eleven specialists from NNC RK will be occupied in the magnetron synthesis of niobium nitride coatings of copper and aluminum foils (five persons) and in its X-ray, nuclear-physical and electron microscopic analysis (six persons). The group of six specialists from the ULBA plant will be occupied in determination of the critical parameters of belt samples with niobium nitride coatings produced by Inst. of Nuclear Physics' specialists. Multi-purpose research test benches for determination of superconductor critical parameters that are available at the ULBA enables to test different types superconductor characteristics, including film ones, in magnetic fields up to 11 T at helium temperatures. Expected Results. As the result of the project execution complete evaluation concerning technical reasoning for magnetron ways of coating synthesis of niobium nitride when

  17. Early Oscillation Detection for DC/DC Converter Fault Diagnosis

    Science.gov (United States)

    Wang, Bright L.

    2011-01-01

    The electrical power system of a spacecraft plays a very critical role for space mission success. Such a modern power system may contain numerous hybrid DC/DC converters both inside the power system electronics (PSE) units and onboard most of the flight electronics modules. One of the faulty conditions for DC/DC converter that poses serious threats to mission safety is the random occurrence of oscillation related to inherent instability characteristics of the DC/DC converters and design deficiency of the power systems. To ensure the highest reliability of the power system, oscillations in any form shall be promptly detected during part level testing, system integration tests, flight health monitoring, and on-board fault diagnosis. The popular gain/phase margin analysis method is capable of predicting stability levels of DC/DC converters, but it is limited only to verification of designs and to part-level testing on some of the models. This method has to inject noise signals into the control loop circuitry as required, thus, interrupts the DC/DC converter's normal operation and increases risks of degrading and damaging the flight unit. A novel technique to detect oscillations at early stage for flight hybrid DC/DC converters was developed.

  18. Phase and Frequency Locked Magnetrons for SRF Sources

    Energy Technology Data Exchange (ETDEWEB)

    Neubauer, Michael [Muons, Inc.; Johnson, Rolland

    2014-09-12

    There is great potential for a magnetron power source that can be controlled both in phase and frequency. Such a power source could revolutionize many particle accelerator systems that require lower capital cost and/or higher power efficiency. Beyond the accelerator community, phase and frequency locked magnetons could improve radar systems around the world and make affordable phased arrays for wireless power transmission for solar powered satellites. This joint project of Muons, Inc., Fermilab, and L-3 CTL was supported by an STTR grant monitored by the Nuclear Physics Office of the DOE Office of Science. The object of the program was to incorporate ferrite materials into the anode of a magnetron and, with appropriate biasing of the ferrites, to maintain frequency lock and to allow for frequency adjustment of the magnetron without mechanical tuners. If successful, this device would have a dual use both as a source for SRF linacs and for military applications where fast tuning of the frequency is a requirement. In order to place the materials in the proper location, several attributes needed to be modeled. First the impact of the magnetron’s magnetic field needed to be shielded from the ferrites so that they were not saturated. And second, the magnetic field required to change the frequency of the magnetron at the ferrites needed to be shielded from the region containing the circulating electrons. ANSYS calculations of the magnetic field were used to optimize both of these parameters. Once the design for these elements was concluded, parts were fabricated and a complete test assembly built to confirm the predictions of the computer models. The ferrite material was also tested to determine its compatibility with magnetron tube processing temperatures. This required a vacuum bake out of the chosen material to determine the cleanliness of the material in terms of outgassing characteristics, and a subsequent room temperature test to verify that the characteristics of

  19. Damp heat stability and annealing behavior of aluminum doped zinc oxide films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Tohsophon, T.; Huepkes, J.; Calnan, S.; Reetz, W.; Rech, B.; Beyer, W.; Sirikulrat, N.

    2006-01-01

    The damp heat stability and subsequent vacuum annealing behavior of aluminum doped zinc oxide (AZO) films was investigated using Hall effect measurements, X-ray diffraction (XRD) and optical spectrometry techniques. The AZO films were deposited on glass or silicon wafers using reactive and non-reactive magnetron sputtering from metallic and ceramic targets, respectively. Additionally, we characterized surface textured AZO films, which are used as light scattering transparent conductive oxide (TCO) in silicon thin film solar cells. For all films a degradation of the electrical film properties was found after the damp heat treatment. For thick compact films, with large grain size, only a small increase in the electrical resistivity was observed, whereas less compact films prepared at high deposition pressures or very thin films (< 300 nm) showed an increase in resistivity by up to a factor of three already after 300 h. The conductivity degradation during damp heat treatment could be largely reversed by annealing in vacuum. However, annealing temperatures of at least 150 deg. C were required. Possible mechanisms explaining the experimental results are discussed

  20. TiOx deposited by magnetron sputtering: a joint modelling and experimental study

    Science.gov (United States)

    Tonneau, R.; Moskovkin, P.; Pflug, A.; Lucas, S.

    2018-05-01

    This paper presents a 3D multiscale simulation approach to model magnetron reactive sputter deposition of TiOx⩽2 at various O2 inlets and its validation against experimental results. The simulation first involves the transport of sputtered material in a vacuum chamber by means of a three-dimensional direct simulation Monte Carlo (DSMC) technique. Second, the film growth at different positions on a 3D substrate is simulated using a kinetic Monte Carlo (kMC) method. When simulating the transport of species in the chamber, wall chemistry reactions are taken into account in order to get the proper content of the reactive species in the volume. Angular and energy distributions of particles are extracted from DSMC and used for film growth modelling by kMC. Along with the simulation, experimental deposition of TiOx coatings on silicon samples placed at different positions on a curved sample holder was performed. The experimental results are in agreement with the simulated ones. For a given coater, the plasma phase hysteresis behaviour, film composition and film morphology are predicted. The used methodology can be applied to any coater and any films. This paves the way to the elaboration of a virtual coater allowing a user to predict composition and morphology of films deposited in silico.

  1. RF magnetron sputtered La3+-modified PZT thin films: Perovskite phase stabilization and properties

    International Nuclear Information System (INIS)

    Singh, Ravindra; Goel, T.C.; Chandra, Sudhir

    2008-01-01

    In this work, we report the preparation of lanthanum-modified lead zirconate titanate (PLZT) thin films in pure perovskite phase by RF magnetron sputtering. Various deposition parameters such as target-to-substrate spacing, sputtering gas composition, deposition temperature, post-deposition annealing temperature and time have been optimized to obtain PLZT films in pure perovskite phase. The films prepared in pure argon at 100 W RF power without external substrate heating exhibit pure perovskite phase after rapid thermal annealing (RTA) at 700 deg. C for 5 min. The film prepared at 225 deg. C substrate temperature also exhibits pure perovskite phase after RTA at 700 deg. C for 2 min. SIMS depth profile performed on one of the pure perovskite films (RTA at 700 deg. C for 5 min) shows very good stoichiometric uniformity of all elements of PLZT. The surface morphology of the films was examined using SEM and AFM. The dielectric, ferroelectric and electrical properties of the pure perovskite films were also investigated in detail. The remanent polarization for the films annealed at 700 deg. C for 5 and 2 min were found to be 15 and 13.5 μC cm -2 , respectively. Both the films have high DC resistivity of the order of 10 11 Ω cm at the electric field of ∼80 kV cm -1

  2. Influence of electrochemical pre-treatment on highly reactive carbon nitride thin films deposited on stainless steel for electrochemical applications

    International Nuclear Information System (INIS)

    Benchikh, A.; Debiemme-Chouvy, C.; Cachet, H.; Pailleret, A.; Saidani, B.; Beaunier, L.; Berger, M.H.

    2012-01-01

    In this work, a-CNx films prepared by DC magnetron sputtering on stainless steel substrate have been investigated as electrode materials. While their wide potential window was confirmed as a property shared by boron doped diamond (BDD) electrodes, their electrochemical activity with respect to fast and reversible redox systems, [Ru(NH 3 ) 6 ] 3+/2+ , [Fe(CN) 6 ] 3−/4− and [IrCl 6 ] 2−/3− , was assessed by Electrochemical Impedance Spectroscopy (EIS) after cathodic or anodic electrochemical pre-treatments or for as grown samples. It was shown for the three systems that electrochemical reactivity of the a-CNx films was improved after the cathodic pre-treatment and degraded after the anodic one, the apparent heterogeneous rate constant k 0app being decreased by at least one order of magnitude for the latter case. A high k 0app value of 0.11 cm s −1 for [IrCl 6 ] 2−/3− was obtained, close to the highest values found for BDD electrodes.

  3. Electron energy distribution function in a cathode fall region of DC-glow discharge

    International Nuclear Information System (INIS)

    Elakshar, F.F.; Garamoon, A.A.; Hassouba, M.A.

    1997-01-01

    Recently a substantial effort has been devoted towards the development of a quantitative microscopic measurements in the cathode fall region of the DC-glow discharge magnetron sputtering unit. The electron energy distribution function (EEDF) has been measured using a single Langmuir probe at the edge of the cathode fall. Two groups of electrons are observed in helium and argon gas discharges. The two groups have no chance to be thermalized since they leave the cathode fall region fast. The electron temperature measurements have been compared with spectroscopic determination. Plasma density has been computed and compared with probe measurements. Sources of the two groups of electrons are also discussed. (author)

  4. Thyristors for dc transmission

    Energy Technology Data Exchange (ETDEWEB)

    1966-05-06

    As a first stage towards determining the feasibility of applying thyristors to hvdc converter terminals, the Westinghouse Electric Corporation has built a converter laboratory capable of testing thyristors under conditions similar to those which would have to be met in a 200 kV dc system. The equipment has been designed to test a 5 kV 600 A group of thyrisotrs, elevated 200 kV above earth. This rating has been chosen so that there would be a sufficient number of thyristors in series to enable the gating and voltage division characteristics to be investigated and at the same time the group could be operated at a potential equivalent to a complete 200 kV dc bridge.

  5. TOPOLOGICAL REVIEW AND ANALYSIS OF DC-DC BOOST CONVERTERS

    Directory of Open Access Journals (Sweden)

    V. INDRA GANDHI

    2017-06-01

    Full Text Available DC voltage boost up is essential in numerous applications; especially considering Photovoltaic (PV based renewable power generation system. The conventional DC-DC boost converter is the most admired configuration for this scheme, even if the converter efficiency is restricted at duty cycle near to maximum value. In order to find solution to the problem and improve its conversion capability, many converter configurations have been implemented so far. With this circumstance, this research work proposes to give overview of a few most imperative research works related to DC-DC boost converters. Some configurations are covered and classified basically based on the application. The major benefits and disadvantages related to the available techniques are also briefly conveyed. At last, a proper evaluation is recognized among the important types of DC-DC boost converters in terms of efficiency, number of components, and stability.

  6. Blue Diode Laser Absorption Spectroscopy of Pulsed Magnetron Discharge

    Czech Academy of Sciences Publication Activity Database

    Olejníček, Jiří; Do, H.T.; Hubička, Zdeněk; Hippler, R.; Jastrabík, Lubomír

    2006-01-01

    Roč. 45, 10B (2006), s. 8090-8094 ISSN 0021-4922 R&D Projects: GA AV ČR 1QS100100563; GA ČR GA202/05/2242 Institutional research plan: CEZ:AV0Z10100521; CEZ:AV0Z10100520 Keywords : laser absorption spectroscopy * pulsed magnetron * sputtering parameters Subject RIV: BH - Optics, Masers, Lasers Impact factor: 1.222, year: 2006

  7. Magnetron based high energy S-band linac system

    International Nuclear Information System (INIS)

    Tiwari, T.; Krishnan, R.; Phatangare, Manoj

    2012-01-01

    This paper deals with the study of magnetron based high energy S-band linear accelerator (linac) system operating at spot frequency 2.998 GHz. The energy and dose are two important parameters of linac system which depend on input power of microwave source and length of linac tube. Here the author has studied how these parameters can be improved for side coupled standing wave S-band linac system

  8. Magnetron co-sputtering system for coating ICF targets

    International Nuclear Information System (INIS)

    Hsieh, E.J.; Meyer, S.F.; Halsey, W.G.; Jameson, G.T.; Wittmayer, F.J.

    1981-01-01

    Fabrication of Inertial Confinement Fusion (ICF) targets requires deposition of various types of coatings on microspheres. The mechanical strength, and surface finish of the coatings are of concern in ICF experiments. The tensile strength of coatings can be controlled through grain refinement, selective doping and alloy formation. We have constructed a magnetron co-sputtering system to produce variable density profile coatings with high tensile strength on microspheres

  9. Deposition of copper coatings in a magnetron with liquid target

    Energy Technology Data Exchange (ETDEWEB)

    Tumarkin, A. V., E-mail: sanyahrustal@mail.ru; Kaziev, A. V.; Kolodko, D. V.; Pisarev, A. A.; Kharkov, M. M.; Khodachenko, G. V. [National Research Nuclear University MEPhI (Moscow Engineering Physics Institute) (Russian Federation)

    2015-12-15

    Copper coatings were deposited on monocrystalline Si substrates using a magnetron discharge with a liquid cathode in the metal vapour plasma. During the deposition, the bias voltage in the range from 0 V to–400 V was applied to the substrate. The prepared films were investigated by a scanning electron microscope, and their adhesive properties were studied using a scratch tester. It was demonstrated that the adhesion of the deposited films strongly depends on the bias voltage and varies in a wide range.

  10. Special traits of the millimeter wave relativistic magnetron

    International Nuclear Information System (INIS)

    Berdin, S.A.; Chizhov, K.V.; Gadetski, N.P.; Korenev, V.G.; Lebedenko, A.N.; Marchenko, M.I.; Magda, I.I.; Melezhik, O.G.; Sinitsin, V.G.; Soshenko, V.A.

    2014-01-01

    A 8 mm band relativistic magnetron is investigated experimentally and by means of numerical simulation. The physical effects are analyzed which influence negatively the r.f. generation. The processes capable of reducing effectiveness of the generation and duration of the generated pulse include forward and backward axial flows of electrons, and intense electric fields - the generated microwaves and the fields owing to the space charge

  11. Methods of Phase and Power Control in Magnetron Transmitters for Superconducting Accelerators

    Energy Technology Data Exchange (ETDEWEB)

    Kazadevich, G. [MUONS Inc., Batavia; Johnson, R. [MUONS Inc., Batavia; Neubauer, M. [MUONS Inc., Batavia; Lebedev, V. [Fermilab; Schappert, W. [Fermilab; Yakovlev, V. [Fermilab

    2017-05-01

    Various methods of phase and power control in magnetron RF sources of superconducting accelerators intended for ADS-class projects were recently developed and studied with conventional 2.45 GHz, 1 kW, CW magnetrons operating in pulsed and CW regimes. Magnetron transmitters excited by a resonant (injection-locking) phasemodulated signal can provide phase and power control with the rates required for precise stabilization of phase and amplitude of the accelerating field in Superconducting RF (SRF) cavities of the intensity-frontier accelerators. An innovative technique that can significantly increase the magnetron transmitter efficiency at the widerange power control required for superconducting accelerators was developed and verified with the 2.45 GHz magnetrons operating in CW and pulsed regimes. High efficiency magnetron transmitters of this type can significantly reduce the capital and operation costs of the ADSclass accelerator projects.

  12. An Integrated Multifunctional Bidirectional AC/DC and DC/DC Converter for Electric Vehicles Applications

    OpenAIRE

    Liwen Pan; Chengning Zhang

    2016-01-01

    This paper presents an on-board vehicular battery charger that integrates bidirectional AC/DC converter and DC/DC converter to achieve high power density for application in electric vehicles (EVs). The integrated charger is able to transfer electrical energy between the battery pack and the electric traction system and to function as an AC/DC battery charger. The integrated charger topology is presented and the design of passive components is discussed. The control schemes are developed for m...

  13. Reconstruction of the static magnetic field of a magnetron

    Science.gov (United States)

    Krüger, Dennis; Köhn, Kevin; Gallian, Sara; Brinkmann, Ralf Peter

    2018-06-01

    The simulation of magnetron discharges requires a quantitatively correct mathematical model of the magnetic field structure. This study presents a method to construct such a model on the basis of a spatially restricted set of experimental data and a plausible a priori assumption on the magnetic field configuration. The example in focus is that of a planar circular magnetron. The experimental data are Hall probe measurements of the magnetic flux density in an accessible region above the magnetron plane [P. D. Machura et al., Plasma Sources Sci. Technol. 23, 065043 (2014)]. The a priori assumption reflects the actual design of the device, and it takes the magnetic field emerging from a center magnet of strength m C and vertical position d C and a ring magnet of strength m R , vertical position d R , and radius R. An analytical representation of the assumed field configuration can be formulated in terms of generalized hypergeometric functions. Fitting the ansatz to the experimental data with a least square method results in a fully specified analytical field model that agrees well with the data inside the accessible region and, moreover, is physically plausible in the regions outside of it. The outcome proves superior to the result of an alternative approach which starts from a multimode solution of the vacuum field problem formulated in terms of polar Bessel functions and vertical exponentials. As a first application of the obtained field model, typical electron and ion Larmor radii and the gradient and curvature drift velocities of the electron guiding center are calculated.

  14. Geometrical aspects of a hollow-cathode planar magnetron

    International Nuclear Information System (INIS)

    Wang, Z.; Cohen, S.A.

    1999-01-01

    A hollow-cathode planar magnetron (HCPM), built by surrounding a planar sputtering-magnetron cathode with a hollow-cathode structure (HCS) [Z. Wang and S. A. Cohen, J. Vac. Sci. Technol. A 17, 77 (1999)], is operable at substantially lower pressures than its planar-magnetron counterpart. HCPM operational parameters depend on the inner diameter D and length L of its cylindrical HCS. Only when L is greater than L 0 , a critical length, is the HCPM operable in the new low-pressure regime. The critical length varies with HCS inner diameter D. Explanations of the lower operational pressure regime, critical length, and plasma shape are proposed and compared with a one-dimension diffusion model for energetic electron transport. At pressures above 1 mTorr, Bohm diffusion (temperature congruent primary electron energy), with an ambipolar constraint, can explain the ion - electron pair creation required to sustain the discharge. At the lowest pressure, ∼0.3 mTorr, collision-limited diffusion creates fewer ion - electron pairs than required for steady state and therefore cannot explain the experimental data. The critical length L 0 is consistent with the magnetization length of the primary electrons. copyright 1999 American Institute of Physics

  15. Epitaxial (100)-oriented Mo/V superlattice grown on MgO(100) by dcMS and HiPIMS

    International Nuclear Information System (INIS)

    Shayestehaminzadeh, S.; Magnusson, R.L.; Gislason, H.P.; Olafsson, S.

    2013-01-01

    Epitaxial (100)-oriented Mo/V superlattices have been grown by High Power Impulse Magnetron Sputtering (HiPIMS) and dc Magnetron Sputtering (dcMS) on single-crystalline MgO(100) substrates at growth temperatures ranging from 30 °C to 600 °C. Superlattice bilayer period of Mo/V around 12/12 monolayers and 15 repeat periods was studied. This study aims to investigate the effect of the HiPIMS process on reducing the growth temperature of Mo/V superlattices using the high energy ionized Mo, V species in the HiPIMS plasma. In one case, the Mo layer was only grown with the HiPIMS process and V layer grown using the dcMS process while in another both layers were grown with the HiPIMS process. The as-deposited films were characterized by X-ray reflection and diffraction techniques. The dcMS process was found to give superior superlattice growth at high growth temperatures while a mixed Mo HiPIMS and V dcMS process gives better result at lower growth temperatures (300 °C). Room temperature growth reveals that neither the mixed Mo HiPIMS and V dcMS process nor the pure HiPIMS for both materials can produce better result compared to the pure dcMS process, which gives a relatively better result. - Highlights: • Epitaxial (100)-oriented Mo/V superlattices have been grown by HiPIMS and dcMS on MgO(100) for various temperatures. • The study was aimed to investigate the effect of ionized HiPIMS process onlowering the growth temperature. • The dcMS process was found to give superior superlattice growth at high growth temperature. • The mixed Mo HiPIMS and V dcMS process gives best result at lower growth temperatures

  16. Magnetron with smooth anode. Statistical theory and ordered oscillations; Magnetron a anode lisse. Theorie statistique et oscillations ordonnees

    Energy Technology Data Exchange (ETDEWEB)

    Coste, J.

    1961-03-15

    We have to investigate the equilibrium regime that appears between a hot cathode and the electronic cloud that is confined around the cathode by a magnetic field parallel to its axis. The densities being high enough to involve the effect of space charge. The challenge of the magnetron theory is to face 2 issues: first the structure of the electronic cloud in a diode submitted to a magnetic field and secondly the oscillations that are likely to appear in this cloud. In this work we have made 2 attempts to clarify the situation, we have extended the classical theory of the static charge of space through a study of its oscillation modes on one hand and on the other hand we have tackled the issue of the structure of the electronic cloud with the tool of statistics. This document is divided into 2 chapters. In the first chapter we present a static study of the magnetron in which we take a statistical approach deliberately. We give answers to the issue of the thermodynamical equilibrium of the electronic cloud and we have found a mode very close to the Brillouin mode. The statistical approach has made us discuss the boundary conditions on the cathode, it means the coupling between the cathode and the electronic cloud. In the second chapter we present the theoretical study of the oscillations in a magnetron operating in the Brillouin mode. The resonances that appear in experimental data stay difficult to explain.

  17. Mechanical, tribological and corrosion properties of CrBN films deposited by combined direct current and radio frequency magnetron sputtering

    International Nuclear Information System (INIS)

    Jahodova, Vera; Ding, Xing-zhao; Seng, Debbie H.L.; Gulbinski, W.; Louda, P.

    2013-01-01

    Cr–B–N films were deposited on stainless steel substrates by a combined direct current and radio frequency (RF) reactive unbalanced magnetron sputtering process using two elemental Cr and one compound BN targets. Boron content in the as-deposited films was qualitatively analyzed by time-of-flight secondary ion mass spectroscopy. Films' microstructure, mechanical and tribological properties were characterized by X-ray diffraction, nanoindentation and pin-on-disk tribometer experiments. Corrosion behavior of the Cr–B–N films was evaluated by electrochemical potentiodynamic polarization method in a 3 wt.% NaCl solution. All the films were crystallized into a NaCl-type cubic structure. At lower RF power applied on the BN target (≤ 600 W), films are relatively randomly oriented, and films' crystallinity increased with increasing RF power. With increasing RF power further (≥ 800 W), films became (200) preferentially oriented, and films' crystallinity decreased gradually. With incorporation of a small amount of boron atoms into the CrN films, hardness, wear- and corrosion-resistance were all improved evidently. The best wear and corrosion resistance was obtained for the film deposited with 600 W RF power applied on the BN target. - Highlights: • CrBN films deposited by direct current and radio frequency magnetron sputtering. • CrBN exhibited higher hardness, wear- and corrosion-resistance than pure CrN. • The best wear- and corrosion-resistant film was deposited with 600 W RF power

  18. An investigation of material properties and tribological performance of magnetron sputtered thin film coatings

    Science.gov (United States)

    Singh, Harpal

    This dissertation is divided into two categories based upon lubrication functionality and its application. The categories are: Dry film lubrication and Fluid film lubrication with thin film coatings. Thin film coatings examined in this work were deposited using closed field unbalanced magnetron sputtering and RF-DC coupled magnetron sputtering systems. In Dry/Solid film lubrication, the mechanical, structural and tribological properties of two Molybdenum disulphide (MoS2) based coatings are examined and evaluated. Among the two coatings, one coating is doped with Ti (Ti-MoS2) and the other is a combination of metal, lubricant and oxide (Sb2O3/Au - MoS2). These coatings are known to provide low friction in vacuum environments. The goal of this work was to evaluate friction and wear performance of MoS2 doped coatings in unidirectional and reciprocating sliding contact under different environmental conditions. Sliding contact results showed friction and wear dependence on temperature and humidity. The formation and removal of transfer films and the recrystallization and reorientation of basal layers on the steel counterface was observed as the mechanism for low friction. Structural analysis revealed a relationship between the microstructural properties and tribological performance. It was also observed that the addition of dopants (Ti, Au, Sb 2O3) improved the mechanical properties as compared to pure MoS2 coatings. Further, the rolling contact performance of the coatings was measured on a five ball on rod tribometer and a Thrust bearing tribometer under vacuum and air environments. The rolling contact experiments indicated that life of the rolling components depend on the amount of material present between the contacts. Fluid film lubrication with thin film coatings investigates the possibilities to improve the performance and durability of tribological components when oils and thin films are synergistically coupled. In this work, the ability of a Diamond Like Carbon

  19. On and off controlled resonant dc-dc power converter

    DEFF Research Database (Denmark)

    2015-01-01

    The present invention relates to a resonant DC-DC power converter comprising an input side circuit comprising a positive and a negative input terminal for receipt of an input voltage or current and an output side circuit comprising positive and negative output terminals for supply of a converter...... output voltage and connection to a converter load. The resonant DC-DC power converter further comprises a rectification circuit connected between an output of a resonant network and the output side circuit. The resonant network is configured for alternatingly being charged from the input voltage...... or current and discharged through the rectification circuit by a first controllable switch arrangement in accordance with a first switch control signal. A second controllable switch arrangement of the resonant DC-DC power converter is configured to select a first impedance characteristic of the resonant...

  20. DC Cable for Railway

    Science.gov (United States)

    Tomita, Masaru

    The development of a superconducting cable for railways has commenced, assuming that a DC transmission cable will be used for electric trains. The cable has been fabricated based on the results of current testing of a superconducting wire, and various evaluation tests have been performed to determine the characteristics of the cable. A superconducting transmission cable having zero electrical resistance and suitable for railway use is expected to enhance regeneration efficiency, reduce power losses, achieve load leveling and integration of sub-stations, and reduce rail potential.

  1. Auxiliary resonant DC tank converter

    Science.gov (United States)

    Peng, Fang Z.

    2000-01-01

    An auxiliary resonant dc tank (ARDCT) converter is provided for achieving soft-switching in a power converter. An ARDCT circuit is coupled directly across a dc bus to the inverter to generate a resonant dc bus voltage, including upper and lower resonant capacitors connected in series as a resonant leg, first and second dc tank capacitors connected in series as a tank leg, and an auxiliary resonant circuit comprising a series combination of a resonant inductor and a pair of auxiliary switching devices. The ARDCT circuit further includes first clamping means for holding the resonant dc bus voltage to the dc tank voltage of the tank leg, and second clamping means for clamping the resonant dc bus voltage to zero during a resonant period. The ARDCT circuit resonantly brings the dc bus voltage to zero in order to provide a zero-voltage switching opportunity for the inverter, then quickly rebounds the dc bus voltage back to the dc tank voltage after the inverter changes state. The auxiliary switching devices are turned on and off under zero-current conditions. The ARDCT circuit only absorbs ripples of the inverter dc bus current, thus having less current stress. In addition, since the ARDCT circuit is coupled in parallel with the dc power supply and the inverter for merely assisting soft-switching of the inverter without participating in real dc power transmission and power conversion, malfunction and failure of the tank circuit will not affect the functional operation of the inverter; thus a highly reliable converter system is expected.

  2. PENGGUNAAN FUZZY LOGIC UNTUK KONTROL PARALLEL CONVERTER DC-DC

    Directory of Open Access Journals (Sweden)

    Bambang Prio Hartono

    2012-09-01

    Full Text Available Abstract: Using system fuzzy logic as control  technology have been used on low load dc-dc converter with combined parallel compiled  dc-dc converter can  obtain big load.   With existence of differrence of component parameter and each parallel compiled converter can obtained different current  and voltage output.  Function of controller  for to do adjustment, so that current which is applied  to  load by each converter  can be obtained  difference error as small as possible or same. The object of research is developing design of large signal dc-dc converter which is  combined with using  FLC so that  obtain  better performance.  To get better performance have been made plant model and simulation with CDE method.  The more systematic  system and design is needed to overcome bigger load  on dc-dc converter, so that parallel  compiled current master slave control system on dc-dc converter with using fuzzy logic  controller is used. Result of  research showed that error or difference of  current  which is applied to load can handled by fuzzy logic  controller.  Technic of current and voltage controller co to do adjustment current and voltage distribution  equally to load.  Distribution of iL1,iL2 and  output voltage Vo on dc-dc  converter with load 2,25 until  7,875 and voltage  100  until 120 volt,  load current beetwen  12 until 48, % relatif  error  Vo  0,4% until  0,9%.

  3. Step-Up DC-DC Power Converter

    DEFF Research Database (Denmark)

    2015-01-01

    The present invention relates to a step-up DC-DC power converter which comprises a primary side circuit and a secondary side circuit coupled through a galvanic isolation barrier. The primary side circuit comprises a positive and a negative input terminal for receipt of an input voltage and an input...... being charged from the input voltage and discharged to the output capacitor through the galvanic isolation barrier in accordance with a switch control signal to produce the converter output voltage. The step-up DC-DC power converter comprises an electrical short-circuit connection across the galvanic...

  4. DC Distribution Systems and Microgrids

    DEFF Research Database (Denmark)

    Dragicevic, Tomislav; Anvari-Moghaddam, Amjad; Quintero, Juan Carlos Vasquez

    2017-01-01

    summarized. Due to its attractive characteristics in terms of compliance with modern generation, storage and electronic load technologies, high reliability and current carrying capacity, as well as simple control, DC systems are already an indispensable part of power systems. Moreover, the existing......A qualitative overview of different hardware topologies and control systems for DC MGs has been presented in this chapter. Some challenges and design considerations of DC protections systems have also been discussed. Finally, applications of DC MGs in emerging smart grid applications have been...... challenges such as protection issues will be effectively resolved in the near future due to fast progress of semiconductor technology which is a key enabler cheap and reliable future DC solid-state protection systems. Therefore, it is the view of the author that more and more DC systems will appear...

  5. Reactive Arthritis

    Directory of Open Access Journals (Sweden)

    Eren Erken

    2013-06-01

    Full Text Available Reactive arthritis is an acute, sterile, non-suppurative and inflammatory arthropaty which has occured as a result of an infectious processes, mostly after gastrointestinal and genitourinary tract infections. Reiter syndrome is a frequent type of reactive arthritis. Both reactive arthritis and Reiter syndrome belong to the group of seronegative spondyloarthropathies, associated with HLA-B27 positivity and characterized by ongoing inflammation after an infectious episode. The classical triad of Reiter syndrome is defined as arthritis, conjuctivitis and urethritis and is seen only in one third of patients with Reiter syndrome. Recently, seronegative asymmetric arthritis and typical extraarticular involvement are thought to be adequate for the diagnosis. However, there is no established criteria for the diagnosis of reactive arthritis and the number of randomized and controlled studies about the therapy is not enough. [Archives Medical Review Journal 2013; 22(3.000: 283-299

  6. Tribology of ZRN, CRN and TIALN thin films deposited by reactive magnetron sputtering

    Directory of Open Access Journals (Sweden)

    Alexander Ruden

    2013-01-01

    Full Text Available El coeficiente de fricción y el coeficiente de desgaste, representan dos variables importantes para la elección de recubrimientos duros en aplicaciones críticas de ingeniería tales como corte y conformado de materiales. Para explicar de manera profunda estas variables, es necesario conocer los diferentes tipos de desgaste que ocurren en estas superficies recubiertas. Se han evaluado recubrimientos de nitruro de circonio (ZrN, nitruro de cromo (CrN y nitruro de titanio aluminio (TiAlN, producidos por la técnica magnetrón sputtering reactivo, determinando las propiedades tribológicas, midiendo coeficientes de fricción (COF y desgaste, y mostrando un análisis de los mecanismos de desgaste presentes para cada recubrimiento durante el contacto tribológico en sistemas cerámicos. Se observó que el voltaje de polarización incrementa las fallas por deformación plástica y la generación de un tercer cuerpo en la superficie del ZrN. El aumento del flujo de nitrógeno en la deposición de CrN, mejora el comportamiento tribológico al segregar la fase cúbica del material, optimizando sus propiedades superficiales. Al incrementar la temperatura de deposición del TiAlN se mejora su calidad superficial (reducción de rugosidad y densidad de poros, reduciendo la abrasión y aumentando la capacidad de carga del compuesto.

  7. Semiconducting WO.sub.3./sub. thin films prepared by pulsed reactive magnetron sputtering

    Czech Academy of Sciences Publication Activity Database

    Brunclíková, M.; Hubička, Zdeněk; Kment, Štěpán; Olejníček, Jiří; Čada, Martin; Kšírová, Petra; Krýsa, J.

    2015-01-01

    Roč. 41, č. 12 (2015), s. 9259-9266 ISSN 0922-6168. [Pannonian Symposium on Catalysis /12./. Třešť, 16.09.2014-20.09.2014] R&D Projects: GA ČR GAP108/12/2104; GA MŠk LH12043 Grant - others:AVČR(CZ) M100101215 Institutional support: RVO:68378271 Keywords : WO 3 * water splitting * HIPIMS * photoanodes Subject RIV: BL - Plasma and Gas Discharge Physics Impact factor: 1.833, year: 2015

  8. A Compact, Pi-Mode Extraction Scheme for the Axial B-Field Recirculating Planar Magnetron

    Science.gov (United States)

    2012-07-23

    Figure 4). Thus, in a planar magnetron, the minimum phase velocity, vph , to stay above cutoff in the rectangular waveguide is ℎ = ...as magnetrons, electrons must be accelerated such that they are in synchronism with the phase velocity, vph , of the electromagnetic wave for an

  9. Very High Frequency Half Bridge DC/DC Converter

    DEFF Research Database (Denmark)

    Madsen, Mickey Pierre; Knott, Arnold; Andersen, Michael A. E.

    2014-01-01

    This paper presents the first, off chip, class DE (resonant half bridge) converter working in the Very High Frequency (VHF) range. The benefits of using half bridge circuits both in the inverter and rectifier part of a VHF resonant dc/dc converter are analyzed and design equations for all...

  10. SCM Handbooks for dc-to-dc Converters

    Science.gov (United States)

    Lee, F.; Mohmoud, M.; Yu, Y.

    1984-01-01

    Two documents aid in design of control modules for dc-to-dc converters. Features of SCM include: Adaptive stability, power component stress limiting, implementation of various control laws, unified design approach. Analysis and quidelines contained in handbooks enable engineer to design SCM circuit and confidently predict resulting overall performance.

  11. Sheppard-Taylor Isolated High Boost DC-DC Converter

    DEFF Research Database (Denmark)

    Chub, Andrii; Siwakoti, Yam Prasad; Vinnikov, Dmitri

    2017-01-01

    This paper presents a new galvanically isolated step-up dc-dc converter intended for low-power but high step-up applications. The proposed converter is capable of regulating output voltage within a wide range of the input voltage or load variations. In contrast to competitors, the converter can...

  12. Dc-To-Dc Converter Uses Reverse Conduction Of MOSFET's

    Science.gov (United States)

    Gruber, Robert P.; Gott, Robert W.

    1991-01-01

    In modified high-power, phase-controlled, full-bridge, pulse-width-modulated dc-to-dc converters, switching devices power metal oxide/semiconductor field-effect transistors (MOSFET's). Decreases dissipation of power during switching by eliminating approximately 0.7-V forward voltage drop in anti-parallel diodes. Energy-conversion efficiency increased.

  13. A Current-Fed Isolated Bidirectional DC-DC Converter

    DEFF Research Database (Denmark)

    Sun, Xiaofeng; Wu, Xiaoying; Shen, Yanfeng

    2017-01-01

    This paper proposes a current-fed isolated bidirectional DC-DC converter (CF-IBDC) which has the advantages of wide input voltage range, low input current ripple, low conduction losses, and soft switching over the full operating range. Compared with conventional CF-IBDCs, the voltage spikes...

  14. Power flow analysis for DC voltage droop controlled DC microgrids

    DEFF Research Database (Denmark)

    Li, Chendan; Chaudhary, Sanjay; Dragicevic, Tomislav

    2014-01-01

    This paper proposes a new algorithm for power flow analysis in droop controlled DC microgrids. By considering the droop control in the power flow analysis for the DC microgrid, when compared with traditional methods, more accurate analysis results can be obtained. The algorithm verification is ca...

  15. High power impulse magnetron sputtering and its applications

    Science.gov (United States)

    Yan, YUAN; Lizhen, YANG; Zhongwei, LIU; Qiang, CHEN

    2018-04-01

    High power impulse magnetron sputtering (HiPIMS) has attracted a great deal of attention because the sputtered material is highly ionized during the coating process, which has been demonstrated to be advantageous for better quality coating. Therefore, the mechanism of the HiPIMS technique has recently been investigated. In this paper, the current knowledge of HiPIMS is described. We focus on the mechanical properties of the deposited thin film in the latest applications, including hard coatings, adhesion enhancement, tribological performance, and corrosion protection layers. A description of the electrical, optical, photocatalytic, and functional coating applications are presented. The prospects for HiPIMS are also discussed in this work.

  16. Pd-catalysts for DFAFC prepared by magnetron sputtering

    Czech Academy of Sciences Publication Activity Database

    Bieloshapka, Igor; Jiříček, Petr; Vorokhta, M.; Tomšík, Elena; Rednyk, A.; Perekrestov, R.; Jurek, Karel; Ukraintsev, Egor; Hruška, Karel; Romanyuk, Olexandr; Lesiak, B.

    2017-01-01

    Roč. 419, Oct (2017), s. 838-846 ISSN 0169-4332 R&D Projects: GA ČR(CZ) GBP108/12/G108; GA MŠk LM2015088 Institutional support: RVO:68378271 ; RVO:61389013 Keywords : Pd catalyst * formic acid fuel cell * magnetron sputtering * DFAFC * surface morphology Subject RIV: BM - Solid Matter Physics ; Magnetism; BM - Solid Matter Physics ; Magnetism (UMCH-V) OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.); Condensed matter physics (including formerly solid state physics, supercond.) (UMCH-V) Impact factor: 3.387, year: 2016

  17. Some properties of the gas magnetron; neke osobine gasnog magnetrona

    Energy Technology Data Exchange (ETDEWEB)

    Miljevic, V [Boris Kidric Institute of nuclear sciences, Vinca, Belgrade (Yugoslavia)

    1979-07-01

    The cylindrical magnetron diode with directly heated cathode, filled with argon at low pressure, has been studied. In the case of high magnetic fields and low gas pressure the motion of electrons is reduced to the rotation around the cathode with superimposed allow radial drift. It is found that the plasma formation time in in the msec region. The critical magnetic field in the vacuum diode (B{sub c}), and its value increases with the increase of the anode voltage and working pressure. (author)

  18. Characterization of Ta–Si–N coatings prepared using direct current magnetron co-sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Yung-I, E-mail: yichen@mail.ntou.edu.tw; Lin, Kun-Yi; Wang, Hsiu-Hui; Cheng, Yu-Ru

    2014-06-01

    Ta–Si–N coatings were prepared using reactive direct current magnetron co-sputtering on silicon substrates. When the sputtering powers and N{sub 2} flow ratio were varied, Ta–Si–N coatings exhibited various chemical compositions and crystalline characteristics. The high-Si-content Ta–Si–N coatings exhibited an amorphous phase in the as-deposited states, whereas the low-Si-content coatings exhibited a face-centered cubic phase or an amorphous phase depending on the N content. This study evaluated the application of amorphous Ta–Si–N coatings, such as the protective coatings on glass molding dies, in high-temperature and oxygen-containing atmospheres for longed operation durations. To explore the oxidation resistance and mechanical properties of the Ta–Si–N coatings, annealing treatments were conducted in a 1%O{sub 2}–99%Ar atmosphere at 600 °C for 4–100 h. The material characteristics and oxidation behavior of the annealed Ta–Si–N coatings were examined using atomic force microscopy, transmission electron microscopy, X-ray photoelectron spectroscopy, and a nanoindentation tester. The Si oxidized preferentially in the Ta–Si–N coatings. The in-diffusion of oxygen during 600 °C annealing was restricted by the formation of an amorphous oxide scale consisting of Si and O.

  19. Chemical mechanical polishing characteristics of ITO thin film prepared by RF magnetron sputtering

    International Nuclear Information System (INIS)

    Lee, Kang-Yeon; Choi, Gwon-Woo; Kim, Yong-Jae; Choi, Youn-Ok; Kim, Nam-Oh

    2012-01-01

    Indium-tin-oxide (ITO) thin films have attracted intensive interest because of their unique properties of good conductivity, high optical transmittance over the visible region and easy patterning ability. ITO thin films have found many applications in anti-static coatings, thermal heaters, solar cells, flat panel displays (FPDs), liquid crystal displays (LCDs), electroluminescent devices, sensors and organic light-emitting diodes (OLEDs). ITO thin films are generally fabricated by using various methods, such as spraying, chemical vapor deposition (CVD), evaporation, electron gun deposition, direct current electroplating, high frequency sputtering, and reactive sputtering. In this research, ITO films were grown on glass substrates by using a radio-frequency (RF) magnetron sputtering method. In order to achieve a high transmittance and a low resistivity, we examined the various film deposition conditions, such as substrate temperature, working pressure, annealing temperature, and deposition time. Next, in order to improve the surface quality of the ITO thin films, we performed a chemical mechanical polishing (CMP) with different process parameters and compared the electrical and the optical properties of the polished ITO thin films. The best CMP conditions with a high removal rate, low nonuniformity, low resistivity and high transmittance were as follows: platen speed, head speed, polishing time, and slurry flow rate of 30 rpm, 30 rpm, 60 sec, and 60 ml/min, respectively.

  20. Magnetron sputtered TiN thin films toward enhanced performance supercapacitor electrodes

    KAUST Repository

    Wei, Binbin

    2018-04-09

    Supercapacitors as a new type of energy storage devices bridging the gap between conventional capacitors and batteries have aroused widespread concern. Herein, binder-free titanium nitride (TiN) thin film electrodes for supercapacitors prepared by reactive magnetron sputtering technology are reported. The effect of N2 content on the supercapacitor performance is evaluated. A highest specific capacitance of 27.3 mF cm−2 at a current density of 1.0 mA cm−2, together with excellent cycling performance (98.2% capacitance retention after 20,000 cycles at 2.0 mA cm−2) is achieved in a 0.5 M H2SO4 aqueous electrolyte. More importantly, a symmetric supercapacitor device assembled on the basis of TiN thin films can deliver a maximum energy density of 17.6 mWh cm−3 at a current density of 0.2 mA cm−2 and a maximum power density of 10.8 W cm−3 at a current density of 2 mA cm−2 with remarkable cycling stability. As a consequence, TiN thin films demonstrate great potential as promising supercapacitor electrode materials.

  1. Mechanical and tribological properties of crystalline aluminum nitride coatings deposited on stainless steel by magnetron sputtering

    International Nuclear Information System (INIS)

    Choudhary, R.K.; Mishra, S.C.; Mishra, P.; Limaye, P.K.; Singh, K.

    2015-01-01

    Aluminum nitride (AlN) coating is a potential candidate for addressing the problems of MHD pressure drop, tritium permeation and liquid metal corrosion of the test blanket module of fusion reactor. In this work, AlN coatings were grown on stainless steel by magnetron sputtering. Grazing incidence X-ray diffraction measurement revealed that formation of mixed phase (wurtzite and rock salt) AlN was favored at low discharge power and substrate negative biasing. However, at sufficiently high discharge power and substrate bias, (100) oriented wurtzite AlN was obtained. Secondary ion mass spectroscopy showed presence of oxygen in the coatings. The highest value of hardness and Young's modulus were 14.1 GPa and 215 GPa, respectively. Scratch test showed adhesive failure at a load of about 20 N. Wear test showed improved wear resistance of the coatings obtained at higher substrate bias. - Highlights: • Crystalline AlN coatings obtained on stainless steel by reactive sputtering. • Wurtzite AlN formed at higher discharge power and higher substrate biasing. • Mixture of wurtzite and rock salt AlN formed at low power and low biasing. • Substrate negative biasing improved adhesion of AlN coatings. • Substrate negative biasing improved wear resistance and hardness of AlN coatings.

  2. Reducing the impurity incorporation from residual gas by ion bombardment during high vacuum magnetron sputtering

    International Nuclear Information System (INIS)

    Rosen, Johanna; Widenkvist, Erika; Larsson, Karin; Kreissig, Ulrich; Mraz, Stanislav; Martinez, Carlos; Music, Denis; Schneider, J. M.

    2006-01-01

    The influence of ion energy on the hydrogen incorporation has been investigated for alumina thin films, deposited by reactive magnetron sputtering in an Ar/O 2 /H 2 O environment. Ar + with an average kinetic energy of ∼5 eV was determined to be the dominating species in the plasma. The films were analyzed with x-ray diffraction, x-ray photoelectron spectroscopy, and elastic recoil detection analysis, demonstrating evidence for amorphous films with stoichiometric O/Al ratio. As the substrate bias potential was increased from -15 V (floating potential) to -100 V, the hydrogen content decreased by ∼70%, from 9.1 to 2.8 at. %. Based on ab initio calculations, these results may be understood by thermodynamic principles, where a supply of energy enables surface diffusion, H 2 formation, and desorption [Rosen et al., J. Phys.: Condens. Matter 17, L137 (2005)]. These findings are of importance for the understanding of the correlation between ion energy and film composition and also show a pathway to reduce impurity incorporation during film growth in a high vacuum ambient

  3. Mechanical and tribological properties of crystalline aluminum nitride coatings deposited on stainless steel by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Choudhary, R.K., E-mail: crupeshbarc@gmail.com [Materials Processing Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Mishra, S.C.; Mishra, P. [Materials Processing Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Limaye, P.K. [Refuelling Technology Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Singh, K. [Fusion Reactor Materials Section, Bhabha Atomic Research Centre, Mumbai 400085 (India)

    2015-11-15

    Aluminum nitride (AlN) coating is a potential candidate for addressing the problems of MHD pressure drop, tritium permeation and liquid metal corrosion of the test blanket module of fusion reactor. In this work, AlN coatings were grown on stainless steel by magnetron sputtering. Grazing incidence X-ray diffraction measurement revealed that formation of mixed phase (wurtzite and rock salt) AlN was favored at low discharge power and substrate negative biasing. However, at sufficiently high discharge power and substrate bias, (100) oriented wurtzite AlN was obtained. Secondary ion mass spectroscopy showed presence of oxygen in the coatings. The highest value of hardness and Young's modulus were 14.1 GPa and 215 GPa, respectively. Scratch test showed adhesive failure at a load of about 20 N. Wear test showed improved wear resistance of the coatings obtained at higher substrate bias. - Highlights: • Crystalline AlN coatings obtained on stainless steel by reactive sputtering. • Wurtzite AlN formed at higher discharge power and higher substrate biasing. • Mixture of wurtzite and rock salt AlN formed at low power and low biasing. • Substrate negative biasing improved adhesion of AlN coatings. • Substrate negative biasing improved wear resistance and hardness of AlN coatings.

  4. Magnetron sputtered TiN thin films toward enhanced performance supercapacitor electrodes

    KAUST Repository

    Wei, Binbin; Liang, Hanfeng; Zhang, Dongfang; Qi, Zhengbing; Shen, Hao; Wang, Zhoucheng

    2018-01-01

    Supercapacitors as a new type of energy storage devices bridging the gap between conventional capacitors and batteries have aroused widespread concern. Herein, binder-free titanium nitride (TiN) thin film electrodes for supercapacitors prepared by reactive magnetron sputtering technology are reported. The effect of N2 content on the supercapacitor performance is evaluated. A highest specific capacitance of 27.3 mF cm−2 at a current density of 1.0 mA cm−2, together with excellent cycling performance (98.2% capacitance retention after 20,000 cycles at 2.0 mA cm−2) is achieved in a 0.5 M H2SO4 aqueous electrolyte. More importantly, a symmetric supercapacitor device assembled on the basis of TiN thin films can deliver a maximum energy density of 17.6 mWh cm−3 at a current density of 0.2 mA cm−2 and a maximum power density of 10.8 W cm−3 at a current density of 2 mA cm−2 with remarkable cycling stability. As a consequence, TiN thin films demonstrate great potential as promising supercapacitor electrode materials.

  5. CH₃NH₃PbI₃-based planar solar cells with magnetron-sputtered nickel oxide.

    Science.gov (United States)

    Cui, Jin; Meng, Fanping; Zhang, Hua; Cao, Kun; Yuan, Huailiang; Cheng, Yibing; Huang, Feng; Wang, Mingkui

    2014-12-24

    Herein we report an investigation of a CH3NH3PbI3 planar solar cell, showing significant power conversion efficiency (PCE) improvement from 4.88% to 6.13% by introducing a homogeneous and uniform NiO blocking interlayer fabricated with the reactive magnetron sputtering method. The sputtered NiO layer exhibits enhanced crystallization, high transmittance, and uniform surface morphology as well as a preferred in-plane orientation of the (200) plane. The PCE of the sputtered-NiO-based perovskite p-i-n planar solar cell can be further promoted to 9.83% when a homogeneous and dense perovskite layer is formed with solvent-engineering technology, showing an impressive open circuit voltage of 1.10 V. This is about 33% higher than that of devices using the conventional spray pyrolysis of NiO onto a transparent conducting glass. These results highlight the importance of a morphology- and crystallization-compatible interlayer toward a high-performance inverted perovskite planar solar cell.

  6. A DC Transformer

    Science.gov (United States)

    Youngquist, Robert C.; Ihlefeld, Curtis M.; Starr, Stanley O.

    2013-01-01

    A component level dc transformer is described in which no alternating currents or voltages are present. It operates by combining features of a homopolar motor and a homopolar generator, both de devices, such that the output voltage of a de power supply can be stepped up (or down) with a corresponding step down (or up) in current. The basic theory for this device is developed, performance predictions are made, and the results from a small prototype are presented. Based on demonstrated technology in the literature, this de transformer should be scalable to low megawatt levels, but it is more suited to high current than high voltage applications. Significant development would be required before it could achieve the kilovolt levels needed for de power transmission.

  7. Phase Grouping of Larmor Electrons by a Synchronous Wave in Controlled Magnetrons

    Energy Technology Data Exchange (ETDEWEB)

    Kazakevich, G. [MUONS Inc., Batavia; Johnson, R. [MUONS Inc., Batavia; Lebedev, V. [Fermilab; Yakovlev, V. [Fermilab

    2018-04-01

    A simplified analytical model based on the charge drift approximation has been developed. It considers the resonant interaction of the synchronous wave with the flow of Larmor electrons in a magnetron. The model predicts stable coherent generation of the tube above and below the threshold of self-excitation. This occurs if the magnetron is driven by a sufficient resonant injected signal (up to -10 dB). The model substantiates precise stability, high efficiency and low noise at the range of the magnetron power control over 10 dB by variation of the magnetron current. The model and the verifying experiments with 2.45 GHz, 1 kW magnetrons are discussed.

  8. Effect of thickness on surface morphology, optical and humidity sensing properties of RF magnetron sputtered CCTO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Ahmadipour, Mohsen [Structural Materials Niche Area, School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia, Engineering Campus, 14300 Nibong Tebal, Penang (Malaysia); Ain, Mohd Fadzil [School of Electrical and Electronic Engineering, Universiti Sains Malaysia, Engineering Campus, 14300 Nibong Tebal, Penang (Malaysia); Ahmad, Zainal Arifin, E-mail: srzainal@usm.my [Structural Materials Niche Area, School of Materials and Mineral Resources Engineering, Universiti Sains Malaysia, Engineering Campus, 14300 Nibong Tebal, Penang (Malaysia)

    2016-11-01

    Highlights: • CCTO thin film was synthesized by RF magnetron sputtering successfully. • Increase in thickness lead to increase in grain size and decrease in band gap. • Short response times and recovery times of lead CCTO humidity sensor. • Sensor could detect humidity range (30–90%). - Abstract: In this study, calcium copper titanate (CCTO) thin films were deposited on ITO substrates successfully by radio frequency (RF) magnetron sputtering method in argon atmosphere. The CCTO thin films present a polycrystalline, uniform and porous structure. The surface morphology, optical and humidity sensing properties of the synthesized CCTO thin films have been studied by X-ray diffraction (XRD), atomic force microscopy (AFM), field emission scanning electron microscopy (FESEM), energy-dispersive X-ray spectroscopy (EDX), UV–vis spectrophotometer and current-voltage (I–V) analysis. XRD and AFM confirmed that the intensity of peaks and pore size of CCTO thin films were enhanced by increasing the thin films. Tauc plot method was adopted to estimate the optical band gaps. The surface structure and energy band gaps of the deposited films were affected by film thickness. Energy band gap of the layers were 3.76 eV, 3.68 eV and 3.5 eV for 200 nm, 400 nm, and 600 nm CCTO thin films layer, respectively. The humidity sensing properties were measured by using direct current (DC) analysis method. The response times were 12 s, 22 s, and 35 s while the recovery times were 500 s, 600 s, and 650 s for 200 nm, 400 nm, and 600 nm CCTO thin films, respectively at humidity range of 30–90% relative humidity (RH).

  9. The performance of the DC motor by the PID controlling PWM DC-DC boost converter

    OpenAIRE

    Can, Erol; Sayan, Hasan Hüseyin

    2017-01-01

    This paper presents the PID controlling direct current (DC) to the direct current boost converter feds DC motor which has a 3.68 kW and 240 V of DC voltage input on its characteristics. What is first formed is the boost converter mathematical model at the design stage. Secondly, a mathematical model of the DC motor is created so that the boost converter with the machine can be established and modeled at the Matlab Simulink. The PID controller is considered for arranging a pulse width modulati...

  10. Laterally resolved ion-distribution functions at the substrate position during magnetron sputtering of indium-tin oxide films

    International Nuclear Information System (INIS)

    Plagemann, A.; Ellmer, K.; Wiesemann, K.

    2007-01-01

    During the magnetron sputtering from an indium-tin oxide (ITO) target (76 mm diameter) we measured the ion-distribution functions (IDFs) of energetic ions (argon, indium, and oxygen ions) at the substrate surface using a combination of a quadrupole mass spectrometer and an electrostatic energy analyzer. We obtained the IDFs for argon sputtering pressures in the range from 0.08 to 2 Pa and for dc as well as rf (13.56 MHz) plasma excitation with powers from 10 to 100 W. The IDF measurements were performed both over the target center at a target-to-substrate distance of 65 mm and at different positions along the target radius in order to scan the erosion track of the target. The mean kinetic energies of argon ions calculated from the IDFs in the dc plasma decreased from about 30 to 15 eV, when the argon pressure increased from 0.08 to 2 Pa, which is caused by a decrease of the electron temperature also by a factor of 2. Indium atoms exhibit higher mean energies due to their additional energy from the sputtering process. The total metal ion flux turns out to be proportional to the discharge power and the pressure, the latter dependence being due to Penning ionization of the metal atoms (In and Sn). From the scans across the target surface the lateral distributions of metal, oxygen, and argon ions were derived. In the dc discharge the position of the erosion track is reproduced by increased ion intensities, while it is not the case for the rf excited plasma. The lateral variations of the observed species do not influence the lateral resistivity distributions of the deposited ITO films

  11. Small grain size zirconium-based coatings deposited by magnetron sputtering at low temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Jimenez, O., E-mail: omar.jimenez.udg@gmail.com [Departamento de Ingeniería de Proyectos, CUCEI, Universidad de Guadalajara, AP 307, CP 45101 Zapopan, Jal (Mexico); Department of Materials Science and Engineering, The University of Sheffield, Sheffield S1 3JD (United Kingdom); Audronis, M.; Leyland, A. [Department of Materials Science and Engineering, The University of Sheffield, Sheffield S1 3JD (United Kingdom); Flores, M.; Rodriguez, E. [Departamento de Ingeniería de Proyectos, CUCEI, Universidad de Guadalajara, AP 307, CP 45101 Zapopan, Jal (Mexico); Kanakis, K.; Matthews, A. [Department of Materials Science and Engineering, The University of Sheffield, Sheffield S1 3JD (United Kingdom)

    2015-09-30

    Hard, partly amorphous, ZrTiB(N) coatings were deposited by Physical Vapour Deposition (PVD) onto (111) silicon wafers at low substrate temperatures of 85 and 110 °C using Closed Field Unbalanced Magnetron Sputtering. A segmented rectangular sputter target composed of three pieces (Zr/TiB{sub 2}/Zr) was used as the source of evaporation of coating components. Two different substrate biases (i.e. floating potential and − 50 V) and N{sub 2} reactive-gas flow rates of 2, 4 and 6 sccm were employed as the main deposition parameter variables. The chemical composition, structure, morphology and mechanical properties were investigated using a variety of analytical techniques such as Glow-Discharge Optical Emission Spectroscopy, cross-sectional Scanning Electron Microscopy (SEM), Glancing Angle X-ray Diffraction (GAXRD) and nanoindentation. With other parameters fixed, coating properties were found to be dependent on the substrate negative bias and nitrogen flow rate. Linear scan profiles and SEM imaging revealed that all coatings were smooth, dense and featureless (in fracture cross section) with no apparent columnar morphology or macro-defects. GAXRD structural analysis revealed that mostly metallic phases were formed for coatings containing no nitrogen, whereas a solid solution (Zr,Ti)N single phase nitride was found in most of the reactively deposited coatings — exhibiting a very small grain size due to nitrogen and boron grain refinement effects. Hardness values from as low as 8.6 GPa up to a maximum of 25.9 GPa are related mainly to solid solution strengthening effects. The measured elastic moduli correlated with the trends in hardness behaviour; values in the range of 120–200 GPa were observed depending on the selected deposition parameters. Also, high H/E values (> 0.1) were achieved with several of the coatings.

  12. 75 FR 61989 - Airworthiness Directives; McDonnell Douglas Corporation Model DC-8-31, DC-8-32, DC-8-33, DC-8-41...

    Science.gov (United States)

    2010-10-07

    ... Airworthiness Directives; McDonnell Douglas Corporation Model DC- 8-31, DC-8-32, DC-8-33, DC-8-41, DC-8-42, and... to all of the McDonnell Douglas Corporation airplanes identified above. The existing AD currently... the following new airworthiness directive (AD): 2010-21-03 McDonnell Douglas Corporation: Amendment 39...

  13. High temperature superconducting films by rf magnetron sputtering

    International Nuclear Information System (INIS)

    Kadin, A.M.; Ballentine, P.H.

    1989-01-01

    The authors have produced sputtered films of Y-Ba-Cu-O and Bi-Sr-Ca-Cu-O by rf magnetron sputtering from an oxide target consisting of loose reacted powder. The use of a large 8-inch stoichiometric target in the magnetron mode permits films located above the central region to be free of negative-ion resputtering effects, and hence yields reproducible, uniform stoichiometric compositions for a wide range of substrate temperatures. Superconducting YBCO films have been obtained either by sputtering at low temperatures followed by an 850 0 C oxygen anneal, or alternatively by depositing onto substrates heated to ∼600 - 650 0 C and cooling in oxygen. Films prepared by the former method on cubic zirconia substrate consist of randomly oriented crystallites with zero resistance above 83 K. Those deposited on zirconia at medium temperatures without the high-temperature anneal contain smooth partially oriented crystallites, with a slightly depressed T/sub c/ ∼75K. Finally, superconducting films have been deposited on MgO using a BiSrCaCu/sub 2/O/sub x/ powder target

  14. Recent operation of the FNAL magnetron H- ion source

    Science.gov (United States)

    Karns, P. R.; Bollinger, D. S.; Sosa, A.

    2017-08-01

    This paper will detail changes in the operational paradigm of the Fermi National Accelerator Laboratory (FNAL) magnetron H- ion source due to upgrades in the accelerator system. Prior to November of 2012 the H- ions for High Energy Physics (HEP) experiments were extracted at ˜18 keV vertically downward into a 90 degree bending magnet and accelerated through a Cockcroft-Walton accelerating column to 750 keV. Following the upgrade in the fall of 2012 the H- ions are now directly extracted from a magnetron at 35 keV and accelerated to 750 keV by a Radio Frequency Quadrupole (RFQ). This change in extraction energy as well as the orientation of the ion source required not only a redesign of the ion source, but an updated understanding of its operation at these new values. Discussed in detail are the changes to the ion source timing, arc discharge current, hydrogen gas pressure, and cesium delivery system that were needed to maintain consistent operation at >99% uptime for HEP, with an increased ion source lifetime of over 9 months.

  15. Plasma properties of RF magnetron sputtering system using Zn target

    Energy Technology Data Exchange (ETDEWEB)

    Nafarizal, N.; Andreas Albert, A. R.; Sharifah Amirah, A. S.; Salwa, O.; Riyaz Ahmad, M. A. [Microelectronic and Nanotechnology - Shamsuddin Research Centre (MiNT-SRC), Faculty of Electrical and Electronic Engineering, Universiti Tun Hussein Onn Malaysia 86400 Parit Raja, Batu Pahat, Johor (Malaysia)

    2012-06-29

    In the present work, we investigate the fundamental properties of magnetron sputtering plasma using Zn target and its deposited Zn thin film. The magnetron sputtering plasma was produced using radio frequency (RF) power supply and Argon (Ar) as ambient gas. A Langmuir probe was used to collect the current from the plasma and from the current intensity, we calculate the electron density and electron temperature. The properties of Zn sputtering plasma at various discharge conditions were studied. At the RF power ranging from 20 to 100 W and gas pressure 5 mTorr, we found that the electron temperature was almost unchanged between 2-2.5 eV. On the other hand, the electron temperature increased drastically from 6 Multiplication-Sign 10{sup 9} to 1 Multiplication-Sign 10{sup 10}cm{sup -3} when the discharge gas pressure increased from 5 to 10 mTorr. The electron microscope images show that the grain size of Zn thin film increase when the discharge power is increased. This may be due to the enhancement of plasma density and sputtered Zn density.

  16. Structure and giant magnetoresistance of carbon-based amorphous films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Ma, L.; He, M.F.; Liu, Z.W.; Zeng, D.C.; Gu, Z.F.; Cheng, G.

    2014-01-01

    Pure amorphous carbon (a-C) and Co-doped Co x C 1−x films were prepared on n-Si(100) substrates by dc magnetron sputtering. In Co–C films, the nano-sized amorphous Co particles were homogeneously dispersed in the amorphous cross-linked carbon matrix. The structures of a-C and Co x C 1−x films were investigated by X-ray photoelectron spectroscopy and Raman spectroscopy. The results showed that the a-C films were diamond-like carbon (DLC) films. After doping cobalt into DLC film, the sp 3 -hybridized carbon content in DLC composite films almost had no change. The as-deposited Co x C 1−x granular films had larger value of magnetoresistance (MR) than the amorphous carbon film. A very high positive MR, up to 15.5% at magnetic field B = 0.8 T and x = 2.5 at.% was observed in a Co x C 1−x granular film with thickness of 80 nm at room temperature when the external magnetic field was perpendicular to the electric current and the film surface. With increase of the film thickness and Co-doped content, the MR decreased gradually. It remains a challenge to well explain the observed MR effect in the Co x C 1−x granular films. - Highlights: • The amorphous carbon films were diamond-like carbon films. • No carbide appearing, the Co–C composite films form a good metal/insulator system. • A high positive magnetoresistance, up to 15.5% at B = 0.8 T was observed in Co–C films

  17. Chemical and Morphological Characterization of Magnetron Sputtered at Different Bias Voltages Cr-Al-C Coatings

    Directory of Open Access Journals (Sweden)

    Aleksei Obrosov

    2017-02-01

    Full Text Available MAX phases (M = transition metal, A = A-group element, and X = C/N are of special interest because they possess a unique combination of the advantages of both metals and ceramics. Most attention is attracted to the ternary carbide Cr2AlC because of its excellent high-temperature oxidation, as well as hot corrosion resistance. Despite lots of publications, up to now the influence of bias voltage on the chemical bonding structure, surface morphology, and mechanical properties of the film is still not well understood. In the current study, Cr-Al-C films were deposited on silicon wafers (100 and Inconel 718 super alloy by dc magnetron sputtering with different substrate bias voltages and investigated using Scanning Electron Microscopy (SEM, X-ray Photoelectron Spectroscopy (XPS, X-ray Diffraction (XRD, Atomic Force Microscopy (AFM, and nanoindentation. Transmission Electron Microscopy (TEM was used to analyze the correlation between the growth of the films and the coating microstructure. The XPS results confirm the presence of Cr2AlC MAX phase due to a negative shift of 0.6–0.9 eV of the Al2p to pure aluminum carbide peak. The XRD results reveal the presence of Cr2AlC MAX Phase and carbide phases, as well as intermetallic AlCr2. The film thickness decreases from 8.95 to 6.98 µm with increasing bias voltage. The coatings deposited at 90 V exhibit the lowest roughness (33 nm and granular size (76 nm combined with the highest hardness (15.9 GPa. The ratio of Al carbide to carbide-like carbon state changes from 0.12 to 0.22 and correlates with the mechanical properties of the coatings. TEM confirms the columnar structure, with a nanocrystalline substructure, of the films.

  18. Structural and electrical properties of CuAlMo thin films prepared by magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Birkett, Martin, E-mail: martin.birkett@northumbria.ac.uk; Penlington, Roger; Wan, Chaoying; Zoppi, Guillaume

    2013-07-01

    The structural and electrical properties of a low resistivity CuAlMo thin film resistor material were investigated. The thin films were grown on Al{sub 2}O{sub 3} and glass substrates by direct current (dc) magnetron sputtering. The key electrical properties of sheet resistance, temperature coefficient of resistance (TCR) and resistance stability were investigated as a function of sputtering pressure and post-deposition heat treatment time and temperature. A low sputtering pressure range of 0.13 to 0.40 Pa produced CuAlMo films with sheet resistance in the range 0.1 to 0.2 Ω/□ and resistance stability of 0.45 to 0.65% with a TCR of − 90 ppm/°C which could be shifted to zero following annealing in air at 425 °C. Films grown at higher sputtering pressures of 0.53 to 0.80 Pa had increased sheet resistance in the range 0.4 to 0.6 Ω/□ and inferior stability of 0.8 to 1.7% with a more negative TCR of − 110 to − 180 ppm/°C which could not be shifted to zero following annealing. The stability of the films grown at 0.13 and 0.40 Pa could be further improved to < 0.25% with heat treatment, due to the formation of a protective aluminium oxide layer. A minimum dwell time of 3 h at 425 °C was required to stabilise the films and set the electrical properties. - Highlights: • Thin films of copper–aluminium–molybdenum were sputtered on alumina substrates. • Film properties were investigated with variation in process conditions. • Low sputtering pressure gave improved electrical performance. • Post deposition annealing in air further improved electrical performance.

  19. Structural and electrical properties of CuAlMo thin films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Birkett, Martin; Penlington, Roger; Wan, Chaoying; Zoppi, Guillaume

    2013-01-01

    The structural and electrical properties of a low resistivity CuAlMo thin film resistor material were investigated. The thin films were grown on Al 2 O 3 and glass substrates by direct current (dc) magnetron sputtering. The key electrical properties of sheet resistance, temperature coefficient of resistance (TCR) and resistance stability were investigated as a function of sputtering pressure and post-deposition heat treatment time and temperature. A low sputtering pressure range of 0.13 to 0.40 Pa produced CuAlMo films with sheet resistance in the range 0.1 to 0.2 Ω/□ and resistance stability of 0.45 to 0.65% with a TCR of − 90 ppm/°C which could be shifted to zero following annealing in air at 425 °C. Films grown at higher sputtering pressures of 0.53 to 0.80 Pa had increased sheet resistance in the range 0.4 to 0.6 Ω/□ and inferior stability of 0.8 to 1.7% with a more negative TCR of − 110 to − 180 ppm/°C which could not be shifted to zero following annealing. The stability of the films grown at 0.13 and 0.40 Pa could be further improved to < 0.25% with heat treatment, due to the formation of a protective aluminium oxide layer. A minimum dwell time of 3 h at 425 °C was required to stabilise the films and set the electrical properties. - Highlights: • Thin films of copper–aluminium–molybdenum were sputtered on alumina substrates. • Film properties were investigated with variation in process conditions. • Low sputtering pressure gave improved electrical performance. • Post deposition annealing in air further improved electrical performance

  20. Abnormal electrical resistivity in γ-TiAl thin films deposited by magnetron sputtering

    International Nuclear Information System (INIS)

    Alford, T.L.; Gadre, K.S.; Kim, H.C.; Deevi, S.C.

    2003-01-01

    Thin films of γ-TiAl are being considered as a potential conductor and/or diffusion barrier for high temperature electronics because of their high melting points and high oxidation resistance. However, it is not possible to form pure γ-TiAl thin films by thermal annealing of Al/Ti bilayers. This study, however, demonstrates the formation of γ-TiAl thin films by dc magnetron sputtering of a compound target. X-ray diffractometry and Rutherford backscattering spectrometry analyses confirm the γ-TiAl phase formation, composition, and thermal stability in vacuum (up to 700 deg. C, 1 h) on SiO 2 . Four-point probe resistivity measurements in vacuum show an initial increase in the resistivity with temperature up to transition temperature for the γ-TiAl thin films. At higher temperatures a decrease in resistivity with additional heating (i.e., negative temperature coefficient of resistivity, TCR) is seen. The values of dρ/dT are typically on the order of -0.32 μΩ cm/ deg. C between 200 and 550 deg. C. At the highest temperature, a minimum value of resistivity of ∼13 μΩ cm is obtained; this value is about one half the value of bulk TiAl at room temperatures. The negative TCR, low resistivity values at high temperatures, and temperature stability are not typically seen in bulk TiAl. This abnormal electrical property is explained using a modified model for a thermally activated polaron-hopping mechanism